Fabrication of metal matrix composites by powder metallurgy: A review

NASA Astrophysics Data System (ADS)

Manohar, Guttikonda; Dey, Abhijit; Pandey, K. M.; Maity, S. R.

2018-04-01

Now a day's metal matrix components are used in may industries and it finds the applications in many fields so, to make it as better performable materials. So, the need to increase the mechanical properties of the composites is there. As seen from previous studies major problem faced by the MMC's are wetting, interface bonding between reinforcement and matrix material while they are prepared by conventional methods like stir casting, squeeze casting and other techniques which uses liquid molten metals. So many researchers adopt PM to eliminate these defects and to increase the mechanical properties of the composites. Powder metallurgy is one of the better ways to prepare composites and Nano composites. And the major problem faced by the conventional methods are uniform distribution of the reinforcement particles in the matrix alloy, many researchers tried to homogeneously dispersion of reinforcements in matrix but they find it difficult through conventional methods, among all they find ultrasonic dispersion is efficient. This review article is mainly concentrated on importance of powder metallurgy in homogeneous distribution of reinforcement in matrix by ball milling or mechanical milling and how powder metallurgy improves the mechanical properties of the composites.

A Novel Process for Joining Ti Alloy and Al Alloy using Two-Stage Sintering Powder Metallurgy

NASA Astrophysics Data System (ADS)

Long, Luping; Liu, Wensheng; Ma, Yunzhu; Wu, Lei; Liu, Chao

2018-04-01

The major challenges for conventional diffusion bonding of joining Ti alloy and Al alloy are the undesirable interfacial reaction, low matrixes and joint strength. To avoid the problem in diffusion bonding, a novel two-stage sintering powder metallurgy process is developed. In the present work, the interface characterization and joint performance of the bonds obtained by powder metallurgy bonding are investigated and are compared with the diffusion bonded Ti/Al joints obtained with the same and the optimized process parameters. The results show that no intermetallic compound is visible in the Ti/Al joint obtained by powder metallurgy bonding, while a new layer formed at the joint diffusion bonded with the same parameters. The maximum tensile strength of joint obtained by diffusion bonding is 58 MPa, while a higher tensile strength reaching 111 MPa for a bond made by powder metallurgy bonding. Brittle fractures occur at all the bonds. It is shown that the powder metallurgy bonding of Ti/Al is better than diffusion bonding. The results of this study should benefit the bonding quality.

One step HIP canning of powder metallurgy composites

NASA Technical Reports Server (NTRS)

Juhas, John J. (Inventor)

1990-01-01

A single step is relied on in the canning process for hot isostatic pressing (HIP) powder metallurgy composites. The binders are totally removed while the HIP can of compatible refractory metal is sealed at high vacuum and temperature. This eliminates outgassing during hot isostatic pressing.

Biaxially textured articles formed by powder metallurgy

DOEpatents

Goyal, Amit; Williams, Robert K.; Kroeger, Donald M.

2003-10-21

A strengthened, biaxially textured alloy article having a magnetism less than pure Ni includes a rolled and annealed, compacted and sintered powder-metallurgy preform article, the preform article having been formed from a powder mixture selected from the group of mixtures consisting of: Ni, Ag, Ag--Cu, Ag--Pd, Ni--Cu, Ni--V, Ni--Mo, Ni--Al, Ni--Cr--Al, Ni--W--Al, Ni--V--Al, Ni--Mo--Al, Ni--Cu--Al; and at least one fine metal oxide powder; the article having a grain size which is fine and homogeneous; and having a dominant cube oriented {100}<100> orientation texture; and further having a Curie temperature less than that of pure Ni.

Powder-metallurgy superalloy strengthened by a secondary gamma phase.

NASA Technical Reports Server (NTRS)

Kotval, P. S.

1971-01-01

Description of experiments in which prealloyed powders of superalloy compositions were consolidated by extrusion after the strengthening by precipitation of a body-centered tetragonal gamma secondary Ni3 Ta phase. Thin foil electron microscopy showed that the mechanical properties of the resultant powder-metallurgy product were correlated with its microstructure. The product exhibited high strength at 1200 F without loss of ductility, after thermomechanical treatment and aging.

Properties of WZ21 (%wt) alloy processed by a powder metallurgy route.

PubMed

Cabeza, Sandra; Garcés, Gerardo; Pérez, Pablo; Adeva, Paloma

2015-06-01

Microstructure, mechanical properties and corrosion behaviour of WZ21 (%wt) alloy prepared by a powder metallurgy route from rapidly solidified powders have been studied. Results were compared to those of the same alloy prepared through a conventional route of casting and extrusion. The microstructure of the extruded ingot consisted of α-Mg grains and Mg3Zn3Y2 (W-phase) and LPSO-phase particles located at grain boundaries. Moreover, stacking faults were also observed within α-Mg grains. The alloy processed by the powder metallurgy route exhibited a more homogeneous and finer microstructure, with a grain size of 2 μm. In this case W-phase and Mg24Y5 phase were identified, but not the LPSO-phase. The microstructural refinement induced by the use of rapidly solidified powders strengthened the alloy at room temperature and promoted superplasticity at higher strain rates. Corrosion behaviour in PBS medium evidenced certain physical barrier effect of the almost continuous arrangements of second phases aligned along the extrusion direction in conventionally processed WZ21 alloy, with a stable tendency around 7 mm/year. On the other hand, powder metallurgy processing promoted significant pitting corrosion, inducing accelerated corrosion rate during prolonged immersion times. Copyright © 2015 Elsevier Ltd. All rights reserved.

Preparation of Three-Dimensional Graphene Foams Using Powder Metallurgy Templates.

PubMed

Sha, Junwei; Gao, Caitian; Lee, Seoung-Ki; Li, Yilun; Zhao, Naiqin; Tour, James M

2016-01-26

A simple and scalable method which combines traditional powder metallurgy and chemical vapor deposition is developed for the synthesis of mesoporous free-standing 3D graphene foams. The powder metallurgy templates for 3D graphene foams (PMT-GFs) consist of particle-like carbon shells which are connected by multilayered graphene that shows high specific surface area (1080 m(2) g(-1)), good crystallization, good electrical conductivity (13.8 S cm(-1)), and a mechanically robust structure. The PMT-GFs did not break under direct flushing with DI water, and they were able to recover after being compressed. These properties indicate promising applications of PMT-GFs for fields requiring 3D carbon frameworks such as in energy-based electrodes and mechanical dampening.

Powder Metallurgy Reconditioning of Food and Processing Equipment Components

NASA Astrophysics Data System (ADS)

Nafikov, M. Z.; Aipov, R. S.; Konnov, A. Yu.

2017-12-01

A powder metallurgy method is developed to recondition the worn surfaces of food and processing equipment components. A combined additive is composed to minimize the powder losses in sintering. A technique is constructed to determine the powder consumption as a function of the required metallic coating thickness. A rapid method is developed to determine the porosity of the coating. The proposed technology is used to fabricate a wear-resistant defectless metallic coating with favorable residual stresses, and the adhesive strength of this coating is equal to the strength of the base metal.

[Hygienic evaluation of risk factors on powder metallurgy production].

PubMed

2011-01-01

Complex hygienic, clinical, sociologic and epidemiologic studies revealed reliable relationship between work conditions and arterial hypertension, locomotory system disorders, monocytosis in powder metallurgy production workers. Findings are more probable cardiovascular and respiratory diseases, digestive tract diseases due to influence of lifestyle factors.

Device for preparing combinatorial libraries in powder metallurgy.

PubMed

Yang, Shoufeng; Evans, Julian R G

2004-01-01

This paper describes a powder-metering, -mixing, and -dispensing mechanism that can be used as a method for producing large numbers of samples for metallurgical evaluation or electrical or mechanical testing from multicomponent metal and cermet powder systems. It is designed to make use of the same commercial powders that are used in powder metallurgy and, therefore, to produce samples that are faithful to the microstructure of finished products. The particle assemblies produced by the device could be consolidated by die pressing, isostatic pressing, laser sintering, or direct melting. The powder metering valve provides both on/off and flow rate control of dry powders in open capillaries using acoustic vibration. The valve is simple and involves no relative movement, avoiding seizure with fine powders. An orchestra of such valves can be arranged on a building platform to prepare multicomponent combinatorial libraries. As with many combinatorial devices, identification and evaluation of sources of mixing error as a function of sample size is mandatory. Such an analysis is presented.

Ceramic Inclusions In Powder Metallurgy Disk Alloys: Characterization and Modeling

NASA Technical Reports Server (NTRS)

Bonacuse, Pete; Kantzos, Pete; Telesman, Jack

2002-01-01

Powder metallurgy alloys are increasingly used in gas turbine engines, especially as the material chosen for turbine disks. Although powder metallurgy materials have many advantages over conventionally cast and wrought alloys (higher strength, higher temperature capability, etc.), they suffer from the rare occurrence of ceramic defects (inclusions) that arise from the powder atomization process. These inclusions can have potentially large detrimental effect on the durability of individual components. An inclusion in a high stress location can act as a site for premature crack initiation and thereby considerably reduce the fatigue life. Because these inclusions are exceedingly rare, they usually don't reveal themselves in the process of characterizing the material for a particular application (the cumulative volume of the test bars in a fatigue life characterization is typically on the order of a single actual component). Ceramic inclusions have, however, been found to be the root cause of a number of catastrophic engine failures. To investigate the effect of these inclusions in detail, we have undertaken a study where a known population of ceramic particles, whose composition and morphology are designed to mimic the 'natural' inclusions, are added to the precursor powder. Surface connected inclusions have been found to have a particularly large detrimental effect on fatigue life, therefore the volume of ceramic 'seeds' added is calculated to ensure that a minimum number will occur on the surface of the fatigue test bars. Because the ceramic inclusions are irregularly shaped and have a tendency to break up in the process of extrusion and forging, a method of calculating the probability of occurrence and expected intercepted surface and embedded cross-sectional areas were needed. We have developed a Monte Carlo simulation to determine the distributions of these parameters and have verified the simulated results with observations of ceramic inclusions found in macro

Preparation of magnesium metal matrix composites by powder metallurgy process

NASA Astrophysics Data System (ADS)

Satish, J.; Satish, K. G., Dr.

2018-02-01

Magnesium is the lightest metal used as the source for constructional alloys. Today Magnesium based metal matrix composites are widely used in aerospace, structural, oceanic and automobile applications for its light weight, low density(two thirds that of aluminium), good high temperature mechanical properties and good to excellent corrosion resistance. The reason of designing metal matrix composite is to put in the attractive attributes of metals and ceramics to the base metal. In this study magnesium metal matrix hybrid composite are developed by reinforcing pure magnesium with silicon carbide (SiC) and aluminium oxide by method of powder metallurgy. This method is less expensive and very efficient. The Hardness test was performed on the specimens prepared by powder metallurgy method. The results revealed that the micro hardness of composites was increased with the addition of silicon carbide and alumina particles in magnesium metal matrix composites.

Advanced powder metallurgy aluminum alloys via rapid solidification technology

NASA Technical Reports Server (NTRS)

Ray, R.

1984-01-01

Aluminum alloys containing 10 to 11.5 wt. pct. of iron and 1.5 to 3 wt. pct. of chromium using the technique of rapid solidification powder metallurgy were studied. Alloys were prepared as thin ribbons (.002 inch thick) rapidly solidified at uniform rate of 10(6) C/second by the melt spinning process. The melt spun ribbons were pulverized into powders (-60 to 400 mesh) by a rotating hammer mill. The powders were consolidated by hot extrusion at a high reduction ratio of 50:1. The powder extrusion temperature was varied to determine the range of desirable processing conditions necessary to yield useful properties. Powders and consolidated alloys were characterized by SEM and optical metallography. The consolidated alloys were evaluated for (1) thermal stability, (2) tensile properties in the range, room temperature to 450 F, and (3) notch toughness in the range, room temperature to 450 F.

Ceramic Inclusions in Powder Metallurgy Disk Alloys: Characterization and Modeling

NASA Technical Reports Server (NTRS)

Bonacuse, Peter J.

2001-01-01

Powder metallurgy alloys are increasingly used in gas turbine engines, especially in turbine disk applications. Although powder metallurgy materials have many advantages over conventionally cast and wrought alloys (higher strength, higher temperature capability, etc.), they suffer from the rare occurrence of ceramic defects (inclusions) that are inherent to the powder atomization process. These inclusions can have a potentially large detrimental effect on the durability of individual components. An inclusion in a high stress location can act as a site for premature crack initiation and thereby considerably reduce the fatigue life. Because these inclusions are exceedingly rare, they typically do not reveal themselves in the process of characterizing the material for a particular application (the cumulative volume of the test bars in a fatigue life characterization is typically on the order of a single actual component). Ceramic inclusions have, however, been found to be the root cause of a number of catastrophic engine failures. To investigate the effect of these inclusions in detail, we have undertaken a study where known populations of ceramic particles, whose composition and morphology are designed to mimic the "natural" inclusions, are added to the precursor powder. Surface-connected inclusions have been found to have a particularly large detrimental effect on fatigue life; therefore, the quantity of ceramic "seeds" added is calculated to ensure that a minimum number will intersect the surface of the fatigue test bars. Because the ceramic inclusions are irregularly shaped and have a tendency to break up in the process of extrusion and forging, a method of calculating the probability of occurrence and expected intercepted surface area was needed. We have developed a Monte Carlo simulation to determine the distributions of these parameters and have verified the simulated results with observations of ceramic inclusions found in macroscopic slices from extrusions

Microstructure and Aging of Powder-Metallurgy Al Alloys

NASA Technical Reports Server (NTRS)

Blackburn, L. B.

1987-01-01

Report describes experimental study of thermal responses and aging behaviors of three new aluminum alloys. Alloys produced from rapidly solidified powders and contain 3.20 to 5.15 percent copper, 0.24 to 1.73 percent magnesium, 0.08 to 0.92 percent iron, and smaller amounts of manganese, nickel, titanium, silicon, and zinc. Peak hardness achieved at lower aging temperatures than with standard ingot-metallurgy alloys. Alloys of interest for automobile, aircraft, and aerospace applications.

Powder metallurgy preparation of Mg-Ca alloy for biodegradable implant application

NASA Astrophysics Data System (ADS)

Annur, D.; Suhardi, A.; Amal, M. I.; Anwar, M. S.; Kartika, I.

2017-04-01

Magnesium and its alloys is a promising candidate for implant application especially due to its biodegradability. In this study, Mg-7Ca alloys (in weight %) were processed by powder metallurgy from pure magnesium powder and calcium granule. Milling process was done in a shaker mill using stainless steel balls in various milling time (3, 5, and 8 hours) followed by compaction and sintering process. Different sintering temperatures were used (450°C and 550°C) to examine the effect of sintering temperature on mechanical properties and corrosion resistance. Microstructure evaluation was characterized by X-ray diffraction, scanning electron microscope and energy dispersive X-ray spectroscopy. Mechanical properties and corrosion behavior were examined through hardness testing and electrochemical testing in Hank’s solution (simulation body fluid). In this report, a prolonged milling time reduced particle size and later affected mechanical properties of Mg alloy. Meanwhile, the phase analysis showed that α Mg, Mg2Ca, MgO phases were formed after the sintering process. Further, this study showed that Mg-Ca alloy with different powder metallurgy process would have different corrosion rate although there were no difference of Ca content in the alloy.

Application of superalloy powder metallurgy for aircraft engines

NASA Technical Reports Server (NTRS)

Dreshfield, R. L.; Miner, R. V., Jr.

1980-01-01

In the last decade, Government/Industry programs have advanced powder metallurgy-near-net-shape technology to permit the use of hot isostatic pressed (HIP) turbine disks in the commercial aircraft fleet. These disks offer a 30% savings of input weight and an 8% savings in cost compared in cast-and-wrought disks. Similar savings were demonstrated for other rotating engine components. A compressor rotor fabricated from hot-die-forged-HIP superalloy billets revealed input weight savings of 54% and cost savings of 35% compared to cast-and-wrought parts. Engine components can be produced from compositions such as Rene 95 and Astroloy by conventional casting and forging, by forging of HIP powder billets, or by direct consolidation of powder by HIP. However, each process produces differences in microstructure or introduces different defects in the parts. As a result, their mechanical properties are not necessarily identical. Acceptance methods should be developed which recognize and account for the differences.

A major advance in powder metallurgy

NASA Technical Reports Server (NTRS)

Williams, Brian E.; Stiglich, Jacob J., Jr.; Kaplan, Richard B.; Tuffias, Robert H.

1991-01-01

Ultramet has developed a process which promises to significantly increase the mechanical properties of powder metallurgy (PM) parts. Current PM technology uses mixed powders of various constituents prior to compaction. The homogeneity and flaw distribution in PM parts depends on the uniformity of mixing and the maintenance of uniformity during compaction. Conventional PM fabrication processes typically result in non-uniform distribution of the matrix, flaw generation due to particle-particle contact when one of the constituents is a brittle material, and grain growth caused by high temperature, long duration compaction processes. Additionally, a significant amount of matrix material is usually necessary to fill voids and create 100 percent dense parts. In Ultramet's process, each individual particle is coated with the matrix material, and compaction is performed by solid state processing. In this program, Ultramet coated 12-micron tungsten particles with approximately 5 wt percent nickel/iron. After compaction, flexure strengths were measured 50 percent higher than those achieved in conventional liquid phase sintered parts (10 wt percent Ni/Fe). Further results and other material combinations are discussed.

Powder metallurgy approaches to high temperature components for gas turbine engines

NASA Technical Reports Server (NTRS)

Probst, H. B.

1974-01-01

Research is reported for the tensile strength, ductility, and heat performance characterisitics of powder metallurgy (p/m) superalloys. Oxide dispersion strengthened alloys were also evaluated for their strength during thermal processing. The mechanical attributes evident in both p/m supperalloys and dispersion strengthened alloys are discussed in terms of research into their possible combination.

Microstructural and mechanical characteristics of porous iron prepared by powder metallurgy.

PubMed

Capek, Jaroslav; Vojtěch, Dalibor

2014-10-01

The demand for porous biodegradable load-bearing implants has been increasing recently. Based on investigations of biodegradable stents, porous iron may be a suitable material for such applications. In this study, we prepared porous iron samples with porosities of 34-51 vol.% by powder metallurgy using ammonium bicarbonate as a space-holder material. We studied sample microstructure (SEM-EDX and XRD), flexural and compressive behaviors (universal loading machine) and hardness HV5 (hardness tester) of the prepared samples. Sample porosity increased with the amount of spacer in the initial mixtures. Only the pore surfaces had insignificant oxidation and no other contamination was observed. Increasing porosity decreased the mechanical properties of the samples; although, the properties were still comparable with human bone and higher than those of porous non-metallic biomaterials and porous magnesium prepared in a similar way. Based on these results, powder metallurgy appears to be a suitable method for the preparation of porous iron for orthopedic applications. Copyright © 2014 Elsevier B.V. All rights reserved.

Innovative technologies for powder metallurgy-based disk superalloys: Progress and proposal

NASA Astrophysics Data System (ADS)

Chong-Lin, Jia; Chang-Chun, Ge; Qing-Zhi, Yan

2016-02-01

Powder metallurgy (PM) superalloys are an important class of high temperature structural materials, key to the rotating components of aero engines. In the purview of the present challenges associated with PM superalloys, two novel approaches namely, powder preparation and the innovative spray-forming technique (for making turbine disk) are proposed and studied. Subsequently, advanced technologies like electrode-induction-melting gas atomization (EIGA), and spark-plasma discharge spheroidization (SPDS) are introduced, for ceramic-free superalloy powders. Presently, new processing routes are sought after for preparing finer and cleaner raw powders for disk superalloys. The progress of research in spray-formed PM superalloys is first summarized in detail. The spray-formed superalloy disks specifically exhibit excellent mechanical properties. This paper reviews the recent progress in innovative technologies for PM superalloys, with an emphasis on new ideas and approaches, central to the innovation driving techniques like powder processing and spray forming. Project supported by the National Natural Science Foundation of China (Grant Nos. 50974016 and 50071014).

Properties of porous magnesium prepared by powder metallurgy.

PubMed

Čapek, Jaroslav; Vojtěch, Dalibor

2013-01-01

Porous magnesium-based materials are biodegradable and promising for use in orthopaedic applications, but their applications are hampered by their difficult fabrication. This work reports the preparation of porous magnesium materials by a powder metallurgy technique using ammonium bicarbonate as spacer particles. The porosity of the materials depended on the amount of ammonium bicarbonate and was found to have strong negative effects on flexural strength and corrosion behaviour. However, the flexural strength of materials with porosities of up to 28 vol.% was higher than the flexural strength of non-metallic biomaterials and comparable with that of natural bone. Copyright © 2012 Elsevier B.V. All rights reserved.

Hydrogen halide cleaning of powder metallurgy nickel-20 chromium-3 thoria.

NASA Technical Reports Server (NTRS)

Herbell, T. P.

1972-01-01

The Cr2O3 content of powder metallurgy nickel-20 chromium-3 thoria was reduced with atmospheres consisting of hydrogen plus hydrogen chloride (HCl) or hydrogen bromide (HBr). The nonthoria oxygen content or 'oxygen excess' was reduced from an initial amount of greater than 50,000 ppm to less than 100 ppm. Low temperatures were effective, but lowest oxygen levels were achieved with the highest cleaning temperature of 1200 C.

Powder metallurgy technology of NiTi shape memory alloy

NASA Astrophysics Data System (ADS)

Dutkiewicz, J. M.; Maziarz, W.; Czeppe, T.; Lityńska, L.; Nowacki, W. K.; Gadaj, S. P.; Luckner, J.; Pieczyska, E. A.

2008-05-01

Powder metallurgy technology was elaborated for consolidation of shape memory NiTi powders. The shape memory alloy was compacted from the prealloyed powder delivered by Memry SA. The powder shows Ms = 10°C and As = -34°C as results from DSC measurements. The samples were hot pressed in the as delivered spherical particle's state. The hot compaction was performed in a specially constructed vacuum press, at temperature of 680°C and pressure of 400 MPa. The alloy powder was encapsulated in copper capsules prior to hot pressing to avoid oxidation or carbides formation. The alloy after hot vacuum compaction at 680°C (i.e. within the B2 NiTi stability range) has shown similar transformation range as the powder. The porosity of samples compacted in the as delivered state was only 1%. The samples tested in compression up to ɛ = 0.06 have shown partial superelastic effect due to martensitic reversible transform- ation which started at the stress above 300 MPa and returned back to ɛ = 0.015 after unloading. They have shown also a high ultimate compression strength of 1600 MPa. Measurements of the samples temperature changes during the process allowed to detect the temperature increase above 12°C for the strain rate 10-2 s-1 accompanied the exothermic martensite transformation during loading and the temperature decrease related to the reverse endothermic transformation during unloading.

Mechanical properties of modified low cobalt powder metallurgy Udimet 700 type alloys

NASA Technical Reports Server (NTRS)

Harf, Fredric H.

1989-01-01

Eight superalloys derived from Udimet 700 were prepared by powder metallurgy, hot isostatically pressed, heat treated and their tensile and creep rupture properties determined. Several of these alloys displayed properties superior to those of Udimet 700 similarly prepared, in one case exceeding the creep rupture life tenfold. Filter clogging by extracted gamma prime, its measurement and significance are discussed in an appendix.

Effect of vanadium carbide on dry sliding wear behavior of powder metallurgy AISI M2 high speed steel processed by concentrated solar energy

DOE Office of Scientific and Technical Information (OSTI.GOV)

García, C.

Mixtures of AISI M2 high speed steel and vanadium carbide (3, 6 or 10 wt.%) were prepared by powder metallurgy and sintered by concentrated solar energy (CSE). Two different powerful solar furnaces were employed to sinter the parts and the results were compared with those obtained by conventional powder metallurgy using a tubular electric furnace. CSE allowed significant reduction of processing times and high heating rates. The wear resistance of compacts was studied by using rotating pin-on-disk and linearly reciprocating ball-on-flat methods. Wear mechanisms were investigated by means of scanning electron microscopy (SEM) observations and chemical inspections of the microstructuresmore » of the samples. Better wear properties than those obtained by conventional powder metallurgy were achieved. The refinement of the microstructure and the formation of carbonitrides were the reasons for this. - Highlights: •Powder metallurgy of mixtures of M2 high speed steel and VC are studied. •Some sintering is done by concentrated solar energy. •Rotating pin-on-disk and linearly reciprocating ball-on-flat methods are used. •The tribological properties and wear mechanisms, under dry sliding, are studied.« less

Development of an extra-high strength powder metallurgy nickel-base superalloy

NASA Technical Reports Server (NTRS)

Kent, W. B.

1977-01-01

A program was conducted to optimize the composition of NASA IIb-11, an alloy originally developed as a wrought material, for thermal stability and to determine the feasibility for producing the alloy using powder metallurgy techniques. Seven compositions were melted and atomized, hot isostatically pressed, cross rolled to disks and heat treated. Tensile and stress rupture properties from room temperature to 870 C (1600 F) were determined in addition to thermal stability characteristics. Processing variables included hot isostatic pressing parameters and handling, cross rolling procedures and heat treatment cycles. NASA IIb-11E displayed the best combination of overall properties for service as a 760 C (1400 F) disk material. Its composition is 0.06 C, 8.5 Cr, 9.0 Co, 2.0 Mo, 7.1 W, 6.6 Ta, 4.5 Al, 0.75 Ti, 0.5 V, 0.7 Hf, 0.01 B, 0.05 Zr and balance Ni. While the alloy exhibits the highest 760 C (1400 F) rupture strength reported for any powder metallurgy disk alloy to date, additional studies to further evaluate the effects of heat treatment may be required. The alloy is not susceptible to topologically close-packed phase formation during thermal exposure at 870 C (1600 F) for 1,500 hours, but its mechanical property levels are lowered due to grain boundary carbide formation.

Assessment of Low Cycle Fatigue Behavior of Powder Metallurgy Alloy U720

NASA Technical Reports Server (NTRS)

Gabb, Tomothy P.; Bonacuse, Peter J.; Ghosn, Louis J.; Sweeney, Joseph W.; Chatterjee, Amit; Green, Kenneth A.

2000-01-01

The fatigue lives of modem powder metallurgy disk alloys are influenced by variabilities in alloy microstructure and mechanical properties. These properties can vary as functions of variables the different steps of materials/component processing: powder atomization, consolidation, extrusion, forging, heat treating, and machining. It is important to understand the relationship between the statistical variations in life and these variables, as well as the change in life distribution due to changes in fatigue loading conditions. The objective of this study was to investigate these relationships in a nickel-base disk superalloy, U720, produced using powder metallurgy processing. Multiple strain-controlled fatigue tests were performed at 538 C (1000 F) at limited sets of test conditions. Analyses were performed to: (1) assess variations of microstructure, mechanical properties, and LCF failure initiation sites as functions of disk processing and loading conditions; and (2) compare mean and minimum fatigue life predictions using different approaches for modeling the data from assorted test conditions. Significant variations in life were observed as functions of the disk processing variables evaluated. However, the lives of all specimens could still be combined and modeled together. The failure initiation sites for tests performed at a strain ratio R(sub epsilon) = epsilon(sub min)/epsilon(sub max) of 0 were different from those in tests at a strain ratio of -1. An approach could still be applied to account for the differences in mean and maximum stresses and strains. This allowed the data in tests of various conditions to be combined for more robust statistical estimates of mean and minimum lives.

Powder metallurgy: Solid and liquid phase sintering of copper

NASA Technical Reports Server (NTRS)

Sheldon, Rex; Weiser, Martin W.

1993-01-01

Basic powder metallurgy (P/M) principles and techniques are presented in this laboratory experiment. A copper based system is used since it is relatively easy to work with and is commercially important. In addition to standard solid state sintering, small quantities of low melting metals such as tin, zinc, lead, and aluminum can be added to demonstrate liquid phase sintering and alloy formation. The Taguchi Method of experimental design was used to study the effect of particle size, pressing force, sintering temperature, and sintering time. These parameters can be easily changed to incorporate liquid phase sintering effects and some guidelines for such substitutions are presented. The experiment is typically carried out over a period of three weeks.

Effects of fine porosity on the fatigue behavior of a powder metallurgy superalloy

NASA Technical Reports Server (NTRS)

Miner, R. V.; Dreshfield, R. L.

1980-01-01

Hot-isostatically-pressed powder-metallurgy Astroloy was obtained which contained 1.4 percent porosity at the grain boundaries produced by argon entering the powder container during pressing. This material was tested at 650 C in fatigue, creep-fatigue, tension, and stress-rupture and the results compared with data on sound Astroloy. They influenced fatigue crack initiation and produced a more intergranular mode of propagation but fatigue life was not drastically reduced. Fatigue behavior of the porous material showed typical correlation with tensile behavior. The plastic strain range-life relation was reduced proportionately with the reduction in tensile ductility, but the elastic strain range-life relation was changed little.

Experimental Characterization of Aluminum-Based Hybrid Composites Obtained Through Powder Metallurgy

NASA Astrophysics Data System (ADS)

Marcu, D. F.; Buzatu, M.; Ghica, V. G.; Petrescu, M. I.; Popescu, G.; Niculescu, F.; Iacob, G.

2018-06-01

The paper presents some experimental results concerning fabrication through powder metallurgy (P/M) of aluminum-based hybrid composites - Al/Al2O3/Gr. In order to understand the mechanisms that occur during the P/M processes of obtaining Al/Al2O3/Gr composite, we correlated the physical characteristics with their micro-structural characteristics. The characterization was performed using analysis techniques specific for P/M process, SEM-EDS and XRD analyses. Micro-structural characterization of the composites has revealed fairly uniform distribution this resulting in good properties of the final composite material.

[Concomitant influence of occupational and social risk factors on health of workers engaged into powder metallurgy].

PubMed

Shur, P Z; Zaĭtseva, N V; Kostarev, V G; Lebedeva-Nesevria, N A; Shliapnikov, D M

2012-01-01

Results of health risk evaluation in workers engaged into powder metallurgy, using complex of hygienic, medical, epidemiologic and sociologic studies, enable to define priority occupational and social risk factors, to assess degree of their influence on the workers' health and to identify occupationally induced diseases.

Retraction Note to: Ultra-High Strength and Ductile Lamellar-Structured Powder Metallurgy Binary Ti-Ta Alloys

NASA Astrophysics Data System (ADS)

Liu, Yong; Xu, Shenghang; Wang, Xin; Li, Kaiyang; Liu, Bin; Wu, Hong; Tang, Huiping

2018-05-01

The editors and authors have retracted the article, "Ultra-High Strength and Ductile Lamellar-Structured Powder Metallurgy Binary Ti-Ta Alloys" by Yong Liu, Shenghang Xu, Xin Wang, Kaiyang Li, Bin Liu, Hong Wu, and Huiping Tang (https://doi.org/10.1007/s11837-015-1801-1).

Powder Metallurgy Processing of a WxTaTiVCr High-Entropy Alloy and Its Derivative Alloys for Fusion Material Applications.

PubMed

Waseem, Owais Ahmed; Ryu, Ho Jin

2017-05-16

The W x TaTiVCr high-entropy alloy with 32at.% of tungsten (W) and its derivative alloys with 42 to 90at.% of W with in-situ TiC were prepared via the mixing of elemental W, Ta, Ti, V and Cr powders followed by spark plasma sintering for the development of reduced-activation alloys for fusion plasma-facing materials. Characterization of the sintered samples revealed a BCC lattice and a multi-phase structure. The selected-area diffraction patterns confirmed the formation of TiC in the high-entropy alloy and its derivative alloys. It revealed the development of C15 (cubic) Laves phases as well in alloys with 71 to 90at.% W. A mechanical examination of the samples revealed a more than twofold improvement in the hardness and strength due to solid-solution strengthening and dispersion strengthening. This study explored the potential of powder metallurgy processing for the fabrication of a high-entropy alloy and other derived compositions with enhanced hardness and strength.

Phase Stability of a Powder Metallurgy Disk Superalloy

NASA Technical Reports Server (NTRS)

Gabb, Timothy P.; Gayda, John; Kantzos, P.; Telesman, Jack; Gang, Anita

2006-01-01

Advanced powder metallurgy superalloy disks in aerospace turbine engines now entering service can be exposed to temperatures approaching 700 C, higher than those previously encountered. They also have higher levels of refractory elements, which can increase mechanical properties at these temperatures but can also encourage phase instabilities during service. Microstructural changes including precipitation of topological close pack phase precipitation and coarsening of existing gamma' precipitates can be slow at these temperatures, yet potentially significant for anticipated disk service times exceeding 1,000 h. The ability to quantify and predict such potential phase instabilities and degradation of capabilities is needed to insure structural integrity and air worthiness of propulsion systems over the full life cycle. A prototypical advanced disk superalloy was subjected to high temperature exposures, and then evaluated. Microstructural changes and corresponding changes in mechanical properties were quantified. The results will be compared to predictions of microstructure modeling software.

Porous titanium scaffolds fabricated using a rapid prototyping and powder metallurgy technique.

PubMed

Ryan, Garrett E; Pandit, Abhay S; Apatsidis, Dimitrios P

2008-09-01

One of the main issues in orthopaedic implant design is the fabrication of scaffolds that closely mimic the biomechanical properties of the surrounding bone. This research reports on a multi-stage rapid prototyping technique that was successfully developed to produce porous titanium scaffolds with fully interconnected pore networks and reproducible porosity and pore size. The scaffolds' porous characteristics were governed by a sacrificial wax template, fabricated using a commercial 3D-printer. Powder metallurgy processes were employed to generate the titanium scaffolds by filling around the wax template with titanium slurry. In the attempt to optimise the powder metallurgy technique, variations in slurry concentration, compaction pressure and sintering temperature were investigated. By altering the wax design template, pore sizes ranging from 200 to 400 microm were achieved. Scaffolds with porosities of 66.8 +/- 3.6% revealed compression strengths of 104.4+/-22.5 MPa in the axial direction and 23.5 +/- 9.6 MPa in the transverse direction demonstrating their anisotropic nature. Scaffold topography was characterised using scanning electron microscopy and microcomputed tomography. Three-dimensional reconstruction enabled the main architectural parameters such as pore size, interconnecting porosity, level of anisotropy and level of structural disorder to be determined. The titanium scaffolds were compared to their intended designs, as governed by their sacrificial wax templates. Although discrepancies in architectural parameters existed between the intended and the actual scaffolds, overall the results indicate that the porous titanium scaffolds have the properties to be potentially employed in orthopaedic applications.

Accelerated Threshold Fatigue Crack Growth Effect-Powder Metallurgy Aluminum Alloy

NASA Technical Reports Server (NTRS)

Piascik, R. S.; Newman, J. A.

2002-01-01

Fatigue crack growth (FCG) research conducted in the near threshold regime has identified a room temperature creep crack growth damage mechanism for a fine grain powder metallurgy (PM) aluminum alloy (8009). At very low (Delta) K, an abrupt acceleration in room temperature FCG rate occurs at high stress ratio (R = K(sub min)/K(sub max)). The near threshold accelerated FCG rates are exacerbated by increased levels of K(sub max) (K(sub max) = 0.4 K(sub IC)). Detailed fractographic analysis correlates accelerated FCG with the formation of crack-tip process zone micro-void damage. Experimental results show that the near threshold and K(sub max) influenced accelerated crack growth is time and temperature dependent.

The synthesis and characterization of Mg-Zn-Ca alloy by powder metallurgy process

DOE Office of Scientific and Technical Information (OSTI.GOV)

Annur, Dhyah; Franciska, P.L.; Erryani, Aprilia

Known for its biodegradation and biocompatible properties, magnesium alloys have gained many interests to be researched as implant material. In this study, Mg-3Zn-1Ca, Mg-29Zn-1Ca, and Mg-53Zn-4.3Ca (in wt%) were synthesized by means of powder metallurgy method. The compression strength and corrosion resistance of magnesium alloy were thoroughly examined. The microstructures of the alloy were characterized using optical microscopy, Scanning Electron Microscope, and also X-ray diffraction analysis. The corrosion resistance were evaluated using electrochemical analysis. The result indicated that Mg- Zn- Ca alloy could be synthesized using powder metallurgy method. This study showed that Mg-29Zn-1Ca would make the highest mechanical strengthmore » up to 159.81 MPa. Strengthening mechanism can be explained by precipitation hardening and grain refinement mechanism. Phase analysis had shown the formation of α Mg, MgO, and intermetallic phases: Mg2Zn11 and also Ca2Mg6Zn3. However, when the composition of Zn reach 53% weight, the mechanical strength will be decreasing. In addition, all of Mg-Zn-Ca alloy studied here had better corrosion resistance (Ecorr around -1.4 VSCE) than previous study of Mg. This study indicated that Mg- 29Zn- 1Ca alloy can be further analyzed to be a biodegradable implant material.« less

Causal Factors of Weld Porosity in Gas Tungsten Arc Welding of Powder-Metallurgy-Produced Titanium Alloys

NASA Astrophysics Data System (ADS)

Muth, T. R.; Yamamoto, Y.; Frederick, D. A.; Contescu, C. I.; Chen, W.; Lim, Y. C.; Peter, W. H.; Feng, Z.

2013-05-01

An investigation was undertaken using gas tungsten arc (GTA) welding on consolidated powder metallurgy (PM) titanium (Ti) plate to identify the causal factors behind observed porosity in fusion welding. Tramp element compounds of sodium and magnesium, residual from the metallothermic reduction of titanium chloride used to produce the titanium, were remnant in the starting powder and were identified as gas-forming species. PM-titanium made from revert scrap, where sodium and magnesium were absent, showed fusion weld porosity, although to a lesser degree. We show that porosity was attributable to hydrogen from adsorbed water on the surface of the powders prior to consolidation. The removal and minimization of both adsorbed water on the surface of titanium powder and the residues from the reduction process prior to consolidation of titanium powders are critical for achieving equivalent fusion welding success similar to that seen in wrought titanium produced via the Kroll process.

Thermal Stability of Zone Melting p-Type (Bi, Sb)2Te3 Ingots and Comparison with the Corresponding Powder Metallurgy Samples

NASA Astrophysics Data System (ADS)

Jiang, Chengpeng; Fan, Xi'an; Hu, Jie; Feng, Bo; Xiang, Qiusheng; Li, Guangqiang; Li, Yawei; He, Zhu

2018-04-01

During the past few decades, Bi2Te3-based alloys have been investigated extensively because of their promising application in the area of low temperature waste heat thermoelectric power generation. However, their thermal stability must be evaluated to explore the appropriate service temperature. In this work, the thermal stability of zone melting p-type (Bi, Sb)2Te3-based ingots was investigated under different annealing treatment conditions. The effect of service temperature on the thermoelectric properties and hardness of the samples was also discussed in detail. The results showed that the grain size, density, dimension size and mass remained nearly unchanged when the service temperature was below 523 K, which suggested that the geometry size of zone melting p-type (Bi, Sb)2Te3-based materials was stable below 523 K. The power factor and Vickers hardness of the ingots also changed little and maintained good thermal stability. Unfortunately, the thermal conductivity increased with increasing annealing temperature, which resulted in an obvious decrease of the zT value. In addition, the thermal stabilities of the zone melting p-type (Bi, Sb)2Te3-based materials and the corresponding powder metallurgy samples were also compared. All evidence implied that the thermal stabilities of the zone-melted (ZMed) p-type (Bi, Sb)2Te3 ingots in terms of crystal structure, geometry size, power factor (PF) and hardness were better than those of the corresponding powder metallurgy samples. However, their thermal stabilities in terms of zT values were similar under different annealing temperatures.

Development of fully dense and high performance powder metallurgy HSLA steel using HIP method

NASA Astrophysics Data System (ADS)

Liu, Wensheng; Pang, Xinkuan; Ma, Yunzhu; Cai, Qingshan; Zhu, Wentan; Liang, Chaoping

2018-05-01

In order to solve the problem that the mechanical properties of powder metallurgy (P/M) steels are much lower than those of traditional cast steels with the same composition due to their porosity, a high–strength–low–alloy (HSLA) steel with fully dense and excellent mechanical properties was fabricated through hot isostatic pressing (HIP) using gas–atomized powders. The granular structure in the P/M HIPed steel composed of bainitic ferrite and martensite–austenite (M–A) islands is obtained without the need of any rapid cooling. The P/M HIPed steel exhibit a combination of tensile strength and ductility that surpasses that of conventional cast steel and P/M sintered steel, confirming the feasibility of fabricating high performance P/M steel through appropriate microstructural control and manufacture process.

Study on Microstructures and Properties of Porous TiC Ceramics Fabricated by Powder Metallurgy

NASA Astrophysics Data System (ADS)

Ma, Yana; Bao, Chonggao; Han, Longhao; Chen, Jie

2017-02-01

Powder metallurgy process was used to fabricate porous titanium carbide (TiC) ceramics, in which TiC powders were taken as the raw materials, nickel was used as the metallic binder and urea was the space-holder. Microstructure, composition and phase of porous TiC ceramics were characterized by scanning electron microscopy (SEM) and x-ray diffraction (XRD). Flexure strength of the porous TiC ceramics was tested by a three-point bending method. The results show that macropores and micropores coexist in the prepared porous TiC ceramics. Moreover, the pore number, size and distribution in porous TiC ceramics can be controlled on demand. Particularly, the factors such as the number or size of space-holder, compacting pressure and Ni content have significant effect on the porosity and flexure strength.

In vitro bioactivity of a biocomposite fabricated from HA and Ti powders by powder metallurgy method.

PubMed

Ning, C Q; Zhou, Y

2002-07-01

Traditionally, hydroxyapatite was used as a coating material on titanium substrate by various techniques. In the present work, a biocomposite was successfully fabricated from hydroxyapatite and titanium powders by powder metallurgy method. Bioactivity of the composite in a simulated body fluid (SBF) was investigated. Main crystal phases of the as-fabricated composite are found to be Ti2O, CaTiO3, CaO, alpha-Ti and a TiP-like phase. When the composite is immersed in the simulated body fluid for a certain time, a poor-crystallized, calcium-deficient, carbonate-containing apatite film will form on the surface of the composite. The time required to induce apatite nucleation is within 2 h. In addition, the apatite is also incorporated with a little magnesium and chlorine element. It is found that Ti2O has the ability to induce the formation of bone-like apatite in the SBF. And a dissolve of the CaO phase could also provide favorable conditions for the apatite formation, by forming open pores on the surface of the composite and increasing the degree of supersaturation of the SBF with respect to the apatite.

N18, powder metallurgy superalloy for disks: Development and applications

DOE Office of Scientific and Technical Information (OSTI.GOV)

Guedou, J.Y.; Lautridou, J.C.; Honnorat, Y.

1993-08-01

The preliminary industrial development of a powder metallurgy (PM) superalloy, designated N18, for disk applications has been completed. This alloy exhibits good overall mechanical properties after appropriate processing of the material. These properties have been measured on both isothermally forged and extruded billets, as well as on specimens cut from actual parts. The temperature capability of the alloy is about 700 C for long-term applications and approximately 750 C for short-term use because of microstructural instability. Further improvements in creep and crack propagation properties, without significant reduction in tensile strength, are possible through appropriate thermomechanical processing, which results in amore » large controlled grain size. Spin pit tests on subscale disks have confirmed that the N18 alloy has a higher resistance than PM Astrology and is therefore an excellent alloy for modern turbine disk applications.« less

The stress-corrosion cracking behavior of high-strength aluminum powder metallurgy alloys

NASA Astrophysics Data System (ADS)

Pickens, J. R.; Christodoulou, L.

1987-01-01

The susceptibility to stress-corrosion cracking (SCC) of rapidly solidified (RS) aluminum powder metallurgy (P/M) alloys 7090 and 7091, mechanically alloyed aluminum P/M alloy IN* 9052, and ingot metallurgy (I/M) alloys of similar compositions was compared using bolt-loaded double cantilever beam specimens. In addition, the effects of aging, grain size, grain boundary segregation, pre-exposure embrittlement, and loading mode on the SCC of 7091 were independently assessed. Finally, the data generated were used to elucidate the mechanisms of SCC in the three P/M alloys. The IN 9052 had the lowest SCC susceptibility of all alloys tested in the peak-strength condition, although no SCC was observed in the two RS alloys in the overaged condition. The susceptibility of the RS alloys was greater in the underaged than the peak-aged temper. We detected no significant differences in susceptibility of 7091 with grain sizes varying from 2 to 300 μm. Most of the crack advance during SCC of 7091 was by hydrogen embrittlement (HE). Furthermore, both RS alloys were found to be susceptible to preexposure embrittlement—also indicative of HE. The P/M alloys were less susceptible to SCC than the I/M alloys in all but one test.

Niobium-titanium superconductors produced by powder metallurgy having artificial flux pinning centers

DOEpatents

Jablonski, Paul D.; Larbalestier, David C.

1993-01-01

Superconductors formed by powder metallurgy have a matrix of niobium-titanium alloy with discrete pinning centers distributed therein which are formed of a compatible metal. The artificial pinning centers in the Nb-Ti matrix are reduced in size by processing steps to sizes on the order of the coherence length, typically in the range of 1 to 10 nm. To produce the superconductor, powders of body centered cubic Nb-Ti alloy and the second phase flux pinning material, such as Nb, are mixed in the desired percentages. The mixture is then isostatically pressed, sintered at a selected temperature and selected time to produce a cohesive structure having desired characteristics without undue chemical reaction, the sintered billet is reduced in size by deformation, such as by swaging, the swaged sample receives heat treatment and recrystallization and additional swaging, if necessary, and is then sheathed in a normal conducting sheath, and the sheathed material is drawn into a wire. The resulting superconducting wire has second phase flux pinning centers distributed therein which provide enhanced J.sub.ct due to the flux pinning effects.

Effects of fine porosity on the fatigue behavior of a powder metallurgy superalloy

NASA Technical Reports Server (NTRS)

Miner, R. V., Jr.; Dreshfield, R. L.

1980-01-01

Hot isostatically pressed powder metallurgy Astroloy was obtained which contained 1.4 percent fine porosity at the grain boundaries produced by argon entering the powder container during pressing. This material was tested at 650 C in fatigue, creep fatigue, tension, and stress-rupture and the results compared with previous data on sound Astroloy. The pores averaged about 2 micrometers diameter and 20 micrometers spacing. They did influence fatigue crack initiation and produced a more intergranular mode of propagation. However, fatigue life was not drastically reduced. A large 25 micrometers pore in one specimen resulting from a hollow particle did not reduce life by 60 percent. Fatigue behavior of the porous material showed typical correlation with tensile behavior. The plastic strain range life relation was reduced proportionately with the reduction in tensile ductility, but the elastic strain range-life relation was little changed reflecting the small reduction in sigma sub u/E for the porous material.

Mechanical Properties of Lightweight Porous Magnesium Processed Through Powder Metallurgy

NASA Astrophysics Data System (ADS)

Zou, Ning; Li, Qizhen

2018-02-01

Porous magnesium (Mg) samples with various overall porosities (28.4 ± 1.8%, 35.5 ± 2.5%, 45.4 ± 1.9%, and 62.4 ± 2.2%) were processed through powder metallurgy and characterized to study their mechanical properties. Different porosities were obtained by utilizing different mass fractions of space holder camphene. Camphene was removed by sublimation before sintering and contributed to processing porous Mg with high purity and small average pore size. The average pore size increased from 5.2 µm to 15.1 µm with increase of the porosity from 28.4 ± 1.8% to 62.4 ± 2.2%. Compressive strain-stress data showed that the strain hardening rate, yield strength, and ultimate compressive strength decreased with increase of the porosity. The theoretical yield strength of porous Mg obtained using the Gibson-Ashby model agreed with experimental data.

[Study on physical properties of titanium alloy sample fabricated with vacuum-sintered powder metallurgy].

PubMed

Ding, X; Liang, X; Chao, Y; Han, X

2000-06-01

To investigate the physical properties of titanium alloy fabricated with vacuum-sintered powder metallurgy. The titanium powders of three different particle sizes(-160mesh, -200 - +300mesh, -300mesh) were selected, and mixed with copper and aluminum powder in different proportions. Two other groups were made up of titanium powder(-200 - +300mesh) plated with copper and tin. The build-up and, condensation method and a double-direction press with a metal mold were used. The green compacts were sintered at 1000 degrees C for 15 minutes in a vacuum furnace at 0.025 Pa. In the double-direction press, the specimens were compacted at the pressure of 100 MPa, 200 MPa and 300 MPa respectively. Then the linear shrinkage ratio and the opening porosity of the sintered compacts were evaluated respectively. 1. The linear shrinkage ratio of specimens decreased with the increased compacted pressure(P < 0.05). There was no significant difference among the linear shrinkage ratios of three different titanium powders at the same compacted pressure(P > 0.05), but that of titanium powder plated with copper and tin was higher than those of other specimens without plating(P < 0.05). 2. The opening porosity of specimens decreased with the increased compacted pressure(P < 0.05). Three different sized particle of titanium powder did not affect the opening porosity at the same compacted pressure(P > 0.05). The composition of titanium-based metal powder mixtures and the compacted pressures affect the physical properties of sintered compacts. Titanium powder plated with copper and tin is compacted and sintered easily, and the physical properties of sintered compacts are greatly improved.

Accelerated Near-Threshold Fatigue Crack Growth Behavior of an Aluminum Powder Metallurgy Alloy

NASA Technical Reports Server (NTRS)

Piascik, Robert S.; Newman, John A.

2002-01-01

Fatigue crack growth (FCG) research conducted in the near threshold regime has identified a room temperature creep crack growth damage mechanism for a fine grain powder metallurgy (PM) aluminum alloy (8009). At very low DK, an abrupt acceleration in room temperature FCG rate occurs at high stress ratio (R = Kmin/Kmax). The near threshold accelerated FCG rates are exacerbated by increased levels of Kmax (Kmax less than 0.4 KIC). Detailed fractographic analysis correlates accelerated FCG with the formation of crack-tip process zone micro-void damage. Experimental results show that the near threshold and Kmax influenced accelerated crack growth is time and temperature dependent.

Dose and Dose Risk Caused by Natural Phenomena - Proposed Powder Metallurgy Core Manufacturing Facility

DOE Office of Scientific and Technical Information (OSTI.GOV)

Holmes, W.G.

2001-08-16

The offsite radiological effects from high velocity straight winds, tornadoes, and earthquakes have been estimated for a proposed facility for manufacturing enriched uranium fuel cores by powder metallurgy. Projected doses range up to 30 mrem/event to the maximum offsite individual for high winds and up to 85 mrem/event for very severe earthquakes. Even under conservative assumptions on meteorological conditions, the maximum offsite dose would be about 20 per cent of the DOE limit for accidents involving enriched uranium storage facilities. The total dose risk is low and is dominated by the risk from earthquakes. This report discusses this test.

Study of alumina-trichite reinforcement of a nickel-based matric by means of powder metallurgy

NASA Technical Reports Server (NTRS)

Walder, A.; Hivert, A.

1982-01-01

Research was conducted on reinforcing nickel based matrices with alumina trichites by using powder metallurgy. Alumina trichites previously coated with nickel are magnetically aligned. The felt obtained is then sintered under a light pressure at a temperature just below the melting point of nickel. The halogenated atmosphere technique makes it possible to incorporate a large number of additive elements such as chromium, titanium, zirconium, tantalum, niobium, aluminum, etc. It does not appear that going from laboratory scale to a semi-industrial scale in production would create any major problems.

Testing of electroformed deposited iridium/powder metallurgy rhenium rockets

NASA Technical Reports Server (NTRS)

Reed, Brian D.; Dickerson, Robert

1996-01-01

High-temperature, oxidation-resistant chamber materials offer the thermal margin for high performance and extended lifetimes for radiation-cooled rockets. Rhenium (Re) coated with iridium (Ir) allow hours of operation at 2200 C on Earth-storable propellants. One process for manufacturing Ir/Re rocket chambers is the fabrication of Re substrates by powder metallurgy (PM) and the application of Ir coatings by using electroformed deposition (ED). ED Ir coatings, however, have been found to be porous and poorly adherent. The integrity of ED Ir coatings could be improved by densification after the electroforming process. This report summarizes the testing of two 22-N, ED Ir/PM Re rocket chambers that were subjected to post-deposition treatments in an effort to densify the Ir coating. One chamber was vacuum annealed, while the other chamber was subjected to hot isostatic pressure (HIP). The chambers were tested on gaseous oxygen/gaseous hydrogen propellants, at mixture ratios that simulated the oxidizing environments of Earth-storable propellants. ne annealed ED Ir/PM Re chamber was tested for a total of 24 firings and 4.58 hr at a mixture ratio of 4.2. After only 9 firings, the annealed ED Ir coating began to blister and spall upstream of the throat. The blistering and spalling were similar to what had been experienced with unannealed, as-deposited ED Ir coatings. The HIP ED Ir/PM Re chamber was tested for a total of 91 firings and 11.45 hr at mixture ratios of 3.2 and 4.2. The HIP ED Ir coating remained adherent to the Re substrate throughout testing; there were no visible signs of coating degradation. Metallography revealed, however, thinning of the HIP Ir coating and occasional pores in the Re layer upstream of the throat. Pinholes in the Ir coating may have provided a path for oxidation of the Re substrate at these locations. The HIP ED Ir coating proved to be more effective than vacuum annealed and as-deposited ED Ir. Further densification is still required to

Application of powder metallurgy technique to produce improved bearing elements for cryogenic aerospace engine turbopumps

NASA Technical Reports Server (NTRS)

Moxson, V. S.; Moracz, D. J.; Bhat, B. N.; Dolan, F. J.; Thom, R.

1987-01-01

Traditionally, vacuum melted 440C stainless steel is used for high performance bearings for aerospace cryogenic systems where corrosion due to condensation is a major concern. For the Space Shuttle Main Engine (SSME), however, 440C performance in the high-pressure turbopumps has been marginal. A basic assumption of this study was that powder metallurgy, rather than cast/wrought, processing would provide the finest, most homogeneous bearing alloy structure. Preliminary testing of P/M alloys (hardness, corrosion resistance, wear resistance, fatigue resistance, and fracture toughness) was used to 'de-select' alloys which did perform as well as baseline 440C. Five out of eleven candidate materials (14-4/6V, X-405, MRC-2001, T-440V, and D-5) based on preliminary screening were selected for the actual rolling-sliding five-ball testing. The results of this test were compared with high-performance vacuum-melted M50 bearing steel. The results of the testing indicated outstanding performance of two P/M alloys, X-405 and MRC-2001, which eventually will be further evaluated by full-scale bearing testing.

Effects of carbon and hafnium concentrations in wrought powder-metallurgy superalloys based on NASA 2B-11 alloy

NASA Technical Reports Server (NTRS)

Miner, R. V., Jr.

1976-01-01

A candidate alloy for advanced-temperature turbine engine disks, and four modifications of that alloy with various C and Hf concentrations were produced as cross-rolled disks from prealloyed powder that was hot isostatically compacted. The mechanical properties, microstructures, and phase relations of the alloys are discussed in terms of their C and Hf concentrations. A low-C and high-Hf modification of IIB-11 had the best balance of mechanical properties for service below about 750 C. Because of their finer grain sizes, none of the powder-metallurgy alloys produced had the high-temperature rupture strength of conventionally cast and wrought IIB-11.

Mechanisms of fatigue crack retardation following single tensile overloads in powder metallurgy aluminum alloys

NASA Technical Reports Server (NTRS)

Bray, G. H.; Reynolds, A. P.; Starke, E. A., Jr.

1992-01-01

In ingot metallurgy (IM) alloys, the number of delay cycles following a single tensile overload typically increases from a minimum at an intermediate baseline stress intensity range, Delta-K(B), with decreasing Delta-K(B) approaching threshold and increasing Delta-K(B) approaching unstable fracture to produce a characteristic 'U' shaped curve. Two models have been proposed to explain this behavior. One model is based on the interaction between roughness and plasticity-induced closure, while the other model only utilizes plasticity-induced closure. This article examines these models, using experimental results from constant amplitude and single overload fatigue tests performed on two powder metallurgy (PM) aluminum alloys, AL-905XL and AA 8009. The results indicate that the 'U'-shaped curve is primarily due to plasticity-induced closure, and that the plasticity-induced retardation effect is through-thickness in nature, occurring in both the surface and interior regions. However, the retardation effect is greater at the surface, because the increase in plastic strain at the crack tip and overload plastic zone size are larger in the plane-stress surface regions than in the plane-strain interior regions. These results are not entirely consistent with either of the proposed models.

The Effect of Forging Variables on the Supersolvus Heat-Treatment Response of Powder-Metallurgy Nickel-Base Superalloys

NASA Astrophysics Data System (ADS)

Semiatin, S. L.; Shank, J. M.; Shiveley, A. R.; Saurber, W. M.; Gaussa, E. F.; Pilchak, A. L.

2014-12-01

The effect of subsolvus forging temperature and strain rate on the grain size developed during final supersolvus heat treatment (SSHT) of two powder-metallurgy, gamma-gamma prime superalloys, IN-100 and LSHR, was established. For this purpose, isothermal, hot compression tests were performed at temperatures ranging from 1144 K (871 °C) and 22 K (22 °C) below the respective gamma-prime solvus temperatures ( T γ') and strain rates between 0.0003 and 10 s-1. Deformed samples were then heat treated 20 K (20 °C) above the solvus for 1 h with selected additional samples exposed for shorter and longer times. For both alloys, the grain size developed during SSHT was in the range of 15 to 30 μm, except for those processing conditions consisting of pre-deformation at the highest temperature, i.e., T γ'—22 K ( T γ'—22 °C), and strain rates in the range of ~0.001 to 0.1 s-1. In these latter instances, the heat-treated grain size was approx. four times as large. The observations were interpreted in terms of the mechanisms of deformation during hot working and their effect on the driving forces for grain-boundary migration which controls the evolution of the gamma-grain size.

Effect of sintering conditions on the microstructural and mechanical characteristics of porous magnesium materials prepared by powder metallurgy.

PubMed

Čapek, Jaroslav; Vojtěch, Dalibor

2014-02-01

There has recently been an increased demand for porous magnesium materials in many applications, especially in the medical field. Powder metallurgy appears to be a promising approach for the preparation of such materials. Many works have dealt with the preparation of porous magnesium; however, the effect of sintering conditions on material properties has rarely been investigated. In this work, we investigated porous magnesium samples that were prepared by powder metallurgy using ammonium bicarbonate spacer particles. The effects of the purity of the argon atmosphere and sintering time on the microstructure (SEM, EDX and XRD) and mechanical behaviour (universal loading machine and Vickers hardness tester) of porous magnesium were studied. The porosities of the prepared samples ranged from 24 to 29 vol.% depending on the sintering conditions. The purity of atmosphere played a significant role when the sintering time exceeded 6h. Under a gettered argon atmosphere, a prolonged sintering time enhanced diffusion connections between magnesium particles and improved the mechanical properties of the samples, whereas under a technical argon atmosphere, oxidation at the particle surfaces caused deterioration in the mechanical properties of the samples. These results suggest that a refined atmosphere is required to improve the mechanical properties of porous magnesium. © 2013.

Biaxially textured articles formed by power metallurgy

DOEpatents

Goyal, Amit; Williams, Robert K.; Kroeger, Donald M.

2003-08-26

A biaxially textured alloy article having a magnetism less than pure Ni includes a rolled and annealed compacted and sintered powder-metallurgy preform article, the preform article having been formed from a powder mixture selected from the group of mixtures consisting of: at least 60 at % Ni powder and at least one of Cr powder, W powder, V powder, Mo powder, Cu powder, Al powder, Ce powder, YSZ powder, Y powder, Mg powder, and RE powder; the article having a fine and homogeneous grain structure; and having a dominant cube oriented {100}<100> orientation texture; and further having a Curie temperature less than that of pure Ni.

Optimization of the Hot Forging Processing Parameters for Powder Metallurgy Fe-Cu-C Connecting Rods Based on Finite Element Simulation

NASA Astrophysics Data System (ADS)

Li, Fengxian; Yi, Jianhong; Eckert, Jürgen

2017-12-01

Powder forged connecting rods have the problem of non-uniform density distributions because of their complex geometric shape. The densification behaviors of powder metallurgy (PM) connecting rod preforms during hot forging processes play a significant role in optimizing the connecting rod quality. The deformation behaviors of a connecting rod preform, a Fe-3Cu-0.5C (wt pct) alloy compacted and sintered by the powder metallurgy route (PM Fe-Cu-C), were investigated using the finite element method, while damage and friction behaviors of the material were considered in the complicated forging process. The calculated results agree well with the experimental results. The relationship between the processing parameters of hot forging and the relative density of the connecting rod was revealed. The results showed that the relative density of the hot forged connecting rod at the central shank changed significantly compared with the relative density at the big end and at the small end. Moreover, the relative density of the connecting rod was sensitive to the processing parameters such as the forging velocity and the initial density of the preform. The optimum forging processing parameters were determined and presented by using an orthogonal design method. This work suggests that the processing parameters can be optimized to prepare a connecting rod with uniform density distribution and can help to better meet the requirements of the connecting rod industry.

Metallurgy and properties of plasma spray formed materials

NASA Technical Reports Server (NTRS)

Mckechnie, T. N.; Liaw, Y. K.; Zimmerman, F. R.; Poorman, R. M.

1992-01-01

Understanding the fundamental metallurgy of vacuum plasma spray formed materials is the key to enhancing and developing full material properties. Investigations have shown that the microstructure of plasma sprayed materials must evolve from a powder splat morphology to a recrystallized grain structure to assure high strength and ductility. A fully, or near fully, dense material that exhibits a powder splat morphology will perform as a brittle material compared to a recrystallized grain structure for the same amount of porosity. Metallurgy and material properties of nickel, iron, and copper base alloys will be presented and correlated to microstructure.

Fabrication of homogeneously dispersed graphene/Al composites by solution mixing and powder metallurgy

NASA Astrophysics Data System (ADS)

Zeng, Xiang; Teng, Jie; Yu, Jin-gang; Tan, Ao-shuang; Fu, Ding-fa; Zhang, Hui

2018-01-01

Graphene-reinforced aluminum (Al) matrix composites were successfully prepared via solution mixing and powder metallurgy in this study. The mechanical properties of the composites were studied using microhardness and tensile tests. Compared to the pure Al alloy, the graphene/Al composites showed increased strength and hardness. A tensile strength of 255 MPa was achieved for the graphene/Al composite with only 0.3wt% graphene, which has a 25% increase over the tensile strength of the pure Al matrix. Raman spectroscopy, Fourier transform infrared spectroscopy, scanning electron microscopy, and transmission electron microscopy were used to investigate the morphologies, chemical compositions, and microstructures of the graphene and the graphene/Al composites. On the basis of fractographic evidence, a relevant fracture mechanism is proposed.

Elevated temperature crack growth in advanced powder metallurgy aluminum alloys

NASA Technical Reports Server (NTRS)

Porr, William C., Jr.; Gangloff, Richard P.

1990-01-01

Rapidly solidified Al-Fe-V-Si powder metallurgy alloy FVS0812 is among the most promising of the elevated temperature aluminum alloys developed in recent years. The ultra fine grain size and high volume fraction of thermally stable dispersoids enable the alloy to maintain tensile properties at elevated temperatures. In contrast, this alloy displays complex and potentially deleterious damage tolerant and time dependent fracture behavior that varies with temperature. J-Integral fracture mechanics were used to determine fracture toughness (K sub IC) and crack growth resistance (tearing modulus, T) of extruded FVS0812 as a function of temperature. The alloy exhibits high fracture properties at room temperature when tested in the LT orientation, due to extensive delamination of prior ribbon particle boundaries perpendicular to the crack front. Delamination results in a loss of through thickness constraint along the crack front, raising the critical stress intensity necessary for precrack initiation. The fracture toughness and tensile ductility of this alloy decrease with increasing temperature, with minima observed at 200 C. This behavior results from minima in the intrinsic toughness of the material, due to dynamic strain aging, and in the extent of prior particle boundary delaminations. At 200 C FVS0812 fails at K levels that are insufficient to cause through thickness delamination. As temperature increases beyond the minimum, strain aging is reduced and delamination returns. For the TL orientation, K (sub IC) decreased and T increased slightly with increasing temperature from 25 to 316 C. Fracture in the TL orientation is governed by prior particle boundary toughness; increased strain localization at these boundaries may result in lower toughness with increasing temperature. Preliminary results demonstrate a complex effect of loading rate on K (sub IC) and T at 175 C, and indicate that the combined effects of time dependent deformation, environment, and strain aging

Compressibility of 304 Stainless Steel Powder Metallurgy Materials Reinforced with 304 Short Stainless Steel Fibers

PubMed Central

Yao, Bibo; Zhou, Zhaoyao; Duan, Liuyang; Xiao, Zhiyu

2016-01-01

Powder metallurgy (P/M) technique is usually used for manufacturing porous metal materials. However, some P/M materials are limitedly used in engineering for their performance deficiency. A novel 304 stainless steel P/M material was produced by a solid-state sintering of 304 stainless steel powders and 304 short stainless steel fibers, which were alternately laid in layers according to mass ratio. In this paper, the compressive properties of the P/M materials were characterized by a series of uniaxial compression tests. The effects of fiber content, compaction pressure and high temperature nitriding on compressive properties were investigated. The results indicated that, without nitriding, the samples changed from cuboid to cydariform without damage in the process of compression. The compressive stress was enhanced with increasing fiber content ranging from 0 to 8 wt.%. For compaction pressure from 55 to 75 MPa, greater compaction pressure improved compressive stress. Moreover, high temperature nitriding was able to significantly improve the yield stress, but collapse failure eventually occurred. PMID:28773285

Compressibility of 304 Stainless Steel Powder Metallurgy Materials Reinforced with 304 Short Stainless Steel Fibers.

PubMed

Yao, Bibo; Zhou, Zhaoyao; Duan, Liuyang; Xiao, Zhiyu

2016-03-04

Powder metallurgy (P/M) technique is usually used for manufacturing porous metal materials. However, some P/M materials are limitedly used in engineering for their performance deficiency. A novel 304 stainless steel P/M material was produced by a solid-state sintering of 304 stainless steel powders and 304 short stainless steel fibers, which were alternately laid in layers according to mass ratio. In this paper, the compressive properties of the P/M materials were characterized by a series of uniaxial compression tests. The effects of fiber content, compaction pressure and high temperature nitriding on compressive properties were investigated. The results indicated that, without nitriding, the samples changed from cuboid to cydariform without damage in the process of compression. The compressive stress was enhanced with increasing fiber content ranging from 0 to 8 wt.%. For compaction pressure from 55 to 75 MPa, greater compaction pressure improved compressive stress. Moreover, high temperature nitriding was able to significantly improve the yield stress, but collapse failure eventually occurred.

Powder metallurgy inspired low-temperature fabrication of high-performance stereocomplexed polylactide products with good optical transparency

NASA Astrophysics Data System (ADS)

Bai, Dongyu; Liu, Huili; Bai, Hongwei; Zhang, Qin; Fu, Qiang

2016-02-01

Stereocomplexation between enantiomeric poly(L-lactide) (PLLA) and poly(D-lactide) (PDLA) provides an avenue to greatly enhance performance of eco-friendly polylactide (PLA). Unfortunately, although the manufacturing of semicrystalline polymers generally involves melt processing, it is still hugely challenging to create high-performance stereocomplexed polylactide (sc-PLA) products from melt-processed high-molecular-weight PLLA/PDLA blends due to the weak crystallization memory effect of stereocomplex (sc) crystallites after complete melting as well as the substantial degradation of PLA chains at elevated melt-processing temperatures of ca. 240-260 °C. Inspired by the concept of powder metallurgy, here we report a new facile route to address these obstacles by sintering of sc-PLA powder at temperatures as low as 180-210 °C, which is distinctly different from traditional sintering of polymer powders performed at temperatures far exceeding their melting temperatures. The enantiomeric PLA chain segments from adjacent powder particles can interdiffuse across particle interfaces and co-crystallize into new sc crystallites capable of tightly welding the interfaces during the low-temperature sintering process, and thus highly transparent sc-PLA products with outstanding heat resistance, mechanical strength, and hydrolytic stability have been successfully fabricated for the first time.

Powder metallurgy inspired low-temperature fabrication of high-performance stereocomplexed polylactide products with good optical transparency

PubMed Central

Bai, Dongyu; Liu, Huili; Bai, Hongwei; Zhang, Qin; Fu, Qiang

2016-01-01

Stereocomplexation between enantiomeric poly(l-lactide) (PLLA) and poly(d-lactide) (PDLA) provides an avenue to greatly enhance performance of eco-friendly polylactide (PLA). Unfortunately, although the manufacturing of semicrystalline polymers generally involves melt processing, it is still hugely challenging to create high-performance stereocomplexed polylactide (sc-PLA) products from melt-processed high-molecular-weight PLLA/PDLA blends due to the weak crystallization memory effect of stereocomplex (sc) crystallites after complete melting as well as the substantial degradation of PLA chains at elevated melt-processing temperatures of ca. 240–260 °C. Inspired by the concept of powder metallurgy, here we report a new facile route to address these obstacles by sintering of sc-PLA powder at temperatures as low as 180–210 °C, which is distinctly different from traditional sintering of polymer powders performed at temperatures far exceeding their melting temperatures. The enantiomeric PLA chain segments from adjacent powder particles can interdiffuse across particle interfaces and co-crystallize into new sc crystallites capable of tightly welding the interfaces during the low-temperature sintering process, and thus highly transparent sc-PLA products with outstanding heat resistance, mechanical strength, and hydrolytic stability have been successfully fabricated for the first time. PMID:26837848

Powder metallurgy inspired low-temperature fabrication of high-performance stereocomplexed polylactide products with good optical transparency.

PubMed

Bai, Dongyu; Liu, Huili; Bai, Hongwei; Zhang, Qin; Fu, Qiang

2016-02-03

Stereocomplexation between enantiomeric poly(l-lactide) (PLLA) and poly(d-lactide) (PDLA) provides an avenue to greatly enhance performance of eco-friendly polylactide (PLA). Unfortunately, although the manufacturing of semicrystalline polymers generally involves melt processing, it is still hugely challenging to create high-performance stereocomplexed polylactide (sc-PLA) products from melt-processed high-molecular-weight PLLA/PDLA blends due to the weak crystallization memory effect of stereocomplex (sc) crystallites after complete melting as well as the substantial degradation of PLA chains at elevated melt-processing temperatures of ca. 240-260 °C. Inspired by the concept of powder metallurgy, here we report a new facile route to address these obstacles by sintering of sc-PLA powder at temperatures as low as 180-210 °C, which is distinctly different from traditional sintering of polymer powders performed at temperatures far exceeding their melting temperatures. The enantiomeric PLA chain segments from adjacent powder particles can interdiffuse across particle interfaces and co-crystallize into new sc crystallites capable of tightly welding the interfaces during the low-temperature sintering process, and thus highly transparent sc-PLA products with outstanding heat resistance, mechanical strength, and hydrolytic stability have been successfully fabricated for the first time.

The Effectiveness of a NiCrY-Coating on a Powder Metallurgy Disk Superalloy

NASA Technical Reports Server (NTRS)

Gabb, Timothy P.; Miller, Robert A.; Nesbitt, James A.; Draper, Susan L.; Rogers, Richard B.; Telesman, Jack

2018-01-01

Protective ductile coatings could be necessary to mitigate oxidation and corrosion attack on superalloy disks in some turbine engine applications. However, the effects of coatings on fatigue life of the disk during service are an important concern. The objective of this study was to investigate how such a coating could perform after varied post-coating processing. Cylindrical gage fatigue specimens of powder metallurgy-processed disk superalloy LSHR were coated with a NiCrY coating, shot peened, preparation treated, exposed, and then subjected to fatigue at high temperature. The effects of varied shot peening, preparation treatment, and exposures on fatigue life with and without the coating were compared. Each of these variables and several of their interactions significantly influenced fatigue life.

Fatigue Performance of Powder Metallurgy (PM) Ti-6Al-4V Alloy: A Critical Analysis of Current Fatigue Data and Metallurgical Approaches for Improving Fatigue Strength

NASA Astrophysics Data System (ADS)

Cao, Fei; Ravi Chandran, K. S.

2016-03-01

A comprehensive assessment of fatigue performance of powder metallurgy (PM) Ti-6Al-4V alloy, manufactured using various powder-based processing approaches to-date, is performed in this work. The focus is on PM processes that use either blended element (BE) or pre-alloyed (PA) powder as feedstock. Porosity and the microstructure condition have been found to be the two most dominant material variables that control the fatigue strength. The evaluation reveals that the fatigue performance of PM Ti-6Al-4V, in the as-sintered state, is far lower than that in the wrought condition. This is largely caused by residual porosity, even if it is present in small amounts, or, by the coarse lamellar colony microstructure. The fatigue strength is significantly improved by the closure of pores, and it approaches the levels of wrought Ti-6Al-4V alloys, after hot-isostatic-pressing (HIPing). Further thermo-mechanical and heat treatments lead to additional increases in fatigue strength-in one case, a high fatigue strength level, exceeding that of the mill-annealed condition, was achieved. The work identifies the powder, process and microstructure improvements that are necessary for achieving high fatigue strength in powder metallurgical Ti-6Al-4V alloys in order for them to effectively compete with wrought forms. The present findings, gathered from the traditional titanium powder metallurgy, are also directly applicable to additively manufactured titanium, because of the similarities in pores, defects, and microstructures between the two manufacturing processes.

Comparison Study on Additive Manufacturing (AM) and Powder Metallurgy (PM) AlSi10Mg Alloys

NASA Astrophysics Data System (ADS)

Chen, B.; Moon, S. K.; Yao, X.; Bi, G.; Shen, J.; Umeda, J.; Kondoh, K.

2018-02-01

The microstructural and mechanical properties of AlSi10Mg alloys fabricated by additive manufacturing (AM) and powder metallurgy (PM) routes were investigated and compared. The microstructures were examined by scanning electron microscopy assisted with electron-dispersive spectroscopy. The crystalline features were studied by x-ray diffraction and electron backscatter diffraction. Room-temperature tensile tests and Vickers hardness measurements were performed to characterize the mechanical properties. It was found that the AM alloy had coarser Al grains but much finer Si precipitates compared with the PM alloy. Consequently, the AM alloy showed more than 100% increment in strength and hardness compared with the PM alloy due to the presence of ultrafine forms of Si, while exhibiting moderate ductility.

A laboratory means to produce tough aluminum sheet from powder

NASA Technical Reports Server (NTRS)

Singleton, O. R.; Royster, D. M.; Thomas, J. R.

1990-01-01

The rapid solidification of aluminum alloys as powder and the subsequent fabrication processes can be used to develop and tailor alloys to satisfy specific aerospace design requirements, including high strength and toughness. Laboratory procedures to produce aluminum powder-metallurgy (PM) materials are efficient but require evidence that the laboratory methods used can produce a product with superior properties. This paper describes laboratory equipment and procedures which can be used to produce tough aluminum PM sheet. The processing of a 2124 + 0.9 percent Zr aluminum alloy powder is used as an example. The fully hardened sheet product is evaluated in terms of properties and microstructure. The key features of the vacuum hot press pressing operation used to consolidate the powder are described. The 2124 + 0.9 percent Zr - T8 temper aluminum sheet produced was both strong (460-490 MPa yield strength) and tough (Kahn Tear unit-propagation- energy values over three times those typical for ingot metallurgy 2024-T81). Both the longitudinal and longitudinal-transverse directions of the sheet were tested. The microstructure was well refined with subgrains of one or two micrometers. Fine dispersoids of Al3Zr in the precipitate free regions adjacent to boundaries are believed to contribute to the improved toughness.

Critical current densities of Jelly-Roll and powder metallurgy Nb{sub 3}Al wires as a function of temperature and magnetic field

DOE Office of Scientific and Technical Information (OSTI.GOV)

Thieme, C.L.H.; Kim, J.B.; Takayasu, M.

Critical current densities of multi-filamentary Nb{sub 3}Al wire made with the Jelly-Roll process (JR) and mono-core powder metallurgy process (PM) wire were measured as a function of temperature and magnetic field. The temperature dependence of the resistive critical field B{sub c2} was measured in PM wires. There is a significant difference between these resistive B{sub c2} values and the ones determined by Kramer plots. The field dependence of the critical current depends on the manufacturing method. In general, it follows a relationship that falls between pure Kramer and one where the pinning force is inversely proportional with B{sup 2}. Inmore » contrast with Nb{sub 3}Sn no maximum in the bulk pinning force is observed down to 3 T (0.15MxB{sub c2}).« less

Interfacial reactions and wetting in Al-Mg sintered by powder metallurgy process

DOE Office of Scientific and Technical Information (OSTI.GOV)

Faisal, Heny, E-mail: faisal@physics.its.ac.id; Darminto,; Triwikantoro,

2016-04-19

Was conducted to analyze the effect of temperature variation on the bonding interface sintered composite Al-Mg and analyze the effect of variations of the density and hardness sinter. Research carried out by the base material powders of Al, Mg powder and solvent n-butanol. The method used in this study is a powder metallurgy, with a composition of 60% volume fraction of Al - 40% Mg. Al-Mg mixing with n-butanol for 1 hour at 500 rpm. Then the emphasis (cold comression) with a size of 1.4 cm in diameter dies and height of 2.8 cm, is pressed with a force of 20 MPa and heldmore » for 15 minutes. After the sample into pellets, then sintered at various temperatures 300 °C, 350 °C, 400 °C and 450 °C. Characterization is done by using the testing green density, sintered density, X-ray diffraction (XRD), Scanning Electron Microscopy (SEM), vickers microhardness, and press test. XRD data analysis done by using X’Pert High Score Plus (HSP) to determine whether there is a new phase is formed. Test results show that the sintered density increasing sintering temperature, the resulting density is also increasing (shrinkage). However, at a temperature of 450 °C decreased (swelling). With the increased sinter density, interfacial bonding getting Kuta and more compact so that its hardness is also increased. From the test results of SEM / EDX, there Mg into Al in the border area. At temperatures of 300 °C, 350 °C, 400 °C, the phase formed is Al, Mg and MgO. While phase is formed at a temperature of 450 °C is aluminum magnesium (Al{sub 3}Mg{sub 2}), Aluminum Magnesium Zinc (AlMg{sub 2}Zn).« less

Iron's Role in Aluminum: A Powder Metallurgy and Sustainability Approach

NASA Astrophysics Data System (ADS)

Saller, Brandon Dale

cryomilling. With respect to the powder, a differential scanning calorimetry and activation energy analysis elucidated the formation and phase transformation temperatures of the relevant intermetallic phases, and the microstructural factors that influenced them. With an understanding of the fundamental science behind the intermetallic formation in the Al-Fe system, the composition of helium atomized Al-2at.% Fe was chosen combined with high-pressure torsion processing to yield a bulk alloy that demonstrated an ultimate tensile strength of 488 MPa. This strength was achieved via a combination of two mechanisms: grain refinement (Hall-Petch) and dislocation-Al6Fe interactions (Orowan strengthening), with notable thermal stability present up until 450°C. Finally, the potential for Al-Fe as a sustainable alloy was studied and a link established between current environmental literature and metallurgy literature on the potential for incorporation of Fe into Al to create a structural alloy.

Fabrication of Powder Metallurgy Pure Ti Material by Using Thermal Decomposition of TiH2

NASA Astrophysics Data System (ADS)

Mimoto, Takanori; Nakanishi, Nozomi; Umeda, Junko; Kondoh, Katsuyoshi

Titanium (Ti) and titanium alloys have been interested as an engineering material because they are widely used across various industrial applications, for example, motorcycle, automotive and aerospace industries, due to their light weight, high specific strength and superior corrosion resistance. Ti materials are particularly significant for the aircraft using carbon/carbon (C/C) composites, for example, carbon fiber reinforced plastics (CFRP), because Ti materials are free from the problem of contact corrosion between C/C composites. However, the applications of Ti materials are limited because of their high cost. From a viewpoint of cost reduction, cost effective process to fabricate Ti materials is strongly required. In the present study, the direct consolidation of titanium hydride (TiH2) raw powders in solid-state was employed to fabricate pure Ti bulk materials by using thermal decomposition of TiH2. In general, the production cost of Ti components is expensive due to using commercially pure (CP) Ti powders after dehydrogenation. On the other hand, the novel process using TiH2 powders as starting materials is a promising low cost approach for powder metallurgy (P/M) Ti products. Furthermore, this new process is also attractive from a viewpoint of energy saving because the dehydrogenation is integrated into the sintering process. In this study, TiH2 raw powders were directly consolidated by conventional press technique at 600 MPa to prepare TiH2 powder compacted billets. To thermally decompose TiH2 and obtain sintered pure Ti billets, the TiH2 powder billets were heated in the integrated sintering process including dehydrogenation. The hot-extruded pure Ti material, which was heat treated at 1273 K for 180 min in argon gas atmosphere, showed tensile strength of 701.8 MPa and elongation of 27.1%. These tensile properties satisfied the requirements for JIS Ti Grade 4. The relationship between microstructures, mechanical properties response and heat treatment

Toxicology and occupational hazards of new materials and processes in metal surface treatment, powder metallurgy, technical ceramics, and fiber-reinforced plastics.

PubMed

Midtgård, U; Jelnes, J E

1991-12-01

Many new materials and processes are about to find their way from the research laboratory into industry. The present paper describes some of these processes and provides an overview of possible occupational hazards and a list of chemicals used or produced in the processes. The technological areas that are considered are metal surface treatment (ion implantation, physical and chemical vapor deposition, plasma spraying), powder metallurgy, advanced technical ceramics, and fiber-reinforced plastics.

Feasibility study of the production of biomedical Ti-6Al-4V alloy by powder metallurgy.

PubMed

Bolzoni, L; Ruiz-Navas, E M; Gordo, E

2015-04-01

Titanium and its alloys are characterized by an exceptional combination of properties like high strength, good corrosion resistance and biocompatibility which makes them suitable materials for biomedical prosthesis and devices. The wrought Ti-6Al-4V alloy is generally favored in comparison to other metallic biomaterials due to its relatively low elastic modulus and it has been long used to obtain products for biomedical applications. In this work an alternative route to fabricate biomedical implants made out of the Ti-6Al-4V alloy is investigated. Specifically, the feasibility of the conventional powder metallurgy route of cold uniaxial pressing and sintering is addressed by considering two types of powders (i.e. blended elemental and prealloyed). The characterization of physical properties, chemical analysis, mechanical behavior and microstructural analysis is carried out in-depth and the properties are correlated among them. On the base of the results found, the produced alloys are promising materials for biomedical applications as well as cheaper surgical devices and tools. Copyright © 2015 Elsevier B.V. All rights reserved.

Uranium silicide pellet fabrication by powder metallurgy for accident tolerant fuel evaluation and irradiation

DOE PAGES

Harp, Jason Michael; Lessing, Paul Alan; Hoggan, Rita Elaine

2015-06-21

In collaboration with industry, Idaho National Laboratory is investigating uranium silicide for use in future light water reactor fuels as a more accident resistant alternative to uranium oxide base fuels. Specifically this project was focused on producing uranium silicide (U 3Si 2) pellets by conventional powder metallurgy with a density greater than 94% of the theoretical density. This work has produced a process to consistently produce pellets with the desired density through careful optimization of the process. Milling of the U 3Si 2 has been optimized and high phase purity U 3Si 2 has been successfully produced. Results are presentedmore » from sintering studies and microstructural examinations that illustrate the need for a finely ground reproducible particle size distribution in the source powder. The optimized process was used to produce pellets for the Accident Tolerant Fuel-1 irradiation experiment. The average density of these pellets was 11.54 ±0.06 g/cm 3. Additional characterization of the pellets by scaning electron microscopy and X-ray diffraction has also been performed. As a result, pellets produced in this work have been encapsulated for irradiation, and irradiation in the Advanced Test Reactor is expected soon.« less

Uranium silicide pellet fabrication by powder metallurgy for accident tolerant fuel evaluation and irradiation

DOE Office of Scientific and Technical Information (OSTI.GOV)

Harp, Jason Michael; Lessing, Paul Alan; Hoggan, Rita Elaine

In collaboration with industry, Idaho National Laboratory is investigating uranium silicide for use in future light water reactor fuels as a more accident resistant alternative to uranium oxide base fuels. Specifically this project was focused on producing uranium silicide (U 3Si 2) pellets by conventional powder metallurgy with a density greater than 94% of the theoretical density. This work has produced a process to consistently produce pellets with the desired density through careful optimization of the process. Milling of the U 3Si 2 has been optimized and high phase purity U 3Si 2 has been successfully produced. Results are presentedmore » from sintering studies and microstructural examinations that illustrate the need for a finely ground reproducible particle size distribution in the source powder. The optimized process was used to produce pellets for the Accident Tolerant Fuel-1 irradiation experiment. The average density of these pellets was 11.54 ±0.06 g/cm 3. Additional characterization of the pellets by scaning electron microscopy and X-ray diffraction has also been performed. As a result, pellets produced in this work have been encapsulated for irradiation, and irradiation in the Advanced Test Reactor is expected soon.« less

The effect of process parameters in Aluminum Metal Matrix Composites with Powder Metallurgy

NASA Astrophysics Data System (ADS)

Vani, Vemula Vijaya; Chak, Sanjay Kumar

2018-06-01

Metal Matrix Composites are developed in recent years as an alternative over conventional engineering materials due to their improved properties. Among all, Aluminium Matrix Composites (AMCs) are increasing their demand due to low density, high strength-to-weight ratio, high toughness, corrosion resistance, higher stiffness, improved wear resistance, increased creep resistance, low co-efficient of thermal expansion, improved high temperature properties. Major applications of these materials have been in aerospace, automobile, military. There are different processing techniques for the fabrication of AMCs. Powder metallurgy is a one of the most promising and versatile routes for fabrication of particle reinforced AMCs as compared to other manufacturing methods. This method ensures the good wettability between matrix and reinforcement, homogeneous microstructure of the fabricated MMC, and prevents the formation of any undesirable phases. This article addresses mainly on the effect of process parameters like sintering time, temperature and particle size on the microstructure of aluminum metal matrix composites.

Residual Stresses in a NiCrY-Coated Powder Metallurgy Disk Superalloy

NASA Technical Reports Server (NTRS)

Gabb, Timothy P.; Rogers, Richard B.; Nesbitt, James A.; Puleo, Bernadette J.; Miller, Robert A.; Telesman, Ignacy; Draper, Susan L.; Locci, Ivan E.

2017-01-01

Protective ductile coatings will be necessary to mitigate oxidation and corrosion attack on superalloy disks exposed to increasing operating temperatures in some turbine engine environments. However, such coatings must be resistant to harmful surface cracking during service. The objective of this study was to investigate how residual stresses evolve in such coatings. Cylindrical gage fatigue specimens of powder metallurgy-processed disk superalloy LSHR were coated with a NiCrY coating, shot peened, and then subjected to fatigue in air at room and high temperatures. The effects of shot peening and fatigue cycling on average residual stresses and other aspects of the coating were assessed. Shot peening did induce beneficial compressive residual stresses in the coating and substrate. However, these stresses became more tensile in the coating with subsequent heating and contributed to cracking of the coating in long intervals of cycling at 760 C. Substantial compressive residual stresses remained in the substrate adjacent to the coating, sufficient to suppress fatigue cracking. The coating continued to protect the substrate from hot corrosion pitting, even after fatigue cracks initiated in the coating.

Improvement of the mechanical properties and corrosion resistance of biodegradable β-Ca3(PO4)2/Mg-Zn composites prepared by powder metallurgy: the adding β-Ca3(PO4)2, hot extrusion and aging treatment.

PubMed

Yan, Yang; Kang, Yijun; Li, Ding; Yu, Kun; Xiao, Tao; Deng, Youwen; Dai, Han; Dai, Yilong; Xiong, Hanqing; Fang, Hongjie

2017-05-01

In this study, 10%β-Ca 3 (PO 4 ) 2 /Mg-6%Zn (wt.%) composites with Mg-6%Zn alloy as control were prepared by powder metallurgy. After hot extrusion, the as-extruded composites were aged for 72h at 150°C. The effects of the adding β-Ca 3 (PO 4 ) 2 , hot extrusion and aging treatment on their microstructure, mechanical properties and corrosion resistance were investigated. The XRD results identified α-Mg, MgZn phase and β-Ca 3 (PO 4 ) 2 phase in these composites. After hot extrusion, grains were significantly refined, and the larger-sized β-Ca 3 (PO 4 ) 2 particles and coarse MgZn phases were broken into linear-distributed β-Ca 3 (PO 4 ) 2 and MgZn phases along the extrusion direction. After aging treatment, the elements of Zn, Ca, P and O presented a more homogeneous distribution. The compressive strengths of the β-Ca 3 (PO 4 ) 2 /Mg-Zn composites were approximately double those of natural bone, and their densities and elastic moduli matched those of natural bone. The immersion tests and electrochemical tests revealed that the adding β-Ca 3 (PO 4 ) 2 , hot extrusion and aging treatment could promote the formation of protective corrosion product layer on the sample surface in Ringer's solution, which improved corrosion resistance of the β-Ca 3 (PO 4 ) 2 /Mg-Zn composites. The XRD results indicated that the corrosion product layer contained Mg(OH) 2 , β-Ca 3 (PO 4 ) 2 and hydroxyapatite (HA). The cytotoxicity assessments showed the as-extruded β-Ca 3 (PO 4 ) 2 /Mg-Zn composite aged for 72h was harmless to L-929 cells. These results suggested that the β-Ca 3 (PO 4 ) 2 /Mg-Zn composites prepared by powder metallurgy were promising to be used for bone tissue engineering. Copyright © 2017 Elsevier B.V. All rights reserved.

Powder Metallurgy of Uranium Alloy Fuels for TRU-Burning Reactors Final Technical Report

DOE Office of Scientific and Technical Information (OSTI.GOV)

McDeavitt, Sean M

2011-04-29

Overview Fast reactors were evaluated to enable the transmutation of transuranic isotopes generated by nuclear energy systems. The motivation for this was that TRU isotopes have high radiotoxicity and relatively long half-lives, making them unattractive for disposal in a long-term geologic repository. Fast reactors provide an efficient means to utilize the energy content of the TRUs while destroying them. An enabling technology that requires research and development is the fabrication metallic fuel containing TRU isotopes using powder metallurgy methods. This project focused upon developing a powder metallurgical fabrication method to produce U-Zr-transuranic (TRU) alloys at relatively low processing temperatures (500ºCmore » to 600ºC) using either hot extrusion or alpha-phase sintering for charecterization. Researchers quantified the fundamental aspects of both processing methods using surrogate metals to simulate the TRU elements. The process produced novel solutions to some of the issues relating to metallic fuels, such as fuel-cladding chemical interactions, fuel swelling, volatility losses during casting, and casting mold material losses. Workscope There were two primary tasks associated with this project: 1. Hot working fabrication using mechanical alloying and extrusion • Design, fabricate, and assemble extrusion equipment • Extrusion database on DU metal • Extrusion database on U-10Zr alloys • Extrusion database on U-20xx-10Zr alloys • Evaluation and testing of tube sheath metals 2. Low-temperature sintering of U alloys • Design, fabricate, and assemble equipment • Sintering database on DU metal • Sintering database on U-10Zr alloys • Liquid assisted phase sintering on U-20xx-10Zr alloys Appendices Outline Appendix A contains a Fuel Cycle Research & Development (FCR&D) poster and contact presentation where TAMU made primary contributions. Appendix B contains MSNE theses and final defense presentations by David Garnetti and Grant

Machinability of Green Powder Metallurgy Components: Part I. Characterization of the Influence of Tool Wear

NASA Astrophysics Data System (ADS)

Robert-Perron, Etienne; Blais, Carl; Pelletier, Sylvain; Thomas, Yannig

2007-06-01

The green machining process is an interesting approach for solving the mediocre machining behavior of high-performance powder metallurgy (PM) steels. This process appears as a promising method for extending tool life and reducing machining costs. Recent improvements in binder/lubricant technologies have led to high green strength systems that enable green machining. So far, tool wear has been considered negligible when characterizing the machinability of green PM specimens. This inaccurate assumption may lead to the selection of suboptimum cutting conditions. The first part of this study involves the optimization of the machining parameters to minimize the effects of tool wear on the machinability in turning of green PM components. The second part of our work compares the sintered mechanical properties of components machined in green state with other machined after sintering.

Crack Formation in Powder Metallurgy Carbon Nanotube (CNT)/Al Composites During Post Heat-Treatment

NASA Astrophysics Data System (ADS)

Chen, Biao; Imai, Hisashi; Li, Shufeng; Jia, Lei; Umeda, Junko; Kondoh, Katsuyoshi

2015-12-01

After the post heat-treatment (PHT) process of powder metallurgy carbon nanotubes (CNT)/Al composites, micro-cracks were observed in the composites, leading to greatly degraded mechanical properties. To understand and suppress the crack formation, an in situ observation of CNT/Al composites was performed at elevated temperatures. PHT was also applied to various bulk pure Al and CNT/Al composites fabricated under different processes. It was observed that the composites consolidated by hot-extrusion might form micro-cracks, but those consolidated by spark plasma sintering (SPS) showed no crack after PHT. A high-temperature SPS process before hot-extrusion was effective to prevent crack formation. The release of residual stress in severe plastic deformed (SPD) materials was responsible for the cracking phenomena during the PHT process. Furthermore, a good particle bonding was essential and effective to suppress cracks for SPD materials in the PHT process.

Microstructure, mechanical behavior and biocompatibility of powder metallurgy Nb-Ti-Ta alloys as biomedical material.

PubMed

Liu, Jue; Chang, Lin; Liu, Hairong; Li, Yongsheng; Yang, Hailin; Ruan, Jianming

2017-02-01

Microstructures, mechanical properties, apatite-forming ability and in vitro experiments were studied for Nb-25Ti-xTa (x=10, 15, 20, 25, 35at.%) alloys fabricated by powder metallurgy. It is confirmed that the alloys could achieve a relative density over 80%. Meanwhile, the increase in Ta content enhances the tensile strength, elastic modulus and hardness of the as-sintered alloys. When increasing the sintering temperatures, the microstructure became more homogeneous for β phase, resulting in a decrease in the modulus and strength. Moreover, the alloys showed a good biocompatibility due to the absence of cytotoxic elements, and were suitable for apatite formation and cell adhesion. In conclusion, Nb-25Ti-xTa alloys are potentially useful in biomedical applications with their mechanical and biological properties being evaluated in this work. Copyright © 2016 Elsevier B.V. All rights reserved.

Power metallurgy approaches to high temperature components for gas turbine engines

NASA Technical Reports Server (NTRS)

Probst, H. B.

1974-01-01

Work conducted by NASA and NASA contractors on prealloyed superalloy powders and materials strengthened by oxide dispersion is reviewed. Fabrication, tensile strength, superplasticity, grain growth control, stress rupture life, and grain-size and dispersion-level effects are covered. Distinct strength advantages of powder metallurgy superalloys over conventional wrought alloys are noted.

Data on processing of Ti-25Nb-25Zr β-titanium alloys via powder metallurgy route: Methodology, microstructure and mechanical properties.

PubMed

Ueda, D; Dirras, G; Hocini, A; Tingaud, D; Ameyama, K; Langlois, P; Vrel, D; Trzaska, Z

2018-04-01

The data presented in this article are related to the research article entitled "Cyclic Shear behavior of conventional and harmonic structure-designed Ti-25Nb-25Zr β-titanium alloy: Back-stress hardening and twinning inhibition" (Dirras et al., 2017) [1]. The datasheet describes the methods used to fabricate two β-titanium alloys having conventional microstructure and so-called harmonic structure (HS) design via a powder metallurgy route, namely the spark plasma sintering (SPS) route. The data show the as-processed unconsolidated powder microstructures as well as the post-SPS ones. The data illustrate the mechanical response under cyclic shear loading of consolidated alloy specimens. The data show how electron back scattering diffraction(EBSD) method is used to clearly identify induced deformation features in the case of the conventional alloy.

Initial Assessment of the Effects of Nonmetallic Inclusions on Fatigue Life of Powder-Metallurgy-Processed Udimet(TM) 720

NASA Technical Reports Server (NTRS)

Gabb, T. P.; Telesman, J.; Kantzos, P. T.; Bonacuse, P. J.; Barrie, R. L.

2002-01-01

The fatigue lives of modern powder metallurgy (PM) disk alloys are influenced by variabilities in alloy microstructure and mechanical properties. These properties can vary due to the different steps of materials/component processing and machining. One of these variables, the presence of nonmetallic inclusions, has been shown to significantly degrade low-cycle fatigue (LCF) life. Nonmetallic inclusions are inherent defects in powder alloys that are a by-product of powder-processing techniques. Contamination of the powder can occur in the melt, during powder atomization, or during any of the various handling processes through consolidation. In modern nickel disk powder processing facilities, the levels of inclusion contamination have been reduced to less than 1 part per million by weight. Despite the efforts of manufacturers to ensure the cleanliness of their powder production processes, the presence of inclusions remains a source of great concern for the designer. the objective of this study was to investigate the effects on fatigue life of these inclusions. Since natural inclusions occur so infrequently, elevated levels of inclusions were carefully introduced in a nickel-based disk superalloy, Udimet 720 (registered trademark of Special Metals Corporation), produced using PM processing. Multiple strain-controlled fatigue tests were then performed on this material at 650 C. Analyses were performed to compare the LCF lives and failure initiation sites as functions of inclusion content and fatigue conditions. A large majority of the failures in specimens with introduced inclusions occurred at cracks initiating from inclusions at the specimen surface. The inclusions could reduce fatigue life by up to 100 times. These effects were found to be dependent on strain range and strain ratio. Tests at lower strain ranges and higher strain ratios produced larger effects of inclusions on life.

Application of powder metallurgy techniques to produce improved bearing elements for liquid rocket engines

NASA Technical Reports Server (NTRS)

Moracz, D. J.; Shipley, R. J.; Moxson, V. S.; Killman, R. J.; Munson, H. E.

1992-01-01

The objective was to apply powder metallurgy techniques for the production of improved bearing elements, specifically balls and races, for advanced cryogenic turbopump bearings. The materials and fabrication techniques evaluated were judged on the basis of their ability to improve fatigue life, wear resistance, and corrosion resistance of Space Shuttle Main Engine (SSME) propellant bearings over the currently used 440C. An extensive list of candidate bearing alloys in five different categories was considered: tool/die steels, through hardened stainless steels, cobalt-base alloys, and gear steels. Testing of alloys for final consideration included hardness, rolling contact fatigue, cross cylinder wear, elevated temperature wear, room and cryogenic fracture toughness, stress corrosion cracking, and five-ball (rolling-sliding element) testing. Results of the program indicated two alloys that showed promise for improved bearing elements. These alloys were MRC-2001 and X-405. 57mm bearings were fabricated from the MRC-2001 alloy for further actual hardware rig testing by NASA-MSFC.

Microstructural investigation of aluminum-graphene nano platelets composites prepared by powder metallurgy

NASA Astrophysics Data System (ADS)

Sreearravind, M.; Peddavarapu, Sreehari; Raghuraman, S.

2018-04-01

Recently, Graphene has attracted a large variety of scientific communities due to its inimitable properties. Typically, Graphene Nanoplatelets (GNPs) are ideal reinforcements for the production of nanocomposites due to its excellent mechanical properties for strength enhancement. This paper reports the Aluminum-Graphene Nanoplatelets (Al/GNPs) composites synthesized through powder metallurgy method. The microstructural investigation was carried out to study the GNPs integration on the Al matrix. For this study, the samples Al-2wt% GNPs, Al-3wt% GNPs and Al- 4wt% GNPs are high-energy ball milled at 200rpm and sintered at 500°C,550°C, and 600°C. Microstructural characterization is carried out with optical microscopy, Scanning electron microscopy. Rockwell hardness test is conducted to evaluate the hardness behavior in Al/GNPs. Microstructural analysis revealed the homogeneous dispersion of GNPs in the Al matrix in all the samples. It is observed that the existence of the graphene nanoparticles and the rise of their concentrations in the aluminum matrix (2 wt.% to 4 wt.%) as reinforcement in addition to rising the sintering temperature (450°C to 600°C) greatly improve the mechanical properties of Al/GNPs composites.

Mechanical strength and thermophysical properties of PM212: A high temperature self-lubricating powder metallurgy composite

NASA Technical Reports Server (NTRS)

Edwards, Phillip M.; Sliney, Harold E.; Dellacorte, Christopher; Whittenberger, J. Daniel; Martineau, Robert R.

1990-01-01

A powder metallurgy composite, PM212, composed of metal bonded chromium carbide and solid lubricants is shown to be self-lubricating to a maximum application temperature of 900 C. The high temperature compressive strength, tensile strength, thermal expansion and thermal conductivity data needed to design PM212 sliding contact bearings and seals are reported for sintered and isostatically pressed (HIPed) versions of PM212. Other properties presented are room temperature density, hardness, and elastic modulus. In general, both versions appear to have adequate strength to be considered as sliding contact bearing materials, but the HIPed version, which is fully dense, is much stronger than the sintered version which contains about 20 percent pore volume. The sintered material is less costly to make, but the HIPed version is better where high compressive strength is important.

Corrosion inhibition of powder metallurgy Mg by fluoride treatments.

PubMed

Pereda, M D; Alonso, C; Burgos-Asperilla, L; del Valle, J A; Ruano, O A; Perez, P; Fernández Lorenzo de Mele, M A

2010-05-01

Pure Mg has been proposed as a potential degradable biomaterial to avoid both the disadvantages of non-degradable internal fixation implants and the use of alloying elements that may be toxic. However, it shows excessively high corrosion rate and insufficient yield strength. The effects of reinforcing Mg by a powder metallurgy (PM) route and the application of biocompatible corrosion inhibitors (immersion in 0.1 and 1M KF solution treatments, 0.1M FST and 1M FST, respectively) were analyzed in order to improve Mg mechanical and corrosion resistance, respectively. Open circuit potential measurements, polarization techniques (PT), scanning electrochemical microscopy (SECM) and electrochemical impedance spectroscopy (EIS) were performed to evaluate its corrosion behavior. SECM showed that the local current of attacked areas decreased during the F(-) treatments. The corrosion inhibitory action of 0.1M FST and 1M FST in phosphate buffered solution was assessed by PT and EIS. Under the experimental conditions assayed, 0.1M FST revealed better performance. X-ray photoelectron spectroscopy, energy dispersive X-ray and X-ray diffraction analyses of Mg(PM) with 0.1M FST showed the presence of KMgF(3) crystals on the surface while a MgF(2) film was detected for 1M FST. After fluoride inhibition treatments, promising results were observed for Mg(PM) as degradable metallic biomaterial due to its higher yield strength and lower initial corrosion rate than untreated Mg, as well as a progressive loss of the protective characteristics of the F(-)-containing film which ensures the gradual degradation process. Copyright (c) 2009 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

Advanced Mechanical Properties of a Powder Metallurgy Ti-Al-N Alloy Doped with Ultrahigh Nitrogen Concentration

NASA Astrophysics Data System (ADS)

Shen, J.; Chen, B.; Umeda, J.; Kondoh, K.

2018-03-01

Titanium and its alloys are recognized for their attractive properties. However, high-performance Ti alloys are often alloyed with rare or noble-metal elements. In the present study, Ti alloys doped with only ubiquitous elements were produced via powder metallurgy. The experimental results showed that pure Ti with 1.5 wt.% AlN incorporated exhibited excellent tensile properties, superior to similarly extruded Ti-6Al-4V. Further analysis revealed that its remarkably advanced strength could primarily be attributed to nitrogen solid-solution strengthening, accounting for nearly 80% of the strength increase of the material. In addition, despite the ultrahigh nitrogen concentration up to 0.809 wt.%, the Ti-1.5AlN sample showed elongation to failure of 10%. This result exceeds the well-known limitation for nitrogen (over 0.45 wt.%) that causes embrittlement of Ti alloys.

Characterisation of titanium-titanium boride composites processed by powder metallurgy techniques

DOE Office of Scientific and Technical Information (OSTI.GOV)

Selva Kumar, M., E-mail: sel_mcet@yahoo.co.in; Chandrasekar, P.; Chandramohan, P.

2012-11-15

In this work, a detailed characterisation of titanium-titanium boride composites processed by three powder metallurgy techniques, namely, hot isostatic pressing, spark plasma sintering and vacuum sintering, was conducted. Two composites with different volume percents of titanium boride reinforcement were used for the investigation. One was titanium with 20% titanium boride, and the other was titanium with 40% titanium boride (by volume). Characterisation was performed using X-ray diffraction, electron probe micro analysis - energy dispersive spectroscopy and wavelength dispersive spectroscopy, image analysis and scanning electron microscopy. The characterisation results confirm the completion of the titanium boride reaction. The results reveal themore » presence of titanium boride reinforcement in different morphologies such as needle-shaped whiskers, short agglomerated whiskers and fine plates. The paper also discusses how mechanical properties such as microhardness, elastic modulus and Poisson's ratio are influenced by the processing techniques as well as the volume fraction of the titanium boride reinforcement. - Highlights: Black-Right-Pointing-Pointer Ti-TiB composites were processed by HIP, SPS and vacuum sintering. Black-Right-Pointing-Pointer The completion of Ti-TiB{sub 2} reaction was confirmed by XRD, SEM and EPMA studies. Black-Right-Pointing-Pointer Hardness and elastic properties of Ti-TiB composites were discussed. Black-Right-Pointing-Pointer Processing techniques were compared with respect to their microstructure.« less

Factors Influencing Dwell Fatigue Cracking in Notches of Powder Metallurgy Superalloys

NASA Technical Reports Server (NTRS)

Gabb, T. P.; Telesman, J.; Ghosn, L.; Garg, A.; Gayda, J.

2011-01-01

The influences of heat treatment and cyclic dwells on the notch fatigue resistance of powder metallurgy disk superalloys were investigated for low solvus high refractory (LSHR) and ME3 disk alloys. Disks were processed to produce material conditions with varied microstructures and associated mechanical properties. Notched specimens were first subjected to baseline dwell fatigue cycles having a dwell at maximum load, as well as tensile, stress relaxation, creep rupture, and dwell fatigue crack growth tests at 704 C. Several material heat treatments displayed a bimodal distribution of fatigue life with the lives varying by two orders-of-magnitude, while others had more consistent fatigue lives. This response was compared to other mechanical properties, in search of correlations. The wide scatter in baseline dwell fatigue life was observed only for material conditions resistant to stress relaxation. For selected materials and conditions, additional tests were then performed with the dwells shifted in part or in total to minimum tensile load. The tests performed with dwells at minimum load exhibited lower fatigue lives than max dwell tests, and also exhibited early crack initiation and a substantial increase in the number of initiation sites. These results could be explained in part by modeling evolution of peak stresses in the notch with continued dwell fatigue cycling. Fatigue-environment interactions were determined to limit life for the fatigue cycles with dwells.

Distribution of Inclusion-Initiated Fatigue Cracking in Powder Metallurgy Udimet 720 Characterized

NASA Technical Reports Server (NTRS)

Bonacuse, Peter J.; Kantzos, Pete T.; Barrie, Robert; Telesman, Jack; Ghosn, Louis J.; Gabb, Timothy P.

2004-01-01

In the absence of extrinsic surface damage, the fatigue life of metals is often dictated by the distribution of intrinsic defects. In powder metallurgy (PM) alloys, relatively large defects occur rarely enough that a typical characterization with a limited number of small volume fatigue test specimens will not adequately sample inclusion-initiated damage. Counterintuitively, inclusion-initiated failure has a greater impact on the distribution in PM alloy fatigue lives because they tend to have fewer defects than their cast and wrought counterparts. Although the relative paucity of defects in PM alloys leads to higher mean fatigue lives, the distribution in observed lives tends to be broader. In order to study this important failure initiation mechanism without expending an inordinate number of specimens, a study was undertaken at the NASA Glenn Research Center where known populations of artificial inclusions (seeds) were introduced to production powder. Fatigue specimens were machined from forgings produced from the seeded powder. Considerable effort has been expended in characterizing the crack growth rate from inclusion-initiated cracks in seeded PM alloys. A rotating and translating positioning system, with associated software, was devised to map the surface inclusions in low-cycle fatigue (LCF) test bars and to monitor the crack growth from these inclusions. The preceding graph illustrates the measured extension in fatigue cracks from inclusions on a seeded LCF test bar subjected to cyclic loading at a strain range of 0.8 percent and a strain ratio (max/min) of zero. Notice that the observed inclusions fall into three categories: some do not propagate at all (arrest), some propagate with a decreasing crack growth rate, and a few propagate at increasing rates that can be modeled by fracture mechanics. The following graph shows the measured inclusion-initiated crack growth rates from 10 interrupted LCF tests plotted against stress intensities calculated for semi

The substitution of nickel for cobalt in hot isostatically pressed powder metallurgy UDIMET 700 alloys

NASA Technical Reports Server (NTRS)

Harf, F. H.

1985-01-01

Nickel was substituted in various proportions for cobalt in a series of five hot-isostatically-pressed powder metallurgy alloys based on the UDIMET 700 composition. These alloys were given 5-step heat treatments appropriate for use in turbine engine disks. The resultant microstructures displayed three distinct sizes of gamma-prime particles in a gamma matrix. The higher cobalt-content alloys contained larger amounts of the finest gamma-prime particles, and had the lowest gamma-gamma-prime lattice mismatch. While all alloys had approximately the same tensile properties at 25 and 650 gamma C, the rupture lives at 650 and 760 C peaked in the alloys with cobalt contents between 12.7 and 4.3 pct. Minimum creep rates increased as cobalt contents were lowered, suggesting their correlation with the gamma-prime particle size distribution and the gamma-gamma-prime mismatch. It was also found that, on overaging at temperatures higher than suitable for turbine disk use, the high cobalt-content alloys were prone to sigma phase formation.

Study on titanium-magnesium composites with bicontinuous structure fabricated by powder metallurgy and ultrasonic infiltration.

PubMed

Jiang, S; Huang, L J; An, Q; Geng, L; Wang, X J; Wang, S

2018-05-01

Titanium-magnesium (Ti-Mg) composites with bicontinuous structure have been successfully fabricated by powder metallurgy and ultrasonic infiltration for biomaterial potential. In the composites, Ti phase is distributed continuously by sintering necks, while Mg phase is also continuous, distributing at the interconnected pores surrounding the Ti phase. The results showed that the fabricated Ti-Mg composites exhibited low modulus and high strength, which are very suitable for load bearing biomedical materials. The composites with 100 µm and 230 µm particle sizes exhibited Young's modulus of 37.6 GPa and 23.4 GPa, 500.7 MPa and 340 MPa of compressive strength and 631.5 MPa and 375.2 MPa of bending strength, respectively. Moreover, both of the modulus and strength of the composites increase with decreasing of Ti particle sizes. In vitro study has been done for the preliminary evaluation of the Ti-Mg composites. Copyright © 2018 Elsevier Ltd. All rights reserved.

Applying Massively Parallel Kinetic Monte Carlo Methods to Simulate Grain Growth and Sintering in Powdered Metals

DTIC Science & Technology

2011-09-01

Structure Evolution During Sintering From [19]. ...................................20 Figure 10. Ising Model Configuration With Eight Nearest Neighbors...INTRODUCTION A. MOTIVATION The ability to fabricate structural components from metals with a fine (micron- sized), controlled grain size is one of the...hallmarks of modern, structural metallurgy. Powder metallurgy, in particular, consists of powder manufacture, powder blending, compacting, and sintering

Phase evolution, mechanical and corrosion behavior of Fe(100-x) Ni(x) alloys synthesized by powder metallurgy

NASA Astrophysics Data System (ADS)

Singh, Neera; Parkash, Om; Kumar, Devendra

2018-03-01

In the present investigation, Fe(100-x) Ni(x) alloys (x = 10, 20, 30, 40 and 50 wt%) were synthesized through the evolution of γ-taenite and α-kamacite phases by powder metallurgy route using commercially available Fe and Ni powders. Mechanically mixed powders of Fe and Ni were compacted at room temperature and sintered at three different temperatures 1000, 1200 and 1250 °C for 1 h. Both Ni concentration and sintering temperature have shown a strong impact on the phase formation, tribological and electrochemical behavior. Micro structural study has shown the formation of taenite (γ-Fe,Ni) and kamacite (α-Fe,Ni) phases in the sintered specimens. An increase in Ni fraction resulted in formation of more taenite which reduces hardness and wear resistance of specimens. Increasing the sintering temperature decreased the defect concentration with enhanced taenite formation, aiding to higher densification. Taenite formed completely in Fe50Ni50 after sintering at 1250 °C. Tribological test revealed the maximum wear resistance for Fe70Ni30 specimen due to the presence of both kamacite and taenite in significant proportions. The formation of taenite as well as the decrease in defect concentration improves the corrosion resistance of the specimens significantly in 1M HCl solution. A maximum corrosion protection efficiency of around ∼87% was achieved in acidic medium for Fe50Ni50, sintered at 1250 °C.

Evaluation of the mechanical properties of powder metallurgy Ti-6Al-7Nb alloy.

PubMed

Bolzoni, L; Ruiz-Navas, E M; Gordo, E

2017-03-01

Titanium and its alloys are common biomedical materials owing to their combination of mechanical properties, corrosion resistance and biocompatibility. Powder metallurgy (PM) techniques can be used to fabricate biomaterials with tailored properties because changing the processing parameters, such as the sintering temperature, products with different level of porosity and mechanical performances can be obtained. This study addresses the production of the biomedical Ti-6Al-7Nb alloy by means of the master alloy addition variant of the PM blending elemental approach. The sintering parameters investigated guarantee that the complete diffusion of the alloying elements and the homogenization of the microstructure is achieved. The sintering of the Ti-6Al-7Nb alloy induces a total shrinkage between 7.4% and 10.7% and the level of porosity decreases from 6.2% to 4.7% with the increment of the sintering temperature. Vickers hardness (280-300 HV30) and tensile properties (different combination of strength and elongation around 900MPa and 3%) are achieved. Copyright © 2016 Elsevier Ltd. All rights reserved.

History of ``NANO''-Scale VERY EARLY Solid-State (and Liquid-State) Physics/Chemistry/Metallurgy/ Ceramics; Interstitial-Alloys Carbides/Nitrides/Borides/...Powders and Cermets, Rock Shocks, ...

NASA Astrophysics Data System (ADS)

Maiden, Colin; Siegel, Edward

History of ``NANO'': Siegel-Matsubara-Vest-Gregson[Mtls. Sci. and Eng. 8, 6, 323(`71); Physica Status Solidi (a)11,45(`72)] VERY EARLY carbides/nitrides/borides powders/cermets solid-state physics/chemistry/metallurgy/ ceramics FIRST-EVER EXPERIMENTAL NANO-physics/chemistry[1968 ->Physica Status Solidi (a)11,45(`72); and EARLY NANO-``physics''/NANO-``chemistry'' THEORY(after: Kubo(`62)-Matsubara(`60s-`70s)-Fulde (`65) [ref.: Sugano[Microcluster-Physics, Springer('82 `98)

In vitro degradation and cytotoxicity of Mg/Ca composites produced by powder metallurgy.

PubMed

Zheng, Y F; Gu, X N; Xi, Y L; Chai, D L

2010-05-01

Mg/Ca (1 wt.%, 5 wt.%, 10 wt.% Ca) composites were prepared from pure magnesium and calcium powders using the powder metallurgy method, aiming to enlarge the addition of Ca content without the formation of Mg(2)Ca. The microstructures, mechanical properties and cytotoxicities of Mg/Ca composite samples were investigated. The corrosion of Mg/Ca composites in Dulbecco's modified Eagle's medium (DMEM) for various immersion intervals was studied by electrochemical impedance spectroscopy measurements and environmental scanning electron microscope, with the concentrations of released Mg and Ca ions in DMEM for various immersion time intervals being measured. It was shown that the main constitutional phases were Mg and Ca, which were uniformly distributed in the Mg matrix. The ultimate tensile strength (UTS) and elongation of experimental composites decreased with increasing Ca content, and the UTS of Mg/1Ca composite was comparable with that of as-extruded Mg-1Ca alloy. The corrosion potential increased with increasing Ca content, whereas the current density and the impedance decreased. It was found that the protective surface film formed quickly at the initial immersion stage. With increasing immersion time, the surface film became compact, and the corrosion rate of Mg/Ca composites slowed down. The surface film consisted mainly of CaCO(3), MgCO(3)x3H(2)O, HA and Mg(OH)(2) after 72 h immersion in DMEM. Mg/1Ca and Mg/5Ca composite extracts had no significant toxicity (p>0.05) to L-929 cells, whereas Mg/10Ca composite extract induced approximately 40% reduced cell viability. Copyright (c) 2009 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

Porous titanium obtained by a new powder metallurgy technique: Preliminary results of human osteoblast adhesion on surface polished substrates.

PubMed

Biasotto, M; Ricceri, R; Scuor, N; Schmid, C; Sandrucci, M A; Di Lenarda, R; Matteazzi, P

2003-01-01

This study concerns a novel powder metallurgy method for producing porous titanium (pTi) exhibiting high mechanical properties. The preparation procedure consisted of the following stages: first, the preparation of Ti and titanium hydride (TiH2) powder mixtures and their consolidation with a cold isostatic press, followed by a sintering of the green bodies performed with hot isostatic press (HIP) equipment. Thermal decomposition in controlled environment of the TiH2 phase results in the foam structure. The resulting porosity percolates with a volume fraction of approximately 20%. The final material exhibits interesting mechanical properties, comparable to those of full density titanium (between grade 2 and grade 3), with the advantage of a minor density. The samples produced were tested to verify their biological response by studying the effectiveness of osteoblast adhesion and growth. In this preliminary study, osteoblastic cell morphology was investigated and compared to that observed on fully dense commercially pure titanium (Ti-cp) (ASTM, grade 3). The preliminary results were promising regarding cellular adhesion and spreading. (Journal of Applied Biomaterials & Biomechanics 2003; 1: 172-7).

An application of powder metallurgy to dentistry.

PubMed

Oda, Y; Ueno, S; Kudoh, Y

1995-11-01

Generally, the dental casting method is used to fabricate dental prostheses made with metal. The method of fabricating dental prostheses from sintered titanium alloy has certain advantages: the elimination of casting defects, a sintering temperature that is lower than the melting point, and a shorter processing time. By examining (1) the properties of green, sintered compacts of titanium powder, (2) the effects of adding aluminum powder on the properties of green, sintered compacts of Ti-Al compound, and (3) the effects of adding copper powder on the properties of green, sintered compacts of Ti-Al-Cu compound, the authors developed a sintered titanium alloy on a trial basis. Because the properties satisfied the requirements of dental restorations, a powder metallurgical method of making dental restorations from this sintered titanium alloy was devised. Applications of such sintered titanium alloys for the metal coping of metal-ceramic crowns and denture base plates were discussed.

Effects of Temperature and Pressure of Hot Isostatic Pressing on the Grain Structure of Powder Metallurgy Superalloy

PubMed Central

Tan, Liming; He, Guoai; Liu, Feng; Li, Yunping; Jiang, Liang

2018-01-01

The microstructure with homogeneously distributed grains and less prior particle boundary (PPB) precipitates is always desired for powder metallurgy superalloys after hot isostatic pressing (HIPping). In this work, we studied the effects of HIPping parameters, temperature and pressure on the grain structure in PM superalloy FGH96, by means of scanning electron microscope (SEM), electron backscatter diffraction (EBSD), transmission electron microscope (TEM) and Time-of-flight secondary ion spectrometry (ToF-SIMS). It was found that temperature and pressure played different roles in controlling PPB precipitation and grain structure during HIPping, the tendency of grain coarsening under high temperature could be inhibited by increasing HIPping pressure which facilitates the recrystallization. In general, relatively high temperature and pressure of HIPping were preferred to obtain an as-HIPped superalloy FGH96 with diminished PPB precipitation and homogeneously refined grains. PMID:29495312

Effects of Temperature and Pressure of Hot Isostatic Pressing on the Grain Structure of Powder Metallurgy Superalloy.

PubMed

Tan, Liming; He, Guoai; Liu, Feng; Li, Yunping; Jiang, Liang

2018-02-24

The microstructure with homogeneously distributed grains and less prior particle boundary (PPB) precipitates is always desired for powder metallurgy superalloys after hot isostatic pressing (HIPping). In this work, we studied the effects of HIPping parameters, temperature and pressure on the grain structure in PM superalloy FGH96, by means of scanning electron microscope (SEM), electron backscatter diffraction (EBSD), transmission electron microscope (TEM) and Time-of-flight secondary ion spectrometry (ToF-SIMS). It was found that temperature and pressure played different roles in controlling PPB precipitation and grain structure during HIPping, the tendency of grain coarsening under high temperature could be inhibited by increasing HIPping pressure which facilitates the recrystallization. In general, relatively high temperature and pressure of HIPping were preferred to obtain an as-HIPped superalloy FGH96 with diminished PPB precipitation and homogeneously refined grains.

The effect of annealing temperature on the properties of powder metallurgy processed Ti-35Nb-2Zr-0.5O alloy.

PubMed

Málek, Jaroslav; Hnilica, František; Veselý, Jaroslav; Smola, Bohumil; Medlín, Rostislav

2017-11-01

Ti-35Nb-2Zr-0.5O (wt%) alloy was prepared via a powder metallurgy process (cold isostatic pressing of blended elemental powders and subsequent sintering) with the primary aim of using it as a material for bio-applications. Sintered specimens were swaged and subsequently the influence of annealing temperature on the mechanical and structural properties was studied. Specimens were annealed at 800, 850, 900, 950, and 1000°C for 0.5h and water quenched. Significant changes in microstructure (i.e. precipitate dissolution or grain coarsening) were observed in relation to increasing annealing temperature. In correlation with those changes, the mechanical properties were also studied. The ultimate tensile strength increased from 925MPa (specimen annealed at 800°C) to 990MPa (900°C). Also the elongation increased from ~ 13% (800°C) to more than 20% (900, 950, and 1000°C). Copyright © 2017 Elsevier Ltd. All rights reserved.

Strain Hardening Behaviour and Its Effect on Properties of ZrB2 Reinforced Al Composite Prepared by Powder Metallurgy Technique

NASA Astrophysics Data System (ADS)

Kaku, Sai Mahesh Yadav; Khanra, Asit Kumar; Davidson, M. J.

2018-04-01

Strain hardening behaviour has significant effect on altering the properties of materials. In the present study, Al-ZrB2 metal matrix composites are made through powder metallurgy route. Incremental weight percentage (wt%) of ZrB2 (0, 2, 4 and 6 wt%) are added to Aluminium matrix to produce different composites. The homogenous powder mixture is compacted and pressurelessly sintered. Sintering of composites is performed over a range of 450-575 °C. The optimized sintered condition is observed at 550 °C for 1 h in controlled atmosphere (argon gas flow). The sintered compacts are strained in incremental steps in different levels up to failure. A visible crack on the bulge of the powder preform is considered as the failure. Composites are strain hardened up to failure. To evaluate the effect of temperature on strain hardening, strain hardening is carried out at different temperatures. Composites are densified with the extent of straining and hardness increases with the increase of strain. Hardness increase with the increase in temperature is maintained during strain hardening. To evaluate the corrosion behaviour of Al-ZrB2 composite, potentiodynamic polarization study are performed on the strained composites. Corrosion rate decrease with the extent of straining.

Application of Box-Behnken Design and Response Surface Methodology for Surface Roughness Prediction Model of CP-Ti Powder Metallurgy Components Through WEDM

NASA Astrophysics Data System (ADS)

Das, Arunangsu; Sarkar, Susenjit; Karanjai, Malobika; Sutradhar, Goutam

2018-04-01

The present work was undertaken to investigate and characterize the machining parameters (such as surface roughness, etc.) of uni-axially pressed commercially pure titanium sintered powder metallurgy components. Powder was uni-axially pressed at designated pressure of 840 MPa to form cylindrical samples and the green compacts were sintered at 0.001 mbar for about 4 h with sintering temperature varying from 1350 to 1450 °C. The influence of the sintering temperature, pulse-on and pulse-off time at wire-EDM on the surface roughness of the preforms has been investigated thoroughly. Experiments were conducted under different machining parameters in a CNC operated wire-cut EDM. The surface roughness of the machined surface was measured and critically analysed. The optimum surface roughness was achieved under the conditions of 6 μs pulse-on time, 9 μs pulse-off time and at sintering temperature of 1450 °C.

Tribological properties of PM212: A high-temperature, self-lubricating, powder metallurgy composite

NASA Technical Reports Server (NTRS)

Dellacorte, Christopher; Sliney, Harold E.

1989-01-01

This paper describes a research program to develop and evaluate a new high temperature, self-lubricating powder metallurgy composite, PM212. PM212 has the same composition as the plasma-sprayed coating, PS212, which contains 70 wt percent metal-bonded chromium carbide, 15 wt percent silver and 15 wt percent barium fluoride/calcium fluoride eutectic. The carbide acts as a wear resistant matrix and the silver and fluorides act as low and high temperature lubricants, respectively. The material is prepared by sequential cold press, cold isostatic pressing and sintering techniques. In this study, hemispherically tipped wear pins of PM212 were prepared and slid against superalloy disks at temperatures from 25 to 850 C in air in a pin-on-disk tribometer. Friction coefficients range from 0.29 to 0.38 and the wear of both the composite pins and superalloy disks was moderate to low in the 10(exp -5) to 10(exp -6) cubic mm/N-m range. Preliminary tests indicate that the material has a compressive strength of at least 130 MPa over the entire temperature range of 25 to 900 C. This material has promise for use as seal inserts, bushings, small inside diameter parts and other applications where plasma-sprayed coatings are impractical or too costly.

Tribological properties of PM212 - A high temperature, self-lubricating, powder metallurgy composite

NASA Technical Reports Server (NTRS)

Dellacorte, Christopher; Sliney, Harold E.

1990-01-01

This paper describes a research program to develop and evaluate a new high temperature, self-lubricating powder metallurgy composite, PM212. PM212 has the same composition as the plasma-sprayed coating, PS212, which contains 70 wt percent metal-bonded chromium carbide, 15 wt percent silver and 15 wt percent barium fluoride/calcium fluoride eutectic. The carbide acts as a wear resistant matrix and the silver and fluorides act as low and high temperature lubricants, respectively. The material is prepared by sequential cold press, cold isostatic pressing and sintering techniques. In this study, hemispherically tipped wear pins of PM212 were prepared and slid against superalloy disks at temperatures from 25 to 850 C in air in a pin-on-disk tribometer. Friction coefficients range from 0.29 to 0.38 and the wear of both the composite pins and superalloy disks was moderate to low in the 10(exp -5) to 10(exp -6) cubic mm/N-m range. Preliminary tests indicate that the material has a compressive strength of at least 130 MPa over the entire temperature range of 25 to 900 C. This material has promise for use as seal inserts, bushings, small inside diameter parts and other applications where plasma-sprayed coatings are impractical or too costly.

Characterization of the carbides and the martensite phase in powder-metallurgy high-speed steel

DOE Office of Scientific and Technical Information (OSTI.GOV)

Godec, Matjaz, E-mail: matjaz.godec@imt.si; Batic, Barbara Setina; Mandrino, Djordje

2010-04-15

A microstructural characterization of the powder-metallurgy high-speed-steel S390 Microclean was performed based on an elemental distribution of the carbide phase as well as crystallographic analyses. The results showed that there were two types of carbides present: vanadium-rich carbides, which were not chemically homogeneous and exhibited a tungsten-enriched or tungsten-depleted central area; and chemically homogeneous tungsten-rich M{sub 6}C-type carbides. Despite the possibility of chemical inhomogenities, the crystallographic orientation of each of the carbides was shown to be uniform. Using electron backscatter diffraction the vanadium-rich carbides were determined to be either cubic VC or hexagonal V{sub 6}C{sub 5}, while the tungsten-rich carbidesmore » were M{sub 6}C. The electron backscatter diffraction results were also verified using X-ray diffraction. Several electron backscatter diffraction pattern maps were acquired in order to define the fraction of each carbide phase as well as the amount of martensite phase. The fraction of martensite was estimated using band-contrast images, while the fraction of carbides was calculated using the crystallographic data.« less

Powder metallurgy in aerospace research: A survey

NASA Technical Reports Server (NTRS)

Blakeslee, H. W.

1971-01-01

The various techniques by which powders can be produced, as pure metals or as alloys, are discussed; the methods by which these powders can be formed into the final parts are explained as well as further processing that may be necessary to meet specific requirements. The NASA developments are detailed, and references are provided for those who wish to obtain further information characteristic of any methodology.

Experimental investigation of amount of nano-Al2O3 on mechanical properties of Al-based nano-composites fabricated by powder metallurgy (PM)

NASA Astrophysics Data System (ADS)

Razzaqi, A.; Liaghat, Gh.; Razmkhah, O.

2017-10-01

In this paper, mechanical properties of Aluminum (Al) matrix nano-composites, fabricated by Powder Metallurgy (PM) method, has been investigated. Alumina (Al2O3) nano particles were added in amounts of 0, 2.5, 5, 7.5 and 10 weight percentages (wt%). For this purpose, Al powder (particle size: 20 µm) and nano-Al2O3 (particle size: 20 nm) in various weight percentages were mixed and milled in a blade mixer for 15 minutes in 1500 rpm. Then, the obtained mixture, compacted by means of a two piece die and uniaxial cold press of about 600 MPa and cold iso-static press (CIP), required for different tests. After that, the samples sintered in 600°C for 90 minutes. Compression and three-point bending tests performed on samples and the results, led us to obtain the optimized particle size for achieving best mechanical properties.

Biaxially textured articles formed by powder metallurgy

DOEpatents

Goyal, Amit; Williams, Robert K.

2001-01-01

A biaxially textured alloy article comprises Ni powder and at least one powder selected from the group consisting of Cr, W, V, Mo, Cu, Al, Ce, YSZ, Y, Rare Earths, (RE), MgO, CeO.sub.2, and Y.sub.2 O.sub.3 ; compacted and heat treated, then rapidly recrystallized to produce a biaxial texture on the article. In some embodiments the alloy article further comprises electromagnetic or electro-optical devices and possesses superconducting properties.

In vitro and in vivo biological performance of porous Ti alloys prepared by powder metallurgy.

PubMed

do Prado, Renata Falchete; Esteves, Gabriela Campos; Santos, Evelyn Luzia De Souza; Bueno, Daiane Acácia Griti; Cairo, Carlos Alberto Alves; Vasconcellos, Luis Gustavo Oliveira De; Sagnori, Renata Silveira; Tessarin, Fernanda Bastos Pereira; Oliveira, Felipe Eduardo; Oliveira, Luciane Dias De; Villaça-Carvalho, Maria Fernanda Lima; Henriques, Vinicius André Rodrigues; Carvalho, Yasmin Rodarte; De Vasconcellos, Luana Marotta Reis

2018-01-01

Titanium (Ti) and Ti-6 Aluminium-4 Vanadium alloys are the most common materials in implants composition but β type alloys are promising biomaterials because they present better mechanical properties. Besides the composition of biomaterial, many factors influence the performance of the biomaterial. For example, porous surface may modify the functional cellular response and accelerate osseointegration. This paper presents in vitro and in vivo evaluations of powder metallurgy-processed porous samples composed by different titanium alloys and pure Ti, aiming to show their potential for biomedical applications. The porous surfaces samples were produced with different designs to in vitro and in vivo tests. Samples were characterized with scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS) and elastic modulus analyses. Osteogenic cells from newborn rat calvaria were plated on discs of different materials: G1-commercially pure Ti group (CpTi); G2-Ti-6Al-4V alloy; G3-Ti-13 Niobium-13 Zirconium alloy; G4-Ti-35 Niobium alloy; G5-Ti-35 Niobium-7 Zirconium-5 Tantalum alloy. Cell adhesion and viability, total protein content, alkaline phosphatase activity, mineralization nodules and gene expression (alkaline phosphatase, Runx-2, osteocalcin and osteopontin) were assessed. After 2 and 4 weeks of implantation in rabbit tibia, bone ingrowth was analyzed using micro-computed tomography (μCT). EDS analysis confirmed the material production of each group. Metallographic and SEM analysis revealed interconnected pores, with mean pore size of 99,5μm and mean porosity of 42%, without significant difference among the groups (p>0.05). The elastic modulus values did not exhibit difference among the groups (p>0.05). Experimental alloys demonstrated better results than CpTi and Ti-6Al-4V, in gene expression and cytokines analysis, especially in early experimental periods. In conclusion, our data suggests that the experimental alloys can be used for biomedical

In vitro and in vivo biological performance of porous Ti alloys prepared by powder metallurgy

PubMed Central

Vasconcellos, Luis Gustavo Oliveira De; Oliveira, Felipe Eduardo; Oliveira, Luciane Dias De; Henriques, Vinicius André Rodrigues; Carvalho, Yasmin Rodarte; De Vasconcellos, Luana Marotta Reis

2018-01-01

Titanium (Ti) and Ti-6 Aluminium-4 Vanadium alloys are the most common materials in implants composition but β type alloys are promising biomaterials because they present better mechanical properties. Besides the composition of biomaterial, many factors influence the performance of the biomaterial. For example, porous surface may modify the functional cellular response and accelerate osseointegration. This paper presents in vitro and in vivo evaluations of powder metallurgy-processed porous samples composed by different titanium alloys and pure Ti, aiming to show their potential for biomedical applications. The porous surfaces samples were produced with different designs to in vitro and in vivo tests. Samples were characterized with scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS) and elastic modulus analyses. Osteogenic cells from newborn rat calvaria were plated on discs of different materials: G1—commercially pure Ti group (CpTi); G2—Ti-6Al-4V alloy; G3—Ti-13 Niobium-13 Zirconium alloy; G4—Ti-35 Niobium alloy; G5—Ti-35 Niobium-7 Zirconium-5 Tantalum alloy. Cell adhesion and viability, total protein content, alkaline phosphatase activity, mineralization nodules and gene expression (alkaline phosphatase, Runx-2, osteocalcin and osteopontin) were assessed. After 2 and 4 weeks of implantation in rabbit tibia, bone ingrowth was analyzed using micro-computed tomography (μCT). EDS analysis confirmed the material production of each group. Metallographic and SEM analysis revealed interconnected pores, with mean pore size of 99,5μm and mean porosity of 42%, without significant difference among the groups (p>0.05). The elastic modulus values did not exhibit difference among the groups (p>0.05). Experimental alloys demonstrated better results than CpTi and Ti-6Al-4V, in gene expression and cytokines analysis, especially in early experimental periods. In conclusion, our data suggests that the experimental alloys can be used for biomedical

Fabrication and characterization of aluminium hybrid composites reinforced with fly ash and silicon carbide through powder metallurgy

NASA Astrophysics Data System (ADS)

Bilal Naim Shaikh, Mohd; Arif, Sajjad; Arif Siddiqui, M.

2018-04-01

This paper reports the fabrication and characterization of aluminium hybrid composites (AMCs) reinforced with commonly available and inexpensive fly ash (FA, 0, 5, 10 and 15 wt.%) particles along silicon carbide (SiC) using powder metallurgy process. Scanning electron microscopy (SEM) and x-ray diffraction (XRD) were employed for microstructural characterization and phase identification respectively. Wear behaviour were investigated using pin-on-disc wear tester for the different combinations of wear parameters like load (10, 20 and 30 N), sliding speed (1.5, 2 and 2.5 m s‑1) and sliding distance (300, 600 and 900 m). SEM confirms the uniform distribution of FA and SiC in aluminium matrix. The hardness of Al/SiC/FA is increased by 20%–25% while wear rate decreased by 15%–40%. From wear analysis, sliding distance was the least significant parameter influencing the wear loss followed by applied load and sliding speed. To identify the mechanism of wear, worn out surface were also analysed by SEM.

Phase composition, microstructure, and mechanical properties of porous Ti-Nb-Zr alloys prepared by a two-step foaming powder metallurgy method.

PubMed

Rao, X; Chu, C L; Zheng, Y Y

2014-06-01

Porous Ti-Nb-Zr alloys with different porosities from 6.06 to 62.8% are prepared by a two-step foaming powder metallurgy method using TiH2, Nb, and Zr powders together with 0 to 50wt% of NH4HCO3. The effects of the amounts of Nb and Zr as well as the sintering temperature (1473 to 1673K) on their phase composition, porosity, morphology, and mechanical characteristics are investigated. By controlling the porosity, Nb and Zr concentrations as well as the sintering temperature, porous Ti-Nb-Zr alloys with different mechanical properties can be obtained, for example, the hardness between 290 and 63HV, the compressive strength between 1530.5 and 73.4MPa, and the elastic modulus between 10.8 and 1.2GPa. The mechanical properties of the sintered porous Ti-Nb-Zr alloys can be tailored to match different requirements for the human bones and are thus potentially useful in the hard tissue implants. Copyright © 2014 Elsevier Ltd. All rights reserved.

Effect of Milling Time on the Microstructure, Physical and Mechanical Properties of Al-Al₂O₃ Nanocomposite Synthesized by Ball Milling and Powder Metallurgy.

PubMed

Toozandehjani, Meysam; Matori, Khamirul Amin; Ostovan, Farhad; Abdul Aziz, Sidek; Mamat, Md Shuhazlly

2017-10-26

The effect of milling time on the morphology, microstructure, physical and mechanical properties of pure Al-5 wt % Al₂O₃ (Al-5Al₂O₃) has been investigated. Al-5Al₂O₃ nanocomposites were fabricated using ball milling in a powder metallurgy route. The increase in the milling time resulted in the homogenous dispersion of 5 wt % Al₂O₃ nanoparticles, the reduction of particle clustering, and the reduction of distances between the composite particles. The significant grain refining during milling was revealed which showed as a reduction of particle size resulting from longer milling time. X-Ray diffraction (XRD) analysis of the nanocomposite powders also showed that designated ball milling contributes to the crystalline refining and accumulation of internal stress due to induced severe plastic deformation of the particles. It can be argued that these morphological and microstructural variations of nanocomposite powders induced by designated ball milling time was found to contribute to an improvement in the density, densification, micro-hardness ( HV ), nano-hardness ( HN ), and Young's modulus ( E ) of Al-5Al₂O₃ nanocomposites. HV , HN , and E values of nanocomposites were increased by ~48%, 46%, and 40%, after 12 h of milling, respectively.

Development of a Power Metallurgy Superalloy for Use at 1800-2000 F (980-1090 C)

NASA Technical Reports Server (NTRS)

Kortovich, C. S.

1973-01-01

A program was conducted to develop a powder metallurgy nickel-base superalloy for 1800-2000 F (980-1090 C) temperature applications. The feasibility of a unique concept for alloying carbon into a superalloy powder matrix and achieving both grain growth and a discrete particle grain boundary carbide precipitation was demonstrated. The process consisted of blending metastable carbides with a carbon free base alloy and consolidating this blend by hot extrusion. This was followed by heat treatment to grow a desired ASTM No. 2-3 grain size and to solution the metastable carbides to allow precipitation of discrete particle grain boundary carbides during subsequent aging heat treatments. The best alloy developed during this program was hydrogen-atomized, thermal-mechanically processed, modified MAR-M246 base alloy plus VC (0.28 w/o C). Although below those for cast MAR-M246, the mechanical properties exhibited by this alloy represent the best combination offered by conventional powder metallurgy processing to date.

Application of superalloy powder metallurgy for aircraft engines

NASA Technical Reports Server (NTRS)

Dreshfield, R. L.; Miner, R. V., Jr.

1980-01-01

The results of the Materials for Advanced Turbine Engines (MATE) program initiated by NASA are presented. Mechanical properties comparisons are made for superalloy parts produced by as-HIP powder consolidation and by forging of HIP consolidated billets. The effect of various defects on the mechanical properties of powder parts are shown.

Synthesis and characterization of T[Ni(CN){sub 4}].2pyz with T=Fe, Ni; pyz=pyrazine: Formation of T-pyz-Ni bridges

DOE Office of Scientific and Technical Information (OSTI.GOV)

Lemus-Santana, A.A.; Rodriguez-Hernandez, J.; Institute of Materials Science and Technology, University of Havana

2011-08-15

The formation of T-pyz-Ni bridges (pyz=pyrazine) in the T[Ni(CN){sub 4}].2pyz series is known for T=Mn, Zn, Cd and Co but not with T=Fe, Ni. In this contribution the existence of such bridges also for T=Fe, Ni is discussed. The obtained pillared solids, T[Ni(CN){sub 4}].2pyz, were characterized from XRD, TG, UV-Vis, IR, Raman, Moessbauer and magnetic data. Their crystal structures were refined in the orthorhombic Pmna space group from XRD powder patterns. The structural behavior of these solids on cooling down to 77 K was also studied. In the 180-200 K temperature range the occurrence of a structural transition to amore » monoclinic structure (P2{sub 1}/c space group) was observed. No temperature induced spin transition was observed for Fe[Ni(CN){sub 4}].2pyz. The iron (II) was found to be in high spin electronic state and this configuration is preserved on cooling down to 2 K. The magnetic data indicate the occurrence of a low temperature weak anti-ferromagnetic interaction between T metal centers within the T[Ni(CN){sub 4}] layer. In the paramagnetic region for Ni[Ni(CN){sub 4}].2pyz, a reversible temperature induced spin transition for the inner Ni atom was detected. - Graphical abstract: Rippled sheets structure for the pillared solids T[Ni(CN){sub 4}].2pyz. The pyrazine molecule is found forming T-pyz-Ni bridges between neighboring layers. Highlights: > Pillared 2D solids. > Inorganic-organic solids. > Assembling of molecular blocks. > From 1D and 2D building blocks to 3D solids.« less

Investigation of the Environmental Durability of a Powder Metallurgy Material

NASA Technical Reports Server (NTRS)

Ward, LaNita D.

2004-01-01

PM304 is a NASA-developed composite powder metallurgy material that is being developed for high temperature applications such as bushings in high temperature industrial furnace conveyor systems. My goal this summer was to analyze and evaluate the effects that heat exposure had on the PM304 material at 500 C and 650 C. The material is composed of Ni-Cr, Ag, Cr2O3, and eutectic BaF2-CaF2. PM304 is designed to eliminate the need for oil based lubricants in high temperature applications, while reducing friction and wear. However, further investigation was needed to thoroughly examine the properties of PM304. The effects of heat exposure on PM304 bushings were investigated. This investigation was necessary due to the high temperatures that the material would be exposed to in a typical application. Each bushing was cut into eight sections. The specimens were heated to 500 C or 650 C for time intervals from 1 hr to 5,000 hrs. Control specimens were kept at room temperature. Weight and thickness measurements were taken before and after the bushing sections were exposed to heat. Then the heat treated specimens were mounted and polished side by side with the control specimens. This enabled optical examination of the material's microstructure using a metallograph. The specimens were also examined with a scanning electron microscope (SEM). The microstructures were compared to observe the effects of the heat exposure. Chemical analysis was done to investigate the interactions between Ni-Cr and BaF2-CaF2 and between Cr2O3 and BaF2-CaF2 at high temperature. To observe this, the two compounds that were being analyzed were mixed in a crucible in varied weight percentages and heated to 1100 C in a furnace for approximately two hours. Then the product was allowed to cool and was then analyzed by X-ray diffraction. Interpretation of the results is in progress.

Dwell Notch Low Cycle Fatigue Behavior of a Powder Metallurgy Nickel Disk Alloy

NASA Technical Reports Server (NTRS)

Telesman, J.; Gabb, T. P.; Yamada, Y.; Ghosn, L. J.; Jayaraman, N.

2012-01-01

A study was conducted to determine the processes which govern dwell notch low cycle fatigue (NLCF) behavior of a powder metallurgy (P/M) ME3 disk superalloy. The emphasis was placed on the environmentally driven mechanisms which may embrittle the highly stressed notch surface regions and reduce NLCF life. In conjunction with the environmentally driven notch surface degradation processes, the visco-plastic driven mechanisms which can significantly change the notch root stresses were also considered. Dwell notch low cycle fatigue testing was performed in air and vacuum on a ME3 P/M disk alloy specimens heat treated using either a fast or a slow cooling rate from the solutioning treatment. It was shown that dwells at the minimum stress typically produced a greater life debit than the dwells applied at the maximum stress, especially for the slow cooled heat treatment. Two different environmentally driven failure mechanisms were identified as the root cause of early crack initiation in the min dwell tests. Both of these failure mechanisms produced mostly a transgranular crack initiation failure mode and yet still resulted in low NLCF fatigue lives. The lack of stress relaxation during the min dwell tests produced higher notch root stresses which caused early crack initiation and premature failure when combined with the environmentally driven surface degradation mechanisms. The importance of environmental degradation mechanisms was further highlighted by vacuum dwell NLCF tests which resulted in considerably longer NLCF lives, especially for the min dwell tests.

Effects of porosity on corrosion resistance of Mg alloy foam produced by powder metallurgy technology

DOE Office of Scientific and Technical Information (OSTI.GOV)

Aghion, E., E-mail: egyon@bgu.ac.il; Perez, Y.

2014-10-15

Magnesium alloy foams have the potential to serve as structural material for regular light-weight applications as well as for biodegradable scaffold implants. However, their main disadvantage relates to the high reactivity of magnesium and consequently their natural tendency to corrode in regular service conditions and in physiological environments. The present study aims at evaluating the effect of porosity on the corrosion resistance of MRI 201S magnesium alloy foams in 0.9% NaCl solution and in phosphate buffer saline solution as a simulated physiological electrolyte. The magnesium foams were produced by powder metallurgy technology using space-holding particles to control the porosity content.more » Machined chips were used as raw material for the production of Mg alloy powder by milling process. The microstructure of the foams was examined using optical and scanning electron microscopy, X-ray diffraction, and X-ray photoelectron spectroscopy analysis. The corrosion behavior was evaluated by immersion test and potentiodynamic polarization analysis. The results obtained clearly demonstrate that the porosity has a significant effect on the corrosion resistance of the tested foams. Foams with 14–19% porosity have a corrosion rate of 4–10 mcd and 7–15 mcd in NaCl and phosphate buffer saline solution, respectively, compared to only 0.10 mcd for the same alloy in as cast conditions. This increased corrosion degradation of the Mg foams by more than one order of magnitude compared to the cast alloy may limit their potential application in regular and physiological environments. - Highlights: • Porosity has a detrimental effect on corrosion resistance of MRI 201S Mg foams. • 14–19% porosity increases the corrosion rate by more than one order of magnitude. • Accelerated corrosion limits the use of foams in regular/physiological environments.« less

Morphological and Wear behaviour of new Al-SiCmicro-SiCnano hybrid nanocomposites fabricated through powder metallurgy

NASA Astrophysics Data System (ADS)

Arif, Sajjad; Tanwir Alam, Md; Aziz, Tariq; Ansari, Akhter H.

2018-04-01

In the present work, aluminium matrix composites reinforced with 10 wt% SiC micro particles along with x% SiC nano particles (x = 0, 1, 3, 5 and 7 wt%) were fabricated through powder metallurgy. The fabricated hybrid composites were characterized by x-ray diffractometer (XRD), scanning electron microscope (SEM), energy dispersive spectrum (EDS) and elemental mapping. The relative density, hardness and wear behaviour of all hybrid nanocomposites were studied. The influence of various control factors like SiC reinforcement, sliding distance (300, 600, 900 and 1200 m) and applied load (20, 30 and 40 N) were explored using pin-on-disc wear apparatus. The uniform distribution of micro and nano SiC particles in aluminium matrix is confirmed by elemental maps. The hardness and wear test results showed that properties of the hybrid composite containing 5 wt% nano SiC was better than other hybrid composites. Additionally, the wear loss of all hybrid nanocomposites increases with increasing sliding distance and applied load. The identification of wear phenomenon were studied through the SEM images of worn surface.

High damping Al-Fe-Mo-Si/Zn-Al composites produced by rapidly solidified powder metallurgy process

DOE Office of Scientific and Technical Information (OSTI.GOV)

Li, P.Y.; Dai, S.L.; Chai, S.C.

2000-05-10

The metallic materials commonly used in aircraft and aerospace fields, such as aluminum and titanium alloys, steels, etc., show extremely low damping capacity (usually of the order of or less than 10{sup {minus}3}). Thus, some problems related to vibration may emerge and influence the reliability, safety and life of airplanes, satellites, etc. It has been reported that almost two thirds of errors for rockets and satellites are related to vibration and noise. One effective way to solve these vibration-related problems is to adopt high damping metallic materials. Conventional high damping alloys exhibit damping capacity above 10{sup {minus}2}, however, their densitiesmore » are usually great than 5 x 10{sup 3} kg m{sup {minus}3}, or their strengths are less than 200 MPa (for alloys based on dislocation damping), making them impossible to be applied to aircraft and aerospace areas. Recently, some low-density high-damping metal/metal composites based on aluminum and high damping alloys have been developed in Beijing Institute of Aeronautical Materials (BIAM) by the rapidly solidified power metallurgy process. This paper aims to report the properties of the composites based on a high temperature Al-Fe-Mo-Si alloy and a high damping Zn-Al alloy, and compare them with that of 2618-T61 alloy produced by the ingot metallurgy process.« less

Formation of Al3Ti/Mg composite by powder metallurgy of Mg-Al-Ti system.

PubMed

Yang, Zi R; Qi Wang, Shu; Cui, Xiang H; Zhao, Yu T; Gao, Ming J; Wei, Min X

2008-07-01

An in situ titanium trialuminide (Al 3 Ti)-particle-reinforced magnesium matrix composite has been successfully fabricated by the powder metallurgy of a Mg-Al-Ti system. The reaction processes and formation mechanism for synthesizing the composite were studied by differential scanning calorimetry (DSC), x-ray diffractometry (XRD), scanning electron microscopy (SEM) and energy-dispersive x-ray spectroscopy (EDS). Al 3 Ti particles are found to be synthesized in situ in the Mg alloy matrix. During the reaction sintering of the Mg-Al-Ti system, Al 3 Ti particles are formed through the reaction of liquid Al with as-dissolved Ti around the Ti particles. The formed intermetallic particles accumulate at the original sites of the Ti particles. As sintering time increases, the accumulated intermetallic particles disperse and reach a relatively homogeneous distribution in the matrix. It is found that the reaction process of the Mg-Al-Ti system is almost the same as that of the Al-Ti system. Mg also acts as a catalytic agent and a diluent in the reactions and shifts the reactions of Al and Ti to lower temperatures. An additional amount of Al is required for eliminating residual Ti and solid-solution strengthening of the Mg matrix.

Powder and particulate production of metallic alloys

NASA Technical Reports Server (NTRS)

Grant, N. J.

1982-01-01

Developments of particulate metallurgy of alloyed materials where the final products is a fully dense body are discussed. Particulates are defined as powders, flakes, foils, silvers, ribbons and strip. Because rapid solidification is an important factor in particulate metallurgy, all of the particulates must have at least one dimension which is very fine, sometimes as fine as 10 to 50 microns, but move typically up to several hundred microns, provided that the dimension permits a minimum solidification rate of at least 100 K/s.

[Application of sintered Ti powder to dental prostheses].

PubMed

Hikosaka, Tatsuya; Tanaka, Yoshinobu; Hoshiai, Kazumoto; Kanazawa, Takeshi; Nakamura, Yoshinori; Tsuda, Kenji; Ohasi, Hideya

2005-04-01

Powder metallurgy is a metal processing technology. Porous titanium produced from powder is widely used. The method is applied to titanium, which is not easy to cast as it sinters under melting point. In prosthetic dentistry, powder metallurgy can be applied to high fusing metal that is biocompatible. In this study, we examined the mechanical characteristics of the Ti sheet produced by sintering and discussed its application to dental prosthesis manufacturing. Ti sheets of 1-mm thickness, in which a binder was added to spherical Ti powder, were produced with the Doctor Blade Method. The sintering was carried out between 900-1150 degrees C at 6 temperatures. The sintered compact was evaluated by dimensional change rate, hardness test, bending strength, tensile strength and SEM observation. Another compact was sintered on the refractory cast. Mechanical strength significantly increased with sintering temperature. In addition, excellent mechanical strength was acquired by adding crushed powder and performing the de-binder process. In the sintering on the refractory cast, pre-baking for more than 100 minutes and sintering at over 1050 degrees C was needed for practical application. It thus seems possible to apply sintered titanium to dental prostheses. However, it will be necessary to examine the control of the shrinkage of the sintered compact in the future too.

Laboratory Powder Metallurgy Makes Tough Aluminum Sheet

NASA Technical Reports Server (NTRS)

Royster, D. M.; Thomas, J. R.; Singleton, O. R.

1993-01-01

Aluminum alloy sheet exhibits high tensile and Kahn tear strengths. Rapid solidification of aluminum alloys in powder form and subsequent consolidation and fabrication processes used to tailor parts made of these alloys to satisfy such specific aerospace design requirements as high strength and toughness.

Review of European Powder Metallurgy of Superalloys.

DTIC Science & Technology

1979-12-01

after suitable slag skiimming, atomization occurs through a ceramic nozzle. Powder falls through the atomizing tower and is collected in a water...shaped container for HIP. Superplastic bag forming is also being investigated( 2 7 ) , but few details are available. Glass cans have also been used for

Effect of Milling Time on the Microstructure, Physical and Mechanical Properties of Al-Al2O3 Nanocomposite Synthesized by Ball Milling and Powder Metallurgy

PubMed Central

Matori, Khamirul Amin; Ostovan, Farhad; Abdul Aziz, Sidek; Mamat, Md Shuhazlly

2017-01-01

The effect of milling time on the morphology, microstructure, physical and mechanical properties of pure Al-5 wt % Al2O3 (Al-5Al2O3) has been investigated. Al-5Al2O3 nanocomposites were fabricated using ball milling in a powder metallurgy route. The increase in the milling time resulted in the homogenous dispersion of 5 wt % Al2O3 nanoparticles, the reduction of particle clustering, and the reduction of distances between the composite particles. The significant grain refining during milling was revealed which showed as a reduction of particle size resulting from longer milling time. X-Ray diffraction (XRD) analysis of the nanocomposite powders also showed that designated ball milling contributes to the crystalline refining and accumulation of internal stress due to induced severe plastic deformation of the particles. It can be argued that these morphological and microstructural variations of nanocomposite powders induced by designated ball milling time was found to contribute to an improvement in the density, densification, micro-hardness (HV), nano-hardness (HN), and Young’s modulus (E) of Al-5Al2O3 nanocomposites. HV, HN, and E values of nanocomposites were increased by ~48%, 46%, and 40%, after 12 h of milling, respectively. PMID:29072632

Making Self-Lubricating Parts By Powder Metallurgy

NASA Technical Reports Server (NTRS)

Sliney, Harold E.; Dellacorte, Christopher

1990-01-01

Compositions and parameters of powder-metallurgical fabrication processes determined for new class of low-friction, low-wear, self-lubricating materials. Used in oxidizing or reducing atmospheres in bearings and seals, at temperatures from below 25 degrees C to as high as 900 degrees C. Thick parts made with minimal waste.

Effect of nickel addition on mechanical properties of powder forged Fe-Cu-C

NASA Astrophysics Data System (ADS)

Archana Barla, Nikki

2018-03-01

Fe-Cu-C system is very popular in P/M industry for its good compressibility and dimensional stability with high strength. Fe-Cu-C is a structural material and is used where high strength with high hardness is required. The composition of powder metallurgy steel plays a vital role in the microstructure and physical properties of the sintered component. Fe-2Cu-0.7C-Ni alloy with varying nickel composition (0%, 0.5%, 1.0%, 1.5%, 2.0%, and 3.0%) wt. % was prepared by powder metallurgy (P/M) sinter forging process. The present work discuss the effect of varying nickel content on microstructure and mechanical properties.

Critical current densities of powder-in-tube MgB2 tapes fabricated with nanometer-size Mg powder

NASA Astrophysics Data System (ADS)

Yamada, H.; Hirakawa, M.; Kumakura, H.; Matsumoto, A.; Kitaguchi, H.

2004-03-01

We fabricated powder-in-tube MgB2/Fe tapes using a powder mixture of nanometer-size Mg and commercial amorphous B and investigated the transport properties. High-purity nanometer-size Mg powder was fabricated by applying the thermal plasma method. 5-10 mol % SiC powder doping was tried to enhance the Jc properties. We found that the use of nanometer-size Mg powder was effective to increase the Jc values. The transport Jc values of the nondoped and 10 mol % SiC-doped tapes prepared with nanometer-size Mg powder reached 90 and 250 A/mm2 at 4.2 K and 10 T, respectively. These values were about five times higher than those of the tapes prepared with commercial Mg powder.

Materials for Advanced Turbine Engines. Volume 1; Power Metallurgy Rene 95 Rotating Turbine Engine Parts

NASA Technical Reports Server (NTRS)

Pfouts, W. R.; Shamblen, C. E.; Mosier, J. S.; Peebles, R. E.; Gorsler, R. W.

1979-01-01

An attempt was made to improve methods for producing powder metallurgy aircraft gas turbine engine parts from the nickel base superalloy known as Rene 95. The parts produced were the high pressure turbine aft shaft for the CF6-50 engine and the stages 5 through 9 compressor disk forgings for the CFM56/F101 engines. A 50% cost reduction was achieved as compared to conventional cast and wrought processing practices. An integrated effort involving several powder producers and a major forging source were included.

Microstructure and Strengthening Mechanisms in an Ultrafine Grained Al-Mg-Sc Alloy Produced by Powder Metallurgy

DOE Office of Scientific and Technical Information (OSTI.GOV)

Tammy J. Harrell; Troy D. Topping; Haiming Wen

2014-12-01

Additions of Sc to an Al-Mg matrix were investigated, paying particular attention to the influence of Al3Sc precipitates and other dispersoids, as well as grain size, on mechanical behavior. Prior studies have shown that Sc significantly increases the strength of coarse-grained Al-Mg alloys. Prompted by these findings, we hypothesized that it would be of fundamental and technological interest to study the behavior of Sc additions to an ultrafine-grained (UFG) microstructure (e.g., 100’s nm). Accordingly, we investigated the microstructural evolution and mechanical behavior of a cryomilled ultrafine grained Al-5Mg-0.4Sc (wt pct) and compared the results to those of an equivalent fine-grainedmore » material (FG) produced by powder metallurgy. Experimental materials were consolidated by hot isostatic pressing (HIP’ing) followed by extrusion or dual mode dynamic forging. Under identical processing conditions, UFG materials generate large Al3Sc precipitates with an average diameter of 154 nm and spaced approximately 1 to 3 µm apart, while precipitates in the FG materials have a diameter of 24 nm and are spaced 50 to 200 nm apart. The strengthening mechanisms are calculated for all materials and it is determined that the greatest strengthening contributions for the UFG and FG materials are Mg-O/N dispersion strengthening and precipitate strengthening, respectively.« less

Method for forming biaxially textured articles by powder metallurgy

DOEpatents

Goyal, Amit; Williams, Robert K.; Kroeger, Donald M.

2002-01-01

A method of preparing a biaxially textured alloy article comprises the steps of preparing a mixture comprising Ni powder and at least one powder selected from the group consisting of Cr, W, V, Mo, Cu, Al, Ce, YSZ, Y, Rare Earths, (RE), MgO, CeO.sub.2, and Y.sub.2 O.sub.3 ; compacting the mixture, followed by heat treating and rapidly recrystallizing to produce a biaxial texture on the article. In some embodiments the alloy article further comprises electromagnetic or electro-optical devices and possesses superconducting properties.

Gamma prime precipitation modeling and strength responses in powder metallurgy superalloys

NASA Astrophysics Data System (ADS)

Mao, Jian

Precipitation-hardened nickel-based superalloys have been widely used as high temperature structural materials in gas turbine engine applications for more than 50 years. Powder metallurgy (P/M) technology was introduced as an innovative manufacturing process to overcome severe segregation and poor workability of alloys with high alloying contents. The excellent mechanical properties of P/M superalloys also depend upon the characteristic microstructures, including grain size and size distribution of gamma' precipitates. Heat treatment is the most critical processing step that has ultimate influences on the microstructure, and hence, on the mechanical properties of the materials. The main objective of this research was to study the gamma ' precipitation kinetics in various cooling circumstances and also study the strength response to the cooling history in two model alloys, Rne88DT and U720LI. The research is summarized below: (1) An experimental method was developed to allow accurate simulation and control of any desired cooling profile. Two novel cooling methods were introduced: continuous cooling and interrupt cooling. Isothermal aging was also carried out. (2) The growth and coarsening kinetics of the cooling gamma' precipitates were experimentally studied under different cooling and aging conditions, and the empirical equations were established. It was found that the cooling gamma' precipitate versus the cooling rate follows a power law. The gamma' precipitate size versus aging time obeys the LSW cube law for coarsening. (3) The strengthening of the material responses to the cooling rate and the decreasing temperature during cooling was investigated in both alloys. The tensile strength increases with the cooling rate. In addition, the non-monotonic response of strength versus interrupt temperature is of great interest. (4) An energy-driven model integrated with the classic growth and coarsen theories was successfully embedded in a computer program developed to

Effects of Process Parameters on Copper Powder Compaction Process Using Multi-Particle Finite Element Method

NASA Astrophysics Data System (ADS)

Güner, F.; Sofuoğlu, H.

2018-01-01

Powder metallurgy (PM) has been widely used in several industries; especially automotive and aerospace industries and powder metallurgy products grow up every year. The mechanical properties of the final product that is obtained by cold compaction and sintering in powder metallurgy are closely related to the final relative density of the process. The distribution of the relative density in the die is affected by parameters such as compaction velocity, friction coefficient and temperature. Moreover, most of the numerical studies utilizing finite element approaches treat the examined environment as a continuous media with uniformly homogeneous porosity whereas Multi-Particle Finite Element Method (MPFEM) treats every particles as an individual body. In MPFEM, each of the particles can be defined as an elastic- plastic deformable body, so the interactions of the particles with each other and the die wall can be investigated. In this study, each particle was modelled and analyzed as individual deformable body with 3D tetrahedral elements by using MPFEM approach. This study, therefore, was performed to investigate the effects of different temperatures and compaction velocities on stress distribution and deformations of copper powders of 200 µm-diameter in compaction process. Furthermore, 3-D MPFEM model utilized von Mises material model and constant coefficient of friction of μ=0.05. In addition to MPFEM approach, continuum modelling approach was also performed for comparison purposes.

Mg-Zn based composites reinforced with bioactive glass (45S5) fabricated via powder metallurgy

NASA Astrophysics Data System (ADS)

Ab llah, N.; Jamaludin, S. B.; Daud, Z. C.; Zaludin, M. A. F.

2016-07-01

Metallic implants are shifting from bio-inert to bioactive and biodegradable materials. These changes are made in order to improve the stress shielding effect and bio-compatibility and also avoid the second surgery procedure. Second surgery procedure is required if the patient experienced infection and implant loosening. An implant is predicted to be well for 15 to 20 years inside patient body. Currently, magnesium alloys are found to be the new biomaterials because of their properties close to the human bones and also able to degrade in the human body. In this work, magnesium-zinc based composites reinforced with different content (5, 15, 20 wt. %) of bioactive glass (45S5) were fabricated through powder metallurgy technique. The composites were sintered at 450˚C. Density and porosity of the composites were determined using the gas pycnometer. Microstructure of the composites was observed using an optical microscope. In-vitro bioactivity behavior was evaluated in the simulated body fluid (SBF) for 7 days. Fourier Transform Infrared (FTIR) was used to characterize the apatite forming on the samples surface. The microstructure of the composite showed that the pore segregated near the grain boundaries and bioglass clustering was observed with increasing content of bioglass. The true density of the composites increased with the increasing content of bioglass and the highest value of porosity was indicated by the Mg-Zn reinforced with 20 wt.% of bioglass. The addition of bio-glass to the Mg-Zn has also induced the formation of apatite layer after soaking in SBF solution.

Powder-Metallurgical Bearings For Turbopumps

NASA Technical Reports Server (NTRS)

Bhat, B. N.; Humphries, T. S.; Thom, R. L.; Moxson, V.; Friedman, G. I.; Dolan, F. J.; Shipley, R. J.

1993-01-01

Bearings fabricated by powder metallurgy developed for use in machines subjected to extremes of temperature, rolling-contact cyclic stresses, and oxidizing or otherwise corrosive fluids. Bearings also extend operating lives of other machines in which bearings required to resist extreme thermal, mechanical, and chemical stresses. One alloy exhibiting outstanding properties was MRC-2001. Resistance to fatigue, stress corrosion cracking, and wear found superior to that of 440C stainless steel.

Processing, characterization, and in vitro/in vivo evaluations of powder metallurgy processed Ti-13Nb-13Zr alloys.

PubMed

Bottino, Marco C; Coelho, Paulo G; Henriques, Vinicius A R; Higa, Olga Z; Bressiani, Ana H A; Bressiani, José C

2009-03-01

This article presents details of processing, characterization and in vitro as well as in vivo evaluations of powder metallurgy processed Ti-13Nb-13Zr samples with different levels of porosity. Sintered samples were characterized for density, crystalline phases (XRD), and microstructure (SEM and EDX). Samples sintered at 1000 degrees C showed the highest porosity level ( approximately 30%), featuring open and interconnected pores ranging from 50 to 100 mum in diameter but incomplete densification. In contrast, samples sintered at 1300 and 1500 degrees C demonstrated high densification with 10% porosity level distributed in a homogeneous microstructure. The different sintering conditions used in this study demonstrated a coherent trend that is increase in temperature lead to higher sample densification, even though densification represents a drawback for bone ingrowth. Cytotoxicity tests did not reveal any toxic effects of the starting and processed materials on surviving cell percentage. After an 8-week healing period in rabbit tibias, the implants were retrieved, processed for nondecalcified histological evaluation, and then assessed by backscattered electron images (BSEI-SEM) and EDX. Bone growth into the microstructure was observed only in samples sintered at 1000 degrees C. Overall, a close relation between newly formed bone and all processed samples was observed. (c) 2008 Wiley Periodicals, Inc.

Precipitation in cold-rolled Al–Sc–Zr and Al–Mn–Sc–Zr alloys prepared by powder metallurgy

DOE Office of Scientific and Technical Information (OSTI.GOV)

Vlach, M., E-mail: martin.vlach@mff.cuni.cz; Stulikova, I.; Smola, B.

2013-12-15

The effects of cold-rolling on thermal, mechanical and electrical properties, microstructure and recrystallization behaviour of the AlScZr and AlMnScZr alloys prepared by powder metallurgy were studied. The powder was produced by atomising in argon with 1% oxygen and then consolidated by hot extrusion at 350 °C. The electrical resistometry and microhardness together with differential scanning calorimetry measurements were compared with microstructure development observed by transmission and scanning electron microscopy, X-ray diffraction and electron backscatter diffraction. Fine (sub)grain structure developed and fine coherent Al{sub 3}Sc and/or Al{sub 3}(Sc,Zr) particles precipitated during extrusion at 350 °C in the alloys studied. Additional precipitationmore » of the Al{sub 3}Sc and/or Al{sub 3}(Sc,Zr) particles and/or their coarsening was slightly facilitated by the previous cold rolling. The presence of Sc,Zr-containing particles has a significant antirecrystallization effect that prevents recrystallization at temperatures minimally up to 420 °C. The precipitation of the Al{sub 6}Mn- and/or Al{sub 6}(Mn,Fe) particles of a size ∼ 1.0 μm at subgrain boundaries has also an essential antirecrystallization effect and totally suppresses recrystallization during 32 h long annealing at 550 °C. The texture development of the alloys seems to be affected by high solid solution strengthening by Mn. The precipitation of the Mn-containing alloy is highly enhanced by a cold rolling. The apparent activation energy of the Al{sub 3}Sc particles formation and/or coarsening and that of the Al{sub 6}Mn and/or Al{sub 6}(Mn,Fe) particle precipitation in the powder and in the compacted alloys were determined. The cold deformation has no effect on the apparent activation energy values of the Al{sub 3}Sc-phase and the Al{sub 6}Mn-phase precipitation. - Highlights: • The Mn, Sc and Zr additions to Al totally suppresses recrystallization at 550 °C. • The Sc

Porous mandrels provide uniform deformation in hydrostatic powder metallurgy

NASA Technical Reports Server (NTRS)

Gripshover, P. J.; Hanes, H. D.

1967-01-01

Porous copper mandrels prevent uneven deformation of beryllium machining blanks. The beryllium powder is arranged around these mandrels and hot isostatically pressed to form the blanks. The mandrels are then removed by leaching.

A new titanium based alloy Ti-27Nb-13Zr produced by powder metallurgy with biomimetic coating for use as a biomaterial.

PubMed

Mendes, Marcio W D; Ágreda, Carola G; Bressiani, Ana H A; Bressiani, José C

2016-06-01

Titanium alloys are widely used in biomedical applications due to their excellent properties such as high strength, good corrosion resistance and biocompatibility. Titanium alloys with alloying elements such as Nb and Zr are biocompatible and have Young's modulus close to that of human bone. To increase the bioactivity of titanium alloy surfaces is used chemical treatment with NaOH followed by immersion in simulated body fluid (SBF). The purpose of this study was to produce the alloy Ti-27Nb-13Zr with low Young's modulus by powder metallurgy using powders produced by the HDH process. The formation of biomimetic coatings on samples immersed in SBF for 3, 7, 11 and 15 days was evaluated. Characterization of the coating was performed by diffuse reflectance infrared Fourier transform spectroscopy (DRIFTS) and scanning electron microscope. The microstructure and composition of the alloy were determined using SEM and XRD, while the mechanical properties were evaluated by determining the elastic modulus and the Vickers microhardness. The sintered alloys were composed of α and β phases, equiaxed grains and with density around 97.8% of its theoretical density. The Vickers microhardness and elasticity modulus of the alloy were determined and their values indicate that this alloy can be used as a biomaterial. Analysis of the coating revealed the presence of calcium phosphate layers on samples immersed for >3 days in the SBF solution. Copyright © 2016 Elsevier B.V. All rights reserved.

Molybdeno-Aluminizing of Powder Metallurgy and Wrought Ti and Ti-6Al-4V alloys by Pack Cementation process

DOE Office of Scientific and Technical Information (OSTI.GOV)

Tsipas, Sophia A., E-mail: stsipas@ing.uc3m.es; Go

Wear and high temperature oxidation resistance of some titanium-based alloys needs to be enhanced, and this can be effectively accomplished by surface treatment. Molybdenizing is a surface treatment where molybdenum is introduced into the surface of titanium alloys causing the formation of wear-resistant surface layers containing molybdenum, while aluminizing of titanium-based alloys has been reported to improve their high temperature oxidation properties. Whereas pack cementation and other surface modification methods have been used for molybdenizing or aluminizing of wrought and/or cast pure titanium and titanium alloys, such surface treatments have not been reported on titanium alloys produced by powder metallurgymore » (PM). Also a critical understanding of the process parameters for simultaneous one step molybdeno-aluminizing of titanium alloys by pack cementation and the predominant mechanism for this process have not been reported. The current research work describes the surface modification of titanium and Ti-6Al-4V prepared by PM by molybdeno-aluminizing and analyzes thermodynamic aspects of the deposition process. Similar coatings are also deposited to wrought Ti-6Al-4V and compared. Characterization of the coatings was carried out using scanning electron microscopy and x-ray diffraction. For both titanium and Ti-6Al-4V, the use of a powder pack containing ammonium chloride as activator leads to the deposition of molybdenum and aluminium into the surface but also introduces nitrogen causing the formation of a thin titanium nitride layer. In addition, various titanium aluminides and mixed titanium aluminium nitrides are formed. The appropriate conditions for molybdeno-aluminizing as well as the phases expected to be formed were successfully determined by thermodynamic equilibrium calculations. - Highlights: •Simultaneous co-deposition of Mo-Al onto powder metallurgy and wrought Ti alloy •Thermodynamic calculations were used to optimize deposition

On the Effect of Nb on the Microstructure and Properties of Next Generation Polycrystalline Powder Metallurgy Ni-Based Superalloys

NASA Astrophysics Data System (ADS)

Christofidou, Katerina A.; Hardy, Mark C.; Li, Hang-Yue; Argyrakis, Christos; Kitaguchi, Hiroto; Jones, Nicholas G.; Mignanelli, Paul M.; Wilson, Alison S.; Messé, Olivier M. D. M.; Pickering, Ed J.; Gilbert, Robert J.; Rae, Cathie M. F.; Yu, Suyang; Evans, Alex; Child, Daniel; Bowen, Paul; Stone, Howard J.

2018-05-01

The effect of Nb on the properties and microstructure of two novel powder metallurgy (P/M) Ni-based superalloys was evaluated, and the results critically compared with the Rolls-Royce alloy RR1000. The Nb-containing alloy was found to exhibit improved tensile and creep properties as well as superior oxidation resistance compared with both RR1000 and the Nb-free variant tested. The beneficial effect of Nb on the tensile and creep properties was due to the microstructures obtained following the post-solution heat treatments, which led to a higher γ' volume fraction and a finer tertiary γ' distribution. In addition, an increase in the anti-phase-boundary energy of the γ' phase is also expected with the addition of Nb, further contributing to the strength of the material. However, these modifications in the γ' distribution detrimentally affect the dwell fatigue crack-growth behavior of the material, although this behavior can be improved through modified heat treatments. The oxidation resistance of the Nb-containing alloy was also enhanced as Nb is believed to accelerate the formation of a defect-free Cr2O3 scale. Overall, both developmental alloys, with and without the addition of Nb, were found to exhibit superior properties than RR1000.

Human alveolar bone cell proliferation, expression of osteoblastic phenotype, and matrix mineralization on porous titanium produced by powder metallurgy.

PubMed

Rosa, Adalberto Luiz; Crippa, Grasiele Edilaine; de Oliveira, Paulo Tambasco; Taba, Mario; Lefebvre, Louis-Philippe; Beloti, Marcio Mateus

2009-05-01

This study aimed at investigating the influence of the porous titanium (Ti) structure on the osteogenic cell behaviour. Porous Ti discs were fabricated by the powder metallurgy process with the pore size typically between 50 and 400 microm and a porosity of 60%. Osteogenic cells obtained from human alveolar bone were cultured until subconfluence and subcultured on dense Ti (control) and porous Ti for periods of up to 17 days. Cultures grown on porous Ti exhibited increased cell proliferation and total protein content, and lower levels of alkaline phosphatase (ALP) activity than on dense Ti. In general, gene expression of osteoblastic markers-runt-related transcription factor 2, collagen type I, alkaline phosphatase, bone morphogenetic protein-7, and osteocalcin was lower at day 7 and higher at day 17 in cultures grown on porous Ti compared with dense Ti, a finding consistent with the enhanced growth rate for such cultures. The amount of mineralized matrix was greater on porous Ti compared with the dense one. These results indicate that the porous Ti is an appropriate substrate for osteogenic cell adhesion, proliferation, and production of a mineralized matrix. Because of the three-dimensional environment it provides, porous Ti should be considered an advantageous substrate for promoting desirable implant surface-bone interactions.

[Atmospheric emission of PCDD/Fs from secondary aluminum metallurgy industry in the southwest area, China].

PubMed

Lu, Yi; Zhang, Xiao-Ling; Guo, Zhi-Shun; Jian, Chuan; Zhu, Ming-Ji; Deng, Li; Sun, Jing; Zhang, Qin

2014-01-01

Five secondary aluminum metallurgy enterprises in the southwest area of China were measured for emissions of PCDD/Fs. The results indicated that the emission levels of PCDD/Fs (as TEQ) were 0.015-0.16 ng x m(-3), and the average was 0.093 ng x m(-3) from secondary aluminum metallurgy enterprises. Emission factors of PCDD/Fs (as TEQ) from the five secondary aluminum metallurgy enterprises varied between 0.041 and 4.68 microg x t(-1) aluminum, and the average was 2.01 microg x t(-1) aluminum; among them, PCDD/Fs emission factors from the crucible smelting furnace was the highest. Congener distribution of PCDD/F in stack gas from the five secondary aluminum metallurgies was very different from each other. Moreover, the R(PCDF/PCDD) was the lowest in the enterprise which was installed only with bag filters; the R(PCDF/PCDD) were 3.8-12.6 (the average, 7.7) in the others which were installed with water scrubbers. The results above indicated that the mechanism of PCDD/Fs formation was related to the types of exhaust gas treatment device. The results of this study can provide technical support for the formulation of PCDD/Fs emission standards and the best available techniques in the secondary aluminum metallurgy industry.

The Reactive Stabilisation of Aluminum-Zinc-X Foams via the Formation of a Transient Liquid Phase Using the Powder Metallurgy Approach

NASA Astrophysics Data System (ADS)

Lafrance, Maxime

During the past few decades, aluminum foam research has focused on the improvement of properties. These properties include pore structure and process reproducibility. High energy absorption capacity, lightweight and high stiffness to weight ratio are some of the properties that make these foams desirable for a number of diverse applications. The use of a transient liquid phase and melting point depressant was studied in order to improve aluminum foam manufactured through the powder metallurgy process and to create reactive Stabilisation. The transient liquid phase reacts with aluminum and helps encapsulate higher levels of hydrogen, simultaneously reducing the difference between the melting point of the alloy and the gas release temperature of the blowing agent (TiH2). A large difference is known to adversely affect foam properties. The study of pure aluminum foam formation was undertaken to understand the basic foaming mechanisms related to crack formations under in-situ conditions. Elemental zinc powder at various concentrations (Al-10wt%Zn, Al-33wt%Zn and Al-50wt%Zn) was added to produce a transient liquid phase. Subsequently, an Al-12wt%Si pre-alloyed powder was added to the Al-Zn mixture in order to further reduce the melting point of the alloy and to increase the amount of transient liquid phase available (Al-3.59wtSi-9.6%Zn and Al-2.4wt%Si-9.7wt%Zn). The mechanical properties of each system at optimal foaming conditions were assessed and compared. It was determined that pure aluminum foam crack formation could be suppressed at higher heating rates, improving the structure through the nucleation of uniform pores. The Al-10wt%Zn foams generated superior pore properties, post maximum expansion stability and mechanical properties at lower temperatures, compared to pure aluminum. The Al-Si-Zn foams revealed remarkable stability and pore structure at very low temperatures (640 to 660°C). Overall, the Al-10wt%Zn and Al-3.59wt%Si-9.6wt%Zn foams offer superior

Study of the mechanical stability and bioactivity of Bioglass(®) based glass-ceramic scaffolds produced via powder metallurgy-inspired technology.

PubMed

Boccardi, Elena; Melli, Virginia; Catignoli, Gabriele; Altomare, Lina; Jahromi, Maryam Tavafoghi; Cerruti, Marta; Lefebvre, Louis-Philippe; De Nardo, Luigi

2016-02-02

Large bone defects are challenging to heal, and often require an osteoconductive and stable support to help the repair of damaged tissue. Bioglass-based scaffolds are particularly promising for this purpose due to their ability to stimulate bone regeneration. However, processing technologies adopted so far do not allow for the synthesis of scaffolds with suitable mechanical properties. Also, conventional sintering processes result in glass de-vitrification, which generates concerns about bioactivity. In this work, we studied the bioactivity and the mechanical properties of Bioglass(®) based scaffolds, produced via a powder technology inspired process. The scaffolds showed compressive strengths in the range of 5-40 MPa, i.e. in the upper range of values reported so far for these materials, had tunable porosity, in the range between 55 and 77%, and pore sizes that are optimal for bone tissue regeneration (100-500 μm). We immersed the scaffolds in simulated body fluid (SBF) for 28 d and analyzed the evolution of the scaffold mechanical properties and microstructure. Even if, after sintering, partial de-vitrification occurred, immersion in SBF caused ion release and the formation of a Ca-P coating within 2 d, which reached a thickness of 10-15 μm after 28 d. This coating contained both hydroxyapatite and an amorphous background, indicating microstructural amorphization of the base material. Scaffolds retained a good compressive strength and structural integrity also after 28 d of immersion (6 MPa compressive strength). The decrease in mechanical properties was mainly related to the increase in porosity, caused by its dissolution, rather than to the amorphization process and the formation of a Ca-P coating. These results suggest that Bioglass(®) based scaffolds produced via powder metallurgy-inspired technique are excellent candidates for bone regeneration applications.

Titanium dental copings prepared by a powder metallurgy method: a preliminary report.

PubMed

Eriksson, Mikael; Andersson, Matts; Carlström, Elis

2004-01-01

The purpose of this study was to determine if the Procera pressed-powder method can be used to fabricate titanium copings. Commercially pure titanium powder was used to prepare the copings. The powder was pressed onto an enlarged tooth preparation die of aluminum using cold isostatic pressing. The outer shape of the coping was formed using a Procera milling machine, and the copings were vacuum sintered. Titanium copings could be prepared using this method. The density of the sintered copings reached 97% to 99%+ of theoretic density, and the copings showed ductile behavior after sintering. Enlarging the tooth preparation die to compensate for the sintering shrinkage could optimize the final size of the copings. Ductile and dense titanium dental copings can be produced with powder-metal processing using cold isostatic pressing, followed by milling and sintering to final shape. The forming technique has, if properly optimized, a potential of becoming a more cost-efficient production method than spark erosion.

Phase identification in boron-containing powder metallurgy steel using EBSD in combination with EPMA

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wu, Ming-Wei, E-mail: mwwu@ntut.edu.tw; Cai, Wen-Zhang

2016-03-15

Boron (B) is extensively used to induce liquid phase sintering (LPS) in powder metallurgy (PM) steels and thereby increase the densification. The alloying elements in B-containing PM steels affect the boride phase, stability of the boride, the temperature of liquid formation, and the progress of LPS. However, the boride phase has not been systematically identified yet. The main objective of this study was to clarify the influences of alloying elements, including C, Cr, and Ni, on the boride phases using electron backscatter diffraction (EBSD) in combination with electron probe microanalysis (EPMA). Network structures consisting of ferrite, Fe{sub 2}B boride, andmore » Fe{sub 3}C carbide were extensively observed in the Fe–0.4B–0.5C steel. The portions of Fe{sub 2}B were sufficiently larger than those of Fe{sub 3}C, and Fe{sub 3}C was mostly distributed at the interfaces between ferrite and Fe{sub 2}B. Adding 1.5 wt.% Cr or 1.8 wt.% Ni to Fe–0.4B–0.5C steel completely changes the Fe{sub 2}B and Fe{sub 3}C phases to a M{sub 3}(B,C) phase, where M represents the metallic elements, including Fe, Cr, Mo, and Ni. Furthermore, Cr, Mo, B, and C atoms tend to concentrate on the M{sub 3}(B,C) phase, but Ni atoms do not. - Highlights: • Network structures consisting of ferrite, Fe{sub 2}B boride, and Fe{sub 3}C carbide were extensively observed in the Fe–0.4B–0.5C steel. • Adding 1.5 wt.% Cr or 1.8 wt.% Ni to Fe–0.4B–0.5C steel completely transforms the Fe{sub 2}B and Fe{sub 3}C phases to a M{sub 3}(B,C) phase. • Cr, Mo, B, and C atoms tend to concentrate on the M{sub 3}(B,C) phase, but Ni atoms do not.« less

Influences of Processing and Fatigue Cycling on Residual Stresses in a NiCrY-Coated Powder Metallurgy Disk Superalloy

NASA Astrophysics Data System (ADS)

Gabb, T. P.; Rogers, R. B.; Nesbitt, J. A.; Miller, R. A.; Puleo, B. J.; Johnson, D.; Telesman, J.; Draper, S. L.; Locci, I. E.

2017-11-01

Oxidation and corrosion can attack superalloy disk surfaces exposed to increasing operating temperatures in some turbine engine environments. Any potential protective coatings must also be resistant to harmful fatigue cracking during service. The objective of this study was to investigate how residual stresses evolve in one such coating. Fatigue specimens of a powder metallurgy-processed disk superalloy were coated with a NiCrY coating, shot peened, and then subjected to fatigue in air at room and high temperatures. The effects of this processing and fatigue cycling on axial residual stresses and other aspects of the coating were assessed. While shot peening did induce beneficial compressive residual stresses in the coating and substrate, these stresses relaxed in the coating with subsequent heating. Several cast alloys having compositions near the coating were subjected to thermal expansion and tensile stress relaxation tests to help explain this response of residual stresses in the coating. For the coated fatigue specimens, this response contributed to earlier cracking of the coating than for the uncoated surface during long intervals of cycling at 760 °C. Yet, substantial compressive residual stresses still remained in the substrate adjacent to the coating, which were sufficient to suppress fatigue cracking there. The coating continued to protect the substrate from hot corrosion pitting, even after fatigue cracks initiated in the coating.

Effect of borides on hot deformation behavior and microstructure evolution of powder metallurgy high borated stainless steel

DOE Office of Scientific and Technical Information (OSTI.GOV)

Zhou, Xuan

To investigate borides effect on the hot deformation behavior and microstructure evolution of powder metallurgy high borated stainless steel, hot compression tests at the temperatures of 950– 1150 °C and the strain rates of 0.01– 10 s{sup −1} were performed. Flow stress curves indicated that borides increased the material's stress level at low temperature but the strength was sacrificed at temperatures above 1100 °C. A hyperbolic-sine equation was used to characterize the dependence of the flow stress on the deformation temperature and strain rate. The hot deformation activation energy and stress exponent were determined to be 355 kJ/mol and 3.2,more » respectively. The main factors leading to activation energy and stress exponent of studied steel lower than those of commercial 304 stainless steel were discussed. Processing maps at the strains of 0.1, 0.3, 0.5, and 0.7 showed that flow instability mainly concentrated at 950– 1150 °C and strain rate higher than 0.6 s{sup −1}. Results of microstructure illustrated that dynamic recrystallization was fully completed at both high temperature-low strain rate and low temperature-high strain rate. In the instability region cracks were generated in addition to cavities. Interestingly, borides maintained a preferential orientation resulting from particle rotation during compression. - Highlights: •The decrement of activation energy was affected by boride and boron solution. •The decrease of stress exponent was influenced by composition and Cottrell atmosphere. •Boride represented a preferential orientation caused by particle rotation.« less

Development and characterization of Powder Metallurgy (PM) 2XXX series Al alloy products and Metal Matrix Composite (MMC) 2XXX Al/SiC materials for high temperature aircraft structural applications

NASA Technical Reports Server (NTRS)

Chellman, D. J.; Gurganus, T. B.; Walker, J. A.

1992-01-01

The results of a series of material studies performed by the Lockheed Aeronautical Systems Company over the time period from 1980 to 1991 are discussed. The technical objective of these evaluations was to develop and characterize advanced aluminum alloy materials with temperature capabilities extending to 350 F. An overview is given of the first five alloy development efforts under this contract. Prior work conducted during the first five modifications of the alloy development program are listed. Recent developments based on the addition of high Zr levels to an optimum Al-Cu-Mg alloy composition by powder metallurgy processing are discussed. Both reinforced and SiC or B4C ceramic reinforced alloys were explored to achieve specific target goals for high temperature aluminum alloy applications.

Mechanical behaviour of pressed and sintered CP Ti and Ti-6Al-7Nb alloy obtained from master alloy addition powder.

PubMed

Bolzoni, L; Weissgaerber, T; Kieback, B; Ruiz-Navas, E M; Gordo, E

2013-04-01

The Ti-6Al-7Nb alloy was obtained using the blending elemental approach with a master alloy and elemental titanium powders. Both the elemental titanium and the Ti-6Al-7Nb powders were characterised using X-ray diffraction, differential thermal analysis and dilatometry. The powders were processed using the conventional powder metallurgy route that includes uniaxial pressing and sintering. The trend of the relative density with the sintering temperature and the microstructural evolution of the materials sintered at different temperatures were analysed using scanning electron microscopy and X-ray diffraction. A minimum sintering temperature of 1200°C has to be used to ensure the homogenisation of the alloying elements and to obtain a pore structure composed of spherical pores. The sintered samples achieve relative density values that are typical for powder metallurgy titanium and no intermetallic phases were detected. Mechanical properties comparable to those specified for wrought Ti-6Al-7Nb medical devices are normally obtained. Therefore, the produced materials are promising candidates for load bearing applications as implant materials. Copyright © 2013 Elsevier Ltd. All rights reserved.

Review of the Methods for Production of Spherical Ti and Ti Alloy Powder

NASA Astrophysics Data System (ADS)

Sun, Pei; Fang, Zhigang Zak; Zhang, Ying; Xia, Yang

2017-10-01

Spherical titanium alloy powder is an important raw material for near-net-shape fabrication via a powder metallurgy (PM) manufacturing route, as well as feedstock for powder injection molding, and additive manufacturing (AM). Nevertheless, the cost of Ti powder including spherical Ti alloy has been a major hurdle that prevented PM Ti from being adopted for a wide range of applications. Especially with the increasing importance of powder-bed based AM technologies, the demand for spherical Ti powder has brought renewed attention on properties and cost, as well as on powder-producing processes. The performance of Ti components manufactured from powder has a strong dependence on the quality of powder, and it is therefore crucial to understand the properties and production methods of powder. This article aims to provide a cursory review of the basic techniques of commercial and emerging methods for making spherical Ti powder. The advantages as well as limitations of different methods are discussed.

XPS and SEM analysis of the surface of gas atomized powder precursor of ODS ferritic steels obtained through the STARS route

NASA Astrophysics Data System (ADS)

Gil, E.; Cortés, J.; Iturriza, I.; Ordás, N.

2018-01-01

An innovative powder metallurgy route to produce ODS FS, named STARS, has succeeded in atomizing steel powders containing the oxide formers (Y and Ti) and, hence, avoids the mechanical alloying (MA) step to dissolve Y in the matrix. A metastable oxide layer forms at the surface of atomized powders and dissociates during HIP consolidation at high temperatures, leading to precipitation of more stable Y-Ti-O nanoparticles.

Ultrasonic hot powder compaction of Ti-6Al-4V.

PubMed

Abedini, Rezvan; Abdullah, Amir; Alizadeh, Yunes

2017-07-01

Power ultrasonic has been recently employed in a wide variety of manufacturing processes among which ultrasonic assisted powder compaction is a promising powder materials processing technique with significant industrial applications. The products manufactured by the powder metallurgy commonly consist of residual porosities, material impurities, structural non-homogeneities and residual stress. In this paper, it is aimed to apply power ultrasonic to the hot consolidation process of Ti-6Al-4V titanium alloy powder in order to improve mechanical properties. To do this, the effects of ultrasonic power and process temperature and pressure were considered and then deeply studied through a series of experiments. It was shown that the addition of ultrasonic vibration leads to a significant improvement in the consolidation performance and the mechanical strength of the fabricated specimens. Copyright © 2017 Elsevier B.V. All rights reserved.

Effect of Pressing Parameters on the Structure of Porous Materials Based on Cobalt and Nickel Powders

NASA Astrophysics Data System (ADS)

Shustov, V. S.; Rubtsov, N. M.; Alymov, M. I.; Ankudinov, A. B.; Evstratov, E. V.; Zelensky, V. A.

2018-03-01

Porous materials with a bulk porosity of more than 68% were synthesized by powder metallurgy methods from a cobalt-nickel mixture. The effect of the ratio of nickel and cobalt powders used in the synthesis of this porous material (including cases when either nickel or cobalt alone was applied) and the conditions of their compaction on structural parameters, such as open and closed porosities and pose size, was established.

Self-passivating bulk tungsten-based alloys manufactured by powder metallurgy

NASA Astrophysics Data System (ADS)

López-Ruiz, P.; Ordás, N.; Lindig, S.; Koch, F.; Iturriza, I.; García-Rosales, C.

2011-12-01

Self-passivating tungsten-based alloys are expected to provide a major safety advantage compared to pure tungsten, which is at present the main candidate material for the first wall armour of future fusion reactors. WC10Si10 alloys were manufactured by mechanical alloying (MA) in a Planetary mill and subsequent hot isostatic pressing (HIP), achieving densities above 95%. Different MA conditions were studied. After MA under optimized conditions, a core with heterogeneous microstructure was found in larger powder particles, resulting in the presence of some large W grains after HIP. Nevertheless, the obtained microstructure is significantly refined compared to previous work. First MA trials were also performed on the Si-free system WCr12Ti2.5. In this case a very homogeneous structure inside the powder particles was obtained, and a majority ternary metastable bcc phase was found, indicating that almost complete alloying occurred. Therefore, a very fine and homogeneous microstructure can be expected after HIP in future work.

Characterization of Plastic Flow Pertinent to the Evolution of Bulk Residual Stress in Powder-Metallurgy, Nickel-Base Superalloys

NASA Astrophysics Data System (ADS)

Semiatin, S. L.; Fagin, P. N.; Goetz, R. L.; Furrer, D. U.; Dutton, R. E.

2015-09-01

The plastic-flow behavior which controls the formation of bulk residual stresses during final heat treatment of powder-metallurgy (PM), nickel-base superalloys was quantified using conventional (isothermal) stress-relaxation (SR) tests and a novel approach which simulates concurrent temperature and strain transients during cooling following solution treatment. The concurrent cooling/straining test involves characterization of the thermal compliance of the test sample. In turn, this information is used to program the ram-displacement- vs-time profile to impose a constant plastic strain rate during cooling. To demonstrate the efficacy of the new approach, SR tests (in both tension and compression) and concurrent cooling/tension-straining experiments were performed on two PM superalloys, LSHR and IN-100. The isothermal SR experiments were conducted at a series of temperatures between 1144 K and 1436 K (871 °C and 1163 °C) on samples that had been supersolvus solution treated and cooled slowly or rapidly to produce starting microstructures comprising coarse gamma grains and coarse or fine secondary gamma-prime precipitates, respectively. The concurrent cooling/straining tests comprised supersolvus solution treatment and various combinations of subsequent cooling rate and plastic strain rate. Comparison of flow-stress data from the SR and concurrent cooling/straining tests showed some similarities and some differences which were explained in the context of the size of the gamma-prime precipitates and the evolution of dislocation substructure. The magnitude of the effect of concurrent deformation during cooling on gamma-prime precipitation was also quantified experimentally and theoretically.

Structure investigations of ferromagnetic Co-Ni-Al alloys obtained by powder metallurgy.

PubMed

Maziarz, W; Dutkiewicz, J; Lityńska-Dobrzyńska, L; Santamarta, R; Cesari, E

2010-03-01

Elemental powders of Co, Ni and Al in the proper amounts to obtain Co(35)Ni(40)Al(25) and Co(40)Ni(35)Al(25) nominal compositions were ball milled in a high-energy mill for 80 h. After 40 h of milling, the formation of a Co (Ni, Al) solid solution with f.c.c. structure was verified by a change of the original lattice parameter and crystallite size. Analytical transmission electron microscopy observations and X-ray diffraction measurements of the final Co (Ni, Al) solid solution showed that the crystallite size scattered from 4 to 8 nm and lattice parameter a = 0.36086 nm. The chemical EDS point analysis of the milled powder particles allowed the calculation of the e/a ratio and revealed a high degree of chemical homogeneity of the powders. Hot pressing in vacuum of the milled powders resulted in obtaining compacts with a density of about 70% of the theoretical one. An additional heat treatment increased the density and induced the martensitic transformation in a parent phase. Selected area diffraction patterns and dark field images obtained from the heat-treated sample revealed small grains around 300 nm in diameter consisting mainly of the ordered gamma phase (gamma'), often appearing as twins, and a small amount of the L1(0) ordered martensite.

Net-Shape HIP Powder Metallurgy Components for Rocket Engines

NASA Technical Reports Server (NTRS)

Bampton, Cliff; Goodin, Wes; VanDaam, Tom; Creeger, Gordon; James, Steve

2005-01-01

True net shape consolidation of powder metal (PM) by hot isostatic pressing (HIP) provides opportunities for many cost, performance and life benefits over conventional fabrication processes for large rocket engine structures. Various forms of selectively net-shape PM have been around for thirty years or so. However, it is only recently that major applications have been pursued for rocket engine hardware fabricated in the United States. The method employs sacrificial metallic tooling (HIP capsule and shaped inserts), which is removed from the part after HIP consolidation of the powder, by selective acid dissolution. Full exploitation of net-shape PM requires innovative approaches in both component design and materials and processing details. The benefits include: uniform and homogeneous microstructure with no porosity, irrespective of component shape and size; elimination of welds and the associated quality and life limitations; removal of traditional producibility constraints on design freedom, such as forgeability and machinability, and scale-up to very large, monolithic parts, limited only by the size of existing HIP furnaces. Net-shape PM HIP also enables fabrication of complex configurations providing additional, unique functionalities. The progress made in these areas will be described. Then critical aspects of the technology that still require significant further development and maturation will be discussed from the perspective of an engine systems builder and end-user of the technology.

Additively Manufactured, Net Shape Powder Metallurgy Cans for Valves Used in Energy Production

DOE Office of Scientific and Technical Information (OSTI.GOV)

Peter, William H.; Gandy, David; Lannom, Robert

This CRADA NFE-14-05241 was conducted as a Technical Collaboration project within the Oak Ridge National Laboratory (ORNL) Manufacturing Demonstration Facility (MDF) sponsored by the US Department of Energy Advanced Manufacturing Office (CPS Agreement Number 24761). Opportunities for MDF technical collaborations are listed in the announcement “Manufacturing Demonstration Facility Technology Collaborations for US Manufacturers in Advanced Manufacturing and Materials Technologies” posted at http://web.ornl.gov/sci/manufacturing/docs/FBO-ORNL-MDF-2013-2.pdf. The goal of technical collaborations is to engage industry partners to participate in short-term, collaborative projects within the Manufacturing Demonstration Facility (MDF) to assess applicability and of new energy efficient manufacturing technologies. Research sponsored by the U.S. Departmentmore » of Energy, Office of Energy Efficiency and Renewable Energy, Advanced Manufacturing Office, under contract DE-AC05-00OR22725 with UT-Battelle, LLC.ORNL would like to acknowledge the leadership of EPRI in pulling together the extensive team and managing the execution of the project. In addition, ORNL would like to acknowledge the other contributions of the team members associated with this project. Quintus provided time, access, expertise, and labor of their hydro forming capabilities to evaluate both conventional and additively manufactured tools through this process. Crane ChemPharma Energy provided guidance and information on valve geometries. Carpenter Powder Products was involved with the team providing information on powder processing as it pertains to the canning and hot isostatic pressing of powder. on providing powder and knowledge as it pertains to powder supply for hot isostatic pressing; they also provided powder for the test trials by the industrial team. Bodycote provided guidance on hot isostatic pressing and can requirements. They were also responsible for the hot isostatic pressing of the test

Reduction of fecal parasites by Arecha catechu L. seed and Anredera cordifolia (Ten) Steenis leaves powder in laying hens

NASA Astrophysics Data System (ADS)

Kusumanti, Endang; Murwani, Retno

2018-02-01

Arecha catechu L (bettle nut) seed and Anredera cordifolia (Ten) Steenis (“Binahong”) have been shown to have anti helmintic and wound healing activities respectively. Their combine use as phytogenic additives in layers have been shown to reduce serum transaminase. Further study was conducted to evaluate the effect of A. catechu seed and A. cordifolia leaves powder supplementation on fecal parasites number and the performance of laying hens obtained from outdoor small scale layer farmers. Forty eight of 42 weeks old laying hens were allocated randomly into 4 treatment groups i.e. no supplementation (T0), supplemented with 0.025% A. catechu seed and A. cordifolia leaves powder (T0.025%), 0.05% A. catechu seed and A. cordifolia leaves powder (T0.05%), 0.1% A. catechu seed and A. cordifolia leaves powder (T0.1%). Each treatment consisted of six replicates with two hens per replicate. Supplementation were carried out by administering alternately A. catechu seed powder for 3 days followed by A. cordifolia leaves powder for another 3 days. The alternate supplementation for each groups was conducted for 18 days. Feed consumption, egg production, egg weight, hen day production (HDP) were recorded daily. Parasites counts were sampled and enumerated at the beginning and at the end of supplementation. The result showed that alternate supplementation of 0.0.025% A. catechu seed and A. cordifolia leaves powder up to 18 days to 42 weeks old laying hens reduced fecal parasites without affecting performance.

Sol-gel synthesis and characterizations of crystalline NaGd(WO4)2 powder for anisotropic transparent ceramic laser application

NASA Astrophysics Data System (ADS)

Durairajan, A.; Thangaraju, D.; Balaji, D.; Moorthy Babu, S.

2013-02-01

NaGd(WO4)2 powders were synthesized at different pH (3.5, 4.5, 5.5, 6.5 and 7.5) values by conventional Pechini method. Sodium and gadolinium nitrate salts and ammonium paratungstate are used as starting precursors. Metal cations were chelated by citric acid and individual citrates were bound together with ethylene glycol. Synthesized gel was analyzed using differential thermal analysis (DTA), thermo gravimetric (TG) and FT-IR spectroscopy to understand the degradation of gel and formation of metal citrates. Calcined powders (250, 600, 700 and 800 °C) were characterized by powder XRD, FT-IR, Raman and FE-SEM analysis. The temperature dependent phase formation was examined by powder XRD. The morphological changes at different pH derived powders were observed with FE-SEM micrographs. Stepwise organic liberation with respect to temperature and presence of carbon content in the pre-fired powder were analyzed using FT-IR analysis. Raman spectrum reveals disordered tungstate vibrations in the NGW matrix.

Properties of boride-added powder metallurgy magnesium alloys

NASA Astrophysics Data System (ADS)

Tanaka, Atsushi; Yoshimura, Syota; Fujima, Takuya; Takagi, Ken-ichi

2009-06-01

Magnesium alloys with metallic borides, magnesium diboride (MgB2) or aluminum diboride (AlB2), were investigated regarding their mechanical properties, transverse rupture strength (TRS) and micro Vickers hardness (HV). The alloys were made from pure Mg, Al and B powders by mechanical alloying and hot pressing to have boride content of between 2.0 and 20 vol%. The alloy with AlB2 exhibited an obvious improvement of HV around a boride content of 6 vol% though the other alloy, with MgB2, did not. TRS showed moderate maxima around the same boride content region for the both alloys. X-ray diffraction measurements indicated an intermetallic compound, Mg17Al12, formed in the alloy with AlB2, which was consistent with its higher hardness.

The metallurgy and processing science of metal additive manufacturing

DOE PAGES

Sames, William J.; List, III, Frederick Alyious; Pannala, Sreekanth; ...

2016-03-07

Here, additive Manufacturing (AM), widely known as 3D printing, is a method of manufacturing that forms parts from powder, wire, or sheets in a process that proceeds layer-by-layer.Many techniques (using many different names) have been developed to accomplish this via melting or solid - state joining. In this review, these techniques for producing metal parts are explored, with a focus on the science of metal AM: processing defects, heat transfer, solidification, solid- state precipitation, mechanical properties, and post-processing metallurgy. The various metal AM techniques are compared, with analysis of the strengths and limitations of each. Few alloys have been developedmore » for commercial production, but recent development efforts are presented as a path for the ongoing development of new materials for AM processes.« less

Mechanical Properties of Mg2Si/Mg Composites via Powder Metallurgy Process

NASA Astrophysics Data System (ADS)

Muramatsu, Hiroshi; Kondoh, Katsuyoshi; Yuasa, Eiji; Aizawa, Tatsuhiko

The mechanical properties of the Mg2Si/Mg composites solid-state synthesized from the mixed Mg-Si powders have been investigated. The macro-hardness (HRE) and the tensile strength of the composites increase with increasing the Si content and decreasing the Si size. The particle size of the synthesized Mg2Si depends on the initial Si size; the mechanical properties of the Mg2Si/Mg composite are remarkably improved by using fine Si particles or by decreasing the grain size of Mg matrix grains when the powder mixture was prepared via bulk mechanical alloying process.

Fluidized reduction of oxides on fine metal powders without sintering

NASA Technical Reports Server (NTRS)

Hayashi, T.

1985-01-01

In the process of reducing extremely fine metal particles (av. particle size or = 1000 angstroms) covered with an oxide layer, the metal particles are fluidized by a gas flow contg. H, heated, and reduced. The method uniformly and easily reduces surface oxide layers of the extremely fine metal particles without causing sintering. The metal particles are useful for magnetic recording materials, conductive paste, powder metallurgy materials, chem. reagents, and catalysts.

USSR and Eastern Europe Scientific Abstracts, Materials Science and Metallurgy, Number 42.

DTIC Science & Technology

1977-01-27

Films 37 Titanium 38 Welding • • 42 Miscellaneous 43 -a - [III - USSR - 21- G S & T] Aluminum and Its Alloys USSR UDC 669.715:621.74...GAYNUTDINOV, R. G . and GOLUBNICHIY, A. V., Kiev Institute of Civil Aviation Engineering [Abstract] Results are presented from a study of the influence of...Sep-Oct 76 pp 38-41 manuscript received 16 Jul 75 TELESHOV, V. V. and KUDRYASHOV, V. G ., All-Union Institute of Light Alloys, Moscow [Abstract] A

Microstructure evolution and dynamic recrystallization behavior of a powder metallurgy Ti-22Al-25Nb alloy during hot compression

DOE Office of Scientific and Technical Information (OSTI.GOV)

Jia, Jianbo

The flow behavior of a powder metallurgy (P/M) Ti-22Al-25Nb alloy during hot compression tests has been investigated at a strain rate of 0.01 s{sup −1} and a temperature range of 980–1100 °C up to various true strains from 0.1 to 0.9. The effects of deformation temperature and strain on microstructure characterization and nucleation mechanisms of dynamic recrystallization (DRX) were assessed by means of Optical microscope (OM), electron backscatter diffraction (EBSD) and transmission electron microscope (TEM) techniques, respectively. The results indicated that the process of DRX was promoted by increasing deformation temperature and strain. By regression analysis, a power exponent relationshipmore » between peak stresses and sizes of stable DRX grains was developed. In addition, it is suggested that the discontinuous dynamic recrystallization (DDRX) and continuous dynamic recrystallization (CDRX) controlled nucleation mechanisms for DRX grains operated simultaneously during the whole hot process, and which played the leading role varied with hot process parameters of temperature and strain. It was further demonstrated that the CDRX featured by progressive subgrain rotation was weakened by elevating deformation temperatures. - Highlights: •Flow behavior of a P/M Ti-22Al-25Nb is studied by hot compression tests. •Microstructure evolution of alloy is affected by deformation temperature and strain. •The relationship between peak stress and stable DRX grain size was developed. •The process of DRX was promoted by increasing deformation temperature and strain. •Nucleation mechanisms of DRX were identified by EBSD analysis and TEM observation.« less

A Nonvolume Preserving Plasticity Theory with Applications to Powder Metallurgy

NASA Technical Reports Server (NTRS)

Cassenti, B. N.

1983-01-01

A plasticity theory has been developed to predict the mechanical response of powder metals during hot isostatic pressing. The theory parameters were obtained through an experimental program consisting of hydrostatic pressure tests, uniaxial compression and uniaxial tension tests. A nonlinear finite element code was modified to include the theory and the results of themodified code compared favorably to the results from a verification experiment.

Comparing Microstructures and Tensile Properties of Intercritically Annealed and Quenched-Tempered 1.7Ni-1.5Cu-0.5Mo-0.2C Powder Metallurgy Steels

NASA Astrophysics Data System (ADS)

Güral, Ahmet; Başak, Hüdayim; Türkan, Mustafa

2018-01-01

The aim of this study was to compare the influence of intercritical quenching (IQ), step quenching (SQ) and quenching plus tempering (QT) heat treatments on the microstructure and tensile properties of 1.7Ni-1.5Cu-0.5Mo-0.2C pre-alloyed powder metallurgy (P/M) steels. In the microstructures of the IQ and SQ specimens partial martensite having Ni-rich phases formed up in the soft ferritic matrix. It was observed that unlike Mo, a Cu alloying element dissolved homogeneously in the specimens. The martensite volume fraction (MVF) in the SQ specimens was higher than that in the IQ specimens. It was found that macrohardness, yield and tensile strengths increased, whereas microhardness of ferrite and elongation decreased with increasing MVF. However, with this increase, microhardness values of martensite phases decreased in the IQ specimen, while they increased in SQ specimens. It was observed that the yield, tensile, and elongation values of the QT specimens were lower than those of all intercritically annealed specimens having the same hardness values.

Enery Efficient Press and Sinter of Titanium Powder for Low-Cost Components in Vehicle Applications

DOE Office of Scientific and Technical Information (OSTI.GOV)

Thomas Zwitter; Phillip Nash; Xiaoyan Xu

2011-03-31

This is the final technical report for the Department of Energy NETL project NT01931 Energy Efficient Press and Sinter of Titanium Powder for Low-Cost Components in Vehicle Applications. Titanium has been identified as one of the key materials with the required strength that can reduce the weight of automotive components and thereby reduce fuel consumption. Working with newly developed sources of titanium powder, Webster-Hoff will develop the processing technology to manufacture low cost vehicle components using the single press/single sinter techniques developed for iron based powder metallurgy today. Working with an automotive or truck manufacturer, Webster-Hoff will demonstrate the feasibilitymore » of manufacturing a press and sinter titanium component for a vehicle application. The project objective is two-fold, to develop the technology for manufacturing press and sinter titanium components, and to demonstrate the feasibility of producing a titanium component for a vehicle application. The lowest cost method for converting metal powder into a net shape part is the Powder Metallurgy Press and Sinter Process. The method involves compaction of the metal powder in a tool (usually a die and punches, upper and lower) at a high pressure (up to 60 TSI or 827 MPa) to form a green compact with the net shape of the final component. The powder in the green compact is held together by the compression bonds between the powder particles. The sinter process then converts the green compact to a metallurgically bonded net shape part through the process of solid state diffusion. The goal of this project is to expand the understanding and application of press and sinter technology to Titanium Powder applications, developing techniques to manufacture net shape Titanium components via the press and sinter process. In addition, working with a vehicle manufacturer, demonstrate the feasibility of producing a titanium component for a vehicle. This is not a research program, but

Estimation and characterization of PCDD/Fs, dl-PCBs, PCNs, HxCBz and PeCBz emissions from magnesium metallurgy facilities in China.

PubMed

Nie, Zhiqiang; Zheng, Minghui; Liu, Wenbin; Zhang, Bing; Liu, Guorui; Su, Guijin; Lv, Pu; Xiao, Ke

2011-12-01

Magnesium production is considered to be one potential source of unintentional persistent organic pollutants (unintentional POPs). However, studies on the emissions of unintentional POPs from magnesium metallurgy are still lacking. Emissions of unintentional POPs, such as polychlorinated dibenzo-p-dioxins/dibenzofurans (PCDD/Fs), dioxin-like polychlorinated biphenyls (dl-PCBs), polychlorinated naphthalenes (PCNs), hexachlorobenzene (HxCBz) and pentachlorobenzene (PeCBz) are covered under the Stockholm Convention. In this study, these emissions were investigated through a magnesium smelting process. Stack gas and fly ash samples from a typical magnesium plant in China were collected and analyzed to estimate the emissions of unintentional POPs from magnesium metallurgy. Emissions factors of 412 ng TEQ t(-1) for PCDD/Fs, 18.6 ng TEQ t(-1) for dl-PCBs, 3329 μg t(-1) for PCNs, 820 μg t(-1) for HxCBz, and 1326 μg t(-1) for PeCBz were obtained in 2009. Annual emissions from magnesium metallurgy in China were estimated to be 0.46 g WHO-TEQ for PCDD/Fs and dl-PCBs, 1651 g for PCNs, 403 g for HxCBz and 653 g for PeCBz, respectively. Copyright © 2011 Elsevier Ltd. All rights reserved.

Powder metallurgy processing of high strength turbine disk alloys

NASA Technical Reports Server (NTRS)

Evans, D. J.

1976-01-01

Using vacuum-atomized AF2-1DA and Mar-M432 powders, full-scale gas turbine engine disks were fabricated by hot isostatically pressing (HIP) billets which were then isothermally forged using the Pratt & Whitney Aircraft GATORIZING forging process. While a sound forging was produced in the AF2-1DA, a container leak had occurred in the Mar-M432 billet during HIP. This resulted in billet cracking during forging. In-process control procedures were developed to identify such leaks. The AF2-1DA forging was heat treated and metallographic and mechanical property evaluation was performed. Mechanical properties exceeded those of Astroloy, one of the highest temperature capability turbine disk alloys presently used.

Correlations between the in vitro and in vivo bioactivity of the Ti/HA composites fabricated by a powder metallurgy method.

PubMed

Ning, Congqin; Zhou, Yu

2008-11-01

Ti/HA composites were successfully prepared by a powder metallurgy method and the effect of phase composition on the in vitro and in vivo bioactivity of the Ti/HA composites was investigated in the present study. The correlations between the in vitro and in vivo biological behaviors were highlighted. The results showed that the in vitro and in vivo bioactivity of the Ti/HA composites was dependent on their phase composition. The in vitro bioactivity of the Ti/HA composites was evaluated in simulated body fluid with ion concentrations similar to those of human plasma. After immersion in the simulated body fluid for a certain time, apatite precipitations formed on the surface of the composites with an initial titanium content of 50 and 70 wt.%, and no apatite was found on the surface of the composite with 30% titanium. Ti(2)O was responsible for the apatite formation on the surfaces of the composites. For in vivo analysis, Ti/HA cylinders were implanted in the metaphases of the rabbit femur. At the early stage of implantation, the new bone formed on the surface of the composite with 30% titanium was much less than that on the surfaces of the composites with 50% and 70% titanium. All the Ti/HA composites formed a chemical bone-bonding interface with the host bone by 6 months after implantation. The Ti/HA composites formed the bone-bonding interface with the surrounding bone through an apatite layer. The results in the present study suggested that the in vivo results agreed well with the in vitro results.

Effect of Cu addition on the martensitic transformation of powder metallurgy processed Ti–Ni alloys

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kim, Yeon-wook, E-mail: ywk@gw.kmu.ac.kr; Choi, Eunsoo

2014-10-15

Highlights: • M{sub s} of Ti{sub 50}Ni{sub 50} powders is 22 °C, while M{sub s} of SPS-sintered porous bulk increases up to 50 °C. • M{sub s} of Ti{sub 50}Ni{sub 40}Cu{sub 20} porous bulk is only 2 °C higher than that of the powders. • Recovered stain of porous TiNi and TiNiCu alloy is more than 1.5%. - Abstract: Ti{sub 50}Ni{sub 50} and Ti{sub 50}Ni{sub 30}Cu{sub 20} powders were prepared by gas atomization and their transformation behaviors were examined by means of differential scanning calorimetry and X-ray diffraction. One-step B2–B19’ transformation occurred in Ti{sub 50}Ni{sub 50} powders, while Ti{sub 50}Ni{submore » 30}Cu{sub 20} powders showed B2–B19 transformation behavior. Porous bulks with 24% porosity were fabricated by spark plasma sintering. The martensitic transformation start temperature (50 °C) of Ti{sub 50}Ni{sub 50} porous bulk is much higher than that (22 °C) of the as-solidified powders. However, the martensitic transformation start temperature (35 °C) of Ti{sub 50}Ni{sub 30}Cu{sub 20} porous bulk is almost the same as that (33 °C) of the powders. When the specimens were compressed to the strain of 8% and then unloaded, the residual strains of Ti{sub 50}Ni{sub 50} and Ti{sub 50}Ni{sub 30}Cu{sub 20} alloy bulks were 3.95 and 3.7%, respectively. However, these residual strains were recovered up to 1.7% after heating by the shape memory phenomenon.« less

Surpassing the Theoretical Limit of Porosity in Conventional Solid-State Foaming: Microstructure Characterization of Length Scales in a Copper Metal Foam

DTIC Science & Technology

2014-11-01

powder metallurgy processes (e.g., using a polymer foam as a fugitive template7) can exceed 85% porosity, it is more common for powder metallurgy ...for the 0.5 GPa compact is a remarkable result from a powder metallurgy process, especially because the pore structure is not dominated by necks...strengths in bulk engineering structures produced via powder metallurgy . Completely unique to this process is the ability to create foamed powder . This

Powder metallurgy of Ge, Si, and Ge-Si

NASA Astrophysics Data System (ADS)

Schilz, Jürgen; Langenbach, Marion

1993-03-01

id="ab1"Planetary ball-milling and pressing behaviour of Ge, Si and Ge-Si powder mixtures are investigated. Scanning and transmission electron microscopy observations revealed the different microstructure of the two elements after milling: Ge remains in a microcrystalline state, whereas Si can be comminuted into grains consisting of nanocrystalline regions. Planetary milling of the two elements together, using agate balls and vial, did not reveal any compound formation. By hot-isostatic pressing, pure Ge and Ge-Si mixtures were densified to a higher value than pure Si. This denotes a plastic flow of the Ge component at a process temperature of 800°C. The microhardness of hot-pressed Ge reaches the bulk value; hot-pressed Si is very soft. Energy dispersive X-ray analysis and X-ray diffraction did not detect any impurity contamination from vial and milling media wear. Moreover, by electrical transport measurements it turned out that the net carrier concentration density resulting from electrical active impurities introduced by the milling and pressing process is below 2 x 1016 cm 3 at room temperature.

Powder metallurgy processing and deformation characteristics of bulk multimodal nickel

DOE Office of Scientific and Technical Information (OSTI.GOV)

Farbaniec, L., E-mail: lfarban1@jhu.edu; Dirras, G., E-mail: dirras@univ-paris13.fr; Krawczynska, A.

2014-08-15

Spark plasma sintering was used to process bulk nickel samples from a blend of three powder types. The resulting multimodal microstructure was made of coarse (average size ∼ 135 μm) spherical microcrystalline entities (the core) surrounded by a fine-grained matrix (average grain size ∼ 1.5 μm) or a thick rim (the shell) distinguishable from the matrix. Tensile tests revealed yield strength of ∼ 470 MPa that was accompanied by limited ductility (∼ 2.8% plastic strain). Microstructure observation after testing showed debonding at interfaces between the matrix and the coarse entities, but in many instances, shallow dimples within the rim weremore » observed indicating local ductile events in the shell. Dislocation emission and annihilation at grain boundaries and twinning at crack tip were the main deformation mechanisms taking place within the fine-grained matrix as revealed by in-situ transmission electron microscopy. Estimation of the stress from loop's curvature and dislocation pile-up indicates that dislocation emission from grain boundaries and grain boundary overcoming largely contributes to the flow stress. - Highlights: • Bulk multi-modal Ni was processed by SPS from a powder blend. • Ultrafine-grained matrix or rim observed around spherical microcrystalline entities • Yield strength (470 MPa) and ductility (2.8% plastic strain) were measured. • Debonding was found at the matrix/microcrystalline entity interfaces. • In-situ TEM showed twinning, dislocation emission and annihilation at grain boundaries.« less

Compact Process for the Preparation of Microfine Spherical High-Niobium-Containing TiAl Alloy Powders

NASA Astrophysics Data System (ADS)

Tong, J. B.; Lu, X.; Liu, C. C.; Wang, L. N.; Qu, X. H.

2015-03-01

High-Nb-containing TiAl alloys are a new generation of materials for high-temperature structural applications because of their superior high-temperature mechanical properties. The alloy powders can be widely used for additive manufacturing, thermal spraying, and powder metallurgy. Because of the difficulty of making microfine spherical alloy powders in quantity by conventional techniques, a compact method was proposed, which consisted of two-step ball milling of elemental powders and subsequent radio frequency (RF) argon plasma spheroidization. In comparison with conventional mechanical alloying techniques, the two-step milling process can be used to prepare alloy powders with uniform scale in a short milling time with no addition of process control agent. This makes the process effective and less contaminating. After RF argon plasma spheroidization, the powders produced exhibit good sphericity, and the number-average diameter is about 8.2 μm with a symmetric unimodal particle size distribution. The powders perform high composition homogeneity and contain predominately supersaturated α 2-Ti3Al phase. The oxygen and carbon contents of the spheroidized powder are 0.47% and 0.050%, respectively.

Development of superalloys by powder metallurgy for use at 1000 - 1400 F

NASA Technical Reports Server (NTRS)

Calhoun, C. D.

1971-01-01

Consolidated powders of four nickel-base superalloys were studied for potential application as compressor and turbine discs in jet engines. All of the alloys were based on the Rene' 95 chemistry. Three of these had variations in carbon and A12O3 contents, and the fourth alloy was chemically modified to a higher volume fraction. The A12O3 was added by preoxidation of the powders prior to extrusion. Various levels of four experimental factors (1) alloy composition, (2) grain size, (3) thermomechanical processing, and (4) room temperature deformation plus final age were evaluated by tensile and stress rupture testing at 1200 F. Various levels of the four factors were assumed in order to construct the statistically-designed experiment, but the actual levels investigated were established in preliminary studies that preceded the statistical process development study.

The extractive metallurgy of gold

NASA Astrophysics Data System (ADS)

Kongolo, K.; Mwema, M. D.

1998-12-01

Mössbauer spectroscopy has been successfully used in investigation of the gold compounds present in ores and the gold species which occur during the process metallurgy of this metal. This paper is a survey of the basic recovery methods and techniques used in extractive metallurgy of gold. Process fundamentals on mineral processing, ore leaching, zinc dust cementation, adsorption on activated carbon, electrowinning and refining are examined. The recovery of gold as a by-product of the copper industry is also described. Alternative processing methods are indicated in order to shed light on new interesting research topics where Mössbauer spectroscopy could be applied.

Application of powder metallurgy to an advanced-temperature nickel-base alloy, NASA-TRW 6-A

NASA Technical Reports Server (NTRS)

Freche, J. C.; Ashbrook, R. L.; Waters, W. J.

1971-01-01

Bar stock of the NASA-TRW 6-A alloy was made by prealloyed powder techniques and its properties evaluated over a range of temperatures. Room temperature ultimate tensile strength was 1894 MN/sq m (274 500 psi). The as-extruded powder product showed substantial improvements in strength over the cast alloy up to 649 C (1200 F) and superplasticity at 1093 C (2000 F). Both conventional and autoclave heat treatments were applied to the extruded powder product. The conventional heat treatment was effective in increasing rupture life at 649 and 704 C (1200 and 1300 F); the autoclave heat treatment, at 760 and 816 C (1400 and 1500 F).

Effect of Surface Densification on the Microstructure and Mechanical Properties of Powder Metallurgical Gears by Using a Surface Rolling Process

PubMed Central

Peng, Jingguang; Zhao, Yan; Chen, Di; Li, Kiade; Lu, Wei; Yan, Biao

2016-01-01

Powder metallurgy (PM) components are widely used in the auto industry due to the advantage of net-shape forming, low cost, and high efficiency. Still, usage of PM components is limited in the auto industry when encountering rigorous situations, like heavy load, due to lower strength, hardness, wear resistance, and other properties compared to wrought components due to the existence of massive pores in the PM components. In this study, through combining the powder metallurgy process and rolling process, the pores in the PM components were decreased and a homogenous densified layer was formed on the surface, which resulted in the enhancement of the strength, hardness, wear resistance, and other properties, which can expand its range of application. In this paper, we study the impact of different rolling feeds on the performance of the components’ surfaces. We found that with the increase of the rolling feed, the depth of the densified layer increased. PMID:28773970

Effect of Surface Densification on the Microstructure and Mechanical Properties of Powder Metallurgical Gears by Using a Surface Rolling Process.

PubMed

Peng, Jingguang; Zhao, Yan; Chen, Di; Li, Kiade; Lu, Wei; Yan, Biao

2016-10-19

Powder metallurgy (PM) components are widely used in the auto industry due to the advantage of net-shape forming, low cost, and high efficiency. Still, usage of PM components is limited in the auto industry when encountering rigorous situations, like heavy load, due to lower strength, hardness, wear resistance, and other properties compared to wrought components due to the existence of massive pores in the PM components. In this study, through combining the powder metallurgy process and rolling process, the pores in the PM components were decreased and a homogenous densified layer was formed on the surface, which resulted in the enhancement of the strength, hardness, wear resistance, and other properties, which can expand its range of application. In this paper, we study the impact of different rolling feeds on the performance of the components' surfaces. We found that with the increase of the rolling feed, the depth of the densified layer increased.

Comparison of the microstructure and phase stability of as-cast, CAD/CAM and powder metallurgy manufactured Co-Cr dental alloys.

PubMed

Li, Kai Chun; Prior, David J; Waddell, J Neil; Swain, Michael V

2015-12-01

The objective of this study was to identify the different microstructures produced by CC, PM and as-cast techniques for Co-Cr alloys and their phase stability following porcelain firings. Three bi-layer porcelain veneered Co-Cr specimens and one monolithic Co-Cr specimen of each alloy group [cast, powder metallurgy (PM), CAD/CAM (CC)] were manufactured and analyzed using electron backscatter diffraction (EBSD), energy dispersive spectrometry (EDS) and X-ray diffraction (XRD). Specimens were treated to incremental numbers of porcelain firings (control 0, 5, 15) with crystallographic data, grain size and chemical composition subsequently obtained and analyzed. EBSD datasets of the cast alloy indicated large grains >200 μm whereas PM and CC alloy consisted of mean arithmetic grain sizes of 29.6 μm and 19.2 μm respectively. XRD and EBSD results both indicated the highest increase in hcp content (>13vol%) for cast Co-Cr alloy after treatment with porcelain firing while PM and CC indicated <2vol% hcp content. A fine grain interfacial layer developed on all surfaces of the alloy after porcelain firing. The depth of this layer increased with porcelain firings for as-cast and PM but no significant increase (p>.05) was observed in CC. EDS line scans indicated an increase in Cr content at the alloy surface after porcelain firing treatment for all three alloys. PM and CC produced alloy had superior fcc phase stability after porcelain firings compared to a traditional cast alloy. It is recommended that PM and CC alloys be used for porcelain-fused-to-metal restorations. Copyright © 2015 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Influence of different grained powders and pellets made of Niobium and Ti-42Nb on human cell viability.

PubMed

Markhoff, Jana; Weinmann, Markus; Schulze, Christian; Bader, Rainer

2017-04-01

Nowadays, biomaterials can be used to maintain or replace several functions of the human body if necessary. Titanium and its alloys, i.e. Ti6Al4V are the most common materials (70 to 80%) used for structural orthopedic implants due to their unique combination of good mechanical properties, corrosion resistance and biocompatibility. Addition of β-stabilizers, e.g. niobium, can improve the mechanical properties of such titanium alloys further, simultaneously offering excellent biocompatibility. In this in vitro study, human osteoblasts and fibroblasts were cultured on different niobium specimens (Nb Amperit, Nb Ampertec), Nb sheets and Ti-42Nb (sintered and 3D-printed by selective laser melting, SLM) and compared with forged Ti6Al4V specimens. Furthermore, human osteoblasts were incubated with particulates of the Nb and Ti-42Nb specimens in three concentrations over four and seven days to imitate influence of wear debris. Thereby, the specimens with the roughest surfaces, i.e. Ti-42Nb and Nb Ampertec, revealed excellent and similar results for both cell types concerning cell viability and collagen synthesis superior to forged Ti6Al4V. Examinations with particulate debris disclosed a dose-dependent influence of all powders with Nb Ampertec showing the highest decrease of cell viability and collagen synthesis. Furthermore, interleukin synthesis was only slightly increased for all powders. In summary, Nb Ampertec (sintered Nb) and Ti-42Nb materials seem to be promising alternatives for medical applications compared to common materials like forged or melted Ti6Al4V. Copyright © 2016 Elsevier B.V. All rights reserved.

Production of fine calcium powders by centrifugal atomization with rotating quench bath

DOE PAGES

Tian, Liang; Ames Lab. and Iowa State Univ., Ames, IA; Anderson, Iver; ...

2016-02-08

Recently, a novel Al/Ca composite was produced by severe plastic deformation of Al powders and Ca granules for possible use as a high-voltage power transmission conductor. Since the strength of such composites is inversely proportional to the Ca filament size, fine Ca powders (less than ~250 μm) are needed to achieve the desired high strength for the powder metallurgy production of an Al-matrix composite reinforced by nano-scale Ca filaments. However, fine Ca powders are not commercially available. Therefore, we have developed a method to produce fine Ca powders via centrifugal atomization to supply Ca powder for prototype development of Al/Camore » composite conductor. A secondary goal of the project was to demonstrate that Ca powder can be safely prepared, stored, and handled and could potentially be scaled for commercial production. Our results showed that centrifugal atomization can yield as much as 83 vol. % Ca powder particles smaller than 250 μm. The mean particle size sometimes matches, sometimes deviates substantially from the predictions of the Champagne & Anger equation likely due to unexpected secondary atomization. The particle size distribution is typical for a ligament-disintegration atomization mode. Scanning electron micrographs showed that the morphology of these Ca powders varied with powder size. Spark testing and auto-ignition tests indicated that the atomized powders were difficult to ignite, providing confidence that this material can be handled safely in air.« less

Ballistic Characterization of the Scalability of Magnesium Alloy AMX602

DTIC Science & Technology

2015-07-01

Powder Metallurgy 4 5. Fabrication Procedure 4 6. Mechanical Property Analysis 5 7. Ballistic Experimental Procedures 6 8. Ballistic Experimental...compositions of noncombustive Mg alloy powders 4. Powder Metallurgy The powder was consolidated at room temperature using a 2,000-kN hydraulic press...evaluation of advanced powder metallurgy magnesium alloys for dynamic applications. Aberdeen Proving Ground (MD): Army Research Laboratory (US); 2009 May

Physical Metallurgy of Rene 65, a Next-Generation Cast and Wrought Nickel Superalloy for use in Aero Engine Components

NASA Astrophysics Data System (ADS)

Wessman, Andrew Ezekiel

Advancements in the design of turbine engines are in large part made possible by advancements in the capability of nickel based superalloys. Greater temperature and stress capabilities in these materials allow for increased operating temperatures and speeds in the engines, which lead to increased fuel efficiency. Early jet engines were built using austenitic stainless steels, and moved to cast and wrought nickel alloys as higher temperatures were required. By the 1970s, the state of the art nickel superalloy was Inconel 718, which is strengthened by the Ni3Nb phase known as gamma double prime. This alloy performs well and is still in heavy use in turbine engines at temperatures up to approximately 650°C (1200°F), but at higher temperatures the main strengthening precipitate phase, gamma', is thermodynamically unstable, resulting in a loss of strength following exposure to high temperature. Further advancements in nickel superalloys generally involved alloys strengthened by the Ni3Al phase known as gamma'. This precipitate is stable at much higher temperatures, but due to compositional segregation in cast and wrought processing, these alloys were processed using powder metallurgy methods, at considerable economic cost. This study will examine the microstructure of a next generation cast and wrought nickel superalloy that can provide increased temperature capability relative to Inconel 718, at lower cost than powder metallurgy superalloys. The alloy chemistry is similar to that of the powder metallurgy superalloy Rene 88DT, with changes to make it better suited for cast and wrought processing and with a different processing route from billet processing through to final part heat treatment. It is a gamma prime strengthened superalloy. The alloy has been recently introduced into service in turbine engines by GE Aviation as the alloy Rene 65, the composition of which is shown below. In this work, the following has been shown: • Rene 65 gamma' precipitate structure

78 FR 8202 - Meeting of the Joint ACRS Subcommittees on Thermal Hydraulic Phenomena and Materials, Metallurgy...

Federal Register 2010, 2011, 2012, 2013, 2014

2013-02-05

... NUCLEAR REGULATORY COMMISSION Advisory Committee on Reactor Safeguards (ACRS) Meeting of the Joint ACRS Subcommittees on Thermal Hydraulic Phenomena and Materials, Metallurgy and Reactor Fuels; Notice... Reactor Fuels will hold a meeting on February 20, 2013, Room T-2B1, 11545 Rockville Pike, Rockville...

Metallurgy and Heat Treating. Welding Module 7. Instructor's Guide.

ERIC Educational Resources Information Center

Missouri Univ., Columbia. Instructional Materials Lab.

This guide is intended to assist vocational educators in teaching a three-unit module in metallurgy and heat treating. The module is part of a welding curriculum that has been designed to be totally integrated with Missouri's Vocational Instruction Management System. The basic principles of metallurgy and heat treatment and techniques for…

Influence of Powder Metallurgical Processing Routes on Phase Formations in a Multicomponent NbSi-Alloy

NASA Astrophysics Data System (ADS)

Seemüller, C.; Hartwig, T.; Mulser, M.; Adkins, N.; Wickins, M.; Heilmaier, M.

2014-09-01

Refractory metal silicide composites on the basis of Nbss-Nb5Si3 have been investigated as potential alternatives for nickel-base superalloys for years because of their low densities and good high-temperature strengths. NbSi-based composites are typically produced by arc-melting or casting. Samples in this study, however, were produced by powder metallurgy because of the potential for near net-shape component fabrication with very homogeneous microstructures. Either gas atomized powder or high-energy mechanically alloyed elemental powders were compacted by powder injection molding or hot isostatic pressing. Heat treatments were applied for phase stability evaluation. Slight compositional changes (oxygen, nitrogen, or iron) introduced by the processing route, i.e., powder production and consolidation, can affect phase formations and phase transitions during the process. Special focus is put on the distinction between different silicides (Nb5Si3 and Nb3Si) and silicide modifications (α-, β-, and γ-Nb5Si3), respectively. These were evaluated by x-ray diffraction and energy-dispersive spectroscopy measurements with the additional inclusion of thermodynamic calculations using the calculated phase diagram method.

Powder Processing of High Temperature Cermets and Carbides at Marshall Space Flight Center

NASA Technical Reports Server (NTRS)

Salvail, Pat; Panda, Binayak; Hickman, Robert R.

2007-01-01

The Materials and Processing Laboratory at NASA Marshall Space Flight Center is developing Powder Metallurgy (PM) processing techniques for high temperature cermet and carbide material consolidation. These new group of materials would be utilized in the nuclear core for Nuclear Thermal Rockets (NTR). Cermet materials offer several advantages for NTR such as retention of fission products and fuels, better thermal shock resistance, hydrogen compatibility, high thermal conductivity, and high strength. Carbide materials offer the highest operating temperatures but are sensitive to thermal stresses and are difficult to process. To support the effort, a new facility has been setup to process refractory metal, ceramic, carbides and depleted uranium-based powders. The facility inciudes inert atmosphere glove boxes for the handling of reactive powders, a high temperature furnace, and powder processing equipment used for blending, milling, and sieving. The effort is focused on basic research to identify the most promising compositions and processing techniques. Several PM processing methods including Cold and Hot Isostatic Pressing are being evaluated to fabricate samples for characterization and hot hydrogen testing.

Oxidation and the Effects of High Temperature Exposures on Notched Fatigue Life of an Advanced Powder Metallurgy Disk Superalloy

NASA Technical Reports Server (NTRS)

Sudbrack, Chantal K.; Draper, Susan L.; Gorman, Timothy T.; Telesman, Jack; Gab, Timothy P.; Hull, David R.

2012-01-01

Oxidation and the effects of high temperature exposures on notched fatigue life were considered for a powder metallurgy processed supersolvus heat-treated ME3 disk superalloy. The isothermal static oxidation response at 704 C, 760 C, and 815 C was consistent with other chromia forming nickel-based superalloys: a TiO2-Cr2O3 external oxide formed with a branched Al2O3 internal subscale that extended into a recrystallized - dissolution layer. These surface changes can potentially impact disk durability, making layer growth rates important. Growth of the external scales and dissolution layers followed a cubic rate law, while Al2O3 subscales followed a parabolic rate law. Cr- rich M23C6 carbides at the grain boundaries dissolved to help sustain Cr2O3 growth to depths about 12 times thicker than the scale. The effect of prior exposures was examined through notched low cycle fatigue tests performed to failure in air at 704 C. Prior exposures led to pronounced debits of up to 99 % in fatigue life, where fatigue life decreased inversely with exposure time. Exposures that produced roughly equivalent 1 m thick external scales at the various isotherms showed statistically equivalent fatigue lives, establishing that surface damage drives fatigue debit, not exposure temperature. Fractographic evaluation indicated the failure mode for the pre-exposed specimens involved surface crack initiations that shifted with exposure from predominately single intergranular initiations with transgranular propagation to multi-initiations from the cracked external oxide with intergranular propagation. Weakened grain boundaries at the surface resulting from the M23C6 carbide dissolution are partially responsible for the intergranular cracking. Removing the scale and subscale while leaving a layer where M23C6 carbides were dissolved did not lead to a significant fatigue life improvement, however, also removing the M23C6 carbide dissolution layer led to nearly full recovery of life, with a

Trithallium hydrogen bis(sulfate), Tl(3)H(SO(4))(2), in the super-ionic phase by X-ray powder diffraction.

PubMed

Matsuo, Yasumitsu; Kawachi, Shinya; Shimizu, Yuya; Ikehata, Seiichiro

2002-07-01

The structure of trithallium hydrogen bis(sulfate), Tl(3)H(SO(4))(2), in the super-ionic phase has been analyzed by Rietveld analysis of the X-ray powder diffraction pattern. Atomic parameters based on the isotypic Rb(3)H(SeO(4))(2) crystal in space group R3m in the super-ionic phase were used as the starting model, because it has been shown from the comparison of thermal and electric properties in Tl(3)H(SO(4))(2) and M(3)H(SO(4))(2) type crystals (M = Rb, Cs or NH(4)) that the room-temperature Tl(3)H(SO(4))(2) phase is isostructural with the high-temperature R3m-symmetry M(3)H(SO(4))(2) crystals. The structure was determined in the trigonal space group R3m and the Rietveld refinement shows that an hydrogen-bond O-H...O separation is slightly shortened compared with O-H...O separations in isotypic M(3)H(SeO(4))(2) crystals. In addition, it was found that the distortion of the SO(4) tetrahedra in Tl(3)H(SO(4))(2) is less than that in isotypic crystals.

40 CFR 471.104 - Pretreatment standards for existing sources (PSES).

Code of Federal Regulations, 2010 CFR

2010-07-01

... (pounds per million off-pounds) of powder metallurgy part steam treated Copper 1.51 0.792 Cyanide 0.230 0...-pounds) of powder metallurgy parts tumbled, burnished, or cleaned Copper 8.36 4.40 Cyanide 1.28 0.528...-pounds) of powder metallurgy parts sawed or ground with emulsions Copper 0.035 0.018 Cyanide 0.005 0.002...

40 CFR 471.103 - New source performance standards (NSPS).

Code of Federal Regulations, 2010 CFR

2010-07-01

... mg/off-kg (pounds per million off-pounds) of powder metallurgy parts steam treated Copper 0.151 0.079... million off-pounds) of powder metallurgy parts tumbled, burnished, or cleaned Copper 0.836 0.440 Cyanide 0... off-pounds) of powder metallurgy parts sawed or ground with emulsions Copper 0.035 0.018 Cyanide 0.005...

40 CFR 471.105 - Pretreatment standards for new sources (PSNS).

Code of Federal Regulations, 2010 CFR

2010-07-01

... mg/off-kg (pounds per million off-pounds) of powder metallurgy parts steam treated Copper 0.151 0.079... million off-pounds) of powder metallurgy parts tumbled, burnished, or cleaned Copper 0.836 0.440 Cyanide 0... off-pounds) of powder metallurgy parts sawed or ground with emulsions Copper 0.035 0.018 Cyanide 0.005...

Welding Metallurgy and Weldability of Stainless Steels

NASA Astrophysics Data System (ADS)

Lippold, John C.; Kotecki, Damian J.

2005-03-01

Welding Metallurgy and Weldability of Stainless Steels, the first book in over twenty years to address welding metallurgy and weldability issues associated with stainless steel, offers the most up-to-date and comprehensive treatment of these topics currently available. The authors emphasize fundamental metallurgical principles governing microstructure evolution and property development of stainless steels, including martensistic, ferric, austenitic, duplex, and precipitation hardening grades. They present a logical and well-organized look at the history, evolution, and primary uses of each stainless steel, including detailed descriptions of the associated weldability issues.

Estimation and characterization of polycyclic aromatic hydrocarbons from magnesium metallurgy facilities in China.

PubMed

Nie, Zhiqiang; Yang, Yufei; Tang, Zhenwu; Liu, Feng; Wang, Qi; Huang, Qifei

2014-11-01

Field monitoring was conducted to develop a polycyclic aromatic hydrocarbon (PAH) emission inventory for the magnesium (Mg) metallurgy industry in China. PAH emissions in stack gas and fly/bottom ash samples from different smelting units of a typical Mg smelter were measured and compared. Large variations of concentrations, congener patterns, and emission factors of PAHs during the oxidation and reduction stages in the Mg smelter were observed. The measured average emission factor (166,487 μg/t Mg) was significantly higher than those of other industrial sources. Annual emission from Mg metallurgy in 2012 in China was estimated at 116 kg (514 g BaPeq) for PAHs. The results of this study suggest that PAH emission from Mg industries should be considered by local government agencies. These data may be helpful for understanding PAH levels produced by the Mg industry and in developing a PAH inventory.

Compressive Deformation Behavior of Open-Cell Cu-Zn-Al Alloy Foam Made Through P/M Route Using Mechanically Alloyed Powder

NASA Astrophysics Data System (ADS)

Barnwal, Ajay Kumar; Mondal, D. P.; Kumar, Rajeev; Prasanth, N.; Dasgupta, R.

2018-03-01

Cu-Zn-Al foams of varying porosity fractions using mechanical alloyed powder have been made through powder metallurgy route. Here, NH4 (HCO3) was used as a space holder. Mechanically alloyed Cu-Zn-Al is made using a planetary ball mill taking the ratio of Cu/Zn/Al = 70:25:5 (by weight ratio). The ball/powder ratios were varied in the four ranges 10:1, 15:1, 20:1, and 25:1. Green compacts of milled powder and space holder samples were sintered at three stages at three different temperatures 350, 550, and 850 °C for 1 h at each stage. The crystalline size and particle size as a function of ball/powder ratios were examined. The compressive deformation responses of foams are varied with relative density and the ball/powder ratio. The plateau stress and energy absorption of these foams increase with an increase in relative density but decreases with increase in ball/powder ratio, even though crystalline size decreases. This has further been explained on the basis of particle morphology as a function of ball/powder ratio.

Pressurized metallurgy for high performance special steels and alloys

NASA Astrophysics Data System (ADS)

Jiang, Z. H.; Zhu, H. C.; Li, H. B.; Li, Y.; Liu, F. B.

2016-07-01

The pressure is one of the basic parameters which greatly influences the metallurgical reaction process and solidification of steels and alloys. In this paper the history and present situation of research and application of pressurized metallurgy, especially pressurized metallurgy for special steels and alloys have been briefly reviewed. In the following part the physical chemistry of pressurized metallurgy is summarized. It is shown that pressurizing may change the conditions of chemical reaction in thermodynamics and kinetics due to the pressure effect on gas volume, solubility of gas and volatile element in metal melt, activity or activity coefficient of components, and change the physical and chemical properties of metal melt, heat transfer coefficient between mould and ingot, thus greatly influencing phase transformation during the solidification process and the solidification structure, such as increasing the solidification nucleation rate, reducing the critical nucleation radius, accelerating the solidification speed and significant macro/micro-structure refinement, and eliminating shrinkage, porosity and segregation and other casting defects. In the third part the research works of pressured metallurgy performed by the Northeastern University including establishment of pressurized induction melting (PIM) and pressurized electroslag remelting (PESR) equipments and development of high nitrogen steels under pressure are described in detail. Finally, it is considered in the paper that application of pressurized metallurgy in manufacture of high performance special steels and alloys is a relatively new research area, and its application prospects will be very broad and bright.

Novel Method for Making Biomedical Segregation-Free Ti-30Ta Alloy Spherical Powder for Additive Manufacturing

NASA Astrophysics Data System (ADS)

Xia, Yang; Fang, Zhigang Zak; Sun, Pei; Zhang, Ying; Zhu, Jun

2018-03-01

Ti-Ta alloys offer a good combination of high strength and low modulus among Ti-based alloys, and are ideal for biomedical applications. However, making Ti-Ta alloys has always been challenging because they tend to suffer from compositional segregation during melting due to the large difference between the melting points of Ti and Ta. This article describes a novel process for making spherical Ti-30Ta alloy powder through a unique powder metallurgy technique, namely the granulation-sintering-deoxygenation process. The results indicate that the compositional segregation problem can be overcome using this process technology. Combined with use of a deoxygenation process, the critical interstitial element, oxygen, can be controlled to < 400 ppm for powder with particle size < 75 µm. The destabilization effect of Ta on Ti-O solid solutions, and the resulting improved deoxygenation process for Ti-Ta, are discussed, as well as the phase composition and microstructure of the powders.

Shape memory characteristics and mechanical properties of powder metallurgy processed Ti50Ni40Cu10 alloy.

PubMed

Kim, Yeon-Wook

2014-10-01

Ti-Ni-Cu alloy powders were prepared by gas atomization and porous bulk specimens were fabricated by spark plasma sintering (SPS). The microstructure of as-solidified powders exhibited a cellular structure and they contained a high density of nano-sized porosities which were located in the intercellular regions. XRD analysis showed that one-step martensitic transformation of B2-B19 occurred in all alloy powders and SPS specimens. When the martensitic transformation start temperature (M(s)) and austenite transformation finish temperature (A(f)) were determined in order to analyze the dependence of powder size on transformation temperatures, the M(s) increased slightly from -17.5 degrees C to - 14.6 degrees C as increasing the powder size ranging from between 25 and 50 μm to ranging between 100 and 150 μm. However, the M(s) and A(f) of the as-atomized powders is much smaller than those of SPS specimens and the M(s) of porous specimen was about 10.9 degrees C. Loading-unloading compressive tests were carried out to investigate the mechanical properties of porous Ti-Ni-Cu specimen. The specimen was compressed to the strain of 6% at a temperature higher than A,. After unloading, the residual strain was 2.1%. After the compressed specimen was heated to 60 degrees C and held for 30 minutes and then cooled to room temperature, the changes in the length of the specimens were measured. Then it was found that the recovered strain ascribed to shape memory effect was 1.5%.

Consolidation processing parameters and alternative processing methods for powder metallurgy Al-Cu-Mg-X-X alloys

NASA Technical Reports Server (NTRS)

Sankaran, K. K.

1987-01-01

The effects of varying the vacuum degassing parameters on the microstructure and properties of Al-4Cu-1Mg-X-X (X-X = 1.5Li-0.2Zr or 1.5Fe-0.75Ce) alloys processed from either prealloyed (PA) or mechanically alloyed (M) powder, and consolidated by either using sealed aluminum containers or containerless vacuum hot pressing were studied. The consolidated billets were hot extruded to evaluate microstructure and properties. The MA Li-containing alloy did not include Zr, and the MA Fe- and Ce-containing alloy was made from both elemental and partially prealloyed powder. The alloys were vacuum degassed both above and below the solution heat treatment temperature. While vacuum degassing lowered the hydrogen content of these alloys, the range over which the vacuum degassing parameters were varied was not large enough to cause significant changes in degassing efficiency, and the observed variations in the mechanical properties of the heat treated alloys were attributed to varying contributions to strengthening by the sub-structure and the dispersoids. Mechanical alloying increased the strength over that of alloys of similar composition made from PA powder. The inferior properties in the transverse orientation, especially in the Li-containing alloys, suggested deficiencies in degassing. Among all of the alloys processed for this study, the Fe- and Ce-containing alloys made from MA powder possessed better combinations of strength and toughness.

Porous Titanium Parts Fabricated by Sintering of TiH2 and Ti Powder Mixtures

NASA Astrophysics Data System (ADS)

Peng, Qin; Yang, Bin; Friedrich, Bernd

2018-01-01

A new simple powder metallurgy process by sintering TiH2 powders was used to manufacture porous Ti components. The effects of the processing parameters (pressure of cold isostatic pressing and sintering temperature) and the TiH2/Ti ratio in the powder mixtures on the impurities, the linear shrinkage and the pore properties (including overall and open porosities) were comprehensively determined. The addition of TiH2 as a reactant has been found beneficial for the synthesis of porous Ti components. The formation mechanisms of pores were demonstrated based on the dehydrogenation process of TiH2 during sintering, resulting in highest reactivity due to the "in statu nascendi" generation of the metal. In addition, the hardness and corrosion resistance of all the sintered samples were evaluated, related to the overall and open porosities. As a result, an optimal composition of Ti-40 wt.% TiH2 was defined, as its maximum open porosity was about 23%.

Aspects of the tribological behaviour of powders recycled from rapid steel treated sub-zero

NASA Astrophysics Data System (ADS)

Radu, S.; Ciobanu, M.

2017-02-01

The recycling of high-alloyed steels represents a significant opportunity in Powder Metallurgy as it permits the use of raw materials with relatively low prices compared to the conventional methods. Recycling can be achieved by two methods: from spraying debris resulted from worn cutting tools and processes obtained from processing chip drilling and re-sharpening of tools. The research aims to confirm that wastes from rapid steels can become, by the successive processing, metal powders that can thereafter be used for cutting tools of lathe type removable plate. After pressing and sintering the recycling powder, cylindrical samples were obtained that were subsequently applied a subcritical annealing. Wear tests conducted on a tribometer type TRB-01-02541 confirmed that their wear resistance is superior to the same samples that were sintered, hardened and tempered in oil. This paper was accepted for publication in Proceedings after double peer reviewing process but was not presented at the Conference ROTRIB’16.

[Respiratory diseases in metallurgy production workers].

PubMed

Shliapnikov, D M; Vlasova, E M; Ponomareva, T A

2012-01-01

The authors identified features of respiratory diseases in workers of various metallurgy workshops. Cause-effect relationships are defined between occupational risk factors and respiratory diseases, with determining the affection level.

αTCP ceramic doped with dicalcium silicate for bone regeneration applications prepared by powder metallurgy method: in vitro and in vivo studies.

PubMed

Velasquez, Pablo; Luklinska, Zofia B; Meseguer-Olmo, Luis; Mate-Sanchez de Val, Jose E; Delgado-Ruiz, Rafael A; Calvo-Guirado, Jose L; Ramirez-Fernandez, Ma P; de Aza, Piedad N

2013-07-01

This study reports on the in vitro and in vivo behavior of α-tricalcium phosphate (αTCP) and also αTCP doped with either 1.5 or 3.0 wt % of dicalcium silicate (C2 S). The ceramics were successfully prepared by powder metallurgy method combined with homogenization and heat treatment procedures. All materials were composed of a single-phase, αTCP in the case of a pure material, or solid solution of C2 S in αTCP for the doped αTCP, which were stable at room temperature. The ceramics were tested for bioactivity in simulated body fluid, cell culture medium containing adult mesenchymal stem cells of human origin, and in animals. Analytical scanning electron microscopy combined with chemical elemental analysis was used and Fourier transform infrared and conventional histology methods. The in vivo behavior of the ceramics matched the in vitro results, independently of the C2 S content in αTCP. Carbonated hydroxyapatite (CHA) layer was formed on the surface and within the inner parts of the specimens in all cases. A fully mineralized new bone growing in direct contact with the implants was found under the in vivo conditions. The bioactivity and biocompatibility of the implants increased with the C2 S content in αTCP. The C2 S doped ceramics also favoured a phase transformation of αTCP into CHA, important for full implant integration during the natural bone healing processes. αTCP ceramic doped with 3.0 wt % C2 S showed the best bioactive in vitro and in vivo properties of all the compositions and hence could be of interest in specific applications for bone restorative purposes. Copyright © 2012 Wiley Periodicals, Inc.

Molecular Dynamics Simulation of the Kinetic Reaction between Ni and Al Nanoparticles

DTIC Science & Technology

2009-01-01

reaction time and temperature for separate nanoparticles has been considered as a model system for a powder metallurgy system. Coated nanoparticles in the...separate nanoparticles has been considered as a model system for a powder metallurgy system. Coated nanoparticles in the form of Ni-coated Al nanoparticles...nanoparticles has been considered as a model system for a powder metallurgy system. Coated nanoparticles in the form of Ni-coated Al nanoparticles

Effect of reduced cobalt contents on hot isostatically pressed powder metallurgy U-700 alloys

NASA Technical Reports Server (NTRS)

Harf, F. H.

1982-01-01

The effect of reducing the cobalt content of prealloyed powders of UDIMET 700 (U-700) alloys to 12.7, 8.6, 4.3, and 0% was examined. The powders were hot isostatically pressed into billets, which were given heat treatments appropriate for turbine disks, namely partial solutioning at temperatures below the gamma prime solvus and four step aging treatments. Chemical analyses, metallographic examinations, and X-ray diffraction measurements were performed on the materials. Minor effects on gamma prime content and on room temperature and 650 C tensile properties were observed. Creep rupture lives at 650 C reached a maximum at the 8.4% concentration, while at 760 C a maximum in life was reached at the 4.3% cobalt level. Minimum creep rates increased with decreasing cobalt content at both test temperatures. Extended exposures at 760 and 815 C resulted in decreased tensile strengths and rupture lives for all alloys. Evidence of sigma phase formation was also found.

In vitro corrosion behavior and in vivo biodegradation of biomedical β-Ca3(PO4)2/Mg-Zn composites.

PubMed

Yu, Kun; Chen, Liangjian; Zhao, Jun; Li, Shaojun; Dai, Yilong; Huang, Qiao; Yu, Zhiming

2012-07-01

In this study 5, 10 and 15% β-Ca(3)(PO(4))(2)/Mg-Zn composites were prepared through powder metallurgy methods, and their corrosion behavior and mechanical properties were studied in simulated body fluid (SBF) at 37°C. The 10% β-Ca(3)(PO(4))(2)/Mg-Zn composite was selected for cytocompatibility assessment and in vivo biodegradation testing. The results identified the α-Mg, MgZn and β-Ca(3)(PO(4))(2) phases in these sintered composites. The density and elastic modulus of the β-Ca(3)(PO(4))(2)/Mg-6% Zn composite match those of natural bone, and the strength is approximately double that of natural bone. The 10% β-Ca(3)(PO(4))(2)/Mg-6% Zn composites exhibit good corrosion resistance, as determined by a 30 day immersion test and electrochemical measurements in SBF at 37°C. The 10% β-Ca(3)(PO(4))(2)/Mg-6% Zn composite is safe for cellular applications, with a cytotoxicity grade of ∼0-1 against L929 cells in in vitro testing. The β-Ca(3)(PO(4))(2)/Mg-6% Zn composite also exhibits good biocompatibility with the tissue and the important visceral organs the heart, kidney and liver of experimental rabbits. The composite has a suitable degradation rate and improves the concrescence of a pre-broken bone. The corrosion products, such as Mg(OH)(2) and Ca(5)(PO(4))(6)(OH)(2), can improve the biocompatibility of the β-Ca(3)(PO(4))(2)/Mg-Zn composite. Copyright © 2012 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

High transport current superconductivity in powder-in-tube Ba0.6K0.4Fe2As2 tapes at 27 T

NASA Astrophysics Data System (ADS)

Huang, He; Yao, Chao; Dong, Chiheng; Zhang, Xianping; Wang, Dongliang; Cheng, Zhe; Li, Jianqi; Awaji, Satoshi; Wen, Haihu; Ma, Yanwei

2018-01-01

The high upper critical field and low anisotropy of iron-based superconductors (IBS) make them particularly attractive for high-field applications, especially for the construction of next-generation nuclear magnetic resonance spectrometers, particle accelerators and high-field magnets. However, for practical use it is essential to make IBS materials into wire and tape conductors with sufficient current carrying capability, which is limited by misaligned grains inside the conductors. Here, based on a simple and low-cost powder-in-tube (PIT) method, we demonstrate a high transport critical current density (J c) reaching 1.5 × 105 A cm-2 (I c = 437 A) at 4.2 K and 10 T in Ba0.6K0.4Fe2As2 (Ba-122) tapes by texturing the grain orientation with optimized hot-press technique. The transport J c measured at 4.2 K under high magnetic fields of 27 T is still on the level of 5.5 × 104 A cm-2. Moreover, at 20 K and 5 T the transport J c is also as high as 5.4 × 104 A cm-2, showing a promising application potential in moderate temperature range which can be reached by liquid hydrogen or cryogenic cooling. All these J c values are the highest ever reported for IBS wires and tapes. The high-performance PIT Ba-122 tapes in this work suggest IBS to be a strong potential competitor of cuprate superconductors for the race of high-field applications in the future.

40 CFR 471.102 - Effluent limitations representing the degree of effluent reduction attainable by the application...

Code of Federal Regulations, 2010 CFR

2010-07-01

... metallurgy parts steam treated Copper 1.51 0.792 Cyanide 0.230 0.095 Lead 0.333 0.159 (e) Tumbling... Maximum for monthly average mg/off-kg (pounds per million off-pounds) or powder metallurgy parts tumbled... monthly average mg/off-kg (pounds per million off-pounds) of powder metallurgy parts sawed or ground with...

Unique coordination of pyrazine in T[Ni(CN){sub 4}].2pyz with T=Mn, Zn, Cd

DOE Office of Scientific and Technical Information (OSTI.GOV)

Lemus-Santana, A.A.; Rodriguez-Hernandez, J.; Castillo, L.F. del, E-mail: lfelipe@servidor.unam.m

2009-04-15

The materials under study, T[Ni(CN){sub 4}].2pyz with T=Mn, Zn, Cd, were prepared by separation of T[Ni(CN){sub 4}] layers in citrate aqueous solution to allow the intercalation of the pyrazine molecules. The obtained solids were characterized from chemical analyses, X-ray diffraction, infrared, Raman, thermogravimetry, UV-Vis, magnetic and adsorption data. Their crystal structure was solved from ab initio using direct methods and then refined by the Rietveld method. A unique coordination for pyrazine to metal centers at neighboring layers was observed. The pyrazine molecule is found forming a bridge between Ni and T atoms, quite different from the proposed structures for T=Fe,more » Ni where it remains coordinated to two T atoms to form a vertical pillar between neighboring layers. The coordination of pyrazine to both Ni and T atoms minimizes the material free volume and leads to form a hydrophobic framework. On heating the solids remain stable up to 140 deg. C. No CO{sub 2} and H{sub 2} adsorption was observed in the small free spaces of their frameworks. - Graphical abstract: Framework for T[Ni(CN){sub 4}].2pyz with T=Mn, Zn, Cd.« less

Enhanced method of magnetic powder alignment for production of PLP Nd-Fe-B magnets

NASA Astrophysics Data System (ADS)

Popov, A. G.; Golovnia, O. A.; Protasov, A. V.

2017-04-01

It is demonstrated how the high degree of powder alignment in PLP magnets can be achieved by loading the powder into a container placed in a magnetic field of moderate strength. The strip-cast alloy with a composition of 30.00 Nd, 1.95 Dy, 66.42 Fe, 0.99 B, 0.54 Co, 0.1 Ga (wt%) was subjected to hydrogen decrepitation and then milled in a vibratory mill in toluene to an average particle size of 2.9 μm determined by the FSSS method. The powder was compacted in the magnetic field of 0.2 - 1.2 T to the filling density 2.6 - 3.2×103 kg/m3. It is shown that loading the powder into a container placed in a magnetic field enhances the degree of powder alignment in sintered Nd-Fe-B magnets produced from non-pressed powder. At the filling density less than 3.2×103 kg/m3, the density of magnets is high but insufficient, because of the formation of magnetostatic chains of particles, which impedes the powder compaction. The simulation by the discrete-element method qualitatively proves that the magnetostatic interaction of the chains of particles that are formed in the course of loading in the magnetic field stimulates a decrease in the density of the sintered magnets and its non-uniform distribution over the sample. As a result of the optimization of the parameters of the alignment and compaction of the powder loaded in a magnetic field, PLP magnets with Br ≥1.34 T, Hc ≥950 kA/m, (BH)max ≥340 kJ/m3, and the degree of alignment exceeding 96% were produced.

The effect of hot isostatic pressing parameters on microstructure and mechanical properties of Eurofer powder HIPed material

NASA Astrophysics Data System (ADS)

Gentzbittel, J. M.; Chu, I.; Burlet, H.

2002-12-01

The production of reduced activation ferritic/martensitic (RAFM) steel by powder metallurgy and high isostatic pressing (HIP) offers numerous advantages for different nuclear applications. The objective of this work is to optimise the Eurofer powder HIP process in order to obtain RAFM solid HIPed steel with similar mechanical properties to those of a forged material. Starting from the forged solid Eurofer steel batch, the material is atomized and the Eurofer powder is characterized in terms of granulometry, chemical composition, surface oxides, etc. Different compaction HIP cycle parameters in the temperature range (950-1100 °C) are tested. The chemical composition of the HIPed material is comparable to the initial forged Eurofer. All the obtained materials are fully dense and the microstructure of the compacted material is well martensitic. The prior austenite grain size seems to be constant in this temperature range. The mechanical tests performed at room temperature reveal acceptable hardness, tensile and Charpy impact properties regarding the ITER specification.

Two-dimensional distribution of carbon nanotubes in copper flake powders.

PubMed

Tan, Zhanqiu; Li, Zhiqiang; Fan, Genlian; Li, Wenhuan; Liu, Qinglei; Zhang, Wang; Zhang, Di

2011-06-03

We report an approach of flake powder metallurgy to the uniform, two-dimensional (2D) distribution of carbon nanotubes (CNTs) in Cu flake powders. It consists of the preparation of Cu flakes by ball milling in an imidazoline derivative (IMD) aqueous solution, surface modification of Cu flakes with polyvinyl alcohol (PVA) hydrosol and adsorption of CNTs from a CNT aqueous suspension. During ball milling, a hydrophobic monolayer of IMD is adsorbed on the surface of the Cu flakes, on top of which a hydrophilic PVA film is adsorbed subsequently. This PVA film could further interact with the carboxyl-group functionalized CNTs and act to lock the CNTs onto the surfaces of the Cu flakes. The CNT volume fraction is controlled easily by adjusting the concentration/volume of CNT aqueous suspension and Cu flake thickness. The as-prepared CNT/Cu composite flakes will serve as suitable building blocks for the self-assembly of CNT/Cu laminated composites that enable the full potential of 2D distributed CNTs to achieve high thermal conductivity.

Protective Effects of Sweet Orange, Unshiu Mikan, and Mini Tomato Juice Powders on t-BHP-Induced Oxidative Stress in HepG2 Cells

PubMed Central

Jannat, Susoma; Ali, Md Yousof; Kim, Hyeung-Rak; Jung, Hyun Ah; Choi, Jae Sue

2016-01-01

The aim of this study was to investigate the protective effects of juice powders from sweet orange [Citrus sinensis (L.) Osbeck], unshiu mikan (Citrus unshiu Marcow), and mini tomato (Solanum lycopersicum L.), and their major flavonoids, hesperidin, narirutin, and rutin in tert-butyl hydroperoxide (t-BHP)-induced oxidative stress in HepG2 cells. The increased reactive oxygen species and decreased glutathione levels observed in t-BHP-treated HepG2 cells were ameliorated by pretreatment with juice powders, indicating that the hepatoprotective effects of juice powders and their major flavonoids are mediated by induction of cellular defense against oxidative stress. Moreover, pretreatment with juice powders up-regulated phase-II genes such as heme oxygenase-1 (HO-1), thereby preventing cellular damage and the resultant increase in HO-1 expression. The high-performance liquid chromatography profiles of the juice powders confirmed that hesperidin, narirutin, and rutin were the key flavonoids present. Our results suggest that these fruit juice powders and their major flavonoids provide a significant cytoprotective effect against oxidative stress, which is most likely due to the flavonoid-related bioactive compounds present, leading to the normal redox status of cells. Therefore, these fruit juice powders could be advantageous as bioactive sources for the prevention of oxidative injury in hepatoma cells. PMID:27752497

Applications of high-temperature powder metal aluminum alloys to small gas turbines

NASA Technical Reports Server (NTRS)

Millan, P. P., Jr.

1982-01-01

A program aimed at the development of advanced powder-metallurgy (PM) aluminum alloys for high-temperature applications up to 650 F using the concepts of rapid solidification and mechanical alloying is discussed. In particular, application of rapidly solidified PM aluminum alloys to centrifugal compressor impellers, currently used in auxiliary power units for both military and commercial aircraft and potentially for advanced automotive gas turbine engines, is examined. It is shown that substitution of high-temperature aluminum for titanium alloy impellers operating in the 360-650 F range provides significant savings in material and machining costs and results in reduced component weight, and consequently, reduced rotating group inertia requirements.

A Fundamental Study of Tool Steels Processed from Rapidly Solidified Powders.

DTIC Science & Technology

1981-12-01

structures, HIP or HIP and hot-worked high speed tool steels and powder forgings of low and medium alloy steels for load- bearing automotive...M7, M7S, M41, M42, M43S, T15 and M50 . These P/M tool steels exhibit a degree of alloy homogeneity and a fineness/uniformity of carbide dispersion...AD-AIl2 758 DREXEL UNIV PHILADEL.PH IA PA DEPT OF MATERIALS ENGINEERING F/6 11/6 A FUNDAMENTAL STUDY OF TOOL STEELS PROCESSED FROM L DEC 81 A

Plutonium Metallurgy

DOE Office of Scientific and Technical Information (OSTI.GOV)

Freibert, Franz J.

2012-08-09

Due to its nuclear properties, Pu will remain a material of global interest well into the future. Processing, Structure, Properties and Performance remains a good framework for discussion of Pu materials science Self-irradiation and aging effects continue to be central in discussions of Pu metallurgy Pu in its elemental form is extremely unstable, but alloying helps to stabilize Pu; but, questions remain as to how and why this stabilization occurs. Which is true Pu-Ga binary phase diagram: US or Russian? Metallurgical issues such as solute coring, phase instability, crystallographic texture, etc. result in challenges to casting, processing, and properties modelingmore » and experiments. For Ga alloyed FCC stabilized Pu, temperature and pressure remain as variables impacting phase stability.« less

Effects of different levels of coriander (Coriandrum sativum) seed powder and extract on serum biochemical parameters, microbiota, and immunity in broiler chicks.

PubMed

Hosseinzadeh, Hesam; Alaw Qotbi, Ali Ahmad; Seidavi, Alireza; Norris, David; Brown, David

2014-01-01

The use of herbs and spices has gained increasing interest as feed additives and possible alternative to antibiotics in poultry production. The effects of using different levels of coriander seed powder or extract on selected blood parameters, intestinal microflora, and immune response of broiler chickens were investigated in this study. A total of 420-day-old broiler chicks were randomly assigned to 7 treatments with 4 replicates and fed for 42 days. Results showed that inclusion of 2.0% coriander powder in broiler diets lowered total cholesterol while blood urea was significantly higher in birds on T4 compared to T1 and T2. Furthermore, there were no treatment effects on Lactobacillus bacteria; however, the population of E. coli was significantly higher in the ileum of chickens fed T0. Noticeable significant improvements of antibody titer against Newcastle, infectious bronchitis, and infectious bursal disease were observed in birds receiving coriander extract in water. Immunoglobulin G antibody against sheep red blood cells showed significant improvement in birds fed T3; likewise, immunoglobulin M was significantly higher in birds on T2 and T3 at 28 d of age. These results revealed that coriander extract or powder can be used as antibiotic alternative in broiler feeds.

Effects of Different Levels of Coriander (Coriandrum sativum) Seed Powder and Extract on Serum Biochemical Parameters, Microbiota, and Immunity in Broiler Chicks

PubMed Central

Hosseinzadeh, Hesam; Alaw Qotbi, Ali Ahmad; Seidavi, Alireza; Norris, David; Brown, David

2014-01-01

The use of herbs and spices has gained increasing interest as feed additives and possible alternative to antibiotics in poultry production. The effects of using different levels of coriander seed powder or extract on selected blood parameters, intestinal microflora, and immune response of broiler chickens were investigated in this study. A total of 420-day-old broiler chicks were randomly assigned to 7 treatments with 4 replicates and fed for 42 days. Results showed that inclusion of 2.0% coriander powder in broiler diets lowered total cholesterol while blood urea was significantly higher in birds on T4 compared to T1 and T2. Furthermore, there were no treatment effects on Lactobacillus bacteria; however, the population of E. coli was significantly higher in the ileum of chickens fed T0. Noticeable significant improvements of antibody titer against Newcastle, infectious bronchitis, and infectious bursal disease were observed in birds receiving coriander extract in water. Immunoglobulin G antibody against sheep red blood cells showed significant improvement in birds fed T3; likewise, immunoglobulin M was significantly higher in birds on T2 and T3 at 28 d of age. These results revealed that coriander extract or powder can be used as antibiotic alternative in broiler feeds. PMID:25614892

Preparation of Cu and Fly Ash Composite by Powder Metallurgy Technique

DOE Office of Scientific and Technical Information (OSTI.GOV)

Chew, P. Y.; Lim, P. S.; Ng, M. C.

2011-03-30

Cu and Fly Ash (FA) mixtures with different weight percentages were prepared. Pellets of the mixture powder were produced with the dimension of 17.7 mm in diameter and 10-15 mm in height. These different composites were compacted at a constant pressure of 280 MPa. One of the selected weight percentages was then compacted to form into pellet and sintered at different temperatures which were at 900, 950 and 1000 deg. C respectively for 2 hours. Density of green pellet was measured before sintered in furnace. After sintering, all the pellets with different temperatures were re-weighed and sintered density were calculated.more » The densification of the green and sintered pellets was required to be measured as one of the parameter in selection of the best material properties. Porosity of the pellet shall not be ignored in order to analyze the close-packed particles stacking in the pellet. SEM micrograph had been captured to observe the presence of pores and agglomeration of particles in the sample produced.« less

Comparing Strengthening Mechanisms of Vapor Grown Carbon Fiber vs. Titanium Carbide Reinforced Powder Metallurgy Titanium Metal Matrix Composites

NASA Astrophysics Data System (ADS)

Franco, Staub; Kondoh, Katsuyoshi; Umeda, Junko; Imai, Hisashi

In this experiment, TILOP-45 commercially pure titanium powder was mixed with vapor grown carbon fibers (VGCF) to form a 200 g 0.5 wt. % VGCF solution. After adding 0.15 grams of cle-safe oil, a rocking mill shook the sample at 60.0 Hz for 2 hours, resulting in satisfactory dispersion of VGCF on the titanium powder surface. The powder solution was compacted by spark plasma sintering (SPS) and hot extruded. The SPS temperature was set to either 800 °C or 1,000 °C and the pressure to 35 kN. Using an extrusion ratio of 13:1 and ram speed of 3 mm/s, the titanium billet, preheated to either 800 °C or 1,000 °C, was deformed to a 10 mm diameter rod. All four permutations of SPS and extrusion temperatures were tested. Microstructure, grain size, hardness, and oxygen/nitrogen/carbon content were observed. Also, a UTS experiment was done followed by SEM observations of the fractured surfaces.

Analysis of Lightweight Materials for the AM2 System

DTIC Science & Technology

2014-06-01

and fatigue behavior in magnesium alloys . Materials Science & Engineering A (Structural Materials: Properties , Microstructure and Processing ), v 434...Table 7. Tensile properties of the alloys AA2024 or the T3 and T81 temper designations (Kuo et al . 2005...using a powder metallurgy technique, such as a standard cold compacting press and sintering process . However, the fatigue life of the liquid-based

Metallurgy Beyond Iron

NASA Astrophysics Data System (ADS)

Gallino, Isabella; Busch, Ralf

2009-08-01

Metallurgy is one of the oldest sciences. Its history can be traced back to 6000 BCE with the discovery of Gold, and each new discovery - Copper, Silver, Lead, Tin, Iron and Mercury - marked the beginning of a new era of civilization. Currently there are 86 known metals, but until the end of the 17th century, only 12 of these were known. Steel (Fe-C alloy) was discovered in the 11th century BCE; however, it took until 1709 CE before we mastered the smelting of pig-iron by using coke instead of charcoal and started the industrial revolution. The metallurgy of nowadays is mainly about discovering better materials with superior properties to fulfil the increasing demand of the global market. Promising are the Glassy Metals or Bulk Metallic Glasses (BMGs) - discovered at first in the late 50s at the California Institute of Technology - which are several times stronger than the best industrial steels and 10-times springier. The unusual structure that lacks crystalline grains makes BMGs so promising. They have a liquid-like structure that means they melt at lower temperatures, can be moulded nearly as easily as plastics, and can be shaped into features just 10 nm across. The best BMG formers are based on Zr, Pd, Pt, Ca, Au and, recently discovered, also Fe. They have typically three to five components with large atomic size mismatch and a composition close to a deep eutectic. Packing in such liquids is very dense, with a low content of free volume, resulting in viscosities that are several orders of magnitude higher than in pure metal melts.

High-resolution study of Gamow-Teller excitations in the 42Ca(3He,t )42Sc reaction and the observation of a "low-energy super-Gamow-Teller state"

NASA Astrophysics Data System (ADS)

Fujita, Y.; Fujita, H.; Adachi, T.; Susoy, G.; Algora, A.; Bai, C. L.; Colò, G.; Csatlós, M.; Deaven, J. M.; Estevez-Aguado, E.; Guess, C. J.; Gulyás, J.; Hatanaka, K.; Hirota, K.; Honma, M.; Ishikawa, D.; Krasznahorkay, A.; Matsubara, H.; Meharchand, R.; Molina, F.; Nakada, H.; Okamura, H.; Ong, H. J.; Otsuka, T.; Perdikakis, G.; Rubio, B.; Sagawa, H.; Sarriguren, P.; Scholl, C.; Shimbara, Y.; Stephenson, E. J.; Suzuki, T.; Tamii, A.; Thies, J. H.; Yoshida, K.; Zegers, R. G. T.; Zenihiro, J.

2015-06-01

To study the Gamow-Teller (GT) transitions from the Tz=+1 nucleus 42Ca to the Tz=0 nucleus 42Sc, where Tz is the z component of isospin T , we performed a (p ,n )-type (3He,t ) charge-exchange reaction at 140 MeV/nucleon and scattering angles around 0∘. With an energy resolution of 29 keV, states excited by GT transitions (GT states) could be studied accurately. The reduced GT transition strengths B (GT) were derived up to the excitation energy of 13 MeV, assuming the proportionality between the cross sections at 0∘ and B (GT) values. The main part of the observed GT transition strength is concentrated in the lowest 0.611-MeV, Jπ=1+ GT state. All the other states at higher energies are weakly excited. Shell-model calculations could reproduce the gross feature of the experimental B (GT) distribution, and random-phase-approximation calculations including an attractive isoscalar interaction showed that the 0.611-MeV state has a collective nature. It was found that this state has all of the properties of a "low-energy super-Gamow-Teller state." It is expected that low-lying Jπ=1+ GT states have T =0 in the Tz=0 nucleus 42Sc. However, T =1 states are situated in a higher energy region. Assuming an isospin-analogous structure in A =42 isobars, analogous T =1 , 1+ states are also expected in 42Ca. Comparing the (3He 42,tCa) 42Sc and 42Ca(p ,p') spectra measured at 0∘, candidates for T =1 GT states could be found in the 10 -12 -MeV region of 42Sc. They were all weakly excited. The mass dependence of the GT strength distributions in Sc isotopes is also discussed.

The physical metallurgy of mechanically-alloyed, dispersion-strengthened Al-Li-Mg and Al-Li-Cu alloys

NASA Technical Reports Server (NTRS)

Gilman, P. S.

1984-01-01

Powder processing of Al-Li-Mg and Al-Li-Cu alloys by mechanical alloying (MA) is described, with a discussion of physical and mechanical properties of early experimental alloys of these compositions. The experimental samples were mechanically alloyed in a Szegvari attritor, extruded at 343 and 427 C, and some were solution-treated at 520 and 566 C and naturally, as well as artificially, aged at 170, 190, and 210 C for times of up to 1000 hours. All alloys exhibited maximum hardness after being aged at 170 C; lower hardness corresponds to the solution treatment at 566 C than to that at 520 C. A comparison with ingot metallurgy alloys of the same composition shows the MA material to be stronger and more ductile. It is also noted that properly aged MA alloys can develop a better combination of yield strength and notched toughness at lower alloying levels.

Calorimetry investigations of milled α-tricalcium phosphate (α-TCP) powders to determine the formation enthalpies of α-TCP and X-ray amorphous tricalcium phosphate.

PubMed

Hurle, Katrin; Neubauer, Juergen; Bohner, Marc; Doebelin, Nicola; Goetz-Neunhoeffer, Friedlinde

2015-09-01

One α-tricalcium phosphate (α-TCP) powder was either calcined at 500°C to obtain fully crystalline α-TCP or milled for different durations to obtain α-TCP powders containing various amounts of X-ray amorphous tricalcium phosphate (ATCP). These powders containing between 0 and 71wt.% ATCP and up to 2.0±0.1wt.% β-TCP as minor phase were then hydrated in 0.1M Na2HPO4 aqueous solution and the resulting heat flows were measured by isothermal calorimetry. Additionally, the evolution of the phase composition during hydration was determined by in situ XRD combined with the G-factor method, an external standard method which facilitates the indirect quantification of amorphous phases. Maximum ATCP hydration was reached after about 1h, while that of crystalline α-TCP hydration occurred between 4 and 11h, depending on the ATCP content. An enthalpy of formation of -4065±6kJ/mol (T=23°C) was calculated for ATCP (Ca3(PO4)2), while for crystalline α-TCP (α-Ca3(PO4)2) a value of -4113±6kJ/mol (T=23°C) was determined. Copyright © 2015 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

Magnetocaloric effect and slow magnetic relaxation in CsGd(MoO4)2 induced by crystal-field anisotropy

NASA Astrophysics Data System (ADS)

Tkáč, V.; Tarasenko, R.; Orendáčová, A.; Orendáč, M.; Sechovský, V.; Feher, A.

2018-05-01

The experimental and theoretical study of magnetocaloric effect and magnetic relaxation of the powder sample of CsGd(MoO4)2 were performed. The large conventional magnetocaloric effect was found around 2 K with - ΔSmax ≈ 26.5 J/(kg K) for B = 7 T. AC susceptibility measurement revealed multiple-time scale magnetic relaxation effects on different time scales. Slowest relaxation effect was attributed to the direct process with a bottleneck effect and two faster relaxation processes are effectively temperature independent, probably as a result of averaging in the powder sample.

Crack Growth Modeling in an Advanced Powder Metallurgy Alloy

DTIC Science & Technology

1980-07-01

Figure ~ ~ ~ ~ ~ 1 90. SpcmnCniuain CorMtra ulfcto Experiments. .= is5.9 mm__ C ,, . 625 inch) , so t’ 0 1 ".6 12.7 mm (0.50 inch) Figure 5. Configuration...best simple correlation of hold time and stress ratio (R = 0.05 through 0.8) effects on Inconel 718 at 650* C (1200" F) was by the maximum stress...in the work done in another studyt22) on Inconel 718. Based on these room-temperature studies, the interpolative model was ex- pected to have a

Ice-core evidence of earliest extensive copper metallurgy in the Andes 2700 years ago

NASA Astrophysics Data System (ADS)

Eichler, A.; Gramlich, G.; Kellerhals, T.; Tobler, L.; Rehren, Th.; Schwikowski, M.

2017-01-01

The importance of metallurgy for social and economic development is indisputable. Although copper (Cu) was essential for the wealth of pre- and post-colonial societies in the Andes, the onset of extensive Cu metallurgy in South America is still debated. Comprehensive archaeological findings point to first sophisticated Cu metallurgy during the Moche culture ~200-800 AD, whereas peat-bog records from southern South America suggest earliest pollution potentially from Cu smelting as far back as ~2000 BC. Here we present a 6500-years Cu emission history for the Andean Altiplano, based on ice-core records from Illimani glacier in Bolivia, providing the first complete history of large-scale Cu smelting activities in South America. We find earliest anthropogenic Cu pollution during the Early Horizon period ~700-50 BC, and attribute the onset of intensified Cu smelting in South America to the activities of the central Andean Chiripa and Chavin cultures ~2700 years ago. This study provides for the first time substantial evidence for extensive Cu metallurgy already during these early cultures.

Ice-core evidence of earliest extensive copper metallurgy in the Andes 2700 years ago.

PubMed

Eichler, A; Gramlich, G; Kellerhals, T; Tobler, L; Rehren, Th; Schwikowski, M

2017-01-31

The importance of metallurgy for social and economic development is indisputable. Although copper (Cu) was essential for the wealth of pre- and post-colonial societies in the Andes, the onset of extensive Cu metallurgy in South America is still debated. Comprehensive archaeological findings point to first sophisticated Cu metallurgy during the Moche culture ~200-800 AD, whereas peat-bog records from southern South America suggest earliest pollution potentially from Cu smelting as far back as ~2000 BC. Here we present a 6500-years Cu emission history for the Andean Altiplano, based on ice-core records from Illimani glacier in Bolivia, providing the first complete history of large-scale Cu smelting activities in South America. We find earliest anthropogenic Cu pollution during the Early Horizon period ~700-50 BC, and attribute the onset of intensified Cu smelting in South America to the activities of the central Andean Chiripa and Chavin cultures ~2700 years ago. This study provides for the first time substantial evidence for extensive Cu metallurgy already during these early cultures.

Ice-core evidence of earliest extensive copper metallurgy in the Andes 2700 years ago

PubMed Central

Eichler, A.; Gramlich, G.; Kellerhals, T.; Tobler, L.; Rehren, Th.; Schwikowski, M.

2017-01-01

The importance of metallurgy for social and economic development is indisputable. Although copper (Cu) was essential for the wealth of pre- and post-colonial societies in the Andes, the onset of extensive Cu metallurgy in South America is still debated. Comprehensive archaeological findings point to first sophisticated Cu metallurgy during the Moche culture ~200–800 AD, whereas peat-bog records from southern South America suggest earliest pollution potentially from Cu smelting as far back as ~2000 BC. Here we present a 6500-years Cu emission history for the Andean Altiplano, based on ice-core records from Illimani glacier in Bolivia, providing the first complete history of large-scale Cu smelting activities in South America. We find earliest anthropogenic Cu pollution during the Early Horizon period ~700–50 BC, and attribute the onset of intensified Cu smelting in South America to the activities of the central Andean Chiripa and Chavin cultures ~2700 years ago. This study provides for the first time substantial evidence for extensive Cu metallurgy already during these early cultures. PMID:28139760

Phase transformation and magnetic properties of MnAl powders prepared by elemental-doping and salt-assisted ball milling

NASA Astrophysics Data System (ADS)

Qian, Hui-Dong; Si, Ping-Zhan; Choi, Chul-Jin; Park, Jihoon; Cho, Kyung Mox

2018-05-01

The effects of elemental doping of Si and Fe on the ɛ→τ phase transformation and the magnetic properties of MnAl were studied. The magnetic powders of Si- and Fe-doped MnAl were prepared by using induction melting followed by water-quenching, annealing, and salt-assisted ball-milling. The Fe-doped MnAl powders are mainly composed of the L10-structured τ-phase, while the Si-doped MnAl are composed of τ-phase and a small fraction of γ2- and β-phases. A unique thin leaves-like morphology with thickness of several tens of nanometers and diameter size up to 500 nm were observed in the Si-doped MnAl powders. The Fe-doped MnAl powders show irregular shape with much larger dimensions in the range from several to 10 μm. The morphology difference of the samples was ascribed to the variation of the mechanical properties affected by different doping elements. The phase transformation temperatures of the ɛ-phase of the samples were measured. The doping of Fe decreases the onset temperature of the massive phase transformation in MnAl, while the Si-doping increases the massive phase transformation temperature. Both Fe and Si increase the Curie temperature of MnAl. A substantially enhanced coercivity up to 0.45 T and 0.42 T were observed in the ball-milled MnAl powders doped with Si and Fe, respectively.

Process Metallurgy an Enabler of Resource Efficiency: Linking Product Design to Metallurgy in Product Centric Recycling

NASA Astrophysics Data System (ADS)

Reuter, Markus; van Schaik, Antoinette

In this paper the link between process metallurgy, classical minerals processing, product centric recycling and urban/landfill mining is discussed. The depth that has to be achieved in urban mining and recycling must glean from the wealth of theoretical knowledge and insight that have been developed in the past in minerals and metallurgical processing. This background learns that recycling demands a product centric approach, which considers simultaneously the multi-material interactions in man-made complex `minerals'. Fast innovation in recycling and urban mining can be achieved by further evolving from this well developed basis, evolving the techniques and tools that have been developed over the years. This basis has already been used for many years to design, operate and control industrial plants for metal production. This has been the basis for Design for Recycling rules for End-of-Life products. Using, among others, the UNEP Metal Recycling report as a basis (authors are respectively Lead and Main authors of report), it is demonstrated that a common theoretical basis as developed in metallurgy and minerals processing can help much to level the playing field between primary processing, secondary processing, recycling, and urban/landfill mining and product design hence enhancing resource efficiency. Thus various scales of detail link product design with metallurgical process design and its fundamentals.

NSF: A "Populist" Pattern in Metallurgy, Materials Research?

ERIC Educational Resources Information Center

Shapley, Deborah

1975-01-01

Describes the testimony of a University of Virginia professor of applied science, who charged that the National Science Foundation grants disproportionately small funds to the best university departments in the field of metallurgy and materials, while preferentially funding middle-ranked departments. (MLH)

X-ray photoelectron spectroscopy (XPS) investigation of the surface film on magnesium powders.

PubMed

Burke, Paul J; Bayindir, Zeynel; Kipouros, Georges J

2012-05-01

Magnesium (Mg) and its alloys are attractive for use in automotive and aerospace applications because of their low density and good mechanical properties. However, difficulty in forming magnesium and the limited number of available commercial alloys limit their use. Powder metallurgy may be a suitable solution for forming near-net-shape parts. However, sintering pure magnesium presents difficulties due to surface film that forms on the magnesium powder particles. The present work investigates the composition of the surface film that forms on the surface of pure magnesium powders exposed to atmospheric conditions and on pure magnesium powders after compaction under uniaxial pressing at a pressure of 500 MPa and sintering under argon at 600 °C for 40 minutes. Initially, focused ion beam microscopy was utilized to determine the thickness of the surface layer of the magnesium powder and found it to be ~10 nm. The X-ray photoelectron analysis of the green magnesium sample prior to sintering confirmed the presence of MgO, MgCO(3)·3H(2)O, and Mg(OH)(2) in the surface layer of the powder with a core of pure magnesium. The outer portion of the surface layer was found to contain MgCO(3)·3H(2)O and Mg(OH)(2), while the inner portion of the layer is primarily MgO. After sintering, the MgCO(3)·3H(2)O was found to be almost completely absent, and the amount of Mg(OH)(2) was also decreased significantly. This is postulated to occur by decomposition of the compounds to MgO and gases during the high temperature of sintering. An increase in the MgO content after sintering supports this theory.

Fabrication and characterization of powder metallurgy tantalum components prepared by high compaction pressure technique

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kim, Youngmoo; Agency for Defense Development, Yuseong, P.O. Box 35, Yuseong-gu, Daejeon 34186, Republic of Korea.; Lee, Dongju

2016-04-15

The present study has investigated the consolidation behaviors of tantalum powders during compaction and sintering, and the characteristics of sintered components. For die compaction, the densification behaviors of the powders are simulated by finite element analyses based on the yield function proposed by Shima and Oyane. Accordingly, the green density distribution for coarser particles is predicted to be more uniform because they exhibits higher initial relative tap density owing to lower interparticle friction. It is also found that cold isostatic pressing is capable of producing higher dense compacts compared to the die pressing. However, unlike the compaction behavior, the sinteredmore » density of smaller particles is found to be higher than those of coarser ones owing to their higher specific surface area. The maximum sintered density was found to be 0.96 of theoretical density where smaller particles were pressed isostatically at 400 MPa followed by sintering at 2000 °C. Moreover, the effects of processing conditions on grain size and texture were also investigated. The average grain size of the sintered specimen is 30.29 μm and its texture is less than 2 times random intensity. Consequently, it is concluded that the higher pressure compaction technique is beneficial to produce high dense and texture-free tantalum components compared to hot pressing and spark plasma sintering. - Highlights: • Higher Ta density is obtained from higher pressure and sintering temperature. • High compaction method enables P/M Ta to achieve the density of 16.00 g·cm{sup −3}. • A P/M Ta component with fine microstructure and random orientation is developed.« less

Powder Processing of Amorphous Tungsten-bearing Alloys and Composites

DTIC Science & Technology

2015-03-01

8725 John J. Kingman Road, MS-6201 Fort Belvoir, VA 22060-6201 T E C H N IC A L R E P O R T DTRA-TR-14-73 Powder Processing of Amorphous Tungsten...Technology, Boise State University, Army Research Laboratory Project Title: Powder Processing of Amorphous Tungsten-bearing Alloys and Composites...Our year 3 tasks, as laid out in the project proposal, were to 1) Consolidate amorphous or nanocrystalline powder blends 2) Mechanical testing

Powder Metallurgy Processing of High-Strength FeCo Alloys (Preprint)

DTIC Science & Technology

2008-09-01

Basu, R.-Hai Yu, J. Q. Xiao, A. Parvizi- Majidi , J. Mat. Sci. 36 (2001) 1451 5. E.P. George, A.N. Gubbi, I. Baker, L. Robertson, Mater. Sci. and Eng...A329–331 (2002) 325 6. R. H. Yu, S. Basu, L. Ren, Y. Zhang, A. Parvizi- Majidi , K. M. Unruh, and J. Q. Xiao, IEEE Trans. Magn., 36, (2000) 3388 7. T

Mechanical behaviour of pressed and sintered titanium alloys obtained from master alloy addition powders.

PubMed

Bolzoni, L; Esteban, P G; Ruiz-Navas, E M; Gordo, E

2012-11-01

The fabrication of the workhorse Ti-6Al-4V alloy and of the Ti-3Al-2.5V alloy was studied considering the master alloy addition variant of the blending elemental approach conventionally used for titanium powder metallurgy. The powders were characterised by means thermal analysis and X-ray diffraction and shaped by means of uniaxial pressing. The microstructural evolution with the sintering temperature (900-1400 °C) was evaluated by SEM and EDS was used to study the composition. XRD patterns as well as the density by Archimedes method were also obtained. The results indicate that master alloy addition is a suitable way to fabricate well developed titanium alloy but also to produce alloy with the desired composition, not available commercially. Density of 4.3 g/cm³ can be obtained where a temperature higher than 1200 °C is needed for the complete diffusion of the alloying elements. Flexural properties comparable to those specified for wrought Ti-6Al-4V medical devices are, generally, obtained. Copyright © 2012 Elsevier Ltd. All rights reserved.

Looking North into Lab Metallurgy Testing Area and Enrichment Motor ...

Library of Congress Historic Buildings Survey, Historic Engineering Record, Historic Landscapes Survey

Looking North into Lab Metallurgy Testing Area and Enrichment Motor within Recycle Recovery Building - Hematite Fuel Fabrication Facility, Recycle Recovery Building, 3300 State Road P, Festus, Jefferson County, MO

Titanium-hydroxyapatite composites sintered at low temperature for tissue engineering: in vitro cell support and biocompatibility.

PubMed

Comín, Romina; Cid, Mariana P; Grinschpun, Luciano; Oldani, Carlos; Salvatierra, Nancy A

2017-04-26

In clinical orthopedics, a critical problem is the bone tissue loss produced by a disease or injury. The use of composites from titanium and hydroxyapatite for biomedical applications has increased due to the resulting advantageous combination of hydroxyapatite bioactivity and favorable mechanical properties of titanium. Powder metallurgy is a simple and lower-cost method that uses powder from titanium and hydroxyapatite to obtain composites having hydroxyapatite phases in a metallic matrix. However, this method has certain limitations arising from thermal decomposition of hydroxyapatite in the titanium-hydroxyapatite system above 800°C. We obtained a composite from titanium and bovine hydroxyapatite powders sintered at 800°C and evaluated its bioactivity and cytocompatibility according to the ISO 10993 standard. Surface analysis and bioactivity of the composite was evaluated by X-ray diffraction and SEM. MTT assay was carried out to assess cytotoxicity on Vero and NIH3T3 cells. Cell morphology and cell adhesion on the composite surface were analyzed using fluorescence and SEM. We obtained a porous composite with hydroxyapatite particles well integrated in titanium matrix which presented excellent bioactivity. Our data did not reveal any toxicity of titanium-hydroxyapatite composite on Vero or NIH3T3 cells. Moreover, extracts from composite did not affect cell morphology or density. Finally, NIH3T3 cells were capable of adhering to and proliferating on the composite surface. The composite obtained displayed promising biomedical applications through the simple method of powder metallurgy. Additionally, these findings provide an in vitro proof for adequate biocompatibility of titanium-hydroxyapatite composite sintered at 800°C.

Magnetic properties of FeCuNbSiB nanocrystalline alloy powder cores using ball-milled powder

NASA Astrophysics Data System (ADS)

Kim, G. H.; Noh, T. H.; Choi, G. B.; Kim, K. Y.

2003-05-01

Cold-pressed nanocrystalline powder cores were fabricated using powders of nanocrystalline ribbons which were ball milled for short time. Their magnetic properties at high frequency were measured. The powder size ranges from 20 to 850 μm and the contents of the glass binder are between 1 and 8 wt %. For cores composed of large particles of 300-850 μm with 5 wt % glass binder, we obtained a stable permeability of 100 up to 800 kHz, a maximum level 31 of quality factor at frequency of 50 kHz, and 320 mW/cm3 core loss at f=50 kHz and Bm=0.1 T. This is mainly due to the good soft magnetic properties of the powders and the higher insulation of powder cores which cause low eddy current losses.

Sol-gel synthesis and densification of aluminoborosilicate powders. Part 2: Densification

NASA Technical Reports Server (NTRS)

Bull, Jeffrey; Selvaduray, Guna; Leiser, Daniel

1992-01-01

Aluminoborosilicate (ABS) powders, high in alumina content, were synthesized by the sol-gel process utilizing four different methods of synthesis. The effect of these methods on the densification behavior of ABS powder compacts was studied. Five regions of shrinkage in the temperature range 25-1184 C were identified. In these regions, the greatest shrinkage occurred between the gel-to-glass transition temperature (T sub g approximately equal to 835 C) and the crystallization transformation temperature (T sub t approximately equal 900 C). The dominant mechanism of densification in this range was found to be viscous sintering. ABS powders were amorphous to x-rays up to T sub t at which a multiphasic structure crystallized. No 2Al2O3.B2O3 was found in these powders as predicted in the phase diagram. Above T sub t, densification was the result of competing mechanisms including grain growth and boria fluxed viscous sintering. Apparent activation energies for densification in each region varied according to the method of synthesis.

Effect of ball milling and heat treatment process on MnBi powders magnetic properties

DOE Office of Scientific and Technical Information (OSTI.GOV)

Xie, Wei; Polikarpov, Evgueni; Choi, Jung-Pyung

The metallic compound MnBi has high intrinsic coercivity with large positive temperature coefficient. The coercivity of MnBi exceeds 12 kOe and 26 kOe at 300 K and 523 K, respectively. Hence MnBi is a good candidate for the hard phase in exchange coupled nanocomposite magnets. In order to maximize the loading of the soft phase, the size of the MnBi particle has to be close to 500 nm, the size of single magnetic domain. Low energy milling is the common method to reduce MnBi particle size. However, only 3-7 mu m size particle can be achieved without significant decomposition. Here,more » we report our effort on preparing submicron MnBi powders using traditional powder metallurgy methods. Mn55Bi45 magnetic powders were prepared using arc melting method, followed by a series of thermal-mechanical treatment to improve purity, and finished with low energy ball milling at cryogenic temperature to achieve submicron particle size. The Mn55Bi45 powders were decomposed during ball milling process and recovered during 24 h 290 degrees C annealing process. With increasing ball-milling time, the saturation magnetization of MnBi decreases, while the coercivity increases. Annealing after ball milling recovers some of the magnetization, indicating the decomposition occurred during the ball-milling process can be reversed. The coercivity of Mn55Bi45 powders are also improved as a result of the heat treatment at 290 degrees C for 24 h. The world record magnetization 71.2 emu/g measured applying a field of 23 kOe has been achieved via low energy ball mill at room temperature« less

Retention of Compressive Residual Stresses Introduced by Shot Peening in a Powder Metal Disk Superalloy

NASA Technical Reports Server (NTRS)

Gabb, Timothy P.; Danetti, Andrew; Draper, Susan L.; Locci, Ivan E.; Telesman, Jack

2016-01-01

The fatigue lives of disk superalloys can be increased by shot peening their surfaces, to induce compressive residual stresses near the surface that impede cracking there. As disk application temperatures increase for improved efficiency, the persistence of these beneficial stresses could be impaired, especially with continued fatigue cycling. The objective of this work was to study the retention of residual stresses introduced by shot peening, when subjected to fatigue and high temperatures. Fatigue specimens of powder metallurgy processed nickel-base disk superalloy ME3 were prepared with consistent processing and heat treatment. They were then shot peened using varied conditions. Strain-controlled fatigue cycles were run at room temperature and 704 C, to allow re-assessment of residual stresses.

Moisture-induced caking of beverage powders.

PubMed

Chávez Montes, Edgar; Santamaría, Nadia Ardila; Gumy, Jean-Claude; Marchal, Philippe

2011-11-01

Beverage powders can exhibit caking during storage due to high temperature and moisture conditions, leading to consumer dissatisfaction. Caking problems can be aggravated by the presence of sensitive ingredients. The caking behaviour of cocoa beverage powders, with varying amounts of a carbohydrate sensitive ingredient, as affected by climate conditions was studied in this work. Sorption isotherms of beverage powders were determined at water activities (a(w) ) ranging from 0.1 to 0.6 in a moisture sorption analyser by gravimetry and fitted to the Brunauer-Emmett-Teller (BET) or the Guggenheim-Anderson-de Boer (GAB) equation. Glass transition temperatures (T(g) ) at several a(w) were analysed by differential scanning calorimetry and fitted to the Gordon-Taylor equation. Deduced T(g) = f(a(w) ) functions helped to identify stability or caking zones. Specific experimental methods, based on the analysis of mechanical properties of powder cakes formed under compression, were used to quantify the degree of caking. Pantry tests complemented this study to put in evidence the visual perception of powder caking with increasing a(w) . The glass transition approach was useful to predict the risks of caking but was limited to products where T(g) can be measured. On the other hand, quantification of the caking degree by analysis of mechanical properties allowed estimation of the extent of degradation for each product. This work demonstrated that increasing amounts of a carbohydrate sensitive ingredient in cocoa beverages negatively affected their storage stability. Copyright © 2011 Society of Chemical Industry.

Near-Net Shape Fabrication Using Low-Cost Titanium Alloy Powders

DOE Office of Scientific and Technical Information (OSTI.GOV)

Dr. David M. Bowden; Dr. William H. Peter

2012-03-31

. Technical feasibility studies were performed to identify the most viable approaches to NNS preform fabrication using basic powder metallurgy mill product forms as the building blocks and advanced joining techniques including fusion and solid state joining to assemble these building blocks into efficient machining performs.« less

High Performance MG-System Alloys For Weight Saving Applications: First Year Results From The Green Metallurgy EU Project

NASA Astrophysics Data System (ADS)

D'Errico, Fabrizio; Plaza, Gerardo Garces; Hofer, Markus; Kim, Shae K.

The GREEN METALLURGY Project, a LIFE+ project co-financed by the EU Commission, has just concluded its first year. The Project seeks to set manufacturing processes at a pre-industrial scale for nanostructured-based high-performance Mg-Zn(Y) magnesium alloys. The Project's goal is the reduction of specific energy consumed and the overall carbon-footprint produced in the cradle-to-exit gate phases. Preliminary results addressed potentialities of the upstream manufacturing process pathway. Two Mg-Zn(Y) system alloys with rapid solidifying powders have been produced and directly extruded for 100% densification. Examination of the mechanical properties showed that such materials exhibit strength and elongation comparable to several high performing aluminum alloys; 390 MPa and 440 MPa for the average UTS for two different system alloys, and 10% and 15% elongations for two system alloys. These results, together with the low-environmental impact targeted, make these novel Mg alloys competitive as lightweight high-performance materials for automotive components.

Development Status of a CVD System to Deposit Tungsten onto UO2 Powder via the WCI6 Process

NASA Technical Reports Server (NTRS)

Mireles, O. R.; Kimberlin, A.; Broadway, J.; Hickman, R.

2014-01-01

Nuclear Thermal Propulsion (NTP) is under development for deep space exploration. NTP's high specific impulse (> 850 second) enables a large range of destinations, shorter trip durations, and improved reliability. W-60vol%UO2 CERMET fuel development efforts emphasize fabrication, performance testing and process optimization to meet service life requirements. Fuel elements must be able to survive operation in excess of 2850 K, exposure to flowing hydrogen (H2), vibration, acoustic, and radiation conditions. CTE mismatch between W and UO2 result in high thermal stresses and lead to mechanical failure as a result UO2 reduction by hot hydrogen (H2) [1]. Improved powder metallurgy fabrication process control and mitigated fuel loss can be attained by coating UO2 starting powders within a layer of high density tungsten [2]. This paper discusses the advances of a fluidized bed chemical vapor deposition (CVD) system that utilizes the H2-WCl6 reduction process.

Advanced Metalworking Solutions for Naval Systems That Go In Harm’s Way

DTIC Science & Technology

2013-01-01

quarter century of projects, including early research and development of technologies such as semi-solid metalworking; powder metallurgy; and process...modeling and simulation. More recent projects have focused on friction stir welding, hybrid laser -arc welded metallic sandwich panels, and improved...Metalworking Center has optimized a wide variety of manufacturing technologies throughout its 25-year history, including powder metallurgy processing, semi

New Powder Metallurgical Approach to Achieve High Fatigue Strength in Ti-6Al-4V Alloy

NASA Astrophysics Data System (ADS)

Cao, Fei; Ravi Chandran, K. S.; Kumar, Pankaj; Sun, Pei; Zak Fang, Z.; Koopman, Mark

2016-05-01

Recently, manufacturing of titanium by sintering and dehydrogenation of hydride powders has generated a great deal of interest. An overarching concern regarding powder metallurgy (PM) titanium is that critical mechanical properties, especially the high-cycle fatigue strength, are lower than those of wrought titanium alloys. It is demonstrated here that PM Ti-6Al-4V alloy with mechanical properties comparable (in fatigue strength) and exceeding (in tensile properties) those of wrought Ti-6Al-4V can be produced from titanium hydride powder, through the hydrogen sintering and phase transformation process. Tensile and fatigue behavior, as well as fatigue fracture mechanisms, have been investigated under three processing conditions. It is shown that a reduction in the size of extreme-sized pores by changing the hydride particle size distribution can lead to improved fatigue strength. Further densification by pneumatic isostatic forging leads to a fatigue strength of ~550 MPa, comparable to the best of PM Ti-6Al-4V alloys prepared by other methods and approaching the fatigue strengths of wrought Ti-6Al-4V alloys. The microstructural factors that limit fatigue strength in PM titanium have been investigated, and pathways to achieve greater fatigue strengths in PM Ti-6Al-4V alloys have been identified.

Tribological properties of the babbit B83-based composite materials fabricated by powder metallurgy

NASA Astrophysics Data System (ADS)

Kalashnikov, I. E.; Bolotova, L. K.; Bykov, P. A.; Kobeleva, L. I.; Katin, I. V.; Mikheev, R. S.; Kobernik, N. V.

2016-07-01

Technological processes are developed to fabricate composite materials based on B83 babbit using hot pressing of a mixture of powders in the presence of a liquid phase. As a result, the structure of the matrix B83 alloy is dispersed, the morphology of intermetallic phases is changed, and reinforcing micro- and nanosized fillers are introduced and uniformly distributed in the matrix. The tribological properties of the synthesized materials are studied. The friction of the B83 babbit + 0.5 wt % MSR + 3 wt % SiC (MSR is modified schungite rock) composite material at high loads is characterized by an increase in the stability coefficient, and the wear resistance of the material increases by a factor of 1.8 as compared to the as-cast alloy at comparable friction coefficients.

Ultrasonic characterization of microstructure in powder metal alloy

NASA Technical Reports Server (NTRS)

Tittmann, B. R.; Ahlberg, L. A.; Fertig, K.

1986-01-01

The ultrasonic wave propagation characteristics were measured for IN-100, a powder metallurgy alloy used for aircraft engine components. This material was as a model system for testing the feasibility of characterizing the microstructure of a variety of inhomogeneous media including powder metals, ceramics, castings and components. The data were obtained for a frequency range from about 2 to 20 MHz and were statistically averaged over numerous volume elements of the samples. Micrographical examination provided size and number distributions for grain and pore structure. The results showed that the predominant source for the ultrasonic attenuation and backscatter was a dense (approx. 100/cubic mm) distribution of small micropores (approx. 10 micron radius). Two samples with different micropore densities were studied in detail to test the feasibility of calculating from observed microstructural parameters the frequency dependence of the microstructural backscatter in the regime for which the wavelength is much larger than the size of the individual scattering centers. Excellent agreement was found between predicted and observed values so as to demonstrate the feasibility of solving the forward problem. The results suggest a way towards the nondestructive detection and characterization of anomalous distributions of micropores when conventional ultrasonic imaging is difficult. The findings are potentially significant toward the application of the early detection of porosity during the materials fabrication process and after manufacturing of potential sites for stress induced void coalescence leading to crack initiation and subsequent failure.

Metals in Past Societies: A Global Perspective on Indigenous African Metallurgy Shadreck Chirikure

DOE Office of Scientific and Technical Information (OSTI.GOV)

Devanathan, Ram

This slim book (166 pages) shines a spotlight on pre-industrial African metallurgy, its global connections, and anthropological implications. It integrates seemingly disparate disciplines, such as history, geology, ethnography, archeology, and metallurgy, to illustrate the diversity and innovation in metallurgy across Africa and the role of metals in the rise of socio-economic inequalities and political power. The book has 7 chapters and the focus on metals as enablers of human needs and wants is evident in each chapter. The first chapter presents the context of the work and data sources. The second chapter focuses on the origin and development of miningmore » and metallurgy in pre-industrial Africa. Chapter 3 is dedicated to the interaction of nature and culture in the process of mining. Chapter 4 deals with the transformation of the ore into metal by smelting and the sociocultural aspects of this process. Chapter 5 explores the social and cultural roles acquired by metals as a result of fabrication into objects. Chapter 6 examines the social role of metals, trade in metals, cultural contact, proto-globalization, and technology transfer. Finally, Chapter 7 draws lessons for global anthropology from the African experience. The sources of information are adequately cited and the long list of references at the end of each chapter will be a boon to researchers in this field. The author highlights the cultural aspects and social context of the adoption of metallurgy in Africa while drawing parallels between practices in pre-industrial Africa and those in other parts of the world. The book is peppered with delightful vignettes that offer insights into the process of transforming nature into culturally significant objects. For instance, African miners, like their counterparts in Nepal and Latin America, called upon deities, spirits and ancestors to mediate between nature and humans. Women had distinct roles in this process, but there were variations in these roles and

[Genetic risk of families with t(1;2)(q42;q33) GTG, RHG, QFQ, FISH].

PubMed

Stasiewicz-Jarocka, B; Raczkiewicz, B; Kowalczyk, D; Zawada, M; Midro, A T

2000-10-01

A central concept in genetic counseling is the estimation of the probability of recurrence of unfavourable pregnancy outcomes (abortion, stillbirth and birth at malformed child). In case of chromosomal changes estimates are made on basis of segregation analyses in actual pedigree. If we have a few of pedigree members than risk estimate should be performed on basis combined our data and empiric data from literature. We present individual genetic risk for carriers of unique reciprocal translocation t(1;2)(q42;q33) detected through karyotyping of the patient with miscarriage. The pedigree consisted 5 families of t(1;2)(q42;q33) carriers with 15 members of progeny was evaluated according to Stene and Stengel-Rutkowski. Cytogenetic analysis of persons of these families (7 persons) was performed on blood samples using GTG, RHG, QFQ and FISH techniques. Additional RCT pedigree analysis of Stengel-Rutkowski et at Collection, Polish Collection, Lituanian Collection, Bielorussian Collection and an available literature cases were performed. The translocation was classified as translocation at risk for double segment imbalances for trisomy 1q42-->qter together with monosomy 2q33-->qter or monosomy 1q42-->qter together with trisomy 2q33-->qter after 2:2 disjunction after adjacent-1 segregation of the meiotic chromosomes. Two improved risk values for RCT with segments 1q42-->qter, 2q33-->qter were obtained i.e. 6/44 (13.6% +/- 5.2%) and 4/20 (20% +/- 8.9%). The probability of occurrence for this translocation carriers was estimated as 7% (medium risk). On basis of direct analysis at presented pedigree a risk for miscarriage was estimated as 2/9. 1. Carrierships of t(1;2)(q42;q33) increased population risk value for unbalanced progeny at birth by 7% (medium risk) and for miscarriage 2/9. 2. Causative relation between presence of t(1;2)(q42;q33) and miscarriages is suggested. 3. Updated, new genetic risk values for RCT at risk for single segment 1q42-->qter imbalance is 6/44 (13

Microstructures and Properties of 40Cu/Ag(Invar) Composites Fabricated by Powder Metallurgy and Subsequent Thermo-Mechanical Treatment

NASA Astrophysics Data System (ADS)

Zhang, Xin; Huang, Yingqiu; Liu, Xiangyu; Yang, Lei; Shi, Changdong; Wu, Yucheng; Tang, Wenming

2018-03-01

Composites of 40Cu/Ag(Invar) were prepared via pressureless sintering and subsequent thermo-mechanical treatment from raw materials of electroless Ag-plated Invar alloy powder and electrolytic Cu powder. Microstructures and properties of the prepared composites were studied to evaluate the effect of the Ag layer on blocking Cu/Invar interfacial diffusion in the composites. The electroless-plated Ag layer was dense, uniform, continuous, and bonded tightly with the Invar alloy substrate. During sintering of the composites, the Ag layer effectively prevented Cu/Invar interfacial diffusion. During cold-rolling, the Ag layer was deformed uniformly with the Invar alloy particles. The composites exhibited bi-continuous network structure and considerably improved properties. After sintering at 775 °C and subsequent thermo-mechanical treatment, the 40Cu/Ag(Invar) composites showed satisfactory comprehensive properties: relative density of 99.0 pct, hardness of HV 253, thermal conductivity of 55.7 W/(m K), and coefficient of thermal expansion of 11.2 × 10-6/K.

Clinicopathological categorization of Epstein-Barr virus-positive T/NK-cell lymphoproliferative disease: an analysis of 42 cases with an emphasis on prognostic implications.

PubMed

Paik, Jin Ho; Choe, Ji-Young; Kim, Hyojin; Lee, Jeong-Ok; Kang, Hyoung Jin; Shin, Hee Young; Lee, Dong Soon; Heo, Dae Seog; Kim, Chul-Woo; Cho, Kwang-Hyun; Kim, Tae Min; Jeon, Yoon Kyung

2017-01-01

Epstein-Barr virus-positive T/NK-cell lymphoproliferative diseases (EBV-T/NK-LPDs) include several overlapping EBV-related conditions with variably aggressive courses. For prognostic categorization, we retrospectively analyzed 42 EBV-T/NK-LPD cases. Male (79% [33/42]), young (≤40 years; 83% [35/42]) patients and T-cell lineage (81% [34/42]; CD8/CD4 = 1.8) were predominant. Clinicopathologically, three systemic and one cutaneous category were developed: hemophagocytic lymphohistiocytosis (HLH; 26% [11/42]), chronic active EBV infection (CAEBV; 31% [13/42]), systemic unclassifiable disease (24% [10/42]), and hydroa vacciniforme/hydroa vacciniforme-like lymphoma (HV/HVL; 19% [8/42]). Prognostically, cutaneous disease (HV/HVL) was better than systemic disease (p = 0.014; median, 285 vs. 10 months). In systemic diseases, HLH was worst (p = 0.002; 3[HLH] vs. 4[unclassifiable] vs. not reached [CAEBV]). Univariate survival analysis (n = 42) revealed cytopenia (≥one lineage; p < 0.001), onset age (>40 years; p = 0.001), T-cell lineage (p = 0.041), hemophagocytic histiocytes (p = 0.031), elevated lactate dehydrogenase (p = 0.020), and liver dysfunction (p = 0.023) predicted shorter survival. In multivariate analysis, T-cell lineage (p = 0.025 [HR =11.3]) and cytopenia (p = 0.028 [HR =5.4]) were independent prognostic factors. Therefore, EBV-T/NK-LPD could be classified into four prognostic categories.

Effect of Sintering Atmosphere and Solution Treatment on Density, Microstructure and Tensile Properties of Duplex Stainless Steels Developed from Pre-alloyed Powders

NASA Astrophysics Data System (ADS)

Murali, Arun Prasad; Mahendran, Sudhahar; Ramajayam, Mariappan; Ganesan, Dharmalingam; Chinnaraj, Raj Kumar

2017-10-01

In this research, Powder Metallurgy (P/M) of Duplex Stainless Steels (DSS) of different compositions were prepared through pre-alloyed powders and elemental powders with and without addition of copper. The powder mix was developed by pot mill for 12 h to obtain the homogeneous mixture of pre-alloyed powder with elemental compositions. Cylindrical green compacts with the dimensions of 30 mm diameter and 12 mm height were compacted through universal testing machine at a pressure level of 560 ± 10 MPa. These green compacts were sintered at 1350 °C for 2 h in hydrogen and argon atmospheres. Some of the sintered stainless steel preforms were solution treated at 1050 °C followed by water quenching. The sintered as well as solution treated samples were analysed by metallography examination, Scanning Electron Microscopy and evaluation of mechanical properties. Ferrite content of sintered and solution treated DSS were measured by Fischer Ferritoscope. It is inferred that the hydrogen sintered DSS depicted better density (94% theoretical density) and tensile strength (695 MPa) than the argon sintered steels. Similarly the microstructure of solution treated DSS revealed existence of more volume of ferrite grains than its sintered condition. Solution treated hydrogen sintered DSS A (50 wt% 316L + 50 wt% 430L) exhibited higher tensile strength of 716 MPa and elongation of 17%, which are 10-13% increment than the sintered stainless steels.

Effect of Pre-Oxidation Treatment of Nano-SiC Particulates on Microstructure and Mechanical Properties of SiC/Mg-8Al-1Sn Composites Fabricated by Powder Metallurgy Combined with Hot Extrusion.

PubMed

Li, Chuan-Peng; Wang, Zhi-Guo; Zha, Min; Wang, Cheng; Yu, Hong-Chen; Wang, Hui-Yuan; Jiang, Qi-Chuan

2016-11-26

Nano-SiC particulates (n-SiC p ) reinforced Mg-8Al-1Sn (AT81) composites with different pre-oxidation parameters were fabricated by powder metallurgy (P/M) process combined with hot extrusion. The effects of pre-oxidization treatment of n-SiC p on the microstructure and tensile properties of 0.5 vol % n-SiC p /AT81 composites were investigated accordingly. The distribution of n-SiC p with different pre-oxidation parameters was homogeneous in the composites. Moreover, it was found that a thin MgAl₂O₄ layer formed at the interface when the n-SiC p were pre-oxidized at 1073 K for 2 h, while the MgAl₂O₄ layer became much thicker with pre-oxidization temperature increasing to 1273 K for 2 h. After an appropriate pre-oxidization treatment of n-SiC p at 1073 K for 2 h, the as-extruded 0.5 vol % n-SiC p /AT81 composites exhibited an enhanced strength. It was found that the yield strength (YS) and ultimate tensile strength (UTS) increased from 168 MPa and 311 MPa to 255 MPa and 393 MPa compared with the as-extruded AT81 alloy, reflecting 51.8% and 26.4% increments, respectively. The improvement of mechanical properties should be mainly attributed to the grain refinement and homogeneous distribution of n-SiC p in the composites. Moreover, a well-bonded interface and the formation of an appropriate amount of interfacial product (MgAl₂O₄) benefited the material's mechanical properties.

Effect of Pre-Oxidation Treatment of Nano-SiC Particulates on Microstructure and Mechanical Properties of SiC/Mg-8Al-1Sn Composites Fabricated by Powder Metallurgy Combined with Hot Extrusion

PubMed Central

Li, Chuan-Peng; Wang, Zhi-Guo; Zha, Min; Wang, Cheng; Yu, Hong-Chen; Wang, Hui-Yuan; Jiang, Qi-Chuan

2016-01-01

Nano-SiC particulates (n-SiCp) reinforced Mg-8Al-1Sn (AT81) composites with different pre-oxidation parameters were fabricated by powder metallurgy (P/M) process combined with hot extrusion. The effects of pre-oxidization treatment of n-SiCp on the microstructure and tensile properties of 0.5 vol % n-SiCp/AT81 composites were investigated accordingly. The distribution of n-SiCp with different pre-oxidation parameters was homogeneous in the composites. Moreover, it was found that a thin MgAl2O4 layer formed at the interface when the n-SiCp were pre-oxidized at 1073 K for 2 h, while the MgAl2O4 layer became much thicker with pre-oxidization temperature increasing to 1273 K for 2 h. After an appropriate pre-oxidization treatment of n-SiCp at 1073 K for 2 h, the as-extruded 0.5 vol % n-SiCp/AT81 composites exhibited an enhanced strength. It was found that the yield strength (YS) and ultimate tensile strength (UTS) increased from 168 MPa and 311 MPa to 255 MPa and 393 MPa compared with the as-extruded AT81 alloy, reflecting 51.8% and 26.4% increments, respectively. The improvement of mechanical properties should be mainly attributed to the grain refinement and homogeneous distribution of n-SiCp in the composites. Moreover, a well-bonded interface and the formation of an appropriate amount of interfacial product (MgAl2O4) benefited the material’s mechanical properties. PMID:28774083

Simulating transfer and persistence of a chemical marker powder for Lycopodium clavatum spores.

PubMed

Howarth, Jennifer; Coulson, Sally; Newton, Angus

2009-11-20

In this research a chemical marker powder, based on Lycopodium clavatum spores, was studied to determine its transfer and persistence on a T-shirt. Such chemical marker powders are used to provide evidence that a person has handled a covertly marked object, such as a drug package. The powder was found to transfer readily between a marked item and the person handling it. The powder was found to persist on a T-shirt for up to 13h; however, there was only a very small amount of powder remaining at this time. The rate of loss of the L. clavatum spores was found to follow a decay curve. The largest decrease in spores from the T-shirt was seen in the first 2h after the marked item had been handled.

MC3T3-E1 osteoblast attachment and proliferation on porous hydroxyapatite scaffolds fabricated with nanophase powder

PubMed Central

Smith, Ian O; McCabe, Laura R; Baumann, Melissa J

2006-01-01

Porous bone tissue engineering scaffolds were fabricated using both nano hydroxyapatite (nano HA) powder (20 nm average particle size) and micro HA powder (10 μm average particle size), resulting in sintered scaffolds of 59 vol% porosity and 8.6±1.9 μm average grain size and 72 vol% porosity and 588±55 nm average grain size, respectively. Scanning electron microscopy was used to measure both the grain size and pore size. MC3T3-E1 osteoblast (OB) attachment and proliferation on both nano HA and micro HA porous scaffolds were quantified. As expected, OB cell number was greater on nano HA scaffolds compared with similarly processed micro HA scaffolds 5 days after seeding, while OB attachment did not appear greater on the nano HA scaffolds (p<0.05). PMID:17722535

Strength-Ductility Property Maps of Powder Metallurgy (PM) Ti-6Al-4V Alloy: A Critical Review of Processing-Structure-Property Relationships

NASA Astrophysics Data System (ADS)

Kumar, P.; Chandran, K. S. Ravi

2017-05-01

A comprehensive assessment of tensile properties of powder metallurgical (PM) processed Ti-6Al-4V alloy, through the mapping of strength-ductility property domains, is performed in this review. Tensile property data of PM Ti-6Al-4V alloys made from blended element (BE) and pre-alloyed powders including that additive manufactured (AM) from powders, as well as that made using titanium hydride powders, have been mapped in the form of strength-ductility domains. Based on this, porosity and microstructure have been identified as the dominant variables controlling both the strength and the tensile ductility of the final consolidated materials. The major finding is that tensile ductility of the PM titanium is most sensitive to the presence of pores. The significance of extreme-sized pores or defects in inducing large variations in ductility is emphasized. The tensile strength, however, has been found to depend only weakly on the porosity. The effect of microstructure on properties is masked by the variations in porosity and to some extent by the oxygen level. It is shown that any meaningful comparison of the microstructure can only be made under a constant porosity or density level. The beneficial effect of a refined microstructure is also brought out by logically organizing the data in terms of microstructure groups. The advantages of new processes, using titanium hydride powder to produce PM titanium alloys, in simultaneously increasing strength and ductility, are also highlighted. The tensile properties of AM Ti-6Al-4V alloys are also brought to light, in comparison with the other PM and wrought alloys, through the strength-ductility maps.

Iron Metallurgy: Technical Terminology Bulletin. Terminotech, Vol. 2, No. 7.

ERIC Educational Resources Information Center

General Electric Co. of Canada, Ltd., Montreal, Quebec.

This issue of a bulletin of technological terminology is devoted to iron metallurgy. Various aspects of iron production are described in both French and English. An English-French dictionary of terms comprises the bulk of the document. Explanatory illustrations are appended. (JB)

Characterization of photocatalytic TiO 2 powder under varied environments using near ambient pressure X-ray photoelectron spectroscopy

DOE Office of Scientific and Technical Information (OSTI.GOV)

Krishnan, Padmaja; Liu, Minghui; Itty, Pierre A.

Consecutive eight study phases under the successive presence and absence of UV irradiation, water vapor, and oxygen were conducted to characterize surface changes in the photocatalytic TiO2 powder using near-ambient-pressure X-ray photoelectron spectroscopy (XPS). Both Ti 2p and O 1s spectra show hysteresis through the experimental course. Under all the study environments, the bridging hydroxyl (OH br) and terminal hydroxyl (OH t) are identified at 1.1–1.3 eV and 2.1–2.3 eV above lattice oxygen, respectively. This enables novel and complementary approach to characterize reactivity of TiO 2 powder. The dynamic behavior of surface-bound water molecules under each study environment is identified,more » while maintaining a constant distance of 1.3 eV from the position of water vapor. In the dark, the continual supply of both water vapor and oxygen is the key factor retaining the activated state of the TiO 2 powder for a time period. Two new surface peaks at 1.7–1.8 and 4.0–4.2 eV above lattice oxygen are designated as peroxides (OOH/H 2O 2) and H 2O 2 dissolved in water, respectively. The persistent peroxides on the powder further explain previously observed prolonged oxidation capability of TiO 2 powder without light irradiation.« less

Characterization of photocatalytic TiO 2 powder under varied environments using near ambient pressure X-ray photoelectron spectroscopy

DOE PAGES

Krishnan, Padmaja; Liu, Minghui; Itty, Pierre A.; ...

2017-02-27

Consecutive eight study phases under the successive presence and absence of UV irradiation, water vapor, and oxygen were conducted to characterize surface changes in the photocatalytic TiO2 powder using near-ambient-pressure X-ray photoelectron spectroscopy (XPS). Both Ti 2p and O 1s spectra show hysteresis through the experimental course. Under all the study environments, the bridging hydroxyl (OH br) and terminal hydroxyl (OH t) are identified at 1.1–1.3 eV and 2.1–2.3 eV above lattice oxygen, respectively. This enables novel and complementary approach to characterize reactivity of TiO 2 powder. The dynamic behavior of surface-bound water molecules under each study environment is identified,more » while maintaining a constant distance of 1.3 eV from the position of water vapor. In the dark, the continual supply of both water vapor and oxygen is the key factor retaining the activated state of the TiO 2 powder for a time period. Two new surface peaks at 1.7–1.8 and 4.0–4.2 eV above lattice oxygen are designated as peroxides (OOH/H 2O 2) and H 2O 2 dissolved in water, respectively. The persistent peroxides on the powder further explain previously observed prolonged oxidation capability of TiO 2 powder without light irradiation.« less

A millennium of metallurgy recorded by lake sediments from Morococha, Peruvian Andes.

PubMed

Cooke, Colin A; Abbott, Mark B; Wolfe, Alexander P; Kittleson, John L

2007-05-15

To date, information concerning pre-Colonial metallurgy in South America has largely been limited to the archaeological record of artifacts. Here, we reconstruct a millennium of smelting activity in the Peruvian Andes using the lake-sediment stratigraphy of atmospherically derived metals (Pb, Zn, Cu, Ag, Sb, Bi, and Ti) and lead isotopic ratios (206Pb/ 207Pb) associated with smelting from the Morococha mining region in the central Peruvian Andes. The earliest evidence for metallurgy occurs ca. 1000 A.D., coinciding with the fall of the Wari Empire and decentralization of local populations. Smelting during this interval appears to have been aimed at copper and copper alloys, because of large increases in Zn and Cu relative to Pb. A subsequent switch to silver metallurgy under Inca control (ca. 1450 to conquest, 1533 A.D.) is indicated by increases in Pb, Sb, and Bi, a conclusion supported by further increases of these metals during Colonial mining, which targeted silver extraction. Rapid development of the central Andes during the 20th century raised metal burdens by an order of magnitude above previous levels. Our results represent the first evidence for pre-Colonial smelting in the central Peruvian Andes, and corroborate the sensitivity of lake sediments to pre-Colonial metallurgical activity suggested by earlier findings from Bolivia.

Valorizing waste iron powder in biogas production: Hydrogen sulfide control and process performances.

PubMed

Andriamanohiarisoamanana, Fetra J; Shirai, Tomoya; Yamashiro, Takaki; Yasui, Seiichi; Iwasaki, Masahiro; Ihara, Ikko; Nishida, Takehiro; Tangtaweewipat, Suchon; Umetsu, Kazutaka

2018-02-15

Biogas is composed of different gases including hydrogen sulfide (H 2 S), which is a hazardous gas that damages pipes and generators in anaerobic digestion system. The objective of this study was to control H 2 S by waste iron powder produced by laser cutting machine in a steel and iron industry. Waste iron powder was mixed with dairy manure at a concentration between 2.0 and 20.0 g/L in batch experiments, while the concentration was varied between 1.0 and 4.0 g/L in bench experiment. In batch experiment, a reduction of up to 93% of H 2 S was observed at waste iron powder of 2.0 g/L (T1), while the reduction was of more than 99% at waste iron powder beyond 8.0 g/L (T4 ∼ T6). The total sulfide concentration (S T ) increased together with waste iron powder concentration and was fitted with a quadratic equation with a maximum S T of 208.0 mg/L at waste iron powder of 20.2 g/L. Waste iron powder did not have significant effect on methane yield in batch and bench experiments. However, hydrolysis rate constant was increased by almost 100%, while the lag-phase period was reduced to half in test digesters compared to that in control digester. In bench experiment, H 2 S concentration was reduced by 89% at 2.0 g/L, while 50% at 1.0 g/L. Therefore, waste iron powder was effectively removed H 2 S and did not affect negatively anaerobic digestion process. Copyright © 2017 Elsevier Ltd. All rights reserved.

Novel Fe-based nanocrystalline powder cores with excellent magnetic properties produced using gas-atomized powder

NASA Astrophysics Data System (ADS)

Chang, Liang; Xie, Lei; Liu, Min; Li, Qiang; Dong, Yaqiang; Chang, Chuntao; Wang, Xin-Min; Inoue, Akihisa

2018-04-01

FeSiBPNbCu nanocrystalline powder cores (NPCs) with excellent magnetic properties were fabricated by cold-compaction of the gas-atomized amorphous powder. Upon annealing at the optimum temperature, the NPCs showed excellent magnetic properties, including high initial permeability of 88, high frequency stability up to 1 MHz with a constant value of 85, low core loss of 265 mW/cm3 at 100 kHz for Bm = 0.05 T, and superior DC-bias permeability of 60% at a bias field of 100 Oe. The excellent magnetic properties of the present NPCs could be attributed to the ultrafine α-Fe(Si) phase precipitated in the amorphous matrix and the use of gas-atomized powder coated with a uniform insulation layer.

Effect of process control agent on the porous structure and mechanical properties of a biomedical Ti-Sn-Nb alloy produced by powder metallurgy.

PubMed

Nouri, A; Hodgson, P D; Wen, C E

2010-04-01

The influence of different amounts and types of process control agent (PCA), i.e., stearic acid and ethylene bis-stearamide, on the porous structure and mechanical properties of a biomedical Ti-16Sn-4Nb (wt.%) alloy was investigated. Alloy synthesis was performed on elemental metal powders using high-energy ball milling for 5h. Results indicated that varying the PCA content during ball milling led to a drastic change in morphology and particle-size distribution of the ball-milled powders. Porous titanium alloy samples sintered from the powders ball milled with the addition of various amounts of PCA also revealed different pore morphology and porosity. The Vickers hardness of the sintered titanium alloy samples exhibited a considerable increase with increasing PCA content. Moreover, the addition of larger amounts of PCA in the powder mixture resulted in a significant increase in the elastic modulus and peak stress for the sintered porous titanium alloy samples under compression. It should also be mentioned that the addition of PCA introduced contamination (mainly carbon and oxygen) into the sintered porous product. Crown Copyright 2009. Published by Elsevier Ltd. All rights reserved.

Anodization Mechanism on SiC Nanoparticle Reinforced Al Matrix Composites Produced by Power Metallurgy.

PubMed

Ferreira, Sonia C; Conde, Ana; Arenas, María A; Rocha, Luis A; Velhinho, Alexandre

2014-12-19

Specimens of aluminum-based composites reinforced by silicon carbide nanoparticles (Al/SiC np ) produced by powder metallurgy (PM) were anodized under voltage control in tartaric-sulfuric acid (TSA). In this work, the influence of the amount of SiC np on the film growth during anodizing was investigated. The current density versus time response and the morphology of the porous alumina film formed at the composite surface are compared to those concerning a commercial aluminum alloy (AA1050) anodized under the same conditions. The processing method of the aluminum alloys influences the efficiency of the anodizing process, leading to a lower thicknesses for the unreinforced Al-PM alloy regarding the AA1050. The current density versus time response is strongly dependent on the amount of SiC np . The current peaks and the steady-state current density recorded at each voltage step increases with the SiC np volume fraction due to the oxidation of the SiC np . The formation mechanism of the anodic film on Al/SiC np composites is different from that occurring in AA1050, partly due the heterogeneous distribution of the reinforcement particles in the metallic matrix, but also to the entrapment of SiC np in the anodic film.

Anodization Mechanism on SiC Nanoparticle Reinforced Al Matrix Composites Produced by Power Metallurgy

PubMed Central

Ferreira, Sonia C.; Conde, Ana; Arenas, María A.; Rocha, Luis A.; Velhinho, Alexandre

2014-01-01

Specimens of aluminum-based composites reinforced by silicon carbide nanoparticles (Al/SiCnp) produced by powder metallurgy (PM) were anodized under voltage control in tartaric-sulfuric acid (TSA). In this work, the influence of the amount of SiCnp on the film growth during anodizing was investigated. The current density versus time response and the morphology of the porous alumina film formed at the composite surface are compared to those concerning a commercial aluminum alloy (AA1050) anodized under the same conditions. The processing method of the aluminum alloys influences the efficiency of the anodizing process, leading to a lower thicknesses for the unreinforced Al-PM alloy regarding the AA1050. The current density versus time response is strongly dependent on the amount of SiCnp. The current peaks and the steady-state current density recorded at each voltage step increases with the SiCnp volume fraction due to the oxidation of the SiCnp. The formation mechanism of the anodic film on Al/SiCnp composites is different from that occurring in AA1050, partly due the heterogeneous distribution of the reinforcement particles in the metallic matrix, but also to the entrapment of SiCnp in the anodic film. PMID:28788295

40 CFR 471.101 - Effluent limitations representing the degree of effluent reduction attainable by the application...

Code of Federal Regulations, 2010 CFR

2010-07-01

... million off-pounds) of power metallurgy parts steam treated Copper 1.51 0.792 Cyanide 0.230 0.095 Lead 0... metallurgy parts tumbled, burnished, or cleaned Copper 8.36 4.40 Cyanide 1.28 0.528 Lead 1.85 0.880 Oil and... Maximum for monthly average mg/off-kg (pounds per million off-pounds) of powder metallurgy parts sawed or...

Indexation Rules for Metallurgy in PASCAL. Original Title: Regles d'Indexation de la Metallurgie'--Technical Note Issued by Informascience--January 1980. Translated by Marie Wallin.

ERIC Educational Resources Information Center

Royal Inst. of Tech., Stockholm (Sweden). Library.

The indexing rules presented are designed for use with a new French-German database on metallurgy being developed under an agreement by CNRS (Centre National de la Recherche Scientifique, Paris) and BAM (Bundesanstalt fur Materialprufung, Berlin). The new database, which will feature multilingual titles and index terms (French-German-English-) and…

Thermal analysis and evolution of shape loss phenomena during polymer burnout in powder metal processing

NASA Astrophysics Data System (ADS)

Enneti, Ravi Kumar

2005-07-01

Powder metallurgy technology involves manufacturing of net shape or near net shape components starting from metal powders. Polymers are used to provide lubrication during shaping and handling strength to the shaped component. After shaping, the polymers are removed from the shaped components by providing thermal energy to burnout the polymers. Polymer burnout is one of the most critical step in powder metal processing. Improper design of the polymer burnout cycle will result in formation of defects, shape loss, or carbon contamination of the components. The effect of metal particles on polymer burnout and shape loss were addressed in the present research. The study addressing the effect of metal powders on polymer burnout was based on the hypothesis that metal powders act to catalyze polymer burnout. Thermogravimetric analysis (TGA) on pure polymer, ethylene vinyl acetate (EVA), and on admixed powders of 316L stainless steel and 1 wt. % EVA were carried out to verify the hypothesis. The effect of metal powders additions was studied by monitoring the onset temperature for polymer degradation and the temperature at which maximum rate of weight loss occurred from the TGA data. The catalytic behavior of the powders was verified by varying the particle size and shape of the 316L stainless powder. The addition of metal particles lowered the polymer burnout temperatures. The onset temperature for burnout was found to be sensitive to the surface area of the metal particle as well as the polymer distribution. Powders with low surface area and uniform distribution of polymer showed a lower burnout temperature. The evolution of shape loss during polymer burnout was based on the hypothesis that shape loss occurs during the softening of the polymer and depends on the sequence of chemical bonding in the polymer during burnout. In situ observation of shape loss was carried out on thin beams compacted from admixed powders of 316L stainless steel and 1 wt. % ethylene vinyl acetate

Fatigue behavior of highly porous titanium produced by powder metallurgy with temporary space holders.

PubMed

Özbilen, Sedat; Liebert, Daniela; Beck, Tilmann; Bram, Martin

2016-03-01

Porous titanium cylinders were produced with a constant amount of temporary space holder (70 vol.%). Different interstitial contents were achieved by varying the starting powders (HDH vs. gas atomized) and manufacturing method (cold compaction without organic binders vs. warm compaction of MIM feedstocks). Interstitial contents (O, C, and N) as a function of manufacturing were measured by chemical analysis. Samples contained 0.34-0.58 wt.% oxygen, which was found to have the greatest effect on mechanical properties. Quasi-static mechanical tests under compression at low strain rate were used for reference and to define parameters for cyclic compression tests. Not unexpectedly, increased oxygen content increased the yield strength of the porous titanium. Cyclic compression fatigue tests were conducted using sinusoidal loading in a servo-hydraulic testing machine. Increased oxygen content was concomitant with embrittlement of the titanium matrix, resulting in significant reduction of compression cycles before failure. For samples with 0.34 wt.% oxygen, R, σ(min) and σ(max) were varied systematically to estimate the fatigue limit (~4 million cycles). Microstructural changes induced by cyclic loading were then characterized by optical microscopy, SEM and EBSD. Copyright © 2015 Elsevier B.V. All rights reserved.

Synthesis of Ti-Ta alloys with dual structure by incomplete diffusion between elemental powders.

PubMed

Liu, Yong; Li, Kaiyang; Wu, Hong; Song, Min; Wang, Wen; Li, Nianfeng; Tang, Huiping

2015-11-01

In this work, powder metallurgical (PM) Ti-Ta alloys were sintered using blended elemental powders. A dual structure, consisting of Ti-rich and Ta-rich zones, was formed due to the insufficient diffusion between Ti and Ta powders. The microstructure, mechanical properties and in vitro biological properties of the alloys were studied. Results indicated that the alloys have inhomogenous microstructures and compositions, but the grain structures were continuous from the Ti-rich zone to the Ta-rich zone. The Ta-rich zone exhibited a much finer grain size than the Ti-rich zone. The alloys had a high relative density in the range of 95-98%, with the porosity increasing with the content of Ta due to the increased difficulty in sintering and the formation of Kirkendall pores. The alloys had a good combination of low elastic modulus and high tensile strength. The strength of alloys was almost doubled compared to that of the ingot metallurgy alloys with the same compositions. The low elastic modulus was due to the residual pores and the alloying effect of Ta, while the high tensile strength resulted from the strengthening effects of solid solution, fine grain size and α phase. The alloys had a high biocompatibility due to the addition of Ta, and were suitable for the attachment of cells due to the surface porosity. It was also indicated that PM Ti-(20-30)Ta alloys are promising for biomedical applications after the evaluations of both the mechanical and the biological properties. Copyright © 2015 Elsevier Ltd. All rights reserved.

Al and Mg Alloys for Aerospace Applications Using Rapid Solidification and Powder Metallurgy Processing.

DTIC Science & Technology

1986-11-14

5wt % Si was completely different from that of the alloy without silicon. The (X phase formed around the primary Mg2 Si crystals, and an irregular...content, and primary crystals in a binary Mg- 5wt % Si alloy did not exhibit this behavior. The surface of the rapidly solidified melt pools was rough and...Microhardness* of the laser treated alloys . Alloy As-cast Laser treated Mg- 5wt %Li 40.8 55.7 o, Mg- 5wt %Li- 5wt % Si 51.1 74.1 Mg-8wt%Li 42.8 71.2

T Cell Epitope Regions of the P. falciparum MSP1-33 Critically Influence Immune Responses and In Vitro Efficacy of MSP1-42 Vaccines

PubMed Central

Pusic, Kae M.; Hashimoto, Caryn N.; Lehrer, Axel; Aniya, Charmaine; Clements, David E.; Hui, George S.

2011-01-01

The C-terminal 42 kDa fragments of the P. falciparum Merozoite Surface Protein 1, MSP1-42 is a leading malaria vaccine candidate. MSP1-33, the N-terminal processed fragment of MSP1-42, is rich in T cell epitopes and it is hypothesized that they enhance antibody response toward MSP1-19. Here, we gave in vivo evidence that T cell epitope regions of MSP1-33 provide functional help in inducing anti-MSP1-19 antibodies. Eleven truncated MSP1-33 segments were expressed in tandem with MSP1-19, and immunogenicity was evaluated in Swiss Webster mice and New Zealand White rabbits. Analyses of anti-MSP1-19 antibody responses revealed striking differences in these segments' helper function despite that they all possess T cell epitopes. Only a few fragments induced a generalized response (100%) in outbred mice. These were comparable to or surpassed the responses observed with the full length MSP1-42. In rabbits, only a subset of truncated antigens induced potent parasite growth inhibitory antibodies. Notably, two constructs were more efficacious than MSP1-42, with one containing only conserved T cell epitopes. Moreover, another T cell epitope region induced high titers of non-inhibitory antibodies and they interfered with the inhibitory activities of anti-MSP1-42 antibodies. In mice, this region also induced a skewed TH2 cellular response. This is the first demonstration that T cell epitope regions of MSP1-33 positively or negatively influenced antibody responses. Differential recognition of these regions by humans may play critical roles in vaccine induced and/or natural immunity to MSP1-42. This study provides the rational basis to re-engineer more efficacious MSP1-42 vaccines by selective inclusion and exclusion of MSP1-33 specific T cell epitopes. PMID:21931852

Cerebroprotective Actions of Triticum aestivum Linn Powder and Bauhinia purpurea Flower Powder in Surgically Induced Cerebral Infraction in Rats.

PubMed

Annapurna, Akula; Vishala, Thonangi C; Bitra, Veera R; Rapaka, Deepthi; Shaik, Asmath

2018-01-01

The prime objective of this study is to evaluate the cerebroprotective actions of Triticum aestivum (wheatgrass) powder and Bauhinia purpurea flower (dev kanchan) powder against the experimentally induced global ischemia reperfusion injury in rats. In the first phase of the studies, 1 h before the surgical procedure, the Wistar rats were orally served with varied doses of wheatgrass powder (5, 10, 30, and 100 μg/kg) and Bauhinia flower powder (30, 100, 200, and 300 μg/kg), respectively. The ischemia was induced by 30-min bilateral carotid artery occlusion in succession to reperfusion for 4 h. It was proved that the wheatgrass powder and Bauhinia flower powder yielded a significant, dose-dependent cerebroprotection in terms of reduction in cerebral infarct size when compared with the control group. Coming to the second phase of the studies, a certain potential dose of 10 μg/kg of wheatgrass and 200 μg/kg of Bauhinia flower powders was selected keeping the protective action in view, and the animals were treated for 15 days. The major findings of the study are that wheatgrass and Bauhinia flower powders significantly augmented the magnitude of the antioxidant enzymes, viz., super oxide dismutase and catalase, and further reduced the levels of lipid peroxidation. The present study clearly showed that the wheatgrass powder and Bauhinia flower powder possess significant antioxidant properties that may act as a key ingredient in various ayurvedic preparations for the treatment of various diseases like cerebral ischemic reperfusion injury. The wheat grass contains high amount of bioflavonoids, alkaloids, SOD etc which are responsible for anti oxidant activity.The Bauhinia purpurea contains glycosides, flavonoids and also plays a major role in DPPH activity which is responsible for anti oxidant activity.The wheat grass (10 mg/kg) and bauhinia (200 mg/kg) significantly(P < 0.0001) reduced the percentage of infract size when compared to Ischemia reperfusion control group

Cerebroprotective Actions of Triticum aestivum Linn Powder and Bauhinia purpurea Flower Powder in Surgically Induced Cerebral Infraction in Rats

PubMed Central

Annapurna, Akula; Vishala, Thonangi C.; Bitra, Veera R.; Rapaka, Deepthi; Shaik, Asmath

2017-01-01

Objective: The prime objective of this study is to evaluate the cerebroprotective actions of Triticum aestivum (wheatgrass) powder and Bauhinia purpurea flower (dev kanchan) powder against the experimentally induced global ischemia reperfusion injury in rats. Materials and Methods: In the first phase of the studies, 1 h before the surgical procedure, the Wistar rats were orally served with varied doses of wheatgrass powder (5, 10, 30, and 100 μg/kg) and Bauhinia flower powder (30, 100, 200, and 300 μg/kg), respectively. The ischemia was induced by 30-min bilateral carotid artery occlusion in succession to reperfusion for 4 h. It was proved that the wheatgrass powder and Bauhinia flower powder yielded a significant, dose-dependent cerebroprotection in terms of reduction in cerebral infarct size when compared with the control group. Coming to the second phase of the studies, a certain potential dose of 10 μg/kg of wheatgrass and 200 μg/kg of Bauhinia flower powders was selected keeping the protective action in view, and the animals were treated for 15 days. Results: The major findings of the study are that wheatgrass and Bauhinia flower powders significantly augmented the magnitude of the antioxidant enzymes, viz., super oxide dismutase and catalase, and further reduced the levels of lipid peroxidation. Conclusions: The present study clearly showed that the wheatgrass powder and Bauhinia flower powder possess significant antioxidant properties that may act as a key ingredient in various ayurvedic preparations for the treatment of various diseases like cerebral ischemic reperfusion injury. SUMMARY The wheat grass contains high amount of bioflavonoids, alkaloids, SOD etc which are responsible for anti oxidant activity.The Bauhinia purpurea contains glycosides, flavonoids and also plays a major role in DPPH activity which is responsible for anti oxidant activity.The wheat grass (10 mg/kg) and bauhinia (200 mg/kg) significantly(P < 0.0001) reduced the percentage of

Quality of low-fat pork sausages with tomato powder as colour and functional additive during refrigerated storage.

PubMed

Kim, Il-Suk; Jin, Sang-Keun; Mandal, Prabhat Kumar; Kang, Suk-Nam

2011-10-01

Low fat pork sausages were formulated with tomato powder at 0% (C), 0.8% (T1), 1.2% (T2) and 1.5% (T3) levels in basic formula. With the increase in tomato powder concentration the lightness of the sausage decreased but the redness and yellowness increased significantly (p < 0.05). The pH values of T2 and T3 were significantly (p < 0.05) lower than the others, whereas, water holding capacity of T2 and T3 was significantly (p < 0.05) higher. Thiobarbituric acid reactive substances, cohesiveness and springiness values of treated groups were significantly (p < 0.05) lower than those of control samples, however, hardness values of sausages with tomato powder were significantly (p < 0.05) higher. The scores of overall acceptability in tested groups were significantly (p < 0.05) higher than those of control samples after 30 days of storage. The low fat pork sausage with tomato powder up to 1.5% was found to be well acceptable up to 30 days at refrigerated storage. This new product will have special value due to the functional additive lycopene in tomato powder.

The Application of Thermal Plasma to Extraction Metallurgy and Related Fields

NASA Technical Reports Server (NTRS)

Akashi, K.

1980-01-01

Various applications of thermal plasma to extraction metallurgy and related fields are surveyed, chiefly on the basis of documents published during the past two or three years. Applications to melting and smelting, to thermal decomposition, to reduction, to manufacturing of inorganic compounds, and to other fields are considered.

Application of probiotics and different size of sodium bicarbonate powders for feedlot sheep fattening

NASA Astrophysics Data System (ADS)

Supratman, Hery; Ramdani, Diky; Kuswaryan, Sondy; Budinuryanto, Dwi Cipto; Joni, I. Made

2018-02-01

This paper reports the use of probiotic and sodium bicarbonate in the diet of feedlot sheep. Probiotics from Heriyaki powder can function as forge preservative and sodium bicarbonate as an artificial rumen buffer that helps to stabilize pH levels in sheep's stomach. The objectives of this formulation is to improve the rumen function, feed efficiency and reduce the risk of acidosis leading to a significant increase of average daily gain (ADG, gram/head/day) of feedlot sheep. Heriyaki probiotic liquid was prepared by fermenting beans mixed with sugarcane molasses while Heriyaki powder was obtained by mixing the Heriyaki probiotic liquid with rice hull powder and additional molasses sugarcane in anaerobic condition for 5 days. The powder was then applied for preparing whole maize silage 0.5 wt% in anaerobic condition for 7 days before feeding. Meanwhile, the feed concentrate contained acid buffer of sodium bicarbonate powder at different doses and sizes [0.35 wt% commercial size (T1), 0.18 wt% mesh -400 (T2) and 0.35 wt% mesh -400 (T3)]. The diet treatment was a total mixed ratio containing 1 kg silage and 700 g concentrate. The experiment was conducted to compare the effect of 3 different treatments (T1, T2 and T3) on dry matter intake (DMI, g/day), ADG and feed conversion ratio (FCR) of feedlot sheep for 2 months fattening, where each treatment was applied into a flock colony for 6 heads of sheep with three flock replications involving 54 heads of sheep in total for all the treatments. The results showed no difference (P>0.05) in DMI, ADG and FCR of feedlot sheep confirming the use of low-dose and finer sodium bicarbonate powder in T2 yield a targeted ADG of > 110 g but being more efficient than other treatments.

[Risk and features of occupational diseases in nonferrous metallurgy workers of Kolsky Transpolar area].

PubMed

Siurin, S A; Chashchin, V P; Frolova, N M

2015-01-01

The study covered data on 977 cases of occupational diseases in 615 workers of nonferrous metallurgy in Kolsky Transpolar area. Findings are high risk of occupational diseases in workers engaged into electrolysis production of aluminium, all nickel reprocessing and pyrometallic copper reprocessing (GR 7.02-10.0). Electrolysis operators and anode operators of aluminium production are more prone to occupational diseases, with bone and muscular disorders (46.8%) prevalent in the morbidity structure. Respiratory diseases are more prevalent (68.2-100%) in the occupational morbidity structure of copper-nickelindustry workers. Conclusion is made on mandatory improvement of the work conditions and more effective individual protective means against occupational hazards in workers of nonferrous metallurgy in Kolsky Transpolar area.

Effect of sintering atmosphere on properties of porous stainless steel for biomedical applications.

PubMed

Dudek, Agata; Włodarczyk, Renata

2013-01-01

This study discusses manufacturing of metallic biomaterials by means of powder metallurgy with consideration for their unquestionable advantages, i.e. opportunities of obtaining materials with controllable porosity. The paper focuses on properties of 316 L stainless steel obtained using the method of powder metallurgy with respect to compacting pressure and sintering atmosphere. All the specimens were compacted at 700, 400 and 225 MPa, and sintered at 1250 °C. In order to analyze the sintering atmosphere, three different media were used: dissociated ammonia, hydrogen and vacuum. The study covered sintering density, porosity, microstructure analysis and corrosion resistance. The proposed method of powder metallurgy allowed for obtaining materials with predictable size and distribution of pores, depending on the parameters of sinter preparation (compaction force, sinter atmosphere). High corrosion resistance of the materials (sintering in the atmosphere of hydrogen and in vacuum) and high porosity in the sinters studied offer opportunities for using them for medical purposes. Copyright © 2012 Elsevier B.V. All rights reserved.

Effects of C and Hf concentration on phase relations and microstructure of a wrought powder-metallurgy superalloy

NASA Technical Reports Server (NTRS)

Miner, R. V., Jr.

1977-01-01

NASA IIB-11, a candidate alloy for advanced temperature turbine engine disks, and four modifications with varying C and Hf concentrations were produced from prealloyed powders. Several notable effects of C and Hf concentration in the alloys were observed. Both the amount of the gamma-prime phase and its solvus temperature increased with decreasing C, but only the gamma-prime solvus was affected by Hf, increasing with increasing Hf. Hf also promoted a cellular gamma-prime precipitation. Hf was, however, about equally distributed between gamma-prime and gamma. Hf and C both affected the carbides formed. Increasing both promoted formation of an MC relative to that of an M6C.

Effects of long-time elevated temperature exposures on hot-isostatically-pressed power-metallurgy Udimet 700 alloys with reduced cobalt contents

NASA Technical Reports Server (NTRS)

Hart, F. H.

1984-01-01

Because almost the entire U.S. consumption of cobalt depends on imports, this metal has been designated "strategic'. The role and effectiveness of cobalt is being evaluated in commercial nickel-base superalloys. Udiment 700 type alloys in which the cobalt content was reduced from the normal 17% down to 12.7%, 8.5%, 4.3%, and 0% were prepared by standard powder metallurgy techniques and hot isostatically pressed into billets. Mechanical testing and microstructural investigations were performed. The mechanical properties of alloys with reduced cobalt contents which were heat-treated identically were equal or better than those of the standard alloy, except that creep rates tended to increase as cobalt was reduced. The effects of long time exposures at 760 C on mechanical properties and at 760 C and 845 C on microstructures were determined. Decreased tensile properties and shorter rupture lives with increased creep rates were observed in alloy modifications. The exposures caused gamma prime particle coarsening and formation of sigma phase in the alloys with higher cobalt contents. Exposure at 845 C also reduced the amount of MC carbides.

Functionally gradient material of the system Ni-MgO, Ni-NiO, Ni-Si3N4 or Al-AlN, by pressureless sintering

DOE Office of Scientific and Technical Information (OSTI.GOV)

Atarashiya, Koji; Kurokawa, Kazuya; Nagai, Tadao

1992-08-01

Generally speaking, the preparation of FGM-blocks, especially in the metal-nitride systems, by the method of powder metallurgy needs an extremely high temperature and high pressure. But, in this work using a ductile nickel metal powder or an ultrafine particle, the FGM-blocks were easily prepared using a powder metallurgy at a lower temperature. A mixture of a metallic powder and a non-metallic powder whose contents were gradually changed was pressed in a steel die under pressure of 20-32 MPa. These green compacts were heated at 900-1573 K in controlled atmosphere under null pressure. The FGM-blocks prepared by this method were characterizedmore » by their properties and were used in joinings. The joinings of metal/FGM/ceramics, metal/FGM and ceramics/FGM were completely accomplished at 900-1573 K. 6 refs.« less

Efficient up-conversion in Yb:Er:NaT(XO4)2 thermal nanoprobes. Imaging of their distribution in a perfused mouse

PubMed Central

Serrano, María Dolores; Han, Xiumei; Cascales, Concepción; Cantero, Marta; Montoliu, Lluís; Arza, Elvira; Caiolfa, Valeria R.; Zamai, Moreno

2017-01-01

Yb and Er codoped NaT(XO4)2 (T = Y, La, Gd, Lu and X = Mo, W) disordered oxides show a green (Er3+ related) up-conversion (UC) efficiency comparable to that of Yb:Er:β-NaYF4 compound and unless 3 times larger UC ratiometric thermal sensitivity. The similar UC efficiency of Yb:Er doped NaT(XO4)2 and β-NaYF4 compounds allowed testing equal subcutaneous depths of ex-vivo chicken tissue in both cases. This extraordinary behavior for NaT(XO4)2 oxides with large cutoff phonon energy (ħω≈ 920 cm-1) is ascribed to 4F9/2 electron population recycling to higher energy 4G11/2 level by a phonon assisted transition. Crystalline nanoparticles of Yb:Er:NaLu(MoO4)2 have been synthesized by sol-gel with sizes most commonly in the 50–80 nm range, showing a relatively small reduction of the UC efficiency with regards to bulk materials. Fluorescence lifetime and multiphoton imaging microscopies show that these nanoparticles can be efficiently distributed to all body organs of a perfused mouse. PMID:28542327

Geomorphic record of historical ferrous metallurgy in Mała Panew and Czarna River valleys (Poland) - Analysis of DEM from airborne LiDAR

NASA Astrophysics Data System (ADS)

Rutkiewicz, Paweł; Malik, Ireneusz; Gawior, Daniel; Woskowicz-Ślezak, Beata; Kryszczuk, Paweł

2017-11-01

Ferrous metallurgy, through the centuries of its activity contributed the transformation of the natural landscape. We can find information on the time of functioning of iron works in historical sources. Among historians, there is an opinion that the traces of iron works activity are not visible in the field, but using GIS methods we can identify different types of objects related to ferrous metallurgy like dams, canals, smelter ponds and charcoal kilns. The aim of the study was to identify imprints of ferrous metallurgy in relief of two valleys in Southern Poland. The study was conducted in Mała Panew and Czarna River valleys where ferrous metallurgy, based on historical sources, has started in the 14th century and declined in the end of the 19th century. The tools used for identification objects related to ferrous metallurgy were standard shaded relief visualization techniques. We created models of terrain elevation with hillshading and spatial density of 0.2 m. During the analysis of DEM images we detected objects interpreted as traces of smelter ponds with accompanying dams and canals, and oval objects recognized as remnants of charcoal kilns. Large number and vast distribution of relief features related to ferrous metallurgy, charcoal kilns in particular, clearly indicate that the historical smelting and ironwork activity natural environment of studied areas was transformed. Relief of valley floors, in particular, was a subject of change.

[Analysis of changes in characteristics of arterial hypertension occupational risk in workers of nonferrous metallurgy].

PubMed

Vlasova, E M; Shliapnikov, D M; Lebedeva, T M

2015-01-01

The article covers changes in occupational cardiovascular risk for workers of nonferrous,metallurgy. Findings are that exposure to noise up to 94 dB with length of service increases possible atherosclerosis and metabolic syndrome. With 5 years of service, risk of the predicted conditions increases by 40.5%. When occupational exposure lasts over 5 years, risk of arterial hypertension increases. A group of workers without exposure to occupational factors appeared to have no connection between length of service and metabolic syndrome and arterial hypertension. Risk evolution modelling proved that risk of functional disorders in nonferrous metallurgy workers becomes unacceptable after 5 years of service (cardiovascular disorders are critical).

Low temperature fabrication of magnesium phosphate cement scaffolds by 3D powder printing.

PubMed

Klammert, Uwe; Vorndran, Elke; Reuther, Tobias; Müller, Frank A; Zorn, Katharina; Gbureck, Uwe

2010-11-01

Synthetic bone replacement materials are of great interest because they offer certain advantages compared with organic bone grafts. Biodegradability and preoperative manufacturing of patient specific implants are further desirable features in various clinical situations. Both can be realised by 3D powder printing. In this study, we introduce powder-printed magnesium ammonium phosphate (struvite) structures, accompanied by a neutral setting reaction by printing farringtonite (Mg(3)(PO(4))(2)) powder with ammonium phosphate solution as binder. Suitable powders were obtained after sintering at 1100°C for 5 h following 20-40 min dry grinding in a ball mill. Depending on the post-treatment of the samples, compressive strengths were found to be in the range 2-7 MPa. Cytocompatibility was demonstrated in vitro using the human osteoblastic cell line MG63.

Air-powder polishing on self-ligating brackets after clinical use: effects on debris levels.

PubMed

Aragón, Mônica L S Castro; Lima, Leandro Santiago; Normando, David

2016-01-01

Debris buildup on brackets and arch surfaces is one of the main factors that can influence the intensity of friction between bracket and orthodontic wire. This study sought to evaluate the effect of air-powder polishing cleaning on debris levels of self-ligating ceramic brackets at the end of orthodontic treatment, compared to the behavior of conventional brackets. Debris levels were evaluated in metal conventional orthodontic brackets (n = 42) and ceramic self-ligating brackets (n = 42) on canines and premolars, arranged in pairs. There were brackets with and without air-powder polishing. At the end of orthodontic treatment, a hemiarch served as control and the contralateral hemiarch underwent prophylaxis with air-powder polishing. Debris buildup in bracket slots was assessed through images, and Wilcoxon test was used to analyze the results. The median debris levels were statistically lower in the conventional metal brackets compared to self-ligating ones (p = 0.02), regarding brackets not submitted to air-powder polishing. Polishing significantly reduced debris buildup to zero in both systems, without differences between groups. Ceramic self-ligating brackets have a higher debris buildup in comparison to conventional metal brackets in vivo, but prophylaxis with sodium bicarbonate jet was effective in reducing debris levels in self-ligating and also in conventional brackets.

Sol-gel synthesis and densification of aluminoborosilicate powders. Part 1: Synthesis

NASA Technical Reports Server (NTRS)

Bull, Jeffrey; Selvaduray, Guna; Leiser, Daniel

1992-01-01

Aluminoborosilicate powders high in alumina content were synthesized by the sol-gel process utilizing various methods of preparation. Properties and microstructural effects related to these syntheses were examined. After heating to 600 C for 2 h in flowing air, the powders were amorphous with the metal oxides comprising 87 percent of the weight and uncombusted organics the remainder. DTA of dried powders revealed a T(sub g) at approximately 835 C and an exotherm near 900 C due to crystallization. Powders derived from aluminum secbutoxide consisted of particles with a mean diameter 5 microns less than those from aluminum isopropoxide. Powders synthesized with aluminum isopropoxide produced agglomerates comprised of rod shaped particulates while powders made with the secbutoxide precursor produced irregular glassy shards. Compacts formed from these powders required different loadings for equivalent densities according to the method of synthesis.

Hardness and wear analysis of Cu/Al2O3 composite for application in EDM electrode

NASA Astrophysics Data System (ADS)

Hussain, M. Z.; Khan, U.; Jangid, R.; Khan, S.

2018-02-01

Ceramic materials, like Aluminium Oxide (Al2O3), have high mechanical strength, high wear resistance, high temperature resistance and good chemical durability. Powder metallurgy processing is an adaptable method commonly used to fabricate composites because it is a simple method of composite preparation and has high efficiency in dispersing fine ceramic particles. In this research copper and novel material aluminium oxide/copper (Al2O3/Cu) composite has been fabricated for the application of electrode in Electro-Discharge Machine (EDM) using powder metallurgy technique. Al2O3 particles with different weight percentages (0, 1%, 3% and 5%) were reinforced into copper matrix using powder metallurgy technique. The powders were blended and compacted at a load of 100MPa to produce green compacts and sintered at a temperature of 574 °C. The effect of aluminium oxide content on mass density, Rockwell hardness and wear behaviour were investigated. Wear behaviour of the composites was investigated on Die-Sink EDM (Electro-Discharge Machine). It was found that wear rate is highly depending on hardness, mass density and green protective carbonate layer formation at the surface of the composite.

Formation and magnetic properties of the L10 phase in bulk, powder and hot compacted Mn-Ga alloys

NASA Astrophysics Data System (ADS)

Mix, T.; Müller, K.-H.; Schultz, L.; Woodcock, T. G.

2015-10-01

The formation and stability of the L10 phase in Mn-Ga binary alloys with compositions in the range 50-75 at% Mn (in steps of 5 at%) has been studied. Of these, single-phase L10 structure was successfully produced in the 55, 60 and 65 at% Mn alloys by annealing the high temperature phases, which had been retained to room temperature following arc melting. Further annealing and thermal analysis were used to determine the phase transformation temperatures in the alloys and the results were used to guide further processing. The saturation magnetisation, Ms, and the anisotropy field, Ha, were determined in applied fields up to 14 T. For Mn55Ga45, μ0Ms=0.807 T and μ0Ha=4.4 T were observed. Mechanically milled Mn55Ga45 powder had coercivity of μ0Hc=0.393 T, which was a twentyfold increase compared to the bulk material but the magnetisation was reduced (cf. powder: μ0M5 T=0.576 T, bulk: μ0M5 T=0.780 T). Annealing the powder at 400 °C led to recovery of the magnetisation but reduced the coercivity, which was still 10 times as high as the bulk value. A degree of texture of 0.45 was achieved by magnetic alignment of the powder particles, leading to a remanence of 0.526 T. Furthermore, isotropic hot compacts of powders were produced with packing density from 83% to 99%, in which the improved coercivity of the powders was partially retained.

Fractionation study in bioleached metallurgy wastes using six-step sequential extraction.

PubMed

Krasnodebska-Ostrega, Beata; Pałdyna, Joanna; Kowalska, Joanna; Jedynak, Łukasz; Golimowski, Jerzy

2009-08-15

The stored metallurgy wastes contain residues from ore processing operations that are characterized by relatively high concentrations of heavy metals. The bioleaching process makes use of bacteria to recover elements from industrial wastes and to decrease potential risk of environmental contamination. Wastes were treated by solutions containing bacteria. In this work, the optimized six-stage sequential extraction procedure was applied for the fractionation of Ni, Cr, Fe, Mn, Cu and Zn in iron-nickel metallurgy wastes deposited in Southern Poland (Szklary). Fractionation and total concentrations of elements in wastes before and after various bioleaching treatments were studied. Analyses of the extracts were performed by ICP-MS and FAAS. To achieve the most effective bioleaching of Zn, Cr, Ni, Cu, Mn, Fe the usage of both autotrophic and heterotrophic bacteria in sequence, combined with flushing of the residue after bioleaching is required. 80-100% of total metal concentrations were mobilized after the proposed treatment. Wastes treated according to this procedure could be deposited without any risk of environmental contamination and additionally the metals could be recovered for industrial purposes.

Powder treatment process

DOEpatents

Weyand, J.D.

1988-02-09

Disclosed are: (1) a process comprising spray drying a powder-containing slurry, the slurry containing a powder constituent susceptible of oxidizing under the temperature conditions of the spray drying, while reducing the tendency for oxidation of the constituent by including as a liquid constituent of the slurry an organic liquid; (2) a process comprising spray drying a powder-containing slurry, the powder having been pretreated to reduce content of a powder constituent susceptible of oxidizing under the temperature conditions of the spray drying, the pretreating comprising heating the powder to react the constituent; and (3) a process comprising reacting ceramic powder, grinding the reacted powder, slurrying the ground powder, spray drying the slurried powder, and blending the dried powder with metal powder. 2 figs.

Powder treatment process

DOEpatents

Weyand, John D.

1988-01-01

(1) A process comprising spray drying a powder-containing slurry, the slurry containing a powder constituent susceptible of oxidizing under the temperature conditions of the spray drying, while reducing the tendency for oxidation of the constituent by including as a liquid constituent of the slurry an organic liquid; (2) a process comprising spray drying a powder-containing slurry, the powder having been pretreated to reduce content of a powder constituent susceptible of oxidizing under the temperature conditions of the spray drying, the pretreating comprising heating the powder to react the constituent; and (3) a process comprising reacting ceramic powder, grinding the reacted powder, slurrying the ground powder, spray drying the slurried powder, and blending the dried powder with metal powder.

Thermogravimetric Control of Intermediate Products in the Metallurgy of Uranium; CONTROL TERMOGRAVIMETRICO DE PRODUCTOS INTERMEDIOS DE LA METALURGIA DEL URANIO

DOE Office of Scientific and Technical Information (OSTI.GOV)

Sanchez, L.G.; Cellini, R.F.

1959-01-01

The thermal decomposition of some intermediate compounds in the metallurgy of uranium such as uranium peroxide, ammonium uranate, ammonium uranium pentafluoride, uranium tetrafluoride, and UO/sub 2/, were studied using Chevenard's thermobalance. Some data on the pyrolysis of synthetic mixtures of intermediate compounds which may appear during the industrial processing are given. Thermogravimetric methods of control are suggested for use in uranium metallurgy. (tr-auth)

Producing High-Quality Titanium Alloy by a Cost-Effective Route Combining Fast Heating and Hot Processing

NASA Astrophysics Data System (ADS)

Yang, Fei; Raynova, Stella; Singh, Ajit; Zhao, Qinyang; Romero, Carlos; Bolzoni, Leandro

2018-02-01

Powder metallurgy is a very attractive method for producing titanium alloys, which can be near-net-shape formed and have freedom in composition selection. However, applications are still limited due to product affordability. In this paper, we will discuss a possible cost-effective route, combining fast heating and hot processing, to produce titanium alloys with similar or even better mechanical properties than that of ingot metallurgy titanium alloys. Two titanium alloys, Ti-5Al-5V-5Mo-3Cr (Ti-5553) and Ti-5Fe, were successfully produced from HDH titanium powder and other master alloy powders using the proposed processing route. The effect of the processing route on microstructural variation and mechanical properties have been discussed.

Solvent Extraction of Copper: An Extractive Metallurgy Exercise for Undergraduate Teaching Laboratories

ERIC Educational Resources Information Center

Smellie, Iain A.; Forgan, Ross S.; Brodie, Claire; Gavine, Jack S.; Harris, Leanne; Houston, Daniel; Hoyland, Andrew D.; McCaughan, Rory P.; Miller, Andrew J.; Wilson, Liam; Woodhall, Fiona M.

2016-01-01

A multidisciplinary experiment for advanced undergraduate students has been developed in the context of extractive metallurgy. The experiment serves as a model of an important modern industrial process that combines aspects of organic/inorganic synthesis and analysis. Students are tasked to prepare a salicylaldoxime ligand and samples of the…

The reduction of optimal heat treatment temperature and critical current density enhancement of ex situ processed MgB2 tapes using ball milled filling powder

NASA Astrophysics Data System (ADS)

Fujii, Hiroki; Iwanade, Akio; Kawada, Satoshi; Kitaguchi, Hitoshi

2018-01-01

The optimal heat treatment temperature (Topt) at which best performance in the critical current density (Jc) property at 4.2 K is obtained is influenced by the quality or reactivity of the filling powder in ex situ processed MgB2 tapes. Using a controlled fabrication process, the Topt decreases to 705-735 °C, which is lower than previously reported by more than 50 °C. The Topt decrease is effective to suppress both the decomposition of MgB2 and hence the formation of impurities such as MgB4, and the growth of crystallite size which decreases upper critical filed (Hc2). These bring about the Jc improvement and the Jc value at 4.2 K and 10 T reaches 250 A/mm2. The milling process also decreases the critical temperature (Tc) below 30 K. The milled powder is easily contaminated in air and thus, the Jc property of the contaminated tapes degrades severely. The contamination can raise the Topt by more than 50 °C, which is probably due to the increased sintering temperature required against contaminated surface layer around the grains acting as a barrier.

Stress corrosion evaluation of powder metallurgy aluminum alloy 7091 with the breaking load test method

NASA Technical Reports Server (NTRS)

Domack, Marcia S.

1987-01-01

The stress corrosion behavior of the P/M aluminum alloy 7091 is evaluated in two overaged heat treatment conditions, T7E69 and T7E70, using an accelerated test technique known as the breaking load test method. The breaking load data obtained in this study indicate that P/M 7091 alloy is highly resistant to stress corrosion in both longitudinal and transverse orientations at stress levels up to 90 percent of the material yield strength. The reduction in mean breaking stress as a result of corrosive attack is smallest for the more overaged T7E70 condition. Details of the test procedure are included.

Performance Characteristics of Waste Glass Powder Substituting Portland Cement in Mortar Mixtures

NASA Astrophysics Data System (ADS)

Kara, P.; Csetényi, L. J.; Borosnyói, A.

2016-04-01

In the present work, soda-lime glass cullet (flint, amber, green) and special glass cullet (soda-alkaline earth-silicate glass coming from low pressure mercury-discharge lamp cullet and incandescent light bulb borosilicate glass waste cullet) were ground into fine powders in a laboratory planetary ball mill for 30 minutes. CEM I 42.5N Portland cement was applied in mortar mixtures, substituted with waste glass powder at levels of 20% and 30%. Characterisation and testing of waste glass powders included fineness by laser diffraction particle size analysis, specific surface area by nitrogen adsorption technique, particle density by pycnometry and chemical analysis by X-ray fluorescence spectrophotometry. Compressive strength, early age shrinkage cracking and drying shrinkage tests, heat of hydration of mortars, temperature of hydration, X-ray diffraction analysis and volume stability tests were performed to observe the influence of waste glass powder substitution for Portland cement on physical and engineering properties of mortar mixtures.

The beginning of metallurgy in the southern Levant: a late 6th millennium CalBC copper awl from Tel Tsaf, Israel.

PubMed

Garfinkel, Yosef; Klimscha, Florian; Shalev, Sariel; Rosenberg, Danny

2014-01-01

The beginning of metallurgy in the ancient Near East attracts much attention. The southern Levant, with the rich assemblage of copper artifacts from the Nahal Mishmar cave and the unique gold rings of the Nahal Qanah cave, is regarded as a main center of early metallurgy during the second half of the 5th millennium CalBC. However, a recently discovered copper awl from a Middle Chalcolithic burial at Tel Tsaf, Jordan Valley, Israel, suggests that cast metal technology was introduced to the region as early as the late 6th millennium CalBC. This paper examines the chemical composition of this item and reviews its context. The results indicate that it was exported from a distant source, probably in the Caucasus, and that the location where it was found is indicative of the social status of the buried individual. This rare finding indicates that metallurgy was first diffused [corrected] to the southern Levant through exchange networks and only centuries later involved local productionThis copper awl, the earliest metal artifact found in the southern Levant, indicates that the elaborate Late Chalcolithic metallurgy developed from a more ancient tradition.

The Beginning of Metallurgy in the Southern Levant: A Late 6th Millennium CalBC Copper Awl from Tel Tsaf, Israel

PubMed Central

Garfinkel, Yosef; Klimscha, Florian; Shalev, Sariel; Rosenberg, Danny

2014-01-01

The beginning of metallurgy in the ancient Near East attracts much attention. The southern Levant, with the rich assemblage of copper artifacts from the Nahal Mishmar cave and the unique gold rings of the Nahal Qanah cave, is regarded as a main center of early metallurgy during the second half of the 5th millennium CalBC. However, a recently discovered copper awl from a Middle Chalcolithic burial at Tel Tsaf, Jordan Valley, Israel, suggests that cast metal technology was introduced to the region as early as the late 6th millennium CalBC. This paper examines the chemical composition of this item and reviews its context. The results indicate that it was exported from a distant source, probably in the Caucasus, and that the location where it was found is indicative of the social status of the buried individual. This rare finding indicates that metallurgy was first defused to the southern Levant through exchange networks and only centuries later involved local production. This copper awl, the earliest metal artifact found in the southern Levant, indicates that the elaborate Late Chalcolithic metallurgy developed from a more ancient tradition. PMID:24671185

Effects of chromium addition on the metallurgy and P/M processing response of Alumix 431D

NASA Astrophysics Data System (ADS)

Mosher, Michael Patrick

The ever growing industry of Powder Metallurgy (P/M) is developing to include new alloys and improve those currently available. This project relates to the optimization of a commercially available Al-Zn-Mg-Cu based alloy (Alumix 431D). This alloy is the P/M equivalent of the wrought 7075 alloy, and yields some of the top performance found in any available aluminum alloy. Optimization of the alloy has been conducted with a focus on sintering conditions; in particular the effect of sintering temperature and post-sintering cooling. Five sintering temperatures were investigated and the optimal temperature was found to be 605°C. Cr was added in trace amounts as per literature recommendations in an attempt to improve corrosion resistance. Both the Cr-free and Cr-containing alloys were then assessed for post-sinter cooling effects. The Alumix 431D w/Cr compacted and sintered to a higher density which further resulted in improved hardness over the Cr-free counterpart. The cooling profile was modified to include an increasingly larger post-sinter furnace-cooling section, before gas quenching. Seven quenching temperatures were chosen to investigate ranging from the sintering temperature (605°C) down to 480°C. This furnace cooling allowed the alloy-rich liquid phase to dwell for an extended time at elevated temperature and thereby diffuse into the matrix grains increasing the alloy content. This was confirmed through EPMA and correlated with an increase in mechanical properties. For both alloys peak hardness was produced by specimens cooled to 520°C before quenching. Tensile strength also increased by as much as 12% when furnace cooled to 540°C. The heat treatment parameters were determined to yield an optimal T6 temper. Specimens of both alloys processed under all conditions were then subjected to this heat treatment and further characterized. Many of the improvements offered by furnace cooling that were obvious in the T1 'as-sintered' product, became less pronounced

Polymer powders for selective laser sintering (SLS)

NASA Astrophysics Data System (ADS)

Schmid, Manfred; Amado, Antonio; Wegener, Konrad

2015-05-01

Selective Laser Sintering (SLS) is close to be accepted as a production technique (Additive Manufacturing). However, one problem limiting employment of SLS for additive manufacturing in a wide-ranging industrial scope is the narrow variety of applicable polymers. The commonly applied SLS powder to date is polyamide 12 (PA 12). PA 12 or ccompounds of PA 12 (dry blends) are approximately 90 % of complete industrial consumption. The remaining small quantity is distributed on polyamide 11 (PA11) and some other `exotic' polymers (TPU, PEBA, P(E)EK). Industry is awaiting commodity polymers like polypropylene (PP) or polyethylene (PE) crucial to open new market segments. But several approaches launching those polymers failed. But what are the reasons for the difficulties in developing new SLS powders? The contribution is to answer this and highlights the combination of intrinsic and extrinsic polymer properties necessary to generate a polymer powder promising for SLS application. Particle shape, powder distribution, thermal, rheological and optical requirements must be considered and only a particularly controlled property combination leads to successful SLS implementation. Thermal behavior, particle shape and -distribution is discussed in detail, although the other properties can't be disregarded for providing new commercially successful SLS powder finally.

[Powder-induced anaphylactic shock following use of powdered latex gloves during gynecological open laparotomy].

PubMed

Mizuno, Ju; In-nami, Hiroshi; Saegusa, Hiroaki; Kibayashi, Junichiro; Jimbo, Masanori; Kida, Kotaro; Ichiishi, Noriko

2006-06-01

A 42-year-old woman with hysteromyoma underwent total abdominal hysterectomy under general and epidural anesthesia. Three years before, she had undergone resection of lipoma on her left shoulder under local anesthesia uneventfully. She had no previous history of hypersensitivity. General anesthesia was induced by intravenous injection of fentanyl, propofol, and vecuronium followed by inhalation of nitrous oxide, oxygen, and sevoflurane. Lidocaine and fentanyl were injected through a lumbar epidural catheter. After the start of open laparotomy, there was a sudden onset of hypotension. Administrations of ephedrine and phenylephrine, and volume loading were ineffective. Moreover, she showed profound hypotension, tachycardia, oxygen desaturation, decreased endtidal carbon dioxide and increased airway pressure. She broke out in a sweat with flushing on her chest and upper extremities. Therefore, we interrupted the surgery, checked her arterial blood gas analysis, performed echocardiography, and inserted a pulmonary artery catheter. We made a diagnosis of anaphylactic shock and administered methylprednisolone, albumin, epinephrine, norepinephrine, and dopamine to treat the circulatory collapse. The gynecologists changed their surgical gloves from a powdered-latex type to a powder-free latex type, and the surgery was resumed. She responded well to appropriate emergent therapy and all vasopressor drugs were gradually decreased and eventually stopped. After the end of the surgery, she recovered completely from the signs and symptoms of shock. Later, we found a high level of plasma latex protein-specific IgE antibody and confirmed the events as anaphylactic shock due to latex. We assumed that the anaphylactic shock was powder-induced latex allergy following use of powdered latex gloves in this case. Latex allergy should be suspected if an anaphylactic reaction or shock accompanied by circulatory collapse, respiratory failure, and skin symptoms of unknown origin occurs during

Emission profiles of polychlorinated dibenzodioxins, polychlorinated dibenzofurans (PCDD/Fs), dioxin-like PCBs and hexachlorobenzene (HCB) from secondary metallurgy industries in Portugal.

PubMed

Antunes, Pedro; Viana, Paula; Vinhas, Tereza; Rivera, J; Gaspar, Elvira M S M

2012-09-01

This paper reports, for the first time, a study of dioxin emissions from 10 siderurgies and metallurgies, secondary copper, aluminum and lead metallurgies, in Portugal. The study reports the emission factors and total emission amounts of PCDD/Fs, dioxin-like PCBs and hexachlorobenzene (HCB). The congener patterns were characterized and are discussed. The results showed that the total amount of PCDFs is higher than PCDDs in flue gas of each industrial unit. The toxic equivalent emission factors of pollutants emitted are 3098-3338 ngI-TEQt(-1) for PCDD/Fs and 597-659 ng I-TEQt(-1) for dioxin-like PCBs in siderurgies production (total estimated emission amounts released to atmosphere of 3.9-4.5 g I-TEQyr(-1)), 50-152 ng I-TEQt(-1) for PCDD/Fs and 24-121 ng I-TEQt(-1) for dioxin-like PCBs in ferrous foundries production (total estimated emission amounts released to atmosphere of 0.0010-0.0016 g I-TEQyr(-1)) and 5.8-5715 ng I-TEQt(-1) for PCDD/Fs and 0.49-259 ng I-TEQt(-1) for dioxin-like PCBs in non-ferrous foundries production (total estimated emission amounts released to atmosphere of 0.00014-0.12 g I-TEQyr(-1)). The HCB emission from siderurgies production is 0.94-3.2 mg t(-1) (total estimated emission amounts released 0.94-3.8 g yr(-1)), being much smaller, residual, in the emissions of the other types of plants (0.0012-0.026 mg t(-1) production and total estimated emission amounts released to atmosphere of 0.013-1.7 mg yr(-1)). Copyright © 2012 Elsevier Ltd. All rights reserved.

The in vivo Therapeutic Effect of Free Wanderer Powder (逍 遙 散 xiāo yáo sǎn, Xiaoyaosan) on Mice with 4T1 Cell Induced Breast Cancer Model

PubMed Central

Chen, Wen-Fang; Xu, Li; Yu, Chung-Him; Ho, Chui-Kwan; Wu, Ka; Leung, Gina CW; Wong, Man-Sau

2012-01-01

In the present study, we investigated the therapeutic effect of a classical TCM formula, Free Wanderer Powder (逍遙散 xiāo yáo sǎn), in a breast cancer mouse model induced with estrogen-insensitive breast cancer 4T1 cells. Ovariectomized Balb/c mice (6-8 weeks) or sham mice were injected into the fourth mammary fat pad with 4T1 cells in which tumors were palpable 7 days after injection. On the eighth day, the mice were divided into 4 groups and tubefed daily with vehicle, Free Wanderer Powder (逍遙散 xiāo yáo sǎn) formula or tamoxifen for 28 days. Tumor growth inhibition and the decrease of the average tumor mass were most evident in mice treated with Free Wanderer Powder (逍遙散 xiāo yáo sǎn). Free Wanderer Powder (逍遙散 xiāo yáo sǎn) treatment significantly reduced Bcl-2 and elevated Bax and p53 protein expressions in breast cancer tumor. These results were further confirmed by immunohistochemisty. Tamoxifen could decrease spleen mass and Bcl-2 protein expression, increase the Bax protein expression as well as exert uterotrophic effects by increasing uterus index and inducing the gene expressions in the uterus. Taken together, these results show that Free Wanderer Powder (逍遙散 xiāo yáo sǎn) treatment induced apoptosis at protein level and inhibited the tumor growth in 4T1-induced ovariectomized Balb/c female mice, indicating the possibility of its future use for treatment of estrogen-insensitive breast caner. PMID:24716117

Equal channel angular pressing of powder processed Al6061/SiC nano metal matrix composites and study of its wear properties

NASA Astrophysics Data System (ADS)

Bongale, Arunkumar M.; Kumar, Satish

2018-03-01

Nano Metal Matrix Composites were fabricated by a novel approach by combining powder metallurgy and equal channel angular pressing (ECAP) using aluminium alloy 6061 (Al6061) as matrix phase and 2, 4 and 6 wt% of silicon carbide nanoparticles (SiCnp) as reinforcements. Alloying elements of Al6061 in their elemental form are blended together using high energy planetary ball mill and calculated wt% of SiCnp were mixed with it. Thus formed composite powder mixture is compacted in a uniaxial compaction die and then subjected to ECAP up to three passes. Density and porosity of samples were estimated using Archimedes’ principle. Pin on disc setup is used to evaluate the wear properties of the composites under different speed and loading conditions. Tests revealed that increase in wt% of SiCnp reduces the wear rate of the composites whereas increasing the load and speed increases wear rate of the composite samples. SEM micrographs of worn surfaces indicated different types of wear mechanism responsible for wear of the specimens under different testing conditions. Also, wt% of SiCnp and the number of passes through ECAP were found to increase the hardness value of the composite material.

The Application of Globular Water-Atomized Iron Powders for Additive Manufacturing by a LENS Technique.

PubMed

Durejko, Tomasz; Aniszewska, Justyna; Ziętala, Michał; Antolak-Dudka, Anna; Czujko, Tomasz; Varin, Robert A; Paserin, Vlad

2018-05-18

The water-atomized ATOMET 28, 1001, 4701, and 4801 powders, manufactured by Rio Tinto Metal Powders, were used for additive manufacturing by a laser engineered net shaping (LENS) technique. Their overall morphology was globular and rounded with a size distribution from about 20 to 200 µm. Only the ATOMET 28 powder was characterized by a strong inhomogeneity of particle size and irregular polyhedral shape of powder particles with sharp edges. The powders were pre-sieved to a size distribution from 40 to 150 µm before LENS processing. One particular sample-LENS-fabricated from the ATOMET 28 powder-was characterized by the largest cross-sectional (2D) porosity of 4.2% and bulk porosity of 3.9%, the latter determined by microtomography measurements. In contrast, the cross-sectional porosities of bulk, solid, nearly cubic LENS-fabricated samples from the other ATOMET powders exhibited very low porosities within the range 0.03⁻0.1%. Unexpectedly, the solid sample-LENS-fabricated from the reference, a purely spherical Fe 99.8 powder-exhibited a porosity of 1.1%, the second largest after that of the pre-sieved, nonspherical ATOMET 28 powder. Vibrations incorporated mechanically into the LENS powder feeding system substantially improved the flow rate vs. feeding rate dependence, making it completely linear with an excellent coefficient of fit, R² = 0.99. In comparison, the reference powder Fe 99.8 always exhibited a linear dependence of the powder flow rate vs. feeding rate, regardless of vibrations.

Development of structural diagram of automated dispatch control system for power consumption at non-ferrous metallurgy enterprises

NASA Astrophysics Data System (ADS)

Klyuev, R. V.; Bosikov, I. I.; Madaeva, M. Z.; A-V Turluev, R.

2018-03-01

The structural scheme of the automated control system of power consumption at the industrial enterprise is developed in the article. At the non-ferrous metallurgy enterprise, an energy inspection and a rank analysis of the electrical energy consumption of the main processing equipment were carried out. It is established that the enterprises of non-ferrous metallurgy are a complex process system consisting of a set of thousands of jointly functioning technological facilities. For the most effective estimation of power consumption of enterprises, it is reasonable to use the automated system of dispatching control of power consumption (ASDCPC). The paper presents the results of the development of the ASDCPC structural diagram that allows one to perform on-line control and management of the energy and process parameters of the main production units and the enterprise as a whole. As a result of the introduction of ASDCPC at the non-ferrous metallurgy enterprise, the consumed active power was reduced during the peak hours of the load by 20%, the specific electricity consumption - by 14%, the cost of the energy component in the cost of production of hard alloys - by 3%.

Ir-based refractory superalloys by pulse electric current sintering (PECS) process (II prealloyed powder)

NASA Astrophysics Data System (ADS)

Huang, C.; Yamabe-Mitarai, Y.; Harada, H.

2002-02-01

Five prealloyed powder samples prepared from binary Ir-based refractory superalloys were sintered at 1800 °C for 4 h by Pulse Electric Current Sintering (PECS). No metal loss was observed during sintering. The relative densities of the sintered specimens all exceeded 90% T.D. The best one was Ir-13% Hf with the density of 97.82% T.D. Phases detected in sintered samples were in accordance with the phase diagram as expected. Fractured surfaces were observed in two samples (Ir-13% Hf and Ir-15% Zr). Some improvements obtained by using prealloyed powders instead of elemental powders, which were investigated in the previous studies, were presented.

Synthesis, structural and vibrational studies on mixed alkali metal gadolinium double tungstate, K1-xNaxGd(WO4)2

NASA Astrophysics Data System (ADS)

Durairajan, A.; Thangaraju, D.; Moorthy Babu, S.

2013-02-01

Mixed alkali double tungstates K1-xNaxGd(WO4)2 (KNGW) (0 ⩽ x ⩽ 1) were synthesized by solid state reaction using sodium doped monoclinic KGd(WO4)2 (KGW). Synthesized KNGW powders were characterized using powder X-ray diffraction (XRD), differential thermal analysis (DTA), scanning electron microscopy (SEM) and Raman analysis. DTA analysis confirms that the melting point of the KGW matrix increases from 1063 °C to 1255 °C with increasing sodium content. The Powder XRD analyses reveal that mixed phases were observed up to 40 wt.% of Na in the KGW matrix above that percentage there is domination of scheelite structure in the synthesized powder. Polyhedral type, bi-pyramidal shape and spheroid shape morphology was observed for KGW, NKGW and NGW powders respectively. The Raman analysis was carried out to understand the vibrational characteristic changes with mixing of sodium ions in the KGW matrix.

Transmission electron microscopy characterization of microstructural features of Al-Li-Cu alloys

NASA Technical Reports Server (NTRS)

Avalos-Borja, M.; Pizzo, P. P.; Larson, L. A.

1983-01-01

A transmission electron microscopy (TEM) examination of aluminum-lithium-copper alloys was conducted. The principal purpose is to characterize the nature, size, and distribution of stringer particles which result from the powder metallurgy (P/M) processing of these alloys. Microstructural features associated with the stringer particles are reported that help explain the stress corrosion susceptibility of the powder metallurgy-processed Al-Li-Cu alloys. In addition, matrix precipitation events are documented for a variety of heat treatments and process variations. Hot rolling is observed to significant alter the nature of matrix precipitation, and the observations are correlated with concomitant mechanical property variations.

Transmission electron microscopy characterization of microstructural features in aluminum-lithium-copper alloys

NASA Technical Reports Server (NTRS)

Avalos-Borja, M.; Larson, L. A.; Pizzo, P. P.

1984-01-01

A transmission electron microscopy (TEM) examination of aluminum-lithium-copper alloys was conducted. The principal purpose is to characterize the nature, size, and distribution of stringer particles which result from the powder metallurgy (P/M) processing of these alloys. Microstructural features associated with the stringer particles are reported that help explain the stress corrosion susceptibility of the powder metallurgy-processed Al-Li-Cu alloys. In addition, matrix precipitaton events are documented for a variety of heat treatments and process variations. Hot rolling is observed to significantly alter the nature of matrix precipitation, and the observations are correlated with concomitant mechanical property variations.

Preparation of TiO₂ nanocrystallite powders coated with 9 mol% ZnO for cosmetic applications in sunscreens.

PubMed

Ko, Horng-Huey; Chen, Hui-Ting; Yen, Feng-Ling; Lu, Wan-Chen; Kuo, Chih-Wei; Wang, Moo-Chin

2012-01-01

The preparation of TiO(2) nanocrystallite powders coated with and without 9 mol% ZnO has been studied for cosmetic applications in sunscreens by a co-precipitation process using TiCl(4) and Zn(NO(3))(2)·6H(2)O as starting materials. XRD results show that the phases of anatase TiO(2) and rutile TiO(2) coexist for precursor powders without added ZnO (T-0Z) and calcined at 523 to 973 K for 2 h. When the T-0Z precursor powders are calcined at 1273 K for 2 h, only the rutile TiO(2) appears. In addition, when the TiO(2) precursor powders contain 9 mol% ZnO (T-9Z) are calcined at 873 to 973 K for 2 h, the crystallized samples are composed of the major phase of rutile TiO(2) and the minor phases of anatase TiO(2) and Zn(2)Ti(3)O(8). The analyses of UV/VIS/NIR spectra reveal that the absorption of the T-9Z precursor powders after being calcined has a red-shift effect in the UV range with increasing calcination temperature. Therefore, the TiO(2) nanocrystallite powders coated with 9 mol% ZnO can be used as the attenuate agent in the UV-A region for cosmetic applications in sunscreens.

Effects of hydrolysis on solid-state relaxation and stickiness behavior of sodium caseinate-lactose powders.

PubMed

Mounsey, J S; Hogan, S A; Murray, B A; O'Callaghan, D J

2012-05-01

Hydrolyzed or nonhydrolyzed sodium caseinate-lactose dispersions were spray dried, at a protein: lactose ratio of 0.5, to examine the effects of protein hydrolysis on relaxation behavior and stickiness of model powders. Sodium caseinate (NC) used included a nonhydrolyzed control (DH 0) and 2 hydrolyzed variants (DH 8.3 and DH 15), where DH = degree of hydrolysis (%). Prior to spray drying, apparent viscosities of liquid feeds (at 70°C) at a shear rate of 20/s were 37.6, 3.14, and 3.19 mPa·s, respectively, for DH 0, DH 8, and DH 15 dispersions. Powders containing hydrolyzed casein were more susceptible to sticking than those containing intact NC. The former had also lower bulk densities and powder particle sizes. Scanning electron microscopy showed that hydrolyzed powders had thinner particle walls and were more friable than powders containing intact NC. Secondary structure of caseinates, determined by Fourier transform infrared spectroscopy, was affected by the relative humidity of storage and the presence of lactose as co-solvent rather than its physical state. Glass transition temperatures and lactose crystallization temperatures, determined by differential scanning calorimetry were not affected by caseinate hydrolysis, although the effects of protein hydrolysis on glass-rubber transitions (T(gr)) could be determined by thermo-mechanical analysis. Powders containing hydrolyzed NC had lower T(gr) values (~30°C) following storage at a higher subcrystallization relative humidity (33%) compared with powder with nonhydrolyzed NC (T(gr) value of ~40°C), an effect that reflects more extensive plasticization of powder matrices by moisture. Results support that sodium caseinate-lactose interactions were weak but that relaxation behavior, as determined by the susceptibility of powder to sticking, was affected by hydrolysis of sodium caseinate. Copyright © 2012 American Dairy Science Association. Published by Elsevier Inc. All rights reserved.

Vacuum powder injector and method of impregnating fiber with powder

NASA Astrophysics Data System (ADS)

Working, Dennis C.

1993-05-01

A method and apparatus uniformly impregnate stranded material with dry powder such as low solubility, high melt flow polymer powder to produce, for example, composite prepregs. The stranded material is expanded in an impregnation chamber by an influx of air so that the powder, which may enter through the same inlet as the air, penetrates to the center of the stranded material. The stranded material then is contracted for holding the powder therein. The stranded material and powder may be pulled through the impregnation chamber in the same direction by vacuum. Larger particles of powder which do not fully penetrate the stranded material may be combed into the stranded material and powder which does not impregnate the stranded material may be collected and reused.

Vacuum powder injector and method of impregnating fiber with powder

NASA Technical Reports Server (NTRS)

Working, Dennis C. (Inventor)

1993-01-01

A method and apparatus uniformly impregnate stranded material with dry powder such as low solubility, high melt flow polymer powder to produce, for example, composite prepregs. The stranded material is expanded in an impregnation chamber by an influx of air so that the powder, which may enter through the same inlet as the air, penetrates to the center of the stranded material. The stranded material then is contracted for holding the powder therein. The stranded material and powder may be pulled through the impregnation chamber in the same direction by vacuum. Larger particles of powder which do not fully penetrate the stranded material may be combed into the stranded material and powder which does not impregnate the stranded material may be collected and reused.

Effects of Initial Powder Size on the Mechanical Properties and Microstructure of As-Extruded GRCop-84

NASA Technical Reports Server (NTRS)

Okoro, Chika L.

2004-01-01

GRCop-84 was developed to meet the mechanical and thermal property requirements for advanced regeneratively cooled rocket engine main combustion chamber liners. It is a ternary Cu- Cr-Nb alloy having approximately 8 at% Cr and 4 at% Nb. The chromium and niobium constituents combine to form 14 vol% Cr2Nb, the strengthening phase. The alloy is made by producing GRCop-84 powder through gas atomization and consolidating the powder using extrusion, hot isostatic pressing (HIP) or vacuum plasma spraying (VPS). GRCop-84 has been selected by Rocketdyne, Ratt & Wlutney and Aerojet for use in their next generation of rocket engines. GRCop-84 demonstrates favorable mechanical and thermal properties at elevated temperatures. Compared to NARloy-Z, the currently used inaterial in the Space Shuttle, GRCop-84 has approximately twice the yield strength, 10-1000 times the creep life, and 1.5-2.5 times the low cycle fatigue life. The thermal expansion of GRCop-84 is 7515% less than NARloy-Z which minimizes thermally induced stresses. The thermal conductivity of the two alloys is comparable at low temperature but NARloy-Z has a 20-50 W/mK thermal conductivity advantage at typical rocket engine hot wall temperatures. GRCop-84 is also much more microstructurally stable than NARloy-Z which translates into better long term stability of mechanical properties. Previous research into metal alloys fabricated by means of powder metallurgy (PM), has demonstrated that initial powder size can affect the microstructural development and mechanical properties of such materials. Grain size, strength, ductility, size of second phases, etc., have all been shown to vary with starting powder size in PM-alloys. This work focuses on characterizing the effect of varying starting powder size on the microstructural evolution and mechanical properties of as- extruded GRCop-84. Tensile tests and constant load creep tests were performed on extrusions of four powder meshes: +140 mesh (great3er than l05 micron

Influence of Metal-Coated Graphite Powders on Microstructure and Properties of the Bronze-Matrix/Graphite Composites

NASA Astrophysics Data System (ADS)

Zhao, Jian-hua; Li, Pu; Tang, Qi; Zhang, Yan-qing; He, Jian-sheng; He, Ke

2017-02-01

In this study, the bronze-matrix/x-graphite (x = 0, 1, 3 and 5%) composites were fabricated by powder metallurgy route by using Cu-coated graphite, Ni-coated graphite and pure graphite, respectively. The microstructure, mechanical properties and corrosive behaviors of bronze/Cu-coated-graphite (BCG), bronze/Ni-coated-graphite (BNG) and bronze/pure-graphite (BPG) were characterized and investigated. Results show that the Cu-coated and Ni-coated graphite could definitely increase the bonding quality between the bronze matrix and graphite. In general, with the increase in graphite content in bronze-matrix/graphite composites, the friction coefficients, ultimate density and wear rates of BPG, BCG and BNG composites all went down. However, the Vickers microhardness of the BNG composite would increase as the graphite content increased, which was contrary to the BPG and BCG composites. When the graphite content was 3%, the friction coefficient of BNG composite was more stable than that of BCG and BPG composites, indicating that BNG composite had a better tribological performance than the others. Under all the values of applied loads (10, 20, 40 and 60N), the BCG and BNG composites exhibited a lower wear rate than BPG composite. What is more, the existence of nickel in graphite powders could effectively improve the corrosion resistance of the BNG composite.

Phosphorus as sintering activator in powder metallurgical steels: characterization of the distribution and its technological impact.

PubMed

Krecar, Dragan; Vassileva, Vassilka; Danninger, Herbert; Hutter, Herbert

2004-06-01

Powder metallurgy is a highly developed method of manufacturing reliable ferrous parts. The main processing steps in a powder metallurgical line are pressing and sintering. Sintering can be strongly enhanced by the formation of a liquid phase during the sintering process when using phosphorus as sintering activator. In this work the distribution (effect) of phosphorus was investigated by means of secondary ion mass spectrometry (SIMS) supported by Auger electron spectroscopy (AES) and electron probe micro analysis (EPMA). To verify the influence of the process conditions (phosphorus content, sintering atmosphere, time) on the mechanical properties, additional measurements of the microstructure (pore shape) and of impact energy were performed. Analysis of fracture surfaces was performed by means of scanning electron microscopy (SEM). The concentration of phosphorus differs in the samples from 0 to 1% (w/ w). Samples with higher phosphorus concentrations (1% (w/ w) and above) are also measurable by EPMA, whereas the distributions of P at technically relevant concentrations and the distribution of possible impurities are only detectable (visible) by means of SIMS. The influence of the sintering time on the phosphorus distribution will be demonstrated. In addition the grain boundary segregation of P was measured by AES at the surface of in-situ broken samples. It will be shown that the distribution of phosphorus depends also on the concentration of carbon in the samples.

Investigation of the Dependences of the Attenuation Properties of Cryogenic Metal-Powder Filters on the Preparation Method

NASA Astrophysics Data System (ADS)

Lee, Sung Hoon; Lee, Soon-Gul

2018-04-01

We fabricated low-pass metal powder filters for use in low-noise measurements at cryogenic temperatures and investigated their attenuation characteristics for different wire-turn densities, metalpowder shapes, and preparation methods at frequencies up to 20 GHz. We used nominally 30-μmsized stainless-steel 304L powder and mixed it with low-temperature binders. The low-temperature binders used were Stycast 2850FT (Emerson and Cumming) with catalyst 23LV and GE-7031 varnish. A 0.1-mm insulated copper wire was wound on preformed powder-mixture bobbins in the shape of a circular rod and was encapsulated in metal tubes with the powder mixture. All the fabricated powder filters showed a large attenuation at high frequencies with a cut-off frequency near 1 GHz. For filters of the same wire length, a lower wiring density showed a larger attenuation, which implies that the amount of powder in close contact with the wire determines the attenuation. Filters made of a powder/varnish mixture showed significantly larger attenuations than those of a powder/stycast mixture, and the attenuation improved with increasing powder ratio in the mixture. The low-temperature thermal conductivities of a 2 : 1 powder/Stycast mixture and a 5 : 1 powder/varnish mixture showed similar values at temperatures up to 4.2 K.

The Effect of Milling Time on the Microstructural Characteristics and Strengthening Mechanisms of NiMo-SiC Alloys Prepared via Powder Metallurgy.

PubMed

Yang, Chao; Muránsky, Ondrej; Zhu, Hanliang; Thorogood, Gordon J; Avdeev, Maxim; Huang, Hefei; Zhou, Xingtai

2017-04-06

A new generation of alloys, which rely on a combination of various strengthening mechanisms, has been developed for application in molten salt nuclear reactors. In the current study, a battery of dispersion and precipitation-strengthened (DPS) NiMo-based alloys containing varying amounts of SiC (0.5-2.5 wt %) were prepared from Ni-Mo-SiC powder mixture via a mechanical alloying (MA) route followed by spark plasma sintering (SPS) and rapid cooling. Neutron Powder Diffraction (NPD), Electron Back Scattering Diffraction (EBSD), and Transmission Electron Microscopy (TEM) were employed in the characterization of the microstructural properties of these in-house prepared NiMo-SiC DPS alloys. The study showed that uniformly-dispersed SiC particles provide dispersion strengthening, the precipitation of nano-scale Ni₃Si particles provides precipitation strengthening, and the solid-solution of Mo in the Ni matrix provides solid-solution strengthening. It was further shown that the milling time has significant effects on the microstructural characteristics of these alloys. Increased milling time seems to limit the grain growth of the NiMo matrix by producing well-dispersed Mo₂C particles during sintering. The amount of grain boundaries greatly increases the Hall-Petch strengthening, resulting in significantly higher strength in the case of 48-h-milled NiMo-SiC DPS alloys compared with the 8-h-milled alloys. However, it was also shown that the total elongation is considerably reduced in the 48-h-milled NiMo-SiC DPS alloy due to high porosity. The porosity is a result of cold welding of the powder mixture during the extended milling process.

The Effect of Milling Time on the Microstructural Characteristics and Strengthening Mechanisms of NiMo-SiC Alloys Prepared via Powder Metallurgy

PubMed Central

Yang, Chao; Muránsky, Ondrej; Zhu, Hanliang; Thorogood, Gordon J.; Avdeev, Maxim; Huang, Hefei; Zhou, Xingtai

2017-01-01

A new generation of alloys, which rely on a combination of various strengthening mechanisms, has been developed for application in molten salt nuclear reactors. In the current study, a battery of dispersion and precipitation-strengthened (DPS) NiMo-based alloys containing varying amounts of SiC (0.5–2.5 wt %) were prepared from Ni-Mo-SiC powder mixture via a mechanical alloying (MA) route followed by spark plasma sintering (SPS) and rapid cooling. Neutron Powder Diffraction (NPD), Electron Back Scattering Diffraction (EBSD), and Transmission Electron Microscopy (TEM) were employed in the characterization of the microstructural properties of these in-house prepared NiMo-SiC DPS alloys. The study showed that uniformly-dispersed SiC particles provide dispersion strengthening, the precipitation of nano-scale Ni3Si particles provides precipitation strengthening, and the solid-solution of Mo in the Ni matrix provides solid-solution strengthening. It was further shown that the milling time has significant effects on the microstructural characteristics of these alloys. Increased milling time seems to limit the grain growth of the NiMo matrix by producing well-dispersed Mo2C particles during sintering. The amount of grain boundaries greatly increases the Hall–Petch strengthening, resulting in significantly higher strength in the case of 48-h-milled NiMo-SiC DPS alloys compared with the 8-h-milled alloys. However, it was also shown that the total elongation is considerably reduced in the 48-h-milled NiMo-SiC DPS alloy due to high porosity. The porosity is a result of cold welding of the powder mixture during the extended milling process. PMID:28772747

Structural properties of a family of hydrogen-bonded co-crystals formed between gemfibrozil and hydroxy derivatives of t-butylamine, determined directly from powder X-ray diffraction data

NASA Astrophysics Data System (ADS)

Cheung, Eugene Y.; David, Sarah E.; Harris, Kenneth D. M.; Conway, Barbara R.; Timmins, Peter

2007-03-01

We report the formation and structural properties of co-crystals containing gemfibrozil and hydroxy derivatives of t-butylamine H 2NC(CH 3) 3-n(CH 2OH) n, with n=0, 1, 2 and 3. In each case, a 1:1 co-crystal is formed, with transfer of a proton from the carboxylic acid group of gemfibrozil to the amino group of the t-butylamine derivative. All of the co-crystal materials prepared are polycrystalline powders, and do not contain single crystals of suitable size and/or quality for single crystal X-ray diffraction studies. Structure determination of these materials has been carried out directly from powder X-ray diffraction data, using the direct-space Genetic Algorithm technique for structure solution followed by Rietveld refinement. The structural chemistry of this series of co-crystal materials reveals well-defined structural trends within the first three members of the family ( n=0, 1, 2), but significantly contrasting structural properties for the member with n=3.

Anomalous Oxidative Diffusion in Titanium Pyrotechnic Powders

DOE PAGES

Erikson, William W.; Coker, Eric N.

2016-11-10

It has long been observed that oxidation processes in metals tend to follow a parabolic rate law associated with the growth of a surface oxide layer. Here we observe that for certain titanium powders, the expected parabolic law (∝t 1/2) is recovered, yet for others, the exponent differs significantly. One explanation for this non-parabolic, anomalous diffusion arises from fractal geometry. Theoretical considerations indicate that the time response of diffusion-limited processes in an object closely follow a power-law in time (t n) with n=(E–D)/2, where E is the object's Euclidean dimension and D is its boundary's Hausdorff dimension. Non-integer, (fractal) valuesmore » of D will result in n≠1/2. Finite element simulations of several canonical fractal objects were performed to verify the application of this theory; the results matched the theory well. Two different types of titanium powder were tested in isothermal thermogravimetric tests under dilute oxygen. Time-dependent mass uptake data were fit with power-law forms and the associated exponents were used to determine an equivalent fractal dimension. One Ti powder type has an implied surface dimension of ca. 2.3 to 2.5, suggesting fractal geometry may be operative. Finally, the other has a dimension near 2.0, indicating it behaves like traditional material.« less

Preparation of TiO2 Nanocrystallite Powders Coated with 9 mol% ZnO for Cosmetic Applications in Sunscreens

PubMed Central

Ko, Horng-Huey; Chen, Hui-Ting; Yen, Feng-Ling; Lu, Wan-Chen; Kuo, Chih-Wei; Wang, Moo-Chin

2012-01-01

The preparation of TiO2 nanocrystallite powders coated with and without 9 mol% ZnO has been studied for cosmetic applications in sunscreens by a co-precipitation process using TiCl4 and Zn(NO3)2·6H2O as starting materials. XRD results show that the phases of anatase TiO2 and rutile TiO2 coexist for precursor powders without added ZnO (T-0Z) and calcined at 523 to 973 K for 2 h. When the T-0Z precursor powders are calcined at 1273 K for 2 h, only the rutile TiO2 appears. In addition, when the TiO2 precursor powders contain 9 mol% ZnO (T-9Z) are calcined at 873 to 973 K for 2 h, the crystallized samples are composed of the major phase of rutile TiO2 and the minor phases of anatase TiO2 and Zn2Ti3O8. The analyses of UV/VIS/NIR spectra reveal that the absorption of the T-9Z precursor powders after being calcined has a red-shift effect in the UV range with increasing calcination temperature. Therefore, the TiO2 nanocrystallite powders coated with 9 mol% ZnO can be used as the attenuate agent in the UV-A region for cosmetic applications in sunscreens. PMID:22408415

Magnetic properties of mechanically alloyed Mn-Al-C powders

NASA Astrophysics Data System (ADS)

Kohmoto, O.; Kageyama, N.; Kageyama, Y.; Haji, H.; Uchida, M.; Matsushima, Y.

2011-01-01

We have prepared supersaturated-solution Mn-Al-C alloy powders by mechanical alloying using a planetary high-energy mill. The starting materials were pure Mn, Al and C powers. The mechanically-alloyed powders were subjected to a two-step heating. Although starting particles are Al and Mn with additive C, the Al peak disappears with MA time. With increasing MA time, transition from α-Mn to β-Mn does not occur; the α-Mn structure maintains. At 100 h, a single phase of supersaturated-solution α-Mn is obtained. The lattice constant of α-Mn decreases with increasing MA time. From the Scherrer formula, the crystallite size at 500 h is obtained as 200Å, which does not mean amorphous state. By two-step heating, high magnetization (66 emu/g) was obtained from short-time-milled powders (t=10 h). The precursor of the as-milled powder is not a single phase α-Mn but contains small amount of fcc Al. After two-step heating, the powder changes to τ-phase. Although the saturation magnetization increases, the value is less than that by conventional bulk MnAl (88 emu/g). Meanwhile, long-time-milled powder of single α-Mn phase results in low magnetization (5.2 emu/g) after two-step heating.

Synthesis, mechanical properties and corrosion behavior of powder metallurgy processed Fe/Mg2Si composites for biodegradable implant applications.

PubMed

Sikora-Jasinska, M; Paternoster, C; Mostaed, E; Tolouei, R; Casati, R; Vedani, M; Mantovani, D

2017-12-01

Recently, Fe and Fe-based alloys have shown their potential as degradable materials for biomedical applications. Nevertheless, the slow corrosion rate limits their performance in certain situations. The shift to iron matrix composites represents a possible approach, not only to improve the mechanical properties, but also to accelerate and tune the corrosion rate in a physiological environment. In this work, Fe-based composites reinforced by Mg 2 Si particles were proposed. The initial powders were prepared by different combinations of mixing and milling processes, and finally consolidated by hot rolling. The influence of the microstructure on mechanical properties and corrosion behavior of Fe/Mg 2 Si was investigated. Scanning electron microscopy and X-ray diffraction were used for the assessment of the composite structure. Tensile and hardness tests were performed to characterize the mechanical properties. Potentiodynamic and static corrosion tests were carried out to investigate the corrosion behavior in a pseudo-physiological environment. Samples with smaller Mg 2 Si particles showed a more homogenous distribution of the reinforcement. Yield and ultimate tensile strength increased when compared to those of pure Fe (from 400MPa and 416MPa to 523MPa and 630MPa, respectively). Electrochemical measurements and immersion tests indicated that the addition of Mg 2 Si could increase the corrosion rate of Fe even twice (from 0.14 to 0.28mm·year -1 ). It was found that the preparation method of the initial composite powders played a major role in the corrosion process as well as in the corrosion mechanism of the final composite. Copyright © 2017 Elsevier B.V. All rights reserved.

The Application of Globular Water-Atomized Iron Powders for Additive Manufacturing by a LENS Technique

PubMed Central

Ziętala, Michał; Antolak-Dudka, Anna; Paserin, Vlad

2018-01-01

The water-atomized ATOMET 28, 1001, 4701, and 4801 powders, manufactured by Rio Tinto Metal Powders, were used for additive manufacturing by a laser engineered net shaping (LENS) technique. Their overall morphology was globular and rounded with a size distribution from about 20 to 200 µm. Only the ATOMET 28 powder was characterized by a strong inhomogeneity of particle size and irregular polyhedral shape of powder particles with sharp edges. The powders were pre-sieved to a size distribution from 40 to 150 µm before LENS processing. One particular sample—LENS-fabricated from the ATOMET 28 powder—was characterized by the largest cross-sectional (2D) porosity of 4.2% and bulk porosity of 3.9%, the latter determined by microtomography measurements. In contrast, the cross-sectional porosities of bulk, solid, nearly cubic LENS-fabricated samples from the other ATOMET powders exhibited very low porosities within the range 0.03–0.1%. Unexpectedly, the solid sample—LENS-fabricated from the reference, a purely spherical Fe 99.8 powder—exhibited a porosity of 1.1%, the second largest after that of the pre-sieved, nonspherical ATOMET 28 powder. Vibrations incorporated mechanically into the LENS powder feeding system substantially improved the flow rate vs. feeding rate dependence, making it completely linear with an excellent coefficient of fit, R2 = 0.99. In comparison, the reference powder Fe 99.8 always exhibited a linear dependence of the powder flow rate vs. feeding rate, regardless of vibrations. PMID:29783704

Data on the influence of cold isostatic pre-compaction on mechanical properties of polycrystalline nickel sintered using Spark Plasma Sintering.

PubMed

Dutel, Guy-Daniel; Langlois, Patrick; Tingaud, David; Vrel, Dominique; Dirras, Guy

2017-04-01

Data regarding bulk polycrystalline nickel samples obtained by powder metallurgy using Spark Plasma Sintering (SPS) are presented, with a special emphasis on the influence of a cold isostatic pre-compaction on the resulting morphologies and subsequent mechanical properties. Three types of initial powders are used, nanometric powders, micrometric powders and a mixture of the formers. For each type of powder, the SPS cycle has been optimized for the powders without pre-compaction and the same cycle has been used to also sinter pre-compacted powders.

Refinement of the crystal structure of the high-temperature phase G0 in (NH4)2WO2F4 (powder, x-ray, and neutron scattering)

DOE Office of Scientific and Technical Information (OSTI.GOV)

Novak, D. M.; Smirnov, Lev S; Kolesnikov, Alexander I

2013-01-01

The (NH4)2WO2F4 compound undergoes a series of phase transitions: G0 -> 201 K -> G1 -> 160 K -> G2, with a significant change in entropy ( S1 ~ Rln10 at the G0 -> G1 transition), which indicates significant orientational disordering in the G0 phase and the order disorder type of the phase transition. X-ray diffraction is used to identify the crystal structure of the G0 phase as rhombohedral (sp. gr. Cmcm, Z = 4), determine the lattice parameters and the positions of all atoms (except hydrogen), and show that [WO2F4]2 ions can form a superposition of dynamic and staticmore » orientational disorders in the anionic sublattice. A determination of the orientational position of [NH4]+ ions calls for the combined method of elastic and inelastic neutron scattering. Inelastic neutron scattering is used to determine the state of hindered rotation for ammonium ions in the G0 phase. Powder neutron diffraction shows that the orientational disorder of NH4 ions can adequately be described within the free rotation approximation.« less

Bio-ecological consequences of crop seeds treatment with metal nano-powders

NASA Astrophysics Data System (ADS)

Churilov, G.

2015-11-01

As a result of our investigations we have determined the optimal concentrations of ferrum, cobalt and cuprum nano-powders recommended to be used as micro-fertilizers increasing the yield and feed value of crops at the expense of accumulating biologically active combinations by 25-35%. In unfavorable climate conditions, for example in a case of excess moisture or heat and drought, the plants development and ripening suffer. Our investigations have shown that the stimulating effect of nano-powders has lowered the effect of stress situations on plants development and simultaneously increased the rape seeds yield and quality. Treating the seeds with the drugs being studied has provided the high crop protection. If consider that the maximum efficiency of protectants Chinuk, SK (20 kg/t of seeds) and Cruiser, KS (10 kg/t of seeds) then for the same effect one needs nano-powders 0.1 g per hectare norm of seeds planting.

Complete genome sequence of Defluviimonas alba cai42T, a microbial exopolysaccharides producer.

PubMed

Zhao, Jie-Yu; Geng, Shuang; Xu, Lian; Hu, Bing; Sun, Ji-Quan; Nie, Yong; Tang, Yue-Qin; Wu, Xiao-Lei

2016-12-10

Defluviimonas alba cai42 T , isolated from the oil-production water in Xinjiang Oilfield in China, has a strong ability to produce exopolysaccharides (EPS). We hereby present its complete genome sequence information which consists of a circular chromosome and three plasmids. The strain characteristically contains various genes encoding for enzymes involved in EPS biosynthesis, modification, and export. According to the genomic and physiochemical data, it is predicted that the strain has the potential to be utilized in industrial production of microbial EPS. Copyright © 2016 Elsevier B.V. All rights reserved.

Welding Metallurgy and Processing Issues for Joining of Power Sources

DOE Office of Scientific and Technical Information (OSTI.GOV)

Lienert, Thomas J.; Reardon, Patrick T.

2012-08-14

Weldability issues with the pertinent alloys have been reviewed and preliminary results of our work on Haynes 25 have been presented. Further results on the mechanical properties and metallography on the EB welds are imminent. Hot-ductility experiments will commence within a few weeks. Aging studies on the effects of heat treatment using the Gleeble are also planned. MST-6 has extensive background in the welding metallurgy of the pertinent alloys. We also have considerable experience with the various welding processes to be used.

Calibration and testing of a Raman hyperspectral imaging system to reveal powdered food adulteration

USDA-ARS?s Scientific Manuscript database

The potential adulteration of foodstuffs has led to increasing concern regarding food safety and security, in particular for powdered food products where cheap ground materials or hazardous chemicals can be added to increase the quantity of powder or to obtain the desired aesthetic quality. Due to t...

Resin-Powder Dispenser

NASA Technical Reports Server (NTRS)

Standfield, Clarence E.

1994-01-01

Resin-powder dispenser used at NASA's Langley Research Center for processing of composite-material prepregs. Dispenser evenly distributes powder (resin polymer and other matrix materials in powder form) onto wet uncured prepregs. Provides versatility in distribution of solid resin in prepreg operation. Used wherever there is requirement for even, continuous distribution of small amount of powder.

Development of Cu Reinforced SiC Particulate Composites

NASA Astrophysics Data System (ADS)

Singh, Harshpreet; Kumar, Lailesh; Nasimul Alam, Syed

2015-02-01

This paper presents the results of Cu-SiCp composites developed by powder metallurgy route and an attempt has been made to make a comparison between the composites developed by using unmilled Cu powder and milled Cu powder. SiC particles as reinforcement was blended with unmilled and as-milled Cu powderwith reinforcement contents of 10, 20, 30, 40 vol. % by powder metallurgy route. The mechanical properties of pure Cu and the composites developed were studied after sintering at 900°C for 1 h. Density of the sintered composites were found out based on the Archimedes' principle. X-ray diffraction of all the composites was done in order to determine the various phases in the composites. Scanning electron microscopy (SEM) and EDS (electron diffraction x-ray spectroscopy) was carried out for the microstructural analysis of the composites. Vickers microhardness tester was used to find out the hardness of the samples. Wear properties of the developed composites were also studied.

Increased T cell recruitment to the CNS after amyloid beta 1-42 immunization in Alzheimer's mice overproducing transforming growth factor-beta 1.

PubMed

Buckwalter, Marion S; Coleman, Bronwen S; Buttini, Manuel; Barbour, Robin; Schenk, Dale; Games, Dora; Seubert, Peter; Wyss-Coray, Tony

2006-11-01

Immunotherapy targeting the amyloid beta (Abeta) peptide is a novel therapy under investigation for the treatment of Alzheimer's disease (AD). A clinical trial using Abeta(1-42) (AN1792) as the immunogen was halted as a result of development of meningoencephalitis in a small number of patients. The cytokine TGF-beta1 is a key modulator of immune responses that is increased in the brain in AD. We show here that local overexpression of TGF-beta1 in the brain increases both meningeal and parenchymal T lymphocyte number. Furthermore, TGF-beta1 overexpression in a mouse model for AD [amyloid precursor protein (APP) mice] leads to development of additional T cell infiltrates when mice were immunized at a young but not old age with AN1792. Notably, only mice overproducing both Abeta (APP mice) and TGF-beta1 experienced a rise in T lymphocyte number after immunization. One-third of infiltrating T cells were CD4 positive. We did not observe significant differences in B lymphocyte numbers in any of the genotypes or treatment groups. These results demonstrate that TGF-beta1 overproduction in the brain can promote T cell infiltration, in particular after Abeta(1-42) immunization. Likewise, levels of TGF-beta1 or other immune factors in brains of AD patients may influence the response to Abeta(1-42) immunization.

Sensory analysis of cosmetic powders: personal care ingredients and emulsions.

PubMed

Moussour, M; Lavarde, M; Pensé-Lhéritier, A-M; Bouton, F

2017-02-01

The powders are ingredients increasingly used in the formulation of cosmetic products for the sensory qualities they give. The objective of this study was the development of a lexicon and a referential for sensory characterization of these pure raw materials as well as formulations which contain them. Eleven expert panellists from Ecole de biologie industrielle de Cergy (France) developed a lexicon and a referential based on 12 powders of different chemical natures. The selected attributes were then used for performing a quantitative descriptive profile of two powders and an emulsion containing or not one of these two powders. A lexicon has been established through a consensus approach of the panel. It contains seven attributes that allow the evaluation of the powders in four phases: the appearance, the pickup, the application and the after-feel. This lexicon contains definitions and assessment protocols and provides references products. The quantitative descriptive profile of two powders of the same chemical nature, but different in physical quality showed significant differences in sensory level between products. These same attributes used to evaluate an emulsion containing the powder or not allowed to prove the contribution of these raw materials on the sensory specificities of the emulsion. The lexicon developed in this study can be used for assessment of other powders but also to define the quantities necessary to put in the formulation to meet the sensory characteristics of these raw materials powder. © 2016 Society of Cosmetic Scientists and the Société Française de Cosmétologie.

Biosorption of praseodymium (III) using Terminalia arjuna bark powder in batch systems: isotherm and kinetic studies.

PubMed

Swain, Krishna Kumari; Mishra, Pravat Manjari; Devi, Aparna Prabha

2018-02-01

The high demand for rare earth elements (REEs) used in various advanced materials implies demand for increased production of REEs or the recycling of solutions to recover the REEs they contain. In this study, the biosorption of Pr(III) from aqueous solution by bark powder of Terminalia arjuna was examined in a batch system as a function of metal concentration, biosorbent dosage, pH and contact time. Results showed that T. arjuna bark powder has a high affinity for adsorbing Pr(III): more than 90% at pH 6.63. The adsorption of Pr(III) by T. arjuna bark powder was investigated by the Langmuir, Freundlich, Temkin and Dubinin-Radushkevich isotherm models. The kinetics of the biosorption process was tested with pseudo-first-order and pseudo-second-order models, and the results showed that the biosorption process was better fitted to the pseudo-second-order model. From Fourier transform infrared spectroscopy (FT-IR) analysis, it is confirmed that the biomolecules of T. arjuna bark powder are involved in the biosorption process of Pr(III) metal ions.

Physical metallurgy: Scientific school of the Academician V.M. Schastlivtsev

NASA Astrophysics Data System (ADS)

Tabatchikova, T. I.

2016-04-01

This paper is to honor Academician Vadim Mikhailovich Schastlivtsev, a prominent scientist in the field of metal physics and materials science. The article comprises an analysis of the topical issues of the physical metallurgy of the early 21st century and of the contribution of V.M. Schastlivtsev and of his school to the science of phase and structural transformations in steels. In 2015, Vadim Mikhailovich celebrates his 80th birthday, and this paper is timed to this honorable date. The list of his main publications is given in it.

Formulation and nutritional evaluation of a healthy vegetable soup powder supplemented with soy flour, mushroom, and moringa leaf.

PubMed

Farzana, Tasnim; Mohajan, Suman; Saha, Trissa; Hossain, Md Nur; Haque, Md Zahurul

2017-07-01

The research study was conducted to develop a healthy vegetables soup powder supplemented with soy flour, mushroom, moringa leaf and compare its nutritional facts with locally available soup powders. Proximate analysis and sensory evaluation were done by standard method. In this study, moisture, ash, protein, fat, fiber, carbohydrate, and energy content were ranged from 2.83% to 5.46%, 9.39% to 16.48%, 6.92% to 16.05%, 4.22% to 6.39%, 0.22% to 1.61%, 58.81% to 75.41%, and 337.42 to 386.72 kcal/100 g, respectively. Highest content of vitamin D, minerals, protein, and fiber and lowest content of moisture, fat, and carbohydrate were found in the presently developed soy-mushroom-moringa soup powder compare to locally available soup powders. Vitamin C was also found significantly higher than locally available soup powders S1, S2, and S3. Heavy metals were not found in any of the soup powders. On the sensory and microbiological point of view, the presently developed soup powder was found highly acceptable up to 6 months. So, the developed soy-mushroom-moringa soup powder is nutritionally superior to locally available soup powders and sufficient to meet day-to-day nutritional requirements as a supplement.

The last glacial maximum locations of summer-green tree refugia using simulations with ECHAM3 T42 uncoupled, ECHAM5 T31 coupled and ECHAM5 T106 uncoupled models

NASA Astrophysics Data System (ADS)

Arpe, K.; Leroy, S. A. G.; Mikolajewicz, U.

2010-04-01

Model simulations of the last glacial maximum (21±2 ka) with the ECHAM3 T42, ECHAM5 T31 coupled and ECHAM5 T106 uncoupled models are compared. The ECHAM5 T106 simulations were forced at the boundaries by results from the coupled ECHAM5-MPIOM atmosphere ocean model while the ECHAM3 T42 model was forced with prescribed sea surface temperatures (SSTs) provided by Climate/Long-Range Investigation, Mapping Prediction project (CLIMAP). The topography, land-sea mask and glacier distribution for the ECHAM5 simulations were taken from the PMIP2 data set while for ECHAM3 they were taken from PMIP1. The ECHAM5 simulations were run with a variable SST in time simulated by the coupled model. These were also used for the T106 run but corrected for systematic errors. The SSTs in the ECHAM5-MPIOM simulations for the last glacial maximum (LGM) were much warmer in the northern Atlantic than those suggested by CLIMAP or GLAMAP while they were cooler everywhere else. This had a clear effect on the temperatures over Europe, warmer for winters in Western Europe and cooler for Eastern Europe than the simulation with CLIMAP SSTs. Considerable differences in the general circulation patterns were found in the different simulations. A ridge over Western Europe for the present climate during winter in the 500 hPa height field remains in the ECHAM5 simulations for the LGM, more so in the T106 version, while the ECHAM3 CLIMAP simulation provided a trough. The zonal wind between 30° W and 10° E shows a southward shift of the polar and subtropical jet in the T106 simulation for the LGM and an extremely strong polar jet for the ECHAM3 CLIMAP. The latter can probably be assigned to the much stronger north-south gradient in the CLIMAP SSTs. The southward shift of the polar jet during LGM is supported by observation evidence. Cyclone tracks in winter represented by high precipitation are characterised over Europe for the present by a main branch from Great Britain to Norway and a secondary branch

[Impact of directly compressed auxiliary materials on powder property of fermented cordyceps powder].

PubMed

Chen, Li-Hua; Yue, Guo-Chao; Guan, Yong-Mei; Yang, Ming; Zhu, Wei-Feng

2014-01-01

To investigate such physical indexes as hygroscopicity, angle of repose, bulk density, fillibility of compression of mixed powder of directly compressed auxiliary materials and fermented cordyceps powder by using micromeritic study methods. The results showed that spray-dried lactose Flowlac100 and microcrystalline cellulose Avicel PH102 had better effect in liquidity and compressibility on fermented cordyceps powder than pregelatinized starch. The study on the impact of directly compressed auxiliary materials on the powder property of fermented cordyceps powder had guiding significant to the research of fermented cordyceps powder tablets, and could provide basis for the development of fermented cordyceps powder tablets.

Vacuum Powder Injector

NASA Technical Reports Server (NTRS)

Working, Dennis C.

1991-01-01

Method developed to provide uniform impregnation of bundles of carbon-fiber tow with low-solubility, high-melt-flow polymer powder materials to produce composite prepregs. Vacuum powder injector expands bundle of fiber tow, applies polymer to it, then compresses bundle to hold powder. System provides for control of amount of polymer on bundle. Crystallinity of polymer maintained by controlled melt on takeup system. All powder entrapped, and most collected for reuse. Process provides inexpensive and efficient method for making composite materials. Allows for coating of any bundle of fine fibers with powders. Shows high potential for making prepregs of improved materials and for preparation of high-temperature, high-modulus, reinforced thermoplastics.

7 CFR 305.42 - Miscellaneous treatment schedules.

Code of Federal Regulations, 2010 CFR

2010-01-01

... 7 Agriculture 5 2010-01-01 2010-01-01 false Miscellaneous treatment schedules. 305.42 Section 305... INSPECTION SERVICE, DEPARTMENT OF AGRICULTURE PHYTOSANITARY TREATMENTS Miscellaneous Treatments § 305.42 Miscellaneous treatment schedules. (a) T102-b, T102-b-1, T102-b-2, soapy water and wax. (1) The fruit must be...

Association of Cerebrospinal Fluid β-Amyloid 1-42, T-tau, P-tau181, and α-Synuclein Levels With Clinical Features of Drug-Naive Patients With Early Parkinson Disease

PubMed Central

Kang, Ju-Hee; Irwin, David J.; Chen-Plotkin, Alice S.; Siderowf, Andrew; Caspell, Chelsea; Coffey, Christopher S.; Waligórska, Teresa; Taylor, Peggy; Pan, Sarah; Frasier, Mark; Marek, Kenneth; Kieburtz, Karl; Jennings, Danna; Simuni, Tanya; Tanner, Caroline M.; Singleton, Andrew; Toga, Arthur W.; Chowdhury, Sohini; Mollenhauer, Brit; Trojanowski, John Q.; Shaw, Leslie M.

2014-01-01

Importance We observed a significant correlation between cerebrospinal fluid (CSF) levels of tau proteins and α-synuclein, but not β-amyloid 1–42 (Aβ1–42), and lower concentration of CSF biomarkers, as compared with healthy controls, in a cohort of entirely untreated patients with Parkinson disease (PD) at the earliest stage of the disease studied so far. Objective To evaluate the baseline characteristics and relationship to clinical features of CSF biomarkers (Aβ1–42, total tau [T-tau], tau phosphorylated at threonine 181 [P-tau181], and α-synuclein) in drug-naive patients with early PD and demographically matched healthy controls enrolled in the Parkinson’s Progression Markers Initiative (PPMI) study. Design, Setting, and Participants Cross-sectional study of the initial 102 research volunteers (63 patients with PD and 39 healthy controls) of the PPMI cohort. Main Outcomes and Measures The CSF biomarkers were measured by INNO-BIA AlzBio3 immunoassay (Aβ1–42, T-tau, and P-tau181; Innogenetics Inc) or by enzyme-linked immunosorbent assay (α-synuclein). Clinical features including diagnosis, demographic characteristics, motor, neuropsychiatric, and cognitive assessments, and DaTscan were systematically assessed according to the PPMI study protocol. Results Slightly, but significantly, lower levels of Aβ1–42, T-tau, P-tau181, α-synuclein, and T-tau/Aβ1–42 were seen in subjects with PD compared with healthy controls but with a marked overlap between groups. Using multivariate regression analysis, we found that lower Aβ1–42 and P-tau181 levels were associated with PD diagnosis and that decreased CSF T-tau and α-synuclein were associated with increased motor severity. Notably, when we classified patients with PD by their motor phenotypes, lower CSF Aβ1–42 and P-tau181 concentrations were associated with the postural instability–gait disturbance–dominant phenotype but not with the tremor-dominant or intermediate phenotype. Finally, we

New technology for separating resin powder and fiberglass powder from fiberglass-resin powder of waste printed circuit boards.

PubMed

Li, Jia; Gao, Bei; Xu, Zhenming

2014-05-06

New recycling technologies have been developed lately to enhance the value of the fiberglass powder-resin powder fraction (FRP) from waste printed circuit boards. The definite aim of the present paper is to present some novel methods that use the image forces for the separation of the resin powder and fiberglass powder generated from FRP during the corona electrostatic separating process. The particle shape charactization and particle trajectory simulation were performed on samples of mixed non-metallic particles. The simulation results pointed out that particles of resin powder and particles of fiberglass powder had different detach trajectories at the conditions of the same size and certain device parameters. An experiment carried out using a corona electrostatic separator validated the possibility of sorting these particles based on the differences in their shape characteristics. The differences in the physical properties of the different types of particles provided the technical basis for the development of electrostatic separation technologies for the recycling industry.

Hot tensile tests of Inconel 718

NASA Technical Reports Server (NTRS)

1980-01-01

The physical metallurgy of near-solidus integranular cracking in Inconel 718 welds was investigated. The data, although inconclusive, suggest at least two mechanisms which might explain intergranular cracking (microfissuring) in the heat-affected zone of several high temperature alloys. One theory is based on the separation of intergranular liquid while the other involves mechanical failure of solid ligaments surrounded by intergranular liquid. Both mechanisms concentrate strain in the grain boundaries resulting in low strain (1%) intergranular brittleness. The mechanisms reported might also pertain to the physical metallurgy of casting, powder metallurgy sintering and hot isostatic pressing.

A Mathematical Model for the Multiphase Transport and Reaction Kinetics in a Ladle with Bottom Powder Injection

NASA Astrophysics Data System (ADS)

Lou, Wentao; Zhu, Miaoyong

2017-12-01

A computation fluid dynamics-population balance model-simultaneous reaction model (CFD-PBM-SRM) coupled model has been proposed to study the multiphase flow behavior and refining reaction kinetics in a ladle with bottom powder injection, and some new and important phenomena and mechanisms are presented. For the multiphase flow behavior, the effects of bubbly plume flow, powder particle motion, particle-particle collision and growth, particle-bubble collision and adhesion, and powder particle removal into top slag are considered. For the reaction kinetics, the mechanisms of multicomponent simultaneous reactions, including Al, S, Si, Mn, Fe, and O, at the multi-interface, including top slag-liquid steel interface, air-liquid steel interface, powder droplet-liquid steel interface, and bubble-liquid steel interface, are presented, and the effect of sulfur solubility in the powder droplet on the desulfurization is also taken into account. Model validation is carried out using hot tests in a 2-t induction furnace with bottom powder injection. The result shows that the powder particles gradually disperse in the entire furnace; in the vicinity of the bottom slot plugs, the desulfurization product CaS is liquid phase, while in the upper region of the furnace, the desulfurization product CaS is solid phase. The predicted sulfur contents by the present model agree well with the measured data in the 2-t furnace with bottom powder injection.

Increased T cell recruitment to the central nervous system after Aβ1–42 immunization in Alzheimer’s mice overproducing TGF-β1

PubMed Central

Buckwalter, Marion S.; Coleman, Bronwen S.; Buttini, Manuel; Barbour, Robin; Schenk, Dale; Games, Dora; Seubert, Peter; Wyss-Coray, T

2007-01-01

Immunotherapy targeting the Aβ peptide is a novel therapy under investigation for the treatment of Alzheimer’s disease (AD). A clinical trial using Aβ1–42 (AN1792) as the immunogen was halted due to development of meningoencephalitis in a small number of patients. The cytokine TGF-β1 is a key modulator of immune responses that is increased in the brain in AD. We show here that local overexpression of TGF-β1 in the brain increases both meningeal and parenchymal T lymphocyte number. Furthermore, TGF-β1 overexpression in a mouse model for AD (APP mice) leads to development of further T cell infiltrates when mice were immunized at a young but not old age with AN1792. Notably, only mice overproducing both Aβ (APP mice) and TGF-β1 experienced a rise in T lymphocyte number after immunization. One third of infiltrating T cells were CD4 positive. We did not observe significant differences in B lymphocyte numbers in any of the genotypes or treatment groups. These results demonstrate that TGF-β1 overproduction in the brain can promote T cell infiltration, in particular after Aβ1–42 immunization. Likewise, levels of TGF-β1 or other immune factors in brains of AD patients may influence the response to Aβ1–42 immunization. PMID:17079673

Early atmospheric metal pollution provides evidence for Chalcolithic/Bronze Age mining and metallurgy in Southwestern Europe.

PubMed

Martínez Cortizas, Antonio; López-Merino, Lourdes; Bindler, Richard; Mighall, Tim; Kylander, Malin E

2016-03-01

Although archaeological research suggests that mining/metallurgy already started in the Chalcolithic (3rd millennium BC), the earliest atmospheric metal pollution in SW Europe has thus far been dated to ~3500-3200 cal.yr. BP in paleo-environmental archives. A low intensity, non-extensive mining/metallurgy and the lack of appropriately located archives may be responsible for this mismatch. We have analysed the older section (>2100 cal.yr. BP) of a peat record from La Molina (Asturias, Spain), a mire located in the proximity (35-100 km) of mines which were exploited in the Chalcolithic/Bronze Age, with the aim of assessing evidence of this early mining/metallurgy. Analyses included the determination of C as a proxy for organic matter content, lithogenic elements (Si, Al, Ti) as markers of mineral matter, and trace metals (Cr, Cu, Zn, Pb) and stable Pb isotopes as tracers of atmospheric metal pollution. From ~8000 to ~4980 cal.yr. BP the Pb composition is similar to that of the underlying sediments (Pb 15 ± 4 μg g(-1); (206)Pb/(207)Pb 1.204 ± 0.002). A sustained period of low (206)Pb/(207)Pb ratios occurred from ~4980 to ~2470 cal.yr. BP, which can be divided into four phases: Chalcolithic (~4980-3700 cal.yr. BP), (206)Pb/(207)Pb ratios decline to 1.175 and Pb/Al ratios increase; Early Bronze Age (~3700-3500 cal.yr. BP), (206)Pb/(207)Pb increase to 1.192 and metal/Al ratios remain stable; Late Bronze Age (~3500-2800 cal.yr. BP), (206)Pb/(207)Pb decline to their lowest values (1.167) while Pb/Al and Zn/Al increase; and Early Iron Age (~2800-2470 cal.yr. BP), (206)Pb/(207)Pb increase to 1.186, most metal/Al ratios decrease but Zn/Al shows a peak. At the beginning of the Late Iron Age, (206)Pb/(207)Pb ratios and metal enrichments show a rapid return to pre-anthropogenic values. These results provide evidence of regional/local atmospheric metal pollution triggered by the earliest phases of mining/metallurgy in the area, and reconcile paleo-environmental and

High-Yield Preparation and Electrochemical Properties of Few-Layer MoS2 Nanosheets by Exfoliating Natural Molybdenite Powders Directly via a Coupled Ultrasonication-Milling Process

NASA Astrophysics Data System (ADS)

Dong, Huina; Chen, Deliang; Wang, Kai; Zhang, Rui

2016-09-01

Cost-effective and scalable preparation of two-dimensional (2D) molybdenum disulfide (MoS2) has been the bottleneck that limits their applications. This paper reports a novel coupled ultrasonication-milling (CUM) process to exfoliate natural molybdenite powders to achieve few-layer MoS2 (FL-MoS2) nanosheets in the solvent of N-methyl-2-pyrrolidone (NMP) with polyvinylpyrrolidone (PVP) molecules. The synergistic effect of ultrasonication and sand milling highly enhanced the exfoliation efficiency, and the precursor of natural molybdenite powders minimizes the synthetic cost of FL-MoS2 nanosheets. The exfoliation of natural molybdenite powders was conducted in a home-made CUM system, mainly consisting of an ultrasonic cell disruptor and a ceramic sand mill. The samples were characterized by X-ray diffraction, UV-vis spectra, Raman spectra, FT-IR, SEM, TEM, AFM, and N2 adsorption-desorption. The factors that influence the exfoliation in the CUM process, including the initial concentration of natural molybdenite powders ( C in, 15-55 g L-1), ultrasonic power ( P u, 200-350 W), rotation speed of sand mill ( ω s, 1500-2250 r.p.m), exfoliation time ( t ex, 0.5-6 h), and the molar ratio of PVP unit to MoS2 ( R pm, 0-1), were systematically investigated. Under the optimal CUM conditions (i.e., C in = 45 g L-1, P u = 280 W, ω s = 2250 r.p.m and R pm = 0.5), the yield at t ex = 6 h reaches 21.6 %, and the corresponding exfoliation rate is as high as 1.42 g L-1 h-1. The exfoliation efficiency of the CUM mode is much higher than that of either the ultrasonication (U) mode or the milling (M) mode. The synergistic mechanism and influencing rules of the CUM process in exfoliating natural molybdenite powders were elaborated. The as-obtained FL-MoS2 nanosheets have a high specific surface area of 924 m2 g-1 and show highly enhanced electrocatalytic performance in hydrogen evolution reaction and good electrochemical sensing property in detecting ascorbic acid. The CUM process

TITANIUM METALLURGY: A BIBLIOGRAPHY OF CONFIDENTIAL U.S. ATOMIC ENERGY COMMISSION REPORTS AVAILABLE THROUGH THE CIVILIAN APPLICATION PROGRAM

DOE Office of Scientific and Technical Information (OSTI.GOV)

None

1956-09-01

This bibliography contains 54 annotated references to reports on titunium metallurgy. References are included to reports written prior to August 1, 1956. Author, subject, and report number indexes are provided. (auth)

Evaluation of Cyclic Behavior of Aircraft Turbine Disk Alloys

NASA Technical Reports Server (NTRS)

Shahani, V.; Popp, H. G.

1978-01-01

An evaluation of the cyclic behavior of three aircraft engine turbine disk materials was conducted to compare their relative crack initiation and crack propagation resistance. The disk alloys investigated were Inconel 718, hot isostatically pressed and forged powder metallurgy Rene '95, and as-hot-isostatically pressed Rene '95. The objective was to compare the hot isostatically pressed powder metallurgy alloy forms with conventionally processed superalloys as represented by Inconel 718. Cyclic behavior was evaluated at 650 C both under continuously cycling and a fifteen minute tensile hold time cycle to simulate engine conditions. Analysis of the test data were made to evaluate the strain range partitioning and energy exhaustion concepts for predicting hold time effects on low cycle fatigue.

The Mechanical Properties of Candidate Superalloys for a Hybrid Turbine Disk

NASA Technical Reports Server (NTRS)

Gabb, Timothy P.; MacKay, Rebecca A.; Draper, Susan L.; Sudbrack, Chantal K.; Nathal, Michael V.

2013-01-01

The mechanical properties of several cast blade superalloys and one powder metallurgy disk superalloy were assessed for potential use in a dual alloy hybrid disk concept of joined dissimilar bore and web materials. Grain size was varied for each superalloy class. Tensile, creep, fatigue, and notch fatigue tests were performed at 704 to 815 degC. Typical microstructures and failure modes were determined. Preferred materials were then selected for future study as the bore and rim alloys in this hybrid disk concept. Powder metallurgy superalloy LSHR at 15 micron grain size and single crystal superalloy LDS-1101+Hf were selected for further study, and future work is recommended to develop the hybrid disk concept.

Interdiffusion behavior of tungsten or rhenium and group 5 and 6 elements and alloys of the periodic table. Part 2A: Appendices A-G

NASA Technical Reports Server (NTRS)

Arcella, F. G.

1974-01-01

Arc cast W, CVD, W, CVD Re, and powder metallurgy Re materials were hot isostatically pressure welded to ten different refractory metals and alloys and thermally aged at 10 to the minus 8th power torr at 1200 C, 1500 C, 1630 C, 1800 C, and 2000 C for 100 hours to 2000 hours. Electron beam microprobe analysis was used to characterize the interdiffusion zone width of each couple system as a function of age time and temperature. Each system was least squares fitted to the equation: In (delta X sq/t) = B/T + A, where delta X is net interdiffusion zone width, t is age time, and T is age temperature. Detailed descriptions of experimental and analytical procedures utilized in conducting the experimental program are provided. For Vol. 1, see N74-34046.

Application of vacuum metallurgy to separate pure metal from mixed metallic particles of crushed waste printed circuit board scraps.

PubMed

Zhan, Lu; Xu, Zhenming

2008-10-15

The principle of separating pure metal from mixed metallic particles (MMPs) byvacuum metallurgy is that the vapor pressures of various metals at the same temperature are different As a result, the metal with high vapor pressure and low boiling point can be separated from the mixed metals through distillation or sublimation, and then it can be recycled through condensation under a certain condition. The vacuum metallurgy separation (VMS) of MMPs of crushed waste printed circuit boards (WPCBs) has been studied in this paper. Theoretical analyses show that the MMPs (copper, zinc, bismuth, lead, and indium, for example) can be separated by vacuum metallurgy. The copper particles (0.15-0.20 mm) and zinc particles (<0.30 mm) were chosen to simulate the MMPs of crushed WPCBs. Experimental results show that the separated efficiency of zinc in the copper-rich particles achieves 96.19 wt % when the vacuum pressure is 0.01-0.10 Pa, the heating temperature is 1123 K, and the heating time is 105 min. Under this operation condition, the separated efficiency of zinc in the copper-rich particles from crushed WPCBs achieves 97.00 wt % and the copper purity increases from 90.68 to 99.84 wt %.

Study on effects of powder and flake chemistry and morphology on the properties of Al-Cu-Mg-X-X-X powder metallurgy advanced aluminum alloys

NASA Technical Reports Server (NTRS)

Meschter, P. J.; Lederich, R. J.; Oneal, J. E.; Pao, P. S.

1985-01-01

The effects of alloy chemistry and particulate morphology on consolidation behavior and consolidated product properties in rapid solidification processed, powder-metallurgical Al-3Li-1.5Cu-1Mg-0.5Co-0.2Zr and Al-4.4Cu-1.5Mg-Fe-Ni-0.2Zr extrusions and forgings were studied. Microstructures and mechanical properties of both alloys are largely unaffected by particulate production method (vacuum atomization, ultrasonic atomization, or twin-roller quenching) and by particulate solidification rates between 1000 and 100,000 K/s. Consolidation processing by canning, cold compaction, degassing, and hot extrusion is sufficient to yield mechanical properties in the non-Li-containing alloy extrusions which are similar to those of 7075-Al, but ductilities and fracture toughnesses are inferior owing to poor interparticle bonding caused by lack of a vacuum-hot-pressing step during consolidation. Mechanical properties of extrusions are superior to those of forgings owing to the stronger textures produced by the more severe hot working during extrusion. The effects on mechanical properties of dispersoid size and volume fraction, substructural refinement, solid solution strengthening by Mg, and precipitate size and distribution are elucidated for both alloy types.

Micro-feeding and dosing of powders via a small-scale powder pump.

PubMed

Besenhard, M O; Fathollahi, S; Siegmann, E; Slama, E; Faulhammer, E; Khinast, J G

2017-03-15

Robust and accurate powder micro-feeding (<100mg/s) and micro-dosing (<5 mg) are major challenges, especially with regard to regulatory limitations applicable to pharmaceutical development and production. Since known micro-feeders that yield feed rates below 5mg/s use gravimetric feeding principles, feed rates depend primarily on powder properties. In contrast, volumetric powder feeders do not require regular calibration because their feed rates are primarily determined by the feeder's characteristic volume replacement. In this paper, we present a volumetric micro-feeder based on a cylinder piston system (i.e., a powder pump), which allows accurate micro-feeding and feed rates of a few grams per hours even for very fine powders. Our experimental studies addressed the influence of cylinder geometries, the initial conditions of bulk powder, and the piston speeds. Additional computational studies via Discrete Element Method simulations offered a better understanding of the feeding process, its possible limitations and ways to overcome them. The powder pump is a simple yet valuable tool for accurate powder feeding at feed rates of several orders of magnitude. Copyright © 2016 Elsevier B.V. All rights reserved.

Coercivity enhancement of anisotropic Dy-free Nd-Fe-B powders by conventional HDDR process

NASA Astrophysics Data System (ADS)

Morimoto, K.; Katayama, N.; Akamine, H.; Itakura, M.

2012-11-01

Coercivity enhancement of Dy-free Nd-Fe-Co-B-Ga-Zr powders was studied using the conventional hydrogenation-decomposition-desorption-recombination (HDDR) process. It was found that the addition of Al together with the proper Nd content and the slow hydrogen desorption of the HDDR treatment can induce high coercivity in the powder. For example, the 14.0 at% Nd-2.0 at% Al powder exhibits HcJ of 1560 kA/m, Br of 1.22 T, and (BH)max of 257 kJ/m3. The high coercivity inducement of the powder is thought to be attributed to the formation of Nd-rich phase, which continuously surrounds fine Nd2Fe14B grains.

Unusual high B{sub s} for Fe-based amorphous powders produced by a gas-atomization technique

DOE Office of Scientific and Technical Information (OSTI.GOV)

Yoshida, K.; Bito, M.; Kageyama, J.

2016-05-15

Fe-based alloy powders with a high Fe content of about 81 at.% were produced by a gas-atomization technique. Powders of Fe{sub 81}Si{sub 1.9}B{sub 5.7}P{sub 11.4} (at.%) alloy showed a good glass forming ability and exhibited unusual high saturation magnetic flux density of 1.57 T. The core-loss property at a frequency of 100 kHz for the compacted core made of the Fe{sub 81}Si{sub 1.9}B{sub 5.7}P{sub 11.4} powder is evaluated to be less than 500 kW/m{sup 3} under a maximum induction of 100 mT. Moreover, good DC-superposition characteristic of the core was also confirmed. These results suggest that the present Fe-based alloymore » powder is promising for low-loss magnetic-core materials and expected to contribute in miniaturization of electric parts in the near future.« less

Assessment of heavy metals exposure, noise and thermal safety in the ambiance of a vacuum metallurgy separation system for recycling heavy metals from crushed e-wastes.

PubMed

Zhan, Lu; Xu, Zhenming

2014-12-01

Vacuum metallurgy separation (VMS) is a technically feasible method to recover Pb, Cd and other heavy metals from crushed e-wastes. To further determine the environmental impacts and safety of this method, heavy metals exposure, noise and thermal safety in the ambiance of a vacuum metallurgy separation system are evaluated in this article. The mass concentrations of total suspended particulate (TSP) and PM10 are 0.1503 and 0.0973 mg m(-3) near the facilities. The concentrations of Pb, Cd and Sn in TSP samples are 0.0104, 0.1283 and 0.0961 μg m(-3), respectively. Health risk assessments show that the hazard index of Pb is 3.25 × 10(-1) and that of Cd is 1.09 × 10(-1). Carcinogenic risk of Cd through inhalation is 1.08 × 10(-5). The values of the hazard index and risk indicate that Pb and Cd will not cause non-cancerous effects or carcinogenic risk on workers. The noise sources are mainly the mechanical vacuum pump and the water cooling pump. Both of them have the noise levels below 80 dB (A). The thermal safety assessment shows that the temperatures of the vacuum metallurgy separation system surface are all below 303 K after adopting the circulated water cooling and heat insulation measures. This study provides the environmental information of the vacuum metallurgy separation system, which is of assistance to promote the industrialisation of vacuum metallurgy separation for recovering heavy metals from e-wastes. © The Author(s) 2014.

Consolidation of Fe16N2 Magnets Using Equal Channel Angular Extrusion

DTIC Science & Technology

2015-06-11

industry such as powder metallurgy and hot deformation. The latter require treatments at high temperatures, typically around 1000 oC. In this work...have any deteriorating effects on the magnetization values (compared to the powder ). However, extrusions at temperatures ~150 oC result in a small...Extrusions at temperatures up to ~150 oC do not have any deteriorating effects on the magnetization values (compared to the powder ). However, extrusions at

Powder-metallurgical preparation of A15 superconductors

NASA Astrophysics Data System (ADS)

Wilhelm, Manfred; Wohlleben, Karl; Springer, Engelbert; Mrowiec, Klaus; Schaper, Wilfried; Wecker, Joachim

1985-08-01

The powder-metallurgical preparation of Cu-Nb3Sn microcomposite superconductors was investigated in order to economize in the manufacture of the conductors and to improve their mechanical and electrical properties. Conditions during high temperature extrusion are optimized by adding Al or Ti as reducing agents, also with a view to the following cold forming. Current densities well above 10,000 A/sq cm at 15T are obtained by applying coarse-grained Nb powder and incorporating small quantities of Ta or Ti. The current carrying behavior of the conductors was determined as a function of the degree of mechanical deformation, the cold forming technique, and the heat treatment conditions. Wires containing an internal tin source as well as bundled assemblies for high current applications were manufactured. Long wires can be produced.

Preparation of titanium diboride powder

DOEpatents

Brynestad, Jorulf; Bamberger, Carlos E.

1985-01-01

Finely-divided titanium diboride or zirconium diboride powders are formed by reacting gaseous boron trichloride with a material selected from the group consisting of titanium powder, zirconium powder, titanium dichloride powder, titanium trichloride powder, and gaseous titanium trichloride.

Preparation of metal diboride powders

DOEpatents

Brynestad, J.; Bamberger, C.E.

Finely-divided titanium diboride or zirconium diboride powders are formed by reacting gaseous boron trichloride with a material selected from the group of consisting of titanium powder, zirconium powder, titanium dichloride powder, titanium trichloride powder, and gaseous titanium trichloride.

Self-Paced Tutorial Courses for Mineral Science - Metallurgy Departments. Final Progress Report (July 1975-August 1980).

ERIC Educational Resources Information Center

Twidwell, L. G.

Four courses in extractive metallurgy (Pyrometallurgy, Hydrometallurgy, Electrometallurgy; and Physical Chemistry of Iron and Steel) were prepared in a modular, self-paced format. Development of the course materials included: (1) preparation of course outlines by unit coordinators and advisory committees; (2) approval of course outlines (included…

Genome-wide association study of CSF biomarkers Abeta1-42, t-tau, and p-tau181p in the ADNI cohort.

PubMed

Kim, S; Swaminathan, S; Shen, L; Risacher, S L; Nho, K; Foroud, T; Shaw, L M; Trojanowski, J Q; Potkin, S G; Huentelman, M J; Craig, D W; DeChairo, B M; Aisen, P S; Petersen, R C; Weiner, M W; Saykin, A J

2011-01-04

CSF levels of Aβ1-42, t-tau, and p-tau181p are potential early diagnostic markers for probable Alzheimer disease (AD). The influence of genetic variation on these markers has been investigated for candidate genes but not on a genome-wide basis. We report a genome-wide association study (GWAS) of CSF biomarkers (Aβ1-42, t-tau, p-tau181p, p-tau181p/Aβ1-42, and t-tau/Aβ1-42). A total of 374 non-Hispanic Caucasian participants in the Alzheimer's Disease Neuroimaging Initiative cohort with quality-controlled CSF and genotype data were included in this analysis. The main effect of single nucleotide polymorphisms (SNPs) under an additive genetic model was assessed on each of 5 CSF biomarkers. The p values of all SNPs for each CSF biomarker were adjusted for multiple comparisons by the Bonferroni method. We focused on SNPs with corrected p<0.01 (uncorrected p<3.10×10(-8)) and secondarily examined SNPs with uncorrected p values less than 10(-5) to identify potential candidates. Four SNPs in the regions of the APOE, LOC100129500, TOMM40, and EPC2 genes reached genome-wide significance for associations with one or more CSF biomarkers. SNPs in CCDC134, ABCG2, SREBF2, and NFATC4, although not reaching genome-wide significance, were identified as potential candidates. In addition to known candidate genes, APOE, TOMM40, and one hypothetical gene LOC100129500 partially overlapping APOE; one novel gene, EPC2, and several other interesting genes were associated with CSF biomarkers that are related to AD. These findings, especially the new EPC2 results, require replication in independent cohorts.

Granulation of fine powder

DOE Office of Scientific and Technical Information (OSTI.GOV)

Chen, Ching-Fong

A mixture of fine powder including thorium oxide was converted to granulated powder by forming a first-green-body and heat treating the first-green-body at a high temperature to strengthen the first-green-body followed by granulation by crushing or milling the heat-treated first-green-body. The granulated powder was achieved by screening through a combination of sieves to achieve the desired granule size distribution. The granulated powder relies on the thermal bonding to maintain its shape and structure. The granulated powder contains no organic binder and can be stored in a radioactive or other extreme environment. The granulated powder was pressed and sintered to formmore » a dense compact with a higher density and more uniform pore size distribution.« less

A Guide for Planning Facilities for Occupational Preparation Programs in Metallurgy Technology. Interim Report. Research 28.

ERIC Educational Resources Information Center

German, Carl, Jr.

The major purpose of this guide is to elicit the information necessary for writing educational specifications for facilities to house technical education programs in metallurgy. It is organized in these parts: (1) Part I discusses the major purpose, underlying assumptions, recent instructional trends, and guiding principles utilized in the…

DOE Office of Scientific and Technical Information (OSTI.GOV)

Ivashchenko, R.K.; Fedorenko, V.K.; Kadryov, V.K.

In this work an attempt was made, by lowering the temperature in the detonation zone, decreasing the particle flight velocity, and employing starting powders in which the WC particle size 20-40 mum predominated, to obtain detonation-deposited VK20 alloy coatings approaching closely in structure and phase composition hard-metal composites produced by the powder metallurgy method.

Studies on the development of functional powder from citrus peel.

PubMed

Kang, H J; Chawla, S P; Jo, C; Kwon, J H; Byun, M W

2006-03-01

The suitability of citrus peels, generated as a by-product of the juice industry, as a source of antioxidants was investigated. Citrus peel powder was prepared by lyophilizing 70% ethanol extract from citrus peels. Extraction was carried out at room temperature (20 degrees C) for 72 h. The extract was subjected to gamma-irradiation treatment (20 kGy). The aqueous solutions of citrus peel powder were examined for color characteristics and antioxidant potential in terms of 1,1-diphenyl-2-picrylhydrazyl (DPPH) radical scavenging, beta-carotene bleaching and nitrite scavenging activities. There were significant changes in Hunter color values due to irradiation. The a*- and b*-values decreased due to radiation treatment. DPPH radical scavenging, beta-carotene bleaching and nitrite scavenging activities were not affected by irradiation treatment. Nitrite scavenging activity was the highest in the extract at pH 1.2 followed by pH 4.2 and 6.0. These functional properties of the aqueous solution were found to be stable in heat treatment. It could significantly improve oxidative stability of lipids in fish meat system. Based on these results there may be opportunities to use citrus peel powder as a functional component in the food processing industry with gamma irradiation treatment improving its color characteristics without adversely influencing the functional properties.

Multiple feed powder splitter

DOEpatents

Lewis, Gary K.; Less, Richard M.

2001-01-01

A device for providing uniform powder flow to the nozzles when creating solid structures using a solid fabrication system such as the directed light fabrication (DLF) process. In the DLF process, gas entrained powders are passed through the focal point of a moving high-power laser light which fuses the particles in the powder to a surface being built up in layers. The invention is a device providing uniform flow of gas entrained powders to the nozzles of the DLF system. The device comprises a series of modular splitters which are slidably interconnected and contain an integral flow control mechanism. The device can take the gas entrained powder from between one to four hoppers and split the flow into eight tubular lines which feed the powder delivery nozzles of the DLF system.

Multiple feed powder splitter

DOEpatents

Lewis, Gary K.; Less, Richard M.

2002-01-01

A device for providing uniform powder flow to the nozzles when creating solid structures using a solid fabrication system such as the directed light fabrication (DLF) process. In the DLF process, gas entrained powders are passed through the focal point of a moving high-power laser light which fuses the particles in the powder to a surface being built up in layers. The invention is a device providing uniform flow of gas entrained powders to the nozzles of the DLF system. The device comprises a series of modular splitters which are slidably interconnected and contain an integral flow control mechanism. The device can take the gas entrained powder from between one to four hoppers and split the flow into eight tubular lines which feed the powder delivery nozzles of the DLF system.

Effects of Precipitant and pH on Coprecipitation of Nanosized Co-Cr-V Alloy Powders

PubMed Central

Chen, Xiaoyu; Li, Yongxia; Huang, Lan; Zou, Dan; Wu, Enxi; Liu, Yanjun; Xie, Yuanyan; Yao, Rui; Liao, Songyi; Wang, Guangrong

2017-01-01

Nanosized Co-Cr-V alloy powders were synthesized via coprecipitation method. Effects of precipitants ((NH4)2C2O4·H2O and Na2CO3) and pH were investigated by X-ray diffraction (XRD), Zeta potential analyzer, thermogravimetry-differential scanning calorimetry (TG-DSC), inductively coupled plasma-atomic emission spectrometry (ICP-AES) and scanning electron microscopy (SEM). Co-Cr-V alloy powders were consisted of major face-centered cubic Co (fcc Co) and minor hexagonal close-packed Co (hcp Co). Grain sizes of precursors and Co-Cr-V alloy powders were increased with pH value (7–10) within the ranges of 3~39 and 39~66 nm, respectively. Rod-like or granular Co-Cr-V alloy particles were assembled by interconnected nanograins. At pH = 7, Na2CO3 precipitant was found to be beneficial to maintain the desirable composition of Co-Cr-V powders. It was also found that lower pH favors the maintenance of pre-designed composition, while grain coarsens at higher pH. Effects of variation for precipitant and pH on the morphology and composition of Co-Cr-V alloy powder were discussed in detail and relevant mechanism was further proposed. PMID:28934147

Fast surface crystallization of amorphous griseofulvin below T g.

PubMed

Zhu, Lei; Jona, Janan; Nagapudi, Karthik; Wu, Tian

2010-08-01

To study crystal growth rates of amorphous griseofulvin (GSF) below its glass transition temperature (T (g)) and the effect of surface crystallization on the overall crystallization kinetics of amorphous GSF. Amorphous GSF was generated by melt quenching. Surface and bulk crystal growth rates were determined using polarized light microscope. X-ray powder diffraction (XRPD) and Raman microscopy were used to identify the polymorph of the crystals. Crystallization kinetics of amorphous GSF powder stored at 40 degrees C (T (g)-48 degrees C) and room temperature (T (g)-66 degrees C) was monitored using XRPD. Crystal growth at the surface of amorphous GSF is 10- to 100-fold faster than that in the bulk. The surface crystal growth can be suppressed by an ultrathin gold coating. Below T (g), the crystallization of amorphous GSF powder was biphasic with a rapid initial crystallization stage dominated by the surface crystallization and a slow or suspended late stage controlled by the bulk crystallization. GSF exhibits the fastest surface crystallization kinetics among the known amorphous pharmaceutical solids. Well below T (g), surface crystallization dominated the overall crystallization kinetics of amorphous GSF powder. Thus, surface crystallization should be distinguished from bulk crystallization in studying, modeling and controlling the crystallization of amorphous solids.

21 CFR 520.1696a - Buffered penicillin powder, penicillin powder with buffered aqueous diluent.

Code of Federal Regulations, 2011 CFR

2011-04-01

... 21 Food and Drugs 6 2011-04-01 2011-04-01 false Buffered penicillin powder, penicillin powder with... FORM NEW ANIMAL DRUGS § 520.1696a Buffered penicillin powder, penicillin powder with buffered aqueous diluent. (a) Specifications. When reconstituted, each milliliter contains penicillin G procaine equivalent...

21 CFR 520.1696a - Buffered penicillin powder, penicillin powder with buffered aqueous diluent.

Code of Federal Regulations, 2010 CFR

2010-04-01

... 21 Food and Drugs 6 2010-04-01 2010-04-01 false Buffered penicillin powder, penicillin powder with... FORM NEW ANIMAL DRUGS § 520.1696a Buffered penicillin powder, penicillin powder with buffered aqueous diluent. (a) Specifications. When reconstituted, each milliliter contains penicillin G procaine equivalent...

21 CFR 520.1696a - Buffered penicillin powder, penicillin powder with buffered aqueous diluent.

Code of Federal Regulations, 2012 CFR

2012-04-01

... 21 Food and Drugs 6 2012-04-01 2012-04-01 false Buffered penicillin powder, penicillin powder with... FORM NEW ANIMAL DRUGS § 520.1696a Buffered penicillin powder, penicillin powder with buffered aqueous diluent. (a) Specifications. When reconstituted, each milliliter contains penicillin G procaine equivalent...

Daily Intake of Milk Powder and Risk of Celiac Disease in Early Childhood: A Nested Case-Control Study.

PubMed

Hård Af Segerstad, Elin M; Lee, Hye-Seung; Andrén Aronsson, Carin; Yang, Jimin; Uusitalo, Ulla; Sjöholm, Ingegerd; Rayner, Marilyn; Kurppa, Kalle; Virtanen, Suvi M; Norris, Jill M; Agardh, Daniel

2018-04-28

Milk powder and gluten are common components in Swedish infants' diets. Whereas large intakes of gluten early in life increases the risk of celiac disease in genetically at-risk Swedish children, no study has yet evaluated if intake of milk powder by 2 years of age is associated with celiac disease. A 1-to-3 nested case-control study, comprised of 207 celiac disease children and 621 controls matched for sex, birth year, and HLA genotype, was performed on a birth cohort of HLA-DR3-DQ2 and/or DR4-DQ8-positive children. Subjects were screened annually for celiac disease using tissue transglutaminase autoantibodies (tTGA). Three-day food records estimated the mean intake of milk powder at ages 6 months, 9 months, 12 months, 18 months, and 24 months. Conditional logistic regression calculated odds ratios (OR) at last intake prior to seroconversion of tTGA positivity, and for each time-point respectively and adjusted for having a first-degree relative with celiac disease and gluten intake. Intake of milk powder prior to seroconversion of tTGA positivity was not associated with celiac disease (OR = 1.00; 95% CI = 0.99, 1.03; p = 0.763). In conclusion, intake of milk powder in early childhood is not associated with celiac disease in genetically susceptible children.

Effect of imaging powder and CAD/CAM stone types on the marginal gap of zirconia crowns.

PubMed

Alghazzawi, Tariq F; Al-Samadani, Khalid H; Lemons, Jack; Liu, Perng-Ru; Essig, Milton E; Bartolucci, Alfred A; Janowski, Gregg M

2015-02-01

To compare the marginal gap using different types of die stones and titanium dies with and without powders for imaging. A melamine tooth was prepared and scanned using a laboratory 3-shape scanner to mill a polyurethane die, which was duplicated into different stones (Jade, Lean, CEREC) and titanium. Each die was sprayed with imaging powders (NP, IPS, Optispray, Vita) to form 15 groups. Ten of each combination of stone/titanium and imaging powders were used to mill crowns. A light-bodied impression material was injected into the intaglio surface of each crown and placed on the corresponding die. Each crown was removed, and the monophase material was injected to form a monophase die, which was cut into 8 sections. Digital images were captured using a stereomicroscope to measure marginal gap. Scanning electron microscopy was used to determine the particle size and shape of imaging powders and stones. Marginal gaps ranged from mean (standard deviation) 49.32 to 1.20 micrometers (3.97-42.41 μm). There was no statistical difference (P > .05) in the marginal gap by any combination of stone/titanium and imaging powders. All of the imaging powders had a similar size and rounded shape, whereas the surface of the stones showed different structures. When a laboratory 3-shape scanner is used, all imaging powders performed the same for scanning titanium abutments. However, there was no added value related to the use of imaging powder on die stone. It is recommended that the selection of stone for a master cast be based on the hysical properties. When a laboratory 3-shape scanner is used, the imaging powder is not required for scanning die stone. Whenever scanning titanium implant abutments, select the least expensive imaging powder. Copyright © 2015 American Dental Association. Published by Elsevier Inc. All rights reserved.

Study on effects of powder and flake chemistry and morphology on the properties of Al-Cu-Mg-X-X-X powder metallurgy advanced aluminum alloys

NASA Technical Reports Server (NTRS)

Meschter, P. J.; Lederich, R. J.; Oneal, J. E.

1986-01-01

A study was conducted: (1) to develop rapid solidification processed (RSP) dispersoid-containing Al-3Cu-2Li-1Mg-0.2Zr alloys as substitutes for titanium alloys and commercial 2XXX aluminum alloys for service to at least 150 C; and (2) to develop RSP Al-4Li-Cu-Mg-Zr alloys as substitutes for high-strength commercial 7XXX alloys in ambient-temperature applications. RSP Al-3Cu-2Li-1Mg-0.2Zr alloys have density-normalized yield stresses at 150 C up to 52% larger than that of 2124-T851 and up to 30% larger than that of Ti-6Al-4V. Strength at 150 C in these alloys is provided by thermally stable delta' (Al3Li), T1 (Al2LiCu), and S' (Al2CuMg) precipitates. Density-normalized yield stresses of RSP Al-3Cu-2Li-1Mg-0.2Zr alloys are up to 100% larger than that of 2124-T851 and equivalent to that of Al-8Fe-4Ce at 260 C. Strength in the RSP alloys at 260 C is provided by incoherent dispersoids and subboundary constituent particles such as T1 and S. The RSP alloys are attractive substitutes in less than or = 100-h exposures for 2xxx and Al-4Fe-Ce alloys up to 260 C and for titanium alloys up to 150 C. RSP Al-4Li-Cu-Mg-Zr alloys have ambient-temperature yield and ultimate tensile stresses similar to that of 7050-T7651, and are 14% less dense. RSP Al-4Li-0.5Cu-1.5Mg-0.2Zr has a 20% higher specific yield stress, 40% higher specific elastic modulus, and superior corrosion resistance compared to the properties of 7050-T7651. Strength in the Al-4Li-Cu-Mg-Zr alloy class is primarily provided by the substructure and delta' precipitates and is independent of Cu:Mg ratio. Improvements in fracture toughness and transverse-orientation properties in both alloy classes depend on improved melt practices to eliminate oxide inclusions which are incorporated into the consolidated forms.

A comparison of mango seed kernel powder, mango leaf powder and Manilkara zapota seed powder for decolorization of methylene blue dye and antimicrobial activity.

PubMed

Sundararaman, B; Muthuramu, K L

2016-11-01

The waste mango seed generated from mango pulp industry in India is a major problem in handling the waste and hence, conversion of mango seed kernel. Mango seeds were collected and processed for oil extraction. Decolorization of methylene blue was achieved by mango seed kernel powder, mango leaf powder and Manilkara zapota seed powder. Higher efficiency was attained in mango seed kernel powder when compared to mango leaf powder and Manilkara zapota seed powder. A 60 to 95 % of removal efficiency was achieved by varying concentration. Effect of pH, dye concentration, adsorbent dosage and temperature were studied. Mango seed kernel powder is a better option that can be used as an adsorbent for the removal of methylene blue and basic red dye from its aqueous solutions.

An analysis of un-dissolved powders of instant powdered soup by using ultrasonographic image

NASA Astrophysics Data System (ADS)

Kawaai, Yukinori; Kato, Kunihito; Yamamoto, Kazuhiko; Kasamatsu, Chinatsu

2008-11-01

Nowadays, there are many instant powdered soups around us. When we make instant powdered soup, sometimes we cannot dissolve powders perfectly. Food manufacturers want to improve this problem in order to make better products. Therefore, they have to measure the state and volume of un-dissolved powders. Earlier methods for analyzing removed the un-dissolved powders from the container, the state of the un-dissolved power was changed. Our research using ultrasonographic image can measure the state of un-dissolved powders with no change by taking cross sections of the soup. We then make 3D soup model from these cross sections of soup. Therefore we can observe the inside of soup that we do not have ever seen. We construct accurate 3D model. We can visualize the state and volume of un-dissolved powders with analyzing the 3D soup models.

Fabrication and properties of multifilamentary MgB 2 wires by in-situ powder-in-tube process

NASA Astrophysics Data System (ADS)

Wang, Q. Y.; Jiao, G. F.; Liu, G. Q.; Xiong, X. M.; Yan, S. C.; Zhang, P. X.; Sulpice, A.; Mossang, E.; Feng, Y.; Yan, G.

2010-11-01

We have fabricated the long TiC-doped MgB2 wires with 6 filaments by in-situ powder-in-tube method using Nb as the barrier and copper as the stabilizer. To improve the strength of wires, the Nb-core was used as the central filament. The transport engineering critical current density (Jce) of the samples sintered at different temperature were measured, which reaches 2.5 × 104 A/cm2 at 4.2 K, 5 T. 100 m MgB2 wires with different diameter were wound into coils and the transport critical current (Ic) of the coil were measured at 30 K in self-field. The Jce value 100 m coil achieves 1.1 × 104 A/cm2 in 1.2 mm wire. The reasons leading to the enhancement of high field Jce were discussed. The results show a good potential to fabricate high performance MgB2 wires and tapes at ambient pressure on an industrial scale.

Laminated composite of magnetic alloy powder and ceramic powder and process for making same

DOEpatents

Moorhead, Arthur J.; Kim, Hyoun-Ee

1999-01-01

A laminated composite structure of alternating metal powder layers, and layers formed of an inorganic bonding media powder, and a method for manufacturing same are discosed. The method includes the steps of assembling in a cavity alternating layers of a metal powder and an inorganic bonding media of a ceramic, glass, and glass-ceramic. Heat, with or without pressure, is applied to the alternating layers until the particles of the metal powder are sintered together and bonded into the laminated composite structure by the layers of sintered inorganic bonding media to form a strong composite structure. The method finds particular application in the manufacture of high performance magnets wherein the metal powder is a magnetic alloy powder.

Laminated composite of magnetic alloy powder and ceramic powder and process for making same

DOEpatents

Moorhead, A.J.; Kim, H.

1999-08-10

A laminated composite structure of alternating metal powder layers, and layers formed of an inorganic bonding media powder, and a method for manufacturing same are disclosed. The method includes the steps of assembling in a cavity alternating layers of a metal powder and an inorganic bonding media of a ceramic, glass, and glass-ceramic. Heat, with or without pressure, is applied to the alternating layers until the particles of the metal powder are sintered together and bonded into the laminated composite structure by the layers of sintered inorganic bonding media to form a strong composite structure. The method finds particular application in the manufacture of high performance magnets wherein the metal powder is a magnetic alloy powder. 9 figs.

High-Yield Preparation and Electrochemical Properties of Few-Layer MoS2 Nanosheets by Exfoliating Natural Molybdenite Powders Directly via a Coupled Ultrasonication-Milling Process.

PubMed

Dong, Huina; Chen, Deliang; Wang, Kai; Zhang, Rui

2016-12-01

Cost-effective and scalable preparation of two-dimensional (2D) molybdenum disulfide (MoS2) has been the bottleneck that limits their applications. This paper reports a novel coupled ultrasonication-milling (CUM) process to exfoliate natural molybdenite powders to achieve few-layer MoS2 (FL-MoS2) nanosheets in the solvent of N-methyl-2-pyrrolidone (NMP) with polyvinylpyrrolidone (PVP) molecules. The synergistic effect of ultrasonication and sand milling highly enhanced the exfoliation efficiency, and the precursor of natural molybdenite powders minimizes the synthetic cost of FL-MoS2 nanosheets. The exfoliation of natural molybdenite powders was conducted in a home-made CUM system, mainly consisting of an ultrasonic cell disruptor and a ceramic sand mill. The samples were characterized by X-ray diffraction, UV-vis spectra, Raman spectra, FT-IR, SEM, TEM, AFM, and N2 adsorption-desorption. The factors that influence the exfoliation in the CUM process, including the initial concentration of natural molybdenite powders (C in, 15-55 g L(-1)), ultrasonic power (P u, 200-350 W), rotation speed of sand mill (ω s, 1500-2250 r.p.m), exfoliation time (t ex, 0.5-6 h), and the molar ratio of PVP unit to MoS2 (R pm, 0-1), were systematically investigated. Under the optimal CUM conditions (i.e., C in = 45 g L(-1), P u = 280 W, ω s = 2250 r.p.m and R pm = 0.5), the yield at t ex = 6 h reaches 21.6 %, and the corresponding exfoliation rate is as high as 1.42 g L(-1) h(-1). The exfoliation efficiency of the CUM mode is much higher than that of either the ultrasonication (U) mode or the milling (M) mode. The synergistic mechanism and influencing rules of the CUM process in exfoliating natural molybdenite powders were elaborated. The as-obtained FL-MoS2 nanosheets have a high specific surface area of 924 m(2) g(-1) and show highly enhanced electrocatalytic performance in hydrogen evolution reaction and good electrochemical sensing property in

A Study of Mechanical Alloying of Metal Powders

DTIC Science & Technology

1981-05-01

UYON STAYt~ENT (d ida .... Approved for public release, distribution unlimited -𔄁. "’ I’ T PJIu TIO N IT A T EMT• ( ofe~ • e ao . m .. M•A 2-9, If...RELATIVE INTENSITY OF TIlE (1i1) BRAGG REFLECTION, 316 STAINLESS STEEL ,. 2.5 w/o Ti02 POWDER MILLED 98 HOURS AT 300 RPM...micrograph. 316.2.5 w/o Ti02 milled at 󈨋 300 RPM. Annealed 1.5 hours at 11000C. 30. Micrographs, iron - 10 w/o TiO2 milled 64 hours 72 at 300 RIh

Preparation of tris(8-hydroxyquinolinato)aluminum thin films by sputtering deposition using powder and pressed powder targets

NASA Astrophysics Data System (ADS)

Kawasaki, Hiroharu; Ohshima, Tamiko; Yagyu, Yoshihito; Ihara, Takeshi; Tanaka, Rei; Suda, Yoshiaki

2017-06-01

Tris(8-hydroxyquinolinato)aluminum (Alq3) thin films, for use in organic electroluminescence displays, were prepared by a sputtering deposition method using powder and pressed powder targets. Experimental results suggest that Alq3 thin films can be prepared using powder and pressed powder targets, although the films were amorphous. The surface color of the target after deposition became dark brown, and the Fourier transform infrared spectroscopy spectrum changed when using a pressed powder target. The deposition rate of the film using a powder target was higher than that using a pressed powder target. That may be because the electron and ion densities of the plasma generated using the powder target are higher than those when using pressed powder targets under the same deposition conditions. The properties of a thin film prepared using a powder target were almost the same as those of a film prepared using a pressed powder target.

Method for the preparation of ferrous low carbon porous material

DOEpatents

Miller, Curtis Jack

2014-05-27

A method for preparing a porous metal article using a powder metallurgy forming process is provided which eliminates the conventional steps associated with removing residual carbon. The method uses a feedstock that includes a ferrous metal powder and a polycarbonate binder. The polycarbonate binder can be removed by thermal decomposition after the metal article is formed without leaving a carbon residue.

Face powder poisoning

MedlinePlus

... poisoning URL of this page: //medlineplus.gov/ency/article/002700.htm Face powder poisoning To use the sharing features on this page, please enable JavaScript. Face powder poisoning occurs when someone swallows or ...

Influence of Ultrafine 2CaO·SiO₂ Powder on Hydration Properties of Reactive Powder Concrete.

PubMed

Sun, Hongfang; Li, Zishanshan; Memon, Shazim Ali; Zhang, Qiwu; Wang, Yaocheng; Liu, Bing; Xu, Weiting; Xing, Feng

2015-09-17

In this research, we assessed the influence of an ultrafine 2CaO·SiO₂ powder on the hydration properties of a reactive powder concrete system. The ultrafine powder was manufactured through chemical combustion method. The morphology of ultrafine powder and the development of hydration products in the cement paste prepared with ultrafine powder were investigated by scanning electron microscopy (SEM), mineralogical composition were determined by X-ray diffraction, while the heat release characteristics up to the age of 3 days were investigated by calorimetry. Moreover, the properties of cementitious system in fresh and hardened state (setting time, drying shrinkage, and compressive strength) with 5% ordinary Portland cement replaced by ultrafine powder were evaluated. From SEM micrographs, the particle size of ultrafine powder was found to be up to several hundred nanometers. The hydration product started formulating at the age of 3 days due to slow reacting nature of belitic 2CaO·SiO₂. The initial and final setting times were prolonged and no significant difference in drying shrinkage was observed when 5% ordinary Portland cement was replaced by ultrafine powder. Moreover, in comparison to control reactive powder concrete, the reactive powder concrete containing ultrafine powder showed improvement in compressive strength at and above 7 days of testing. Based on above, it can be concluded that the manufactured ultrafine 2CaO·SiO₂ powder has the potential to improve the performance of a reactive powder cementitious system.

JPRS Report, Science & Technology, Japan, Powder Metallurgy Technology

DTIC Science & Technology

1988-12-13

100 mO« 132 Hz i i i i -K H JL x’ c-p’an« (film) ! f • j 0 60 70 M TOO 90 1C Figure 3. Real and...necessary to develop a new manufacturing process focusing on the control of grain orientation. References 1. M . Okada, et al., Jpn. J. Appl. Phys. 27...Tc drops as the amount of Sr added is increased. References 1. M . Oda, et al., Jpn. J. Phys., 26, L804, 1987. 2. Z. Qi-rui, et al., Solid State

Aluminum base alloy powder metallurgy process and product

NASA Technical Reports Server (NTRS)

Paris, Henry G. (Inventor)

1986-01-01

A metallurgical method including cooling molten aluminum particles and consolidating resulting solidified particles into a multiparticle body, wherein the improvement comprises the provision of greater than 0.15% of a metal which diffuses in the aluminum solid state at a rate less than that of Mn. Aluminum containing greater than 0.15% of a metal which diffuses in the aluminum solid state at a rate less than that of Mn.

Dual-Alloy Disks are Formed by Powder Metallurgy

NASA Technical Reports Server (NTRS)

Harf, F. H.; Miner, R. V.; Kortovich, C. S.; Marder, J. M.

1982-01-01

High-performance disks have widely varying properties from hub to rim. Dual property disk is fabricated using two nickel-base alloys, AF-115 for rim and Rene 95 for hub. Dual-alloy fabrication may find applications in automobiles, earth-moving equipment, and energy conversion systems as well as aircraft powerplants. There is potential for such applications as shafts, gears, and blades.

Silicon nitride/silicon carbide composite powders

DOEpatents

Dunmead, Stephen D.; Weimer, Alan W.; Carroll, Daniel F.; Eisman, Glenn A.; Cochran, Gene A.; Susnitzky, David W.; Beaman, Donald R.; Nilsen, Kevin J.

1996-06-11

Prepare silicon nitride-silicon carbide composite powders by carbothermal reduction of crystalline silica powder, carbon powder and, optionally, crystalline silicon nitride powder. The crystalline silicon carbide portion of the composite powders has a mean number diameter less than about 700 nanometers and contains nitrogen. The composite powders may be used to prepare sintered ceramic bodies and self-reinforced silicon nitride ceramic bodies.

The Heterogeneous Photocatalytic Oxidation of Hydrocarbons on Platinized TiO2 Powders.

DTIC Science & Technology

1980-08-28

V W DUNN, K 0 WILBOURN NOO1-78-C-OS92 UCLASSIFIE D T - 10 ML I.’ fflfllfl~fflfllflfEEEEEEEEEl IIIII 1.1 . ILL 111L25 .4~I~ ( .6III MICROCOPY...Photocatalytic Oxidation of Hydrocarbons on Platinized TiO 2 Powders O by Ikuichiro Izumi, Wendell W. Dunn, Keith 0. Wilbourn , Fu-Ren F. Fan, and Allen J. Bard...Hydrocarbons on Platinized TiO 2 Powders. Ikuichiro Izumi, Wendell W. Dunn, Keith 0. Wilbourn , Fu-Ren F. Fan, and Allen J. Bard* Department of Chemistry, The

Experimental ammonia-free phosphate-bonded investments using Mg(H2PO4)2 solution.

PubMed

Takashiba, Shigeyuki; Zhang, Zutai; Tamaki, Yukimichi

2002-12-01

In our previous study, we investigated ammonia-free phosphate-bonded investments using Mg (H2PO4)2 powder. The purpose of the present study was to attempt usage of 50 wt% Mg (H2PO4)2 solution instead of powder. Magnesium oxide (MgO) was prepared as a binder and cristobalite was selected as a refractory. After arranging six kinds of experimental investments (A-F) with different cristobalite/MgO ratios, the fundamental properties of the dental investments were examined. The properties of the molds were influenced by the amount of MgO. Decreases in MgO showed lower mold strengths, longer setting time and larger setting expansion. According to XRD analysis, the peaks of MgH(PO4)3 x 3H2O newly formed, cristobalite and MgO were detected in the A set, but MgO peaks in F set were reduced. On the other hand, the surface of F was entirely covered by phosphorus. From these results, it was found that the usage of Mg(H2PO4)2 solution was possible for ammonia-free investments.

Evaluation of crystallization behavior on the surface of nifedipine solid dispersion powder using inverse gas chromatography.

PubMed

Miyanishi, Hideo; Nemoto, Takayuki; Mizuno, Masayasu; Mimura, Hisashi; Kitamura, Satoshi; Iwao, Yasunori; Noguchi, Shuji; Itai, Shigeru

2013-02-01

To investigate crystallization behavior on the surface of amorphous solid dispersion powder using inverse gas chromatography (IGC) and to predict the physical stability at temperatures below the glass transition temperature (T (g)). Amorphous solid dispersion powder was prepared by melt-quenching of a mixture of crystalline nifedipine and polyvinylpyrrolidon (PVP) K-30. IGC was conducted by injecting undecane (probe gas) and methane (reference gas) repeatedly to the solid dispersion at temperatures below T (g). Surface crystallization was evaluated by the retention volume change of undecane based on the observation that the surface of the solid dispersion with crystallized nifedipine gives an increased retention volume. On applying the retention volume change to the Hancock-Sharp equation, surface crystallization was found to follow a two-dimensional growth of nuclei mechanism. Estimation of the crystallization rates at temperatures far below T (g) using the Avrami-Erofeev equation and Arrhenius equation showed that, to maintain its quality for at least three years, the solid dispersion should be stored at -20°C (T (g) - 65°C). IGC can be used to evaluate crystallization behavior on the surface of a solid dispersion powder, and, unlike traditional techniques, can also predict the stability of the solid dispersion based on the surface crystallization behavior.

Synthesis of Al₂Ca Dispersoids by Powder Metallurgy Using a Mg-Al Alloy and CaO Particles.

PubMed

Fujita, Junji; Umeda, Junko; Kondoh, Katsuyoshi

2017-06-28

The elemental mixture of Mg-6 wt %Al-1 wt %Zn-0.3 wt %Mn (AZ61B) alloy powder and CaO particles was consolidated by an equal-channel angular bulk mechanical alloying (ECABMA) process to form a composite precursor. Subsequently, the precursor was subjected to a heat treatment to synthesize fine Al₂Ca particles via a solid-state reaction between the Mg-Al matrix and CaO additives. Scanning electron microscopy-energy-dispersive spectroscopy (SEM-EDS) and electron probe micro-analysis on the precursor indicated that 4.7-at % Al atoms formed a supersaturated solid solution in the α-Mg matrix. Transmission electron microscopy-EDS and X-ray diffraction analyses on the AZ61B composite precursor with 10-vol % CaO particles obtained by heat treatment confirmed that CaO additives were thermally decomposed in the Mg-Al alloy, and the solid-soluted Ca atoms diffused along the α-Mg grain boundaries. Al atoms also diffused to the grain boundaries because of attraction to the Ca atoms resulting from a strong reactivity between Al and Ca. As a result, needle-like (Mg,Al)₂Ca intermetallics were formed as intermediate precipitates in the initial reaction stage during the heat treatment. Finally, the precipitates were transformed into spherical Al₂Ca particles by the substitution of Al atoms for Mg atoms in (Mg,Al)₂Ca after a long heat treatment.

Silica powders for powder evacuated thermal insulating panel and method

DOEpatents

Harris, Michael T.; Basaran, Osman A.; Kollie, Thomas G.; Weaver, Fred J.

1996-01-01

A powder evacuated thermal insulating panel using generally spherical and porous silica particles of a median size less than about 100 nanometers in diameter, a pour packing density of about 0.4 to 0.6 g/cm.sup.3 and an external surface area in the range of about 90 to 600 m.sup.2/ g is described. The silica powders are prepared by reacting a tetraakyl silicate with ammonia and water in an alcohol solvent, distilling the solution after the reaction to remove the ammonia and recover the alcohol. The resulting aqueous slurry was dried, ball-milled, and dried again to provide the silica particles with defined internal and external porosity. The nanometer size and the large external surface area of the silica particles along with the internal and external porosity of the silica particles provide powder evacuated thermal insulating panels with significantly higher R-values than obtainable using previously known silica powders.

Silica powders for powder evacuated thermal insulating panel and method

DOEpatents

Harris, Michael T.; Basaran, Osman A.; Kollie, Thomas G.; Weaver, Fred J.

1994-01-01

A powder evacuated thermal insulating panel using generally spherical and porous silica particles of a median size less than about 100 nanometers in diameter, a pour packing density of about 0.4 to 0.6 g/cm.sup.3 and an external surface area in the range of about 90 to 600 m.sup.2 /g is described. The silica powders are prepared by reacting a tetraakyl silicate with ammonia and water in an alcohol solvent, distilling the solution after the reaction to remove the ammonia and recover the alcohol. The resulting aqueous slurry was dried, ball-milled, and dried again to provide the silica particles with defined internal and external porosity. The nanometer size and the large external surface area of the silica particles along with the internal and external porosity of the silica particles provide powder evacuated thermal insulating panels with significantly higher R-values than obtainable using previously known silica powders.

Silica powders for powder evacuated thermal insulating panel and method

DOEpatents

Harris, Michael T.; Basaran, Osman A.; Kollie, Thomas G.; Weaver, Fred J.

1995-01-01

A powder evacuated thermal insulating panel using generally spherical and porous silica particles of a median size less than about 100 nanometers in diameter, a pour packing density of about 0.4 to 0.6 g/cm.sup.3 and an external surface area in the range of about 90 to 600 m.sup.2/ g is described. The silica powders are prepared by reacting a tetraakyl silicate with ammonia and water in an alcohol solvent, distilling the solution after the reaction to remove the ammonia and recover the alcohol. The resulting aqueous slurry was dried, ball-milled, and dried again to provide the silica particles with defined internal and external porosity. The nanometer size and the large external surface area of the silica particles along with the internal and external porosity of the silica particles provide powder evacuated thermal insulating panels with significantly higher R-values than obtainable using previously known silica powders.

Silica powders for powder evacuated thermal insulating panel and method

DOEpatents

Harris, M.T.; Basaran, O.A.; Kollie, T.G.; Weaver, F.J.

1996-01-02

A powder evacuated thermal insulating panel using generally spherical and porous silica particles of a median size less than about 100 nanometers in diameter, a pour packing density of about 0.4 to 0.6 g/cm{sup 3} and an external surface area in the range of about 90 to 600 m{sup 2}/g is described. The silica powders are prepared by reacting a tetraalkyl silicate with ammonia and water in an alcohol solvent, distilling the solution after the reaction to remove the ammonia and recover the alcohol. The resulting aqueous slurry was dried, ball-milled, and dried again to provide the silica particles with defined internal and external porosity. The nanometer size and the large external surface area of the silica particles along with the internal and external porosity of the silica particles provide powder evacuated thermal insulating panels with significantly higher R-values than obtainable using previously known silica powders. 2 figs.

Precision powder feeder

DOEpatents

Schlienger, M. Eric; Schmale, David T.; Oliver, Michael S.

2001-07-10

A new class of precision powder feeders is disclosed. These feeders provide a precision flow of a wide range of powdered materials, while remaining robust against jamming or damage. These feeders can be precisely controlled by feedback mechanisms.

Evaluation of Genotoxicity and 28-day Oral Dose Toxicity on Freeze-dried Powder of Tenebrio molitor Larvae (Yellow Mealworm).

PubMed

Han, So-Ri; Yun, Eun-Young; Kim, Ji-Young; Hwang, Jae Sam; Jeong, Eun Ju; Moon, Kyoung-Sik

2014-06-01

The larval form of Tenebrio molitor (T. molitor) has been eaten in many countries and provides benefits as a new food source of protein for humans. However, no information exists regarding its safety for humans. The objective of the present study was to evaluate the genotoxicity and repeated dose oral toxicity of the freeze-dried powder of T. molitor larvae. The genotoxic potential was evaluated by a standard battery testing: bacterial reverse mutation test, in vitro chromosome aberration test, and in vivo micronucleus test. To assess the repeated dose toxicity, the powder was administered once daily by oral gavage to Sprague-Dawley (SD) rats at dose levels of 0, 300, 1000 and 3000 mg/kg/day for 28 days. The parameters which were applied to the study were mortality, clinical signs, body and organ weights, food consumption, ophthalmology, urinalysis, hematology, serum chemistry, gross findings and histopathologic examination. The freezedried powder of T. molitor larvae was not mutagenic or clastogenic based on results of in vitro and in vivo genotoxicity assays. Furthermore, no treatment-related changes or findings were observed in any parameters in rats after 28 days oral administration. In conclusion, the freeze-dried powder of T. molitor larvae was considered to be non-genotoxic and the NOAEL (No Observed Adverse Effect Level) was determined to be 3000 mg/kg/day in both sexes of SD rats under our experimental conditions.

Magnetic Properties of Amorphous Fe-Si-B Powder Cores Mixed with Pure Iron Powder

NASA Astrophysics Data System (ADS)

Kim, Hyeon-Jun; Nam, Seul Ki; Kim, Kyu-Sung; Yoon, Sung Chun; Sohn, Keun-Yong; Kim, Mi-Rae; Sul Song, Yong; Park, Won-Wook

2012-10-01

Amorphous Fe-Si-B alloy was prepared by melt-spinning, and then the ribbons were pulverized and ball-milled to make the amorphous powder of ˜25 µm in size. Subsequently those were mixed with pure iron powders with an average particle size of 3 µm, and 1.5 wt % water glass diluted by distilled water at the ratio of 1:2. The powder mixtures were cold compacted at 650 MPa in toroid die, and heat treated at 430-440 °C under a nitrogen atmosphere for 1 h and 30 min, respectively. The soft magnetic properties of powder core were investigated using a B-H analyzer and a flux meter at the frequency range of ˜100 kHz. The microstructure was observed using scanning electron microscope (SEM), and the density of the core was measured using the principle of Archimedes. Based on the experimental results, the amorphous powder mixed with pure iron powder showed the improved powder compactability, which resulted in the increased permeability and the reduced core loss.

Milk does not affect the bioavailability of cocoa powder flavonoid in healthy human.

PubMed

Roura, Elena; Andrés-Lacueva, Cristina; Estruch, Ramon; Mata-Bilbao, M Lourdes; Izquierdo-Pulido, Maria; Waterhouse, Andrew L; Lamuela-Raventós, Rosa M

2007-01-01

The beneficial effects of cocoa polyphenols depend on the amount consumed, their bioavailability and the biological activities of the formed conjugates. The food matrix is one the factors than can affect their bioavailability, but previous studies have concluded rather contradictory results about the effect of milk on the bioavailability of polyphenols. The objective was to evaluate the possible interaction of milk on the absorption of (-)-epicatechin ((-)-Ec) from cocoa powder in healthy humans. 21 volunteers received three interventions in a randomized crossover design with a 1-week interval (250 ml of whole milk (M-c) (control), 40 g of cocoa powder dissolved in 250 ml of whole milk (CC-M), and 40 g of cocoa powder dissolved with 250 ml of water (CC-W)). Quantification of (-)-Ec in plasma was determined by LC-MS/MS analysis prior to a solid-phase extraction procedure. 2 h after the intake of the two cocoa beverages, (-)-Ec-glucuronide was the only (-)-Ec metabolite detected, showing a mean (SD) plasma concentration of 330.44 nmol/l (156.1) and 273.7 nmol/l (138.42) for CC-W and CC-M, respectively (p = 0.076). Cocoa powder dissolved in milk as one of the most common ways of cocoa powder consumption seems to have a negative effect on the absorption of polyphenols; however, statistical analyses have shown that milk does not impair the bioavailability of polyphenols and thus their potential beneficial effect in chronic and degenerative disease prevention. (c) 2007 S. Karger AG, Basel

Needle-Free Inhalable Vaccine and Antibiotic Powder Aerosols

DTIC Science & Technology

2004-11-15

NEEDLE-FREE INHALABLE VACCINE AND ANTIBIOTIC POWDER AEROSOLS R. E. Sievers, J.L. Burger,, S. P. Cape, E.T.S. Huang, J.A. Best, J.A. Madsen and...currently valid OMB control number. 1. REPORT DATE 15 NOV 2004 2. REPORT TYPE N/A 3. DATES COVERED - 4. TITLE AND SUBTITLE Needle-Free Inhalable ...soluble drugs: naproxen, budesonide, betamethsone, amphotericin B, cyclosporin, DPPC Sugars: lactose, sucrose, trehalose , mannitol Polymers: PLA, PLGA

Preparation of superconductor precursor powders

DOEpatents

Bhattacharya, R.

1998-08-04

A process for the preparation of a precursor metallic powder composition for use in the subsequent formation of a superconductor. The process comprises the steps of providing an electrodeposition bath comprising an electrolyte medium and a cathode substrate electrode, and providing to the bath one or more soluble salts of one or more respective metals which are capable of exhibiting superconductor properties upon subsequent appropriate treatment. The bath is continually energized to cause the metallic and/or reduced particles formed at the electrode to drop as a powder from the electrode into the bath, and this powder, which is a precursor powder for superconductor production, is recovered from the bath for subsequent treatment. The process permits direct inclusion of all metals in the preparation of the precursor powder, and yields an amorphous product mixed on an atomic scale to thereby impart inherent high reactivity. Superconductors which can be formed from the precursor powder include pellet and powder-in-tube products. 7 figs.

Preparation of superconductor precursor powders

DOEpatents

Bhattacharya, Raghunath; Blaugher, Richard D.

1995-01-01

A process for the preparation of a precursor metallic powder composition for use in the subsequent formation of a superconductor. The process comprises the steps of providing an electrodeposition bath comprising an electrolyte medium and a cathode substrate electrode, and providing to the bath one or more soluble salts of one or more respective metals, such as nitrate salts of thallium, barium, calcium, and copper, which are capable of exhibiting superconductor properties upon subsequent appropriate treatment. The bath is continually energized to cause the metallic particles formed at the electrode to drop as a powder from the electrode into the bath, and this powder, which is a precursor powder for superconductor production, is recovered from the bath for subsequent treatment. The process permits direct inclusion of thallium in the preparation of the precursor powder, and yields an amorphous product mixed on an atomic scale to thereby impart inherent high reactivity. Superconductors which can be formed from the precursor powder include pellet and powder-in-tube products.

Preparation of superconductor precursor powders

DOEpatents

Bhattacharya, Raghunath

1998-01-01

A process for the preparation of a precursor metallic powder composition for use in the subsequent formation of a superconductor. The process comprises the steps of providing an electrodeposition bath comprising an electrolyte medium and a cathode substrate electrode, and providing to the bath one or more soluble salts of one or more respective metals which are capable of exhibiting superconductor properties upon subsequent appropriate treatment. The bath is continually energized to cause the metallic and/or reduced particles formed at the electrode to drop as a powder from the electrode into the bath, and this powder, which is a precursor powder for superconductor production, is recovered from the bath for subsequent treatment. The process permits direct inclusion of all metals in the preparation of the precursor powder, and yields an amorphous product mixed on an atomic scale to thereby impart inherent high reactivity. Superconductors which can be formed from the precursor powder include pellet and powder-in-tube products.

In vitro biodegradation testing of Mg-alloy EZK400 and manufacturing of implant prototypes using PM (powder metallurgy) methods.

PubMed

Wolff, M; Luczak, M; Schaper, J G; Wiese, B; Dahms, M; Ebel, T; Willumeit-Römer, R; Klassen, T

2018-09-01

The study is focussing towards Metal Injection Moulding (MIM) of Mg-alloys for biomedical implant applications. Especially the influence of the sintering processing necessary for the consolidation of the finished part is in focus of this study. In doing so, the chosen high strength EZK400 Mg-alloy powder material was sintered using different sintering support bottom plate materials to evaluate the possibility of iron impurity pick up during sintering. It can be shown that iron pick up took place from the steel bottom plate into the specimen. Despite the fact that a separating boron nitrite (BN) barrier layer was used and the Mg-Fe phase diagram is not predicting any significant solubility to each other. As a result of this study a new bottom plate material not harming the sintering and the biodegradation performance of the as sintered material, namely a carbon plate material, was found.

SINTERING METHOD

DOEpatents

Googin, J.M.

1963-11-01

Methods of making articles by powder metallurgy techniques are presented. An article is made by packing a metal powder into a desired shape, raising the temperature of the powder compact to a sintering temperature in the presence of a reducing gas, and alternately increasing and decreasing the pressure of the gas while the temperatume is being raised. The product has a greater density than can be achieved by sintering for the same length of time at a constant gas pressure. (AEC)

A DNA vaccine targeting p42.3 induces protective antitumor immunity via eliciting cytotoxic CD8+T lymphocytes in a murine melanoma model.

PubMed

Liu, Hu; Geng, Shuang; Feng, Congcong; Xie, Xiaoping; Wu, Bing; Chen, Xuan; Zou, Qiang; Wang, Shuang; Cui, Jiantao; Xing, Rui; Li, Wenmei; Lu, Youyong; Wang, Bin

2013-10-01

The p42.3 gene was recently identified and characterized as having tumor-specific and mitosis phase-dependent expression in many types of cancer. This suggested that p42.3 antigen could be used as a target for vaccines against cancers. In this study, we immunized C57BL/6 mice with a DNA vaccine encoding p42.3. We used intramuscular injection with electroporation, either before or after challenge with tumor B16F10 cells. Vaccination with pcDNA3-p42.3 induced some degree of antitumor effect both therapeutically and prophylactically, as evaluated by the inhibition of tumor growth and decrease in tumor weight. Immunized mice showed a high level of specific cytotoxic activity against the p42.3 protein in vivo and had activated CD8 T cells that secreted IFN-γ, perforin, and granzyme B in response to stimulation with the antigen in vitro. Thus, this study presents the DNA vaccination against novel tumor target p42.3 as a promising antitumor modality.

Semisolid Microstructural Evolution during Partial Remelting of a Bulk Alloy Prepared by Cold Pressing of the Ti-Al-2024Al Powder Mixture

PubMed Central

Qin, Yahong; Chen, Tijun; Wang, Yingjun; Zhang, Xuezheng; Li, Pubo

2016-01-01

A new method, powder thixoforming, has been proposed to fabricate an in situ Al3Tip/2024Al composite. During partial remelting, the microstructural evolution of the bulk alloy prepared by cold pressing of the Ti, Al, 2024Al powder mixture was investigated, and the formation mechanism of the Al3Ti particles produced by the reaction between the Ti powder and the Al alloy melt is also discussed in detail. The results indicate that the microstructural evolution of the 2024 alloy matrix can be divided into three stages: a rapid coarsening of the powder grains; a formation of primary α-Al particles surrounded with a continuous liquid film; and a slight coarsening of the primary α-Al particles. Simultaneously, a reaction layer of Al3Ti can be formed on the Ti powder surface when the bulk is heated for 10 min at 640 °C The thickness (X) of the reaction layer increases with the time according to the parabolic law of X=−0.43t2+4.21t+0.17. The stress generated in the reaction layer due to the volume dilatation can be calculated by using the equation σAl3Ti=−EAl3Ti6(1−υAl3Ti)t2Al3TitTi(1R−1R0). Comparing the obtained data with the results of the drip experiment, the reaction rate for the Ti powder and Al powder mixture is greater than that for the Ti plate and Al alloy mixture, respectively.

Influence of Ultrafine 2CaO·SiO2 Powder on Hydration Properties of Reactive Powder Concrete

PubMed Central

Sun, Hongfang; Li, Zishanshan; Memon, Shazim Ali; Zhang, Qiwu; Wang, Yaocheng; Liu, Bing; Xu, Weiting; Xing, Feng

2015-01-01