Science.gov

Sample records for alcohol pva films

  1. Luminescence study of ZnSe/PVA (polyvinyl alcohol) composite film

    NASA Astrophysics Data System (ADS)

    Lahariya, Vikas

    2016-05-01

    The ZnSe nanocrystals have been prepared into poly vinyl alcohol(PVA) polymer matrix on glass using ZnCl2 and Na2SeSO3 as zinc and selenium source respectively. Poly vinyl Alcohol (PVA) used as polymer matrix cum capping agent due to their high viscosity and water solubility. It is transparent for visible region and prevents Se- ions to photo oxidation. The ZnSe/PVA composite film was deposited on glass substrate. The film was characterized by X Ray Diffraction (XRD) and UV-Visible absorption Spectroscopy and Photoluminescence. The X Ray Diffraction (XRD) study confirms the nanometer size (10 nm) particle formation within PVA matrix with cubic zinc blend crystal structure. The UV-Visible Absorption spectrum of ZnSe/PVA composite film shown blue shift in absorption edge indicating increased band gap due to quantum confinement. The calculated energy band gap from the absorption edge using Tauc relation is 3.4eV. From the Photoluminescence study a broad peak at 435 nm has been observed in violet blue region due to recombination of surface states.

  2. Surface resistivity temperature dependence measures of commercial, multiwall carbon nanotubes (MWCNT), or silver nano-particle doped polyvinylidene difluoride (PVDF) and polyvinyl alcohol (PVA) films

    NASA Astrophysics Data System (ADS)

    Edwards, Matthew; Egarievwe, Stephen; Kukhtareva, Tatiana; Polius, Jemilia; Janen, Afef; Corda, John

    2014-10-01

    The detection of infrared radiation (IR) with pure and doped Polyvinylidene difluoride (PVDF) films has been well documented using the mechanism of pyroelectricity. Alternatively, the electrical properties of films made from Polyvinyl Alcohol (PVA) have received considerable attention in recent years. The investigation of surface resistivities of both such films, to this point, has received far less consideration in comparison to pyroelectric effects. In this research, we report temperature dependent surface resistivity measurements of commercial, and of multiwall carbon nanotubes (MWCNT), or Ag-nanoparticle doped PVA films. Without any variation in the temperature range from 22°C to 40°C with controlled humidity, we found that the surface resistivity decreases initially, reaches a minimum, but rises steadily as the temperature continues to increase. This research was conducted with the combined instrumentation of the Keithley Model 6517 Electrometer and Keithley Model 8009 resistivity test fixture using both commercial and in-house produced organic thin films. With the objective to quantify the suitability of PVDF and PVA films as IR detector materials, when using the surface resistivity phenomenon, instead of or in addition to the pyroelectricity, surface resistivity measurements are reported when considering bolometry. We find the surface resistivity of PVDF films to be in the range, which extends beyond the upper limit of our Keithley electrometer, but our measurements on PVA films were readily implemented.

  3. Determining the electrical mechanism of the surface resistivity property of doped polyvinyl alcohol (PVA) and the pyroelectric property of polyvinylidene difluoride (PVDF) thin films

    NASA Astrophysics Data System (ADS)

    Edwards, Matthew; Janen, Afef; Guggilla, Padmaja; Polius, Jemelia; Douglas, Jade; Curley, Michael

    2015-08-01

    Previously, we have reported measurements of the temperature-dependent surface resistivity of pure and multi-walled carbon nanotubes doped Polyvinyl Alcohol (PVA) thin films. In the temperature range from 22 °C to 40 °C, with a humidity-controlled environment, we found the surface resistivity to decrease initially but to rise steadily as the temperature continued to increase. Correspondingly, we have measured the temperature-dependent pyroelectric coefficient of doped polyvinylidene difluoride (PVDF) thin films, very well. While the physical mechanism of the pyroelectric phenomenon in PVDF thin films is quite well known, the surface resistivity behavior of PVA thin films is not so well known. Here, we address this concern by reporting the electrical mechanistic phenomena that contribute to surface resistivity of pure and doped PVA thin films, and give preliminary surface resistivity detectivity and other relevant quality factors for infrared (IR) and motion sensors. Regarding the pyroelectric effect of doped PVDF thin films, we give materials Figures-of-Merit based on our measurements. In addition, pyroelectric and surface resistivity infrared fundamentals, IR sensor uniqueness, and innovative techniques are presented.

  4. Fabrication of silver nanoparticles embedded into polyvinyl alcohol (Ag/PVA) composite nanofibrous films through electrospinning for antibacterial and surface-enhanced Raman scattering (SERS) activities.

    PubMed

    Zhang, Zhijie; Wu, Yunping; Wang, Zhihua; Zou, Xueyan; Zhao, Yanbao; Sun, Lei

    2016-12-01

    Silver nanoparticle-embedded polyvinyl alcohol (PVA) nanofibers were prepared through electrospinning technique, using as antimicrobial agents and surface-enhanced Raman scattering (SERS) substrates. Ag nanoparticles (NPs) were synthesized in liquid phase, followed by evenly dispersing in PVA solution. After electrospinning of the mixed solution at room temperature, the PVA embedded with Ag NPs (Ag/PVA) composite nanofibers were obtained. The morphologies and structures of the as-synthesized Ag nanoparticles and Ag/PVA fibers were characterized by the techniques of transmission electron microscopy (TEM), X-ray diffraction (XRD), ultraviolet-visible absorption spectroscopy (UV-vis), Fourier transform infrared spectroscopy (FTIR), scanning electron microscopy (SEM) and energy-dispersive X-ray spectroscopy (EDX). Ag NPs have an average diameter of 13.8nm, were found to be uniformly dispersed in PVA nanofibers. The Ag/PVA nanofibers provided robust antibacterial activities against both Gram-positive Staphylococcus aureus (S. aureus) and Gram-negative Escherichia coli (E. coli) microorganisms. It's also found that Ag/PVA nanofibers make a significant contribution to the high sensitivity of SERS to 4-mercaptophenol (4-MPh) molecules. PMID:27612736

  5. Fabrication of silver nanoparticles embedded into polyvinyl alcohol (Ag/PVA) composite nanofibrous films through electrospinning for antibacterial and surface-enhanced Raman scattering (SERS) activities.

    PubMed

    Zhang, Zhijie; Wu, Yunping; Wang, Zhihua; Zou, Xueyan; Zhao, Yanbao; Sun, Lei

    2016-12-01

    Silver nanoparticle-embedded polyvinyl alcohol (PVA) nanofibers were prepared through electrospinning technique, using as antimicrobial agents and surface-enhanced Raman scattering (SERS) substrates. Ag nanoparticles (NPs) were synthesized in liquid phase, followed by evenly dispersing in PVA solution. After electrospinning of the mixed solution at room temperature, the PVA embedded with Ag NPs (Ag/PVA) composite nanofibers were obtained. The morphologies and structures of the as-synthesized Ag nanoparticles and Ag/PVA fibers were characterized by the techniques of transmission electron microscopy (TEM), X-ray diffraction (XRD), ultraviolet-visible absorption spectroscopy (UV-vis), Fourier transform infrared spectroscopy (FTIR), scanning electron microscopy (SEM) and energy-dispersive X-ray spectroscopy (EDX). Ag NPs have an average diameter of 13.8nm, were found to be uniformly dispersed in PVA nanofibers. The Ag/PVA nanofibers provided robust antibacterial activities against both Gram-positive Staphylococcus aureus (S. aureus) and Gram-negative Escherichia coli (E. coli) microorganisms. It's also found that Ag/PVA nanofibers make a significant contribution to the high sensitivity of SERS to 4-mercaptophenol (4-MPh) molecules.

  6. Holographic characterization of DYE-PVA films studied at 442 nm for optical elements fabrication

    NASA Astrophysics Data System (ADS)

    Couture, Jean J.

    1991-12-01

    The present work is an experimental study of the speed of hologram recording in dichromated polyvinyl alcohol films (DC-PVA) and DYE-DC-PVA films. Real-time recordings give high diffraction efficiency and low signal-to-noise ratio holograms without any chemical development. The dyes studied here are MALACHITE GREEN, EOSIN Y, and ROSE BENGAL introduced in DC-PVA films having a thickness of 60 - 62 micrometers . The best of these DYE-DC-PVA systems is a good candidate for holographic optical elements fabrication.

  7. Effect of cross linking of PVA/starch and reinforcement of modified barley husk on the properties of composite films.

    PubMed

    Mittal, Aanchal; Garg, Sangeeta; Kohli, Deepak; Maiti, Mithu; Jana, Asim Kumar; Bajpai, Shailendra

    2016-10-20

    Barley husk (BH) was graft copolymerized by palmitic acid. The crystalline behavior of BH decreased after grafting. Poly vinyl alcohol (PVA)/starch (St) blend film, urea formaldehyde cross linked PVA/St films and composite films containing natural BH, grafted BH were prepared separately. The effect of urea/starch ratio, content of BH and grafted BH on the mechanical properties, water uptake (%), and biodegradability of the composite films was observed. With increase in urea: starch ratio from 0 to 0.5 in the blend, tensile strength of cross linked film increased by 40.23% compared to the PVA/St film. However, in grafted BH composite film, the tensile strength increased by 72.4% than PVA/St film. The degradation rate of natural BH composite film was faster than PVA/St film. Various films were characterized by SEM, FT-IR and thermal analysis. PMID:27474641

  8. Effect of interfibrillar PVA bridging on water stability and mechanical properties of TEMPO/NaClO2 oxidized cellulosic nanofibril films.

    PubMed

    Hakalahti, Minna; Salminen, Arto; Seppälä, Jukka; Tammelin, Tekla; Hänninen, Tuomas

    2015-08-01

    TEMPO/NaClO2 oxidized cellulosic nanofibrils (TCNF) were covalently bonded with poly(vinyl alcohol) (PVA) to render water stable films. Pure TCNF films and TCNF-PVA films in dry state showed similar humidity dependent behavior in the elastic region. However, in wet films PVA had a significant effect on stability and mechanical characteristics of the films. When soaked in water, pure TCNF films exhibited strong swelling behavior and poor wet strength, whereas covalently bridged TCNF-PVA composite films remained intact and could easily be handled even after 24h of soaking. Wet tensile strength of the films was considerably enhanced with only 10 wt% PVA addition. At 25% PVA concentration wet tensile strengths were decreased and films were more yielding. This behavior is attributed to the ability of PVA to reinforce and plasticize TCNF-based films. The developed approach is a simple and straightforward method to produce TCNF films that are stable in wet conditions.

  9. Anammox sludge immobilized in polyvinyl alcohol (PVA) cryogel carriers

    Technology Transfer Automated Retrieval System (TEKTRAN)

    This study evaluated the use of polyvinyl alcohol (PVA) cryogels to encapsulate slow-growing anammox bacteria for deammonification treatment of wastewater. The cryogel pellets were prepared by a freezing-thawing procedure at -8 oC. On average, pellets contained 11.8 mg TSS/g-pellet of enriched anamm...

  10. Effect of PVA concentration on bond modifications in PVA-PMMA blend films

    NASA Astrophysics Data System (ADS)

    Tripathi, J.; Tripathi, S.; Sharma, A.; Bisen, R.; Shripathi, T.

    2016-05-01

    The optical properties of poly (methylmethacrylate) (PMMA) polymer are found to be modified when PVA molecules are added in the matrix of PMMA and vice versa making a blend. The concentrations studied were kept low to preserve the original properties of the host. It was seen that PMMA well protects its bonds and dominated the optical properties, while the properties of PVA are comparatively easier to modify when small amount of PMMA is inserted in PVA matrix. The results are interpreted in terms of bond modifications as seen from FTIR and absorption measurements and are useful in understanding the transparency and bandgap of the blend films.

  11. Synthesis, characterization and antibacterial activity of biodegradable starch/PVA composite films reinforced with cellulosic fibre.

    PubMed

    Priya, Bhanu; Gupta, Vinod Kumar; Pathania, Deepak; Singha, Amar Singh

    2014-08-30

    Cellulosic fibres reinforced composite blend films of starch/poly(vinyl alcohol) (PVA) were prepared by using citric acid as plasticizer and glutaraldehyde as the cross-linker. The mechanical properties of cellulosic fibres reinforced composite blend were compared with starch/PVA crossed linked blend films. The increase in the tensile strength, elongation percentage, degree of swelling and biodegradability of blend films was evaluated as compared to starch/PVA crosslinked blend films. The value of different evaluated parameters such as citric acid, glutaraldehyde and reinforced fibre to starch/PVA (5:5) was found to be 25 wt.%, 0.100 wt.% and 20 wt.%, respectively. The blend films were characterized using Fourier transform-infrared spectrophotometry (FTIR), scanning electron microscopy (SEM) and thermogravimetric analysis (TGA/DTA/DTG). Scanning electron microscopy illustrated a good adhesion between starch/PVA blend and fibres. The blend films were also explored for antimicrobial activities against pathogenic bacteria like Staphylococcus aureus and Escherichia coli. The results confirmed that the blended films may be used as exceptional material for food packaging.

  12. Micro structural studies of PVA doped with metal oxide nanocomposites films

    SciTech Connect

    Kumar, N. B. Rithin; Crasta, Vincent Viju, F.; Praveen, B. M.; Shreeprakash, B.

    2014-04-24

    Nanostructured PVA polymer composites are of rapidly growing interest because of their sized-coupled properties. The present article deals with both ZnO and WO{sub 3} embedded in a polyvinyl alcohol (PVA) matrix using a solvent casting method. These films were characterized using FTIR, XRD, and SEM techniques. The FTIR spectra of the doped PVA shows shift in the bands, which can be understood on the basis of intra/inter molecular hydrogen bonding with the adjacent OH group of PVA. The phase homogeneity and morphology of the polymer composites have been analyzed using scanning electron microscope (SEM). The crystal structure and crystallinity of polymer nanocomposites were studied by X-ray diffraction technique (XRD). Thus due to the interaction of dopant and complex formation, the structural repositioning takes place and crystallinity of the nanocomposites decreases.

  13. Microstructural and electrical properties of PVA/PVP polymer blend films doped with cupric sulphate

    NASA Astrophysics Data System (ADS)

    Hemalatha, K.; Mahadevaiah, Gowtham, G. K.; Urs, G. Thejas; Somashekarappa, H.; Somashekar, R.

    2016-05-01

    A series of polyvinyl alcohol (PVA)/polyvinyl pyrrolidone (PVP) polymer blends added with different concentrations of cupric sulphate (CuSO4) were prepared by solution casting method and were subjected to X-ray diffraction (XRD) and Ac conductance measurements. An attempt has been made to study the changes in crystal imperfection parameters in PVA/PVP blend films with the increase in concentration of CuSO4. Results show that decrease in micro crystalline parameter values is accompanied with increase in the amorphous content in the film which is the reason for film to have more flexibility, biodegradability and good ionic conductivity. AC conductance measurements in these films show that the conductivity increases as the concentration of CuSO4 increases. These films were suitable for electro chemical applications.

  14. Spectral studies of Donepezil release from streched PVA polymer films

    NASA Astrophysics Data System (ADS)

    Nechifor, Cristina-Delia; Zelinschi, Carmen-Beatrice; Stoica, Iuliana; Closca, Valentina; Dorohoi, Dana-Ortansa

    2013-07-01

    The focus of this research is to obtain poly vinyl alcohol (PVA) polymer foils containing Donepezil in different concentration, in order to be used in controlled drug release as a palliative treatment of mild to moderate Alzheimer's disease. The influence of polymeric foil stretching degree on drug release was analyzed using spectral measurements.

  15. Low doping concentration studies of doped PVA-Coumarin nanocomposite films

    NASA Astrophysics Data System (ADS)

    Tripathi, J.; Tripathi, S.; Bisen, R.; Sharma, A.; Choudhary, A.; Shripathi, T.

    2016-05-01

    The observations of combination of Poly (vinyl) alcohol and Coumarin properties in nanocmposite films are reported. The X-ray diffraction measurements reveal nanocrystalline nature of PVA film, which remains nanocrystalline after doping Coumarin but along with PVA peaks, additional peak due to dopant crystallinity is seen. The absorption edge shows a double edge feature, where distinct bandgaps for PVA host and dopant Coumarin are obtained. However at a higher doping wt % of 1 and 2, the absorption is mainly dominated by Coumarin and single absorption edge is observed giving a bandgap equal to that of bulk Coumarin (3.3 eV). The composite formation affects the bonding of host drastically and is seen through the bond modification in FTIR spectra. The results suggest that doping below 2 wt% is advantageous as combination of PVA and Coumarin properties are obtained but at 2 wt %, the properties are dominated by mainly Coumarin and the signature of PVA from optical properties is completely lost.

  16. X-ray irradiation-induced changes in (PVA-PEG-Ag) polymer nanocomposites films

    NASA Astrophysics Data System (ADS)

    Nouh, S. A.; Benthami, K.; Abutalib, M. M.

    2016-02-01

    The effects of X-ray irradiation on the structural, thermal and optical properties of polyvinyl alcohol-polyethylene glycol-silver (PVA-PEG-Ag) nanocomposites have been investigated. The samples of nanocomposites were prepared by adding Ag nanoparticles with 5 wt% to the (PVA-PEG) blend. The films of 0.05 mm thickness were prepared by the casting method. These films were irradiated with X-ray doses ranging from 20 to 200 kGy. The resultant effect of X-ray irradiation on the structural properties of PVA-PEG-Ag has been investigated using X-ray diffraction and Fourier transform infrared spectroscopy. Also, thermal property studies were carried out using thermogravimetric analysis. Further, the transmission of the PVA-PEG-Ag samples and any color changes were studied. Fourier transform infrared spectroscopy measurements showed that the crosslinking is the dominant mechanism at the dose range 50-200 kGy. This led to a more compact structure of PVA-PEG-Ag samples, which resulted in an improvement in its thermal stability with an increase in the activation energy of thermal decomposition. Moreover, the color intensity ΔE was greatly increased with an increase in the dose, and was accompanied by a significant increase in the yellow color component.

  17. Effects of PVA(Polyvinyl Alcohol) on Supercooling Phenomena of Water

    NASA Astrophysics Data System (ADS)

    Kumano, Hiroyuki; Saito, Akio; Okawa, Seiji; Takizawa, Hiroshi

    In this paper, effects of polymer additive on supercooling of water were investigated experimentally. Poly-vinyl alcohol (PVA) were used as the polymer, and the samples were prepared by dissolving PVA in ultra pure water. Concentration, degree of polymerization and saponification of PVA were varied as the experimental parameters. The sample was cooled, and the temperature at the instant when ice appears was measured. Since freezing of supercooled water is statistical phenomenon, many experiments were carried out and average degrees of supercooling were obtained for each experimental condition. As the result, it was found that PVA affects nucleation of supercooling and the degree of supercooling increases by adding the PVA. Especially, it is found that the average degree of supercooling increases and the standard deviation of average degree of supercooling decreases with increase of degree of saponification of PVA. However, the average degree of supercooling are independent of the degree of polymerization of PVA in the range of this study.

  18. Synthesis, characterisation and antibacterial activity of PVA/TEOS/Ag-Np hybrid thin films.

    PubMed

    Bryaskova, Rayna; Pencheva, Daniela; Kale, Girish M; Lad, Umesh; Kantardjiev, T

    2010-09-01

    Novel hybrid material thin films based on polyvinyl alcohol (PVA)/tetraethyl orthosilicate (TEOS) with embedded silver nanoparticles (AgNps) were synthesized using sol-gel method. Two different strategies for the synthesis of silver nanoparticles in PVA/TEOS matrix were applied based on reduction of the silver ions by thermal annealing of the films or by preliminary preparation of silver nanoparticles using PVA as a reducing agent. The successful incorporation of silver nanoparticles ranging from 5 to 7nm in PVA/TEOS matrix was confirmed by TEM and EDX analysis, UV-Vis spectroscopy and XRD analysis. The antibacterial activity of the synthesized hybrid materials against etalon strains of three different groups of bacteria -Staphylococcus aureus (gram-positive bacteria), Escherichia coli (gram-negative bacteria), Pseudomonas aeruginosa (non-ferment gram-negative bacteria) has been studied as they are commonly found in hospital environment. The hybrid materials showed a strong bactericidal effect against E. coli, S. aureus and P. aeruginosa and therefore have potential applications in biotechnology and biomedical science.

  19. Silk Nanospheres and Microspheres from Silk/PVA Blend Films for Drug Delivery

    PubMed Central

    Wang, Xiaoqin; Yucel, Tuna; Lu, Qiang; Hu, Xiao; Kaplan, David L.

    2009-01-01

    Silk fibroin protein-based micro- and nanospheres provide new options for drug delivery due to their biocompatibility, biodegradability and their tunable drug loading and release properties. In the present study, we report a new aqueous-based preparation method for silk spheres with controllable sphere size and shape. The preparation was based on phase separation between silk fibroin and polyvinyl alcohol (PVA) at a weight ratio of 1/1 and 1/4. Water-insoluble silk spheres were easily obtained from the blend in a three step process: (1) air-drying the blend solution into a film, (2) film dissolution in water and (3) removal of residual PVA by subsequent centrifugation. In both cases, the spheres had approximately 30% beta-sheet content and less than 5% residual PVA. Spindle-shaped silk particles, as opposed to the spherical particles formed above, were obtained by stretching the blend films before dissolving in water. Compared to the 1/1 ratio sample, the silk spheres prepared from the 1/4 ratio sample showed a more homogeneous size distribution ranging from 300 nm up to 20 μm. Further studies showed that sphere size and polydispersity could be controlled either by changing the concentration of silk and PVA or by applying ultrasonication on the blend solution. Drug loading was achieved by mixing model drugs in the original silk solution. The distribution and loading efficiency of the drug molecules in silk spheres depended on their hydrophobicity and charge, resulting in different drug release profiles. The entire fabrication procedure could be completed within one day. The only chemical used in the preparation except water was PVA, an FDA-approved ingredient in drug formulations. Silk micro- and nanospheres reported have potential as drug delivery carriers in a variety of biomedical applications. PMID:19945157

  20. Influence of Glyoxal on Preparation of Poly(Vinyl Alcohol)/Poly(Acrylic Acid) Blend Film.

    PubMed

    Park, Ju-Young; Hwang, Kyung-Jun; Yoon, Soon-Do; Lee, Ju-Heon; Lee, In-Hwa

    2015-08-01

    The preparation of a poly(vinyl alcohol)/poly(acrylic acid)/glyoxal film (PVA = poly(vinyl alcohol); PAA = poly(acrylic acid)) with high tensile strength and hydrophobic properties by using the crosslinking reaction for OH group removal is reported herein. PAA was selected as a crosslinking agent because the functional carboxyl group in each monomer unit facilitates reaction with PVA. The OH groups on unreacted PVA were removed by the addition of glyoxal to the PVA/PAA solution. The chemical properties of the PVA/PAA films were investigated using Fourier transformation infrared spectroscopy and the thermal properties of the PVA/PAA/glyoxal films were investigated by means of differential scanning calorimetry and thermogravimetric analysis. A tensile strength of 48.6 N/mm2 was achieved at a PVA/PAA ratio of 85/15 for the PVA/PAA film. The tensile strength of the cross-linked PVA/PAA/glyoxal film (10 wt% glyoxal) was increased by 55% relative to the pure PVA/PAA (85/15) film. The degree of swelling (DS) and solubility (S) of the 10 wt% (PVA/PAA = 85/15, wt%) film added 10 wt% glyoxal were 1.54 and 0.6, respectively. PMID:26369179

  1. Crystal structures and magnetic properties of magnetite (Fe3O4)/Polyvinyl alcohol (PVA) ribbon

    NASA Astrophysics Data System (ADS)

    Ardiyanti, Harlina; Suharyadi, Edi; Kato, Takeshi; Iwata, Satoshi

    2016-04-01

    Ribbon of magnetite (Fe3O4)/Polyvinyl Alcohol (PVA) nanoparticles have been successfully fabricated with various concentration of PVA synthesized by co-precipitation method. Particle size of nanoparticles Fe3O4 sample and ribbon Fe3O4/PVA 25% sample is about 9.34 nm and 11.29 nm, respectively. The result of Vibrating Sample Magnetometer (VSM) showed that saturation magnetization value decreased from 76.99 emu/g to 15.01 emu/g and coercivity increased from 49.30 Oe to 158.35 Oe as increasing concentration of PVA. Atomic Force Microscopy (AFM) analysis showed that encapsulated PVA given decreasing agglomeration, controlled shape of nanoparticles Fe3O4 more spherical and dispersed. Surface roughness decreased with increasing concentration of PVA.

  2. Cross-linked polyvinyl alcohol films as alkaline battery separators

    NASA Technical Reports Server (NTRS)

    Sheibley, D. W.; Manzo, M. A.; Gonzalez-Sanabria, O. D.

    1982-01-01

    Cross-linking methods were investigated to determine their effect on the performance of polyvinyl alcohol (PVA) films as alkaline battery separators. The following types of cross-linked PVA films are discussed: (1) PVA-dialdehyde blends post-treated with an acid or acid periodate solution (two-step method) and (2) PVA-dialdehyde blends cross-linked during film formation (drying) by using a reagent with both aldehyde and acid functionality (one-step method). Laboratory samples of each cross-linked type of film were prepared and evaluated in standard separator screening tests. The pilot-plant batches of films were prepared and compared to measure differences due to the cross-linking method. The pilot-plant materials were then tested in nickel oxide - zinc cells to compare the two methods with respect to performance characteristics and cycle life. Cell test results are compared with those from tests with Celgard.

  3. Cross-linked polyvinyl alcohol films as alkaline battery separators

    NASA Technical Reports Server (NTRS)

    Sheibley, D. W.; Manzo, M. A.; Gonzalez-Sanabria, O. D.

    1983-01-01

    Cross-linking methods have been investigated to determine their effect on the performance of polyvinyl alcohol (PVA) films as alkaline battery separators. The following types of cross-linked PVA films are discussed: (1) PVA-dialdehyde blends post-treated with an acid or acid periodate solution (two-step method) and (2) PVA-dialdehyde blends cross-linked during film formation (drying) by using a reagent with both aldehyde and acid functionality (one-step method). Laboratory samples of each cross-linked type of film were prepared and evaluated in standard separator screening tests. Then pilot-plant batches of films were prepared and compared to measure differences due to the cross-linking method. The pilot-plant materials were then tested in nickel oxide-zinc cells to compare the two methods with respect to performance characteristics and cycle life. Cell test results are compared with those from tests with Celgard.

  4. Isothermal and non-isothermal crystallization kinetics of PVA + ionic liquid [BDMIM][BF4]-based polymeric films

    NASA Astrophysics Data System (ADS)

    Saroj, A. L.; Chaurasia, S. K.; Kataria, Shalu; Singh, R. K.

    2016-06-01

    The effect of ionic liquid (IL), 1-butyl-2,3-dimethylimidazolium tetrafluoroborate [BDMIM][BF4], on crystallization behavior of poly(vinyl alcohol) (PVA) has been studied by isothermal and non-isothermal differential scanning calorimetry techniques. The PVA + IL based polymer electrolyte films have been prepared using solution casting technique. To describe the isothermal and non-isothermal crystallization kinetics, several kinetic equations have been employed on PVA + IL based films. There is strong dependence of the peak crystallization temperature (Tc), relative degree of crystallity (Xt), half-time of crystallization (t1/2), crystallization rate constants (Avrami Kt and Tobin AT), and Avrami (n) and Tobin (nT) exponents on the cooling rate and IL loading.

  5. The plasticizing mechanism and effect of calcium chloride on starch/poly(vinyl alcohol) films.

    PubMed

    Jiang, Xiancai; Jiang, Ting; Gan, Lingling; Zhang, Xiaofei; Dai, Hua; Zhang, Xi

    2012-11-01

    Starch/poly(vinyl alcohol) (PVA) films were prepared with calcium chloride (CaCl(2)) as the plasticizer. The micro morphology of pure starch/PVA film and CaCl(2) plasticized starch/PVA film was observed by scanning electron microscope. The interaction between CaCl(2) and starch/PVA molecules was investigated by Fourier transform infrared spectroscopy. The influence of CaCl(2) on the crystalline, thermal and mechanical properties of starch/PVA films was studied by X-ray diffraction, differential scanning calorimetry, thermogravimetric analysis, and tensile testing, respectively. The results indicated that CaCl(2) could interact with starch and PVA molecules and then effectively destroy the crystals of starch and PVA. Starch/PVA films plasticized with CaCl(2) became soft and ductile, with lower tensile strength and higher elongation at break compared with pure starch/PVA film. The water content of starch/PVA film would increase with the addition of CaCl(2). This is an important cause of the plasticization of CaCl(2) on starch/PVA film.

  6. Improvement of a Si solar cell efficiency using pure and Fe3+ doped PVA films

    NASA Astrophysics Data System (ADS)

    Khalifa, N.; Kaouach, H.; Chtourou, R.

    2015-07-01

    One of the most important key driving the economic viability of solar cells is the high efficiency. This research focuses on the enhancement of commercial Si solar cell performance by deposing a pure and Fe3+ doped polyvinyl alcohol (PVA) layer on the top of the Si wafer of the considered cells. The use of such polymer to improve solar cells efficiency is actually a first. The authors will rely on the optical characteristics of the pure and doped PVA films including absorption and emission properties to justify the effect on Si cells. Commercial monocrystalline silicon solar cells of 15 cm2 (0.49 V/460 mA) are used in this work. Films of almost 80 μm of the ferric polymer are deposed on the cells. Films with the same thickness are characterized by UV-Vis spectroscopy and photoluminescent emission of the films is then investigated. The electrical properties of the cells with and without the organometallic layer are evaluated. It will be deduced an important improvement of all electrical parameters, including short-circuit current, open-circuit voltage, fill factor and spatially the conversion efficiency by almost 3%.

  7. Formation mechanism of a silane-PVA/PVAc complex film on a glass fiber surface.

    PubMed

    Repovsky, Daniel; Jane, Eduard; Palszegi, Tibor; Slobodnik, Marek; Velic, Dusan

    2013-10-21

    Mechanical properties of glass fiber reinforced composite materials are affected by fiber sizing. A complex film formation, based on a silane film and PVA/PVAc (polyvinyl alcohol/polyvinyl acetate) microspheres on a glass fiber surface is determined at 1) the nanoscale by using atomic force microscopy (AFM), and 2) the macroscale by using the zeta potential. Silane groups strongly bind through the Si-O-Si bond to the glass surface, which provides the attachment mechanism as a coupling agent. The silane groups form islands, a homogeneous film, as well as empty sites. The average roughness of the silanized surface is 6.5 nm, whereas it is only 0.6 nm for the non-silanized surface. The silane film vertically penetrates in a honeycomb fashion from the glass surface through the deposited PVA/PVAc microspheres to form a hexagonal close pack structure. The silane film not only penetrates, but also deforms the PVA/PVAc microspheres from the spherical shape in a dispersion to a ellipsoidal shape on the surface with average dimensions of 300/600 nm. The surface area value Sa represents an area of PVA/PVAc microspheres that are not affected by the silane penetration. The areas are found to be 0.2, 0.08, and 0.03 μm(2) if the ellipsoid sizes are 320/570, 300/610, and 270/620 nm for silane concentrations of 0, 3.8, and 7.2 μg mL(-1), respectively. The silane film also moves PVA/PVAc microspheres in the process of complex film formation, from the low silane concentration areas to the complex film area providing enough silane groups to stabilize the structure. The values for the residual silane honeycomb structure heights (Ha ) are 6.5, 7, and 12 nm for silane concentrations of 3.8, 7.2, and 14.3 μg mL(-1), respectively. The pH-dependent zeta-potential results suggest a specific role of the silane groups with effects on the glass fiber surface and also on the PVA/PVAc microspheres. The non-silanized glass fiber surface and the silane film have similar zeta potentials ranging

  8. Micropatterning of silver nanoclusters embedded in polyvinyl alcohol films.

    PubMed

    Karimi, Nazanin; Kunwar, Puskal; Hassinen, Jukka; Ras, Robin H A; Toivonen, Juha

    2016-08-01

    Direct laser writing has been utilized to fabricate highly photostable fluorescent nanocluster microstructures in an organic polymer poly(methacrylic acid), where the carboxyl functional group is reported to play a vital role in nanocluster stabilization. In this Letter, we demonstrate that not only the polymer containing the carboxyl functional group, but also the polymer comprising the hydroxyl group, namely polyvinyl alcohol (PVA), can act as an appropriate stabilizer matrix for laser-induced synthesis and patterning of silver nanoclusters. The as-formed nanoclusters in the PVA film exhibit broadband emission and photostability comparable to the nanoclusters formed in the poly(methacrylic acid) polymer. As PVA is a widely used, nontoxic, biocompatible and biodegradable polymer, the technique of patterning fluorescent nanoclusters in PVA thin films is expected to find numerous applications in fields like fluorescence imaging, biolabeling, and sensing. PMID:27472635

  9. Electrical properties of irradiated PVA film by using ion/electron beam

    NASA Astrophysics Data System (ADS)

    Abdelrahman, M. M.; Osman, M.; Hashhash, A.

    2016-02-01

    Ion/electron beam bombardment has shown great potential for improving the surface properties of polymers. Low-energy charged (ion/electron) beam irradiation of polymers is a good technique to modify properties such as electrical conductivity, structural behavior, and their mechanical properties. This paper reports on the effect of nitrogen and electron beam irradiation on the electrical properties of polyvinyl alcohol (PVA) films. PVA films of 4 mm were exposed to a charged (ion/electron) beam for different treatment times (15, 30, and 60 minutes); the beam was produced from a dual beam source using nitrogen gas with the other ion/electron source parameters optimized. The dielectric loss tangent tan δ , electrical conductivity σ , and dielectric constant ɛ ^' } in the frequency range 100 Hz-100 kHz were measured at room temperature. The variation of dielectric constant and loss tangent as a function of frequency was also studied at room temperature. The dielectric constant was found to be strongly dependent on frequency for both ion and electron beam irradiation doses. The real (ɛ ^' }) and imaginary (ɛ ^' ' }) parts of the dielectric constant decreased with frequency for all irradiated and non-irradiated samples. The AC conductivity showed an increase with frequency for all samples under the influence of both ion and electron irradiation for different times. Photoluminescence (PL) spectral changes were also studied. The formation of clusters and defects (which serve as non-radiative centers on the polymer surface) is confirmed by the decrease in the PL intensity.

  10. Spectroscopic properties of (PVA+ZnO):Mn{sup 2+} polymer films

    SciTech Connect

    Rani, Ch.; Raju, D. Siva; Bindu, S. Hima; Krishna, J. Suresh; Raju, Ch. Linga

    2015-05-15

    Electron Paramagnetic Resonance (EPR), optical absorption and infrared spectral studies have been carried out on Mn{sup 2+} ions doped in poly(vinyl alcohol) complexed with zinc oxide polymer films prepared by solution cast technique. The EPR spectra of 1 mol% Mn{sup 2+} ions doped polymer complex (PVA+ZnO) at room temperature exhibit sextet hyperfine structure (hfs), centered at 2.01. The spin-Hamiltonian parameter values indicate that the ground state of Mn{sup 2+} ion in d{sup 5} and the site symmetry around Mn{sup 2+} ions in tetragonally distorted octa hedral site. The optical absorption spectra exhibits two bands centered at 275nm at 437nm. The FTIR spectrum exhibits bands characteristic of stretching and banding vibrations of O-H, C-H and C=C groups.

  11. Spectroscopic properties of (PVA+ZnO):Mn2+ polymer films

    NASA Astrophysics Data System (ADS)

    Rani, Ch.; Raju, D. Siva; Bindu, S. Hima; Krishna, J. Suresh; Raju, Ch. Linga

    2015-05-01

    Electron Paramagnetic Resonance (EPR), optical absorption and infrared spectral studies have been carried out on Mn2+ ions doped in poly(vinyl alcohol) complexed with zinc oxide polymer films prepared by solution cast technique. The EPR spectra of 1 mol% Mn2+ ions doped polymer complex (PVA+ZnO) at room temperature exhibit sextet hyperfine structure (hfs), centered at 2.01. The spin-Hamiltonian parameter values indicate that the ground state of Mn2+ ion in d5 and the site symmetry around Mn2+ ions in tetragonally distorted octa hedral site. The optical absorption spectra exhibits two bands centered at 275nm at 437nm. The FTIR spectrum exhibits bands characteristic of stretching and banding vibrations of O-H, C-H and C=C groups.

  12. Modifying Poly(Vinyl Alcohol) (PVA) from Insulator to Small-Bandgap Polymer: A Novel Approach for Organic Solar Cells and Optoelectronic Devices

    NASA Astrophysics Data System (ADS)

    Aziz, Shujahadeen B.

    2016-01-01

    An innovative method has been used to reduce the bandgap of poly(vinyl alcohol) (PVA) polymer by addition of a nontoxic, inexpensive, and environmentally friendly material. The resulting materials are small-bandgap polymers, hence opening new frontiers in green chemistry. The doped PVA films showed a wide range of light absorption of the solar spectrum from 200 nm to above 800 nm. Nonsharp absorption behavior versus wavelength was observed for the samples. The refractive index exhibited a wide range of dispersion. Shift of the absorption edge from 6.2 eV to 1.5 eV was observed. The energy bandgap of PVA was diminished to 1.85 eV upon addition of black tea extract solution, lying in the range of small-bandgap polymers. Increase of the optical dielectric constant was observed with increasing tea solution addition. The results indicate that small-bandgap PVA with good film-forming ability could be useful in terms of cost-performance tradeoff, solving problems of short lifetime, cost, and flexibility associated with conjugated polymers. The decrease of the Urbach energy upon addition of black tea extract solution indicates modification of PVA from a disordered to ordered material. X-ray diffraction results confirm an increase of the crystalline fraction in the doped samples.

  13. Study of parallel oriented electrospun polyvinyl alcohol (PVA) nanofibers using modified electrospinning method

    NASA Astrophysics Data System (ADS)

    Yusuf, Yusril; Ula, Nur Mufidatul; Jahidah, Khannah; Kusumasari, Ervanggis Minggar; Triyana, Kuwat; Sosiati, Harini; Harsojo

    2016-04-01

    Parallel orientedpolyvinyl alcohol (PVA) nanofibershasbeen successfully prepared by using modified electrospinning method. This method uses two pairs of copper (Cu) electrodes which are set apart at a certain distance and applied voltage of 15 kV. The concentrations of PVA were varied from 11%, 13%, 15%, 17%, and 19%. The width of gap collector were varied from 5 mm, 10 mm, 15 mm, and 20 mm. The diameter of nanofibers increase as increasing concentration of PVA. As the width of gap collector increase, first diameter of nanofibers decrease and reach a minimum value at 355 ± 7nm in 15 mm of gap, then the diameters increase again. We also calculated the alignment parameter (S) for given aligned nanofiber. The result showed that alignment parameters (S) were on values around 0,9-1.

  14. Enhanced mechanical, thermal and antimicrobial properties of poly(vinyl alcohol)/graphene oxide/starch/silver nanocomposites films.

    PubMed

    Usman, Adil; Hussain, Zakir; Riaz, Asim; Khan, Ahmad Nawaz

    2016-11-20

    In the present work, synthesis of poly(vinyl alcohol)/graphene oxide/starch/silver (PVA/GO/Starch/Ag) nanocomposites films is reported. Such films have been characterized and investigated for their mechanical, thermal and antimicrobial properties. The exfoliation of GO in the PVA matrix occurs owing to the non-covalent interactions of the polymer chains of PVA and hydrophilic surface of the GO layers. Presence of GO in PVA and PVA/starch blends were found to enhance the tensile strength of the nanocomposites system. It was found that the thermal stability of PVA as well as PVA/starch blend systems increased by the incorporation of GO where strong physical bonding between GO layers and PVA/starch blends is assumed to cause thermal barrier effects. Antimicrobial properties of the prepared films were investigated against Escherichia coli and Staphylococcus aureus. Our results show enhanced antimicrobial properties of the prepared films where PVA-GO, PVA-Ag, PVA-GO-Ag and PVA-GO-Ag-Starch showed antimicrobial activity in ascending order. PMID:27561532

  15. Rhizobia survival in seeds coated with polyvinyl alcohol (PVA) electrospun nanofibres.

    PubMed

    Damasceno, Raquel; Roggia, Isabel; Pereira, Claudio; de Sá, Enilson

    2013-11-01

    The electrospinning technique of rhizobia immobilization in nanofibres is an innovative and promising alternative for reducing the harmful effects of environmental stress on bacteria strains in a possible inoculant nanotechnology product for use in agriculture. The use of polyvinyl alcohol (PVA) shows up as an effective polymer in cell encapsulation because of its physical characteristics, such as viscosity and power of scattering. The aim of these studies has been to evaluate the survival of rhizobia incorporated in PVA nanofibres, which were applied to soybean seed and then subjected to different storage times and exposure to fungicide. The maintenance of the symbiotic characteristics of the incorporated bacterial strains was also evaluated, noting the formation of nodules in the soybean seedlings. No significant differences in the cell survival at 0 h and after 24 h of storage were observed. After 48 h, a significant difference in the bacterial cell concentration of the seeds affixed with PVA nanofibres was observed. Exposure to the fungicide decreased the viability of the bacteria strains even when coated with the nanofibres. A larger number of nodules formed in soybean seedlings from seeds inoculated with rhizobia incorporated in PVA nanofibres than from seeds inoculated with rhizobia without PVA. Thus, the electrospinning technique is a great alternative to the usual protector inoculants because of its unprecedented capacity to control the release of bacteria. PMID:24206353

  16. Enhanced blue light emission in transparent ZnO:PVA nanocomposite free standing polymer films

    NASA Astrophysics Data System (ADS)

    Karthikeyan, B.; Pandiyarajan, T.; Mangalaraja, R. V.

    2016-01-01

    ZnO:PVA nanocomposite films were prepared and their fluorescence and time resolved photoluminescence properties were discussed. X-ray diffraction and infrared spectroscopy results confirmed the ZnO:PVA interaction. Optical absorption spectra showed two bands at 280 and 367 nm which were ascribed to PVA and excitonic absorption band, respectively. Fluorescence spectra showed that the blue emission of ZnO was enhanced about tenfold through chemical interface electron transfer. The electron transfer from ZnO to PVA and its decay dynamics were experimentally analyzed through time resolved fluorescence measurements. The study revealed that the excited electrons found pathway through PVA to ground state which was slower than the pure ZnO nanoparticles.

  17. [Study on hydrophilicity and degradability of polyvinyl alcohol/polylactic acid blend film].

    PubMed

    Wang, Hualin; Sheng, Mingang; Zhai, Linfeng; Li, Yanhong

    2008-02-01

    Based on casting and solvent evaporation method, the degradable PLA/PVA blend film was prepared with polylactic acid (PLA) and polyvinyl alcohol (PVA) as raw material. The moisture absorbability, water absorbability and degradability of the polylactic acid/polyvinyl alcohol (PLA/PVA) blend film were studied; also the degradation mechanism of blend film was investigated. The results showed that the moisture absorption and water absorption of blend film decreased as the concentration of PLA increased. The degradation process of blend film in the normal saline is conducted by stepwise. At the forepart, the degradation of PLA played an important role, while PVA was the main degradation substance later. The solvent acidity could catalyze the degradation of PLA, and degradation of PLA was always turning from noncrystalline region to crystalline region. PVA had abilities to accelerate the degradation of PLA by increasing the hydrophilicity of the blend film and by breaking the crystallinity of PLA. Therefore, the hydrophilicity and degradability of PLA/PVA blend film can be controlled in a certain range by adjusting the proportion of PLA and PVA. PMID:18435276

  18. Dielectric relaxation analysis and Ac conductivity of polyvinyl alcohol/polyacrylonitrile film

    NASA Astrophysics Data System (ADS)

    Abdel-Baset, T. A.; Hassen, A.

    2016-10-01

    A film of 0.98 polyvinyl alcohol (PVA)/0.02 Polyacrylonitrile (PAN) has been prepared using casting method. The dielectric properties were measured as function of temperature and frequency. The dielectric permittivity of PVA is considerably enhanced by doping with PAN. Different relaxation processes have been recognized within the studied ranges of temperature and frequency. The frequency temperature superposition (FTS) is well verified. Frequency and temperature dependence of Ac conductivity, σac, were studied. The conduction mechanism of pure PVA and PVA doped with PAN are discussed. The activation energy either for relaxation or conduction was calculated. Comparison with similar polymeric materials is discussed.

  19. Dichromated polyvinyl alcohol (DC-PVA) wet processed for high index modulation

    NASA Astrophysics Data System (ADS)

    Rallison, Richard D.

    1997-04-01

    PVA films have been used as mold releases, strippable coatings, binders for photopolymers and when sensitized with metals and/or dyes they have been used as photoresists, volume HOEs, multiplexed holographic optical memory and real time non destructive holographic testing. The list goes on and includes Slime and birth control. In holography, DC-PVA is a real time photoanisotropic recording material useful for phase conjugation experiments and also a stable long term storage medium needing no processing other than heat. Now we add the capability of greatly increasing the versatility of PVA by boosting the index modulation by almost two orders of magnitude. We can add broadband display and HOE applications that were not possible before. Simple two or three step liquid processing is all that is required to make the index modulation grow.

  20. DBS investigation on films of cobalt chloride doped PVA-PVP blend

    NASA Astrophysics Data System (ADS)

    Hammannavar, Preeti B.; Baraker, Basavarajeshwari M.; Bhajantri, R. F.; Ravindrachary, V.; Lobo, Blaise

    2015-06-01

    Films of Cobalt Chloride (CoCl2) doped polyvinylalcohol(PVA)- polyvinylpyrrolidone(PVP) blend (doped from 0.5 wt% up to 28 wt%) were prepared by solution casting, and characterized by XRD, DSC, UV-Visible Spectrometry TGA, FTIR and electrical measurements. In this paper, the results of Doppler Broadening Spectroscopy (DBS) in CoCl2 doped PVA-PVP blend is discussed. An increase in crystallinity of PVA-PVP blend, is observed, on doping it with CoCl2. The DBS results are complemented by XRD and DSC scans.

  1. A stimuli-responsive and bioactive film based on blended polyvinyl alcohol and cashew gum polysaccharide.

    PubMed

    Silva, Fábio E F; Batista, Karla A; Di-Medeiros, Maria C B; Silva, Cassio N S; Moreira, Bruna R; Fernandes, Kátia F

    2016-01-01

    In this study, a stimuli-responsive, biodegradable and bioactive film was produced by blending cashew gum polysaccharide (CGP) and polyvinyl alcohol (PVA). The film presented malleability and mechanical properties enabling an easy handling. Wetting the film changed the optical property from opacity to levels of transparency higher than 70% and resulted in up to 2-fold increase in its superficial area. Different swelling indexes were obtained varying the pH of solvent, which allows classifying the CGP/PVA film as pH sensitive stimuli-responsive material. The bioactivity was achieved through covalent immobilization of papain, which remained active after storage of CGP/PVA-papain film for 24h in the presence of buffer or in a dry form. These results evidenced that CGP/PVA-papain film is a very promising material for biomedical applications.

  2. A stimuli-responsive and bioactive film based on blended polyvinyl alcohol and cashew gum polysaccharide.

    PubMed

    Silva, Fábio E F; Batista, Karla A; Di-Medeiros, Maria C B; Silva, Cassio N S; Moreira, Bruna R; Fernandes, Kátia F

    2016-01-01

    In this study, a stimuli-responsive, biodegradable and bioactive film was produced by blending cashew gum polysaccharide (CGP) and polyvinyl alcohol (PVA). The film presented malleability and mechanical properties enabling an easy handling. Wetting the film changed the optical property from opacity to levels of transparency higher than 70% and resulted in up to 2-fold increase in its superficial area. Different swelling indexes were obtained varying the pH of solvent, which allows classifying the CGP/PVA film as pH sensitive stimuli-responsive material. The bioactivity was achieved through covalent immobilization of papain, which remained active after storage of CGP/PVA-papain film for 24h in the presence of buffer or in a dry form. These results evidenced that CGP/PVA-papain film is a very promising material for biomedical applications. PMID:26478388

  3. Carboxyl-modified poly(vinyl alcohol)-crosslinked chitosan hydrogel films for potential wound dressing.

    PubMed

    Zhang, Di; Zhou, Wei; Wei, Bing; Wang, Xin; Tang, Rupei; Nie, Jiemin; Wang, Jun

    2015-07-10

    The objective of this study was to develop a novel carboxyl-modified poly(vinyl alcohol)-crosslinked chitosan hydrogel films for potential wound dressing. To prepare the crosslinked hydrogels, poly(vinyl alcohol) (PVA) was grafted with succinate acid to yield carboxyl-modified poly(vinyl alcohol) (PVA-COOH). Hydrogel films based on PVA-COOH and chitosan (CS) at different concentrations were crosslinked through the formation of amide linkages. The mechanical properties of these crosslinked hydrogel films in dry and swollen state were greatly improved with high swelling ratio. Water vapor and oxygen permeability evaluations indicated that crosslinked hydrogel films could maintain a moist environment over wound bed. Biocompatibility test showed the crosslinked hydrogels had no cytotoxicity and hemolytic potential. Gentamicin sulfate-loaded crosslinked hydrogel films showed sustained drug release profile, and could effectively suppress bacterial proliferation and protect wound from infection.

  4. Structural analysis, and antioxidant and antibacterial properties of chitosan-poly (vinyl alcohol) biodegradable films.

    PubMed

    Hajji, Sawssen; Chaker, Achraf; Jridi, Mourad; Maalej, Hana; Jellouli, Kemel; Boufi, Sami; Nasri, Moncef

    2016-08-01

    The development and characterization of biodegradable blend films based on chitosan and poly (vinyl alcohol) for possible use in a variety of biological activities are reported. Fourier transform infrared spectroscopy (FTIR) spectra of chitosan-poly (vinyl alcohol) (Ch/PVA) films showed characteristics peaks shifting to a lower frequency range due to hydrogen bonding between -OH of PVA and -NH2 of chitosan. The chitosan and PVA polymers presented good compatibility. The morphology study of chitosan and composite films showed a compact and homogenous structure. The tensile strength and elongation at break increased with PVA content. In fact, the highest tensile strength and elongation at break (53.58 MPa and 454 %) occurs with pure PVA film. The results showed that PVA incorporation in the blends contributes to increase the intermolecular interactions, thus improving the mechanical properties. In addition, the prepared films demonstrated high antioxidant activities monitored by 2,2-diphenyl-1-picrylhydrazyl (DPPH) radical-scavenging, reducing power, and β-carotene bleaching activity. Nevertheless, PVA addition reduced antioxidant and antibacterial activities against Gram-positive and Gram-negative bacteria tested. PMID:27106077

  5. Nitric oxide-releasing poly(vinyl alcohol) film for increasing dermal vasodilation.

    PubMed

    Marcilli, Raphael H M; de Oliveira, Marcelo G

    2014-04-01

    Pathological conditions associated with the impairment of nitric oxide (NO) production in the vasculature, such as Raynaud's syndrome and diabetic angiopathy, have stimulated the development of new biomaterials capable of delivering NO topically. With this purpose, we modified poly(vinyl-alcohol) (PVA) by chemically crosslinking it via esterification with mercaptosuccinic acid. This reaction allowed the casting of sulfhydrylated PVA (PVA-SH) films. Differential scanning calorimetry and X-ray diffractometry showed that the crosslinking reaction completely suppressed the crystallization of PVA, leading to a non-porous film with a homogeneous distribution of -SH groups. The remaining free hydroxyl groups in the PVA-SH network conferred partial hydrophylicity to the material, which was responsible for a swelling degree of ca. 110%. The PVA-SH films were subjected to an S-nitrosation reaction of the -SH groups, yielding a PVA containing S-nitrosothiol groups (PVA-SNO). Amperometric and chemiluminescence measurements showed that the PVA-SNO films were capable of releasing NO spontaneously after immersion in physiological medium. Laser Doppler-flowmetry, used to assess the blood flow in the dermal microcirculation, showed that the topical application of hydrated PVA-SNO films on the health skin led to a dose- and time-dependent increase of more than 5-fold in the dermal baseline blood flow in less than 10min, with a prolonged action of more than 4h during continuous application. These results show that PVA-SNO films might emerge as a new material with potential for the topical treatment of microvascular skin disorders.

  6. Fiber optic humidity sensor based on the graphene oxide/PVA composite film

    NASA Astrophysics Data System (ADS)

    Wang, Youqing; Shen, Changyu; Lou, Weimin; Shentu, Fengying

    2016-08-01

    Fiber optic humidity sensor based on an in-fiber Mach-Zehnder interferometer (MZI) coated with graphene oxide (GO)/PVA composite film was investigated. The MZI is constructed of two waist-enlarged tapers. The length between two waist-enlarged tapers is 20 mm. By comparing the experiment results of MZI coated with different GO/PVA composite films, composite film formed by the ratio of 0.3 g PVA mixed with 10 ml GO dispersion shows a better performance of relative humidity sensing. By using the molecular structure model of the composited GO/PVA, the operation mechanism between GO/PVA composite film and water molecules was illustrated. The sensitivity of 0.193 dB/%RH with a linear correlation coefficient of 99.1% and good stability under the relative humidity range of 25-80% was obtained. Temperature effect on the proposed fiber optic humidity sensor was also considered and analyzed. According to the repetitive experimental results, the proposed humidity sensor shows a good repeatability.

  7. Osteochondral defect repair using a polyvinyl alcohol-polyacrylic acid (PVA-PAAc) hydrogel.

    PubMed

    Bichara, David A; Bodugoz-Sentruk, Hatice; Ling, Doris; Malchau, Erik; Bragdon, Charles R; Muratoglu, Orhun K

    2014-08-01

    Poly(vinyl alcohol) (PVA) hydrogels can be candidates for articular cartilage repair due to their high water content. We synthesized a PVA-poly(acrylic acid) (PAAc) hydrogel formulation and determined its ability to function as a treatment option for condylar osteochondral (OC) defects in a New Zealand white rabbit (NZWR) model for 12 weeks and 24 weeks. In addition to hydrogel OC implants, tensile bar-shaped hydrogels were also implanted subcutaneously to evaluate changes in mechanical properties as a function of in vivo duration. There were no statistically significant differences (p > 0.05) in the water content measured in the OC hydrogel implant that was harvested after 12 weeks and 24 weeks, and non-implanted controls. There were no statistically significant differences (p > 0.05) in the break stress, strain at break or modulus of the tensile bars either between groups. Histological analysis of the OC defect, synovial capsule and fibrous tissue around the tensile bars determined hydrogel biocompatibility. Twelve-week hydrogels were found to be in situ flush with the articular cartilage; meniscal tissue demonstrated an intact surface. Twenty-four week hydrogels protruded from the defect site due to lack of integration with subchondral tissue, causing fibrillation to the meniscal surface. Condylar micro-CT scans ruled out osteolysis and bone cysts of the subchondral bone, and no PVA-PAAc hydrogel contents were found in the synovial fluid. The PVA-PAAc hydrogel was determined to be fully biocompatible, maintained its properties over time, and performed well at the 12 week time point. Physical fixation of the PVA-PAAc hydrogel to the subchondral bone is required to ensure long-term performance of hydrogel plugs for OC defect repair.

  8. Passive optical limiting studies of nanostructured Cu doped ZnO-PVA composite thin films

    NASA Astrophysics Data System (ADS)

    Tamgadge, Y. S.; Sunatkari, A. L.; Talwatkar, S. S.; Pahurkar, V. G.; Muley, G. G.

    2016-01-01

    We prepared undoped and Cu doped ZnO semiconducting nanoparticles (NPs) by chemical co-precipitation method and obtained Cu doped ZnO-polyvinyl alcohol (PVA) nanocomposite thin films by spin coating to investigate third order nonlinear optical and optical limiting properties under cw laser excitation. Powder samples of NPs were characterized by X-ray diffraction (XRD), field emission scanning electron microscopy (FE-SEM), energy dispersive spectroscopy, transmission electron microscopy, ultraviolet-visible (UV-vis) and Fourier transform infrared spectroscopy. XRD pattern and FE-SEM micrograph revealed the presence of hexagonal wurtzite phase ZnO NPs having uniform morphology with average particle size of 20 nm. The presence of excitons and absorption peaks in the range 343-360 nm, revealed by UV-vis study, were attributed to excitons in n = 1 quantum state. Third order NLO properties of all composite thin films were investigated by He-Ne continuous wave (cw) laser of wavelength 632.8 nm using Z-scan technique. Thermally stimulated enhanced values of nonlinear refraction and absorption coefficients were obtained which may be attributed to self-defocusing effect, reverse saturable absorption, weak free carrier absorption and surface states properties originated from thermo optic effect. Optical limiting properties have been studied using cw diode laser of wavelength 808 nm and results are presented.

  9. Dynamics in poly vinyl alcohol (PVA) based hydrogel: Neutron scattering study

    SciTech Connect

    Prabhudesai, S. A. Mitra, S.; Mukhopadhyay, R.; Lawrence, Mathias B.; Desa, J. A. E.

    2015-06-24

    Results of quasielastic neutron scattering measurements carried out on Poly Vinyl Alcohol (PVA) based hydrogels are reported here. PVA hydrogels are formed using Borax as a cross-linking agent in D{sub 2}O solvent. This synthetic polymer can be used for obtaining the hydrogels with potential use in the field of biomaterials. The aim of this paper is to study the dynamics of polymer chain in the hydrogel since it is known that polymer mobility influences the kinetics of loading and release of drugs. It is found that the dynamics of hydrogen atoms in the polymer chain could be described by a model where the diffusion of hydrogen atoms is limited within a spherical volume of radius 3.3 Å. Average diffusivity estimated from the behavior of quasielastic width is found to be 1.2 × 10{sup −5} cm{sup 2}/sec.

  10. Dynamics in poly vinyl alcohol (PVA) based hydrogel: Neutron scattering study

    NASA Astrophysics Data System (ADS)

    Prabhudesai, S. A.; Lawrence, Mathias B.; Mitra, S.; Desa, J. A. E.; Mukhopadhyay, R.

    2015-06-01

    Results of quasielastic neutron scattering measurements carried out on Poly Vinyl Alcohol (PVA) based hydrogels are reported here. PVA hydrogels are formed using Borax as a cross-linking agent in D2O solvent. This synthetic polymer can be used for obtaining the hydrogels with potential use in the field of biomaterials. The aim of this paper is to study the dynamics of polymer chain in the hydrogel since it is known that polymer mobility influences the kinetics of loading and release of drugs. It is found that the dynamics of hydrogen atoms in the polymer chain could be described by a model where the diffusion of hydrogen atoms is limited within a spherical volume of radius 3.3 Å. Average diffusivity estimated from the behavior of quasielastic width is found to be 1.2 × 10-5 cm2/sec.

  11. Enhanced mechanical properties and morphological characterizations of poly(vinyl alcohol) carbon nanotube composite films

    NASA Astrophysics Data System (ADS)

    Chen, Wei; Tao, Xiaoming; Xue, Pu; Cheng, Xiaoyin

    2005-12-01

    Tensile tests were carried out on free-standing composite films of poly(vinyl alcohol) (PVA) and multiwall carbon nanotubes (MWNTs) for different loading levels. Results show that overall mechanical properties of the composite were greatly improved as compared to the neat PVA film. For PVA-based materials at significant high loading level such as 9.1 wt.% MWNTs, considerable increases in Young's modulus, tensile strength and toughness by factors of 4.5, 2.7 and 4.1, respectively, were achieved. Raman, SEM, TEM, and DSC techniques were used to evaluate the PVA/MWNTs composite system. Strong acid-modification of the pristine MWNTs and the subsequent ultrasonication processing allowed good distribution of the nanotubes in the matrix. SEM together with DSC result shows apparent good wetting of the nanotubes by the PVA matrix, which are supportive of good interfacial bonding between the modified carbon nanotubes and the hosting polymer matrix.

  12. Development of polyvinyl alcohol and apple pomace bio-composite film with antioxidant properties for active food packaging application.

    PubMed

    Gaikwad, Kirtiraj K; Lee, Jin Yong; Lee, Youn Suk

    2016-03-01

    Active antioxidant food packaging films were developed by incorporation of apple pomace (AP) with 1, 5, 10, and 30 % (w/w) into polyvinyl alcohol (PVA) matrix. A complete thermal, structural, mechanical and functional characterization was carried out. The findings of this study showed that the incorporation of AP into PVA films enhanced the total phenolic content and antioxidant properties. As regards the physical properties, higher AP content incorporated into PVA films revealed significantly lower tensile strength, elongation at break and increase in thickness. PVA-AP films exhibited lower transparency value compared to control film. The thermal stability of PVA-AP films was improved and grew with the increasing concentration of AP. FTIR spectra indicated that protein-polyphenol interactions were involved in the PVA-AP films. Rough surface and compact-structure were observed in PVA-AP films. The storage study of soybean oil at 60 °C in PVA-AP pouch showed the antioxidant activity and the effectiveness for delaying its lipid oxidation. PMID:27570286

  13. Development of polyvinyl alcohol and apple pomace bio-composite film with antioxidant properties for active food packaging application.

    PubMed

    Gaikwad, Kirtiraj K; Lee, Jin Yong; Lee, Youn Suk

    2016-03-01

    Active antioxidant food packaging films were developed by incorporation of apple pomace (AP) with 1, 5, 10, and 30 % (w/w) into polyvinyl alcohol (PVA) matrix. A complete thermal, structural, mechanical and functional characterization was carried out. The findings of this study showed that the incorporation of AP into PVA films enhanced the total phenolic content and antioxidant properties. As regards the physical properties, higher AP content incorporated into PVA films revealed significantly lower tensile strength, elongation at break and increase in thickness. PVA-AP films exhibited lower transparency value compared to control film. The thermal stability of PVA-AP films was improved and grew with the increasing concentration of AP. FTIR spectra indicated that protein-polyphenol interactions were involved in the PVA-AP films. Rough surface and compact-structure were observed in PVA-AP films. The storage study of soybean oil at 60 °C in PVA-AP pouch showed the antioxidant activity and the effectiveness for delaying its lipid oxidation.

  14. TiO2 and polyvinyl alcohol (PVA) coated polyester filter in bioreactor for wastewater treatment.

    PubMed

    Liu, Lifen; Zhao, Chuanqi; Yang, Fenglin

    2012-04-15

    Prepared by coating TiO(2)/polyvinyl alcohol (PVA) on a low cost polyester filter cloth (22 μm), a composite membrane (10 μm pore size) was successfully used in an anoxic/oxic membrane bioreactor (A/O-MBR) for treating a simulate wastewater in removing nitrate/ammonium for water reuse in a polyester fiber production plant. Its permeate flux and the anti-fouling properties against extracellular polymeric substances (EPS) were studied. Comparing with a commercial (0.1 μm) PVDF (polyvinylidene fluoride) membrane, similar effluent qualities were achieved, meeting the basic COD requirements for reuse. Anti-EPS accumulation, the TiO(2)/PVA Polyester composite membrane had higher sustained permeability and required less frequent cleaning. Its filtration time was 4 times longer when operated at a higher flux than the PVDF membrane. The nano-TiO(2) enhances the interaction between PVA and polyester, forms a more hydrophilic surface, drastically reduces the contact angle with water and reduces EPS fouling. The slow (trans-membrane pressure) TMP rise, loose cake layer, the low filtration resistances, and the EPS, SEM analysis confirmed the advantage of the composite membrane. Potential in lowering the membrane cost, the operation and maintenance cost, and in enhancing MBR waste water treatment efficiency is expected by the use of this new composite membrane. PMID:22325932

  15. TiO2 and polyvinyl alcohol (PVA) coated polyester filter in bioreactor for wastewater treatment.

    PubMed

    Liu, Lifen; Zhao, Chuanqi; Yang, Fenglin

    2012-04-15

    Prepared by coating TiO(2)/polyvinyl alcohol (PVA) on a low cost polyester filter cloth (22 μm), a composite membrane (10 μm pore size) was successfully used in an anoxic/oxic membrane bioreactor (A/O-MBR) for treating a simulate wastewater in removing nitrate/ammonium for water reuse in a polyester fiber production plant. Its permeate flux and the anti-fouling properties against extracellular polymeric substances (EPS) were studied. Comparing with a commercial (0.1 μm) PVDF (polyvinylidene fluoride) membrane, similar effluent qualities were achieved, meeting the basic COD requirements for reuse. Anti-EPS accumulation, the TiO(2)/PVA Polyester composite membrane had higher sustained permeability and required less frequent cleaning. Its filtration time was 4 times longer when operated at a higher flux than the PVDF membrane. The nano-TiO(2) enhances the interaction between PVA and polyester, forms a more hydrophilic surface, drastically reduces the contact angle with water and reduces EPS fouling. The slow (trans-membrane pressure) TMP rise, loose cake layer, the low filtration resistances, and the EPS, SEM analysis confirmed the advantage of the composite membrane. Potential in lowering the membrane cost, the operation and maintenance cost, and in enhancing MBR waste water treatment efficiency is expected by the use of this new composite membrane.

  16. Design and manufacture of a polyvinyl alcohol (PVA) cryogel tri-leaflet heart valve prosthesis.

    PubMed

    Jiang, Hongjun; Campbell, Gord; Boughner, Derek; Wan, Wan-Kei; Quantz, Mackenzie

    2004-05-01

    Although current artificial heart valves are life sustaining medical devices, improvements are still necessary to address deficiencies. Bioprosthetic valves have a compromised fatigue life, while mechanical valves have better durability but are prone to thromboembolic complications. A novel, one-piece, tricuspid valve, consisting of leaflets, stent and sewing ring, made entirely from the hydrogel, polyvinyl alcohol cryogel (PVA-C), has been developed and demonstrated. This valve has three thin leaflets attached to a cylindrical stent. In order to approximate the complex shape of the surface of the natural heart valve leaflets, two different geometries have been proposed: revolution about an axis of a hyperboloid shape and revolution about an axis of an arc subtending (joining) two straight lines. The parameters of both geometries were examined based on a compromise between avoiding sharp curvature of leaflets and minimization of the central opening of the valve when closed. The revolution of an arc subtending two straight lines was selected as the preferred geometry since it has the benefit of a smaller central opening when the value of the maximum curvature for the leaflets is the same for each valve geometry. A cavity mold has been designed and constructed to form the PVA-C heart valve. The three leaflets were formed and integrated into the stent and sewing ring in a single process. Prototype heart valves were manufactured in the mold from a solution of PVA and water, by controlled freezing and thawing cycles. PMID:15121052

  17. Biodegradable starch/poly (vinyl alcohol) film reinforced with titanium dioxide nanoparticles

    NASA Astrophysics Data System (ADS)

    Hejri, Zahra; Seifkordi, Ali Akbar; Ahmadpour, Ali; Zebarjad, Seyed Mojtaba; Maskooki, Abdolmajid

    2013-10-01

    Biodegradable starch/poly (vinyl alcohol)/nano-titanium dioxide (ST/PVA/nano-TiO2) nanocomposite films were prepared via a solution casting method. Their biodegradability, mechanical properties, and thermal properties were also studied in this paper. A general full factorial experimental approach was used to determine effective parameters on the mechanical properties of the prepared films. ST/PVA/TiO2 nanocomposites were characterized by scanning electron microscopy (SEM) and X-ray diffraction (XRD). The results of mechanical analysis show that ST/PVA films with higher contents of PVA have much better mechanical properties. In thermal analysis, it is found that the addition of TiO2 nanoparticles improves the thermal stability of the films. SEM micrographs, taken from the fracture surface of samples, illustrate that the addition of PVA makes the film softer and more flexible. The results of soil burial biodegradation indicate that the biodegradability of ST/PVA/TiO2 films strongly depends on the starch proportion in the film matrix. The degradation rate is increased by the addition of starch in the films.

  18. ZnO-PVA nanocomposite films for low threshold optical limiting applications

    SciTech Connect

    Viswanath, Varsha; Beenakumari, C.; Muneera, C. I.

    2014-10-15

    Zinc oxide-PVA nanocomposite films were fabricated adopting a simple method based on solution-casting, incorporating small weight percentages (<1.2 wt%) of ZnO in PVA (∼0.625×10{sup −3}M to 7×10{sup −3}M), and their structure, morphology, linear and low threshold nonlinear optical properties were investigated. The films were characterized as nanostructured ZnO encapsulated between the molecules/chains of the semicrystalline host polymer PVA. The samples exhibited low threshold nonlinear absorption and negative nonlinear refraction, as studied using the Z-scan technique. A switchover from SA to RSA was observed as the concentration of ZnO was increased. The optical limiting of 632.8 nm CW laser light displayed by these nanocomposite films is also demonstrated. The estimated values of the effective coefficients of nonlinear absorption, nonlinear refraction and third-order nonlinear susceptibility, |χ{sup (3)}|, compared to those reported for continuous wave laser light excitation, measure up to the highest among them. The results show that the ZnO-PVA nanocomposite films have great potential applications in future optical and photonic devices.

  19. ZnO-PVA nanocomposite films for low threshold optical limiting applications

    NASA Astrophysics Data System (ADS)

    Viswanath, Varsha; Beenakumari, C.; Muneera, C. I.

    2014-10-01

    Zinc oxide-PVA nanocomposite films were fabricated adopting a simple method based on solution-casting, incorporating small weight percentages (<1.2 wt%) of ZnO in PVA (˜0.625×10-3M to 7×10-3M), and their structure, morphology, linear and low threshold nonlinear optical properties were investigated. The films were characterized as nanostructured ZnO encapsulated between the molecules/chains of the semicrystalline host polymer PVA. The samples exhibited low threshold nonlinear absorption and negative nonlinear refraction, as studied using the Z-scan technique. A switchover from SA to RSA was observed as the concentration of ZnO was increased. The optical limiting of 632.8 nm CW laser light displayed by these nanocomposite films is also demonstrated. The estimated values of the effective coefficients of nonlinear absorption, nonlinear refraction and third-order nonlinear susceptibility, |χ(3)|, compared to those reported for continuous wave laser light excitation, measure up to the highest among them. The results show that the ZnO-PVA nanocomposite films have great potential applications in future optical and photonic devices.

  20. Effects of Saponification Rate on Electrooptical Properties and Morphology of Poly(vinyl alcohol)/Liquid Crystal Composite Films

    NASA Astrophysics Data System (ADS)

    Ono, Hiroshi; Kawatsuki, Nobuhiro

    1995-03-01

    The relationship between the saponification rate of poly(vinyl alcohol) (PVA), and the electrooptical properties and morphology of the PVA/liquid crystal (LC) composite films was investigated. Light transmission clazing and the LC droplet size were varied by changing the saponification rate or the blend ratio of two kinds of PVA with different saponification rates because the refractive index and surface tension could be controlled by the saponification rate of PVA. The threshold voltage decreased with increasing saponification rate though the extrapolation length was decreased. It was suggested that the electrooptical properties were strongly dependent on the droplet size.

  1. Effect of the PVA (polyvinyl alcohol) concentration on the optical properties of Eu-doped YAG phosphors

    NASA Astrophysics Data System (ADS)

    Hora, Daniela A.; Andrade, Adriano B.; Ferreira, Nilson S.; Teixeira, Verônica C.; dos S. Rezende, Marcos V.

    2016-10-01

    The influence of the polyvinyl alcohol (PVA) concentration on the synthesis and structural, morphological and optical properties of Y3Al5O13: Eu (Eu-doped YAG) was systematically investigated in this work. The final concentration of PVA in the preparation step influenced the crystallite size and also the degree of particle agglomeration in Eu-doped YAG phosphors. X-ray excited optical luminescence (XEOL) emission spectra results indicated typical Eu3+ emission lines and an abnormally intense 5D0 → 7F4. The intensity parameters Ω2 and Ω4 were calculated and indicated the PVA concentration affects the ratio Ω2:Ω4. X-ray absorption spectroscopy (XAS) results showed Eu valence did not change and the symmetry around the Eu3+ is influenced by the PVA concentration. XEOL-XAS showed the luminescence increases as a function of energy.

  2. Electrical and optical properties of ferric doped PVA-PVP-PPy composite films

    NASA Astrophysics Data System (ADS)

    Patil, Ravikumar V.; Ranganath, M. R.; Lobo, Blaise

    2013-02-01

    The analysis of experimental optical spectra & electrical properties of PVA-PVP-PPy composite films is discussed in this paper. The optical parameters like activation energy of optical transitions and the optical band gap for direct and indirect allowed transitions were determined for PVA-PVP-PPy composite films doped with different concentrations of ferric chloride. The optical band gap showed best fit for indirect allowed transitions, and there is a decrease in the optical band gap with increase in concentration of ferric chloride. The DC electrical properties of these films indicated agreement with Mott's Variable Range Hopping Model in three dimensions. The width of the forbidden band gap was determined from the Arrhenius relation after experimentally studying in-situ, the variation of DC electrical conductivity with temperature.

  3. Electrical transport properties and current density - voltage characteristic of PVA-Ag nanocomposite film

    NASA Astrophysics Data System (ADS)

    Das, A. K.; Dutta, B.; Sinha, S.; Mukherjee, A.; Basu, S.; Meikap, A. K.

    2016-05-01

    Silver (Ag) nanoparticle and Polyvinyl alcohol (PVA) - Silver (Ag) composite have been prepared and its dielectric constant, ac conductivity, and current density-voltage characteristics have been studied, at and above room temperature. Here correlated barrier hopping found to be the dominant charge transport mechanism with maximum barrier height of 0.11 eV. The sample, under ±5 V applied voltage, show back to back Schottky diode behaviour.

  4. Preparation and properties of nanometer silk fibroin peptide/polyvinyl alcohol blend films for cell growth.

    PubMed

    Luo, Qin; Chen, Zhongmin; Hao, Xuefei; Zhu, Qiangsong; Zhou, Yucheng

    2013-10-01

    Nanometer silk fibroin peptide (Nano-SFP) was prepared from silkworm cocoons through the process of dissolution, dialysis and enzymolysis. For comparison, silk fibroin was decomposed with α-chymotrypsin, trypsin and neutrase, respectively. From the SEM and particle size analysis results, the Nano-SFP prepared by neutrase was found to be the most desirable at about 50-200 nm. Nano-SFP/polyvinyl alcohol films (Nano-SFP/PVA) were prepared by blending Nano-SFP and PVA in water with different weight ratios of 10/90, 20/80, 30/70, and 40/60. The films were characterized by IR, SEM, TG, DSC and tensile strength test for investigating their structure, surface morphology, thermostability, and mechanical property. The results showed that Nano-SFP inserted in the PVA films with small linear particles, and Nano-SFP/PVA films exhibited smooth surface, good thermostability and tensile strength. The growth of Chinese hamster ovary (CHO) cells on films with and without Nano-SFP was investigated with MTT colorimetric assay to assess the films' ability to promote cell growth. It was observed that the Nano-SFP improved cell adhesion on the film surface, and the ability of promoting cell growth increased with the increasing content of Nano-SFP in the blend films. Nano-SFP/PVA film with the ratio of 30/70 was concluded to have the best properties.

  5. [Preparation of polyvinyl alcohol film inlaid with silk fibroin peptide nano-scale particles and evaluation of its function to promote cell growth].

    PubMed

    Chen, Zhongmin; Hao, Xuefei; Fan, Kai

    2010-12-01

    Nano-scale particles of silk fibroin peptide (SFP) were prepared from discarded materials of cocoon or filature by dissolving and enzymolysis. Polyvinyl Alcohol films inlaid with silk fibroin peptide nano-scale particles (SFP in PVA) were prepared by blending nano-SFP and PVA in water according to different blending ratios. The films' characteristics and their promoting cell growth functions were investigated. Silk fibroin fiber was dissolved in 60% NaSCN solution, and was decomposed with alpha-Chymotrypsin, Trypsin and Neutral, respectively. The uniformity of size of SFP nano-particles prepared by Neutral was better and appeared about 80-150 nm. (SFP in PVA) films were characterized by infrared spectroscopy (IR) measurement which demonstrated the combination of SFP and PVA. Scanning electron microscopy revealed the PVA films already inlaid with SFP micro-segment. The surface and form stability in water of the (SFP in PVA) films with blending ratios of 10/90, 20/80, 30/70 and 40/60 were observed. And the results showed that SFP/PVA film with the blending ratio of 30/70 has smoother surface and better stability in water. The Chinese hamster ovary (CHO) cells were cultured, and the promoting cell growth function of (SFP in PVA) films was assessed by MTT colorimetric assay. These findings indicate that SFP/PVA (30/70) film has excellent function of promoting cell growth.

  6. Degradation of polyvinyl alcohol (PVA) by homogeneous and heterogeneous photocatalysis applied to the photochemically enhanced Fenton reaction.

    PubMed

    Bossmann, S H; Oliveros, E; Göb, S; Kantor, M; Göppert, A; Lei, L; Yue, P L; Braun, A M

    2001-01-01

    The reaction mechanism of the oxidative degradation of polyvinyl alcohol (PVA) by the photochemically enhanced Fenton reaction was studied using a homogeneous (Fe2+(aq) + H2O2) and a heterogeneous reaction system (iron(III)-exchanged zeolite Y+ H2O2). In the homogeneous Fenton system, efficient degradation was observed in a batch reactor, equipped with a medium pressure mercury arc in a Pyrex envelope and employing 80% of the stoichiometric amount of H2O2 required for the total oxidation of PVA and a concentration ratio as low as I mole of iron(II) sulfate per 20 moles of PVA sub-units (C2H40). Model PVA polymers of three different molecular weights (15,000, 49,000 and 100,000 g mol(-1)) were found to follow identical degradation patterns. Strong experimental evidence supports the formation of supermacromolecules (MW: 1-5 x 10(6) g/mol) consisting of oxidized PVA and trapped iron(III) at an early reaction stage. Low molecular weight intermediates, such as oxalic acid, formic acid or formaldehyde were not found during PVA degradation in the homogeneous Fenton system, and we may deduce that the manifold of degradation reactions is mainly taking place within the super-macromolecules from which CO2 is directly released. However, in the heterogeneous Fenton system, the reaction behavior was found to be distinctly different: a decrease of the molecular weights of all three tested monodisperse PVA samples was observed by the broadening of the GPC-traces during irradiation, and oxalic acid was formed. The results lead to the mechanistic hypothesis that during the heterogeneous Fenton process, the cleavage of the PVA-chains may occur at random positions, the reactive centres being located inside the iron(III)-doped zeolite Y photocatalysts.

  7. Tuning optical and three photon absorption properties in graphene oxide-polyvinyl alcohol free standing films

    NASA Astrophysics Data System (ADS)

    Karthikeyan, B.; Udayabhaskar, R.; Hariharan, S.

    2016-07-01

    We report the optical and nonlinear optical properties of graphene oxide (GO)-polyvinyl alcohol (PVA) free standing films. The composite polymer films were prepared in ex-situ method. The variation in optical absorption spectra and optical constants with the amount of GO loading was noteworthy from the optical absorption spectroscopic studies. Nonlinear optical studies done at 532 nm using 5 ns laser pulses show three photon absorption like behaviour. Both steady state and time resolved fluorescence studies reveal that the GO was functioning as a pathway for the decay of fluorescence from PVA. This is attributed to the energy level modifications of GO through hydroxyl groups with PVA. Raman spectroscopy also supports the interaction between GO and PVA ions through OH radicals.

  8. XPS study of Rhodamine B doped PVA nanocomposite films as a function of annealing

    NASA Astrophysics Data System (ADS)

    Tripathi, J.; Tripathi, S.; Sharma, A.; Bisen, R.; Singh, J.

    2016-05-01

    The bonding properties of PVA thin films are explored as a function of annealing in pure and Rhodamine B doped self-standing films. X-ray photoelectron spectroscopy measurements have shown high quality, impurity free films, where the bonding is found between C and O elements in agreement with the standard data of polymers. Upon annealing, the bonds break and signals come only from elemental carbon and oxygen at their respective binding energy positions. The experiments are able to show that upon annealing at 65° C, all the bonds break and hence electronic properties are completely modified.

  9. Kinetics and functional effectiveness of nisin loaded antimicrobial packaging film based on chitosan/poly(vinyl alcohol).

    PubMed

    Wang, Hualin; Zhang, Ru; Zhang, Heng; Jiang, Suwei; Liu, Huan; Sun, Min; Jiang, Shaotong

    2015-01-01

    The aim of this study was to evaluate the kinetics and functional effectiveness of Nisin loaded chitosan/poly(vinyl alcohol) (Nisin-CS/PVA) as an antibacterial packaging film. The films were prepared by coating method and Staphylococcus aureus (S. aureus, ATCC6538) was used as test bacterium. The intermolecular hydrogen bonds between CS and PVA molecules were confirmed. The elasticity of films was significantly improved by the incorporation of PVA, and the film could also bear a relative high tensile strength at 26.7 MPa for CS/PVA=1/1. As CS/PVA ratio decreased, the water vapor permeability (WVP) decreased and reached its minimum value 0.983 × 10(-10)gm(-1)s(-1) at CS/PVA=1/1, meanwhile, oxygen permeability (OP) increased but still lower than 0.91 cm(3) μm m(-2)d(-1)kPa(-1) for CS/PVA=1/1 as the CS/PVA ratio was above 1:1. The initial diffusion of nisin (Mt/M ∞ < 2/3) from CS/PVA film could be well described by the Fickian diffusion equation. Owing to the positively charged nisin at pH below isoelectric point (pI, 8.8) and its increasing dissolubility in water as the pH reduced, the diffusion of nisin from the films strongly depended on pH and ionic strength besides CS/PVA ratio and temperature. Moreover, the thermodynamic parameters suggested the spontaneous and endothermic diffusion of nisin from the films. The resulting data can provide some valuable information for the design of film in structure and ingredient.

  10. Kinetics and functional effectiveness of nisin loaded antimicrobial packaging film based on chitosan/poly(vinyl alcohol).

    PubMed

    Wang, Hualin; Zhang, Ru; Zhang, Heng; Jiang, Suwei; Liu, Huan; Sun, Min; Jiang, Shaotong

    2015-01-01

    The aim of this study was to evaluate the kinetics and functional effectiveness of Nisin loaded chitosan/poly(vinyl alcohol) (Nisin-CS/PVA) as an antibacterial packaging film. The films were prepared by coating method and Staphylococcus aureus (S. aureus, ATCC6538) was used as test bacterium. The intermolecular hydrogen bonds between CS and PVA molecules were confirmed. The elasticity of films was significantly improved by the incorporation of PVA, and the film could also bear a relative high tensile strength at 26.7 MPa for CS/PVA=1/1. As CS/PVA ratio decreased, the water vapor permeability (WVP) decreased and reached its minimum value 0.983 × 10(-10)gm(-1)s(-1) at CS/PVA=1/1, meanwhile, oxygen permeability (OP) increased but still lower than 0.91 cm(3) μm m(-2)d(-1)kPa(-1) for CS/PVA=1/1 as the CS/PVA ratio was above 1:1. The initial diffusion of nisin (Mt/M ∞ < 2/3) from CS/PVA film could be well described by the Fickian diffusion equation. Owing to the positively charged nisin at pH below isoelectric point (pI, 8.8) and its increasing dissolubility in water as the pH reduced, the diffusion of nisin from the films strongly depended on pH and ionic strength besides CS/PVA ratio and temperature. Moreover, the thermodynamic parameters suggested the spontaneous and endothermic diffusion of nisin from the films. The resulting data can provide some valuable information for the design of film in structure and ingredient. PMID:25965457

  11. Combined nitric oxide-releasing poly(vinyl alcohol) film/F127 hydrogel for accelerating wound healing.

    PubMed

    Schanuel, Fernanda Seabra; Raggio Santos, Karen Slis; Monte-Alto-Costa, Andréa; de Oliveira, Marcelo G

    2015-06-01

    Nitric oxide (NO) releasing biomaterials represent a potential strategy for use as active wound dressings capable of accelerating wound healing. Topical NO-releasing poly(vinyl alcohol) (PVA) films and Pluronic F127 hydrogels (F127) have already exhibited effective skin vasodilation and wound healing actions. In this study, we functionalized PVA films with SNO groups via esterification with a mixture of mercaptosucinic acid (MSA) and thiolactic acid (TLA) followed by S-nitrosation of the SH moieties. These films were combined with an underlying layer of poly(ethylene oxide)-poly(propylene oxide)-poly(ethylene oxide), i.e., PEO-PPO-PEO (Pluronic F127) hydrogel and used for the topical treatment of skin lesions in an animal model. The mixed esterification of PVA with MSA and TLA led to chemically crosslinked PVA-SNO films with a high swelling capacity capable of spontaneously releasing NO. Real time NO-release measurements revealed that the hydrogel layer reduces the initial NO burst from the PVA-SNO films. We demonstrate that the combination of PVA-SNO films with F127 hydrogel accelerates wound contraction, decreases wound gap and cellular density and accelerates the inflammatory phase of the lesion. These results were reflected in an increase in myofibroblastic differentiation and collagen type III expression in the cicatricial tissue. Therefore, PVA-SNO films combined with F127 hydrogel may represent a new approach for active wound dressings capable of accelerating wound healing. PMID:25907598

  12. Nonlinear optical properties of ZnO/poly (vinyl alcohol) nanocomposite films

    SciTech Connect

    Jeeju, P. P.; Jayalekshmi, S.; Chandrasekharan, K.

    2014-01-28

    Extensive studies have already been reported on the optical characteristics of ZnO/polymer nanocomposite films, using a variety of polymers including transparent polymers such as polystyrene, polymethyl methacrylate etc and many interesting results have been established regarding the non linear optical characteristics of these systems. Poly (vinyl alcohol)(PVA) is a water soluble polymer. Though the structural and optical studies of ZnO/PVA nanocomposite films have already been investigated, there are no detailed reports on the nonlinear optical characteristics of ZnO/PVA nanocomposite films, irrespective of the fact that these nanocomposite films can be synthesized using quite easy and cost effective methods. The present work is an attempt to study in detail the nonlinear optical behaviour of ZnO/PVA nanocomposite films using Z-scan technique. Highly transparent ZnO/PVA nanocomposite films were prepared from the ZnO incorporated PVA solution in water using spin coating technique. The ZnO nanoparticles were synthesized by the simple chemical route at room temperature. High-resolution transmission electron microscopy studies show that the ZnO nanoparticles are of size around 10 nm. The ZnO/PVA nanocomposite films were structurally characterized by X-ray diffraction technique, from which the presence of both PVA and ZnO in the nanocomposite was established. The optical absorptive nonlinearity in the nanocomposite films was investigated using open aperture Z-scan technique. The results indicate optical limiting type nonlinearity in the films due to two photon absorption in ZnO with efficiency more than 50%. These films also show a self defocusing type negative nonlinear refraction in closed aperture Z-scan experiment. The present studies indicate that, highly transparent and homogeneous films of ZnO/PVA nanocomposite can be obtained on glass substrates using simple methods, in a highly cost effective way, since PVA is water soluble. These nanocomposite films offer

  13. Preparation of cellulose/polyvinyl alcohol biocomposite films using 1-n-butyl-3-methylimidazolium chloride.

    PubMed

    Abdulkhani, Ali; Hojati Marvast, Ebrahim; Ashori, Alireza; Hamzeh, Yahya; Karimi, Ali Naghi

    2013-11-01

    This study has been focused on developing cellulose/polyvinyl alcohol (PVA), a biocomposite film, pretreated with 1-n-butyl-3-methylimidazolium chloride ([bmim]Cl). The dissolved polymers were blended and their biocomposite films including cellulose and cellulose/PVA were prepared. The effect of PVA composition with cellulose was evaluated by comparing the physical, mechanical, chemical and thermal characteristics of produced films with neat cellulosic film. The results showed that the ionic liquid had a great capability in dissolving the polymers. Furthermore, in composition of the raw cellulose some chemical bonds were incorporated between the two components. Water uptake, thickness swelling and water vapor permeability of blend films were increased comparing to cellulosic film. Mechanical strength and Young's modulus of the films made of cellulose/PVA were decreased while the strain at break was increased. The optical transparency and thermal properties of the blend films were almost the same as neat cellulosic film. This work demonstrated a promising route for the preparation of biodegradable green composites. In addition, this biocomposite film is composed of sustainable biodegradable resources, which is suitable for release to the environment. The biocomposite films showed good optical transparency, thermal stabilities properties.

  14. Radiation preparation of graphene/carbon nanotubes hybrid fillers for mechanical reinforcement of poly(vinyl alcohol) films

    NASA Astrophysics Data System (ADS)

    Ma, Hui-Ling; Zhang, Long; Zhang, Youwei; Wang, Shuojue; Sun, Chao; Yu, Hongyan; Zeng, Xinmiao; Zhai, Maolin

    2016-01-01

    Graphene/carbon nanotubes (G/CNTs) hybrid fillers were synthesized by γ-ray radiation reduction of graphene oxide (GO) in presence of CNTs. The obtained hybrid fillers with three-dimensional (3D) interconnected network structure were characterized by X-ray diffraction (XRD) and scanning electron microscope (SEM). Poly(vinyl alcohol) (PVA) composite films with enhanced mechanical properties and thermal stability were subsequently prepared by solution blending of G/CNTs with PVA matrix. The tensile strength and Young's modulus of PVA composite films containing 1 wt% G/CNTs were measured to be 81.9 MPa and 3.9 GPa respectively, which were 56% and 33.6% higher than those of pure PVA. These substantial improvements could be attributed to the interconnected 3D structure of G/CNTs, homogeneous dispersion as well as the strong hydrogen-bonding interaction between G/CNTs and PVA macromolecular chains.

  15. Microstructure and molecular interaction in glycerol plasticized chitosan/poly(vinyl alcohol) blending films

    Technology Transfer Automated Retrieval System (TEKTRAN)

    Poly (vinyl alcohol) (PVA)/chitosan (CS) blended films plasticized by glycerol were investigated using mechanical testing, atomic force microscopy (AFM), differential scanning calorimetry (DSC) and FTIR spectroscopy, with primary emphasis on the effects of the glycerol content and the molecular weig...

  16. Electrical Conductivity Study of Polymer Electrolyte Magnetic Nanocomposite Based Poly(Vinyl) Alcohol (PVA) Doping Lithium and Nickel Salt

    NASA Astrophysics Data System (ADS)

    Aji, Mahardika Prasetya; Rahmawati, Silvia, Bijaksana, Satria; Khairurrijal, Abdullah, Mikrajuddin

    2010-10-01

    Composite polymer electrolyte magnetic systems composed of poly(vinyl) alcohol (PVA) as the host polymer, lithium and nickel salt as dopant were studied. The effect upon addition of lithium ions in polimer PVA had been enhanced conductivity with the increase of lithium concentration. The conductivity values were 1.19x10-6, 1.25x10-5, 4.89x-5, 1.88x10-4, and 1.33x10-3 Sṡcm-1 for pure PVA and 1%, 3%, 5% and 7% LiOH complexed PVA, respectively. Meanwhile, the addition nickel salt into polymer electrolyte PVA-LiOH does not significantly change of conductivity value, on order 10-3 Sṡcm-1. The ionic transport is dominantly regarded by Li+ ions present in polymer electrolyte magnetic because the atomic mass Li+ is smaller than Ni2+. The absence of external magnetic field in polimer electrolyte magnetic causes the existence Ni2+ ions not significantly affected of conductivity.

  17. Poly(vinyl alcohol)/Liquid Crystal Composite Films with Low Driving Voltage

    NASA Astrophysics Data System (ADS)

    Ono, Hiroshi; Kawatsuki, Nobuhiro

    1994-12-01

    A poly(vinyl alcohol) (PVA)/liquid crystal (LC) composite film with a low driving voltage of 6 Vrms, a low hysteresis of less than 0.2 Vrms, and a fast response time of 11 ms at the operating voltage of 6 Vrms was formed from the emulsion composed of a mixture of water with methanol (WM-mixture), PVA, LC, and a photocrosslinkable mixture of nonaoxyethylenediacrylate (9EG-A) with perfluorooctylethylacrylate (FA-108). It was found in the composite film that the liquid crystal droplets, surrounded by a thin layer of the photocured polymer, were deformed as well as disordered, which enhanced light scattering.

  18. Optical Properties of Neodymium Oxide Nanoparticle-Doped Polyvinyl Alcohol Film

    NASA Astrophysics Data System (ADS)

    Keikhaei, Mansoureh; Motevalizadeh, Leili; Attaran-Kakhki, Ebrahim

    2016-04-01

    The structural and optical characteristics of polyvinyl alcohol (PVA) doped with different concentration of Nd2O3 nanoparticles to use an active media for polymer laser were studied. The PVA polymer was considered as the host and Nd2O3 nanoparticles as the active element. The media as a thin film was prepared using spin coating technique. Structural properties of layers were investigated by X-ray diffraction (XRD) pattern and atomic force microscope (AFM) technique. The effect of the concentrations of the neodymium source on the optical properties of Nd2O3/PVA thin films was investigated through UV-Vis absorption spectroscopy and their optical band gap was evaluated. Also, the FTIR and fluorescence spectra of the samples were detected. The fluorescence spectra of films showed that the maximum wavelength occurred at 568nm with no significant shift.

  19. Anomalous dielectric behaviour of poly(vinyl alcohol)-silicon dioxide (PVA-SiO2) nanocomposites

    NASA Astrophysics Data System (ADS)

    Choudhary, Shobhna; Sengwa, R. J.

    2016-05-01

    Complex dielectric function, electric modulus, ac conductivity and impedance spectra of PVA-SiO2 nanocomposite films have been investigated in the frequency range of 20 Hz to 1 MHz and temperature range from 30 °C to 60 °C. Real part of dielectric function of the nanocomposites slowly decreases with increase of frequency and it shows a non-linear increase with the increase of temperature. An anomalous variation is observed in dielectric and electrical functions with increase of SiO2 concentrations in the PVA matrix. The ac conductivity of these materials increases whereas impedance values decrease linearly by five orders of magnitude with increase of frequency from 20 Hz to 1 MHz. Dielectric loss values of these films are found minimum at intermediate frequency region, and it increases at low and high frequency regions confirming the presence of multiple relaxation processes. The contributions of interfacial polarization effect and dipolar ordering in dielectric properties of these materials have been explored, and their technological applications as nanodielectrics have been discussed. The XRD patterns reveal that the interactions between PVA and SiO2 disturb the dipolar ordering resulting decrease of crystallinity of the PVA in the nanocomposites.

  20. Investigation of polypyrrole/polyvinyl alcohol-titanium dioxide composite films for photo-catalytic applications

    NASA Astrophysics Data System (ADS)

    Cao, Shaoqiang; Zhang, Hongyang; Song, Yuanqing; Zhang, Jianling; Yang, Haigang; Jiang, Long; Dan, Yi

    2015-07-01

    Polypyrrole/polyvinyl alcohol-titanium dioxide (PPy/PVA-TiO2) composite films used as photo-catalysts were fabricated by combining TiO2 sol with PPy/PVA solution in which PPy was synthesized by in situ polymerization of pyrrole (Py) in polyvinyl alcohol (PVA) matrix and loaded on glass. The prepared photo-catalysts were investigated by X-ray diffraction (XRD), ultraviolet-visible diffuse reflection spectroscopy (UV-vis DRS), scanning electron microscopy (SEM), Fourier transform infrared (FT-IR) spectra and photoluminescence (PL). The results indicate that the composites have same crystal structure as the TiO2 and extend the optic absorption from UV region to visible light region. By detecting the variation ratio, detected by ultraviolet-vis spectroscopy, of model pollutant rhodamine B (RhB) solution in the presence of the composite films under both UV and visible light irradiation, the photo-catalytic performance of the composite films was investigated. The results show that the PPy/PVA-TiO2 composite films show better photo-catalytic properties than TiO2 film both under UV and visible light irradiation, and the photo-catalytic degradation of RhB follows the first-order kinetics. The effects of the composition of composite films and the concentration of RhB on the photo-catalytic performance, as well as the possible photo-catalytic mechanism, were also discussed. By photo-catalytic recycle experiments, the structure stability of the PPy/PVA-TiO2 composite film was investigated and the results show that the photo-catalytic activity under both UV and visible light irradiation have no significant decrease after four times of recycle experiments, suggesting that the photo-catalyst film is stable during the photo-catalytic process, which was also confirmed by the XRD pattern and FT-IR spectra of the composite film before and after photo-catalytic.

  1. Characterizing p-channel thin film transistors using ZnO/hydrated polyvinyl alcohol as the conducting channel

    SciTech Connect

    Liau, Leo Chau-Kuang Hsu, Tzu-Hsien; Lo, Pei-Hsuan

    2014-08-11

    We report the characteristics of p-channel thin film transistors (p-TFTs) with ZnO/hydrated polyvinyl alcohol (PVA) (ZnO/PVA) conducting channels. The metal-oxide-semiconductor structure of the p-TFTs was composed of indium tin oxide (ITO)/SiO{sub 2}/ZnO/PVA layers. The TFT was assembled using PVA gel, which was glued to ITO substrates patterned to form source and drain electrodes. The ZnO/PVA composite film acted as an effective conducting film because of the chemisorption reaction at the film interface where free electrons can be generated. The formation of the conducting channel was also affected by V{sub G} applied to the TFT. The ZnO/PVA-based TFTs demonstrated p-channel transistor performance, shown by current-voltage (I-V) data analysis. The electrical parameters of the device were evaluated, including the on/off ratio (∼10{sup 3}), threshold voltage (V{sub th}, −1 V), and subthreshold swing (−2.2 V/dec). The PVA/ZnO-based p-TFTs were fabricated using simple and cost-effective approaches instead of doping methods.

  2. Effect of beam expansion loss in a carbon nanotube-doped PVA film on passively mode-locked erbium-doped fiber lasers with different feedback ratios

    NASA Astrophysics Data System (ADS)

    Cheng, Kuang-Nan; Chi, Yu-Chieh; Cheng, Chih-Hsien; Lin, Yung-Hsiang; Lo, Jui-Yung; Lin, Gong-Ru

    2014-10-01

    The effect of beam expansion induced divergent loss in a single-wall carbon nanotube (SWCNT) doped polyvinyl alcohol (PVA) based ultrafast saturable absorber (SA) film thickness on the passive mode-locking (PML) performances of erbium-doped fiber lasers are demonstrated. The variation on the PML pulsewidth of the EDFL is discussed by changing the SWCNT-PVA SA film thicknesses, together with adjusting the pumping power and the intra-cavity feedback ratio. An almost 6 dB increment of divergent loss when enlarging the SWCNT-PVA based SA film thickness from 30-130 µm is observed. When shrinking the SA thickness to 30 µm at the largest pumping power of 52.5 mW, the optical spectrum red-shifts to 1558.8 nm with its 3 dB spectral linewidth broadening up to 2.7 nm, while the pulse has already entered the soliton regime with multi-order Kelly sidebands aside the spectral shoulder. The soliton pulsewidth is as short as 790 fs, which is much shorter than those obtained with other thicker SWCNT doped PVA polymer film based SAs; therefore, the peak power from the output of the PML-EDFL is significantly enlarged accompanied by a completely suppressed residual continuous-wave level to achieve the largest on/off extinction ratio. The main mechanism of pulse shortening with reducing thickness of SWCNT doped PVA polymer film based SA is attributed to the limited beam expansion as well as the enlarged modulation depth, which results in shortened soliton pulsewidth with a clean dc background, and broadened spectrum with enriched Kelly sidebands. The increase of total SWCNT amount in the thicker SA inevitably causes a higher linear absorption; hence, the mode-locking threshold also rises accordingly. By enlarging pumping power from 38.5-52.5 mW, the highest ascent on pulse extinction of up to 32 dB is observed among all kinds of feedback conditions. Nevertheless, the enlargement on the extinction slightly decays with increasing the feedback ratio from 30-90%, as

  3. Geometry optimization and excited state properties of the new symmetric (E)-Stilbene derivative for application in thermostable polarizing PVA-films: A combined experimental and DFT approach

    NASA Astrophysics Data System (ADS)

    Shahab, Siyamak; Almodarresiyeh, Hora Alhosseini; Filippovich, Liudmila; Hajikolaee, Fatemeh Haji; Kumar, Rakesh; Darroudi, Mahdieh; Mashayekhi, Mahsa

    2016-09-01

    In the present work, quantum-chemical calculations used for the structural analysis of the new symmetric (E)-Stilbene derivative: (Potassium 2,2‧-((ethane-1,2-diylbis(4,1-phenylene))bis(azanediyl))diacetate) (P) (Trans isomer) using DFT/B3LYP/LanL2MB level of theory. The FT-IR and 1H NMR spectra of the compound P are presented. The electronic absorption spectrum of the P in aqueous medium was calculated using TDB3LYP/LanL2MB method. The excitation energies, electronic transitions and oscillator strengths for studied structure have also been calculated. The experimental, calculated UV/Vis and emission spectra of the P are presented and discussed. The geometry optimization of the molecule P in excited state and its electronic spectrum was carried out by the same method. In excited state the molecule P loses its symmetry and becomes unstable form. First time on the basis of polyvinyl alcohol (PVA) and the new designed structure P thermostable polarizing film absorbing at λmax = 410 nm was created. Polarizing Efficiency (PE) of obtained film is 96% at Stretching Degree (Rs) 3.0. In oriented PVA-films is the phenomenon of anisotropy of thermal conductivity (λ||/λ⊥) which is very important for development of thermostable polarizing films.

  4. Glutaraldehyde-chitosan and poly (vinyl alcohol) blends, and fluorescence of their nano-silica composite films.

    PubMed

    Hu, Huawen; Xin, John H; Hu, Hong; Chan, Allan; He, Liang

    2013-01-01

    In this study, a commercial chitosan cross-linked with glutaraldehyde (GA-chitosan) having the autofluorescent property was effectively blended with a poly (vinyl alcohol) (PVA) matrix, in the formation of a transparent and fluorescent blend film. The fluorescent efficiency of the film was enhanced with red-shifted emission band by increasing the concentrations of the GA-chitosan and decreasing the PVA crystallinity. It was found that the incorporation of silica nanoparticles could further decrease the PVA crystallinity, enhance the fluorescent efficiency, and largely redshift the emission band, as compared with the neat GA-chitosan-PVA blend film. This fluorescent property could be finely tuned by careful doping of the silica nanoparticles and change of the PVA crystallinity. These phenomena could be reasonably explained by high extent of isolation of the fluorophores, increase of the stiffness of the fluorescent conjugated planar structure, and further decrease of the PVA crystallinity. In addition, the introduction of the nano-silica could improve the water and heat resistances of the GA-chitosan-PVA based silica nanocomposites. PMID:23044137

  5. The effect of adsorption kinetics on film formation of silica/PVA suspension.

    PubMed

    Kim, Sunhyung; Sung, Jun Hee; Hur, Kangheon; Ahn, Kyung Hyun; Lee, Seung Jong

    2010-04-15

    Particle/binder/solvent systems are widely used in many applications and have long been studied. Understanding and controlling polymer adsorption in these complex material systems are important to achieve successful final performance. In this study, the effect of polymer adsorption on film formation and the relation between the microstructures of the suspension and film have been investigated by measuring the amount of polymer adsorption and the stress development during drying. In terms of mixing (or dispersion) time (t(m)), the adsorption amount (Gamma(PVA)), characteristic stress (sigma(ch)) and dried film density (rho) showed a similar behavior in the form of 1 - e(t(m)/tau) with a single characteristic time tau = 45 h, which implies that the drying process is determined by this single time constant. The porous and non-uniform microstructure of the dried film at short t(m) became close-packed and uniform with longer t(m). The polymer adsorption was found to play a key role in film formation as it introduces steric repulsion in suspension and suppresses the flocculation during solvent evaporation. It was also pointed out that enough mixing time for the saturated polymer adsorption is critical to acquire the consolidated and uniform film microstructure.

  6. Optimization and spectroscopic studies on carbon nanotubes/PVA nanocomposites

    NASA Astrophysics Data System (ADS)

    Alghunaim, Naziha Suliman

    Nanocomposite films of polyvinyl alcohol (PVA) containing constant ratio of both single and multi-wall carbon nanotubes had been obtained by dispersion techniques and were investigated by different techniques. The infrared spectrum confirmed that SWNTs and MWNTs have been covalently related OH and Csbnd C bonds within PVA. The X-ray diffraction indicated lower crystallinity after the addition of carbon nanotubes (CNTs) due to interaction between CNTs and PVA. Transmission electron microscope (TEM) illustrated that SWNTs and MWNTs have been dispersed into PVA polymeric matrix and it wrapped with PVA. The properties of PVA were enhanced by the presence of CNTs. TEM images show uniform distribution of CNTs within PVA and a few broken revealing that CNTs broke aside as opposed to being pulled out from fracture surface which suggests an interfacial bonding between CNTs and PVA. Maximum value of AC conductivity was recorded at higher frequencies. The behavior of both dielectric constant (ɛ‧) and dielectric loss (ɛ″) were decreased when frequency increased related to dipole direction within PVA films to orient toward the applied field. At higher frequencies, the decreasing trend seems nearly stable as compared with lower frequencies related to difficulty of dipole rotation.

  7. Thiazole yellow G dyed PVA films for optoelectronics: microstructrural, thermal and photophysical studies

    NASA Astrophysics Data System (ADS)

    Hebbar, Vidyashree; Bhajantri, R. F.; Naik, Jagadish; Rathod, Sunil G.

    2016-07-01

    In this paper, we report the microstructural, optical and fluorescence properties of poly(vinyl alcohol) (PVA)/Thiazole Yellow G (TY) dye composite prepared by solvent casting. The formation of change-transfer complex as a result of the interaction between the dye molecules and polymer chain is confirmed in FTIR, FT-Raman, XRD and DSC studies. SEM studies present the morphology of the samples. The UV-visible absorption spectra possess characteristic peaks of the TY dye corresponding to n-π* transition along with a characteristic peak of PVA. The composites exhibit the decreasing energy gap and increasing refractive index with an increase in wt.% of the TY dye. The fluorescence-quenching phenomena are observed in emission wavelength range of 391–406 nm upon excitation in the vicinity of absorption maxima (335 nm) with the quantum yield of 0.72 for lowest concentration of dye. The prepared composites bear high brightness, and improved thermal stability, which make them a promising material for sensors and optoelectronic applications.

  8. Preparation and Characterization of Palm Leaf Incorporated Polyvinyl Alcohol Bio Composites

    NASA Astrophysics Data System (ADS)

    Patel, Arunendra Kumar; Bajpai, Rakesh; Keller, J. M.; Saha, Abhijit

    2011-12-01

    The Bio Composites of palm leaf (PL) incorporated polyvinyl alcohol (PVA) has been prepared using solution cast technique. Structural and microhardness properties of pure PVA and PL filled PVA Bio Composites has been determined by using FTIR and Vicker's indentation techniquque respectively. The FTIR analysis reveals the presence of PL moieties in PVA, which indicates the good compatibility between PL and PVA. The values of microhardness increases in all composition of PL incorporated PVA films as compared to the pure PVA. This increment in the microhardness is attributed to the excellent binding of PL into PVA.

  9. Chitosan and polyvinyl alcohol composite films containing nitrofurazone: preparation and evaluation

    PubMed Central

    Kouchak, Maryam; Ameri, Abdolghani; Naseri, Basireh; Kargar Boldaji, Sara

    2014-01-01

    Objective(s): The aim of this study was to insert nitrofurazone in a chitosan membrane to be used as a wound dressing. Materials and Methods: Several blend films using chitosan (Cs) and polyvinyl alcohol (PVA), containing nitrofurazone were prepared by means of casting/solvent evaporating technique. Different characteristics such as mechanical properties, water vapor transmission rate (WVTR), oxygen permeability (OP), swelling ability (SW), differential scanning calorimetric (DSC), drug release profiles and antibacterial activity of the films were investigated. Results: The results showed that nitrofurazone decreased tensile strength, OP and SW of Cs films, while increased WVTR. Addition of PVA at any concentration improved mechanical properties, reduced WVTR, and increased OP and SW of nitrofurazone-loaded Cs films. The latter films showed higher activity against Pseudomonas aeruginosa than drug-free chitosan films. Conclusion: The presence of PVA improves many properties of Cs-nitrofurazone films and makes them more desirable as dressing material for burn wounds. Although nitrofurazone alone is ineffective against P. aeruginosa, it is able to increase antibacterial effect of chitosan in composite films. PMID:24592302

  10. The effect of poly vinyl alcohol (PVA) surfactant on phase formation and magnetic properties of hydrothermally synthesized CoFe2O4 nanoparticles

    NASA Astrophysics Data System (ADS)

    Jalalian, M.; Mirkazemi, S. M.; Alamolhoda, S.

    2016-12-01

    Nanoparticles of CoFe2O4 were synthesized by hydrothermal process at 190 °C with and without poly vinyl alcohol (PVA) addition using treatment durations of 1.5-6 h. The synthesized powders were characterized with X-ray diffraction (XRD), Raman spectroscopy, scanning electron microscope (SEM), Field emission scanning electron microscope (FESEM) and vibration sample magnetometer (VSM) techniques. XRD results show presence of CoFe2O4 as the main phase and Co3O4 as the lateral phase in some samples. The results show that in the samples synthesized without PVA addition considerable amount of lateral phase is present after 3 h of hydrothermal treatment while with PVA addition this phase is undetectable in the XRD patterns of the sample synthesized at the same conditions. Microstructural studies represent increasing of particle size with increasing of hydrothermal duration and formation of coarser particles with PVA addition. The highest maximum magnetization (Mmax) values in both of the samples that were synthesized with and without PVA addition are about 59 emu/g that were obtained after 4.5 h of hydrothermal treatment. Intrinsic coercive field (iHc) value of the sample without PVA addition increases from 210 to 430 Oe. While with PVA addition the iHc value changes from 83 Oe to 493 Oe. The mechanism of changes in Mmax and iHc values has been explained.

  11. Enhancement of micro structural properties of PVA doped with MWCNT’s and metal oxide nanocomposites films

    SciTech Connect

    Kumar N B, Rithin; Crasta, Vincent; Praveen, B. M.; B, Shreeprakash

    2015-06-24

    WO{sub 3} nanoparticles were prepared by using precipitation method and the multiwall Carbon nanotubes (MWCNT’s) were functionalized to make Carboxylated MWCNTs. Further, prepared WO{sub 3} and carboxylated MWCNT were doped into PVA matrix by coagulation technique and PVA nanocomposites were prepared by simple solvent casting technique. The films were characterized by XRD, FTIR spectroscopy and AFM. FTIR spectroscopy reveals the intensity of absorption of radiation at 3624.55 cm{sup −1} corresponds to the OH group of PVA. It changes in accordance with dopant concentration causing inter/intra molecular hydrogen bonding between the dopants and PVA back bone which leads to the complex formation. XRD data explores the crystalline nature of the film. It is found that for doping concentration x= 7.5 wt% the percentage crystallinity and crystallite size increases whereas micro structural strain and dislocation density decreases. An atomic force microscopy topographic analysis proves that the doped particles have an average size less than 15 nm, as confirmed by XRD data. It was found that roughness of the sample varies with dopant concentration causing variation in crystallinity.

  12. Effect of Polyvinyl Alcohol (PVA) Containing Artemether in Treatment of Cutaneous Leishmaniasis Caused by Leishmania major in BALB/c Mice

    PubMed Central

    Ebrahimisadr, Parisa; Ghaffarifar, Fatemeh; Hassan, Zuhir Mohammad; Sirousazar, Mohammad; Mohammadnejad, Fatemeh

    2014-01-01

    Background: Polyvinyl alcohol (PVA) is one of the well-known polymers, which has been used in numerous biomedical applications because of its good biocompatibility. Objectives: Due to problems made by the therapeutics already used for leishmaniasis, the aim of this study was to evaluate the effect of PVA containing artemether in treating cutaneous leishmaniasis in BALB/c mice. Materials and Methods: Aqueous solution of PVA was prepared by mixing with Double Distilled Water. After preparation of PVA, 4.33 mg of each drug (main drug artemether and control drug 14% glucantime) was added to 100 g of prepared PVA-honey solution. The solution was incubated at 37°C and the release of artemether was evaluated by measuring absorbance at 260 nm wave length. In this study for treatment of mice lesion, we used PVA containing artemether and glucantime and this method was compared with ointment treatment. Results: Mean diameters of lesions in mice treated with artemether were smaller than the control group and the differences were significant (P < 0.05). The mean lesion size of mice treated with PVA containing artemether in comparison with the group treated with ointment of artemether were smaller and the differences were significant (P < 0.05). Conclusions: PVA containing artemether is a new method for treatment of cutaneous leishmaniasis and according to the obtained results, artemether is an appropriate and effective drug, especially when used with PVA as a lesion dressing; thus we suggest that this method can be applied for the treatment of cutaneous leishmaniasis. PMID:25147717

  13. Fabrication of Poly (methyl methacrylate) and Poly(vinyl alcohol) Thin Film Capacitors on Flexible Substrates

    NASA Astrophysics Data System (ADS)

    Salim, Bindu; Meenaa Pria KNJ, Jaisree; Alagappan, M.; Kandaswamy, A.

    2015-11-01

    Flexible electronics is becoming more popular with introduction of more and more organic conducting materials and processes for making thin films. The use of polymers as gate dielectric has over ruled the usage of conventional inorganic oxides in Organic Thin Film Transistors (OTFTs) on account of its solution process ability and ease of making highly insulating thin film. In this work Capacitance is fabricated with polymeric dielectrics namely poly (methyl methacrylate) - PMMA and poly (vinyl alcohol) - PVA. The electrodes used for these capacitors are Indium Tin Oxide (ITO) and Aluminium. Capacitance value of 9.5nF/cm2 and 33.12nF/cm2 is achieved for thickness of 510 nm of PMMA and 80 nm of PVA respectively. This study on capacitance can be used for assessing the suitability of these polymers as gate insulators in OTFTs.

  14. Nanofibrillated Cellulose and Copper Nanoparticles Embedded in Polyvinyl Alcohol Films for Antimicrobial Applications

    PubMed Central

    Zhong, Tuhua; Oporto, Gloria S.; Jaczynski, Jacek; Jiang, Changle

    2015-01-01

    Our long-term goal is to develop a hybrid cellulose-copper nanoparticle material as a functional nanofiller to be incorporated in thermoplastic resins for efficiently improving their antimicrobial properties. In this study, copper nanoparticles were first synthesized through chemical reduction of cupric ions on TEMPO nanofibrillated cellulose (TNFC) template using borohydride as a copper reducing agent. The resulting hybrid material was embedded into a polyvinyl alcohol (PVA) matrix using a solvent casting method. The morphology of TNFC-copper nanoparticles was analyzed by transmission electron microscopy (TEM); spherical copper nanoparticles with average size of 9.2 ± 2.0 nm were determined. Thermogravimetric analysis and antimicrobial performance of the films were evaluated. Slight variations in thermal properties between the nanocomposite films and PVA resin were observed. Antimicrobial analysis demonstrated that one-week exposure of nonpathogenic Escherichia coli DH5α to the nanocomposite films results in up to 5-log microbial reduction. PMID:26137482

  15. Ultrasonic force microscopy on poly(vinyl alcohol)/SrTiO(3) nano-perovskites hybrid films.

    PubMed

    Marino, Salvatore; Joshi, Girish M; Lusuardi, Angelo; Cuberes, M Teresa

    2014-07-01

    Atomic Force Microscopy (AFM) and Ultrasonic Force Microscopy (UFM) have been applied to the characterization of composite samples formed by SrTiO3 (STO) nanoparticles (NPs) and polyvinyl alcohol (PVA). The morphological features of the STO NPs were much better resolved using UFM than contact-mode AFM topography. For high STO concentrations the individual STO NPs formed nanoclusters, which gathered in microaggregates. The STO aggregates, covered by PVA, exhibited no AFM frictional contrast, but were clearly distinguished from the PVA matrix using UFM. Similar aggregation was observed for NPs in the composite samples and for NPs deposited on top of a flat silicon substrate from milliQ water solution in the absence of polymer. In the hybrid films, most STO nanoparticles typically presented a lower UFM contrast than the PVA matrix, even though stiffer sample regions such as STO should give rise to a higher UFM contrast. STO NPs with intermediate contrast were characterized by an UFM halo of lower contrast at the PVA/STO interface. The results may be explained by considering that ultrasound is effectively damped on the nanometer scale at PVA/STO interfaces. According to our data, the nanoscale ultrasonic response at the PVA/STO interface plays a fundamental role in the UFM image contrast.

  16. Preparation and characterization of PVP-PVA-ZnO blend polymer nano composite films

    NASA Astrophysics Data System (ADS)

    Divya, S.; Saipriya, G.; Hemalatha, J.

    2016-05-01

    Flexible self-standing films of PVP-PVA blend composites are prepared by using ZnO as a nano filler at different concentrations. The structural, compositional, morphological and optical studies made with the help of X-ray diffraction (XRD), Fourier Transform Infra-Red spectroscopy (FTIR), Scanning electron microscope (SEM), Atomic Force Microscopy (AFM), Ultraviolet-visible spectroscopy (UV-vis) and Photoluminescence (PL) spectra are presented in this paper. The results of XRD indicate that ZnO nanoparticles are formed with hexagonal phase in the polymeric matrix. SEM images show the dispersion of ZnO nano filler in the polymer matrix. UV-vis spectra reveal that the absorption peak is centered around 235nm and 370nm for the nano composite films. The blue shift is observed with decrease in the concentration of the nano filler. PL spectra shows the excitation wavelength is given at 320nm.The emission peaks were observed at 383 nm ascribing to the electronic transitions between valence band and conduction band and the peak at 430 nm.

  17. Photoluminescence and electrical properties of polyvinyl alcohol films doped with CdS nanoparticles

    NASA Astrophysics Data System (ADS)

    Ali, Z. I.; Hosni, H. M.; Saleh, H. H.; Ghazy, O. A.

    2016-05-01

    In situ preparation of polyvinyl alcohol (PVA) films doped with cadmium sulfide (CdS) nanoparticles was conducted by gamma radiation. The films were characterized in terms of photoluminescence and electrical conductivity. The photoluminescence results indicated the existence of two emission peaks around 470 and 530 nm, which are due to electron-hole recombination of CdS nanoparticles and surface trapped emission due to the PVA capping, respectively. DC electrical conductivity ( σ DC) measurement in the temperature range from 303 up to 373 K reveals an increase in its value with increasing both Cd2+ ion molar concentration and irradiation dose. AC electrical conductivity ( σ AC) measurement over the same temperature range at an applied field frequency of 10, 100, 500 and 1000 kHz shows an increase behavior with increasing temperature, frequency, Cd2+ ion molar concentration and irradiation dose. Dielectric constant ( ɛ 1) exhibits an increase with temperature, whereas it shows reduced values with increasing frequency, Cd2+ ion molar concentration and irradiation dose. Also, the dielectric loss tangent (tan δ) follows an increasing trend with increasing temperature, Cd2+ ion molar concentration and irradiation dose while it has an opposite trend with increasing frequency. The CdS/PVA nanocomposite films behavior could be explained on the basis of formation of charge-transfer complexes (CTCs) by the CdS nanoparticles doped into the PVA matrix and the role of radiation in enhancing the charge carrier mobility of such CTCs.

  18. Preliminary characterization of genipin-cross-linked silk sericin/poly(vinyl alcohol) films as two-dimensional wound dressings for the healing of superficial wounds.

    PubMed

    Siritientong, Tippawan; Ratanavaraporn, Juthamas; Srichana, Teerapol; Aramwit, Pornanong

    2013-01-01

    The genipin-cross-linked silk sericin/poly(vinyl alcohol) (PVA) films were developed aiming to be applied as two-dimensional wound dressings for the treatment of superficial wounds. The effects of genipin cross-linking concentration on the physical and biological properties of the films were investigated. The genipin-cross-linked silk sericin/PVA films showed the increased surface density, tensile strength, and percentage of elongation, but decreased percentage of light transmission, water vapor transmission rate, and water swelling, compared to the non-cross-linked films. This explained that the cross-linking bonds between genipin and silk sericin would reduce the mobility of molecular chains within the films, resulting in the more rigid molecular structure. Silk sericin was released from the genipin-cross-linked films in a sustained manner. In addition, either L929 mouse fibroblast or HaCat keratinocyte cells showed high percentage of viability when cultured on the silk sericin/PVA films cross-linked with 0.075 and 0.1% w/v genipin. The in vivo safety test performed according to ISO 10993-6 confirmed that the genipin-cross-linked silk sericin/PVA films were safe for the medical usages. The efficacy of the films for the treatment of superficial skin wounds will be further investigated in vivo and clinically. The genipin-cross-linked silk sericin/PVA films would be promising choices of two-dimensional wound dressings for the treatment of superficial wounds.

  19. Synthesis of biphenyl derivative and its application as dichroic materials in poly (vinyl alcohol) polarizing films

    NASA Astrophysics Data System (ADS)

    Shahab, Siyamak; Almodarresiyeh, Hora A.; Filippovich, Ljudmila; Kumar, Rakesh; Darroudi, Mahdieh; Hajikolaee, Fatemeh Haji

    2016-03-01

    In the present work, first time on the basis of polyvinyl alcohol (PVA) and new designed structure (Potassium 2,2‧-([1,1‧-biphenyl]-4,4‧-diylbis(azanediyl))diacetate) (I) thermostable polarizing film was created. The structure (I) was first modeled and then synthesized and obtained polarizing film absorbing at λmax = 300 nm used for electronic applications. Polarizing efficiency (PE) of polarizing film is 96% at stretching degree (Rs) 4.0. On the basis of PVA, Potassium 2,2‧-([1,1‧-biphenyl]-4,4‧-diylbis(azanediyl))diacetate (I), Sodium 2-hydroxy-5-((2-methoxy-4-((4-sulfonatophenyl)diazenyl)phenyl)diazenyl)benzoate (II) and commercial dye (Congo Red) thermostable polarizing film for wide spectral range of spectrum (λmax = 288-561 nm) was developed. During the work it was established that oriented PVA-films is phenomenon of anisotropy of thermal conductivity (λ||/λ⊥). It is very important for creation of thermostable polarizing films. Thermal conductivity in a direction of orientation (λ||) is higher than in a direction perpendicular orientations (λ⊥). The optimization of the molecule (1) was carried out by Density Functional Theory (DFT) using B3LYP/6-311 + G* method. Electronic absorption spectrum of the molecule (I) in dimethylformamide (DMF) solution was calculated using TDB3LYP/6-311 + G* level. The nature of absorption bands in the UV spectral region was interpreted.

  20. Dielectric relaxation and ac conductivity behaviour of polyvinyl alcohol-HgSe quantum dot hybrid films

    NASA Astrophysics Data System (ADS)

    Sinha, Subhojyoti; Chatterjee, Sanat Kumar; Ghosh, Jiten; Meikap, Ajit Kumar

    2014-07-01

    Here we report a comparative study on the dielectric relaxation and ac conductivity behaviour of pure polyvinyl alcohol (PVA) and PVA-mercury selenide (HgSe) quantum dot hybrid films in the temperature range 298 K ⩽ T ⩽ 420 K and in the frequency range 100 Hz ⩽ f ⩽ 1 MHz. The prepared nanocomposite exhibits a larger dielectric constant as compared to the pure PVA. The real and imaginary parts of the dielectric constants were found to fit appreciably with the modified Cole-Cole equation, from which temperature-dependent values of the relaxation times, free charge carrier conductivity and space charge carrier conductivity were calculated. The relaxation time decreases with the quantum dot's inclusion in the PVA matrix and with an increase in temperature, whereas free charge carrier conductivity and space charge carrier conductivity increases with an increase in temperature. An increase in ac conductivity for the nanocomposites has also been observed, while the charge transport mechanism was found to follow the correlated barrier hopping model in both cases. An easy-path model with a suitable electrical equivalent circuit has been employed to analyse the temperature-dependent impedance spectra. The imaginary part of the complex electric modulus spectra exhibit an asymmetric nature and a non-Debye type of behaviour, which has been elucidated considering a generalized susceptibility function. The electric modulus spectra of the nanocomposite demonstrate a smaller amplitude and broader width, as compared to the pure PVA sample.

  1. Cellulose Nanocrystals/ZnO as a Bifunctional Reinforcing Nanocomposite for Poly(vinyl alcohol)/Chitosan Blend Films: Fabrication, Characterization and Properties

    PubMed Central

    Azizi, Susan; Ahmad, Mansor B.; Ibrahim, Nor Azowa; Hussein, Mohd Zobir; Namvar, Farideh

    2014-01-01

    In this study, cellulose nanocrystals/zinc oxide (CNCs/ZnO) nanocomposites were dispersed as bifunctional nano-sized fillers into poly(vinyl alcohol) (PVA) and chitosan (Cs) blend by a solvent casting method to prepare PVA/Cs/CNCs/ZnO bio-nanocomposites films. The morphology, thermal, mechanical and UV-vis absorption properties, as well antimicrobial effects of the bio-nanocomposite films were investigated. It demonstrated that CNCs/ZnO were compatible with PVA/Cs and dispersed homogeneously in the polymer blend matrix. CNCs/ZnO improved tensile strength and modulus of PVA/Cs significantly. Tensile strength and modulus of bio-nanocomposite films increased from 55.0 to 153.2 MPa and from 395 to 932 MPa, respectively with increasing nano-sized filler amount from 0 to 5.0 wt %. The thermal stability of PVA/Cs was also enhanced at 1.0 wt % CNCs/ZnO loading. UV light can be efficiently absorbed by incorporating ZnO nanoparticles into a PVA/Cs matrix, signifying that these bio-nanocomposite films show good UV-shielding effects. Moreover, the biocomposites films showed antibacterial activity toward the bacterial species Salmonella choleraesuis and Staphylococcus aureus. The improved physical properties obtained by incorporating CNCs/ZnO can be useful in variety uses. PMID:24945313

  2. Study of Dielectric Behavior and Charge Conduction Mechanism of Poly(Vinyl Alcohol) (PVA)-Copper (Cu) and Gold (Au) Nanocomposites as a Bio-resorbable Material for Organic Electronics

    NASA Astrophysics Data System (ADS)

    Mahendia, Suman; Goyal, Parveen Kumar; Tomar, Anil Kumar; Chahal, Rishi Pal; Kumar, Shyam

    2016-10-01

    Poly(vinyl alcohol) (PVA) embedded with varying concentrations of chemically synthesized copper (Cu) and gold (Au) nanoparticles (NPs) were prepared using ex situ sol-gel casting method. The addition of almost the same concentration of CuNPs in PVA improves the conducting properties, while that of AuNPs improves the dielectric nature of composite films. It has been found that addition of AuNPs up to ˜0.4 wt.% concentration enhaneces the capacitive nature due to the formation of small Coulomb tunneling knots as internal capacitors. The dielectric studies suggest the Maxwell-Wagner interfacial polarization as the dominant dielectric relaxation process, whereas the I- V characteristics indicate bulk limited Poole-Frenkel emission at high voltages as the dominant charge transport mechanism operating at room temperature in all specimens. These novel features lead to the conclusion that addition of a small quantity of metal nanoparticles can help tune the properties of PVA for desired applications in bio-compatible polymer-based organic electronic devices.

  3. Study of Dielectric Behavior and Charge Conduction Mechanism of Poly(Vinyl Alcohol) (PVA)-Copper (Cu) and Gold (Au) Nanocomposites as a Bio-resorbable Material for Organic Electronics

    NASA Astrophysics Data System (ADS)

    Mahendia, Suman; Goyal, Parveen Kumar; Tomar, Anil Kumar; Chahal, Rishi Pal; Kumar, Shyam

    2016-06-01

    Poly(vinyl alcohol) (PVA) embedded with varying concentrations of chemically synthesized copper (Cu) and gold (Au) nanoparticles (NPs) were prepared using ex situ sol-gel casting method. The addition of almost the same concentration of CuNPs in PVA improves the conducting properties, while that of AuNPs improves the dielectric nature of composite films. It has been found that addition of AuNPs up to ˜0.4 wt.% concentration enhaneces the capacitive nature due to the formation of small Coulomb tunneling knots as internal capacitors. The dielectric studies suggest the Maxwell-Wagner interfacial polarization as the dominant dielectric relaxation process, whereas the I-V characteristics indicate bulk limited Poole-Frenkel emission at high voltages as the dominant charge transport mechanism operating at room temperature in all specimens. These novel features lead to the conclusion that addition of a small quantity of metal nanoparticles can help tune the properties of PVA for desired applications in bio-compatible polymer-based organic electronic devices.

  4. Permanent hydrophilic modification of polypropylene and poly(vinyl alcohol) films by vacuum ultraviolet radiation

    NASA Astrophysics Data System (ADS)

    Belmonte, Guilherme Kretzmann; Charles, German; Strumia, Miriam Cristina; Weibel, Daniel Eduardo

    2016-09-01

    Polypropylene (PP) and Poly(vinyl alcohol) (PVA) both synthetics polymers but one of them biodegradable, were surface modified by vacuum ultraviolet (VUV) irradiation. After VUV irradiation in an inert nitrogen atmosphere, the films were exposed to oxygen gas. The treated films were characterized by water contact angle measurements (WCA), optical profilometry, FTIR-ATR, XPS, UPS and NEXAFS techniques. PP and PVA VUV-treated films reached superhydrophilic conditions (WCAs <10°) in about 30 min of irradiation under our experimental conditions. It was observed that when the WCAs reached about 35-40° the hydrophilicity was permanent in both polymers. These results contrasted with typical plasma treatments were a rapid hydrophobic recovery with aging time is usually observed. UPS and XPS data showed the presence of new functionalities on the PP and PVA surfaces that were assigned to COO, Cdbnd O, Csbnd O and Cdbnd C functional groups. Finally, grafting of styrene (ST) as a typical monomer was tested on PP films. It was confirmed that only in the VUV irradiated region an efficient grafting of ST or polymerized ST was found. Outside the irradiated regions no ST grafted was observed. Our results showed the potential use of VUV treatment for surface modification and processing of polymers which lack chromophores in the UV region.

  5. 21 CFR 177.1670 - Polyvinyl alcohol film.

    Code of Federal Regulations, 2014 CFR

    2014-04-01

    ... 21 Food and Drugs 3 2014-04-01 2014-04-01 false Polyvinyl alcohol film. 177.1670 Section 177.1670... Contact Surfaces § 177.1670 Polyvinyl alcohol film. Polyvinyl alcohol film may be safely used in contact..., in accordance with the following prescribed conditions: (a) The polyvinyl alcohol film is...

  6. Composite films based on biorelated agro-industrial waste and poly(vinyl alcohol). Preparation and mechanical properties characterization.

    PubMed

    Chiellini, E; Cinelli, P; Imam, S H; Mao, L

    2001-01-01

    As a part of an ongoing project on the production of composite materials based on poly(vinyl alcohol) (PVA) and polymeric materials from renewable resources, the present paper reports on the incorporation of agricultural waste materials as organic fillers in a film matrix based on PVA as continuous phase. In this study lignocellulosic fibers byproducts, derived from sugar cane (SC) and apple (AP) and orange (OR) fruit juice extraction, were cast from PVA aqueous solutions. The effect of fiber type and composition on the relative properties of cast films was evaluated and compared. OR resulted to be suitable for blending in higher amounts by weight than SC and AP. Glycerol and urea were added as plasticizing agents and were observed to be effective in giving flexible films. Additionally, cornstarch was added to further increase the composition of polymers from renewable resources in cost-effective and ecoefficient composite film formulations. The prepared films resulted sensitive to moisture and water. To reduce water sensitivity, hexamethoxymethylmelamine (HMMM) was tested as a cross-linking agent for the present composite formulations. Cross-linked films exhibited significant improvement in water-resistance that can be taken as a tuneable structural feature for customized applications. The mechanical properties of the prepared composite films (elongation at break, tensile strength, Young modulus) were found to be dependent upon the nature and content of the filler and on environmental conditions.

  7. In situ fabricated platinum—poly(vinyl alcohol) nanocomposite thin film: a highly reusable ‘dip catalyst’ for hydrogenation

    NASA Astrophysics Data System (ADS)

    Divya Madhuri, U.; Kesava Rao, V.; Hariprasad, E.; Radhakrishnan, T. P.

    2016-04-01

    A simple protocol for the in situ generation of platinum nanoparticles in a poly(vinyl alcohol) (PVA) thin film is developed. Chloroplatinic acid as well as potassium platinum(II) chloride are used as precursors and the film is fabricated by spin coating followed by mild thermal annealing. The chemical process occurring inside the film, wherein the polymer itself acts as the reducing agent, is explored through different spectroscopy and microscopy techniques. The Pt-PVA film, <100 nm thick and containing ˜1 nm size Pt nanoparticles, is shown to be a highly efficient catalyst for the reduction of methylene blue using sodium borohydride. The ease of retrieval and reuse of the thin film is highlighted by the term ‘dip catalyst’. The reaction yield, kinetics and rate are reproducible through several reuses of the same catalyst film. Turnover number (TON = number of mols of product/number of mols of catalyst) and turnover frequency (TOF = TON/reaction time) are significantly higher than those reported earlier for this reaction using metal nanocatalysts. Utility of Pt-PVA film as an efficient catalyst for other hydrogenation reactions is demonstrated.

  8. In situ fabricated platinum—poly(vinyl alcohol) nanocomposite thin film: a highly reusable ‘dip catalyst’ for hydrogenation

    NASA Astrophysics Data System (ADS)

    Divya Madhuri, U.; Kesava Rao, V.; Hariprasad, E.; Radhakrishnan, T. P.

    2016-04-01

    A simple protocol for the in situ generation of platinum nanoparticles in a poly(vinyl alcohol) (PVA) thin film is developed. Chloroplatinic acid as well as potassium platinum(II) chloride are used as precursors and the film is fabricated by spin coating followed by mild thermal annealing. The chemical process occurring inside the film, wherein the polymer itself acts as the reducing agent, is explored through different spectroscopy and microscopy techniques. The Pt–PVA film, <100 nm thick and containing ∼1 nm size Pt nanoparticles, is shown to be a highly efficient catalyst for the reduction of methylene blue using sodium borohydride. The ease of retrieval and reuse of the thin film is highlighted by the term ‘dip catalyst’. The reaction yield, kinetics and rate are reproducible through several reuses of the same catalyst film. Turnover number (TON = number of mols of product/number of mols of catalyst) and turnover frequency (TOF = TON/reaction time) are significantly higher than those reported earlier for this reaction using metal nanocatalysts. Utility of Pt–PVA film as an efficient catalyst for other hydrogenation reactions is demonstrated.

  9. Ultrasonic degradation of polymers: effect of operating parameters and intensification using additives for carboxymethyl cellulose (CMC) and polyvinyl alcohol (PVA).

    PubMed

    Mohod, Ashish V; Gogate, Parag R

    2011-05-01

    Use of ultrasound can yield polymer degradation as reflected by a significant reduction in the intrinsic viscosity or the molecular weight. The ultrasonic degradation of two water soluble polymers viz. carboxymethyl cellulose (CMC) and polyvinyl alcohol (PVA) has been studied in the present work. The effect of different operating parameters such as time of irradiation, immersion depth of horn and solution concentration has been investigated initially using laboratory scale operation followed by intensification studies using different additives such as air, sodium chloride and surfactant. Effect of scale of operation has been investigated with experiments in the available different capacity reactors with an objective of recommending a suitable type of configuration for large scale operation. The experimental results show that the viscosity of polymer solution decreased with an increase in the ultrasonic irradiation time and approached a limiting value. Use of additives such as air, sodium chloride and surfactant helps in increasing the extent of viscosity reduction. At higher frequency operation the viscosity reduction has been found to be negligible possibly attributed to less contribution of the physical effects. The viscosity reduction in the case of ultrasonic horn has been observed to be more as compared to other large capacity reactors. Kinetic analysis of the polymer degradation process has also been performed. The present work has enabled us to understand the role of the different operating parameters in deciding the extent of viscosity reduction in polymer systems and also the controlling effects of low frequency high power ultrasound with experiments on different scales of operation.

  10. Study of enhanced red emission from Sm(Sal) 3Phen ternary complexes in Poly Vinyl Alcohol film

    NASA Astrophysics Data System (ADS)

    Kaur, Gagandeep; Dwivedi, Y.; Rai, S. B.

    2010-09-01

    In the present work, dinuclear complexes of salicylic acid (Sal) and 1,10-phenanthroline (Phen) were synthesized with different concentrations of Samarium ion (Sm 3+) in Poly Vinyl Alcohol (PVA) polymer films and their structural and spectroscopic properties were investigated. Judd-Ofelt theory has been employed to estimate the several radiative parameters for SmCl 3 and Sm(Sal) 3Phen complex in PVA polymer film which are in fairly agreement between the experimental and the theoretical values supporting the J-O theory. Photoluminescence properties of the complex have been studied on 355 nm and 400 nm excitations in steady state as well as in time domain. On the basis of the UV-Vis absorption, FT-IR absorption, excitation, emission spectra and decay curves, spectroscopic properties of these films were studied and the photophysics involved was explained in terms of energy transfer and the RE encapsulation effect.

  11. Effect of Copper Sulfide Nanoparticles on the Optical and Electrical Behavior of Poly(vinyl alcohol) Films

    NASA Astrophysics Data System (ADS)

    Abdullah, Omed Gh.; Saleem, Salwan A.

    2016-11-01

    Polymer nanocomposite films based on poly(vinyl alcohol) (PVA) containing copper sulfide nanoparticles (CuS) were prepared using in situ chemical reduction and casting techniques. The synthesized nanocomposites were analyzed using x-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), scanning electron microscope, and ultraviolet-visible spectroscopy. The XRD pattern reveals that the CuS nanoparticles incorporated in the PVA showed a crystalline nature. The observed FTIR band shifts indicate the intermolecular interaction between the CuS nanoparticles and the PVA matrix. The absorbance of nanocomposite samples increased with increasing CuS concentration. The optical band gap energy was estimated using Tauc's formula and it decreased with increasing dopant concentration. The conductivity and dielectric behavior of the samples were studied over the frequency range of 300 Hz to 1 MHz in the temperature range of 30-110°C. The ac conductivity was found to increase with the increase of dopant concentration as well as frequency. Moreover, the variation of frequency exponent ( s) indicated that the conduction mechanism was the correlated barrier hopping model. The experimental results reveal that the optical and electrical performance of PVA can be enhanced dramatically by the addition of a small amount of CuS nanoparticles. This improved properties of the PVA/CuS nanocomposite suggest uses in optoelectronic devices.

  12. Effect of Copper Sulfide Nanoparticles on the Optical and Electrical Behavior of Poly(vinyl alcohol) Films

    NASA Astrophysics Data System (ADS)

    Abdullah, Omed Gh.; Saleem, Salwan A.

    2016-07-01

    Polymer nanocomposite films based on poly(vinyl alcohol) (PVA) containing copper sulfide nanoparticles (CuS) were prepared using in situ chemical reduction and casting techniques. The synthesized nanocomposites were analyzed using x-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), scanning electron microscope, and ultraviolet-visible spectroscopy. The XRD pattern reveals that the CuS nanoparticles incorporated in the PVA showed a crystalline nature. The observed FTIR band shifts indicate the intermolecular interaction between the CuS nanoparticles and the PVA matrix. The absorbance of nanocomposite samples increased with increasing CuS concentration. The optical band gap energy was estimated using Tauc's formula and it decreased with increasing dopant concentration. The conductivity and dielectric behavior of the samples were studied over the frequency range of 300 Hz to 1 MHz in the temperature range of 30-110°C. The ac conductivity was found to increase with the increase of dopant concentration as well as frequency. Moreover, the variation of frequency exponent (s) indicated that the conduction mechanism was the correlated barrier hopping model. The experimental results reveal that the optical and electrical performance of PVA can be enhanced dramatically by the addition of a small amount of CuS nanoparticles. This improved properties of the PVA/CuS nanocomposite suggest uses in optoelectronic devices.

  13. Fabrication and Characterization of Polyaniline/PVA Humidity Microsensors

    PubMed Central

    Yang, Ming-Zhi; Dai, Ching-Liang; Lin, Wei-Yi

    2011-01-01

    This study presents the fabrication and characterization of a humidity microsensor that consists of interdigitated electrodes and a sensitive film. The area of the humidity microsensor is about 2 mm2. The sensitive film is polyaniline doping polyvinyl alcohol (PVA) that is prepared by the sol-gel method, and the film has nanofiber and porous structures that help increase the sensing reaction. The commercial 0.35 μm Complimentary Metal Oxide Semiconductor (CMOS) process is used to fabricate the humidity microsensor. The sensor needs a post-CMOS process to etch the sacrificial layer and to coat the sensitive film on the interdigitated electrodes. The sensor produces a change in resistance as the polyaniline/PVA film absorbs or desorbs vapor. Experimental results show that the sensitivity of the humidity sensor is about 12.6 kΩ/%RH at 25 °C. PMID:22164067

  14. Drying of the silica/PVA suspension: effect of suspension microstructure.

    PubMed

    Kim, Sunhyung; Sung, Jun Hee; Ahn, Kyung Hyun; Lee, Seung Jong

    2009-06-01

    The particle/polymer/solvent suspension system shows complicated microstructure. When the suspension system experiences an industrial process such as coating and drying, the system experiences microstructural change. In this study, we investigated the microstructural change during the drying of a silica/polyvinyl alcohol (PVA) suspension, with an emphasis on suspension stability. We controlled the amount of PVA adsorption on the silica surface by adjusting the pH (1.5, 3.6, and 9) of the silica/PVA suspension. The amount of adsorption was measured to increase with decreasing pH, and the degree of flocculation in the silica/PVA suspension became stronger with decreasing pH. However, through the measurement of stress development during drying and the observation of film microstructure after drying, we found that the more strongly flocculated suspension became a more disperse, close-packed film after drying. By evaluating the potential energy, we could suggest the role of adsorbed polymers in structural change during the drying of the silica/PVA suspension. As pH decreases, the adsorbed polymers could bridge the particles and lead to a flocculated suspension before drying. As the solvent evaporates during drying, the adsorbed polymers introduce steric repulsion between approaching particles, leading to a change from flocculated to dispersed microstructure. This implies that the required silica/PVA film performance and the microstructure of the silica/PVA suspension can be tailored through controlling the polymer adsorption in suspension.

  15. Drying of the silica/PVA suspension: effect of suspension microstructure.

    PubMed

    Kim, Sunhyung; Sung, Jun Hee; Ahn, Kyung Hyun; Lee, Seung Jong

    2009-06-01

    The particle/polymer/solvent suspension system shows complicated microstructure. When the suspension system experiences an industrial process such as coating and drying, the system experiences microstructural change. In this study, we investigated the microstructural change during the drying of a silica/polyvinyl alcohol (PVA) suspension, with an emphasis on suspension stability. We controlled the amount of PVA adsorption on the silica surface by adjusting the pH (1.5, 3.6, and 9) of the silica/PVA suspension. The amount of adsorption was measured to increase with decreasing pH, and the degree of flocculation in the silica/PVA suspension became stronger with decreasing pH. However, through the measurement of stress development during drying and the observation of film microstructure after drying, we found that the more strongly flocculated suspension became a more disperse, close-packed film after drying. By evaluating the potential energy, we could suggest the role of adsorbed polymers in structural change during the drying of the silica/PVA suspension. As pH decreases, the adsorbed polymers could bridge the particles and lead to a flocculated suspension before drying. As the solvent evaporates during drying, the adsorbed polymers introduce steric repulsion between approaching particles, leading to a change from flocculated to dispersed microstructure. This implies that the required silica/PVA film performance and the microstructure of the silica/PVA suspension can be tailored through controlling the polymer adsorption in suspension. PMID:19466778

  16. Retardation Measurements of Infrared PVA Wave plate

    NASA Astrophysics Data System (ADS)

    Sun, Y.; Z, H.; W, D.; D, Y.; Z, Z.; S, J.

    The wave plate made of Polyvinyl Alcohol PVA plastic film has several advantages such as its lower cost and insensitivity to temperature and incidence angle so it has been used in the Solar Multi-Channel Telescope SMCT in China But the important parameter retardations of PVA wave plates in the near infrared wavelength have never been provided In this paper a convenient and high precise instrument to get the retardations of discrete wavelengths or a continuous function of wavelength in near infrared is developed In this method the retardations of wave plates have been determined through calculating the maximum and minimum of light intensity The instrument error has been shown Additionally we can get the continuous direction of wavelength retardations in the ultraviolet visible or infrared spectral in another way

  17. Preliminary Characterization of Genipin-Cross-Linked Silk Sericin/Poly(vinyl alcohol) Films as Two-Dimensional Wound Dressings for the Healing of Superficial Wounds

    PubMed Central

    Siritientong, Tippawan; Ratanavaraporn, Juthamas; Srichana, Teerapol; Aramwit, Pornanong

    2013-01-01

    The genipin-cross-linked silk sericin/poly(vinyl alcohol) (PVA) films were developed aiming to be applied as two-dimensional wound dressings for the treatment of superficial wounds. The effects of genipin cross-linking concentration on the physical and biological properties of the films were investigated. The genipin-cross-linked silk sericin/PVA films showed the increased surface density, tensile strength, and percentage of elongation, but decreased percentage of light transmission, water vapor transmission rate, and water swelling, compared to the non-cross-linked films. This explained that the cross-linking bonds between genipin and silk sericin would reduce the mobility of molecular chains within the films, resulting in the more rigid molecular structure. Silk sericin was released from the genipin-cross-linked films in a sustained manner. In addition, either L929 mouse fibroblast or HaCat keratinocyte cells showed high percentage of viability when cultured on the silk sericin/PVA films cross-linked with 0.075 and 0.1% w/v genipin. The in vivo safety test performed according to ISO 10993-6 confirmed that the genipin-cross-linked silk sericin/PVA films were safe for the medical usages. The efficacy of the films for the treatment of superficial skin wounds will be further investigated in vivo and clinically. The genipin-cross-linked silk sericin/PVA films would be promising choices of two-dimensional wound dressings for the treatment of superficial wounds. PMID:24106722

  18. 21 CFR 177.1670 - Polyvinyl alcohol film.

    Code of Federal Regulations, 2013 CFR

    2013-04-01

    ... 21 Food and Drugs 3 2013-04-01 2013-04-01 false Polyvinyl alcohol film. 177.1670 Section 177.1670... Components of Single and Repeated Use Food Contact Surfaces § 177.1670 Polyvinyl alcohol film. Polyvinyl alcohol film may be safely used in contact with food of the types identified in § 176.170(c) of...

  19. 21 CFR 177.1670 - Polyvinyl alcohol film.

    Code of Federal Regulations, 2011 CFR

    2011-04-01

    ... 21 Food and Drugs 3 2011-04-01 2011-04-01 false Polyvinyl alcohol film. 177.1670 Section 177.1670... Components of Single and Repeated Use Food Contact Surfaces § 177.1670 Polyvinyl alcohol film. Polyvinyl alcohol film may be safely used in contact with food of the types identified in § 176.170(c) of...

  20. 21 CFR 177.1670 - Polyvinyl alcohol film.

    Code of Federal Regulations, 2012 CFR

    2012-04-01

    ... 21 Food and Drugs 3 2012-04-01 2012-04-01 false Polyvinyl alcohol film. 177.1670 Section 177.1670... Components of Single and Repeated Use Food Contact Surfaces § 177.1670 Polyvinyl alcohol film. Polyvinyl alcohol film may be safely used in contact with food of the types identified in § 176.170(c) of...

  1. 21 CFR 177.1670 - Polyvinyl alcohol film.

    Code of Federal Regulations, 2010 CFR

    2010-04-01

    ... 21 Food and Drugs 3 2010-04-01 2009-04-01 true Polyvinyl alcohol film. 177.1670 Section 177.1670... Components of Single and Repeated Use Food Contact Surfaces § 177.1670 Polyvinyl alcohol film. Polyvinyl alcohol film may be safely used in contact with food of the types identified in § 176.170(c) of...

  2. Nonlinear optical characterization of the Ag nanoparticles doped in polyvinyl alcohol films

    NASA Astrophysics Data System (ADS)

    Ghanipour, Mahshad; Dorranian, Davoud

    2015-06-01

    The effect of silver nanoparticles doped in polyvinyl alcohol (PVA) on the nonlinear optical properties of composite films is studied experimentally. Samples are PVA films of 0.14 mm thickness doped with different concentrations of silver nanoparticles. Nonlinear optical properties of doped polymer films are studied experimentally employing Z-scan techniques. Experiments are performed using the second harmonic of a continuous Nd-Yag laser beam at 532 nm wavelength and 45 mW power. The effect of nonlinear refractive index of samples is obtained by measuring the profile of propagated beam through the samples and their nonlinear refractive index is found to be negative. The nonlinear absorption coefficient is calculated using open aperture Z-scan data while its nonlinear refractive index is measured using the closed aperture Z-scan data, leads to measuring the third order susceptibility |χ(3)|. Real and imaginary parts of the third-order nonlinear optical susceptibility |χ(3)| are decrease with increasing the concentration of Ag nanoparticles in the films. The values of thermo-optic coefficient are determined at different concentrations of silver nanoparticles for samples.

  3. Effect of nanosilica on optical, electric modulus and AC conductivity of polyvinyl alcohol/polyaniline films

    NASA Astrophysics Data System (ADS)

    El-Sayed, Somyia; Abel-Baset, Tarob; Elfadl, Azza Abou; Hassen, Arafa

    2015-05-01

    Nanosilica (NS) was synthesized by a sol-gel method and mixed with 0.98 polyvinyl alcohol (PVA)/0.02 polyaniline (PANI) in different amounts to produce nanocomposite films. High-resolution transmission electron microscopy (HR-TEM) revealed the average particle size of the NS to be ca. 15 nm. Scanning electron microscopy (SEM) showed that the NS was well-dispersed on the surface of the PVA/PNAI films. The Fourier transform infrared (FTIR) spectra of the samples showed a significant change in the intensity of the characteristic peak of the functional groups in the composite films with the amount of NS added. The absorbance and refractive index (n) of the composites were studied in the UV-vis range, and the optical energy band gap, Eg, and different optical parameters were calculated. The dielectric loss modulus, M″ and ac conductivity, σac, of the samples were studied within 300-425 K and 0.1 kHz-5 MHz, respectively. Two relaxation peaks were observed in the frequency dependence of the dielectric loss modulus, M″. The behavior of σac(f) for the composite films indicated that the conduction mechanism was correlated barrier hopping (CBH). The results of this work are discussed and compared with those of previous studies of similar composites.

  4. Neomycin-loaded poly(styrene sulfonic acid-co-maleic acid) (PSSA-MA)/polyvinyl alcohol (PVA) ion exchange nanofibers for wound dressing materials.

    PubMed

    Nitanan, Todsapon; Akkaramongkolporn, Prasert; Rojanarata, Theerasak; Ngawhirunpat, Tanasait; Opanasopit, Praneet

    2013-05-01

    In this study, poly(styrene sulfonic acid-co-maleic acid) (PSSA-MA) blended with polyvinyl alcohol (PVA) was electrospun and then subjected to thermal crosslinking to produce PSSA-MA/PVA ion exchange nanofiber mats. The cationic drug neomycin (0.001, 0.01, and 0.1%, w/v) was loaded onto the cationic exchange fibers. The amount of neomycin loaded and released and the cytotoxicity of the fiber mats were analyzed. In vivo wound healing tests were also performed in Wistar rats. The results indicated that the diameters of the fibers were on the nanoscale (250 ± 21 nm). The ion exchange capacity (IEC) value and the percentage of water uptake were 2.19 ± 0.1 mequiv./g-dry fibers and 268 ± 15%, respectively. The loading capacity was increased upon increasing the neomycin concentration. An initial concentration of 0.1% (w/v) neomycin (F3) showed the highest loading capacity (65.7 mg/g-dry fibers). The neomycin-loaded nanofiber mats demonstrated satisfactory antibacterial activity against both Gram-positive and Gram-negative bacteria, and an in vivo wound healing test revealed that these mats performed better than gauze and blank nanofiber mats in decreasing acute wound size during the first week after tissue damage. In conclusion, the antibacterial neomycin-loaded PSSA-MA/PVA cationic exchange nanofiber mats have the potential for use as wound dressing materials.

  5. An ultrasound tomography system with polyvinyl alcohol (PVA) moldings for coupling: in vivo results for 3-D pulse-echo imaging of the female breast.

    PubMed

    Koch, Andreas; Stiller, Florian; Lerch, Reinhard; Ermert, Helmut

    2015-02-01

    Full-angle spatial compounding (FASC) is a concept for pulse-echo imaging using an ultrasound tomography (UST) system. With FASC, resolution is increased and speckles are suppressed by averaging pulse-echo data from 360°. In vivo investigations have already shown a great potential for 2-D FASC in the female breast as well as for finger-joint imaging. However, providing a small number of images of parallel cross-sectional planes with enhanced image quality is not sufficient for diagnosis. Therefore, volume data (3-D) is needed. For this purpose, we further developed our UST add-on system to automatically rotate a motorized array (3-D probe) around the object of investigation. Full integration of external motor and ultrasound electronics control in a custom-made program allows acquisition of 3-D pulse-echo RF datasets within 10 min. In case of breast cancer imaging, this concept also enables imaging of near-thorax tissue regions which cannot be achieved by 2-D FASC. Furthermore, moldings made of polyvinyl alcohol hydrogel (PVA-H) have been developed as a new acoustic coupling concept. It has a great potential to replace the water bath technique in UST, which is a critical concept with respect to clinical investigations. In this contribution, we present in vivo results for 3-D FASC applied to imaging a female breast which has been placed in a PVA-H molding during data acquisition. An algorithm is described to compensate time-of-flight and consider refraction at the water-PVA-H molding and molding-tissue interfaces. Therefore, the mean speed of sound (SOS) for the breast tissue is estimated with an image-based method. Our results show that the PVA-H molding concept is applicable and feasible and delivers good results. 3-D FASC is superior to 2-D FASC and provides 3-D volume data at increased image quality.

  6. Surface-coated fly ash reinforced biodegradable poly(vinyl alcohol) composite films: part 2-analysis and characterization

    NASA Astrophysics Data System (ADS)

    Nath, D. C. D.; Bandyopadhyay, S.; Campbell, J.; Yu, A.; Blackburn, D.; White, C.

    2010-12-01

    Composite films of poly(vinyl alcohol) (PVA) reinforced with 5, 10, 15, 20 and 25 wt.% surface-coated fly ash by surfactant, sodium lauryl sulphate (SLS-FA) along with 1 wt.% cross-linking agent, glutaraldehyde (GLA) were prepared by aqueous casting method. The tensile strengths of the composite films were increased proportionally with the addition of SLS-FA. The maximum 75% higher strength of the composite with 20 wt.% was achieved compared to that of neat PVA. The modulus of the composites was also increased proportionally with SLS-FA and the maximum 218% reached in composite with 20 wt.%, but the strain at break was decreased with addition of SLS-FA. Changes in FTIR spectra reflect the chemical and/or physical bonding in the ternary PVA, SLS-FA and GLA component systems. In the study of surface morphology, the connectivity was visualized in SEM images along with interstitial voids. The films with SLS-FA show 53% smoother surface calculated with AFM compared to unmodified FA composite films.

  7. Design of freeze-dried Soluplus/polyvinyl alcohol-based film for the oral delivery of an insoluble drug for the pediatric use.

    PubMed

    Shamma, Rehab; Elkasabgy, Nermeen

    2016-01-01

    Spironolactone (SL) is a poorly water-soluble drug. Being poorly soluble affects its dissolution rate which in turn affects its oral bioavailability. This work aimed to prepare freeze-dried SL-Soluplus/polyvinyl alcohol (PVA) oral thin film in an attempt to enhance the drug solubility on one hand and at the same time prepare a solid dosage form convenient for the pediatric use. SL-Soluplus/PVA films were prepared using polyethylene glycol 400 (PEG 400) as a plasticizer applying the solvent-casting technique. The prepared films were evaluated for their thickness, tensile strength, and in vitro dissolution studies. Box-Behnken design (17 runs) was applied to optimize the effects of the formulation variables on the film properties. The optimized film formulation was freeze-dried after casting so as to enhance the drug dissolution. Moreover, the optimized freeze-dried film was re-characterized in vitro and evaluated in vivo in human volunteers to investigate its palatability and satisfaction. The results showed that the optimized formulation composed of 10% polymer concentration containing Soluplus:PVA (0.33:0.66) and plasticized with 30% PEG 400 possessed the highest desirability value (0.836). Freeze-drying of the optimized formulation succeeded to improve SL in vitro dissolution due to the preparation of a more porous film compared to the non-freeze-dried one. In vivo evaluation of the optimized freeze-dried film showed high satisfaction among the participating volunteers concerning the ease of administration and sensation thereafter, where all the film specimens dissolved without the need for water and no film residues remained in the mouth following film dissolution. In conclusion, freeze-dried Soluplus®/PVA-based oral thin film proved to be a successful carrier for the oral delivery of insoluble drugs like SL for pediatrics.

  8. Modification of structural and optical properties of polyvinyl alcohol/polyethylene glycol thin film by laser irradiation

    NASA Astrophysics Data System (ADS)

    Nouh, S. A.; Benthami, K.; Abutalib, M. M.

    2016-02-01

    The effect of infrared laser irradiation on the structural and the optical properties of polyvinyl alcohol/polyethylene glycol (PVA/PEG) co-polymer has been investigated. Thin films of PVA/PEG (nearly 50 µm thickness) were irradiated up to 15 J/cm2 of Ga-As laser pulses of 904 nm, 5 W power, and 200-ns pulse duration. The resultant effect of laser irradiation on the structural properties of PVA/PEG has been investigated using X-ray diffraction and Fourier transform infrared spectroscopy (FTIR). Further, the refractive index and the color difference between the exposed samples and the pristine have been studied. FTIR spectroscopy showed that the PVA/PEG samples exhibited degradation under the effect of laser irradiation up to 9 J/cm2, where crosslinking started and continued until 15 J/cm2. The refractive index had a minimum value of 1.5020 at 9 J/cm2, accompanied by a high degree of ordering and maximum value of 1.5640 at 15 J/cm2, with an increase in disordering character due to the degradation and crosslinking formation inside the sample, respectively. Moreover, the color intensity ΔE was greatly increased with increasing the laser fluence, accompanied by a significant increase in the yellow color component.

  9. Lignosulfonate as reinforcement in polyvinyl alcohol film: Mechanical properties and interaction analysis.

    PubMed

    Ye, De-zhan; Jiang, Li; Hu, Xiao-qin; Zhang, Ming-hua; Zhang, Xi

    2016-02-01

    Recently, there has been a growing research interest on renewable composite due to sustainability concerns. This work demonstrated the possibility of using eucalyptus lignosulfonate calcium (HLS) particles as reinforcement in polyvinyl alcohol (PVA) matrix. 41% and 384.7% improvement of pure PVA tensile strength and Young's modulus were achieved with incorporation of 5 wt% HLS. The above results were ascribed to specific intermolecular interactions between HLS and PVA, suggested by the increasing PVA glass transition and crystalline relaxations temperature, depression of melting point with HLS incorporation. Moreover, this interaction was quantitatively determined by q value of -62.4±10.0 in Kwei equation. Additionally, the remarkable red shift of wavenumber corresponding to hydroxyl group also indicated the formation of strong hydrogen bond in HLS/PVA blend. SEM characterization confirmed that HLS/PVA blends are at least miscible.

  10. Fabrication and photocatalytic performance of electrospun PVA/silk/TiO2 nanocomposite textile

    NASA Astrophysics Data System (ADS)

    Wu, Ming-Chung; Chan, Shun-Hsiang; Lin, Ting-Han

    2015-02-01

    Many organic/inorganic nanocomposites have been fabricated into fibrous materials using electrospinning techniques, because electrospinning processes have many attractive advantages and the ability to produce relatively large-scale continuous films. In this study, the polyvinyl alcohol (PVA)/silk/titanium dioxide (TiO2) nanocomposite self-cleaning textiles were successfully produced using electrospinning technique. After optimizing electrospinning conditions, we successfully obtained the PVA/silk/TiO2 nanocomposite fibers with average diameter of ˜220 nm and TiO2 concentration can be as high as 18.0 wt.%. For the case of the PVA/silk/TiO2 nanocomposite textile, the color of brilliant green coated on the textile surface changed from the initial green color to colorless after ultraviolet (UV) irradiation. Because of its worthy photocatalytic performance, the developed PVA/silk/TiO2 nanocomposite materials in this study will be beneficial for the design and fabrication of multifunctional fibers and textiles.

  11. Synthesis and characterization of CdSe quantum dots dispersed in PVA matrix by chemical route

    NASA Astrophysics Data System (ADS)

    Khan, Zubair M. S. H.; Ganaie, Mohsin; Khan, Shamshad A.; Husain, M.; Zulfequar, M.

    2016-05-01

    CdSe quantum dots using polyvinyl alcohol as a capping agent have been synthesized via a simple heat induced thermolysis technique. The structural analysis of CdSe/PVA thin film was studied by X-ray diffraction, which confirms crystalline nature of the prepared film. The surface morphology and particle size of the prepared sample was studied by Scanning Electron Microscopy (SEM) and Transmission Electron Microscopy (TEM). The SEM studies of CdSe/PVA thin film shows the average size of particles in the form of clusters of several quantum dots in the range of 10-20 nm. The morphology of CdSe/PVA thin film was further examined by TEM. The TEM image shows the fringes of tiny dots with average sizes of 4-7 nm. The optical properties of CdSe/PVA thin film were studied by UV-VIS absorption spectroscopy. The CdSe/PVA quantum dots follow the role of direct transition and the optical band gap is found to be 4.03 eV. From dc conductivity measurement, the observed value of activation energy was found to be 0.71 eV.

  12. Effects of O2 plasma treatment of PDMS on the deposition of electrospun PVA nanofibers

    NASA Astrophysics Data System (ADS)

    Kobayashi, Natsumi; Miki, Norihisa; Hishida, Koichi; Hotta, Atsushi

    2014-03-01

    A new polymeric nanofiber-alignment technique with the selective deposition of the nanofibers using oxygen (O2) plasma treatment on a base material for the electrospinning was introduced. Generally, without any pretreatments, electrospun fibers are deposited randomly on the collector. In this work, we focused on the O2 plasma treatment of the surface of the base material to modify the surface morphology and to add polar groups to the surface. O2 plasma-treated and untreated surface of poly (dimethylsiloxane) (PDMS) was prepared by masking a part of PDMS film by another PDMS film. The polyvinyl alcohol (PVA) fibers were then deposited onto the PDMS film. The surface structure of the PDMS film with PVA nanofibers was analyzed by scanning electron microscopy, water contact angle measurements, and X-ray photon spectroscopy. Only a few PVA nanofibers were deposited randomly on the untreated area of the PDMS film, while a number of PVA nanofibers were selectively deposited onto the O2 plasma-treated area. Intriguingly, PVA nanofibers were neatly aligned along the border of the untreated and the treated areas. The contact angle of the plasma-treated surface of PDMS decreased from 105 to 22 degree and the atomic ratio of O/Si was 1.7 times higher than that of the untreated PDMS.

  13. Effect of gamma irradiation on biopolymer composite films of poly(vinyl alcohol) and bacterial cellulose

    NASA Astrophysics Data System (ADS)

    Jipa, Iuliana Mihaela; Stroescu, Marta; Stoica-Guzun, Anicuta; Dobre, Tanase; Jinga, Sorin; Zaharescu, Traian

    2012-05-01

    Composite materials containing in different ratios poly(vinyl alcohol) (PVA), bacterial cellulose (BC) and glycerol (G) as plasticizer were obtained and exposed to different γ radiation doses using an irradiator GAMMATOR provided with 137Cs source. These films successively received up to 50 kGy absorbed doses at a dose rate of 0.4 kGy/h at room temperature. In order to study the chemical and structural changes during γ irradiation, Fourier-transformed infrared spectroscopy (FTIR), scanning electron microscopy (SEM) and UV-Vis spectroscopy were used. Water vapour permeability (WVP), Hunter colour parameters and hardness were also measured for the irradiated samples. Investigation revealed that WVP was not significantly affected by the irradiation. Colour measurements indicated a slight decrease of pure PVA films transparency and it made clear that all samples became more reddish and yellowish after irradiation. The samples hardness was not affected by the irradiation doses used. However, the results showed no drastic structural or chemical changes of the irradiated samples, which prove, in consequence, a good durability. These composite materials could be used as packaging materials for γ irradiated products.

  14. Mechanical and dielectric properties of carbon nanotubes/poly (vinyl alcohol) nanocomposites

    NASA Astrophysics Data System (ADS)

    Amrin, Sayed; Deshpande, V. D.

    2016-05-01

    In this work, two series of nanocomposites of poly(vinyl alcohol) (PVA) incorporated with multiwalled carbon nanotubes (MWNT) and carboxyl functionalized multiwalled carbon nanotubes (MWNT-COOH) were fabricated using solution-cast method and their tensile and dielectric properties were studied. Tensile tests were carried out on composite films of MWNT/PVA and MWNT-COOH/PVA for different loading levels. Results show that overall mechanical properties of the MWNT-COOH/PVA composite was greatly improved as compared to the MWNT/PVA film. The dielectric properties of nanocomposites were investigated in a frequency range from 0.1Hz to 10MHz at room temperature respectively. Compared to MWNT/PVA composites, higher dielectric constant and ac conductivity was achieved in MWNT-COOH/PVA nanocomposite, which can be well explained by the interfacial polarization effect.

  15. The effects of addition of poly(vinyl) alcohol (PVA) as a green corrosion inhibitor to the phosphate conversion coating on the anticorrosion and adhesion properties of the epoxy coating on the steel substrate

    NASA Astrophysics Data System (ADS)

    Ramezanzadeh, B.; Vakili, H.; Amini, R.

    2015-02-01

    Steel substrates were chemically treated by room temperature zinc phosphate conversion coating. Poly(vinyl) alcohol (PVA) was added to the phosphate solution as a green corrosion inhibitor. Finally, the epoxy/polyamide coating was applied on the untreated and surface treated steel samples. The effects of PVA on the morphological properties of the phosphate coating were studied by scanning electron microscope (SEM), X-ray photoelectron spectroscopy (XPS) and contact angle measuring device. The adhesion properties of the epoxy coatings applied on the surface treated samples were investigated by pull-off and cathodic delamination tests. Also, the anticorrosion properties of the epoxy coatings were studied by electrochemical impedance spectroscopy (EIS). Results showed that addition of PVA to the phosphate coating increased the population density of the phosphate crystals and decreased the phosphate grain size. The contact angle of the steel surface treated by Zn-PVA was lower than Zn treated one. The corrosion resistance of the epoxy coating was considerably increased on the steel substrate treated by zinc phosphate conversion coating containing PVA. PVA also enhanced the adhesion properties of the epoxy coating to the steel surface and decreased the cathodic delamination significantly.

  16. Boronic acid as an efficient anchor group for surface modification of solid polyvinyl alcohol.

    PubMed

    Nishiyabu, Ryuhei; Shimizu, Ai

    2016-07-28

    We report the use of boronic acid as an anchor group for surface modification of solid polyvinyl alcohol (PVA); the surfaces of PVA microparticles, films, and nanofibers were chemically modified with boronic acid-appended fluorescent dyes through boronate esterification using a simple soaking technique in a short time under ambient conditions. PMID:27311634

  17. Performance properties and antibacterial activity of crosslinked films of quaternary ammonium modified starch and poly(vinyl alcohol).

    PubMed

    Sekhavat Pour, Zahra; Makvandi, Pooyan; Ghaemy, Mousa

    2015-09-01

    There has been a growing interest in developing antibacterial polymeric materials. In the present work, novel antibacterial cross-linked blend films were prepared based on polyvinyl alcohol (PVA) and quaternary ammonium starch (ST-GTMAC) using citric acid (CA) as plasticizer and glutaraldehyde (GA) as cross-linker. The ST-GTMAC was successfully synthesized from reaction between water-soluble oxidized starch and glycidyltrimethylammonium chloride (GTMAC). The effect of ST-GTMAC, CA and GA contents on the swelling, solubility, mechanical and thermal properties of the films was investigated. It was found that incorporation of ST-GTMAC reduced UV-transmittance and provided antibacterial properties, increasing GA content increased tensile strength and decreased solubility and swelling degree of the films, while CA acted as plasticizer when its concentration was above 10 wt%. The results showed that ST-GTMAC/PVA/CA/GA film has fair antibacterial activity against Gram-positive (Staphylococcus aureus and Bacillus subtilis) and Gram-negative (Escherichia coli and Pseudomonas aeruginosa) bacteria. These results suggest that the prepared film might be used as potential antibacterial material in medical and packaging applications.

  18. Reverse osmosis performance of modified polyvinyl alcohol thin-film composite membranes

    SciTech Connect

    Lang, K.; Chowdhury, G.; Matsuura, T.; Sourirajan, S. )

    1994-08-01

    Membrane separation characteristics in the nanofiltration (NF) and reverse osmosis (RO) regions of the filtration spectrum are governed by a complex combination of both steric hindrance and surface force interactions. NF and RO membranes having surface charges show unusual selectivity behavior not predicted on the basis of physical pore size alone. Hence, practical characterizations should employ techniques to gain insight on membrane function. In this work, the separation characteristics of an anionically charged modified polyvinyl alcohol (PVA) thin-film composite membrane under different operating pressures were investigated. A qualitative measurement of the surface force interactions between solutes and membrane polymer was conducted using liquid chromatography technique. An attempt was also made to study the chlorine resistance of the composite membrane.

  19. Study of structural modification of PVA by incorporating Ag nanoparticles

    NASA Astrophysics Data System (ADS)

    Saini, Isha; Sharma, Annu; Rozra, Jyoti; Aggarwal, Sanjeev; Dhiman, Rajnish; Sharma, Pawan K.

    2016-05-01

    Nanocomposites of PVA with Ag nanoparticles dispersed in it were synthesized using solution casting method. The morphology and size distribution of Ag nanoparticles embedded in PVA matrix were obtained by transmission electron microscopy (TEM) and Field emission scanning electron microscopy (FE-SEM). Raman spectroscopy was used to examine structural changes taking place inside polyvinyl alcohol (PVA) matrix due to incorporation of Ag nanoparticle. Raman analysis indicates that Ag nanoparticles interact with PVA through H-bonding.

  20. In Situ Cross-Linking of Polyvinyl Alcohol Films

    NASA Technical Reports Server (NTRS)

    Philipp, W. H.; Shu, L. C.; May, C. E.

    1984-01-01

    Films or impregnated matrices readily made from aqueous polyvinyl alcohol solution. Controlled thickness films made by casting precise quantities of aqueous polymer solution on smooth surface, allowing water to evaporate and then removing film. Composite separators formed in similar fashion by impregnating cloth matrix with polyvinyl alcohol solution and drying composite. Insoluble thin hydrophilic membranes made from aqueous systems, and use of undesirable organic solvents not required.

  1. Studies of the plasticizing effect of different hydrophilic inorganic salts on starch/poly (vinyl alcohol) films.

    PubMed

    Jiang, Xiancai; Li, Hongmei; Luo, Yong; Zhao, Yulai; Hou, Linxi

    2016-01-01

    The effects of different inorganic salts LiCl, MgCl2·6H2O, CaCl2, and AlCl3·6H2O on the crystalline, thermal, water vapor barrier, and tensile properties of starch/PVA films were studied. The high plasticizing efficiency of all these four inorganic salts for starch/PVA film was confirmed by the obtained results. These four salts all had a good compatibility with starch/PVA within the content of 15 wt% and starch/PVA became completely miscible with the addition of 15 wt% inorganic salts. All these four salts had a strong destroying effect on the crystals of starch and PVA. Among these four salts, AlCl3·6H2O had the largest negative effect on the thermal stability of starch/PVA and LiCl had the largest improving effect on the water sorption rate of starch/PVA film. On the whole MgCl2·6H2O and CaCl2 were the more suitable plasticizer for starch/PVA film among these four inorganic salts. With the addition of 15 wt% MgCl2·6H2O and CaCl2, the elongation at break of starch/PVA film could reach to 418.83% and 434.80%, respectively.

  2. Biomimetic design and assembly of organic-inorganic composite films with simultaneously enhanced strength and toughness.

    PubMed

    Han, Jingbin; Dou, Yibo; Yan, Dongpeng; Ma, Jing; Wei, Min; Evans, David G; Duan, Xue

    2011-05-14

    Inorganic nanoplatelet reinforced polymer films were fabricated via alternate layer-by-layer assembly of layered double hydroxide (LDH) nanoplatelets with poly(vinyl alcohol) (PVA), which showed largely enhanced strength and good ductility simultaneously.

  3. Effect of glycerol on sustained insulin release from PVA hydrogels and its application in diabetes therapy

    PubMed Central

    Cai, Yunpeng; Che, Junyi; Yuan, Minglu; Shi, Xiaohong; Chen, Wei; Yuan, Wei-En

    2016-01-01

    The present study aimed to investigate the effects of glycerol on the physical properties and release of an insulin-loaded polyvinyl alcohol (PVA) hydrogel film. The insulin-loaded hydrogel composite film was produced using the freeze-thawing method, after which the in vitro swelling ratio, transmittance and insulin release, and the in vivo pharmacodynamics, of hydrogels containing various volumes of glycerol were investigated. The results demonstrated that the addition of glycerol reduced the swelling ratio and increased the softness of the PVA hydrogel film. An analysis of insulin release in vitro and of the hypoglycemic effects in rats demonstrated that the PVA hydrogel film had a sustained release of insulin and long-acting effect over 10 days. The results of the present study suggested that, as a hydrophilic plasticizer, glycerol was able to enhance the release of insulin in the early stage of release profile by enhancing the formation of water channels, although the total swelling ratio was decreased. Therefore, the insulin-loaded glycerol/PVA hydrogel film may be a promising sustained-release preparation for the treatment of diabetes. PMID:27698690

  4. Effect of glycerol on sustained insulin release from PVA hydrogels and its application in diabetes therapy

    PubMed Central

    Cai, Yunpeng; Che, Junyi; Yuan, Minglu; Shi, Xiaohong; Chen, Wei; Yuan, Wei-En

    2016-01-01

    The present study aimed to investigate the effects of glycerol on the physical properties and release of an insulin-loaded polyvinyl alcohol (PVA) hydrogel film. The insulin-loaded hydrogel composite film was produced using the freeze-thawing method, after which the in vitro swelling ratio, transmittance and insulin release, and the in vivo pharmacodynamics, of hydrogels containing various volumes of glycerol were investigated. The results demonstrated that the addition of glycerol reduced the swelling ratio and increased the softness of the PVA hydrogel film. An analysis of insulin release in vitro and of the hypoglycemic effects in rats demonstrated that the PVA hydrogel film had a sustained release of insulin and long-acting effect over 10 days. The results of the present study suggested that, as a hydrophilic plasticizer, glycerol was able to enhance the release of insulin in the early stage of release profile by enhancing the formation of water channels, although the total swelling ratio was decreased. Therefore, the insulin-loaded glycerol/PVA hydrogel film may be a promising sustained-release preparation for the treatment of diabetes.

  5. Dielectric and electric conductivity studies of PVA (Mowiol 10-98) doped with MWCNTs and WO3 nanocomposites films

    NASA Astrophysics Data System (ADS)

    Rithin Kumar, N. B.; Crasta, Vincent; Praveen, B. M.

    2016-05-01

    In this article, we report the doping of MWCNTs and WO3 nanoparticles into the PVA matrix for fabricating a novel class of PVA nanocomposite using solvent casting method. The behavioral effect of these embedded nanoparticles in PVA matrix for different doping concentrations on microstructural, dielectric and electric properties are analyzed for possible device applications. The formation of nanocomposites and their microstructural variations for different doping concentration were inspected by x-ray diffraction studies. As the doping concentration increases from x = 0 to 7.5 wt%, the DC conductivity rises from 1.0528 × 10-11 to 3.7764 × 10-9 S cm-1 and beyond the dopant concentration x > 7.5 wt% the DC conductivity was found to decrease. The frequency dependent dielectric constant decreases with an increase in dopant concentration. The values of electric modulus, AC conductivity and polarization relaxation time extracted from dielectric data spectacles an enhancement behavior in conducting property of PVA nanocomposites with increasing concentration up to x = 7.5 wt% and above x > 7.5 wt% the values found decreasing. The information regarding the surface morphology and chemical configuration of the nanocomposites are determined by using atomic force microscope (AFM), scanning electron microscope (SEM) and energy dispersive analysis of x-rays (EDS) techniques.

  6. Polyvinyl alcohol-polyvinyl pyrrolidone thin films provide local short-term release of anti-inflammatory agents post spinal cord injury.

    PubMed

    Comolli, Noelle; Donaldson, Olivia; Grantier, Nathan; Zhukareva, Victoria; Tom, Veronica J

    2012-10-01

    Spinal cord injury (SCI) triggers a large inflammatory response that results in exacerbated tissue damage. Locally delivering anti-inflammatory drugs could mitigate this secondary wave of degeneration. The mitogen-activated protein kinase family members p38 and c-Jun N-terminal kinase (JNK) play important roles in the inflammatory response and cell death. We propose that the use of polymer thin films, made of polyvinyl alcohol and polyvinyl pyrrolidone blends (PVA-PVP), can be used to provide local release of inhibitors to p38 and JNK post-SCI. Release studies performed in vitro confirmed the inhibitors could be released from the film for up to 7 days. The thin film was also tested for its surgical feasibility using a cervical contusion model of SCI in adult female rats. Films with or without the inhibitors were placed subdurally over the injury site immediately following SCI. Animals were sacrificed 5 days post-SCI and spinal cord tissue above and below the injury site was harvested. Additionally, films were removed for analysis. Scanning electron microscopy confirmed the anti-fouling properties of the PVA-PVP film. Tissue histology confirmed that the films themselves did not generate a large immune response, but they did compress the tissue slightly at its placement above the injury site. Finally, quantitative Western blot analysis determined the films loaded with p38 and JNK inhibitors delivered bioactive agents to the injury site and resulted in a significantly decreased amount of pro-cell death proteins. These data indicate that PVA-PVP films can be used to effectively deliver drugs to a SCI site.

  7. SHI irradiated PVA/Ag nanocomposites and possibility of UV blocking

    NASA Astrophysics Data System (ADS)

    Chahal, Rishi Pal; Mahendia, Suman; Tomar, A. K.; Kumar, Shyam

    2016-02-01

    The polyvinyl alcohol-silver (PVA/Ag) nanocomposites were prepared by in-situ chemical reduction method. The appearance of surface plasmon resonance (SPR) in the absorption spectrum of PVA/Ag nanocomposite films around 425 nm, confirmed the presence of Ag in the form of nanoparticles in host PVA matrix. In order to study the effect of swift heavy ions (SHI) irradiation on the optical and structural properties of these nanocomposites, the prepared films were irradiated to 90 MeV O6+ ion beam at two different fluence of 3 × 1010 and 1 × 1011 ions/cm2. The optical energy gap is found to be reduced from 4.57 eV (for PVA/Ag nanocomposite without irradiation) to 3.05 eV after irradiation at fluence of 1 × 1011 ions/cm2. The decline in the transmission of PVA/Ag nanocomposites in ultraviolet region, as a result of SHI irradiation, leads to their possible application in UV blocking devices. The induced structural re-arrangements, as a result of SHI irradiation, were revealed through the FTIR & Raman spectroscopy and found to be in strong association with the changes in optical behavior of these nanocomposites.

  8. Dielectric relaxation and alternating current conductivity of lanthanum, gadolinium, and erbium-polyvinyl alcohol doped films.

    PubMed

    Hanafy, Taha A

    2012-08-01

    Fourier transform infrared (FTIR) spectrum dielectric constant, ε', loss tangent, tan(δ), electric modulus, M*, and ac conductivity, σ(ac), of pure polyvinyl alcohol (PVA) as well as La-, Gd-, and Er-PVA doped samples have been carried out. The dielectric properties have been studied in the temperature and frequency ranges; 300-450 K and 1 kHz-4 MHz, respectively. FTIR measurements reveal that La(3+), Gd(3+), and Er(3+) ions form complex configuration within PVA structure. Two relaxation processes, namely, ρ and α were observed in pure PVA sample. The first process is due to the interfacial or Maxwell-Wagner-Sillers polarization. The second one is related to the micro-Brownian motion of the main chains. For doped PVA samples, α-relaxation process splits into α(a) and α(c). This splitting is due to the segmental motion in the amorphous (α(a)) and crystalline (α(c)) phases of PVA matrix. Electric modulus analysis was discussed to understand the mechanism of the electrical transport process. The behavior of ac conductivity for all PVA samples indicates that the conduction mechanism is correlated barrier hopping.

  9. Facile production of thermoelectric bismuth telluride thick films in the presence of polyvinyl alcohol.

    PubMed

    Lei, C; Burton, M R; Nandhakumar, I S

    2016-06-01

    Bismuth telluride is currently the best performing thermoelectric material for room temperature operations in commercial thermoelectric devices. We report the reproducible and facile production of 600 micron thick bismuth telluride (Bi2Te3) layers by low cost and room temperature pulsed and potentiostatic electrodeposition from a solution containing bismuth and tellurium dioxide in 2 M nitric acid onto nickel in the presence of polyvinyl alcohol (PVA). This was added to the electrolyte to promote thick layer formation and its effect on the structure, morphology and composition of the electrodeposits was investigated by SEM and EDX. Well adherent, uniform, compact and stoichiometric n-type Bi2Te3 films with a high Seebeck coefficient of up to -200 μV K(-1) and a high electrical conductivity of up to 400 S cm(-1) resulting in a power factor of 1.6 × 10(-3) W m(-1) K(-2) at film growth rates of 100 μm h(-1) for potentiostatic electrodeposition were obtained. The films also exhibited a well defined hexagonal structure as determined by XRD.

  10. Illumination Dependent Admittance Characteristics of Au/Zinc Acetate Doped Polyvinyl Alcohol (PVA:Zn)/n-Si Schottky Barrier Diodes (SBDs)

    NASA Astrophysics Data System (ADS)

    Taşçıoǧlu, I.; Aydemir, U.; Altındal, Ş.; Tunç, T.

    2011-12-01

    This study presents the effect of illumination on main electrical parameters of Schottky barrier diode (SBD). The admittance (capacitance-voltage (C-V) and conductance-voltage (G/ω-V)) characteristics of Au/Zinc acetate doped polyvinyl alcohol (PVA:Zn)/n-Si SBD were investigated in dark and under various illumination intensities. Experimental results demonstrate that the C-V plots give a peak due to the illumination induced interface states or electron-hole pairs at metal/semiconductor (M/S) interface. The C-2-V plots were also drawn to determine main electrical parameters such as doping concentration (ND), depletion layer width (WD) and barrier height (ΦB(C-V)) of device. In addition, the voltage dependence Rs values were obtained from C-V and G/ω-V data by using Nicollian and Brews method. In order to obtain the real diode capacitance and conductance, the high frequency (1 MHz) Cm and Gm/w values were corrected for the effect of series resistance. All these observations confirm that both C-V and G/w-V characteristics were strongly affected by illumination.

  11. A novel gellan-PVA nanofibrous scaffold for skin tissue regeneration: Fabrication and characterization.

    PubMed

    Vashisth, Priya; Nikhil, Kumar; Roy, Partha; Pruthi, Parul A; Singh, Rajesh P; Pruthi, Vikas

    2016-01-20

    In this investigation, we have introduced novel electrospun gellan based nanofibers as a hydrophilic scaffolding material for skin tissue regeneration. These nanofibers were fabricated using a blend mixture of gellan with polyvinyl alcohol (PVA). PVA reduced the repulsive force of resulting solution and lead to formation of uniform fibers with improved nanostructure. Field emission scanning electron microscopy (FESEM) confirmed the average diameter of nanofibers down to 50 nm. The infrared spectra (IR), differential scanning calorimetry (DSC) and X-ray diffraction (XRD) analysis evaluated the crosslinking, thermal stability and highly crystalline nature of gellan-PVA nanofibers, respectively. Furthermore, the cell culture studies using human dermal fibroblast (3T3L1) cells established that these gellan based nanofibrous scaffold could induce improved cell adhesion and enhanced cell growth than conventionally proposed gellan based hydrogels and dry films. Importantly, the nanofibrous scaffold are biodegradable and could be potentially used as a temporary substrate/or biomedical graft to induce skin tissue regeneration.

  12. 'One-component' ultrathin multilayer films based on poly(vinyl alcohol) as stabilizing coating for phenytoin-loaded liposomes.

    PubMed

    Zasada, Katarzyna; Łukasiewicz-Atanasov, Magdalena; Kłysik, Katarzyna; Lewandowska-Łańcucka, Joanna; Gzyl-Malcher, Barbara; Puciul-Malinowska, Agnieszka; Karewicz, Anna; Nowakowska, Maria

    2015-11-01

    Ultrathin "one-component" multilayer polymeric films for potential biomedical applications were designed based on polyvinyl alcohol,-a non-toxic, fully degradable synthetic polymer. Good uniformity of the obtained film and adequate adsorption properties of the polymeric layers were achieved by functional modification of the polymer, which involved synthesis of cationic and anionic derivatives. Synthesized polymers were characterized by FTIR, NMR spectroscopy, dynamic light scattering measurements and elemental analysis. The layer by layer assembly technique was used to build up a multilayer film and this process was followed using UV-Vis spectroscopy and ellipsometry. The morphology and thickness of the obtained multilayered film material was evaluated by atomic force microscopy (AFM). Preliminary studies on the application of the obtained multilayer film for coating of liposomal nanocarriers containing phenytoin, an antiarrhythmic drug, were performed. The coating effectively stabilizes liposomes and the effect increases with an increasing number of deposited layers until the polymeric film reaches the optimal thickness. The obtained release profiles suggest that bilayer-coated liposomes release phenytoin less rapidly than uncoated ones. The cytotoxicity studies performed for all obtained nanocarriers confirmed that none of them has negative effect on cell viability. All of the performed experiments suggest that liposomes coated with ultrathin film obtained from PVA derivatives can be attractive drug nanocarriers. PMID:26253533

  13. Electrical properties of starch-PVA biodegradable polymer blend

    NASA Astrophysics Data System (ADS)

    Chatterjee, B.; Kulshrestha, N.; Gupta, P. N.

    2015-02-01

    Solid polymer electrolyte films were prepared by adding different contents of potassium chloride (KCl) in a polymer matrix composed of two versatile biodegradable polymers: starch and polyvinyl alcohol (PVA), using the solution cast method. The complexation of the added salt (KCl) with the polymer matrix was confirmed from an x-ray diffraction study (XRD). The evolution of a smooth and uniform morphology with the increasing content of KCl was confirmed from scanning electron microscopy (SEM). The transference number measurement established ions as the dominant charge carriers in the system. The maximum ionic conductivity ˜5.44 × 10-5 S cm-1 at ambient conditions was obtained for the film with 1.5 wt% of KCl using complex impedance spectroscopy. The ionic conductivity and dielectric constant increased with the salt content, thus affirming the amplification in the number of charge carriers. The noteworthy aspect of the investigation is the observation of appreciable ionic conductivity at a relatively low salt content. Low values of activation energy obtained from temperature-dependent ionic conductivity could be favorable from the point of view of the application. Electric modulus studies confirmed the absence of electrode polarization effects in the polymer electrolyte films. The scaling of the electric modulus shows a distribution of relaxation times in the polymer electrolyte films. The study unveils the efficiency of the starch-PVA blend, with glycerol and citric acid as additives, as a hopeful material for preparing biodegradable solid polymer electrolyte films.

  14. Comparison of properties of poly(vinyl alcohol) nanocomposites containing two different clays.

    PubMed

    Chang, Jin-Hae; Ham, Miran; Kim, Jeong-Cheol

    2014-11-01

    Morphologies, thermo-optical properties, and gas barriers of poly(vinyl alcohol) (PVA) hybrid films containing two different clays are compared. Saponite (SPT) and hydrophilic bentonite (BTT) were used as the reinforcing filler in the fabrication of PVA hybrid films, which were synthesized from aqueous solutions and were solvent-cast at room temperature under vacuum, yielding 20-31-μm-thick PVA hybrid films with varying clay contents. The addition of small amounts of clay is sufficient to improve the thermal properties and gas barriers of PVA hybrid films. Even polymers with a low clay content (3-10 wt%) were found to exhibit much higher transition temperature values than pure PVA. The addition of BTT was more effective than the addition of SPT for improving the thermal properties and gas barrier in the PVA matrix. The PVA hybrid films containing 5 wt% SPT were equibiaxially stretched, with stretching ratios ranging from 150% to 250%. Clay dispersion, morphology, optical transparency, and gas permeability were then examined as a function of the equibiaxial stretching ratio. PVA hybrid films with a stretching ratio of ≥ 150% displayed homogeneously dispersed clay within the polymer matrix and exfoliated nanocomposites.

  15. Visible light photo-catalytic activity of C-PVA/TiO2 composites for degrading rhodamine B

    NASA Astrophysics Data System (ADS)

    Yang, Haigang; Zhang, Jianling; Song, Yuanqing; Xu, Shoubin; Jiang, Long; Dan, Yi

    2015-01-01

    In this article, a novel visible light (VL) active photo-catalyst, calcinated-poly (vinyl alcohol) (C-PVA)/TiO2 composites, was prepared by calcinating the films on glass substrates obtained from TiO2 sol and initially thermally treated PVA solution. The results showed that the C-PVA with conjugated C=C bonds was doped onto the surface of TiO2 and expanded the photo-response from ultraviolet spectrum of the TiO2 to VL spectrum of the composites; meanwhile, the photo-luminescence of C-PVA was quenched by TiO2, indicating charge transfer between C-PVA and TiO2. The C-PVA/TiO2 composites showed improved adsorption and photo-catalytic performances toward rhodamine B (RhB) compared to TiO2. When the mass feed ratio (P/T) of polymer (P) to TiO2 (T) increased from 1:10 to 1:2, the equilibrium adsorption ratio of C-PVA/TiO2 composites toward RhB continuously increased from 8.2 to 21.6%; while the VL photo-degradation ratio of RhB increased at first, achieving maximum value (92.2%) at P/T = 1:6, and then decreased consecutively. SEM images showed that there were lots of aggregates of TiO2 and C-PVA on the surface of the composites. Moreover, the morphologies of those aggregates were related to the value of P/T, and the dispersion of TiO2 in the C-PVA matrix was best while P/T = 1:6. The photo-catalytic activity of C-PVA/TiO2 composites was closely correlated to aggregate states of C-PVA and TiO2, while the adsorption performance was contributed to the exposed C-PVA on the surface of C-PVA/TiO2 composites.

  16. Polyvinyl alcohol membranes as alkaline battery separators

    NASA Technical Reports Server (NTRS)

    Sheibley, D. W.; Gonzalez-Sanabria, O.; Manzo, M. A.

    1982-01-01

    Polyvinly alcohol (PVA) cross-linked with aldehyde reagents yields membranes that demonstrate properties that make them suitable for use as alkaline battery separators. Film properties can be controlled by the choice of cross-linker, cross-link density and the method of cross-linking. Three methods of cross-linking and their effects on film properties are discussed. Film properties can also be modified by using a copolymer of vinyl alcohol and acrylic acid as the base for the separator and cross-linking it similarly to the PVA. Fillers can be incorporated into the films to further modify film properties. Results of separator screening tests and cell tests for several variations of PBA films are discussed.

  17. Starch-polyvinyl alcohol cast film-performance and biodegradation

    SciTech Connect

    Chen, Liang; Imam, S.H.; Stein, T.M.

    1996-10-01

    Starch-polyvinyl alcohol (PVOH) cast films were prepared in the absence of plasticizer. Their physical and biodegradable properties were examined. Moisture absorption by the films was similar to that of PVOH at low humidity and increased linearly as the relative humidity increased. The tensile strength of the films decreased with increased humidity and did not display significant improvement with increased PVOH content. Higher PVOH content improved elongation when the relative humidity was 80% or higher. Biodegradation studies revealed that the presence of PVOH in the films slowed the rate of degradation.

  18. Temperature dependent dielectric and conductivity studies of polyvinyl alcohol-ZnO nanocomposite films by impedance spectroscopy

    NASA Astrophysics Data System (ADS)

    Hemalatha, K. S.; Sriprakash, G.; Ambika Prasad, M. V. N.; Damle, R.; Rukmani, K.

    2015-10-01

    Dielectric and conductivity behaviors of nano ZnO doped polyvinyl alcohol (PVA) composites for various concentrations of dopant were investigated using impedance spectroscopy for a wide range of temperatures (303 K-423 K) and frequencies (5 Hz-30 MHZ). The dielectric properties of host polymer matrix have been improved by the addition of nano ZnO and are found to be highly temperature dependent. Anomalous dielectric behavior was observed in the frequency range of 2.5 MHz-5 MHz. Increase in dielectric permittivity and dielectric loss was observed with respect to temperature. The Cole-Cole plot could be modeled by low resistance regions in a high resistance matrix and the lowest resistance was observed for the 10 mol. % films. The imaginary part of the electric modulus showed asymmetric peaks with the relaxation following Debye nature below and non-Debye nature above the peaks. The ac conductivity is found to obey Jonscher's power law, whereas the variation of dc conductivity with temperature was found to follow Arrhenius behavior. Two different activation energy values were obtained from Arrhenius plot indicating that two conduction mechanisms are involved in the composite films. Fitting the ac conductivity data to Jonscher's law indicates that large polaron assisted tunneling is the most likely conduction mechanism in the composites. Maximum conductivity is observed at 423 K for all the samples and it is optimum for 10 mol. % ZnO doped PVA composite film. Significant increase in dc and ac conductivities in these composite films makes them a potential candidate for application in electronic devices.

  19. Temperature dependent dielectric and conductivity studies of polyvinyl alcohol-ZnO nanocomposite films by impedance spectroscopy

    SciTech Connect

    Hemalatha, K. S.; Damle, R.; Rukmani, K.; Sriprakash, G.; Ambika Prasad, M. V. N.

    2015-10-21

    Dielectric and conductivity behaviors of nano ZnO doped polyvinyl alcohol (PVA) composites for various concentrations of dopant were investigated using impedance spectroscopy for a wide range of temperatures (303 K–423 K) and frequencies (5 Hz–30 MHZ). The dielectric properties of host polymer matrix have been improved by the addition of nano ZnO and are found to be highly temperature dependent. Anomalous dielectric behavior was observed in the frequency range of 2.5 MHz–5 MHz. Increase in dielectric permittivity and dielectric loss was observed with respect to temperature. The Cole-Cole plot could be modeled by low resistance regions in a high resistance matrix and the lowest resistance was observed for the 10 mol. % films. The imaginary part of the electric modulus showed asymmetric peaks with the relaxation following Debye nature below and non-Debye nature above the peaks. The ac conductivity is found to obey Jonscher's power law, whereas the variation of dc conductivity with temperature was found to follow Arrhenius behavior. Two different activation energy values were obtained from Arrhenius plot indicating that two conduction mechanisms are involved in the composite films. Fitting the ac conductivity data to Jonscher's law indicates that large polaron assisted tunneling is the most likely conduction mechanism in the composites. Maximum conductivity is observed at 423 K for all the samples and it is optimum for 10 mol. % ZnO doped PVA composite film. Significant increase in dc and ac conductivities in these composite films makes them a potential candidate for application in electronic devices.

  20. Surfactant and Plasticizer Segregation in Thin Poly(vinyl alcohol) Films.

    PubMed

    Briddick, Arron; Li, Peixun; Hughes, Arwel; Courchay, Florence; Martinez, Alberto; Thompson, Richard L

    2016-01-26

    The vertical depth distributions of individual additive components [cetyltrimethylammonium bromide (CTAB), deuterated pentaethylene glycol monododecyl ether (d25-C12E5), and deuterated glycerol (d-glycerol)] in PVA films have been isolated and explored by ion beam analysis techniques and neutron reflectometry. The additives display an unexpectedly rich variety of surface and interfacial behaviors in spin-cast films. In separate binary films with PVA, both d-glycerol and CTAB were evenly distributed, whereas d25-C12E5 showed clear evidence for surface and interfacial segregation. The behavior of each surfactant in PVA was reversed when the plasticizer (glycerol) was also incorporated into the films. With increasing plasticizer content, the surface activity of d25-C12E5 systematically decreased, but remarkably, when glycerol and CTAB were present in PVA, the surface and interfacial activities of CTAB increased dramatically in the presence of glycerol. Quantification of the surface excess by ion beam analysis revealed that, in many cases, the adsorbed quantity far exceeded what could reasonably be explained by a single layer, thus indicating a wetting transition of the small molecules at the surface or interface of the film. It appears that the surface and interfacial behaviors are partly driven by the relative surface energies of the components, but are also significantly augmented by the incompatibility of the components. PMID:26717264

  1. Photoluminescence study of PVP capped CdS nanoparticles embedded in PVA matrix

    SciTech Connect

    Pattabi, Manjunatha . E-mail: manjupattabi@yahoo.com; Saraswathi Amma, B.; Manzoor, K.

    2007-05-03

    Photoluminescence properties of polyvinyl pyrrolidone (PVP) capped cadmium sulphide (CdS) nanoparticles embedded in polyvinyl alcohol matrix (PVA) are reported. The PVP-CdS nanoparticles are prepared by non-aqueous method wherein cadmium nitrate is used as the cadmium source and hydrogen sulphide as the sulphur source. The synthesized nanoparticles are dispersed in polyvinyl alcohol (PVA) matrix and cast as self-standing flexible (PVP-CdS)-PVA films. The nanocomposites are characterized by optical absorption spectroscopy, X-ray diffraction (XRD) and transmission electron microscopy (TEM) studies. XRD and TEM studies show the formation of cubic CdS particles with average size {approx}3-5 nm. Thermal studies, carried out to observe the changes in PVA matrix due to the incorporation of PVP-CdS nanoparticles show strong interaction between the polymer matrix and nanoparticles. The photoluminescence emission spectra of the nanocomposites show two peaks, at 502 and 636 nm, which are attributed to the band edge and surface defects respectively, of CdS nanoparticles. Effective surface capping with optimum concentration of polyvinyl pyrrolidone leads to the quenching of surface defect-related emission.

  2. Plasmon enhancement of Raman scattering and fluorescence for rhodamine 6G molecules in the porous glass and PVA films with nanoparticles of silver citrate hydrosol

    NASA Astrophysics Data System (ADS)

    Konstantinova, E. I.; Zyubin, A. U.; Slezhkin, V. A.; Samusev, I. G.; Bryukhanov, V. V.

    2016-08-01

    The study of Raman and fluorescence spectra for Rhodamine 6G molecules in a film of polyvinyl alcohol on the modified by silver nanoparticles (NPs) porous glass and without the porous glass has been done. The gain of the scattering intensity and fluorescence emission has been obtained in the presence of silver nanoparticles. The gain order was obtained as ~ 1011

  3. Ternary PVA nanocomposites containing cellulose nanocrystals from different sources and silver particles: part II.

    PubMed

    Fortunati, E; Luzi, F; Puglia, D; Terenzi, A; Vercellino, M; Visai, L; Santulli, C; Torre, L; Kenny, J M

    2013-09-12

    Cellulose nanocrystals (CNC) extracted from three different sources, namely flax, phormium, and commercial microcrystalline cellulose (MCC) have been used in a polyvinyl alcohol (PVA) matrix to produce anti-bacterial films using two different amounts of silver nanoparticles (0.1 wt% and 0.5 wt%). In general, CNC confer an effect of reinforcement to PVA film, the best values of stiffness being offered by composites produced using phormium fibres, whilst for strength those produced using flax are slightly superior. This was obtained without inducing any particular modification in transition temperatures and in the thermal degradation patterns. As regards antibacterial properties, systems with CNC from flax proved slightly better than those with CNC from phormium and substantially better than those including commercial MCC. Dynamic mechanical thermal analysis (DMTA) has only been performed on the ternary composite containing 0.1 wt% Ag, which yielded higher values of Young's modulus, and as a whole confirmed the above results.

  4. A fiber Fabry-Perot interferometer based on a PVA coating for humidity measurement

    NASA Astrophysics Data System (ADS)

    Su, Dan; Qiao, Xueguang; Rong, Qiangzhou; Sun, Hao; Zhang, Jing; Bai, Zhengyuan; Du, Yanying; Feng, Dingyi; Wang, Yupeng; Hu, Manli; Feng, Zhongyao

    2013-01-01

    A fiber Fabry-Perot interferometer (FPI) for humidity measurement based on a Polyvinyl alcohol (PVA) film is proposed and experimentally demonstrated. This FPI is fabricated by coating a PVA film on the ending face of a Single-mode fiber (SMF) to form a Fabry-Perot cavity. A well-confined interference spectrum with a free spectra range (FSR) of 15 nm is obtained. Several saturated salt solutions are employed to obtain the different humidity environments in the inclosed containers, of which the relative humidity values range from 7% RH to 91.2% RH. The proposed FPI sensor is sensitive to the humidity change, and a sensitivity of 0.07 nm/(1%) is obtained. Therefore, the characteristics of compact size, low cost and simple fabrication identify it a good candidate for environment monitoring application.

  5. Ternary PVA nanocomposites containing cellulose nanocrystals from different sources and silver particles: part II.

    PubMed

    Fortunati, E; Luzi, F; Puglia, D; Terenzi, A; Vercellino, M; Visai, L; Santulli, C; Torre, L; Kenny, J M

    2013-09-12

    Cellulose nanocrystals (CNC) extracted from three different sources, namely flax, phormium, and commercial microcrystalline cellulose (MCC) have been used in a polyvinyl alcohol (PVA) matrix to produce anti-bacterial films using two different amounts of silver nanoparticles (0.1 wt% and 0.5 wt%). In general, CNC confer an effect of reinforcement to PVA film, the best values of stiffness being offered by composites produced using phormium fibres, whilst for strength those produced using flax are slightly superior. This was obtained without inducing any particular modification in transition temperatures and in the thermal degradation patterns. As regards antibacterial properties, systems with CNC from flax proved slightly better than those with CNC from phormium and substantially better than those including commercial MCC. Dynamic mechanical thermal analysis (DMTA) has only been performed on the ternary composite containing 0.1 wt% Ag, which yielded higher values of Young's modulus, and as a whole confirmed the above results. PMID:23911522

  6. Degradation Ability of Modified Polyvinyl Alcohol Film for Coating of Fertilizer.

    PubMed

    Zou, Hong-tao; Ling, Yao; Yu, Yang; Zhang, Yu-ling; Yu, Na; Zhang, Yu-long

    2015-11-01

    Using outdoor exposure and cinnamon soil incubation test, by quality changes, infrared spectroscopy and electron microscopic scanning technology, to research the degradation ability of self-developed coated fertilizer films. The results of outdoor exposure and cinnamon soil incubation test showed that all films had certain degradation ability, and the degradation rate increased with the increase of time. Under two kinds of test conditions, the highest degradation rate could reach above 35%. The degradation ability of film citric acid/ PVA was much stronger than epoxy resin/PVA. The degradation ability of citric acid/PVA/diatomite composite film materials was further enhanced because of the addition of diatomite. The epoxy resin/PVA composite film materials, although they had certain degradability, compared to the contrast, the difference was not significant, and adding diatomite can't obviously increase the degradation rate. The results of IR spectroscopy showed that some major functional groups, such as C==O, C==C, ==C--H would be reduced after degradation, and the transmission rate also increased, which showed that the degradation of composite film materials must be happened Scanning electron microscopy showed that the surface becomes rough and uneven, and it also meant the films have some degradation. The results of IR spectroscopy and scanning electron microscopy were consistent with the results of quality change test, and could more objectively represent the degradability of film material. Modified film materials can effectively control nutrient release without causing harm to the soil environment, so it is suitable for the film materials of coated fertilizer. PMID:26978946

  7. Degradation Ability of Modified Polyvinyl Alcohol Film for Coating of Fertilizer.

    PubMed

    Zou, Hong-tao; Ling, Yao; Yu, Yang; Zhang, Yu-ling; Yu, Na; Zhang, Yu-long

    2015-11-01

    Using outdoor exposure and cinnamon soil incubation test, by quality changes, infrared spectroscopy and electron microscopic scanning technology, to research the degradation ability of self-developed coated fertilizer films. The results of outdoor exposure and cinnamon soil incubation test showed that all films had certain degradation ability, and the degradation rate increased with the increase of time. Under two kinds of test conditions, the highest degradation rate could reach above 35%. The degradation ability of film citric acid/ PVA was much stronger than epoxy resin/PVA. The degradation ability of citric acid/PVA/diatomite composite film materials was further enhanced because of the addition of diatomite. The epoxy resin/PVA composite film materials, although they had certain degradability, compared to the contrast, the difference was not significant, and adding diatomite can't obviously increase the degradation rate. The results of IR spectroscopy showed that some major functional groups, such as C==O, C==C, ==C--H would be reduced after degradation, and the transmission rate also increased, which showed that the degradation of composite film materials must be happened Scanning electron microscopy showed that the surface becomes rough and uneven, and it also meant the films have some degradation. The results of IR spectroscopy and scanning electron microscopy were consistent with the results of quality change test, and could more objectively represent the degradability of film material. Modified film materials can effectively control nutrient release without causing harm to the soil environment, so it is suitable for the film materials of coated fertilizer.

  8. Alcohol imagery and branding, and age classification of films popular in the UK

    PubMed Central

    Lyons, Ailsa; McNeill, Ann; Gilmore, Ian; Britton, John

    2011-01-01

    Background Exposure to alcohol products in feature films is a risk factor for use of alcohol by young people. This study was designed to document the extent to which alcohol imagery and brand appearances occur in popular UK films, and in relation to British Board of Film Classification (BBFC) age ratings intended to protect children and young people from harmful imagery. Methods Alcohol appearances (classified as ‘alcohol use, inferred alcohol use, other alcohol reference and alcohol brand appearances’) were measured using 5-min interval coding of 300 films, comprising the 15 highest grossing films at the UK Box Office each year over a period of 20 years from 1989 to 2008. Results At least one alcohol appearance occurred in 86% of films, at least one episode of alcohol branding in 35% and nearly a quarter (23%) of all intervals analysed contained at least one appearance of alcohol. The occurrence of ‘alcohol use and branded alcohol appearances’ was particularly high in 1989, but the frequency of these and all other appearance categories changed little in subsequent years. Most films containing alcohol appearances, including 90% of those including ‘alcohol brand appearances’, were rated as suitable for viewing by children and young people. The most frequently shown brands were American beers: Budweiser, Miller and Coors. Alcohol appearances were similarly frequent in films originating from the UK, as from the USA. Conclusion Alcohol imagery is extremely common in all films popular in the UK, irrespective of BBFC age classification. Given the relationship between exposure to alcohol imagery in films and use of alcohol by young people, we suggest that alcohol imagery should be afforded greater consideration in determining the suitability of films for viewing by children and young people. PMID:22039199

  9. Morphological influence of cellulose nanoparticles (CNs) from cottonseed hulls on rheological properties of polyvinyl alcohol/CN suspensions.

    PubMed

    Zhou, Ling; He, Hui; Li, Mei-Chun; Song, Kunlin; Cheng, H N; Wu, Qinglin

    2016-11-20

    The present work describes the isolation of cellulose nanoparticles (CNs) with different morphologies and their influence on rheological properties of CN and CN-poly (vinyl alcohol) (PVA) suspensions. Cottonseed hulls were used for the first time to extract three types of CNs, including fibrous cellulose nanofibers, rod-like cellulose nanocrystals and spherical cellulose nanoparticles through mechanical and chemical methods. Rheology results showed that the rheological behavior of the CN suspensions was strongly dependent on CN concentration and particle morphology. For PVA/CN systems, concentration of PVA/CN suspension, morphology of CNs, and weight ratio of CN to PVA were three main factors that influenced their rheology behaviors. This research reveals the importance of CN morphology and composition concentration on the rheological properties of PVA/CN, providing new insight in preparing high performance hydrogels, fibers and films base on PVA/CN suspension systems. PMID:27561516

  10. Livestock air treatment using PVA-coated powdered activated carbon biofilter

    Technology Transfer Automated Retrieval System (TEKTRAN)

    The efficacy of polyvinyl alcohol (PVA) biofilters was studied using bench-scale biofilters and air from aerobically-treated swine manure. The PVA-coated powdered activated carbon particles showed excellent properties as a biofiltration medium: water holding capacity of 1.39 g H2O/g-dry PVA; wet por...

  11. Effect of particle size and inter-electrode distance on the field-emission properties of nanocrystalline CdS thin films grown in a polymer matrix by chemical bath deposition

    NASA Astrophysics Data System (ADS)

    Ghosh, P. K.; Jana, S.; Maity, U. N.; Chattopadhyay, K. K.

    2006-10-01

    The field-emission property of transparent nanocrystalline CdS thin films, grown by chemical bath deposition (CBD) within the pores of polyvinyl alcohol (PVA) on Si and glass substrates, has been studied. X-ray diffraction and transmission electron microscopy studies confirmed the nanocrystalline nature of the CdS particles with sizes lying in the range 6-12 nm. The Fowler-Nordhiem plots of the emission current from the nano-CdS/PVA thin films are almost straight line. The turn-on fields of the grown nano-CdS/PVA thin films are found to be in the range of 3.6-6.6 V/μm. The turn-on field decreases with the decrease of particle size. Only PVA thin film and bulk CdS/PVA composite thin film grown on Si substrates have not showed field-emission property under the same conditions.

  12. Covalently-layers of PVA and PAA and in situ formed Ag nanoparticles as versatile antimicrobial surfaces.

    PubMed

    Fragal, Vanessa H; Cellet, Thelma S P; Pereira, Guilherme M; Fragal, Elizângela H; Costa, Marco Antonio; Nakamura, Celso Vataru; Asefa, Tewodros; Rubira, Adley F; Silva, Rafael

    2016-10-01

    The in situ synthesis of silver nanoparticles (AgNPs) within covalently-modified poly(ethylene terephthalate) (PET) films possessing ultra-thin layer of poly(vinyl alcohol) (PVA) and poly(acrylic acid) (PAA) is successfully demonstrated. The resulting polymeric films are shown to exhibit antimicrobial activities toward Gram-positive (Staphylococcus aureus) and Gram-negative (Escherichia coli) bacteria and fungus (Candida albicans). To make the films, first PET surfaces were subject to photo-oxidation and subsequent solid-state grafting to attach a PVA layer, followed by a PAA layer. To synthesize the AgNPs inside the films, the PVA and PAA-modified PET was soaked in AgNO3 solution and the polymeric film was modified with the Ag(+) ions via Ag(+)-carboxylate interaction, and then the Ag(+) ions-containing polymer film was subject to either photo-reduction or thermal reduction processes. The PVA and PAA thin layers attached by covalent bonds to the PET surface uniquely promoted not only the in situ synthesis but also the stabilization of AgNPs. The formation of the AgNPs was confirmed by UV-vis spectroscopy or by monitoring the surface plasmon resonance (SPR) peak associated with AgNPs. The resulting PVA and PAA ultrathin layers modified and AgNPs containing PET served as bactericide and fungicide, inhibiting the growth of bacteria and fungi on the surfaces. Given PET's versatility and common use in many commercial processes, the method can be used for producing plastic surfaces with versatile antimicrobial and antibacterial properties. PMID:27196366

  13. Sporocidic properties of poly(vinyl alcohol)/silver nanoparticles/TEOS thin hybrid films.

    PubMed

    Pencheva, Daniela; Bryaskova, Rayna; Lad, Umesh; Kale, Girish M; Kantardjiev, T

    2012-06-01

    The sporocidic activity of hybrid materials based on PVA/AgNps/TEOS thin films has been investigated. Deep Agar Method has been applied to study the sporocidic properties of these hybrid materials with different silver concentrations. This method has been used because of the lack of standard methods for testing the sporocidic activity in such materials and due to the specific characteristics of bacterial spore. Clear and pronounced presence of sporocidic activity of the hybrid materials towards spores of control strains Bacillus subtilis ATCC 6633 and Geobacillus stearothermophilus ATCC 7953 has been established. The use of chromatographic paper disks impregnated with PVA/AgNps/TEOS showed the advantages in testing the biological properties of the hybrid material in comparison to the disks obtained by directly cutting the PVA/AgNps/TEOS films. The highest sporocidic activity, although with small deviation of 0.5-1.0 mm, was established at the PVA/AgNps/TEOS hybrid films with concentration of silver precursor 9.2 mg/mL and 18.3 mg/mL. The experiments were performed with the aim to reveal the opportunities for a practical application of the material.

  14. Effect of γ irradiation on poly(vinyl alcohol) and bacterial cellulose composites used as packaging materials

    NASA Astrophysics Data System (ADS)

    Stoica-Guzun, Anicuta; Stroescu, Marta; Jipa, Iuliana; Dobre, Loredana; Zaharescu, Traian

    2013-03-01

    The aim of this paper is to present the influence of bacterial cellulose microfibrils and γ-radiation dose on poly(vinyl alcohol) (PVA)-bacterial cellulose (BC) composites. Two composite materials were obtained: the first one from PVA aqueous solution 4% and 5% wet bacterial cellulose and the second from the same PVA solution and 10% wet bacterial cellulose. In terms of PVA/dry BC ratios (w/w) for these films the ratios are 1/0.025 and 1/0.050. The obtained composite materials were characterized by infrared spectroscopy with Fourier transform (FT-IR) and UV-vis spectroscopy in order to evaluate the irradiation effect on their stability. The swelling behavior of the polymeric composites was also studied. The composite materials were compared with a film of pure PVA and a dry BC membrane.

  15. Surface-coated fly ash used as filler in biodegradable poly(vinyl alcohol) composite films: Part 1—The modification process

    NASA Astrophysics Data System (ADS)

    Nath, D. C. D.; Bandyopadhyay, S.; Gupta, S.; Yu, A.; Blackburn, D.; White, C.

    2010-02-01

    The surfaces of fly ash (FA) particles were modified by surfactant, sodium lauryl sulphate (SLS) and used in fabrication of composite films with polyvinyl alcohol (PVA). Both unmodified fly ash (FA) and modified fly ash (SLS-FA) samples were examined using a range of analytical tools including X-ray fluorescence spectroscopy (XRF), scanning electron microscopy (SEM), transmission electron microscopy (TEM), Fourier transform infrared (FTIR) and X-ray photoelectron spectroscopy (XPS). The distribution patterns of SLS-FA particles were shifted to the higher regions compared to FA by adding 1.2-4.2 μm in the ranges between 2 and 25 μm, whereas the modification process reduced the size of the particles over 25 μm due to grinding during the activation process. The increased 1.2-4.2 μm in average can be considered the thickness of the surfactant on the SLS-FA surface. On the oxides based chemical analysis by XRF, the compositions were almost unchanged. SEM and TEM were visualised the irregular sizes morphology mostly spherical of the particles, although it is impossible to capture the images of exactly same particles in modified and unmodified forms. The composite films reinforced with SLS-FA showed 33% higher strength than those of FA filled films. The enhancement of tensile strength attributed from the level of physical bonding between SLS-FA and PVA surfaces.

  16. Preparation and Characterisation of Pva Doped with Beta Alanine

    NASA Astrophysics Data System (ADS)

    Bhuvaneshwari, R.; Karthikeyan, S.; Rajeswari, N.; Selvasekarapandian, S.; Sanjeeviraja, C.

    2013-07-01

    Pure PVA has been doped with different amount of β - alanine. Film has been prepared by Solution Casting Technique using water as a solvent. The Complex formation between the PVA and β - alanine has been confirmed by FTIR. The Pure PVA conductivity is in the order 10-10 Scm-1 at ambient temperature. The conductivity has been found to increase to the order 10-6 when doped with 10% β - alanine. In this paper characterization of a PVA doped with β-ala has been studied using XRD, FTIR, AC impedance analysis and the results are reported.

  17. UV irradiated PVA-Ag nanocomposites for optical applications

    NASA Astrophysics Data System (ADS)

    Chahal, Rishi Pal; Mahendia, Suman; Tomar, A. K.; Kumar, Shyam

    2015-07-01

    The present paper is focused on the in-situ prepared Poly (vinyl alcohol)-Silver (PVA-Ag) nanocomposites and tailoring their optical properties by means of UV irradiation in such a way that these can be used for anti-reflective coatings and bandpass filters. The reflectance from these irradiated nanocomposites has been found to decrease leading to the increase in refractive index (RI), with increasing UV exposure time, in the entire visible region. Decrease in optical energy gap of PVA film from 4.92 to 4.57 eV on doping with Ag nanoparticles has been observed which reduces further to 4.1 eV on exposure to UV radiations for 300 min. This decrease in optical energy gap can be correlated to the formation of charge transfer complexes within the base polymer network on embedding Ag nanoparticles, which further enhances with increasing exposure time. Such complexes may also be responsible for increased molecular density of the composite films which corresponds to decrease in reflectance corroborating the observed results.

  18. Studies on PVA pectin cryogels containing crosslinked enzyme aggregates of keratinase.

    PubMed

    Martínez, Yanina N; Cavello, Ivana; Cavalitto, Sebastián; Illanes, Andres; Castro, Guillermo R

    2014-05-01

    Polyvinyl alcohol-pectin (PVA-P) films containing enrofloxacin and keratinase were developed to treat wounds and scars produced by burns and skin injuries. However, in order to prevent enzyme inactivation at the interface between the patch and the scars, crosslinked enzyme aggregates (CLEAs) from a crude extract of keratinase produced by Paecilomyces lilacinus (LPSC#876) were synthesized by precipitation with acetone and crosslinking with glutaraldehyde. Soluble vs. CLEA keratinase (K-CLEA) activities were tested in 59% (v/v) hydrophobic (isobutanol and n-hexane) and hydrophilic (acetone and dimethylsulfoxide) solvents mixtures. K-CLEA activity was 1.4, 1.7 and 6.6 times higher in acetone, n-hexane and isobutanol than the soluble enzyme at 37 °C after 1 h of incubation, respectively. K-CLEA showed at least 45% of enzyme residual activity in the 40-65 °C range, meanwhile the soluble biocatalyst was fully inactivated at 65 °C after 1h incubation. Also, the soluble enzyme was completely inactivated after 12 h at pH 7.4 and 45 °C, even though K-CLEA retained full activity. The soluble keratinase was completely inactivated at 37 °C after storage in buffer solution (pH 7.4) for 2 months, meanwhile K-CLEAs kept 51% of their activity. K-CLEA loaded into polyvinyl alcohol (PVA) and PVA-P cryogels showed six times lower release rate compared to the soluble keratinase at skin pH (5.5). Small angle X-ray scattering (SAXS) analysis showed that K-CLEA bound to pectin rather than to PVA in the PVA-P matrix.

  19. Aggregation and excitation trapping of 3,3‧-diethyl-9-methylthiacarbocyanine iodide in disordered and uniaxially oriented polymer films

    NASA Astrophysics Data System (ADS)

    Synak, Anna; Bojarski, Piotr; Gryczyński, Ignacy; Gryczyński, Zygmunt; Rangełowa-Jankowska, Simeonika; Kułak, Leszek; Sadownik, Michał; Kubicki, Aleksander; Koprowska, Ewa

    2008-08-01

    Photophysical properties of 3,3'-diethyl-9-methylthiacarbocyanine iodide (MDTCI) in disordered and uniaxially stretched poly(vinyl alcohol) films (PVA) are reported at high dye concentration. Ground-state formation of fluorescent MDTCI aggregates at high concentration was observed in unstretched and stretched PVA films using steady-state and time-resolved spectroscopic methods. It was found that fluorescence of MDTCI aggregates is almost totally depolarized in disordered matrix, but it remains partly polarized in the stretched PVA film despite energy transfer from monomers. The differences between spectral properties of aggregates in both matrices may result from partial orientation of aggregate transition moment and its immobilization in polymer cage.

  20. Effect of UV irradiation on optical, mechanical and microstructural properties of PVA/NaAlg blends

    NASA Astrophysics Data System (ADS)

    Sheela, T.; Bhajantri, R. F.; Ravindrachary, V.; Rathod, Sunil G.; Pujari, P. K.; Poojary, Boja; Somashekar, R.

    2014-10-01

    Poly(vinyl alcohol) (PVA)/Sodium alginate (NaAlg) blend films with 60:40 wt% were prepared by solution casting method and subjected to UV irradiation for different intervals of time. The optical, mechanical and morphological properties of the blend films were modified after UV irradiation. The FTIR and FT-Raman results show the chemical interaction between PVA and NaAlg. The UV-vis absorption peak at 278 nm shifts slightly towards longer wavelength and the absorption increases with irradiation time, indicate the increase in crosslinking network. The XRD results show an increase in amorphous nature with increase in UV irradiation time. The DSC/TGA results show a single glass transition temperature (Tg), which confirm that the blends are completely miscible and thermally stable up to 250 °C. The Young's modulus, tensile strength and stiffness of the blend films increase with increase in UV irradiation time. The SEM images confirm that the surface of 48 h UV irradiated PVA:NaAlg blend is more photo-resistant than unirradiated blend.

  1. Anodic deprotonation of polyaniline films in alcohol solutions

    SciTech Connect

    Susumu Kuwabata, Nobuo Kihira ); Hiroshi Yoneyama

    1993-05-01

    Polyaniline films prepared by electrochemical oxidation of aniline possess high redox activities both in aqueous acidic and in nonaqueous solutions. The high durability of the film against the redox cycling opens applications of this material to electrochromic and electronic devices and cathode-active materials of rechargeable lithium batteries. Polyaniline films immersed in alcohol solutions such as methanol, ethanol, 1-propanol, and 2-propanol are deprotonated by applying anodic potentials. The potential at which the deprotonation reaction is induced to occur is the most negative at methanol among the above four kinds of alcohols used, and ethanol, 1-propanol, and 2-propanol follow in this order. This finding is quantitatively discussed in terms of the difference of the affinity of the solvent for the protonated polyaniline. An equation to predict the potential at which the conductance of polyaniline is decreased to one-half of the highest conductance by the deprotonation is derived, and the validity of the equation is verified for results obtained both in aqueous solutions of different pH values and in the above alcohol solutions. 26 refs., 9 figs.

  2. Controlling the Optical Creation of Gold Nanoparticles in a PVA Matrix by Direct Laser Writing

    NASA Astrophysics Data System (ADS)

    Ritacco, T.; Ricciardi, L.; La Deda, M.; Giocondo, M.

    2016-02-01

    We report about the study on the physical features of gold nano-particles (GNPs) created by 2-photons photo-reduction Direct Laser Writing in a Poly-Vinyl Alcohol (PVA) matrix doped with HAuCl4. We drop cast a film of the PVA+ HAuCl4 onto a glass substrate, in which we create 1D gratings made by stripes of GNPs with a single laser sweep. We show that the stripe width increases with the laser power and the exposure time. We also analyse the influence of the exposure time over the created nano-particles size distribution and density and we show that by suitably adjusting the exposure time it is possible to maximize the frequency of a given diameter. By comparing the experimental results with a polymerization "voxel" model, we are able to evaluate the effective cross section for 2- photons absorption of our material.

  3. Impedance studies of a green blend polymer electrolyte based on PVA and Aloe-vera

    NASA Astrophysics Data System (ADS)

    Selvalakshmi, S.; Mathavan, T.; Vijaya, N.; Selvasekarapandian, Premalatha, M.; Monisha, S.

    2016-05-01

    The development of polymer electrolyte materials for energy generating and energy storage devices is a challenge today. A new type of blended green electrolyte based on Poly-vinyl alcohol (PVA) and Aloe-vera has been prepared by solution casting technique. The blending of polymers may lead to the increase in stability due to one polymer portraying itself as a mechanical stiffener and the other as a gelled matrix supported by the other. The prepared blend electrolytes were subjected to Ac impedance studies. It has been found out that the polymer film in which 1 gm of PVA was dissolved in 40 ml of Aloe-vera extract exhibits highest conductivity and its value is 3.08 × 10-4 S cm-1.

  4. Synthesis of Nanocomposites of Polyvinyl Alcohol with Silver Nanoparticles and Their Use

    NASA Astrophysics Data System (ADS)

    Bhat, N. V.; Karmakar, N. S.; Kothari, D. C.

    2013-08-01

    Composites of polyvinyl alcohol (PVA) containing silver nanoparticles were prepared using in situ synthesis of nanoparticles. Structure and properties of these composites were investigated using UV-Vis spectroscopy, XRD, DSC, SEM and AFM. The studies show that PVA can reduce the AgNO3 to yield silver nanoparticles and in the process forms bonds with PVA chains. The anti-bacterial properties of these films were studied by qualitative as well as quantitative methods which gave the values of 98% for gram positive and 89% for gram negative bacteria.

  5. Plasma functionalization of poly(vinyl alcohol) hydrogel for cell adhesion enhancement

    PubMed Central

    Ino, Julia M.; Chevallier, Pascale; Letourneur, Didier; Mantovani, Diego; Le Visage, Catherine

    2013-01-01

    Tailoring the interface interactions between a biomaterial and the surrounding tissue is a capital aspect to consider for the design of medical devices. Poly(vinyl alcohol) (PVA) hydrogels present suitable mechanical properties for various biological substitutes, however the lack of cell adhesion on their surface is often a problem. The common approach is to incorporate biomolecules, either by blending or coupling. But these modifications disrupt PVA intra- and intermolecular interactions leading therefore to a loss of its original mechanical properties. In this work, surface modification by glow discharge plasma, technique known to modify only the surface without altering the bulk properties, has been investigated to promote cell attachment on PVA substrates. N2/H2 microwave plasma treatment has been performed, and the chemical composition of PVA surface has been investigated. X-ray photoelectron and Fourier transform infrared analyses on the plasma-treated films revealed the presence of carbonyl and nitrogen species, including amine and amide groups, while the main structure of PVA was unchanged. Plasma modification induced an increase in the PVA surface wettability with no significant change in surface roughness. In contrast to untreated PVA, plasma-modified films allowed successful culture of mouse fibroblasts and human endothelial cells. These results evidenced that the grafting was stable after rehydration and that it displayed cell adhesive properties. Thus plasma amination of PVA is a promising approach to improve cell behavior on contact with synthetic hydrogels for tissue engineering. PMID:23989063

  6. Controllable layer-by-layer assembly of PVA and phenylboronic acid-derivatized chitosan.

    PubMed

    Zhang, Dan; Yu, Guanghua; Long, Zhu; Yang, Guihua; Wang, Bin

    2016-04-20

    Phenylboronic acid-derivatized chitosan (chitosan-PBA) were prepared by grafting small molecules bearing phenylboronic acid groups onto chitosan with N-hydroxysuccinimide (NHS) and N-(3-dimethylaminopropyl)-N'-ethylcarbodiimide hydrochloride (EDC) as a coupling reagent pair. Self-assembly multilayer thin films of chitosan-PBA and poly(vinyl alcohol) were subsequently produced under pH control on supporting surfaces, either a silicon wafer or polystyrene latex particles. The driving force of the self-assembly was the ester formation of phenylboronic acid containing polymers with PVA, which can be "turned off" by simple pH control. PMID:26876848

  7. Electromechanical behavior of polyaniline/poly (vinyl alcohol) blend films under static, dynamic and time-dependent strains

    NASA Astrophysics Data System (ADS)

    Akhilesan, S.; Lakshmana Rao, C.; Varughese, S.

    2014-07-01

    We report on the experimentally observed electrical conductivity enhancement in polyaniline/poly (vinyl alcohol) blend films under uniaxial tensile loading. Polyaniline (PANI) is an intrinsically conducting polymer, which does not form stretchable free-standing films easily and hence its electromechanical characterization is a challenge. Blending of PANI with other insulating polymers is a good choice to overcome the processability problem. We report the electromechanical response of solution blended and HCl doped PANI/PVA blends subjected to uniaxial, static, dynamic and time-dependent tensile loading. The demonstrated viscoelastic and morphological contributions of the component polymers to the electrical conductivity behavior in these blends could lead to interesting applications in strain sensors and flexible electronics. The reversibility of the electromechanical response under dynamic strain is found to increase in blends with higher PANI content. Time-dependent conductivity studies during mechanical stress relaxation reveal that variations in the micro-domain ordering and the relative relaxation rate of the individual polymer phases can give rise to interesting electrical conductivity changes in PANI blends. From morphological and electrical conductivity studies, we show that PANI undergoes primary and secondary agglomeration behavior in these blends that contributes to the changes in conductivity behavior during the deformation. A 3D variable range hopping (VRH) process, which uses a deformable core and shell concept based on blend morphology analysis, is used to explain the experimentally observed electromechanical behavior.

  8. Processing and characterization of chitosan/PVA and methylcellulose porous scaffolds for tissue engineering.

    PubMed

    Kanimozhi, K; Khaleel Basha, S; Sugantha Kumari, V

    2016-04-01

    Biomimetic porous scaffold chitosan/poly(vinyl alcohol) CS/PVA containing various amounts of methylcellulose (MC) (25%, 50% and 75%) incorporated in CS/PVA blend was successfully produced by a freeze drying method in the present study. The composite porous scaffold membranes were characterized by infrared spectroscopy (FTIR), X-ray diffraction (XRD), thermogravimetric analysis (TGA), differential scanning calorimetry (DSC), scanning electron microscopy (SEM), swelling degree, porosity, degradation of films in Hank's solution and the mechanical properties. Besides these characterizations, the antibacterial activity of the prepared scaffolds was tested, toward the bacterial species Staphylococcus aureus (S.aureus) and Escherichia coli (E.coli). FTIR, XRD and DSC demonstrated that there was strong intermolecular hydrogen bonding between the molecules of CS/PVA and MC. The crystalline microstructure of the scaffold membranes was not well developed. SEM images showed that the morphology and diameter of the scaffolds were mainly affected by the weight ratio of MC. By increasing the MC content in the hybrid scaffolds, their swelling capacity and porosity increased. The mechanical properties of these scaffolds in dry and swollen state were greatly improved with high swelling ratio. The elasticity of films was also significantly improved by the incorporation of MC, and the scaffolds could also bear a relative high tensile strength. These findings suggested that the developed scaffold possess the prerequisites and can be used as a scaffold for tissue engineering. PMID:26838875

  9. Thermal, mechanical and dielectric properties of poly(vinyl alcohol)/graphene oxide composites

    NASA Astrophysics Data System (ADS)

    Rathod, Sunil G.; Bhajantri, R. F.; Ravindrachary, V.; Pujari, P. K.; Sheela, T.; Naik, Jagadish

    2014-04-01

    In this work the composite films of poly(vinyl alcohol) (PVA) doped with functionalized Graphene Oxide (GO) were prepared by solution casting method. The films were characterized using FT-IR, DSC, XRD, mechanical properties and dielectric studies at room temperature. FTIR spectra shows the formation of hydrogen bonds between hydroxyl groups of PVA and the hydroxy groups of GO. The DSC thermograms shows the addition of GO to PVA greatly improves the thermal stability of the composites. XRD patterns shows that the GO exfoliated and uniformly dispersed in PVA matrix. Mechanical properties are significantly improved in PVA/GO composites. The tensile strength increased from 8.2 to 13.7 MPa and the Young's modulus increased from 7.5 to 24.8 MPa for 5 wt% GO doped sample. Dielectric spectroscopy showed a highest dielectric constant for the 5 wt% GO doped PVA films. This work provides a potential design strategy on PVA/GO composite, which would lead to higher-performance, flexible dielectric materials, high charge-storage devices.

  10. Synthesis and characterization of alkaline polyvinyl alcohol and poly(epichlorohydrin) blend polymer electrolytes and performance in electrochemical cells

    NASA Astrophysics Data System (ADS)

    Yang, Chun-Chen; Lin, Sheng-Jen; Hsu, Sung-Ting

    Alkaline SPE was obtained from a blend of polyvinyl alcohol (PVA) and poly(epichlorohydrin) (PECH), PVA-PECH, by a solution-cast technique. The PVA host polymer is blended with PECH polymer to provide a polymer electrolyte with improved chemical and mechanical properties. The ionic conductivity of the PVA-PECH polymer electrolytes is between 10 -2 and 10 -3 S cm -1 at room temperature when the blend ratio is varied from 1:0.2 to 1:1. The PVA-PECH polymer was characterized by means of scanning electron microscopy, X-ray diffraction, stress-strain test, cyclic voltammetry, and a.c. impedance spectroscopy. It is found that the polymer electrolytes exhibit good mechanical strength and excellent chemical stability. The electrochemical performance of solid-state Zn-air batteries with various types of the blended polymer electrolyte films is examined by a galvanostatic discharge method.

  11. Rainfastness of Poly(vinyl alcohol) Deposits on Vicia faba Leaf Surfaces: From Laboratory-Scale Washing to Simulated Rain.

    PubMed

    Symonds, Brett L; Thomson, Niall R; Lindsay, Christopher I; Khutoryanskiy, Vitaliy V

    2016-06-01

    Rainfastness is the ability of agrochemical deposits to resist wash-off by rain and other related environmental phenomena. This work reports laboratory-scale and raintower studies of the rainfastness of fluorescently labeled poly(vinyl alcohol) (PVA) using fluorescent microscopy combined with image analysis. Samples of hydrolyzed PVA exhibit improved rainfastness over a threshold molecular weight, which correlates with PVA film dissolution, swelling, and crystalline properties. It was also established that the rainfastness of PVA scaled with the molecular weight over this threshold. These PVA samples were further characterized in order to determine the effect of the crystallinity on rainfastness. The quantification of rainfastness is of great interest to the field of agrochemical formulation development in order to improve the efficacy of pesticides and their adjuvants. PMID:27070864

  12. Dielectric, thermal and mechanical properties of ADP doped PVA composites

    NASA Astrophysics Data System (ADS)

    Naik, Jagadish; Bhajantri, R. F.; Ravindrachary, V.; Rathod, Sunil G.; Sheela, T.; Naik, Ishwar

    2015-06-01

    Polymer composites of poly(vinyl alcohol) (PVA), doped with different concentrations of ammonium dihydrogen phosphate (ADP) has been prepared by solution casting. The formation of complexation between ADP and PVA was confirmed with the help of Fourier transforms infrared (FTIR) spectroscopy. Thermogravimetric analysis (TGA) shows thermal stability of the prepared composites. Impedance analyzer study revealed the increase in dielectric constant and loss with increase the ADP concentration and the strain rate of the prepared composites decreases with ADP concentration.

  13. Broadband tuning in a passively Q-switched erbium doped fiber laser (EDFL) via multiwall carbon nanotubes/polyvinyl alcohol (MWCNT/PVA) saturable absorber

    NASA Astrophysics Data System (ADS)

    Ahmad, H.; Hassan, S. N. M.; Ahmad, F.; Zulkifli, M. Z.; Harun, S. W.

    2016-04-01

    An MWCNT/PVA-based Q-switched erbium-doped fiber laser (EDFL) that uses a tunable bandpass filter (TBPF) as the wavelength tuning and filtering mechanism to achieve a broadband tuning range is proposed and demonstrated. The tuning range of the generated Q-switched pulses covered a wide wavelength range of 50 nm, which spanned from 1519 nm to 1569 nm and corresponded to the S- and C-band regions. In addition, the lasing and Q-switching operations had low thresholds of 8.9 mW and 22.4 mW respectively. The highest pulse energy of 52.13 nJ was obtained at an output wavelength of 1569 nm, with a corresponding repetition rate of 26.53 kHz and pulse width of 6.10 μs, at the maximum power of 114.8 mW.

  14. Water swelling properties of the electron beam irradiated PVA-g-AAc hydrogels

    NASA Astrophysics Data System (ADS)

    Wang, Qingguo; Zhou, Xue; Zeng, Jinxia; Wang, Jizeng

    2016-02-01

    In this paper, the electron beam irradiation technology being more suitable for the industry application is explored to fabricate the acrylic acid (AAc) monomer-grafted polyvinyl alcohol (PVA-g-AAc) hydrogels. ATR-IR spectra of the PVA-g-AAc hydrogels shows an obvious absorption peak of the sbnd Cdbnd O group at 1701 cm-1, indicating that the AAc monomers were grafted onto the PVA macromolecules. This paper also studied some effects of the mass ratio of PVA/AAc, pH of buffer solution and irradiation dosage on the water swelling properties of the electron beam irradiated PVA-g-AAc hydrogels. The water swelling ratio of PVA-g-AAc hydrogels decreases with increased irradiation dosage and mass ratio of PVA/AAc, whereas swelling ratio increases with increased pH of buffer solution and soaking time. The water-swelling behavior of PVA-g-AAc hydrogels occurred easily in an alkaline environment, particularly in a buffer solution with pH 9.2. Both PVA-g-AAc hydrogels (PVA/AAc = 1/5, w/w) irradiated with 5 kilogray (kGy) and PVA-g-AAc hydrogels (PVA/AAc = 1/1, w/w) irradiated with 15 kGy could easily absorb water and lead to high water swelling ratios (up to about 600%), which are potential candidates to meet the requirements for some biomedical applications.

  15. Influence of solution viscosity on hydrothermally grown ZnO thin films for DSSC applications

    NASA Astrophysics Data System (ADS)

    Marimuthu, T.; Anandhan, N.; Thangamuthu, R.; Surya, S.

    2016-10-01

    Zinc oxide (ZnO) nanowire arrays (NWAs) were grown onto zinc oxide-titanium dioxide (ZnO-TiO2) seeded fluorine doped tin oxide (FTO) conductive substrate by hydrothermal technique. X-ray diffraction (XRD) patterns depict that ZnO thin films are preferentially oriented along the (002) plane with hexagonal wurtzite structure. Viscosity measurements reveal that viscosity of the solutions linearly increases as the concentrations of the polyvinyl alcohol (PVA) increase in the growth solution. Field emission scanning electron microscope (FE-SEM) images show that the NWAs are vertically grown to seeded FTO substrate with hexagonal structure, and the growth of NWAs decreases as the concentration of the PVA increases. Stylus profilometer and atomic force microscopic (AFM) studies predict that the thickness and roughness of the films decrease with increasing the PVA concentrations. The NWAs prepared at 0.1% of PVA exhibits a lower transmittance and higher absorbance than that of the other films. The band gap of the optimized films prepared at 0.0 and 0.1% of PVA is found to be 3.270 and 3.268 eV, respectively. The photo to current conversion efficiency of the DSSC based on photoanodes prepared at 0.0 and 0.1% of PVA exhibits about 0.64 and 0.82%, respectively. Electrochemical impedance spectra reveal that the DSSC based on photoanode prepared at 0.1% of PVA has the highest charge transfer recombination resistance.

  16. Bio-inspired nacre-like composite films based on graphene with superior mechanical, electrical, and biocompatible properties.

    PubMed

    Li, Yuan-Qing; Yu, Ting; Yang, Tian-Yi; Zheng, Lian-Xi; Liao, Kin

    2012-07-01

    Bio-inspired multifunctional composite films based on reduced poly(vinyl alcohol)/graphene oxide (R-PVA/GO) layers are prepared by a facile solution casting method followed by a reduction procedure. The resulting films with nacre-like, bricks-and-mortar microstructure have excellent mechanical properties, electrical conductivity, and biocompatibility. PMID:22730223

  17. Hydrogen Bonding Based Layer-by-Layer Assembly of Poly(vinyl alcohol) with Weak Polyacids

    NASA Astrophysics Data System (ADS)

    Lee, Hyomin; Mensire, Remy; Cohen, Robert; Rubner, Michael

    2012-02-01

    Multilayer thin films that consist of poly(vinyl alcohol) (PVA) and weak polyacids such as poly(acrylic acid) (PAA) and poly(methacrylic acid) (PMAA) were prepared by hydrogen bonding interactions. Both the degree of hydrolysis and molecular weight of PVA were investigated in terms of their influence on growth behavior and pH stability. Multilayer films containing PVA and PAA could be assembled successfully only by using partially hydrolyzed PVA and low pH solutions. By comparing films containing PAA with those containing a more strongly interacting partner, PMAA, it was shown that the extent of PVA hydrolysis becomes significant only when weak hydrogen bonding pairs such as PVA and PAA were used. pH-triggered dissolution experiments demonstrated that the degree of hydrolysis can be used as an additional parameter by which to tune the pH stability of the film. Also, the presence of an abundance of free hydroxyl and carboxylic acid groups in the multilayer allowed enhanced pH stability to be obtained by thermal and chemical methods as well as numerous opportunities for post-assembly functionalization.

  18. Spectral and Polarizing Properties of Anisotropic Films Based on Polyvinyl Alcohol and 4,4'-Bis[4-(Phenylamino)-6-(Methoxy-1,3,5-Triazin-2-YL) Amino]Stilbene-2,2'-Disulfonic Acid

    NASA Astrophysics Data System (ADS)

    Bondarev, S. L.; Ariko, N. G.; Filippovich, L. N.; Karoza, A. G.; Stupak, A. P.

    2016-09-01

    The spectral and polarization characteristics of optically anisotropic polyvinyl alcohol (PVA) films containing 4,4'-bis[4-(phenylamino)-6-(methoxy-1,3,5-triazin-2-yl)amino]stilbene-2,2'-disulfonic acid as dichroic dye, which has intense blue fluorescence, were investigated by polarized luminescence and absorptionspectroscopy in the IR and UV regions. With fourfold uniaxial stretching of the film the orientation parameter of the dye amounts to 0.82-0.86, the maximum polarizing ability of the film is 96% (at the maximum of the absorption band at 375 nm), and the degree of polarization and quantum yield of fluorescence at the optimum concentration of the dye amount to 0.90 and 0.91. The degree of orientation of the dye molecules depends weakly on the concentration (0.01-0.50 wt.%) and increases with increase of the uniaxial stretching of the film. The insertion of the dye molecules between the PVA chains leads to a reduction of the crystallinity of the polymeric matrix.

  19. Performance enhancement of poly(3-hexylthiophene-2,5-diyl) based field effect transistors through surfactant treatment of the poly(vinyl alcohol) gate insulator surface.

    PubMed

    Nawaz, Ali; Cruz-Cruz, Isidro; Rodrigues, Rafael; Hümmelgen, Ivo A

    2015-10-28

    We report on the improvement of field effect transistors based on poly(3-hexylthiophene-2,5-diyl) (P3HT) as a channel semiconductor and crosslinked poly(vinyl alcohol) (cr-PVA) as a gate insulator, through the treatment of the cr-PVA film surface before P3HT deposition. We treated the cr-PVA either with hydrochloric acid (HCl) or with a cationic surfactant, hexadecyltrimethylammonium bromide (CTAB), aiming at the passivation of the hole traps at the cr-PVA/P3HT interface. The treatment with HCl leads to an excessive increase in the transistor leakage current and unstable electrical characteristics, despite implying an increase in the gate capacitance. The treatment with CTAB leads to transistors with ca. 50% higher specific capacitance and a tenfold increase in the charge carrier field-effect mobility, when compared to devices based on untreated cr-PVA.

  20. Properties of novel polyvinyl alcohol/cellulose nanocrystals/silver nanoparticles blend membranes.

    PubMed

    Xu, Xu; Yang, Yi-Qin; Xing, Ying-Ying; Yang, Jiu-Fang; Wang, Shi-Fa

    2013-11-01

    Novel polyvinyl alcohol (PVA) blend membranes containing cellulose nanocrystals (CNs) and silver nanoparticles (AgNPs) were prepared via a simple method. CNs were prepared by sulfuric acid treatment of microcrystalline cellulose. AgNO3 aqueous solution mixed with the CNs aqueous suspension and was reduced by NaBH4 at room temperature. Purified CNs/AgNPs nanocomposites as functional fillers mixed with polyvinyl alcohol to prepare blend membrane. The morphology, mechanical properties, and antibacterial activities of PVA/CNs/AgNPs composite films were investigated. The PVA/CNs/AgNPs composite films were stable and homogeneous. The tensile strength of PVA was increased from 57.02 MPa to 81.21 MPa when filled with CNs/AgNPs. Antibacterial ratio of PVA/CNs/AgNPs composite against Gram-negative Escherichia coli and Gram-positive Staphylococcus aureus was 96.9% and 88.2%, respectively. The CNs/AgNPs nanocomposites could be applied as bi-functional nanofillers within PVA to improve the mechanical properties and antibacterial activities. PMID:24053842

  1. Properties of novel polyvinyl alcohol/cellulose nanocrystals/silver nanoparticles blend membranes.

    PubMed

    Xu, Xu; Yang, Yi-Qin; Xing, Ying-Ying; Yang, Jiu-Fang; Wang, Shi-Fa

    2013-11-01

    Novel polyvinyl alcohol (PVA) blend membranes containing cellulose nanocrystals (CNs) and silver nanoparticles (AgNPs) were prepared via a simple method. CNs were prepared by sulfuric acid treatment of microcrystalline cellulose. AgNO3 aqueous solution mixed with the CNs aqueous suspension and was reduced by NaBH4 at room temperature. Purified CNs/AgNPs nanocomposites as functional fillers mixed with polyvinyl alcohol to prepare blend membrane. The morphology, mechanical properties, and antibacterial activities of PVA/CNs/AgNPs composite films were investigated. The PVA/CNs/AgNPs composite films were stable and homogeneous. The tensile strength of PVA was increased from 57.02 MPa to 81.21 MPa when filled with CNs/AgNPs. Antibacterial ratio of PVA/CNs/AgNPs composite against Gram-negative Escherichia coli and Gram-positive Staphylococcus aureus was 96.9% and 88.2%, respectively. The CNs/AgNPs nanocomposites could be applied as bi-functional nanofillers within PVA to improve the mechanical properties and antibacterial activities.

  2. The Dynamic Reinforcement of Polyvinyl Alcohol (PVA) as a Result of Non-equilibrium State of Polymer Supermolecular Structures and their Confinement in Nanofibers

    NASA Astrophysics Data System (ADS)

    Zussman, Eyal; Shaked, Emil; Arinstein, Arkadi

    2009-03-01

    The results of mechanical testing of PVA -based electrospun nanofibers and bulk in static and dynamic modes are presented. An increase in the elastic moduli resulting from sample deformation was observed in both the bulk and as-spun fibers. This increase occurs when the deformation rate exceeds a critical value and can be attributed to the non-equilibrium dynamics of the supermolecular structures of the polymer matrix. That is, the evolution of these supermolecular structures results in an observably extended relaxation time. It is noted that the rate of the modulus increase of the nanofibers is nearly double that of the bulk fibers' rate. This difference can be explained by confinement influence on the polymer matrix of the nanofibers. In addition, the tests revealed that the, Tg, of the nanofiber is noticeably higher than that of bulk specimen. Reinforcing the nanofibrs by cellulose whiskers showing that the dependence of the effective modulus on the whisker concentration has an initial increase that changes to a decrease when the whisker concentration exceeds 2 %. Such behavior can be explained in the framework of an aggregation concept -- when the cluster size reaches that of the fiber diameter (cluster confinement), the whisker distribution becomes inhomogeneous and results in a measurable weakening of the composite.

  3. Novel PVA/MOF Nanofibres: Fabrication, Evaluation and Adsorption of Lead Ions from Aqueous Solution.

    PubMed

    Shooto, Ntaote David; Dikio, Charity Wokwu; Wankasi, Donbebe; Sikhwivhilu, Lucky Mashudu; Mtunzi, Fanyana Moses; Dikio, Ezekiel Dixon

    2016-12-01

    Plain polyvinyl alcohol (PVA) nanofibres and novel polyvinyl alcohol benzene tetracarboxylate nanofibres incorporated with strontium, lanthanum and antimony ((PVA/Sr-TBC), (PVA/La-TBC) and (PVA/Sb-TBC)), respectively, where TBC is benzene 1,2,4,5-tetracarboxylate adsorbents, were fabricated by electrospinning. The as-prepared electrospun nanofibres were characterized by scanning electron microscope (SEM), Fourier transform infrared (FTIR) and thermogravimetric analysis (TGA). Only plain PVA nanofibres followed the Freundlich isotherm with a correlation coefficient of 0.9814, while novel nanofibres (PVA/Sb-TBC, PVA/Sr-TBC and PVA/La-TBC) followed the Langmuir isotherm with correlation coefficients of 0.9999, 0.9994 and 0.9947, respectively. The sorption process of all nanofibres followed a pseudo second-order kinetic model. Adsorption capacity of novel nanofibres was twofold and more compared to that of plain PVA nanofibres. The thermodynamic studies: apparent enthalpy (ΔH°) and entropy (ΔS°), showed that the adsorption of Pb(II) onto nanofibres was spontaneous and exothermic. The novel nanofibres exhibited higher potential removal of Pb(II) ions than plain PVA nanofibres. Ubiquitous cations adsorption test was also investigated and studied. PMID:27644240

  4. Novel PVA/MOF Nanofibres: Fabrication, Evaluation and Adsorption of Lead Ions from Aqueous Solution

    NASA Astrophysics Data System (ADS)

    Shooto, Ntaote David; Dikio, Charity Wokwu; Wankasi, Donbebe; Sikhwivhilu, Lucky Mashudu; Mtunzi, Fanyana Moses; Dikio, Ezekiel Dixon

    2016-09-01

    Plain polyvinyl alcohol (PVA) nanofibres and novel polyvinyl alcohol benzene tetracarboxylate nanofibres incorporated with strontium, lanthanum and antimony ((PVA/Sr-TBC), (PVA/La-TBC) and (PVA/Sb-TBC)), respectively, where TBC is benzene 1,2,4,5-tetracarboxylate adsorbents, were fabricated by electrospinning. The as-prepared electrospun nanofibres were characterized by scanning electron microscope (SEM), Fourier transform infrared (FTIR) and thermogravimetric analysis (TGA). Only plain PVA nanofibres followed the Freundlich isotherm with a correlation coefficient of 0.9814, while novel nanofibres (PVA/Sb-TBC, PVA/Sr-TBC and PVA/La-TBC) followed the Langmuir isotherm with correlation coefficients of 0.9999, 0.9994 and 0.9947, respectively. The sorption process of all nanofibres followed a pseudo second-order kinetic model. Adsorption capacity of novel nanofibres was twofold and more compared to that of plain PVA nanofibres. The thermodynamic studies: apparent enthalpy (Δ H°) and entropy (Δ S°), showed that the adsorption of Pb(II) onto nanofibres was spontaneous and exothermic. The novel nanofibres exhibited higher potential removal of Pb(II) ions than plain PVA nanofibres. Ubiquitous cations adsorption test was also investigated and studied.

  5. A novel gellan-PVA nanofibrous scaffold for skin tissue regeneration: Fabrication and characterization.

    PubMed

    Vashisth, Priya; Nikhil, Kumar; Roy, Partha; Pruthi, Parul A; Singh, Rajesh P; Pruthi, Vikas

    2016-01-20

    In this investigation, we have introduced novel electrospun gellan based nanofibers as a hydrophilic scaffolding material for skin tissue regeneration. These nanofibers were fabricated using a blend mixture of gellan with polyvinyl alcohol (PVA). PVA reduced the repulsive force of resulting solution and lead to formation of uniform fibers with improved nanostructure. Field emission scanning electron microscopy (FESEM) confirmed the average diameter of nanofibers down to 50 nm. The infrared spectra (IR), differential scanning calorimetry (DSC) and X-ray diffraction (XRD) analysis evaluated the crosslinking, thermal stability and highly crystalline nature of gellan-PVA nanofibers, respectively. Furthermore, the cell culture studies using human dermal fibroblast (3T3L1) cells established that these gellan based nanofibrous scaffold could induce improved cell adhesion and enhanced cell growth than conventionally proposed gellan based hydrogels and dry films. Importantly, the nanofibrous scaffold are biodegradable and could be potentially used as a temporary substrate/or biomedical graft to induce skin tissue regeneration. PMID:26572421

  6. A Study on the Fabrication of Organic Thin Film Transistor Sensors using Gravure Printing

    NASA Astrophysics Data System (ADS)

    Hwang, Won-Jin; Hong, Jae-Min; Ju, Byeong-Kwon; Yu, Jae-Woong

    2011-12-01

    Conducting polymer TFT was fabricated with gravure printing technique using a vapor polymerization method. Polyvinyl alcohol (PVA) with excellent film forming characteristics was used as a matrix polymer. After the printing of the oxidant dispersed PVA dissolved in DI water, the vapor polymerization of the pyrrole monomer formed a thin conducting polymer film. The conductivity of the film was dependent on the concentration of the oxidant and the polymerization time. In order to be used for TFT application, the conductivity had to be reduced by controlling the various conditions. The effect of exposure to humidity on TFT signal was studied.

  7. Local, real-time measurement of drying films of aqueous polymer solutions using active microrheology.

    PubMed

    Komoda, Yoshiyuki; Leal, L Gary; Squires, Todd M

    2014-05-13

    Oscillatory microdisk rheometry was applied to evaluate the evolution of the viscoelastic properties at the surface of a film of an aqueous solution of poly(vinyl alcohol) (PVA) during drying. The drying rate was measured concurrently, based upon measurements of the variation of film thickness. A fully hydrolyzed PVA solution shows a constant drying rate, while a less hydrolyzed PVA solution exhibits a decreased drying rate in the latter part of the drying process, which occurred at the same time as an increase of the elastic modulus. We suggest that this difference in behavior is a consequence of the fact that both the configuration of the PVA molecule and the strength of interaction with water depend on the degree to which the PVA is hydrolyzed. The polymer concentration at the film surface can be estimated from the measured viscosity at the surface for the fully hydrolyzed PVA solution, and this result then can be compared with two theoretical calculations: one in which the polymer concentration is assumed to remain uniform throughout the film, and the other in which the polymer concentration distribution is determined via a one-dimensional diffusion model. This comparison suggests that the polymer is first concentrated locally near the surface but later in the drying process the distribution of polymer becomes increasingly uniform, possibly due to a spontaneously generated convective flow inside the film.

  8. Highly conductive quasi-coaxial electrospun quaternized polyvinyl alcohol nanofibers and composite as high-performance solid electrolytes

    NASA Astrophysics Data System (ADS)

    Liao, Guan-Ming; Li, Pin-Chieh; Lin, Jia-Shiun; Ma, Wei-Ting; Yu, Bor-Chern; Li, Hsieh-Yu; Liu, Ying-Ling; Yang, Chun-Chen; Shih, Chao-Ming; Lue, Shingjiang Jessie

    2016-02-01

    Electrospun quaternized polyvinyl alcohol (Q-PVA) nanofibers are prepared, and a potassium hydroxide (KOH)-doped nanofiber mat demonstrates enhanced ionic conductivity compared with a dense Q-PVA film with KOH doping. The Q-PVA composite containing 5.98% electrospun Q-PVA nanofibers exhibits suppressed methanol permeability. Both the high conductivity and suppressed methanol permeability are attributed to the quasi-coaxial structure of the electrospun nanofibers. The core of the fibers exhibits a more amorphous region that forms highly conductive paths, while the outer shell of the nanofibers contains more polymer crystals that serve as a hard sheath surrounding the soft core. This shell induces mass transfer resistance and creates a tortuous fuel pathway that suppresses methanol permeation. Such a Q-PVA composite is an effective solid electrolyte that makes the use of alkaline fuel cells viable. In a direct methanol alkaline fuel cell operated at 60 °C, a peak power density of 54 mW cm-2 is obtained using the electrospun Q-PVA composite, a 36.4% increase compared with a cell employing a pristine Q-PVA film. These results demonstrate that highly conductive coaxial electrospun nanofibers can be prepared through a single-opening spinneret and provide a possible approach for high-performance electrolyte fabrication.

  9. Multifunctional Polyphenols- and Catecholamines-Based Self-Defensive Films for Health Care Applications.

    PubMed

    Dhand, Chetna; Harini, Sriram; Venkatesh, Mayandi; Dwivedi, Neeraj; Ng, Alice; Liu, Shouping; Verma, Navin Kumar; Ramakrishna, Seeram; Beuerman, Roger W; Loh, Xian Jun; Lakshminarayanan, Rajamani

    2016-01-20

    In an era of relentless evolution of antimicrobial resistance, there is an increasing demand for the development of efficient antimicrobial coatings or surfaces for food, biomedical, and industrial applications. This study reports the laccase-catalyzed room-temperature synthesis of mechanically robust, thermally stable, broad spectrum antimicrobial films employing interfacial interactions between poly(vinyl alcohol), PVA, and 14 naturally occurring catecholamines and polyphenols. The oxidative products of catecholamines and polyphenols reinforce the PVA films and also alter their surface and bulk properties. Among the catecholamines-reinforced films, optimum surface and bulk properties can be achieved by the oxidative products of epinephrine. For polyphenols, structure-property correlation reveals an increase in surface roughness and elasticity of PVA films with increasing number of phenolic groups in the precursors. Interestingly, PVA films reinforced with oxidized/polymerized products of pyrogallol (PG) and epinephrine (EP) display potent antimicrobial activity against pathogenic Gram-positive and Gram-negative strains, whereas hydroquinone (HQ)-reinforced PVA films display excellent antimicrobial properties against Gram-positive bacteria only. We further demonstrate that HQ and PG films retain their antimicrobial efficacy after steam sterilization. With an increasing trend of giving value to natural and renewable resources, our results have the potential as durable self-defensive antimicrobial surfaces/films for advanced healthcare and industrial applications. PMID:26709441

  10. Multifunctional Polyphenols- and Catecholamines-Based Self-Defensive Films for Health Care Applications.

    PubMed

    Dhand, Chetna; Harini, Sriram; Venkatesh, Mayandi; Dwivedi, Neeraj; Ng, Alice; Liu, Shouping; Verma, Navin Kumar; Ramakrishna, Seeram; Beuerman, Roger W; Loh, Xian Jun; Lakshminarayanan, Rajamani

    2016-01-20

    In an era of relentless evolution of antimicrobial resistance, there is an increasing demand for the development of efficient antimicrobial coatings or surfaces for food, biomedical, and industrial applications. This study reports the laccase-catalyzed room-temperature synthesis of mechanically robust, thermally stable, broad spectrum antimicrobial films employing interfacial interactions between poly(vinyl alcohol), PVA, and 14 naturally occurring catecholamines and polyphenols. The oxidative products of catecholamines and polyphenols reinforce the PVA films and also alter their surface and bulk properties. Among the catecholamines-reinforced films, optimum surface and bulk properties can be achieved by the oxidative products of epinephrine. For polyphenols, structure-property correlation reveals an increase in surface roughness and elasticity of PVA films with increasing number of phenolic groups in the precursors. Interestingly, PVA films reinforced with oxidized/polymerized products of pyrogallol (PG) and epinephrine (EP) display potent antimicrobial activity against pathogenic Gram-positive and Gram-negative strains, whereas hydroquinone (HQ)-reinforced PVA films display excellent antimicrobial properties against Gram-positive bacteria only. We further demonstrate that HQ and PG films retain their antimicrobial efficacy after steam sterilization. With an increasing trend of giving value to natural and renewable resources, our results have the potential as durable self-defensive antimicrobial surfaces/films for advanced healthcare and industrial applications.

  11. Self Nucleation and Crystallization of Poly(vinyl alcohol)

    NASA Astrophysics Data System (ADS)

    Thomas, David; Cebe, Peggy

    Polyvinyl alcohol (PVA) is a hydrophilic, biodegradable, semi-crystalline polymer with uses ranging from textiles to medicine. Film samples of PVA were investigated to assess crystallization and melting behavior during self-nucleation experiments, and thermal degradation, using differential scanning calorimetry (DSC) and thermogravimetric (TG) analysis, respectively. TG results show that degradation occurred at temperatures close to the observed peak melting temperature of 223 C. Using conventional DSC, PVA was heated at a rate of 10 C/min to various self-nucleation temperatures, Ts, within its melting range, briefly annealed, cooled and reheated. Three distinct crystallization regimes were observed upon cooling, depending upon self nucleation temperature. At low values of Ts, below 227 C, PVA only partially melts; residual crystal anneals while new, less perfect crystals form during cooling. Between 228 C and 234 C, PVA was found to crystallize exclusively by self-nucleation. For Ts above 235 C the PVA melts completely. Fast scanning chip-based calorimetry was used to heat and cool at 2000 K/s, to prevent degradation. Results of self nucleation experiments using fast scanning and conventional DSC will be compared. NSF DMR-1206010.

  12. 16mm Films on Drug, Alcohol and Tobacco Abuse. Product Information Supplement No.6

    ERIC Educational Resources Information Center

    Educ Prod Rep, 1970

    1970-01-01

    Sixty-two films on drug abuse, 33 on smoking abuse, and 28 on alcohol abuse are listed showing title, distributor, suggested grade level, technical information, description of content, cost, and availability. (MLF)

  13. Electrospinning, mechanical properties, and cell behavior study of chitosan/PVA nanofibers.

    PubMed

    Koosha, Mojtaba; Mirzadeh, Hamid

    2015-09-01

    Electrospinning process has been widely used to produce nanofibers from polymer blends. Poly(vinyl alcohol) (PVA) and chitosan (CS) have numerous biomedical applications such as wound healing and tissue engineering. Nanofibers of CS/PVA have been prepared by many works, however, a complete physicochemical and mechanical characterization as well as cell behavior has not been reported. In this study, PVA and CS/PVA blend solutions in acetic acid 70% with different volume ratios (30/70, 50/50, and 70/30) were electrospun in constant electrospinning process parameters. The structure and morphology of nanofibrous mats were characterized by SEM, FTIR, and XRD methods. The best nanofibrous mat was achieved from the CS/PVA 30/70 blend solution regarding the electrospinning throughput. The dynamic mechanical thermal analysis (DMTA) of PVA and CS/PVA 30/70 nanofibrous mats were measured which were not considered in the previous studies. DMTA results in accordance to the DSC analysis approved the partial compatibility between the two polymers, while a single glass transition temperature was not observed for the blend. The tensile strength of PVA and CS/PVA nanofibers were also reported. Results of cell behavior study indicated that the heat stabilized nanofibrous mat CS/PVA 30/70 was able to support the attachment and proliferation of the fibroblast cells.

  14. Formulation and characterization of acetaminophen nanoparticles in orally disintegrating films.

    PubMed

    Al-Nemrawi, Nusaiba K; Dave, Rutesh H

    2016-01-01

    The purpose of this study was to prepare orally disintegrating films containing nanoparticles loaded with acetaminophen. Nanoparticles were prepared by the emulsion-solvent evaporation method where acetone phase containing acetaminophen and poly(lactide-co-glycolide acid) (PLGA) was added to water phase containing hydroxypropyl methyl cellulose, poly ethylene glycol, polyvinyl alcohol (PVA) and aspartame in a rate of 1.5 drop s(-1) and agitated at 1200 rpm. The size, polydispersity index (PI) and drug entrapment (DE) were measured. The emulsions were cast to form films, which were evaluated physico-mechanically. The effect of different degrees of hydrolization of PVA and polymerization of PLGA and the effect of different ratios of PVA to PLGA was studied. Films with acceptable physico-mechanical properties were further studied. The size and PI of the nanoparticles was dependent on PVA hydrolization, PLGA polymerization and the ratio of PVA to PLGA. All films disintegrated in less than one minute, but acetaminophen was not free in the dissolution media even after six days. These results may indicate that although the nanoparticles released from the films immediately when impressed in solution the drug is sustained in the nanoparticles for longer time, which is to be clarified in future work.

  15. Selective permeability of PVA membranes. I - Radiation-crosslinked membranes

    NASA Technical Reports Server (NTRS)

    Katz, M. G.; Wydeven, T., Jr.

    1981-01-01

    The water and salt transport properties of ionizing radiation crosslinked poly(vinyl alcohol) (PVA) membranes were investigated. The studied membranes showed high permeabilities and low selectivities for both water and salt. The results were found to be in accord with a modified solution-diffusion model for transport across the membranes, in which pressure-dependent permeability coefficients are employed.

  16. Selective Permeability of PVA Membranes. I: Radiation-Crosslinked Membranes

    NASA Technical Reports Server (NTRS)

    Katz, Moshe G.; Wydeven, Theodore, Jr.

    1981-01-01

    The water and salt transport properties of ionizing radiation crosslinked poly(vinyl alcohol) (PVA) membranes were investigated. The studied membranes showed high permeabilities and low selectivities for both water and salt. The results were found to be in accord with a modified solution-diffusion model for transport across the membranes, in which pressure-dependent permeability coefficients are employed.

  17. Gel characterisation and in vivo evaluation of minocycline-loaded wound dressing with enhanced wound healing using polyvinyl alcohol and chitosan.

    PubMed

    Sung, Jung Hoon; Hwang, Ma-Ro; Kim, Jong Oh; Lee, Jeong Hoon; Kim, Yong Il; Kim, Jeong Hoon; Chang, Sun Woo; Jin, Sung Giu; Kim, Jung Ae; Lyoo, Won Seok; Han, Sung Soo; Ku, Sae Kwang; Yong, Chul Soon; Choi, Han-Gon

    2010-06-15

    The purpose of this study was to develop a minocycline-loaded wound dressing with an enhanced healing effect. The cross-linked hydrogel films were prepared with polyvinyl alcohol (PVA) and chitosan using the freeze-thawing method. Their gel properties, in vitro protein adsorption, release, in vivo wound healing effect and histopathology were then evaluated. Chitosan decreased the gel fraction, maximum strength and thermal stability of PVA hydrogel, while it increased the swelling ability, water vapour transmission rate, elasticity and porosity of PVA hydrogel. Incorporation of minocycline (0.25%) did not affect the gel properties, and chitosan hardly affected drug release and protein adsorption. Furthermore, the minocycline-loaded wound dressing composed of 5% PVA, 0.75% chitosan and 0.25% drug was more swellable, flexible and elastic than PVA alone because of relatively weak cross-linking interaction of chitosan with PVA. In wound healing test, this minocycline-loaded PVA-chitosan hydrogel showed faster healing of the wound made in rat dorsum than the conventional product or the control (sterile gauze) due to antifungal activity of chitosan. In particular, from the histological examination, the healing effect of minocycline-loaded hydrogel was greater than that of the drug-loaded hydrogel, indicating the potential healing effect of minocycline. Thus, the minocycline-loaded wound dressing composed of 5% PVA, 0.75% chitosan and 0.25% drug is a potential wound dressing with excellent forming and enhanced wound healing.

  18. Evaluation of the Antimicrobial Effect of Chitosan/Polyvinyl Alcohol Electrospun Nanofibers Containing Mafenide Acetate

    PubMed Central

    Abbaspour, Mohammadreza; Sharif Makhmalzadeh, Behzad; Rezaee, Behjat; Shoja, Saeed; Ahangari, Zohreh

    2015-01-01

    Background: Chitosan, an important biodegradable and biocompatible polymer, has demonstrated wound-healing and antimicrobial properties. Objectives: This study aimed to evaluate the antimicrobial properties of mafenide acetate-loaded nanofibrous films, prepared by the electrospinning technique, using chitosan and polyvinyl alcohol (PVA). Materials and Methods: A 32 full factorial design was used for formulating electrospinning solutions. The chitosan percentage in chitosan/PVA solutions (0%, 10%, and 30%) and the drug content (0%, 20%, and 40%) were chosen as independent variables. The release rate of mafenide acetate from nanofibrous films and their microbial penetration were evaluated. The antimicrobial activity of different nanofibrous film formulations against Staphylococcus aureus and Pseudomonas aeruginosa was studied. Results: The results indicated that all nanofibrous films, with and without drug, can prevent bacterial penetration. Incorporation of mafenide acetate into chitosan/PVA nanofibers enhanced their antimicrobial activity against P. aeruginosa and S. aureus. Conclusions: Overall, the results showed that chitosan/polyvinyl alcohol (PVA) nanofibrous films are applicable for use as a wound dressing with protective, healing, and antimicrobial effects. PMID:26587214

  19. Films from spruce galactoglucomannan blended with poly(vinyl alcohol), corn arabinoxylan and konjac glucomannan

    Technology Transfer Automated Retrieval System (TEKTRAN)

    The improvement of mechanical properties of spruce galactoglucomannan (GGM)-based films was sought by blending GGM with each of poly(vinyl alcohol) (PVOH), corn arabinoxylan (cAX), and konjac glucomannan (KGM). The blend ratios were 3:1, 1:1, and 1:3(w/w), and in addition films were made from each o...

  20. Biodegradability of poly(3-hydroxybutyrate) film grafted with vinyl acetate: Effect of grafting and saponification

    NASA Astrophysics Data System (ADS)

    Wada, Yuki; Seko, Noriaki; Nagasawa, Naotsugu; Tamada, Masao; Kasuya, Ken-ichi; Mitomo, Hiroshi

    2007-06-01

    Radiation-induced graft polymerization of vinyl acetate (VAc) onto poly(3-hydroxybutyrate) (PHB) film was carried out. At a degree of grafting higher than 5%, the grafted films (PHB-g-VAc) completely lost the enzymatic degradability that is characteristic of PHB due to the grafted VAc covering the surface of the PHB film. However, the biodegradability of the PHB-g-VAc films was recovered when the films were saponified in alkali solution under optimum conditions. Graft chains of the PHB-g-VAc film reacted selectively to become biodegradable polyvinyl alcohol (PVA). The biodegradability of the saponified PHB-g-VAc film increased rapidly with time.

  1. Graphene Oxide Transparent Hybrid Film and Its Ultraviolet Shielding Property.

    PubMed

    Xie, Siyuan; Zhao, Jianfeng; Zhang, Bowu; Wang, Ziqiang; Ma, Hongjuan; Yu, Chuhong; Yu, Ming; Li, Linfan; Li, Jingye

    2015-08-19

    Herein, we first reported a facile strategy to prepare functional Poly(vinyl alcohol) (PVA) hybrid film with well ultraviolet (UV) shielding property and visible light transmittance using graphene oxide nanosheets as UV-absorber. The absorbance of ultraviolet light at 300 nm can be up to 97.5%, while the transmittance of visible light at 500 nm keeps 40% plus. This hybrid film can protect protein from UVA light induced photosensitive damage, remarkably. PMID:26226281

  2. Alkaline direct ethanol fuel cell performance using alkali-impregnated polyvinyl alcohol/functionalized carbon nano-tube solid electrolytes

    NASA Astrophysics Data System (ADS)

    Huang, Chien-Yi; Lin, Jia-Shiun; Pan, Wen-Han; Shih, Chao-Ming; Liu, Ying-Ling; Lue, Shingjiang Jessie

    2016-01-01

    This study investigates the application of a polyvinyl alcohol (PVA)/functionalized carbon nano-tubes (m-CNTs) composite in alkaline direct ethanol fuel cells (ADEFC). The m-CNTs are functionalized with PVA using the ozone mediation method, and the PVA composite containing the modified CNTs is prepared. Adding m-CNT into the PVA matrix enhances the alkaline uptake and the ionic conductivity of the KOH-doped electrolyte. Meanwhile, the m-CNT-containing membrane exhibited a lower swelling ratio and suppressed ethanol permeability compared to the pristine PVA film. The optimal condition for the ADEFC is determined to be under operation at an anode feed of 3 M ethanol in a 5 M KOH solution (at a flow rate of 5 cm3 min-1) with a cathode feed of moisturized oxygen (with a flow rate of 100 cm3 min-1) and the KOH-doped PVA/m-CNT electrolyte. We achieved a peak power density value of 65 mW cm-2 at 60 °C, which is the highest among the ADEFC literature data and several times higher than the proton-exchange direct ethanol fuel cells using sulfonated membrane electrolytes. Therefore, the KOH-doped PVA/m-CNT electrolyte is a suitable solid electrolyte for ADEFCs and has potential for commercialization in alkaline fuel cell applications.

  3. Novel electroactive PVA-TOCN actuator that is extremely sensitive to low electrical inputs

    NASA Astrophysics Data System (ADS)

    Wang, Fan; Kim, Si-Seup; Kee, Chang-Doo; Shen, Yun-De; Oh, Il-Kwon

    2014-07-01

    A novel electroactive biopolymer actuator was developed based on a cross-linked ionic networking membrane of TEMPO-oxidized bacterial cellulose nanofibers (TOCNs) and polyvinyl alcohol (PVA). Ionic liquids were added to develop an air-working artificial muscle and to enhance the performance of the PVA-TOCN actuator. Poly(3,4-ethylenedioxythiophene)-poly(styrenesulfonate) (PEDOT:PSS) conducting layers were deposited on the top and bottom surfaces of the PVA-TOCN membrane via a simple dipping and drying method. The electroactive PVA-TOCN actuator under both step and harmonic electrical inputs shows much larger tip displacements and faster bending deformation than the pure TOCN actuator. The cross-linking reaction between PVA and TOCN was observed in the Fourier transform-near-infrared (FT-IR) spectrum of the PVA-TOCN networking membrane. Scanning electron microscopy (SEM), x-ray diffusion (XRD), thermogravimetric analysis (TGA) and tensile and ion conductivity testing results for the PVA-TOCN membrane were compared with those of pristine TOCN. Most important, the PVA-TOCN actuator shows much larger bending deformation under even extremely low input voltages, and this could be attributed to the cross-linking mechanism and the greater flexibility resulting from the synergistic effects between PVA and TOCN.

  4. Determination of mechanical and hydraulic properties of PVA hydrogels.

    PubMed

    Kazimierska-Drobny, Katarzyna; El Fray, Miroslawa; Kaczmarek, Mariusz

    2015-03-01

    In this paper the identification of mechanical and hydraulic parameters of poly(vinyl alcohol) (PVA) hydrogels is described. The identification method follows the solution of inverse problem using experimental data from the unconfined compression test and the poroelastic creep model. The sensitivity analysis of the model shows significant dependence of the creep curves on investigated parameters. The hydrogels containing 22% PVA and 25% PVA were tested giving: the drained Youngs modulus of 0.71 and 0.9MPa; the drained Poisson's ratio of 0.18 and 0.31; and the permeability of 3.64·10(-15) and 3.29·10(15)m(4)/Ns, respectively. The values of undrained Youngs modulus were determined by measuring short period deformation of samples in the unconfined tests. A discussion on obtained results is presented.

  5. Borax mediated layer-by-layer self-assembly of neutral poly(vinyl alcohol) and chitosan.

    PubMed

    Manna, Uttam; Patil, Satish

    2009-07-01

    We report a multilayer film of poly(vinyl alcohol) (PVA)-borate complex and chitosan by using a layer-by-layer approach. PVA is an uncharged polymer, but hydroxyl functional groups of PVA can be cross-linked by using borax as a cross-linking agent. As a result electrostatic charges and intra- and interchain cross-links are introduced in the PVA chain and provide physically cross-linked networks. The PVA-borate was then deposited on a flat substrate as well as on colloidal particles with chitosan as an oppositely charged polyelectrolyte. Quartz crystal microbalance, scanning electron microscopy, and atomic force microscopy were used to follow the growth of thin film on flat substrate. Analogous experiments were performed on melamine formaldehyde colloidal particles (3-3.5 microm) to quantify the process for the preparation of hollow microcapsules. Removal of the core in 0.1 N HCl results in hollow microcapsules. Characterization of microcapsules by transmission electron microscopy revealed formation of stable microcapsules. Further, self-assembly of PVA-borate/chitosan was loaded with the anticancer drug doxorubicin, and release rates were determined at different pH values to highlight the drug delivery potential of this system.

  6. Development and evaluation of polyvinyl-alcohol blend polymer films as battery separators

    NASA Technical Reports Server (NTRS)

    Manzo, M. A.

    1982-01-01

    Several dialdehydes and epoxies were evaluated for their suitability as cross-linkers. Optium concentrations of several cross-linking reagents were determined. A two-step method of cross-linking, which involves treatment of the film in an acid or acid periodate bath, was investigated and dropped in favor of a one-step method in which the acid catalyst, which initiates cross-linking, is added to the PVA - cross-linker solution before casting. The cross-linking was thus achieved during the drying step. This one-step method was much more adaptable to commercial processing. Cross-linked films were characterized as alkaline battery separators. Films were prepared in the lab and tested in cells in order to evaluate the effect of film composition and a number of processing parameters on cell performance. These tests were conducted in order to provide a broader data base from which to select optimum processing parameters. Results of the separator screening tests and the cell tests are discussed.

  7. Molecular Interactions Between Alcohols and Metal Phthalocyanine Thin Films for Optical Gas Sensor Applications

    NASA Astrophysics Data System (ADS)

    Uttiya, Sureeporn; Kladsomboon, Sumana; Chamlek, Onanong; Suwannet, Wiriya; Osotchan, Tanakorn; Kerdcharoen, Teerakiat; Brinkmann, Martin; Pratontep, Sirapat

    Optically active organic gas sensors represent a promising molecular sensing device with low power consumption. We report experimental and computational investigations into the molecular interactions of metal phthalocyanine thin films with alcohol vapor. In the gas-sensing regime, the interactions of zinc phthalocyanine and alcohol molecules were studied by the Density Functional Theory (DFT) calculations, in comparison to the x-ray absorption spectroscopy. The DFT results reveal a reversible charge interaction mechanism between the zinc atom and the oxygen atom in the alcohol OH group, which corresponds to a shift in the x-ray absorption edge of the zinc atom. In the irreversible interaction regime, the effect of saturated alcohol vapor on spin-coated zinc phthalocyanine films was studied by the phase contrast microscopy, the optical absorption spectroscopy, and the transmission electron microscopy. Annealing the spin-coated films in saturated methanol vapor was found to induce an irreversible structural transformation from an amorphous to a crystalline phase, similar to the effect of a thermal annealing process. These crystallization processes of the zinc phthalocyanine films were also found to enhance their stability and alcohol sensing performance.

  8. Enzymatic conversion of atmospheric aldehydes into alcohol in a phospholipid polymer film.

    PubMed

    Tanaka, Naoki; Watari, Akihiro; Tada, Tomoko; Asada, Tomoko; Kunugi, Shigeru; Lee, Yin-Fai; Yamada, Satoshi; Shuto, Kenshiro; Sakaki, Shujiro

    2009-02-01

    We developed a unique method for converting atmospheric aldehyde into alcohol using formaldehyde dehydrogenase from Pseudomonas putida (PFDH) doped in a polymer film. A film of poly(2-methacryloyloxyethylphosphorylcholine-co-n-butyl methacrylate) (PMB), which has a chemical structure similar to that of a biological membrane, was employed for its biocompatibility. A water-incorporated polymer film entrapping PFDH and its cofactor NAD(+) was obtained by drying a buffered solution of PMB, PFDH, and NAD(+). The aldehydes in the air were absorbed into the polymer film and then enzymatically oxidized by PFDH doped in the PMB film. Interestingly, alcohol and carboxylic acid were produced by the enzymatic reaction, indicating that PFDH catalyzes dismutation of aldehyde in the PMB film. Importantly, a PFDH-PMB film catalyzes aldehyde degradation without consuming the nucleotide cofactor, thereby allowing repeated use of the film. The activity of PFDH in the PMB film was higher than that in other common water-soluble polymers, suggesting that the hydrational state in a phospholipid polymer matrix is suitable for enzymatic activity.

  9. Preparation and properties of poly(vinyl alcohol)/chitosan blend bionanocomposites reinforced with cellulose nanocrystals/ZnO-Ag multifunctional nanosized filler

    PubMed Central

    Azizi, Susan; Ahmad, Mansor Bin; Hussein, Mohd Zobir; Ibrahim, Nor Azowa; Namvar, Farideh

    2014-01-01

    A series of novel bionanocomposites were cast using different contents of zinc oxide-silver nanoparticles (ZnO-AgNPs) stabilized by cellulose nanocrystals (CNC) as multifunctional nanosized fillers in poly(vinyl alcohol)/chitosan (PVA/Cs) matrices. The morphological structure, mechanical properties, ultraviolet-visible absorption, and antimicrobial properties of the prepared films were investigated as a function of their CNC/ZnO-AgNP content and compared with PVA/chitosan/CNC bionanocomposite films. X-ray diffraction and field emission scanning electron microscopic analyses showed that the CNC/ZnO-AgNPs were homogeneously dispersed in the PVA/Cs matrix and the crystallinity increased with increasing nanosized filler content. Compared with pure PVA/Cs, the tensile strength and modulus in the films increased from 0.055 to 0.205 GPa and from 0.395 to 1.20 GPa, respectively. Ultraviolet and visible light can be efficiently absorbed by incorporating ZnO-AgNPs into a PVA/Cs matrix, suggesting that these bionanocomposite films show good visibility and ultraviolet-shielding effects. The bionanocomposite films had excellent antimicrobial properties, killing both Gram-negative Salmonella choleraesuis and Gram-positive Staphylococcus aureus. The enhanced physical properties achieved by incorporating CNC/ZnO-AgNPs could be beneficial in various applications. PMID:24790433

  10. Protein-resistant cross-linked poly(vinyl alcohol) micropatterns via photolithography using removable polyoxometalate photocatalyst.

    PubMed

    Pavli, Pagona; Petrou, Panagiota S; Douvas, Antonios M; Dimotikali, Dimitra; Kakabakos, Sotirios E; Argitis, Panagiotis

    2014-10-22

    In the last years, there has been an increasing interest in controlling the protein adsorption properties of surfaces because this control is crucial for the design of biomaterials. On the other hand, controlled immobilization of proteins is also important for their application as solid surfaces in immunodiagnostics and biosensors. Herein we report a new protein patterning method where regions of the substrate are covered by a hydrophilic film that minimizes protein adsorption. Particularly, poly(vinyl alcohol) (PVA) cross-linked structures created by an especially developed photolithographic process are proved to prevent protein physisorption and they are used as a guide for selective protein adsorption on the uncovered areas of a protein adsorbing substrate such as polystyrene. The PVA cross-linking is induced by photo-oxidation using, as a catalyst, polyoxometalate (H3PW12O40 or α-(NH4)6P2W18O62), which is removed using a methyl alcohol/water mixed solvent as the developer. We demonstrate that the polystyrene and the cross-linked PVA exhibit dramatically different performances in terms of protein physisorption. In particular, the polystyrene areas presented up to 130 times higher protein binding capacity than the PVA ones, whereas the patterning resolution could easily reach dimensions of a few micrometers. The proposed approach can be applied on any substrate where PVA films can be coated for controlling protein adsorption onto surface areas custom defined by the user.

  11. Alcohol

    MedlinePlus

    ... How Can I Help a Friend Who Cuts? Alcohol KidsHealth > For Teens > Alcohol Print A A A ... you can make an educated choice. What Is Alcohol? Alcohol is created when grains, fruits, or vegetables ...

  12. Properties of polyvinyl alcohol/xylan composite films with citric acid.

    PubMed

    Wang, Shuaiyang; Ren, Junli; Li, Weiying; Sun, Runcang; Liu, Shijie

    2014-03-15

    Composite films of xylan and polyvinyl alcohol were produced with citric acid as a new plasticizer or a cross-linking agent. The effects of citric acid content and polyvinyl alcohol/xylan weight ratio on the mechanical properties, thermal stability, solubility, degree of swelling and water vapor permeability of the composite films were investigated. The intermolecular interactions and morphology of composite films were characterized by FTIR spectroscopy and SEM. The results indicated that polyvinyl alcohol/xylan composite films had good compatibility. With an increase in citric acid content from 10% to 50%, the tensile strength reduced from 35.1 to 11.6 MPa. However, the elongation at break increased sharply from 15.1% to 249.5%. The values of water vapor permeability ranged from 2.35 to 2.95 × 10(-7)g/(mm(2)h). Interactions between xylan and polyvinyl alcohol in the presence of citric acid become stronger, which were caused by hydrogen bond and ester bond formation among the components during film forming.

  13. Biochemistry of microbial polyvinyl alcohol degradation.

    PubMed

    Kawai, Fusako; Hu, Xiaoping

    2009-08-01

    Effect of minor chemical structures such as 1,2-diol content, ethylene content, tacticity, a degree of polymerization, and a degree of saponification of the main chain on biodegradability of polyvinyl alcohol (PVA) is summarized. Most PVA-degraders are Gram-negative bacteria belonging to the Pseudomonads and Sphingomonads, but Gram-positive bacteria also have PVA-degrading abilities. Several examples show symbiotic degradation of PVA by different mechanisms. Penicillium sp. is the only reported eukaryotic degrader. A vinyl alcohol oligomer-utilizing fungus, Geotrichum fermentans WF9101, has also been reported. Lignolytic fungi have displayed non-specific degradation of PVA. Extensive published studies have established a two-step process for the biodegradation of PVA. Some bacteria excrete extracellular PVA oxidase to yield oxidized PVA, which is partly under spontaneous depolymerization and is further metabolized by the second step enzyme (hydrolase). On the other hand, PVA (whole and depolymerized to some extent) must be taken up into the periplasmic space of some Gram-negative bacteria, where PVA is oxidized by PVA dehydrogenase, coupled to a respiratory chain. The complete pva operon was identified in Sphingopyxis sp. 113P3. Anaerobic biodegradability of PVA has also been suggested.

  14. Influence of Cr2O3 nanoparticles on the physical properties of polyvinyl alcohol

    NASA Astrophysics Data System (ADS)

    Hassen, A.; El Sayed, A. M.; Morsi, W. M.; El-Sayed, S.

    2012-11-01

    Nano-sized chromium oxide (Cr2O3) was synthesized by sol-gel method and mixed with polyvinyl alcohol (PVA) to produce nanocomposite films. Scanning electron microscopy (SEM) was used to observe the morphology and dispersion of Cr2O3 on the surface of the PVA films. X-ray diffraction (XRD) was performed on nano-sized Cr2O3, pure PVA, and Cr2O3/PVA composites. Based on the results of both XRD and high-resolution transmission electron microscopy (HR-TEM), the average particle size of the Cr2O3 was ≈ 46 nm. Differential scanning calorimetry (DSC) showed that the thermal stability and degree of crystallinity of the PVA were reinforced by the addition of Cr2O3 nanoparticles. The absorbance and extinction coefficients of the composites were studied in the UV-vis range and compared with those of pure PVA. The optical energy band gap, Eg, was calculated. Dielectric constant, ɛ', dielectric loss modulus, M″, and ac conductivity, σac, of all samples were measured within temperature and frequency ranges of 300-468 K and 10 kHz-2 MHz, respectively. According to the frequency and temperature dependence of the dielectric loss modulus, M″, the observed α-relaxation peak was due to the micro-Brownian motion of the polymer main chains. The behavior of σac(f) for the composite films indicated that the conduction mechanism was correlated barrier hopping (CBH). The results of this work were discussed and compared with those of previous studies of PVA composites.

  15. PVA bio-nanocomposites: a new take-off using cellulose nanocrystals and PLGA nanoparticles.

    PubMed

    Rescignano, N; Fortunati, E; Montesano, S; Emiliani, C; Kenny, J M; Martino, S; Armentano, I

    2014-01-01

    The formation of a new generation of hybrid bio-nanocomposites is reported: these are intended at modulating the mechanical, thermal and biocompatibility properties of the poly(vinyl alcohol) (PVA) by the combination of cellulose nanocrystals (CNC) and poly (D,L-lactide-co-glycolide) (PLGA) nanoparticles (NPs) loaded with bovine serum albumin fluorescein isothiocynate conjugate (FITC-BSA). CNC were synthesized from microcrystalline cellulose by hydrolysis, while PLGA nanoparticles were produced by a double emulsion with subsequent solvent evaporation. Firstly, binary bio-nanocomposites with different CNC amounts were developed in order to select the right content of CNC. Next, ternary PVA/CNC/NPs bio-nanocomposites were developed. The addition of CNC increased the elongation properties without compromising the other mechanical responses. Thermal analysis underlined the nucleation effect of the synergic presence of cellulose and nanoparticles. Remarkably, bio-nanocomposite films are suitable to vehiculate biopolymeric nanoparticles to adult bone marrow mesenchymal stem cells successfully, thus representing a new tool for drug delivery strategies.

  16. In vitro release of salicylic acid from lanolin alcohols-ethylcellulose films.

    PubMed

    Khan, A R; Iyer, B V; Cirelli, R A; Vasavada, R C

    1984-03-01

    Lanolin alcohols-ethylcellulose films were investigated as a potential drug delivery system for the controlled release of salicylic acid. The effects of changes in film composition, drug concentration, drug solubility, and stirrer speed on the in vitro release of salicylic acid have been examined. The drug release has been found to obey a diffusion-controlled matrix model and square root of time release profile both in the suspension and solution cases.

  17. Fabrication of top-contact pentacene-based organic thin-film transistors with short channels using two-step SU8/poly(vinyl alcohol) lift-off photolithography process

    NASA Astrophysics Data System (ADS)

    Fan, Ching-Lin; Lin, Wei-Chun; Lee, Cheng-Chieh; Lin, Yu-Zuo; Huang, Bohr-Ran

    2016-02-01

    We propose a two-step SU8/poly(vinyl alcohol) (PVA) lift-off photolithography scheme for fabricating top-contact pentacene-based organic thin-film transistors (OTFTs) with small channels. The bilayer of PVA and SU8 will not damage the pentacene channel layer in the lift-off photolithography process used in forming the patterned pentacene channel layer and source/drain metal electrodes. We demonstrate a device that not only obtains a 5 µm short channel length for source/drain metal-electrode patterning but also avoids fringe current resulting from pentacene channel layer patterning. The field-effect mobility and threshold voltage of the pentacene-based OTFTs were changed from 0.29 to 0.12 cm2 V-1 s-1 and from -5.74 to -3.19 V by varying the channel length from 50 to 5 µm, respectively. The proposed scheme is a good candidate for use in the design and fabrication of high-performance short-channel organic electronics.

  18. Radiation grafting on natural films

    NASA Astrophysics Data System (ADS)

    Lacroix, M.; Khan, R.; Senna, M.; Sharmin, N.; Salmieri, S.; Safrany, A.

    2014-01-01

    Different methods of polymer grafting using gamma irradiation are reported in the present study for the preparation of newly functionalized biodegradable films, and some important properties related to their mechanical and barrier properties are described. Biodegradable films composed of zein and poly(vinyl alcohol) (PVA) were gamma-irradiated in presence of different ratios of acrylic acid (AAc) monomer for compatibilization purpose. Resulting grafted films (zein/PVA-g-AAc) had their puncture strength (PS=37-40 N mm-1) and puncture deformation (PD=6.5-9.8 mm) improved for 30% and 50% PVA in blend, with 5% AAc under 20 kGy. Methylcellulose (MC)-based films were irradiated in the presence of 2-hydroxyethyl methacrylate (HEMA) or silane, in order to determine the effect of monomer grafting on the mechanical properties of films. It was found that grafted films (MC-g-HEMA and MC-g-silane) using 35% monomer performed higher mechanical properties with PS values of 282-296 N mm-1 and PD of 5.0-5.5 mm under 10 kGy. Compatibilized polycaprolactone (PCL)/chitosan composites were developed via grafting silane in chitosan films. Resulting trilayer grafted composite film (PCL/chitosan-g-silane/PCL) presented superior tensile strength (TS=22 MPa) via possible improvement of interfacial adhesion (PCL/chitosan) when using 25% silane under 10 kGy. Finally, MC-based films containing crystalline nanocellulose (CNC) as a filling agent were prepared and irradiated in presence of trimethylolpropane trimethacrylate (TMPTMA) as a grafted plasticizer. Grafted films (MC-g-TMPTMA) presented superior mechanical properties with a TS of 47.9 MPa and a tensile modulus (TM) of 1792 MPa, possibly due to high yield formation of radicals to promote TMPTMA grafting during irradiation. The addition of CNC led to an additional improvement of the barrier properties, with a significant 25% reduction of water vapor permeability (WVP) of grafted films.

  19. Heat resistance poly(vinyl alcohol) hydrogel

    NASA Astrophysics Data System (ADS)

    Yoshii, F.; Makuuchi, K.; Darwis, D.; Iriawan, T.; Razzak, M. T.; Rosiak, Janusz M.

    1995-08-01

    Six methods were used to evaluate the heat resistance of poly(vinyl alcohol) (PVA) hydrogel prepared by a combination of electron beam irradiation and acetalization of PVA. The physical properties of the hydrogel depended on the degree of acetilization which was affected by content of water in PVA sheet of acetalization in formaldehyde solution at 60°C. It was found that the optimum water content was 20-30%. The acetalized PVA sheet gave maximum tensile strength in electron beams irradiation at 100 kGy. The tensile strength of the hydrogel film increased to 20 MPa from 14 MPa by the irradiation. Heat resistance of the hydrogel was evaluated by measuring the mechanical properties after sterilization in a steam autoclave at 121°C for 90 min. The tensile strength decreased to 10 MPa whereas the elongation at break increased to 300%. The tackiness of the hydrogel was improved by radiation grafting of acrylic acid. Wholesomeness of the hydrogel as a wound dressing was evaluated by attaching to a burn or wound of the back skin of marmots. Advantages of the hydrogel over a gauze dressing were homogeneous adhesion to the affected parts, easy removal without damage to renewed skin and slightly faster rate of reconstruction of the injured skin.

  20. The role of MgBr2 to enhance the ionic conductivity of PVA/PEDOT:PSS polymer composite

    PubMed Central

    Sheha, Eslam M.; Nasr, Mona M.; El-Mansy, Mabrouk K.

    2014-01-01

    A solid polymer electrolyte system based on poly(vinyl alcohol) (PVA) and poly(3,4-Etylenedioxythiophene):poly(styrenesulfonate) (PEDOT:PSS) complexed with magnesium bromide (MgBr2) salt was prepared using solution cast technique. The ionic conductivity is observed to increase with increasing MgBr2 concentration. The maximum conductivity was found to be 9.89 × 10−6 S/cm for optimum polymer composite film (30 wt.% MgBr2) at room temperature. The increase in the conductivity is attributed to the increase in the number of ions as the salt concentration is increased. This has been proven by dielectric studies. The increase in conductivity is also attributable to the increase in the fraction of amorphous region in the electrolyte films as confirmed by their structural, thermal, electrical and optical properties. PMID:26199746

  1. Fabrication of electrospun almond gum/PVA nanofibers as a thermostable delivery system for vanillin.

    PubMed

    Rezaei, Atefe; Tavanai, Hossein; Nasirpour, Ali

    2016-10-01

    In this study, the fabrication of vanillin incorporated almond gum/polyvinyl alcohol (PVA) nanofibers through electrospinning has been investigated. Electrospinning of only almond gum was proved impossible. It was found that the aqueous solution of almond gum/PVA (80:20, concentration=7% (w/w)) containing 3% (w/w) vanillin could have successfully electrospun to uniform nanofibers with diameters as low as 77nm. According to the thermal analysis, incorporated vanillin in almond gum/PVA nanofibers showed higher thermal stability than free vanillin, making this composite especially suitable for high temperature applications. XRD and FTIR analyses proved the presence of vanillin in the almond gum/PVA nanofibers. It was also found that vanillin was dispersed as big crystallites in the matrix of almond gum/PVA nanofibers. FTIR analysis showed almond gum and PVA had chemical cross-linking by etheric bonds between COH groups of almond gum and OH groups of PVA. Also, in the nanofibers, there were no major interaction between vanillin and either almond gum or PVA. PMID:27267574

  2. Fabrication of electrospun almond gum/PVA nanofibers as a thermostable delivery system for vanillin.

    PubMed

    Rezaei, Atefe; Tavanai, Hossein; Nasirpour, Ali

    2016-10-01

    In this study, the fabrication of vanillin incorporated almond gum/polyvinyl alcohol (PVA) nanofibers through electrospinning has been investigated. Electrospinning of only almond gum was proved impossible. It was found that the aqueous solution of almond gum/PVA (80:20, concentration=7% (w/w)) containing 3% (w/w) vanillin could have successfully electrospun to uniform nanofibers with diameters as low as 77nm. According to the thermal analysis, incorporated vanillin in almond gum/PVA nanofibers showed higher thermal stability than free vanillin, making this composite especially suitable for high temperature applications. XRD and FTIR analyses proved the presence of vanillin in the almond gum/PVA nanofibers. It was also found that vanillin was dispersed as big crystallites in the matrix of almond gum/PVA nanofibers. FTIR analysis showed almond gum and PVA had chemical cross-linking by etheric bonds between COH groups of almond gum and OH groups of PVA. Also, in the nanofibers, there were no major interaction between vanillin and either almond gum or PVA.

  3. Microstructure characteristics of concrete incorporating metakaolin and PVA fibers and influence on the compressive strength

    NASA Astrophysics Data System (ADS)

    Khan, Sadaqat Ullah; Shafiq, Nasir; Ayub, Tehmina

    2015-07-01

    In this paper, microstructure of concrete is investigated using metakaolin (MK) as cement replacing material and Polyvinyl Alcohol (PVA) fibers. Total ten (10) mixes of concrete are examined by varying PVA fiber aspect ratio. It was found that MK refines the pore structure, improves interfacial transition zone (ITZ) due to its pozzolanic effects, reduces portlandite (Ca(OH)2) content and bridges the gap between matrix and aggregates due to finer particle size. Due to improvement in ITZ, the compressive strength was improved. There was no indication of Ca(OH)2 around the PVA fibers in the presence of MK and the interface between the fiber and matrix was observed very narrow.

  4. Tobacco, Alcohol, and Other Risk Behaviors in Film: How Well Do MPAA Ratings Distinguish Content?

    PubMed Central

    Tickle, Jennifer J.; Beach, Michael L.; Dalton, Madeline L.

    2009-01-01

    To evaluate the usefulness of MPAA ratings for parental selection of appropriate films for children, the 100 top grossing movies each year from 1996 through 2004 (N=900) were content analyzed to measure risk behaviors in each film. More restrictive MPAA ratings (R and PG-13) were associated with increased mean seconds of portrayals of tobacco use, alcohol use, and sexual content; increased frequency of violent content; and increased salience of drug use. However, MPAA ratings did not clearly distinguish films based on tobacco or alcohol use. Fifty percent of R-rated movies contained 124 seconds or more of tobacco use, comparable to 26% of PG-13 and 17% of PG movies. Fifty percent of R-rated movies contained 162 seconds or more of alcohol use, comparable to 49% of PG-13 and 25% of PG movies. Because of the high degree of overlap in alcohol and tobacco content between rating categories, the MPAA rating system, as currently defined, is not adequate for parents who wish to limit their children’s exposure to tobacco or alcohol content in movies. PMID:20029709

  5. Size-dependent mechanical properties of PVA nanofibers reduced via air plasma treatment

    NASA Astrophysics Data System (ADS)

    Fu, Qiang; Jin, Yu; Song, Xuefeng; Gao, Jingyun; Han, Xiaobing; Jiang, Xingyu; Zhao, Qing; Yu, Dapeng

    2010-03-01

    Organic nanowires/fibers have great potential in applications such as organic electronics and soft electronic techniques. Therefore investigation of their mechanical performance is of importance. The Young's modulus of poly(vinyl alcohol) (PVA) nanofibers was analyzed by scanning probe microscopy (SPM) methods. Air plasma treatment was used to reduce the nanofibers to different sizes. Size-dependent mechanical properties of PVA nanofibers were studied and revealed that the Young's modulus increased dramatically when the scales became very small (<80 nm).

  6. PVA/K2Ti6O13 synthetic composite for dielectric applications

    NASA Astrophysics Data System (ADS)

    Pandey, Mayank; Joshi, Girish M.; Khutia, Moumita; Rao, N. Madhusudhana; Kaleemulla, S.; Ramesh Kumar, C.; Cuberes, M. Teresa

    2016-05-01

    We demonstrated the preparation of polyvinyl alcohol (PVA) /Potassium titanate (K2Ti6O13) synthetic composite by solution blending. The loading of K2Ti6O13 well dispersed in PVA and improved electrical performance. The dielectric constant and loss as a function of temperature were recorded under frequency (200Hz-1 kHz). The real dielectric constant value obtained is (ɛ=1000) feasible for various electronic and non-conventional energy applications.

  7. A new fabrication route for PVA/graphene platelets composites with enhanced functionalities

    NASA Astrophysics Data System (ADS)

    Lavecchia, Teresa; Tamburri, Emanuela; Angjellari, Mariglen; Savi, Damiano; Terranova, Maria Letizia

    2016-05-01

    This work deals with the synthesis and characterization of composites made of poly(vinyl alcohol) (PVA) and oxidized graphene platelets obtained from an ad hoc treatment of graphite. The composite is produced by a modified solution mixing procedure in which the in situ crosslinking of PVA with maleic anhydride has been carried out in the presence of the carbon filler. A complete characterization of the material is presented carried out by SEM, DTGA, Raman spectroscopy and I-V characteristics analysis.

  8. Linear Dichroism of Cyanine Dyes in Stretched Polyvinyl Alcohol Films: A Physical Chemistry Laboratory Experiment.

    ERIC Educational Resources Information Center

    Natarajan, L. V.; And Others

    1983-01-01

    Provides background information, procedures, and results of an undergraduate physical chemistry experiment on the polarization of absorption spectra of cyanine dyes in stretched polyvinyl alcohol films. The experiment gives a simple demonstration of the concept of linear dichromism and the validity of the TEM method used in the analyses. (JN)

  9. Alcohol vapor sensing by cadmium-doped zinc oxide thick films based chemical sensor

    NASA Astrophysics Data System (ADS)

    Zargar, R. A.; Arora, M.; Chackrabarti, S.; Ahmad, S.; Kumar, J.; Hafiz, A. K.

    2016-04-01

    Cadmium-doped zinc oxide nanoparticles were derived by simple chemical co-precipitation route using zinc acetate dihydrate and cadmium acetate dihydrate as precursor materials. The thick films were casted from chemical co-precipitation route prepared nanoparticles by economic facile screen printing method. The structural, morphological, optical and electrical properties of the film were characterized relevant to alcohol vapor sensing application by powder XRD, SEM, UV-VIS and DC conductivity techniques. The response and sensitivity of alcohol (ethanol) vapor sensor are obtained from the recovery curves at optimum working temperature range from 20∘C to 50∘C. The result shows that maximum sensitivity of the sensor is observed at 25∘C operating temperature. On varying alcohol vapor concentration, minor variation in resistance has been observed. The sensing mechanism of sensor has been described in terms of physical adsorption and chemical absorption of alcohol vapors on cadmium-doped zinc oxide film surface and inside film lattice network through weak hydrogen bonding, respectively.

  10. Formulation and in vitro characterization of novel sildenafil citrate-loaded polyvinyl alcohol-polyethylene glycol graft copolymer-based orally dissolving films.

    PubMed

    Xu, Li-Li; Shi, Li-Li; Cao, Qing-Ri; Xu, Wei-Juan; Cao, Yue; Zhu, Xiao-Yin; Cui, Jing-Hao

    2014-10-01

    This work was aimed to develop novel sildenafil citrate (SC)-loaded polyvinyl alcohol (PVA)-polyethylene glycol (PEG) graft copolymer (Kollicoat(®) IR)-based orally dissolving films (ODFs) using a solvent casting method. Formulation factors such as plasticizers and disintegrants were optimized on the basis of characteristics of blank ODFs. The SC-loaded ODF with a loading capacity up to 6.25mg in an area of 6 cm(2) was prepared and evaluated in terms of mechanical properties, disintegration time and dissolution rate. The physicochemical properties of drug-loaded ODF were also investigated using the scanning electron microscope (SEM), X-ray diffraction (XRD), differential scanning calorimetry (DSC) and Fourier transform infrared spectroscopy (FT-IR). The blank ODF composed of Kollicoat(®) IR, sodium alginate (ALG-Na) and glycerol (10:2:1.5, w/w) had a remarkably short disintegration time of about 20s. The SC-loaded ODF showed a delayed disintegration time (about 25s), but exhibited improved mechanical properties when compared to the blank ODF. SC was homogeneously dispersed throughout the ODF and the crystalline form of drug had been partly changed, existing strong hydrogen bonding between the drug and carriers. The Kollicoat(®) IR/ALG-Na based ODFs containing SC might be an alternative to conventional tablet for the treatment of male erectile dysfunction.

  11. Dyed-polyvinyl alcohol films: molecular weight and hydrolysis degree influence on optical recording

    NASA Astrophysics Data System (ADS)

    Solano, Cristina; Martinez-Ponce, Geminiano; Castañeda, Carlos

    2006-07-01

    An analysis of different polyvinyl alcohol films dyed with Malachite Green is presented. Absorbance and diffraction efficiency of holographic gratings are compared, taking as a parameter the molecular weight and hydrolysis degree of the polymer. It is observed that, using the same dye concentration, the absorption coefficient of the films increases as the molecular weight increases. The absorbance of these plates can be modified when exposed to UV light. In addition, it is found that for holographic recording there is an optimal dye-polymer system film.

  12. In-situ cross linking of polyvinyl alcohol. [application to battery separator films

    NASA Technical Reports Server (NTRS)

    Philipp, W. H.; Hsu, L. C.; Sheibley, D. W. (Inventor)

    1981-01-01

    A method of producing a crosslinked polyvinyl alcohol structure, such as a battery separator membrane or electrode envelope is described. An aqueous solution of a film-forming polyvinyl alcohol is admixed with an aldehyde crosslinking agent a basic pH to inhibit crosslinking. The crosslinking agent, perferably a dialdehyde such as glutaraldehyde, is used in an amount of from about 1/2 to about 20% of the theoretical amount required to crosslink all of the hydroxyl groups of the polymer. The aqueous admixture is formed into a desired physical shape, such as by casting a sheet of the solution. The sheet is then dried to form a self-supporting film. Crosslinking is then effected by immersing the film in aqueous acid solution. The resultant product has excellent properties for use as a battery separator.

  13. A tribo-mechanical analysis of PVA-based building-blocks for implementation in a 2-layered skin model.

    PubMed

    Morales Hurtado, M; de Vries, E G; Zeng, X; van der Heide, E

    2016-09-01

    Poly(vinyl) alcohol hydrogel (PVA) is a well-known polymer widely used in the medical field due to its biocompatibility properties and easy manufacturing. In this work, the tribo-mechanical properties of PVA-based blocks are studied to evaluate their suitability as a part of a structure simulating the length scale dependence of human skin. Thus, blocks of pure PVA and PVA mixed with Cellulose (PVA-Cel) were synthesised via freezing/thawing cycles and their mechanical properties were determined by Dynamic Mechanical Analysis (DMA) and creep tests. The dynamic tests addressed to elastic moduli between 38 and 50kPa for the PVA and PVA-Cel, respectively. The fitting of the creep compliance tests in the SLS model confirmed the viscoelastic behaviour of the samples with retardation times of 23 and 16 seconds for the PVA and PVA-Cel, respectively. Micro indentation tests were also achieved and the results indicated elastic moduli in the same range of the dynamic tests. Specifically, values between 45-55 and 56-81kPa were obtained for the PVA and PVA-Cel samples, respectively. The tribological results indicated values of 0.55 at low forces for the PVA decreasing to 0.13 at higher forces. The PVA-Cel blocks showed lower friction even at low forces with values between 0.2 and 0.07. The implementation of these building blocks in the design of a 2-layered skin model (2LSM) is also presented in this work. The 2LSM was stamped with four different textures and their surface properties were evaluated. The hydration of the 2LSM was also evaluated with a corneometer and the results indicated a gradient of hydration comparable to the human skin. PMID:27236420

  14. Alcohol

    MedlinePlus

    ... Text Size: A A A Listen En Español Alcohol Wondering if alcohol is off limits with diabetes? Most people with diabetes can have a moderate amount of alcohol. Research has shown that there can be some ...

  15. Alcohol

    MedlinePlus

    If you are like many Americans, you drink alcohol at least occasionally. For many people, moderate drinking ... risky. Heavy drinking can lead to alcoholism and alcohol abuse, as well as injuries, liver disease, heart ...

  16. Electrocatalytic Oxidation of Alcohols on Cu2O/Cu Thin Film Electrodeposited on Titanium Substrate

    NASA Astrophysics Data System (ADS)

    Bezghiche-Imloul, T.; Hammache-Makhloufi, H.; Ait Ahmed, N.

    2016-05-01

    A novel class of nanomaterials consisting of a composite thin film of cooper metal nanoparticles and cuprous oxide (Cu2O/Cu) for the catalytic electrooxidation of methanol, ethanol and ethylene glycol is considered here. The material was prepared by electrochemical deposition under a potentiostatic condition of -250mV vs saturated calomel electrode (SCE) from acetate bath at titanium substrate. The effect of electrodeposition time on the structure, composition and morphology of the deposit was investigated using X-ray diffraction (XRD) and scanning electron microscopy (SEM). The results indicated the formation of pure cuprous oxide Cu2O thin film at low electrodeposition time (5 min) and Cu2O oxide thin film decorated with Cu nanoparticles (Cu2O/Cu) at high electrodeposition time. The obtained Cu2O and Cu2O/Cu thin films were explored for the electrochemical oxidation of alcohols in 1 M NaOH alkaline medium using cyclic voltammetry (CV) method. The Cu2O/Cu thin film grown at electrodeposition time of 15 min shows the best electrocatalytic performance toward ethanol oxidation. The effect of concentration of alcohols on the oxidation reaction was studied by CV and chronoamperometry. It was found that the reaction is governed by an irreversible diffusion process. The promising electrocatalytic activity of the Cu2O/Cu electrode provides a new platform for the fabrication of high-performance thin films for alcohols oxidation in alkaline medium. Therefore, the Cu2O/Cu electrode is a suitable as a less expensive electrocatalyst for alcohols oxidation.

  17. Effect of incorporation of different modified Al2O3 nanoparticles on holographic characteristics of PVA/AA photopolymer composites.

    PubMed

    Li, Yunxi; Wang, Chunhui; Li, Hailong; Wang, Xiaoyi; Han, Junhe; Huang, Mingju

    2015-11-20

    Al2O3 nanoparticles modified with different chemical reagents, prepared by using three chemical dispersants [high definition (HD), sodium dodecyl benzene sulfonate, and cetyl trimethyl ammonium chloride], were doped into photopolymer films in a polyvinyl alcohol/acrylamide (PVA/AA) system, respectively. A 647 nm Ar-Kr laser was used to expose and study the holographic properties of the samples. The research shows that doping Al2O3 nanoparticles into PVA/AA photopolymer film leads to different levels of improvement of the holographic characteristics. The diffraction efficiency of the sample can be raised to 93.8%, the maximum refractive index modulation increased to 2.28×10(-3), the shrinkage can be depressed to 0.8%, and the Bragg mismatch is 0.04°, while the concentration of 10 nm Al2O3 nanoparticles modified by HD dispersant is 1.02×10(-3)  mol·L(-1). PMID:26836540

  18. Adsorption of anionic and cationic dyes by activated carbons, PVA hydrogels, and PVA/AC composite.

    PubMed

    Sandeman, Susan R; Gun'ko, Vladimir M; Bakalinska, Olga M; Howell, Carol A; Zheng, Yishan; Kartel, Mykola T; Phillips, Gary J; Mikhalovsky, Sergey V

    2011-06-15

    The textural and adsorption characteristics of a series of activated carbons (ACs), porous poly(vinyl alcohol) (PVA) gels, and PVA/AC composites were studied using scanning electron microscopy, mercury porosimetry, adsorption of nitrogen (at 77.4 K), cationic methylene blue (MB), anionic methyl orange (MO), and Congo red (CR) from the aqueous solutions. Dye-PVA-AC-water interactions were modeled using the semiempirical quantum chemical method PM6. The percentage of dye removed (C(rem)) by the ACs was close to 100% at an equilibrium concentration (C(eq)) of less than 0.1 mM but decreased with increasing dye concentration. This decrease was stronger at C(eq) of less than 1 mM, and C(rem) was less than 50% at a C(eq) of 10-20 mM. For PVA and the PVA/AC composite containing C-7, the C(rem) values were minimal (<75%). The free energy distribution functions (f(ΔG)) for dye adsorption include one to three peaks in the -ΔG range of 1-60 kJ/mol, depending on the dye concentration range used and the spatial, charge symmetry of the hydrated dye ions and the structural characteristics of the adsorbents. The f(ΔG) shape is most complex for MO with the most asymmetrical geometry and charge distribution and adsorbed at concentrations over a large C(eq) range. For symmetrical CR ions, adsorbed over a narrow C(eq) range, the f(ΔG) plot includes mainly one narrow peak. MB has a minimal molecular size at a planar geometry (especially important for effective adsorption in slit-shaped pores) which explains its greater adsorptive capacity over that of MO or CR. Dye adsorption was greatest for ACs with the largest surface area but as molecular size increases adsorption depends to a greater extent on the pore size distribution in addition to total and nanopore surface areas and pore volume.

  19. Adsorption of anionic and cationic dyes by activated carbons, PVA hydrogels, and PVA/AC composite.

    PubMed

    Sandeman, Susan R; Gun'ko, Vladimir M; Bakalinska, Olga M; Howell, Carol A; Zheng, Yishan; Kartel, Mykola T; Phillips, Gary J; Mikhalovsky, Sergey V

    2011-06-15

    The textural and adsorption characteristics of a series of activated carbons (ACs), porous poly(vinyl alcohol) (PVA) gels, and PVA/AC composites were studied using scanning electron microscopy, mercury porosimetry, adsorption of nitrogen (at 77.4 K), cationic methylene blue (MB), anionic methyl orange (MO), and Congo red (CR) from the aqueous solutions. Dye-PVA-AC-water interactions were modeled using the semiempirical quantum chemical method PM6. The percentage of dye removed (C(rem)) by the ACs was close to 100% at an equilibrium concentration (C(eq)) of less than 0.1 mM but decreased with increasing dye concentration. This decrease was stronger at C(eq) of less than 1 mM, and C(rem) was less than 50% at a C(eq) of 10-20 mM. For PVA and the PVA/AC composite containing C-7, the C(rem) values were minimal (<75%). The free energy distribution functions (f(ΔG)) for dye adsorption include one to three peaks in the -ΔG range of 1-60 kJ/mol, depending on the dye concentration range used and the spatial, charge symmetry of the hydrated dye ions and the structural characteristics of the adsorbents. The f(ΔG) shape is most complex for MO with the most asymmetrical geometry and charge distribution and adsorbed at concentrations over a large C(eq) range. For symmetrical CR ions, adsorbed over a narrow C(eq) range, the f(ΔG) plot includes mainly one narrow peak. MB has a minimal molecular size at a planar geometry (especially important for effective adsorption in slit-shaped pores) which explains its greater adsorptive capacity over that of MO or CR. Dye adsorption was greatest for ACs with the largest surface area but as molecular size increases adsorption depends to a greater extent on the pore size distribution in addition to total and nanopore surface areas and pore volume. PMID:21457992

  20. Environmentally friendly Zn0.75Cd0.25S/PVA heterosystem nanocomposite: UV-stimulated emission and absorption spectra

    NASA Astrophysics Data System (ADS)

    Imam, N. G.; Mohamed, Mohamed Bakr

    2016-02-01

    Zn0.75Cd0.25S nanoparticles prepared at different temperatures were composited with polyvinyl alcohol for functionalization it in wide spectrum of applications such as in photocatalysis. The nanostructure of the Zn0.75Cd0.25S mother phase is confirmed by X-ray diffraction in addition to absorption and fluorescence spectra. UV/VIS. measurements show that, the transmittance coefficient of Zn0.75Cd0.25S/PVA nanocomposite is lesser than that of pure PVA by 0.33% and varies upon increasing the preparation temperature; reaching a maximum value for the sample prepared at 300 °C. It was found that the optical band gap tunes with annealing temperature which, in turns, with particle size. The refractive index of the Zn0.75Cd0.25S/PVA nanocomposite films decrease with increasing wavelength and saturates at high wavelengths. The optical conductivity increases with increasing photon energy which may be due to the excitation of electrons by photon energy. The optical conductivity of Zn0.75Cd0.25S/PVA nanocomposite is lesser than that of pure PVA and it decreases as the preparation temperature of Zn0.75Cd0.25S nanoparticles in PVA matrix increases which could be related to the decrease in the extinction coefficient and the density of localized states in the gap. Abroad peak deconvoluted, by Gaussian fitting function, into two violet and blue colors was observed in the fluorescence spectra under UV light irradiation. The two emission bands are attributed to band edge emission and neutral oxygen vacancies respectively. Analysis of fluorescence (FL) spectra reveals quenching in FL intensity and a peak shifting towards the lower wavelength side with increasing the preparation temperature of the mother phase. The results suggest that the 200 °C Zn0.75Cd0.25S/PVA nanocomposites have been regarded as a promising candidate in many technical fields, such as photocatalytic hydrogen production and/or photocatalytic degradation of organic dyes under UV irradiation due to its high optical

  1. A sustainable slashing industry using biodegradable sizes from modified soy protein to replace petro-based poly(vinyl alcohol).

    PubMed

    Zhao, Yi; Zhao, Yuzhu; Xu, Helan; Yang, Yiqi

    2015-02-17

    Biodegradable sizing agents from triethanolamine (TEA) modified soy protein could substitute poly(vinyl alcohol)(PVA) sizes for high-speed weaving of polyester and polyester/cotton yarns to substantially decrease environmental pollution and impel sustainability of textile industry. Nonbiodegradable PVA sizes are widely used and mainly contribute to high chemical oxygen demand (COD) in textile effluents. It has not been possible to effectively degrade, reuse or replace PVA sizes so far. Soy protein with good biodegradability showed potential as warp sizes in our previous studies. However, soy protein sizes lacked film flexibility and adhesion for required high-speed weaving. Additives with multiple hydroxyl groups, nonlinear molecule, and electric charge could physically modify secondary structure of soy protein and lead to about 23.6% and 43.3% improvement in size adhesion and ability of hair coverage comparing to unmodified soy protein. Industrial weaving results showed TEA-soy protein had relative weaving efficiency 3% and 10% higher than PVA and chemically modified starch sizes on polyester/cotton fabrics, and had relative weaving efficiency similar to PVA on polyester fabrics, although with 3- 6% lower add-on. In addition, TEA-soy sizes had a BOD5/COD ratio of 0.44, much higher than 0.03 for PVA, indicating that TEA-soy sizes were easily biodegradable in activated sludge.

  2. Biodegradation behaviors and water adsorption of poly(vinyl alcohol)/starch/carboxymethyl cellulose/clay nanocomposites

    NASA Astrophysics Data System (ADS)

    Taghizadeh, Mohammad Taghi; Sabouri, Narges

    2013-09-01

    The focus of this work is to study the effect of sodium montmorillonite (MMT-Na) clay content on the rate and extent of enzymatic hydrolysis polyvinyl alcohol (PVA)/starch (S)/carboxymethyl cellulose (CMC) blends using enzyme cellulase. The rate of glucose production from each nanocomposite substrates was most rapid for the substrate without MMT-Na and decreased with the addition of MMT-Na for PVA/S/CMC blend (51.5 μg/ml h), PVA/S/CMC/1% MMT (45.4 μg/ml h), PVA/S/CMC/3% MMT (42.8 μg/ml h), and PVA/S/CMC/5% MMT (39.2 μg/ml h). The results of this study have revealed that films with MMT-Na content at 5 wt.% exhibited a significantly reduced rate and extent of hydrolysis. Enzymatic degradation behavior of MMT-Na containing nanocomposites of PVA/S/CMC was based on the determinations of weight loss and the reducing sugars. The degraded residues have been characterized by various analytical techniques, such as Fourier transform infrared spectroscopy, scanning electronic microscopy, and UV-vis spectroscopy.

  3. Spreading and recoil of a surfactant-containing water drop on glass-supported alcohol films.

    PubMed

    Chowdhury, Devasish; Sarkar, Surya Protim; Kalita, Dipankar; Sarma, Tridib Kumar; Paul, Anumita; Chattopadhyay, Arun

    2004-02-17

    In this paper we report the experimental observation of spreading and recoil of surfactant-containing water drops on various alcohol films supported on glass slides. The time evolution of spreading and recoil behavior was recorded by placing a web camera above the drop. We observed that the drop spread the fastest on CH3OH, followed by C2H5OH, and the slowest on i-PrOH. On the other hand, the recoil behavior was just the opposite. The drop recoiled the slowest on CH3OH and fastest on i-PrOH, while it recoiled in an intermediate time on C2H5OH. In addition, concentration of surfactant in the drop played a prominent role in the spreading and recoil time of the drop, with higher surfactant concentration making the drop spread and recoil faster. The time evolution of spreading velocity of the drop on different alcohol films at various surfactant concentrations occurred with a Gaussian distribution and the peak velocity was reached earliest on CH3OH followed by C2H5OH, while on i-PrOH it took the longest time. The recoil behavior was similar. The variation of velocity as a function of radius exhibited oscillatory behavior, indicating the existence of an interfacial phenomenon. We also report the observation that spreading of the drop occurred without observable fingering instability. Further, we observed by Fourier transform infrared (FTIR) spectroscopic measurements that the drop had mixed with the alcohol films as it spread. Miscibility of the alcohol in the film with the drop, alcohol evaporation cooling-induced temperature gradient, and Marangoni effect probably play important roles in the spreading and recoil behavior of the drop.

  4. Antibacterial silver nanoparticles in polyvinyl alcohol/sodium alginate blend produced by gamma irradiation.

    PubMed

    Eghbalifam, Naeimeh; Frounchi, Masoud; Dadbin, Susan

    2015-09-01

    Polyvinyl alcohol/sodium alginate/nano silver (PVA/SA/Ag) composite films were made by solution casting method. Gamma irradiation was used to synthesize silver nanoparticles in situ via reduction of silver nitrate without using harmful chemical agents for biomedical applications. UV-vis and XRD results demonstrated that spherical silver nanoparticles were produced even at low irradiation dose of 5 kGy. By increasing irradiation dose, more nanoparticles were synthesized while no PVA hydrogel was formed up to 15 kGy. Also the size of nanoparticles was reduced with increasing gamma dose evidenced by higher release rate of silver nanoparticles in lukewarm water and SEM images. Comparing SEM images with DLS results indicated good performance of PVA/SA as an efficient stabilizer in preventing agglomeration of the silver nanoparticles. Good miscibility of polyvinyl alcohol and sodium alginate observed on the SEM images was supported with FTIR spectroscopy. Upon addition of sodium alginate to polyvinyl alcohol and increasing silver nanoparticles, the melting peak shifted to lower temperature and crystallinity percent was decreased. Addition of sodium alginate led to remarkable increase in rigidity of PVA. The composites exhibited strong antibacterial activity against Staphylococcus aureus and Escherichia coli even at very low level of silver nanoparticles. PMID:26123816

  5. Antibacterial silver nanoparticles in polyvinyl alcohol/sodium alginate blend produced by gamma irradiation.

    PubMed

    Eghbalifam, Naeimeh; Frounchi, Masoud; Dadbin, Susan

    2015-09-01

    Polyvinyl alcohol/sodium alginate/nano silver (PVA/SA/Ag) composite films were made by solution casting method. Gamma irradiation was used to synthesize silver nanoparticles in situ via reduction of silver nitrate without using harmful chemical agents for biomedical applications. UV-vis and XRD results demonstrated that spherical silver nanoparticles were produced even at low irradiation dose of 5 kGy. By increasing irradiation dose, more nanoparticles were synthesized while no PVA hydrogel was formed up to 15 kGy. Also the size of nanoparticles was reduced with increasing gamma dose evidenced by higher release rate of silver nanoparticles in lukewarm water and SEM images. Comparing SEM images with DLS results indicated good performance of PVA/SA as an efficient stabilizer in preventing agglomeration of the silver nanoparticles. Good miscibility of polyvinyl alcohol and sodium alginate observed on the SEM images was supported with FTIR spectroscopy. Upon addition of sodium alginate to polyvinyl alcohol and increasing silver nanoparticles, the melting peak shifted to lower temperature and crystallinity percent was decreased. Addition of sodium alginate led to remarkable increase in rigidity of PVA. The composites exhibited strong antibacterial activity against Staphylococcus aureus and Escherichia coli even at very low level of silver nanoparticles.

  6. Bioadhesive film formed from a novel organic-inorganic hybrid gel for transdermal drug delivery system.

    PubMed

    Guo, Ruiwei; Du, Xiaoyan; Zhang, Rui; Deng, Liandong; Dong, Anjie; Zhang, Jianhua

    2011-11-01

    A novel organic-inorganic hybrid film-forming agent for TDDS was developed by a modified poly(vinyl alcohol) (PVA) gel using γ-(glycidyloxypropyl)trimethoxysilane (GPTMS) as an inorganic-modifying agent, poly(N-vinyl pyrrolidone) (PVP) as a tackifier and glycerol (GLY) as a plasticizer. The prepared gels can be applied to the skin by a coating method and in situ form very thin and transparent films with good performance, comfortable feel and cosmetic attractiveness. The key properties of the bioadhesive films produced from the hybrid gels were investigated and the results showed that the incorporation of appropriate GPTMS (GPTMS/(PVA+GPTMS) in the range of 20-30%) into the PVA matrix not only can significantly enhance mechanical strength and skin adhesion properties of the resultant film, but also can decrease the crystalline regions of PVA and hence facilitate the diffusion of water vapor and drug. Furthermore, the investigations into in vivo skin irritation suggested the films caused non-irritation to skin after topical application for 120 h. In conclusion, the bioadhesive films formed from organic-inorganic hybrid gels possessed very good qualities for application on the skin and may provide a promising formulation for TDDS, especially when the patient acceptability from an aesthetic perspective of the dosage form is a prime consideration. PMID:21723945

  7. Alcohol

    MedlinePlus

    ... Got Homework? Here's Help White House Lunch Recipes Alcohol KidsHealth > For Kids > Alcohol Print A A A Text Size What's in ... What Is Alcoholism? Say No en español El alcohol Getting the Right Message "Hey, who wants a ...

  8. Electroactive Film of Myoglobin Incorporated in a 3D-porous Calcium Alginate Film with Polyvinyl Alcohol, Glycerin and Gelatin.

    PubMed

    Zheng, Xueqin; Sun, Hong; Hou, Shifeng

    2015-01-01

    In this work, an electroactive porous Mb-CA's composite film was fabricated by incorporating myoglobin (Mb) in a three-dimension (3D) porous calcium alginate (CA) film with polyvinyl alcohol, glycerol, and gelatin. The porous Mb-CA's film modified electrodes exhibited a pair of well-defined, quasi-reversible cyclic voltammetric (CV) peaks at about -0.37 V vs. SCE in pH 7.0 buffers, characteristic of Mb heme Fe((III))/Fe((II)) redox couples. The electrochemical parameters, such as formal potentials (E(o')) and apparent heterogeneous electron-transfer rate constants (ks), were estimated by square-wave voltammetry with nonlinear regression analysis. The porous CA's composite film could form hydrogel in aqueous solution. The positions of the Soret absorbance band suggest that Mb in the CA's composite film kept its native states in the medium pH range. Hydrogen peroxide, oxygen, and nitrite were electrochemically catalyzed by the Mb-CA's composite film with significant lowering of the reduction overpotential.

  9. The feasibility of producing MWCNT paper and strong MWCNT film from VACNT array

    NASA Astrophysics Data System (ADS)

    Xu, Guanghui; Zhang, Qiang; Zhou, Weiping; Huang, Jiaqi; Wei, Fei

    2008-08-01

    This study sought to produce carbon nanotube (CNT) pulp out of extremely long, vertically aligned CNT arrays as raw materials. After high-speed shearing and mixing nitric acid and sulfuric acid, which served as the treatment, the researchers produced the desired pulp, which was further transformed into CNT paper by a common filtration process. The paper’s tensile strength, Young’s modulus and electrical conductivity were 7.5 MPa, 785 MPa and 1.0×104 S/m, respectively, when the temperature of the acid treatment was at 110°C. Apart from this, the researchers also improved the mechanical property of CNT paper by polymers. The CNT paper was soaked in polyethylene oxide, polyvinyl pyrrolidone, and polyvinyl alcohol (PVA) solution, eventually making the CNT/PVA film show its mechanical properties, which increased, while its electrical conductivity decreased. To diffuse the polymer into the CNT paper thoroughly, the researchers used vacuum filtration to fabricate a CNT/PVA film by penetrating PVA into the CNT paper. After a ten-hour filtration, the tensile strength and Young’s modulus of CNT/PVA film were 96.1 MPa and 6.23 GPa, respectively, which show an increase by factors of 12 and 7, respectively, although the material’s electrical conductivity was lowered to 0.16×104 S/m.

  10. Characterization and mechanical performance study of silk/PVA cryogels: towards nucleus pulposus tissue engineering.

    PubMed

    Neo, Puay Yong; Shi, Pujiang; Goh, James Cho-Hong; Toh, Siew Lok

    2014-10-20

    Poly (vinyl) alcohol (PVA) cryogels are reported in the literature for application in nucleus pulposus (NP) replacement strategies. However, these studies are mainly limited to acellular approaches-in part due to the high hydrophilicity of PVA gels that renders cellular adhesion difficult. Silk is a versatile biomaterial with excellent biocompatibility. We hypothesize that the incorporation of silk with PVA will (i) improve the cell-hosting abilities of PVA cryogels and (ii) allow better tailoring of physical properties of the composite cryogels for an NP tissue engineering purpose. 5% (wt/vol) PVA is blended with 5% silk fibroin (wt/vol) to investigate the effect of silk : PVA ratios on the cryogels' physical properties. Results show that the addition of silk results in composite cryogels that are able to swell to more than 10 times its original dry weight and rehydrate to at least 70% of its original wet weight. Adding at least 20% silk significantly improves surface hydrophobicity and is correlated with an improvement in cell-hosting abilities. Cell-seeded cryogels also display an increment in compressive modulus and hoop stress values. In all, adding silk to PVA creates cryogels that can be potentially used as NP replacements.

  11. Anti-plasticizing effect of amorphous indomethacin induced by specific intermolecular interactions with PVA copolymer.

    PubMed

    Ueda, Hiroshi; Aikawa, Shohei; Kashima, Yousuke; Kikuchi, Junko; Ida, Yasuo; Tanino, Tadatsugu; Kadota, Kazunori; Tozuka, Yuichi

    2014-09-01

    The mechanism of how poly(vinyl alcohol-co-acrylic acid-co-methyl methacrylate) (PVA copolymer) stabilizes an amorphous drug was investigated. Solid dispersions of PVA copolymer, poly(vinyl pyrrolidone) (PVP), and poly(vinyl pyrrolidone-co-vinyl acetate) (PVPVA) with indomethacin (IMC) were prepared. The glass transition temperature (Tg)-proportion profiles were evaluated by differential scanning calorimetry (DSC). General Tg profiles decreasing with the IMC ratio were observed for IMC-PVP and IMC-PVPVA samples. An interesting antiplasticizing effect of IMC on PVA copolymer was observed; Tg increased up to 20% IMC ratio. Further addition of IMC caused moderate reduction with positive deviation from theoretical values. Specific hydrophilic and hydrophobic interactions between IMC and PVA copolymer were revealed by infrared spectra. The indole amide of IMC played an important role in hydrogen bonding with PVA copolymer, but not with PVP and PVPVA. X-ray diffraction findings and the endotherm on DSC profiles suggested that PVA copolymer could form a semicrystalline structure and a possibility of correlation of the crystallographic nature with its low hygroscopicity was suggested. PVA copolymer was able to prevent crystallization of amorphous IMC through both low hygroscopicity and the formation of a specific intermolecular interaction compared with that with PVP and PVPVA.

  12. Characterization and mechanical performance study of silk/PVA cryogels: towards nucleus pulposus tissue engineering.

    PubMed

    Neo, Puay Yong; Shi, Pujiang; Goh, James Cho-Hong; Toh, Siew Lok

    2014-12-01

    Poly (vinyl) alcohol (PVA) cryogels are reported in the literature for application in nucleus pulposus (NP) replacement strategies. However, these studies are mainly limited to acellular approaches-in part due to the high hydrophilicity of PVA gels that renders cellular adhesion difficult. Silk is a versatile biomaterial with excellent biocompatibility. We hypothesize that the incorporation of silk with PVA will (i) improve the cell-hosting abilities of PVA cryogels and (ii) allow better tailoring of physical properties of the composite cryogels for an NP tissue engineering purpose. 5% (wt/vol) PVA is blended with 5% silk fibroin (wt/vol) to investigate the effect of silk : PVA ratios on the cryogels' physical properties. Results show that the addition of silk results in composite cryogels that are able to swell to more than 10 times its original dry weight and rehydrate to at least 70% of its original wet weight. Adding at least 20% silk significantly improves surface hydrophobicity and is correlated with an improvement in cell-hosting abilities. Cell-seeded cryogels also display an increment in compressive modulus and hoop stress values. In all, adding silk to PVA creates cryogels that can be potentially used as NP replacements. PMID:25329452

  13. Cytotoxicity associated with electrospun polyvinyl alcohol.

    PubMed

    Pathan, Saif G; Fitzgerald, Lisa M; Ali, Syed M; Damrauer, Scott M; Bide, Martin J; Nelson, David W; Ferran, Christiane; Phaneuf, Tina M; Phaneuf, Matthew D

    2015-11-01

    Polyvinyl alcohol (PVA) is a synthetic, water-soluble polymer, with applications in industries ranging from textiles to biomedical devices. Research on electrospinning of PVA has been targeted toward optimizing or finding novel applications in the biomedical field. However, the effects of electrospinning on PVA biocompatibility have not been thoroughly evaluated. In this study, the cytotoxicity of electrospun PVA (nPVA) which was not crosslinked after electrospinning was assessed. PVA polymers of several molecular weights were dissolved in distilled water and electrospun using the same parameters. Electrospun PVA materials with varying molecular weights were then dissolved in tissue culture medium and directly compared against solutions of nonelectrospun PVA polymer in human coronary artery smooth muscle cells and human coronary artery endothelial cells cultures. All nPVA solutions were cytotoxic at a threshold molar concentration that correlated with the molecular weight of the starting PVA polymer. In contrast, none of the nonelectrospun PVA solutions caused any cytotoxicity, regardless of their concentration in the cell culture. Evaluation of the nPVA material by differential scanning calorimetry confirmed that polymer degradation had occurred after electrospinning. To elucidate the identity of the nPVA component that caused cytotoxicity, nPVA materials were dissolved, fractionated using size exclusion columns, and the different fractions were added to HCASMC and human coronary artery endothelial cells cultures. These studies indicated that the cytotoxic component of the different nPVA solutions were present in the low-molecular-weight fraction. Additionally, the amount of PVA present in the 3-10 kg/mol fraction was approximately sixfold greater than that in the nonelectrospun samples. In conclusion, electrospinning of PVA resulted in small-molecular-weight fractions that were cytotoxic to cells. This result demonstrates that biocompatibility of electrospun

  14. A pilot-scale study on PVA gel beads based integrated fixed film activated sludge (IFAS) plant for municipal wastewater treatment.

    PubMed

    Kumar Singh, Nitin; Singh, Jasdeep; Bhatia, Aakansha; Kazmi, A A

    2016-01-01

    In the present study, a pilot-scale reactor incorporating polyvinyl alcohol gel beads as biomass carrier and operating in biological activated sludge mode (a combination of moving bed biofilm reactor (MBBR) and activated sludge) was investigated for the treatment of actual municipal wastewater. The results, during a monitoring period of 4 months, showed effective removal of chemical oxygen demand (COD), biological oxygen demand (BOD) and NH3-N at optimum conditions with 91%, ∼92% and ∼90% removal efficiencies, respectively. Sludge volume index (SVI) values of activated sludge varied in the range of 25-72 mL/g, indicating appreciable settling characteristics. Furthermore, soluble COD and BOD in the effluent of the pilot plant were reduced to levels well below discharge limits of the Punjab Pollution Control Board, India. A culture dependent method was used to enrich and isolate abundant heterotrophic bacteria in activated sludge. In addition to this, 16S rRNA genes analysis was performed to identify diverse dominant bacterial species in suspended and attached biomass. Results revealed that Escherichia coli, Pseudomonas sp. and Nitrosomonas communis played a significant role in biomass carrier, while Acinetobactor sp. were dominant in activated sludge of the pilot plant. Identification of ciliated protozoa populations rendered six species of ciliates in the plant, among which Vorticella was the most dominant. PMID:26744941

  15. Adsorption and Reaction of C1-C3 Alcohols over CeOx(111) Thin Films

    SciTech Connect

    D Mullins; S Senanayake; T Chen

    2011-12-31

    This study reports the interaction of methanol, ethanol, 1-propanol, and 2-propanol with well-ordered CeO{sub 2}(111) thin film surfaces. All of the alcohols adsorb at low temperature by forming alkoxy and hydroxyl species on the surface. On fully oxidized CeO{sub 2}(111), recombination occurs between some of the alkoxys and hydroxyls, resulting in alcohol desorption near 220 K. At the same temperature, some of the surface hydroxyls disproportionate to produce water and the loss of lattice O. The remaining alkoxys react above 550 K. The primary alcohols favor dehydrogenation products (aldehydes). There is a net loss of O from the system, resulting in a reduction of the ceria. The secondary alcohol, 2-propanol, undergoes primarily dehydration, producing propene with no net change in the cerium oxidation state. Reduced CeO{sub x}(111) competes with the gaseous products for available O. Little or no water is produced. The reaction selectivity for the C{sub 2} and C{sub 3} alcohols shifts toward favoring dehydration products. The loss of O from the alcohols leads to oxidation of the reduced ceria. Compared with the oxidized surface, the alkene desorption shifts to lower temperature, whereas the aldehyde desorption shifts to higher temperature. This indicates that, on the reduced surface, it is easier to break the C-O bond but more difficult to break the O-substrate bond.

  16. Fiber introduction mass spectrometry: determination of pesticides in herbal infusions using a novel sol-gel PDMS/PVA fiber for solid-phase microextraction.

    PubMed

    da Silva, Rogério Cesar; Zuin, Vânia Gomes; Yariwake, Janete Harumi; Eberlin, Marcos Nogueira; Augusto, Fabio

    2007-10-01

    An application of the direct coupling of solid-phase microextraction (SPME) with mass spectrometry (MS), a technique known as fiber introduction mass spectrometry (FIMS), is described to determine organochlorine (OCP) and organophosphorus (OPP) pesticides in herbal infusions of Passiflora L. A new fiber coated with a composite of poly(dimethylsiloxane) and poly(vinyl alcohol) (PDMS/PVA) was used. Sensitive, selective, simple and simultaneous quantification of several OCP and OPP was achieved by monitoring diagnostic fragment ions of m/z 266 (chlorothalonil), m/z 195 (alpha-endosulfan), m/z 278 (fenthion), m/z 263 (methyl parathion) and m/z 173 (malathion). Simple headspace SPME extraction (25 min) and fast FIMS detection (less than 40 s) of OCP and OPP from a highly complex herbal matrix provided good linearity with correlation coefficients of 0.991-0.999 for concentrations ranging from 10 to 140 ng ml(-1) of each compound. Good accuracy (80 to 110%), precision (0.6-14.9%) and low limits of detection (0.3-3.9 ng ml(-1)) were also obtained. Even after 400 desorption cycles inside the ionization source of the mass spectrometer, no visible degradation of the novel PDMS/PVA fiber was detected, confirming its suitability for FIMS. Fast (ca 20 s) pesticide desorption occurs for the PDMS/PVA fiber owing to the small thickness of the film and its reduced water sorption. PMID:17902108

  17. Excitation energy migration between elongated fluorophores in uniaxially oriented polyvinyl alcohol films

    NASA Astrophysics Data System (ADS)

    Bojarski, P.; Gryczyński, I.; Kułak, L.; Synak, A.; Barnett, A.

    2006-11-01

    Nonradiative multistep energy migration is studied for 3,3'-diethylthiacarbocyanine iodide (DTCI) in uniaxially stretched and unstretched poly(vinyl alcohol) films. The results of fluorescence anisotropy decay measurements were found to be extremely different for unstretched and (stretched) systems. For disordered systems, fast depolarization was observed due to effective energy migration between randomly distributed fluorophores. However, for partly ordered systems, much slower depolarization was found as a result of preferential angular distribution of transition dipole moments of identical fluorophores. These results and properties of energy transport in uniaxially stretched polymer films are analyzed using the technique of Monte-Carlo simulation.

  18. Polyaniline films photoelectrochemically reduce CO2 to alcohols.

    PubMed

    Hursán, Dorottya; Kormányos, Attila; Rajeshwar, Krishnan; Janáky, Csaba

    2016-07-01

    In this communication, we demonstrate that polyaniline, the very first example of an organic semiconductor, is a promising photocathode material for the conversion of carbon dioxide (CO2) to alcohol fuels. CO2 is a greenhouse gas; thus using solar energy to convert CO2 to transportation fuels (such as methanol or ethanol) is a value-added approach to simultaneous generation of alternative fuels and environmental remediation of carbon emissions. Insights into its unique behavior obtained from photoelectrochemical measurements and adsorption studies, together with spectroscopic data, are presented. Through a comparative study involving various conducting polymers, a set of criteria is developed for an organic semiconductor to function as a photocathode for generation of solar fuels from CO2. PMID:27345191

  19. Flexible all-solid-state supercapacitors based on graphene/carbon black nanoparticle film electrodes and cross-linked poly(vinyl alcohol)-H2SO4 porous gel electrolytes

    NASA Astrophysics Data System (ADS)

    Fei, Haojie; Yang, Chongyang; Bao, Hua; Wang, Gengchao

    2014-11-01

    Flexible all-solid-state supercapacitors (SCs) are fabricated using graphene/carbon black nanoparticle (GCB) film electrodes and cross-linked poly(vinyl alcohol)-H2SO4 porous gel electrolytes (gPVAP-H2SO4). The GCB composite films, with carbon black (CB) nanoparticles uniformly distributed in the graphene nanosheets, greatly improve the active surface areas and ion transportation of pristine graphene film. The porous structure of as-prepared gPVAP-H2SO4 membrane improves the equilibrium swelling ratio in electrolyte and provides interconnected ion transport channels. The chemical crosslinking solves the fluidity problem of PVA-H2SO4 gel electrolyte at high temperature. As-fabricated GCB//gPVAP(20)-H2SO4//GCB flexible SC displays an increased specific capacitance (144.5 F g-1 at 0.5 A g-1) and a higher specific capacitance retention (67.9% from 0.2 to 4 A g-1). More importantly, the flexible SC possesses good electrochemical performance at high temperature (capacitance retention of 78.3% after 1000 cycles at 70 °C).

  20. Influence of Al doping on optical properties of CdS/PVA nanocomposites: Theory and experiment

    SciTech Connect

    Bala, Vaneeta Tripathi, S. K. Kumar, Ranjan

    2014-04-24

    In the present work theoretical and experimental studies of aluminium doped cadmium sulphide polyvinyl alcohol (Al:CdS/PVA) nanocomposites have been carried out. Tetrahedral cluster AlCd{sub 9}S{sub 2}(SH){sub 18}]{sup 1−} has been encapsulated by small segments of polyvinyl alcohol (PVA) chains in order to simulate experimental environment of nanocomposites. Density functional theory (DFT) using local density approximation (LDA) functionals is employed to study the broadening of band gap upon ligation of nanoclusters. We have used in situ chemical route to synthesize nanocomposites. Optical band gap has been calculated from both experimental and theoretical approach.

  1. Unusual Morphologies of Poly(vinyl alcohol) Thin Films Adsorbed on Poly(dimethylsiloxane) Substrates.

    PubMed

    Karki, Akchheta; Nguyen, Lien; Sharma, Bhanushee; Yan, Yan; Chen, Wei

    2016-04-01

    Adsorption of poly(vinyl alcohol) (PVOH), 99% and 88% hydrolyzed poly(vinyl acetate), to poly(dimethylsiloxane) (PDMS) substrates was studied. The substrates were prepared by covalently attaching linear PDMS polymers of 2, 9, 17, 49, and 116 kDa onto silicon wafers. As the PDMS molecular weight/thickness increases, the adsorbed PVOH thin films progressively transition from continuous to discontinuous morphologies, including honeycomb and fractal/droplet. The structures are the result of thin film dewetting that occurs upon exposure to air. The PVOH film thickness does not vary significantly on these PDMS substrates, implicating the PDMS thickness as the cause for the morphology differences. The adsorbed PVOH thin films are less stable and have a stronger tendency to dewet on thicker, more liquid-like PDMS layers. When PVOH(99%) and PVOH(88%) thin films are compared, fractal and droplet morphologies are observed on high molecular weight PDMS substrates, respectively. The formation of the unique fractal features in the PVOH(99%) thin films as well as other crystalline and semicrystalline thin films is most likely driven by crystallization during the dehydration process in a diffusion-limited aggregation fashion. The only significant enhancement in hydrophilicity via PVOH adsorption was obtained on PDMS(2k), which is completely covered with a PVOH thin film. To mimic the lower receding contact angle and less liquid-like character of the PDMS(2k) substrate, light plasma treatment of the higher molecular weight PDMS substrates was carried out. On the treated PDMS substrates, the adsorbed PVOH thin films are in the more continuous honeycomb morphology, giving rise to significantly enhanced wettability. Furthermore, hydrophobic recovery of the hydrophilized PDMS substrates was not observed during a 1 week period. Thus, light plasma oxidation and subsequent PVOH adsorption can be utilized as a means to effectively hydrophilize conventional PDMS substrates. This study

  2. Enhanced Mechanical Properties in PVA/SWNT Composite Fibers

    NASA Astrophysics Data System (ADS)

    Sampson, William; Dalton, Alan

    2005-03-01

    Composite fibers of polyvinyl alcohol (PVA) and HiPco Single Walled Carbon Nanotubes (SWNT) have been developed at The University of Texas at Dallas that show greatly enhanced mechanical properties, with typical strengths of 1.8GPa and toughness in excess of that of spider silk, making these the toughest known fibers to date. However, the exact interactions leading to the enhanced mechanical properties are not as yet fully understood. We have used a series of Raman and DSC experiments to discover the nature of the strength-enhancing interactions in these composite materials. The results lead to the conclusion that the bulk of the improvements are due to SWNT-nucleated PVA crystallinity, with the SWNTs playing less of a direct role than we originally thought.

  3. Excitation energy migration in uniaxially oriented polymer films

    NASA Astrophysics Data System (ADS)

    Bojarski, P.; Kamińska, A.; Kułak, L.; Sadownik, M.

    2003-07-01

    Multistep nonradiative excitation energy transport is for the first time studied in uniaxially stretched polymer films. Concentration depolarization studies performed for 3,3 '-diethylthiacarbocyanine iodide (DTCI) for stretched (system I) and unstretched (system II) polyvinyl alcohol films (PVA) yield extremely different results. As expected, disordered system II exhibits strong concentration depolarization due to energy migration between identical fluorophores. However, for stretched films, concentration depolarization effect is much weaker and it occurs at higher dye concentrations compared to system II. This fact is mostly due to strongly modified angular distribution of dipole moments of molecules taking part in the excitation energy migration.

  4. Alcoholism

    PubMed Central

    Girard, Donald E.; Carlton, Bruce E.

    1978-01-01

    There are important measurements of alcoholism that are poorly understood by physicians. Professional attitudes toward alcoholic patients are often counterproductive. Americans spend about $30 billion on alcohol a year and most adults drink alcohol. Even though traditional criteria allow for recognition of the disease, diagnosis is often made late in the natural course, when intervention fails. Alcoholism is a major health problem and accounts for 10 percent of total health care costs. Still, this country's 10 million adult alcoholics come from a pool of heavy drinkers with well defined demographic characteristics. These social, cultural and familial traits, along with subtle signs of addiction, allow for earlier diagnosis. Although these factors alone do not establish a diagnosis of alcoholism, they should alert a physician that significant disease may be imminent. Focus must be directed to these aspects of alcoholism if containment of the problem is expected. PMID:685264

  5. Effects of silica nanoparticles on copper nanowire dispersions in aqueous PVA solutions

    NASA Astrophysics Data System (ADS)

    Lee, Seung Hak; Song, Hyeong Yong; Hyun, Kyu

    2016-05-01

    In this study, the effects of adding silica nanoparticles to PVA/CuNW suspensions were investigated rheologically, in particular, by small and large amplitude oscillatory shear (SAOS and LAOS) test. Interesting, the SAOS test showed the complex viscosities of CuNW/silica based PVA matrix were smaller than those of PVA/CuNW without silica. These phenomena show that nano-sized silica affects the dispersion of CuNW in aqueous PVA, which suggests small particles can prevent CuNW aggregation. Nonlinearity (third relative intensity ≡ I 3/1) was calculated from LAOS test results using Fourier Transform rheology (FT-rheology) and nonlinear linear viscoelastic ratio (NLR) value was calculated using the nonlinear parameter Q and complex modulus G*. Nonlinearity ( I 3/1) results showed more CuNW aggregation in PVA/CuNW without silica than in PVA/CuNW with silica. NLR (= [ Q 0( ϕ)/ Q 0(0)]/[ G*( ϕ)/ G*(0)]) results revealed an optimum concentration ratio of silica to CuNW to achieve a well-dispersed state. Degree of dispersion was assessed through the simple optical method. SAOS and LAOS test, and dried film morphologies showed nano-sized silica can improve CuNW dispersion in aqueous PVA solutions.

  6. Hemicelluloses/montmorillonite hybrid films with improved mechanical and barrier properties

    PubMed Central

    Chen, Ge-Gu; Qi, Xian-Ming; Li, Ming-Peng; Guan, Ying; Bian, Jing; Peng, Feng; Yao, Chun-Li; Sun, Run-Cang

    2015-01-01

    A facile and environmentally friendly method was introduced to incorporate montmorillonite (MMT) as an inorganic phase into quaternized hemicelluloses (QH) for forming hemicellulose-based films. Two fillers, polyvinyl alcohol (PVA) and chitin nanowhiskers (NCH), were added into the hemicelluloses/MMT hybrid matrices to prepare hybrid films, respectively. The hybrid films were nanocomposites with nacre-like structure and multifunctional characteristics including higher strength and good oxygen barrier properties via the electrostatic and hydrogen bonding interactions. The addition of PVA and NCH could induce changes in surface topography, and effectively enhance mechanical strength, thermal stability, transparency, and oxygen barrier properties. The tensile strengths of the composite films FPVA(0.3), FPVA(0.5), and FNCH(0.8) were 53.7, 46.3, and 50.1 MPa, respectively, which were 171%, 134%, and 153% larger than the FQH-MMT film (19.8 MPa). The tensile strength, and oxygen transmission rate of QH-MMT-PVA film were better than those of quaternized hemicelluloses/MMT films. Thus, the proper filler is very important for the strength of the hybrid film. These results provide insights into the understanding of the structural relationships of hemicellulose-based composite films in coating and packaging application for the future. PMID:26549418

  7. Hemicelluloses/montmorillonite hybrid films with improved mechanical and barrier properties

    NASA Astrophysics Data System (ADS)

    Chen, Ge-Gu; Qi, Xian-Ming; Li, Ming-Peng; Guan, Ying; Bian, Jing; Peng, Feng; Yao, Chun-Li; Sun, Run-Cang

    2015-11-01

    A facile and environmentally friendly method was introduced to incorporate montmorillonite (MMT) as an inorganic phase into quaternized hemicelluloses (QH) for forming hemicellulose-based films. Two fillers, polyvinyl alcohol (PVA) and chitin nanowhiskers (NCH), were added into the hemicelluloses/MMT hybrid matrices to prepare hybrid films, respectively. The hybrid films were nanocomposites with nacre-like structure and multifunctional characteristics including higher strength and good oxygen barrier properties via the electrostatic and hydrogen bonding interactions. The addition of PVA and NCH could induce changes in surface topography, and effectively enhance mechanical strength, thermal stability, transparency, and oxygen barrier properties. The tensile strengths of the composite films FPVA(0.3), FPVA(0.5), and FNCH(0.8) were 53.7, 46.3, and 50.1 MPa, respectively, which were 171%, 134%, and 153% larger than the FQH-MMT film (19.8 MPa). The tensile strength, and oxygen transmission rate of QH-MMT-PVA film were better than those of quaternized hemicelluloses/MMT films. Thus, the proper filler is very important for the strength of the hybrid film. These results provide insights into the understanding of the structural relationships of hemicellulose-based composite films in coating and packaging application for the future.

  8. Hemicelluloses/montmorillonite hybrid films with improved mechanical and barrier properties.

    PubMed

    Chen, Ge-Gu; Qi, Xian-Ming; Li, Ming-Peng; Guan, Ying; Bian, Jing; Peng, Feng; Yao, Chun-Li; Sun, Run-Cang

    2015-01-01

    A facile and environmentally friendly method was introduced to incorporate montmorillonite (MMT) as an inorganic phase into quaternized hemicelluloses (QH) for forming hemicellulose-based films. Two fillers, polyvinyl alcohol (PVA) and chitin nanowhiskers (NCH), were added into the hemicelluloses/MMT hybrid matrices to prepare hybrid films, respectively. The hybrid films were nanocomposites with nacre-like structure and multifunctional characteristics including higher strength and good oxygen barrier properties via the electrostatic and hydrogen bonding interactions. The addition of PVA and NCH could induce changes in surface topography, and effectively enhance mechanical strength, thermal stability, transparency, and oxygen barrier properties. The tensile strengths of the composite films FPVA(0.3), FPVA(0.5), and FNCH(0.8) were 53.7, 46.3, and 50.1 MPa, respectively, which were 171%, 134%, and 153% larger than the FQH-MMT film (19.8 MPa). The tensile strength, and oxygen transmission rate of QH-MMT-PVA film were better than those of quaternized hemicelluloses/MMT films. Thus, the proper filler is very important for the strength of the hybrid film. These results provide insights into the understanding of the structural relationships of hemicellulose-based composite films in coating and packaging application for the future. PMID:26549418

  9. Determination of glass transition temperature of reduced graphene oxide-poly(vinyl alcohol) composites using temperature dependent Fourier transform infrared spectroscopy

    NASA Astrophysics Data System (ADS)

    Mahendia, Suman; Heena; Kandhol, Geeta; Deshpande, Uday P.; Kumar, Shyam

    2016-05-01

    In the present work, structural properties of reduced graphene oxide (RGO) synthesized using modified Hummer's method and its composites with Poly(vinyl alcohol) (PVA) fabricated using solution-cast method have been studied. The structural properties of prepared samples have been systematically studied through UV-Visible absorption, Raman, Fourier Transform Infrared (FTIR) and Differential Scanning Calorimeter (DSC) spectroscopy. Infrared spectroscopy indicates the grafting of PVA chains with graphene layer through the formation of H-bonding linkage in the composites. Temperature-dependent FTIR spectra of PVA-RGO composite films were recorded to obtain the glass transition temperature (Tg) and to study its molecular origin. From these spectra the values of Tg were obtained using two-dimensional (2D) mapping of the first derivative of the absorbance intensity with respect to temperature (dA/dT), over the space of wavenumber and temperature. The value of Tg obtained for pure PVA increases from 78 °C to 92 °C after loading 0.5 wt.% of RGO in PVA and can be attributed to the strong H-bonding interaction between polymer chains and grafted solid surface of RGO. These results are in good agreement with those obtained from DSC analysis. This clearly indicates that the thermal behavior of PVA gets modified with loading of RGO.

  10. Simple and non-toxic fabrication of poly(vinyl alcohol)-patterned polymer surface for the formation of cell patterns

    NASA Astrophysics Data System (ADS)

    Hwang, In-Tae; Jin, Yu-Ran; Oh, Min-Suk; Jung, Chan-Hee; Choi, Jae-Hak

    2014-10-01

    In this study, a facile and non-toxic method for the formation of cell-adhesive poly(vinyl alcohol) (PVA) patterns on the surface of a non-biological polystyrene substrate (NPS) is developed to control cellular micro-organization. PVA thin films spin-coated onto the NPS are selectively irradiated with 150 keV H+ ions through a pattern mask and developed with deionized water to form negative-type PVA patterns. Well-defined stripe patterns of PVA with a width of 100 μm are created on the NPS at a higher fluence than 5 × 1015 ions/cm2, and their surface chemical compositions are changed by ion irradiation without any significant morphological change. Based on the results of the protein adsorption test and in vitro cell culture, cancer cells are preferentially adhered and proliferated onto the more hydrophilic PVA regions of the PVA-patterned NPS, resulting in well-defined cell patterns.

  11. Disposable urea biosensor based on nanoporous ZnO film fabricated from omissible polymeric substrate.

    PubMed

    Rahmanian, Reza; Mozaffari, Sayed Ahmad; Abedi, Mohammad

    2015-12-01

    In the present study, a facile and simple fabrication method of a semiconductor based urea biosensor was reported via three steps: (i) producing a ZnO-PVA composite film by means of a polymer assisted electrodeposition of zinc oxide (ZnO) on the F-doped SnO2 conducting glass (FTO) using water soluble polyvinyl alcohol (PVA), (ii) obtaining a nanoporous ZnO film by PVA omission via a subsequent post-treatment by annealing of the ZnO-PVA film, and (iii) preparation of a FTO/ZnO/Urs biosensor by exploiting a nanoporous ZnO film as an efficient and excellent platform area for electrostatic immobilization of urease enzyme (Urs) which was forced by the difference in their isoelectric point (IEP). The characterization techniques focused on the analysis of the ZnO-PVA film surfaces before and after annealing, which had a prominent effect on the porosity of the prepared ZnO film. The surface characterization of the nanostructured ZnO film by a field emission-scanning electron microscopy (FE-SEM), exhibited a film surface area as an effective bio-sensing matrix for enzyme immobilization. The structural characterization and monitoring of the biosensor fabrication was performed using UV-Vis, Fourier Transform Infrared (FT-IR), Raman Spectroscopy, Thermogravimetric Analysis (TGA), Cyclic Voltammetry (CV), and Electrochemical Impedance Spectroscopy (EIS) techniques. The impedimetric results of the FTO/ZnO/Urs biosensor showed a high sensitivity for urea detection within 8.0-110.0mg dL(-1) with the limit of detection as 5.0mg dL(-1).

  12. CMOS Alcohol Sensor Employing ZnO Nanowire Sensing Films

    NASA Astrophysics Data System (ADS)

    Santra, S.; Ali, S. Z.; Guha, P. K.; Hiralal, P.; Unalan, H. E.; Dalal, S. H.; Covington, J. A.; Milne, W. I.; Gardner, J. W.; Udrea, F.

    2009-05-01

    This paper reports on the utilization of zinc oxide nanowires (ZnO NWs) on a silicon on insulator (SOI) CMOS micro-hotplate for use as an alcohol sensor. The device was designed in Cadence and fabricated in a 1.0 μm SOI CMOS process at XFAB (Germany). The basic resistive gas sensor comprises of a metal micro-heater (made of aluminum) embedded in an ultra-thin membrane. Gold plated aluminum electrodes, formed of the top metal, are used for contacting with the sensing material. This design allows high operating temperatures with low power consumption. The membrane was formed by using deep reactive ion etching. ZnO NWs were grown on SOI CMOS substrates by a simple and low-cost hydrothermal method. A few nanometer of ZnO seed layer was first sputtered on the chips, using a metal mask, and then the chips were dipped in a zinc nitrate hexahydrate and hexamethylenetramine solution at 90° C to grow ZnO NWs. The chemical sensitivity of the on-chip NWs were studied in the presence of ethanol (C2H5OH) vapour (with 10% relative humidity) at two different temperatures: 200 and 250° C (the corresponding power consumptions are only 18 and 22 mW). The concentrations of ethanol vapour were varied from 175-1484 ppm (pers per million) and the maximum response was observed 40% (change in resistance in %) at 786 ppm at 250° C. These preliminary measurements showed that the on-chip deposited ZnO NWs could be a promising material for a CMOS based ethanol sensor.

  13. Poly(vinyl alcohol) composite films with high percent elongation prepared from amylose-fatty ammonium salt inclusion complexes

    Technology Transfer Automated Retrieval System (TEKTRAN)

    Amylose inclusion complexes prepared from cationic fatty ammonium salts and jet-cooked high amylose starch were combined with poly(vinyl alcohol) (PVOH) to form glycerol-plasticized films. Their tensile properties were compared with similar films prepared previously with analogous anionic fatty acid...

  14. A reduction of diffusion in PVA Fricke hydrogels

    NASA Astrophysics Data System (ADS)

    Smith, S. T.; Masters, K. S.; Hosokawa, K.; Blinco, J.; Crowe, S. B.; Kairn, T.; Trapp, J. V.

    2015-01-01

    A modification to the PVA-FX hydrogel whereby the chelating agent, xylenol orange, was partially bonded to the gelling agent, poly-vinyl alcohol, resulted in an 8% reduction in the post irradiation Fe3+ diffusion, adding approximately 1 hour to the useful timespan between irradiation and readout. This xylenol orange functionalised poly-vinyl alcohol hydrogel had an OD dose sensitivity of 0.014 Gy-1 and a diffusion rate of 0.133 mm2 h-1. As this partial bond yields only incremental improvement, it is proposed that more efficient methods of bonding xylenol orange to poly-vinyl alcohol be investigated to further reduce the diffusion in Fricke gels.

  15. Transarterial Embolization for Hepatocellular Carcinoma: A Comparison between Nonspherical PVA and Microspheres.

    PubMed

    Scaffaro, Leandro Armani; Kruel, Cleber Dario Pinto; Stella, Steffan Frosi; Gravina, Gabriela Leal; Machado Filho, Geraldo; Borges de Almeida, Carlos Podalirio; Pinto, Luiz Cezar Pontes Fonseca; Alvares-da-Silva, Mario Reis; Kruel, Cleber Rosito Pinto

    2015-01-01

    Transarterial chemoembolization (TACE) and transarterial embolization (TAE) have improved the survival rates of patients with unresectable hepatocellular carcinoma (HCC); however, the optimal TACE/TAE embolic agent has not yet been identified. The aim of this study was to compare the effect of two different embolic agents such as microspheres (ME) and polyvinyl alcohol (PVA) on survival, tumor response, and complications in patients with HCC submitted to transarterial embolization (TAE). Eighty HCC patients who underwent TAE between June 2008 and December 2012 at a single center were retrospectively studied. A total of 48 and 32 patients were treated with PVA and ME, respectively. There were no significant differences in survival (P = 0.679) or tumoral response (P = 0.369) between groups (PVA or ME). Overall survival rates at 12, 18, 24, 36, and 48 months were 97.9, 88.8, 78.9, 53.4, and 21.4% in the PVA-TAE group and 100, 92.9, 76.6, 58.8, and 58% in the ME-TAE group (P = 0.734). Patients submitted to TAE with ME presented postembolization syndrome more frequently when compared with the PVA group (P = 0.02). According to our cohort, the choice of ME or PVA as embolizing agent had no significant impact on overall survival.

  16. Transarterial Embolization for Hepatocellular Carcinoma: A Comparison between Nonspherical PVA and Microspheres.

    PubMed

    Scaffaro, Leandro Armani; Kruel, Cleber Dario Pinto; Stella, Steffan Frosi; Gravina, Gabriela Leal; Machado Filho, Geraldo; Borges de Almeida, Carlos Podalirio; Pinto, Luiz Cezar Pontes Fonseca; Alvares-da-Silva, Mario Reis; Kruel, Cleber Rosito Pinto

    2015-01-01

    Transarterial chemoembolization (TACE) and transarterial embolization (TAE) have improved the survival rates of patients with unresectable hepatocellular carcinoma (HCC); however, the optimal TACE/TAE embolic agent has not yet been identified. The aim of this study was to compare the effect of two different embolic agents such as microspheres (ME) and polyvinyl alcohol (PVA) on survival, tumor response, and complications in patients with HCC submitted to transarterial embolization (TAE). Eighty HCC patients who underwent TAE between June 2008 and December 2012 at a single center were retrospectively studied. A total of 48 and 32 patients were treated with PVA and ME, respectively. There were no significant differences in survival (P = 0.679) or tumoral response (P = 0.369) between groups (PVA or ME). Overall survival rates at 12, 18, 24, 36, and 48 months were 97.9, 88.8, 78.9, 53.4, and 21.4% in the PVA-TAE group and 100, 92.9, 76.6, 58.8, and 58% in the ME-TAE group (P = 0.734). Patients submitted to TAE with ME presented postembolization syndrome more frequently when compared with the PVA group (P = 0.02). According to our cohort, the choice of ME or PVA as embolizing agent had no significant impact on overall survival. PMID:26413523

  17. Effects of PVA-coated nanoparticles on human T helper cell activity.

    PubMed

    Strehl, Cindy; Schellmann, Saskia; Maurizi, Lionel; Hofmann-Amtenbrink, Margarethe; Häupl, Thomas; Hofmann, Heinrich; Buttgereit, Frank; Gaber, Timo

    2016-03-14

    Superparamagnetic iron oxide nanoparticles (SPION) are used as high-sensitive enhancer for magnetic resonance imaging, where they represent a promising tool for early diagnosis of destructive diseases such as rheumatoid arthritis (RA). Since we could demonstrate that professional phagocytes are activated by amino-polyvinyl-alcohol-coated-SPION (a-PVA-SPION), the study here focuses on the influence of a-PVA-SPION on human T cells activity. Therefore, primary human CD4+ T cells from RA patients and healthy subjects were treated with varying doses of a-PVA-SPION for 20h or 72h. T cells were then analyzed for apoptosis, cellular energy, expression of the activation marker CD25 and cell proliferation. Although, we observed that T cells from RA patients are more susceptible to low-dose a-PVA-SPION-induced apoptosis than T cells from healthy subjects, in both groups a-PVA-SPION do not activate CD4+ T cells per se and do not influence mitogen-mediated T cells activation with regard to CD25 expression and cell proliferation. Nevertheless, our results demonstrate that CD4+ T cells from RA patients and healthy subjects differ in their response to mitogen stimulation and oxygen availability. We conclude from our data, that a-PVA-SPION do neither activate nor significantly influence mitogen-stimulated CD4+ T cells activation and have negligible influence on T cells apoptosis. PMID:26774940

  18. Impermeable flexible liquid barrier film for encapsulation of DSSC metal electrodes

    NASA Astrophysics Data System (ADS)

    Yang, Junghee; Min, Misook; Yoon, Yeoheung; Kim, Won Jung; Kim, Sol; Lee, Hyoyoung

    2016-06-01

    Encapsulation of electronic devices such as dye-sensitized solar cells (DSSCs) is prone to degradation under normal atmospheric conditions, even with hermetic barriers on the metal electrodes. Overcoming this problem is crucial to increasing DSSC lifetimes and making them commercially viable. Herein, we report a new impermeable flexible liquid barrier film using polyvinyl alcohol (PVA) and partially reduced graphene oxide (PrGO), which dramatically enhances the lifetime of Ag metal electrodes (typically used in DSSCs) immersed in a highly acidic iodolyte solution. The Ag metal electrode encapsulated by the PVA/PrGO film survived for over 500 hrs, superior to existing barriers of glass frits, epoxy resins and polymers. The PVA/PrGO film strongly adheres to the Ag metal surface, and the resulting PVA/PrGO/Ag electrode is stable even on a curved substrate, with a sheet resistance nearly independent of curvature. These results give new insight for the design of high-performance and solution-processable flexible liquid barrier films for a wide range of applications, in particular for the encapsulation of electronic devices with liquid electrolytes.

  19. Impermeable flexible liquid barrier film for encapsulation of DSSC metal electrodes.

    PubMed

    Yang, Junghee; Min, Misook; Yoon, Yeoheung; Kim, Won Jung; Kim, Sol; Lee, Hyoyoung

    2016-01-01

    Encapsulation of electronic devices such as dye-sensitized solar cells (DSSCs) is prone to degradation under normal atmospheric conditions, even with hermetic barriers on the metal electrodes. Overcoming this problem is crucial to increasing DSSC lifetimes and making them commercially viable. Herein, we report a new impermeable flexible liquid barrier film using polyvinyl alcohol (PVA) and partially reduced graphene oxide (PrGO), which dramatically enhances the lifetime of Ag metal electrodes (typically used in DSSCs) immersed in a highly acidic iodolyte solution. The Ag metal electrode encapsulated by the PVA/PrGO film survived for over 500 hrs, superior to existing barriers of glass frits, epoxy resins and polymers. The PVA/PrGO film strongly adheres to the Ag metal surface, and the resulting PVA/PrGO/Ag electrode is stable even on a curved substrate, with a sheet resistance nearly independent of curvature. These results give new insight for the design of high-performance and solution-processable flexible liquid barrier films for a wide range of applications, in particular for the encapsulation of electronic devices with liquid electrolytes. PMID:27263654

  20. Impermeable flexible liquid barrier film for encapsulation of DSSC metal electrodes

    PubMed Central

    Yang, Junghee; Min, Misook; Yoon, Yeoheung; Kim, Won Jung; Kim, Sol; Lee, Hyoyoung

    2016-01-01

    Encapsulation of electronic devices such as dye-sensitized solar cells (DSSCs) is prone to degradation under normal atmospheric conditions, even with hermetic barriers on the metal electrodes. Overcoming this problem is crucial to increasing DSSC lifetimes and making them commercially viable. Herein, we report a new impermeable flexible liquid barrier film using polyvinyl alcohol (PVA) and partially reduced graphene oxide (PrGO), which dramatically enhances the lifetime of Ag metal electrodes (typically used in DSSCs) immersed in a highly acidic iodolyte solution. The Ag metal electrode encapsulated by the PVA/PrGO film survived for over 500 hrs, superior to existing barriers of glass frits, epoxy resins and polymers. The PVA/PrGO film strongly adheres to the Ag metal surface, and the resulting PVA/PrGO/Ag electrode is stable even on a curved substrate, with a sheet resistance nearly independent of curvature. These results give new insight for the design of high-performance and solution-processable flexible liquid barrier films for a wide range of applications, in particular for the encapsulation of electronic devices with liquid electrolytes. PMID:27263654

  1. Impermeable flexible liquid barrier film for encapsulation of DSSC metal electrodes.

    PubMed

    Yang, Junghee; Min, Misook; Yoon, Yeoheung; Kim, Won Jung; Kim, Sol; Lee, Hyoyoung

    2016-01-01

    Encapsulation of electronic devices such as dye-sensitized solar cells (DSSCs) is prone to degradation under normal atmospheric conditions, even with hermetic barriers on the metal electrodes. Overcoming this problem is crucial to increasing DSSC lifetimes and making them commercially viable. Herein, we report a new impermeable flexible liquid barrier film using polyvinyl alcohol (PVA) and partially reduced graphene oxide (PrGO), which dramatically enhances the lifetime of Ag metal electrodes (typically used in DSSCs) immersed in a highly acidic iodolyte solution. The Ag metal electrode encapsulated by the PVA/PrGO film survived for over 500 hrs, superior to existing barriers of glass frits, epoxy resins and polymers. The PVA/PrGO film strongly adheres to the Ag metal surface, and the resulting PVA/PrGO/Ag electrode is stable even on a curved substrate, with a sheet resistance nearly independent of curvature. These results give new insight for the design of high-performance and solution-processable flexible liquid barrier films for a wide range of applications, in particular for the encapsulation of electronic devices with liquid electrolytes.

  2. Livestock Air Treatment Using PVA-Coated Powdered Activated Carbon Biofilter

    Technology Transfer Automated Retrieval System (TEKTRAN)

    Ideal biofilter media provide surface for attachment of microorganisms responsible for removing air-born contaminants while facilitating passage of air. This study evaluated the efficacy of polyvinyl alcohol (PVA)-coated powdered activated carbon particles as a biofiltration medium. This material e...

  3. A comparison of flexural strengths of polymer (SBR and PVA) modified, roller compacted concrete

    PubMed Central

    Karadelis, John N.; Lin, Yougui

    2015-01-01

    This brief article aims to reveal the flexural performance, including the equivalent flexural strength of PVA (Polyvinyl Alcohol) modified concrete by comparing it primarily with that of SBR (Styrene Butadiene Rubber) concrete. This data article is directly related to Karadelis and Lin [6]. PMID:26306313

  4. Synergistic effect of ozonation and ionizing radiation for PVA decomposition.

    PubMed

    Sun, Weihua; Chen, Lujun; Zhang, Yongming; Wang, Jianlong

    2015-08-01

    Ozonation and ionizing radiation are both advanced oxidation processes (AOPs) without chemical addition and secondary pollution. Also, the two processes' efficiency is determined by different pH conditions, which creates more possibilities for their combination. Importantly, the combined process of ozonation and ionizing radiation could be suitable for treating wastewaters with extreme pH values, i.e., textile wastewater. To find synergistic effects, the combined process of ozonation and ionizing radiation mineralization was investigated for degradation of polyvinyl alcohol (PVA) at different pH levels. A synergistic effect was found at initial pH in the range 3.0-9.4. When the initial pH was 3.0, the combined process of ozonation and ionizing radiation gave a PVA mineralization degree of 17%. This was 2.7 times the sum achieved by the two individual processes, and factors of 2.1 and 1.7 were achieved at initial pH of 7.0 and 9.4, respectively. The combined process of ozonation and ionizing radiation was demonstrated to be a feasible strategy for treatment of PVA-containing wastewater. PMID:26257347

  5. Synergistic effect of ozonation and ionizing radiation for PVA decomposition.

    PubMed

    Sun, Weihua; Chen, Lujun; Zhang, Yongming; Wang, Jianlong

    2015-08-01

    Ozonation and ionizing radiation are both advanced oxidation processes (AOPs) without chemical addition and secondary pollution. Also, the two processes' efficiency is determined by different pH conditions, which creates more possibilities for their combination. Importantly, the combined process of ozonation and ionizing radiation could be suitable for treating wastewaters with extreme pH values, i.e., textile wastewater. To find synergistic effects, the combined process of ozonation and ionizing radiation mineralization was investigated for degradation of polyvinyl alcohol (PVA) at different pH levels. A synergistic effect was found at initial pH in the range 3.0-9.4. When the initial pH was 3.0, the combined process of ozonation and ionizing radiation gave a PVA mineralization degree of 17%. This was 2.7 times the sum achieved by the two individual processes, and factors of 2.1 and 1.7 were achieved at initial pH of 7.0 and 9.4, respectively. The combined process of ozonation and ionizing radiation was demonstrated to be a feasible strategy for treatment of PVA-containing wastewater.

  6. [Research on the treatment of wastewater containing PVA by ozonation-activated sludge process].

    PubMed

    Xing, Xiao-Qiong; Huang, Cheng-Lan; Liu, Min; Chen, Ying

    2012-11-01

    The wastewater containing polyvinyl alcohol (PVA) was characterized with poor biodegradability, and was difficult to remove. In order to find an economically reasonable and practical technology, the research on the removal efficiency of different concentration wastewater containing PVA by ozonation-activated sludge process was studied, and the result was compared with the traditional activated sludge process. The results showed that the ozonation-activated sludge process was not suitable for treating influent with COD below 500 mg x L(-1) and the wastewater PVA concentration was 10-30 mg x L(-1). When the influent COD was between 500-800 mg x L(-1) and the PVA concentration was 15-60 mg x L(-1), the system had advantages on dealing with this kind of wastewater, and the average removal efficiency of COD and PVA were 92.8% and 57.4%, which were better than the traditional activated sludge process 4.1% and 15.2% respectively. In addition, the effluent concentrations of COD could keep between 30-60 mg x L(-1). When the influent COD was 1 000-1 200 mg x L(-1) and the PVA concentration was 20-70 mg x L(-1), the average removal efficiencies of COD and PVA were 90.9% and 45.3%, which were better than the traditional activated sludge process 12.8% and 12.1% respectively, but the effluent should to be further treated. Compared with the traditional activated sludge process, ozonation-activated sludge process had high treatment efficiency, stable running effect, and effectively in dealing with industrial wastewater containing PVA. PMID:23323416

  7. Poly(vinyl alcohol)-based film potentially suitable for antimicrobial packaging applications.

    PubMed

    Musetti, Alessandro; Paderni, Katia; Fabbri, Paola; Pulvirenti, Andrea; Al-Moghazy, Marwa; Fava, Patrizia

    2014-04-01

    This work aimed at developing a thin and water-resistant food-grade poly(vinyl alcohol) (PVOH)-based matrix able to swell when in contact with high moisture content food products without rupturing to release antimicrobial agents onto the food surface. This film was prepared by blending PVOH and 7.20% (wt/wt of PVOH) of poly(ethylene glycol) (PEG) with citric acid as crosslinking agent. The film-forming solution was then casted onto a flat surface and the obtained film was 60 μm in thickness and showed a good transparency (close to T = 100%) in the visible region (400 to 700 nm). After immersion in water for 72 h at room temperature, the crosslinked matrix loses only 19.2% of its original weight (the percentage includes the amount of unreacted crosslinking agent, antimicrobial in itself). Water content, degree of swelling, and crosslinking density of the film prove that the presence of PEG diminishes the hydrophilic behavior of the material. Also the mechanical properties of the wet and dry film were assessed. Alongside this, 2.5% (wt/wt of dry film) of grapefruit seed extract (GSE), an antimicrobial agent, was added to the film-forming solution just before casting and the ability of the plastic matrix to release the additive was then evaluated in vitro against 2 GSE-susceptible microorganisms, Salmonella enteritidis and Listeria innocua. The results indicate that the developed matrix may be a promising food-grade material for the incorporation of active substances. PMID:24611868

  8. Improvement of Starch Digestion Using α-Amylase Entrapped in Pectin-Polyvinyl Alcohol Blend

    PubMed Central

    Cruz, Maurício; Fernandes, Kátia; Cysneiros, Cristine; Nassar, Reginaldo; Caramori, Samantha

    2015-01-01

    Polyvinyl alcohol (PVA) and pectin blends were used to entrap α-amylase (Termamyl) using glutaraldehyde as a cross-linker. The effect of glutaraldehyde concentration (0.25, 0.5, 0.75, 1.0, and 1.25%) on the activity of the immobilized enzyme and rate of enzyme released was tested during a 24 h period. Characteristics of the material, such as scanning electron microscopy (SEM), tensile strength (TS), elongation, and rate of dissolution in water (pH 5.7), ruminal buffering solution (pH 7.0), and reactor containing 0.1 mol L−1 sodium phosphate buffer (pH 6.5), were also analyzed. SEM results showed that the surfaces of the pectin/PVA/amylase films were highly irregular and rough. TS values increased as a function of glutaraldehyde concentration, whereas percentage of elongation (%E) decreased. Pectin/PVA/amylase films presented similar values of solubility in the tested solvents. The material obtained with 0.25% glutaraldehyde performed best with repeated use (active for 24 h), in a phosphate buffer reactor. By contrast, the material obtained with 1.25% glutaraldehyde presented higher performance during in vitro testing using an artificial rumen. The results suggest that pectin/PVA/amylase is a highly promising material for biotechnological applications. PMID:25949991

  9. Improvement of starch digestion using α-amylase entrapped in pectin-polyvinyl alcohol blend.

    PubMed

    Cruz, Maurício; Fernandes, Kátia; Cysneiros, Cristine; Nassar, Reginaldo; Caramori, Samantha

    2015-01-01

    Polyvinyl alcohol (PVA) and pectin blends were used to entrap α-amylase (Termamyl) using glutaraldehyde as a cross-linker. The effect of glutaraldehyde concentration (0.25, 0.5, 0.75, 1.0, and 1.25%) on the activity of the immobilized enzyme and rate of enzyme released was tested during a 24 h period. Characteristics of the material, such as scanning electron microscopy (SEM), tensile strength (TS), elongation, and rate of dissolution in water (pH 5.7), ruminal buffering solution (pH 7.0), and reactor containing 0.1 mol L(-1) sodium phosphate buffer (pH 6.5), were also analyzed. SEM results showed that the surfaces of the pectin/PVA/amylase films were highly irregular and rough. TS values increased as a function of glutaraldehyde concentration, whereas percentage of elongation (%E) decreased. Pectin/PVA/amylase films presented similar values of solubility in the tested solvents. The material obtained with 0.25% glutaraldehyde performed best with repeated use (active for 24 h), in a phosphate buffer reactor. By contrast, the material obtained with 1.25% glutaraldehyde presented higher performance during in vitro testing using an artificial rumen. The results suggest that pectin/PVA/amylase is a highly promising material for biotechnological applications.

  10. Improvement of starch digestion using α-amylase entrapped in pectin-polyvinyl alcohol blend.

    PubMed

    Cruz, Maurício; Fernandes, Kátia; Cysneiros, Cristine; Nassar, Reginaldo; Caramori, Samantha

    2015-01-01

    Polyvinyl alcohol (PVA) and pectin blends were used to entrap α-amylase (Termamyl) using glutaraldehyde as a cross-linker. The effect of glutaraldehyde concentration (0.25, 0.5, 0.75, 1.0, and 1.25%) on the activity of the immobilized enzyme and rate of enzyme released was tested during a 24 h period. Characteristics of the material, such as scanning electron microscopy (SEM), tensile strength (TS), elongation, and rate of dissolution in water (pH 5.7), ruminal buffering solution (pH 7.0), and reactor containing 0.1 mol L(-1) sodium phosphate buffer (pH 6.5), were also analyzed. SEM results showed that the surfaces of the pectin/PVA/amylase films were highly irregular and rough. TS values increased as a function of glutaraldehyde concentration, whereas percentage of elongation (%E) decreased. Pectin/PVA/amylase films presented similar values of solubility in the tested solvents. The material obtained with 0.25% glutaraldehyde performed best with repeated use (active for 24 h), in a phosphate buffer reactor. By contrast, the material obtained with 1.25% glutaraldehyde presented higher performance during in vitro testing using an artificial rumen. The results suggest that pectin/PVA/amylase is a highly promising material for biotechnological applications. PMID:25949991

  11. Development of clindamycin-loaded wound dressing with polyvinyl alcohol and sodium alginate.

    PubMed

    Kim, Jong Oh; Choi, Jun Young; Park, Jung Kil; Kim, Jeong Hoon; Jin, Sung Giu; Chang, Sun Woo; Li, Dong Xun; Hwang, Ma-Ro; Woo, Jong Soo; Kim, Jung-Ae; Lyoo, Won Seok; Yong, Chul Soon; Choi, Han-Gon

    2008-12-01

    To develop a clindamycin-loaded wound dressing, cross-linked hydrogel films were prepared using freeze-thawing method with various mixtures of polyvinyl alcohol (PVA) and sodium alginate (SA). The physicochemical properties such as swelling ratio, tensile strength and elongation of hydrogels were evaluated. The drug release from this clindamycin-loaded hydrogel, in vitro protein adsorption test and in vivo wound healing observations in rats were then performed. Increased SA concentration decreased the gelation %, maximum strength and break elongation, but it resulted into an increment in the swelling ability, elasticity and thermal stability of hydrogel film. However, SA had insignificant effect on the release of clindamycin. This hydrogel improved the healing rate of artificial wounds in rats. Thus, a clindamycin-loaded wound dressing with PVA and SA hydrogel should be a candidate for wound care.

  12. Comparative bio-safety and in vivo evaluation of native or modified locust bean gum-PVA IPN microspheres.

    PubMed

    Kaity, Santanu; Ghosh, Animesh

    2015-01-01

    Strategically developed natural polymer-based controlled release multiparticulate drug delivery systems have gained special interest for “spatial placement” and “temporal delivery” of drug molecules. In our earlier study, locust bean gum-poly(vinyl alcohol) interpenetrating polymer network (LBG-PVA IPN), carboxymethylated locust bean gum-poly(vinyl alcohol) interpenetrating polymer network (CMLBG-PVA IPN) and acrylamide grafted locust bean gum-poly(vinyl alcohol) interpenetrating polymer network (Am-g-LBG-PVA IPN) were prepared and characterized. The present study deals with accelerating stability testing, comparative bio-safety and single dose in vivo pharmacokinetic study of all three IPN microspheres for controlled oral delivery of buflomedil hydrochloride (BH). From the stability study, it was observed that the particles were stable throughout the study period. From toxicity and biodegradability study it was proved that the microspheres were safe for internal use and complied with bio-safety criterion. From the in vivo pharmacokinetic study in rabbits, it was observed that the CMLBG-PVA IPN microspheres possessed almost similar Tmax value with BH oral suspension. However, in comparison between the LBG-PVA and Am-g-LBG-PVA IPN microspheres, the later showed well controlled release property than the first in biological condition. Thus, this type of delivery system might be useful to achieve the lofty goals of the controlled release drug delivery.

  13. Comparative bio-safety and in vivo evaluation of native or modified locust bean gum-PVA IPN microspheres.

    PubMed

    Kaity, Santanu; Ghosh, Animesh

    2015-01-01

    Strategically developed natural polymer-based controlled release multiparticulate drug delivery systems have gained special interest for “spatial placement” and “temporal delivery” of drug molecules. In our earlier study, locust bean gum-poly(vinyl alcohol) interpenetrating polymer network (LBG-PVA IPN), carboxymethylated locust bean gum-poly(vinyl alcohol) interpenetrating polymer network (CMLBG-PVA IPN) and acrylamide grafted locust bean gum-poly(vinyl alcohol) interpenetrating polymer network (Am-g-LBG-PVA IPN) were prepared and characterized. The present study deals with accelerating stability testing, comparative bio-safety and single dose in vivo pharmacokinetic study of all three IPN microspheres for controlled oral delivery of buflomedil hydrochloride (BH). From the stability study, it was observed that the particles were stable throughout the study period. From toxicity and biodegradability study it was proved that the microspheres were safe for internal use and complied with bio-safety criterion. From the in vivo pharmacokinetic study in rabbits, it was observed that the CMLBG-PVA IPN microspheres possessed almost similar Tmax value with BH oral suspension. However, in comparison between the LBG-PVA and Am-g-LBG-PVA IPN microspheres, the later showed well controlled release property than the first in biological condition. Thus, this type of delivery system might be useful to achieve the lofty goals of the controlled release drug delivery. PMID:25307127

  14. Kinetic studies and performance evaluation of an anaerobic fixed-film reactor treating fuel alcohol wastewater

    SciTech Connect

    Gonzalez, R.A.

    1987-01-01

    This study was part of an extensive treatability study of the fuel alcohol wastewater generated at the OSU Agricultural Engineering Fuel Alcohol Research Facility. A bench-scale fixed-film upflow anaerobic reactor was operated for a period of over two years in order to collect the appropriate data for reliable design and operation of a full-scale fixed film anaerobic system. The biological kinetic constants for substrate removal, total gas production, and methane production were developed in terms of BOD{sub 5}, COD, and TOC, at two different temperatures, 36C and 25C. Shock loads studies were also performed, including organic shock loads, low temperature shocks, and shut-down (no feeding) periods. The alcohol wastewater can be easily treated using fixed-film upflow anaerobic reactor. The substrate removal characteristics were a function of the applied mass substrate loading. For applied mass substrate loading rates higher than 27 lbs BOD{sub 5} per day per 1000 sq. ft., the treatment efficiency and the gas production deteriorated, mainly due to accumulation of volatile fatty acids. The methane content of the gas decreased and the carbon dioxide content increased as the applied mass loading rates were increased up to around 12 lbs BOD{sub 5}/day/1000 sq. ft. at which point they leveled out 59% and 39%, respectively. The total gas production and the methane production were also a function of the applied mass substrate loading rate. The substrate removal kinetics and the gas kinetics were considerably different at the two temperatures. The reactor was able to successfully accommodate organic and low temperature shock loads, as well as, shut-down or no feeding periods.

  15. Preparation and characterization of chitosan/gelatin/PVA hydrogel for wound dressings.

    PubMed

    Fan, Lihong; Yang, Huan; Yang, Jing; Peng, Min; Hu, Jin

    2016-08-01

    Chitosan (CS)/gelatin (Gel)/polyvinyl alcohol (PVA) hydrogels were prepared by the gamma irradiation method for usage in wound dressing applications. Chitosan and gelatin solution was mixed with poly(vinyl alcohol) (PVA) solution at different weight ratios of CS/Gel of 1:3, 1:2, 1:1, 2:1 and 3:1. The hydrogels irradiated at 40kGy. The structure of the hydrogels was characterized by using FT-IR and SEM. The CS/Gel/PVA hydrogels were characterized for physical properties and blood clotting activity. The tensile strength of CS/Gel/PVA hydrogel enhanced than on the basis of the Gel/PVA hydrogel. The highest tensile strength reached the 2.2Mpa. All hydrogels have shown a good coagulation effect. It takes only 5min for the BCI index to reached 0.032 only 5min when the weight ratio of CS/Gel was 1:1. It means that the hemostatic effect of hydrogels were optimal. And the hydrogrls also showed good pH-sensitivity, swelling ability and water evaporation rate. Therefore, this hydrogel showed a promising potential to be applied as wound dressing. PMID:27112893

  16. Adsorption-stress relationship in drying of silica/PVA suspensions.

    PubMed

    Kim, Sunhyung; Sung, Jun Hee; Chun, Sangki; Ahn, Kyung Hyun; Lee, Seung Jong

    2011-09-15

    In this study, we investigated drying process of silica/PVA suspensions. After measuring the amount of polymer adsorption and the stress evolution of a film during drying process, we could find a quantitative relationship between polymer adsorption and stress development, for silica/PVA suspensions of different pH and mixing time. For all the suspensions of different pH, both the amount of polymer adsorption (Γ) and the plateau stress of dry film (σ(p)) could be scaled onto a single master curve as a function of mixing time (t(m)). The scaling of mixing time for both Γ and σ(p) could be performed by the same scale factor, which implies that there is a one to one correlation between adsorption and stress. This correlation implies that we can control the microstructure and performance of dry film by adjusting the amount of polymer adsorption. The origin of adsorption kinetics of silica/PVA suspension was also discussed in terms of saponification of acetate groups in PVA, which facilitates hydrogen bonding between silica and PVA.

  17. Flexible and conductive MXene films and nanocomposites with high capacitance

    SciTech Connect

    Ling, Zheng; Ren, Chang E.; Zhao, Meng-Qiang; Yang, Jian; Giammarco, James M.; Qiu, Jieshan; Barsoum, Michel W.; Gogotsi, Yury

    2014-11-11

    MXenes, a new family of 2D materials, combine hydrophilic surfaces with metallic conductivity. Delamination of MXene produces single-layer nanosheets with thickness of about a nanometer and lateral size of the order of micrometers. The high aspect ratio of delaminated MXene renders it promising nanofiller in multifunctional polymer nanocomposites. In this study, Ti3C2Tx MXene was mixed with either a charged polydiallyldimethylammonium chloride (PDDA) or an electrically neutral polyvinyl alcohol (PVA) to produce Ti3C2Tx/polymer composites. The as-fabricated composites are flexible and have electrical conductivities as high as 2.2 × 104 S/m in the case of the Ti3C2Tx/PVA composite film and 2.4 × 105 S/m for pure Ti3C2Tx films. The tensile strength of the Ti3C2Tx/PVA composites was significantly enhanced compared with pure Ti3C2Tx or PVA films. The intercalation and confinement of the polymer between the MXene flakes not only increased flexibility but also enhanced cationic intercalation, offering an impressive volumetric capacitance of ~530 F/cm3 for MXene/PVA-KOH composite film at 2 mV/s. Finally, to our knowledge, this study is a first, but crucial, step in exploring the potential of using MXenes in polymer-based multifunctional nanocomposites for a host of applications, such as structural components, energy storage devices, wearable electronics, electrochemical actuators, and radiofrequency shielding, to name a few.

  18. Flexible and conductive MXene films and nanocomposites with high capacitance

    DOE PAGES

    Ling, Zheng; Ren, Chang E.; Zhao, Meng-Qiang; Yang, Jian; Giammarco, James M.; Qiu, Jieshan; Barsoum, Michel W.; Gogotsi, Yury

    2014-11-11

    MXenes, a new family of 2D materials, combine hydrophilic surfaces with metallic conductivity. Delamination of MXene produces single-layer nanosheets with thickness of about a nanometer and lateral size of the order of micrometers. The high aspect ratio of delaminated MXene renders it promising nanofiller in multifunctional polymer nanocomposites. In this study, Ti3C2Tx MXene was mixed with either a charged polydiallyldimethylammonium chloride (PDDA) or an electrically neutral polyvinyl alcohol (PVA) to produce Ti3C2Tx/polymer composites. The as-fabricated composites are flexible and have electrical conductivities as high as 2.2 × 104 S/m in the case of the Ti3C2Tx/PVA composite film and 2.4 ×more » 105 S/m for pure Ti3C2Tx films. The tensile strength of the Ti3C2Tx/PVA composites was significantly enhanced compared with pure Ti3C2Tx or PVA films. The intercalation and confinement of the polymer between the MXene flakes not only increased flexibility but also enhanced cationic intercalation, offering an impressive volumetric capacitance of ~530 F/cm3 for MXene/PVA-KOH composite film at 2 mV/s. Finally, to our knowledge, this study is a first, but crucial, step in exploring the potential of using MXenes in polymer-based multifunctional nanocomposites for a host of applications, such as structural components, energy storage devices, wearable electronics, electrochemical actuators, and radiofrequency shielding, to name a few.« less

  19. Flexible and conductive MXene films and nanocomposites with high capacitance

    PubMed Central

    Ling, Zheng; Ren, Chang E.; Zhao, Meng-Qiang; Yang, Jian; Giammarco, James M.; Qiu, Jieshan; Barsoum, Michel W.; Gogotsi, Yury

    2014-01-01

    MXenes, a new family of 2D materials, combine hydrophilic surfaces with metallic conductivity. Delamination of MXene produces single-layer nanosheets with thickness of about a nanometer and lateral size of the order of micrometers. The high aspect ratio of delaminated MXene renders it promising nanofiller in multifunctional polymer nanocomposites. Herein, Ti3C2Tx MXene was mixed with either a charged polydiallyldimethylammonium chloride (PDDA) or an electrically neutral polyvinyl alcohol (PVA) to produce Ti3C2Tx/polymer composites. The as-fabricated composites are flexible and have electrical conductivities as high as 2.2 × 104 S/m in the case of the Ti3C2Tx/PVA composite film and 2.4 × 105 S/m for pure Ti3C2Tx films. The tensile strength of the Ti3C2Tx/PVA composites was significantly enhanced compared with pure Ti3C2Tx or PVA films. The intercalation and confinement of the polymer between the MXene flakes not only increased flexibility but also enhanced cationic intercalation, offering an impressive volumetric capacitance of ∼530 F/cm3 for MXene/PVA-KOH composite film at 2 mV/s. To our knowledge, this study is a first, but crucial, step in exploring the potential of using MXenes in polymer-based multifunctional nanocomposites for a host of applications, such as structural components, energy storage devices, wearable electronics, electrochemical actuators, and radiofrequency shielding, to name a few. PMID:25389310

  20. Unusual Morphologies of Poly(vinyl alcohol) Thin Films Adsorbed on Poly(dimethylsiloxane) Substrates.

    PubMed

    Karki, Akchheta; Nguyen, Lien; Sharma, Bhanushee; Yan, Yan; Chen, Wei

    2016-04-01

    Adsorption of poly(vinyl alcohol) (PVOH), 99% and 88% hydrolyzed poly(vinyl acetate), to poly(dimethylsiloxane) (PDMS) substrates was studied. The substrates were prepared by covalently attaching linear PDMS polymers of 2, 9, 17, 49, and 116 kDa onto silicon wafers. As the PDMS molecular weight/thickness increases, the adsorbed PVOH thin films progressively transition from continuous to discontinuous morphologies, including honeycomb and fractal/droplet. The structures are the result of thin film dewetting that occurs upon exposure to air. The PVOH film thickness does not vary significantly on these PDMS substrates, implicating the PDMS thickness as the cause for the morphology differences. The adsorbed PVOH thin films are less stable and have a stronger tendency to dewet on thicker, more liquid-like PDMS layers. When PVOH(99%) and PVOH(88%) thin films are compared, fractal and droplet morphologies are observed on high molecular weight PDMS substrates, respectively. The formation of the unique fractal features in the PVOH(99%) thin films as well as other crystalline and semicrystalline thin films is most likely driven by crystallization during the dehydration process in a diffusion-limited aggregation fashion. The only significant enhancement in hydrophilicity via PVOH adsorption was obtained on PDMS(2k), which is completely covered with a PVOH thin film. To mimic the lower receding contact angle and less liquid-like character of the PDMS(2k) substrate, light plasma treatment of the higher molecular weight PDMS substrates was carried out. On the treated PDMS substrates, the adsorbed PVOH thin films are in the more continuous honeycomb morphology, giving rise to significantly enhanced wettability. Furthermore, hydrophobic recovery of the hydrophilized PDMS substrates was not observed during a 1 week period. Thus, light plasma oxidation and subsequent PVOH adsorption can be utilized as a means to effectively hydrophilize conventional PDMS substrates. This study

  1. All-normal dispersion passively mode-locked Yb-doped fiber laser using MoS2-PVA saturable absorber

    NASA Astrophysics Data System (ADS)

    Sathiyan, S.; Velmurugan, V.; Senthilnathan, K.; Babu, P. Ramesh; Sivabalan, S.

    2016-05-01

    We demonstrate the generation of a dissipative soliton in an all-normal dispersion ytterbium (Yb)-doped fiber laser using few-layer molybdenum disulfide (MoS2) as a saturable absorber. The saturable absorber is prepared by mixing few-layer MoS2 solution with polyvinyl alcohol (PVA) to form a free-standing composite film. The modulation depth and saturation intensity of the MoS2-PVA film are 11% and 5.86 MW cm-2, respectively. By incorporating the MoS2 saturable absorber in the fiber laser cavity, the mode-locked pulses are generated with a pulse width of 1.55 ns and a 3 dB spectral bandwidth of 0.9 nm centered at 1037.5 nm. The fundamental repetition rate and the average power are measured as 15.43 MHz and 1.5 mW, respectively. These results reveal the feasibility of deploying liquid-phase exfoliated few-layer MoS2 nanosheets for dissipative soliton generation in the near-IR region.

  2. CIS(CIGS) thin films prepared for solar cells by one-step electrodeposition in alcohol solution

    NASA Astrophysics Data System (ADS)

    Long, Fei; Wang, Weiming; Du, Jingjing; Zou, Zhengguang

    2009-03-01

    The precursors of CIS and CIGS thin films were prepared by one-step electrodeposition in alcohol solution and then annealed in Ar atmosphere at 550°C for 30min. The influences of deposition potentials and salt concentrations on the morphology and composition of the thin films were studied in details. The films were characterized by X-ray diffraction(XRD), scanning electron microscopy(SEM), and energy-dispersive X-ray spectroscopy(EDS). The results show that annealed films have pure CIS or CIGS phases with good crystallization and the morphology of the films are very uniform and dense. The high quality precursor films were obtained using optimized deposition parameters. Moreover the electrodeposition mechanism of CIS thin films was briefly discussed.

  3. Characterization of nanocellulose reinforced semi-interpenetrating polymer network of poly(vinyl alcohol) & polyacrylamide composite films.

    PubMed

    Mandal, Arup; Chakrabarty, Debabrata

    2015-12-10

    Semi-interpenetrating polymer network (semi-IPN) of poly(vinyl alcohol)/polyacrylamide was reinforced with various doses of nanocellulose. The different composite films thus prepared were characterized with respect to their mechanical, thermal, morphological and barrier properties. The composite film containing 5 wt.% of nanocellulose showed the highest tensile strength. The semi-interpenetrating polymer network of poly(vinyl alcohol)/polyacrylamide; and its various composites with nanocellulose were almost identical in their thermal stability. Each of the composites however exhibited much superior stability with respect to the linear poly(vinyl alcohol) and crosslinked polyacrylamide. The scanning electron microscopy (SEM) and atomic force microscopy (AFM) studies exhibited phase separated morphology where agglomerates of nanocellulose were found to be dispersed in the matrix of the semi-IPN. The moisture vapor transmission rate (MVTR) was the lowest for the film containing 5 wt.% of nanocellulose. PMID:26428121

  4. Physicochemical properties of biodegradable polyvinyl alcohol-agar films from the red algae Hydropuntia cornea.

    PubMed

    Madera-Santana, Tomás J; Robledo, Daniel; Freile-Pelegrín, Yolanda

    2011-08-01

    Agar obtained from the red alga Hydropuntia cornea was blended with polyvinyl alcohol (PVOH) in order to produce biodegradable films. In this study, we compare the properties of biopolymeric films formulated with agars extracted from H. cornea collected at different seasons (rainy and dry) in the Gulf of Mexico coast and PVOH as synthetic matrix. The films were prepared at different agar contents (0%, 25%, 50%, 75%, and 100%) and their optical, mechanical, thermal, and morphological properties analyzed. The tensile strength of PVOH-agar films increased when agar content was augmented. The formulation with 50% agar from rainy season (RS) had a significant higher tensile strength when compared to those from dry season (DS; p < 0.05). Tensile modulus also displayed an increasing trend and likewise, for 50% and 75% agar blends from RS showed higher values than those from DS (p < 0.05). In contrast, elongation at break decreased as the agar content increased, independently of the season. Environmental scanning electron microscopy images of PVOH-agar 75% biofilms from RS showed a homogeneous structure with good interfacial adhesion between the two components. The changes evidenced in the FTIR spectrum of this blend suggest that hydrogen bonding is taking place between the agar ether linkages (C-O-C) and the hydroxyl groups (OH) of the PVOH. Based on the above mentioned results, blends of PVOH and 75% agar from H. cornea collected in rainy season showed good properties for applications in the biodegradable packaging industry.

  5. Marangoni spreading due to a localized alcohol supply on a thin water film

    NASA Astrophysics Data System (ADS)

    Hernández-Sánchez, José Federico; Eddi, Antonin; Snoeijer, J. H.

    2015-03-01

    Bringing two miscible fluids into contact naturally generates strong gradients in surface tension. Here, we investigate such a Marangoni-driven flow by continuously supplying isopropyl alcohol (IPA) on a film of water, using micron-sized droplets of IPA-water mixtures. These droplets create a localized depression in surface tension that leads to the opening of a circular, thin region in the water film. At the edge of the thin region, there is a growing rim that collects the water of the film, reminiscent of Marangoni spreading due to locally deposited surfactants. In contrast to the surfactant case, the driving by IPA-water drops gives rise to a dynamics of the thin zone that is independent of the initial layer thickness. The radius grows as r ˜ t1/2, which can be explained from a balance between Marangoni and viscous stresses. We derive a scaling law that accurately predicts the influence of the IPA flux as well as the thickness of the thin film at the interior of the spreading front.

  6. Covalent immobilization of lysozyme on ethylene vinyl alcohol films for nonmigrating antimicrobial packaging applications.

    PubMed

    Muriel-Galet, V; Talbert, J N; Hernandez-Munoz, P; Gavara, R; Goddard, J M

    2013-07-10

    The objective of this study was to develop a new antimicrobial film, in which lysozyme was covalently attached onto two different ethylene vinyl alcohol copolymers (EVOH 29 and EVOH 44). The EVOH surface was modified with UV irradiation treatment to generate carboxylic acid groups, and lysozyme was covalently attached to the functionalized polymer surface. Surface characterization of control and modified films was performed using attenuated total reflectance Fourier transform infrared spectroscopy (ATR-FTIR) and dye assay. The value of protein loading after attachment on the surface was 8.49 μg protein/cm(2) and 5.74 μg protein/cm(2) for EVOH 29 and EVOH 44, respectively, after 10 min UV irradiation and bioconjugation. The efficacy of the EVOH-lysozyme films was assessed using Micrococcus lysodeikticus. The antimicrobial activity of the films was tested against Listeria monocytogenes and was similar to an equivalent amount of free enzyme. The reduction was 1.08 log for EVOH 29-lysozyme, 0.95 log for EVOH 44-lysozyme, and 1.34 log for free lysozyme. This work confirmed the successful use of lysozyme immobilization on the EVOH surface for antimicrobial packaging.

  7. Oxidative Mineralization and Characterization of Polyvinyl Alcohol Solutions for Wastewater Treatment

    SciTech Connect

    Oji, L.N.

    1999-08-31

    The principal objectives of this study are to identify an appropriate polyvinyl alcohol (PVA) oxidative mineralization technique, perform compatibility and evaporation fate tests for neat and mineralized PVA, and determine potential for PVA chemical interferences which may affect ion exchange utilization for radioactive wastewater processing in the nuclear industry.

  8. Alcohol.

    ERIC Educational Resources Information Center

    Schibeci, Renato

    1996-01-01

    Describes the manufacturing of ethanol, the effects of ethanol on the body, the composition of alcoholic drinks, and some properties of ethanol. Presents some classroom experiments using ethanol. (JRH)

  9. Anisotropic optical properties of oriented silver nanorice and nanocarrots in stretched polymer films

    NASA Astrophysics Data System (ADS)

    Tong, Xia; Liang, Hongyan; Liu, Yanlong; Tan, Long; Ma, Dongling; Zhao, Yue

    2015-05-01

    Stretching-induced orientation of both silver nanorice and silver nanocarrots dispersed in or deposited on the surface of poly(vinyl alcohol) (PVA) films was investigated using polarized UV-visible-near-infrared (NIR) spectroscopy and atomic force microscopy (AFM). The results show that the film stretching not only aligns the long axis of individual nanorice or nanocarrots preferentially along the stretching direction, but also induces assembly of these nanostructures into oriented arrays of random lengths in the deformation process. Consequently, the longitudinal surface plasmon resonance peaked at 820 nm for nanorice and 1050 nm for nanocarrots before stretching can be replaced by continuous extinction over the entire 800-1800 nm NIR spectral range after stretching. Stretched PVA films containing either silver nanorice or nanocarrots thus display polarization-dependent transmission of NIR light.

  10. Multiferroic properties of stretchable BiFeO3 nano-composite film

    NASA Astrophysics Data System (ADS)

    Hwang, J. S.; Cho, J. Y.; Park, S. Y.; Yoo, Y. J.; Yoo, P. S.; Lee, B. W.; Lee, Y. P.

    2015-02-01

    We present a simple drop-casting method for preparing multiferroic nano-composite film where BiFeO3 (BFO) nanoparticles (NPs) were evenly dispersed into polyvinyl alcohol (PVA) polymer. BFO NPs used in this work were synthesized by the conventional sol-gel method, having diameter of tens of nm and being in good crystallinity. The BFO NPs were loaded into a highly insulating PVA polymer solution as filler. The multiferroic properties of the film reveal ferromagnetic ordering due to the uncompensated spiral ordering and saturated ferroelectric curves due to the cut-off of current leakage. Moreover, the prepared films show high flexibility and their multiferroicities are preserved well even in a high curved condition, reflecting the possibility for fabricating wearable devices based on multiferroic materials.

  11. Low-threshold Optical limiting and Nonlinear refraction in Nanocomposite films of Light Green dye-polymer system

    NASA Astrophysics Data System (ADS)

    Sreeja, S.; Louie Frobel, P. G.; Mayadevi, S.; Suresh, S. R.; Muneera, C. I.

    2015-02-01

    Poly(vinyl alcohol) (PVA) /Light Green (LG) dye nanocomposites were fabricated and their structure, microstructure, linear and nonlinear optical properties were investigated. The samples were characterized as nanocomposites with dye molecules encapsulated between the larger molecules (molecular chains) of the polymer host PVA. The nonlinear refraction behaviour was investigated employing the Z-scan technique, using a continuous wave (cw) He- Ne laser operating at 632.8 nm, as the excitation source. The samples displayed negative nonlinear refraction (self-defocusing) under the experimental conditions. Low-threshold optical limiting behaviour exhibited by the PVA based nanocomposites was demonstrated using an aperture limited geometry. The low limiting thresholds (~4 mW and ~2.4 mW) observed for the samples indicate that these low cost and durable nanocomposite films are potential media for optical limiting application under cw laser light excitation.

  12. A novel transdermal drug delivery system based on self-adhesive Janus nanofibrous film with high breathability and monodirectional water-penetration.

    PubMed

    Shi, Yongli; Li, Yue; Wu, Jianming; Wang, Weiguo; Dong, Anjie; Zhang, Jianhua

    2014-01-01

    Transdermal drug delivery systems (TDDS) had achieved significant success in medical practice, but still suffered from adhesion failure and skin reaction due to the occlusive properties of hydrophobic pressure sensitive adhesives (PSAs). In order to solve these problems, a novel TDDS patch based on self-adhesive Janus nanofibrous film was prepared by a multilayered electrospinning. This multifunctional patch was a bilayer structure. The subjacent layer was a hydrophobic and adhesive fibrous layer electrospun from polyacrylate PSA (HPSA), and the upper backing layer was a hydrophilic cross-linked poly (vinyl alcohol) (c-PVA) nanofibrous film. The structures of the HPSA/c-PVA composite fibrous films were characterized and their application properties, including adherence performance, water vapor permeability, water-penetration, release characteristics, and skin irritation were evaluated. The results indicated that the HPSA/c-PVA composite fibrous films could provide suitable adhesive properties for TDDS application, excellent capacity for drug loading and release, aesthetical appearance and high safety for use on the skin. Especially, due to the nanofibrous network structures and the hydrophobic-hydrophilic wettability gradient from hydrophobic HPSA layer to the hydrophilic c-PVA layer, the Janus films possessed high breathability and monodirectional water-penetration. Water could penetrate from the hydrophobic to the hydrophilic side, but could not permeate through in the opposite direction. This may provide a feasible solution to the problems caused by the water, sweat, or wound exudate on the skin, when the hydrophobic PSAs were used as matrix for TDDS and wound dressing patches.

  13. Surface Partitioning and Stability of Mixed Films of Fluorinated Alcohols and Acids at the Air- Water Interface

    NASA Astrophysics Data System (ADS)

    Rontu, N. A.; Vaida, V.

    2007-05-01

    The production of fluorinated compounds over the past 50 years has had numerous industrial applications. For example, perfluorinated carboxylic acids are used in the synthesis of polymers and fire retardants, perfluoroalkyl sulfonates act as surface protectors, and fluorotelomer alcohols are incorporated into products such as paints, coatings, polymers, and adhesives. Fluorotelomer alcohols (FTOHs) are linear polyfluorinated alcohols with the formula CF3(CF2)nCH2CH2OH (n=1,3,5,...). They have been suggested as possible precursors for perfluorinated carboxylic acids and detected in the troposphere over several North American sites. Perfluorocarboxylic acids have even been detected in the arctic food chain, human blood, tissues of animals and environmental waters. We report the surface activity of fluorotelomer alcohols and perfluorinated carboxylic acids at the air-water interface by using a Langmuir trough. Isotherms of the pure compounds along with mixed films with other organic carboxylic acids were collected. The main objective of these experiments was to understand their heterogeneous chemistry by characterizing the pure and mixed films, which serves as a representative model for organic films on atmospheric surfaces such as those found on oceans and aqueous aerosols. Film properties and behavior, notably stabilization, evaporation from the subphase, and miscibility in the single-component mixtures as well as in the mixed films will be discussed. An important consequence of FTOHs and perfluorocarboxylic acids being found to partition to the air-water interface is the possibility of their transport and widespread distribution and deposition using atmospheric aerosols.

  14. Enhancement of Singlet-Triplet Energy Transfer Between Dyes in a Polymer Film by Surface Plasmons of Gold Nanoparticles

    NASA Astrophysics Data System (ADS)

    Tsibul'nikova, A. V.; Bryukhanov, V. V.; Slezhkin, V. A.

    2015-04-01

    The effect of the plasmon energy generated in Ag citrate hydrosol and ablated Au nanoparticles on the singlettriplet electron energy transfer between rhodamine 6G (R6G) and acriflavine (ACF) molecules incorporated into polyvinyl alcohol (PVA) films is studied. The increased efficiency of non-radiative energy transfer in the presence of Au nanoparticles and the increased lifetime of excited states of molecules are established.

  15. Impact of electron-beam irradiation on free-volume related microstructural properties of PVA:NaBr polymer composites

    NASA Astrophysics Data System (ADS)

    Ismayil; Vasachar, Ravindrachary; Bhajantri, Rajashekhar F.; Dhola, Praveena S.; Sanjeev, Ganesh

    2015-01-01

    Sodium Bromide doped Poly(vinyl alcohol) (PVA:NaBr, 80:20) polymer composite films were prepared using a solution casting method. These films were subjected to 8 MeV electron beam radiation at a dose of up to 300 kGy in air at room temperature. The free volume related microstructural and electrical properties of these irradiated films were studied using various characterization methods, such as positron annihilation lifetime spectroscopy (PALS) and AC & DC conductivity measurement techniques. The variations in the positron lifetime data indicate that the free-volume related properties of the doped polymer are affected by irradiation. From the results, it is found that at lower doses, a cross-linking network provides hopping sites for Na+ ions, and at higher doses, the chain-scission process facilitates ionic transport through segmental motion. Thus, the free volume around the polymer chain leads to mobility of the ions as well as the polymer segments and hence contributes to the enhancement of conductivity.

  16. Relative humidity sensing using dye-doped polymer thin-films on metal substrates

    NASA Astrophysics Data System (ADS)

    Kumari, Madhuri; Ding, Boyang; Blaikie, Richard

    2015-12-01

    We demonstrate humidity sensors based on optical resonances sustained in sub-wavelength thick dye-doped polymer coatings on reflecting surfaces. As a result of coupling between dye molecular absorption and Fabry-Perot resonances in the air-coating-surface cavity, the absorption spectra of such thin-film structures show a strong resonant peak under certain illumination conditions. These resonances are sensitive to the structural and material properties of the thin-film, metal underlayer and ambient conditions and hence can be used for gas and vapor sensing applications. Specifically, we present our proof of principle experimental results for humidity sensing using a thin-film structure comprising Rhodamine6G-doped polyvinyl alcohol (PVA) films on silver substrates. Depending on the PVA film thickness, dye-concertation and angle of incidence, the resonant absorption peak can undergo either red-shift or blue-shift as RH level increases in the range 20% to 60%. Also, the absorption magnitude at certain wavelengths near to resonance show almost linear reduction which can be used as the sensing signal. Our simulation studies show a very good agreement with the experimental data. The spectral and temporal sensitivity of this thin-film structure is attributed to the changes in the thickness of the PVA layer which swells by absorbing water molecules

  17. Electrooptic Kerr effect of porphyrin H-aggregates in polymer films: Polymer specific spectral blue shift

    NASA Astrophysics Data System (ADS)

    Suzuki, Masaya; Nakata, Kazuaki; Kuroda, Reiko; Kobayashi, Takayoshi; Tokunaga, Eiji

    2016-05-01

    J- and H-aggregates of porphyrin molecules (TPPS4) in spin-coated polymer films have been studied by electroabsorption and circular dichroism (CD) spectroscopy. A spectral blue shift of the H-band due to the electrooptic Kerr effect was observed for the first time. This occurs only for a polyvinylpyrrolidone (PVP) film, with negligibly small spectral shift observed in polyvinyl alcohol (PVA), polyvinyl sulfate (PVS), and polyacrylic acid (PAA) films, in contrast to the red shift of the J-band which is commonly observed for any host polymers. Accordingly, the CD activity in both of J- and H-bands is more enhanced in PVP films than in PVA films. The mechanism of the blue and red shifts of the respective H- and J-bands is discussed by invoking a helical structure in micro-aggregates, which is compatible with the CD spectra, based on the molecular rearrangement model. It is proved that blue- and red-shifts occur evenly to cancel each other in the H-band if a simple helical structure is assumed, in good agreement with no spectral shifts in the H-band in PVA, PVS, and PAA films.

  18. Interface porcelain tile/PVA modified mortar: a novel nanostructure approach.

    PubMed

    Mansur, Alexandra Ancelmo Piscitelli; Mansur, Herman Sander

    2009-02-01

    In ceramic tile systems, the overall result of adherence between porcelain tiles and polymer modified mortars could be explained based on the nano-order structure that is developed at the interface. Based on pull-off tests, Scanning Electron Microscopy images, and Small Angle X-ray Scattering experiments a nanostructured approach for interface tile/PVA modified mortar was built. The increase of adhesion between tile and mortar due to poly(vinyl alcohol), PVA, addition can be explained by the formation of a hybrid ceramic-polymer-ceramic interface by hydrogen bonds between PVA hydroxyl groups and silanol from tile surface and water from nanostructured C-S-H gel interlayer.

  19. Crystal growth of ZnO bulk by CVT method using PVA

    NASA Astrophysics Data System (ADS)

    Udono, H.; Sumi, Y.; Yamada, S.; Kikuma, I.

    2008-04-01

    Seeded crystal growth of Zinc oxide (ZnO) by the closed ampoule chemical vapor transport (CVT) is carried out using polyvinyl alcohol (PVA) as a transport agent. Under the conditions of TS=1100 °C, Δ T=10 K and the amount of PVA=0.13-0.91 mg/cm 3, single-crystalline ZnO was grown continuously on the ZnO seed-crystal, of which the surface was (0 0 0 1) Zn-face. The grown crystals had well-marked growth facets belonged to {1 0 1¯0} and {1 0 1¯ 1} faces. The color of the crystals was changed from pale yellow to dark orange-red depending on the amount of PVA. Typical electron density and the Hall mobility of the crystals were 1×10 17 cm -3 and 2×10 2 cm 2/V s at 300 K, respectively.

  20. Analysis of Crystallization on Polymeric Thin Films Deposited on Silicon Dioxide

    NASA Astrophysics Data System (ADS)

    Cummings, Ethan

    2013-03-01

    Polyvinyl Alcohol (PVA) is a synthetic polymer containing carbon chains with hydroxide groups bonded to every other carbon. Poly (propylmethacrylisobutyl POSS co-methylmethacrylate) (POSS-MA) is a co-polymer that contains polyhedral oligomeric silsesquioxane (POSS) cages co-polymerized to a poly methyl methacrylate (PMMA) backbone. PVA is dissolved into water at various concentrations and coated onto a silica wafer using spin casting. Then, various concentrations of 30-40 wt% POSS-MA are dissolved in chloroform and deposited onto the same sample. After spin casting, these samples are analyzed using AFM and ellipsometry. Typical samples of POSS-MA and PVA/POSS-MA thin films exhibit varying rates of micro-phase separation in the form of dendritic structures. Once seperation is completed, the pixel areas of the dendrite structures are measured using IDL. These varying area determinations are normalized, and then fit to an Avrami plot by graphing ln(-ln(1-f)) vs. ln(time), where ``f'' is normalized area, and the time is the time after deposition. On the graphs, the slope is the dimensionality of the growth constant, and the y-intercept is the natural log of the rate constant (ln(k)). Samples also undergo ellipsometry to determine the thickness of the SiO2/PVA/POSS-MA thin films. Additional experiments include a process that etches away the PVA thin film layer in water, leaving the POSS-MA thin film layer on the surface of the water. The thin film is then lifted onto a TEM grid to be analyzed using TEM.

  1. Sensitivity and Response of Polyvinyl Alcohol/Tin Oxide Nanocomposite Multilayer Thin Film Sensors.

    PubMed

    Sriram, G; Dhineshbabu, N R; Nithyavathy, N; Saminathan, K; Kaler, K V I S; Rajendran, V

    2016-01-01

    Nanocrystalline Tin Oxide (SnO₂) is Non-Stoichiometric in Nature with Functional Properties Suitable for gas sensing. In this study, SnO₂nanoparticles were prepared by the sol-gel technique, which were then characterised using X-ray diffraction. The nanoparticles showed tetragonal structure with an average crystallite size of 18 nm. The stretching and vibration modes of SnO₂were confirmed using Fourier transform infrared spectroscopy. The size of SnO₂ nanoparticles was determined using particle size analyser, which was found be 60 ± 10 nm on average. The surface morphology of the nanoparticles was investigated using scanning electron microscope, which showed irregular-sized agglomerated SnO₂nanostructures. In addition, primary particle size was evaluated using high-resolution transmission electron microscopy, which was found to be 50 nm on average. The polyvinyl alcohol/SnO₂ composite thin film was prepared on a glass substrate using spin-coating method. The values of band gap energy and electrical conductance of 13-layer thin film were found to be 2.96 eV and 0.0505 mho, respectively. Sulfur dioxide (SO₂) was suitably tailored to verify the sensor response over a concentration range of 10-70 ppm at room temperature. The performance, response, and recovery time of sensors were increased by increasing the layers of the thin film. PMID:27398561

  2. Formation of linear polyenes in poly(vinyl alcohol) films catalyzed by phosphotungstic acid, aluminum chloride, and hydrochloric acid

    NASA Astrophysics Data System (ADS)

    Tretinnikov, O. N.; Sushko, N. I.; Malyi, A. B.

    2016-07-01

    Formation of linear polyenes-(CH=CH)n-via acid-catalyzed thermal dehydration of polyvinyl alcohol in 9- to 40-µm-thick films of this polymer containing hydrochloric acid, aluminum chloride, and phosphotungstic acid as dehydration catalysts was studied by electronic absorption spectroscopy. The concentration of long-chain ( n ≥ 8) polyenes in films containing phosphotungstic acid is found to monotonically increase with the duration of thermal treatment of films, although the kinetics of this process is independent of film thickness. In films containing hydrochloric acid and aluminum chloride, the formation rate of polyenes with n ≥ 8 rapidly drops as film thickness decreases and the annealing time increases. As a result, at a film thickness of less than 10-12 µm, long-chain polyenes are not formed at all in these films no matter how long thermal duration is. The reason for this behavior is that hydrochloric acid catalyzing polymer dehydration in these films evaporates from the films during thermal treatment, the evaporation rate inversely depending on film thickness.

  3. The Effects of plasticizers and palmitic acid toward the properties of the carrageenan Film

    NASA Astrophysics Data System (ADS)

    Heru Wibowo, Atmanto; Listiyawati, Oktaviana; Purnawan, Candra

    2016-02-01

    Varied plasticizers and palmitic acid additive have been added in the carrageenan film. The film was made by mixing of the carrageenan and plasticizers (glycerol, polyethylene glycol, polyvinyl alcohol) with composition of 92:3, 90:6, 87:9, 84:12, 81:15(%w/w) and in the presence of palmitic acid as additive with 1%, 2%, 3%, 4%, 5% of total weight. Casting method was used for the film molding and drying at 60oC with the oven for 12 hours. To investigate the effects of plasticizers and additive, some mechanical tests on film were performed. The test result concludes that plasticizers in the film decreased the tensile strength and increased the elongation break of the carrageenan film. The additive of palmitic acid decreased the tensile strength of the carrageenan film and also decreased the-the water absorbance of the film. The highest tensile strength of films made was with the formulation of carrageenan: PEG with composition of 92:3 (% w/w). The highest elongation break of the film was for carrageenan:PVA with the composition of 81: 15 (%w/w) and carrageenan:palmitic acid:PEG with the composition of 92: 3: 1 (%w/w). The lowest water absorption of the film was achieved for carrageenan:PVA:palmitic acid with the composition of 87: 3: 5 (%w/w).

  4. Natural polysaccharides promote chondrocyte adhesion and proliferation on magnetic nanoparticle/PVA composite hydrogels.

    PubMed

    Hou, Ruixia; Nie, Lei; Du, Gaolai; Xiong, Xiaopeng; Fu, Jun

    2015-08-01

    This paper aims to investigate the synergistic effects of natural polysaccharides and inorganic nanoparticles on cell adhesion and growth on intrinsically cell non-adhesive polyvinyl alcohol (PVA) hydrogels. Previously, we have demonstrated that Fe2O3 and hydroxyapatite (nHAP) nanoparticles are effective in increasing osteoblast growth on PVA hydrogels. Herein, we blended hyaluronic acid (HA) and chondroitin sulfate (CS), two important components of cartilage extracellular matrix (ECM), with Fe2O3/nHAP/PVA hydrogels. The presence of these natural polyelectrolytes dramatically increased the pore size and the equilibrium swelling ratio (ESR) while maintaining excellent compressive strength of hydrogels. Chondrocytes were seeded and cultured on composite PVA hydrogels containing Fe2O3, nHAP and Fe2O3/nHAP hybrids and Fe2O3/nHAP with HA or CS. Confocal laser scanning microscopy (CLSM) and cell counting kit-8 (CCK-8) assay consistently confirmed that the addition of HA or CS promotes chondrocyte adhesion and growth on PVA and composite hydrogels. Particularly, the combination of HA and CS exhibited further promotion to cell adhesion and proliferation compared with any single polysaccharide. The results demonstrated that the magnetic composite nanoparticles and polysaccharides provided synergistic promotion to cell adhesion and growth. Such polysaccharide-augmented composite hydrogels may have potentials in biomedical applications.

  5. Natural polysaccharides promote chondrocyte adhesion and proliferation on magnetic nanoparticle/PVA composite hydrogels.

    PubMed

    Hou, Ruixia; Nie, Lei; Du, Gaolai; Xiong, Xiaopeng; Fu, Jun

    2015-08-01

    This paper aims to investigate the synergistic effects of natural polysaccharides and inorganic nanoparticles on cell adhesion and growth on intrinsically cell non-adhesive polyvinyl alcohol (PVA) hydrogels. Previously, we have demonstrated that Fe2O3 and hydroxyapatite (nHAP) nanoparticles are effective in increasing osteoblast growth on PVA hydrogels. Herein, we blended hyaluronic acid (HA) and chondroitin sulfate (CS), two important components of cartilage extracellular matrix (ECM), with Fe2O3/nHAP/PVA hydrogels. The presence of these natural polyelectrolytes dramatically increased the pore size and the equilibrium swelling ratio (ESR) while maintaining excellent compressive strength of hydrogels. Chondrocytes were seeded and cultured on composite PVA hydrogels containing Fe2O3, nHAP and Fe2O3/nHAP hybrids and Fe2O3/nHAP with HA or CS. Confocal laser scanning microscopy (CLSM) and cell counting kit-8 (CCK-8) assay consistently confirmed that the addition of HA or CS promotes chondrocyte adhesion and growth on PVA and composite hydrogels. Particularly, the combination of HA and CS exhibited further promotion to cell adhesion and proliferation compared with any single polysaccharide. The results demonstrated that the magnetic composite nanoparticles and polysaccharides provided synergistic promotion to cell adhesion and growth. Such polysaccharide-augmented composite hydrogels may have potentials in biomedical applications. PMID:26037704

  6. Non-woven PGA/PVA fibrous mesh as an appropriate scaffold for chondrocyte proliferation.

    PubMed

    Rampichová, M; Koštáková, E; Filová, E; Prosecká, E; Plencner, M; Ocheretná, L; Lytvynets, A; Lukáš, D; Amler, E

    2010-01-01

    Non-woven textile mesh from polyglycolic acid (PGA) was found as a proper material for chondrocyte adhesion but worse for their proliferation. Neither hyaluronic acid nor chitosan nor polyvinyl alcohol (PVA) increased chondrocyte adhesion. However, chondrocyte proliferation suffered from acidic byproducts of PGA degradation. However, the addition of PVA and/or chitosan into a wet-laid non-woven textile mesh from PGA improved chondrocyte proliferation seeded in vitro on the PGA-based composite scaffold namely due to a diminished acidification of their microenvironment. This PVA/PGA composite mesh used in combination with a proper hydrogel minimized the negative effect of PGA degradation without dropping positive parameters of the PGA wet-laid non-woven textile mesh. In fact, presence of PVA and/or chitosan in the PGA-based wet-laid non-woven textile mesh even advanced the PGA-based wet-laid non-woven textile mesh for chondrocyte seeding and artificial cartilage production due to a positive effect of PVA in such a scaffold on chondrocyte proliferation.

  7. Is there an association between seeing incidents of alcohol or drug use in films and young Scottish adults' own alcohol or drug use? A cross sectional study

    PubMed Central

    2011-01-01

    Background As the promotion of alcohol and tobacco to young people through direct advertising has become increasingly restricted, there has been greater interest in whether images of certain behaviours in films are associated with uptake of those behaviours in young people. Associations have been reported between exposure to smoking images in films and smoking initiation, and between exposure to film alcohol images and initiation of alcohol consumption, in younger adolescents in the USA and Germany. To date no studies have reported on film images of recreational drug use and young people's own drug use. Methods Cross sectional multivariable logistic regression analysis of data collected at age 19 (2002-4) from a cohort of young people (502 boys, 500 girls) previously surveyed at ages 11 (in 1994-5), 13 and 15 in schools in the West of Scotland. Outcome measures at age 19 were: exceeding the 'sensible drinking' guidelines ('heavy drinkers') and binge drinking (based on alcohol consumption reported in last week), and ever use of cannabis and of 'hard' drugs. The principle predictor variables were an estimate of exposure to images of alcohol, and of drug use, in films, controlling for factors related to the uptake of substance use in young people. Results A third of these young adults (33%) were classed as 'heavy drinkers' and half (47%) as 'binge drinkers' on the basis of their previous week's consumption. Over half (56%) reported ever use of cannabis and 13% ever use of one or more of the 'hard' drugs listed. There were linear trends in the percentage of heavy drinkers (p = .018) and binge drinkers (p = 0.012) by film alcohol exposure quartiles, and for ever use of cannabis by film drug exposure (p = .000), and for ever use of 'hard' drugs (p = .033). The odds ratios for heavy drinking (1.56, 95% CI 1.06-2.29 comparing highest with lowest quartile of film alcohol exposure) and binge drinking (1.59, 95% CI 1.10-2.30) were attenuated by adjustment for gender, social

  8. Free-standing crystalline CaCO3 films composed of three-dimensional microstructures with different morphologies

    NASA Astrophysics Data System (ADS)

    Dong, Lihong; Yang, Lijuan; Wang, Yanping; Han, Mingjuan

    2012-03-01

    Crystalline vaterite CaCO3 self-standing films composed of three-dimensional microstructures were synthesized by a simple gas diffuse method with the assistance of poly(vinyl alcohol) (PVA). The microstructures with different morphology (sphere-like, rose-like, and pumpkin-like) were self-assembled by three-dimensional oriented attachment of faceted micro-platelets, and the films were all stable in air for more than one year. The concentrations of Ca2+ ions and PVA all played important roles in the formation of vaterite crystal phase. In addition, the introduction of salt (NaCl, NaNO3) would reduce the size of the micro-platelets significantly. A possible mechanism for the formation of the self-standing films is put forward.

  9. Effect of hydroxypropyl-β-cyclodextrin and coadjuvants on the sorption capacity of hydrophilic polymer films for monoterpene alcohols.

    PubMed

    Higueras, Laura; López-Carballo, Gracia; Gavara, Rafael; Hernández-Muñoz, Pilar

    2016-10-20

    Chitosan films filled with hydroxypropyl-β-cyclodextrin at a 1:1 weight ratio and plasticized with 35 or 50% glycerol or 35% propylene glycol were prepared by casting and conditioned at different relative humidities to achieve a similar water content. Sorption properties of the films for various monoterpene compounds with phenolic, or with linear or cyclohexyl alcohol structures were studied after their immersion in the volatile liquids. In general, the films presented a considerable capacity to retain monophenolic compounds, with sorption values ranging from 455% for meta-cumenol to 193% for guaiacol, for chitosan films with the same formulation. These values were two orders of magnitude higher than those of compounds without the phenol group. The affinity for monophenolic compounds decreased in films plasticized with hydrophilic propylene glycol, whereas no changes were observed in the retention of non-phenolic monoterpenes. Replacement of chitosan with polyvinyl alcohol polymer considerably decreased the retention of monophenolic compounds, with the exception of isoeugenol. Finally, the antimicrobial activity of monoterpenes and films loaded with them was evaluated in vitro by the microatmosphere test against Escherichia coli and Staphylococcus aureus. The present study shows that hydroxypropyl-β-cyclodextrin and the plasticization level achieved by hydrophilic films can be used to regulate loading capacity and sorption selectivity of naturally occurring antimicrobial compounds. PMID:27474670

  10. Direct growth of nanocrystalline graphitic carbon films on BaF2 by alcohol CVD

    NASA Astrophysics Data System (ADS)

    Tan, Yan; Nakamura, Atsushi; Kubono, Atsushi

    2016-03-01

    Multilayered nanocrystalline graphitic carbon films were directly formed on BaF2 substrates by the alcohol chemical vapor deposition method using ethanol. Domain size was typically 46 nm as estimated from the peak intensity ratios of G- and D-band of the Raman spectra, which were higher than currently reported values for various dielectric substrates. Sheet resistance measured by the four-probe method was 900 Ω/sq. A possible formation mechanism of the graphitic carbon layer was discussed referring to the results of X-ray photoelectron spectroscopy (XPS) and energy dispersive X-ray spectroscopy (EDX) for a composition analysis. It was found that the graphitic carbon layers were formed on the BaO surface, which was produced by the oxidization of the BaF2 substrate by the ethanol source.

  11. Some Physical Properties of Pure and Doped Polyvinyl Alcohol under Applied Stress

    NASA Astrophysics Data System (ADS)

    Hemeda, O. M.; Hemeda, D. M.; Said, M. Z.

    Thick films of polyvinyl alcohol (PVA) containing very fine metallic powder, copper (Cu), iron (Fe) and aluminum (Al) 2.5% by weight, were prepared by the casting method. The temperature dependence of Young's modulus at constant stress, the stress dependence of Young's modulus (Y), the stress dependence of dielectric constant (ɛ) and stress dependence of phonon velocity, were studied. It was found that Young's modulus (Y) of the pure sample has the lowest value and that of PVA + Al has the highest value. This can be explained on the basis that Y depends on the ratio between the energy of molecular interactions and the energy of thermal motion of the sample units. We also found that the dielectric constant increases with the addition of metallic powder, and with an increasing applied stress. The phonon velocity increased with increasing stress. The increase of stress decreases imperfections leading to the increased phonon velocity. The electronic absorption spectra of PVA is not affected by doping Al and Fe, whereas the PVA doped with Cu shows a shift of the absorption maxima toward a longer wavelength. The instantaneous elastic behavior may be observed only at low temperatures and very short creep times.

  12. Synthesis, characterization, optical and antimicrobial studies of polyvinyl alcohol-silver nanocomposites

    NASA Astrophysics Data System (ADS)

    Mahmoud, K. H.

    2015-03-01

    Silver nanoparticles (Ag NPs) were synthesized by chemical reduction of silver salt (AgNO3) through sodium borohydride. The characteristic surface plasmon resonance band located at around 400 nm in the UV-Visible absorption spectrum confirmed the formation of Ag nanoparticles. Polyvinyl alcohol-silver (PVA-Ag) nanocomposite films were prepared by the casting technique. The morphology and interaction of PVA with Ag NPs were examined by transmission electron microscopy and FTIR spectroscopy. Optical studies show that PVA exhibited indirect allowed optical transition with optical energy gap of 4.8 eV, which reduced to 4.45 eV under addition of Ag NPs. Optical parameters such as refractive index, complex dielectric constant and their dispersions have been analyzed using Wemple and DiDomenco model. Color properties of the nanocomposites are discussed in the framework of CIE L∗u∗v∗ color space. The antimicrobial activity of the nanocomposite samples was tested against Gram positive bacteria (Staphylococcus aureus NCTC 7447 &Bacillus subtillis NCIB 3610), Gram negative bacteria (Escherichia coli, NTC10416 &Pseudomonas aeruginosa NCIB 9016) and fungi (Aspergillus niger Ferm - BAM C-21) using the agar diffusion technique. The antimicrobial study showed that PVA has moderate antibacterial activity against B. subtillis and the 0.04 wt% Ag NPs composite sample effect was strong against S. aureus.

  13. The structure and phase diagram of Langmuir films of alcohols on mercury.

    PubMed

    Kraack, H; Ocko, B M; Pershan, P S; Sloutskin, E; Tamam, L; Deutsch, M

    2004-06-22

    The coverage-dependent phase behavior of molecular films of alcohols (CH3(CH2)n-2CH2OH, denoted as CnOH) on mercury was studied for chain lengths 8 < or = n < or = 28, using surface tensiometry and surface specific X-ray methods. Phases with surface-normal-oriented molecules are found at high coverage, showing the CS, S, and LS phases found also on water. Phases comprising surface parallel molecules, which do not exist on water, are found here at low coverage. For the lowest coverage a two-dimensional gas phase is found, followed, upon increasing the coverage, by an n-dependent sequence of condensed phases of up to four layers of surface-parallel molecules before converting to the surface-normal phases. In contrast with the surface-normal phases, all of the surface-parallel phases are found to lack long-range order in the surface-parallel direction. Adsorption energies are derived from the phase diagram for the alkyl chain and the alcohol headgroup.

  14. Multiwall carbon nanotube polyvinyl alcohol-based saturable absorber in passively Q-switched fiber laser.

    PubMed

    Ahmad, H; Ismail, M F; Hassan, S N M; Ahmad, F; Zulkifli, M Z; Harun, S W

    2014-10-20

    In this work, we demonstrated a compact Q-switched erbium-doped fiber laser capable of generating high-energy pulses using a newly developed multiwall carbon nanotube (CNT) polyvinyl alcohol (PVA) thin film based saturable absorber. Q-switched pulse operation is obtained by sandwiching the thin film between two fiber ferrules forming a saturable absorber. A saturable absorber with 1.25 wt. % of PVA concentration shows a consistency in generating pulsed laser with a good range of tunable repetition rate, shortest pulse width, and produces a high pulse energy and peak power. The pulse train generated has a maximum repetition rate of 29.9 kHz with a corresponding pulse width of 3.49 μs as a function of maximum pump power of 32.15 mW. The maximum average output power of the Q-switched fiber laser system is 1.49 mW, which translates to a pulse energy of 49.8 nJ. The proposed method of multiwall CNT/PVA thin film fabrication is low in cost and involves uncomplicated processes. PMID:25402790

  15. Functional data analysis of experimental parameters obtained in PVA doped CdCl2 polymer composites

    NASA Astrophysics Data System (ADS)

    Prakash, M. B. Nanda; Urs, Gopal Krishne; Somashekar, R.

    2016-05-01

    Using solution casting method, PVA based polymer composites films with various concentrations of CdCl2 were prepared. Prepared polymer composites films were investigated using XRD. Crystallite size for different concentrations of CdCl2 are computed here using Williamson and Hall plot (WH plot), an in-house program developed by us. To correlate between two independent physical parameters size and conductivity, we have chosen functional data analysis to estimate the maxima and minima in these polymer composites systems.

  16. Spectral-Polarization Properties and Light Resistance of Polyvinyl-Alcohol Films Colored With Disazo Dyes

    NASA Astrophysics Data System (ADS)

    Fillipovich, L. N.; Ariko, N. G.; Agabekov, V. E.; Malashko, P. M.

    2005-09-01

    Polarizers containing disazo dyes from the group of azobenzene-azonaphthalene have been developed. It has been established that their polarizing ability is determined by the mutual disposition of the azo group and electron-donor substituents in the naphthalene ring. On diazo coupling of γ acid into the α position relative to the oxy group, the M1 and M3 dyes are formed, the polarizing ability of which in uniaxially oriented polyvinyl-alcohol films is higher than in the M2 dye produced as a result of diazo coupling into the α position relative to the amino group. On irradiation by UV light, the dyes are subjected to photodestruction, which, in the case of M2, proceeds through trans-cis-isomerization. The rate of photodestruction depends on the aggregation of the dye molecules, and it increases in the presence of a free-radical initiator. The UV absorber (substituted benzotriazole) and the uniaxial orientation of the film retard this process.

  17. Engineering a Highly Hydrophilic PVDF Membrane via Binding TiO₂Nanoparticles and a PVA Layer onto a Membrane Surface.

    PubMed

    Qin, Aiwen; Li, Xiang; Zhao, Xinzhen; Liu, Dapeng; He, Chunju

    2015-04-29

    A highly hydrophilic PVDF membrane was fabricated through chemically binding TiO2 nanoparticles and a poly(vinyl alcohol) (PVA) layer onto a membrane surface simultaneously. The chemical composition of the modified membrane surface was determined by X-ray photoelectron spectroscopy, and the binding performance of TiO2 nanoparticles and the PVA layer was investigated by a rinsing test. The results indicated that the TiO2 nanoparticles were uniformly and strongly tailored onto the membrane surface, while the PVA layer was firmly attached onto the surface of TiO2 nanoparticles and the membrane by adsorption-cross-linking. The possible mechanisms during the modification process and filtration performance, i.e., water permeability and bovine serum albumin (BSA) rejection, were investigated as well. Furthermore, antifouling property was discussed through multicycles of BSA solution filtration tests, where the flux recovery ratio was significantly increased from 20.0% for pristine PVDF membrane to 80.5% for PVDF/TiO2/PVA-modified membrane. This remarkable promotion is mainly ascribed to the improvement of surface hydrophilicity, where the water contact angle of the membrane surface was decreased from 84° for pristine membrane to 24° for PVDF/TiO2/PVA membrane. This study presents a novel and varied strategy for immobilization of nanoparticles and PVA layer on substrate surface, which could be easily adapted for a variety of materials for surface modification. PMID:25806418

  18. Engineering a Highly Hydrophilic PVDF Membrane via Binding TiO₂Nanoparticles and a PVA Layer onto a Membrane Surface.

    PubMed

    Qin, Aiwen; Li, Xiang; Zhao, Xinzhen; Liu, Dapeng; He, Chunju

    2015-04-29

    A highly hydrophilic PVDF membrane was fabricated through chemically binding TiO2 nanoparticles and a poly(vinyl alcohol) (PVA) layer onto a membrane surface simultaneously. The chemical composition of the modified membrane surface was determined by X-ray photoelectron spectroscopy, and the binding performance of TiO2 nanoparticles and the PVA layer was investigated by a rinsing test. The results indicated that the TiO2 nanoparticles were uniformly and strongly tailored onto the membrane surface, while the PVA layer was firmly attached onto the surface of TiO2 nanoparticles and the membrane by adsorption-cross-linking. The possible mechanisms during the modification process and filtration performance, i.e., water permeability and bovine serum albumin (BSA) rejection, were investigated as well. Furthermore, antifouling property was discussed through multicycles of BSA solution filtration tests, where the flux recovery ratio was significantly increased from 20.0% for pristine PVDF membrane to 80.5% for PVDF/TiO2/PVA-modified membrane. This remarkable promotion is mainly ascribed to the improvement of surface hydrophilicity, where the water contact angle of the membrane surface was decreased from 84° for pristine membrane to 24° for PVDF/TiO2/PVA membrane. This study presents a novel and varied strategy for immobilization of nanoparticles and PVA layer on substrate surface, which could be easily adapted for a variety of materials for surface modification.

  19. Novel Starch-PVA Polymer for Microparticle Preparation and Optimization Using Factorial Design Study

    PubMed Central

    Chattopadhyay, Helen; De, Amit Kumar; Datta, Sriparna

    2015-01-01

    The aim of our present work was to optimize the ratio of a very novel polymer, starch-polyvinyl alcohol (PVA), for controlled delivery of Ornidazole. Polymer-coated drug microparticles were prepared by emulsion method. Microscopic study, scanning electron microscopic study, and atomic force microscopic study revealed that the microparticles were within 10 micrometers of size with smooth spherical shape. The Fourier transform infrared spectroscopy showed absence of drug polymer interaction. A statistical 32 full factorial design was used to study the effect of different concentration of starch and PVA on the drug release profile. The three-dimensional plots gave us an idea about the contribution of each factor on the release kinetics. Hence this novel polymer of starch and polyvinyl alcohol can be utilized for control release of the drug from a targeted delivery device. PMID:27347511

  20. Tuning the stability of CaCO3 crystals with magnesium ions for the formation of aragonite thin films on organic polymer templates.

    PubMed

    Zhu, Fangjie; Nishimura, Tatsuya; Sakamoto, Takeshi; Tomono, Hidekazu; Nada, Hiroki; Okumura, Yasushi; Kikuchi, Hirotsugu; Kato, Takashi

    2013-12-01

    Thin-film growth of aragonite CaCO3 on annealed poly(vinyl alcohol) (PVA) matrices is induced by adding Mg(2+) into a supersaturated solution of CaCO3. Both the growth rate and surface morphology of the aragonite thin films depend upon the concentration of Mg(2+) in the mineralization solution. In the absence of PVA matrices, no thin films are formed, despite the presence of Mg(2+). Molecular dynamics simulation of the CaCO3 precursor suggests that the transition of amorphous calcium carbonate to crystals is suppressed in the presence of Mg(2+). The role for ionic additives in the crystallization of CaCO3 on organic templates obtained in this study may provide useful information for the development of functional hybrid materials.

  1. Adsorption and Reaction of C(1)-C(3) Alcohols over CeO(x)(111) Thin Films

    SciTech Connect

    Mullins, David R; Senanayake, Sanjaya D; Chen, Tsung-Liang

    2010-01-01

    This study reports the interaction of methanol, ethanol, 1-propanol, and 2-propanol with well-ordered CeO{sub 2}(111) thin film surfaces. All of the alcohols adsorb at low temperature by forming alkoxy and hydroxyl species on the surface. On fully oxidized CeO{sub 2}(111), recombination occurs between some of the alkoxys and hydroxyls, resulting in alcohol desorption near 220 K. At the same temperature, some of the surface hydroxyls disproportionate to produce water and the loss of lattice O. The remaining alkoxys react above 550 K. The primary alcohols favor dehydrogenation products (aldehydes). There is a net loss of O from the system, resulting in a reduction of the ceria. The secondary alcohol, 2-propanol, undergoes primarily dehydration, producing propene with no net change in the cerium oxidation state. Reduced CeO{sub X}(111) competes with the gaseous products for available O. Little or no water is produced. The reaction selectivity for the C{sub 2} and C{sub 3} alcohols shifts toward favoring dehydration products. The loss of O from the alcohols leads to oxidation of the reduced ceria. Compared with the oxidized surface, the alkene desorption shifts to lower temperature, whereas the aldehyde desorption shifts to higher temperature. This indicates that, on the reduced surface, it is easier to break the C-O bond but more difficult to break the O-substrate bond.

  2. Graphite Thin Films Consisting of Nanograins of Multilayer Graphene on Sapphire Substrates Directly Grown by Alcohol Chemical Vapor Deposition

    NASA Astrophysics Data System (ADS)

    Miyasaka, Yuta; Nakamura, Atsushi; Temmyo, Jiro

    2011-04-01

    Graphene has been attracting a strong interest as a transparent electrode as well as a THz nanoelectronic device owing to its unique properties. To date, large-area graphene growth has been realized by chemical vapor deposition (CVD) with a catalyst metal. To avoid the transfer of segregated graphene, we have examined directly graphite thin film growth on nonpolar a-sapphire substrates without any catalyst metal by alcohol CVD. Graphite thin films consisting of nanograins of multilayer graphene on a-sapphire substrates were verified by a combination of transmission electron spectroscopy (TEM), and Raman analyses, and optical transparent and sheet resistance measurements.

  3. ZnS/PVA nanocomposites for nonlinear optical applications

    NASA Astrophysics Data System (ADS)

    Ozga, K.; Michel, J.; Nechyporuk, B. D.; Ebothé, J.; Kityk, I. V.; Albassam, A. A.; El-Naggar, A. M.; Fedorchuk, A. O.

    2016-07-01

    We have found a correlation between ZnS nanocomposite nonlinear optical features and technological processing using electrolytic method. In the earlier researches this factor was neglected. However, it may open a new stage for operation by photovoltaic features of the well known semiconductors within a wide range of magnitudes. The titled nanostructured zinc sulfide (ZnS) was synthesized by electrolytic method. The obtained ZnS nano-crystallites possessed nano-particles sizes varying within 1.6 nm…1.8 nm. The titled samples were analyzed by XRD, HR-TEM, STEM, and nonlinear optical methods such as photo-induced two-photon absorption (TPA) and second harmonic generation (SHG). For this reason the nano-powders were embedded into the photopolymer poly(vinyl) alcohol (PVA) matrices. Role of aggregation in the mentioned properties is discussed. Possible origin of the such correlations are discussed.

  4. Gentamicin-loaded wound dressing with polyvinyl alcohol/dextran hydrogel: gel characterization and in vivo healing evaluation.

    PubMed

    Hwang, Ma-Ro; Kim, Jong Oh; Lee, Jeong Hoon; Kim, Yong Il; Kim, Jeong Hoon; Chang, Sun Woo; Jin, Sung Gju; Kim, Jung Ae; Lyoo, Won Seok; Han, Sung Soo; Ku, Sae Kwang; Yong, Chul Soon; Choi, Han-Gon

    2010-09-01

    To develop a gentamicin-loaded wound dressing, cross-linked hydrogel films were prepared with polyvinyl alcohol (PVA) and dextran using the freezing-thawing method. Their gel properties such as gel fraction, swelling, water vapor transmission test, morphology, tensile strength, and thermal property were investigated. In vitro protein adsorption test, in vivo wound healing test, and histopathology were performed. Dextran decreased the gel fraction, maximum strength, and thermal stability of hydrogels. However, it increased the swelling ability, water vapor transmission rate, elasticity, porosity, and protein adsorption. The drug gave a little positive effect on the gel properties of hydrogels. The gentamicin-loaded wound dressing composed of 2.5% PVA, 1.13% dextran, and 0.1% drug was more swellable, flexible, and elastic than that with only PVA because of its cross-linking interaction with PVA. In particular, it could provide an adequate level of moisture and build up the exudates on the wound area. From the in vivo wound healing and histological results, this gentamicin-loaded wound dressing enhanced the healing effect more compared to conventional product because of the potential healing effect of gentamicin. Thus, this gentamicin-loaded wound dressing would be used as a potential wound dressing with excellent forming and improved healing effect in wound care.

  5. Permeation Studies of Captopril Transdermal Films Through Human Cadaver Skin.

    PubMed

    Nair, Rajesh Sreedharan; Nair, Sujith

    2015-01-01

    Mortality rate due to heart diseases increases dramatically with age. Captopril is an angiotensin converting enzyme inhibitor (ACE) used effectively for the management of hypertension. Due to short elimination half-life of captopril the oral dose is very high. Captopril is prone to oxidation and it has been reported that the oxidation rate of captopril in skin tissues is considerably low when compared to intestinal tissues. All these factors make captopril an ideal drug candidate for transdermal delivery. In this research work an effort was made to formulate transdermal films of captopril by utilizing polyvinylpyrrolidone (PVP) and polyvinyl alcohol (PVA) as film formers and polyethylene glycol 400 (PEG400) as a plasticizer. Dimethyl sulfoxide (DMSO) and dimethylformamide (DMF) were used as permeation enhancers. Physicochemical parameters of the films such as appearance, thickness, weight variation and drug content were evaluated. The invitro permeation studies were carried out through excised human cadaver skin using Franz diffusion cells. The in-vitro permeation studies demonstrated that the film (P4) having the polymer ratio (PVP:PVA = 80:20) with DMSO (10%) resulted a promising drug release of 79.58% at 24 hours with a flux of 70.0 µg/cm(2)/hr. No signs of erythema or oedema were observed on the rabbit skin as a result of skin irritation study by Draize test. Based on the stability report it was confirmed that the films were physically and chemically stable, hence the prepared films are very well suited for transdermal application.

  6. Formulation optimization and characterization of transdermal film of simvastatin by response surface methodology.

    PubMed

    Parhi, Rabinarayan; Suresh, Padilam

    2016-01-01

    Matrix type of simvastatin transdermal film (SSTF) was developed with poly(vinyl alcohol) (PVA) and eudragit RL100 (EG) using response surface methodology (RSM) to investigate combined effect of the selected process variables like SS concentration, PVA:EG ratio and the dibutyl phthalate (DBT) concentration at different levels on dependent variables such as tensile strength and flux, with an aim to optimize a suitable combination of drug, polymer and plasticizer ratio. The study reveals that the effect of DBT concentration was highest on tensile strength, while SS concentration exhibited pronounced effect on SS flux through the abdominal skin of rat. According to Derringer's desirability prediction tool, the composition of optimized film was found to be 2% of SS, 2:1 ratio of PVA:EG and 40% of DBT. Under these conditions, the SSTF exhibited a predicted value of tensile strength and flux of 11.871 MPa and 43.569 μg/cm(2)/h, respectively. The in vivo hypolipidemic study conducted for 14 days in hyperlipidemia induced Sprague-Dawley rats reveals that the optimized SSTF exhibited significant lowering of blood lipid level. The absence of skin irritation indicates that the prepared film was safe and well tolerated as transdermal formulation. Thus, the film may serve as an alternative therapy to oral dosage form of SS. PMID:26478318

  7. Study of polyvinyl alcohol nanofibrous membrane by electrospinning as a magnetic nanoparticle delivery approach

    NASA Astrophysics Data System (ADS)

    Ger, Tzong-Rong; Huang, Hao-Ting; Huang, Chen-Yu; Hu, Keng-Shiang; Lai, Jun-Yang; Chen, Jiann-Yeu; Lai, Mei-Feng

    2014-05-01

    Electrospinning technique was used to fabricate polyvinyl alcohol (PVA)-based magnetic biodegradable nanofibers. PVA solution was mixed with ferrofluid or magnetic nanoparticles (MNPs) powder and formed two individual nanofibrous membranes (PVA/ferrofluid and PVA/MNPs powder) by electrospinning. The surface morphology of the nanofibrous membrane was characterized by scanning electron microscopy and the magnetic properties were measured by vibrating sample magnetometer. Macrophages (RAW 264.7) were co-cultured with the nanofibrous membranes for 12, 24, and 48 h and exhibited good cell viability (>95%). Results showed that the PVA fibers would be degraded and the embedded Fe3O4 nanoparticles would be released and delivered to cells.

  8. Apatite coating of electrospun PLGA fibers using a PVA vehicle system carrying calcium ions.

    PubMed

    Kim, In Ae; Rhee, Sang-Hoon

    2010-01-01

    A novel method to coat electrospun poly(D,L-lactic-co-glycolic acid) (PLGA) fiber surfaces evenly and efficiently with low-crystalline carbonate apatite crystals using a poly(vinyl alcohol) (PVA) vehicle system carrying calcium ions was presented. A non-woven PLGA fabric was prepared by electrospinning: a 10 wt% PLGA solution was prepared using 1,1,3,3-hexafluoro-2-propanol as a solvent and electrospun under a electrical field of 1 kV/cm using a syringe pump with a flowing rate of 3 ml/h. The non-woven PLGA fabric, 12 mm in diameter and 1 mm in thickness, was cut and then coated with a PVA solution containing calcium chloride dihydrate (specimen PPC). As controls, pure non-woven PLGA fabric (specimen P) and fabric coated with a calcium chloride dihydrate solution without PVA (specimen PC) were also prepared. Three specimens were exposed to simulated body fluid for 1 week and this exposure led to form uniform and complete apatite coating layer on the fiber surfaces of specimen PPC. However, no apatite had formed to the fiber surfaces of specimen P and only inhomogeneous coating occurred on the fiber surfaces of specimen PC. These results were explained in terms of the calcium chelating and adhesive properties of PVA vehicle system. The practical implication of the results is that this method provides a simple but efficient technique for coating the fiber surface of an initially non-bioactive material with low-crystalline carbonate apatite.

  9. Changes induced by UV radiation in the presence of sodium benzoate in films formulated with polyvinyl alcohol and carboxymethyl cellulose.

    PubMed

    Villarruel, S; Giannuzzi, L; Rivero, S; Pinotti, A

    2015-11-01

    This work was focused on: i) developing single and blend films based on carboxymethyl cellulose (CMC) and polyvinyl alcohol (PVOH) studying their properties, ii) analyzing the interactions between CMC and PVOH and their modifications UV-induced in the presence of sodium benzoate (SB), and iii) evaluating the antimicrobial capacity of blend films containing SB with and without UV treatment. Once the blend films with SB were exposed to UV radiation, they exhibited lower moisture content as well as a greater elongation at break and rougher surfaces compared to those without treatment. Considering oxygen barrier properties, the low values obtained would allow their application as packaging with selective oxygen permeability. Moreover, the characteristics of the amorphous phase of the matrix prevailed with a rearrangement of the structure of the polymer chain, causing a decrease of the crystallinity degree. These results were supported by X-rays and DSC analysis. FT-IR spectra reflected some degree of polymer-polymer interaction at a molecular level in the amorphous regions. The incorporation of sodium benzoate combined with UV treatment in blend films was positive from the microbial point of view because of the growth inhibition of a wide spectrum of microorganisms. From a physicochemical perspective, the UV treatment of films also changed their morphology rendering them more insoluble in water, turning the functionalized blend films into a potential material to be applied as food packaging.

  10. Influence of surface concentration on poly(vinyl alcohol) behavior at the water-vacuum interface: a molecular dynamics simulation study.

    PubMed

    Tesei, Giulio; Paradossi, Gaio; Chiessi, Ester

    2014-06-19

    Poly(vinyl alcohol) (PVA) is an amphiphilic macromolecule with surfactant activity. The peculiar behavior of this polymer at the water-air interface is at the basis of its use as material for hydrated microdevices, films, and nanofibers. This work aims to investigate the behavior of PVA and water within the surface domain of highly diluted aqueous solutions by means of atomistic molecular dynamics simulations. Monodisperse atactic oligomers of 30 residues were distributed within water slabs in a vacuum box and allowed to diffuse toward the surface. After equilibration, structural features and dynamical properties of polymer chains and water in the interfacial domains were analyzed as a function of PVA surface concentration at 293 K. Surface pressure values obtained from simulations are in agreement with experimental values at corresponding polymer specific surface areas. In the explored concentration range of 6-34 μmol of residues/m(2), the chains display a transition between two states. At lower surface concentrations, elongated, quite rigid structures are adsorbed on the surface, whereas partially submerged globular aggregates, locally covered by thin water layers, are formed at higher surface concentrations. At PVA concentrations higher than about 20 μmol of residues/m(2), the percolation of chain aggregates over the interface plane produces a surface-confined polymer network with stable pores filled by water molecules. A substantial slowing of polymer and water dynamics in the interfacial domains is highlighted by the mean squared displacement time behavior of terminal residues and the interaction time of PVA-water hydrogen bonding. The diffusion coefficient of water and lifetime of hydrogen bonds between solvent molecules are halved and doubled, respectively, at the interface with the highest polymer concentration. The attenuation of water and polymer mobility concur to stabilize PVA hydrated networks in contact with air.

  11. Measurements of Dynamic Viscoelasticity of Poly (vinyl alcohol) Hydrogel for the Development of Blood Vessel Biomodeling

    NASA Astrophysics Data System (ADS)

    Kosukegawa, Hiroyuki; Mamada, Keisuke; Kuroki, Kanju; Liu, Lei; Inoue, Kosuke; Hayase, Toshiyuki; Ohta, Makoto

    In vitro blood vessel biomodeling with realistic mechanical properties and geometrical structures is helpful for training in surgical procedures, especial those used in endovascular treatment. Poly (vinyl alcohol) hydrogel (PVA-H), which is made of Poly (vinyl alcohol) (PVA) and water, may be useful as a material for blood vessel biomodeling due to its low surface friction resistance and good transparency. In order to simulate the mechanical properties of blood vessels, measurements of mechanical properties of PVA-H were carried out with a dynamic mechanical analyzer, and the storage modulus (G’) and loss modulus (G”) of PVA-H were obtained. PVA-Hs were prepared by the low-temperature crystallization method. They were made of PVA with various concentrations (C) and degrees of polymerization (DP), and made by blending two kinds of PVA having different DP or saponification values (SV). The G’ and G” of PVA-H increased, as the C or DP of PVA increased, or as the proportion of PVA with higher DP or SV increased. These results indicate that it is possible to obtain PVA-H with desirable dynamic viscoelasticity. Furthermore, it is suggested that PVA-H is stable in the temperature range of 0°C to 40°C, indicating that biomodeling made of PVA-H should be available at 37°C, the physiological temperature. The dynamic viscoelasticity of PVA-H obtained was similar to that of the dog blood vessel measured in previous reports. In conclusion, PVA-H is suggested to be useful as a material of blood vessel biomodeling.

  12. Spectroscopic analysis of PVA/CMC: NiCuZnFe2O4 polymer nanocomposites

    NASA Astrophysics Data System (ADS)

    Hemalatha, K.; Mahadevaiah, G., Thejas Urs; Somashekarappa, H.; Somashekar, R.

    2015-06-01

    Nickel copper zinc ferrite nanoparticle doped PVA/CMC nanocomposites are synthesized by solution casting method. Wide angle X-ray scattering technique has been used to characterize these nanocomposites. Using Williamson-Hall plot we have determined the microcrystalline parameters like crystallite size and lattice strain for theses samples for various concentration of nanoparticles. We find significant changes in the microstructural parameters with the concentration of nanoparticles. The prepared films are analyzed using FTIR.

  13. Application of the two-film model to the volatilization of acetone and t-butyl alcohol from water as a function of temperature

    USGS Publications Warehouse

    Rathbun, R.E.; Tai, D.Y.

    1988-01-01

    The two-film model is often used to describe the volatilization of organic substances from water. This model assumes uniformly mixed water and air phases separated by thin films of water and air in which mass transfer is by molecular diffusion. Mass-transfer coefficients for the films, commonly called film coefficients, are related through the Henry's law constant and the model equation to the overall mass-transfer coefficient for volatilization. The films are modeled as two resistances in series, resulting in additive resistances. The two-film model and the concept of additivity of resistances were applied to experimental data for acetone and t-butyl alcohol. Overall mass-transfer coefficients for the volatilization of acetone and t-butyl alcohol from water were measured in the laboratory in a stirred constant-temperature bath. Measurements were completed for six water temperatures, each at three water mixing conditions. Wind-speed was constant at about 0.1 meter per second for all experiments. Oxygen absorption coefficients were measured simultaneously with the measurement of the acetone and t-butyl alcohol mass-transfer coefficients. Gas-film coefficients for acetone, t-butyl alcohol, and water were determined by measuring the volatilization fluxes of the pure substances over a range of temperatures. Henry's law constants were estimated from data from the literature. The combination of high resistance in the gas film for solutes with low values of the Henry's law constants has not been studied previously. Calculation of the liquid-film coefficients for acetone and t-butyl alcohol from measured overall mass-transfer and gas-film coefficients, estimated Henry's law constants, and the two-film model equation resulted in physically unrealistic, negative liquid-film coefficients for most of the experiments at the medium and high water mixing conditions. An analysis of the two-film model equation showed that when the percentage resistance in the gas film is large and

  14. Three methods for in situ cross-linking of polyvinyl alcohol films for application as ion-conducting membranes in potassium hydroxide electrolyte. [battery separators

    NASA Technical Reports Server (NTRS)

    Philipp, W. H.; Hsu, L. C.

    1979-01-01

    Three methods of in situ cross-linking polyvinyl alcohol films are presented. They are: (1) acetalization with a dialdehyde such as glutaraldehyde, (2) acetalization with aldehyde groups formed by selective oxidative cleaving of the few percent of 1,2 diol units present in polyvinyl alcohol, and (3) cross-linking by hydrogen abstraction by reaction with hydrogen atoms and hydroxyl radicals from irradiated water. For the third method, improvement in film conductivity in KOH solution at the expense of mechanical strength is obtained by the presence of polyacrylic acid in the polyvinyl alcohol films. Resistivities in 45 percent KOH are given for in situ cross-linked films prepared by each of the three methods.

  15. PVA with nopal dye as holographic recording material

    NASA Astrophysics Data System (ADS)

    Toxqui-López, S.; Olivares-Pérez, A.; Fuentes-Tapia, I.; Pinto-Iguanero, B.

    2011-09-01

    Cactus nopal dye is introduced into a polyvinyl alcohol matrix achieving a like brown appearance thick film, such that they can be used as a recording medium. This dye material provides excellent property as photosensitizer, i.e., easy handling, low cost and can be used in real time holographic recording applications. The experimental results show the diffraction efficiencies obtained by recording grating patterns induced by a He-Cd laser (442nm). For the samples, a thick film of polyvinyl alcohol and dye from cactus nopal was deposited by the gravity technique on a glass substrate. This mixture dries to form a photosensitive emulsion.

  16. Ionic conductivity studies in crystalline PVA/NaAlg polymer blend electrolyte doped with alkali salt KCl

    NASA Astrophysics Data System (ADS)

    Sheela, T.; Bhajantri, R. F.; Ravindrachary, V.; Pujari, P. K.; Rathod, Sunil G.; Naik, Jagadish

    2014-04-01

    Potassium Chloride (KCl) doped poly(vinyl alcohol) (PVA)/sodium alginate (NaAlg) in 60:40 wt% polymer blend electrolytes were prepared by solution casting method. The complexation of KCl with host PVA/NaAlg blend is confirmed by FTIR and UV-Vis spectra. The XRD studies show that the crystallinity of the prepared blends increases with increase in doping. The dc conductivity increases with increase in dopant concentration. Temperature dependent dc conductivity shows an Arrhenius behavior. The dielectric properties show that both the dielectric constant and dielectric loss increases with increase in KCl doping concentration and decreases with frequency. The cole-cole plots show a decrease in bulk resistance, indicates the increase in ac conductivity, due to increase in charge carrier mobility. The doping of KCl enhances the mechanical properties of PVA/NaAlg, such as Young's modulus, tensile strength, stiffness.

  17. Uniaxial Drawing of Graphene-PVA Nanocomposites: Improvement in Mechanical Characteristics via Strain-Induced Exfoliation of Graphene

    NASA Astrophysics Data System (ADS)

    Jan, Rahim; Habib, Amir; Akram, Muhammad Aftab; Zia, Tanveer-ul-Haq; Khan, Ahmad Nawaz

    2016-08-01

    Polyvinyl alcohol (PVA)-stabilized graphene nanosheets (GNS) of lateral dimension ( L) ~1 μm are obtained via liquid phase exfoliation technique to prepare its composites in the PVA matrix. These composites show low levels of reinforcements due to poor alignment of GNS within the matrix as predicted by the modified Halpin-Tsai model. Drawing these composites up to 200 % strain, a significant improvement in mechanical properties is observed. Maximum values for Young's modulus and strength are ~×4 and ~×2 higher respectively than that of neat PVA. Moreover, the rate of increase of the modulus with GNS volume fraction is up to 700 GPa, higher than the values predicted using the Halpin-Tsai theory. However, alignment along with strain-induced de-aggregation of GNS within composites accounts well for the obtained results as confirmed by X-ray diffraction (XRD) characterization.

  18. Uniaxial Drawing of Graphene-PVA Nanocomposites: Improvement in Mechanical Characteristics via Strain-Induced Exfoliation of Graphene.

    PubMed

    Jan, Rahim; Habib, Amir; Akram, Muhammad Aftab; Zia, Tanveer-Ul-Haq; Khan, Ahmad Nawaz

    2016-12-01

    Polyvinyl alcohol (PVA)-stabilized graphene nanosheets (GNS) of lateral dimension (L) ~1 μm are obtained via liquid phase exfoliation technique to prepare its composites in the PVA matrix. These composites show low levels of reinforcements due to poor alignment of GNS within the matrix as predicted by the modified Halpin-Tsai model. Drawing these composites up to 200 % strain, a significant improvement in mechanical properties is observed. Maximum values for Young's modulus and strength are ~×4 and ~×2 higher respectively than that of neat PVA. Moreover, the rate of increase of the modulus with GNS volume fraction is up to 700 GPa, higher than the values predicted using the Halpin-Tsai theory. However, alignment along with strain-induced de-aggregation of GNS within composites accounts well for the obtained results as confirmed by X-ray diffraction (XRD) characterization. PMID:27558496

  19. Preparation and photochromic properties of ultra-fine H3PW11MoO40/PVA fibre mats

    NASA Astrophysics Data System (ADS)

    Yang, Guo-Cheng; Gong, Jian; Pan, Yan; Cui, Xiu-Jun; Shao, Chang-Lu; Guo, Yi-Hang; Wen, Shang-Bin; Qu, Lun-Yu

    2004-07-01

    Novel photochromic materials, H3PW11MoO40/Poly (vinyl alcohol) (PVA) ultra-fine fibre mats containing different weight percentages of H3PW11MoO40, have been prepared from different H3PW11MoO40/PVA solutions by an electrospinning technique. IR spectroscopy, wide-angle x-ray diffraction, and scanning electron microscope spectroscopy are used to characterize the fibre mats. Results of viscosity and conductivity measurements of the solutions indicate that lower viscosity and higher conductivity favour the formation of thin fibres without beads. When irradiated with ultraviolet light (313.2 nm), the colour of the fibre mats changes from white to blue, and the mats show reversible photochromism. IR and ESR spectra of the irradiated fibre mats indicate a conceivable photochromic mechanism, i.e. MoVI is reduced under ultraviolet irradiation. Meanwhile, PVA is oxidized to unsaturated ketone or aldehyde.

  20. A Simple Visual Ethanol Biosensor Based on Alcohol Oxidase Immobilized onto Polyaniline Film for Halal Verification of Fermented Beverage Samples

    PubMed Central

    Kuswandi, Bambang; Irmawati, Titi; Hidayat, Moch Amrun; Jayus; Ahmad, Musa

    2014-01-01

    A simple visual ethanol biosensor based on alcohol oxidase (AOX) immobilised onto polyaniline (PANI) film for halal verification of fermented beverage samples is described. This biosensor responds to ethanol via a colour change from green to blue, due to the enzymatic reaction of ethanol that produces acetaldehyde and hydrogen peroxide, when the latter oxidizes the PANI film. The procedure to obtain this biosensor consists of the immobilization of AOX onto PANI film by adsorption. For the immobilisation, an AOX solution is deposited on the PANI film and left at room temperature until dried (30 min). The biosensor was constructed as a dip stick for visual and simple use. The colour changes of the films have been scanned and analysed using image analysis software (i.e., ImageJ) to study the characteristics of the biosensor's response toward ethanol. The biosensor has a linear response in an ethanol concentration range of 0.01%–0.8%, with a correlation coefficient (r) of 0.996. The limit detection of the biosensor was 0.001%, with reproducibility (RSD) of 1.6% and a life time up to seven weeks when stored at 4 °C. The biosensor provides accurate results for ethanol determination in fermented drinks and was in good agreement with the standard method (gas chromatography) results. Thus, the biosensor could be used as a simple visual method for ethanol determination in fermented beverage samples that can be useful for Muslim community for halal verification. PMID:24473284

  1. Study of nanoparticles TiO2 thin films on p-type silicon substrate using different alcoholic solvents

    NASA Astrophysics Data System (ADS)

    Muaz, A. K. M.; Hashim, U.; Arshad, M. K. Md.; Ruslinda, A. R.; Ayub, R. M.; Gopinath, Subash C. B.; Voon, C. H.; Liu, Wei-Wen; Foo, K. L.

    2016-07-01

    In this paper, sol-gel method spin coating technique is adopted to prepare nanoparticles titanium dioxide (TiO2) thin films. The prepared TiO2 sol was synthesized using titanium butoxide act as a precursor and subjected to deposited on the p-type silicon oxide (p-SiO2) and glass slide substrates under room temperature. The effect of different alcoholic solvents of methanol and ethanol on the structural, morphological, optical and electrical properties were systematically investigated. The coated TiO2 thin films were annealed in furnace at 773 K for 1 h. The structural properties of the TiO2 films were examined with X-ray Diffraction (XRD). From the XRD analysis, both solvents showing good crystallinity with anatase phase were the predominant structure. Atomic Force Microscopy (AFM) was employed to study the morphological of the thin films. The optical properties were investigated by Ultraviolet-visible (UV-Vis) spectroscopy were found that ethanol as a solvent give a higher optical transmittance if compare to the methanol solvent. The electrical properties of the nanoparticles TiO2 thin films were measured using two-point-probe technique.

  2. A simple visual ethanol biosensor based on alcohol oxidase immobilized onto polyaniline film for halal verification of fermented beverage samples.

    PubMed

    Kuswandi, Bambang; Irmawati, Titi; Hidayat, Moch Amrun; Jayus; Ahmad, Musa

    2014-01-27

    A simple visual ethanol biosensor based on alcohol oxidase (AOX) immobilised onto polyaniline (PANI) film for halal verification of fermented beverage samples is described. This biosensor responds to ethanol via a colour change from green to blue, due to the enzymatic reaction of ethanol that produces acetaldehyde and hydrogen peroxide, when the latter oxidizes the PANI film. The procedure to obtain this biosensor consists of the immobilization of AOX onto PANI film by adsorption. For the immobilisation, an AOX solution is deposited on the PANI film and left at room temperature until dried (30 min). The biosensor was constructed as a dip stick for visual and simple use. The colour changes of the films have been scanned and analysed using image analysis software (i.e., ImageJ) to study the characteristics of the biosensor's response toward ethanol. The biosensor has a linear response in an ethanol concentration range of 0.01%-0.8%, with a correlation coefficient (r) of 0.996. The limit detection of the biosensor was 0.001%, with reproducibility (RSD) of 1.6% and a life time up to seven weeks when stored at 4 °C. The biosensor provides accurate results for ethanol determination in fermented drinks and was in good agreement with the standard method (gas chromatography) results. Thus, the biosensor could be used as a simple visual method for ethanol determination in fermented beverage samples that can be useful for Muslim community for halal verification.

  3. Gel spinning of PVA composite fibers with high content of multi-walled carbon nanotubes and graphene oxide hybrids

    NASA Astrophysics Data System (ADS)

    Wei, Yizhe; Lai, Dengpan; Zou, Liming; Ling, Xinlong; Lu, Hongwei; Xu, Yongjing

    2015-07-01

    In this report, poly (vinyl alcohol) (PVA) composite fibers with high content of multi-walled carbon nanotubes and graphene oxide (MWCNTs-GO) hybrids were prepared by gel spinning, and were characterized by TGA, DSC, SEM, XL-2 yarn strength tester and electrical conductivity measurement. The total content of MWCNTs-GO hybrids in the PVA composite fibers, which is up to 25 wt%, was confirmed by TGA analysis. The DSC measurement shows that the melting and crystallization peaks decreased after the addition of nano-fillers. This is due to the reason that the motion of PVA chains is completely confined by strong hydrogen bonding interaction between PVA and nano-fillers. After the addtion of GO, the dispersibility of MWCNTs in composite fibers improved slightly. And the tensile strength and Young's modulus increased by 38% and 67%, respectively. This is caused by the increased hydrogen bonding interaction and synergistic effect through hybridization of MWCNTs and GO. More significantly, the electrical conductivity of PVA/MWCNTs/GO composite fibers enhanced by three orders of magnitude with the addition of GO.

  4. Tuning the SERS Response with Ag-Au Nanoparticle-Embedded Polymer Thin Film Substrates.

    PubMed

    Rao, V Kesava; Radhakrishnan, T P

    2015-06-17

    Development of facile routes to the fabrication of thin film substrates with tunable surface enhanced Raman scattering (SERS) efficiency and identification of the optimal conditions for maximizing the enhancement factor (EF) are significant in terms of both fundamental and application aspects of SERS. In the present work, polymer thin films with embedded bimetallic nanoparticles of Ag-Au are fabricated by a simple two-stage protocol. Ag nanoparticles are formed in the first stage, by the in situ reduction of silver nitrate by the poly(vinyl alcohol) (PVA) film through mild thermal annealing, without any additional reducing agent. In the second stage, aqueous solutions of chloroauric acid spread on the Ag-PVA thin film under ambient conditions, lead to the galvanic displacement of Ag by Au in situ inside the film, and the formation of Ag-Au particles. Evolution of the morphology of the bimetallic nanoparticles into hollow cage structures and the distribution of Au on the nanoparticles are revealed through electron microscopy and energy dispersive X-ray spectroscopy. The localized surface plasmon resonance (LSPR) extinction of the nanocomposite thin film evolves with the Ag-Au composition; theoretical simulation of the extinction spectra provides insight into the observed trends. The Ag-Au-PVA thin films are found to be efficient substrates for SERS. The EF follows the variation of the LSPR extinction vis-à-vis the excitation laser wavelength, but with an offset, and the maximum SERS effect is obtained at very low Au content; experiments with Rhodamine 6G showed EFs on the order of 10(8) and a limit of detection of 0.6 pmol. The present study describes a facile and simple fabrication of a nanocomposite thin film that can be conveniently deployed in SERS investigations, and the utility of the bimetallic system to tune and maximize the EF.

  5. Performance of composite Nafion/PVA membranes for direct methanol fuel cells

    NASA Astrophysics Data System (ADS)

    Mollá, Sergio; Compañ, Vicente

    2011-03-01

    This work has been focused on the characterization of the methanol permeability and fuel cell performance of composite Nafion/PVA membranes in function of their thickness, which ranged from 19 to 97 μm. The composite membranes were made up of Nafion® polymer deposited between polyvinyl alcohol (PVA) nanofibers. The resistance to methanol permeation of the Nafion/PVA membranes shows a linear variation with the thickness. The separation between apparent and true permeability permits to give an estimated value of 4.0 × 10-7 cm2 s-1 for the intrinsic or true permeability of the bulk phase at the composite membranes. The incorporation of PVA nanofibers causes a remarkable reduction of one order of magnitude in the methanol permeability as compared with pristine Nafion® membranes. The DMFC performances of membrane-electrode assemblies prepared from Nafion/PVA and pristine Nafion® membranes were tested at 45, 70 and 95 °C under various methanol concentrations, i.e., 1, 2 and 3 M. The nanocomposite membranes with thicknesses of 19 μm and 47 μm reached power densities of 211 mW cm-2 and 184 mW cm-2 at 95 °C and 2 M methanol concentration. These results are comparable to those found for Nafion® membranes with similar thickness at the same conditions, which were 210 mW cm-2 and 204 mW cm-2 respectively. Due to the lower amount of Nafion® polymer present within the composite membranes, it is suggested a high degree of utilization of Nafion® as proton conductive material within the Nafion/PVA membranes, and therefore, significant savings in the consumed amount of Nafion® are potentially able to be achieved. In addition, the reinforcement effect caused by the PVA nanofibers offers the possibility of preparing membranes with very low thickness and good mechanical properties, while on the other hand, pristine Nafion® membranes are unpractical below a thickness of 50 μm.

  6. Development of functionalized hydroxyapatite/poly(vinyl alcohol) composites

    NASA Astrophysics Data System (ADS)

    Stipniece, Liga; Salma-Ancane, Kristine; Rjabovs, Vitalijs; Juhnevica, Inna; Turks, Maris; Narkevica, Inga; Berzina-Cimdina, Liga

    2016-06-01

    Based on the well-known pharmaceutical excipient potential of poly(vinyl alcohol) (PVA) and clinical success of hydroxyapatite (HAp), the objective of this work was to fabricate functionalized composite microgranules. PVA was modified with succinic anhydride to introduce carboxyl groups (-COOH), respectively, by reaction between the -OH groups of PVA and succinic anhydride, for attachment of drug molecules. For the first time, the functionalized composite microgranules containing HAp/PVA in the ratio of 1:1 were prepared through in situ precipitation of HAp in modified PVA aqueous solutions followed by spray drying of obtained suspensions. The microgranules were characterized by Fourier-transform infrared spectroscopy (FT-IR), X-ray diffraction (XRD), field emission scanning electron microscopy (FE-SEM), and differential scanning calorimetry (DSC). The presence of -COOH groups was verified by FT-IR, and the amount of functional groups added to PVA molecules (averaging 15 mol%) was determined by nuclear magnetic resonance spectroscopy (NMR). DSC results showed that modification with -COOH groups slightly decreased the thermal stability of PVA. FT-IR and XRD analysis confirmed that the resulting composites contain mainly nanocrystalline HAp and PVA. Moreover, the images taken by FE-SEM revealed that the microgranules consisted of nanosized HAp crystallites homogenously embedded in the PVA matrix. DSC measurements indicated that decomposition mechanism of the HAp/PVA differs from that of pure PVA and occurs at lower temperatures. However, the presence of HAp had minor influence on the thermal decomposition of the PVA modified with succinic anhydride. The investigation of composite microgranules confirmed interaction and integration between the HAp and PVA.

  7. Copper-containing polyvinyl alcohol composite systems: Preparation, characterization and biological activity

    NASA Astrophysics Data System (ADS)

    Reza Hajipour, Abdol; Mohammadsaleh, Fatemeh; Reza Sabzalian, Mohammad

    2015-08-01

    The present investigation reports, the complex formation of Cu(II) with polyvinyl alcohol (PVA) and the synthesis of PVA-stabilized Cu2O particles. This PVA-Cu2O composite has been prepared via chemical reduction method using PVA-Cu(II) complex as precursor. At first, Cu(II) ions were stabilized in PVA matrix via complex formation with OH groups; subsequently, this PVA-Cu(II) macromolecular complex as precursor reacted with ascorbic acid as reducing agent at pH=12 to prepare PVA-Cu2O composite. The products were characterized by FTIR, XRD, FE-SEM, HRTEM, Visible Spectroscopy and atomic absorption. In the following, the antibacterial properties of as-prepared composites were examined against Gram-positive (Bacillus thuringiensis) and Gram-negative bacteria (Escherichia coli), and the results showed excellent antibacterial activity of these materials.

  8. Characterization of proton conducting blend polymer electrolyte using PVA-PAN doped with NH4SCN

    NASA Astrophysics Data System (ADS)

    Premalatha, M.; Mathavan, T.; Selvasekarapandian, S.; Genova, F. Kingslin Mary; Umamaheswari, R.

    2016-05-01

    Polymer electrolytes with proton conductivity based on blend polymer using polyvinyl alcohol (PVA) and poly acrylo nitrile (PAN) doped with ammonium thiocyanate have been prepared by solution casting method using DMF as solvent. The complex formation between the blend polymer and the salt has been confirmed by FTIR Spectroscopy. The amorphous nature of the blend polymer electrolytes have been confirmed by XRD analysis. The highest conductivity at 303 K has been found to be 3.25 × 10-3 S cm-1 for 20 mol % NH4SCN doped 92.5PVA:7.5PAN system. The increase in conductivity of the doped blend polymer electrolytes with increasing temperature suggests the Arrhenius type thermally activated process. The activation energy is found to be low (0.066 eV) for the highest conductivity sample.

  9. Cationic-modified PVA as a dry strength additive for rice straw fibers.

    PubMed

    Fatehi, P; Tutus, A; Xiao, H

    2009-01-01

    Extensive research has shown that non-wood fibers are able to be substituted for wood fibers. The major shortcoming of non-fibers is their high silica content that causes some operational problems in mills, and hence silica should be kept in pulps. By keeping silica in pulps, however, the mechanical properties of papers are reduced, and a dry strength additive may be required. In this study, cationic polyvinyl alcohols (C-PVA) with two different molecular weights were prepared, and employed as dry strength additives. The adsorption of polymers on rice straw fibers obtained via soda-air-anthraquinone (AQ) pulping under various conditions was investigated thoroughly. Convincing results demonstrated that high molecular weight polymers performed more efficiently on dry strength enhancements of papers, while they adsorbed less than lower molecular weight polymers on fibers. However, the stiffness of fibers was increased to a larger extent by applying a higher molecular weight C-PVA. PMID:18774707

  10. Spectroelectrochemical Studies on Quinacridone by Using Poly(vinyl alcohol) Coating as Protection Layer

    PubMed Central

    Enengl, Sandra; Enengl, Christina; Stadler, Philipp; Neugebauer, Helmut; Sariciftci, Niyazi Serdar

    2015-01-01

    Spectroscopic measurements in the infrared range combined with electrochemistry are a powerful technique for investigation of organic semiconductors to track changes during oxidation and reduction (p- and n-doping) processes. For these measurements it is important that the studied material, mostly deposited as a thin film on an internal reflection element, does not dissolve during this characterization. In this study we introduce a technique that allows infrared spectroelectrochemical characterization of films of these materials for the first time. In many cases so far this has been impossible, due to solubility in the oxidized and/or reduced form. This novel technique is shown on thin films of quinacridone by adding a protection layer of poly(vinyl alcohol) (PVA). PMID:26013836

  11. Lysozyme-immobilized electrospun PAMA/PVA and PSSA-MA/PVA ion-exchange nanofiber for wound healing.

    PubMed

    Tonglairoum, Prasopchai; Ngawhirunpat, Tanasait; Rojanarata, Theerasak; Opanasopit, Praneet

    2014-08-27

    Abstract This research was aimed to develop the lysozyme immobilized ion-exchange nanofiber mats for wound healing. To promote the healing process, the PSSA-MA/PVA and PAMA ion-exchange nanofiber mats were fabricated to mimic the extracellular matrix structure using electrospinning process followed by thermally crosslinked. Lysozyme was immobilized on the ion-exchane nanofibers by an adsorption method. The ion-exchange nanofibers were investigated using SEM, FTIR and XRPD. Moreover, the lysozyme-immobilized ion-exchange nanofibers were further investigated for lysozyme content and activity, lysozyme release and wound healing activity. The fiber diameters of the mats were in the nanometer range. Lysozyme was gradually absorbed into the PSSA-MA/PVA nanofiber with higher extend than that is absorbed on the PAMA/PVA nanofiber and exhibited higher activity than lysozyme-immobilized PAMA/PVA nanofiber. The total contents of lysozyme on the PSSA-MA/PVA and PAMA/PVA nanofiber were 648 and 166 µg/g, respectively. FTIR and lysozyme activity results confirmed the presence of lysozyme on the nanofiber mats. The lysozyme was released from the PSSA-MA/PVA and PAMA/PVA nanofiber in the same manner. The lysozyme-immobilized PSSA-MA/PVA nanofiber mats and lysozyme-immobilized PAMA/PVA nanofiber mats exhibited significantly faster healing rate than gauze and similar to the commercial antibacterial gauze dressing. These results suggest that these nanofiber mats could provide the promising candidate for wound healing application.

  12. The synthesis of high molecular weight partially hydrolysed poly(vinyl alcohol) grades suitable for nanoparticle fabrication.

    PubMed

    Chana, Jasminder; Forbes, Ben; Jones, Stuart Allen

    2008-11-01

    Poly(vinyl alcohol) (PVA) is a highly versatile synthetic polymer that is formed by full or partial hydrolysis of poly(vinyl acetate) (PVAc). A wide range of PVA partially hydrolysed grades are commercially available, but the amphiphilic grades of the polymer (30-60% hydrolysis), which probably the most interesting in terms of drug delivery, are not readily available. As a consequence few studies have assessed the application of low hydrolysis PVA polymers to form nanocarriers. The aims of this study were to synthesise amphiphilic grades of PVA on a laboratory scale, analyse their chemical properties and determine whether these grades could be used to form nanoparticles. PVA 30%, PVA 40%, PVA 50% and PVA 60% were synthesised via direct saponification of PVAc. All grades of PVA synthesised had degrees of hydrolysis close to those predicted from the stoichiometry of the saponification reaction. The PVA grades displayed <1.5% batch to batch variability (n=3) in terms of percentage hydrolysis, demonstrating the manufacture process was both reproducible and predictable. Analysis of the polymer characteristics using 13C nuclear magnetic resonance and differential scanning calorimetry revealed that all PVA grades contained block distributions (i.e., eta <1) of vinyl alcohol monomers (eta ranged from 0.33-0.45) with a high probability of adjacency calculated for the hydroxylated units (P(OH) ranged 0.926-0.931). All the grades of PVA formed nanoparticles using a precipitation technique with a trend towards smaller particle size with increasing degree of PVA hydrolysis; PVA 30% resulted in significantly larger nanoparticles (225 nm) compared to PVA 40-60% (137-174 nm).

  13. Linear and nonlinear optical study of pure PVA and CdSe doped PVA nanocomposite

    NASA Astrophysics Data System (ADS)

    Tyagi, Chetna; Sharma, Ambika

    2016-05-01

    This research work reports the synthesis and optical properties of CdSe/PVA polymer nanocomposite (PNC's) prepared by wet chemical co-precipitation method. The transmission spectra obtained from UV-Vis-NIR spectrophotometer has been investigated to determine the optical properties of PNC's. Absorption spectra give the information about energy band gap (Eg) and type of transition. Refractive index (n), extinction coefficient (k) was calculated using well known Swanepoel method. Wemple-Di Domenico model (WDD) has been used to calculate dispersion energy (Ed) and oscillator energy (E0). Boling formula is used to calculate nonlinear refractive index (n2) of CdSe/PVA nanocomposite.

  14. Efficient etching-free transfer of high quality, large-area CVD grown graphene onto polyvinyl alcohol films

    NASA Astrophysics Data System (ADS)

    Marta, Bogdan; Leordean, Cosmin; Istvan, Todor; Botiz, Ioan; Astilean, Simion

    2016-02-01

    Graphene transfer is a procedure of paramount importance for the production of graphene-based electronic devices. The transfer procedure can affect the electronic properties of the transferred graphene and can be detrimental for possible applications both due to procedure induced defects which can appear and due to scalability of the method. Hence, it is important to investigate new transfer methods for graphene that are less time consuming and show great promise. In the present study we propose an efficient, etching-free transfer method that consists in applying a thin polyvinyl alcohol layer on top of the CVD grown graphene on Cu and then peeling-off the graphene onto the polyvinyl alcohol film. We investigate the quality of the transferred graphene before and after the transfer, using Raman spectroscopy and imaging as well as optical and atomic force microscopy techniques. This simple transfer method is scalable and can lead to complete transfer of graphene onto flexible and transparent polymer support films without affecting the quality of the graphene during the transfer procedure.

  15. Core-shell nanofibers: Integrating the bioactivity of gelatin and the mechanical property of polyvinyl alcohol.

    PubMed

    Merkle, Valerie M; Zeng, Like; Slepian, Marvin J; Wu, Xiaoyi

    2014-04-01

    Coaxial electrospinning is used to fabricate nanofibers with gelatin in the shell and polyvinyl alcohol (PVA) in the core in order to derive mechanical strength from PVA and bioactivity from gelatin. At a 1:1 PVA/gelatin mass ratio, the core-shell nanofiber scaffolds display a Young's modulus of 168.6 ± 36.5 MPa and a tensile strength of 5.42 ± 1.95 MPa, which are significantly higher than those of the scaffolds composed solely of gelatin or PVA. The Young's modulus and tensile strength of the core-shell nanofibers are further improved by reducing the PVA/gelatin mass ratio from 1:1 to 1:3. The mechanical analysis of the core-shell nanofibers suggests that the presence of the gelatin shell may improve the molecular alignment of the PVA core, transforming the semi-crystalline, plastic PVA into a more crystallized, elastic PVA, and enhancing the mechanical properties of the core. Lastly, the PVA/gelatin core-shell nanofibers possess cellular viability, proliferation, and adhesion similar to these of the gelatin nanofibers, and show significantly higher proliferation and adhesion than the PVA nanofibers. Taken together, the coaxial electrospinning of nanofibers with a core-shell structure permits integration of the bioactivity of gelatin and the mechanical strength of PVA in single fibers.

  16. Vaginal absorption of polyvinyl alcohol in Fischer 344 rats.

    PubMed

    Sanders, J M; Matthews, H B

    1990-03-01

    Polyvinyl alcohol (PVA) is a polymer with a wide range of molecular weights and uses. Recently, low molecular weight formulations of PVA have been used as components of contraceptive products designed for intravaginal administration in human females. Previous studies in animals have determined that little or no absorption of PVA occurs from the gastrointestinal (GI) tract. However, there is some concern that PVA of lower molecular weights might be absorbed across membranes of the reproductive tract. Consequently, this work has investigated the absorption of low molecular weight PVA across biological membranes of the reproductive and GI tracts of Fischer 344 rats. Oral administration of ten consecutive daily doses of 14C PVA resulted in little apparent absorption of the dose from the GI tract. In contrast, intravaginal administration of 14C PVA resulted in increasing concentrations of PVA-derived radioactivity in major tissues following one, three or ten daily doses of the estimated human dose of 3 mg/kg. PVA-derived radioactivity was concentrated mainly in the liver, reaching a peak greater than 1750 ng equivalents/g tissue 24 hours following ten daily doses. Over 300 ng equivalents/g tissue were still present in the liver 30 days following the last dose.

  17. A facile route of microwave to fabricate PVA-coating Ag nanofilm used as NIR-SERS active substrate

    NASA Astrophysics Data System (ADS)

    Liu, Renming; Feng, Mingjun; Zhang, Deqing; Su, Yongbo; Cai, Chenbo; Si, Minzhen

    2013-04-01

    Surface-enhanced Raman spectroscopy (SERS) is a very sensitive and selective technique for detecting surface species. Recently, SERS has been increasingly employed in the study of biological macromolecules, from DNA and peptides to whole proteins, and cells. However, visible laser sources usually employed in SERS detections always lead to photochemical reactions as well as intensive fluorescence emission from the biological samples. A way to avoid these questions is the employment of near infrared (NIR) laser excitation; thus, it demands the appropriate designs of NIR-SERS substrates in order to obtain the maximum enhancement of the Raman signals from biological analytes. In this work, we demonstrate the fabrication of a new NIR-SERS substrate of polyvinyl alcohol (PVA) coating Ag nanofilms (PVA-coating Ag nanofilm) using a simple and low-cost microwave strategy. The experimental data show that, the plasmon resonance band of the PVA-coating Ag nanofilm is in the region of 400-900 nm, and the maximum center is at ∼780 nm, which matches well with the 785 nm laser excitation employed in this work. With the NIR-SERS detections of hematin and hemoglobin molecules adsorbed on this PVA-coating Ag nanofilm, one can see that the NIR-SERS activity and spectroscopy reproducibility of this NIR-SERS substrate are all perfect. By using of the tested molecule of hematin, the PVA-coating Ag nanofilm shows a high enhancement factor (EF) of ∼107. As the fabrication process of this NIR-SERS substrate is very simple and inexpensive, this method may be used in large-scale preparation of SERS substrates that have been widely applied in Raman analysis. Especially, this PVA-coating Ag nanofilm can also be served as a novel NIR-SERS substrate in biochemical analysis due to its good NIR characteristics.

  18. Development of a complex hydrogel of hyaluronan and PVA embedded with silver nanoparticles and its facile studies on Escherichia coli.

    PubMed

    Zhang, Fei; Wu, Juan; Kang, Ding; Zhang, Hongbin

    2013-01-01

    Novel nanocomposite hydrogels composed of hyaluronan (HA), poly(vinyl alcohol) (PVA) and silver nanoparticles were prepared by several cycles of freezing and thawing. The nanocomposite was then characterised using Fourier transform infrared spectroscopy (FTIR), differential scanning calorimetry (DSC), wide-angle X-ray diffraction (XRD) and scanning electron microscopy (SEM). The complex hydrogels consisted of semi-interpenetrating network structures, with PVA microcrystallines as junction zones. By increasing the HA content, the crystallinity and melting temperature of the complex hydrogels decreased, whereas the glass transition temperatures of these materials increased because of the steric hindrance of HA and the occurrence of intermolecular interactions through hydrogen bonding between HA and PVA in the complex hydrogels. Swelling studies showed that in comparison with the swelling properties of the cryogels from PVA alone, those of the complex hydrogels can be significantly improved and presented in a pH-sensitive manner. In addition, silver nanoparticles were synthesised through UV-initiated photoreduction with HA functioning as a reducing agent and stabiliser. The silver nanoparticles were then incorporated in situ into the HA/PVA complex hydrogel matrix. The size and morphology of the as-prepared Ag nanoparticles were investigated through ultraviolet-visible light spectroscopy, transmission electron microscopy, XRD and thermogravimetric analysis. The experimental results indicated that silver nanoparticles 20-50 nm in size were uniformly dispersed in the hydrogel matrix. The antibacterial effects of the HA/PVA/Ag nanocomposite hydrogel against Escherichia coli were evaluated. The results show that this nanocomposite hydrogel possesses high antibacterial property and has a potential application as a wound dressing material. PMID:23829455

  19. The surface structure and thermal properties of novel polymer composite films based on partially phosphorylated poly(vinyl alcohol) with aluminum phosphate.

    PubMed

    Mohamed Saat, Asmalina; Johan, Mohd Rafie

    2014-01-01

    Partially phosphorylated polyvinyl alcohol (PPVA) with aluminum phosphate (ALPO4) composites was synthesized by solution casting technique to produce (PPVA)(100-y) - (ALPO4)(y) (y = 0, 1, and 2). The surface structure and thermal properties of the films were characterized using Fourier transform infrared (FTIR) spectroscopy and thermogravimetric analysis (TGA). The results showed that the films have higher thermal stability with strong bonding between PPVA and ALPO4.

  20. The Surface Structure and Thermal Properties of Novel Polymer Composite Films Based on Partially Phosphorylated Poly(vinyl alcohol) with Aluminum Phosphate

    PubMed Central

    Mohamed Saat, Asmalina

    2014-01-01

    Partially phosphorylated polyvinyl alcohol (PPVA) with aluminum phosphate (ALPO4) composites was synthesized by solution casting technique to produce (PPVA)100−y − (ALPO4)y (y = 0, 1, and 2). The surface structure and thermal properties of the films were characterized using Fourier transform infrared (FTIR) spectroscopy and thermogravimetric analysis (TGA). The results showed that the films have higher thermal stability with strong bonding between PPVA and ALPO4. PMID:25506069

  1. Enhancement of PVA-degrading enzyme production by the application of pH control strategy.

    PubMed

    Li, Min; Zhang, Dongxu; Du, Guocheng; Chen, Jian

    2012-02-01

    In batch culture for Poly(vinyl alcohol) (PVA)-degrading enzyme (PVAase) production by a mixed culture, higher pH (pH 7.5) was favorable for PVAase production at the prophase of cultivation, but lower pH (pH 7.0) was favorable at the anaphase. This situation was caused by the fact that the optimum pH for different key enzymes [PVA dehydrogenase (PVADH) and oxidized PVA hydrolase (OPH)] production is various. The activity and average specific production rate of PVADH reached the highest values at constant pH 7.5, whereas those of OPH appeared at pH 7.0. A two-stage pH control strategy was therefore developed and compared for its potential in improving PVAase production. By using this strategy, the maximal PVAase activity reached 2.05 U/ml, which increased by 15.2% and 24.2% over the fermentation at constant pH 7.5 and 7.0.

  2. Optical Absorption Behavior of co (ii) Ion Doped Pva Assisted CdSe Nanoparticles

    NASA Astrophysics Data System (ADS)

    Ravindranadh, K.; Ravikumar, R. V. S. S. N.; Rao, M. C.

    CdSe is an important II-VI, n-type direct band gap semiconductor with wide band gap (bulk band gap of 2.6 eV) and an attractive host for the development of doped nanoparticles. Poly vinyl alcohol (PVA) is used as a capping agent to stabilize the CdSe nanoparticles. The optical properties of Co (II) ion doped PVA capped CdSe nanoparticles grown at room temperature are studied in the wavelength region of 200-1400 nm. The spectrum of Co (II) ion doped PVA capped CdSe nanoparticles exhibit five bands at 1185, 620, 602, 548 and 465 nm (8437, 16125, 16607, 18243 and 21499 cm-1). The bands observed at 1185, 548 and 465 nm are correspond to the three spin allowed transitions 4T1g (F) → 4T2g (F), 4T1g (F) → 4A2g (F) and 4T1g (F) → 4T1g (P) respectively. The other bands observed at 602 nm and 620 nm are assigned to spin forbidden transitions 4T1g (F) → 2T2g (G), 4T1g (F) → 2T1g (G). The small value of the Urbach energy indicates greater stability of the prepared sample.

  3. Preparation and characterization of electrical conductive PVA based materials for peripheral nerve tube-guides.

    PubMed

    Gonçalves, C; Ribeiro, J; Pereira, T; Luís, A L; Mauricio, A C; Santos, J D; Lopes, M A

    2016-08-01

    Peripheral nerve regeneration is a serious clinical problem. Presently, there are several nerve tube-guides available in the market, however with some limitations. The goal of this work was the development of a biomaterial with high electrical conductivity to produce tube-guides for nerve regeneration after neurotmesis injuries whenrver an end-to-end suture without tension is not possible. A matrix of poly(vinyl alcohol) (PVA) was used loaded with the following electrical conductive materials: COOH-functionalized multiwall carbon nanotubes (MWCNTs), poly(pyrrole) (PPy), magnesium chloride (MgCl2 ), and silver nitrate (AgNO3 ). The tube-guide production was carried out by a freezing/thawing process (physical crosslinking) with a final annealing treatment. After producing the tube-guide for nerve regeneration, the physicochemical characterization was performed. The most interesting results were achieved by loading PVA with 0.05% of PPy or COOH- functionalized CNTs. These tubes combined the electrical conductivity of carbon nanotubes (CNTs) and PPy with the biocompatibility of PVA matrix, with potential clinical application for nerve regeneration. © 2016 Wiley Periodicals, Inc. J Biomed Mater Res Part A: 104A: 1981-1987, 2016. PMID:27027727

  4. NOVEL METALLIC AND BIMETALLIC CROSS-LINKED POLY (VINYL ALCOHOL) NANOCOMPOSITES PREPARED UNDER MICROWAVE IRRADIATION

    EPA Science Inventory

    A facile microwave irradiation approach that results in a cross-linking reaction of poly (vinyl alcohol) (PVA) with metallic and bimetallic systems is described. Nanocomposites of PVA cross-linked metallic systems such as Pt, Cu, and In and bimetallic systems such as Pt-In, Ag-P...

  5. A polyvinyl alcohol-coated silica gel stationary phase for hydrophilic interaction chromatography.

    PubMed

    Ji, Shunli; Zheng, Yang; Zhang, Feifang; Liang, Xinmiao; Yang, Bingcheng

    2015-09-21

    Multiple layers of polyvinyl alcohol (PVA) coating are generated onto silica gel by thermal immobilization to form a stationary phase applied for hydrophilic interaction liquid chromatography (HILIC). It offers an easy way to manipulate the thickness of PVA coating and the obtained stationary phase demonstrated high efficiency and high chemical stability. PMID:26280030

  6. Compatibility of Polyvinyl Alcohol with the 241-F/H Tank Farm Liquid Waste

    SciTech Connect

    Oji, L.N.

    1998-11-25

    This report describes results from laboratory-scale oxidative mineralization of polyvinyl alcohol (PVA), and the evaluation of the F/H Tank Farms as a storage/disposal option for PVA waste solution generated in the Canyons and B-line decontamination operations.

  7. Oxidative mineralization and characterization of polyvinyl alcohol for compatibility with tank farm processing chemistry

    SciTech Connect

    Oji, L.N.

    2000-01-04

    Polyvinyl alcohol (PVA) material has been evaluated for use as a cost-effective substitute for conventional cellulose-based disposal materials (decontamination mops and wipes), plastic bags, and disposable personal protection clothing, that are currently used at Savannah River Site. This study also provides process design criteria for ultraviolet/ultrasonic/hydrogen peroxide PVA reactor system.

  8. A PVA/PVP hydrogel for human lens substitution: Synthesis, rheological characterization, and in vitro biocompatibility.

    PubMed

    Leone, Gemma; Consumi, Marco; Greco, Giuseppe; Bonechi, Claudia; Lamponi, Stefania; Rossi, Claudio; Magnani, Agnese

    2011-05-01

    To overcome opacification and absence of accommodation of human lens substitutes a new poly(vinyl alcohol) (PVA)/poly(N-vinyl-2- pyrrolidinone) (PVP) based hydrogel (PPS31075) was realised. The Infrared Spectroscopy and the mechanical spectra confirmed the successful occurrence of crosslinking reaction. The rheological analysis pointed out a behavior comparable with that of young human lens in terms of complex shear modulus and accommodation capability. Further analysis in terms of optical properties, water content measurements, diffusion coefficient, cytotoxicity, and human capsular cell adhesion confirmed the applicability of such a hydrogel as potential human lens substitute.

  9. Immobilization of a Plant Lipase from Pachira aquatica in Alginate and Alginate/PVA Beads.

    PubMed

    Bonine, Bárbara M; Polizelli, Patricia Peres; Bonilla-Rodriguez, Gustavo O

    2014-01-01

    This study reports the immobilization of a new lipase isolated from oleaginous seeds of Pachira aquatica, using beads of calcium alginate (Alg) and poly(vinyl alcohol) (PVA). We evaluated the morphology, number of cycles of reuse, optimum temperature, and temperature stability of both immobilization methods compared to the free enzyme. The immobilized enzymes were more stable than the free enzyme, keeping 60% of the original activity after 4 h at 50°C. The immobilized lipase was reused several times, with activity decreasing to approximately 50% after 5 cycles. Both the free and immobilized enzymes were found to be optimally active between 30 and 40°C.

  10. Cylindrical diffractive lenses recorded on PVA/AA photopolymers

    NASA Astrophysics Data System (ADS)

    Fernández, R.; Gallego, S.; Márquez, A.; Navarro-Fuster, V.; Francés, J.; Neipp, C.; Beléndez, A.; Pascual, I.

    2016-04-01

    Photopolymers are optical recording materials appealing for many different applications such as holography, data storage, interconnectors, solar concentrations, or wave-guides fabrication. Recently the capacity of photopolymers to record diffractive optical elements (DOE's) has been investigated. Different authors have reported proposes to record DOE like fork gratings, photonics structures, lenses, sinusoidal, blazed or fork gratings. In these experiments there are different experimental set-ups and different photopolymers. In this work due to the improvement in the spatial light modulation technology together with the photopolymer science we propose a recording experimental system of DOE using a Liquid Cristal based on Silicon (LCoS) display as a master to store complex DOE like cylindrical lenses. This technology permits us an accurate control of the phase and the amplitude of the recording beam, with a very small pixel size. The main advantage of this display is that permit us to modify the DOE automatically, we use the software of the LCoS to send the voltage to each pixel In this work we use a photopolymer composed by acrylamide (AA) as polymerizable monomer and polyvinyl alcohol (PVA). We use a coverplated and index matched photopolymer to avoid the influence of the thickness variation on the transmitted light. In order to reproduce the material behaviour during polymerization, we have designed our model to simulate cylindrical lenses and used Fresnel propagation to simulate the light propagation through the DOE and analyze the focal plane and the properties of the recorded lenses.

  11. HEA-PVA gel system for UVA radiation dose measurement.

    PubMed

    Zhang, Wei; Yang, Liming; Fang, Sijia; Chen, Jie

    2016-10-01

    Acrylic monomer is known to be sensitive to ultraviolet radiation (UVR) through photoinitiator. Upon irradiation, the acrylic monomers formed stable polymer through free radical polymerization, hence its appearance will change from colorless and transparent to colored and non-transparent. Furthermore, the degree of changes was based on the UVR dose, and those optical changes could be detected by UV-vis spectrophotometer at the fixed wavelength of 550nm. In this study, we used 2-hydroxyethyl acrylate (HEA) as acrylic monomer, which mixed with polyvinyl alcohol (PVA), and finally obtained a three-dimensional hydrogel material through cross-linking by glutaraldehyde (GA). After doping with photoinitiator-Bis(2,6-difluoro-3-(1-hydropyrro-1-yl)-phenyl) titanocene (784), the gel material was sensitive to UV-A radiation (400-315nm), which forms an important part (~97%) of the natural solar UV radiation reaching the earth surface. The behavior of different formulations' dose response sensitivity, detector linearity, diffusion, stability after UVA radiation were investigated. The results showed that when the dosage range of UVA radiation was 0-560J/cm(2), the gel had a great sensitivity and the linearity was found to be closed to 1. After UVA radiation, the gel also had a very good optical stability. In addition to this, when irradiated with high dose UVA, the gel could maintain a low diffusion. PMID:27543762

  12. Bioactivity of permselective PVA hydrogels with mixed ECM analogues.

    PubMed

    Nafea, Eman H; Poole-Warren, Laura A; Martens, Penny J

    2015-12-01

    The presentation of multiple biological cues, which simulate the natural in vivo cell environment within artificial implants, has recently been identified as crucial for achieving complex cellular functions. The incorporation of two or more biological cues within a largely synthetic network can provide a simplified model of multifunctional ECM presentation to encapsulated cells. Therefore, the aim of this study was to examine the effects of simultaneously and covalently incorporating two dissimilar biological molecules, heparin and gelatin, within a PVA hydrogel. PVA was functionalized with 7 and 20 methacrylate functional groups per chain (FG/c) to tailor the permselectivity of UV photopolymerized hydrogels. Both heparin and gelatin were covalently incorporated into PVA at an equal ratio resulting in a final PVA:heparin:gelatin composition of 19:0.5:0.5. The combination of both heparin and gelatin within a PVA network has proven to be stable over time without compromising the PVA base characteristics including its permselectivity to different proteins. Most importantly, this combination of ECM analogues supplemented PVA with the dual functionalities of promoting cellular adhesion and sequestering growth factors essential for cellular proliferation. Multi-functional PVA hydrogels with synthetically controlled network characteristics and permselectivity show potential in various biomedical applications including artificial cell implants.

  13. Films prepared from poly(vinyl alcohol) and amylose-fatty acid salt inclusion complexes with increased surface hydrophobicity and high elongation

    Technology Transfer Automated Retrieval System (TEKTRAN)

    In this study, water-soluble amylose-inclusion complexes were prepared from high amylose corn starch and sodium salts of lauric, palmitic, and stearic acid by steam jet cooking. Cast films were prepared by combining the amylose complexes with poly(vinyl alcohol)(PVOH) solution at ratios varying from...

  14. Monitoring of Temperature Fatigue Failure Mechanism for Polyvinyl Alcohol Fiber Concrete Using Acoustic Emission Sensors

    PubMed Central

    Li, Dongsheng; Cao, Hai

    2012-01-01

    The applicability of acoustic emission (AE) techniques to monitor the mechanism of evolution of polyvinyl alcohol (PVA) fiber concrete damage under temperature fatigue loading is investigated. Using the temperature fatigue test, real-time AE monitoring data of PVA fiber concrete is achieved. Based on the AE signal characteristics of the whole test process and comparison of AE signals of PVA fiber concretes with different fiber contents, the damage evolution process of PVA fiber concrete is analyzed. Finally, a qualitative evaluation of the damage degree is obtained using the kurtosis index and b-value of AE characteristic parameters. The results obtained using both methods are discussed. PMID:23012555

  15. Surfactant mediated one- and two-dimensional ZnO nanostructured thin films for dye sensitized solar cell application

    NASA Astrophysics Data System (ADS)

    Marimuthu, T.; Anandhan, N.; Thangamuthu, R.; Mummoorthi, M.; Rajendran, S.; Ravi, G.

    2015-01-01

    One-dimensional (1D) and two-dimensional (2D) nanostructured zinc oxide (ZnO) thin films were electrodeposited from aqueous zinc chloride on FTO glass substrates. The effects of organic surfactant such as cetyltrimethyl ammonium bromide (CTAB) and polyvinyl alcohol (PVA) on structural, morphological, crystal quality and optical properties of electrodeposited ZnO films were investigated. The x-ray diffraction pattern revealed that the prepared thin films were pure wutrzite hexagonal structure. The thin films deposited using organic surfactant in this work showed different morphologies such as nanoplatelet and flower. The hexagonal platelet and flower-like nanostructures were obtained in the presence of CTAB and PVA surfactant, respectively. The crystal quality and atomic vacancies of the prepared nanostructured thin films were investigated by micro Raman spectroscopic technique. The emission properties and optical quality of the films were studied by photoluminescence spectrometry. PEMA-LiClO4-EC gel polymer electrolyte has been used to replace the liquid electrolyte for reducing the leakage problem. Graphene counter electrode was used as an alternative for platinum electrode. Eosin yellow dye was used as a sensitizer. J-V characterizations were carried out for different 1D and 2D nanostructures. The nanoflower structure exhibited higher efficiency (η = 0.073%) than the other two nanostructures.

  16. Functionalized polyvinyl alcohol derivatives thin films for controlled drug release and targeting systems: MAPLE deposition and morphological, chemical and in vitro characterization

    NASA Astrophysics Data System (ADS)

    Cristescu, R.; Popescu, C.; Popescu, A. C.; Grigorescu, S.; Duta, L.; Mihailescu, I. N.; Caraene, G.; Albulescu, R.; Albulescu, L.; Andronie, A.; Stamatin, I.; Ionescu, A.; Mihaiescu, D.; Buruiana, T.; Chrisey, D. B.

    2009-03-01

    We report thin film deposition of polyvinyl alcohol functionalized with carboxylic groups bound to aromatic nucleus (PVACOOH) by matrix-assisted pulsed laser evaporation (MAPLE). We used a KrF* excimer laser source ( λ = 248 nm, τ = 25 ns, ν= 5 Hz ). The obtained thin films have been investigated by FTIR, AFM, and in vitro tests. We identified the best compromise between the parameters of laser processing and characteristics of nanostructured thin films of PVACOOH in terms of porosity and similar composition with those of starting material.

  17. Immobilization of Firefly Luciferase on PVA-co-PE Nanofibers Membrane as Biosensor for Bioluminescent Detection of ATP.

    PubMed

    Wang, Wenwen; Zhao, Qinghua; Luo, Mengying; Li, Mufang; Wang, Dong; Wang, Yuedan; Liu, Qiongzhen

    2015-09-16

    The bioluminescent reaction catalyzed by firefly luciferase has become widely established as an outstanding analytical system for assay of adenosine triphosphate (ATP). When in solution, the luciferase is unstable and cannot be reused. The problem can be partially solved by immobilizing the luciferase on solid substrates. The poly(vinyl alcohol-co-ethylene) (PVA-co-PE) nanofibers membrane has abundant active hydroxyl groups on the surface. The PVA-co-PE nanofibers membrane was first activated by cyanuric chloride with triazinyl group. Then the activated PVA-co-PE nanofibers membrane was subsequently reacted with 1,3-propanediamine and biotin. The firefly luciferase was immobilized onto the surface of 1,3-propanediamine- and biotin-functionalized membranes. The surface chemical structure and morphologies of nanofibers membranes were characterized by FTIR-ATR spectra and SEM. The hydrophilicity of membranes was tested by water contact angle measurements. The detection of fluorescence intensity displayed that the firefly-luciferase-immobilized PVA-co-PE nanofibers membranes indicated high catalytic activity and efficiency. Especially, the firefly-luciferase-immobilized nanofiber membrane which was functionalized by biotin can be a promising candidate as biosensor for bioluminescent detection of ATP because of its high detection sensitivity. PMID:26275118

  18. Immobilization of Firefly Luciferase on PVA-co-PE Nanofibers Membrane as Biosensor for Bioluminescent Detection of ATP.

    PubMed

    Wang, Wenwen; Zhao, Qinghua; Luo, Mengying; Li, Mufang; Wang, Dong; Wang, Yuedan; Liu, Qiongzhen

    2015-09-16

    The bioluminescent reaction catalyzed by firefly luciferase has become widely established as an outstanding analytical system for assay of adenosine triphosphate (ATP). When in solution, the luciferase is unstable and cannot be reused. The problem can be partially solved by immobilizing the luciferase on solid substrates. The poly(vinyl alcohol-co-ethylene) (PVA-co-PE) nanofibers membrane has abundant active hydroxyl groups on the surface. The PVA-co-PE nanofibers membrane was first activated by cyanuric chloride with triazinyl group. Then the activated PVA-co-PE nanofibers membrane was subsequently reacted with 1,3-propanediamine and biotin. The firefly luciferase was immobilized onto the surface of 1,3-propanediamine- and biotin-functionalized membranes. The surface chemical structure and morphologies of nanofibers membranes were characterized by FTIR-ATR spectra and SEM. The hydrophilicity of membranes was tested by water contact angle measurements. The detection of fluorescence intensity displayed that the firefly-luciferase-immobilized PVA-co-PE nanofibers membranes indicated high catalytic activity and efficiency. Especially, the firefly-luciferase-immobilized nanofiber membrane which was functionalized by biotin can be a promising candidate as biosensor for bioluminescent detection of ATP because of its high detection sensitivity.

  19. Development, mechanical evaluation and surface characteristics of chitosan/polyvinyl alcohol based polymer composite coatings on titanium metal.

    PubMed

    Mishra, Sandeep K; Kannan, S

    2014-12-01

    Mechanical properties of orthopedic implants play important role in the regeneration and cell growth of the diseased body part. The present investigation was aimed at the development of a biocompatible, biodegradable and mechanically stable coating of chitosan (CS)-polyvinyl alcohol (PVA) polymer composite on Titanium (Ti) metal by employing a simple methodology at ambient conditions. The PVA to CS concentrations were maintained in fixed ratios of 1:4 weight/weight (w/w) for the development of all the coatings on Ti metal. Four different concentrations of the polymers ranging in the order of 5%, 10%, 15% and 20% weight/volume (w/v) solution of CS were selected in an aim to test their efficacy on mechanical stability. The results obtained from the analysis confirmed considerable improvement in mechanical properties of the composite polymer film comprising CS and PVA on Ti metal with the four different concentrations showing variable elastic modulus and hardness. The difference in mechanical properties of both dehydrated and hydrated coatings demonstrates the effective and efficient shielding of high mechanical properties of Ti metal in physiological conditions. The scratch tests performed on the coated specimens also indicated a good adhesion of the polymer on the Ti metal surface.

  20. Improvement of wound tissue repair by chitosan films containing (-)-borneol, a bicyclic monoterpene alcohol, in rats.

    PubMed

    Barreto, Rosana Ss; Quintans, Jullyana Ss; Barreto, André S; Albuquerque-Júnior, Ricardo Lc; Galvão, Juliana G; Gonsalves, Joice Kmc; Nunes, Rogéria S; Camargo, Enilton A; Lucca-Júnior, Waldecy; Soares, Rosilene C; Feitosa, Vera Lúcia C; Quintans-Júnior, Lucindo J

    2016-10-01

    The aim of this study was to investigate the wound-healing activity of (-)-borneol (BOR) incorporated in chitosan film on healing protocol in rodents. To assess the BOR wound-healing potential, male Wistar rats were subjected to a full-thickness excisional wound. The animals were divided into three groups: dressed with chitosan-based film (QUIN); dressed with chitosan-based film containing 0·5% BOR (QUIBO05); or dressed with chitosan-based film containing 1% BOR (QUIBO1). Dressing the wound areas and histological analysis were performed on the 3rd, 7th, 14th, and 21st days. The myeloperoxidase (MPO) activity was assessed on the third and seventh days after surgical procedures. Wounds dressed with chitosan-based film containing BOR reduced significantly the MPO activity (P < 0·001), showed significantly larger wound retraction rates (7 days, P < 0·05), improved the granulation reaction, and also provided better collagenisation density and arrangement during wound healing. It is suggested that BOR modulates the wound-healing process and is a promising compound to be used in wound care. This product may be quite useful in improving wound healing and could be a new biotechnological product with healing properties and clinical application. Further ongoing studies will enable us to understand the precise mechanisms whereby BOR improves the wound-healing process.

  1. Effects of thermomechanical properties of polarizer components on light leakage in thin-film transistor liquid-crystal displays

    NASA Astrophysics Data System (ADS)

    Lin, Taiy-In; Chen, Alexander; Chen, Shou-I.; Leu, Jihperng

    2015-07-01

    In this paper, we present static thermal analysis of stress and strain on a thin-film transistor liquid-crystal display (TFT-LCD) panel and their correlation with light leakage phenomena under high-temperature durability test. Three-dimensional (3D) finite element analysis (FEA) is coupled with experimental parameters of key components of the TFT-LCD panel for the analysis. A strong correlation exists between light leakage and retardation difference induced by stress on triacetyl cellulose (TAC) films. Moreover, shrinkage in stretched poly(vinyl alcohol) (PVA) film and modulus of the adhesive layer are key factors affecting stress distribution and displacement of polarizer stack. An increase in Young’s modulus (E) of the adhesive layer effectively reduces polarizer shrinkage and light leakage at the center of the panel. A TAC film with lower Young’s modulus and/or coefficient of thermal expansion (CTE) is also an effective solution.

  2. Transport Properties of Anatase-TiO2 Polycrystalline-Thin-Film Field-Effect Transistors with Electrolyte Gate Layers

    NASA Astrophysics Data System (ADS)

    Horita, Ryohei; Ohtani, Kyosuke; Kai, Takahiro; Murao, Yusuke; Nishida, Hiroya; Toya, Taku; Seo, Kentaro; Sakai, Mio; Okuda, Tetsuji

    2013-11-01

    We have fabricated anatase-TiO2 polycrystalline-thin-film field-effect transistors (FETs) with poly(vinyl alcohol) (PVA), ion-liquid (IL), and ion-gel (IG) gate layers, and have tried to improve the response to gate voltage by varying the concentration of mobile ions in these electrolyte gate layers. The increase in the concentration of mobile ions by doping NaOH into the PVA gate layer or reducing the gelator in the IG gate layer markedly increases the drain-source current and reduces the driving gate voltage, which show that the mobile ions in the PVA, IL, and IG gate layers cause the formation of electric double layers (EDLs), which act as nanogap capacitors. In these TiO2-EDL-FETs, the slow formation of EDLs and the oxidation reaction at the interface between the surface of the TiO2 film and the electrolytes cause unideal FET properties. In the optimized IL and IG TiO2-EDL-FETs, the driving gate voltage is less than 1 V and the ON/OFF ratios of the transfer characteristics are about 1×104 at RT, and the nearly metallic state is realized at the interface purely by applying a gate voltage.

  3. Thermal stability of polyvinyl alcohol/nanocrystalline cellulose composites.

    PubMed

    Voronova, Marina I; Surov, Oleg V; Guseinov, Sabir S; Barannikov, Vladimir P; Zakharov, Anatoly G

    2015-10-01

    Thermal stability of polyvinyl alcohol/cellulose nanocrystals (PVA/CNCs) composites prepared with solution casting technique was studied. The PVA/CNCs composites were characterized by Fourier transform infrared spectrometry, X-ray diffraction, differential scanning calorimeter (DSC) and thermogravimetric (TG) analysis. Due to the presence of CNCs nanoparticles, thermal degradation of the composites occurs at much higher temperatures compared to that of the neat PVA. Thermal stability of the PVA/CNCs composites is maximally enhanced with CNCs content of 8-12 wt%. Some thermal degradation products of the PVA/CNCs composites were identified by mass spectrometric analysis. TG measurements with synchronous recording of mass spectra revealed that the thermal degradation of both CNCs and PVA in the composites with CNCs content of 8-12 wt% occurs simultaneously at a much higher temperature than that of CNCs or the neat PVA. However, with increasing CNCs content more than 12 wt% the thermal stability of the composites decreases. In this case, the degradation of CNCs comes first followed by the degradation of PVA.

  4. Accelerated in vitro release testing of implantable PLGA microsphere/PVA hydrogel composite coatings

    PubMed Central

    Shen, Jie; Burgess, Diane J.

    2011-01-01

    Dexamethasone loaded poly(lactic-co-glycolic acid) (PLGA) microsphere/PVA hydrogel composites have been investigated as an outer drug-eluting coating for implantable devices such as glucose sensors to counter negative tissue responses to implants. The objective of this study was to develop a discriminatory, accelerated in vitro release testing method for this drug-eluting coating using United States Pharmacopeia (USP) apparatus 4. Polymer degradation and drug release kinetics were investigated under “real-time” and accelerated conditions (i.e. extreme pH, hydro-alcoholic solutions and elevated temperatures). Compared to “real-time” conditions, the initial burst and lag phases were similar using hydro-alcoholic solutions and extreme pH conditions, while the secondary apparent zero-order release phase was slightly accelerated. Elevated temperatures resulted in a significant acceleration of dexamethasone release. The accelerated release data were able to predict “real-time” release when applying the Arrhenius equation. Microsphere batches with faster and slower release profiles were investigated under “real-time” and elevated temperature (60°C) conditions to determine the discriminatory ability of the method. The results demonstrated both the feasibility and the discriminatory ability of this USP apparatus 4 method for in vitro release testing of drug loaded PLGA microsphere/PVA hydrogel composites. This method may be appropriate for similar drug/device combination products and drug delivery systems. PMID:22016033

  5. In situ synthesis of magnetic CaraPVA IPN nanocomposite hydrogels and controlled drug release.

    PubMed

    Mahdavinia, Gholam Reza; Etemadi, Hossein

    2014-12-01

    In this work, the magnetic nanocomposite hydrogels that focused on targeted drug delivery were synthesized by incorporation of polyvinyl alcohol (PVA), kappa-carrageenan (Cara), and magnetite Fe3O4 nanoparticles. The magnetic nanoparticles were obtained in situ in the presence of a mixture of polyvinyl alcohol/kappa-carrageenan (CaraPVA). The produced magnetite-polymers were cross-linked with freezing-thawing technique and subsequent with K(+) solution. The synthesized hydrogels were thoroughly characterized by transmittance electron microscopy (TEM), scanning electron microscopy (SEM), X-ray diffraction (XRD), thermal gravimetric analysis (TGA), Fourier transform infrared spectroscopy (FT-IR), and vibrating sample magnetometer (VSM) techniques. The dynamic swelling kinetic models of hydrogels were analyzed according to the first- and second-order kinetic models and were found that the experimental kinetics data followed the second-order model well. Drug loading and release efficiency were evaluated by diclofenac sodium (DS) as the model drug. The in vitro drug release studies from hydrogels exhibited significant behaviors on the subject of physiological simulated pHs and external magnetic fields. Investigation on the antibacterial activity revealed the ability of drug-loaded hydrogels to inactivate the Gram-positive Staphylococcus aureus (S. aureus) bacteria. The mucoadhesive properties of the hydrogels were studied and the hydrogels containing kappa-carrageenan showed good mucoadhesiveness in both simulated gastric and intestinal conditions.

  6. Facile synthesis of silver nanoparticles-modified PVA/H4SiW12O40 nanofibers-based electrospinning to enhance photocatalytic activity

    NASA Astrophysics Data System (ADS)

    Sui, Chunhong; Li, Chao; Guo, Xiaohong; Cheng, Tiexin; Gao, Yukun; Zhou, Guangdong; Gong, Jian; Du, Jianshi

    2012-07-01

    Regarding poly(vinyl alcohol)/silicotungstic acid (PVA/H4SiW12O40) gel as precursor, the silver nanoparticles (NPs) were selectively deposited on the surface of the PVA/H4SiW12O40 nanofibers by using electrospinning and photoreduction methods. X-ray photoelectron spectroscopy, Fourier transformation infrared spectroscopy, and UV-vis diffuse reflectance spectroscopy were used to affirm the structure and formation of tri-component nanohybrids. Field environmental scanning electron microscope and transmission electron microscopy indicate that the average diameter of silver NPs was changed from 25 nm to 50 nm, with decreasing the relative concentration of SiW12 in the as-electrospun nanofibers. The nanocomposites exhibit excellent photocatalytic activity in degradation of Rhodamine B. This result arises from the synergistic effects and the large specific surface areas of Ag/PVA/H4SiW12O40 tri-component nanohybrids.

  7. The influence of different plasticizers and polymers on the mechanical and thermal properties, porosity and drug permeability of free shellac films.

    PubMed

    Qussi, Basel; Suess, Wolfgang G

    2006-04-01

    The effect of triethyl citrate (TEC) and different molecular weights and concentrations of polyethylene glycol (PEG), in addition to the effect of different water-soluble polymers and dispersions at different levels, hydroxypropyl methylcellulose (HPMC), methylcellulose (MC), carbomer 940, polyvinyl alcohol (PVA), ethyl cellulose (EC), on the mechanical and thermal properties, drug permeability, and porosity of free shellac films were investigated. Shellac films were cast from aqueous solutions, and their mechanical properties were studied by tensile test. Thermal analyses were performed using differential scanning calorimetry (DSC). The results showed that the addition of plasticizer caused a decrease in both elastic modulus and glass transition temperature (T(g)) and an increase in elongation at break of free shellac films. This effect was related to the concentrations of plasticizers. Different molecular weights of PEGs have different plasticization mechanisms.Moreover, the incorporation of different amounts of HPMC, MC, or carbomer in free shellac films caused an increase in the flexibility, decrease in T(g), and a marked increase in drug permeability of free shellac films, whereas the addition of PVA caused a decrease in flexibility and drug permeability and an increase in T(g). Addition of EC resulted in a slight decrease of the elasticity and a small decrease in drug permeability. However it does not show a considerable effect on the T(g). In addition, it was found that the drug permeability is directly related to the mechanical properties and T(g) of shellac films. PMID:16638678

  8. Synthesis of fast response crosslinked PVA-g-NIPAAm nanohydrogels by very low radiation dose in dilute aqueous solution

    NASA Astrophysics Data System (ADS)

    Fathi, Marziyeh; Reza Farajollahi, Ali; Akbar Entezami, Ali

    2013-05-01

    Nanohydrogels of poly(vinyl alcohol)-g-N-isopropylacrylamide (PVA-g-NIPAAm) are synthesized by PVA and NIPAAm dilute aqueous solution using much less radiation dose of 1-20 Gy via intramolecular crosslinking at ambient temperature. The radiation synthesis of nanohydrogels is performed in the presence of tetrakis (hydroxymethyl) phosphonium chloride (THPC) due to its rapid oxygen scavenging abilities and hydrogen peroxide (H2O2) as a source of hydroxyl radicals. The effect of radiation dose, feed composition ratio of PVA and H2O2 is investigated on swelling properties such as temperature and pH dependence of equilibrium swelling ratio as well as deswelling kinetics. Experimental data exhibit high equilibrium swelling ratio and fast response time for the synthesized nanohydrogels. The average molecular weight between crosslinks (Mc) and crosslinking density (ρx) of the obtained nanohydrogels are calculated from swelling data as a function of radiation dose, H2O2 and PVA amount. Fourier transform infrared spectroscopy (FT-IR), elemental analysis of nitrogen content and thermogravimetric analysis (TGA) are used to confirm the grafting reaction. Lower critical solution temperature (LCST) is measured around 33 °C by differential scanning calorimetry (DSC) for PVA-g-NIPAAm nanohydrogels. Dynamic light scattering (DLS) data demonstrate that the increase of radiation dose leads to the decreasing in dimension of nanohydrogels. Also, rheological studies are confirmed an improvement in the mechanical properties of the nanohydrogels with increasing the radiation dose. A cytotoxicity study exhibits a good biocompatibility for the obtained nanohydrogels. The prepared nanohydrogels show fast swelling/deswelling behavior, high swelling ratio, dual sensitivity and good cytocompatibility, which may find potential applications as biomaterial.

  9. Formulation and Characterization of Acetaminophen Nanoparticles in Orally Disintegrating Films

    NASA Astrophysics Data System (ADS)

    AI-Nemrawi, Nusaiba K.

    in the pharmaceutical industry. These thin films are designed to dissolve within a few seconds without the need for water or chewing. The introduction of fast disintegrating dosage forms has solved some problems encountered in the administration of drugs to pediatric and elderly patients. This convenience provides both marketing advantages and higher patient compliance. Acetaminophen was chosen to be the model drug due to its safety. The amount of acetaminophen in each film is much below the therapeutic dose, but the purpose of using acetaminophen is to be an analytical tracer only. Films were formulated using hydroxypropyl methyl cellulose (HPMC) as film forming polymer, polyethylene glycol 400 (PEG) as a plasticizer and polyvinyl alcohol (PVA) as a NPs stabilizer. First of all, the effect of different Methocel grades and concentration, PEG 400 concentration and PVA 80% concentration on the films were determined. Ingredients that gave best physico-mechanical properties to the films were used in the formulation of ODFs that are loaded with the NPs. Nanoparticles were prepared by the emulsion-solvent evaporation method where acetone phase containing the drug and NPs forming polymers were added to water phase containing other additives. Three types of NPs were prepared: empty, loaded and loaded in ODF dispersion. The size, polydispersity index (PI), zeta potential and drug entrapment efficacy (EE) of NPs were measured. The effect of addition rate, agitation rate, viscosity of the continuous phase, PVA hydrolization, PLGA polymerization and the PLGA to PVA ratio on NPs properties was investigated. The nanoemulsions were cast to form films which were studied in vitro and ex-vivo. Furthermore, the mechanism of drug appearance in the receiver of a Franz cell was explored. Films were placed on a pork buccal membrane using a Franz cell and samples were withdrawn at specific time intervals. Samples were divided into two portions; one of them was extracted while the other was

  10. High-performance n-channel organic thin-film transistor based on naphthalene diimide.

    PubMed

    Dey, Anamika; Kalita, Anamika; Krishnan Iyer, Parameswar

    2014-08-13

    A conjugated molecule comprising 1,4,5,8-naphthalene diimide (NDI) substituted with two octadecylamine (OD) chains has been synthesized (NDI-OD2) in a single step from commercial materials, and its organic thin-film transistor (OTFT) devices on glass substrate have been studied using poly(vinyl alcohol) (PVA) gate dielectric material. Although we utilized the PVA dielectric without any intermediate buffer layer or PVA cross-linkers, excellent electron mobility as high as ∼1.0 cm(2)V(-1) s(-1) are obtained. This NDI-OD2 molecule exhibits comparable optical (Eg(UV) ∼3.1 eV) and electrochemical band gaps (Eg(CV) ∼3.02 eV) with a lowest unoccupied molecular orbital (LUMO) energy levels of ∼3.3 eV. When processed by solution method, this material forms rod-shaped crystalline microstructures, whereas, when thermally deposited, it assumes the formation of smooth 2D films. The chemical as well as physical properties and theoretical calculations of NDI-OD2 have been studied and the effect of the C-18 alkyl chain unit has been discussed. The OTFT consisting of NDI-OD2 exhibits excellent performance parameters such as high electron mobility (μe) and Ion-to-Ioff ratio. After demonstrating the high performance of NDI-OD2-based TFT devices fabricated with biocompatible PVA dielectric, we have also demonstrated that these devices can be degraded because of the presence of this PVA dielectric when exposed to a high-moisture environment. The systematic degradation of the device activity in a controlled way within 10 days of exposure (>80% moisture) is also presented here. In this study, a conceptually important feature and futuristic aspect that the n-channel TFT devices can also be biodegraded irreversibly is demonstrated. This concept of developing a low cost and biodegradable OTFT device with biocompatible PVA dielectric with excellent electron mobility is expected to have diverse applications in disposable electronic tags, biomedical devices, and food industry packing

  11. Controllable promotion of chondrocyte adhesion and growth on PVA hydrogels by controlled release of TGF-β1 from porous PLGA microspheres.

    PubMed

    Nie, Lei; Zhang, Guohua; Hou, Ruixia; Xu, Haiping; Li, Yaping; Fu, Jun

    2015-01-01

    Poly(vinyl alcohol) (PVA) hydrogels have been candidate materials for cartilage tissue engineering. However, the cell non-adhesive nature of PVA hydrogels has been a limit. In this paper, the cell adhesion and growth on PVA hydrogels were promoted by compositing with transform growth factor-β1 (TGF-β1) loaded porous poly(D,L-lactide-co-glycolide) (PLGA) microspheres. The porous microspheres were fabricated by a modified double emulsion method with bovine serum albumin (BSA) as porogen. The average pore size of microspheres was manipulated by changing the BSA/PLGA ratio. Such controllable porous structures effectively influenced the encapsulation efficiency (Eencaps) and release profile of TGF-β1. By compositing PVA hydrogels with such TGF-β1-loaded PLGA microspheres, chondrocyte adhesion and proliferation were significantly promoted in a controllable manner, as confirmed by fluorescent imaging and quantitative CCK-8 assay. That is, the chondrocyte proliferation was favored by using PLGA microspheres with high Eencaps of TGF-β1 or by increasing the PLGA microsphere content in the hydrogels. These results demonstrated a facile method to improve the cell adhesion and growth on the intrinsically cell non-adhesive PVA hydrogels, which may find applications in cartilage substitution.

  12. X-ray diffraction study of the molecular propolis films deposited from an alcohol solution onto the cleavage surfaces of layered V2VI3 compounds

    NASA Astrophysics Data System (ADS)

    Drapak, S. I.; Gavrylyuk, S. V.; Kaminskii, V. M.; Kovalyuk, Z. D.

    2008-09-01

    The structures of the molecular propolis films deposited from an alcohol solution on the (0001) cleavage surface of layered bismuth selenide and telluride are studied by X-ray diffraction. Despite the chemical interaction between the semiconductor substrates and the organic-substance components, the molecular structural ordering of the propolis films is shown to be identical to that in the films of this substance on the surface of amorphous glass substrates. The chemical and deformation interaction between the organic substance and the layered V2VI3 compounds is found to result in the formation of an organic-inorganic sandwich nanostructure at a distance of ˜0.3 μm from the layered crystal-propolis film interface.

  13. Characteristic time scales of coalescence of silver nanocomposite and nanoparticle films induced by continuous wave laser irradiation

    SciTech Connect

    Paeng, Dongwoo; Grigoropoulos, Costas P.; Lee, Daeho

    2014-08-18

    In-situ optical probing has been performed to analyze and compare the characteristic coalescence time scales of silver ion-doped polyvinylalcohol nanocomposite (Ag-PVA NC) and polyvinylpyrrolidone-capped silver nanoparticle (Ag-PVP NP) films subjected to continuous wave laser irradiation. The Ag-PVA NC yielded conductive metallic patterns by photothermal reduction of PVA, formation of nanoparticles from silver ions and their subsequent coalescence. On the other hand, Ag-PVP NP thin films produced conductive patterns through only coalescence of nanoparticles. Upon laser irradiation, Ag-PVA NC and Ag-PVP NP films exhibited different coalescence characteristics.

  14. Fabrication of Li2TiO3 pebbles using PVA-boric acid reaction for solid breeding materials

    NASA Astrophysics Data System (ADS)

    Park, Yi-Hyun; Cho, Seungyon; Ahn, Mu-Young

    2014-12-01

    Lithium metatitanate (Li2TiO3) is a candidate breeding material of the Helium Cooled Ceramic Reflector (HCCR) Test Blanket Module (TBM). The breeding material is used in pebble-bed form to reduce the uncertainty of the interface thermal conductance. In this study, Li2TiO3 pebbles were successfully fabricated by the slurry droplet wetting method using the cross-linking reaction between polyvinyl alcohol (PVA) and boric acid. The effects of fabrication parameters on the shaping of Li2TiO3 green body were investigated. In addition, the basic characteristics of the sintered pebble were also evaluated. The shape of Li2TiO3 green bodies was affected by slurry viscosity, PVA content and boric acid content. The grain size and average crush load of sintered Li2TiO3 pebble were controlled by the sintering time. The boron was completely removed during the final sintering process.

  15. Development of ethyl alcohol-precipitated silk sericin/polyvinyl alcohol scaffolds for accelerated healing of full-thickness wounds.

    PubMed

    Siritienthong, Tippawan; Ratanavaraporn, Juthamas; Aramwit, Pornanong

    2012-12-15

    Silk sericin has been recently reported for its advantageous biological properties to promote wound healing. In this study, we established that the ethyl alcohol (EtOH) could be used to precipitate sericin and form the stable sericin/polyvinyl alcohol (PVA) scaffolds without the crosslinking. The sericin/PVA scaffolds were fabricated via freeze-drying and subsequently precipitating in various concentrations of EtOH. The EtOH-precipitated sericin/PVA scaffolds showed denser structure, higher compressive modulus, but lower water swelling ability than the non-precipitated scaffolds. Sericin could be released from the EtOH-precipitated sericin/PVA scaffolds in a sustained manner. After cultured with L929 mouse fibroblasts, the 70 vol% EtOH-precipitated sericin/PVA scaffolds showed the highest potential to promote cell proliferation. After applied to the full-thickness wounds of rats, the 70 vol% EtOH-precipitated sericin/PVA scaffolds showed significantly higher percentage of wound size reduction and higher extent of type III collagen formation and epithelialization, compared with the control scaffolds without sericin. The accelerated wound healing by the 70 vol% EtOH-precipitated sericin/PVA scaffolds was possibly due to (1) the bioactivity of sericin itself to promote wound healing, (2) the sustained release of precipitated sericin from the scaffolds, and (3) the activation and recruitment of wound healing-macrophages by sericin to the wounds. This finding suggested that the EtOH-precipitated sericin/PVA scaffolds were more effective for the wound healing, comparing with the EtOH-precipitated PVA scaffolds without sericin.

  16. Optical, electrical, thermal properties of cadmium chloride doped PVA - PVP blend

    NASA Astrophysics Data System (ADS)

    Baraker, Basavarajeshwari M.; Hammannavar, Preeti B.; Lobo, Blaise

    2015-06-01

    Films of polyvinylalcohol (PVA) - polyvinylpyrrolidone (PVP) blend doped with Cadmium Chloride (CdCl2) in the doping range 1 wt% to 40 wt% were prepared by solution casting technique. These films were characterized using optical/UV-Vis- NIR spectroscopy, Differential Scanning Calorimetry (DSC) and DC electrical measurements. The UV-Visible spectra were quantitatively analyzed to yield the optical parameters. The UV-Visible Spectra show intermediate absorption bands (before the final absorption edge) due to formation of energy bands in the forbidden gap of PVA-PVP. There is a prominent absorption band at 2.9 eV, from 0.5 wt% up to 1.8 wt% doping level (DL) caused by the dopant (CdCl2). The DC electrical studies showed an increase in activation energy from 2.8 eV at 0.5 wt% DL up to 3.5 eV at 4.4 wt% DL, reaching a low of 2.4 eV at 11.2 wt% DL. DSC scans show evidence of formation of chain fragments, at doping levels beyond 8 wt%.

  17. Optical, electrical, thermal properties of cadmium chloride doped PVA – PVP blend

    SciTech Connect

    Baraker, Basavarajeshwari M.; Hammannavar, Preeti B.; Lobo, Blaise

    2015-06-24

    Films of polyvinylalcohol (PVA) – polyvinylpyrrolidone (PVP) blend doped with Cadmium Chloride (CdCl{sub 2}) in the doping range 1 wt% to 40 wt% were prepared by solution casting technique. These films were characterized using optical/UV-Vis- NIR spectroscopy, Differential Scanning Calorimetry (DSC) and DC electrical measurements. The UV-Visible spectra were quantitatively analyzed to yield the optical parameters. The UV-Visible Spectra show intermediate absorption bands (before the final absorption edge) due to formation of energy bands in the forbidden gap of PVA-PVP. There is a prominent absorption band at 2.9 eV, from 0.5 wt% up to 1.8 wt% doping level (DL) caused by the dopant (CdCl{sub 2}). The DC electrical studies showed an increase in activation energy from 2.8 eV at 0.5 wt% DL up to 3.5 eV at 4.4 wt% DL, reaching a low of 2.4 eV at 11.2 wt% DL. DSC scans show evidence of formation of chain fragments, at doping levels beyond 8 wt%.

  18. Isothermal Dendritic Growth Experiment - PVA Dendrites

    NASA Technical Reports Server (NTRS)

    1997-01-01

    The Isothermal Dendritic Growth Experiment (IDGE), flown on three Space Shuttle missions, is yielding new insights into virtually all industrially relevant metal and alloy forming operations. IDGE used transparent organic liquids that form dendrites (treelike structures) similar to those inside metal alloys. Comparing Earth-based and space-based dendrite growth velocity, tip size and shape provides a better understanding of the fundamentals of dentritic growth, including gravity's effects. Shalowgraphic images of pivalic acid (PVA) dendrites forming from the melt show the subtle but distinct effects of gravity-driven heat convection on dentritic growth. In orbit, the dendrite grows as its latent heat is liberated by heat conduction. This yields a blunt dendrite tip. On Earth, heat is carried away by both conduction and gravity-driven convection. This yields a sharper dendrite tip. In addition, under terrestrial conditions, the sidebranches growing in the direction of gravity are augmented as gravity helps carry heat out of the way of the growing sidebranches as opposed to microgravity conditions where no augmentation takes place. IDGE was developed by Rensselaer Polytechnic Institute and NASA/Glenn Research Center. Advanced follow-on experiments are being developed for flight on the International Space Station. Photo Credit: NASA/Glenn Research Center

  19. Properties and Applications of Polyvinyl Alcohol, Halloysite Nanotubes and Their Nanocomposites.

    PubMed

    Gaaz, Tayser Sumer; Sulong, Abu Bakar; Akhtar, Majid Niaz; Kadhum, Abdul Amir H; Mohamad, Abu Bakar; Al-Amiery, Ahmed A

    2015-01-01

    The aim of this review was to analyze/investigate the synthesis, properties, and applications of polyvinyl alcohol-halloysite nanotubes (PVA-HNT), and their nanocomposites. Different polymers with versatile properties are attractive because of their introduction and potential uses in many fields. Synthetic polymers, such as PVA, natural polymers like alginate, starch, chitosan, or any material with these components have prominent status as important and degradable materials with biocompatibility properties. These materials have been developed in the 1980s and are remarkable because of their recyclability and consideration of the natural continuation of their physical and chemical properties. The fabrication of PVA-HNT nanocomposites can be a potential way to address some of PVA's limitations. Such nanocomposites have excellent mechanical properties and thermal stability. PVA-HNT nanocomposites have been reported earlier, but without proper HNT individualization and PVA modifications. The properties of PVA-HNT for medicinal and biomedical use are attracting an increasing amount of attention for medical applications, such as wound dressings, drug delivery, targeted-tissue transportation systems, and soft biomaterial implants. The demand for alternative polymeric medical devices has also increased substantially around the world. This paper reviews individualized HNT addition along with crosslinking of PVA for various biomedical applications that have been previously reported in literature, thereby showing the attainability, modification of characteristics, and goals underlying the blending process with PVA. PMID:26703542

  20. A visco-hyperelastic constitutive approach for modeling polyvinyl alcohol sponge.

    PubMed

    Karimi, Alireza; Navidbakhsh, Mahdi; Beigzadeh, Borhan

    2014-02-01

    This study proposes the quasi-linear viscoelastic (QLV) model to characterize the time dependent mechanical behavior of poly(vinyl alcohol) (PVA) sponges. The PVA sponges have implications in many viscoelastic soft tissues, including cartilage, liver, and kidney as an implant. However, a critical barrier to the use of the PVA sponge as tissue replacement material is a lack of sufficient study on its viscoelastic mechanical properties. In this study, the nonlinear mechanical behavior of a fabricated PVA sponge is investigated experimentally and computationally using relaxation and stress failure tests as well as finite element (FE) modeling. Hyperelastic strain energy density functions, such as Yeoh and Neo-Hookean, are used to capture the mechanical behavior of PVA sponge at ramp part, and viscoelastic model is used to describe the viscose behavior at hold part. Hyperelastic material constants are obtained and their general prediction ability is verified using FE simulations of PVA tensile experiments. The results of relaxation and stress failure tests revealed that Yeoh material model can define the mechanical behavior of PVA sponge properly compared with Neo-Hookean one. FE modeling results are also affirmed the appropriateness of Yeoh model to characterize the mechanical behavior of PVA sponge. Thus, the Yeoh model can be used in future biomechanical simulations of the spongy biomaterials. These results can be utilized to understand the viscoelastic behavior of PVA sponges and has implications for tissue engineering as scaffold.

  1. Properties and Applications of Polyvinyl Alcohol, Halloysite Nanotubes and Their Nanocomposites.

    PubMed

    Gaaz, Tayser Sumer; Sulong, Abu Bakar; Akhtar, Majid Niaz; Kadhum, Abdul Amir H; Mohamad, Abu Bakar; Al-Amiery, Ahmed A

    2015-12-19

    The aim of this review was to analyze/investigate the synthesis, properties, and applications of polyvinyl alcohol-halloysite nanotubes (PVA-HNT), and their nanocomposites. Different polymers with versatile properties are attractive because of their introduction and potential uses in many fields. Synthetic polymers, such as PVA, natural polymers like alginate, starch, chitosan, or any material with these components have prominent status as important and degradable materials with biocompatibility properties. These materials have been developed in the 1980s and are remarkable because of their recyclability and consideration of the natural continuation of their physical and chemical properties. The fabrication of PVA-HNT nanocomposites can be a potential way to address some of PVA's limitations. Such nanocomposites have excellent mechanical properties and thermal stability. PVA-HNT nanocomposites have been reported earlier, but without proper HNT individualization and PVA modifications. The properties of PVA-HNT for medicinal and biomedical use are attracting an increasing amount of attention for medical applications, such as wound dressings, drug delivery, targeted-tissue transportation systems, and soft biomaterial implants. The demand for alternative polymeric medical devices has also increased substantially around the world. This paper reviews individualized HNT addition along with crosslinking of PVA for various biomedical applications that have been previously reported in literature, thereby showing the attainability, modification of characteristics, and goals underlying the blending process with PVA.

  2. Poly(vinyl alcohol)-heparin biosynthetic microspheres produced by microfluidics and ultraviolet photopolymerisation.

    PubMed

    Young, Cara; Rozario, Kester; Serra, Christophe; Poole-Warren, Laura; Martens, Penny

    2013-01-01

    Biosynthetic microspheres have the potential to address some of the limitations in cell microencapsulation; however, the generation of biosynthetic hydrogel microspheres has not been investigated or applied to cell encapsulation. Droplet microfluidics has the potential to produce more uniform microspheres under conditions compatible with cell encapsulation. Therefore, the aim of this study was to understand the effect of process parameters on biosynthetic microsphere formation, size, and morphology with a co-flow microfluidic method. Poly(vinyl alcohol) (PVA), a synthetic hydrogel and heparin, a glycosaminoglycan were chosen as the hydrogels for this study. A capillary-based microfluidic droplet generation device was used, and by varying the flow rates of both the polymer and oil phases, the viscosity of the continuous oil phase, and the interfacial surface tension, monodisperse spheres were produced from ∼200 to 800 μm. The size and morphology were unaffected by the addition of heparin. The modulus of spheres was 397 and 335 kPa for PVA and PVA/heparin, respectively, and this was not different from the bulk gel modulus (312 and 365 for PVA and PVA/heparin, respectively). Mammalian cells encapsulated in the spheres had over 90% viability after 24 h in both PVA and PVA/heparin microspheres. After 28 days, viability was still over 90% for PVA-heparin spheres and was significantly higher than in PVA only spheres. The use of biosynthetic hydrogels with microfluidic and UV polymerisation methods offers an improved approach to long-term cell encapsulation.

  3. Extraordinarily large swelling energy of iodine-treated poly(vinyl alcohol) demonstrated by jump of a film

    PubMed Central

    Takamura, Tatsuro; Nozawa, Kazuya; Sugimoto, Yoshiki; Shioya, Masatoshi

    2014-01-01

    Organic material characteristics of volume change and stress generation have attracted the attention of many researchers aiming to develop chemomechanical systems such as artificial muscles and polymer engines having the advantages of high energy density and silent operation. Although polymer gels offer a relatively large actuator stroke, their mechanical properties are relatively poor and the working temperature is relatively low, often limited by the evaporation of liquid if contained. We have developed an iodine-treated poly(vinyl alcohol) having extraordinarily large vapor-induced deswelling stress reaching 59 MPa, which is one to two orders of magnitude greater than those of ordinary polymer gels. Furthermore, this material has extremely large volumetric and gravimetric energy densities reaching 1.3 × 106 J m−3 and 9.6 × 102 J kg−1, respectively, and an elastic modulus of a few GPa and is heat-resistant to at least 200 °C. The high performance of this material can be demonstrated by a jump of a film. © 2014 The Authors. Journal of Polymer Science Part B: Polymer Physics published by Wiley Periodicals, Inc. J. Polym. Sci., Part B: Polym. Phys. 2014, 52, 1357–1365 PMID:25678738

  4. Patterned surfaces in the drying of films composed of water, polymer, and alcohol.

    PubMed

    Fichot, Julie; Heyd, Rodolphe; Josserand, Christophe; Chourpa, Igor; Gombart, Emilie; Tranchant, Jean-Francois; Saboungi, Marie-Louise

    2012-12-01

    A study of the complex drying dynamics of polymeric mixtures with optical microscopy and gravimetric measurement is presented. Droplet formation is observed, followed by a collapse that leads to the residual craters in the dried film. The process is followed in situ under well-defined temperature and hygrometric conditions to determine the origin and nature of these droplets and craters. The drying process is usually completed within 1 h. The observations are explained using a simple diffusion model based on experimental results collected from mass and optical measurements as well as Raman confocal microspectrometry. Although the specific polymeric mixtures used here are of interest to the cosmetic industry, the general conclusions reached can apply to other polymeric aqueous solutions with applications to commercial and artistic painting. PMID:23367958

  5. Patterned surfaces in the drying of films composed of water, polymer, and alcohol.

    PubMed

    Fichot, Julie; Heyd, Rodolphe; Josserand, Christophe; Chourpa, Igor; Gombart, Emilie; Tranchant, Jean-Francois; Saboungi, Marie-Louise

    2012-12-01

    A study of the complex drying dynamics of polymeric mixtures with optical microscopy and gravimetric measurement is presented. Droplet formation is observed, followed by a collapse that leads to the residual craters in the dried film. The process is followed in situ under well-defined temperature and hygrometric conditions to determine the origin and nature of these droplets and craters. The drying process is usually completed within 1 h. The observations are explained using a simple diffusion model based on experimental results collected from mass and optical measurements as well as Raman confocal microspectrometry. Although the specific polymeric mixtures used here are of interest to the cosmetic industry, the general conclusions reached can apply to other polymeric aqueous solutions with applications to commercial and artistic painting.

  6. Synthesis, micellization behavior and alcohol induced amphipathic cellulose film of cellulose-based amphiphilic surfactant

    NASA Astrophysics Data System (ADS)

    Yang, Fang; Liu, Ya-nan; Yu, Jian-ling; Li, Hai-peng; Li, Gang

    2015-08-01

    This paper presented a novel preparation method of the cellulose-based amphiphilic surfactant, and the surfactant was used to prepare amphipathic cellulose membrane. The native cotton cellulose was tailored to cellulose segments in ionic liquid 1-butyl-3-methylimidazolium chloride. Then, the hydrophobic and hydrophilic modification of cellulose segments were carried out by esterification and graft polymerization of the ɛ-caprolactone (ɛ-CL) monomer onto the hydroxyl group of cellulose as well as sulphonation with sulfamic acid. The amphipathic cellulose membrane was made by cellulose-based amphiphilic surfactant cross-linking with glutaraldehyde. The molecular structure of amphipathic cellulose surfactant was confirmed by FT-IR, and its surface active properties were investigated by Wilhelmy plate method and Steady-state fluorescence probe method, respectively. Experimental results showed that cellulose-based amphiphilic surfactant caused low interfacial tension of 48.62 mN/m and its critical micelle concentration (cmc) value was 0.65 wt% when the grafting ratio of cellulose-g-PCL (poly-caprolactone) was 25.40%. The contact angle between a droplet of water and the surface of membrane was 90.84o, and the surface free energy of the alcohol induced cellulose membrane was 15.7 mJ/m2. This study may help increase using natural and biodegradable surface-activity materials with improved properties as surfactants.

  7. Synthesis, micellization behavior and alcohol induced amphipathic cellulose film of cellulose-based amphiphilic surfactant

    NASA Astrophysics Data System (ADS)

    Yang, Fang; Liu, Ya-nan; Yu, Jian-ling; Li, Hai-peng; Li, Gang

    2015-08-01

    This paper presented a novel preparation method of the cellulose-based amphiphilic surfactant, and the surfactant was used to prepare amphipathic cellulose membrane. The native cotton cellulose was tailored to cellulose segments in ionic liquid 1-butyl-3-methylimidazolium chloride. Then, the hydrophobic and hydrophilic modification of cellulose segments were carried out by esterification and graft polymerization of the ɛ-caprolactone (ɛ-CL) monomer onto the hydroxyl group of cellulose as well as sulphonation with sulfamic acid. The amphipathic cellulose membrane was made by cellulose-based amphiphilic surfactant cross-linking with glutaraldehyde. The molecular structure of amphipathic cellulose surfactant was confirmed by FT-IR, and its surface active properties were investigated by Wilhelmy plate method and Steady-state fluorescence probe method, respectively. Experimental results showed that cellulose-based amphiphilic surfactant caused low interfacial tension of 48.62 mN/m and its critical micelle concentration (cmc) value was 0.65 wt% when the grafting ratio of cellulose-g-PCL (poly-caprolactone) was 25.40%. The contact angle between a droplet of water and the surface of membrane was 90.84o, and the surface free energy of the alcohol induced cellulose membrane was 15.7 mJ/m2. This study may help increase using natural and biodegradable surface-activity materials with improved properties as surfactants.

  8. Electrospun chitosan/polyvinyl alcohol nanofibre mats for wound healing.

    PubMed

    Charernsriwilaiwat, Natthan; Rojanarata, Theerasak; Ngawhirunpat, Tanasait; Opanasopit, Praneet

    2014-04-01

    Chitosan (CS) aqueous salt blended with polyvinyl alcohol (PVA) nanofibre mats was prepared by electrospinning. CS was dissolved with hydroxybenzotriazole (HOBt), thiamine pyrophosphate (TPP) and ethylenediaminetetraacetic acid (EDTA) in distilled water without the use of toxic or hazardous solvents. The CS aqueous salts were blended with PVA at different weight ratios, and the effect of the solution ratios was investigated. The morphologies and mechanical and swelling properties of the generated fibres were analysed. Indirect cytotoxicity studies indicated that the CS/PVA nanofibre mats were non-toxic to normal human fibroblast cells. The CS-HOBt/PVA and CS-EDTA/PVA nanofibre mats demonstrated satisfactory antibacterial activity against both gram-positive and gram-negative bacteria, and an in vivo wound healing test showed that the CS-EDTA/PVA nanofibre mats performed better than gauze in decreasing acute wound size during the first week after tissue damage. In conclusion, the biodegradable, biocompatible and antibacterial CS-EDTA/PVA nanofibre mats have potential for use as wound dressing materials.

  9. Tuning the luminescence and optical properties of graphene oxide and reduced graphene oxide functionnalized with PVA

    NASA Astrophysics Data System (ADS)

    Goumri, Meryem; Venturini, Jany Wéry; Bakour, Anass; Khenfouch, Mohammed; Baitoul, Mimouna

    2016-03-01

    The attractive optoelectronic properties of graphene are universally known. Also, their combination with polymer matrix added an exciting physical investigation. In the present work, nanocomposites based on poly (vinyl alcohol) (PVA) with low graphene oxide (GO) and partially reduced graphene oxide (PRGO) loadings (0.5, 1 and 2 wt%) were successfully prepared by a simple and environmentally friendly process using aqueous solution in both acidic (pH 4) and neutral media (pH 7)and optimized sonication time, in order to tailor the optical/electronic properties of the GO/PRGO nanosheets. FT-IR and Raman scattering spectroscopy reveal a strong interfacial interaction by hydrogen bonding between the two components. Steady-state photoluminescence results showed a pH-dependent fluorescence of these nanocomposites, and a significant luminescence over a wide range of the visible wavelengths was achieved at a concentration of 1 wt% GO and PRGO loading. A quenching of the PL started at 2 wt% suggesting the possibility of tuning the luminescence properties of GO/PRGO-based composites with PVA.

  10. Preparation of silver-hydroyapatite/PVA nanocomposites: Giant dielectric material for industrial and clinical applications

    NASA Astrophysics Data System (ADS)

    Uddin, Md Jamal; Middya, T. R.; Chaudhuri, B. K.

    2015-02-01

    Pure hydroxyappatite Ca10(PO4)6(OH)2 (or HAP) was prepared from eggshell and potassium dihydrogen phosphate (KH2PO4) by a simple self-chemical reaction method. The clean eggshell was heated at 800 °C in air giving the source of CaO. Appropriate amount of CaO was dissolved in KH2PO4 solution at 37°C for few days. The PH value decreases with increasing the duration of preparation of HAP. Silver nanoparticles derived from silver nitrate solution using black tea leaf extract had been introduced to hydroxyapatite due to its biocompatibility. The unique size- dependent properties of nanomaterials make them superior and indispensable. In this work, hydroxyapatite-silver nanoparticles/polyvinyl alcohol (PVA) composites with 4 different concentrations of hydroxyapatite (1-4 wt %) were prepared by bio-reduction method. Several techniques like XRD and SEM were used to characterize the prepared samples. Frequency dependent capacitance and conductance of the samples were measured using an impedance analyzer. The results showed a remarkable increase in dielectric permittivity (~5117) with low loss (~0.23) at1000 HZ and room temperature (300K) for 4wt% Hydroxapatie-Silver/PVA nanocomposite. Such nanocomposite might be directly applied in manufacturing clinical devices and also for embedding capacitor applications.

  11. Electrospinning of PVA/chitosan nanocomposite nanofibers containing gelatin nanoparticles as a dual drug delivery system.

    PubMed

    Fathollahipour, Shahrzad; Abouei Mehrizi, Ali; Ghaee, Azadeh; Koosha, Mojtaba

    2015-12-01

    Nanofibrous core-sheath nanocomposite dual drug delivery system based on poly(vinyl alcohol) (PVA)/chitosan/lidocaine hydrochloride loaded with gelatin nanoparticles were successfully prepared by the electrospinning method. Gelatin nanoparticles were prepared by nanoprecipitation and were then loaded with erythromycin antibiotic agent with the average particle size of ∼175 nm. The morphology of gelatin nanoparticles observed by field emission scanning electron microscopy (FE-SEM) was shown to be optimal at the concentration of 1.25 wt % of gelatin in aqueous phase by addition of 20 µL of glutaraldehyde 5% as the crosslinking agent. The nanoparticles were also characterized by dynamic light scattering, zeta potential measurement, and Fourier transform infrared spectroscopy (FTIR). The best bead free morphology for the PVA/chitosan nanofibrous mats were obtained at the solution weight ratio of 96/4. The nanofibrous mats were analyzed by swelling studies, FTIR and antibacterial tests. In vitro dual release profile of the core-sheath nanofibers was also studied within 72 h and showed the release efficiency equal to 84.69 and 75.13% for lidocaine hydrochloride and erythromycin, respectively. According to release exponent n, the release of lidocaine hydrochloride from the sheath part of the matrix is quasi-Fickian diffusion mechanism, while the release of erythromycin is based on anomalous or non-Fickian mechanisms.

  12. Swelling, mechanical and friction properties of PVA/PVP hydrogels after swelling in osmotic pressure solution.

    PubMed

    Shi, Yan; Xiong, Dangsheng; Liu, Yuntong; Wang, Nan; Zhao, Xiaoduo

    2016-08-01

    The potential of polyvinyl alcohol/polyvinylpyrrolidone (PVA/PVP) hydrogels as articular cartilage replacements was in vitro evaluated by using a macromolecule-based solution to mimic the osmotic environment of cartilage tissue. The effects of osmotic pressure solution on the morphology, crystallinity, swelling, mechanical and friction properties of PVA/PVP hydrogels were investigated by swelling them in non-osmotic and osmotic pressure solutions. The results demonstrated that swelling ratio and equilibrium water content were greatly reduced by swelling in osmotic solution, and the swelling process was found to present pseudo-Fickian diffusion character. The crystallization degree of hydrogels after swelling in osmotic solution increased more significantly when it compared with that in non-osmotic solution. After swelling in osmotic solution for 28days, the compressive tangent modulus and storage modulus of hydrogels were significantly increased, and the low friction coefficient was reduced. However, after swelling in the non-osmotic solution, the compressive tangent modulus and friction coefficient of hydrogels were comparable with those of as-prepared hydrogels. The better material properties of hydrogels in vivo than in vitro evaluation demonstrated their potential application in cartilage replacement.

  13. Preparation and rheological studies of uncoated and PVA-coated magnetite nanofluid

    NASA Astrophysics Data System (ADS)

    Khosroshahi, M. E.; Ghazanfari, L.

    2012-12-01

    Experimental studies of rheological behavior of uncoated magnetite nanoparticles (MNPs)U and polyvinyl alcohol (PVA) coated magnetite nanoparticles (MNPs)C were performed. A Co-precipitation technique under N2 gas was used to prevent undesirable critical oxidation of Fe2+. The results showed that smaller particles can be synthesized in both cases by decreasing the NaOH concentration which in our case this corresponded to 35 nm and 7 nm using 0.9 M NaOH at 750 rpm for (MNPs)U and (MNPs)C. The stable magnetic fluid contained well-dispersed Fe3O4/PVA nanocomposites which indicated fast magnetic response. The rheological measurement of magnetic fluid indicated an apparent viscosity range (0.1-1.2) pa s at constant shear rate of 20 s-1 with a minimum value in the case of (MNPs)U at 0 T and a maximum value for (MNPs)C at 0.5 T. Also, as the shear rate increased from 20 s-1 to 150 s-1 at constant magnetic field, the apparent viscosity also decreased correspondingly. The water-based ferrofluid exhibited the non-Newtonian behavior of shear thinning under magnetic field.

  14. Development of composite membranes of PVA-TEOS doped KOH for alkaline membrane fuel cell

    NASA Astrophysics Data System (ADS)

    Haryadi, Sugianto, D.; Ristopan, E.

    2015-12-01

    Anion exchange membranes (AEMs) play an important role in separating fuel and oxygen (or air) in the Alkaline Membrane Fuel Cells. Preparation of hybrid organic inorganic materials of Polyvinylalcohol (PVA) - Tetraethylorthosilicate (TEOS) composite membrane doped KOH for direct alcohol alkaline fuel cell application has been investigated. The sol-gel method has been used to prepare the composite membrane of PVA-TEOS through crosslinking step and catalyzed by concentrated of hydrochloric acid. The gel solution was cast on the membrane plastic plate to obtain membrane sheets. The dry membranes were then doped by immersing in various concentrations of KOH solutions for about 4 hours. Investigations of the cross-linking process and the presence of hydroxyl group were conducted by FTIR as shown for frequency at about 1600 cm-1 and 3300 cm-1 respectively. The degree of swelling in ethanol decreased as the KOH concentration for membrane soaking process increased. The ion exchange capacity (IEC) of the membrane was 0.25meq/g. This composite membranes display significant ionic conductivity of 3.23 x 10-2 S/cm in deionized water at room temperature. In addition, the morphology observation by scanning electron microscope (SEM) of the membrane indicates that soaking process of membrane in KOH increased thermal resistant.

  15. Investigations on Pva:. NH4F: ZrO2 Composite Polymer Electrolytes

    NASA Astrophysics Data System (ADS)

    Radha, K. P.; Selvasekarapandian, S.; Karthikeyan, S.; Sanjeeviraja, C.

    2013-07-01

    Composite polymer electrolytes have been prepared using Poly (vinyl alcohol), ammonium fluoride, nanofiller ZrO2 by solution casting technique. The amorphous nature of the composite polymer electrolyte has been confirmed by XRD analysis. FTIR analysis confirms the complex formation among the polymer, salt and nanofiller. The maximum ionic conductivity for 85 PVA:15 NH4F has been found to be 6.9 × 10-6 Scm-1 at ambient temperature. In the present work, the addition of 2 mol% nanofilller ZrO2 to the electrolyte 85PVA:15NH4F enhances the conductivity to 3.4 × 10-5 Scm-1. The temperature dependence of the conductivity of composite polymer electrolytes obeys Arrhenius relation. In the modulus spectra, there is a long tail at low frequencies which is an evidence for large capacitance associated with the electrodes. In the high frequency region, ∈'(ω) value saturates and giving rise to the dielectric constant of the material.

  16. Development of composite membranes of PVA-TEOS doped KOH for alkaline membrane fuel cell

    SciTech Connect

    Haryadi, Sugianto, D.; Ristopan, E.

    2015-12-29

    Anion exchange membranes (AEMs) play an important role in separating fuel and oxygen (or air) in the Alkaline Membrane Fuel Cells. Preparation of hybrid organic inorganic materials of Polyvinylalcohol (PVA) - Tetraethylorthosilicate (TEOS) composite membrane doped KOH for direct alcohol alkaline fuel cell application has been investigated. The sol-gel method has been used to prepare the composite membrane of PVA-TEOS through crosslinking step and catalyzed by concentrated of hydrochloric acid. The gel solution was cast on the membrane plastic plate to obtain membrane sheets. The dry membranes were then doped by immersing in various concentrations of KOH solutions for about 4 hours. Investigations of the cross-linking process and the presence of hydroxyl group were conducted by FTIR as shown for frequency at about 1600 cm{sup −1} and 3300 cm{sup −1} respectively. The degree of swelling in ethanol decreased as the KOH concentration for membrane soaking process increased. The ion exchange capacity (IEC) of the membrane was 0.25meq/g. This composite membranes display significant ionic conductivity of 3.23 x 10{sup −2} S/cm in deionized water at room temperature. In addition, the morphology observation by scanning electron microscope (SEM) of the membrane indicates that soaking process of membrane in KOH increased thermal resistant.

  17. A novel fixed-bed reactor design incorporating an electrospun PVA/chitosan nanofiber membrane.

    PubMed

    Esmaeili, Akbar; Beni, Ali Aghababai

    2014-09-15

    In this research, a novel fixed-bed reactor was designed with a nanofiber membrane composed of a polyvinyl alcohol (PVA)/chitosan nanofiber blend prepared using an electrospinning technique. The applied voltage, tip-collector distance, and solution flow rate of the electrospinning process were 18 kV, 14.5 cm, and 0.5 mL h(-1), respectively. Brunauer-Emmett-Teller (BET) theory, scanning electron microscope (SEM), and Fourier transform infrared spectroscopy (FT-IR) were employed to characterize and analyze the nanofiber membranes. Homogeneous electrospun nanofibers with an average diameter of 99.47 nm and surface area of 214.12 m(2)g(-1) were obtained. Adsorption experiments were carried out in a batch system to investigate the effect of different adsorption parameters such as pH, adsorbent dose, biomass dose, contact time, and temperature. The kinetic data, obtained at the optimal pH of 6, were analyzed by pseudo first-order and pseudo second-order kinetic models. Three isotherm models and thermodynamic parameters (ΔG°, ΔH°, and ΔS°) were applied to describe the equilibrium data of the metal ions adsorbed onto the PVA/chitosan nanofiber membrane.

  18. Development of antioxidant active films containing sodium ascorbate (SA) and ethylene vinyl alcohol (EVOH) to extend the shelf life of peanut.

    PubMed

    Sangatash, Masoomeh Mehraban; Niazmand, Razieh; Jamab, Mahboobe Sarabi; Modaressi, Amir Sajad

    2016-04-01

    In this study, low-density polyethylene (LDPE) containing oxygen scavenger based on sodium ascorbate (SA) and ethylene vinyl alcohol (EVOH) at 5, 10 and 15 % concentrations were produced through extrusion method. In addition, the effect of size of SA, thickness LDPE (7.5, 15, 30 and 45 μm), and number of layers (monolayer, two-layers, three-layers and four-layers) were investigated. Oxygen and water vapor permeability, tensile stress, SA migration and antioxidant activity, thermal stability, scan electron microscopy (SEM), and FT-IR of the films were measured. Moreover, the performance of produced films to prevent of oxidation of packaged peanuts during storage at 40 °C was studied. The results revealed that the active films containing SA (especially at 10 % SA) present suitable performance and features to increase the shelf-life of peanuts. PMID:27413205

  19. Alcoholism and Alcohol Abuse

    MedlinePlus

    ... This means that their drinking causes distress and harm. It includes alcoholism and alcohol abuse. Alcoholism, or ... brain, and other organs. Drinking during pregnancy can harm your baby. Alcohol also increases the risk of ...

  20. Phase controlled colour tuning of samarium and europium complexes and excellent photostability of their PVA encapsulated materials. Structural elucidation, photophysical parameters and the energy transfer mechanism in the Eu(3+) complex by Sparkle/PM3 calculations.

    PubMed

    Dar, Wakeel Ahmed; Iftikhar, K

    2016-06-01

    Luminescent [Sm(acac)3(pyz)2] (1) and [Eu(acac)3(pyz)2] (2) complexes (acac is the anion of acetylacetone and pyz is pyrazine) have been synthesized and thoroughly characterized by microanalyses, TGA, DTA, IR, ESI-MS(+) and NMR spectroscopy. The photophysical properties of these complexes have been investigated. The Sparkle/PM3 model was utilized for predicting the ground-state geometry of (2). The Judd-Ofelt intensity parameters, radiative parameters, intramolecular energy transfer rates and quantum efficiency are calculated and discussed. The intramolecular energy transfer rates predict that the major energy transfer (96%) is from the ligand triplet state to the levels (5)D1 (74.53%) and (5)D0 (21.87%) of the Eu(3+) ion, in the complex. Complexes (1) and (2) were analysed for colour tuning properties and these show varying colours upon changing phases. This property would possibly allow the use of these complexes as 'colour indicators'. The photoluminescence and photostability of the thin hybrid films of both complexes (1) and (2) in polyvinyl alcohol (PVA) are investigated and discussed. The hybrid films of (1) and (2) are quite robust due to their higher photostability. An important feature of complex (2) is that the excitation window extends close to the visible range (393 nm). The lasing property of the Eu(3+) complex in various phases is also presented. PMID:27157414

  1. MICROWAVE-ASSISTED SYNTHESIS OF CROSSLINKED POLY(VINYL ALCOHOL) NANOCOMPOSITES COMPRISING SINGLE-WALLED CARBON NANOTUBES, MULTI-WALLED CARBON NANOTUBES AND BUCKMINSTERFULLERENE

    EPA Science Inventory

    We report a facile method to accomplish cross-linking reaction of poly (vinyl alcohol) (PVA) with single-wall carbon nanotubes (SWNT), multi-wall carbon nanotubes (MWNT), and Buckminsterfullerene (C-60) using microwave (MW) irradiation. Nanocomposites of PVA cross-linked with SW...

  2. Formulation and Characterization of Acetaminophen Nanoparticles in Orally Disintegrating Films

    NASA Astrophysics Data System (ADS)

    AI-Nemrawi, Nusaiba K.

    in the pharmaceutical industry. These thin films are designed to dissolve within a few seconds without the need for water or chewing. The introduction of fast disintegrating dosage forms has solved some problems encountered in the administration of drugs to pediatric and elderly patients. This convenience provides both marketing advantages and higher patient compliance. Acetaminophen was chosen to be the model drug due to its safety. The amount of acetaminophen in each film is much below the therapeutic dose, but the purpose of using acetaminophen is to be an analytical tracer only. Films were formulated using hydroxypropyl methyl cellulose (HPMC) as film forming polymer, polyethylene glycol 400 (PEG) as a plasticizer and polyvinyl alcohol (PVA) as a NPs stabilizer. First of all, the effect of different Methocel grades and concentration, PEG 400 concentration and PVA 80% concentration on the films were determined. Ingredients that gave best physico-mechanical properties to the films were used in the formulation of ODFs that are loaded with the NPs. Nanoparticles were prepared by the emulsion-solvent evaporation method where acetone phase containing the drug and NPs forming polymers were added to water phase containing other additives. Three types of NPs were prepared: empty, loaded and loaded in ODF dispersion. The size, polydispersity index (PI), zeta potential and drug entrapment efficacy (EE) of NPs were measured. The effect of addition rate, agitation rate, viscosity of the continuous phase, PVA hydrolization, PLGA polymerization and the PLGA to PVA ratio on NPs properties was investigated. The nanoemulsions were cast to form films which were studied in vitro and ex-vivo. Furthermore, the mechanism of drug appearance in the receiver of a Franz cell was explored. Films were placed on a pork buccal membrane using a Franz cell and samples were withdrawn at specific time intervals. Samples were divided into two portions; one of them was extracted while the other was

  3. [Methods and applications of population viability analysis (PVA): a review].

    PubMed

    Tian, Yu; Wu, Jian-Guo; Kou, Xiao-Jun; Wang, Tian-Ming; Smith, Andrew T; Ge, Jian-Ping

    2011-01-01

    With the accelerating human consumption of natural resources, the problems associated with endangered species caused by habitat loss and fragmentation have become greater and more urgent than ever. Conceptually associated with the theories of island biogeography, population viability analysis (PVA) has been one of the most important approaches in studying and protecting endangered species, and this methodology has occupied a central place in conservation biology and ecology in the past several decades. PVA has been widely used and proven effective in many cases, but its predictive ability and accuracy are still in question. Also, its application needs expand. To overcome some of the problems, we believe that PVA needs to incorporate some principles and methods from other fields, particularly landscape ecology and sustainability science. Integrating landscape pattern and socioeconomic factors into PVA will make the approach theoretically more comprehensive and practically more useful. Here, we reviewed the history, basic conception, research methods, and modeling applications and their accuracies of PVA, and proposed the perspective in this field. PMID:21548317

  4. Hemocompatibility study of a bacterial cellulose/polyvinyl alcohol nanocomposite.

    PubMed

    Leitão, Alexandre F; Gupta, Swati; Silva, João Pedro; Reviakine, Ilya; Gama, Miguel

    2013-11-01

    Bacterial cellulose (BC) has been suggested to be a suitable biomaterial for the development of cardiovascular grafts. The combination of BC with polyvinyl alcohol (PVA) results in nanocomposites with improved properties. Surprisingly, there are very few studies on the BC-blood interaction. This is the focus of this paper. We present the first thorough assessment of the hemocompatibility of the BC/PVA nanocomposite. Whole blood clotting time, plasma recalcification, Factor XII activation, platelet adhesion and activation, hemolytic index and complement activation are all determined. The platelet activation profiles on BC and BC/PVA surfaces are comprehensively characterized. BC and BC/PVA outperformed ePTFE--used as a point of comparison--thus evidencing their suitability for cardiovascular applications.

  5. Structural insights into enzymatic degradation of oxidized polyvinyl alcohol.

    PubMed

    Yang, Yu; Ko, Tzu-Ping; Liu, Long; Li, Jianghua; Huang, Chun-Hsiang; Chan, Hsiu-Chien; Ren, Feifei; Jia, Dongxu; Wang, Andrew H-J; Guo, Rey-Ting; Chen, Jian; Du, Guocheng

    2014-09-01

    The ever-increasing production and use of polyvinyl alcohol (PVA) threaten our environment. Yet PVA can be assimilated by microbes in two steps: oxidation and cleavage. Here we report novel α/β-hydrolase structures of oxidized PVA hydrolase (OPH) from two known PVA-degrading organisms, Sphingopyxis sp. 113P3 and Pseudomonas sp. VM15C, including complexes with substrate analogues, acetylacetone and caprylate. The active site is covered by a lid-like β-ribbon. Unlike other esterase and amidase, OPH is unique in cleaving the CC bond of β-diketone, although it has a catalytic triad similar to that of most α/β-hydrolases. Analysis of the crystal structures suggests a double-oxyanion-hole mechanism, previously only found in thiolase cleaving β-ketoacyl-CoA. Three mutations in the lid region showed enhanced activity, with potential in industrial applications.

  6. Biodegradable poly(ethylene-g-vinyl alcohol) copolymer

    SciTech Connect

    Watanabe, T.; Huang, S.J.

    1993-12-31

    A graft reaction of poly(vinyl alcohol), PVA, and polyethylene grafted width maleic anhydride has been carried out in order to add hydrophobicity to PVA. Biodegradabilities of PVA and the polyethylene derivative are well-known. The graft reaction product that was prepared by a simple procedure was characterized with FTIR, DSC, and TGA. The FTIR spectra indicated that ester bonds were formed in the product. It was also found from the thermal analysis that the graft compound was less crystalline that raw PVA and the thermal properties of the graft copolymer remarkably depended on molar ratio of succinic anhydride group in the polyethylene derivative that was used in the graft reaction. The degradation of the material will be discussed.

  7. Synthesis of wheat straw cellulose-g-poly (potassium acrylate)/PVA semi-IPNs superabsorbent resin.

    PubMed

    Liu, Jia; Li, Qian; Su, Yuan; Yue, Qinyan; Gao, Baoyu; Wang, Rui

    2013-04-15

    To better use wheat straw and minimize its negative impact on environment, a novel semi-interpenetrating polymer networks (semi-IPNs) superabsorbent resin (SAR) composed of wheat straw cellulose-g-poly (potassium acrylate) (WSC-g-PKA) network and linear polyvinyl alcohol (PVA) was prepared by polymerization in the presence of a redox initiating system. The structure and morphology of semi-IPNs SAR were characterized by means of FTIR, SEM and TGA, which confirmed that WSC and PVA participated in the graft polymerization reaction with acrylic acid (AA). The factors that can influence the water absorption of the semi-IPNs SAR were investigated and optimized, including the weight ratios of AA to WSC and PVA to WSC, the content of initiator and crosslinker, neutralization degree (ND) of AA, reaction temperature and time. The semi-IPNs SAR prepared under optimized synthesis condition gave the best water absorption of 266.82 g/g in distilled water and 34.32 g/g in 0.9 wt% NaCl solution. PMID:23544572

  8. Functionalized graphene oxide quantum dot-PVA hydrogel: a colorimetric sensor for Fe2+, Co2+ and Cu2+ ions

    NASA Astrophysics Data System (ADS)

    Baruah, Upama; Chowdhury, Devasish

    2016-04-01

    Functionalized graphene oxide quantum dots (GOQDs)-poly(vinyl alcohol) (PVA) hybrid hydrogels were prepared using a simple, facile and cost-effective strategy. GOQDs bearing different surface functional groups were introduced as the cross-linking agent into the PVA matrix thereby resulting in gelation. The four different types of hybrid hydrogels were prepared using graphene oxide, reduced graphene oxide, ester functionalized graphene oxide and amine functionalized GOQDs as cross-linking agents. It was observed that the hybrid hydrogel prepared with amine functionalized GOQDs was the most stable. The potential applicability of using this solid sensing platform has been subsequently explored in an easy, simple, effective and sensitive method for optical detection of M2+ (Fe2+, Co2+ and Cu2+) in aqueous media involving colorimetric detection. Amine functionalized GOQDs-PVA hybrid hydrogel when put into the corresponding solution of Fe2+, Co2+ and Cu2+ renders brown, orange and blue coloration respectively of the solution detecting the presence of Fe2+, Co2+ and Cu2+ ions in the solution. The minimum detection limit observed was 1 × 10-7 M using UV-visible spectroscopy. Further, the applicability of the sensing material was also tested for a mixture of co-existing ions in solution to demonstrate the practical applicability of the system. Insight into the probable mechanistic pathway involved in the detection process is also being discussed.

  9. Encapsulation and immobilization of papain in electrospun nanofibrous membranes of PVA cross-linked with glutaraldehyde vapor.

    PubMed

    Moreno-Cortez, Iván E; Romero-García, Jorge; González-González, Virgilio; García-Gutierrez, Domingo I; Garza-Navarro, Marco A; Cruz-Silva, Rodolfo

    2015-01-01

    In this paper, papain enzyme (E.C. 3.4.22.2, 1.6 U/mg) was successfully immobilized in poly(vinyl alcohol) (PVA) nanofibers prepared by electrospinning. The morphology of the electrospun nanofibers was characterized by scanning electron microscopy (SEM) and the diameter distribution was in the range of 80 to 170 nm. The presence of the enzyme within the PVA nanofibers was confirmed by infrared spectroscopy (FTIR), X-ray photoelectron spectroscopy (XPS) and energy dispersive X-ray spectroscopy (EDXS) analyses. The maximum catalytic activity was reached when the enzyme loading was 13%. The immobilization of papain in the nanofiber membrane was achieved by chemical crosslinking with a glutaraldehyde vapor treatment (GAvt). The catalytic activity of the immobilized papain was 88% with respect to the free enzyme. The crosslinking time by GAvt to immobilize the enzyme onto the nanofiber mat was 24h, and the enzyme retained its catalytic activity after six cycles. The crosslinked samples maintained 40% of their initial activity after being stored for 14 days. PVA electrospun nanofibers are excellent matrices for the immobilization of enzymes due to their high surface area and their nanoporous structure.

  10. Air plasma or UV-irradiation applied to surface modification of pectin/poly(vinyl alcohol) blends

    NASA Astrophysics Data System (ADS)

    Kowalonek, Jolanta; Kaczmarek, Halina; Dąbrowska, Aldona

    2010-10-01

    Poly(vinyl alcohol), pectin and their blends with different components ratio were exposed to low-temperature air plasma or high energy UV-irradiation ( λ = 254 nm) for the purpose of surface modification. The physico-chemical changes in surface properties have been studied by attenuated total reflectance Fourier transform infrared spectroscopy (ATR-FTIR) and contact angle measurements. Surface free energy of polymeric films, its polar and dispersive components have been calculated by Owens-Wendt method. Moreover, the work of adhesion was estimated and the recovery of hydrophobic properties of modified films after storage have been also studied. The few seconds air-plasma treatment caused more effective surface modification than 5-6 h UV-irradiation. The observed changes were partially reversible, contrary to these caused by photo-modification. It was found that pectin/PVA (50:50) blend was characterised by larger susceptibility to plasma modification compared to pure pectin and pure PVA, whereas the photosensitivity to radiation of 254 nm wavelength was the lowest for this specimen in comparison to other studied samples.

  11. Effect of different polyol-based plasticizers on thermal properties of polyvinyl alcohol:starch blends.

    PubMed

    Aydın, Ahmet Alper; Ilberg, Vladimir

    2016-01-20

    A series of gelatinized polyvinyl alcohol (PVA):starch blends were prepared with various polyol-based plasticizers in 5 wt%, 15 wt% and 25 wt% ratios via solution casting method. The obtained films were analyzed by Fourier transform infrared (FT-IR) spectroscopy, differential scanning calorimetry (DSC) and thermogravimetric analysis (TGA). Remarkable changes have been observed in glass-transition temperature (Tg) and thermal stability of the samples containing varying concentrations of different plasticizers and they have been discussed in detail with respect to the conducted thermal and chemical analyses. The observed order of Tg point depression of the samples containing 15 wt% plasticizer is 1,4-butanediol - 1,2,6-hexanetriol--pentaerythriyol--xylitol--mannitol, which is similar to the sequence of the thermal stability changes of the samples.

  12. Effect of different polyol-based plasticizers on thermal properties of polyvinyl alcohol:starch blends.

    PubMed

    Aydın, Ahmet Alper; Ilberg, Vladimir

    2016-01-20

    A series of gelatinized polyvinyl alcohol (PVA):starch blends were prepared with various polyol-based plasticizers in 5 wt%, 15 wt% and 25 wt% ratios via solution casting method. The obtained films were analyzed by Fourier transform infrared (FT-IR) spectroscopy, differential scanning calorimetry (DSC) and thermogravimetric analysis (TGA). Remarkable changes have been observed in glass-transition temperature (Tg) and thermal stability of the samples containing varying concentrations of different plasticizers and they have been discussed in detail with respect to the conducted thermal and chemical analyses. The observed order of Tg point depression of the samples containing 15 wt% plasticizer is 1,4-butanediol - 1,2,6-hexanetriol--pentaerythriyol--xylitol--mannitol, which is similar to the sequence of the thermal stability changes of the samples. PMID:26572374

  13. Diffraction efficiency improvement in high spatial frequency holographic gratings stored in PVA/AA photopolymers: several ACPA concentrations

    NASA Astrophysics Data System (ADS)

    Fernandez, Elena; Fuentes, Rosa; Ortuño, Manuel; Beléndez, Augusto; Pascual, Inmaculada

    2015-01-01

    High spatial frequency in holographic gratings is difficult to obtain due to limitations of the recording material. In this paper, the results obtained after storing holographic transmission gratings with a spatial frequency of 2656 lines/mm in a material based on polyvinyl alcohol and acrylamide (PVA/AA) are presented. A chain transfer agent, 4, 4‧-azobis (4-cyanopentanoic acid) (ACPA) was incorporated in the composition of the material to improve the response of the material at a high spatial frequency. Different concentrations of ACPA were used in order to find the optimal concentration giving maximum diffraction efficiency for high spatial frequencies.

  14. Poly(vinyl alcohol) physical hydrogels: new vista on a long serving biomaterial.

    PubMed

    Alves, Marie-Helene; Jensen, Bettina E B; Smith, Anton A A; Zelikin, Alexander N

    2011-10-10

    Poly(vinyl alcohol), PVA, and physical hydrogels derived thereof have an excellent safety profile and a successful history of biomedical applications. However, these materials are hardly in the focus of biomedical research, largely due to poor opportunities in nano- and micro-scale design associated with PVA hydrogels in their current form. In this review we aim to demonstrate that with PVA, a (sub)molecular control over polymer chemistry translates into fine-tuned supramolecular association of chains and this, in turn, defines macroscopic properties of the material. This nano- to micro- to macro- translation of control is unique for PVA and can now be accomplished using modern tools of macromolecular design. We believe that this strategy affords functionalized PVA physical hydrogels which meet the demands of modern nanobiotechnology and have a potential to become an indispensable tool in the design of biomaterials.

  15. Study of polyvinyl alcohol nanofibrous membrane by electrospinning as a magnetic nanoparticle delivery approach

    SciTech Connect

    Ger, Tzong-Rong; Huang, Hao-Ting; Hu, Keng-Shiang; Huang, Chen-Yu; Lai, Jun-Yang; Chen, Jiann-Yeu; Lai, Mei-Feng

    2014-05-07

    Electrospinning technique was used to fabricate polyvinyl alcohol (PVA)-based magnetic biodegradable nanofibers. PVA solution was mixed with ferrofluid or magnetic nanoparticles (MNPs) powder and formed two individual nanofibrous membranes (PVA/ferrofluid and PVA/MNPs powder) by electrospinning. The surface morphology of the nanofibrous membrane was characterized by scanning electron microscopy and the magnetic properties were measured by vibrating sample magnetometer. Macrophages (RAW 264.7) were co-cultured with the nanofibrous membranes for 12, 24, and 48 h and exhibited good cell viability (>95%). Results showed that the PVA fibers would be degraded and the embedded Fe{sub 3}O{sub 4} nanoparticles would be released and delivered to cells.

  16. Fabrication and Characterization of Graphene/Graphene Oxide-Based Poly(vinyl alcohol) Nanocomposite Membranes

    NASA Astrophysics Data System (ADS)

    Hieu, Nguyen Huu; Long, Nguyen Huynh Bach Son; Kieu, Dang Thi Minh; Nhiem, Ly Tan

    2016-05-01

    Graphene (GE)- or graphene oxide (GO)-based poly(vinyl alcohol) (PVA) nanocomposite membranes have been prepared by the solution blending method. Raman spectra and atomic force microscopy images confirmed that GE and GO were synthesized with average thickness of 0.901 nm and 0.997 nm, respectively. X-ray diffraction patterns indicated good exfoliation of GE or GO in the PVA matrix. Fourier-transform infrared spectra revealed the chemical fractions of the nanocomposite membranes. Differential scanning calorimetry results proved that the thermal stability of the nanocomposite membranes was enhanced compared with neat PVA membrane. Transmission electron microscopy images revealed good dispersion of GE or GO sheets in the PVA matrix with thickness in the range of 19 nm to 39 nm. As a result, good compatibility between GE or GO and PVA was obtained at 0.5 wt.% filler content.

  17. FABRICATION OF A NEW TYPE OF DOUBLE SHELL TARGET HAVING A PVA INNER LAYER

    SciTech Connect

    STEINMAN,D.A; WALLACE,R; GRANT,S.E; HOPPE,M.L; SMITH,JR.J.N

    2003-06-01

    OAK-B135 The General Atomics Target Fabrication team was tasked in FY03, under its ICF Target Support contract, to make a new type of double-shell target. its specifications called for the outer shell to have an inner lining of PVA (poly(vinyl alcohol)) that would keep the xenon gas fill from occupying the target wall. The inner shell consisted of a glass shell coated with 2000 {angstrom} of silver and filled with 9 atm of deuterium. Furthermore, the delivery deadline was less than seven weeks away. This paper describes the fielding of this double-shell target, made possible through the combined efforts of Lawrence Livermore National Laboratory and General Atomics target fabrication specialists.

  18. Immobilization of a Plant Lipase from Pachira aquatica in Alginate and Alginate/PVA Beads

    PubMed Central

    Bonine, Bárbara M.; Polizelli, Patricia Peres; Bonilla-Rodriguez, Gustavo O.

    2014-01-01

    This study reports the immobilization of a new lipase isolated from oleaginous seeds of Pachira aquatica, using beads of calcium alginate (Alg) and poly(vinyl alcohol) (PVA). We evaluated the morphology, number of cycles of reuse, optimum temperature, and temperature stability of both immobilization methods compared to the free enzyme. The immobilized enzymes were more stable than the free enzyme, keeping 60% of the original activity after 4 h at 50°C. The immobilized lipase was reused several times, with activity decreasing to approximately 50% after 5 cycles. Both the free and immobilized enzymes were found to be optimally active between 30 and 40°C. PMID:24818012

  19. Preparation and characterization of antimicrobial wound dressings based on silver, gellan, PVA and borax.

    PubMed

    Cencetti, C; Bellini, D; Pavesio, A; Senigaglia, D; Passariello, C; Virga, A; Matricardi, P

    2012-10-15

    Silver-loaded dressings are designed to provide the same antimicrobial activity of topical silver, with the advantages of a sustained silver release and a reduced number of dressing changes. Moreover, such type of dressing must provide a moist environment, avoiding fiber shedding, dehydration and adherence to the wound site. Here we describe the preparation of a novel silver-loaded dressing based on a Gellan/Hyaff(®) (Ge-H) non woven, treated with a polyvinyl alcohol (PVA)/borax system capable to enhance the entrapment of silver in the dressing and to modulate its release. The new hydrophilic non woven dressings show enhanced water uptake capability and slow dehydration rates. A sustained silver release is also achieved. The antibacterial activity was confirmed on Staphylococcus aureus and Pseudomonas aeruginosa. PMID:22939352

  20. Preparation and characterization of antimicrobial wound dressings based on silver, gellan, PVA and borax.

    PubMed

    Cencetti, C; Bellini, D; Pavesio, A; Senigaglia, D; Passariello, C; Virga, A; Matricardi, P

    2012-10-15

    Silver-loaded dressings are designed to provide the same antimicrobial activity of topical silver, with the advantages of a sustained silver release and a reduced number of dressing changes. Moreover, such type of dressing must provide a moist environment, avoiding fiber shedding, dehydration and adherence to the wound site. Here we describe the preparation of a novel silver-loaded dressing based on a Gellan/Hyaff(®) (Ge-H) non woven, treated with a polyvinyl alcohol (PVA)/borax system capable to enhance the entrapment of silver in the dressing and to modulate its release. The new hydrophilic non woven dressings show enhanced water uptake capability and slow dehydration rates. A sustained silver release is also achieved. The antibacterial activity was confirmed on Staphylococcus aureus and Pseudomonas aeruginosa.

  1. Water-soluble thin film transistors and circuits based on amorphous indium-gallium-zinc oxide.

    PubMed

    Jin, Sung Hun; Kang, Seung-Kyun; Cho, In-Tak; Han, Sang Youn; Chung, Ha Uk; Lee, Dong Joon; Shin, Jongmin; Baek, Geun Woo; Kim, Tae-il; Lee, Jong-Ho; Rogers, John A

    2015-04-22

    This paper presents device designs, circuit demonstrations, and dissolution kinetics for amorphous indium-gallium-zinc oxide (a-IGZO) thin film transistors (TFTs) comprised completely of water-soluble materials, including SiNx, SiOx, molybdenum, and poly(vinyl alcohol) (PVA). Collections of these types of physically transient a-IGZO TFTs and 5-stage ring oscillators (ROs), constructed with them, show field effect mobilities (∼10 cm2/Vs), on/off ratios (∼2×10(6)), subthreshold slopes (∼220 mV/dec), Ohmic contact properties, and oscillation frequency of 5.67 kHz at supply voltages of 19 V, all comparable to otherwise similar devices constructed in conventional ways with standard, nontransient materials. Studies of dissolution kinetics for a-IGZO films in deionized water, bovine serum, and phosphate buffer saline solution provide data of relevance for the potential use of these materials and this technology in temporary biomedical implants.

  2. Radiation sensitive indicator based on tetrabromophenol blue dyed poly(vinyl alcohol)

    NASA Astrophysics Data System (ADS)

    Beshir, W. B.

    2013-05-01

    Radiation sensitive indicators based on dyed polyvinyl alcohol (PVA) containing acid- sensitive dye (tetrabromophenol blue, TBPB) and chloral hydrate (CCl3·CH·(OH)2, 2,2,2-trichloroethane-1,1-diol) have been developed. These plastic film dosimeters undergo color change from blue (the alkaline form of TBPB) to yellow (the acidic form of TBPB), indicating acid formation. The concentration of radiation formed acids in the films containing different concentrations of chloral hydrate was calculated at different doses. These films can be used as dosimeters for food irradiation applications where the maximum of the useful dose ranges are between 1 and 8 kGy depending on chloral hydrate concentration in the film. The films have the advantage of negligible humidity effects on response in the intermediate range of relative humidity from 0 to 70% as good post irradiation stability when stored in the dark at room temperature. The overall combined uncertainty (at 2σ) associated with measurement of response (ΔA mm-1) at 623 nm for dose range 1-8 kGy is 4.53%.

  3. Influences of alcoholic solvents on spray pyrolysis deposition of TiO{sub 2} blocking layer films for solid-state dye-sensitized solar cells

    SciTech Connect

    Jiang, Changyun; Koh, Wei Lin; Leung, Man Yin; Hong, Wei; Li, Yuning; Zhang, Jie

    2013-02-15

    Influences of alcoholic solvents for titanium diisopropoxide bis(acetylacetonate) (TPA) precursor solutions on the spray pyrolysis deposited TiO{sub 2} films and the photovoltaic performance of the solid-state dye-sensitized solar cells (SDSCs) using these TiO{sub 2} films as the blocking layers were investigated. Smooth TiO{sub 2} films were obtained by spray pyrolysis deposition of a TPA solution in isopropanol (IPA) at a relatively low temperature of 260 Degree-Sign C. On the other hand, when ethanol was used as solvent, the TiO{sub 2} films fabricated at the same temperature showed much rougher surfaces with many pinholes. Our results showed that ethanol reacts with TPA to form titanium diethoxide bis(acetylacetonate) (TEA), which requires a higher thermal decomposition temperature than that of TPA. SDSCs with TiO{sub 2} blocking layer films fabricated using a TPA solution in IPA showed higher power conversion efficiencies with smaller variations. - Graphical abstract: Alcoholic solvents used for the TiO{sub 2} precursor play a critical role in determining the surface morphology of blocking layers and thus the photovoltaic performance of the SDSCs. Highlights: Black-Right-Pointing-Pointer Solvent influences morphology of spray pyrolysis deposited TiO{sub 2} blocking layer. Black-Right-Pointing-Pointer Ethanol reacts with TPA, resulting poor quality of blocking layer. Black-Right-Pointing-Pointer Isopropanol is better than ethanol for obtaining smooth blocking layer. Black-Right-Pointing-Pointer SDSC with blocking layer made with isopropanol showed better performance.

  4. Facile synthesis of boehmite/PVA composite membrane with enhanced adsorption performance towards Cr(VI).

    PubMed

    Luo, Lei; Cai, Weiquan; Zhou, Jiabin; Li, Yuanzhi

    2016-11-15

    A novel boehmite/PVA composite membrane (BPCM) with remarkably enhanced adsorption performance towards Cr(VI) was successfully synthesized from Al(NO3)3·9H2O using HAc as the peptizing agent via a facile sol-gel method. The physicochemical properties of the BPCM, the boehmite powder (BP) without PVA and a commercial boehmite powder (CBP) were comparatively characterized by XRD, TGA-DSC, FT-IR and XPS. Batch adsorption experiments showed that the adsorption performance of the BPCM is much better than those of BP and CBP. Its adsorption process was well described by the pseudo-second-order kinetic model, and its equilibrium data fit the Langmuir isotherm well with a maximum adsorption capacity of 36.41mgg(-1). Its interference adsorption experiment in presence of coexisting anions showed that SO4(2-) and HPO4(2-) have greater effect than those of the Cl(-), F(-), C2O4(2-) and HCO3(-). A three step action mechanism including adsorption of Cr(VI) anions, complexation between Cr(VI) anions and the functional groups on the surface of BPCM, and the reduction of Cr(VI) to Cr(III) was proposed to illustrate the adsorption process. This efficient film could be easily separated after adsorption, exhibiting great potential for the removal of Cr(VI) from aqueous solution, and other fields of environmental remediation. PMID:27450337

  5. Effect of Cross-Linking on the Mechanical and Thermal Properties of Poly(amidoamine) Dendrimer/Poly(vinyl alcohol) Hybrid Membranes for CO2 Separation

    PubMed Central

    Duan, Shuhong; Kai, Teruhiko; Saito, Takashi; Yamazaki, Kota; Ikeda, Kenichi

    2014-01-01

    Poly(amidoamine) (PAMAM) dendrimers were incorporated into cross-linked poly(vinyl alcohol) (PVA) matrix to improve carbon dioxide (CO2) separation performance at elevated pressures. In our previous studies, PAMAM/PVA hybrid membranes showed high CO2 separation properties from CO2/H2 mixed gases. In this study, three types of organic Ti metal compounds were selected as PVA cross-linkers that were used to prepare PAMAM/cross-linked PVA hybrid membranes. Characterization of the PAMAM/cross-linked PVA hybrid membranes was conducted using nanoindentation and thermogravimetric analyses. The effects of the cross-linker and CO2 partial pressure in the feed gas on CO2 separation performance were discussed. H2O and CO2 sorption of the PAMAM/PVA hybrid membranes were investigated to explain the obtained CO2 separation efficiencies. PMID:24957172

  6. An intensive study on the optical, rheological, and electrokinetic properties of polyvinyl alcohol-capped nanogold

    NASA Astrophysics Data System (ADS)

    Behera, Manoranjan

    2015-05-01

    Low-temperature-assisted wet chemical synthesis of nanogold (NG) using gold hydroxide, a new precursor salt in the presence of a macroscopic ligand poly(vinyl alcohol) PVA in water in the form of nanofluid, is reported for the first time in this article. In the absorption spectra, the surface Plasmon resonance absorption band in the range of 520-545 nm signifies the formation of NG via a controlled Au3+ + 3e → Au reaction grafted in small assemblies with polymer. Absorption maximum increases nonlinearly with Au-contents up to 100 µM Au in Au-PVA charge-transfer complex. Marked enhancement in the peak intensity of some of the vibration bands of PVA polymer such as C-H stretching, C=O stretching, CH2 bending, and C-C in-plane bending in the presence of NG reveals an interfacial interaction between NG and oxidized PVA via C=O group. Execution of shear thinning behavior regardless of the Au-content strongly suggests that crosslinking exists between NG and PVA in Au-PVA rheo-optical nanofluids. Hydrodynamic diameter and polydispersity index draw a nonlinear path with the Au doping with 30.0 g/L PVA in water over a wide region of 5-100 μM Au covered in this study. Enhancement in the zetapotential of Au-PVA nanofluid over bare PVA in water is ascribed to buildup of nonbonding electrons of "-C=O" moieties from the oxidized PVA on the NG surface. Displaying of lattice fringes in the microscopic image of core-shell Au-PVA nanostructure confirms that crystalline nature of NG core with inter planar spacing 0.235 nm corresponds to Au (111) plane.

  7. Hydrogen-Bonding-Supported Self-Healing Antifogging Thin Films

    NASA Astrophysics Data System (ADS)

    Zhang, Xiaojie; He, Junhui

    2015-03-01

    Inspired by the repair of DNA through efficient reformation of hydrogen bonds (H-bonds), herein we report a facile one-step approach to construction of self-healing antifogging thin films on the basis of partly cross-linked poly(vinyl alcohol)(PVA) and poly(acrylic acid)(PAA). By designing the molar ratio of hydroxyl groups to carboxyl groups, the cross-linked polymer thin films maintain abundant free hydroxyl groups to present excellent antifogging property, which is derived from the hydrophilicity and hygroscopicity of the thin films. The thin films showed smart intrinsic self-healing characteristics towards wounds caused by external forces, which is attributed to sufficient free hydroxyl groups at the scratched interfaces to reform H-bonds across the interfaces and a sufficient chain mobility that is indispensable for chain diffusion across the interfaces and hydroxyl groups association to form H-bonds. No synthetic surfaces reported so far possess all the unique characteristics of the polymer thin films: intrinsic self-healing, long-term antifogging, excellent mechanical property, high transmittance and large-scale feasibility.

  8. Hydrogen-Bonding-Supported Self-Healing Antifogging Thin Films

    PubMed Central

    Zhang, Xiaojie; He, Junhui

    2015-01-01

    Inspired by the repair of DNA through efficient reformation of hydrogen bonds (H-bonds), herein we report a facile one-step approach to construction of self-healing antifogging thin films on the basis of partly cross-linked poly(vinyl alcohol)(PVA) and poly(acrylic acid)(PAA). By designing the molar ratio of hydroxyl groups to carboxyl groups, the cross-linked polymer thin films maintain abundant free hydroxyl groups to present excellent antifogging property, which is derived from the hydrophilicity and hygroscopicity of the thin films. The thin films showed smart intrinsic self-healing characteristics towards wounds caused by external forces, which is attributed to sufficient free hydroxyl groups at the scratched interfaces to reform H-bonds across the interfaces and a sufficient chain mobility that is indispensable for chain diffusion across the interfaces and hydroxyl groups association to form H-bonds. No synthetic surfaces reported so far possess all the unique characteristics of the polymer thin films: intrinsic self-healing, long-term antifogging, excellent mechanical property, high transmittance and large-scale feasibility. PMID:25784188

  9. Oral delivery of ivermectin using a fast dissolving oral film: Implications for repurposing ivermectin as a pharmacotherapy for alcohol use disorder.

    PubMed

    Yardley, Megan M; Huynh, Nhat; Rodgers, Kathleen E; Alkana, Ronald L; Davies, Daryl L

    2015-09-01

    Individuals suffering from an alcohol-use disorder (AUD) constitute a major health concern. Preclinical studies in our laboratory show that acute and chronic intraperitoneal (i.p.) administration of ivermectin (IVM) reduces alcohol intake and preference in mice. To enable clinical investigation to use IVM for the treatment of an AUD, development of an oral formulation that can be used in animals as well as long-term preclinical toxicology studies are required. The present work explores the use of a promising alternative dosage form of IVM, fast-dissolving oral films (Cure Pharmaceutical®), to test the efficacy and safety of oral IVM in conjunction with alcohol exposure. We tested the effect of IVM (0.21 mg) using a fast-dissolving oral film delivery method on reducing 10% v/v alcohol (10E) intake in female C57BL/6 mice using a 24-h access two-bottle choice paradigm for 6 weeks (5 days per week). Differences in ethanol intake, preference for ethanol, water intake, fluid intake, food intake, changes in mouse and organ weights, as well as histological changes to kidney, liver, and brain were analyzed. The IVM group drank significantly less ethanol over the 30-day period compared to the placebo (blank strip) and the no-treatment groups. Organ weights did not differ between the groups. Histological evaluation showed no differences in the brain and kidney between groups. In the liver, there was a slight increase in the incidence of microvesicular fatty and degenerative changes of the animals receiving the thin strips. No overt hepatocellular necrosis or perivascular inflammation was noted. Overall, these data support the use of this novel method of oral drug delivery for longer-term studies and should facilitate FDA required preclinical testing that is necessary to repurpose IVM for treatment of an AUD.

  10. An experimental study for syndiotactic polyvinyl alcohol spheres as an embolic agent: can it maintain spherical shape in vivo?

    PubMed

    Chun, Ho Jong; Lee, Hae Giu; Lyoo, Won Seok; Lee, Ji Youl; Kim, Jina

    2014-01-01

    Syndiotactic polyvinyl alcohol (PVA) had been developed to overcome the drawbacks of atactic PVA spheres that deform easily, which can lead to non-target embolization. This study was performed to evaluate the in vivo stability of spherical shape of the syndiotactic PVA spheres. Selective arteriography and transarterial embolization (TAE) were performed in the main renal arteries of eight New Zealand white rabbits using syndiotactic PVA sphere that consisted of syndiotactic PVA skin and a copolymer core of vinyl acetate/vinyl pivalate. The size of the syndiotactic PVA spheres used for the TAE was 212-355 μm. The rabbits were sacrificed 12-14 days after TAE. Gross and microscopic examinations of each kidney were performed. The microscopic examination showed infarction of all embolized kidneys. Syndiotactic PVA spheres were seen uniformly within the arterial lumen and appeared as round ring-like structures without any deformity. The syndiotactic PVA spheres exclusively occupied the arterial lumen. As a conclusion, syndiotactic PVA spheres maintained their spherical shape without significant deformation in this in vivo short-term experimental study. Further investigation is necessary for evaluation of detailed effects of physical stability in tumor embolization.

  11. Large-scale synthesis of flexible free-standing SERS substrates with high sensitivity: electrospun PVA nanofibers embedded with controlled alignment of silver nanoparticles.

    PubMed

    He, Dian; Hu, Bo; Yao, Qiao-Feng; Wang, Kan; Yu, Shu-Hong

    2009-12-22

    A new and facile way to synthesize a free-standing and flexible surface-enhanced Raman scattering (SERS) substrate has been successfully developed, where high SERS-active Ag dimers or aligned aggregates are assembled within poly(vinyl alcohol) (PVA) nanofibers with chain-like arrays via electrospinning technique. The aggregation state of the obtained Ag nanoparticle dimers or larger, which are formed in a concentrated PVA solution, makes a significant contribution to the high sensitivity of SERS to 4-mercaptobenzoic acid (4-MBA) molecules with an enhancement factor (EF) of 10(9). The superiority of enhancement ability of this Ag/PVA nanofiber mat is also shown in the comparison to other substrates. Furthermore, the Ag/PVA nanofiber mat would keep a good reproducibility under a low concentration of 4-MBA molecule (10(-6) M) detection with the average RSD values of the major Raman peak less than 0.07. The temporal stability of the substrate has also been demonstrated. This disposable, easy handled, flexible free-standing substrate integrated the advantages including the superiority of high sensitivity, reproducibility, stability, large-scale, and low-cost production compared with other conventional SERS substrates, implying that it is a perfect choice for practical SERS detection application.

  12. Electrospun tungsten oxide NPs/PVA nanofibers: A study on the morphology and Kramers-Kronig analysis of infrared reflectance spectra

    NASA Astrophysics Data System (ADS)

    Chenari, Hossein Mahmoudi; Kangarlou, Haleh

    2016-10-01

    The major objective of this work is focused on the preparation and characterization of poly (vinyl alcohol) (PVA) embedding tungsten oxide nanoparticles based on electrospinning technique. A surfactant (CTAB) was introduced to incorporate tungsten oxide nanoparticles into the PVA nanofibers homogeneously. To prepare a viscous solution of PVA nanofiber containing tungsten oxide nanoparticles, the distance between the tip of the needle and the surface of the foil was chosen as 10 and 15 cm. The tungsten oxide NPs/PVA composite nanofibers have been characterized using scanning electron microscopy (SEM), Fourier transform infrared spectroscopy (FTIR) and reflectance spectrum in the wave length range of 200-1200 nm. Fiber diameters decrease with increasing of tip-to-collector distance from 10 to 15 cm. The average diameters were estimated about 165±30 nm and 145±30 nm from scanning electron microscopy at 10 and 15 cm, respectively. The optical properties of the electrospun nanofibers were examined by the Kramers-Kronig model. The optical results show that tungsten oxide nanopowder show almost five times higher conductivity, lower absorbance and zero band gap energy.

  13. Graphene-poly(vinyl alcohol) composites: Fabrication, adsorption and electrochemical properties

    NASA Astrophysics Data System (ADS)

    Wang, Ning; Chang, Peter R.; Zheng, Pengwu; Ma, Xiaofei

    2014-09-01

    Porous composites of graphene oxide (GO)-poly(vinyl alcohol) (PVA) were fabricated using a process of aqueous suspension precursor freezing, solvent exchange, and ethanol drying. When frozen, ice crystals formed leaving a porous structure, composed of randomly oriented GO sheets consolidated by PVA. The yellow GO-PVA composite could be reduced with glucose to obtain a black porous RGO (PRGO). XRD revealed that PVA enlarged the GO interlay spacing in the GO-PVA composite, and that RGO sheets were highly disordered in single or several layers in PRGO. GO-PVA and PRGO exhibited ultralight densities of 10.52 and 11.42 mg/cm3, respectively. GO-PVA adsorbed greater quantities of water, ethanol, and soybean oil than PRGO. The methylene blue (MB) adsorption pattern for both materials was also investigated. The kinetic adsorption and isotherm data fit the pseudo second-order and the Langmuir models, respectively. The maximum adsorption capacity according to the Langmuir isotherm model was 571.4 mg/g for GO-PVA. The electrochemical properties of PRGO were estimated using cyclic voltammetry, electrochemical impedance spectrometry, and chronopotentiometry. The PRGO electrode exhibited large capacitance (82.8 F/g) and small internal resistance (0.52 Ω).

  14. Conditions for obtaining polyvinyl alcohol/trisodium trimetaphosphate hydrogels as vitreous humor substitute.

    PubMed

    Morandim-Giannetti, Andreia de Araujo; Silva, Rosianne Cristina; Magalhães, Octaviano; Schor, Paulo; Bersanetti, Patrícia Alessandra

    2016-10-01

    Hydrogels are polymeric materials with numerous medical and biological applications because of their physicochemical properties. In this context, the conditions were defined for obtaining a hydrogel with characteristics similar to the vitreous humor using polyvinyl alcohol (PVA) and trisodium trimetaphosphate (STMP). The concentration of PVA (X1 ), PVA/STMP ratio (X2 ), and initial pH (X3 ) were modified, and their effect was analyzed in terms of the refractive index (Y1 ), density (Y2 ), dynamic viscosity (Y3 ), and final pH (Y4 ). The results demonstrated that X1 interferes with Y1 , Y2 , and Y3 , and X2 interferes with Y2 and Y3 . The best condition for obtaining a hydrogel with characteristics similar to the vitreous humor was 4.2586% PVA (wt/wt), STMP/PVA ratio of 1:6.8213 (wt/wt), and initial pH of 9.424. DSC, ATR-FTIR, swelling degree, and AFM analysis confirmed the PVA reticulation with STMP. Furthermore, STMP increased the glass transition temperature and decreased the water uptake of ∼50% of the hydrogels, which can be explained by the crosslinking of PVA chains. Infrared spectroscopy revealed a decrease of hydroxyl bonds and confirmed the reticulation between PVA and STMP. © 2015 Wiley Periodicals, Inc. J Biomed Mater Res Part B: Appl Biomater, 104B: 1386-1395, 2016.

  15. Preparation and Properties of Nano-Hydroxyapatite/Gelatin/Poly(vinyl alcohol) Composite Membrane.

    PubMed

    Liao, Haotian; Shi, Kun; Peng, Jinrong; Qu, Ying; Liao, Jinfeng; Qian, Zhiyong

    2015-06-01

    In this study, the bone-like composite membrane based on blends of gelatin (Gel), nano-hydroxyapatite (n-HA) and poly(vinyl alcohol) (PVA) was fabricated by solvent casting and evaporation methods. The effect of n-HA content and the ratio of Gel/PVA on the properties of the composite was investigated. The Gel/PVA and n-HA/Gel/PVA composite membranes were characterized by Fourier transform infrared spectroscopy (FT-IR), X-ray diffraction (XRD), water contact angle measurement and scanning electron microscopy (SEM). The mechanical properties of the composites were determined by tensile tests. The as prepared composite membranes exhibited hydrophobility, the water contact angle of composite membrane was 126.6 when its mass ratio of n-HA/Gel/PVA was 10/50/40. The tensile strength of composite membranes was greatly increased due to the introduction of n-HA, and the tensile strength was increased to 74.92 MPa when the mass ratio of n-HA/Gel/PVA was 10/50/40. SEM observation indicated that n-HA was dispersed in the membranes and a sea-island structure was formed in the n-HA/Gel/PVA composite membranes, resulting in a significant increase in tensile strength. The as-prepared n-HA/Gel/PVA composite membranes may be applied in the field of bone tissue engineering. PMID:26369028

  16. Conditions for obtaining polyvinyl alcohol/trisodium trimetaphosphate hydrogels as vitreous humor substitute.

    PubMed

    Morandim-Giannetti, Andreia de Araujo; Silva, Rosianne Cristina; Magalhães, Octaviano; Schor, Paulo; Bersanetti, Patrícia Alessandra

    2016-10-01

    Hydrogels are polymeric materials with numerous medical and biological applications because of their physicochemical properties. In this context, the conditions were defined for obtaining a hydrogel with characteristics similar to the vitreous humor using polyvinyl alcohol (PVA) and trisodium trimetaphosphate (STMP). The concentration of PVA (X1 ), PVA/STMP ratio (X2 ), and initial pH (X3 ) were modified, and their effect was analyzed in terms of the refractive index (Y1 ), density (Y2 ), dynamic viscosity (Y3 ), and final pH (Y4 ). The results demonstrated that X1 interferes with Y1 , Y2 , and Y3 , and X2 interferes with Y2 and Y3 . The best condition for obtaining a hydrogel with characteristics similar to the vitreous humor was 4.2586% PVA (wt/wt), STMP/PVA ratio of 1:6.8213 (wt/wt), and initial pH of 9.424. DSC, ATR-FTIR, swelling degree, and AFM analysis confirmed the PVA reticulation with STMP. Furthermore, STMP increased the glass transition temperature and decreased the water uptake of ∼50% of the hydrogels, which can be explained by the crosslinking of PVA chains. Infrared spectroscopy revealed a decrease of hydroxyl bonds and confirmed the reticulation between PVA and STMP. © 2015 Wiley Periodicals, Inc. J Biomed Mater Res Part B: Appl Biomater, 104B: 1386-1395, 2016. PMID:26224170

  17. Vitamin C hinders radiation cross-linking in aqueous poly(vinyl alcohol) solutions

    NASA Astrophysics Data System (ADS)

    Oral, Ebru; Bodugoz-Senturk, Hatice; Macias, Celia; Muratoglu, Orhun K.

    2007-12-01

    Poly(vinyl alcohol) (PVA) is a promising semi-crystalline material for biomedical applications. It is soluble in water and can be formed into hydrogels by freezing and thawing or crystallizing from an aqueous theta solution such as that of polyethylene glycol (PEG). Radiation cross-linking caused by sterilization or high dose irradiation of concentrated PVA solutions could compromise some properties of these hydrogels. Therefore, we hypothesized that radiation cross-linking of PVA solutions and PVA-PEG theta gels could be prevented by using the antioxidant vitamin C as an anticross-linking agent. Our hypothesis tested positive. Vitamin C concentrations of 0.75 and 4.5 mol/mol of PVA repeating unit could prevent cross-linking in 17.5 wt/v% PVA solutions made with PVA molecular weight of 115,000 g/mol irradiated to 25 and 100 kGy, respectively. Vitamin C also prevented cross-linking in 25 kGy irradiated PVA-PEG theta gels containing up to 5 wt% PEG and decreased the viscosity of those up to 39 wt%.

  18. Facile fabrication of magnetic carboxymethyl starch/poly(vinyl alcohol) composite gel for methylene blue removal.

    PubMed

    Gong, Guisheng; Zhang, Faai; Cheng, Zehong; Zhou, Li

    2015-11-01

    This study presents a simple method to fabricate magnetic carboxymethyl starch/poly(vinyl alcohol) (mCMS/PVA) composite gel. The obtained mCMS/PVA was characterized by Fourier transform infrared (FTIR) spectra, vibrating-sample magnetometer (VSM) and scanning electron microscopy (SEM) measurements. The application of mCMS/PVA as an adsorbent for removal of cationic methylene blue (MB) dye from water was investigated. Benefiting from the combined merits of carboxymethyl starch and magnetic gel, the mCMS/PVA simultaneously exhibited excellent adsorption property toward MB and convenient magnetic separation capability. The effects of initial dye concentration, contact time, pH and ionic strength on the adsorption performance of mCMS/PVA adsorbent were investigated systematically. The adsorption process of mCMS/PVA for MB fitted pseudo-second-order model and Freundlich isotherm. Moreover, desorption experiments revealed that the mCMS/PVA adsorbent could be well regenerated in ethanol solution without obvious compromise of removal efficiency even after eight cycles of desorption/adsorption. Considering the facile fabrication process and robust adsorption performance, the mCMS/PVA composite gel has great potential as a low cost adsorbent for environmental decontamination.

  19. Preparation and characterization of poly(vinyl alcohol)/graphene nanofibers synthesized by electrospinning

    NASA Astrophysics Data System (ADS)

    Barzegar, Farshad; Bello, Abdulhakeem; Fabiane, Mopeli; Khamlich, Saleh; Momodu, Damilola; Taghizadeh, Fatemeh; Dangbegnon, Julien; Manyala, Ncholu

    2015-02-01

    We report on the synthesis and characterization of electrospun polyvinyl alcohol (PVA)/graphene nanofibers. The samples produced were characterized by Raman spectroscopy for structural and defect density analysis, scanning electron microscopy (SEM) for morphological analysis, and thermogravimetric (TGA) for thermal analysis. SEM measurements show uniform hollow PVA fibers formation and excellent graphene dispersion within the fibers, while TGA measurements show the improved thermal stability of PVA in the presence of graphene. The synthesized polymer reinforced nanofibers have potential to serve in many different applications such as thermal management, supercapacitor electrodes and biomedical materials for drug delivery.

  20. Suppression of instability by double ablation in tungsten doped polyvinyl alcohol foils

    NASA Astrophysics Data System (ADS)

    Peedikakkandy, Leshma; Chaurasia, S.

    2012-07-01

    In Inertial fusion Energy (IFE) research stable acceleration of fusion targets is a significant problem due to hydrodynamic instabilities. This paper presents the results of the experiments done to investigate the effects of doping 20% of Tungsten (W) (by weight) in Polyvinyl Alcohol (PVA) polymer foils for suppression of instability during laser ablative acceleration. A 20J, 1.060μm, 900ps, Nd: Glass laser system with a focusable intensity of 3 to 9.6×1013W/cm2 was used in the experiment. It is observed that the doped PVA targets yielded stable and enhanced foil acceleration as compared to the undoped PVA foils.