Science.gov

Sample records for actual boiler environment

  1. Investigations on the Behavior of HVOF and Cold Sprayed Ni-20Cr Coating on T22 Boiler Steel in Actual Boiler Environment

    NASA Astrophysics Data System (ADS)

    Bala, Niraj; Singh, Harpreet; Prakash, Satya; Karthikeyan, J.

    2012-01-01

    High temperature corrosion accompanied by erosion is a severe problem, which may result in premature failure of the boiler tubes. One countermeasure to overcome this problem is the use of thermal spray protective coatings. In the current investigation high velocity oxy-fuel (HVOF) and cold spray processes have been used to deposit commercial Ni-20Cr powder on T22 boiler steel. To evaluate the performance of the coatings in actual conditions the bare as well as the coated steels were subjected to cyclic exposures, in the superheater zone of a coal fired boiler for 15 cycles. The weight change and thickness loss data were used to establish kinetics of the erosion-corrosion. X-ray diffraction, surface and cross-sectional field emission scanning electron microscope/energy dispersive spectroscopy (FE-SEM/EDS) and x-ray mapping techniques were used to analyse the as-sprayed and corroded specimens. The HVOF sprayed coating performed better than its cold sprayed counterpart in actual boiler environment.

  2. High Temperature Behavior of Cr3C2-NiCr Coatings in the Actual Coal-Fired Boiler Environment

    NASA Astrophysics Data System (ADS)

    Bhatia, Rakesh; Sidhu, Hazoor Singh; Sidhu, Buta Singh

    2015-03-01

    Erosion-corrosion is a serious problem observed in steam-powered electricity generation plants, and industrial waste incinerators. In the present study, four compositions of Cr3C2-(Ni-20Cr) alloy coating powder were deposited by high-velocity oxy-fuel spray technique on T-91 boiler tube steel. The cyclic studies were performed in a coal-fired boiler at 1123 K ± 10 K (850 °C ± 10 °C). X-ray diffraction, scanning electron microscopy/energy dispersive X-ray analysis and elemental mapping analysis techniques were used to analyze the corrosion products. All the coatings deposited on T-91 boiler tube steel imparted hot corrosion resistance. The 65 pctCr3C2 -35 pct (Ni-20Cr)-coated T-91 steel sample performed better than all other coated samples in the given environment.

  3. Performance of high-velocity oxy-fuel-sprayed chromium carbide-nickel chromium coating in an actual boiler environment of a thermal power plant

    SciTech Connect

    Sidhu, T.S.; Prakash, S.; Agrawal, R.D.

    2007-09-15

    The present study aims to evaluate the performance of a high-velocity oxy-fuel (HVOF)-sprayed Cr{sub 3}C{sub 2}-NiCr (chromium carbide-nickel chromium) coating on a nickel-based super-alloy in an actual industrial environment of a coal-fired boiler, with the objective to protect the boiler super-heater and reheater tubes from hot corrosion. The tests were performed in the platen super heater zone of a coal-fired boiler for 1,000 h at 900 degrees C under cyclic conditions. The Cr{sub 3}C{sub 2}-NiCr coating imparted the necessary protection to the nickel-based super alloy in the given environment. The dense and flat splat structure of the coating, and the formation of oxides of chromium and nickel and their spinels, might have protected the substrate super alloy from the inward permeation of corrosive species.

  4. Research into Students' Perceptions of Preferred and Actual Learning Environment.

    ERIC Educational Resources Information Center

    Hattie, John A.; And Others

    Measures of both preferred and actual classroom and school environment were administered to 1,675 secondary school students in New South Wales (Australia). Shortened versions of the My Class Inventory, Classroom Environment Scale, and Individualized Classroom Environment Questionnaire, as well as the Quality of School Life questionnaire were…

  5. Carbon dioxide fixation by microalgae photosynthesis using actual flue gas discharged from a boiler

    SciTech Connect

    Matsumoto, Hiroyo; Shioji, Norio; Hamasaki, Akihiro

    1995-12-31

    To mitigate CO{sub 2} discharged from thermal power plants, studies on CO{sub 2} fixation by the photosynthesis of microalgae using actual exhaust gas have been carried out. The results are as follows: (1) A method is proposed for evaluating the maximum photosynthesis rate in the raceway cultivator using only the algal physical properties; (2) Outdoor cultivation tests taking actual flue gas were performed with no trouble or break throughout 1 yr using the strain collected in the test; (3) The produced microalgae is effective as solid fuel; and (4) The feasibility studies of this system were performed. The system required large land area, but the area is smaller than that required for other biomass systems, such as tree farms.

  6. Nickel-chromium plasma spray coatings: A way to enhance degradation resistance of boiler tube steels in boiler environment

    SciTech Connect

    Sidhu, B.S.; Prakash, S.

    2006-03-15

    Boiler tube steels, namely low carbon steel ASTM-SA210-Grade A1 (GrA1), 1Cr-0.5Mo steel ASTM-SA213-T-11 (T11), and 2.25Cr-1Mo steel ASTM-SA213-T-22 (T22), were used as substrate steels. Ni-22Cr-10AI-1Y powder was sprayed as a bond coat 150 {mu}m thick before a 200 {mu}m final coating of Ni-20Cr was applied. Coatings were characterized prior to testing in the environment of a coal fired boiler. The uncoated and coated steels were inserted in the platen superheater zone of a coal fired boiler at around 755{sup o}C for 10 cycles, each 100 h. Coated steels showed lower degradation (erosion-corrosion) rate than uncoated steels showed. The lowest rate was observed in the case of Ni-20Cr coated T11 steel. Among the uncoated steels, the observed rate of degradation was the lowest for the T22 steel.

  7. Determining heat loss into the environment based on comprehensive investigation of boiler performance characteristics

    NASA Astrophysics Data System (ADS)

    Lyubov, V. K.; Malygin, P. V.; Popov, A. N.; Popova, E. I.

    2015-08-01

    A refined procedure for determining heat loss into the environment from heat-generating installations is presented that takes into account the state of their lining and heat insulation quality. The fraction of radiative component in the total amount of heat loss through the outer surfaces is determined. The results from experimental investigations of the thermal engineering and environmental performance characteristics of a foreign hot-water boiler in firing wood pellets are presented. A conclusion is drawn about the possibility of using such hot-water boilers for supplying heat to low-rise buildings, especially for the conditions of the North-Arctic region. The results from a thermal engineering investigation of wood pellets and furnace residue carried out on installations of a thermal analysis laboratory are presented together with the grain-size composition of fuel and indicators characterizing the mechanical strength of wood pellets. The velocity fields, flue gas flow rates, and soot particle concentrations are determined using the external filtration methods, and the composition of combustion products is investigated using a gas analyzer. The graphs of variation with time of boiler external surface temperature from the moment of achieving the nominal mode of operation and heat loss into the environment for stationary boilers are presented.

  8. Performance of composite coatings in a coal-fired boiler environment

    SciTech Connect

    Nava, J.C.

    2009-09-15

    Four samples of thermal spray coatings, each made from different core wire consumables by twin wire arc spray, were exposed for 18 months in a coal-fired boiler environment. The tests are described and the performance of each coating is evaluated. Results indicated that the four consumable wire alloys showed remarkable resistance to fly ash erosion and corrosion over the period of the test.

  9. Clinical learning environments (actual and expected): perceptions of Iran University of Medical Sciences nursing students

    PubMed Central

    Bigdeli, Shoaleh; Pakpour, Vahid; Aalaa, Maryam; Shekarabi, Robabeh; Sanjari, Mahnaz; Haghani, Hamid; Mehrdad, Neda

    2015-01-01

    Background: Educational clinical environment has an important role in nursing students' learning. Any difference between actual and expected clinical environment will decrease nursing students’ interest in clinical environments and has a negative correlation with their clinical performance. Methods: This descriptive cross-sectional study is an attempt to compare nursing students' perception of the actual and expected status of clinical environments in medical-surgical wards. Participants of the study were 127 bachelor nursing students of Iran University of Medical Sciences in the internship period. Data gathering instruments were a demographic questionnaire (including sex, age, and grade point average), and the Clinical Learning Environment Inventory (CLEI) originally developed by Professor Chan (2001), in which its modified Farsi version (Actual and Preferred forms) consisting 42 items, 6 scales and 7 items per scale was used. Descriptive and inferential statistics (t-test, paired t-test, ANOVA) were used for data analysis through SPSS version 16. Results: The results indicated that there were significant differences between the preferred and actual form in all six scales. In other word, comparing with the actual form, the mean scores of all items in the preferred form were higher. The maximum mean difference was in innovation and the highest mean difference was in involvement scale. Conclusion: It is concluded that nursing students do not have a positive perception of their actual clinical teaching environment and this perception is significantly different from their perception of their expected environment. PMID:26034726

  10. Using Student Perceptions to Compare Actual and Preferred Classroom Environment in Queensland Schools

    ERIC Educational Resources Information Center

    Dorman, Jeffrey P.

    2008-01-01

    Students' perceptions of actual and preferred classroom environment were investigated using the "What is happening in this class? questionnaire" (WIHIC). The WIHIC assesses seven classroom environment dimensions: student cohesiveness, teacher support, involvement, task orientation, investigation, cooperation and equity. A sample of 978 secondary…

  11. Preferred-Actual Learning Environment "Spaces" and Earth Science Outcomes in Taiwan

    ERIC Educational Resources Information Center

    Chang, Chun-Yen; Hsiao, Chien-Hua; Barufaldi, James P.

    2006-01-01

    This study examines the possibilities of differential impacts on students' earth science learning outcomes between different preferred-actual learning environment spaces by using a newly developed ESCLEI (Earth Science Classroom Learning Environment Instrument). The instrument emphasizes three simultaneously important classroom components:…

  12. A Comparison of Actual and Preferred Classroom Environments as Perceived by Middle School Students

    ERIC Educational Resources Information Center

    Lai, Hsiang-Ru; Chou, Wei-Lun; Miao, Nae-Fang; Wu, Yu-Ping; Lee, Pi-Hsia; Jwo, Jiunn-Chern

    2015-01-01

    Background: A good classroom environment can promote students' learning motivation and affect their academic efficacy and adaptation. This study compares the perceptions of Taiwanese middle school students regarding actual and preferred classroom environments and explores the association with sex and grade level. Methods: Data were collected using…

  13. Preferred-actual learning environment spaces and earth science outcomes in Taiwan

    NASA Astrophysics Data System (ADS)

    Chang, Chun-Yen; Hsiao, Chien-Hua; Barufaldi, James P.

    2006-05-01

    This study examines the possibilities of differential impacts on students' earth science learning outcomes between different preferred-actual learning environment spaces by using a newly developed ESCLEI (Earth Science Classroom Learning Environment Instrument). The instrument emphasizes three simultaneously important classroom components: content, method, and assessment with both student-centered and teacher-centered scales embedded. Findings suggest that preferred-actual space (PASmatch) between posttreatment perceptions and pretreatment preferences accounted for a more substantial and statistically significant amount of learning outcomes in terms of students' attitudes toward the subject matter with greater than large effect size, concerning practical significance in the actual earth science classroom. These findings suggest that earth science instruction in the secondary schools should bridge the gap between students' preferred/perceived learning environment with the aim to enhance their learning outcomes.

  14. Forced-flow once-through boilers. [structural design criteria/aerospace environments

    NASA Technical Reports Server (NTRS)

    Stone, J. R.; Gray, V. H.; Gutierrez, O. A.

    1975-01-01

    A compilation and review of NASA-sponsored research on boilers for use in spacecraft electrical power generation systems is presented. Emphasis is on the heat-transfer and fluid-flow problems. In addition to space applications, much of the boiler technology is applicable to terrestrial and marine uses such as vehicular power, electrical power generation, vapor generation, and heating and cooling. Related research areas are discussed such as condensation, cavitation, line and boiler dynamics, the SNAP-8 project (Mercury-Rankine cycle), and conventional terrestrial boilers (either supercritical or gravity-assisted liquid-vapor separation types). The research effort was directed at developing the technology for once-through compact boilers with high heat fluxes to generate dry vapor stably, without utilizing gravity for phase separations. A background section that discusses, tutorially, the complex aspects of the boiling process is presented. Discussions of tests on alkali metals are interspersed with those on water and other fluids on a phenomenological basis.

  15. Development and Validation of Short Forms of Some Instruments Measuring Student Perceptions of Actual and Preferred Classroom Learning Environment.

    ERIC Educational Resources Information Center

    Fraser, Barry J.; Fisher, Darrell L.

    1983-01-01

    Describes development/validation of short forms of Individualized Classroom Environment Questionnaire (ICEQ), My Class Inventory (MCI), and Classroom Environment Scale (CES). In addition to these forms measuring perceptions of actual classroom environment, ICEQ and CES short forms measuring preferred classroom environment were also developed.…

  16. Moving Sound Source Localization Based on Sequential Subspace Estimation in Actual Room Environments

    NASA Astrophysics Data System (ADS)

    Tsuji, Daisuke; Suyama, Kenji

    This paper presents a novel method for moving sound source localization and its performance evaluation in actual room environments. The method is based on the MUSIC (MUltiple SIgnal Classification) which is one of the most high resolution localization methods. When using the MUSIC, a computation of eigenvectors of correlation matrix is required for the estimation. It needs often a high computational costs. Especially, in the situation of moving source, it becomes a crucial drawback because the estimation must be conducted at every the observation time. Moreover, since the correlation matrix varies its characteristics due to the spatial-temporal non-stationarity, the matrix have to be estimated using only a few observed samples. It makes the estimation accuracy degraded. In this paper, the PAST (Projection Approximation Subspace Tracking) is applied for sequentially estimating the eigenvectors spanning the subspace. In the PAST, the eigen-decomposition is not required, and therefore it is possible to reduce the computational costs. Several experimental results in the actual room environments are shown to present the superior performance of the proposed method.

  17. College Science Students' Perception Gaps in Preferred-Actual Learning Environment in a Reformed Introductory Earth Science Course in Taiwan

    ERIC Educational Resources Information Center

    Chang, Chun-Yeh; Chang, Yueh-Hsia

    2010-01-01

    This study used an instrument to examine undergraduate students' preferred and actual learning environment perceptions in an introductory earth science course. The results show that science students expect to learn in a learning environment combining teacher-centred and student-centred approaches. However, an expectation incongruence was found in…

  18. A Comparison of the Actual and Preferred Classroom Learning Environment in Biology and Chemistry as Perceived by High School Students.

    ERIC Educational Resources Information Center

    Hofstein, Avi; Lazarowitz, Reuven

    1986-01-01

    The actual and preferred students' perception of classroom learning environment was measured using a modified Hebrew version of the Learning Environment Inventory (LEI). This (validated and analyzed for reliability) was given to chemistry (N=1080) and biology (N=400) students. Results and implications are discussed. (Author/JN)

  19. The Impact of Congruency between Preferred and Actual Learning Environments on Tenth Graders' Science Literacy in Taiwan

    ERIC Educational Resources Information Center

    Chang, Chun-Yen; Yeh, Ting-Kuang; Lin, Chun-Yen; Chang, Yueh-Hsia; Chen, Chia-Li D.

    2010-01-01

    This study explored the effects of congruency between preferred and actual learning environment (PLE & ALE) perceptions on students' science literacy in terms of science concepts, attitudes toward science, and the understanding of the nature of science in an innovative curriculum of High Scope Project, namely Sci-Tech Mind and Humane Heart…

  20. Experimental study using infrared thermography on the convective heat transfer of a TGV brake disc in the actual environment

    NASA Astrophysics Data System (ADS)

    Siroux, Monica; Harmand, Souad; Desmet, Bernard

    2002-07-01

    We present an experimental identification of the local and mean Nusselt number from a rotating TGV brake disk model in the actual environment and exposed to an air flow parallel to the disk surface. This method is based on the use of a heated thermally thick disk combined with the technique of temperature measurement by infrared thermography. The local and mean convective heat transfer coefficient from the disk surface is identified by solving the steady state heat equation by a finite difference method using the experimental temperature distribution as boundary conditions. The experimental setup is constituted of a model disk with all the representative parts of the actual TGV brake system. The disk and its actual environment are inside a wind tunnel test section, so that the rotational disk speed and the air flow velocity can be varied. Tests were carried out for rotational speeds w between 325 and 2000 rpm (rotational Reynolds number Re between 88,500 and 545,000), and for an air flow velocity U ranging between 0 and 12 m(DOT)s-1 (air flow Reynolds number Re0 between 0 and 153,000).

  1. Corrosion loss measurement of boiler tubes in a waste incineration environment by A.C. impedance method

    SciTech Connect

    Matsunaga, Yasuo; Nakagawa, Kiyokazu

    1997-08-01

    To monitor the corrosion rate of materials of boiler tubes in simulated waste incineration environment, A.C. impedance measurements were carried out for Alloy 625, SUS347H and STBA24 embedded in NaCl- KCl- NaSO{sub 4}-K{sub 2}SO{sub 4}-Al{sub 2}O{sub 3} mixed synthetic ash deposit at 600 C. Though the ash includes some non-melting component, A.C. impedance measurements can be applied to evaluate corrosion rates in the same manner the corrosion of materials immersed in molten salts. Supposing the difference of impedance between the low frequency and high frequency ({Delta}R) as polarization resistance, a linear relation was obtained between 1/{Delta}R and corrosion losses in air, air-0.1 vol.% HCl and air-10vol.% H{sub 2}O atmospheres. The HCl addition in accelerated the corrosion of all specimens by reducing basicity of the molten salt. On the other hand, the H{sub 2}O addition reduced the corrosion of Alloy 625, but it accelerated the corrosion of SUS347H and STBA24.

  2. Application of High Temperature Corrosion-Resistant Materials and Coatings Under Severe Corrosive Environment in Waste-to-Energy Boilers

    NASA Astrophysics Data System (ADS)

    Kawahara, Yuuzou

    2007-06-01

    Corrosion-resistant materials (CRMs) and coatings are key technologies to increase power generation efficiency and reduce maintenance in waste-to-energy (WTE) plants. Corrosion environment became severe as steam temperatures have increased. The steam condition of more than 400 °C/3.9 MPa became possible in WTE boilers by using highly durable corrosion-resistant coatings, such as thermal spray of Al/80Ni20Cr alloy, HVOF-sprayed NiCrSiB alloy, Alloy 625 weld overlay for waterwall tubes and also superheater tubes. Also, the use of 310S type stainless steels and high Cr-high Mo-Ni base and high Si-Cr-Ni-Fe alloys have progressed because of a better understanding of corrosion mechanisms. Furthermore, high durability coatings using cermet and ceramic materials were applied to high temperature superheaters. This paper describes the major developments and the application of CRMs and coating technologies in the last 30 years in WTE plants, the corrosion mechanisms of alloys, the deterioration mechanisms of spray coating layers, and future subjects for the development of corrosion-resistant materials and coatings.

  3. Experimental study using infrared thermography on the convective heat transfer of a TGV brake disc in the actual environment

    NASA Astrophysics Data System (ADS)

    Siroux, Monica; Harmand, Souad; Desmet, Bernard

    2001-03-01

    Local and mean convective heat transfer from a rotating TGV brake disc model in the actual environment and submitted to an air flow parallel to the disc surface is studied experimentally in this paper. The experimental technique is based on the use of a heated thermally thick disc combined with the technique of temperature measurement by infrared thermography. The local convective heat transfer coefficient from the disc surface is identified by solving the steady state heat equation by finite difference method using the experimental temperature distribution as boundary conditions. These tests were carried out for rotational speed (omega) between 325 and 2000 rpm (rotational Reynolds number Re between 88500 and 545000) so as to obtain laminar and turbulent flow on the disc, and for air flow velocity U ranging between 0 and 12 m s-1 (air flow Reynolds number Re0 between 0 and 153000).

  4. Correlation between quantitative fit factors and workplace protection factors measured in actual workplace environments at a steel foundry.

    PubMed

    Zhuang, Ziqing; Coffey, Christopher C; Jensen, Paul A; Campbell, Donald L; Lawrence, Robert B; Myers, Warren R

    2003-01-01

    Past studies have found little or no correlation between workplace protection factors (WPFs) and quantitative fit factors (FFs). This study investigated the effect of good- and poor-fitting half-facepiece, air-purifying respirators on protection in actual workplace environments at a steel foundry and the correlation between WPFs and FFs. Fifteen burners and welders, who wore respirators voluntarily, and chippers participated in this study. Each subject was fit-tested with two respirator models each with three sizes, for a total of six fit-tests. Models and sizes were assigned this way to provide a wide range of FFs among study participants. Each worker donned the respirator twice per day (at the beginning of the shift and following the lunch break) for 2 days. Quantitative FFs were first obtained for each donning using the PortaCount Plus trade mark in a separate room. Without redonning the respirators, workers performed normal work for 1 to 2 hours, and WPFs were measured by collecting ambient and in-facepiece samples simultaneously. A second fit-test was conducted without disturbing the respirator. FFs were obtained by averaging the results from the first and second fit-tests. The resulting FFs had a geometric mean (GM) of 400 (range=10-6010) and a geometric standard deviation (GSD) of 6.1. Of the 55 valid donnings, 43 were good fitting (FFs> or =100) and 12 were poor fitting (FFs<100). The WPFs had a GM of 920 (range=13-230,000) and a GSD of 17.8. The WPFs were found to be significantly correlated with the FFs (R(2)=.55 and p-value=.0001). Therefore, FF was shown to be a meaningful indicator of respirator performance in actual workplace environments. PMID:14674806

  5. SNAP-8 refractory boiler development program

    NASA Technical Reports Server (NTRS)

    Fuller, R. A.

    1974-01-01

    Performance and endurance tests of the SNAP-8, SN-1 refractory metal boiler are described. The tests were successful and indicated that the boiler heat transfer area could be reduced significantly primarily because of the wetting characteristics of mercury on tantalum in a contaminant-free environment. A continuous endurance test of more than 10,000 hours was conducted without noticeable change in the thermal performance of the boiler. A conclusion of the metallographic examination of the boiler following the endurance test was that expected boiler life would be of the order of 40,000 hours at observed corrosion rates.

  6. Cermet composite thermal spray coatings for erosion and corrosion protection in combustion environments of advanced coal-fired boilers. Semi-annual technical progress report, February 1996--July 1996

    SciTech Connect

    Banovic, S.W.; Levin, B.F.; DuPont, J.N.; Marder, A.R.

    1996-08-01

    Present coal-fired boiler environments remain hostile to the materials of choice since corrosion and erosion can be a serious problem in certain regions of the boiler. Recently, the Clean Air Act Amendment is requiring electric power plants to reduce NO{sub x}, emissions to the environment. To reduce NO{sub x}, emissions, new low NO{sub x}, combustors are utilized which burn fuel with a substoichiometric amount of oxygen (i.e., low oxygen partial pressure). In these low NO{sub x} environments, H{sub 2}S gas is a major source of sulfur. Due to the sulfidation process, corrosion rates in reducing parts of boilers have increased significantly and existing boiler tube materials do not always provide adequate corrosion resistance. Combined attack due to corrosion and erosion is a concern because of the significantly increased operating costs which result in material failures. One method to combat corrosion and erosion in coal-fired boilers is to apply coatings to the components subjected to aggressive environments. Thermal spray coatings, a cermet composite comprised of hard ceramic phases of oxide and/or carbide in a metal binder, have been used with some success as a solution to the corrosion and erosion problems in boilers. However, little is known on the effect of the volume fraction, size, and shape of the hard ceramic phase on the erosion and corrosion resistance of the thermally sprayed coatings. It is the objective of this research to investigate metal matrix composite (cermet) coatings in order to determine the optimum ceramic/metal combination that will give the best erosion and corrosion resistance in new advanced coal-fired boilers.

  7. Cermet composite thermal spray coatings for erosion and corrosion protection in combustion environments of advanced coal-fired boilers

    SciTech Connect

    Levin, B.F.; DuPont, J.N.; Marder, A.R.

    1996-05-01

    Research is presently being initiated to determine the optimum ceramic/metal combination in thermally sprayed metal matrix composite coatings for erosion and corrosion resistance in new coal-fired boilers. The research will be accomplished by producing model cermet composites using powder metallurgy and electrodeposition methods in which the effect of ceramic/metal combination for the erosion and corrosion resistance will be determined. These results will provide the basis for determining the optimum hard phase constituents` size and volume percent in thermal spray coatings. Thermal spray coatings will be applied by our industrial sponsor and tested in our erosion and corrosion laboratories. During the last quarter, model Ni-Al{sub 2}O{sub 3} powder cermet composites were produced at Idaho National Engineering Laboratory by the Hot Isostatic Pressing (HIP) technique. The composite samples contained 0, 21, 27, 37, and 45 volume percent of Al{sub 2}O{sub 2} in a nickel matrix with an average size of alumina particles of 12 micrometers. The increase in volume fraction of alumina in the nickel matrix from 0 to 45% led to an increase in hardness of these composites from 85 to 180 HV{sub 1000}. The experimental procedure and preliminary microstructural characterization of Ni-Al{sub 2}O{sub 3} composites are presented in this progress report along with plans for the research in coming year. 3 figs.

  8. 40 CFR 761.71 - High efficiency boilers.

    Code of Federal Regulations, 2013 CFR

    2013-07-01

    ... 40 Protection of Environment 32 2013-07-01 2013-07-01 false High efficiency boilers. 761.71... PROHIBITIONS Storage and Disposal § 761.71 High efficiency boilers. (a) To burn mineral oil dielectric fluid containing a PCB concentration of ≥50 ppm, but boiler shall comply with the...

  9. 40 CFR 761.71 - High efficiency boilers.

    Code of Federal Regulations, 2010 CFR

    2010-07-01

    ... 40 Protection of Environment 30 2010-07-01 2010-07-01 false High efficiency boilers. 761.71... PROHIBITIONS Storage and Disposal § 761.71 High efficiency boilers. (a) To burn mineral oil dielectric fluid containing a PCB concentration of ≥50 ppm, but boiler shall comply with the...

  10. 40 CFR 65.149 - Boilers and process heaters.

    Code of Federal Regulations, 2013 CFR

    2013-07-01

    ... requirements of 40 CFR part 266, subpart H; or (B) The boiler or process heater has certified compliance with...). If an owner or operator elects to use a boiler or process heater to replace an existing recovery... 40 Protection of Environment 16 2013-07-01 2013-07-01 false Boilers and process heaters....

  11. 40 CFR 65.149 - Boilers and process heaters.

    Code of Federal Regulations, 2012 CFR

    2012-07-01

    ... requirements of 40 CFR part 266, subpart H; or (B) The boiler or process heater has certified compliance with...). If an owner or operator elects to use a boiler or process heater to replace an existing recovery... 40 Protection of Environment 16 2012-07-01 2012-07-01 false Boilers and process heaters....

  12. 40 CFR 65.149 - Boilers and process heaters.

    Code of Federal Regulations, 2011 CFR

    2011-07-01

    ... requirements of 40 CFR part 266, subpart H; or (B) The boiler or process heater has certified compliance with...). If an owner or operator elects to use a boiler or process heater to replace an existing recovery... 40 Protection of Environment 15 2011-07-01 2011-07-01 false Boilers and process heaters....

  13. 40 CFR 65.149 - Boilers and process heaters.

    Code of Federal Regulations, 2014 CFR

    2014-07-01

    ... requirements of 40 CFR part 266, subpart H; or (B) The boiler or process heater has certified compliance with...). If an owner or operator elects to use a boiler or process heater to replace an existing recovery... 40 Protection of Environment 16 2014-07-01 2014-07-01 false Boilers and process heaters....

  14. 40 CFR 65.149 - Boilers and process heaters.

    Code of Federal Regulations, 2010 CFR

    2010-07-01

    ... requirements of 40 CFR part 266, subpart H; or (B) The boiler or process heater has certified compliance with...). If an owner or operator elects to use a boiler or process heater to replace an existing recovery... 40 Protection of Environment 15 2010-07-01 2010-07-01 false Boilers and process heaters....

  15. Perception Shapes Experience: The Influence of Actual and Perceived Classroom Environment Dimensions on Girls' Motivations for Science

    ERIC Educational Resources Information Center

    Spearman, Juliette; Watt, Helen M. G.

    2013-01-01

    The classroom environment influences students' academic outcomes, but it is often students' perceptions that shape their classroom experiences. Our study examined the extent to which observed classroom environment features shaped perceptions of the classroom, and explained levels of, and changes in, girls' motivation in junior secondary school…

  16. Fossil-Fired Boilers

    1993-09-23

    Boiler Performance Model (BPM 3.0S) is a set of computer programs developed to analyze the performance of fossil-fired utility boilers. The programs can model a wide variety of boiler designs, and can model coal, oil, or natural gas firing. The programs are intended for use by engineers performing analyses of alternative fuels, alternative operating modes, or boiler modifications.

  17. Stress-Assisted Corrosion in Boiler Tubes

    SciTech Connect

    Preet M Singh; Steven J Pawel

    2006-05-27

    A number of industrial boilers, including in the pulp and paper industry, needed to replace their lower furnace tubes or decommission many recovery boilers due to stress-assisted corrosion (SAC) on the waterside of boiler tubes. More than half of the power and recovery boilers that have been inspected reveal SAC damage, which portends significant energy and economic impacts. The goal of this project was to clarify the mechanism of stress-assisted corrosion (SAC) of boiler tubes for the purpose of determining key parameters in its mitigation and control. To accomplish this in-situ strain measurements on boiler tubes were made. Boiler water environment was simulated in the laboratory and effects of water chemistry on SAC initiation and growth were evaluated in terms of industrial operations. Results from this project have shown that the dissolved oxygen is single most important factor in SAC initiation on carbon steel samples. Control of dissolved oxygen can be used to mitigate SAC in industrial boilers. Results have also shown that sharp corrosion fatigue and bulbous SAC cracks have similar mechanism but the morphology is different due to availability of oxygen during boiler shutdown conditions. Results are described in the final technical report.

  18. 40 CFR 63.11195 - Are any boilers not subject to this subpart?

    Code of Federal Regulations, 2012 CFR

    2012-07-01

    ... 40 Protection of Environment 15 2012-07-01 2012-07-01 false Are any boilers not subject to this..., and Institutional Boilers Area Sources What This Subpart Covers § 63.11195 Are any boilers not subject to this subpart? The types of boilers listed in paragraphs (a) through (g) of this section are...

  19. 40 CFR 63.11195 - Are any boilers not subject to this subpart?

    Code of Federal Regulations, 2013 CFR

    2013-07-01

    ... 40 Protection of Environment 15 2013-07-01 2013-07-01 false Are any boilers not subject to this..., and Institutional Boilers Area Sources What This Subpart Covers § 63.11195 Are any boilers not subject to this subpart? The types of boilers listed in paragraphs (a) through (k) of this section are...

  20. 40 CFR 63.7499 - What are the subcategories of boilers and process heaters?

    Code of Federal Regulations, 2012 CFR

    2012-07-01

    ... 40 Protection of Environment 14 2012-07-01 2011-07-01 true What are the subcategories of boilers..., and Institutional Boilers and Process Heaters Emission Limits and Work Practice Standards § 63.7499 What are the subcategories of boilers and process heaters? The subcategories of boilers and...

  1. 40 CFR 63.11200 - What are the subcategories of boilers?

    Code of Federal Regulations, 2011 CFR

    2011-07-01

    ... 40 Protection of Environment 14 2011-07-01 2011-07-01 false What are the subcategories of boilers... Institutional Boilers Area Sources Emission Limits, Work Practice Standards, Emission Reduction Measures, and Management Practices § 63.11200 What are the subcategories of boilers? The subcategories of boilers are...

  2. 40 CFR 63.7499 - What are the subcategories of boilers and process heaters?

    Code of Federal Regulations, 2010 CFR

    2010-07-01

    ... 40 Protection of Environment 13 2010-07-01 2010-07-01 false What are the subcategories of boilers..., and Institutional Boilers and Process Heaters Emission Limits and Work Practice Standards § 63.7499 What are the subcategories of boilers and process heaters? The subcategories of boilers and...

  3. 40 CFR 63.7491 - Are any boilers or process heaters not subject to this subpart?

    Code of Federal Regulations, 2014 CFR

    2014-07-01

    ... 40 Protection of Environment 14 2014-07-01 2014-07-01 false Are any boilers or process heaters not..., Commercial, and Institutional Boilers and Process Heaters What This Subpart Covers § 63.7491 Are any boilers or process heaters not subject to this subpart? The types of boilers and process heaters listed...

  4. 40 CFR 63.7491 - Are any boilers or process heaters not subject to this subpart?

    Code of Federal Regulations, 2013 CFR

    2013-07-01

    ... 40 Protection of Environment 14 2013-07-01 2013-07-01 false Are any boilers or process heaters not..., Commercial, and Institutional Boilers and Process Heaters What This Subpart Covers § 63.7491 Are any boilers or process heaters not subject to this subpart? The types of boilers and process heaters listed...

  5. 40 CFR 63.11195 - Are any boilers not subject to this subpart?

    Code of Federal Regulations, 2014 CFR

    2014-07-01

    ... 40 Protection of Environment 15 2014-07-01 2014-07-01 false Are any boilers not subject to this..., and Institutional Boilers Area Sources What This Subpart Covers § 63.11195 Are any boilers not subject to this subpart? The types of boilers listed in paragraphs (a) through (k) of this section are...

  6. 40 CFR 63.7499 - What are the subcategories of boilers and process heaters?

    Code of Federal Regulations, 2011 CFR

    2011-07-01

    ... 40 Protection of Environment 13 2011-07-01 2011-07-01 false What are the subcategories of boilers..., and Institutional Boilers and Process Heaters Emission Limits and Work Practice Standards § 63.7499 What are the subcategories of boilers and process heaters? The subcategories of boilers and...

  7. 40 CFR 63.11200 - What are the subcategories of boilers?

    Code of Federal Regulations, 2014 CFR

    2014-07-01

    ... 40 Protection of Environment 15 2014-07-01 2014-07-01 false What are the subcategories of boilers... Institutional Boilers Area Sources Emission Limits, Work Practice Standards, Emission Reduction Measures, and Management Practices § 63.11200 What are the subcategories of boilers? The subcategories of boilers,...

  8. 40 CFR 63.11195 - Are any boilers not subject to this subpart?

    Code of Federal Regulations, 2011 CFR

    2011-07-01

    ... 40 Protection of Environment 14 2011-07-01 2011-07-01 false Are any boilers not subject to this..., and Institutional Boilers Area Sources What This Subpart Covers § 63.11195 Are any boilers not subject to this subpart? The types of boilers listed in paragraphs (a) through (g) of this section are...

  9. 40 CFR 63.11200 - What are the subcategories of boilers?

    Code of Federal Regulations, 2012 CFR

    2012-07-01

    ... 40 Protection of Environment 15 2012-07-01 2012-07-01 false What are the subcategories of boilers... Institutional Boilers Area Sources Emission Limits, Work Practice Standards, Emission Reduction Measures, and Management Practices § 63.11200 What are the subcategories of boilers? The subcategories of boilers are...

  10. 40 CFR 63.11200 - What are the subcategories of boilers?

    Code of Federal Regulations, 2013 CFR

    2013-07-01

    ... 40 Protection of Environment 15 2013-07-01 2013-07-01 false What are the subcategories of boilers... Institutional Boilers Area Sources Emission Limits, Work Practice Standards, Emission Reduction Measures, and Management Practices § 63.11200 What are the subcategories of boilers? The subcategories of boilers,...

  11. Infrared imaging of fossil fuel power plant boiler interiors

    NASA Astrophysics Data System (ADS)

    Howard, James W.; Cranton, Brian W.; Armstrong, Karen L.; Hammaker, Robert G.

    1997-08-01

    Fossil fuel power plant boilers operate continuously for months at a time, typically shutting down only for routine maintenance or to address serious equipment failures. These shutdowns are very costly, and diagnostic tools and techniques which could be used to minimize shutdown duration and frequency are highly desirable. Due to the extremely hostile environment in these boilers, few tools exist to inspect and monitor operating boiler interiors. This paper presents the design of a passively cooled, infrared borescope used to inspect the interior of operating boilers. The borescope operates at 3.9 micrometer, where flame is partially transparent. The primary obstacles overcome in the instrument design were the harsh industrial environment surrounding the boilers and the high temperatures encountered inside the boilers. A portable yet durable lens system and enclosure was developed to work with a scanning radiometer to address these two problems by both shielding the radiometer from the environment and by extending the optical train into a snout designed to be inserted into access ports on the sides of the boiler. In this manner, interior images of the boiler can be made while keeping the radiometer safely outside the boiler. The lens views a 40 degree field of view through any 2.5' or larger opening in a foot thick boiler wall. Three of these borescopes have been built, and high resolution images of boiler interiors have been obtained.

  12. Urban thermal environment measurements and numerical simulation for an actual complex urban area covering a large district heating and cooling system in summer

    NASA Astrophysics Data System (ADS)

    Huang, Hong; Ooka, Ryozo; Kato, Shinsuke

    Urban thermal situation is thought to have a great influence on the air quality in urban areas. In recent years, the urban thermal environment has become worse, such as the days on which the temperature goes above 30 °C, the sultry nights and heat stroke increase due to changes in terrestrial cover and increased anthropogenic heat emission accompanied by urbanization. Therefore, the urban thermal environment should be carefully investigated and accurately analyzed for a better study of the air quality. Here, in order to study the urban thermal environment in summer, (1) the actual status of an urban thermal environment in a complex urban area covering a large district heating and cooling (DHC) system in Tokyo is investigated using field measurements, and (2) a numerical simulation program which can be adapted to complex urban areas coupled with convection, radiation and conduction is developed and used to predict the urban thermal environment. Wind velocity, temperature and humidity are obtained from the simulation, which shows good agreement with results of the field measurement. The spatial distribution of the standard effective temperature (SET *), the comprehensive index of human thermal comfort, is also calculated using the above results, to estimate the thermal comfort at the pedestrian level. This urban thermal numerical simulation can be coupled with air pollution dispersion and chemical processes to provide a more precise air quality prediction in complex urban areas.

  13. BOILER PERF MODEL

    SciTech Connect

    Winslow, J.C. )

    1988-01-01

    The BOILER PERFORMANCE MODEL is a package of eleven programs for predicting the heat transfer performance of fossil-fired utility boilers. The programs can model a wide variety of boiler designs, provide boiler performance estimates for coal, oil or gaseous fuels, determine the influence of slagging and fouling characteristics on boiler performance, and calculate performance factors for tradeoff analyses comparing boilers and fuels. Given a set of target operating conditions, the programs can estimate control settings, gas and steam operating profiles through the boiler, overall boiler efficiency, and fuel consumption. The programs are broken into three categories: data, calculation, and reports with a central processor program acting as the link allowing the user to access any of the data or calculation programs and easily move between programs. The calculations are divided among the following five programs: heat duty calculation, combustion calculation, furnace performance calculation, convection pass performance calculation, and air heater performance calculation. The programs can model subcritical or supercritical boilers, most configurations of convective passes including boilers that achieve final reheat steam temperature control by split back pass, boilers with as many as two reheat circuits and/or multiple attemperator stations in series, and boilers with or without economizers and/or air heaters. Either regenerative or tubular air heaters are supported. For wall-fired or tangentially-fired furnaces, the furnace performance program predicts the temperature of the flue gases leaving the furnace. It accounts for variations in excess air, gas recirculation, burner tilt, wall temperature, and wall cleanliness. For boilers having radiant panels or platens above the furnace, the convective pass program uses the results of the combustion chamber calculation to estimate the gas temperature entering the convective pass.

  14. 33. BOILER HOUSE FURNACE AND BOILER Close view of ...

    Library of Congress Historic Buildings Survey, Historic Engineering Record, Historic Landscapes Survey

    33. BOILER HOUSE - FURNACE AND BOILER Close view of the Dorward Engineering Company furnace and boiler which provided steam to the cooking retorts in the adjacent room. - Hovden Cannery, 886 Cannery Row, Monterey, Monterey County, CA

  15. 51. BOILER ROOM. SMALL BOILER ON LEFT OF UNKNOWN MANUFACTURE, ...

    Library of Congress Historic Buildings Survey, Historic Engineering Record, Historic Landscapes Survey

    51. BOILER ROOM. SMALL BOILER ON LEFT OF UNKNOWN MANUFACTURE, WITH INDUCTION MOTORS. HARTLEY BOILER, MONTGOMERY, ALABAMA, ON RIGHT. - Prattville Manufacturing Company, Number One, 242 South Court Street, Prattville, Autauga County, AL

  16. Boiler saves pollution problem

    SciTech Connect

    Kaiser, J.A.

    1981-02-01

    Monarch Furniture Industries, High Point, N.C. replaced their old locomotive-type boiler in 1978 with a multifuel boiler system from Energy Systems, Inc. of Chattanooga. The system burns the company's wood wastes, supplemented with low-cost coal in winter. It generates 17,250 lbs. per hour of steam, gives a much cleaner burn than the old boiler, and has a calculated payback period of 1.67 years.

  17. Compartment B3, boiler room; showing boiler facing of boiler #5 ...

    Library of Congress Historic Buildings Survey, Historic Engineering Record, Historic Landscapes Survey

    Compartment B-3, boiler room; showing boiler facing of boiler #5 aft to forward from passing room B-25. (030A) - USS Olympia, Penn's Landing, 211 South Columbus Boulevard, Philadelphia, Philadelphia County, PA

  18. Improving boiler efficiency

    SciTech Connect

    Yost, L.

    1982-06-24

    Boilers and burners are designed to operate most efficiently at, or near, full load. This fact seems to indicate that on/off operation is more efficient; however, standby losses must be considered. This article examines various types of industrial boiler heat losses that reduce efficiency and discusses methods for improving operation.

  19. 39. (Credit JTL) Interior of boiler room looking east; boiler ...

    Library of Congress Historic Buildings Survey, Historic Engineering Record, Historic Landscapes Survey

    39. (Credit JTL) Interior of boiler room looking east; boiler casing in background, boiler feedwater pumps and feedwater heater in middle ground; hot well on columns in left foreground. Steam lines from boilers to high service engines pass overhead. - McNeil Street Pumping Station, McNeil Street & Cross Bayou, Shreveport, Caddo Parish, LA

  20. 68. 1911 BOILER HOUSE LOOKING SOUTH. BOILERS ARE CA. 1945. ...

    Library of Congress Historic Buildings Survey, Historic Engineering Record, Historic Landscapes Survey

    68. 1911 BOILER HOUSE LOOKING SOUTH. BOILERS ARE CA. 1945. SPACE HEATING BOILER S REPLACED ORIGINAL 8 VERTICAL HIGH PRESSURE STEAM POWER BOILERS. THE ORIGINAL SHEET METAL FLUE IS IN THE UPPER CENTER. - Boston Manufacturing Company, 144-190 Moody Street, Waltham, Middlesex County, MA

  1. 40 CFR Table 4 to Subpart Ddddd of... - Operating Limits for Boilers and Process Heaters

    Code of Federal Regulations, 2013 CFR

    2013-07-01

    ... 40 Protection of Environment 14 2013-07-01 2013-07-01 false Operating Limits for Boilers and...: Industrial, Commercial, and Institutional Boilers and Process Heaters Pt. 63, Subpt. DDDDD, Table 4 Table 4 to Subpart DDDDD of Part 63—Operating Limits for Boilers and Process Heaters As stated in §...

  2. 40 CFR Table 3 to Subpart Jjjjjj... - Operating Limits for Boilers With Emission Limits

    Code of Federal Regulations, 2013 CFR

    2013-07-01

    ... 40 Protection of Environment 15 2013-07-01 2013-07-01 false Operating Limits for Boilers With..., Commercial, and Institutional Boilers Area Sources Pt. 63, Subpt. JJJJJJ, Table 3 Table 3 to Subpart JJJJJJ of Part 63—Operating Limits for Boilers With Emission Limits As stated in § 63.11201, you must...

  3. 40 CFR Table 4 to Subpart Ddddd of... - Operating Limits for Boilers and Process Heaters

    Code of Federal Regulations, 2014 CFR

    2014-07-01

    ... 40 Protection of Environment 14 2014-07-01 2014-07-01 false Operating Limits for Boilers and...: Industrial, Commercial, and Institutional Boilers and Process Heaters Pt. 63, Subpt. DDDDD, Table 4 Table 4 to Subpart DDDDD of Part 63—Operating Limits for Boilers and Process Heaters As stated in §...

  4. 40 CFR Table 3 to Subpart Jjjjjj... - Operating Limits for Boilers With Emission Limits

    Code of Federal Regulations, 2012 CFR

    2012-07-01

    ... 40 Protection of Environment 15 2012-07-01 2012-07-01 false Operating Limits for Boilers With..., Commercial, and Institutional Boilers Area Sources Pt. 63, Subpt. JJJJJJ, Table 3 Table 3 to Subpart JJJJJJ of Part 63—Operating Limits for Boilers With Emission Limits As stated in § 63.11201, you must...

  5. 40 CFR Table 3 to Subpart Jjjjjj... - Operating Limits for Boilers With Emission Limits

    Code of Federal Regulations, 2014 CFR

    2014-07-01

    ... 40 Protection of Environment 15 2014-07-01 2014-07-01 false Operating Limits for Boilers With..., Commercial, and Institutional Boilers Area Sources Pt. 63, Subpt. JJJJJJ, Table 3 Table 3 to Subpart JJJJJJ of Part 63—Operating Limits for Boilers With Emission Limits As stated in § 63.11201, you must...

  6. 40 CFR Table 3 to Subpart Jjjjjj... - Operating Limits for Boilers With Emission Limits

    Code of Federal Regulations, 2011 CFR

    2011-07-01

    ... 40 Protection of Environment 14 2011-07-01 2011-07-01 false Operating Limits for Boilers With..., Commercial, and Institutional Boilers Area Sources Pt. 63, Subpt. JJJJJJ, Table 3 Table 3 to Subpart JJJJJJ of Part 63—Operating Limits for Boilers With Emission Limits As stated in § 63.11201, you must...

  7. Drying Milk With Boiler Exhaust

    NASA Technical Reports Server (NTRS)

    Broussard, M. R.

    1984-01-01

    Considerable energy saved in powdered-milk industry. Only special requirement boiler fired with natural gas or other clean fuel. Boiler flue gas fed to spray drier where it directly contacts product to be dried. Additional heat supplied by auxillary combustor when boiler output is low. Approach adaptable to existing plants with minimal investment because most already equipped with natural-gas-fired boilers.

  8. Evaluation of thermal overload in boiler operators.

    PubMed

    Braga, Camila Soares; Rodrigues, Valéria Antônia Justino; Campos, Julio César Costa; de Souza, Amaury Paulo; Minette, Luciano José; de Moraes, Angêlo Casali; Sensato, Guilherme Luciano

    2012-01-01

    The Brazilians educational institutions need a large energy demand for the operation of laundries, restaurants and accommodation of students. Much of that energy comes from steam generated in boilers with wood fuel. The laboral activity in boiler may present problems for the operator's health due to exposure to excessive heat, and its operation has a high degree of risk. This paper describes an analysis made the conditions of thermal environment in the operation of a B category boiler, located at a Higher Education Institution, located in the Zona da Mata Mineira The equipments used to collect data were Meter WBGT of the Heat Index; Meter of Wet Bulb Index and Globe Thermometer (WBGT); Politeste Instruments, an anemometer and an Infrared Thermometer. By the application of questionnaires, the second phase consisted of collecting data on environmental factors (temperature natural environment, globe temperature, relative humidity and air velocity). The study concluded that during the period evaluated, the activity had thermal overload. PMID:22316768

  9. Corrosion probes for fireside monitoring in coal-fired boilers

    SciTech Connect

    Covino, Bernard S., Jr.; Bullard, Sophie J.; Ziomek-Moroz, M.; Holcomb, Gordon R.

    2005-01-01

    Corrosion probes are being developed and combined with an existing measurement technology to provide a tool for assessing the extent of corrosion of metallic materials on the fireside in coal-fired boilers. The successful development of this technology will provide power plant operators the ability to (1) accurately monitor metal loss in critical regions of the boiler, such as waterwalls, superheaters, and reheaters; and (2) use corrosion rates as process variables. In the former, corrosion data could be used to schedule maintenance periods and in the later, processes can be altered to decrease corrosion rates. The research approach involves laboratory research in simulated environments that will lead to field tests of corrosion probes in coal-fired boilers. Laboratory research has already shown that electrochemically-measured corrosion rates for ash-covered metals are similar to actual mass loss corrosion rates. Electrochemical tests conducted using a potentiostat show the corrosion reaction of ash-covered probes at 500?C to be electrochemical in nature. Corrosion rates measured are similar to those from an automated corrosion monitoring system. Tests of corrosion probes made with mild steel, 304L stainless steel (SS), and 316L SS sensors showed that corrosion of the sensors in a very aggressive incinerator ash was controlled by the ash and not by the alloy content. Corrosion rates in nitrogen atmospheres tended to decrease slowly with time. The addition of oxygen-containing gases, oxygen and carbon dioxide to nitrogen caused a more rapid decrease in corrosion rate, while the addition of water vapor increased the corrosion rate.

  10. Definition of hydraulic stability of KVGM-100 hot-water boiler and minimum water flow rate

    NASA Astrophysics Data System (ADS)

    Belov, A. A.; Ozerov, A. N.; Usikov, N. V.; Shkondin, I. A.

    2016-08-01

    In domestic power engineering, the methods of quantitative and qualitative-quantitative adjusting the load of the heat supply systems are widely distributed; furthermore, during the greater part of the heating period, the actual discharge of network water is less than estimated values when changing to quantitative adjustment. Hence, the hydraulic circuits of hot-water boilers should ensure the water velocities, minimizing the scale formation and excluding the formation of stagnant zones. The results of the calculations of hot-water KVGM-100 boiler and minimum water flow rate for the basic and peak modes at the fulfillment of condition of the lack of surface boil are presented in the article. The minimal flow rates of water at its underheating to the saturation state and the thermal flows in the furnace chamber were defined. The boiler hydraulic calculation was performed using the "Hydraulic" program, and the analysis of permissible and actual velocities of the water movement in the pipes of the heating surfaces was carried out. Based on the thermal calculations of furnace chamber and thermal- hydraulic calculations of heating surfaces, the following conclusions were drawn: the minimum velocity of water movement (by condition of boiling surface) at lifting movement of environment increases from 0.64 to 0.79 m/s; it increases from 1.14 to 1.38 m/s at down movement of environmental; the minimum water flow rate by the boiler in the basic mode (by condition of the surface boiling) increased from 887 t/h at the load of 20% up to 1074 t/h at the load of 100%. The minimum flow rate is 1074 t/h at nominal load and is achieved at the pressure at the boiler outlet equal to 1.1 MPa; the minimum water flow rate by the boiler in the peak mode by condition of surface boiling increases from 1669 t/h at the load of 20% up to 2021 t/h at the load of 100%.

  11. Utilization of silt as CFB boiler fuel

    SciTech Connect

    Herb, B.; Tsao, T.R.; Bickley, D.

    1994-12-31

    Bituminous silt represents an enormous source of discarded energy that is polluting the environment. Although bituminous silt is a potential opportunity fuel for circulating fluidized bed (CFB) boilers, handling problems and uncertainties about the impact of this fuel on CFB boiler performance and operating economics have prevented its use. Under sponsorship of the Pennsylvania Energy Development Authority, five different technologies having the potential to process silt into CFB boiler fuel were evaluated. The technologies evaluated include: washing, pelletizing, thermal drying, mulling and flaking. The desired goal was to process the silt into a form that can be fed to CFB boilers using conventional coal handling equipment and combusted in an environmentally acceptable manner. Criteria were developed for the product characteristics that are desired and tests were run to evaluate the technical feasibility of each silt processing technology. Based on these test results, the design and cost bases for a commercial silt processing facility were developed for each technology capable of achieving the desired product characteristics. As a result of considering both engineering and economic factors, the technology that best meets the objectives for use of processed silt as CFB boiler fuel was selected for further demonstration testing. This paper will present the results of this project up through the selection of the best silt processing technology.

  12. 42. BOILER HOUSE FOURTH FLOOR, FORCED DRAFT FANS ABOVE BOILERS ...

    Library of Congress Historic Buildings Survey, Historic Engineering Record, Historic Landscapes Survey

    42. BOILER HOUSE FOURTH FLOOR, FORCED DRAFT FANS ABOVE BOILERS (SEE DRAWING Nos. 10 & 11 OF 13) - Delaware County Electric Company, Chester Station, Delaware River at South end of Ward Street, Chester, Delaware County, PA

  13. Interior view of boiler house looking south. Boiler units are ...

    Library of Congress Historic Buildings Survey, Historic Engineering Record, Historic Landscapes Survey

    Interior view of boiler house looking south. Boiler units are on left. - Burnsville Natural Gas Pumping Station, Saratoga Avenue between Little Kanawha River & C&O Railroad line, Burnsville, Braxton County, WV

  14. 4. INTERIOR, CENTRAL BOILER ROOM, LOWER LEVEL, BOILERS, FROM SOUTHWEST ...

    Library of Congress Historic Buildings Survey, Historic Engineering Record, Historic Landscapes Survey

    4. INTERIOR, CENTRAL BOILER ROOM, LOWER LEVEL, BOILERS, FROM SOUTHWEST CORNER OF ROOM, LOOKING SOUTHEAST. - Oakland Naval Supply Center, Heating Plant, North of B Street & West of Third Street, Oakland, Alameda County, CA

  15. 1. EXTERIOR VIEW OF BOILER HOUSE FROM SOUTHWEST. THE BOILER ...

    Library of Congress Historic Buildings Survey, Historic Engineering Record, Historic Landscapes Survey

    1. EXTERIOR VIEW OF BOILER HOUSE FROM SOUTHWEST. THE BOILER HOUSE WAS USED FOR HEATING THE MILL; HYDRO-ELECTRIC POWER FOR PRODUCTION WAS PURCHASED FROM THE COLUMBUS LIGHT & POWER COMPANY. NORTH END OF 1924 MILL TO RIGHT, c. 1970 WINDOWLESS WEAVE ROOM ADDITION TO LEFT. - Stark Mill, Boiler House, 117 Corinth Road, Hogansville, Troup County, GA

  16. Super Boiler: First Generation, Ultra-High Efficiency Firetube Boiler

    SciTech Connect

    2006-06-01

    This factsheet describes a research project whose goal is to develop and demonstrate a first-generation ultra-high-efficiency, ultra-low emissions, compact gas-fired package boiler (Super Boiler), and formulate a long-range RD&D plan for advanced boiler technology out to the year 2020.

  17. Cermet composite thermal spray coatings for erosion and corrosion protection in combustion environments of advanced coal-fired boilers. Semiannual technical report, January 14, 1997--August 14, 1997

    SciTech Connect

    Schorr, B.S.; Levin, B.F.; DuPont, J.N.; Marder, A.R.

    1997-08-31

    Research is presently being conducted to determine the optimum ceramic/metal combination in thermally sprayed metal matrix composite coatings for erosion and corrosion resistance in new coal-fired boilers. The research will be accomplished by producing model cermet composites using powder metallurgy and electrodeposition methods in which the effect of ceramic/metal combination for the erosion and corrosion resistance will be determined. These results will provide the basis for determining the optimum hard phase constituent size and volume percent in thermal spray coatings. Thermal spray coatings will be applied by our industrial sponsor and tested in our erosion and corrosion laboratories. Bulk powder processed Ni-Al{sub 2}O{sub 3} composites were produced at Idaho National Engineering Laboratory. The composite samples contained 0, 21, 27, 37, and 45 volume percent Al{sub 2}O{sub 3} with an average particle size of 12 um. Also, to deposit model Ni-Al{sub 2}O{sub 3} coatings, an electrodeposition technique was developed and coatings with various volume fractions (0-35%) of Al{sub 2}O{sub 3} were produced. The powder and electrodeposition processing of Ni-Al{sub 2}O{sub 3} Composites provide the ability to produce two phase microstructure without changing the microstructure of the matrix material. Therefore, the effect of hard second phase particles size and volume fraction on erosion resistance could be analyzed.

  18. Dry bottom ash removal -- Ash cooling vs. boiler efficiency effects

    SciTech Connect

    Carrea, E.; Scavizzi, G.C.; Barsin, J.

    1998-07-01

    The current wet method of removing boiler bottom ash from coal fired utility boilers quenches the ash which in turn heats the water, evaporates a portion of it adding to the gas weights moved through the steam generator. The newer dry ash removal systems use a portion of the combustion air to cool ash and thus return some of the otherwise lost latent heat back to the furnace. There has been some debate concerning the overall effect upon boiler efficiency. For example when a large quantity of ash cooling air is required and the resulting decrease in air side air heater mass flow could result in an elevate stack gas temperature thus negating the efficiency enhancing dry bottom ash effect expected. The presentation will present actual data form operating units and provide various heat balances to demonstrate the actual performance conditions that have been achieved.

  19. 40 CFR Table 2 to Subpart Ddddd of... - Operating Limits for Boilers and Process Heaters With Particulate Matter Emission Limits

    Code of Federal Regulations, 2012 CFR

    2012-07-01

    ... 40 Protection of Environment 14 2012-07-01 2011-07-01 true Operating Limits for Boilers and... Hazardous Air Pollutants for Industrial, Commercial, and Institutional Boilers and Process Heaters Pt. 63, Subpt. DDDDD, Table 2 Table 2 to Subpart DDDDD of Part 63—Operating Limits for Boilers and...

  20. 40 CFR Table 2 to Subpart Ddddd of... - Operating Limits for Boilers and Process Heaters With Particulate Matter Emission Limits

    Code of Federal Regulations, 2010 CFR

    2010-07-01

    ... 40 Protection of Environment 13 2010-07-01 2010-07-01 false Operating Limits for Boilers and... Hazardous Air Pollutants for Industrial, Commercial, and Institutional Boilers and Process Heaters Pt. 63, Subpt. DDDDD, Table 2 Table 2 to Subpart DDDDD of Part 63—Operating Limits for Boilers and...

  1. 40 CFR Table 2 to Subpart Ddddd of... - Operating Limits for Boilers and Process Heaters With Particulate Matter Emission Limits

    Code of Federal Regulations, 2011 CFR

    2011-07-01

    ... 40 Protection of Environment 13 2011-07-01 2011-07-01 false Operating Limits for Boilers and... Hazardous Air Pollutants for Industrial, Commercial, and Institutional Boilers and Process Heaters Pt. 63, Subpt. DDDDD, Table 2 Table 2 to Subpart DDDDD of Part 63—Operating Limits for Boilers and...

  2. 40 CFR 76.8 - Early election for Group 1, Phase II boilers.

    Code of Federal Regulations, 2010 CFR

    2010-07-01

    ... 40 Protection of Environment 16 2010-07-01 2010-07-01 false Early election for Group 1, Phase II boilers. 76.8 Section 76.8 Protection of Environment ENVIRONMENTAL PROTECTION AGENCY (CONTINUED) AIR PROGRAMS (CONTINUED) ACID RAIN NITROGEN OXIDES EMISSION REDUCTION PROGRAM § 76.8 Early election for Group 1, Phase II boilers. (a) General...

  3. 40 CFR 76.5 - NOX emission limitations for Group 1 boilers.

    Code of Federal Regulations, 2010 CFR

    2010-07-01

    ... 40 Protection of Environment 16 2010-07-01 2010-07-01 false NOX emission limitations for Group 1 boilers. 76.5 Section 76.5 Protection of Environment ENVIRONMENTAL PROTECTION AGENCY (CONTINUED) AIR PROGRAMS (CONTINUED) ACID RAIN NITROGEN OXIDES EMISSION REDUCTION PROGRAM § 76.5 NOX emission limitations for Group 1 boilers. (a) Beginning January...

  4. 40 CFR 76.6 - NOX emission limitations for Group 2 boilers.

    Code of Federal Regulations, 2010 CFR

    2010-07-01

    ... 40 Protection of Environment 16 2010-07-01 2010-07-01 false NOX emission limitations for Group 2 boilers. 76.6 Section 76.6 Protection of Environment ENVIRONMENTAL PROTECTION AGENCY (CONTINUED) AIR PROGRAMS (CONTINUED) ACID RAIN NITROGEN OXIDES EMISSION REDUCTION PROGRAM § 76.6 NOX emission limitations for Group 2 boilers. (a) Beginning January...

  5. Optimising boiler performance.

    PubMed

    Mayoh, Paul

    2009-01-01

    Soaring fuel costs continue to put the squeeze on already tight health service budgets. Yet it is estimated that combining established good practice with improved technologies could save between 10% and 30% of fuel costs for boilers. Paul Mayoh, UK technical manager at Spirax Sarco, examines some of the practical measures that healthcare organisations can take to gain their share of these potential savings. PMID:19192603

  6. Development of Computational Capabilities to Predict the Corrosion Wastage of Boiler Tubes in Advanced Combustion Systems

    SciTech Connect

    Kung, Steven; Rapp, Robert

    2014-08-31

    A comprehensive corrosion research project consisting of pilot-scale combustion testing and long-term laboratory corrosion study has been successfully performed. A pilot-scale combustion facility available at Brigham Young University was selected and modified to enable burning of pulverized coals under the operating conditions typical for advanced coal-fired utility boilers. Eight United States (U.S.) coals were selected for this investigation, with the test conditions for all coals set to have the same heat input to the combustor. In addition, the air/fuel stoichiometric ratio was controlled so that staged combustion was established, with the stoichiometric ratio maintained at 0.85 in the burner zone and 1.15 in the burnout zone. The burner zone represented the lower furnace of utility boilers, while the burnout zone mimicked the upper furnace areas adjacent to the superheaters and reheaters. From this staged combustion, approximately 3% excess oxygen was attained in the combustion gas at the furnace outlet. During each of the pilot-scale combustion tests, extensive online measurements of the flue gas compositions were performed. In addition, deposit samples were collected at the same location for chemical analyses. Such extensive gas and deposit analyses enabled detailed characterization of the actual combustion environments existing at the lower furnace walls under reducing conditions and those adjacent to the superheaters and reheaters under oxidizing conditions in advanced U.S. coal-fired utility boilers. The gas and deposit compositions were then carefully simulated in a series of 1000-hour laboratory corrosion tests, in which the corrosion performances of different commercial candidate alloys and weld overlays were evaluated at various temperatures for advanced boiler systems. Results of this laboratory study led to significant improvement in understanding of the corrosion mechanisms operating on the furnace walls as well as superheaters and reheaters in

  7. Super Boiler 2nd Generation Technology for Watertube Boilers

    SciTech Connect

    Mr. David Cygan; Dr. Joseph Rabovitser

    2012-03-31

    This report describes Phase I of a proposed two phase project to develop and demonstrate an advanced industrial watertube boiler system with the capability of reaching 94% (HHV) fuel-to-steam efficiency and emissions below 2 ppmv NOx, 2 ppmv CO, and 1 ppmv VOC on natural gas fuel. The boiler design would have the capability to produce >1500 F, >1500 psig superheated steam, burn multiple fuels, and will be 50% smaller/lighter than currently available watertube boilers of similar capacity. This project is built upon the successful Super Boiler project at GTI. In that project that employed a unique two-staged intercooled combustion system and an innovative heat recovery system to reduce NOx to below 5 ppmv and demonstrated fuel-to-steam efficiency of 94% (HHV). This project was carried out under the leadership of GTI with project partners Cleaver-Brooks, Inc., Nebraska Boiler, a Division of Cleaver-Brooks, and Media and Process Technology Inc., and project advisors Georgia Institute of Technology, Alstom Power Inc., Pacific Northwest National Laboratory and Oak Ridge National Laboratory. Phase I of efforts focused on developing 2nd generation boiler concepts and performance modeling; incorporating multi-fuel (natural gas and oil) capabilities; assessing heat recovery, heat transfer and steam superheating approaches; and developing the overall conceptual engineering boiler design. Based on our analysis, the 2nd generation Industrial Watertube Boiler when developed and commercialized, could potentially save 265 trillion Btu and $1.6 billion in fuel costs across U.S. industry through increased efficiency. Its ultra-clean combustion could eliminate 57,000 tons of NOx, 460,000 tons of CO, and 8.8 million tons of CO2 annually from the atmosphere. Reduction in boiler size will bring cost-effective package boilers into a size range previously dominated by more expensive field-erected boilers, benefiting manufacturers and end users through lower capital costs.

  8. Fuel sulfur and boiler fouling

    SciTech Connect

    Litzke, W.; Celebi, Y.; Butcher, T.

    1995-04-01

    Fouling of the heat transfer surfaces of boilers and furnaces by `soot` leads to reduced efficiency and increased service requirements. The average level of annual efficiency reduction as a result of fouling if generally accepted as 2% per year. Improving the efficiency of equipment in the field may be the most important oil heat conservation opportunity at present. Improvements can be realized by reducing fouling rates, promoting lower firing rates in existing equipment, and enabling excess air levels to be set lower without raising concerns about increased service requirements. In spite of the importance of efficiency in the field there is very little data available on efficiency degradation rates with modern equipment, actual field operating conditions (excess air and smoke number settings) and service problems which affect efficiency. During 1993-94 field tests were initiated to obtain such data and to obtain information that would compliment existing and current laboratory work. Experimental work conducted on a bench scale level have included tests with various advanced burners, fuel types, and different operating conditions which have been done at the BNL Rapid Fouling Test Facility. This report will focus on the field study of fouling effects on ten residential heating service problems at each site are summarized. In addition, the technical difficulties involved with conducting such a field study shall also be discussed as the findings should serve to improve future work in this area.

  9. [Actual problems of the impact of production and management of industrial waste on the environment and public health (review of literature)].

    PubMed

    Cherniaeva, T K

    2013-01-01

    In the modern society the importance and applicability of the problem concerning the negative effect of production and consumption waste on the objects of the environment and the state sa people's health is related to their daily emergency, large tonnage, storage, and utilization. Wastes and places of their storage and waste burial constitute an toxicological and epidemiological risk. Chemical and biological contamination of solid waste is a threat to its penetration into the soil, air, groundwater and surface water bodies, vegetation, directly or indirectly, cause variations in health status of the population. PMID:24340576

  10. Interior view of boiler house looking north. Boiler units are ...

    Library of Congress Historic Buildings Survey, Historic Engineering Record, Historic Landscapes Survey

    Interior view of boiler house looking north. Boiler units are on right. HAER Engineer/Historian Donald C. Jackson on right is interviewing Garry Dobbins concerning operation of the facility. - Burnsville Natural Gas Pumping Station, Saratoga Avenue between Little Kanawha River & C&O Railroad line, Burnsville, Braxton County, WV

  11. Small boiler uses waste coal

    SciTech Connect

    Virr, M.J.

    2009-07-15

    Burning coal waste in small boilers at low emissions poses considerable problem. While larger boiler suppliers have successfully installed designs in the 40 to 80 MW range for some years, the author has been developing small automated fluid bed boiler plants for 25 years that can be applied in the range of 10,000 to 140,000 lbs/hr of steam. Development has centered on the use of an internally circulating fluid bed (CFB) boiler, which will burn waste fuels of most types. The boiler is based on the traditional D-shaped watertable boiler, with a new type of combustion chamber that enables a three-to-one turndown to be achieved. The boilers have all the advantages of low emissions of the large fluid boilers while offering a much lower height incorporated into the package boiler concept. Recent tests with a waste coal that had a high nitrogen content of 1.45% demonstrated a NOx emission below the federal limit of 0.6 lbs/mm Btu. Thus a NOx reduction on the order of 85% can be demonstrate by combustion modification alone. Further reductions can be made by using a selective non-catalytic reduction (SNCR) system and sulfur absorption of up to 90% retention is possible. The article describes the operation of a 30,000 lbs/hr boiler at the Fayette Thermal LLC plant. Spinheat has installed three ICFB boilers at a nursing home and a prison, which has been tested on poor-grade anthracite and bituminous coal. 2 figs.

  12. Virtual and Actual: Relative Accuracy of On-Site and Web-based Instruments in Auditing the Environment for Physical Activity

    PubMed Central

    Ben-Joseph, Eran; Lee, Jae Seung; Cromley, Ellen K.; Laden, Francine; Troped, Philip J.

    2015-01-01

    Objectives To assess the relative accuracy and usefulness of web tools in evaluating and measuring street-scale built environment characteristics. Methods A well-known audit tool was used to evaluate 84 street segments at the urban edge of metropolitan Boston, Massachusetts, using on-site visits and three web-based tools. The assessments were compared to evaluate their relative accuracy and usefulness. Results Web-based audits, based-on Google Maps, Google Street View, and MS Visual Oblique, tend to strongly agree with on-site audits on land-use and transportation characteristics (e.g., types of buildings, commercial destinations, and streets). However, the two approaches to conducting audits (web versus on-site) tend to agree only weakly on fine-grain, temporal, and qualitative environmental elements. Among the web tools used, auditors rated MS Visual Oblique as the most valuable. Yet Street View tends to be rated as the most useful in measuring fine-grain features, such as levelness and condition of sidewalks. Conclusion While web-based tools do not offer a perfect substitute for on-site audits, they allow for preliminary audits to be performed accurately from remote locations, potentially saving time and cost and increasing the effectiveness of subsequent on-site visits. PMID:23247423

  13. Examining the relationships between acculturation orientations, perceived and actual norms, and drinking behaviors of short-term american sojourners in foreign environments.

    PubMed

    Pedersen, Eric R; Cruz, Rick A; Labrie, Joseph W; Hummer, Justin F

    2011-12-01

    As little research has examined factors influencing increased and heavy drinking behavior among American sojourners abroad, this study was designed to examine how acculturation orientations (i.e., separation versus assimilation), host country per capita drinking rates, and perceptions about the drinking behavior among other sojourners and natives in the host country predicted alcohol risk abroad. A sample of 216 American college students completing study abroad programs completed a pre-abroad questionnaire to document their pre-abroad drinking levels, followed by a post-return questionnaire to assess drinking while abroad, acculturation orientations and perceived norms of drinking behavior within the foreign environment. A dichotomous variable was created to compare United States (U.S.) per capita drinking rates with those of the host country. Hierarchical repeated-measures ANOVAs examined the changes in drinking from pre-abroad to abroad levels. Participants studying in countries with higher drinking rates than the U.S. and those with higher perceptions about the drinking behavior in the country increased their drinking to a greater extent. Those with higher separation acculturation orientations and greater perceptions drank at heavier levels while abroad. Participants with a greater assimilation orientation and higher perceptions about native drinking, as well as those with a greater separation orientation and higher perceptions about other students' alcohol use drank the heaviest while abroad. These findings have implications for future preventive work with American students and other sojourning groups to promote pre-abroad knowledge of more accurate drinking norms and greater engagement in the culture to potentially prevent increased and heavier drinking. PMID:21720781

  14. Examining the Relationships Between Acculturation Orientations, Perceived and Actual Norms, and Drinking Behaviors of Short-Term American Sojourners in Foreign Environments

    PubMed Central

    Cruz, Rick A.; LaBrie, Joseph W.; Hummer, Justin F.

    2013-01-01

    As little research has examined factors influencing increased and heavy drinking behavior among American sojourners abroad, this study was designed to examine how acculturation orientations (i.e., separation versus assimilation), host country per capita drinking rates, and perceptions about the drinking behavior among other sojourners and natives in the host country predicted alcohol risk abroad. A sample of 216 American college students completing study abroad programs completed a pre-abroad questionnaire to document their pre-abroad drinking levels, followed by a post-return questionnaire to assess drinking while abroad, acculturation orientations and perceived norms of drinking behavior within the foreign environment. A dichotomous variable was created to compare United States (U.S.) per capita drinking rates with those of the host country. Hierarchical repeated-measures ANOVAs examined the changes in drinking from pre-abroad to abroad levels. Participants studying in countries with higher drinking rates than the U.S. and those with higher perceptions about the drinking behavior in the country increased their drinking to a greater extent. Those with higher separation acculturation orientations and greater perceptions drank at heavier levels while abroad. Participants with a greater assimilation orientation and higher perceptions about native drinking, as well as those with a greater separation orientation and higher perceptions about other students’ alcohol use drank the heaviest while abroad. These findings have implications for future preventive work with American students and other sojourning groups to promote pre-abroad knowledge of more accurate drinking norms and greater engagement in the culture to potentially prevent increased and heavier drinking. PMID:21720781

  15. Slag monitoring system for combustion chambers of steam boilers

    SciTech Connect

    Taler, J.; Taler, D.

    2009-07-01

    The computer-based boiler performance system presented in this article has been developed to provide a direct and quantitative assessment of furnace and convective surface cleanliness. Temperature, pressure, and flow measurements and gas analysis data are used to perform heat transfer analysis in the boiler furnace and evaporator. Power boiler efficiency is calculated using an indirect method. The on-line calculation of the exit flue gas temperature in a combustion chamber allows for an on-line heat flow rate determination, which is transferred to the boiler evaporator. Based on the energy balance for the boiler evaporator, the superheated steam mass flow rate is calculated taking into the account water flow rate in attemperators. Comparing the calculated and the measured superheated steam mass flow rate, the effectiveness of the combustion chamber water walls is determined in an on-line mode. Soot-blower sequencing can be optimized based on actual cleaning requirements rather than on fixed time cycles contributing to lowering of the medium usage in soot blowers and increasing of the water-wall lifetime.

  16. [Emission characteristics of fine particles from grate firing boilers].

    PubMed

    Wang, Shu-Xiao; Zhao, Xiu-Juan; Li, Xing-Hua; Wei, Wei; Hao, Ji-Ming

    2009-04-15

    Grate firing boilers are the main type of Chinese industrial boilers, which accounts for 85% of the industrial boilers and is one of the most important emission sources of primary air pollutants in China. In this study, five boilers in three cities were selected and tested to measure the emission characteristics of PM2.5, and gaseous pollutants were applied by a compact dilution sampling system, which was developed for this field study. Results showed that particles mass size distributions for the five industrial boilers presented single peak or double peak, former peaks near 0.14 microm and the later peaks after 1.0 microm; the cyclone dust remover and wet scrubber dust remover had effective removal efficiencies not only to PM2.5, but also to PM1.0; and under the condition of same control techniques, grate firing boiler with high capacity has less PM2.5 emission than the boiler with low capacity. In the PM2.5 collected from flue gases, SO4(2-) was the most abundant ion, accounted for 20%-40% of the PM2.5; and C was the most abundant element (7.5%-31.8%), followed by S (8.4%-18.7%). Carbon balance method was applied to calculate the emission factors of these pollutants. The emission factors of PM2.5, NO, and SO2 were in the range of 0.046-0.486 g x kg(-1), 1.63-2.47 g x kg(-1), 1.35-9.95 g x kg(-1) respectively. The results are useful for the emission inventory development of industrial boilers and the source analysis of PM2.5 in atmospheric environment. PMID:19544990

  17. 40 CFR 260.32 - Variances to be classified as a boiler.

    Code of Federal Regulations, 2011 CFR

    2011-07-01

    ... 40 Protection of Environment 26 2011-07-01 2011-07-01 false Variances to be classified as a boiler... be classified as a boiler. In accordance with the standards and criteria in § 260.10 (definition of “boiler”), and the procedures in § 260.33, the Administrator may determine on a case-by-case basis...

  18. 40 CFR 260.32 - Variances to be classified as a boiler.

    Code of Federal Regulations, 2014 CFR

    2014-07-01

    ... 40 Protection of Environment 26 2014-07-01 2014-07-01 false Variances to be classified as a boiler... be classified as a boiler. In accordance with the standards and criteria in § 260.10 (definition of “boiler”), and the procedures in § 260.33, the Administrator may determine on a case-by-case basis...

  19. 40 CFR 260.32 - Variances to be classified as a boiler.

    Code of Federal Regulations, 2010 CFR

    2010-07-01

    ... 40 Protection of Environment 25 2010-07-01 2010-07-01 false Variances to be classified as a boiler... be classified as a boiler. In accordance with the standards and criteria in § 260.10 (definition of “boiler”), and the procedures in § 260.33, the Administrator may determine on a case-by-case basis...

  20. 40 CFR 260.32 - Variances to be classified as a boiler.

    Code of Federal Regulations, 2012 CFR

    2012-07-01

    ... 40 Protection of Environment 27 2012-07-01 2012-07-01 false Variances to be classified as a boiler... be classified as a boiler. In accordance with the standards and criteria in § 260.10 (definition of “boiler”), and the procedures in § 260.33, the Administrator may determine on a case-by-case basis...

  1. 40 CFR 260.32 - Variances to be classified as a boiler.

    Code of Federal Regulations, 2013 CFR

    2013-07-01

    ... 40 Protection of Environment 27 2013-07-01 2013-07-01 false Variances to be classified as a boiler... be classified as a boiler. In accordance with the standards and criteria in § 260.10 (definition of “boiler”), and the procedures in § 260.33, the Administrator may determine on a case-by-case basis...

  2. Mining wavelet transformed boiler data sets

    NASA Astrophysics Data System (ADS)

    Letsche, Terry Lee

    Accurate combustion models provide information that allows increased boiler efficiency optimization, saving money and resources while reducing waste. Boiler combustion processes are noted for being complex, nonstationary and nonlinear. While numerous methods have been used to model boiler processes, data driven approaches reflect actual operating conditions within a particular boiler and do not depend on idealized, complex, or expensive empirical models. Boiler and combustion processes vary in time, requiring a denoising technique that preserves the temporal and frequency nature of the data. Moving average, a common technique, smoothes data---low frequency noise is not removed. This dissertation examines models built with wavelet denoising techniques that remove low and high frequency noise in both time and frequency domains. The denoising process has a number of parameters, including choice of wavelet, threshold value, level of wavelet decomposition, and disposition of attributes that appear to be significant at multiple thresholds. A process is developed to experimentally evaluate the predictive accuracy of these models and compares this result against two benchmarks. The first research hypothesis compares the performance of these wavelet denoised models to the model generated from the original data. The second research hypothesis compares the performance of the models generated with this denoising approach to the most effective model generated from a moving average process. In both experiments it was determined that the Daubechies 4 wavelet was a better choice than the more typically chosen Haar wavelet, wavelet packet decomposition outperforms other levels of wavelet decomposition, and discarding all but the lowest threshold repeating attributes produces superior results. The third research hypothesis examined using a two-dimensional wavelet transform on the data. Another parameter for handling the boundary condition was introduced. In the two-dimensional case

  3. Design and research of retrofitting PC boiler into CFB boiler

    SciTech Connect

    Chen, H.P.; Lu, J.D.; Huang, L.; Liu, H.; Lin, Z.; Liu, D.C.

    1997-12-31

    In China, there are a large number of aged pulverized coal (PC) boilers at aging utility power plants. Many of them are beyond their reasonable working life or in a condition of unreliable operation, low combustion efficiency, and serious air pollution. It is very important and urgent to retrofit the aged PC boilers, and repower the aging utility power plants in China. Circulating fluidized bed (CFB) boilers have been developed rapidly, and paid great attention to in China. There are many striking advantages to retrofit an aged boiler with a CFB boiler. The retrofitting is suitable to meet the needs of effective utilization of low-grade coal, reducing SO{sub 2} and NO{sub x} emissions and repowering an aging power plant. The cost is much lower than that of building a new CFB unit. The National Laboratory of Coal Combustion (NLCC) has always paid great attention to studying and developing CFB combustion technology in connection with Chinese national conditions, and has evolved distinguishing technology features of its own. This paper introduces a new design concept of retrofitting PC boiler into Pi ({Pi}-shaped) CFB boiler with downward exhaust cyclone, and relevant research work and results of design and calculation.

  4. Evaluation of iron aluminide weld overlays for erosion - corrosion resistant boiler tube coatings in low NO{sub x} boilers

    SciTech Connect

    DuPont, J.N.; Banovic, S.W.; Marder, A.R.

    1996-08-01

    Low NOx burners are being installed in many fossil fired power plants in order to comply with new Clean Air Regulations. Due to the operating characteristics of these burners, boiler tube sulfidation corrosion is often enhanced and premature tube failures can occur. Failures due to oxidation and solid particle erosion are also a concern. A program was initiated in early 1996 to evaluate the use of iron aluminide weld overlays for erosion/corrosion protection of boiler tubes in Low NOx boilers. Composite iron/aluminum wires will be used with the Gas Metal Arc Welding (GMAW) process to prepare overlays on boiler tubes steels with aluminum contents from 8 to 16wt%. The weldability of the composite wires will be evaluated as a function of chemical composition and welding parameters. The effect of overlay composition on corrosion (oxidation and sulfidation) and solid particle erosion will also be evaluated. The laboratory studies will be complemented by field exposures of both iron aluminide weld overlays and co-extruded tubing under actual boiler conditions.

  5. 49 CFR 230.47 - Boiler number.

    Code of Federal Regulations, 2012 CFR

    2012-10-01

    ... 49 Transportation 4 2012-10-01 2012-10-01 false Boiler number. 230.47 Section 230.47..., DEPARTMENT OF TRANSPORTATION STEAM LOCOMOTIVE INSPECTION AND MAINTENANCE STANDARDS Boilers and Appurtenances Steam Gauges § 230.47 Boiler number. (a) Generally. The builder's number of the boiler, if known,...

  6. 49 CFR 230.47 - Boiler number.

    Code of Federal Regulations, 2013 CFR

    2013-10-01

    ... 49 Transportation 4 2013-10-01 2013-10-01 false Boiler number. 230.47 Section 230.47..., DEPARTMENT OF TRANSPORTATION STEAM LOCOMOTIVE INSPECTION AND MAINTENANCE STANDARDS Boilers and Appurtenances Steam Gauges § 230.47 Boiler number. (a) Generally. The builder's number of the boiler, if known,...

  7. 49 CFR 230.47 - Boiler number.

    Code of Federal Regulations, 2014 CFR

    2014-10-01

    ... 49 Transportation 4 2014-10-01 2014-10-01 false Boiler number. 230.47 Section 230.47..., DEPARTMENT OF TRANSPORTATION STEAM LOCOMOTIVE INSPECTION AND MAINTENANCE STANDARDS Boilers and Appurtenances Steam Gauges § 230.47 Boiler number. (a) Generally. The builder's number of the boiler, if known,...

  8. 30 CFR 77.413 - Boilers.

    Code of Federal Regulations, 2012 CFR

    2012-07-01

    ... 30 Mineral Resources 1 2012-07-01 2012-07-01 false Boilers. 77.413 Section 77.413 Mineral... Mechanical Equipment § 77.413 Boilers. (a) Boilers shall be equipped with guarded, well-maintained water... the gages shall be kept clean and free of scale and rust. (b) Boilers shall be equipped with...

  9. 49 CFR 230.47 - Boiler number.

    Code of Federal Regulations, 2010 CFR

    2010-10-01

    ... 49 Transportation 4 2010-10-01 2010-10-01 false Boiler number. 230.47 Section 230.47..., DEPARTMENT OF TRANSPORTATION STEAM LOCOMOTIVE INSPECTION AND MAINTENANCE STANDARDS Boilers and Appurtenances Steam Gauges § 230.47 Boiler number. (a) Generally. The builder's number of the boiler, if known,...

  10. 30 CFR 77.413 - Boilers.

    Code of Federal Regulations, 2011 CFR

    2011-07-01

    ... 30 Mineral Resources 1 2011-07-01 2011-07-01 false Boilers. 77.413 Section 77.413 Mineral... Mechanical Equipment § 77.413 Boilers. (a) Boilers shall be equipped with guarded, well-maintained water... the gages shall be kept clean and free of scale and rust. (b) Boilers shall be equipped with...

  11. 30 CFR 77.413 - Boilers.

    Code of Federal Regulations, 2013 CFR

    2013-07-01

    ... 30 Mineral Resources 1 2013-07-01 2013-07-01 false Boilers. 77.413 Section 77.413 Mineral... Mechanical Equipment § 77.413 Boilers. (a) Boilers shall be equipped with guarded, well-maintained water... the gages shall be kept clean and free of scale and rust. (b) Boilers shall be equipped with...

  12. 30 CFR 77.413 - Boilers.

    Code of Federal Regulations, 2010 CFR

    2010-07-01

    ... 30 Mineral Resources 1 2010-07-01 2010-07-01 false Boilers. 77.413 Section 77.413 Mineral... Mechanical Equipment § 77.413 Boilers. (a) Boilers shall be equipped with guarded, well-maintained water... the gages shall be kept clean and free of scale and rust. (b) Boilers shall be equipped with...

  13. 49 CFR 230.47 - Boiler number.

    Code of Federal Regulations, 2011 CFR

    2011-10-01

    ... 49 Transportation 4 2011-10-01 2011-10-01 false Boiler number. 230.47 Section 230.47..., DEPARTMENT OF TRANSPORTATION STEAM LOCOMOTIVE INSPECTION AND MAINTENANCE STANDARDS Boilers and Appurtenances Steam Gauges § 230.47 Boiler number. (a) Generally. The builder's number of the boiler, if known,...

  14. 30 CFR 77.413 - Boilers.

    Code of Federal Regulations, 2014 CFR

    2014-07-01

    ... 30 Mineral Resources 1 2014-07-01 2014-07-01 false Boilers. 77.413 Section 77.413 Mineral... Mechanical Equipment § 77.413 Boilers. (a) Boilers shall be equipped with guarded, well-maintained water... the gages shall be kept clean and free of scale and rust. (b) Boilers shall be equipped with...

  15. High-performance nanoscale composite coatings for boiler applications

    NASA Astrophysics Data System (ADS)

    Branagan, D. J.; Breitsameter, M.; Meacham, B. E.; Belashchenko, V.

    2005-06-01

    In this article, we will show how unconventional nanoscale composite coatings can be formed using conventional wire-arc thermal spray systems. The as-sprayed SHS7170 wire-arc coatings are found to develop an amorphous matrix structure containing starburst-shaped boride and carbide crystallites with sizes ranging from 60 to 140 nm. After heating to temperatures above the peak crystalline temperature (566 °C), a solid/state transformation occurs that results in the formation of an intimate three-phase matrix structure consisting of the same complex boride and carbide phases, along with α-iron interdispersed on a structural scale from 60 to 110 nm. The nanocomposite microstructure contains clean grain boundaries, which are found to be extremely stable and resist coarsening throughout the range of temperatures found in boilers. Additionally, the properties of the coating are presented including the bond strength, hardness, bend resistance, and impact resistance. The sprayability, forgiveness, and repairability of the SHS7170 wire-arc coatings are explained in detail, with an emphasis on field applicability in boiler environments. The performance of the SHS7170 coatings in boiler environments is measured via elevated temperature-erosion experiments conducted at 300, 450, and 600 °C using bed ash from an operating circulating fluidized-bed combustor boiler, and the results are compared with those for existing boiler coatings.

  16. 40 CFR 270.235 - Options for incinerators, cement kilns, lightweight aggregate kilns, solid fuel boilers, liquid...

    Code of Federal Regulations, 2013 CFR

    2013-07-01

    ... 40 Protection of Environment 28 2013-07-01 2013-07-01 false Options for incinerators, cement kilns, lightweight aggregate kilns, solid fuel boilers, liquid fuel boilers and hydrochloric acid production furnaces to minimize emissions from startup, shutdown, and malfunction events. 270.235 Section 270.235 Protection of Environment...

  17. Boiler Tube Corrosion Characterization with a Scanning Thermal Line

    NASA Technical Reports Server (NTRS)

    Cramer, K. Elliott; Jacobstein, Ronald; Reilly, Thomas

    2001-01-01

    Wall thinning due to corrosion in utility boiler water wall tubing is a significant operational concern for boiler operators. Historically, conventional ultrasonics has been used for inspection of these tubes. Unfortunately, ultrasonic inspection is very manpower intense and slow. Therefore, thickness measurements are typically taken over a relatively small percentage of the total boiler wall and statistical analysis is used to determine the overall condition of the boiler tubing. Other inspection techniques, such as electromagnetic acoustic transducer (EMAT), have recently been evaluated, however they provide only a qualitative evaluation - identifying areas or spots where corrosion has significantly reduced the wall thickness. NASA Langley Research Center, in cooperation with ThermTech Services, has developed a thermal NDE technique designed to quantitatively measure the wall thickness and thus determine the amount of material thinning present in steel boiler tubing. The technique involves the movement of a thermal line source across the outer surface of the tubing followed by an infrared imager at a fixed distance behind the line source. Quantitative images of the material loss due to corrosion are reconstructed from measurements of the induced surface temperature variations. This paper will present a discussion of the development of the thermal imaging system as well as the techniques used to reconstruct images of flaws. The application of the thermal line source coupled with the analysis technique represents a significant improvement in the inspection speed and accuracy for large structures such as boiler water walls. A theoretical basis for the technique will be presented to establish the quantitative nature of the technique. Further, a dynamic calibration system will be presented for the technique that allows the extraction of thickness information from the temperature data. Additionally, the results of the application of this technology to actual water wall

  18. Chemical corrosion potential in boilers

    SciTech Connect

    Bairr, D.L.; McDonough, C.J.

    1998-12-31

    Misuse or abuse of chelants has long been recognized as a potential corrosion problem in boilers. In recent years all polymer chemical treatment programs have been introduced and although they are much more benign even all polymer programs must be properly designed and controlled. Under extreme conditions a similar corrosion potential exists. This paper discusses the potential for chelant or polymer corrosion in boilers and the proper safeguards. Case histories are presented.

  19. Boiler-turbine life extension

    SciTech Connect

    Natzkov, S.; Nikolov, M.

    1995-12-01

    The design life of the main power equipment-boilers and turbines is about 105 working hours. The possibilities for life extension are after normatively regulated control tests. The diagnostics and methodology for Boilers and Turbines Elements Remaining Life Assessment using up to date computer programs, destructive and nondestructive control of metal of key elements of units equipment, metal creep and low cycle fatigue calculations. As well as data for most common damages and some technical decisions for elements life extension are presented.

  20. CFB boiler at Gardanne (France)

    SciTech Connect

    Jaud, P.; Jacquet, L.; Delot, P.; Bayle, F.

    1995-06-01

    Among the new Clean Coal Technologies, {open_quotes}Circulating Fluidized Bed{close_quotes} is one of the most promising. Today, the largest project in commissioning`s the 250 MWe Provence CFB boiler, located near MARSEILLE in the south of France. At such a size, the CFB technique has now reached a capacity corresponding to thermal power plants operated by utilities. This new unit is a very important step towards larger size i.e. 400 MWe and greater. The SO{sub 2} emissions of this CFB boiler are guaranteed to be less than 400 mg / Nm{sup 3} at 6% O{sub 2} with the ratio of Ca/S lower than 3 while total sulfur in local coal used can reach 3.68 %. The purpose of the Provence project was to replace the existing pulverized coal boiler unit 4, commissioned in 1967, of the Provence power plant, with a new CFB boiler while reusing most of the existing equipment. The new boiler has been ordered from GEC ALSTHOM STEIN INDUSTREE (GASI) by Electricite de France (EDF) on behalf of the SOPROLIF consortium. Architect Engineering and construction management was performed by EDF jointly with Charbonnages de France (CdF: the French Coal Board). The 250 MWe CFB boiler is of the superheat-reheat type. The first firing of the boiler is due in April 1995. The poster session will describe the progress in the construction of the plant and provides technical details of the new boiler and auxiliaries.

  1. The Self Actualized Reader.

    ERIC Educational Resources Information Center

    Marino, Michael; Moylan, Mary Elizabeth

    A study examined the commonalities that "voracious" readers share, and how their experiences can guide parents, teachers, and librarians in assisting children to become self-actualized readers. Subjects, 25 adults ranging in age from 20 to 67 years, completed a questionnaire concerning their reading histories and habits. Respondents varied in…

  2. Ultra-Supercritical Pressure CFB Boiler Conceptual Design Study

    SciTech Connect

    Zhen Fan; Steve Goidich; Archie Robertson; Song Wu

    2006-06-30

    Electric utility interest in supercritical pressure steam cycles has revived in the United States after waning in the 1980s. Since supercritical cycles yield higher plant efficiencies than subcritical plants along with a proportional reduction in traditional stack gas pollutants and CO{sub 2} release rates, the interest is to pursue even more advanced steam conditions. The advantages of supercritical (SC) and ultra supercritical (USC) pressure steam conditions have been demonstrated in the high gas temperature, high heat flux environment of large pulverized coal-fired (PC) boilers. Interest in circulating fluidized bed (CFB) combustion, as an alternative to PC combustion, has been steadily increasing. Although CFB boilers as large as 300 MWe are now in operation, they are drum type, subcritical pressure units. With their sizes being much smaller than and their combustion temperatures much lower than those of PC boilers (300 MWe versus 1,000 MWe and 1600 F versus 3500 F), a conceptual design study was conducted herein to investigate the technical feasibility and economics of USC CFB boilers. The conceptual study was conducted at 400 MWe and 800 MWe nominal plant sizes with high sulfur Illinois No. 6 coal used as the fuel. The USC CFB plants had higher heating value efficiencies of 40.6 and 41.3 percent respectively and their CFB boilers, which reflect conventional design practices, can be built without the need for an R&D effort. Assuming construction at a generic Ohio River Valley site with union labor, total plant costs in January 2006 dollars were estimated to be $1,551/kW and $1,244/kW with costs of electricity of $52.21/MWhr and $44.08/MWhr, respectively. Based on the above, this study has shown that large USC CFB boilers are feasible and that they can operate with performance and costs that are competitive with comparable USC PC boilers.

  3. Design and Application of Novel Horizontal Circulating Fluidized Bed Boiler

    NASA Astrophysics Data System (ADS)

    Lit, Q. H.; Zhang, Y. G.; Meng, A. H.

    The vertical circulating fluidized bed (CFB) boiler has been found wide application in power generation and tends to be enlarged in capacity. Because CFB is one of environment friendly and high efficiency combustion technologies, the CFB boiler has also been expected to be used in the industrial area, such as textile mill, region heating, brewery, seed drying and so on. However, the necessary height of furnace is hard to be implemented for CFB with especially small capacity. Thereby, a novel horizontal circulating fluidized bed boiler has been proposed and developed. The horizontal CFB is composed of primary combustion chamber, secondary combustion chamber, burnout chamber, cyclone, loop seal, heat recovery area. The primary combustion chamber is a riser like as that in vertical CFB, and the secondary combustion chamber is a downward passage that is a natural extension of the primary riser, which can reduce the overall height of the boiler. In some extent, the burnout chamber is also the extension of primary riser. The capacity of horizontal CFB is about 4.2-24.5MWth (6-35t/h) steam output or equivalent hot water supply. The hot water boiler of 7MWth and steam boilers of 4.2MWth (6t/h) and 10.5MWth (15t/h) are all designed and working well now. The three units of hot water horizontal CFB boiler were erected in the Neimenggu Autonomous Region, Huhehaote city for region heating. The three units of steam horizontal CFB has been installed in Yunnan, Jiang Xi and Guangdong provinces, respectively. The basic principle for horizontal CFB and experiences for designing and operating are presented in this paper. Some discussions are also given to demonstrate the promising future of horizontal CFB.

  4. Computational Modeling and Assessment Of Nanocoatings for Ultra Supercritical Boilers

    SciTech Connect

    Gandy, David W.; Shingledecker, John P.

    2011-05-11

    Coal-fired power plants are a significant part of the nation's power generating capacity, currently accounting for more than 55% of the country's total electricity production. Extending the reliable lifetimes of fossil fired boiler components and reducing the maintenance costs are essential for economic operation of power plants. Corrosion and erosion are leading causes of superheater and reheater boiler tube failures leading to unscheduled costly outages. Several types of coatings and weld overlays have been used to extend the service life of boiler tubes; however, the protection afforded by such materials was limited approximately one to eight years. Power companies are more recently focused in achieving greater plant efficiency by increasing steam temperature and pressure into the advanced-ultrasupercritical (A-USC) condition with steam temperatures approaching 760°C (1400°F) and operating pressures in excess of 35MPa (5075 psig). Unfortunately, laboratory and field testing suggests that the resultant fireside environment when operating under A-USC conditions can potentially cause significant corrosion to conventional and advanced boiler materials1-2. In order to improve reliability and availability of fossil fired A-USC boilers, it is essential to develop advanced nanostructured coatings that provide excellent corrosion and erosion resistance without adversely affecting the other properties such as toughness and thermal fatigue strength of the component material.

  5. Study on Combustion Characteristics of Lignite in a CFB Boiler

    NASA Astrophysics Data System (ADS)

    Leng, J.; Zou, T. S.; Wu, J. X.; Jiang, C.; Gao, J. L.; Wu, J.; Su, D.; Song, D. Y.

    The shortage of coal promotes the lignite utility in power plant because of the rapid economy development recently. However, lignite is high in moisture content as well as volatile content and low in calorific value. It is very difficult to burn in traditional pulverized coal fired boiler. Circulating fluidized bed (CFB) boiler is an alternative with low pollutant emission. Some CFB boilers are built and put into commercial operation in Northeast China and East Inner Mongolia where lignite is abundant. The operation experiences of these boilers are introduced in this paper. The effect of coal particle size on bottom ash ratio, combustion efficiency, thermal efficiency, pollution emission, and ash deposits in convective heating surface were investigated. It was found that for the lignite fired CFB boiler, the largest coal particle size should be 20 to 40mm to maintain bed material balance. But the bottom ash only shares less than 10% of the total ash. Due to high volatile content in the lignite, the combustion efficiency could achieve more than 99%. Meanwhile, NOx emission was relative low and satisfied national environment protection requirement. It is suggested that flue gas velocity in convective heating surface should be ranged in a certain scope to prevent ash deposit and erosion.

  6. Boiler using combustible fluid

    DOEpatents

    Baumgartner, H.; Meier, J.G.

    1974-07-03

    A fluid fuel boiler is described comprising a combustion chamber, a cover on the combustion chamber having an opening for introducing a combustion-supporting gaseous fluid through said openings, means to impart rotation to the gaseous fluid about an axis of the combustion chamber, a burner for introducing a fluid fuel into the chamber mixed with the gaseous fluid for combustion thereof, the cover having a generally frustro-conical configuration diverging from the opening toward the interior of the chamber at an angle of between 15/sup 0/ and 55/sup 0/; means defining said combustion chamber having means defining a plurality of axial hot gas flow paths from a downstream portion of the combustion chamber to flow hot gases into an upstream portion of the combustion chamber, and means for diverting some of the hot gas flow along paths in a direction circumferentially of the combustion chamber, with the latter paths being immersed in the water flow path thereby to improve heat transfer and terminating in a gas outlet, the combustion chamber comprising at least one modular element, joined axially to the frustro-conical cover and coaxial therewith. The modular element comprises an inner ring and means of defining the circumferential, radial, and spiral flow paths of the hot gases.

  7. Controlling boiler emissions

    SciTech Connect

    Katzel, J.

    1992-10-22

    This paper reports that if you are confused about how to interpret the Clean Air Act Amendments of 1990, you are not alone. The massive document runs several hundred pages and consists of 11 titles, each addressing a different aspect of air quality. In some cases, specific emissions levels are established; in others, they are left to the discretion of state and local governments. In many ways, the impact of the CAAA right now is no impact. But now is not the time for plant engineers to play any waiting games. The annual cost of complying with the comprehensive environmental legislation is estimated at $4 to $7 billion. Despite the ambiguity and uncertainty, one conclusion appears clear: control of emissions, especially nitrogen oxides, from all types of boilers and process units can be expected to become more stringent. More and more equipment and industries will fall under the regulations as they are implemented by the Environmental Protection Agency (EPA). An newly available and improved strategies and technologies will make it more and more difficult to circumvent the law. As the general concepts of the legislation are molded into specifics, plant engineers are well advised to take an active role in shaping the attainment and control programs being formed by their state sand in understanding and applying available control technologies.

  8. New controls spark boiler efficiency

    SciTech Connect

    Engels, T. )

    1993-09-01

    Monsanto's NutraSweet plant in University Park, IL, produces aspartame, the patented NutraSweet artificial sweetener product. Until recently, boiler control was managed by a '60s-era Fireye jackshaft system in which air and natural gas were mechanically linked with an offset to compensate for oxygen trim. The interlocking devices on the Fireye system were becoming obsolete, and the boiler needed a new front end retrofitted for low emissions. In order to improve boiler control efficiency, we decided to modernize and automate the entire boiler control system. We replaced the original jackshaft system, and installed a Gordon-Piet burner system, including gas valves, air dampers, blowers, and burner. The upgrade challenges included developing a control strategy and selecting and implementing a process control system. Since our plant has standardized on the PROVOX process management information system from Fisher Controls (now Fisher-Rosemount Systems) to support most of our process, it was a natural and logical choice for boiler controls as well. 2 figs.

  9. Program to Train Boiler Operators Developed

    ERIC Educational Resources Information Center

    Chemical and Engineering News, 1978

    1978-01-01

    This program initiated by Nalco Chemical, a major supplier of chemicals for boiler feedwater treatment, uses texts, audiovisual aids, and hands-on experience and is designed to boost the efficiency of boiler operators. (BB)

  10. Boiler for generating high quality vapor

    NASA Technical Reports Server (NTRS)

    Gray, V. H.; Marto, P. J.; Joslyn, A. W.

    1972-01-01

    Boiler supplies vapor for use in turbines by imparting a high angular velocity to the liquid annulus in heated rotating drum. Drum boiler provides a sharp interface between boiling liquid and vapor, thereby, inhibiting the formation of unwanted liquid droplets.

  11. The potential of pulse-jet baghouses for utility boilers. Part 1: A worldwide survey of users

    SciTech Connect

    Belba, V.H. ); Grubb, W.T. ); Chang, R. )

    1992-02-01

    Pulse-jet fabric filters (PJFFs) are widely used in US industrial boiler applications and in utility and industrial boilers abroad. Their smaller size and reduced cost relative to more conventional baghouses make PJFFs appear to be a particularly attractive particulate control option for utility boilers. This paper summarizes the results of a survey co-funded by the Electric Power Research Institute and Canadian Electric Association to characterize the performance of and operating experiences with PJFFs applied to coal-fired boilers. The survey involved site visits to interview technical and plant personnel involved in the design, installation and day-to-day operation of PJFFs worldwide. Actual field experiences with PJFF performance in terms of outlet emissions, pressure drop and bag life for different types of pulse-jet cleaning methods, fabrics and boilers are compared.

  12. 29 CFR 1915.162 - Ship's boilers.

    Code of Federal Regulations, 2010 CFR

    2010-07-01

    ... Ship's boilers. (a) Before work is performed in the fire, steam, or water spaces of a boiler where employees may be subject to injury from the direct escape of a high temperature medium such as steam, or... employees are working in the boilers shall be hung in a conspicuous location in the engine room. This...

  13. 29 CFR 1915.162 - Ship's boilers.

    Code of Federal Regulations, 2013 CFR

    2013-07-01

    ... Ship's boilers. (a) Before work is performed in the fire, steam, or water spaces of a boiler where employees may be subject to injury from the direct escape of a high temperature medium such as steam, or... that employees are working in the boilers shall be hung in a conspicuous location in the engine...

  14. 29 CFR 1915.162 - Ship's boilers.

    Code of Federal Regulations, 2014 CFR

    2014-07-01

    ... Ship's boilers. (a) Before work is performed in the fire, steam, or water spaces of a boiler where employees may be subject to injury from the direct escape of a high temperature medium such as steam, or... that employees are working in the boilers shall be hung in a conspicuous location in the engine...

  15. 29 CFR 1915.162 - Ship's boilers.

    Code of Federal Regulations, 2011 CFR

    2011-07-01

    ... Ship's boilers. (a) Before work is performed in the fire, steam, or water spaces of a boiler where employees may be subject to injury from the direct escape of a high temperature medium such as steam, or... employees are working in the boilers shall be hung in a conspicuous location in the engine room. This...

  16. 29 CFR 1915.162 - Ship's boilers.

    Code of Federal Regulations, 2012 CFR

    2012-07-01

    ... Ship's boilers. (a) Before work is performed in the fire, steam, or water spaces of a boiler where employees may be subject to injury from the direct escape of a high temperature medium such as steam, or... that employees are working in the boilers shall be hung in a conspicuous location in the engine...

  17. Sootblowing optimization for improved boiler performance

    DOEpatents

    James, John Robert; McDermott, John; Piche, Stephen; Pickard, Fred; Parikh, Neel J

    2013-07-30

    A sootblowing control system that uses predictive models to bridge the gap between sootblower operation and boiler performance goals. The system uses predictive modeling and heuristics (rules) associated with different zones in a boiler to determine an optimal sequence of sootblower operations and achieve boiler performance targets. The system performs the sootblower optimization while observing any operational constraints placed on the sootblowers.

  18. Sootblowing optimization for improved boiler performance

    DOEpatents

    James, John Robert; McDermott, John; Piche, Stephen; Pickard, Fred; Parikh, Neel J.

    2012-12-25

    A sootblowing control system that uses predictive models to bridge the gap between sootblower operation and boiler performance goals. The system uses predictive modeling and heuristics (rules) associated with different zones in a boiler to determine an optimal sequence of sootblower operations and achieve boiler performance targets. The system performs the sootblower optimization while observing any operational constraints placed on the sootblowers.

  19. 30 CFR 57.13030 - Boilers.

    Code of Federal Regulations, 2010 CFR

    2010-07-01

    ... American Society of Mechanical Engineers to protect against hazards from overpressure, flameouts, fuel...) The ASME Boiler and Pressure Vessel Code, 1977, published by the American Society of Mechanical... VIIRecommended Rules for Care of Power Boilers (2) The National Board Inspection Code, a Manual for Boiler...

  20. EVALUATION OF UTILITY BOILER RADIANT FURNACE RESIDENCE TIME/TEMPERATURE CHARACTERISTICS: FIELD TESTS AND HEAT TRANSFER MODELING

    EPA Science Inventory

    The report describes an investigation of the adequacy of a modeling approach in predicting the thermal environment and flow field of pulverized-coal-fired utility boilers. Two 420 MWe coal-fired boilers were evaluated: a single-wall-fired unit and a tangentially fired unit, repre...

  1. Research, Development and Demonstration of Bio-Mass Boiler for Food Industry

    SciTech Connect

    Fisher, Steve; Knapp, David

    2012-07-01

    Frito-Lay is working to reduce carbon emissions from their manufacturing plants. As part of this effort, they invested in a biomass-fired boiler at the Topeka, Kansas, plant. Frito-Lay partnered with Burns & McDonnell Engineering, Inc. and CPL Systems, Inc., to design and construct a steam producing boiler using carbon neutral fuels such as wood wastes (e.g. tree bark), shipping pallets, and used rubber vehicle tires. The U.S. Department of Energy (DOE) joined with Frito-Lay, Burns & McDonnell, and CPL to analyze the reductions in carbon dioxide (CO2) emissions that result from use of biomass-fired boilers in the food manufacturing environment. DOE support provided for the data collection and analysis, and reporting necessary to evaluate boiler efficiencies and reductions in CO2 emissions. The Frito-Lay biomass-fired boiler has resulted in significant reductions in CO2 emissions from the Topeka production facility. The use of natural gas has been reduced by 400 to 420 million standard cubic feet per year with corresponding reductions of 24,000 to 25,000 tons of CO2. The boiler does require auxiliary functions, however, that are unnecessary for a gas-fired boiler. These include heavy motors and fans for moving fuel and firing the boiler, trucks and equipment for delivering the fuel and moving at the boiler plant, and chippers for preparing the fuel prior to delivery. Each of these operations requires the combustion of fossil fuels or electricity and has associated CO2 emissions. Even after accounting for each of these auxiliary processes, however, the biomass-fired boiler results in net emission reductions of 22,500 to 23,500 tons of CO2 per year.

  2. Development of a reburning boiler process model

    SciTech Connect

    Wu, K.T.

    1992-01-30

    The overall objective of this program is to integrate EER's expertise in boiler reburning performance evaluation into a package of analytical computer tools. Specific objectives of the program are to develop a computational capability with the following features: (1) can be used to predict the impact of gas reburning application on thermal conditions in the boiler radiant furnace, and on overall boiler performance; (2) can estimate gas reburning NO{sub x} reduction effectiveness based on specific reburning configurations and furnace/boiler configurations; (3) can be used as an analytical tool to evaluate the impact of boiler process parameters (e.g., fuel switching and changes in boiler operating conditions) on boiler thermal performance; (4) is adaptable to most boiler designs (tangential and wall fire boilers) and a variety of fuels (solid, liquid, gaseous and slurried fuels); (5) is sufficiently user friendly to be exercisable by engineers with a reasonable knowledge of boilers, and with reasonable computer skills. Here, user friendly'' means that the user will be guided by computer codes during the course of setting up individual input files for the boiler performance model.

  3. Steam conservation and boiler plant efficiency advancements

    SciTech Connect

    Fiorino, D.P.

    1999-07-01

    This paper examines several cost-effective steam conservation and boiler plant efficiency advancements that were implemented during a recently completed central steam boiler plant replacement project at a very large semiconductor manufacturing complex. They were: (1) Reheating of dehumidified clean room makeup air with heat extracted during precooling; (2) Preheating of deionization feedwater with refrigerant heat of condensation; (3) Preheating of boiler combustion air with heat extracted from boiler flue gas; (4) Preheating of boiler feedwater with heat extracted from gas turbine exhaust; (5) Variable-speed operation of boiler feedwater pumps and forced-draft fans; and (6) Preheating of boiler makeup water with heat extracted from boiler surface blow-down. The first two advancements (steam conservation measures) saved about $1,010,000 per year by using recovered waste heat rather than steam-derived heat at selected heating loads. The last four advancements (boiler plant efficiency measures) reduced the cost of steam produced by about 13%, or $293,500 per year, by reducing use of natural gas and electricity at the steam boiler plant. These advancements should prove of interest to industrial energy users faced with replacement of aging, inefficient boiler plants, rising fuel and power prices, and increasing pressures to reduce operating costs in order to enhance competitiveness.

  4. Predictive modelling of boiler fouling

    SciTech Connect

    Not Available

    1992-01-01

    In this reporting period, efforts were initiated to supplement the comprehensive flow field description obtained from the RNG-Spectral Element Simulations by incorporating, in a general framework, appropriate modules to model particle and condensable species transport to the surface. Specifically, a brief survey of the literature revealed the following possible mechanisms for transporting different ash constituents from the host gas to boiler tubes as deserving prominence in building the overall comprehensive model: (1) Flame-volatilized species, chiefly sulfates, are deposited on cooled boiler tubes via the mechanism of classical vapor diffusion. This mechanism is more efficient than the particulate ash deposition, and as a result there is usually an enrichment of condensable salts, chiefly sulfates, in boiler deposits; (2) Particle diffusion (Brownian motion) may account for deposition of some fine particles below 0. 1 mm in diameter in comparison with the mechanism of vapor diffusion and particle depositions, however, the amount of material transported to the tubes via this route is probably small. (3) Eddy diffusion, thermophoretic and electrophoretic deposition mechanisms are likely to have a marked influence in transporting 0.1 to 5[mu]m particles from the host gas to cooled boiler tubes; (4) Inertial impaction is the dominant mechanism in transporting particles above 5[mu]m in diameter to water and steam tubes in pulverized coal fired boiler, where the typical flue gas velocity is between 10 to 25 m/s. Particles above 10[mu]m usually have kinetic energies in excess of what can be dissipated at impact (in the absence of molten sulfate or viscous slag deposit), resulting in their entrainment in the host gas.

  5. Neural network predictions of slagging and fouling in pulverized coal-fired utility boilers

    SciTech Connect

    Wildman, D.; Smouse, S.; Chi, R.

    1996-12-31

    Feed-forward back-propagation neural networks were trained to relate the occurrence and characteristics of troublesome slagging and fouling deposits in utility boilers to coal properties, boiler design features, and boiler operating conditions. The data used in this effort were from a survey of utility boilers conducted by Battelle Columbus Laboratories in an Electric Power Research Institute project. Two networks were developed in this study, one for slagging and one for fouling, to predict ash deposition in various types of boilers (wall-, opposed wall-, tangentially, and cyclone-fired) that fire bituminous and sub-bituminous coals. Both networks predicted the frequency of deposition problems, physical nature (or state) of the deposit, and the thickness of the deposit. Since deposit characteristics vary with boiler location and operating conditions, the worst documented cases of ash deposition were used to train the neural networks. Comparison of actual and predicted deposition showed very good agreement in general. The relative importance of some of the input variables on the predicted deposit characteristics were assessed in a sensitivity analysis. Also, the slagging and fouling characteristics of a blend of two coals with significant different deposition characteristics were predicted to demonstrate a practical application of developed neural networks.

  6. Modeling energy consumption of residential furnaces and boilers in U.S. homes

    SciTech Connect

    Lutz, James; Dunham-Whitehead, Camilla; Lekov, Alex; McMahon, James

    2004-02-01

    In 2001, DOE initiated a rulemaking process to consider whether to amend the existing energy efficiency standards for furnaces and boilers. A key factor in DOE's consideration of new standards is their cost-effectiveness to consumers. Determining cost-effectiveness requires an appropriate comparison of the additional first cost of energy efficiency design options with the savings in operating costs. This report describes calculation of equipment energy consumption (fuel and electricity) based on estimated conditions in a sample of homes that are representative of expected furnace and boiler installations. To represent actual houses with furnaces and boilers in the United States, we used a set of houses from the Residential Energy Consumption Survey of 1997 conducted by the Energy Information Administration. Our calculation methodology estimates the energy consumption of alternative (more-efficient) furnaces, if they were to be used in each house in place of the existing equipment. We developed the method of calculation described in this report for non-weatherized gas furnaces. We generalized the energy consumption calculation for this product class to the other furnace product classes. Fuel consumption calculations for boilers are similar to those for the other furnace product classes. The electricity calculations for boilers are simpler than for furnaces, because boilers do not provide thermal distribution for space cooling as furnaces often do.

  7. Anthracite culm fired fluidized-bed boiler

    SciTech Connect

    Lentz, E.C.

    1984-01-01

    This chapter discusses a DOE-sponsored project to design, fabricate, install and demonstrate a system which can be fired with anthracite refuse coal (culm) or other coal. It is estimated that there are over 800 culm banks containing approximately 900 million ton of material in the northeast Pennsylvania area, which represents 1 billion barrels (159 GL) of oil equivalent. Culm combustion tests were conducted to establish and confirm the start-up and load following control systems to be used in the fluidized-bed boiler. The main purpose of the examined project is to demonstrate to industry that mine-site preparation/delivery of ready-to-burn fuel and disposal of the ash can be accomplished reliably, economically, and without detriment to the industrial or community environment.

  8. Final technical report. In-situ FT-IR monitoring of a black liquor recovery boiler

    SciTech Connect

    James Markham; Joseph Cosgrove; David Marran; Jorge Neira; Chad Nelson; Peter Solomon

    1999-05-31

    This project developed and tested advanced Fourier transform infrared (FT-IR) instruments for process monitoring of black liquor recovery boilers. The state-of-the-art FT-IR instruments successfully operated in the harsh environment of a black liquor recovery boiler and provided a wealth of real-time process information. Concentrations of multiple gas species were simultaneously monitored in-situ across the combustion flow of the boiler and extractively at the stack. Sensitivity to changes of particulate fume and carryover levels in the process flow were also demonstrated. Boiler set-up and operation is a complex balance of conditions that influence the chemical and physical processes in the combustion flow. Operating parameters include black liquor flow rate, liquor temperature, nozzle pressure, primary air, secondary air, tertiary air, boiler excess oxygen and others. The in-process information provided by the FT-IR monitors can be used as a boiler control tool since species indicative of combustion efficiency (carbon monoxide, methane) and pollutant emissions (sulfur dioxide, hydrochloric acid and fume) were monitored in real-time and observed to fluctuate as operating conditions were varied. A high priority need of the U.S. industrial boiler market is improved measurement and control technology. The sensor technology demonstrated in this project is applicable to the need of industry.

  9. 46 CFR 63.25-1 - Small automatic auxiliary boilers.

    Code of Federal Regulations, 2013 CFR

    2013-10-01

    ... 46 Shipping 2 2013-10-01 2013-10-01 false Small automatic auxiliary boilers. 63.25-1 Section 63.25... AUXILIARY BOILERS Requirements for Specific Types of Automatic Auxiliary Boilers § 63.25-1 Small automatic auxiliary boilers. Small automatic auxiliary boilers defined as having heat-input ratings of 400,000...

  10. 46 CFR 63.25-1 - Small automatic auxiliary boilers.

    Code of Federal Regulations, 2010 CFR

    2010-10-01

    ... 46 Shipping 2 2010-10-01 2010-10-01 false Small automatic auxiliary boilers. 63.25-1 Section 63.25... AUXILIARY BOILERS Requirements for Specific Types of Automatic Auxiliary Boilers § 63.25-1 Small automatic auxiliary boilers. Small automatic auxiliary boilers defined as having heat-input ratings of 400,000...

  11. 46 CFR 63.25-1 - Small automatic auxiliary boilers.

    Code of Federal Regulations, 2012 CFR

    2012-10-01

    ... 46 Shipping 2 2012-10-01 2012-10-01 false Small automatic auxiliary boilers. 63.25-1 Section 63.25... AUXILIARY BOILERS Requirements for Specific Types of Automatic Auxiliary Boilers § 63.25-1 Small automatic auxiliary boilers. Small automatic auxiliary boilers defined as having heat-input ratings of 400,000...

  12. 46 CFR 63.25-1 - Small automatic auxiliary boilers.

    Code of Federal Regulations, 2011 CFR

    2011-10-01

    ... 46 Shipping 2 2011-10-01 2011-10-01 false Small automatic auxiliary boilers. 63.25-1 Section 63.25... AUXILIARY BOILERS Requirements for Specific Types of Automatic Auxiliary Boilers § 63.25-1 Small automatic auxiliary boilers. Small automatic auxiliary boilers defined as having heat-input ratings of 400,000...

  13. 46 CFR 63.25-1 - Small automatic auxiliary boilers.

    Code of Federal Regulations, 2014 CFR

    2014-10-01

    ... 46 Shipping 2 2014-10-01 2014-10-01 false Small automatic auxiliary boilers. 63.25-1 Section 63.25... AUXILIARY BOILERS Requirements for Specific Types of Automatic Auxiliary Boilers § 63.25-1 Small automatic auxiliary boilers. Small automatic auxiliary boilers defined as having heat-input ratings of 400,000...

  14. Superheater Corrosion In Biomass Boilers: Today's Science and Technology

    SciTech Connect

    Sharp, William

    2011-12-01

    This report broadens a previous review of published literature on corrosion of recovery boiler superheater tube materials to consider the performance of candidate materials at temperatures near the deposit melting temperature in advanced boilers firing coal, wood-based fuels, and waste materials as well as in gas turbine environments. Discussions of corrosion mechanisms focus on the reactions in fly ash deposits and combustion gases that can give corrosive materials access to the surface of a superheater tube. Setting the steam temperature of a biomass boiler is a compromise between wasting fuel energy, risking pluggage that will shut the unit down, and creating conditions that will cause rapid corrosion on the superheater tubes and replacement expenses. The most important corrosive species in biomass superheater corrosion are chlorine compounds and the most corrosion resistant alloys are typically FeCrNi alloys containing 20-28% Cr. Although most of these materials contain many other additional additions, there is no coherent theory of the alloying required to resist the combination of high temperature salt deposits and flue gases that are found in biomass boiler superheaters that may cause degradation of superheater tubes. After depletion of chromium by chromate formation or chromic acid volatilization exceeds a critical amount, the protective scale gives way to a thick layer of Fe{sub 2}O{sub 3} over an unprotective (FeCrNi){sub 3}O{sub 4} spinel. This oxide is not protective and can be penetrated by chlorine species that cause further acceleration of the corrosion rate by a mechanism called active oxidation. Active oxidation, cited as the cause of most biomass superheater corrosion under chloride ash deposits, does not occur in the absence of these alkali salts when the chloride is present as HCl gas. Although a deposit is more corrosive at temperatures where it is molten than at temperatures where it is frozen, increasing superheater tube temperatures through

  15. Burning wastes in steam boiler

    SciTech Connect

    Feeley, F.G.

    1984-01-01

    A review of the advantages and precautions in the burning of a wide variety of industrial wastes is presented. The reasons for burning industrial wastes are economics and pollution control. The incineration of the following industrial wastes is discussed: pulp cooking liquors, wood wastes, coffee grounds and other biomass, pitch and tars, gases, and miscellaneous solid fuels. Boiler cycles and types are also discussed. (RCK)

  16. Fluidized bed boiler feed system

    DOEpatents

    Jones, Brian C.

    1981-01-01

    A fluidized bed boiler feed system for the combustion of pulverized coal. Coal is first screened to separate large from small particles. Large particles of coal are fed directly to the top of the fluidized bed while fine particles are first mixed with recycled char, preheated, and then fed into the interior of the fluidized bed to promote char burnout and to avoid elutriation and carryover.

  17. Energy storage-boiler tank

    NASA Technical Reports Server (NTRS)

    Chubb, T. A.; Nemecek, J. J.; Simmons, D. E.

    1980-01-01

    Activities performed in an effort to demonstrate heat of fusion energy storage in containerized salts are reported. The properties and cycle life characteristics of a eutectic salt having a boiling point of about 385 C (NaCl, KCl, Mg Cl2) were determined. M-terphenyl was chosen as the heat transfer fluid. Compatibility studies were conducted and mild steel containers were selected. The design and fabrication of a 2MWh storage boiler tank are discussed.

  18. APPLICATION OF LIMB TO PULVERIZED COAL BOILERS - A SYSTEMS ANALYSIS: LIMESTONE FEED AND BOILER SYSTEMS

    EPA Science Inventory

    The report gives results of a systems analysis of the application of Limestone Injection Multistaged Burner (LIMB) technology to pulverized-coal boilers. It evaluates alternative limestone handling, preparation, and injection methods and boiler system impacts associated with LIMB...

  19. 5. North/northwest elevations of boiler stack and boiler room. Note ...

    Library of Congress Historic Buildings Survey, Historic Engineering Record, Historic Landscapes Survey

    5. North/northwest elevations of boiler stack and boiler room. Note tires on roof to reduce impact of brick work falling from stack. - Lowe Mill, Eighth Avenue, Southwest, Huntsville, Madison County, AL

  20. Unmanned boiler operation a reality in Europe

    SciTech Connect

    Ilg, E.

    1996-08-01

    With the rise in liquid level technology in Europe comes new standards for boiler operation. SMART technology for level probes and auxiliary equipment, means many European countries allow a boiler to operate completely unmanned (without operators) for up to 72 hours at a time. It is not just a level control system, but a total boiler control scheme. This incorporates level control, continuous TDS monitoring with blowdown, automatic timed bottom blowdown, feed water control, contamination detection systems for monitoring of incoming feed water, monitoring of exhaust stack temperatures, over pressure alarms and timed automatic blowdown of level pots. One of the main reasons for the development of the SMART equipment and the new boiler codes was to increase reliability of boiler operation. Surveys in Germany and England showed that almost 90 percent of boiler failures was due to operator error, this has almost been eliminated through the use of new equipment based on the new codes.

  1. Intelligent Control System of Stack-boiler

    NASA Astrophysics Data System (ADS)

    Jing, Li; Jingxia, Niu; Jianhua, Lang; Shaofeng, Li; Zhi, Li

    Boiler combustion control system's basic task is to make fuel burn calories adapt to the needs of the water temperature and ensure the economical combustion and the safe operation. In the foundations which have analyzed the stack-boiler's work process and control system structure, the system designed by using the self-learning and self-optimizing fuzzy control system of the PC to make air/coal ratio achieve the best and realize the optimized combustion; through PLC to accelerate the speed of response to the boiler, and speed up the PC to optimize the speed and realize the double loop control system for stack-boiler. The control system in premise of the stack-boiler reaches the goal of the load to achieve the highest efficiency of the boiler combustion.

  2. Industrials fear new boiler-pollution regs

    SciTech Connect

    Betts, M.

    1982-07-12

    The Council of Industrial Boiler Owners (CIBO) claims that new Environmental Protection Agency (EPA) regulations requiring costly pollution-control equipment on coal- and waste-fueled boilers conflict with national fuel-substitution goals. EPA counters that capital and annual costs will each increase only 2%, but CIBO considers that a financial barrier during the current recession. Fuel choices determined on the basis of environmental regulations could delay conversion to more-efficient boilers and alternative fuels. CIBO concerns focus on the New Source performance Standards applying to emissions from new, modified, and reconstructed industrial boilers larger than 100 million Btus per hour. (DCK)

  3. 6. VIEW WESTINTERIOR OF BOILER SHOP SECTION OF THE BETHLEHEM ...

    Library of Congress Historic Buildings Survey, Historic Engineering Record, Historic Landscapes Survey

    6. VIEW WEST-INTERIOR OF BOILER SHOP SECTION OF THE BETHLEHEM STEEL COMPANY SHIPYARD BLACKSMITH SHOP/BOILER SHOP. - Bethlehem Steel Company Shipyard, Blacksmith Shop-Boiler Shop, 1201-1321 Hudson Street, Hoboken, Hudson County, NJ

  4. 2. VIEW SOUTHWESTNORTH ELEVATION OF BOILER SHOP SECTION OF THE ...

    Library of Congress Historic Buildings Survey, Historic Engineering Record, Historic Landscapes Survey

    2. VIEW SOUTHWEST-NORTH ELEVATION OF BOILER SHOP SECTION OF THE BETHLEHEM STEEL COMPANY SHIPYARD BLACKSMITH SHOP/BOILER SHOP. - Bethlehem Steel Company Shipyard, Blacksmith Shop-Boiler Shop, 1201-1321 Hudson Street, Hoboken, Hudson County, NJ

  5. Looking east at the boiler water treatment tank located off ...

    Library of Congress Historic Buildings Survey, Historic Engineering Record, Historic Landscapes Survey

    Looking east at the boiler water treatment tank located off the west wall of the boiler house. - Wheeling-Pittsburgh Steel Corporation, Allenport Works, Boiler House, Route 88 on West bank of Monongahela River, Allenport, Washington County, PA

  6. 7. VIEW EASTINTERIOR OF BOILER SHOP SECTION OF THE BETHLEHEM ...

    Library of Congress Historic Buildings Survey, Historic Engineering Record, Historic Landscapes Survey

    7. VIEW EAST-INTERIOR OF BOILER SHOP SECTION OF THE BETHLEHEM STEEL COMPANY SHIPYARD BLACKSMITH SHOP/BOILER SHOP. - Bethlehem Steel Company Shipyard, Blacksmith Shop-Boiler Shop, 1201-1321 Hudson Street, Hoboken, Hudson County, NJ

  7. 12. Forward end of Boiler Room showing open firing doors ...

    Library of Congress Historic Buildings Survey, Historic Engineering Record, Historic Landscapes Survey

    12. Forward end of Boiler Room showing open firing doors for boilers. Note ladderway retracted overhead by which firemen entered and left Boiler Room. Coal ejectors shown at extreme left of view. - Ferry TICONDEROGA, Route 7, Shelburne, Chittenden County, VT

  8. Boiler efficiency calculation for multiple fuel burning boilers

    SciTech Connect

    Khodabakhsh, F.; Munukutla, S.; Clary, A.T.

    1996-12-31

    A rigorous method based on the output/loss approach is developed for calculating the coal flow rate for multiple fuel burning boilers. It is assumed that the ultimate analyses of all the fuels are known. In addition, it is assumed that the flow rates of all the fuels with the exception of coal are known. The calculations are performed iteratively, with the first iteration taking into consideration coal as the only fuel. The results converge to the correct answer after a few number of iterations, typically four or five.

  9. 40 CFR 76.7 - Revised NOX emission limitations for Group 1, Phase II boilers.

    Code of Federal Regulations, 2013 CFR

    2013-07-01

    ... 40 Protection of Environment 17 2013-07-01 2013-07-01 false Revised NOX emission limitations for Group 1, Phase II boilers. 76.7 Section 76.7 Protection of Environment ENVIRONMENTAL PROTECTION AGENCY (CONTINUED) AIR PROGRAMS (CONTINUED) ACID RAIN NITROGEN OXIDES EMISSION REDUCTION PROGRAM § 76.7 Revised...

  10. 40 CFR 76.7 - Revised NOX emission limitations for Group 1, Phase II boilers.

    Code of Federal Regulations, 2011 CFR

    2011-07-01

    ... 40 Protection of Environment 16 2011-07-01 2011-07-01 false Revised NOX emission limitations for Group 1, Phase II boilers. 76.7 Section 76.7 Protection of Environment ENVIRONMENTAL PROTECTION AGENCY (CONTINUED) AIR PROGRAMS (CONTINUED) ACID RAIN NITROGEN OXIDES EMISSION REDUCTION PROGRAM § 76.7 Revised...

  11. 40 CFR 76.7 - Revised NOX emission limitations for Group 1, Phase II boilers.

    Code of Federal Regulations, 2010 CFR

    2010-07-01

    ... 40 Protection of Environment 16 2010-07-01 2010-07-01 false Revised NOX emission limitations for Group 1, Phase II boilers. 76.7 Section 76.7 Protection of Environment ENVIRONMENTAL PROTECTION AGENCY (CONTINUED) AIR PROGRAMS (CONTINUED) ACID RAIN NITROGEN OXIDES EMISSION REDUCTION PROGRAM § 76.7 Revised NOX emission limitations for Group 1,...

  12. 40 CFR 76.7 - Revised NOX emission limitations for Group 1, Phase II boilers.

    Code of Federal Regulations, 2012 CFR

    2012-07-01

    ... 40 Protection of Environment 17 2012-07-01 2012-07-01 false Revised NOX emission limitations for Group 1, Phase II boilers. 76.7 Section 76.7 Protection of Environment ENVIRONMENTAL PROTECTION AGENCY (CONTINUED) AIR PROGRAMS (CONTINUED) ACID RAIN NITROGEN OXIDES EMISSION REDUCTION PROGRAM § 76.7 Revised...

  13. 40 CFR 76.7 - Revised NOX emission limitations for Group 1, Phase II boilers.

    Code of Federal Regulations, 2014 CFR

    2014-07-01

    ... 40 Protection of Environment 17 2014-07-01 2014-07-01 false Revised NOX emission limitations for Group 1, Phase II boilers. 76.7 Section 76.7 Protection of Environment ENVIRONMENTAL PROTECTION AGENCY (CONTINUED) AIR PROGRAMS (CONTINUED) ACID RAIN NITROGEN OXIDES EMISSION REDUCTION PROGRAM § 76.7 Revised...

  14. Cermet composite thermal spray coatings for erosion and corrosion protection in combustion environments of advanced coal-fired boilers. Semiannual technical progress report, August 14, 1996--January 14, 1997

    SciTech Connect

    Levin, B.F.; DuPont, J.N.; Marder, A.R.

    1997-02-01

    Research is presently being conducted to determine the optimum ceramic/metal combination in thermally sprayed metal matrix composite coatings for erosion and corrosion resistance in new coal-fired boilers. The research will be accomplished by producing model cermet composites using powder metallurgy and electrodeposition methods in which the effect of ceramic/metal combination for the erosion and corrosion resistance will be determined. These results will provide the basis for determining the optimum hard phase constituent size and volume percent in thermal spray coatings. Thermal spray coatings will be applied by our industrial sponsor and tested in our erosion and corrosion laboratories. In the first six months of this project, bulk powder processed Ni-Al{sub 2}O{sub 3} composites were produced at Idaho National Engineering Laboratory. The results of microstructural characterization of these alloys were presented in the first semiannual report. The composite samples contained 0, 21, 27, 37, and 45 volume percent Al{sub 2}O{sub 3} with an average particle size of 12 um. An increase in the volume fraction of alumina in the nickel matrix from 0 to 45% led to a significant increase in hardness of these composites.

  15. 46 CFR 109.555 - Propulsion boilers.

    Code of Federal Regulations, 2011 CFR

    2011-10-01

    ... 46 Shipping 4 2011-10-01 2011-10-01 false Propulsion boilers. 109.555 Section 109.555 Shipping COAST GUARD, DEPARTMENT OF HOMELAND SECURITY (CONTINUED) A-MOBILE OFFSHORE DRILLING UNITS OPERATIONS Miscellaneous § 109.555 Propulsion boilers. The master or person in charge and the engineer in charge...

  16. 46 CFR 109.555 - Propulsion boilers.

    Code of Federal Regulations, 2014 CFR

    2014-10-01

    ... 46 Shipping 4 2014-10-01 2014-10-01 false Propulsion boilers. 109.555 Section 109.555 Shipping COAST GUARD, DEPARTMENT OF HOMELAND SECURITY (CONTINUED) A-MOBILE OFFSHORE DRILLING UNITS OPERATIONS Miscellaneous § 109.555 Propulsion boilers. The master or person in charge and the engineer in charge...

  17. 46 CFR 109.555 - Propulsion boilers.

    Code of Federal Regulations, 2010 CFR

    2010-10-01

    ... 46 Shipping 4 2010-10-01 2010-10-01 false Propulsion boilers. 109.555 Section 109.555 Shipping COAST GUARD, DEPARTMENT OF HOMELAND SECURITY (CONTINUED) A-MOBILE OFFSHORE DRILLING UNITS OPERATIONS Miscellaneous § 109.555 Propulsion boilers. The master or person in charge and the engineer in charge...

  18. 46 CFR 109.555 - Propulsion boilers.

    Code of Federal Regulations, 2012 CFR

    2012-10-01

    ... 46 Shipping 4 2012-10-01 2012-10-01 false Propulsion boilers. 109.555 Section 109.555 Shipping COAST GUARD, DEPARTMENT OF HOMELAND SECURITY (CONTINUED) A-MOBILE OFFSHORE DRILLING UNITS OPERATIONS Miscellaneous § 109.555 Propulsion boilers. The master or person in charge and the engineer in charge...

  19. 46 CFR 109.555 - Propulsion boilers.

    Code of Federal Regulations, 2013 CFR

    2013-10-01

    ... 46 Shipping 4 2013-10-01 2013-10-01 false Propulsion boilers. 109.555 Section 109.555 Shipping COAST GUARD, DEPARTMENT OF HOMELAND SECURITY (CONTINUED) A-MOBILE OFFSHORE DRILLING UNITS OPERATIONS Miscellaneous § 109.555 Propulsion boilers. The master or person in charge and the engineer in charge...

  20. Baghouse cleans flyash from boiler exhaust

    SciTech Connect

    Not Available

    1981-02-01

    A large baghouse installation recently started up on the boilerhouse of the Avtex Fibers Inc. rayon plant in Front Royal, Virginia. The baghouse removes 99.7% of the flyash particulate from the combustion fumes of five coal-fired boilers. The boilers have a combined capacity of one million lb/h of steam. Emissions from the plant are well below EPA limitations.

  1. 30 CFR 56.13030 - Boilers.

    Code of Federal Regulations, 2010 CFR

    2010-07-01

    ..., automatic pressure-relief valves, blowdown piping, and other safety devices approved by the American Society... and Pressure Vessel Code, 1977, Published by the American Society of Mechanical Engineers. Section and... Care of Power Boilers (2) The National Board Inspection Code, a Manual for Boiler and Pressure...

  2. PAH emission from the industrial boilers.

    PubMed

    Li, C; Mi, H; Lee, W; You, W; Wang, Y

    1999-10-01

    Polycyclic aromatic hydrocarbons (PAHs) emitted from 25 industrial boilers were investigated. The fuels used for these 25 boilers included 21 heavy oil, two diesel, a co-combustion of heavy oil and natural gas (HO+NG) and a co-combustion of coke oven gas and blast furnace gas (COG+BFG) boilers. PAH samples from the stack flue gas (gas and particle phases) of these 25 boilers were collected by using a PAH stack sampling system. Twenty one individual PAHs were analyzed primarily by a gas chromatography/mass spectrometer (GC/MS). Total-PAH concentration in the flue gas of 83 measured data for these 25 boiler stacks ranged between 29.0 and 4250 microg/m(3) and averaged 488 microg/m(3). The average of PAH-homologue mass (F%) counted for the total-PAH mass was 54.7%, 9.47% and 15.3% for the 2-ring, 3-ring and 4-ring PAHs, respectively. The PAHs in the stack flue gas were dominant in the lower molecular weight PAHs. The emission factors (EFs) of total-PAHs were 13,300, 2920, 2880 and 208 microg/kg-fuel for the heavy oil, diesel, HO+NG and COG+BFG fueled-boiler, respectively. Nap was the most predominant PAH occurring in the stack flue gas. In addition, the EF of 21 individual PAHs in heavy-oil boiler were almost the highest among the four various fueled-boilers except for those of FL and BkF in the diesel boiler. Furthermore, the EF of total-PAHs or BaP for heavy oil were both one order of magnitude higher than that for the diesel-fueled boiler. PMID:10502602

  3. Environment.

    ERIC Educational Resources Information Center

    White, Gilbert F.

    1980-01-01

    Presented are perspectives on the emergence of environmental problems. Six major trends in scientific thinking are identified including: holistic approaches to examining environments, life support systems, resource management, risk assessment, streamlined methods for monitoring environmental change, and emphasis on the global framework. (Author/SA)

  4. The actual goals of geoethics

    NASA Astrophysics Data System (ADS)

    Nemec, Vaclav

    2014-05-01

    The most actual goals of geoethics have been formulated as results of the International Conference on Geoethics (October 2013) held at the geoethics birth-place Pribram (Czech Republic): In the sphere of education and public enlightenment an appropriate needed minimum know how of Earth sciences should be intensively promoted together with cultivating ethical way of thinking and acting for the sustainable well-being of the society. The actual activities of the Intergovernmental Panel of Climate Changes are not sustainable with the existing knowledge of the Earth sciences (as presented in the results of the 33rd and 34th International Geological Congresses). This knowledge should be incorporated into any further work of the IPCC. In the sphere of legislation in a large international co-operation following steps are needed: - to re-formulate the term of a "false alarm" and its legal consequences, - to demand very consequently the needed evaluation of existing risks, - to solve problems of rights of individuals and minorities in cases of the optimum use of mineral resources and of the optimum protection of the local population against emergency dangers and disasters; common good (well-being) must be considered as the priority when solving ethical dilemmas. The precaution principle should be applied in any decision making process. Earth scientists presenting their expert opinions are not exempted from civil, administrative or even criminal liabilities. Details must be established by national law and jurisprudence. The well known case of the L'Aquila earthquake (2009) should serve as a serious warning because of the proven misuse of geoethics for protecting top Italian seismologists responsible and sentenced for their inadequate superficial behaviour causing lot of human victims. Another recent scandal with the Himalayan fossil fraud will be also documented. A support is needed for any effort to analyze and to disclose the problems of the deformation of the contemporary

  5. Results of heat tests of the TGE-435 main boiler in the PGU-190/220 combined-cycle plant of the Tyumen' TETs-2 cogeneration plant

    SciTech Connect

    A.V. Kurochkin; A.L. Kovalenko; V.G. Kozlov; A.I. Krivobok

    2007-01-15

    Special features of operation of a boiler operating as a combined-cycle plant and having its own furnace and burner unit are descried. The flow of flue gases on the boiler is increased due to feeding of exhaust gases of the GTU into the furnace, which intensifies the convective heat exchange. In addition, it is not necessary to preheat air in the convective heating surfaces (the boiler has no air preheater). The convective heating surfaces of the boiler are used for heating the feed water, thus replacing the regeneration extractions of the steam turbine (HPP are absent in the circuit) and partially replacing the preheating of condensate (the LPP in the circuit of the unit are combined with preheaters of delivery water). Regeneration of the steam turbine is primarily used for the district cogeneration heating purposes. The furnace and burner unit of the exhaust-heat boiler (which is a new engineering solution for the given project) ensures utilization of not only the heat of the exhaust gases of the GTU but also of their excess volume, because the latter contains up to 15% oxygen that oxidizes the combustion process in the boiler. Thus, the gas temperature at the inlet to the boiler amounts to 580{sup o}C at an excess air factor a = 3.50; at the outlet these parameters are utilized to T{sub out} = 139{sup o}C and a{sub out} = 1.17. The proportions of the GTU/boiler loads that can actually be organized at the generating unit (and have been checked by testing) are presented and the proportions of loads recommended for the most efficient operation of the boiler are determined. The performance characteristics of the boiler are presented for various proportions of GTU/boiler loads. The operating conditions of the superheater and of the convective trailing heating surfaces are presented as well as the ecological parameters of the generating unit.

  6. Looking east at the west wall of the boiler house, ...

    Library of Congress Historic Buildings Survey, Historic Engineering Record, Historic Landscapes Survey

    Looking east at the west wall of the boiler house, boiler water treatment tank, and waste gas stack. Water tower is to the left of the boiler house. - Wheeling-Pittsburgh Steel Corporation, Allenport Works, Boiler House, Route 88 on West bank of Monongahela River, Allenport, Washington County, PA

  7. 49 CFR 230.36 - Hydrostatic testing of boilers.

    Code of Federal Regulations, 2014 CFR

    2014-10-01

    ... 49 Transportation 4 2014-10-01 2014-10-01 false Hydrostatic testing of boilers. 230.36 Section 230... ADMINISTRATION, DEPARTMENT OF TRANSPORTATION STEAM LOCOMOTIVE INSPECTION AND MAINTENANCE STANDARDS Boilers and Appurtenances Pressure Testing of Boilers § 230.36 Hydrostatic testing of boilers. (a) Time of test....

  8. 49 CFR 230.36 - Hydrostatic testing of boilers.

    Code of Federal Regulations, 2013 CFR

    2013-10-01

    ... 49 Transportation 4 2013-10-01 2013-10-01 false Hydrostatic testing of boilers. 230.36 Section 230... ADMINISTRATION, DEPARTMENT OF TRANSPORTATION STEAM LOCOMOTIVE INSPECTION AND MAINTENANCE STANDARDS Boilers and Appurtenances Pressure Testing of Boilers § 230.36 Hydrostatic testing of boilers. (a) Time of test....

  9. Retrofitted coal-fired firetube boiler and method employed therewith

    DOEpatents

    Wagoner, C.L.; Foote, J.P.

    1995-07-04

    A coal-fired firetube boiler and a method for converting a gas-fired firetube boiler to a coal-fired firetube boiler are disclosed. The converted boiler includes a plurality of combustion zones within the firetube and controlled stoichiometry within the combustion zones. 19 figs.

  10. 49 CFR 230.36 - Hydrostatic testing of boilers.

    Code of Federal Regulations, 2011 CFR

    2011-10-01

    ... 49 Transportation 4 2011-10-01 2011-10-01 false Hydrostatic testing of boilers. 230.36 Section 230... ADMINISTRATION, DEPARTMENT OF TRANSPORTATION STEAM LOCOMOTIVE INSPECTION AND MAINTENANCE STANDARDS Boilers and Appurtenances Pressure Testing of Boilers § 230.36 Hydrostatic testing of boilers. (a) Time of test....

  11. Retrofitted coal-fired firetube boiler and method employed therewith

    DOEpatents

    Wagoner, Charles L.; Foote, John P.

    1995-01-01

    A coal-fired firetube boiler and a method for converting a gas-fired firetube boiler to a coal-fired firetube boiler, the converted boiler including a plurality of combustion zones within the firetube and controlled stoichiometry within the combustion zones.

  12. 46 CFR 63.25-7 - Exhaust gas boilers.

    Code of Federal Regulations, 2013 CFR

    2013-10-01

    ... 46 Shipping 2 2013-10-01 2013-10-01 false Exhaust gas boilers. 63.25-7 Section 63.25-7 Shipping COAST GUARD, DEPARTMENT OF HOMELAND SECURITY (CONTINUED) MARINE ENGINEERING AUTOMATIC AUXILIARY BOILERS Requirements for Specific Types of Automatic Auxiliary Boilers § 63.25-7 Exhaust gas boilers. (a)...

  13. 49 CFR 230.36 - Hydrostatic testing of boilers.

    Code of Federal Regulations, 2010 CFR

    2010-10-01

    ... 49 Transportation 4 2010-10-01 2010-10-01 false Hydrostatic testing of boilers. 230.36 Section 230... ADMINISTRATION, DEPARTMENT OF TRANSPORTATION STEAM LOCOMOTIVE INSPECTION AND MAINTENANCE STANDARDS Boilers and Appurtenances Pressure Testing of Boilers § 230.36 Hydrostatic testing of boilers. (a) Time of test....

  14. 49 CFR 230.36 - Hydrostatic testing of boilers.

    Code of Federal Regulations, 2012 CFR

    2012-10-01

    ... 49 Transportation 4 2012-10-01 2012-10-01 false Hydrostatic testing of boilers. 230.36 Section 230... ADMINISTRATION, DEPARTMENT OF TRANSPORTATION STEAM LOCOMOTIVE INSPECTION AND MAINTENANCE STANDARDS Boilers and Appurtenances Pressure Testing of Boilers § 230.36 Hydrostatic testing of boilers. (a) Time of test....

  15. 24. VIEW OF FIRING AISLE OF EAST BOILER ROOM LOOKING ...

    Library of Congress Historic Buildings Survey, Historic Engineering Record, Historic Landscapes Survey

    24. VIEW OF FIRING AISLE OF EAST BOILER ROOM LOOKING SOUTH. BOILERS 900 AND 901 ARE ON THE RIGHT, BOILERS 902, 903, AND 904 ARE ON THE LEFT. NOTE REMAINS OF THE LARRY CAR TRACK SYSTEM FOR TRANSFERRING COAL TO BOILER HOPPERS ABOVE THE AISLE. - New York, New Haven & Hartford Railroad, Cos Cob Power Plant, Sound Shore Drive, Greenwich, Fairfield County, CT

  16. 49 CFR 230.30 - Lap-joint seam boilers.

    Code of Federal Regulations, 2011 CFR

    2011-10-01

    ... 49 Transportation 4 2011-10-01 2011-10-01 false Lap-joint seam boilers. 230.30 Section 230.30..., DEPARTMENT OF TRANSPORTATION STEAM LOCOMOTIVE INSPECTION AND MAINTENANCE STANDARDS Boilers and Appurtenances Inspection and Repair § 230.30 Lap-joint seam boilers. Every boiler having lap-joint longitudinal...

  17. Corrosion/erosion detection of boiler tubes utilizing pulsed infrared imaging

    NASA Astrophysics Data System (ADS)

    Bales, Maurice J.; Bishop, Chip C.

    1995-05-01

    This paper discusses a new technique for locating and detecting wall thickness reduction in boiler tubes caused by erosion/corrosion. Traditional means for this type of defect detection utilizes ultrasonics (UT) to perform a point by point measurement at given intervals of the tube length, which requires extensive and costly shutdown or `outage' time to complete the inspection, and has led to thin areas going undetected simply because they were located in between the sampling points. Pulsed infrared imaging (PII) can provide nearly 100% inspection of the tubes in a fraction of the time needed for UT. The IR system and heat source used in this study do not require any special access or fixed scaffolding, and can be remotely operated from a distance of up to 100 feet. This technique has been tried experimentally in a laboratory environment and verified in an actual field application. Since PII is a non-contact technique, considerable time and cost savings should be realized as well as the ability to predict failures rather than repairing them once they have occurred.

  18. Boiler efficiency methodology for solar heat applications

    NASA Astrophysics Data System (ADS)

    Maples, D.; Conwell, J. C.; Pacheco, J. E.

    1992-08-01

    This report contains a summary of boiler efficiency measurements which can be applied to evaluate the performance of steam-generating boilers via both the direct and indirect methods. This methodology was written to assist industries in calculating the boiler efficiency for determining the applicability and value of thermal industrial heat, as part of the efforts of the Solar Thermal Design Assistance Center (STDAC) funded by Sandia National Laboratories. Tables of combustion efficiencies are enclosed as functions of stack temperatures and the amount of carbon dioxide and carbon monoxide in the gas stream.

  19. Neural Modeling and Experimental Investigation of the Erosion Characteristics of Boiler Grade Steels Impacted by Fly Ash

    NASA Astrophysics Data System (ADS)

    Das, S. K.; Mandal, Durbadal; Sahoo, K. L.

    2015-09-01

    In this study, experimental investigations on solid particle erosion have been carried out for two typical boiler grade steels used for fabricating boiler components, namely, 0.22C steel and 1.25Cr-Mo-V steel. The erosion tests were conducted using an air jet erosion testing facility conforming to ASTM Standard G76 international testing method. Impingement angle of the air-particle stream on the target material was varied from 30° to 75°, and the particle impact velocity was also varied from 40 to 150 m/s. The surface morphology of the eroded samples was investigated by SEM to elucidate the erosion mechanism under different particle impact conditions. Further, an artificial neural network (ANN) model has been developed to predict the erosion behavior of these boiler grade steels impacted by boiler fly ash for more realistic characterization of erosion potential using pertinent data. An efficient network training optimization algorithm has been employed for faster convergence and better predictions. The ANN predictions of erosion rate are found to be in excellent agreement with the actual measured data as reported in the literature. It has been observed from the neural model results that the erosion potential of actual boiler fly ash with various levels of silica content is considerably higher than the synthetic erodent (alumina particles) usually used in the experiments to mimic fly ash erosion behavior under simulated conditions.

  20. Experiences with hydrazine substitutes in boiler systems

    SciTech Connect

    Costa, S.T.; Dilcer, S.B.; Walker, J.L. )

    1990-07-01

    Several case histories are given to show the improved results obtained when strong passivating agents replace hydrazine in load-following boilers. Feedwater iron and copper levels obtained with hydrazine and with the new stronger reducing agents are compared.

  1. Exploiting the On-Campus Boiler House.

    ERIC Educational Resources Information Center

    Woods, Donald R.; And Others

    1986-01-01

    Shows how a university utility building ("boiler house") is used in a chemical engineering course for computer simulations, mathematical modeling and process problem exercises. Student projects involving the facility are also discussed. (JN)

  2. Boiler scale prevention employing an organic chelant

    DOEpatents

    Wallace, Steven L.; Griffin, Jr., Freddie; Tvedt, Jr., Thorwald J.

    1984-01-01

    An improved method of treating boiler water which employs an oxygen scavenging compound and a compound to control pH together with a chelating agent, wherein the chelating agent is hydroxyethylethylenediaminetriacetic acid.

  3. Correlating benzene, total hydrocarbon and carbon monoxide emissions from wood-fired boilers

    SciTech Connect

    Hubbard, A.J.; Grande, D.E.; Berens, J.R.; Piotrowski, J.

    1997-12-31

    Hazardous air pollutants, including benzene, are generated by the incomplete combustion of fuels. Organic compound emissions, which are generally products of incomplete combustion, are reduced by promoting high quality combustion, for example by controlling furnace exit temperatures and establishing minimum residence times. Monitoring carbon monoxide (CO) emissions is important since the amount of carbon monoxide emitted represents the quality of combustion which in turn represents the amount of hazardous air pollutants being generated. Total hydrocarbon (THC) emissions are also related to the quality of combustion. Recently the Wisconsin Department of Natural Resources (DNR) measured the benzene and total hydrocarbon emissions from two large industrial wood fired boilers. These boilers are located at Tenneco Packaging, a container board manufacturing facility in northern Wisconsin. Temperature, oxygen and carbon monoxide concentrations were sampled continuously by Tenneco Packaging`s emission monitoring system. The Department`s team used an organic vapor analyzer to continuously measure concentrations of total hydrocarbons (THC). The Department`s team also used a modified USEPA Method 18 sampling train to capture organic vapors for subsequent analysis by gas chromatography. The data show correlations between benzene and carbon monoxide, and between benzene and THC concentrations. The emissions sampling occurred both upstream of the particulate emissions control system as well as at the stack. The CO variations during actual boiler operation appeared to be well correlated with changes in boiler steam load. That is, increases in CO generally accompanied a change, either up or down, in boiler load. Lower concentrations of CO were associated with stable combustion, as indicated by periods of constant or nearly constant boiler load.

  4. Boiler burden reduced at Bedford site.

    PubMed

    Horsley, Chris

    2011-10-01

    With the NHS aiming to reduce its 2007 carbon footprint by 10% by 2015, Chris Horsley, managing director of Babcock Wanson UK, a provider of industrial boilers and burners, thermal oxidisers, air treatment, water treatment, and associated services, looks at how one NHS Trust has approached the challenge, and considerably reduced its carbon emissions, by refurbishing its boiler house and moving from oil to gas-fired steam generation. PMID:22049674

  5. Fluidized-bed-fired industrial boilers

    SciTech Connect

    Leon, A.M.; McCoy, D.E.

    1981-01-01

    E. Keeler Company and Dorr-Oliver, Inc. have joined to design, market and manufacture atmospheric fluidized-bed-fired boilers. The first contract, called Shamokin, was a 23,400 lb/hr unit fired with anthracite culm having a heating value of 4000 Btu/lb and 67% ash. The Department of Energy sponsored this plant as a demonstration project. Boiler erection is nearly complete and start-up is scheduled for mid-1981. In conjunction with the Shamokin project, a line of fluidized-bed-fired boilers to 250,000 lb/hr has been developed for conventional solid fuels. The development of fluidized-bed-fired, industrial boilers is in its very early stages. At this point, it is not possible for any manufacturer to claim extensive operating experience with any particular design under the varied applications normal to industrial watertube boilers. Many different designs and approaches will develop over the next few years and until there has been some operating experience, it is not possible to evaluate just what share of the future industrial boiler market will utilize fluidized-bed firing.

  6. Foster Wheeler compact CFB boiler with INTREX

    SciTech Connect

    Hyppaenen, T.; Rainio, A.; Kauppinen, K.V.O.; Stone, J.E.

    1997-12-31

    Foster Wheeler has introduced a new COMPACT Circulating Fluidized Bed (CFB) boiler design based on the rectangular hot solids separator. The Compact design also enables easy implementation of new designs for INTREX fluid bed heat exchangers. These new products result in many benefits which affect the boiler economy and operation. After initial development of the Compact CFB design it has been applied in demonstration and industrial scale units. The performance of Compact CFB has been proved to be equivalent to conventional Foster Wheeler CFB has been proved to be equivalent to conventional Foster Wheeler CFB boilers with high availability. Several new Foster Wheeler Compact boilers are being built or already in operation. Operational experiences from different units will be discussed in this paper. There are currently Compact units with 100--150 MW{sub e} capacity under construction. With the scale-up experience with conventional CFB boilers and proven design approach and scale-up steps, Foster Wheeler will have the ability to provide large Compact CFB boilers up to 400--600 MW{sub e} capacity.

  7. Assessment of physical workload in boiler operations.

    PubMed

    Rodrigues, Valéria Antônia Justino; Braga, Camila Soares; Campos, Julio César Costa; Souza, Amaury Paulo de; Minette, Luciano José; Sensato, Guilherme Luciano; Moraes, Angelo Casali de; Silva, Emília Pio da

    2012-01-01

    The use of boiler wood-fired is fairly common equipment utilized in steam generation for energy production in small industries. The boiler activities are considered dangerous and heavy, mainly due to risks of explosions and the lack of mechanization of the process. This study assessed the burden of physical labor that operators of boilers are subjected during the workday. Assessment of these conditions was carried out through quantitative and qualitative measurements. A heart rate monitor, a wet-bulb globe thermometer (WBGT), a tape-measure and a digital infrared camera were the instruments used to collect the quantitative data. The Nordic Questionnaire and the Painful Areas Diagram were used to relate the health problems of the boiler operator with activity. With study, was concluded that the boiler activity may cause pains in the body of intensity different, muscle fatigue and diseases due to excessive weight and the exposure to heat. The research contributed to improve the boiler operator's workplace and working conditions. PMID:22316759

  8. Linguistic Theory and Actual Language.

    ERIC Educational Resources Information Center

    Segerdahl, Par

    1995-01-01

    Examines Noam Chomsky's (1957) discussion of "grammaticalness" and the role of linguistics in the "correct" way of speaking and writing. It is argued that the concern of linguistics with the tools of grammar has resulted in confusion, with the tools becoming mixed up with the actual language, thereby becoming the central element in a metaphysical…

  9. 40 CFR 270.66 - Permits for boilers and industrial furnaces burning hazardous waste.

    Code of Federal Regulations, 2010 CFR

    2010-07-01

    ... CFR 124.10(c)(1)(ix) and to the appropriate units of State and local government as set forth in 40 CFR... furnaces burning hazardous waste. 270.66 Section 270.66 Protection of Environment ENVIRONMENTAL PROTECTION... PROGRAM Special Forms of Permits § 270.66 Permits for boilers and industrial furnaces burning...

  10. Microfine coal firing results from a retrofit gas/oil-designed industrial boiler

    SciTech Connect

    Patel, R.; Borio, R.W.; Liljedahl, G.

    1995-11-01

    Under US Department of Energy, Pittsburgh Energy Technology Center (PETC) support, the development of a High Efficiency Advanced Coal Combustor (HEACC) has been in progress since 1987 at the ABB Power Plant Laboratories. The initial work on this concept produced an advanced coal firing system that was capable of firing both water-based and dry pulverized coal in an industrial boiler environment.

  11. Computational Modeling and Assessment Of Nanocoatings for Ultra Supercritical Boilers

    SciTech Connect

    David W. Gandy; John P. Shingledecker

    2011-04-11

    Forced outages and boiler unavailability in conventional coal-fired fossil power plants is most often caused by fireside corrosion of boiler waterwalls. Industry-wide, the rate of wall thickness corrosion wastage of fireside waterwalls in fossil-fired boilers has been of concern for many years. It is significant that the introduction of nitrogen oxide (NOx) emission controls with staged burners systems has increased reported waterwall wastage rates to as much as 120 mils (3 mm) per year. Moreover, the reducing environment produced by the low-NOx combustion process is the primary cause of accelerated corrosion rates of waterwall tubes made of carbon and low alloy steels. Improved coatings, such as the MCrAl nanocoatings evaluated here (where M is Fe, Ni, and Co), are needed to reduce/eliminate waterwall damage in subcritical, supercritical, and ultra-supercritical (USC) boilers. The first two tasks of this six-task project-jointly sponsored by EPRI and the U.S. Department of Energy (DE-FC26-07NT43096)-have focused on computational modeling of an advanced MCrAl nanocoating system and evaluation of two nanocrystalline (iron and nickel base) coatings, which will significantly improve the corrosion and erosion performance of tubing used in USC boilers. The computational model results showed that about 40 wt.% is required in Fe based nanocrystalline coatings for long-term durability, leading to a coating composition of Fe-25Cr-40Ni-10 wt.% Al. In addition, the long term thermal exposure test results further showed accelerated inward diffusion of Al from the nanocrystalline coatings into the substrate. In order to enhance the durability of these coatings, it is necessary to develop a diffusion barrier interlayer coating such TiN and/or AlN. The third task 'Process Advanced MCrAl Nanocoating Systems' of the six-task project jointly sponsored by the Electric Power Research Institute, EPRI and the U.S. Department of Energy (DE-FC26-07NT43096)- has focused on processing of

  12. Laser-induced breakdown spectroscopy at high temperatures in industrial boilers and furnaces

    NASA Astrophysics Data System (ADS)

    Blevins, Linda G.; Shaddix, Christopher R.; Sickafoose, Shane M.; Walsh, Peter M.

    2003-10-01

    Laser-induced breakdown spectroscopy (LIBS) was applied (1) near the superheater of an electric power generation boiler burning biomass, coal, or both; (2) at the exit of a glass-melting furnace burning natural gas and oxygen; and (3) near the nose arches of two paper mill recovery boilers burning black liquor. Difficulties associated with the high temperatures and high particle loadings in these environments were surmounted by use of novel LIBS probes. Echelle and linear spectrometers coupled to intensified CCD cameras were used individually and sometimes simultaneously. Elements detected include Na, K, Ca, Mg, C, B, Si, Mn, Al, Fe, Rb, Cl, and Ti.

  13. Laser-induced breakdown spectroscopy at high temperatures in industrial boilers and furnaces.

    PubMed

    Blevins, Linda G; Shaddix, Christopher R; Sickafoose, Shane M; Walsh, Peter M

    2003-10-20

    Laser-induced breakdown spectroscopy (LIBS) was applied (1) near the superheater of an electric power generation boiler burning biomass, coal, or both; (2) at the exit of a glass-melting furnace burning natural gas and oxygen; and (3) near the nose arches of two paper mill recovery boilers burning black liquor. Difficulties associated with the high temperatures and high particle loadings in these environments were surmounted by use of novel LIBS probes. Echelle and linear spectrometers coupled to intensified CCD cameras were used individually and sometimes simultaneously. Elements detected include Na, K, Ca, Mg, C, B, Si, Mn, Al, Fe, Rb, Cl, and Ti. PMID:14594073

  14. Development of Erosion-Corrosion-Resistant Cold-Spray Nanostructured Ni-20Cr Coating for Coal-Fired Boiler Applications

    NASA Astrophysics Data System (ADS)

    Kumar, M.; Singh, H.; Singh, N.; Chavan, N. M.; Kumar, S.; Joshi, S. V.

    2015-12-01

    The erosion-corrosion (E-C) behavior of a cold-spray nanostructured Ni-20Cr coating was studied under cyclic conditions in a coal-fired boiler. This study was done for 15 cycles (1500 h), in which each cycle comprised 100 h of heating in the boiler environment, followed by 1 h of cooling under ambient air conditions. The E-C extent was evaluated in terms of thickness loss data of the samples. The eroded-corroded samples were characterized using XRD, SEM/EDS, and x-ray mapping analyses. The nanostructured coating offered excellent E-C protection to boiler tube material (SA 516 steel) under harsh live conditions of the boiler. This E-C resistance offered by investigated coating may be attributed to the presence of protective NiO and Cr2O3 phases in its oxide scale and its superior as-sprayed microhardness.

  15. 33. VIEW OF BASEMENT UNDER EAST BOILER ROOM LOOKING TOWARD ...

    Library of Congress Historic Buildings Survey, Historic Engineering Record, Historic Landscapes Survey

    33. VIEW OF BASEMENT UNDER EAST BOILER ROOM LOOKING TOWARD WEST BOILER ROOM BASEMENT THROUGH THE ASH TRANSFER TUNNEL. ASH HOPPER FOR BOILER 900 IS ON THE RIGHT. NOTE THE TRACKS ALONG THE FLOOR OF THE TUNNEL. A SMALL ELECTRIC LOCOMOTIVE HAULED CARS FOR TRANSFERRING ASH FROM BOILERS TO DISPOSAL SITES OUTSIDE THE BUILDING. THIS SYSTEM BECAME OBSOLETE IN 1938 WHEN BOILERS IN THE WEST BOILER ROOM WERE REMOVED AND PULVERIZED COAL WAS ADOPTED AS THE FUEL. - New York, New Haven & Hartford Railroad, Cos Cob Power Plant, Sound Shore Drive, Greenwich, Fairfield County, CT

  16. {open_quotes}The next generations of Tampella Power`s CFB boilers{close_quotes}

    SciTech Connect

    Alliston, M.G.

    1995-12-31

    The next generation of Tampella Power Corporation`s CFB boilers is discussed in outline form. The following topics are outlined: CFB boiler advantages, CFB boiler fuel flexibility and CYMIC boiler construction.

  17. Thermal Spray Coatings for High-Temperature Corrosion Protection in Biomass Co-Fired Boilers

    NASA Astrophysics Data System (ADS)

    Oksa, M.; Metsäjoki, J.; Kärki, J.

    2015-01-01

    There are over 1000 biomass boilers and about 500 plants using waste as fuel in Europe, and the numbers are increasing. Many of them encounter serious problems with high-temperature corrosion due to detrimental elements such as chlorides, alkali metals, and heavy metals. By HVOF spraying, it is possible to produce very dense and well-adhered coatings, which can be applied for corrosion protection of heat exchanger surfaces in biomass and waste-to-energy power plant boilers. Four HVOF coatings and one arc sprayed coating were exposed to actual biomass co-fired boiler conditions in superheater area with a probe measurement installation for 5900 h at 550 and 750 °C. The coating materials were Ni-Cr, IN625, Fe-Cr-W-Nb-Mo, and Ni-Cr-Ti. CJS and DJ Hybrid spray guns were used for HVOF spraying to compare the corrosion resistance of Ni-Cr coating structures. Reference materials were ferritic steel T92 and nickel super alloy A263. The circulating fluidized bed boiler burnt a mixture of wood, peat and coal. The coatings showed excellent corrosion resistance at 550 °C compared to the ferritic steel. At higher temperature, NiCr sprayed with CJS had the best corrosion resistance. IN625 was consumed almost completely during the exposure at 750 °C.

  18. Thermal Spray Coatings for High-Temperature Corrosion Protection in Biomass Co-Fired Boilers

    NASA Astrophysics Data System (ADS)

    Oksa, M.; Metsäjoki, J.; Kärki, J.

    2014-09-01

    There are over 1000 biomass boilers and about 500 plants using waste as fuel in Europe, and the numbers are increasing. Many of them encounter serious problems with high-temperature corrosion due to detrimental elements such as chlorides, alkali metals, and heavy metals. By HVOF spraying, it is possible to produce very dense and well-adhered coatings, which can be applied for corrosion protection of heat exchanger surfaces in biomass and waste-to-energy power plant boilers. Four HVOF coatings and one arc sprayed coating were exposed to actual biomass co-fired boiler conditions in superheater area with a probe measurement installation for 5900 h at 550 and 750 °C. The coating materials were Ni-Cr, IN625, Fe-Cr-W-Nb-Mo, and Ni-Cr-Ti. CJS and DJ Hybrid spray guns were used for HVOF spraying to compare the corrosion resistance of Ni-Cr coating structures. Reference materials were ferritic steel T92 and nickel super alloy A263. The circulating fluidized bed boiler burnt a mixture of wood, peat and coal. The coatings showed excellent corrosion resistance at 550 °C compared to the ferritic steel. At higher temperature, NiCr sprayed with CJS had the best corrosion resistance. IN625 was consumed almost completely during the exposure at 750 °C.

  19. 40 CFR 270.235 - Options for incinerators, cement kilns, lightweight aggregate kilns, solid fuel boilers, liquid...

    Code of Federal Regulations, 2012 CFR

    2012-07-01

    ..., lightweight aggregate kilns, solid fuel boilers, liquid fuel boilers and hydrochloric acid production furnaces..., solid fuel boilers, liquid fuel boilers and hydrochloric acid production furnaces to minimize emissions..., liquid fuel boiler, or hydrochloric acid production furnace that has conducted a...

  20. 40 CFR 270.235 - Options for incinerators, cement kilns, lightweight aggregate kilns, solid fuel boilers, liquid...

    Code of Federal Regulations, 2014 CFR

    2014-07-01

    ..., lightweight aggregate kilns, solid fuel boilers, liquid fuel boilers and hydrochloric acid production furnaces..., solid fuel boilers, liquid fuel boilers and hydrochloric acid production furnaces to minimize emissions..., liquid fuel boiler, or hydrochloric acid production furnace that has conducted a...

  1. 40 CFR 270.235 - Options for incinerators, cement kilns, lightweight aggregate kilns, solid fuel boilers, liquid...

    Code of Federal Regulations, 2011 CFR

    2011-07-01

    ..., lightweight aggregate kilns, solid fuel boilers, liquid fuel boilers and hydrochloric acid production furnaces..., solid fuel boilers, liquid fuel boilers and hydrochloric acid production furnaces to minimize emissions..., liquid fuel boiler, or hydrochloric acid production furnace that has conducted a...

  2. 40 CFR 270.235 - Options for incinerators, cement kilns, lightweight aggregate kilns, solid fuel boilers, liquid...

    Code of Federal Regulations, 2010 CFR

    2010-07-01

    ..., lightweight aggregate kilns, solid fuel boilers, liquid fuel boilers and hydrochloric acid production furnaces..., solid fuel boilers, liquid fuel boilers and hydrochloric acid production furnaces to minimize emissions..., liquid fuel boiler, or hydrochloric acid production furnace that has conducted a...

  3. Boiler wood ash as a soil amendment

    SciTech Connect

    Mitchell, C.C.

    1996-12-31

    Each of the 88 pulp and paper mills in the southeastern United States produces an average of 43 t of boiler ash daily (47 US tons). Forty percent is wood ash, 5% is coal ash, and the remaining is a combination ash. An analysis of boiler ash from 14 Alabama pulp and paper mills averaged 38% CaCO3 equivalent with a dry density of 500 kg m{sup -3}. Most agricultural soils in the southeastern US require periodic application of ground limestone in order to maintain productivity. Using boiler wood ash and combination ash as an alternative to ground limestone is agronomically productive, environmentally safe, and fiscally sound for both the ash producer and the landowner/ farmer. While plant, nutrient content of ash is variable, it should be considered as an incidental source of plant nutrients for field crops. Metals and phytotoxic components are very low. Extensive research has been reported on the value and safety of wood-fired boiler ashes. Nevertheless, research and development projects continue in efforts to assure safe use of boiler wood ash as an alternative soil liming material.

  4. Boiler house modernization through shared savings program

    SciTech Connect

    Breault, R.W.

    1995-12-31

    Throughout Poland as well as the rest of Eastern Europe, communities and industries rely on small heat only boilers to provide district and process heat. Together these two sectors produce about 85,000 MW from boilers in the 2 to 35 MW size range. The bulk of these units were installed prior to 1992 and must be completely overhauled to meet the emission regulations which will be coming into effect on January 1, 1998. Since the only practical fuel is coal in most cases, these boilers must be either retrofit with emission control technology or be replaced entirely. The question that arises is how to accomplish this given the current tight control of capital in Poland and other East European countries. A solution that we have for this problem is shared savings. These boilers are typically operating with a quiet low efficiency as compared to western standards and with excessive manual labor. Installing modernization equipment to improve the efficiency and to automate the process provides savings. ECOGY provides the funds for the modernization to improve the efficiency, add automation and install emission control equipment. The savings that are generated during the operation of the modernized boiler system are split between the client company and ECOGY for a number of years and then the system is turned over in entirety to the client. Depending on the operating capacity, the shared savings agreement will usually span 6 to 10 years.

  5. Boiler MACT Technical Assistance (Fact Sheet)

    SciTech Connect

    Not Available

    2012-03-01

    Fact sheet describing the changes to Environmental Protection Act process standards. The DOE will offer technical assistance to ensure that major sources burning coal and oil have information on cost-effective, clean energy strategies for compliance, and to promote cleaner, more efficient boiler burning to cut harmful pollution and reduce operational costs. The U.S. Environmental Protection Agency (EPA) is expected to finalize the reconsideration process for its Clean Air Act pollution standards National Emissions Standards for Hazardous Air Pollutants for Major Sources: Industrial, Commercial, and Institutional Boilers and Process Heaters (known as Boiler Maximum Achievable Control Technology (MACT)), in Spring 2012. This rule applies to large and small boilers in a wide range of industrial facilities and institutions. The U.S. Department of Energy (DOE) will offer technical assistance to ensure that major sources burning coal or oil have information on cost-effective clean energy strategies for compliance, including combined heat and power, and to promote cleaner, more efficient boilers to cut harmful pollution and reduce operational costs.

  6. 40 CFR 63.1217 - What are the standards for liquid fuel boilers that burn hazardous waste?

    Code of Federal Regulations, 2012 CFR

    2012-07-01

    ... 40 Protection of Environment 12 2012-07-01 2011-07-01 true What are the standards for liquid fuel boilers that burn hazardous waste? 63.1217 Section 63.1217 Protection of Environment ENVIRONMENTAL PROTECTION AGENCY (CONTINUED) AIR PROGRAMS (CONTINUED) NATIONAL EMISSION STANDARDS FOR HAZARDOUS AIR POLLUTANTS FOR SOURCE CATEGORIES National...

  7. 40 CFR 63.1216 - What are the standards for solid fuel boilers that burn hazardous waste?

    Code of Federal Regulations, 2012 CFR

    2012-07-01

    ... 40 Protection of Environment 12 2012-07-01 2011-07-01 true What are the standards for solid fuel boilers that burn hazardous waste? 63.1216 Section 63.1216 Protection of Environment ENVIRONMENTAL PROTECTION AGENCY (CONTINUED) AIR PROGRAMS (CONTINUED) NATIONAL EMISSION STANDARDS FOR HAZARDOUS AIR POLLUTANTS FOR SOURCE CATEGORIES National...

  8. Looking north at the stokers for boilers numbers 1 through ...

    Library of Congress Historic Buildings Survey, Historic Engineering Record, Historic Landscapes Survey

    Looking north at the stokers for boilers numbers 1 through 4. - Wheeling-Pittsburgh Steel Corporation, Allenport Works, Boiler House, Route 88 on West bank of Monongahela River, Allenport, Washington County, PA

  9. Looking south at the ash disposal hoppers for boilers numbers ...

    Library of Congress Historic Buildings Survey, Historic Engineering Record, Historic Landscapes Survey

    Looking south at the ash disposal hoppers for boilers numbers 1 through 6. - Wheeling-Pittsburgh Steel Corporation, Allenport Works, Boiler House, Route 88 on West bank of Monongahela River, Allenport, Washington County, PA

  10. View of the rear of the electrical department & boiler ...

    Library of Congress Historic Buildings Survey, Historic Engineering Record, Historic Landscapes Survey

    View of the rear of the electrical department & boiler house, behind the upper shops - Johnson Steel Street Rail Company, Electrical Department & Boiler House, 525 Central Avenue, Johnstown, Cambria County, PA

  11. 1. VIEW OS SOUTH FRONT OF BOILER HOUSE, WITH SCALE ...

    Library of Congress Historic Buildings Survey, Historic Engineering Record, Historic Landscapes Survey

    1. VIEW OS SOUTH FRONT OF BOILER HOUSE, WITH SCALE STICK, SHOWING HEAVY SCALES OFFICE TO LEFT, LOOKING NORTH - Marvine Colliery, Boiler House No. 2, West side Boulevard Avenue, between East Parker Street & Route 380, Scranton, Lackawanna County, PA

  12. 1. VIEW TO EAST, WITH BOILER HOUSE TO LEFT, FILTH ...

    Library of Congress Historic Buildings Survey, Historic Engineering Record, Historic Landscapes Survey

    1. VIEW TO EAST, WITH BOILER HOUSE TO LEFT, FILTH HOIST HOUSE TO RIGHT, WITH ENGINE HOUSE AT RIGHT REAR. - Providence Sewage Treatment System, Ernest Street Pumping Station, Boiler House, Ernest Street & Allens Avenue, Providence, Providence County, RI

  13. 3. NORTH ELEVATION OF BOILER HOUSE; PARTIAL NORTH ELEVATION OF ...

    Library of Congress Historic Buildings Survey, Historic Engineering Record, Historic Landscapes Survey

    3. NORTH ELEVATION OF BOILER HOUSE; PARTIAL NORTH ELEVATION OF ENGINE HOUSE, LEFT REAR. - Providence Sewage Treatment System, Ernest Street Pumping Station, Boiler House, Ernest Street & Allens Avenue, Providence, Providence County, RI

  14. BOILER SHOP, NORTH END, WITH DROP PIT IN FOREGROUND AND ...

    Library of Congress Historic Buildings Survey, Historic Engineering Record, Historic Landscapes Survey

    BOILER SHOP, NORTH END, WITH DROP PIT IN FOREGROUND AND SP 2902 PASSENGER CAR UNDER RESTORATION, LOOKING SOUTHEAST. - Southern Pacific, Sacramento Shops, Boiler Shop, 111 I Street, Sacramento, Sacramento County, CA

  15. 32. VIEW OF BASEMENT BELOW BOILER 904 LOOKING SOUTHEAST AT ...

    Library of Congress Historic Buildings Survey, Historic Engineering Record, Historic Landscapes Survey

    32. VIEW OF BASEMENT BELOW BOILER 904 LOOKING SOUTHEAST AT TURBINE DRIVEN FORCED DRAFT FAN FOR BOILER 904. - New York, New Haven & Hartford Railroad, Cos Cob Power Plant, Sound Shore Drive, Greenwich, Fairfield County, CT

  16. Looking south at boiler feedwater pumps (steam turbine pump on ...

    Library of Congress Historic Buildings Survey, Historic Engineering Record, Historic Landscapes Survey

    Looking south at boiler feedwater pumps (steam turbine pump on left, electric motor pump on right). - Wheeling-Pittsburgh Steel Corporation, Allenport Works, Boiler House, Route 88 on West bank of Monongahela River, Allenport, Washington County, PA

  17. 38. Photocopy of photograph. STEEL PLANT, BOILERS UNDER CONSTRUCTION IN ...

    Library of Congress Historic Buildings Survey, Historic Engineering Record, Historic Landscapes Survey

    38. Photocopy of photograph. STEEL PLANT, BOILERS UNDER CONSTRUCTION IN BOILER PLANT LOCATED EAST OF MAIN STEEL PLANT, 1909. (From the Bethlehem Steel Corporation collection, Seattle, WA) - Irondale Iron & Steel Plant, Port Townsend, Jefferson County, WA

  18. 4. STEAM PLANT MARINE BOILERS WEST OF STEAM PLANT AND ...

    Library of Congress Historic Buildings Survey, Historic Engineering Record, Historic Landscapes Survey

    4. STEAM PLANT MARINE BOILERS WEST OF STEAM PLANT AND SOUTH OF ORIGINAL STEAM PLANT BOILERS, FROM SOUTH. November 13, 1990 - Crosscut Steam Plant, North side Salt River near Mill Avenue & Washington Street, Tempe, Maricopa County, AZ

  19. BOILERS COFIRING HAZARDOUS WASTE: EFFECTS OF HYSTERESIS ON PERFORMANCE MEASUREMENTS

    EPA Science Inventory

    The Hazardous Waste Engineering Research Laboratory (HWERL) has conducted full scale and pilot scale boiler testing to determine hazardous waste destruction and removal efficiencies (DRE's) and other associated boiler performance parameters during the last five years. The effort ...

  20. Corrosion fatigue boiler tube failures in waterwalls and economizers

    SciTech Connect

    McNabb, D.; Sidey, D. )

    1992-04-01

    Corrosion fatigue is a cracking mechanism initiating on the inside surface of water-touched boiler tubing at locations subject to high fatigue stresses, usually at pressure/nonpressure attachments. The mechanism is considered one of the last major sources of boiler tube failures in subcritical drum-type boilers without a root cause solution. The Electric Power Research Institute initiated a study to derive solutions to corrosion fatigue for in-service boilers and guidelines for the design of new boilers. The study consisted of a number of tasks including a survey of industry experience, field testing, theoretical stress analysis, and laboratory testing. The present volume summarizes the survey results. Ten subcritical drum-type boilers participated in the survey. The procedure involved a review of maintenance and boiler water chemistry history, and a detailed inspection of the boiler.

  1. Looking northwest at central boiler house, with 16" skelp mill ...

    Library of Congress Historic Buildings Survey, Historic Engineering Record, Historic Landscapes Survey

    Looking northwest at central boiler house, with 16" skelp mill furnace building in foreground. - U.S. Steel National Tube Works, Central Boiler House, Along Monongahela River, McKeesport, Allegheny County, PA

  2. 3. Partial view of SE sides of Boiler Building (left), ...

    Library of Congress Historic Buildings Survey, Historic Engineering Record, Historic Landscapes Survey

    3. Partial view of SE sides of Boiler Building (left), Incineration Building (to right of stack) and Machine Shop (right). - Pacific Creosoting Plant, Boiler Building, 5350 Creosote Place, Northeast, Bremerton, Kitsap County, WA

  3. 6. View along E wall of Engine Room, Boiler House ...

    Library of Congress Historic Buildings Survey, Historic Engineering Record, Historic Landscapes Survey

    6. View along E wall of Engine Room, Boiler House and Pattern Room. - Central of Georgia Railway, Savannah Repair Shops & Terminal Facilities, Engine Boiler & Pattern Building, Bounded by West Broad, Jones, West Boundary & Hull Streets, Savannah, Chatham County, GA

  4. 14. Door leading from Boiler Room to Pattern Room. ...

    Library of Congress Historic Buildings Survey, Historic Engineering Record, Historic Landscapes Survey

    14. Door leading from Boiler Room to Pattern Room. - Central of Georgia Railway, Savannah Repair Shops & Terminal Facilities, Engine Boiler & Pattern Building, Bounded by West Broad, Jones, West Boundary & Hull Streets, Savannah, Chatham County, GA

  5. 5. N elevation of Engine Room, Boiler House and Pattern ...

    Library of Congress Historic Buildings Survey, Historic Engineering Record, Historic Landscapes Survey

    5. N elevation of Engine Room, Boiler House and Pattern Room. - Central of Georgia Railway, Savannah Repair Shops & Terminal Facilities, Engine Boiler & Pattern Building, Bounded by West Broad, Jones, West Boundary & Hull Streets, Savannah, Chatham County, GA

  6. 11. Interior view of Engine Room and Boiler House showing ...

    Library of Congress Historic Buildings Survey, Historic Engineering Record, Historic Landscapes Survey

    11. Interior view of Engine Room and Boiler House showing wall buttress. - Central of Georgia Railway, Savannah Repair Shops & Terminal Facilities, Engine Boiler & Pattern Building, Bounded by West Broad, Jones, West Boundary & Hull Streets, Savannah, Chatham County, GA

  7. 2. S. elevation of Engine Room, Boiler House and Pattern ...

    Library of Congress Historic Buildings Survey, Historic Engineering Record, Historic Landscapes Survey

    2. S. elevation of Engine Room, Boiler House and Pattern Room. - Central of Georgia Railway, Savannah Repair Shops & Terminal Facilities, Engine Boiler & Pattern Building, Bounded by West Broad, Jones, West Boundary & Hull Streets, Savannah, Chatham County, GA

  8. EVALUATION OF LIME PRECIPITATION FOR TREATING BOILER TUBE CLEANING WASTES

    EPA Science Inventory

    The report gives results of an evaluation of lime precipitation for treating boiler tube cleaning wastes. In this project, wastewater samples were collected from six boiler tubeside chemical cleanings, using complexing and chelating agents. The samples represented: (1) ammoniacal...

  9. 36. REDUCTION PLANT CLOSE VIEW OF FURNACE AND BOILER ...

    Library of Congress Historic Buildings Survey, Historic Engineering Record, Historic Landscapes Survey

    36. REDUCTION PLANT - CLOSE VIEW OF FURNACE AND BOILER Reduction Plant furnace and boiler used to provide heat for drying the fish and fish offal, in their conversion to meal. - Hovden Cannery, 886 Cannery Row, Monterey, Monterey County, CA

  10. 3. GENERAL VIEW OF BOILER ROOM, LOOKING NORTH; CONTROL PANEL ...

    Library of Congress Historic Buildings Survey, Historic Engineering Record, Historic Landscapes Survey

    3. GENERAL VIEW OF BOILER ROOM, LOOKING NORTH; CONTROL PANEL AT CENTER; BOXLIKE, RIVETED HOUSING AT TOP CENTER CONTAINED AUGER FOR COAL DISTRIBUTION SYSTEM - Rath Packing Company, Boiler Room, Sycamore Street between Elm & Eighteenth Streets, Waterloo, Black Hawk County, IA

  11. 2. EAST SIDE; COAL ASH FROM BOILERS WAS BLOWN INTO ...

    Library of Congress Historic Buildings Survey, Historic Engineering Record, Historic Landscapes Survey

    2. EAST SIDE; COAL ASH FROM BOILERS WAS BLOWN INTO TANK AT RIGHT, THEN DROPPED INTO RAIL CARS FOR REMOVAL - Rath Packing Company, Boiler Room, Sycamore Street between Elm & Eighteenth Streets, Waterloo, Black Hawk County, IA

  12. Computer simulation of the fire-tube boiler hydrodynamics

    NASA Astrophysics Data System (ADS)

    Khaustov, Sergei A.; Zavorin, Alexander S.; Buvakov, Konstantin V.; Sheikin, Vyacheslav A.

    2015-01-01

    Finite element method was used for simulating the hydrodynamics of fire-tube boiler with the ANSYS Fluent 12.1.4 engineering simulation software. Hydrodynamic structure and volumetric temperature distribution were calculated. The results are presented in graphical form. Complete geometric model of the fire-tube boiler based on boiler drawings was considered. Obtained results are suitable for qualitative analysis of hydrodynamics and singularities identification in fire-tube boiler water shell.

  13. Direct contact, binary fluid geothermal boiler

    DOEpatents

    Rapier, P.M.

    1979-12-27

    Energy is extracted from geothermal brines by direct contact with a working fluid such as isobutane which is immiscible with the brine in a geothermal boiler. The geothermal boiler provides a distributor arrangement which efficiently contacts geothermal brine with the isobutane in order to prevent the entrainment of geothermal brine in the isobutane vapor which is directed to a turbine. Accordingly the problem of brine carryover through the turbine causing corrosion and scaling thereof is eliminated. Additionally the heat exchanger includes straightening vanes for preventing startup and other temporary fluctuations in the transitional zone of the boiler from causing brine carryover into the turbine. Also a screen is provided in the heat exchanger to coalesce the working fluid and to assist in defining the location of the transitional zone where the geothermal brine and the isobutane are initially mixed.

  14. Direct contact, binary fluid geothermal boiler

    DOEpatents

    Rapier, Pascal M.

    1982-01-01

    Energy is extracted from geothermal brines by direct contact with a working fluid such as isobutane which is immiscible with the brine in a geothermal boiler. The geothermal boiler provides a distributor arrangement which efficiently contacts geothermal brine with the isobutane in order to prevent the entrainment of geothermal brine in the isobutane vapor which is directed to a turbine. Accordingly the problem of brine carry-over through the turbine causes corrosion and scaling thereof is eliminated. Additionally the heat exchanger includes straightening vanes for preventing startup and other temporary fluctuations in the transitional zone of the boiler from causing brine carryover into the turbine. Also a screen is provided in the heat exchanger to coalesce the working fluid and to assist in defining the location of the transitional zone where the geothermal brine and the isobutane are initially mixed.

  15. Condensing heat exchangers for maximum boiler efficiency

    SciTech Connect

    Johnson, D.W.; DiVitto, J.G.; Rakocy, M.E.

    1994-12-31

    Until now, boiler efficiency has been limited due to the minimum temperature allowed at the stack. Heat lost up the stack was in exchange for keeping the flue gas temperature above the water vapor dew point. If water vapor was allowed to condense out, rapid deterioration, due to acid corrosion, of the outlet duct and stack would result. With the development of the condensing heat exchanger, boiler efficiency can now exceed 90%. Approximately 1% gain in boiler efficiency can be expected for every 40 F (4.5 C) reduction in flue gas stack temperature. In the CHX{reg_sign} condensing heat exchanger, all gas wetted surfaces are covered with DuPont Teflon{reg_sign}. The Teflon covered heat exchanger surfaces are impervious to all acids normally resulting from the combustion of fossil fuels. This allows the flue gas to be cooled to below the water vapor dew point with no subsequent corrosion of the heat exchanger surfaces.

  16. How People Actually Use Thermostats

    SciTech Connect

    Meier, Alan; Aragon, Cecilia; Hurwitz, Becky; Mujumdar, Dhawal; Peffer, Therese; Perry, Daniel; Pritoni, Marco

    2010-08-15

    Residential thermostats have been a key element in controlling heating and cooling systems for over sixty years. However, today's modern programmable thermostats (PTs) are complicated and difficult for users to understand, leading to errors in operation and wasted energy. Four separate tests of usability were conducted in preparation for a larger study. These tests included personal interviews, an on-line survey, photographing actual thermostat settings, and measurements of ability to accomplish four tasks related to effective use of a PT. The interviews revealed that many occupants used the PT as an on-off switch and most demonstrated little knowledge of how to operate it. The on-line survey found that 89% of the respondents rarely or never used the PT to set a weekday or weekend program. The photographic survey (in low income homes) found that only 30% of the PTs were actually programmed. In the usability test, we found that we could quantify the difference in usability of two PTs as measured in time to accomplish tasks. Users accomplished the tasks in consistently shorter times with the touchscreen unit than with buttons. None of these studies are representative of the entire population of users but, together, they illustrate the importance of improving user interfaces in PTs.

  17. Effect of chlorine on furnace wall corrosion in utility boilers

    SciTech Connect

    Kung, S.C.; Daniel, P.L.; Seeley, R.R.

    1996-08-01

    The corrosion resistance of several commercial alloys was investigated in laboratory retort tests under a reducing/sulfidizing mixed gas at 700 and 900 F (371 and 482 C) for 1,000 hours. The test conditions were designed to simulate the corrosion of furnace walls in the combustion zone of utility boilers burning sulfur/chlorine-bearing coal substoichiometrically. Corrosion rates of these alloys were determined and compared to those obtained from a previous study in which the same alloys were evaluated under chlorine-free substoichiometric combustion environments. Results of the two studies reveal that the presence of chlorine in the reducing/sulfidizing mixed gas has a negligible effect on the corrosion behavior of these alloys in this gas at 700 F (371 C), whereas a beneficial effect was observed at 900 F (482 C). The beneficial effect implies that the presence of HCl may impede the sulfidation attack by H{sub 2}S under certain substoichiometric combustion environments.

  18. 16 CFR Appendix G7 to Part 305 - Boilers (Oil)

    Code of Federal Regulations, 2014 CFR

    2014-01-01

    ... 16 Commercial Practices 1 2014-01-01 2014-01-01 false Boilers (Oil) G7 Appendix G7 to Part 305... RULEâ) Appendix G7 to Part 305—Boilers (Oil) Type Range of annual fuel utilization efficiencies (AFUEs) Low High Oil Boilers Manufactured Before the Compliance Date of DOE Regional Standards for...

  19. 49 CFR 230.30 - Lap-joint seam boilers.

    Code of Federal Regulations, 2014 CFR

    2014-10-01

    ... 49 Transportation 4 2014-10-01 2014-10-01 false Lap-joint seam boilers. 230.30 Section 230.30... Inspection and Repair § 230.30 Lap-joint seam boilers. Every boiler having lap-joint longitudinal seams... annual inspection so that an inspection of the entire joint, inside and out, can be made, taking...

  20. 49 CFR 230.30 - Lap-joint seam boilers.

    Code of Federal Regulations, 2012 CFR

    2012-10-01

    ... 49 Transportation 4 2012-10-01 2012-10-01 false Lap-joint seam boilers. 230.30 Section 230.30... Inspection and Repair § 230.30 Lap-joint seam boilers. Every boiler having lap-joint longitudinal seams... annual inspection so that an inspection of the entire joint, inside and out, can be made, taking...

  1. 49 CFR 230.30 - Lap-joint seam boilers.

    Code of Federal Regulations, 2013 CFR

    2013-10-01

    ... 49 Transportation 4 2013-10-01 2013-10-01 false Lap-joint seam boilers. 230.30 Section 230.30... Inspection and Repair § 230.30 Lap-joint seam boilers. Every boiler having lap-joint longitudinal seams... annual inspection so that an inspection of the entire joint, inside and out, can be made, taking...

  2. 49 CFR 230.30 - Lap-joint seam boilers.

    Code of Federal Regulations, 2010 CFR

    2010-10-01

    ... 49 Transportation 4 2010-10-01 2010-10-01 false Lap-joint seam boilers. 230.30 Section 230.30... Inspection and Repair § 230.30 Lap-joint seam boilers. Every boiler having lap-joint longitudinal seams... annual inspection so that an inspection of the entire joint, inside and out, can be made, taking...

  3. 46 CFR 109.205 - Inspection of boilers and machinery.

    Code of Federal Regulations, 2013 CFR

    2013-10-01

    ... 46 Shipping 4 2013-10-01 2013-10-01 false Inspection of boilers and machinery. 109.205 Section 109... OPERATIONS Tests, Drills, and Inspections § 109.205 Inspection of boilers and machinery. The chief engineer or engineer in charge, before he assumes charge of the boilers and machinery of a unit shall...

  4. 30 CFR 77.411 - Compressed air and boilers; general.

    Code of Federal Regulations, 2012 CFR

    2012-07-01

    ... 30 Mineral Resources 1 2012-07-01 2012-07-01 false Compressed air and boilers; general. 77.411... COAL MINES Safeguards for Mechanical Equipment § 77.411 Compressed air and boilers; general. All boilers and pressure vessels shall be constructed, installed, and maintained in accordance with...

  5. 23. VIEW FROM CATWALK OF EAST BOILER ROOM LOOKING NORTH. ...

    Library of Congress Historic Buildings Survey, Historic Engineering Record, Historic Landscapes Survey

    23. VIEW FROM CATWALK OF EAST BOILER ROOM LOOKING NORTH. BOILERS 900 AND 901 ARE ON THE LEFT, BOILERS 902 AND 903 ARE ON THE RIGHT. - New York, New Haven & Hartford Railroad, Cos Cob Power Plant, Sound Shore Drive, Greenwich, Fairfield County, CT

  6. 30 CFR 77.411 - Compressed air and boilers; general.

    Code of Federal Regulations, 2010 CFR

    2010-07-01

    ... 30 Mineral Resources 1 2010-07-01 2010-07-01 false Compressed air and boilers; general. 77.411... COAL MINES Safeguards for Mechanical Equipment § 77.411 Compressed air and boilers; general. All boilers and pressure vessels shall be constructed, installed, and maintained in accordance with...

  7. 46 CFR 176.812 - Pressure vessels and boilers.

    Code of Federal Regulations, 2011 CFR

    2011-10-01

    ... 46 Shipping 7 2011-10-01 2011-10-01 false Pressure vessels and boilers. 176.812 Section 176.812... TONS) INSPECTION AND CERTIFICATION Material Inspections § 176.812 Pressure vessels and boilers. (a.... (b) Periodic inspection and testing requirements for boilers are contained in § 61.05 in subchapter...

  8. 16 CFR Appendix G8 to Part 305 - Boilers (Electric)

    Code of Federal Regulations, 2014 CFR

    2014-01-01

    ... 16 Commercial Practices 1 2014-01-01 2014-01-01 false Boilers (Electric) G8 Appendix G8 to Part... LABELING RULEâ) Appendix G8 to Part 305—Boilers (Electric) Type Range of annual fuel utilization efficiencies (AFUEs) Low High Electric Boilers 100 100...

  9. 46 CFR 109.205 - Inspection of boilers and machinery.

    Code of Federal Regulations, 2012 CFR

    2012-10-01

    ... 46 Shipping 4 2012-10-01 2012-10-01 false Inspection of boilers and machinery. 109.205 Section 109... OPERATIONS Tests, Drills, and Inspections § 109.205 Inspection of boilers and machinery. The chief engineer or engineer in charge, before he assumes charge of the boilers and machinery of a unit shall...

  10. 26. VIEW OF SOUTHERN PORTION OF EAST BOILER ROOM LOOKING ...

    Library of Congress Historic Buildings Survey, Historic Engineering Record, Historic Landscapes Survey

    26. VIEW OF SOUTHERN PORTION OF EAST BOILER ROOM LOOKING EAST AT BOILER 904. BOILER 904 WAS MANUFACTURED BY RILEY STOKER AND INSTALLED IN 1944. ORIGINALLY FUELED BY PULVERIZED COAL, IT WAS CONVERTED TO GAS/OIL OPERATION IN 1978 AND OPERATED UNTIL THE PLANT CLOSED. - New York, New Haven & Hartford Railroad, Cos Cob Power Plant, Sound Shore Drive, Greenwich, Fairfield County, CT

  11. 46 CFR 109.205 - Inspection of boilers and machinery.

    Code of Federal Regulations, 2014 CFR

    2014-10-01

    ... 46 Shipping 4 2014-10-01 2014-10-01 false Inspection of boilers and machinery. 109.205 Section 109... OPERATIONS Tests, Drills, and Inspections § 109.205 Inspection of boilers and machinery. The chief engineer or engineer in charge, before he assumes charge of the boilers and machinery of a unit shall...

  12. Overview of Boiler House and Sheet Metal and Electrical Shops ...

    Library of Congress Historic Buildings Survey, Historic Engineering Record, Historic Landscapes Survey

    Overview of Boiler House and Sheet Metal and Electrical Shops Building (center - with single large chimney), note the monitor on the original section of the Boiler House Building, view facing north - Kahului Cannery, Plant No. 28, Boiler House, Sheet Metal and Electrical Shops, 120 Kane Street, Kahului, Maui County, HI

  13. 30 CFR 77.411 - Compressed air and boilers; general.

    Code of Federal Regulations, 2011 CFR

    2011-07-01

    ... 30 Mineral Resources 1 2011-07-01 2011-07-01 false Compressed air and boilers; general. 77.411... COAL MINES Safeguards for Mechanical Equipment § 77.411 Compressed air and boilers; general. All boilers and pressure vessels shall be constructed, installed, and maintained in accordance with...

  14. 30 CFR 77.411 - Compressed air and boilers; general.

    Code of Federal Regulations, 2014 CFR

    2014-07-01

    ... 30 Mineral Resources 1 2014-07-01 2014-07-01 false Compressed air and boilers; general. 77.411... COAL MINES Safeguards for Mechanical Equipment § 77.411 Compressed air and boilers; general. All boilers and pressure vessels shall be constructed, installed, and maintained in accordance with...

  15. 35. VIEW LOOKING EAST IN SOUTH END OF EAST BOILER ...

    Library of Congress Historic Buildings Survey, Historic Engineering Record, Historic Landscapes Survey

    35. VIEW LOOKING EAST IN SOUTH END OF EAST BOILER ROOM. CYLINDRICAL TANKS ARE WORTHINGTON DEAERATORS. THESE REMOVED AIR FROM BOILER FEED WATER TO MINIMIZE CORROSION AND PITTING OF THE BOILER TUBES. AIR REMOVAL ALSO HELPED AVOID THE FORMATION OF FOAM IN THE SYSTEM. - New York, New Haven & Hartford Railroad, Cos Cob Power Plant, Sound Shore Drive, Greenwich, Fairfield County, CT

  16. 30 CFR 77.411 - Compressed air and boilers; general.

    Code of Federal Regulations, 2013 CFR

    2013-07-01

    ... 30 Mineral Resources 1 2013-07-01 2013-07-01 false Compressed air and boilers; general. 77.411... COAL MINES Safeguards for Mechanical Equipment § 77.411 Compressed air and boilers; general. All boilers and pressure vessels shall be constructed, installed, and maintained in accordance with...

  17. 16 CFR Appendix G6 to Part 305 - Boilers (Gas)

    Code of Federal Regulations, 2014 CFR

    2014-01-01

    ... 16 Commercial Practices 1 2014-01-01 2014-01-01 false Boilers (Gas) G6 Appendix G6 to Part 305... RULEâ) Appendix G6 to Part 305—Boilers (Gas) Type Range of annual fuel utilization efficiencies (AFUEs) Low High Gas (Except Steam) Boilers Manufactured Before the Compliance Date of DOE Regional...

  18. 46 CFR 115.812 - Pressure vessels and boilers.

    Code of Federal Regulations, 2010 CFR

    2010-10-01

    ... 46 Shipping 4 2010-10-01 2010-10-01 false Pressure vessels and boilers. 115.812 Section 115.812... CERTIFICATION Material Inspections § 115.812 Pressure vessels and boilers. (a) Pressure vessels must be tested... testing requirements for boilers are contained in § 61.05 in subchapter F of this chapter....

  19. 46 CFR 109.205 - Inspection of boilers and machinery.

    Code of Federal Regulations, 2011 CFR

    2011-10-01

    ... 46 Shipping 4 2011-10-01 2011-10-01 false Inspection of boilers and machinery. 109.205 Section 109... OPERATIONS Tests, Drills, and Inspections § 109.205 Inspection of boilers and machinery. The chief engineer or engineer in charge, before he assumes charge of the boilers and machinery of a unit shall...

  20. 46 CFR 109.205 - Inspection of boilers and machinery.

    Code of Federal Regulations, 2010 CFR

    2010-10-01

    ... 46 Shipping 4 2010-10-01 2010-10-01 false Inspection of boilers and machinery. 109.205 Section 109... OPERATIONS Tests, Drills, and Inspections § 109.205 Inspection of boilers and machinery. The chief engineer or engineer in charge, before he assumes charge of the boilers and machinery of a unit shall...

  1. 40 CFR 63.988 - Incinerators, boilers, and process heaters.

    Code of Federal Regulations, 2013 CFR

    2013-07-01

    ... status requirements of 40 CFR part 265, subpart O; (ii) A boiler or process heater with a design heat... 40 CFR part 266, subpart H; or (B) The boiler or process heater has certified compliance with the interim status requirements of 40 CFR part 266, subpart H. (c) Incinerator, boiler, and process...

  2. 40 CFR 63.988 - Incinerators, boilers, and process heaters.

    Code of Federal Regulations, 2011 CFR

    2011-07-01

    ... status requirements of 40 CFR part 265, subpart O; (ii) A boiler or process heater with a design heat... 40 CFR part 266, subpart H; or (B) The boiler or process heater has certified compliance with the interim status requirements of 40 CFR part 266, subpart H. (c) Incinerator, boiler, and process...

  3. 40 CFR 63.988 - Incinerators, boilers, and process heaters.

    Code of Federal Regulations, 2012 CFR

    2012-07-01

    ... status requirements of 40 CFR part 265, subpart O; (ii) A boiler or process heater with a design heat... 40 CFR part 266, subpart H; or (B) The boiler or process heater has certified compliance with the interim status requirements of 40 CFR part 266, subpart H. (c) Incinerator, boiler, and process...

  4. 40 CFR 63.988 - Incinerators, boilers, and process heaters.

    Code of Federal Regulations, 2014 CFR

    2014-07-01

    ... status requirements of 40 CFR part 265, subpart O; (ii) A boiler or process heater with a design heat... 40 CFR part 266, subpart H; or (B) The boiler or process heater has certified compliance with the interim status requirements of 40 CFR part 266, subpart H. (c) Incinerator, boiler, and process...

  5. Design of a 350 MWe CFB boiler

    SciTech Connect

    Darling, S.L.; Li, X.

    1997-12-31

    Circulating fluidized bed (CFB) boilers have been in operation for many years in industrial steam and power generation applications, primarily in the 50--100 MWe size range. Recently, several utility-scale CFB boilers have entered service and several others are under construction, in the 150--250 MWe size range. The next step for CFB technology is the 350 MWe size range. This paper will describe Foster Wheeler`s utility CFB experience, scale-up philosophy and the major design features of the 350 MWe CFB design.

  6. Compact CFB: The next generation CFB boiler

    SciTech Connect

    Utt, J.

    1996-12-31

    The next generation of compact circulating fluidized bed (CFB) boilers is described in outline form. The following topics are discussed: compact CFB = pyroflow + compact separator; compact CFB; compact separator is a breakthrough design; advantages of CFB; new design with substantial development history; KUHMO: successful demo unit; KUHMO: good performance over load range with low emissions; KOKKOLA: first commercial unit and emissions; KOKKOLA: first commercial unit and emissions; compact CFB installations; next generation CFB boiler; grid nozzle upgrades; cast segmented vortex finders; vortex finder installation; ceramic anchors; pre-cast vertical bullnose; refractory upgrades; and wet gunning.

  7. Transients in a circulating fluidized bed boiler

    NASA Astrophysics Data System (ADS)

    Baskakov, A. P.; Munts, V. A.; Pavlyuk, E. Yu.

    2013-11-01

    Transients in a circulating fluidized bed boiler firing biomass are considered. An attempt is made to describe transients with the use of concepts applied in the automatic control theory. The parameters calculated from an analysis of unsteady heat balance equations are compared with the experimental data obtained in the 12-MW boiler of the Chalmers University of Technology. It is demonstrated that these equations describe the transient modes of operation with good accuracy. Dependences for calculating the time constants of unsteady processes are obtained.

  8. GUIDELINES FOR INDUSTRIAL BOILER PERFORMANCE IMPROVEMENT. (BOILER ADJUSTMENT PROCEDURES TO MINIMIZE AIR POLLUTION AND TO ACHIEVE EFFICIENT USE OF FUEL)

    EPA Science Inventory

    Recommended procedures for improving industrial boiler performance to minimize air pollution and to achieve efficient use of fuel are given. It is intended for use by industrial boiler operators to perform an efficiency and emissions tune-up on boilers firing gas, oil, or coal. P...

  9. Super Boiler: Packed Media/Transport Membrane Boiler Development and Demonstration

    SciTech Connect

    Liss, William E; Cygan, David F

    2013-04-17

    Gas Technology Institute (GTI) and Cleaver-Brooks developed a new gas-fired steam generation system the Super Boiler for increased energy efficiency, reduced equipment size, and reduced emissions. The system consists of a firetube boiler with a unique staged furnace design, a two-stage burner system with engineered internal recirculation and inter-stage cooling integral to the boiler, unique convective pass design with extended internal surfaces for enhanced heat transfer, and a novel integrated heat recovery system to extract maximum energy from the flue gas. With these combined innovations, the Super Boiler technical goals were set at 94% HHV fuel efficiency, operation on natural gas with <5 ppmv NOx (referenced to 3%O2), and 50% smaller than conventional boilers of similar steam output. To demonstrate these technical goals, the project culminated in the industrial demonstration of this new high-efficiency technology on a 300 HP boiler at Clement Pappas, a juice bottler located in Ontario, California. The Super Boiler combustion system is based on two stage combustion which combines air staging, internal flue gas recirculation, inter-stage cooling, and unique fuel-air mixing technology to achieve low emissions rather than external flue gas recirculation which is most commonly used today. The two-stage combustion provides lower emissions because of the integrated design of the boiler and combustion system which permit precise control of peak flame temperatures in both primary and secondary stages of combustion. To reduce equipment size, the Super Boiler's dual furnace design increases radiant heat transfer to the furnace walls, allowing shorter overall furnace length, and also employs convective tubes with extended surfaces that increase heat transfer by up to 18-fold compared to conventional bare tubes. In this way, a two-pass boiler can achieve the same efficiency as a traditional three or four-pass firetube boiler design. The Super Boiler is consequently up to

  10. Design and experience with utility-scale CFB boilers

    SciTech Connect

    Darling, S.L.; Hennenfent, M.

    1995-12-31

    Circulating fluidized bed (CFB) boilers have been in operation for many years in industrial steam and power generation applications, primarily in the 50-100 MWe range. In the past few years, however, several utility-scale CFB boilers have entered service. The scale-up of the Foster Wheeler Pyropower, Inc. CFB boilers has proceeded smoothly, and today FWPI CFB boilers up to 180 MWe are in operation, two 235 MWe boilers are now under construction, and other large units are in the design stage.

  11. REBURN TECHNOLOGY FOR BOILER NOX CONTROL

    EPA Science Inventory

    The paper reports the progress principally of design-relate phases of a demonstration of reburning on a large cyclone-fired boiler, for which coal is the primary fuel and natural gas, the reburn fuel. Reburn system design criteria are presented, as well as the methodology and res...

  12. Digital radiographic systems detect boiler tube cracks

    SciTech Connect

    Walker, S.

    2008-06-15

    Boiler water wall leaks have been a major cause of steam plant forced outages. But conventional nondestructive evaluation techniques have a poor track record of detecting corrosion fatigue cracking on the inside surface of the cold side of waterwall tubing. EPRI is performing field trials of a prototype direct-digital radiographic system that promises to be a game changer. 8 figs.

  13. Micronized coal solves mushroom grower's boiler headaches

    SciTech Connect

    Reason, J.

    1984-03-01

    A brief account is given of a Utah mushroom grower who has replaced two underfeed stoker-fired boilers requiring 7 attendants by an ultra-fine pulverised coal-fired system. The coal is ground in a proprietary rotary grinder to 80% through a 325-mesh screen. Information is presented on the mill and the special refractory burners required.

  14. REBURNING APPLICATION TO FIRETUBE PACKAGE BOILERS

    EPA Science Inventory

    The report gives results of pilot-scale experimental research that examined the physical and chemical phenomena associated with the NOx control technology of reburning applied to gas- and liquid-fired firetube package boilers. Reburning (staged fuel combustion) diverts some of th...

  15. Microphone Detects Boiler-Tube Leaks

    NASA Technical Reports Server (NTRS)

    Parthasarathy, S. P.

    1985-01-01

    Unit simple, sensitive, rugged, and reliable. Diaphragmless microphone detects leaks from small boiler tubes. Porous plug retains carbon granules in tube while allowing pressure changes to penetrate to granules. Has greater life expectancy than previous controllers and used in variety of hot corrosive atmospheres.

  16. Is That Boiler Ready To Blow?

    ERIC Educational Resources Information Center

    Robinson, Glenn S.; Trombley, Robert E.

    2001-01-01

    Discusses implementation of a thorough assessment program to determine the condition of boilers, pressure vessels and other plant equipment to determine the feasibility of part or entire system replacement. Assessment basics are examined as are tips for selecting the right inspection and engineering contractor for assessments. (GR)

  17. 30 CFR 57.13030 - Boilers.

    Code of Federal Regulations, 2011 CFR

    2011-07-01

    ... Stamp for Safety and Safety Relief Valves D-VR2Outline of Basic Elements of Written Quality Control... Resources MINE SAFETY AND HEALTH ADMINISTRATION, DEPARTMENT OF LABOR METAL AND NONMETAL MINE SAFETY AND HEALTH SAFETY AND HEALTH STANDARDS-UNDERGROUND METAL AND NONMETAL MINES Compressed Air and Boilers §...

  18. 30 CFR 57.13030 - Boilers.

    Code of Federal Regulations, 2014 CFR

    2014-07-01

    ... Stamp for Safety and Safety Relief Valves D-VR2Outline of Basic Elements of Written Quality Control... Resources MINE SAFETY AND HEALTH ADMINISTRATION, DEPARTMENT OF LABOR METAL AND NONMETAL MINE SAFETY AND HEALTH SAFETY AND HEALTH STANDARDS-UNDERGROUND METAL AND NONMETAL MINES Compressed Air and Boilers §...

  19. 30 CFR 56.13030 - Boilers.

    Code of Federal Regulations, 2013 CFR

    2013-07-01

    ... Safety Relief Valves D-VR2Outline of Basic Elements of Written Quality Control System for Repairers of... Resources MINE SAFETY AND HEALTH ADMINISTRATION, DEPARTMENT OF LABOR METAL AND NONMETAL MINE SAFETY AND HEALTH SAFETY AND HEALTH STANDARDS-SURFACE METAL AND NONMETAL MINES Compressed Air and Boilers §...

  20. 30 CFR 57.13030 - Boilers.

    Code of Federal Regulations, 2012 CFR

    2012-07-01

    ... Stamp for Safety and Safety Relief Valves D-VR2Outline of Basic Elements of Written Quality Control... Resources MINE SAFETY AND HEALTH ADMINISTRATION, DEPARTMENT OF LABOR METAL AND NONMETAL MINE SAFETY AND HEALTH SAFETY AND HEALTH STANDARDS-UNDERGROUND METAL AND NONMETAL MINES Compressed Air and Boilers §...

  1. 30 CFR 56.13030 - Boilers.

    Code of Federal Regulations, 2014 CFR

    2014-07-01

    ... Safety Relief Valves D-VR2Outline of Basic Elements of Written Quality Control System for Repairers of... Resources MINE SAFETY AND HEALTH ADMINISTRATION, DEPARTMENT OF LABOR METAL AND NONMETAL MINE SAFETY AND HEALTH SAFETY AND HEALTH STANDARDS-SURFACE METAL AND NONMETAL MINES Compressed Air and Boilers §...

  2. 30 CFR 56.13030 - Boilers.

    Code of Federal Regulations, 2011 CFR

    2011-07-01

    ... Safety Relief Valves D-VR2Outline of Basic Elements of Written Quality Control System for Repairers of... Resources MINE SAFETY AND HEALTH ADMINISTRATION, DEPARTMENT OF LABOR METAL AND NONMETAL MINE SAFETY AND HEALTH SAFETY AND HEALTH STANDARDS-SURFACE METAL AND NONMETAL MINES Compressed Air and Boilers §...

  3. 30 CFR 56.13030 - Boilers.

    Code of Federal Regulations, 2012 CFR

    2012-07-01

    ... Safety Relief Valves D-VR2Outline of Basic Elements of Written Quality Control System for Repairers of... Resources MINE SAFETY AND HEALTH ADMINISTRATION, DEPARTMENT OF LABOR METAL AND NONMETAL MINE SAFETY AND HEALTH SAFETY AND HEALTH STANDARDS-SURFACE METAL AND NONMETAL MINES Compressed Air and Boilers §...

  4. 30 CFR 57.13030 - Boilers.

    Code of Federal Regulations, 2013 CFR

    2013-07-01

    ... Stamp for Safety and Safety Relief Valves D-VR2Outline of Basic Elements of Written Quality Control... Resources MINE SAFETY AND HEALTH ADMINISTRATION, DEPARTMENT OF LABOR METAL AND NONMETAL MINE SAFETY AND HEALTH SAFETY AND HEALTH STANDARDS-UNDERGROUND METAL AND NONMETAL MINES Compressed Air and Boilers §...

  5. New thinking for the boiler room.

    PubMed

    Rose, Wayne

    2008-09-01

    Wayne Rose, marketing manager at integrated plant room manufacturer Armstrong Integrated Systems, explains how increasing use of off-site manufacture, the latest 3D modelling technology, and advances in control technology, are revolutionising boiler room design and construction. PMID:18822819

  6. Interactive simulation and analysis of emission reduction systems in commercial boilers

    SciTech Connect

    Diachin, D.; Freitag, L.; Heath, D.; Herzog, J.; Plassmann, P.; Michels, W.

    1996-12-31

    In this paper the authors describe an interactive virtual environment developed to model an emission reduction system for commercial boilers. The interactive environment is used to optimize the performance of the reduction system through the spatial adjustment and spray reconfiguration of reagent injectors. They describe the three principal components of the system: a computational model for the particle dynamics, a three-dimensional display device and graphics environment, and the communication layer that allows the interaction of the user in the visualization environment with the computational model. Timing results for each component are given for three hardware configurations that demonstrate the real-time performance of this tool.

  7. The next generation of oxy-fuel boiler systems

    SciTech Connect

    Ochs, Thomas L.; Gross, Alex; Patrick, Brian; Oryshchyn, Danylo B.; Summers, Cathy A.; Turner, Paul C.

    2005-01-01

    Research in the area of oxy-fuel combustion which is being pioneered by Jupiter Oxygen Corporation combined with boiler research conducted by the USDOE/Albany Research Center has been applied to designing the next generation of oxy-fuel combustion systems. The new systems will enhance control of boiler systems during turn-down and improve response time while improving boiler efficiency. These next generation boiler systems produce a combustion product that has been shown to be well suited for integrated pollutant removal. These systems have the promise of reducing boiler foot-print and boiler construction costs. The modularity of the system opens the possibility of using this design for replacement of boilers for retrofit on existing systems.

  8. Design and experience with large-size CFB boilers

    SciTech Connect

    Darling, S.L.

    1994-12-31

    CFB boilers have been in operation for many years in industrial steam and power generation applications demonstrating the low SO{sub x}/NO{sub x} emissions and fuel flexibility of the technology. In the past few years, several large-size CFB boilers (over 100 MWe) have entered service and are operating successfully. On the basis of this experience, CFB boilers up to 400 MWe in size are now being offered with full commercial guarantees. Such large CFB boilers will be of interest to countries with strict emission regulations or the need to reduce emissions, and to countries with both a large need for additional power and low grade indigenous solid fuel. This paper will describe Ahlstrom Pyropower`s scale-up of the AHLSTROM PYROFLOW CFB boiler, experience with large-size CFB boilers and the design features of CFB boilers in the 400 MWe size range.

  9. Design considerations of B&W internal circulation CFB boilers

    SciTech Connect

    Kavidass, S.; Belin, F.; James, D.E.

    1995-12-31

    Worldwide, the use of Circulating Fluidized-Bed (CFB) boiler technology is rapidly increasing due to the ability to burn low grade fuels while meeting the required NO{sub x}, SO{sub 2}, CO, VOC, and particulate emissions requirements. The CFB boiler can produce steam economically for process and electric power generation. This paper discusses various aspects of Babcock & Wilcox (B&W) internal recirculation circulating fluidized-bed (IR-CFB) boiler design including fuel, boiler process parameters, and emissions. The B&W CFB boiler is unique in design. It utilizes proven impact-type particle separators (U-beams) with in-furnace solids recirculation recirculation. The paper describes the methodology for setting up process parameters, heat duty, boiler design, including auxiliary equipment selection and advantages. The paper also updates the ongoing IR-CFB boiler contracts.

  10. Stress Assisted Corrosion in Boiler Tubes - Failure Analysis

    SciTech Connect

    Singh, Preet M; Pawel, Steven J; Yang, Dong; Mahmood, Jamshad

    2007-01-01

    Stress assisted corrosion (SAC) of carbon steel boiler tubes is one of the major causes of waterside failure in industrial boilers. SAC is a major concern for kraft recovery boilers in the pulp and paper industry as any water leak into the furnace can cause a smelt-water explosion in the boiler. Failed carbon steel boiler tubes from different kraft recovery boilers were examined to understand the role of carbon steel microstructure on crack initiation and SAC crack morphology. A number of carbon steel tubes showed a deep decarburized layer on the inner surface (water-touched) and also an unusually large grain size at the inner tube surface. SAC cracks were found to initiate in these areas with large-graineddecarburized microstructure. Tubes without such microstructure were also found to have SAC cracks. It was found that the decarburization and large grained microstructure may facilitate initiation and growth but is not necessary for SAC of carbon steel boiler tubes.

  11. Oxy-Combustion Boiler Material Development

    SciTech Connect

    Michael Gagliano; Andrew Seltzer; Hans Agarwal; Archie Robertson; Lun Wang

    2012-01-31

    Under U.S. Department of Energy Cooperative Agreement No. DE-NT0005262 Foster Wheeler North America Corp conducted a laboratory test program to determine the effect of oxy-combustion on boiler tube corrosion. In this program, CFD modeling was used to predict the gas compositions that will exist throughout and along the walls of air-fired and oxy-fired boilers operating with low to high sulfur coals. Test coupons of boiler tube materials were coated with deposits representative of those coals and exposed to the CFD predicted flue gases for up to 1000 hours. The tests were conducted in electric tube furnaces using oxy-combustion and air-fired flue gases synthesized from pressurized cylinders. Following exposure, the test coupons were evaluated to determine the total metal wastage experienced under air and oxy-combustions conditions and materials recommendations were made. Similar to air-fired operation, oxy-combustion corrosion rates were found to vary with the boiler material, test temperature, deposit composition, and gas composition. Despite this, comparison of air-fired and oxy-fired corrosion rates showed that oxy-firing rates were, for the most part, similar to, if not lower than those of air-firing; this finding applied to the seven furnace waterwall materials (wrought and weld overlay) and the ten superheater/reheater materials (wrought and weld overlay) that were tested. The results of the laboratory oxy-combustion tests, which are based on a maximum bulk flue gas SO{sub 2} level of 3200 ppmv (wet) / 4050 ppmv (dry), suggest that, from a corrosion standpoint, the materials used in conventional subcritical and supercritical, air-fired boilers should also be suitable for oxy-combustion retrofits. Although the laboratory test results are encouraging, they are only the first step of a material evaluation process and it is recommended that follow-on corrosion tests be conducted in coal-fired boilers operating under oxy-combustion to provide longer term (one to

  12. Oxy-Combustion Boiler Material Development

    SciTech Connect

    Gagliano, Michael; Seltzer, Andrew; Agarwal, Hans; Robertson, Archie; Wang, Lun

    2012-01-31

    Under U.S. Department of Energy Cooperative Agreement No. DE-NT0005262 Foster Wheeler North America Corp conducted a laboratory test program to determine the effect of oxy-combustion on boiler tube corrosion. In this program, CFD modeling was used to predict the gas compositions that will exist throughout and along the walls of air-fired and oxy-fired boilers operating with low to high sulfur coals. Test coupons of boiler tube materials were coated with deposits representative of those coals and exposed to the CFD predicted flue gases for up to 1000 hours. The tests were conducted in electric tube furnaces using oxy-combustion and air-fired flue gases synthesized from pressurized cylinders. Following exposure, the test coupons were evaluated to determine the total metal wastage experienced under air and oxy-combustions conditions and materials recommendations were made. Similar to air-fired operation, oxy-combustion corrosion rates were found to vary with the boiler material, test temperature, deposit composition, and gas composition. Despite this, comparison of air-fired and oxy-fired corrosion rates showed that oxy-firing rates were, for the most part, similar to, if not lower than those of air-firing; this finding applied to the seven furnace waterwall materials (wrought and weld overlay) and the ten superheater/reheater materials (wrought and weld overlay) that were tested. The results of the laboratory oxy-combustion tests, which are based on a maximum bulk flue gas SO2 level of 3200 ppmv (wet) / 4050 ppmv (dry), suggest that, from a corrosion standpoint, the materials used in conventional subcritical and supercritical, air-fired boilers should also be suitable for oxy-combustion retrofits. Although the laboratory test results are encouraging, they are only the first step of a material evaluation process and it is recommended that follow-on corrosion tests be conducted in coal-fired boilers operating under oxy-combustion to provide longer term (one to two year

  13. Startup, Commissioning and Operation of Fenyi 100MW CFB Boiler

    NASA Astrophysics Data System (ADS)

    Wang, Zhiwei; Yu, Wugao; Bo, Shi

    The first 100MW CFB boiler, designed by the Thermal Power Research Institute and manufactured by Harbin Boiler Company Limited, has been successfully running in Jiangxi Fenyi Power Plant since 2003. Local high ash content anthracite and lean coal that are very difficult to burn out are used in the 100 MW CFB boiler. The results of the 100MW CFB boiler shows that the CFB boiler can run in 30% MCR and startup with two under bed burners, and the boiler efficiency higher than 88% can be got after the combustion modification test. The CFB boiler can be operated with full load and reaches design parameters. The emissions of NO, N2O and CO are less than 7Omg/m3, 30mg/m3, and 125mg/m3, respectively, and SO2 less than 400mg/m3 after limestone injection. The bottom ash temperature from bed ash coolers is less than 120°C after its modification. Coal blockage at the coal storage silo is the main problem influencing the CFB boiler continuous operation. The running experiences for 5 years proved that the CFB boiler performance is successful, and the results were applied in 210 MW and 330 MW CFB Boiler design of Fenyi Power Plant.

  14. Design for a 350 MWe class CFB boiler

    SciTech Connect

    Darling, S.L.

    1998-07-01

    This paper describes Foster Wheeler's design for a 350 MWe Class boiler. Foster Wheeler's experience with large CFB boilers and with large suspension fired boilers is summarized. A reference 350 MWe CFB boiler design is presented and major design features are described along with expected performance. Areas in the CFB boiler design which benefit from suspension from boiler experience are highlighted. CFB boilers are now proven in the 150--250 MWe size range, with several in operation and many others scheduled to begin operation this year. The next step for CFB boiler technology is the 300 - 400 MWe size range. This paper will describe Foster Wheeler's design for a 350 MWe class CFB boiler, including the major design features and anticipated performance. The authors will demonstrate how Foster Wheeler's experience in designing large suspension-fired boilers in sizes over 900 MWe has been applied to the 350 MWe class CFB, in order to minimize scale-up risk and ensure high reliability. This design will bring the benefits of CFB technology, which include flexibility and low emissions, to the 350 MWe size range.

  15. Guide to Low-Emission Boiler and Combustion Equipment Selection

    SciTech Connect

    Oland, CB

    2002-05-06

    Boiler owners and operators who need additional generating capacity face a number of legal, political, environmental, economic, and technical challenges. Their key to success requires selection of an adequately sized low-emission boiler and combustion equipment that can be operated in compliance with emission standards established by state and federal regulatory agencies. Recognizing that many issues are involved in making informed selection decisions, the U.S. Department of Energy (DOE), Office of Industrial Technologies (OIT) sponsored efforts at the Oak Ridge National Laboratory (ORNL) to develop a guide for use in choosing low-emission boilers and combustion equipment. To ensure that the guide covers a broad range of technical and regulatory issues of particular interest to the commercial boiler industry, the guide was developed in cooperation with the American Boiler Manufacturers Association (ABMA), the Council of Industrial Boiler Owners (CIBO), and the U.S. Environmental Protection Agency (EPA). The guide presents topics pertaining to industrial, commercial, and institutional (ICI) boilers. Background information about various types of commercially available boilers is provided along with discussions about the fuels that they burn and the emissions that they produce. Also included are discussions about emissions standards and compliance issues, technical details related to emissions control techniques, and other important selection considerations. Although information in the guide is primarily applicable to new ICI boilers, it may also apply to existing boiler installations.

  16. BPM2.0. Fossil-Fired Boilers

    SciTech Connect

    Winslow, J.C.

    1988-01-01

    BOILER PERFORMANCE MODEL (BPM2.0) is a set of programs for predicting the heat transfer performance of fossil-fired utility boilers. The programs can model a wide variety of boiler designs, provide boiler performance estimates for coal, oil or gaseous fuels, determine the influence of slagging and fouling characteristics on boiler performance, and calculate performance factors for tradeoff analyses comparing boilers and fuels. Given a set of target operating conditions, the programs can estimate control settings, gas and steam operating profiles through the boiler, overall boiler efficiency, and fuel consumption. The programs are broken into three categories: data, calculation, and reports with a central processor program acting as the link allowing the user to access any of the data or calculation programs and easily move between programs. The calculations are divided among the following five programs: heat duty calculation, combustion calculation, furnace performance calculation, convection pass performance calculation, and air heater performance calculation. The programs can model subcritical or supercritical boilers, most configurations of convective passes including boilers that achieve final reheat steam temperature control by split back pass, boilers with as many as two reheat circuits and/or multiple attemperator stations in series, and boilers with or without economizers and/or air heaters. Either regenerative or tubular air heaters are supported. For wall-fired or tangentially-fired furnaces, the furnace performance program predicts the temperature of the flue gases leaving the furnace. It accounts for variations in excess air, gas recirculation, burner tilt, wall temperature, and wall cleanliness. For boilers having radiant panels or platens above the furnace, the convective pass program uses the results of the combustion chamber calculation to estimate the gas temperature entering the convective pass.

  17. BPM3.0. Fossil-Fired Boilers

    SciTech Connect

    Winslow, J.C.

    1992-03-01

    The BOILER PERFORMANCE MODEL (BPM3.0) is a set of programs for predicting the heat transfer performance of fossil-fired utility boilers. The programs can model a wide variety of boiler designs, provide boiler performance estimates for coal, oil or gaseous fuels, determine the influence of slagging and fouling characteristics on boiler performance, and calculate performance factors for tradeoff analyses comparing boilers and fuels. Given a set of target operating conditions, the programs can estimate control settings, gas and steam operating profiles through the boiler, overall boiler efficiency, and fuel consumption. The programs are broken into three categories: data, calculation, and reports with a central processor program acting as the link allowing the user to access any of the data or calculation programs and easily move between programs. The calculations are divided among the following five programs: heat duty calculation, combustion calculation, furnace performance calculation, convection pass performance calculation, and air heater performance calculation. The programs can model subcritical or supercritical boilers, most configurations of convective passes including boilers that achieve final reheat steam temperature control by split back pass, boilers with as many as two reheat circuits and/or multiple attemperator stations in series, and boilers with or without economizers and/or air heaters. Either regenerative or tubular air heaters are supported. For wall-fired or tangentially-fired furnaces, the furnace performance program predicts the temperature of the flue gases leaving the furnace. It accounts for variations in excess air, gas recirculation, burner tilt, wall temperature, and wall cleanliness. For boilers having radiant panels or platens above the furnace, the convective pass program uses the results of the combustion chamber calculation to estimate the gas temperature entering the convective pass.

  18. Stationary Engineers Apprenticeship. Related Training Modules. 12.1-12.9. Boilers.

    ERIC Educational Resources Information Center

    Lane Community Coll., Eugene, OR.

    This learning module, one in a series of 20 related training modules for apprentice stationary engineers, deals with boilers. Addressed in the individual instructional packages included in the module are the following topics: firetube and watertube boilers; boiler construction; procedures for operating and cleaning boilers; and boiler fittings,…

  19. 32. (Credit CBF) Boilers in the McNeil Street Station, November ...

    Library of Congress Historic Buildings Survey, Historic Engineering Record, Historic Landscapes Survey

    32. (Credit CBF) Boilers in the McNeil Street Station, November 1911: two 100 hp Atlas boilers and one Chattanooga boiler. The Atlas boilers were installed c1892, the Chattanooga boiler c1897. - McNeil Street Pumping Station, McNeil Street & Cross Bayou, Shreveport, Caddo Parish, LA

  20. 40 CFR Appendix C to Part 72 - Actual 1985 Yearly SO2 Emissions Calculation

    Code of Federal Regulations, 2013 CFR

    2013-07-01

    ... 40 Protection of Environment 17 2013-07-01 2013-07-01 false Actual 1985 Yearly SO2 Emissions Calculation C Appendix C to Part 72 Protection of Environment ENVIRONMENTAL PROTECTION AGENCY (CONTINUED) AIR PROGRAMS (CONTINUED) PERMITS REGULATION Pt. 72, App. C Appendix C to Part 72—Actual 1985 Yearly...

  1. 40 CFR Appendix C to Part 72 - Actual 1985 Yearly SO2 Emissions Calculation

    Code of Federal Regulations, 2010 CFR

    2010-07-01

    ... 40 Protection of Environment 16 2010-07-01 2010-07-01 false Actual 1985 Yearly SO2 Emissions Calculation C Appendix C to Part 72 Protection of Environment ENVIRONMENTAL PROTECTION AGENCY (CONTINUED) AIR PROGRAMS (CONTINUED) PERMITS REGULATION Pt. 72, App. C Appendix C to Part 72—Actual 1985 Yearly...

  2. Classification and quantification for boiler dust

    NASA Astrophysics Data System (ADS)

    Zeng, Zhoumo; Liang, Yi; Yang, Qing; Jin, Shijiu

    2002-09-01

    A non-intrusive optical technique for the study of moving particles and their statistics, laser phase Doppler anemometry (PDA), is used in on-line inspecting and quantifying boiler dusty. PDA collects and processes Doppler signals from moving scattering particles and provides a deterministic measure of particle velocity and statistical information about particles" size and size distribution. Furthermore, PDA is superior to the traditional intensity based optical particle analyzer, as Doppler frequency or phase shift is less susceptible to electronic noise than intensity. These features are important for reliable results, especially at in-situ application. The present system operated successfully in inspecting soot letting of coal-fired boiler, which leads to an active structure that can be applied in the conditions of limited optical access. The measuring results of soot parameters, as well as the statistics of soot are presented in this paper.

  3. Recycle device for circulating fluidized bed boilers

    SciTech Connect

    Wang, Q.; Luo, Z.Y.; Li, X.T.; Cheng, F.; Ni, M.J.; Cen, K.

    1997-12-31

    Because the pressure at the outlet of a separator is lower than that at an inlet of a furnace, a recycle device is one of the most important components of circulating fluidized bed boilers for handling circulating ash. Although it has been extensively used in circulating fluidized bed boilers, its properties have not yet been well understood. Many experiments have been conducted for a kind of recycle device and the operational properties were obtained. The experimental results show that the structure of the recycle device and aeration conditions have a strong influence on the solid flow rate and operational stability of the recycle device. The authors will discuss the effect of the major parameters, such as opening and aeration air at different locations, on solids flow rate. The operational considerations will be given in this paper.

  4. Particulate Emission Abatement for Krakow Boiler Houses

    SciTech Connect

    1998-09-01

    Environmental clean-up and pollution control are considered the foremost national priorities in Poland. The target of this cleanup is the Polish coal industry, which currently comprises over 78% of Poland`s primary energy production. This project addresses the problem of airborne dust and uncontrolled particulate emissions from boilerhouses, which represent a large fraction of the total in Poland. In Krakow alone, there are more than 2,000 uncontrolled boilers accounting for about half the total fuel use. The large number of low- capacity boilers poses both technical and economic challenges, since the cost of control equipment is a significant factor in the reduction of emissions. A new concept in dust collection, called a Core Separator, is proposed for this important application. The Core Separator is an advanced technology developed through research sponsored by the Department of Energy.

  5. Maximising safety in the boiler house.

    PubMed

    Derry, Carr

    2013-03-01

    Last month's HEJ featured an article, the second in our new series of guidance pieces aimed principally at Technician-level engineers, highlighting some of the key steps that boiler operators can take to maximise system performance and efficiency, and thus reduce running both costs and carbon footprint. In the third such article, Derry Carr, C.Env, I.Eng, BSc (Hons), M.I.Plant.E., M.S.O.E., technical manager & group gas manager at Dalkia, who is vice-chairman of the Combustion Engineering Association, examines the key regulatory and safety obligations for hospital energy managers and boiler technicians, a number of which have seen changes in recent years with revision to guidance and other documentation. PMID:23573684

  6. Anthracite culm fired fluidized-bed boiler

    SciTech Connect

    Lentz, E.C.

    1984-01-01

    The author describes a fluidised-bed boiler that has been designed by FluiDyne Engineering Corp. for the combustion of anthracite culm, a material containing about 40% ash and consisting of coal particles embedded in mineral matter. There are some 900 million tons of anthracite culm in northeast Pennsylvania within easy reach of many large metropolitan areas. It is estimated that the material can be used economically within a distance of 200 miles.

  7. Waste combustion in boilers and industrial furnaces

    SciTech Connect

    1996-12-31

    This publication contains technical papers published as they were presented at a recent specialty conference sponsored by the Air & Waste Management Association, titled Waste Combustion in Boilers and Industrial Furnaces, held March 26-27, 1996, in Kansas City, Missouri. Papers touch on compilance concerns for air pollution, air monitoring methodologies, risk assessment, and problems related to public anxiety. Separate abstracts have been indexed into the database from this proceedings.

  8. Microfine coal firing results from a retrofit gas/oil-designed industrial boiler

    SciTech Connect

    Patel, R.; Borio, R.W.; Liljedahl, G.; Miller, B.G.; Scaroni, A.W.; McGowan, J.G.

    1995-12-31

    The development of a High Efficiency Advanced Coal Combustor (HEACC) has been in progress since 1987 and the ABB Power Plant Laboratories. The initial work on this concept produced an advanced coal firing system that was capable of firing both water-based and dry pulverized coal in an industrial boiler environment. Economics may one day dictate that it makes sense to replace oil or natural gas with coal in boilers that were originally designed to burn these fuels. The objective of the current program is to demonstrate the technical and economic feasibility of retrofitting a gas/oil designed boiler to burn micronized coal. In support of this overall objective, the following specific areas were targeted: A coal handling/preparation system that can meet the technical requirements for retrofitting microfine coal on a boiler designed for burning oil or natural gas; Maintaining boiler thermal performance in accordance with specifications when burning oil or natural gas; Maintaining NOx emissions at or below 0.6 lb/MBtu; Achieving combustion efficiencies of 98% or higher; and Calculating economic payback periods as a function of key variables. The overall program has consisted of five major tasks: (1) A review of current state-of-the-art coal firing system components; (2) Design and experimental testing of a prototype HEACC burner; (3) Installation and testing of a HEACC system in a commercial retrofit application; (4) Economic evaluation of the HEACC concept for retrofit applications; and (5) Long term demonstration under commercial user demand conditions. This paper will summarize the latest key experimental results (Task 3) and the economic evaluation (Task 4) of the HEACC concept for retrofit applications. 28 figs., 6 tabs.

  9. Residual carbon from pulverized coal fired boilers 1: Size distribution and combustion reactivity

    SciTech Connect

    Hurt, R.H.; Gibbins, J.R.

    1994-08-01

    The amount of residual, or unburned, carbon in fly ash is an important concern in the design and operation of pulverized coal-fired boilers. Char oxidation is the slowest step in the coal combustion process, and the rate at which this heterogeneous reaction-proceeds has an important effect on the degree of carbon burnout. There is an extensive literature on char combustion kinetics based on data in the early and intermediate stages of carbon conversion. A critical fundamental question is whether the small fraction of the fuel carbon that passes unreacted through a boiler is representative of the char during the main portion of the combustion process. This article addresses that question through a detailed characterization of eight carbon-containing fly ash samples acquired from commercial-scale combustion systems. The fly ash characterization included measurement-of joint carbon/size distribution and determination.of the combustion reactivity of the residual carbon. To minimize mineral matter interactions in the reactivity tests, the technique of incipient fluidization was developed for separation of carbon-rich extracts from the inorganic portion of the fly ash. Reactivity measurements were made at 1400--1800 K to represent conditions in pulverized coal fired boilers. Measurements were also made at 700--1100 K to. minimize transport effects and isolate the influence of char chemistry and microstructure. In both temperature regimes, the residual carbon extracts. were significantly less reactive than chars extracted from a laboratory-scale laminar flow reactor in the early-to-intermediate stages of combustion. It is concluded that the boiler environment deactivates chars, making high carbon burnout more difficult to achieve than is predicted by existing char combustion kinetic models that were developed from data on the laboratory chars. Finally, the results are used to discuss potential char deactivation mechanisms, both thermal and oxidative, in coal-fired boilers.

  10. Particulate emission abatement for Krakow boiler houses

    SciTech Connect

    Wysk, R.

    1995-12-31

    Among the many strategies for improving air quality in Krakow, one possible method is to adapt new and improved emission control technology. This project focuses on such a strategy. In order to reduce dust emissions from coal-fueled boilers, a new device called a Core Separator has been introduced in several boiler house applications. This advanced technology has been successfully demonstrated in Poland and several commercial units are now in operation. Particulate emissions from the Core Separator are typically 3 to 5 times lower than those from the best cyclone collectors. It can easily meet the new standard for dust emissions which will be in effect in Poland after 1997. The Core Separator is a completely inertial collector and is based on a unique recirculation method. It can effectively remove dust particles below 10 microns in diameter, the so-called PM-10 emissions. Its performance approaches that of fabric filters, but without the attendant cost and maintenance. It is well-suited to the industrial size boilers located in Krakow. Core Separators are now being marketed and sold by EcoInstal, one of the leading environmental firms in Poland, through a cooperative agreement with LSR Technologies.

  11. BOILER MATERIALS FOR ULTRASUPERCRITICAL COAL POWER PLANTS

    SciTech Connect

    R. Viswanathan; K. Coleman; R.W. Swindeman; J. Sarver; J. Blough; W. Mohn; M. Borden; S. Goodstine; I. Perrin

    2003-08-04

    The principal objective of this project is to develop materials technology for use in ultrasupercritical (USC) plant boilers capable of operating with 760 C (1400 F), 35 MPa (5000 psi) steam. This project has established a government/industry consortium to undertake a five-year effort to evaluate and develop of advanced materials that allow the use of advanced steam cycles in coal-based power plants. These advanced cycles, with steam temperatures up to 760 C, will increase the efficiency of coal-fired boilers from an average of 35% efficiency (current domestic fleet) to 47% (HHV). This efficiency increase will enable coal-fired power plants to generate electricity at competitive rates (irrespective of fuel costs) while reducing CO{sub 2} and other fuel-related emissions by as much as 29%. Success in achieving these objectives will support a number of broader goals. First, from a national prospective, the program will identify advanced materials that will make it possible to maintain a cost-competitive, environmentally acceptable coal-based electric generation option. High sulfur coals will specifically benefit in this respect by having these advanced materials evaluated in high-sulfur coal firing conditions and from the significant reductions in waste generation inherent in the increased operational efficiency. Second, from a national prospective, the results of this program will enable domestic boiler manufacturers to successfully compete in world markets for building high-efficiency coal-fired power plants.

  12. BOILER MATERIALS FOR ULTRASUPERCRITICAL COAL POWER PLANTS

    SciTech Connect

    R. Viswanathan; K. Coleman; R.W. Swindeman; J. Sarver; J. Blough; W. Mohn; M. Borden; S. Goodstine; I. Perrin

    2003-10-20

    The principal objective of this project is to develop materials technology for use in ultrasupercritical (USC) plant boilers capable of operating with 760 C (1400 F), 35 MPa (5000 psi) steam. This project has established a government/industry consortium to undertake a five-year effort to evaluate and develop of advanced materials that allow the use of advanced steam cycles in coal-based power plants. These advanced cycles, with steam temperatures up to 760 C, will increase the efficiency of coal-fired boilers from an average of 35% efficiency (current domestic fleet) to 47% (HHV). This efficiency increase will enable coal-fired power plants to generate electricity at competitive rates (irrespective of fuel costs) while reducing CO{sub 2} and other fuel-related emissions by as much as 29%. Success in achieving these objectives will support a number of broader goals. First, from a national prospective, the program will identify advanced materials that will make it possible to maintain a cost-competitive, environmentally acceptable coal-based electric generation option. High sulfur coals will specifically benefit in this respect by having these advanced materials evaluated in high-sulfur coal firing conditions and from the significant reductions in waste generation inherent in the increased operational efficiency. Second, from a national prospective, the results of this program will enable domestic boiler manufacturers to successfully compete in world markets for building high-efficiency coal-fired power plants.

  13. Field Test of Boiler Primary Loop Temperature Controller

    SciTech Connect

    Glanville, P.; Rowley, P.; Schroeder, D.; Brand, L.

    2014-09-01

    Beyond these initial system efficiency upgrades are an emerging class of Advanced Load Monitoring (ALM) aftermarket controllers that dynamically respond to the boiler load, with claims of 10% to 30% of fuel savings over a heating season. For hydronic boilers specifically, these devices perform load monitoring, with continuous measurement of supply and, in some cases, return water temperatures. Energy savings from these ALM controllers are derived from dynamic management of the boiler differential, where a microprocessor with memory of past boiler cycles prevents the boiler from firing for a period of time, to limit cycling losses and inefficient operation during perceived low load conditions. These differ from OTR controllers, which vary boiler setpoint temperatures with ambient conditions while maintaining a fixed differential.

  14. Design considerations of B&W internal circulation CFB boilers

    SciTech Connect

    Kavidass, S.; Alexander, K.C.

    1995-12-31

    Worldwide, the use of Circulating Fluidized-Bed (CFB) boiler technology is rapidly increasing due to the ability to burn low grade fuels while meeting the required NO{sub x}, SO{sub 2}, CO, VOC, and particulate emissions requirements. The CFB boiler can produce steam economically for process and electric power generation. This paper discusses various aspects of Babcock & Wilcox (B&W) internal recirculation circulating fluidized-bed (IR-CFB) boiler design including fuel, boiler process parameters, and emissions. The B&W CFB boiler is unique in design. It utilizes proven impact-type particle separators (U-beams) with in-furnace solids recirculation. The paper describes the methodology for setting up process parameters, heat duty, boiler design, including auxiliary equipment selection and advantages.

  15. A Rule-Based Industrial Boiler Selection System

    NASA Astrophysics Data System (ADS)

    Tan, C. F.; Khalil, S. N.; Karjanto, J.; Tee, B. T.; Wahidin, L. S.; Chen, W.; Rauterberg, G. W. M.; Sivarao, S.; Lim, T. L.

    2015-09-01

    Boiler is a device used for generating the steam for power generation, process use or heating, and hot water for heating purposes. Steam boiler consists of the containing vessel and convection heating surfaces only, whereas a steam generator covers the whole unit, encompassing water wall tubes, super heaters, air heaters and economizers. The selection of the boiler is very important to the industry for conducting the operation system successfully. The selection criteria are based on rule based expert system and multi-criteria weighted average method. The developed system consists of Knowledge Acquisition Module, Boiler Selection Module, User Interface Module and Help Module. The system capable of selecting the suitable boiler based on criteria weighted. The main benefits from using the system is to reduce the complexity in the decision making for selecting the most appropriate boiler to palm oil process plant.

  16. 36. VIEW OF SOUTH END OF EAST BOILER ROOM LOOKING ...

    Library of Congress Historic Buildings Survey, Historic Engineering Record, Historic Landscapes Survey

    36. VIEW OF SOUTH END OF EAST BOILER ROOM LOOKING SOUTHWEST. THE CYLINDRICAL TANKS IN THE FOREGROUND CONTAIN AN ION-EXCHANGE RESIN FOR REMOVING CALCIUM FROM THE BOILER FEED TO REDUCE WATER "HARDNESS". THE SHALLOW TANK IN THE RIGHT BACKGROUND IS A DIATOMACEOUS EARTH FILTER TO REMOVE PARTICULATE MATTER FROM THE BOILER FEED. THE ION-EXCHANGE WATER SOFTENING SYSTEM WAS INSTALLED IN 1977. - New York, New Haven & Hartford Railroad, Cos Cob Power Plant, Sound Shore Drive, Greenwich, Fairfield County, CT

  17. 33. 20HORSE POWER VERTICAL BOILER WAS MANUFACTURED BY ORR & ...

    Library of Congress Historic Buildings Survey, Historic Engineering Record, Historic Landscapes Survey

    33. 20-HORSE POWER VERTICAL BOILER WAS MANUFACTURED BY ORR & SEMBOWER, FROM READING, PA. IT WAS INSTALLED IN 1929 TO REPLACE THE ORIGINAL BOILER. THE BOILER PROVIDED STEAM TO THE STEAM ENGINE. TO LUBRICATING THE DIE OF THE BRICK AUGER, AND TO THE STEAM PIPES OF THE DRYING ROOM ON THE FLOOR ABOVE. - Moravian Pottery & Tile Works, Southwest side of State Route 313 (Swamp Road), Northwest of East Court Street, Doylestown, Bucks County, PA

  18. 16. View into interior steam spaces of boiler above fireboxes ...

    Library of Congress Historic Buildings Survey, Historic Engineering Record, Historic Landscapes Survey

    16. View into interior steam spaces of boiler above fireboxes through manhole (see photo VT-14-16 for manhole location). Tops-or crown sheets--of fireboxes show below. Vertical and inclined bars are stays used to hold boiler together and reinforce flat plates under pressure. Note water level used in boilers indicated by scale encrustation on stays. (Threaded stud in extreme foreground belongs to manhole cover opened for purposed of photography.) - Ferry TICONDEROGA, Route 7, Shelburne, Chittenden County, VT

  19. 27. VIEW OF SOUTHERN PORTION OF EAST BOILER ROOM LOOKING ...

    Library of Congress Historic Buildings Survey, Historic Engineering Record, Historic Landscapes Survey

    27. VIEW OF SOUTHERN PORTION OF EAST BOILER ROOM LOOKING EAST AT UPPER PORTION BOILER 904. BOILER 904 WAS MANUFACTURED BY RILEY STOKER AND INSTALLED IN 1944. ORIGINALLY FUELED BY PULVERIZED COAL, IT WAS CONVERTED TO GAS/OIL OPERATION IN 1978 AND OPERATED UNTIL THE PLANT CLOSED. - New York, New Haven & Hartford Railroad, Cos Cob Power Plant, Sound Shore Drive, Greenwich, Fairfield County, CT

  20. 22. (Credit JTL) Detail, south elevation of boiler room; view ...

    Library of Congress Historic Buildings Survey, Historic Engineering Record, Historic Landscapes Survey

    22. (Credit JTL) Detail, south elevation of boiler room; view looking NNW at Adolphous Custodis stack base (1900), boiler room doors, boiler backheads and edge of old high service pump room. Note joint in bricks to right of Poller room doors showing extent of wall replacement when doors were installed. - McNeil Street Pumping Station, McNeil Street & Cross Bayou, Shreveport, Caddo Parish, LA

  1. Contributions to the use of macrosounds for boiler decrusting

    NASA Technical Reports Server (NTRS)

    Bradeteanu, C.

    1974-01-01

    The results of an investigation indicate the following: (1) The deposition of incrustations on the heating surfaces of steam boilers can be prevented by inserting between heating surface and water an insulating layer on which the boiler incrustation will be deposited. (2) The insulating layer reduces the coefficient of heat transmission by 2%. (3) The insulating layer can be removed by macrosounds with a frequency of about 20 kHz, after any interval of boiler operation.

  2. The Characterization of Twin-Wire Arc-Sprayed FeCrBSi Coating and the Application in Sewage Sludge Boilers

    NASA Astrophysics Data System (ADS)

    Qin, Enwei; Huang, Qian; Shao, Yumin; Chen, Guoxing; Ye, Lin; Gu, Qin; Wu, Shuhui

    2014-12-01

    Incineration in boilers is an environment-friendly treatment for industrial and civil sewage sludge. However, due to the aggressive nature of the sludge, the boiler fireside-surface is subjected to severe wear, erosive, and high temperature corrosion problems during incineration. In this study, we developed an economical FeCrBSi wire material with iron weight content as high as 80%. The coating was prepared by twin-wire arc spraying processing. The chemical compositions of the coating, as well as phase components were analyzed by energy-dispersive spectroscopy and x-ray diffraction method. The surface roughness, porosity, and cross-sectional morphology were further characterized. The coating hardness is close to that of the commercial Armacor M and Armacor C materials. In-boiler test was also carried out. The low thickness loss of the tube indicates a promising application future in sludge boilers.

  3. The Characterization of Twin-Wire Arc-Sprayed FeCrBSi Coating and the Application in Sewage Sludge Boilers

    NASA Astrophysics Data System (ADS)

    Qin, Enwei; Huang, Qian; Shao, Yumin; Chen, Guoxing; Ye, Lin; Gu, Qin; Wu, Shuhui

    2014-09-01

    Incineration in boilers is an environment-friendly treatment for industrial and civil sewage sludge. However, due to the aggressive nature of the sludge, the boiler fireside-surface is subjected to severe wear, erosive, and high temperature corrosion problems during incineration. In this study, we developed an economical FeCrBSi wire material with iron weight content as high as 80%. The coating was prepared by twin-wire arc spraying processing. The chemical compositions of the coating, as well as phase components were analyzed by energy-dispersive spectroscopy and x-ray diffraction method. The surface roughness, porosity, and cross-sectional morphology were further characterized. The coating hardness is close to that of the commercial Armacor M and Armacor C materials. In-boiler test was also carried out. The low thickness loss of the tube indicates a promising application future in sludge boilers.

  4. NOx Control for Utility Boiler OTR Compliance

    SciTech Connect

    Hamid Farzan; Jennifer L. Sivy

    2005-07-30

    Babcock & Wilcox Power Generation Group (B&W) and Fuel Tech, Inc. (Fuel Tech) teamed to evaluate an integrated solution for NO{sub x} control comprised of B&W's DRB-4Z{reg_sign} low-NO{sub x} pulverized coal (PC) burner technology and Fuel Tech's NO{sub x}OUT{reg_sign}, a selective non-catalytic reduction (SNCR) technology, capable of meeting a target emission limit of 0.15 lb NO{sub x}/10{sup 6} Btu. In a previous project sponsored by the U.S. Department of Energy (DOE), promising results were obtained with this technology from large-scale testing in B&W's 100-million Btu/hr Clean Environment Development Facility (CEDF) which simulates the conditions of large coal-fired utility boilers. Under the most challenging boiler temperatures at full load conditions, NO{sub x} emissions of 0.19 lb/10{sup 6} Btu were achieved firing Powder River Basin coal while controlling ammonia slip to less than 5 ppm. At a 40 million Btu/hr firing rate, NO{sub x} emissions were as low as 0.09 lb/10{sup 6} Btu. Improved performance with this system was proposed for this new program with injection at full load via a convective pass multiple nozzle lance (MNL) in front of the superheater tubes or in the convective tube bank. Convective pass lances represent the current state-of-the-art in SNCR and needed to be evaluated in order to assess the full potential of the combined technologies. The objective of the program was to achieve a NO{sub x} level below 0.15 lb/10{sup 6} Btu (with ammonia slip of less than 5 ppm) in the CEDF using PRB coal and B&W's DRB-4Z{reg_sign} low-NO{sub x} pulverized coal (PC) burner in combination with dual zone overfire air ports and Fuel Tech's NO{sub x}OUT{reg_sign} System. Commercial installations of B&W's low-NO{sub x} burner, in combination with overfire air ports using PRB coal, have demonstrated a NO{sub x} level of 0.15 to 0.2 lb/10{sup 6} Btu under staged combustion conditions. The proposed goal of the combustion system (no SNCR) for this project is a NO

  5. Evaluation of the behavior of shrouded plasma spray coatings in the platen superheater of coal-fired boilers

    SciTech Connect

    Sidhu, B.S.; Prakash, S.

    2006-06-15

    Nickel- and cobalt-based coatings were formulated by a shrouded plasma spray process on boiler tube steels, namely, ASTM-SA210-grade A1 (GrA1), ASTM-SA213-T-11 (T11), and ASTM-SA213-T-22 (T22). The Ni-22Cr-10A1-1Y alloy powder was sprayed as a bond in each case before the final coating. The degradation behavior of the bared and coated steels was studied in the platen superheater of the coal-fired boiler. The samples were inserted through the soot blower dummy points with the help of stainless steel wires. The coatings were found to be effective in increasing resistance to degradation in the given boiler environment. The maximum protection was observed in the case of Stellite-6 (St-6) coating.

  6. Comparison of simulated and actual wind shear radar data products

    NASA Technical Reports Server (NTRS)

    Britt, Charles L.; Crittenden, Lucille H.

    1992-01-01

    Prior to the development of the NASA experimental wind shear radar system, extensive computer simulations were conducted to determine the performance of the radar in combined weather and ground clutter environments. The simulation of the radar used analytical microburst models to determine weather returns and synthetic aperture radar (SAR) maps to determine ground clutter returns. These simulations were used to guide the development of hazard detection algorithms and to predict their performance. The structure of the radar simulation is reviewed. Actual flight data results from the Orlando and Denver tests are compared with simulated results. Areas of agreement and disagreement of actual and simulated results are shown.

  7. Predictive modelling of boiler fouling

    SciTech Connect

    Not Available

    1991-01-01

    The primary objective of this work is the development of a comprehensive numerical model describing the time evolution of fouling under realistic heat exchanger conditions. As fouling is a complex interaction of gas flow, mineral transport and adhesion mechanisms, understanding and subsequently improved controlling of fouling achieved via appropriate manipulation of the various coupled, nonlinear processes in a complex fluid mechanics environment will undoubtedly help reduce the substantial operating costs incurred by the utilities annually, as well as afford greater flexibility in coal selection and reduce the emission of various pollutants. In a more specialized context, the numerical model to be developed as part of this activity will be used as a tool to address the interaction of the various mechanisms controlling deposit development in specific regimes or correlative relationships. These should prove of direct use to the coal burning industry. 11 figs.

  8. Predictive modelling of boiler fouling

    SciTech Connect

    Not Available

    1992-01-01

    The primary objective of this work is the development of a comprehensive numerical model describing the time evolution of fouling under realistic heat exchanger conditions. As fouling is complex interaction of gas flow, mineral transport and adhesion mechanisms, understanding and subsequently improved controlling of fouling achieved via appropriate manipulation of the various coupled, nonlinear processes in a complex fluid mechanics environment will undoubtedly help reduce the substantial operating costs incurred by the utilities annually, as well as afford greater flexibility in coal selection and reduce the emission of various pollutants. In a more specialized context, the numerical model to be developed as part of this activity will be used as a tool to address the interaction of the various mechanisms controlling deposit development in specific regimes or correlative relationships. These should prove of direct use to the coal burning industry.

  9. Predictive modelling of boiler fouling

    SciTech Connect

    Not Available

    1991-01-01

    The primary objective of this work is the development of a comprehensive numerical model describing the time evolution of fouling under realistic heat exchanger conditions. As fouling is a complex interaction of gas flow, mineral transport and adhesion mechanisms, understanding and subsequently improved controlling of fouling achieved via appropriate manipulation of the various coupled, nonlinear processes in a complex fluid mechanics environment will undoubtedly help reduce the substantial operating costs incurred by the utilities annually, as well as afford greater flexibility in coal selection and reduce the emission of various pollutants. In a more specialized context, the numerical model to be developed as part of this activity will be used as a tool to address the interaction of the various mechanisms controlling deposit development in specific regimes or correlative relationships. These should prove of direct use to the coal burning industry.

  10. 13. RW Meyer Sugar Mill: 18761889. Engine and boiler house, ...

    Library of Congress Historic Buildings Survey, Historic Engineering Record, Historic Landscapes Survey

    13. RW Meyer Sugar Mill: 1876-1889. Engine and boiler house, ca. 1881. Locomotive-type, fire-tube, portable boiler, no. I model. Manufactured by Ames Iron Works, Oswego, New York, 1879. 120 lbs./sq. in. working pressure, 66 sq. ft. heating surface in tubes. View: Historical view, 1934, from T.T. Waterman Collection, Hawaiian Sugar Planters' Association. View shows engine and boiler house structure intact. The water and pressure gauge to the right of the boiler are in more complete condition than in 1978 views. - R. W. Meyer Sugar Mill, State Route 47, Kualapuu, Maui County, HI

  11. Cost and performance of Group 2 boiler NOx controls

    SciTech Connect

    Khan, S.; Maibodi, M.; Srivastava, R.

    1997-12-31

    This paper presents the results of a study conducted to assist EPA in developing the Phase II NO{sub x} rule under Title IV of the Clean Air Act Amendment of 1990 (the Act). The specific purpose of this study was to assess the performance and capital and total levelized costs of NO{sub x} controls pertinent to Group 2 boilers. Group 2 boilers are all coal-fired boilers that are not dry-bottom wall-fired and tangentially fired and include cell burner-fired, cyclone-fired, wet-bottom, vertically fired, stoker-fired, and fluidized-bed boilers.

  12. Field Test of Boiler Primary Loop Temperature Controller

    SciTech Connect

    Glanville, P.; Rowley, P.; Schroeder, D.; Brand, L.

    2014-09-01

    Beyond these initial system efficiency upgrades are an emerging class of Advanced Load Monitoring (ALM) aftermarket controllers that dynamically respond to the boiler load, with claims of 10% to 30% of fuel savings over a heating season. For hydronic boilers specifically, these devices perform load monitoring, with continuous measurement of supply and in some cases return water temperatures. Energy savings from these ALM controllers are derived from dynamic management of the boiler differential, where a microprocessor with memory of past boiler cycles prevents the boiler from firing for a period of time, to limit cycling losses and inefficient operation during perceived low load conditions. These differ from OTR controllers, which vary boiler setpoint temperatures with ambient conditions while maintaining a fixed differential. PARR installed and monitored the performance of one type of ALM controller, the M2G from Greffen Systems, at multifamily sites in the city of Chicago and its suburb Cary, IL, both with existing OTR control. Results show that energy savings depend on the degree to which boilers are over-sized for their load, represented by cycling rates. Also savings vary over the heating season with cycling rates, with greater savings observed in shoulder months. Over the monitoring period, over-sized boilers at one site showed reductions in cycling and energy consumption in line with prior laboratory studies, while less over-sized boilers at another site showed muted savings.

  13. Application of Boiler Op for combustion optimization at PEPCO

    SciTech Connect

    Maines, P.; Williams, S.; Levy, E.

    1997-09-01

    Title IV requires the reduction of NOx at all stations within the PEPCO system. To assist PEPCO plant personnel in achieving low heat rates while meeting NOx targets, Lehigh University`s Energy Research Center and PEPCO developed a new combustion optimization software package called Boiler Op. The Boiler Op code contains an expert system, neural networks and an optimization algorithm. The expert system guides the plant engineer through a series of parametric boiler tests, required for the development of a comprehensive boiler database. The data are then analyzed by the neural networks and optimization algorithm to provide results on the boiler control settings which result in the best possible heat rate at a target NOx level or produce minimum NOx. Boiler Op has been used at both Potomac River and Morgantown Stations to help PEPCO engineers optimize combustion. With the use of Boiler Op, Morgantown Station operates under low NOx restrictions and continues to achieve record heat rate values, similar to pre-retrofit conditions. Potomac River Station achieves the regulatory NOx limit through the use of Boiler Op recommended control settings and without NOx burners. Importantly, any software like Boiler Op cannot be used alone. Its application must be in concert with human intelligence to ensure unit safety, reliability and accurate data collection.

  14. Design of a large-scale CFB boiler

    SciTech Connect

    Darling, S.; Li, S.

    1997-12-31

    Many CFB boilers sized 100--150 MWe are in operation, and several others sized 150--250 MWe are in operation or under construction. The next step for CFB technology is the 300--400 MWe size range. This paper will describe Foster Wheeler`s large-scale CFB boiler experience and the design for a 300 MWe CFB boiler. The authors will show how the design incorporates Foster Wheeler`s unique combination of extensive utility experience and CFB boiler experience. All the benefits of CFB technology which include low emissions, fuel flexibility, low maintenance and competitive cost are now available in the 300--400 MWe size range.

  15. CFB boiler for Southern Illinois University: Planning and design

    SciTech Connect

    Silvey, M.; Roth, N.; Haake, A.

    1995-12-31

    Southern Illinois University (SIU) is in the process of installing a Babcock and Wilcox (B and W) coal fired circulating fluidized bed (CFB) boiler at its Carbondale, Illinois campus. The CFB boiler will be used for cogeneration. Funding for this project was made possible by the State of Illinois Capital Development Board. Illinois coal will be fired in this CFB boiler. This paper provides a description of the planning process and design of the CFB boiler and related equipment with specific emphasis on particulate removal and recirculation. The startup of this new installation is scheduled for the summer of 1996, with commercial operation by fall of 1996.

  16. Residual Strain Distribution in Bent Composite Boiler Tubes

    SciTech Connect

    Hubbard, Camden R; Gorti, Sarma B; Tang, Fei

    2006-01-01

    Kraft recovery boilers are typically constructed of carbon steel boiler tubes clad with a corrosion resistant layer, and these composite tubes are bent and welded together to form air port panels which enable the combustion air to enter the boiler. In this paper, the through-thickness residual strain in the carbon steel layer of non-heat-treated and heat-treated composite bent tubes were measured by neutron diffraction techniques and modeled by finite element modeling. The results can be used to optimize material selection and manufacturing processes to prevent stress corrosion and corrosion fatigue cracking in the boiler tubes.

  17. POLLUTANT CONTROL TECHNIQUES FOR PACKAGE BOILERS: HARDWARE MODIFICATIONS AND ALTERNATE FUELS

    EPA Science Inventory

    The report gives results of investigations of four ways to control nitrogen oxide (NOx) emissions from package boilers (both field operating boilers and boiler simulators): (1) variations in combustor operating procedure; (2) combustion modification (flue gas recirculation and st...

  18. Thermographic imaging of material loss in boiler water-wall tubing by application of scanning line source

    NASA Astrophysics Data System (ADS)

    Cramer, K. Elliott; Winfree, William P.

    2000-06-01

    Localized wall thinning due to corrosion in utility boiler water-wall tubing is a significant inspection concern for boiler operators. Historically, conventional ultrasonics has been used for inspection of these tubes. This technique has proven to be very manpower and time intensive. This has resulted in a 'spot check' approach to inspections, documenting thickness measurements over a relatively small percentage of the total boiler wall area. NASA Langley Research Center has developed a thermal NDE technique designed to image and quantitatively characterize the amount of material thinning present in steel tubing. The technique involves the movement of a thermal line source across the outer surface of the tubing followed by an infrared imager at a fixed distance behind the line source. Quantitative images of the material loss due to corrosion are reconstructed from measurements of the induced surface temperature variations. This paper will present a discussion of the development of the thermal imaging system as well as the techniques used to reconstruct images of flaws. The application of the thermal line source coupled with the analysis technique represents a significant improvement in the inspection speed for large structures such as boiler water-walls. A theoretical basis for the technique will be presented which explains the quantitative nature of the technique. Further, a dynamic calibration system will be presented for the technique that allows the extraction of thickness information from the temperature data. Additionally, the results of applying this technology to actual water-wall tubing samples and in situ inspections will be presented.

  19. Thermographic Imaging of Material Loss in Boiler Water-Wall Tubing by Application of Scanning Line Source

    NASA Technical Reports Server (NTRS)

    Cramer, K. Elliott; Winfree, William P.

    2000-01-01

    Localized wall thinning due to corrosion in utility boiler water-wall tubing is a significant inspection concern for boiler operators. Historically, conventional ultrasonics has been used for inspection of these tubes. This technique has proven to be very manpower and time intensive. This has resulted in a spot check approach to inspections, documenting thickness measurements over a relatively small percentage of the total boiler wall area. NASA Langley Research Center has developed a thermal NDE technique designed to image and quantitatively characterize the amount of material thinning present in steel tubing. The technique involves the movement of a thermal line source across the outer surface of the tubing followed by an infrared imager at a fixed distance behind the line source. Quantitative images of the material loss due to corrosion are reconstructed from measurements of the induced surface temperature variations. This paper will present a discussion of the development of the thermal imaging system as well as the techniques used to reconstruct images of flaws. The application of the thermal line source coupled with the analysis technique represents a significant improvement in the inspection speed for large structures such as boiler water-walls. A theoretical basis for the technique will be presented which explains the quantitative nature of the technique. Further, a dynamic calibration system will be presented for the technique that allows the extraction of thickness information from the temperature data. Additionally, the results of applying this technology to actual water-wall tubing samples and in situ inspections will be presented.

  20. Combining support vector regression and ant colony optimization to reduce NOx emissions in coal-fired utility boilers

    SciTech Connect

    Ligang Zheng; Hao Zhou; Chunlin Wang; Kefa Cen

    2008-03-15

    Combustion optimization has recently demonstrated its potential to reduce NOx emissions in high capacity coal-fired utility boilers. In the present study, support vector regression (SVR), as well as artificial neural networks (ANN), was proposed to model the relationship between NOx emissions and operating parameters of a 300 MW coal-fired utility boiler. The predicted NOx emissions from the SVR model, by comparing with that of the ANN-based model, showed better agreement with the values obtained in the experimental tests on this boiler operated at different loads and various other operating parameters. The mean modeling error and the correlation factor were 1.58% and 0.94, respectively. Then, the combination of the SVR model with ant colony optimization (ACO) to reduce NOx emissions was presented in detail. The experimental results showed that the proposed approach can effectively reduce NOx emissions from the coal-fired utility boiler by about 18.69% (65 ppm). A time period of less than 6 min was required for NOx emissions modeling, and 2 min was required for a run of optimization under a PC system. The computing times are suitable for the online application of the proposed method to actual power plants. 37 refs., 8 figs., 3 tabs.

  1. Computation Modeling and Assessment of Nanocoatings for Ultra Supercritical Boilers

    SciTech Connect

    J. Shingledecker; D. Gandy; N. Cheruvu; R. Wei; K. Chan

    2011-06-21

    Forced outages and boiler unavailability of coal-fired fossil plants is most often caused by fire-side corrosion of boiler waterwalls and tubing. Reliable coatings are required for Ultrasupercritical (USC) application to mitigate corrosion since these boilers will operate at a much higher temperatures and pressures than in supercritical (565 C {at} 24 MPa) boilers. Computational modeling efforts have been undertaken to design and assess potential Fe-Cr-Ni-Al systems to produce stable nanocrystalline coatings that form a protective, continuous scale of either Al{sub 2}O{sub 3} or Cr{sub 2}O{sub 3}. The computational modeling results identified a new series of Fe-25Cr-40Ni with or without 10 wt.% Al nanocrystalline coatings that maintain long-term stability by forming a diffusion barrier layer at the coating/substrate interface. The computational modeling predictions of microstructure, formation of continuous Al{sub 2}O{sub 3} scale, inward Al diffusion, grain growth, and sintering behavior were validated with experimental results. Advanced coatings, such as MCrAl (where M is Fe, Ni, or Co) nanocrystalline coatings, have been processed using different magnetron sputtering deposition techniques. Several coating trials were performed and among the processing methods evaluated, the DC pulsed magnetron sputtering technique produced the best quality coating with a minimum number of shallow defects and the results of multiple deposition trials showed that the process is repeatable. scale, inward Al diffusion, grain growth, and sintering behavior were validated with experimental results. The cyclic oxidation test results revealed that the nanocrystalline coatings offer better oxidation resistance, in terms of weight loss, localized oxidation, and formation of mixed oxides in the Al{sub 2}O{sub 3} scale, than widely used MCrAlY coatings. However, the ultra-fine grain structure in these coatings, consistent with the computational model predictions, resulted in accelerated Al

  2. The reapplication of energetic materials as boiler fuels

    SciTech Connect

    Buckley, S.G.; Sclippa, G.C.; Ross, J.R.

    1997-02-01

    Decommissioning of weapons stockpiles, off-specification production, and upgrading of weapons systems results in a large amount of energetic materials (EM) such as rocket propellant and primary explosives that need to be recycled or disposed of each year. Presently, large quantities of EM are disposed of in a process known as open-burn/open-detonation (OB/OD), which not only wastes their energy content, but may release large quantities of hazardous material into the environment. Here the authors investigate the combustion properties of several types of EM to determine the feasibility of reapplication of these materials as boiler fuels, a process that could salvage the energy content of the EM as well as mitigate any potential adverse environmental impact. Reapplication requires pretreatment of the fuels to make them safe to handle and to feed. Double-base nitrocellulose and nitroglycerin, trinitrotoluene (TNT), nitroguanidine, and a rocket propellant binder primarily composed of polybutidiene impregnated with aluminum flakes have been burned in a 100-kW downfired flow reactor. Most of these fuels have high levels of fuel-bound nitrogen, much of it bound in the form of nitrate groups, resulting in high NO{sub x} emissions during combustion. The authors have measured fuel-bound nitrate conversion efficiencies to NO{sub x} of up to 80%, suggesting that the nitrate groups do not follow the typical path of fuel nitrogen through HCN leading to NO{sub x}, but rather form NO{sub x} directly. They show that staged combustion is effective in reducing NO{sub x} concentrations in the postcombustion gases by nearly a factor of 3. In the rocket binder, measured aluminum particle temperatures in excess of 1700{degrees}C create high levels of thermal NO{sub x}, and also generate concern that molten aluminum particles could potentially damage boiler equipment. Judicious selection of the firing method is thus required for aluminum-containing materials.

  3. NOx CONTROL OPTIONS AND INTEGRATION FOR US COAL FIRED BOILERS

    SciTech Connect

    Mike Bockelie; Marc Cremer; Kevin Davis; Temi Linjewile; Connie Senior; Hong-Shig Shim; Bob Hurt; Eric Eddings; Larry Baxter

    2003-01-30

    This is the tenth Quarterly Technical Report for DOE Cooperative Agreement No: DE-FC26-00NT40753. The goal of the project is to develop cost effective analysis tools and techniques for demonstrating and evaluating low NO{sub x} control strategies and their possible impact on boiler performance for firing US coals. The Electric Power Research Institute (EPRI) is providing cofunding for this program. This program contains multiple tasks and good progress is being made on all fronts. During this quarter, progress was made on the computational simulation of a full-scale boiler with the purpose of understanding the potential impacts of burner operating conditions on soot and NO{sub x} generation. Sulfation tests on both the titania support and vanadia/titania catalysts were completed using BYU's in situ spectroscopy reactor this quarter. These experiments focus on the extent to which vanadia and titania sulfate in an SO{sub 2}-laden, moist environment. Construction of the CCS reactor system is essentially complete and the control hardware and software are largely in place. A large batch of vanadia/titania catalyst in powder form has been prepared for use in poisoning tests. During this quarter, minor modifications were made to the multi-catalyst slipstream reactor and to the control system. The slipstream reactor was installed at AEP's Rockport plant at the end of November 2002. In this report, we describe the reactor system, particularly the control system, which was created by REI specifically for the reactor, as well as the installation at Rockport.

  4. Erosion-corrosion of as-plasma-sprayed and laser-remelted NiCrAlY bond coats in working conditions of a coal-fired boiler

    SciTech Connect

    Sidhu, B.S.; Prakash, S.

    2008-01-15

    Ni-22Cr-10Al-1Y plasma spray coating has been formulated on boiler tube steels. namely, low-carbon steel ASTM SA210-Grade A1. 1Cr-0.5Mo steel ASTM SA213-T-11, and 2.25Cr-1Mo steel ASTM SA213-T-22. The coated steels also have been laser-remelted using a Nd:YAG laser. The degradation behavior of as-sprayed and laser-remelted coatings have been evaluated in actual conditions in a coal-fired boiler for 1,000 h at 755{sup o}C. The laser remelting has been found to be effective to increase the degradation resistance of plasma-sprayed boiler steels. ASTM SA213-T-22-coated and laser-remelted steel has proved to be most effective in resistance to degrading species.

  5. 40 CFR Appendix A to Part 76 - Phase I Affected Coal-Fired Utility Units With Group 1 or Cell Burner Boilers

    Code of Federal Regulations, 2011 CFR

    2011-07-01

    ... 40 Protection of Environment 16 2011-07-01 2011-07-01 false Phase I Affected Coal-Fired Utility Units With Group 1 or Cell Burner Boilers A Appendix A to Part 76 Protection of Environment ENVIRONMENTAL PROTECTION AGENCY (CONTINUED) AIR PROGRAMS (CONTINUED) ACID RAIN NITROGEN OXIDES...

  6. 40 CFR Appendix A to Part 76 - Phase I Affected Coal-Fired Utility Units With Group 1 or Cell Burner Boilers

    Code of Federal Regulations, 2012 CFR

    2012-07-01

    ... 40 Protection of Environment 17 2012-07-01 2012-07-01 false Phase I Affected Coal-Fired Utility Units With Group 1 or Cell Burner Boilers A Appendix A to Part 76 Protection of Environment ENVIRONMENTAL PROTECTION AGENCY (CONTINUED) AIR PROGRAMS (CONTINUED) ACID RAIN NITROGEN OXIDES...

  7. 40 CFR Appendix B to Part 76 - Procedures and Methods for Estimating Costs of Nitrogen Oxides Controls Applied to Group 1, Boilers

    Code of Federal Regulations, 2013 CFR

    2013-07-01

    ... 40 Protection of Environment 17 2013-07-01 2013-07-01 false Procedures and Methods for Estimating Costs of Nitrogen Oxides Controls Applied to Group 1, Boilers B Appendix B to Part 76 Protection of Environment ENVIRONMENTAL PROTECTION AGENCY (CONTINUED) AIR PROGRAMS (CONTINUED) ACID RAIN NITROGEN...

  8. 40 CFR Appendix B to Part 76 - Procedures and Methods for Estimating Costs of Nitrogen Oxides Controls Applied to Group 1, Boilers

    Code of Federal Regulations, 2014 CFR

    2014-07-01

    ... 40 Protection of Environment 17 2014-07-01 2014-07-01 false Procedures and Methods for Estimating Costs of Nitrogen Oxides Controls Applied to Group 1, Boilers B Appendix B to Part 76 Protection of Environment ENVIRONMENTAL PROTECTION AGENCY (CONTINUED) AIR PROGRAMS (CONTINUED) ACID RAIN NITROGEN...

  9. 40 CFR Appendix B to Part 76 - Procedures and Methods for Estimating Costs of Nitrogen Oxides Controls Applied to Group 1, Boilers

    Code of Federal Regulations, 2011 CFR

    2011-07-01

    ... 40 Protection of Environment 16 2011-07-01 2011-07-01 false Procedures and Methods for Estimating Costs of Nitrogen Oxides Controls Applied to Group 1, Boilers B Appendix B to Part 76 Protection of Environment ENVIRONMENTAL PROTECTION AGENCY (CONTINUED) AIR PROGRAMS (CONTINUED) ACID RAIN NITROGEN...

  10. 40 CFR Appendix A to Part 76 - Phase I Affected Coal-Fired Utility Units With Group 1 or Cell Burner Boilers

    Code of Federal Regulations, 2013 CFR

    2013-07-01

    ... 40 Protection of Environment 17 2013-07-01 2013-07-01 false Phase I Affected Coal-Fired Utility Units With Group 1 or Cell Burner Boilers A Appendix A to Part 76 Protection of Environment ENVIRONMENTAL PROTECTION AGENCY (CONTINUED) AIR PROGRAMS (CONTINUED) ACID RAIN NITROGEN OXIDES...

  11. 40 CFR Appendix A to Part 76 - Phase I Affected Coal-Fired Utility Units With Group 1 or Cell Burner Boilers

    Code of Federal Regulations, 2014 CFR

    2014-07-01

    ... 40 Protection of Environment 17 2014-07-01 2014-07-01 false Phase I Affected Coal-Fired Utility Units With Group 1 or Cell Burner Boilers A Appendix A to Part 76 Protection of Environment ENVIRONMENTAL PROTECTION AGENCY (CONTINUED) AIR PROGRAMS (CONTINUED) ACID RAIN NITROGEN OXIDES...

  12. 40 CFR Appendix B to Part 76 - Procedures and Methods for Estimating Costs of Nitrogen Oxides Controls Applied to Group 1, Boilers

    Code of Federal Regulations, 2010 CFR

    2010-07-01

    ... 40 Protection of Environment 16 2010-07-01 2010-07-01 false Procedures and Methods for Estimating Costs of Nitrogen Oxides Controls Applied to Group 1, Boilers B Appendix B to Part 76 Protection of Environment ENVIRONMENTAL PROTECTION AGENCY (CONTINUED) AIR PROGRAMS (CONTINUED) ACID RAIN NITROGEN OXIDES EMISSION REDUCTION PROGRAM Pt. 76, App....

  13. 40 CFR Appendix B to Part 76 - Procedures and Methods for Estimating Costs of Nitrogen Oxides Controls Applied to Group 1, Boilers

    Code of Federal Regulations, 2012 CFR

    2012-07-01

    ... 40 Protection of Environment 17 2012-07-01 2012-07-01 false Procedures and Methods for Estimating Costs of Nitrogen Oxides Controls Applied to Group 1, Boilers B Appendix B to Part 76 Protection of Environment ENVIRONMENTAL PROTECTION AGENCY (CONTINUED) AIR PROGRAMS (CONTINUED) ACID RAIN NITROGEN...

  14. 40 CFR Appendix A to Part 76 - Phase I Affected Coal-Fired Utility Units With Group 1 or Cell Burner Boilers

    Code of Federal Regulations, 2010 CFR

    2010-07-01

    ... 40 Protection of Environment 16 2010-07-01 2010-07-01 false Phase I Affected Coal-Fired Utility Units With Group 1 or Cell Burner Boilers A Appendix A to Part 76 Protection of Environment ENVIRONMENTAL PROTECTION AGENCY (CONTINUED) AIR PROGRAMS (CONTINUED) ACID RAIN NITROGEN OXIDES EMISSION REDUCTION PROGRAM Pt. 76, App. A Appendix A to Part...

  15. Characterization of single-tube model-boiler dented intersection specimens. Final report. [PWR

    SciTech Connect

    Varsanik, R.G.; Gibbon, D.L.

    1983-05-01

    Crevice denting, caused by the uncontrolled growth of magnetite in the space between carbon-steel tube-support plates and Inconel heat-exchange tubes is a major cause of concern in nuclear steam generators. This particular form of localized corrosion has been modeled experimentally by the Westinghouse Electric Corporation using prototypical boiler systems. In this study, three corrosion specimens from these model-boiler systems have been characterized by Calgon Corporation using light and scanning electron microscopy along with both energy- and wave-length-dispersive x-ray spectrophotometry. Samples examined consisted of specimens which had been exposed to a known corrosive environment and then either left untreated, treated with calcium hydroxide, or treated with boric acid in an attempt to halt the corrosion process. The destructive examination of the samples was conducted on both polished sections as well as sections fractured in liquid nitrogen to expose uncontaminated interfaces between the multiple phases involved.

  16. Cracking and Corrosion of Composite Tubes in Black Liquor Recovery Boiler Primary Air Ports

    SciTech Connect

    Keiser, James R.; Singbeil, Douglas L.; Sarma, Gorti B.; Kish, Joseph R.; Yuan, Jerry; Frederick, Laurie A.; Choudhury, Kimberly A.; Gorog, J. Peter; Jetté, Francois R.; Hubbard, Camden R.; Swindeman, Robert W.; Singh, Prett M.; Maziasz, Phillip J.

    2006-10-01

    Black liquor recovery boilers are an essential part of kraft mills. Their design and operating procedures have changed over time with the goal of providing improved boiler performance. These performance improvements are frequently associated with an increase in heat flux and/or operating temperature with a subsequent increase in the demand on structural materials associated with operation at higher temperatures and/or in more corrosive environments. Improvements in structural materials have therefore been required. In most cases the alternate materials have provided acceptable solutions. However, in some cases the alternate materials have solved the original problem but introduced new issues. This report addresses the performance of materials in the tubes forming primary air port openings and, particularly, the problems associated with use of stainless steel clad carbon steel tubes and the solutions that have been identified.

  17. Application of 1-hydroxyethylidene-1, 1-diphosphonic acid in boiler water for industrial boilers.

    PubMed

    Zeng, Bin; Li, Mao-Dong; Zhu, Zhi-Ping; Zhao, Jun-Ming; Zhang, Hui

    2013-01-01

    The primary method used for boiler water treatment is the addition of chemicals to industrial boilers to prevent corrosion and scaling. The static scale inhibition method was used to evaluate the scale inhibition performance of 1-hydroxyethylidene-1, 1-diphosphonic acid (HEDP). Autoclave static experiments were used to study the corrosion inhibition properties of the main material for industrial boilers (20# carbon steel) with an HEDP additive in the industrial boiler water medium. The electrochemical behavior of HEDP on carbon steel corrosion control was investigated using electrochemical impedance spectroscopy and Tafel polarization techniques. Experimental results indicate that HEDP can have a good scale inhibition effect when added at a quantity of 5 to 7 mg/L at a test temperature of not more than 100 °C. To achieve a high scale inhibition rate, the HEDP dosage must be increased when the test temperature exceeds 100 °C. Electrochemical and autoclave static experimental results suggest that HEDP has a good corrosion inhibition effect on 20# carbon steel at a concentration of 25 mg/L. HEDP is an excellent water treatment agent. PMID:23552243

  18. Moral Reasoning in Hypothetical and Actual Situations.

    ERIC Educational Resources Information Center

    Sumprer, Gerard F.; Butter, Eliot J.

    1978-01-01

    Results of this investigation suggest that moral reasoning of college students, when assessed using the DIT format, is the same whether the dilemmas involve hypothetical or actual situations. Subjects, when presented with hypothetical situations, become deeply immersed in them and respond as if they were actual participants. (Author/BEF)

  19. Factors Related to Self-Actualization.

    ERIC Educational Resources Information Center

    Hogan, H. Wayne; McWilliams, Jettie M.

    1978-01-01

    Provides data to further support the notions that females score higher in self-actualization measures and that self-actualization scores correlate inversely to the degree of undesirability individuals assign to their heights and weights. Finds that, contrary to predictions, greater androgyny was related to lower, not higher, self-actualization…

  20. Materials development for ultra-supercritical boilers

    SciTech Connect

    2005-09-30

    Progress is reported on a US Department of Energy project to develop high temperature, corrosion resistant alloys for use in ultra-supercritical steam cycles. The aim is to achieve boiler operation at 1,400{sup o}F/5,000 psi steam conditions with 47% net cycle efficiency. Most ferritic steel tested such as T92 and Save 12 showed severe corrosion. Nickel-based alloys, especially IN 740 and CCA 617, showed greatest resistance to oxidation with no evidence of exfoliation. Laboratory and in-plant tests have begun. 2 figs.

  1. Coal reburning application on a Cyclone boiler

    SciTech Connect

    Maringo, G.J.; Yagiela, A.S.; Newell, R.J.; Farzan, H.

    1994-12-31

    Cyclone reburn involves the injection of a supplemental fuel (natural gas, oil or coal) into the main furnace of a Cyclone-fired boiler to produce locally reducing conditions which convert NO{sub x}, generated in the main combustion zone, to molecular nitrogen, thereby reducing overall NO{sub x} emissions. The world`s only application of the Cyclone reburn technology using pulverized coal as the reburn fuel was installed at Wisconsin Power & Light`s Nelson Dewey Generating Station, Unit 2. The project was selected for demonstration under the US Department of Energy`s Clean Coal Technology Demonstration Program, Round II.

  2. Flame spectral analysis for boiler control

    SciTech Connect

    Metcalfe, C.I.; Cole, W.E.; Batra, S.K.

    1987-09-01

    An instrument has been developed by Tecogen, Inc., to determine the combustion characteristics of individual burners in multiburner installations. The technology is based on measuring the emissions in the ultraviolet (uv) and infrared (ir) spectral range from the flames and using these measurements to determine the burner operating conditions. Two prototype instruments have been installed on package boilers at a Con Edison powerplant and a Polaroid facility, and their performance has been evaluated. These instruments provide data relating to the variations in the ir and uv spectrum with a change in the combustion condition in individual burners. This paper describes the instrument's operation and these tests. 2 refs.

  3. Controlling formaldehyde emissions with boiler ash.

    PubMed

    Cowan, Jennifer; Abu-Daabes, Malyuba; Banerjee, Sujit

    2005-07-01

    Fluidized wood ash reduces formaldehyde in air from about 20 to <1 ppmv. Methanol is removed to a much lower extent. The efficiency of formaldehyde reduction increases with increasing moisture content of the ash. Sorption of formaldehyde to ash can be substantially accounted for by partitioning to the water contained in the ash followed by rate-controlling binding to the ash solids. Adsorption occurs at temperatures of up to 165 degrees C; oxidation predominates thereafter. It is proposed that formaldehyde could be stripped from an air stream in a fluidized bed containing ash, which could then be returned to a boiler to incinerate the formaldehyde. PMID:16053116

  4. Sulfur capture in combination bark boilers

    SciTech Connect

    Someshwar, A.V.; Jain, A.K. )

    1993-07-01

    A review of sulfur dioxide emission data for eight combination bark boilers in conjunction with the sulfur contents of the fuels reveals significant sulfur capture ranging from 10% to over 80% within the solid ash phase. Wood ash characteristics similar to activated carbon as well as the significant wood ash alkali oxide and carbonate fractions are believed responsible for the sulfur capture. Sulfur emissions from combination bark-fossil fuel firing are correlated to the sulfur input per ton of bark or wood residue fired.

  5. 46 CFR 52.25-20 - Exhaust gas boilers.

    Code of Federal Regulations, 2010 CFR

    2010-10-01

    ... COAST GUARD, DEPARTMENT OF HOMELAND SECURITY (CONTINUED) MARINE ENGINEERING POWER BOILERS Other Boiler... designed, constructed, inspected, tested and stamped in accordance with the applicable provisions in this part. The design temperature of parts exposed to the exhaust gas must be the maximum temperature...

  6. 46 CFR 56.50-30 - Boiler feed piping.

    Code of Federal Regulations, 2014 CFR

    2014-10-01

    ... APPURTENANCES Design Requirements Pertaining to Specific Systems § 56.50-30 Boiler feed piping. (a) General... paragraph (d) or (e) of this section. (2) Feed pump supply to power boilers may utilize the group feed... required stop and stop-check valves, shall be designed for either the feed pump relief valve setting or...

  7. 46 CFR 56.50-30 - Boiler feed piping.

    Code of Federal Regulations, 2013 CFR

    2013-10-01

    ... APPURTENANCES Design Requirements Pertaining to Specific Systems § 56.50-30 Boiler feed piping. (a) General... paragraph (d) or (e) of this section. (2) Feed pump supply to power boilers may utilize the group feed... required stop and stop-check valves, shall be designed for either the feed pump relief valve setting or...

  8. 46 CFR 52.25-20 - Exhaust gas boilers.

    Code of Federal Regulations, 2011 CFR

    2011-10-01

    ... COAST GUARD, DEPARTMENT OF HOMELAND SECURITY (CONTINUED) MARINE ENGINEERING POWER BOILERS Other Boiler... designed, constructed, inspected, tested and stamped in accordance with the applicable provisions in this part. The design temperature of parts exposed to the exhaust gas must be the maximum temperature...

  9. 46 CFR 56.50-30 - Boiler feed piping.

    Code of Federal Regulations, 2011 CFR

    2011-10-01

    ... APPURTENANCES Design Requirements Pertaining to Specific Systems § 56.50-30 Boiler feed piping. (a) General... paragraph (d) or (e) of this section. (2) Feed pump supply to power boilers may utilize the group feed... required stop and stop-check valves, shall be designed for either the feed pump relief valve setting or...

  10. 46 CFR 52.25-20 - Exhaust gas boilers.

    Code of Federal Regulations, 2014 CFR

    2014-10-01

    ... COAST GUARD, DEPARTMENT OF HOMELAND SECURITY (CONTINUED) MARINE ENGINEERING POWER BOILERS Other Boiler... designed, constructed, inspected, tested and stamped in accordance with the applicable provisions in this part. The design temperature of parts exposed to the exhaust gas must be the maximum temperature...

  11. 46 CFR 56.50-30 - Boiler feed piping.

    Code of Federal Regulations, 2012 CFR

    2012-10-01

    ... APPURTENANCES Design Requirements Pertaining to Specific Systems § 56.50-30 Boiler feed piping. (a) General... paragraph (d) or (e) of this section. (2) Feed pump supply to power boilers may utilize the group feed... required stop and stop-check valves, shall be designed for either the feed pump relief valve setting or...

  12. 46 CFR 52.25-20 - Exhaust gas boilers.

    Code of Federal Regulations, 2012 CFR

    2012-10-01

    ... COAST GUARD, DEPARTMENT OF HOMELAND SECURITY (CONTINUED) MARINE ENGINEERING POWER BOILERS Other Boiler... designed, constructed, inspected, tested and stamped in accordance with the applicable provisions in this part. The design temperature of parts exposed to the exhaust gas must be the maximum temperature...

  13. 46 CFR 56.50-30 - Boiler feed piping.

    Code of Federal Regulations, 2010 CFR

    2010-10-01

    ... APPURTENANCES Design Requirements Pertaining to Specific Systems § 56.50-30 Boiler feed piping. (a) General... paragraph (d) or (e) of this section. (2) Feed pump supply to power boilers may utilize the group feed... required stop and stop-check valves, shall be designed for either the feed pump relief valve setting or...

  14. 46 CFR 52.25-20 - Exhaust gas boilers.

    Code of Federal Regulations, 2013 CFR

    2013-10-01

    ... COAST GUARD, DEPARTMENT OF HOMELAND SECURITY (CONTINUED) MARINE ENGINEERING POWER BOILERS Other Boiler... designed, constructed, inspected, tested and stamped in accordance with the applicable provisions in this part. The design temperature of parts exposed to the exhaust gas must be the maximum temperature...

  15. 46 CFR 115.812 - Pressure vessels and boilers.

    Code of Federal Regulations, 2014 CFR

    2014-10-01

    ... 46 Shipping 4 2014-10-01 2014-10-01 false Pressure vessels and boilers. 115.812 Section 115.812 Shipping COAST GUARD, DEPARTMENT OF HOMELAND SECURITY (CONTINUED) SMALL PASSENGER VESSELS CARRYING MORE... CERTIFICATION Material Inspections § 115.812 Pressure vessels and boilers. (a) Pressure vessels must be...

  16. 46 CFR 115.812 - Pressure vessels and boilers.

    Code of Federal Regulations, 2011 CFR

    2011-10-01

    ... 46 Shipping 4 2011-10-01 2011-10-01 false Pressure vessels and boilers. 115.812 Section 115.812 Shipping COAST GUARD, DEPARTMENT OF HOMELAND SECURITY (CONTINUED) SMALL PASSENGER VESSELS CARRYING MORE... CERTIFICATION Material Inspections § 115.812 Pressure vessels and boilers. (a) Pressure vessels must be...

  17. 46 CFR 115.812 - Pressure vessels and boilers.

    Code of Federal Regulations, 2013 CFR

    2013-10-01

    ... 46 Shipping 4 2013-10-01 2013-10-01 false Pressure vessels and boilers. 115.812 Section 115.812 Shipping COAST GUARD, DEPARTMENT OF HOMELAND SECURITY (CONTINUED) SMALL PASSENGER VESSELS CARRYING MORE... CERTIFICATION Material Inspections § 115.812 Pressure vessels and boilers. (a) Pressure vessels must be...

  18. 46 CFR 176.812 - Pressure vessels and boilers.

    Code of Federal Regulations, 2012 CFR

    2012-10-01

    ... 46 Shipping 7 2012-10-01 2012-10-01 false Pressure vessels and boilers. 176.812 Section 176.812... TONS) INSPECTION AND CERTIFICATION Material Inspections § 176.812 Pressure vessels and boilers. (a) Pressure vessels must be tested and inspected in accordance with part 61, subpart 61.10, of this...

  19. 46 CFR 176.812 - Pressure vessels and boilers.

    Code of Federal Regulations, 2013 CFR

    2013-10-01

    ... 46 Shipping 7 2013-10-01 2013-10-01 false Pressure vessels and boilers. 176.812 Section 176.812... TONS) INSPECTION AND CERTIFICATION Material Inspections § 176.812 Pressure vessels and boilers. (a) Pressure vessels must be tested and inspected in accordance with part 61, subpart 61.10, of this...

  20. 46 CFR 176.812 - Pressure vessels and boilers.

    Code of Federal Regulations, 2010 CFR

    2010-10-01

    ... 46 Shipping 7 2010-10-01 2010-10-01 false Pressure vessels and boilers. 176.812 Section 176.812... TONS) INSPECTION AND CERTIFICATION Material Inspections § 176.812 Pressure vessels and boilers. (a) Pressure vessels must be tested and inspected in accordance with part 61, subpart 61.10, of this...

  1. 46 CFR 115.812 - Pressure vessels and boilers.

    Code of Federal Regulations, 2012 CFR

    2012-10-01

    ... 46 Shipping 4 2012-10-01 2012-10-01 false Pressure vessels and boilers. 115.812 Section 115.812 Shipping COAST GUARD, DEPARTMENT OF HOMELAND SECURITY (CONTINUED) SMALL PASSENGER VESSELS CARRYING MORE... CERTIFICATION Material Inspections § 115.812 Pressure vessels and boilers. (a) Pressure vessels must be...

  2. 46 CFR 176.812 - Pressure vessels and boilers.

    Code of Federal Regulations, 2014 CFR

    2014-10-01

    ... 46 Shipping 7 2014-10-01 2014-10-01 false Pressure vessels and boilers. 176.812 Section 176.812... TONS) INSPECTION AND CERTIFICATION Material Inspections § 176.812 Pressure vessels and boilers. (a) Pressure vessels must be tested and inspected in accordance with part 61, subpart 61.10, of this...

  3. TECHNOLOGY ASSESSMENT REPORT FOR INDUSTRIAL BOILER APPLICATIONS: SYNTHETIC FUELS

    EPA Science Inventory

    The report, part of a series to aid in determining the technological basis for New Source Performance Standards for Industrial Boilers, addresses the use of synthetic fuels produced from coal as a precombustion emission control for new industrial boilers. The synthetic fuels tech...

  4. 34. TOP O THE BOILER SHOWING CONSTRUCTION DETAILS. NOTE THE ...

    Library of Congress Historic Buildings Survey, Historic Engineering Record, Historic Landscapes Survey

    34. TOP O THE BOILER SHOWING CONSTRUCTION DETAILS. NOTE THE 1/2-INCH ROUND IRON REINFORCING ROD AND GALVANIZED FARM FENCING IN THE RIGHT FOREGROUND. AND THE EXPANDED METAL LATH WITH CEMENT COATING IN THE CEILING ABOVE THE BOILER. - Moravian Pottery & Tile Works, Southwest side of State Route 313 (Swamp Road), Northwest of East Court Street, Doylestown, Bucks County, PA

  5. DESIGN REPORT: LOW-NOX BURNERS FOR PACKAGE BOILERS

    EPA Science Inventory

    The report describes a low-NOx burner design, presented for residual-oil-fired industrial boilers and boilers cofiring conventional fuels and nitrated hazardous wastes. The burner offers lower NOx emission levels for these applications than conventional commercial burners. The bu...

  6. NOX EMISSION FACTORS FOR WOOD-FIRED BOILERS

    EPA Science Inventory

    The report gives results of a review of NOx emission data from 14 wood-fired boilers. Types of wood used as fuel included sawdust, chips, shavings, edgings, bark, and other processing residues. Boilers tested ranged in size from 1.5 to 67 MW (4,500 to 200,000 lb steam/hr). The ma...

  7. 18. Internal view of boiler in steam space above return ...

    Library of Congress Historic Buildings Survey, Historic Engineering Record, Historic Landscapes Survey

    18. Internal view of boiler in steam space above return flues, looking aft in ship toward return chamber. Inclined and vertical stays are used to reinforce flat boiler plates against distortion under pressure. - Ferry TICONDEROGA, Route 7, Shelburne, Chittenden County, VT

  8. 16. Boiler room, view looking east showing three, four pass ...

    Library of Congress Historic Buildings Survey, Historic Engineering Record, Historic Landscapes Survey

    16. Boiler room, view looking east showing three, four pass horizontal Cleaver Brooks Package Boilers, 1-150 H.P. and 2-200 H.P., 6900 lbs/hour and 5175 lbs/hour, 200 PSI - East Boston Pumping Station, Chelsea Street at Chelsea Creek, Boston, Suffolk County, MA

  9. 46 CFR 61.05-20 - Boiler safety valves.

    Code of Federal Regulations, 2011 CFR

    2011-10-01

    ... 46 Shipping 2 2011-10-01 2011-10-01 false Boiler safety valves. 61.05-20 Section 61.05-20 Shipping COAST GUARD, DEPARTMENT OF HOMELAND SECURITY (CONTINUED) MARINE ENGINEERING PERIODIC TESTS AND..., superheater, or reheater of a boiler shall be tested at the interval specified by table 61.05-10....

  10. 46 CFR 61.05-20 - Boiler safety valves.

    Code of Federal Regulations, 2013 CFR

    2013-10-01

    ... 46 Shipping 2 2013-10-01 2013-10-01 false Boiler safety valves. 61.05-20 Section 61.05-20 Shipping COAST GUARD, DEPARTMENT OF HOMELAND SECURITY (CONTINUED) MARINE ENGINEERING PERIODIC TESTS AND..., superheater, or reheater of a boiler shall be tested at the interval specified by table 61.05-10....

  11. 46 CFR 61.05-20 - Boiler safety valves.

    Code of Federal Regulations, 2014 CFR

    2014-10-01

    ... 46 Shipping 2 2014-10-01 2014-10-01 false Boiler safety valves. 61.05-20 Section 61.05-20 Shipping COAST GUARD, DEPARTMENT OF HOMELAND SECURITY (CONTINUED) MARINE ENGINEERING PERIODIC TESTS AND..., superheater, or reheater of a boiler shall be tested at the interval specified by table 61.05-10....

  12. 46 CFR 61.05-20 - Boiler safety valves.

    Code of Federal Regulations, 2012 CFR

    2012-10-01

    ... 46 Shipping 2 2012-10-01 2012-10-01 false Boiler safety valves. 61.05-20 Section 61.05-20 Shipping COAST GUARD, DEPARTMENT OF HOMELAND SECURITY (CONTINUED) MARINE ENGINEERING PERIODIC TESTS AND..., superheater, or reheater of a boiler shall be tested at the interval specified by table 61.05-10....

  13. 46 CFR 61.05-20 - Boiler safety valves.

    Code of Federal Regulations, 2010 CFR

    2010-10-01

    ... 46 Shipping 2 2010-10-01 2010-10-01 false Boiler safety valves. 61.05-20 Section 61.05-20 Shipping COAST GUARD, DEPARTMENT OF HOMELAND SECURITY (CONTINUED) MARINE ENGINEERING PERIODIC TESTS AND..., superheater, or reheater of a boiler shall be tested at the interval specified by table 61.05-10....

  14. FABRIC FILTRATION ANALYSES FOR THREE UTILITY BOILER FLYASHES

    EPA Science Inventory

    The report gives results of fabric filter analyses of flyash from three utility boilers. A major aim of the program was to augment the present data base for modeling fabric filter systems designed to control inhalable particulate (IP) emissions from coal-fired boilers. Emphasis w...

  15. 38. ELEPHANT BOILERS 1905: Photocopy of April 1905 photograph ...

    Library of Congress Historic Buildings Survey, Historic Engineering Record, Historic Landscapes Survey

    38. ELEPHANT BOILERS - 1905: Photocopy of April 1905 photograph showing elephant boilers along the west wall of the Washington and Mason Street powerhouse and car barn. View looking west on first floor of building. - San Francisco Cable Railway, Washington & Mason Streets, San Francisco, San Francisco County, CA

  16. 76. General view looking east showing Rust Co. boiler stacks ...

    Library of Congress Historic Buildings Survey, Historic Engineering Record, Historic Landscapes Survey

    76. General view looking east showing Rust Co. boiler stacks at left, Babcock & Wilcox type boiler stacks at right, Dovel horizontal gas washer in foreground, and No. 1 Furnace in distance. - Sloss-Sheffield Steel & Iron, First Avenue North Viaduct at Thirty-second Street, Birmingham, Jefferson County, AL

  17. 32. INTERIOR BOILER HOUSE Above the two furnaces, one ...

    Library of Congress Historic Buildings Survey, Historic Engineering Record, Historic Landscapes Survey

    32. INTERIOR - BOILER HOUSE Above the two furnaces, one of the boilers can be seen to the upper left. The large pipes in the foreground are all that remain of the distribution system. Most of the pipe and tubing have been stripped from the room and sold for scrap. - Hovden Cannery, 886 Cannery Row, Monterey, Monterey County, CA

  18. 13. VIEW LOOKING NORTHEAST FROM ROOF OF WEST BOILER ROOM ...

    Library of Congress Historic Buildings Survey, Historic Engineering Record, Historic Landscapes Survey

    13. VIEW LOOKING NORTHEAST FROM ROOF OF WEST BOILER ROOM AT SIROCCO DUST COLLECTOR WHICH FORMED PART OF THE ORIGINAL POLLUTION CONTROL SYSTEM FOR BOILERS 900 AND 901 INSTALLED IN 1926-1928. - New York, New Haven & Hartford Railroad, Cos Cob Power Plant, Sound Shore Drive, Greenwich, Fairfield County, CT

  19. 11. VIEW OF GAS FIRED BOILERS. Erie City Iron Works, ...

    Library of Congress Historic Buildings Survey, Historic Engineering Record, Historic Landscapes Survey

    11. VIEW OF GAS FIRED BOILERS. Erie City Iron Works, Model AA60, SN No. 685, size 16, Fuel No. 2 oil or gas, max input 13400. - Juniata Shops, Power Plant & Boiler House, East of Fourth Avenue at Second Street, Altoona, Blair County, PA

  20. DESIGN REPORT LOW-NOX BURNERS FOR PACKAGE BOILERS

    EPA Science Inventory

    The report describes a low-NOx burner design, presented for residual-oil-fired industrial boilers and boilers cofiring conventional fuels and nitrated hazardous wastes. The burner offers lower NOx emission levels for these applications than conventional commercial burners. The bu...

  1. 9. RW Meyer Sugar Mill: 18761889. Locomotivetype, firetube, portable boiler, ...

    Library of Congress Historic Buildings Survey, Historic Engineering Record, Historic Landscapes Survey

    9. RW Meyer Sugar Mill: 1876-1889. Locomotive-type, fire-tube, portable boiler, No. 1 model. Manufactured by Ames Iron Works, Oswego, New York, 1879. 120 lbs/sq. inch working pressure, 66 sq. ft. heating surface in tubes. View: from side. The boiler provided steam for steam engine which in turn powered the mill's centrifugals. The section on the left side included the firebox with its surrounding water-legs. The fluted chimney-type structure is the steam port, safety valve, and whistle. Column projecting from side was part of steam pressure and water gauge. Pipe running above boiler carried steam to the engine. Pipe running below boiler provided the boiler feed-water. Cylindrical section included 22 fire-tube surrounded by water. The far right ... - R. W. Meyer Sugar Mill, State Route 47, Kualapuu, Maui County, HI

  2. Coal reburning for cyclone boiler NO sub x control demonstration

    SciTech Connect

    Haggard, R.W. Jr.

    1991-01-01

    It is the objective of the Coal Reburning for Cyclone Boiler NOx Control Project to fully establish that the coal reburning clean coal technology offers cost-effective alternatives to cyclone operating electric utilities for overall oxides of nitrogen control. The project will evaluate the applicability of the reburning technology for reducing NOx emissions in full scale cyclone-fired boilers which use coal as a primary fuel. The performance goals while burning coal are: (1) Greater than 50 percent reduction in NOx emissions, as referenced to the uncontrolled (baseline) conditions at full load. (2) No serious impact on cyclone combustor operation, boiler efficiency or boiler fireside performance (corrosion and deposition), or boiler ash removal system performance.

  3. Coal reburning for cyclone boiler NO sub x control demonstration

    SciTech Connect

    Not Available

    1991-01-01

    It is the objective of the Coal Reburning for Cyclone Boiler NO{sub x} Control Project to fully establish that the cola reburning clean coal technology offers cost-effective alternatives to cyclone operating electric utilities for overall oxides of nitrogen control. The project will evaluate the applicability of the reburning technology for reducing NO{sub x} emissions in full scale cyclone-fired boilers which use coal as a primary fuel. The performance goals while burning coal are: (1) Greater than 50 percent reduction in NO{sub x} emissions, as referenced to the uncontrolled (baseline) conditions at full load. (2) No serious impact on cyclone combustor operation, boiler efficiency or boiler fireside performance (corrosion and deposition), or boiler ash removal system performance.

  4. A Flexural Mode Tuning Technique for Membraned Boiler Tubing

    SciTech Connect

    Quarry, M J; Chinn, D J; Rose, J L

    2005-03-21

    Corrosion of tubing used in black-liquor recovery boilers is a major concern in all pulp and paper mills. Extensive corrosion in recovery boiler tubes can result in a significant safety and environmental hazard. Considerable plant resources are expended to inspect recovery boiler tubing. Currently, visual and ultrasonic inspections are primarily used during the annual maintenance shutdown to monitor corrosion rates and cracking of tubing. This project is developing guided acoustic waves for use on recovery boiler tubing. The feature of this acoustic technique is its cost-effectiveness in inspecting long lengths of tubes from a single inspection point. A piezoelectric or electromagnetic transducer induces guided waves into the tubes. The transducer detects fireside defects from the cold side or fireside of the tube. Cracking and thinning on recovery boiler tubes have been detected with this technique in both laboratory and field applications.

  5. Conversion of a recovery boiler to bark burning

    SciTech Connect

    Barsin, J.A.; Pottera, J.; Stewart, G.

    1988-03-01

    Georgia-Pacific (GP) operates a large integrated pulp and paper mill in Crossett, Ark., which produces in excess of 1400 dry tons/day of various grades of bleached kraft paper. Steam generation in the mill is approximately 1.2 million lb/h, which is supplied by a 1500-ton recovery boiler, a 400,000-lb/h wood-waste boiler, and two power boilers. Because GP wanted to minimize its use of natural gas as a boiler fuel and because it had a retired recovery boiler which could be converted, the decision was made to proceed with this fuel conversion product as a means of reducing energy costs per ton of product. This paper also discusses the biomass fuel handling system.

  6. INFLUENCE OF OXIDE GROWTH AND METAL CREEP ON STRAIN DEVELOPMENT IN THE STEAM-SIDE OXIDE IN BOILER TUBES

    SciTech Connect

    Sabau, Adrian S; Wright, Ian G

    2010-01-01

    This effort is concerned with developing a quantitative description of the exfoliation behavior of oxide scales grown inside steam tubes in a pressure boiler. Consideration of the development of stress/strain in growing oxides has included expansion mismatch-induced strains during thermal cycling as well as inelastic mechanical effects from oxide/alloy creep phenomena and volume change from oxide growth. The magnitude of the parameters used has been closely matched to actual boiler operating practice. The creep model used was validated against published data. Representation of oxide growth-induced strain was found to be a difficult challenge because the processes involved are not fully understood. In addition to the traditional uniaxial (radial) and dilatational models, lateral growth models are discussed in the context of experimentally-derived criteria, such as the level of elastic strains involved in oxide exfoliation. It was found that strain variation in the oxide cannot be neglected.

  7. Gas reburn retrofit on an industrial cyclone boiler

    SciTech Connect

    Farzan, H.; Latham, C.E.; Maringo, G.J.

    1996-01-01

    Eastman Kodak Company`s cyclone boiler (Unit No. 43), located in Rochester, New York, is being retrofitted with the gas reburning technology developed by Babcock & Wilcox (B & W) to reduce NO{sub x} emissions in order to comply with the Title I, ozone nonattainment, of the Clean Air Act Amendments (CAAA) of 1990. The required NO{sub x} reduction from baseline levels necessary to meet the presumptive limit set in New York`s regulation is about 47%. Eastman Kodak and the Gas Research Institute (GRI) are cosponsoring this project. B & W is the prime contractor and contract negotiations with Chevron as the gas supplier are presently being finalized. Equipment installation for the gas reburn system is scheduled for a September 1995 outage. No. 43 Boiler`s maximum continuous rating (MCR) is 550,000 pounds per hour of steam flow or approximately equivalent to 60 MW{sub e}. Because of the compact boiler design, there is insufficient gas residence time to use pulverized coal or oil as the reburn fuel, thus making it a prime candidate for gas reburn. Kodak currently has four cyclone boilers. Based on successful completion of this gas reburn project, modifying the other three cyclone boilers with gas reburn technology is anticipated. The paper will describe B & W`s gas reburn data from a cyclone-equipped pilot facility (B & W`s Small Boiler Simulator), gas reburn design information specific to Eastman Kodak No. 43 Boiler, and numerical modeling experiences based on the pilot-scale Small Boiler Simulator (SBS) results along with those from a full-scale commercial boiler.

  8. Old boilers to profitable use with local biofuels

    SciTech Connect

    Hankala, J.

    1998-07-01

    To convert an old plant is often an economically advantageous alternative for a new boiler. The most important sources of biomass in industrial countries are residues from forestry, industry and agriculture. Sludges and wastes from industry, communities and households also contain useful energy. Still in many places there are existing power plants which can be converted to burn biofuels with low investment costs. An efficient and proven way is to convert an existing boiler to fluidized bed combustion (FBC) or use atmospheric circulating fluidized bed biofuel gasification connected to an existing boiler. Modern Fluidized Bed Combustion and Gasification gives us a possibility to burn biomass, sludges and many kinds of wastes in an efficient way with low emissions. Fluidized bed technologies are divided into bubbling fluidized bed (BFB) and circulating fluidized bed (CFB) solutions. When making a boiler conversion to fluidized bed combustion, lower furnace of an existing boiler is converted and fuel receiving, handling and transportation system is installed. In many cases most of the existing boiler heating surfaces and a majority of the existing auxiliary equipment can be utilized. The circulating fluidized bed gasifier consists of the inside refractory-lined steel vessel, where fuel is gasified in a hot fluidized gas solid particle suspension. In the gasifier, the biofuels will be converted to combustible gas at atmospheric pressure at the temperature 800--900 C. The hot gas from the gasifier will be cooled down to 650--750 C in the air preheater. The hot gas is led directly to separate burners, which are located in the existing boiler furnace. The gas is burned in the boiler and replaces a part of the coal used in the boiler. Typical fuels for the FBC-boilers are wet fuels such as bark, wood waste, peat and sludges. These fuels normally contain 40--70% water.

  9. Establishing an energy efficiency recommendation for commercial boilers

    SciTech Connect

    Ware, Michelle J.

    2000-08-01

    To assist the federal government in meeting its energy reduction goals, President Clinton's Executive Order 12902 established the Procurement Challenge, which directed all federal agencies to purchase equipment within the top 25th percentile of efficiency. Under the direction of DOE's Federal Energy Management Program (FEMP), the Procurement Challenge's goal is to create efficiency recommendations for all energy-using products that could substantially impact the government's energy reduction goals, like commercial boilers. A typical 5,000,000 Btuh boiler, with a thermal efficiency of 83.2%, can have lifetime energy cost savings of $40,000 when compared to a boiler with a thermal efficiency of 78%. For the federal market, which makes up 2% of the boiler market, this means lifetime energy cost savings of over $25,600,000. To establish efficiency recommendations, FEMP uses standardized performance ratings for products sold in the marketplace. Currently, the boiler industry uses combustion efficiency and, sometimes, thermal efficiency performance measures when specifying a commercial boiler. For many years, the industry has used these efficiency measures interchangeably, causing confusion about boiler performance measurements, and making it difficult for FEMP to establish the top 25th percentile of efficiency. This paper will illustrate the method used to establish FEMP's recommendation for boilers. The method involved defining a correlation between thermal and combustion efficiency among boiler classifications; using the correlation to model a data set of all the boiler types available in the market; and identifying how the correlation affected the top 25th percentile analysis. The paper also will discuss the applicability of this method for evaluating other equipment for which there are limited data on performance ratings.

  10. Evaluation of Iron Aluminide Weld Overlays for Erosion-Corrosion Resistant Boiler Tube Coatings in Low NOx Boilers

    SciTech Connect

    Regina, J.R.; Lim, M.; Barbosa, N., DuPont, J.N.; Marder, A.R.

    2000-04-28

    Iron aluminide weld overlays containing ternary additions and thermal spray coatings are being investigated for corrosion protection of boiler tubes in Low NO{sub x} burners. The primary objective of the research is to identify overlay and thermal spray compositions that provide corrosion protection of waterwall boiler tubes.

  11. Boiler Materials for Ultrasupercritical Coal Power Plants

    SciTech Connect

    R. Viswanathan; K. Coleman; J. Shingledecker; J. Sarver; G. Stanko; M. Borden; W. Mohn; S. Goodstine; I. Perrin

    2006-01-31

    The U.S. Department of Energy (DOE) and the Ohio Coal Development Office (OCDO) have recently initiated a project aimed at identifying, evaluating, and qualifying the materials needed for the construction of the critical components of coal-fired boilers capable of operating at much higher efficiencies than current generation of supercritical plants. This increased efficiency is expected to be achieved principally through the use of ultrasupercritical steam conditions (USC). A limiting factor in this can be the materials of construction. The project goal is to assess/develop materials technology that will enable achieving turbine throttle steam conditions of 760 C (1400 F)/35 MPa (5000 psi). This goal seems achievable based on a preliminary assessment of material capabilities. The project is further intended to build further upon the alloy development and evaluation programs that have been carried out in Europe and Japan. Those programs have identified ferritic steels capable of meeting the strength requirements of USC plants up to approximately 620 C (1150 F) and nickel-based alloys suitable up to 700 C (1300 F). In this project, the maximum temperature capabilities of these and other available high-temperature alloys are being assessed to provide a basis for materials selection and application under a range of conditions prevailing in the boiler. This report provides a quarterly status report for the period of October 1 to December 30, 2005.

  12. BOILER MATERIALS FOR ULTRASUPERCRITICAL COAL POWER PLANTS

    SciTech Connect

    R. Viswanathan; K. Coleman; J. Shingledecker; J. Sarver; G. Stanko; M. Borden; W. Mohn; S. Goodstine; I. Perrin

    2005-10-27

    The U.S. Department of Energy (DOE) and the Ohio Coal Development Office (OCDO) have recently initiated a project aimed at identifying, evaluating, and qualifying the materials needed for the construction of the critical components of coal-fired boilers capable of operating at much higher efficiencies than current generation of supercritical plants. This increased efficiency is expected to be achieved principally through the use of ultrasupercritical steam conditions (USC). A limiting factor in this can be the materials of construction. The project goal is to assess/develop materials technology that will enable achieving turbine throttle steam conditions of 760 C (1400 F)/35 MPa (5000 psi). This goal seems achievable based on a preliminary assessment of material capabilities. The project is further intended to build further upon the alloy development and evaluation programs that have been carried out in Europe and Japan. Those programs have identified ferritic steels capable of meeting the strength requirements of USC plants up to approximately 620 C (1150 F) and nickel-based alloys suitable up to 700 C (1300 F). In this project, the maximum temperature capabilities of these and other available high-temperature alloys are being assessed to provide a basis for materials selection and application under a range of conditions prevailing in the boiler. This report provides a quarterly status report for the period of July 1 to September 30, 2005.

  13. 'Boilers' along the southeast coast of Bermuda

    NASA Technical Reports Server (NTRS)

    2002-01-01

    Along the south shore of Bermuda, waves break continuously along algal/vermetid reefs (composed of algae and molluscs, not coral), forming 'boilers.' Boilers are named because the continuous breaking of waves makes it look as if the sea is boiling. This photograph taken from the International Space Station shows the eastern half of the main islands of Bermuda. Land use is about 6 percent cropland, 55 percent developed and 34 percent rural. Reflective white-colored areas are buildings and other developments surrounded by green areas of vegetation. St. David's Island is also home to the airport, with runways built out into Castle Harbour. Hurricane Erin passed northeast of Bermuda early on September 10 with 115 mile-per-hour winds (a Category 3 storm on the Saffir-Simpson Scale), but causing very minimal damage. Astronauts aboard Space Station Alpha photographed the area on September 14, 2001. By then, the skies had cleared and Erin had become an extratropical low near Newfoundland. Image ISS003-E-5735, was provided by the Earth Sciences and Image Analysis Laboratory at Johnson Space Center. Additional images taken by astronauts and cosmonauts can be viewed at the NASA-JSC Gateway to Astronaut Photography of Earth.

  14. Pyroflow Compact: The next generation CFB boiler

    SciTech Connect

    Darling, S.L.

    1995-12-31

    CFB technology is the modern way to burn coal and other solid fuels. This technology was specifically developed to address today`s needs for fuel flexibility and low emissions. The low furnace temperatures characteristic of CFB technology provide for (a) low NO{sub x} emissions, (b) low SO{sub 2} emissions via simple furnace limestone injection and (c) the ability to fire a wide range of fuels because slagging is avoided. Lack of pulverizers and stack gas scrubbers results in a simple design with low maintenance costs and high availability. Ahlstrom, responsible for many innovations in CFB technology, has recently developed an improved CFB boiler design called the Pyroflow Compact. This new design retains all the benefits of the proven AHLSTROM PYROFLOW{reg_sign}CFB boiler while providing many advantages. This paper will describe the design features of the new Pyroflow Compact design, the advantages of this new design, operating experience, an up-to-date list of projects and Ahlstrom`s future plans for the new design.

  15. Boiler Materials for Ultrasupercritical Coal Power Plants

    SciTech Connect

    R. Viswanathan; K. Coleman; J. Shingledecker; J. Sarver; G. Stanko; M. Borden; W. Mohn; S. Goodstine; I. Perrin

    2006-07-17

    The U.S. Department of Energy (DOE) and the Ohio Coal Development Office (OCDO) have recently initiated a project aimed at identifying, evaluating, and qualifying the materials needed for the construction of the critical components of coal-fired boilers capable of operating at much higher efficiencies than current generation of supercritical plants. This increased efficiency is expected to be achieved principally through the use of ultrasupercritical steam conditions (USC). A limiting factor in this can be the materials of construction. The project goal is to assess/develop materials technology that will enable achieving turbine throttle steam conditions of 760 C (1400 F)/35 MPa (5000 psi). This goal seems achievable based on a preliminary assessment of material capabilities. The project is further intended to build further upon the alloy development and evaluation programs that have been carried out in Europe and Japan. Those programs have identified ferritic steels capable of meeting the strength requirements of USC plants up to approximately 620 C (1150 F) and nickel-based alloys suitable up to 700 C (1300 F). In this project, the maximum temperature capabilities of these and other available high-temperature alloys are being assessed to provide a basis for materials selection and application under a range of conditions prevailing in the boiler. This report provides a quarterly status report for the period of April 1 to June 30, 2006.

  16. Boiler Materials For Ultrasupercritical Coal Power Plants

    SciTech Connect

    R. Viswanathan; K. Coleman; J. Shingledecker; J. Sarver; G. Stanko; M. Borden; W. Mohn; S. Goodstine; I. Perrin

    2006-09-30

    The U.S. Department of Energy (DOE) and the Ohio Coal Development Office (OCDO) have recently initiated a project aimed at identifying, evaluating, and qualifying the materials needed for the construction of the critical components of coal-fired boilers capable of operating at much higher efficiencies than current generation of supercritical plants. This increased efficiency is expected to be achieved principally through the use of ultrasupercritical steam conditions (USC). A limiting factor in this can be the materials of construction. The project goal is to assess/develop materials technology that will enable achieving turbine throttle steam conditions of 760 C (1400 F)/35 MPa (5000 psi). This goal seems achievable based on a preliminary assessment of material capabilities. The project is further intended to build further upon the alloy development and evaluation programs that have been carried out in Europe and Japan. Those programs have identified ferritic steels capable of meeting the strength requirements of USC plants up to approximately 620 C (1150 F) and nickel-based alloys suitable up to 700 C (1300 F). In this project, the maximum temperature capabilities of these and other available high-temperature alloys are being assessed to provide a basis for materials selection and application under a range of conditions prevailing in the boiler. This report provides a quarterly status report for the period of July 1 to September 30, 2006.

  17. BOILER MATERIALS FOR ULTRASUPERCRITICAL COAL POWER PLANTS

    SciTech Connect

    R. Viswanathan; K. Coleman; J. Shingledecker; J. Sarver; G. Stanko; M. Borden; W. Mohn; S. Goodstine; I. Perrin

    2005-08-01

    The U.S. Department of Energy (DOE) and the Ohio Coal Development Office (OCDO) have recently initiated a project aimed at identifying, evaluating, and qualifying the materials needed for the construction of the critical components of coal-fired boilers capable of operating at much higher efficiencies than current generation of supercritical plants. This increased efficiency is expected to be achieved principally through the use of ultrasupercritical steam conditions (USC). A limiting factor in this can be the materials of construction. The project goal is to assess/develop materials technology that will enable achieving turbine throttle steam conditions of 760 C (1400 F)/35 MPa (5000 psi). This goal seems achievable based on a preliminary assessment of material capabilities. The project is further intended to build further upon the alloy development and evaluation programs that have been carried out in Europe and Japan. Those programs have identified ferritic steels capable of meeting the strength requirements of USC plants up to approximately 620 C (1150 F) and nickel-based alloys suitable up to 700 C (1300 F). In this project, the maximum temperature capabilities of these and other available high-temperature alloys are being assessed to provide a basis for materials selection and application under a range of conditions prevailing in the boiler. This report provides a quarterly status report for the period of April 1 to June 30, 2005.

  18. BOILER MATERIALS FOR ULTRASUPERCRITICAL COAL POWER PLANTS

    SciTech Connect

    R. Viswanathan; K. Coleman; J. Shingledecker; J. Sarver; G. Stanko; M. Borden; W. Mohn; S. Goodstine; I. Perrin

    2005-04-27

    The U.S. Department of Energy (DOE) and the Ohio Coal Development Office (OCDO) have recently initiated a project aimed at identifying, evaluating, and qualifying the materials needed for the construction of the critical components of coal-fired boilers capable of operating at much higher efficiencies than current generation of supercritical plants. This increased efficiency is expected to be achieved principally through the use of ultrasupercritical steam conditions (USC). The project goal initially was to assess/develop materials technology that will enable achieving turbine throttle steam conditions of 760 C (1400 F)/35 MPa (5000 psi), although this goal for the main steam temperature had to be revised down to 732 C (1350 F), based on a preliminary assessment of material capabilities. The project is intended to build further upon the alloy development and evaluation programs that have been carried out in Europe and Japan. Those programs have identified ferritic steels capable of meeting the strength requirements of USC plants up to approximately 620 C (1150 F) and nickel-based alloys suitable up to 700 C (1300 F). In this project, the maximum temperature capabilities of these and other available high-temperature alloys are being assessed to provide a basis for materials selection and application under a range of conditions prevailing in the boiler. This report provides a quarterly status report for the period of July 1 to September 30, 2004.

  19. BOILER MATERIALS FOR ULTRASUPERCRITICAL COAL POWER PLANTS

    SciTech Connect

    R. Viswanathan; K. Coleman; J. Shingledecker; J. Sarver; G. Stanko; M. Borden; W. Mohn; S. Goodstine; I. Perrin

    2004-10-30

    The U.S. Department of Energy (DOE) and the Ohio Coal Development Office (OCDO) have recently initiated a project aimed at identifying, evaluating, and qualifying the materials needed for the construction of the critical components of coal-fired boilers capable of operating at much higher efficiencies than current generation of supercritical plants. This increased efficiency is expected to be achieved principally through the use of ultrasupercritical steam conditions (USC). The project goal initially was to assess/develop materials technology that will enable achieving turbine throttle steam conditions of 760 C (1400 F)/35 MPa (5000 psi), although this goal for the main steam temperature had to be revised down to 732 C (1350 F), based on a preliminary assessment of material capabilities. The project is intended to build further upon the alloy development and evaluation programs that have been carried out in Europe and Japan. Those programs have identified ferritic steels capable of meeting the strength requirements of USC plants up to approximately 620 C (1150 F) and nickel-based alloys suitable up to 700 C (1300 F). In this project, the maximum temperature capabilities of these and other available high-temperature alloys are being assessed to provide a basis for materials selection and application under a range of conditions prevailing in the boiler. This report provides a quarterly status report for the period of April to June 30, 2004.

  20. Boiler Materials for Ultrasupercritical Coal Power Plants

    SciTech Connect

    R. Viswanathan; J. Sarver; M. Borden; K. Coleman; J. Blough; S. Goodstine; R.W. Swindeman; W. Mohn; I. Perrin

    2003-04-21

    The U.S. Department of Energy (DOE) and the Ohio Coal Development Office (OCDO) have recently initiated a project aimed at identifying, evaluating, and qualifying the materials needed for the construction of the critical components of coal-fired boilers capable of operating at much higher efficiencies than current generation of supercritical plants. This increased efficiency is expected to be achieved principally through the use of ultrasupercritical steam conditions (USC). The project goal initially was to assess/develop materials technology that will enable achieving turbine throttle steam conditions of 760 C (1400 F)/35 MPa (5000 psi), although this goal for the main steam temperature had to be revised down to 732 C (1350 F), based on a preliminary assessment of material capabilities. The project is intended to build further upon the alloy development and evaluation programs that have been carried out in Europe and Japan. Those programs have identified ferritic steels capable of meeting the strength requirements of USC plants up to approximately 620 C (1150 F) and nickel-based alloys suitable up to 700 C (1300 F). In this project, the maximum temperature capabilities of these and other available high-temperature alloys are being assessed to provide a basis for materials selection and application under a range of conditions prevailing in the boiler. This report provides a quarterly status report for the period of July 1 to September 30, 2004.

  1. BOILER MATERIALS FOR ULTRASUPERCRITICAL COAL POWER PLANTS

    SciTech Connect

    R. Viswanathan; K. Coleman; J. Shingledecker; J. Sarver; G. Stanko; W. Mohn; M. Borden; S. Goodstine; I. Perrin

    2004-07-30

    The U.S. Department of Energy (DOE) and the Ohio Coal Development Office (OCDO) have recently initiated a project aimed at identifying, evaluating, and qualifying the materials needed for the construction of the critical components of coal-fired boilers capable of operating at much higher efficiencies than current generation of supercritical plants. This increased efficiency is expected to be achieved principally through the use of ultrasupercritical steam conditions (USC). The project goal initially was to assess/develop materials technology that will enable achieving turbine throttle steam conditions of 760 C (1400 F)/35 MPa (5000 psi), although this goal for the main steam temperature had to be revised down to 732 C (1350 F), based on a preliminary assessment of material capabilities. The project is intended to build further upon the alloy development and evaluation programs that have been carried out in Europe and Japan. Those programs have identified ferritic steels capable of meeting the strength requirements of USC plants up to approximately 620 C (1150 F) and nickel-based alloys suitable up to 700 C (1300 F). In this project, the maximum temperature capabilities of these and other available high-temperature alloys are being assessed to provide a basis for materials selection and application under a range of conditions prevailing in the boiler. This report provides a quarterly status report for the period of April to June 30, 2004.

  2. BOILER MATERIALS FOR ULTRASUPERCRITICAL COAL POWER PLANTS

    SciTech Connect

    K. Coleman; R. Viswanathan; J. Shingledecker; J. Sarver; G. Stanko; W. Mohn; M. Borden; S. Goodstine; I. Perrin

    2004-01-23

    The U.S. Department of Energy (DOE) and the Ohio Coal Development Office (OCDO) have recently initiated a project aimed at identifying, evaluating, and qualifying the materials needed for the construction of the critical components of coal-fired boilers capable of operating at much higher efficiencies than current generation of supercritical plants. This increased efficiency is expected to be achieved principally through the use of ultrasupercritical steam conditions (USC). The project goal initially was to assess/develop materials technology that will enable achieving turbine throttle steam conditions of 760 C (1400 F)/35 MPa (5000 psi), although this goal for the main steam temperature had to be revised down to 732 C (1350 F), based on a preliminary assessment of material capabilities. The project is intended to build further upon the alloy development and evaluation programs that have been carried out in Europe and Japan. Those programs have identified ferritic steels capable of meeting the strength requirements of USC plants up to approximately 620 C (1150 F) and nickel-based alloys suitable up to 700 C (1300 F). In this project, the maximum temperature capabilities of these and other available high-temperature alloys are being assessed to provide a basis for materials selection and application under a range of conditions prevailing in the boiler. This report provides a quarterly status report for the period of October 1 to December 30, 2003.

  3. BOILER MATERIALS FOR ULTRASUPERCRITICAL COAL POWER PLANTS

    SciTech Connect

    R. Viswanathan; K. Coleman; J. Shingledecker; J. Sarver; G. Stanko; M. Borden; W. Mohn; S. Goodstine; I. Perrin

    2005-01-31

    The U.S. Department of Energy (DOE) and the Ohio Coal Development Office (OCDO) have recently initiated a project aimed at identifying, evaluating, and qualifying the materials needed for the construction of the critical components of coal-fired boilers capable of operating at much higher efficiencies than current generation of supercritical plants. This increased efficiency is expected to be achieved principally through the use of ultrasupercritical steam conditions (USC). The project goal initially was to assess/develop materials technology that will enable achieving turbine throttle steam conditions of 760 C (1400 F)/35 MPa (5000 psi), although this goal for the main steam temperature had to be revised down to 732 C (1350 F), based on a preliminary assessment of material capabilities. The project is intended to build further upon the alloy development and evaluation programs that have been carried out in Europe and Japan. Those programs have identified ferritic steels capable of meeting the strength requirements of USC plants up to approximately 620 C (1150 F) and nickel-based alloys suitable up to 700 C (1300 F). In this project, the maximum temperature capabilities of these and other available high-temperature alloys are being assessed to provide a basis for materials selection and application under a range of conditions prevailing in the boiler. This report provides a quarterly status report for the period of July 1 to September 30, 2004.

  4. BOILER MATERIALS FOR ULTRASUPERCRITICAL COAL POWER PLANTS

    SciTech Connect

    R. Viswanathan; K. Coleman; J. Shingledecker; J. Sarver; G. Stanko; W. Mohn; M. Borden; S. Goodstine; I. Perrin

    2004-04-23

    The U.S. Department of Energy (DOE) and the Ohio Coal Development Office (OCDO) have recently initiated a project aimed at identifying, evaluating, and qualifying the materials needed for the construction of the critical components of coal-fired boilers capable of operating at much higher efficiencies than current generation of supercritical plants. This increased efficiency is expected to be achieved principally through the use of ultrasupercritical steam conditions (USC). The project goal initially was to assess/develop materials technology that will enable achieving turbine throttle steam conditions of 760 C (1400 F)/35 MPa (5000 psi), although this goal for the main steam temperature had to be revised down to 732 C (1350 F), based on a preliminary assessment of material capabilities. The project is intended to build further upon the alloy development and evaluation programs that have been carried out in Europe and Japan. Those programs have identified ferritic steels capable of meeting the strength requirements of USC plants up to approximately 620 C (1150 F) and nickel-based alloys suitable up to 700 C (1300 F). In this project, the maximum temperature capabilities of these and other available high-temperature alloys are being assessed to provide a basis for materials selection and application under a range of conditions prevailing in the boiler. This report provides a quarterly status report for the period of October 1 to December 30, 2003.

  5. Boiler Materials for Ultrasupercritical Coal Power Plants

    SciTech Connect

    R. Viswanathan; K. Coleman; J. Shingledecker; J. Sarver; G. Stanko; M. Borden; W. Mohn; S. Goodstine; I. Perrin

    2006-04-20

    The U.S. Department of Energy (DOE) and the Ohio Coal Development Office (OCDO) have recently initiated a project aimed at identifying, evaluating, and qualifying the materials needed for the construction of the critical components of coal-fired boilers capable of operating at much higher efficiencies than current generation of supercritical plants. This increased efficiency is expected to be achieved principally through the use of ultrasupercritical steam conditions (USC). A limiting factor in this can be the materials of construction. The project goal is to assess/develop materials technology that will enable achieving turbine throttle steam conditions of 760 C (1400 F)/35 MPa (5000 psi). This goal seems achievable based on a preliminary assessment of material capabilities. The project is further intended to build further upon the alloy development and evaluation programs that have been carried out in Europe and Japan. Those programs have identified ferritic steels capable of meeting the strength requirements of USC plants up to approximately 620 C (1150 F) and nickel-based alloys suitable up to 700 C (1300 F). In this project, the maximum temperature capabilities of these and other available high-temperature alloys are being assessed to provide a basis for materials selection and application under a range of conditions prevailing in the boiler. This report provides a quarterly status report for the period of January 1 to March 31, 2006.

  6. Selection of stainless steel tubes to minimize hot corrosion in utility boilers

    SciTech Connect

    Fujikawa, H.; Makiura, H.

    1982-12-01

    Austenitic stainless steel tubes of AISI 304, 316, 321, and 347 types are sometimes exposed to severe hot corrosion environments in superheaters and reheaters of utility boilers. Hot corrosion depends on the existence of V/sub 2/O/sub 5/ and Na/sub 2/SO/sub 4/ in the oil-fired boilers, and of Na/sub 2/SO/sub 4/ and K/sub 2/SO/sub 4/ in the coal-fired boilers. Among various kinds of ash corrosions, the alkali sulphate-side corrosion has been mainly studied. Type 347 steel better resistance to alkali sulphate-side corrosion than 304, 316, and 321 steels. Alloying with Nb was more effective than Mo or Ti. A (Cr, Fe, Ni)-spinel oxide layer with little ash content formed at the scale-metal interface in 347 steel. In field tests, 347 tubes have maintained good resistance to both fire-side and steam-side corrosion for five years. However, 321 tubes were removed after three years of service, because of severe fire-side corrosion.

  7. Results from Alloy 600 And Alloy 690 Caustic SCC Model Boiler Tests

    SciTech Connect

    Miller, Frederick D.; Thomas, Larry E.

    2009-08-03

    A versatile model boiler test methodology was developed and used to compare caustic stress corrosion cracking (SCC) of mill annealed Alloy 600 and thermally treated Alloy 690. The model boiler included simulated crevice devices that efficiently and consistently concentrated Na2CO3, resulting in volatilization of CO2 with the steam and concentration of NaOH at the tube surfaces. The test methodology also included variation in tube stress, either produced by the primary to secondary side pressure differential, or by a novel method that reproducibly yields a higher stress condition on the tube. The significant effect of residual stress on tube SCC was also considered. SCC of both Alloy 600 and Alloy 690 were evaluated as a function of temperature and stress. Analytical transmission electron microscopy (ATEM) evaluations of the cracks and the grain boundaries ahead of the cracks were performed, providing insight into the SCC mechanism. This model boiler test methodology may be applicable to a range of bulkwater secondary chemistries that concentrate to produce aggressive crevice environments.

  8. 46 CFR 189.15-1 - Standards in inspection of hulls, boilers, and machinery.

    Code of Federal Regulations, 2014 CFR

    2014-10-01

    ... 46 Shipping 7 2014-10-01 2014-10-01 false Standards in inspection of hulls, boilers, and machinery... inspection of hulls, boilers, and machinery. In the inspection of hulls, boilers, and machinery of vessels... chapter, respecting material and construction of hulls, boilers, and machinery, and certificate...

  9. 46 CFR 52.20-17 - Opening between boiler and safety valve (modifies PFT-44).

    Code of Federal Regulations, 2014 CFR

    2014-10-01

    ... 46 Shipping 2 2014-10-01 2014-10-01 false Opening between boiler and safety valve (modifies PFT-44). 52.20-17 Section 52.20-17 Shipping COAST GUARD, DEPARTMENT OF HOMELAND SECURITY (CONTINUED) MARINE ENGINEERING POWER BOILERS Requirements for Firetube Boilers § 52.20-17 Opening between boiler and safety...

  10. 46 CFR 52.20-17 - Opening between boiler and safety valve (modifies PFT-44).

    Code of Federal Regulations, 2010 CFR

    2010-10-01

    ... 46 Shipping 2 2010-10-01 2010-10-01 false Opening between boiler and safety valve (modifies PFT-44). 52.20-17 Section 52.20-17 Shipping COAST GUARD, DEPARTMENT OF HOMELAND SECURITY (CONTINUED) MARINE ENGINEERING POWER BOILERS Requirements for Firetube Boilers § 52.20-17 Opening between boiler and safety...

  11. 46 CFR 52.20-17 - Opening between boiler and safety valve (modifies PFT-44).

    Code of Federal Regulations, 2011 CFR

    2011-10-01

    ... 46 Shipping 2 2011-10-01 2011-10-01 false Opening between boiler and safety valve (modifies PFT-44). 52.20-17 Section 52.20-17 Shipping COAST GUARD, DEPARTMENT OF HOMELAND SECURITY (CONTINUED) MARINE ENGINEERING POWER BOILERS Requirements for Firetube Boilers § 52.20-17 Opening between boiler and safety...

  12. 46 CFR 189.15-1 - Standards in inspection of hulls, boilers, and machinery.

    Code of Federal Regulations, 2012 CFR

    2012-10-01

    ... 46 Shipping 7 2012-10-01 2012-10-01 false Standards in inspection of hulls, boilers, and machinery... inspection of hulls, boilers, and machinery. In the inspection of hulls, boilers, and machinery of vessels... chapter, respecting material and construction of hulls, boilers, and machinery, and certificate...

  13. 46 CFR 61.05-5 - Preparation of boilers for inspection and test.

    Code of Federal Regulations, 2011 CFR

    2011-10-01

    ... 46 Shipping 2 2011-10-01 2011-10-01 false Preparation of boilers for inspection and test. 61.05-5... PERIODIC TESTS AND INSPECTIONS Tests and Inspections of Boilers § 61.05-5 Preparation of boilers for... preparing the boilers for the hydrostatic test, they shall be filled with water at not less than 70 °F....

  14. 46 CFR 52.25-7 - Electric boilers (modifies PEB-1 through PEB-19).

    Code of Federal Regulations, 2013 CFR

    2013-10-01

    ... Vessel Code (incorporated by reference; see 46 CFR 52.01-1). ... 46 Shipping 2 2013-10-01 2013-10-01 false Electric boilers (modifies PEB-1 through PEB-19). 52.25... ENGINEERING POWER BOILERS Other Boiler Types § 52.25-7 Electric boilers (modifies PEB-1 through...

  15. 30 CFR 56.13001 - General requirements for boilers and pressure vessels.

    Code of Federal Regulations, 2012 CFR

    2012-07-01

    ... 30 Mineral Resources 1 2012-07-01 2012-07-01 false General requirements for boilers and pressure... MINES Compressed Air and Boilers § 56.13001 General requirements for boilers and pressure vessels. All boilers and pressure vessels shall be constructed, installed, and maintained in accordance with...

  16. 30 CFR 56.13001 - General requirements for boilers and pressure vessels.

    Code of Federal Regulations, 2014 CFR

    2014-07-01

    ... 30 Mineral Resources 1 2014-07-01 2014-07-01 false General requirements for boilers and pressure... MINES Compressed Air and Boilers § 56.13001 General requirements for boilers and pressure vessels. All boilers and pressure vessels shall be constructed, installed, and maintained in accordance with...

  17. 46 CFR 91.15-1 - Standards in inspection of hulls, boilers, and machinery.

    Code of Federal Regulations, 2013 CFR

    2013-10-01

    ... 46 Shipping 4 2013-10-01 2013-10-01 false Standards in inspection of hulls, boilers, and machinery... hulls, boilers, and machinery. In the inspection of hulls, boilers, and machinery of vessels, the..., respecting material and inspection of hulls, boilers, and machinery, and the certificate of...

  18. 46 CFR 189.15-1 - Standards in inspection of hulls, boilers, and machinery.

    Code of Federal Regulations, 2013 CFR

    2013-10-01

    ... 46 Shipping 7 2013-10-01 2013-10-01 false Standards in inspection of hulls, boilers, and machinery... inspection of hulls, boilers, and machinery. In the inspection of hulls, boilers, and machinery of vessels... chapter, respecting material and construction of hulls, boilers, and machinery, and certificate...

  19. 49 CFR 230.20 - Alteration and repair report for steam locomotive boilers.

    Code of Federal Regulations, 2014 CFR

    2014-10-01

    ... boilers. 230.20 Section 230.20 Transportation Other Regulations Relating to Transportation (Continued... boilers. (a) Alterations. When an alteration is made to a steam locomotive boiler, the steam locomotive... maintained for the life of the boiler. (See appendix B of this part.) (b) Welded and riveted repairs...

  20. 9 CFR 91.22 - Protection from heat of boilers and engines.

    Code of Federal Regulations, 2011 CFR

    2011-01-01

    ... 9 Animals and Animal Products 1 2011-01-01 2011-01-01 false Protection from heat of boilers and... Protection from heat of boilers and engines. No animals shall be stowed along the alleyways leading to the engine or boiler rooms unless the sides of said engine or boiler rooms are covered by a tongue and...

  1. 46 CFR 91.15-1 - Standards in inspection of hulls, boilers, and machinery.

    Code of Federal Regulations, 2014 CFR

    2014-10-01

    ... 46 Shipping 4 2014-10-01 2014-10-01 false Standards in inspection of hulls, boilers, and machinery... hulls, boilers, and machinery. In the inspection of hulls, boilers, and machinery of vessels, the..., respecting material and inspection of hulls, boilers, and machinery, and the certificate of...

  2. 46 CFR 189.15-1 - Standards in inspection of hulls, boilers, and machinery.

    Code of Federal Regulations, 2011 CFR

    2011-10-01

    ... 46 Shipping 7 2011-10-01 2011-10-01 false Standards in inspection of hulls, boilers, and machinery... inspection of hulls, boilers, and machinery. In the inspection of hulls, boilers, and machinery of vessels... chapter, respecting material and construction of hulls, boilers, and machinery, and certificate...

  3. 30 CFR 57.13001 - General requirements for boilers and pressure vessels.

    Code of Federal Regulations, 2010 CFR

    2010-07-01

    ... 30 Mineral Resources 1 2010-07-01 2010-07-01 false General requirements for boilers and pressure... NONMETAL MINES Compressed Air and Boilers § 57.13001 General requirements for boilers and pressure vessels. All boilers and pressure vessels shall be constructed, installed, and maintained in accordance...

  4. 46 CFR 52.25-7 - Electric boilers (modifies PEB-1 through PEB-19).

    Code of Federal Regulations, 2010 CFR

    2010-10-01

    ... Vessel Code (incorporated by reference; see 46 CFR 52.01-1). ... 46 Shipping 2 2010-10-01 2010-10-01 false Electric boilers (modifies PEB-1 through PEB-19). 52.25... ENGINEERING POWER BOILERS Other Boiler Types § 52.25-7 Electric boilers (modifies PEB-1 through...

  5. 52. KEWANEE BOILER, MODEL FE561L. INSTALLED C. 1960 TO SUPPLEMENT ...

    Library of Congress Historic Buildings Survey, Historic Engineering Record, Historic Landscapes Survey

    52. KEWANEE BOILER, MODEL FE-561-L. INSTALLED C. 1960 TO SUPPLEMENT THE HARTLEY BOILERS (SEE PREVIOUS PHOTOS 50 AND 51). LOCATED IN BOILER ROOM ADDITION WEST OF MAIN BOILER ROOM. - Prattville Manufacturing Company, Number One, 242 South Court Street, Prattville, Autauga County, AL

  6. 30 CFR 57.13001 - General requirements for boilers and pressure vessels.

    Code of Federal Regulations, 2014 CFR

    2014-07-01

    ... 30 Mineral Resources 1 2014-07-01 2014-07-01 false General requirements for boilers and pressure... NONMETAL MINES Compressed Air and Boilers § 57.13001 General requirements for boilers and pressure vessels. All boilers and pressure vessels shall be constructed, installed, and maintained in accordance...

  7. 46 CFR 61.05-5 - Preparation of boilers for inspection and test.

    Code of Federal Regulations, 2010 CFR

    2010-10-01

    ... 46 Shipping 2 2010-10-01 2010-10-01 false Preparation of boilers for inspection and test. 61.05-5... PERIODIC TESTS AND INSPECTIONS Tests and Inspections of Boilers § 61.05-5 Preparation of boilers for... preparing the boilers for the hydrostatic test, they shall be filled with water at not less than 70 °F....

  8. 30 CFR 56.13001 - General requirements for boilers and pressure vessels.

    Code of Federal Regulations, 2011 CFR

    2011-07-01

    ... 30 Mineral Resources 1 2011-07-01 2011-07-01 false General requirements for boilers and pressure... MINES Compressed Air and Boilers § 56.13001 General requirements for boilers and pressure vessels. All boilers and pressure vessels shall be constructed, installed, and maintained in accordance with...

  9. 30 CFR 57.13001 - General requirements for boilers and pressure vessels.

    Code of Federal Regulations, 2013 CFR

    2013-07-01

    ... 30 Mineral Resources 1 2013-07-01 2013-07-01 false General requirements for boilers and pressure... NONMETAL MINES Compressed Air and Boilers § 57.13001 General requirements for boilers and pressure vessels. All boilers and pressure vessels shall be constructed, installed, and maintained in accordance...

  10. 46 CFR 91.15-1 - Standards in inspection of hulls, boilers, and machinery.

    Code of Federal Regulations, 2011 CFR

    2011-10-01

    ... 46 Shipping 4 2011-10-01 2011-10-01 false Standards in inspection of hulls, boilers, and machinery... hulls, boilers, and machinery. In the inspection of hulls, boilers, and machinery of vessels, the..., respecting material and inspection of hulls, boilers, and machinery, and the certificate of...

  11. 49 CFR 230.20 - Alteration and repair report for steam locomotive boilers.

    Code of Federal Regulations, 2011 CFR

    2011-10-01

    ... boilers. 230.20 Section 230.20 Transportation Other Regulations Relating to Transportation (Continued... boilers. (a) Alterations. When an alteration is made to a steam locomotive boiler, the steam locomotive... maintained for the life of the boiler. (See appendix B of this part.) (b) Welded and riveted repairs...

  12. 46 CFR 52.20-17 - Opening between boiler and safety valve (modifies PFT-44).

    Code of Federal Regulations, 2013 CFR

    2013-10-01

    ... 46 Shipping 2 2013-10-01 2013-10-01 false Opening between boiler and safety valve (modifies PFT-44). 52.20-17 Section 52.20-17 Shipping COAST GUARD, DEPARTMENT OF HOMELAND SECURITY (CONTINUED) MARINE ENGINEERING POWER BOILERS Requirements for Firetube Boilers § 52.20-17 Opening between boiler and safety...

  13. 46 CFR 61.05-5 - Preparation of boilers for inspection and test.

    Code of Federal Regulations, 2012 CFR

    2012-10-01

    ... 46 Shipping 2 2012-10-01 2012-10-01 false Preparation of boilers for inspection and test. 61.05-5... PERIODIC TESTS AND INSPECTIONS Tests and Inspections of Boilers § 61.05-5 Preparation of boilers for... preparing the boilers for the hydrostatic test, they shall be filled with water at not less than 70 °F....

  14. 49 CFR 230.20 - Alteration and repair report for steam locomotive boilers.

    Code of Federal Regulations, 2010 CFR

    2010-10-01

    ... boilers. 230.20 Section 230.20 Transportation Other Regulations Relating to Transportation (Continued... boilers. (a) Alterations. When an alteration is made to a steam locomotive boiler, the steam locomotive... maintained for the life of the boiler. (See appendix B of this part.) (b) Welded and riveted repairs...

  15. 46 CFR 71.15-1 - Standards in inspection of hulls, boilers, and machinery.

    Code of Federal Regulations, 2013 CFR

    2013-10-01

    ... 46 Shipping 3 2013-10-01 2013-10-01 false Standards in inspection of hulls, boilers, and machinery..., boilers, and machinery. In the inspection of hulls, boilers, and machinery of vessels, the standards... and inspection of hulls, boilers, and machinery, and the certificate of classification...

  16. 46 CFR 52.25-7 - Electric boilers (modifies PEB-1 through PEB-19).

    Code of Federal Regulations, 2014 CFR

    2014-10-01

    ... Vessel Code (incorporated by reference; see 46 CFR 52.01-1). ... 46 Shipping 2 2014-10-01 2014-10-01 false Electric boilers (modifies PEB-1 through PEB-19). 52.25... ENGINEERING POWER BOILERS Other Boiler Types § 52.25-7 Electric boilers (modifies PEB-1 through...

  17. 46 CFR 91.15-1 - Standards in inspection of hulls, boilers, and machinery.

    Code of Federal Regulations, 2012 CFR

    2012-10-01

    ... 46 Shipping 4 2012-10-01 2012-10-01 false Standards in inspection of hulls, boilers, and machinery... hulls, boilers, and machinery. In the inspection of hulls, boilers, and machinery of vessels, the..., respecting material and inspection of hulls, boilers, and machinery, and the certificate of...

  18. 46 CFR 52.25-5 - Miniature boilers (modifies PMB-1 through PMB-21).

    Code of Federal Regulations, 2010 CFR

    2010-10-01

    ... (incorporated by reference; see 46 CFR 52.01-1) ... 46 Shipping 2 2010-10-01 2010-10-01 false Miniature boilers (modifies PMB-1 through PMB-21). 52.25... ENGINEERING POWER BOILERS Other Boiler Types § 52.25-5 Miniature boilers (modifies PMB-1 through...

  19. 46 CFR 52.25-7 - Electric boilers (modifies PEB-1 through PEB-19).

    Code of Federal Regulations, 2012 CFR

    2012-10-01

    ... Vessel Code (incorporated by reference; see 46 CFR 52.01-1). ... 46 Shipping 2 2012-10-01 2012-10-01 false Electric boilers (modifies PEB-1 through PEB-19). 52.25... ENGINEERING POWER BOILERS Other Boiler Types § 52.25-7 Electric boilers (modifies PEB-1 through...

  20. 46 CFR 52.25-5 - Miniature boilers (modifies PMB-1 through PMB-21).

    Code of Federal Regulations, 2012 CFR

    2012-10-01

    ... (incorporated by reference; see 46 CFR 52.01-1) ... 46 Shipping 2 2012-10-01 2012-10-01 false Miniature boilers (modifies PMB-1 through PMB-21). 52.25... ENGINEERING POWER BOILERS Other Boiler Types § 52.25-5 Miniature boilers (modifies PMB-1 through...

  1. 46 CFR 71.15-1 - Standards in inspection of hulls, boilers, and machinery.

    Code of Federal Regulations, 2014 CFR

    2014-10-01

    ... 46 Shipping 3 2014-10-01 2014-10-01 false Standards in inspection of hulls, boilers, and machinery..., boilers, and machinery. In the inspection of hulls, boilers, and machinery of vessels, the standards... and inspection of hulls, boilers, and machinery, and the certificate of classification...

  2. 30 CFR 57.13001 - General requirements for boilers and pressure vessels.

    Code of Federal Regulations, 2011 CFR

    2011-07-01

    ... 30 Mineral Resources 1 2011-07-01 2011-07-01 false General requirements for boilers and pressure... NONMETAL MINES Compressed Air and Boilers § 57.13001 General requirements for boilers and pressure vessels. All boilers and pressure vessels shall be constructed, installed, and maintained in accordance...

  3. 30 CFR 56.13001 - General requirements for boilers and pressure vessels.

    Code of Federal Regulations, 2010 CFR

    2010-07-01

    ... 30 Mineral Resources 1 2010-07-01 2010-07-01 false General requirements for boilers and pressure... MINES Compressed Air and Boilers § 56.13001 General requirements for boilers and pressure vessels. All boilers and pressure vessels shall be constructed, installed, and maintained in accordance with...

  4. 46 CFR 52.25-5 - Miniature boilers (modifies PMB-1 through PMB-21).

    Code of Federal Regulations, 2013 CFR

    2013-10-01

    ... (incorporated by reference; see 46 CFR 52.01-1) ... 46 Shipping 2 2013-10-01 2013-10-01 false Miniature boilers (modifies PMB-1 through PMB-21). 52.25... ENGINEERING POWER BOILERS Other Boiler Types § 52.25-5 Miniature boilers (modifies PMB-1 through...

  5. 49 CFR 230.20 - Alteration and repair report for steam locomotive boilers.

    Code of Federal Regulations, 2012 CFR

    2012-10-01

    ... boilers. 230.20 Section 230.20 Transportation Other Regulations Relating to Transportation (Continued... boilers. (a) Alterations. When an alteration is made to a steam locomotive boiler, the steam locomotive... maintained for the life of the boiler. (See appendix B of this part.) (b) Welded and riveted repairs...

  6. 46 CFR 71.15-1 - Standards in inspection of hulls, boilers, and machinery.

    Code of Federal Regulations, 2012 CFR

    2012-10-01

    ... 46 Shipping 3 2012-10-01 2012-10-01 false Standards in inspection of hulls, boilers, and machinery..., boilers, and machinery. In the inspection of hulls, boilers, and machinery of vessels, the standards... and inspection of hulls, boilers, and machinery, and the certificate of classification...

  7. 46 CFR 61.05-5 - Preparation of boilers for inspection and test.

    Code of Federal Regulations, 2014 CFR

    2014-10-01

    ... 46 Shipping 2 2014-10-01 2014-10-01 false Preparation of boilers for inspection and test. 61.05-5... PERIODIC TESTS AND INSPECTIONS Tests and Inspections of Boilers § 61.05-5 Preparation of boilers for... preparing the boilers for the hydrostatic test, they shall be filled with water at not less than 70 °F....

  8. 49 CFR 230.20 - Alteration and repair report for steam locomotive boilers.

    Code of Federal Regulations, 2013 CFR

    2013-10-01

    ... boilers. 230.20 Section 230.20 Transportation Other Regulations Relating to Transportation (Continued... boilers. (a) Alterations. When an alteration is made to a steam locomotive boiler, the steam locomotive... maintained for the life of the boiler. (See appendix B of this part.) (b) Welded and riveted repairs...

  9. 46 CFR 52.25-5 - Miniature boilers (modifies PMB-1 through PMB-21).

    Code of Federal Regulations, 2011 CFR

    2011-10-01

    ... (incorporated by reference; see 46 CFR 52.01-1) ... 46 Shipping 2 2011-10-01 2011-10-01 false Miniature boilers (modifies PMB-1 through PMB-21). 52.25... ENGINEERING POWER BOILERS Other Boiler Types § 52.25-5 Miniature boilers (modifies PMB-1 through...

  10. 30 CFR 56.13001 - General requirements for boilers and pressure vessels.

    Code of Federal Regulations, 2013 CFR

    2013-07-01

    ... 30 Mineral Resources 1 2013-07-01 2013-07-01 false General requirements for boilers and pressure... MINES Compressed Air and Boilers § 56.13001 General requirements for boilers and pressure vessels. All boilers and pressure vessels shall be constructed, installed, and maintained in accordance with...

  11. 46 CFR 71.15-1 - Standards in inspection of hulls, boilers, and machinery.

    Code of Federal Regulations, 2011 CFR

    2011-10-01

    ... 46 Shipping 3 2011-10-01 2011-10-01 false Standards in inspection of hulls, boilers, and machinery..., boilers, and machinery. In the inspection of hulls, boilers, and machinery of vessels, the standards... and inspection of hulls, boilers, and machinery, and the certificate of classification...

  12. 46 CFR 52.20-17 - Opening between boiler and safety valve (modifies PFT-44).

    Code of Federal Regulations, 2012 CFR

    2012-10-01

    ... 46 Shipping 2 2012-10-01 2012-10-01 false Opening between boiler and safety valve (modifies PFT-44). 52.20-17 Section 52.20-17 Shipping COAST GUARD, DEPARTMENT OF HOMELAND SECURITY (CONTINUED) MARINE ENGINEERING POWER BOILERS Requirements for Firetube Boilers § 52.20-17 Opening between boiler and safety...

  13. 46 CFR 61.05-5 - Preparation of boilers for inspection and test.

    Code of Federal Regulations, 2013 CFR

    2013-10-01

    ... 46 Shipping 2 2013-10-01 2013-10-01 false Preparation of boilers for inspection and test. 61.05-5... PERIODIC TESTS AND INSPECTIONS Tests and Inspections of Boilers § 61.05-5 Preparation of boilers for... preparing the boilers for the hydrostatic test, they shall be filled with water at not less than 70 °F....

  14. 46 CFR 52.25-5 - Miniature boilers (modifies PMB-1 through PMB-21).

    Code of Federal Regulations, 2014 CFR

    2014-10-01

    ... (incorporated by reference; see 46 CFR 52.01-1) ... 46 Shipping 2 2014-10-01 2014-10-01 false Miniature boilers (modifies PMB-1 through PMB-21). 52.25... ENGINEERING POWER BOILERS Other Boiler Types § 52.25-5 Miniature boilers (modifies PMB-1 through...

  15. 46 CFR 52.25-7 - Electric boilers (modifies PEB-1 through PEB-19).

    Code of Federal Regulations, 2011 CFR

    2011-10-01

    ... Vessel Code (incorporated by reference; see 46 CFR 52.01-1). ... 46 Shipping 2 2011-10-01 2011-10-01 false Electric boilers (modifies PEB-1 through PEB-19). 52.25... ENGINEERING POWER BOILERS Other Boiler Types § 52.25-7 Electric boilers (modifies PEB-1 through...

  16. 30 CFR 57.13001 - General requirements for boilers and pressure vessels.

    Code of Federal Regulations, 2012 CFR

    2012-07-01

    ... 30 Mineral Resources 1 2012-07-01 2012-07-01 false General requirements for boilers and pressure... NONMETAL MINES Compressed Air and Boilers § 57.13001 General requirements for boilers and pressure vessels. All boilers and pressure vessels shall be constructed, installed, and maintained in accordance...

  17. 46 CFR 71.15-1 - Standards in inspection of hulls, boilers, and machinery.

    Code of Federal Regulations, 2010 CFR

    2010-10-01

    ... 46 Shipping 3 2010-10-01 2010-10-01 false Standards in inspection of hulls, boilers, and machinery..., boilers, and machinery. In the inspection of hulls, boilers, and machinery of vessels, the standards... and inspection of hulls, boilers, and machinery, and the certificate of classification...

  18. 46 CFR 189.15-1 - Standards in inspection of hulls, boilers, and machinery.

    Code of Federal Regulations, 2010 CFR

    2010-10-01

    ... 46 Shipping 7 2010-10-01 2010-10-01 false Standards in inspection of hulls, boilers, and machinery... inspection of hulls, boilers, and machinery. In the inspection of hulls, boilers, and machinery of vessels... chapter, respecting material and construction of hulls, boilers, and machinery, and certificate...

  19. 46 CFR 91.15-1 - Standards in inspection of hulls, boilers, and machinery.

    Code of Federal Regulations, 2010 CFR

    2010-10-01

    ... 46 Shipping 4 2010-10-01 2010-10-01 false Standards in inspection of hulls, boilers, and machinery... hulls, boilers, and machinery. In the inspection of hulls, boilers, and machinery of vessels, the..., respecting material and inspection of hulls, boilers, and machinery, and the certificate of...

  20. NaK pool-boiler solar receiver durability bench test. Volume 2: Metallurgical analysis

    NASA Astrophysics Data System (ADS)

    Goods, S. H.; Bradshaw, R. W.

    1995-01-01

    The principal materials used in the construction of a NaK based pool-boiler were analyzed. The device, operated for 7500 hours, accumulated 1000 thermal cycles to a peak temperature of 750 C. Haynes 230, used to fabricate the pool-boiler vessel, was found to perform satisfactorily. Air-side corrosion of the pool-boiler vessel was insignificant. Internal surface of the alloy exhibited some NaK-induced elemental dissolution; this dissolution was somewhat more extensive where the alloy was exposed to the liquid metal compared to regions exposed only to NaK vapor; however, the corresponding metal loss in all regions was inconsequential, never exceeding more than a few microns. Autogenous seam welds of the alloy responded in a similar fashion, exhibiting only minimal metal loss over the course of the experiment. While there was 50% loss in ductility of the alloy there remained adequate ductility for the anticipated operating environment. An enhanced boiling nucleation surface comprised of stainless steel powder brazed to the vessel ID showed no change in its structure. It remained intact, showing no cracking after repeated thermal cycling. Other materials used in the experiment showed more extensive degradation after exposure to the NaK. IN 600, used to fabricate thermowells, exhibited extensive surface and intergranular dissolution. Grain boundary dissolution was sufficiently severe in one of the thermowells to cause an air leak, resulting in experiment termination. BNi-3, a brazing alloy used to join the pool-boiler vessel, endcaps and thermowells, showed some dissolution where it was exposed to the NaK as well as thermal aging effects. However, all brazes remained structurally sound. A nickel metal ribbon showed catastrophic dissolution, resulting in the formation of deep (greater than 30 (mu)m) pits and cavities. A zirconium metal foil used to getter oxygen from the NaK became extremely brittle.