  1. Evidence for adsorbate-enhanced field emission from carbon nanotube fibers

    NASA Astrophysics Data System (ADS)

    Murray, P. T.; Back, T. C.; Cahay, M. M.; Fairchild, S. B.; Maruyama, B.; Lockwood, N. P.; Pasquali, M.

    2013-07-01

    We used residual gas analysis (RGA) to identify the species desorbed during field emission (FE) from a carbon nanotube (CNT) fiber. The RGA data show a sharp threshold for H2 desorption at an external field strength that coincides with a breakpoint in the FE data. A comprehensive model for the gradual transition of FE from adsorbate-enhanced CNTs at low bias to FE from CNTs with reduced H2 adsorbate coverage at high bias is developed which accounts for the gradual desorption of the H2 adsorbates, alignment of the CNTs at the fiber tip, and importance of self-heating effects with applied bias.

  2. Carbon fibers: Thermochemical recovery from advanced composite materials and activation to an adsorbent

    NASA Astrophysics Data System (ADS)

    Staley, Todd Andrew

    This research addresses an expanding waste disposal problem brought about by the increasing use of advanced composite materials, and the lack of technically and environmentally viable recycling methods for these materials. A thermochemical treatment process was developed and optimized for the recycling of advanced composite materials. Counter-current gasification was employed for the treatment of carbon fiber reinforced-epoxy resin composite wastes. These materials were treated, allowing the reclamation of the material's valuable components. As expected in gasification, the organic portion of the waste was thermochemically converted to a combustible gas with small amounts of organic compounds that were identified by GC/MS. These compounds were expected based on data in the literature. The composites contain 70% fiber reinforcement, and gasification yielded approximately 70% recovered fibers, representing nearly complete recovery of fibers from the waste. Through SEM and mechanical testing, the recovered carbon fibers were found to be structurally and mechanically intact, and amenable to re-use in a variety of applications, some of which were identified and tested. In addition, an application was developed for the carbon fiber component of the waste, as an activated carbon fiber adsorbent for the treatment of wastewaters. This novel class of adsorbent was found to have adsorption rates, for various organic molecules, up to a factor of ten times those of commercial granular activated carbon, and adsorption capacities similar to conventional activated carbons. Overall, the research addresses an existing environmental waste problem, employing a thermochemical technique to recycle and reclaim the waste. Components of the reclaimed waste material are then employed, after further modification, to address other existing and potential environmental waste problems.

  3. Porous, platinum nanoparticle-adsorbed carbon nanotube yarns for efficient fiber solar cells.

    PubMed

    Zhang, Sen; Ji, Chunyan; Bian, Zuqiang; Yu, Pingrong; Zhang, Luhui; Liu, Dianyi; Shi, Enzheng; Shang, Yuanyuan; Peng, Haitao; Cheng, Qiao; Wang, Dong; Huang, Chunhui; Cao, Anyuan

    2012-08-28

    Pt is a classical catalyst that has been extensively used in fuel cell and solar cell electrodes, owing to its high catalytic activity, good conductivity, and stability. In conventional fiber-shaped solar cells, solid Pt wires are usually adopted as the electrode material. Here, we report a Pt nanoparticle-adsorbed carbon nanotube yarn made by solution adsorption and yarn spinning processes, with uniformly dispersed Pt nanoparticles through the porous nanotube network. We have fabricated TiO(2)-based dye-sensitized fiber solar cells with a Pt-nanotube hybrid yarn as counter electrode and achieved a power conversion efficiency of 4.85% under standard illumination (AM1.5, 100 mW/cm(2)), comparable to the same type of fiber cells with a Pt wire electrode (4.23%). Adsorption of Pt nanoparticles within a porous nanotube yarn results in enhanced Pt-electrolyte interfacial area and significantly reduced charge-transfer resistance across the electrolyte interface, compared to a pure nanotube yarn or Pt wire. Our porous Pt-nanotube hybrid yarns have the potential to reduce the use of noble metals, lower the device weight, and improve the solar cell efficiency. PMID:22861684

  4. Sorption and modeling of mass transfer of toxic chemical vapors in activated-carbon fiber-cloth adsorbers

    USGS Publications Warehouse

    Lordgooei, M.; Sagen, J.; Rood, M.J.; Rostam-Abadi, M.

    1998-01-01

    A new activated-carbon fiber-cloth (ACFC) adsorber coupled with an electrothermal regenerator and a cryogenic condenser was designed and developed to efficiently capture and recover toxic chemical vapors (TCVs) from simulated industrial gas streams. The system was characterized for adsorption by ACFC, electrothermal desorption, and cryogenic condensation to separate acetone and methyl ethyl ketone from gas streams. Adsorption dynamics are numerically modeled to predict system characteristics during scale-up and optimization of the process in the future. The model requires diffusivities of TCVs into an activated-carbon fiber (ACF) as an input. Effective diffusivities of TCVs into ACFs were modeled as a function of temperature, concentration, and pore size distribution. Effective diffusivities for acetone at 65 ??C and 30-60 ppmv were measured using a chromatography method. The energy factor for surface diffusion was determined from comparison between the experimental and modeled effective diffusivities. The modeled effective diffusivities were used in a dispersive computational model to predict mass transfer zones of TCVs in fixed beds of ACFC under realistic conditions for industrial applications.

  5. A novel fiber-based adsorbent technology

    SciTech Connect

    Reynolds, T.A.

    1997-10-01

    In this Phase I Small Business Innovation Research program, Chemica Technologies, Inc. is developing an economical, robust, fiber-based adsorbent technology for removal of heavy metals from contaminated water. The key innovation is the development of regenerable adsorbent fibers and adsorbent fiber cloths that have high capacity and selectivity for heavy metals and are chemically robust. The process has the potential for widespread use at DOE facilities, mining operations, and the chemical process industry.

  6. Activated carbon fiber cloth adsorber with cryogenic condensation to capture and recover MEK and toluene from gas streams

    SciTech Connect

    Reece, C.S.; Lordgooei, M.; Rood, M.J.

    1998-12-31

    The Clean Air Act Amendments (CAAAs) of 1990 mandate reductions in emissions of toxic volatile organic compounds (TVOCs) to the atmosphere. These regulations have stimulated interest in developing new technologies to remove, capture, and recover TVOCs from air for reuse. A laboratory-scale activated carbon fiber cloth (ACFC)-cryogenic air quality control device was developed and operated to remove, capture, and recover methyl ethyl ketone (MEK) and toluene from gas streams. The system was tested with gas streams at room temperature, ambient pressure, and TVOC concentrations near 1000 ppmv in air. The relative humidity of the inlet gas stream was controlled to either 0 or 90%. The fixed bed adsorber contained 19.2 g of ACFC with a cross-sectional area of 16 cm2. The superficial gas velocity through the bed was 5.2 cm/sec, with a pressure drop near 23 cm H{sub 2}O. Breakthrough times for MEK were between 5.5 and 6.0 hr for dry inlet gas streams. Breakthrough times decreased by 36% at 90% RH. Comparable results were obtained for tests with toluene. Once the ACFC was saturated, it was regenerated in a low flow rate stream of N{sub 2} using electrothermal desorption. The gas stream emitted from the fixed bed during regeneration had TVOC concentrations near the saturation values for the compounds of interest. The TVOCs were then recovered for reuse with a cryogenic condenser between 203 and 233 K. Laboratory-scale tests demonstrate that the ACFC-cryogenic condensation system can operate consistently at low inlet TVOC concentrations generated over 18 hr periods. Results from the laboratory-scale system indicate this new device allows for successful removal, capture, and recovery of TVOCs such as MEK and toluene from simulated industrial gas streams, at low and high relative humidity conditions. No contamination of TVOC in the adsorption-regeneration-recovery process was detected by mass spectrometry.

  7. Hollow-fiber-based adsorbers for gas separation by pressure-swing adsorption

    SciTech Connect

    Feng, X.; Pan, C.Y.; McMinis, C.W.; Ivory, J.; Ghosh, D.

    1998-07-01

    Hollow-fiber-based adsorbers for gas separation by pressure-swing adsorption (PSA) was studied experimentally. The high efficiency of hollow-fiber-based adsorbers for gas separation was illustrated by hydrogen separation using fine-powder-activated carbon and molecular sieve as adsorbents. The adsorption equilibrium and dynamics of the hollow-fiber adsorbers were determined. The pressure drop of the gas flowing through the adsorbers was also examined. The adsorbers were tested for hydrogen separation from nitrogen, carbon dioxide, and a multicomponent gas mixture simulating ammonia synthesis purge gas. The PSA systems using the hollow-fiber adsorbers were very effective for hydrogen purification. The high separation efficiency is derived from the fast mass-transfer rate and low pressure drop, two key features of hollow-fiber-based adsorbers.

  8. A novel carbon fiber based porous carbon monolith

    SciTech Connect

    Burchell, T.D.; Klett, J.W.; Weaver, C.E.

    1995-06-01

    A novel porous carbon material based on carbon fibers has been developed. The material, when activated, develops a significant micro- or mesopore volume dependent upon the carbon fiber type utilized (isotropic pitch or polyacrylonitrile). The materials will find applications in the field of fluid separations or as a catalyst support. Here, the manufacture and characterization of our porous carbon monoliths are described. A novel adsorbent carbon composite material has been developed comprising carbon fibers and a binder. The material, called carbon fiber composite molecular sieve (CFCMS), was developed through a joint research program between Oak Ridge National Laboratory (ORNL) and the University of Kentucky, Center for Applied Energy Research (UKCAER).

  9. Adsorbed natural gas storage with activated carbon

    SciTech Connect

    Sun, Jian; Brady, T.A.; Rood, M.J.

    1996-12-31

    Despite technical advances to reduce air pollution emissions, motor vehicles still account for 30 to 70% emissions of all urban air pollutants. The Clean Air Act Amendments of 1990 require 100 cities in the United States to reduce the amount of their smog within 5 to 15 years. Hence, auto emissions, the major cause of smog, must be reduced 30 to 60% by 1998. Natural gas con be combusted with less pollutant emissions. Adsorbed natural gas (ANG) uses adsorbents and operates with a low storage pressure which results in lower capital costs and maintenance. This paper describes the production of an activated carbon adsorbent produced from an Illinois coal for ANG.

  10. Pyrolyzed feather fibers for adsorbent and high temperature applications

    NASA Astrophysics Data System (ADS)

    Senoz, Erman

    Chicken feather fibers (CFF) are problematic and costly for the poultry industry in terms of managing maintenance and disposal. Considering their great availability, low cost, and unique protein structure, CFF can be an environmentally friendly and bio-renewable candidate to replace petroleum products. CFF's low degradation and melting temperature render them useless at high temperatures. Pyrolysis methods were developed for CFF by using two temperature steps to convert them into high temperature resistant and adsorbent fibers while retaining their original physical appearance and affine dimensions. An intermolecular crosslinking mechanism in the first step of pyrolysis at 215 ºC for 24 h provided an intact fibrous structure with no subsequent melting. The evidence obtained from the thermal, bulk, and surface analysis techniques was indication of the simultaneous side chain degradation, polypeptide backbone scission, disulfide bond cleavage, and isopeptide crosslinking. The variation in the reaction kinetics of disulfide bond cleavage and isopeptide crosslinking played an important role in the melting transition. Consequently, long-lasting heat treatments below the melting point provided sufficient crosslinks in the protein matrix to keep the fibrous structure intact. Water-insoluble and crosslinked CFF reinforced the triglyceride-fatty acid based composites by providing a 15 fold increase in storage and tensile modulus at room temperature. These thermally stable fibers can be used instead of CFF in composites which may require high temperature compounding and molding processes. The second step of pyrolysis at 400--450 ºC for 1 h resulted in microporous fibers with a micropore volume of ˜0.18 cm3/g STP and with a narrower pore size distribution than commercial activated carbons through thermal degradation. Nearly all accessible pores in the microporous pyrolyzed chicken feather fibers (PCFF) had diameters less than 1 nm and therefore, showed a potential to be

  11. Adsorbent capability testing using desorption efficiency method on palm oil fiber

    NASA Astrophysics Data System (ADS)

    Manap, Nor Rahafza Abdul; Shamsudin, Roslinda

    2015-09-01

    The palm oil fiber had been used as filler in making thermoplastics, biocomposites and also used as adsorbent in treating waste water. In this study, palm oil fiber was used as adsorbent to treat indoor air pollutants that caused by toluene, ethylbenzene, ortho-, meta-, and para- xylene (o-, m-, p-xylene). Known amount of pollutants, ranges between 1.3 to 28 ppm was spiked into palm oil fiber and left in refrigerator for 24 hours. Then, elution of the pollutants was carried out by carbon disulphide as mobile phase or eluent. The ability of palm oil fiber as adsorbent was determine using desorption efficiency technique by gas chromatography with flame ionization detector (GC/FID). The desorption efficiency percentage given by toluene was in the range of 88.9% to 100%, 91% to 100% for ethylbenzene, 65% to 100% for pm-xylene and 92.9% to 100% for o-xylene. This percentage indicates that palm oil fiber can be used as adsorbent to treat indoor air pollutants.

  12. Nanotube composite carbon fibers

    NASA Astrophysics Data System (ADS)

    Andrews, R.; Jacques, D.; Rao, A. M.; Rantell, T.; Derbyshire, F.; Chen, Y.; Chen, J.; Haddon, R. C.

    1999-08-01

    Single walled carbon nanotubes (SWNTs) were dispersed in isotropic petroleum pitch matrices to form nanotube composite carbon fibers with enhanced mechanical and electrical properties. We find that the tensile strength, modulus, and electrical conductivity of a pitch composite fiber with 5 wt % loading of purified SWNTs are enhanced by ˜90%, ˜150%, and 340% respectively, as compared to the corresponding values in unmodified isotropic pitch fibers. These results serve to highlight the potential that exits for developing a spectrum of material properties through the selection of the matrix, nanotube dispersion, alignment, and interfacial bonding.

  13. Carbon Fiber Risk Analysis. [conference

    NASA Technical Reports Server (NTRS)

    1979-01-01

    The scope and status of the effort to assess the risks associated with the accidental release of carbon/graphite fibers from civil aircraft is presented. Vulnerability of electrical and electronic equipment to carbon fibers, dispersal of carbon fibers, effectiveness of filtering systems, impact of fiber induced failures, and risk methodology are among the topics covered.

  14. Carbon Fibers Conductivity Studies

    NASA Technical Reports Server (NTRS)

    Yang, C. Y.; Butkus, A. M.

    1980-01-01

    In an attempt to understand the process of electrical conduction in polyacrylonitrile (PAN)-based carbon fibers, calculations were carried out on cluster models of the fiber consisting of carbon, nitrogen, and hydrogen atoms using the modified intermediate neglect of differential overlap (MINDO) molecular orbital (MO) method. The models were developed based on the assumption that PAN carbon fibers obtained with heat treatment temperatures (HTT) below 1000 C retain nitrogen in a graphite-like lattice. For clusters modeling an edge nitrogen site, analysis of the occupied MO's indicated an electron distribution similar to that of graphite. A similar analysis for the somewhat less stable interior nitrogen site revealed a partially localized II electron distribution around the nitrogen atom. The differences in bonding trends and structural stability between edge and interior nitrogen clusters led to a two-step process proposed for nitrogen evolution with increasing HTT.

  15. Boron nitride converted carbon fiber

    DOEpatents

    Rousseas, Michael; Mickelson, William; Zettl, Alexander K.

    2016-04-05

    This disclosure provides systems, methods, and apparatus related to boron nitride converted carbon fiber. In one aspect, a method may include the operations of providing boron oxide and carbon fiber, heating the boron oxide to melt the boron oxide and heating the carbon fiber, mixing a nitrogen-containing gas with boron oxide vapor from molten boron oxide, and converting at least a portion of the carbon fiber to boron nitride.

  16. Carbon Fiber Composites

    NASA Technical Reports Server (NTRS)

    1997-01-01

    HyComp(R), Inc. development a line of high temperature carbon fiber composite products to solve wear problems in the harsh environment of steel and aluminum mills. WearComp(R), self-lubricating composite wear liners and bushings, combines carbon graphite fibers with a polyimide binder. The binder, in conjunction with the fibers, provides the slippery surface, one that demands no lubrication, yet wears at a very slow rate. WearComp(R) typically lasts six to ten times longer than aluminum bronze. Unlike bronze, WearComp polishes the same surface and imparts a self-lube film for years of service. It is designed for continuous operation at temperatures of 550 degrees Fahrenheit and can operate under high compressive loads.

  17. Method of carbonizing polyacrylonitrile fibers

    NASA Technical Reports Server (NTRS)

    Cagliostro, D. E.; Lerner, N. R. (Inventor)

    1983-01-01

    This invention relates to a method of carbonizing polyacrylonitrile fibers by exposing the fibers at an elevated temperature to an oxidizing atmosphere; then exposing the oxidized fibers to an atmosphere of an inert gas such as nitrogen containing a carbonaceous material such as acetylene. The fibers are preferably treated with an organic compound, for example benzoic acid, before the exposure to an oxidizing atmosphere. The invention also relates to the resulting fibers. The treated fibers have enhanced tensile strength.

  18. Method for the preparation of carbon fiber from polyolefin fiber precursor, and carbon fibers made thereby

    DOEpatents

    Naskar, Amit Kumar; Hunt, Marcus Andrew; Saito, Tomonori

    2015-08-04

    Methods for the preparation of carbon fiber from polyolefin fiber precursor, wherein the polyolefin fiber precursor is partially sulfonated and then carbonized to produce carbon fiber. Methods for producing hollow carbon fibers, wherein the hollow core is circular- or complex-shaped, are also described. Methods for producing carbon fibers possessing a circular- or complex-shaped outer surface, which may be solid or hollow, are also described.

  19. Multimetallic Electrodeposition on Carbon Fibers

    NASA Astrophysics Data System (ADS)

    Böttger-Hiller, F.; Kleiber, J.; Böttger, T.; Lampke, T.

    2016-03-01

    Efficient lightweight design requires intelligent materials that meet versatile functions. One approach is to extend the range of properties of carbon fiber reinforced plastics (CFRP) by plating the fiber component. Electroplating leads to metalized layers on carbon fibers. Herein only cyanide-free electrolytes where used. Until now dendrite-free layers were only obtained using current densities below 1.0 A dm-2. In this work, dendrite-free tin and copper coatings were achieved by pre-metalizing the carbon fiber substrates. Furthermore, applying a combination of two metals with different sized thermal expansion coefficient lead to a bimetallic coating on carbon fiber rovings, which show an actuatory effect.

  20. Stronger Carbon Fibers for Reinforced Plastics

    NASA Technical Reports Server (NTRS)

    Cagliostro, D. E.; Lerner, N. R.

    1983-01-01

    Process makes fibers 70 percent stronger at lower carbonization temperature. Stronger carbon fibers result from benzoic acid pretreatment and addition of acetylene to nitrogen carbonizing atmosphere. New process also makes carbon fibers of higher electrical resistance -- an important safety consideration.

  1. Carbon-fiber composite molecular sieves for gas separation

    SciTech Connect

    Jagtoyen, M.; Derbyshire, F.; Kimber, G.; Fei, Y.Q.

    1995-08-01

    The progress of research in the development of novel, rigid, monolithic adsorbent carbon fiber composites is described. Carbon fiber composites are produced at ORNL and activated at the CAER using steam or CO{sub 2} under different conditions, with the aims of producing a uniform degree of activation through the material, and of closely controlling pore structure and adsorptive properties The principal focus of the work to date has been to produce materials with narrow porosity for use in gas separations.

  2. Carbon Fiber Biocompatibility for Implants

    PubMed Central

    Petersen, Richard

    2016-01-01

    Carbon fibers have multiple potential advantages in developing high-strength biomaterials with a density close to bone for better stress transfer and electrical properties that enhance tissue formation. As a breakthrough example in biomaterials, a 1.5 mm diameter bisphenol-epoxy/carbon-fiber-reinforced composite rod was compared for two weeks in a rat tibia model with a similar 1.5 mm diameter titanium-6-4 alloy screw manufactured to retain bone implants. Results showed that carbon-fiber-reinforced composite stimulated osseointegration inside the tibia bone marrow measured as percent bone area (PBA) to a great extent when compared to the titanium-6-4 alloy at statistically significant levels. PBA increased significantly with the carbon-fiber composite over the titanium-6-4 alloy for distances from the implant surfaces of 0.1 mm at 77.7% vs. 19.3% (p < 10−8) and 0.8 mm at 41.6% vs. 19.5% (p < 10−4), respectively. The review focuses on carbon fiber properties that increased PBA for enhanced implant osseointegration. Carbon fibers acting as polymer coated electrically conducting micro-biocircuits appear to provide a biocompatible semi-antioxidant property to remove damaging electron free radicals from the surrounding implant surface. Further, carbon fibers by removing excess electrons produced from the cellular mitochondrial electron transport chain during periods of hypoxia perhaps stimulate bone cell recruitment by free-radical chemotactic influences. In addition, well-studied bioorganic cell actin carbon fiber growth would appear to interface in close contact with the carbon-fiber-reinforced composite implant. Resulting subsequent actin carbon fiber/implant carbon fiber contacts then could help in discharging the electron biological overloads through electrochemical gradients to lower negative charges and lower concentration. PMID:26966555

  3. Gasifiable carbon-graphite fibers

    NASA Technical Reports Server (NTRS)

    Humphrey, Marshall F. (Inventor); Ramohalli, Kumar N. R. (Inventor); Dowler, Warren L. (Inventor)

    1982-01-01

    Fine, carbon-graphite fibers do not combust during the combustion of a composite and are expelled into the air as fine conductive particles. Coating of the fibers with a salt of a metal having a work function below 4.2 eV such as an alkaline earth metal salt, e.g., calcium acetate, catalytically enhances combustion of the fibers at temperatures below 1000.degree. C. such that the fibers self-support combustion and burn to produce a non-conductive ash. Fire-polishing the fibers before application of the coating is desirable to remove sizing to expose the carbon surface to the catalyst.

  4. Fiber-based adsorbents having high adsorption capacities for recovering dissolved metals and methods thereof

    DOEpatents

    Janke, Christopher J; Dai, Sheng; Oyola, Yatsandra

    2014-05-13

    A fiber-based adsorbent and a related method of manufacture are provided. The fiber-based adsorbent includes polymer fibers with grafted side chains and an increased surface area per unit weight over known fibers to increase the adsorption of dissolved metals, for example uranium, from aqueous solutions. The polymer fibers include a circular morphology in some embodiments, having a mean diameter of less than 15 microns, optionally less than about 1 micron. In other embodiments, the polymer fibers include a non-circular morphology, optionally defining multiple gear-shaped, winged-shaped or lobe-shaped projections along the length of the polymer fibers. A method for forming the fiber-based adsorbents includes irradiating high surface area polymer fibers, grafting with polymerizable reactive monomers, reacting the grafted fibers with hydroxylamine, and conditioning with an alkaline solution. High surface area fiber-based adsorbents formed according to the present method demonstrated a significantly improved uranium adsorption capacity per unit weight over existing adsorbents.

  5. Fiber-based adsorbents having high adsorption capacities for recovering dissolved metals and methods thereof

    DOEpatents

    Janke, Christopher J.; Dai, Sheng; Oyola, Yatsandra

    2016-09-06

    A fiber-based adsorbent and a related method of manufacture are provided. The fiber-based adsorbent includes polymer fibers with grafted side chains and an increased surface area per unit weight over known fibers to increase the adsorption of dissolved metals, for example uranium, from aqueous solutions. The polymer fibers include a circular morphology in some embodiments, having a mean diameter of less than 15 microns, optionally less than about 1 micron. In other embodiments, the polymer fibers include a non-circular morphology, optionally defining multiple gear-shaped, winged-shaped or lobe-shaped projections along the length of the polymer fibers. A method for forming the fiber-based adsorbents includes irradiating high surface area polymer fibers, grafting with polymerizable reactive monomers, reacting the grafted fibers with hydroxylamine, and conditioning with an alkaline solution. High surface area fiber-based adsorbents formed according to the present method demonstrated a significantly improved uranium adsorption capacity per unit weight over existing adsorbents.

  6. Source of released carbon fibers

    NASA Technical Reports Server (NTRS)

    Bell, V. L.

    1979-01-01

    The potential for the release of carbon fibers from aircraft crashes/fires is addressed. Simulation of the conditions of aircraft crash fires in order to predict the quantities and forms of fibrous materials which might be released from civilian aircraft crashes/fires is considered. Figures are presented which describe some typical fiber release test activities together with some very preliminary results of those activities. The state of the art of carbon fiber release is summarized as well as some of the uncertainties concerning accidental fiber release.

  7. Coating Carbon Fibers With Platinum

    NASA Technical Reports Server (NTRS)

    Effinger, Michael R.; Duncan, Peter; Coupland, Duncan; Rigali, Mark J.

    2007-01-01

    A process for coating carbon fibers with platinum has been developed. The process may also be adaptable to coating carbon fibers with other noble and refractory metals, including rhenium and iridium. The coated carbon fibers would be used as ingredients of matrix/fiber composite materials that would resist oxidation at high temperatures. The metal coats would contribute to oxidation resistance by keeping atmospheric oxygen away from fibers when cracks form in the matrices. Other processes that have been used to coat carbon fibers with metals have significant disadvantages: Metal-vapor deposition processes yield coats that are nonuniform along both the lengths and the circumferences of the fibers. The electrical resistivities of carbon fibers are too high to be compatible with electrolytic processes. Metal/organic vapor deposition entails the use of expensive starting materials, it may be necessary to use a furnace, and the starting materials and/or materials generated in the process may be hazardous. The present process does not have these disadvantages. It yields uniform, nonporous coats and is relatively inexpensive. The process can be summarized as one of pretreatment followed by electroless deposition. The process consists of the following steps: The surfaces of the fiber are activated by deposition of palladium crystallites from a solution. The surface-activated fibers are immersed in a solution that contains platinum. A reducing agent is used to supply electrons to effect a chemical reduction in situ. The chemical reduction displaces the platinum from the solution. The displaced platinum becomes deposited on the fibers. Each platinum atom that has been deposited acts as a catalytic site for the deposition of another platinum atom. Hence, the deposition process can also be characterized as autocatalytic. The thickness of the deposited metal can be tailored via the duration of immersion and the chemical activity of the solution.

  8. Carbon Fiber Risk Analysis: Conclusions

    NASA Technical Reports Server (NTRS)

    Huston, R. J.

    1979-01-01

    It was concluded that preliminary estimates indicate that the public risk due to accidental release of carbon fiber from air transport aircraft is small. It was also concluded that further work is required to increase confidence in these estimates.

  9. Uranium Adsorbent Fibers Prepared by Atom-Transfer Radical Polymerization from Chlorinated Polypropylene and Polyethylene Trunk Fibers

    SciTech Connect

    Brown, Suree; Chatterjee, Sabornie; Li, Meijun; Yue, Yanfeng; Tsouris, Costas; Janke, Christopher J.; Saito, Tomonori; Dai, Sheng

    2015-12-10

    Seawater contains a large amount of uranium (~4.5 billion tons) which can serve as a limitless supply of an energy source. However, in order to make the recovery of uranium from seawater economically feasible, lower manufacturing and deployment costs are required, and thus, solid adsorbents must have high uranium uptake, reusability, and high selectivity toward uranium. In this study, atom-transfer radical polymerization (ATRP), without the radiation-induced graft polymerization (RIGP), was used for grafting acrylonitrile (AN) and tert-butyl acrylate (tBA) from a new class of trunk fibers, forming adsorbents in a readily deployable form. The new class of trunk fibers was prepared by the chlorination of PP round fiber, hollow-gear-shaped PP fiber, and hollow-gear-shaped PE fiber. During ATRP, degrees of grafting (d.g.) varied according to the structure of active chlorine sites on trunk fibers and ATRP conditions, and the d.g. as high as 2570% was obtained. Resulting adsorbent fibers were evaluated in U-spiked simulated seawater and the maximum adsorption capacity of 146.6 g U/kg, much higher than that of a standard adsorbent JAEA fiber (75.1 g/kg), was obtained. This new type of trunk fibers can be used for grafting a variety of uranium-interacting ligands, including designed ligands that are highly selective toward uranium.

  10. Uranium Adsorbent Fibers Prepared by Atom-Transfer Radical Polymerization from Chlorinated Polypropylene and Polyethylene Trunk Fibers

    DOE PAGES

    Brown, Suree; Chatterjee, Sabornie; Li, Meijun; Yue, Yanfeng; Tsouris, Costas; Janke, Christopher J.; Saito, Tomonori; Dai, Sheng

    2015-12-10

    Seawater contains a large amount of uranium (~4.5 billion tons) which can serve as a limitless supply of an energy source. However, in order to make the recovery of uranium from seawater economically feasible, lower manufacturing and deployment costs are required, and thus, solid adsorbents must have high uranium uptake, reusability, and high selectivity toward uranium. In this study, atom-transfer radical polymerization (ATRP), without the radiation-induced graft polymerization (RIGP), was used for grafting acrylonitrile (AN) and tert-butyl acrylate (tBA) from a new class of trunk fibers, forming adsorbents in a readily deployable form. The new class of trunk fibers wasmore » prepared by the chlorination of PP round fiber, hollow-gear-shaped PP fiber, and hollow-gear-shaped PE fiber. During ATRP, degrees of grafting (d.g.) varied according to the structure of active chlorine sites on trunk fibers and ATRP conditions, and the d.g. as high as 2570% was obtained. Resulting adsorbent fibers were evaluated in U-spiked simulated seawater and the maximum adsorption capacity of 146.6 g U/kg, much higher than that of a standard adsorbent JAEA fiber (75.1 g/kg), was obtained. This new type of trunk fibers can be used for grafting a variety of uranium-interacting ligands, including designed ligands that are highly selective toward uranium.« less

  11. Numerical Analysis on Adsorption Characteristics of Activated Carbon/Ethanol Pair in Finned Tube Type Adsorber

    NASA Astrophysics Data System (ADS)

    Makimoto, Naoya; Kariya, Keishi; Koyama, Shigeru

    The cycle performance of adsorption cooling system depends on the thermophysical properties of the adsorbent/refrigerant pair and configuration of the adsorber/desorber heat exchanger. In this study, a twodimensional analysis is carried out in order to clarify the performance of the finned tube type adsorber/desorber heat exchanger using a highly porous activated carbon powder (ACP)/ethanol pair. The simulation results show that the average cooling capacity per unit volume of adsorber/desorber heat exchanger and coefficient of performance (COP) can be improved by optimizing fin thickness, fin height, fin pitch and tube diameter. The performance of a single stage adsorption cooling system using ACP/ethanol pair is also compared with that of activated carbon fiber (ACF)/ethanol pair. It is found that the cooling capacities of each adsorbent/refrigerant pair increase with the decrease of adsorption/desorption time and the cooling capacity of ACP/ethanol pair is approximately 2.5 times as much as that of ACF/ethanol pair. It is also shown that COP of ACP/ethanol pair is superior to that of ACF/ethanol pair.

  12. Carbon adsorbents from products of solid fuel processing

    SciTech Connect

    Pokonova, Yu.V.; Grabovskii, A.I.

    1995-01-10

    Total shale phenols (mixture of alkylresorcinols) or their solution in commercial-grade furfural can be used for forming carbon adsorbents with high mechanical strength (up to 97%), high microporosity (up to 0.41 cm{sup 3}{center_dot}cm{sup -3}), and higher sorption capacity. Samples with medium burnout exhibit higher selectivity (than those molded from conventional wood tar) in the recovery of noble metals from multicomponent metal salt solutions. In these parameters they surpass commercial adsorbents as well. Samples with low burnout exhibit high selectivity and separation ability with respect to gas mixtures.

  13. Oil adsorbent produced by the carbonization of rice husks.

    PubMed

    Kumagai, Seiji; Noguchi, Yosuke; Kurimoto, Yasuji; Takeda, Koichi

    2007-01-01

    In this study, rice husks considered to be agricultural waste are converted into an adsorbent intended for use in the disposal of oil spills. The raw and refined (defiberized) husks of Japanese Akita Komachi rice were pyrolyzed in a vacuum (500 Pa) at 300-800 degrees C. The amount of A-heavy and B-heavy oils adsorbed on the carbonized rice husk were then evaluated. Oil adsorption is dependent on the type of oil. Rice husks refined and then pyrolyzed at 600-700 degrees C (1.0 g) adsorbed >6.0 g of B-heavy oil and <1.5 g of water, which indicates their usefulness as an adsorbent for oil spill cleanup in Japan. The refining process contributes to an improvement in the oil adsorption capacity, while the carbonization time (at 600 degrees C) has only a minor influence. The residual fluid components in the carbonized rice husks, rather than their porosity, are closely related to oil adsorption capacity.

  14. Biomass waste carbon materials as adsorbents for CO2 capture under post-combustion conditions

    NASA Astrophysics Data System (ADS)

    Calvo-Muñoz, Elisa; García-Mateos, Francisco José; Rosas, Juana; Rodríguez-Mirasol, José; Cordero, Tomás

    2016-05-01

    A series of porous carbon materials obtained from biomass waste have been synthesized, with different morphologies and structural properties, and evaluated as potential adsorbents for CO2 capture in post-combustion conditions. These carbon materials present CO2 adsorption capacities, at 25 ºC and 101.3 kPa, comparable to those obtained by other complex carbon or inorganic materials. Furthermore, CO2 uptakes under these conditions can be well correlated to the narrow micropore volume, derived from the CO2 adsorption data at 0 ºC (VDRCO2). In contrast, CO2 adsorption capacities at 25 ºC and 15 kPa are more related to only pores of sizes lower than 0.7 nm. The capacity values obtained in column adsorption experiments were really promising. An activated carbon fiber obtained from Alcell lignin, FCL, presented a capacity value of 1.3 mmol/g (5.7 %wt). Moreover, the adsorption capacity of this carbon fiber was totally recovered in a very fast desorption cycle at the same operation temperature and total pressure and, therefore, without any additional energy requirement. Thus, these results suggest that the biomass waste used in this work could be successfully valorized as efficient CO2 adsorbent, under post-combustion conditions, showing excellent regeneration performance.

  15. Uranium Recovery from Seawater: Development of Fiber Adsorbents Prepared via Atom-Transfer Radical Polymerization

    SciTech Connect

    Saito, Tomonori; Brown, Suree; Chatterjee, Sabornie; Kim, Jungseung; Tsouris, Costas; Mayes, Richard T; Kuo, Li-Jung; Gill, Gary; Oyola, Yatsandra; Janke, Christopher James; Dai, Sheng

    2014-01-01

    A novel adsorbent preparation method using atom-transfer radical polymerization (ATRP) combined with radiation-induced graft polymerization (RIGP) was developed to synthesize an adsorbent for uranium recovery from seawater. The ATRP method allowed a much higher degree of grafting on the adsorbent fibers (595 2818%) than that allowed by RIGP alone. The adsorbents were prepared with varied composition of amidoxime groups and hydrophilic acrylate groups. The successful preparation revealed that both ligand density and hydrophilicity were critical for optimal performance of the adsorbents. Adsorbents synthesized in this study showed a relatively high performance (141 179 mg/g at 49 62 % adsorption) in laboratory screening tests using a uranium concentration of ~6 ppm. This performance is much higher than that of known commercial adsorbents. However, actual seawater experiment showed impeded performance compared to the recently reported high-surface-area-fiber adsorbents, due to slow adsorption kinetics. The impeded performance motivated an investigation of the effect of hydrophilic block addition on the graft chain terminus. The addition of hydrophilic block on the graft chain terminus nearly doubled the uranium adsorption capacity in seawater, from 1.56 mg/g to 3.02 mg/g. The investigation revealed the importance of polymer chain conformation, in addition to ligand and hydrophilic group ratio, for advanced adsorbent synthesis for uranium recovery from seawater.

  16. Carbon fiber composite molecular sieves

    SciTech Connect

    Burchell, T.D.; Rogers, M.R.

    1997-12-01

    Monolithic adsorbents based on isotropic pitch fibers have been developed jointly by ORNL and the University of Kentucky, Center for Applied Energy Research. The monoliths are attractive for gas separation and storage applications because of their unique combination of physical properties and microporous structure. Currently at ORNL the monoliths are produced in billets that are 10 cm in diameter and 25 cm in length. The monolithic adsorbent material is being considered for guard bed applications on a natural gas (NG) powered device. In order for the material to be successful in this application, one must attain a uniform activation to modest micropore volumes throughout the large monoliths currently being produced. Here the authors report the results of a study directed toward attaining uniform activation in these billets.

  17. Compressive strength of carbon fibers

    SciTech Connect

    Prandy, J.M. ); Hahn, H.T. )

    1991-01-01

    Most composites are weaker in compression than in tension, which is due to the poor compressive strength of the load bearing fibers. The present paper discusses the compressive strengths and failure modes of 11 different carbon fibers: PAN-AS1, AS4, IM6, IM7, T700, T300, GY-30, pitch-75, ultra high modulus (UHM), high modulus (HM), and high strength (HS). The compressive strength was determined by embedding a fiber bundle in a transparent epoxy matrix and testing in compression. The resin allows for the containment and observation of failure during and after testing while also providing lateral support to the fibers. Scanning electron microscopy (SEM) was used to determine the global failure modes of the fibers.

  18. Interfacial adhesion of carbon fibers

    NASA Technical Reports Server (NTRS)

    Bascom, Willard D.

    1987-01-01

    Relative adhesion strengths between AS4, AS1, and XAS carbon fibers and thermoplastic polymers were determined using the embedded single filament test. Polymers studied included polycarbonate, polyphenylene oxide, polyetherimide, polysulfone, polyphenylene oxide blends with polystyrene, and polycarbonate blends with a polycarbonate polysiloxane block copolymer. Fiber surface treatments and sizings improved adhesion somewhat, but adhesion remained well below levels obtained with epoxy matrices. An explanation for the differences between the Hercules and Grafil fibers was sought using X ray photon spectroscopy, wetting, scanning electron microscopy and thermal desorption analysis.

  19. Nanoporous-carbon adsorbers for chemical microsensors.

    SciTech Connect

    Overmyer, Donald L.; Siegal, Michael P.; Staton, Alan W.; Provencio, Paula Polyak; Yelton, William Graham

    2004-11-01

    Chemical microsensors rely on partitioning of airborne chemicals into films to collect and measure trace quantities of hazardous vapors. Polymer sensor coatings used today are typically slow to respond and difficult to apply reproducibly. The objective of this project was to produce a durable sensor coating material based on graphitic nanoporous-carbon (NPC), a new material first studied at Sandia, for collection and detection of volatile organic compounds (VOC), toxic industrial chemicals (TIC), chemical warfare agents (CWA) and nuclear processing precursors (NPP). Preliminary studies using NPC films on exploratory surface-acoustic-wave (SAW) devices and as a {micro}ChemLab membrane preconcentrator suggested that NPC may outperform existing, irreproducible coatings for SAW sensor and {micro}ChemLab preconcentrator applications. Success of this project will provide a strategic advantage to the development of a robust, manufacturable, highly-sensitive chemical microsensor for public health, industrial, and national security needs. We use pulsed-laser deposition to grow NPC films at room-temperature with negligible residual stress, and hence, can be deposited onto nearly any substrate material to any thickness. Controlled deposition yields reproducible NPC density, morphology, and porosity, without any discernable variation in surface chemistry. NPC coatings > 20 {micro}m thick with density < 5% that of graphite have been demonstrated. NPC can be 'doped' with nearly any metal during growth to provide further enhancements in analyte detection and selectivity. Optimized NPC-coated SAW devices were compared directly to commonly-used polymer coated SAWs for sensitivity to a variety of VOC, TIC, CWA and NPP. In every analyte, NPC outperforms each polymer coating by multiple orders-of-magnitude in detection sensitivity, with improvements ranging from 103 to 108 times greater detection sensitivity! NPC-coated SAW sensors appear capable of detecting most analytes tested to

  20. Thermoplastic coating of carbon fibers

    NASA Technical Reports Server (NTRS)

    Edie, D. D.; Lickfield, G. C.; Allen, L. E.; Mccollum, J. R.

    1989-01-01

    A continuous powder coating system was developed for coating carbon fiber with LaRC-TPI (Langley Research Center-Thermoplastic Polyimide), a high-temperature thermoplastic polymide invented by NASA-Langley. The coating line developed used a pneumatic fiber spreader to separate the individual fibers. The polymer was applied within a recirculating powder coating chamber then melted using a combination of direct electrical resistance and convective heating to make it adhere to the fiber tow. The tension and speed of the line were controlled with a dancer arm and an electrically driven fiber wind-up and wind-off. The effects of heating during the coating process on the flexibility of the prepreg produced were investigated. The uniformity with which the fiber tow could be coated with polymer also was examined. Composite specimens were fabricated from the prepreg and tested to determine optimum process conditions. The study showed that a very uniform and flexible prepeg with up to 50 percent by volume polymer could be produced with this powder coating system. The coating line minimized powder loss and produced prepeg in lengths of up to 300 m. The fiber spreading was found to have a major effect on the coating uniformity and flexibility. Though test results showed low composite tensile strengths, analysis of fracture surfaces under scanning electron microscope indicated that fiber/matrix adhesion was adequate.

  1. Use of Carbon Fiber Composite Molecular Sieves for Air Separation

    SciTech Connect

    Baker, Frederick S; Contescu, Cristian I; Gallego, Nidia C; Burchell, Timothy D

    2005-09-01

    A novel adsorbent material, 'carbon fiber composite molecular sieve' (CFCMS), has been developed by the Oak Ridge National Laboratory. Its features include high surface area, large pore volume, and a rigid, permeable carbon structure that exhibits significant electrical conductivity. The unique combination of high adsorptive capacity, permeability, good mechanical properties, and electrical conductivity represents an enabling technology for the development of novel gas separation and purification systems. In this context, it is proposed that a fast-cycle air separation process that exploits a kinetic separation of oxygen and nitrogen should be possible using a CFCMS material coupled with electrical swing adsorption (ESA). The adsorption of O{sub 2}, N{sub 2}, and CO{sub 2} on activated carbon fibers was investigated using static and dynamic techniques. Molecular sieving effects in the activated carbon fiber were highlighted by the adsorption of CO{sub 2}, a more sensitive probe molecule for the presence of microporosity in adsorbents. The kinetic studies revealed that O2 was more rapidly adsorbed on the carbon fiber than N{sub 2}, and with higher uptake under equilibrium conditions, providing the fiber contained a high proportion of very narrow micropores. The work indicated that CFCMS is capable of separating O{sub 2} and N{sub 2} from air on the basis of the different diffusion rates of the two molecules in the micropore network of the activated carbon fibers comprising the composite material. In response to recent enquires from several potential users of CFCMS materials, attention has been given to the development of a viable continuous process for the commercial production of CFCMS material. As part of this effort, work was implemented on characterizing the performance of lignin-based activated carbon fiber, a potentially lower cost fiber than the pitch-based fibers used for CFCMS production to date. Similarly, to address engineering issues, measurements were

  2. Surface properties of mesoporous carbon-silica gel adsorbents

    SciTech Connect

    Leboda, R.; Turov, V.V.; Charmas, B.; Skubiszewska-Zieba, J.; Gun'ko, V.M.

    2000-03-01

    Carbon/silica (carbosil) samples prepared utilizing mesoporous silica gel (Si-60) modified by methylene chloride pyrolysis were studied by nitrogen adsorption, quasi-isothermal thermogravimetry, p-nitrophenol adsorption from aqueous solution, and {sup 1}H NMR methods. The structural characteristics and other properties of carbosils depend markedly on the synthetic conditions and the amount of carbon deposited. The changes in the pore size distribution with increasing carbon concentration suggest grafting of carbon mainly in pores, leading to diminution of the mesopore radii. However, heating pure silica gel at the pyrolysis temperature of 550 C leads to an increase in the pore radii. The quasi-isothermal thermogravimetry and {sup 1}H NMR spectroscopy methods used to investigate the water layers on carbosils showed a significant capability of carbosils to adsorb water despite a relatively large content of the hydrophobic carbon deposit, which represents a nonuniform layer incompletely covering the oxide surface.

  3. Assessment of Carbon Fiber Electrical Effects

    NASA Technical Reports Server (NTRS)

    1980-01-01

    The risks associated with the use of carbon fiber composites in civil aircraft are discussed along with the need for protection of civil aircraft equipment from fire-released carbon fibers. The size and number of carbon fibers released in civil aircraft crash fires, the downwind dissemination of the fibers, their penetration into buildings and equipment, and the vulnerability of electrical/electronic equipment to damage by the fibers are assessed.

  4. Carbon fiber study

    NASA Technical Reports Server (NTRS)

    1977-01-01

    A coordinated Federal Government action plan for dealing with the potential problems arising from the increasing use of graphite fiber reinforced composite materials in both military and civilian applications is presented. The required dissemination of declassified information and an outline of government actions to minimize the social and economic consequences of proliferated composite materials applications were included.

  5. Development Trends in Porous Adsorbents for Carbon Capture.

    PubMed

    Sreenivasulu, Bolisetty; Sreedhar, Inkollu; Suresh, Pathi; Raghavan, Kondapuram Vijaya

    2015-11-01

    Accumulation of greenhouse gases especially CO2 in the atmosphere leading to global warming with undesirable climate changes has been a serious global concern. Major power generation in the world is from coal based power plants. Carbon capture through pre- and post- combustion technologies with various technical options like adsorption, absorption, membrane separations, and chemical looping combustion with and without oxygen uncoupling have received considerable attention of researchers, environmentalists and the stake holders. Carbon capture from flue gases can be achieved with micro and meso porous adsorbents. This review covers carbonaceous (organic and metal organic frameworks) and noncarbonaceous (inorganic) porous adsorbents for CO2 adsorption at different process conditions and pore sizes. Focus is also given to noncarbonaceous micro and meso porous adsorbents in chemical looping combustion involving insitu CO2 capture at high temperature (>400 °C). Adsorption mechanisms, material characteristics, and synthesis methods are discussed. Attention is given to isosteric heats and characterization techniques. The options to enhance the techno-economic viability of carbon capture techniques by integrating with CO2 utilization to produce industrially important chemicals like ammonia and urea are analyzed. From the reader's perspective, for different classes of materials, each section has been summarized in the form of tables or figures to get a quick glance of the developments.

  6. Sustainable catalyst supports for carbon dioxide gas adsorbent

    NASA Astrophysics Data System (ADS)

    Mazlee, M. N.

    2016-07-01

    The adsorption of carbon dioxide (CO2) become the prime attention nowadays due to the fact that increasing CO2 emissions has been identified as a contributor to global climate change. Major sources of CO2 emissions are thermoelectric power plants and industrial plants which account for approximately 45% of global CO2 emissions. Therefore, it is an urgent need to develop an efficient CO2 reduction technology such as carbon capture and storage (CCS) that can reduce CO2 emissions particularly from the energy sector. A lot of sustainable catalyst supports have been developed particularly for CO2 gas adsorbent applications.

  7. Characterization of carbon cryogel microspheres as adsorbents for VOC.

    PubMed

    Yamamoto, Takuji; Kataoka, Sho; Ohmori, Takao

    2010-05-15

    Adsorption characteristics of carbon cryogel microspheres (CC microspheres) with controlled porous structure composed of mesopores (2 nmadsorbents for a volatile organic compound (VOC). The amount of toluene, as a model VOC, adsorbed on the CC microspheres could be changed by varying either the size of the mesopores or the volume of the micropores. The peak temperature of the temperature-programmed desorption profiles of toluene from the CC microspheres was higher than that from granular activated carbon (GAC) with numerous micropores, indicating that toluene is adsorbed more strongly on CC microspheres than on GAC. To permit the practical use of CC microspheres, the adsorption characteristic of moisture on CC microspheres and GAC were evaluated. The effect of adsorption of moisture on the gas permeation property of an adsorption module prepared from the CC microspheres was also examined. PMID:20042276

  8. Least cost process design for granular activated carbon adsorbers

    SciTech Connect

    Narbaitz, R.M.; Benedek, A.

    1983-10-01

    Although toxic organics may be removed from industrial effluents by activated carbon adsorbers, the cost of this process is relatively high. Also, adsorber design is complex because of the unsteady-state nature of the process and the numerous operational variables. A package of computer programs has been developed to help to minimise the ultimate cost of 4 types of column configurations. It determines the effect of treatment facility costs of different values for design and operational variables, such as empty bed contact time (EBCT), hydraulic loading, and column configurations. The results of a sample problem indicated that the optimum EBCT for all the column configurations was significantly higher than values typically used by designers.

  9. Thermoplastic-carbon fiber hybrid yarn

    NASA Technical Reports Server (NTRS)

    Ketterer, M. E.

    1984-01-01

    Efforts were directed to develop processing methods to make carbon fiber/thermoplastic fiber preforms that are easy to handle and drapeable, and to consolidate them into low void content laminates. The objectives were attained with the development of the hybrid yarn concept; whereby, thermoplastic fiber can be intimately intermixed with carbon fiber into a hybrid yarn. This was demonstrated with the intermixing of Celion 3000 with a Celanese liquid crystal polymer fiber, polybutylene terepthalate fiber, or polyetheretherketone fiber. The intermixing of the thermoplastic matrix fiber and the reinforcing carbon fiber gives a preform that can be easily fabricated into laminates with low void content. Mechanical properties of the laminates were not optimized; however, initial results indicated properties typical of a thermoplastic/carbon fiber composites prepared by more conventional methods.

  10. Aminosilane-grafted polymer/silica hollow fiber adsorbents for CO₂ capture from flue gas.

    PubMed

    Rezaei, Fateme; Lively, Ryan P; Labreche, Ying; Chen, Grace; Fan, Yanfang; Koros, William J; Jones, Christopher W

    2013-05-01

    Amine/silica/polymer composite hollow fiber adsorbents are produced using a novel reactive post-spinning infusion technique, and the obtained fibers are shown to capture CO2 from simulated flue gas. The post-spinning infusion technique allows for functionalization of polymer/silica hollow fibers with different types of amines during the solvent exchange step after fiber spinning. The post-spinning infusion of 3-aminopropyltrimethoxysilane (APS) into mesoporous silica/cellulose acetate hollow fibers is demonstrated here, and the materials are compared with hollow fibers infused with poly(ethyleneimine) (PEI). This approach results in silica/polymer composite fibers with good amine distribution and accessibility, as well as adequate porosity retained within the fibers to facilitate rapid mass transfer and adsorption kinetics. The CO2 adsorption capacities for the APS-infused hollow fibers are shown to be comparable to those of amine powders with similar amine loadings. In contrast, fibers that are spun with presynthesized, amine-loaded mesoporous silica powders show negligible CO2 uptake and low amine loadings because of loss of amines from the silica materials during the fiber spinning process. Aminosilica powders are shown to be more hydrophilic than the corresponding amine containing composite hollow fibers, the bare polymer as well as silica support. Both the PEI-infused and APS-infused fibers demonstrate reduced CO2 adsorption upon elevating the temperature from 35 to 80 °C, in accordance with thermodynamics, whereas PEI-infused powders show increased CO2 uptake over that temperature range because of competing diffusional and thermodynamic effects. The CO2 adsorption kinetics as probed via TGA show that the APS-infused hollow fiber adsorbents have more rapid uptake kinetics than their aminosilica powder analogues. The adsorption performance of the functionalized hollow fibers is also assessed in CO2 breakthrough experiments. The breakthrough results show a

  11. Carbon fiber internal pressure vessels

    NASA Technical Reports Server (NTRS)

    Simon, R. A.

    1973-01-01

    Internal pressure vessels were designed; the filament was wound of carbon fibers and epoxy resin and tested to burst. The fibers used were Thornel 400, Thornel 75, and Hercules HTS. Additional vessels with type A fiber were made. Polymeric linears were used, and all burst testing was done at room temperature. The objective was to produce vessels with the highest attainable PbV/W efficiencies. The type A vessels showed the highest average efficiency: 2.56 x 10 to the 6th power cm. Next highest efficiency was with Thornel 400 vessels: 2.21 x 10 to the 6th power cm. These values compare favorably with efficiency values from good quality S-glass vessels, but strains averaged 0.97% or less, which is less than 1/3 the strain of S-glass vessels.

  12. Carbon nanotube fiber spun from wetted ribbon

    SciTech Connect

    Zhu, Yuntian T; Arendt, Paul; Zhang, Xiefei; Li, Qingwen; Fu, Lei; Zheng, Lianxi

    2014-04-29

    A fiber of carbon nanotubes was prepared by a wet-spinning method involving drawing carbon nanotubes away from a substantially aligned, supported array of carbon nanotubes to form a ribbon, wetting the ribbon with a liquid, and spinning a fiber from the wetted ribbon. The liquid can be a polymer solution and after forming the fiber, the polymer can be cured. The resulting fiber has a higher tensile strength and higher conductivity compared to dry-spun fibers and to wet-spun fibers prepared by other methods.

  13. Activity of catalase adsorbed to carbon nanotubes: effects of carbon nanotube surface properties.

    PubMed

    Zhang, Chengdong; Luo, Shuiming; Chen, Wei

    2013-09-15

    Nanomaterials have been studied widely as the supporting materials for enzyme immobilization. However, the interactions between enzymes and carbon nanotubes (CNT) with different morphologies and surface functionalities may vary, hence influencing activities of the immobilized enzyme. To date how the adsorption mechanisms affect the activities of immobilized enzyme is not well understood. In this study the adsorption of catalase (CAT) on pristine single-walled carbon nanotubes (SWNT), oxidized single-walled carbon nanotubes (O-SWNT), and multi-walled carbon nanotubes (MWNT) was investigated. The adsorbed enzyme activities decreased in the order of O-SWNT>SWNT>MWNT. Fourier transforms infrared spectroscopy (FTIR) and circular dichrois (CD) analyses reveal more significant loss of α-helix and β-sheet of MWNT-adsorbed than SWNT-adsorbed CAT. The difference in enzyme activities between MWNT-adsorbed and SWNT-adsorbed CAT indicates that the curvature of surface plays an important role in the activity of immobilized enzyme. Interestingly, an increase of β-sheet content was observed for CAT adsorbed to O-SWNT. This is likely because as opposed to SWNT and MWNT, O-SWNT binds CAT largely via hydrogen bonding and such interaction allows the CAT molecule to maintain the rigidity of enzyme structure and thus the biological function.

  14. Carbon fibers from SRC pitch

    DOEpatents

    Greskovich, Eugene J.; Givens, Edwin N.

    1981-01-01

    This invention relates to an improved method of manufacturing carbon fibers from a coal derived pitch. The improvement resides in the use of a solvent refined coal which has been hydrotreated and subjected to solvent extraction whereby the hetero atom content in the resulting product is less than 4.0% by weight and the softening point is between about 100.degree.-250.degree. F.

  15. Storing Fluorine In Graphitelike Carbon Fibers

    NASA Technical Reports Server (NTRS)

    Hung, Ching-Cheh

    1995-01-01

    Fluorine stored in graphite or graphitelike carbon fibers for later release and/or use in chemical reactions. Storage in carbon fibers eliminates difficulty and risk of using high-pressure tanks and pipes to hold corrosive gas. Storage in carbon fibers makes fluorine more readily accessible than does storage as constituent of metal fluoride. Carbon fibers heated to release stored fluorine, which draws away to vessel where reacts with material to be fluorinated, possibly at temperature other than release temperature. Alternatively, material to be fluorinated mixed or otherwise placed in contact with fibers and entire mass heated to or beyond release temperature.

  16. Interfacial Studies of Sized Carbon Fiber

    SciTech Connect

    Shahrul, S. N.; Hartini, M. N.; Hilmi, E. A.; Nizam, A.

    2010-03-11

    This study was performed to investigate the influence of sizing treatment on carbon fiber in respect of interfacial adhesion in composite materials, Epolam registered 2025. Fortafil unsized carbon fiber was used to performed the experiment. The fiber was commercially surface treated and it was a polyacrylonitrile based carbon fiber with 3000 filament per strand. Epicure registered 3370 was used as basic sizing chemical and dissolved in two types of solvent, ethanol and acetone for the comparison purpose. The single pull out test has been used to determine the influence of sizing on carbon fiber. The morphology of carbon fiber was observed by atomic force microscopy (AFM) and scanning electron microscopy (SEM). The apparent interfacial strength IFSS values determined by pull out test for the Epicure registered 3370/ethanol sized carbon fiber pointed to a good interfacial behaviour compared to the Epicure registered 3370/acetone sized carbon fiber. The Epicure registered 3370/ethanol sizing agent was found to be effective in promoting adhesion because of the chemical reactions between the sizing and Epolam registered 2025 during the curing process. From this work, it showed that sized carbon fiber using Epicure registered 3370 with addition of ethanol give higher mechanical properties of carbon fiber in terms of shear strength and also provided a good adhesion between fiber and matrix compared to the sizing chemical that contain acetone as a solvent.

  17. Interfacial Studies of Sized Carbon Fiber

    NASA Astrophysics Data System (ADS)

    Shahrul, S. N.; Hartini, M. N.; Hilmi, E. A.; Nizam, A.

    2010-03-01

    This study was performed to investigate the influence of sizing treatment on carbon fiber in respect of interfacial adhesion in composite materials, Epolam® 2025. Fortafil unsized carbon fiber was used to performed the experiment. The fiber was commercially surface treated and it was a polyacrylonitrile based carbon fiber with 3000 filament per strand. Epicure® 3370 was used as basic sizing chemical and dissolved in two types of solvent, ethanol and acetone for the comparison purpose. The single pull out test has been used to determine the influence of sizing on carbon fiber. The morphology of carbon fiber was observed by atomic force microscopy (AFM) and scanning electron microscopy (SEM). The apparent interfacial strength IFSS values determined by pull out test for the Epicure® 3370/ethanol sized carbon fiber pointed to a good interfacial behaviour compared to the Epicure® 3370/acetone sized carbon fiber. The Epicure® 3370/ethanol sizing agent was found to be effective in promoting adhesion because of the chemical reactions between the sizing and Epolam® 2025 during the curing process. From this work, it showed that sized carbon fiber using Epicure® 3370 with addition of ethanol give higher mechanical properties of carbon fiber in terms of shear strength and also provided a good adhesion between fiber and matrix compared to the sizing chemical that contain acetone as a solvent.

  18. Carbon fiber manufacturing via plasma technology

    DOEpatents

    Paulauskas, Felix L.; Yarborough, Kenneth D.; Meek, Thomas T.

    2002-01-01

    The disclosed invention introduces a novel method of manufacturing carbon and/or graphite fibers that avoids the high costs associated with conventional carbonization processes. The method of the present invention avoids these costs by utilizing plasma technology in connection with electromagnetic radiation to produce carbon and/or graphite fibers from fully or partially stabilized carbon fiber precursors. In general, the stabilized or partially stabilized carbon fiber precursors are placed under slight tension, in an oxygen-free atmosphere, and carbonized using a plasma and electromagnetic radiation having a power input which is increased as the fibers become more carbonized and progress towards a final carbon or graphite product. In an additional step, the final carbon or graphite product may be surface treated with an oxygen-plasma treatment to enhance adhesion to matrix materials.

  19. High voltage spark carbon fiber detection system

    NASA Technical Reports Server (NTRS)

    Yang, L. C.

    1980-01-01

    The pulse discharge technique was used to determine the length and density of carbon fibers released from fiber composite materials during a fire or aircraft accident. Specifications are given for the system which uses the ability of a carbon fiber to initiate spark discharge across a high voltage biased grid to achieve accurate counting and sizing of fibers. The design of the system was optimized, and prototype hardware proved satisfactory in laboratory and field tests.

  20. Characteristics of activated carbon and carbon nanotubes as adsorbents to remove annatto (norbixin) in cheese whey.

    PubMed

    Zhang, Yue; Pan, Kang; Zhong, Qixin

    2013-09-25

    Removing annatto from cheese whey without bleaching has potential to improve whey protein quality. In this work, the potential of two activated carbon products and multiwalled carbon nanotubes (CNT) was studied for extracting annatto (norbixin) in aqueous solutions. Batch adsorption experiments were studied for the effects of solution pH, adsorbent mass, contact duration, and ionic strength. The equilibrium adsorption data were observed to fit both Langmuir and Freundlich isotherm models. The thermodynamic parameters estimated from adsorption isotherms demonstrated that the adsorption of norbixin on three adsorbents is exothermic, and the entropic contribution differs with adsorbent structure. The adsorption kinetics, with CNT showing a higher rate than activated carbon, followed the pseudo first order and second order rate expressions and demonstrated the significance of intraparticle diffusion. Electrostatic interactions were observed to be significant in the adsorption. The established adsorption parameters may be used in the dairy industry to decolorize cheese whey without applying bleaching agents.

  1. Characterization of porous carbon fibers and related materials

    SciTech Connect

    Fuller, E.L. Jr.

    1996-07-15

    This program was geared to support the Fossil Energy Material Sciences Program with respect to several areas of interest in efficient production and utilization of energy. Carbon molecular sieves have great potential for economically purifying gases; i.e. removal of carbon dioxide from natural gas without having to resort to cryogenic techniques. Microporous carbons can be tailored to serve as adsorbents for natural gas in on-board storage in automotive applications, avoiding high pressures and heavy storage tanks. This program is a laboratory study to evaluate production methodologies and activation processes to produce porous carbons for specific applications. The Carbon Materials Technology Group of Oak Ridge National Laboratory (ORNL) is engaged in developmental programs to produce activated carbon fibers (ACF) for applications in fixed beds and/or flowing reactors engineering applications.

  2. Laser Processing of Carbon Fiber Reinforced Plastics - Release of Carbon Fiber Segments During Short-pulsed Laser Processing of CFRP

    NASA Astrophysics Data System (ADS)

    Walter, Juergen; Brodesser, Alexander; Hustedt, Michael; Bluemel, Sven; Jaeschke, Peter; Kaierle, Stefan

    Cutting and ablation using short-pulsed laser radiation are promising technologies to produce or repair CFRP components with outstanding mechanical properties e.g. for automotive and aircraft industry. Using sophisticated laser processing strategies and avoiding excessive heating of the workpiece, a high processing quality can be achieved. However, the interaction of laser radiation and composite material causes a notable release of hazardous substances from the process zone, amongst others carbon fiber segments or fibrous particles. In this work, amounts and geometries of the released fiber segments are analyzed and discussed in terms of their hazardous potential. Moreover, it is investigated to what extent gaseous organic process emissions are adsorbed at the fiber segments, similar to an adsorption of volatile organic compounds at activated carbon, which is typically used as filter material.

  3. Effects of heat treatment on carbon fibers

    NASA Technical Reports Server (NTRS)

    Brown, D. Kyle; Phillips, Wayne M.

    1990-01-01

    Commercially produced carbon fibers were heat treated to graphitization temperatures. The fibers were characterized for mechanical and physical properties, including density, D0002 spacing, strength, and modulus in both the 'as received' and heat treated conditions. Mechanical property changes were correlated with the physical property changes in the fibers.

  4. Photoconductivity of Activated Carbon Fibers

    DOE R&D Accomplishments Database

    Kuriyama, K.; Dresselhaus, M. S.

    1990-08-01

    The photoconductivity is measured on a high-surface-area disordered carbon material, namely activated carbon fibers, to investigate their electronic properties. Measurements of decay time, recombination kinetics and temperature dependence of the photoconductivity generally reflect the electronic properties of a material. The material studied in this paper is a highly disordered carbon derived from a phenolic precursor, having a huge specific surface area of 1000--2000m{sup 2}/g. Our preliminary thermopower measurements suggest that this carbon material is a p-type semiconductor with an amorphous-like microstructure. The intrinsic electrical conductivity, on the order of 20S/cm at room temperature, increases with increasing temperature in the range 30--290K. In contrast with the intrinsic conductivity, the photoconductivity in vacuum decreases with increasing temperature. The recombination kinetics changes from a monomolecular process at room temperature to a biomolecular process at low temperatures. The observed decay time of the photoconductivity is {approx equal}0.3sec. The magnitude of the photoconductive signal was reduced by a factor of ten when the sample was exposed to air. The intrinsic carrier density and the activation energy for conduction are estimated to be {approx equal}10{sup 21}/cm{sup 3} and {approx equal}20meV, respectively. The majority of the induced photocarriers and of the intrinsic carriers are trapped, resulting in the long decay time of the photoconductivity and the positive temperature dependence of the conductivity.

  5. High performance pitch-based carbon fiber

    SciTech Connect

    Tadokoro, Hiroyuki; Tsuji, Nobuyuki; Shibata, Hirotaka; Furuyama, Masatoshi

    1996-12-31

    The high performance pitch-based carbon fiber with smaller diameter, six micro in developed by Nippon Graphite Fiber Corporation. This fiber possesses high tensile modulus, high tensile strength, excellent yarn handle ability, low thermal expansion coefficient, and high thermal conductivity which make it an ideal material for space applications such as artificial satellites. Performance of this fiber as a reinforcement of composites was sufficient. With these characteristics, this pitch-based carbon fiber is expected to find wide variety of possible applications in space structures, industrial field, sporting goods and civil infrastructures.

  6. The transport properties of activated carbon fibers

    SciTech Connect

    di Vittorio, S.L. . Dept. of Materials Science and Engineering); Dresselhaus, M.S. . Dept. of Electrical Engineering and Computer Science Massachusetts Inst. of Tech., Cambridge, MA . Dept. of Physics); Endo, M. . Dept. of Electrical Engineering); Issi, J-P.; Piraux, L.

    1990-07-01

    The transport properties of activated isotropic pitch-based carbon fibers with surface area 1000 m{sup 2}/g have been investigated. We report preliminary results on the electrical conductivity, the magnetoresistance, the thermal conductivity and the thermopower of these fibers as a function of temperature. Comparisons are made to transport properties of other disordered carbons. 19 refs., 4 figs.

  7. The Transport Properties of Activated Carbon Fibers

    DOE R&D Accomplishments Database

    di Vittorio, S. L.; Dresselhaus, M. S.; Endo, M.; Issi, J-P.; Piraux, L.

    1990-07-01

    The transport properties of activated isotropic pitch-based carbon fibers with surface area 1000 m{sup 2}/g have been investigated. We report preliminary results on the electrical conductivity, the magnetoresistance, the thermal conductivity and the thermopower of these fibers as a function of temperature. Comparisons are made to transport properties of other disordered carbons.

  8. Carbon fiber behavior in an enclosed volume

    NASA Technical Reports Server (NTRS)

    Harvey, M. C.

    1979-01-01

    Tests were performed to evaluate the behavior of single carbon fibers existing in an enclosed space such as a room of a building. Three general phenomena were explored: the concentration decay rate of a fiber-charged room, the degree of uniform mixing of fibers within a room, and the effects of fibers being redisseminated off deposition surfaces within a room. The results were required in understanding the ratio of total indoor fiber exposure to total outdoor fiber exposure, a quantity essential to risk analysis. Results indicate that decay rate is predictable within acceptable limits and that homogeneous mixing can always be assumed. Some factors of redissemination are identified and effects discussed.

  9. Thermal behaviour of arsenic trioxide adsorbed on activated carbon.

    PubMed

    Cuypers, Frederic; De Dobbelaere, Christopher; Hardy, An; Van Bael, Marlies K; Helsen, Lieve

    2009-07-30

    The thermal stability and desorption of arsenic trioxide (As(2)O(3)) adsorbed on activated carbon (AC) was investigated as this phenomenon is expected to influence the arsenic release during low temperature pyrolysis of chromated copper arsenate (CCA) wood waste. Firstly, a thermogravimetric (TG) experiment with arsenolite, an allotropic form of As(2)O(3), was performed. The sample starts to sublime at temperatures lower than 200 degrees C with a sublimation peak temperature of 271 degrees C. Subsequently, TG experiments with samples of As(2)O(3) adsorbed on AC revealed that only very little (max. 6+/-3 wt%) As(2)O(3) was volatilized at temperatures below 280 degrees C, while still 41.6 (+/-5)wt% of the original arsenic concentration was retained at 440 degrees C and 28.5 (+/-3)wt% at 600 degrees C. The major arsenic volatilization occurred between 300 degrees C and 500 degrees C. The kinetic parameters of desorption, activation energy of desorption (E(d)) and pre-exponential factor (A), were determined by fitting an Arrhenius model to the experimental data, resulting in E(d)=69 kJ/mol, A=1.21 x 10(4)s(-1). It can be concluded that the adsorption of As(2)O(3) on AC can contribute to the thermal stabilisation of As(2)O(3). Consequently, during low temperature pyrolysis of CCA wood arsenic release may be prevented by adsorption of As(2)O(3) on the coal-type product formed during the thermal decomposition of the wood. PMID:19136209

  10. Characterization of electrospun lignin based carbon fibers

    NASA Astrophysics Data System (ADS)

    Poursorkhabi, Vida; Mohanty, Amar; Misra, Manjusri

    2015-05-01

    The production of lignin fibers has been studied in order to replace the need for petroleum based precursors for carbon fiber production. In addition to its positive environmental effects, it also benefits the economics of the industries which cannot take advantage of carbon fiber properties because of their high price. A large amount of lignin is annually produced as the byproduct of paper and growing cellulosic ethanol industry. Therefore, finding high value applications for this low cost, highly available material is getting more attention. Lignin is a biopolymer making about 15 - 30 % of the plant cell walls and has a high carbon yield upon carbonization. However, its processing is challenging due to its low molecular weight and also variations based on its origin and the method of separation from cellulose. In this study, alkali solutions of organosolv lignin with less than 1 wt/v% of poly (ethylene oxide) and two types of lignin (hardwood and softwood) were electrospun followed by carbonization. Different heating programs for carbonization were tested. The carbonized fibers had a smooth surface with an average diameter of less than 5 µm and the diameter could be controlled by the carbonization process and lignin type. Scanning electron microscopy (SEM) was used to study morphology of the fibers before and after carbonization. Thermal conductivity of a sample with amorphous carbon was 2.31 W/m.K. The electrospun lignin carbon fibers potentially have a large range of application such as in energy storage devices and water or gas purification systems.

  11. Surface analyses of carbon fibers produced from polyacrylonitrile fibers at low carbonization temperatures

    NASA Technical Reports Server (NTRS)

    Cagliostro, D. E.

    1983-01-01

    A process for producing carbon fibers from polyacrylonitrile at low carbonization temperatures was studied. The bulk and surface properties of fibers obtained after reaction with benzoic acid, air and carbonizing in nitrogen or a dilute acetylene atmosphere are discussed. All fiber products had different surface and internal compositions. Samples produced at temperatures up to 950 C and carbonized in nitrogen contained substantial quantities of nitrogen and oxygen at the surface. During carbonization, the surface nitrogen converted into two new forms, possibly nitrile and an azo or a new carbon-nitrogen bond. Samples carbonized in acetylene contained a carbon-rich surface stable to oxidation.

  12. Adsorption capacities of activated carbons for geosmin and 2-methylisoborneol vary with activated carbon particle size: Effects of adsorbent and adsorbate characteristics.

    PubMed

    Matsui, Yoshihiko; Nakao, Soichi; Sakamoto, Asuka; Taniguchi, Takuma; Pan, Long; Matsushita, Taku; Shirasaki, Nobutaka

    2015-11-15

    The adsorption capacities of nine activated carbons for geosmin and 2-methylisoborneol (MIB) were evaluated. For some carbons, adsorption capacity substantially increased when carbon particle diameter was decreased from a few tens of micrometers to a few micrometers, whereas for other carbons, the increase of adsorption capacity was small for MIB and moderate for geosmin. An increase of adsorption capacity was observed for other hydrophobic adsorbates besides geosmin and MIB, but not for hydrophilic adsorbates. The parameter values of a shell adsorption model describing the increase of adsorption capacity were negatively correlated with the oxygen content of the carbon among other characteristics. Low oxygen content indicated low hydrophilicity. The increase of adsorption capacity was related to the hydrophobic properties of both adsorbates and activated carbons. For adsorptive removal of hydrophobic micropollutants such as geosmin, it is therefore recommended that less-hydrophilic activated carbons, such as coconut-shell-based carbons, be microground to a particle diameter of a few micrometers to enhance their equilibrium adsorption capacity. In contrast, adsorption by hydrophilic carbons or adsorption of hydrophilic adsorbates occur in the inner pores, and therefore adsorption capacity is unchanged by particle size reduction. PMID:26302219

  13. Adsorption capacities of activated carbons for geosmin and 2-methylisoborneol vary with activated carbon particle size: Effects of adsorbent and adsorbate characteristics.

    PubMed

    Matsui, Yoshihiko; Nakao, Soichi; Sakamoto, Asuka; Taniguchi, Takuma; Pan, Long; Matsushita, Taku; Shirasaki, Nobutaka

    2015-11-15

    The adsorption capacities of nine activated carbons for geosmin and 2-methylisoborneol (MIB) were evaluated. For some carbons, adsorption capacity substantially increased when carbon particle diameter was decreased from a few tens of micrometers to a few micrometers, whereas for other carbons, the increase of adsorption capacity was small for MIB and moderate for geosmin. An increase of adsorption capacity was observed for other hydrophobic adsorbates besides geosmin and MIB, but not for hydrophilic adsorbates. The parameter values of a shell adsorption model describing the increase of adsorption capacity were negatively correlated with the oxygen content of the carbon among other characteristics. Low oxygen content indicated low hydrophilicity. The increase of adsorption capacity was related to the hydrophobic properties of both adsorbates and activated carbons. For adsorptive removal of hydrophobic micropollutants such as geosmin, it is therefore recommended that less-hydrophilic activated carbons, such as coconut-shell-based carbons, be microground to a particle diameter of a few micrometers to enhance their equilibrium adsorption capacity. In contrast, adsorption by hydrophilic carbons or adsorption of hydrophilic adsorbates occur in the inner pores, and therefore adsorption capacity is unchanged by particle size reduction.

  14. FIBER ORIENTATION IN INJECTION MOLDED LONG CARBON FIBER THERMOPLASTIC COMPOSITES

    SciTech Connect

    Wang, Jin; Nguyen, Ba Nghiep; Mathur, Raj N.; Sharma, Bhisham; Sangid, Michael D.; Costa, Franco; Jin, Xiaoshi; Tucker III, Charles L.; Fifield, Leonard S.

    2015-03-23

    A set of edge-gated and center-gated plaques were injection molded with long carbon fiber-reinforced thermoplastic composites, and the fiber orientation was measured at different locations of the plaques. Autodesk Simulation Moldflow Insight (ASMI) software was used to simulate the injection molding of these plaques and to predict the fiber orientation, using the anisotropic rotary diffusion and the reduced strain closure models. The phenomenological parameters of the orientation models were carefully identified by fitting to the measured orientation data. The fiber orientation predictions show very good agreement with the experimental data.

  15. Heat Treated Carbon Fiber Material Selection Database

    NASA Technical Reports Server (NTRS)

    Effinger, M.; Patel, B.; Koenig, J.

    2008-01-01

    Carbon fibers are used in a variety high temperature applications and materials. However, one limiting factor in their transition into additional applications is an understanding of their functional properties during component processing and function. The requirements on the fibers are governed by the nature of the materials and the environments in which they will be used. The current carbon fiber vendor literature is geared toward the polymeric composite industry and not the ceramic composite industry. Thus, selection of carbon fibers is difficult, since their properties change as a function of heat treatment, processing or component operational temperature, which ever is greatest. To enable proper decisions to be made, a program was established wherein multiple fibers were selected and heat treated at different temperatures. The fibers were then examined for their physical and mechanical properties which are reported herein.

  16. Wettability of a Single Carbon Fiber.

    PubMed

    Qiu, Si; Fuentes, Carlos A; Zhang, Dongxing; Van Vuure, Aart Willem; Seveno, David

    2016-09-27

    Wettability as determined from contact angle measurements is a suitable parameter for characterizing the physical bonding of a polymer matrix and reinforcing fibers, but it is very challenging to measure the capillary force exerted by a probe liquid on a fiber accurately for very fine fibers such as single carbon fibers. Herein, we propose an innovative method for measuring dynamic contact angles with a tensiometer, considering both the intrinsic variability of the carbon fiber diameter and the extremely small amplitude of the capillary forces, allowing the measurement of reliable dynamic contact angles over a large range of contact line velocities. The analysis of the contact angle dynamics by the molecular-kinetic theory permits us to check the relevancy of the measured contact angles and to obtain the static contact angle value, improving the prospect of employing tensiometry to better understand the wetting behavior of carbon fibers.

  17. Preparation and characterization of high capacity, strong cation-exchange fiber based adsorbents.

    PubMed

    Schwellenbach, Jan; Taft, Florian; Villain, Louis; Strube, Jochen

    2016-05-20

    Motivated by the demand for more economical capture and polishing steps in downstream processing of protein therapeutics, a novel strong cation-exchange chromatography stationary phase based on polyethylene terephthalate (PET) high surface area short-cut fibers is presented. The fiber surface is modified by grafting glycidyl methacrylate (GMA) via surface-initiated atom transfer radical polymerization (SI-ATRP) and a subsequent derivatization leading to sulfonic acid groups. The obtained cation-exchange fibers have been characterized and compared to commercially available resin and membrane based adsorbers. High volumetric static binding capacities for lysozyme (90mg/mL) and polyclonal human IgG (hIgG, 92mg/mL) were found, suggesting an efficient multi-layer binding within the grafted hydrogel layer. A packed bed of randomly orientated fibers has been tested for packing efficiency, permeability and chromatographic performance. High dynamic binding capacities for lysozyme (50mg/mL) and hIgG (54mg/mL) were found nearly independent of the bed-residence time, revealing a fast mass-transport mechanism. Height equivalent to a theoretical plate (HETP) values in the order of 0.1 cm and a peak asymmetry factor (AF) of 1.8 have been determined by tracer experiments. Additionally inverse size-exclusion chromatography (iSEC) revealed a bimodal structure within the fiber bed, consisting of larger transport channels, formed by the voidage between the fibers, and a hydrogel layer with porous properties. PMID:27106396

  18. Method of Manufacturing Carbon Fiber Reinforced Carbon Composite Valves

    NASA Technical Reports Server (NTRS)

    Rivers, H. Kevin (Inventor); Ransone, Philip O. (Inventor); Northam, G. Burton (Inventor)

    1998-01-01

    A method for forming a carbon composite valve for internal combustion engines is discussed. The process includes the steps of braiding carbon fiber into a rope thereby forming a cylindrically shaped valve stem portion and continuing to braid said fiber while introducing into the braiding carbon fiber rope a carbon matrix plug having an outer surface in a net shape of a valve head thereby forming a valve head portion. The said carbon matrix plug acting as a mandrel over which said carbon fiber rope is braided, said carbon fiber rope and carbon matrix plug forming a valve head portion suitable for mating with a valve seat; cutting said braided carbon valve stem portion at one end to form a valve tip and cutting said braided carbon fiber after said valve head portion to form a valve face and thus provide a composite valve preform; and densifying said preform by embedding the braided carbon in a matrix of carbon to convert said valve stem portion to a valve stem and said valve head portion to a valve head thereby providing said composite valve.

  19. High electrical resistivity carbon/graphite fibers

    NASA Technical Reports Server (NTRS)

    Vogel, F. L.; Forsman, W. C.

    1980-01-01

    Carbon/graphite fibers were chemically oxidized in the liquid phase to fibers of graphite oxide. Resistivity increases as high as 10,000 times were obtained, the oxidized fiber decomposed on exposure to atmosphere. A factor of 1,000 remained as a stable increment. The largest change observed was 1,000,000 times. Best results were obtained on the most highly graphitized fibers. Electrochemical oxidation yielded a lower increase--about 10 times, but provided a controllable method of synthesis and insight to the mechanism of reaction. Tensile tests indicated that the strength of the fiber on oxidation was decreased by no more than 25 percent.

  20. 40 CFR 65.152 - Carbon adsorbers used as control devices.

    Code of Federal Regulations, 2010 CFR

    2010-07-01

    ... cycle, and a carbon-bed temperature monitoring device capable of recording the carbon bed temperature... regeneration stream flow per regeneration cycle and the temperature of the carbon-bed determined within 15... 40 Protection of Environment 15 2010-07-01 2010-07-01 false Carbon adsorbers used as...

  1. 40 CFR 65.152 - Carbon adsorbers used as control devices.

    Code of Federal Regulations, 2011 CFR

    2011-07-01

    ... cycle, and a carbon-bed temperature monitoring device capable of recording the carbon bed temperature... regeneration stream flow per regeneration cycle and the temperature of the carbon-bed determined within 15... 40 Protection of Environment 15 2011-07-01 2011-07-01 false Carbon adsorbers used as...

  2. 40 CFR 65.152 - Carbon adsorbers used as control devices.

    Code of Federal Regulations, 2012 CFR

    2012-07-01

    ... cycle, and a carbon-bed temperature monitoring device capable of recording the carbon bed temperature... regeneration stream flow per regeneration cycle and the temperature of the carbon-bed determined within 15... 40 Protection of Environment 16 2012-07-01 2012-07-01 false Carbon adsorbers used as...

  3. 40 CFR 65.152 - Carbon adsorbers used as control devices.

    Code of Federal Regulations, 2013 CFR

    2013-07-01

    ... cycle, and a carbon-bed temperature monitoring device capable of recording the carbon bed temperature... regeneration stream flow per regeneration cycle and the temperature of the carbon-bed determined within 15... 40 Protection of Environment 16 2013-07-01 2013-07-01 false Carbon adsorbers used as...

  4. 40 CFR 65.152 - Carbon adsorbers used as control devices.

    Code of Federal Regulations, 2014 CFR

    2014-07-01

    ... cycle, and a carbon-bed temperature monitoring device capable of recording the carbon bed temperature... regeneration stream flow per regeneration cycle and the temperature of the carbon-bed determined within 15... 40 Protection of Environment 16 2014-07-01 2014-07-01 false Carbon adsorbers used as...

  5. Development of carbon dioxide adsorbent from rice husk char

    NASA Astrophysics Data System (ADS)

    Abang, S.; Janaun, J.; Anisuzzaman, S. M.; Ikhwan, F. S.

    2016-06-01

    This study was mainly concerned about the development of carbon dioxide (CO2) adsorbent from rice husk (RH). Several chemical treatments were used to produce activated rice husk char (RHAC) from RH. Initially the RH was refluxed with 3M of sodium hydroxide (NaOH) solution, activation followed by using 0.5M of zinc chloride (ZnCl2) solution and finally acidic treatment by using 0.1M of hydrochloric acid (HCl). Then, the RHAC was functionalized by using 3-chloropropylamine hydrochloride (3-CPA) and noted as RHN. RHN samples were characterized with scanning electron microscopy (SEM), mercury intrusion porosimetry (MIP), fourier transform infrared spectroscopy (FTIR). Based on the SEM, the RHN sample had a large pore diameter compared to RH sample after being treated. Based on MIP data, the average pore diameter between RH and RHAC samples were increased significantly from 0.928 microns to 1.017 microns. The RHN sample also had higher total porosity (%) compared to RHAC and RH (58.45%, 47.82% and 45.57% respectively). The total specific surface area of the sample was much increasing from RHO to RHAC (29.17 m2/g and 62.94 m2/g respectively) and slightly being decreasing from RHAC to RHN (58.88 m2/g). FTIR result showed the present of weak band at 1587 cm-1 which demonstrating of the amine group present on the sample. The CO2 capture result showed that the decreasing of operating temperature can increase the breakthrough time of CO2 capture. On the contrary decreasing of CO2 gas flow rate can increase the breakthrough time of CO2 capture. The highest total amount of CO2 adsorbed was 25338.57 mg of CO2/g of RHN sample by using 100 mL/min of gas flow rate at 30oC. Based on adsorption isotherm analysis, the Freundlich isotherm was the best isotherm to describe the CO2 adsorption on the sample.

  6. Large-scale carbon fiber tests

    NASA Technical Reports Server (NTRS)

    Pride, R. A.

    1980-01-01

    A realistic release of carbon fibers was established by burning a minimum of 45 kg of carbon fiber composite aircraft structural components in each of five large scale, outdoor aviation jet fuel fire tests. This release was quantified by several independent assessments with various instruments developed specifically for these tests. The most likely values for the mass of single carbon fibers released ranged from 0.2 percent of the initial mass of carbon fiber for the source tests (zero wind velocity) to a maximum of 0.6 percent of the initial carbon fiber mass for dissemination tests (5 to 6 m/s wind velocity). Mean fiber lengths for fibers greater than 1 mm in length ranged from 2.5 to 3.5 mm. Mean diameters ranged from 3.6 to 5.3 micrometers which was indicative of significant oxidation. Footprints of downwind dissemination of the fire released fibers were measured to 19.1 km from the fire.

  7. Carbon fiber content measurement in composite

    NASA Astrophysics Data System (ADS)

    Wang, Qiushi

    Carbon fiber reinforced polymers (CFRPs) have been widely used in various structural applications in industries such as aerospace and automotive because of their high specific stiffness and specific strength. Their mechanical properties are strongly influenced by the carbon fiber content in the composites. Measurement of the carbon fiber content in CFRPs is essential for product quality control and process optimization. In this work, a novel carbonization-in-nitrogen method (CIN) is developed to characterize the fiber content in carbon fiber reinforced thermoset and thermoplastic composites. In this method, a carbon fiber composite sample is carbonized in a nitrogen environment at elevated temperatures, alongside a neat resin sample. The carbon fibers are protected from oxidization while the resin (the neat resin and the resin matrix in the composite sample) is carbonized under the nitrogen environment. The residue of the carbonized neat resin sample is used to calibrate the resin carbonization rate and calculate the amount of the resin matrix in the composite sample. The new method has been validated on several thermoset and thermoplastic resin systems and found to yield an accurate measurement of fiber content in carbon fiber polymer composites. In order to further understand the thermal degradation behavior of the high temperature thermoplastic polymer during the carbonization process, the mechanism and the kinetic model of thermal degradation behavior of carbon fiber reinforced poly (phenylene sulfide) (CPPS) are studied using thermogravimetry analysis (TGA). The CPPS is subjected to TGA in an air and nitrogen atmosphere at heating rates from 5 to 40°C min--1. The TGA curves obtained in air are different from those in nitrogen. This demonstrates that weight loss occurs in a single stage in nitrogen but in two stages in air. To elucidate this difference, thermal decomposition kinetics is analyzed by applying the Kissinger, Flynn-Wall-Ozawa, Coat-Redfern and

  8. Adsorption and Desorption of Carbon Dioxide and Water Mixtures on Synthetic Hydrophobic Carbonaceous Adsorbents

    NASA Technical Reports Server (NTRS)

    Finn, John E.; Harper, Lynn D. (Technical Monitor)

    1994-01-01

    Several synthetic carbonaceous adsorbents produced through pyrolysis of polymeric materials are available commercially. Some appear to have advantages over activated carbon for certain adsorption applications. In particular, they can have tailored hydrophobicities that are significantly greater than that of activated carbon, while moderately high surfaces areas are retained. These sorbents are being investigated for possible use in removing trace contaminants and excess carbon dioxide from air in closed habitats, plant growth chambers, and other applications involving purification of humid gas streams. We have analyzed the characteristics of a few of these adsorbents through adsorption and desorption experiments and standard characterization techniques. This paper presents pure and multicomponent adsorption data collected for carbon dioxide and water on two synthetic carbonaceous adsorbents having different hydrophobicities and capillary condensation characteristics. The observations are interpreted through consideration of the pore structure and surface chemistry of the solids and interactions between adsorbed carbon dioxide, water, and the solvent gas.

  9. Carbon dioxide pressure swing adsorption process using modified alumina adsorbents

    DOEpatents

    Gaffney, T.R.; Golden, T.C.; Mayorga, S.G.; Brzozowski, J.R.; Taylor, F.W.

    1999-06-29

    A pressure swing adsorption process for absorbing CO[sub 2] from a gaseous mixture containing CO[sub 2] comprises introducing the gaseous mixture at a first pressure into a reactor containing a modified alumina adsorbent maintained at a temperature ranging from 100 C and 500 C to adsorb CO[sub 2] to provide a CO[sub 2] laden alumina adsorbent and a CO[sub 2] depleted gaseous mixture and contacting the CO[sub 2] laden adsorbent with a weakly adsorbing purge fluid at a second pressure which is lower than the first pressure to desorb CO[sub 2] from the CO[sub 2] laden alumina adsorbent. The modified alumina adsorbent which is formed by depositing a solution having a pH of 3.0 or more onto alumina and heating the alumina to a temperature ranging from 100 C and 600 C, is not degraded by high concentrations of water under process operating conditions. 1 fig.

  10. Carbon dioxide pressure swing adsorption process using modified alumina adsorbents

    DOEpatents

    Gaffney, Thomas Richard; Golden, Timothy Christopher; Mayorga, Steven Gerard; Brzozowski, Jeffrey Richard; Taylor, Fred William

    1999-01-01

    A pressure swing adsorption process for absorbing CO.sub.2 from a gaseous mixture containing CO.sub.2 comprising introducing the gaseous mixture at a first pressure into a reactor containing a modified alumina adsorbent maintained at a temperature ranging from 100.degree. C. and 500.degree. C. to adsorb CO.sub.2 to provide a CO.sub.2 laden alumina adsorbent and a CO.sub.2 depleted gaseous mixture and contacting the CO.sub.2 laden adsorbent with a weakly adsorbing purge fluid at a second pressure which is lower than the first pressure to desorb CO.sub.2 from the CO.sub.2 laden alumina adsorbent. The modified alumina adsorbent which is formed by depositing a solution having a pH of 3.0 or more onto alumina and heating the alumina to a temperature ranging from 100.degree. C. and 600.degree. C., is not degraded by high concentrations of water under process operating conditions.

  11. Risk analysis approach. [of carbon fiber release

    NASA Technical Reports Server (NTRS)

    Huston, R. J.

    1979-01-01

    The assessment of the carbon fiber hazard is outlined. Program objectives, requirements of the risk analysis, and elements associated with the physical phenomena of the accidental release are described.

  12. Properties and potential environmental applications of carbon adsorbents from waste tire rubber

    USGS Publications Warehouse

    Lehmann, C.M.B.; Rameriz, D.; Rood, M.J.; Rostam-Abadi, M.

    2000-01-01

    The properties of tire-derived carbon adsorbents (TDCA) produced from select tire chars were compared with those derived from an Illinois coal and pistachio nut shells. Chemical analyses of the TDCA indicated that these materials contain metallic elements not present in coal-and nut shell-derived carbons. These metals, introduced during the production of tire rubber, potentially catalyze steam gasification reactions of tire char. TDCA carbons contained larger meso-and macopore volumes than their counterparts derived from coal and nut shell (on the moisture-and ash-free-basis). Adsorptive properties of the tire-derived adsorbent carbons for air separation, gas storage, and gas clean up were also evaluated and compared with those of the coal-and nut shell derived carbons as well as a commercial activated carbon. The results revealed that TDCA carbons are suitable adsorbents for removing vapor-phase mercury from combustion flue gases and hazardous organic compounds from industrial gas streams.

  13. Carbon fiber composite molecular sieves

    SciTech Connect

    Burchell, T.D.; Rogers, M.R.; Williams, A.M.

    1996-06-01

    The removal of CO{sub 2} is of significance in several energy applications. The combustion of fossil fuels, such as coal or natural gas, releases large volumes of CO{sub 2} to the environment. Several options exist to reduce CO{sub 2} emissions, including substitution of nuclear power for fossil fuels, increasing the efficiency of fossil plants and capturing the CO{sub 2} prior to emission to the environment. All of these techniques have the attractive feature of limiting the amount of CO{sub 2} emitted to the atmosphere, but each has economic, technical, or societal limitations. In the production of natural gas, the feed stream from the well frequently contains contaminants and diluents which must be removed before the gas can enter the pipeline distribution system. Notable amongst these diluent gasses is CO{sub 2}, which has no calorific value. Currently, the pipeline specification calls for <2 mol % CO{sub 2} in the gas. Gas separation is thus a relevant technology in the field of energy production. A novel separation system based on a parametric swing process has been developed that utilizes the unique combination of properties exhibited by our carbon fiber composite molecular sieve (CFCMS).

  14. Interaction between adsorbed hydrogen and potassium on a carbon nanocone containing material as studied by photoemission

    SciTech Connect

    Yu, Xiaofeng; Raaen, Steinar

    2015-09-14

    Hydrogen adsorption on a potassium doped carbon nanocone containing material was studied by photoelectron spectroscopy and work function measurement. The valence band spectra indicate that there is charge transfer from potassium to carbon. Upon deposition on carbon potassium is in its ionic state for lower doping and shows both ionic and metallic behavior at higher doping. Adsorption of hydrogen facilitates diffusion of potassium on the carbon material as seen by changes in the K{sub 2p} core level spectrum. Variations in the measured sample work function indicate that hydrogen initially adsorb on the K dopants and subsequently adsorb on the carbon cone containing material.

  15. Enhanced performance of electrospun carbon fibers modified with carbon nanotubes: promising electrodes for enzymatic biofuel cells

    NASA Astrophysics Data System (ADS)

    Both Engel, A.; Cherifi, A.; Tingry, S.; Cornu, D.; Peigney, A.; Laurent, Ch

    2013-06-01

    New nanostructured electrodes, promising for the production of clean and renewable energy in biofuel cells, were developed with success. For this purpose, carbon nanofibers were produced by the electrospinning of polyacrylonitrile solution followed by convenient thermal treatments (stabilization followed by carbonization at 1000, 1200 and 1400° C), and carbon nanotubes were adsorbed on the surfaces of the fibers by a dipping method. The morphology of the developed electrodes was characterized by several techniques (SEM, Raman spectroscopy, electrical conductivity measurement). The electrochemical properties were evaluated through cyclic voltammetry, where the influence of the carbonization temperature of the fibers and the beneficial contribution of the carbon nanotubes were observed through the reversibility and size of the redox peaks of K3Fe(CN)6 versus Ag/AgCl. Subsequently, redox enzymes were immobilized on the electrodes and the electroreduction of oxygen to water was realized as a test of their efficiency as biocathodes. Due to the fibrous and porous structure of these new electrodes, and to the fact that carbon nanotubes may have the ability to promote electron transfer reactions of redox biomolecules, the new electrodes developed were capable of producing higher current densities than an electrode composed only of electrospun carbon fibers.

  16. Enhanced performance of electrospun carbon fibers modified with carbon nanotubes: promising electrodes for enzymatic biofuel cells.

    PubMed

    Engel, A Both; Cherifi, A; Tingry, S; Cornu, D; Peigney, A; Laurent, Ch

    2013-06-21

    New nanostructured electrodes, promising for the production of clean and renewable energy in biofuel cells, were developed with success. For this purpose, carbon nanofibers were produced by the electrospinning of polyacrylonitrile solution followed by convenient thermal treatments (stabilization followed by carbonization at 1000, 1200 and 1400° C), and carbon nanotubes were adsorbed on the surfaces of the fibers by a dipping method. The morphology of the developed electrodes was characterized by several techniques (SEM, Raman spectroscopy, electrical conductivity measurement). The electrochemical properties were evaluated through cyclic voltammetry, where the influence of the carbonization temperature of the fibers and the beneficial contribution of the carbon nanotubes were observed through the reversibility and size of the redox peaks of K3Fe(CN)6 versus Ag/AgCl. Subsequently, redox enzymes were immobilized on the electrodes and the electroreduction of oxygen to water was realized as a test of their efficiency as biocathodes. Due to the fibrous and porous structure of these new electrodes, and to the fact that carbon nanotubes may have the ability to promote electron transfer reactions of redox biomolecules, the new electrodes developed were capable of producing higher current densities than an electrode composed only of electrospun carbon fibers.

  17. Characterization of electrospun lignin based carbon fibers

    SciTech Connect

    Poursorkhabi, Vida; Mohanty, Amar; Misra, Manjusri

    2015-05-22

    The production of lignin fibers has been studied in order to replace the need for petroleum based precursors for carbon fiber production. In addition to its positive environmental effects, it also benefits the economics of the industries which cannot take advantage of carbon fiber properties because of their high price. A large amount of lignin is annually produced as the byproduct of paper and growing cellulosic ethanol industry. Therefore, finding high value applications for this low cost, highly available material is getting more attention. Lignin is a biopolymer making about 15 – 30 % of the plant cell walls and has a high carbon yield upon carbonization. However, its processing is challenging due to its low molecular weight and also variations based on its origin and the method of separation from cellulose. In this study, alkali solutions of organosolv lignin with less than 1 wt/v% of poly (ethylene oxide) and two types of lignin (hardwood and softwood) were electrospun followed by carbonization. Different heating programs for carbonization were tested. The carbonized fibers had a smooth surface with an average diameter of less than 5 µm and the diameter could be controlled by the carbonization process and lignin type. Scanning electron microscopy (SEM) was used to study morphology of the fibers before and after carbonization. Thermal conductivity of a sample with amorphous carbon was 2.31 W/m.K. The electrospun lignin carbon fibers potentially have a large range of application such as in energy storage devices and water or gas purification systems.

  18. Preparation and characterization of novel carbon dioxide adsorbents based on polyethylenimine-modified Halloysite nanotubes.

    PubMed

    Cai, Haohao; Bao, Feng; Gao, Jie; Chen, Tao; Wang, Si; Ma, Rui

    2015-01-01

    New nano-sized carbon dioxide (CO2) adsorbents based on Halloysite nanotubes impregnated with polyethylenimine (PEI) were designed and synthesized, which were excellent adsorbents for the capture of CO2 at room temperature and had relatively high CO2 adsorption capacity. The prepared adsorbents were characterized by various techniques such as Fourier transform infrared spectrometry, gel permeation chromatography, dynamic light scattering, thermogravimetry, thermogravimetry-Fourier transform-infrared spectrometry, scanning electron microscopy and transmission electron microscopy. The adsorption characteristics and capacity were studied at room temperature, the highest CO2 adsorption capacity of 156.6 mg/g-PEI was obtained and the optimal adsorption capacity can reach a maximum value of 54.8 mg/g-adsorbent. The experiment indicated that this kind of adsorbent has a high stability at 80°C and PEI-impregnated adsorbents showed good reversibility and stability during cyclic adsorption-regeneration tests.

  19. Mesoporous carbon adsorbents from melamine-formaldehyde resin using nanocasting technique for CO2 adsorption.

    PubMed

    Goel, Chitrakshi; Bhunia, Haripada; Bajpai, Pramod K

    2015-06-01

    Mesoporous carbon adsorbents, having high nitrogen content, were synthesized via nanocasting technique with melamine-formaldehyde resin as precursor and mesoporous silica as template. A series of adsorbents were prepared by varying the carbonization temperature from 400 to 700°C. Adsorbents were characterized thoroughly by nitrogen sorption, X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), thermogravimetric analysis (TGA), elemental (CHN) analysis, Fourier transform infrared (FTIR) spectroscopy and Boehm titration. Carbonization temperature controlled the properties of the synthesized adsorbents ranging from surface area to their nitrogen content, which play major role in their application as adsorbents for CO2 capture. The nanostructure of these materials was confirmed by XRD and TEM. Their nitrogen content decreased with an increase in carbonization temperature while other properties like surface area, pore volume, thermal stability and surface basicity increased with the carbonization temperature. These materials were evaluated for CO2 adsorption by fixed-bed column adsorption experiments. Adsorbent synthesized at 700°C was found to have the highest surface area and surface basicity along with maximum CO2 adsorption capacity among the synthesized adsorbents. Breakthrough time and CO2 equilibrium adsorption capacity were investigated from the breakthrough curves and were found to decrease with increase in adsorption temperature. Adsorption process for carbon adsorbent-CO2 system was found to be reversible with stable adsorption capacity over four consecutive adsorption-desorption cycles. From three isotherm models used to analyze the equilibrium data, Temkin isotherm model presented a nearly perfect fit implying the heterogeneous adsorbent surface.

  20. Effects of carbon fibers on consumer products

    NASA Technical Reports Server (NTRS)

    Wise, R. A.; Lovett, C. D.

    1980-01-01

    The potential effects of carbon fibers on consumer products such as dishwashers, microwave ovens, and smoke detectors were investigated. The investigation was divided into two categories to determine the potential faults and hazards that could occur if fibers should enter the electrical circuits of the selected appliances. The categories were a fault analysis and a hazard analysis. Hazards considered were fire, flood, physical harm, explosion, and electrical shock. Electrical shock was found to be a possible occurrence related to carbon fibers. Faults were considered to be any effect on the performance of an appliance which would result in complaint or require service action.

  1. Enhanced carbon nanotube fibers by polyimide

    NASA Astrophysics Data System (ADS)

    Fang, Chao; Zhao, Jingna; Jia, Jingjing; Zhang, Zuoguang; Zhang, Xiaohua; Li, Qingwen

    2010-11-01

    The performance of carbon nanotube (CNT) fibers is limited by the intertube characteristics. Here we report a direct method of curing to improve mechanical properties of poly(amic acid)-infiltrated fibers. After curing at 190 °C for 60 min the fibers composed of double- and triple-walled CNTs, their strength is stably improved by 30.3%, from 1.58 to 2.06 GPa. The enhancement arises from the increase in shear stress between tube surfaces, by measuring the static frictional force of CNT fibers. Due to the existence of CNTs, the imidization temperature of polyimide drops greatly from 218 to 157 °C.

  2. Carbon nanotube-doped polymer optical fiber.

    PubMed

    Uchida, Sho; Martinez, Amos; Song, Yong-Won; Ishigure, Takaaki; Yamashita, Shinji

    2009-10-15

    We present a method to fabricate graded-index multimode polymer optical fibers doped with carbon nanotubes (CNTs). Such fiber structures provide the means to fully utilize the exceptional optical properties of the CNTs. The core region of the fiber is composed of CNTs and polymethyl methacrylate (PMMA) with the addition of diphenyl sulfide (DPS), which acts as the dispersion stabilizer of CNTs in PMMA as well as the dopant to increase the refractive index of the core. Utilizing 2.5 cm of the fiber as a saturable absorber, passively mode-locked lasing with duration of 3.0 ps and repetition rate of 30.3 MHz was demonstrated.

  3. High Performance Multifunctional Carbon Nanotube Fibers

    NASA Astrophysics Data System (ADS)

    Dalton, Alan; Collins, Steve; Munoz, Edgar; Razal, Joselito; Ebron, Von; Ferraris, John; Baughman, Ray

    2003-03-01

    Exploiting the extraordinary properties of carbon nanotubes has remained somewhat elusive due to the inability to process the as produced insoluble soot into functional macroscopic assemblies. To this end we have developed a simple but effective method to produce continuous, homogeneous fibers containing carbon nanotubes having as-spun mechanical properties that compare very favorably to recognized synthetic and natural "super fibers" such as Kevlar and spider silk. By using novel spinning apparatus, spinning solutions, and spinning coagulants, we have spun nanotube fibers having record lengths, record tensile strengths, and having an energy-to-break (toughness) higher than any material that we have found. As an example of the potential multi-functionalities of our fibers, we have fabricated fiber supercapacitors, which we weave into textiles.

  4. Extraction of palladium from acidic solutions with the use of carbon adsorbents

    SciTech Connect

    O.N. Kononova; N.G. Goryaeva; N.B. Dostovalova; S.V. Kachin; A.G. Kholmogorov

    2007-08-15

    We studied the sorption of palladium(II) on LKAU-4, LKAU-7, and BAU carbon adsorbents from model hydrochloric acid solutions and the solutions of spent palladium-containing catalysts. It was found that sorbents based on charcoal (BAU) and anthracite (LKAU-4) were characterized by high sorption capacities for palladium. The kinetics of the saturation of carbon adsorbents with palladium(II) ions was studied, and it was found that more than 60% of the initial amount of Pd(II) was recovered in a 1-h contact of an adsorbent with a model solution. This value for the solutions of spent catalysts was higher than 35%.

  5. Adsorption characteristics of benzene on biosolid adsorbent and commercial activated carbons

    SciTech Connect

    Hung-Lung Chiang; Kuo-Hsiung Lin; Chih-Yu Chen; Ching-Guan Choa; Ching-Shyung Hwu; Nina Lai

    2006-05-15

    This study selected biosolids from a petrochemical wastewater treatment plant as the raw material. The sludge was immersed in 0.5-5 M of zinc chloride (ZnCl{sub 2}) solutions and pyrolyzed at different temperatures and times. Results indicated that the 1-M ZnCl{sub 2}-immersed biosolids pyrolyzed at 500{sup o}C for 30 min could be reused and were optimal biosolid adsorbents for benzene adsorption. Pore volume distribution analysis indicated that the mesopore contributed more than the macropore and micropore in the biosolid adsorbent. The benzene adsorption capacity of the biosolid adsorbent was 65 and 55% of the G206 (granular-activated carbon) and BPL (coal-based activated carbon; Calgon, Carbon Corp.) activated carbons, respectively. Data from the adsorption and desorption cycles indicated that the benzene adsorption capacity of the biosolid adsorbent was insignificantly reduced compared with the first-run capacity of the adsorbent; therefore, the biosolid adsorbent could be reused as a commercial adsorbent, although its production cost is high. 18 refs., 9 figs., 3 tabs.

  6. Rotary adsorbers for continuous bulk separations

    DOEpatents

    Baker, Frederick S.

    2011-11-08

    A rotary adsorber for continuous bulk separations is disclosed. The rotary adsorber includes an adsorption zone in fluid communication with an influent adsorption fluid stream, and a desorption zone in fluid communication with a desorption fluid stream. The fluid streams may be gas streams or liquid streams. The rotary adsorber includes one or more adsorption blocks including adsorbent structure(s). The adsorbent structure adsorbs the target species that is to be separated from the influent fluid stream. The apparatus includes a rotary wheel for moving each adsorption block through the adsorption zone and the desorption zone. A desorption circuit passes an electrical current through the adsorbent structure in the desorption zone to desorb the species from the adsorbent structure. The adsorbent structure may include porous activated carbon fibers aligned with their longitudinal axis essentially parallel to the flow direction of the desorption fluid stream. The adsorbent structure may be an inherently electrically-conductive honeycomb structure.

  7. Carbon fiber production at low temperatures from polyacrylonitrile

    NASA Technical Reports Server (NTRS)

    Cagliostro, D. E.

    1980-01-01

    Recent safety considerations have sought to lower the electrical conductivity of carbon fibers. Carbon fibers produced from polyacrylonitrile at low carbonization temperatures (600-900 C) possess low electrical conductivity but do not possess adequate strength. Low-temperature processes are described which improve fiber strength but do not increase electrical conductivity substantially. The processes result in a carbon fiber with nearly twice the tensile strength compared to the old process. Process development and its effect on fiber properties are reported.

  8. FIBER LENGTH DISTRIBUTION MEASUREMENT FOR LONG GLASS AND CARBON FIBER REINFORCED INJECTION MOLDED THERMOPLASTICS

    SciTech Connect

    Kunc, Vlastimil; Frame, Barbara J; Nguyen, Ba N.; TuckerIII, Charles L.; Velez-Garcia, Gregorio

    2007-01-01

    Procedures for fiber length distribution (FLD) measurement of long fiber reinforced injection molded thermoplastics were refined for glass and carbon fibers. Techniques for sample selection, fiber separation, digitization and length measurement for both fiber types are described in detail. Quantitative FLD results are provided for glass and carbon reinforced polypropylene samples molded with a nominal original fiber length of 12.7 mm (1/2 in.) using equipment optimized for molding short fiber reinforced thermoplastics.

  9. Large diameter carbon-boron fiber

    NASA Technical Reports Server (NTRS)

    Veltri, R. D.; Jacob, B. A.; Galasso, F. S.

    1975-01-01

    Investigations concerned with a development of large-diameter carbon fibers are considered, taking into account the employment of vapor deposition techniques. In the experiments a carbon monofilament substrate is used together with reacting gases which consist of combinations of hydrogen, methane, and boron trichloride. It is found that the described approach can be used to obtain a large-diameter carbon filament containing boron. The filament has reasonable strength and modulus properties.

  10. Development of nitrogen enriched nanostructured carbon adsorbents for CO2 capture.

    PubMed

    Goel, Chitrakshi; Bhunia, Haripada; Bajpai, Pramod K

    2015-10-01

    Nanostructured carbon adsorbents containing high nitrogen content were developed by templating melamine-formaldehyde resin in the pores of mesoporous silica by nanocasting technique. A series of adsorbents were prepared by altering the carbonization temperature from 400 to 700 °C and characterized in terms of their textural and morphological properties. CO2 adsorption performance was investigated at various temperatures from 30 to 100 °C by using a thermogravimetric analyzer under varying CO2 concentrations. Multiple adsorption-desorption experiments were also carried out to investigate the adsorbent regenerability. X-ray diffraction (XRD) and transmission electron microscopy (TEM) confirmed the development of nanostructured materials. Fourier transform infrared spectroscopy (FTIR) and elemental analysis indicated the development of carbon adsorbents having high nitrogen content. The surface area and pore volume of the adsorbent carbonized at 700 °C were found to be 266 m(2) g(-1) and 0.25 cm(3) g(-1) respectively. CO2 uptake profile for the developed adsorbents showed that the maximum CO2 adsorption occurred within ca. 100 s. CO2 uptake of 0.792 mmol g(-1) at 30 °C was exhibited by carbon obtained at 700 °C with complete regenerability in three adsorption-desorption cycles. Furthermore, kinetics of CO2 adsorption on the developed adsorbents was studied by fitting the experimental data of CO2 uptake to three kinetic models with best fit being obtained by fractional order kinetic model with error% within range of 5%. Adsorbent surface was found to be energetically heterogeneous as suggested by Temkin isotherm model. Also the isosteric heat of adsorption for CO2 was observed to increase from ca. 30-44 kJ mol(-1) with increase in surface coverage.

  11. Thermoplastic coated carbon fibers for textile preforms

    NASA Technical Reports Server (NTRS)

    Allen, L. E.; Edie, D. D.; Lickfield, G. C.; Mccollum, J. R.

    1988-01-01

    A continuous process for producing prepreg from carbon fiber and thermoplastic matrix is described. After the tow has been spread using a pneumatic device, the process utilizes a fluidized bed to apply thermoplastic powder to the bundle. Finally, direct electrical heating of the coated fiber tow melts the polymer on the individual fibers, creating a uniform and extremely flexible prepreg. The efficiency of the process was evaluated during initial trials in which a thermoplastic polyimide, LaRC-TPI, was applied to T-300, 3K (3000 filament) carbon fiber tow. The physical properties of unidirectional composite specimens fabricated from this prepreg were measured, and the matrix uniformity and void content of the samples was determined. The results of these evaluations are detailed and discussed.

  12. Epoxide-functionalization of polyethyleneimine for synthesis of stable carbon dioxide adsorbent in temperature swing adsorption.

    PubMed

    Choi, Woosung; Min, Kyungmin; Kim, Chaehoon; Ko, Young Soo; Jeon, Jae Wan; Seo, Hwimin; Park, Yong-Ki; Choi, Minkee

    2016-01-01

    Amine-containing adsorbents have been extensively investigated for post-combustion carbon dioxide capture due to their ability to chemisorb low-concentration carbon dioxide from a wet flue gas. However, earlier studies have focused primarily on the carbon dioxide uptake of adsorbents, and have not demonstrated effective adsorbent regeneration and long-term stability under such conditions. Here, we report the versatile and scalable synthesis of a functionalized-polyethyleneimine (PEI)/silica adsorbent which simultaneously exhibits a large working capacity (2.2 mmol g(-1)) and long-term stability in a practical temperature swing adsorption process (regeneration under 100% carbon dioxide at 120 °C), enabling the separation of concentrated carbon dioxide. We demonstrate that the functionalization of PEI with 1,2-epoxybutane reduces the heat of adsorption and facilitates carbon dioxide desorption (>99%) during regeneration compared with unmodified PEI (76%). Moreover, the functionalization significantly improves long-term adsorbent stability over repeated temperature swing adsorption cycles due to the suppression of urea formation and oxidative amine degradation. PMID:27572662

  13. Epoxide-functionalization of polyethyleneimine for synthesis of stable carbon dioxide adsorbent in temperature swing adsorption

    NASA Astrophysics Data System (ADS)

    Choi, Woosung; Min, Kyungmin; Kim, Chaehoon; Ko, Young Soo; Jeon, Jae Wan; Seo, Hwimin; Park, Yong-Ki; Choi, Minkee

    2016-08-01

    Amine-containing adsorbents have been extensively investigated for post-combustion carbon dioxide capture due to their ability to chemisorb low-concentration carbon dioxide from a wet flue gas. However, earlier studies have focused primarily on the carbon dioxide uptake of adsorbents, and have not demonstrated effective adsorbent regeneration and long-term stability under such conditions. Here, we report the versatile and scalable synthesis of a functionalized-polyethyleneimine (PEI)/silica adsorbent which simultaneously exhibits a large working capacity (2.2 mmol g-1) and long-term stability in a practical temperature swing adsorption process (regeneration under 100% carbon dioxide at 120 °C), enabling the separation of concentrated carbon dioxide. We demonstrate that the functionalization of PEI with 1,2-epoxybutane reduces the heat of adsorption and facilitates carbon dioxide desorption (>99%) during regeneration compared with unmodified PEI (76%). Moreover, the functionalization significantly improves long-term adsorbent stability over repeated temperature swing adsorption cycles due to the suppression of urea formation and oxidative amine degradation.

  14. Epoxide-functionalization of polyethyleneimine for synthesis of stable carbon dioxide adsorbent in temperature swing adsorption.

    PubMed

    Choi, Woosung; Min, Kyungmin; Kim, Chaehoon; Ko, Young Soo; Jeon, Jae Wan; Seo, Hwimin; Park, Yong-Ki; Choi, Minkee

    2016-08-30

    Amine-containing adsorbents have been extensively investigated for post-combustion carbon dioxide capture due to their ability to chemisorb low-concentration carbon dioxide from a wet flue gas. However, earlier studies have focused primarily on the carbon dioxide uptake of adsorbents, and have not demonstrated effective adsorbent regeneration and long-term stability under such conditions. Here, we report the versatile and scalable synthesis of a functionalized-polyethyleneimine (PEI)/silica adsorbent which simultaneously exhibits a large working capacity (2.2 mmol g(-1)) and long-term stability in a practical temperature swing adsorption process (regeneration under 100% carbon dioxide at 120 °C), enabling the separation of concentrated carbon dioxide. We demonstrate that the functionalization of PEI with 1,2-epoxybutane reduces the heat of adsorption and facilitates carbon dioxide desorption (>99%) during regeneration compared with unmodified PEI (76%). Moreover, the functionalization significantly improves long-term adsorbent stability over repeated temperature swing adsorption cycles due to the suppression of urea formation and oxidative amine degradation.

  15. Epoxide-functionalization of polyethyleneimine for synthesis of stable carbon dioxide adsorbent in temperature swing adsorption

    PubMed Central

    Choi, Woosung; Min, Kyungmin; Kim, Chaehoon; Ko, Young Soo; Jeon, Jae Wan; Seo, Hwimin; Park, Yong-Ki; Choi, Minkee

    2016-01-01

    Amine-containing adsorbents have been extensively investigated for post-combustion carbon dioxide capture due to their ability to chemisorb low-concentration carbon dioxide from a wet flue gas. However, earlier studies have focused primarily on the carbon dioxide uptake of adsorbents, and have not demonstrated effective adsorbent regeneration and long-term stability under such conditions. Here, we report the versatile and scalable synthesis of a functionalized-polyethyleneimine (PEI)/silica adsorbent which simultaneously exhibits a large working capacity (2.2 mmol g−1) and long-term stability in a practical temperature swing adsorption process (regeneration under 100% carbon dioxide at 120 °C), enabling the separation of concentrated carbon dioxide. We demonstrate that the functionalization of PEI with 1,2-epoxybutane reduces the heat of adsorption and facilitates carbon dioxide desorption (>99%) during regeneration compared with unmodified PEI (76%). Moreover, the functionalization significantly improves long-term adsorbent stability over repeated temperature swing adsorption cycles due to the suppression of urea formation and oxidative amine degradation. PMID:27572662

  16. Coating for gasifiable carbon-graphite fibers

    NASA Technical Reports Server (NTRS)

    Harper-Tervet, Jan (Inventor); Dowler, Warren L. (Inventor); Yen, Shiao-Ping S. (Inventor); Mueller, William A. (Inventor)

    1982-01-01

    A thin, uniform, firmly adherent coating of metal gasification catalyst is applied to a carbon-graphite fiber by first coating the fiber with a film-forming polymer containing functional moieties capable of reaction with the catalytic metal ions. Multivalent metal cations such as calcium cross-link the polymer such as a polyacrylic acid to insolubilize the film by forming catalytic metal macro-salt links between adjacent polymer chains. The coated fibers are used as reinforcement for resin composites and will gasify upon combustion without evolving conductive airborne fragments.

  17. Hybrid solar cell on a carbon fiber.

    PubMed

    Grynko, Dmytro A; Fedoryak, Alexander N; Smertenko, Petro S; Dimitriev, Oleg P; Ogurtsov, Nikolay A; Pud, Alexander A

    2016-12-01

    In this work, a method to assemble nanoscale hybrid solar cells in the form of a brush of radially oriented CdS nanowire crystals around a single carbon fiber is demonstrated for the first time. A solar cell was assembled on a carbon fiber with a diameter of ~5-10 μm which served as a core electrode; inorganic CdS nanowire crystals and organic dye or polymer layers were successively deposited on the carbon fiber as active components resulting in a core-shell photovoltaic structure. Polymer, dye-sensitized, and inverted solar cells have been prepared and compared with their analogues made on the flat indium-tin oxide electrode.

  18. Hybrid solar cell on a carbon fiber.

    PubMed

    Grynko, Dmytro A; Fedoryak, Alexander N; Smertenko, Petro S; Dimitriev, Oleg P; Ogurtsov, Nikolay A; Pud, Alexander A

    2016-12-01

    In this work, a method to assemble nanoscale hybrid solar cells in the form of a brush of radially oriented CdS nanowire crystals around a single carbon fiber is demonstrated for the first time. A solar cell was assembled on a carbon fiber with a diameter of ~5-10 μm which served as a core electrode; inorganic CdS nanowire crystals and organic dye or polymer layers were successively deposited on the carbon fiber as active components resulting in a core-shell photovoltaic structure. Polymer, dye-sensitized, and inverted solar cells have been prepared and compared with their analogues made on the flat indium-tin oxide electrode. PMID:27216603

  19. CARBON FIBER COMPOSITES IN HIGH VOLUME

    SciTech Connect

    Warren, Charles David; Das, Sujit; Jeon, Dr. Saeil

    2014-01-01

    Vehicle lightweighting represents one of several design approaches that automotive and heavy truck manufacturers are currently evaluating to improve fuel economy, lower emissions, and improve freight efficiency (tons-miles per gallon of fuel). With changes in fuel efficiency and environmental regulations in the area of transportation, the next decade will likely see considerable vehicle lightweighting throughout the ground transportation industry. Greater use of carbon fiber composites and light metals is a key component of that strategy. This paper examines the competition between candidate materials for lightweighting of heavy vehicles and passenger cars. A 53-component, 25 % mass reduction, body-in-white cost analysis is presented for each material class, highlighting the potential cost penalty for each kilogram of mass reduction and then comparing the various material options. Lastly, as the cost of carbon fiber is a major component of the elevated cost of carbon fiber composites, a brief look at the factors that influence that cost is presented.

  20. Hybrid solar cell on a carbon fiber

    NASA Astrophysics Data System (ADS)

    Grynko, Dmytro A.; Fedoryak, Alexander N.; Smertenko, Petro S.; Dimitriev, Oleg P.; Ogurtsov, Nikolay A.; Pud, Alexander A.

    2016-05-01

    In this work, a method to assemble nanoscale hybrid solar cells in the form of a brush of radially oriented CdS nanowire crystals around a single carbon fiber is demonstrated for the first time. A solar cell was assembled on a carbon fiber with a diameter of ~5-10 μm which served as a core electrode; inorganic CdS nanowire crystals and organic dye or polymer layers were successively deposited on the carbon fiber as active components resulting in a core-shell photovoltaic structure. Polymer, dye-sensitized, and inverted solar cells have been prepared and compared with their analogues made on the flat indium-tin oxide electrode.

  1. Novel method for carbon nanofilament growth on carbon fibers

    SciTech Connect

    Phillips, Johathan; Luhrs, Claudia; Terani, Mehran; Al - Haik, Marwan; Garcia, Daniel; Taha, Mahmoud R

    2009-01-01

    Fiber reinforced structural composites such as fiber reinforced polymers (FRPs) have proven to be key materials for blast mitigation due to their enhanced mechanical performance. However, there is a need to further increase total energy absorption of the composites in order to retain structural integrity in high energy environments, for example, blast events. Research has shown that composite failure in high energy environments can be traced to their relatively low shear strength attributed to the limited bond strength between the matrix and the fibers. One area of focus for improving the strength of composite materials has been to create 'multi-scale' composites. The most common approach to date is to introduce carbon nanotubes into a more traditional composite consisting of epoxy with embedded micron scale fibers. The inclusion of carbon nanotubes (CNT) clearly toughens different matrices. Depositing CNT in brittle matrix increases stiffness by orders of magnitude. Currently, this approach to create multiscale composites is limited due to the difficulty of dispersing significant amounts of nanotubes. It has repeatedly been reported that phase separation occurs above relatively low weight percent loading (ca. 3%) due to the strong van der Waals forces between CNTs compared with that between CNT and polymer. Hence, the nanotubes tend to segregate and form inclusions. One means to prevent nanotube or nanofilament agglomeration is to anchor one end of the nanostructure, thereby creating a stable multi-phase structure. This is most easily done by literally growing the CNTs directly on micron scale fibers. Recently, CNT were grown on carbon fibers, both polyacrylonitrile- (PAN-) and pitch-based, by hot filament chemical vapor deposition (HFCVD) using H2 and CH4 as precursors. Nickel clusters were electrodeposited on the fiber surfaces to catalyze the growth and uniform CNT coatings were obtained on both the PAN- and pitch-based carbon fibers. Multiwalled CNTs with

  2. PREDICTING THE ADSORPTION CAPACITY OF ACTIVATED CARBON FOR ORGANIC CONTAMINANTS FROM ADSORBENT AND ADSORBATE PROPERTIES

    EPA Science Inventory

    A quantitative structure-property relationship (QSPR) was developed and combined with the Polanyi-Dubinin-Manes model to predict adsorption isotherms of emerging contaminants on activated carbons with a wide range of physico-chemical properties. Affinity coefficients (βl

  3. Binding energies and electronic structures of adsorbed titanium chains on carbon nanotubes

    NASA Astrophysics Data System (ADS)

    Yang, Chih-Kai; Zhao, Jijun; Lu, Jianping

    2002-03-01

    Our calculations based on first principles have shown that titanium is much favored energetically over gold and aluminum to form a continuous chain on a variety of single-wall carbon nanotubes (SWNT). Results from two zigzag nanotubes, (10,0) and (14,0), and two armchairs, (6,6) and (8,8), indicate that binding energy for a Ti-adsorbed SWNT is generally six to seven eV per unit cell larger than a Au or Al-adsorbed SWNT. Furthermore, the adsorbed Ti chain generates additional states in the band gaps of the two semi-conducting zigzag nanotubes, transforming them into metals.

  4. Carbon-Fiber Brush Heat Exchangers

    NASA Technical Reports Server (NTRS)

    Knowles, Timothy R.

    2004-01-01

    Velvetlike and brushlike pads of carbon fibers have been proposed for use as mechanically compliant, highly thermally conductive interfaces for transferring heat. A pad of this type would be formed by attaching short carbon fibers to either or both of two objects that one desires to place in thermal contact with each other. The purpose of using a thermal-contact pad of this or any other type is to reduce the thermal resistance of an interface between a heat source and a heat sink.

  5. Carbon Fiber Reinforced Carbon Composite Valve for an Internal Combustion Engine

    NASA Technical Reports Server (NTRS)

    Rivers, H. Kevin (Inventor); Ransone, Philip O. (Inventor); Northam, G. Burton (Inventor)

    1999-01-01

    A carbon fiber reinforced carbon composite valve for internal combustion engines and the like formed of continuous carbon fibers throughout the valve's stem and head is disclosed. The valve includes braided carbon fiber material over axially aligned unidirectional carbon fibers forming a valve stem; the braided and unidirectional carbon fibers being broomed out at one end of the valve stem forming the shape of the valve head; the valve-shaped structure being densified and rigidized with a matrix of carbon containing discontinuous carbon fibers: and the finished valve being treated to resist oxidation. Also disclosed is a carbon matrix plug containing continuous and discontinuous carbon fibers and forming a net-shape valve head acting as a mandrel over which the unidirectional and braided carbon fibers are formed according to textile processes. Also disclosed are various preform valves and processes for making finished and preform carbon fiber reinforced carbon composite valves.

  6. Copper ions removal from water using functionalized carbon nanotubes–mullite composite as adsorbent

    SciTech Connect

    Tofighy, Maryam Ahmadzadeh; Mohammadi, Toraj

    2015-08-15

    Highlights: • CNTs–mullite composite was prepared via chemical vapor deposition (CVD) method. • The prepared composite was modified with concentrated nitric acid and chitosan. • The modified CNTs–mullite composites were used as novel adsorbents. • Copper ion removal from water by the prepared adsorbents was performed. • Langmuir and Freundlich isotherms and two kinetic models were applied to fit the experimental data. - Abstract: Carbon nanotubes–mullite composite was synthesized by direct growth of carbon nanotubes on mullite particles via chemical vapor deposition method using cyclohexanol and ferrocene as carbon precursor and catalyst, respectively. The carbon nanotubes–mullite composite was oxidized with concentrated nitric acid and functionalized with chitosan and then used as a novel adsorbent for copper ions removal from water. The results demonstrated that modification with concentrated nitric acid and chitosan improves copper ions adsorption capacity of the prepared composite, significantly. Langmuir and Freundlich isotherms and two kinetic models were applied to fit the experimental data. The carbon nanotubes growth on mullite particles to form the carbon nanotubes–mullite composite with further modification is an inherently safe approach for many promising environmental applications to avoid some concerns regarding environment, health and safety. It was found that the modified carbon nanotubes–mullite composite can be considered as an excellent adsorbent for copper ions removal from water.

  7. Comparison of toluene adsorption among granular activated carbon and different types of activated carbon fibers (ACFs).

    PubMed

    Balanay, Jo Anne G; Crawford, Shaun A; Lungu, Claudiu T

    2011-10-01

    Activated carbon fiber (ACF) has been demonstrated to be a good adsorbent for the removal of organic vapors in air. Some ACF has a comparable or larger surface area and higher adsorption capacity when compared with granular activated carbon (GAC) commonly used in respiratory protection devices. ACF is an attractive alternative adsorbent to GAC because of its ease of handling, light weight, and decreasing cost. ACF may offer the potential for short-term respiratory protection for first responders and emergency personnel. This study compares the critical bed depths and adsorption capacities for toluene among GAC and ACF of different forms and surface areas. GAC and ACF in cloth (ACFC) and felt (ACFF) forms were challenged in stainless steel chambers with a constant concentration of 500 ppm toluene via conditioned air at 25°C, 50% RH, and constant airflow (7 L/min). Breakthrough data were obtained for each adsorbent using gas chromatography with flame ionization detector. Surface areas of each adsorbent were determined using a physisorption analyzer. Results showed that the critical bed depth of GAC is 275% higher than the average of ACFC but is 55% lower than the average of ACFF. Adsorption capacity of GAC (with a nominal surface area of 1800 m(2)/g) at 50% breakthrough is 25% higher than the average of ACF with surface area of 1000 m(2)/g, while the rest of ACF with surface area of 1500 m(2)/g and higher have 40% higher adsorption capacities than GAC. ACFC with higher surface area has the smallest critical bed depth and highest adsorption capacity, which makes it a good adsorbent for thinner and lighter respirators. We concluded that ACF has great potential for application in respiratory protection considering its higher adsorption capacity and lower critical bed depth in addition to its advantages over GAC, particularly for ACF with higher surface area.

  8. CTE Measurements of Carbon Fibers in ESEM

    NASA Technical Reports Server (NTRS)

    Effinger, Michael; Ochoa, Ozden; Munafo, Paul M. (Technical Monitor)

    2001-01-01

    The strong appeal of carbon fiber reinforced ceramic matrix and carbon-carbon composites arises from their promising high temperature performance within laboratory-simulated nozzle, leading edge and combustor environments. The main drawback in these systems are two fold; namely oxidation affinity and CTE mismatch. To date the emphasis has been on axial CTE mismatch with the push on estimating (component) laminate level data. However, in heterogeneous and anisotropic systems, all failure mechanisms are at micro or nano scales. This paper will report plans and progress on single carbon fibers efforts in order to develop its temperature dependent, anisotropic thermophysical and thermomechanical properties using combination of x-ray spectroscopy and environmental scanning electron microscopy to capture circumferential expansion from 20-900 C in within the SEM chamber. Surface roughness measurements were also determined. Crystallinity was also determined by the quality of the electron diffraction (ED) patterns.

  9. Designing the Structure of Carbon Fibers for Optimal Mechanical Properties

    SciTech Connect

    Ozcan, Soydan; Vautard, Frederic; Naskar, Amit K

    2014-01-01

    Carbon fiber manufacturing follows generic processing steps: formation of thermoplastic fibers, stabilization, and carbonization. The final structures and end properties of the carbon fiber can differ significantly depending on the precursor chemistry and the associated processing sciences. Polyacrylonitrile (PAN) and mesophase pitch are the predominant precursors used in the production of carbon fibers. PAN-based carbon fibers consist of nanocrystalline graphitic domains typically 1.5 5 nm in size surrounded by amorphous carbon; in contrast, pitch-based carbon fibers are 10 50 nm crystallites with the graphitic (002) planes mostly aligned parallel to the fiber axis. It has been seen that the skin core structure of PAN-based carbon fibers plays a significant role in their mechanical properties. Designing a more homogenous carbon fiber microstructure by controlling the starting polymer and process parameters results in a different set of tensile strengths and elastic moduli. In this study the microstructural defect distribution (0.1 200 nm), measured by small-angle X-ray scattering, was shown to be directly related to the tensile strength of the carbon fibers. Here the formation of carbon structures from various polymer precursors is reviewed. Such a comprehensive understanding offers the opportunity to design carbon fiber microstructures with improved properties and to ultimately create new types of carbon fibers from alternative precursors at reduced cost.

  10. Carbon Fibers from Chicken Feather Keratin

    NASA Astrophysics Data System (ADS)

    Miller, Melissa E.; Wool, Richard

    2006-03-01

    As the availability of synthetic and fossil-fuel based resources is becoming limited, bio-based materials offer an environmentally friendly alternative. Chicken feathers remain a huge agricultural waste. The feathers are comprised of approximately 97% keratin, but are currently used only to enrich animal feed. However, this usage is becoming a problem with the spread of diseases such as Bovine Spongiform Encephalopathy, commonly called ``Mad Cow Disease.'' The hollow, microcrystalline, oriented keratin feather fibers offer a novel, low cost approach to producing carbon fibers through controlled pyrolysis. Carbonized feather fibers (CFF) were prepared by first heating to 225 ^oC (below the melting point)in N2 for 26 hours to crosslink and stabilize the fiber structure; then carbonization occurred by increasing the temperature to 450 ^oC for two more hours. The resulting CFF were hollow, stiff and strong and had an affine 80% weight loss, which is near the theoretical value for the C-content of keratin. Initial studies showed that a composite with the CFF and an epoxidized soybean oil (AESO) gave an improved fiber modulus ECFF of order 13.5--66.1 GPa. With continued research, the goals are to increase the stiffness of the feathers to 100 GPa, while increasing the strength in the range of 5-10 GPa.

  11. Carbon dioxide adsorbents containing magnesium oxide suitable for use at high temperatures

    DOEpatents

    Mayorga, Steven Gerard; Weigel, Scott Jeffrey; Gaffney, Thomas Richard; Brzozowski, Jeffrey Richard

    2001-01-01

    Adsorption of carbon dioxide from gas streams at temperatures in the range of 300 to 500.degree. C. is carried out with a solid adsorbent containing magnesium oxide, preferably promoted with an alkali metal carbonate or bicarbonate so that the atomic ratio of alkali metal to magnesium is in the range of 0.006 to 2.60. Preferred adsorbents are made from the precipitate formed on addition of alkali metal and carbonate ions to an aqueous solution of a magnesium salt. Atomic ratios of alkali metal to magnesium can be adjusted by washing the precipitate with water. Low surface area adsorbents can be made by dehydration and CO.sub.2 removal of magnesium hydroxycarbonate, with or without alkali metal promotion. The process is especially valuable in pressure swing adsorption operations.

  12. Metal fiber - carbon electrodes for oxygen reduction

    NASA Astrophysics Data System (ADS)

    Smith, Robert Fendlay

    An investigation was carried out to determine activities for oxygen reduction and current efficiencies to hydrogen peroxide of commercially available nickel fibers, carbon fibers, and carbon powders. The activities and current efficiencies were determined by conducting Rotating Ring Disk Electrode Experiments (RRDE) on porous electrodes that utilize an interlocking network of metal fibers with carbon fibers and/or powders. Experimentation was also done using PTFE - carbon powder and PTFE - nickel fiber paste electrodes to remove any porosity and symbiotic effects of the nickel - carbon electrodes. Results of the traditional flat plate PTFE electrodes were compared to the porous electrodes to verify the proposed mathematical viability of porous electrode RRDE. RRDE experiments showed that the most active carbons for oxygen reduction have a surface area to volume ratio of 1000 m2/g, and current rent efficiency to hydrogen peroxide was increased as the average pore size increased. A mathematical model and half-cell polarization experiments were used to characterize and optimize oxygen reduction in gas diffusion electrodes consisting of carbon fibers and/or powders entrapped in a sinter-locked network of nickel microfibers. Important electrode physical parameters, such as nickel fiber loading (0.005 to 0.01 g/cm2) , nickel fiber diameter (2 to 12 mum), void volume (73 to 96%), distance of the active layer from the gas supply (0 to 0.005 cm), and addition of a peroxide decomposition catalyst (0 to 0.004 g/cm2) were systematically varied to determine their effects on electrode performance. Experimentally determined total currents and current efficiencies to hydrogen peroxide were compared to calculated values for model verification. Other important parameters, including intra-electrode oxygen and hydrogen peroxide concentrations, overpotentials, and reaction rates, were simulated to help optimize the electrode. Fabricated metal fiber-carbon electrodes were compared to a

  13. Process for producing an activated carbon adsorbent with integral heat transfer apparatus

    NASA Technical Reports Server (NTRS)

    Jones, Jack A. (Inventor); Yavrouian, Andre H. (Inventor)

    1996-01-01

    A process for producing an integral adsorbent-heat exchanger apparatus useful in ammonia refrigerant heat pump systems. In one embodiment, the process wets an activated carbon particles-solvent mixture with a binder-solvent mixture, presses the binder wetted activated carbon mixture on a metal tube surface and thereafter pyrolyzes the mixture to form a bonded activated carbon matrix adjoined to the tube surface. The integral apparatus can be easily and inexpensively produced by the process in large quantities.

  14. [Fusion implants of carbon fiber reinforced plastic].

    PubMed

    Früh, H J; Liebetrau, A; Bertagnoli, R

    2002-05-01

    Carbon fiber reinforced plastics (CFRP) are used in the medical field when high mechanical strength, innovative design, and radiolucency (see spinal fusion implants) are needed. During the manufacturing process of the material CFRP carbon fibers are embedded into a resin matrix. This resin material could be thermoset (e.g., epoxy resin EPN/DDS) or thermoplastic (e.g., PEAK). CFRP is biocompatible, radiolucent, and has higher mechanical capabilities compared to other implant materials. This publication demonstrates the manufacturing process of fusion implants made of a thermoset matrix system using a fiber winding process. The material has been used clinically since 1994 for fusion implants of the cervical and lumbar spine. The results of the fusion systems CORNERSTONE-SR C (cervical) and UNION (lumbar) showed no implant-related complications. New implant systems made of this CFRP material are under investigation and are presented.

  15. Chemisorption on surfaces — an historical look at a representative adsorbate: carbon monoxide

    NASA Astrophysics Data System (ADS)

    Yates, John T.

    1994-01-01

    The study of the interaction of molecules with clean surfaces extends back to the work of Irving Langmuir. In this historical account, the development of selected experimental methods for the study of molecular adsorption will be discussed. This will be done by historically reviewing research on one of the most well-studied adsorbate molecules, carbon monoxide. Many of the modern surface science techniques have first been used to study chemisorbed carbon monoxide, and the CO molecule is employed even today as a test molecule for currently developing surface measurement instruments such as the low temperature STM. In addition to being a good test molecule for new surface measurement techniques, adsorbed carbon monoxide is one of the centrally important molecules in the field of heterogeneous catalysis where the production of synthetic fuels and useful organic molecules often depends on the catalytic behavior of the adsorbed CO molecule. Interestingly, the carbon monoxide molecule also serves as a bridge between surface chemistry on the transition metals and the field of organometallic chemistry. Concepts about the chemical bonding and the reactive behavior of CO chemisorbed on transition metal surfaces and CO bound in transition metal carbonyls link these two fields together in a significant manner. The carbon monoxide molecule has been the historical focal point of many endeavors in surface chemistry and surface physics, and research on adsorbed carbon monoxide well represents many of the key advances which characterize the first thirty years of the development of surface science.

  16. Microwave axial dielectric properties of carbon fiber.

    PubMed

    Hong, Wen; Xiao, Peng; Luo, Heng; Li, Zhuan

    2015-01-01

    Randomly distributed carbon fibers (CFs) reinforced epoxy resin composites are prepared by the pouring method, the dielectric properties of CF composites with different fiber content and length have been performed in the frequency range from 8.2 to 12.4 GHz. The complex permittivity of the composite increases with the fiber length, which is attributed to the decrease of depolarization field, and increases with the volume fraction, which is attributed to the increase of polarization. A formula, based on the theory of Reynolds-Hugh, is proposed to calculate the effective permittivity of CF composites, and validated by the experiments. The proposed formula is further applied to derive the axial permittivity of CF and analyze the effect of fiber length on the axial permittivity. PMID:26477579

  17. Microwave axial dielectric properties of carbon fiber

    PubMed Central

    Hong, Wen; Xiao, Peng; Luo, Heng; Li, Zhuan

    2015-01-01

    Randomly distributed carbon fibers (CFs) reinforced epoxy resin composites are prepared by the pouring method, the dielectric properties of CF composites with different fiber content and length have been performed in the frequency range from 8.2 to 12.4 GHz. The complex permittivity of the composite increases with the fiber length, which is attributed to the decrease of depolarization field, and increases with the volume fraction, which is attributed to the increase of polarization. A formula, based on the theory of Reynolds-Hugh, is proposed to calculate the effective permittivity of CF composites, and validated by the experiments. The proposed formula is further applied to derive the axial permittivity of CF and analyze the effect of fiber length on the axial permittivity. PMID:26477579

  18. Overview of the carbon fiber problem

    NASA Technical Reports Server (NTRS)

    1979-01-01

    Carbon fibers (CF) composite structures are being utilized more as alternatives to metals in both civilian and military applications. They are valued for their light weight and high strength as well as for their ease of designing structures with specific shapes and sizes. However, a problem may exist due to the high conductivity of CF. CF are manufactured from a precursor material which is subjected to great stress and heat treatment causing a change in the physical and electrical properties. The fibers are bound together by a matrix of epoxy. In the event of fire (aircraft accident) the epoxy would burn away releasing these fibers into the atmosphere. When these fibers come in contact with electronic equipment, they might cause damage to by settling on electrical junctions. An overview is given of the objectives for a study, and the approach and methodology developed for determination of risk profiles.

  19. Microwave axial dielectric properties of carbon fiber

    NASA Astrophysics Data System (ADS)

    Hong, Wen; Xiao, Peng; Luo, Heng; Li, Zhuan

    2015-10-01

    Randomly distributed carbon fibers (CFs) reinforced epoxy resin composites are prepared by the pouring method, the dielectric properties of CF composites with different fiber content and length have been performed in the frequency range from 8.2 to 12.4 GHz. The complex permittivity of the composite increases with the fiber length, which is attributed to the decrease of depolarization field, and increases with the volume fraction, which is attributed to the increase of polarization. A formula, based on the theory of Reynolds-Hugh, is proposed to calculate the effective permittivity of CF composites, and validated by the experiments. The proposed formula is further applied to derive the axial permittivity of CF and analyze the effect of fiber length on the axial permittivity.

  20. Risk methodology overview. [for carbon fiber release

    NASA Technical Reports Server (NTRS)

    Credeur, K. R.

    1979-01-01

    Some considerations of risk estimation, how risk is measured, and how risk analysis decisions are made are discussed. Specific problems of carbon fiber release are discussed by reviewing the objective, describing the main elements, and giving an example of the risk logic and outputs.

  1. Passive CO{sub 2} removal using a carbon fiber composite molecular sieve

    SciTech Connect

    Burchell, T.D.; Judkins, R.R.

    1995-12-01

    Manufacture and characterization of a carbon fiber composite molecular sieve (CFCMS), and its efficacy as a CO{sub 2} gas adsorbent are reported. The CFCMS consists of an isotropic pitch derived carbon fiber and a phenolic resin derived carbon binder. Activation (selective gasification) of the CFCMS creates microporosity in the carbon fibers, yielding high micropore volumes (>0.5 cm{sup 3}/g) and BET surface areas (>1000 m{sup 2}/g). Moreover, the CFCMS material is a rigid, strong, monolith with an open structure that allows the free-flow of fluids through the material. This combination of properties provides an adsorbent material that has several distinct advantages over granular adsorbents in gas separation systems such as pressure swing adsorption (PSA) units. The results of our initial evaluations of the CO{sub 2} adsorption capacity and kinetics of CFCMS are reported. The room temperature CO{sub 2} adsorption capacity of CFCMS is >120 mg of CO{sub 2} per g of CFCMS. A proposed project is described that targets the development, over a three-year period, of a demonstration separation system based on CFCMS for the removal of CO{sub 2} from a flue gas slip stream at a coal-fired power plant. The proposed program would be conducted jointly with industrial and utility partners.

  2. Carbon Dioxide Laser Fiber Optics In Endoscopy

    NASA Astrophysics Data System (ADS)

    Fuller, Terry A.

    1982-12-01

    Carbon dioxide laser surgery has been limited to a great extent to surgical application on the integument and accessible cavities such as the cervix, vagina, oral cavities, etc. This limitation has been due to the rigid delivery systems available to all carbon dioxide lasers. Articulating arms (series of hollow tubes connected by articulating mirrors) have provided an effective means of delivery of laser energy to the patient as long as the lesion was within the direct line of sight. Even direct line-of-sight applications were restricted to physical dimension of the articulating arm or associated hand probes, manipulators and hollow tubes. The many attempts at providing straight endoscopic systems to the laser only stressed the need for a fiber optic capable of carrying the carbon dioxide laser wavelength. Rectangular and circular hollow metal waveguides, hollow dielectric waveguides have proven ineffective to the stringent requirements of a flexible surgical delivery system. One large diameter (1 cm) fiber optic delivery system, incorporates a toxic thalliumAbased fiber optic material. The device is an effective alternative to an articulating arm for external or conventional laser surgery, but is too large and stiff to use as a flexible endoscopic tool. The author describes the first highly flexible inexpensive series of fiber optic systems suitable for either conventional or endoscopic carbon dioxide laser surgery. One system (IRFLEX 3) has been manufactured by Medlase, Inc. for surgical uses capable of delivering 2000w, 100 mJ pulsed energy and 15w continuous wave. The system diameter is 0.035 inches in diameter. Surgically suitable fibers as small as 120 um have been manufactured. Other fibers (IRFLEX 142,447) have a variety of transmission characteristics, bend radii, etc.

  3. Synthesis of magnetic ordered mesoporous carbon (Fe-OMC) adsorbent and its evaluation for fuel desulfurization

    NASA Astrophysics Data System (ADS)

    Farzin Nejad, N.; Shams, E.; Amini, M. K.

    2015-09-01

    In this work, magnetic ordered mesoporous carbon adsorbent was synthesized using soft templating method to adsorb sulfur from model oil (dibenzothiophene in n-hexane). Through this research, pluronic F-127, resorcinol-formaldehyde and hydrated iron nitrate were respectively used as soft template, carbon source and iron source. The adsorbent was characterized by X-ray diffraction, nitrogen adsorption-desorption isotherm and transmission electron microscopy. Nitrogen adsorption-desorption measurement revealed the high surface area (810 m2 g-1), maxima pore size of 3.3 nm and large pore volume (1.01 cm3 g-1) of the synthesized sample. The adsorbent showed a maximum adsorption capacity of 111 mg dibenzothiophene g-1 of adsorbent. Sorption process was described by the pseudo-second-order rate equation and could be better fitted by the Freundlich model, showing the heterogeneous feature of the adsorption process. In addition, the adsorption capacity of regenerated adsorbent was 78.6% of the initial level, after five regeneration cycles.

  4. [Adsorption kinetics of reactive dyes on activated carbon fiber].

    PubMed

    Li, Ying; Yue, Qin-Yan; Gao, Bao-Yu; Yang, Jing; Zheng, Yan

    2007-11-01

    The adsorption capability of activated carbon fiber (ACF) to four reactive dyes (reactive brilliant red K-2BP, reactive turquoise blue KN-G, reactive golden yellow K-3RP, reactive black KN-B) in aqueous solution was studied, and adsorption mechanism was focused on from kinetics point of view. The results show that the equilibrium adsorbing capacity (q(e)) of each dye increases with the addition of initial concentration or temperature. On the same condition, the order of q(e) is: reactive brilliant red > reactive golden yellow > reactive black > reactive turquoise blue. The adsorption processes follow a pseudo second-order kinetic rate equation, and the steric structure, size and polarity of dyes are important influence factors to initial adsorption rate. The adsorption activation energy of each dye is low (16.42, 3.56, 5.21, 26.38 kJ x mol(-1) respectively), which indicates that it belongs to physics adsorption.

  5. Prussian blue caged in spongiform adsorbents using diatomite and carbon nanotubes for elimination of cesium.

    PubMed

    Hu, Baiyang; Fugetsu, Bunshi; Yu, Hongwen; Abe, Yoshiteru

    2012-05-30

    We developed a spongiform adsorbent that contains Prussian blue, which showed a high capacity for eliminating cesium. An in situ synthesizing approach was used to synthesize Prussian blue inside diatomite cavities. Highly dispersed carbon nanotubes (CNTs) were used to form CNT networks that coated the diatomite to seal in the Prussian blue particles. These ternary (CNT/diatomite/Prussian-blue) composites were mixed with polyurethane (PU) prepolymers to produce a quaternary (PU/CNT/diatomite/Prussian-blue), spongiform adsorbent with an in situ foaming procedure. Prussian blue was permanently immobilized in the cell walls of the spongiform matrix and preferentially adsorbed cesium with a theoretical capacity of 167 mg/g cesium. Cesium was absorbed primarily by an ion-exchange mechanism, and the absorption was accomplished by self-uptake of radioactive water by the quaternary spongiform adsorbent.

  6. Growth of Aligned Multiwall Carbon Nanotubes and the Effect of Adsorbates on the Field Emission Properties

    NASA Astrophysics Data System (ADS)

    Milne, W. I.; Teo, K. B. K.; Lansley, S. B.; Chhowalla, M.; Amaratunga, G. A. J.; Semet, V.; Binh, Vu Thien; Pirio, G.; Legagneux, P.

    2003-10-01

    In attempt to decipher the field emission characteristics of multiwall carbon nanotubes (MWCNTs), we have developed a fabrication method based on plasma enhanced chemical vapour deposition (PECVD) to provide utmost control of the nanotube structure such as their alignment, individual position, diameter, length and morphology. We investigated the field emission properties of these nanotubes to elucidate the effect of adsorbates on the nanotubes. Our results show that although the adsorbates cause an apparent lowering of the required turn on voltage/field of the nanotubes, the adsorbates undesirably cause a saturation of the current, large temporal fluctuations in the current, and also a deviation of the emission characteristics from Fowler-Nordheim like emission. The adsorbates are easily removed by extracting an emission current of 1 uA per nanotube or using a high applied electric field (˜25V/um).

  7. Experimental and analytical studies for the NASA carbon fiber risk assessment

    NASA Technical Reports Server (NTRS)

    1980-01-01

    Various experimental and analytical studies performed for the NASA carbon fiber risk assessment program are described with emphasis on carbon fiber characteristics, sensitivity of electrical equipment and components to shorting or arcing by carbon fibers, attenuation effect of carbon fibers on aircraft landing aids, impact of carbon fibers on industrial facilities. A simple method of estimating damage from airborne carbon fibers is presented.

  8. Activation and Micropore Structure Determination of Activated Carbon-Fiber Composites

    SciTech Connect

    Jagtoyen, M.; Derbyshire, F.

    1999-04-23

    Previous work focused on the production of carbon fiber composites and subsequently activating them to induce adsorbent properties. One problem related to this approach is the difficulty of uniformly activating large composites. In order to overcome this problem, composites have been made from pre-activated fibers. The loss of surface area upon forming the composites after activation of the fibers was investigated. The electrical resistivity and strength of these composites were compared to those made by activation after forming. It was found that the surface area is reduced by about 35% by forming the composite from pre-activated fibers. However, the properties of the activated sample are very uniform: the variation in surface area is less than {+-}0.5%. So, although the surface area is somewhat reduced, it is believed that making composites from pre-activated fibers could be useful in applications where the BET surface area is not required to be very high. The strength of the composites produced from pre-activated fibers is lower than for composites activated after forming when the carbon burnoff is below 45%. For higher burnoffs, the strength of composites made with pre-activated fibers is as good or better. In both cases, there is a dramatic decrease in strength when the fiber:binder ratio is reduced below 4:1. The electrical resistivity is slightly higher for composites made from pre-activated fibers than for composites that are activated after forming, other parameters being constant (P-200 fibers, similar carbon burnoffs). For both types of composite the resistivity was also found to increase with carbon burnoff. This is attributed to breakage of the fiber causing shorter conductive paths. The electrical resistivity also increases when the binder content is lowered, which suggests that there are fewer solid contact points between the fibers.

  9. Thermoplastic coating of carbon fibers

    NASA Technical Reports Server (NTRS)

    Edie, D. D.; Lickfield, G. C.; Drews, M. J.; Ellison, M. S.; Allen, L. E.; Mccollum, J. R.; Thomas, H. L.

    1988-01-01

    Now that quantities of prepreg were made on the thermoplastic coating line, they are being formed into both textile preform structures and directly into composite samples. The textile preforms include both woven and knitted structures which will be thermoformed into a finished part. In order to determine if the matrix resin is properly adhering to the fibers or if voids are being formed in the coating process, the tensile strength and modulus of these samples will be tested. The matrix uniformity of matrix distribution in these samples is also being determined using an image analyzer.

  10. Adsorption of bisphenol-A from aqueous solution onto minerals and carbon adsorbents.

    PubMed

    Tsai, Wen-Tien; Lai, Chi-Wei; Su, Ting-Yi

    2006-06-30

    The adsorption behaviors of bisphenol-A, which has been listed as one of endocrine disrupting chemicals, from aqueous solution onto four minerals including andesite, diatomaceous earth, titanium dioxide, and activated bleaching earth, and two activated carbons with coconut-based and coal-based virgins were examined in this work. Based on the adsorption results at the specified conditions, the adsorption capacities of activated carbons are significantly larger than those of mineral adsorbents, implying that the former is effective for removal of the highly hydrophobic adsorbate from the aqueous solution because of its high surface area and low surface polarity. The adsorption capacities of bisphenol-A onto these mineral adsorbents with different pore properties are almost similar in magnitude mainly due to the weakly electrostatic interaction between the mineral surface with negative charge and the target adsorbate with hydrophobic nature. Further, a simplified kinetic model, pseudo-second-order, was tested to investigate the adsorption behaviors of bisphenol-A onto the two common activated carbons at different solution conditions. It was found that the adsorption process could be well described with the pseudo-second-order model. The kinetic parameters of the model obtained in the present work are in line with the pore properties of the two adsorbents.

  11. Adsorption of bisphenol-A from aqueous solution onto minerals and carbon adsorbents.

    PubMed

    Tsai, Wen-Tien; Lai, Chi-Wei; Su, Ting-Yi

    2006-06-30

    The adsorption behaviors of bisphenol-A, which has been listed as one of endocrine disrupting chemicals, from aqueous solution onto four minerals including andesite, diatomaceous earth, titanium dioxide, and activated bleaching earth, and two activated carbons with coconut-based and coal-based virgins were examined in this work. Based on the adsorption results at the specified conditions, the adsorption capacities of activated carbons are significantly larger than those of mineral adsorbents, implying that the former is effective for removal of the highly hydrophobic adsorbate from the aqueous solution because of its high surface area and low surface polarity. The adsorption capacities of bisphenol-A onto these mineral adsorbents with different pore properties are almost similar in magnitude mainly due to the weakly electrostatic interaction between the mineral surface with negative charge and the target adsorbate with hydrophobic nature. Further, a simplified kinetic model, pseudo-second-order, was tested to investigate the adsorption behaviors of bisphenol-A onto the two common activated carbons at different solution conditions. It was found that the adsorption process could be well described with the pseudo-second-order model. The kinetic parameters of the model obtained in the present work are in line with the pore properties of the two adsorbents. PMID:16343748

  12. Improving the interlaminar shear strength of carbon fiber-epoxy composites through carbon fiber bromination

    NASA Technical Reports Server (NTRS)

    Jaworske, Donald A.; Maciag, Carolyn

    1987-01-01

    The use of bromine to improve the interlaminar shear strength of PAN-based carbon fibers was investigated. Composite test specimens fabicated from brominated T-300 fibers and a MY720 matrix exhibited on average a 30% improvement in ILSS over their pristine counterparts. Mass, electrical resistivity, density, contact angle, and scanning Auger microscopy results suggested a mechanism in which the bromine was covalently bonded to the surface of the fiber, and this resulted in an increased van der Waal's adhesion between fiber and matrix.

  13. Carbon Fiber Foam Composites and Methods for Making the Same

    NASA Technical Reports Server (NTRS)

    Leseman, Zayd Chad (Inventor); Atwater, Mark Andrew (Inventor); Phillips, Jonathan (Inventor)

    2014-01-01

    Exemplary embodiments provide methods and apparatus of forming fibrous carbon foams (FCFs). In one embodiment, FCFs can be formed by flowing a fuel rich gas mixture over a catalytic material and components to be encapsulated in a mold to form composite carbon fibers, each composite carbon fiber having a carbon phase grown to encapsulate the component in situ. The composite carbon fibers can be intertwined with one another to form FCFs having a geometry according to the mold.

  14. OZONE REACTION WITH N-ALDEHYDES (N=4-10), BENZALDEHYDE, ETHANOL, ISOPROPANOL, AND N-PROPANOL ADSORBED ON A DUAL-BED GRAPHITIZED CARBON/CARBON MOLECULAR SIEVE ADSORBENT CARTRIDGE

    EPA Science Inventory

    Ozone reacts with n-aldehydes (n = 4 - 10), benzaldehyde, ethanol, isopropanol, and n-propanol adsorbed on a dual-bed graphitized carbon/carbon molecular sieve adsorbent cartridge. Destruction of n-aldehydes increases with n number and with ozone concentration. In some samp...

  15. Decontamination of adsorbed chemical warfare agents on activated carbon using hydrogen peroxide solutions.

    PubMed

    Osovsky, Ruth; Kaplan, Doron; Nir, Ido; Rotter, Hadar; Elisha, Shmuel; Columbus, Ishay

    2014-09-16

    Mild treatment with hydrogen peroxide solutions (3-30%) efficiently decomposes adsorbed chemical warfare agents (CWAs) on microporous activated carbons used in protective garments and air filters. Better than 95% decomposition of adsorbed sulfur mustard (HD), sarin, and VX was achieved at ambient temperatures within 1-24 h, depending on the H2O2 concentration. HD was oxidized to the nontoxic HD-sulfoxide. The nerve agents were perhydrolyzed to the respective nontoxic methylphosphonic acids. The relative rapidity of the oxidation and perhydrolysis under these conditions is attributed to the microenvironment of the micropores. Apparently, the reactions are favored due to basic sites on the carbon surface. Our findings suggest a potential environmentally friendly route for decontamination of adsorbed CWAs, using H2O2 without the need of cosolvents or activators.

  16. Decontamination of adsorbed chemical warfare agents on activated carbon using hydrogen peroxide solutions.

    PubMed

    Osovsky, Ruth; Kaplan, Doron; Nir, Ido; Rotter, Hadar; Elisha, Shmuel; Columbus, Ishay

    2014-09-16

    Mild treatment with hydrogen peroxide solutions (3-30%) efficiently decomposes adsorbed chemical warfare agents (CWAs) on microporous activated carbons used in protective garments and air filters. Better than 95% decomposition of adsorbed sulfur mustard (HD), sarin, and VX was achieved at ambient temperatures within 1-24 h, depending on the H2O2 concentration. HD was oxidized to the nontoxic HD-sulfoxide. The nerve agents were perhydrolyzed to the respective nontoxic methylphosphonic acids. The relative rapidity of the oxidation and perhydrolysis under these conditions is attributed to the microenvironment of the micropores. Apparently, the reactions are favored due to basic sites on the carbon surface. Our findings suggest a potential environmentally friendly route for decontamination of adsorbed CWAs, using H2O2 without the need of cosolvents or activators. PMID:25133545

  17. Citrus pectin derived porous carbons as a superior adsorbent toward removal of methylene blue

    NASA Astrophysics Data System (ADS)

    Zhang, Wenlin; Zhang, Lian Ying; Zhao, Xi Juan; Zhou, Zhiqin

    2016-11-01

    An adsorbent, citrus pectin derived porous carbons with ultra-high adsorption capacity, rapid adsorption rate and good reusability toward removal of methylene blue, was synthesized by a facile zinc chloride activation approach in this study. The materials hold a great potential for treatment of dye wastewater.

  18. Carbon Nanotubes Growth on Graphite Fibers

    NASA Technical Reports Server (NTRS)

    Zhu, Shen; Su, Ching-Hua; Lehoczky, S. L.; Muntele, I.; Ila, D.; Curreri, Peter A. (Technical Monitor)

    2002-01-01

    Carbon nanotubes (CNT) were synthesized on graphite fibers by thermal Chemical Vapor Deposition (CVD). On the fiber surface, iron nanoparticles are coated and act as catalysts for CNT growth. The growth temperature ranges from 550 to 1000 C at an ambient pressure. Methane and hydrogen gases with methane contents of 10% to 100% are used for the CNT synthesis. At high growth temperatures (greater than 800 C), the rapid inter-diffusion of the transition metal iron on the graphite surface results in a rough fiber surface with no CNT grown on the surface. When the growth temperature is relatively low (650 - 800 C), CNT are fabricated on the graphite surface with catalytic particles on the nanotube top ends. Using micro Raman spectroscopy in the breath mode region, single-walled or multi-walled CNT can be determined, depending on methane concentrations.

  19. Single-walled carbon nanotubes as solid-phase microextraction adsorbent for the determination of low-level concentrations of butyltin compounds in seawater.

    PubMed

    Rastkari, Noushin; Ahmadkhaniha, Reza; Samadi, Nasrin; Shafiee, Abbas; Yunesian, Masud

    2010-03-01

    Carbon nanotubes are a kind of new carbon-based nanomaterials, which have drawn great attention in many application fields. The potential of single-walled carbon nanotubes (SWCNTs) as solid-phase microextraction (SPME) adsorbent for the preconcentration of environmental pollutants has been investigated in recent years. In the present study, the feasibility of SWCNTs as SPME adsorbent for the determination of monobutyltin, dibutyltin and tributyltin in seawater samples was studied. To achieve this aim, the potential factors affecting the SPME efficiency, including extraction time, extraction temperature, desorption time, desorption temperature, and salinity were optimized. The developed method showed good performance according to the ICH (International Conference on Harmonization of Technical Requirements for Analytical Methods) criteria. The acquired calibration curves were linear (r > or = 0.992) over the concentration range from < or = 12 to 2000 ng L(-1). For all of the analytes, the limit of detection at signal-to-noise ratio of 3 was below 5 ng L(-1). Furthermore, in comparison with the commercial carboxen/polydimethylsiloxane fiber, the developed SWCNT fiber showed better thermal stability (over 350 degrees C) and longer life span (over 150 times). The application of the proposed method in environmental analyses was shown by analyzing seawater samples from the harbors on the Persian Gulf for butyltin residues. Some of the butyltins were detected in the analyzed samples. Results of the present study demonstrate the feasibility of the SWCNTs as SPME adsorbent for the determination of butyltins in seawater samples. PMID:20152270

  20. Activated carbon fibers and engineered forms from renewable resources

    DOEpatents

    Baker, Frederick S.

    2010-06-01

    A method of producing activated carbon fibers (ACFs) includes the steps of providing a natural carbonaceous precursor fiber material, blending the carbonaceous precursor material with a chemical activation agent to form chemical agent-impregnated precursor fibers, spinning the chemical agent-impregnated precursor material into fibers, and thermally treating the chemical agent-impregnated precursor fibers. The carbonaceous precursor material is both carbonized and activated to form ACFs in a single step. The method produces ACFs exclusive of a step to isolate an intermediate carbon fiber.

  1. Activated carbon fibers and engineered forms from renewable resources

    DOEpatents

    Baker, Frederick S

    2013-02-19

    A method of producing activated carbon fibers (ACFs) includes the steps of providing a natural carbonaceous precursor fiber material, blending the carbonaceous precursor material with a chemical activation agent to form chemical agent-impregnated precursor fibers, spinning the chemical agent-impregnated precursor material into fibers, and thermally treating the chemical agent-impregnated precursor fibers. The carbonaceous precursor material is both carbonized and activated to form ACFs in a single step. The method produces ACFs exclusive of a step to isolate an intermediate carbon fiber.

  2. Production of superconductor/carbon bicomponent fibers

    NASA Technical Reports Server (NTRS)

    Wise, S. A.; Fain, C. C.; Leigh, H. D.

    1991-01-01

    Certain materials are unable to be drawn or spun into fiber form due to their improper melting characteristics or brittleness. However, fibrous samples of such materials are often necessary for the fabrication of intricate shapes and composites. In response to this problem, a unique process, referred to as the piggyback process, was developed to prepare fibrous samples of a variety of nonspinnable ceramics. In this technique, specially produced C shaped carbon fibers serve as micromolds to hold the desired materials prior to sintering. Depending on the sintering atmosphere used, bicomponent or single component fibers result. While much has been shown worldwide concerning the YBa2Cu3O(7-x) superconductor, fabrication into unique forms has proven quite difficult. However, a variety of intricate shapes are necessary for rapid commercialization of the superconducting materials. The potential for producing fibrous samples of the YBa2Cu3O(7-x) compound by the piggyback process is being studied. Various organic and acrylic materials were studied to determine suspending ability, reactivity with the YBa2Cu3O(7-x) compound during long term storage, and burn out characteristics. While many questions were answered with respect to the interfacial reactions between YBa2Cu3O(7-x) and carbon, much work is still necessary to improve the quality of the sintered material if the fibers produced are to be incorporated into useful composite or cables.

  3. Carbon nanotube and graphene nanoribbon-coated conductive Kevlar fibers.

    PubMed

    Xiang, Changsheng; Lu, Wei; Zhu, Yu; Sun, Zhengzong; Yan, Zheng; Hwang, Chi-Chau; Tour, James M

    2012-01-01

    Conductive carbon material-coated Kevlar fibers were fabricated through layer-by-layer spray coating. Polyurethane was used as the interlayer between the Kevlar fiber and carbon materials to bind the carbon materials to the Kevlar fiber. Strongly adhering single-walled carbon nanotube coatings yielded a durable conductivity of 65 S/cm without significant mechanical degradation. In addition, the properties remained stable after bending or water washing cycles. The coated fibers were analyzed using scanning electron microcopy and a knot test. The as-produced fiber had a knot efficiency of 23%, which is more than four times higher than that of carbon fibers. The spray-coating of graphene nanoribbons onto Kevlar fibers was also investigated. These flexible coated-Kevlar fibers have the potential to be used for conductive wires in wearable electronics and battery-heated armors.

  4. Determination of pressure drop across activated carbon fiber respirator cartridges.

    PubMed

    Balanay, Jo Anne G; Lungu, Claudiu T

    2016-01-01

    Activated carbon fiber (ACF) is considered as an alternative adsorbent to granular activated carbon (GAC) for the development of thinner, lighter, and efficient respirators because of their larger surface area and adsorption capacities, thinner critical bed depth, lighter weight, and fabric form. This study aims to measure the pressure drop across different types of commercially available ACFs in respirator cartridges to determine the ACF composition and density that will result in acceptably breathable respirators. Seven ACF types in cloth (ACFC) and felt (ACFF) forms were tested. ACFs in cartridges were challenged with pre-conditioned constant air flow (43 LPM, 23°C, 50% RH) at different compositions (single- or combination-ACF type) in a test chamber. Pressure drop across ACF cartridges were obtained using a micromanometer, and compared among different cartridge configurations, to those of the GAC cartridge, and to the NIOSH breathing resistance requirements for respirator cartridges. Single-ACF type cartridges filled with any ACFF had pressure drop measurements (23.71-39.93 mmH2O) within the NIOSH inhalation resistance requirement of 40 mmH2O, while those of the ACFC cartridges (85.47±3.67 mmH2O) exceeded twice the limit due possibly to the denser weaving of ACFC fibers. All single ACFF-type cartridges had higher pressure drop compared to the GAC cartridge (23.13±1.14 mmH2O). Certain ACF combinations (2 ACFF or ACFC/ACFF types) resulted to pressure drop (26.39-32.81 mmH2O) below the NIOSH limit. All single-ACFF type and all combination-ACF type cartridges with acceptable pressure drop had much lower adsorbent weights than GAC (≤15.2% of GAC weight), showing potential for light-weight respirator cartridges. 100% ACFC in cartridges may result to respirators with high breathing resistance and, thus, is not recommended. The more dense ACFF and ACFC types may still be possibly used in respirators by combining them with less dense ACFF materials and/or by

  5. Determination of pressure drop across activated carbon fiber respirator cartridges.

    PubMed

    Balanay, Jo Anne G; Lungu, Claudiu T

    2016-01-01

    Activated carbon fiber (ACF) is considered as an alternative adsorbent to granular activated carbon (GAC) for the development of thinner, lighter, and efficient respirators because of their larger surface area and adsorption capacities, thinner critical bed depth, lighter weight, and fabric form. This study aims to measure the pressure drop across different types of commercially available ACFs in respirator cartridges to determine the ACF composition and density that will result in acceptably breathable respirators. Seven ACF types in cloth (ACFC) and felt (ACFF) forms were tested. ACFs in cartridges were challenged with pre-conditioned constant air flow (43 LPM, 23°C, 50% RH) at different compositions (single- or combination-ACF type) in a test chamber. Pressure drop across ACF cartridges were obtained using a micromanometer, and compared among different cartridge configurations, to those of the GAC cartridge, and to the NIOSH breathing resistance requirements for respirator cartridges. Single-ACF type cartridges filled with any ACFF had pressure drop measurements (23.71-39.93 mmH2O) within the NIOSH inhalation resistance requirement of 40 mmH2O, while those of the ACFC cartridges (85.47±3.67 mmH2O) exceeded twice the limit due possibly to the denser weaving of ACFC fibers. All single ACFF-type cartridges had higher pressure drop compared to the GAC cartridge (23.13±1.14 mmH2O). Certain ACF combinations (2 ACFF or ACFC/ACFF types) resulted to pressure drop (26.39-32.81 mmH2O) below the NIOSH limit. All single-ACFF type and all combination-ACF type cartridges with acceptable pressure drop had much lower adsorbent weights than GAC (≤15.2% of GAC weight), showing potential for light-weight respirator cartridges. 100% ACFC in cartridges may result to respirators with high breathing resistance and, thus, is not recommended. The more dense ACFF and ACFC types may still be possibly used in respirators by combining them with less dense ACFF materials and/or by

  6. Property and Shape Modulation of Carbon Fibers Using Lasers.

    PubMed

    Blaker, Jonny J; Anthony, David B; Tang, Guang; Shamsuddin, Siti-Ros; Kalinka, Gerhard; Weinrich, Malte; Abdolvand, Amin; Shaffer, Milo S P; Bismarck, Alexander

    2016-06-29

    An exciting challenge is to create unduloid-reinforcing fibers with tailored dimensions to produce synthetic composites with improved toughness and increased ductility. Continuous carbon fibers, the state-of-the-art reinforcement for structural composites, were modified via controlled laser irradiation to result in expanded outwardly tapered regions, as well as fibers with Q-tip (cotton-bud) end shapes. A pulsed laser treatment was used to introduce damage at the single carbon fiber level, creating expanded regions at predetermined points along the lengths of continuous carbon fibers, while maintaining much of their stiffness. The range of produced shapes was quantified and correlated to single fiber tensile properties. Mapped Raman spectroscopy was used to elucidate the local compositional and structural changes. Irradiation conditions were adjusted to create a swollen weakened region, such that fiber failure occurred in the laser treated region producing two fiber ends with outwardly tapered ends. Loading the tapered fibers allows for viscoelastic energy dissipation during fiber pull-out by enhanced friction as the fibers plough through a matrix. In these tapered fibers, diameters were locally increased up to 53%, forming outward taper angles of up to 1.8°. The tensile strength and strain to failure of the modified fibers were significantly reduced, by 75% and 55%, respectively, ensuring localization of the break in the expanded region; however, the fiber stiffness was only reduced by 17%. Using harsher irradiation conditions, carbon fibers were completely cut, resulting in cotton-bud fiber end shapes. Single fiber pull-out tests performed using these fibers revealed a 6.75-fold increase in work of pull-out compared to pristine carbon fibers. Controlled laser irradiation is a route to modify the shape of continuous carbon fibers along their lengths, as well as to cut them into controlled lengths leaving tapered or cotton-bud shapes. PMID:27227575

  7. Property and Shape Modulation of Carbon Fibers Using Lasers.

    PubMed

    Blaker, Jonny J; Anthony, David B; Tang, Guang; Shamsuddin, Siti-Ros; Kalinka, Gerhard; Weinrich, Malte; Abdolvand, Amin; Shaffer, Milo S P; Bismarck, Alexander

    2016-06-29

    An exciting challenge is to create unduloid-reinforcing fibers with tailored dimensions to produce synthetic composites with improved toughness and increased ductility. Continuous carbon fibers, the state-of-the-art reinforcement for structural composites, were modified via controlled laser irradiation to result in expanded outwardly tapered regions, as well as fibers with Q-tip (cotton-bud) end shapes. A pulsed laser treatment was used to introduce damage at the single carbon fiber level, creating expanded regions at predetermined points along the lengths of continuous carbon fibers, while maintaining much of their stiffness. The range of produced shapes was quantified and correlated to single fiber tensile properties. Mapped Raman spectroscopy was used to elucidate the local compositional and structural changes. Irradiation conditions were adjusted to create a swollen weakened region, such that fiber failure occurred in the laser treated region producing two fiber ends with outwardly tapered ends. Loading the tapered fibers allows for viscoelastic energy dissipation during fiber pull-out by enhanced friction as the fibers plough through a matrix. In these tapered fibers, diameters were locally increased up to 53%, forming outward taper angles of up to 1.8°. The tensile strength and strain to failure of the modified fibers were significantly reduced, by 75% and 55%, respectively, ensuring localization of the break in the expanded region; however, the fiber stiffness was only reduced by 17%. Using harsher irradiation conditions, carbon fibers were completely cut, resulting in cotton-bud fiber end shapes. Single fiber pull-out tests performed using these fibers revealed a 6.75-fold increase in work of pull-out compared to pristine carbon fibers. Controlled laser irradiation is a route to modify the shape of continuous carbon fibers along their lengths, as well as to cut them into controlled lengths leaving tapered or cotton-bud shapes.

  8. Adsorbent materials for carbon dioxide capture from large anthropogenic point sources.

    PubMed

    Choi, Sunho; Drese, Jeffrey H; Jones, Christopher W

    2009-01-01

    Since the time of the industrial revolution, the atmospheric CO(2) concentration has risen by nearly 35 % to its current level of 383 ppm. The increased carbon dioxide concentration in the atmosphere has been suggested to be a leading contributor to global climate change. To slow the increase, reductions in anthropogenic CO(2) emissions are necessary. Large emission point sources, such as fossil-fuel-based power generation facilities, are the first targets for these reductions. A benchmark, mature technology for the separation of dilute CO(2) from gas streams is via absorption with aqueous amines. However, the use of solid adsorbents is now being widely considered as an alternative, potentially less-energy-intensive separation technology. This Review describes the CO(2) adsorption behavior of several different classes of solid carbon dioxide adsorbents, including zeolites, activated carbons, calcium oxides, hydrotalcites, organic-inorganic hybrids, and metal-organic frameworks. These adsorbents are evaluated in terms of their equilibrium CO(2) capacities as well as other important parameters such as adsorption-desorption kinetics, operating windows, stability, and regenerability. The scope of currently available CO(2) adsorbents and their critical properties that will ultimately affect their incorporation into large-scale separation processes is presented.

  9. Carbon fiber-reinforced carbon as a potential implant material.

    PubMed

    Adams, D; Williams, D F; Hill, J

    1978-01-01

    A carbon fiber-reinforced carbon is being evaluated as a promising implant material. In a unidirectional composite, high strengths (1200 MN/m2 longitudinal flexural strength) and high modulus (140 GN/m2 flexural modulus) may be obtained with an interlaminar shear strength of 18 MN/m2. Alternatively, layers of fibers may be laid in two directions to give more isotopic properties. The compatibility of the material with bone has been studied by implanting specimens in holes drilled in rat femora. For a period of up to 8 weeks, a thin layer of fibrous tissue bridged the gap between bone and implant; but this tissue mineralizes and by 10 weeks, bone can be observed adjacent to the implant, giving firm fixation. Potential applications include endosseous dental implants where a greater strength in the neck than that provided by unreinforced carbon would be advantageous.

  10. Aqueous phase adsorption of different sized molecules on activated carbon fibers: Effect of textural properties.

    PubMed

    Prajapati, Yogendra N; Bhaduri, Bhaskar; Joshi, Harish C; Srivastava, Anurag; Verma, Nishith

    2016-07-01

    The effect that the textural properties of rayon-based activated carbon fibers (ACFs), such as the BET surface area and pore size distribution (PSD), have on the adsorption of differently sized molecules, namely, brilliant yellow (BY), methyl orange (MO) and phenol (PH), was investigated in the aqueous phase. ACF samples with different BET areas and PSDs were produced by steam-activating carbonized fibers for different activation times (0.25, 0.5, and 1 h). The samples activated for 0.25 h were predominantly microporous, whereas those activated for relatively longer times contained hierarchical micro-mesopores. The adsorption capacities of the ACFs for the adsorbate increased with increasing BET surface area and pore volume, and ranged from 51 to 1306 mg/g depending on the textural properties of the ACFs and adsorbate size. The adsorption capacities of the hierarchical ACF samples followed the order BY > MO > PH. Interestingly, the number of molecules adsorbed by the ACFs followed the reverse order: PH > MO > BY. This anomaly was attributed to the increasing molecular weight of the PH, MO and BY molecules. The equilibrium adsorption data were described using the Langmuir isotherm. This study shows that suitable textural modifications to ACFs are required for the efficient aqueous phase removal of an adsorbate. PMID:27107386

  11. Aqueous phase adsorption of different sized molecules on activated carbon fibers: Effect of textural properties.

    PubMed

    Prajapati, Yogendra N; Bhaduri, Bhaskar; Joshi, Harish C; Srivastava, Anurag; Verma, Nishith

    2016-07-01

    The effect that the textural properties of rayon-based activated carbon fibers (ACFs), such as the BET surface area and pore size distribution (PSD), have on the adsorption of differently sized molecules, namely, brilliant yellow (BY), methyl orange (MO) and phenol (PH), was investigated in the aqueous phase. ACF samples with different BET areas and PSDs were produced by steam-activating carbonized fibers for different activation times (0.25, 0.5, and 1 h). The samples activated for 0.25 h were predominantly microporous, whereas those activated for relatively longer times contained hierarchical micro-mesopores. The adsorption capacities of the ACFs for the adsorbate increased with increasing BET surface area and pore volume, and ranged from 51 to 1306 mg/g depending on the textural properties of the ACFs and adsorbate size. The adsorption capacities of the hierarchical ACF samples followed the order BY > MO > PH. Interestingly, the number of molecules adsorbed by the ACFs followed the reverse order: PH > MO > BY. This anomaly was attributed to the increasing molecular weight of the PH, MO and BY molecules. The equilibrium adsorption data were described using the Langmuir isotherm. This study shows that suitable textural modifications to ACFs are required for the efficient aqueous phase removal of an adsorbate.

  12. Utilization of granular activated carbon adsorber for nitrates removal from groundwater of the Cluj region.

    PubMed

    Moşneag, Silvia C; Popescu, Violeta; Dinescu, Adrian; Borodi, George

    2013-01-01

    The level of nitrates from groundwater from Cluj County and other areas from Romania have increased values, exceeding or getting close to the allowed limit values, putting in danger human and animal heath. In this study we used granular activated carbon adsorbent (GAC) for nitrate (NO(-)3) removal for the production of drinking water from groundwater of the Cluj county. The influences of the contact time, nitrate initial concentration, and adsorbent concentration have been studied. We determined the equilibrium adsorption capacity of GAC, used for NO(-)3 removal and we applied the Langmuir and Freundlich isotherm models. Ultraviolet-visible (UV-Vis) and Fourier transform infrared (FTIR) spectroscopy, X ray diffraction (XRD), Scanning Electron Microscopy (SEM) were used for process characterization. We also determined: pH, conductivity, Total Dissolved Solids and Total Hardness. The GAC adsorbents have excellent capacities of removing nitrate from groundwater from Cluj County areas.

  13. Waste polyvinylchloride derived pitch as a precursor to develop carbon fibers and activated carbon fibers.

    PubMed

    Qiao, W M; Yoon, S H; Mochida, I; Yang, J H

    2007-01-01

    Polyvinylchloride (PVC) was successfully recycled through the solvent extraction from waste pipe with an extraction yield of ca. 86%. The extracted PVC was pyrolyzed by a two-stage process (260 and 410 degrees C) to obtain free-chlorine PVC based pitch through an effective removal of chlorine from PVC during the heat-treatment. As-prepared pitch (softening point: 220 degrees C) was spun, stabilized, carbonized into carbon fibers (CFs), and further activated into activated carbon fibers (ACFs) in a flow of CO2. As-prepared CFs show comparable mechanical properties to commercial CFs, whose maximum tensile strength and modulus are 862 MPa and 62 GPa, respectively. The resultant ACFs exhibit a high surface area of 1200 m2/g, narrow pore size distribution and a low oxygen content of 3%. The study provides an effective insight to recycle PVC from waste PVC and develop a carbon precursor for high performance carbon materials such as CFs and ACFs.

  14. Activation and micropore structure determination of activated carbon-fiber composites

    SciTech Connect

    Jagtoyen, M.; Derbyshire, F.; Kimber, G.

    1997-09-05

    Rigid, high surface area activated carbon fiber composites have been produced with high permeabilities for environmental applications in gas and water purification. These novel monolithic adsorbents can be produced in single pieces to a given size and shape. The project involves a collaboration between the Oak Ridge National Laboratory (ORNL) and the Center for Applied Energy Research (CAER), University of Kentucky. The carbon fiber composites are produced at the ORNL and activated at the CAER using different methods, with the aims of producing a uniform degree of activation, and of closely controlling pore structure and adsorptive properties. The main focus of the present work has been to find a satisfactory means to uniformly activate large samples of carbon fiber composites and produce controlled pore structures. Several environmental applications have been explored for the activated carbon fiber composites. One of these was to evaluate the activated composites for the separation of CH{sub 4}-CO{sub 2} mixtures, and an apparatus was constructed specifically for this purpose. The composites were further evaluated in the cyclic recovery of volatile organics. The activated carbon fiber composites have also been tested for possible water treatment applications by studying the adsorption of sodium pentachlorophenolate, PCP.

  15. Carbon molecular sieves for air separation from Nomex aramid fibers.

    PubMed

    Villar-Rodil, Silvia; Martínez-Alonso, Amelia; Tascón, Juan M D

    2002-10-15

    Activated carbon fibers prepared from aramid fibers have proved to possess outstanding homogeneity in pore size, most of all when Nomex aramid fiber is used as precursor. Taking advantage of this feature, microporous carbon molecular sieves for air separation have been prepared through carbon vapor deposition of benzene on Nomex-derived carbon fibers activated to two different burnoff degrees. Carbon molecular sieves with good selectivity for this separation and showing acceptable adsorption capacities were obtained from ACFs activated to the two burnoff degrees chosen. PMID:12702417

  16. Study on Adsorption Process of Ethanol Vapor to Activated Carbon Fibers

    NASA Astrophysics Data System (ADS)

    Kariya, Keishi; I. I., El-Sharkawy; Suda, Keisuke; B. B., Saha; Kuwahara, Ken; Koyama, Shigeru

    Performance enhancement of adsorption cooling system has been required for commercial use. Therefore, revealing details of adsorption phenomena are important for optimizing adsorber/desorber heat exchanger which is the bottle-neck of the system. This study deals with the experimental investigation of ethanol vapor adsorption on activated carbon fiber (ACF) under equilibrium condition along with one-dimensional transient numerical simulation of heat and mass transfer in the adsorbent bed is also performed. In order to suggest optimizing method for performance improvement, the present study considered the relationships between cooling capacity and system performance inducing parameters, such as cooling water temperature, ACF height and apparent density in the simulation model. Simulation results agreed well with the experimental data and it is found that the cooling capacity can be enhanced by optimizing ACF bed thickness. Simulation results also shows that the temperatures of adsorber and evaporator do not have significant effects on the optimum adsorption cycle time.

  17. Oxygen Reactivity of a Carbon Fiber Composite

    SciTech Connect

    Marshall, Theron Devol; Pawelko, Robert James; Anderl, Robert Andrew; Smolik, Galen Richard

    2002-09-01

    Carbon Fiber Composites (CFCs) are often suggested as armor material for the first wall of a fusion plasma chamber due to carbon's low atomic number, high thermal conductivity, and high melting point. However, carbon is chemically reactive in air and will react with ingress air during a Loss of Vacuum Accident and release tritium fuel that has been retained in the carbon. Tritium mobilization and carbon monoxide generation via CFC oxidation are both safety concerns. This paper discusses chemical reactivity experiments that were performed using the state-of-the-art 3-dimensional NB31 CFC produced by SNECMA and a laminar reaction gas of Ar–21 vol% O2. Oxidation reaction rates were measured for CFC temperatures of 525, 600, 700, 800, 900, and 1000 °C and a 100 standard cubic centimeters per minute (sccm) Ar–O2 flow rate. Experiments were also performed at CFC temperatures of 700 and 1000 °C and a 1000 sccm Ar–O2 flow rate. Mass spectral analyses of the exhaust reaction gas suggested that carbon monoxide was the primary reaction at the CFC surface and carbon dioxide was readily produced in the exiting reaction gas. The measured reaction rates compare well with the literature and were used to produce a CFC oxidation curve that is recommended for use in fusion safety analyses.

  18. Lignin-based microporous materials as selective adsorbents for carbon dioxide separation.

    PubMed

    Meng, Qing Bo; Weber, Jens

    2014-12-01

    Suitable solid adsorbents are demanded for carbon capture and storage (CCS) processes. In this work, a novel microporous polymer is developed by hypercrosslinking of organosolv lignin, which is a renewable resource. Reaction with formaldehyde dimethyl acetal (FDA) via Friedel-Crafts reaction gives microporous networks, with moderate capacity of carbon dioxide but excellent selectivity towards CO2 /N2 mixture as predicted on the basis of ideal adsorption-solution theory (IAST). Pyrolysis of pure organosolv lignin results in microporous carbon powders, while pyrolysis of hypercrosslinked organosolv lignin yields shape-persistent materials with increased CO2 capacity while maintaining very good selectivity.

  19. Visualization and Measurement of Adsorption/Desorption Process of Ethanol in Activated Carbon Adsorber

    NASA Astrophysics Data System (ADS)

    Asano, Hitoshi; Murata, Kenta; Takenaka, Nobuyuki; Saito, Yasushi

    Adsorption refrigerator is one of the efficient tools for waste heat recovery, because the system is driven by heat at relative low temperature. However, the coefficient of performance is low due to its batch operation and the heat capacity of the adsorber. In order to improve the performance, it is important to optimize the configuration to minimize the amount of driving heat, and to clarify adsorption/desorption phenomena in transient conditions. Neutron radiography was applied to visualize and measure the adsorption amount distribution in an adsorber. The visualization experiments had been performed at the neutron radiography facility of E-2 port of Kyoto University Research Reactor. Activated carbon and ethanol were used as the adsorbent and refrigerant. From the acquired radiographs, adsorption amount was quantitatively measured by applying the umbra method using a checkered neutron absorber with boron powder. Then, transient adsorption and desorption processes of a rectangular adsorber with 84 mm in width, 50 mm in height and 20 mm in depth were visualized. As the result, the effect of fins in the adsorbent layer on the adsorption amount distribution was clearly visualized.

  20. Contribution to the evaluation of density of methane adsorbed on activated carbon.

    PubMed

    Rodríguez-Reinoso, Francisco; Almansa, Cristina; Molina-Sabio, Miguel

    2005-11-01

    The adsorption isotherms of N(2) at -196 degrees C, CO(2) at 0 degrees C, and CH(4) at 25 degrees C on 35 activated carbons with a wide range of micropore volumes and pore size distributions have been compared to evaluate the density of adsorbed methane. Results indicate that methane is adsorbed in the micropores of the activated carbon with a density that is a function of the carbon porosity because methane is packed more compactly in narrow than in wide micropores. An experimental procedure is proposed to evaluate the density in both types of micropores as a function of pressure. Its application to these porous carbons indicates that density of adsorbed methane increases rapidly with pressure on narrow micropores, the increase becoming slower above 1.5 MPa. The value reached at 3 MPa is 0.21 g/cm(3), near that estimated as the limiting value, 0.23 g/cm(3). Density in wide micropores is low, 0.09 g/cm(3) at 3 MPa, but it continuously increases with pressure.

  1. Liquid-phase adsorption of organic compounds by granular activated carbon and activated carbon fibers

    SciTech Connect

    Lin, S.H.; Hsu, F.M.

    1995-06-01

    Liquid-phase adsorption of organic compounds by granular activated carbon (GAC) and activated carbon fibers (ACFs) is investigated. Acetone, isopropyl alcohol (IPA), phenol, and tetrahydrofuran (THF) were employed as the model compounds for the present study. It is observed from the experimental results that adsorption of organic compounds by GAC and ACF is influenced by the BET (Brunauer-Emmett-Teller) surface area of adsorbent and the molecular weight, polarity, and solubility of the adsorbate. The adsorption characteristics of GAC and ACFs were found to differ rather significantly. In terms of the adsorption capacity of organic compounds, the time to reach equilibrium adsorption, and the time for complete desorption, ACFs have been observed to be considerably better than GAC. For the organic compounds tested here, the GAC adsorptions were shown to be represented well by the Langmuir isotherm while the ACF adsorption could be adequately described by the Langmuir or the Freundlich isotherm. Column adsorption tests indicated that the exhausted ACFs can be effectively regenerated by static in situ thermal desorption at 150 C, but the same regeneration conditions do not do as well for the exhausted GAC.

  2. Electronic equipment vulnerability to fire released carbon fibers

    NASA Technical Reports Server (NTRS)

    Pride, R. A.; Mchatton, A. D.; Musselman, K. A.

    1980-01-01

    The vulnerability of electronic equipment to damage by carbon fibers released from burning aircraft type structural composite materials was investigated. Tests were conducted on commercially available stereo power amplifiers which showed that the equipment was damaged by fire released carbon fibers but not by the composite resin residue, soot and products of combustion of the fuel associated with burning the carbon fiber composites. Results indicate that the failure rates of the equipment exposed to the fire released fiber were consistent with predictions based on tests using virgin fibers.

  3. Vibration damping with active carbon fiber structures

    NASA Astrophysics Data System (ADS)

    Neugebauer, Reimund; Kunze, Holger; Riedel, Mathias; Roscher, Hans-Jürgen

    2007-04-01

    This paper presents a mechatronic strategy for active reduction of vibrations on machine tool struts or car shafts. The active structure is built from a carbon fiber composite with embedded piezofiber actuators that are composed of piezopatches based on the Macro Fiber Composite (MFC) technology, licensed by NASA and produced by Smart Material GmbH in Dresden, Germany. The structure of these actuators allows separate or selectively combined bending and torsion, meaning that both bending and torsion vibrations can be actively absorbed. Initial simulation work was done with a finite element model (ANSYS). This paper describes how state space models are generated out of a structure based on the finite element model and how controller codes are integrated into finite element models for transient analysis and the model-based control design. Finally, it showcases initial experimental findings and provides an outlook for damping multi-mode resonances with a parallel combination of resonant controllers.

  4. Production of superconductor/carbon bicomponent fibers

    NASA Technical Reports Server (NTRS)

    Wise, S. A.; Fain, C. C.; Leigh, H. D.; Sherrill, M.

    1990-01-01

    Certain materials are unable to be drawn or spun into fiber form due to their improper melting characteristics or brittleness. However, fibrous samples of such materials are often necessary for the fabrication of intricate shapes and composites. In response to this problem, a unique process, referred to as the piggyback process, was developed to prepare fibrous samples of a variety of nonspinnable ceramics. In this technique, specially produced C-shaped carbon fibers serve as micromolds to hold the desired materials prior to sintering. Depending on the sintering atmosphere used, bicomponent or single component fibers result. While much has been demonstrated worldwide concerning the YBa2Cu3O(7-x) superconductor, fabrication into unique forms has proven quite difficult. However, a variety of intricate shapes are necessary for rapid commercialization of the superconducting materials. The potential for producing fibrous samples of the YBa2Cu3O(7-x) compound by the piggyback process is being investigated. Various organic and acrylic materials were investigated to determine suspending ability, reactivity with the YBa2Cu3O(7-x) compound during long term storage, and burn out characteristics. While many questions were answered with respect to the interfacial reactions between YBa2Cu3O(7-x) and carbon, much work is still necessary to improve the quality of the sintered material if the fibers produced are to be incorporated into useful composites or cables. Additional research is necessary to evaluate quality of the barrier layer during long soakings at the peak temperature; adjust the firing schedule to avoid microcracking and improve densification; and increase the solids loading in the superconductive suspension to decrease porosity.

  5. Designed amyloid fibers as materials for selective carbon dioxide capture.

    PubMed

    Li, Dan; Furukawa, Hiroyasu; Deng, Hexiang; Liu, Cong; Yaghi, Omar M; Eisenberg, David S

    2014-01-01

    New materials capable of binding carbon dioxide are essential for addressing climate change. Here, we demonstrate that amyloids, self-assembling protein fibers, are effective for selective carbon dioxide capture. Solid-state NMR proves that amyloid fibers containing alkylamine groups reversibly bind carbon dioxide via carbamate formation. Thermodynamic and kinetic capture-and-release tests show the carbamate formation rate is fast enough to capture carbon dioxide by dynamic separation, undiminished by the presence of water, in both a natural amyloid and designed amyloids having increased carbon dioxide capacity. Heating to 100 °C regenerates the material. These results demonstrate the potential of amyloid fibers for environmental carbon dioxide capture.

  6. The Impact of Adsorbed Triethylene Glycol on Water Wettability of the {1014} Calcium Carbonate Surface

    NASA Astrophysics Data System (ADS)

    Olsen, R.

    2015-12-01

    Water flooding is increasingly being used as a method of enhanced oil recovery and frequently involves calcium carbonate reservoirs. Very often, thermodynamic conditions in the upper few hundred meters allow for hydrate formation. One possible method of preventing hydrates is to inject hydrate inhibitors such as triethylene glycol (TEG) into the reservoir. Thus, it is of importance to know how such glycols affect water wettability, which is an important factor defining the oil behavior in such reservoirs. Wettability of a surface is defined by the contact angle of a liquid drop on the surface. The stronger the liquid is attracted to the surface, the smaller the wetting angle becomes, implying an increased degree of wetting. Therefore, it is possible to gain qualitative knowledge of the change in wetting properties with respect to external influences by studying corresponding changes in free energy of adsorption of the liquid. In our work [1], we used molecular dynamics (MD) and Born-Oppenheimer molecular dynamics (BOMD) to study how adsorbed TEG on the {1014} calcium carbonate surface affected adsorbed water. We used the changes in density profiles of water to estimate changes in adsorption free energy of water. The adaptive biasing force (ABF) method was applied to TEG to calculate the adsorption free energy of TEG on the calcium carbonate surface. We found that water wetting of the calcium carbonate surface decreased in the presence of adsorbed TEG. [1] - Olsen, R.; Leirvik, K.; Kvamme, B.; Kuznetsova, T. Adsorption Properties of Triethylene Glycol on a Hydrated {1014} Calcite Surface and Its Effect on Adsorbed Water, Langmuir 2015, DOI: 10.1021/acs.langmuir.5b02228

  7. Voltammetric detection of biological molecules using chopped carbon fiber.

    PubMed

    Sugawara, Kazuharu; Yugami, Asako; Kojima, Akira

    2010-01-01

    Voltammetric detection of biological molecules was carried out using chopped carbon fibers produced from carbon fiber reinforced plastics that are biocompatible and inexpensive. Because chopped carbon fibers normally are covered with a sizing agent, they are difficult to use as an electrode. However, when the surface of a chopped carbon fiber was treated with ethanol and hydrochloric acid, it became conductive. To evaluate the functioning of chopped carbon fibers, voltammetric measurements of [Fe(CN)(6)](3-) were carried out. Redoxes of FAD, ascorbic acid and NADH as biomolecules were recorded using cyclic voltammetry. The sizing agents used to bundle the fibers were epoxy, polyamide and polyurethane resins. The peak currents were the greatest when using the chopped carbon fibers that were created with epoxy resins. When the electrode response of the chopped carbon fibers was compared with that of a glassy carbon electrode, the peak currents and the reversibility of the electrode reaction were sufficient. Therefore, the chopped carbon fibers will be useful as disposable electrodes for the sensing of biomolecules. PMID:20953048

  8. Polarization dependence of laser interaction with carbon fibers and CFRP.

    PubMed

    Freitag, Christian; Weber, Rudolf; Graf, Thomas

    2014-01-27

    A key factor for laser materials processing is the absorptivity of the material at the laser wavelength, which determines the fraction of the laser energy that is coupled into the material. Based on the Fresnel equations, a theoretical model is used to determine the absorptivity for carbon fiber fabrics and carbon fiber reinforced plastics (CFRP). The surface of each carbon fiber is considered as multiple layers of concentric cylinders of graphite. With this the optical properties of carbon fibers and their composites can be estimated from the well-known optical properties of graphite.

  9. Voltammetric detection of biological molecules using chopped carbon fiber.

    PubMed

    Sugawara, Kazuharu; Yugami, Asako; Kojima, Akira

    2010-01-01

    Voltammetric detection of biological molecules was carried out using chopped carbon fibers produced from carbon fiber reinforced plastics that are biocompatible and inexpensive. Because chopped carbon fibers normally are covered with a sizing agent, they are difficult to use as an electrode. However, when the surface of a chopped carbon fiber was treated with ethanol and hydrochloric acid, it became conductive. To evaluate the functioning of chopped carbon fibers, voltammetric measurements of [Fe(CN)(6)](3-) were carried out. Redoxes of FAD, ascorbic acid and NADH as biomolecules were recorded using cyclic voltammetry. The sizing agents used to bundle the fibers were epoxy, polyamide and polyurethane resins. The peak currents were the greatest when using the chopped carbon fibers that were created with epoxy resins. When the electrode response of the chopped carbon fibers was compared with that of a glassy carbon electrode, the peak currents and the reversibility of the electrode reaction were sufficient. Therefore, the chopped carbon fibers will be useful as disposable electrodes for the sensing of biomolecules.

  10. Surface area of vermiculite with nitrogen and carbon dioxide as adsorbates

    USGS Publications Warehouse

    Thomas, J.; Bohor, B.F.

    1969-01-01

    Surface-area studies were made on several homoionic vermiculites with both nitrogen and carbon dioxide as adsorbates. These studies show that only very slight penetration occurs between individual vermiculite platelets. This is in contrast to an earlier investigation of montmorillonite where it was found that the degree of penetration between layers is quite high, particularly for carbon dioxide, and is governed by the size and charge of the interlayer cation. The inability of these adsorbates to penetrate substantially between vermiculite platelets is due primarily to this mineral's high surface-charge density. The extent of penetration of nitrogen and carbon dioxide at the edges of vermiculite platelets, though slight, is influenced by the coordinated water retained within the sample at a given degassing temperature. Forces between layers are weakened with increasing water content, which permits slightly greater penetration by adsorbate gases. Thus, the surface area of vermiculite, as determined by gas adsorption, is larger than the calculated external surface area based upon particle size and shape considerations. In addition, "extra" surface is provided by the lifting and scrolling of terminal platelets. These morphological features are shown in scanning electron micrographs of a naturally occuring vermiculite. ?? 1969.

  11. Radiation effects on carbon fiber reinforced thermoplastics

    SciTech Connect

    Sasuga, Tsuneo; Udagawa, Akira; Seguchi, Tadao

    1993-12-31

    Polyether-ether-ketone (PEEK) and a newly developed thermoplastic polyimide ``new-TPI`` were applied to carbon fiber reinforced plastic (CFRP) as a matrix resin. PEEK and new-TPI showed excellent resistance over 50 MGy to electron irradiation and the crosslinking proceeded predominantly by irradiation. The changes in mechanical properties induced by electron irradiation of the CFRP with the two resins were examined at various temperatures. The flexural strength and modulus measured at {minus}196 and 25{degree}C were scarcely affected up to 120 MGy and both the values measured at high temperature were increased with dose.

  12. A fiber optics system for monitoring utilization of ZnO adsorbent beds during desulfurization for logistic fuel cell applications

    NASA Astrophysics Data System (ADS)

    Sujan, Achintya; Yang, Hongyun; Dimick, Paul; Tatarchuk, Bruce J.

    2016-05-01

    An in-situ fiber optic based technique for direct measurement of capacity utilization of ZnO adsorbent beds by monitoring bed color changes during desulfurization for fuel cell systems is presented. Adsorbents composed of bulk metal oxides (ZnO) and supported metal oxides (ZnO/SiO2 and Cusbnd ZnO/SiO2) for H2S removal at 22 °C are examined. Adsorbent bed utilization at breakthrough is determined by the optical sensor as the maximum derivative of area under UV-vis spectrum from 250 to 800 nm observed as a function of service time. Since the response time of the sensor due to bed color change is close to bed breakthrough time, a series of probes along the bed predicts utilization of the portion of bed prior to H2S breakthrough. The efficacy of the optical sensor is evaluated as a function of inlet H2S concentration, H2S flow rate and desulfurization in presence of CO, CO2 and moisture in feed. A 6 mm optical probe is employed to measure utilization of a 3/16 inch ZnO extrudate bed for H2S removal. It is envisioned that with the application of the optical sensor, desulfurization can be carried out at high adsorbent utilization and low operational costs during on-board miniaturized fuel processing for logistic fuel cell power systems.

  13. Carbon fibers from electrospun polymeric phenolic resin precursors

    NASA Astrophysics Data System (ADS)

    Gee, Diane L.

    This dissertation presents a technique for producing carbon fibers of nano- to micro-sized dimension by utilizing a non-conventional fiber spinning approach with refractory polymers, followed by post-processing steps, to create new carbon materials with distinctive chemical/physical property characteristics. Phenolic resins, novolak and resole, are selected for this study because of their low cost, marketability, environmental friendliness, and high char yield upon pyrolysis. The new carbon fibers are at least an order of magnitude smaller than their conventionally processed counterpart, and possess significant advantages. Phenolic resin fibers, consisting of a blend of novolak and resole, are generated via electrospinning and are subsequently cured and pyrolyzed at temperatures from 800°C to 2000°C to form carbon fibers having diameters of ˜1 mum. Fiber analysis by scanning electron microscopy confirms that the morphology generated during the electrospinning processing is retained throughout the curing and carbonization processes. X-ray diffraction suggests the presence of highly graphitized carbon, which is further validated by high-resolution transmission electron microscopy (HRTEM) analysis. There is evidence of crystalline graphite, which may have nucleated on aligned sheets presence on the fiber surface. The physical characteristics of electrospun fibers are contrary to those exhibited by pyrolyzed phenolic resins, which fall into the classification of non-graphitizing. It is likely that the thin electrospun fibers offer a template that encourages ordering not usually seen in thicker fibers or bulk samples of carbonized phenolic resins.

  14. On the nature of interface of carbon nanotube coated carbon fibers with different polymers

    NASA Astrophysics Data System (ADS)

    Singh Bedi, Harpreet; Padhee, Srikant S.; Agnihotri, Prabhat K.

    2016-07-01

    Experimental investigations are carried out to analyse the wetting behaviour of carbon nanotube (CNT) coated carbon fiber to determine their suitability to process carbon nanotube coated carbon fiber/polymer multiscale composites for structural applications. To overcome the problem of agglomeration, CNTs are grown directly on the surface of carbon fibers as well as fabric using thermal chemical vapour deposition (CVD) technique. The term multiscale is used because different reinforcement mechanisms operate at the scale of long fibers and CNTs which are of few micrometers in length. The load carrying capacity of these multiscale composites critically depends on the efficiency and extent of load transfer from low strength matrix to high strength fiber which in turn depends on the interfacial strength between CNT coated carbon fiber and polymer matrix. A systematic analysis of wetting behaviour of CNT coated carbon fiber with epoxy and polyester matrix is carried out in this study. It is shown that CNT coated carbon fibers as well as fabric show better wettability with epoxy matrix as compared to polyester matrix. This results in stronger interface of CNT coated carbon fiber with epoxy as compared to polyester in multiscale composite system. A similar observation is made in nanoindentation testing of single fiber multiscale composites processed with epoxy and polyester matrix. In addition, it is observed that wettability, interfacial strength and average properties of CNT coated carbon fiber/polymer composites are a function of CNT density on the surface of carbon fibers.

  15. Hollow mesoporous carbon spheres with magnetic cores and their performance as separable bilirubin adsorbents.

    PubMed

    Guo, Limin; Cui, Xiangzhi; Li, Yongsheng; He, Qianjun; Zhang, Lingxia; Bu, Wenbo; Shi, Jianlin

    2009-09-01

    Hollow mesoporous carbon spheres with magnetic cores are directly replicated from hollow mesoporous aluminosilicate spheres with hematite cores by a simple incipient-wetness impregnation technique. The amount of magnetic cores and the saturation magnetization value can be easily tuned by changing the concentration of iron nitrate solution used in the synthesis procedure. As-prepared hollow mesoporous carbon spheres with magnetic cores are used as separable bilirubin adsorbents and show very good adsorptive properties. The characteristics of as-prepared composites are examined by XRD, N(2) sorption, TEM, vibrating-sample magnetometry, and UV/Vis spectroscopy. PMID:19582733

  16. Oxidized multiwalled carbon nanotubes as adsorbent for the removal of manganese from aqueous solution.

    PubMed

    Ganesan, Pandian; Kamaraj, Ramakrishnan; Sozhan, Ganapathy; Vasudevan, Subramanyan

    2013-02-01

    A batch adsorption process was applied to investigate the removal of manganese from aqueous solution by oxidized multiwalled carbon nanotubes (MWCNTs). In doing so, the thermodynamic, adsorption isotherm, and kinetic studies were also carried out. MWCNT with 5-10-nm outer diameter, surface area of 40-600 m(2)/g, and purity above 95 % was used as an adsorbent. A systematic study of the adsorption process was performed by varying pH, ionic strength, and temperature. Manganese-adsorbed MWCNT was characterized by Raman, FTIR, X-ray diffraction, XPS, SEM, and TEM. The adsorption efficiency could reach 96.82 %, suggesting that MWCNT is an excellent adsorbent for manganese removal from water. The results indicate that second-order kinetics model was well suitable to model the kinetic adsorption of manganese. Equilibrium data were well described by the typical Langmuir adsorption isotherm. Thermodynamic studies revealed that the adsorption reaction was spontaneous and endothermic process. The experimental results showed that MWCNT is an excellent manganese adsorbent. The MWCNTs removed the manganese present in the water and reduced it to a permissible level making it drinkable.

  17. Fluoride removal in water by a hybrid adsorbent lanthanum-carbon.

    PubMed

    Vences-Alvarez, Esmeralda; Velazquez-Jimenez, Litza Halla; Chazaro-Ruiz, Luis Felipe; Diaz-Flores, Paola E; Rangel-Mendez, Jose Rene

    2015-10-01

    Various health problems associated with drinking water containing high fluoride levels, have motivated researchers to develop more efficient adsorbents to remove fluoride from water for beneficial concentrations to human health. The objective of this research was to anchor lanthanum oxyhydroxides on a commercial granular activated carbon (GAC) to remove fluoride from water considering the effect of the solution pH, and the presence of co-existing anions and organic matter. The activated carbon was modified with lanthanum oxyhydroxides by impregnation. SEM and XRD were performed in order to determine the crystal structure and morphology of the La(III) particles anchored on the GAC surface. FT-IR and pK(a)'s distribution were determined in order to elucidate both the possible mechanism of the lanthanum anchorage on the activated carbon surface and the fluoride adsorption mechanism on the modified material. The results showed that lanthanum ions prefer binding to carboxyl and phenolic groups on the activated carbon surface. Potentiometric titrations revealed that the modified carbon (GAC-La) possesses positive charge at a pH lower than 9. The adsorption capacity of the modified GAC increased five times in contrast to an unmodified GAC adsorption capacity at an initial F(-) concentration of 20 mg L(-1). Moreover, the presence of co-existing anions had no effect on the fluoride adsorption capacity at concentrations below 30 mg L(-1), that indicated high F(-) affinity by the modified adsorbent material (GAG-La).

  18. Fluoride removal in water by a hybrid adsorbent lanthanum-carbon.

    PubMed

    Vences-Alvarez, Esmeralda; Velazquez-Jimenez, Litza Halla; Chazaro-Ruiz, Luis Felipe; Diaz-Flores, Paola E; Rangel-Mendez, Jose Rene

    2015-10-01

    Various health problems associated with drinking water containing high fluoride levels, have motivated researchers to develop more efficient adsorbents to remove fluoride from water for beneficial concentrations to human health. The objective of this research was to anchor lanthanum oxyhydroxides on a commercial granular activated carbon (GAC) to remove fluoride from water considering the effect of the solution pH, and the presence of co-existing anions and organic matter. The activated carbon was modified with lanthanum oxyhydroxides by impregnation. SEM and XRD were performed in order to determine the crystal structure and morphology of the La(III) particles anchored on the GAC surface. FT-IR and pK(a)'s distribution were determined in order to elucidate both the possible mechanism of the lanthanum anchorage on the activated carbon surface and the fluoride adsorption mechanism on the modified material. The results showed that lanthanum ions prefer binding to carboxyl and phenolic groups on the activated carbon surface. Potentiometric titrations revealed that the modified carbon (GAC-La) possesses positive charge at a pH lower than 9. The adsorption capacity of the modified GAC increased five times in contrast to an unmodified GAC adsorption capacity at an initial F(-) concentration of 20 mg L(-1). Moreover, the presence of co-existing anions had no effect on the fluoride adsorption capacity at concentrations below 30 mg L(-1), that indicated high F(-) affinity by the modified adsorbent material (GAG-La). PMID:26070190

  19. Experimental Behavior of Carbon Fiber Reinforced Isolators

    SciTech Connect

    Russo, Gaetano; Pauletta, Margherita; Cortesia, Andrea; Dal Bianco, Alberto

    2008-07-08

    This paper describes an investigation on the experimental behavior of innovative elastomeric isolators reinforced by carbon fiber fabrics. These fabrics are very much lighter than steel plates used in conventional isolators and able to transfer to the adjacent elastomer layers tangential stresses adequate to oppose the transversal deformation of rubber under vertical loads. The isolators are not bonded to the sub- and super-structure (elimination of the steel end-plates), hence their weight and cost are reduced. The experimental investigation is carried out on small-scale isolator prototypes reinforced by quadridirectional carbon fiber fabrics. The isolators are subjected to the following qualification tests prescribed by the Italian Code 'Ordinanza 3274' for steel reinforced isolators: 1) 'Static assessment of the compression stiffness'; 2) 'Static assessment of the shear modulus G'; 3) 'Dynamic assessment of the dynamic shear modulus G{sub din} and of the damping coefficient {xi}; 4) 'Assessment of the G{sub din}-{gamma} and {xi}-{gamma} diagrams by means of dynamic tests'; 5) 'Assessment of creep characteristics'; 6) 'Evaluation of the capacity of sustaining at least 10 cycles'. As a result of the tests, the isolators survived large shear strains, comparable to those expected for conventional isolators.

  20. Liquid crystal polyester-carbon fiber composites

    NASA Technical Reports Server (NTRS)

    Chung, T. S.

    1984-01-01

    Liquid crystal polymers (LCP) have been developed as a thermoplastic matrix for high performance composites. A successful melt impregnation method has been developed which results in the production of continuous carbon fiber (CF) reinforced LCP prepreg tape. Subsequent layup and molding of prepreg into laminates has yielded composites of good quality. Tensile and flexural properties of LCP/CF composites are comparable to those of epoxy/CF composites. The LCP/CF composites have better impact resistance than the latter, although epoxy/CF composites possess superior compression and shear strength. The LCP/CF composites have good property retention until 200 F (67 % of room temperature value). Above 200 F, mechanical properties decrease significantly. Experimental results indicate that the poor compression and shear strength may be due to the poor interfacial adhesion between the matrix and carbon fiber as adequate toughness of the LCP matrix. Low mechanical property retention at high temperatures may be attributable to the low beta-transition temperature (around 80 C) of the LCP matrix material.

  1. Adsorption of hydrogen sulfide onto activated carbon fibers: effect of pore structure and surface chemistry.

    PubMed

    Feng, Wenguo; Kwon, Seokjoon; Borguet, Eric; Vidic, Radisav

    2005-12-15

    To understand the nature of H2S adsorption onto carbon surfaces under dry and anoxic conditions, the effects of carbon pore structure and surface chemistry were studied using activated carbon fibers (ACFs) with different pore structures and surface areas. Surface pretreatments, including oxidation and heattreatment, were conducted before adsorption/desorption tests in a fixed-bed reactor. Raw ACFs with higher surface area showed greater adsorption and retention of sulfur, and heat treatment further enhanced adsorption and retention of sulfur. The retained amount of hydrogen sulfide correlated well with the amount of basic functional groups on the carbon surface, while the desorbed amount reflected the effect of pore structure. Temperature-programmed desorption (TPD) and thermal gravimetric analysis (TGA) showed that the retained sulfurous compounds were strongly bonded to the carbon surface. In addition, surface chemistry of the sorbent might determine the predominant form of adsorbate on the surface. PMID:16475362

  2. Adsorption of hydrogen sulfide onto activated carbon fibers: effect of pore structure and surface chemistry.

    PubMed

    Feng, Wenguo; Kwon, Seokjoon; Borguet, Eric; Vidic, Radisav

    2005-12-15

    To understand the nature of H2S adsorption onto carbon surfaces under dry and anoxic conditions, the effects of carbon pore structure and surface chemistry were studied using activated carbon fibers (ACFs) with different pore structures and surface areas. Surface pretreatments, including oxidation and heattreatment, were conducted before adsorption/desorption tests in a fixed-bed reactor. Raw ACFs with higher surface area showed greater adsorption and retention of sulfur, and heat treatment further enhanced adsorption and retention of sulfur. The retained amount of hydrogen sulfide correlated well with the amount of basic functional groups on the carbon surface, while the desorbed amount reflected the effect of pore structure. Temperature-programmed desorption (TPD) and thermal gravimetric analysis (TGA) showed that the retained sulfurous compounds were strongly bonded to the carbon surface. In addition, surface chemistry of the sorbent might determine the predominant form of adsorbate on the surface.

  3. Dissemination, resuspension, and filtration of carbon fibers. [aircraft fires

    NASA Technical Reports Server (NTRS)

    Elber, W.

    1980-01-01

    Carbon fiber transport was studied using mathematical models established for other pollution problems. It was demonstrated that resuspension is not a major factor contributing to the risk. Filtration and fragmentation tests revealed that fiber fragmentation shifts the fiber spectrum to shorter mean lengths in high velocity air handling systems.

  4. Visualization of the exothermal VOC adsorption in a fixed-bed activated carbon adsorber.

    PubMed

    Le Cloirec, P; Pré, P; Delage, F; Giraudet, S

    2012-01-01

    Activated carbon fixed beds are classically used to remove volatile organic compounds (VOCs) present in gaseous emissions. In such use, an increase of local temperature due to exothermal adsorption has been reported; some accidental fires in the carbon bed due to the removal of high concentrations of ketones have been published. In this work, removal of VOCs was performed in a laboratory-scale pilot unit. In order to visualize the increase in local temperature, the adsorption front was tracked with a flame ionization detector and the thermal wave was simultaneously visualized with an infrared camera. In extreme conditions, fire in the adsorber and the combustion of activated carbon was achieved during ketone adsorption. Data have been extracted from these experiments, including local temperature, front velocity and carbon bed combustion conditions.

  5. Characterization and Oxidation Behavior of Rayon-Derived Carbon Fibers

    NASA Technical Reports Server (NTRS)

    Jacobson, Nathan; Hull, David

    2010-01-01

    Rayon-derived fibers are the central constituent of reinforced carbon/ carbon (RCC) composites. Optical, scanning electron, and transmission electron microscopy were used to characterize the as-fabricated fibers and the fibers after oxidation. Oxidation rates were measured with weight loss techniques in air and oxygen. The as-received fibers are approximately 10 micron in diameter and characterized by grooves or crenulations around the edges. Below 800 C, in the reaction-controlled region, preferential attack began in the crenulations and appeared to occur down fissures in the fibers.

  6. 40 CFR 63.993 - Absorbers, condensers, carbon adsorbers and other recovery devices used as final recovery devices.

    Code of Federal Regulations, 2010 CFR

    2010-07-01

    ... flow for each regeneration cycle; and a carbon-bed temperature monitoring device, capable of recording... 40 Protection of Environment 10 2010-07-01 2010-07-01 false Absorbers, condensers, carbon... Absorbers, condensers, carbon adsorbers and other recovery devices used as final recovery devices. (a)...

  7. 40 CFR 63.993 - Absorbers, condensers, carbon adsorbers and other recovery devices used as final recovery devices.

    Code of Federal Regulations, 2011 CFR

    2011-07-01

    ... flow for each regeneration cycle; and a carbon-bed temperature monitoring device, capable of recording... 40 Protection of Environment 10 2011-07-01 2011-07-01 false Absorbers, condensers, carbon... Absorbers, condensers, carbon adsorbers and other recovery devices used as final recovery devices. (a)...

  8. 40 CFR 63.993 - Absorbers, condensers, carbon adsorbers and other recovery devices used as final recovery devices.

    Code of Federal Regulations, 2013 CFR

    2013-07-01

    ... flow for each regeneration cycle; and a carbon-bed temperature monitoring device, capable of recording... 40 Protection of Environment 11 2013-07-01 2013-07-01 false Absorbers, condensers, carbon... Absorbers, condensers, carbon adsorbers and other recovery devices used as final recovery devices. (a)...

  9. Magnetic graphene-carbon nanotube iron nanocomposites as adsorbents and antibacterial agents for water purification.

    PubMed

    Sharma, Virender K; McDonald, Thomas J; Kim, Hyunook; Garg, Vijayendra K

    2015-11-01

    One of the biggest challenges of the 21st century is to provide clean and affordable water through protecting source and purifying polluted waters. This review presents advances made in the synthesis of carbon- and iron-based nanomaterials, graphene-carbon nanotubes-iron oxides, which can remove pollutants and inactivate virus and bacteria efficiently in water. The three-dimensional graphene and graphene oxide based nanostructures exhibit large surface area and sorption sites that provide higher adsorption capacity to remove pollutants than two-dimensional graphene-based adsorbents and other conventional adsorbents. Examples are presented to demonstrate removal of metals (e.g., Cu, Pb, Cr(VI), and As) and organics (e.g., dyes and oil) by grapheme-based nanostructures. Inactivation of Gram-positive and Gram-negative bacterial species (e.g., Escherichia coli and Staphylococcus aureus) is also shown. A mechanism involving the interaction of adsorbents and pollutants is briefly discussed. Magnetic graphene-based nanomaterials can easily be separated from the treated water using an external magnet; however, there are challenges in implementing the graphene-based nanotechnology in treating real water. PMID:26498500

  10. Magnetic graphene-carbon nanotube iron nanocomposites as adsorbents and antibacterial agents for water purification.

    PubMed

    Sharma, Virender K; McDonald, Thomas J; Kim, Hyunook; Garg, Vijayendra K

    2015-11-01

    One of the biggest challenges of the 21st century is to provide clean and affordable water through protecting source and purifying polluted waters. This review presents advances made in the synthesis of carbon- and iron-based nanomaterials, graphene-carbon nanotubes-iron oxides, which can remove pollutants and inactivate virus and bacteria efficiently in water. The three-dimensional graphene and graphene oxide based nanostructures exhibit large surface area and sorption sites that provide higher adsorption capacity to remove pollutants than two-dimensional graphene-based adsorbents and other conventional adsorbents. Examples are presented to demonstrate removal of metals (e.g., Cu, Pb, Cr(VI), and As) and organics (e.g., dyes and oil) by grapheme-based nanostructures. Inactivation of Gram-positive and Gram-negative bacterial species (e.g., Escherichia coli and Staphylococcus aureus) is also shown. A mechanism involving the interaction of adsorbents and pollutants is briefly discussed. Magnetic graphene-based nanomaterials can easily be separated from the treated water using an external magnet; however, there are challenges in implementing the graphene-based nanotechnology in treating real water.

  11. Carbon nanowalls grown by microwave plasma enhanced chemical vapor deposition during the carbonization of polyacrylonitrile fibers

    NASA Astrophysics Data System (ADS)

    Li, Jiangling; Su, Shi; Zhou, Lei; Kundrát, Vojtěch; Abbot, Andrew M.; Mushtaq, Fajer; Ouyang, Defang; James, David; Roberts, Darren; Ye, Haitao

    2013-01-01

    We used microwave plasma enhanced chemical vapor deposition (MPECVD) to carbonize an electrospun polyacrylonitrile (PAN) precursor to form carbon fibers. Scanning electron microscopy, Raman spectroscopy, and Fourier transform infrared spectroscopy were used to characterize the fibers at different evolution stages. It was found that MPECVD-carbonized PAN fibers do not exhibit any significant change in the fiber diameter, whilst conventionally carbonized PAN fibers show a 33% reduction in the fiber diameter. An additional coating of carbon nanowalls (CNWs) was formed on the surface of the carbonized PAN fibers during the MPECVD process without the assistance of any metallic catalysts. The result presented here may have a potential to develop a novel, economical, and straightforward approach towards the mass production of carbon fibrous materials containing CNWs.

  12. Carbon nanowalls grown by microwave plasma enhanced chemical vapor deposition during the carbonization of polyacrylonitrile fibers

    SciTech Connect

    Li Jiangling; Su Shi; Kundrat, Vojtech; Abbot, Andrew M.; Ye, Haitao; Zhou Lei; Mushtaq, Fajer; Ouyang Defang; James, David; Roberts, Darren

    2013-01-14

    We used microwave plasma enhanced chemical vapor deposition (MPECVD) to carbonize an electrospun polyacrylonitrile (PAN) precursor to form carbon fibers. Scanning electron microscopy, Raman spectroscopy, and Fourier transform infrared spectroscopy were used to characterize the fibers at different evolution stages. It was found that MPECVD-carbonized PAN fibers do not exhibit any significant change in the fiber diameter, whilst conventionally carbonized PAN fibers show a 33% reduction in the fiber diameter. An additional coating of carbon nanowalls (CNWs) was formed on the surface of the carbonized PAN fibers during the MPECVD process without the assistance of any metallic catalysts. The result presented here may have a potential to develop a novel, economical, and straightforward approach towards the mass production of carbon fibrous materials containing CNWs.

  13. Process for the manufacture of carbon or graphite fibers

    NASA Technical Reports Server (NTRS)

    Overhoff, D.; Winkler, E.; Mueller, D.

    1979-01-01

    Carbon or graphite fibers are manufactured by heating polyacrylonitrile fiber materials in various solutions and gases. They are characterized in that the materials are heated to temperatures from 150 to 300 C in a solution containing one or more acids from the group of carbonic acids, sulfonic acids, and/or phenols. The original molecular orientation of the fibers is preserved by the cyclization that occurs before interlacing, which gives very strong and stiff carbon or graphite fibers without additional high temperature stretching treatments.

  14. Nanoclay-Based Solid-Amine Adsorbents for Carbon Dioxide Capture

    NASA Astrophysics Data System (ADS)

    Roth, Elliot A.

    The objective of this research was to develop an efficient, low cost, recyclable solid sorbent for carbon dioxide adsorption from large point sources, such as coal-fired power plants. The current commercial way to adsorb CO 2 is to use a liquid amine or ammonia process. These processes are used in industry in the "sweetening" of natural gas, but liquid based technologies are not economically viable in the adsorption of CO2 from power plants due to the extremely large volume of CO2 and the inherent high regeneration costs of cycling the sorbent. Therefore, one of the main objectives of this research was to develop a novel sorbent that can be cycled and uses very little energy for regeneration. The sorbent developed here is composed of a nanoclay (montmorillonite), commonly used in the production of polymer nanocomposites, grafted with commercially available amines. (3-aminopropyl) trimethoxysilane (APTMS) was chemically grafted to the edge hydroxyl groups of the clay. While another amine, polyethylenimine (PEI), was attached to the surface of the clay by electrostatic interactions. To confirm the attachment of amines to the clay, the samples were characterized using FTIR and the corresponding peaks for amines were observed. The amount of amine loaded onto the support was determined by TGA techniques. The treated clay was initially analyzed for CO2 adsorption in a pure CO 2 stream. The adsorption temperatures that had the highest adsorption capacity were determined to be between 75°C and 100°C for all of the samples tested at atmospheric pressure. The maximum CO2 adsorption capacity observed was with nanoclay treated with both APTMS and PEI at 85°C. In a more realistic flue gas of 10% CO2 and 90% N2, the adsorbents had essentially the same overall CO2 adsorption capacity indicating that the presence of nitrogen did not hinder the adsorption of CO2. Adsorption studies in pure CO2 at room temperature under pressure from 40-300 PSI were also conducted. The average

  15. Carbon-fiber low-voltage electron guns

    SciTech Connect

    Drori, R.; Jerby, E.

    1995-12-31

    Carbon-fiber cathodes am used in cold electron-guns in our laboratory. They operate in low-voltage (< 10 kV) free-electron maser and cyclotron-resonance maser experiments. The paper presents I-V characteristics of various carbon-fiber electron-guns and show results of the corresponding maser experiments.

  16. Structure and growth process of vapor-grown carbon fibers

    NASA Technical Reports Server (NTRS)

    Koyama, T.; Endo, M.

    1983-01-01

    The structure, effect of heat, and growth process of vapor-grown carbon fibers are investigated. The growth process of the carbon fibers could be divided into three stages; nucleation, elongation, and thickening processes. Also, a multi-layered structure can be produced as well as graphitization.

  17. Uranium Adsorbent Fibers Prepared by Atom-Transfer Radical Polymerization (ATRP) from Poly(vinyl chloride)- co -chlorinated Poly(vinyl chloride) (PVC- co -CPVC) Fiber

    DOE PAGES

    Brown, Suree; Yue, Yanfeng; Kuo, Li-Jung; Mehio, Nada; Li, Meijun; Gill, Gary; Tsouris, Costas; Mayes, Richard T.; Saito, Tomonori; Dai, Sheng

    2016-03-11

    The need to secure future supplies of energy attracts researchers in several countries to a vast resource of nuclear energy fuel: uranium in seawater (estimated at 4.5 billion tons in seawater). In this study, we developed effective adsorbent fibers for the recovery of uranium from seawater via atom-transfer radical polymerization (ATRP) from a poly-(vinyl chloride)-co-chlorinated poly(vinyl chloride) (PVC-co-CPVC) fiber. ATRP was employed in the surface graft polymerization of acrylonitrile (AN) and tert-butyl acrylate (tBA), precursors for uranium-interacting functional groups, from PVC-co-CPVC fiber. The [tBA]/[AN] was systematically varied to identify the optimal ratio between hydrophilic groups (from tBA) and uranyl-binding ligandsmore » (from AN). The best performing adsorbent fiber, the one with the optimal [tBA]/[AN] ratio and a high degree of grafting (1390%), demonstrated uranium adsorption capacities that are significantly greater than those of the Japan Atomic Energy Agency (JAEA) reference fiber in natural seawater tests (2.42 3.24 g/kg in 42 days of seawater exposure and 5.22 g/kg in 49 days of seawater exposure, versus 1.66 g/kg in 42 days of seawater exposure and 1.71 g/kg in 49 days of seawater exposure for JAEA). Lastly, adsorption of other metal ions from seawater and their corresponding kinetics were also studied. The grafting of alternative monomers for the recovery of uranium from seawater is now under development by this versatile technique of ATRP.« less

  18. High efficient preparation of carbon nanotube-grafted carbon fibers with the improved tensile strength

    NASA Astrophysics Data System (ADS)

    Fan, Wenxin; Wang, Yanxiang; Wang, Chengguo; Chen, Jiqiang; Wang, Qifen; Yuan, Yan; Niu, Fangxu

    2016-02-01

    An innovative technique has been developed to obtain the uniform catalyst coating on continuously moving carbon fibers. Carbon nanotube (CNT)-grafted carbon fibers with significantly improved tensile strength have been succeeded to produce by using chemical vapor deposition (CVD) when compared to the tensile strength of untreated carbon fibers. The critical requirements for preparation of CNT-grafted carbon fibers with high tensile strength have been found, mainly including (i) the obtainment of uniform coating of catalyst particles with small particle size, (ii) the low catalyst-induced and mechano-chemical degradation of carbon fibers, and (iii) the high catalyst activity which could facilitate the healing and strengthening of carbon fibers during the growth of CNTs. The optimum growth temperature was found to be about 500 °C, and the optimum catalyst is Ni due to its highest activity, there is a pronounced increase of 10% in tensile strength of carbon fibers after CNT growth at 500 °C by using Ni catalyst. Based on the observation from HRTEM images, a healing and crosslink model of neighboring carbon crystals by CNTs has been formulated to reveal the main reason that causes an increase in tensile strength of carbon fibers after the growth of CNTs. Such results have provided the theoretical and experimental foundation for the large-scale preparation of CNT-grafted carbon fibers with the improved tensile strength, significantly promoting the development of CNT-grafted carbon fiber reinforced polymer composites.

  19. Adsorbed Natural Gas Storage in Optimized High Surface Area Microporous Carbon

    NASA Astrophysics Data System (ADS)

    Romanos, Jimmy; Rash, Tyler; Nordwald, Erik; Shocklee, Joshua Shawn; Wexler, Carlos; Pfeifer, Peter

    2011-03-01

    Adsorbed natural gas (ANG) is an attractive alternative technology to compressed natural gas (CNG) or liquefied natural gas (LNG) for the efficient storage of natural gas, in particular for vehicular applications. In adsorbants engineered to have pores of a few molecular diameters, a strong van der Walls force allows reversible physisorption of methane at low pressures and room temperature. Activated carbons were optimized for storage by varying KOH:C ratio and activation temperature. We also consider the effect of mechanical compression of powders to further enhance the volumetric storage capacity. We will present standard porous material characterization (BET surface area and pore-size distribution from subcritical N2 adsorption) and methane isotherms up to 250 bar at 293K. At sufficiently high pressure, specific surface area, methane binding energy and film density can be extracted from supercritical methane adsorption isotherms. Research supported by the California Energy Commission (500-08-022).

  20. Comprehensive study of mesoporous carbon functionalized with carboxylate groups and magnetic nanoparticles as a promising adsorbent.

    PubMed

    Chi, Yue; Geng, Wangchang; Zhao, Liang; Yan, Xiao; Yuan, Qing; Li, Nan; Li, Xiaotian

    2012-03-01

    Highly ordered mesoporous carbon functionalized with carboxylate groups and magnetic nanoparticles has been successfully synthesized. By oxidative treatment using (NH(4))(2)S(2)O(8) and H(2)SO(4) mixed solution, numerous hydrophilic groups were created in the mesopores without destroying the ordered mesostructure of CMK-3. Through the in situ reduction in Fe(3+), magnetic nanoparticles were successfully introduced into the mesopores, resulting in the multifunctional mesoporous carbon Fe-CMK-3. The obtained hybrid carbon material possesses ordered mesostructure, high Brunauer-Emmett-Teller (BET) surface area up to 1013 m(2)/g, large pore volume of about 1.16 cm(3)/g, carboxylic surface, and excellent magnetic property. When used as an adsorbent, Fe-CMK-3 exhibits excellent performances for removing toxic organic compounds from waster-water, with a high adsorption capacity, an extremely rapid adsorption rate, and an easy magnetically separable process. In the case of requiring emergency removal of large amount of organic pollutants in aqueous, the hybrid carbon adsorbent would be an ideal choice.

  1. Thermal Properties of Hybrid Carbon Nanotube/Carbon Fiber Polymer

    NASA Technical Reports Server (NTRS)

    Kang, Jin Ho; Cano, Roberto J.; Luong, Hoa; Ratcliffe, James G.; Grimsley, Brian W.; Siochi, Emilie J.

    2016-01-01

    Carbon fiber reinforced polymer (CFRP) composites possess many advantages for aircraft structures over conventional aluminum alloys: light weight, higher strength- and stiffness-to-weight ratio, and low life-cycle maintenance costs. However, the relatively low thermal and electrical conductivities of CFRP composites are deficient in providing structural safety under certain operational conditions such as lightning strikes. One possible solution to these issues is to interleave carbon nanotube (CNT) sheets between conventional carbon fiber (CF) composite layers. However, the thermal and electrical properties of the orthotropic hybrid CNT/CF composites have not been fully understood. In this study, hybrid CNT/CF polymer composites were fabricated by interleaving layers of CNT sheets with Hexcel (Registered Trademark) IM7/8852 prepreg. The CNT sheets were infused with a 5% solution of a compatible epoxy resin prior to composite fabrication. Orthotropic thermal and electrical conductivities of the hybrid polymer composites were evaluated. The interleaved CNT sheets improved the in-plane thermal conductivity of the hybrid composite laminates by about 400% and the electrical conductivity by about 3 orders of magnitude.

  2. Multifunctional Hybrid Carbon Nanotube/Carbon Fiber Polymer Composites

    NASA Technical Reports Server (NTRS)

    Kang, Jin Ho; Cano, Roberto J.; Ratcliffe, James G.; Luong, Hoa; Grimsley, Brian W.; Siochi, Emilie J.

    2016-01-01

    For aircraft primary structures, carbon fiber reinforced polymer (CFRP) composites possess many advantages over conventional aluminum alloys due to their light weight, higher strengthand stiffness-to-weight ratio, and low life-cycle maintenance costs. However, the relatively low electrical and thermal conductivities of CFRP composites fail to provide structural safety in certain operational conditions such as lightning strikes. Despite several attempts to solve these issues with the addition of carbon nanotubes (CNT) into polymer matrices, and/or by interleaving CNT sheets between conventional carbon fiber (CF) composite layers, there are still interfacial problems that exist between CNTs (or CF) and the resin. In this study, hybrid CNT/CF polymer composites were fabricated by interleaving layers of CNT sheets with Hexcel® IM7/8852 prepreg. Resin concentrations from 1 wt% to 50 wt% were used to infuse the CNT sheets prior to composite fabrication. The interlaminar properties of the resulting hybrid composites were characterized by mode I and II fracture toughness testing (double cantilever beam and end-notched flexure test). Fractographical analysis was performed to study the effect of resin concentration. In addition, multi-directional physical properties like thermal conductivity of the orthotropic hybrid polymer composite were evaluated. Interleaving CNT sheets significantly improved the in-plane (axial and perpendicular direction of CF alignment) thermal conductivity of the hybrid composite laminates by 50 - 400%.

  3. Effects of welding fumes on nuclear air cleaning system carbon adsorber banks

    SciTech Connect

    Roberson, P.W.

    1997-08-01

    Standard Technical Specifications for nuclear air cleaning systems include requirements for surveillance tests following fire, painting, or chemical release in areas communicating with the affected system. To conservatively implement this requirement, many plants categorize welding as a chemical release process, and institute controls to ensure that welding fumes do not interact with carbon adsorbers in a filter system. After reviewing research data that indicated welding had a minimal impact on adsorber iodine removal efficiency, further testing was performed with the goal of establishing a welding threshold. It was anticipated that some quantity of weld electrodes could be determined that had a corresponding detrimental impact on iodine removal efficiency for the exposed adsorber. This value could be used to determine a conservative sampling schedule that would allow the station to perform laboratory testing to ensure system degradation did not occur without a full battery of surveillance tests. A series of tests was designed to demonstrate carbon efficiency versus cumulative welding fume exposure. Three series of tests were performed, one for each of three different types of commonly used weld electrodes. Carbon sampling was performed at baseline conditions, and every five pounds of electrode thereafter. Two different laboratory tests were performed for each sample; one in accordance with ASTM 3803/1989 at 95% relative humidity and 30 degrees C, and another using the less rigorous conditions of 70% relative humidity and 80 degrees C. Review of the test data for all three types of electrodes failed to show a significant correlation between carbon efficiency degradation and welding fume exposure. Accordingly, welding is no longer categorized as a `chemical release process` at McGuire Nuclear Station, and limits on welding fume interaction with ventilation systems have been eliminated. 4 refs., 3 figs., 1 tab.

  4. Preliminary experimental study of a carbon fiber array cathode

    NASA Astrophysics Data System (ADS)

    Li, An-kun; Fan, Yu-wei

    2016-08-01

    The preliminary experimental results of a carbon fiber array cathode for the magnetically insulated transmission line oscillator (MILO) operations are reported. When the diode voltage and diode current were 480 kV and 44 kA, respectively, high-power microwaves with a peak power of about 3 GW and a pulse duration of about 60 ns were obtained in a MILO device with the carbon fiber array cathode. The preliminary experimental results show that the shot-to-shot reproducibility of the diode current and the microwave power is stable until 700 shots. No obvious damage or deterioration can be observed in the carbon fiber surface morphology after 700 shots. Moreover, the cathode performance has no observable deterioration after 700 shots. In conclusion, the maintain-free lifetime of the carbon fiber array cathode is more than 700 shots. In this way, this carbon fiber array cathode offers a potential replacement for the existing velvet cathode.

  5. Carbon-Based Adsorbents for Postcombustion CO2 Capture: A Critical Review.

    PubMed

    Creamer, Anne Elise; Gao, Bin

    2016-07-19

    The persistent increase in atmospheric CO2 from anthropogenic sources makes research directed toward carbon capture and storage imperative. Current liquid amine absorption technology has several drawbacks including hazardous byproducts and a high-energy requirement for regeneration; therefore, research is ongoing to develop more practical methods for capturing CO2 in postcombustion scenarios. The unique properties of carbon-based materials make them specifically promising for CO2 adsorption at low temperature and moderate to high partial pressure. This critical review aims to highlight the development of carbon-based solid sorbents for postcombustion CO2 capture. Specifically, it provides an overview of postcombustion CO2 capture processes with solid adsorbents and discusses a variety of carbon-based materials that could be used. This review focuses on low-cost pyrogenic carbon, activated carbon (AC), and metal-carbon composites for CO2 capture. Further, it touches upon the recent progress made to develop metal organic frameworks (MOFs) and carbon nanomaterials and their general CO2 sorption potential.

  6. Potential mechanistic routes for the oxidative disintegration of ketones on carbon adsorbents

    SciTech Connect

    Akubuiro, E.C.

    1993-12-01

    Solvent recovery and air emission control are among the many industrial uses of activated carbon. The efficient use of activated carbon technology for these applications requires some understanding of carbon-solvent interactions and associated system behavior, especially in an oxidizing atmosphere. The oxidative activity characteristics of a number of organic solvents adsorbed on activated carbon were determined using temperature programmed oxidation (TPO) and temperature programmed desorption (TPD) techniques. Thermogravimetry (TG), differential thermal gravimetry (DTG), differential scanning calorimetry (DSC), and Fourier transform infrared (FTIR) spectroscopy were employed to provide some insights on the thermal behavior of the carbon-solvent systems in oxidative and inert atmospheres. The thermal desorption patterns and oxidation stabilities of selected ketones were monitored, and the formation of products due to incomplete combustion was established. Based on the observed results, plausible mechanisms associated with the decomposition of these oxidizable organic solvents on activated carbon are discussed to delineate the types of reactions that initiate carbon bed combustion and/or carbon degradation.

  7. Carbon-Based Adsorbents for Postcombustion CO2 Capture: A Critical Review.

    PubMed

    Creamer, Anne Elise; Gao, Bin

    2016-07-19

    The persistent increase in atmospheric CO2 from anthropogenic sources makes research directed toward carbon capture and storage imperative. Current liquid amine absorption technology has several drawbacks including hazardous byproducts and a high-energy requirement for regeneration; therefore, research is ongoing to develop more practical methods for capturing CO2 in postcombustion scenarios. The unique properties of carbon-based materials make them specifically promising for CO2 adsorption at low temperature and moderate to high partial pressure. This critical review aims to highlight the development of carbon-based solid sorbents for postcombustion CO2 capture. Specifically, it provides an overview of postcombustion CO2 capture processes with solid adsorbents and discusses a variety of carbon-based materials that could be used. This review focuses on low-cost pyrogenic carbon, activated carbon (AC), and metal-carbon composites for CO2 capture. Further, it touches upon the recent progress made to develop metal organic frameworks (MOFs) and carbon nanomaterials and their general CO2 sorption potential. PMID:27257991

  8. Graphitized-carbon fiber/carbon char fuel

    SciTech Connect

    Cooper, John F.

    2007-08-28

    A method for recovery of intact graphitic fibers from fiber/polymer composites is described. The method comprises first pyrolyzing the graphite fiber/polymer composite mixture and then separating the graphite fibers by molten salt electrochemical oxidation.

  9. Graphene nanoribbons as an advanced precursor for making carbon fiber.

    PubMed

    Xiang, Changsheng; Behabtu, Natnael; Liu, Yaodong; Chae, Han Gi; Young, Colin C; Genorio, Bostjan; Tsentalovich, Dmitri E; Zhang, Chenguang; Kosynkin, Dmitry V; Lomeda, Jay R; Hwang, Chih-Chau; Kumar, Satish; Pasquali, Matteo; Tour, James M

    2013-02-26

    Graphene oxide nanoribbons (GONRs) and chemically reduced graphene nanoribbons (crGNRs) were dispersed at high concentrations in chlorosulfonic acid to form anisotropic liquid crystal phases. The liquid crystal solutions were spun directly into hundreds of meters of continuous macroscopic fibers. The relationship of fiber morphology to coagulation bath conditions was studied. The effects of colloid concentration, annealing temperature, spinning air gap, and pretension during annealing on the fibers' performance were also investigated. Heat treatment of the as-spun GONR fibers at 1500 °C produced thermally reduced graphene nanoribbon (trGNR) fibers with a tensile strength of 378 MPa, Young's modulus of 36.2 GPa, and electrical conductivity of 285 S/cm, which is considerably higher than that in other reported graphene-derived fibers. This better trGNR fiber performance was due to the air gap spinning and annealing with pretension that produced higher molecular alignment within the fibers, as determined by X-ray diffraction and scanning electron microscopy. The specific modulus of trGNR fibers is higher than that of the commercial general purpose carbon fibers and commonly used metals such as Al, Cu, and steel. The properties of trGNR fibers can be further improved by optimizing the spinning conditions with higher draw ratio, annealing conditions with higher pretensions, and using longer flake GONRs. This technique is a new high-carbon-yield approach to make the next generation carbon fibers based on solution-based liquid crystal phase spinning. PMID:23339339

  10. Graphene nanoribbons as an advanced precursor for making carbon fiber.

    PubMed

    Xiang, Changsheng; Behabtu, Natnael; Liu, Yaodong; Chae, Han Gi; Young, Colin C; Genorio, Bostjan; Tsentalovich, Dmitri E; Zhang, Chenguang; Kosynkin, Dmitry V; Lomeda, Jay R; Hwang, Chih-Chau; Kumar, Satish; Pasquali, Matteo; Tour, James M

    2013-02-26

    Graphene oxide nanoribbons (GONRs) and chemically reduced graphene nanoribbons (crGNRs) were dispersed at high concentrations in chlorosulfonic acid to form anisotropic liquid crystal phases. The liquid crystal solutions were spun directly into hundreds of meters of continuous macroscopic fibers. The relationship of fiber morphology to coagulation bath conditions was studied. The effects of colloid concentration, annealing temperature, spinning air gap, and pretension during annealing on the fibers' performance were also investigated. Heat treatment of the as-spun GONR fibers at 1500 °C produced thermally reduced graphene nanoribbon (trGNR) fibers with a tensile strength of 378 MPa, Young's modulus of 36.2 GPa, and electrical conductivity of 285 S/cm, which is considerably higher than that in other reported graphene-derived fibers. This better trGNR fiber performance was due to the air gap spinning and annealing with pretension that produced higher molecular alignment within the fibers, as determined by X-ray diffraction and scanning electron microscopy. The specific modulus of trGNR fibers is higher than that of the commercial general purpose carbon fibers and commonly used metals such as Al, Cu, and steel. The properties of trGNR fibers can be further improved by optimizing the spinning conditions with higher draw ratio, annealing conditions with higher pretensions, and using longer flake GONRs. This technique is a new high-carbon-yield approach to make the next generation carbon fibers based on solution-based liquid crystal phase spinning.

  11. Shear transfer in concrete reinforced with carbon fibers

    NASA Astrophysics Data System (ADS)

    El-Mokadem, Khaled Mounir

    2001-10-01

    Scope and method of study. The research started with preliminary tests and studies on the behavior and effect of carbon fibers in different water solutions and mortar/concrete mixes. The research work investigated the use of CF in the production of concrete pipes and prestressed concrete double-tee sections. The research then focused on studying the effect of using carbon fibers on the direct shear transfer of sand-lightweight reinforced concrete push-off specimens. Findings and conclusions. In general, adding carbon fibers to concrete improved its tensile characteristics but decreased its compressive strength. The decrease in compressive strength was due to the decrease in concrete density as fibers act as three-dimensional mesh that entrapped air. The decrease in compressive strength was also due to the increase in the total surface area of non-cementitious material in the concrete. Sand-lightweight reinforced concrete push-off specimens with carbon fibers had lower shear carrying capacity than those without carbon fibers for the same cement content in the concrete. Current building codes and specifications estimate the shear strength of concrete as a ratio of the compressive strength. If applying the same principals then the ratio of shear strength to compressive strength for concrete reinforced with carbon fibers is higher than that for concrete without carbon fibers.

  12. Surface characterization of LDEF carbon fiber/polymer matrix composites

    NASA Technical Reports Server (NTRS)

    Grammer, Holly L.; Wightman, James P.; Young, Philip R.; Slemp, Wayne S.

    1995-01-01

    XPS (x-ray photoelectron spectroscopy) and SEM (scanning electron microscopy) analysis of both carbon fiber/epoxy matrix and carbon fiber/polysulfone matrix composites revealed significant changes in the surface composition as a result of exposure to low-earth orbit. The carbon 1s curve fit XPS analysis in conjunction with the SEM photomicrographs revealed significant erosion of the polymer matrix resins by atomic oxygen to expose the carbon fibers of the composite samples. This erosion effect on the composites was seen after 10 months in orbit and was even more obvious after 69 months.

  13. Carbon nanotube reinforced polyacrylonitrile and poly(etherketone) fibers

    NASA Astrophysics Data System (ADS)

    Jain, Rahul

    The graphitic nature, continuous structure, and high mechanical properties of carbon nanotubes (CNTs) make them good candidate for reinforcing polymer fiber. The different types of CNTs including single-wall carbon nanotubes (SWNTs), few-wall carbon nanotubes (FWNTs), and multi-wall carbon nanotubes (MWNTs), and carbon nanofibers (CNFs) differ in terms of their diameter and number of graphitic walls. The desire has been to increase the concentration of CNTs as much as possible to make next generation multi-functional materials. The work in this thesis is mainly focused on MWNT and CNF reinforced polyacrylonitrile (PAN) composite fibers, and SWNT, FWNT, and MWNT reinforced poly(etherketone) (PEK) composite fibers. To the best of our knowledge, this is the first study to report the spinning of 20% MWNT or 30% CNF reinforced polymer fiber spun using conventional fiber spinning. Also, this is the first study to report the PEK/CNT composite fibers. The fibers were characterized for their thermal, tensile, mechanical, and dynamic mechanical properties. The fiber structure and morphology was studied using WAXD and SEM. The effect of two-stage heat drawing, sonication time for CNF dispersion, fiber drying temperature, and molecular weight of PAN was also studied. Other challenges associated with processing high concentrations of solutions for making composite fibers have been identified and reported. The effect of CNT diameter and concentration on fiber spinnability and electrical conductivity of composite fiber have also been studied. This work suggests that CNT diameter controls the maximum possible concentration of CNTs in a composite fiber. The results show that by properly choosing the type of CNT, length of CNTs, dispersion of CNTs, fiber spinning method, fiber draw ratio, and type of polymer, one can get electrically conducting fibers with wide range of conductivities for different applications. The PEK based control and composite fibers possess high thermal

  14. Synthesis of porous sulfonated carbon as a potential adsorbent for phenol wastewater.

    PubMed

    Prabhu, Azhagapillai; Al Shoaibi, Ahmed; Srinivasakannan, C

    2015-01-01

    The work reports a facile synthesis procedure for preparation of porous sulfonated carbons and its suitability for adsorption of phenol. The sulfonated carbon was synthesized utilizing a simplified, single-step, shorter duration process by sulfonation, dehydration and carbonization of sucrose in sulfuric acid and tetraethylorthosilicate. The surface and internal structures of the adsorbents were characterized utilizing various characterization techniques to understand the porous nature and surface functional groups of the porous matrix. Adsorption capacity was found to be highest for the sample heat treated at 600 °C, with the maximum adsorption capacity of 440 mg/g at 30 °C. The adsorption isotherms were tested with the Freundlich and Langmuir adsorption isotherms models to identify the appropriate adsorption mechanism.

  15. Free-standing carbon nanotube/graphene hybrid papers as next generation adsorbents.

    PubMed

    Dichiara, Anthony B; Sherwood, Tyler J; Benton-Smith, Jared; Wilson, Jonathan C; Weinstein, Steven J; Rogers, Reginald E

    2014-06-21

    The adsorption of a series of aromatic compounds from aqueous solution onto purified, free-standing single-walled carbon nanotube/graphene nanoplatelet hybrid papers is studied both experimentally and theoretically. Experimental data is obtained via changes in optical absorption spectra of the aqueous solutions and is used to extract all parameters required to implement a semi-empirical mass-transfer model. Agreement between experiment and theory is excellent and data from all compounds can be cast on a universal adsorption curve. Results indicate that the rate of adsorption and long-time capacity of many aromatic compounds on hybrid paper adsorbent significantly exceeds that of activated carbon by at least an order of magnitude. The combination of carbon nanotubes and graphene also promotes on the order of a 25% improvement in adsorption rates and capacities than either component alone. Hybrid nanocomposites show significant promise as adsorption materials used for environmental remediation efforts.

  16. RADIATION EFFECTS ON EPOXY CARBON FIBER COMPOSITE

    SciTech Connect

    Hoffman, E

    2008-05-30

    Carbon fiber-reinforced bisphenol-A epoxy matrix composite was evaluated for gamma radiation resistance. The composite was exposed to total gamma doses of 50, 100, and 200 Mrad. Irradiated and baseline samples were tested for tensile strength, hardness and evaluated using FTIR (Fourier transform infrared) spectroscopy and DSC (differential scanning calorimetry) for structural changes. Scanning electron microscopy was used to evaluate microstructural behavior. Mechanical testing of the composite bars revealed no apparent change in modulus, strain to failure, or fracture strength after exposures. However, testing of only the epoxy matrix revealed changes in hardness, thermal properties, and FTIR results with increasing gamma irradiation. The results suggest the epoxy within the composite can be affected by exposure to gamma irradiation.

  17. Selective adsorption for removal of nitrogen compounds from hydrocarbon streams over carbon-based adsorbents

    NASA Astrophysics Data System (ADS)

    Almarri, Masoud S.

    The ultimate goal of this thesis is to develop a fundamental understanding of the role of surface oxygen functional groups on carbon-based adsorbents in the adsorption of nitrogen compounds that are known to be present in liquid fuels. N2 adsorption was used to characterize pore structures. The surface chemical properties of the adsorbents were characterized by X-ray photoelectron spectroscopy (XPS) and temperature-programmed desorption (TPD) techniques with a mass spectrometer to identify and quantify the type and concentration of oxygen functional groups on the basis of CO2 and CO evolution profiles. It was found that although surface area and pore size distribution are important for the adsorption process, they are not primary factors in the adsorption of nitrogen compounds. On the other hand, both the type and concentration of surface oxygen-containing functional groups play an important role in determining adsorptive denitrogenation performance. Higher concentrations of the oxygen functional groups on the adsorbents resulted in a higher adsorption capacity for the nitrogen compounds. A fundamental insight was gained into the contributions of different oxygen functional groups by analyzing the changes in the monolayer maximum adsorption capacity, qm, and the adsorption constant, K, for nitrogen compounds on different activated carbons. Acidic functional groups such as carboxylic acids and carboxylic anhydrides appear to contribute more to the adsorption of quinoline, while the basic oxygen functional groups such as carbonyls and quinones enhance the adsorption of indole. Despite the high number of publications on the adsorptive desulfurization of liquid hydrocarbon fuels, these studies did not consider the presence of coexisting nitrogen compounds. It is well-known that, to achieve ultraclean diesel fuel, sulfur must be reduced to a very low level, where the concentrations of nitrogen and sulfur compounds are comparable. The adsorptive denitrogenation and

  18. Waste polyvinylchloride derived pitch as a precursor to develop carbon fibers and activated carbon fibers.

    PubMed

    Qiao, W M; Yoon, S H; Mochida, I; Yang, J H

    2007-01-01

    Polyvinylchloride (PVC) was successfully recycled through the solvent extraction from waste pipe with an extraction yield of ca. 86%. The extracted PVC was pyrolyzed by a two-stage process (260 and 410 degrees C) to obtain free-chlorine PVC based pitch through an effective removal of chlorine from PVC during the heat-treatment. As-prepared pitch (softening point: 220 degrees C) was spun, stabilized, carbonized into carbon fibers (CFs), and further activated into activated carbon fibers (ACFs) in a flow of CO2. As-prepared CFs show comparable mechanical properties to commercial CFs, whose maximum tensile strength and modulus are 862 MPa and 62 GPa, respectively. The resultant ACFs exhibit a high surface area of 1200 m2/g, narrow pore size distribution and a low oxygen content of 3%. The study provides an effective insight to recycle PVC from waste PVC and develop a carbon precursor for high performance carbon materials such as CFs and ACFs. PMID:17157493

  19. Forsterite Carbonation in Wet-scCO2: Dependence on Adsorbed Water Concentration

    NASA Astrophysics Data System (ADS)

    Loring, J.; Benezeth, P.; Qafoku, O.; Thompson, C.; Schaef, T.; Bonneville, A.; McGrail, P.; Felmy, A.; Rosso, K.

    2013-12-01

    Capturing and storing CO2 in basaltic formations is one of the most promising options for mitigating atmospheric CO2 emissions resulting from the burning of fossil fuels. These geologic reservoirs have high reactive potential for CO2-mineral trapping due to an abundance of divalent-cation containing silicates, such as forsterite (Mg2SiO4). Recent studies have shown that carbonation of these silicates under wet scCO2 conditions, e. g. encountered near a CO2 injection well, proceeds along a different pathway and is more effective than in CO2-saturated aqueous fluids. The presence of an adsorbed water film on the forsterite surface seems to be key to reactivity towards carbonation. In this study, we employed in situ high pressure IR spectroscopy to investigate the dependence of adsorbed water film thickness on forsterite carbonation chemistry. Post reaction ex situ SEM, TEM, TGA, XRD, and NMR measurements will also be discussed. Several IR titrations were performed of forsterite with water at 50 °C and 90 bar scCO2. Aliquots of water were titrated at 4-hour reaction-time increments. Once a desired total water concentration was reached, data were collected for about another 30 hours. One titration involved 10 additions, which corresponds to 6.8 monolayers of adsorbed water. Clearly, a carbonate was precipitating, and its spectral signature matched magnesite. Another titration involved 8 aliquots, or up to 4.4 monolayers of water. The integrated absorbance under the CO stretching bands of carbonate as a function of time after reaching 4.4 monolayers showed an increase and then a plateau. We are currently unsure of the identity of the carbonate that precipitated, but it could be an amorphous anhydrous phase or magnesite crystals with dimensions of only several nanometers. A third titration only involved 3 additions, or up to 1.6 monolayers of water. The integrated absorbance under the CO stretching bands of carbonate as a function of time after reaching 1.6 monolayers

  20. Adsorption of perfluoroalkyl acids by carbonaceous adsorbents: Effect of carbon surface chemistry.

    PubMed

    Zhi, Yue; Liu, Jinxia

    2015-07-01

    Adsorption by carbonaceous sorbents is among the most feasible processes to remove perfluorooctane sulfonic (PFOS) and carboxylic acids (PFOA) from drinking and ground waters. However, carbon surface chemistry, which has long been recognized essential for dictating performance of such sorbents, has never been considered for PFOS and PFOA adsorption. Thus, the role of surface chemistry was systematically investigated using sorbents with a wide range in precursor material, pore structure, and surface chemistry. Sorbent surface chemistry overwhelmed physical properties in controlling the extent of uptake. The adsorption affinity was positively correlated carbon surface basicity, suggesting that high acid neutralizing or anion exchange capacity was critical for substantial uptake of PFOS and PFOA. Carbon polarity or hydrophobicity had insignificant impact on the extent of adsorption. Synthetic polymer-based Ambersorb and activated carbon fibers were more effective than activated carbon made of natural materials in removing PFOS and PFOA from aqueous solutions.

  1. Carbonized material adsorbents for the removal of mercury from aqueous solutions

    SciTech Connect

    1996-10-01

    Charcoal in itself is porous making it an excellent material for activated charcoal manufacture. However, few studies have been conducted in harnessing its potential for adsorption purposes, especially in water treatment. This paper describes the possibility of utilizing charcoal materials from Sugi (Cryptomeria japonica) for adsorbing heavy metals like mercury from aqueous solutions of different concentrations. The effect of soaking time, pore analyses and chemical properties on the adsorption capabilities of the carbonized materials were discussed. The pH value and chemical oxygen demand (COD) monitored during the soaking period were also described.

  2. Carbon Nanotubes-Adsorbed Electrospun PA66 Nanofiber Bundles with Improved Conductivity and Robust Flexibility.

    PubMed

    Guan, Xiaoyang; Zheng, Guoqiang; Dai, Kun; Liu, Chuntai; Yan, Xingru; Shen, Changyu; Guo, Zhanhu

    2016-06-01

    Electrospun polyamide (PA) 66 nanofiber bundles with high conductivity, improved strength, and robust flexibility were successfully manufactured through simply adsorbing multiwall carbon nanotubes (MWNTs) on the surface of electrospun PA66 nanofibers. The highest electrical conductivity (0.2 S/cm) and tensile strength (103.3 MPa) were achieved for the bundles immersed in the suspension with 0.05 wt % MWNTs, indicating the formation of conductive network from adsorbed MWNTs on the surface of PA66 nanofibers. The decrease of porosity for the bundles immersed in the MWNT dispersion and the formation of hydrogen bond between PA66 nanofibers and MWNTs suggest a superb interfacial interaction, which is responsible for the excellent mechanical properties of the nanocomposite bundles. Furthermore, the resistance fluctuation under bending is less than 3.6%, indicating a high flexibility of the nanocomposite bundles. The resistance of the nanocomposite bundle had a better linear dependence on the temperature applied between 30 and 150 °C. More importantly, such highest working temperature of 150 °C far exceeded that of other polymer-based temperature sensors previously reported. This suggests that such prepared MWNTs-adsorbed electrospun PA66 nanofiber bundles have great potentials in high temperature detectors.

  3. Carbon Nanotubes-Adsorbed Electrospun PA66 Nanofiber Bundles with Improved Conductivity and Robust Flexibility.

    PubMed

    Guan, Xiaoyang; Zheng, Guoqiang; Dai, Kun; Liu, Chuntai; Yan, Xingru; Shen, Changyu; Guo, Zhanhu

    2016-06-01

    Electrospun polyamide (PA) 66 nanofiber bundles with high conductivity, improved strength, and robust flexibility were successfully manufactured through simply adsorbing multiwall carbon nanotubes (MWNTs) on the surface of electrospun PA66 nanofibers. The highest electrical conductivity (0.2 S/cm) and tensile strength (103.3 MPa) were achieved for the bundles immersed in the suspension with 0.05 wt % MWNTs, indicating the formation of conductive network from adsorbed MWNTs on the surface of PA66 nanofibers. The decrease of porosity for the bundles immersed in the MWNT dispersion and the formation of hydrogen bond between PA66 nanofibers and MWNTs suggest a superb interfacial interaction, which is responsible for the excellent mechanical properties of the nanocomposite bundles. Furthermore, the resistance fluctuation under bending is less than 3.6%, indicating a high flexibility of the nanocomposite bundles. The resistance of the nanocomposite bundle had a better linear dependence on the temperature applied between 30 and 150 °C. More importantly, such highest working temperature of 150 °C far exceeded that of other polymer-based temperature sensors previously reported. This suggests that such prepared MWNTs-adsorbed electrospun PA66 nanofiber bundles have great potentials in high temperature detectors. PMID:27172292

  4. Plasma treatment of carbon fibers: Non-equilibrium dynamic adsorption and its effect on the mechanical properties of RTM fabricated composites

    NASA Astrophysics Data System (ADS)

    Ma, Keming; Wang, Baichen; Chen, Ping; Zhou, Xia

    2011-02-01

    The effect of oxygen plasma treatment on the non-equilibrium dynamic adsorption of the carbon fabric reinforcements in RTM process was studied. 5-Dimethylamino-1-naphthalene-sulfonylchloride (DNS-Cl) was attached to the curing agent to study the change of curing agent content in the epoxy resin matrix. Steady state fluorescence spectroscopy (FS) analysis was used to study this changes in the epoxy resin at the inlet and outlet of the RTM mould, and XPS was used to study the chemical changes on the carbon fiber surfaces introduced by plasma treatment. The interlaminar shear strength (ILSS) and flexural strength were also measured to study the effects of this non-equilibrium dynamic adsorption progress on the mechanical properties of the end products. FS analysis shows that the curing agent adsorbed onto the fiber surface preferentially for untreated carbon fiber, the curing agent content in the resin matrix maintain unchanged after plasma treatment for 3 min and 5 min, but after oxygen plasma treatment for 7 min, the epoxy resin adsorbed onto the fiber surface preferentially. XPS analysis indicated that the oxygen plasma treatment successfully increased some polar functional groups concentration on the carbon fiber surfaces, this changes on the carbon fiber surfaces can change the adsorption ability of carbon fiber to the resin and curing agent. The mechanical properties of the composites were correlated to this results.

  5. Aligning carbon fibers in micro-extruded composite ink

    NASA Astrophysics Data System (ADS)

    Mahajan, Chaitanya G.

    Direct write processes include a wide range of additive manufacturing techniques with the ability to fabricate structures directly onto planar and non-planar surfaces. Most additive manufacturing techniques use unreinforced polymers to produce parts. By adding carbon fiber as a reinforcing material, properties such as mechanical strength, electrical conductivity, and thermal conductivity can be enhanced. Carbon fibers can be long and continuous, or short and discontinuous. The strength of carbon fiber composite parts is greatly increased when the fibers are preferentially aligned. This research focuses on increasing the strength of additively manufactured parts reinforced using discontinuous carbon fibers that have been aligned during the micro extrusion process. A design of experiments (DOE) approach was used to identify significant process parameters affecting fiber alignment. Factors such as the length of carbon fibers, nozzle diameter, fiber loading fraction, air pressure, translational speed and standoff distance were considered. A two dimensional Fast Fourier Transform (2D FFT) was used to quantify the degree of fiber alignment in the extruded composite inks. ImageJ software supported by an oval profile plugin was used with micrographs of printed samples to obtain the carbon fiber alignment values. The optimal value for the factors was derived by identifying the significant main and interaction effects. Based on the results of the DOE, tensile test samples were printed with fibers aligned parallel and perpendicular to the tensile axis. A standard test method for tensile properties of plastic revealed that the extruded parts with fibers aligned along the tensile axis were better in tensile strength and modulus.

  6. Carbon nanotubes on carbon fibers: Synthesis, structures and properties

    NASA Astrophysics Data System (ADS)

    Zhang, Qiuhong

    The interface between carbon fibers (CFs) and the resin matrix in traditional high performance composites is characterized by a large discontinuity in mechanical, electrical, and thermal properties which can cause inefficient energy transfer. Due to the exceptional properties of carbon nanotubes (CNTs), their growth at the surface of carbon fibers is a promising approach to controlling interfacial interactions and achieving the enhanced bulk properties. However, the reactive conditions used to grow carbon nanotubes also have the potential to introduce defects that can degrade the mechanical properties of the carbon fiber (CF) substrate. In this study, using thermal chemical vapor deposition (CVD) method, high density multi-wall carbon nanotubes have been successfully synthesized directly on PAN-based CF surface without significantly compromising tensile properties. The influence of CVD growth conditions on the single CF tensile properties and carbon nanotube (CNT) morphology was investigated. The experimental results revealed that under high temperature growth conditions, the tensile strength of CF was greatly decreased at the beginning of CNT growth process with the largest decrease observed for sized CFs. However, the tensile strength of unsized CFs with CNT was approximately the same as the initial CF at lower growth temperature. The interfacial shear strength of CNT coated CF (CNT/CF) in epoxy was studied by means of the single-fiber fragmentation test. Results of the test indicate an improvement in interfacial shear strength with the addition of a CNT coating. This improvement can most likely be attributed to an increase in the interphase yield strength as well as an improvement in interfacial adhesion due to the presence of the nanotubes. CNT/CF also offers promise as stress and strain sensors in CF reinforced composite materials. This study investigates fundamental mechanical and electrical properties of CNT/CF using nanoindentation method by designed

  7. Adlayer structure dependent ultrafast desorption dynamics in carbon monoxide adsorbed on Pd (111).

    PubMed

    Hong, Sung-Young; Xu, Pan; Camillone, Nina R; White, Michael G; Camillone, Nicholas

    2016-07-01

    We report our ultrafast photoinduced desorption investigation of the coverage dependence of substrate-adsorbate energy transfer in carbon monoxide adlayers on the (111) surface of palladium. As the CO coverage is increased, the adsorption site population shifts from all threefold hollows (up to 0.33 ML), to bridge and near bridge (>0.5 to 0.6 ML) and finally to mixed threefold hollow plus top site (at saturation at 0.75 ML). We show that between 0.24 and 0.75 ML this progression of binding site motifs is accompanied by two remarkable features in the ultrafast photoinduced desorption of the adsorbates: (i) the desorption probability increases roughly two orders magnitude, and (ii) the adsorbate-substrate energy transfer rate observed in two-pulse correlation experiments varies nonmonotonically, having a minimum at intermediate coverages. Simulations using a phenomenological model to describe the adsorbate-substrate energy transfer in terms of frictional coupling indicate that these features are consistent with an adsorption-site dependent electron-mediated energy coupling strength, ηel, that decreases with binding site in the order: three-fold hollow > bridge and near bridge > top site. This weakening of ηel largely counterbalances the decrease in the desorption activation energy that accompanies this progression of adsorption site motifs, moderating what would otherwise be a rise of several orders of magnitude in the desorption probability. Within this framework, the observed energy transfer rate enhancement at saturation coverage is due to interadsorbate energy transfer from the copopulation of molecules bound in three-fold hollows to their top-site neighbors.

  8. Adlayer structure dependent ultrafast desorption dynamics in carbon monoxide adsorbed on Pd (111)

    NASA Astrophysics Data System (ADS)

    Hong, Sung-Young; Xu, Pan; Camillone, Nina R.; White, Michael G.; Camillone, Nicholas

    2016-07-01

    We report our ultrafast photoinduced desorption investigation of the coverage dependence of substrate-adsorbate energy transfer in carbon monoxide adlayers on the (111) surface of palladium. As the CO coverage is increased, the adsorption site population shifts from all threefold hollows (up to 0.33 ML), to bridge and near bridge (>0.5 to 0.6 ML) and finally to mixed threefold hollow plus top site (at saturation at 0.75 ML). We show that between 0.24 and 0.75 ML this progression of binding site motifs is accompanied by two remarkable features in the ultrafast photoinduced desorption of the adsorbates: (i) the desorption probability increases roughly two orders magnitude, and (ii) the adsorbate-substrate energy transfer rate observed in two-pulse correlation experiments varies nonmonotonically, having a minimum at intermediate coverages. Simulations using a phenomenological model to describe the adsorbate-substrate energy transfer in terms of frictional coupling indicate that these features are consistent with an adsorption-site dependent electron-mediated energy coupling strength, ηel, that decreases with binding site in the order: three-fold hollow > bridge and near bridge > top site. This weakening of ηel largely counterbalances the decrease in the desorption activation energy that accompanies this progression of adsorption site motifs, moderating what would otherwise be a rise of several orders of magnitude in the desorption probability. Within this framework, the observed energy transfer rate enhancement at saturation coverage is due to interadsorbate energy transfer from the copopulation of molecules bound in three-fold hollows to their top-site neighbors.

  9. Strong, conductive carbon nanotube fibers as efficient hole collectors.

    PubMed

    Jia, Yi; Li, Xiao; Li, Peixu; Wang, Kunlin; Cao, Anyuan; Wei, Jinquan; Zhu, Hongwei; Wu, Dehai

    2012-02-17

    We present the photovoltaic properties of heterojunctions made from single-walled carbon nanotube (SWNT) fibers and n-type silicon wafers. The use of the opaque SWNT fiber allows photo-generated holes to transport along the axis direction of the fiber. The heterojunction solar cells show conversion efficiencies of up to 3.1% (actual) and 10.6% (nominal) at AM1.5 condition. In addition, the use of strong, environmentally benign carbon nanotube fibers provides excellent structural stability of the photovoltaic devices.

  10. Strong, conductive carbon nanotube fibers as efficient hole collectors

    PubMed Central

    2012-01-01

    We present the photovoltaic properties of heterojunctions made from single-walled carbon nanotube (SWNT) fibers and n-type silicon wafers. The use of the opaque SWNT fiber allows photo-generated holes to transport along the axis direction of the fiber. The heterojunction solar cells show conversion efficiencies of up to 3.1% (actual) and 10.6% (nominal) at AM1.5 condition. In addition, the use of strong, environmentally benign carbon nanotube fibers provides excellent structural stability of the photovoltaic devices. PMID:22340519

  11. Micromechanism of sulfurizing activated carbon and its ability to adsorb mercury

    NASA Astrophysics Data System (ADS)

    Wu, Guofang; Xu, Minren; Liu, Qingcai; Yang, Jian; Ma, Dongran; Lu, Cunfang; Lan, Yuanpei

    2013-11-01

    To eliminate mercury from coal-fired flue gas, sulfurization of carbons has been found to be the most inexpensive approach to solve the problem of environment contamination by mercury. This study focuses on improving the adsorption capacity of activate carbon loaded with elemental sulfur as an active phase and further use in the removal of mercury vapors from fuel gas. In this paper, equipment such as the scanning electron microscope, specific surface area test machine and fluorescence spectrophotometer are employed to study the ability of the S-loaded activated carbon. The results show that unmodified activate carbon has smooth hole surface and uneven distributed hole size. Pore walls of activate carbon modified became rougher and the hole size distribution is asymmetrical. Sulfur is uniformly distributed and is mainly bonded on the surface of the skeleton of activate carbon. In addition, a small amount of granular sulfur was loaded on the surface of the pore walls. Higher temperature creates smaller pore size and larger microporous volume. Improving the process temperature is conducive to the development of micropore and the distribution of sulfur, and a larger amount of small molecular weight sulfur are created, which is helpful in the removal of HgO through chemical adsorption. The optimum modification temperature and holding time is 550 °C and 60 min, which creates the adsorbents of the max absorption capability of 1227.5 μg Hg/g.

  12. Acetylation of oil palm empty fruit bunch fiber as an adsorbent for removal of crude oil.

    PubMed

    Asadpour, Robabeh; Sapari, Nasiman B; Isa, Mohamed Hasnain; Kakooei, Saeid

    2016-06-01

    Removal of oil spillage from the environment is a global concern. Various methods, including the use of fibers as sorbents, have been developed for oil spill control. Oil palm empty fruit bunch (OPEFB) fiber is a plant biomass that may be acetylated by acetic anhydride using N-bromosuccinimide (NBS) as a catalyst; here, the extent of acetylation may be calculated in terms of weight percent gain (WPG). The modified fiber was used to remove Tapis and Arabian crude oils. The optimum time, temperature, and catalyst concentration were 4 h, 120 °C, and 3 %, respectively, and these parameters could achieve an 11.49 % increase in WPG. The optimized parameters improved the adsorption capacity of OPEFB fibers for crude oil removal. The acetylated OPEFB fibers were characterized by using Fourier transform infrared spectroscopy and field emission scanning electron microscopy to observe the functional groups available and morphology. Kinetic and isotherm studies were conducted using different contact times and oil/water ratios. The rate of oil sorption onto the OPEFB fibers can be adequately described by the pseudo-second-order equation. Adsorption studies revealed that adsorption of crude oil on treated OPEFB fiber could be best described by the Langmuir isotherm model.

  13. Evaluation of activated carbon fiber filter for sampling of organochlorine pesticides in environmental water samples.

    PubMed

    Murayama, Hitoshi; Moriyama, Noboru; Mitobe, Hideko; Mukai, Hiroyuki; Takase, Yuuya; Shimizu, Ken ichi; Kitayama, Yoshie

    2003-08-01

    A simple method for quantitative analyses of organic chlorine pesticides (OCPs) in environmental water samples such as rainwater, river water and seawater using activated carbon fiber filters (ACFF) is described. ACFF was used as adsorbent to collect the chemicals in water samples. The collection of OCPs was completed almost for one day by stirring the mixture of the sample and the ACFF chips at room temperature. The adsorbed OCPs on the ACFF could be extracted easily with toluene-ethanol (4:1) mixed solvent. The purified extract by a florisil column chromatograph was followed by the analysis using high-resolution gas chromatograph/high-resolution mass spectrometer. Recoveries of OCPs spiked to actual samples such as rainwater, river water and seawater samples were approximately more than 80%, and the coefficients of variations were within 10%. This method was applied to the actual samples and was confirmed to be applicable for monitoring sub-ng/l level OCPs in environmental water samples.

  14. [Carbon fiber-reinforced plastics as implant materials].

    PubMed

    Bader, R; Steinhauser, E; Rechl, H; Siebels, W; Mittelmeier, W; Gradinger, R

    2003-01-01

    Carbon fiber-reinforced plastics have been used clinically as an implant material for different applications for over 20 years.A review of technical basics of the composite materials (carbon fibers and matrix systems), fields of application,advantages (e.g., postoperative visualization without distortion in computed and magnetic resonance tomography), and disadvantages with use as an implant material is given. The question of the biocompatibility of carbon fiber-reinforced plastics is discussed on the basis of experimental and clinical studies. Selected implant systems made of carbon composite materials for treatments in orthopedic surgery such as joint replacement, tumor surgery, and spinal operations are presented and assessed. Present applications for carbon fiber reinforced plastics are seen in the field of spinal surgery, both as cages for interbody fusion and vertebral body replacement.

  15. Ceria modified activated carbon: an efficient arsenic removal adsorbent for drinking water purification

    NASA Astrophysics Data System (ADS)

    Sawana, Radha; Somasundar, Yogesh; Iyer, Venkatesh Shankar; Baruwati, Babita

    2016-03-01

    Ceria (CeO2) coated powdered activated carbon was synthesized by a single step chemical process and demonstrated to be a highly efficient adsorbent for the removal of both As(III) and As(V) from water without any pre-oxidation process. The formation of CeO2 on the surface of powdered activated carbon was confirmed by X-ray diffraction, Raman spectroscopy and X-ray photoelectron spectroscopy. The percentage of Ce in the adsorbent was confirmed to be 3.5 % by ICP-OES. The maximum removal capacity for As(III) and As(V) was found to be 10.3 and 12.2 mg/g, respectively. These values are comparable to most of the commercially available adsorbents. 80 % of the removal process was completed within 15 min of contact time in a batch process. More than 95 % removal of both As(III) and As(V) was achieved within an hour. The efficiency of removal was not affected by change in pH (5-9), salinity, hardness, organic (1-4 ppm of humic acid) and inorganic anions (sulphate, nitrate, chloride, bicarbonate and fluoride) excluding phosphate. Presence of 100 ppm phosphate reduced the removal significantly from 90 to 18 %. The equilibrium adsorption pattern of both As(III) and As(V) fitted well with the Freundlich model with R 2 values 0.99 and 0.97, respectively. The material shows reusability greater than three times in a batch process (arsenic concentration reduced below 10 ppb from 330 ppb) and a life of at least 100 L in a column study with 80 g material when tested under natural hard water (TDS 1000 ppm, pH 7.8, hardness 600 ppm as CaCO3) spiked with 330 ppb of arsenic.

  16. An investigation of carbon fiber/polyphenylene sulfide adhesion

    SciTech Connect

    Fisher, G.S.; Drzal, L.T.

    1996-12-31

    The level of adhesion between reinforcing fibers and a thermoplastic matrix can have a strong effect on composite mechanical properties. In composites of polyphenylene sulfide (PPS) with carbon fibers, Phillips Petroleum Company has reported an increase in transverse tensile strength from 30 MPa to 74 MPa and an increase in transverse flexural strength from 44 to 141 MPa when extrusion grade PPS resin is replaced with a composite grade resin. Since transverse composite properties are particularly sensitive to adhesion, it was suspected that improved fiber/matrix adhesion could be responsible for the improved mechanical properties. Several factors can affect the adhesion between carbon fibers and a semicrystalline thermoplastic such as PPS. These factors include fiber surface structure and chemistry, adsorption of matrix onto fibers, chemical bonding between fiber and matrix, and morphology of the matrix near the fibers. The objectives of this study were to determine the interfacial shear strengths of several types of carbon fibers with both grades of PPS and to determine which factors affect fiber/matrix adhesion. This will allow the authors to determine whether the differences in composite mechanical properties can be correlated to different levels of adhesion and to identify the key factor(s) that lead to any differences in adhesion.

  17. The Tensile Behavior of High-Strength Carbon Fibers.

    PubMed

    Langston, Tye

    2016-08-01

    Carbon fibers exhibit exceptional properties such as high stiffness and specific strength, making them excellent reinforcements for composite materials. However, it is difficult to directly measure their tensile properties and estimates are often obtained by tensioning fiber bundles or composites. While these macro scale tests are informative for composite design, their results differ from that of direct testing of individual fibers. Furthermore, carbon filament strength also depends on other variables, including the test length, actual fiber diameter, and material flaw distribution. Single fiber tensile testing was performed on high-strength carbon fibers to determine the load and strain at failure. Scanning electron microscopy was also conducted to evaluate the fiber surface morphology and precisely measure each fiber's diameter. Fiber strength was found to depend on the test gage length and in an effort to better understand the overall expected performance of these fibers at various lengths, statistical weak link scaling was performed. In addition, the true Young's modulus was also determined by taking the system compliance into account. It was found that all properties (tensile strength, strain to failure, and Young's modulus) matched very well with the manufacturers' reported values at 20 mm gage lengths, but deviated significantly at other lengths.

  18. The Tensile Behavior of High-Strength Carbon Fibers.

    PubMed

    Langston, Tye

    2016-08-01

    Carbon fibers exhibit exceptional properties such as high stiffness and specific strength, making them excellent reinforcements for composite materials. However, it is difficult to directly measure their tensile properties and estimates are often obtained by tensioning fiber bundles or composites. While these macro scale tests are informative for composite design, their results differ from that of direct testing of individual fibers. Furthermore, carbon filament strength also depends on other variables, including the test length, actual fiber diameter, and material flaw distribution. Single fiber tensile testing was performed on high-strength carbon fibers to determine the load and strain at failure. Scanning electron microscopy was also conducted to evaluate the fiber surface morphology and precisely measure each fiber's diameter. Fiber strength was found to depend on the test gage length and in an effort to better understand the overall expected performance of these fibers at various lengths, statistical weak link scaling was performed. In addition, the true Young's modulus was also determined by taking the system compliance into account. It was found that all properties (tensile strength, strain to failure, and Young's modulus) matched very well with the manufacturers' reported values at 20 mm gage lengths, but deviated significantly at other lengths. PMID:27278219

  19. Activated carbon fiber composite material and method of making

    DOEpatents

    Burchell, Timothy D.; Weaver, Charles E.; Chilcoat, Bill R.; Derbyshire, Frank; Jagtoyen, Marit

    2000-01-01

    An activated carbon fiber composite for separation and purification, or catalytic processing of fluids is described. The activated composite comprises carbon fibers rigidly bonded to form an open, permeable, rigid monolith capable of being formed to near-net-shape. Separation and purification of gases are effected by means of a controlled pore structure that is developed in the carbon fibers contained in the composite. The open, permeable structure allows the free flow of gases through the monolith accompanied by high rates of adsorption. By modification of the pore structure and bulk density the composite can be rendered suitable for applications such as gas storage, catalysis, and liquid phase processing.

  20. Activated carbon fiber composite material and method of making

    DOEpatents

    Burchell, Timothy D.; Weaver, Charles E.; Chilcoat, Bill R.; Derbyshire, Frank; Jagtoyen, Marit

    2001-01-01

    An activated carbon fiber composite for separation and purification, or catalytic processing of fluids is described. The activated composite comprises carbon fibers rigidly bonded to form an open, permeable, rigid monolith capable of being formed to near-net-shape. Separation and purification of gases are effected by means of a controlled pore structure that is developed in the carbon fibers contained in the composite. The open, permeable structure allows the free flow of gases through the monolith accompanied by high rates of adsorption. By modification of the pore structure and bulk density the composite can be rendered suitable for applications such as gas storage, catalysis, and liquid phase processing.

  1. Oxidation of Carbon Fibers in Water Vapor Studied

    NASA Technical Reports Server (NTRS)

    Opila, Elizabeth J.

    2003-01-01

    T-300 carbon fibers (BP Amoco Chemicals, Greenville, SC) are a common reinforcement for silicon carbide composite materials, and carbon-fiber-reinforced silicon carbide composites (C/SiC) are proposed for use in space propulsion applications. It has been shown that the time to failure for C/SiC in stressed oxidation tests is directly correlated with the fiber oxidation rate (ref. 1). To date, most of the testing of these fibers and composites has been conducted in oxygen or air environments; however, many components for space propulsion, such as turbopumps, combustors, and thrusters, are expected to operate in hydrogen and water vapor (H2/H2O) environments with very low oxygen contents. The oxidation rate of carbon fibers in conditions representative of space propulsion environments is, therefore, critical for predicting component lifetimes for real applications. This report describes experimental results that demonstrate that, under some conditions, lower oxidation rates of carbon fibers are observed in water vapor and H2/H2O environments than are found in oxygen or air. At the NASA Glenn Research Center, the weight loss of the fibers was studied as a function of water pressure, temperature, and gas velocity. The rate of carbon fiber oxidation was determined, and the reaction mechanism was identified.

  2. Ultra-Thin Optically Transparent Carbon Electrodes Produced from Layers of Adsorbed Proteins

    PubMed Central

    Alharthi, Sarah A.; Benavidez, Tomas E.; Garcia, Carlos D.

    2013-01-01

    This work describes a simple, versatile, and inexpensive procedure to prepare optically transparent carbon electrodes, using proteins as precursors. Upon adsorption, the protein-coated substrates were pyrolyzed under reductive conditions (5% H2) to form ultra-thin, conductive electrodes. Because proteins spontaneously adsorb to interfaces forming uniform layers, the proposed method does not require a precise control of the preparation conditions, specialized instrumentation, or expensive precursors. The resulting electrodes were characterized by a combination of electrochemical, optical, and spectroscopic means. As a proof-of-concept, the optically-transparent electrodes were also used as substrate for the development of an electrochemical glucose biosensor. The proposed films represent a convenient alternative to more sophisticated, and less available, carbon-based nanomaterials. Furthermore, these films could be formed on a variety of substrates, without classical limitations of size or shape. PMID:23421732

  3. Economical and ecological comparison of granular activated carbon (GAC) adsorber refill strategies.

    PubMed

    Bayer, Peter; Heuer, Edda; Karl, Ute; Finkel, Michael

    2005-05-01

    Technical constraints can leave a considerable freedom in the design of a technology, production or service strategy. Choosing between economical or ecological decision criteria then characteristically leads to controversial solutions of ideal systems. For the adaptation of granular-activated carbon (GAC) fixed beds, various technical factors determine the adsorber volume required to achieve a desired service life. In considering carbon replacement and recycling, a variety of refill strategies are available that differ in terms of refill interval, respective adsorber volume, and time-dependent use of virgin, as well as recycled GAC. Focusing on the treatment of contaminant groundwater, we compare cost-optimal reactor configurations and refill strategies to the ecologically best alternatives. Costs and consumption of GAC are quantified within a technical-economical framework. The emissions from GAC production out of hard coal, transport and recycling are equally derived through a life cycle impact assessment. It is shown how high discount rates lead to a preference of small fixed-bed volumes, and accordingly, a high number of refills. For fixed discount rates, the investigation reveals that both the economical as well as ecological assessment of refill strategies are especially sensitive to the relative valuation of virgin and recycled GAC. Since recycling results in economic and ecological benefits, optimized systems thus may differ only slightly.

  4. Polyethylenimine carbon nanotube fiber electrodes for enhanced detection of neurotransmitters.

    PubMed

    Zestos, Alexander G; Jacobs, Christopher B; Trikantzopoulos, Elefterios; Ross, Ashley E; Venton, B Jill

    2014-09-01

    Carbon nanotube (CNT)-based microelectrodes have been investigated as alternatives to carbon-fiber microelectrodes for the detection of neurotransmitters because they are sensitive, exhibit fast electron transfer kinetics, and are more resistant to surface fouling. Wet spinning CNTs into fibers using a coagulating polymer produces a thin, uniform fiber that can be fabricated into an electrode. CNT fibers formed in poly(vinyl alcohol) (PVA) have been used as microelectrodes to detect dopamine, serotonin, and hydrogen peroxide. In this study, we characterize microelectrodes with CNT fibers made in polyethylenimine (PEI), which have much higher conductivity than PVA-CNT fibers. PEI-CNT fibers have lower overpotentials and higher sensitivities than PVA-CNT fiber microelectrodes, with a limit of detection of 5 nM for dopamine. The currents for dopamine were adsorption controlled at PEI-CNT fiber microelectrodes, independent of scan repetition frequency, and stable for over 10 h. PEI-CNT fiber microelectrodes were resistant to surface fouling by serotonin and the metabolite interferant 5-hydroxyindoleacetic acid (5-HIAA). No change in sensitivity was observed for detection of serotonin after 30 flow injection experiments or after 2 h in 5-HIAA for PEI-CNT electrodes. The antifouling properties were maintained in brain slices when serotonin was exogenously applied multiple times or after bathing the slice in 5-HIAA. Thus, PEI-CNT fiber electrodes could be useful for the in vivo monitoring of neurochemicals. PMID:25117550

  5. Strong, light, multifunctional fibers of carbon nanotubes with ultrahigh conductivity.

    PubMed

    Behabtu, Natnael; Young, Colin C; Tsentalovich, Dmitri E; Kleinerman, Olga; Wang, Xuan; Ma, Anson W K; Bengio, E Amram; ter Waarbeek, Ron F; de Jong, Jorrit J; Hoogerwerf, Ron E; Fairchild, Steven B; Ferguson, John B; Maruyama, Benji; Kono, Junichiro; Talmon, Yeshayahu; Cohen, Yachin; Otto, Marcin J; Pasquali, Matteo

    2013-01-11

    Broader applications of carbon nanotubes to real-world problems have largely gone unfulfilled because of difficult material synthesis and laborious processing. We report high-performance multifunctional carbon nanotube (CNT) fibers that combine the specific strength, stiffness, and thermal conductivity of carbon fibers with the specific electrical conductivity of metals. These fibers consist of bulk-grown CNTs and are produced by high-throughput wet spinning, the same process used to produce high-performance industrial fibers. These scalable CNT fibers are positioned for high-value applications, such as aerospace electronics and field emission, and can evolve into engineered materials with broad long-term impact, from consumer electronics to long-range power transmission. PMID:23307737

  6. Potential release of fibers from burning carbon composites. [aircraft fires

    NASA Technical Reports Server (NTRS)

    Bell, V. L.

    1980-01-01

    A comprehensive experimental carbon fiber source program was conducted to determine the potential for the release of conductive carbon fibers from burning composites. Laboratory testing determined the relative importance of several parameters influencing the amounts of single fibers released, while large-scale aviation jet fuel pool fires provided realistic confirmation of the laboratory data. The dimensions and size distributions of fire-released carbon fibers were determined, not only for those of concern in an electrical sense, but also for those of potential interest from a health and environmental standpoint. Fire plume and chemistry studies were performed with large pool fires to provide an experimental input into an analytical modelling of simulated aircraft crash fires. A study of a high voltage spark system resulted in a promising device for the detection, counting, and sizing of electrically conductive fibers, for both active and passive modes of operation.

  7. Method for fabricating light weight carbon-bonded carbon fiber composites

    DOEpatents

    Wrenn, Jr., George E.; Abbatiello, Leonard A.; Lewis, Jr., John

    1989-01-01

    Ultralight carbon-bonded carbon fiber composites of densities in the range of about 0.04 to 0.10 grams per cubic centimeter are fabricated by forming an aqueous slurry of carbonaceous fibers which include carbonized fibers and 0-50 weight percent fugitive fibers and a particulate thermosetting resin precursor. The slurry is brought into contact with a perforated mandrel and the water is drained from the slurry through the perforations at a controlled flow rate of about 0.03 to 0.30 liters per minutes per square inch of mandrel surface. The deposited billet of fibers and resin precursor is heated to cure the resin precursor to bind the fibers together, removed from the mandrel, and then the resin and fugitive fibers, if any, are carbonized.

  8. Method for fabricating light weight carbon-bonded carbon fiber composites

    DOEpatents

    Wrenn, G.E. Jr.; Abbatiello, L.A.; Lewis, J. Jr.

    1987-06-17

    The invention is directed to the fabrication of ultralight carbon- bonded carbon fiber composites of densities in the range of about 0. 04 to 0.10 grams per cubic centimeter. The composites are fabricated by forming an aqueous slurry of carbonaceous fibers which include carbonized fibers and 0-50 weight percent fugitive fibers and a particulate thermosetting resin precursor. The slurry is brought into contact with a perforated mandrel and the water is drained from the slurry through the perforations at a controlled flow rate of about 0. 03 to 0.30 liters per minutes per square inch of a mandrel surface. The deposited billet of fibers and resin precursor is heated to cure the resin precursor to bind the fibers together, removed from the mandrel, and then the resin and fugitive fibers, if any, are carbonized.

  9. The surface properties of carbon fibers and their adhesion to organic polymers

    NASA Technical Reports Server (NTRS)

    Bascom, W. D.; Drzal, L. T.

    1987-01-01

    The state of knowledge of the surface properties of carbon fibers is reviewed, with emphasis on fiber/matrix adhesion in carbon fiber reinforced plastics. Subjects treated include carbon fiber structure and chemistry, techniques for the study of the fiber surface, polymer/fiber bond strength and its measurement, variations in polymer properties in the interphase, and the influence of fiber matrix adhesion on composite mechanical properties. Critical issues are summarized and search recommendations are made.

  10. Adsorption characteristics of activated carbon fibers (ACFs) for toluene: application in respiratory protection.

    PubMed

    Balanay, Jo Anne G; Bartolucci, Alfred A; Lungu, Claudiu T

    2014-01-01

    Granular activated carbon (GAC) is currently the standard adsorbent in respirators against several gases and vapors because of its efficiency, low cost, and available technology. However, a drawback of GAC due to its granular form is its need for containment, adding weight and bulkiness to respirators. This makes respirators uncomfortable to wear, resulting in poor compliance in their use. Activated carbon fibers (ACF) are considered viable alternative adsorbent materials for developing thinner, light-weight, and efficient respirators because of their larger surface area, lighter weight, and fabric form. This study aims to determine the critical bed depth and adsorption capacity of different types of commercially available ACFs for toluene to understand how thin a respirator can be and the service life of the adsorbents, respectively. ACF in cloth (ACFC) and felt (ACFF) forms with three different surface areas per form were tested. Each ACF type was challenged with six concentrations of toluene (50, 100, 200, 300, 400, 500 ppm) at constant air temperature (23°C), relative humidity (50%), and airflow (16 LPM) at different adsorbent weights and bed depths. Breakthrough data were obtained for each adsorbent using gas chromatography with flame ionization detector. The ACFs' surface areas were measured by an automatic physisorption analyzer. The results showed that ACFC has a lower critical bed depth and higher adsorption capacity compared to ACFF with similar surface area for each toluene concentration. Among the ACF types, ACFC2000 (cloth with the highest measured surface area of 1614 ± 5 m(2)/g) has one of the lowest critical bed depths (ranging from 0.11-0.22 cm) and has the highest adsorption capacity (ranging from 595-878 mg/g). Based on these studied adsorption characteristics, it is concluded that ACF has great potential for application in respiratory protection against toluene, particularly the ACFC2000, which is the best candidate for developing thinner and

  11. Designed amyloid fibers as materials for selective carbon dioxide capture

    PubMed Central

    Li, Dan; Furukawa, Hiroyasu; Deng, Hexiang; Liu, Cong; Yaghi, Omar M.; Eisenberg, David S.

    2014-01-01

    New materials capable of binding carbon dioxide are essential for addressing climate change. Here, we demonstrate that amyloids, self-assembling protein fibers, are effective for selective carbon dioxide capture. Solid-state NMR proves that amyloid fibers containing alkylamine groups reversibly bind carbon dioxide via carbamate formation. Thermodynamic and kinetic capture-and-release tests show the carbamate formation rate is fast enough to capture carbon dioxide by dynamic separation, undiminished by the presence of water, in both a natural amyloid and designed amyloids having increased carbon dioxide capacity. Heating to 100 °C regenerates the material. These results demonstrate the potential of amyloid fibers for environmental carbon dioxide capture. PMID:24367077

  12. Evaluation of Equipment Vulnerability and Potential Shock Hazards. [carbon fibers

    NASA Technical Reports Server (NTRS)

    Taback, I.

    1980-01-01

    The vulnerability of electric equipment to carbon fibers released from aircraft accidents is investigated and the parameters affecting vulnerability are discussed. The shock hazard for a hypothetical set of accidents is computed.

  13. A carbon fiber exposure test facility and instrumentation

    NASA Technical Reports Server (NTRS)

    Newcomb, A. L., Jr.

    1980-01-01

    A facility to evaluate the risk associated with the exposure of electrical and electronic equipment to airborne carbon/graphite fibers was constructed. A wide variety of instrumentation is described and illustrated.

  14. The Importance of Carbon Fiber to Polymer Additive Manufacturing

    SciTech Connect

    Love, Lonnie J; Kunc, Vlastimil; Rios, Orlando; Duty, Chad E; Post, Brian K; Blue, Craig A

    2014-01-01

    Additive manufacturing holds tremendous promise in terms of revolutionizing manufacturing. However, fundamental hurdles limit mass adoption of the technology. First, production rates are extremely low. Second, the physical size of parts is generally small, less than a cubic foot. Third, while there is much excitement about metal additive manufacturing, the major growth area is in polymer additive manufacturing systems. Unfortunately, the mechanical properties of the polymer parts are poor, limiting the potential for direct part replacement. To address this issue, we describe three benefits of blending carbon fiber with polymer additive manufacturing. First, development of carbon fiber reinforced polymers for additive manufacturing achieves specific strengths approaching aerospace quality aluminum. Second, carbon fiber radically changes the behavior of the material during deposition, enabling large scale, out-of-the-oven, high deposition rate manufacturing. Finally, carbon fiber technology and additive manufacturing complement each other. Merging the two manufacturing processes enables the construction of complex components that would not be possible otherwise.

  15. Assessment of risk to Boeing commerical transport aircraft from carbon fibers. [fiber release from graphite/epxoy materials

    NASA Technical Reports Server (NTRS)

    Clarke, C. A.; Brown, E. L.

    1980-01-01

    The possible effects of free carbon fibers on aircraft avionic equipment operation, removal costs, and safety were investigated. Possible carbon fiber flow paths, flow rates, and transfer functions into the Boeing 707, 727, 737, 747 aircraft and potentially vulnerable equipment were identified. Probabilities of equipment removal and probabilities of aircraft exposure to carbon fiber were derived.

  16. International Space Station (ISS) Carbon Dioxide Removal Assembly (CDRA) Desiccant/Adsorbent Bed (DAB) Orbital Replacement Unit (ORU) Redesign

    NASA Technical Reports Server (NTRS)

    Reysa, Richard P.; Lumpkin, John P.; Sherif, Dian El; Kay, Robert; Williams, David E.

    2007-01-01

    The Carbon Dioxide Removal Assembly (CDRA) is a part of the International Space Station (ISS) Environmental Control and Life Support (ECLS) system. The CDRA provides carbon dioxide (CO2) removal from the ISS on-orbit modules. Currently, the CDRA is the secondary removal system on the ISS, with the primary system being the Russian Vozdukh. Within the CDRA are two desiccant/adsorbent beds (DAB), which perform the carbon dioxide removal function. The DAB adsorbent containment approach required improvements with respect to adsorbent containment. These improvements were implemented through a redesign program and have been implemented on units returning from orbit. This paper presents a DAB design modification implementation description, a hardware performance comparison between the unmodified and modified DAB configurations, and a description of the modified DAB hardware implementation into the on-orbit CDRA.

  17. Transforming Pristine Carbon Fiber Tows into High Performance Solid-State Fiber Supercapacitors.

    PubMed

    Yu, Dingshan; Zhai, Shengli; Jiang, Wenchao; Goh, Kunli; Wei, Li; Chen, Xudong; Jiang, Rongrong; Chen, Yuan

    2015-09-01

    A facile activation strategy can transform pristine carbon fiber tows into high-performance fiber electrodes with a specific capacitance of 14.2 F cm(-3) . The knottable fiber supercapacitor shows an energy density of 0.35 mW h cm(-3) , an ultrahigh power density of 3000 mW cm(-3) , and a remarkable capacitance retention of 68%, when the scan rate increases from 10 to 1000 mV s(-1) . PMID:26179414

  18. Nanowire modified carbon fibers for enhanced electrical energy storage

    NASA Astrophysics Data System (ADS)

    Shuvo, Mohammad Arif Ishtiaque; (Bill) Tseng, Tzu-Liang; Ashiqur Rahaman Khan, Md.; Karim, Hasanul; Morton, Philip; Delfin, Diego; Lin, Yirong

    2013-09-01

    The study of electrochemical super-capacitors has become one of the most attractive topics in both academia and industry as energy storage devices because of their high power density, long life cycles, and high charge/discharge efficiency. Recently, there has been increasing interest in the development of multifunctional structural energy storage devices such as structural super-capacitors for applications in aerospace, automobiles, and portable electronics. These multifunctional structural super-capacitors provide structures combining energy storage and load bearing functionalities, leading to material systems with reduced volume and/or weight. Due to their superior materials properties, carbon fiber composites have been widely used in structural applications for aerospace and automotive industries. Besides, carbon fiber has good electrical conductivity which will provide lower equivalent series resistance; therefore, it can be an excellent candidate for structural energy storage applications. Hence, this paper is focused on performing a pilot study for using nanowire/carbon fiber hybrids as building materials for structural energy storage materials; aiming at enhancing the charge/discharge rate and energy density. This hybrid material combines the high specific surface area of carbon fiber and pseudo-capacitive effect of metal oxide nanowires, which were grown hydrothermally in an aligned fashion on carbon fibers. The aligned nanowire array could provide a higher specific surface area that leads to high electrode-electrolyte contact area thus fast ion diffusion rates. Scanning Electron Microscopy and X-Ray Diffraction measurements are used for the initial characterization of this nanowire/carbon fiber hybrid material system. Electrochemical testing is performed using a potentio-galvanostat. The results show that gold sputtered nanowire carbon fiber hybrid provides 65.9% higher energy density than bare carbon fiber cloth as super-capacitor.

  19. Development of Commodity Grade, Lower Cost Carbon Fiber - Commercial Applications

    SciTech Connect

    Warren, Charles David; Paulauskas, Felix L; Baker, Frederick S; Eberle, Cliff; Naskar, Amit K

    2009-01-01

    In pursuit of the goal to produce ultra-lightweight fuel efficient vehicles, there has been great excitement during the last few years about the potential for using carbon fiber reinforced composites in high volume applications. Currently, the greatest hurdle that inhibits wider implementation of carbon fiber composites in transportation is the high cost of the fiber when compared to other candidate materials. As part of the United States Department of Energy s FreedomCAR initiative, significant research is being conducted to develop lower cost, high volume technologies for producing carbon fiber. This paper will highlight the on-going research in this area. Through Department of Energy (DOE) sponsorship, Oak Ridge National Laboratory (ORNL) and its partners have been working with the US Automotive Composites Consortium (ACC) to develop technologies that would enable the production of carbon fiber at 5-7 dollars per pound. Achievement of this cost goal would allow the introduction of carbon fiber based composites into a greater number of applications for future vehicles. The approach has necessitated the development of both alternative precursors and more efficient production methods. Alternative precursors under investigation include textile grade polyacrylonitrile (PAN) fibers and fibers from lignin-based feedstocks. Previously, as part of the research program, Hexcel Corporation developed the science necessary to allow textile grade PAN to be used as a precursor rather than typical carbon fiber grade precursors. Efforts are also underway to develop carbon fiber precursors from lignin-based feedstocks. ORNL and its partners are working on this effort with domestic pulp and paper producers. In terms of alternative production methods, ORNL has developed a microwave-based carbonization unit that can process pre-oxidized fiber at over 200 inches per minute. ORNL has also developed a new method of high speed oxidation and a new method for precursor stabilization

  20. Carbon fiber enhanced bioelectricity generation in soil microbial fuel cells.

    PubMed

    Li, Xiaojing; Wang, Xin; Zhao, Qian; Wan, Lili; Li, Yongtao; Zhou, Qixing

    2016-11-15

    The soil microbial fuel cell (MFC) is a promising biotechnology for the bioelectricity recovery as well as the remediation of organics contaminated soil. However, the electricity production and the remediation efficiency of soil MFC are seriously limited by the tremendous internal resistance of soil. Conductive carbon fiber was mixed with petroleum hydrocarbons contaminated soil and significantly enhanced the performance of soil MFC. The maximum current density, the maximum power density and the accumulated charge output of MFC mixed carbon fiber (MC) were 10, 22 and 16 times as high as those of closed circuit control due to the carbon fiber productively assisted the anode to collect the electron. The internal resistance of MC reduced by 58%, 83% of which owed to the charge transfer resistance, resulting in a high efficiency of electron transfer from soil to anode. The degradation rates of total petroleum hydrocarbons enhanced by 100% and 329% compared to closed and opened circuit controls without the carbon fiber respectively. The effective range of remediation and the bioelectricity recovery was extended from 6 to 20cm with the same area of air-cathode. The mixed carbon fiber apparently enhanced the bioelectricity generation and the remediation efficiency of soil MFC by means of promoting the electron transfer rate from soil to anode. The use of conductively functional materials (e.g. carbon fiber) is very meaningful for the remediation and bioelectricity recovery in the bioelectrochemical remediation. PMID:27162144

  1. Carbon fiber enhanced bioelectricity generation in soil microbial fuel cells.

    PubMed

    Li, Xiaojing; Wang, Xin; Zhao, Qian; Wan, Lili; Li, Yongtao; Zhou, Qixing

    2016-11-15

    The soil microbial fuel cell (MFC) is a promising biotechnology for the bioelectricity recovery as well as the remediation of organics contaminated soil. However, the electricity production and the remediation efficiency of soil MFC are seriously limited by the tremendous internal resistance of soil. Conductive carbon fiber was mixed with petroleum hydrocarbons contaminated soil and significantly enhanced the performance of soil MFC. The maximum current density, the maximum power density and the accumulated charge output of MFC mixed carbon fiber (MC) were 10, 22 and 16 times as high as those of closed circuit control due to the carbon fiber productively assisted the anode to collect the electron. The internal resistance of MC reduced by 58%, 83% of which owed to the charge transfer resistance, resulting in a high efficiency of electron transfer from soil to anode. The degradation rates of total petroleum hydrocarbons enhanced by 100% and 329% compared to closed and opened circuit controls without the carbon fiber respectively. The effective range of remediation and the bioelectricity recovery was extended from 6 to 20cm with the same area of air-cathode. The mixed carbon fiber apparently enhanced the bioelectricity generation and the remediation efficiency of soil MFC by means of promoting the electron transfer rate from soil to anode. The use of conductively functional materials (e.g. carbon fiber) is very meaningful for the remediation and bioelectricity recovery in the bioelectrochemical remediation.

  2. Tensile Properties of Polyimide Composites Incorporating Carbon Nanotubes-Grafted and Polyimide-Coated Carbon Fibers

    NASA Astrophysics Data System (ADS)

    Naito, Kimiyoshi

    2014-09-01

    The tensile properties and fracture behavior of polyimide composite bundles incorporating carbon nanotubes-grafted (CNT-grafted) and polyimide-coated (PI-coated) high-tensile-strength polyacrylonitrile (PAN)-based (T1000GB), and high-modulus pitch-based (K13D) carbon fibers were investigated. The CNT were grown on the surface of the carbon fibers by chemical vapor deposition. The pyromellitic dianhydride/4,4'-oxydianiline PI nanolayer coating was deposited on the surface of the carbon fiber by high-temperature vapor deposition polymerization. The results clearly demonstrate that CNT grafting and PI coating were effective for improving the Weibull modulus of T1000GB PAN-based and K13D pitch-based carbon fiber bundle composites. In addition, the average tensile strength of the PI-coated T1000GB carbon fiber bundle composites was also higher than that of the as-received carbon fiber bundle composites, while the average tensile strength of the CNT-grafted T1000GB, K13D, and the PI-coated K13D carbon fiber bundle composites was similar to that of the as-received carbon fiber bundle composites.

  3. Carbon Fiber Reinforced Carbon Composite Rotary Valve for an Internal Combustion Engine

    NASA Technical Reports Server (NTRS)

    Northam, G.Burton (Inventor); Ransone, Philip O. (Inventor); Rivers, H. Kevin (Inventor)

    2000-01-01

    Carbon fiber reinforced carbon composite rotary sleeve, and disc valves for internal combustion engines and the like are disclosed. The valves are formed from knitted or braided or wrap-locked carbon fiber shapes. Also disclosed are valves fabricated from woven carbon fibers and from molded carbon matrix material. The valves of the present invention with their very low coefficient of thermal expansion and excellent thermal and self-lubrication properties do not present the sealing and lubrication problems that have prevented rotary sleeve and disc valves from operating efficiently and reliably in the past. Also disclosed are a sealing tang to further improve sealing capabilities and anti-oxidation treatments.

  4. Carbon Fiber Reinforced Carbon Composites Rotary Valves for Internal Combustion Engines

    NASA Technical Reports Server (NTRS)

    Northam, G. Burton (Inventor); Ransone, Philip O. (Inventor); Rivers, H. Kevin (Inventor)

    1999-01-01

    Carbon fiber reinforced carbon composite rotary, sleeve, and disc valves for internal combustion engines and the like are disclosed. The valves are formed from knitted or braided or warp-locked carbon fiber shapes. Also disclosed are valves fabricated from woven carbon fibers and from molded carbon matrix material. The valves of the present invention with their very low coefficient of thermal expansion and excellent thermal and self-lubrication properties, do not present the sealing and lubrication problems that have prevented rotary, sleeve, and disc valves from operating efficiently and reliably in the past. Also disclosed are a sealing tang to further improve sealing capabilities and anti-oxidation treatments.

  5. Improved high modulus carbon fibers. [elimination of hazards due to electrical properties

    NASA Technical Reports Server (NTRS)

    Ansell, G. S.; Chen, S. H.; Diffendorf, R. J.; Kim, C. M.; Lemaistre, C. W.; Lyman, C. E.; Shen, T. H.; Wang, J. J. H.

    1979-01-01

    Carbon fibers which are electrically insulating but still maintain the mechanical properties of the original carbon fibers were investigated. Three approaches were taken to increase the electrical resistance of carbon fibers: (1) boron nitride (BN) coatings; (2) doping of carbon fibers to alter their electrical properties; and (3) low temperature final heat treatment. The structure of carbon fibers and its effect upon properties was also studied. Results are presented.

  6. Easily regenerable solid adsorbents based on polyamines for carbon dioxide capture from the air.

    PubMed

    Goeppert, Alain; Zhang, Hang; Czaun, Miklos; May, Robert B; Prakash, G K Surya; Olah, George A; Narayanan, S R

    2014-05-01

    Adsorbents prepared easily by impregnation of fumed silica with polyethylenimine (PEI) are promising candidates for the capture of CO2 directly from the air. These inexpensive adsorbents have high CO2 adsorption capacity at ambient temperature and can be regenerated in repeated cycles under mild conditions. Despite the very low CO2 concentration, they are able to scrub efficiently all CO2 out of the air in the initial hours of the experiments. The influence of parameters such as PEI loading, adsorption and desorption temperature, particle size, and PEI molecular weight on the adsorption behavior were investigated. The mild regeneration temperatures required could allow the use of waste heat available in many industrial processes as well as solar heat. CO2 adsorption from the air has a number of applications. Removal of CO2 from a closed environment, such as a submarine or space vehicles, is essential for life support. The supply of CO2-free air is also critical for alkaline fuel cells and batteries. Direct air capture of CO2 could also help mitigate the rising concerns about atmospheric CO2 concentration and associated climatic changes, while, at the same time, provide the first step for an anthropogenic carbon cycle.

  7. Easily regenerable solid adsorbents based on polyamines for carbon dioxide capture from the air.

    PubMed

    Goeppert, Alain; Zhang, Hang; Czaun, Miklos; May, Robert B; Prakash, G K Surya; Olah, George A; Narayanan, S R

    2014-05-01

    Adsorbents prepared easily by impregnation of fumed silica with polyethylenimine (PEI) are promising candidates for the capture of CO2 directly from the air. These inexpensive adsorbents have high CO2 adsorption capacity at ambient temperature and can be regenerated in repeated cycles under mild conditions. Despite the very low CO2 concentration, they are able to scrub efficiently all CO2 out of the air in the initial hours of the experiments. The influence of parameters such as PEI loading, adsorption and desorption temperature, particle size, and PEI molecular weight on the adsorption behavior were investigated. The mild regeneration temperatures required could allow the use of waste heat available in many industrial processes as well as solar heat. CO2 adsorption from the air has a number of applications. Removal of CO2 from a closed environment, such as a submarine or space vehicles, is essential for life support. The supply of CO2-free air is also critical for alkaline fuel cells and batteries. Direct air capture of CO2 could also help mitigate the rising concerns about atmospheric CO2 concentration and associated climatic changes, while, at the same time, provide the first step for an anthropogenic carbon cycle. PMID:24644023

  8. Cadmium telluride nanoparticles loaded on activated carbon as adsorbent for removal of sunset yellow

    NASA Astrophysics Data System (ADS)

    Ghaedi, M.; Hekmati Jah, A.; Khodadoust, S.; Sahraei, R.; Daneshfar, A.; Mihandoost, A.; Purkait, M. K.

    2012-05-01

    Adsorption is a promising technique for decolorization of effluents of textile dyeing industries but its application is limited due to requirement of high amounts of adsorbent required. The objective of this study was to assess the potential of cadmium telluride nanoparticles loaded onto activated carbon (CdTN-AC) for the removal of sunset yellow (SY) dye from aqueous solution. Adsorption studies were conducted in a batch mode varying solution pH, contact time, initial dye concentration, CdTN-AC dose, and temperature. In order to investigate the efficiency of SY adsorption on CdTN-AC, pseudo-first-order, pseudo-second-order, Elovich, and intra-particle diffusion kinetic models were studied. It was observed that the pseudo-second-order kinetic model fits better than other kinetic models with good correlation coefficient. Equilibrium data were fitted to the Langmuir model. Thermodynamic parameters such as enthalpy, entropy, activation energy, and sticking probability were also calculated. It was found that the sorption of SY onto CdTN-AC was spontaneous and endothermic in nature. The proposed adsorbent is applicable for SY removal from waste of real effluents including pea-shooter, orange drink and jelly banana with efficiency more than 97%.

  9. Easily Regenerable Solid Adsorbents Based on Polyamines for Carbon Dioxide Capture from the Air

    SciTech Connect

    Goeppert, A; Zhang, H; Czaun, M; May, RB; Prakash, GKS; Olah, GA; Narayanan, SR

    2014-03-18

    Adsorbents prepared easily by impregnation of fumed silica with polyethylenimine (PEI) are promising candidates for the capture of CO2 directly from the air. These inexpensive adsorbents have high CO2 adsorption capacity at ambient temperature and can be regenerated in repeated cycles under mild conditions. Despite the very low CO2 concentration, they are able to scrub efficiently all CO2 out of the air in the initial hours of the experiments. The influence of parameters such as PEI loading, adsorption and desorption temperature, particle size, and PEI molecular weight on the adsorption behavior were investigated. The mild regeneration temperatures required could allow the use of waste heat available in many industrial processes as well as solar heat. CO2 adsorption from the air has a number of applications. Removal of CO2 from a closed environment, such as a submarine or space vehicles, is essential for life support. The supply of CO2-free air is also critical for alkaline fuel cells and batteries. Direct air capture of CO2 could also help mitigate the rising concerns about atmospheric CO2 concentration and associated climatic changes, while, at the same time, provide the first step for an anthropogenic carbon cycle.

  10. Formation and composition of adsorbates on hydrophobic carbon surfaces from aqueous laccase-maltodextrin mixture suspension

    NASA Astrophysics Data System (ADS)

    Corrales Ureña, Yendry Regina; Lisboa-Filho, Paulo Noronha; Szardenings, Michael; Gätjen, Linda; Noeske, Paul-Ludwig Michael; Rischka, Klaus

    2016-11-01

    A robust procedure for the surface bio-functionalization of carbon surfaces was developed. It consists on the modification of carbon materials in contact with an aqueous suspension of the enzyme laccase from Trametes versicolor and the lyophilization agent maltodextrin, with the pH value adjusted close to the isoelectric point of the enzyme. We report in-situ investigations applying Quartz Crystal Microbalance with Dissipation (QCM-D) for carbon-coated sensor surfaces and, moreover, ex-situ measurements with static contact angle measurements, X-ray Photoelectron Spectroscopy (XPS) and Scanning Force Microscopy (SFM) for smooth Highly Oriented Pyrolytic Graphite (HOPG) substrates, for contact times between the enzyme formulation and the carbon material surface ranging from 20 s to 24 h. QCM-D studies reveals the formation of rigid layer of biomaterial, a few nanometers thin, which shows a strongly improved wettability of the substrate surface upon contact angle measurements. Following spectroscopic characterization, these layers are composed of mixtures of laccase and maltodextrin. The formation of these adsorbates is attributed to attractive interactions between laccase, the maltodextrin-based lyophilization agent and the hydrophobic carbon surfaces; a short-term contact between the aqueous laccase mixture suspension and HOPG surfaces is shown to merely result in de-wetting patterns influencing the results of contact angle measurements. The new enzyme-based surface modification of carbon-based materials is suggested to be applicable for the improvement of not only the wettability of low energy substrate surfaces with fluid formulations like coatings or adhesives, but also their adhesion in contact with hardened polymers.

  11. Carbon fiber reinforced thermoplastic composites for future automotive applications

    NASA Astrophysics Data System (ADS)

    Friedrich, K.

    2016-05-01

    After a brief introduction to polymer composite properties and markets, the state of the art activities in the field of manufacturing of advanced composites for automotive applications are elucidated. These include (a) long fiber reinforced thermoplastics (LFT) for secondary automotive components, and (b) continuous carbon fiber reinforced thermosetting composites for car body applications. It is followed by future possibilities of carbon fiber reinforced thermoplastic composites for e.g. (i) crash elements, (ii) racing car seats, and (iii) production and recycling of automotive fenders.

  12. Porous texture evolution in Nomex-derived activated carbon fibers.

    PubMed

    Villar-Rodil, S; Denoyel, R; Rouquerol, J; Martínez-Alonso, A; Tascón, J M D

    2002-08-01

    In the present work, the textural evolution of a series of activated carbon fibers with increasing burn-off degree, prepared by the pyrolysis and steam activation of Nomex aramid fibers, is followed by measurements of physical adsorption of N(2) (77 K) and CO(2) (273 K) and immersion calorimetry into different liquids (dichloromethane, benzene, cyclohexane). The immersion calorimetry results are discussed in depth, paying special attention to the choice of the reference material. The activated carbon fibers studied possess an essentially homogeneous microporous texture, which suggests that these materials may be applied in gas separation, either directly or with additional CVD treatment. PMID:16290775

  13. Transverse thermal expansion of carbon fiber/epoxy matrix composites

    NASA Technical Reports Server (NTRS)

    Helmer, J. F.; Diefendorf, R. J.

    1983-01-01

    Thermal expansion coefficients and moduli of elasticity have been determined experimentally for a series of epoxy-matrix composites reinforced with carbon and Kevlar fibers. It is found that in the transverse direction the difference between the properties of the fiber and the matrix is not as pronounced as in the longitudinal direction, where the composite properties are fiber-dominated. Therefore, the pattern of fiber packing tends to affect transverse composite properties. The transverse properties of the composites tested are examined from the standpoint of the concept of homogeneity defined as the variation of packing (or lack thereof) throughout a sample.

  14. Interactions between the glass fiber coating and oxidized carbon nanotubes

    NASA Astrophysics Data System (ADS)

    Ku-Herrera, J. J.; Avilés, F.; Nistal, A.; Cauich-Rodríguez, J. V.; Rubio, F.; Rubio, J.; Bartolo-Pérez, P.

    2015-03-01

    Chemically oxidized multiwall carbon nanotubes (MWCNTs) were deposited onto commercial E-glass fibers using a dipping procedure assisted by ultrasonic dispersion. In order to investigate the role of the fiber coating (known as "sizing"), MWCNTs were deposited on the surface of as-received E-glass fibers preserving the proprietary coating as well as onto glass fibers which had the coating deliberately removed. Scanning electron microscopy and Raman spectroscopy were used to assess the distribution of MWCNTs onto the fibers. A rather homogeneous coverage with high density of MWCNTs onto the glass fibers is achieved when the fiber coating is maintained. Fourier transform infrared spectroscopy (FTIR), X-ray photoelectron spectroscopy (XPS) and nuclear magnetic resonance (NMR) analyses of the chemical composition of the glass fiber coating suggest that such coating is a complex mixture with multiple oxygen-containing functional groups such as hydroxyl, carbonyl and epoxy. FTIR and XPS of MWCNTs over the glass fibers and of a mixture of MWCNTs and fiber coating provided evidence that the hydroxyl and carboxyl groups of the oxidized MWCNTs react with the oxygen-containing functional groups of the glass fiber coating, forming hydrogen bonding and through epoxy ring opening. Hydrogen bonding and ester formation between the functional groups of the MWCNTs and the silane contained in the coating are also possible.

  15. Mechanical properties of carbon fiber composites for environmental applications

    SciTech Connect

    Andrews, R.; Grulke, E.

    1996-10-01

    Activated carbon fiber composites show great promise as fixed-bed catalytic reactors for use in environmental applications such as flue gas clean-up and ground water decontamination. A novel manufacturing process produces low density composites from chopped carbon fibers and binders. These composites have high permeability, can be activated to have high surface area, and have many potential environmental applications. This paper reports the mechanical and flow properties of these low density composites. Three point flexural strength tests were used to measure composite yield strength and flexural moduli. Composites containing over 10 pph binder had an adequate yield strength of about 200 psi at activations up to 40% weight loss. The composites were anisotropic, having along-fiber to cross-fiber yield strength ratios between 1.2 and 2.0. The friction factor for flow through the composites can be correlated using the fiber Reynolds number, and is affected by the composite bulk density.

  16. Rapid oxidation/stabilization technique for carbon foams, carbon fibers and C/C composites

    DOEpatents

    Tan, Seng; Tan, Cher-Dip

    2004-05-11

    An enhanced method for the post processing, i.e. oxidation or stabilization, of carbon materials including, but not limited to, carbon foams, carbon fibers, dense carbon-carbon composites, carbon/ceramic and carbon/metal composites, which method requires relatively very short and more effective such processing steps. The introduction of an "oxygen spill over catalyst" into the carbon precursor by blending with the carbon starting material or exposure of the carbon precursor to such a material supplies required oxygen at the atomic level and permits oxidation/stabilization of carbon materials in a fraction of the time and with a fraction of the energy normally required to accomplish such carbon processing steps. Carbon based foams, solids, composites and fiber products made utilizing this method are also described.

  17. SURFACE MORPHOLOGY OF CARBON FIBER POLYMER COMPOSITES AFTER LASER STRUCTURING

    SciTech Connect

    Sabau, Adrian S; Chen, Jian; Jones, Jonaaron F.; Alexandra, Hackett; Jellison Jr, Gerald Earle; Daniel, Claus; Warren, Charles David; Rehkopf, Jackie D.

    2015-01-01

    The increasing use of Carbon Fiber Polymer Composite (CFPC) as a lightweight material in automotive and aerospace industries requires the control of surface morphology. In this study, the composites surface was prepared by ablating the resin in the top fiber layer of the composite using an Nd:YAG laser. The CFPC specimens with T700S carbon fiber and Prepreg - T83 resin (epoxy) were supplied by Plasan Carbon Composites, Inc. as 4 ply thick, 0/90o plaques. The effect of laser fluence, scanning speed, and wavelength was investigated to remove resin without an excessive damage of the fibers. In addition, resin ablation due to the power variation created by a laser interference technique is presented. Optical property measurements, optical micrographs, 3D imaging, and high-resolution optical profiler images were used to study the effect of the laser processing on the surface morphology.

  18. Electrospinning of Continuous Carbon Naonofiber-Filled Composite Fibers

    NASA Astrophysics Data System (ADS)

    Aboutalebi, Seyed Hamed; Gholamvand, Zahra; Keyanpour-Rad, Mansoor

    In order to translate the superior properties of carbon nanofibers (CNFs) to macro-scale structures, an electrospinning route capable of placing CNFs into a continuous nano-scale composite fibril is introduced. In this work, composite fibers were produced by electrospinning solution of polyacrylonitrile (PAN) with carbon nanofibers dispersed in dimethylformamide (DMF), which is an effective solvent for carbon nanofibers. Atomic force microscopy (AFM) and scanning electron microscopy (SEM) demonstrated rough and globular surfaces on the CNF containing fibers. Raman spectra confirmed the presence of CNFs in the polymer fibers prepared employing the electrospinning method. Raman observation served as the direct evidence of successful filling of PAN fibers with CNFs and complemented the results obtained by SEM and AFM studies.

  19. Regenerable granular carbon nanotubes/alumina hybrid adsorbents for diclofenac sodium and carbamazepine removal from aqueous solution.

    PubMed

    Wei, Haoran; Deng, Shubo; Huang, Qian; Nie, Yao; Wang, Bin; Huang, Jun; Yu, Gang

    2013-08-01

    A novel granular carbon nanotubes (CNTs)/alumina (Al2O3) hybrid adsorbent with good sorption and regeneration properties was successfully prepared by mixing CNTs with surfactant Brij 35 and pseudo boehmite, followed by calcining to remove surfactant and form porous granules. Alumina binder increased the mechanical strength, hydrophilicity and porosity of the granular adsorbent, while the dispersed CNTs in the granular adsorbent were responsible for the sorption of diclofenac sodium (DS) and carbamazepine (CBZ). Scanning electron microscopy (SEM) showed that the CNTs and Al2O3 were mixed well and the porous structure was formed in the granular adsorbent. The high surface area and appropriate pore size of granular CNTs/Al2O3 adsorbent were favorable for sorption. The sorption of DS decreased with increasing solution pH, while pH had little effect on CBZ sorption. The maximum sorption capacities of CBZ and DS on the CNTs/Al2O3 adsorbent were 157.4 and 106.5 μmol/g according to the Langmuir fitting. Moreover, the spent CNTs/Al2O3 adsorbent can be thermally regenerated at 400 °C in air due to the thermal stability of CNTs. The removal of CBZ and DS changed a little in the initial reuse cycles and then kept relatively constant until tenth cycles. The adsorbed CBZ and DS were decomposed in the regeneration process. This regenerable adsorbent may find potential application in water or wastewater treatment for the removal of some micropollutants such as pharmaceuticals.

  20. Regenerable granular carbon nanotubes/alumina hybrid adsorbents for diclofenac sodium and carbamazepine removal from aqueous solution.

    PubMed

    Wei, Haoran; Deng, Shubo; Huang, Qian; Nie, Yao; Wang, Bin; Huang, Jun; Yu, Gang

    2013-08-01

    A novel granular carbon nanotubes (CNTs)/alumina (Al2O3) hybrid adsorbent with good sorption and regeneration properties was successfully prepared by mixing CNTs with surfactant Brij 35 and pseudo boehmite, followed by calcining to remove surfactant and form porous granules. Alumina binder increased the mechanical strength, hydrophilicity and porosity of the granular adsorbent, while the dispersed CNTs in the granular adsorbent were responsible for the sorption of diclofenac sodium (DS) and carbamazepine (CBZ). Scanning electron microscopy (SEM) showed that the CNTs and Al2O3 were mixed well and the porous structure was formed in the granular adsorbent. The high surface area and appropriate pore size of granular CNTs/Al2O3 adsorbent were favorable for sorption. The sorption of DS decreased with increasing solution pH, while pH had little effect on CBZ sorption. The maximum sorption capacities of CBZ and DS on the CNTs/Al2O3 adsorbent were 157.4 and 106.5 μmol/g according to the Langmuir fitting. Moreover, the spent CNTs/Al2O3 adsorbent can be thermally regenerated at 400 °C in air due to the thermal stability of CNTs. The removal of CBZ and DS changed a little in the initial reuse cycles and then kept relatively constant until tenth cycles. The adsorbed CBZ and DS were decomposed in the regeneration process. This regenerable adsorbent may find potential application in water or wastewater treatment for the removal of some micropollutants such as pharmaceuticals. PMID:23579087

  1. Influence of carbon nanotubes coatings onto carbon fiber by oxidative treatments combined with electrophoretic deposition on interfacial properties of carbon fiber composite

    NASA Astrophysics Data System (ADS)

    Deng, Chao; Jiang, Jianjun; Liu, Fa; Fang, Liangchao; Wang, Junbiao; Li, Dejia; Wu, Jianjun

    2015-12-01

    To improve the interfacial performance of carbon fiber (CF) and epoxy resin, carbon nanotubes (CNTs) coatings were utilized to achieve this purpose through coating onto CF by the treatment with hydrogen peroxide and concentrated nitric acid combined with electrophoretic deposition (EPD) process. The influence of electrophoretically deposited CNTs coatings on the surface properties of CFs were investigated by Fourier transform infrared spectrometer, atomic force microscopy, scanning electron microscopy and dynamic contact angle analysis. The results indicated that the deposition of carbon nanotubes introduced some polar groups to carbon fiber surfaces, enhanced surface roughness and changed surface morphologies of carbon fibers. Surface wettability of carbon fibers may be significantly improved by increasing surface free energy of the fibers due to the deposition of CNTs. The thickness and density of the coatings increases with the introduction of pretreatment of the CF during the EPD process. Short beam shear test was performed to examine the effect of carbon fiber functionalization on mechanical properties of the carbon fiber/epoxy resin composites. The interfacial adhesion of CNTs/CF reinforced epoxy composites showed obvious enhancement of interlaminar shear strength by 60.2% and scanning electron microscope photographs showed that the failure mode of composites was changed after the carbon fibers were coated with CNTs.

  2. Carbon nanotube fibers spun from a sizing material

    NASA Astrophysics Data System (ADS)

    Meng, Fancheng; Lu, Weibang; Li, Qingwen; Claes, Michaël; Kchit, Nadir; Chou, Tsu-Wei

    2014-12-01

    Carbon nanotube (CNT) fibers with large pores of hundreds of nanometers in diameter are synthesized from a commercially available sizing material. The pore size can be well controlled by varying the processing conditions including fiber drying temperature and shrinkage ratio. With the use of small amount H2SO4 (1 wt. %), low-concentration (1 wt. %) polyvinyl alcohol (PVA) bath coagulated porous fibers are flexible, with both high mechanical strength and electrical conductivity. Ethylene glycol/methanol mixture bath is also used to fabricate PVA-free porous CNT fibers. The porous fiber demonstrates good performance in foreign components accessing and accommodating, which may facilitate more CNT fiber practical applications, such as absorbents and supercapacitors.

  3. Effect of plasma surface treatment of recycled carbon fiber on carbon fiber-reinforced plastics (CFRP) interfacial properties

    NASA Astrophysics Data System (ADS)

    Lee, Hooseok; Ohsawa, Isamu; Takahashi, Jun

    2015-02-01

    We studied the effects of plasma surface treatment of recycled carbon fiber on adhesion of the fiber to polymers after various treatment times. Conventional surface treatment methods have been attempted for recycled carbon fiber, but most require very long processing times, which may increase cost. Hence, in this study, plasma processing was performed for 0.5 s or less. Surface functionalization was quantified by X-ray photoelectron spectroscopy. O/C increased from approximately 11% to 25%. The micro-droplet test of adhesion properties and the mechanical properties of CFRP were also investigated.

  4. Electromechanical characterization of carbon nanotubes grown on carbon fiber

    NASA Astrophysics Data System (ADS)

    Patton, Steven T.; Zhang, Qiuhong; Qu, Liangti; Dai, Liming; Voevodin, Andrey A.; Baur, Jeff

    2009-11-01

    Mechanical and electrical properties of carbon fiber (CF) and vertically aligned carbon nanotubes (CNTs) have been thoroughly investigated in previous studies. Growth of radially aligned CNTs on silicon oxide (SiO2) coated CF has recently been accomplished resulting in multiscale composite fiber (CNT/SiO2/CF). CNT/SiO2/CF offers promise as stress and strain sensors in CF reinforced composite materials. However, to date there have been no investigations of the electromechanical properties of CNT/SiO2/CF that would facilitate their usage as sensors in composite materials, which is the focus of this research. This study investigates fundamental mechanical and electrical properties of CF, SiO2/CF (SiO2 coated CF), and CNT/SiO2/CF during localized transverse compression at low loads (μN to mN) and small displacements (nm to a few μms). Force, strain, stiffness, and electrical resistance were monitored simultaneously during compression experiments. For CF, resistance decreased sharply upon compressive loading with hysteresis in both force and resistance being observed at low strain. For SiO2/CF, high resistance and negligible electrical conduction occurred, and the force-displacement curve was linear. CNT/SiO2/CF stiffness increased as force and strain increased and became comparable to that of CF at high strain (˜30%). Hysteresis in both force-displacement and resistance-displacement curves was observed with CNT/SiO2/CF, but was more evident as maximum strain increased and did not depend on strain rate. Force was higher and resistance was lower during compression as compared to decompression. Hysteretic energy loss is associated with internal friction between entangled CNTs. Van der Waals force between deformed and entangled CNTs hindered disentanglement, which reduced the number of electrical current paths and increased resistance during decompression. The results of this study provide new understanding of the mechanical and electrical behavior of CNT/SiO2/CF that

  5. Multiscale carbon nanotube-carbon fiber reinforcement for advanced epoxy composites.

    PubMed

    Bekyarova, E; Thostenson, E T; Yu, A; Kim, H; Gao, J; Tang, J; Hahn, H T; Chou, T-W; Itkis, M E; Haddon, R C

    2007-03-27

    We report an approach to the development of advanced structural composites based on engineered multiscale carbon nanotube-carbon fiber reinforcement. Electrophoresis was utilized for the selective deposition of multi- and single-walled carbon nanotubes (CNTs) on woven carbon fabric. The CNT-coated carbon fabric panels were subsequently infiltrated with epoxy resin using vacuum-assisted resin transfer molding (VARTM) to fabricate multiscale hybrid composites in which the nanotubes were completely integrated into the fiber bundles and reinforced the matrix-rich regions. The carbon nanotube/carbon fabric/epoxy composites showed approximately 30% enhancement of the interlaminar shear strength as compared to that of carbon fiber/epoxy composites without carbon nanotubes and demonstrate significantly improved out-of-plane electrical conductivity. PMID:17326671

  6. Effects of fiber, matrix, and interphase on carbon fiber composite compression strength

    NASA Technical Reports Server (NTRS)

    Nairn, John A.; Harper, Sheila I.; Bascom, Willard D.

    1994-01-01

    The major goal of this project was to obtain basic information on compression failure properties of carbon fiber composites. To do this, we investigated fiber effects, matrix effects, and fiber/matrix interface effects. Using each of nine fiber types, we prepared embedded single-fiber specimens, single-ply specimens, and full laminates. From the single-fiber specimens, in addition to the standard fragmentation test analysis, we were able to use the low crack density data to provide information about the distribution of fiber flaws. The single-ply specimens provided evidence of a correlation between the size of kink band zones and the quality of the interface. Results of the laminate compression experiments mostly agreed with the results from single-ply experiments, although the ultimate compression strengths of laminates were higher. Generally, these experiments showed a strong effect of interfacial properties. Matrix effects were examined using laminates subjected to precracking under mixed-mode loading conditions. A large effect of precracking conditions on the mode 1 toughness of the laminates was found. In order to control the properties of the fiber/matrix interface, we prepared composites of carbon fiber and polycarbonate and subjected these to annealing. The changes in interfacial properties directly correlated with changes in compression strength.

  7. Surface and interfacial properties of carbon fibers

    NASA Technical Reports Server (NTRS)

    Bascom, Willard D.

    1991-01-01

    The adhesion strength of AS4 fibers to thermoplastic polymers was determined. The specific polymers were polycarbonate, polyphenylene oxide, polyetherimide, polyphenylene oxide blends with polystyrene, and polycarbonate blends with a polycarbonate-polysiloxan copolymer. Data are also included for polysulfone. It was recognized at the outset that an absolute measure of the fiber matrix adhesion would be difficult. However, it is feasible to determine the fiber bond strengths to the thermoplastics relative to the bond strengths of the same fibers to epoxy polymers. It was anticipated, and in fact realized, that the adhesion of AS4 to the thermoplastic polymers was relatively low. Therefore, further objectives of the study were to identify means of increasing fiber/matrix adhesion and to try to determine why the adhesion of AS4 to thermoplastics is significantly less than to epoxy polymers.

  8. PREDICTING THE ADSORPTION CAPACITY OF ACTIVATED CARBON FOR EMERGING ORGANIC CONTAMINANTS FROM FUNDAMENTAL ADSORBENT AND ADSORBATE PROPERTIES - PRESENTATION

    EPA Science Inventory

    A quantitative structure-property relationship (QSPR) was developed and combined with the Polanyi-Dubinin-Manes model to predict adsorption isotherms of emerging contaminants on activated carbons with a wide range of physico-chemical properties. Affinity coefficients (βl

  9. Energy Absorption in Chopped Carbon Fiber Compression Molded Composites

    SciTech Connect

    Starbuck, J.M.

    2001-07-20

    In passenger vehicles the ability to absorb energy due to impact and be survivable for the occupant is called the ''crashworthiness'' of the structure. To identify and quantify the energy absorbing mechanisms in candidate automotive composite materials, test methodologies were developed for conducting progressive crush tests on composite plate specimens. The test method development and experimental set-up focused on isolating the damage modes associated with the frond formation that occurs in dynamic testing of composite tubes. Quasi-static progressive crush tests were performed on composite plates manufactured from chopped carbon fiber with an epoxy resin system using compression molding techniques. The carbon fiber was Toray T700 and the epoxy resin was YLA RS-35. The effect of various material and test parameters on energy absorption was evaluated by varying the following parameters during testing: fiber volume fraction, fiber length, fiber tow size, specimen width, profile radius, and profile constraint condition. It was demonstrated during testing that the use of a roller constraint directed the crushing process and the load deflection curves were similar to progressive crushing of tubes. Of all the parameters evaluated, the fiber length appeared to be the most critical material parameter, with shorter fibers having a higher specific energy absorption than longer fibers. The combination of material parameters that yielded the highest energy absorbing material was identified.

  10. Characterization of low thermal conductivity PAN-based carbon fibers

    NASA Technical Reports Server (NTRS)

    Katzman, Howard A.; Adams, P. M.; Le, T. D.; Hemminger, Carl S.

    1992-01-01

    The microstructure and surface chemistry of eight low thermal conductivity (LTC) PAN-based carbon fibers were determined and compared with PAN-based fibers heat treated to higher temperatures. Based on wide-angle x ray diffraction, the LTC PAN fibers all appear to have a similar turbostratic structure with large 002 d-spacings, small crystallite sizes, and moderate preferred orientation. Limited small-angle x ray scattering (SAXS) results indicate that, with the exception of LTC fibers made by BASF, the LTC fibers do not have well developed pores. Transmission electron microscopy shows that the texture of the two LTC PAN-based fibers studied (Amoco T350/23X and /25X) consists of multiple sets of parallel, wavy, bent layers that interweave with each other forming a complex three dimensional network oriented randomly around the fiber axis. X ray photoelectron spectroscopy (XPS) analysis finds correlations between heat treated temperatures and the surface composition chemistry of the carbon fiber samples.

  11. The dynamic response of carbon fiber-filled polymer composites

    NASA Astrophysics Data System (ADS)

    Dattelbaum, D. M.; Gustavsen, R. L.; Sheffield, S. A.; Stahl, D. B.; Scharff, R. J.; Rigg, P. A.; Furmanski, J.; Orler, E. B.; Patterson, B.; Coe, J. D.

    2012-08-01

    The dynamic (shock) responses of two carbon fiber-filled polymer composites have been quantified using gas gun-driven plate impact experimentation. The first composite is a filament-wound, highly unidirectional carbon fiber-filled epoxy with a high degree of porosity. The second composite is a chopped carbon fiber- and graphite-filled phenolic resin with little-to-no porosity. Hugoniot data are presented for the carbon fiber-epoxy (CE) composite to 18.6 GPa in the through-thickness direction, in which the shock propagates normal to the fibers. The data are best represented by a linear Rankine-Hugoniot fit: Us = 2.87 + 1.17 ×up(ρ0 = 1.536g/cm3). The shock wave structures were found to be highly heterogeneous, both due to the anisotropic nature of the fiber-epoxy microstructure, and the high degree of void volume. Plate impact experiments were also performed on a carbon fiber-filled phenolic (CP) composite to much higher shock input pressures, exceeding the reactants-to-products transition common to polymers. The CP was found to be stiffer than the filament-wound CE in the unreacted Hugoniot regime, and transformed to products near the shock-driven reaction threshold on the principal Hugoniot previously shown for the phenolic binder itself. [19] On-going research is focused on interrogating the direction-dependent dyanamic response and dynamic failure strength (spall) for the CE composite in the TT and 0∘ (fiber) directions.

  12. Comparison between Brazilian agro-wastes and activated carbon as adsorbents to remove Ni(II) from aqueous solutions.

    PubMed

    Dotto, Guilherme Luiz; Meili, Lucas; de Souza Abud, Ana Karla; Tanabe, Eduardo Hiromitsu; Bertuol, Daniel Assumpção; Foletto, Edson Luiz

    2016-01-01

    This research was performed to find an alternative, low-cost, competitive, locally available and efficient adsorbent to treat nickel (Ni) containing effluents. For this purpose, several Brazilian agro-wastes like sugarcane bagasse (SCB), passion fruit wastes (PFW), orange peel (OP) and pineapple peel (PP) were compared with an activated carbon (AC). The adsorbents were characterized. Effects of fundamental factors affecting the adsorption were investigated using batch tests. Kinetic and equilibrium studies were performed using conventional models. It was verified that the adsorption was favored at pH of 6.0 for all agro-wastes, being dependent of the Ni speciation, point of zero charge and surface area of the adsorbents. The Ni removal percentage was in the following order: SCB > OP > AC > PFW > PP. From the kinetic viewpoint, the Elovich model was appropriate to fit the Ni adsorption onto SCB, while for the other adsorbents, the pseudo-first-order model was the most suitable. For all adsorbents, the Langmuir model was the more adequate to represent the equilibrium data, being the maximum adsorption capacities of 64.1 mg g(-1), 60.7 mg g(-1), 63.1 mg g(-1), 48.1 mg g(-1) and 64.3 mg g(-1) for SCB, PFW, OP, PP and AC, respectively. These results indicated that mainly SCB and OP can be used as alternative adsorbents to treat Ni containing effluents. PMID:27232408

  13. Effect of Polarity of Activated Carbon Surface, Solvent and Adsorbate on Adsorption of Aromatic Compounds from Liquid Phase.

    PubMed

    Goto, Tatsuru; Amano, Yoshimasa; Machida, Motoi; Imazeki, Fumio

    2015-01-01

    In this study, introduction of acidic functional groups onto a carbon surface and their removal were carried out through two oxidation methods and outgassing to investigate the adsorption mechanism of aromatic compounds which have different polarity (benzene and nitrobenzene). Adsorption experiments for these aromatics in aqueous solution and n-hexane solution were conducted in order to obtain the adsorption isotherms for commercial activated carbon (BAC) as a starting material, its two types of oxidized BAC samples (OXs), and their outgassed samples at 900 °C (OGs). Adsorption and desorption kinetics of nitrobenzene for the BAC, OXs and OGs in aqueous solution were also examined. The results showed that the adsorption of benzene molecules was significantly hindered by abundant acidic functional groups in aqueous solution, whereas the adsorbed amount of nitrobenzene on OXs gradually increased as the solution concentration increased, indicating that nitrobenzene can adsorb favourably on a hydrophilic surface due to its high dipole moment, in contrast to benzene. In n-hexane solution, it was difficult for benzene to adsorb on any sample owing to the high affinity between benzene and n-hexane solvent. On the other hand, adsorbed amounts of nitrobenzene on OXs were larger than those of OGs in n-hexane solution, implying that nitrobenzene can adsorb two adsorption sites, graphene layers and surface acidic functional groups. The observed adsorption and desorption rate constants of nitrobenzene on the OXs were lower than those on the BAC due to disturbance of diffusion by the acidic functional groups.

  14. Adsorption of SO2 on bituminous coal char and activated carbon fiber

    USGS Publications Warehouse

    DeBarr, Joseph A.; Lizzio, Anthony A.; Daley, Michael A.

    1997-01-01

    The SO2 adsorption behaviors of activated carbons produced from Illinois coal and of commercially prepared activated carbon fibers (ACFs) were compared. There was no relation between surface area of coal-based carbons and SO2 adsorption, whereas adsorption of SO2 on the series of ACFs was inversely proportional to N2 BET surface area. Higher surface area ACFs had wider pores and adsorbed less SO2; thus, pore size distribution is thought to play a significant role in SO2 adsorption for these materials. Oxidation with HNO3 and/or H2SO4, followed by heat treatment at 700−925°C to remove carbon−oxygen complexes, resulted in increased SO2 adsorption for both coal chars and ACFs. This behavior was explained by an increase in the available number of free sites, previously occupied by oxygen and now available for SO2 adsorption. The use of nitrogen-containing functional groups on ACFs of proper pore size shows promise for further increasing SO2 adsorption capacities. Knowledge of the relationship among the number of free sites, pore size, and surface chemistry on corresponding SO2 adsorption should lead to the development of more efficient adsorbents prepared from either coal or ACFs.

  15. Strain measurements on concrete beam and carbon fiber cable with distributed optical fiber Bragg grating sensors

    NASA Astrophysics Data System (ADS)

    Nellen, Philipp M.; Bronnimann, Rolf; Sennhauser, Urs J.; Askins, Charles G.; Putnam, Martin A.

    1996-09-01

    We report on civil engineering applications of wavelength multiplexed optical fiber Bragg grating arrays directly produced on the draw tower for testing and surveying advanced structures and materials such as carbon fiber reinforced concrete elements and prestressing cables. We equipped a 6 by 0.9 by 0.5 m concrete beam, which was reinforced with carbon fiber reinforced epoxy laminates, and a 7-m long prestressing carbon fiber cable made of seven twisted strands, with optical fiber Bragg grating sensors. Static strains up to 8000 micrometers/m and dynamic strains up to 1200 micrometers/m were measured with a Michelson interferometer used as Fourier spectrometer with a resolution of about 10 micrometers/m for all sensors. Comparative measurements with electrical resistance strain gauges were in good agreement with the fiber optical results. We installed the fiber sensors in two different arrangements: some Bragg grating array elements measured local strain while others were applied in an extensometric configuration to measure moderate strain over a base length of 0.1 to 1 m.

  16. Fabrication of a novel magnetic carbon nanocomposite adsorbent via pyrolysis of sugar.

    PubMed

    Cho, Dong-Wan; Lee, Jechan; Ok, Yong Sik; Kwon, Eilhann E; Song, Hocheol

    2016-11-01

    A new-fashioned fabrication recipe for a magnetic carbon nanocomposite (Fe3O4@C) via pyrolysis of sugar with magnetite (Fe3O4) nanoparticles was developed for the practical environmental application as an adsorbent. In order to synthesize Fe3O4@C, the thermal degradation of sugar was firstly investigated via thermo-gravimetric analysis (TGA) to explore the optimal pyrolytic conditions for fabricating Fe3O4@C. This study laid a great emphasis on the physicochemical characterization of pyrogenic Fe3O4@C through various analytical techniques, which experimentally validated that Fe3O4@C retained thin graphitic carbon layers containing carboxyl groups on the surface with the point of zero charge (pHpzc) of 7.5. Based on adsorption tests of methylene blue (MB), it was found the optimal mass ratio of sugar to Fe3O4 was 0.15 with pyrolysis temperature of 500 °C. The adsorption capacity of Fe3O4@C for MB was 52.6 mg g(-1) and MB adsorption showed a strong pH dependence, which implies an active role of electrostatic interactions in the adsorption process. In regeneration experiments, Fe3O4@C retained 84% of its initial adsorption capacity after completing four consecutive adsorption cycles. PMID:27543680

  17. Fabrication of a novel magnetic carbon nanocomposite adsorbent via pyrolysis of sugar.

    PubMed

    Cho, Dong-Wan; Lee, Jechan; Ok, Yong Sik; Kwon, Eilhann E; Song, Hocheol

    2016-11-01

    A new-fashioned fabrication recipe for a magnetic carbon nanocomposite (Fe3O4@C) via pyrolysis of sugar with magnetite (Fe3O4) nanoparticles was developed for the practical environmental application as an adsorbent. In order to synthesize Fe3O4@C, the thermal degradation of sugar was firstly investigated via thermo-gravimetric analysis (TGA) to explore the optimal pyrolytic conditions for fabricating Fe3O4@C. This study laid a great emphasis on the physicochemical characterization of pyrogenic Fe3O4@C through various analytical techniques, which experimentally validated that Fe3O4@C retained thin graphitic carbon layers containing carboxyl groups on the surface with the point of zero charge (pHpzc) of 7.5. Based on adsorption tests of methylene blue (MB), it was found the optimal mass ratio of sugar to Fe3O4 was 0.15 with pyrolysis temperature of 500 °C. The adsorption capacity of Fe3O4@C for MB was 52.6 mg g(-1) and MB adsorption showed a strong pH dependence, which implies an active role of electrostatic interactions in the adsorption process. In regeneration experiments, Fe3O4@C retained 84% of its initial adsorption capacity after completing four consecutive adsorption cycles.

  18. Structural characteristics of oligomeric DNA strands adsorbed onto single-walled carbon nanotubes.

    PubMed

    Roxbury, Daniel; Jagota, Anand; Mittal, Jeetain

    2013-01-10

    The single-stranded DNA to single-walled carbon nanotube (SWCNT) hybrid continues to attract significant interest as an exemplary biological molecule-nanomaterial conjugate. In addition to their many biomedical uses, such as in vivo sensing and delivery of molecular cargo, DNA-SWCNT hybrids enable the sorting of SWCNTs according to their chirality. Current experimental methods have fallen short of identifying the actual structural ensemble of DNA adsorbed onto SWCNTs that enables and controls several of these phenomena. Molecular dynamics (MD) simulation has been a useful tool for studying the structure of these hybrid molecules. In recent studies, using replica exchange MD (REMD) simulation we have shown that novel secondary structures emerge and that these structures are DNA-sequence and SWCNT-type dependent. Here, we use REMD to investigate in detail the structural characteristics of two DNA-SWCNT recognition pairs: (TAT)(4)-(6,5)-SWCNT, i.e., DNA sequence TATTATTATTAT bound to the (6,5) chirality SWCNT, and (CCG)(2)CC-(8,7)-SWCNT as well as off-recognition pairs (TAT)(4)-(8,7)-SWCNT and (CCG)(2)CC-(6,5)-SWCNT. From a structural clustering analysis, dominant equilibrium structures are identified and show a right-handed self-stitched motif for (TAT)(4)-(6,5) in contrast to a left-handed β-barrel for (CCG)(2)CC-(8,7). Additionally, characteristics such as DNA end-to-end distance, solvent accessible SWCNT surface area, DNA hydrogen bonding between bases, and DNA dihedral distributions have been probed in detail as a function of the number of DNA strands adsorbed onto the nanotube. We find that the DNA structures adsorbed onto a nanotube are also stabilized by significant numbers of non-Watson-Crick hydrogen bonds (intrastrand and interstrand) in addition to π-π stacking between DNA bases and nanotube surface and Watson-Crick pairs. Finally, we provide a summary of DNA structures observed for various DNA-SWCNT hybrids as a preliminary set of motifs that may be

  19. Water and ion transport in ultra-adsorbing porous magnesium carbonate studied by dielectric spectroscopy

    NASA Astrophysics Data System (ADS)

    Pochard, Isabelle; Frykstrand, Sara; Ahlström, Olle; Forsgren, Johan; Strømme, Maria

    2014-01-01

    Porous materials are used in application areas ranging from drug and vaccine delivery, medical implants, molecular sieves and cosmetics to catalysis and humidity control. In the present work, we employed an alternative approach to gain in-depth understanding about water interaction properties in such materials by the use of dielectric spectroscopy and thereby show that it is possible to obtain information that is not accessible from the more commonly employed water interaction analysis techniques. Specifically, the complex dielectric response of Upsalite, a novel, super-hydroscopic, high-surface area, porous magnesium carbonate material was measured in isothermal frequency scans between 10-3 and 106 Hz at controlled relative humidity (RH). We found the dielectric constant of the dry material to be 1.82. The ratio of bound to free water present in Upsalite after adsorption at room temperature was found to be high irrespective of the surrounding humidity with values ranging from ˜67% to ˜90%. We further found that OH- ions are the charge carriers responsible for the electrode polarization observed in the dielectric response and that the amount of these ions that are free to move in the material corresponds to a concentration of the order of 1-10 μmol l-1 independent of RH. Finally, the OH- diffusion coefficient displayed a drastic decrease with decreasing RH, typical of transport in unsaturated conditions. The presented results provide detailed insight about water interactions in the novel water adsorbing material under study and it is foreseen that the employed analysis methods can be used to evaluate other types of moisture adsorbing materials as well as the movement of functional species in the pores of inorganic drug delivery materials and materials tailored for adsorption of harmful charged species.

  20. Adlayer structure dependent ultrafast desorption dynamics in carbon monoxide adsorbed on Pd (111)

    DOE PAGES

    Hong, Sung -Young; Xu, Pan; Camillone, Nina R.; White, Michael G.; Camillone, III, Nicholas

    2016-07-01

    Here, we report our ultrafast photoinduced desorption investigation of the coverage dependence of substrate–adsorbate energy transfer in carbon monoxide adlayers on the (111) surface of palladium. As the CO coverage is increased, the adsorption site population shifts from all threefold hollows (up to 0.33 ML), to bridge and near bridge (>0.5 to 0.6 ML) and finally to mixed threefold hollow plus top site (at saturation at 0.75 ML). We show that between 0.24 and 0.75 ML this progression of binding site motifs is accompanied by two remarkable features in the ultrafast photoinduced desorption of the adsorbates: (i) the desorption probabilitymore » increases roughly two orders magnitude, and (ii) the adsorbate–substrate energy transfer rate observed in two-pulse correlation experiments varies nonmonotonically, having a minimum at intermediate coverages. Simulations using a phenomenological model to describe the adsorbate–substrate energy transfer in terms of frictional coupling indicate that these features are consistent with an adsorption-site dependent electron-mediated energy coupling strength, ηel, that decreases with binding site in the order: three-fold hollow > bridge and near bridge > top site. This weakening of ηel largely counterbalances the decrease in the desorption activation energy that accompanies this progression of adsorption site motifs, moderating what would otherwise be a rise of several orders of magnitude in the desorption probability. Within this framework, the observed energy transfer rate enhancement at saturation coverage is due to interadsorbate energy transfer from the copopulation of molecules bound in three-fold hollows to their top-site neighbors.« less

  1. Polymer/carbon nanotube nano composite fibers--a review.

    PubMed

    Liu, Yaodong; Kumar, Satish

    2014-05-14

    Carbon nanotubes (CNTs) are regarded as ideal filler materials for polymeric fiber reinforcement due to their exceptional mechanical properties and 1D cylindrical geometry (nanometer-size diameter and very high aspect ratio). The reported processing conditions and property improvements of CNT reinforced polymeric fiber are summarized in this review. Because of CNT polymer interaction, polymer chains in CNTs' vicinity (interphase) have been observed to have more compact packing, higher orientation, and better mechanical properties than bulk polymer. Evidences of the existence of interphase polymers in composite fibers, characterizations of their structures, and fiber properties are summarized and discussed. Implications of interphase phenomena on a broader field of fiber and polymer processing to make much stronger materials are now in the early stages of exploration. Beside improvements in tensile properties, the presence of CNTs in polymeric fibers strongly affects other properties, such as thermal stability, thermal transition temperature, fiber thermal shrinkage, chemical resistance, electrical conductivity, and thermal conductivity. This paper will be helpful to better understand the current status of polymer/CNT fibers, especially high-performance fibers, and to find the most suitable processing techniques and conditions. PMID:24520802

  2. Measurement of population inversions and gain in carbon fiber plasmas

    SciTech Connect

    Milchberg, H.; Skinner, C.H.; Suckewer, S.; Voorhees, D.

    1985-10-01

    A CO/sub 2/ laser (approx.0.5 kJ energy, 70 nsec pulse width) was focussed onto the end of an axially oriented, thick (35 to 350 ..mu..) carbon fiber with or without a magnetic field present along the laser-fiber axis. We present evidence for axial-to-transverse enhancement of the CVI 182A (n = 3 ..-->.. 2) transition, which is correlated with the appearance of a population inversion between levels n = 3 and 2. For the B = 0 kG, zero field case, the maximum gain-length product of kl approx. =3 (k approx. =6 cm/sup -1/) was measured for a carbon fiber coated with a thin layer of aluminum (for additional radiation cooling). The results are interpreted in terms of fast recombination due mostly to thermal conduction from the plasma to the cold fiber core.

  3. Carbon fiber composites for cryogenic filament-wound vessels

    NASA Technical Reports Server (NTRS)

    Larsen, J. V.; Simon, R. A.

    1972-01-01

    Advanced unidirectional and bidirectional carbon fiber/epoxy resin composites were evaluated for physical and mechanical properties over a cryogenic to room temperature range for potential application to cryogenic vessels. The results showed that Courtaulds HTS carbon fiber was the superior fiber in terms of cryogenic strength properties in epoxy composites. Of the resin systems tested in ring composites, CTBN/ERLB 4617 exhibited the highest composite strengths at cryogenic temperatures, but very low interlaminar shear strengths at room temperature. Tests of unidirectional and bidirectional composite bars showed that the Epon 828/Empol 1040 resin was better at all test temperatures. Neither fatigue cycling nor thermal shock had a significant effect on composite strengths or moduli. Thermal expansion measurements gave negative values in the fiber direction and positive values in the transverse direction of the composites.

  4. Study and modification of the reactivity of carbon fibers

    NASA Technical Reports Server (NTRS)

    Walker, P. L., Jr.; Ismail, I. M.; Mahajan, O. P.; Eapen, T. A.

    1980-01-01

    The reactivity to air of polyactylonitrile-based carbon fiber cloth was enhanced by the addition of metals to the cloth. The cloth was oxidized in 54 wt% nitric acid in order to increase the surface area of the cloth and to add carbonyl groups to the surface. Metal addition was then achieved by soaking the cloth in metal acetate solution to effect exchange between the metal carbon and hydrogen on the carbonyl groups. The addition of potassium, sodium, calcium and barium enhanced fiber cloth reactivity to air at 573 K. Extended studies using potassium addition showed that success in enhancing fiber cloth reactivity to air depends on: extent of cloth oxidation in nitric acid, time of exchange in potassium acetate solution and the thoroughness of removing metal acetate from the fiber pore structure following exchange. Cloth reactivity increases essentially linearly with increase in potassium addition via exchange.

  5. Mechanical properties of carbon fiber composites for environmental applications

    SciTech Connect

    Andrews, R.; Grulke, E.; Kimber, G.

    1996-12-31

    Activated carbon fiber composites show great promise as fixed-bed catalytic reactors for use in environmental applications such as flue gas clean-up and ground water decontamination. A novel manufacturing process produces low density composites from chopped carbon fibers and binders. These composites have high permeability, can be activated to have high surface area, and have many potential environmental applications. This paper reports the mechanical and flow properties of these low density composites. Three point flexural strength tests were used to measure composite yield strength and flexural moduli. Composites containing over 10 pph binder had an adequate yield strength of about 200 psi at activations up to 40% weight loss. The composites were anisotropic, having along-fiber to cross-fiber yield strength ratios between 1.2 and 2.0. The pressure drop of air through the composites correlated with the gas velocity, and showed a dependence on sample density.

  6. Preparation of a new adsorbent from activated carbon and carbon nanofiber (AC/CNF) for manufacturing organic-vacbpour respirator cartridge.

    PubMed

    Jahangiri, Mehdi; Adl, Javad; Shahtaheri, Seyyed Jamaleddin; Rashidi, Alimorad; Ghorbanali, Amir; Kakooe, Hossein; Forushani, Abbas Rahimi; Ganjali, Mohammad Reza

    2013-01-26

    In this study a composite of activated carbon and carbon nanofiber (AC/CNF) was prepared to improve the performance of activated carbon (AC) for adsorption of volatile organic compounds (VOCs) and its utilization for respirator cartridges. Activated carbon was impregnated with a nickel nitrate catalyst precursor and carbon nanofibers (CNF) were deposited directly on the AC surface using catalytic chemical vapor deposition. Deposited CNFs on catalyst particles in AC micropores, were activated by CO2 to recover the surface area and micropores. Surface and textural characterizations of the prepared composites were investigated using Brunauer, Emmett and Teller's (BET) technique and electron microscopy respectively. Prepared composite adsorbent was tested for benzene, toluene and xylene (BTX) adsorption and then employed in an organic respirator cartridge in granular form. Adsorption studies were conducted by passing air samples through the adsorbents in a glass column at an adjustable flow rate. Finally, any adsorbed species not retained by the adsorbents in the column were trapped in a charcoal sorbent tube and analyzed by gas chromatography. CNFs with a very thin diameter of about 10-20 nm were formed uniformly on the AC/CNF. The breakthrough time for cartridges prepared with CO2 activated AC/CNF was 117 minutes which are significantly longer than for those cartridges prepared with walnut shell- based activated carbon with the same weight of adsorbents. This study showed that a granular form CO2 activated AC/CNF composite could be a very effective alternate adsorbent for respirator cartridges due to its larger adsorption capacities and lower weight.

  7. Preparation of a new adsorbent from activated carbon and carbon nanofiber (AC/CNF) for manufacturing organic-vacbpour respirator cartridge

    PubMed Central

    2013-01-01

    In this study a composite of activated carbon and carbon nanofiber (AC/CNF) was prepared to improve the performance of activated carbon (AC) for adsorption of volatile organic compounds (VOCs) and its utilization for respirator cartridges. Activated carbon was impregnated with a nickel nitrate catalyst precursor and carbon nanofibers (CNF) were deposited directly on the AC surface using catalytic chemical vapor deposition. Deposited CNFs on catalyst particles in AC micropores, were activated by CO2 to recover the surface area and micropores. Surface and textural characterizations of the prepared composites were investigated using Brunauer, Emmett and Teller’s (BET) technique and electron microscopy respectively. Prepared composite adsorbent was tested for benzene, toluene and xylene (BTX) adsorption and then employed in an organic respirator cartridge in granular form. Adsorption studies were conducted by passing air samples through the adsorbents in a glass column at an adjustable flow rate. Finally, any adsorbed species not retained by the adsorbents in the column were trapped in a charcoal sorbent tube and analyzed by gas chromatography. CNFs with a very thin diameter of about 10-20 nm were formed uniformly on the AC/CNF. The breakthrough time for cartridges prepared with CO2 activated AC/CNF was 117 minutes which are significantly longer than for those cartridges prepared with walnut shell- based activated carbon with the same weight of adsorbents. This study showed that a granular form CO2 activated AC/CNF composite could be a very effective alternate adsorbent for respirator cartridges due to its larger adsorption capacities and lower weight. PMID:23369424

  8. Electronic properties of carbon fibers intercalated with copper chloride

    NASA Technical Reports Server (NTRS)

    Oshima, H.; Natarajan, V.; Woollam, J. A.; Yavrouian, A.; Haugland, E. J.; Tsuzuku, T.

    1984-01-01

    Copper chloride intercalated pitch-based carbon fibers are found to have electrical resistivities as low as 12.9 micro-ohm-cm, and are air- and thermally-stable at and above room temperature. This is therefore a good candidate system for conductor application. In addition, Shubnikov-deHaas quantum oscillatory effects were found, and electronic properties of the intercalated fiber are studied using magnetic fields to 20 tesla.

  9. Apparatus and method for carbon fiber surface treatment

    DOEpatents

    Paulauskas, Felix L.; Sherman, Daniel M.

    2012-07-24

    An apparatus and method for enhancing the surface energy and/or surface chemistry of carbon fibers involves exposing the fibers to direct or indirect contact with atmospheric pressure plasma generated using a background gas containing at least some oxygen or other reactive species. The fiber may be exposed directly to the plasma, provided that the plasma is nonfilamentary, or the fiber may be exposed indirectly through contact with gases exhausting from a plasma discharge maintained in a separate volume. In either case, the process is carried out at or near atmospheric pressure, thereby eliminating the need for vacuum equipment. The process may be further modified by moistening the fibers with selected oxygen-containing liquids before exposure to the plasma.

  10. Apparatus and method for carbon fiber surface treatment

    DOEpatents

    Paulauskas, Felix L; Sherman, Daniel M

    2014-06-03

    An apparatus and method for enhancing the surface energy and/or surface chemistry of carbon fibers involves exposing the fibers to direct or indirect contact with atmospheric pressure plasma generated using a background gas containing at least some oxygen or other reactive species. The fiber may be exposed directly to the plasma, provided that the plasma is nonfilamentary, or the fiber may be exposed indirectly through contact with gases exhausting from a plasma discharge maintained in a separate volume. In either case, the process is carried out at or near atmospheric pressure, thereby eliminating the need for vacuum equipment. The process may be further modified by moistening the fibers with selected oxygen-containing liquids before exposure to the plasma.

  11. Adsorption of SO2 onto oxidized and heat-treated activated carbon fibers (ACFS)

    USGS Publications Warehouse

    Daley, M.A.; Mangun, C.L.; DeBarr, J.A.; Riha, S.; Lizzio, A.A.; Donnals, G.L.; Economy, J.

    1997-01-01

    A series of activated carbon fibers (ACFs) and heat-treated oxidized ACFs prepared from phenolic fiber precursors have been studied to elucidate the role of pore size, pore surface chemistry and pore volume for the adsorption of SO2 and its catalytic conversion to H2SO4. For untreated ACFs, the initial rate of SO2 adsorption from flue gas was shown to be inversely related to pore size. At longer times, the amount of SO2 adsorbed from flue gas was dependent on both the pore size and pore volume. Oxidation of the ACFs, using an aqueous oxidant, decreased their adsorption capacity for SO2 from flue gas due to a decrease in pore volume and repulsion of the SO2 from acidic surface groups. If these samples were heat-treated to desorb the oxygen containing function groups, the amount of SO2 adsorption increased. This increase in adsorption capacity was directly correlated to the amount of CO2 evolved during heat-treatment of the oxidized ACFs. The amount of SO2 adsorbed for these samples was related to the pore size, pore surface chemistry and pore volume. This analysis is explained in more detail in this paper. ?? 1997 Elsevier Science Ltd. All rights reserved.

  12. Performance of waste activated carbon as a low-cost adsorbent for the removal of anionic surfactant from aquatic environment.

    PubMed

    Gupta, Sandeep; Pal, Anjali; Ghosh, Pranab Kumar; Bandyopadhyay, Manas

    2003-02-01

    In the present study, different low cost adsorbents were screened for their sodium dodecyl sulfate (SDS, an anionic surfactant) removal capacity. Waste activated carbon (WAC) from the aqua purifier has shown high efficiency for SDS removal. The performance evaluation in the presence of various ions (Ca2+, SO4(2-), NO3-, and Cl-) and at various pH was studied. Desorption studies were conducted using simple sonication and pH variation technique. Column adsorption studies were performed. SEM and EDS studies were done on the adsorbing material before adsorption, after adsorption and after desorption of SDS. PMID:12638703

  13. Application of carbon foam for heavy metal removal from industrial plating wastewater and toxicity evaluation of the adsorbent.

    PubMed

    Lee, Chang-Gu; Song, Mi-Kyung; Ryu, Jae-Chun; Park, Chanhyuk; Choi, Jae-Woo; Lee, Sang-Hyup

    2016-06-01

    Electroplating wastewater contains various types of toxic substances, such as heavy metals, solvents, and cleaning agents. Carbon foam was used as an adsorbent for the removal of heavy metals from real industrial plating wastewater. Its sorption capacity was compared with those of a commercial ion-exchange resin (BC258) and a heavy metal adsorbent (CupriSorb™) in a batch system. The experimental carbon foam has a considerably higher sorption capacity for Cr and Cu than commercial adsorbents for acid/alkali wastewater and cyanide wastewater. Additionally, cytotoxicity test showed that the newly developed adsorbent has low cytotoxic effects on three kinds of human cells. In a pilot plant, the carbon foam had higher sorption capacity for Cr (73.64 g kg(-1)) than for Cu (14.86 g kg(-1)) and Ni (7.74 g kg(-1)) during 350 h of operation time. Oxidation pretreatments using UV/hydrogen peroxide enhance heavy metal removal from plating wastewater containing cyanide compounds.

  14. Accuracy of density functional theory in the prediction of carbon dioxide adsorbent materials.

    PubMed

    Cazorla, Claudio; Shevlin, Stephen A

    2013-04-01

    Density functional theory (DFT) has become the computational method of choice for modeling and characterization of carbon dioxide adsorbents, a broad family of materials which at present are urgently sought after for environmental applications. The description of polar carbon dioxide (CO(2)) molecules in low-coordinated environments like surfaces and porous materials, however, may be challenging for local and semi-local DFT approximations. Here, we present a thorough computational study in which the accuracy of DFT methods in describing the interactions of CO(2) with model alkali-earth-metal (AEM, Ca and Li) decorated carbon structures, namely anthracene (C(14)H(10)) molecules, is assessed. We find that gas-adsorption energies and equilibrium structures obtained with standard (i.e. LDA and GGA), hybrid (i.e. PBE0 and B3LYP) and van der Waals exchange-correlation functionals of DFT dramatically differ from the results obtained with second-order Møller-Plesset perturbation theory (MP2), an accurate computational quantum chemistry method. The major disagreements found can be mostly rationalized in terms of electron correlation errors that lead to wrong charge-transfer and electrostatic Coulomb interactions between CO(2) and AEM-decorated anthracene molecules. Nevertheless, we show that when the concentration of AEM atoms in anthracene is tuned to resemble as closely as possible the electronic structure of AEM-decorated graphene (i.e. an extended two-dimensional material), hybrid exchange-correlation DFT and MP2 methods quantitatively provide similar results. PMID:23361567

  15. A probabilistic analysis of electrical equipment vulnerability to carbon fibers

    NASA Technical Reports Server (NTRS)

    Elber, W.

    1980-01-01

    The statistical problems of airborne carbon fibers falling onto electrical circuits were idealized and analyzed. The probability of making contact between randomly oriented finite length fibers and sets of parallel conductors with various spacings and lengths was developed theoretically. The probability of multiple fibers joining to bridge a single gap between conductors, or forming continuous networks is included. From these theoretical considerations, practical statistical analyses to assess the likelihood of causing electrical malfunctions was produced. The statistics obtained were confirmed by comparison with results of controlled experiments.

  16. Dark pulse generation in fiber lasers incorporating carbon nanotubes.

    PubMed

    Liu, H H; Chow, K K

    2014-12-01

    We demonstrate the generation of dark pulses from carbon nanotube (CNT) incorporated erbium-doped fiber ring lasers with net anomalous dispersion. A side-polished fiber coated with CNT layer by optically-driven deposition method is embedded into the laser in order to enhance the birefringence and nonlinearity of the laser cavity. The dual-wavelength domain-wall dark pulses are obtained from the developed CNT-incorporated fiber laser at a relatively low pump threshold of 50.6 mW. Dark pulses repeated at the fifth-order harmonic of the fundamental cavity frequency are observed by adjusting the intra-cavity polarization state.

  17. Deposition of carbon nanotubes onto aramid fibers using as-received and chemically modified fibers

    NASA Astrophysics Data System (ADS)

    Rodríguez-Uicab, O.; Avilés, F.; Gonzalez-Chi, P. I.; Canché-Escamilla, G.; Duarte-Aranda, S.; Yazdani-Pedram, M.; Toro, P.; Gamboa, F.; Mazo, M. A.; Nistal, A.; Rubio, J.

    2016-11-01

    Multiwall carbon nanotubes (MWCNTs) oxidized by an acid treatment were deposited on the surface of as-received commercial aramid fibers containing a surface coating ("sizing"), and fibers modified by either a chlorosulfonic treatment or a mixture of nitric and sulfuric acids. The surface of the aramid fiber activated by the chemical treatments presents increasing density of CO, COOH and OH functional groups. However, these chemical treatments reduced the tensile mechanical properties of the fibers, especially when the nitric and sulfuric acid mixture was used. Characterization of the MWCNTs deposited on the fiber surface was conducted by scanning electron microscopy, Raman spectroscopy mapping and X-ray photoelectron spectroscopy. These characterizations showed higher areal concentration and more homogeneous distribution of MWCNTs over the aramid fibers for as-received fibers and for those modified with chlorosulfonic acid, suggesting the existence of interaction between the oxidized MWCNTs and the fiber coating. The electrical resistance of the MWCNT-modified aramid yarns comprising ∼1000 individual fibers was in the order of MΩ/cm, which renders multifunctional properties.

  18. Nano-yarn carbon nanotube fiber based enzymatic glucose biosensor

    NASA Astrophysics Data System (ADS)

    Zhu, Zhigang; Song, Wenhui; Burugapalli, Krishna; Moussy, Francis; Li, Ya-Li; Zhong, Xiao-Hua

    2010-04-01

    A novel brush-like electrode based on carbon nanotube (CNT) nano-yarn fiber has been designed for electrochemical biosensor applications and its efficacy as an enzymatic glucose biosensor demonstrated. The CNT nano-yarn fiber was spun directly from a chemical-vapor-deposition (CVD) gas flow reaction using a mixture of ethanol and acetone as the carbon source and an iron nano-catalyst. The fiber, 28 µm in diameter, was made of bundles of double walled CNTs (DWNTs) concentrically compacted into multiple layers forming a nano-porous network structure. Cyclic voltammetry study revealed a superior electrocatalytic activity for CNT fiber compared to the traditional Pt-Ir coil electrode. The electrode end tip of the CNT fiber was freeze-fractured to obtain a unique brush-like nano-structure resembling a scale-down electrical 'flex', where glucose oxidase (GOx) enzyme was immobilized using glutaraldehyde crosslinking in the presence of bovine serum albumin (BSA). An outer epoxy-polyurethane (EPU) layer was used as semi-permeable membrane. The sensor function was tested against a standard reference electrode. The sensitivities, linear detection range and linearity for detecting glucose for the miniature CNT fiber electrode were better than that reported for a Pt-Ir coil electrode. Thermal annealing of the CNT fiber at 250 °C for 30 min prior to fabrication of the sensor resulted in a 7.5 fold increase in glucose sensitivity. The as-spun CNT fiber based glucose biosensor was shown to be stable for up to 70 days. In addition, gold coating of the electrode connecting end of the CNT fiber resulted in extending the glucose detection limit to 25 µM. To conclude, superior efficiency of CNT fiber for glucose biosensing was demonstrated compared to a traditional Pt-Ir sensor.

  19. Nano-yarn carbon nanotube fiber based enzymatic glucose biosensor.

    PubMed

    Zhu, Zhigang; Song, Wenhui; Burugapalli, Krishna; Moussy, Francis; Li, Ya-Li; Zhong, Xiao-Hua

    2010-04-23

    A novel brush-like electrode based on carbon nanotube (CNT) nano-yarn fiber has been designed for electrochemical biosensor applications and its efficacy as an enzymatic glucose biosensor demonstrated. The CNT nano-yarn fiber was spun directly from a chemical-vapor-deposition (CVD) gas flow reaction using a mixture of ethanol and acetone as the carbon source and an iron nano-catalyst. The fiber, 28 microm in diameter, was made of bundles of double walled CNTs (DWNTs) concentrically compacted into multiple layers forming a nano-porous network structure. Cyclic voltammetry study revealed a superior electrocatalytic activity for CNT fiber compared to the traditional Pt-Ir coil electrode. The electrode end tip of the CNT fiber was freeze-fractured to obtain a unique brush-like nano-structure resembling a scale-down electrical 'flex', where glucose oxidase (GOx) enzyme was immobilized using glutaraldehyde crosslinking in the presence of bovine serum albumin (BSA). An outer epoxy-polyurethane (EPU) layer was used as semi-permeable membrane. The sensor function was tested against a standard reference electrode. The sensitivities, linear detection range and linearity for detecting glucose for the miniature CNT fiber electrode were better than that reported for a Pt-Ir coil electrode. Thermal annealing of the CNT fiber at 250 degrees C for 30 min prior to fabrication of the sensor resulted in a 7.5 fold increase in glucose sensitivity. The as-spun CNT fiber based glucose biosensor was shown to be stable for up to 70 days. In addition, gold coating of the electrode connecting end of the CNT fiber resulted in extending the glucose detection limit to 25 microM. To conclude, superior efficiency of CNT fiber for glucose biosensing was demonstrated compared to a traditional Pt-Ir sensor. PMID:20348597

  20. Puncture-Healing Thermoplastic Resin Carbon-Fiber-Reinforced Composites

    NASA Technical Reports Server (NTRS)

    Gordon, Keith L. (Inventor); Siochi, Emilie J. (Inventor); Grimsley, Brian W. (Inventor); Cano, Roberto J. (Inventor); Czabaj, Michael W. (Inventor)

    2015-01-01

    A composite comprising a combination of a self-healing polymer matrix and a carbon fiber reinforcement is described. In one embodiment, the matrix is a polybutadiene graft copolymer matrix, such as polybutadiene graft copolymer comprising poly(butadiene)-graft-poly(methyl acrylate-co-acrylonitrile). A method of fabricating the composite is also described, comprising the steps of manufacturing a pre-impregnated unidirectional carbon fiber preform by wetting a plurality of carbon fibers with a solution, the solution comprising a self-healing polymer and a solvent, and curing the preform. A method of repairing a structure made from the composite of the invention is described. A novel prepreg material used to manufacture the composite of the invention is described.

  1. Carbon fiber composite characterization in adverse thermal environments.

    SciTech Connect

    Gomez-Vasquez, Sylvia; Brown, Alexander L.; Hubbard, Joshua A.; Ramirez, Ciro J.; Dodd, Amanda B.

    2011-05-01

    The behavior of carbon fiber aircraft composites was studied in adverse thermal environments. The effects of resin composition and fiber orientation were measured in two test configurations: 102 by 127 millimeter (mm) test coupons were irradiated at approximately 22.5 kW/m{sup 2} to measure thermal response, and 102 by 254 mm test coupons were irradiated at approximately 30.7 kW/m{sup 2} to characterize piloted flame spread in the vertically upward direction. Carbon-fiber composite materials with epoxy and bismaleimide resins, and uni-directional and woven fiber orientations, were tested. Bismaleimide samples produced less smoke, and were more resistant to flame spread, as expected for high temperature thermoset resins with characteristically lower heat release rates. All materials lost approximately 20-25% of their mass regardless of resin type, fiber orientation, or test configuration. Woven fiber composites displayed localized smoke jetting whereas uni-directional composites developed cracks parallel to the fibers from which smoke and flames emanated. Swelling and delamination were observed with volumetric expansion on the order of 100% to 200%. The purpose of this work was to provide validation data for SNL's foundational thermal and combustion modeling capabilities.

  2. Removal of Ozone by Carbon Nanotubes/Quartz Fiber Film.

    PubMed

    Yang, Shen; Nie, Jingqi; Wei, Fei; Yang, Xudong

    2016-09-01

    Ozone is recognized as a harmful gaseous pollutant, which can lead to severe human health problems. In this study, carbon nanotubes (CNTs) were tested as a new approach for ozone removal. The CNTs/quartz fiber film was fabricated through growth of CNTs upon pure quartz fiber using chemical vapor deposition method. Ozone conversion efficiency of the CNTs/quartz fiber film was tested for 10 h and compared with that of quartz film, activated carbon (AC), and a potassium iodide (KI) solution under the same conditions. The pressure resistance of these materials under different airflow rates was also measured. The results showed that the CNTs/quartz fiber film had better ozone conversion efficiency but also higher pressure resistance than AC and the KI solution of the same weight. The ozone removal performance of the CNTs/quartz fiber film was comparable with AC at 20 times more weight. The CNTs played a dominant role in ozone removal by the CNTs/quartz fiber film. Its high ozone conversion efficiency, lightweight and free-standing properties make the CNTs/quartz fiber film applicable to ozone removal. Further investigation should be focused on reducing pressure resistance and studying the CNT mechanism for removing ozone.

  3. Removal of Ozone by Carbon Nanotubes/Quartz Fiber Film.

    PubMed

    Yang, Shen; Nie, Jingqi; Wei, Fei; Yang, Xudong

    2016-09-01

    Ozone is recognized as a harmful gaseous pollutant, which can lead to severe human health problems. In this study, carbon nanotubes (CNTs) were tested as a new approach for ozone removal. The CNTs/quartz fiber film was fabricated through growth of CNTs upon pure quartz fiber using chemical vapor deposition method. Ozone conversion efficiency of the CNTs/quartz fiber film was tested for 10 h and compared with that of quartz film, activated carbon (AC), and a potassium iodide (KI) solution under the same conditions. The pressure resistance of these materials under different airflow rates was also measured. The results showed that the CNTs/quartz fiber film had better ozone conversion efficiency but also higher pressure resistance than AC and the KI solution of the same weight. The ozone removal performance of the CNTs/quartz fiber film was comparable with AC at 20 times more weight. The CNTs played a dominant role in ozone removal by the CNTs/quartz fiber film. Its high ozone conversion efficiency, lightweight and free-standing properties make the CNTs/quartz fiber film applicable to ozone removal. Further investigation should be focused on reducing pressure resistance and studying the CNT mechanism for removing ozone. PMID:27501513

  4. A comparison of the electrochemical behavior of carbon aerogels and activated carbon fiber cloths

    SciTech Connect

    Tran, T.D.; Alviso, C.T.; Hulsey, S.S.; Nielsen, J.K.; Pekala, R.W.

    1996-05-10

    Electrochemical capacitative behavior of carbon aerogels and commercial carbon fiber cloths was studied in 5M KOH, 3M sulfuric acid, and 0.5M tetrethylammonium tetrafluoroborate/propylene carbonate electrolytes. The resorcinol-formaldehyde based carbon aerogels with a range of denisty (0.2-0.85 g/cc) have open-cell structures with ultrafine pore sizes (5-50 nm), high surface area (400-700 m{sup 2}/g), and a solid matrix composed of interconnected particles or fibers with characteristic diameters of 10 nm. The commercial fiber cloths in the density range 0.2-04g/cc have high surface areas (1000-2500 m{sup 2}/g). The volumetric capacitances of high-density aerogels are shown to be comparable to or exceeding those from activated carbon fibers. Electrochemical behavior of these materials in various electrolytes is compared and related to their physical properties.

  5. Effect of Carbon Nanotubes Upon Emissions From Cutting and Sanding Carbon Fiber-Epoxy Composites

    PubMed Central

    Heitbrink, William A.; Lo, Li-Ming

    2015-01-01

    Carbon nanotubes (CNTs) are being incorporated into structural composites to enhance material strength. During fabrication or repair activities, machining nanocomposites may release CNTs into the workplace air. An experimental study was conducted to evaluate the emissions generated by cutting and sanding on three types of epoxy-composite panels: Panel A containing graphite fibers, Panel B containing graphite fibers and carbon-based mat, and Panel C containing graphite fibers, carbon-based mat, and multi-walled CNTs. Aerosol sampling was conducted with direct-reading instruments, and filter samples were collected for measuring elemental carbon (EC) and fiber concentrations. Our study results showed that cutting Panel C with a band saw did not generate detectable emissions of fibers inspected by transmission electron microscopy but did increase the particle mass, number, and EC emission concentrations by 20% to 80% compared to Panels A and B. Sanding operation performed on two Panel C resulted in fiber emission rates of 1.9×108 and 2.8×106 fibers per second (f/s), while no free aerosol fibers were detected from sanding Panels A and B containing no CNTs. These free CNT fibers may be a health concern. However, the analysis of particle and EC concentrations from these same samples cannot clearly indicate the presence of CNTs, because extraneous aerosol generation from machining the composite epoxy material increased the mass concentrations of the EC. PMID:26478716

  6. Process for preparing tapes from thermoplastic polymers and carbon fibers

    NASA Technical Reports Server (NTRS)

    Chung, Tai-Shung (Inventor); Furst, Howard (Inventor); Gurion, Zev (Inventor); McMahon, Paul E. (Inventor); Orwoll, Richard D. (Inventor); Palangio, Daniel (Inventor)

    1986-01-01

    The instant invention involves a process for use in preparing tapes or rovings, which are formed from a thermoplastic material used to impregnate longitudinally extended bundles of carbon fibers. The process involves the steps of (a) gas spreading a tow of carbon fibers; (b) feeding the spread tow into a crosshead die; (c) impregnating the tow in the die with a thermoplastic polymer; (d) withdrawing the impregnated tow from the die; and (e) gas cooling the impregnated tow with a jet of air. The crosshead die useful in the instant invention includes a horizontally extended, carbon fiber bundle inlet channel, means for providing melted polymer under pressure to the die, means for dividing the polymeric material flowing into the die into an upper flow channel and a lower flow channel disposed above and below the moving carbon fiber bundle, means for applying the thermoplastic material from both the upper and lower channels to the fiber bundle, and means for withdrawing the resulting tape from the die.

  7. Compression Molding of CFRTP Used with Carbon Fiber Extracted from CFRP Waste

    NASA Astrophysics Data System (ADS)

    Kimura, Teruo; Ino, Haruhiro; Nishida, Yuichi; Aoyama, Naoki; Shibata, Katsuji

    This study investigated a compression molding method of carbon fiber reinforced thermoplastics (CFRTP) made of carbon fiber extracted from CFRP waste. The short carbon fibers were mixed with polyester fibers using a papermaking method to make the preform sheet of compression molding. The waste obtained from a textile water jet loom was used as a matrix material. The setting speed of each fiber during the papermaking process was regulated by using a dispersing agent to obtain the good dispersion of each fiber. Laminated preform sheets combined with polyester fibers and carbon fibers were compressed with heating at 300°C and then the polyester fiber was melted as a matrix material. It was cleared from the experimental results that the mechanical properties of molded CFRTP largely depends on both the fiber dispersion and the content of carbon fiber in the preform.

  8. Tamarind (Tamarindus indica) fruit shell carbon: A calcium-rich promising adsorbent for fluoride removal from groundwater.

    PubMed

    Sivasankar, V; Rajkumar, S; Murugesh, S; Darchen, A

    2012-07-30

    Tamarindus indica fruit shells (TIFSs) are naturally calcium rich compounds. They were impregnated with ammonium carbonate and then carbonized, leading to ammonium carbonate activated ACA-TIFS carbon. The resulting materials and carbon arising from virgin fruit shells V-TIFS were characterized and assayed as adsorbent for the removal of fluoride anions from groundwater. The fluoride scavenging ability of TIFS carbons was due to naturally dispersed calcium compounds. X-ray diffraction (XRD) showed that TIFS carbon contained a mixture of calcium oxalate and calcium carbonate. Batch studies on the fluoride removal efficiency of TIFS carbons with respect to contact time, pH, initial fluoride concentration, and co-ion interference were conducted. Applicability of various kinetic models (viz., pseudo-first-order, pseudo-second-order, intra-particle diffusion and Elovich) and sorption isotherms were tested for batch techniques. The fluoride removal capacity of TIFS carbons was found to be 91% and 83% at a pH of 7.05 for V-TIFS and ACA-TIFS carbons, respectively. The practical applicability of TIFS carbons using groundwater samples was approved. The fluoride removal was greater in groundwater without hydrogen carbonate ions than those containing these ions. The characterizations of fluoride unloaded and loaded TIFS carbons were done by SEM and XRD studies.

  9. Activation and micropore structure determination of carbon-fiber composite molecular sieves. Topical report, 30 March 1994--14 April 1995

    SciTech Connect

    Jagtoyen, M.; Derbyshire, F.; Kimber, G.; Fei, You Qing

    1995-05-19

    Progress in developing novel, rigid, monolithic adsorbent carbon fiber composites is described. Carbon fiber composites are activated using steam or CO{sub 2}, in order to produce uniform activation through the material and to control the pore structure and adsorptive properties. There is an overall shrinkage during activation, which is directly correlated with burnoff; burnoff above 40% results in fracture. Burnoffs higher than 10% does not produce any benefit for separation of CH{sub 4}-CO{sub 2} mixtures. Five samples of CFCMS have been prepared for testing as molecular sieves; all have relatively narrow pore size distributions with average pore diameters around 6A.

  10. Review and developments of dissemination models for airborne carbon fibers

    NASA Technical Reports Server (NTRS)

    Elber, W.

    1980-01-01

    Dissemination prediction models were reviewed to determine their applicability to a risk assessment for airborne carbon fibers. The review showed that the Gaussian prediction models using partial reflection at the ground agreed very closely with a more elaborate diffusion analysis developed for the study. For distances beyond 10,000 m the Gaussian models predicted a slower fall-off in exposure levels than the diffusion models. This resulting level of conservatism was preferred for the carbon fiber risk assessment. The results also showed that the perfect vertical-mixing models developed herein agreed very closely with the diffusion analysis for all except the most stable atmospheric conditions.

  11. Carbon Fiber Reinforced Ceramic Composites for Propulsion Applications

    NASA Technical Reports Server (NTRS)

    Shivakumar, Kunigal; Argade, Shyam

    2003-01-01

    This report presents a critical review of the processing techniques for fabricating continuous fiber-reinforced CMCs for possible applications at elevated temperatures. Some of the issues affecting durability of the composite materials such as fiber coatings and cracking of the matrix because of shrinkage in PIP-process are also examined. An assessment of the potential inexpensive processes is also provided. Finally three potential routes of manufacturing C/SiC composites using a technology that NC A&T developed for carbon/carbon composites are outlined. Challenges that will be encountered are also listed.

  12. Collector surface for a microwave tube comprising a carbon-bonded carbon-fiber composite

    DOEpatents

    Lauf, Robert J.; McMillan, April D.; Johnson, Arvid C.; Moorhead, Arthur J.

    1998-01-01

    In a microwave tube, an improved collector surface coating comprises a porous carbon composite material, preferably a carbon-bonded carbon fiber composite having a bulk density less than about 2 g/cc. Installation of the coating is readily adaptable as part of the tube manufacturing process.

  13. Collector surface for a microwave tube comprising a carbon-bonded carbon-fiber composite

    DOEpatents

    Lauf, R.J.; McMillan, A.D.; Johnson, A.C.; Moorhead, A.J.

    1998-07-28

    In a microwave tube, an improved collector surface coating comprises a porous carbon composite material, preferably a carbon-bonded carbon fiber composite having a bulk density less than about 2 g/cc. Installation of the coating is readily adaptable as part of the tube manufacturing process. 4 figs.

  14. Adhesion between thermoplastic polymer particles and carbon and glass fibers

    SciTech Connect

    Colton, J.S.

    1996-12-31

    High performance composites consist of polymer matrices reinforced with continuous fibers. Polymer powders can be coated and fused onto the fibers by various techniques to produce these composites. One such technique consists of spreading the fibers with an air banding jet, and then running the fibers through a fluidized bed of the powder. The fluidizing air is typically charged, imparting a charge to the powder particles. The fibers are grounded which leads to an attraction between the particles and the fibers. The particle-coated fibers then go through a tunnel oven, sintering the particles onto the fibers, leaving a flexible {open_quotes}tow-preg{close_quotes} which can then be processed into a preform for manufacture into a final part. To develop an initial understanding of the powder coating process, the adhesion of uncharged particles and fibers was studied. Contact mechanics predicts that the adhesion force between uncharged particles depends on the mutual (or equivalent) radius of curvature between the contacting objects, as well as their surface energies. For the materials of interest, the Derjaguin approximation is appropriate and is applied. PEEK (poly ether ether ketone) and PET (poly ethylene terephthalate) particles, cryogenically ground to nominal diameters of 10 to 100 {mu}m were brought into contact with themselves, with E-glass fibers (nominal diameter of 20 {mu}m), carbon fibers (nominal diameter of 8 {mu}m), and glass microscope slides using an AFM. Adhesion forces were measured and compared to predictions using Derjaguin`s approximation. SEM micrographs were used to determine the scale of the radii of curvature of contacting sites.

  15. Adhesion of novel high-performance polymers to carbon fibers: Fiber surface treatment, characterization, and microbond single fiber pull-out test. Ph.D. Thesis

    SciTech Connect

    Heisey, C.L.

    1993-12-31

    The adhesion of carbon fibers to several high performance polymers, including a phosphorus-containing bismaleimite, a cyanate ester resin, and a pyridine-containing thermoplastic, was evaluated using the microbond single fiber pull-out test. The objective was to determine the chemical and mechanical properties of the fiber and the polymer which affect the fiber/polymer adhesion in a given composite system. Fiber/matrix adhesion is of interest since the degree of adhesion and the nature of the fiber/matrix interphase has a major influence on the mechanical properties of a composite. The surface chemical composition, topography, tensile strength, and surface energy of untreated AU-4 and commercially surface treated AS-4 carbon fibers were evaluated using x-ray photoelectron spectroscopy (XPS), scanning electron microscopy (SEM), single fiber tensile tests, and dynamic contact angle analysis. The commercial surface treatment which converted the AU-4 to the AS-4 fiber oxidized the carbon fiber surface. The surface of the AS-4 carbon fiber was further modified using air, oxygen, ammonia, and ethylene plasmas. The AS-4 fiber tow was also characterized following exposure to the aqueous poly(amic acid) solution used to disperse the matrix powder during aqueous suspension prepregging of thermoplastic matrix composites. The air and oxygen plasma treatments significantly oxidized and roughened the surface of the AS-4 carbon fibers. In addition, the air and oxygen plasma increased the polar component of the AS-4 fiber surface energy. The ammonia plasma increased the concentration of nitrogen on the fiber surface, without significantly altering the fiber topography (at a magnification of 50,000X). The atomic oxygen present in the air and oxygen plasma treatments is capable of reacting with both the edge and basal planes in the carbon fiber structure. As a result, the oxygen-containing plasmas progressively ablated the organic material in the carbon fiber surface.

  16. Carbon-fiber composite molecular sieves for gas separation

    SciTech Connect

    Jagtoyen, M.; Derbyshire, F.

    1996-08-01

    This report describes continuing work on the activation and characterization of formed carbon fiber composites. The composites are produced at the Oak Ridge National Laboratory (ORNL) and activated at the Center for Applied Energy Research (CAER) using steam, CO{sub 2}, or O{sub 2} at different conditions of temperature and time, and with different furnace configurations. The general aims of the project are to produce uniformly activated samples with controlled pore structures for specialist applications such as gas separation and water treatment. In previous work the authors reported that composites produced from isotropic pitch fibers weighing up to 25g can be uniformly activated through the appropriate choice of reaction conditions and furnace configurations. They have now succeeded in uniformly activating composites of dimensions up to 12 x 7 x 6 cm, or up to about 166 gram - a scale-up factor of about six. Part of the work has involved the installation of a new furnace that can accommodate larger composites. Efforts were made to achieve uniform activation in both steam and CO{sub 2}. The authors have also succeeded in producing materials with very uniform and narrow pore size distributions by using a novel method involving low temperature oxygen chemisorption in combination with heat treatment in N{sub 2} at high temperatures. Work has also started on the activation of PAN based carbon fibers and fiber composites with the aim of producing composites with wide pore structures for use as catalyst supports. So far activation of the PAN fiber composites supplied by ORNL has been difficult which is attributed to the low reactivity of the PAN fibers. As a result, studies are now being made of the activation of the PAN fibers to investigate the optimum carbonization and activation conditions for PAN based fibers.

  17. Carbon nanotubes coated fiber optic ammonia gas sensor

    NASA Astrophysics Data System (ADS)

    Manivannan, S.; Shobin, L. R.; Saranya, A. M.; Renganathan, B.; Sastikumar, D.; Park, Kyu Chang

    2011-01-01

    We report, intrinsic fiber optic carbon nanotubes coated sensor for the detection of ammonia gas at room temperature. Multimode step index polymethyl methacrylate (PMMA) optical fiber passive cladding is partly replaced by an active coating of single and multi-walled carbon nanotubes following the dip coating technique and the reaction with ammonia is studied by measuring the change in output intensity from the optical fiber under various ammonia gas concentrations in the range 0-500 ppm in step of 50 ppm. The sensitivity is calculated for different wavelengths in the range 200-1100 nm both for single and multi-walled carbon nanotubes coated fiber. Higher sensitivities are obtained as 0.26 counts/ppm and 0.31 counts/ppm for single-walled (average diameter 1.3 nm, 30 wt.% purity) and multi-walled (average diameter 10-15 nm, 95 wt.% purity) carbon nanotubes respectively. The role of diameter and purity of carbon nanotubes towards the ammonia sensing is studied and the results are discussed.

  18. The effect of bromination of carbon fibers on the coefficient of thermal expansion of graphite fiber-epoxy composites

    NASA Technical Reports Server (NTRS)

    Jaworske, D. A.; Maciag, C.

    1987-01-01

    To examine the effect of bromination of carbon fibers on the coefficient of thermal expansion (CTE) of carbon fiber epoxy composites, several pristine and brominated carbon fiber-epoxy composite samples were subjected to thermomechanical analysis. The CTE's of these samples were measured in the uniaxial and transverse directions. The CTE was dominated by the fibers in the uniaxial direction, while it was dominated by the matrix in the transverse directions. Bromination had no effect on the CTE of any of the composites. In addition, the CTE of fiber tow was measured in the absence of a polymer matrix, using an extension probe. The results from this technique were inconclusive.

  19. Polyaniline/Carbon Nanotube Composite Fiber-Based Dye-Sensitized Photovoltaic Wire.

    PubMed

    Pan, Shaowu; Yang, Jinhu

    2015-09-01

    Polyaniline/carbon nanotube composite fiber was prepared from aligned multi-walled carbon nano- tube fiber coupling with subsequent electrochemical polymerization of aniline. Novel wire-shaped dye-sensitized solar cells were obtained by using the composite fiber as counter electrode. Photovoltaic wire based on the composite fiber showed a conversion efficiency of 3.8%, which is 63% higher than the pure carbon nanotube fiber. PMID:26716346

  20. Formation of continuous activated carbon fibers for barrier fabrics

    NASA Astrophysics Data System (ADS)

    Liang, Ying

    1997-08-01

    Commercial protective suits made of active carbon granules or nonwoven fabrics are heavy, have low moisture vapor transport rate, and are uncomfortable. Inherent problems due to construction of barrier fabrics lead to severe heat stress when worn for even short time in warm environments. One proposed method to eliminate these problems is to facilitate the construction of a fabric made of continuous activated carbon fibers (CACF). This study is directed toward investigating the possibility of developing CAFC from two precursors: aramid and fibrillated PAN fiber. It was shown in this study that Kevlar-29 fibers could be quickly carbonized and activated to CACF with high adsorptivity and relatively low weight loss. CACF with high surface area (>500 msp2/g) and reasonable tenacity (≈1g/denier) were successfully prepared from Kevlar fibers through a three-step process: pretreatment, carbonization, and activation. X-ray diffraction, Fourier Transform Infrared Spectroscopy (FTIR), and thermal analysis were conducted to understand the evolution of physical and chemical properties during pretreatment. The influence of temperature, heating rate, and pyrolysis environment on the thermal behavior was determined by DSC and TGA/DTA and used as an indicator for optimizing the pyrolysis conditions. Surface analysis by nitrogen isotherms indicated that the resultant fibers had micropores and mesopores on the surface of CACF. This was also inferred by studies on the surface morphology through Scanning Electron Microscopy (SEM) and Scanning Tunneling Microscopy (STM). An investigation of the surface chemical structure by X-ray photoelectron spectroscopy (XPS) before and after activation and elemental analysis confirmed that adsorption of Kevlar based CACF mainly arises due to the physisorption instead of chemisorption. A multistep stabilization along with carbonization and activation was used to prepare active carbon fiber from fibrillated PAN fiber. The resultant fiber retained

  1. Rapid Fabrication of Carbide Matrix/Carbon Fiber Composites

    NASA Technical Reports Server (NTRS)

    Williams, Brian E.; Bernander, Robert E.

    2007-01-01

    Composites of zirconium carbide matrix material reinforced with carbon fibers can be fabricated relatively rapidly in a process that includes a melt infiltration step. Heretofore, these and other ceramic matrix composites have been made in a chemical vapor infiltration (CVI) process that takes months. The finished products of the CVI process are highly porous and cannot withstand temperatures above 3,000 F (approx.1,600 C). In contrast, the melt-infiltration-based process takes only a few days, and the composite products are more nearly fully dense and have withstood temperatures as high as 4,350 F (approx.2,400 C) in a highly oxidizing thrust chamber environment. Moreover, because the melt- infiltration-based process takes much less time, the finished products are expected to cost much less. Fabrication begins with the preparation of a carbon fiber preform that, typically, is of the size and shape of a part to be fabricated. By use of low-temperature ultraviolet-enhanced chemical vapor deposition, the carbon fibers in the preform are coated with one or more interfacial material(s), which could include oxides. The interfacial material helps to protect the fibers against chemical attack during the remainder of the fabrication process and against oxidation during subsequent use; it also enables slippage between the fibers and the matrix material, thereby helping to deflect cracks and distribute loads. Once the fibers have been coated with the interfacial material, the fiber preform is further infiltrated with a controlled amount of additional carbon, which serves as a reactant for the formation of the carbide matrix material. The next step is melt infiltration. The preform is exposed to molten zirconium, which wicks into the preform, drawn by capillary action. The molten metal fills most of the interstices of the preform and reacts with the added carbon to form the zirconium carbide matrix material. The zirconium does not react with the underlying fibers because they

  2. Electrochemical behavior of flavin adenine dinucleotide adsorbed onto carbon nanotube and nitrogen-doped carbon nanotube electrodes.

    PubMed

    Goran, Jacob M; Stevenson, Keith J

    2013-11-01

    Flavin adenine dinucleotide (FAD) is a cofactor for many enzymes, but also an informative redox active surface probe for electrode materials such as carbon nanotubes (CNTs) and nitrogen-doped CNTs (N-CNTs). FAD spontaneously adsorbs onto the surface of CNTs and N-CNTs, displaying Langmuir adsorption characteristics. The Langmuir adsorption model provides a means of calculating the electroactive surface area (ESA), the equilibrium constant for the adsorption and desorption processes (K), and the Gibbs free energy of adsorption (ΔG°). Traditional ESA measurements based on the diffusional flux of a redox active molecule to the electrode surface underestimate the ESA of porous materials because pores are not penetrated. Techniques such as gas adsortion (BET) overestimate the ESA because it includes both electroactive and inactive areas. The ESA determined by extrapolation of the Langmuir adsorption model with the electroactive surface probe FAD will penetrate pores and only include electroactive areas. The redox activity of adsorbed FAD also displays a strong dependency on pH, which provides a means of determining the pKa of the surface confined species. The pKa of FAD decreases as the nitrogen content in the CNTs increases, suggesting a decreased hydrophobicity of the N-CNT surface. FAD desorption at N-CNTs slowly transforms the main FAD surface redox reaction with E1/2 at -0.84 V into two new, reversible, surface confined redox reactions with E1/2 at -0.65 and -0.76 V (vs Hg/Hg2SO4), respectively (1.0 M sodium phosphate buffer pH = 6.75). This is the first time these redox reactions have been observed. The new surface confined redox reactions were not observed during FAD desorption from nondoped CNTs.

  3. Does Moisture Influence the Chemical Detection of Gas Molecules Adsorbed on Single-Wall Carbon Nanotubes?

    NASA Astrophysics Data System (ADS)

    Yu, Ming; Tian, W. Q.; Jayanthi, C. S.; Wu, S. Y.

    2009-03-01

    In this work, the role of water in the detection of hydrazine (N2H4) by a single-wall carbon nanotube (SWCNT) is investigated using first principles electronic structure calculations (DFT/GGA--USPP)[1]. This calculation is undertaken to interpret the experimental resistivity measurements for N2H4 adsorbed on SWCNT that reveal an n-type behavior [2]. Our preliminary theoretical studies of the adsorption of N2H4 on SWCNT revealed physisorption for N2H4 and an unaltered band structure for the SWCNT [3]. This prompted us to look into the role of water on the bonding of N2H4 to the SWCNT. We found that, by introducing a monolayer of water film on the (8,0) SWCNT, the adsorption of N2H4 can introduce occupied states near the Fermi level, exhibiting an n-type behavior. However, the introduction of just few water molecules was not sufficient to influence the electronic structure of N2H4/SWCNT. Presently, we are studying the influence of water films on the chemical detection of a variety of other gas molecules (N2, NH3, etc.) by SWCNTs, and the results from such studies will also be reported. [1]. G. Kresse et al. Phys. Rev. B 54, 11169 (1996). [2]. S. Desai, et al. (APS, March 2008). [3]. M. Yu, et al. (APS, March 2008).

  4. Regeneration of granular activated carbon with adsorbed trichloroethylene using wet peroxide oxidation.

    PubMed

    Okawa, Kiyokazu; Suzuki, Kazuyoshi; Takeshita, Toshihiro; Nakano, Katsuyuki

    2007-03-01

    The objective of this study is to clarify the regeneration of granular activated carbon (GAC) adsorbed trichloroethylene (TCE) using wet peroxide oxidation (WPO). TCE and TOC concentrations decreased during WPO, whereas Cl(-) accumulated in water indicating that TCE was not only decomposed but was also mineralized to Cl(-) and CO(2) using WPO. Regeneration efficiencies (q/q(0)) of GAC regenerated at 150, 165 and 180 degrees C (initial pH 4) were 0.36, 0.45, 0.48, respectively. In addition, regeneration efficiencies of GAC regenerated in the solution of various initial pH (2.5, 3.0, 4.0) at 180 degrees C were 0.71, 0.60, 0.48, respectively. These results suggest that regeneration of GAC is more effective at higher reaction temperature and lower initial pH of the solution. In the repeated regeneration of GAC, the adsorption capacity of GAC for TCE gradually decreased and regeneration efficiency of the regenerated GAC at sixth step was 0.40. The adsorption capacity loss of regenerated GAC is probably due to oxidation of GAC during WPO. PMID:17224174

  5. Activated carbon prepared from coffee pulp: potential adsorbent of organic contaminants in aqueous solution.

    PubMed

    Gonçalves, Maraisa; Guerreiro, Mário César; Ramos, Paulize Honorato; de Oliveira, Luiz Carlos Alves; Sapag, Karim

    2013-01-01

    The processing of coffee beans generates large amounts of solid and liquid residues. The solid residues (pulp, husk and parchment) represent a serious environmental problem and do not have an adequate disposal mechanism. In this work, activated carbons (ACs) for adsorption of organic compounds were prepared from coffee pulp by controlled temperature at different pulp/Na2HPO4 ratios (4:1, 2:1, 5:4 and 1:1). The N2 adsorption/desorption isotherms showed ACs with high quantities of mesopores and micropores and specific surface areas of 140, 150, 450 and 440 m(2)g(-1) for AC 4:1, AC 2:1, AC 5:4 and AC 1:1, respectively. The prepared material AC 5:4 showed a higher removal capacity of the organic contaminants methylene blue (MB), direct red (DR) and phenol than did a Merck AC. The maximum capacities for this AC are approximately 150, 120 and 120 mg g(-1) for MB, DR and phenol, respectively. Thus, a good adsorbent was obtained from coffee pulp, an abundant Brazilian residue.

  6. Effect of biomass addition on the surface and adsorption characterization of carbon-based adsorbents from sewage sludge.

    PubMed

    Wu, Changzi; Song, Min; Jin, Baosheng; Wu, Yimin; Huang, Yaji

    2013-02-01

    Sewage sludge with the additive corn cob was used as prescusor to prepare sludge-based carbon adsorbents by pyrolysis method. And then, the carbonizated products were activated with potassium hydroxide. The mixing ratio of the corn cob to sewage sludge was investigated. The surface area and pore size distribution, elemental composition, surface chemistry structure and the surface physical morphology were determined and compared. The results demonstrated that the addition of corn cob into the sewage sludge sample could effectively improve the surface area (from 287 to 591 m2/g) and the microporosity (from 5% to 48%) of the carbon based adsorbent, thus enhancing the adsorption behavior. The sulfur dioxide adsorption capacity was measured according to breakthrough test. It was found that the sulfur dioxide adsorption capacity of the adsorbents was obviously enhanced after the addition of the corn cob. It is presumed that not only highly porous adsorbents, but also a high metallic content of these materials are required to achieve good performances. PMID:23596963

  7. Thermodynamics of the adsorption of organic compounds from the gas phase over a monolayer of liquid crystal formed on the surface of a carbon adsorbent

    NASA Astrophysics Data System (ADS)

    Kopytin, K. A.; Bykov, E. S.; Onuchak, L. A.; Kudryashov, S. Yu.; Kuvshinova, S. A.; Burmistrov, V. A.

    2015-04-01

    Inverse gas-solid chromatography is used to study the adsorption of vapors of organic compounds with different structures and polarities on a carbon adsorbent modified with a monolayer of 4-(3-hydroxypropyloxy)-4'-formylazobenzene (HPOFAB) polar LIQUID crystal. The resulting thermodynamic characteristics of adsorption on the original and modified adsorbents are compared. The effect the nature and structure of adsorbate molecules and the liquid crystal modifier have on the thermodynamic characteristics of adsorption is considered.

  8. Characterization of carbon fiber reinforced resin composites by the nanoindentation technique

    NASA Astrophysics Data System (ADS)

    Sun, Yuli; Zuo, Dunwen; Cao, Lianjing; Lu, Wenzhuang; Zhu, Yongwei; Li, Jun

    2013-08-01

    The mechanical properties of carbon fiber reinforced resin composites (CFRP) including the epoxy matrix, the carbon fiber and the interface of the carbon fiber/epoxy composites were investigated by means of nanoindentation technique. The hardness, Young's modulus of the components in CFRP were obtained. The results show that the hardness and Young's modulus have a gradient variation from the epoxy matrix to carbon fiber.

  9. Double-peak mechanical properties of carbon-nanotube fibers.

    PubMed

    Zhao, Jingna; Zhang, Xiaohua; Di, Jiangtao; Xu, Geng; Yang, Xiaojie; Liu, Xiangyang; Yong, Zhenzhong; Chen, Minghai; Li, Qingwen

    2010-11-22

    The introduction of twist during the spinning of carbon nanotubes from their arrays (forests) has been widely applied in making ultrastrong, stiff, and lightweight nanotube fibers. Here, for the first time, an important observation of a double-peak behavior of the tensile properties, as a function of the twist angle, that is different from the single peak of traditional fibers is reported. Raman spectra show that the new peak arises from the collapse of nanotubes, showing a strong "nano" element in applying the ancient draw-and-twist technique, besides the downsizing. A qualitative continuum model is also presented to describe the collapse-induced enhancement as well as traditional fibers. Our combined experimental and theoretical studies indicate the direction of full utilization of the nano element in improving the mechanical properties of nanotube fibers. PMID:20941775

  10. Diamagnetic studies on as-processed carbon fibers

    NASA Technical Reports Server (NTRS)

    Scott, C. B.; Fischbach, D. B.

    1976-01-01

    The Faraday method has been used to measure the diamagnetic susceptibilities of small bundles of aligned carbon fibers of different types at room temperature. It was found that the tensor trace susceptibility of the fibers varies systematically over the range 0.8-20 (in units of -10 to the -6th emu/g) as a function of precursor type and processing history. The susceptibility increases, in general, with increasing nominal treatment temperature and hot stretching, and with increasing tensile elastic modulus. The anisotropy ratio of fibers increases approximately linearly with tensile elastic modulus for all fibers from about 1 for a modulus of about 70 GN/sq m to about 22 for a modulus of 700 GN/sq m in air, and is quantitatively consistent with the layer-plane orientation textures determined by X-ray diffraction when appropriate values of the crystallite principal susceptibilities are used.

  11. Treated carbon fibers with improved performance for electrochemical and chemical applications

    DOEpatents

    Chu, Xi; Kinoshita, Kimio

    1999-01-01

    A treated mesophase carbon fiber is disclosed having a high density of exposed edges on the fiber surface, and a method of making such a treated fiber. A carbon electrode is also described which is constructed from such treated mesophase carbon fibers. The resulting electrode, formed from such treated flexible carbon fibers, is characterized by a high density of active sites formed from such exposed edges, low corrosion, and good mechanical strength, and may be fabricated into various shapes. The treated mesophase carbon fibers of the invention are formed by first loading the surface of the mesophase carbon fiber with catalytic metal particles to form catalytic etch sites on a hard carbon shell of the fiber. The carbon fiber is then subject to an etch step wherein portions of the hard carbon shell or skin are selectively removed adjacent the catalytic metal particles adhering to the carbon shell. This exposes the underlying radial edges of the graphite-like layers within the carbon shell of the mesophase carbon fiber, which exposed radial edges then act as active sites of a carbon electrode subsequently formed from the treated mesophase carbon fibers.

  12. Treated carbon fibers with improved performance for electrochemical and chemical applications

    DOEpatents

    Chu, X.; Kinoshita, Kimio

    1999-02-23

    A treated mesophase carbon fiber is disclosed having a high density of exposed edges on the fiber surface, and a method is described for making such a treated fiber. A carbon electrode is also described which is constructed from such treated mesophase carbon fibers. The resulting electrode, formed from such treated flexible carbon fibers, is characterized by a high density of active sites formed from such exposed edges, low corrosion, and good mechanical strength, and may be fabricated into various shapes. The treated mesophase carbon fibers of the invention are formed by first loading the surface of the mesophase carbon fiber with catalytic metal particles to form catalytic etch sites on a hard carbon shell of the fiber. The carbon fiber is then subject to an etch step wherein portions of the hard carbon shell or skin are selectively removed adjacent the catalytic metal particles adhering to the carbon shell. This exposes the underlying radial edges of the graphite-like layers within the carbon shell of the mesophase carbon fiber, which exposed radial edges then act as active sites of a carbon electrode subsequently formed from the treated mesophase carbon fibers. 14 figs.

  13. Amperometric Carbon Fiber Nitrite Microsensor for In Situ Biofilm Monitoring

    EPA Science Inventory

    A highly selective needle type solid state amperometric nitrite microsensor based on direct nitrite oxidation on carbon fiber was developed using a simplified fabrication method. The microsensor’s tip diameter was approximately 7 µm, providing a high spatial resolution of at lea...

  14. Vibration monitoring of carbon fiber composites by multiple fiber optic sensors

    NASA Astrophysics Data System (ADS)

    Olivero, Massimo; Perrone, Guido; Vallan, Alberto; Chen, Wei; Tosi, Daniele

    2014-05-01

    This work presents the comparison between the fiber Bragg grating technology and a vibration-measurement technique based on the detection of polarization rotation (polarimetric sensor) in a standard optical fiber, applied to the dynamic structural monitoring of carbon reinforced composites for the automotive industry. A carbon reinforced composite test plate in a 4-layer configuration was equipped with fiber Bragg gratings and polarimetric fiber sensors, then it was mechanically stressed by static and dynamic loads while monitoring the sensors response. The fiber Bragg grating setup exhibited 1.15+/-0.0016 pm/kg static load response and reproduced dynamic excitation with 0.1% frequency uncertainty, while the polarimetric sensing system exhibited a sensitivity of 1.74+/-0.001 mV/kg and reproduced the dynamic excitation with 0.5% frequency uncertainty. It is shown that the polarimetric sensor technology represents a cheap yet efficient alternative to the fiber Bragg grating sensors in the case of vibration-monitoring of small structures at high frequency.

  15. Approach to the assessment of the hazard. [fire released carbon fiber electrical effects

    NASA Technical Reports Server (NTRS)

    Huston, R. J.

    1980-01-01

    An overview of the carbon fiber hazard assessment is presented. The potential risk to the civil sector associated with the accidental release of carbon fibers from aircraft having composite structures was assessed along with the need for protection of civil aircraft from carbon fibers.

  16. Preparation of array of long carbon nanotubes and fibers therefrom

    DOEpatents

    Arendt, Paul N.; DePaula, Ramond F.; Zhu, Yuntian T.; Usov, Igor O.

    2015-11-19

    An array of carbon nanotubes is prepared by exposing a catalyst structure to a carbon nanotube precursor. Embodiment catalyst structures include one or more trenches, channels, or a combination of trenches and channels. A system for preparing the array includes a heated surface for heating the catalyst structure and a cooling portion that cools gas above the catalyst structure. The system heats the catalyst structure so that the interaction between the precursor and the catalyst structure results in the formation of an array of carbon nanotubes on the catalyst structure, and cools the gas near the catalyst structure and also cools any carbon nanotubes that form on the catalyst structure to prevent or at least minimize the formation of amorphous carbon. Arrays thus formed may be used for spinning fibers of carbon nanotubes.

  17. Evaluation of micron size carbon fibers released from burning graphite composites

    NASA Technical Reports Server (NTRS)

    Sussholz, B.

    1980-01-01

    Quantitative estimates were developed of micron carbon fibers released during the burning of graphite composites. Evidence was found of fibrillated particles which were the predominant source of the micron fiber data obtained from large pool fire tests. The fibrillation phenomena were attributed to fiber oxidation effects caused by the fire environment. Analysis of propane burn test records indicated that wind sources can cause considerable carbon fiber oxidation. Criteria estimates were determined for the number of micron carbon fibers released during an aircraft accident. An extreme case analysis indicated that the upper limit of the micron carbon fiber concentration level was only about half the permissible asbestos ceiling concentration level.

  18. Mechanical properties of continuously spun fibers of carbon nanotubes.

    PubMed

    Motta, Marcelo; Li, Ya-Li; Kinloch, Ian; Windle, Alan

    2005-08-01

    We report on the mechanical properties of fibers consisting of pure carbon nanotube fibers directly spun from an aerogel formed during synthesis by chemical vapor deposition. The continuous withdrawal of product from the gas phase imparts a high commercial potential to the process, either for the production of particularly strong fibers or for the economic production of bulk quantities of carbon nanotubes. Tensile tests were performed on fibers produced from the dissociation of three different hydrocarbons, namely, ethanol, ethylene glycol, and hexane, with a range of iron (catalyst) concentrations. The conditions were chosen to lie within the range known to enable satisfactory continuous spinning, the iron concentration being varied within this range. Increasing proportions of single wall nanotubes were found as the iron concentration was decreased, conditions which also produced fibers of best strength and stiffness. The maximum tensile strength obtained was 1.46 GPa (equivalent to 0.70 N/tex assuming a density of 2.1 g/cm(3)). The experiments indicate that significant improvements in the mechanical properties can be accomplished by optimizing the process conditions. PMID:16089483

  19. Interfacial Microstructure and Enhanced Mechanical Properties of Carbon Fiber Composites Caused by Growing Generation 1-4 Dendritic Poly(amidoamine) on a Fiber Surface.

    PubMed

    Gao, Bo; Zhang, Ruliang; Gao, Fucheng; He, Maoshuai; Wang, Chengguo; Liu, Lei; Zhao, Lifen; Cui, Hongzhi

    2016-08-23

    In an attempt to improve the mechanical properties of carbon fiber composites, propagation of poly(amidoamine) (PAMAM) dendrimers by in situ polymerization on a carbon fiber surface was performed. During polymerization processes, PAMAM was grafted on carbon fiber by repeated Michael addition and amidation reactions. The changes in surface microstructure and the chemical composition of carbon fibers before and after modification were investigated by atomic force microscopy, X-ray photoelectron spectroscopy, and Raman spectroscopy. All the results indicated that PAMAM was successfully grown on the carbon fiber surface. Such propagation could significantly increase the surface roughness and introduce sufficient polar groups onto the carbon fiber surface, enhancing the surface wettability of carbon fiber. The fractured surface of carbon fiber-reinforced composites showed a great enhancement of interfacial adhesion. Compared with those of desized fiber composites, the interlaminar shear strength and interfacial shear strength of PAMAM/fiber-reinforced composites showed increases of 55.49 and 110.94%, respectively.

  20. Carbon fiber plume sampling for large scale fire tests at Dugway Proving Ground. [fiber release during aircraft fires

    NASA Technical Reports Server (NTRS)

    Chovit, A. R.; Lieberman, P.; Freeman, D. E.; Beggs, W. C.; Millavec, W. A.

    1980-01-01

    Carbon fiber sampling instruments were developed: passive collectors made of sticky bridal veil mesh, and active instruments using a light emitting diode (LED) source. These instruments measured the number or number rate of carbon fibers released from carbon/graphite composite material when the material was burned in a 10.7 m (35 ft) dia JP-4 pool fire for approximately 20 minutes. The instruments were placed in an array suspended from a 305 m by 305 m (1000 ft by 1000 ft) Jacob's Ladder net held vertically aloft by balloons and oriented crosswind approximately 140 meters downwind of the pool fire. Three tests were conducted during which released carbon fiber data were acquired. These data were reduced and analyzed to obtain the characteristics of the released fibers including their spatial and size distributions and estimates of the number and total mass of fibers released. The results of the data analyses showed that 2.5 to 3.5 x 10 to the 8th power single carbon fibers were released during the 20 minute burn of 30 to 50 kg mass of initial, unburned carbon fiber material. The mass released as single carbon fibers was estimated to be between 0.1 and 0.2% of the initial, unburned fiber mass.

  1. A phase-stabilized carbon nanotube fiber laser frequency comb.

    PubMed

    Lim, Jinkang; Knabe, Kevin; Tillman, Karl A; Neely, William; Wang, Yishan; Amezcua-Correa, Rodrigo; Couny, François; Light, Philip S; Benabid, Fetah; Knight, Jonathan C; Corwin, Kristan L; Nicholson, Jeffrey W; Washburn, Brian R

    2009-08-01

    A frequency comb generated by a 167 MHz repetition frequency erbium-doped fiber ring laser using a carbon nanotube saturable absorber is phase-stabilized for the first time. Measurements of the in-loop phase noise show an integrated phase error on the carrier envelope offset frequency of 0.35 radians. The carbon nanotube fiber laser comb is compared with a CW laser near 1533 nm stabilized to the nu(1) + nu(3) overtone transition in an acetylene-filled kagome photonic crystal fiber reference, while the CW laser is simultaneously compared to another frequency comb based on a Cr:Forsterite laser. These measurements demonstrate that the stability of a GPS-disciplined Rb clock is transferred to the comb, resulting in an upper limit on the locked comb's frequency instability of 1.2 x 10(-11) in 1 s, and a relative instability of <3 x 10(-12) in 1 s. The carbon nanotube laser frequency comb offers much promise as a robust and inexpensive all-fiber frequency comb with potential for scaling to higher repetition frequencies.

  2. THERMAL INSULATION FROM LIGNIN-DERIVED CARBON FIBERS

    SciTech Connect

    Albers, Tracy; Chen, Chong; Eberle, Cliff; Webb, Daniel C

    2014-01-01

    Oak Ridge National Laboratory (ORNL) and GrafTech International Holdings Inc. (GrafTech) have collaborated to develop and demonstrate the performance of high temperature thermal insulation prototypes made from lignin-based carbon fibers (LBCF). This was the first reported production of LBCF or resulting products at scale > 1 kg. The results will potentially lead to the first commercial application of LBCF. The goal of the commercial application is to replace expensive, foreign-sourced isotropic pitch carbon fibers with lower cost carbon fibers made from a domestically sourced, bio-derived (renewable) feedstock. LBCF can help resolve supply chain vulnerability and reduce the production cost for high temperature thermal insulation as well as create US jobs. The performance of the LBCF prototypes was measured and found to be comparable to that of the current commercial product. During production of the insulation prototypes, the project team demonstrated lignin compounding/pelletization, fiber production, heat treatment, and compositing at scales far surpassing those previously demonstrated in LBCF R&D or production.

  3. Life Cycle Assessment of Carbon Fiber-Reinforced Polymer Composites

    SciTech Connect

    Das, Sujit

    2011-01-01

    Carbon fiber-reinforced polymer matrix composites is gaining momentum with the pressure to lightweight vehicles, however energy-intensity and cost remain some of the major barriers before this material could be used in large-scale automotive applications. A representative automotive part, i.e., a 30.8 kg steel floor pan having a 17% weight reduction potential with stringent cash performance requirements has been considered for the life cycle energy and emissions analysis based on the latest developments occurring in the precursor type (conventional textile-based PAN vs. renewable-based lignin), part manufacturing (conventional SMC vs. P4) and fiber recycling technologies. Carbon fiber production is estimated to be about 14 times more energy-intensive than conventional steel production, however life cycle primary energy use is estimated to be quite similar to the conventional part, i.e., 18,500 MJ/part, especially when considering the uncertainty in LCI data that exists from using numerous sources in the literature. Lignin P4 technology offers the most life cycle energy and CO2 emissions benefits compared to a conventional stamped steel technology. With a 20% reduction in energy use in the lignin conversion to carbon fiber and free availability of lignin as a by-product of ethanol and wood production, a 30% reduction in life cycle energy use could be obtained. A similar level of life cycle energy savings could also be obtained with a higher part weight reduction potential of 43%.

  4. Single walled carbon nanotubes functionally adsorbed to biopolymers for use as chemical sensors

    DOEpatents

    Johnson, Jr., Alan T.; Gelperin, Alan; Staii, Cristian

    2011-07-12

    Chemical field effect sensors comprising nanotube field effect devices having biopolymers such as single stranded DNA functionally adsorbed to the nanotubes are provided. Also included are arrays comprising the sensors and methods of using the devices to detect volatile compounds.

  5. Interfacial properties of two-carbon fiber reinforced polycarbonate composites using two-synthesized graft copolymers as coupling agents

    SciTech Connect

    Park, J.M.

    2000-05-15

    Two model coupling agents, water-dispersible (WDGP) and tetrahydrofuran (THF)-soluble graft copolymers (TSGP), were synthesized for carbon fiber/polycarbonate (PC) composites. WDGP contains a long polyacrylamide (PAAm) chain grafted on a PC backbone, whereas TSGP contains a short grafted PAAm Chain. Measurements of the interfacial shear strength (IFSS) and other interfacial properties were evaluated using a fragmentation test for two-fiber composites (TFC) to provide the same loading state. Optimal conditions for the treatment was established as a function of treatment time, temperature, initial concentration, and melting procedure. The amount adsorbed on the carbon fiber was higher for WDGP and TSGP were 54% and 74%, respectively. Mechanisms of energy adsorption for WDGP and intermolecular interaction for TSGP can be considered to contribute differently to IFSS improvement. The improvement in IFSS for both coupling agents may be due to chemical and hydrogen bonding in the interface between functional groups in the carbon fiber and PAAm in the coupling agents and to interdiffusion in the interface between PC in coupling agents and matrix PC.

  6. Development of a Novel Activated Carbon Based Adsorbents for control of Mercury Emissions from Coal-Fired Power Plants

    SciTech Connect

    Vidic, R.D.

    1997-03-17

    The overall objective of this study is to evaluate pertinent design and operational parameters that would enable successful application of activated carbon adsorption for the reduction of mercury emissions from coal-fired power plants. The study will evaluate the most suitable impregnate such as sulfur, chloride and other chelating agents for its ability to enhance the adsorptive capacity of activated carbon for mercury vapor under various process conditions. The main process variables to be evaluated include temperature, mercury concentration and speciation, relative humidity, oxygen content, and presence of S0{sub 2} and NO{sub x} in the flue gas. The optimal amount of impregnate for each of these carbons will be determined based on the exhibited performance. Another important parameter which governs the applicability of adsorption technology for the flue gas clean up is the rate at which vapor phase mercury is being removed from the flue gas by activated carbon. Therefore, the second part of this study will evaluate the adsorption kinetics using the impregnated activated carbons listed above. The rate of mercury uptake will also be evaluated under the process conditions that are representative of coal-fired power plants. Concerned with the ability of the adsorbed mercury to migrate back into the environment once saturated adsorbent is removed from the system, the study will also focus on the mercury desorption rate as a function of the type of impregnate, loading conditions, and the time of contact prior to disposal.

  7. Multifunctional structural supercapacitor composites based on carbon aerogel modified high performance carbon fiber fabric.

    PubMed

    Qian, Hui; Kucernak, Anthony R; Greenhalgh, Emile S; Bismarck, Alexander; Shaffer, Milo S P

    2013-07-10

    A novel multifunctional material has been designed to provide excellent mechanical properties while possessing a high electrochemical surface area suitable for electrochemical energy storage: structural carbon fiber fabrics are embedded in a continuous network of carbon aerogel (CAG) to form a coherent but porous monolith. The CAG-modification process was found to be scalable and to be compatible with a range of carbon fiber fabrics with different surface properties. The incorporation of CAG significantly increased the surface area of carbon fiber fabrics, and hence the electrochemical performance, by around 100-fold, resulting in a CAG-normalized specific electrode capacitance of around 62 F g(-1), determined by cyclic voltammetry in an aqueous electrolyte. Using an ionic liquid (IL) electrolyte, the estimated energy density increased from 0.003 to 1 Wh kg(-1), after introducing the CAG into the carbon fiber fabric. 'Proof-of-concept' multifunctional structural supercapacitor devices were fabricated using an IL-modified solid-state polymer electrolyte as a multifunctional matrix to provide both ionic transport and physical support for the primary fibers. Two CAG-impregnated carbon fabrics were sandwiched around an insulating separator to form a functioning structural electrochemical double layer capacitor composite. The CAG-modification not only improved the electrochemical surface area, but also reinforced the polymer matrix surrounding the primary fibers, leading to dramatic improvements in the matrix-dominated composite properties. Increases in in-plane shear strength and modulus, of up to 4.5-fold, were observed, demonstrating that CAG-modified structural carbon fiber fabrics have promise in both pure structural and multifunctional energy storage applications.

  8. Mesocarbon Microbead Carbon-Supported Magnesium Hydroxide Nanoparticles: Turning Spent Li-ion Battery Anode into a Highly Efficient Phosphate Adsorbent for Wastewater Treatment.

    PubMed

    Zhang, Yan; Guo, Xingming; Wu, Feng; Yao, Ying; Yuan, Yifei; Bi, Xuanxuan; Luo, Xiangyi; Shahbazian-Yassar, Reza; Zhang, Cunzhong; Amine, Khalil

    2016-08-24

    Phosphorus in water eutrophication has become a serious problem threatening the environment. However, the development of efficient adsorbents for phosphate removal from water is lagging. In this work, we recovered the waste material, graphitized carbon, from spent lithium ion batteries and modified it with nanostructured Mg(OH)2 on the surface to treat excess phosphate. This phosphate adsorbent shows one of the highest phosphate adsorption capacities to date, 588.4 mg/g (1 order of magnitude higher than previously reported carbon-based adsorbents), and exhibits decent stability. A heterogeneous multilayer adsorption mechanism was proposed on the basis of multiple adsorption results. This highly efficient adsorbent from spent Li-ion batteries displays great potential to be utilized in industry, and the mechanism study paved a way for further design of the adsorbent for phosphate adsorption. PMID:27463402

  9. Strong Carbon Nanotube Fibers by Drawing Inspiration from Polymer Fiber Spinning.

    PubMed

    Alemán, Belén; Reguero, Víctor; Mas, Bartolomé; Vilatela, Juan J

    2015-07-28

    We present a method to spin highly oriented continuous fibers of adjustable carbon nanotube (CNT) type, with mechanical properties in the high-performance range. By lowering the concentration of nanotubes in the gas phase, through either reduction of the precursor feed rate or increase in carrier gas flow rate, the density of entanglements is reduced and the CNT aerogel can thus be drawn (up to 18 draw ratio) and wound at fast rates (>50 m/min). This is achieved without affecting the synthesis process, as demonstrated by Raman spectroscopy, and implies that the parameters controlling composition in terms of CNT diameter and number of layers are decoupled from those fixing CNT orientation. Applying polymer fiber wet-spinning principles then, strong CNT fibers (1 GPa/SG) are produced under dilute conditions and high draw ratios, corresponding to highly aligned fibers (from wide- and small-angle X-ray scattering). This is demonstrated for fibers either made up of predominantly single-wall CNTs (SWCNTs) or predominantly multiwall CNTs (MWCNTs), which surprisingly have very similar tensile properties. Finally, we show that postspin densification has no substantial effect on either alignment or properties (mechanical and electrical). These results demonstrate a route to control CNT assembly and reinforce their potential as a high-performance fiber. PMID:26082976

  10. Strong Carbon Nanotube Fibers by Drawing Inspiration from Polymer Fiber Spinning.

    PubMed

    Alemán, Belén; Reguero, Víctor; Mas, Bartolomé; Vilatela, Juan J

    2015-07-28

    We present a method to spin highly oriented continuous fibers of adjustable carbon nanotube (CNT) type, with mechanical properties in the high-performance range. By lowering the concentration of nanotubes in the gas phase, through either reduction of the precursor feed rate or increase in carrier gas flow rate, the density of entanglements is reduced and the CNT aerogel can thus be drawn (up to 18 draw ratio) and wound at fast rates (>50 m/min). This is achieved without affecting the synthesis process, as demonstrated by Raman spectroscopy, and implies that the parameters controlling composition in terms of CNT diameter and number of layers are decoupled from those fixing CNT orientation. Applying polymer fiber wet-spinning principles then, strong CNT fibers (1 GPa/SG) are produced under dilute conditions and high draw ratios, corresponding to highly aligned fibers (from wide- and small-angle X-ray scattering). This is demonstrated for fibers either made up of predominantly single-wall CNTs (SWCNTs) or predominantly multiwall CNTs (MWCNTs), which surprisingly have very similar tensile properties. Finally, we show that postspin densification has no substantial effect on either alignment or properties (mechanical and electrical). These results demonstrate a route to control CNT assembly and reinforce their potential as a high-performance fiber.

  11. High performance carbon fibers from very high molecular weight polyacrylonitrile precursors

    DOE PAGES

    Morris, E. Ashley; Weisenberger, Matthew C.; Abdallah, Mohamed G.; Vautard, Frederic; Grappe, Hippolyte A.; Ozcan, Soydan; Paulauskas, Felix L.; Eberle, Cliff; Jackson, David C.; Mecham, Sue J.; et al

    2016-02-02

    In this study, carbon fibers are unique reinforcing agents for lightweight composite materials due to their outstanding mechanical properties and low density. Current technologies are capable of producing carbon fibers with 90-95% of the modulus of perfect graphite (~1025 GPa). However, these same carbon fibers possess less than 10% of the theoretical carbon fiber strength, estimated to be about 100 GPa.[1] Indeed, attempts to increase carbon fiber rigidity results in lower breaking strength. To develop advanced carbon fibers with both very high strength and modulus demands a new manufacturing methodology. Here, we report a method of manufacturing high strength, verymore » high modulus carbon fibers from a very high molecular weight (VHMW) polyacrylonitrile (PAN) precursor without the use of nanomaterial additives such as nucleating or structure-templating agents, as have been used by others.[2,3]« less

  12. Microstructure analysis of complex CuO/ZnO@carbon adsorbers: what are the limits of powder diffraction methods?

    PubMed

    Tseng, J C; Schmidt, W; Sager, U; Däuber, E; Pommerin, A; Weidenthaler, C

    2015-05-14

    Activate carbon impregnated with a mixture of copper oxide and zinc oxide performs well as active adsorber for NO2 removal in automotive cabin air filters. The oxide-loaded activated carbon exhibits superior long-term stability in comparison to pure activated carbon as has been shown in previous studies. The carbon material was loaded only with 2.5 wt% of each metal oxide. Characterization of the oxide nanoparticles within the pores of the activated carbon is difficult because of the rather low concentration of the oxides. Therefore, a systematic study was performed to evaluate the limits of line profile analysis of X-ray powder diffraction patterns. The method allows evaluation of crystalline domain size distributions, crystal defect concentrations and twinning probabilities of nanoscopic materials. Here, the analysis is hampered by the presence of several phases including more or less amorphous carbon. By using physical mixtures of defined copper oxide and zinc oxide particles with activated carbon, potential errors and limits could be identified. The contribution of the activated carbon to the scattering curve was modeled with a convolution of an exponential decay curve, a Chebyshev polynomial, and two Lorentzian peaks. With this approach, domain size distributions can be calculated that are shifted only by about 0.5-1.0 nm for very low loadings (≤4 wt%). Oxide loadings of 4 wt% and 5 wt% allow very reliable analyses from diffraction patterns measured in Bragg-Brentano and Debye-Scherrer geometry, respectively. For the real adsorber material, mean domain sizes have been calculated to be 2.8 nm and 2.4 nm before and after the NO2 removal tests. PMID:25892653

  13. Influence of Lignin modification on PAN-Lignin copolymers as potential carbon fiber precursors

    NASA Astrophysics Data System (ADS)

    Ramasubramanian, Gauri

    Carbon fiber based polymer composites have been recognized as advanced materials for structural applications. The unique reinforcing abilities of carbon fibers with their combination of high strength-to-weight ratio and excellent fatigue resistance have made carbon fiber based composites exceptional compared to other fiber reinforced composites. However, the high cost involved in current precursor materials for carbon fibers has limited the widespread applicability of carbon fibers. Hence, intensification of research efforts towards cheaper and easily available raw material for fabrication of carbon fibers is justified. The growing demand for low cost carbon fibers for mainstream composite applications has driven recent interests in using lignin as alternative choice of material for carbon fiber precursor. Lignin is a highly aromatic, plant-derived amorphous polymer and has been considered as potential low-cost, bio-based carbon fiber precursor. Copolymers of polyacrylonitrile/lignin were developed as alternative precursors for fabrication of raw fibers using conventional solution spinning techniques. Lignin/polyacrylonitrile copolymers were successfully synthesized and characterized using FT-IR and NMR techniques. The thermal properties of the copolymers were studied by DSC and TGA analysis. The effect of chemical modification on the morphology and stability of the carbon fibers from PAN-Lignin copolymers has been studied using Raman Spectroscopy, X-ray Diffraction and Scanning Electron Microscopy. Modification of lignin prior to copolymerization provided a significant advantage in the improvement of precursor processability using solution spinning. Additionally, carbon fibers obtained from copolymers containing different varieties of lignins were examined. Carbon fibers produced from organosolv lignin/polyacrylonitrile copolymers exhibit promising carbon fiber structure when compared to softwood/lignin polyacrylonitrile copolymers.

  14. Modified carbon fibers to improve composite properties. [sizing fibers for reduced electrical conductivity and adhesion during combustion

    NASA Technical Reports Server (NTRS)

    Shepler, R. E.

    1979-01-01

    Thin coatings, 5 to 10 wt. percent, were applied to PAN-based carbon fibers. These coatings were intended to make the carbon fibers less electrically conductive or to cause fibers to stick together when a carbon fiber/epoxy composite burned. The effectiveness of the coatings in these regards was evaluated in burn tests with a test rig designed to simulate burning, impact and wind conditions which might release carbon fibers. The effect of the coatings on fiber and composite properties and handling was also investigated. Attempts at sizing carbon fibers with silicon dioxide, silicon carbide and boron nitride meet with varying degrees of success; however, none of these materials provided an electrically nonconductive coating. Coatings intended to stick carbon fibers together after a composite burned were sodium silicate, silica gel, ethyl silicate, boric acid and ammonium borate. Of these, only the sodium silicate and silica gel provided any sticking together of fibers. The amount of sticking was insufficient to achieve the desired objectives.

  15. A New Fiber Preform with Nanocarbon Binder for Manufacturing Carbon Fiber Reinforced Composite by Liquid Molding Process.

    PubMed

    Seong, Dong Gi; Ha, Jong Rok; Lee, Jea Uk; Lee, Wonoh; Kim, Byung Sun

    2015-11-01

    Carbon fiber reinforced composite has been a good candidate of lightweight structural component in the automotive industry. As fast production speed is essential to apply the composite materials for the mass production area such as automotive components, the high speed liquid composite molding processes have been developed. Fast resin injection through the fiber preform by high pressure is required to improve the production speed, but it often results in undesirable deformations of the fiber preform which causes defectives in size and properties of the final composite products. In order to prevent the undesirable deformation and improve the stability of preform shape, polymer type binder materials are used. More stable fiber preform can be obtained by increasing the amount of binder material, but it disturbs the resin impregnation through the fiber preform. In this study, carbon nanomaterials such as graphene oxide were embedded on the surface of carbon fiber by electrophoretic deposition method in order to improve the shape stability of fiber preform and interfacial bonding between polymer and the reinforcing fiber. Effects of the modified reinforcing fiber were investigated in two respects. One is to increase the binding energy between fiber tows, and the other is to increase the interfacial bonding between polymer matrix and fiber surface. The effects were analyzed by measuring the binding force of fiber preform and interlaminar shear strength of the composite. This study also investigated the high speed liquid molding process of the composite materials composed of polymer matrix and the carbon fiber preforms embedded by carbon nanomaterials. Process parameter such as permeability of fiber preform was measured to investigate the effect of nanoscale surface modification on the macroscale processing condition for composite manufacturing. PMID:26726642

  16. A New Fiber Preform with Nanocarbon Binder for Manufacturing Carbon Fiber Reinforced Composite by Liquid Molding Process.

    PubMed

    Seong, Dong Gi; Ha, Jong Rok; Lee, Jea Uk; Lee, Wonoh; Kim, Byung Sun

    2015-11-01

    Carbon fiber reinforced composite has been a good candidate of lightweight structural component in the automotive industry. As fast production speed is essential to apply the composite materials for the mass production area such as automotive components, the high speed liquid composite molding processes have been developed. Fast resin injection through the fiber preform by high pressure is required to improve the production speed, but it often results in undesirable deformations of the fiber preform which causes defectives in size and properties of the final composite products. In order to prevent the undesirable deformation and improve the stability of preform shape, polymer type binder materials are used. More stable fiber preform can be obtained by increasing the amount of binder material, but it disturbs the resin impregnation through the fiber preform. In this study, carbon nanomaterials such as graphene oxide were embedded on the surface of carbon fiber by electrophoretic deposition method in order to improve the shape stability of fiber preform and interfacial bonding between polymer and the reinforcing fiber. Effects of the modified reinforcing fiber were investigated in two respects. One is to increase the binding energy between fiber tows, and the other is to increase the interfacial bonding between polymer matrix and fiber surface. The effects were analyzed by measuring the binding force of fiber preform and interlaminar shear strength of the composite. This study also investigated the high speed liquid molding process of the composite materials composed of polymer matrix and the carbon fiber preforms embedded by carbon nanomaterials. Process parameter such as permeability of fiber preform was measured to investigate the effect of nanoscale surface modification on the macroscale processing condition for composite manufacturing.

  17. System to continuously produce carbon fiber via microwave assisted plasma processing

    DOEpatents

    White, Terry L [Knoxville, TN; Paulauskas, Felix L [Knoxville, TN; Bigelow, Timothy S [Knoxville, TN

    2010-11-02

    A system to continuously produce fully carbonized or graphitized carbon fibers using microwave-assisted plasma (MAP) processing comprises an elongated chamber in which a microwave plasma is excited in a selected gas atmosphere. Fiber is drawn continuously through the chamber, entering and exiting through openings designed to minimize in-leakage of air. There is a gradient of microwave power within the chamber with generally higher power near where the fiber exits and lower power near where the fiber enters. Polyacrylonitrile (PAN), pitch, or any other suitable organic/polymeric precursor fibers can be used as a feedstock for the inventive system. Oxidized or partially oxidized PAN or pitch or other polymeric fiber precursors are run continuously through a MAP reactor in an inert, non-oxidizing atmosphere to heat the fibers, drive off the unwanted elements such as oxygen, nitrogen, and hydrogen, and produce carbon or graphite fibers faster than conventionally produced carbon fibers.

  18. BASIC PROPERTIES OF REFERENCE CROSSPLY CARBON-FIBER COMPOSITE

    SciTech Connect

    Corum, J.M.

    2001-01-11

    This report provides basic in-air property data and correlations-tensile, compressive, shear, tensile fatigue, and tensile creep-for a reference carbon-fiber composite being characterized as a part of the Durability of Carbon-Fiber Composites Project at Oak Ridge National Laboratory. The overall goal of the project, which is sponsored by the Department of Energy's Office of Advanced Automotive Materials and is closely coordinated with the Advanced Composites Consortium, is to develop durability-based design guidance for polymeric composites for automotive structural applications. The composite addressed here is a {+-}45{degree} crossply consisting of continuous Thornel T300 fibers in a Baydur 420 IMR urethane matrix. Basic tensile, compressive, and shear properties are tabulated for the temperature range from {minus}40 to 120 C. Fatigue response at room-temperature and 120 C are presented, and creep and creep rupture at room temperature only are reported. In all cases, two fiber orientations--0/90{degree} and {+-}45{degree}--relative to the specimen axes are addressed. The properties and correlations presented are interim in nature. They are intended as a baseline for planning a full durability test program on this reference composite.

  19. Vapor grown carbon fiber for space thermal management systems

    NASA Technical Reports Server (NTRS)

    Lake, Max L.; Hickok, J. Kyle; Brito, Karren K.; Begg, Lester L.

    1990-01-01

    Research that uses a novel, highly graphitic, vapor grown carbon fiber (VGCF) to fabricate composites for thermal management applications is described. These VGCF/Carbon composites have shown a specific thermal conductivity with values of twenty-to-ten times that of copper in the 500-900 K temperature range needed for waste heat management. It is concluded that development of this high specific thermal conductivity composite for thermal radiator panels will provide the foundation for a reevaluation of space power designs heretofore limited by the mass of waste heat dissipation systems. Further, it is suggested that through optimization of fiber handling and composite processing, thermal conductivities exceeding 1000 W/m-K (at 300 K) are achievable in composites reinforced with VGCF.

  20. Activation and micropore structure of carbon-fiber composites

    SciTech Connect

    Jagtoyen, M.; Derbyshire, F.; Kimber, G.

    1997-12-01

    Rigid, high surface area activated carbon fiber composites have been produced with high permeabilities for environmental applications in gas and water purification. The project involves a collaboration between the Oak Ridge National Laboratory (ORNL) and the Center for Applied Energy Research (CAER), University of Kentucky. The main focus of recent work has been to find a satisfactory means to uniformly activate large samples of carbon fiber composites to produce controlled pore structures. Processes have been developed using activation in steam and CO{sub 2}, and a less conventional method involving oxygen chemisorption and subsequent heat treatment. Another objective has been to explore applications for the activated composites in environmental applications related to fossil energy production.

  1. Defect visualization in carbon fiber composite using laser ultrasound

    SciTech Connect

    Dewhurst, R.J.; He, Ruhua; Shan, Qing . Dept. of Instrumentation and Analytical Science)

    1993-08-01

    A non-contacting laser ultrasound system has been developed to visualize laminar defects in carbon fiber composite materials. Laser-generated ultrasound (LGU) was produced from a Nd:YAG Q-switched laser. Ultrasound was detected with the use of an actively stabilized Fabry-Perot interferometer using a 400 mW argon-ion laser source. It detected ultrasound in a typical frequency range of 1 to 10 MHz. Through-transmission C-scan measurements were made in carbon fiber composite materials of thickness 1 to 20 mm. Peak-to-peak amplitudes of the first longitudinal ultrasonic pulse were measured, with attenuation used as the basis of defect examination. Digital filtering was adopted to enhance defect visibility. Results showed that images with size resolution better than 1 mm can be achieved. Such measurements take into account any variation of surface reflectivity which can arise in industrial materials.

  2. Dry synthesis of lithium intercalated graphite powders and carbon fibers

    SciTech Connect

    Sacci, Robert L; Adamczyk, Leslie A; Veith, Gabriel M; Dudney, Nancy J

    2014-01-01

    Herein we describe the direct synthesis of lithium intercalated graphite by heating under vacuum or ball milling under pressurized Ar(g). Both methods allow for stoichometric control of Li-C ratio in batter-grade graphites and carbon fibers prior formation of a solid electrolyte interphase. The products' surface chemistries, as probed by XPS, suggest that LiC6 are extremely reactive with trace amounts of moisture or oxygen. The open circuit potential and SEM data show that the reactivity of the lithiated battery-grade graphite and the carbon fiber can be related to the density of edge/defect sites on the surfaces. Preliminary results of spontaneous SEI formation on Li-graphite in electrolyte are also given.

  3. Effect of surface modification on carbon fiber and its reinforced phenolic matrix composite

    NASA Astrophysics Data System (ADS)

    Yuan, Hua; Wang, Chengguo; Zhang, Shan; Lin, Xue

    2012-10-01

    In this work, polyacrylonitrile (PAN)-based carbon fiber were chemically modified with H2SO4, KClO3 and silane coupling agent (γ-aminopropyltriethoxysilane, APS), and carbon fiber reinforced phenolic matrix composites were prepared. The structural and surface characteristics of the carbon fiber were investigated by scanning electron microscopy (SEM), X-ray photoelectron spectroscopy (XPS), laser Raman scattering (LRS) and Fourier transform infrared spectroscopy (FTIR). Single fiber mechanical properties, specific surface area, composite impact properties and interfacial shear strength (ILSS) were researched to indicate the effects of surface modification on fibers and the interaction between modified fiber surface and phenolic matrix. The results showed that carbon fiber surface modification by oxidation and APS can strengthen fiber surface chemical activity and enlarge the fiber surface area as well as its roughness. When carbon fiber (CF) is oxidized treatment, the oxygen content as well as the O/C ratio will be obviously increased. Oxygen functional groups increase with oxidation time increasing. Carbon fiber treated with APS will make Csbnd Osbnd R content increase and Osbnd Cdbnd O content decrease due to surface reaction. Proper treatment of carbon fiber with acid and silane coupling agent prove an effective way to increase the interfacial adhesion and improve the mechanical and outdoor performance of the resulting fiber/resin composites.

  4. Production of graphene oxide from pitch-based carbon fiber

    NASA Astrophysics Data System (ADS)

    Lee, Miyeon; Lee, Jihoon; Park, Sung Young; Min, Byunggak; Kim, Bongsoo; in, Insik

    2015-07-01

    Pitch-based graphene oxide (p-GO) whose compositional/structural features are comparable to those of graphene oxide (GO) was firstly produced by chemical exfoliation of pitch-based carbon fiber rather than natural graphite. Incorporation of p-GO as nanofillers into poly(methyl methacrylate) (PMMA) as a matrix polymer resulted in excellent mechanical reinforcement. p-GO/PMMA nanocomposite (1 wt.-% p-GO) demonstrated 800% higher modulus of toughness of neat PMMA.

  5. Carbon-Fiber/Epoxy Tube Lined With Aluminum Foil

    NASA Technical Reports Server (NTRS)

    Gernet, Nelson J.; Kerr, Gregory K.

    1995-01-01

    Carbon-fiber/epoxy composite tube lined with welded aluminum foil useful as part of lightweight heat pipe in which working fluid ammonia. Aluminum liner provides impermeability for vacuum seal, to contain ammonia in heat pipe, and to prevent flow of noncondensable gases into heat pipe. Similar composite-material tubes lined with foils also incorporated into radiators, single- and two-phase thermal buses, tanks for storage of cryogenic materials, and other plumbing required to be lightweight.

  6. Production of graphene oxide from pitch-based carbon fiber

    PubMed Central

    Lee, Miyeon; Lee, Jihoon; Park, Sung Young; Min, Byunggak; Kim, Bongsoo; In, Insik

    2015-01-01

    Pitch-based graphene oxide (p-GO) whose compositional/structural features are comparable to those of graphene oxide (GO) was firstly produced by chemical exfoliation of pitch-based carbon fiber rather than natural graphite. Incorporation of p-GO as nanofillers into poly(methyl methacrylate) (PMMA) as a matrix polymer resulted in excellent mechanical reinforcement. p-GO/PMMA nanocomposite (1 wt.-% p-GO) demonstrated 800% higher modulus of toughness of neat PMMA. PMID:26156067

  7. Carbon fiber composite molecular sieve electrically regenerable air filter media

    DOEpatents

    Wilson, Kirk A.; Burchell, Timothy D.; Judkins, Roddie R.

    1998-01-01

    An electrically regenerable gas filter system includes a carbon fiber composite molecular sieve (CFCMS) filter medium. After a separate medium-efficiency pre-filter removes particulate from the supply airstream, the CFCMS filter sorbs gaseous air pollutants before the air is recirculated to the space. When saturated, the CFCMS media is regenerated utilizing a low-voltage current that is caused to pass through the filter medium.

  8. Carbon fiber composite molecular sieve electrically regenerable air filter media

    DOEpatents

    Wilson, K.A.; Burchell, T.D.; Judkins, R.R.

    1998-10-27

    An electrically regenerable gas filter system includes a carbon fiber composite molecular sieve (CFCMS) filter medium. After a separate medium-efficiency pre-filter removes particulate from the supply air stream, the CFCMS filter sorbs gaseous air pollutants before the air is recirculated to the space. When saturated, the CFCMS media is regenerated utilizing a low-voltage current that is caused to pass through the filter medium. 3 figs.

  9. Pitch-based short carbon fiber. Final report

    SciTech Connect

    Lin, S.S.

    1991-12-01

    Short carbon fiber manufactured from coal tar pitch by Osaka Gas Co. is examined by chemical composition analysis, X-ray powder diffraction, optical microscope, and electron spectroscopic techniques. The present analytical results are compared with the data obtainable from other sources. Owing to the low cost of the short fiber, it is recommended that the fiber could be used for a wide variety of reinforcement applications such as, cement/concrete mixtures, polymer composites, and high temperature materials. Processing includes the mechanical separation of mesophase microbeads of three to 30 micron diameters from crude coal tar during three heat treatment stages. The mesophases obtained are then subjected to solvent extraction, hydrogenation, and polymerization to yield isotropic and anisotropic pitches suitable for melt spinning. The short fiber is fabricated from isotropic pitch by the rotary gas jet method, and the process yields a higher quality fiber as compared to other melt spinning methods. The most important feature is that this process is highly cost effective.

  10. Determination of carbon-14-labeled 3,4-benzopyrene adsorbed on different solids

    SciTech Connect

    Janssen, F.; Kanij, J.

    1983-09-01

    Recovery studies for 3,4-benzopyrene (BaP) are necessary for quantifying polynuclear aromatic hydrocarbons on solid matrices. One of the main problems in recovery studies is the simulation of samples, on which a known quantity of BaP is adsorbed and homogeneously divided on solid substrates. In this study the samples were spiked by the addition of a toluene solution containing /sup 14/C-BaP, taking into account that BaP was not homogeneously divided on the adsorbent. The samples were treated by two destruction methods, i.e., a wet destruction with a potassium dichromate-sulfuric acid and orthophosphoric acid and a combustion with oxygen. The liberated CO/sub 2/ was adsorbed and the /sup 14/C radioactivity analyzed by means of liquid scintillation counting. 6 references, 1 figure, 5 tables.

  11. Carbon nanotube fibers are compatible with Mammalian cells and neurons.

    PubMed

    Dubin, R A; Callegari, G; Kohn, J; Neimark, A

    2008-03-01

    We demonstrate the biocompatibility of carbon nanotube fibers (CNFs) fabricated from single-wall carbon nanotubes. Produced by a particle-coagulation spinning process, CNFs are "hair-like" conductive microwires, which uniquely combine properties of porous nanostructured scaffolds, high-area electrodes, and permeable microfluidic conduits. We report that CNFs are nontoxic and support the attachment, spreading, and growth of mammalian cells and the extension of processes from neurons in vitro. Our findings suggest that CNF may be employed for an electrical interfacing of nerve cells and external devices. PMID:18334451

  12. Development of multifunctional carbon fiber reinforced composites (CFRCs) - Manufacturing process

    NASA Astrophysics Data System (ADS)

    Guadagno, Liberata; Raimondo, Marialuigia; Vietri, Umberto; Barra, Giuseppina; Vertuccio, Luigi; Volponi, Ruggero; Cosentino, Giovanni; De Nicola, Felice; Grilli, Andrea; Spena, Paola

    2014-05-01

    This work describes a successful attempt toward the development of CFRCs based on nanofilled epoxy resins. The epoxy matrix was prepared by mixing a tetrafunctional epoxy precursor with a reactive diluent which allows to reduce the viscosity of the initial epoxy precursor and facilitate the nanofiller dispersion step. As nanofiller, multiwall carbon nanotubes (MWCNTs) were embedded in the epoxy matrix with the aim of improving the electrical properties of the resin used to manufacture CFRCs. Panels were manufactured by Resin Film Infusion (RFI) using a non-usual technique to infuse a nano-filled resin into a carbon fiber dry preform.

  13. Microstructure and properties of SiC-coated carbon fibers prepared by radio frequency magnetron sputtering

    NASA Astrophysics Data System (ADS)

    Cheng, Yong; Huang, Xiaozhong; Du, Zuojuan; Xiao, Jianrong; Zhou, Shan; Wei, Yongshan

    2016-04-01

    SiC-coated carbon fibers are prepared at room temperature with different radio-frequency magnetron sputtering powers. Results show that the coated carbon fibers have uniform, continuous, and flawless surfaces. The mean strengths of the coated carbon fibers with different sputtering powers are not influenced by other factors. Filament strength of SiC-coated carbon fibers increases by approximately 2% compared with that of uncoated carbon fibers at a sputtering power of <200 W. The filament strengths of the coated fibers increase by 9.3% and 12% at sputtering powers of 250 and 300 W, respectively. However, the mean strength of the SiC-coated carbon fibers decreased by 8% at a sputtering power of 400 W.

  14. Ultrasonic Fatigue Endurance of Thin Carbon Fiber Sheets

    NASA Astrophysics Data System (ADS)

    Domínguez Almaraz, Gonzalo M.; Ruiz Vilchez, Julio A.; Dominguez, Aymeric; Meyer, Yann

    2016-04-01

    Ultrasonic fatigue tests were carried out on thin carbon fiber sheets (0.3 mm of thickness) to determine the fatigue endurance under very high-frequency loading (20 kHz). This material, called the gas diffusion layer (GDL), plays a major role in the overall performances of proton exchange membrane fuel cells (PEMFCs). The study of its physical-chemical properties is an on-going subject in the literature; nevertheless, no knowledge is available concerning the high-frequency fatigue endurance. A principal difficulty in carrying out ultrasonic fatigue tests on this material was to determine the dimensions of testing specimen to fit the resonance condition. This aspect was solved by modal numerical simulation: The testing specimen has been a combination of a low-strength steel frame (to facilitate the attachment to the ultrasonic machine and to increase the mass of the specimen), and the carbon fiber hourglass-shape profile. Under resonance condition, a stationary elastic wave is generated along the specimen that induces high stress at the neck section and high displacements at the ends. Results show that fatigue life was close to 3 × 108 cycles when the high Von Misses stress at the neck section was 170 MPa, whereas fatigue life attains the 4.5 × 109 cycles when stress decreases to 117 MPa. Crack initiation and propagation were analyzed, and conclusions were drawn concerning the fatigue endurance of these fiber carbon sheets under ultrasonic fatigue testing.

  15. MNASA as a Test for Carbon Fiber Thermal Barrier Development

    NASA Technical Reports Server (NTRS)

    Bauer, Paul; McCool, Alex (Technical Monitor)

    2001-01-01

    A carbon fiber rope thermal barrier is being evaluated as a replacement for the conventional room temperature vulcanizing (RTV) thermal barrier that is currently used to protect o-rings in Reusable Solid Rocket Motor (RSRM) nozzle joints. Performance requirements include its ability to cool any incoming, hot propellant gases that fill and pressurize the nozzle joints, filter slag and particulates, and to perform adequately in various joint assembly conditions as well as dynamic flight motion. Modified National Aeronautics and Space Administration (MNASA) motors, with their inherent and unique ability to replicate select RSRM internal environment features, were an integral step in the development path leading to full scale RSRM static test demonstration of the carbon fiber rope (CFR) joint concept. These 1/4 scale RSRM motors serve to bridge the gap between the other classes of subscale test motors (extremely small and moderate duration, or small scale and short duration) and the critical asset RSRM static test motors. A series of MNASA tests have been used to demonstrate carbon fiber rope performance and have provided rationale for implementation into a full-scale static motor and flight qualification.

  16. Radiation-curable carbon fiber prepreg composites

    SciTech Connect

    Saunders, C.B.; Dickson, L.W.; Singh, A.; Carmichael, A.A.; Lopata, V.J.

    1988-12-01

    A radiation-curable prepreg designed to meet the specifications set by a major aircraft company is described. The resin, consisting of a mixture of an epoxy diacrylate, polybutadiene diacrylate, and a multifunctional monomer, was used to impregnate a plain weave carbon fabric by a solvent process. The cured polymer, produced by irradiation in air to a dose of 40 kGy, is amorphous, with a gel fraction of 85 percent. The linear thermal expansion coefficient of the polymer was found to be 0.00017 m/m deg C from 25 to 150 C; it was not affected by varying the applied irradiation dose from 30 to 50 kGy. 14 references.

  17. Correlations of Henry's Law Gas-Solid Virial Coefficients and Chromatographic Retention Times for Hydrocarbons and Halocarbons Adsorbed on Carbopack C Carbon.

    PubMed

    Rybolt; Logan; Milburn; Thomas; Waters

    1999-12-01

    Second gas-solid virial coefficients were determined at 403.5 +/- 0.5 K for 6 adsorbates, including butane, chloroform, trichlorofluoromethane (Freon 11), bromochloromethane, 1-chloro-2-methylpropane, and dibromodifluoromethane. For another 11 adsorbates, including dichlorodifluoromethane (Freon 12), chlorodifluoromethane (Freon 22), methyl chloride, methylene chloride, propane, n-pentane, n-hexane, carbon tetrachloride, 1,2-dichloropropane, butyl chloride, and cyclohexane, B(2s) was measured over a range of temperatures between 308 and 494 K. These values were found using gas-solid chromatography with Carbopack C (Supelco Inc.), a graphitized carbon black powder, as the adsorbent. We find that both the ln B(2s) values and the gas-solid interaction energies are effectively correlated with adsorbate-calculated molar refractivity, r(2) = 0.947 and r(2) = 0.964, respectively. Dipole moment alone provides a nearly random correlation of ln B(2s) and, if used with molar refractivity, gives r(2) = 0.970 for the 17 hydrocarbon and alkyl halide (halocarbon) adsorbates. A theoretical equation was developed that predicts a quantitative structure retention relationship (QSRR) used to correlate ln B(2s) values with molar refractivity. B(2s) values are directly proportional to the retention times of the adsorbates. Using one-surface and two-surface models, a calculation of the surface area of the Carbopack C for each of the 17 adsorbates provided a check on the consistency of the analysis as the adsorbate was varied. Copyright 1999 Academic Press.

  18. Tensile Properties and Fracture Behavior of Different Carbon Nanotube-Grafted Polyacrylonitrile-Based Carbon Fibers

    NASA Astrophysics Data System (ADS)

    Naito, Kimiyoshi

    2014-11-01

    The tensile properties and fracture behavior of different carbon nanotube (CNT)-grafted polyacrylonitrile-based (T1000GB) single carbon fibers were investigated. Grafting of CNTs was achieved via chemical vapor deposition (CVD). When Fe(C5H5)2 (also applied via CVD) was used as the catalyst, the tensile strength and Weibull modulus of the carbon fibers were improved, possibly due to the growth of dense CNT networks on the carbon fibers, which may have led to a reduction in the number of strength-limiting defects. Separately, at lower concentrations of an Fe(NO3)3·9H2O catalyst in ethanol, which was applied via dipping, the tensile strength of CNT-grafted fibers was nearly identical to that of the as-received fibers, although the Weibull modulus was higher. For higher concentrations of the Fe(NO3)3·9H2O catalyst, however, the tensile strength and the Weibull modulus were lower than those for the as-received material. Although the density of the CNT network increased with the concentration of the Fe(NO3)3·9H2O catalyst in the ethanol solution, heating of the ethanolic Fe(NO3)3·9H2O catalyst solution generated nitric acid (HNO3) due to decomposition, which damaged the fiber surfaces, resulting in an increase in the number of flaws and consequently a reduction in the tensile strength. Therefore, the tensile strength and Weibull modulus of CNT-grafted carbon fibers vary due to the combination of these effects and as a function of the catalyst concentration.

  19. Studies of the Surface Treatment and Sizing of Carbon Fiber Surfaces on the Mechanical Properties of Composites Containing Carbon Fibers

    NASA Technical Reports Server (NTRS)

    Sherwood, Peter M. A.; Lease, Kevin B.; Locke, James E.; Tomblin, John S.; Wang, Youqi

    1996-01-01

    Carbon fiber reinforced composites are materials where carbon fibers are used to reinforce a matrix to produce a light and strong material with important applications in the aerospace industry. There are many aspects of the preparation of these materials that would benefit from a study which combines the research of groups involved in the production, testing and analysis of these materials, and studies of the basic surface chemistry involved. This final reports presents the results of a project that has developed a collaboration between groups in all three of the major research universities in the State of Kansas, and promises to lead to a collaborative program that covers the major aspects of composite development and application. Sherwood has provided initial fiber surface treatment and sizing together with fiber and composite surface analysis; Lease, Tomblin and Wang have worked together toward the goal of preparing pre-preg and fabrication of laminated panels; Locke has developed computational models to evaluate the effect of surface treatment (and chemistry) on mechanical properties; Lease, Tomblin and Wang have worked together to perform all necessary mechanical testing. The research has been focused on materials that would benefit the High Speed Civil Transport (HSCT) program. The group has visited Dr. Howard Maars and his colleagues at NASA Langley, and has focused their studies on the NASA requirements discussed in this meeting. An important development, requested by NASA scientists, has been the acquisition and study of K3B as a matrix material for the composites. The project has led to the successful acquisition and surface analysis of K3B, together with the successful deposition of this material onto surface oxidized carbon fibers. Mechanical testing, modelling and the construction of composite preparation equipment has been achieved during the grant period.

  20. Method of making carbon fiber-carbon matrix reinforced ceramic composites

    NASA Technical Reports Server (NTRS)

    Williams, Brian (Inventor); Benander, Robert (Inventor)

    2007-01-01

    A method of making a carbon fiber-carbon matrix reinforced ceramic composite wherein the result is a carbon fiber-carbon matrix reinforcement is embedded within a ceramic matrix. The ceramic matrix does not penetrate into the carbon fiber-carbon matrix reinforcement to any significant degree. The carbide matrix is a formed in situ solid carbide of at least one metal having a melting point above about 1850 degrees centigrade. At least when the composite is intended to operate between approximately 1500 and 2000 degrees centigrade for extended periods of time the solid carbide with the embedded reinforcement is formed first by reaction infiltration. Molten silicon is then diffused into the carbide. The molten silicon diffuses preferentially into the carbide matrix but not to any significant degree into the carbon-carbon reinforcement. Where the composite is intended to operate between approximately 2000 and 2700 degrees centigrade for extended periods of time such diffusion of molten silicon into the carbide is optional and generally preferred, but not essential.

  1. Direct observation of solid-phase adsorbate concentration profile in powdered activated carbon particle to elucidate mechanism of high adsorption capacity on super-powdered activated carbon.

    PubMed

    Ando, Naoya; Matsui, Yoshihiko; Matsushita, Taku; Ohno, Koichi

    2011-01-01

    Decreasing the particle size of powdered activated carbon (PAC) by pulverization increases its adsorption capacities for natural organic matter (NOM) and polystyrene sulfonate (PSS, which is used as a model adsorbate). A shell adsorption mechanism in which NOM and PSS molecules do not completely penetrate the adsorbent particle and instead preferentially adsorb near the outer surface of the particle has been proposed as an explanation for this adsorption capacity increase. In this report, we present direct evidence to support the shell adsorption mechanism. PAC particles containing adsorbed PSS were sectioned with a focused ion beam, and the solid-phase PSS concentration profiles of the particle cross-sections were directly observed by means of field emission-scanning electron microscopy/energy-dispersive X-ray spectrometry (FE-SEM/EDXS). X-ray emission from sulfur, an index of PSS concentration, was higher in the shell region than in the inner region of the particles. The X-ray emission profile observed by EDXS did not agree completely with the solid-phase PSS concentration profile predicted by shell adsorption model analysis of the PSS isotherm data, but the observed and predicted profiles were not inconsistent when the analytical errors were considered. These EDXS results provide the first direct evidence that PSS is adsorbed mainly in the vicinity of the external surface of the PAC particles, and thus the results support the proposition that the increase in NOM and PSS adsorption capacity with decreasing particle size is due to the increase in external surface area on which the molecules can be adsorbed. PMID:20851447

  2. Effects of precursor thermal aging and fiber arrangement on the properties of carbon/carbon (C/C) composites

    SciTech Connect

    Ma, C.C.M.; Chang, W.C.; Tai, N.H.

    1993-12-31

    Carbon/carbon composites fabricated by the pyrolysis of high strength carbon fiber fabrics reinforced phenolic resin were investigated. A liquid impregnation process has been used to fabricate composite precursor for 2-D carbon/carbon composite and an unique pultrusion process also used to fabricate the 1-D carbon/carbon composite precursor. Effects of thermal aging of the precursor on flexural strength of the resulted carbon/carbon composites are studied. Results shows that suitable thermal aging improves the flexural properties of carbon/carbon composites in this study. And based on the SEM examination and flexural tests, they show that the 2-D plain woven fiber arrangement results the significant degradation of the carbon fiber and the decreasing of composites flexural properties.

  3. Artificial muscles of dielectric elastomers attached to artificial tendons of functionalized carbon fibers

    NASA Astrophysics Data System (ADS)

    Ye, Zhihang; Faisal, Md. Shahnewaz Sabit; Asmatulu, Ramazan; Chen, Zheng

    2014-03-01

    Dielectric elastomers are soft actuation materials with promising applications in robotics and biomedical de- vices. In this paper, a bio-inspired artificial muscle actuator with artificial tendons is developed for robotic arm applications. The actuator uses dielectric elastomer as artificial muscle and functionalized carbon fibers as artificial tendons. A VHB 4910 tape is used as the dielectric elastomer and PDMS is used as the bonding material to mechanically connect the carbon fibers to the elastomer. Carbon fibers are highly popular for their high electrical conductivities, mechanical strengths, and bio-compatibilities. After the acid treatments for the functionalization of carbon fibers (500 nm - 10 μm), one end of carbon fibers is spread into the PDMS material, which provides enough bonding strength with other dielectric elastomers, while the other end is connected to a DC power supply. To characterize the actuation capability of the dielectric elastomer and electrical conductivity of carbon fibers, a diaphragm actuator is fabricated, where the carbon fibers are connected to the actuator. To test the mechanical bonding between PDMS and carbon fibers, specimens of PDMS bonded with carbon fibers are fabricated. Experiments have been conducted to verify the actuation capability of the dielectric elastomer and mechanical bonding of PDMS with carbon fibers. The energy efficiency of the dielectric elastomer increases as the load increases, which can reach above 50%. The mechanical bonding is strong enough for robotic arm applications.

  4. Single walled carbon nanotubes with functionally adsorbed biopolymers for use as chemical sensors

    DOEpatents

    Johnson, Jr., Alan T

    2013-12-17

    Chemical field effect sensors comprising nanotube field effect devices having biopolymers such as single stranded DNA or RNA functionally adsorbed to the nanotubes are provided. Also included are arrays comprising the sensors and methods of using the devices to detect volatile compounds.

  5. Model for the Effect of Fiber Bridging on the Fracture Resistance of Reinforced-Carbon-Carbon

    NASA Technical Reports Server (NTRS)

    Chan, Kwai S.; Lee, Yi-Der; Hudak, Stephen J., Jr.

    2009-01-01

    A micromechanical methodology has been developed for analyzing fiber bridging and resistance-curve behavior in reinforced-carbon-carbon (RCC) panels with a three-dimensional (3D) composite architecture and a silicon carbide (SiC) surface coating. The methodology involves treating fiber bridging traction on the crack surfaces in terms of a weight function approach and a bridging law that relates the bridging stress to the crack opening displacement. A procedure has been developed to deduce material constants in the bridging law from the linear portion of the K-resistance curve. This report contains information on the application of procedures and outcomes.

  6. Photoelectrochemical cell using dye sensitized zinc oxide nanowires grown on carbon fibers

    NASA Astrophysics Data System (ADS)

    Unalan, Husnu Emrah; Wei, Di; Suzuki, Kenichi; Dalal, Sharvari; Hiralal, Pritesh; Matsumoto, Hidetoshi; Imaizumi, Shinji; Minagawa, Mie; Tanioka, Akihiko; Flewitt, Andrew J.; Milne, William I.; Amaratunga, Gehan A. J.

    2008-09-01

    Zinc oxide (ZnO) nanowires (NWs) grown on carbon fibers using a vapor transport and condensation approach are used as the cathode of a photoelectrochemical cell. The carbon fibers were obtained by electrospray deposition and take the form of a flexible carbon fabric. The ZnO NW on carbon fiber anode is combined with a "black dye" photoabsorber, an electrolyte, and a platinum (Pt) counterelectrode to complete the cell. The results show that ZnO NW and carbon fibers can be used for photoinduced charge separation/charge transport and current collection, respectively, in a photoelectrochemical cell.

  7. Microwave-assisted activated carbon from cocoa shell as adsorbent for removal of sodium diclofenac and nimesulide from aqueous effluents.

    PubMed

    Saucier, Caroline; Adebayo, Matthew A; Lima, Eder C; Cataluña, Renato; Thue, Pascal S; Prola, Lizie D T; Puchana-Rosero, M J; Machado, Fernando M; Pavan, Flavio A; Dotto, G L

    2015-05-30

    Microwave-induced chemical activation process was used to prepare an activated carbon from cocoa shell for efficient removal of two anti-inflammatories, sodium diclofenac (DFC) and nimesulide (NM), from aqueous solutions. A paste was obtained from a mixture of cocoa shell and inorganic components; with a ratio of inorganic: organic of 1 (CSC-1.0). The mixture was pyrolyzed in a microwave oven in less than 10 min. The CSC-1.0 was acidified with a 6 mol L(-1) HCl under reflux to produce MWCS-1.0. The CSC-1.0 and MWCS-1.0 were characterized using FTIR, SEM, N2 adsorption/desorption curves, X-ray diffraction, and point of zero charge (pHpzc). Experimental variables such as initial pH of the adsorbate solutions and contact time were optimized for adsorptive characteristics of MWCS-1.0. The optimum pH for removal of anti-inflammatories ranged between 7.0 and 8.0. The kinetic of adsorption was investigated using general order, pseudo first-order and pseu do-second order kinetic models. The maximum amounts of DCF and NM adsorbed onto MWCS-1.0 at 25 °C are 63.47 and 74.81 mg g(-1), respectively. The adsorbent was tested on two simulated hospital effluents. MWCS-1.0 is capable of efficient removal of DCF and NM from a medium that contains high sugar and salt concentrations.

  8. Silver and zinc oxide nanostructures loaded on activated carbon as new adsorbents for removal of methylene green: a comparative study.

    PubMed

    Ghaedi, M; Karimi, H; Yousefi, F

    2014-09-01

    In this study, the removal of methylene green (MG) from aqueous solution based on two new adsorbents including silver nanoparticles and zinc oxide nanorods loaded on activated carbon (Ag-NP-AC and ZnO-NR-AC, respectively) has been carried out. The dependency of removal process to variables such as contact time, pH, amount of adsorbents, and initial MG concentration were examined and optimized. It was found that the maximum MG removal percentage was achieved at pH = 7.0 following stirring at 400 r min(-1) for 7 and 6 min for Ag-NP-AC and ZnO-NR-AC, respectively. Equilibrium data were well fitted with the Langmuir model having maximum adsorption capacity of 166.7 and 200 mg g(-1) for Ag-NP-AC and ZnO-NR-AC, respectively. Thermodynamic parameters of MG adsorption on Ag-NP-AC such as enthalpy and entropy changes, activation energy, sticking probability, and Gibbs free energy changes show the spontaneous and endothermic nature of the removal process. Among different conventional kinetic models, the pseudo second-order kinetics in addition to particle diffusion mechanism is the best and efficient model for the prediction and explanation of experimental data of MG adsorption onto both adsorbents.

  9. Resilience of gas-phase anharmonicity in the vibrational response of adsorbed carbon monoxide and breakdown under electrical conditions

    NASA Astrophysics Data System (ADS)

    Dabo, Ismaila

    2012-07-01

    In surface catalysis, the adsorption of carbon monoxide on transition-metal electrodes represents the prototype of strong chemisorption. Notwithstanding significant changes in the molecular orbitals of adsorbed CO, spectroscopic experiments highlight a close correlation between the adsorbate stretching frequency and equilibrium bond length for a wide range of adsorption geometries and substrate compositions. In this work, we study the origins of this correlation, commonly known as Badger's rule, by deconvoluting and examining the contributions from the adsorption environment to the intramolecular potential using first-principles calculations. Noting that intramolecular anharmonicity is preserved upon CO chemisorption, we show that Badger's rule for adsorbed CO can be expressed solely in terms of the tabulated Herzberg spectroscopic constants of isolated CO. Moreover, although it had been previously established using finite-cluster models that Badger's rule is not affected by electrical conditions, we find here that Badger's rule breaks down when the electrified surface is represented as a periodic slab. Examination of this breakdown in terms of anharmonic contributions from the effective surface charge reveals limitations of conventional finite-cluster models in describing electrical conditions at metal electrodes.

  10. Carboxylated carbon nanotubes as an efficient and cost-effective adsorbent for sustainable removal of insecticide fenvalerate from contaminated solutions

    NASA Astrophysics Data System (ADS)

    Naeimi, Atena; Saeidi, Mahboubeh; Baroumand, Naser

    2016-10-01

    In this study, carboxylic multiwall carbon nanotubes (CMNTs) were used as an adsorbent for removing fenvalerate as a toxic insecticide from solution through batch experiments. The influence of four independent parameters of HCl, initial fenvalerate concentration, CMNTs dosage, and contact time on the fenvalerate adsorption process was investigated. Raman spectroscopy and thermogravimetric analysis confirmed that the adsorption and maximum adsorption capacity (40.0 mg g-1) showed high adsorption potential of the proposed sorbent. The kinetic, isothermic, and thermodynamic of fenvalerate adsorptionon CMNTs were evaluated to better understand this environmental friendly adsorption strategy. A pseudo-first-order kinetic described very well the experimental data of the adsorption kinetics. The experimental data found to be properly fitted to Freundlich model, which indicates that the sorption takes place on a heterogeneous material. The thermodynamic results showed the negative value of the standard free energy (Δ G0 ) and standard enthalpy change (Δ H0 ) showing an exothermic and spontaneous system. Repeated availability of adsorbent investigated and SEM and HRTEM of reused adsorbent showed stability and non-aggregatable attributes of CMNTs.

  11. Process Optimization of Bismaleimide (BMI) Resin Infused Carbon Fiber Composite

    NASA Technical Reports Server (NTRS)

    Ehrlich, Joshua W.; Tate, LaNetra C.; Cox, Sarah B.; Taylor, Brian J.; Wright, M. Clara; Faughnan, Patrick D.; Batterson, Lawrence M.; Caraccio, Anne J.; Sampson, Jeffery W.

    2013-01-01

    Engineers today are presented with the opportunity to design and build the next generation of space vehicles out of the lightest, strongest, and most durable materials available. Composites offer excellent structural characteristics and outstanding reliability in many forms that will be utilized in future aerospace applications including the Commercial Crew and Cargo Program and the Orion space capsule. NASA's Composites for Exploration (CoEx) project researches the various methods of manufacturing composite materials of different fiber characteristics while using proven infusion methods of different resin compositions. Development and testing on these different material combinations will provide engineers the opportunity to produce optimal material compounds for multidisciplinary applications. Through the CoEx project, engineers pursue the opportunity to research and develop repair patch procedures for damaged spacecraft. Working in conjunction with Raptor Resins Inc., NASA engineers are utilizing high flow liquid infusion molding practices to manufacture high-temperature composite parts comprised of intermediate modulus 7 (IM7) carbon fiber material. IM7 is a continuous, high-tensile strength composite with outstanding structural qualities such as high shear strength, tensile strength and modulus as well as excellent corrosion, creep, and fatigue resistance. IM7 carbon fiber, combined with existing thermoset and thermoplastic resin systems, can provide improvements in material strength reinforcement and deformation-resistant properties for high-temperature applications. Void analysis of the different layups of the IM7 material discovered the largest total void composition within the [ +45 , 90 , 90 , -45 ] composite panel. Tensile and compressional testing proved the highest mechanical strength was found in the [0 4] layup. This paper further investigates the infusion procedure of a low-cost/high-performance BMI resin into an IM7 carbon fiber material and the

  12. Magnetic alignment of nickel-coated carbon fibers

    SciTech Connect

    Hao, Chuncheng; Li, Xiaojiao; Wang, Guizhen

    2011-11-15

    Graphical abstract: Carbon nanofibers were subjected to a two-step pretreatment, sensitization and activation. Carbon nanofibers were encapsulated by a uniform layer of nickel nanoparticles. The prepared composites are ferromagnetic and with a small value of coercivity. Upon such functionalization, the carbon nanofibers can be aligned in a relatively small external magnetic field. Highlights: {center_dot} A simple microwave-assisted procedure for the magnetic composite. {center_dot} Dense layer of nickel on pretreated carbon nanofibers. {center_dot} Ferromagnetic properties and low coercivity. {center_dot} A long-chain aligned structure under magnetic field. -- Abstract: Magnetic composites of nickel-coated carbon nanofibers have been successfully fabricated by employing a simple microwave-assisted procedure. The scanning electron microscopy images show that a complete and uniform nickel coating with mean size of 25 nm could be deposited on carbon fibers. Magnetization curves demonstrate that the prepared composites are ferromagnetic and that the coercivity is 96 Oe. The magnetic carbon nanofibers can be aligned as a long-chain structure in an external magnetic field.

  13. Multiscale Analysis of Delamination of Carbon Fiber-Epoxy Laminates with Carbon Nanotubes

    NASA Technical Reports Server (NTRS)

    Riddick, Jaret C.; Frankland, SJV; Gates, TS

    2006-01-01

    A multi-scale analysis is presented to parametrically describe the Mode I delamination of a carbon fiber/epoxy laminate. In the midplane of the laminate, carbon nanotubes are included for the purposes of selectively enhancing the fracture toughness of the laminate. To analyze carbon fiber epoxy carbon nanotube laminate, the multi-scale methodology presented here links a series of parameterizations taken at various length scales ranging from the atomistic through the micromechanical to the structural level. At the atomistic scale molecular dynamics simulations are performed in conjunction with an equivalent continuum approach to develop constitutive properties for representative volume elements of the molecular structure of components of the laminate. The molecular-level constitutive results are then used in the Mori-Tanaka micromechanics to develop bulk properties for the epoxy-carbon nanotube matrix system. In order to demonstrate a possible application of this multi-scale methodology, a double cantilever beam specimen is modeled. An existing analysis is employed which uses discrete springs to model the fiber bridging affect during delamination propagation. In the absence of empirical data or a damage mechanics model describing the effect of CNTs on fracture toughness, several tractions laws are postulated, linking CNT volume fraction to fiber bridging in a DCB specimen. Results from this demonstration are presented in terms of DCB specimen load-displacement responses.

  14. UV-vis spectroscopy of iodine adsorbed on alkali-metal-modified zeolite catalysts for addition of carbon dioxide to ethylene oxide

    SciTech Connect

    Doskocil, E.J.; Bordawekar, S.V.; Kaye, B.G.; Davis, R.J.

    1999-07-29

    The basicity of alkali-metal-exchange (Na, K, Cs) zeolites X and Y was probed by UV-vis diffuse reflectance spectroscopy of adsorbed iodine. The observed blue shift in the visible absorption spectrum of adsorbed iodine, compared to gaseous iodine, correlated well with the negative charge on the framework oxygen atoms calculated from the Sanderson electronegativity equalization principle. The blue shifts associated with iodine adsorbed on classical catalytic supports like silica, alumina, and magnesia suggest that the iodine adsorption technique for probing basicity is applicable to a wide variety of solids. Iodine was also adsorbed on X and Y zeolites containing occluded cesium oxide formed by decomposition of impregnated cesium acetate. However, the iodine appeared to irreversibly react on these strongly basic samples, possibly forming an adsorbed triiodide ions. As a complement to the adsorption studies, the activity of alkali-metal-containing zeolites for the base-catalyzed formation of ethylene carbonate from ethylene oxide and carbon dioxide was investigated. Among the ion-exchanged zeolites, the cesium form of zeolite X exhibited the highest activity for ethylene carbonate formation. The catalytic activity of a zeolite containing occluded cesium was even higher than that of a cesium-exchanged zeolite. The presence of water adsorbed in zeolite pores promoted the rate of ethylene carbonate formation for both cesium-exchanged and cesium-impregnated zeolite X.

  15. Thermal conductivity, electrical conductivity and specific heat of copper-carbon fiber composite

    NASA Technical Reports Server (NTRS)

    Kuniya, Keiichi; Arakawa, Hideo; Kanai, Tsuneyuki; Chiba, Akio

    1988-01-01

    A new material of copper/carbon fiber composite is developed which retains the properties of copper, i.e., its excellent electrical and thermal conductivity, and the property of carbon, i.e., a small thermal expansion coefficient. These properties of the composite are adjustable within a certain range by changing the volume and/or the orientation of the carbon fibers. The effects of carbon fiber volume and arrangement changes on the thermal and electrical conductivity, and specific heat of the composite are studied. Results obtained are as follows: the thermal and electrical conductivity of the composite decrease as the volume of the carbon fiber increases, and were influenced by the fiber orientation. The results are predictable from a careful application of the rule of mixtures for composites. The specific heat of the composite was dependent, not on fiber orientation, but on fiber volume. In the thermal fatigue tests, no degradation in the electrical conductivity of this composite was observed.

  16. Adhesion of preceramic inorganic polymer coatings to carbon fibers

    SciTech Connect

    Chaudhry, T.M.; Drzal, L.T.; Ho, H.; Laine, R.

    1996-12-31

    To determine whether the preceramic inorganic polymer coating can provide not only the thermal oxidative protection during both processing and use in metal matrix composites or ceramic matrix composites but also the appropriate composite properties, it is desirable to know how and at what point in the thermal processing cycle the coating-carbon fiber interface undergoes changes that affect the interfacial adhesion and failure mode. Also, it is important to identify the locus of interfacial failure i.e. between fiber and coating or between coating and matrix. This work is directed at determining the interfacial changes and the locus of failure in order to optimize both the coating chemistry and the conversion process. The characteristics of the benchmark interface coating material, silicon oxycarbide, SiO{sub x}C{sub y} or black glass have been studied. SiO{sub x}C{sub y} was chosen because (1) SiO{sub x}C{sub y} is amorphous, (2) it is possible to prepare very well-defined materials, where the chemistry and the evolution of the material with time and temperature are known in detail, and (3) SiO{sub x}C{sub y} is a matrix material used in commercial composites. It has been shown that these coatings are effective in increasing the oxidation resistance of the carbon fibers themselves.

  17. Carbon fiber study. A compilation of an intergovernmental committee study

    NASA Technical Reports Server (NTRS)

    1978-01-01

    Carbon fibers have opened a wealth of new structural engineering and consumer product opportunities. The potential benefits are higher strength, and lighter weight military and commercial products, which portend energy savings and increases safety. Unfortunately, these benefits are not realized without risk. Inadvertent fiber release, during manufacture or by destruction of the resin binder in fire, is the major hazard associated with composites. The carbon (or graphite) fibers are finer than human hair and if released into the air, they can be easily transported by winds or currents. In contact with electrical devices, they can create resistive loading, short circuits, and arcing, resulting in stoppages or destruction. Their health impact is not fully known and requires careful research and analysis before any firm conclusions can be reached; however, based upon current available information, they are primarily an irritant to the eyes and skin, like fiberglass, rather than carcinogenic or destructive to lung tissue. Major manufacturers are aware of the unique problems associated with these materials and have successfully applied controls to avoid the inplant problems.

  18. Bonded carbon or ceramic fiber composite filter vent for radioactive waste

    DOEpatents

    Brassell, Gilbert W.; Brugger, Ronald P.

    1985-02-19

    Carbon bonded carbon fiber composites as well as ceramic or carbon bonded ceramic fiber composites are very useful as filters which can separate particulate matter from gas streams entraining the same. These filters have particular application to the filtering of radioactive particles, e.g., they can act as vents for containers of radioactive waste material.

  19. Nanocomposite fibers and film containing polyolefin and surface-modified carbon nanotubes

    DOEpatents

    Chu,Benjamin; Hsiao, Benjamin S.

    2010-01-26

    Methods for modifying carbon nanotubes with organic compounds are disclosed. The modified carbon nanotubes have enhanced compatibility with polyolefins. Nanocomposites of the organo-modified carbon nanotubes and polyolefins can be used to produce both fibers and films having enhanced mechanical and electrical properties, especially the elongation-to-break ratio and the toughness of the fibers and/or films.

  20. Characterization of Porous Carbon Fibers and Related Materials

    SciTech Connect

    Fuller, E.L., Jr.

    1993-01-01

    A one-year subcontract sponsored by the Carbon Materials Technology Group of the Oak Ridge National Laboratory (ORNL) with the Department of Geological Sciences, University Of Tennessee, has been completed. A volumetric sorption system has been upgraded, in cooperation with commercial vendor, to allow the acquisition of data relevant to the program for the production of activated carbon molecular fiber sieves (ACFMS). The equipment and experimental techniques have been developed to determine the pore structure and porosity of reference materials and materials produced at ORNL as part of the development of methods for the activation of carbon fibers by various etching agents. Commercial activated coconut shell charcoal (ACSC) has been studied to verify instrument performance and to develop methodology for deducing cause and effects in the activation processes and to better understand the industrial processes (gas separation, natural gas storage, etc.). Operating personnel have been trained, standard operating procedures have been established, and quality assurance procedures have been developed and put in place. Carbon dioxide and methane sorption have been measured over a temperature range 0 to 200 C for both ACFMS and ACSC and similarities and differences related to the respective structures and mechanisms of interaction with the sorbed components. Nitrogen sorption (at 77 K) has been used to evaluate ''surface area'' and ''porosity'' for comparison with the large data base that exists for other activated carbons and related materials. The preliminary data base reveals that techniques and theories currently used to evaluate activated carbons may be somewhat erroneous and misleading. Alternate thermochemical and structural analyses have been developed that show promise in providing useful information related both to the activation process and to industrial applications of interest in the efficient and economical utilization of fossil fuels in a manner that is

  1. A small-scale test for fiber release from carbon composites. [pyrolysis and impact

    NASA Technical Reports Server (NTRS)

    Gilwee, W. J., Jr.; Fish, R. H.

    1980-01-01

    A test method was developed to determine relative fiber loss from pyrolyzed composites with different resins and fiber construction. Eleven composites consisting of woven and unwoven carbon fiber reinforcement and different resins were subjected to the burn and impact test device. The composites made with undirectional tape had higher fiber loss than those with woven fabric. Also, the fiber loss was inversely proportional to the char yield of the resin.

  2. A series of tufted carbon fiber cathodes designed for different high power microwave sources

    NASA Astrophysics Data System (ADS)

    Liu, Lie; Li, Limin; Zhang, Jun; Zhang, Xiaoping; Wen, Jianchun; Liu, Yonggui

    2008-06-01

    We report the fabrication technique of tufted carbon fiber cathodes for different microwave sources. Three carbon fiber cathodes were constructed, including a planar cathode, an annular cathode, and a cylindrical cathode for radial emission. Experimental investigations on these cathodes were performed in a reflex triode virtual cathode oscillator (vircator), a backward wave oscillator (BWO), and a magnetically insulated transmission line oscillator (MILO), respectively. The pulse duration of microwave emission from the reflex triode vircator was lengthened by using the planar carbon fiber cathode. In the BWO with the annular carbon fiber cathode, the uniform electron beam with a kA /cm2 current density was observed. In addition, carbon fiber has great promise as field emitter for MILOs. These results show that the carbon fiber cathodes can be utilized for electron emission in high power diodes with different structures.

  3. A series of tufted carbon fiber cathodes designed for different high power microwave sources.

    PubMed

    Liu, Lie; Li, Limin; Zhang, Jun; Zhang, Xiaoping; Wen, Jianchun; Liu, Yonggui

    2008-06-01

    We report the fabrication technique of tufted carbon fiber cathodes for different microwave sources. Three carbon fiber cathodes were constructed, including a planar cathode, an annular cathode, and a cylindrical cathode for radial emission. Experimental investigations on these cathodes were performed in a reflex triode virtual cathode oscillator (vircator), a backward wave oscillator (BWO), and a magnetically insulated transmission line oscillator (MILO), respectively. The pulse duration of microwave emission from the reflex triode vircator was lengthened by using the planar carbon fiber cathode. In the BWO with the annular carbon fiber cathode, the uniform electron beam with a kA/cm(2) current density was observed. In addition, carbon fiber has great promise as field emitter for MILOs. These results show that the carbon fiber cathodes can be utilized for electron emission in high power diodes with different structures.

  4. Multi-scale Rule-of-Mixtures Model of Carbon Nanotube/Carbon Fiber/Epoxy Lamina

    NASA Technical Reports Server (NTRS)

    Frankland, Sarah-Jane V.; Roddick, Jaret C.; Gates, Thomas S.

    2005-01-01

    A unidirectional carbon fiber/epoxy lamina in which the carbon fibers are coated with single-walled carbon nanotubes is modeled with a multi-scale method, the atomistically informed rule-of-mixtures. This multi-scale model is designed to include the effect of the carbon nanotubes on the constitutive properties of the lamina. It included concepts from the molecular dynamics/equivalent continuum methods, micromechanics, and the strength of materials. Within the model both the nanotube volume fraction and nanotube distribution were varied. It was found that for a lamina with 60% carbon fiber volume fraction, the Young's modulus in the fiber direction varied with changes in the nanotube distribution, from 138.8 to 140 GPa with nanotube volume fractions ranging from 0.0001 to 0.0125. The presence of nanotube near the surface of the carbon fiber is therefore expected to have a small, but positive, effect on the constitutive properties of the lamina.

  5. Laser cutting of carbon fiber reinforced thermo-plastics (CFRTP) by single-mode fiber laser irradiation

    NASA Astrophysics Data System (ADS)

    Niino, Hiroyuki; Kawaguchi, Yoshizo; Sato, Tadatake; Narazaki, Aiko; Kurosaki, Ryozo; Muramatsu, Mayu; Harada, Yoshihisa; Anzai, Kenji; Aoyama, Mitsuaki; Matsushita, Masafumi; Furukawa, Koichi; Nishino, Michiteru; Fujisaki, Akira; Miyato, Taizo; Kayahara, Takashi

    2014-03-01

    We report on the laser cutting of carbon fiber reinforced thermo-plastics (CFRTP) with a cw IR fiber laser (single-mode fiber laser, average power: 350 W). CFRTP is a high strength composite material with a lightweight, and is increasingly being used various applications. A well-defined cutting of CFRTP which were free of debris and thermal-damages around the grooves, were performed by the laser irradiation with a fast beam galvanometer scanning on a multiple-scanpass method.

  6. Water/carbonate stripping for CO.sub.2 capture adsorber regeneration and CO.sub.2 delivery to photoautotrophs

    SciTech Connect

    Chance, Ronald; Koros, William J.; McCool, Benjamin; Noel, James

    2015-08-11

    The invention provides systems and methods for the delivery of carbon to photoautotrophs. The invention utilizes low energy regeneration of adsorbent for CO.sub.2 capture and provides for effective CO.sub.2 loading into liquids useful for photoautotroph growth and/or production of photosynthetic products, such as biofuels, via photoautotrophic culture media. The inventive system comprises a fluid/membrane/fluid contactor that provides selective transfer of molecular CO.sub.2 via a dense (non-porous) membrane from a carbonate-based CO.sub.2 snipping solution to a culture medium where the CO.sub.2 is consumed by a photoautotroph for the production of biofuels, biofuel precursors or other commercial products.

  7. Quantification of the effects of organic and carbonate buffers on arsenate and phosphate adsorption on a goethite-based granular porous adsorbent.

    PubMed

    Kanematsu, Masakazu; Young, Thomas M; Fukushi, Keisuke; Sverjensky, Dimitri A; Green, Peter G; Darby, Jeannie L

    2011-01-15

    Interest in the development of oxide-based materials for arsenate removal has led to a variety of experimental methods and conditions for determining arsenate adsorption isotherms, which hinders comparative evaluation of their adsorptive capacities. Here, we systematically investigate the effects of buffer (HEPES or carbonate), adsorbent dose, and solution pH on arsenate and phosphate adsorption isotherms for a previously well characterized goethite-based adsorbent (Bayoxide E33 (E33)). All adsorption isotherms obtained at different adsorbate/adsorbent concentrations were identical when 1 mM of HEPES (96 mg C/L) was used as a buffer. At low aqueous arsenate and phosphate concentration (∼1.3 μM), however, adsorption isotherms obtained using 10 mM of NaHCO(3) buffer, which is a reasonable carbonate concentration in groundwater, are significantly different from those obtained without buffer or with HEPES. The carbonate competitive effects were analyzed using the extended triple layer model (ETLM) with the adsorption equilibrium constant of carbonate calibrated using independent published carbonate adsorption data for pure goethite taking into consideration the different surface properties. The successful ETLM calculations of arsenate adsorption isotherms for E33 under various conditions allowed quantitative comparison of the arsenate adsorption capacity between E33 and other major adsorbents initially tested under varied experimental conditions in the literature.

  8. Oxidation Behavior of Carbon Fiber-Reinforced Composites

    NASA Technical Reports Server (NTRS)

    Sullivan, Roy M.

    2008-01-01

    OXIMAP is a numerical (FEA-based) solution tool capable of calculating the carbon fiber and fiber coating oxidation patterns within any arbitrarily shaped carbon silicon carbide composite structure as a function of time, temperature, and the environmental oxygen partial pressure. The mathematical formulation is derived from the mechanics of the flow of ideal gases through a chemically reacting, porous solid. The result of the formulation is a set of two coupled, non-linear differential equations written in terms of the oxidant and oxide partial pressures. The differential equations are solved simultaneously to obtain the partial vapor pressures of the oxidant and oxides as a function of the spatial location and time. The local rate of carbon oxidation is determined at each time step using the map of the local oxidant partial vapor pressure along with the Arrhenius rate equation. The non-linear differential equations are cast into matrix equations by applying the Bubnov-Galerkin weighted residual finite element method, allowing for the solution of the differential equations numerically.

  9. Advanced fire-resistant forms of activated carbon and methods of adsorbing and separating gases using same

    DOEpatents

    Xiong, Yongliang; Wang, Yifeng

    2015-02-03

    Advanced, fire-resistant activated carbon compositions useful in adsorbing gases; and having vastly improved fire resistance are provided, and methods for synthesizing the compositions are also provided. The advanced compositions have high gas adsorption capacities and rapid adsorption kinetics (comparable to commercially-available activated carbon), without having any intrinsic fire hazard. They also have superior performance to Mordenites in both adsorption capacities and kinetics. In addition, the advanced compositions do not pose the fibrous inhalation hazard that exists with use of Mordenites. The fire-resistant compositions combine activated carbon mixed with one or more hydrated and/or carbonate-containing minerals that release H.sub.2O and/or CO.sub.2 when heated. This effect raises the spontaneous ignition temperature to over 500.degree. C. in most examples, and over 800.degree. C. in some examples. Also provided are methods for removing and/or separating target gases, such as Krypton or Argon, from a gas stream by using such advanced activated carbons.

  10. A model to predict the adsorber thermal behavior during treatment of volatile organic compounds onto wet activated carbon.

    PubMed

    Pré, P; Delage, F; Le Cloirec, P

    2002-11-01

    A model for adsorption of volatile organic compounds (VOCs) onto a wet activated carbon bed was proposed in this study. This model accounts for temperature changes induced by the reversed and coupled mass-transfer processes of both organic species adsorption and water desorption. Indeed, it was experimentally pointed out that temperature rises, which result from the exothermal nature of the energetic interactions between the organic molecule and the activated carbon surface, are notably reduced when the adsorbent contains an initial moisture of approximately 10% in weight. Moreover, it was shown that water rate desorption was enhanced in the presence of organic vapor. This phenomenon may be explained by the displacement of sorbed water bythe organic molecules, owing to more intensive interactions with the activated carbon surface. The model proposed was elaborated from a previous comprehensive analysis of the diffusion mechanisms governing VOC adsorption at high concentrations onto a dry activated carbon bed. In a similar way, a theoretical approach was developed to model water desorption during drying of a wet activated carbon bed under pure flowing air. At last, a theoretical depiction of both competitive and reverse processes was outlined. The final model fits reasonably with experimental data relative to both breakthrough curves and thermal wave shape along the bed, even if local temperature change calculation may require some further improvement.

  11. 2, 4 dichlorophenol (2, 4-DCP) sorption from aqueous solution using granular activated carbon and polymeric adsorbents and studies on effect of temperature on activated carbon adsorption.

    PubMed

    Ghatbandhe, A S; Yenkie, M K N

    2008-04-01

    Adsorption equilibrium, kinetics and thermodynamics of 2,4-dichlorophenol (2,4-DCP), one of the most commonly used chlorophenol, onto bituminous coal based Filtrasorb-400 grade granular activated carbon, were studied in aqueous solution in a batch system with respect to temperature. Uptake capacity of activated carbon found to increase with temperature. Langmuir isotherm models were applied to experimental equilibrium data of 2, 4-DCP adsorption and competitive studies with respect to XAD resin were carried out. Equilibrium data fitted very well to the Langmuir equilibrium model. Adsorbent monolayer capacity 'Q0, Langmuir constant 'b' and adsorption rate constant 'k(a)' were evaluated at different temperatures for activated carbon adsorption. This data was then used to calculate the energy of activation of adsorption and also the thermodynamic parameters, namely the free energy of adsorption, deltaG0, enthalpy of adsorption, deltaH0 and the entropy of adsorption deltaS0. The obtained results showed that the monolayer capacity increases with the increase in temperatures. The obtained values of thermodynamic parameters showed that adsorption of 2,4 DCP is an endothermic process. Synthetic resin was not found efficient to adsorb 2,4 DCP compared to activated carbon. The order of adsorption efficiencies of three resins used in the study found as XAD7HP > XAD4 > XAD1180.

  12. 40 CFR 63.990 - Absorbers, condensers, and carbon adsorbers used as control devices.

    Code of Federal Regulations, 2014 CFR

    2014-07-01

    ... and § 63.996. (1) Where an absorber is used, a scrubbing liquid temperature monitoring device and a...) temperature monitoring device capable of providing a continuous record shall be used. (3) Where a carbon... regeneration cycle; and a carbon bed temperature monitoring device, capable of recording the carbon...

  13. 40 CFR 63.990 - Absorbers, condensers, and carbon adsorbers used as control devices.

    Code of Federal Regulations, 2011 CFR

    2011-07-01

    ... regeneration cycle; and a carbon bed temperature monitoring device, capable of recording the carbon bed... 40 Protection of Environment 10 2011-07-01 2011-07-01 false Absorbers, condensers, and carbon..., Recovery Devices and Routing to a Fuel Gas System or a Process § 63.990 Absorbers, condensers, and...

  14. 40 CFR 63.990 - Absorbers, condensers, and carbon adsorbers used as control devices.

    Code of Federal Regulations, 2013 CFR

    2013-07-01

    ... regeneration cycle; and a carbon bed temperature monitoring device, capable of recording the carbon bed... 40 Protection of Environment 11 2013-07-01 2013-07-01 false Absorbers, condensers, and carbon..., Recovery Devices and Routing to a Fuel Gas System or a Process § 63.990 Absorbers, condensers, and...

  15. 40 CFR 63.990 - Absorbers, condensers, and carbon adsorbers used as control devices.

    Code of Federal Regulations, 2010 CFR

    2010-07-01

    ... regeneration cycle; and a carbon bed temperature monitoring device, capable of recording the carbon bed... 40 Protection of Environment 10 2010-07-01 2010-07-01 false Absorbers, condensers, and carbon..., Recovery Devices and Routing to a Fuel Gas System or a Process § 63.990 Absorbers, condensers, and...

  16. 40 CFR 63.990 - Absorbers, condensers, and carbon adsorbers used as control devices.

    Code of Federal Regulations, 2012 CFR

    2012-07-01

    ... regeneration cycle; and a carbon bed temperature monitoring device, capable of recording the carbon bed... 40 Protection of Environment 11 2012-07-01 2012-07-01 false Absorbers, condensers, and carbon..., Recovery Devices and Routing to a Fuel Gas System or a Process § 63.990 Absorbers, condensers, and...

  17. Lightning Strike Induced Damage Mechanisms of Carbon Fiber Composites

    NASA Astrophysics Data System (ADS)

    Kawakami, Hirohide

    Composite materials have a wide application in aerospace, automotive, and other transportation industries, because of the superior structural and weight performances. Since carbon fiber reinforced polymer composites possess a much lower electrical conductivity as compared to traditional metallic materials utilized for aircraft structures, serious concern about damage resistance/tolerance against lightning has been rising. Main task of this study is to clarify the lightning damage mechanism of carbon fiber reinforced epoxy polymer composites to help further development of lightning strike protection. The research on lightning damage to carbon fiber reinforced polymer composites is quite challenging, and there has been little study available until now. In order to tackle this issue, building block approach was employed. The research was started with the development of supporting technologies such as a current impulse generator to simulate a lightning strike in a laboratory. Then, fundamental electrical properties and fracture behavior of CFRPs exposed to high and low level current impulse were investigated using simple coupon specimens, followed by extensive parametric investigations in terms of different prepreg materials frequently used in aerospace industry, various stacking sequences, different lightning intensity, and lightning current waveforms. It revealed that the thermal resistance capability of polymer matrix was one of the most influential parameters on lightning damage resistance of CFRPs. Based on the experimental findings, the semi-empirical analysis model for predicting the extent of lightning damage was established. The model was fitted through experimental data to determine empirical parameters and, then, showed a good capability to provide reliable predictions for other test conditions and materials. Finally, structural element level lightning tests were performed to explore more practical situations. Specifically, filled-hole CFRP plates and patch

  18. RADIATION EFFECTS ON EPOXY/CARBON FIBER COMPOSITE

    SciTech Connect

    Hoffman, E; Eric Skidmore, E

    2008-12-12

    The Department of Energy Savannah River Site vitrifies nuclear waste incident to defense programs through its Defense Waste Processing Facility (DWPF). The piping in the DWPF seal pot jumper configuration must withstand the stresses during an unlikely but potential deflagration event, and maintain its safety function for a 20-year service life. Carbon fiber-reinforced epoxy composites (CFR) were proposed for protection and reinforcement of piping during such an event. The proposed CFR materials have been ASME-approved (Section XI, Code Case N-589-1) for post-construction maintenance and is DOT-compliant per 49CFR 192 and 195. The proposed carbon fiber/epoxy composite reinforcement system was originally developed for pipeline rehabilitation and post-construction maintenance in petrochemical, refineries, DOT applications and other industries. The effects of ionizing radiation on polymers and organic materials have been studied for many years. The majority of available data are based on traditional exposures to gamma irradiation at high dose rates ({approx}10,000 Gy/hr) allowing high total dose within reasonable test periods and general comparison of different materials exposed at such conditions. However, studies in recent years have shown that degradation of many polymers are sensitive to dose rate, with more severe degradation often observed at similar or even lower total doses when exposed to lower dose rates. This behavior has been primarily attributed to diffusion-limited oxidation which is minimized during very high dose rate exposures. Most test standards for accelerated aging and nuclear qualification of components acknowledge these limitations. The results of testing to determine the radiation resistance and microstructural effects of gamma irradiation exposure on a bisphenol-A based epoxy matrix composite reinforced with carbon fibers are presented. This work provides a foundation for a more extensive evaluation of dose rate effects on advanced epoxy

  19. Influence of metal-containing carbon fibers on the properties of carbon-filled plastics based on aromatic polyamide

    NASA Astrophysics Data System (ADS)

    Burya, A. I.; Safonova, A. M.; Rula, I. V.

    2012-07-01

    The influence of metal-containing carbon fibers on the thermal properties of carbon-filled phenylone-based plastics has been investigated. It has been shown that carbometallic fibers containing in their composition 20- 30 mass % of a finely dispersed metal (Co, Cu) are promising fillers of phenylone C-2 for making carbonfilled plastics working in frictional units of various machines and mechanisms.

  20. Strengthened PAN-based carbon fibers obtained by slow heating rate carbonization

    PubMed Central

    Kim, Min-A; Jang, Dawon; Tejima, Syogo; Cruz-Silva, Rodolfo; Joh, Han-Ik; Kim, Hwan Chul; Lee, Sungho; Endo, Morinobu

    2016-01-01

    Large efforts have been made over the last 40 years to increase the mechanical strength of polyacrylonitrile (PAN)-based carbon fibers (CFs) using a variety of chemical or physical protocols. In this paper, we report a new method to increase CFs mechanical strength using a slow heating rate during the carbonization process. This new approach increases both the carbon sp3 bonding and the number of nitrogen atoms with quaternary bonding in the hexagonal carbon network. Theoretical calculations support a crosslinking model promoted by the interstitial carbon atoms located in the graphitic interlayer spaces. The improvement in mechanical performance by a controlled crosslinking between the carbon hexagonal layers of the PAN based CFs is a new concept that can contribute further in the tailoring of CFs performance based on the understanding of their microstructure down to the atomic scale. PMID:27004752

  1. Laser ultrasound technology for fault detection on carbon fiber composites

    NASA Astrophysics Data System (ADS)

    Seyrkammer, Robert; Reitinger, Bernhard; Grün, Hubert; Sekelja, Jakov; Burgholzer, Peter

    2014-05-01

    The marching in of carbon fiber reinforced polymers (CFRPs) to mass production in the aeronautic and automotive industry requires reliable quality assurance methods. Laser ultrasound (LUS) is a promising nondestructive testing technique for sample inspection. The benefits compared to conventional ultrasound (US) testing are couplant free measurements and an easy access to complex shapes due to remote optical excitation and detection. Here the potential of LUS is present on composite test panels with relevant testing scenarios for industry. The results are evaluated in comparison to conventional ultrasound used in the aeronautic industry.

  2. Defect depth measurement of carbon fiber reinforced polymers by thermography

    NASA Astrophysics Data System (ADS)

    Chen, Terry Y.; Chen, Jian-Lun

    2016-01-01

    Carbon fiber reinforced polymers has been widely used in all kind of the industries. However the internal defects can result in the change of material or mechanical properties, and cause safety problem. In this study, step-heating thermography is employed to measure the time series temperature distribution of composite plate. The principle of heat conduction in a flat plate with defect inside is introduced. A temperature separation criterion to determine the depth of defect inside the specimen is obtained experimentally. Applying this criterion to CFRP specimens with embedded defects, the depth of embedded defect in CFRP can be determined quite well from the time series thermograms obtained experimentally.

  3. Damage-tolerant composite materials produced by stitching carbon fibers

    NASA Technical Reports Server (NTRS)

    Dow, Marvin B.; Smith, Donald L.

    1989-01-01

    NASA-Langley has undertaken the investigation of composite damage-tolerance enhancement and fabrication economies-maximization via reinforcement-stitching, in combination with resin transfer molding. Attention is given to results obtained by an experimental evaluation of composites tailored for damage tolerance by stitching layers of dry carbon-fiber fabric with closely-spaced threads, in order to furnish through-the-thickness reinforcement. Various stitching patterns and thread materials have been evaluated, using flat-plate specimens; blade-stiffened structural elements have been fabricated and tested. The results presented indicate that stitched laminates furnish damage tolerance performance comparable to that of more expensive, toughened-matrix composites.

  4. A carbonyl iron/carbon fiber material for electromagnetic wave absorption.

    PubMed

    Youh, Meng-Jey; Wu, Hung-Chih; Lin, Wang-Hua; Chiu, Sheng-Cheng; Huang, Chien-Fa; Yu, Hsin-Chih; Hsu, Jen-Sung; Li, Yuan-Yao

    2011-03-01

    A carbonyl iron/carbon fiber material consisting of carbon fibers grown on micrometer-sized carbonyl iron sphere, was synthesized by chemical vapor deposition using a mixture of C2H2 and H2. The hollow-core carbon fibers (outer diameter: 140 nm and inner diameter: 40 nm) were composed of well-ordered graphene layers which were almost parallel to the long axis of the fibers. A composite (2 mm thick) consisting of the carbonyl iron/carbon fibers and epoxy resin demonstrated excellent electromagnetic (EM) wave absorption. Minimum reflection losses of -36 dB (99.95% of EM wave absorption) at 7.6 GHz and -32 dB (99.92% of EM wave absorption) at 34.1 GHz were achieved. The well-dispersed and network-like carbon fibers in the resin matrix affected the dielectric loss of the EM wave while the carbonyl iron affected the magnetic loss.

  5. Hybrid carbon fiber/carbon nanotube composites for structural damping applications.

    PubMed

    Tehrani, M; Safdari, M; Boroujeni, A Y; Razavi, Z; Case, S W; Dahmen, K; Garmestani, H; Al-Haik, M S

    2013-04-19

    Carbon nanotubes (CNTs) were grown on the surface of carbon fibers utilizing a relatively low temperature synthesis technique; graphitic structures by design (GSD). To probe the effects of the synthesis protocols on the mechanical properties, other samples with surface grown CNTs were prepared using catalytic chemical vapor deposition (CCVD). The woven graphite fabrics were thermally shielded with a thin film of SiO2 and CNTs were grown on top of this film. Raman spectroscopy and electron microscopy revealed the grown species to be multi-walled carbon nanotubes (MWCNTs). The damping performance of the hybrid CNT-carbon fiber-reinforced epoxy composite was examined using dynamic mechanical analysis (DMA). Mechanical testing confirmed that the degradations in the strength and stiffness as a result of the GSD process are far less than those encountered through using the CCVD technique and yet are negligible compared to the reference samples. The DMA results indicated that, despite the minimal degradation in the storage modulus, the loss tangent (damping) for the hybrid composites utilizing GSD-grown MWCNTs improved by 56% compared to the reference samples (based on raw carbon fibers with no surface treatment or surface grown carbon nanotubes) over the frequency range 1-60 Hz. These results indicated that the energy dissipation in the GSD-grown MWCNTs composite can be primarily attributed to the frictional sliding at the nanotube/epoxy interface and to a lesser extent to the stiff thermal shielding SiO2 film on the fiber/matrix interface. PMID:23518871

  6. Carbon Nanotubes Growth by CVD on Graphite Fibers

    NASA Technical Reports Server (NTRS)

    Zhu, Shen; Su, Ching-Hua; Cochrane, J. C.; Lehoczky, S. L.; Muntele, I.; Ila, D.; Curreri, Peter A. (Technical Monitor)

    2002-01-01

    Due to the superior electrical and mechanical properties of carbon nanotubes (CNT), synthesizing CNT on various substances for electronics devices and reinforced composites have been engaged in many efforts for applications. This presentation will illustrate CNT synthesized on graphite fibers by thermal CVD. On the fiber surface, iron nanoparticles as catalysts for CNT growth are coated. The growth temperature ranges from 600 to 1000 C and the pressure ranges from 100 Torr to one atmosphere. Methane and hydrogen gases with methane content of 10% to 100% are used for the CNT synthesis. At high growth temperatures (greater than or equal to 900 C), the rapid inter-diffusion of the transition metal iron on the graphite surface results in the rough fiber surface without any CNT grown on it. When the growth temperature is relative low (650-800 C), CNT with catalytic particles on the nanotube top ends are fabricated on the graphite surface. (Methane and hydrogen gases with methane content of 10% to 100% are used for the CNT synthesis.) (By measuring the samples) Using micro Raman spectroscopy in the breath mode region, single-walled or multi-walled CNT (MWCNT), depending on growth concentrations, are found. Morphology, length and diameter of these MWCNT are determined by scanning electron microscopy and Raman spectroscopy. The detailed results of syntheses and characterizations will be discussed in the presentation.

  7. Oxidation Behavior of Carbon Fiber Reinforced Silicon Carbide Composites

    NASA Technical Reports Server (NTRS)

    Valentin, Victor M.

    1995-01-01

    Carbon fiber reinforced Silicon Carbide (C-SiC) composites offer high strength at high temperatures and good oxidation resistance. However, these composites present some matrix microcracks which allow the path of oxygen to the fiber. The aim of this research was to study the effectiveness of a new Silicon Carbide (SiC) coating developed by DUPONT-LANXIDE to enhance the oxidation resistance of C-SiC composites. A thermogravimetric analysis was used to determine the oxidation rate of the samples at different temperatures and pressures. The Dupont coat proved to be a good protection for the SiC matrix at temperatures lower than 1240 C at low and high pressures. On the other hand, at temperatures above 1340 C the Dupont coat did not seem to give good protection to the composite fiber and matrix. Even though some results of the tests have been discussed, because of time restraints, only a small portion of the desired tests could be completed. Therefore, no major conclusions or results about the effectiveness of the coat are available at this time.

  8. Fast voltammetry of metals at carbon-fiber microelectrodes: copper adsorption onto activated carbon aids rapid electrochemical analysis.

    PubMed

    Pathirathna, Pavithra; Samaranayake, Srimal; Atcherley, Christopher W; Parent, Kate L; Heien, Michael L; McElmurry, Shawn P; Hashemi, Parastoo

    2014-09-21

    Rapid, in situ trace metal analysis is essential for understanding many biological and environmental processes. For example, trace metals are thought to act as chemical messengers in the brain. In the environment, some of the most damaging pollution occurs when metals are rapidly mobilized and transported during hydrologic events (storms). Electrochemistry is attractive for in situ analysis, primarily because electrodes are compact, cheap and portable. Electrochemical techniques, however, do not traditionally report trace metals in real-time. In this work, we investigated the fundamental mechanisms of a novel method, based on fast-scan cyclic voltammetry (FSCV), that reports trace metals with sub-second temporal resolution at carbon-fiber microelectrodes (CFMs). Electrochemical methods and geochemical models were employed to find that activated CFMs rapidly adsorb copper, a phenomenon that greatly advances the temporal capabilities of electrochemistry. We established the thermodynamics of surface copper adsorption and the electrochemical nature of copper deposition onto CFMs and hence identified a unique adsorption-controlled electrochemical mechanism for ultra-fast trace metal analysis. This knowledge can be exploited in the future to increase the sensitivity and selectivity of CFMs for fast voltammetry of trace metals in a variety of biological and environmental models.

  9. Magnetic nanoporous carbon as an adsorbent for the extraction of phthalate esters in environmental water and aloe juice samples.

    PubMed

    Liu, Li; Hao, Yunhui; Ren, Yiqian; Wang, Chun; Wu, Qiuhua; Wang, Zhi

    2015-05-01

    In this work, magnetic nanoporous carbon with high surface area and ordered structure was synthesized using cheap commercial silica gel as template and sucrose as the carbon source. The prepared magnetic nanoporous carbon was firstly used as an adsorbent for the extraction of phthalate esters, including diethyl phthalate, diallyl phthalate, and di-n-propyl-phthalate, from lake water and aloe juice samples. Several parameters that could affect the extraction efficiency were optimized. Under the optimum conditions, the limit of detection of the method (S/N = 3) was 0.10 ng/mL for water sample and 0.20 ng/mL for aloe juice sample. The linearity was observed over the concentration range of 0.50-150.0 and 1.0-200.0 ng/mL for water and aloe juice samples, respectively. The results showed that the magnetic nanoporous carbon has a high adsorptive capability toward the target phthalate esters in water and aloe juice samples.

  10. Comparison of granular activated carbon and macroreticular synthetic adsorbents for groundwater remediation

    SciTech Connect

    Musterman, J.L.; Boero, V.J.; Plantz, D.A.

    1995-12-31

    An evaluation of Calgon F-400 and Ambersorb 563 and 572 and XAD-4 resins for removal of VOCs from an activated sludge treated groundwater was performed using continuous flow reactors. Breakthrough and EBCT-ST curves were developed and the capacities of the adsorbents were determined. Comparison of the performance of the adsorbents indicated that: (1) Ambersorb 563 resin provided greater VOC adsorption capacity and run-time to breakthrough than Ambersorb 572 and XAD-4 resins or the F-400 GAC. (2) Ambersorb 563 resin could also be operated at three times the surface loading rate of the GAC system resulting in smaller equipment size. (3) The Ambersorb 563 resin showed negligible TOC removal despite a high specificity for the target organic analytes. A cost analysis indicated that the installed cost for a 6.31 L/s Ambersorb 563 resin system was 2.8 times the cost of a F-400 GAC system. The annual operating cost however, was four times lower and the total present worth was $549,000 less.

  11. Evaluation of cation-exchanged zeolite adsorbents for post-combustion carbon dioxide capture

    SciTech Connect

    Bae, TH; Hudson, MR; Mason, JA; Queen, WL; Dutton, JJ; Sumida, K; Micklash, KJ; Kaye, SS; Brown, CM; Long, JR

    2013-01-01

    A series of zeolite adsorbents has been evaluated for potential application in post-combustion CO2 capture using a new high-throughput gas adsorption instrument capable of measuring 28 samples in parallel. Among the zeolites tested, Ca-A exhibits the highest CO2 uptake (3.72 mmol g(-1) and 5.63 mmol cm(-3)) together with an excellent CO2 selectivity over N-2 under conditions relevant to capture from the dry flue gas stream of a coal-fired power plant. The large initial isosteric heat of adsorption of -58 kJ mol(-1) indicates the presence of strong interactions between CO2 and the Ca-A framework. Neutron and X-ray powder diffraction studies reveal the precise location of the adsorption sites for CO2 in Ca-A and Mg-A. A detailed study of CO2 adsorption kinetics further shows that the performance of Ca-A is not limited by slow CO2 diffusion within the pores. Significantly, Ca-A exhibited a higher volumetric CO2 uptake and CO2/N-2 selectivity than Mg-2(dobdc) (dobdc(4-) = 1,4-dioxido-2,5-benzenedicarboxylate; Mg-MOF-74, CPO-27-Mg), one of the best performing adsorbents. The exceptional performance of Ca-A was maintained in CO2 breakthrough simulations.

  12. Adsorption separation of carbon dioxide from flue gas by a molecularly imprinted adsorbent.

    PubMed

    Zhao, Yi; Shen, Yanmei; Ma, Guoyi; Hao, Rongjie

    2014-01-01

    CO2 separation by molecularly imprinted adsorbent from coal-fired flue gas after desulfurization system has been studied. The adsorbent was synthesized by molecular imprinted technique, using ethanedioic acid, acrylamide, and ethylene glycol dimethacrylate as the template, functional monomer, and cross-linker, respectively. According to the conditions of coal-fired flue gas, the influencing factors, including adsorption temperature, desorption temperature, gas flow rate, and concentrations of CO2, H2O, O2, SO2, and NO, were studied by fixed bed breakthrough experiments. The experimental conditions were optimized to gain the best adsorption performance and reduce unnecessary energy consumption in future practical use. The optimized adsorption temperature, desorption temperature, concentrations of CO2, and gas flow rate are 60 °C, 80 °C, 13%, and 170 mL/min, respectively, which correspond to conditions of practical flue gases to the most extent. The CO2 adsorption performance was nearly unaffected by H2O, O2, and NO in the flue gas, and was promoted by SO2 within the emission limit stipulated in the Chinese emission standards of air pollutants for a thermal power plant. The maximum CO2 adsorption capacity, 0.57 mmol/g, was obtained under the optimized experimental conditions, and the SO2 concentration was 150 mg/m(3). The influence mechanisms of H2O, O2, SO2, and NO on CO2 adsorption capacity were investigated by infrared spectroscopic analysis. PMID:24410306

  13. Adsorption dynamics of trichlorofluoromethane in activated carbon fiber beds.

    PubMed

    Zhang, Xiaoping; Zhao, Xin; Hu, Jiaqi; Wei, Chaohai; Bi, Hsiaotao T

    2011-02-28

    Adsorption on carbon fixed-beds is considered as an inexpensive and highly effective way for controlling chlorofluorocarbons (CFCs) emissions. In the present work, a dynamic model under constant-pattern wave conditions has been developed to predict the breakthrough behavior of trichlorofluoromethane (CFC-11) adsorption in a fixed bed packed with activated carbon fibers (ACFs). The adsorption of CFC-11 vapor onto viscose-based ACFs was performed in a fixed bed at different test conditions. The results showed that, in a deep bed (>120 mm), the analytical model based on the external mass transfer with the Langmuir isotherm could describe the adsorption dynamics well. The model parameters, the characteristic breakthrough time and the film mass-transfer coefficients are related to such operating parameters as the superficial gas velocity, feed concentration and bed height. It was found from the breakthrough dynamics that the mass transfer from the fluid phase to the fiber surface dominated the CFC-11 adsorption onto ACFs in fixed beds.

  14. Creep rupture testing of carbon fiber-reinforced epoxy composites

    NASA Astrophysics Data System (ADS)

    Burton, Kathryn Anne

    Carbon fiber is becoming more prevalent in everyday life. As such, it is necessary to have a thorough understanding of, not solely general mechanical properties, but of long-term material behavior. Creep rupture testing of carbon fiber is very difficult due to high strength and low strain to rupture properties. Past efforts have included testing upon strands, single tows and overwrapped pressure vessels. In this study, 1 inch wide, [0°/90°]s laminated composite specimens were constructed from fabric supplied by T.D. Williamson Inc. Specimen fabrication methods and gripping techniques were investigated and a method was developed to collect long term creep rupture behavior data. An Instron 1321 servo-hydraulic material testing machine was used to execute static strength and short term creep rupture tests. A hanging dead-weight apparatus was designed to perform long-term creep rupture testing. The testing apparatus, specimens, and specimen grips functioned well. Collected data exhibited a power law distribution and therefore, a linear trend upon a log strength-log time plot. Statistical analysis indicated the material exhibited slow degradation behavior, similar to previous studies, and could maintain a 50 year carrying capacity at 62% of static strength, approximately 45.7 ksi.

  15. Adsorption dynamics of trichlorofluoromethane in activated carbon fiber beds.

    PubMed

    Zhang, Xiaoping; Zhao, Xin; Hu, Jiaqi; Wei, Chaohai; Bi, Hsiaotao T

    2011-02-28

    Adsorption on carbon fixed-beds is considered as an inexpensive and highly effective way for controlling chlorofluorocarbons (CFCs) emissions. In the present work, a dynamic model under constant-pattern wave conditions has been developed to predict the breakthrough behavior of trichlorofluoromethane (CFC-11) adsorption in a fixed bed packed with activated carbon fibers (ACFs). The adsorption of CFC-11 vapor onto viscose-based ACFs was performed in a fixed bed at different test conditions. The results showed that, in a deep bed (>120 mm), the analytical model based on the external mass transfer with the Langmuir isotherm could describe the adsorption dynamics well. The model parameters, the characteristic breakthrough time and the film mass-transfer coefficients are related to such operating parameters as the superficial gas velocity, feed concentration and bed height. It was found from the breakthrough dynamics that the mass transfer from the fluid phase to the fiber surface dominated the CFC-11 adsorption onto ACFs in fixed beds. PMID:21216098

  16. Oxidation of carbon fiber surfaces for use as reinforcement in high-temperature cementitious material systems

    DOEpatents

    Sugama, Toshifumi.

    1990-05-22

    The interfacial bond characteristics between carbon fiber and a cement matrix, in high temperature fiber-reinforced cementitious composite systems, can be improved by the oxidative treatment of the fiber surfaces. Compositions and the process for producing the compositions are disclosed. 2 figs.

  17. Oxidation of carbon fiber surfaces for use as reinforcement in high-temperature cementitious material systems

    DOEpatents

    Sugama, Toshifumi

    1990-01-01

    The interfacial bond characteristics between carbon fiber and a cement matrix, in high temperature fiber-reinforced cementitious composite systems, can be improved by the oxidative treatment of the fiber surfaces. Compositions and the process for producing the compositions are disclosed.

  18. The transfer of carbon fibers through a commercial aircraft water separator and air cleaner

    NASA Technical Reports Server (NTRS)

    Meyers, J. A.

    1979-01-01

    The fraction of carbon fibers passing through a water separator and an air filter was determined in order to estimate the proportion of fibers outside a closed aircraft that are transmitted to the electronics through the air conditioning system. When both devices were used together and only fibers 3 mm or larger were considered, a transfer function of .001 was obtained.

  19. Adsorbed natural gas storage with activated carbons made from Illinois coals and scrap tires

    USGS Publications Warehouse

    Sun, Jielun; Brady, T.A.; Rood, M.J.; Lehmann, C.M.; Rostam-Abadi, M.; Lizzio, A.A.

    1997-01-01

    Activated carbons for natural gas storage were produced from Illinois bituminous coals (IBC-102 and IBC-106) and scrap tires by physical activation with steam or CO2 and by chemical activation with KOH, H3PO4, or ZnCl2. The products were characterized for N2-BET area, micropore volume, bulk density, pore size distribution, and volumetric methane storage capacity (Vm/Vs). Vm/Vs values for Illinois coal-derived carbons ranged from 54 to 83 cm3/cm3, which are 35-55% of a target value of 150 cm3/cm3. Both granular and pelletized carbons made with preoxidized Illinois coal gave higher micropore volumes and larger Vm/Vs values than those made without preoxidation. This confirmed that preoxidation is a desirable step in the production of carbons from caking materials. Pelletization of preoxidized IBC-106 coal, followed by steam activation, resulted in the highest Vm/Vs value. With roughly the same micropore volume, pelletization alone increased Vm/Vs of coal carbon by 10%. Tire-derived carbons had Vm/Vs values ranging from 44 to 53 cm3/cm3, lower than those of coal carbons due to their lower bulk densities. Pelletization of the tire carbons increased bulk density up to 160%. However, this increase was offset by a decrease in micropore volume of the pelletized materials, presumably due to the pellet binder. As a result, Vm/Vs values were about the same for granular and pelletized tire carbons. Compared with coal carbons, tire carbons had a higher percentage of mesopores and macropores.

  20. Processes for preparing carbon fibers using sulfur trioxide in a halogenated solvent

    SciTech Connect

    Patton, Jasson T.; Barton, Bryan E.; Bernius, Mark T.; Chen, Xiaoyun; Hukkanen, Eric J.; Rhoton, Christina A.; Lysenko, Zenon

    2015-12-29

    Disclosed here are processes for preparing carbonized polymers (preferably carbon fibers), comprising sulfonating a polymer with a sulfonating agent that comprises SO.sub.3 dissolved in a solvent to form a sulfonated polymer; treating the sulfonated polymer with a heated solvent, wherein the temperature of the solvent is at least 95.degree. C.; and carbonizing the resulting product by heating it to a temperature of 500-3000.degree. C. Carbon fibers made according to these methods are also disclosed herein.

  1. Bond strength of individual carbon nanotubes grown directly on carbon fibers

    NASA Astrophysics Data System (ADS)

    Kim, Kyoung Ju; Lee, Geunsung; Kim, Sung-Dae; Kim, Seong-Il; Youk, Ji Ho; Lee, Jinyong; Kim, Young-Woon; Yu, Woong-Ryeol

    2016-10-01

    The performance of carbon nanotube (CNT)-based devices strongly depends on the adhesion of CNTs to the substrate on which they were directly grown. We report on the bond strength of CNTs grown on a carbon fiber (T700SC Toray), measured via in situ pulling of individual CNTs inside a transmission electron microscope. The bond strength of an individual CNT, obtained from the measured pulling force and CNT cross-section, was very high (˜200 MPa), 8-10 times higher than that of an adhesion model assuming only van der Waals interactions (25 MPa), presumably due to carbon-carbon interactions between the CNT (its bottom atoms) and the carbon substrate.

  2. Bond strength of individual carbon nanotubes grown directly on carbon fibers.

    PubMed

    Kim, Kyoung Ju; Lee, Geunsung; Kim, Sung-Dae; Kim, Seong-Il; Youk, Ji Ho; Lee, Jinyong; Kim, Young-Woon; Yu, Woong-Ryeol

    2016-10-01

    The performance of carbon nanotube (CNT)-based devices strongly depends on the adhesion of CNTs to the substrate on which they were directly grown. We report on the bond strength of CNTs grown on a carbon fiber (T700SC Toray), measured via in situ pulling of individual CNTs inside a transmission electron microscope. The bond strength of an individual CNT, obtained from the measured pulling force and CNT cross-section, was very high (∼200 MPa), 8-10 times higher than that of an adhesion model assuming only van der Waals interactions (25 MPa), presumably due to carbon-carbon interactions between the CNT (its bottom atoms) and the carbon substrate.

  3. Bond strength of individual carbon nanotubes grown directly on carbon fibers.

    PubMed

    Kim, Kyoung Ju; Lee, Geunsung; Kim, Sung-Dae; Kim, Seong-Il; Youk, Ji Ho; Lee, Jinyong; Kim, Young-Woon; Yu, Woong-Ryeol

    2016-10-01

    The performance of carbon nanotube (CNT)-based devices strongly depends on the adhesion of CNTs to the substrate on which they were directly grown. We report on the bond strength of CNTs grown on a carbon fiber (T700SC Toray), measured via in situ pulling of individual CNTs inside a transmission electron microscope. The bond strength of an individual CNT, obtained from the measured pulling force and CNT cross-section, was very high (∼200 MPa), 8-10 times higher than that of an adhesion model assuming only van der Waals interactions (25 MPa), presumably due to carbon-carbon interactions between the CNT (its bottom atoms) and the carbon substrate. PMID:27581367

  4. Delamination behavior of carbon fiber/epoxy composite laminates with short fiber reinforcement

    SciTech Connect

    Sohn, M.S.; Hu, X.Z. . Dept. of Mechanical and Materials Engineering)

    1994-06-01

    Delamination in laminated materials is one major mode of damage and failure encountered in application. Fracture mechanics is often used to characterize the interlaminar fracture behavior. The interlaminar fracture energies, G[sub I], G[sub II] and G[sub I/II] are the major concerns to characterize the interlaminar toughness of the composite laminates. Typical mode-I fracture is caused by normal tension, and typical mode-II fracture by shear in the direction of crack extension. The objective of the present study is to compare and discuss the mode-I and mode-II interlaminar fracture energies, G[sub I] and G[sub II] of carbon fiber/epoxy composite laminates with and without the reinforcement of short Kevlar fibers (5--7 mm in length) and to identify the microfracture features of the Kevlar fibers under those two delamination modes through SEM observations. Double cantilever beam (DCB) specimens and end notched flexure (ENF) specimens are used for the mode-I and -II delamination experiments.

  5. Kinetics and isotherm analysis of Tropaeoline 000 adsorption onto unsaturated polyester resin (UPR): a non-carbon adsorbent.

    PubMed

    Jain, Rajeev; Sharma, Pooja; Sikarwar, Shalini

    2013-03-01

    The presence of dyes in water is undesirable due to the toxicological impact of their entrance into the food chain. Owing to the recalcitrant nature of dyes to biological oxidation, a tertiary treatment like adsorption is required. In the present study, unsaturated polyester resin (UPR) has been used as a sorbent in the treatment of dye-contaminated water. Different concentrations of Tropaeoline 000 containing water were treated with UPR. The preliminary investigations were carried out by batch adsorption to examine the effects of pH, adsorbate concentration, adsorbent dosage, contact time, and temperature. A plausible mechanism for the ongoing adsorption process and thermodynamic parameters have also been obtained from Langmuir and Freundlich adsorption isotherm models. Thermodynamic parameter showed that the sorption process of Tropaeoline 000 onto activated carbon (AC) and UPR were feasible, spontaneous, and endothermic under studied conditions. The estimated values for (ΔG) are -10.48 × 10(3) and -6.098 × 10(3) kJ mol(-1) over AC and UPR at 303 K (30 °C), indicating towards a spontaneous process. The adsorption process followed pseudo-first-order model. The mass transfer property of the sorption process was studied using Lagergren pseudo-first-order kinetic models. The values of % removal and k (ad) for dye systems were calculated at different temperatures (303-323 K). The mechanism of the adsorption process was determined from the intraparticle diffusion model. PMID:22689095

  6. Polypyrrole/cobalt ferrite/multiwalled carbon nanotubes as an adsorbent for removing uranium ions from aqueous solutions.

    PubMed

    Liu, Qi; Zhu, Jiahui; Tan, Lichao; Jing, Xiaoyan; Liu, Jingyuan; Song, Dalei; Zhang, Hongsen; Li, Rumin; Emelchenko, G A; Wang, Jun

    2016-05-31

    A novel rod-like, dual-shell structural adsorbent of polypyrrole/cobalt ferrite/multiwalled carbon nanotubes (PPy/CoFe2O4/MWCNTs) was successfully synthesized by a hydrothermal method, which could easily separate uranium(vi) ions with an external magnetic field. The structure and morphology of PPy/CoFe2O4/MWCNTs were characterized by VSM, XRD, XPS TEM and FT-IR. The results proved that the dual-shell structure was obtained in which a shell of cobalt ferrite and polypyrrole formed around the MWCNTs core. In batch adsorption experiments, including pH, equilibrium time and temperature on uranium adsorption, were investigated. The main results show that the PPy/CoFe2O4/MWCNTs composite has a higher affinity towards the uptake of uranium(vi) from aqueous solutions. The highest adsorption capacity reached was 148.8 mg U per g at pH 7. A kinetic analysis showed that the adsorption process was best described by a pseudo-second-order kinetic model. The uranium sorption equilibrium data correlated well with the Langmuir sorption isotherm model in the thermodynamic analysis. 0.5 mol per L NaHCO3 was used as the desorbent and good adsorption properties were shown after the desorption procedures were repeated three times. Thus, PPy/CoFe2O4/MWCNTs was an excellent adsorbent for removing uranium(vi) ions. PMID:27169495

  7. Polypyrrole/cobalt ferrite/multiwalled carbon nanotubes as an adsorbent for removing uranium ions from aqueous solutions.

    PubMed

    Liu, Qi; Zhu, Jiahui; Tan, Lichao; Jing, Xiaoyan; Liu, Jingyuan; Song, Dalei; Zhang, Hongsen; Li, Rumin; Emelchenko, G A; Wang, Jun

    2016-05-31

    A novel rod-like, dual-shell structural adsorbent of polypyrrole/cobalt ferrite/multiwalled carbon nanotubes (PPy/CoFe2O4/MWCNTs) was successfully synthesized by a hydrothermal method, which could easily separate uranium(vi) ions with an external magnetic field. The structure and morphology of PPy/CoFe2O4/MWCNTs were characterized by VSM, XRD, XPS TEM and FT-IR. The results proved that the dual-shell structure was obtained in which a shell of cobalt ferrite and polypyrrole formed around the MWCNTs core. In batch adsorption experiments, including pH, equilibrium time and temperature on uranium adsorption, were investigated. The main results show that the PPy/CoFe2O4/MWCNTs composite has a higher affinity towards the uptake of uranium(vi) from aqueous solutions. The highest adsorption capacity reached was 148.8 mg U per g at pH 7. A kinetic analysis showed that the adsorption process was best described by a pseudo-second-order kinetic model. The uranium sorption equilibrium data correlated well with the Langmuir sorption isotherm model in the thermodynamic analysis. 0.5 mol per L NaHCO3 was used as the desorbent and good adsorption properties were shown after the desorption procedures were repeated three times. Thus, PPy/CoFe2O4/MWCNTs was an excellent adsorbent for removing uranium(vi) ions.

  8. Core-shell Fe3O4 polydopamine nanoparticles serve multipurpose as drug carrier, catalyst support and carbon adsorbent.

    PubMed

    Liu, Rui; Guo, Yunlong; Odusote, Gloria; Qu, Fengli; Priestley, Rodney D

    2013-09-25

    We present the synthesis and multifunctional utilization of core-shell Fe3O4 polydopamine nanoparticles (Fe3O4@PDA NPs) to serve as the enabling platform for a range of applications including responsive drug delivery, recyclable catalyst support, and adsorbent. Magnetite Fe3O4 NPs formed in a one-pot process by the hydrothermal approach were coated with a polydopamine shell layer of ~20 nm in thickness. The as prepared Fe3O4@PDA NPs were used for the controlled drug release in a pH-sensitive manner via reversible bonding between catechol and boronic acid groups of PDA and the anticancer drug bortezomib (BTZ), respectively. The facile deposition of Au NPs atop Fe3O4@PDA NPs was achieved by utilizing PDA as both the reducing agent and the coupling agent. The nanocatalysts exhibited high catalytic performance for the reduction of o-nitrophenol. Furthermore, the recovery and reuse of the catalyst was demonstrated 10 times without any detectible loss in activity. Finally, the PDA layers were converted into carbon to obtain Fe3O4@C and used as an adsorbent for the removal of Rhodamine B from an aqueous solution. The synergistic combination of unique features of PDA and magnetic nanoparticles establishes these core-shell NPs as a versatile platform for multiple applications.

  9. Relation Between the Adsorbed Quantity and the Immersion Enthalpy in Catechol Aqueous Solutions on Activated Carbons

    PubMed Central

    Moreno-Piraján, Juan Carlos; Blanco, Diego; Giraldo, Liliana

    2012-01-01

    An activated carbon, CarbochemTM—PS230, was modified by chemical and thermal treatment in flow of H2, in order to evaluate the influence of the activated carbon chemical characteristics in the adsorption of the catechol. The catechol adsorption in aqueous solution was studied along with the effect of the pH solution in the adsorption process of modified activated carbons and the variation of immersion enthalpy of activated carbons in the aqueous solutions of catechol. The interaction solid-solution is characterized by adsorption isotherms analysis, at 298 K and pH 7, 9 and 11 in order to evaluate the adsorption value above and below that of the catechol pKa. The adsorption capacity of carbons increases when the solution pH decreases. The retained amount increases slightly in the reduced carbon to maximum adsorption pH and diminishes in the oxidized carbon. Similar conclusions are obtained from the immersion enthalpies, whose values increase with the solute quantity retained. In granular activated carbon (CAG), the immersion enthalpies obtained are between 21.5 and 45.7 J·g−1 for catechol aqueous solutions in a range of 20 at 1500 mg·L−1. PMID:22312237

  10. Carbyne fiber synthesis within evaporating metallic liquid carbon

    SciTech Connect

    Cannella, Christopher B.; Goldman, Nir

    2015-07-09

    Carbyne (e.g., linear chains of sp-bonded carbon) has been the subject of intense research focus due to its presence in astrophysical bodies, as well as its potential for use as a nanoelectronic device and superhard material. In this work, we discuss the formation of carbyne fiber bundles over a nanosecond time scale in laser pulse melting studies, using a previously determined density functional tight binding model for carbon coupled with a new correction for the dispersion energy. We determine our dispersion energy model by optimizing a modified Lennard-Jones potential to an experimentally determined equation of state for graphite, yielding excellent results for the bulk modulus and density under ambient conditions. We then simulate previous experiments by heating graphite to high temperature, followed by expanding the ensuing liquid phase to low density. Our results indicate that the initial, hot liquid phase mainly consists of sp2-bonded carbon atoms, which form a system of sp-bonded strands bound together via dispersion interactions upon achieving low density and temperature. Lastly, the high computational efficiency of our approach allows for direct comparison with experiments that span a wide range of thermodynamic conditions and can help determine parameters for synthesis of carbon-based materials with potentially exotic properties.

  11. Carbyne fiber synthesis within evaporating metallic liquid carbon

    DOE PAGES

    Cannella, Christopher B.; Goldman, Nir

    2015-07-09

    Carbyne (e.g., linear chains of sp-bonded carbon) has been the subject of intense research focus due to its presence in astrophysical bodies, as well as its potential for use as a nanoelectronic device and superhard material. In this work, we discuss the formation of carbyne fiber bundles over a nanosecond time scale in laser pulse melting studies, using a previously determined density functional tight binding model for carbon coupled with a new correction for the dispersion energy. We determine our dispersion energy model by optimizing a modified Lennard-Jones potential to an experimentally determined equation of state for graphite, yielding excellentmore » results for the bulk modulus and density under ambient conditions. We then simulate previous experiments by heating graphite to high temperature, followed by expanding the ensuing liquid phase to low density. Our results indicate that the initial, hot liquid phase mainly consists of sp2-bonded carbon atoms, which form a system of sp-bonded strands bound together via dispersion interactions upon achieving low density and temperature. Lastly, the high computational efficiency of our approach allows for direct comparison with experiments that span a wide range of thermodynamic conditions and can help determine parameters for synthesis of carbon-based materials with potentially exotic properties.« less

  12. Comparison of nutshell granular activated carbons to commercial adsorbents for the purge-and-trap gas chromatographic analysis of volatile organic compounds.

    PubMed

    Wartelle, L H; Marshall, W E; Toles, C A; Johns, M M

    2000-05-26

    Granular activated carbons (GACs) made from agricultural by-products were investigated as adsorbents for short path thermal desorption gas chromatographic analysis of selected polar and nonpolar organic compounds. GACs made from macadamia nut, black walnut and hazelnut shells were compared to four commercially available adsorbents, namely, Tenax TA, Carboxen 569, Carbosieve SIII and coconut charcoal for their properties in purge-and-trap analysis. Adsorption values and breakthrough volumes were calculated for compounds from C3 and C6-C10. GACs derived from macadamia nut shells were found to adsorb and desorb between 80% (benzene) and 277% (ethylbenzene) more acetone (C3), benzene (C6), toluene (C7), ethyl- (C8), n-propyl- (C9), or sec.-butylbenzenes (C10) purged from water at the 100 ppb level than the commercial adsorbents tested. PMID:10893033

  13. Ceramic silicon-boron-carbon fibers from organic silicon-boron-polymers

    NASA Technical Reports Server (NTRS)

    Riccitiello, Salvatore R. (Inventor); Hsu, Ming-Ta S. (Inventor); Chen, Timothy S. (Inventor)

    1993-01-01

    Novel high strength ceramic fibers derived from boron, silicon, and carbon organic precursor polymers are discussed. The ceramic fibers are thermally stable up to and beyond 1200 C in air. The method of preparation of the boron-silicon-carbon fibers from a low oxygen content organosilicon boron precursor polymer of the general formula Si(R2)BR(sup 1) includes melt-spinning, crosslinking, and pyrolysis. Specifically, the crosslinked (or cured) precursor organic polymer fibers do not melt or deform during pyrolysis to form the silicon-boron-carbon ceramic fiber. These novel silicon-boron-carbon ceramic fibers are useful in high temperature applications because they retain tensile and other properties up to 1200 C, from 1200 to 1300 C, and in some cases higher than 1300 C.

  14. Effects of carbon/graphite fiber contamination on high voltage electrical insulation

    NASA Technical Reports Server (NTRS)

    Garrity, T.; Eichler, C.

    1980-01-01

    The contamination mechanics and resulting failure modes of high voltage electrical insulation due to carbon/graphite fibers were examined. The high voltage insulation vulnerability to carbon/graphite fiber induced failure was evaluated using a contamination system which consisted of a fiber chopper, dispersal chamber, a contamination chamber, and air ducts and suction blower. Tests were conducted to evaluate the effects of fiber length, weathering, and wetness on the insulator's resistance to carbon/graphite fibers. The ability of nuclear, fossil, and hydro power generating stations to maintain normal power generation when the surrounding environment is contaminated by an accidental carbon fiber release was investigated. The vulnerability assessment included only the power plant generating equipment and its associated controls, instrumentation, and auxiliary and support systems.

  15. Hybridization of poly(rI) with poly(rC) adsorbed to the carbon nanotube surface

    PubMed Central

    2014-01-01

    Hybridization of homopolynucleotide poly(rC) adsorbed to the carbon nanotube surface with poly(rI) free in solution has been studied by absorption spectroscopy and molecular dynamics method. It was found that hybridization on the nanotube surface has a slow kinetics, the behavior of which differs essentially from fast hybridization of free polymers. The duplex obtained is characterized with the reduced thermostability and a lower hyperchromic coefficient than it was observed when the duplex was formed in the absence of the nanotube. These features point to the imperfectness in the structure of the duplex hybridized on the nanotube surface. Computer simulation showed that the strong interaction of nitrogen bases with the nanotube surface weakens significantly hybridization of two complementary oligomers, as the surface prevents the necessary conformational mobility of the polymer to be hybridized. PMID:24690381

  16. Mesophase pitch-based carbon fiber for improved inflammability of CFRP

    SciTech Connect

    Nakagoshi, Akira; Tomonoh, Shigeki; Sakamoto, Yosihiro

    1995-10-01

    Carbon Fiber Reinforced Plastics (CFRP) are extensively used because of their favorable physical properties such as high strength-to-weight ratio and small thermal expansion. However, flammability of CFRP has limited their application especially in the transportation and industrial field. Exposed to flame, CFRP laminates made of PAN-based carbon fibers burst into flame in short time, while CFRP laminates made from mesophase pitch-based carbon fibers don`t burst into flame. This paper describes the experimental results of local heating test by gas burner. When the flame temperature was 1,000 C, a CFRP laminate made from PAN-based carbon fiber burned within 40 sec. Under the same condition, a CFRP laminate made from mesophase pitch-based carbon fiber didn`t burn in 10 min. The matrix resin of both laminates was 250 F curable epoxy resin. This behavior mainly depends upon the thermal conductivity of the carbon fibers. The mesophase pitch-based carbon fibers have high thermal conductivity, so they can diffuse thermal energy and lower laminate surface temperature. On the other hand, PAN-based carbon fibers have low thermal conductivity, so they can`t diffuse thermal energy enough, and the laminates made from them burn easily. Mechanical properties of CFRP during local heating test in comparison with Aluminum plate are also discussed.

  17. [Modification of activated carbon fiber for electro-Fenton degradation of phenol].

    PubMed

    Ma, Nan; Tian, Yao-Jin; Yang, Guang-Ping; Xie, Xin-Yuan

    2014-07-01

    Microwave-modified activated carbon fiber (ACF-1), nitric acid-modified activated carbon fiber (ACF-2), phosphoric acid-modified activated carbon fiber (ACF-3) and ammonia-modified activated carbon fiber (ACF-4) were successfully fabricated. The electro-Fenton catalytic activities of modified activated carbon fiber were evaluated using phenol as a model pollutant. H2O2 formation, COD removal efficiency and phenol removal efficiency were investigated compared with the unmodified activated carbon fiber (ACF-0). Results indicated that ACF-1 showed the best adsorption and electrocatalytic activity. Modification was in favor of the formation of H2O2. The performance of different systems on phenol degradation and COD removal were ACF-1 > ACF-3 > ACF-4 > ACF-2 > ACF-0 and ACF-1 > ACF-4 > ACF-3 > ACF-2 > ACF-0, respectively, which confirmed that electrocatalytic activities of modified activated carbon fiber were better than the unmodified. In addition, phenol intermediates were not the same while using different modified activated carbon fibers.

  18. CuFe2O4/activated carbon composite: a novel magnetic adsorbent for the removal of acid orange II and catalytic regeneration.

    PubMed

    Zhang, Gaosheng; Qu, Jiuhui; Liu, Huijuan; Cooper, Adrienne T; Wu, Rongcheng

    2007-06-01

    CuFe2O4/activated carbon magnetic adsorbents, which combined the adsorption features of activated carbon with the magnetic and the excellent catalytic properties of powdered CuFe2O4, were developed using a simple chemical coprecipitation procedure. The prepared magnetic composites can be used to adsorb acid orange II (AO7) in water and subsequently, easily be separated from the medium by a magnetic technique. CuFe2O4/activated carbon magnetic adsorbents with mass ratio of 1:1, 1:1.5 and 1:2 were prepared. Magnetization measurements, BET surface area measurements, powder XRD and SEM were used to characterize the prepared adsorbents. The results indicate that the magnetic phase present is spinel copper ferrite and the presence of CuFe2O4 did not significantly affect the surface area and pore structure of the activated carbon. The adsorption kinetics and adsorption isotherm of acid orange II (AO7) onto the composites at pH 5.2 also showed that the presence of CuFe2O4 did not affect the adsorption capacity of the activated carbon. The thermal decomposition of AO7 adsorbed on the activated carbon and the composite was investigated by in situ FTIR, respectively. The results suggest that the composite has much higher catalytic activity than that of activated carbon, attributed to the presence of CuFe2O4. The variation of the adsorption capacity of the composites after several adsorption-regeneration cycles has also been studied.

  19. Impeded repair of abasic site damaged lesions in DNA adsorbed over functionalized multiwalled carbon nanotube and graphene oxide.

    PubMed

    Kumari, Rina; Mondal, Titash; Bhowmick, Anil K; Das, Prolay

    2016-06-01

    The processing of abasic site DNA damage lesions in extracellular DNA in the presence of engineered carbon nanomaterials (CNMs) is demonstrated. The efficacy of the apurinic-apyrimidinic endonuclease 1 (APE1) in the cleavage of abasic site lesions in the presence of carboxylated multi-walled carbon nanotubes (MWCNT-COOH) and graphene oxide (GO) are compared. The CNMs were found to perturb the incision activity of APE1. The reason for such perturbation process was anticipated to take place either by the non-specific adsorption of APE1 over the free surface of the CNMs or steric hindrance offered by the CNM-DNA complex. Accordingly, bovine serum albumin (BSA) was selectively utilized to block the free surface of the CNM-DNA hybrid material. Further treatment of the CNM-DNA-BSA complex with APE1 resulted in a marginal increase in APE1 efficiency. This indicates that APE1 in solution is unable to process the abasic sites on DNA adsorbed over the CNMs. However, the cleavage activity of APE1 was restored in the presence of non-ionic surfactant (Tween 20) that inhibits adsorption of the DNA on the surface of the CNMs. The conformational deformation of the DNA, along with steric hindrance induced by the CNMs resulted in the inhibition of abasic site DNA repair by APE1. Moreover, appreciable changes in the secondary structure of APE1 adsorbed over the CNMs were observed that contribute further to the repair refractivity of the abasic sites. From a toxicological viewpoint, these findings can be extended to the study of the effect of engineered nanoparticles in the intracellular DNA repair process. PMID:27265379

  20. Preparation and characterization of humic acid-carbon hybrid materials as adsorbents for organic micro-pollutants.

    PubMed

    Radwan, Emad K; Abdel Ghafar, Hany H; Moursy, Ahmed S; Langford, Cooper H; Bedair, Ahmed H; Achari, Gopal

    2015-08-01

    The present work involves the preparation of novel adsorbent materials by the insolubilization and hybridization of humic acid (HA) with carbon. The prepared materials were characterized by N2 adsorption, elemental analysis, Fourier transform infrared spectroscopy, scanning electron microscopy, transmission electron microscopy, solid-state (13)C cross polarization magic angle spinning nuclear magnetic resonance, and low-field nuclear magnetic resonance (NMR) relaxometry on wetted samples. The water solubility of these materials and the lack of effect of oxidants were also confirmed. With this background, the adsorption capacities toward phenol, 2,4,6-tricholrophenol, and atrazine were evaluated, using these as model compounds for organic micropollutants of concern in water. Experimental results show that the prepared materials are mesoporous and have a higher surface area than humic acid and even than the porous carbon in the case of carbon coating. They retain the basic features of the starting materials with lowered functional group content. Moreover, there are interesting new features. NMR relaxometry shows that equilibration of water uptake is very fast, making use in water simple. They have higher adsorption capacities than the pure materials, and they can be applied under a wide range of environmental conditions. PMID:25874433