Weathering of a carbon nanotube/epoxy nanocomposite under UV light and in water bath: impact on abraded particles

NASA Astrophysics Data System (ADS)

Schlagenhauf, Lukas; Kianfar, Bahareh; Buerki-Thurnherr, Tina; Kuo, Yu-Ying; Wichser, Adrian; Nüesch, Frank; Wick, Peter; Wang, Jing

2015-11-01

Weathering processes can influence the surface properties of composites with incorporated nanoparticles. These changes may affect the release behavior of nanoparticles when an abrasion process is applied. Therefore, the influence of two different weathering processes, immersion in water and exposure to UV light, on the properties of abraded particles from a carbon nanotube (CNT)/epoxy nanocomposite was investigated. The investigation included the measurement of the weathering impact on the surface chemistry of the exposed samples, the particle size of abraded particles, the quantity of exposed CNTs in the respirable part of the abraded particles, and the toxicity of abraded particles, measured by in vitro toxicity tests using the THP-1 monocyte-derived macrophages. The results showed that weathering by immersion in water had no influence on the properties of abraded particles. The exposure to UV light caused a degradation of the epoxy on the surface, followed by delamination of an approx. 2.5 μm thick layer. An increased quantity of exposed CNTs in abraded particles was not found; on the contrary, longer UV exposure times decreased the released fraction of CNTs from 0.6% to 0.4%. The toxicity tests revealed that abraded particles from the nanocomposites did not induce additional acute cytotoxic effects compared to particles from the neat epoxy.Weathering processes can influence the surface properties of composites with incorporated nanoparticles. These changes may affect the release behavior of nanoparticles when an abrasion process is applied. Therefore, the influence of two different weathering processes, immersion in water and exposure to UV light, on the properties of abraded particles from a carbon nanotube (CNT)/epoxy nanocomposite was investigated. The investigation included the measurement of the weathering impact on the surface chemistry of the exposed samples, the particle size of abraded particles, the quantity of exposed CNTs in the respirable part of

Finite Element Simulation of Residual Stress Development in Thermally Sprayed Coatings

NASA Astrophysics Data System (ADS)

Elhoriny, Mohamed; Wenzelburger, Martin; Killinger, Andreas; Gadow, Rainer

2017-04-01

The coating buildup process of Al2O3/TiO2 ceramic powder deposited on stainless-steel substrate by atmospheric plasma spraying has been simulated by creating thermomechanical finite element models that utilize element death and birth techniques in ANSYS commercial software and self-developed codes. The simulation process starts with side-by-side deposition of coarse subparts of the ceramic layer until the entire coating is created. Simultaneously, the heat flow into the material, thermal deformation, and initial quenching stress are computed. The aim is to be able to predict—for the considered spray powder and substrate material—the development of residual stresses and to assess the risk of coating failure. The model allows the prediction of the heat flow, temperature profile, and residual stress development over time and position in the coating and substrate. The proposed models were successfully run and the results compared with actual residual stresses measured by the hole drilling method.

Effect of ceramic coating by aerosol deposition on abrasion resistance of a resin composite material.

PubMed

Taira, Yohsuke; Hatono, Hironori; Mizukane, Masahiro; Tokita, Masahiro; Atsuta, Mitsuru

2006-12-01

Aerosol deposition (AD coating) is a novel technique to coat solid substances with a ceramic film. The purpose of the present study was to investigate the effect of AD coating on abrasion resistance of a resin composite material. A 5-microm-thick aluminum oxide layer was created on the polymerized resin composite. The specimen was cyclically abraded using a toothbrush abrasion simulator for 100,000 cycles. Abraded surface was then measured with a profilometer to determine the average roughness (Ra) and maximum roughness (Rmax). It was found that abrasion cycling increased the Ra value of the No-AD-coating group, but decreased the Ra and Rmax values of the AD coating group. Moreover, the AD coating group showed significantly smaller Ra and Rmax values after 100,000 abrasion cycles as compared to the No-coating control group. Microscopic observation supported these findings. In conclusion, the resistance of the resin composite against toothbrush abrasion was improved by AD coating.

Nanohardness and Residual Stress in TiN Coatings.

PubMed

Hernández, Luis Carlos; Ponce, Luis; Fundora, Abel; López, Enrique; Pérez, Eduardo

2011-05-17

TiN films were prepared by the Cathodic arc evaporation deposition method under different negative substrate bias. AFM image analyses show that the growth mode of biased coatings changes from 3D island to lateral when the negative bias potential is increased. Nanohardness of the thin films was measured by nanoindentation, and residual stress was determined using Grazing incidence X ray diffraction. The maximum value of residual stress is reached at -100 V substrate bias coinciding with the biggest values of adhesion and nanohardness. Nanoindentation measurement proves that the force-depth curve shifts due to residual stress. The experimental results demonstrate that nanohardness is seriously affected by the residual stress.

Weathering of a carbon nanotube/epoxy nanocomposite under UV light and in water bath: impact on abraded particles.

PubMed

Schlagenhauf, Lukas; Kianfar, Bahareh; Buerki-Thurnherr, Tina; Kuo, Yu-Ying; Wichser, Adrian; Nüesch, Frank; Wick, Peter; Wang, Jing

2015-11-28

Weathering processes can influence the surface properties of composites with incorporated nanoparticles. These changes may affect the release behavior of nanoparticles when an abrasion process is applied. Therefore, the influence of two different weathering processes, immersion in water and exposure to UV light, on the properties of abraded particles from a carbon nanotube (CNT)/epoxy nanocomposite was investigated. The investigation included the measurement of the weathering impact on the surface chemistry of the exposed samples, the particle size of abraded particles, the quantity of exposed CNTs in the respirable part of the abraded particles, and the toxicity of abraded particles, measured by in vitro toxicity tests using the THP-1 monocyte-derived macrophages. The results showed that weathering by immersion in water had no influence on the properties of abraded particles. The exposure to UV light caused a degradation of the epoxy on the surface, followed by delamination of an approx. 2.5 μm thick layer. An increased quantity of exposed CNTs in abraded particles was not found; on the contrary, longer UV exposure times decreased the released fraction of CNTs from 0.6% to 0.4%. The toxicity tests revealed that abraded particles from the nanocomposites did not induce additional acute cytotoxic effects compared to particles from the neat epoxy.

Articulating spacers used in two-stage revision of infected hip and knee prostheses abrade with time.

PubMed

Fink, Bernd; Rechtenbach, Annett; Büchner, Hubert; Vogt, Sebastian; Hahn, Michael

2011-04-01

Articulating spacers used in two-stage revision surgery of infected prostheses have the potential to abrade and subsequently induce third-body wear of the new prosthesis. We asked whether particulate material abraded from spacers could be detected in the synovial membrane 6 weeks after implantation when the spacers were removed for the second stage of the revision. Sixteen hip spacers (cemented prosthesis stem articulating with a cement cup) and four knee spacers (customized mobile cement spacers) were explanted 6 weeks after implantation and the synovial membranes were removed at the same time. The membranes were examined by xray fluorescence spectroscopy, xray diffraction for the presence of abraded particles originating from the spacer material, and analyzed in a semiquantitative manner by inductively coupled plasma mass spectrometry. Histologic analyses also were performed. We found zirconium dioxide in substantial amounts in all samples, and in the specimens of the hip synovial lining, we detected particles that originated from the metal heads of the spacers. Histologically, zirconium oxide particles were seen in the synovial membrane of every spacer and bone cement particles in one knee and two hip spacers. The observations suggest cement spacers do abrade within 6 weeks. Given the presence of abrasion debris, we recommend total synovectomy and extensive lavage during the second-stage reimplantation surgery to minimize the number of abraded particles and any retained bacteria.

Evaluation of spatial and functional roughness parameters on air-abraded zirconia as a function of particle type and deposition pressure.

PubMed

Queiroz, José Renato Cavalcanti; Botelho, Marco Antonio; Sousa, Samira Albuquerque de; Martinelli, Antonio Eduardo; Özcan, Mutlu

2015-02-01

This study evaluated the spatial and functional roughness parameters on air-abraded zirconia as a function of particle type and deposition pressure. Polished zirconia blocks (Cercon, Degussa/Dentsply) (N=30) with dimensions of 5 × 4 × 4 mm3 were air abraded according to 2 factors: a) particle type - 30-μm silica-coated alumina (CoJet) or alumina particles (45 μm); b) deposition pressure (1.5, 2.5 and 4.5 bar). Roughness parameters (Sdr, Vi, Sci and Svi) were measured in an optical profilometer (Wyko NT 1100) at the center of the air-abraded area (301.3 × 229.2 μm). Two measurements were made for each parameter from each surface. The means of each group were analyzed by 2-way ANOVA followed by Tukey's adjustment test and Student's t-test (alpha = 0.05). Both the particle type (p < 0.05) and deposition pressure (p < 0.05) significantly affected the roughness parameters. Interaction terms were significant except for Sci and Svi. With the increase in pressure from 1.5 to 4.5 bar, Sdr (CoJet 1.5: 15.7 ± 0.2; CoJet 4.5: 26.6 ± 0.2; alumina 1.5: 14.7 ± 0.2; alumina 4.5: 24.4 ± 0.2) and Vi (CoJet 1.5: 0.66 ± 0.01; CoJet 4.5: 1.37 ± 0.07; alumina 1.5: 0.62 ± 0.02; alumina 4.5: 1.19 ± 0.02) parameters showed a significant increase with both alumina and CoJet particles. Mean Sci values (CoJet 1.5: 1.62 ± 0.01, CoJet 4.5: 1.49 ± 0.02; alumina 1.5: 1.6 ± 0.03; alumina 4.5: 1.42 ± 0.04) and SVi (CoJet 1.5: 0.98 ± 0.01, CoJet 4.5: 0.112 ± 0.01; alumina 1.5: 0.98 ± 0.01, alumina 4.5: 0.12 ± 0.01) decreased significantly (p < 0.05) with the increase in pressure from 1.5 to 4.5 bar. The pressure increase from 2.5 to 4.5 bar did not cause any significant difference (p > 0.05) in these parameters for either particle type. Considering roughness parameters for micromechanical retention and parameters for adsorption mechanisms of adhesion, zirconia surfaces presented better morphological features when air abraded with silica-coated alumina than alumina particles at

Ageing kinetics and strength of airborne-particle abraded 3Y-TZP ceramics.

PubMed

Cotič, Jasna; Jevnikar, Peter; Kocjan, Andraž

2017-07-01

The combined effects of alumina airborne-particle abrasion and prolonged in vitro ageing on the flexural strength of 3Y-TZP ceramic have been studied. The aim was to identify the different effects on the surface and subsurface regions that govern the performance of this popular bioceramic known for its susceptibility to low-temperature degradation (LTD). As-sintered or airborne-particle abraded 3Y-TZP discs were subjected to ageing at 134°C for up to 480h. Biaxial flexural strength was measured and the relative amount of monoclinic phase determined using X-ray diffraction. The transformed zone depth (TZD) was observed on cross-sections with scanning electron microscopy coupled with a focused ion beam. Segmented linear regression was used to analyze the flexural strength and TZD as functions of the ageing time. A two-step linear ageing kinetics was detected in airborne-particle abraded specimens, reflecting the different microstructures through which the LTD proceeds into the bulk. A 10μm thick altered zone under the abraded surface was involved in both the surface strengthening and the increased ageing resistance. When the zone was annihilated by the LTD, the strength of the ceramic specimens and the speed of LTD returned to the values measured before abrasion. Even at prolonged ageing times, the strength of abraded groups was not lower than that of as-sintered groups. Both the ageing kinetics and the flexural strength were prominently affected by airborne-particle abrasion, which altered the subsurface microstructure and phase composition. Airborne-particle abrasion was not harmful to the 3Y-TZP ceramics' stability. Copyright © 2017 The Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Conformational states of mutant M13 coat proteins are regulated by transmembrane residues.

PubMed

Li, Z; Glibowicka, M; Joensson, C; Deber, C M

1993-03-05

Mutational and structural analysis of the 28 viable bacteriophage M13 mutants obtained by randomized mutagenesis of the effective transmembrane (TM) segment of the 50-residue major coat (gene VIII) protein (residues 21-39) demonstrated that M13 coat protein functionality, as reflected by phage viability, is incompatible with an increase in Gly + beta-branched residue content in its TM core. SDS-polyacrylamide gel electrophoresis and circular dichroism spectroscopy performed in membrane environments on purified mutant coat proteins revealed that these proteins exist in a range of state(s), identified as helical monomers and dimers and polymeric (alpha-helical and/or beta-sheet) species, of which relative populations, and thermally induced conformational transitions, were dependent uniquely upon mutation type and locus. Mutations to relatively polar residues (e.g. G23D, Y24D, Y24H, A27E, I32T, and T36S) stabilized principally monomeric species, while mutants with decreased beta-branched content in the protein TM hydrophobic core (e.g. V29A, V30A, V31A, V31L, and V33A) displayed mainly dimeric species. Mutation of Ile37-->Thr within a "Sternberg-Gullick" consensus sequence of the coat protein TM segment led to a highly oligomerized/polymerized protein. The overall results suggest that TM residues in M13 coat protein are not universal components of a hydrophobic anchor segment per se, but are further selected (i) to impart conformational flexibility to the TM segment through helix destabilization and (ii) to retain the capacity to regulate protein-protein association and packing motifs within membranes.

Influences of Processing and Fatigue Cycling on Residual Stresses in a NiCrY-Coated Powder Metallurgy Disk Superalloy

NASA Astrophysics Data System (ADS)

Gabb, T. P.; Rogers, R. B.; Nesbitt, J. A.; Miller, R. A.; Puleo, B. J.; Johnson, D.; Telesman, J.; Draper, S. L.; Locci, I. E.

2017-11-01

Oxidation and corrosion can attack superalloy disk surfaces exposed to increasing operating temperatures in some turbine engine environments. Any potential protective coatings must also be resistant to harmful fatigue cracking during service. The objective of this study was to investigate how residual stresses evolve in one such coating. Fatigue specimens of a powder metallurgy-processed disk superalloy were coated with a NiCrY coating, shot peened, and then subjected to fatigue in air at room and high temperatures. The effects of this processing and fatigue cycling on axial residual stresses and other aspects of the coating were assessed. While shot peening did induce beneficial compressive residual stresses in the coating and substrate, these stresses relaxed in the coating with subsequent heating. Several cast alloys having compositions near the coating were subjected to thermal expansion and tensile stress relaxation tests to help explain this response of residual stresses in the coating. For the coated fatigue specimens, this response contributed to earlier cracking of the coating than for the uncoated surface during long intervals of cycling at 760 °C. Yet, substantial compressive residual stresses still remained in the substrate adjacent to the coating, which were sufficient to suppress fatigue cracking there. The coating continued to protect the substrate from hot corrosion pitting, even after fatigue cracks initiated in the coating.

Aerodynamic performance of conventional and advanced design labyrinth seals with solid-smooth abradable, and honeycomb lands. [gas turbine engines

NASA Technical Reports Server (NTRS)

Stocker, H. L.; Cox, D. M.; Holle, G. F.

1977-01-01

Labyrinth air seal static and dynamic performance was evaluated using solid, abradable, and honeycomb lands with standard and advanced seal designs. The effects on leakage of land surface roughness, abradable land porosity, rub grooves in abradable lands, and honeycomb land cell size and depth were studied using a standard labyrinth seal. The effects of rotation on the optimum seal knife pitch were also investigated. Selected geometric and aerodynamic parameters for an advanced seal design were evaluated to derive an optimized performance configuration. The rotational energy requirements were also measured to determine the inherent friction and pumping energy absorbed by the various seal knife and land configurations tested in order to properly assess the net seal system performance level. Results indicate that: (1) seal leakage can be significantly affected with honeycomb or abradable lands; (2) rotational energy absorption does not vary significantly with the use of a solid-smooth, an abradable, or a honeycomb land; and (3) optimization of an advanced lab seal design produced a configuration that had leakage 25% below a conventional stepped seal.

Study of Traverse Speed Effects on Residual Stress State and Cavitation Erosion Behavior of Arc-Sprayed Aluminum Bronze Coatings

NASA Astrophysics Data System (ADS)

Hauer, Michél; Henkel, Knuth Michael; Krebs, Sebastian; Kroemmer, Werner

2017-01-01

Within a research project regarding cavitation erosion-resistant coatings, arc spraying was used with different traverse speeds to influence heat transfer and the resulting residual stress state. The major reason for this study is the lack of knowledge concerning the influence of residual stress distribution on mechanical properties and coating adhesion, especially with respect to heterogeneous aluminum bronze alloys. The materials used for spray experiments were the highly cavitation erosion-resistant propeller alloys CuAl9Ni5Fe4Mn (Ni-Al-Bronze) and CuMn13Al8Fe3Ni2 (Mn-Al-Bronze). Analyses of cavitation erosion behavior were carried out to evaluate the suitability for use in marine environments. Further microstructural, chemical and mechanical analyses were realized to examine adhesive and cohesive coating properties. Residual stress distribution was measured by modified hole drilling method using electronic speckle pattern interferometry (ESPI). It was found that the highest traverse speed led to higher tensile residual stresses near the surface and less cavitation erosion resistance of the coatings. Moreover, high oxygen affinity of main alloying element aluminum was identified to severely influence the microstructures by the formation of large oxides and hence the coating properties. Overall, Mn-Al-Bronze coatings showed lower residual stresses, a more homogeneous pore and oxide distribution and less material loss by cavitation than Ni-Al-Bronze coatings.

Antifibrotic effect of dexamethasone/alginate-coated silicone sheet in the abraded middle ear mucosa.

PubMed

Jang, Chul Ho; Ahn, Seung Hyun; Kim, Geun Hyung

2016-12-01

Silicone sheet is a material which is commonly used in middle ear surgery to prevent the formation of adhesions between the tympanic membrane and the medial bony wall of the middle ear cavity. However, silicone sheet can induce a tight and hard fibrous capsule in the region of the stapes, and this is particularly common in cases of eustachian tube dysfunction. As a result of the fibrous encapsulation around the silicone sheet, postoperative aeration of the stapes can be interrupted causing poor hearing gain. In this study, we performed an in vitro and in vivo evaluation of the antifibrotic effects of a dexamethasone and alginate (Dx/alginate) coating on silicone sheet. The Dx/alginate-coated silicone sheets were fabricated using a plasma-treatment and coating method. The Dx/alginate-coated silicone sheets effectively limited in vitro fibroblast attachment and proliferation due to the controlled release of Dx, which can be modified by manipulation of the alginate coating. For the in-vivo evaluation, guinea pigs (albino, male, weighing 250g) were divided into two groups, with the control group (n=5) implanted with silicone sheet and the test group (n=5) receiving Dx/alginate-coated silicone sheet. Animals were sacrificed 3 weeks after implantation, and histological analysis was performed using hematoxylin and eosin (H&E) and immunohistochemical staining techniques. Dx/alginate-coated silicone sheets showed marked inhibition of fibrosis in both the in vitro and in vivo studies. Silicone sheet that incorporates a Dx/alginate coating can release Dx and inhibit fibrosis in the middle ear. This material could be utilized in middle ear surgery as a means of preserving proper aeration and hearing gain following ossiculoplasty. Copyright © 2016 Elsevier B.V. All rights reserved.

Crack prediction in EB-PVD thermal barrier coatings based on the simulation of residual stresses

NASA Astrophysics Data System (ADS)

Chen, J. W.; Zhao, Y.; Liu, S.; Zhang, Z. Z.; Ma, J.

2016-07-01

Thermal barrier coatings systems (TBCs) are widely used in the field of aerospace. The durability and insulating ability of TBCs are highly dependent on the residual stresses of top coatings, thus the investigation of the residual stresses is helpful to understand the failure mechanisms of TBCs. The simulation of residual stresses evolution in electron beam physical vapor deposition (EB-PVD) TBCs is described in this work. The interface morphology of TBCs subjected to cyclic heating and cooling is observed using scanning electron microscope (SEM). An interface model of TBCs is established based on thermal elastic-plastic finite method. Residual stress distributions in TBCs are obtained to reflect the influence of interfacial roughness. Both experimental and simulation results show that it is feasible to predict the crack location by stress analysis, which is crucial to failure prediction.

Comparative challenge model of Flavobacterium columnare using abraded and unabraded channel catfish, Ictalurus punctatus (Rafinesque).

PubMed

Bader, J A; Nusbaum, K E; Shoemaker, C A

2003-08-01

The early entry of the fish pathogen Flavobacterium columnare and enhancement by abrasion was studied in channel catfish, Ictalurus punctatus (Rafinesque), using the polymerase chain reaction and a species-specific primer set for a bacterial 16S rRNA gene product. Evaluations were conducted following an abrasion bath immersion challenge with F. columnare. Abrasion, a practice which has historically been used prior to bacterial challenge, had significant effects on the early entry of the pathogen and on cumulative percent survival (CPS). The FvpF1-FvpR1 primer set was useful in detecting the early entry of F. columnare in mucus, skin, gill, blood, liver and trunk kidney tissues in both abraded and unabraded fish following immersion challenge at 29 +/- 2 degrees C. Bacteria were detected earlier in all tissues in abraded fish, except in the trunk kidney. These differences were not significant, except in the case of blood. Mucus, skin and gill tissues were positive for F. columnare earliest regardless of treatment (after 5 min in abraded fish and after 15 min in unabraded fish). CPS following challenge with F. columnare was significantly affected by abrasion, which supports the use of abrasion for the F. columnare challenge model for channel catfish.

Alternative Gas Mixtures in Arc Spraying: A Chance to Improve Coating Properties and Residual Stress States

NASA Astrophysics Data System (ADS)

Hauer, Michél; Henkel, Knuth Michael; Krebs, Sebastian; Kroemmer, Werner

2018-01-01

The highly cavitation erosion-resistant propeller alloys CuAl9Ni5Fe4Mn (Ni-Al-Bronze) and CuMn13Al8Fe3Ni2 (Mn-Al-Bronze) were arc-sprayed using a mixture of nitrogen and 2% of hydrogen as atomizing gas and different traverse speeds. The objective was to identify the influences of the different spraying conditions, such as temperature regime and melting loss, on the resulting residual stress states and coating properties. Residual stresses were measured by the incremental hole-drilling method using ESPI. Temperature measurements were carried out by thermographic imaging. Microstructural, chemical and mechanical analyses were realized to examine adhesive and cohesive properties. Additionally, the cavitation erosion behavior was investigated to analyze cohesive coating properties. The spraying process itself was improved, which was apparent by mainly enhanced deposition efficiency and reduced surface temperatures. The amount of oxides and pores as well as the melting loss of alloying elements were reduced. Moreover, an increased cavitation erosion resistance and thus coating cohesion as well as less residual stresses were identified. The change in atomizing gas diminished the impact of the quenching stresses on the coating properties. In contrast, the adhesive strength, Young's moduli and partially the hardness were slightly reduced. With regard to materials, Ni-Al-Bronze revealed superior coating properties in comparison with Mn-Al-Bronze.

Research on residual stress inside Fe-Mn-Si shape memory alloy coating by laser cladding processing

NASA Astrophysics Data System (ADS)

Ju, Heng; Lin, Cheng-xin; Zhang, Jia-qi; Liu, Zhi-jie

2016-09-01

The stainless Fe-Mn-Si shape memory alloy (SMA) coating was prepared on the surface of AISI 304 stainless steel. The principal residual stress measured by the mechanical hole-drilling method indicates that the Fe-Mn-Si SMA cladding specimen possesses a lower residual stress compared with the 304 stainless steel cladding specimen. The mean stress values of the former and the latter on 10-mm-thick substrate are 4.751 MPa and 7.399 MPa, respectively. What's more, their deformation values on 2-mm-thick substrate are about 0° and 15°, respectively. Meanwhile, the variation trend and the value of the residual stress simulated by the ANSYS finite element software consist with experimental results. The X-ray diffraction (XRD) pattern shows ɛ-martensite exists in Fe-Mn-Si SMA coating, which verifies the mechanism of low residual stress. That's the γ→ɛ martensite phase transformation, which relaxes the residual stress of the specimen and reduces its deformation in the laser cladding processing.

Chem-Braze Abradable Seal Attachment to Aircraft Gas Turbine Compressor Components.

DTIC Science & Technology

1982-01-01

seals to compressor blade tip-shrouds using the im- proved Chem-Braze system compared to attachment with gold-nickel braze. The Chem-Braze system has been...used successfully to bond abradable seals to titanium ’ cobalt, nickel and iron base alloys; however, attempts to use Chem-Braze to bond seals to...attaching FELTMETALO seals to steel, titanium , and nickel-based alloys, and ICB bonding procedures were investigated for attaching seals to selected

Effect of dissolution/precipitation on the residual stress redistribution of plasma-sprayed hydroxyapatite coating on titanium substrate in simulated body fluid (SBF).

PubMed

Rakngarm Nimkerdphol, Achariya; Otsuka, Yuichi; Mutoh, Yoshiharu

2014-08-01

The residual stress distributions in hydroxyapatite (HAp) coating with and without mixed hydroxyapatite/titanium (HAp/Ti) bond coating on commercially pure Titanium substrate (cp-Ti) were evaluated by Raman piezo-spectroscopy analysis. The Raman shifted position 962cm(-1), which is the symmetrical stretching of surrounded oxygen atoms with phosphorous atom ( [Formula: see text] ), was referred to analyses of stress dependency. The piezo-spectroscopic coefficient, which is a Raman shift value per stress (cm(-1)/GPa), was fitted from the result of four-points bending test of rectangular HAp bar and as-sprayed HAp on Zn plate. The calculated values were 3.89cm(-1)/GPa for the former and 7.11cm(-1)/GPa for the latter. By using these calibrations, the compressive residual stress in HAp coating with HAp/Ti bond coating (HA-B) has been found to be distributed in the range of -137MPa to -75MPa. For the heat-treated HAp coating (HA-B-HT) specimen, the compressive residual stresses placed in the range of -40--22MPa. The changes in the values of residual stress of the HAp coating after immersion in SBF were also evaluated. The residual stress in HA-WB specimens tend to change from compressive to tensile after 30 days immersion. The HA-B-HT specimens exhibited similar behavior and reached to zero stress after the immersion. The mechanism of the changes in residual stress would be the effect of stress redistribution around melted calcium phosphate particles to remained HAp splats. Copyright © 2014 Elsevier Ltd. All rights reserved.

Residual Stresses in Thermal Barrier Coatings for a Cu-8Cr-4Nb Substrate System

NASA Technical Reports Server (NTRS)

Ghosn, Louis J.; Raj, Sai V.

2002-01-01

Analytical calculations were conducted to determine the thermal stresses developed in a coated copper-based alloy, Cu-8%(at.%)Cr-4%Nb (designated as GRCop-84), after plasma spraying and during heat-up in a simulated rocket engine environment. Finite element analyses were conducted for two coating systems consisting of a metallic top coat, a pure copper bond coat and the GRCop-84. The through thickness temperature variations were determined as a function of coating thickness for two metallic coatings, a Ni-17%(wt%)Cr-6%Al-0.5%Y alloy and a Ni-50%(at.%)Al alloy. The residual stresses after low-pressure plasma spraying of the NiCrAlY and NiAl coatings on GRCop-84 substrate were also evaluated. These analyses took into consideration a 50.8 mm copper bond coat and the effects of an interface coating roughness. The through the thickness thermal stresses developed in coated liners were also calculated after 15 minutes of exposure in a rocket environment with and without an interfacial roughness.

Raman Study of Uncoated and P-bn/sic-coated Hi-nicalon Reinforced Celsian Matrix Composites. Part 2; Residual Stress in the Fibers

NASA Technical Reports Server (NTRS)

Gouadec, Gwenael; Colomban, Philippe; Bansal, Narottam P.

2000-01-01

Band shifts on Raman spectra were used to assess, at a microscopic scale, the residual strain existing in Hi-Nicalon fibers reinforcing celsian matrix composites. Uncoated as well as p-BN/SiC- and p-B(Si)N/SiC-coated Hi-Nicalon fibers were used as the reinforcements. We unambiguously conclude that the fibers are in a state of compressive residual stress. Quantitative determination of the residual stress was made possible by taking into account the heating induced by laser probing and by using a reference line, of fixed wavenumber. We found fiber compressive residual stress values between 110 and 960 MPa depending on the fiber/matrix coating in the composite. A stress relaxation-like phenomenon was observed at the surface of p-BN/SiC-coated Hi-Nicalon fibers whereas the uncoated or p-B(Si)N/SiC-coated Hi-Nicalon fibers did not show any stress relaxation in the Celsian matrix composites.

Residual stress in thick low-pressure chemical-vapor deposited polycrystalline SiC coatings on Si substrates

NASA Astrophysics Data System (ADS)

Choi, D.; Shinavski, R. J.; Steffier, W. S.; Spearing, S. M.

2005-04-01

Residual stress in thick coatings of polycrystalline chemical-vapor deposited SiC on Si substrates is a key variable that must be controlled if SiC is to be used in microelectromechanical systems. Studies have been conducted to characterize the residual stress level as a function of deposition temperature, Si wafer and SiC coating thickness, and the ratios of methyltrichlorosilane to hydrogen and hydrogen chloride. Wafer curvature was used to monitor residual stress in combination with a laminated plate analysis. Compressive intrinsic (growth) stresses were measured with magnitudes in the range of 200-300MPa; however, these can be balanced with the tensile stress due to the thermal-expansion mismatch to leave near-zero stress at room temperature. The magnitude of the compressive intrinsic stress is consistent with previously reported values of surface stress in combination with the competition between grain-boundary energy and elastic strain energy.

Method of fabricating an abradable gas path seal

NASA Technical Reports Server (NTRS)

Bill, R. C.; Wisander, D. W. (Inventor)

1984-01-01

The thermal shock resistance of a ceramic layer is improved. The invention is particularly directed to an improved abradable lining that is deposited on shroud forming a gas path in turbomachinery. Improved thermal shock resistance of a shroud is effected through the deliberate introduction of benign cracks. These are microcracks which will not propagate appreciably upon exposure to the thermal shock environment in which a turbine seal must function. Laser surface fusion treatment is used to introduce these microcracks. The ceramic surface is laser scanned to form a continuous dense layer. As this layer cools and solidifies, shrinkage results in the formation of a very fine crack network. The presence of this deliberately introduced fine crack network precludes the formation of a catastrophic crack during thermal shock exposure.

Superabsorbent hydrogels coating increased degradation and decreased bound residues formation of carbendazim in soil.

PubMed

Yang, Yatian; Zhang, Sufen; Yang, Jingying; Bai, Chan; Tang, Shenghua; Ye, Qingfu; Wang, Haiyan

2018-07-15

The intensive use of pesticides has caused serious environmental pollution and ecological issues. Thus, it is imperative to explore an efficient way to minimize the pesticide residues and pollution. In the present study, we employed the superabsorbent hydrogels (SHs)-coated pesticide 14 C-carbendazim (H- 14 C-MBC) to investigate the fate of MBC in aerobic soils and to assess the soil microbial state during incubation. The results showed that after coating with SHs, MBC dissipation was improved significantly by 34.2-54.1% compared with that in the control (p<0.05), reducing the persistence of MBC in soil matrix. At 100d, the release of 14 C-CO 2 was enhanced by 68.0% and 46.6% in neutral loamy soil and basic saline soil, respectively, with respect to the control, resulting in more complete degradation and detoxification of MBC. Additionally, the bound residue in soils, which was associated with potential environmental risk and pollution, was reduced by 15.2% and 14.2%, respectively, compared with that in control soils. The microbial diversity of post-H- 14 C-MBC soil varied, and microbial composition and abundance remained different from the control, even with the refreshment of soil stability and fertility compared with the blank soil. These results demonstrate the environmental behavior of SHs-coated MBC in soils, and illustrate that SHs-encapsulated formulations would be a promising measure for reducing the soil-residue pollution and environmental risk of pesticides. Copyright © 2018 Elsevier B.V. All rights reserved.

Residual contamination and corrosion on electrochemically marked uranium

NASA Astrophysics Data System (ADS)

Seals, R. D.; Bullock, J. S.; Cristy, S. S.; Bennett, R. K.

Residual contamination and potential corrosion problems on uranium parts electrochemically marked with PHB-1 and PHB-1E electroetchants have been investigated using ion microprobe mass analysis (IMMA), scanning electron microscopy (SEM), and light microscopy (LM). The effectiveness of various solvent-cleaning sequences and the influence of the use of an abrasive cleaner were evaluated. The corrosion depths and chlorine distributions resulting from the electroetching process were determined. To meet the objective, the surfaces of uranium coupons, which had been processed according to production procedures for parts, i.e., machining, cleaning, marking, inspecting and coating with Shell Vitrea-29® oil, were studied. The greater surface wetting capability of the PHB-1E electroetchant solution relative to PHB-1 resulted in less localized corrosion at the point of attack which provided a more legible mark. Components of the electroetchants (aluminum, potassium and chromium) were found in the marked areas of both types of electroetched samples. Chromium, resulting from the corrosion inhibitor in the electroetchants, was found in the etched areas as well as on the coupon away from the electroetched areas. Depth profile data indicated that the major etching action (marking thickness) of the electroetchants penetrated to a depth of approximately 200 nm. Trace amounts of chlorine were present primarily within the first 65 nm of the marked surface. Comparison of the solvent rinsing sequences revealed that the most effective cleaning process included a degreaser, such as perchloroethylene, followed by a polar solvent, such as alcohol. Evaluation of the use of an abrasive cleaner on the electroetched areas indicates that this process removed residual contaminants, increased mark legibility and did not introduce significant residuals from the abrading material or cause significant surface damage.

Clinical Efficacy and Residue Depletion of 10% Enrofloxacin Enteric-Coated Granules in Pigs.

PubMed

Lei, Zhixin; Liu, Qianying; Yang, Bing; Xiong, Jincheng; Li, Kun; Ahmed, Saeed; Hong, Liping; Chen, Pin; He, Qigai; Cao, Jiyue

2017-01-01

A new, more palatable formulation of 10% enrofloxacin enteric-coated granules was investigated to evaluate the pharmacokinetic effect in plasma, the residue elimination in tissues and the clinical efficacy against Actinobacillus pleuropneumonia (APP) and Mycoplasam suis (MS) in pigs. In this study, the enrofloxacin concentrations in plasma and tissues were detected using high-performance liquid chromatography with phosphate buffer (pH = 3) and acetonitrile. The pharmacokinetics and elimination of enrofloxacin enteric-coated granules were performed after oral administration at a single dose of 10 mg/kg body weight (bw) and 5 mg/kg twice per day for 5 consecutive days, respectively. The in vivo antibacterial efficacy and clinical effectiveness of enrofloxacin enteric-coated granules against APP and MS were assayed at 2.5, 5, 10 mg/kg, compared with tiamulin (8 mg/kg) based on establishment of APP and MS infection models. 56 APP strains were selected and tested for in vitro antibacterial activity of enrofloxacin enteric-coated granules. The main parameters of elimination half-life (t 1/2β ), T max , and area under the curve (AUC) were 14.99 ± 4.19, 3.99 ± 0.10, and 38.93 ± 1.52 μg h/ml, respectively, revealing that the enrofloxacin concentration remained high and with a sustainable distribution in plasma. Moreover, the analysis on the evaluation of enrofloxacin and ciprofloxacin in muscle, fat, liver and kidney showed that the recovery were more than 84% recovery in accordance with the veterinary drug residue guidelines of United States pharmacopeia, and the withdrawal periods were 4.28, 3.81, 4.84, and 3.51 days, respectively, suggesting that the withdrawal period was 5 d after oral administration of 5 mg/kg twice per day. The optimal dosage of enrofloxacin enteric-coated granules against APP and MS was 5 mg/kg, with over 90% efficacy, which was significantly different ( p < 0.05) to the 2.5 mg/kg group, but not to the 10 mg/kg group or the positive control

Determination of elastic modulus and residual stress of plasma-sprayed tungsten coating on steel substrate

NASA Astrophysics Data System (ADS)

You, J. H.; Höschen, T.; Lindig, S.

2006-01-01

Plasma-sprayed tungsten, which is a candidate material for the first wall armour, shows a porous, heterogeneous microstructure. Due to its characteristic morphology, the properties are significantly different from those of its dense bulk material. Measurements of the elastic modulus of this coating have not been reported in the literature. In this work Young's modulus of highly porous plasma-sprayed tungsten coatings deposited on steel (F82H) substrates was measured. For the fabrication of the coating system the vacuum plasma-spray process was applied. Measurements were performed by means of three-point and four-point bending tests. The obtained modulus values ranged from 53 to 57 GPa. These values could be confirmed by the test result of a detached coating strip, which was 54 GPa. The applied methods produced consistent results regardless of testing configurations and specimen sizes. The errors were less than 1%. Residual stress of the coating was also estimated.

An Assessment of the Residual Stresses in Low Pressure Plasma Sprayed Coatings on an Advanced Copper Alloy

NASA Technical Reports Server (NTRS)

Raj, S. V.; Ghosn, L. J.; Agarwal, A.; Lachtrupp, T. P.

2002-01-01

Modeling studies were conducted on low pressure plasma sprayed (LPPS) NiAl top coat applied to an advanced Cu-8(at.%)Cr-4%Nb alloy (GRCop-84) substrate using Ni as a bond coat. A thermal analysis suggested that the NiAl and Ni top and bond coats, respectively, would provide adequate thermal protection to the GRCop-84 substrate in a rocket engine operating under high heat flux conditions. Residual stress measurements were conducted at different depths from the free surface on coated and uncoated GRCop-84 specimens by x-ray diffraction. These data are compared with theoretically estimated values assessed by a finite element analysis simulating the development of these stresses as the coated substrate cools down from the plasma spraying temperature to room temperature.

Effects of interface morphology and TGO thickness on residual stress of EB-PVD thermal barrier coatings

NASA Astrophysics Data System (ADS)

Chen, Jianwei; Zhao, Yang; Ma, Jian

2015-04-01

The residual stress of electron beam-physical vapor deposition (EB-PVD) thermal barrier coatings (TBC) is complex and difficult to be obtained. In this paper, the interface morphology of TBCs subjected to cyclic heating and cooling was observed by SEM. Based on the thermal elastic-plastic finite method, corresponding interface model of TBCs was established. The residual stress of EB-PVD TBCs with different interface morphologies and TGO thicknesses was calculated using the FE method without regard to the presence of cracks and defects. The result shows that the distribution of residual stress is significantly affected by the interface morphology, and the growth of TGO also has influence on the residual stress of TC and TGO.

Thermal input control and enhancement for laser based residual stress measurements using liquid temperature indicating coatings

DOEpatents

Pechersky, M.J.

1999-07-06

An improved method for measuring residual stress in a material is disclosed comprising the steps of applying a spot of temperature indicating coating to the surface to be studied, establishing a speckle pattern surrounds the spot of coating with a first laser then heating the spot of coating with a far infrared laser until the surface plastically deforms. Comparing the speckle patterns before and after deformation by subtracting one pattern from the other will produce a fringe pattern that serves as a visual and quantitative indication of the degree to which the plasticized surface responded to the stress during heating and enables calculation of the stress. 3 figs.

Thermal input control and enhancement for laser based residual stress measurements using liquid temperature indicating coatings

DOEpatents

Pechersky, Martin J.

1999-01-01

An improved method for measuring residual stress in a material comprising the steps of applying a spot of temperature indicating coating to the surface to be studied, establishing a speckle pattern surrounds the spot of coating with a first laser then heating the spot of coating with a far infrared laser until the surface plastically deforms. Comparing the speckle patterns before and after deformation by subtracting one pattern from the other will produce a fringe pattern that serves as a visual and quantitative indication of the degree to which the plasticized surface responded to the stress during heating and enables calculation of the stress.

Implementation and Development of the Incremental Hole Drilling Method for the Measurement of Residual Stress in Thermal Spray Coatings

NASA Astrophysics Data System (ADS)

Valente, T.; Bartuli, C.; Sebastiani, M.; Loreto, A.

2005-12-01

The experimental measurement of residual stresses originating within thick coatings deposited by thermal spray on solid substrates plays a role of fundamental relevance in the preliminary stages of coating design and process parameters optimization. The hole-drilling method is a versatile and widely used technique for the experimental determination of residual stress in the most superficial layers of a solid body. The consolidated procedure, however, can only be implemented for metallic bulk materials or for homogeneous, linear elastic, and isotropic materials. The main objective of the present investigation was to adapt the experimental method to the measurement of stress fields built up in ceramic coatings/metallic bonding layers structures manufactured by plasma spray deposition. A finite element calculation procedure was implemented to identify the calibration coefficients necessary to take into account the elastic modulus discontinuities that characterize the layered structure through its thickness. Experimental adjustments were then proposed to overcome problems related to the low thermal conductivity of the coatings. The number of calculation steps and experimental drilling steps were finally optimized.

Plasma sprayed hydroxyapatite coatings on titanium substrates. Part 1: Mechanical properties and residual stress levels.

PubMed

Tsui, Y C; Doyle, C; Clyne, T W

1998-11-01

Hydroxyapatite (HA) coatings have been sprayed on to substrates of Ti-6Al-4V, using a range of input power levels and plasma gas mixtures. Coatings have also been produced on substrates of mild steel and tungsten, in order to explore certain aspects of the mechanical behaviour of HA without the complication of yielding or creep in the substrate. Studies have been made of the phase constitution, porosity, degree of crystallinity, OH ion content, microstructure and surface roughness of the HA coatings. The Young's moduli in tension and in compression were evaluated by the cantilever beam bend test using a tungsten/HA composite beam. The flexural Young's modulus was determined using a free-standing deposit under the same test. Adhesion was characterised using the single-edge notch-bend test; this is considered superior to the tensile bond strength test in common use. Measured interfacial fracture energies were of the order 1-10 J m(-2). Stress levels were investigated using specimen curvature measurements in conjunction with a numerical process model. The quenching stress for HA was measured to be about 10-25 MPa and the residual stress level in HA coatings at room temperature are predicted to lie in the approximate range of 20-40 MPa (tensile). These residual stresses could be reduced in magnitude by maintaining the substrate at a low temperature (possibly below room temperature) during spraying and it may be worthwhile to explore this. Ideally, the HA coating should have low porosity, high cohesive strength, good adhesion to the substrate, a high degree of crystallinity and high chemical purity and phase stability. In practice, such combinations are rather difficult to achieve by just varying the spraying parameters.

Residual stresses and phase transformations in Ytterbium silicate environmental barrier coatings

NASA Astrophysics Data System (ADS)

Stolzenburg, Fabian

Due to their high melting temperature, low density, and good thermomechanical stability, silicon-based ceramics (SiC, Si3N4) are some of the most promising materials systems for high temperature structural applications in gas turbine engines. However, their silica surface layer reacts with water vapor contained in combustion environments. The resulting hydroxide layer volatilizes, leading to component recession. Environmental barrier coatings (EBCs) have been developed to shield the substrate from degradation. Next generation coatings for silicon-based ceramics based on ytterbium silicates have shown a promising combination of very low and good thermomechanical properties. The focus of this thesis is threefold: In the first part, phase transformations in plasma sprayed ytterbium silicates were investigated. Plasma sprayed materials are known to contain large amounts of amorphous material. Phase changes during the conversion from amorphous to crystalline materials were investigated as they have been known to lead to failure in many coatings. The second part of this work focused on measuring residual stresses in multilayer EBCs using synchrotron X-ray diffraction (XRD). Strains were resolved spatially, with probe sizes as small as 20 um. Stresses were calculated using mechanical properties of ytterbium silicates, determined with in-situ loading and heating experiments. In-situ and ex-situ heating experiments allowed for the study of changes in stress states that occur in these EBC materials during heating and cooling cycles. Lastly, the interaction of ytterbium silicates with low-melting environmental calcium-magnesium-aluminosilicate (CMAS) glasses was studied. Synchrotron XRD was used to study the influence of CMAS on the stress state in the coating, X-ray computed tomography was used to provide 3D images of coatings, and EDS and TEM analysis were used to study the interactions at the CMAS/ytterbium silicate interface in detail.

The effect of nano-structured alumina coating on resin-bond strength to zirconia ceramics.

PubMed

Jevnikar, Peter; Krnel, Kristoffer; Kocjan, Andraz; Funduk, Nenad; Kosmac, Tomaz

2010-07-01

The aim of this study was to functionalize the surface of yttria partially stabilized tetragonal zirconia ceramics (Y-TZP) with a nano-structured alumina coating to improve resin bonding. A total of 120 densely sintered disc-shaped specimens (15.5+/-0.03 mm in diameter and 2.6+/-0.03 mm thick) were produced from biomedical-grade TZ-3YB-E zirconia powder (Tosoh, Tokyo, Japan), randomly divided into three groups of 40 and subjected to the following surface treatments: AS - as-sintered; APA - airborne-particle abraded; POL - polished. Half of the discs in each group received an alumina coating that was fabricated by exploiting the hydrolysis of aluminium nitride (AlN) powder (groups AS-C, APA-C, POL-C). The coating was characterized using scanning electron microscopy (SEM), atomic force microscopy (AFM), and transmission electron microscopy (TEM). The shear-bond strength of the self-etching composite resin (RelyX Unicem, 3M ESPE, USA) was then studied for the coated and uncoated surfaces of the as-sintered, polished and airborne-particle abraded specimens before and after thermocycling (TC). The SEM/TEM analyses revealed that the application of an alumina coating to Y-TZP ceramics created a highly retentive surface for resin penetration. The coating showed good surface coverage and a uniform thickness of 240 nm. The resin-bond strength to the groups AS-C, APA-C, POL-C was significantly higher than to the groups AS, APA and POL, both before and after TC (p< or =0.05). During TC all the specimens in the POL and AS groups debonded spontaneously. In contrast, the TC did not affect the bond strength of the AS-C, POL-C and APA-C groups. A non-invasive method has been developed that significantly improves resin-bond strength to Y-TZP ceramics. After surface functionalization the bond survives thermocycling without reduction in strength. The method is relatively simple and has the potential to become an effective conditioning method for zirconia ceramics. Copyright 2010

In-situ composite formation of damage tolerant coatings utilizing laser

DOEpatents

Blue, Craig A [Knoxville, TN; Wong, Frank [Livermore, CA; Aprigliano, Louis F [Berlin, MD; Engleman, Peter G [Knoxville, TN; Peter, William H [Knoxville, TN; Rozgonyi, Tibor G [Golden, CO; Ozdemir, Levent [Golden, CO

2011-05-10

A coating steel component with a pattern of an iron based matrix with crystalline particles metallurgically bound to the surface of a steel substrate for use as disc cutters or other components with one or more abrading surfaces that can experience significant abrasive wear, high point loads, and large shear stresses during use. The coated component contains a pattern of features in the shape of freckles or stripes that are laser formed and fused to the steel substrate. The features can display an inner core that is harder than the steel substrate but generally softer than the matrix surrounding the core, providing toughness and wear resistance to the features. The features result from processing an amorphous alloy where the resulting matrix can be amorphous, partially devitrified or fully devitrified.

In-situ composite formation of damage tolerant coatings utilizing laser

DOEpatents

Blue, Craig A; Wong, Frank; Aprigliano, Louis F; Engleman, Peter G; Rozgonyi, Tibor G; Ozdemir, Levent

2014-03-18

A coating steel component with a pattern of an iron based matrix with crystalline particles metallurgically bound to the surface of a steel substrate for use as disc cutters or other components with one or more abrading surfaces that can experience significant abrasive wear, high point loads, and large shear stresses during use. The coated component contains a pattern of features in the shape of freckles or stripes that are laser formed and fused to the steel substrate. The features can display an inner core that is harder than the steel substrate but generally softer than the matrix surrounding the core, providing toughness and wear resistance to the features. The features result from processing an amorphous alloy where the resulting matrix can be amorphous, partially devitrified or fully devitrified.

In-situ composite formation of damage tolerant coatings utilizing laser

DOEpatents

Blue, Craig A.; Wong, Frank; Aprigliano, Louis F.; Engleman, Peter G.; Peter, William H.; Rozgonyi, Tibor G.; Ozdemir, Levent

2016-05-24

A coating steel component with a pattern of an iron based matrix with crystalline particles metallurgically bound to the surface of a steel substrate for use as disc cutters or other components with one or more abrading surfaces that can experience significant abrasive wear, high point loads, and large shear stresses during use. The coated component contains a pattern of features in the shape of freckles or stripes that are laser formed and fused to the steel substrate. The features can display an inner core that is harder than the steel substrate but generally softer than the matrix surrounding the core, providing toughness and wear resistance to the features. The features result from processing an amorphous alloy where the resulting matrix can be amorphous, partially devitrified or fully devitrified.

Shear bond strength between an indirect composite layering material and feldspathic porcelain-coated zirconia ceramics.

PubMed

Fushiki, Ryosuke; Komine, Futoshi; Blatz, Markus B; Koizuka, Mai; Taguchi, Kohei; Matsumura, Hideo

2012-10-01

This study aims to evaluate the effect of both feldspathic porcelain coating of zirconia frameworks and priming agents on shear bond strength between an indirect composite material and zirconia frameworks. A total of 462 airborne-particle-abraded zirconia disks were divided into three groups: untreated disks (ZR-AB), airborne-particle-abraded zirconia disks coated with feldspathic porcelain, (ZR-PO-AB), and hydrofluoric acid-etched zirconia disks coated with feldspathic porcelain (ZR-PO-HF). Indirect composite (Estenia C&B) was bonded to zirconia specimens with no (CON) or one of four priming agents--Clearfil Photo Bond (CPB), Clearfil Photo Bond with Clearfil Porcelain Bond Activator (CPB + activator), Estenia Opaque primer, or Porcelain Liner M Liquid B (PLB)--with or without an opaque material (Estenia C&B Opaque). All specimens were tested for shear bond strength before and after 20,000 thermocycles. The Steel-Dwass test and Mann-Whitney U test were used to compare shear bond strength. In ZR-AB specimens, the initial bond strength of the CPB and CPB + Activator groups was significantly higher as compared with the other three groups (P < 0.05), whereas the PLB and CPB + Activator groups had the highest pre- and post-thermocycling bond strengths in ZR-PO-AB and ZR-PO-HF specimens. Among CON disks without opaque material, bond strength was significantly lower in ZR-AB specimens than in ZR-PO-AB and ZR-PO-HF specimens (P < 0.05). Feldspathic porcelain coating of a Katana zirconia framework enhanced the bond strength of Estenia C&B indirect composite to zirconia independent of surface treatment. The use of a silane coupling agent and opaque material yields durable bond strength between the indirect composite and feldspathic-porcelain-coated zirconia. The results of the present study suggest that feldspathic porcelain coating of zirconia frameworks is an effective method to obtain clinically acceptable bond strengths of a layering indirect

Effect of heat treatment on residual stress and wear behaviors of the TiNi/Ti2Ni based laser cladding composite coatings

NASA Astrophysics Data System (ADS)

Tao, Yang-Feng; Li, Jun; Lv, Ying-Hao; Hu, Lie-Feng

2017-12-01

The TiNi/Ti2Ni based composite coatings reinforced by TiC and TiB2 were prepared on Ti6Al4V at different circumstance temperatures (25 °C, 400 °C, 600 °C, and 800 °C) by laser cladding, then were preserved for 3 h. Macromorphologies and microstructures of the coatings were examined through an optical microscope (OM), an X-ray diffractometer (XRD), a scanning electron microscope (SEM), and an energy dispersive spectrometer (EDS). Residual stresses along the depth direction of the coatings were measured by the nanoindentation method, and wear behaviors of the coatings were also investigated using an ultra-functional wear testing machine. Results showed that the coatings were mainly composed of TiNi/Ti2Ni as the matrix and TiC/TiB2 as the reinforcement. A small amount of Cr2Ti was formed in the coatings prepared at 400 °C and 600 °C. Besides that, Ti3Al was also observed in the coating prepared at 800 °C. The tensile stress existed in the coatings prepared at 25 °C, 400 °C and 600 °C when the coating prepared at 800 °C was regarded as the stress-free reference. The average residual stress in the surface of coating prepared at 25 °C reached the largest value of about 2.79 GPa and presented a decreasing tendency with increasing the circumstance temperature (1.03 GPa at 400 °C, 0.52 GPa at 600 °C, and 0 GPa at 800 °C). It revealed that the rise in circumstance temperature contributed to the reduction in cracking susceptibility in the laser cladding coating. However, the wear volumes of the coatings were increased with increasing the circumstance temperature (0.1912 mm3 at 25 °C, 0.2828 mm3 at 400 °C, 0.3732 mm3 at 600 °C, and 0.6073 mm3 at 800 °C) due to the weakening in strain-hardening effect and the reduction in reinforcement density. The wear mechanism of the coatings was transformed from the single brittle-debonding into the combination of micro-cutting and brittle-debonding when the circumstance temperature was changed from room temperature to

Production of reactive oxygen species from abraded silicates. Implications for the reactivity of the Martian soil

NASA Astrophysics Data System (ADS)

Bak, Ebbe N.; Zafirov, Kaloyan; Merrison, Jonathan P.; Jensen, Svend J. Knak; Nørnberg, Per; Gunnlaugsson, Haraldur P.; Finster, Kai

2017-09-01

The results of the Labeled Release and the Gas Exchange experiments conducted on Mars by the Viking Landers show that compounds in the Martian soil can cause oxidation of organics and a release of oxygen in the presence of water. Several sources have been proposed for the oxidizing compounds, but none has been validated in situ and the cause of the observed oxidation has not been resolved. In this study, laboratory simulations of saltation were conducted to examine if and under which conditions wind abrasion of silicates, a process that is common on the Martian surface, can give rise to oxidants in the form of hydrogen peroxide (H2O2) and hydroxyl radicals (ṡOH). We found that silicate samples abraded in simulated Martian atmospheres gave rise to a significant production of H2O2 and ṡOH upon contact with water. Our experiments demonstrated that abraded silicates could lead to a production of H2O2 facilitated by atmospheric O2 and inhibited by carbon dioxide. Furthermore, during simulated saltation the silicate particles became triboelectrically charged and at pressures similar to the Martian surface pressure we observed glow discharges. Electrical discharges can cause dissociation of CO2 and through subsequent reactions lead to a production of H2O2. These results indicate that the reactions linked to electrical discharges are the dominant source of H2O2 during saltation of silicates in a simulated Martian atmosphere, given the low pressure and the relatively high concentration of CO2. Our experiments provide evidence that wind driven abrasion could enhance the reactivity of the Martian soil and thereby could have contributed to the oxidation of organic compounds and the O2 release observed in the Labeled Release and the Gas Exchange experiments. Furthermore, the release of H2O2 and ṡOH from abraded silicates could have a negative effect on the persistence of organic compounds in the Martian soil and the habitability of the Martian surface.

Sea water Corrosion of Nickel based Plasma Spray Coating

NASA Astrophysics Data System (ADS)

Parida, M.; Nanda, S. P.; Bhuyan, S. K.; Mishra, S. C.

2018-03-01

Different types of erosion resistant coatings are applied/deposited on aero components, depending on the operating/working temperatures. Nickel based coating are applied on the air craft (compressor) components, which can sustain up to working temperature of 650°C. In the present investigation, to improve the compatibility between substrate (i.e. the machine component) and the top coat, application of bond coat is there. The application of Nickel based coating by thermal plasma spray technique has proven to be a satisfactory means of producing acceptable sealing surface with excellent abradability. Before the corrosion study, coated sample is subjected to hardness, thickness and porosity testing. Hence the result is being evaluated. The corrosion behavior of coating was studied by sea water immersion with a time period of 16 weeks. It is observed that, up to 9 weeks increase in weight of coating occurs in a sharp trend and then takes a decreasing trend. The weight gain of the samples has varied from 37.23% (with one week immersion in sea water) to a maximum of about 64.36% for six weeks immersion. Coating morphology and composition analysis of the coatings are studied using SEM and EDS. This behavior shows adsorption/deposition of the foreign particles with polygonal shape on the coating surface by sea water interaction. Foreign particles with polygonal shape deposited on the coating and with increase in immersion/treatment time, washing out of the deposited materials starts, which reflects the decreasing trend of weight gain of the specimen.

Flow accelerated organic coating degradation

NASA Astrophysics Data System (ADS)

Zhou, Qixin

Applying organic coatings is a common and the most cost effective way to protect metallic objects and structures from corrosion. Water entry into coating-metal interface is usually the main cause for the deterioration of organic coatings, which leads to coating delamination and underfilm corrosion. Recently, flowing fluids over sample surface have received attention due to their capability to accelerate material degradation. A plethora of works has focused on the flow induced metal corrosion, while few studies have investigated the flow accelerated organic coating degradation. Flowing fluids above coating surface affect corrosion by enhancing the water transport and abrading the surface due to fluid shear. Hence, it is of great importance to understand the influence of flowing fluids on the degradation of corrosion protective organic coatings. In this study, a pigmented marine coating and several clear coatings were exposed to the laminar flow and stationary immersion. The laminar flow was pressure driven and confined in a flow channel. A 3.5 wt% sodium chloride solution and pure water was employed as the working fluid with a variety of flow rates. The corrosion protective properties of organic coatings were monitored inline by Electrochemical Impedance Spectroscopy (EIS) measurement. Equivalent circuit models were employed to interpret the EIS spectra. The time evolution of coating resistance and capacitance obtained from the model was studied to demonstrate the coating degradation. Thickness, gloss, and other topography characterizations were conducted to facilitate the assessment of the corrosion. The working fluids were characterized by Fourier Transform Infrared Spectrometer (FTIR) and conductivity measurement. The influence of flow rate, fluid shear, fluid composition, and other effects in the coating degradation were investigated. We conclude that flowing fluid on the coating surface accelerates the transport of water, oxygen, and ions into the coating, as

An inter-residue network model to identify mutational-constrained regions on the Ebola coat glycoprotein

PubMed Central

Quinlan, Devin S.; Raman, Rahul; Tharakaraman, Kannan; Subramanian, Vidya; del Hierro, Gabriella; Sasisekharan, Ram

2017-01-01

Recently, progress has been made in the development of vaccines and monoclonal antibody cocktails that target the Ebola coat glycoprotein (GP). Based on the mutation rates for Ebola virus given its natural sequence evolution, these treatment strategies are likely to impose additional selection pressure to drive acquisition of mutations in GP that escape neutralization. Given the high degree of sequence conservation among GP of Ebola viruses, it would be challenging to determine the propensity of acquiring mutations in response to vaccine or treatment with one or a cocktail of monoclonal antibodies. In this study, we analyzed the mutability of each residue using an approach that captures the structural constraints on mutability based on the extent of its inter-residue interaction network within the three-dimensional structure of the trimeric GP. This analysis showed two distinct clusters of highly networked residues along the GP1-GP2 interface, part of which overlapped with epitope surfaces of known neutralizing antibodies. This network approach also permitted us to identify additional residues in the network of the known hotspot residues of different anti-Ebola antibodies that would impact antibody-epitope interactions. PMID:28397835

Investigations on antibody binding to a micro-cantilever coated with a BAM pesticide residue.

PubMed

Bache, Michael; Taboryski, Rafael; Schmid, Silvan; Aamand, Jens; Jakobsen, Mogens Havsteen

2011-05-16

The attachment of an antibody to an antigen-coated cantilever has been investigated by repeated experiments, using a cantilever-based detection system by Cantion A/S. The stress induced by the binding of a pesticide residue BAM (2,6 dichlorobenzamide) immobilized on a cantilever surface to anti-BAM antibody is measured using the CantiLab4© system from Cantion A/S with four gold-coated cantilevers and piezo resistive readout. The detection mechanism is in principle label-free, but fluorescent-marked antibodies have been used to subsequently verify the binding on the cantilever surface. The bending and increase in mass of each cantilever has also been investigated using a light interferometer and a Doppler Vibrometer. The system has been analyzed during repeated measurements to investigate whether the CantiLab4© system is a suited platform for a pesticide assay system.

Selection criteria for wear resistant powder coatings under extreme erosive wear conditions

NASA Astrophysics Data System (ADS)

Kulu, P.; Pihl, T.

2002-12-01

Wear-resistant thermal spray coatings for sliding wear are hard but brittle (such as carbide and oxide based coatings), which makes them useless under impact loading conditions and sensitive to fatigue. Under extreme conditions of erosive wear (impact loading, high hardness of abrasives, and high velocity of abradant particles), composite coatings ensure optimal properties of hardness and toughness. The article describes tungsten carbide-cobalt (WC-Co) systems and self-fluxing alloys, containing tungsten carbide based hardmetal particles [NiCrSiB-(WC-Co)] deposited by the detonation gun, continuous detonation spraying, and spray fusion processes. Different powder compositions and processes were studied, and the effect of the coating structure and wear parameters on the wear resistance of coatings are evaluated. The dependence of the wear resistance of sprayed and fused coatings on their hardness is discussed, and hardness criteria for coating selection are proposed. The so-called “double cemented” structure of WC-Co based hardmetal or metal matrix composite coatings, as compared with a simple cobalt matrix containing particles of WC, was found optimal. Structural criteria for coating selection are provided. To assist the end user in selecting an optimal deposition method and materials, coating selection diagrams of wear resistance versus hardness are given. This paper also discusses the cost-effectiveness of coatings in the application areas that are more sensitive to cost, and composite coatings based on recycled materials are offered.

Lateral gradients of phases, residual stress and hardness in a laser heated Ti0.52Al0.48N coating on hard metal

PubMed Central

Bartosik, M.; Daniel, R.; Zhang, Z.; Deluca, M.; Ecker, W.; Stefenelli, M.; Klaus, M.; Genzel, C.; Mitterer, C.; Keckes, J.

2012-01-01

The influence of a local thermal treatment on the properties of Ti–Al–N coatings is not understood. In the present work, a Ti0.52Al0.48N coating on a WC–Co substrate was heated with a diode laser up to 900 °C for 30 s and radially symmetric lateral gradients of phases, residual stress and hardness were characterized ex-situ using position-resolved synchrotron X-ray diffraction, Raman spectroscopy, transmission electron microscopy and nanoindentation. The results reveal (i) a residual stress relaxation at the edge of the irradiated area and (ii) a compressive stress increase of few GPa in the irradiated area center due to the Ti–Al–N decomposition, in particular due to the formation of small wurtzite (w) AlN domains. The coating hardness increased from 35 to 47 GPa towards the center of the heated spot. In the underlying heated substrate, a residual stress change from about − 200 to 500 MPa down to a depth of 6 μm is observed. Complementary, in-situ high-temperature X-ray diffraction analysis of stresses in a homogeneously heated Ti0.52Al0.48N coating on a WC–Co substrate was performed in the range of 25–1003 °C. The in-situ experiment revealed the origin of the observed thermally-activated residual stress oscillation across the laser heated spot. Finally, it is demonstrated that the coupling of laser heating to produce lateral thermal gradients and position-resolved experimental techniques opens the possibility to perform fast screening of structure–property relationships in complex materials. PMID:23471140

Optical tools for high-throughput screening of abrasion resistance of combinatorial libraries of organic coatings

NASA Astrophysics Data System (ADS)

Potyrailo, Radislav A.; Chisholm, Bret J.; Olson, Daniel R.; Brennan, Michael J.; Molaison, Chris A.

2002-02-01

Design, validation, and implementation of an optical spectroscopic system for high-throughput analysis of combinatorially developed protective organic coatings are reported. Our approach replaces labor-intensive coating evaluation steps with an automated system that rapidly analyzes 8x6 arrays of coating elements that are deposited on a plastic substrate. Each coating element of the library is 10 mm in diameter and 2 to 5 micrometers thick. Performance of coatings is evaluated with respect to their resistance to wear abrasion because this parameter is one of the primary considerations in end-use applications. Upon testing, the organic coatings undergo changes that are impossible to quantitatively predict using existing knowledge. Coatings are abraded using industry-accepted abrasion test methods at single-or multiple-abrasion conditions, followed by high- throughput analysis of abrasion-induced light scatter. The developed automated system is optimized for the analysis of diffusively scattered light that corresponds to 0 to 30% haze. System precision of 0.1 to 2.5% relative standard deviation provides capability for the reliable ranking of coatings performance. While the system was implemented for high-throughput screening of combinatorially developed organic protective coatings for automotive applications, it can be applied to a variety of other applications where materials ranking can be achieved using optical spectroscopic tools.

A synchrotron X-ray diffraction deconvolution method for the measurement of residual stress in thermal barrier coatings as a function of depth.

PubMed

Li, C; Jacques, S D M; Chen, Y; Daisenberger, D; Xiao, P; Markocsan, N; Nylen, P; Cernik, R J

2016-12-01

The average residual stress distribution as a function of depth in an air plasma-sprayed yttria stabilized zirconia top coat used in thermal barrier coating (TBC) systems was measured using synchrotron radiation X-ray diffraction in reflection geometry on station I15 at Diamond Light Source, UK, employing a series of incidence angles. The stress values were calculated from data deconvoluted from diffraction patterns collected at increasing depths. The stress was found to be compressive through the thickness of the TBC and a fluctuation in the trend of the stress profile was indicated in some samples. Typically this fluctuation was observed to increase from the surface to the middle of the coating, decrease a little and then increase again towards the interface. The stress at the interface region was observed to be around 300 MPa, which agrees well with the reported values. The trend of the observed residual stress was found to be related to the crack distribution in the samples, in particular a large crack propagating from the middle of the coating. The method shows promise for the development of a nondestructive test for as-manufactured samples.

Internal coating of zirconia restoration with silica-based ceramic improves bonding of resin cement to dental zirconia ceramic.

PubMed

Kitayama, Shuzo; Nikaido, Toru; Ikeda, Masaomi; Alireza, Sadr; Miura, Hiroyuki; Tagami, Junji

2010-01-01

Resin bonding to zirconia ceramic cannot be established by standard methods that are utilized for conventional silica-based dental ceramics. This study was aimed to examine the tensile bond strength of resin cement to zirconia ceramic using a new laboratory technique. Sixty-four zirconia ceramic specimens were air-abraded using Al2O3 particles and divided into two groups; the control group with no pretreatment (Control), and the group pretreated using the internal coating technique (INT), in which the surface of the zirconia specimens were thinly coated by fusing silica-based ceramic and air-abraded in the same manner. The specimens in each group were further divided into two subgroups according to the silane coupling agents applied; a mixture of dentin primer/silane coupling agent (Clearfil SE Bond Primer/Porcelain Bond Activator) or a newly developed single-component silane coupling agent (Clearfil Ceramic Primer). After bonding with dual-cured resin cement (Panavia F 2.0), they were stored in water for 24 h and half of them were additionally subjected to thermal cycling. The tensile bond strengths were tested using a universal testing machine. ANOVAs revealed significant influence of ceramic surface pretreatment (p<0.001), silane coupling agent (p<0.001) and thermal cycling (p<0.001); the INT coating technique significantly increased the bond strengths of resin cement to zirconia ceramic, whereas thermal cycling significantly decreased the bond strengths. The use of a single-component silane coupling agent demonstrated significantly higher bond strengths than that of a mixture of dentin primer/silane coupling agent. The internal coating of zirconia dental restorations with silica-based ceramic followed by silanization may be indicated in order to achieve better bonding for the clinical success.

Edible films and coatings based on biodegradable residues applied to acerolas (Malpighia punicifolia L.).

PubMed

Ferreira, Mariana S L; Fai, Ana Elizabeth C; Andrade, Cristina T; Picciani, Paulo H; Azero, Edwin G; Gonçalves, Édira C B A

2016-03-30

This study aimed to produce and characterize edible films and coatings from fruit and vegetable residue (FVR) flour and potato peel (P) flour. Two coating approaches (immersion and film) were studied on the quality of acerolas. Film-forming solutions (FFS) presented a viscoelastic behavior and a gelation process occurring at 70 °C. Maximum density (1.018 g cm(-3) ), viscosity (44.404 cP) and starch content were obtained for FFS based on 8% FVR flour with 4% P flour. This same film presented enhanced mechanical properties such as tensile strength and elongation at break (0.092 MPa and 36% respectively). Solubility of the films averaged 87%, demonstrating high hydrophilicity. Improved performance was obtained for film-packaged acerolas, which exhibited an increase in shelf life of 50% compared with control fruits. A lower loss of weight was observed for these samples by about 30-57% compared with control fruits, but minor modifications of pH, titratable acidity and soluble solid content occurred during storage. This study demonstrated the potential of FVR flour for edible coating and film formulation. Practical application on acerolas constituted a motivating route to evaluate and optimize this process; however, microbiological and sensory analyses are necessary to assess the material acceptability and safety. © 2015 Society of Chemical Industry.

A flexible method for residual stress measurement of spray coated layers by laser made hole drilling and SLM based beam steering

NASA Astrophysics Data System (ADS)

Osten, W.; Pedrini, G.; Weidmann, P.; Gadow, R.

2015-08-01

A minimum invasive but high resolution method for residual stress analysis of ceramic coatings made by thermal spraycoating using a pulsed laser for flexible hole drilling is described. The residual stresses are retrieved by applying the measured surface data for a model-based reconstruction procedure. While the 3D deformations and the profile of the machined area are measured with digital holography, the residual stresses are calculated by FE analysis. To improve the sensitivity of the method, a SLM is applied to control the distribution and the shape of the holes. The paper presents the complete measurement and reconstruction procedure and discusses the advantages and challenges of the new technology.

Nanocryl Coating of PMMA Complete Denture Base Materials to Prevent Scratching.

PubMed

Fathi, Hawa M; Benonn, Hajer A; Johnson, Anthony

2017-09-01

The surface of polymethylmethacrylate (PMMA) is vulnerable to indentation by hard objects that may contribute to abrade the material surface and subject it to wear. This phenomenon promotes an increase in the surface roughness leading to microbial colonisation which can endanger the general health of wearers and damage the intra-oral prosthesis. The aim of this study is to investigate the effect of three different nanocryl coating agents (Easy Glaze, G-Coat Plus and Formulation XP) on surface roughness and thickness of PMMA material after a simulating cleaning process utilizing an electric toothbrush and three different dentifrices (pastes and immersion). Acrylic uncoated discs were used as a control group. The results showed that the G-Coat Plus coating agent had less changes in the surface roughness and thickness layer whereas the immersion cleaner revealed less abrasion effect compared with the paste cleaners which could be considered the most suitable cleaner to provide lower abrasivenes and good removal of organic debris. However, using nanofilled sealants did not demonstrate significant improvement in reducing surface roughness p ⟩ 0.05. Nevertheless, it could provide some protection against wearing to the acrylic resin surface during tooth brushing and may provide better resistance to microbial colonisation. Copyright© 2017 Dennis Barber Ltd.

Effect of an internal coating technique on tensile bond strengths of resin cements to zirconia ceramics.

PubMed

Kitayama, Shuzo; Nikaido, Toru; Maruoka, Rena; Zhu, Lei; Ikeda, Masaomi; Watanabe, Akihiko; Foxton, Richard M; Miura, Hiroyuki; Tagami, Junji

2009-07-01

This study was conducted to enhance the tensile bond strengths of resin cements to zirconia ceramics. Fifty-six zirconia ceramic specimens (Cercon Base) and twenty-eight silica-based ceramic specimens (GN-1, GN-1 Ceramic Block) were air-abraded using alumina. Thereafter, the zirconia ceramic specimens were divided into two subgroups of 28 each according to the surface pretreatment; no pretreatment (Zr); and the internal coating technique (INT). For INT, the surface of zirconia was coated by fusing silica-based ceramics (Cercon Ceram Kiss). Ceramic surfaces were conditioned with/without a silane coupling agent followed by bonding with one of two resin cements; Panavia F 2.0 (PF) and Superbond C&B (SB). After 24 hours storage in water, the tensile bond strengths were tested (n=7). For both PF and SB, silanization significantly improved the bond strength to GN-1 and INT (p<0.05). The INT coating followed by silanizaton demonstrated enhancement of bonding to zirconia ceramics.

Sustainable and long-time 'rejuvenation' of biomimetic water-repellent silica coating on polyester fabrics induced by rough mechanical abrasion.

PubMed

Rosu, Cornelia; Lin, Haisheng; Jiang, Lu; Breedveld, Victor; Hess, Dennis W

2018-04-15

The economical use of water-repellent coatings on polymeric materials in commercial and industrial applications is limited by their mechanical wear robustness and long-term durability. In this study, we demonstrate that polyethylene terephthalate (PET) fabric modified with inorganic, methyltrimethoxysilane (MTMS)-based coatings shows excellent resistance against various types of wear damage, thereby mimicking superhydrophobic biological materials. These features were facilitated by the rational design of coating processing that also enabled tunable hierarchical surface structure. A series of custom and standard testing protocols revealed that coating-to-substrate adhesion was remarkably high, as was the resistance to various mechanical abradents. The most intriguing characteristic observed during aging and abrasion cycles was the enhancement in non-wettability or 'rejuvenation' reflected by water droplet roll-off behavior, a characteristic of self-cleaning materials. Water-repellent properties of coated polyester were also enhanced by prolonged thermal annealing and were maintained after custom laundry. The developed technology offers opportunities to design low cost, durable and functional textiles for both indoor and outdoor applications. Copyright © 2018 Elsevier Inc. All rights reserved.

Active thermography and post-processing image enhancement for recovering of abraded and paint-covered alphanumeric identification marks

NASA Astrophysics Data System (ADS)

Montanini, R.; Quattrocchi, A.; Piccolo, S. A.

2016-09-01

Alphanumeric marking is a common technique employed in industrial applications for identification of products. However, the realised mark can undergo deterioration, either by extensive use or voluntary deletion (e.g. removal of identification numbers of weapons or vehicles). For recovery of the lost data many destructive or non-destructive techniques have been endeavoured so far, which however present several restrictions. In this paper, active infrared thermography has been exploited for the first time in order to assess its effectiveness in restoring paint covered and abraded labels made by means of different manufacturing processes (laser, dot peen, impact, cold press and scribe). Optical excitation of the target surface has been achieved using pulse (PT), lock-in (LT) and step heating (SHT) thermography. Raw infrared images were analysed with a dedicated image processing software originally developed in Matlab™, exploiting several methods, which include thermographic signal reconstruction (TSR), guided filtering (GF), block guided filtering (BGF) and logarithmic transformation (LN). Proper image processing of the raw infrared images resulted in superior contrast and enhanced readability. In particular, for deeply abraded marks, good outcomes have been obtained by application of logarithmic transformation to raw PT images and block guided filtering to raw phase LT images. With PT and LT it was relatively easy to recover labels covered by paint, with the latter one providing better thermal contrast for all the examined targets. Step heating thermography never led to adequate label identification instead.

On the Electrodeposition of Ca-P Coatings on Nitinol Alloy: A Comparison Between Different Surface Modification Methods

NASA Astrophysics Data System (ADS)

Etminanfar, M. R.; Khalil-Allafi, J.

2016-02-01

In this study, a combination of surface modification process and the electrochemical deposition of Ca-P coatings was used for the modification of the Nitinol shape memory alloy. DSC, SEM, GIB-XRD, FT-Raman, XPS, and FTIR measurements were performed for the characterization of the samples. Results indicated that chemical etching and boiling of the samples in distilled water formed TiO film on the surface. After the chemical modification, subsequent aging of the sample, at 470 °C for 30 min, converted the oxide film to a stable structure of titanium dioxide. In that case, the treated substrate indicated a superelastic behavior. At the same electrochemical condition, the treated substrate revealed more stable and uniform Ca-P coatings in comparison with the abraded Nitinol substrate. This difference was attributed to the presence of hydroxyl groups on the titanium dioxide surface. Also, after soaking the sample in SBF, the needle-like coating on the treated substrate was completely covered with the hydroxyapatite phase which shows a good bioactivity of the coating.

Evaluation of the residual stresses in 95wt%Al2O3-5wt% SiC wear protection coating using X-Ray diffraction technique

NASA Astrophysics Data System (ADS)

Mahmoud, Adel K.; Hammoudi, Zaid S.; Student Samah Rasheed, M. Sc.

2018-02-01

This paper aims to measuring the residual stresses practically in wear protection coatings using the sin2ψ method according to X-ray diffraction technique. The wear protection coatings used in this study was composite coating 95wt% Al2O3-5wt% SiC, while bond coat was AlNi alloy produced by using flame spraying technique on the mild steel substrate. The diffraction angle, 2θ, is measured experimentally and then the lattice spacing is calculated from the diffraction angle, and the known X-ray wavelength using Bragg’s Law. Once the dspacing values are known, they can be plotted versus sin2ψ, (ψ is the tilt angle). In this paper, stress measurement of the samples that exhibit a linear behavior as in the case of a homogenous isotropic sample in a biaxial stress state is included. The plot of dspacing versus sin2ψ is a straight line which slope is proportional to stress. On the other hand, the second set of samples showed oscillatory dspacing versus sin2ψ behaviour. The oscillatory behaviour indicates the presence of inhomogeneous stress distribution. In this case the X-ray elastic constants must be used instead of Young’s modulus (E) and Poisson ratio (ν)values. These constants can be obtained from the literature for a given material and reflection combination. The value of the residual stresses for the present coating calculated was compressive stresses (-325.6758MPa).

X-ray analysis of residual stress gradients in TiN coatings by a Laplace space approach and cross-sectional nanodiffraction: a critical comparison.

PubMed

Stefenelli, Mario; Todt, Juraj; Riedl, Angelika; Ecker, Werner; Müller, Thomas; Daniel, Rostislav; Burghammer, Manfred; Keckes, Jozef

2013-10-01

Novel scanning synchrotron cross-sectional nanobeam and conventional laboratory as well as synchrotron Laplace X-ray diffraction methods are used to characterize residual stresses in exemplary 11.5 µm-thick TiN coatings. Both real and Laplace space approaches reveal a homogeneous tensile stress state and a very pronounced compressive stress gradient in as-deposited and blasted coatings, respectively. The unique capabilities of the cross-sectional approach operating with a beam size of 100 nm in diameter allow the analysis of stress variation with sub-micrometre resolution at arbitrary depths and the correlation of the stress evolution with the local coating microstructure. Finally, advantages and disadvantages of both approaches are extensively discussed.

An Abraded Surface of Doxorubicin-Loaded Surfactant-Containing Drug Delivery Systems Effectively Reduces the Survival of Carcinoma Cells.

PubMed

Schmidt, Christian; Yokaichiya, Fabiano; Doğangüzel, Nurdan; Dias Franco, Margareth K K; Cavalcanti, Leide P; Brown, Mark A; Alkschbirs, Melissa I; de Araujo, Daniele R; Kumpugdee-Vollrath, Mont; Storsberg, Joachim

2016-09-15

An effective antitumor remedy is yet to be developed. All previous approaches for a targeted delivery of anticancer medicine have relied on trial and error. The goal of this study was to use structural insights gained from the study of delivery systems and malignant cells to provide for a systematic approach to the development of next-generation drugs. We used doxorubicin (Dox) liposomal formulations. We assayed for cytotoxicity via the electrical current exclusion method. Dialysis of the samples yielded information about their drug release profiles. Information about the surface of the delivery systems was obtained through synchrotron small-angle X-ray scattering (SAXS) measurements. SAXS measurements revealed that Dox-loading yielded an abraded surface of our Dox liposomal formulation containing soybean oil, which also correlated with an effective reduction of the survival of carcinoma cells. Furthermore, a dialysis assay revealed that a higher burst of Dox was released from soybean oil-containing preparations within the first five hours. We conclude from our results that an abraded surface of Dox-loaded drug delivery system increases their efficacy. The apparent match between surface geometry of drug delivery systems and target cells is suggested as a steppingstone for refined development of drug delivery systems. This is the first study to provide a systematic approach to developing next-generation drug carrier systems using structural insights to guide the development of next-generation drug delivery systems with increased efficacy and reduced side effects.

A Theoretical Model for Predicting Residual Stress Generation in Fabrication Process of Double-Ceramic-Layer Thermal Barrier Coating System.

PubMed

Song, Yan; Wu, Weijie; Xie, Feng; Liu, Yilun; Wang, Tiejun

2017-01-01

Residual stress arisen in fabrication process of Double-Ceramic-Layer Thermal Barrier Coating System (DCL-TBCs) has a significant effect on its quality and reliability. In this work, based on the practical fabrication process of DCL-TBCs and the force and moment equilibrium, a theoretical model was proposed at first to predict residual stress generation in its fabrication process, in which the temperature dependent material properties of DCL-TBCs were incorporated. Then, a Finite Element method (FEM) has been carried out to verify our theoretical model. Afterwards, some important geometric parameters for DCL-TBCs, such as the thickness ratio of stabilized Zirconia (YSZ, ZrO2-8%Y2O3) layer to Lanthanum Zirconate (LZ, La2Zr2O7) layer, which is adjustable in a wide range in the fabrication process, have a remarkable effect on its performance, therefore, the effect of this thickness ratio on residual stress generation in the fabrication process of DCL-TBCs has been systematically studied. In addition, some thermal spray treatment, such as the pre-heating treatment, its effect on residual stress generation has also been studied in this work. It is found that, the final residual stress mainly comes from the cooling down process in the fabrication of DCL-TBCs. Increasing the pre-heating temperature can obviously decrease the magnitude of residual stresses in LZ layer, YSZ layer and substrate. With the increase of the thickness ratio of YSZ layer to LZ layer, magnitudes of residual stresses arisen in LZ layer and YSZ layer will increase while residual stress in substrate will decrease.

Anti-icing properties of superhydrophobic ZnO/PDMS composite coating

NASA Astrophysics Data System (ADS)

Yang, Chao; Wang, Fajun; Li, Wen; Ou, Junfei; Li, Changquan; Amirfazli, Alidad

2016-01-01

We present the excellent anti-icing performance for a superhydrophobic coating surface based on ZnO/polydimethylsiloxane (ZnO/PDMS) composite. The superhydrophobic ZnO/PDMS coating surface was prepared by a facile solution mixing, drop coating, room-temperature curing and surface abrading procedure. The superhydrophobic ZnO/PDMS composite coating possesses a water contact angle of 159.5° and a water sliding angle of 8.3° at room temperature (5 °C). The anti-icing properties of the superhydrophobic coating were investigated by continuously dropping cold-water droplets (about 0 °C) onto the pre-cooled surface using a home-made apparatus. The sample was placed at different tilting angle (0° and 10°) and pre-cooled to various temperatures (-5, -10 and -15 °C) prior to measure. The pure Al surface was also studied for comparison. It was found that icing accretion on the surface could be reduced apparently because the water droplets merged together and slid away from the superhydrophobic surface at all of the measuring temperatures when the surface is horizontally placed. In addition, water droplet slid away completely from the superhydrophobic surface at -5 and -10 °C when the surface is tilted at 10°, which demonstrates its excellent anti-icing properties at these temperatures. When the temperature decreased to -15 °C, though ice accretion on the tilted superhydrophobic coating surface could not be avoided absolutely, the amount of ice formed on the surface is very small, which indicated that the coating surface with superhydrophobicity could significantly reduce ice accumulation on the surface at very low temperature (-15 °C). Importantly, the sample is also stable against repeated icing/deicing cycles. More meaningfully, once the superhydrophobic surface is damaged, it can be repaired easily and rapidly.

Transient and residual stresses in a pressable glass-ceramic before and after resin-cement coating determined using profilometry.

PubMed

Isgró, G; Addison, O; Fleming, G J P

2011-05-01

The effect of heat-pressing and subsequent pre-cementation (acid-etching) and resin-cementation operative techniques on the development of transient and residual stresses in different thicknesses of a lithium disilicate glass-ceramic were characterised using profilometry prior to biaxial flexure strength (BFS) determination. 60 IPS e.max Press discs were pressed and divested under controlled conditions. The discs were polished on one surface to thicknesses of 0.61±0.05, 0.84±0.08, and 1.06±0.07 mm (Groups A-C, respectively). The mean of the maximum deflection (acid-etching and resin-coating was determined using high resolution profilometery prior to BFS testing. Paired sample t-tests were performed (p<0.05) on the 20 individual samples in each group (Groups A-C) for each comparison. Differences between the baseline quantification and resin-cement coating deflection values and BFS values for Groups A-C were determined using a one-way ANOVA with post hoc Tukey tests (p<0.05). Baseline quantification for Groups A-C identified no significant differences between the group means of the maximum deflection values (p=0.341). Following HF acid-etching, a significant increase in deflection for all groups (p<0.001) was identified compared with the baseline quantification. Additionally, resin-cement coating significantly increased deflection for Group A (p<0.001), Group B (p<0.001) and Group C (p=0.001) specimens for the individual groups. The increased deflection from baseline quantification to resin-cement coating was significantly different (p<0.001) for the three specimen thicknesses, although the BFS values were not. The lower reported baseline quantification range of the mean of the maximum deflection for the IPS e.max(®) Press specimens was predominantly the result of specimen polishing regime inducing a tensile stress state across the surface defect integral which accounted for the observed surface convexity. Acid-etching and resin-cementation had a significant

Biofilm development by blastospores and hyphae of Candida albicans on abraded denture acrylic resin surfaces.

PubMed

Jackson, Sarah; Coulthwaite, Lisa; Loewy, Zvi; Scallan, Anthony; Verran, Joanna

2014-10-01

Candida albicans is a known etiologic agent of denture stomatitis. Candida hyphae exhibit the ability to respond directionally to environmental stimuli. This characteristic is thought to be important in the penetration of substrata such as resilient denture liners and host epithelium. It has been suggested that hyphal production also enhances adhesion and survival of Candida on host and denture surfaces. Surface roughness, in addition, can enhance adhesion where stronger interactions occur between cells and surface features of similar dimensions. The purpose of this study was to assess the development of hyphal and blastospore biofilms on abraded denture acrylic resin specimens and measure the ease of removal of these biofilms. Biofilms were grown for 48 hours on abraded 1-cm² denture acrylic resin specimens from adhered hyphal phase C albicans or from adhered blastospores. Subsequently, all specimens were stained with Calcofluor White and examined with confocal scanning laser microscopy. Biofilms were removed by vortex mixing in sterile phosphate buffered saline solution. Removed cells were filtered (0.2-μm pore size). Filters were dried at 37°C for 24 hours for dry weight measurements. Any cells that remained on the acrylic resin specimens were stained with 0.03% acridine orange and examined with epifluorescence microscopy. Biofilms grown from both cell types contained all morphologic forms of C albicans. Although the underlying surface topography did not affect the amount of biofilm produced, biofilms grown from hyphal phase Candida were visibly thicker and had greater biomass (P<.05). These biofilms were less easily removed from the denture acrylic resin, especially in the case of rougher surfaces, evidenced by the higher numbers of retained cells (P≤.05). The presence of hyphae in early Candida biofilms increased biofilm mass and resistance to removal. Increased surface roughness enhances retention of hyphae and yeast cells, and, therefore, will

A Theoretical Model for Predicting Residual Stress Generation in Fabrication Process of Double-Ceramic-Layer Thermal Barrier Coating System

PubMed Central

Song, Yan; Wu, Weijie; Xie, Feng; Liu, Yilun; Wang, Tiejun

2017-01-01

Residual stress arisen in fabrication process of Double-Ceramic-Layer Thermal Barrier Coating System (DCL-TBCs) has a significant effect on its quality and reliability. In this work, based on the practical fabrication process of DCL-TBCs and the force and moment equilibrium, a theoretical model was proposed at first to predict residual stress generation in its fabrication process, in which the temperature dependent material properties of DCL-TBCs were incorporated. Then, a Finite Element method (FEM) has been carried out to verify our theoretical model. Afterwards, some important geometric parameters for DCL-TBCs, such as the thickness ratio of stabilized Zirconia (YSZ, ZrO2-8%Y2O3) layer to Lanthanum Zirconate (LZ, La2Zr2O7) layer, which is adjustable in a wide range in the fabrication process, have a remarkable effect on its performance, therefore, the effect of this thickness ratio on residual stress generation in the fabrication process of DCL-TBCs has been systematically studied. In addition, some thermal spray treatment, such as the pre-heating treatment, its effect on residual stress generation has also been studied in this work. It is found that, the final residual stress mainly comes from the cooling down process in the fabrication of DCL-TBCs. Increasing the pre-heating temperature can obviously decrease the magnitude of residual stresses in LZ layer, YSZ layer and substrate. With the increase of the thickness ratio of YSZ layer to LZ layer, magnitudes of residual stresses arisen in LZ layer and YSZ layer will increase while residual stress in substrate will decrease. PMID:28103275

Phase transformations and residual stresses in environmental barrier coatings

NASA Astrophysics Data System (ADS)

Harder, Bryan J.

Silicon-based ceramics (SiC, Si3N4) are promising materials for high-temperature structural applications in turbine engines. However, the silica layer that forms on these materials is susceptible to attack from water vapor present in combustion environments. To protect against this degradation, environmental barrier coatings (EBCs) were developed to protect the underlying substrate. In the case of silicon carbide (SiC), multilayer coating systems consist of a Ba1-xSrxAl2Si 2O8 (BSAS) topcoat, a mullite or mullite + SrAl2Si 2O8 (SAS) interlayer, and a silicon bond coat. In this work, biaxial strains were measured on as-sprayed and heat-treated samples to analyze the stress and phase evolution in the coating system as a function of depth and temperature. Models were used to compare the results with an ideal coating system. In the assprayed state, tensile stresses as high as 175 MPa were measured, and cracking was observed. After thermally cycling the samples, stresses were significantly reduced and cracks in the topcoat had closed. The addition of SAS to the interlayer increased the compressive stress in the BSAS topcoat in thermally-cycled samples, which was desirable for EBC applications. The BSAS topcoat transformed from the as-deposited hexacelsian state to the stable celsian above 1200°C. This phase transformation is accompanied by a CTE reduction. The kinetics of the hexacelsian-to-celsian transformation were quantified for freestanding plasma-sprayed BSAS. Activation energies for bulk bars and crushed powder were determined to be ˜340 kJ/mol and ˜500 kJ/mol, respectively. X-ray diffraction and electron backscatter diffraction were used to establish how microstructural constraints reduce the transformation energy. Barrier coating lifetime and stability are also influenced by exposure to reactive, low-melting point calcium-magnesium-aluminosilicate (CMAS) deposits formed from dust and sand. Multilayer doped aluminosilicate coatings and bulk BSAS material were

The improvement of adhesive properties of PEEK through different pre-treatments

NASA Astrophysics Data System (ADS)

Hallmann, Lubica; Mehl, Albert; Sereno, Nuno; Hämmerle, Christoph H. F.

2012-07-01

The purpose of this in vitro study was the evaluation of the bond strength of the adhesives/composite resin to Poly Ether Ether Ketone (PEEK) based dental polymer after using different surface conditioning methods. PEEK blanks were cut into discs. All disc specimens were polished with 800 grit SiC paper and divided into 6 main groups. Main groups were divided into 2 subgroups. The main groups of 32 specimens each were treated as follow: (1) control specimens (no treatment), (2) piranha solution etching, (3) abraded with 50 μm alumina particles and chemical etching, (4) abraded with 110 μm alumina particles and chemical etching, (5) abraded with 30 μm silica-coated alumina particles and chemical etching, (6) abraded with 110 μm silica-coated alumina particles and chemical etching. Plexiglas tubes filled with a composite resin (RelyX Unicem) were bonded to the specimens. The adhesives used were Heliobond and Clearfil Ceramic Primer. Each specimen was stored in distilled water (37 °C) for 3 days. Tensile bond strength was measured in a universal testing machine and failure methods were evaluated. Abraded surface with 50 μm alumina particles followed by etching with piranha solution lead to the highest bond strength of 21.4 MPa when Heliobond like adhesive was used. Tribochemical silica coated/etched PEEK surfaces did not have an effect on the bond strength. Non-treated PEEK surface was not able to establish a bond with composite resin. The proper choice of adhesive/composite resin system leads to a strong bond. ConclusionAirborne particle abrasion in combination with piranha solution etching improves the adhesive properties of PEEK.

Accelerated crack growth, residual stress, and a cracked zinc coated pressure shell

NASA Technical Reports Server (NTRS)

Dittman, Daniel L.; Hampton, Roy W.; Nelson, Howard G.

1987-01-01

During a partial inspection of a 42 year old, operating, pressurized wind tunnel at NASA-Ames Research Center, a surface connected defect 114 in. long having an indicated depth of a 0.7 in. was detected. The pressure shell, constructed of a medium carbon steel, contains approximately 10 miles of welds and is cooled by flowing water over its zinc coated external surface. Metallurgical and fractographic analysis showed that the actual detect was 1.7 in. deep, and originated from an area of lack of weld penetration. Crack growth studies were performed on the shell material in the laboratory under various loading rates, hold times, and R-ratios with a simulated shell environment. The combination of zinc, water with electrolyte, and steel formed an electrolytic cell which resulted in an increase in cyclic crack growth rate by as much as 500 times over that observed in air. It was concluded that slow crack growth occurred in the pressure shell by a combination of stress corrosion cracking due to the welding residual stress and corrosion fatigue due to the cyclic operating stress.

Deposition stress effects on thermal barrier coating burner rig life

NASA Technical Reports Server (NTRS)

Watson, J. W.; Levine, S. R.

1984-01-01

A study of the effect of plasma spray processing parameters on the life of a two layer thermal barrier coating was conducted. The ceramic layer was plasma sprayed at plasma arc currents of 900 and 600 amps onto uncooled tubes, cooled tubes, and solid bars of Waspalloy in a lathe with 1 or 8 passes of the plasma gun. These processing changes affected the residual stress state of the coating. When the specimens were tested in a Mach 0.3 cyclic burner rig at 1130 deg C, a wide range of coating lives resulted. Processing factors which reduced the residual stress state in the coating, such as reduced plasma temperature and increased heat dissipation, significantly increased coating life.

Silica-Based and Borate-Based, Titania-Containing Bioactive Coatings Characterization: Critical Strain Energy Release Rate, Residual Stresses, Hardness, and Thermal Expansion.

PubMed

Rodriguez, Omar; Matinmanesh, Ali; Phull, Sunjeev; Schemitsch, Emil H; Zalzal, Paul; Clarkin, Owen M; Papini, Marcello; Towler, Mark R

2016-12-01

Silica-based and borate-based glass series, with increasing amounts of TiO₂ incorporated, are characterized in terms of their mechanical properties relevant to their use as metallic coating materials. It is observed that borate-based glasses exhibit CTE (Coefficient of Thermal Expansion) closer to the substrate's (Ti6Al4V) CTE, translating into higher mode I critical strain energy release rates of glasses and compressive residual stresses and strains at the coating/substrate interface, outperforming the silica-based glasses counterparts. An increase in the content of TiO₂ in the glasses results in an increase in the mode I critical strain energy release rate for both the bulk glass and for the coating/substrate system, proving that the addition of TiO₂ to the glass structure enhances its toughness, while decreasing its bulk hardness. Borate-based glass BRT3, with 15 mol % TiO₂ incorporated, exhibits superior properties overall compared to the other proposed glasses in this work, as well as 45S5 Bioglass ® and Pyrex.

Silica-Based and Borate-Based, Titania-Containing Bioactive Coatings Characterization: Critical Strain Energy Release Rate, Residual Stresses, Hardness, and Thermal Expansion

PubMed Central

Rodriguez, Omar; Matinmanesh, Ali; Phull, Sunjeev; Schemitsch, Emil H.; Zalzal, Paul; Clarkin, Owen M.; Papini, Marcello; Towler, Mark R.

2016-01-01

Silica-based and borate-based glass series, with increasing amounts of TiO2 incorporated, are characterized in terms of their mechanical properties relevant to their use as metallic coating materials. It is observed that borate-based glasses exhibit CTE (Coefficient of Thermal Expansion) closer to the substrate’s (Ti6Al4V) CTE, translating into higher mode I critical strain energy release rates of glasses and compressive residual stresses and strains at the coating/substrate interface, outperforming the silica-based glasses counterparts. An increase in the content of TiO2 in the glasses results in an increase in the mode I critical strain energy release rate for both the bulk glass and for the coating/substrate system, proving that the addition of TiO2 to the glass structure enhances its toughness, while decreasing its bulk hardness. Borate-based glass BRT3, with 15 mol % TiO2 incorporated, exhibits superior properties overall compared to the other proposed glasses in this work, as well as 45S5 Bioglass® and Pyrex. PMID:27916951

Diffraction grating strain gauge method: error analysis and its application for the residual stress measurement in thermal barrier coatings

NASA Astrophysics Data System (ADS)

Yin, Yuanjie; Fan, Bozhao; He, Wei; Dai, Xianglu; Guo, Baoqiao; Xie, Huimin

2018-03-01

Diffraction grating strain gauge (DGSG) is an optical strain measurement method. Based on this method, a six-spot diffraction grating strain gauge (S-DGSG) system has been developed with the advantages of high and adjustable sensitivity, compact structure, and non-contact measurement. In this study, this system is applied for the residual stress measurement in thermal barrier coatings (TBCs) combining the hole-drilling method. During the experiment, the specimen’s location is supposed to be reset accurately before and after the hole-drilling, however, it is found that the rigid body displacements from the resetting process could seriously influence the measurement accuracy. In order to understand and eliminate the effects from the rigid body displacements, such as the three-dimensional (3D) rotations and the out-of-plane displacement of the grating, the measurement error of this system is systematically analyzed, and an optimized method is proposed. Moreover, a numerical experiment and a verified tensile test are conducted, and the results verify the applicability of this optimized method successfully. Finally, combining this optimized method, a residual stress measurement experiment is conducted, and the results show that this method can be applied to measure the residual stress in TBCs.

Engineered Surfaces for Mitigation of Insect Residue Adhesion

NASA Technical Reports Server (NTRS)

Siochi, Emilie J.; Smith, Joseph G.; Wohl, Christopher J.; Gardner, J. M.; Penner, Ronald K.; Connell, John W.

2013-01-01

Maintenance of laminar flow under operational flight conditions is being investigated under NASA s Environmentally Responsible Aviation (ERA) Program. Among the challenges with natural laminar flow is the accretion of residues from insect impacts incurred during takeoff or landing. Depending on air speed, temperature, and wing structure, the critical residue height for laminar flow disruption can be as low as 4 microns near the leading edge. In this study, engineered surfaces designed to minimize insect residue adhesion were examined. The coatings studied included chemical compositions containing functional groups typically associated with abhesive (non-stick) surfaces. To reduce surface contact by liquids and enhance abhesion, the engineered surfaces consisted of these coatings doped with particulate additives to generate random surface topography, as well as coatings applied to laser ablated surfaces having precision patterned topographies. Performance evaluation of these surfaces included contact angle goniometry of pristine coatings and profilometry of surfaces after insect impacts were incurred in laboratory scale tests, wind tunnel tests and flight tests. The results illustrate the complexity of designing antifouling surfaces for effective insect contamination mitigation under dynamic conditions and suggest that superhydrophobic surfaces may not be the most effective solution for preventing insect contamination on aircraft wing leading edges.

Thermal stress fracture of ceramic coatings

NASA Technical Reports Server (NTRS)

Andersson, C. A.

1983-01-01

Thermal stress failures of ceramic coatings are discussed in terms of fracture mechanics concepts. The effects of transient and residual stresses on single and multiple cycle failure mechanisms are considered. A specific example of a zirconia thermal barrier coating is presented and its endurance calculated using the proposed relationships.

Investigation of the Effect of Residual Stress Gradient on the Wear Behavior of PVD Thin Films

NASA Astrophysics Data System (ADS)

Tlili, B.; Nouveau, C.; Guillemot, G.; Besnard, A.; Barkaoui, A.

2018-02-01

The control of residual stresses has been seldom investigated in multilayer coatings dedicated to improvement of wear behavior. Here, we report the preparation and characterization of superposed structures composed of Cr, CrN and CrAlN layers. Nano-multilayers CrN/CrAlN and Cr/CrN/CrAlN were deposited by Physical Vapor Deposition (PVD) onto Si (100) and AISI4140 steel substrates. The Cr, CrN and CrAlN monolayers were developed with an innovative approach in PVD coatings technologies corresponding to deposition with different residual stresses levels. Composition and wear tracks morphologies of the coatings were characterized by scanning electron microscopy, high-resolution transmission electron microscopy, atomic force microscopy, x-ray photoelectron spectroscopy, energy-dispersive x-ray spectroscopy, x-ray diffraction and 3D-surface analyzer. The mechanical properties (hardness, residual stresses and wear) were investigated by nanoindentation, interferometry and micro-tribometry (fretting-wear tests). Observations suggest that multilayer coatings are composed mostly of nanocrystalline. The residual stresses level in the films has practically affected all the physicochemical and mechanical properties as well as the wear behavior. Consequently, it is demonstrated that the coating containing moderate stresses has a better wear behavior compared to the coating developed with higher residual stresses. The friction contact between coated samples and alumina balls shows also a large variety of wear mechanisms. In particular, the abrasive wear of the coatings was a combination of plastic deformation, fine microcracking and microspallation. The application of these multilayers will be wood machining of green wood.

Antiadhesive effect of bioresorbable polylactide film in abraded middle ear mucosa.

PubMed

Jang, Chul Ho; Jo, Si Young; Cho, Yong Beom; Choi, Cheol Hee; Jung, Won Kyo

2014-12-01

Polylactide film (PLF) is used to prevent postoperative peridural adhesion in spinal surgery. Up until now, the antiadhesive effect of bioresorbable PLF in ear middle surgery has not been reported. The purpose of this study is to evaluate the antiadhesive effect of PLF in guinea pigs serving as a model for middle ear mucosal trauma. The animals were divided into two groups: the PLF group and the silastic sheeting group. There were seven guinea pigs (fourteen ears) in both groups. Under aseptic conditions, the middle ear mucosa was abraded using a pick inserted transbullaly. A PLF or silicone sheet was then placed into the guinea pigs' middle ear cavities. The auditory brainstem responses (ABRs) were assessed preoperatively and at three weeks postoperatively while the animals were under general anesthesia. A histopathological study was performed 3 weeks after the operation. The difference between the ABR results before the operation and three weeks postoperatively were not statistically significant. The adhesion formation did not appeared in either group. Prominent fibrous capsule formation and inflammation were observed in the silastic sheeting group, but not in the PLF group. Mild fibrous thickening of regenerated mucosa was observed in the PLF group. From our results, bioresorbable PLF is nonototoxic and biocompatible with the guinea pig's middle ear cavity by short-term evaluation. Further long-term evaluation study is necessary before clinical application. Copyright © 2014 Elsevier Ireland Ltd. All rights reserved.

Long-term Bond Strength between Layering Indirect Composite Material and Zirconia Coated with Silicabased Ceramics.

PubMed

Fushiki, Ryosuke; Komine, Futoshi; Honda, Junichi; Kamio, Shingo; Blatz, Markus B; Matsumura, Hideo

2015-06-01

This study evaluated the long-term shear bond strength between an indirect composite material and a zirconia framework coated with silica-based ceramics, taking the effect of different primers into account. A total of 165 airborne-particle abraded zirconia disks were subjected to one of three pretreatments: no pretreatment (ZR-AB), airborne-particle abrasion of zirconia coated with feldspathic porcelain (ZR-PO-AB), and 9.5% hydrofluoric acid etching of zirconia coated with feldspathic porcelain (ZR-PO-HF). An indirect composite material (Estenia C&B) was then bonded to the zirconia disks after they were treated with one of the following primers: Clearfil Photo Bond (CPB), Clearfil Photo Bond with Clearfil Porcelain Bond Activator (CPB + Activator), Estenia Opaque Primer (EOP), Porcelain Liner M Liquid B (PLB), or no priming (CON, control group). Shear bond strength was tested after 100,000 thermocycles, and the data were analyzed using the Steel-Dwass U-test (α = 0.05). For ZR-PO-AB and ZR-PO-HF specimens, bond strength was highest in the CPB+Activator group (25.8 MPa and 22.4 MPa, respectively). Bond strengths were significantly lower for ZR-AB specimens in the CON and PLB groups and for ZR-PO-AB specimens in the CON, CPB, and EOP groups. Combined application of a hydrophobic phosphate monomer (MDP) and silane coupling agent enhanced the long-term bond strength of indirect composite material to a zirconia coated with silica-based ceramics.

Theoretical modelling of residual and transformational stresses in SMA composites

NASA Astrophysics Data System (ADS)

Berman, J. B.; White, S. R.

1996-12-01

SMA composites are a class of smart materials in which shape memory alloy (SMA) actuators are embedded in a polymer matrix composite. The difference in thermal expansion between the SMA and the host material leads to residual stresses during processing. Similarly, the SMA transformations from martensite to austenite, or the reverse, also generate stresses. These stresses acting in combination can lead to SMA/epoxy interfacial debonding or microcracking of the composite phase. In this study the residual and transformational stresses are investigated for a nitinol wire embedded in a graphite/epoxy composite. A three-phase micromechanical model is developed. The nitinol wire is assumed to behave as a thermoelastic material. Nitinol austenitic and martensitic transformations are modelled using linear piecewise interpolation of experimental data. The interphase is modelled as a thermoelastic polymer. A transversely isotropic thermoelastic composite is used for the outer phase. Stress-free conditions are assumed immediately before cool down from the cure temperature. The effect of nitinol, coating and composite properties on residual and transformational stresses are evaluated. Fiber architectures favoring the axial direction decrease the magnitude of all residual stresses. A decrease in stresses at the composite/coating interface is also predicted through the use of thick, compliant coatings. Reducing the recovery strain and moving the transformation to higher temperatures were found to be most effective in reducing residual stresses.

Solventless pharmaceutical coating processes: a review.

PubMed

Bose, Sagarika; Bogner, Robin H

2007-01-01

Coatings are an essential part in the formulation of pharmaceutical dosage form to achieve superior aesthetic quality (e.g., color, texture, mouth feel, and taste masking), physical and chemical protection for the drugs in the dosage forms, and modification of drug release characteristics. Most film coatings are applied as aqueous- or organic-based polymer solutions. Both organic and aqueous film coating bring their own disadvantages. Solventless coating technologies can overcome many of the disadvantages associated with the use of solvents (e.g., solvent exposure, solvent disposal, and residual solvent in product) in pharmaceutical coating. Solventless processing reduces the overall cost by eliminating the tedious and expensive processes of solvent disposal/treatment. In addition, it can significantly reduce the processing time because there is no drying/evaporation step. These environment-friendly processes are performed without any heat in most cases (except hot-melt coating) and thus can provide an alternative technology to coat temperature-sensitive drugs. This review discusses and compares six solventless coating methods - compression coating, hot-melt coating, supercritical fluid spray coating, electrostatic coating, dry powder coating, and photocurable coating - that can be used to coat the pharmaceutical dosage forms.

Deposition stress effects on the life of thermal barrier coatings on burner rigs

NASA Technical Reports Server (NTRS)

Watson, J. W.; Levine, S. R.

1984-01-01

A study of the effect of plasma spray processing parameters on the life of a two layer thermal barrier coating was conducted. The ceramic layer was plasma sprayed at plasma arc currents of 900 and 600 amps onto uncooled tubes, cooled tubes, and solid bars of Waspalloy in a lathe with 1 or 8 passes of the plasma gun. These processing changes affected the residual stress state of the coating. When the specimens were tested in a Mach 0.3 cyclic burner rig at 1130 deg C, a wide range of coating lives resulted. Processing factors which reduced the residual stress state in the coating, such as reduced plasma temperature and increased heat dissipation, significantly increased coating life.

Fort Campbell Childers House: Historic Maintenance and Repair Manual

DTIC Science & Technology

2006-09-01

coal-tar pitch and surfaced with a layer of gravel or slag in a heavy coat of asphalt or coal-tar pitch or finished with a cap sheet; generally used...such as lead, tin, copper, terneplate, and zinc with appropriate chemical methods because their finishes can be easily abraded by blasting methods...tin, copper, terneplate, and zinc with grit blasting which will abrade the surface of the metal. • Using cleaning methods, which alter or damage

Deposition and Characterization of HVOF Thermal Sprayed Functionally Graded Coatings Deposited onto a Lightweight Material

NASA Astrophysics Data System (ADS)

Hasan, M.; Stokes, J.; Looney, L.; Hashmi, M. S. J.

2009-02-01

There is a significant interest in lightweight materials (like aluminum, magnesium, titanium, and so on) containing a wear resistance coating, in such industries as the automotive industry, to replace heavy components with lighter parts in order to decrease vehicle weight and increase fuel efficiency. Functionally graded coatings, in which the composition, microstructure, and/or properties vary gradually from the bond coat to the top coat, may be applied to lightweight materials, not only to decrease weight, but also to enhance components mechanical properties by ensuring gradual microstructural (changes) together with lower residual stress. In the current work, aluminum/tool-steel functionally graded coatings were deposited onto lightweight aluminum substrates. The graded coatings were then characterized in terms of residual stress and hardness. Results show that residual stress increased with an increase in deposition thickness and a decrease in number of layers. However, the hardness also increased with an increase in deposition thickness and decrease in number of layers. Therefore, an engineer must compromise between the hardness and stress values while designing a functionally graded coating-substrate system.

Aluminum and Other Coatings for the Passivation of Tritium Storage Vessels

DOE Office of Scientific and Technical Information (OSTI.GOV)

Spencer, W.; Korinko, P.

Using a highly sensitive residual gas analyzer, the off-gassing of hydrogen, water, and hydrocarbons from surface-treated storage vessels containing deuterium was measured. The experimental storage vessels were compared to a low-off-gassing, electro-polished 304L canister. Alternative vessels were made out of aluminum, or were coatings on 304L steel. Coatings included powder pack aluminide, electro-plated aluminum, powder pack chromide, dense electro-plated chromium, copper plated, and copper plated with 25 and 50 percent nano-diamond. Vessels were loaded with low pressure deuterium to observe exchange with protium or hydrogen as observed with formation of HD and HDO. Off gas of D 2O or possiblemore » CD 4 was observed at mass 20. The main off-gas in all of the studies was H 2. The studies indicated that coatings required significant post-coating treatment to reduce off-gas and enhance the permeation barrier from gases likely added during the coating process. Dense packed aluminum coatings needed heating to drive off water. Electro-plated aluminum, chromium and copper coatings appeared to trap hydrogen from the plating process. Nano-diamond appeared to enhance the exchange rate with hydrogen off gas, and its coating process trapped significant amounts of hydrogen. Aluminum caused more protium exchange than chromium-treated surfaces. Aluminum coatings released more water, but pure aluminum vessels released small amounts of hydrogen, little water, and generally performed well. Chromium coating had residual hydrogen that was difficult to totally outgas but otherwise gave low residuals for water and hydrocarbons. Our studies indicated that simple coating of as received 304L metal will not adequately block hydrogen. The base vessel needs to be carefully out-gassed before applying a coating, and the coating process will likely add additional hydrogen that must be removed. Initial simple bake-out and leak checks up to 350° C for a few hours was found to be inadequate

Molecular interactions of mussel protective coating protein, mcfp-1, from Mytilus californianus.

PubMed

Lu, Qingye; Hwang, Dong Soo; Liu, Yang; Zeng, Hongbo

2012-02-01

Protective coating of the byssus of mussels (Mytilus sp.) has been suggested as a new paradigm of medical coating due to its high extensibility and hardness co-existence without their mutual detriment. The only known biomacromolecule in the extensible and tough coating on the byssus is mussel foot protein-1 (mfp-1), which is made up with positively charged residues (~20 mol%) and lack of negatively charged residues. Here, adhesion and molecular interaction mechanisms of Mytilus californianus foot protein-1 (mcfp-1) from California blue mussel were investigated using a surface forces apparatus (SFA) in buffer solutions of different ionic concentrations (0.2-0.7 M) and pHs (3.0-5.5). Strong and reversible cohesion between opposed positively charged mcfp-1 films was measured in 0.1 M sodium acetate buffer with 0.1 M KNO(3). Cohesion of mcfp-1 was gradually reduced with increasing the ionic strength, but was not changed with pH variations. Oxidation of 3,4-dihydroxyphenylalanine (DOPA) residues of mcfp-1, a key residue for adhesive and coating proteins of mussel, didn't change the cohesion strength of mcfp-1 films, but the addition of chemicals with aromatic groups (i.e., aspirin and 4-methylcatechol) increased the cohesion. These results suggest that the cohesion of mcfp-1 films is mainly mediated by cation-π interactions between the positively charged residues and benzene rings of DOPA and other aromatic amino acids (~20 mol% of total amino acids of mcfp-1), and π-π interactions between the phenyl groups in mcfp-1. The adhesion mechanism obtained for the mcfp-1 proteins provides important insight into the design and development of functional biomaterials and coatings mimicking the extensible and robust mussel cuticle coating. Copyright © 2011 Elsevier Ltd. All rights reserved.

Optical residual stress measurement in TFT-LCD panels

NASA Astrophysics Data System (ADS)

Wang, Wei-Chung; Sung, Po-Chi

2017-06-01

The residual stress of the glass substrate might be one of causes to produce the non-uniform light distribution defect, i.e. Mura, in thin film transistor-liquid crystal display (TFT-LCD) panels. Glass is a birefringent material with very low birefringence. Furthermore, the thinner and thinner thickness request from the market makes the traditional photoelasticity almost impossible to measure the residual stresses produced in thin glass plates. Recently, a low-level stress measurement method called transmissivity extremities theory of photoelasticity (TEToP) was successfully developed to measure the residual stress in glass plate. Besides, to measure the stress of the glass plate in the TFT-LCD panel whose rear surface may has different kinds of coatings, an advanced reflection photoelasticity was also developed. In this paper, three commercially available glass plates with 0.33mm nominal thickness and three glass circular disks with different coatings were inspected to verify the feasibility of the TEToP and the advanced reflection photoelasticity, respectively.

Rocket thrust chamber thermal barrier coatings

NASA Technical Reports Server (NTRS)

Batakis, A. P.; Vogan, J. W.

1985-01-01

A research program was conducted to generate data and develop analytical techniques to predict the performance and reliability of ceramic thermal barrier coatings in high heat flux environments. A finite element model was used to analyze the thermomechanical behavior of coating systems in rocket thrust chambers. Candidate coating systems (using a copper substrate, NiCrAlY bond coat and ZrO2.8Y2O3 ceramic overcoat) were selected for detailed study based on photomicrographic evaluations of experimental test specimens. The effects of plasma spray application parameters on the material properties of these coatings were measured and the effects on coating performance evaluated using the finite element model. Coating design curves which define acceptable operating envelopes for seleted coating systems were constructed based on temperature and strain limitations. Spray gun power levels was found to have the most significant effect on coating structure. Three coating systems were selected for study using different power levels. Thermal conductivity, strain tolerance, density, and residual stress were measured for these coatings. Analyses indicated that extremely thin coatings ( 0.02 mm) are required to accommodate the high heat flux of a rocket thrust chamber and ensure structural integrity.

Protozoal Digestion of Coat-Defective Bacillus subtilis Spores Produces “Rinds” Composed of Insoluble Coat Protein▿

PubMed Central

Carroll, Alicia Monroe; Plomp, Marco; Malkin, Alexander J.; Setlow, Peter

2008-01-01

The Bacillus subtilis spore coat is a multilayer, proteinaceous structure that consists of more than 50 proteins. Located on the surface of the spore, the coat provides resistance to potentially toxic molecules as well as to predation by the protozoan Tetrahymena thermophila. When coat-defective spores are fed to Tetrahymena, the spores are readily digested. However, a residue termed a “rind” that looks like coat material remains. As observed with a phase-contrast microscope, the rinds are spherical or hemispherical structures that appear to be devoid of internal contents. Atomic force microscopy and chemical analyses showed that (i) the rinds are composed of insoluble protein largely derived from both outer and inner spore coat layers, (ii) the amorphous layer of the outer coat is largely responsible for providing spore resistance to protozoal digestion, and (iii) the rinds and intact spores do not contain significant levels of silicon. PMID:18689521

Improvement on the Fatigue Performance of 2024-T4 Alloy by Synergistic Coating Technology

PubMed Central

Wang, Xi-Shu; Guo, Xing-Wu; Li, Xu-Dong; Ge, Dong-Yun

2014-01-01

In this paper, rotating bending fatigue tests of 2024-T4 Al alloy with different oxide coatings were carried out. Compared to the uncoated and previously reported oxide coatings of aluminum alloys, the fatigue strength is able to be enhanced by using a novel oxide coating with sealing pore technology. These results indicate that the better the coating surface quality is, the more excellent the fatigue performance under rotating bending fatigue loading is. The improvement on the fatigue performance is mainly because the fatigue crack initiation and the early stage of fatigue crack growth at the coating layer can be delayed after PEO coating with pore sealing. Therefore, it is a so-called synergistic coating technology for various uses, including welding thermal cracks and filling micro-pores. The effects of different oxide coatings on surface hardness, compressive residual stress, morphology and fatigue fracture morphology are discussed. A critical compressive residual stress of about 95–100 MPa is proposed. PMID:28788634

Crystal structure of the coat protein from the GA bacteriophage: model of the unassembled dimer.

PubMed Central

Ni, C. Z.; White, C. A.; Mitchell, R. S.; Wickersham, J.; Kodandapani, R.; Peabody, D. S.; Ely, K. R.

1996-01-01

There are four groups of RNA bacteriophages with distinct antigenic and physicochemical properties due to differences in surface residues of the viral coat proteins. Coat proteins also play a role as translational repressor during the viral life cycle, binding an RNA hairpin within the genome. In this study, the first crystal structure of the coat protein from a Group II phage GA is reported and compared to the Group I MS2 coat protein. The structure of the GA dimer was determined at 2.8 A resolution (R-factor = 0.20). The overall folding pattern of the coat protein is similar to the Group I MS2 coat protein in the intact virus (Golmohammadi R, Valegård K, Fridborg K, Liljas L. 1993, J Mol Biol 234:620-639) or as an unassembled dimer (Ni Cz, Syed R, Kodandapani R. Wickersham J, Peabody DS, Ely KR, 1995, Structure 3:255-263). The structures differ in the FG loops and in the first turn of the alpha A helix. GA and MS2 coat proteins differ in sequence at 49 of 129 amino acid residues. Sequence differences that contribute to distinct immunological and physical properties of the proteins are found at the surface of the intact virus in the AB and FG loops. There are six differences in potential RNA contact residues within the RNA-binding site located in an antiparallel beta-sheet across the dimer interface. Three differences involve residues in the center of this concave site: Lys/Arg 83, Ser/Asn 87, and Asp/Glu 89. Residue 87 was shown by molecular genetics to define RNA-binding specificity by GA or MS2 coat protein (Lim F. Spingola M, Peabody DS, 1994, J Biol Chem 269:9006-9010). This sequence difference reflects recognition of the nucleotide at position -5 in the unpaired loop of the translational operators bound by these coat proteins. In GA, the nucleotide at this position is a purine whereas in MS2, it is a pyrimidine. PMID:8976557

Crystal structure of the coat protein from the GA bacteriophage: model of the unassembled dimer.

PubMed

Ni, C Z; White, C A; Mitchell, R S; Wickersham, J; Kodandapani, R; Peabody, D S; Ely, K R

1996-12-01

There are four groups of RNA bacteriophages with distinct antigenic and physicochemical properties due to differences in surface residues of the viral coat proteins. Coat proteins also play a role as translational repressor during the viral life cycle, binding an RNA hairpin within the genome. In this study, the first crystal structure of the coat protein from a Group II phage GA is reported and compared to the Group I MS2 coat protein. The structure of the GA dimer was determined at 2.8 A resolution (R-factor = 0.20). The overall folding pattern of the coat protein is similar to the Group I MS2 coat protein in the intact virus (Golmohammadi R, Valegård K, Fridborg K, Liljas L. 1993, J Mol Biol 234:620-639) or as an unassembled dimer (Ni Cz, Syed R, Kodandapani R. Wickersham J, Peabody DS, Ely KR, 1995, Structure 3:255-263). The structures differ in the FG loops and in the first turn of the alpha A helix. GA and MS2 coat proteins differ in sequence at 49 of 129 amino acid residues. Sequence differences that contribute to distinct immunological and physical properties of the proteins are found at the surface of the intact virus in the AB and FG loops. There are six differences in potential RNA contact residues within the RNA-binding site located in an antiparallel beta-sheet across the dimer interface. Three differences involve residues in the center of this concave site: Lys/Arg 83, Ser/Asn 87, and Asp/Glu 89. Residue 87 was shown by molecular genetics to define RNA-binding specificity by GA or MS2 coat protein (Lim F. Spingola M, Peabody DS, 1994, J Biol Chem 269:9006-9010). This sequence difference reflects recognition of the nucleotide at position -5 in the unpaired loop of the translational operators bound by these coat proteins. In GA, the nucleotide at this position is a purine whereas in MS2, it is a pyrimidine.

A fundamental approach to the sticking of insect residues to aircraft wings

NASA Technical Reports Server (NTRS)

Eiss, N. S., Jr.; Wightman, J. P.; Gilliam, D. R.; Siochi, E. J.

1984-01-01

A proposed testing scheme is described for obtaining data on the effects of surface roughness and surface energy on insect adhesion. The road test apparatus is discussed as well as surface preparation techniques. Uncoated and polymer coated metal substrates were analyzed by SEM/ESCA/IRS before and following collision with insects. Critical surface tensions of unexposed Nyebar and poly sulfone coatings were 10 and 33 dynes/cm, respectively, as determined from contact angles. A total of 95% of insect residues collected belong to order Diptera. Significantly less insect debris was detected on the coated plates as compared to the uncoated plates. Minimal contamination at the 5 nm level of both coated and uncoated plates occurs even after hours of exposure to road conditions as determined by ESCA analysis. The presence of nitrogen detected by ESCA on exposed plates is unequivocal evidence for insect residues left on plates.

Direct morphological comparison of vacuum plasma sprayed and detonation gun sprayed hydroxyapatite coatings for orthopaedic applications.

PubMed

Gledhill, H C; Turner, I G; Doyle, C

1999-02-01

Hydroxyapatite coatings on titanium substrates were produced using two thermal spray techniques vacuum plasma spraying and detonation gun spraying. X-ray diffraction was used to compare crystallinity and residual stresses in the coatings. Porosity was measured using optical microscopy in conjunction with an image analysis system. Scanning electron microscopy and surface roughness measurements were used to characterise the surface morphologies of the coatings. The vacuum plasma sprayed coatings were found to have a lower residual stress, a higher crystallinity and a higher level of porosity than the detonation gun coatings. It is concluded that consideration needs to be given to the significance of such variations within the clinical context.

Effect of Turning and Ball Burnishing on the Microstructure and Residual Stress Distribution in Stainless Steel Cold Spray Deposits

NASA Astrophysics Data System (ADS)

Sova, A.; Courbon, C.; Valiorgue, F.; Rech, J.; Bertrand, Ph.

2017-12-01

In this paper, an experimental study of influence of machining by turning and ball burnishing on the surface morphology, structure and residual stress distribution of cold spray 17-4 PH stainless steel deposits is provided. It is shown that cold spray deposits could be machined by turning under parameters closed to turning of bulk 17-4 PH stainless steel. Ball burnishing process permits to decrease surface roughness. Cross-sectional observation revealed that the turning and ball burnishing process allowed microstructure changes in the coating near-surface zone. In particular, significant particle deformation and particle boundary fragmentation is observed. Measurements of residual stresses showed that residual stresses in the as-spray deposit are compressive. After machining by turning, tensile residual stresses in the near-surface zone were induced. Further surface finishing of turned coating by ball burnishing allowed the establishment of the compressive residual stresses in the coating.

High reflectance-low stress Mo-Si multilayer reflective coatings

DOEpatents

Montcalm, Claude; Mirkarimi, Paul B.

2000-01-01

A high reflectance-low stress Mo-Si multilayer reflective coating particularly useful for the extreme ultraviolet (EUV) wavelength region. While the multilayer reflective coating has particular application for EUV lithography, it has numerous other applications where high reflectance and low stress multilayer coatings are utilized. Multilayer coatings having high near-normal incidence reflectance (R.gtoreq.65%) and low residual stress (.ltoreq.100 MPa) have been produced using thermal and non-thermal approaches. The thermal approach involves heating the multilayer coating to a given temperature for a given time after deposition in order to induce structural changes in the multilayer coating that will have an overall "relaxation" effect without reducing the reflectance significantly.

Physical stability of arginine-glycine-aspartic acid peptide coated on anodized implants after installation.

PubMed

Huh, Jung-Bo; Lee, Jeong-Yeol; Jeon, Young-Chan; Shin, Sang-Wan; Ahn, Jin-Soo; Ryu, Jae-Jun

2013-05-01

The aim of this study was to evaluate the stability of arginine-glycine-aspartic acid (RGD) peptide coatings on implants by measuring the amount of peptide remaining after installation. Fluorescent isothiocyanate (FITC)-fixed RGD peptide was coated onto anodized titanium implants (width 4 mm, length 10 mm) using a physical adsorption method (P) or a chemical grafting method (C). Solid Rigid Polyurethane Foam (SRPF) was classified as either hard bone (H) or soft bone (S) according to its density. Two pieces of artificial bone were fixed in a customized jig, and coated implants were installed at the center of the boundary between two pieces of artificial bone. The test groups were classified as: P-H, P-S, C-H, or C-S. After each installation, implants were removed from the SRPF, and the residual amounts and rates of RGD peptide in implants were measured by fluorescence spectrometry. The Kruskal-Wallis test was used for the statistical analysis (α=0.05). Peptide-coating was identified by fluorescence microscopy and XPS. Total coating amount was higher for physical adsorption than chemical grafting. The residual rate of peptide was significantly larger in the P-S group than in the other three groups (P<.05). The result of this study suggests that coating doses depend on coating method. Residual amounts of RGD peptide were greater for the physical adsorption method than the chemical grafting method.

KEY INTERACTIONS FOR CLATHRIN COAT STABILITY

PubMed Central

Böcking, Till; Aguet, Francois; Rapoport, Iris; Banzhaf, Manuel; Yu, Anan; Zeeh, Jean Christophe; Kirchhausen, Tom

2014-01-01

SUMMARY Clathrin-coated vesicles are major carriers of vesicular traffic in eukaryotic cells. This endocytic pathway relies on cycles of clathrin coat assembly and Hsc70-mediated disassembly. Here we identify histidine residues as major determinants of lattice assembly and stability. They are located at the invariant interface between the proximal and distal segments of clathrin heavy chains, in triskelions centered on two adjacent vertices of the coated-vesicle lattice. Mutation of these histidine to glutamine alters the pH dependence of coat stability. We then describe single-particle fluorescence imaging experiments in which we follow the effect of these histidine mutations on susceptibility to Hsc70-dependent uncoating. Coats destabilized by these mutations require fewer Hsc70 molecules to initiate disassembly as predicted by a model in which Hsc70 traps conformational distortions during the auxilin- and Hsc70:ATP-mediated uncoating reaction. PMID:24815030

Advanced Coating Removal Techniques

NASA Technical Reports Server (NTRS)

Seibert, Jon

2006-01-01

An important step in the repair and protection against corrosion damage is the safe removal of the oxidation and protective coatings without further damaging the integrity of the substrate. Two such methods that are proving to be safe and effective in this task are liquid nitrogen and laser removal operations. Laser technology used for the removal of protective coatings is currently being researched and implemented in various areas of the aerospace industry. Delivering thousands of focused energy pulses, the laser ablates the coating surface by heating and dissolving the material applied to the substrate. The metal substrate will reflect the laser and redirect the energy to any remaining protective coating, thus preventing any collateral damage the substrate may suffer throughout the process. Liquid nitrogen jets are comparable to blasting with an ultra high-pressure water jet but without the residual liquid that requires collection and removal .As the liquid nitrogen reaches the surface it is transformed into gaseous nitrogen and reenters the atmosphere without any contamination to surrounding hardware. These innovative technologies simplify corrosion repair by eliminating hazardous chemicals and repetitive manual labor from the coating removal process. One very significant advantage is the reduction of particulate contamination exposure to personnel. With the removal of coatings adjacent to sensitive flight hardware, a benefit of each technique for the space program is that no contamination such as beads, water, or sanding residue is left behind when the job is finished. One primary concern is the safe removal of coatings from thin aluminum honeycomb face sheet. NASA recently conducted thermal testing on liquid nitrogen systems and found that no damage occurred on 1/6", aluminum substrates. Wright Patterson Air Force Base in conjunction with Boeing and NASA is currently testing the laser remOval technique for process qualification. Other applications of liquid

Phase evolution and thermal properties of yttria-stabilized hafnia nano-coatings deposited on alumina

NASA Astrophysics Data System (ADS)

Rubio, Ernesto Javier

High-temperature coatings are critical to the future power-generation systems and industries. Thermal barrier coatings (TBCs), which are usually the ceramic materials applied as thin coatings, protect engine components and allow further increase in engine temperatures for higher efficiency. Thus, the durability and reliability of the coating systems have to be more robust compared to current natural gas based engines. While a near and mid-term target is to develop TBC architecture with a 1300 °C surface temperature tolerance, a deeper understanding of the structure evolution and thermal behavior of the TBC-bond coat interface, specifically the thermally grown oxide (TGO), is of primary importance. In the present work, attention is directed towards yttria-stabilized hafnia (YSH) coatings on alumina (α-Al2O 3) to simulate the TBC-TGO interface and understand the phase evolution, microstructure and thermal oxidation of the coatings. YSH coatings were grown on α-Al2O3 substrates by sputter deposition by varying coating thickness in a wide range ˜30-1000 nm. The effect of coating thickness on the structure, morphology and the residual stress has been investigated using X-ray diffraction (XRD) and high resolution scanning electron microscopy (SEM). Thermal oxidation behavior of the coatings has been evaluated using the isothermal oxidation measurements under static conditions. X-ray diffraction analyses revealed the existence of monoclinic hafnia phase for relatively thin coatings indicating that the interfacial phenomena are dominant in phase stabilization. The evolution towards pure stabilized cubic phase of hafnia with the increasing coating thickness is observed. The SEM results indicate the changes in morphology of the coatings; the average grain size increases from 15 to 500 nm with increasing thickness. Residual stress was calculated employing XRD using the variable ψ-angle. Relation between residual stress and structural change is also studied. The results

Formation Mechanisms, Structure, and Properties of HVOF-Sprayed WC-CoCr Coatings: An Approach Toward Process Maps

NASA Astrophysics Data System (ADS)

Varis, T.; Suhonen, T.; Ghabchi, A.; Valarezo, A.; Sampath, S.; Liu, X.; Hannula, S.-P.

2014-08-01

Our study focuses on understanding the damage tolerance and performance reliability of WC-CoCr coatings. In this paper, the formation of HVOF-sprayed tungsten carbide-based cermet coatings is studied through an integrated strategy: First-order process maps are created by using online-diagnostics to assess particle states in relation to process conditions. Coating properties such as hardness, wear resistance, elastic modulus, residual stress, and fracture toughness are discussed with a goal to establish a linkage between properties and particle characteristics via second-order process maps. A strong influence of particle state on the mechanical properties, wear resistance, and residual stress stage of the coating was observed. Within the used processing window (particle temperature ranged from 1687 to 1831 °C and particle velocity from 577 to 621 m/s), the coating hardness varied from 1021 to 1507 HV and modulus from 257 to 322 GPa. The variation in coating mechanical state is suggested to relate to the microstructural changes arising from carbide dissolution, which affects the properties of the matrix and, on the other hand, cohesive properties of the lamella. The complete tracking of the coating particle state and its linking to mechanical properties and residual stresses enables coating design with desired properties.

Environmental Barrier Coating (EBC) Durability Modeling; An Overview and Preliminary Analysis

NASA Technical Reports Server (NTRS)

Abdul-Aziz, A.; Bhatt, R. T.; Grady, J. E.; Zhu, D.

2012-01-01

A study outlining a fracture mechanics based model that is being developed to investigate crack growth and spallation of environmental barrier coating (EBC) under thermal cycling conditions is presented. A description of the current plan and a model to estimate thermal residual stresses in the coating and preliminary fracture mechanics concepts for studying crack growth in the coating are also discussed. A road map for modeling life and durability of the EBC and the results of FEA model(s) developed for predicting thermal residual stresses and the cracking behavior of the coating are generated and described. Further initial assessment and preliminary results showed that developing a comprehensive EBC life prediction model incorporating EBC cracking, degradation and spalling mechanism under stress and temperature gradients typically seen in turbine components is difficult. This is basically due to mismatch in thermal expansion difference between sub-layers of EBC as well as between EBC and substrate, diffusion of moisture and oxygen though the coating, and densification of the coating during operating conditions as well as due to foreign object damage, the EBC can also crack and spall from the substrate causing oxidation and recession and reducing the design life of the EBC coated substrate.

Electroless Plated Nanodiamond Coating for Stainless Steel Passivation

DOE Office of Scientific and Technical Information (OSTI.GOV)

Li, D.; Korinko, P.; Spencer, W.

Tritium gas sample bottles and manifold components require passivation surface treatments to minimize the interaction of the hydrogen isotopes with surface contamination on the stainless steel containment materials. This document summarizes the effort to evaluate electroless plated nanodiamond coatings as a passivation layer for stainless steel. In this work, we developed an electroless nanodiamond (ND)-copper (Cu) coating process to deposit ND on stainless steel parts with the diamond loadings of 0%, 25% and 50% v/v in a Cu matrix. The coated Conflat Flanged Vessel Assemblies (CFVAs) were evaluated on surface morphology, composition, ND distribution, residual hydrogen release, and surface reactivitymore » with deuterium. For as-received Cu and ND-Cu coated CFVAs, hydrogen off-gassing is rapid, and the off-gas rates of H 2 was one to two orders of magnitude higher than that for both untreated and electropolished stainless steel CFVAs, and hydrogen and deuterium reacted to form HD as well. These results indicated that residual H 2 was entrapped in the Cu and ND-Cu coated CFVAs during the coating process, and moisture was adsorbed on the surface, and ND and/or Cu might facilitate catalytic isotope exchange reaction for HD formation. However, hydrocarbons (i.e., CH 3) did not form, and did not appear to be an issue for the Cu and ND-Cu coated CFVAs. After vacuum heating, residual H 2 and adsorbed H 2O in the Cu and ND-Cu coated CFVAs were dramatically reduced. The H 2 off-gassing rate after the vacuum treatment of Cu and 50% ND-Cu coated CFVAs was on the level of 10 -14 l mbar/s cm 2, while H 2O off-gas rate was on the level of 10 -15 l mbar/s cm 2, consistent with the untreated or electropolished stainless steel CFVA, but the HD formation remained. The Restek EP bottle was used as a reference for this work. The Restek Electro-Polished (EP) bottle and their SilTek coated bottles tested under a different research project exhibited very little hydrogen off-gassing and

Insect Residue Contamination on Wing Leading Edge Surfaces: A Materials Investigation for Mitigation

NASA Technical Reports Server (NTRS)

Lorenzi, Tyler M.; Wohl, Christopher J.; Penner, Ronald K.; Smith, Joseph G.; Siochi, Emilie J.

2011-01-01

Flight tests have shown that residue from insect strikes on aircraft wing leading edge surfaces may induce localized transition of laminar to turbulent flow. The highest density of insect populations have been observed between ground level and 153 m during light winds (2.6 -- 5.1 m/s), high humidity, and temperatures from 21 -- 29 C. At a critical residue height, dependent on the airfoil and Reynolds number, boundary layer transition from laminar to turbulent results in increased drag and fuel consumption. Although this represents a minimal increase in fuel burn for conventional transport aircraft, future aircraft designs will rely on maintaining laminar flow across a larger portion of wing surfaces to reduce fuel burn during cruise. Thus, insect residue adhesion mitigation is most critical during takeoff and initial climb to maintain laminar flow in fuel-efficient aircraft configurations. Several exterior treatments investigated to mitigate insect residue buildup (e.g., paper, scrapers, surfactants, flexible surfaces) have shown potential; however, implementation has proven to be impractical. Current research is focused on evaluation of wing leading edge surface coatings that may reduce insect residue adhesion. Initial work under NASA's Environmentally Responsible Aviation Program focused on evaluation of several commercially available products (commercial off-the-shelf, COTS), polymers, and substituted alkoxy silanes that were applied to aluminum (Al) substrates. Surface energies of these coatings were determined from contact angle data and were correlated to residual insect excrescence on coated aluminum substrates using a custom-built "bug gun." Quantification of insect excrescence surface coverage was evaluated by a series of digital photographic image processing techniques.

Modelling the Properties of Rock Coatings Observed by the Mars Exploration Rovers' Alpha Particle X-ray Spectrometer and Hypthesized Environments of Formation

NASA Astrophysics Data System (ADS)

Perrett, G.; Clark, B. C.; Squyres, S. W.; Campbell, J. L.

2016-12-01

Rock coatings on Mars have been of interest to the scientific community since in situ exploration of the martian surface began in the late 1970s [1-3]. The presence of rock coatings on Mars was speculative until the positive identification of a dark coating on the Adirondack-class rock Mazatzal by the MER Rover Spirit [4]. There has since been evidence for additional rock coatings at both MER and MSL rover sites [5]. These coatings are primarily Cl-rich, which suggests aqueous activity, and their formation may be common in the martian equatorial region [6]. An important objective to better understanding these coatings and their influence on geochemical data sets is to determine their thickness and various other properties [3]. For this work additional coated rocks have been identified in the MER alpha particle X-ray spectrometer (APXS) data set [7]. Using the APXS bulk chemistry for both brushed (dust-free) and abraded (coating-free) measurements on the identified targets the thicknesses, area coverage, and coating compositions have been modelled. The modelling results for the well-studied Mazatzal coating will be compared to previous studies that report thickness [8] and compositional enrichments [4] and environments of formation will be hypothesized. The formation age of the Mazatzal coating is poorly constrained but it could have conceivably formed over a period spanning much of martian history. References: [1] Binder, A.B. et al. (1977), Journal of Geophysical Research, 82:28, 4439-4451;[2] Strickland, E.L. et al. (1979), 10th LPSC, 3, 3055-3077;[3] Guinness, E.A. et al. (1996), 27th LPSC, 27, 471-472;[4] Haskin, L. A. et al. (2005), Nature, 436, 66-69;[5] Lanza, N. et al (2016), Geophysical Research Letters, 43;[6] Clark, B.C. and R. Gellert (2016), 79th Annual Meeting of the Meteoritical Society, #6079;[7] http://pds-geosciences.wustl.edu/missions/mer/mer_apxs_oxide.htm;[8] Fleischer, I. et al (2008), Hyperfine Interact, 186, 193-198.

Simulation of residual stresses and their effects on thermal barrier coating systems using finite element method

NASA Astrophysics Data System (ADS)

Zhu, JianGuo; Chen, Wei; Xie, HuiMin

2015-03-01

Thermal barrier coating (TBC) systems are widely used in industrial gas-turbine engines. However, premature failures have impaired the use of TBCs and cut down their lifetime, which requires a better understanding of their failure mechanisms. In the present study, experimental studies of isothermal cycling are firstly carried out with the observation and estimation of microstructures. According to the experimental results, a finite element model is established for the analysis of stress perpendicular to the TBC/BC interface. Detailed residual stress distributions in TBC are obtained to reflect the influence of mechanical properties, oxidation, and interfacial roughness. The calculated results show that the maximum tensile stress concentration appears at the peak of TBC and continues to increase with thermal cycles. Because of the microstructural characteristics of plasma-sprayed TBCs, cracks initialize in tensile stress concentration (TSC) regions at the peaks of TBC and propagate along the TBC/BC interface resulting in the spallation of TBC. Also, the inclusion of creep is crucial to failure prediction and is more important than the inclusion of sintering in the simulation.

Material Properties of Silicon Carbide Fibers with Continuously Applied Sol-Gel Alumina Coatings

DTIC Science & Technology

1990-12-01

71 Coating Characterization ...................... 73 iii Two-Dimensional Plane Strain Analysis .................. 78 VI ...Axial Load in the Coating of Fiber Serie T ...... .82 vi List of Figures (continued) Figure Page 39. Tangential Stress Due to Axial Load in the Coating...residual stress will be presented 17 Fiur Vi o a CaFber EfIVfef Sic=’/. Figure 1. Sectional View of a Coated Fiber first, since these stresses are of

CVD Fiber Coatings for Al2O3/NiAl Composites

NASA Technical Reports Server (NTRS)

Boss, Daniel E.

1995-01-01

While sapphire-fiber-reinforced nickel aluminide (Al2O3/NiAl) composites are an attractive candidate for high-temperature structures, the significant difference in the coefficient of thermal expansion between the NiAl matrix and the sapphire fiber creates substantial residual stresses in the composite. This study seeks to produce two fiber-coating systems with the potential to reduce the residual stresses in the sapphire/NiAl composite system. Chemical vapor deposition (CVD) was used to produce both the compensating and compliant-fiber coatings for use in sapphire/NiAl composites. A special reactor was designed and built to produce the FGM and to handle the toxic nickel precursors. This process was successfully used to produce 500-foot lengths of fiber with coating thicknesses of approximately 3 microns, 5 microns, and 10 microns.

Water treatment residual (WTR)-coated wood mulch for alleviation of toxic metals and phosphorus from polluted urban stormwater runoff.

PubMed

Soleimanifar, Hanieh; Deng, Yang; Wu, Laying; Sarkar, Dibyendu

2016-07-01

Aluminum-based water treatment residual (WTR)-coated wood mulches were synthesized and tested for removal of heavy metals and phosphorus (P) in synthetic urban stormwater. WTRs are an industrial waste produced from coagulation in water treatment facilities, primarily composed of amorphous aluminum or iron hydroxides. Batch tests showed that the composite filter media could effectively adsorb 97% lead (Pb), 76% zinc (Zn), 81% copper (Cu) and 97% P from the synthetic stormwater (Pb = 100 μg/L, Zn = 800 μg/L, Cu = 100 μg/L, P = 2.30 mg/L, and pH = 7.0) within 120 min, due to the presence of aluminum hydroxides as an active adsorbent. The adsorption was a 2(nd)-order reaction with respect toward each pollutant. Column tests demonstrated that the WTR-coated mulches considerably alleviated the select pollutants under a continuous-flow condition over the entire filtration period. The effluent Pb, Zn, Cu, and P varied at 0.5-8.9%, 33.4-46.7%, 45.8-55.8%, and 6.4-51.9% of their respective initial concentrations with the increasing bed volume from 0 to 50. Synthetic precipitation leaching procedure (SPLP) and toxicity characteristic leaching procedure (TCLP) tests indicated that leached contaminants were all below the U.S. criteria, suggesting that the release of undesired chemicals under rainfall or landfilling conditions is not a concern during application. This study demonstrates that the WTR-coated mulches are a new, low-cost, and effective filter media for urban stormwater treatment. Equally important, this study provides a sustainable approach to beneficially reuse an industrial waste for environmental pollution control. Copyright © 2016 Elsevier Ltd. All rights reserved.

Potential benefits of a ceramic thermal barrier coating on large power generation gas turbine

NASA Technical Reports Server (NTRS)

Clark, J. S.; Nainiger, J. J.

1977-01-01

Thermal barrier coating design option offers benefit in terms of reduced electricity costs when used in utility gas turbines. Options considered include: increased firing temperature, increased component life, reduced cooling air requirements, and increased corrosion resistance (resulting in increased tolerance for dirty fuels). Performance and cost data were obtained. Simple, recuperated and combined cycle applications were considered, and distillate and residual fuels were assumed. The results indicate that thermal barrier coatings could produce large electricity cost savings if these coatings permit turbine operation with residual fuels at distillate-rated firing temperatures. The results also show that increased turbine inlet temperature can result in substantial savings in fuel and capital costs.

Highly specific salt bridges govern bacteriophage P22 icosahedral capsid assembly: identification of the site in coat protein responsible for interaction with scaffolding protein.

PubMed

Cortines, Juliana R; Motwani, Tina; Vyas, Aashay A; Teschke, Carolyn M

2014-05-01

Icosahedral virus assembly requires a series of concerted and highly specific protein-protein interactions to produce a proper capsid. In bacteriophage P22, only coat protein (gp5) and scaffolding protein (gp8) are needed to assemble a procapsid-like particle, both in vivo and in vitro. In scaffolding protein's coat binding domain, residue R293 is required for procapsid assembly, while residue K296 is important but not essential. Here, we investigate the interaction of scaffolding protein with acidic residues in the N-arm of coat protein, since this interaction has been shown to be electrostatic. Through site-directed mutagenesis of genes 5 and 8, we show that changing coat protein N-arm residue 14 from aspartic acid to alanine causes a lethal phenotype. Coat protein residue D14 is shown by cross-linking to interact with scaffolding protein residue R293 and, thus, is intimately involved in proper procapsid assembly. To a lesser extent, coat protein N-arm residue E18 is also implicated in the interaction with scaffolding protein and is involved in capsid size determination, since a cysteine mutation at this site generated petite capsids. The final acidic residue in the N-arm that was tested, E15, is shown to only weakly interact with scaffolding protein's coat binding domain. This work supports growing evidence that surface charge density may be the driving force of virus capsid protein interactions. Bacteriophage P22 infects Salmonella enterica serovar Typhimurium and is a model for icosahedral viral capsid assembly. In this system, coat protein interacts with an internal scaffolding protein, triggering the assembly of an intermediate called a procapsid. Previously, we determined that there is a single amino acid in scaffolding protein required for P22 procapsid assembly, although others modulate affinity. Here, we identify partners in coat protein. We show experimentally that relatively weak interactions between coat and scaffolding proteins are capable of driving

Applications of bauxite residue: A mini-review.

PubMed

Verma, Ajay S; Suri, Narendra M; Kant, Suman

2017-10-01

Bauxite residue is the waste generated during alumina production by Bayer's process. The amount of bauxite residue (40-50 wt%) generated depends on the quality of bauxite ore used for the processing. High alkalinity and high caustic content in bauxite residue causes environmental risk for fertile soil and ground water contamination. The caustic (NaOH) content in bauxite residue leads to human health risks, like dermal problems and irritation to eyes. Moreover, disposal of bauxite residue requires a large area; such problems can only be minimised by utilising bauxite residue effectively. For two decades, bauxite residue has been used as a binder in cement industries and filler/reinforcement for composite materials in the automobile industry. Valuable metals and oxides, like alumina (Al 2 O 3 ), titanium oxide (TiO 2 ) and iron oxide Fe 2 O 3 , were extracted from bauxite residue to reduce waste. Bauxite residue was utilised in construction and structure industries to make geopolymers. It was also used in the making of glass-ceramics and a coating material. Recently bauxite residue has been utilised to extract rare earth elements like scandium (Sc), yttrium (Y), lanthanum (La), cerium (Ce), neodymium (Nd) and dysprosium (Dy). In this review article, the mineralogical characteristics of bauxite residue are summarised and current progresses on utilisation of bauxite residue in different fields of science and engineering are presented in detail.

Effects of Co contents on the microstructures and properties of the electrodeposited NiCo–Zr composite coatings

DOE Office of Scientific and Technical Information (OSTI.GOV)

Cai, Fei; Jiang, Chuanhai, E-mail: chuanhaijiang1963@163.com; Zhao, Yuantao

2015-05-15

Highlights: • The novel NiCo–Zr coatings were prepared by electro-deposition. • Surface morphology, crystal structure, grain size and microstrain were examined. • Texture, residual stress and corrosion resistance were investigated. • Addition of Co increased the hardness and corrosion resistance of the coatings. - Abstract: In this study, the NiCo–Zr composite coatings were prepared from the electrolytes with different Co{sup 2+} concentrations by electrodeposition method. The effects of Co contents on the crystal structure, surface morphology, grain size, microstrain and residual stress were examined by X-ray diffractometer (XRD), field emission scanning electron microscopy (FESEM), Energy dispersive X-ray spectroscopy (EDX) andmore » atomic force microscope (AFM). The corrosion resistance of the composite coatings was also examined by the potentiodynamic polarization and electrochemical impedance (EIS) measurements. The results revealed that the crystal structures of the coatings were dependent on the Co contents and addition of Co content of 58 wt% resulted in the formation of hexagonal (hcp) Co. The increasing Co contents in the NiCo–Zr composite coatings resulted in the smoother and more compact surface, decreased the grain size and increased the microstrain. The micro-hardness and residual stress also increased with increasing Co contents. The addition of Co increased the corrosion resistance of the NiCo–Zr composite coatings compared with the Ni–Zr coating while the corrosion resistance of the NiCo–Zr composite coatings decreased as the Co contents increased.« less

Thermal Alternating Polymer Nanocomposite (TAPNC) Coating Designed to Prevent Aerodynamic Insect Fouling

PubMed Central

Bayer, Ilker S.; Krishnan, K. Ghokulla; Robison, Robert; Loth, Eric; Berry, Douglas H.; Farrell, Thomas E.; Crouch, Jeffrey D.

2016-01-01

Insect residue adhesion to moving surfaces such as turbine blades and aircraft not only causes surface contamination problems but also increases drag on these surfaces. Insect fouling during takeoff, climb and landing can result in increased drag and fuel consumption for aircraft with laminar-flow surfaces. Hence, certain topographical and chemical features of non-wettable surfaces need to be designed properly for preventing insect residue accumulation on surfaces. In this work, we developed a superhydrophobic coating that is able to maintain negligible levels of insect residue after 100 high speed (50 m/s) insect impact events produced in a wind tunnel. The coating comprises alternating layers of a hydrophobic, perfluorinated acrylic copolymer and hydrophobic surface functional silicon dioxide nanoparticles that are infused into one another by successive thermal treatments. The design of this coating was achieved as a result of various experiments conducted in the wind tunnel by using a series of superhydrophobic surfaces made by the combination of the same polymer and nanoparticles in the form of nanocomposites with varying surface texture and self-cleaning hydrophobicity properties. Moreover, the coating demonstrated acceptable levels of wear abrasion and substrate adhesion resistance against pencil hardness, dry/wet scribed tape peel adhesion and 17.5 kPa Taber linear abraser tests. PMID:27924913

Thermal Alternating Polymer Nanocomposite (TAPNC) Coating Designed to Prevent Aerodynamic Insect Fouling.

PubMed

Bayer, Ilker S; Krishnan, K Ghokulla; Robison, Robert; Loth, Eric; Berry, Douglas H; Farrell, Thomas E; Crouch, Jeffrey D

2016-12-07

Insect residue adhesion to moving surfaces such as turbine blades and aircraft not only causes surface contamination problems but also increases drag on these surfaces. Insect fouling during takeoff, climb and landing can result in increased drag and fuel consumption for aircraft with laminar-flow surfaces. Hence, certain topographical and chemical features of non-wettable surfaces need to be designed properly for preventing insect residue accumulation on surfaces. In this work, we developed a superhydrophobic coating that is able to maintain negligible levels of insect residue after 100 high speed (50 m/s) insect impact events produced in a wind tunnel. The coating comprises alternating layers of a hydrophobic, perfluorinated acrylic copolymer and hydrophobic surface functional silicon dioxide nanoparticles that are infused into one another by successive thermal treatments. The design of this coating was achieved as a result of various experiments conducted in the wind tunnel by using a series of superhydrophobic surfaces made by the combination of the same polymer and nanoparticles in the form of nanocomposites with varying surface texture and self-cleaning hydrophobicity properties. Moreover, the coating demonstrated acceptable levels of wear abrasion and substrate adhesion resistance against pencil hardness, dry/wet scribed tape peel adhesion and 17.5 kPa Taber linear abraser tests.

Thermal Alternating Polymer Nanocomposite (TAPNC) Coating Designed to Prevent Aerodynamic Insect Fouling

NASA Astrophysics Data System (ADS)

Bayer, Ilker S.; Krishnan, K. Ghokulla; Robison, Robert; Loth, Eric; Berry, Douglas H.; Farrell, Thomas E.; Crouch, Jeffrey D.

2016-12-01

Insect residue adhesion to moving surfaces such as turbine blades and aircraft not only causes surface contamination problems but also increases drag on these surfaces. Insect fouling during takeoff, climb and landing can result in increased drag and fuel consumption for aircraft with laminar-flow surfaces. Hence, certain topographical and chemical features of non-wettable surfaces need to be designed properly for preventing insect residue accumulation on surfaces. In this work, we developed a superhydrophobic coating that is able to maintain negligible levels of insect residue after 100 high speed (50 m/s) insect impact events produced in a wind tunnel. The coating comprises alternating layers of a hydrophobic, perfluorinated acrylic copolymer and hydrophobic surface functional silicon dioxide nanoparticles that are infused into one another by successive thermal treatments. The design of this coating was achieved as a result of various experiments conducted in the wind tunnel by using a series of superhydrophobic surfaces made by the combination of the same polymer and nanoparticles in the form of nanocomposites with varying surface texture and self-cleaning hydrophobicity properties. Moreover, the coating demonstrated acceptable levels of wear abrasion and substrate adhesion resistance against pencil hardness, dry/wet scribed tape peel adhesion and 17.5 kPa Taber linear abraser tests.

The HMDS Coating Flaw Removal Tool

DOE Office of Scientific and Technical Information (OSTI.GOV)

Monticelli, M V; Nostrand, M C; Mehta, N

2008-10-24

In many high energy laser systems, optics with HMDS sol gel antireflective coatings are placed in close proximity to each other making them particularly susceptible to certain types of strong optical interactions. During the coating process, halo shaped coating flaws develop around surface digs and particles. Depending on the shape and size of the flaw, the extent of laser light intensity modulation and consequent probability of damaging downstream optics may increase significantly. To prevent these defects from causing damage, a coating flaw removal tool was developed that deploys a spot of decane with a syringe and dissolves away the coatingmore » flaw. The residual liquid is evacuated leaving an uncoated circular spot approximately 1mm in diameter. The resulting uncoated region causes little light intensity modulation and thus has a low probability of causing damage in optics downstream from the mitigated flaw site.« less

Dilation Behavior of Thermal Spray Coatings

NASA Astrophysics Data System (ADS)

Bejarano Lopez, Miryan Lorena

Thermal Spray (TS) is a very versatile manufacturing process to deposit thick coatings on a variety of substrates. Coatings are used in protective (i.e. wear, chemical attack, high temperature, etc.) and functional (i.e. sensors) applications. TS coatings have a unique lamellar microstructure as a result of the overlapping of millions of molten and partially-molten particles. During processing, high deformation by impact, high temperature, and rapid solidification lead to a complex hierarchical material system that contains a high amount of microstructural defects. The presence of defects in the microstructure contribute to differences in property values in comparison to bulk materials. Thermal stresses and residual strains arise from processing, thermal gradients and thermal exposure. Evaluation of thermal properties, in this case, the coefficient of thermal expansion (CTE) is of vital importance to enhance coating performance. In this dissertation, expansion measurements of various metals, alloys, ceramics, and cermet coatings; were carried out using various techniques (push rod dilatometry, x-ray diffraction XRD, digital image correlation DIC, and curvature method) to determine the dilation behavior at the atomic, micro- and macro-scale levels. The main results were. 1) Mathematical models (Turner and Kerner) used for composite materials, successfully predicted the CTE property of a TS coating where the primary phase is the coating material and the secondary phases can be oxides, precipitates, etc. (formed as a byproduct of the spraying process). CTE was found not to be affected by porosity. 2) Despite the anisotropic behavior characteristic of TS coatings, the experimental results shown that CTE results to be reasonable isotropic within the scope of this study. 3) The curvature method was found to be an alternative technique to obtain the CTE, as well as the Young's modulus of coating in a bi-material strip, with good approximation. 4) An anomalous expansion

Buckling of graded coatings: A continuum model

NASA Astrophysics Data System (ADS)

Chiu, Tz-Cheng

2000-12-01

Requirements for the protection of hot section components in many high temperature applications such as earth-to-orbit winged planes and advanced turbine systems have led to the application of thermal barrier coatings (TBCs) that utilize ceramic coatings on metal substrates. An alternative concept to homogeneous ceramic coatings is the functionally graded materials (FGM) in which the composition of the coating is intentionally graded to improve the bonding strength and to reduce the magnitude of the residual and thermal stresses. A widely observed failure mode in such layered systems is known to be interface cracking that leads to spallation fracture. In most cases, the final stage of the failure process for a thin coating appears to be due to buckling instability under thermally or mechanically induced compressive stress. The objective of this study is to develop a solution to the buckling instability problem by using continuum elasticity rather than a structural mechanics approach. The emphasis in the solution will be on the investigation of the effect of material inhomogeneity in graded coatings on the instability load, the postbuckling behavior, and fracture mechanics parameters such as the stress intensity factors and strain energy release rate. In this analysis, a nonlinear continuum theory is employed to examine the interface crack problem. The analytical solution of the instability problem permits the study of the effect of material inhomogeneity upon the inception of buckling and establishes benchmark results for the numerical solutions of related problems. To study the postbuckling behavior and to calculate the stress intensity factors and strain energy release rate a geometrically nonlinear finite element procedure with enriched crack-tip element is developed. Both plane strain and axisymmetric interface crack problems in TBCs with either homogeneous or graded coating are then considered by using the finite element procedure. It is assumed that the

Coating Development for GRCop-84 Liners for Reusable Launch Vehicles Aided by Modeling Studies

NASA Technical Reports Server (NTRS)

Raj, Sai V.; Ghosn, Louis J.

2004-01-01

. These temperatures are not acutely sensitive to the thermal conductivity of the top coat when it exceeds 25 and 50 W/m/K for low and high heat flux engines. This observation is significant for two reasons. First, several different top-coat compositions can be evaluated as potential protective coatings without loss in the heat-transfer efficiency of the coated system. Second, materials with thermal conductivities less than the critical values of 25 or 50 W/m/K are more likely to act as thermal barrier coatings. The deposition of overlay coatings on GRCop-84 substrates results in the development of residual stresses. The presence of these residual stresses influences the probability of coating spallation, the thermal cycling life, and the fatigue properties of the coated substrate during use. Since it is important to understand how these stresses develop during the vacuum-plasma-spraying coating deposition process, the nature and magnitudes of the cool-down residual stresses were calculated and compared with experimentally determined values across the coated cross section of a disk specimen. The calculations were conducted assuming that the specimen cools down to room temperature from vacuum plasma-spraying temperatures of either 250 or 650 C. The effects of coating the substrate with and without grit blasting were also theoretically examined. The final graph compares the predicted and the experimental results for a GRCop-84 disk coated with about a 50- m-thick Ni bond coat and a 75- to 100- m NiAl top coat, where the curves for NASA-2 assume the presence of a prior residual stress generated by grit blasting under conditions similar to the experimental situation. The predicted cool-down in-plane stresses were compressive in both the NiAl top coat and the Ni bond coat. They were also compressive in the substrate to a depth of about 0.25 mm from the Ni/GRCop-84 interface when the vacuum-plasma-spraying temperature was low. However, using a higher plasma spraying temperaturs

Thermal barrier coatings application in diesel engines

NASA Technical Reports Server (NTRS)

Fairbanks, J. W.

1995-01-01

Commercial use of thermal barrier coatings in diesel engines began in the mid 70's by Dr,. Ingard Kvernes at the Central Institute for Industrial Research in Oslo, Norway. Dr. Kvernes attributed attack on diesel engine valves and piston crowns encountered in marine diesel engines in Norwegian ships as hot-corrosion attributed to a reduced quality of residual fuel. His solution was to coat these components to reduce metal temperature below the threshold of aggressive hot-corrosion and also to provide protection. The Department of Energy has supported thermal barrier coating development for diesel engine applications. In the Clean Diesel - 50 Percent Efficient (CD-50) engine for the year 2000, thermal barrier coatings will be used on piston crowns and possibly other components. The primary purpose of the thermal barrier coatings will be to reduce thermal fatigue as the engine peak cylinder pressure will nearly be doubled. As the coatings result in higher available energy in the exhaust gas, efficiency gains are achieved through use of this energy by turbochargers, turbocompounding or thermoelectric generators.

Does impaction of titanium-coated interbody fusion cages into the disc space cause wear debris or delamination?

PubMed

Kienle, Annette; Graf, Nicolas; Wilke, Hans-Joachim

2016-02-01

A large number of interbody fusion cages are made of polyetheretherketone (PEEK). To improve bone on-growth, some are coated with a thin layer of titanium. This coating may fail when subjected to shear loading. The purpose of this testing was to investigate whether impaction of titanium-coated PEEK cages into the disc space can result in wear or delamination of the coating, and whether titanium cages with subtractive surface etching (no coating) are less susceptible to such failure. A biomechanical study was carried out to simulate the impaction process in clinical practice and to evaluate if wear or delamination may result from impaction. Two groups of posterior lumbar interbody fusion cages with a similar geometry were tested: n=6 titanium-coated PEEK and n=6 surface-etched titanium cages. The cages were impacted into the space in between two vertebral body substitutes (polyurethane foam blocks). The two vertebral body substitutes were fixed in a device, through which a standardized axial preload of 390 N was applied. The anterior tip of the cage was positioned at the posterior border of the space between the two vertebral body substitutes. The cages were then inserted using a drop weight with a mass representative of a surgical hammer. The drop weight impacted the insertion instrument at a maximum speed of about 2.6 m/s, which is in the range of the impaction speed in vivo. This was repeated until the cages were fully inserted. The wear particles were captured and analyzed according to the pertinent standards. The surface-etched titanium cages did not show any signs of wear debris or surface damage. In contrast, the titanium-coated PEEK cages resulted in detached wear particles of different sizes (1-191 µm). Over 50% of these particles had a size <10 µm. In median, on 26% of the implants' teeth, the coating was abraded. Full delamination was not observed. In contrast to the surface-etched implants, the titanium-coated PEEK implants lost some coating material

Surface protection of austenitic steels by carbon nanotube coatings

NASA Astrophysics Data System (ADS)

MacLucas, T.; Schütz, S.; Suarez, S.; Mücklich, F.

2018-03-01

In the present study, surface protection properties of multiwall carbon nanotubes (CNTs) deposited on polished austenitic stainless steel are evaluated. Electrophoretic deposition is used as a coating technique. Contact angle measurements reveal hydrophilic as well as hydrophobic wetting characteristics of the carbon nanotube coating depending on the additive used for the deposition. Tribological properties of carbon nanotube coatings on steel substrate are determined with a ball-on-disc tribometer. Effective lubrication can be achieved by adding magnesium nitrate as an additive due to the formation of a holding layer detaining CNTs in the contact area. Furthermore, wear track analysis reveals minimal wear on the coated substrate as well as carbon residues providing lubrication. Energy dispersive x-ray spectroscopy is used to qualitatively analyse the elemental composition of the coating and the underlying substrate. The results explain the observed wetting characteristics of each coating. Finally, merely minimal oxidation is detected on the CNT-coated substrate as opposed to the uncoated sample.

The effect of silicon on the oxidation behavior of NiAlHf coating system

NASA Astrophysics Data System (ADS)

Dai, Pengchao; Wu, Qiong; Ma, Yue; Li, Shusuo; Gong, Shengkai

2013-04-01

Two types of NiAlHf coatings doped with different content of Si (1 at.% and 2 at.%) were deposited on a Ni3Al based single crystal superalloy IC32 by electron beam physical vapor deposition (EB-PVD) method, respectively. For comparison, NiAlHf coating with 0 at.% Si was also prepared. The oxidation tests were carried out at 1423 K in air. At the initial stage of oxidation, large amount of flake-like θ-Al2O3 was found on NiAlHf coating surface. However, no θ-Al2O3 was observed in 2 at.% Si doped NiAlHf coating except α-Al2O3. It revealed that the Si additions could contribute to the transformation from θ-Al2O3 to α-Al2O3. When oxidation time prolonged to 100 h, it was found that the degradation of NiAlHf coating was very severe with no residual β-phase, which was due to the serious inter-diffusion between the coating and substrate. In contrast, the inter-diffusion in Si-doped coating was reduced with some residual β-phase and R-Ni(Mo, Re) precipitates. The presence of Si could retard the inter-diffusion of elements between coating and substrate, indicating a barrier diffusion effect. As a result, the oxidation resistance of NiAlHf coating was improved significantly.

Evaluation of present-day thermal barrier coatings for industrial/utility applications

NASA Technical Reports Server (NTRS)

Bratton, R. J.; Lau, S. K.; Lee, S. Y.

1980-01-01

Atmospheric burner rig tests have been conducted to evaluate the corrosion resistance of present-day thermal barrier coatings. The coatings are primarily plasma-sprayed and zirconia-based. Both duplex and graded coating systems were tested at a gas temperature of 2100 F and metal temperatures that range from 1475 F to 1650 F. The fuels ranged from clean GT No. 2 to that doped with impurity levels which simulate water-washed residual fuels. Results to date suggest that liquid sulfate condensates play an important role in the coating degradation mechanisms, whereas the role of vanadium and its salts is less clear.

Computational homogenisation for thermoviscoplasticity: application to thermally sprayed coatings

NASA Astrophysics Data System (ADS)

Berthelsen, Rolf; Denzer, Ralf; Oppermann, Philip; Menzel, Andreas

2017-11-01

Metal forming processes require wear-resistant tool surfaces in order to ensure a long life cycle of the expensive tools together with a constant high quality of the produced components. Thermal spraying is a relatively widely applied coating technique for the deposit of wear protection coatings. During these coating processes, heterogeneous coatings are deployed at high temperatures followed by quenching where residual stresses occur which strongly influence the performance of the coated tools. The objective of this article is to discuss and apply a thermo-mechanically coupled simulation framework which captures the heterogeneity of the deposited coating material. Therefore, a two-scale finite element framework for the solution of nonlinear thermo-mechanically coupled problems is elaborated and applied to the simulation of thermoviscoplastic material behaviour including nonlinear thermal softening in a geometrically linearised setting. The finite element framework and material model is demonstrated by means of numerical examples.

Quantitation of Surface Coating on Nanoparticles Using Thermogravimetric Analysis.

PubMed

Dongargaonkar, Alpana A; Clogston, Jeffrey D

2018-01-01

Nanoparticles are critical components in nanomedicine and nanotherapeutic applications. Some nanoparticles, such as metallic nanoparticles, consist of a surface coating or surface modification to aid in its dispersion and stability. This surface coating may affect the behavior of nanoparticles in a biological environment, thus it is important to measure. Thermogravimetric analysis (TGA) can be used to determine the amount of coating on the surface of the nanoparticle. TGA experiments run under inert atmosphere can also be used to determine residual metal content present in the sample. In this chapter, the TGA technique and experimental method are described.

Effects of Laser Re-melting on the Corrosion Properties of HVOF Coatings

NASA Astrophysics Data System (ADS)

Yilbas, B. S.; Toor, I. H.; Patel, F.; Baig, M. A.

2013-05-01

HVOF coating of Inconel 625 powder on carbon steel is carried out. Laser melting of the resulting coating is realized to improve coating structural integrity. Morphological and microstructural changes are examined in the coating prior and after laser treatment process using scanning electron microscopy, energy dispersive spectroscopy, and x-ray diffraction (XRD). The residual stress developed is measured on the surface vicinity of the laser-treated coating using the XRD technique. The corrosion resistance of the laser-treated and untreated coating surfaces is measured, incorporating the potentiodynamic tests in 0.5 M NaCl aqueous solution. It is found that laser treatment reduces the pores and produces cellular structures with different sizes and orientations in the coating. Laser-controlled melting improves the corrosion resistance of the coating surface.

Process for fabricating high reflectance-low stress Mo--Si multilayer reflective coatings

DOEpatents

Montcalm, Claude; Mirkarimi, Paul B.

2001-01-01

A high reflectance-low stress Mo--Si multilayer reflective coating particularly useful for the extreme ultraviolet (EUV) wavelength region. While the multilayer reflective coating has particular application for EUV lithography, it has numerous other applications where high reflectance and low stress multilayer coatings are utilized. Multilayer coatings having high near-normal incidence reflectance (R.gtoreq.65%) and low residual stress (.ltoreq.100 MPa) have been produced using thermal and non-thermal approaches. The thermal approach involves heating the multilayer coating to a given temperature for a given time after deposition in order to induce structural changes in the multilayer coating that will have an overall "relaxation" effect without reducing the reflectance significantly.

Bond Stability of a Universal Adhesive System to Eroded/Abraded Dentin After Deproteinization.

PubMed

Augusto, M G; Torres, Crg; Pucci, C R; Schlueter, N; Borges, A B

Erosive/abrasive challenges can potentially compromise bonding to dentin. Aiming to improve the quality and stability of bonding to this substrate, this study investigated the combined effect of erosion and toothbrush abrasion on the microtensile bond strength (μTBS) stability to dentin using a universal adhesive system in total and self-etching modes, associated or not associated with deproteinization. Bovine dentin specimens were divided into five groups according to the organic matrix condition (n=20): control (C); erosion (E); erosion + abrasion (EA); erosion + sodium hypochlorite (EH); erosion + abrasion + sodium hypochlorite (EAH). The groups were further divided (n=10) according to the mode of application (total or self-etching) of a universal adhesive. After the bonding procedure, composite blocks were built up, and the samples were cut to obtain sticks for μTBS testing. For each specimen, one-half of the sticks was immediately tested, and the other one-half was tested after artificial aging (5000 thermocycles, 5°C and 55°C). Three-way analysis of variance (α=5%) showed a significant difference for the triple interaction ( p=0.0007). Higher μTBS means were obtained for the EH and EAH groups compared with the E and EA groups. The control group showed immediate μTBS values similar to that of the E and EA groups for both bond strategies. Erosion and erosion/abrasion did not significantly influence the immediate μTBS to dentin. Artificial aging reduced μTBS values for the groups C, E, and EA using the total-etching mode. Deproteinization maintained the bond stability to artificially aged eroded and eroded/abraded dentin.

40 CFR 174.515 - Coat Protein of Papaya Ringspot Virus; exemption from the requirement of a tolerance.

Code of Federal Regulations, 2010 CFR

2010-07-01

... 40 Protection of Environment 23 2010-07-01 2010-07-01 false Coat Protein of Papaya Ringspot Virus...-INCORPORATED PROTECTANTS Tolerances and Tolerance Exemptions § 174.515 Coat Protein of Papaya Ringspot Virus; exemption from the requirement of a tolerance. Residues of Coat Protein of Papaya Ringspot Virus are exempt...

40 CFR 174.516 - Coat protein of cucumber mosaic virus; exemption from the requirement of a tolerance.

Code of Federal Regulations, 2010 CFR

2010-07-01

... 40 Protection of Environment 23 2010-07-01 2010-07-01 false Coat protein of cucumber mosaic virus...-INCORPORATED PROTECTANTS Tolerances and Tolerance Exemptions § 174.516 Coat protein of cucumber mosaic virus; exemption from the requirement of a tolerance. Residues of Coat Protein of Cucumber Mosaic Virus are exempt...

40 CFR 174.512 - Coat Protein of Potato Virus Y; exemption from the requirement of a tolerance.

Code of Federal Regulations, 2010 CFR

2010-07-01

... 40 Protection of Environment 23 2010-07-01 2010-07-01 false Coat Protein of Potato Virus Y...-INCORPORATED PROTECTANTS Tolerances and Tolerance Exemptions § 174.512 Coat Protein of Potato Virus Y; exemption from the requirement of a tolerance. Residues of Coat Protein of Potato Virus Y are exempt from...

40 CFR 174.512 - Coat Protein of Potato Virus Y; exemption from the requirement of a tolerance.

Code of Federal Regulations, 2012 CFR

2012-07-01

... 40 Protection of Environment 25 2012-07-01 2012-07-01 false Coat Protein of Potato Virus Y...-INCORPORATED PROTECTANTS Tolerances and Tolerance Exemptions § 174.512 Coat Protein of Potato Virus Y; exemption from the requirement of a tolerance. Residues of Coat Protein of Potato Virus Y are exempt from...

40 CFR 174.515 - Coat Protein of Papaya Ringspot Virus; exemption from the requirement of a tolerance.

Code of Federal Regulations, 2013 CFR

2013-07-01

... 40 Protection of Environment 25 2013-07-01 2013-07-01 false Coat Protein of Papaya Ringspot Virus...-INCORPORATED PROTECTANTS Tolerances and Tolerance Exemptions § 174.515 Coat Protein of Papaya Ringspot Virus; exemption from the requirement of a tolerance. Residues of Coat Protein of Papaya Ringspot Virus are exempt...

40 CFR 174.516 - Coat protein of cucumber mosaic virus; exemption from the requirement of a tolerance.

Code of Federal Regulations, 2012 CFR

2012-07-01

... 40 Protection of Environment 25 2012-07-01 2012-07-01 false Coat protein of cucumber mosaic virus...-INCORPORATED PROTECTANTS Tolerances and Tolerance Exemptions § 174.516 Coat protein of cucumber mosaic virus; exemption from the requirement of a tolerance. Residues of Coat Protein of Cucumber Mosaic Virus are exempt...

40 CFR 174.515 - Coat Protein of Papaya Ringspot Virus; exemption from the requirement of a tolerance.

Code of Federal Regulations, 2011 CFR

2011-07-01

... 40 Protection of Environment 24 2011-07-01 2011-07-01 false Coat Protein of Papaya Ringspot Virus...-INCORPORATED PROTECTANTS Tolerances and Tolerance Exemptions § 174.515 Coat Protein of Papaya Ringspot Virus; exemption from the requirement of a tolerance. Residues of Coat Protein of Papaya Ringspot Virus are exempt...

40 CFR 174.516 - Coat protein of cucumber mosaic virus; exemption from the requirement of a tolerance.

Code of Federal Regulations, 2011 CFR

2011-07-01

... 40 Protection of Environment 24 2011-07-01 2011-07-01 false Coat protein of cucumber mosaic virus...-INCORPORATED PROTECTANTS Tolerances and Tolerance Exemptions § 174.516 Coat protein of cucumber mosaic virus; exemption from the requirement of a tolerance. Residues of Coat Protein of Cucumber Mosaic Virus are exempt...

40 CFR 174.516 - Coat protein of cucumber mosaic virus; exemption from the requirement of a tolerance.

Code of Federal Regulations, 2013 CFR

2013-07-01

... 40 Protection of Environment 25 2013-07-01 2013-07-01 false Coat protein of cucumber mosaic virus...-INCORPORATED PROTECTANTS Tolerances and Tolerance Exemptions § 174.516 Coat protein of cucumber mosaic virus; exemption from the requirement of a tolerance. Residues of Coat Protein of Cucumber Mosaic Virus are exempt...

40 CFR 174.512 - Coat Protein of Potato Virus Y; exemption from the requirement of a tolerance.

Code of Federal Regulations, 2013 CFR

2013-07-01

... 40 Protection of Environment 25 2013-07-01 2013-07-01 false Coat Protein of Potato Virus Y...-INCORPORATED PROTECTANTS Tolerances and Tolerance Exemptions § 174.512 Coat Protein of Potato Virus Y; exemption from the requirement of a tolerance. Residues of Coat Protein of Potato Virus Y are exempt from...

40 CFR 174.512 - Coat Protein of Potato Virus Y; exemption from the requirement of a tolerance.

Code of Federal Regulations, 2014 CFR

2014-07-01

... 40 Protection of Environment 24 2014-07-01 2014-07-01 false Coat Protein of Potato Virus Y...-INCORPORATED PROTECTANTS Tolerances and Tolerance Exemptions § 174.512 Coat Protein of Potato Virus Y; exemption from the requirement of a tolerance. Residues of Coat Protein of Potato Virus Y are exempt from...

40 CFR 174.515 - Coat Protein of Papaya Ringspot Virus; exemption from the requirement of a tolerance.

Code of Federal Regulations, 2012 CFR

2012-07-01

... 40 Protection of Environment 25 2012-07-01 2012-07-01 false Coat Protein of Papaya Ringspot Virus...-INCORPORATED PROTECTANTS Tolerances and Tolerance Exemptions § 174.515 Coat Protein of Papaya Ringspot Virus; exemption from the requirement of a tolerance. Residues of Coat Protein of Papaya Ringspot Virus are exempt...

40 CFR 174.515 - Coat Protein of Papaya Ringspot Virus; exemption from the requirement of a tolerance.

Code of Federal Regulations, 2014 CFR

2014-07-01

... 40 Protection of Environment 24 2014-07-01 2014-07-01 false Coat Protein of Papaya Ringspot Virus...-INCORPORATED PROTECTANTS Tolerances and Tolerance Exemptions § 174.515 Coat Protein of Papaya Ringspot Virus; exemption from the requirement of a tolerance. Residues of Coat Protein of Papaya Ringspot Virus are exempt...

40 CFR 174.512 - Coat Protein of Potato Virus Y; exemption from the requirement of a tolerance.

Code of Federal Regulations, 2011 CFR

2011-07-01

... 40 Protection of Environment 24 2011-07-01 2011-07-01 false Coat Protein of Potato Virus Y...-INCORPORATED PROTECTANTS Tolerances and Tolerance Exemptions § 174.512 Coat Protein of Potato Virus Y; exemption from the requirement of a tolerance. Residues of Coat Protein of Potato Virus Y are exempt from...

40 CFR 174.516 - Coat protein of cucumber mosaic virus; exemption from the requirement of a tolerance.

Code of Federal Regulations, 2014 CFR

2014-07-01

... 40 Protection of Environment 24 2014-07-01 2014-07-01 false Coat protein of cucumber mosaic virus...-INCORPORATED PROTECTANTS Tolerances and Tolerance Exemptions § 174.516 Coat protein of cucumber mosaic virus; exemption from the requirement of a tolerance. Residues of Coat Protein of Cucumber Mosaic Virus are exempt...

Labyrinth seal testing for lift fan engines

NASA Technical Reports Server (NTRS)

Dobek, L. J.

1973-01-01

An abradable buffered labyrinth seal for the control of turbine gas path leakage in a tip-turbine driven lift fan was designed, tested, and analyzed. The seal configuration was not designed to operate in any specific location but was sized to be evaluated in an existing test rig. The final sealing diameter selected was 28 inches. Results of testing indicate that the flow equations predicted seal air flows consistent with measured values. Excellent sealing characteristics of the abradable coating on the stator land were demonstrated when a substantial seal penetration of .030 inch into the land surface was encountered without appreciable wear on the labyrinth knife edges.

40 CFR 174.531 - Coat protein of plum pox virus; exemption from the requirement of a tolerance.

Code of Federal Regulations, 2010 CFR

2010-07-01

... 40 Protection of Environment 23 2010-07-01 2010-07-01 false Coat protein of plum pox virus...-INCORPORATED PROTECTANTS Tolerances and Tolerance Exemptions § 174.531 Coat protein of plum pox virus; exemption from the requirement of a tolerance. Residues of the coat protein of plum pox virus in or on the...

40 CFR 174.531 - Coat protein of plum pox virus; exemption from the requirement of a tolerance.

Code of Federal Regulations, 2011 CFR

2011-07-01

... 40 Protection of Environment 24 2011-07-01 2011-07-01 false Coat protein of plum pox virus...-INCORPORATED PROTECTANTS Tolerances and Tolerance Exemptions § 174.531 Coat protein of plum pox virus; exemption from the requirement of a tolerance. Residues of the coat protein of plum pox virus in or on the...

40 CFR 174.531 - Coat protein of plum pox virus; exemption from the requirement of a tolerance.

Code of Federal Regulations, 2014 CFR

2014-07-01

... 40 Protection of Environment 24 2014-07-01 2014-07-01 false Coat protein of plum pox virus...-INCORPORATED PROTECTANTS Tolerances and Tolerance Exemptions § 174.531 Coat protein of plum pox virus; exemption from the requirement of a tolerance. Residues of the coat protein of plum pox virus in or on the...

40 CFR 174.531 - Coat protein of plum pox virus; exemption from the requirement of a tolerance.

Code of Federal Regulations, 2012 CFR

2012-07-01

... 40 Protection of Environment 25 2012-07-01 2012-07-01 false Coat protein of plum pox virus...-INCORPORATED PROTECTANTS Tolerances and Tolerance Exemptions § 174.531 Coat protein of plum pox virus; exemption from the requirement of a tolerance. Residues of the coat protein of plum pox virus in or on the...

40 CFR 174.531 - Coat protein of plum pox virus; exemption from the requirement of a tolerance.

Code of Federal Regulations, 2013 CFR

2013-07-01

... 40 Protection of Environment 25 2013-07-01 2013-07-01 false Coat protein of plum pox virus...-INCORPORATED PROTECTANTS Tolerances and Tolerance Exemptions § 174.531 Coat protein of plum pox virus; exemption from the requirement of a tolerance. Residues of the coat protein of plum pox virus in or on the...

Liposomes physically coated with peptides: preparation and characterization.

PubMed

Su, Cuicui; Xia, Yuqiong; Sun, Jianbo; Wang, Nan; Zhu, Lin; Chen, Tao; Huang, Yanyi; Liang, Dehai

2014-06-03

Physically coating liposomes with peptides of desirable functions is an economic, versatile, and less time-consuming approach to prepare drug delivery vehicles. In this work, we designed three peptides-Ac-WWKKKGGNNN-NH2 (W2K3), Ac-WWRRRGGNNN-NH2(W2R3), Ac-WWGGGGGNNN-NH2(W2G3)-and studied their coating ability on negatively charged liposomes. It was found that the coating was mainly driven by the electrostatic interaction between the peptides' cationic side groups and the acidic lipids, which also mediated the "anchoring " of Trp residuals in the interfacial region of lipid bilayers. At the same conditions, the amount of the coated W2R3 was more than that of W2K3, but the stability of the liposome coated with W2R3 was deteriorated. This was caused by the delocalized charge of the guanidinium group of arginine. The coating of the peptide rendered the liposome pH-responsive behavior but did not prominently change the phase transition temperature. The liposome coated with peptides displayed appropriate pH/temperature dual responsive characteristics and was able to release the content in a controlled manner.

Gas turbine coatings eddy current quantitative and qualitative evaluation

NASA Astrophysics Data System (ADS)

Ribichini, Remo; Giolli, Carlo; Scrinzi, Erica

2017-02-01

Gas turbine blades (buckets) are among the most critical and expensive components of the engine. Buckets rely on protective coatings in order to withstand the harsh environment in which they operate. The thickness and the microstructure of coatings during the lifespan of a unit are fundamental to evaluate their fitness for service. A frequency scanning Eddy Current instrument can allow the measurement of the thickness and of physical properties of coatings in a Non-Destructive manner. The method employed relies on the acquisition of impedance spectra and on the inversion of the experimental data to derive the coating properties and structure using some assumptions. This article describes the experimental validation performed on several samples and real components in order to assess the performance of the instrument as a coating thickness gage. The application of the technique to support residual life assessment of serviced buckets is also presented.

Detection of pesticide residues on individual particles.

PubMed

Whiteaker, Jeffrey R; Prather, Kimberly A

2003-01-01

An aerosol time-of-flight mass spectrometer (ATOFMS) is used to analyze the size and composition of individual particles containing pesticides. Pesticide residues are found in the atmosphere as a result of spray drift, volatilization, and suspension of coated soils. The ability of the ATOFMS to identify the presence of these contaminants on individual particles is assessed for particles created from pure solutions of several commonly used pesticides, as well as pesticides mixed with an organic matrix, and coated on soils. The common names of the pesticides studied are 2,4-D, atrazine, chlorpyrifos, malathion, permethrin, and propoxur. Analysis of the mass spectra produced by single- and two-step laser desorption/ionization of pesticide-containing particles allows for identification of peaks that can be used for detection of pesticide residues in the ambient aerosol. The identified marker peaks are used to approximate detection limits for the pesticides applied to soils, which are on the order of a fraction of a monolayer for individual particles. Results suggest that this technique may be useful for studying the real-time partitioning and distribution of pesticides in the atmosphere immediately following application in agricultural regions.

"Combined Occlusion and Atropine Therapy" Versus "Augmented Part-Time Patching" in Children with Refractory/Residual Amblyopia: A Pilot Study.

PubMed

Sachdeva, Virender; Mittal, Vaibhev; Gupta, Varun; Gunturu, Rekha; Kekunnaya, Ramesh; Chandrasekharan, Anjali; Chabblani, Preeti Patil; Rao, Harsha L

2016-01-01

To compare the efficacy of combined occlusion and atropine therapy (COAT) and augmented part-time patching for the treatment of unilateral refractory/residual amblyopia. This retrospective study evaluated children between 4 and 11 years with refractory/residual amblyopia who were treated with either additional atropine (COAT group) or increased hours of patching (augmented group). Data were collected on improvement in best-corrected visual acuity (BCVA; logarithm of the minimum angle of resolution [logMAR] units) at each follow-up visit. There were 19 children in the COAT group and 17 children in the augmented group. The baseline BCVA of the amblyopic eye was 0.79 ± 0.36 logMAR in the COAT group and 0.72 ± 0.26 logMAR in augmented group. Children were statistically significantly younger in the COAT group (6.4 ± 2.2 years) compared to the augmented group (8.6 ± 3.3 years, P = 0.02). The mean duration of follow-up was statistically significantly longer in the augmented group (20.2 COAT group; 13.9 months augmented group) (P = 0.03). Compliance was similar in both groups. LogMAR BCVA (adjusted for difference in age and baseline BCVA) was statistically significantly better in the COAT group (0.56 ± 0.04) compared to the augmented group (0.80 ± 0.04) at 3 months (P = 0.000); 6 months (COAT group, 0.50 ± 0.04 vs. augmented group, 0.74 ± 0.04; P = 0.04) and at 1 year (COAT group, 0.42 ± 0.04 vs. augmented group, 0.67 ± 0.04, P = 0.000). There was statistically significantly greater improvement in logMAR BCVA at 6 months in COAT group (0.26 ± 0.15) compared to the augmented group (0.02 ± 0.14), (P = 0.0002). Age, gender, pretreatment BCVA, duration of follow-up, or compliance to patching did not affect improvement in BCVA. COAT may result in greater improvement in BCVA than augmented part-time patching in children with unilateral residual/refractory amblyopia.

Influences of metal ions crosslinked alginate based coatings on thermal stability and fire resistance of cotton fabrics.

PubMed

Pan, Ying; Wang, Wei; Liu, Longxiang; Ge, Hua; Song, Lei; Hu, Yuan

2017-08-15

Bio-based and phosphorus-free coating was fabricated by layer-by-layer assembly method to obtain the flame retardant cotton fabric. For the first time, the modified cotton fabrics were prepared by utilizing positively charged polyethylenimine and negatively charged alginate together with subsequent crosslinking of barium, nickel and cobalt ions. Scanning electron microscopy and energy-dispersive X-ray demonstrated that the metal ions crosslinked coating was successfully constructed on the substrate. The thermal stability and flame retardancy were investigated by thermogravimetric analysis (TGA) and horizontal flame tests. TGA results showed that the degradation of the coated cotton fabrics were retarded at high temperature and the char residue of the cotton fabrics were improved after covered with the barium, nickel and cobalt ions crosslinked coatings. Furthermore, the fire resistance of cotton-Ba sample was enhanced significantly compared with the untreated sample, as evidenced by the obvious reduction (28%) of flame spread rate and complete char residue. Finally, the washing durability of coating on the fabric was enhanced after metal ions crosslinked with alginate based coating. Copyright © 2017. Published by Elsevier Ltd.

Effects of thermal cycling parameters on residual stresses in alumina scales of CoNiCrAlY and NiCoCrAlY bond coats

DOE PAGES

Nordhorn, Christian; Mücke, Robert; Unocic, Kinga A.; ...

2014-08-20

In this paper, furnace cycling experiments were performed on free-standing high-velocity oxygen-fuel bond coat samples to investigate the effect of material composition, surface texture, and cycling conditions on the average stresses in the formed oxide scales after cooling. The oxide scale thicknesses were determined by SEM image analyses and information about the stresses were acquired by photo-stimulated luminescence-spectroscopy. Additionally, the scale thickness dependent stress fields were calculated in finite-element analyses including approximation functions for the surface roughness derived on the basis of profilometry data. The evolution of the average residual stress as a function of oxide scale thickness was subjectmore » to stochastic fluctuations predominantly caused by local scale spallations. In comparison to the supplemental modeling results, thermal stresses due to mismatch of thermal expansion coefficients are identified as the main contribution to the residual stresses. Finally, the theoretical results emphasize that analyses of spectroscopic data acquired for average stress investigations of alumina scales rely on detailed information about microstructural features.« less

40 CFR 174.514 - Coat Protein of Watermelon Mosaic Virus-2 and Zucchini Yellow Mosaic Virus; exemption from the...

Code of Federal Regulations, 2010 CFR

2010-07-01

... 40 Protection of Environment 23 2010-07-01 2010-07-01 false Coat Protein of Watermelon Mosaic... Coat Protein of Watermelon Mosaic Virus-2 and Zucchini Yellow Mosaic Virus; exemption from the requirement for a tolerance. Residues of Coat Protein of Watermelon Mosaic Virus-2 and Zucchini Yellow Mosaic...

Deposition of dual-layer coating on Ti6Al4V

NASA Astrophysics Data System (ADS)

Hussain Din, Sajad; Shah, M. A.; Sheikh, N. A.

2017-03-01

Dual-layer diamond coatings were deposited on titanium alloy (Ti6Al4V) using a hot filament chemical vapour deposition technique with the anticipation of studying the structural and morphology properties of the alloy. The coated diamond films were characterized using scanning electron microscope, x-ray diffraction (XRD), and Raman spectroscopy. The XRD studies reveal that the deposited films are highly crystalline in nature, whereas morphological studies show that the films have a cauliflower structure. XRD analysis was used to calculate the structural parameters of the Ti6Al4V and CVD-coated Ti6Al4V. Raman spectroscopy was used to determine the nature and magnitude of the residual stress of the coatings.

Characteristics of hydroxyapatite coated titanium porous coatings on Ti-6Al-4V substrates by plasma sprayed method.

PubMed

Yang, C Y; Chen, C R; Chang, E; Lee, T M

2007-08-01

A porous metal coating applied to solid substrate implants has been shown, in vivo, to anchor implants by bone ingrowth. Calcium phosphate ceramics, in particular hydroxyapatite [Ca(10)(PO(4))(6)(OH)(2), HA], are bioactive ceramics, which are known to be biocompatible and osteoconductive, and these ceramics deposited on to porous-coated devices may enhance bone ingrowth and implant fixation. In this study, bi-feedstock of the titanium powder and composite (Na(2)CO(3)/HA) powder were simultaneously deposited on a Ti-6Al-4V substrate by a plasma sprayed method. At high temperature of plasma torch, the solid state of Na(2)CO(3) would decompose to release CO(2) gas and then eject the molten Ti powder to induce the interconnected pores in the coatings. After cleaning and soaking in deionized water, the residual Na(2)CO(3) in the coating would dissolve to form the open pores, and the HA would exist at the surface of pores in the inner coatings. By varying the particle size of the composite powder, the porosity of porous coating could be varied from 25.0 to 34.0%, and the average pore size of the porous coating could be varied to range between 158.5 and 202.0 microm. Using a standard adhesive test (ASTM C-633), the bonding strength of the coating is between 27.3 and 38.2 MPa. By SEM, the HA was observed at the surface of inner pore in the porous coating. These results suggest that the method exhibits the potential to manufacture the bioactive ceramics on to porous-coated specimen to achieve bone ingrowth fixation for biomedical applications.

Multilayer composition coatings for cutting tools: formation and performance properties

NASA Astrophysics Data System (ADS)

Tabakov, Vladimir P.; Vereschaka, Anatoly S.; Vereschaka, Alexey A.

2018-03-01

The paper considers the concept of a multi-layer architecture of the coating in which each layer has a predetermined functionality. Latest generation of coatings with multi-layered architecture for cutting tools secure a dual nature of the coating, in which coatings should not only improve the mechanical and physical characteristics of the cutting tool material, but also reduce the thermo-mechanical effect on the cutting tool determining wear intensity. Here are presented the results of the development of combined methods of forming multi-layer coatings with improved properties. Combined method of forming coatings using a pulsed laser allowed reducing excessively high levels of compressive residual stress and increasing micro hardness of the multilayered coatings. The results in testing coated HSS tools showed that the use of additional pulse of laser processing increases tool life up to 3 times. Using filtered cathodic vacuum arc deposition for the generation of multilayer coatings based on TiAlN compound has increased the wear-resistance of carbide tools by 2 fold compared with tool life of cutting tool with commercial TiN coatings. The aim of this study was to develop an innovative methodological approach to the deposition of multilayer coatings for cutting tools with functional architectural selection, properties and parameters of the coating based on sound knowledge of coating failure in machining process.

Mo doped DLC nanocomposite coatings with improved mechanical and blood compatibility properties

NASA Astrophysics Data System (ADS)

Tang, X. S.; Wang, H. J.; Feng, L.; Shao, L. X.; Zou, C. W.

2014-08-01

Mo (molybdenum) doped diamond like carbon (Mo-DLC) coatings with improved mechanical and blood compatibility properties were deposited by closed field unbalanced magnetron sputtering. The undoped and Mo-doped DLC coatings were analyzed by various characterization techniques such as Raman spectra, Atomic force microscopy, and temperature-dependent frictional wear testing. The results showed that the Mo-DLC coating with low Mo concentration was a effective protective coating with reduced residual stress and increased cohesive strength, and kept good wear resistance at the ambient temperature of 500 °C. The blood compatibility of Mo-DLC coatings was investigated by platelet adhesion. The results showed that the amount of thrombus on the Mo-DLC nanocomposite coatings was much less than that of thrombus on pyrolytic carbon films. The Mo-DLC nanocomposite coatings would be a new kind of promising materials applied to artificial heart valve and endovascula stent.

Enhanced fatigue performance of porous coated Ti6Al4V biomedical alloy

NASA Astrophysics Data System (ADS)

Apachitei, I.; Leoni, A.; Riemslag, A. C.; Fratila-Apachitei, L. E.; Duszczyk, J.

2011-05-01

Biofunctional coatings are necessary to improve integration of titanium implants in the host tissue but they may be detrimental for the implant fatigue properties. This study presents an attempt towards enhancement of the in vitro fatigue strength of plasma electrolytic oxidation coated Ti6Al4V alloy by applying shot peening process prior to coating. The electrolytic oxidation was performed in calcium acetate and calcium glycerophosphate electrolytes that allowed formation of porous oxide coatings with high surface free energy and apatite like ability. A deformed surface layer coupled with induced residual compressive stresses seem to affect oxide growth rate and fatigue behavior of the titanium alloy.

Correlating Coating Characteristics with the Performance of Drug-Coated Balloons – A Comparative In Vitro Investigation of Own Established Hydrogel- and Ionic Liquid-Based Coating Matrices

PubMed Central

Kaule, Sebastian; Minrath, Ingo; Stein, Florian; Kragl, Udo; Schmidt, Wolfram; Schmitz, Klaus-Peter; Sternberg, Katrin; Petersen, Svea

2015-01-01

Drug-coated balloons (DCB), which have emerged as a therapeutic alternative to drug-eluting stents in percutaneous cardiovascular intervention, are well described with regard to clinical efficacy and safety within a number of clinical studies. In vitro studies elucidating the correlation between coating additive and DCB performance are however rare but considered important for the understanding of DCB requirements and the improvement of established DCB. In this regard, we examined three different DCB-systems, which were developed in former studies based on the ionic liquid cetylpyridinium salicylate, the body-own hydrogel hyaluronic acid and the pharmaceutically well-established hydrogel polyvinylpyrrolidone, considering coating morphology, coating thickness, drug-loss, drug-transfer to the vessel wall, residual drug-concentration on the balloon surface and entire drug-load during simulated use in an in vitro vessel model. Moreover, we investigated particle release of the different DCB during simulated use and determined the influence of the three coatings on the mechanical behavior of the balloon catheter. We could show that coating characteristics can be indeed correlated with the performance of DCB. For instance, paclitaxel incorporation in the matrix can reduce the drug wash-off and benefit a high drug transfer. Additionally, a thin coating with a smooth surface and high but delayed solubility can reduce drug wash-off and decrease particle burden. As a result, we suggest that it is very important to characterize DCB in terms of mentioned properties in vitro in addition to their clinical efficacy in order to better understand their function and provide more data for the clinicians to improve the tool of DCB in coronary angioplasty. PMID:25734818

Influence of Surface Properties and Impact Conditions on Adhesion of Insect Residues

NASA Technical Reports Server (NTRS)

Wohl, Christopher J.; Smith, Joseph G.; Connell, John W.; Siochi, Emilie J.; Doss, Jereme R.; Shanahan, Michelle H.; Penner, Ronald K.

2015-01-01

Insect residues can cause premature transition to turbulent flow on laminar flow airfoils. Engineered surfaces that mitigate the adhesion of insect residues provide, therefore, a route to more efficient aerodynamics and reduced fuel burn rates. Areal coverage and heights of residues depend not only on surface properties, but also on impact conditions. We report high speed photography of fruit fly impacts at different angles of inclination on a rigid aluminum surface, optical microscopy and profilometry, and contact angle goniometry to support the design of engineered surfaces. For the polyurethane and epoxy coatings studied, some of which exhibited superhydrophobicity, it was determined that impact angle and surface compositions play critical roles in the efficacy of these surfaces to reduce insect residue adhesion.

Laser shock peening without coating induced residual stress distribution, wettability characteristics and enhanced pitting corrosion resistance of austenitic stainless steel

NASA Astrophysics Data System (ADS)

Prabhakaran, S.; Kulkarni, Aniket; Vasanth, G.; Kalainathan, S.; Shukla, Pratik; Vasudevan, Vijay K.

2018-01-01

Low energy laser shock peening without coating (LSPwC) was conducted on AISI 304 austenitic stainless steel specimens with varying pulse densities or overlapping. Highest magnitude of compressive residual stress (CRS) was achieved for an optimized pulse density of 2500 pulses/cm2 (75% overlapping). The 2-D and 3-D topographical analysis were indicative of the fact that controlled roughening of the surface was achieved after the LSPwC process. After the LSPwC process, the hydrophilic unpeened surface was converted into the hydrophobic surface, thus decreasing the wettability characteristics of the surface. The X-ray diffraction (XRD) results reveal that there is a beginning of the martensite transformation and the rise in the intensity value of the peaks after LSPwC indicates the presence of compressive residual stresses induced in the specimen. The optical microscope and high-resolution transmission electron microscope results provided evidence of grain refinement and deformation induced refinement features such as multidirectional mechanical twinning, dislocations lines, micro shear cells and stacking faults in the near and sub-surface areas. The average hardness value of the LSPwC specimens was found to be increased by 28% more than the untreated specimen. The potentiodynamic polarization revealed that there was a considerable amount of increase in the pitting corrosion resistance after the LSPwC process, thus, supporting to extend the fatigue life of the specimen. The electrochemical impedance spectroscopic (EIS) analysis depicts that the LSPwC process supports the formation of the strong passivation layer in 3.5% NaCl solution.

Surface protection coating material for controlling the decay of major construction stone

NASA Astrophysics Data System (ADS)

Arun, T.; Ray, D. K.; Gupta, V. P.; Panda, S. S.; Sahoo, P. K.; Ghosh, Jaydip; Sengupta, Pranesh; Satyam, P. V.

2017-05-01

Degradation of the building stones are creating instability in the old building and monuments which is to be protected. To investigate the characteristics of such a stones used for the construction in eastern India, we have collected the khondalite stones. The microstructural and elemental composition analysis of the khondalite stones are analyzed by using SEM, EDX and PIXE trace elemental analysis. We have prepared surface protection coating material with graphene oxide and cobalt ferrite as a base material along with other residuals. The prepared coating materials is coated on the galvanized iron substrate for further characterization. The surface morphology characteristics of the coating material is analyzed by SEM and AFM. The corrosion resistance characteristics of the prepared coating material is studied by the electrochemical impedance spectroscopy. The results suggests that the prepared coating material can be used as a surface protection materials to control the self-destruction of khondalite stones.

A fundamental study of the sticking of insect residues to aircraft wings

NASA Technical Reports Server (NTRS)

Eiss, N. S., Jr.; Wightman, J. P.; Gilliam, D. R.; Siochi, E. J.

1985-01-01

The aircraft industry has long been concerned with the increase of drag on airplanes due to fouling of the wings by insects. The present research studied the effects of surface energy and surface roughness on the phenomenon of insect sticking. Aluminum plates of different roughnesses were coated with thin films of polymers with varying surface energies. The coated plates were attached to a custom jig and mounted on top of an automobile for insect collection. Contact angle measurements, X-ray photoelectron spectroscopy and specular reflectance infrared spectroscopy were used to characterize the surface before and after the insect impact experiments. Scanning electron microscopy showed the topography of insect residues on the exposed plates. Moments were calculated in order to find a correlation between the parameters studied and the amount of bugs collected on the plates. An effect of surface energy on the sticking of insect residues was demonstrated.

The macroscopic, microscopic and spectrometric effects of various chemotherapeutic agents on the plasma-sprayed hydroxyapatite-coated implant surface.

PubMed

Zablotsky, M; Meffert, R; Mills, O; Burgess, A; Lancaster, D

1992-12-01

The purpose of this research was to determine the nature of the residual hydroxyapatite (HA)-coated implant surface after treatment with various chemotherapeutic modalities, including: citric acid, chlorhexidine gluconate, hydrogen peroxide, tetracycline HCl, stannous fluoride, polymyxin B and a prototype plastic Cavitron tip. Implant surfaces were evaluated macroscopically, microscopically (scanning electron microscopy (SEM)) and spectrometrically (energy-dispersive spectrometry and X-ray diffraction). HA-substrate bond strength and dissolution testing was also performed for surfaces treated with a supersaturated citric acid solution. All treatments left either microscopic residues or a loss of surface roughness when viewed on SEM. A 30- to 60-s application of citric acid left a significantly greater coating thickness than all other treatments, whereas a 3-min application of citric acid removed significantly more HA than untreated controls. Significant changes in Ca/P ratios were seen with most treatments. The clinical significance of this phenomenon is not known. No treatments altered the crystallinity of the residual HA coating. A 1-min application of citric acid did not significantly alter the tensile bond strength of the coating to the substrate. The clinical significance of these findings is not known at present. However, when taken with results from previous studies, it appears that in treating the infected HA-coated implant surface, a 30- to 60-s application of citric acid (pH 1) may be beneficial in detoxifying the HA coating prior to regenerative procedures. Further in vitro and in vivo studies are necessary to evaluate the biological response to citric acid when used to detoxify the infected implant surface.

Guanidine Soaps As Vehicles For Coating Ceramic Fibers

NASA Technical Reports Server (NTRS)

Philipp, Warren H.; Veitch, Lisa C.; Jaskowiak, Martha H.

1994-01-01

Soaps made from strong organic base guanidine and organic fatty acids serve as vehicles and binders for coating ceramic fibers, various smooth substrates, and other problematic surfaces with thin precious-metal or metal-oxide films. Films needed to serve as barriers to diffusion in fiber/matrix ceramic composite materials. Guanidine soaps entirely organic and burn off, leaving no residues.

Val-->Ala mutations selectively alter helix-helix packing in the transmembrane segment of phage M13 coat protein.

PubMed Central

Deber, C M; Khan, A R; Li, Z; Joensson, C; Glibowicka, M; Wang, J

1993-01-01

Val-->Ala mutations within the effective transmembrane segment of a model single-spanning membrane protein, the 50-residue major coat (gene VIII) protein of bacteriophage M13, are shown to have sequence-dependent impacts on stabilization of membrane-embedded helical dimeric structures. Randomized mutagenesis performed on the coat protein hydrophobic segment 21-39 (YIGYAWAMV-VVIVGATIGI) produced a library of viable mutants which included those in which each of the four valine residues was replaced by an alanine residue. Significant variations found among these Val-->Ala mutants in the relative populations and thermal stabilities of monomeric and dimeric helical species observed on SDS/PAGE, and in the range of their alpha-helix-->beta-sheet transition temperatures confirmed that intramembranous valine residues are not simply universal contributors to membrane anchoring. Additional analyses of (i) nonmutatable sites in the mutant protein library, (ii) the properties of the double mutant V29A-V31A obtained by recycling mutant V31A DNA through mutagenesis procedures, and (iii) energy-minimized helical dimer structures of wild-type and mutant V31A transmembrane regions indicated that the transmembrane hydrophobic core helix of the M13 coat protein can be partitioned into alternating pairs of potential protein-interactive residues (V30, V31; G34, A35; G38, I39) and membrane-interactive residues (M28, V29; I32, V33; T36, I37). The overall results consitute an experimental approach to categorizing the distinctive contributions to structure of the residues comprising a protein-protein packing interface vs. those facing lipid and confirm the sequence-dependent capacity of specific residues within the transmembrane domain to modulate protein-protein interactions which underlie regulatory events in membrane proteins. Images Fig. 2 Fig. 4 PMID:8265602

Val-->Ala mutations selectively alter helix-helix packing in the transmembrane segment of phage M13 coat protein.

PubMed

Deber, C M; Khan, A R; Li, Z; Joensson, C; Glibowicka, M; Wang, J

1993-12-15

Val-->Ala mutations within the effective transmembrane segment of a model single-spanning membrane protein, the 50-residue major coat (gene VIII) protein of bacteriophage M13, are shown to have sequence-dependent impacts on stabilization of membrane-embedded helical dimeric structures. Randomized mutagenesis performed on the coat protein hydrophobic segment 21-39 (YIGYAWAMV-VVIVGATIGI) produced a library of viable mutants which included those in which each of the four valine residues was replaced by an alanine residue. Significant variations found among these Val-->Ala mutants in the relative populations and thermal stabilities of monomeric and dimeric helical species observed on SDS/PAGE, and in the range of their alpha-helix-->beta-sheet transition temperatures confirmed that intramembranous valine residues are not simply universal contributors to membrane anchoring. Additional analyses of (i) nonmutatable sites in the mutant protein library, (ii) the properties of the double mutant V29A-V31A obtained by recycling mutant V31A DNA through mutagenesis procedures, and (iii) energy-minimized helical dimer structures of wild-type and mutant V31A transmembrane regions indicated that the transmembrane hydrophobic core helix of the M13 coat protein can be partitioned into alternating pairs of potential protein-interactive residues (V30, V31; G34, A35; G38, I39) and membrane-interactive residues (M28, V29; I32, V33; T36, I37). The overall results consitute an experimental approach to categorizing the distinctive contributions to structure of the residues comprising a protein-protein packing interface vs. those facing lipid and confirm the sequence-dependent capacity of specific residues within the transmembrane domain to modulate protein-protein interactions which underlie regulatory events in membrane proteins.

Modified Surface Having Low Adhesion Properties to Mitigate Insect Residue Adhesion

NASA Technical Reports Server (NTRS)

Wohl, Christopher J., Jr. (Inventor); Smith, Joseph G., Jr. (Inventor); Siochi, Emilie J. (Inventor); Penner, Ronald K. (Inventor)

2016-01-01

A process to modify a surface to provide reduced adhesion surface properties to mitigate insect residue adhesion. The surface may include the surface of an article including an aircraft, an automobile, a marine vessel, all-terrain vehicle, wind turbine, helmet, etc. The process includes topographically and chemically modifying the surface by applying a coating comprising a particulate matter, or by applying a coating and also topographically modifying the surface by various methods, including but not limited to, lithographic patterning, laser ablation and chemical etching, physical vapor phase deposition, chemical vapor phase deposition, crystal growth, electrochemical deposition, spin casting, and film casting.

Development of a plasma sprayed ceramic gas path seal for high pressure turbine applications

NASA Technical Reports Server (NTRS)

Shiembob, L. T.

1977-01-01

The plasma sprayed graded layered yittria stabilized zirconia (ZrO2)/metal(CoCrAlY) seal system for gas turbine blade tip applications up to 1589 K (2400 F) seal temperatures was studied. Abradability, erosion, and thermal fatigue characteristics of the graded layered system were evaluated by rig tests. Satisfactory abradability and erosion resistance was demonstrated. Encouraging thermal fatigue tolerance was shown. Initial properties for the plasma sprayed materials in the graded, layered seal system was obtained, and thermal stress analyses were performed. Sprayed residual stresses were determined. Thermal stability of the sprayed layer materials was evaluated at estimated maximum operating temperatures in each layer. Anisotropic behavior in the layer thickness direction was demonstrated by all layers. Residual stresses and thermal stability effects were not included in the analyses. Analytical results correlated reasonably well with results of the thermal fatigue tests. Analytical application of the seal system to a typical gas turbine engine application predicted performance similar to rig specimen thermal fatigue performance. A model for predicting crack propagation in the sprayed ZrO2/CoCrAlY seal system was proposed, and recommendations for improving thermal fatigue resistance were made. Seal system layer thicknesses were analytically optimized to minimize thermal stresses in the abradability specimen during thermal fatigue testing. Rig tests on the optimized seal configuration demonstrated some improvement in thermal fatigue characteristics.

Evaluation of present thermal barrier coatings for potential service in electric utility gas turbines

NASA Technical Reports Server (NTRS)

Bratton, R. J.; Lau, S. K.; Lee, S. Y.

1982-01-01

The resistance of present-day thermal barrier coatings to combustion gases found in electric utility turbines was assessed. The plasma sprayed coatings, both duplex and graded types, were primarily zirconia-based, although a calcium silicate was also evaluated. Both atmospheric burner rig tests and high pressure tests (135 psig) showed that several present-day thermal barrier coatings have a high potential for service in gas turbines burning the relatively clean GT No. 2 fuel. However, coating improvements are needed for use in turbines burning lower grade fuel such as residual oil. The duplex ZrO2.8Y2O3/NiCrA1Y coating was ranked highest and selected for near-term field testing, with Ca2SiO4/NiCrA1Y ranked second. Graded coatings show potential for corrosive turbine operating conditions and warrant further development. The coating degradation mechanisms for each coating system subjected to the various environmental conditions are also described.

“Combined Occlusion and Atropine Therapy” Versus “Augmented Part-Time Patching” in Children with Refractory/Residual Amblyopia: A Pilot Study

PubMed Central

Sachdeva, Virender; Mittal, Vaibhev; Gupta, Varun; Gunturu, Rekha; Kekunnaya, Ramesh; Chandrasekharan, Anjali; Chabblani, Preeti Patil; Rao, Harsha L.

2016-01-01

Purpose: To compare the efficacy of combined occlusion and atropine therapy (COAT) and augmented part-time patching for the treatment of unilateral refractory/residual amblyopia. Methodology: This retrospective study evaluated children between 4 and 11 years with refractory/residual amblyopia who were treated with either additional atropine (COAT group) or increased hours of patching (augmented group). Data were collected on improvement in best-corrected visual acuity (BCVA; logarithm of the minimum angle of resolution [logMAR] units) at each follow-up visit. Results: There were 19 children in the COAT group and 17 children in the augmented group. The baseline BCVA of the amblyopic eye was 0.79 ± 0.36 logMAR in the COAT group and 0.72 ± 0.26 logMAR in augmented group. Children were statistically significantly younger in the COAT group (6.4 ± 2.2 years) compared to the augmented group (8.6 ± 3.3 years, P = 0.02). The mean duration of follow-up was statistically significantly longer in the augmented group (20.2 COAT group; 13.9 months augmented group) (P = 0.03). Compliance was similar in both groups. LogMAR BCVA (adjusted for difference in age and baseline BCVA) was statistically significantly better in the COAT group (0.56 ± 0.04) compared to the augmented group (0.80 ± 0.04) at 3 months (P = 0.000); 6 months (COAT group, 0.50 ± 0.04 vs. augmented group, 0.74 ± 0.04; P = 0.04) and at 1 year (COAT group, 0.42 ± 0.04 vs. augmented group, 0.67 ± 0.04, P = 0.000). There was statistically significantly greater improvement in logMAR BCVA at 6 months in COAT group (0.26 ± 0.15) compared to the augmented group (0.02 ± 0.14), (P = 0.0002). Age, gender, pretreatment BCVA, duration of follow-up, or compliance to patching did not affect improvement in BCVA. Conclusions: COAT may result in greater improvement in BCVA than augmented part-time patching in children with unilateral residual/refractory amblyopia. PMID:27162453

Masking technique for coating thickness control on large and strongly curved aspherical optics.

PubMed

Sassolas, B; Flaminio, R; Franc, J; Michel, C; Montorio, J-L; Morgado, N; Pinard, L

2009-07-01

We discuss a method to control the coating thickness deposited onto large and strongly curved optics by ion beam sputtering. The technique uses an original design of the mask used to screen part of the sputtered materials. A first multielement mask is calculated from the measured two-dimensional coating thickness distribution. Then, by means of an iterative process, the final mask is designed. By using such a technique, it has been possible to deposit layers of tantalum pentoxide having a high thickness gradient onto a curved substrate 500 mm in diameter. Residual errors in the coating thickness profile are below 0.7%.

Structurally Integrated, Damage-Tolerant, Thermal Spray Coatings

NASA Astrophysics Data System (ADS)

Vackel, Andrew; Dwivedi, Gopal; Sampath, Sanjay

2015-07-01

Thermal spray coatings are used extensively for the protection and life extension of engineering components exposed to harsh wear and/or corrosion during service in aerospace, energy, and heavy machinery sectors. Cermet coatings applied via high-velocity thermal spray are used in aggressive wear situations almost always coupled with corrosive environments. In several instances (e.g., landing gear), coatings are considered as part of the structure requiring system-level considerations. Despite their widespread use, the technology has lacked generalized scientific principles for robust coating design, manufacturing, and performance analysis. Advances in process and in situ diagnostics have provided significant insights into the process-structure-property-performance correlations providing a framework-enhanced design. In this overview, critical aspects of materials, process, parametrics, and performance are discussed through exemplary studies on relevant compositions. The underlying connective theme is understanding and controlling residual stresses generation, which not only addresses process dynamics but also provides linkage for process-property relationship for both the system (e.g., fatigue) and the surface (wear and corrosion). The anisotropic microstructure also invokes the need for damage-tolerant material design to meet future goals.

Effects of laser remelting on microstructures and immersion corrosion performance of arc sprayed Al coating in 3.5% NaCl solution

NASA Astrophysics Data System (ADS)

Sun, Ze; Zhang, Donghui; Yan, Baoxu; Kong, Dejun

2018-02-01

An arc sprayed aluminum (Al) coating on S355 steel was processed using a laser remelting (LR). The microstructures, chemical element composition, and phases of the obtained Al coating were analyzed using a field mission scanning electronic microscope (FESEM), energy dispersive spectrometer (EDS), and X-ray diffractometer (XRD), respectively, and the residual stresses were measured using an X-ray diffraction stress tester. The immersion corrosion tests and potentiodynamic polarization of Al coating in 3.5% NaCl solution were performed to investigate the effects of LR on its immersion corrosion behaviors, and the corrosion mechanism of Al coating was also discussed. The results show that the arc sprayed Al coating is composed of Al phase, while that by LR is composed of Al-Fe and AlO4FeO6 phases, and the porosities and cracks in the arc sprayed Al coating are eliminated by LR, The residual stress of arc sprayed Al coating is -5.6 ± 18 MPa, while that after LR is 137.9 ± 12 MPa, which deduces the immersion corrosion resistance of Al coating. The corrosion mechanism of arc sprayed Al coating is pitting corrosion and crevice corrosion, while that by LR is uniform corrosion and pitting corrosion. The corrosion potential of arc sprayed Al coating by LR shifts positively, which improves its immersion corrosion resistance.

Quantifying the mode II critical strain energy release rate of borate bioactive glass coatings on Ti6Al4V substrates.

PubMed

Matinmanesh, A; Li, Y; Clarkin, O; Zalzal, P; Schemitsch, E H; Towler, M R; Papini, M

2017-11-01

Bioactive glasses have been used as coatings for biomedical implants because they can be formulated to promote osseointegration, antibacterial behavior, bone formation, and tissue healing through the incorporation and subsequent release of certain ions. However, shear loading on coated implants has been reported to cause the delamination and loosening of such coatings. This work uses a recently developed fracture mechanics testing methodology to quantify the critical strain energy release rate under nearly pure mode II conditions, G IIC , of a series of borate-based glass coating/Ti6Al4V alloy substrate systems. Incorporating increasing amounts of SrCO 3 in the glass composition was found to increase the G IIC almost twofold, from 25.3 to 46.9J/m 2 . The magnitude and distribution of residual stresses in the coating were quantified, and it was found that the residual stresses in all cases distributed uniformly over the cross section of the coating. The crack was driven towards, but not into, the glass/Ti6Al4V substrate interface due to the shear loading. This implied that the interface had a higher fracture toughness than the coating itself. Copyright © 2017 Elsevier Ltd. All rights reserved.

Microstructures and Properties of Laser Cladding Al-TiC-CeO₂ Composite Coatings.

PubMed

He, Xing; Kong, Dejun; Song, Renguo

2018-01-26

Al-TiC-CeO₂ composite coatings have been prepared by using a laser cladding technique, and the microstructure and properties of the resulting composite coatings have been investigated using scanning electron microscopy (SEM), a 3D microscope system, X-ray diffraction (XRD), micro-hardness testing, X-ray stress measurements, friction and wear testing, and an electrochemical workstation. The results showed that an Al-Fe phase appears in the coatings under different applied laser powers and shows good metallurgical bonding with the matrix. The dilution rate of the coating first decreases and then increases with increasing laser power. The coating was transformed from massive and short rod-like structures into a fine granular structure, and the effect of fine grain strengthening is significant. The microhardness of the coatings first decreases and then increases with increasing laser power, and the maximum microhardness can reach 964.3 HV 0.2 . In addition, the residual stress of the coating surface was tensile stress, and crack size increases with increasing stress. When the laser power was 1.6 kW, the coating showed high corrosion resistance.

Wear mechanisms of the biotribological nanocomposite a-C : H coatings implanted by metallic nanoparticles.

PubMed

Major, L; Janusz, M; Lackner, J M; Kot, M; Dyner, M; Major, B

2017-10-01

Recently, to reduce the residual stress and increase the mechanical properties of a-C:H coatings, metallic nanoparticles have been implanted into their structure. In the present work, to improve the properties of the coating, metallic nanoparticles, including Cu, Nb, Ta, Zr, AgPt and Ag, were inserted into the a-C:H structure. The applied biological and mechanical analysis allowed the optimal biotribological parameters to be indicated for the potential application as protective coatings for metallic medical tools. Wear mechanisms operating at the small length of the designed biotribological coating, such as a-C:H implanted by Zr nanoparticles, were studied by means of transmission electron microscopy (TEM). The TEM analysis confirmed very good coating adhesion to the metallic substrate. © 2017 The Authors Journal of Microscopy © 2017 Royal Microscopical Society.

Effect of Thickness on the Structure, Composition and Properties of Titanium Nitride Nano-Coatings

DOE Office of Scientific and Technical Information (OSTI.GOV)

Martinez, Gustavo; Shutthanandan, V.; Thevuthasan, Suntharampillai

2014-05-05

Titanium nitride (TiNx) coatings were grown by magnetron sputtering onto Si(1 0 0) substrates by varying time of deposition to produce coatings with variable thickness (dTiN) in the range of 20-120 nm. TiNx coatings were characterized by studying their structure, composition, and mechanical properties. Nuclear reaction analysis (NRA) combined with Rutherford backscattering spectrometry (RBS) analyses indicate that the grown coatings were stoichiometric TiN. Grazing incidence X-ray diffraction (GIXRD) measurements indicate that the texturing of TiN coatings changes as a function of dTiN. The (1 1 1) and (0 0 2) peaks appear initially; (1 1 1) becomes intense while (0more » 0 2) disappears with increasing dTiN. Dense, columnar grain structure was evident for all the coatings in electron microscopy analyses. The residual stress for TiN coatings with dTiN~120 nm was 1.07 GPa in compression while thinner samples exhibit higher values of stress.« less

Fire performance, microstructure and thermal degradation of an epoxy based nano intumescent fire retardant coating for structural applications

DOE Office of Scientific and Technical Information (OSTI.GOV)

Aziz, Hammad, E-mail: engr.hammad.aziz03@gmail.com; Ahmad, Faiz, E-mail: faizahmad@petronas.com.my; Yusoff, P. S. M. Megat

Intumescent fire retardant coating (IFRC) is a passive fire protection system which swells upon heating to form expanded multi-cellular char layer that protects the substrate from fire. In this research work, IFRC’s were developed using different flame retardants such as ammonium polyphosphate, expandable graphite, melamine and boric acid. These flame retardants were bound together with the help of epoxy binder and cured together using curing agent. IFRC was then reinforced with nano magnesium oxide and nano alumina as inorganic fillers to study their effect towards fire performance, microstructure and thermal degradation. Small scale fire test was conducted to investigate themore » thermal insulation of coating whereas fire performance was calculated using thermal margin value. Field emission scanning electron microscopy was used to examine the microstructure of char obtained after fire test. Thermogravimetric analysis was conducted to investigate the residual weight of coating. Results showed that the performance of the coating was enhanced by reinforcement with nano size fillers as compared to non-filler based coating. Comparing both nano size magnesium oxide and nano size alumina; nano size alumina gave better fire performance with improved microstructure of char and high residual weight.« less

Fire performance, microstructure and thermal degradation of an epoxy based nano intumescent fire retardant coating for structural applications

NASA Astrophysics Data System (ADS)

Aziz, Hammad; Ahmad, Faiz; Yusoff, P. S. M. Megat; Zia-ul-Mustafa, M.

2015-07-01

Intumescent fire retardant coating (IFRC) is a passive fire protection system which swells upon heating to form expanded multi-cellular char layer that protects the substrate from fire. In this research work, IFRC's were developed using different flame retardants such as ammonium polyphosphate, expandable graphite, melamine and boric acid. These flame retardants were bound together with the help of epoxy binder and cured together using curing agent. IFRC was then reinforced with nano magnesium oxide and nano alumina as inorganic fillers to study their effect towards fire performance, microstructure and thermal degradation. Small scale fire test was conducted to investigate the thermal insulation of coating whereas fire performance was calculated using thermal margin value. Field emission scanning electron microscopy was used to examine the microstructure of char obtained after fire test. Thermogravimetric analysis was conducted to investigate the residual weight of coating. Results showed that the performance of the coating was enhanced by reinforcement with nano size fillers as compared to non-filler based coating. Comparing both nano size magnesium oxide and nano size alumina; nano size alumina gave better fire performance with improved microstructure of char and high residual weight.

Antireflective graded index silica coating, method for making

DOEpatents

Yoldas, Bulent E.; Partlow, Deborah P.

1985-01-01

Antireflective silica coating for vitreous material is substantially non-reflecting over a wide band of radiations. This is achieved by providing the coating with a graded degree of porosity which grades the index of refraction between that of air and the vitreous material of the substrate. To prepare the coating, there is first prepared a silicon-alkoxide-based coating solution of particular polymer structure produced by a controlled proportion of water to alkoxide and a controlled concentration of alkoxide to solution, along with a small amount of catalyst. The primary solvent is alcohol and the solution is polymerized and hydrolized under controlled conditions prior to use. The prepared solution is applied as a film to the vitreous substrate and rapidly dried. It is thereafter heated under controlled conditions to volatilize the hydroxyl radicals and organics therefrom and then to produce a suitable pore morphology in the residual porous silica layer. The silica layer is then etched in order to enlarge the pores in a graded fashion, with the largest of the pores remaining being sufficiently small that radiations to be passed through the substrate are not significantly scattered. For use with quartz substrates, extremely durable coatings which display only 0.1% reflectivity have been prepared.

40 CFR 174.514 - Coat Protein of Watermelon Mosaic Virus-2 and Zucchini Yellow Mosaic Virus; exemption from the...

Code of Federal Regulations, 2014 CFR

2014-07-01

... Virus-2 and Zucchini Yellow Mosaic Virus; exemption from the requirement for a tolerance. 174.514... Coat Protein of Watermelon Mosaic Virus-2 and Zucchini Yellow Mosaic Virus; exemption from the requirement for a tolerance. Residues of Coat Protein of Watermelon Mosaic Virus-2 and Zucchini Yellow Mosaic...

40 CFR 174.514 - Coat Protein of Watermelon Mosaic Virus-2 and Zucchini Yellow Mosaic Virus; exemption from the...

Code of Federal Regulations, 2013 CFR

2013-07-01

... Virus-2 and Zucchini Yellow Mosaic Virus; exemption from the requirement for a tolerance. 174.514... Coat Protein of Watermelon Mosaic Virus-2 and Zucchini Yellow Mosaic Virus; exemption from the requirement for a tolerance. Residues of Coat Protein of Watermelon Mosaic Virus-2 and Zucchini Yellow Mosaic...

40 CFR 174.514 - Coat Protein of Watermelon Mosaic Virus-2 and Zucchini Yellow Mosaic Virus; exemption from the...

Code of Federal Regulations, 2011 CFR

2011-07-01

... Virus-2 and Zucchini Yellow Mosaic Virus; exemption from the requirement for a tolerance. 174.514... Coat Protein of Watermelon Mosaic Virus-2 and Zucchini Yellow Mosaic Virus; exemption from the requirement for a tolerance. Residues of Coat Protein of Watermelon Mosaic Virus-2 and Zucchini Yellow Mosaic...

40 CFR 174.514 - Coat Protein of Watermelon Mosaic Virus-2 and Zucchini Yellow Mosaic Virus; exemption from the...

Code of Federal Regulations, 2012 CFR

2012-07-01

... Virus-2 and Zucchini Yellow Mosaic Virus; exemption from the requirement for a tolerance. 174.514... Coat Protein of Watermelon Mosaic Virus-2 and Zucchini Yellow Mosaic Virus; exemption from the requirement for a tolerance. Residues of Coat Protein of Watermelon Mosaic Virus-2 and Zucchini Yellow Mosaic...

Microstructural design of functionally graded coatings composed of suspension plasma sprayed hydroxyapatite and bioactive glass.

PubMed

Cattini, Andrea; Bellucci, Devis; Sola, Antonella; Pawłowski, Lech; Cannillo, Valeria

2014-04-01

Various bioactive glass/hydroxyapatite (HA) functional coatings were designed by the suspension plasma spraying (SPS) technique. Their microstructure, scratch resistance, and apatite-forming ability in a simulated body fluid (SBF) were compared. The functional coatings design included: (i) composite coating, that is, randomly distributed constituent phases; (ii) duplex coating with glass top layer onto HA layer; and (iii) graded coating with a gradual changing composition starting from pure HA at the interface with the metal substrate up to pure glass on the surface. The SPS was a suitable coating technique to produce all the coating designs. The SBF tests revealed that the presence of a pure glass layer on the working surface significantly improved the reactivity of the duplex and graded coatings, but the duplex coating suffered a relatively low scratch resistance because of residual stresses. The graded coating therefore provided the best compromise between mechanical reliability and apatite-forming ability in SBF. © 2013 Wiley Periodicals, Inc. J Biomed Mater Res Part B: Appl Biomater, 102B: 551-560, 2014. Copyright © 2013 Wiley Periodicals, Inc.

Uveal Melanoma Mimicking Advanced Coats' Disease in a Young Patient.

PubMed

Gupta, Naina; Terrell, William; Schoenfield, Lynn; Kirsch, Claudia; Cebulla, Colleen M

2016-04-01

To report a case and the unique histopathology of a necrotic uveal melanoma mimicking advanced Coats' disease in a young adult. A 26-year-old male presented with a blind, painful eye, total exudative retinal detachment, and bulbous aneurysms consistent with Coats' disease. No masses were visualized on ultrasound or CT scan, and the patient underwent enucleation of the eye. Histopathology of the involved eye confirmed a necrotic uveal melanoma with persistent spindle cells forming a collar around residual tumor vessels. Careful consideration is needed in approaching any patient with a blind, painful eye and opaque media, even in younger populations.

An electro-conductive organic coating for scanning electron microscopy (déjà vu)

NASA Astrophysics Data System (ADS)

Burnett, Bryan R.

2014-09-01

An organic compound, originally marketed as an antistatic, can form an extremely thin electro-conductive coating upon drying. A scanning electron microscope (SEM) application for this compound was first explored in the late 1960s. A coating of this compound eliminates the need for carbon or gold coating in some applications. It is well suited for the viewing of fabric samples and associated gunshot residue (GSR) in the SEM and makes it possible to quickly analyze fabric bullet wipe and bore wipe GSR. Fabric samples can also be examined for GSR from intermediate-range shots to estimate muzzle-target distances. Scanning

Evidence for lysine acetylation in the coat protein of a Polerovirus

USDA-ARS?s Scientific Manuscript database

Virions of the RPV strain of Cereal yellow dwarf virus (CYDV-RPV) were purified from infected oat tissue and analyzed by mass spectrometry. Two conserved residues, K147 and K181, residing in the virus coat protein, were confidently identified to contain epsilon-N-acetyl groups. While no functional ...

Joint DoD Demonstration And Validation Of Magnesium-Rich Primer Coating Technology

DTIC Science & Technology

2012-01-01

Recovery Act SCE .....................................Standard Calomel Electrode xi TCP ..................................... Trivalent Chromium ...8 performed the best, followed by trivalent chromium pretreatment (TCP), with the panel that did not receive any chemical pretreatment performing...Abraded) MIL-DTL-81706 Type II – Trivalent Chromium (Alodine T5900) MIL-DTL-81706 Type I – Hexavalent Chromium No Chemical Pretreatment MIL-DTL-81706

Vacuum Sputtered and Ion-Plated Coatings for Wear and Corrosion Protection

NASA Technical Reports Server (NTRS)

Spalvins, T.

1982-01-01

The plasma or ion-assisted coating techniques such as sputtering and ion plating are discussed in view of wear and corrosion protection. The basic processes and the unique features of the technique are discussed in regard to the synthesis and development of high reliability wear and corrosion resistant films. The ions of the plasma which transfer energy, momentum, and charge to the substrate and the growing films can be beneficially used. As a result, coating adherence and cohesion is improved. Favorable morphological growth such as high density and porosity-free films can be developed, and residual stresses can be reduced.

High temperature glass thermal control structure and coating. [for application to spacecraft reusable heat shielding

NASA Technical Reports Server (NTRS)

Stewart, D. A.; Goldstein, H. E.; Leiser, D. B. (Inventor)

1983-01-01

A high temperature stable and solar radiation stable thermal control coating is described which is useful either as such, applied directly to a member to be protected, or applied as a coating on a re-usable surface insulation (RSI). It has a base coat layer and an overlay glass layer. The base coat layer has a high emittance, and the overlay layer is formed from discrete, but sintered together glass particles to give the overlay layer a high scattering coefficient. The resulting two-layer space and thermal control coating has an absorptivity-to-emissivity ratio of less than or equal to 0.4 at room temperature, with an emittance of 0.8 at 1200 F. It is capable of exposure to either solar radiation or temperatures as high as 2000 F without significant degradation. When used as a coating on a silica substrate to give an RSI structure, the coatings of this invention show significantly less reduction in emittance after long term convective heating and less residual strain than prior art coatings for RSI structures.

Damage tolerant functionally graded materials for advanced wear and friction applications

NASA Astrophysics Data System (ADS)

Prchlik, Lubos

The research work presented in this dissertation focused on processing effects, microstructure development, characterization and performance evaluation of composite and graded coatings used for friction and wear control. The following issues were addressed. (1) Definition of prerequisites for a successful composite and graded coating formation by means of thermal spraying. (2) Improvement of characterization methods available for homogenous thermally sprayed coating and their extension to composite and graded materials. (3) Development of novel characterization methods specifically for FGMs, with a focus on through thickness property measurement by indentation and in-situ curvature techniques. (4) Design of composite materials with improved properties compared to homogenous coatings. (5) Fabrication and performance assessment of FGM with improved wear and impact damage properties. Materials. The materials studied included several material systems relevant to low friction and contact damage tolerant applications: MO-Mo2C, WC-Co cermets as materials commonly used sliding components of industrial machinery and NiCrAlY/8%-Yttria Partially Stabilized Zirconia composites as a potential solution for abradable sections of gas turbines and aircraft engines. In addition, uniform coatings such as molybdenum and Ni5%Al alloy were evaluated as model system to assess the influence of microstructure variation onto the mechanical property and wear response. Methods. The contact response of the materials was investigated through several techniques. These included methods evaluating the relevant intrinsic coating properties such as elastic modulus, residual stress, fracture toughness, scratch resistance and tests measuring the abrasion and friction-sliding behavior. Dry-sand and wet two-body abrasion testing was performed in addition to traditional ball on disc sliding tests. Among all characterization techniques the spherical indentation deserved most attention and enabled to

Development of nanostructured PVD coatings for total knee replacement joints using HIPIMS

NASA Astrophysics Data System (ADS)

Sugumaran, Arunprabhu A.

The aim of this study was to develop thin film coatings for total knee replacement joints using high power impulse magnetron sputtering (HIPIMS). An industrial size four cathode magnetron sputtering system equipped with direct current (DC) and HIPIMS power supplies was used for this purpose. Initially, Plasma diagnostics were carried out using optical emission spectroscopy (OES) while sputtering Ti target in Ar + N2 atmosphere by utilizing various HIP IMS/conventional DCMS (henceforth UBM) source combinations by varying the process parameters such as coil current and N2 flow. Then, single layer titanium nitride (TiN) coating was deposited by varying the degree of HIPIMS utilisation and the process parameters such as bias voltage and coil current to thoroughly understand the effect of degree of HIPIMS utilisation on the microstructure, residual stress, texture, mechanical, tribological and corrosion properties of such coatings. The degree of HIPIMS utilisation was altered by increasing the number of HIPIMS targets used for the deposition. Four different source combinations were used for this purpose, as follows: 4 cathodes in conventional DCMS mode to deposit pure UBM coating, 1 HIPIMS + 3UBM and 2HIPIMS + 2UBM cathodes to deposit combined HIPIMS/UBM coatings and 2HIPIMS cathodes to deposit pure HIPIMS coatings. TiN/NbN, TiCN/NbCN and CrN/NbN multilayer coatings were deposited on CoCr alloy test buttons along with other (HSS, SS and Si) substrates since our intended application is on total knee replacement joints made of CoCr alloy. The knowledge gained by investigating the TiN (Ar + N[2]) plasma and the properties of TiN was used to determine the process parameters for depositing the multilayer coatings. X- ray diffraction (XRD) technique was used for calculating the texture, residual stress and bilayer thickness of the coatings. Nanoindentation method was used to determine the nano hardness of the coatings. The adhesion strength of the coatings was estimated by

CrAlN coating to enhance the power loss and magnetostriction in grain oriented electrical steel

NASA Astrophysics Data System (ADS)

Goel, Vishu; Anderson, Philip; Hall, Jeremy; Robinson, Fiona; Bohm, Siva

2016-05-01

Grain oriented electrical steels (GOES) are coated with aluminium orthophosphate on top of a forsterite (Mg2SiO4) layer to provide stress and insulation resistance to reduce the power loss and magnetostriction. In this work Chromium Aluminium Nitride (CrAlN) was coated on GOES samples with electron beam physical vapour deposition and was tested in the single strip and magnetostriction tester to measure the power loss and magnetostriction before and after coating. Power loss was reduced by 2% after coating and 6 % post annealing at 800 °C. For applied compressive stress of 6 MPa, the magnetostrictive strain was zero with the CrAlN coating as compared to 22 and 24 μɛ for fully finished GOES and GOES without phosphate coating. The thickness of the coating was found to be 1.9 ± 0.2 μm estimated with Glow Discharge Optical Emission Spectroscopy (GDOES). The magnetic domain imaging showed domain narrowing after coating. The reduction in power loss and magnetostriction was due to the large residual compressive stress and Young's modulus (270 GPa) of the coating.

Thin coatings for heavy industry: Advanced coatings for pipes and valves

NASA Astrophysics Data System (ADS)

Vernhes, Luc

investigation of an HVOF 80/20 Cr 3C2-NiCr coating failure in an on-off metal-seated ball valve (MSBV) used in supercritical steam lines in a power plant, along with an assessment of alternative coating solutions that are less susceptible to this failure mode. HVOF 80/20 Cr3C2-NiCr coating has been used to protect thousands of MSBVs without incident. However, in this case the valves were challenged with exposure to rapid variations in high-pressure flow and temperature, resulting in a unique situation that caused the coating to undergo cracking and cohesive failure. Carbide precipitation was found to be a major factor, resulting in coating embrittlement. Reduced coating toughness and ductility allowed thermal, mechanical, and residual stresses to initiate cracks and propagate them more easily, leading to coating failure with exposure to thermal shock. To alleviate these issues, possible coating alternatives were assessed. The third article presents the mechanical, tribological, and corrosion properties of two novel hybrid coating systems: 1) a tungsten-tungsten carbide (W-WC) top layer and a laser cladded cobalt-chromium (Co-Cr) interlayer (StelliteRTM 6 superalloy) applied to a 316 stainless steel substrate; and 2) the same W-WC top layer and an HVOF spray-and-fused Ni-W-Cr-B interlayer (ColmonoyRTM 88 superalloy) applied to an InconelRTM 718 substrate. X-ray diffraction, energy dispersive spectroscopy, and scanning electron microscopy were used to analyze the microstructure of the coating layers. Microindentation was used to measure surface hardness and the hardness profile of the coating systems. Rockwell indentation was used to assess coating adhesion according to CEN/TS 1071-8. Surface load-carrying capacity was also assessed by measuring micro- and macrohardness at high loads. Tribological properties were assessed with a linear reciprocating ball-on-flat sliding wear test, and corrosion resistance was measured by potentiodynamic polarization and electrochemical impedance

Thermal Expansion of Vacuum Plasma Sprayed Coatings

NASA Technical Reports Server (NTRS)

Raj, S V.; Palczer, A. R.

2010-01-01

Metallic Cu-8%Cr, Cu-26%Cr, Cu-8%Cr-1%Al, NiAl and NiCrAlY monolithic coatings were fabricated by vacuum plasma spray deposition processes for thermal expansion property measurements between 293 and 1223 K. The corrected thermal expansion, (DL/L(sub 0) varies with the absolute temperature, T, as (DL/L(sub 0) = A(T - 293)(sup 3) + BIT - 293)(sup 2) + C(T - 293) + D, where, A, B, C and D are thermal, regression constants. Excellent reproducibility was observed for all of the coatings except for data obtained on the Cu-8%Cr and Cu-26%Cr coatings in the first heat-up cycle, which deviated from those determined in the subsequent cycles. This deviation is attributed to the presence of residual stresses developed during the spraying of the coatings, which are relieved after the first heat-up cycle. In the cases of Cu-8%Cr and NiAl, the thermal expansion data were observed to be reproducible for three specimens. The linear expansion data for Cu-8% Cr and Cu-26%Cr agree extremely well with rule of mixture (ROM) predictions. Comparison of the data for the Cu-8%Cr coating with literature data for Cr and Cu revealed that the thermal expansion behavior of this alloy is determined by the Cu-rich matrix. The data for NiAl and NiCrAlY are in excellent agreement with published results irrespective of composition and the methods used for processing the materials. The implications of these results on coating GRCop-84 copper alloy combustor liners for reusable launch vehicles are discussed.

Understanding cracking failures of coatings: A fracture mechanics approach

NASA Astrophysics Data System (ADS)

Kim, Sung-Ryong

A fracture mechanics analysis of coating (paint) cracking was developed. A strain energy release rate (G(sub c)) expression due to the formation of a new crack in a coating was derived for bending and tension loadings in terms of the moduli, thicknesses, Poisson's ratios, load, residual strain, etc. Four-point bending and instrumented impact tests were used to determine the in-situ fracture toughness of coatings as functions of increasing baking (drying) time. The system used was a thin coating layer on a thick substrate layer. The substrates included steel, aluminum, polycarbonate, acrylonitrile-butadiene-styrene (ABS), and Noryl. The coatings included newly developed automotive paints. The four-point bending configuration promoted nice transversed multiple coating cracks on both steel and polymeric substrates. The crosslinked type automotive coatings on steel substrates showed big cracks without microcracks. When theoretical predictions for energy release rate were compared to experimental data for coating/steel substrate samples with multiple cracking, the agreement was good. Crosslinked type coatings on polymeric substrates showed more cracks than theory predicted and the G(sub c)'s were high. Solvent evaporation type coatings on polymeric substrates showed clean multiple cracking and the G(sub c)'s were higher than those obtained by tension analysis of tension experiments with the same substrates. All the polymeric samples showed surface embrittlement after long baking times using four-point bending tests. The most apparent surface embrittlement was observed in the acrylonitrile-butadiene-styrene (ABS) substrate system. The impact properties of coatings as a function of baking time were also investigated. These experiments were performed using an instrumented impact tester. There was a rapid decrease in G(sub c) at short baking times and convergence to a constant value at long baking times. The surface embrittlement conditions and an embrittlement toughness

Improvement in the properties of plasma-sprayed metallic, alloy and ceramic coatings using dry-ice blasting

NASA Astrophysics Data System (ADS)

Dong, Shujuan; Song, Bo; Hansz, Bernard; Liao, Hanlin; Coddet, Christian

2011-10-01

Dry-ice blasting, as an environmental-friendly method, was introduced into atmospheric plasma spraying for improving properties of metallic, alloy and ceramic coatings. The deposited coatings were then compared with coatings plasma-sprayed using conventional air cooling in terms of microstructure, temperature, oxidation, porosity, residual stress and adhesion. It was found that a denser steel or CoNiCrAlY alloy coating with a lower content of oxide can be achieved with the application of dry-ice blasting during the plasma spraying. In addition, the adhesive strength of Al 2O 3 coating deposited with dry-ice blasting exceeded 60 MPa, which was nearly increased by 30% compared with that of the coating deposited with conventional air cooling. The improvement in properties of plasma-sprayed metallic, alloy and ceramic coatings caused by dry-ice blasting was attributed to the decrease of annulus-ringed disk like splats, the better cooling efficiency of dry-ice pellets and even the mechanical effect of dry-ice impact.

Fabrication and Anti-Oxidation Ability of SiC-SiO₂ Coated Carbon Fibers Using Sol-Gel Method.

PubMed

Yang, Guangyuan; Huang, Zhixiong; Wang, Xu; Wang, Bo

2018-02-27

The paper proposed a method to improve the anti-oxidation performance of carbon fibers (CF) at high temperature environment by coating silicon dioxide (SiO₂) and silicon carbide (SiC). The modified sol-gel method had been used to ensure the proper interface between fibers and coating. We used polydimethylsiloxane and ethyl orthosilicate to make stable emulsion to uniformly disperse SiC nanoparticles. The modified SiO₂/SiC coating had been coated on CF successfully. Compared with the untreated CF, the coated fibers started to be oxidized around 900 °C and the residual weight was 57% at 1400 °C. The oxidation mechanism had been discussed. The structure of SiC/SiO₂ coated CF had been characterized by scanning electron microscope and X-ray diffraction analysis. Thermal gravimetric analysis was used to test the anti-oxidation ability of CF with different coatings.

Microstructures and Properties of Laser Cladding Al-TiC-CeO2 Composite Coatings

PubMed Central

Kong, Dejun; Song, Renguo

2018-01-01

Al-TiC-CeO2 composite coatings have been prepared by using a laser cladding technique, and the microstructure and properties of the resulting composite coatings have been investigated using scanning electron microscopy (SEM), a 3D microscope system, X-ray diffraction (XRD), micro-hardness testing, X-ray stress measurements, friction and wear testing, and an electrochemical workstation. The results showed that an Al-Fe phase appears in the coatings under different applied laser powers and shows good metallurgical bonding with the matrix. The dilution rate of the coating first decreases and then increases with increasing laser power. The coating was transformed from massive and short rod-like structures into a fine granular structure, and the effect of fine grain strengthening is significant. The microhardness of the coatings first decreases and then increases with increasing laser power, and the maximum microhardness can reach 964.3 HV0.2. In addition, the residual stress of the coating surface was tensile stress, and crack size increases with increasing stress. When the laser power was 1.6 kW, the coating showed high corrosion resistance. PMID:29373555

Metal organic chemical vapor deposition of environmental barrier coatings for the inhibition of solid deposit formation from heated jet fuel

NASA Astrophysics Data System (ADS)

Mohan, Arun Ram

deposits depending on the surface acidity of the coatings. In the last part of the study, the residual carbon was incorporated in the zirconia coating by deposition with and without oxygen. As carbon surface is less active towards coke deposition, presence of residual carbon in the coating was expected to reduce its activity towards carbon deposition. The residual carbon in the coating was characterized by Raman spectroscopy and thermal analysis. However, it has been observed that residual carbon in the coating beyond a certain concentration compromises the integrity of the coating during the process of cooling the substrate from deposition temperature to room temperature. It has been found that residual carbon in the zirconia coating does not appear to affect the activity of the surface towards carbon deposition.

Influence of substrate temperature on properties of MgF 2 coatings

NASA Astrophysics Data System (ADS)

Yu, Hua; Qi, Hongji; Cui, Yun; Shen, Yanming; Shao, JianDa; Fan, ZhengXiu

2007-05-01

Thermal boat evaporation was employed to prepare MgF 2 single-layer coatings upon both JGS1 and UBK7 substrates at different substrate temperatures. Microstructure, transmittance and residual stress of these coatings were measured by X-ray diffraction, spectrophotometer, and optical interferometer, respectively. Measurement of laser induced damage threshold (LIDT) of the samples was performed at 355 nm, 8 ns pulses. The results showed that high substrate temperature was beneficial to crystallization of the film. Above 244 °C, the refractive index increased gradually with the substrate temperature rising. Whereas, it was exceptional at 210 °C that the refractive index was higher than those deposited at 244 and 277 °C. The tensile residual stresses were exhibited in all MgF 2 films, but not well correlated with the substrate temperature. In addition, the stresses were comparatively smaller upon JGS1 substrates. A tendency could be seen that the LIDTs reached the highest values at about 244 °C, and the films upon JGS1 had higher LIDTs than those upon UBK7 substrates at the same temperature. Meanwhile, the damage morphologies showed that the laser damage of the coating resulted from an absorbing center at the film-substrate interface. The features of the damages were displayed by an absorbing center dominated model. Furthermore, the reason of the difference in LIDT values was discussed in detail.

Effect of basalt fibres reinforcement and aluminum trihydrate on the thermal properties of intumescent fire retardant coatings

NASA Astrophysics Data System (ADS)

Yasir, Muhammad; Amir, Norlaili Binti; Ahmad, Faiz; Syahirah Rodzhan, N.

2017-08-01

This research is carried out in order to study the synergistic effect of aluminium trihydrate and basalt fibres on the properties of fire resistant intumescent coatings. Intumescent fire retardant coatings were developed using different flame retardants such as ammonium polyphosphate, expandable graphite, melamine and boric acid. These flame retardants were bound together with the help of epoxy binder along with curing agent. Furthermore, individual and combinations of aluminium trihydrate and basalt fibres was incorporated in the formulations to analyse mechanical and chemical properties of the coatings. Char expansion was observed using furnace test, thermogravimetric analysis was used to determine residual weight, X-Ray Diffraction was performed to investigate compounds present in the char, shear test was conducted to determine char strength and scanning electron microscopy analysis was performed to observe morphology of the burnt char. From the microscopic investigation it was concluded that the dense structure of the char increased the char integrity by adding basalt and aluminium trihydrate as fillers. X-Ray Diffraction results shows the presence boron phosphate, and boric acid which enhanced the thermal performance of the coating up to 800°C. From the Thermogravimetric analysis it was concluded that the residual weight of the char was increased up to 34.9 % for IC-B2A4 which enhanced thermal performance of intumescent coating.

Low Contribution of PbO 2 -Coated Lead Service Lines to Water Lead Contamination at the Tap

DOE Office of Scientific and Technical Information (OSTI.GOV)

Triantafyllidou, Simoni; Schock, Michael R.; DeSantis, Michael K.

2015-02-24

To determine if residential water sampling corroborates the expectation that formation of stable PbO2 coatings on lead service lines (LSLs) provides an effective lead release control strategy, lead profile sampling was evaluated for eight home kitchen taps in three U.S. cities with observed PbO2-coated LSLs (Newport, Rhode Island; Cincinnati and Oakwood, Ohio). After various water standing times, these LSLs typically released similar or lower peak lead levels (1 to 18 μg/L) than the lead levels from the respective kitchen faucets (1 to 130 μg/L), and frequently 50–80% lower than the lead levels typically reported from Pb(II)-coated LSLs in comparable publishedmore » sampling studies. Prolonged stagnation (10–101 h) at the Cincinnati sites produced varying results. One site showed minimal (0–4 μg/L) increase in lead release from the PbO2-coated LSL, and persistence of free chlorine residual. However, the other site showed up to a 3-fold increase proportional to standing time, with essentially full depletion of the chlorine residual. Overall, lead release was consistently much lower than that reported in studies of Pb(II)-coated LSL scales, suggesting that natural formation of PbO2 in LSLs is an effective lead “corrosion” control strategy.« less

Descriptions of crack growth behaviors in glass-ZrO2 bilayers under thermal residual stresses.

PubMed

Belli, Renan; Wendler, Michael; Zorzin, José I; Petschelt, Anselm; Tanaka, Carina B; Meira, Josete; Lohbauer, Ulrich

2016-09-01

This study was intended to separate residual stresses arising from the mismatch in coefficients of thermal expansion between glass and zirconia (ZrO2) from those stresses arising solely from the cooling process. Slow crack growth experimentes were undertaken to demonstrate how cracks grow in different residual stress fields. Aluminosilicate glass discs were sintered onto ZrO2 to form glass-ZrO2 bilayers. Glass discs were allowed to bond to the ZrO2 substrate during sintering or prevented from bonding by means of coating the ZrO2 with a thin boron nitrade coating. Residual stress gradients on "bonded" and "unbonded" bilayers were assessed using birefringence measurements. Unbonded glass discs were further tested under biaxial flexure in dynamic fatigue conditions in order to evaluate the effect of residual stress on the slow crack growth behavior. When fast-ccoling was induced, residual tensile stresses on the glass increased significantly on the side toward the ZrO2 substrate. By allowing the bond between glass and ZrO2, those tensile stresses observed in unbonded specimens are overwhelmed by the contraction mismatch stresses between the ZrO2 substrate and the glassy overlayer. Specimens containing residual tensile stresses on the bending surface showed a time-dependent strength increase in relation to stress-free annealed samples in the dynamic biaxial bending test, with this effect being dependent on the magnitude of the residual tensile stress. The phenomenon observed is explained here on the basis of the water toughening effect, in which water diffuses into the glass promoting local swelling. An additional residual tensile stress at the crack tip adds an applied-stress-independent (Kres) term to the total tip stress intensity factor (Ktip), increasing the stress-enhanced diffusion and the shielding of the crack tip through swelling of the crack faces. Residual stresses in the glass influence the crack growth behavior of veneered-ZrO2 bilayered dental prostheses

Thermogravimetric investigation of the co-combustion between the pyrolysis oil distillation residue and lignite.

PubMed

Li, Hao; Xia, Shuqian; Ma, Peisheng

2016-10-01

Co-combustion of lignite with distillation residue derived from rice straw pyrolysis oil was investigated by non-isothermal thermogravimetric analysis (TGA). The addition of distillation residue improved the reactivity and combustion efficiency of lignite, such as increasing the weight loss rate at peak temperature and decreasing the burnout temperature and the total burnout. With increasing distillation residue content in the blended fuels, the synergistic interactions between distillation residue and lignite firstly increased and then decreased during co-combustion stage. Results of XRF, FTIR, (13)C NMR and SEM analysis indicated that chemical structure, mineral components and morphology of samples have great influence on the synergistic interactions. The combustion mechanisms and kinetic parameters were calculated by the Coats Redfern model, suggesting that the lowest apparent activation energy (120.19kJ/mol) for the blended fuels was obtained by blending 60wt.% distillation residue during main co-combustion stage. Copyright © 2016 Elsevier Ltd. All rights reserved.

In vitro evaluation of whole faba bean and its seed coat as a potential source of functional food components.

PubMed

Çalışkantürk Karataş, Selen; Günay, Demet; Sayar, Sedat

2017-09-01

In vitro studies were conducted to evaluate the particular nutritional benefits of whole faba bean seed (WFB) and fava bean seed coat (FBSC). Total dietary fiber contents of WFB and FBSC were 27.5% and 82.3%, respectively. FBSC were contained much higher total phenolic substances, condensed tannins, and total antioxidant activity than WFB. Bile acid (BA)-binding capacities of in vitro digested samples and nutritionally important products produced by in vitro fermentation of digestion residues were also studied. The BA-binding capacities of WFB and FBSC were 1.94 and 37.50μmol/100mg, respectively. Total BA bound by FBSC was even higher than the positive standard cholestyramine. Lignin and other constituents of the Klason residue were found to influence BA-binding properties. Moreover, the extent of the in vitro fermentation process showed that, fermentability of FBSC residue was significantly lower than that of WFB residue. Overall, faba bean, especially its seed coat, has great potential as a functional food. Copyright © 2017 Elsevier Ltd. All rights reserved.

Synthesis of cuprous oxide epoxy nanocomposite as an environmentally antimicrobial coating.

PubMed

M El Saeed, Ashraf; Abd El-Fattah, M; Azzam, Ahmed M; Dardir, M M; Bader, Magd M

2016-08-01

Cuprous oxide is commonly used as a pigment; paint manufacturers begin to employ cuprous oxide as booster biocides in their formulations, to replace the banned organotins as the principal antifouling compounds. Epoxy coating was reinforced with cuprous oxide nanoparticles (Cu2O NPs). The antibacterial as well as antifungal activity of Cu2O epoxy nanocomposite (Cu2O EN) coating films was investigated. Cu2O NPs were also experimented for antibiofilm and time-kill assay. The thermal stability and the mechanical properties of Cu2O EN coating films were also investigated. The antimicrobial activity results showed slowdown, the growth of organisms on the Cu2O EN coating surface. TGA results showed that incorporating Cu2O NPs into epoxy coating considerably enhanced the thermal stability and increased the char residue. The addition of Cu2O NPs at lower concentration into epoxy coating also led to an improvement in the mechanical resistance such as scratch and abrasion. Cu2O NPs purity was confirmed by XRD. The TEM photograph demonstrated that the synthesized Cu2O NPs were of cubic shape and the average diameter of the crystals was around 25nm. The resulting perfect dispersion of Cu2O NPs in epoxy coating revealed by SEM ensured white particles embedded in the epoxy matrix. Copyright © 2016 Elsevier B.V. All rights reserved.

Plasma-Sprayed Hydroxylapatite-Based Coatings: Chemical, Mechanical, Microstructural, and Biomedical Properties

NASA Astrophysics Data System (ADS)

Heimann, Robert B.

2016-06-01

This contribution discusses salient properties and functions of hydroxylapatite (HA)-based plasma-sprayed coatings, including the effect on biomedical efficacy of coating thickness, phase composition and distribution, amorphicity and crystallinity, porosity and surface roughness, cohesion and adhesion, micro- and nano-structured surface morphology, and residual coating stresses. In addition, it will provide details of the thermal alteration that HA particles undergo in the extremely hot plasma jet that leads to dehydroxylated phases such as oxyhydroxylapatite (OHA) and oxyapatite (OA) as well as thermal decomposition products such as tri-(TCP) and tetracalcium phosphates (TTCP), and quenched phases such as amorphous calcium phosphate (ACP). The contribution will further explain the role of ACP during the in vitro interaction of the as-deposited coatings with simulated body fluid resembling the composition of extracellular fluid (ECF) as well as the in vivo responses of coatings to the ECF and the host tissue, respectively. Finally, it will briefly describe performance profiles required to fulfill biological functions of osteoconductive bioceramic coatings designed to improve osseointegration of hip endoprostheses and dental root implants. In large parts, the content of this contribution is a targeted review of work done by the author and his students and coworkers over the last two decades. In addition, it is considered a stepping stone toward a standard operation procedure aimed at depositing plasma-sprayed bioceramic implant coatings with optimum properties.

Impact Resistance of EBC Coated SiC/SiC Composites

NASA Technical Reports Server (NTRS)

Fox, Dennis S.; Bhatt, Ramakrishna T.; Choi, Sung R.; Cosgriff, Laura M.; Fox, Dennis s.; Lee, Kang N.

2008-01-01

Impact performance of 2-D woven SiC/SiC composites coated with 225 and 525 m thick environmental barrier coating (EBC) was investigated. The composites were fabricated by melt infiltration and the EBC was deposited by plasma spray. Impact tests were conducted at room temperature and at 1316 C in air using 1.59-mm diameter steel-balls at projectile velocities ranging from 110 to 375 m/s. Both microscopy and nondestructive evaluation (NDE) methods were used to determine the extent of damage in the substrate and coating with increasing projectile velocity. The impacted specimens were tensile tested at room temperature to determine their residual mechanical properties. At projectile velocities less than 125 m/s, no detectable damage was noticed in the MI SiC/SiC composites coated with 525 m EBC. With increase in projectile velocity beyond this value, spallation of EBC layers, delamination of fiber plies, and fiber fracture were detected. At a fixed projectile velocity, the composites coated with 525 m EBC showed less damage than the composite coated with 225 m EBC. Both types of EBC coated composites retained a large fraction of the baseline properties of as-fabricated composites and exhibited non-brittle failure after impact testing at projectile velocities up to 375 m/s. Exposure of impact tested specimens in a moisture environment at 1316 C for 500 hr indicated that the through-the-thickness cracks in the EBC coating and delamination cracks in the substrate generated after impact testing acted as conduits for internal oxidation.

Microstructure evolution and mechanical properties of TiCN-Cr nano/micro composite coatings prepared by reactive plasma spraying

NASA Astrophysics Data System (ADS)

Zhang, Fanyong; He, Jining; Chen, Kai; Qin, Yanfang; Li, Chao; Yin, Fuxing

2018-01-01

Nanostructured TiCN based composite coatings with various Cr content were prepared by reactive plasma spray (RPS) from mixed powder (Ti-graphite + Cr) under nitrogen atmosphere. Results showed that composite coatings consisted mainly of TiC0.7N0.3 phase and residual metal Cr. Metal Cr plates were homogeneously embedded in TiCN matrix with good interface bond. The TiCN-Cr composite coatings exhibited lower porosity than TiCN coatings, but increasing porosity with excess Cr addition (30 wt.%). The TiCN-20 wt.% Cr coating showed the highest hardness (1309 HV0.2) among composite coatings, slight lower than the TiCN matrix coating (1526 HV0.2). Compared with the TiCN matrix coating, the TiCN-Cr composite coatings showed higher variability in surface microhardness distribution. The TiCN-Cr composite coatings showed slight higher friction coefficients (0.4-0.6) than TiCN matrix coating (0.35). The wear resistance of TiCN-Cr composite coatings was improved with less mass loss compared with TiCN coating under the test load of 400 N. The TiCN-Cr composite coatings with high Cr content showed the mixture of abrasive and adhesive wear.

Evaluation of experimental coating to improve the zirconia-veneering ceramic bond strength.

PubMed

Matani, Jay D; Kheur, Mohit; Jambhekar, Shantanu Subhashchandra; Bhargava, Parag; Londhe, Aditya

2014-12-01

To evaluate the shear bond strength (SBS) between zirconia and veneering ceramic following different surface treatments of zirconia. The efficacy of an experimental zirconia coating to improve the bond strength was also evaluated. Zirconia strips were fabricated and were divided into four groups as per their surface treatment: polished (control), airborne-particle abrasion, laser irradiation, and application of the experimental coating. The surface roughness and the residual monoclinic content were evaluated before and after the respective surface treatments. A scanning electron microscope (SEM) analysis of the experimental surfaces was performed. All specimens were subjected to shear force in a universal testing machine. The SBS values were analyzed with one-way ANOVA followed by Bonferroni post hoc for groupwise comparisons. The fractured specimens were examined to observe the failure mode. The SBS (29.17 MPa) and roughness values (0.80) of the experimental coating group were the highest among the groups. The residual monoclinic content was minimal (0.32) when compared to the remaining test groups. SEM analysis revealed a homogenous surface well adhered to an undamaged zirconia base. The other test groups showed destruction of the zirconia surface. The analysis of failure following bond strength testing showed entirely cohesive failures in the veneering ceramic in all study groups. The experimental zirconia surface coating is a simple technique to increase the microroughness of the zirconia surface, and thereby improve the SBS to the veneering ceramic. It results in the least monoclinic content and produces no structural damage to the zirconia substructure. © 2014 by the American College of Prosthodontists.

Fire resistance properties of ceramic wool fiber reinforced intumescent coatings

NASA Astrophysics Data System (ADS)

Amir, N.; Othman, W. M. S. W.; Ahmad, F.

2015-07-01

This research studied the effects of varied weight percentage and length of ceramic wool fiber (CWF) reinforcement to fire retardant performance of epoxy-based intumescent coating. Ten formulations were developed using ammonium polyphosphate (APP), expandable graphite (EG), melamine (MEL) and boric acid (BA). The mixing was conducted in two stages; powdered materials were grinded in Rocklabs mortar grinder and epoxy-mixed using Caframo mixer at low speed mixing. The samples were applied on mild steel substrate and exposed to 500°C heat inside Carbolite electric furnace. The char expansion and its physical properties were observed. Scanning electron microscopy (SEM) analyses were conducted to inspect the fiber dispersion, fiber condition and the cell structure of both coatings and chars produced. Thermogravimetric analyses (TGA) were conducted to study the thermal properties of the coating such as degradation temperature and residual weight. Fire retardant performance was determined by measuring backside temperature of substrate in 1-hour, 1000°C Bunsen burner test according to UL 1709 fire regime. The results showed that intumescent coating reinforced with CWF produced better fire resistance performance. When compared to unreinforced coating, formulation S6-15 significantly reduced steel temperature at approximately 34.7% to around 175°C. However, higher fiber weight percentage had slightly decreased fire retardant performance of the coating.

Impact Resistance of Environmental Barrier Coated SiC/SiC Composites

NASA Technical Reports Server (NTRS)

Bhatt, Ramakrishna T.; Choi, Sung R.; Cosgriff, Laura M.; Fox, Dennis S.; Lee, Kang N.

2008-01-01

Impact performance of 2D woven SiC/SiC composites coated with 225 and 525 microns thick environmental barrier coating (EBC) was investigated. The composites were fabricated by melt infiltration and the EBC was deposited by plasma spray. Impact tests were conducted at room temperature and at 1316 C in air using 1.59 mm diameter steel-balls at projectile velocities ranging from 110 to 375 m/s . Both microscopy and non-destructive evaluation (NDE) methods were used to determine the extent of damage in the substrate and coating with increasing projectile velocity. The impacted specimens were tensile tested at room temperature to determine their residual mechanical properties. At projectile velocities less than 125 m/s , no detectable internal damage was noticed in the MI SiC/SiC composites coated with 525 microns EBC. With increase in projectile velocity beyond this value, spallation of EBC layers, delamination of fiber plies, and fiber fracture were detected. At a fixed projectile velocity, the composites coated with 525 microns EBC showed less damage than those coated with 225 microns EBC. Both types of coated composites retained a large fraction of the baseline properties of the as-fabricated composites and exhibited non-brittle failure after impact testing. Furnace exposure of impacted specimens in a moisture environment at 1316 C for 500 h indicated that the through-the-thickness cracks in the coating and delamination cracks in the substrate generated after impact testing acted as conduits for internal oxidation.

Tribological performance of an H-DLC coating prepared by PECVD

NASA Astrophysics Data System (ADS)

Solis, J.; Zhao, H.; Wang, C.; Verduzco, J. A.; Bueno, A. S.; Neville, A.

2016-10-01

Carbon-based coatings are of wide interest due to their application in machine elements subjected to continuous contact where fluid lubricant films are not permitted. This paper describes the tribological performance under dry conditions of duplex layered H-DLC coating sequentially deposited by microwave excited plasma enhanced chemical vapour deposition on AISI 52100 steel. The architecture of the coating comprised Cr, WC, and DLC (a-C:H) with a total thickness of 2.8 μm and compressive residual stress very close to 1 GPa. Surface hardness was approximately 22 GPa and its reduced elastic modulus around 180 GPa. Scratch tests indicated a well adhered coating achieving a critical load of 80 N. The effect of normal load on the friction and wear behaviours were investigated with steel pins sliding against the actual coating under dry conditions at room temperature (20 ± 2 °C) and 35-50% RH. The results show that coefficient of friction of the coating decreased from 0.21 to 0.13 values with the increase in the applied loads (10-50 N). Specific wear rates of the surface coating also decrease with the increase in the same range of applied loads. Maximum and minimum values were 14 × 10-8 and 5.5 × 10-8 mm-3/N m, respectively. Through Raman spectroscopy and electron microscopy it was confirmed the carbon-carbon contact, due to the tribolayer formation on the wear scars of the coating and pin. In order to further corroborate the experimental observations regarding the graphitisation behaviour, the existing mathematical relationships to determine the graphitisation temperature of the coating/steel contact as well as the flash temperature were used.

Influence of Cu Content on the Microstructure and Mechanical Properties of Cr-Cu-N Coatings

PubMed Central

Ding, Ji Cheng; Zhang, Teng Fei; Wan, Zhi Xin; Mei, Hai Juan; Kang, Myung Chang

2018-01-01

The Cr-Cu-N coatings with various Cu contents (0–25.18 (±0.17) at.%) were deposited on Si wafer and stainless steel (SUS 304) substrates in reactive Ar+N2 gas mixture by a hybrid coating system combining pulsed DC and RF magnetron sputtering techniques. The influence of Cu content on the coating composition, microstructure, and mechanical properties was investigated. The microstructure of the coatings was significantly altered by the introduction of Cu. The deposited coatings exhibit solid solution structure with different compositions in all of the samples. Addition of Cu is intensively favored for preferred orientation growth along (200) direction by restricting in (111) direction. With increasing Cu content, the surface and cross-sectional morphology of coatings were changed from triangle cone-shaped, columnar feature to broccoli-like and compact glassy microstructure, respectively. The mechanical properties including the residual stress, nanohardness, and toughness of the coatings were explored on the basis of Cu content. The highest hardness was obtained at the Cu content of 1.49 (±0.10) at.%. PMID:29552269

Influence of Cu Content on the Microstructure and Mechanical Properties of Cr-Cu-N Coatings.

PubMed

Ding, Ji Cheng; Zhang, Teng Fei; Wan, Zhi Xin; Mei, Hai Juan; Kang, Myung Chang; Wang, Qi Min; Kim, Kwang Ho

2018-01-01

The Cr-Cu-N coatings with various Cu contents (0-25.18 (±0.17) at.%) were deposited on Si wafer and stainless steel (SUS 304) substrates in reactive Ar+N 2 gas mixture by a hybrid coating system combining pulsed DC and RF magnetron sputtering techniques. The influence of Cu content on the coating composition, microstructure, and mechanical properties was investigated. The microstructure of the coatings was significantly altered by the introduction of Cu. The deposited coatings exhibit solid solution structure with different compositions in all of the samples. Addition of Cu is intensively favored for preferred orientation growth along (200) direction by restricting in (111) direction. With increasing Cu content, the surface and cross-sectional morphology of coatings were changed from triangle cone-shaped, columnar feature to broccoli-like and compact glassy microstructure, respectively. The mechanical properties including the residual stress, nanohardness, and toughness of the coatings were explored on the basis of Cu content. The highest hardness was obtained at the Cu content of 1.49 (±0.10) at.%.

Analysis of thermal stresses in HfO2/SiO2 high reflective optical coatings for high power laser applications

NASA Astrophysics Data System (ADS)

Gao, Chunxue; Zhao, Zhiwei; Zhu, Zhuoya; Li, Shuang; Mi, Changwen

2015-02-01

HfO2/SiO2 high reflective optical coatings are widely used in high power laser applications because of their high laser damage resistance and appropriate spectral performance. The residual stresses strongly influence the performance and longevity of the optical coatings. Thermal stresses are the primary components of the residual stresses. In the present work, the distribution of thermal stresses in HfO2/SiO2 high reflective optical coatings was investigated using two different computational methods: finite element method (FEM) and an analytical method based on force and moment balances and classical beam bending theory. The results by these two methods were compared and found to be in agreement with each other, demonstrating that these two methods are effective and accurate ways to predict the thermal stresses in HfO2/SiO2 optical coatings. In addition, these two methods were also used to obtain the thermal stresses in HfO2/SiO2 optical coatings with different layer number to investigate the effect of the layer number on the thermal stresses of the HfO2/SiO2 optical coatings. The results show that with the increase of the layer number, the stresses in the substrate increase, while the stresses in the respective SiO2 and HfO2 layers decrease. Besides, it was also found that the radius of curvature of the coating system decreases as the layer number increases, leading to larger bending curvature in the system.

Complex fine-scale diffusion coating formed at low temperature on high-speed steel substrate

NASA Astrophysics Data System (ADS)

Chaus, A. S.; Pokorný, P.; Čaplovič, Ľ.; Sitkevich, M. V.; Peterka, J.

2018-04-01

A complex B-C-N diffusion coating was produced at 580 °C for 1 h on AISI M35 steel substrate and compared with a reference coating formed at 880 °C for 2.5 h. The surface and the cross-sections of the samples were subjected to detailed characterisation. The surface roughness, hardness, residual stresses and adhesion of the coatings were also evaluated together with cutting tests using drills on coated and uncoated samples while monitoring cutting force and torque. The surface of the steel treated at 580 °C revealed Fe2B, boron nitride and boron iron carbide, but FeB was noted to be absent. The 580 °C coating had the fine-scale microstructure, which resulted in the excellent adhesion and enhanced wear resistance, relative to reference samples that contained coarse borides. The results established that a complex fine-scale diffusion coating enhanced the wear resistance and reduces the cutting force and torque during drilling, thereby increasing the drill life by a factor of 2.2.

Fabrication and Anti-Oxidation Ability of SiC-SiO2 Coated Carbon Fibers Using Sol-Gel Method

PubMed Central

Yang, Guangyuan; Huang, Zhixiong; Wang, Xu; Wang, Bo

2018-01-01

The paper proposed a method to improve the anti-oxidation performance of carbon fibers (CF) at high temperature environment by coating silicon dioxide (SiO2) and silicon carbide (SiC). The modified sol-gel method had been used to ensure the proper interface between fibers and coating. We used polydimethylsiloxane and ethyl orthosilicate to make stable emulsion to uniformly disperse SiC nanoparticles. The modified SiO2/SiC coating had been coated on CF successfully. Compared with the untreated CF, the coated fibers started to be oxidized around 900 °C and the residual weight was 57% at 1400 °C. The oxidation mechanism had been discussed. The structure of SiC/SiO2 coated CF had been characterized by scanning electron microscope and X-ray diffraction analysis. Thermal gravimetric analysis was used to test the anti-oxidation ability of CF with different coatings. PMID:29495499

Excitation of surface plasmons in Al-coated SNOM tips

NASA Astrophysics Data System (ADS)

Palm, Viktor; Rähn, Mihkel; Jäme, Joonas; Hizhnyakov, Vladimir

2012-10-01

The mesoscopic effect of spectral modulation occurring due to the interference of two photonic fiber modes filtered out by a metal-coated SNOM tip is used to observe the surface plasmon polariton (SPP) excitation in SNOM tips. In a spectrum of the broadband light transmitted by a SNOM tip a region of highly regular spectral modulation can be found, indicating the spectral interval in which only two photonic modes (apparently HE11 and TM01) are transmitted with significant and comparable amplitudes. The modulation period yields the value of optical path difference (OPD) for this pair of modes. Due to the multimode fiber's inherent modal dispersion, this OPD value depends linearly on the fiber tail length l. An additional contribution to OPD can be generated in a metal-coated SNOM tip due to a mode-dependent photon-plasmon coupling strength resulting in generation of SPPs with different propagation velocities. For an Al-coated 200 nm SNOM tip spectra of transmitted light have been registered for ten different l values. An extrapolation of the linear OPD (l) dependence to l=0 yields a significant residual OPD value, indicating according to our theoretical considerations a mode-selective SPP excitation in the metal-coated tip. The modal dispersion is shown to switch its sign in the SNOM tip. First results of analogous experiments with an Al-coated 150 nm SNOM tip confirm our conclusions.

Application of lasers and pulsed power to coating removal

NASA Astrophysics Data System (ADS)

Young, Chris M.; Moeny, William M.; Curry, Randy D.; McDonald, Ken; Bosma, John T.

1995-03-01

Lasers and other pulsed power systems are uniquely suited for removal of coatings from a wide variety of substrates. Coatings which can be removed by these systems include paint, adhesives, epoxies, dips, rust, scale, and bird droppings. Suitable substrates include wood, metal, cloth, stone, ceramic, plastics, and even skin. These systems have the advantage over chemical stripping or mechanical abrasion in that the substrate is left virtually unharmed and in many cases the residue is reduced to a form that is more easily disposed of without toxic byproducts or expensive refurbishment. Furthermore, laser and other pulsed power based systems can be operated using only local containment without the need for special operator protective gear or complete enclosure of the substrate structure. Additional advantages are gained in these systems because they typically combine multiple removal mechanisms for greater effectiveness. For example, pulsed lasers create rapid heating of the coating. This rapid heating can result in chemical breakdown of the coating, thermomechanical stress induced dislocation, shock wave agitation, and physical ablation. This paper presents some of the latest research findings on coating removal using these systems. A comparative survey of the system technology, effectiveness, cost, and application is presented. Also presented is a survey of the commercial potential for the systems. Systems which are presented include lasers (CW, pulsed, Infrared, UV, etc.), flashlamps, electro-cathodic debonders, electron beams, and glow discharges.

Understanding the effects of process parameters on the properties of cold gas dynamic sprayed pure titanium coatings

NASA Astrophysics Data System (ADS)

Wong, Wilson

their corresponding coatings. For all feedstock powder morphologies, it was observed that the larger the particle size, the higher the temperature generated on impact. For the spherical powders, the higher the temperature generated on impact, the lower the stress needed to deform the particle. In addition, as the kinetic energy of the impacting particle increased, the flow peak stress decreased while the final strain increased. Furthermore, higher final flow strains were associated with higher coating DeltaHV 10 (between the coatings and the feedstock powders). Similar relationships are expected to exist for the sponge and irregular feedstock powders. Based on porosity, the spherical medium powder was found to have the best cold sprayability. The final part of the investigation focussed on the effect of substrate surface roughness and coating thickness on the adhesion strength of commercially pure titanium cold sprayed coatings onto Steel 1020, Al 6061, and Ti substrates. Adhesion strength was measured by tensile/pull tests according to ASTM C-633-01 standard. Through-thickness residual stresses of selected coatings were measured using the modified layer removal method (MLRM). In addition, mean coating residual stresses were calculated from MLRM results. It was found that adhesion strength increases with increasing substrate surface roughness and decreases with increasing coating thickness. Furthermore, mean coating residual stresses were correlated with adhesion strength and it was suggested that higher adhesion strengths are associated with higher mean compressive stresses and a higher probability for adiabatic shear instability to occur due to the higher particle impact velocities. In general, it was found that under similar cold spray conditions and substrate surface preparation method, adhesion strength was strongest for commercially pure titanium coatings deposited onto Al 6061, followed by Ti, then Steel 1020.

Corrosion and Fatigue Behavior of High-Strength Steel Treated with a Zn-Alloy Thermo-diffusion Coating

NASA Astrophysics Data System (ADS)

Mulligan, C. P.; Vigilante, G. N.; Cannon, J. J.

2017-11-01

High and low cycle fatigue tests were conducted on high-strength steel using four-point bending. The materials tested were ASTM A723 steel in the as-machined condition, grit-blasted condition, MIL-DTL-16232 heavy manganese phosphate-coated condition, and ASTM A1059 Zn-alloy thermo-diffusion coated (Zn-TDC). The ASTM A723 steel base material exhibits a yield strength of 1000 MPa. The effects of the surface treatments versus uncoated steel were examined. The fatigue life of the Zn-TDC specimens was generally reduced on as-coated specimens versus uncoated or phosphate-coated specimens. Several mechanisms are examined including the role of compressive residual stress relief with the Zn-TDC process as well as fatigue crack initiation from the hardened Zn-Fe alloy surface layer produced in the gas-metal reaction. Additionally, the effects of corrosion pitting on the fatigue life of coated specimens are explored as the Zn-TDC specimens exhibit significantly improved corrosion resistance over phosphate-coated and oiled specimens.

CrAlN coating to enhance the power loss and magnetostriction in grain oriented electrical steel

DOE Office of Scientific and Technical Information (OSTI.GOV)

Goel, Vishu; Anderson, Philip; Hall, Jeremy

Grain oriented electrical steels (GOES) are coated with aluminium orthophosphate on top of a forsterite (Mg{sub 2}SiO{sub 4}) layer to provide stress and insulation resistance to reduce the power loss and magnetostriction. In this work Chromium Aluminium Nitride (CrAlN) was coated on GOES samples with electron beam physical vapour deposition and was tested in the single strip and magnetostriction tester to measure the power loss and magnetostriction before and after coating. Power loss was reduced by 2% after coating and 6 % post annealing at 800 °C. For applied compressive stress of 6 MPa, the magnetostrictive strain was zero with themore » CrAlN coating as compared to 22 and 24 μϵ for fully finished GOES and GOES without phosphate coating. The thickness of the coating was found to be 1.9 ± 0.2 μm estimated with Glow Discharge Optical Emission Spectroscopy (GDOES). The magnetic domain imaging showed domain narrowing after coating. The reduction in power loss and magnetostriction was due to the large residual compressive stress and Young’s modulus (270 GPa) of the coating.« less

Coating liposomes with collagen (Mr 50,000) increases uptake into liver.

PubMed

Fonseca, M J; Alsina, M A; Reig, F

1996-03-13

Collagen-coated small unilamellar liposomes were prepared by incubation of two hydrophobic derivatives of collagen (average Mr 50 000) with preformed vesicles. The introduction of hexyl and lauryl residues to the collagen molecule improved by 10-fold the ability of collagen to coat liposomes. In vitro stability of the different coated vesicles prepared, was studied by their ability to retain entrapped carboxyfluorescein as a function of the time. Coated vesicles were clearly more stable in vitro than control liposomes, except for those containing the lauryl derivative in a protein/phospholipid weight ratio higher than 10(-3). Vesicle clearance from circulation as well as tissue distribution were also determined. Pharmacokinetics (determined by both fluorescence and radioactive techniques) were highly dependent on the injected dose, phospholipids used and the content of collagen. Half-lives were maximum for liposomes composed of saturated phospholipids injected at a dose of 2 micromol phospholipid. Besides, blood elimination of collagen-containing vesicles was about 2-fold faster and liver uptake 1.5 to 2-fold higher than control liposomes.

Paint Removal from Composites and Protective Coating Development

DTIC Science & Technology

1991-01-01

bonds between these layers relax, and the removal of the top layer is facilitated. This phenomena is known as fracking . Cold Jet has completed an initial...sublimed carbon dioxide "atmosphere" and the top layer of material, so that fracking occurs. Cold Jet adds that removal tends to occur layer by layer...often removed faster (than thinner coatings) as a result of the fracking mechanism. The paint residue from the stripping process is comprised of varying

Sliding Wear Response of Nanostructured YSZ Suspension Plasma-Sprayed Coating

NASA Astrophysics Data System (ADS)

Kossman, S.; Chicot, D.; Decoopman, X.; Iost, A.; van Gorp, A.; Meillot, E.; Puchi-Cabrera, E. S.; Santana, Y. Y.; Staia, M. H.

2014-12-01

Nanostructured yttria-stabilized zirconia coatings for applications in high-temperature environments can be deposited by suspension plasma spraying (SPS) techniques. The present research has been conducted in order to study the sliding wear response of a SPS ZrO2-8% mol. Y2O3 coating (75 μm in thickness) deposited onto a Haynes 230 substrate, using pin-on-disc tests. Some of the coated samples were subsequently heat-treated for 1 h at 300 and 600 °C. Samples characterization prior and after the wear tests was carried out by SEM, EDS, XRD and optical profilometry techniques. Instrumented indentation was employed to determine elastic modulus and hardness. The results have shown that the as-sprayed and heat-treated samples experienced severe wear (10-13 m3/Nm) and the worst wear performance corresponded to the sample heat treated at 600 °C. Such a behavior could be related to both the structural changes that took place during heat treatment and the nature and level of the residual stresses in the coatings. In general, the morphologies of the wear tracks observed by SEM have shown a smoothing of the surface, brittle fracture, smearing and grain pull-out.

Features of degradation and recovery of the optical properties of coatings based on ZnO powder modified with nanoparticles after irradiation

NASA Astrophysics Data System (ADS)

Mikhailov, M.; Neschimenko, V.; Sokolovskiy, A.

2018-04-01

The effect of electron irradiation with energy of 30 keV and fluence up to 7 × 1016 cm-2 on diffuse reflection spectra in situ of coatings based on ZnO powders unmodified and modified with zirconium dioxide and aluminum oxide nanopowders was investigated. The higher radiation stability of coatings based on modified pigments in comparison to unmodified pigments has been established. A significant recovery of the reflection spectra of irradiated coatings after exposure to residual vacuum and air was shown.

Ultra-high pressure waterjets efficient in removing coatings

DOE Office of Scientific and Technical Information (OSTI.GOV)

NONE

1996-06-01

Little if any thought was given to pipeline rehabilitation 50 years, a time when pipe manufacturers often coated the external diameter of pipe with coal tar to help eliminate corrosion. Unfortunately, contractors rehabilitating these pipelines today encounter major difficulties when attempting to remove coal tar with traditional removal processes. A leading pipeline rehabilitation firm, F.F. Yockey Company, Inc. of Magnolia, Texas, faced a constant challenge stripping coal tar with rotating knives and brushes. The process generated heat that melted the tar and caused the machines to jam. Another problem was the damage to the substrate caused by the friction-based cleaningmore » techniques of rotating knives and brushes. The knives also failed to completely clean the substrate, leaving behind a significant amount of residue. Contractors learned that new coating bonded poorly to the substrates covered with residual contaminants, thus yielding unsatisfactory results. As he looked for a solution, Dick Yockey, president and CEO of R.F. Yockey, began exploring the use of ultra-high pressure waterjet surface preparation equipment. This system involved water pressurized at levels ranging from 35,000 to 55,000 psi. The water travels through small orifices in a high-speed rotating nozzle, forming a cohesive stream of water. This paper reviews the design and performance of this system.« less

Thermal performance of glass fiber reinforced intumescent fire retardant coating for structural applications

NASA Astrophysics Data System (ADS)

Ahmad, Faiz; Ullah, Sami; Aziz, Hammad; Omar, Nor Sharifah

2015-07-01

The results of influence of glass fiber addition into the basic intumescent coating formulation towards the enhancement of its thermal insulation properties are presented. The intumescent coatings were formulated from expandable graphite, ammonium polyphosphate, melamine, boric acid, bisphenol A epoxy resin BE-188, polyamide amine H-2310 hardener and fiberglass (FG) of length 3.0 mm. Eight intumescent formulations were developed and the samples were tested for their fire performance by burning them at 450°C, 650°C and 850°C in the furnace for two hours. The effects of each fire test at different temperatures; low and high temperature were evaluated. Scanning Electron Microscope, X-Ray Diffraction technique and Thermo Gravimetric Analysis were conducted on the samples to study the morphology, the chemical components of char and the residual weight of the coatings. The formulation, FG08 containing 7.0 wt% glass fiber provided better results with enhanced thermal insulation properties of the coatings.

Parametric Studies Of Failure Mechanisms In Thermal Barrier Coatings During Thermal Cycling Using FEM

NASA Astrophysics Data System (ADS)

Srivathsa, B.; Das, D. K.

2015-12-01

Thermal barrier coatings (TBCs) are widely used on different hot components of gas turbine engines such as blades and vanes. Although, several mechanisms for the failure of the TBCs have been suggested, it is largely accepted that the durability of these coatings is primarily determined by the residual stresses that are developed during the thermal cycling. In the present study, the residual stress build-up in an electron beam physical vapour deposition (EB-PVD) based TBCs on a coupon during thermal cycling has been studied by varying three parameters such as the cooling rate, TBC thickness and substrate thickness. A two-dimensional thermomechanical generalized plane strain finite element simulations have been performed for thousand cycles. It was observed that these variations change the stress profile significantly and the stress severity factor increases non-linearly. Overall, the predictions of the model agree with reported experimental results and help in predicting the failure mechanisms.

Quality optimization of thermally sprayed coatings produced by the JP-5000 (HVOF) gun using mathematical modeling

NASA Technical Reports Server (NTRS)

Tawfik, Hazem

1994-01-01

Currently, thermal barrier coatings (TBC) of gas-turbine blades and similar applications have centered around the use of zirconia as a protective coating for high thermal applications. The advantages of zirconia include low thermal conductivity and good thermal shock resistance. Thermally sprayed tungsten carbide hardface coatings are used for a wide range of applications spanning both the aerospace and other industrial markets. Major aircraft engine manufacturers and repair facilities use hardface coatings for original engine manufacture (OEM), as well as in the overhaul of critical engine components. The principle function of these coatings is to resist severe wear environments for such wear mechanisms as abrasion, adhesion, fretting, and erosion. The (JP-5000) thermal spray gun is the most advanced in the High Velocity Oxygen Fuel (HVOF) systems. Recently, it has received considerable attention because of its relative low cost and its production of quality coatings that challenge the very successful but yet very expensive Vacuum Plasma Spraying (VPS) system. The quality of thermal spray coatings is enhanced as porosity, oxidation, residual stress, and surface roughness are reduced or minimized. Higher densification, interfacial bonding strength, hardness and wear resistance of coating are desirable features for quality improvement.

Mechanical Performance of Cold-Sprayed A357 Aluminum Alloy Coatings for Repair and Additive Manufacturing

NASA Astrophysics Data System (ADS)

Petráčková, K.; Kondás, J.; Guagliano, M.

2017-12-01

Cold-sprayed coatings made of A357 aluminum alloy, a casting alloy widely used in aerospace, underwent set of standard tests as well as newly developed fatigue test to gain an information about potential of cold spray for repair and additive manufacturing of loaded parts. With optimal spray parameters, coating deposition on substrate with smooth surface resulted in relatively good bonding, which can be further improved by application of grit blasting on substrate's surface. However, no enhancement of adhesion was obtained for shot-peened surface. Process temperature, which was set either to 450 or 550 °C, was shown to have an effect on adhesion and cohesion strength, but it does not influence residual stress in the coating. To assess cold spray perspectives for additive manufacturing, flat tensile specimens were machined from coating and tested in as-sprayed and heat-treated (solution treatment and aging) condition. Tensile properties of the coating after the treatment correspond to properties of the cast A357-T61 aluminum alloy. Finally, fatigue specimen was proposed to test overall performance of the coating and coating's fatigue limit is compared to the results obtained on cast A357-T61 aluminum alloy.

Fracture toughness and sliding properties of magnetron sputtered CrBC and CrBCN coatings

NASA Astrophysics Data System (ADS)

Wang, Qianzhi; Zhou, Fei; Ma, Qiang; Callisti, Mauro; Polcar, Tomas; Yan, Jiwang

2018-06-01

CrBC and CrBCN coatings with low and high B contents were deposited on 316L steel and Si wafers using an unbalanced magnetron sputtering system. Mechanical properties including hardness (H), elastic modulus (E) and fracture toughness (KIc) as well as residual stresses (σ) were quantified. A clear correlation between structural, mechanical and tribological properties of coatings was found. In particular, structural analyses indicated that N incorporation in CrBC coatings with high B content caused a significant structural evolution of the nanocomposite structure (crystalline grains embedded into an amorphous matrix) from nc-CrB2/(a-CrBx, a-BCx) to nc-CrN/(a-BCx, a-BN). As a result, the hardness of CrBC coating with high B content decreased from 23.4 to 16.3 GPa but the fracture toughness was enhanced. Consequently, less cracks initiated on CrBCN coatings during tribological tests, which combined with the shielding effect of a-BN on wear debris, led to a low friction coefficient and wear rate.

Controlled Thermal Expansion Coat for Thermal Barrier Coatings

NASA Technical Reports Server (NTRS)

Brindley, William J. (Inventor); Miller, Robert A. (Inventor); Aikin, Beverly J. M. (Inventor)

1999-01-01

A improved thermal barrier coating and method for producing and applying such is disclosed herein. The thermal barrier coating includes a high temperature substrate, a first bond coat layer applied to the substrate of MCrAlX, and a second bond coat layer of MCrAlX with particles of a particulate dispersed throughout the MCrAlX and the preferred particulate is Al2O3. The particles of the particulate dispersed throughout the second bond coat layer preferably have a diameter of less then the height of the peaks of the second bond coat layer, or a diameter of less than 5 microns. The method of producing the second bond coat layer may either include the steps of mechanical alloying of particles throughout the second bond coat layer, attrition milling the particles of the particulate throughout the second bond coat layer, or using electrophoresis to disperse the particles throughout the second bond coat layer. In the preferred embodiment of the invention, the first bond coat layer is applied to the substrate, and then the second bond coat layer is thermally sprayed onto the first bond coat layer. Further, in a preferred embodiment of die invention, a ceramic insulating layer covers the second bond coat layer.

Novel Epoxy Particulate Composites for Mitigation of Insect Residue Adhesion on Future Aircraft Surfaces

NASA Technical Reports Server (NTRS)

Wohl, Christopher J.; Smith, Joseph G., Jr.; Gardner, John M.; Penner, Ronald K.; Connell, John W.; Siochi, Emilie J.

2014-01-01

Drag is reduced significantly for airflow over surfaces when laminar flow can be maintained over greater chord lengths, the distance from the leading edge of an airfoil.1 However, surface imperfections, such as chipped paint, scratches, and events that change topography on a microscopic scale can introduce airflow instabilities resulting in premature transition to turbulent flow.1 Although many of these surface imperfections can be avoided with proper maintenance, advanced materials, and advanced manufacturing practices, topographical surface anomalies arising during flight from insect impacts cannot be controlled and can influence laminar flow stability. Practical solutions to this operational challenge need to be developed for future aircraft to have full advantage of laminar flow designs that improve fuel efficiency.2 Researchers have investigated various methods to mitigate insect residue adhesion for decades.3 Although several techniques have demonstrated efficacy including mechanical scrapers, active liquid discharge systems, and sacrificial paper coatings, they have not been commercially implemented due to increased manufacturing and operational complexity, environmental impact, and weight penalties. Coatings offer a simple route for passive insect residue adhesion prevention without many of the challenges associated with maintenance of laminar flow.4 In our previous work, we determined that most commercially available materials were not effective at insect residue adhesion.5 We also identified improvements when both surface energy could be controlled by surface modifying agents and the topography could be altered through the use of micron-sized and nanometer-sized filler materials.6 In this work, these general principles were applied to an epoxy system to evaluate the behavior of the surface modifying agent, a fluorinated alkyl ether oligomer, on surface energy and insect residue adhesion properties.

An abundantly expressed mucin-like protein from Toxocara canis infective larvae: the precursor of the larval surface coat glycoproteins.

PubMed Central

Gems, D; Maizels, R M

1996-01-01

Evasion of host immunity by Toxocara canis infective larvae is mediated by the nematode surface coat, which is shed in response to binding by host antibody molecules or effector cells. The major constituent of the coat is the TES-120 glycoprotein series. We have isolated a 730-bp cDNA from the gene encoding the apoprotein precursor of TES-120. The mRNA is absent from T. canis adults but hyperabundant in larvae, making up approximately 10% of total mRNA, and is trans-spliced with the nematode 5' leader sequence SL1. It encodes a 15.8-kDa protein (after signal peptide removal) containing a typical mucin domain: 86 amino acid residues, 72.1% of which are Ser or Thr, organized into an array of heptameric repeats, interspersed with proline residues. At the C-terminal end of the putative protein are two 36-amino acid repeats containing six Cys residues, in a motif that can also be identified in several genes in Caenorhabditis elegans. Although TES-120 displays size and charge heterogeneity, there is a single copy gene and a homogeneous size of mRNA. The association of overexpression of some membrane-associated mucins with immunosuppression and tumor metastasis suggests a possible model for the role of the surface coat in immune evasion by parasitic nematodes. Images Fig. 1 Fig. 4 PMID:8643687

LSP/MAO composite bio-coating on AZ80 magnesium alloy for biomedical application.

PubMed

Xiong, Ying; Hu, Qiang; Song, Renguo; Hu, Xiaxia

2017-06-01

A composite bio-coating was fabricated on AZ80 magnesium (Mg) alloy by using micro-arc oxidation (MAO) under the pretreatment of laser shock peening (LSP) in order to improve the bio-corrosion resistance and the mechanical integrity. LSP treatment could induce grain refinement and compressive residual stress field on the surface of material. MAO bio-coating was grown in alkaline electrolyte with hydroxyapatite (HA, Ca 10 (PO4) 6 (OH) 2 ) to improve the biological properties of the material. The microstructure, element and phase composition for untreated based material (BM) and treated samples (LSP layer, MAO bio-coating and LSP/MAO composite bio-coating) were investigated by transmission electron microscopy (TEM), scanning electron microscope (SEM), energy dispersion spectroscopy (EDS) and X-ray diffraction (XRD). Electrochemical tests and slow strain rate tensile (SSRT) tests were used to evaluate the corrosion resistance and the stress corrosion susceptibility in simulated body fluid (SBF). The results indicated that LSP/MAO composite bio-coating can not only improve the corrosion resistance of Mg alloy substrate evidently but also increase the mechanical properties in SBF compared to LSP layer and MAO bio-coating. Mg alloy treated by LSP/MAO composite technique should be better suited as biodegradable orthopedic implants. Copyright © 2017 Elsevier B.V. All rights reserved.

Liquisolid technique: a promising alternative to conventional coating for improvement of drug photostability in solid dosage forms.

PubMed

Khames, Ahmed

2013-10-01

The objective of this study was to investigate the photoprotective effect of liquisolid technique on amlodipine, a calcium channel blocker antihypertensive drug, representing a photosensitive drug model. Several liquisolid formulations were prepared using propylene glycol as a water-miscible nonvolatile vehicle at drug/solvent ratio (1:1), Avicel PH 102 as a carrier, nanometer-sized amorphous silicon and titanium dioxide either alone or in combination as coating materials. The carrier/coat ratio (R) was varied from 5 to 50. The prepared liquisolids, coated, noncoated tablets and drug substance were irradiated with a light dose of 0.5 W/m(2)/h visible light, 55.1 W/m(2)/h UVA, and 0.247 W/m(2)/h UVB for 8 h. The effect of coating material type and (R) value on the drug dissolution rate and photostability was studied. Results were statistically analyzed by post hoc two-way ANOVA at a probability level (α = 0.05). The results indicated that liquisolid technique not only improved the dissolution rate, but also significantly inhibited the photodegradative effect of different light energies in all prepared liquisolid formulations. The residual drug percentage reached 97.37% in comparison to 73.8% for the drug substance after 8 h of irradiation. The residual drug percentage was affected by the (R) value. Statistically; the detected difference was significant at the selected probability level (α = 0.05). It can thus be concluded that this liquisolid technique is a promising alternative to conventional coating procedures in formulations containing photosensitive drugs.

Mirrors for High Resolution X-Ray Optics---Figure Preserving IR/PT Coating

NASA Technical Reports Server (NTRS)

Chan, Kai-Wing; Olsen, Lawrence; Sharpe, Marton; Numata, Ai; McClelland, Ryan; Saha, Timo; Zhang, Will

2016-01-01

Coating stress of 10 - 20 nm of Ir is sufficiently high to distort the figure of arc-second thin lightweight mirrors. For iridium: --Stress sigma 4 GPa for 15 nm film implies 60 Nm integrated stress-- Need less than 3 N/m (or stress less than 200 MPa) for sub-arcsecond optics. Basic Approaches for Mitigation. A. Annealing the film-- Glass can be heat up to 400 C without distortion. Silicon is even more resistant.-- It was found that recovery is limited by residual thermal stress from taking the mirror down from high T. B. Coating bi-layer films with compressive stress with tensile stress. C. Front-and-back coating with magnetron sputtering or atomic layer deposition-- Sputtering involve spanning of substrates. Geometric difference in setup (convexness/concaveness of curved mirrors) does not permit precise front-and-back matching-- Atomic layer deposition can provide a uniform deposition front and back simultaneously.

Removal of metal(oid)s from contaminated water using iron-coated peat sorbent.

PubMed

Kasiuliene, Alfreda; Carabante, Ivan; Bhattacharya, Prosun; Caporale, Antonio Giandonato; Adamo, Paola; Kumpiene, Jurate

2018-05-01

This study aimed at combining iron and peat to produce a sorbent suitable for a simultaneous removal of cations and anions from a solution. Peat powder, an industrial residue, was coated with iron by immersing peat into iron salt solutions. The adsorption efficiency of the newly produced sorbent towards As, Cr, Cu and Zn was tested by means of batch adsorption experiments at a constant pH value of 5. Coating of Fe on peat significantly increased the adsorption of As (from <5% to 80%) and Cr (from <3% to 25%) in comparison to uncoated peat. Removal of cations on coated peat slightly decreased (by 10-15%), yet remained within acceptable range. Electron Microscopy combined with X-Ray Energy Dispersive Spectroscopy revealed that iron coating on the peat was rather homogenous and As and Cr were abundantly adsorbed on the surface. By contrast, Cu and Zn displayed a sparing distribution on the surface of the iron coated peat. These results indicate that iron-peat simultaneously target sufficient amounts of both cations and anions and can be used for a one-step treatment of contaminated groundwater. Copyright © 2018 The Authors. Published by Elsevier Ltd.. All rights reserved.

High Rate Deposition of Thick CrN and Cr2N Coatings Using Modulated Pulse Power (MPP) Magnetron Sputtering

DTIC Science & Technology

2010-12-01

in the conventional Bragg-Bentano mode. The residual stress of the coatings was measured by glancing incident angle XRD (GIXRD) in the same X - ray ...micro-analysis (EPMA), x - ray diffraction (XRD), field-emission scanning electron microscopy (FESEM), nanoindentation, scratch test, and ball-on...the coatings was determined by XRD using a SIEMENS X - ray diffractometer (Model KRISTALLOFLEX-810) operated with K-alpha Cu radiation (30 kV and 20 mA

Platelet storage lesion in interim platelet unit concentrates: A comparison with buffy-coat and apheresis concentrates.

PubMed

Singh, Sukhi; Shams Hakimi, Caroline; Jeppsson, Anders; Hesse, Camilla

2017-12-01

Platelet storage lesion is characterized by morphological changes and impaired platelet function. The collection method and storage medium may influence the magnitude of the storage lesion. The aim of this study was to compare the newly introduced interim platelet unit (IPU) platelet concentrates (PCs) (additive solution SSP+, 40% residual plasma content) with the more established buffy-coat PCs (SSP, 20% residual plasma content) and apheresis PCs (autologous plasma) in terms of platelet storage lesions. Thirty PCs (n=10 for each type) were assessed by measuring metabolic parameters (lactate, glucose, and pH), platelet activation markers, and in vitro platelet aggregability on days 1, 4, and 7 after donation. The expression of platelet activation markers CD62p (P-selectin), CD63 (LAMP-3), and phosphatidylserine was measured using flow cytometry and in vitro aggregability was measured with multiple electrode aggregometry. Higher platelet activation and lower in vitro aggregability was observed in IPU than in buffy-coat PCs on day 1 after donation. In contrast, metabolic parameters, expression of platelet activation markers, and in vitro aggregability were better maintained in IPU than in buffy-coat PCs at the end of the storage period. Compared to apheresis PCs, IPU PCs had higher expression of activation markers and lower in vitro aggregability throughout storage. In conclusion, the results indicate that there are significant differences in platelet storage lesions between IPU, buffy-coat, and apheresis PCs. The quality of IPU PCs appears to be at least comparable to buffy-coat preparations. Further studies are required to distinguish the effect of the preparation methods from storage conditions. Copyright © 2017 Elsevier Ltd. All rights reserved.

Determining the effect of cartridge case coatings on GSR using post-fire priming cup residue.

PubMed

Terry, Molly; Fookes, Barry; Bridge, Candice M

2017-07-01

Ammunition is typically composed of a lead-based priming mixture which contributes to the characteristics most commonly used for the identification of gunshot residue (GSR). Due to the health risks often associated with lead, the use of lead-free primers in ammunitions is becoming more popular. Thus, the presence of GSR is becoming more difficult to discern based on the traditional means, i.e. the presence of lead (Pb), barium (Ba), and antimony (Sb). While research has been conducted on the differences between lead-based and lead-free muzzle discharge residue, few have researched other components of ammunition which may lead to other means of characterizing GSR. This research, therefore, covers that gap by focusing on the priming cup present in ammunition and the residue which may originate from it, that can contribute to muzzle discharge residue. In this study, a lead-based and a lead-free ammunition from four different manufacturers were chosen. The cartridges were fired using a Glock 17, 9mm Parabellum, collected post-fire, and subsequently de-primed resulting in the removal of the anvil. The GSR present on the anvils and cups was analyzed using scanning electron microscopy coupled with energy dispersive x-ray spectrometry (SEM-EDX). The data was then processed using unit vector analysis for normalization and analyzed using principal component analysis (PCA) and linear discriminant analysis (LDA). This data was then used to determine the components of the cartridge case which contribute to GSR and develop a method of characterization between lead-free and lead-based ammunition. Such a method will improve the detection of GSR by strengthening the criteria of identification. Copyright © 2017 Elsevier B.V. All rights reserved.

Influence of hydrophobic and superhydrophobic surfaces on reducing aerodynamic insect residues

NASA Astrophysics Data System (ADS)

Krishnan, K. Ghokulla; Milionis, Athanasios; Loth, Eric; Farrell, Thomas E.; Crouch, Jeffrey D.; Berry, Douglas H.

2017-01-01

Insect fouling during takeoff, climb and landing can result in increased drag and fuel consumption for aircrafts with laminar-flow surfaces. This study investigates the effectiveness of various hydrophobic and superhydrophobic surfaces in reducing residue of insects on an aerodynamic surface at relatively high impact speeds (about 45 m/s). An experimental setup consisting of a wind tunnel and a method to inject live flightless fruit flies was used to test the effectiveness of various surfaces against insect fouling. Insect fouling was analyzed based on residue area and height from multiple impacts. In general most of the residue area was due to the hemolymph spreading while most of the residue height was due to adhesion of exoskeleton parts. Hydrophobic and especially superhydrophobic surfaces performed better than a hydrophilic aluminum surface in terms of minimizing the residue area of various insect components (exoskeleton, hemolymph, and red fluid). Surfaces with reduced wettability and short lateral length scales tended to have the smallest residue area. Residue height was not as strongly influenced by surface wettability since even a single exoskeleton adhered to the surface upon impact was enough to produce a residue height of the order of one mm. In general, the results indicate that hemolymph spread needs to be avoided (e.g. by having reduced wettability and short lateral correlation lengths) in order to minimize the residue area, while exoskeleton adherence needs to be avoided (e.g. by having oleophobic properties and micro/nano roughness) in order to minimize the residue height. In particular, two of the superhydrophobic coatings produced substantial reduction in residue height and area, relative to the baseline surface of aluminum. However, the surfaces also showed poor mechanical durability on the high-speed insect impact location. This suggests that although low wettability materials show great insect anti-fouling behavior, their durability needs to

Evidence for lysine acetylation in the coat protein of a polerovirus.

PubMed

Cilia, Michelle; Johnson, Richard; Sweeney, Michelle; DeBlasio, Stacy L; Bruce, James E; MacCoss, Michael J; Gray, Stewart M

2014-10-01

Virions of the RPV strain of Cereal yellow dwarf virus-RPV were purified from infected oat tissue and analysed by MS. Two conserved residues, K147 and K181, in the virus coat protein, were confidently identified to contain epsilon-N-acetyl groups. While no functional data are available for K147, K181 lies within an interfacial region critical for virion assembly and stability. The signature immonium ion at m/z 126.0919 demonstrated the presence of N-acetyllysine, and the sequence fragment ions enabled an unambiguous assignment of the epsilon-N-acetyl modification on K181. We hypothesize that selection favours acetylation of K181 in a fraction of coat protein monomers to stabilize the capsid by promoting intermonomer salt bridge formation.

Nanoparticle/Polymer Nanocomposite Bond Coat or Coating

NASA Technical Reports Server (NTRS)

Miller, Sandi G.

2011-01-01

This innovation addresses the problem of coatings (meant to reduce gas permeation) applied to polymer matrix composites spalling off in service due to incompatibility with the polymer matrix. A bond coat/coating has been created that uses chemically functionalized nanoparticles (either clay or graphene) to create a barrier film that bonds well to the matrix resin, and provides an outstanding barrier to gas permeation. There is interest in applying clay nanoparticles as a coating/bond coat to a polymer matrix composite. Often, nanoclays are chemically functionalized with an organic compound intended to facilitate dispersion of the clay in a matrix. That organic modifier generally degrades at the processing temperature of many high-temperature polymers, rendering the clay useless as a nano-additive to high-temperature polymers. However, this innovation includes the use of organic compounds compatible with hightemperature polymer matrix, and is suitable for nanoclay functionalization, the preparation of that clay into a coating/bondcoat for high-temperature polymers, the use of the clay as a coating for composites that do not have a hightemperature requirement, and a comparable approach to the preparation of graphene coatings/bond coats for polymer matrix composites.

Thermal barrier coatings application in diesel engines

NASA Technical Reports Server (NTRS)

Fairbanks, J. W.

1995-01-01

Commercial use of thermal barrier coatings in diesel engines began in the mid 70's by Dr. Ingard Kvernes at the Central Institute for Industrial Research in Oslo, Norway. Dr. Kvernes attributed attack on diesel engine valves and piston crowns encountered in marine diesel engines in Norwegian ships as hot-corrosion attributed to a reduced quality of residual fuel. His solution was to coat these components to reduce metal temperature below the threshold of aggressive hot-corrosion and also provide protection. Roy Kamo introduced thermal barrier coatings in his 'Adiabatic Diesel Engine' in the late 70's. Kamo's concept was to eliminate the engine block water cooling system and reduce heat losses. Roy reported significant performance improvements in his thermally insulated engine at the SAE Congress in 1982. Kamo's work stimulates major programs with insulated engines, particularly in Europe. Most of the major diesel engine manufacturers conducted some level of test with insulated combustion chamber components. They initially ran into increased fuel consumption. The German engine consortium had Prof. Woschni of the Technical Institute in Munich. Woschni conducted testing with pistons with air gaps to provide the insulation effects. Woschni indicated the hot walls of the insulated engine created a major increase in heat transfer he refers to as 'convection vive.' Woschni's work was a major factor in the abrupt curtailment of insulated diesel engine work in continental Europe. Ricardo in the UK suggested that combustion should be reoptimized for the hot-wall effects of the insulated combustion chamber and showed under a narrow range of conditions fuel economy could be improved. The Department of Energy has supported thermal barrier coating development for diesel engine applications. In the Clean Diesel - 50 Percent Efficient (CD-50) engine for the year 2000, thermal barrier coatings will be used on piston crowns and possibly other components. The primary purpose of the

A sensitive monoclonal antibody-based enzyme-linked immunosorbent assay for chlorpyrifos residue determination in Chinese agricultural smaples

USDA-ARS?s Scientific Manuscript database

A monoclonal antibody-based competitive antibody-coated enzyme-linked immunosorbent assay (ELISA) was developed and optimized for determining chlorpyrifos residue in agricultural products. The IC50 and IC10 of this ELISA were 3.3 ng/mL and 0.1 ng/mL respectively. The average recoveries recovery rate...

Photoresist-Free Patterning by Mechanical Abrasion of Water-Soluble Lift-Off Resists and Bare Substrates: Toward Green Fabrication of Transparent Electrodes

PubMed Central

Printz, Adam D.; Chan, Esther; Liong, Celine; Martinez, René S.; Lipomi, Darren J.

2013-01-01

This paper describes the fabrication of transparent electrodes based on grids of copper microwires using a non-photolithographic process. The process—“abrasion lithography”—takes two forms. In the first implementation (Method I), a water-soluble commodity polymer film is abraded with a sharp tool, coated with a conductive film, and developed by immersion in water. Water dissolves the polymer film and lifts off the conductive film in the unabraded areas. In the second implementation (Method II), the substrate is abraded directly by scratching with a sharp tool (i.e., no polymer film necessary). The abraded regions of the substrate are recessed and roughened. Following deposition of a conductive film, the lower profile and roughened topography in the abraded regions prevents mechanical exfoliation of the conductive film using adhesive tape, and thus the conductive film remains only where the substrate is scratched. As an application, conductive grids exhibit average sheet resistances of 17 Ω sq–1 and transparencies of 86% are fabricated and used as the anode in organic photovoltaic cells in concert with the conductive polymer, poly(3,4-ethylenedioxythiophene):poly(styrenesulfonate) (PEDOT:PSS). Compared to devices in which PEDOT:PSS alone serves as an anode, devices comprising grids of copper/nickel microwires and PEDOT:PSS exhibit lowered series resistance, which manifests in greater fill factor and power conversion efficiency. This simple method of forming micropatterns could find use in applications where cost and environmental impact should be minimized, especially as a potential replacement for the transparent electrode indium tin oxide (ITO) in thin-film electronics over large areas (i.e., solar cells) or as a method of rapid prototyping for laboratory-scale devices. PMID:24358321

Photoresist-free patterning by mechanical abrasion of water-soluble lift-off resists and bare substrates: toward green fabrication of transparent electrodes.

PubMed

Printz, Adam D; Chan, Esther; Liong, Celine; Martinez, René S; Lipomi, Darren J

2013-01-01

This paper describes the fabrication of transparent electrodes based on grids of copper microwires using a non-photolithographic process. The process--"abrasion lithography"--takes two forms. In the first implementation (Method I), a water-soluble commodity polymer film is abraded with a sharp tool, coated with a conductive film, and developed by immersion in water. Water dissolves the polymer film and lifts off the conductive film in the unabraded areas. In the second implementation (Method II), the substrate is abraded directly by scratching with a sharp tool (i.e., no polymer film necessary). The abraded regions of the substrate are recessed and roughened. Following deposition of a conductive film, the lower profile and roughened topography in the abraded regions prevents mechanical exfoliation of the conductive film using adhesive tape, and thus the conductive film remains only where the substrate is scratched. As an application, conductive grids exhibit average sheet resistances of 17 Ω sq(-1) and transparencies of 86% are fabricated and used as the anode in organic photovoltaic cells in concert with the conductive polymer, poly(3,4-ethylenedioxythiophene):poly(styrenesulfonate) (PEDOT:PSS). Compared to devices in which PEDOT:PSS alone serves as an anode, devices comprising grids of copper/nickel microwires and PEDOT:PSS exhibit lowered series resistance, which manifests in greater fill factor and power conversion efficiency. This simple method of forming micropatterns could find use in applications where cost and environmental impact should be minimized, especially as a potential replacement for the transparent electrode indium tin oxide (ITO) in thin-film electronics over large areas (i.e., solar cells) or as a method of rapid prototyping for laboratory-scale devices.

Thickness limitations in carbon nanotube reinforced silicon nitride coatings synthesized by vapor infiltration

DOE Office of Scientific and Technical Information (OSTI.GOV)

Eres, Gyula

Chemical vapor infiltration is a convenient method for synthesizing carbon nanotube (CNT)-reinforced ceramic coatings. The thickness over which infiltration is relatively uniform is limited by gas phase diffusion in the pore structure. These effects were investigated in two types of silicon nitride matrix composites. With CNTs that were distributed uniformly on the substrate surface dense coatings were limited to thicknesses of several microns. With dual structured CNT arrays produced by photolithography coatings up to 400 gm thick were obtained with minimal residual porosity. Gas transport into these dual structured materials was facilitated by creating micron sized channels between "CNT pillars"more » (i.e. each pillar consisted of a large number of individual CNTs). The experimental results are consistent with basic comparisons between the rates of gas diffusion and silicon nitride growth in porous structures. This analysis also provides a general insight into optimizing infiltration conditions during the fabrication of thick CNT-reinforced composite coatings. (C) 2012 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.« less

Spin-coating: A new approach for improving dispersion of cellulose nanocrystals and mechanical properties of poly (lactic acid) composites.

PubMed

Shojaeiarani, Jamileh; Bajwa, Dilpreet S; Stark, Nicole M

2018-06-15

This study systematically evaluated the influence of masterbatch preparation techniques, solvent casting and spin-coating methods, on composite properties. Composites were manufactured by combining CNCs masterbatches and PLA resin using twin screw extruder followed by injection molding. Different microscopy techniques were used to investigate the dispersion of CNCs in masterbatches and composites. Thermal, thermomechanical, and mechanical properties of composites were evaluated. Scanning electron microscopy (SEM) images showed superior dispersion of CNCs in spin-coated masterbatches compared to solvent cast masterbatches. At lower CNCs concentrations, both SEM and optical microscope images confirmed more uniform CNCs dispersion in spin-coated composites than solvent cast samples. Degree of crystallinity of PLA exhibited a major enhancement by 147% and 380% in solvent cast and spin-coated composites, respectively. Spin-coated composites with lower CNCs concentration exhibited a noticeable improvement in mechanical properties. However, lower thermal characteristics in spin-coated composites were observed, which could be attributed to the residual solvents in masterbatches. Copyright © 2018 Elsevier Ltd. All rights reserved.

Development of an Innovative Laser-Assisted Coating Process for Extending Lifetime of Metal Casting Dies. Final Report

DOE Office of Scientific and Technical Information (OSTI.GOV)

Madhav Rao Gonvindaraju

1999-10-18

Die casting dies used in the metal casting industry fail due to thermal fatigue cracking accompanied by the presence of residual tensile stresses, corrosion, erosion and wear of die surfaces. This phase 1 SBIR Final Report summarize Karta Technologies research involving the development of an innovative laser coating technology for metal casting dies. The process involves depositing complex protective coatings of nanocrystalline powders of TiC followed by a laser shot peening. The results indicate a significant improvement in corrosion and erosion resistance in molten aluminum for H13 die casting die steels. The laser-coated samples also showed improved surface finish, amore » homogeneous and uniform coating mircrostructure. The technology developed in this research can have a significant impact on the casting industry by saving the material costs involved in replacing dies, reducing downtime and improving the quality.« less

Cyclic peptides and their interaction with peptide coated surfaces

NASA Astrophysics Data System (ADS)

Palmer, F.; Tünnemann, R.; Leipert, D.; Stingel, C.; Jung, G.; Hoffmann, V.

2001-05-01

Focusing on biochemical and pharmaceutical inhibitor systems the interaction of cyclic peptides with model peptides have been investigated by ATR-FTIR-spectroscopy. Information about the participation of special functional groups e.g. COOH, COO -, NH 3+ or peptide backbone was gathered by observing cyclohexapeptides (c(X 1LX 2LX 3)) which are interacting with covalently coated Si-ATR-crystals ( L-arginine, tripeptide I (aNS), tripeptide II (SNa)). To determine the interaction, further studies about the band sequence (1800-1500 cm -1) for non-adsorbed cyclohexapeptides and for the interaction with the silicon surface (SiOH) were necessary. The spectra of the interacting cyclohexapeptides with the SiOH-groups were treated like reference spectra for the evaluation of the peptide-peptide interaction. Based on these spectra, we can conclude that there is peptide-peptide interaction with the coating and not with the residual OH-groups. Determination of interaction mechanisms was done by spectra which represent adsorbed molecules only. The amount of adsorbed molecules was considerably less than a monolayer. Therefore the intensities of the spectra are about 10 -4 absorbance units. The spectra contain information about both changes of the coating and of the cyclohexapeptide.

Screening of Potential Inhibitor against Coat Protein of Apple Chlorotic Leaf Spot Virus.

PubMed

Purohit, Rituraj; Kumar, Sachin; Hallan, Vipin

2018-06-01

In this study, we analyzed Coat protein (CP) of Apple chlorotic leaf spot virus (ACLSV), an important latent virus on Apple. Incidence of the virus is upto 60% in various apple cultivars, affecting yield losses of the order of 10-40% (depending upon the cultivar). CP plays an important role as the sole building block of the viral capsid. Homology approach was used to model 193 amino acid sequence of the coat protein. We used various servers such as ConSurf, TargetS, OSML, COACH, COFACTOR for the prediction of active site residues in coat protein. Virtual screening strategy was employed to search potential inhibitors for CP. Top twenty screened molecules considered for drugability, and toxicity analysis and one potential molecule was further analyzed by docking analysis. Here, we reported a potent molecule which could inhibit the formation of viron assembly by targeting the CP protein of virus.

Electrocurtain coating process for coating solar mirrors

DOEpatents

Kabagambe, Benjamin; Boyd, Donald W.; Buchanan, Michael J.; Kelly, Patrick; Kutilek, Luke A.; McCamy, James W.; McPheron, Douglas A.; Orosz, Gary R.; Limbacher, Raymond D.

2013-10-15

An electrically conductive protective coating or film is provided over the surface of a reflective coating of a solar mirror by flowing or directing a cation containing liquid and an anion containing liquid onto the conductive surface. The cation and the anion containing liquids are spaced from, and preferably out of contact with one another on the surface of the reflective coating as an electric current is moved through the anion containing liquid, the conductive surface between the liquids and the cation containing liquid to coat the conductive surface with the electrically conductive coating.

Backbone dynamics of a model membrane protein: assignment of the carbonyl carbon /sup 13/C NMR resonances in detergent-solubilized M13 coat protein

DOE Office of Scientific and Technical Information (OSTI.GOV)

Henry, G.D.; Weiner, J.H.; Sykes, B.D.

The major coat protein of the filamentous bacteriophage M13 is a 50-residue amphiphilic polypeptide which is inserted, as an integral membrane-spanning protein, in the inner membrane of the Escherichia coli host during infection. /sup 13/C was incorporated biosynthetically into a total of 23 of the peptide carbonyls using labeled amino acids (alanine, glycine, lysine, phenylalanine, and proline). The structure and dynamics of carbonyl-labeled M13 coat protein were monitored by /sup 13/C nuclear magnetic resonance (NMR) spectroscopy. Assignment of many resonances was achieved by using protease digestion, pH titration, or labeling of the peptide bond with both /sup 13/C and /supmore » 15/N. The carbonyl region of the natural-abundance /sup 13/C NMR spectrum of M13 coat protein in sodium dodecyl sulfate solution shows approximately eight backbone carbonyl resonances with line widths much narrower than the rest. Three of these more mobile residues correspond to assigned peaks (glycine-3, lysine-48, and alanine-49) in the individual amino acid spectra, and another almost certainly arises from glutamic acid-2. A ninth residue, alanine-1, also gives rise to a very narrow carbonyl resonance if the pH is well above or below the pK/sub a/ of the terminal amino group. These data suggest that only about four residues at either end of the protein experience large-amplitude spatial fluctuations; the rest of the molecule is essentially rigid on the time scale of the overall rotational tumbling of the protein-detergent complex. The relative exposure of different regions of detergent-bound protein was monitored by limited digestion with proteinase K. Comparable spectra and digestion patterns were obtained when the protein was solubilized in sodium deoxycholate, suggesting that the coat protein binds both amphiphiles in a similar fashion.« less

Effect of Surface Preparation on Residual Stresses in Multilayer Coatings and the Consequences for Disbondment Following Construction Damage and Exposure to In-Service Stress

DOT National Transportation Integrated Search

2009-01-01

Underground pipelines are protected by a combination of cathodic protection and a protective coating. Multi-layer coatings offer protection against corrosion and from mechanical damage during construction or during service. Multi-layer coatings are w...

Assessment of Quantum Dot Penetration into Skin in Different Species Under Different Mechanical Actions

NASA Astrophysics Data System (ADS)

Monteiro-Riviere, N. A.; Zhang, L. W.

Skin penetration is one of the major routes of exposure for nanoparticles to gain access to a biological system. QD nanoparticles have received a great deal of attention due to their fluorescent characteristics and potential use in medical applications. However, little is known about their permeability in skin. This study focuses on three types of quantum dots (QD) with different surface coatings and concentrations on their ability to penetrate skin. QD621 (polyethylene glycol coated, PEG) was studied for 24 h in porcine skin flow-through diffusion cells. QD565 and QD655 coated with carboxylic acid were studied for 8 and 24 h in flow-through diffusion cells with flexed, tape stripped and abraded rat skin to determine if these mechanical actions could perturb the barrier and affect penetration. Confocal microscopy depicted QD621 penetration through the uppermost layers of the stratum corneum (SC) and fluorescence was found in the SC and near hair follicles. QD621 were found in the intercellular lipid layers of the SC by transmission electron microscopy (TEM). QD565 and 655 with flexed and tape-stripped skin did not show penetration; only abraded skin showed penetration in the viable dermal layers. In all QD studies, inductively coupled plasma-optical emission spectroscopy (ICP-OES) analysis for cadmium (Cd) and fluorescence for QD did not detect Cd or fluorescence signal in the perfusate at any time point, concentration or type of QD. These results indicate that porcine skin penetration of QD621 is minimal and limited primarily to the outer SC layers, while QD565 and 655 penetrated into the dermis of abraded skin. The anatomical complexity of skin and species differences should be taken into consideration when selecting an animal model to study nanoparticle absorption/penetration. These findings are of importance to risk assessment for nanoscale materials because it indicates that if skin barrier is altered such as in wounds, scrapes, or dermatitis conditions could

Electroplating chromium on CVD SiC and SiCf-SiC advanced cladding via PyC compatibility coating

NASA Astrophysics Data System (ADS)

Ang, Caen; Kemery, Craig; Katoh, Yutai

2018-05-01

Electroplating Cr on SiC using a pyrolytic carbon (PyC) bond coat is demonstrated as an innovative concept for coating of advanced fuel cladding. The quantification of coating stress, SEM morphology, XRD phase analysis, and debonding test of the coating on CVD SiC and SiCf-SiC is shown. The residual tensile stress (by ASTM B975) of electroplated Cr is > 1 GPa prior to stress relaxation by microcracking. The stress can remove the PyC/Cr layer from SiC. Surface etching of ∼20 μm and roughening to Ra > 2 μm (by SEM observation) was necessary for successful adhesion. The debonding strength (by ASTM D4541) of the coating on SiC slightly improved from 3.6 ± 1.4 MPa to 5.9 ± 0.8 MPa after surface etching or machining. However, this improvement is limited due to the absence of an interphase, and integrated CVI processing may be required for further advancement.

Dry coating, a novel coating technology for solid pharmaceutical dosage forms.

PubMed

Luo, Yanfeng; Zhu, Jesse; Ma, Yingliang; Zhang, Hui

2008-06-24

Dry coating is a coating technology for solid pharmaceutical dosage forms derived from powder coating of metals. In this technology, powdered coating materials are directly coated onto solid dosage forms without using any solvent, and then heated and cured to form a coat. As a result, this technology can overcome such disadvantages caused by solvents in conventional liquid coating as serious air pollution, high time- and energy-consumption and expensive operation cost encountered by liquid coating. Several dry coating technologies, including plasticizer-dry-coating, electrostatic-dry-coating, heat-dry-coating and plasticizer-electrostatic-heat-dry-coating have been developed and extensively reported. This mini-review summarized the fundamental principles and coating processes of various dry coating technologies, and thoroughly analyzed their advantages and disadvantages as well as commercialization potentials.

Tribological investigation of diamond-like carbon coated micro-dimpled surface under bovine serum and osteoarthritis oriented synovial fluid

NASA Astrophysics Data System (ADS)

Ghosh, Subir; Choudhury, Dipankar; Roy, Taposh; Mamat, Azuddin Bin; Masjuki, H. H.; Pingguan-Murphy, Belinda

2015-06-01

Osteoarthritis-oriented synovial fluid (OASF), i.e., that typical of a patient with osteoarthritis, has different physical and biological characteristics than bovine serum (BS), a lubricant widely used in biotribological investigations. Micro-dimpled and diamond-like carbon- (DLC) coated surfaces are key emerging interfaces for orthopedic implants. In this study, tribological performances of dimpled surfaces, with and without DLC coating, have been investigated under both BS and OASF. The friction tests were performed utilizing a pin on a disk tribometer, whereas contact pressure, speed, and temperature were simulated to a ‘medium walking gait’ of hip joint conditions. The mechanical properties of the specimen and the physical properties of the lubricant were characterized before the friction test. Raman analysis was conducted to identify the coating condition both before and after the test. The DLC-coated dimpled surface showed maximum hardness and residual stress. A DLC-coated dimpled surface under an OASF lubricated condition yielded a lower friction coefficient and wear compared to those of plain and dimpled specimens. The higher graphitization of coated materials with increasing load was confirmed by Raman spectroscopy.

Active coatings technologies for tailorable military coating systems

NASA Astrophysics Data System (ADS)

Zunino, J. L., III

2007-04-01

The main objective of the U.S. Army's Active Coatings Technologies Program is to develop technologies that can be used in combination to tailor coatings for utilization on Army Materiel. The Active Coatings Technologies Program, ACT, is divided into several thrusts, including the Smart Coatings Materiel Program, Munitions Coatings Technologies, Active Sensor packages, Systems Health Monitoring, Novel Technology Development, as well as other advanced technologies. The goal of the ACT Program is to conduct research leading to the development of multiple coatings systems for use on various military platforms, incorporating unique properties such as self repair, selective removal, corrosion resistance, sensing, ability to modify coatings' physical properties, colorizing, and alerting logistics staff when tanks or weaponry require more extensive repair. A partnership between the U.S. Army Corrosion Office at Picatinny Arsenal, NJ along with researchers at the New Jersey Institute of Technology, NJ, Clemson University, SC, University of New Hampshire, NH, and University of Massachusetts (Lowell), MA, are developing the next generation of Smart Coatings Materiel via novel technologies such as nanotechnology, Micro-electromechanical Systems (MEMS), meta-materials, flexible electronics, electrochromics, electroluminescence, etc. This paper will provide the reader with an overview of the Active Coatings Technologies Program, including an update of the on-going Smart Coatings Materiel Program, its progress thus far, description of the prototype Smart Coatings Systems and research tasks as well as future nanotechnology concepts, and applications for the Department of Defense.

Systematic Investigation on the Influence of Spray Parameters on the Mechanical Properties of Atmospheric Plasma-Sprayed YSZ Coatings

NASA Astrophysics Data System (ADS)

Mutter, Markus; Mauer, Georg; Mücke, Robert; Guillon, Olivier; Vaßen, Robert

2018-04-01

In the atmospheric plasma spray (APS) process, micro-sized ceramic powder is injected into a thermal plasma where it is rapidly heated and propelled toward the substrate. The coating formation is characterized by the subsequent impingement of a large number of more or less molten particles forming the so-called splats and eventually the coating. In this study, a systematic investigation on the influence of selected spray parameters on the coating microstructure and the coating properties was conducted. The investigation thereby comprised the coating porosity, the elastic modulus, and the residual stress evolution within the coating. The melting status of the particles at the impingement on the substrate in combination with the substrate surface condition is crucial for the coating formation. Single splats were collected on mirror-polished substrates for selected spray conditions and evaluated by identifying different types of splats (ideal, distorted, weakly bonded, and partially molten) and their relative fractions. In a previous study, these splat types were evaluated in terms of their effect on the above-mentioned coating properties. The particle melting status, which serves as a measure for the particle spreading behavior, was determined by in-flight particle temperature measurements and correlated to the coating properties. It was found that the gun power and the spray distance have a strong effect on the investigated coating properties, whereas the feed rate and the cooling show minor influence.

Flow coating apparatus and method of coating

DOEpatents

Hanumanthu, Ramasubrahmaniam; Neyman, Patrick; MacDonald, Niles; Brophy, Brenor; Kopczynski, Kevin; Nair, Wood

2014-03-11

Disclosed is a flow coating apparatus, comprising a slot that can dispense a coating material in an approximately uniform manner along a distribution blade that increases uniformity by means of surface tension and transfers the uniform flow of coating material onto an inclined substrate such as for example glass, solar panels, windows or part of an electronic display. Also disclosed is a method of flow coating a substrate using the apparatus such that the substrate is positioned correctly relative to the distribution blade, a pre-wetting step is completed where both the blade and substrate are completed wetted with a pre-wet solution prior to dispensing of the coating material onto the distribution blade from the slot and hence onto the substrate. Thereafter the substrate is removed from the distribution blade and allowed to dry, thereby forming a coating.

SiAlON COATINGS OF SILICON NITRIDE AND SILICON CARBIDE

DOE Office of Scientific and Technical Information (OSTI.GOV)

Jan W. Nowok; John P. Hurley; John P. Kay

2000-06-01

The need for new engineering materials in aerospace applications and in stationary power turbine blades for high-efficiency energy-generating equipment has led to a rapid development of ceramic coatings. They can be tailored to have superior physical (high specific strength and stiffness, enhanced high-temperature performance) and chemical (high-temperature corrosion resistance in more aggressive fuel environments) properties than those of monolithic ceramic materials. Among the major chemical properties of SiAlON-Y ceramics are their good corrosion resistance against aggressive media combined with good thermal shock behavior. The good corrosion resistance results from the yttria-alumina-garnet (YAG), Al{sub 5}Y{sub 3}O{sub 12}, formed during the corrosionmore » process of SiAlON-Y ceramics in combustion gases at 1300 C. The interfacial chemical precipitation of the YAG phase is beneficial. This phase may crystallize in cubic and/or tetragonal modifications and if formed in SiAlON-Y ceramic may simultaneously generate residual stress. Also, this phase can contain a large number of point defects, which is a consequence of the large unit cell and complexity of the YAG structure because it has no close-packed oxygen planes. Therefore, the need exists to elucidate the corrosion mechanism of a multilayered barrier with respect to using SiAlON-YAG as a corrosion-protective coating. Stress corrosion cracking in the grain boundary of a silicon nitride (Si{sub 3}N{sub 4}) ceramic enriched in a glassy phase such as SiAlON can significantly affect its mechanical properties. It has been suggested that the increased resistance of the oxynitride glass to stress corrosion is related to the increased surface potential of the fracture surface created in the more durable and highly cross-linked oxynitride glass network structure. We expect that either increased or decreased surface potential of the intergranular glassy phase is brought about by changes in the residual stress of

Influence of heat treatment on bond strength and corrosion resistance of sol-gel derived bioglass-ceramic coatings on magnesium alloy.

PubMed

Shen, Sibo; Cai, Shu; Xu, Guohua; Zhao, Huan; Niu, Shuxin; Zhang, Ruiyue

2015-05-01

In this study, bioglass-ceramic coatings were prepared on magnesium alloy substrates through sol-gel dip-coating route followed by heat treatment at the temperature range of 350-500°C. Structure evolution, bond strength and corrosion resistance of samples were studied. It was shown that increasing heat treatment temperature resulted in denser coating structure as well as increased interfacial residual stress. A failure mode transition from cohesive to adhesive combined with a maximum on the measured bond strength together suggested that heat treatment enhanced the cohesion strength of coating on the one hand, while deteriorated the adhesion strength of coating/substrate on the other, thus leading to the highest bond strength of 27.0MPa for the sample heat-treated at 450°C. This sample also exhibited the best corrosion resistance. Electrochemical tests revealed that relative dense coating matrix and good interfacial adhesion can effectively retard the penetration of simulated body fluid through the coating, thus providing excellent protection for the underlying magnesium alloy. Copyright © 2015 Elsevier Ltd. All rights reserved.

Environmental Barrier Coatings Having a YSZ Top Coat

NASA Technical Reports Server (NTRS)

Lee, Kang N.; Gray, Hugh (Technical Monitor)

2002-01-01

Environmental barrier coatings (EBCs) with a Si bond coat, a yttria-stabilized zirconia (YSZ) top coat, and various intermediate coats were investigated. EBCs were processed by atmospheric pressure plasma spraying. The EBC durability was determined by thermal cycling tests in water vapor at 1300 C and 1400 C, and in air at 1400 C and 1500 C. EBCs with a mullite (3Al2O3 (dot) 2SiO2) + BSAS (1 - xBaO (dot) xSrO (dot) Al2O3 (dot) 2SiO2) intermediate coat were more durable than EBCs with a mullite intermediate coat, while EBCs with a mullite/BSAS duplex intermediate coat resulted in inferior durability. The improvement with a mullite + BSAS intermediate coat was attributed to enhanced compliance of the intermediate coat due to the addition of a low modulus BSAS second phase. Mullite + BSAS/YSZ and BSAS/YSZ interfaces produced a low melting (less than 1400 C) reaction product, which is expected to degrade the EBC performance by increasing the thermal conductivity. EBCs with a mullite + BSAS / graded mullite + YSZ intermediate coat showed the best durability among the EBCs investigated in this study. This improvement was attributed to diffused CTE (Coefficient of Thermal Expansion) mismatch stress and improved chemical stability due to the compositionally graded mullite+YSZ layer.

Asymmetric interactions in the adenosine-binding pockets of the MS2 coat protein dimer

PubMed Central

Powell, Amy J; Peabody, David S

2001-01-01

Background The X-ray structure of the MS2 coat protein-operator RNA complex reveals the existence of quasi-synmetric interactions of adenosines -4 and -10 in pockets formed on different subunits of the coat protein dimer. Both pockets utilize the same five amino acid residues, namely Val29, Thr45, Ser47, Thr59, and Lys61. We call these sites the adenosine-binding pockets. Results We present here a heterodimer complementation analysis of the contributions of individual A-pocket amino acids to the binding of A-4 and A-10 in different halves of the dimer. Various substitutions of A-pocket residues were introduced into one half of single-chain coat protein heterodimers where they were tested for their abilities to complement Y85H or T91I substitutions (defects in the A-4 and A-10 half-sites, respectively) present in the other dimer half. Conclusions These experiments provide functional tests of interactions predicted from structural analyses, demonstrating the importance of certain amino acid-nucleotide contacts observed in the crystal structure, and showing that others make little or no contribution to the stability of the complex. In summary, Val29 and Lys61 form important stabilizing interactions with both A-4 and A-10. Meanwhile, Ser47 and Thr59 interact primarily with A-10. The important interactions with Thr45 are restricted to A-4. PMID:11504563

Influence of the aqueous film coating process on the properties and stability of tablets containing a moisture-labile drug.

PubMed

Ruotsalainen, Mirja; Heinämäki, Jyrki; Taipale, Krista; Yliruusi, Jouko

2003-01-01

The effects of an aqueous film coating process on the morphology and storage stability of hydroxypropyl methylcellulose-coated tablets containing a moisture-labile model drug (acetylsalicylic acid, ASA) were evaluated using an instrumented side-vented tablet pan coater. Coating parameters studied were inlet air absolute humidity 5 g/m3 and 12 g/m3, spraying air pressure 100 kPa and 500 kPa, pan air temperature 35 degrees C and 55 degrees C, and coating solution flow rate 2.2 g/min and 7.8 g/min. The surface roughness of the coatings was measured with a laser profilometer and the chemical hydrolysis of the model drug ASA with an UV-spectrophotometer. The film-coated tablets were stored at 25 degrees C/60% RH and 40 degrees C/75% RH for three months. The high absolute humidity of the inlet air increased the residual water content and surface roughness of the coated tablets. Using a lower coating solution flow rate, higher spraying air pressure and pan temperature the coatings were smooth and homogeneous. In both ambient and accelerated storage conditions, the roughness of the coatings and the hydrolysis of ASA increased, but this was independent of the film coating process. Uniform and smooth hydroxypropyl methylcellulose coatings can be achieved by improved control of process parameters related to the application of the coating solution and water evaporation of the tablet surface.

Lotus Dust Mitigation Coating and Molecular Adsorber Coating

NASA Technical Reports Server (NTRS)

O'Connor, Kenneth M.; Abraham, Nithin S.

2015-01-01

NASA Goddard Space Flight Center has developed two unique coating formulations that will keep surfaces clean and sanitary and contain contaminants.The Lotus Dust Mitigation Coating, modeled after the self-cleaning, water-repellant lotus leaf, disallows buildup of dust, dirt, water, and more on surfaces. This coating, has been successfully tested on painted, aluminum, glass, silica, and some composite surfaces, could aid in keeping medical assets clean.The Molecular Adsorber Coating is a zeolite-based, sprayable molecular adsorber coating, designed to prevent outgassing in materials in vacuums. The coating works well to adsorb volatiles and contaminates in manufacturing and processing, such as in pharmaceutical production. The addition of a biocide would also aid in controlling bacteria levels.

Wear Analysis of Thermal Spray Coatings on 3D Surfaces

NASA Astrophysics Data System (ADS)

Tillmann, W.; Luo, W.; Selvadurai, U.

2014-01-01

Even though the application of thermal spray coatings on complex geometries gained a greater interest in the last decade, the effect of different geometrical features on the wear behavior is still ill-defined. In this study, the wear resistance of FTC-FeCSiMn coated 3D surfaces was investigated. The wear test was carried out by means of two innovative testing procedures. The first test is a Pin-on-Tubes test where the rotating motion is realized by a lathe chuck. The specimens in the second test were fixed on the table and a robot arm operated the pin. This wear test was applied on specimens with concave or convex surfaces. The residual stresses, which were determined by means of an incremental hole-drilling method, show a dependency on the substrate geometry. The obtained stresses were put in relation to the different radii. After the wear test, a 3D-profilometer determined the wear volume and the sections of the coatings were characterized by a scanning electron microscope. The results indicate that the wear resistance is strongly influenced by the geometry of the substrate.

Throughput increase by adjustment of the BARC drying time with coat track process

NASA Astrophysics Data System (ADS)

Brakensiek, Nickolas L.; Long, Ryan

2005-05-01

Throughput of a coater module within the coater track is related to the solvent evaporation rate from the material that is being coated. Evaporation rate is controlled by the spin dynamics of the wafer and airflow dynamics over the wafer. Balancing these effects is the key to achieving very uniform coatings across a flat unpatterned wafer. As today"s coat tracks are being pushed to higher throughputs to match the scanner, the coat module throughput must be increased as well. For chemical manufacturers the evaporation rate of the material depends on the solvent used. One measure of relative evaporation rates is to compare flash points of a solvent. The lower the flash point, the quicker the solvent will evaporate. It is possible to formulate products with these volatile solvents although at a price. Shipping and manufacturing a more flammable product increase chances of fire, thereby increasing insurance premiums. Also, the end user of these chemicals will have to take extra precautions in the fab and in storage of these more flammable chemicals. An alternative coat process is possible which would allow higher throughput in a distinct coat module without sacrificing safety. A tradeoff is required for this process, that being a more complicated coat process and a higher viscosity chemical. The coat process uses the fact that evaporation rate depends on the spin dynamics of the wafer by utilizing a series of spin speeds that first would set the thickness of the material followed by a high spin speed to remove the residual solvent. This new process can yield a throughput of over 150 wafers per hour (wph) given two coat modules. The thickness uniformity of less than 2 nm (3 sigma) is still excellent, while drying times are shorter than 10 seconds to achieve the 150 wph throughput targets.

EVALUATION OF THE EFFECTIVENESS OF COATINGS IN REDUCING DISLODGEABLE ARSENIC, CHROMIUM, AND COPPER FROM CCA TREATED WOOD; FINAL REPORT

EPA Science Inventory

EPA conducted a study to evaluate the effect of coatings on dislodgeable arsenic, chromium, and copper residues on the surfaces of chromated copper arsenate (CAA) treated wood. Dislodgeable CCA, determined by wipe sampling the wood surfaces, was the primary evaluation criterion f...

Zircon-Based Ceramics Composite Coating for Environmental Barrier Coating

NASA Astrophysics Data System (ADS)

Suzuki, M.; Sodeoka, S.; Inoue, T.

2008-09-01

Studies on plasma spraying of zircon (ZrSiO4) have been carried out by the authors as one of the candidates for an environmental barrier coating (EBC) application, and had reported that substrate temperature is one of the most important factors to obtain crack-free and highly adhesive coating. In this study, several amounts of yttria were added to zircon powder, and the effect of the yttria addition on the structure and properties of the coatings were evaluated to improve the stability of the zircon coating structure at elevated temperature. The coatings obtained were composed of yttria-stabilized zirconia (YSZ), glassy silica, whereas the one prepared from monolithic zircon powder was composed of the metastable high temperature tetragonal phase of zirconia and glassy silica. After the heat treatment over 1200 °C, silica and zirconia formed zircon in all coatings. However, coatings with higher amounts of yttria exhibited lower amounts of zircon. This resulted in the less open porosity of the coating at elevated temperature. These yttria-added coatings also showed good adhesion even after the heat treatment, while monolithic zircon coating pealed off.

Long-duration orbital effects on optical coating materials

NASA Technical Reports Server (NTRS)

Herzig, Howard; Toft, Albert R.; Fleetwood, Charles M., Jr.

1993-01-01

We flew specimens of eight different optical coating materials in low earth orbit as part of the Long Duration Exposure Facility manifest to determine their ability to withstand exposure to the residual atomic 0 and other environmental effects at those altitudes. We included samples of Al, Au, Ir, Os, Pt, Al + MgF2, Al + SiO(x), and chemical-vapor-deposited SiC, representing reflective optical applications from the vacuum ultraviolet through the visible portions of the spectrum. We found that the majority of the materials suffered sufficient reflectance degradation to warrant careful consideration in the design of future space-flight instrumentation.

Tablet coating by injection molding technology - Optimization of coating formulation attributes and coating process parameters.

PubMed

Desai, Parind M; Puri, Vibha; Brancazio, David; Halkude, Bhakti S; Hartman, Jeremy E; Wahane, Aniket V; Martinez, Alexander R; Jensen, Keith D; Harinath, Eranda; Braatz, Richard D; Chun, Jung-Hoon; Trout, Bernhardt L

2018-01-01

We developed and evaluated a solvent-free injection molding (IM) coating technology that could be suitable for continuous manufacturing via incorporation with IM tableting. Coating formulations (coating polymers and plasticizers) were prepared using hot-melt extrusion and screened via stress-strain analysis employing a universal testing machine. Selected coating formulations were studied for their melt flow characteristics. Tablets were coated using a vertical injection molding unit. Process parameters like softening temperature, injection pressure, and cooling temperature played a very important role in IM coating processing. IM coating employing polyethylene oxide (PEO) based formulations required sufficient room humidity (>30% RH) to avoid immediate cracks, whereas other formulations were insensitive to the room humidity. Tested formulations based on Eudrajit E PO and Kollicoat IR had unsuitable mechanical properties. Three coating formulations based on hydroxypropyl pea starch, PEO 1,000,000 and Opadry had favorable mechanical (<700MPa Young's modulus, >35% elongation, >95×10 4 J/m 3 toughness) and melt flow (>0.4g/min) characteristics, that rendered acceptable IM coats. These three formulations increased the dissolution time by 10, 15 and 35min, respectively (75% drug release), compared to the uncoated tablets (15min). Coated tablets stored in several environmental conditions remained stable to cracking for the evaluated 8-week time period. Copyright © 2017 Elsevier B.V. All rights reserved.

Strip Coating Metrology on Large Scale Telescope Optics: Scalable Cost Saving Preventative Maintenance with First Contact Polymer

NASA Astrophysics Data System (ADS)

Hamilton, J.

2012-09-01

Protection and cleaning of precision optical surfaces on large scale astronomical instruments has entered a new era. First surface mirrors have been restored to "like-new" condition avoiding the expense and downtime of recoating. Nearly 10 years of testing and evaluation at a variety of sites including optics at Vandenberg Air Force Base, the Canada France Hawaii Telescope (CFHT) and the W.M Keck Telescope on Mauna Kea, have yielded impressive results: restored reflectivity, no residue, insitu cleaning and better coating performance when used as a precleaner when coating. Metrology and research in our labs has resulted in these novel, commercially available polymeric stripcoatings that are applied as a liquid and subsequently peeled off the substrate as a solid film. These designer polymer solutions safely clean and protect a wide variety of nanostructured surfaces and leave the surface almost atomically clean. Contaminant removal was monitored by a variety of techniques including Reflectivity, Nomarski, Atomic Force and Scanning Electron Microscopy as well as XPS. In addition, data demonstrates that the material safely removes particulate contamination and finger oils from nanostructures such as the 300nm wide lines on diffraction gratings and similar submicron features on Si wafers. High power laser damage testing found no residue on the optical surfaces following dried film removal and YAG laser damage thresholds after cleaning on coated BK7 of 15J/cm2 at 20ns and 20Hz were unchanged. Additionally to these adhesion tunable polymer systems, nanotube and graphene doped, ESD free polymer strip coatings for surface protection, nanoreplication, cleaning and dust mitigation have also been developed. Our coatings have been successfully used on diverse surfaces like high power laser optics, the Hope Diamond in Washington DC, CCD s for the 520 megapixel Dark Energy Survey Camera being built at Fermilab and lithographically fabbed detector surfaces for the Cryogenic Dark

Aluminide coatings

DOEpatents

Henager, Jr; Charles, H [Kennewick, WA; Shin, Yongsoon [Richland, WA; Samuels, William D [Richland, WA

2009-08-18

Disclosed herein are aluminide coatings. In one embodiment coatings are used as a barrier coating to protect a metal substrate, such as a steel or a superalloy, from various chemical environments, including oxidizing, reducing and/or sulfidizing conditions. In addition, the disclosed coatings can be used, for example, to prevent the substantial diffusion of various elements, such as chromium, at elevated service temperatures. Related methods for preparing protective coatings on metal substrates are also described.

On tide-induced Lagrangian residual current and residual transport: 1. Lagrangian residual current

USGS Publications Warehouse

Feng, Shizuo; Cheng, Ralph T.; Pangen, Xi

1986-01-01

Residual currents in tidal estuaries and coastal embayments have been recognized as fundamental factors which affect the long-term transport processes. It has been pointed out by previous studies that it is more relevant to use a Lagrangian mean velocity than an Eulerian mean velocity to determine the movements of water masses. Under weakly nonlinear approximation, the parameter k, which is the ratio of the net displacement of a labeled water mass in one tidal cycle to the tidal excursion, is assumed to be small. Solutions for tides, tidal current, and residual current have been considered for two-dimensional, barotropic estuaries and coastal seas. Particular attention has been paid to the distinction between the Lagrangian and Eulerian residual currents. When k is small, the first-order Lagrangian residual is shown to be the sum of the Eulerian residual current and the Stokes drift. The Lagrangian residual drift velocity or the second-order Lagrangian residual current has been shown to be dependent on the phase of tidal current. The Lagrangian drift velocity is induced by nonlinear interactions between tides, tidal currents, and the first-order residual currents, and it takes the form of an ellipse on a hodograph plane. Several examples are given to further demonstrate the unique properties of the Lagrangian residual current.

New method for determination of epichlorohydrin in epoxy-coated cans by oxolane derivatization and gas chromatography-mass spectrometry.

PubMed

Sung, Jun Hyun; Lee, Young Ja; Park, Hyun Jin

2008-08-01

A new method was developed for the determination of epichlorohydrin (ECH) in food contact surface of epoxy-coated cans. The oxolane derivative, which produced by reaction of epoxy moiety in ECH with cyclopentanone in the presence of borontrifluoride-diethyletherate, was analyzed by gas chromatography (GC)/mass spectrometry (MS). 1,2-Epoxyhexane was used as internal standard (IS), which produced an oxolane derivative under the same reaction mechanism as ECH. The developed method was validated with 1 ng ml(-1) of limit of detection (LOD, surface area related 20 ng dm(-2)), >0.999 of linearity. Good precision, which was tested both in terms of intra-day repeatability and inter-day reproducibility, and 97.3-102.7% of good recoveries were obtained on three spiked levels of 5.2, 40.3 and 149.1 ng ml(-1). The excellent validation data suggests that this method is more simple, quick and effective than the official method in European Committee for Standardization (CEN) to determine the residual amount of ECH in food contact materials for food law compliance test. The residual amount of ECH for 13 epoxy-coated can samples was analyzed, and none of the samples was found to be detectable levels of ECH in epoxy-coated cans.

COATED ALLOYS

DOEpatents

Harman, C.G.; O'Bannon, L.S.

1958-07-15

A coating is described for iron group metals and alloys, that is particularly suitable for use with nickel containing alloys. The coating is glassy in nature and consists of a mixture containing an alkali metal oxide, strontium oxide, and silicon oxide. When the glass coated nickel base metal is"fired'' at less than the melting point of the coating, it appears the nlckel diffuses into the vitreous coating, thus providing a closely adherent and protective cladding.

Intense pulsed light annealing of copper zinc tin sulfide nanocrystal coatings

DOE Office of Scientific and Technical Information (OSTI.GOV)

Williams, Bryce A.; Smeaton, Michelle A.; Holgate, Collin S.

2016-09-15

A promising method for forming the absorber layer in copper zinc tin sulfide [Cu{sub 2}ZnSnS{sub 4} (CZTS)] thin film solar cells is thermal annealing of coatings cast from dispersions of CZTS nanocrystals. Intense pulsed light (IPL) annealing utilizing xenon flash lamps is a potential high-throughput, low-cost, roll-to-roll manufacturing compatible alternative to thermal annealing in conventional furnaces. The authors studied the effects of flash energy density (3.9–11.6 J/cm{sup 2}) and number of flashes (1–400) during IPL annealing on the microstructure of CZTS nanocrystal coatings cast on molybdenum-coated soda lime glass substrates (Mo-coated SLG). The annealed coatings exhibited cracks with two distinct linearmore » crack densities, 0.01 and 0.2 μm{sup −1}, depending on the flash intensity and total number of flashes. Low density cracking (0.01 μm{sup −1}, ∼1 crack per 100 μm) is caused by decomposition of CZTS at the Mo-coating interface. Vapor decomposition products at the interface cause blisters as they escape the coating. Residual decomposition products within the blisters were imaged using confocal Raman spectroscopy. In support of this hypothesis, replacing the Mo-coated SLG substrate with quartz eliminated blistering and low-density cracking. High density cracking is caused by rapid thermal expansion and contraction of the coating constricted on the substrate as it is heated and cooled during IPL annealing. Finite element modeling showed that CZTS coatings on low thermal diffusivity materials (i.e., SLG) underwent significant differential heating with respect to the substrate with rapid rises and falls of the coating temperature as the flash is turned on and off, possibly causing a build-up of tensile stress within the coating prompting cracking. Use of a high thermal diffusivity substrate, such as a molybdenum foil (Mo foil), reduces this differential heating and eliminates the high-density cracking. IPL annealing in presence

Influence of Powder Morphology and Microstructure on the Cold Spray and Mechanical Properties of Ti6Al4V Coatings

NASA Astrophysics Data System (ADS)

Munagala, Venkata Naga Vamsi; Akinyi, Valary; Vo, Phuong; Chromik, Richard R.

2018-06-01

The powder microstructure and morphology has significant influence on the cold sprayability of Ti6Al4V coatings. Here, we compare the cold sprayability and properties of coatings obtained from Ti6Al4V powders of spherical morphology (SM) manufactured using plasma gas atomization and irregular morphology (IM) manufactured using the Armstrong process. Coatings deposited using IM powders had negligible porosity and better properties compared to coatings deposited using SM powders due to higher particle impact velocities, porous surface morphology and more deformable microstructure. To evaluate the cohesive strength, multi-scale indentation was performed and hardness loss parameter was calculated. Coatings deposited using SM powders exhibited poor cohesive strength compared to coatings deposited using IM powders. Images of the residual indents showed de-bonding and sliding of adjacent splats in the coatings deposited using SM powders irrespective of the load. Coatings deposited using IM powders showed no evidence of de-bonding at low loads. At high loads, splat de-bonding was observed resulting in hardness loss despite negligible porosity. Thus, while the powders from Armstrong process lead to a significant improvement in sprayability and coating properties, further optimization of powder and cold spray process will be required as well as consideration of post-annealing treatments to obtain acceptable cohesive strength.

Performance of vacuum plasma spray and HVOF bond coatings at 900° and 1100 °C

DOE Office of Scientific and Technical Information (OSTI.GOV)

Lance, Michael J.; Haynes, James A.; Pint, Bruce A.

The effects of Ti and B additions to a vacuum plasma sprayed (VPS) NiCoCrAlYHfSi bond coating on thermal barrier coating (TBC) performance were studied at 1100 °C and 900 °C and compared to high-velocity oxy-fuel (HVOF) bond coatings. Using alloy 247 substrates and air plasma sprayed Y2O3-stabilized ZrO2 top coatings, additions of B or Ti + B did not improve the average TBC lifetime in 1-h cycles at 1100 °C in air with 10% H2O. The addition of Ti resulted in a decrease in lifetime. Photo-stimulated luminescence spectroscopy was used to map residual stresses in the thermally-grown Al2O3 scale. Atmore » 900 °C, closer to a typical land based turbine operating bond coating temperature, specimens were examined after ten 500-h cycles in laboratory air and air with 10%H2O to study the effect of H2O. The addition of water vapor had little effect on the measured parabolic rate constants at 900 °C and a comparison of the oxide microstructures in both environments is reported.« less

Tribological investigation of diamond-like carbon coated micro-dimpled surface under bovine serum and osteoarthritis oriented synovial fluid

PubMed Central

Ghosh, Subir; Choudhury, Dipankar; Roy, Taposh; Bin Mamat, Azuddin; Masjuki, H H; Pingguan-Murphy, Belinda

2015-01-01

Osteoarthritis-oriented synovial fluid (OASF), i.e., that typical of a patient with osteoarthritis, has different physical and biological characteristics than bovine serum (BS), a lubricant widely used in biotribological investigations. Micro-dimpled and diamond-like carbon- (DLC) coated surfaces are key emerging interfaces for orthopedic implants. In this study, tribological performances of dimpled surfaces, with and without DLC coating, have been investigated under both BS and OASF. The friction tests were performed utilizing a pin on a disk tribometer, whereas contact pressure, speed, and temperature were simulated to a ‘medium walking gait’ of hip joint conditions. The mechanical properties of the specimen and the physical properties of the lubricant were characterized before the friction test. Raman analysis was conducted to identify the coating condition both before and after the test. The DLC-coated dimpled surface showed maximum hardness and residual stress. A DLC-coated dimpled surface under an OASF lubricated condition yielded a lower friction coefficient and wear compared to those of plain and dimpled specimens. The higher graphitization of coated materials with increasing load was confirmed by Raman spectroscopy. PMID:27877803

Rheology of Coating Materials and Their Coating Characteristics

NASA Astrophysics Data System (ADS)

Grabsch, C.; Grüner, S.; Otto, F.; Sommer, K.

2008-07-01

Lots of particles used in the pharmaceutical and the food industry are coated to protect the core material. But almost no investigations about the coating material behavior do exist. In this study the focus was on the rheological material properties of fat based coating materials. Rotational shear experiments to determine the viscosity of a material were compared to oscillatory shear tests to get information about the vicoelastic behavior of the coating materials. At the liquid state the viscosity and the viscoelastic properties showed a good analogy. The viscoelastic properties of the solid coating materials yielded differences between materials that have the same properties at the liquid state.

Method of Producing Controlled Thermal Expansion Coat for Thermal Barrier Coatings

NASA Technical Reports Server (NTRS)

Brindley, William J. (Inventor); Miller, Robert A. (Inventor); Aikin, Beverly J. M. (Inventor)

2000-01-01

An improved thermal barrier coating and method for producing and applying such is disclosed herein. The thermal barrier coatings includes a high temperature substrate, a first bond coat layer applied to the substrate of MCrAlX and a second bond coat layer of MCrAlX with particles of a particulate dispersed throughout the MCrAlX and the preferred particulate is Al2O3. The particles of the particulate dispersed throughout the second bond coat layer preferably have a diameter of less then the height of the peaks of the second bond coat layer or a diameter of less than 5 micron. The method of producing the second bond coat layer may either include the steps of mechanical alloying of particles throughout the second bond coat layer, attrition milling the particles of the particulate throughout the second bond coat layer, or using electrophoresis to disperse the particles throughout the second bond coat layer. In the preferred embodiment of the invention the first bond coat layer is applied to the substrate. and then the second bond coat layer is thermally sprayed onto the first bond coat layer. Further, in a preferred embodiment of the invention a ceramic insulating layer covers the second bond coat layer.

Analytical approaches to identify potential migrants in polyester-polyurethane can coatings.

PubMed

Louise Bradley, Emma; Driffield, Malcolm; Guthrie, James; Harmer, Nick; Thomas Oldring, Peter Kenneth; Castle, Laurence

2009-12-01

The safety of a polyester-polyurethane can coating has been assessed using a suite of complementary analytical methods to identify and estimate the concentrations of potential chemical migrants. The polyester was based on phthalic acids and aliphatic diols. The polyisocyanate cross-linking agent was 1-isocyanato-3-isocyanatomethyl-3,5,5-trimethyl cyclohexane homopolymer (IPDI) blocked with methylethylketone oxime (MEKO) to make a one-part formulation. The overall migrate, obtained using solvent extraction of cured films, comprised almost completely of 12 cyclic and one linear polyester oligomer up to molecular weight 800 and containing up to six monomer units. These 13 oligomers covered a total of 28 isomeric forms. Other minor components detected were plasticisers and surfactants as well as impurities present in the starting materials. There was no detectable residue of either the blocked isocyanate (<0.01 microg/dm(2)) used as the starting substance or the unblocked isocyanate (<0.02 microg/dm(2)). The level of extractable IPDI was used as an indicator of the completeness of cure in experimental coatings. These studies revealed that there was an influence of time, temperature and catalyst content. Polymerisation was also influenced by the additives used and by the ageing of the wet coating formulation over several months. These studies allow parameters to be specified to ensure that commercial production coatings receive a full cure giving low migration characteristics.

The Effect of Interface Roughness and Oxide Film Thickness on the Inelastic Response of Thermal Barrier Coatings to Thermal Cycling

NASA Technical Reports Server (NTRS)

Pindera, Marek-Jerzy; Aboudi, Jacob; Arnold, Steven M.

1999-01-01

The effects of interfacial roughness and oxide film thickness on thermally-induced stresses in plasma-sprayed thermal barrier coatings subjected to thermal cycling are investigated using the recently developed higher-order theory for functionally graded materials. The higher-order theory is shown to be a viable alternative to the finite-element approach, capable of modeling different interfacial roughness architectures in the presence of an aluminum oxide layer and capturing the high stress gradients that occur at the top coat/bond coat interface. The oxide layer thickness is demonstrated to have a substantially greater effect on the evolution of residual stresses than local variations in interfacial roughness. Further, the location of delamination initiation in the top coat is predicted to change with increasing oxide layer thickness. This result can be used to optimize the thickness of a pre-oxidized layer introduced at the top coat/bond coat interface in order to enhance TBC durability as suggested by some researchers. The results of our investigation also support a recently proposed hypothesis regarding delamination initiation and propagation in the presence of an evolving bond coat oxidation, while pointing to the importance of interfacial roughness details and specimen geometry in modeling this phenomenon.

Studies on the surface modification of TiN coatings using MEVVA ion implantation with selected metallic species

NASA Astrophysics Data System (ADS)

Ward, L. P.; Purushotham, K. P.; Manory, R. R.

2016-02-01

Improvement in the performance of TiN coatings can be achieved using surface modification techniques such as ion implantation. In the present study, physical vapor deposited (PVD) TiN coatings were implanted with Cr, Zr, Nb, Mo and W using the metal evaporation vacuum arc (MEVVA) technique at a constant nominal dose of 4 × 1016 ions cm-2 for all species. The samples were characterized before and after implantation, using Rutherford backscattering (RBS), glancing incident angle X-ray diffraction (GIXRD), atomic force microscopy (AFM) and optical microscopy. Friction and wear studies were performed under dry sliding conditions using a pin-on-disc CSEM Tribometer at 1 N load and 450 m sliding distance. A reduction in the grain size and surface roughness was observed after implantation with all five species. Little variation was observed in the residual stress values for all implanted TiN coatings, except for W implanted TiN which showed a pronounced increase in compressive residual stress. Mo-implanted samples showed a lower coefficient of friction and higher resistance to breakdown during the initial stages of testing than as-received samples. Significant reduction in wear rate was observed after implanting with Zr and Mo ions compared with unimplanted TiN. The presence of the Ti2N phase was observed with Cr implantation.

Corrosion resistant coating

DOEpatents

Wrobleski, D.A.; Benicewicz, B.C.; Thompson, K.G.; Bryan, C.J.

1997-08-19

A method of protecting a metal substrate from corrosion including coating a metal substrate of, e.g., steel, iron or aluminum, with a conductive polymer layer of, e.g., polyaniline, coating upon said metal substrate, and coating the conductive polymer-coated metal substrate with a layer of a topcoat upon the conductive polymer coating layer, is provided, together with the resultant coated article from said method.

Corrosion resistant coating

DOEpatents

Wrobleski, Debra A.; Benicewicz, Brian C.; Thompson, Karen G.; Bryan, Coleman J.

1997-01-01

A method of protecting a metal substrate from corrosion including coating a metal substrate of, e.g., steel, iron or aluminum, with a conductive polymer layer of, e.g., polyaniline, coating upon said metal substrate, and coating the conductive polymer-coated metal substrate with a layer of a topcoat upon the conductive polymer coating layer, is provided, together with the resultant coated article from said method.

Pixelated coatings and advanced IR coatings

NASA Astrophysics Data System (ADS)

Pradal, Fabien; Portier, Benjamin; Oussalah, Meihdi; Leplan, Hervé

2017-09-01

Reosc developed pixelated infrared coatings on detector. Reosc manufactured thick pixelated multilayer stacks on IR-focal plane arrays for bi-spectral imaging systems, demonstrating high filter performance, low crosstalk, and no deterioration of the device sensitivities. More recently, a 5-pixel filter matrix was designed and fabricated. Recent developments in pixelated coatings, shows that high performance infrared filters can be coated directly on detector for multispectral imaging. Next generation space instrument can benefit from this technology to reduce their weight and consumptions.

Effects of coating thickness on high power metal coated fibre lasers

NASA Astrophysics Data System (ADS)

Daniel, Jae M. O.; Simakov, Nikita; Hemming, Alexander; Clarkson, W. Andrew; Haub, John

2017-03-01

We investigate the effects of coating thickness on the scattering losses of metal coated active fibre. A range of low numerical aperture metal coated optical fibres are placed in etchant solutions whilst measuring propagation loss as a function of time. By utilising concurrent coating diameter measurements, we are able to correlate propagation losses with coating thickness. Experimentally we find a monotonic dependence on coating thickness and scattering loss. We present the results of this work, providing useful parameters for high power metal coated fibre laser designs.

Nanoscale View of Dewetting and Coating on Partially Wetted Solids.

PubMed

Deng, Yajun; Chen, Lei; Liu, Qiao; Yu, Jiapeng; Wang, Hao

2016-05-19

There remain significant gaps in our ability to predict dewetting and wetting despite the extensive study over the past century. An important reason is the absence of nanoscopic knowledge about the processes near the moving contact line. This experimental study for the first time obtained the liquid morphology within 10 nm of the contact line, which was receding at low speed (U < 50 nm/s). The results put an end to long-standing debate about the microscopic contact angle, which turned out to be varying with the speed as opposed to the constant-angle assumption that has been frequently employed in modeling. Moreover, a residual film of nanometer thickness ubiquitously remained on the solid after the receding contact line passed. This microscopic residual film modified the solid surface and thus made dewetting far from a simple reverse of wetting. A complete scenario for dewetting and coating is provided.

Phenol-formaldehyde intumescent coating composition and coating prepared therefrom

NASA Technical Reports Server (NTRS)

Salyer, Ival O. (Inventor); Fox, Bernard L. (Inventor)

1986-01-01

Intumescent coatings which form a thick, uniform, fine celled, low density foam upon exposure to a high intensity heat flux or flame are disclosed, the invention coatings comprise phenolic resin prepolymer containing a blowing agent and a nucleating agent; in the preferred embodiments the coatings also contains a silicone surfactant, the coatings are useful in thermal and fire protection systems.

The coat protein of prunus necrotic ringspot virus specifically binds to and regulates the conformation of its genomic RNA.

PubMed

Aparicio, Frederic; Vilar, Marçal; Perez-Payá, Enrique; Pallás, Vicente

2003-08-15

Binding of coat protein (CP) to the 3' nontranslated region (3'-NTR) of viral RNAs is a crucial requirement to establish the infection of Alfamo- and Ilarviruses. In vitro binding properties of the Prunus necrotic ringspot ilarvirus (PNRSV) CP to the 3'-NTR of its genomic RNA using purified E. coli- expressed CP and different synthetic peptides corresponding to a 26-residue sequence near the N-terminus were investigated by electrophoretic mobility shift assays. PNRSV CP bound to, at least, three different sites existing on the 3'-NTR. Moreover, the N-terminal region between amino acid residues 25 to 50 of the protein could function as an independent RNA-binding domain. Single exchange of some arginine residues by alanine eliminated the RNA-interaction capacity of the synthetic peptides, consistent with a crucial role for Arg residues common to many RNA-binding proteins possessing Arg-rich domains. Circular dichroism spectroscopy revealed that the RNA conformation is altered when amino-terminal CP peptides bind to the viral RNA. Finally, mutational analysis of the 3'-NTR suggested the presence of a pseudoknotted structure at this region on the PNRSV RNA that, when stabilized by the presence of Mg(2+), lost its capability to bind the coat protein. The existence of two mutually exclusive conformations for the 3'-NTR of PNRSV strongly suggests a similar regulatory mechanism at the 3'-NTR level in Alfamo- and Ilarvirus genera.

Multi-layer coatings

DOEpatents

Maghsoodi, Sina; Brophy, Brenor L.; Abrams, Ze'ev R.; Gonsalves, Peter R.

2016-06-28

Disclosed herein are coating materials and methods for applying a top-layer coating that is durable, abrasion resistant, highly transparent, hydrophobic, low-friction, moisture-sealing, anti-soiling, and self-cleaning to an existing conventional high temperature anti-reflective coating. The top coat imparts superior durability performance and new properties to the under-laying conventional high temperature anti-reflective coating without reducing the anti-reflectiveness of the coating. Methods and data for optimizing the relative thickness of the under-layer high temperature anti-reflective coating and the top-layer thickness for optimizing optical performance are also disclosed.

Low friction and galling resistant coatings and processes for coating

DOEpatents

Johnson, Roger N.

1987-01-01

The present invention describes coating processes and the resultant coated articles for use in high temperature sodium environments, such as those found in liquid metal fast breeder reactors and their associated systems. The substrate to which the coating is applied may be either an iron base or nickel base alloy. The coating itself is applied to the substrate by electro-spark deposition techniques which result in metallurgical bonding between the coating and the substrate. One coating according to the present invention involves electro-spark depositing material from a cemented chromium carbide electrode and an aluminum electrode. Another coating according to the present invention involves electro-spark depositing material from a cemented chromium carbide electrode and a nickel-base hardfacing alloy electrode.

Analysis of Particulate and Chemical Residue Resulting from Exposure to Burning and Abrading Composite Materials

DTIC Science & Technology

2013-05-31

21 Figure 15. Example of a Possible Foreign Object Observed in a Small Number of Slides. This Object May Be a Hair, Thread, or Plant Material that...h)anthracene Fluoranthene Fluorene Indeno(1,2,3-cd)pyrene Naphthalene Phenanthrene Pyrene 16 Distribution A. Approved for public release...material during sampling. These were subject to particle analysis as described above in order to estimate the coverage ratio and particle density of

Microstructure, Tensile Adhesion Strength and Thermal Shock Resistance of TBCs with Different Flame-Sprayed Bond Coat Materials Onto BMI Polyimide Matrix Composite

NASA Astrophysics Data System (ADS)

Abedi, H. R.; Salehi, M.; Shafyei, A.

2017-10-01

In this study, thermal barrier coatings (TBCs) composed of different bond coats (Zn, Al, Cu-8Al and Cu-6Sn) with mullite top coats were flame-sprayed and air-plasma-sprayed, respectively, onto bismaleimide matrix composites. These polyimide matrix composites are of interest to replace PMR-15, due to concerns about the toxicity of the MDA monomer from which PMR-15 is made. The results showed that pores and cracks appeared at the bond coat/substrate interface for the Al-bonded TBC because of its high thermal conductivity and diffusivity resulting in transferring of high heat flux and temperature to the polymeric substrate during top coat deposition. The other TBC systems due to the lower conductivity and diffusivity of bonding layers could decrease the adverse thermal effect on the polymer substrate during top coat deposition and exhibited adhesive bond coat/substrate interfaces. The tensile adhesion test showed that the adhesion strength of the coatings to the substrate is inversely proportional to the level of residual stress in the coatings. However, the adhesion strength of Al bond-coated sample decreased strongly after mullite top coat deposition due to thermal damage at the bond coat/substrate interface. TBC system with the Cu-6Sn bond coat exhibited the best thermal shock resistance, while Al-bonded TBC showed the lowest. It was inferred that thermal mismatch stresses and oxidation of the bond coats were the main factors causing failure in the thermal shock test.

Effects of nano-sized boron nitride (BN) reinforcement in expandable graphite based in-tumescent fire retardant coating

NASA Astrophysics Data System (ADS)

Zulkurnain, E. S.; Ahmad, F.; Gillani, Q. F.

2016-08-01

The purpose of in-tumescent fire retardant coating (IFRC) is to protect substrate from fire attack by limiting heat transfer. A range of coating formulations have been prepared using Bisphenol A epoxy resin BE-188 and polyamide solidifier H-2310 as two-part binder, ammonium polyphosphate (APP) as acid source, melamine (MEL) as the blowing agent, expandable graphite (EG) as carbon source and nano-boron nitride (BN) as inorganic nano filler. The filler was used to improve the performances of the APP-EG-MEL coating. The effects of nano-BN on the char morphology and thermal degradation were investigated by fire test, thermo gravimetric analysis (TGA), Fourier transform infrared spectroscopy (FTIR), X- ray photoelectron spectroscopy (XPS) and field emission scanning electron microscopy (FESEM). The results showed that by substituting or reinforcing of 4% weight percentage of nano-BN, residual weight of the char increases by 23.82% compared to APP-EG-MEL coating without filler. Higher carbon content was obtained in the char and a more compact char was produced. The results indicated that nano-BN could be used as a filler to improve thermal stability of the APP-EG-MEL coating.

Thermal Processing Effects on the Adhesive Strength of PS304 High Temperature Solid Lubricant Coatings

NASA Technical Reports Server (NTRS)

DellaCorte, Christopher; Edmonds, Brian J.; Benoy, Patricia A.

2001-01-01

In this paper the effects of post deposition heat treatments on the cohesive and adhesive strength properties of PS304, a plasma sprayed nickel-chrome based, high temperature solid lubricant coating deposited on stainless steel, are studied. Plasma spray deposited coating samples were exposed in air at temperatures from 432 to 650 C for up to 500 hr to promote residual stress relief, enhance particle to particle bonding and increase coating to substrate bond strength. Coating pull-off strength was measured using a commercial adhesion tester that utilizes 13 mm diameter aluminum pull studs attached to the coating surface with epoxy. Pull off force was automatically recorded and converted to coating pull off strength. As deposited coating samples were also tested as a baseline. The as-deposited (untreated) samples either delaminated at the coating-substrate interface or failed internally (cohesive failure) at about 17 MPa. Samples heat treated at temperatures above 540 C for 100 hr or at 600 C or above for more than 24 hr exhibited strengths above 31 MPa, nearly a two fold increase. Coating failure occurred inside the body of the coating (cohesive failure) for nearly all of the heat-treated samples and only occasionally at the coating substrate interface (adhesive failure). Metallographic analyses of heat-treated coatings indicate that the Nickel-Chromium binder in the PS304 appears to have segregated into two phases, a high nickel matrix phase and a high chromium precipitated phase. Analysis of the precipitates indicates the presence of silicon, a constituent of a flow enhancing additive in the commercial NiCr powder. The exact nature and structure of the precipitate phase is not known. This microstructural change is believed to be partially responsible for the coating strength increase. Diffusion bonding between particles may also be playing a role. Increasing the heat treatment temperature, exposure time or both accelerate the heat treatment process. Preliminary

Metal Coatings

NASA Technical Reports Server (NTRS)

1994-01-01

During the Apollo Program, General Magnaplate Corporation developed process techniques for bonding dry lubricant coatings to space metals. The coatings were not susceptible to outgassing and offered enhanced surface hardness and superior resistance to corrosion and wear. This development was necessary because conventional lubrication processes were inadequate for lightweight materials used in Apollo components. General Magnaplate built on the original technology and became a leader in development of high performance metallurgical surface enhancement coatings - "synergistic" coatings, - which are used in applications from pizza making to laser manufacture. Each of the coatings is designed to protect a specific metal or group of metals to solve problems encountered under operating conditions.

The peculiar behavior of the glass transition temperature of amorphous drug-polymer films coated on inert sugar spheres.

PubMed

Dereymaker, Aswin; Van Den Mooter, Guy

2015-05-01

Fluid bed coating has been proposed in the past as an alternative technology for manufacturing of drug-polymer amorphous solid dispersions, or so-called glass solutions. It has the advantage of being a one-step process, and thus omitting separate drying steps, addition of excipients, or manipulation of the dosage form. In search of an adequate sample preparation method for modulated differential scanning calorimetry analysis of beads coated with glass solutions, glass transition broadening and decrease of the glass transition temperature (Tg ) were observed with increasing particle size of crushed coated beads and crushed isolated films of indomethacin (INDO) and polyvinylpyrrolidone (PVP). Substituting INDO with naproxen gave comparable results. When ketoconazole was probed or the solvent in INDO-PVP films was switched to dichloromethane (DCM) or a methanol-DCM mixture, two distinct Tg regions were observed. Small particle sizes had a glass transition in the high Tg region, and large particle sizes had a glass transition in the low Tg region. This particle size-dependent glass transition was ascribed to different residual solvent amounts in the bulk and at the surface of the particles. A correlation was observed between the deviation of the Tg from that calculated from the Gordon-Taylor equation and the amount of residual solvent at the Tg of particles with different sizes. © 2015 Wiley Periodicals, Inc. and the American Pharmacists Association.

Dissolution behavior and early bone apposition of calcium phosphate-coated machined implants

PubMed Central

Hwang, Ji-Wan; Lee, Eun-Ung; Lee, Jung-Seok; Jung, Ui-Won; Lee, In-Seop

2013-01-01

Purpose Calcium phosphate (CaP)-coated implants promote osseointegration and survival rate. The aim of this study was to (1) analyze the dissolution behavior of the residual CaP particles of removed implants and (2) evaluate bone apposition of CaP-coated machined surface implants at the early healing phase. Methods Mandibular premolars were extracted from five dogs. After eight weeks, the implants were placed according to drilling protocols: a nonmobile implant (NI) group and rotational implant (RI) group. For CaP dissolution behavior analysis, 8 implants were removed after 0, 1, 2, and 4 weeks. The surface morphology and deposition of the coatings were observed. For bone apposition analysis, block sections were obtained after 1-, 2-, and 4-week healing periods and the specimens were analyzed. Results Calcium and phosphorus were detected in the implants that were removed immediately after insertion, and the other implants were composed mainly of titanium. There were no notable differences between the NI and RI groups in terms of the healing process. The bone-to-implant contact and bone density in the RI group showed a remarkable increase after 2 weeks of healing. Conclusions It can be speculated that the CaP coating dissolves early in the healing phase and chemically induces early bone formation regardless of the primary stability. PMID:24455442

APS TBC performance on directionally-solidified superalloy substrates with HVOF NiCoCrAlYHfSi bond coatings

DOE PAGES

Lance, Michael J.; Unocic, Kinga A.; Haynes, James A.; ...

2015-09-04

Directionally-solidified (DS) superalloy components with advanced thermal barrier coatings (TBC) to lower the metal operating temperature have the potential to replace more expensive single crystal superalloys for large land-based turbines. In order to assess relative TBC performance, furnace cyclic testing was used with superalloys 1483, X4 and Hf-rich DS 247 substrates and high velocity oxygen fuel (HVOF)-NiCoCrAlYHfSi bond coatings at 1100 °C with 1-h cycles in air with 10% H 2O. With these coating and test conditions, there was no statistically-significant effect of substrate alloy on the average lifetime of the air plasma sprayed (APS) yttria-stabilized zirconia (YSZ) top coatingsmore » on small coupons. Using photo-stimulated luminescence piezospectroscopy maps at regular cycling intervals, the residual compressive stress in the α-Al 2O 3 scale underneath the YSZ top coating and on a bare bond coating was similar for all three substrates and delaminations occurred at roughly the same rate and frequency. As a result, x-ray fluorescence (XRF) measurements collected from the bare bond coating surface revealed higher Ti interdiffusion occurring with the 1483 substrate, which contained the highest Ti content.« less

Bonding of Resin Cement to Zirconia with High Pressure Primer Coating

PubMed Central

Wang, Ying-jie; Jiao, Kai; Liu, Yan; Zhou, Wei; Shen, Li-juan; Fang, Ming; Li, Meng; Zhang, Xiang; Tay, Franklin R.; Chen, Ji-hua

2014-01-01

Objectives To investigate the effect of air-drying pressure during ceramic primer coating on zirconia/resin bonding and the surface characteristics of the primed zirconia. Methods Two ceramic primers (Clearfil Ceramic Primer, CCP, Kuraray Medical Inc. and Z-Prime Plus, ZPP, Bisco Inc.) were applied on the surface of air-abraded zirconia (Katana zirconia, Noritake) and dried at 4 different air pressures (0.1–0.4 MPa). The primed zirconia ceramic specimens were bonded with a resin-based luting agent (SA Luting Cement, Kuraray). Micro-shear bond strengths of the bonded specimens were tested after 3 days of water storage or 5,000× thermocycling (n = 12). Failure modes of the fractured specimens were examined with scanning electron miscopy. The effects of air pressure on the thickness of the primer layers and the surface roughness (Sa) of primed zirconia were evaluated using spectroscopic ellipsometry (n = 6), optical profilometry and environmental scanning electron microscopy (ESEM) (n = 6), respectively. Results Clearfil Ceramic Primer air-dried at 0.3 and 0.4 MPa, yielding significantly higher µSBS than gentle air-drying subgroups (p<0.05). Compared to vigorous drying conditions, Z-Prime Plus air-dried at 0.2 MPa exhibited significantly higher µSBS (p<0.05). Increasing air-drying pressure reduced the film thickness for both primers. Profilometry measurements and ESEM showed rougher surfaces in the high pressure subgroups of CCP and intermediate pressure subgroup of ZPP. Conclusion Air-drying pressure influences resin/zirconia bond strength and durability significantly. Higher air-drying pressure (0.3-0.4 MPa) for CCP and intermediate pressure (0.2 MPa) for ZPP are recommended to produce strong, durable bonds between resin cement and zirconia ceramics. PMID:24992678

Do adhesive systems leave resin coats on the surfaces of the metal matrix bands? An adhesive remnant characterization.

PubMed

Arhun, Neslihan; Cehreli, Sevi Burcak

2013-01-01

Reestablishing proximal contacts with composite resins may prove challenging since the applied adhesives may lead to resin coating that produces additional thickness. The aim of this study was to investigate the surface of metal matrix bands after application of adhesive systems and blowing or wiping off the adhesive before polymerization. Seventeen groups of matrix bands were prepared. The remnant particles were characterized by energy dispersive spectrum and scanning electron microscopy. Total etch and two-step self-etch adhesives did not leave any resin residues by wiping and blowing off. All-in-one adhesive revealed resin residues despite wiping off. Prime and Bond NT did not leave any remnant with compomer. Clinicians must be made aware of the consequences of possible adhesive remnants on matrix bands that may lead to a defective definitive restoration. The adhesive resin used for Class II restorations may leave resin coats on metal matrix bands after polymerization, resulting in additional thickness on the metal matrix bands and poor quality of the proximal surface of the definitive restoration when the adhesive system is incorporated in the restoration.

Thermal radiative properties: Coatings.

NASA Technical Reports Server (NTRS)

Touloukian, Y. S.; Dewitt, D. P.; Hernicz, R. S.

1972-01-01

This volume consists, for the most part, of a presentation of numerical data compiled over the years in a most comprehensive manner on coatings for all applications, in particular, thermal control. After a moderately detailed discussion of the theoretical nature of the thermal radiative properties of coatings, together with an overview of predictive procedures and recognized experimental techniques, extensive numerical data on the thermal radiative properties of pigmented, contact, and conversion coatings are presented. These data cover metallic and nonmetallic pigmented coatings, enamels, metallic and nonmetallic contact coatings, antireflection coatings, resin coatings, metallic black coatings, and anodized and oxidized conversion coatings.

Protection of alodine coatings from thermal aging by removable polymer coatings.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wagstaff, Brett R.; Bradshaw, Robert W.; Whinnery, LeRoy L., Jr.

2006-12-01

Removable polymer coatings were evaluated as a means to suppress dehydration of Alodine chromate conversion coatings during thermal aging and thereby retain the corrosion protection afforded by Alodine. Two types of polymer coatings were applied to Alodine-treated panels of aluminum alloys 7075-T73 and 6061-T6 that were subsequently aged for 15 to 50 hours at temperatures between 135 F to 200 F. The corrosion resistance of the thermally aged panels was evaluated, after stripping the polymer coatings, by exposure to a standard salt-fog corrosion test and the extent of pitting of the polymer-coated and untreated panels compared. Removable polymer coatings mitigatedmore » the loss of corrosion resistance due to thermal aging experienced by the untreated alloys. An epoxide coating was more effective than a fluorosilicone coating as a dehydration barrier.« less

Coated Aerogel Beads

NASA Technical Reports Server (NTRS)

Littman, Howard (Inventor); Plawsky, Joel L. (Inventor); Paccione, John D. (Inventor)

2014-01-01

Methods and apparatus for coating particulate material are provided. The apparatus includes a vessel having a top and a bottom, a vertically extending conduit having an inlet in the vessel and an outlet outside of the vessel, a first fluid inlet in the bottom of the vessel for introducing a transfer fluid, a second fluid inlet in the bottom of the vessel for introducing a coating fluid, and a fluid outlet from the vessel. The method includes steps of agitating a material, contacting the material with a coating material, and drying the coating material to produce a coated material. The invention may be adapted to coat aerogel beads, among other materials. A coated aerogel bead and an aerogel-based insulation material are also disclosed.

Molecular Adsorber Coating

NASA Technical Reports Server (NTRS)

Straka, Sharon; Peters, Wanda; Hasegawa, Mark; Hedgeland, Randy; Petro, John; Novo-Gradac, Kevin; Wong, Alfred; Triolo, Jack; Miller, Cory

2011-01-01

A document discusses a zeolite-based sprayable molecular adsorber coating that has been developed to alleviate the size and weight issues of current ceramic puck-based technology, while providing a configuration that more projects can use to protect against degradation from outgassed materials within a spacecraft, particularly contamination-sensitive instruments. This coating system demonstrates five times the adsorption capacity of previously developed adsorber coating slurries. The molecular adsorber formulation was developed and refined, and a procedure for spray application was developed. Samples were spray-coated and tested for capacity, thermal optical/radiative properties, coating adhesion, and thermal cycling. Work performed during this study indicates that the molecular adsorber formulation can be applied to aluminum, stainless steel, or other metal substrates that can accept silicate-based coatings. The coating can also function as a thermal- control coating. This adsorber will dramatically reduce the mass and volume restrictions, and is less expensive than the currently used molecular adsorber puck design.

Characterization, optical properties and laser ablation behavior of epoxy resin coatings reinforced with high reflectivity ceramic particles

NASA Astrophysics Data System (ADS)

Li, Wenzhi; Kong, Jing; Wu, Taotao; Gao, Lihong; Ma, Zhuang; Liu, Yanbo; Wang, Fuchi; Wei, Chenghua; Wang, Lijun

2018-04-01

Thermal damage induced by high power energy, especially high power laser, significantly affects the lifetime and performance of equipment. High-reflectance coating/film has attracted considerable attention due to its good performance in the damage protection. Preparing a high-reflectance coating with high reaction endothermal enthalpy will effectively consume a large amount of incident energy and in turn protect the substrate from thermal damage. In this study, a low temperature process was used to prepare coatings onto substrate with complex shape and avoid thermal effect during molding. An advanced high reflection ceramic powder, La1‑xSrxTiO3+δ , was added in the epoxy adhesive matrix to improve the reflectivity of coating. The optical properties and laser ablation behaviors of coatings with different ceramic additive ratio of La1‑xSrxTiO3+δ and modified epoxy-La1‑xSrxTiO3+δ with ammonium polyphosphate coatings were investigated, respectively. We found that the reflectivity of coatings is extremely high due to mixed high-reflection La1‑xSrxTiO3+δ particles, up to 96% at 1070 nm, which can significantly improve the laser resistance. In addition, the ammonium polyphosphate modifies the residual carbon structure of epoxy resin from discontinuous fine particles structure to continuous and porous structure, which greatly enhances the thermal-insulation property of coating. Furthermore, the laser ablation threshold is improved obviously, which is from 800 W cm‑2 to 1000 W cm‑2.

Immobilization of pectinase and lipase on macroporous resin coated with chitosan for treatment of whitewater from papermaking.

PubMed

Liu, Kai; Zhao, Guanglei; He, Beihai; Chen, Lihui; Huang, Liulian

2012-11-01

Anionic residues and pitch deposits in whitewater negatively impact the operation of paper-forming equipment. In order to remove these substances, a macroporous resin based on a methyl acrylate matrix was synthesized and coated with chitosan of various molecular weights through glutaraldehyde cross-linking. Pectinase from Bacillus licheniformis and lipase from Thermomyces lanuginosus were immobilized on the resin coated with chitosan by a Schiff base reaction. The highest hydrolysis activities of the immobilized enzymes were achieved by using chitosan with 10×10(5)DaMW for coating and 0.0025% glutaraldehyde for cross-linking chitosan. The cationic demand and pitch deposits in whitewater were reduced by 58% and 74%, respectively, when treating whitewater with immobilized dual-enzymes for 15min at 55°C and pH 7.5. This method is useful for treatment of whitewater in the papermaking industry. Copyright © 2012 Elsevier Ltd. All rights reserved.

Nonadhesive, silica nanoparticles-based brush-coated contact lens cases--compromising between ease of cleaning and microbial transmission to contact lenses.

PubMed

Qu, Wenwen; Hooymans, Johanna M M; Qiu, Jun; de-Bont, Nik; Gelling, Onko-Jan; van der Mei, Henny C; Busscher, Henk J

2013-05-01

Surface properties of lens cases are determinant for their cleanability and for microbial transmission from lens cases to contact lenses (CLs). PEG-polymer-brush-coatings are known to decrease microbial adhesion more than other surface-coatings. Here, we applied a robust, silica nanoparticles-based brush-coating to polypropylene cases to evaluate their ease of cleaning and probability of bacterial transmission to CLs. Adhesion forces of nine bacterial strains (Pseudomonas, Staphylococci, and Serratia) to rigid CLs, polypropylene, and silica nanoparticles-based brush-coated polypropylene were measured using atomic-force-microscopy and subjected to Weibull analyses to yield bacterial transmission probabilities. Biofilms of each strain were grown in coated and uncoated cases and rinsed with a NaCl or antimicrobial lens care solution. Residual, viable organisms were quantified. Bacterial adhesion forces of all strains were significantly, up to tenfold smaller on brush-coated than on uncoated polypropylene. This yielded, higher transmission probabilities to a CL, but mild-rinsing yielded 10-100 fold higher removal of bacteria from brush-coated than from polypropylene cases. Moreover, due to weak adhesion forces, bacteria on brush-coated cases were two-to-three fold more susceptible to an antimicrobial lens care solution than on polypropylene cases. Therewith, the design of lens case surfaces is a compromise between ease of cleaning and transmission probability to CLs. Copyright © 2013 Wiley Periodicals, Inc.

Raman microscopic studies of PVD deposited hard ceramic coatings

NASA Astrophysics Data System (ADS)

Constable, Christopher Paul

. This was then expanded to real wear situations in which tools were monitored after 3,6,12,64,120 and 130 minutes-in-cut. A PCA chemometrics model able to distinguish between component layers and oxides was developed.Raman microscopy was found to provide structural and compositional information on oxide scales formed on the surfaces of heat-treated coatings. Wear debris, generated as a consequence of sliding wear tests on various coatings, was also found to be primarily oxide products. The comparison of the oxide types within the debris to those formed on the surface of the same coating statically oxidised, facilitated a contact temperature during sliding to be estimated.Raman microscopy, owing to the piezo-spectroscopic effect, is sensitive to stress levels. The application of Raman microscopy for the determination of residual compressive stresses within PVD coatings was evaluated. TiAlN/VN superlattice coatings with engineered stresses ranging -3 to -11.3 GPa were deposited onto SS and HSS substrates. Subsequent Raman measurements found a correlation coefficient of 0.996 between Raman band position and stress (determined via XRD methods). In addition, there was also a similar correlation coefficient observed between hardness and Raman shift (cm-1). The application of mechanical stresses on a TiAlCrN coating via a stress rig was investigated and tensile and compressive shifts were observed.

An iodine supplementation of tomato fruits coated with an edible film of the iodide-doped chitosan.

PubMed

Limchoowong, Nunticha; Sricharoen, Phitchan; Techawongstien, Suchila; Chanthai, Saksit

2016-06-01

In general, the risk of numerous thyroid cancers inevitably increases among people with iodine deficiencies. An iodide-doped chitosan (CT-I) solution was prepared for dipping tomatoes to coat the fresh surface with an edible film (1.5 μm), thereby providing iodine-rich fruits for daily intake. Characterisation of the thin film was conducted by FTIR and SEM. Stability of the CT-I film was studied via water immersion at various time intervals, and no residual iodide leached out due to intrinsic interactions between the cationic amino group of chitosan and iodide ions. Moreover, the iodide supplement exhibited no effect on the antioxidant activity of tomatoes. The iodine content in the film-coated tomato was determined by ICP-OES. The tomato coating with 1.5% (w/v) CT-I contained approximately 0.4 μg iodide per gram fresh weight. In addition, the freshness and storability of iodine-doped tomatoes were also maintained for shelf-life concerns. Copyright © 2016 Elsevier Ltd. All rights reserved.

Effect of sandblasting intensity on microstructures and properties of pure titanium micro-arc oxidation coatings in an optimized composite technique

NASA Astrophysics Data System (ADS)

Wang, Hong-Yuan; Zhu, Rui-Fu; Lu, Yu-Peng; Xiao, Gui-Yong; He, Kun; Yuan, Y. F.; Ma, Xiao-Ni; Li, Ying

2014-02-01

Sandblasting is one of the most effective methods to modify a metal surface and improve its properties for application. Micro-arc oxidation (MAO) could produce a ceramic coating on a dental implant, facilitating cellular differentiation and osseocomposite on it. This study aims to deposit bioceramic Ca- and P-containing coatings on sandblasted commercially pure titanium by an optimum composite technique to improve the bioactive performance. The effect of sandblasting intensity on microstructures and properties of the implant coatings is examined, and the modified surfaces are characterized in terms of their topography, phase, chemical composition, mechanical properties and hydroxyapatite (HA)-inducing ability. The results show that a moderate sandblasting micromachines the substrate in favorable combination of rough and residual stresses; its MAO coating deposits nano-hydroxyapatite after immersion in simulated body fluid (SBF) for 5 days exhibiting better bioactivity. The further improvement of the implant surface performance is attributed to an optimized composite technique.

Top coat or no top coat for immersion lithography?

NASA Astrophysics Data System (ADS)

Stepanenko, N.; Kim, Hyun-Woo; Kishimura, S.; Van Den Heuvel, D.; Vandenbroeck, N.; Kocsis, M.; Foubert, P.; Maenhoudt, M.; Ercken, M.; Van Roey, F.; Gronheid, R.; Pollentier, I.; Vangoidsenhoven, D.; Delvaux, C.; Baerts, C.; O'Brien, S.; Fyen, W.; Wells, G.

2006-03-01

Since the moment immersion lithography appeared in the roadmaps of IC manufacturers, the question whether to use top coats has become one of the important topics for discussions. The top coats used in immersion lithography have proved to serve as good protectors from leaching of the resist components (PAGs, bases) into the water. However their application complicates the process and may lead to two side effects. First, top coats can affect the process window and resist profile depending on the material's refractive index, thickness, acidity, chemical interaction with the resist and the soaking time. Second, the top coat application may increase the total amount of defects on the wafer. Having an immersion resist which could work without the top coat would be a preferable solution. Still, it is quite challenging to make such a resist as direct water/resist interaction may also result in process window changes, CD variations, generation of additional defects. We have performed a systematic evaluation of a large number of immersion resist and top coat combinations, using the ASML XT:1250Di scanner at IMEC. The samples for the experiments were provided by all the leading resist and top coat suppliers. Particular attention was paid to how the resist and top coat materials from different vendors interacted with each other. Among the factors which could influence the total amount of defects or CD variations on the wafer were: the material's dynamic contact angle and its interaction with the scanner stage speed, top coat thickness and intermixing layer formation, water uptake and leaching. We have examined the importance of all mentioned factors, using such analytical techniques as Resist Development Analyser (RDA), Quartz Crystal Microbalance (QCM), Mass Spectroscopy (MS) and scatterometry. We have also evaluated the influence of the pre- and pos- exposure rinse processes on the defectivity. In this paper we will present the data on imaging and defectivity performance of

Influence of the Manufacturing Process on Defects in the Galvanized Coating of High Carbon Steel Wires.

PubMed

Gelfi, Marcello; Solazzi, Luigi; Poli, Sandro

2017-03-06

This study is a detailed failure analysis of galvanized high carbon steel wires, which developed coating cracks during the torsion test performed as a quality control at the end of the manufacturing process. Careful visual inspections showed that the cracks are already present in the coating before the torsion test. In order to explain the origin of these cracks, systematic metallographic investigations were performed by means of optical and scanning electron microscope on both the wires and the rods that have been cold drawn to produce the wire. The chemical composition of the galvanized coatings was evaluated by means of energy dispersive spectroscopy. Micro bidimensional X-ray diffraction experiments were also performed to measure the residual stresses in the galvanized coating. The results showed that the failure is related to two main factors: the relatively high content of silicon in the steel and the unsuitable cooling rate of the rods at the exit from the galvanizing bath. The mechanism proposed to explain the origin of the defects was supported by Finite Elements Methods simulations and verified with in-plant tests. The proper countermeasures were then applied and the problem successfully solved.

Influence of the Manufacturing Process on Defects in the Galvanized Coating of High Carbon Steel Wires

PubMed Central

Gelfi, Marcello; Solazzi, Luigi; Poli, Sandro

2017-01-01

This study is a detailed failure analysis of galvanized high carbon steel wires, which developed coating cracks during the torsion test performed as a quality control at the end of the manufacturing process. Careful visual inspections showed that the cracks are already present in the coating before the torsion test. In order to explain the origin of these cracks, systematic metallographic investigations were performed by means of optical and scanning electron microscope on both the wires and the rods that have been cold drawn to produce the wire. The chemical composition of the galvanized coatings was evaluated by means of energy dispersive spectroscopy. Micro bidimensional X-ray diffraction experiments were also performed to measure the residual stresses in the galvanized coating. The results showed that the failure is related to two main factors: the relatively high content of silicon in the steel and the unsuitable cooling rate of the rods at the exit from the galvanizing bath. The mechanism proposed to explain the origin of the defects was supported by Finite Elements Methods simulations and verified with in-plant tests. The proper countermeasures were then applied and the problem successfully solved. PMID:28772623

Environmental barrier coating (EBC) durability modeling using a progressive failure analysis approach

NASA Astrophysics Data System (ADS)

Abdul-Aziz, Ali; Abumeri, Galib; Troha, William; Bhatt, Ramakrishna T.; Grady, Joseph E.; Zhu, D.

2012-04-01

Ceramic matrix composites (CMCs) are getting the attention of most engine manufacturers and aerospace firms for turbine engine and other related applications. This is because of their potential weight advantage and performance benefits. As a protecting guard for these materials, a highly specialized form of environmental barrier coating (EBC) is being developed and explored for high temperature applications that are greater than 1100 °C1,2. The EBCs are typically a multilayer of coatings and are on the order of hundreds of microns thick. CMCs are generally porous materials and this feature is somewhat beneficial since it allows some desirable infiltration of the EBC. Their degradation usually includes coating interface oxidation as opposed to moisture induced matrix degradation which is generally seen at a higher temperature. A variety of factors such as residual stresses, coating process related flaws, and casting conditions may influence the strength of degradation. The cause of such defects which cause cracking and other damage is that not much energy is absorbed during fracture of these materials. Therefore, an understanding of the issues that control crack deflection and propagation along interfaces is needed to maximize the energy dissipation capabilities of layered ceramics. Thus, evaluating components and subcomponents made out of CMCs under gas turbine engine conditions is suggested to demonstrate that these material will perform as expected and required under these aggressive environmental circumstances. Progressive failure analysis (PFA) is applied to assess the damage growth of the coating under combined thermal and mechanical loading conditions. The PFA evaluation is carried out using a full-scale finite element model to account for the average material failure at the microscopic or macroscopic levels. The PFA life prediction evaluation identified the root cause for damage initiation and propagation. It indicated that delamination type damage

Stent Coating Integrity of Durable and Biodegradable Coated Drug Eluting Stents.

PubMed

Yazdani, Saami K; Sheehy, Alexander; Pacetti, Stephen; Rittlemeyer, Brandon; Kolodgie, Frank D; Virmani, Renu

2016-10-01

Coatings consisting of a polymer and drug are widely used in drug-eluting stents (DES) and are essential in providing programmable drug release kinetics. Among other factors, stent coating technologies can influence blood compatibility, affect acute and sub-acute healing, and potentially trigger a chronic inflammatory response. The aim of this study was to investigate the short-term (7 and 28 days) and long-term (90 and 180 days) coating integrity of the Xience Prime Everolimus-Eluting Stent (EES), Resolute Zotarolimus-Eluting Stent (ZES), Taxus Paclitaxel-Eluting Stent (PES), and Nobori Biolimus A9-Eluting Stent (BES) in a rabbit ilio-femoral stent model. Stented arteries (n = 48) were harvested and the tissue surrounding the implanted stents digested away with an enzymatic solution. Results demonstrated that the majority of struts of EES were without any coating defects with a few struts showing minor defects. Similarly, for the ZES, most of the struts were without coating defects at all time points except at 180 days. The majority of PES demonstrated mostly webbing and uneven coating. In the BES group, the majority of strut coating showed polymer cracking. Overall, the EES and ZES had fewer coating defects than the PES and BES. Coating defects, however increase over time for the ZES, whereas the percent of coating irregularities remained constant for the EES. These results provide, for the first time, a comparison of the long-term durability of these drug-eluting stent coatings in vivo. © 2016, Wiley Periodicals, Inc.

Coatings for directional eutectics

NASA Technical Reports Server (NTRS)

Rairden, J. R.; Jackson, M. R.

1976-01-01

Significant advances have been made in the development of an environmentally stable coating for a very high strength, directionally solidified eutectic alloy designated NiTaC-13. Three duplex (two-layer) coatings survived 3,000 hours on a cyclic oxidation test (1,100 C to 90 C). These coatings were fabricated by first depositing a layer of NiCrAl(Y) by vacuum evaporation from an electron beam heated source, followed by depositing an aluminizing overlayer. The alloy after exposure with these coatings was denuded of carbide fibers at the substrate/coating interface. It was demonstrated that TaC fiber denudation can be greatly retarded by applying a carbon-bearing coating. The coating was applied by thermal spraying followed by aluminization. Specimens coated with NiCrAlCY+Al survived over 2,000 hours in the cyclic oxidation test with essentially no TaC denudation. Coating ductility was studied for coated and heat-treated bars, and stress rupture life at 871 C and 1,100 C was determined for coated and cycled bars.

CTAB-coated gold nanorods elicit allergic response through degranulation and cell death in human basophils

NASA Astrophysics Data System (ADS)

Cheung, Ka Lun; Chen, Huanjun; Chen, Qiulan; Wang, Jianfang; Ho, Ho Pui; Wong, Chun Kwok; Kong, Siu Kai

2012-07-01

The effect of CTAB (cetyltrimethylammonium bromide)- or PEG (polyethylene glycol)-coated gold-nanorods (Au-NRs) on the non-IgE mediated allergic response was studied. We found that the CTAB-Au-NRs released more allergic mediators such as histamine and β-hexosaminidase from human basophil KU812, a common model for studying allergy, after 20 min incubation. Also, the CTAB-Au-NRs induced more apoptosis than the PEG-Au-NRs in KU812 24 h after treatment. These short- and long-term effects were not solely due to the CTAB residues in the supernatant desorbed from the Au-NRs.The effect of CTAB (cetyltrimethylammonium bromide)- or PEG (polyethylene glycol)-coated gold-nanorods (Au-NRs) on the non-IgE mediated allergic response was studied. We found that the CTAB-Au-NRs released more allergic mediators such as histamine and β-hexosaminidase from human basophil KU812, a common model for studying allergy, after 20 min incubation. Also, the CTAB-Au-NRs induced more apoptosis than the PEG-Au-NRs in KU812 24 h after treatment. These short- and long-term effects were not solely due to the CTAB residues in the supernatant desorbed from the Au-NRs. Electronic supplementary information (ESI) available. See DOI: 10.1039/c2nr30435j

Multispectral Coatings

DTIC Science & Technology

2010-01-01

failure, whereas the polymer nanocomposite gave ductile failure with less surface damage. Task 2. Highly reflective self-assembled coatings . The...AFRL-RX-WP-TR-2010-4036 MULTISPECTRAL COATINGS Eric Grulke University of Kentucky Thad Druffel Optical Dynamics JANUARY...REPORT TYPE 3. DATES COVERED (From - To) January 2010 Final 28 November 2005 – 30 September 2008 4. TITLE AND SUBTITLE MULTISPECTRAL COATINGS 5a

Solvent Effects of Model Polymeric Corrosion Control Coatings on Water Transport and Corrosion Rate

NASA Astrophysics Data System (ADS)

Konecki, Christina

Industrial coating formulations are often made for volatile organic content compliance and ease of application, with little regard for the solvent impact on resultant performance characteristics. Our research objective was to understand the effect of both solvent retention and chemical structure on water transport through polymer films and resultant corrosion area growth of coated steel substrates. A clear, unpigmented Phenoxy(TM) thermoplastic polymer (PKHH) was formulated into resin solutions with three separate solvent blends selected by Hansen solubility parameter (HSP), boiling point, and ability to solubilize PKHH. Polymer films cast from MEK/PGME (methyl ethyl ketone/ propylene glycol methyl ether), dried under ambient conditions (AMB, > 6wt.% residual solvent) produced a porous morphology, which resulted in a corrosion area greater than 50%. We attributed this to the water-soluble solvent used in film preparation, which enabled residual PGME to be extracted by water. The resin solution prepared with CYCOH/DXL (Cyclohexanol/ 1,3 dioxolane) was selected because CYCOH is a solid at room temperature which acts as a pigment in the final film. Therefore, increasing the tortuosity of water transport, as well as a high hydrogen bonding character, which caused more interactions with water, slowing diffusion, producing a nodular morphology, and 37% less corrosion area than MEK/PGME AMB. The HSP of PKHH and EEP (ethyl 3-ethoxypropionate) are within 5% of each other, which produced a homogeneous morphology and resulted in comparable corrosion rates regardless of residual solvent content. We utilized electrochemical techniques and attenuated total reflectance- Fourier transform infrared spectroscopy to elucidate dynamic water absorption and solvent extraction in the exposed model formulations. We found that water absorption resulted in a loss of barrier properties, and increased corrosion due to the voids formed by solvent extraction. The polymer films were rejuvenated

An In Situ Method for Sizing Insoluble Residues in Precipitation and Other Aqueous Samples

PubMed Central

Axson, Jessica L.; Creamean, Jessie M.; Bondy, Amy L.; Capracotta, Sonja S.; Warner, Katy Y.; Ault, Andrew P.

2015-01-01

Particles are frequently incorporated into clouds or precipitation, influencing climate by acting as cloud condensation or ice nuclei, taking up coatings during cloud processing, and removing species through wet deposition. Many of these particles, particularly ice nuclei, can remain suspended within cloud droplets/crystals as insoluble residues. While previous studies have measured the soluble or bulk mass of species within clouds and precipitation, no studies to date have determined the number concentration and size distribution of insoluble residues in precipitation or cloud water using in situ methods. Herein, for the first time we demonstrate that Nanoparticle Tracking Analysis (NTA) is a powerful in situ method for determining the total number concentration, number size distribution, and surface area distribution of insoluble residues in precipitation, both of rain and melted snow. The method uses 500 μL or less of liquid sample and does not require sample modification. Number concentrations for the insoluble residues in aqueous precipitation samples ranged from 2.0–3.0(±0.3)×108 particles cm−3, while surface area ranged from 1.8(±0.7)–3.2(±1.0)×107 μm2 cm−3. Number size distributions peaked between 133–150 nm, with both single and multi-modal character, while surface area distributions peaked between 173–270 nm. Comparison with electron microscopy of particles up to 10 μm show that, by number, > 97% residues are <1 μm in diameter, the upper limit of the NTA. The range of concentration and distribution properties indicates that insoluble residue properties vary with ambient aerosol concentrations, cloud microphysics, and meteorological dynamics. NTA has great potential for studying the role that insoluble residues play in critical atmospheric processes. PMID:25705069

Influence of deposition temperature on mechanical properties of plasma-sprayed hydroxyapatite coating on titanium alloy with ZrO2 intermediate layer

NASA Astrophysics Data System (ADS)

Chou, Bang-Yen; Chang, Edward

2003-06-01

Hydroxyapatite coatings were plasma sprayed on the Ti6A14V substrate with and without an intermediate ZrO2 layer; meanwhile the temperatures of substrates were varied at 90, 140, and 200 °C. The coatings were subjected to the standard adhesion test per ASTM C633-79. The purpose of the investigation was to study the effects of those processing variables on the bonding strength and failure behavior of the system. It is found that the bonding strengths of HA/ZrO2 and HA coatings generally decrease with increasing substrate temperature, except for the HA/ZrO2 coating deposited at 200 °C. The rationale of the results is attributed to the residual stress reported in the literature. Introducing ZrO2 bond coat is found to significantly promote the bonding strength of HA coating. The possible strengthening mechanism is the rougher surface of ZrO2 bond coat and the higher toughness of ZrO2, which provide the mechanical strengthening effects. The slightly denser HA in 200 °C deposited HA coating cannot explain the high bonding strength of the HA/ZrO2 coating, nor the mechanical strengthening effect of ZrO2 intermediate layer should apply. It is believed that a stronger diffusion bonding is formed at the interface of HA and ZrO2, which increases the bonding between them chemically. The bonding strengths of HA/ZrO2 and HA coatings are correlated with the area fraction of adhesive failure of the coatings. The correlation explains the findings in this study.

Laser-induced reaction alumina coating on ceramic composite

NASA Astrophysics Data System (ADS)

Xiao, Chenghe

Silicon carbide ceramics are susceptible to corrosion by certain industrial furnace environments. It is also true for a new class of silicon carbide-particulate reinforced alumina-matrix composite (SiCsb(P)Alsb2Osb3) since it contains more than 55% of SiC particulate within the composite. This behavior would limit the use of SiCsb(P)Alsb2Osb3 composites in ceramic heat exchangers. Because oxide ceramics corrode substantially less in the same environments, a laser-induced reaction alumina coating technique has been developed for improving corrosion resistance of the SiCsb(P)Alsb2Osb3 composite. Specimens with and without the laser-induced reaction alumina coating were subjected to corrosion testing at 1200sp°C in an air atmosphere containing Nasb2COsb3 for 50 ˜ 200 hours. Corroded specimens were characterized via x-ray diffraction (XRD), scanning electron microscopy (SEM), and energy dispersive spectrometer (EDS). The uncoated SiCsbP/Alsb2Osb3 composite samples experienced an initial increase in weight during the exposure to Nasb2COsb3 at 1200sp°C due to the oxidation of residual aluminum metal in the composite. There was no significant weight change difference experienced during exposure times between 50 and 200 hours. The oxidation layer formed on the as-received composite surface consisted of Si and Alsb2Osb3 (after washing with a HF solution). The oxidation layer grew outward and inward from the original surface of the composite. The growth rate in the outward direction was faster than in the inward direction. The formation of the Si/Alsb2Osb3 oxidation layer on the as-received composite was nonuniform, and localized corrosion was observed. The coated samples experienced very little mass increase. The laser-induced reaction alumina coating effectively provided protection for the SiCsbP/Alsb2Osb3 composite by keeping the corrodents from contacting the composite and by the formation of some refractory compounds such as Nasb2OAlsb2Osb3SiOsb2 and Nasb2Alsb{22}Osb

Investigation of hydrophobic substrates for solution residue analysis utilizing an ambient desorption liquid sampling-atmospheric pressure glow discharge microplasma.

PubMed

Paing, Htoo W; Marcus, R Kenneth

2018-03-12

A practical method for preparation of solution residue samples for analysis utilizing the ambient desorption liquid sampling-atmospheric pressure glow discharge optical emission spectroscopy (AD-LS-APGD-OES) microplasma is described. Initial efforts involving placement of solution aliquots in wells drilled into copper substrates, proved unsuccessful. A design-of-experiment (DOE) approach was carried out to determine influential factors during sample deposition including solution volume, solute concentration, number of droplets deposited, and the solution matrix. These various aspects are manifested in the mass of analyte deposited as well as the size/shape of the product residue. Statistical analysis demonstrated that only those initial attributes were significant factors towards the emission response of the analyte. Various approaches were investigated to better control the location/uniformity of the deposited sample. Three alternative substrates, a glass slide, a poly(tetrafluoro)ethylene (PTFE) sheet, and a polydimethylsiloxane (PDMS)-coated glass slide, were evaluated towards the microplasma analytical performance. Co-deposition with simple organic dyes provided an accurate means of determining the location of the analyte with only minor influence on emission responses. The PDMS-coated glass provided the best performance by virtue of its providing a uniform spatial distribution of the residue material. This uniformity yielded an improved limits of detection by approximately 22× for 20 μL and 4 x for 2 μL over the other two substrates. While they operate by fundamentally different processes, this choice of substrate is not restricted to the LS-APGD, but may also be applicable to other AD methods such as DESI, DART, or LIBS. Further developments will be directed towards a field-deployable ambient desorption OES source for quantitative analysis of microvolume solution residues of nuclear forensics importance.

Overlay coating degradation by simultaneous oxidation and coating/substrate interdiffusion. Ph.D. Thesis

NASA Technical Reports Server (NTRS)

Nesbitt, J. A.

1983-01-01

Degradation of NiCrAlZr overlay coatings on various NiCrAl substrates was examined after cyclic oxidation. Concentration/distance profiles were measured in the coating and substrate after various oxidation exposures at 1150 C. For each stubstrate, the Al content in the coating decreased rapidly. The concentration/distance profiles, and particularly that for Al, reflected the oxide spalling resistance of each coated substrate. A numerical model was developed to simulate diffusion associated with overlay-coating degradation by oxidation and coating/substrate interdiffusion. Input to the numerical model consisted of the Cr and Al content of the coating and substrate, ternary diffusivities, and various oxide spalling parameters. The model predicts the Cr and Al concentrations in the coating and substrate after any number of oxidation/thermal cycles. The numerical model also predicts coating failure based on the ability of the coating to supply sufficient Al to the oxide scale. The validity of the model was confirmed by comparison of the predicted and measured concentration/distance profiles. The model was subsequently used to identify the most critical system parameters affecting coating life.

Protective Coating

NASA Technical Reports Server (NTRS)

1984-01-01

Inorganic Coatings, Inc.'s K-Zinc 531 protective coating is water-based non-toxic, non-flammable and has no organic emissions. High ratio silicate formula bonds to steel, and in 30 minutes, creates a very hard ceramic finish with superior adhesion and abrasion resistance. Improved technology allows application over a minimal commercial sandblast, fast drying in high humidity conditions and compatibility with both solvent and water-based topcoats. Coating is easy to apply and provides long term protection with a single application. Zinc rich coating with water-based potassium silicate binder offers cost advantages in materials, labor hours per application, and fewer applications over a given time span.

Vacuum plasma spray coating

NASA Technical Reports Server (NTRS)

Holmes, Richard R.; Mckechnie, Timothy N.

1989-01-01

Currently, protective plasma spray coatings are applied to space shuttle main engine turbine blades of high-performance nickel alloys by an air plasma spray process. Originally, a ceramic coating of yttria-stabilized zirconia (ZrO2.12Y2O3) was applied for thermal protection, but was removed because of severe spalling. In vacuum plasma spray coating, plasma coatings of nickel-chromium-aluminum-yttrium (NiCrAlY) are applied in a reduced atmosphere of argon/helium. These enhanced coatings showed no spalling after 40 MSFC burner rig thermal shock cycles between 927 C (1700 F) and -253 C (-423 F), while current coatings spalled during 5 to 25 test cycles. Subsequently, a process was developed for applying a durable thermal barrier coating of ZrO2.8Y2O3 to the turbine blades of first-stage high-pressure fuel turbopumps utilizing the enhanced NiCrAlY bond-coating process. NiCrAlY bond coating is applied first, with ZrO2.8Y2O3 added sequentially in increasing amounts until a thermal barrier coating is obtained. The enchanced thermal barrier coating has successfully passed 40 burner rig thermal shock cycles.

Viscoelastic Thin Polymer Films under Transient Residual Stresses: Two-Stage Dewetting on Soft Substrates

NASA Astrophysics Data System (ADS)

Al Akhrass, S.; Reiter, G.; Hou, S. Y.; Yang, M. H.; Chang, Y. L.; Chang, F. C.; Wang, C. F.; Yang, A. C.-M.

2008-05-01

A nonmonotonic, two-stage dewetting behavior was observed for spin coated thin viscoelastic polymer films on soft elastic substrates. At times shorter than the relaxation time of the polymer (t<τrep), dewetting generated deep trenches in the soft rubbery substrate which, in turn, almost stopped dewetting. At later stages (t≫τrep), dewetting accelerated, accompanied by an unstable rim. However, holes nucleated at t<τrep showed only this second-stage behavior. Our observations are attributed to large elastic deformations in the substrate caused by transient residual stresses within the film.

Coating Life Prediction

NASA Technical Reports Server (NTRS)

Nesbitt, J. A.; Gedwill, M. A.

1984-01-01

Hot-section gas-turbine components typically require some form of coating for oxidation and corrosion protection. Efficient use of coatings requires reliable and accurate predictions of the protective life of the coating. Currently engine inspections and component replacements are often made on a conservative basis. As a result, there is a constant need to improve and develop the life-prediction capability of metallic coatings for use in various service environments. The purpose of this present work is aimed at developing of an improved methodology for predicting metallic coating lives in an oxidizing environment and in a corrosive environment.

Aircraft surface coatings

NASA Technical Reports Server (NTRS)

1982-01-01

Liquid, spray on elastomeric polyurethanes are selected and investigated as best candidates for aircraft external protective coatings. Flight tests are conducted to measure drag effects of these coatings compared to paints and a bare metal surface. The durability of two elastometric polyurethanes are assessed in airline flight service evaluations. Laboratory tests are performed to determine corrosion protection properties, compatibility with aircraft thermal anti-icing systems, the effect of coating thickness on erosion durability, and the erosion characteristics of composite leading edges-bare and coated. A cost and benefits assessment is made to determine the economic value of various coating configurations to the airlines.

Nanosecond multi-pulse laser milling for certain area removal of metal coating on plastics surface

NASA Astrophysics Data System (ADS)

Zhao, Kai; Jia, Zhenyuan; Ma, Jianwei; Liu, Wei; Wang, Ling

2014-12-01

Metal coating with functional pattern on engineering plastics surface plays an important role in industry applications; it can be obtained by adding or removing certain area of metal coating on engineering plastics surface. However, the manufacturing requirements are improved continuously and the plastic substrate presents three-dimensional (3D) structure-many of these parts cannot be fabricated by conventional processing methods, and a new manufacturing method is urgently needed. As the laser-processing technology has many advantages like high machining accuracy and constraints free substrate structure, the machining of the parts is studied through removing certain area of metal coating based on the nanosecond multi-pulse laser milling. To improve the edge quality of the functional pattern, generation mechanism and corresponding avoidance strategy of the processing defects are studied. Additionally, a prediction model for the laser ablation depth is proposed, which can effectively avoid the existence of residual metal coating and reduces the damage of substrate. With the optimal machining parameters, an equiangular spiral pattern on copper-clad polyimide (CCPI) is machined based on the laser milling at last. The experimental results indicate that the edge of the pattern is smooth and consistent, the substrate is flat and without damage. The achievements in this study could be applied in industrial production.

(Mn,Co)(3)O-4 Spinel Coatings on Ferritic Stainless Steels for SOFC Interconnect Applications

DOE Office of Scientific and Technical Information (OSTI.GOV)

Yang, Z Gary; Xia, Gordon; Li, Xiaohong S.

(Mn,Co)3O4 spinel with a nominal composition of Mn1.5Co1.5O4 demonstrates excellent electrical conductivity, satisfactory thermal and structural stability, as well as good thermal expansion match to ferritic stainless steel interconnects. A slurry-coating technique was developed for fabricating the spinel coatings onto the steel interconnects. Thermally grown layers of Mn1.5Co1.5O4 not only significantly decreased the contact resistance between a LSF cathode and stainless steel interconnect, but also acted as a mass barrier to inhibit scale growth on the stainless steel and to prevent Cr outward migration through the coating. The level of improvement in electrical performance and oxidation resistance (i.e. the scalemore » growth rate) was dependent on the ferritic substrate composition. For E-brite and Crofer22 APU, with a relatively high Cr concentration (27wt% and 23%, respectively) and negligible Si, the reduction of contact ASR and scale growth on the ferritic substrates was significant. In comparison, limited improvement was achieved by application of the Mn1.5Co1.5O4 spinel coating on AISI430, which contains only 17% Cr and a higher amount of residual Si.« less

Method of coating metal surfaces to form protective metal coating thereon

DOEpatents

Krikorian, Oscar H.; Curtis, Paul G.

1992-01-01

A process is disclosed for forming a protective metal coating on a metal surface using a flux consisting of an alkali metal fluoride, an alkaline earth metal fluoride, an alkali metal fluoaluminate, an alkali metal fluosilicate, and mixtures thereof. The flux, in particulate form, is mixed with particles of a metal coating material which may comprise aluminum, chromium, mixtures thereof, and alloys containing at least 50 wt. % aluminum and the particulate mixture is applied to the metal surface in a single step, followed by heating the coated metal surface to a temperature sufficient to cause the metal coating material to react with the metal surface to form a protective reaction product in the form of a metal coating bonded to the metal surface. The metal surface which reacts with the metal coating material to form the protective coating may comprise Fe, Co, Ni, Ti, V, Cr, Mn, Zr, Nb, Mo, Tc, Hf, Ta, W, Re and alloys thereof.

Method of coating metal surfaces to form protective metal coating thereon

DOEpatents

Krikorian, O.H.; Curtis, P.G.

1992-03-31

A process is disclosed for forming a protective metal coating on a metal surface using a flux consisting of an alkali metal fluoride, an alkaline earth metal fluoride, an alkali metal fluoaluminate, an alkali metal fluosilicate, and mixtures thereof. The flux, in particulate form, is mixed with particles of a metal coating material which may comprise aluminum, chromium, mixtures thereof, and alloys containing at least 50 wt. % aluminum and the particulate mixture is applied to the metal surface in a single step, followed by heating the coated metal surface to a temperature sufficient to cause the metal coating material to react with the metal surface to form a protective reaction product in the form of a metal coating bonded to the metal surface. The metal surface which reacts with the metal coating material to form the protective coating may comprise Fe, Co, Ni, Ti, V, Cr, Mn, Zr, Nb, Mo, Tc, Hf, Ta, W, Re and alloys thereof. 1 figure.

One-step fabrication of robust superhydrophobic and superoleophilic surfaces with self-cleaning and oil/water separation function.

PubMed

Zhang, Zhi-Hui; Wang, Hu-Jun; Liang, Yun-Hong; Li, Xiu-Juan; Ren, Lu-Quan; Cui, Zhen-Quan; Luo, Cheng

2018-03-01

Superhydrophobic surfaces have great potential for application in self-cleaning and oil/water separation. However, the large-scale practical applications of superhydrophobic coating surfaces are impeded by many factors, such as complicated fabrication processes, the use of fluorinated reagents and noxious organic solvents and poor mechanical stability. Herein, we describe the successful preparation of a fluorine-free multifunctional coating without noxious organic solvents that was brushed, dipped or sprayed onto glass slides and stainless-steel meshes as substrates. The obtained multifunctional superhydrophobic and superoleophilic surfaces (MSHOs) demonstrated self-cleaning abilities even when contaminated with or immersed in oil. The superhydrophobic surfaces were robust and maintained their water repellency after being scratched with a knife or abraded with sandpaper for 50 cycles. In addition, stainless-steel meshes sprayed with the coating quickly separated various oil/water mixtures with a high separation efficiency (>93%). Furthermore, the coated mesh maintained a high separation efficiency above 95% over 20 cycles of separation. This simple and effective strategy will inspire the large-scale fabrication of multifunctional surfaces for practical applications in self-cleaning and oil/water separation.

Development of an Heterologous Immunoassay for Ciprofloxacin Residue in Milk

NASA Astrophysics Data System (ADS)

Jinqing, Jiang; Haitang, Zhang; Zhixing, An; Zhiyong, Xu; Xuefeng, Yang; Huaguo, Huang; Ziliang, Wang

A heterologous immunoassay has been developed for the determination of Ciprofloxacin (CPFX) residues in milk. For this reason, carbodiimide active ester method was employed to synthesize the artificial antigen of CPFX-BSA, and mixed anhydride reaction was used to prepare the coating antigen of CPFX-OVA to pursue the heterologous sensitivity. Based on the square matrix titration, an icELISA method was developed for the quantitative detection of CPFX in cattle milk. The dynamic range was from 0.036 to 92.5 ng/mL, with LOD and IC50 value of 0.019 ng/mL and 1.8 ng/mL, respectively. Except for a high cross-reactivity (89.7%) to Enrofloxacin, negligible cross-reactivity to the other compounds was observed. After optimization, 0.03 mol/L of HCl, or 10% of methanol was used in the assay buffer. 20-fold dilution in cattle milk gave an inhibition curve almost the same as that in PBS buffer. The regression equation for this assay was y = 0.9036 x + 1.4574, with a correlation coefficient (R2) of 0.9844. The results suggest the veracity of the heterologous immunoassay for detecting CPFX residue in milk.

Partitioning Residue-derived and Residue-induced Emissions of N2O Using 15N-labelled Crop Residues

NASA Astrophysics Data System (ADS)

Farrell, R. E.; Carverhill, J.; Lemke, R.; Knight, J. D.

2014-12-01

Estimates of N2O emissions in Canada indicate that 17% of all agriculture-based emissions are associated with the decomposition of crop residues. However, research specific to the western Canadian prairies (including Saskatchewan) has shown that the N2O emission factor for N sources in this region typically ranges between 0.2 and 0.6%, which is well below the current IPCC default emission factor of 1.0%. Thus, it stands to reason that emissions from crop residues should also be lower than those calculated using the current IPCC emission factor. Current data indicates that residue decomposition, N mineralization and N2O production are affected by a number of factors such as C:N ratio and chemical composition of the residue, soil type, and soil water content; thus, a bench-scale incubation study was conducted to examine the effects of soil type and water content on N2O emissions associated with the decomposition of different crop residues. The study was carried out using soils from the Black, Dark Brown, Brown, and Gray soil zones and was conducted at both 50% and 70% water-filled pore space (WFPS); the soils were amended with 15N-labeled residues of wheat, pea, canola, and flax, or with an equivalent amount of 15N-labeled urea; 15N2O production was monitored using a Picarro G5101-i isotopic N2O analyzer. Crop residue additions to the soils resulted in both direct and indirect emissions of N2O, with residue derived emissions (RDE; measured as 15N2O) generally exceeding residue-induced emissions (RIE) at 50% WFPS—with RDEs ranging from 42% to 88% (mean = 58%) of the total N2O. Conversely, at 70% WFPS, RDEs were generally lower than RIEs—ranging from 21% to 83% (mean = 48%). Whereas both water content and soil type had an impact on N2O production, there was a clear and consistent trend in the emission factors for the residues; i.e., emissions were always greatest for the canola residue and lowest for the wheat residue and urea fertilizer; and intermediate for pea

Failure Mechanisms of the Coating/Metal Interface in Waterborne Coatings: The Effect of Bonding

PubMed Central

Wan, Hongxia; Song, Dongdong; Li, Xiaogang; Zhang, Dawei; Gao, Jin; Du, Cuiwei

2017-01-01

Waterborne coating is the most popular type of coating, and improving its performance is a key point of research. Cathodic delamination is one of the major modes of failure for organic coatings. It refers to the weakening or loss of adhesion between the coating and substrate. Physical and chemical characteristics of coatings have been studied via scanning electron microscopy (SEM), atomic force microscopy (AFM), contact angle measurements, Fourier transform infrared spectroscopy (FTIR), and secondary ion mass spectrometry (SIMS). Early heterogeneous swelling at the metal-coating interface in non-defective coated metals was elucidated using frequency-dependent alternating-current scanning electrochemical microscopy. Two types of coatings (styrene-acrylic coating and terpolymer coating) were compared. The effects of thickness, surface roughness, and chemical bonding on cathodic delamination were investigated. PMID:28772757

Antibacterial polymer coatings.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wilson, Mollye C.; Allen, Ashley N.; Barnhart, Meghan

2009-09-01

A series of poly(sulfone)s with quaternary ammonium groups and another series with aldehyde groups are synthesized and tested for biocidal activity against vegetative bacteria and spores, respectively. The polymers are sprayed onto substrates as coatings which are then exposed to aqueous suspensions of organisms. The coatings are inherently biocidal and do not release any agents into the environment. The coatings adhere well to both glass and CARC-coated coupons and they exhibit significant biotoxicity. The most effective quaternary ammonium polymers kills 99.9% of both gram negative and gram positive bacteria and the best aldehyde coating kills 81% of the spores onmore » its surface.« less

Thermal Barrier Coatings

NASA Technical Reports Server (NTRS)

1993-01-01

In order to reduce heat transfer between a hot gas heat source and a metallic engine component, a thermal insulating layer of material is placed between them. This thermal barrier coating is applied by plasma spray processing the thin films. The coating has been successfully employed in aerospace applications for many years. Lewis Research Center, a leader in the development engine components coating technology, has assisted Caterpillar, Inc. in applying ceramic thermal barrier coatings on engines. Because these large engines use heavy fuels containing vanadium, engine valve life is sharply decreased. The barrier coating controls temperatures, extends valve life and reduces operating cost. Additional applications are currently under development.

Stripping methods studies for HVOF WC-10Co-4Cr coating removal

NASA Astrophysics Data System (ADS)

Menini, Richard; Salah, Nihad Ben; Nciri, Rachid

2004-04-01

The use of high-velocity oxyfuel (HVOF) cermet coatings is considered to be a valuable and innovative alternative technology to replace Cr(VI) electroplating. Among others, a WC-10Co-4Cr coating is one of the best choices for landing gear components due to its excellent tribology and corrosion properties. The stripping process of such a cermet coating was studied due to its importance for the repair and overhaul of landing gear components. Stripping solutions fulfill the following criteria: keep substrate integrity; exhibit a high strip rate (SR); lead to uniform dissolution; show no galvanic corrosion; and be environmentally friendly. Three different high-strength steel substrates (4340, 300M, and Aermet100) were studied. Five different stripping solutions were selected for the electrochemical study. Only three met the targeted criteria: the meta-nitrobenzane sulfonate-sodium cyanide solution; the Rochelle salt; and a commercial nickel stripper. It was found that the process must be electrolytic, and that ultrasonic agitation is needed to enhance the overall mass transport and removal of WC particles and metallic matrix residues. When choosing the most efficient solution and conditions, the SR was found to be as high as 162 µm h-1, which is a very acceptable SR for productivity sake.

A missense mutation in melanocortin 1 receptor is associated with the red coat colour in donkeys.

PubMed

Abitbol, M; Legrand, R; Tiret, L

2014-12-01

The seven donkey breeds recognised by the French studbook are characterised by few coat colours: black, bay and grey. Normand bay donkeys seldom give birth to red foals, a colour more commonly seen and recognised in American miniature donkeys. Red resembles the equine chestnut colour, previously attributed to a mutation in the melanocortin 1 receptor gene (MC1R). We used a panel of 124 donkeys to identify a recessive missense c.629T>C variant in MC1R that showed a perfect association with the red coat colour. This variant leads to a methionine to threonine substitution at position 210 in the protein. We showed that methionine 210 is highly conserved among vertebrate melanocortin receptors. Previous in silico and in vitro analyses predicted this residue to lie within a functional site. Our in vivo results emphasised the pivotal role played by this residue, the alteration of which yielded a phenotype fully compatible with a loss of function of MC1R. We thus propose to name the c.629T>C allele in donkeys the e allele, which further enlarges the panel of recessive MC1R loss-of-function alleles described in animals and humans. © 2014 Stichting International Foundation for Animal Genetics.

Mixed zirconia calcium phosphate coatings for dental implants: tailoring coating stability and bioactivity potential.

PubMed

Pardun, Karoline; Treccani, Laura; Volkmann, Eike; Streckbein, Philipp; Heiss, Christian; Li Destri, Giovanni; Marletta, Giovanni; Rezwan, Kurosch

2015-03-01

Enhanced coating stability and adhesion are essential for long-term success of orthopedic and dental implants. In this study, the effect of coating composition on mechanical, physico-chemical and biological properties of coated zirconia specimens is investigated. Zirconia discs and dental screw implants are coated using the wet powder spraying (WPS) technique. The coatings are obtained by mixing yttria-stabilized zirconia (TZ) and hydroxyapatite (HA) in various ratios while a pure HA coating served as reference material. Scanning electron microscopy (SEM) and optical profilometer analysis confirm a similar coating morphology and roughness for all studied coatings, whereas the coating stability can be tailored with composition and is probed by insertion and dissections experiments in bovine bone with coated zirconia screw implants. An increasing content of calcium phosphate (CP) resulted in a decrease of mechanical and chemical stability, while the bioactivity increased in simulated body fluid (SBF). In vitro experiments with human osteoblast cells (HOB) revealed that the cells grew well on all samples but are affected by dissolution behavior of the studied coatings. This work demonstrates the overall good mechanical strength, the excellent interfacial bonding and the bioactivity potential of coatings with higher TZ contents, which provide a highly interesting coating for dental implants. Copyright © 2014 Elsevier B.V. All rights reserved.

Rapid Detection of Chloramphenicol Residues in Aquatic Products Using Colloidal Gold Immunochromatographic Assay

PubMed Central

Zhou, Chennan; Zhang, Xueyin; Huang, Xinxin; Guo, Xishan; Cai, Qiang; Zhu, Songming

2014-01-01

A colloidal gold immunochromatographic assay (GICA) was developed for rapid detection of chloramphenicol (CAP) residues in aquatic products. A nitrocellulose (NC) membrane was used as the carrier, and the polyclonal CAP antibody was used as the marker protein. The average diameter of as-prepared colloidal gold nanoparticles (AuNPs) was about 20 nm. The optimal pH value of colloidal gold solutions and the amount of the antibody of CAP were 8.0 and 7.2 μg/mL, respectively. The CAP antibody was immobilized onto the conjugate pad after purification. The CAP conjugate and goat anti-rabbit IgG (secondary antibody) were coated onto the NC membrane. Next, the non-specific sites were blocked with 1% bovine serum albumin. The minimum detectable concentration of CAP in standard solution is 0.5 ng/mL, with good reproducibility. For the real samples from crucian carps injected with a single-dose of CAP in the dorsal muscles, the minimum detectable concentration of CAP residues was 0.5 μg/kg. The chromatographic analysis time was less than 10 min, and the strip had a long storage lifetime of more than 90 days at different temperatures. The strips provide a means for rapid detection of CAP residues in aquatic products. PMID:25412221

Lubricant Coating Process

NASA Technical Reports Server (NTRS)

1989-01-01

"Peen Plating," a NASA developed process for applying molybdenum disulfide, is the key element of Techniblast Co.'s SURFGUARD process for applying high strength solid lubricants. The process requires two machines -- one for cleaning and one for coating. The cleaning step allows the coating to be bonded directly to the substrate to provide a better "anchor." The coating machine applies a half a micron thick coating. Then, a blast gun, using various pressures to vary peening intensities for different applications, fires high velocity "media" -- peening hammers -- ranging from plastic pellets to steel shot. Techniblast was assisted by Rural Enterprises, Inc. Coating service can be performed at either Techniblast's or a customer's facility.

Isomolybdate conversion coatings

NASA Technical Reports Server (NTRS)

Minevski, Zoran (Inventor); Maxey, Jason (Inventor); Nelson, Carl (Inventor); Eylem, Cahit (Inventor)

2002-01-01

A conversion coating solution and process forms a stable and corrosion-resistant layer on metal substrates or layers or, more preferably, on a boehmite layer or other base conversion coating. The conversion coating process involves contacting the substrate, layer or coating with an aqueous alkali metal isomolybdate solution in order to convert the surface of the substrate, layer or coating to a stable conversion coating. The aqueous alkali metal molybdates are selected from sodium molybdate (Na.sub.2 MoO.sub.4), lithium molybdate (Li.sub.2 MoO.sub.4), potassium molybdate (K.sub.2 MoO.sub.4), or combinations thereof, with the most preferred alkali metal molybdate being sodium molybdate. The concentration of alkali metal molybdates in the solution is preferably less than 5% by weight. In addition to the alkali metal molybdates, the conversion coating solution may include alkaline metal passivators selected from lithium nitrate (LiNO.sub.3), sodium nitrate (NaNO.sub.3), ammonia nitrate (NH.sub.4 NO.sub.3), and combinations thereof; lithium chloride, potassium hexafluorozirconate (K.sub.2 ZrF.sub.6) or potassium hexafluorotitanate (K.sub.2 TiF.sub.6).

Interaction of flavonols with human serum albumin: a biophysical study showing structure-activity relationship and enhancement when coated on silver nanoparticles.

PubMed

Das, Pratyusa; Chaudhari, Sunil Kumar; Das, Asmita; Kundu, Somashree; Saha, Chabita

2018-04-24

Binding affinities of flavonols namely quercetin, myricetin, and kaempferol to human serum albumin (HSA) were determined fluorimetrically and the order was observed to be myricetin > quercetin > kaempferol demonstrating structure-activity relationship. Quercetin-coated silver nanoparticles (AgNPs) show higher binding affinity to HSA compared to free quercetin with binding constants 6.04 × 10 7  M -1 and 4.2 × 10 6  M -1 , respectively. Using site-specific markers it is concluded that free quercetin and that coated on AgNPs bind at different sites. Significant structural changes in circular dichroism (CD) spectra of HSA were recorded with quercetin-coated AgNPs compared to free quercetin. These results were further substantiated by time-resolved fluorescence spectroscopy where fluorescence life time of the tryptophan residue in HSA-quercetin-coated AgNPs complex decreased to 3.63 ns from 4.22 ns in HSA-quercetin complex. Isothermal calorimetric studies reveal two binding modes for quercetin-coated AgNPs and also higher binding constants compared to free quercetin. These higher binding affinities are attributed to altered properties of quercetin when coated on AgNPs enabling it to reach the binding sites other than site II where free quercetin mainly binds.

Utilizing polymer-coated vials to illustrate the fugacity and bioavailability of chlorinated pesticide residues in contaminated soils

USDA-ARS?s Scientific Manuscript database

Fugacity and bioavailability concepts can be challenging topics to communicate effectively in the timeframe of an academic laboratory course setting. In this experiment, students observe partitioning of the residues over time into an artificial biological matrix. The three compounds utilized are o...

Quantitative image analysis for evaluating the coating thickness and pore distribution in coated small particles.

PubMed

Laksmana, F L; Van Vliet, L J; Hartman Kok, P J A; Vromans, H; Frijlink, H W; Van der Voort Maarschalk, K

2009-04-01

This study aims to develop a characterization method for coating structure based on image analysis, which is particularly promising for the rational design of coated particles in the pharmaceutical industry. The method applies the MATLAB image processing toolbox to images of coated particles taken with Confocal Laser Scanning Microscopy (CSLM). The coating thicknesses have been determined along the particle perimeter, from which a statistical analysis could be performed to obtain relevant thickness properties, e.g. the minimum coating thickness and the span of the thickness distribution. The characterization of the pore structure involved a proper segmentation of pores from the coating and a granulometry operation. The presented method facilitates the quantification of porosity, thickness and pore size distribution of a coating. These parameters are considered the important coating properties, which are critical to coating functionality. Additionally, the effect of the coating process variations on coating quality can straight-forwardly be assessed. Enabling a good characterization of the coating qualities, the presented method can be used as a fast and effective tool to predict coating functionality. This approach also enables the influence of different process conditions on coating properties to be effectively monitored, which latterly leads to process tailoring.

Convergent Evolution of Slick Coat in Cattle through Truncation Mutations in the Prolactin Receptor.

PubMed

Porto-Neto, Laercio R; Bickhart, Derek M; Landaeta-Hernandez, Antonio J; Utsunomiya, Yuri T; Pagan, Melvin; Jimenez, Esbal; Hansen, Peter J; Dikmen, Serdal; Schroeder, Steven G; Kim, Eui-Soo; Sun, Jiajie; Crespo, Edward; Amati, Norman; Cole, John B; Null, Daniel J; Garcia, Jose F; Reverter, Antonio; Barendse, William; Sonstegard, Tad S

2018-01-01

Evolutionary adaptations are occasionally convergent solutions to the same problem. A mutation contributing to a heat tolerance adaptation in Senepol cattle, a New World breed of mostly European descent, results in the distinct phenotype known as slick, where an animal has shorter hair and lower follicle density across its coat than wild type animals. The causal variant, located in the 11 th exon of prolactin receptor , produces a frameshift that results in a truncated protein. However, this mutation does not explain all cases of slick coats found in criollo breeds. Here, we obtained genome sequences from slick cattle of a geographically distinct criollo breed, namely Limonero, whose ancestors were originally brought to the Americas by the Spanish. These data were used to identify new causal alleles in the 11 th exon of the prolactin receptor , two of which also encode shortened proteins that remove a highly conserved tyrosine residue. These new mutations explained almost 90% of investigated cases of animals that had slick coats, but which also did not carry the Senepol slick allele. These results demonstrate convergent evolution at the molecular level in a trait important to the adaptation of an animal to its environment.

Convergent Evolution of Slick Coat in Cattle through Truncation Mutations in the Prolactin Receptor

PubMed Central

Porto-Neto, Laercio R.; Bickhart, Derek M.; Landaeta-Hernandez, Antonio J.; Utsunomiya, Yuri T.; Pagan, Melvin; Jimenez, Esbal; Hansen, Peter J.; Dikmen, Serdal; Schroeder, Steven G.; Kim, Eui-Soo; Sun, Jiajie; Crespo, Edward; Amati, Norman; Cole, John B.; Null, Daniel J.; Garcia, Jose F.; Reverter, Antonio; Barendse, William; Sonstegard, Tad S.

2018-01-01

Evolutionary adaptations are occasionally convergent solutions to the same problem. A mutation contributing to a heat tolerance adaptation in Senepol cattle, a New World breed of mostly European descent, results in the distinct phenotype known as slick, where an animal has shorter hair and lower follicle density across its coat than wild type animals. The causal variant, located in the 11th exon of prolactin receptor, produces a frameshift that results in a truncated protein. However, this mutation does not explain all cases of slick coats found in criollo breeds. Here, we obtained genome sequences from slick cattle of a geographically distinct criollo breed, namely Limonero, whose ancestors were originally brought to the Americas by the Spanish. These data were used to identify new causal alleles in the 11th exon of the prolactin receptor, two of which also encode shortened proteins that remove a highly conserved tyrosine residue. These new mutations explained almost 90% of investigated cases of animals that had slick coats, but which also did not carry the Senepol slick allele. These results demonstrate convergent evolution at the molecular level in a trait important to the adaptation of an animal to its environment. PMID:29527221

In-situ phosphatizing coatings for aerospace, OEM and coil coating applications

NASA Astrophysics Data System (ADS)

Neuder, Heather Aurelia

The current metal coating process is a multi-step process. The surface is cleaned, primered, dried and then painted. The process is labor intensive and time consuming. The wash primer is a conversion coating, which prepares metal surface for better paint adhesion. The wash primers currently used often contain hexavalent chromium (Cr6+), which seals the pores in the conversion coating. The presence of hexavalent chromium, a known carcinogen, and volatile organic compounds (VOCs) make waste disposal expensive and pose dangers to workers. The novel technique of in-situ phosphatizing coating (ISPC) is a single-step, chrome-free alternative to the present coating practice. Formulation of an ISPC involves predispersal of an in-situ phosphatizing reagent (ISPR) into the paint system to form a stable formulation. The ISPR reacts with the metal surface and bonds with the paint film simultaneously, which eliminates the need for a conversion coating. In acid catalyzed paint systems, such as polyester-melamine paints, the ISPR also catalyzes cross-linking reactions between the melamine and the polyester polyols. ISPCs are formulated using commercially available coating systems including: polyester-melamine, two-component epoxy, polyurethane and high-hydroxy content polyester-melamine coil coating. The ISPCs are applied to metal substrates and their performances are evaluated using electrochemical, thermal and standard American Society for Testing and Materials (ASTM) testing methods. In addition, ISPCs were designed and formulated based on: (1) phosphate chemistry, (2) polymer chemistry, (3) sol-gel chemistry, and (4) the ion-exchange principle. Organo-functionalized silanes, which serve as excellent coupling and dispersion agents, are incorporated into the optimized ISPC formula and evaluated using standard ASTM testing methods and electrochemical spectroscopy. Also, an ion-exchange pigment, which leads to better adhesion by forming a mixed metal silicate surface, is

Dense protective coatings, methods for their preparation and coated articles

DOE Office of Scientific and Technical Information (OSTI.GOV)

Tulyani, Sonia; Bhatia, Tania; Smeggil, John G.

A method for depositing a protective coating on a complex shaped substrate includes the steps of: (1) dipping a complex shaped substrate into a slurry to form a base coat thereon, the slurry comprising an aqueous solution, at least one refractory metal oxide, and at least one transient fluid additive present in an amount of about 0.1 percent to 10 percent by weight of the slurry; (2) curing the dipped substrate; (3) dipping the substrate into a precursor solution to form a top barrier coat thereon; and (4) heat treating the dipped, cured substrate to form a protective coating.

Kinetics of interaction of Cotton Leaf Curl Kokhran Virus-Dabawali (CLCuKV-Dab) coat protein and its mutants with ssDNA

DOE Office of Scientific and Technical Information (OSTI.GOV)

Priyadarshini, C.G. Poornima; Savithri, H.S., E-mail: bchss@biochem.iisc.ernet.i

Gemini viral assembly and transport of viral DNA into nucleus for replication, essentially involve DNA-coat protein interactions. The kinetics of interaction of Cotton Leaf Curl Kokhran Virus-Dabawali recombinant coat protein (rCP) with DNA was studied by electrophoretic mobility shift assay (EMSA) and surface plasmon resonance (SPR). The rCP interacted with ssDNA with a K{sub A}, of 2.6 +- 0.29 x 10{sup 8} M{sup -1} in a sequence non-specific manner. The CP has a conserved C2H2 type zinc finger motif composed of residues C68, C72, H81 and H85. Mutation of these residues to alanine resulted in reduced binding to DNA probes.more » The H85A mutant rCP showed the least binding with approximately 756 fold loss in the association rate and a three order magnitude decrease in the binding affinity as compared to rCP. The CP-DNA interactions via the zinc finger motif could play a crucial role in virus assembly and in nuclear transport.« less

Residual Stress Distribution and Microstructure of a Multiple Laser-Peened Near-Alpha Titanium Alloy

NASA Astrophysics Data System (ADS)

Umapathi, A.; Swaroop, S.

2018-04-01

Laser peening without coating (LPwC) was performed on a Ti-2.5 Cu alloy with multiple passes (1, 3 and 5), using a Nd:YAG laser (1064 nm) at a constant overlap rate of 70% and power density of 6.7 GW cm-2. Hardness and residual stress profiles indicated thermal softening near the surface (< 100 μm) and bulk softening due to adiabatic heating. Maximum hardness (235 HV at 500 μm) and maximum residual stress (- 890 MPa at 100 μm) were observed for LPwC with 1 pass. Surface roughness and surface 3-D topography imaging showed that the surface roughness increased with the increase in the number of passes. XRD results indicated no significant β phases. However, peak shifts, broadening and asymmetry were observed and interpreted based on dislocation activity. Microstructures indicated no melting or resolidification or refinement of grains at the surface. Twin density was found to increase with the increase in the number of passes.

Residual Stress Distribution and Microstructure of a Multiple Laser-Peened Near-Alpha Titanium Alloy

NASA Astrophysics Data System (ADS)

Umapathi, A.; Swaroop, S.

2018-05-01

Laser peening without coating (LPwC) was performed on a Ti-2.5 Cu alloy with multiple passes (1, 3 and 5), using a Nd:YAG laser (1064 nm) at a constant overlap rate of 70% and power density of 6.7 GW cm-2. Hardness and residual stress profiles indicated thermal softening near the surface (< 100 μm) and bulk softening due to adiabatic heating. Maximum hardness (235 HV at 500 μm) and maximum residual stress (- 890 MPa at 100 μm) were observed for LPwC with 1 pass. Surface roughness and surface 3-D topography imaging showed that the surface roughness increased with the increase in the number of passes. XRD results indicated no significant β phases. However, peak shifts, broadening and asymmetry were observed and interpreted based on dislocation activity. Microstructures indicated no melting or resolidification or refinement of grains at the surface. Twin density was found to increase with the increase in the number of passes.

Versatile Coating

NASA Technical Reports Server (NTRS)

1990-01-01

A radome at Logan Airport and a large parabolic antenna at the Wang Building in Massachusetts are protected from weather, corrosion and ultraviolet radiation by a coating, specially designed for antennas and radomes, known as CRC Weathertite 6000. The CRC 6000 line that emerged from Boyd Coatings Research Co., Inc. is a solid dispersion of fluorocarbon polymer and polyurethane that yields a tough, durable film with superior ultraviolet resistance and the ability to repel water and ice over a long term. Additionally, it provides resistance to corrosion, abrasion, chemical attacks and impacts. Material can be used on a variety of substrates, such as fiberglass, wood, plastic and concrete in addition to steel and aluminum. In addition Boyd Coatings sees CRC 6000 applicability as an anti-icing system coated on the leading edge of aircraft wings.

Coatings for Graphite Fibers

NASA Technical Reports Server (NTRS)

Galasso, F. S.; Scola, D. A.; Veltri, R. D.

1980-01-01

Several approaches for applying high resistance coatings continuously to graphite yarn were investigated. Two of the most promising approaches involved (1) chemically vapor depositing (CVD) SiC coatings on the surface of the fiber followed by oxidation, and (2) drawing the graphite yarn through an organo-silicone solution followed by heat treatments. In both methods, coated fibers were obtained which exhibited increased electrical resistances over untreated fibers and which were not degraded. This work was conducted in a previous program. In this program, the continuous CVD SiC coating process used on HTS fiber was extended to the coating of HMS, Celion 6000, Celion 12000 and T-300 graphite fiber. Electrical resistances three order of magnitude greater than the uncoated fiber were measured with no significant degradation of the fiber strength. Graphite fibers coated with CVD Si3N4 and BN had resistances greater than 10(exp 6) ohm/cm. Lower pyrolysis temperatures were used in preparing the silica-like coatings also resulting in resistances as high as three orders of magnitude higher than the uncoated fiber. The epoxy matrix composites prepared using these coated fibers had low shear strengths indicating that the coatings were weak.

Ningnanmycin inhibits tobacco mosaic virus virulence by binding directly to its coat protein discs

PubMed Central

Li, Xiangyang; Hao, Gefei; Wang, Qingmin; Chen, Zhuo; Ding, Yan; Yu, Lu; Hu, Deyu; Song, Baoan

2017-01-01

Tobacco mosaic virus (TMV) causes severe plant diseases worldwide; however, effective antiviral agents for controlling TMV infections are not available. This lack of effective antiviral agents is mainly due to the poor understanding of potential targets associated with TMV infections. During infection, the coat protein (CP), which is delivered by viral particles into susceptible host cells, provides protection for viral RNA. Here, we found that Ningnanmycin (NNM), a commercially used plant antibacterial agent, inhibits the assembly of the CP by directly binding several residues. These interactions cause the disassembly of the CP from discs into monomers, leading to an almost complete loss of pathogenicity. Substitutions in the involved binding residues resulted in mutants that were significantly less sensitive to NNM. Thus, targeting the binding of viral CPs through small molecular agents offers an effective strategy to study the mechanism of NNM. PMID:29137277

Preventing Cracking of Anodized Coatings

NASA Technical Reports Server (NTRS)

He, Charles C.; Heslin, Thomas M.

1995-01-01

Anodized coatings have been used as optical and thermal surfaces in spacecraft. Particulate contamination from cracked coatings is a concern for many applications. The major cause for the cracking is the difference in the coefficient of thermal expansion between the oxide coatings and the aluminum substrate. The loss of water when the coating is exposed to a vacuum also could induce cracking of the coating. Hot-water sealing was identified as the major cause for the cracking of the coatings because of the large temperature change when the parts were immersed in boiling water and the water was absorbed in the coating. when the hot-water sealing process was eliminated, the cracking resistance of the anodized coatings was greatly improved. Also, it was found that dyed black coatings were more susceptible than clear coatings to cracking during thermo-vacuum cyclings.

Analytical investigations of poly(acrylic acid) coatings electrodeposited on titanium-based implants: a versatile approach to biocompatibility enhancement.

PubMed

De Giglio, E; Cometa, S; Cioffi, N; Torsi, L; Sabbatini, L

2007-12-01

A polyacrylic acid film was synthesized on titanium substrates from aqueous solutions via an electroreductive process for the first time. This work was done in order to develop a versatile coating for titanium-based orthopaedic implants that acts as both an effective bioactive surface and an effective anti-corrosion barrier. The chemical structure of the PAA coating was investigated by X-ray photoelectron spectroscopy (XPS). Scanning electron microscopy (SEM) was employed to evaluate the effect of annealing treatment on the morphology of the coatings in terms of their uniformity and porosity. Inductively coupled plasma mass spectrometry was used to measure ion concentrations in ion release tests performed on Ti-6Al-4V sheets modified with PAA coatings (annealed and unannealed). Results indicate that the annealing process produces coatings that possess considerable anti-corrosion performance. Moreover, the availability and the reactivity of the surface carboxylic groups were exploited in order to graft biological molecules onto the PAA-modified titanium implants. The feasibility of the grafting reaction was tested using a single aminoacid residue. A fluorinated aminoacid was selected, and the grafting reaction was monitored both by XPS, using fluorine as a marker element, and via quartz crystal microbalance (QCM) measurements. The success of the grafting reaction opens the door to the synthesis of a wide variety of PAA-based coatings that are functionalized with selected bioactive molecules and promote positive reactions with the biological system interfacing the implant while considerably reducing ion release into surrounding tissues.

Effects of post-heat treatment on microstructure and properties of laser cladded composite coatings on titanium alloy substrate

NASA Astrophysics Data System (ADS)

Li, G. J.; Li, J.; Luo, X.

2015-01-01

The composite coatings were produced on the Ti6Al4V alloy substrate by laser cladding. Subsequently, the coatings were heated at 500 °C for 1 h and 2 h and then cooled in air. Effects of post-heat treatment on microstructure, microhardness and fracture toughness of the coatings were investigated by scanning electron microscopy (SEM), X-ray diffraction (XRD), energy dispersive spectroscopy (EDS), optical microscopy (OM). Wear resistance of the coatings was evaluated under the dry sliding reciprocating friction condition at room temperature. The results indicated that the coatings mainly consist of a certain amount of coarse white equiaxed WC particles surrounded by the white-bright W2C, a great deal of fine dark spherical TiC particles and the matrix composed of the α(Ti), Ti2Ni and TiNi phases. Effects of the post-heat treatment on phase constituents and microstructure of the coatings were almost negligible due to the low temperature. However, the post-heat treatment could decrease the residual stress and increase fracture toughness of the coatings, and fracture toughness of the coatings was improved from 2.77 MPa m1/2 to 3.80 MPa m1/2 and 4.43 MPa m1/2 with the heat treatment for 1 h and 2 h, respectively. The mutual role would contribute to the reduction in cracking susceptibility. Accompanied with the increase in fracture toughness, microhardness of the coatings was reduced slightly. The dominant wear mechanism for all the coatings was abrasive wear, characterized by micro-cutting or micro-plowing. The heat treatment could significantly decrease the average friction coefficient and reduce the fluctuation of the friction coefficient with the change in sliding time. The appropriate heat treatment time (approximately 1 h) had a minimal effect on wear mass loss and volume loss. Moreover, the improvement in fracture toughness will also be beneficial to wear resistance of the coatings under the long service.

Silicates Eroded under Simulated Martian Conditions Effectively Kill Bacteria—A Challenge for Life on Mars

PubMed Central

Bak, Ebbe N.; Larsen, Michael G.; Moeller, Ralf; Nissen, Silas B.; Jensen, Lasse R.; Nørnberg, Per; Jensen, Svend J. K.; Finster, Kai

2017-01-01

The habitability of Mars is determined by the physical and chemical environment. The effect of low water availability, temperature, low atmospheric pressure and strong UV radiation has been extensively studied in relation to the survival of microorganisms. In addition to these stress factors, it was recently found that silicates exposed to simulated saltation in a Mars-like atmosphere can lead to a production of reactive oxygen species. Here, we have investigated the stress effect induced by quartz and basalt abraded in Mars-like atmospheres by examining the survivability of the three microbial model organisms Pseudomonas putida, Bacillus subtilis, and Deinococcus radiodurans upon exposure to the abraded silicates. We found that abraded basalt that had not been in contact with oxygen after abrasion killed more than 99% of the vegetative cells while endospores were largely unaffected. Exposure of the basalt samples to oxygen after abrasion led to a significant reduction in the stress effect. Abraded quartz was generally less toxic than abraded basalt. We suggest that the stress effect of abraded silicates may be caused by a production of reactive oxygen species and enhanced by transition metal ions in the basalt leading to hydroxyl radicals through Fenton-like reactions. The low survivability of the usually highly resistant D. radiodurans indicates that the effect of abraded silicates, as is ubiquitous on the Martian surface, would limit the habitability of Mars as well as the risk of forward contamination. Furthermore, the reactivity of abraded silicates could have implications for future manned missions, although the lower effect of abraded silicates exposed to oxygen suggests that the effects would be reduced in human habitats. PMID:28955310

Silicates Eroded under Simulated Martian Conditions Effectively Kill Bacteria-A Challenge for Life on Mars.

PubMed

Bak, Ebbe N; Larsen, Michael G; Moeller, Ralf; Nissen, Silas B; Jensen, Lasse R; Nørnberg, Per; Jensen, Svend J K; Finster, Kai

2017-01-01

The habitability of Mars is determined by the physical and chemical environment. The effect of low water availability, temperature, low atmospheric pressure and strong UV radiation has been extensively studied in relation to the survival of microorganisms. In addition to these stress factors, it was recently found that silicates exposed to simulated saltation in a Mars-like atmosphere can lead to a production of reactive oxygen species. Here, we have investigated the stress effect induced by quartz and basalt abraded in Mars-like atmospheres by examining the survivability of the three microbial model organisms Pseudomonas putida, Bacillus subtilis , and Deinococcus radiodurans upon exposure to the abraded silicates. We found that abraded basalt that had not been in contact with oxygen after abrasion killed more than 99% of the vegetative cells while endospores were largely unaffected. Exposure of the basalt samples to oxygen after abrasion led to a significant reduction in the stress effect. Abraded quartz was generally less toxic than abraded basalt. We suggest that the stress effect of abraded silicates may be caused by a production of reactive oxygen species and enhanced by transition metal ions in the basalt leading to hydroxyl radicals through Fenton-like reactions. The low survivability of the usually highly resistant D. radiodurans indicates that the effect of abraded silicates, as is ubiquitous on the Martian surface, would limit the habitability of Mars as well as the risk of forward contamination. Furthermore, the reactivity of abraded silicates could have implications for future manned missions, although the lower effect of abraded silicates exposed to oxygen suggests that the effects would be reduced in human habitats.

Aircraft surface coatings

NASA Technical Reports Server (NTRS)

1983-01-01

A series of studies in which films and liquid spray-on materials were evaluated in the laboratory for transport aircraft external surface coatings are summarized. Elastomeric polyurethanes were found to best meet requirements. Two commercially available products, CAAPCO B-274 and Chemglaze M313, were subjected to further laboratory testing, airline service evaluations, and drag-measurement flight tests. It was found that these coatings were compatible with the severe operating environment of airlines and that coatings reduced airplane drag. An economic analysis indicated significant dollar benefits to airlines from application of the coatings.

SERS strategy based on the modified Au nanoparticles for highly sensitive detection of bisphenol A residues in milk.

PubMed

Yang, Libin; Chen, Yongliang; Shen, Yu; Yang, Ming; Li, Xiuling; Han, Xiaoxia; Jiang, Xin; Zhao, Bing

2018-03-01

Bisphenol A (BPA) is a highly toxic chemical, and its residue in milk product is threatening people's health due to its possible leaching from the packagings and cans with BPA coating. In this work, halides modified Au nanoparticles (NPs) as the modification substrates were first designed for rapid and sensitive determination of BPA residue in real milk by SERS method with the assistance of aggregation agents (Zn 2+ ). It can be concluded that Au NPs modification substrate with assistance of the aggregation agent can remarkably improve the detection sensitivity of BPA residue, which can significantly enhance the SERS signal of BPA and achieve the trace-level detection of BPA residue. Under the optimal conditions, the limit of detection of BPA residue can be as low as to 4.3 × 10 -9 mol/L (equal to 0.98 × 10 -3 mg/kg), which is much less than the standard of European Union (0.6mg/kg). And, there is a good linear relationship (R 2 = 0.990) between the intensity of SERS signal and the logarithm of BPA concentration in the range of 1.0 × 10 -8 -1.0 × 10 -3 mol/L. By this method, the recovery of BPA residue ranges from 89.5% to 100.2% with relative standard deviation between 4.6% and 2.7%. The proposed SERS method proves to be reliable, highly sensitive and possesses good reproducibility, which is very promising for sensitive detection of bisphenols residue in foodstuff. Copyright © 2017 Elsevier B.V. All rights reserved.

A deletion mutation at the ep locus causes low seed coat peroxidase activity in soybean.

PubMed

Gijzen, M

1997-11-01

The Ep locus severely affects the amount of peroxidase enzyme in soybean seed coats. Plants containing the dominant Ep allele accumulate large amounts of peroxidase in the hourglass cells of the sub-epidermis. Homozygous recessive epep genotypes do not accumulate peroxidase in the hourglass cells and are much reduced in total seed coat peroxidase activity. To isolate the gene encoding the seed coat peroxidase and to determine whether it corresponds to the Ep locus, a cDNA library was constructed from developing seed coats and an abundant 1.3 kb peroxidase transcript was cloned. The corresponding structural gene was also isolated from a genomic library. Sequence analysis shows that the seed coat peroxidase is translated as a 352 amino acid precursor protein of 38 kDa. Processing of a putative 26 amino acid signal sequence results in a mature protein of 326 residues with a calculated mass of 35 kDa and a pl of 4.4. Using probes derived from the cDNA, genomic DNA blot hybridization and polymerase chain reaction analysis detected polymorphisms that distinguished EpEp and epep genotypes. Co-segregation of the polymorphisms in an F2 population from a cross of EpEp and epep plants shows that the Ep locus encodes the seed coat peroxidase protein. Comparison of Ep and ep alleles indicates that the recessive gene lacks 87 bp of sequence encompassing the translation start codon. Analysis by RNA blot hybridization shows that epep plants have drastically reduced amounts of peroxidase transcript compared with EpEp plants. The peroxidase mRNA is abundant in seed coat tissues of EpEp plants during the late stages of seed maturation, and could also be detected in root tissues, but not in the flower, embryo, pod or leaf. The results indicate that the lack of peroxidase accumulation in seed coats of homozygous recessive epep plants is due to a mutation of the structural gene that reduces transcript abundance.

Method for coating ultrafine particles, system for coating ultrafine particles

DOE Office of Scientific and Technical Information (OSTI.GOV)

Li, Jie; Liu, Yung

The invention provides a method for dispersing particles within a reaction field, the method comprising confining the particles to the reaction field using a standing wave. The invention also provides a system for coating particles, the system comprising a reaction zone; a means for producing fluidized particles within the reaction zone; a fluid to produce a standing wave within the reaction zone; and a means for introducing coating moieties to the reaction zone. The invention also provides a method for coating particles, the method comprising fluidizing the particles, subjecting the particles to a standing wave; and contacting the subjected particlesmore » with a coating moiety.« less

Coatings on Atacama Desert Basalt: A Possible Analog for Coatings on Gusev Plains Basalt

NASA Technical Reports Server (NTRS)

Sutter, B.; Golden, D. C.; Amundson, R.; Chong-Diaz, G.; Ming, D. W.

2007-01-01

Surface coatings on Gusev Plains basalt have been observed and may contain hematite and nanophase Fe-oxides along with enrichments in P, S, Cl, and K relative to the underlying rock. The Gusev coatings may be derived from the dissolution of adhering soil and/or parent rock along with the addition of S and Cl from outside sources. Transient water for dissolution could be sourced from melting snow during periods of high obliquity, acid fog, and/or ground water (Haskin et al., 2005). Coatings on basalt in the hyper-arid (less than 2mm y(sup -1)) Atacama Desert may assist in understanding the chemistry, mineralogy and formation mechanisms of the Gusev basalt coatings. The Atacama Desert climate is proposed to be analogous to a paleo-Mars climate that was characterized by limited aqueous activity when the Gusev coatings could have formed. The objectives of this work are to (i) determine the chemical nature and extent of surface coatings on Atacama Desert basalt, and (ii) assess coating formation mechanisms in the Atacama Desert. Preliminary backscattered electron imaging of Atacama basalt thin-sections indicated that the coatings are as thick as 20 m. The boundary between the coating and the basalt labradorite, ilmenite, and augite grains was abrupt indicating that the basalt minerals underwent no chemical dissolution. The Atacama coatings have been added to the basalt instead of being derived from basalt chemical weathering. Semi-quantitative energy dispersive spectroscopy shows the coatings to be chemically homogeneous. The coating is depleted in Ca (0.9 wt% CaO) and enriched in K (1.3 wt.% K2O) and Si (69.1 wt.% SiO2) relative to the augite and labradorite grains. A dust source enriched in Si (e.g., poorly crystalline silica) and K and depleted in Ca appears to have been added to the basalt surface. Unlike the Gusev coatings, no P, S, and Cl enrichment was observed. However, Fe (3.2 wt.% FeO) was present in the Atacama coatings suggesting the present of Fe

Influence of Deposition Conditions on Fatigue Properties of Martensitic Stainless Steel with Tin Film Coated by Arc Ion Plating Method

NASA Astrophysics Data System (ADS)

Fukui, Satoshi; Yonekura, Daisuke; Murakami, Ri-Ichi

The surface properties like roughness etc. strongly influence the fatigue strength of high-tensile steel. To investigate the effect of surface condition and TiN coating on the fatigue strength of high-strength steel, four-point bending fatigue tests were carried out for martensitic stainless steel with TiN film coated using arc ion plating (AIP) method. This study, using samples that had been polished under several size of grind particle, examines the influence of pre-coating treatment on fatigue properties. A 2-µm-thick TiN film was deposited onto the substrate under three kinds of polishing condition. The difference of the hardness originated in the residual stress or thin deformation layer where the difference of the size of grinding particle of the surface polishing. And it leads the transformation of the interface of the substrate and the TiN film and improves fatigue limit.

Diamond Coatings

NASA Technical Reports Server (NTRS)

1990-01-01

Advances in materials technology have demonstrated that it is possible to get the advantages of diamond in a number of applications without the cost penalty, by coating and chemically bonding an inexpensive substrate with a thin film of diamond-like carbon (DLC). Diamond films offer tremendous technical and economic potential in such advances as chemically inert protective coatings; machine tools and parts capable of resisting wear 10 times longer; ball bearings and metal cutting tools; a broad variety of optical instruments and systems; and consumer products. Among the American companies engaged in DLC commercialization is Diamonex, Inc., a diamond coating spinoff of Air Products and Chemicals, Inc. Along with its own proprietary technology for both polycrystalline diamond and DLC coatings, Diamonex is using, under an exclusive license, NASA technology for depositing DLC on a substrate. Diamonex is developing, and offering commercially, under the trade name Diamond Aegis, a line of polycrystalline diamond-coated products that can be custom tailored for optical, electronic and engineering applications. Diamonex's initial focus is on optical products and the first commercial product is expected in late 1990. Other target applications include electronic heat sink substrates, x-ray lithography masks, metal cutting tools and bearings.

Infrared Thermography as a Non-destructive Testing Solution for Thermal Spray Metal Coatings

NASA Astrophysics Data System (ADS)

Santangelo, Paolo E.; Allesina, Giulio; Bolelli, Giovanni; Lusvarghi, Luca; Matikainen, Ville; Vuoristo, Petri

2017-12-01

In this work, an infrared (IR) thermographic procedure was evaluated as a non-destructive testing tool to detect damage in thermal spray metallic coatings. As model systems, polished HVOF- and HVAF-sprayed Fe-based layers deposited onto steel plates were employed. Damage by external-object impingement was simulated through a cyclic impact-test apparatus, which induced circumferential and radial cracks across all model systems, and interface cracks of different sizes in distinct samples. Damaged and undamaged plates were bulk-heated to above 100 °C using an IR lamp; their free-convection cooling was then recorded by an IR thermocamera. The intentionally induced defects were hardly detectable in IR thermograms, due to IR reflection and artificial "hot" spots induced by residuals of transfer material from the impacting counterbody. As a micrometer-thin layer of black paint was applied, surface emissivity got homogenized and any artifacts were effectively suppressed, so that failed coating areas clearly showed up as "cold spots." This effect was more apparent when large interface cracks occurred. Finite-element modeling proved the physical significance of the IR-thermography approach, showing that failed coating areas are cooled by surrounding air faster than they are heated by conduction from the hot substrate, which is due to the insulating effect of cracks.

Friction surfaced Stellite6 coatings

DOE Office of Scientific and Technical Information (OSTI.GOV)

Rao, K. Prasad; Damodaram, R.; Rafi, H. Khalid, E-mail: khalidrafi@gmail.com

2012-08-15

Solid state Stellite6 coatings were deposited on steel substrate by friction surfacing and compared with Stellite6 cast rod and coatings deposited by gas tungsten arc and plasma transferred arc welding processes. Friction surfaced coatings exhibited finer and uniformly distributed carbides and were characterized by the absence of solidification structure and compositional homogeneity compared to cast rod, gas tungsten arc and plasma transferred coatings. Friction surfaced coating showed relatively higher hardness. X-ray diffraction of samples showed only face centered cubic Co peaks while cold worked coating showed hexagonally close packed Co also. - Highlights: Black-Right-Pointing-Pointer Stellite6 used as coating material formore » friction surfacing. Black-Right-Pointing-Pointer Friction surfaced (FS) coatings compared with casting, GTA and PTA processes. Black-Right-Pointing-Pointer Finer and uniformly distributed carbides in friction surfaced coatings. Black-Right-Pointing-Pointer Absence of melting results compositional homogeneity in FS Stellite6 coatings.« less

Strain isolated ceramic coatings

NASA Technical Reports Server (NTRS)

Tolokan, R. P.; Brady, J. B.; Jarrabet, G. P.

1985-01-01

Plasma sprayed ceramic coatings are used in gas turbine engines to improve component temperature capability and cooling air efficiency. A compliant metal fiber strain isolator between a plasma sprayed ceramic coating and a metal substrate improves ceramic durability while allowing thicker coatings for better insulation. Development of strain isolated coatings has concentrated on design and fabrication of coatings and coating evaluation via thermal shock testing. In thermal shock testing, five types of failure are possible: buckling failure im compression on heat up, bimetal type failure, isothermal expansion mismatch failure, mudflat cracking during cool down, and long term fatigue. A primary failure mode for thermally cycled coatings is designated bimetal type failure. Bimetal failure is tensile failure in the ceramic near the ceramic-metal interface. One of the significant benefits of the strain isolator is an insulating layer protecting the metal substrate from heat deformation and thereby preventing bimetal type failure.

Coatings Guide

EPA Science Inventory

The Coatings Guide is a free online information resource that focuses on alternative, low-emission coatings for metal, plastic, and architectural substrates. Developed cooperatively by the U.S. EPA's Office of Research and Development and Research Triangle Institute (RTI) Interna...

Innovations in coating technology.

PubMed

Behzadi, Sharareh S; Toegel, Stefan; Viernstein, Helmut

2008-01-01

Despite representing one of the oldest pharmaceutical techniques, coating of dosage forms is still frequently used in pharmaceutical manufacturing. The aims of coating range from simply masking the taste or odour of drugs to the sophisticated controlling of site and rate of drug release. The high expectations for different coating technologies have required great efforts regarding the development of reproducible and controllable production processes. Basically, improvements in coating methods have focused on particle movement, spraying systems, and air and energy transport. Thereby, homogeneous distribution of coating material and increased drying efficiency should be accomplished in order to achieve high end product quality. Moreover, given the claim of the FDA to design the end product quality already during the manufacturing process (Quality by Design), the development of analytical methods for the analysis, management and control of coating processes has attracted special attention during recent years. The present review focuses on recent patents claiming improvements in pharmaceutical coating technology and intends to first familiarize the reader with the available procedures and to subsequently explain the application of different analytical tools. Aiming to structure this comprehensive field, coating technologies are primarily divided into pan and fluidized bed coating methods. Regarding pan coating procedures, pans rotating around inclined, horizontal and vertical axes are reviewed separately. On the other hand, fluidized bed technologies are subdivided into those involving fluidized and spouted beds. Then, continuous processing techniques and improvements in spraying systems are discussed in dedicated chapters. Finally, currently used analytical methods for the understanding and management of coating processes are reviewed in detail in the last section of the review.

Coated article and method of making

NASA Technical Reports Server (NTRS)

Wang, Hongyu (Inventor); Lee, Kang Neung (Inventor)

2002-01-01

An article includes a silicon-containing substrate and a modified mullite coating. The modified mullite coating comprises mullite and a modifier component that reduces cracks in the modified mullite coating. The article can further comprise a thermal barrier coating applied to the modified mullite coating. The modified mullite coating functions as a bond coating between the external environmental/thermal barrier coating and the silicon-containing substrate. In a method of forming an article, a silicon-containing substrate is formed and a modified mullite coating is applied. The modified mullite coating comprises mullite and a modifier component that reduces cracks in the modified mullite coating.

Coated article and method of making

NASA Technical Reports Server (NTRS)

Wang, Hongyu (Inventor); Lee, Kang Neung (Inventor)

2003-01-01

An article includes a silicon-containing substrate and a modified mullite coating. The modified mullite coating comprises mullite and a modifier component that reduces cracks in the modified mullite coating. The article can further comprise a thermal barrier coating applied to the modified mullite coating. The modified mullite coating functions as a bond coating between the external environmental/thermal barrier coating and the silicon-containing substrate. In a method of forming an article, a silicon-containing substrate is formed and a modified mullite coating is applied. The modified mullite coating comprises mullite and a modifier component that reduces cracks in the modified mullite coating.

LEVELING METAL COATINGS

DOEpatents

Gage, H.A.

1959-02-10

A method is described for applying metallic coatings to a cylinder of uranium. An aluminum-silicon coat is applied by a process consisting of first cleaning the article by immersion for 5 minutes in 50% nitric acid at 65 C. The article then is dipped through a flux, prepared by adding 10% sodium fluoride to 90% of a flux comprising 53% potassium chloride, 42% lithium chloride, and 5% sodium chloride at 560 for 2 minutes and then directly into a molten metal bath comprising 99% aluminun and 12% silicon at 620 C for 3 minutes. While the coating is yet molten the article is transferred to a pair of steel rollers and rolled until the coating solidifies. By varying the composition of the flux other metals such as zinc, lead or the like may be coated on uranium in a similar manner.

Low Temperature Powder Coating

DTIC Science & Technology

2011-02-09

of volatile organic compounds (VOCs) and hazardous air pollutants (HAPs) • Legacy primers contain hexavalent chrome • Conventional powder coatings...coatings both in laboratory and field service evaluations • LTCPC allows environmental cost reductions through VOC/HAP elimination and hexavalent ... chrome reduction. • The LTCPC process greatly shortens the coating operation (LTCPC cures much more rapidly then conventional wet coatings) resulting in

Age and significance of the Quaternary cemented deposits of the Duje Valley (Picos de Europa, Northern Spain)

NASA Astrophysics Data System (ADS)

Villa, Elisa; Stoll, Heather; Farias, Pedro; Adrados, Luna; Edwards, R. Lawrence; Cheng, Hai

2013-01-01

Cemented calcareous breccias appear in the Picos de Europa (Cantabrian Mountains, Spain) resting on glacially abraded surfaces and covered by moraines. U/Th dating of the calcite coating the clasts was successful in two samples, the oldest one indicating that the breccias accumulated during or prior to Marine Isotope Stage (MIS) 11, and the youngest indicating later cementation during MIS 8. The former introduces a limit for the age of the glaciation preceding the breccias, which cannot correspond to an event younger than MIS 12. This is the oldest absolute age so far obtained for intercalated glacial/interglacial deposits of the Iberian Peninsula.

Coating Layer Characterization of Laser Deposited AlSi Coating over Laser Weld Bead

NASA Astrophysics Data System (ADS)

Gu, Hongping; Van Gelder, Aldo

Corrosion protection of steel components is an important topic in automotive industry. Laser beam welding makes a narrow weld bead, thus minimizing the damage to the original coating on the steel material. However, the weld bead loses its original coating and is vulnerable to corrosive attack. It was demonstrated in this study that laser beam generated AlSi coating is an effective way to apply a protective coating on the weld bead. Coatings with different thickness and topography have been deposited under different laser power and processing speed. The microstructure of the as-deposited coating and its evolution after heat treatment has been studied. EDS was employed to analyze the distribution of chemical compositions of the laser generated coatings. Several metallic compounds of Al and iron have been identified. It was found that the type of metallic compounds can be influenced by the laser processing parameters.

40 CFR 180.519 - Bromide ion and residual bromine; tolerances for residues.

Code of Federal Regulations, 2010 CFR

2010-07-01

... 40 Protection of Environment 23 2010-07-01 2010-07-01 false Bromide ion and residual bromine... Tolerances § 180.519 Bromide ion and residual bromine; tolerances for residues. (a) General. The food additives, bromide ion and residual bromine, may be present in water, potable in accordance with the...

40 CFR 180.519 - Bromide ion and residual bromine; tolerances for residues.

Code of Federal Regulations, 2011 CFR

2011-07-01

... 40 Protection of Environment 24 2011-07-01 2011-07-01 false Bromide ion and residual bromine... Tolerances § 180.519 Bromide ion and residual bromine; tolerances for residues. (a) General. The food additives, bromide ion and residual bromine, may be present in water, potable in accordance with the...

THE COATINGS GUIDE: AN INTEGRATED TOOL FOR COATINGS DECISIONS

EPA Science Inventory

The Coatings Guide, formerly known as the Coatings Alternative Guide (CAGE), is a free Internet pollution prevention tool designed to help small-business coaters of metal and plastic substrates identify alternatives as potential drop-in replacements for existing operations. As sh...