Method of producing amorphous thin films

DOEpatents

Brusasco, R.M.

1992-09-01

Disclosed is a method of producing thin films by sintering which comprises: (a) coating a substrate with a thin film of an inorganic glass forming material possessing the capability of being sintered; and (b) irradiating said thin film of said particulate material with a laser beam of sufficient power to cause sintering of said material below the temperature of liquidus thereof. Also disclosed is the article produced by the method claimed. 4 figs.

Thermal annealing and SHI irradiation induced modifications in sandwiched structured Carbon-gold-Carbon (a-C/Au/a-C) nanocomposite thin film

NASA Astrophysics Data System (ADS)

Singh, S. K.; Singhal, R.

2017-09-01

In the present work, we study the annealing and swift heavy ion (SHI) beam induced modifications in the optical and structural properties of sandwiched structured Carbon-gold-Carbon (a-C/Au/a-C) nanocomposite (NCs) thin films. The NCs thin films were synthesized by electron-beam evaporation technique at room temperature with ∼30 nm thickness for both carbon layer and ∼6 nm for gold layer. Gold-carbon NCs thin films were annealed in the presence of argon at a temperature of 500 °C, 600 °C and 750 °C. The NCs thin films were also irradiated with 90 MeV Ni ions beam with different ion fluences in the range from 3 × 1012, 6 × 1012 and 1 × 1013 ions/cm2. Surface plasmon resonance (SPR) of Au nanoparticles are not observed in the pristine film but, after annealing at temperature of 600 °C and 750 °C, it was clearly seen at ∼534 nm as confirmed by UV-visible absorption spectroscopy. 90 MeV Ni irradiated thin film at the fluence of 1 × 1013 ions/cm2 also show strong absorption band at ∼534 nm. The growth and size of Au nanoparticle for pristine and 90 MeV Ni ion irradiated thin film with fluence of 1 × 1013 ions/cm2, were estimated by Transmission electron microscopy (TEM) images with the bi-model distribution. The size of the gold nanoparticle (NPs) was found to be ∼4.5 nm for the pristine film and ∼5.4 nm for the irradiated film at a fluence of 1 × 1013 ions/cm2. The thickness and metal atomic fraction in carbon matrix were estimated by Rutherford backscattering spectroscopy (RBS). The effect of annealing as well as heavy ion irradiation on D and G band of carbon matrix were studied by Raman spectroscopy.

Effect of substrate temperature on magnetic properties of MnFe2O4 thin films

NASA Astrophysics Data System (ADS)

Rajagiri, Prabhu; Sahu, B. N.; Venkataramani, N.; Prasad, Shiva; Krishnan, R.

2018-05-01

MnFe2O4 thin films were pulsed laser deposited on to quartz substrate from room temperature (RT) to 650 °C in a pure argon environment. Temperature dependence of spontaneous magnetization (4πMS) was measured on these films from 10 K to 350 K using a vibrating sample magnetometer. Ferromagnetic resonance (FMR) study was also carried out at 300 K. The exchange stiffness constant (D) values were obtained by fitting the 4πMS data to the Bloch's equation. The D values of the films thus found decreases while the 4πMS value increases, though non-monotonically, with the increase in TS and tend to reach bulk values at TS = 650 °C. The variation in D and 4πMS values of the films are explained based on the degree of inversion and oxidation state of cations in thin films.

Doping induced c-axis oriented growth of transparent ZnO thin film

NASA Astrophysics Data System (ADS)

Mistry, Bhaumik V.; Joshi, U. S.

2018-04-01

c-Axis oriented In doped ZnO (IZO) transparent conducting thin films were optimized on glass substrate using sol gel spin coating method. The Indium content in ZnO was varied systematically and the structural parameters were studied. Along with the crystallographic properties, the optoelectronic and electrical properties of IZO thin films were investigated in detail. The IZO thin films revealed hexagonal wurtzite structure. It was found that In doping in ZnO promotes the c-axis oriented growth of the thin films deposited on amorphous substrate. The particle size of the IZO films were increase as doping content increases from 2% to 5%. The 2% In doped ZnO film show electrical resistivity of 0.11 Ω cm, which is far better than the reported value for ZnO thin film. Better than 75% average optical transmission was estimated in the wavelength range from 400-800 nm. Systematic variartions in the electron concentration and band gap was observed with increasing In doping. Note worthy finding is that, with suitable amount of In doping improves not only transparency and conductivity but also improves the preferred orientation of the oxide thin film.

Chemical spray pyrolyzed kesterite Cu2ZnSnS4 (CZTS) thin films

NASA Astrophysics Data System (ADS)

Khalate, S. A.; Kate, R. S.; Deokate, R. J.

2018-04-01

Pure kesterite phase thin films of Cu2ZnSnS4 (CZTS) were synthesized at different substrate temperatures using sulphate precursors by spray pyrolysis method. The significance of synthesis temperature on the structural, morphological and optical properties has been studied. The X-ray analysis assured that synthesized CZTS thin films showing pure kesterite phase. The value of crystallite size was found maximum at the substrate temperature 400 °C. At the same temperature, microstructural properties such as dislocation density, micro-strain and stacking fault probability were found minimum. The morphological examination designates the development of porous and uniform CZTS thin films. The synthesized CZTS thin films illustrate excellent optical absorption (105 cm-1) in the visible band and the optical band gap varies in the range of 1.489 eV to 1.499 eV.

Sputtered magnesium diboride thin films: Growth conditions and surface morphology

NASA Astrophysics Data System (ADS)

O'Brien, April; Villegas, Brendon; Gu, J. Y.

2009-01-01

Magnesium diboride (MgB 2) thin films were deposited on C-plane sapphire substrates by sputtering pure B and Mg targets at different substrate temperatures, and were followed by in situ annealing. A systematic study about the effects of the various growth and annealing parameters on the physical properties of MgB 2 thin films showed that the substrate temperature is the most critical factor that determines the superconducting transition temperature ( Tc), while annealing plays a minor role. There was no superconducting transition in the thin films grown at room temperature without post-annealing. The highest Tc of the samples grown at room temperature after the optimized annealing was 22 K. As the temperature of the substrate ( Ts) increased, Tc rose. However, the maximum Ts was limited due to the low magnesium sticking coefficient and thus the Tc value was limited as well. The highest Tc, 29 K, was obtained for the sample deposited at 180 °C, annealed at 620 °C, and was subsequently annealed a second time at 800 °C. Three-dimensional (3D) AFM images clearly demonstrated that the thin films with no transition, or very low Tc, did not have the well-developed MgB 2 grains while the films with higher Tc displayed the well-developed grains and smooth surface. Although the Tc of sputtered MgB 2 films in the current work is lower than that for the bulk and ex situ annealed thin films, this work presents an important step towards the fabrication of MgB 2 heterostructures using rather simple physical vapor deposition method such as sputtering.

Conformal Thin Film Packaging for SiC Sensor Circuits in Harsh Environments

NASA Technical Reports Server (NTRS)

Scardelletti, Maximilian C.; Karnick, David A.; Ponchak, George E.; Zorman, Christian A.

2011-01-01

In this investigation sputtered silicon carbide annealed at 300 C for one hour is used as a conformal thin film package. A RF magnetron sputterer was used to deposit 500 nm silicon carbide films on gold metal structures on alumina wafers. To determine the reliability and resistance to immersion in harsh environments, samples were submerged in gold etchant for 24 hours, in BOE for 24 hours, and in an O2 plasma etch for one hour. The adhesion strength of the thin film was measured by a pull test before and after the chemical immersion, which indicated that the film has an adhesion strength better than 10(exp 8) N/m2; this is similar to the adhesion of the gold layer to the alumina wafer. MIM capacitors are used to determine the dielectric constant, which is dependent on the SiC anneal temperature. Finally, to demonstrate that the SiC, conformal, thin film may be used to package RF circuits and sensors, an LC resonator circuit was fabricated and tested with and without the conformal SiC thin film packaging. The results indicate that the SiC coating adds no appreciable degradation to the circuits RF performance. Index Terms Sputter, silicon carbide, MIM capacitors, LC resonators, gold etchants, BOE, O2 plasma

Growth directions of C8-BTBT thin films during drop-casting

NASA Astrophysics Data System (ADS)

Iizuka, Naoki; Zanka, Tomohiko; Onishi, Yosuke; Fujieda, Ichiro

2016-02-01

Because charge transport in a single crystal is anisotropic, control of its orientation is important for enhancing electrical characteristics and reducing variations among devices. For growing an organic thin film, a solution process such as inkjet printing offers advantages in throughput. We have proposed to apply an external temperature gradient during drop-casting and to control the direction of solvent evaporation. In experiment, a temperature gradient was generated in a bare Si substrate by placing it on a Si plate bridging two heat stages. When a solution containing 2,7-dioctyl [1]benzothieno[3,2-b]benzothiophene (C8-BTBT) was dropped on the substrate, evaporation started at the hotter side of the droplet and proceeded toward the colder side. The front line of the liquid was not pinned and the solution extended toward the colder region. As a result, a thin film was formed in a 7mm-long region. The peripheral region of the film was significantly thicker due to the coffee ring effect. The surface of the rest of the film was mostly smooth and terrace structures with 2.6nm steps were observed. The step roughly corresponds to the length of the C8-BTBT molecule. The film thickness varied from 20nm to 50nm over the distance of 3mm. Another film was grown on a glass substrate under a similar condition. Observation of the film with a polarizing microscope revealed that fan-shaped domains were formed in the film and that their optical axes were mostly along the directions of the solvent evaporation.

Liquid-Phase Processing of Barium Titanate Thin Films

NASA Astrophysics Data System (ADS)

Harris, David Thomas

Processing of thin films introduces strict limits on the thermal budget due to substrate stability and thermal expansion mismatch stresses. Barium titanate serves as a model system for the difficulty in producing high quality thin films because of sensitivity to stress, scale, and crystal quality. Thermal budget restriction leads to reduced crystal quality, density, and grain growth, depressing ferroelectric and nonlinear dielectric properties. Processing of barium titanate is typically performed at temperatures hundreds of degrees above compatibility with metalized substrates. In particular integration with silicon and other low thermal expansion substrates is desirable for reductions in costs and wider availability of technologies. In bulk metal and ceramic systems, sintering behavior has been encouraged by the addition of a liquid forming second phase, improving kinetics and promoting densification and grain growth at lower temperatures. This approach is also widespread in the multilayer ceramic capacitor industry. However only limited exploration of flux processing with refractory thin films has been performed despite offering improved dielectric properties for barium titanate films at lower temperatures. This dissertation explores physical vapor deposition of barium titanate thin films with addition of liquid forming fluxes. Flux systems studied include BaO-B2O3, Bi2O3-BaB2O 4, BaO-V2O5, CuO-BaO-B2O3, and BaO-B2O3 modified by Al, Si, V, and Li. Additions of BaO-B2O3 leads to densification and an increase in average grain size from 50 nm to over 300 nm after annealing at 900 °C. The ability to tune permittivity of the material improved from 20% to 70%. Development of high quality films enables engineering of ferroelectric phase stability using residual thermal expansion mismatch in polycrystalline films. The observed shifts to TC match thermodynamic calculations, expected strain from the thermal expansion coefficients, as well as x-ray diffract measurements

Characterization of Cu2ZnSnS4 thin films prepared by photo-chemical deposition

NASA Astrophysics Data System (ADS)

Moriya, Katsuhiko; Watabe, Jyunichi; Tanaka, Kunihiko; Uchiki, Hisao

2006-09-01

Cu2ZnSnS4 (CZTS) thin films were prepared by post-annealing films of metal sulfides of Cu2S, ZnS and SnS2 precursors deposited on soda-lime glass substrates by photo-chemical deposition (PCD) from aqueous solution containing CuSO4, ZnSO4, SnSO4 and Na2S2O3. In this study, sulfurization was employed to prepare high quality CZTS thin films. Deposited films of metal sulfides were annealed in a furnace in an atmosphere of N2 or N2+H2S(5%) at the temperature of 300°, 400° or 500 °C. The sulfured films showed X-ray diffraction peaks from (112), (220), and (312) planes of CZTS and the peaks became sharp by an increase in the sulfurization temperature. CZTS thin film annealed in atmosphere of N2 was S-poor. After annealing atmosphere was changed from N2 into N2+H2S(5%), the decrease of a composi- tional ratio of sulfur could be suppressed.

Synthesis of thin films in boron-carbon-nitrogen ternary system by microwave plasma enhanced chemical vapor deposition

NASA Astrophysics Data System (ADS)

Kukreja, Ratandeep Singh

The Boron Carbon Nitorgen (B-C-N) ternary system includes materials with exceptional properties such as wide band gap, excellent thermal conductivity, high bulk modulus, extreme hardness and transparency in the optical and UV range that find application in most fields ranging from micro-electronics, bio-sensors, and cutting tools to materials for space age technology. Interesting materials that belong to the B-C-N ternary system include Carbon nano-tubes, Boron Carbide, Boron Carbon Nitride (B-CN), hexagonal Boron Nitride ( h-BN), cubic Boron Nitride (c-BN), Diamond and beta Carbon Nitride (beta-C3N4). Synthesis of these materials requires precisely controlled and energetically favorable conditions. Chemical vapor deposition is widely used technique for deposition of thin films of ceramics, metals and metal-organic compounds. Microwave plasma enhanced chemical vapor deposition (MPECVD) is especially interesting because of its ability to deposit materials that are meta-stable under the deposition conditions, for e.g. diamond. In the present study, attempt has been made to synthesize beta-carbon nitride (beta-C3N4) and cubic-Boron Nitride (c-BN) thin films by MPECVD. Also included is the investigation of dependence of residual stress and thermal conductivity of the diamond thin films, deposited by MPECVD, on substrate pre-treatment and deposition temperature. Si incorporated CNx thin films are synthesized and characterized while attempting to deposit beta-C3N4 thin films on Si substrates using Methane (CH4), Nitrogen (N2), and Hydrogen (H2). It is shown that the composition and morphology of Si incorporated CNx thin film can be tailored by controlling the sequence of introduction of the precursor gases in the plasma chamber. Greater than 100mum size hexagonal crystals of N-Si-C are deposited when Nitrogen precursor is introduced first while agglomerates of nano-meter range graphitic needles of C-Si-N are deposited when Carbon precursor is introduced first in the

Nanoporous structures on ZnO thin films

NASA Astrophysics Data System (ADS)

Gür, Emre; Kılıç, Bayram; Coşkun, C.; Tüzemen, S.; Bayrakçeken, Fatma

2010-01-01

Porous structures were formed on ZnO thin films which were grown by an electrochemical deposition (ECD) method. The growth processes were carried out in a solution of dimethylsulfoxide (DMSO) zinc perchlorate, Zn(ClO 4) 2, at 120 ∘C on indium tin oxide (ITO) substrates. Optical and structural characterizations of electrochemically grown ZnO thin films have shown that the films possess high (0002) c-axis orientation, high nucleation, high intensity and low FWHM of UV emission at the band edge region and a sharp UV absorption edge. Nanoporous structures were formed via self-assembled monolayers (SAMs) of hexanethiol (C 6SH) and dodecanethiol (C 12SH). Scanning electron microscope (SEM) measurements showed that while a nanoporous structure (pore radius 20 nm) is formed on the ZnO thin films by hexanathiol solution, a macroporous structure (pore radius 360 nm) is formed by dodecanethiol solution. No significant variation is observed in X-ray diffraction (XRD) measurements on the ZnO thin films after pore formation. However, photoluminescence (PL) measurements showed that green emission is observed as the dominant emission for the macroporous structures, while no variation is observed for the thin film nanoporous ZnO sample.

Sulvanite (Cu 3VS 4) nanocrystals for printable thin film photovoltaics

DOE PAGES

Chen, Ching -Chin; Stone, Kevin H.; Lai, Cheng -Yu; ...

2017-09-21

Copper Vanadium Sulfide (Cu 3VS 4), also known as sulvanite, has recently emerged as a suitable absorber material for thin film photovoltaics. The synthesis of Cu 3VS 4 nanocrystals via a rapid solvothermal route is reported for the first time. The phase purity of the Cu 3VS 4 nanocrystals has been confirmed by X-ray powder diffraction (XRD) and Raman spectroscopy, while the nanoparticle size, of about 10 nm, was evaluated by transmission electron microscopy (TEM). Successful ligand exchange with sulfide, an inorganic ligand, demonstrated that the nanoparticles are amenable to surface modifications, key element in solution processing. Further annealing ofmore » as-synthesized nanocrystals under a sulfur/argon atmosphere at 600 °C, rendered highly crystalline Cu 3VS 4 powders exhibiting an impurity that could be potentially mitigated by annealing temperature optimization. Furthermore, Cu 3VS 4, formed solely from Earth-abundant elements, could provide an inexpensive, reliable approach to fabricating solution processed thin film photovoltaic absorbers.« less

Sulvanite (Cu 3VS 4) nanocrystals for printable thin film photovoltaics

DOE Office of Scientific and Technical Information (OSTI.GOV)

Chen, Ching -Chin; Stone, Kevin H.; Lai, Cheng -Yu

Copper Vanadium Sulfide (Cu 3VS 4), also known as sulvanite, has recently emerged as a suitable absorber material for thin film photovoltaics. The synthesis of Cu 3VS 4 nanocrystals via a rapid solvothermal route is reported for the first time. The phase purity of the Cu 3VS 4 nanocrystals has been confirmed by X-ray powder diffraction (XRD) and Raman spectroscopy, while the nanoparticle size, of about 10 nm, was evaluated by transmission electron microscopy (TEM). Successful ligand exchange with sulfide, an inorganic ligand, demonstrated that the nanoparticles are amenable to surface modifications, key element in solution processing. Further annealing ofmore » as-synthesized nanocrystals under a sulfur/argon atmosphere at 600 °C, rendered highly crystalline Cu 3VS 4 powders exhibiting an impurity that could be potentially mitigated by annealing temperature optimization. Furthermore, Cu 3VS 4, formed solely from Earth-abundant elements, could provide an inexpensive, reliable approach to fabricating solution processed thin film photovoltaic absorbers.« less

Synthesis, characterization and oxidation of metallic cobalt (Co) thin film into semiconducting cobalt oxide (Co3O4)thin film using microwave plasma CVD

NASA Astrophysics Data System (ADS)

Rahman Ansari, Akhalakur; Hussain, Shahir; Imran, Mohd; Abdel-wahab, M. Sh; Alshahrie, Ahmed

2018-06-01

The pure cobalt thin film was deposited on the glass substrate by using DC magnetron sputtering and then exposed to microwave assist oxygen plasma generated in microwave plasma CVD. The oxidation process of Co thin film into Co3O4 thin films with different microwave power and temperature were studied. The influences of microwave power, temperature and irradiation time were investigated on the morphology and particle size of oxide thin films. The crystal structure, chemical conformation, morphologies and optical properties of oxidized Co thin films (Co3O4) were studied by using x-ray diffraction (XRD), Field emission scanning electron microscopy (FESEM), Raman Spectroscopy and UV–vis Spectroscopy. The data of these films showed complete oxidation pure metallic cobalt (Co) into cobalt oxide (Co3O4). The optical properties were studied for calculating the direct band gaps which ranges from 1.35 to 1.8 eV.

Effective vortex pinning in MgB2 thin films

NASA Astrophysics Data System (ADS)

Bugoslavsky, Y.; Cowey, L.; Tate, T. J.; Perkins, G. K.; Moore, J.; Lockman, Z.; Berenov, A.; MacManus-Driscoll, J. L.; Caplin, A. D.; Cohen, L. F.; Zhai, H. Y.; Christen, H. M.; Paranthaman, M. P.; Lowndes, D. H.; Jo, M. H.; Blamire, M. G.

2002-10-01

We discuss the pinning properties of MgB2 thin films grown by pulsed-laser deposition (PLD) and by electron-beam (EB) evaporation. Two mechanisms are identified that contribute most effectively to the pinning of vortices in randomly oriented films. The EB process produces low defected crystallites with a small grain size providing enhanced pinning at grain boundaries without any degradation of Tc. The PLD process produces films with structural disorder on a scale less than the coherence length that further improves pinning, but also depresses Tc.

Nanoporous Ca3Co4O9 Thin Films for Transferable Thermoelectrics

PubMed Central

2018-01-01

The development of high-performance and transferable thin-film thermoelectric materials is important for low-power applications, e.g., to power wearable electronics, and for on-chip cooling. Nanoporous films offer an opportunity to improve thermoelectric performance by selectively scattering phonons without affecting electronic transport. Here, we report the growth of nanoporous Ca3Co4O9 thin films by a sequential sputtering-annealing method. Ca3Co4O9 is promising for its high Seebeck coefficient and good electrical conductivity and important for its nontoxicity, low cost, and abundance of its constituent raw materials. To grow nanoporous films, multilayered CaO/CoO films were deposited on sapphire and mica substrates by rf-magnetron reactive sputtering from elemental Ca and Co targets, followed by annealing at 700 °C to form the final phase of Ca3Co4O9. This phase transformation is accompanied by a volume contraction causing formation of nanopores in the film. The thermoelectric propoperties of the nanoporous Ca3Co4O9 films can be altered by controlling the porosity. The lowest electrical resistivity is ∼7 mΩ cm, yielding a power factor of 2.32 × 10–4 Wm–1K–2 near room temperature. Furthermore, the films are transferable from the primary mica substrates to other arbitrary polymer platforms by simple dry transfer, which opens an opportunity of low-temperature use these materials. PMID:29905306

A comparative study of heterostructured CuO/CuWO4 nanowires and thin films

NASA Astrophysics Data System (ADS)

Polyakov, Boris; Kuzmin, Alexei; Vlassov, Sergei; Butanovs, Edgars; Zideluns, Janis; Butikova, Jelena; Kalendarev, Robert; Zubkins, Martins

2017-12-01

A comparative study of heterostructured CuO/CuWO4 core/shell nanowires and double-layer thin films was performed through X-ray diffraction, confocal micro-Raman spectroscopy and electron (SEM and TEM) microscopies. The heterostructures were produced using a two-step process, starting from a deposition of amorphous WO3 layer on top of CuO nanowires and thin films by reactive DC magnetron sputtering and followed by annealing at 650 °C in air. The second step induced a solid-state reaction between CuO and WO3 oxides through a thermal diffusion process, revealed by SEM-EDX analysis. Morphology evolution of core/shell nanowires and double-layer thin films upon heating was studied by electron (SEM and TEM) microscopies. A formation of CuWO4 phase was confirmed by X-ray diffraction and confocal micro-Raman spectroscopy.

Fabrication of luminescent SrWO{sub 4} thin films by a novel electrochemical method

DOE Office of Scientific and Technical Information (OSTI.GOV)

Chen Lianping; Gao Yuanhong

2007-10-02

Highly crystallized SrWO{sub 4} thin films with single scheelite structure were prepared within 60 min by a cell electrochemical method. X-ray diffraction analysis shows that SrWO{sub 4} thin films have a tetragonal structure. Scanning electron microscopy examinations reveal that SrWO{sub 4} grains grow well in tetragonal tapers and grains like flowers or bunches, which can usually form by using the electrolysis electrochemical method, have disappeared under cell electrochemical conditions. X-ray photoelectron spectra and energy dispersive X-ray microanalysis examinations demonstrate that the composition of the film is consistent with its stoichiometry. These SrWO{sub 4} films show a single blue emission peakmore » (located at 460 nm) using an excitation wave of 230 nm. The speed of cell electrochemical method can be controlled by changing temperature. The optimum treatment temperature is about 50-60 deg. C.« less

Cross-sectional TEM specimen preparation for W/B{sub 4}C multilayer sample using FIB

DOE Office of Scientific and Technical Information (OSTI.GOV)

Mondal, Puspen, E-mail: puspen@rrcat.gov.in; Pradhan, P. C.; Tiwari, Pragya

2016-05-23

A recent emergence of a cross-beam scanning electron microscopy (SEM)/focused-ion-beam (FIB) system have given choice to fabricate cross-sectional transmission electron microscopy (TEM) specimen of thin film multilayer sample. A 300 layer pair thin film multilayer sample of W/B{sub 4}C was used to demonstrate the specimen lift-out technique in very short time as compared to conventional cross-sectional sample preparation technique. To get large area electron transparent sample, sample prepared by FIB is followed by Ar{sup +} ion polishing at 2 kV with grazing incident. The prepared cross-sectional sample was characterized by transmission electron microscope.

Thin-film rechargeable lithium batteries

NASA Astrophysics Data System (ADS)

Dudney, N. J.; Bates, J. B.; Lubben, D.

1994-11-01

Small thin-film rechargeable cells have been fabricated with a lithium phosphorus oxynitride electrolyte, Li metal anode, and Li(1-x)Mn2O4 as the cathode film. The cathode films were fabricated by several different techniques resulting in both crystalline and amorphous films. These were compared by observing the cell discharge behavior. Estimates have been made for the scale-up of such a thin-film battery to meet the specifications for the electric vehicle application. The specific energy, energy density, and cycle life are expected to meet the USABC mid-term criteria. However, the areas of the thin-films needed to fabricate such a cell are very large. The required areas could be greatly reduced by operating the battery at temperatures near 100 C or by enhancing the lithium ion transport rate in the cathode material.

Highly stable, protein resistant thin films on SiC-modified silicon substrates.

PubMed

Qin, Guoting; Zhang, Rui; Makarenko, Boris; Kumar, Amit; Rabalais, Wayne; López Romero, J Manuel; Rico, Rodrigo; Cai, Chengzhi

2010-05-21

Thin films terminated with oligo(ethylene glycol) (OEG) could be photochemically grafted onto ultrathin silicon carbide layers that were generated on silicon substrates via carbonization with acetylene at 820 degrees C. The OEG coating reduced the non-specific adsorption of fibrinogen on the substrates by 99.5% and remained resistant after storage in PBS for 4 weeks at 37 degrees C.

Formation and photopatterning of nanoporous titania thin films

DOE Office of Scientific and Technical Information (OSTI.GOV)

Park, Oun-Ho; Cheng, Joy Y.; Kim, Hyun Suk

2007-06-04

Photopatternable nanoporous titania thin films were generated from mixtures of an organic diblock copolymer, poly(styrene-b-ethylene oxide) (PS-b-PEO), and an oligomeric titanate (OT) prepared from a chelated titanium isopropoxide. The PS-b-PEO templates well-defined microdomains in thin films of the mixtures, which upon thermal treatment at 450 deg. C, become nanopores in titania. Average pore size and porosity are controlled by the molecular weight and loading level of the PS-b-PEO, respectively. Patterns of nanoporous titania were created by selectively exposing UV light on the mixture films. The UV irradiation destroys the chelating bond and induces the cross-linking reaction of the OT. Subsequentmore » wet development followed by thermal treatment gives patterned nanoporous films of anatase phase titania.« less

Two-stage processed high-quality famatinite thin films for photovoltaics

NASA Astrophysics Data System (ADS)

Chalapathi, U.; Poornaprakash, B.; Cui, Hao; Park, Si-Hyun

2017-11-01

Famatinite (Cu3SbS4) thin films were prepared by annealing chemically grown Sb2S3-CuS stacks in a graphite box at 370-430 °C for 30 min under sulfur and N2 atmospheres. The films grown at 370 °C contain a minor CuSbS2 phase with dominant Cu3SbS4. Those films prepared at 400 °C and 430 °C are single-phase Cu3SbS4 with a tetragonal structure and lattice parameters a = 0.537 nm and b = 1.087 nm and a crystallite size of 25 nm. The grain size of the films increases as the annealing temperature is increased to 400 °C and subsequently decreases. The film morphology is compact and void-free with a grain size of 300-800 nm at 400 °C. The band gap of the films is 0.89 eV. The films exhibited p-type electrical conductivity and a relatively high hole mobility of 14.70 cm2V-1s-1 at 400 °C. Their attractive optoelectronic properties suggest that these films are suitable as solar cell absorber layers.

Growth and characterization of ultra thin vanadium oxide films

NASA Astrophysics Data System (ADS)

Song, Fangfang

This dissertation focuses on the growth and characterization of ultra thin VO2 films on technologically relevant Si/SiO2 substrate. The samples were prepared by magnetron sputtering with varying deposition and post annealing conditions. VO2(M1) films prepared under optimal condition with thickness around 42nm shows a continuous micro-structure and a metal insulator transition with resistivity change of two orders of magnitude. The transition temperature is determined to be 345K with a hysteresis width of approximately 8°C. The activation energy of the low temperature semiconducting VO2 monoclinic phase is determined to be 0.16+/-0.03ev. These properties are found to be fairly stable over time under ambient atmosphere. Temperature dependent hall measurements suggest that the decrease of the resistivity with increasing temperature is mainly caused by the increase of the number density of charge carriers, the energy gap of VO2 film in the semiconducting phase is 0.4ev and phonon scattering is the dominant scattering mechanism in the temperature range from 195K to 340K. Analysis based on composite model suggested that the sample has some untransitional phases with a length that is 1/4 of the grain size. Stress measurements using X-ray diffraction indicate that the ultra thin VO2 film has a large tensile stress of 2.0+/-0.2GPa. This value agrees well with that calculated thermal stress assuming the stress is due to differential thermal expansion between VO2 film and substrate. The stress is expected to lead to a shift of the transition temperature in the film, as observed. Using magnetron sputtering, VO2(B) film was able to obtained on Si substrate. The temperature dependent current voltage measurement on VO2(B) film did not show any abrupt change in the electrical resistivity. W - VO2(B) thin film - W metal semiconductor-metal I-V properties were found to be determined by reverse biased Schottky barrier at the W/VO 2(b) interface. And the Schottky height between VO2(B

Preparation and microstructural characterization of TiC and Ti{sub 0.6}W{sub 0.4}/TiC{sub 0.6} composite thin films obtained by activated reactive evaporation

DOE Office of Scientific and Technical Information (OSTI.GOV)

Montes de Oca, J. A.; LePetitcorps, Y.; Manaud, J.-P.

2008-05-15

Titanium carbide-based coatings were deposited on W substrates at a high coating growth rate by activated reactive evaporation at 500 and 600 deg. C in a L560 Leybold system using propene as reactive atmosphere. The crystal structure, lattice parameter, preferred orientation, and grain size of the coatings were determined by x-ray diffraction technique using Cu K{alpha}. The analysis of the coating morphology was performed by scanning electron microscopy (SEM), and the composition of the films was analyzed by Auger electron spectroscopy and electron-probe microanalysis. Experimental results suggested that temperature was one of the most important parameters in the fabrication ofmore » stoichiometric TiC coatings. Thus, TiC coatings were obtained at 600 deg. C, whereas TiC{sub 0.6} nonstoichiometric coatings codeposited with a free Ti phase were obtained at 500 deg. C, giving rise to the formation of a composite thin film. After annealing at 1000 deg. C, the stoichiometric films remained stable, but a crack pattern was formed over the entire coating surface. In addition, Ti{sub 0.6}W{sub 0.4}/TiC{sub 0.6} composite thin coatings were obtained for the films synthesized at 500 deg. C. The formation of a Ti{sub 0.6}W{sub 0.4} ductile phase in the presence of a TiC{sub 0.6} phase was responsible to avoid the coating cracking.« less

Electrical and optical properties of C46H22N8O4KM (M=Co, Fe, Pb) molecular-material thin films prepared by the vacuum thermal evaporation technique.

PubMed

Sánchez-Vergara, M E; Ruiz Farfán, M A; Alvarez, J R; Ponce Pedraza, A; Ortiz, A; Alvarez Toledano, C

2007-03-01

In this work, the synthesis of new materials formed from metallic phthalocyanines (Pcs) and double potassium salt from 1,8-dihydroxianthraquinone is reported. The newly synthesized materials were characterized by scanning electron microscope (SEM), atomic force microscopy (AFM), infrared (IR) and Ultraviolet-visible (UV-vis) spectroscopy. The powder and thin-film samples of the synthesized materials, deposited by vacuum thermal evaporation, show the same intra-molecular bonds as in the IR spectroscopy studies, which suggests that the thermal evaporation process does not alter these bonds. The effect of temperature on conductivity and electrical conduction mechanism was measured in the thin films (approximately 137 nm thickness). They showed a semiconductor-like behaviour with an optical activation energy arising from indirect transitions of 2.15, 2.13 and 3.6eV for the C(46)H(22)N(8)O(4)KFe, C(46)H(22)N(8)O(4)KPb and C(46)H(22)N(8)O(4)KCo thin films.

Dewetting of Thin Polymer Films

NASA Astrophysics Data System (ADS)

Dixit, P. S.; Sorensen, J. L.; Kent, M.; Jeon, H. S.

2001-03-01

DEWETTING OF THIN POLYMER FILMS P. S. Dixit,(1) J. L. Sorensen,(2) M. Kent,(2) H. S. Jeon*(1) (1) Department of Petroleum and Chemical Engineering, New Mexico Institute of Mining and Technology, 801 Leroy Place, Socorro, NM 87801, jeon@nmt.edu (2) Department 1832, Sandia National Laboratories, Albuquerque, NM. Dewetting of thin polymer films is of technological importance for a variety of applications such as protective coatings, dielectric layers, and adhesives. Stable and smooth films are required for the above applications. Above the glass transition temperature (Tg) the instability of polymer thin films on a nonwettable substrate can be occurred. The dewetting mechanism and structure of polypropylene (Tg = -20 ^circC) and polystyrene (Tg = 100 ^circC) thin films is investigated as a function of film thickness (25 Åh < 250 Åand quenching temperature. Contact angle measurements are used in conjunction with optical microscope to check the surface homogeneity of the films. Uniform thin films are prepared by spin casting the polymer solutions onto silicon substrates with different contact angles. We found that the stable and unstable regions of the thin films as a function of the film thickness and quenching temperature, and then constructed a stability diagram for the dewetting of thin polymer films. We also found that the dewetting patterns of the thin films are affected substantially by the changes of film thickness and quenching temperature.

The order-to-disorder transition behavior of PS-b-P2VP thin film system

NASA Astrophysics Data System (ADS)

Ahn, Hyungju; Ryu, Du

2013-03-01

We investigated the transition behavior such as the order-to-disorder transition (ODT) for symmetric poly(styrene)-block-poly(2-vinly pridine) (PS-b-P2VP) using SAXS and GISAXS for block copolymer bulks and films. The bulk transition temperature of PS-b-P2VP was significantly influenced by the interfacial interactions in thin films, leading to the different transition temperature. From these results, we will discuss about the interfacial interaction effects on the phase behaviors in bulks and thin films system of PS-b-P2VP.

Characterization of ALD grown TixAlyN and TixAlyC thin films

NASA Astrophysics Data System (ADS)

Kinnunen, S. A.; Malm, J.; Arstila, K.; Lahtinen, M.; Sajavaara, T.

2017-09-01

Atomic layer deposition (ALD) was used to grow TixAlyN and TixAlyC thin films using trimethylaluminum (TMA), titanium tetrachloride and ammonia as precursors. Deposition temperature was varied between 325 °C and 500 °C. Films were also annealed in vacuum and N2-atmosphere at 600-1000 °C. Wide range of characterization methods was used including time-of-flight elastic recoil detection analysis (ToF-ERDA), X-ray diffractometry (XRD), X-ray reflectometry (XRR), Raman spectroscopy, ellipsometry, helium ion microscopy (HIM), atomic force microscopy (AFM) and 4-point probe measurement for resistivity. Deposited films were roughly 100 nm thick and contained mainly desired elements. Carbon, chlorine and hydrogen were found to be the main impurities.

Optical and mechanical properties of nanocrystalline ZrC thin films grown by pulsed laser deposition.

DOE PAGES

Craciun, D.; Socol, G.; Lambers, E.; ...

2015-01-17

Thin ZrC films (<500 nm) were grown on (100) Si substrates at a substrate temperature of 500 °C by the pulsed laser deposition (PLD) technique using a KrF excimer laser under different CH 4 pressures. Glancing incidence X-ray diffraction showed that films were nanocrystalline, while X-ray reflectivity studies found out films were very dense and exhibited a smooth surface morphology. Optical spectroscopy data shows that the films have high reflectivity (>90%) in the infrared region, characteristic of metallic behavior. Nanoindentation results indicated that films deposited under lower CH 4 pressures exhibited slightly higher nanohardness and Young modulus values than filmsmore » deposited under higher pressures. As a result, tribological characterization revealed that these films exhibited relatively high wear resistance and steady-state friction coefficients on the order of μ = 0.4.« less

Femtosecond pulsed laser deposition of amorphous, ultrahard boride thin films

NASA Astrophysics Data System (ADS)

Stock, Michael; Molian, Pal

2004-05-01

Amorphous thin films (300-500 nm) of ultrahard AlMgB10 with oxygen and carbon impurities were grown on Si (100) substrates at 300 K using a solid target of AlMgB14 containing a spinel phase (MgAl2O4) and using a 120 fs pulsed, 800 nm wavelength Ti:sapphire laser. The films were subsequently annealed in argon gas up to 1373 K for 2 h. Scanning electron microscopy (SEM) was used to examine the particulate formation, atomic force microscopy was employed to characterize the film surface topography, x-ray diffraction and transmission electron microscopy were used to determine the microstructure, x-ray photoelectron spectroscopy was performed to examine the film composition, and nanoindentation was employed to study the hardness of thin films. The as-deposited and postannealed films (up to 1273 K) had a stochiometry of AlMgB10 with a significant amount of oxygen and carbon impurities and exhibited amorphous structures for a maximum hardness of 40+/-3 GPa. However, postannealing at higher temperatures led to crystallization and transformation of the film to SiB6 with a substantial loss in hardness. Results are also compared with our previous study on 23 ns, 248 nm wavelength (KrF excimer) pulsed laser deposition of AlMgB14 reported in this journal [Y. Tian, A. Constant, C. C. H. Lo, J. W. Anderegg, A. M. Russell, J. E. Snyder, and P. A. Molian, J. Vac. Sci. Technol. A 21, 1055 (2003)]. .

Development of hot-electron THz bolometric mixers using MgB2 thin films

NASA Astrophysics Data System (ADS)

Cunnane, Daniel; Kawamura, Jonathan; Karasik, Boris S.; Wolak, Matthaeus A.; Xi, X. X.

2014-07-01

Terahertz high-resolution spectroscopy of interstellar molecular clouds greatly relies on hot-electron superconducting bolometric (HEB) mixers. Current state-of-the-art receivers use mixer devices made from ultrathin (~ 3-5 nm) films of NbN with critical temperature ~ 9-11 K. Such mixers have been deployed on a number of groundbased, suborbital, and orbital platforms including the HIFI instrument on the Hershel Space Observatory. Despite its good sensitivity and well-established fabrication process, the NbN HEB mixer suffers from the narrow intermediate frequency (IF) bandwidth ~ 2-3 GHz and is limited to operation at liquid Helium temperature. As the heterodyne receivers are now trending towards "high THz" frequencies, the need in a larger IF bandwidth becomes more pressing since the same velocity resolution for a Doppler shifted line at 5 THz requires a 5-times greater IF bandwidth than at 1 THz. Our work is focusing on the realization of practical HEB mixers using ultrathin (10-20 nm) MgB2 films. They are prepared using a Hybrid Physical-Chemical Vapor Deposition (HPCVD) process yielding ultrathin films with critical temperature ~ 37-39 K. The expectation is that the combination of small thickness, high acoustic phonon transparency at the interface with the substrate, and very short electron-phonon relaxation time may lead to IF bandwidth ~ 10 GHz or even higher. SiC continues to be the most favorable substrate for MgB2 growth and as a result, a study has been conducted on the transparency of SiC at THz frequencies. FTIR measurements show that semi-insulating SiC substrates are at least as transparent as Si up to 2.5 THz. Currently films are passivated using a thin (10 nm) SiO2 layer which is deposited ex-situ via RF magnetron sputtering. Micron-sized spiral antenna-coupled HEB mixers have been fabricated using MgB2 films as thin as 10 nm. Fabrication was done using contact UV lithography and Ar Ion milling, with E-beam evaporated Au films deposited for the

X-ray structural investigation of nonsymmetrically and symmetrically alkylated [1]benzothieno[3,2-b]benzothiophene derivatives in bulk and thin films.

PubMed

Gbabode, Gabin; Dohr, Michael; Niebel, Claude; Balandier, Jean-Yves; Ruzié, Christian; Négrier, Philippe; Mondieig, Denise; Geerts, Yves H; Resel, Roland; Sferrazza, Michele

2014-08-27

A detailed structural study of the bulk and thin film phases observed for two potential high-performance organic semiconductors has been carried out. The molecules are based on [1]benzothieno[3,2-b]benzothiophene (BTBT) as conjugated core and octyl side groups, which are anchored either symmetrically at both sides of the BTBT core (C8-BTBT-C8) or nonsymmetrically at one side only (C8-BTBT). Thin films of different thickness (8-85 nm) have been prepared by spin-coating for both systems and analyzed by combining specular and grazing incidence X-ray diffraction. In the case of C8-BTBT-C8, the known crystal structure obtained from single-crystal investigations is observed within all thin films, down to a film thickness of 9 nm. In the case of C8-BTBT, the crystal structure of the bulk phase has been determined from X-ray powder diffraction data with a consistent matching of experimental and calculated X-ray diffraction patterns (Rwp = 5.8%). The packing arrangement of C8-BTBT is similar to that of C8-BTBT-C8, that is, consisting of a lamellar structure with molecules arranged in a "herringbone" fashion, yet with lamellae composed of two head-to-head (or tail-to-tail as the structure is periodic) superimposed molecules instead of only one molecule for C8-BTBT-C8. As for C8-BTBT-C8, we demonstrate that the same phase is observed in bulk and thin films for C8-BTBT whatever the film thickness investigated.

Thin Films

NASA Astrophysics Data System (ADS)

Khorshidi, Zahra; Bahari, Ali; Gholipur, Reza

2014-11-01

Effect of annealing temperature on the characteristics of sol-gel-driven Ta ax La(1- a) x O y thin film spin-coated on Si substrate as a high- k gate dielectric was studied. Ta ax La(1- a) x O y thin films with different amounts of a were prepared (as-prepared samples). X-ray diffraction measurements of the as-prepared samples indicated that Ta0.3 x La0.7 x Oy film had an amorphous structure. Therefore, Ta0.3 x La0.7 x O y film was chosen to continue the present studies. The morphology of Ta0.3 x La0.7 x O y films was studied using scanning electron microscopy and atomic force microscopy techniques. The obtained results showed that the size of grain boundaries on Ta0.3 x La0.7 x O y film surfaces was increased with increasing annealing temperature. Electrical and optical characterizations of the as-prepared and annealed films were investigated as a function of annealing temperature using capacitance-voltage ( C- V) and current density-voltage ( J- V) measurements and the Tauc method. The obtained results demonstrated that Ta0.3 x La0.7 x O y films had high dielectric constant (≈27), wide band gap (≈4.5 eV), and low leakage current density (≈10-6 A/cm2 at 1 V).

Thermosensitive block copolymer [(PNIPAM)-b-(Glycine)] thin film as protective layer for drug loaded mesoporous silica nanoparticles

NASA Astrophysics Data System (ADS)

Amgoth, Chander; Joshi, Suman

2017-10-01

Synthesis and characterization of [(PNIPAM)-b-(Gly)] and mesoporous silica nanoparticles (MP-SiO2 NPs) were carried out separately and used to develop [(PNIPAM)-b-(Gly)]-(MP-SiO2 NPs). The synthesized MP-SiO2 NPs were meso porous in nature. The size of SiO2 NPs is in the range of ~180-250 nm (in diameter) with an average pore size of 2.8 nm within the particles. Interestingly, these mesoporous SiO2 NPs were loaded with anticancer drug (ITM-imatinib mesylate) fallow by the incubation for 24 h at RT. However, ITM loaded MP-SiO2 NPs were capped or covered with synthesized [(PNIPAM)-b-(Gly)] thin film. Here, thin film acts as protective layer for drug loaded MP-SiO2 NPs, with that leakage of drug molecules throughout its transport pathway can be avoided. Significantly, thermosensitive [(PNIPAM)-b-(Gly)] polymer thin film depletes at body temperature (~37 °C) and drug molecules come out from the pores of SiO2 NPs. However, developed [(PNIPAM)-b-(Gly)]-(MP-SiO2 NPs) is compatible and used for cell inhibition studies. After 24 h treatment, drug ITM released from [(PNIPAM)-b-(Gly)]-(MP-SiO2 NPs) shows significant (>90%) inhibition on leukemia blood cancer (K562) cells.

Structurally-driven Enhancement of Thermoelectric Properties within Poly(3,4-ethylenedioxythiophene) thin Films

PubMed Central

Petsagkourakis, Ioannis; Pavlopoulou, Eleni; Portale, Giuseppe; Kuropatwa, Bryan A.; Dilhaire, Stefan; Fleury, Guillaume; Hadziioannou, Georges

2016-01-01

Due to the rising need for clean energy, thermoelectricity has raised as a potential alternative to reduce dependence on fossil fuels. Specifically, thermoelectric devices based on polymers could offer an efficient path for near-room temperature energy harvesters. Thus, control over thermoelectric properties of conducting polymers is crucial and, herein, the structural, electrical and thermoelectric properties of poly(3,4-ethylenedioxythiophene) (PEDOT) thin films doped with p-toluenesulfonate (Tos) molecules were investigated with regards to thin film processing. PEDOT:Tos thin films were prepared by in-situ polymerization of (3,4-ethylenedioxythiophene) monomers in presence of iron(III) p-toluenesulfonate with different co-solvents in order to tune the film structure. While the Seebeck coefficient remained constant, a large improvement in the electrical conductivity was observed for thin films processed with high boiling point additives. The increase of electrical conductivity was found to be solely in-plane mobility-driven. Probing the thin film structure by Grazing Incidence Wide Angle X-ray Scattering has shown that this behavior is dictated by the structural properties of the PEDOT:Tos films; specifically by the thin film crystallinity combined to the preferential edge-on orientation of the PEDOT crystallites. Consequentially enhancement of the power factor from 25 to 78.5 μW/mK2 has been readily obtained for PEDOT:Tos thin films following this methodology. PMID:27470637

Structurally-driven Enhancement of Thermoelectric Properties within Poly(3,4-ethylenedioxythiophene) thin Films.

PubMed

Petsagkourakis, Ioannis; Pavlopoulou, Eleni; Portale, Giuseppe; Kuropatwa, Bryan A; Dilhaire, Stefan; Fleury, Guillaume; Hadziioannou, Georges

2016-07-29

Due to the rising need for clean energy, thermoelectricity has raised as a potential alternative to reduce dependence on fossil fuels. Specifically, thermoelectric devices based on polymers could offer an efficient path for near-room temperature energy harvesters. Thus, control over thermoelectric properties of conducting polymers is crucial and, herein, the structural, electrical and thermoelectric properties of poly(3,4-ethylenedioxythiophene) (PEDOT) thin films doped with p-toluenesulfonate (Tos) molecules were investigated with regards to thin film processing. Tos thin films were prepared by in-situ polymerization of (3,4-ethylenedioxythiophene) monomers in presence of iron(III) p-toluenesulfonate with different co-solvents in order to tune the film structure. While the Seebeck coefficient remained constant, a large improvement in the electrical conductivity was observed for thin films processed with high boiling point additives. The increase of electrical conductivity was found to be solely in-plane mobility-driven. Probing the thin film structure by Grazing Incidence Wide Angle X-ray Scattering has shown that this behavior is dictated by the structural properties of the Tos films; specifically by the thin film crystallinity combined to the preferential edge-on orientation of the PEDOT crystallites. Consequentially enhancement of the power factor from 25 to 78.5 μW/mK(2) has been readily obtained for Tos thin films following this methodology.

Liquid crystals for organic thin-film transistors

NASA Astrophysics Data System (ADS)

Iino, Hiroaki; Usui, Takayuki; Hanna, Jun-Ichi

2015-04-01

Crystalline thin films of organic semiconductors are a good candidate for field effect transistor (FET) materials in printed electronics. However, there are currently two main problems, which are associated with inhomogeneity and poor thermal durability of these films. Here we report that liquid crystalline materials exhibiting a highly ordered liquid crystal phase of smectic E (SmE) can solve both these problems. We design a SmE liquid crystalline material, 2-decyl-7-phenyl-[1]benzothieno[3,2-b][1]benzothiophene (Ph-BTBT-10), for FETs and synthesize it. This material provides uniform and molecularly flat polycrystalline thin films reproducibly when SmE precursor thin films are crystallized, and also exhibits high durability of films up to 200 °C. In addition, the mobility of FETs is dramatically enhanced by about one order of magnitude (over 10 cm2 V-1 s-1) after thermal annealing at 120 °C in bottom-gate-bottom-contact FETs. We anticipate the use of SmE liquid crystals in solution-processed FETs may help overcome upcoming difficulties with novel technologies for printed electronics.

Properties of Nanocrystalline Cubic Silicon Carbide Thin Films Prepared by Hot-Wire Chemical Vapor Deposition Using SiH4/CH4/H2 at Various Substrate Temperatures

NASA Astrophysics Data System (ADS)

Tabata, Akimori; Komura, Yusuke; Hoshide, Yoshiki; Narita, Tomoki; Kondo, Akihiro

2008-01-01

Silicon carbide (SiC) thin films were prepared by hot-wire chemical vapor deposition from SiH4/CH4/H2 gases, and the influence of substrate temperature, Ts (104 < Ts < 434 °C), on the properties of the SiC thin films was investigated. X-ray diffraction patterns and Raman scattering spectra revealed that nanocrystalline cubic SiC (nc-3C-SiC) films grew at Ts above 187 °C, while completely amorphous films grew at Ts = 104 °C. Fourier transform infrared absorption spectra revealed that the crystallinity of the nc-3C-SiC was improved with increasing Ts up to 282 °C and remained almost unchanged with a further increase in Ts from 282 to 434 °C. The spin density was reduced monotonically with increasing Ts.

GaN thin films growth and their application in photocatalytic removal of sulforhodamine B from aqueous solution under UV pulsed laser irradiation.

PubMed

Gondal, Mohammed A; Chang, Xiao F; Yamani, Zain H; Yang, Guo F; Ji, Guang B

2011-01-01

Single-crystalline Gallium Nitride (GaN) thin films were fabricated and grown by metal organic chemical vapor deposition (MOCVD) method on c-plane sapphire substrates and then characterized by high resolution-X-ray diffraction (HR-XRD) and photoluminescence (PL) measurements. The photocatalytic decomposition of Sulforhodamine B (SRB) molecules on GaN thin films was investigated under 355 nm pulsed UV laser irradiation. The results demonstrate that as-grown GaN thin films exhibited efficient degradation of SRB molecules and exhibited an excellent photocatalytic-activity-stability under UV pulsed laser exposure.

Dewetting behavior of polystyrene film filled with (C6H5C2H4NH3)2PbI4

NASA Astrophysics Data System (ADS)

Xue, Longjian; Cheng, Ziyong; Fu, Jun; Han, Yanchun

2008-08-01

The dewetting behavior of thin (about 30 nm) polystyrene (PS) films filled with different amount of (C6H5C2H4NH3)2PbI4 (PhE-PbI4) on the silicon substrate with a native oxide layer was investigated. For different additive concentrations, PhE-PbI4 showed different spatial distributions in the PS films, which had a strong influence on the film wettability, dewetting dynamics, and mechanism. With 0.5 wt % additive, PhE-PbI4 formed a noncontinuous diffusion layer, which caused a continuous hole nucleation in the film. With about 1 wt % additive, a continuous gradient distribution layer of PhE-PbI4 formed in the film, which inhibited the dewetting. When the concentration is higher (2 wt %), large PhE-PbI4 aggregates, in addition to the PhE-PbI4 continuous layer, formed in the film. These large aggregates (larger than radius of gyration of PS) migrated to the interface, resulting in the hole nucleation and eventually the complete dewetting of the film.

Optical and structural properties of sputtered CdS films for thin film solar cell applications

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kim, Donguk; Park, Young; Kim, Minha

2015-09-15

Graphical abstract: Photo current–voltage curves (a) and the quantum efficiency (QE) (b) for the solar cell with CdS film grown at 300 °C. - Highlights: • CdS thin films were grown by a RF magnetron sputtering method. • Influence of growth temperature on the properties of CdS films was investigated. • At higher T{sub g}, the crystallinity of the films improved and the grains enlarged. • CdS/CdTe solar cells with efficiencies of 9.41% were prepared at 300 °C. - Abstract: CdS thin films were prepared by radio frequency magnetron sputtering at various temperatures. The effects of growth temperature on crystallinity,more » surface morphology and optical properties of the films were characterized with X-ray diffraction (XRD), field emission scanning electron microscopy (FESEM), Raman spectra, UV–visible spectrophotometry, and photoluminescence (PL) spectra. As the growth temperature was increased, the crystallinity of the sputtered CdS films was improved and the grains were enlarged. The characteristics of CdS/CdTe thin film solar cell appeared to be significantly influenced by the growth temperature of the CdS films. Thin film CdS/CdTe solar cells with efficiencies of 9.41% were prepared at a growth temperature of 300 °C.« less

Multifunctional Parylene-C Microfibrous Thin Films

NASA Astrophysics Data System (ADS)

Chindam, Chandraprakash

Towards sustainable development, multifunctional products have many advantageous over single-function products: reduction in number of parts, raw material, assembly time, and cost involved in a product's life cycle. My goal for this thesis was to demonstrate the multifunctionalities of Parylene-C microfibrous thin films. To achieve this goal, I chose Parylene C, a polymer, because the fabrication of periodic mediums of Parylene C in the form of microfibrous thin films (muFTFs) was already established. A muFTFs is a parallel arrangement of identical micrometer-sized fibers of shapes cylindrical, chevronic, or helical. Furthermore, Parylene C had three existing functions: in medical-device industries as corrosion-resistive coatings, in electronic industries as electrically insulating coatings, and in biomedical research for tissue-culture substrates. As the functionalities of a material are dependent on the microstructure and physical properties, the investigation made for this thesis was two-fold: (1) Experimentally, I determined the wetting, mechanical, and dielectric properties of columnar muFTFs and examined the microstructural and molecular differences between bulk films and muFTFs. (2) Using physical properties of bulk film, I computationally determined the elastodynamic and determined the electromagnetic filtering capabilities of Parylene-C muFTFs. Several columnar muFTFs of Parylene C were fabricated by varying the monomer deposition angle. Following are the significant experimental findings: 1. Molecular and microstructural characteristics: The dependence of the microfiber inclination angle on the monomer deposition angle was classified into four regimes of two different types. X-ray diffraction experiments indicated that the columnar muFTFs contain three crystal planes not evident in bulk Parylene-C films and that the columnar muFTFs are less crystalline than bulk films. Infrared absorbance spectra revealed that the atomic bonding is the same in all

Ionic Self-Assembled Monolayer (ISAM) Nonlinear Optical Thin Films and Devices

DTIC Science & Technology

1998-05-12

SUBTITLE " Ionic Self-Assembled Monolayer (ISAM) Nonlinear Optical Thin Films and Devices" 6. AUTHORS Michael B. Miller 5. FUNDING NUMBERS F49620-97...ii. Lü. Ionic Self-Assembled Monolayer (ISAM) Nonlinear Optical Thin Films and Devices Final Technical Report Performance Period: 15 August 1997...Investigator F&S. Inc.N ̂ 1. INTRODUCTION .’ 2 2. PROGRAM TASK REVIEW 2 3. BACKGROUND 4 3.1 NONLINEAR OPTICAL THIN FILMS 4 3.2 IONIC SELF

Photoluminescence spectra of thin films of ZnTPP–C{sub 60} and CuTPP–C{sub 60} molecular complexes

DOE Office of Scientific and Technical Information (OSTI.GOV)

Elistratova, M. A., E-mail: marina.elistratova@mail.ioffe.ru; Zakharova, I. B.; Romanov, N. M.

2016-09-15

The results of studies of thin composite films of zinc and copper tetraphenylporphyrins with different fractions of fullerene C{sub 60} are reported. The photoluminescence spectra are recorded, and the composition and surface morphology are analyzed by means of scanning electron microscopy. The results show a difference in the structure of films with two types of metals (Zn, Cu) entering into the complex of the porphyrin macrocycle. An additional long-wavelength photoluminescence band at 1.4 eV is detected for the first time, which is evidence of the formation of ZnTPP–C{sub 60} molecular complexes from a gas-dynamic vapor flow upon condensation. In CuTPPmore » thin films, the processes of self-assembly into nanowires 20 nm in diameter and up to 50 µm in length and the formation of nanoheterojunctions upon the addition of fullerene C{sub 60} are observed. Quantum-chemical calculations in the context of density-functional theory are carried out to interpret the experimental data.« less

Multi-jump magnetic switching in ion-beam sputtered amorphous Co{sub 20}Fe{sub 60}B{sub 20} thin films

DOE Office of Scientific and Technical Information (OSTI.GOV)

Raju, M.; Chaudhary, Sujeet; Pandya, D. K.

2013-08-07

Unconventional multi-jump magnetization reversal and significant in-plane uniaxial magnetic anisotropy (UMA) in the ion-beam sputtered amorphous Co{sub 20}Fe{sub 60}B{sub 20}(5–75 nm) thin films grown on Si/amorphous SiO{sub 2} are reported. While such multi-jump behavior is observed in CoFeB(10 nm) film when the magnetic field is applied at 10°–20° away from the easy-axis, the same is observed in CoFeB(12.5 nm) film when the magnetic field is 45°–55° away from easy-axis. Unlike the previous reports of multi-jump switching in epitaxial films, their observance in the present case of amorphous CoFeB is remarkable. This multi-jump switching is found to disappear when the filmsmore » are crystallized by annealing at 420 °C. The deposition geometry and the energy of the sputtered species appear to intrinsically induce a kind of bond orientation anisotropy in the films, which leads to the UMA in the as-grown amorphous CoFeB films. Exploitation of such multi-jump switching in amorphous CoFeB thin films could be of technological significance because of their applications in spintronic devices.« less

Optimization of high quality Cu2ZnSnS4 thin film by low cost and environment friendly sol-gel technique for thin film solar cells applications

NASA Astrophysics Data System (ADS)

Chaudhari, J. J.; Joshi, U. S.

2018-05-01

In this study kesterite Cu2ZnSnS4 (CZTS) thin films suitable for absorber layer in thin film solar cells (TFSCs) were successfully fabricated on glass substrate by sol-gel method. The effects of complexing agent on formation of CZTS thin films have been investigated. X-ray diffraction (XRD) analysis confirms formation of polycrystalline CZTS thin films with single phase kesterite structure. XRD and Raman spectroscopy analysis of CZTS thin films with optimized concentration of complexing agent confirmed formation of kesterite phase in CZTS thin films. The direct optical band gap energy of CZTS thin films is found to decrease from 1.82 to 1.50 eV with increase of concentration of complexing agent triethanolamine. Morphological analysis of CZTS thin films shows smooth, uniform and densely packed CZTS grains and increase in the grain size with increase of concentration of complexing agent. Hall measurements revealed that concentration of charge carrier increases and resistivity decreases in CZTS thin films as amount of complexing agent increases.

An Electrostatically Self-Assembled Thin Film Made of Zn-Substituted Tungstoborate and Rhodamine B with Photoelectrochemical Properties.

PubMed

Mao, Xu; Zhang, Jia-Ning; Gao, Li-Hua; Su, Yu; Chen, Peng-Xia; Wang, Ke-Zhi

2016-04-01

An electrostatically self-assembled multilayer thin film consisting of alternating layers of Keggin polyoxometalate of Zn-substituted tungstoborate (BW11Zn) and Rhodamine B (RhB) has successfully been prepared on a quartz and indium-tin oxide (ITO) glass substrate. The ultraviolet-visible (UV-vis) absorption spectra demonstrated that the electrostatically self-assembled film of (BW11Zn/RhB)n was uniformly deposited layer by layer, and the RhB molecules in the film formed the J-aggregation. The photoelectrochemical investigations showed that the films generated stable cathodic photocurrents that originated from RhB, and the maximal cathodic photocurrent density generated by an eight-layer film was 4.9 µA/cm2 while the film was irradiated with 100 mW/cm2 polychromatic light of 730 nm > λ > 325 nm at an applied potential of 0 V versus a saturated calomel electrode.

Atomic structures of B20 FeGe thin films grown on the Si(111) surface

NASA Astrophysics Data System (ADS)

Kim, Wondong; Noh, Seungkyun; Yoon, Jisoo; Kim, Young Heon; Lee, Inho; Kim, Jae-Sung; Hwang, Chanyong

We investigated the growth and atomic structures of FeGe thin films on the Si (111) surface by using scanning tunneling microscopy (STM) and transmission electron microscopy (TEM). The 2 5nm- thick FeGe thin films were prepared on the clean Si(111) 7x7 surface by co-deposition of Fe and Ge from separated electron-beam evaporators. With direct deposition on the substrate at the temperature above 550 K, the surface of FeGe films was not smooth and consisted of coarse grains. By the combination of room-temperature annealing and post-annealing process around 800 K, the structure of FeGe thin films evolved into the well crystalized structures. Atom-resolved STM images revealed that there are at least four different surface terminations. We constructed atomic models for each surface terminations based on the bulk atomic arrangement of a B20 chiral structure and confirmed that the observed STM images are successfully reproduced by using computational simulations employing Vienna Ab Initio Simulation package (VASP) with a B20 chiral structure model. TEM cross-sectional images also support our atomic models by revealing clearly the characteristic zigzag features of B20 structures of FeGe(111) thin films.

Experimental analysis of silicon oxycarbide thin films and waveguides

NASA Astrophysics Data System (ADS)

Memon, Faisal Ahmed; Morichetti, Francesco; Somaschini, Claudio; Iseni, Giosue; Melloni, Andrea

2017-05-01

Silicon oxycarbide (SiOC) thin films are produced with reactive rf magnetron sputtering of a silicon carbide (SiC) target on Si (100) and SiO2/Si substrates under varying deposition conditions. The optical properties of the deposited SiOC thin films are characterized with spectroscopic ellispometry at multiple angles of incidence over a wavelength range 300- 1600 nm. The derived optical constants of the SiOC films are modeled with Tauc-Lorentz model. The refractive index n of the SiOC films range from 1.45 to 1.85 @ 1550 nm and the extinction coefficient k is estimated to be less than 10-4 in the near-infrared region above 1000 nm. The topography of SiOC films is studied with SEM and AFM giving rms roughness of 0.9 nm. Channel waveguides with a SiOC core with a refractive index of 1.7 have been fabricated to demonstrate the potential of sputtered SiOC for integrated photonics applications. Propagation loss as low as 0.39 +/- 0.05 dB/mm for TE and 0.41 +/- 0.05 dB/mm for TM polarizations at telecommunication wavelength 1550 nm is demonstrated.

In Situ deposition of YBCO high-T(sub c) superconducting thin films by MOCVD and PE-MOCVD

NASA Technical Reports Server (NTRS)

Zhao, J.; Noh, D. W.; Chern, C.; Li, Y. Q.; Norris, P.; Gallois, B.; Kear, B.

1990-01-01

Metalorganic Chemical Vapor Deposition (MOCVD) offers the advantages of a high degree of compositional control, adaptability for large scale production, and the potential for low temperature fabrication. The capability of operating at high oxygen partial pressure is particularly suitable for in situ formation of high temperature superconducting (HTSC) films. Yttrium barium copper oxide (YBCO) thin films having a sharp zero-resistance transition with T( sub c) greater than 90 K and Jc approx. 10 to the 4th power A on YSZ have been prepared, in situ, at a substrate temperature of about 800 C. Moreover, the ability to form oxide films at low temperature is very desirable for device applications of HTSC materials. Such a process would permit the deposition of high quality HTSC films with a smooth surface on a variety of substrates. Highly c-axis oriented, dense, scratch resistant, superconducting YBCO thin films with mirror-like surfaces have been prepared, in situ, at a reduced substrate temperature as low as 570 C by a remote microwave-plasma enhanced metalorganic chemical vapor deposition (PE-MOCVD) process. Nitrous oxide was used as a reactant gas to generate active oxidizing species. This process, for the first time, allows the formation of YBCO thin films with the orthorhombic superconducting phase in the as-deposited state. The as-deposited films grown by PE-MOCVD show attainment of zero resistance at 72 K with a transition width of about 5 K. MOCVD was carried out in a commercial production scale reactor with the capability of uniform deposition over 100 sq cm per growth run. Preliminary results indicate that PE-MOCVD is a very attractive thin film deposition process for superconducting device technology.

Effect of annealing atmosphere on properties of Cu2ZnSn(S,Se)4 thin films

NASA Astrophysics Data System (ADS)

Xue, Yuming; Yu, Bingbing; Li, Wei; Feng, Shaojun; Wang, Yukun; Huang, Shengming; Zhang, Chao; Qiao, Zaixiang

2017-12-01

Earth-abundant Cu2ZnSn(S,Se)4(CZTSSe) thin film photovoltaic absorber layers were fabricated by co-evaporated Cu, ZnS, SnS and Se sources in a vacuum chamber followed by annealing at tubular furnace for 30 min at 550 °C. In this paper, we investigated the metal elements with stoichiometric ratio film to study the effect of annealing conditions of Se, SnS + Se, S and SnS + S atmosphere on the structure, surface morphological, optical and electrical properties of Cu2ZnSn(S,Se)4 thin films respectively. These films were characterized by Inductively Coupled Plasma-Mass Spectrometer, scanning electron microscopy, X-ray diffraction to investigate the composition, morphological and crystal structural properties. The grain size of samples were found to increase after annealing. XRD patterns confirmed the formation of pure polycrystalline CZTSSe thin films at S atmosphere, the optical band gaps are 1.02, 1.05, 1.23, 1.35 eV for Se, SnS + Se, SnS + S and S atmosphere respectively.

Ultra-high power capabilities in amorphous FePO4 thin films

NASA Astrophysics Data System (ADS)

Gandrud, Knut B.; Nilsen, Ola; Fjellvåg, Helmer

2016-02-01

Record breaking electrochemical properties of FePO4 have been found through investigation of the thickness dependent electrochemical properties of amorphous thin film electrodes. Atomic layer deposition was used for production of thin films of amorphous FePO4 with highly accurate thickness and topography. Electrochemical characterization of these thin film electrodes revealed that the thinner electrodes behave in a pseudocapacitive manner even at high rates of Li+ de/intercalation, which enabled specific powers above 1 MW kg-1 FePO4 to be obtained with minimal capacity loss. In addition, a self-enhancing kinetic effect was observed during cycling enabling more than 10,000 cycles at current rates approaching that of a supercapacitor (11s charge/discharge). The current findings may open for construction of ultra-high power battery electrodes that combines the energy density of batteries with the power capabilities of supercapacitors.

Ferromagnetic thin films

DOEpatents

Krishnan, K.M.

1994-12-20

A ferromagnetic [delta]-Mn[sub 1[minus]x]Ga[sub x] thin film having perpendicular anisotropy is described which comprises: (a) a GaAs substrate, (b) a layer of undoped GaAs overlying said substrate and bonded thereto having a thickness ranging from about 50 to about 100 nanometers, (c) a layer of [delta]-Mn[sub 1[minus]x]Ga[sub x] overlying said layer of undoped GaAs and bonded thereto having a thickness ranging from about 20 to about 30 nanometers, and (d) a layer of GaAs overlying said layer of [delta]-Mn[sub 1[minus]x]Ga[sub x] and bonded thereto having a thickness ranging from about 2 to about 5 nanometers, wherein x is 0.4[+-]0.05. 7 figures.

Tuning Bandgap of p-Type Cu2Zn(Sn, Ge)(S, Se)4 Semiconductor Thin Films via Aqueous Polymer-Assisted Deposition.

PubMed

Yi, Qinghua; Wu, Jiang; Zhao, Jie; Wang, Hao; Hu, Jiapeng; Dai, Xiao; Zou, Guifu

2017-01-18

Bandgap engineering of kesterite Cu 2 Zn(Sn, Ge)(S, Se) 4 with well-controlled stoichiometric composition plays a critical role in sustainable inorganic photovoltaics. Herein, a cost-effective and reproducible aqueous solution-based polymer-assisted deposition approach is developed to grow p-type Cu 2 Zn(Sn, Ge)(S, Se) 4 thin films with tunable bandgap. The bandgap of Cu 2 Zn(Sn, Ge)(S, Se) 4 thin films can be tuned within the range 1.05-1.95 eV using the aqueous polymer-assisted deposition by accurately controlling the elemental compositions. One of the as-grown Cu 2 Zn(Sn, Ge)(S, Se) 4 thin films exhibits a hall coefficient of +137 cm 3 /C. The resistivity, concentration and carrier mobility of the Cu 2 ZnSn(S, Se) 4 thin film are 3.17 ohm·cm, 4.5 × 10 16 cm -3 , and 43 cm 2 /(V·S) at room temperature, respectively. Moreover, the Cu 2 ZnSn(S, Se) 4 thin film when used as an active layer in a solar cell leads to a power conversion efficiency of 3.55%. The facile growth of Cu 2 Zn(Sn, Ge)(S, Se) 4 thin films in an aqueous system, instead of organic solvents, provides great promise as an environmental-friendly platform to fabricate a variety of single/multi metal chalcogenides for the thin film industry and solution-processed photovoltaic devices.

Effects of bacteria on CdS thin films used in technological devices

NASA Astrophysics Data System (ADS)

Alpdoğan, S.; Adıgüzel, A. O.; Sahan, B.; Tunçer, M.; Metin Gubur, H.

2017-04-01

Cadmium sulfide (CdS) thin films were fabricated on glass substrates by the chemical bath deposition method at 70 {}^\\circ \\text{C} considering deposition times ranging from 2 h to 5 h. The optical band gaps of CdS thin films were found to be in the 2.42-2.37 eV range. CdS thin films had uniform spherical nano-size grains which had polycrystalline, hexagonal and cubic phases. The films had a characteristic electrical resistivity of the order of {{10}5} Ω \\text{cm} and n-type conductivity at room condition. CdS thin films were incubated in cultures of B.domonas aeruginosa and Staphylococcus aureus, which exist abundantly in the environment, and form biofilms. SEM images showed that S. aureus and K. pneumonia were detected significantly on the film surfaces with a few of P. aeruginosa and B. subtilis cells attached. CdS thin film surface exhibits relatively good resistance to the colonization of P. aeruginosa and B. subtilis. Optical results showed that the band gap of CdS thin films which interacted with the bacteria is 2.42 \\text{eV} . The crystal structure and electrical properties of CdS thin films were not affected by bacterial adhesion. The antimicrobial effect of CdS nanoparticles was different for different bacterial strains.

Ultrahigh-Performance Cu2ZnSnS4 Thin Film and Its Application in Microscale Thin-Film Lithium-Ion Battery: Comparison with SnO2.

PubMed

Lin, Jie; Guo, Jianlai; Liu, Chang; Guo, Hang

2016-12-21

To develop a high-performance anode for thin-film lithium-ion batteries (TFBs, with a total thickness on the scale of micrometers), a Cu 2 ZnSnS 4 (CZTS) thin film is fabricated by magnetron sputtering and exhibits an ultrahigh performance of 950 mAh g -1 even after 500 cycles, which is the highest among the reported CZTS for lithium storage so far. The characterization and electrochemical tests reveal that the thin-film structure and additional reactions both contribute to the excellent properties. Furthermore, the microscale TFBs with effective footprints of 0.52 mm 2 utilizing the CZTS thin film as anode are manufactured by microfabrication techniques, showing superior capability than the analogous TFBs with the SnO 2 thin film as anode. This work demonstrates the advantages of exploiting thin-film electrodes and novel materials into micropower sources by electronic manufacture methods.

Liquid crystals for organic thin-film transistors

PubMed Central

Iino, Hiroaki; Usui, Takayuki; Hanna, Jun-ichi

2015-01-01

Crystalline thin films of organic semiconductors are a good candidate for field effect transistor (FET) materials in printed electronics. However, there are currently two main problems, which are associated with inhomogeneity and poor thermal durability of these films. Here we report that liquid crystalline materials exhibiting a highly ordered liquid crystal phase of smectic E (SmE) can solve both these problems. We design a SmE liquid crystalline material, 2-decyl-7-phenyl-[1]benzothieno[3,2-b][1]benzothiophene (Ph-BTBT-10), for FETs and synthesize it. This material provides uniform and molecularly flat polycrystalline thin films reproducibly when SmE precursor thin films are crystallized, and also exhibits high durability of films up to 200 °C. In addition, the mobility of FETs is dramatically enhanced by about one order of magnitude (over 10 cm2 V−1 s−1) after thermal annealing at 120 °C in bottom-gate-bottom-contact FETs. We anticipate the use of SmE liquid crystals in solution-processed FETs may help overcome upcoming difficulties with novel technologies for printed electronics. PMID:25857435

Liquid crystals for organic thin-film transistors.

PubMed

Iino, Hiroaki; Usui, Takayuki; Hanna, Jun-ichi

2015-04-10

Crystalline thin films of organic semiconductors are a good candidate for field effect transistor (FET) materials in printed electronics. However, there are currently two main problems, which are associated with inhomogeneity and poor thermal durability of these films. Here we report that liquid crystalline materials exhibiting a highly ordered liquid crystal phase of smectic E (SmE) can solve both these problems. We design a SmE liquid crystalline material, 2-decyl-7-phenyl-[1]benzothieno[3,2-b][1]benzothiophene (Ph-BTBT-10), for FETs and synthesize it. This material provides uniform and molecularly flat polycrystalline thin films reproducibly when SmE precursor thin films are crystallized, and also exhibits high durability of films up to 200 °C. In addition, the mobility of FETs is dramatically enhanced by about one order of magnitude (over 10 cm(2) V(-1) s(-1)) after thermal annealing at 120 °C in bottom-gate-bottom-contact FETs. We anticipate the use of SmE liquid crystals in solution-processed FETs may help overcome upcoming difficulties with novel technologies for printed electronics.

Finding pathways to prepare Fe4N thin films at low substrate temperature

NASA Astrophysics Data System (ADS)

Seema, Gupta, Nitiand Mukul

2018-04-01

In Fe-N phase diagram the formation of Fe4N thin films occur in a very narrow region, specially below 573 K. Above this, the range of homogeneity for formation of Fe4N start to increase yielding more favorable conditions for formation of single phase Fe4N. However, when deposited at high substrate temperature (Ts) typically above 650 K, nitrogen (N) tends to diffuse out of the system yielding a N deficient phase. In this work, we attempt to find pathways to deposit Fe4N thin films at low Ts and successfully prepared single phase Fe4N thin films at Ts as low as 423 K. This was achieved by utilizing an underlayer of CrN. We find that such underlayer not only has close lattice matching with Fe4N, it also acts as a diffusion barrier for the film-substrate interface.

Thermal, Structural, AC Conductivity, and Dielectric Properties of Ethyl-2-amino-6-ethyl-5-oxo-4-(3-phenoxyphenyl)-5,6-dihydro-4H-pyrano[3,2-c]quinoline-3-carboxylate Thin Films

NASA Astrophysics Data System (ADS)

El-Shabaan, M. M.

2018-05-01

Thermal, structural, alternating-current (AC) conductivity (σ AC), and dielectric properties of ethyl-2-amino-6-ethyl-5-oxo-4-(3-phenoxyphenyl)-5,6-dihydro-4H-pyrano[3,2-c]quinoline-3-carboxylate (HPQC) thin films have been studied. Thermogravimetry analysis and differential scanning calorimetry confirmed the thermal stability of HPQC over a wide temperature range. Fourier-transform infrared spectroscopy and x-ray diffraction analysis were carried out on HPQC in powder form and as-deposited thin film. The crystal system and space group type were determined for HPQC in powder form. The AC conductivity and dielectric properties were determined in the frequency range from 0.5 kHz to 5 MHz and temperature range from 296 K to 443 K. The AC electrical conduction of HPQC thin film was found to be governed by the small-polaron tunneling mechanism. The polaron hopping energy (W H), tunneling distance (R), and density of states (N) near the Fermi level were determined as functions of temperature and frequency. The dielectric properties of HPQC thin film were studied by analysis of Nyquist diagrams, the dissipation factor (tan δ), and real (ɛ') and imaginary (ɛ″) parts of the dielectric constant.

Optical Properties and Electrochemical Performance of LiFePO4 Thin Films Deposited on Transparent Current Collectors.

PubMed

Lee, HyunSeok; Yim, Haena; Kim, Kwang-Bum; Choi, Ji-Won

2015-11-01

LiFePO4 thin film cathodes are deposited on various transparent conducting oxide thin films on glass, which are used as cathode current collectors. The XRD patterns show that the thin films have the phase of LiFePO4 with an ordered olivine structure indexed to the orthorhombic Pmna space group. LiFePO4 thin film deposited on various TCO glass substrates exhibits transmittance of about 53%. The initial specific discharge capacities of LiFePO4 thin films are 25.0 μAh/cm2 x μm on FTO, 33.0 μAh/cm2 x μm on ITO, and 13.0 μAh/cm2 x μm on AZO coated glass substrates. Interestingly, the retention capacities of LiFePO4 thin films are 76.0% on FTO, 31.2% on ITO, and 37.7% on AZO coated glass substrates at 20th cycle. The initial specific discharge capacity of the LiFePO4/FTO electrode is slightly lower, but the discharge capacities of the LiFePO4/FTO electrode relatively decrease less than those of the others such as LiFePO4/ITO and LiFePO4/AZO with cycling. The results reported here provide the high transparency of LiFePO4 thin films cathode materials and the good candidate as FTO current collector of the LiFePO4 thin film cathode of transparent thin film rechargeable batteries due to its high transparency and cyclic retention.

Durability Evaluation of a Thin Film Sensor System With Enhanced Lead Wire Attachments on SiC/SiC Ceramic Matrix Composites

NASA Technical Reports Server (NTRS)

Lei, Jih-Fen; Kiser, J. Douglas; Singh, Mrityunjay; Cuy, Mike; Blaha, Charles A.; Androjna, Drago

2000-01-01

An advanced thin film sensor system instrumented on silicon carbide (SiC) fiber reinforced SiC matrix ceramic matrix composites (SiC/SiC CMCs), was evaluated in a Mach 0.3 burner rig in order to determine its durability to monitor material/component surface temperature in harsh environments. The sensor system included thermocouples in a thin film form (5 microns thick), fine lead wires (75 microns diameter), and the bonds between these wires and the thin films. Other critical components of the overall system were the heavy, swaged lead wire cable (500 microns diameter) that contained the fine lead wires and was connected to the temperature readout, and ceramic attachments which were bonded onto the CMCs for the purpose of securing the lead wire cables, The newly developed ceramic attachment features a combination of hoops made of monolithic SiC or SiC/SiC CMC (which are joined to the test article) and high temperature ceramic cement. Two instrumented CMC panels were tested in a burner rig for a total of 40 cycles to 1150 C (2100 F). A cycle consisted of rapid heating to 1150 C (2100 F), a 5 minute hold at 1150 C (2100 F), and then cooling down to room temperature in 2 minutes. The thin film sensor systems provided repeatable temperature measurements for a maximum of 25 thermal cycles. Two of the monolithic SiC hoops debonded during the sensor fabrication process and two of the SiC/SiC CMC hoops failed during testing. The hoops filled with ceramic cement, however, showed no sign of detachment after 40 thermal cycle test. The primary failure mechanism of this sensor system was the loss of the fine lead wire-to-thin film connection, which either due to detachment of the fine lead wires from the thin film thermocouples or breakage of the fine wire.

Origin of the emergence of higher T c than bulk in iron chalcogenide thin films

DOE Office of Scientific and Technical Information (OSTI.GOV)

Seo, Sehun; Kang, Jong-Hoon; Oh, Myeong Jun

Fabrication of epitaxial FeSe xTe 1-x thin films using pulsed laser deposition (PLD) enables improving their superconducting transition temperature (T c) by more than ~40% than their bulk T c. Intriguingly, T c enhancement in FeSe xTe 1-x thin films has been observed on various substrates and with different Se content, x. To date, various mechanisms for T c enhancement have been reported, but they remain controversial in universally explaining the T c improvement in the FeSe xTe 1-x films. In this report, we demonstrate that the controversies over the mechanism of T c enhancement are due to the abnormalmore » changes in the chalcogen ratio (Se:Te) during the film growth and that the previously reported T c enhancement in FeSe 0.5Te 0.5 thin films is caused by a remarkable increase of Se content. Although our FeSe xTe 1-x thin films were fabricated via PLD using a Fe 0.94Se 0.45Te 0.55 target, the precisely measured composition indicates a Se-rich FeSe xTe 1-x (0.6 < x < 0.8) as ascertained through accurate compositional analysis by both wavelength dispersive spectroscopy (WDS) and Rutherford backscattering spectrometry (RBS). We suggest that the origin of the abnormal composition change is the difference in the thermodynamic properties of ternary FeSe xTe 1-x, based on first principle calculations.« less

Origin of the emergence of higher T c than bulk in iron chalcogenide thin films

DOE PAGES

Seo, Sehun; Kang, Jong-Hoon; Oh, Myeong Jun; ...

2017-08-30

Fabrication of epitaxial FeSe xTe 1-x thin films using pulsed laser deposition (PLD) enables improving their superconducting transition temperature (T c) by more than ~40% than their bulk T c. Intriguingly, T c enhancement in FeSe xTe 1-x thin films has been observed on various substrates and with different Se content, x. To date, various mechanisms for T c enhancement have been reported, but they remain controversial in universally explaining the T c improvement in the FeSe xTe 1-x films. In this report, we demonstrate that the controversies over the mechanism of T c enhancement are due to the abnormalmore » changes in the chalcogen ratio (Se:Te) during the film growth and that the previously reported T c enhancement in FeSe 0.5Te 0.5 thin films is caused by a remarkable increase of Se content. Although our FeSe xTe 1-x thin films were fabricated via PLD using a Fe 0.94Se 0.45Te 0.55 target, the precisely measured composition indicates a Se-rich FeSe xTe 1-x (0.6 < x < 0.8) as ascertained through accurate compositional analysis by both wavelength dispersive spectroscopy (WDS) and Rutherford backscattering spectrometry (RBS). We suggest that the origin of the abnormal composition change is the difference in the thermodynamic properties of ternary FeSe xTe 1-x, based on first principle calculations.« less

Effects of drying temperature on tomato-based thin film as self-powered UV photodetector

NASA Astrophysics Data System (ADS)

Thu, Myo Myo; Mastuda, Atsunori; Cheong, Kuan Yew

2018-07-01

In this work, tomato thin-film is used as an active natural organic layer for UV photodetector. The effects of drying temperature (60-140 °C) on structural, chemical, electrical and UV sensing properties of tomato thin-film have been investigated. The photodetector consists of a glass substrate/tomato thin-film active layer/interdigitated aluminium electrode structure. As the drying temperature increases, surface and density of tomato thin-film is smoother and denser with thinner physical thickness. Chemical functional groups as a function of drying temperature is evaluated and correlated with the electrical property of thin film. A comparison between dark and UV (B and C) illumination with respect to the electrical property has been revealed and the observation has been linked to the active chemical compounds that controlling antioxidant activity in the tomato. By drying the tomato thin-film at 120°C, a self-powered (V = 0 V) photodetector that is able to selectively detecting UV-C can be obtained with external quantum efficiency (η) of 2.53 × 10-7%. While drying it at 140 °C, the detector is better in detecting UV-B when operating at either 5 or -5 V with η of 7.7384 × 10-6% and 8.87 × 10-6%, respectively. The typical response time for raising and falling for all samples are less than 0.3 s.

Leakage current conduction and reliability assessment of passivating thin silicon dioxide films on n-4H-SiC

NASA Astrophysics Data System (ADS)

Samanta, Piyas; Mandal, Krishna C.

2016-09-01

We have analyzed the mechanisms of leakage current conduction in passivating silicon dioxide (SiO2) films grown on (0 0 0 1) silicon (Si) face of n-type 4H-SiC (silicon carbide). It was observed that the experimentally measured gate current density in metal-oxide-silicon carbide (MOSiC) structures under positive gate bias at an oxide field Eox above 5 MV/cm is comprised of Fowler-Nordheim (FN) tunneling of electrons from the accumulated n-4H-SiC and Poole-Frenkel (PF) emission of trapped electrons from the localized neutral traps in the SiO2 gap, IFN and IPF, respectively at temperatures between 27 and 200 °C. In MOSiC structures, PF mechanism dominates FN tunneling of electrons from the accumulation layer of n-4H-SiC due to high density (up to 1013 cm-2) of carbon-related acceptor-like traps located at about 2.5 eV below the SiO2 conduction band (CB). These current conduction mechanisms were taken into account in studying hole injection/trapping into 10 nm-thick tunnel oxide on the Si face of 4H-SiC during electron injection from n-4H-SiC under high-field electrical stress with positive bias on the heavily doped n-type polysilicon (n+-polySi) gate at a wide range of temperatures between 27 and 200 °C. Holes were generated in the n+-polySi anode material by the hot-electrons during their transport through thin oxide films at oxide electric fields Eox from 5.6 to 8.0 MV/cm (prior to the intrinsic oxide breakdown field). Time-to-breakdown tBD of the gate dielectric was found to follow reciprocal field (1/E) model irrespective of stress temperatures. Despite the significant amount of process-induced interfacial electron traps contributing to a large amount of leakage current via PF emission in thermally grown SiO2 on the Si-face of n-4H-SiC, MOSiC devices having a 10 nm-thick SiO2 film can be safely used in 5 V TTL logic circuits over a period of 10 years.

Thin transparent film characterization by photothermal reflectance (abstract)

NASA Astrophysics Data System (ADS)

Li Voti, R.; Wright, O. B.; Matsuda, O.; Larciprete, M. C.; Sibilia, C.; Bertolotti, M.

2003-01-01

Photothermal reflectance methods have been intensively applied to the nondestructive testing of opaque thin films [D. P. Almond and P. M. Patel, Photothermal Science and Techniques (Chapman and Hall, London, 1996); C. Bento and D. P. Almond, Meas. Sci. Technol. 6, 1022 (1995); J. Opsal, A. Rosencwaig, and D. Willenborg, Appl. Opt. 22, 3169 (1983)]. The basic principle is based on thermal wave interferometry: the opaque specimen is illuminated by a laser beam, periodically chopped at the frequency f, so as to generate a plane thermal wave in the surface region. This wave propagates in the film, approaches the rear interface (film-bulk), is partially reflected back, reaches the front surface, is again partially reflected back and so on, giving rise to thermal wave interference. A consequence of this interference is that the surface temperature may be enhanced (constructive interference) or reduced (destructive interference) by simply scanning the frequency f (that is, the thermal diffusion length μ=√D/πf ), so as to observe damped oscillations as a function of f; in practice only the first oscillation may be clearly resolved and used to measure either the film thickness d or the film thermal diffusivity D, and this situation occurs when μ≈d. In general, photothermal reflectance does not measure directly the surface temperature variation, but rather a directly related signal determined by the thermo-optic coefficients and the sample geometry; for detection it is common to monitor the optical reflectivity variation of a probe beam normally incident on the sample. If the thin film is partially transparent to the probe, the theory becomes more difficult [O. Matsuda and O. B. Wright, J. Opt. Soc. Am. B (in press)] and one should consider the probe beam multiple reflections in the thin film. The probe modulation is optically inhomogeneous due to the temperature-induced changes in refractive index. Although in the past the complexity of the analysis has impeded

Optical characterization of sputtered YBaCo 4O 7+ δ thin films

NASA Astrophysics Data System (ADS)

Montoya, J. F.; Izquierdo, J. L.; Causado, J. D.; Bastidas, A.; Nisperuza, D.; Gómez, A.; Arnache, O.; Osorio, J.; Marín, J.; Paucar, C.; Morán, O.

2011-02-01

Thin films of YBaCo 4O 7+ δ were deposited on r (1012)-oriented Al 2O 3 substrates by dc magnetron sputtering. The as-grown films were characterized after their structural, morphological and optical properties. Special attention is devoted to the analysis of the optical response of these films as reports on optical properties of YBaCo 4O 7+ δ, especially in thin film form, are not frequently reported in the literature. Transmittance/absorbance measurements allow for determining two well defined energy gaps at 3.7 and 2.2 eV. In turn, infrared (IR) measurements show infrared transparency in the wave length range 4000-2500 nm with a sharp absorption edge at wave lengths less than 2500 nm. Complementary Raman spectra measurements on the thin films allowed for identifying bands associated with vibrating modes of CoO 4 and YO 6 in tetrahedral and octahedral oxygen coordination, respectively. Additional bands which seemed to stem from Co ions in octahedral oxygen coordination were also clearly identified.

Characterization of diamond thin films and related materials

NASA Astrophysics Data System (ADS)

McKindra, Travis Kyle

Thin carbon films including sputtered deposited graphite and CO 2 laser-assisted combustion-flame deposited graphite and diamond thin films were characterized using optical and electron microscopy, X-ray diffraction and micro-Raman spectroscopy. Amorphous carbon thin films were deposited by DC magnetron sputtering using Ar/O2 gases. The film morphology changed with the oxygen content. The deposition rate decreased as the amount of oxygen increased due to oxygen reacting with the growing film. The use of oxygen in the working gas enhanced the crystalline nature of the films. Graphite was deposited on WC substrates by a CO2 laser-assisted O2/C2H2 combustion-flame method. Two distinct microstructural areas were observed; an inner core of dense material surrounded by an outer shell of lamellar-like material. The deposits were crystalline regardless of the laser power and deposition times of a few minutes. Diamond films were deposited by a CO2 laser-assisted O 2/C2H2/C2H4 combustion-flame method with the laser focused parallel to the substrate surface. The laser enhanced diamond growth was most pronounced when deposited with a 10.532 microm CO2 laser wavelength tuned to the CH2-wagging vibrational mode of the C2H4 molecule. Nucleation of diamond thin films deposited with and without using a CO 2 laser-assisted combustion-flame process was investigated. With no laser there was nucleation of a sub-layer of grains followed by irregular grain growth. An untuned laser wavelength yielded nucleation of a sub-layer then columnar grain growth. The 10.532 microm tuned laser wavelength caused growth of columnar grains.

Polymer Thin Film Stabilization.

NASA Astrophysics Data System (ADS)

Costa, A. C.; Oslanec, R.; Composto, R. J.; Vlcek, P.

1998-03-01

We study the dewetting dynamics of thin polystyrene (PS) films deposited on silicon oxide surfaces using optical (OM) and atomic force (AFM) microscopes. Quantitative analysis of the hole diameter as a function of annealing time at 175^oC shows that blending poly(styrene-block-methyl-methacrylate) (PS-b-PMMA) with PS acts to dramatically slow down the dewetting rate and even stops holes growth before they impinge. AFM studies show that the hole floor is smooth for a pure PS film but contains residual polymer for the blend. At 5% vol., a PS-b-PMMA with high molar mass and low PMMA is a more effective stabilizing agent than a low molar mass/high PMMA additive. The optimum copolymer concentration is 3% vol. beyond which film stability doesn't improve. Although dewetting is slowed down relative to pure PS, PS/PS-b-PMMA bilayers dewet at a faster rate than blends having the same overall additive concentration.

Probing localized strain in solution-derived YB a2C u3O7 -δ nanocomposite thin films

NASA Astrophysics Data System (ADS)

Guzman, Roger; Gazquez, Jaume; Mundet, Bernat; Coll, Mariona; Obradors, Xavier; Puig, Teresa

2017-07-01

Enhanced pinning due to nanoscale strain is unique to the high-Tc cuprates, where pairing may be modified with lattice distortion. Therefore a comprehensive understanding of the defect landscape is required for a broad range of applications. However, determining the type and distribution of defects and their associated strain constitutes a critical task, and for this aim, real-space techniques for atomic resolution characterization are necessary. Here, we use scanning transmission electron microscopy (STEM) to study the atomic structure of individual defects of solution-derived YB a2C u3O7 (YBCO) nanocomposites, where the inclusion of incoherent secondary phase nanoparticles within the YBCO matrix dramatically increases the density of Y1B a2C u4O8 (Y124) intergrowths, the commonest defect in YBCO thin films. The formation of the Y124 is found to trigger a concatenation of strain-derived interactions with other defects and the concomitant nucleation of intrinsic defects, which weave a web of randomly distributed nanostrained regions that profoundly transform the vortex-pinning landscape of the YBCO nanocomposite thin films.

Method for measurement of diffusivity: Calorimetric studies of Fe/Ni multilayer thin films

DOE Office of Scientific and Technical Information (OSTI.GOV)

Liu, JX; Barmak, K

2015-07-15

A calorimetric method for the measurement of diffusivity in thin film multilayers is introduced and applied to the Fe Ni system. Using this method, the diffusivity in [Fe (25 nm)/Ni (25 nm)](20) multilayer thin films is measured as 4 x 10(-3)exp(-1.6 +/- 0.1 eV/ k(B)T) cm(2)/s, respectively. The diffusion mechanism in the multilayers and its relevance to laboratory synthesis of L1(0) ordered FeNi are discussed. (C) 2015 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

Effect of dopants on the soft magnetic properties and high frequency characteristics of FeCoBM (M = Ti, Nb, Hf, and Ta) thin films.

PubMed

Hsieh, C C; Lin, T H; Chang, H W; Chang, C W; Chang, W C; Yang, C C

2011-03-01

Effect of dopants on the soft magnetic properties and high frequency characteristics of FeCoBM thin films (M = Ti, Nb, Hf, and Ta) have been studied. For (Fe0.55Co0.45)(100-x)B(x) (x = 5-15) thin films, with the increase of B content, the resistivity was increased because B could decrease the crystallinity of the films. The (Fe0.55Co0.45)90B10 thin film showed the optimum properties, where 4piM(s) = 16.1 kG, H(ce) = 64.2 Oe, H(ch) = 13.5 Oe, H(k) = 310 Oe and p = 338 microomega-cm. To reduce the coercivity of the film, the elements M, including Ti, Nb, Hf, and Ta, were selected to substitute for B in the FeCoB films. It was found that (Fe0.55Co0.45)90B6Ti2Nb2 thin film after annealing at a temperature of 200 degrees C for 30 min showed the optimal properties, where 4piM(s) = 15.8 kG, H(ce) = 4.8 Oe, H(ch) = 3.6 Oe, H(k) = 224 Oe and p = 290 microomega-cm. The theoretically calculated ferromagnetic resonance frequency of the developed films can be higher than 5 GHz.

RF critical field measurement of MgB2 thin films coated on Nb

NASA Astrophysics Data System (ADS)

Tajima, T.; Eremeev, G.; Zou, G.; Dolgashev, V.; Martin, D.; Nantista, C.; Tantawi, S.; Yoneda, C.; Moeckly, B. H.; Campisi, I.

2010-06-01

Niobium (Nb) Superconducting RF (SRF) cavities have been used or will be used for a number of particle accelerators. The fundamental limit of the accelerating gradient has been thought to be around 50 MV/m due to its RF critical magnetic field of around 200 mT. This limit will prevent new projects requiring higher gradient and compact accelerators from considering SRF structures. There is a theory, however, that promises to overcome this limitation by coating thin (less than the penetration depth) superconductors on Nb. We initiated measurements of critical magnetic fields of Nb coated with various thin film superconductors, starting with MgB2 films deposited using reactive evaporation technique, with the goal to apply this coating to SRF cavities. This paper will present first test results of the RF critical magnetic field of a system consisting of a 10 nm B and a 100 nm MgB2 films deposited on a chemically polished 2-inch single grain Nb substrate.

The Cu2ZnSnSe4 thin films solar cells synthesized by electrodeposition route

NASA Astrophysics Data System (ADS)

Li, Ji; Ma, Tuteng; Wei, Ming; Liu, Weifeng; Jiang, Guoshun; Zhu, Changfei

2012-06-01

An electrodeposition route for preparing Cu2ZnSnSe4 thin films for thin film solar cell absorber layers is demonstrated. The Cu2ZnSnSe4 thin films are prepared by co-electrodeposition Cu-Zn-Sn metallic precursor and subsequently annealing in element selenium atmosphere. The structure, composition and optical properties of the films were investigated by X-ray diffraction (XRD), Raman spectrometry, energy dispersive spectrometry (EDS) and UV-VIS absorption spectroscopy. The Cu2ZnSnSe4 thin film with high crystalline quality was obtained, the band gap and absorption coefficient were 1.0 eV and 10-4 cm-1, which is quite suitable for solar cells fabrication. A solar cell with the structure of ZnO:Al/i-ZnO/CdS/Cu2ZnSnSe4/Mo/glass was fabricated and achieved an conversion efficiency of 1.7%.

The effect of Argon pressure dependent V thin film on the phase transition process of (020) VO2 thin film

NASA Astrophysics Data System (ADS)

Meng, Yifan; Huang, Kang; Tang, Zhou; Xu, Xiaofeng; Tan, Zhiyong; Liu, Qian; Wang, Chunrui; Wu, Binhe; Wang, Chang; Cao, Juncheng

2018-01-01

It has been proved challenging to fabricate the single crystal orientation of VO2 thin film by a simple method. Based on chemical reaction thermodynamic and crystallization analysis theory, combined with our experimental results, we find out that when stoichiometric number of metallic V in the chemical equation is the same, the ratio of metallic V thin film surface average roughness Ra to thin film average particle diameter d decreases with the decreasing sputtering Argon pressure. Meanwhile, the oxidation reaction equilibrium constant K also decreases, which will lead to the increases of oxidation time, thereby the crystal orientation of the VO2 thin film will also become more uniform. By sputtering oxidation coupling method, metallic V thin film is deposited on c-sapphire substrate at 1 × 10-1 Pa, and then oxidized in the air with the maximum oxidation time of 65s, high oriented (020) VO2 thin film has been fabricated successfully, which exhibits ∼4.6 orders sheet resistance change across the metal-insulator transition.

Li-ion diffusion kinetics in LiCoPO 4 thin films deposited on NASICON-type glass ceramic electrolytes by magnetron sputtering

NASA Astrophysics Data System (ADS)

Xie, J.; Imanishi, N.; Zhang, T.; Hirano, A.; Takeda, Y.; Yamamoto, O.

LiCoPO 4 thin films were deposited on Li 1+ x+ yAl xTi 2- xSi yP 3- yO 12 (LATSP) solid electrolyte by radio frequency magnetron sputtering and were characterized by X-ray diffraction and scanning electron microscope. The films show a (1 1 1) preferred orientation upon annealing and are chemically stable with LATSP up to 600 °C in air. An all-solid-state Li/PEO 18-Li(CF 3SO 2) 2N/LATSP/LiCoPO 4/Au cell was fabricated to investigate the electrochemical performance and Li-ion chemical diffusion coefficients, D˜Li , of the LiCoPO 4 thin films. The potential dependence of D˜Li values of the LiCoPO 4 thin film was investigated by potentiostatic intermittent titration technique and was compared with those of the LiFePO 4 thin film. These results showed that the intercalation mechanism of Li-ion in LiCoPO 4 is different from that in LiFePO 4.

BiVO4 thin film photoanodes grown by chemical vapor deposition.

PubMed

Alarcón-Lladó, Esther; Chen, Le; Hettick, Mark; Mashouf, Neeka; Lin, Yongjing; Javey, Ali; Ager, Joel W

2014-01-28

BiVO4 thin film photoanodes were grown by vapor transport chemical deposition on FTO/glass substrates. By controlling the flow rate, the temperatures of the Bi and V sources (Bi metal and V2O5 powder, respectively), and the temperature of the deposition zone in a two-zone furnace, single-phase monoclinic BiVO4 thin films can be obtained. The CVD-grown films produce global AM1.5 photocurrent densities up to 1 mA cm(-2) in aqueous conditions in the presence of a sacrificial reagent. Front illuminated photocatalytic performance can be improved by inserting either a SnO2 hole blocking layer and/or a thin, extrinsically Mo doped BiVO4 layer between the FTO and the CVD-grown layer. The incident photon to current efficiency (IPCE), measured under front illumination, for BiVO4 grown directly on FTO/glass is about 10% for wavelengths below 450 nm at a bias of +0.6 V vs. Ag/AgCl. For BiVO4 grown on a 40 nm SnO2/20 nm Mo-doped BiVO4 back contact, the IPCE is increased to over 40% at wavelengths below 420 nm.

Effects of ultraviolet light on B-doped CdS thin films prepared by spray pyrolysis method using perfume atomizer

NASA Astrophysics Data System (ADS)

Novruzov, V. D.; Keskenler, E. F.; Tomakin, M.; Kahraman, S.; Gorur, O.

2013-09-01

Boron doped CdS thin films were deposited by spray pyrolysis method using perfume atomizer. The effects of ultraviolet light on the structural, optical and electrical properties of B-doped CdS thin films were investigated as a function of dopant concentration (B/Cd). X-ray diffraction studies showed that all samples were polycrystalline nature with hexagonal structure. It was determined that the preferred orientation of non-illuminated samples changes from (1 0 1) to (0 0 2) with B concentration. The c lattice constant of films decreases from 6.810 Å to 6.661 Å with boron doping. The XRD peak intensity increased with the illumination for almost all the samples. The lattice parameters of B-doped samples remained nearly constant after illumination. It was found that the optical transmittance, photoluminescence spectra, resistivity and carrier concentration of the B-doped samples are stable after the illumination with UV light. Also the effects of UV light on B-doped CdS/Cu2S solar cell were investigated and it was determined that photoelectrical parameters of B-doped solar cell were more durable against the UV light.

Effect of Mo substitution on ferroelectric properties of Bi3.6Ho0.4Ti3O12 thin films prepared by sol-gel method

NASA Astrophysics Data System (ADS)

Guo, Dongyun; Wang, Chuanbin; Shen, Qiang; Zhang, Lianmeng; Li, Meiya; Liu, Jun

2008-12-01

The series of (Bi0.9Ho0.1)4-2x/3Ti3-xMoxO12 (BHTM) (x=0, 0.9%, 1.5%, 3.0%, and 6.0%) thin films on Pt/Ti/SiO2/Si substrates is prepared by sol-gel method, and the effect of Mo content on the microstructure and ferroelectric properties of these films are investigated. When the Mo content is not excessive, the BHTM films consisted of the single phase of Bi-layered Aurivillius phase. The B-site substitution with high-valent cation of Mo6+, in Bi3.6Ho0.4Ti3O12 films, enhanced the 2Pr (remanent polarization) and reduced the 2Ec (coercive field) of these films. The BHTM thin film with x =1.5% exhibited the best electrical properties with 2Pr of 48.4 μC/cm2, 2Ec of 263.5 kV/cm, dielectric constant of 391 (at 1 MHz), good insulting behavior, as well as the fatigue-free characteristic.

Rechargeable Thin-film Lithium Batteries

DOE R&D Accomplishments Database

Bates, J. B.; Gruzalski, G. R.; Dudney, N. J.; Luck, C. F.; Yu, Xiaohua

1993-08-01

Rechargeable thin film batteries consisting of lithium metal anodes, an amorphous inorganic electrolyte, and cathodes of lithium intercalation compounds have recently been developed. The batteries, which are typically less than 6 {mu}m thick, can be fabricated to any specified size, large or small, onto a variety of substrates including ceramics, semiconductors, and plastics. The cells that have been investigated include Li TiS{sub 2}, Li V{sub 2}O{sub 5}, and Li Li{sub x}Mn{sub 2}O{sub 4}, with open circuit voltages at full charge of about 2.5, 3.6, and 4.2, respectively. The development of these batteries would not have been possible without the discovery of a new thin film lithium electrolyte, lithium phosphorus oxynitride, that is stable in contact with metallic lithium at these potentials. Deposited by rf magnetron sputtering of Li{sub 3}PO{sub 4} in N{sub 2}, this material has a typical composition of Li{sub 2.9}PO{sub 3.3}N{sub 0.46} and a conductivity at 25{degrees}C of 2 {mu}S/cm. The maximum practical current density obtained from the thin film cells is limited to about 100 {mu}A/cm{sup 2} due to a low diffusivity of Li{sup +} ions in the cathodes. In this work, the authors present a short review of their work on rechargeable thin film lithium batteries.

Low work function, stable thin films

DOEpatents

Dinh, Long N.; McLean, II, William; Balooch, Mehdi; Fehring, Jr., Edward J.; Schildbach, Marcus A.

2000-01-01

Generation of low work function, stable compound thin films by laser ablation. Compound thin films with low work function can be synthesized by simultaneously laser ablating silicon, for example, and thermal evaporating an alkali metal into an oxygen environment. For example, the compound thin film may be composed of Si/Cs/O. The work functions of the thin films can be varied by changing the silicon/alkali metal/oxygen ratio. Low work functions of the compound thin films deposited on silicon substrates were confirmed by ultraviolet photoelectron spectroscopy (UPS). The compound thin films are stable up to 500.degree. C. as measured by x-ray photoelectron spectroscopy (XPS). Tests have established that for certain chemical compositions and annealing temperatures of the compound thin films, negative electron affinity (NEA) was detected. The low work function, stable compound thin films can be utilized in solar cells, field emission flat panel displays, electron guns, and cold cathode electron guns.

Effects on crystal structure of CZTS thin films owing to deionized water and sulfurization treatment

DOE Office of Scientific and Technical Information (OSTI.GOV)

Nadi, Samia Ahmed; Chelvanathan, Puvaneswaran; Islam, M. A.

2015-05-15

To condense the cost and increase the production, using abundantly obtainable non-toxic elements, Cu{sub 2}ZnSnS{sub 4} (CZTS) seem to be a strong contender among the photovoltaic thin film technologies. Cu{sub 2}ZnSnS{sub 4} thin films were fabricated by RF magnetron sputtering system. CZTS were sputtered on Molybdenum (Mo) coated soda lime glass (SLG) using a single target sputtering technique. The sputtering parameters (base pressure, working pressure, Argon (Ar) flow rate, RF power and sputtering time) were kept same for all three types of films. For sulfurization, the temperature used was 500 °C. Finally, As-deposited film was immersed in DIW before undergoingmore » identical sulfurization profile. As-deposited film (Sample A), sulfurized films (Sample B) and sulfurized plus DIW treated (Sample C) were compared in terms of their structural properties by means of X-Ray Diffraction (XRD) measurement and Atomic Force Microscopy (AFM). Sample B and C showed peak of (1 1 2) planes of CZTS which are characteristics of stannite structure. Post deposition treatment on CZTS films proved to be beneficial as evident from the observed enhancement in the crystallinity and grain growth. Significant difference on grain size and area roughness could be observed from the AFM measurement. The roughness of Sample A, B and C increased from 5.007 nm to 20.509 nm and 14.183 nm accordingly. From XRD data secondary phases of Cu{sub x}MoS{sub x} could be observed.« less

Influence of spray time on the optical and electrical properties of CoNi2S4 thin films

NASA Astrophysics Data System (ADS)

El Radaf, I. M.; Fouad, S. S.; Ismail, A. M.; Sakr, G. B.

2018-04-01

In this paper, a facile spray pyrolysis technique was utilized to synthesize CoNi2S4 thin films. The influence of spray time on the structural, optical and electrical properties of the CoNi2S4 thin films was studied. The x-ray diffraction studies of the CoNi2S4 thin films illustrate that the films exhibit a polycrystalline nature with cubic structure. The values of the lattice strain ε, and the dislocation density δ, were decreased as the spray time increase while the grain size has reverse manner to lattice strain ε, and the dislocation density δ. The transmittance and reflectance spectra of the CoNi2S4 thin films were recorded in the wavelength range of (400–2500) nm to evaluate the optical parameters of the CoNi2S4 thin films. Optical absorption coefficient of CoNi2S4 thin films revealed a presence of a direct energy gap and the values of energy gap were decreased from 1.68 to 1.53 eV as the spray time increases from 15 min to 45 min. The nonlinear refractive index of the CoNi2S4 thin films was increased with increasing of the spray time. The CoNi2S4 thin films exhibit single activation energy and the activation energy was decreased as the spray time increased.

Synthesis of Cu2ZnSnS4 thin films by a precursor solution paste for thin film solar cell applications.

PubMed

Cho, Jin Woo; Ismail, Agus; Park, Se Jin; Kim, Woong; Yoon, Sungho; Min, Byoung Koun

2013-05-22

Cu2ZnSnS4 (CZTS) is a very promising semiconductor material when used for the absorber layer of thin film solar cells because it consists of only abundant and inexpensive elements. In addition, a low-cost solution process is applicable to the preparation of CZTS absorber films, which reduces the cost when this film is used for the production of thin film solar cells. To fabricate solution-processed CZTS thin film using an easily scalable and relatively safe method, we suggest a precursor solution paste coating method with a two-step heating process (oxidation and sulfurization). The synthesized CZTS film was observed to be composed of grains of a size of ~300 nm, showing an overall densely packed morphology with some pores and voids. A solar cell device with this film as an absorber layer showed the highest efficiency of 3.02% with an open circuit voltage of 556 mV, a short current density of 13.5 mA/cm(2), and a fill factor of 40.3%. We also noted the existence of Cd moieties and an inhomogeneous Zn distribution in the CZTS film, which may have been triggered by the presence of pores and voids in the CZTS film.

Molecular beam epitaxy growth of SmB6+/-δ thin films

NASA Astrophysics Data System (ADS)

Hoffman, Jason; Saleem, Muhammad; Day, James; Bonn, Doug; Hoffman, Jennifer

SmB6 has emerged as a leading candidate in the search for exotic topological states generated by strong interactions. The synthesis of epitaxial SmB6 thin films presents new avenues to control surface termination, thickness, and strain in this system. In this work, we use molecular beam epitaxy (MBE) to deposit SmB6+/-δ films on insulating (001)-oriented MgO substrates. We use ex-situ x-ray diffraction and magnetotransport measurements to assess the properties of the samples and compare them to previously reported values for single crystals. We also discuss the prospects of using rare-earth substitution to control the correlation strength and alter the topology of the bulk and surface electronic states.

Barium ferrite thin-film recording media

NASA Astrophysics Data System (ADS)

Sui, Xiaoyu; Scherge, Matthias; Kryder, Mark H.; Snyder, John E.; Harris, Vincent G.; Koon, Norman C.

1996-03-01

Both longitudinal and perpendicular barium ferrite thin films are being pursued as overcoatless magnetic recording media. In this paper, prior research on thin-film Ba ferrite is reviewed and the most recent results are presented. Self-textured high-coercivity longitudinal Ba ferrite thin films have been achieved using conventional rf diode sputtering. Microstructural studies show that c-axis in-plane oriented grains have a characteristic acicular shape, while c-axis perpendicularly oriented grains have a platelet shape. Extended X-ray absorption fine structure (EXAFS) measurements indicate that the crystal orientations are predetermined by the structural anisotropy in the as-sputtered 'amorphous' state. Recording tests on 1500 Oe coercivity longitudinal Ba ferrite disks show performance comparable with that of a 1900 Oe Co alloy disk. To further improve the recording performance, both grain size and aspect ratio need to be reduced. Initial tribological tests indicate high hardness of Ba ferrite thin films. However, surface roughness needs to be reduced. For future ultrahigh-density contact recording, it is believed that perpendicular recording may be used. A thin Pt underlayer has been found to be capable of producing Ba ferrite thin films with excellent c-axis perpendicular orientation.

Electroactive species-doped poly(3,4-ethylenedioxythiophene) films: enhanced sensitivity for electrochemical simultaneous determination of vitamins B2, B6 and C.

PubMed

Nie, Tao; Xu, Jing-Kun; Lu, Li-Min; Zhang, Kai-Xin; Bai, Ling; Wen, Yang-Ping

2013-12-15

Herein, functionalized PEDOT films were prepared by incorporation of two electroactive species, ferrocenecarboxylic acid (Fc(-)) and ferricyanide (Fe(CN)6(4-)) as doping anions during the electropolymerization of PEDOT at glassy carbon electrodes (GCEs) from aqueous solution. The electrochemically synthesized electroactive species-doped PEDOT films have been carefully characterized by scanning electron microscopy (SEM), FTIR and UV/Vis spectra and various electrochemical techniques. Such nanostructured films combined the advantages of PEDOT (high conductivity and stability) together with electroactive species (good electrochemical activity) and were applied as electrochemical sensors for simultaneous determination of vitamin B2 (VB2), vitamin B6 (VB6) and vitamin C (VC). The results showed that the oxidation peak currents of vitamins obtained at the GCEs modified with electroactive species-doped PEDOT films were much higher than those at the ClO4(-)-doped PEDOT films and bare GCEs. The experiment results also illustrated that the sensors possessed high selectivity with no interference from other potential competing species. Moreover, the proposed sensors were successfully employed for the determination of vitamins in orange juice samples with satisfactory results. Crown Copyright © 2013. Published by Elsevier B.V. All rights reserved.

Characteristics of Iron-Palladium alloy thin films deposited by magnetron sputtering

NASA Astrophysics Data System (ADS)

Chiu, Y.-J.; Shen, C.-Y.; Chang, H.-W.; Jian, S.-R.

2018-06-01

The microstructural features, magnetic, nanomechanical properties and wettability behaviors of Iron-Palladium (FePd) alloy thin films are investigated by using X-ray diffraction (XRD), atomic force microscopy (AFM), vibrating sample magnetometer (VSM), nanoindentation and water contact angle (CA) techniques, respectively. The FePd alloy thin films were deposited on glass substrates using a magnetron sputtering system. The post-annealing processes of FePd alloy thin films were carried out at 400 °C and 750 °C and resulted in a significant increase of both the average grain size and surface roughness. The XRD analysis showed that FePd alloy thin films exhibited a predominant (1 1 1) orientation. The magnetic field dependence of magnetization of all FePd thin films are measured at room temperature showed the ferromagnetic characteristics. The nanoindentation with continuous stiffness measurement (CSM) is used to measure the hardness and Young's modulus of present films. The contact angle (θCA) increased with increasing surface roughness. The maximum θCA of 75° was achieved for the FePd alloy thin film after annealing at 750 °C and a surface roughness of 4.2 nm.

Highly polarized single-c-domain single-crystal Pb(Mn,Nb)O(3)-PZT thin films.

PubMed

Wasa, Kiyotaka; Adachi, Hideaki; Nishida, Ken; Yamamoto, Takashi; Matsushima, Tomoaki; Kanno, Isaku; Kotera, Hidetoshi

2012-01-01

In-plane unstrained single-c-domain/single-crystal thin films of PZT-based ternary ferroelectric perovskite, ξPb(Mn,Nb)O3-(1 - ξ)PZT, were grown on SrRuO(3)/Pt/MgO substrates using magnetron sputtering followed by quenching. The sputtered unstrained thin films exhibit unique ferroelectric properties: high coercive field, Ec > 180 kV/cm, large remanent polarization, P(r) = 100 μC/cm(2), small relative dielectric constants, ε* = 100 to 150, high Curie temperature, Tc = ~600 °C, and bulk-like large transverse piezoelectric constants, e31,f = -12.0 C/m(2) for PZT(48/52) at ξ = 0.06. The unstrained thin films are an ideal structure to extract the bulk ferroelectric properties. Their micro-structures and ferroelectric properties are discussed in relation to the potential applications for piezoelectric MEMS. © 2012 IEEE

Perovskite phase thin films and method of making

DOEpatents

Boyle, Timothy J.; Rodriguez, Mark A.

2000-01-01

The present invention comprises perovskite-phase thin films, of the general formula A.sub.x B.sub.y O.sub.3 on a substrate, wherein A is selected from beryllium, magnesium, calcium, strontium, and barium or a combination thereof; B is selected from niobium and tantalum or a combination thereof; and x and y are mole fractions between approximately 0.8 and 1.2. More particularly, A is strontium or barium or a combination thereof and B is niobium or tantalum or a combination thereof. Also provided is a method of making a perovskite-phase thin film, comprising combining at least one element-A-containing compound, wherein A is selected from beryllium, magnesium, calcium, strontium or barium, with at least one element-B-containing compound, wherein B niobium or tantalum, to form a solution; adding a solvent to said solution to form another solution; spin-coating the solution onto a substrate to form a thin film; and heating the film to form the perovskite-phase thin film.

Polarization-Dependent Raman Spectroscopy of Epitaxial TiO 2 (B) Thin Films

DOE Office of Scientific and Technical Information (OSTI.GOV)

Jokisaari, Jacob R.; Bayerl, Dylan; Zhang, Kui

2015-12-08

The bronze polymorph of titanium dioxide, known as TiO 2(B), has promising photochemical and electronic properties for potential applications in Li-ion batteries, photocatalysis, chemical sensing, and solar cells. In contrast to previous studies performed with powder samples, which often suffer from impurities and lattice water, here we report Raman spectra from highly crystalline TiO 2(B) films epitaxially grown on Si substrates with a thin SrTiO 3 buffer layer. The reduced background from the Si substrate significantly benefits acquisition of polarization-dependent Raman spectra collected from the high-quality thin films, which are compared to nanopowder results reported in the literature. The experimentalmore » spectra were compared with density functional theory calculations to analyze the atomic displacements associated with each Raman-active vibrational mode. These results provide a standard reference for further investigation of the crystallinity, structure, composition, and properties of TiO 2(B) materials with Raman spectroscopy.« less

Investigation of microstructure, micro-mechanical and optical properties of HfTiO{sub 4} thin films prepared by magnetron co-sputtering

DOE Office of Scientific and Technical Information (OSTI.GOV)

Mazur, Michal, E-mail: michal.mazur@pwr.edu.pl; Wojcieszak, Damian; Domaradzki, Jaroslaw

2015-12-15

Highlights: • HfTiO{sub 4} thin films were deposited by magnetron co-sputtering. • As-prepared and annealed at 800 °C thin films were nanocrystalline. • Optical properties and hardness were investigated in relation to thin films structure. • Hardness was 3-times higher in the case of as-deposited thin films. • HfTiO{sub 4} thin films are suitable for use as optical coatings with protective properties. - Abstract: Titania (TiO{sub 2}) and hafnium oxide (HfO{sub 2}) thin films are in the focus of interest to the microelectronics community from a dozen years. Because of their outstanding properties like, among the others, high stability, highmore » refractive index, high electric permittivity, they found applications in many optical and electronics domains. In this work discussion on the hardness, microstructure and optical properties of as-deposited and annealed HfTiO{sub 4} thin films has been presented. Deposited films were prepared using magnetron co-sputtering method. Performed investigations revealed that as-deposited coatings were nanocrystalline with HfTiO{sub 4} structure. Deposited films were built from crystallites of ca. 4–12 nm in size and after additional annealing an increase in crystallites size up to 16 nm was observed. Micro-mechanical properties, i.e., hardness and elastic modulus were determined using conventional load-controlled nanoindentation testing. the annealed films had 3-times lower hardness as-compared to as-deposited ones (∼9 GPa). Based on optical investigations real and imaginary components of refractive index were calculated, both for as-deposited and annealed thin films. The real refractive index component increased after annealing from 2.03 to 2.16, while extinction coefficient increased by an order from 10{sup −4} to 10{sup −3}. Structure modification was analyzed together with optical energy band-gap, Urbach energy and using Wemple–DiDomenico model.« less

Enhanced electrical properties in bilayered ferroelectric thin films

NASA Astrophysics Data System (ADS)

Zhang, Hao; Long, WeiJie; Chen, YaQing; Guo, DongJie

2013-03-01

Sr2Bi4Ti5O18 (SBTi) single layered and Sr2Bi4Ti5O18/Pb(Zr0.53Ti0.47)O3 (SBTi/PZT) bilayered thin films have been prepared on Pt/TiO2/SiO2/Si substrates by pulsed-laser deposition (PLD). The related structural characterizations and electrical properties have been comparatively investigated. X-ray diffraction reveals that both films have crystallized into perovskite phases and scanning electron microscopy shows the sharp interfaces. Both films show well-saturated ferroelectric hysteresis loops, however, compared with the single layered SBTi films, the SBTi/PZT bilayered films have significantly increased remnant polarization ( P r) and decreased coercive field ( E c), with the applied field of 260 kV/cm. The measured P r and E c of SBTi and SBTi/PZT films were 7.9 μC/cm2, 88.1 kV/cm and 13.0 μC/cm2, 51.2 kV/cm, respectively. In addition, both films showed good fatigue-free characteristics, the switchable polarization decreased by 9% and 11% of the initial values after 2.2×109 switching cycles for the SBTi single layered films and the SBTi/PZT bilayered films, respectively. Our results may provide some guidelines for further optimization of multilayered ferroelectric thin films.

Method of producing amorphous thin films

DOEpatents

Brusasco, Raymond M.

1992-01-01

Disclosed is a method of producing thin films by sintering which comprises: a. coating a substrate with a thin film of an inorganic glass forming parulate material possessing the capability of being sintered, and b. irridiating said thin film of said particulate material with a laser beam of sufficient power to cause sintering of said material below the temperature of liquidus thereof. Also disclosed is the article produced by the method claimed.

Engineering epitaxial γ-Al2O3 gate dielectric films on 4H-SiC

NASA Astrophysics Data System (ADS)

Tanner, Carey M.; Toney, Michael F.; Lu, Jun; Blom, Hans-Olof; Sawkar-Mathur, Monica; Tafesse, Melat A.; Chang, Jane P.

2007-11-01

The formation of epitaxial γ-Al2O3 thin films on 4H-SiC was found to be strongly dependent on the film thickness. An abrupt interface was observed in films up to 200 Å thick with an epitaxial relationship of γ-Al2O3(111)‖4H-SiC(0001) and γ-Al2O3(44¯0)‖4H-SiC(112¯0). The in-plane alignment between the film and the substrate is nearly complete for γ-Al2O3 films up to 115 Å thick, but quickly diminishes in thicker films. The films are found to be slightly strained laterally in tension; the strain increases with thickness and then decreases in films thicker than 200 Å, indicating strain relaxation which is accompanied by increased misorientation. By controlling the structure of ultrathin Al2O3 films, metal-oxide-semiconductor capacitors with Al2O3 gate dielectrics on 4H-SiC were found to have a very low leakage current density, suggesting suitability of Al2O3 for SiC device integration.

Optical constants, dispersion energy parameters and dielectric properties of ultra-smooth nanocrystalline BiVO4 thin films prepared by rf-magnetron sputtering

NASA Astrophysics Data System (ADS)

Sarkar, S.; Das, N. S.; Chattopadhyay, K. K.

2014-07-01

BiVO4 thin films have been prepared through radio frequency (rf) magnetron sputtering of a pre-fabricated BiVO4 target on ITO coated glass (ITO-glass) substrate and bare glass substrates. BiVO4 target material was prepared through solid-state reaction method by heating Bi2O3 and V2O5 mixture at 800 °C for 8 h. The films were characterized by X-ray diffraction, UV-Vis spectroscopy, LCR meter, field emission scanning electron microscopy, transmission electron microscopy and atomic force microscopy. BiVO4 thin films deposited on the ITO-glass substrate are much smoother compared to the thin films prepared on bare glass substrate. The rms surface roughness calculated from the AFM images comes out to be 0.74 nm and 4.2 nm for the films deposited on the ITO-glass substrate and bare glass substrate for the deposition time 150 min respectively. Optical constants and energy dispersion parameters of these extra-smooth BiVO4 thin films have been investigated in detail. Dielectric properties of the BiVO4 thin films on ITO-glass substrate were also investigated. The frequency dependence of dielectric constant of the BiVO4 thin films has been measured in the frequency range from 20 Hz to 2 MHz. It was found that the dielectric constant increased from 145 to 343 at 20 Hz as the film thickness increased from 90 nm to 145 nm (deposition time increased from 60 min to 150 min). It shows higher dielectric constant compared to the literature value of BiVO4.

Nanocrystalline Pd:NiFe2O4 thin films: A selective ethanol gas sensor

NASA Astrophysics Data System (ADS)

Rao, Pratibha; Godbole, R. V.; Bhagwat, Sunita

2016-10-01

In this work, Pd:NiFe2O4 thin films were investigated for the detection of reducing gases. These films were fabricated using spray pyrolysis technique and characterized using X-ray diffraction (XRD) to confirm the crystal structure. The surface morphology was studied using scanning electron microscopy (SEM). Magnetization measurements were carried out using SQUID VSM, which shows ferrimagnetic behavior of the samples. These thin film sensors were tested against methanol, ethanol, hydrogen sulfide and liquid petroleum gas, where they were found to be more selective to ethanol. The fabricated thin film sensors exhibited linear response signal for all the gases with concentrations up to 5 w/o Pd. Reduction in optimum operating temperature and enhancement in response was also observed. Pd:NiFe2O4 thin films exhibited faster response and recovery characteristic. These sensors have potential for industrial applications because of their long-term stability, low power requirement and low production cost.

Carbon Nanotube Thin-Film Antennas.

PubMed

Puchades, Ivan; Rossi, Jamie E; Cress, Cory D; Naglich, Eric; Landi, Brian J

2016-08-17

Multiwalled carbon nanotube (MWCNT) and single-walled carbon nanotube (SWCNT) dipole antennas have been successfully designed, fabricated, and tested. Antennas of varying lengths were fabricated using flexible bulk MWCNT sheet material and evaluated to confirm the validity of a full-wave antenna design equation. The ∼20× improvement in electrical conductivity provided by chemically doped SWCNT thin films over MWCNT sheets presents an opportunity for the fabrication of thin-film antennas, leading to potentially simplified system integration and optical transparency. The resonance characteristics of a fabricated chlorosulfonic acid-doped SWCNT thin-film antenna demonstrate the feasibility of the technology and indicate that when the sheet resistance of the thin film is >40 ohm/sq no power is absorbed by the antenna and that a sheet resistance of <10 ohm/sq is needed to achieve a 10 dB return loss in the unbalanced antenna. The dependence of the return loss performance on the SWCNT sheet resistance is consistent with unbalanced metal, metal oxide, and other CNT-based thin-film antennas, and it provides a framework for which other thin-film antennas can be designed.

High-Throughput Synthesis and Characterization of Eu Doped Ba xSr2- xSiO4 Thin Film Phosphors.

PubMed

Frost, Sara; Guérin, Samuel; Hayden, Brian E; Soulié, Jean-Philippe; Vian, Chris

2018-06-20

High-throughput techniques have been employed for the synthesis and characterization of thin film phosphors of Eu-doped Ba x Sr 2- x SiO 4 . Direct synthesis from evaporation of the constituent elements under a flux of atomic oxygen on a sapphire substrate at 850 °C was used to directly produce thin film libraries (415 nm thickness) of the crystalline orthosilicate phase with the desired compositional variation (0.24 > x > 1.86). The orthosilicate phase could be synthesized as a pure, or predominantly pure, phase. Annealing the as synthesized library in a reducing atmosphere resulted in the reduction of the Eu while retaining the orthosilicate phase, and resulted in a materials thin film library where fluorescence excited by blue light (450 nm) was observable by the naked eye. Parallel screening of the fluorescence from the combinatorial libraries of Eu doped Ba x Sr 2- x SiO 4 has been implemented by imaging the fluorescent radiation over the library using a monochrome digital camera using a series of color filters. Informatics tools have been developed to allow the 1931 CIE color coordinates and the relative quantum efficiencies of the materials library to be rapidly assessed and mapped against composition, crystal structure and phase purity. The range of compositions gave values of CIE x between 0.17 and 0.52 and CIE y between 0.48 and 0.69 with relative efficiencies in the range 2.0 × 10 -4 -7.6 × 10 -4 . Good agreement was obtained between the thin film phosphors and the fluorescence characteristics of a number of corresponding bulk phosphor powders. The thermal quenching of fluorescence in the thin film libraries was also measured in the temperature range 25-130 °C: The phase purity of the thin film was found to significantly influence both the relative quantum efficiency and the thermal quenching of the fluorescence.

Characterization of aluminum selenide bi-layer thin film

NASA Astrophysics Data System (ADS)

Boolchandani, Sarita; Soni, Gyanesh; Srivastava, Subodh; Vijay, Y. K.

2018-05-01

The Aluminum Selenide (AlSe) bi-layer thin films were grown on glass substrate using thermal evaporation method under high vacuum condition. The morphological characterization was done using SEM. Electrical measurement with temperature variation shows that thin films exhibit the semiconductor nature. The optical properties of prepared thin films have also been characterized by UV-VIS spectroscopy measurements. The band gap of composite thin films has been calculated by Tauc's relation at different temperature ranging 35°C-100°C.

Lanthanum aluminum oxide thin-film dielectrics from aqueous solution.

PubMed

Plassmeyer, Paul N; Archila, Kevin; Wager, John F; Page, Catherine J

2015-01-28

Amorphous LaAlO3 dielectric thin films were fabricated via solution processing from inorganic nitrate precursors. Precursor solutions contained soluble oligomeric metal-hydroxyl and/or -oxo species as evidenced by dynamic light scattering (DLS) and Raman spectroscopy. Thin-film formation was characterized as a function of annealing temperature using Fourier transform infrared (FTIR), X-ray diffraction (XRD), X-ray reflectivity (XRR), scanning electron microscopy (SEM), and an array of electrical measurements. Annealing temperatures ≥500 °C result in thin films with low leakage-current densities (∼1 × 10(-8) A·cm(-2)) and dielectric constants ranging from 11.0 to 11.5. When incorporated as the gate dielectric layer in a-IGZO thin-film transistors (TFTs), LaAlO3 thin films annealed at 600 °C in air yielded TFTs with relatively low average mobilities (∼4.5 cm(2)·V(-1)·s(-1)) and high turn-on voltages (∼26 V). Interestingly, reannealing the LaAlO3 in 5%H2/95%N2 at 300 °C before deposition of a-IGZO channel layers resulted in TFTs with increased average mobilities (11.1 cm(2)·V(-1)·s(-1)) and lower turn-on voltages (∼6 V).

Uncooled thin film pyroelectric IR detector with aerogel thermal isolation

DOEpatents

Ruffner, Judith A.; Bullington, Jeff A.; Clem, Paul G.; Warren, William L.; Brinker, C. Jeffrey; Tuttle, Bruce A.; Schwartz, Robert W.

1999-01-01

A monolithic infrared detector structure which allows integration of pyroelectric thin films atop low thermal conductivity aerogel thin films. The structure comprises, from bottom to top, a substrate, an aerogel insulating layer, a lower electrode, a pyroelectric layer, and an upper electrode layer capped by a blacking layer. The aerogel can offer thermal conductivity less than that of air, while providing a much stronger monolithic alternative to cantilevered or suspended air-gap structures for pyroelectric thin film pixel arrays. Pb(Zr.sub.0.4 Ti.sub.0.6)O.sub.3 thin films deposited on these structures displayed viable pyroelectric properties, while processed at 550.degree. C.

Synthesis and characterization of novel 4-Tetra-4-Tolylsulfonyl ZnPc thin films for optoelectronic applications

NASA Astrophysics Data System (ADS)

Khalil, Salah; Tazarki, Helmi; Souli, Mehdi; Guasch, Cathy; Jamoussi, Bassem; Kamoun, Najoua

2017-11-01

Novel 4-Tetra-4-Tolylsulfonyl:zinc phthalocyanine and simple zinc phthalocyanine were synthesized. Our materials were grown on glass substrates by spin coating technique. Thin films were characterized by X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), scanning electronic micrograph (SEM), atomic force microscopy (AFM), spectrophotometer and Hall effect measurement. X-ray spectra reveal that 4-Tetra-4-Tolylsulfonyl:zinc phthalocyanine (4T4TS:ZnPc) and zinc phthalocyanine (ZnPc) thin films have a monoclinic crystalline structure in β phase. The surface properties and chemical composition were detailed using XPS measurement. SEM were used to investigate the surface morphology for 4T4TS:ZnPc and ZnPc thin films. Atomic force microscopy images have shown a decrease in surface roughness after substitution. Optical properties were investigated by measuring transmission and reflection spectra. Electrical properties were studied and the different electrical parameters was measured and compared on glass, silicon and tin dioxide substrates by Hall Effect technique. All obtained results indicate an improvement in physical properties of 4T4TS:ZnPc which allows used it in optoelectronic applications.

PEALD grown high-k ZrO{sub 2} thin films on SiC group IV compound semiconductor

DOE Office of Scientific and Technical Information (OSTI.GOV)

Khairnar, A. G., E-mail: agkhairnar@gmail.com; Patil, V. S.; Agrawal, K. S.

The study of ZrO{sub 2} thin films on SiC group IV compound semiconductor has been studied as a high mobility substrates. The ZrO{sub 2} thin films were deposited using the Plasma Enhanced Atomic Layer Deposition System. The thickness of the thin films were measured using ellipsometer and found to be 5.47 nm. The deposited ZrO{sub 2} thin films were post deposition annealed in rapid thermal annealing chamber at temperature of 400°Ð¡. The atomic force microscopy and X-гау photoelectron spectroscopy has been carried out to study the surface topography, roughness and chemical composition of thin film, respectively.

Blending crystalline/liquid crystalline small molecule semiconductors: A strategy towards high performance organic thin film transistors

NASA Astrophysics Data System (ADS)

He, Chao; He, Yaowu; Li, Aiyuan; Zhang, Dongwei; Meng, Hong

2016-10-01

Solution processed small molecule polycrystalline thin films often suffer from the problems of inhomogeneity and discontinuity. Here, we describe a strategy to solve these problems through deposition of the active layer from a blended solution of crystalline (2-phenyl[1]benzothieno[3,2-b][1]benzothiophene, Ph-BTBT) and liquid crystalline (2-(4-dodecylphenyl) [1]benzothieno[3,2-b]benzothiophene, C12-Ph-BTBT) small molecule semiconductors with the hot spin-coating method. Organic thin film transistors with average hole mobility approaching 1 cm2/V s, much higher than that of single component devices, have been demonstrated, mainly due to the improved uniformity, continuity, crystallinity, and stronger intermolecular π-π stacking in blend thin films. Our results indicate that the crystalline/liquid crystalline semiconductor blend method is an effective way to enhance the performance of organic transistors.

Structural and magnetic analysis of Cu, Co substituted NiFe2O4 thin films

NASA Astrophysics Data System (ADS)

Sharma, Hakikat; Bala, Kanchan; Negi, N. S.

2016-05-01

In the present work we prepared NiFe2O4, Ni0.95Cu0.05Fe2O4 and Ni0.94Cu0.05Co0.01 Fe2O4 thin films by metallo-organic decomposition method (MOD) using spin coating technique. The thin films were analyzed by X-ray diffractometer (XRD) and Atomic force microscope (AFM) for structural studies. The XRD patterns confirmed the ferrite phase of thin films. From AFM, we analyzed surface morphology, calculated grain size (GS) and root mean square roughness (RMSR). Room temperature magnetic properties were investigated by vibrating sample magnetometer (VSM).

Structure disorder degree of polysilicon thin films grown by different processing: Constant C from Raman spectroscopy

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wang, Quan, E-mail: wangq@mail.ujs.edu.cn; State Key Laboratory of Solid Lubrication, Lanzhou Institute of Chemical Physics, Chinese Academy of Sciences, Lanzhou 730000; Zhang, Yanmin

2013-11-14

Flat, low-stress, boron-doped polysilicon thin films were prepared on single crystalline silicon substrates by low pressure chemical vapor deposition. It was found that the polysilicon films with different deposition processing have different microstructure properties. The confinement effect, tensile stresses, defects, and the Fano effect all have a great influence on the line shape of Raman scattering peak. But the effect results are different. The microstructure and the surface layer are two important mechanisms dominating the internal stress in three types of polysilicon thin films. For low-stress polysilicon thin film, the tensile stresses are mainly due to the change of microstructuremore » after thermal annealing. But the tensile stresses in flat polysilicon thin film are induced by the silicon carbide layer at surface. After the thin film doped with boron atoms, the phenomenon of the tensile stresses increasing can be explained by the change of microstructure and the increase in the content of silicon carbide. We also investigated the disorder degree states for three polysilicon thin films by analyzing a constant C. It was found that the disorder degree of low-stress polysilicon thin film larger than that of flat and boron-doped polysilicon thin films due to the phase transformation after annealing. After the flat polysilicon thin film doped with boron atoms, there is no obvious change in the disorder degree and the disorder degree in some regions even decreases.« less

Semiconductor-insulator transition in VO{sub 2} (B) thin films grown by pulsed laser deposition

DOE Office of Scientific and Technical Information (OSTI.GOV)

Rúa, Armando; Díaz, Ramón D.; Lysenko, Sergiy

2015-09-28

Thin films of B-phase VO{sub 2} were grown by pulsed-laser deposition on glass and (100)-cut MgO substrates in a temperature range from 375 to 425 °C and at higher gas pressures than usual for this technique. The films were strongly oriented, with ab-planes parallel to the substrate surface. Detailed study of surface morphology through Atomic Force Microscopy images suggest significant differences in evolution as a function of growth temperature for films on the two types of substrates. Measurements of electrical conductivities through cooling-heating cycles from room temperature to 120 K showed changes of five orders of magnitude, with steeper changes between roommore » temperature and ∼150 K, which corresponds with the extended and reversible phase transition known to occur for this material. At lower temperatures conductivities exhibited Arrhenius behavior, indicating that no further structural change was occurring and that conduction is thermally activated. In this lower temperature range, conductivity of the samples can be described by the near-neighbor hopping model. No hysteresis was found between the cooling and heating braches of the cycles, which is at variance with previous results published for VO{sub 2} (B). This apparent lack of hysteresis for thin films grown in the manner described and the large conductivity variation as a function of temperature observed for the samples suggests this material could be of interest for infrared sensing applications.« less

Multilayer SnSb4-SbSe Thin Films for Phase Change Materials Possessing Ultrafast Phase Change Speed and Enhanced Stability.

PubMed

Liu, Ruirui; Zhou, Xiao; Zhai, Jiwei; Song, Jun; Wu, Pengzhi; Lai, Tianshu; Song, Sannian; Song, Zhitang

2017-08-16

A multilayer thin film, comprising two different phase change material (PCM) components alternatively deposited, provides an effective means to tune and leverage good properties of its components, promising a new route toward high-performance PCMs. The present study systematically investigated the SnSb 4 -SbSe multilayer thin film as a potential PCM, combining experiments and first-principles calculations, and demonstrated that these multilayer thin films exhibit good electrical resistivity, robust thermal stability, and superior phase change speed. In particular, the potential operating temperature for 10 years is shown to be 122.0 °C and the phase change speed reaches 5 ns in the device test. The good thermal stability of the multilayer thin film is shown to come from the formation of the Sb 2 Se 3 phase, whereas the fast phase change speed can be attributed to the formation of vacancies and a SbSe metastable phase. It is also demonstrated that the SbSe metastable phase contributes to further enhancing the electrical resistivity of the crystalline state and the thermal stability of the amorphous state, being vital to determining the properties of the multilayer SnSb 4 -SbSe thin film.

All-Ceramic Thin Film Battery

DOE Office of Scientific and Technical Information (OSTI.GOV)

BOYLE, TIMOTHY J.; INGERSOLL, DAVID; CYGAN, RANDALL T.

2002-11-01

We have undertaken the synthesis of a thin film ''All Ceramic Battery'' (ACB) using solution route processes. Based on the literature and experimental results, we selected SnO{sub 2}, LiCoO{sub 2}, and LiLaTiO{sub 3} (LLT) as the anode, cathode, and electrolyte, respectively. Strain induced by lattice mismatch between the cathode and bottom electrode, as estimated by computational calculations, indicate that thin film orientations for batteries when thicknesses are as low as 500 {angstrom} are strongly controlled by surface energies. Therefore, we chose platinized silicon as the basal platform based on our previous experience with this material. The anode thin films weremore » generated by standard spin-cast methods and processing using a solution of [Sn(ONep)]{sub 8} and HOAc which was found to form Sn{sub 6}(O){sub 4}(ONep){sub 4}. Electrochemical evaluation showed that the SnO{sub 2} was converted to Sn{sup o} during the first cycle. The cathode was also prepared by spin coating using the novel [Li(ONep)]{sub 8} and Co(OAc){sub 2}. The films could be electrochemically cycled (i.e., charged/discharged), with all of the associated structural changes being observable by XRD. Computational models indicated that the LLT electrolyte would be the best available ceramic material for use as the electrolyte. The LLT was synthesized from [Li(ONep)]{sub 8}, [Ti(ONep){sub 4}]{sub 2}, and La(DIP){sub 3}(py){sub 3} with RTP processing at 900 C being necessary to form the perovskite phase. Alternatively, a novel route to thin films of the block co-polymer ORMOLYTE was developed. The integration of these components was undertaken with each part of the assembly being identifiably by XRD analysis (this will allow us to follow the progress of the charge/discharge cycles of the battery during use). SEM investigations revealed the films were continuous with minimal mixing. All initial testing of the thin-film cathode/electrolyte/anode ACB devices revealed electrical shorting

Analysis of Hard Thin Film Coating

NASA Technical Reports Server (NTRS)

Shen, Dashen

1998-01-01

Marshall Space Flight Center (MSFC) is interested in developing hard thin film coating for bearings. The wearing of the bearing is an important problem for space flight engine. Hard thin film coating can drastically improve the surface of the bearing and improve the wear-endurance of the bearing. However, many fundamental problems in surface physics, plasma deposition, etc, need further research. The approach is using Electron Cyclotron Resonance Chemical Vapor Deposition (ECRCVD) to deposit hard thin film on stainless steel bearing. The thin films in consideration include SiC, SiN and other materials. An ECRCVD deposition system is being assembled at MSFC.

Analysis of Hard Thin Film Coating

NASA Technical Reports Server (NTRS)

Shen, Dashen

1998-01-01

MSFC is interested in developing hard thin film coating for bearings. The wearing of the bearing is an important problem for space flight engine. Hard thin film coating can drastically improve the surface of the bearing and improve the wear-endurance of the bearing. However, many fundamental problems in surface physics, plasma deposition, etc, need further research. The approach is using electron cyclotron resonance chemical vapor deposition (ECRCVD) to deposit hard thin film an stainless steel bearing. The thin films in consideration include SiC, SiN and other materials. An ECRCVD deposition system is being assembled at MSFC.

Enhancement of magnetostrictive properties of Galfenol thin films

NASA Astrophysics Data System (ADS)

Nivedita, Lalitha Raveendran; Manivel, Palanisamy; Pandian, Ramanathaswamy; Murugesan, S.; Morley, Nicola Ann; Asokan, K.; Rajendra Kumar, Ramasamy Thangavelu

2018-04-01

The present study investigates the role of substrate temperatures on the structural, morphological, magnetic and magnetostrictive properties of DC sputtered FeGa thin films grown on Si substrates. These films were deposited at various substrate temperatures between 50 and 350 °C. The structural characterization of the films revealed columnar growth and the transformation of surface morphology from prismatic to spherical at high substrate temperatures. Both L12 and B2 phases of FeGa existed in the films, with the L12 phase dominating. The in-plane and out-of-plane vibration sample magnetometry measurements showed the evolution of magnetic anisotropy in these films. It was revealed from the magnetostriction measurements that the films deposited at 250 °C exhibited the maximum value of 59 ppm.

Formation of Fe2SiO4 thin films on Si substrates and influence of substrate to its thermoelectric transport properties

NASA Astrophysics Data System (ADS)

Choi, Jeongyong; Nguyen, Van Quang; Duong, Van Thiet; Shin, Yooleemi; Duong, Anh Tuan; Cho, Sunglae

2018-03-01

Fe2SiO4 thin films have been grown on n-type, p-type and semi-insulating Si(100) substrates by molecular beam epitaxy. When Fe-O thin films were deposited on Si(100) substrate at 300 °C, the film reacted with Si, resulting in a Fe2SiO4 film because of the high reactivity between Fe and Si. The electrical resistance and Seebeck coefficient of Fe2SiO4 thin films grown were different in different doping states. On n-type and p-type Si(100), the electrical resistance decreased suddenly and increased again at 350 and 250 K, respectively, while on semi-insulating Si(100), it exhibited typical semiconducting resistance behavior. We observed similar crossovers at 350 and 250 K in temperature dependent Seebeck coefficients on n-type and p-type Si(100), respectively. These results suggest that the measured electrical and thermoelectric properties originate from Si substrate.

Long-Wavelength Infrared Sensing by Cytochrome C Protein Thin Film Deposited by the Spin Coating Method

PubMed Central

Lai, Bo-Yu; Chu, Chung-Hao; Su, Guo-Dung John

2013-01-01

High infrared absorption, large temperature coefficient of resistance (TCR) and small 1/f noise are preferred characteristics for sensing materials used in bolometers. In this paper, we discuss a cytochrome c protein as a potential sensing material for long-wavelength bolometers. We simulated and experimentally proved high infrared absorption of cytochrome c in the wavelength between 8 μm and 14 μm. Cytochrome c thin films were deposited on a hydrophilic surface using the spin coating method. The resistance variation with temperature is measured and we show that the TCR of cytochrome c thin films is consistently higher than 20%. The measured values of 1/f noise were as low as 2.33 × 10−13 V2/Hz at 60 Hz. Finally, we test the reliability of cytochrome c by measuring the resistance changes over time under varying conditions. We found that cytochrome c thin films deteriorated significantly without appropriate packaging. PMID:24264331

Effects of europium content on the microstructural and ferroelectric properties of Bi4-xEuxTi3O12 thin films

NASA Astrophysics Data System (ADS)

Zheng, X. J.; He, L.; Zhou, Y. C.; Tang, M. H.

2006-12-01

The effects of europium (Eu) content on the microstructure, fatigue endurance, leakage current density, and remnant polarization (2Pr) of Bi4-xEuxTi3O12 (BET) thin films prepared by metal-organic decomposition method at 700°C annealing temperature were studied in detail. The results showed that 2Pr (82μC/cm2 under 300kV/cm), fatigue endurance (2% loss of 2Pr after 9.0×109 switching cycles), and leakage current density (1×10-8A/cm2 at 200kV/cm) of BET thin film with x =0.85 are better than those of thin films with other contents. Additionally, the mechanism concerning the dependence of ferroelectric properties on Eu content was discussed.

Multi-functional properties of CaCu3Ti4O12 thin films

NASA Astrophysics Data System (ADS)

Felix, A. A.; Rupp, J. L. M.; Varela, J. A.; Orlandi, M. O.

2012-09-01

In this work, electric transport properties of CaCu3Ti4O12 (CCTO) thin films were investigated for resistive switching, rectifying and gas sensor applications. Single phase CCTO thin films were produced by polymeric precursor method (PPM) on different substrates and their electrical properties were studied. Films produced on LNO/Si substrates have symmetrical non-ohmic current-voltage characteristics, while films deposited on Pt/Si substrates have a highly asymmetrical non-ohmic behavior which is related to a metal-semiconductor junction formed at the CCTO/Pt interface. In addition, results confirm that CCTO has a resistive switching response which is enhanced by Schottky contacts. Sensor response tests revealed that CCTO films are sensitive to oxygen gas and exhibit n-type conductivity. These results demonstrate the versatility of CCTO thin film prepared by the PPM method for gas atmosphere or bias dependent resistance applications.

Microstructure of Thin Films

DTIC Science & Technology

1990-02-07

Proceedings, Thin film Technologies II, 652, 256-263, (1986) B. Schmitt, J.P. Borgogno, G. Albrand and E. Pelletier, "In situ and air index measurements...34 SPIE Proceedings, "Optical Components and Systems", 805, 128 (1987) 11 B. Schmitt, J.P. Borgogno, G. Albrand and E. Pelletier. "In situ and air index...aT , m..a, lot,, o ,,f,02,d I4 k -1-1..... autocovariance lengths, less than 0.5 um, indicate that , 514n, ob0 o p’,Ofclllc....,,o,,oy0,1- agua sblrt

High-T sub c thin films on low microwave loss alkaline-rare-earth-aluminate crystals

DOE Office of Scientific and Technical Information (OSTI.GOV)

Sobolewski, R.; Gierlowski, P.; Kula, W.

1991-03-01

This paper reports on the alkaline-rare-earth aluminates (K{sub 2}NiF{sub 4}-type perovskites) which are an excellent choice as the substrate material for the growth of high-T{sub c} thin films suitable for microwave and far-infrared applications. The CaNdAlO{sub 4}, and SrLaAlO{sub 4} single crystals have been grown by Czochralski pulling and fabricated into the form of (001) oriented wafers. The Y-Ba-Cu-O and Bi-Sr-Ca-Cu-O films deposited on these substrates by a single-target magnetron sputtering exhibited very good superconducting and structural properties.

Temperature Behavior of Thin Film Varactor

DTIC Science & Technology

2012-01-01

Temperature Behavior of Thin Film Varactor By Richard X. Fu ARL-TR-5905 January 2012...Thin Film Varactor Richard X. Fu Sensors and Electron Devices Directorate, ARL...DD-MM-YYYY) January 2012 2. REPORT TYPE Final 3. DATES COVERED (From - To) 4. TITLE AND SUBTITLE Temperature Behavior of Thin Film Varactor 5a

Photoluminescence and cathodoluminescence properties of green emitting SrGa2{S}4 : Eu2+ thin film

NASA Astrophysics Data System (ADS)

Chartier, Céline; Benalloul, Paul; Barthou, Charles; Frigerio, Jean-Marc; Mueller, Gerd O.; Mueller-Mach, Regina; Trottier, Troy

2002-02-01

Photoluminescence and cathodoluminescence properties of SrGa2S4 : Eu2+ thin films prepared by reactive RF magnetron sputtering are investigated. Luminescence performances of the phosphor in the thin film form are compared to those of powder samples: the brightness efficiency of thin films is found to be about 30% of the efficiency of powder at low current density. A ratio higher than 40% is expected at higher current density. Thin film screens for FEDs will become a positive alternative to powder screens provided that film quality and light extraction could be improved by optimization of thickness and deposition parameters.

New organic semiconductor thin film derived from p-toluidine monomer

NASA Astrophysics Data System (ADS)

Al-Hossainy, A. F.; Zoromba, M. Sh

2018-03-01

p-Toluidine was used as a precursor to synthesize new organic compound [(E)-4-methyl-N1-((E)-4-methyl-6-(p-tolylimino) cyclohex-3-en-1-ylidene)-N2-(p-tolyl) benzene-1,2-diamine] (MBD) by oxidative reaction via potassium dichromate as oxidizing agent at room temperature. Spin coater was used to fabricate nano-size crystalline thin film of the MBD with thickness 73 nm. The characterizations of the MBD powder and thin film have been described by various techniques including Fourier Transform Infrared (FT-IR), Mass Spectra, X-ray Diffraction (XRD), Scanning Electron Microscope (SEM), UV-Visible measurements and Atomic Force Microscope (AFM). The results revealed that the MBD as an organic material is semi-crystalline containing benzenoid (Bensbnd Nsbnd Ben) and quinonoid (Quin = N = Quin) structures. Various optical constants such as refractive index (n), and the absorption index, (k) of the MBD thin film were determined. The effect of temperature on the electrical resistivity of MBD film was studied by a Keithley 6517B electrometer. The energy band gap value of the MBD thin film was found to be 2.24 eV. Thus, MBD is located in the semiconductor materials range. In addition, structural and optical mechanisms of MBD nanostructured thin film were investigated. The obtained results illustrate the possibility of controlling the organic semiconductor MBD thin film for the optoelectronic applications.

Influence of film thickness and Fe doping on LPG sensing properties of Mn3O4 thin film grown by SILAR method

NASA Astrophysics Data System (ADS)

Belkhedkar, M. R.; Ubale, A. U.

2018-05-01

Nanocrystalline Fe doped and undoped Mn3O4 thin films have been deposited by Successive Ionic Layer Adsorption and Reaction (SILAR) method onto glass substrates using MnCl2 and NaOH as cationic and anionic precursors. The grazing incidence X-ray diffraction (GIXRD) and field emission scanning electron microscopy (FESEM)) have been carried out to analyze structural and surface morphological properties of the films. The LPG sensing performance of Mn3O4thin films have been studied by varying temperature, concentration of LPG, thickness of the film and doping percentage of Fe. The LPG response of the Mn3O4thin films were found to be enhances with film thickness and decreases with increased Fe doping (0 to 8 wt. %) at 573 K temperature.

Growth of C60 thin films on Al2O3/NiAl(100) at early stages

NASA Astrophysics Data System (ADS)

Hsu, S.-C.; Liao, C.-H.; Hung, T.-C.; Wu, Y.-C.; Lai, Y.-L.; Hsu, Y.-J.; Luo, M.-F.

2018-03-01

The growth of thin films of C60 on Al2O3/NiAl(100) at the earliest stage was studied with scanning tunneling microscopy and synchrotron-based photoelectron spectroscopy under ultrahigh-vacuum conditions. C60 molecules, deposited from the vapor onto an ordered thin film of Al2O3/NiAl(100) at 300 K, nucleated into nanoscale rectangular islands, with their longer sides parallel to direction either [010] or [001] of NiAl. The particular island shape resulted because C60 diffused rapidly, and adsorbed and nucleated preferentially on the protrusion stripes of the crystalline Al2O3 surface. The monolayer C60 film exhibited linear protrusions of height 1-3 Å, due to either the structure of the underlying Al2O3 or the lattice mismatch at the boundaries of the coalescing C60 islands; such protrusions governed also the growth of the second layer. The second layer of the C60 film grew only for a C60 coverage >0.60 ML, implying a layer-by-layer growth mode, and also ripened in rectangular shapes. The thin film of C60 was thermally stable up to 400 K; above 500 K, the C60 islands dissociated and most C60 desorbed.

A thin film nitinol heart valve.

PubMed

Stepan, Lenka L; Levi, Daniel S; Carman, Gregory P

2005-11-01

In order to create a less thrombogenic heart valve with improved longevity, a prosthetic heart valve was developed using thin film nitinol (NiTi). A "butterfly" valve was constructed using a single, elliptical piece of thin film NiTi and a scaffold made from Teflon tubing and NiTi wire. Flow tests and pressure readings across the valve were performed in vitro in a pulsatile flow loop. Bio-corrosion experiments were conducted on untreated and passivated thin film nitinol. To determine the material's in vivo biocompatibility, thin film nitinol was implanted in pigs using stents covered with thin film NiTi. Flow rates and pressure tracings across the valve were comparable to those through a commercially available 19 mm Perimount Edwards tissue valve. No signs of corrosion were present on thin film nitinol samples after immersion in Hank's solution for one month. Finally, organ and tissue samples explanted from four pigs at 2, 3, 4, and 6 weeks after thin film NiTi implantation appeared without disease, and the thin film nitinol itself was without thrombus formation. Although long term testing is still necessary, thin film NiTi may be very well suited for use in artificial heart valves.

Dependence of electrical and optical properties of amorphous SiC:H thin films grown by rf plasma enhanced chemical vapor deposition on annealing temperature

NASA Astrophysics Data System (ADS)

Park, M. G.; Choi, W. S.; Hong, B.; Kim, Y. T.; Yoon, D. H.

2002-05-01

In this article, we investigated the dependence of optical and electrical properties of hydrogenated amorphous silicon carbide (a-SiC:H) films on annealing temperature (Ta) and radio frequency (rf) power. The substrate temperature (Ts) was 250 °C, the rf power was varied from 30 to 400 W, and the range of Ta was from 400 to 600 °C. The a-SiC:H films were deposited by using the plasma enhanced chemical vapor deposition system on Corning 7059 glasses and p-type Si (100) wafers with a SiH4+CH4 gas mixture. The experimental results have shown that the optical bandgap energy (Eg) of the a-SiC:H thin films changed little on the annealing temperature while Eg increased with the rf power. The Raman spectrum of the thin films annealed at high temperatures showed that graphitization of carbon clusters and microcrystalline silicon occurs. The current-voltage characteristics have shown good electrical properties in relation to the annealed films.

Superconducting thin-film gyroscope readout for Gravity Probe-B

NASA Technical Reports Server (NTRS)

Lockhart, James M.; Cheung, W. Stephen; Gill, Dale K.

1987-01-01

The high-resolution gyroscope readout system for the Stanford Gravity Probe-B experiment, whose purpose is to measure two general relativistic precessions of gyroscopes in earth orbit, is described. In order to achieve the required resolution in angle (0.001 arcsec), the readout system combines high-precision mechanical fabrication and measurement techniques with superconducting thin-film technology, ultralow magnetic fields, and SQUID detectors. The system design, performance limits achievable with current technology, and the results of fabrication and laboratory testing to date are discussed.

Benzothienobenzothiophene-based conjugated oligomers as semiconductors for stable organic thin-film transistors.

PubMed

Yu, Han; Li, Weili; Tian, Hongkun; Wang, Haibo; Yan, Donghang; Zhang, Jingping; Geng, Yanhou; Wang, Fosong

2014-04-09

Two benzothienobenzothiophene (BTBT)-based conjugated oligomers, i.e., 2,2'-bi[1]benzothieno[3,2-b][1]benzothiophene (1) and 5,5'-bis([1]benzothieno[3,2-b][1]benzothiophen-2-yl)-2,2'-bithiophene (2), were prepared and characterized. Both oligomers exhibit excellent thermal stability, with 5% weight-loss temperatures (T(L)) above 370 °C; no phase transition was observed before decomposition. The highest occupied molecular orbital (HOMO) levels of 1 and 2 are -5.3 and -4.9 eV, respectively, as measured by ultraviolet photoelectron spectroscopy. Thin-film X-ray diffraction and atomic force microscopy characterizations indicate that both oligomers form highly crystalline films with large domain sizes on octadecyltrimethoxysilane-modified substrates. Organic thin-film transistors with top-contact and bottom-gate geometry based on 1 and 2 exhibited mobilities up to 2.12 cm(2)/V·s for 1 and 1.39 cm(2)/V·s for 2 in an ambient atmosphere. 1-based devices exhibited great air and thermal stabilities, as evidenced by the slight performance degradation after 2 months of storage under ambient conditions and after thermal annealing at temperatures below 250 °C.

Bandgap tuning in highly c-axis oriented Zn1-xMgxO thin films

NASA Astrophysics Data System (ADS)

Kumar, Parmod; Malik, Hitendra K.; Ghosh, Anima; Thangavel, R.; Asokan, K.

2013-06-01

We propose Mg doping in zinc oxide (ZnO) films for realizing wider optical bandgap in highly c-axis oriented Zn1-xMgxO (0 ≤ x ≤ 0.3) thin films. A remarkable enhancement of 25% in the bandgap by 30% Mg doping was achieved. The bandgap was tuned between 3.25 eV (ZnO) and 4.06 eV (Zn0.7Mg0.3O), which was further confirmed by density functional theory based wien2k simulation employing a combined generalized gradient approximation with scissor corrections. The change of stress and crystallite size in these films were found to be the causes for the observed blueshift in the bandgap.

Germanium Lift-Off Masks for Thin Metal Film Patterning

NASA Technical Reports Server (NTRS)

Brown, Ari

2012-01-01

A technique has been developed for patterning thin metallic films that are, in turn, used to fabricate microelectronics circuitry and thin-film sensors. The technique uses germanium thin films as lift-off masks. This requires development of a technique to strip or undercut the germanium chemically without affecting the deposited metal. Unlike in the case of conventional polymeric lift-off masks, the substrate can be exposed to very high temperatures during processing (sputter deposition). The reason why polymeric liftoff masks cannot be exposed to very high temperatures (greater than 100 C) is because (a) they can become cross linked, making lift-off very difficult if not impossible, and (b) they can outgas nitrogen and oxygen, which then can react with the metal being deposited. Consequently, this innovation is expected to find use in the fabrication of transition edge sensors and microwave kinetic inductance detectors, which use thin superconducting films deposited at high temperature as their sensing elements. Transition edge sensors, microwave kinetic inductance detectors, and their circuitry are comprised of superconducting thin films, for example Nb and TiN. Reactive ion etching can be used to pattern these films; however, reactive ion etching also damages the underlying substrate, which is unwanted in many instances. Polymeric lift-off techniques permit thin-film patterning without any substrate damage, but they are difficult to remove and the polymer can outgas during thin-film deposition. The outgassed material can then react with the film with the consequence of altered and non-reproducible materials properties, which, in turn, is deleterious for sensors and their circuitry. The purpose of this innovation was to fabricate a germanium lift-off mask to be used for patterning thin metal films.

Thin-film decoupling capacitors for multi-chip modules

NASA Astrophysics Data System (ADS)

Dimos, D.; Lockwood, S. J.; Schwartz, R. W.; Rogers, M. S.

Thin-film decoupling capacitors based on ferroelectric lead lanthanum zirconate titanate (PLZT) films are being developed for use in advanced packages, such as multi-chip modules. These thin-film decoupling capacitors are intended to replace multi-layer ceramic capacitors for certain applications, since they can be more fully integrated into the packaging architecture. The increased integration that can be achieved should lead to decreased package volume and improved high-speed performance, due to a decrease in interconnect inductance. PLZT films are fabricated by spin coating using metal carboxylate/alkoxide solutions. These films exhibit very high dielectric constants ((var epsilon) greater than or equal to 900), low dielectric losses (tan(delta) = 0.01), excellent insulation resistances (rho greater than 10(exp 13) (Omega)-cm at 125 C), and good breakdown field strengths (E(sub B) = 900 kV/cm). For integrated circuit applications, the PLZT dielectric is less than 1 micron thick, which results in a large capacitance/area (8-9 nF/sq mm). The thin-film geometry and processing conditions also make these capacitors suitable for direct incorporation onto integrated circuits and for packages that require embedded components.

Synthesis and characterization of magnesium aluminate (MgAl2O4) spinel (MAS) thin films

NASA Astrophysics Data System (ADS)

Ahmad, Syed Muhammad; Hussain, Tousif; Ahmad, Riaz; Siddiqui, Jamil; Ali, Dilawar

2018-01-01

In a quest to identify more economic routes for synthesis of magnesium aluminate (MgAl2O4) spinel (MAS) thin films, dense plasma focus device was used with multiple plasma focus shots. Structural, bonding between composite films, surface morphological, compositional and hardness properties of MAS thin films were investigated by using x-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), scanning electron microscopy (SEM), energy dispersive x-rays (EDX) analysis and Vickers micro hardness test respectively. In XRD graph, the presence of MgAl2O4 diffraction peaks in crystallographic orientations (222), (400) and (622) pointed out the successful formation of polycrystalline thin films of MgAl2O4 with face centered cubic structure. The FTIR spectrums showed a major common transmittance band at 697.95 cm-1 which belongs to MgAl2O4. SEM micrographs illustrated a mesh type, granular and multi layers microstructures with significant melting effects. EDX spectrum confirmed the existence of magnesium, oxygen and aluminum in MAS films. A common increasing behavior in micro-hardness of composite MgAl2O4 films by increasing number of plasma focus shots was found.

The effect of stoichiometry on Cu-Zn ordering kinetics in Cu2ZnSnS4 thin films

NASA Astrophysics Data System (ADS)

Rudisch, Katharina; Davydova, Alexandra; Platzer-Björkman, Charlotte; Scragg, Jonathan

2018-04-01

Cu-Zn disorder in Cu2ZnSnS4 (CZTS) may be responsible for the large open circuit voltage deficit in CZTS based solar cells. In this study, it was investigated how composition-dependent defect complexes influence the order-disorder transition. A combinatorial CZTS thin film sample was produced with a cation composition gradient across the sample area. The graded sample was exposed to various temperature treatments and the degree of order was analyzed with resonant Raman spectroscopy for various compositions ranging from E- and A-type to B-, F-, and C-type CZTS. We observe that the composition has no influence on the critical temperature of the order-disorder transition, but strongly affects the activation energy. Reduced activation energy is achieved with compositions with Cu/Sn > 2 or Cu/Sn < 1.8 suggesting an acceleration of the cation ordering in the presence of vacancies or interstitials. This is rationalized with reference to the effect of point defects on exchange mechanisms. The implications for reducing disorder in CZTS thin films are discussed in light of the new findings.

Epitaxy of boron phosphide on AlN, 4H-SiC, 3C-SiC and ZrB2 substrates

NASA Astrophysics Data System (ADS)

Padavala, Balabalaji

The semiconductor boron phosphide (BP) has many outstanding features making it attractive for developing various electronic devices, including neutron detectors. In order to improve the efficiency of these devices, BP must have high crystal quality along with the best possible electrical properties. This research is focused on growing high quality crystalline BP films on a variety of superior substrates like AlN, 4H-SiC, 3C-SiC and ZrB2 by chemical vapor deposition. In particular, the influence of various parameters such as temperature, reactant flow rates, and substrate type and its crystalline orientation on the properties of BP films were studied in detail. Twin-free BP films were produced by depositing on off-axis 4H-SiC(0001) substrate tilted 4° toward [11¯00] and crystal symmetry matched zincblende 3C-SiC. BP crystalline quality improved at higher deposition temperature (1200°C) when deposited on AlN, 4H-SiC, whereas increased strain in 3C-SiC and increased boron segregation in ZrB2 at higher temperatures limited the best deposition temperature to below 1200°C. In addition, higher flow ratios of PH 3 to B2H6 resulted in smoother films and improved quality of BP on all substrates. The FWHM of the Raman peak (6.1 cm -1), XRD BP(111) peak FWHM (0.18°) and peak ratios of BP(111)/(200) = 5157 and BP(111)/(220) = 7226 measured on AlN/sapphire were the best values reported in the literature for BP epitaxial films. The undoped films on AlN/sapphire were n-type with a highest electron mobility of 37.8 cm2/V˙s and a lowest carrier concentration of 3.15x1018 cm -3. Raman imaging had lower values of FWHM (4.8 cm-1 ) and a standard deviation (0.56 cm-1) for BP films on AlN/sapphire compared to 4H-SiC, 3C-SiC substrates. X-ray diffraction and Raman spectroscopy revealed residual tensile strain in BP on 4H-SiC, 3C-SiC, ZrB2/4H-SiC, bulk AlN substrates while compressive strain was evident on AlN/sapphire and bulk ZrB2 substrates. Among the substrates studied, Al

Structure and magnetization of Co4N thin film

NASA Astrophysics Data System (ADS)

Pandey, Nidhi; Gupta, Mukul; Gupta, Rachana; Rajput, Parasmani; Stahn, Jochen

2018-02-01

In this work, we studied the local structure and the magnetization of Co4N thin films deposited by a reactive dc magnetron sputtering process. The interstitial incorporation of N atoms in a fcc Co lattice is expected to expand the structure. This expansion yields interesting magnetic properties e.g. a larger magnetic moment (than Co) and a very high value of spin polarization ratio in Co4N . By optimizing the growth conditions, we prepared Co4N film having lattice parameter close to its theoretically predicted value. The N concentration was measured using secondary ion mass spectroscopy. Detailed magnetization measurements using bulk magnetization method and polarized neutron reflectivity confirm that the magnetic moment of Co in Co4N is higher than that of Co.

Thin-film Rechargeable Lithium Batteries

DOE R&D Accomplishments Database

Dudney, N. J.; Bates, J. B.; Lubben, D.

1995-06-01

Thin film rechargeable lithium batteries using ceramic electrolyte and cathode materials have been fabricated by physical deposition techniques. The lithium phosphorous oxynitride electrolyte has exceptional electrochemical stability and a good lithium conductivity. The lithium insertion reaction of several different intercalation materials, amorphous V{sub 2}O{sub 5}, amorphous LiMn{sub 2}O{sub 4}, and crystalline LiMn{sub 2}O{sub 4} films, have been investigated using the completed cathode/electrolyte/lithium thin film battery.

Stretchable, adhesive and ultra-conformable elastomer thin films.

PubMed

Sato, Nobutaka; Murata, Atsushi; Fujie, Toshinori; Takeoka, Shinji

2016-11-16

Thermoplastic elastomers are attractive materials because of the drastic changes in their physical properties above and below the glass transition temperature (T g ). In this paper, we report that free-standing polystyrene (PS, T g : 100 °C) and polystyrene-polybutadiene-polystyrene triblock copolymer (SBS, T g : -70 °C) thin films with a thickness of hundreds of nanometers were prepared by a gravure coating method. Among the mechanical properties of these thin films determined by bulge testing and tensile testing, the SBS thin films exhibited a much lower elastic modulus (ca. 0.045 GPa, 212 nm thickness) in comparison with the PS thin films (ca. 1.19 GPa, 217 nm thickness). The lower elastic modulus and lower thickness of the SBS thin films resulted in higher conformability and thus higher strength of adhesion to an uneven surface such as an artificial skin model with roughness (R a = 10.6 μm), even though they both have similar surface energies. By analyzing the mechanical properties of the SBS thin films, the elastic modulus and thickness of the thin films were strongly correlated with their conformability to a rough surface, which thus led to a high adhesive strength. Therefore, the SBS thin films will be useful as coating layers for a variety of materials.

Magnesium Diboride thin Films, multilayers, and coatings for SRF cavities

DOE Office of Scientific and Technical Information (OSTI.GOV)

Xi, Xiaoxing

Superconducting radio frequency (SRF) cavities currently use low-temperature superconductor niobium, and the Nb SRF cavities have approached the performance levels predicted theoretically. Compared to Nb, MgB 2 becomes superconducting at a much higher temperature and promises a better RF performance in terms of higher quality factor Q and higher acceleration capability. An MgB 2 SRF technology can significantly reduce the operating costs of particle accelerators when these potentials are realized. This project aimed to advance the development of an MgB 2 SRF technology. It had two main objectives: (1) materials issues of MgB 2 thin films and multilayers related tomore » their applications in SRF cavities; and (2) coating single-cell cavities for testing at RF frequencies. The key technical thrust of the project is the deposition of high quality clean MgB 2 films and coatings by the hybrid physical-chemical vapor deposition (HPCVD) technique, which was developed in my group. We have achieved technical progress in each of the two areas. For the first objective, we have confirmed that MgB 2 thin film coatings can be used to effectively enhance the vortex penetration field of an SRF cavity. A vortex is a normal region in the shape of spaghetti that threads through a superconductor. Its existence is due to an applied magnetic field that is greater than a so-called lower critical field, H c1. Once a vortex enters the superconductor, its movement leads to loss. This has been shown to be the reason for an SRF cavity to break down. Thus, enhancing the magnetic field for a vortex to enter the superconductor that forms the SRF cavity has be a goal of intense research. To this end, Gurevich proposed that a coating of thin superconductor layer can impede the vortex entrance. In this project, we have done two important experiment to test this concept. One, we showed that the enhancement of H c1 can be achieved by using in both epitaxial and polycrystalline MgB 2 films

Low thermal diffusivity measurements of thin films using mirage technique

NASA Astrophysics Data System (ADS)

Wong, P. K.; Fung, P. C. W.; Tam, H. L.

1998-12-01

Mirage technique is proved to be powerful in measurements of thermal diffusivity. Its contactless nature makes it suitable for delicate samples such as thin films and single crystals. However, as the damping of the thermal wave profile increases progressively upon the decrease in thermal diffusivity of the medium, mirage technique becomes more difficult to be applied to low thermal diffusivity measurements. Moreover influences from substrate signals make analysis difficult when the samples are thermally thin. Recently a thermal-wave-coupling method for mirage signal analysis [P. K. Wong, P. C. W. Fung, H. L. Tam, and J. Gao, Phys. Rev. B 51, 523 (1995)] was reported for thermal diffusivity measurements of thin film down to 60 nm thick. In this article we apply the thermal-wave-coupling method to thin films of low thermal diffusivity, especially polymer films. A new lower limit of thermal diffusivity measurable by mirage technique has been reached.

Flexoelectricity in barium strontium titanate thin film

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kwon, Seol Ryung; Huang, Wenbin; Yuan, Fuh-Gwo

2014-10-06

Flexoelectricity, the linear coupling between the strain gradient and the induced electric polarization, has been intensively studied as an alternative to piezoelectricity. Especially, it is of interest to develop flexoelectric devices on micro/nano scales due to the inherent scaling effect of flexoelectric effect. Ba{sub 0.7}Sr{sub 0.3}TiO{sub 3} thin film with a thickness of 130 nm was fabricated on a silicon wafer using a RF magnetron sputtering process. The flexoelectric coefficients of the prepared thin films were determined experimentally. It was revealed that the thin films possessed a transverse flexoelectric coefficient of 24.5 μC/m at Curie temperature (∼28 °C) and 17.44 μC/m at 41 °C. Themore » measured flexoelectric coefficients are comparable to that of bulk BST ceramics, which are reported to be 10–100 μC/m. This result suggests that the flexoelectric thin film structures can be effectively used for micro/nano-sensing devices.« less

Gas Control and Thermal Modeling Methods for Pressed Pellet and Fast Rise Thin-Film Thermal Batteries

DTIC Science & Technology

2015-09-01

Thin-Film Thermal Batteries by Frank C Krieger and Michael S Ding Approved for public release; distribution unlimited...Laboratory Gas Control and Thermal Modeling Methods for Pressed Pellet and Fast Rise Thin-Film Thermal Batteries by Frank C Krieger and Michael S...Batteries 5a. CONTRACT NUMBER 5b. GRANT NUMBER 5c. PROGRAM ELEMENT NUMBER 6. AUTHOR(S) Frank C Krieger and Michael S Ding 5d. PROJECT NUMBER

One step electrodeposition of Cu2ZnSnS4 thin films in a novel bath with sulfurization free annealing

NASA Astrophysics Data System (ADS)

Tang, Aiyue; Li, Zhilin; Wang, Feng; Dou, Meiling; Pan, Youya; Guan, Jingyu

2017-04-01

Cu2ZnSnS4 (CZTS) is a quaternary kesterite compound with suitable band gap for thin film solar cells. In most electrodeposition-anneal routes, sulfurization is inevitable because the as-deposited film is lack of S. In this work, a novel green electrolyte was designed for synthesizing CZTS thin films with high S content. In the one-step electrodeposition, K4P2O7 and C7H6O6S were added to form complex with metallic ions in the electrolyte, which could attribute to co-deposition. The as-deposited film obtained high S content satisfying stoichiometry. After a sulfurization free annealing, the continuous and uniform CZTS thin film was obtained, which had pure kesterite structure and a suitable band gap of 1.53 eV. Electrodeposition mechanism investigation revealed that the K4P2O7 prevented the excessive deposition of Cu2+ and Sn2+. The C7H6O6S promoted the reduction of Zn2+. So the additives narrowed the co-deposition potentials of the metallic elements through a synergetic effect. They also promoted the reduction of S2O32- to ensure the co-deposition of the four elements and the stoichiometry. The sulfurization free annealing process can promote the commercialization of CZTS films and the successful design principle of environmental friendly electrolytes could be applied in other electrodeposition systems.

Synthesis of non-hydrazine solution processed Cu2(ZnSn)S4 thin films for solar cells applications

NASA Astrophysics Data System (ADS)

Gupta, Indu; Gupta, Preeti; Mohanty, Bhaskar Chandra

2017-05-01

Solution processing provides a versatile and inexpensive means to prepare Cu2ZnSnS4 (CZTS) thin films for photovoltaic applications. Differently with the reported growth of CZTS films from hydrazine based toxic solutions, we demonstrate a simple non-toxic ethanol based solution approach to synthesize the films. Using the chemical bath deposition (CBD) method, the CZTS thin films were grown from metal salts (copper chloride, zinc chloride, and tin chloride) in ethanol and monoethanol amine (MEA) and thioacetamide in ethanol as sulfur source in a single dip followed by sulfurization. The structure, composition, morphology and optical properties of the CZTS film were studied by X-ray diffraction, scanning electron microscopy and UV-vis spectroscopy. The results revealed that a post-deposition sulfurization is necessary to the phase formation and among all, sulfurization at 450°C for 60 min yielded phase pure CZTS films having kesterite structure, relatively compact morphology and an optical band gap of ˜1.52 eV indicating its suitability for solar cell applications. The results clearly validate the CBD method as a potential scalable route of preparation of CZTS thin films.

Scanning Angle Raman spectroscopy in polymer thin film characterization

DOE Office of Scientific and Technical Information (OSTI.GOV)

Nguyen, Vy H.T.

The focus of this thesis is the application of Raman spectroscopy for the characterization of thin polymer films. Chapter 1 provides background information and motivation, including the fundamentals of Raman spectroscopy for chemical analysis, scanning angle Raman scattering and scanning angle Raman scattering for applications in thin polymer film characterization. Chapter 2 represents a published manuscript that focuses on the application of scanning angle Raman spectroscopy for the analysis of submicron thin films with a description of methodology for measuring the film thickness and location of an interface between two polymer layers. Chapter 3 provides an outlook and future directionsmore » for the work outlined in this thesis. Appendix A, contains a published manuscript that outlines the use of Raman spectroscopy to aid in the synthesis of heterogeneous catalytic systems. Appendix B and C contain published manuscripts that set a foundation for the work presented in Chapter 2.« less

Electrical transport properties of spray deposited transparent conducting ortho-Zn2SnO4 thin films

NASA Astrophysics Data System (ADS)

Ramarajan, R.; Thangaraju, K.; Babu, R. Ramesh; Joseph, D. Paul

2018-04-01

Ortho Zinc Stannate (Zn2SnO4) exhibits excellent electrical and optical properties to serve as alternate transparent electrode in optoelectronic devices. Here we have optimized ortho-Zn2SnO4 thin film by spray pyrolysis method. Deposition was done onto a pre-heated glass substrate at a temperature of 400 °C. The XRD pattern indicated films to be polycrystalline with cubic structure. The surface of films had globular and twisted metal sheet like morphologies. Films were transparent in the visible region with band gap around 3.6 eV. Transport properties were studied by Hall measurements at 300 K. Activation energies were calculated from Arrhenius's plot from temperature dependent electrical measurements and the conduction mechanism is discussed.

Piezoelectric thin films and their applications for electronics

NASA Astrophysics Data System (ADS)

Yoshino, Yukio

2009-03-01

ZnO and AlN piezoelectric thin films have been studied for applications in bulk acoustic wave (BAW) resonator. This article introduces methods of forming ZnO and AlN piezoelectric thin films by radio frequency sputtering and applications of BAW resonators considering the relationship between the crystallinity of piezoelectric thin films and the characteristics of the BAW resonators. Using ZnO thin films, BAW resonators were fabricated for a contour mode at 3.58 MHz and thickness modes from 200 MHz to 5 GHz. The ZnO thin films were combined with various materials, substrates, and thin films to minimize the temperature coefficient of frequency (TCF). The minimum TCF of BAW resonators was approximately 2 ppm/°C in the range -20 to 80 °C. The electromechanical coupling coefficient (k2) in a 1.9 GHz BAW resonator was 6.9%. Using AlN thin films, 5-20 GHz BAW resonators with an ultrathin membrane were realized. The membrane thickness of a 20 GHz BAW resonator was about 200 nm, k2 was 6.1%, and the quality factor (Q) was about 280. Q decreased with increasing resonant frequency. The value of k2 is almost the same for 5-20 GHz resonators. This result could be obtained by improving the thickness uniformity, by controlling internal stress of thin films, and by controlling the crystallinity of AlN piezoelectric thin film.

Interface electronic structure and morphology of 2,7-dioctyl[1]benzothieno[3,2-b]benzothiophene (C8-BTBT) on Au film

NASA Astrophysics Data System (ADS)

Wang, Shitan; Niu, Dongmei; Lyu, Lu; Huang, Yingbao; Wei, Xuhui; Wang, Can; Xie, Haipeng; Gao, Yongli

2017-09-01

The interfacial electronic structure and morphology of 2,7-dioctyl[1]benzothieno[3,2-b]benzothiophene(C8-BTBT) on polycrystalline Au film was investigated with photoemission spectroscopy (PES), atomic force microscopy (AFM) and grazing incidence X-ray diffraction (GIXRD). The transport barriers of holes and electrons at the interface are 1.72 eV and 2.12 eV, respectively, from the UPS measurement. There is no chemical reaction of C8-BTBT with Au from the XPS investigation of core levels Au 4f, C 1s and S 2p. The upmost molecules adopt a standing up configuration deduced from the diffraction peaks in GIXRD and the step height in AFM. Increasing order of the upright orientation of C8-BTBT molecules with film growth result in decreasing work function of the C8-BTBT thin film by forming an outward pointing dipole layer with the ordered end Csbnd H bonds.

Structure-property relationships in the optimization of polysilicon thin films for electrical recording/stimulation of single neurons.

PubMed

Saha, Rajarshi; Muthuswamy, Jit

2007-06-01

We had earlier demonstrated the use of polysilicon microelectrodes for recording electrical activity from single neurons in vivo. Good machinability and compatibility with CMOS processing further make polysilicon an attractive interface material between biological environments on one hand and MEMS technology and digital circuits on the other hand. In this study, we focus on optimizing the polysilicon thin films for (a) electrical recording and (b) stimulation of single neurons by minimizing its electrochemical impedance spectra and maximizing its charge storage/injection capacity respectively. The structure-property relationships in ion-implanted (phosphorus) LPCVD polysilicon thin films under different annealing and doping conditions were carefully assessed during this optimization process. A 2D model of the polysilicon thin film consisting of 4 grains and 3 grain boundaries was constructed and the effect of grain size and grain boundaries on dc resistivity was simulated using device simulator ATLAS. Optimal processing conditions and doping concentrations resulted in a 10-fold decrease in electrochemical impedance from 1.1 kOmega to 0.1 kOmega at 1 kHz (area of polysilicon interface = 4.8 mm(2)). Subsequent characterizations showed that evolution of secondary grains within the polysilicon thin films at optimal doping and annealing conditions (10(21)/cm(3) of phosphorus and annealed at 1200 degrees C) was responsible for decreasing the impedance. Cyclic voltammetry studies demonstrated that charge storage properties of low doped (10(15)/cm(3)) thin films was 111.4 microC/cm(2) in phosphate buffered saline which compares well with platinum wires (approximately 50 microC/cm(2)) and the double-layered capacitance (C(dl)) could be sustained between -1 to 1 V before breakdown and hydrolysis. We conclude that polysilicon can be optimized for recording and stimulating single neurons and can be a valuable interface material between neurons and CMOS or MEMS devices.

Organic-inorganic hybrid materials as semiconducting channels in thin-film field-effect transistors

PubMed

Kagan; Mitzi; Dimitrakopoulos

1999-10-29

Organic-inorganic hybrid materials promise both the superior carrier mobility of inorganic semiconductors and the processability of organic materials. A thin-film field-effect transistor having an organic-inorganic hybrid material as the semiconducting channel was demonstrated. Hybrids based on the perovskite structure crystallize from solution to form oriented molecular-scale composites of alternating organic and inorganic sheets. Spin-coated thin films of the semiconducting perovskite (C(6)H(5)C(2)H(4)NH(3))(2)SnI(4) form the conducting channel, with field-effect mobilities of 0.6 square centimeters per volt-second and current modulation greater than 10(4). Molecular engineering of the organic and inorganic components of the hybrids is expected to further improve device performance for low-cost thin-film transistors.

Fiber-Optic Temperature Sensor Using a Thin-Film Fabry-Perot Interferometer

NASA Technical Reports Server (NTRS)

Beheim, Glenn

1997-01-01

A fiber-optic temperature sensor was developed that is rugged, compact, stable, and can be inexpensively fabricated. This thin-film interferometric temperature sensor was shown to be capable of providing a +/- 2 C accuracy over the range of -55 to 275 C, throughout a 5000 hr operating life. A temperature-sensitive thin-film Fabry-Perot interferometer can be deposited directly onto the end of a multimode optical fiber. This batch-fabricatable sensor can be manufactured at a much lower cost than can a presently available sensor, which requires the mechanical attachment of a Fabry-Perot interferometer to a fiber. The principal disadvantage of the thin-film sensor is its inherent instability, due to the low processing temperatures that must be used to prevent degradation of the optical fiber's buffer coating. The design of the stable thin-film temperature sensor considered the potential sources of both short and long term drifts. The temperature- sensitive Fabry-Perot interferometer was a silicon film with a thickness of approx. 2 microns. A laser-annealing process was developed which crystallized the silicon film without damaging the optical fiber. The silicon film was encapsulated with a thin layer of Si3N4 over coated with aluminum. Crystallization of the silicon and its encapsulation with a highly stable, impermeable thin-film structure were essential steps in producing a sensor with the required long-term stability.

Single-crystal-like, c-axis oriented BaTiO3 thin films with high-performance on flexible metal templates for ferroelectric applications

NASA Astrophysics Data System (ADS)

Shin, Junsoo; Goyal, Amit; Jesse, Stephen; Kim, Dae Ho

2009-06-01

Epitaxial, c-axis oriented BaTiO3 thin films were deposited using pulsed laser ablation on flexible, polycrystalline Ni alloy tape with biaxially textured oxide buffer multilayers. The high quality of epitaxial BaTiO3 thin films with P4mm group symmetry was confirmed by x-ray diffraction. The microscopic ferroelectric domain structure and the piezoelectric domain switching in these films were confirmed via spatially resolved piezoresponse mapping and local hysteresis loops. Macroscopic measurements demonstrate that the films have well-saturated hysteresis loops with a high remanent polarization of ˜11.5 μC/cm2. Such high-quality, single-crystal-like BaTiO3 films on low-cost, polycrystalline, flexible Ni alloy substrates are attractive for applications in flexible lead-free ferroelectric devices.

Nanostructural Tailoring to Induce Flexibility in Thermoelectric Ca3Co4O9 Thin Films

PubMed Central

2017-01-01

Because of their inherent rigidity and brittleness, inorganic materials have seen limited use in flexible thermoelectric applications. On the other hand, for high output power density and stability, the use of inorganic materials is required. Here, we demonstrate a concept of fully inorganic flexible thermoelectric thin films with Ca3Co4O9-on-mica. Ca3Co4O9 is promising not only because of its high Seebeck coefficient and good electrical conductivity but also because of the abundance, low cost, and nontoxicity of its constituent raw materials. We show a promising nanostructural tailoring approach to induce flexibility in inorganic thin-film materials, achieving flexibility in nanostructured Ca3Co4O9 thin films. The films were grown by thermally induced phase transformation from CaO–CoO thin films deposited by reactive rf-magnetron cosputtering from metallic targets of Ca and Co to the final phase of Ca3Co4O9 on a mica substrate. The pattern of nanostructural evolution during the solid-state phase transformation is determined by the surface energy and strain energy contributions, whereas different distributions of CaO and CoO phases in the as-deposited films promote different nanostructuring during the phase transformation. Another interesting fact is that the Ca3Co4O9 film is transferable onto an arbitrary flexible platform from the parent mica substrate by etch-free dry transfer. The highest thermoelectric power factor obtained is above 1 × 10–4 W m–1 K–2 in a wide temperature range, thus showing low-temperature applicability of this class of materials. PMID:28699345

Effects of doping on ferroelectric properties and leakage current behavior of KNN-LT-LS thin films on SrTiO3 substrate

NASA Astrophysics Data System (ADS)

Abazari, M.; Safari, A.

2009-05-01

We report the effects of Ba, Ti, and Mn dopants on ferroelectric polarization and leakage current of (K0.44Na0.52Li0.04)(Nb0.84Ta0.1Sb0.06)O3 (KNN-LT-LS) thin films deposited by pulsed laser deposition. It is shown that donor dopants such as Ba2+, which increased the resistivity in bulk KNN-LT-LS, had an opposite effect in the thin film. Ti4+ as an acceptor B-site dopant reduces the leakage current by an order of magnitude, while the polarization values showed a slight degradation. Mn4+, however, was found to effectively suppress the leakage current by over two orders of magnitude while enhancing the polarization, with 15 and 23 μC/cm2 remanent and saturated polarization, whose values are ˜70% and 82% of the reported values for bulk composition. This phenomenon has been associated with the dual effect of Mn4+ in KNN-LT-LS thin film, by substituting both A- and B-site cations. A detailed description on how each dopant affects the concentrations of vacancies in the lattice is presented. Mn-doped KNN-LT-LS thin films are shown to be a promising candidate for lead-free thin films and applications.

Growth and physical investigations of sprayed ZnMoO4 thin films along with wettability tests

NASA Astrophysics Data System (ADS)

Askri, Besma; Mhamdi, Ammar; Mahdhi, Noureddine; Amlouk, Mosbah

2018-06-01

Ternary oxides based on zinc and molybdenum elements have known as semiconductor oxides with large band gap energies. With the focus mainly on their synthesis by cost-effective process as thin films, the aspect of their stability and reactivity as transparent layers against both UV radiation and oxidation under wet medium due to their oxygen deficiency has so far not been investigated. This work covers the synthesis as well as the structural, electrical and the wettability properties of ZnMoO4 thin films which have been prepared by the spray pyrolysis method on glass substrates at 460 °C. First, X-ray diffraction analysis shows that this oxide crystallizes in triclinic structure with the space group P-1. The thickness value of ZnMoO4 thin film of about 1.5 μm was estimated by spectroscopic ellipsometry (SE). Moreover, a special emphasis has been focused on the photoluminescence properties of such films to reach possible presence of defaults and oxygen vacancy. Second, the electrical conductivity, conduction mechanism, relaxation model of these films were indeed studied using impedance spectroscopy technique in the frequency range 10-1-106 Hz at various temperatures (25-300 °C). At high temperature, σAC conductivity obeys to the power law established by Jonscher. Besides, the variation of σDC with the inverse of the temperature follows Arrhenius law. This evolution suggests that the conduction process is thermally activated and the activation energy of this process is equal to 0.97 eV. Finally, the wettability tests reveal that zinc molybdates loses its hydrophobic character during aging under UV radiation to become completely hydrophilic. All these physical investigations demonstrated that such ternary oxide contains oxygen deficiency which may be of interest for photocatalytic purposes and pave the way for various sensitivity applications like gas and bio-sensors.

l/f Noise in the Superconducting Transition of a MgB2 Thin Film

NASA Technical Reports Server (NTRS)

Lakew, B.; Aslam, S.; Jones, H.; Stevenson, T.; Cao, N.

2010-01-01

The noise voltage spectral density in the superconducting transition of a MgB2 thin film on a SiN-coated Si thick substrate was measured over the frequency range 1 Hz-to-1 KHz. Using established bolometer noise theory the theoretical noise components due to Johnson, 1/f(excess) and phonon noise are modeled to the measured data. It is shown that for the case of a MgB2 thin film in the vicinity of the mid-point of transition, coupled to a heat sink via a fairly high thermal conductance (approximately equal to 10(sup -1) W/K)) that the measured noise voltage spectrum is 1/f limited and exhibits lit dependence with a varying between 0.3 and 0.5 in the measured frequency range. At a video frame rate frequency of 30 Hz the measured noise voltage density in the film is approximately equal to 61 nV /the square root of HZ, using this value an upper limit of electrical NEP approximately equal to 0.67pW / the square root of Hz is implied for a practical MgB2 bolometer operating at 36.1 K.

Thin film contamination effects on laser-induced damage of fused silica surfaces at 355 nm

DOE Office of Scientific and Technical Information (OSTI.GOV)

Burnham, A. K.; Cordillot, C.; Fornier, A.

1998-07-28

Fused silica windows were artificially contaminated to estimate the resistance of target chamber debris shields against laser damage during NIF operation. Uniform contamination thin films (1 to 5 nm thick) were prepared by sputtering various materials (Au, Al, Cu, and B 4C). The loss of transmission of the samples was first measured. They were then tested at 355 nm in air with an 8-ns Nd:YAG laser. The damage morphologies were characterized by Nomarski optical microscopy and SEM. Both theory and experiments showed that metal contamination for films as thin as 1 nm leads to a substantial loss of transmission. Themore » laser damage resistance dropped very uniformly across the entire surface (e.g. 6 J/cm 2 for 5 nm of Cu). The damage morphology characterization showed that contrary to clean silica, metal coated samples did not produce pits on the surface. B 4C coated silica, on the other hand, led to a higher density of such damage pits. A model for light absorption in the thin film was coupled with a simple heat deposition and diffusion model to perform preliminary theoretical estimates of damage thresholds. The estimates of the loss due to light absorption and reflection pointed out significant .differences between metals (e.g. Al and Au). The damage threshold predictions were in qualitative agreement with experimental measurements.« less

Tungsten-rhenium thin film thermocouples for SiC-based ceramic matrix composites

NASA Astrophysics Data System (ADS)

Tian, Bian; Zhang, Zhongkai; Shi, Peng; Zheng, Chen; Yu, Qiuyue; Jing, Weixuan; Jiang, Zhuangde

2017-01-01

A tungsten-rhenium thin film thermocouple is designed and fabricated, depending on the principle of thermal-electric effect caused by the high temperature. The characteristics of thin film thermocouples in different temperatures are investigated via numerical analysis and analog simulation. The working mechanism and thermo-electric features of the thermocouples are analyzed depending on the simulation results. Then the thin film thermocouples are fabricated and calibrated. The calibration results show that the thin film thermocouples based on the tungsten-rhenium material achieve ideal static characteristics and work well in the practical applications.

High-Efficiency Thin-Film Silicon-on-GaP Solar Cell for Improved Radiation Resistance.

DTIC Science & Technology

1987-09-01

UNCLASSIFIED MyUM 21 LIX E / 82H M D 132 11111_Lt5l1. t FILE UPI" AD-A190 268 AFWAL-TR-87-2070 HIGH-EFFICIENCY THIN- FILM SILICON-ON-GaP SOLAR CELL...EFFICIENCY THIN- FILM SILICON-ON-GaP SOLAR CELL FOR IMPROVED RADIATION RESISTANCE 12. PERSONAL AUTHOR(S) JEROME S. CULIK 13a. TYPE OF REPORT 13b. TIME...C tinue on reverse if necessary and identify by block number) 10 01 SILICONs THIN* FILM , . HETEROEPITAXIAL, RADIATION, 10 01 i GALLIUM PHOSPHIDE 19

Vapor deposition of thin films

DOEpatents

Smith, David C.; Pattillo, Stevan G.; Laia, Jr., Joseph R.; Sattelberger, Alfred P.

1992-01-01

A highly pure thin metal film having a nanocrystalline structure and a process of preparing such highly pure thin metal films of, e.g., rhodium, iridium, molybdenum, tungsten, rhenium, platinum, or palladium by plasma assisted chemical vapor deposition of, e.g., rhodium(allyl).sub.3, iridium(allyl).sub.3, molybdenum(allyl).sub.4, tungsten(allyl).sub.4, rhenium(allyl).sub.4, platinum(allyl).sub.2, or palladium(allyl).sub.2 are disclosed. Additionally, a general process of reducing the carbon content of a metallic film prepared from one or more organometallic precursor compounds by plasma assisted chemical vapor deposition is disclosed.

Scanning Probe Microscopy on heterogeneous CaCu3Ti4O12 thin films

PubMed Central

2011-01-01

The conductive atomic force microscopy provided a local characterization of the dielectric heterogeneities in CaCu3Ti4O12 (CCTO) thin films deposited by MOCVD on IrO2 bottom electrode. In particular, both techniques have been employed to clarify the role of the inter- and sub-granular features in terms of conductive and insulating regions. The microstructure and the dielectric properties of CCTO thin films have been studied and the evidence of internal barriers in CCTO thin films has been provided. The role of internal barriers and the possible explanation for the extrinsic origin of the giant dielectric response in CCTO has been evaluated. PMID:21711646

Scanning Probe Microscopy on heterogeneous CaCu3Ti4O12 thin films

NASA Astrophysics Data System (ADS)

Fiorenza, Patrick; Lo Nigro, Raffaella; Raineri, Vito

2011-12-01

The conductive atomic force microscopy provided a local characterization of the dielectric heterogeneities in CaCu3Ti4O12 (CCTO) thin films deposited by MOCVD on IrO2 bottom electrode. In particular, both techniques have been employed to clarify the role of the inter- and sub-granular features in terms of conductive and insulating regions. The microstructure and the dielectric properties of CCTO thin films have been studied and the evidence of internal barriers in CCTO thin films has been provided. The role of internal barriers and the possible explanation for the extrinsic origin of the giant dielectric response in CCTO has been evaluated.

Scanning Probe Microscopy on heterogeneous CaCu3Ti4O12 thin films.

PubMed

Fiorenza, Patrick; Lo Nigro, Raffaella; Raineri, Vito

2011-02-04

The conductive atomic force microscopy provided a local characterization of the dielectric heterogeneities in CaCu3Ti4O12 (CCTO) thin films deposited by MOCVD on IrO2 bottom electrode. In particular, both techniques have been employed to clarify the role of the inter- and sub-granular features in terms of conductive and insulating regions. The microstructure and the dielectric properties of CCTO thin films have been studied and the evidence of internal barriers in CCTO thin films has been provided. The role of internal barriers and the possible explanation for the extrinsic origin of the giant dielectric response in CCTO has been evaluated.

Thin-Film Ceramic Thermocouples Fabricated and Tested

NASA Technical Reports Server (NTRS)

Wrbanek, John D.; Fralick, Gustave C.; Farmer, Serene C.; Sayir, Ali; Gregory, Otto J.; Blaha, Charles A.

2004-01-01

The Sensors and Electronics Technology Branch of the NASA Glenn Research Center is developing thin-film-based sensors for surface measurement in propulsion system research. Thin-film sensors do not require special machining of the components on which they are mounted, and they are considerably thinner than wire- or foil-based sensors. One type of sensor being advanced is the thin-film thermocouple, specifically for applications in high-temperature combustion environments. Ceramics are being demonstrated as having the potential to meet the demands of thin-film thermocouples in advanced aerospace environments. The maximum-use temperature of noble metal thin-film thermocouples, 1500 C (2700 F), may not be adequate for components used in the increasingly harsh conditions of advanced aircraft and next-generation launch vehicles. Ceramic-based thermocouples are known for their high stability and robustness at temperatures exceeding 1500 C, but are typically in the form of bulky rods or probes. As part of ASTP, Glenn's Sensors and Electronics Technology Branch is leading an in-house effort to apply ceramics as thin-film thermocouples for extremely high-temperature applications as part of ASTP. Since the purity of the ceramics is crucial for the stability of the thermocouples, Glenn's Ceramics Branch and Case Western Reserve University are developing high-purity ceramic sputtering targets for fabricating high-temperature sensors. Glenn's Microsystems Fabrication Laboratory, supported by the Akima Corporation, is using these targets to fabricate thermocouple samples for testing. The first of the materials used were chromium silicide (CrSi) and tantalum carbide (TaC). These refractory materials are expected to survive temperatures in excess of 1500 C. Preliminary results indicate that the thermoelectric voltage output of a thin-film CrSi versus TaC thermocouple is 15 times that of the standard type R (platinum-rhodium versus platinum) thermocouple, producing 20 mV with a 200

Method for synthesizing thin film electrodes

DOEpatents

Boyle, Timothy J [Albuquerque, NM

2007-03-13

A method for making a thin-film electrode, either an anode or a cathode, by preparing a precursor solution using an alkoxide reactant, depositing multiple thin film layers with each layer approximately 500 1000 .ANG. in thickness, and heating the layers to above 600.degree. C. to achieve a material with electrochemical properties suitable for use in a thin film battery. The preparation of the anode precursor solution uses Sn(OCH.sub.2C(CH.sub.3).sub.3).sub.2 dissolved in a solvent in the presence of HO.sub.2CCH.sub.3 and the cathode precursor solution is formed by dissolving a mixture of (Li(OCH.sub.2C(CH.sub.3).sub.3)).sub.8 and Co(O.sub.2CCH.sub.3).H.sub.2O in at least one polar solvent.

Characterization of Doped Amorphous Silicon Thin Films through the Investigation of Dopant Elements by Glow Discharge Spectrometry. A Correlation of Conductivity and Bandgap Energy Measurements

PubMed Central

Sánchez, Pascal; Lorenzo, Olaya; Menéndez, Armando; Menéndez, Jose Luis; Gomez, David; Pereiro, Rosario; Fernández, Beatriz

2011-01-01

The determination of optical parameters, such as absorption and extinction coefficients, refractive index and the bandgap energy, is crucial to understand the behavior and final efficiency of thin film solar cells based on hydrogenated amorphous silicon (a-Si:H). The influence of small variations of the gas flow rates used for the preparation of the p-a-SiC:H layer on the bandgap energy, as well as on the dopant elements concentration, thickness and conductivity of the p-layer, is investigated in this work using several complementary techniques. UV-NIR spectrophotometry and ellipsometry were used for the determination of bandgap energies of four p-a-SiC:H thin films, prepared by using different B2H6 and SiH4 fluxes (B2H6 from 12 sccm to 20 sccm and SiH4 from 6 sccm to 10 sccm). Moreover, radiofrequency glow discharge optical emission spectrometry technique was used for depth profiling characterization of p-a-SiC:H thin films and valuable information about dopant elements concentration and distribution throughout the coating was found. Finally, a direct relationship between the conductivity of p-a-SiC:H thin films and the dopant elements concentration, particularly boron and carbon, was observed for the four selected samples. PMID:21731436

Non-resonant microwave absorption in high-T c thin films

NASA Astrophysics Data System (ADS)

Durny, R.; Dulcic, A.; Crepeau, R. H.; Freed, J. H.; Kus, P.

1990-11-01

Magnetic-field-dependent non-resonant microwave absorption in thin film samples of various high- Tc superconductors is reported. Complex types of signals were observed as the temperature was lowered from Tc to ≈ 10 K. Possible correlation between the thin film quality and the occurrence of the signals is suggested.

Magnetization and anisotropy of cobalt ferrite thin films

NASA Astrophysics Data System (ADS)

Eskandari, F.; Porter, S. B.; Venkatesan, M.; Kameli, P.; Rode, K.; Coey, J. M. D.

2017-12-01

The magnetization of thin films of cobalt ferrite frequently falls far below the bulk value of 455 kA m-1 , which corresponds to an inverse cation distribution in the spinel structure with a significant orbital moment of about 0.6 μB that is associated with the octahedrally coordinated Co2+ ions. The orbital moment is responsible for the magnetostriction and magnetocrystalline anisotropy and its sensitivity to imposed strain. We have systematically investigated the structure and magnetism of films produced by pulsed-laser deposition on different substrates (Ti O2 , MgO, MgA l2O4 , SrTi O3 , LSAT, LaAl O3 ) and as a function of temperature (500 -700 °C) and oxygen pressure (10-4-10 Pa ) . Magnetization at room-temperature ranges from 60 to 440 kA m-1 , and uniaxial substrate-induced anisotropy ranges from +220 kJ m-3 for films on deposited on MgO (100) to -2100 kJ m-3 for films deposited on MgA l2O4 (100), where the room-temperature anisotropy field reaches 14 T. No rearrangement of high-spin Fe3+ and Co2+ cations on tetrahedral and octahedral sites can reduce the magnetization below the bulk value, but a switch from Fe3+ and Co2+ to Fe2+ and low-spin Co3+ on octahedral sites will reduce the low-temperature magnetization to 120 kA m-1 , and a consequent reduction of Curie temperature can bring the room-temperature value to near zero. Possible reasons for the appearance of low-spin cobalt in the thin films are discussed.

Thin-Film Photoluminescent Properties and the Atomistic Model of Mg2TiO4 as a Non-rare Earth Matrix Material for Red-Emitting Phosphor

NASA Astrophysics Data System (ADS)

Huang, Chieh-Szu; Chang, Ming-Chuan; Huang, Cheng-Liang; Lin, Shih-kang

2016-12-01

Thin-film electroluminescent devices are promising solid-state lighting devices. Red light-emitting phosphor is the key component to be integrated with the well-established blue light-emitting diode chips for stimulating natural sunlight. However, environmentally hazardous rare-earth (RE) dopants, e.g. Eu2+ and Ce2+, are commonly used for red-emitting phosphors. Mg2TiO4 inverse spinel has been reported as a promising matrix material for "RE-free" red light luminescent material. In this paper, Mg2TiO4 inverse spinel is investigated using both experimental and theoretical approaches. The Mg2TiO4 thin films were deposited on Si (100) substrates using either spin-coating with the sol-gel process, or radio frequency sputtering, and annealed at various temperatures ranging from 600°C to 900°C. The crystallinity, microstructures, and photoluminescent properties of the Mg2TiO4 thin films were characterized. In addition, the atomistic model of the Mg2TiO4 inverse spinel was constructed, and the electronic band structure of Mg2TiO4 was calculated based on density functional theory. Essential physical and optoelectronic properties of the Mg2TiO4 luminance material as well as its optimal thin-film processing conditions were comprehensively reported.

High-piezoelectric behavior of c-axis-oriented lead zirconate titanate thin films with composition near the morphotropic phase boundary

NASA Astrophysics Data System (ADS)

Fu, Desheng; Suzuki, Hisao; Ogawa, Takeshi; Ishikawa, Kenji

2002-05-01

The piezoelectric responses of c-axis-oriented Pb(Zr0.53Ti0.47)O3 (PZT) thin films have been studied by measuring the stress-induced charge with an accurate charge integrator. These measurements reveal that the c-axis-oriented PZT films have high values of d33, which are several times those of ceramic materials. The intrinsic d33 values of poled films are about 680 and 800 pC/N for the c-axis-oriented films on Si and MgO single-crystal substrates, respectively. It shows that the thin-film deposition technique opens an approach for exploring the potential superior properties of PZT near the morphotropic phase boundary.

Microstructure evolution and coercivity enhancement in Nd-Fe-B thin films diffusion-processed by R-Al alloys (R=Nd, Pr)

NASA Astrophysics Data System (ADS)

Xie, Yigao; Yang, Yang; Zhang, Tongbo; Fu, Yanqing; Jiang, Qingzheng; Ma, Shengcan; Zhong, Zhenchen; Cui, Weibin; Wang, Qiang

2018-05-01

Diffusion process by Nd-Al and Pr-Al alloys was compared and investigated in Nd-Fe-B thin films. Enhanced coercivity 2.06T and good squareness was obtained by using Pr85Al15 and Nd85Al15 alloys as diffusion sources. But the coercivity of diffusion-processed thin films by Pr70Al30 and Pr55Al45 alloys decreased to 2.04T and 1.82T. High ambient coercivity of 2.26T was achieved in diffusion-processed thin film by Nd70Al30 leading to an improved coercivity thermal stability because Nd2Fe14B grains were enveloped by Nd-rich phase as seen by transmission electron microscopy Nd-loss image. Meanwhile, microstructure-dependent parameters α and Neff were improved. However, high content of Al in diffusion-processed thin film by Nd55Al45 lead to degraded texture and coercivity.

Thermoelectric Properties of Al-Doped ZnO Thin Films

NASA Astrophysics Data System (ADS)

Saini, S.; Mele, P.; Honda, H.; Matsumoto, K.; Miyazaki, K.; Ichinose, A.

2014-06-01

We have prepared 2 % Al-doped ZnO (AZO) thin films on SrTiO3 substrates by a pulsed laser deposition technique at various deposition temperatures ( T dep = 300-600 °C). The thermoelectric properties of AZO thin films were studied in a low temperature range (300-600 K). Thin film deposited at 300 °C is fully c-axis-oriented and presents electrical conductivity 310 S/cm with Seebeck coefficient -65 μV/K and power factor 0.13 × 10-3 Wm-1 K-2 at 300 K. The performance of thin films increases with temperature. For instance, the power factor is enhanced up to 0.55 × 10-3 Wm-1 K-2 at 600 K, surpassing the best AZO film previously reported in the literature.

Non-Volatile Ferroelectric Switching of Ferromagnetic Resonance in NiFe/PLZT Multiferroic Thin Film Heterostructures (Postprint)

DTIC Science & Technology

2016-09-01

AFRL-RX-WP-JA-2017-0140 NON-VOLATILE FERROELECTRIC SWITCHING OF FERROMAGNETIC RESONANCE IN NIFE/PLZT MULTIFERROIC THIN FILM ...OF FERROMAGNETIC RESONANCE IN NIFE/PLZT MULTIFERROIC THIN FILM HETEROSTRUCTURES (POSTPRINT) 5a. CONTRACT NUMBER FA8650-14-C-5706 5b. GRANT... films , where the magnetic anisotropy of NiFe can be electrically modified by low voltages. Ferromagnetic resonance measurements confirm that the

Lithium diffusion in sputter-deposited Li4Ti5O12 thin films

NASA Astrophysics Data System (ADS)

Wunde, F.; Berkemeier, F.; Schmitz, G.

2012-10-01

Li4Ti5O12 (LTO) thin films are deposited by dc-ion beam sputtering at different oxygen partial pressures and different substrate temperatures. In order to investigate, how these two parameters influence the atomic structure, the specimens are characterized by X-ray diffraction and transmission electron microscopy. Electrochemical characterization of the films is done by cyclic voltammetry and chrono-potentiometry. To determine an averaged chemical diffusion coefficient of lithium, a method is developed, evaluating c-rate tests. The results obtained by this method are compared to results obtained by the well established galvanostatic intermittent titration technique (GITT), which is used to determine a concentration dependent diffusion coefficient of lithium in LTO.

Synthesis and annealing study of RF sputtered ZnO thin film

DOE Office of Scientific and Technical Information (OSTI.GOV)

Singh, Shushant Kumar, E-mail: singhshushant86@gmail.com; Sharma, Himanshu; Singhal, R.

2016-05-23

In this paper, we have investigated the annealing effect on optical and structural properties of ZnO thin films, synthesized by RF magnetron sputtering. ZnO thin films were deposited on glass and silicon substrates simultaneously at a substrate temperature of 300 °C using Argon gas in sputtering chamber. Thickness of as deposited ZnO thin film was found to be ~155 nm, calculated by Rutherford backscattering spectroscopy (RBS). These films were annealed at 400 °C and 500 °C temperature in the continuous flow of oxygen gas for 1 hour in tube furnace. X-ray diffraction analysis confirmed the formation of hexagonal wurtzite structuremore » of ZnO thin film along the c-axis (002) orientation. Transmittance of thin films was increased with increasing the annealing temperature estimated by UV-visible transmission spectroscopy. Quality and texture of the thin films were improved with annealing temperature, estimated by Raman spectroscopy.« less

PECVD based silicon oxynitride thin films for nano photonic on chip interconnects applications.

PubMed

Sharma, Satinder K; Barthwal, Sumit; Singh, Vikram; Kumar, Anuj; Dwivedi, Prabhat K; Prasad, B; Kumar, Dinesh

2013-01-01

Thin silicon oxynitride (SiO(x)N(y)) films were deposited by low temperature (~300°C) plasma enhanced chemical vapour deposition (PECVD), using SiH(4), N(2)O, NH(3) precursor of the flow rate 25, 100, 30 sccm and subjected to the post deposition annealing (PDA) treatment at 400°C and 600°C for nano optical/photonics on chip interconnects applications. AFM result reveals the variation of roughness from 60.9 Å to 23.4 Å after PDA treatment with respect to the as-deposited films, favourable surface topography for integrated waveguide applications. A model of decrease in island height with the effect of PDA treatment is proposed in support of AFM results. Raman spectroscopy and FTIR measurements are performed in order to define the change in crystallite and chemical bonding of as-deposited as well as PDA treated samples. These outcomes endorsed to the densification of SiO(x)N(y) thin films, due to decrease in Si-N and Si-O bonds strain, as well the O-H, N-H bonds with in oxynitride network. The increase in refractive index and PL intensity of as deposited SiO(x)N(y) thin films to the PDA treated films at 400°C and 600°C are observed. The significant shift of PL spectra peak positions indicate the change in cluster size as the result of PDA treatment, which influence the optical properties of thin films. It might be due to out diffusion of hydrogen containing species from silicon oxynitride films after PDA treatment. In this way, the structural and optical, feasibility of SiO(x)N(y) films are demonstrated in order to obtain high quality thin films for nano optical/photonics on chip interconnects applications. Copyright © 2012 Elsevier Ltd. All rights reserved.

Metal-insulator transition of valence-controlled VO2 thin film prepared by RF magnetron sputtering using oxygen radical

NASA Astrophysics Data System (ADS)

Suetsugu, Takaaki; Shimazu, Yuichi; Tsuchiya, Takashi; Kobayashi, Masaki; Minohara, Makoto; Sakai, Enju; Horiba, Koji; Kumigashira, Hiroshi; Higuchi, Tohru

2016-06-01

We have prepared b-axis-oriented VO2 thin films by RF magnetron sputtering using oxygen radicals as the reactive gas. The VO2 thin films consist of a mixed-valence V3+/V4+ state formed by oxygen vacancies. The V3+ ratio strongly depends on the film thickness and the oxygen partial pressure of the radical gun during deposition. The lattice constant of the b-axis increases and the metal-insulator transition (MIT) temperature decreases with decreasing V3+ ratio, although the VO2 thin films with a high V3+ ratio of 42% do not exhibit MIT. The bandwidths and spectral weights of V 3d a1g and \\text{e}\\text{g}σ bands at around the Fermi level, which correspond to the insulating phase at 300 K, are smaller in the VO2 thin films with a low V3+ ratio. These results indicate that the control of the mixed-valence V3+/V4+ state is important for the MIT of b-axis-oriented VO2 thin films.

A photochemical proposal for the preparation of ZnAl{sub 2}O{sub 4} and MgAl{sub 2}O{sub 4} thin films from β-diketonate complex precursors

DOE Office of Scientific and Technical Information (OSTI.GOV)

Cabello, G., E-mail: gerardocabelloguzman@hotmail.com; Lillo, L.; Caro, C.

2016-05-15

Highlights: • ZnAl{sub 2}O{sub 4} and MgAl{sub 2}O{sub 4} thin films were prepared by photo-chemical method. • The Zn(II), Mg(II) and Al(III) β-diketonate complexes were used as precursors. • The photochemical reaction was monitored by UV–vis and FT-IR spectroscopy. • The results reveal spinel oxide formation and the generation of intermediate products. - Abstract: ZnAl{sub 2}O{sub 4} and MgAl{sub 2}O{sub 4} thin films were grown on Si(100) and quartz plate substrates using a photochemical method in the solid phase with thin films of β-diketonate complexes as the precursors. The films were deposited by spin-coating and subsequently photolyzed at room temperaturemore » using 254 nm UV light. The photolysis of these films results in the deposition of metal oxide thin films and fragmentation of the ligands from the coordination sphere of the complexes. The obtained samples were post-annealed at different temperatures (350–1100 °C) for 2 h and characterized by FT-Infrared spectroscopy, X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), atomic force miscroscopy (AFM), and UV–vis spectroscopy. The results indicate the formation of spinel-type structures and other phases. These characteristics determined the quality of the films, which were obtained from the photodeposition of ternary metal oxides.« less

Structural and magnetic properties of nanocrystalline NiFe2O4 thin film prepared by spray pyrolysis technique

NASA Astrophysics Data System (ADS)

Chavan, Apparao R.; Chilwar, R. R.; Shisode, M. V.; Hivrekar, Mahesh M.; Mande, V. K.; Jadhav, K. M.

2018-05-01

The nanocrystalline NiFe2O4 thin film has been prepared using a spray pyrolysis technique on glass substrate. The prepared thin film was characterized by using X-ray diffraction (XRD), Fourier transform Infrared spectroscopy (FTIR), and Field Emission-Scanning Electron Microscopy (FE-SEM) characterization techniques for the structural and microstructural analysis. The magnetic property was measured using vibrating sample magnetometer (VSM) at room temperature. X-ray diffraction studies show the formation of single phase spinel structure of the thin film. The octahedral and tetrahedral vibration in the sample was studied by Fourier transform infrared (FT-IR) spectra. Magnetic hysteresis loop was recorded for thin film at room temperature. At 15 kOe, saturation magnetization (Ms) was found to increase while coercivity (Hc) decreases with thickness of the NiFe2O4 thin film.

Zirconium doped TiO2 thin films deposited by chemical spray pyrolysis

NASA Astrophysics Data System (ADS)

Juma, A.; Oja Acik, I.; Oluwabi, A. T.; Mere, A.; Mikli, V.; Danilson, M.; Krunks, M.

2016-11-01

Chemical spray pyrolysis (CSP) is a flexible deposition technique that allows for mixing of the precursor solutions in different proportions suitable for doping thin films. The CSP method was used to dope TiO2 thin films with Zr by adding zirconium(IV) acetylacetonate into a solution of titanium(IV) isopropoxide in ethanol stabilized by acetylacetone at [Zr]/[Ti] of 0, 5, 10 and 20 at%. The Zr-doped TiO2 thin films were uniform and homogeneous showing much smaller grains than the undoped TiO2 films. Zr stabilized the anatase phase to temperatures above 800 °C depending on Zr concentration in the spray solution. The concentration of Zr determined by XPS was 6.4 at% for the thin film deposited from the 20 at% solution. According to AFM studies, Zr doping decreased the root mean square roughness of TiO2 film from 5.9 to 1.1 nm. An XRD study of samples with the highest Zr amount showed the ZrTiO4 phase started forming after annealing at 800 °C. The optical band gap for TiO2 decreased from 3.3 eV to 3.0 eV after annealing at 800 °C but for the TiO2:Zr(20) film it remained at 3.4 eV. The dielectric constant increased by more than four times with Zr-doping and this was associated with the change in the bond formations caused by substitution of Ti by Zr in the lattice.

Sputtered boron indium oxide thin-film transistors

NASA Astrophysics Data System (ADS)

Stewart, Kevin A.; Gouliouk, Vasily; Keszler, Douglas A.; Wager, John F.

2017-11-01

Boron indium oxide (BIO) is studied for thin-film transistor (TFT) channel layer applications. Sputtered BIO thin films exhibit an amorphous phase over a wide range of B2O3/In2O3 ratios and remain amorphous up to 500 °C. The band gap decreases linearly with decreasing boron content, whereas device performance generally improves with decreasing boron content. The best amorphous BIO TFT exhibits a field-effect mobility of 10 cm2 V-1 s-1, turn-on voltage of 2.5 V, and sub-threshold swing of 0.72 V/dec. Decreasing the boron content to 12.5% leads to a polycrystalline phase, but further increases the mobility up to 20-40 cm2 V-1 s-1. TCAD simulation results suggest that the reason for higher performance after increasing the anneal temperature from 200 to 400 °C is due to a lower defect density in the sub-bandgap region of the BIO channel layer.

AZO nanorods thin films by sputtering method

NASA Astrophysics Data System (ADS)

Rosli, A. B.; Shariffudin, S. S.; Awang, Z.; Herman, S. H.

2018-05-01

Al-doped zinc oxide (AZO) nanorods thin film were deposited on Au catalyst using RF sputtering at 300 °C. The 15 nm thickness Au catalyst were deposited on glass substrates by sputtering method followed by annealing for 15 min at 500 °C to form Au nanostructures on the glass substrate. The AZO thin films were then deposited on Au catalyst at different RF power ranging from 50 - 200 W. The morphology of AZO was characterized using Field Emission Scanning Electron Microscopy while X-ray Diffraction was used to examine crystallinity of AZO thin films. From this work, the AZO nanorods was found grow at 200 W RF power.

Integration of Peptides into Organic Thin Film Transistor (OTFT)-based Printable Sensors

DTIC Science & Technology

2017-02-10

AFRL-AFOSR-JP-TR-2017-0009 Integration of Peptides into Organic Thin Film Transistor (OTFT)-based Printable Sensors Paul Dastoor UNIVERSITY OF...collection of information   if it does not display a currently valid OMB control number. PLEASE DO NOT RETURN YOUR FORM TO THE ABOVE ORGANIZATION . 1...Peptides into Organic Thin Film Transistor (OTFT)-based Printable Sensors 5a.  CONTRACT NUMBER 5b.  GRANT NUMBER FA2386-15-1-4002 5c.  PROGRAM ELEMENT

Epitaxial Growth of MOF Thin Film for Modifying the Dielectric Layer in Organic Field-Effect Transistors.

PubMed

Gu, Zhi-Gang; Chen, Shan-Ci; Fu, Wen-Qiang; Zheng, Qingdong; Zhang, Jian

2017-03-01

Metal-organic framework (MOF) thin films are important in the application of sensors and devices. However, the application of MOF thin films in organic field effect transistors (OFETs) is still a challenge to date. Here, we first use the MOF thin film prepared by a liquid-phase epitaxial (LPE) approach (also called SURMOFs) to modify the SiO 2 dielectric layer in the OFETs. After the semiconductive polymer of PTB7-Th (poly[4,8-bis(5-(2-ethylhexyl)thiophene-2-yl)benzo[1,2-b:4,5-b']dithiophene-co-3-fluorothieno[3,4-b]thiophene-2-carboxylate]) was coated on MOF/SiO 2 and two electrodes on the semiconducting film were deposited sequentially, MOF-based OFETs were fabricated successfully. By controlling the LPE cycles of SURMOF HKUST-1 (also named Cu 3 (BTC) 2 , BTC = 1,3,5-benzenetricarboxylate), the performance of the HKUST-1/SiO 2 -based OFETs showed high charge mobility and low threshold voltage. This first report on the application of MOF thin film in OFETs will offer an effective approach for designing a new kind of materials for the OFET application.

Thin film thermocouples for high temperature measurement on ceramic materials

NASA Technical Reports Server (NTRS)

Holanda, Raymond

1992-01-01

Thin film thermocouples have been developed for use on metal parts in jet engines to 1000 C. However, advanced propulsion systems are being developed that will use ceramic materials and reach higher temperatures. The purpose of this work is to develop thin film thermocouples for use on ceramic materials. The thin film thermocouples are Pt13Rh/Pt fabricated by the sputtering process. Lead wires are attached using the parallel-gap welding process. The ceramic materials are silicon nitride, silicon carbide, aluminum oxide, and mullite. Both steady state and thermal cycling furnace tests were performed in the temperature range to 1500 C. High-heating-rate tests were performed in an arc lamp heat-flux-calibration facility. The fabrication of the thin film thermocouples is described. The thin film thermocouple output was compared to a reference wire thermocouple. Drift of the thin film thermocouples was determined, and causes of drift are discussed. The results of high-heating-rate tests up to 2500 C/sec are presented. The stability of the ceramic materials is examined. It is concluded that Pt13Rh/Pt thin film thermocouples are capable of meeting lifetime goals of 50 hours or more up to temperatures of 1500 C depending on the stability of the particular ceramic substrate.

Orientation effect on microwave dielectric properties of Si-integrated Ba0.6Sr0.4TiO3 thin films for frequency agile devices

NASA Astrophysics Data System (ADS)

Kim, Hyun-Suk; Hyun, Tae-Seon; Kim, Ho-Gi; Kim, Il-Doo; Yun, Tae-Soon; Lee, Jong-Chul

2006-07-01

The effect of texture with (100) and (110) preferred orientations on dielectric properties of Ba0.6Sr0.4TiO3 (BST) thin films grown on SrO (9nm) and CeO2 (70nm ) buffered Si substrates, respectively, was investigated. The coplanar waveguide (CPW) phase shifter using (100) oriented BST films on SrO buffered Si exhibited a much-enhanced figure of merit of 24.7°/dB, as compared to that (10.2°/dB) of a CPW phase shifter using (110) oriented BST films on CeO2 buffered Si at 12GHz. This work demonstrates that the microwave properties of the Si-integrated BST thin films are highly correlated with crystal orientation.

Hydride CVD Hetero-epitaxy of B 12P 2 on 4H-SiC

DOE Office of Scientific and Technical Information (OSTI.GOV)

Frye, C. D.; Saw, C. K.; Padavala, Balabalaji

Icosahedral boron phosphide (B 12P 2) is a wide bandgap semiconductor (3.35 eV) that has been reported to “self-heal” from high-energy electron bombardment, making it attractive for potential use in radioisotope batteries, radiation detection, or in electronics in high radiation environments. Our study focused on improving B 12P 2 hetero-epitaxial films by growing on 4H-SiC substrates over the temperature range of 1250–1450 °C using B 2H 6 and PH 3 precursors in a H 2 carrier gas. Furthermore, XRD scans and Laue transmission photographs revealed that the epitaxial relationship was (0001)<11more » $$\\bar{2}$$0> B12P2|| (0001)<11$$\\bar{2}$$0> 4H-SiC. The film morphology and crystallinity were investigated as a function of growth temperature and growth time. At 1250 °C, films tended to form rough, polycrystalline layers, but at 1300 and 1350 °C, films were continuous and comparatively smooth (R RMS≤7 nm). At 1400 or 1450 °C, the films grew in islands that coalesced as the films became thicker. Using XRD rocking curves to evaluate the crystal quality, 1300 °C was the optimum growth temperature tested. Finally, at 1300 °C, the rocking curve FWHM decreased with increasing film thickness from 1494 arcsec for a 1.1 μm thick film to 954 arcsec for a 2.7 µm thick film, suggesting a reduction in defects with thickness.« less

Hydride CVD Hetero-epitaxy of B 12P 2 on 4H-SiC

DOE PAGES

Frye, C. D.; Saw, C. K.; Padavala, Balabalaji; ...

2016-11-27

Icosahedral boron phosphide (B 12P 2) is a wide bandgap semiconductor (3.35 eV) that has been reported to “self-heal” from high-energy electron bombardment, making it attractive for potential use in radioisotope batteries, radiation detection, or in electronics in high radiation environments. Our study focused on improving B 12P 2 hetero-epitaxial films by growing on 4H-SiC substrates over the temperature range of 1250–1450 °C using B 2H 6 and PH 3 precursors in a H 2 carrier gas. Furthermore, XRD scans and Laue transmission photographs revealed that the epitaxial relationship was (0001)<11more » $$\\bar{2}$$0> B12P2|| (0001)<11$$\\bar{2}$$0> 4H-SiC. The film morphology and crystallinity were investigated as a function of growth temperature and growth time. At 1250 °C, films tended to form rough, polycrystalline layers, but at 1300 and 1350 °C, films were continuous and comparatively smooth (R RMS≤7 nm). At 1400 or 1450 °C, the films grew in islands that coalesced as the films became thicker. Using XRD rocking curves to evaluate the crystal quality, 1300 °C was the optimum growth temperature tested. Finally, at 1300 °C, the rocking curve FWHM decreased with increasing film thickness from 1494 arcsec for a 1.1 μm thick film to 954 arcsec for a 2.7 µm thick film, suggesting a reduction in defects with thickness.« less

Thin Films of Reduced Hafnium Oxide with Excess Carbon for High-Temperature Oxidation Protection

DTIC Science & Technology

2010-02-01

Cho, N. V. Nguyen, C. A. Richter, J. R. Ehrstein, B . H. Lee, and J. C. Lee, "Spectroscopic Ellipsometry Characterization of High- k Dielectric Hf02...34 Canadian Journal of Chemistry, 61 850-55 (1983). I6D. B . Chrisey and G. K . Hubler (Eds.), "Pulsed Laser Deposition of Thin Films." John Wiley...smaller than b rim. It was shown that high carbon content in the films inhibits crystaliization of HtO( at temperatures at least up to 333 C. Study ot

Thermo-optical properties of 1H[3,4-b] quinoline films used in electroluminescent devices

NASA Astrophysics Data System (ADS)

Jaglarz, Janusz; Kępińska, Mirosława; Sanetra, Jerzy

2014-06-01

Electroluminescence cells with H[3,4-b] quinoline layers are promising devices for a blue light emitting EL diode. This work measured the optical reflectance as a function of temperature in copolymers PAQ layers deposited on Si crystalline substrate. Using the extended Cauchy dispersion model of the film refractive index we determined the thermo-optical coefficients for quinoline layers in the temperature range of 76-333 K from combined ellipsometric and spectrofotometric studies. The obtained values of thermo-optical coefficients of thin PAQ film, were negative and ranged in 5-10 × 10-4 [1/K].

Transport Measurements on NEODYMIUM(1.85) CERIUM(.15) Copper OXYGEN(4-DELTA) Thin Films

NASA Astrophysics Data System (ADS)

Kussmaul, Andreas

1992-01-01

This work describes the synthesis and the study of the transport properties of thin films of Nd _{1.85}Ce_{.15 }CuO_{4-delta} carried out respectively at the IBM T. J. Watson Research Center in collaboration with Dr. A. Gupta, and at the Francis Bitter National Magnet Laboratory under the direction of Dr. P. M. Tedrow. The thin films were prepared by laser ablation of a stoichiometric target on heated substrates in a reactive ambient. The influence of the deposition parameters was studied, and the use of a nitreous oxide ambient was found to yield a clear improvement of the sample quality. The transport properties of the films were measured at low temperatures and in high magnetic fields. Non superconducting samples showed a strong, highly anisotropic, negative magnetoresistance that is consistent with two dimensional weak-localization. Superconducting samples show two dimensional fluctuation effects above T_{c}. The theory of fluctuations in a magnetic field was used to extract the position of H_{c2} (in the perpendicular direction) in the broad and almost featureless resistive transition, and the extracted values were fit to the theory of dirty superconductors. The angular dependence of the resistive transition was studied close to T _{c} and found to be somewhat better described by a two-dimensional model. (Copies available exclusively from MIT Libraries, Rm. 14-0551, Cambridge, MA 02139-4307. Ph. 617-253-5668; Fax 617-253-1690.).

Epitaxial Ba2IrO4 thin-films grown on SrTiO3 substrates by pulsed laser deposition

NASA Astrophysics Data System (ADS)

Nichols, J.; Korneta, O. B.; Terzic, J.; Cao, G.; Brill, J. W.; Seo, S. S. A.

2014-03-01

We have synthesized epitaxial Ba2IrO4 (BIO) thin-films on SrTiO3 (001) substrates by pulsed laser deposition and studied their electronic structure by dc-transport and optical spectroscopic experiments. We have observed that BIO thin-films are insulating but close to the metal-insulator transition boundary with significantly smaller transport and optical gap energies than its sister compound, Sr2IrO4. Moreover, BIO thin-films have both an enhanced electronic bandwidth and electronic-correlation energy. Our results suggest that BIO thin-films have great potential for realizing the interesting physical properties predicted in layered iridates.

Polycrystalline Superconducting Thin Films: Texture Control and Critical Current Density

NASA Astrophysics Data System (ADS)

Yang, Feng

1995-01-01

The growth processes of polycrystalline rm YBa_2CU_3O_{7-X} (YBCO) and yttria-stabilized-zirconia (YSZ) thin films have been developed. The effectiveness of YSZ buffer layers on suppression of the reaction between YBCO thin films and metallic substrates was carefully studied. Grown on the chemically inert surfaces of YSZ buffer layers, YBCO thin films possessed good quality of c-axis alignment with the c axis parallel to the substrate normal, but without any preferred in-plane orientations. This leads to the existence of a large percentage of the high-angle grain boundaries in the YBCO films. The critical current densities (rm J_{c}'s) found in these films were much lower than those in single crystal YBCO thin films, which was the consequence of the weak -link effect of the high-angle grain boundaries in these films. It became clear that the in-plane alignment is vital for achieving high rm J_{c }s in polycrystalline YBCO thin films. To induce the in-plane alignment, ion beam-assisted deposition (IBAD) technique was integrated into the conventional pulsed laser deposition process for the growth of the YSZ buffer layers. It was demonstrated that using IBAD the in-plane orientations of the YSZ grains could be controlled within a certain range of a common direction. This ion -bombardment induced in-plane texturing was explained using the anisotropic sputtering yield theory. Our observations and analyses have provided valuable information on the optimization of the IBAD process, and shed light on the texturing mechanism in YSZ. With the in-plane aligned YSZ buffer layers, YBCO thin films grown on metallic substrates showed improved rm J_{c}s. It was found that the in-plane alignment of YSZ and that of YBCO were closely related. A direct correlation was revealed between the rm J_{c} value and the degree of the in-plane alignment for the YBCO thin films. To explain this correlation, a numerical model was applied to multi-grain superconducting paths with different

Incorporation of surface plasmon resonance with novel valinomycin doped chitosan-graphene oxide thin film for sensing potassium ion.

PubMed

Zainudin, Afiq Azri; Fen, Yap Wing; Yusof, Nor Azah; Al-Rekabi, Sura Hmoud; Mahdi, Mohd Adzir; Omar, Nur Alia Sheh

2018-02-15

In this study, the combination of novel valinomycin doped chitosan-graphene oxide (C-GO-V) thin film and surface plasmon resonance (SPR) system for potassium ion (K + ) detection has been developed. The novel C-GO-V thin film was deposited on the gold surface using spin coating technique. The system was used to monitor SPR signal for K + in solution with and without C-GO-V thin film. The K + can be detected by measuring the SPR signal when C-GO-V thin film is exposed to K + in solution. The sensor produces a linear response for K + ion up to 100ppm with sensitivity and detection limit of 0.00948°ppm -1 and 0.001ppm, respectively. These results indicate that the C-GO-V film is high potential as a sensor element for K + that has been proved by the SPR measurement. Copyright © 2017 Elsevier B.V. All rights reserved.

Effect of rapid thermal annealing on the structural and electrical properties of RF sputtered CCTO thin film

NASA Astrophysics Data System (ADS)

Tripathy, N.; Das, K. C.; Ghosh, S. P.; Bose, G.; Kar, J. P.

2017-02-01

CaCu3Ti4O12 (CCTO) thin films have been deposited by RF magnetron sputtering on silicon substrates at room temperature. As-deposited thin films were subjected to rapid thermal annealing (RTA) at different temperatures ranging from 850°C to 1000°C. XRD and capacitance - voltage studies indicate that the structural and electrical properties of CCTO thin film strongly depend upon the annealing temperature. XRD pattern of CCTO thin film annealed at 950°C revealed the polycrystalline nature with evolutions of microstructures. Electrical properties of the dielectric films were investigated by fabricating Al/CCTO/Si metal oxide semiconductor structure. Electrical properties were found to be deteriorated with increasing in annealing temperature.

Electrodeposition of Metal Matrix Composites and Materials Characterization for Thin-Film Solar Cells

DTIC Science & Technology

2017-12-04

34High-Concentration III-V Multijunction Solar Cells," 2017, <http://www.nrel.gov/ pv /high-concentration-iii-v-multijunction- solar - cells.html>. O. K...AFRL-RV-PS- AFRL-RV-PS- TR-2017-0174 TR-2017-0174 ELECTRODEPOSITION OF METAL MATRIX COMPOSITES AND MATERIALS CHARACTERIZATION FOR THIN-FILM SOLAR ...0242 Electrodeposition of Metal Matrix Composites and Materials Characterization for Thin-Film Solar Cells 5b. GRANT NUMBER 5c. PROGRAM ELEMENT

Enhanced energy storage and pyroelectric properties of highly (100)-oriented (Pb1-x-yLaxCay)Ti1-x/4O3 thin films derived at low temperature

NASA Astrophysics Data System (ADS)

Zhu, Hanfei; Ma, Hongfang; Zhao, Yuyao

2018-05-01

Highly (100)-oriented (Pb1-x-yLaxCay)Ti1-x/4O3 (x = 0.15, y = 0.05; x = 0.1, y = 0.1; x = 0.05, y = 0.15) thin films were deposited on Pt/Ti/SiO2/Si substrates at a low temperature of 450 °C via a sol-gel route. It was found that all the (Pb1-x-yLaxCay)Ti1-x/4O3 thin films could be completely crystallized and the content of La/Ca showed a significant effect on the electrical properties of films. Among the three films, the (Pb1-x-yLaxCay)Ti1-x/4O3 (x = 0.1, y = 0.1) thin film exhibited the enhanced overall electrical properties, such as a low dielectric loss (tan ⁡ δ < 0.08) and leakage current (J ∼ 4.6 ×10-5 A/cm2), a high recoverable energy density (Wre ∼ 15 J/cm3), as well as a large pyroelectric coefficient (p ∼ 190 μC/m2K) and figure of merit (Fd‧∼ 77 μC /m2K). The findings suggest that the fabricated thin films with a good (100) orientation can be an attractive candidate for applications in Si-based energy storage and pyroelectric devices.

Controlled crystal growth of layered-perovskite thin films as an approach to study their basic properties

NASA Astrophysics Data System (ADS)

Watanabe, Takayuki; Funakubo, Hiroshi

2006-09-01

This article describes the current progress in thin bismuth layer-structured ferroelectric films (BLSFs) including SrBi2Ta2O9 and (Bi,La)4Ti3O12, particularly those developed in the last ten years. BLSF thin films can be applied to ferroelectric random access memories because of their durable fatigue-free properties and lead-free composition. We will briefly introduce epitaxial thin films grown on a variety of substrates. Because of the difficulty in growing single crystals of sufficient size to characterize the ferroelectric behavior in specific crystal growth directions, we will characterize epitaxially grown thin films to obtain basic information about the anisotropic switching behavior, which is important for evaluating the performance of emerging materials. We will then discuss the fiber-textured growth on the (111)Pt-covered Si substrates of SrBi2Ta2O9 and Bi4Ti3O12 thin films. Because we expect that the spread crystal orientation will affect the bit-to-bit errors, we believe that the fiber-textured growth and the characterization technique for the deposited film orientation are interesting from a practical standpoint. Another specific challenge of thin film growth is the growth of a-axis-(polar axis)-oriented films. a-/b-axis-oriented films are characterized both crystallographically and by electric hysteresis loop. The hysteresis performance was in accordance with the volume fraction of the a /b domains; however, no evidence for 90° switching of the b domain by an external electric field was obtained. The control of film orientation also allows systematic studies on the effects of a structural modification and relation between spontaneous polarization and Curie temperature, examples of which are given in this paper. After a short description of the piezoelectric properties, we will conclude with a summary and the future prospects of BLSF thin films for research and applications.

Deposition and characterization of aluminum magnesium boride thin film coatings

NASA Astrophysics Data System (ADS)

Tian, Yun

Boron-rich borides are a special group of materials possessing complex structures typically comprised of B12 icosahedra. All of the boron-rich borides sharing this common structural unit exhibit a variety of exceptional physical and electrical properties. In this work, a new ternary boride compound AlMgB14, which has been extensively studied in bulk form due to its novel mechanical properties, was fabricated into thin film coatings by pulsed laser deposition (PLD) technology. The effect of processing conditions (laser operating modes, vacuum level, substrate temperature, and postannealing, etc.) on the composition, microstructure evolution, chemical bonding, and surface morphology of AlMgB14 thin film coatings has been investigated by X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), transmission electron microscopy (TEM), atomic force microscopy (AFM) and Fourier transform infrared (FTIR) spectrometry; the mechanical, electrical, and optical properties of AlMgB14 thin films have been characterized by nanoindentation, four-point probe, van der Pauw Hall measurement, activation energy measurement, and UV-VIS-NIR spectrophotometer. Experimental results show that AlMgB14 films deposited in the temperature range of 300 K - 873 K are amorphous. Depositions under a low vacuum level (5 x 10-5 Torr) can introduce a significant amount of C and O impurities into AlMgB14 films and lead to a complex oxide glass structure. Orthorhombic AlMgB14 phase cannot be obtained by subsequent high temperature annealing. By contrast, the orthorhombic AlMgB 14 crystal structure can be attained via high temperature-annealing of AlMgB14 films deposited under a high vacuum level (< 3 x 10-6 Torr), accompanied by strong texture formation. Low vacuum level-as deposited AlMgB14 films have low hardness (10 GPa), but high vacuum level-as deposited AlMgB14 films exhibit an extremely high hardness (45 GPa - 51 GPa), and the higher deposition temperature results in still higher hardness

Thin film phase diagram of iron nitrides grown by molecular beam epitaxy

NASA Astrophysics Data System (ADS)

Gölden, D.; Hildebrandt, E.; Alff, L.

2017-01-01

A low-temperature thin film phase diagram of the iron nitride system is established for the case of thin films grown by molecular beam epitaxy and nitrided by a nitrogen radical source. A fine-tuning of the nitridation conditions allows for growth of α ‧ -Fe8Nx with increasing c / a -ratio and magnetic anisotropy with increasing x until almost phase pure α ‧ -Fe8N1 thin films are obtained. A further increase of nitrogen content below the phase decomposition temperature of α ‧ -Fe8N (180 °C) leads to a mixture of several phases that is also affected by the choice of substrate material and symmetry. At higher temperatures (350 °C), phase pure γ ‧ -Fe4N is the most stable phase.

Low-temperature photoluminescence study of thin epitaxial GaAs films on Ge substrates

NASA Astrophysics Data System (ADS)

Brammertz, Guy; Mols, Yves; Degroote, Stefan; Motsnyi, Vasyl; Leys, Maarten; Borghs, Gustaaf; Caymax, Matty

2006-05-01

Thin epitaxial GaAs films, with thickness varying from 140 to 1000 nm and different Si doping levels, were grown at 650 °C by organometallic vapor phase epitaxy on Ge substrates and analyzed by low-temperature photoluminescence (PL) spectroscopy. All spectra of thin GaAs on Ge show two different structures, one narrow band-to-band (B2B) structure at an energy of ~1.5 eV and a broad inner-band-gap (IB) structure at an energy of ~1.1 eV. Small strain in the thin GaAs films causes the B2B structure to be separated into a light-hole and a heavy-hole peak. At 2.5 K the good structural quality of the thin GaAs films on Ge can be observed from the narrow excitonic peaks. Peak widths of less than 1 meV are measured. GaAs films with thickness smaller than 200 nm show B2B PL spectra with characteristics of an n-type doping level of approximately 1018 at./cm3. This is caused by heavy Ge diffusion from the substrate into the GaAs at the heterointerface between the two materials. The IB structure observed in all films consists of two Gaussian peaks with energies of 1.04 and 1.17 eV. These deep trapping states arise from Ge-based complexes formed within the GaAs at the Ge-GaAs heterointerface, due to strong diffusion of Ge atoms into the GaAs. Because of similarities with Si-based complexes, the peak at 1.04 eV was identified to be due to a GeGa-GeAs complex, whereas the peak at 1.17 eV was attributed to the GeGa-VGa complex. The intensity of the IB structure decreases strongly as the GaAs film thickness is increased. PL intensity of undoped GaAs films containing antiphase domains (APDs) is four orders of magnitude lower than for similar films without APDs. This reduction in intensity is due to the electrically active Ga-Ga and As-As bonds at the boundaries between the different APDs. When the Si doping level is increased, the PL intensity of the APD-containing films is increased again as well. A film containing APDs with a Si doping level of ~1018 at./cm3 has only a factor 10

The promise of solution-processed Fe 2GeS 4 thin films in iron chalcogenide photovoltaics

DOE Office of Scientific and Technical Information (OSTI.GOV)

Liu, Mimi; Berg, Dominik M.; Hwang, Po-Yu

The olivine Fe 2GeS 4, featuring non-toxic elements, cost-effective synthesis, and suitable optoelectronic properties, recently emerged as a promising light-absorbing candidate. Fe 2GeS 4 precursor powders obtained via a simple solution-based process were converted to highly crystalline Fe 2GeS 4 powders upon a thermal treatment in controlled atmosphere. Thin films fabricated by dip coating in the Fe 2GeS 4 precursor dispersion and subjected to the same thermal treatment render high-purity Fe 2GeS 4 thin films with a band gap of 1.4 eV, measured by room-temperature photoluminescence. Using Fe 2GeS 4 thin films as the sole absorber in a solution-based solarmore » cell, open-circuit voltages of 361 mV are observed, while the use of the Fe 2GeS 4 films as counter electrodes in dye-sensitized solar cell constructs enhances the overall power conversion efficiency of the cell by a factor of five. Finally, this is the first report of a photovoltaic device based onFe 2GeS 4.« less

The promise of solution-processed Fe 2GeS 4 thin films in iron chalcogenide photovoltaics

DOE PAGES

Liu, Mimi; Berg, Dominik M.; Hwang, Po-Yu; ...

2018-02-06

The olivine Fe 2GeS 4, featuring non-toxic elements, cost-effective synthesis, and suitable optoelectronic properties, recently emerged as a promising light-absorbing candidate. Fe 2GeS 4 precursor powders obtained via a simple solution-based process were converted to highly crystalline Fe 2GeS 4 powders upon a thermal treatment in controlled atmosphere. Thin films fabricated by dip coating in the Fe 2GeS 4 precursor dispersion and subjected to the same thermal treatment render high-purity Fe 2GeS 4 thin films with a band gap of 1.4 eV, measured by room-temperature photoluminescence. Using Fe 2GeS 4 thin films as the sole absorber in a solution-based solarmore » cell, open-circuit voltages of 361 mV are observed, while the use of the Fe 2GeS 4 films as counter electrodes in dye-sensitized solar cell constructs enhances the overall power conversion efficiency of the cell by a factor of five. Finally, this is the first report of a photovoltaic device based onFe 2GeS 4.« less

Experimental study of Pulsed Laser Deposited Cu2ZnSnS 4 (CZTS) thin films for photovoltaic applications

NASA Astrophysics Data System (ADS)

Nandur, Abhishek S.

Thin film solar cells are gaining momentum as a renewable energy source. Reduced material requirements (< 2 mum in total film thickness) coupled with fast, low-cost production processes make them an ideal alternative to Si (>15 mum in total thickness) solar cells. Among the various thin film solar absorbers that have been proposed, CZTS (Cu2ZnSnS4) has become the subject of intense interest because of its optimal band gap (1.45 eV), high absorption coefficient (104 cm--1 ) and abundant elemental components. Pulsed Laser Deposition (PLD) provides excellent control over film composition since films are deposited under high vacuum with excellent stoichiometry transfer from the target. Defect-free, near-stoichiometric poly-crystalline CZTS thin films were deposited using PLD from a stoichiometrically close CZTS target (Cu2.6Zn1.1Sn0.7S3.44). The effects of fabrication parameters such as laser energy density, deposition time, substrate temperature and sulfurization (annealing in sulfur) on the surface morphology, composition and optical absorption of the CZTS thin films were examined. The results show that the presence of secondary phases, present both in the bulk and on the surface, affected the electrical and optical properties of the CZTS thin films and the CZTS based TFSCs. After selectively etching away the secondary phases with DIW, HCl and KCN, it was observed that their removal improved the performance of CZTS based TFSCs. Optimal CZTS thin films exhibited an optical band gap of 1.54 eV with an absorption coefficient of 4x10 4cm-1 with a low volume of secondary phases. A TFSC fabricated with the best CZTS thin film obtained from the experimental study done in this thesis showed a conversion efficiency of 6.41% with Voc = 530 mV, Jsc= 27.5 mA/cm2 and a fill factor of 0.44.

Nanocrystalline silicon thin films and grating structures for solar cells

NASA Astrophysics Data System (ADS)

Juneja, Sucheta; Sudhakar, Selvakumar; Khonina, Svetlana N.; Skidanov, Roman V.; Porfirevb, Alexey P.; Moissev, Oleg Y.; Kazanskiy, Nikolay L.; Kumar, Sushil

2016-03-01

Enhancement of optical absorption for achieving high efficiencies in thin film silicon solar cells is a challenge task. Herein, we present the use of grating structure for the enhancement of optical absorption. We have made grating structures and same can be integrated in hydrogenated micro/nanocrystalline silicon (μc/nc-Si: H) thin films based p-i-n solar cells. μc/nc-Si: H thin films were grown using plasma enhanced chemical vapor deposition method. Grating structures integrated with μc/nc-Si: H thin film solar cells may enhance the optical path length and reduce the reflection losses and its characteristics can be probed by spectroscopic and microscopic technique with control design and experiment.

Thin-film optical initiator

DOEpatents

Erickson, Kenneth L.

2001-01-01

A thin-film optical initiator having an inert, transparent substrate, a reactive thin film, which can be either an explosive or a pyrotechnic, and a reflective thin film. The resultant thin-film optical initiator system also comprises a fiber-optic cable connected to a low-energy laser source, an output charge, and an initiator housing. The reactive thin film, which may contain very thin embedded layers or be a co-deposit of a light-absorbing material such as carbon, absorbs the incident laser light, is volumetrically heated, and explodes against the output charge, imparting about 5 to 20 times more energy than in the incident laser pulse.

Structural and magnetic analysis of Cu, Co substituted NiFe{sub 2}O{sub 4} thin films

DOE Office of Scientific and Technical Information (OSTI.GOV)

Sharma, Hakikat; Bala, Kanchan; Negi, N. S.

2016-05-23

In the present work we prepared NiFe{sub 2}O{sub 4}, Ni{sub 0.95}Cu{sub 0.05}Fe{sub 2}O{sub 4} and Ni{sub 0.94}Cu{sub 0.05}Co{sub 0.01} Fe{sub 2}O{sub 4} thin films by metallo-organic decomposition method (MOD) using spin coating technique. The thin films were analyzed by X-ray diffractometer (XRD) and Atomic force microscope (AFM) for structural studies. The XRD patterns confirmed the ferrite phase of thin films. From AFM, we analyzed surface morphology, calculated grain size (GS) and root mean square roughness (RMSR). Room temperature magnetic properties were investigated by vibrating sample magnetometer (VSM).

Synthesis, characterization, and photocatalytic properties of nanocrystalline NZO thin films

NASA Astrophysics Data System (ADS)

Aryanto, D.; Hastuti, E.; Husniya, N.; Sudiro, T.; Nuryadin, B. W.

2018-03-01

Nanocrystalline Ni-doped ZnO (NZO) thin films were synthesized on glass substrate using sol-gel spin coating methods. The effect of annealing on the structural and optical properties of nanocrystalline thin film was studied using X-ray diffractometer (XRD), field emission scanning electron microscopy (FESEM), UV-VIS spectrophotometry, and photoluminescence (PL). The results showed that the annealing temperature strongly influenced the physical properties of nanocrystalline NZO thin films. The photocatalytic properties of nanocrystalline NZO thin films were evaluated using an aqueous solution of Rhodamine-B. The photocatalytic activity of nanocrystalline NZO thin films increased with the increase of annealing temperature. The results indicated that the structure, morphology, and band gap energy of nanocrystalline NZO thin films played an important role in photocatalytic activity.

A weak-light-responsive TiO2/g-C3N4 composite film: photocatalytic activity under low-intensity light irradiation.

PubMed

Wang, Peifang; Guo, Xiang; Rao, Lei; Wang, Chao; Guo, Yong; Zhang, Lixin

2018-05-10

A TiO 2 /g-C 3 N 4 composite photocatalytic film was prepared by in situ synthesis method and its photocatalytic capability under weak-visible-light condition was studied. The co-precursor with different ratio of melamine and TiO 2 sol-gel precursor were treated using ultrasonic mixing, physical deposition, and co-sintering method to form the smooth, white-yellow, and compact TiO 2 /g-C 3 N 4 composite films. The prepared TiO 2 /g-C 3 N 4 materials were characterized by SEM, TEM, EDS, XRD, BET, VBXPS, and UV-vis diffuse reflectance spectra. The results of composite showed that TiO 2 and g-C 3 N 4 have close interfacial connections which are favorable to charge transfer between these two semiconductors with suitable band structure, g-C 3 N 4 retard the anatase-to-rutile phase transition of TiO 2 significantly, the specific surface area were increased with g-C 3 N 4 ratio raised. Under weak-light irradiation, composite films photocatalytic experiments exhibited RhB removal efficiency approaching 90% after three recycles. Powders suspension degradation experiments revealed the removal efficiency of TiO 2 /g-C 3 N 4 (90.8%) was higher than pure TiO 2 (52.1%) and slightly lower than pure g-C 3 N 4 (96.6%). By control experiment, the enhanced photocatalysis is ascribed to the combination of TiO 2 and g-C 3 N 4 , which not only produced thin films with greater stability but also formed heterojunctions that can be favorable to charge transfer between these two semiconductors with suitable band structure. This study presents the potential application of photocatalytic film in the wastewater treatment under weak-light situation.

Effect of thermal annealing on the structural and optical properties of Cu2FeSnS4 thin films grown by vacuum evaporation method

NASA Astrophysics Data System (ADS)

Oueslati, H.; Rabeh, M. Ben; Kanzari, M.

2018-02-01

In this work, the effect of different types of thermal annealing on the properties of Cu2FeSnS4 (CFTS) thin films deposited by thermal evaporation at room temperature on glass substrate were investigated. CFTS powder was synthesized by direct melting of the constituent elements taken in stoichiometry compositions. The X-ray diffraction experimental data indicating that the Cu2FeSnS4 powder illustrating a stannite structure in space group I\\bar {4}2m. From the XRD analysis we have found that the polycrystalline CFTS thin film was only obtained by thermal annealed in sulfur atmosphere under a high vacuum of 400 °C temperature during 2 h. Optical study reveals that the thin films have relatively high absorption coefficients (≈ 105cm-1) and the values of optical band gap energy ranged between 1.38 and 1.48 eV. Other optical parameters were evaluated according to the models of Wemple Di-Domenico and Spitzer-Fan. Finally, hot probe measurements of CFTS thin films reveal p-type conductivity.

Phase Composition of Samarium Niobate and Tantalate Thin Films Prepared by Sol-Gel Method

NASA Astrophysics Data System (ADS)

Bruncková, H.; Medvecký, Ľ.; Múdra, E.; Kovalčiková, A.; Ďurišin, J.; Šebek, M.; Girman, V.

2017-12-01

Samarium niobate SmNbO4 (SNO) and tantalate SmTaO4 (STO) thin films ( 100 nm) were prepared by sol-gel/spin-coating process on alumina substrates with PZT interlayer and annealing at 1000°C. The precursors of films were synthesized using Nb or Ta tartrate complexes. The improvement of the crystallinity of monoclinic M'-SmTaO4 phase via heating was observed through the coexistence of small amounts of tetragonal T-SmTa7O19 phase in STO precursor at 1000°C. The XRD results of SNO and STO films confirmed monoclinic M-SmNbO4 and M'-SmTaO4 phases, respectively, with traces of orthorhombic O-SmNbO4 (in SNO). In STO film, the single monoclinic M'-SmTaO4 phase was revealed. The surface morphology and topography of thin films were investigated by SEM and AFM analysis. STO film was smoother with roughness 3.2 nm in comparison with SNO (6.3 nm). In the microstructure of SNO film, small spherical ( 50 nm) and larger cuboidal particles ( 100 nm) of the SmNbO4 phase were observed. In STO, compact clusters composed of fine spherical SmTaO4 particles ( 20-50 nm) were found. Effect of samarium can contribute to the formation different polymorphs of these films for the application to environmental electrolytic thin film devices.

Epitaxial integration of CoFe2O4 thin films on Si (001) surfaces using TiN buffer layers

NASA Astrophysics Data System (ADS)

Prieto, Pilar; Marco, José F.; Prieto, José E.; Ruiz-Gomez, Sandra; Perez, Lucas; del Real, Rafael P.; Vázquez, Manuel; de la Figuera, Juan

2018-04-01

Epitaxial cobalt ferrite thin films with strong in-plane magnetic anisotropy have been grown on Si (001) substrates using a TiN buffer layer. The epitaxial films have been grown by ion beam sputtering using either metallic, CoFe2, or ceramic, CoFe2O4, targets. X-ray diffraction (XRD) and Rutherford spectrometry (RBS) in random and channeling configuration have been used to determine the epitaxial relationship CoFe2O4 [100]/TiN [100]/Si [100]. Mössbauer spectroscopy, in combination with XRD and RBS, has been used to determine the composition and structure of the cobalt ferrite thin films. The TiN buffer layer induces a compressive strain in the cobalt ferrite thin films giving rise to an in-plane magnetic anisotropy. The degree of in-plane anisotropy depends on the lattice mismatch between CoFe2O4 and TiN, which is larger for CoFe2O4 thin films grown on the reactive sputtering process with ceramic targets.

Effects of air annealing on CdS quantum dots thin film grown at room temperature by CBD technique intended for photosensor applications

DOE Office of Scientific and Technical Information (OSTI.GOV)

Shaikh, Shaheed U.; Desale, Dipalee J.; Siddiqui, Farha Y.

2012-11-15

Graphical abstract: The effect of different intensities (40, 60 100 and 200 W) of light on CdS quantum dots thin film annealed at 350 °C indicating enhancement in (a) photo-current and (b) photosensitivity. Highlights: ► The preparation of CdS nanodot thin film at room temperature by M-CBD technique. ► Study of air annealing on prepared CdS nanodots thin film. ► The optimized annealing temperature for CdS nanodot thin film is 350 °C. ► Modified CdS thin films can be used in photosensor application. -- Abstract: CdS quantum dots thin-films have been deposited onto the glass substrate at room temperature usingmore » modified chemical bath deposition technique. The prepared thin films were further annealed in air atmosphere at 150, 250 and 350 °C for 1 h and subsequently characterized by scanning electron microscopy, ultraviolet–visible spectroscopy, electrical resistivity and I–V system. The modifications observed in morphology and opto-electrical properties of the thin films are presented.« less

Fabrication and etching processes of silicon-based PZT thin films

NASA Astrophysics Data System (ADS)

Zhao, Hongjin; Liu, Yanxiang; Liu, Jianshe; Ren, Tian-Ling; Liu, Li-Tian; Li, Zhijian

2001-09-01

Lead-zirconate-titanate (PZT) thin films on silicon were prepared by a sol-gel method. Phase characterization and crystal orientation of the films were investigated by x-ray diffraction analysis (XRD). It was shown that the PZT thin films had a perfect perovskite structure after annealed at a low temperature of 600 degrees C. PZT thin films were chemically etched using HCl/HF solution through typical semiconductor lithographic process, and the etching condition was optimized. The scanning electron microscopy results indicated that the PZT thin film etching problem was well solved for the applications of PZT thin film devices.

Memristive Properties of Thin Film Cuprous Oxide

DTIC Science & Technology

2011-03-01

Equation Chapter 1 Section 1 MEMRISTIVE PROPERTIES OF THIN FILM CUPROUS OXIDE THESIS Brett C...Force Base, Ohio APPROVED FOR PUBLIC RELEASE; DISTRIBUTION UNLIMITED The views expressed in this thesis are those of the...MEMRISTIVE PROPERTIES OF THIN FILM CUPROUS OXIDE THESIS Presented to the Faculty Department of Engineering Physics Graduate School of

Switching of magnetic easy-axis using crystal orientation for large perpendicular coercivity in CoFe2O4 thin film

PubMed Central

Shirsath, Sagar E.; Liu, Xiaoxi; Yasukawa, Yukiko; Li, Sean; Morisako, Akimitsu

2016-01-01

Perpendicular magnetization and precise control over the magnetic easy axis in magnetic thin film is necessary for a variety of applications, particularly in magnetic recording media. A strong (111) orientation is successfully achieved in the CoFe2O4 (CFO) thin film at relatively low substrate temperature of 100 °C, whereas the (311)-preferred randomly oriented CFO is prepared at room temperature by the DC magnetron sputtering technique. The oxygen-deficient porous CFO film after post-annealing gives rise to compressive strain perpendicular to the film surface, which induces large perpendicular coercivity. We observe the coercivity of 11.3 kOe in the 40-nm CFO thin film, which is the highest perpendicular coercivity ever achieved on an amorphous SiO2/Si substrate. The present approach can guide the systematic tuning of the magnetic easy axis and coercivity in the desired direction with respect to crystal orientation in the nanoscale regime. Importantly, this can be achieved on virtually any type of substrate. PMID:27435010

Effect of external magnetic field on the crystal growth of nano-structured Zn xMn 1- x+ yZr yFe 2-2 yO 4 thin films

NASA Astrophysics Data System (ADS)

Anjum, Safia; Rafique, M. S.; Khaleeq-ur-Rahaman, M.; Siraj, K.; Usman, Arslan; Ahsan, A.; Naseem, S.; Khan, K.

2011-06-01

Zn 0.2Mn 0.81Zr 0.01Fe 1.98O 4 and Zn 0.2Mn 0.83Zr 0.03Fe 1.94O 4 thin films with different concentrations of Mn and Zr have been deposited on single crystal n-Si (400) at room temperature (RT) by pulse laser deposition technique (PLD). The films have been deposited under two conditions: (i) with the applied external magnetic field across the propagation of the plume (ii) without applied external magnetic field ( B=0). XRD results show the films have spinel cubic structure when deposited in the presence of magnetic field. SEM and AFM observations clearly show the effect of external applied magnetic field on the growth of films in terms of small particle size, improved uniformity and lower r.m.s. roughness. Thin films deposited under the influence of external magnetic field exhibit higher magnetization as measured by the VSM. The optical band gap energy Eg, refractive index n, reflection, absorption and the thickness of the thin films were measured by spectroscopy ellipsometer. The reflection of Zn 0.2Mn 0.83Zr 0.03Fe 1.94O 4 thin films is higher than Zn 0.2Mn 0.81Zr 0.01Fe 1.98O 4 thin films due to the greater concentration of Zr. The thicknesses of the thin films under the influence of external magnetic field are larger than the films grown without field for both samples. The optical band gap energy Eg decreases with increasing film thickness. The films with external magnetic field are found highly absorbing in nature due to the larger film thickness.

Polarized optical absorption and photoluminescence measurements in single-crystal thin films of 4'-dimethylamino-N-methyl-4-stilbazolium tosylate

NASA Astrophysics Data System (ADS)

Bhowmik, Achintya K.; Xu, Jianjun; Thakur, Mrinal

1999-11-01

Single-crystal thin films of the anhydrous (red) and the hydrated (orange) phases of the organic salt 4'-dimethylamino-N-methyl-4-stilbazolium tosylate were grown by a modification of the shear method. The optical absorption coefficients of the films were measured with light polarized along and normal to the dipole/molecular axis at both resonant and off-resonant wavelengths, and a strong dichroism was observed at the resonant wavelengths. The absorption measurements are important considering potential applications of these films (red phase) in high-speed single-pass thin-film electro-optic modulators [M. Thakur, J. Xu, A. Bhowmik, and L. Zhou, Appl. Phys. Lett. 74, 635 (1999)] and other photonic devices. Highly polarized photoluminescence (PL) has been observed in these films. The PL efficiencies of the red- and orange-phase single-crystal films were measured to be about 12% and 14%, respectively, which are significantly higher than the maximum PL efficiency measured in solution (3%).

Physical properties of high performance fluoride ion conductor BaSnF4 thin films by pulsed laser deposition

NASA Astrophysics Data System (ADS)

Patro, L. N.; Ravi Chandra Raju, N.; Meher, S. R.; Kamala Bharathi, K.

2013-09-01

This article presents the results on the growth and characterization of BaSnF4 thin films on glass substrates prepared by pulsed laser deposition technique. The structural results of BaSnF4 thin film carried out by glancing angle X-ray diffraction technique indicates the formation of the film with similar structure (tetragonal, P4/nmm) to the bulk target material. The absorption coefficient and band gap of the film is determined by suitable analysis of the transmittance spectra. The transport properties of the thin films are studied using impedance spectroscopy in the temperature range of 323-573 K. The frequency-dependent imaginary part of impedance plot shows that the conductivity relaxation is non-Debye in nature. The scaling behavior of the imaginary part of impedance at various frequencies indicates temperature-independent relaxation behavior.

Epitaxial growth of Ti{sub 3}SiC{sub 2} thin films with basal planes parallel or orthogonal to the surface on {alpha}-SiC

DOE Office of Scientific and Technical Information (OSTI.GOV)

Drevin-Bazin, A.; Barbot, J. F.; Alkazaz, M.

2012-07-09

The growth of Ti{sub 3}SiC{sub 2} thin films were studied onto {alpha}-SiC substrates differently oriented by thermal annealing of TiAl layers deposited by magnetron sputtering. For any substrate's orientation, transmission electron microscopy coupled with x-ray diffraction showed the coherent epitaxial growth of Ti{sub 3}SiC{sub 2} films along basal planes of SiC. Specifically for the (1120) 4H-SiC, Ti{sub 3}SiC{sub 2} basal planes are found to be orthogonal to the surface. The continuous or textured nature of Ti{sub 3}SiC{sub 2} films does not depend of the SiC stacking sequence and is explained by a step-flow mechanism of growth mode. The ohmic charactermore » of the contact was confirmed by current-voltage measurements.« less

Preparation and characterization of sprayed FTO thin films

NASA Astrophysics Data System (ADS)

Abd-Lefdil, M.; Diaz, R.; Bihri, H.; Aouaj, M. Ait; Rueda, F.

2007-06-01

Fluorine doped tin oxide (FTO) thin films have been prepared by spray pyrolysis technique with no further annealing. Films with 2.5% of fluorine grown at 400 °C present a single phase and exhibit a tetragonal structure with lattice parameters a = 4.687 Å and c = 3.160 Å. Scanning electron micrographs showed homogeneous surfaces with average grain size around 190 nm. The films are transparent in the visible zone and exhibit a high reflectance in the near infrared region. The best electrical resistivity was 6.3 × 10-4 Ω cm for FTO with 2.5% of fluorine. The ratio of transmittance in the visible to the sheet resistance are in the 0.57 × 10-2 1.96 × 10-2 {Ω }-1 range.

Growth of nanocrystalline Cu2ZnSnS4 thin films using the spray pyrolysis technique and their characterization

NASA Astrophysics Data System (ADS)

Chandel, Tarun; Halaszova, Sona; Prochazka, Michal; Hasko, Daniel; Velic, Dusan; Thakur, Vikas; Dwivedi, Shailendra Kumar; Zaman, M. Buhanuz; Rajaram, Poolla

2018-05-01

Nanocrystalline thin films of Cu2ZnSnS4 (CZTS) were grown on the glass substrates using the spray pyrolysis technique. The films were grown at a substrate temperature of 300 °C after which they were annealed at 350 °C in vacuum. X-ray diffraction (XRD) studies showed that the films crystallized in the kesterite structure. Energy dispersive analysis of X-rays (EDAX) studies showed that the films possess the desired stoichiometry i.e. the proportion of Cu:Zn:Sn:S in the CZTS solid solution is close to 2:1:1:4. Secondary Ions Mass Spectroscopy (SIMS) depth profiling confirmed the uniformity in elemental composition along the depth of the films. SEM studies showed that the films are covered with CZTS particles forming sheet like structures. AFM studies show that the size of the particles on the surface of the films is around 10-15 nm. UV-VIS-NIR transmission spectra were used to determine the optical band gap of the CZTS films which was found to be around 1.55eV.

Optical and structural properties of indium doped bismuth selenide thin films

NASA Astrophysics Data System (ADS)

Pavagadhi, Himanshu; Vyas, S. M.; Patel, Piyush; Patel, Vimal; Patel, Jaydev; Jani, M. P.

2015-08-01

In: Bi2Se3 crystals were grown by Bridgman method at a growth velocity of 0.5cm/h with temperature gradient of 650 C/cm in our laboratory. The thin films of In:Bi2se3 were grown on amorphous substrate (glass) at a room temperature under a pressure of 10-4Pa by thermal evaporation technique. Thin film were deposited at various thicknesses and optical absorption spectrum of such thin films, obtain in wave no. range 300 to 2600 cm-1. The optical energy gap calculated from this data were found to be inverse function of square of thickness, particularly for thickness about 1800 Å or less. This dependence is explained in terms of quantum size effect. For thicker films, the bandgap is found to be independent of film thickness. For the surface stud of the as grown thin film by using AFM, which shows continuous film with some step height and surface roughness found in terms of few nm and particle size varies with respect to thickness.

Solution-processed hybrid organic-inorganic complementary thin-film transistor inverter

NASA Astrophysics Data System (ADS)

Cheong, Heajeong; Kuribara, Kazunori; Ogura, Shintaro; Fukuda, Nobuko; Yoshida, Manabu; Ushijima, Hirobumi; Uemura, Sei

2016-04-01

We investigated hybrid organic-inorganic complementary inverters with a solution-processed indium-gallium-zinc-oxide (IGZO) n-channel thin-film transistor (TFT) and p-channel TFTs using the high-uniformity polymer poly[2,5-bis(alkyl)pyrrolo[3,4-c]pyrrolo-1,4(2H,5H)-dione-alt-5,5-di(thiophene-2-yl)-2,2-(E)-2-(2-(thiophen-2-yl)vinyl)thiophene] (PDVT-10). The IGZO TFT was fabricated at 150 °C for 1 min. It showed a high field-effect mobility of 0.9 cm2·V-1·s-1 and a high on/off current ratio of 107. A hybrid complementary inverter was fabricated by combining IGZO with a PDVT-10 thin-film transistor and its operation was confirmed.

Synthesis of thin film containing 4-amino-1,2,4-triazole iron(II) complexes

DOE Office of Scientific and Technical Information (OSTI.GOV)

Onggo, Djulia, E-mail: djulia@Chem.itb.ac.id

The Iron(II) complex with 4-amino-1,2,4 triazole (NH{sub 2}-trz) ligand has potential applications as smart material since the compounds show a distinct color change from lilac at low temperature to colorless at high temperature. The lilac color of the complex represent the diamagnetic low spin state while the colorless correspond to the paramagnetic high spin state of iron(II). The transition between the two states could be tuned by changing the anionic group. Generally, the complex was synthesized directly from aqueous solution of iron(II) salt with considerable amounts of NH{sub 2}-trz solution produced solid powder compound. For application as an electronic molecularmore » device, the complex should be obtained as a thin film. The transparent [Fe(NH{sub 2}trz){sub 3}]-Nafion film has been successfully obtained, however, no anion variation can be produced since the nafion is an anionic resin. In this work, the [Fe(NH{sub 2}trz){sub 3}]-complexes with several anions have been synthesized inside nata de coco membrane that commonly used as a medium for deposition metal nano-particles. After drying the membrane containing the complex became a thin film. At room temperature, the film containing iron(II) complexes of sulphate and nitrate salts show lilac color, similar to that of the original complexes in the powder form. On heating, the color of the complex film changed to colorless and this color change was observed reversibly. In contrast, the films containing perchlorate and tetrafluoroborate iron(II) complexes are colorless at room temperature and changed to lilac on cooling. The significant color changing of the iron(II)complexes in the nata de coco film can be used for demonstration thermo chromic effect of smart materials with relatively small amount of the compounds.« less

Magnetic hysteresis measurements of thin films under isotropic stress.

NASA Astrophysics Data System (ADS)

Holland, Patrick; Dubey, Archana; Geerts, Wilhelmus

2000-10-01

Nowadays, ferromagnetic thin films are widely applied in devices for information technology (credit cards, video recorder tapes, floppies, hard disks) and sensors (air bags, anti-breaking systems, navigation systems). Thus, with the increase in the use of magnetic media continued investigation of magnetic properties of materials is necessary to help in determining the useful properties of materials for new or improved applications. We are currently interested in studying the effect of applied external stress on Kerr hysteresis curves of thin magnetic films. The Ni and NiFe films were grown using DC magnetron sputtering with Ar as the sputter gas (pAr=4 mTorr; Tsub=55-190 C). Seed and cap layers of Ti were used on all films for adhesion and oxidation protection, respectively. A brass membrane pressure cell was designed to apply in-plane isotropic stress to thin films. In this pressure cell, gas pressure is used to deform a flexible substrate onto which a thin magnetic film has been sputtered. The curvature of the samples could be controlled by changing the gas pressure to the cell. Magneto-Optical in-plane hysteresis curves at different values of strain were measured. The results obtained show that the stress sensitivity is dependent on the film thickness. For the 500nm NiFe films, the coercivity strongly decreased as a function of the applied stress.

Improvement of corrosion resistance of NiTi sputtered thin films by anodization

NASA Astrophysics Data System (ADS)

Bayat, N.; Sanjabi, S.; Barber, Z. H.

2011-08-01

Anodization of sputtered NiTi thin films has been studied in 1 M acetic acid at 23 °C for different voltages from 2 to 10 V. The morphology and cross-sectional structures of the untreated and anodized surfaces were investigated by field emission scanning electron microscopy (FE-SEM). The results show that increasing anodization voltage leads to film surface roughening and unevenness. It can be seen that the thickness of the anodized layer formed on the NiTi surface is in the nanometer range. The corrosion resistance of anodized thin films was studied by potentiodynamic scan (PDS) and impedance spectroscopy (EIS) techniques in Hank's solution at 310 K (37 °C). It was shown that the corrosion resistance of the anodized film surface improved with increasing voltage to 6 V. Anodization of austenitic sputtered NiTi thin films has also been studied, in the same anodizing conditions, at 4 V. Comparison of anodized sputtered NiTi thin films with anodized austenitic shape memory films illustrate that the former are more corrosion resistant than the latter after 1 h immersion in Hank's solution, which is attributed to the higher grain boundary density to quickly form a stable and protective passive film.

Pyrolyzed thin film carbon

NASA Technical Reports Server (NTRS)

Harder, Theodore (Inventor); Konishi, Satoshi (Inventor); Miserendino, Scott (Inventor); Tai, Yu-Chong (Inventor); Liger, Matthieu (Inventor)

2010-01-01

A method of making carbon thin films comprises depositing a catalyst on a substrate, depositing a hydrocarbon in contact with the catalyst and pyrolyzing the hydrocarbon. A method of controlling a carbon thin film density comprises etching a cavity into a substrate, depositing a hydrocarbon into the cavity, and pyrolyzing the hydrocarbon while in the cavity to form a carbon thin film. Controlling a carbon thin film density is achieved by changing the volume of the cavity. Methods of making carbon containing patterned structures are also provided. Carbon thin films and carbon containing patterned structures can be used in NEMS, MEMS, liquid chromatography, and sensor devices.

Enhanced dielectric and electrical properties of annealed PVDF thin film

NASA Astrophysics Data System (ADS)

Arshad, A. N.; Rozana, M. D.; Wahid, M. H. M.; Mahmood, M. K. A.; Sarip, M. N.; Habibah, Z.; Rusop, M.

2018-05-01

Poly (vinylideneflouride) (PVDF) thin films were annealed at various annealing temperatures ranging from 70°C to 170°C. This study demonstrates that PVDF thin films annealed at temperature of 70°C (AN70) showed significant enhancement in their dielectric constant (14) at frequency of 1 kHz in comparison to un-annealed PVDF (UN-PVDF), dielectric constant (10) at the same measured frequency. As the annealing temperature was increased from 90°C (AN90) to 150°C (AN150), the dielectric constant value of PVDF thin films was observed to decrease gradually to 11. AN70 also revealed low tangent loss (tan δ) value at similar frequency. With respect to its resistivity properties, the values were found to increase from 1.98×104 Ω.cm to 3.24×104 Ω.cm for AN70 and UN-PVDF films respectively. The improved in dielectric constant, with low tangent loss and high resistivity value suggests that 70°C is the favorable annealing temperature for PVDF thin films. Hence, AN70 is a promising film to be utilized for application in electronic devices such as low frequency capacitor.

In situ Pulsed Laser Deposition of C-Axis Oriented MgB2 Films and Their Characterization

NASA Technical Reports Server (NTRS)

Shinde, Sanjay; Lakew, Brook; Ogale, S. B.; Kulkarni, V. N.; Kale, S. N.; Venkatesan, T.

2004-01-01

The recent discovery of an intermetallic superconductor MgB2 has renewed interest in the area of superconductivity not only because of fundamental understanding of superconductivity but also due to its potential applicability in devices such as thermal detectors. Considerable amount of research has been devoted to obtain MgB2 films by an all in situ growth technique. We have grown MgB2 thin films by an all in situ pulsed laser deposition process from pure B and Mg targets. Ultrathin layers of B and Mg were deposited in a multilayer configuration. Hundreds of such Mg-B bilayers with a capping Mg layer on the top were deposited on sapphire substrate. These depositions were done in high vacuum (approx. 10(exp -7) Torr) and at room temperature. After deposition, such a configuration was annealed at high temperature for a short time in a forming gas (4% H2 in Ar). The best films, obtained by this procedure, showed superconducting transition temperature approx. 30 K. These films have been characterized by x-ray diffraction, Rutherford Backscattering Spectrometry, AC susceptibility-, resistivity- (with and without magnetic field) and 1/f noise-measurements. The physical properties of these films will be presented and discussed.

Determination of diffusion coefficients in polypyrrole thin films using a current pulse relaxation method

NASA Technical Reports Server (NTRS)

Penner, Reginald M.; Vandyke, Leon S.; Martin, Charles R.

1987-01-01

The current pulse E sub oc relaxation method and its application to the determination of diffusion coefficients in electrochemically synthesized polypyrrole thin films is described. Diffusion coefficients for such films in Et4NBF4 and MeCN are determined for a series of submicron film thicknesses. Measurement of the double-layer capacitance, C sub dl, and the resistance, R sub u, of polypyrrole thin films as a function of potential obtained with the galvanostatic pulse method is reported. Measurements of the electrolyte concentration in reduced polypyrrole films are also presented to aid in the interpretation of the data.

Tuning the Curie temperature of epitaxial Nd0.6Sr0.4MnO3 thin films

NASA Astrophysics Data System (ADS)

Bhat, Shwetha G.; Kumar, P. S. Anil

2018-02-01

NdxSr1-xMnO3 (0.2 ≤ x ≤ 0.5) systems are widely studied in magnetism, popular for high colossal magnetoresistance and are ferromagnetic oxides with TC ranging from 200 K to 300 K. Recently, many of such compounds are re-visited for exploring the correlation of spin, charge and lattice degrees of freedom. Although, manganite thin films are the ideal candidates for studying the electron-correlation effects, the puzzle of obtaining a high quality epitaxial thin films of NdxSr1-xMnO3 are still unsolved contrary to its sister compound LaxSr1-xMnO3. Hence, in this study, we demonstrate the growth of best quality of Nd0.6Sr0.4MnO3 (NSMO) epitaxial thin films. This is evident from the TC and a sharp insulator-to-metal transition (IMT) coinciding at as high as ∼255 K against the bulk TC (∼270 K). It is the highest reported TC in Nd0.6Sr0.4MnO3 thin films to date. Moreover, as-deposited films with in situ oxygen annealing are not enough to relax the lattice of NSMO films due to the significant Jahn-Teller distortion in the film. With ex situ annealing processes alongside the various deposition and in situ annealing conditions, we have extensively studied the growth of epitaxial NSMO thin films on LaAlO3 (0 0 1) and SrTiO3 (0 0 1) to investigate the evolution of lattice and its one-to-one correspondence with the magnetism and the electrical properties of thin films. Accordingly, the enhanced magnetization, reduced resistivity and the higher TC and IMT of the NSMO films obtained from our extensive growth analysis looks promising for the future applications across the TC and IMT.

Purely hopping conduction in c-axis oriented LiNbO3 thin films

NASA Astrophysics Data System (ADS)

Shandilya, Swati; Tomar, Monika; Sreenivas, K.; Gupta, Vinay

2009-05-01

Dielectric constant and ac conductivity of highly c-axis oriented LiNbO3 thin film grown by pulsed laser deposition were studied in a metal-insulator-metal configuration over a wide temperature (200 to 450 K) and frequency (100 Hz to 1 MHz) range. The preferred oriented Al (1%) doped ZnO film with electrical conductivity 1.1×103 Ω-1 cm-1 was deposited for dual purpose: (1) to serve as nucleating center for LiNbO3 crystallites along preferred c-axis growth direction, and (2) to act as a suitable bottom electrode for electrical studies. The room temperature dc conductivity (σdc) of LiNbO3 film was about 5.34×10-10 Ω-1 cm-1 with activation energy ˜0.3 eV, indicating extrinsic conduction. The ac conductivity σac was found to be much higher in comparison to σdc in the low temperature region (<300 K) and exhibits a power law behavior due to the hopping of charge carriers. In higher temperature region (>300 K), σac shows a weak frequency dependence, whereas dielectric constant exhibits a strong frequency dispersion. The dielectric dispersion data has been discussed in the light of theoretical models based on Debye type mixed conduction and purely hopping conduction. The dominant conduction in c-axis oriented LiNbO3 thin film is attributed to the purely hopping where both σdc and σac arise due to same mechanism.

Lateral assembly of oxidized graphene flakes into large-scale transparent conductive thin films with a three-dimensional surfactant 4-sulfocalix[4]arene

PubMed Central

Sundramoorthy, Ashok K.; Wang, Yilei; Wang, Jing; Che, Jianfei; Thong, Ya Xuan; Lu, Albert Chee W.; Chan-Park, Mary B.

2015-01-01

Graphene is a promising candidate material for transparent conductive films because of its excellent conductivity and one-carbon-atom thickness. Graphene oxide flakes prepared by Hummers method are typically several microns in size and must be pieced together in order to create macroscopic films. We report a macro-scale thin film fabrication method which employs a three-dimensional (3-D) surfactant, 4-sulfocalix[4]arene (SCX), as a lateral aggregating agent. After electrochemical exfoliation, the partially oxidized graphene (oGr) flakes are dispersed with SCX. The SCX forms micelles, which adsorb on the oGr flakes to enhance their dispersion, also promote aggregation into large-scale thin films under vacuum filtration. A thin oGr/SCX film can be shaved off from the aggregated oGr/SCX cake by immersing the cake in water. The oGr/SCX thin-film floating on the water can be subsequently lifted from the water surface with a substrate. The reduced oGr (red-oGr) films can be as thin as 10−20 nm with a transparency of >90% and sheet resistance of 890 ± 47 kΩ/sq. This method of electrochemical exfoliation followed by SCX-assisted suspension and hydrazine reduction, avoids using large amounts of strong acid (unlike Hummers method), is relatively simple and can easily form a large scale conductive and transparent film from oGr/SCX suspension. PMID:26040436

Enhancement of electrical properties in polycrystalline BiFeO3 thin films

NASA Astrophysics Data System (ADS)

Yun, Kwi Young; Ricinschi, Dan; Kanashima, Takeshi; Okuyama, Masanori

2006-11-01

Ferroelectric BiFeO3 thin films were grown on Pt /TiO2/SiO2/Si substrates by pulsed-laser deposition. From the x-ray diffraction analysis, the BiFeO3 thin films consist of perovskite single phase, and the crystal structure shows the tetragonal structure with a space group P4mm. The BiFeO3 thin films show enhanced electrical properties with low leakage current density value of ˜10-4A /cm2 at a maximum applied voltage of 31V. This enhanced electrical resistivity allowed the authors to obtain giant ferroelectric polarization values such as saturation polarizations of 110 and 166μC/cm2 at room temperature and 80K, respectively.

Cr doping induced negative transverse magnetoresistance in C d3A s2 thin films

NASA Astrophysics Data System (ADS)

Liu, Yanwen; Tiwari, Rajarshi; Narayan, Awadhesh; Jin, Zhao; Yuan, Xiang; Zhang, Cheng; Chen, Feng; Li, Liang; Xia, Zhengcai; Sanvito, Stefano; Zhou, Peng; Xiu, Faxian

2018-02-01

The magnetoresistance of a material conveys various dynamic information about charge and spin carriers, inspiring both fundamental studies in physics and practical applications such as magnetic sensors, data storage, and spintronic devices. Magnetic impurities play a crucial role in the magnetoresistance as they induce exotic states of matter such as the quantum anomalous Hall effect in topological insulators and tunable ferromagnetic phases in dilute magnetic semiconductors. However, magnetically doped topological Dirac semimetals are hitherto lacking. Here, we report a systematic study of Cr-doped C d3A s2 thin films grown by molecular-beam epitaxy. With the Cr doping, C d3A s2 thin films exhibit unexpected negative transverse magnetoresistance and strong quantum oscillations, bearing a trivial Berry's phase and an enhanced effective mass. More importantly, with ionic gating the magnetoresistance of Cr-doped C d3A s2 thin films can be drastically tuned from negative to positive, demonstrating the strong correlation between electrons and the localized spins of the Cr impurities, which we interpret through the formation of magnetic polarons. Such a negative magnetoresistance under perpendicular magnetic field and its gate tunability have not been observed previously in the Dirac semimetal C d3A s2 . The Cr-induced topological phase transition and the formation of magnetic polarons in C d3A s2 provide insights into the magnetic interaction in Dirac semimetals as well as their potential applications in spintronics.

Broadly tunable thin-film intereference coatings: active thin films for telecom applications

NASA Astrophysics Data System (ADS)

Domash, Lawrence H.; Ma, Eugene Y.; Lourie, Mark T.; Sharfin, Wayne F.; Wagner, Matthias

2003-06-01

Thin film interference coatings (TFIC) are the most widely used optical technology for telecom filtering, but until recently no tunable versions have been known except for mechanically rotated filters. We describe a new approach to broadly tunable TFIC components based on the thermo-optic properties of semiconductor thin films with large thermo-optic coefficients 3.6X10[-4]/K. The technology is based on amorphous silicon thin films deposited by plasma-enhanced chemical vapor deposition (PECVD), a process adapted for telecom applications from its origins in the flat-panel display and solar cell industries. Unlike MEMS devices, tunable TFIC can be designed as sophisticated multi-cavity, multi-layer optical designs. Applications include flat-top passband filters for add-drop multiplexing, tunable dispersion compensators, tunable gain equalizers and variable optical attenuators. Extremely compact tunable devices may be integrated into modules such as optical channel monitors, tunable lasers, gain-equalized amplifiers, and tunable detectors.

Temperature dependent fabrication of cost-effective and nontoxic Cu{sub 2}ZnSnS{sub 4} (CZTS) thin films for solar cell

DOE Office of Scientific and Technical Information (OSTI.GOV)

Digraskar, Renuka, E-mail: renukad120@gmail.com; Sathe, Bhaskar, E-mail: bhaskarsathe@gmail.com; Gattu, Ketan

2016-05-06

In the present work, Cu{sub 2}ZnSnS{sub 4} (CZTS) thin films have been fabricated onto the glass substrate by simple and economic chemical bath deposition technique{sup 1}, and the effect of deposition temperature is reported. The deposition temperatures used were 50°C and 60°C for a deposition time of 60 min, which are significantly lower than earlier reports. These CZTS thin films were characterized for optical, electrical, morphological and elemental properties using, UV-Vis spectrophotometer, I-V system for photosensitivity, two probe resistivity system for resistivity, scanning electron microscopy, energy dispersive spectroscopy and Raman spectroscopy.

Influence of gold species (AuCl4(-) and AuCl2(-)) on self-assembly of PS-b-P2VP in solutions and morphology of composite thin films fabricated at the air/liquid interfaces.

PubMed

Zhao, Xingjuan; Wang, Qian; Zhang, Xiaokai; Lee, Yong-Ill; Liu, Hong-Guo

2016-01-21

Composite thin films doped with Au species were fabricated at an air/liquid interface via a series of steps, including the mass transfer of polystyrene-b-poly(2-vinylpyridine) (PS-b-P2VP) across the liquid/liquid interface between a DMF/CHCl3 solution and an aqueous solution containing either AuCl4(-) or AuCl2(-), self-assembly of PS-b-P2VP in a mixed DMF-water solution, and adsorption and further self-organization of the formed aggregates at the air/liquid interface. This is a new approach for fabricating composite polymer films and can be completed within a very short time. AuCl4(-) and AuCl2(-) ions were found to significantly influence the self-assembly behavior of the block copolymer and the morphologies of the composite films, leading to the formation of nanowire arrays and a foam structure at the air/liquid interface, respectively, which originated from rod-like micelles and microcapsules that had formed in the respective solutions. The effect of the metal complex was analyzed based on the packing parameters of the amphiphilic polymer molecules in different microenvironments and the interactions between the pyridine groups and the metal chloride anions. In addition, these composite thin films exhibited stable and durable performance as heterogeneous catalysts for the hydrogenation of nitroaromatics in aqueous solutions.

Ferro- and piezoelectric properties of polar-axis-oriented CaBi4Ti4O15 films

NASA Astrophysics Data System (ADS)

Kato, Kazumi; Fu, Desheng; Suzuki, Kazuyuki; Tanaka, Kiyotaka; Nishizawa, Kaori; Miki, Takeshi

2004-05-01

Polar-axis-oriented CaBi4Ti4O15 (CBTi144) films were fabricated on Pt foils using a complex metal alkoxide solution. The 500-nm-thick film showed the columnar structure and consisted of well-developed grains. The a/b-axis orientation of the ferroelectric films is considered to be associated with the preferred orientation of Pt foil. The film showed good ferro- and piezoelectric properties. The Pr and Ec were 25 μC/cm2 and 306 kV/cm, respectively, at an applied voltage of 115 V. The d33 was characterized as 30 pm/V by piezoresponse force microscopy. The values were twice as large as those of the CBTi144 thin film with random orientation. The polar-axis-oriented CBTi144 films would open up possibilities for devices as Pb-free piezoelectric materials.

Nanometre-scale 3D defects in Cr2AlC thin films.

PubMed

Chen, Y T; Music, D; Shang, L; Mayer, J; Schneider, J M

2017-04-20

MAX-phase Cr 2 AlC containing thin films were synthesized by magnetron sputtering in an industrial system. Nanometre-scale 3D defects are observed near the boundary between regions of Cr 2 AlC and of the disordered solid solution (CrAl) x C y . Shrinkage of the Cr-Cr interplanar distance and elongation of the Cr-Al distance in the vicinity of the defects are detected using transmission electron microscopy. The here observed deformation surrounding the defects was described using density functional theory by comparing the DOS of bulk Cr 2 AlC with the DOS of a strained and unstrained Cr 2 AlC(0001) surface. From the partial density of states analysis, it can be learned that Cr-C bonds are stronger than Cr-Al bonds in bulk Cr 2 AlC. Upon Cr 2 AlC(0001) surface formation, both bonds are weakened. While the Cr-C bonds recover their bulk strength as Cr 2 AlC(0001) is strained, the Cr-Al bonds experience only a partial recovery, still being weaker than their bulk counterparts. Hence, the strain induced bond strengthening in Cr 2 AlC(0001) is larger for Cr d - C p bonds than for Cr d - Al p bonds. The here observed changes in bonding due to the formation of a strained surface are consistent with the experimentally observed elongation of the Cr-Al distance in the vicinity of nm-scale 3D defects in Cr 2 AlC thin films.

Hybrid thin-film amplifier

NASA Technical Reports Server (NTRS)

Cleveland, G.

1977-01-01

Miniature amplifier for bioelectronic instrumentation consumes only about 100 mW and has frequency response flat to within 0.5 dB from 0.14 to 450 Hz. Device consists of five thin film substrates, which contain eight operational amplifiers and seven field-effect transistor dice.

Magneto-Optical Thin Films for On-Chip Monolithic Integration of Non-Reciprocal Photonic Devices

PubMed Central

Bi, Lei; Hu, Juejun; Jiang, Peng; Kim, Hyun Suk; Kim, Dong Hun; Onbasli, Mehmet Cengiz; Dionne, Gerald F.; Ross, Caroline A.

2013-01-01

Achieving monolithic integration of nonreciprocal photonic devices on semiconductor substrates has been long sought by the photonics research society. One way to achieve this goal is to deposit high quality magneto-optical oxide thin films on a semiconductor substrate. In this paper, we review our recent research activity on magneto-optical oxide thin films toward the goal of monolithic integration of nonreciprocal photonic devices on silicon. We demonstrate high Faraday rotation at telecommunication wavelengths in several novel magnetooptical oxide thin films including Co substituted CeO2−δ, Co- or Fe-substituted SrTiO3−δ, as well as polycrystalline garnets on silicon. Figures of merit of 3~4 deg/dB and 21 deg/dB are achieved in epitaxial Sr(Ti0.2Ga0.4Fe0.4)O3−δ and polycrystalline (CeY2)Fe5O12 films, respectively. We also demonstrate an optical isolator on silicon, based on a racetrack resonator using polycrystalline (CeY2)Fe5O12/silicon strip-loaded waveguides. Our work demonstrates that physical vapor deposited magneto-optical oxide thin films on silicon can achieve high Faraday rotation, low optical loss and high magneto-optical figure of merit, therefore enabling novel high-performance non-reciprocal photonic devices monolithically integrated on semiconductor substrates. PMID:28788379

Evolution of magnetic properties in the vicinity of the Verwey transition in Fe3O4 thin films

NASA Astrophysics Data System (ADS)

Liu, X. H.; Liu, W.; Zhang, Z. D.

2017-09-01

We have systematically studied the evolution of magnetic properties, especially the coercivity and the remanence ratio in the vicinity of the Verwey transition temperature (TV), of high-quality epitaxial Fe3O4 thin films grown on MgO (001), MgAl2O4 (MAO) (001), and SrTiO3 (STO) (001) substrates. We observed rapid change of magnetization, coercivity, and remanence ratio at TV, which are consistent with the behaviors of resistivity versus temperature [ρ (T )] curves for the different thin films. In particular, we found quite different magnetic behaviors for the thin films on MgO from those on MAO and STO, in which the domain size and the strain state play very important roles. The coercivity is mainly determined by the domain size but the demagnetization process is mainly dependent on the strain state. Furthermore, we observed a reversal of remanence ratio at TV with thickness for the thin films grown on MgO: from a rapid enhancement for 40-nm- to a sharp drop for 200-nm-thick film, and the critical thickness is about 80 nm. Finally, we found an obvious hysteretic loop of coercivity (or remanence ratio) with temperature around TV, corresponding to the hysteretic loop of the ρ (T ) curve, in Fe3O4 thin film grown on MgO.

Consequence of oxidant concentration on XPS properties of chemically synthesized polythiophene thin films

NASA Astrophysics Data System (ADS)

Kamat, Sandip V.; Chhabra, Jasvinder; Patil, V. S.; Yadav, J. B.; Puri, R. K.; Puri, Vijaya

2018-05-01

The polythiophene thin films were prepared by a wellknown chemical bath deposition technique. The deposited thin films were characterized for structural morphological properties and the adhesion of these thin films were measured by direct pull off (DPO) method, the effect of oxidant concentration on these thin films also studied. The FTIR spectra of chemically deposited polythiophene thin films shows the absorption peak at 836 cm-1 which represents c-s stretching vibrations, shifts to 869 cm-1 as the oxidant concentration increases. The band at 666 cm-1 representing c-s-c ring deformation becomes sharper and appears with a shoulder peak due to increase in oxidant concentration.

Microstructure and dielectric properties of pyrochlore Bi2Ti2O7 thin films

NASA Astrophysics Data System (ADS)

Cagnon, Joël; Boesch, Damien S.; Finstrom, Nicholas H.; Nergiz, Saide Z.; Keane, Sean P.; Stemmer, Susanne

2007-08-01

Bi2Ti2O7 thin films were grown by radio-frequency magnetron sputtering on bare and Pt-coated sapphire substrates at low substrate temperatures (˜200 °C). Postdeposition anneals were carried out at different temperatures to crystallize the films. Nearly phase-pure Bi2Ti2O7 thin films with the cubic pyrochlore structure were obtained at annealing temperatures up to 800 °C. Impurity phases, in particular Bi4Ti3O12, formed at higher temperatures. At 1 MHz, the dielectric constants were about 140-150 with a very small tunability and the dielectric loss was about 4×10-3. The dielectric loss increased with frequency. The dielectric properties of Bi2Ti2O7 films are compared to those of pyrochlore bismuth zinc niobate films.

Solution-processed flexible fluorine-doped indium zinc oxide thin-film transistors fabricated on plastic film at low temperature.

PubMed

Seo, Jin-Suk; Jeon, Jun-Hyuck; Hwang, Young Hwan; Park, Hyungjin; Ryu, Minki; Park, Sang-Hee Ko; Bae, Byeong-Soo

2013-01-01

Transparent flexible fluorine-doped indium zinc oxide (IZO:F) thin-film transistors (TFTs) were demonstrated using the spin-coating method of the metal fluoride precursor aqueous solution with annealing at 200°C for 2 hrs on polyethylene naphthalate films. The proposed thermal evolution mechanism of metal fluoride aqueous precursor solution examined by thermogravimetric analysis and Raman spectroscopy can easily explain oxide formation. The chemical composition analysed by XPS confirms that the fluorine was doped in the thin films annealed below 250°C. In the IZO:F thin films, a doped fluorine atom substitutes for an oxygen atom generating a free electron or occupies an oxygen vacancy site eliminating an electron trap site. These dual roles of the doped fluorine can enhance the mobility and improve the gate bias stability of the TFTs. Therefore, the transparent flexible IZO:F TFT shows a high mobility of up to 4.1 cm(2)/V·s and stable characteristics under the various gate bias and temperature stresses.

Flexible magnetic thin films and devices

NASA Astrophysics Data System (ADS)

Sheng, Ping; Wang, Baomin; Li, Runwei

2018-01-01

Flexible electronic devices are highly attractive for a variety of applications such as flexible circuit boards, solar cells, paper-like displays, and sensitive skin, due to their stretchable, biocompatible, light-weight, portable, and low cost properties. Due to magnetic devices being important parts of electronic devices, it is essential to study the magnetic properties of magnetic thin films and devices fabricated on flexible substrates. In this review, we mainly introduce the recent progress in flexible magnetic thin films and devices, including the study on the stress-dependent magnetic properties of magnetic thin films and devices, and controlling the properties of flexible magnetic films by stress-related multi-fields, and the design and fabrication of flexible magnetic devices. Project supported by the National Key R&D Program of China (No. 2016YFA0201102), the National Natural Science Foundation of China (Nos. 51571208, 51301191, 51525103, 11274321, 11474295, 51401230), the Youth Innovation Promotion Association of the Chinese Academy of Sciences (No. 2016270), the Key Research Program of the Chinese Academy of Sciences (No. KJZD-EW-M05), the Ningbo Major Project for Science and Technology (No. 2014B11011), the Ningbo Science and Technology Innovation Team (No. 2015B11001), and the Ningbo Natural Science Foundation (No. 2015A610110).

Desertification of the peritoneum by thin-film evaporation during laparoscopy.

PubMed

Ott, Douglas E

2003-01-01

To assess the effects of gas flow during insufflation on peritoneal fluid and peritoneal tissue regarding transient thermal behavior and thin-film evaporation. The effects of laparoscopic gas on peritoneal cell desiccation and peritoneal fluid thin-film evaporation were analyzed. Measurment of tissue and peritoneal fluid and analysis of gas flow dynamics during laparoscopy. High-velocity gas interface conditions during laparoscopic gas insufflation result in peritoneal surface temperature and decreases up to 20 degrees C/second due to rapid thin-film evaporation of the peritoneal fluid. Evaporation of the thin film of peritoneal fluid extends quickly to the peritoneal cell membrane, causing peritoneal cell desiccation, internal cytoplasmic stress, and disruption of the cell membrane, resulting in loss of peritoneal surface continuity and integrity. Changing the gas conditions to 35 degrees C and 95% humidity maintains normal peritoneal fluid thin-film characteristics, cellular integrity, and prevents evaporative losses. Cold, dry gas and the characteristics of the laparoscopic gas delivery apparatus cause local peritoneal damaging alterations by high-velocity gas flow with extremely dry gas, creating extreme arid surface conditions, rapid evaporative and hydrological changes, tissue desiccation, and peritoneal fluid alterations that contribute to the process of desertification and thin-film evaporation. Peritoneal desertification is preventable by preconditioning the gas to 35 degrees C and 95% humidity.

Magnetoelectric coupling of multiferroic chromium doped barium titanate thin film probed by magneto-impedance spectroscopy

DOE Office of Scientific and Technical Information (OSTI.GOV)

Shah, Jyoti, E-mail: shah.jyoti1@gmail.com; Kotnala, Ravinder K., E-mail: rkkotnala@nplindia.org, E-mail: rkkotnala@gmail.com

2014-04-07

Thin film of BaTiO{sub 3} doped with 0.1 at. % Cr (Cr:BTO) has been prepared by pulsed laser deposition technique. Film was deposited on Pt/SrTiO{sub 3} substrate at 500 °C in 50 mTorr Oxygen gas pressure using KrF (298 nm) laser. Polycrystalline growth of single phase Cr:BTO thin film has been confirmed by grazing angle X-ray diffraction. Cr:BTO film exhibited remnant polarization 6.4 μC/cm{sup 2} and 0.79 MV/cm coercivity. Magnetization measurement of Cr:BTO film showed magnetic moment 12 emu/cc. Formation of weakly magnetic domains has been captured by magnetic force microscopy. Theoretical impedance equation fitted to experimental data in Cole-Cole plot for thin film inmore » presence of transverse magnetic field resolved the increase in grain capacitance from 4.58 × 10{sup −12} to 5.4 × 10{sup −11} F. Film exhibited high value 137 mV/cm-Oe magneto-electric (ME) coupling coefficient at room temperature. The high value of ME coupling obtained can reduce the typical processing steps involved in multilayer deposition to obtain multiferrocity in thin film. Barium titanate being best ferroelectric material has been tailored to be multiferroic by non ferromagnetic element, Cr, doping in thin film form opens an avenue for more stable and reliable spintronic material for low power magnetoelectric random excess memory applications.« less

Magnetic properties of epitaxial β-Nb2N thin film on SiC substrate

NASA Astrophysics Data System (ADS)

Yang, Zihao; Myers, Roberto; Katzer, D. Scott; Nepal, Neeraj; Meyer, David J.

Previously superconductivity in Nb2N was studied in thin films synthesized by reactive magnetron sputtering or pulsed laser deposition. Recently, Nb2N was synthesized by molecular beam epitaxy (MBE). Here, we report on the magnetic properties of MBE grown Nb2N measured by SQUID magnetometry. The single hexagonal β phase Nb2N is grown on a semi-insulating Si-face 4H SiC (0001) substrate in nitrogen rich conditions at a substrate temperature of 850 °C. In-plane magnetization as a function of magnetic field measured at 5 K shows type-II superconductivity with critical fields Hc1 and Hc2 of 300 Oe and 10 kOe, respectively. In-plane field-cooled and zero-field-cooled a critical temperature (Tc) of 11.5 K, higher than in sputtered Nb2N films. This work was supported by Army Research Office and the Office of Naval Research.

Electrolyte and Electrode Passivation for Thin Film Batteries

NASA Technical Reports Server (NTRS)

West, W.; Whitacre, J.; Ratnakumar, B.; Brandon, E.; Blosiu, J.; Surampudi, S.

2000-01-01

Passivation films for thin film batteries have been prepared and the conductivity and voltage stability window have been measured. Thin films of Li2CO3 have a large voltage stability window of 4.8V, which facilitates the use of this film as a passivation at both the lithium anode-electrolyte interface at high cathodic potentials.

Effect of different thickness crystalline SiC buffer layers on the ordering of MgB{sub 2} films probed by extended x-ray absorption fine structure

DOE Office of Scientific and Technical Information (OSTI.GOV)

Putri, W. B. K.; Tran, D. H.; Kang, B., E-mail: bwkang@chungbuk.ac.kr

2014-03-07

Extended X-ray absorption fine structure (EXAFS) spectroscopy is a powerful method to investigate the local structure of thin films. Here, we have studied EXAFS of MgB{sub 2} films grown on SiC buffer layers. Crystalline SiC buffer layers with different thickness of 70, 100, and 130 nm were deposited on the Al{sub 2}O{sub 3} (0001) substrates by using a pulsed laser deposition method, and then MgB{sub 2} films were grown on the SiC buffer layer by using a hybrid physical-chemical vapor deposition technique. Transition temperature of MgB{sub 2} film decreased with increasing thickness of SiC buffer layer. However, the T{sub c} droppingmore » went no farther than 100 nm-thick-SiC. This uncommon behavior of transition temperature is likely to be created from electron-phonon interaction in MgB{sub 2} films, which is believed to be related to the ordering of MgB{sub 2} atomic bonds, especially in the ordering of Mg–Mg bonds. Analysis from Mg K-edge EXAFS measurements showed interesting ordering behavior of MgB{sub 2} films. It is noticeable that the ordering of Mg–B bonds is found to decrease monotonically with the increase in SiC thickness of the MgB{sub 2} films, while the opposite happens with the ordering in Mg–Mg bonds. Based on these results, crystalline SiC buffer layers in MgB{sub 2} films seemingly have evident effects on the alteration of the local structure of the MgB{sub 2} film.« less

Facile fabrication of an efficient BiVO4 thin film electrode for water splitting under visible light irradiation.

PubMed

Jia, Qingxin; Iwashina, Katsuya; Kudo, Akihiko

2012-07-17

An efficient BiVO(4) thin film electrode for overall water splitting was prepared by dipping an F-doped SnO(2) (FTO) substrate electrode in an aqueous nitric acid solution of Bi(NO(3))(3) and NH(4)VO(3), and subsequently calcining it. X-ray diffraction of the BiVO(4) thin film revealed that a photocatalytically active phase of scheelite-monoclinic BiVO(4) was obtained. Scanning electron microscopy images showed that the surface of an FTO substrate was uniformly coated with the BiVO(4) film with 300-400 nm of the thickness. The BiVO(4) thin film electrode gave an excellent anodic photocurrent with 73% of an IPCE at 420 nm at 1.0 V vs. Ag/AgCl. Modification with CoO on the BiVO(4) electrode improved the photoelectrochemical property. A photoelectrochemical cell consisting of the BiVO(4) thin film electrode with and without CoO, and a Pt counter electrode was constructed for water splitting under visible light irradiation and simulated sunlight irradiation. Photocurrent due to water splitting to form H(2) and O(2) was confirmed with applying an external bias smaller than 1.23 V that is a theoretical voltage for electrolysis of water. Water splitting without applying external bias under visible light irradiation was demonstrated using a SrTiO(3)Rh photocathode and the BiVO(4) photoanode.

Photoelectrochemical performance of W-doped BiVO4 thin-films deposited by spray pyrolysis

NASA Astrophysics Data System (ADS)

Holland, Stephen K.; Dutter, Melissa R.; Lawrence, David J.; Reisner, Barbara A.; DeVore, Thomas C.

2013-09-01

The effect of tungsten doping and hydrogen annealing treatments on the photoelectrochemical (PEC) performance of bismuth vanadate (BiVO4) photoanodes for solar water splitting was studied. Thin films of BiVO4 were deposited on ITO-coated glass slides by ultrasonic spray pyrolysis of an aqueous solution containing bismuth nitrate and vanadium oxysulfate. Tungsten doping was achieved by adding either silicotungstic acid (STA) or ammonium metatungstate (AMT) in the aqueous precursor. The 1.7 μm - 2.2 μm thick films exhibited a highly porous microstructure. Undoped films that were reduced at 375 ºC in 3% H2 exhibited the largest photocurrent densities under 0.1 W cm-2 AM1.5 illumination. This performance enhancement was believed to be due to the formation of oxygen vacancies, which are shallow electron donors, in the films. Films doped with 1% or 5% tungsten from either STA or AMT exhibited reduced photoelectrochemical performance and greater sample-to-sample performance variations. Powder X-ray diffraction data of the undoped films indicated that they were comprised primarily of the monoclinic scheelite phase while unidentified phases were also present. Scanning electron microscopy showed slightly different morphology characteristics for the Wdoped films. It is surmised that the addition of W in the deposition process promoted the morphology differences and the formation of different phases, thus reducing the PEC performance of the photoanode samples. Significant PEC performance variability was also observed among films deposited using the described process.

Conformal self-assembled thin films for optical pH sensors

NASA Astrophysics Data System (ADS)

Topasna, Daniela M.; Topasna, Gregory A.; Liu, Minghanbo; Tseng, Ching-Hung

2016-04-01

Simple, reliable, lightweight, and inexpensive thin films based sensors are still in intense development and high demand in many applications such as biomedical, industrial, environmental, military, and consumer products. One important class of sensors is the optical pH sensor. In addition, conformal thin film based sensors extend the range of application for pH optical sensors. We present the results on the fabrication and characterization of optical pH sensing coatings made through ionic self-assembled technique. These thin films are based on the combination of a polyelectrolyte and water-soluble organic dye molecule Direct Yellow 4. A series of films was fabricated and characterized in order to determine the optimized parameters of the polymer and of the organic dye solutions. The optical pH responses of these films were also studied. The transparent films were immersed in solutions at various temperature and pH values. The films are stable when immersed in solutions with pH below 9.0 and temperatures below 90 °C and they maintain their performance after longer immersion times. We also demonstrate the functionality of these coatings as conformal films.

Surface-emitting stimulated emission in high-quality ZnO thin films

NASA Astrophysics Data System (ADS)

Zhang, X. Q.; Suemune, Ikuo; Kumano, H.; Wang, J.; Huang, S. H.

2004-10-01

High-quality ZnO thin films were grown by plasma-enhanced molecular-beam epitaxy on sapphire substrates. Three excitonic transitions associated with the valence bands A, B, and C were clearly revealed in the reflectance spectrum measured at 33K. This result indicates that the ZnO thin films have the wurtzite crystalline structure. The emission spectra were measured with backscattering geometry at room temperature. When the excitation exceeded a certain value, linewidth narrowing, nonlinear rise of emission intensity, and the shortening of the carrier lifetime were clearly observed and these demonstrate the onset of stimulated emission. Together with the ZnO thickness dependence, we conclude that the observation of a stimulated emission in a direction perpendicular to the film surface is predominantly due to scattering of the in-plane stimulated emission by slightly remaining surface undulations in the ZnO films.

Center for Thin Film Studies

DTIC Science & Technology

1991-01-22

highly oriented pyrolitic graphite ( HOPG ) for detailed studies of nucleation and of the development of surface roughness. Using a shadowing technique, we...laser to a temperature of approximately 600’C, a polycrystalline film resulted, as indicated b x-ray diffraction ( XRD ) data shown in Fig. 4. vI Figure 4...stress level rose in films deposited at colder temperatures. Development of second harmonic generation as a technique for evaluation of anisotropy in

Effects of sulfurization on the optical properties of Cu2ZnxFe1-xSnS4 thin films

NASA Astrophysics Data System (ADS)

Hannachi, A.; Oueslati, H.; Khemiri, N.; Kanzari, M.

2017-10-01

In order to prepare thin films of novel semiconductor materials that contain only earth abundant, low cost and nontoxic elements, Cu2ZnxFe1-xSnS4 ingots were successfully synthesized by direct fusion method. Crushed powders of these ingots were used as raw materials for the thermal evaporation. Cu2ZnxFe1-xSnS4 (with x = 0, 0.25, 0.5, 0.75 and 1) thin films were deposited on non-heated glass substrates by vacuum evaporation method. The as deposited films were sulfurized for 30 min at sulfurization temperature Ts = 400 °C. The effects of the sulfurization on the structural and optical properties of CZFTS films were realized by X-ray diffraction (XRD) and UV-Vis spectroscopy. XRD patterns show that all sulfurized CZFTS films were polycrystalline in nature with a preferential orientation along the (112) plane. CFTS films exhibit a stannite structure while CZTS films had a kesterite structure. Optical measurements showed that CZFTS films sulfurized at 400 °C exhibited an optical transmittance between 60 and 80% and all materials had relatively high absorption coefficients in the range of 104-105 cm-1. The band gap energies of sulfurized CZFTS films decreased from 1.71 to 1.50 eV with the increase of the Zn content. The dispersion of the refractive index was discussed in terms of the single oscillator model proposed by Wemple and DiDomenico and the optical parameters such as refractive index, extinction coefficient, oscillator energy and dispersion energy were calculated. The electrical free carrier susceptibility and the carrier concentration on the effective mass ratio were evaluated according to the model of Spitzer and Fan. The hot probe analysis showed that all sulfurized CZFTS films are p-type conductivity.

Thin film superconductor magnetic bearings

DOEpatents

Weinberger, Bernard R.

1995-12-26

A superconductor magnetic bearing includes a shaft (10) that is subject to a load (L) and rotatable around an axis of rotation, a magnet (12) mounted to the shaft, and a stator (14) in proximity to the shaft. The stator (14) has a superconductor thin film assembly (16) positioned to interact with the magnet (12) to produce a levitation force on the shaft (10) that supports the load (L). The thin film assembly (16) includes at least two superconductor thin films (18) and at least one substrate (20). Each thin film (18) is positioned on a substrate (20) and all the thin films are positioned such that an applied magnetic field from the magnet (12) passes through all the thin films. A similar bearing in which the thin film assembly (16) is mounted on the shaft (10) and the magnet (12) is part of the stator (14) also can be constructed.

Thin-film Rechargeable Lithium Batteries

DOE R&D Accomplishments Database

Bates, J. B.; Gruzalski, G. R.; Dudney, N. J.; Luck, C. F.; Yu, X.

1993-11-01

Rechargeable thin films batteries with lithium metal anodes, an amorphous inorganic electrolyte, and cathodes of lithium intercalation compounds have been fabricated and characterized. The cathodes include TiS{sub 2}, the {omega} phase of V{sub 2}O{sub 5}, and the cubic spinel Li{sub x}Mn{sub 2}O{sub 4} with open circuit voltages at full charge of about 2.5 V, 3.7 V, and 4.2 V, respectively. The development of these robust cells, which can be cycled thousands of times, was possible because of the stability of the amorphous lithium electrolyte, lithium phosphorus oxynitride. This material has a typical composition of Li{sub 2.9}PO{sub 3.3}N{sub 0.46} and a conductivity at 25 C of 2 {mu}S/cm. Thin film cells have been cycled at 100% depth of discharge using current densities of 2 to 100 {mu}A/cm{sup 2}. The polarization resistance of the cells is due to the slow insertion rate of Li{sup +} ions into the cathode. Chemical diffusion coefficients for Li{sup +} ions in the three types of cathodes have been estimated from the analysis of ac impedance measurements.

The effect of solution pH on the electrochemical performance of nanocrystalline metal ferrites MFe2O4 (M=Cu, Zn, and Ni) thin films

NASA Astrophysics Data System (ADS)

Elsayed, E. M.; Rashad, M. M.; Khalil, H. F. Y.; Ibrahim, I. A.; Hussein, M. R.; El-Sabbah, M. M. B.

2016-04-01

Nanocrystalline metal ferrite MFe2O4 (M=Cu, Zn, and Ni) thin films have been synthesized via electrodeposition-anodization process. Electrodeposited (M)Fe2 alloys were obtained from aqueous sulfate bath. The formed alloys were electrochemically oxidized (anodized) in aqueous (1 M KOH) solution, at room temperature, to the corresponding hydroxides. The parameters controlling the current efficiency of the electrodeposition of (M)Fe2 alloys such as the bath composition and the current density were studied and optimized. The anodized (M)Fe2 alloy films were annealed in air at 400 °C for 2 h. The results revealed the formation of three ferrite thin films were formed. The crystallite sizes of the produced films were in the range between 45 and 60 nm. The microstructure of the formed film was ferrite type dependent. The corrosion behavior of ferrite thin films in different pH solutions was investigated using open circuit potential (OCP) and potentiodynamic polarization measurements. The open circuit potential indicates that the initial potential E im of ZnFe2O4 thin films remained constant for a short time, then sharply increased in the less negative direction in acidic and alkaline medium compared with Ni and Cu ferrite films. The values of the corrosion current density I corr were higher for the ZnFe2O4 films at pH values of 1 and 12 compared with that of NiFe2O4 and CuFe2O4 which were higher only at pH value 1. The corrosion rate was very low for the three ferrite films when immersion in the neutral medium. The surface morphology recommended that Ni and Cu ferrite films were safely used in neutral and alkaline medium, whereas Zn ferrite film was only used in neutral atmospheres.

Synthesis and characterization of MoB{sub 2−x} thin films grown by nonreactive DC magnetron sputtering

DOE Office of Scientific and Technical Information (OSTI.GOV)

Malinovskis, Paulius, E-mail: paulius.malinovskis@kemi.uu.se; Lewin, Erik; Jansson, Ulf

2016-05-15

DC magnetron sputtering was used to deposit molybdenum boride thin films for potential low-friction applications. The films exhibit a nanocomposite structure with ∼10 nm large MoB{sub 2−x} (x > 0.4) grains surrounded by a boron-rich tissue phase. The preferred formation of the metastable and substoichiometric hP3-MoB{sub 2} structure (AlB{sub 2}-type) is explained with kinetic constraints to form the thermodynamically stable hR18-MoB{sub 2} phase with a very complex crystal structure. Nanoindentation revealed a relatively high hardness of (29 ± 2) GPa, which is higher than bulk samples. The high hardness can be explained by a hardening effect associated with the nanocomposite microstructure where the surrounding tissuemore » phase restricts dislocation movement. A tribological study confirmed a significant formation of a tribofilm consisting of molybdenum oxide and boron oxide, however, without any lubricating effects at room temperature.« less

Effects of high temperature and film thicknesses on the texture evolution in Ag thin films

NASA Astrophysics Data System (ADS)

Eshaghi, F.; Zolanvari, A.

2017-04-01

In situ high-temperature X-ray diffraction techniques were used to study the effect of high temperatures (up to 600°C) on the texture evolution in silver thin films. Ag thin films with different thicknesses of 40, 80, 120 and 160nm were sputtered on the Si(100) substrates at room temperature. Then, microstructure of thin films was determined using X-ray diffraction. To investigate the influence of temperature on the texture development in the Ag thin films with different thicknesses, (111), (200) and (220) pole figures were evaluated and orientation distribution functions were calculated. Minimizing the total energy of the system which is affected by competition between surface and elastic strain energy was a key factor in the as-deposited and post annealed thin films. Since sputtering depositions was performed at room temperature and at the same thermodynamic conditions, the competition growth caused the formation of the {122} < uvw \\rangle weak fiber texture in as-deposited Ag thin films. It was significantly observed that the post annealed Ag thin films showed {111} < uvw \\rangle orientations as their preferred orientations, but their preferred fiber texture varied with the thickness of thin films. Increasing thin film thickness from 40nm to 160nm led to decreasing the intensity of the {111} < uvw \\rangle fiber texture.

[Spectral emissivity of thin films].

PubMed

Zhong, D

2001-02-01

In this paper, the contribution of multiple reflections in thin film to the spectral emissivity of thin films of low absorption is discussed. The expression of emissivity of thin films derived here is related to the thin film thickness d and the optical constants n(lambda) and k(lambda). It is shown that in the special case d-->infinity the emissivity of thin films is equivalent to that of the bulk material. Realistic numerical and more precise general numerical results for the dependence of the emissivity on d, n(lambda) and k(lambda) are given.

Ceramic Composite Thin Films

NASA Technical Reports Server (NTRS)

Dikin, Dmitriy A. (Inventor); Nguyen, SonBinh T. (Inventor); Ruoff, Rodney S. (Inventor); Stankovich, Sasha (Inventor)

2013-01-01

A ceramic composite thin film or layer includes individual graphene oxide and/or electrically conductive graphene sheets dispersed in a ceramic (e.g. silica) matrix. The thin film or layer can be electrically conductive film or layer depending the amount of graphene sheets present. The composite films or layers are transparent, chemically inert and compatible with both glass and hydrophilic SiOx/silicon substrates. The composite film or layer can be produced by making a suspension of graphene oxide sheet fragments, introducing a silica-precursor or silica to the suspension to form a sol, depositing the sol on a substrate as thin film or layer, at least partially reducing the graphene oxide sheets to conductive graphene sheets, and thermally consolidating the thin film or layer to form a silica matrix in which the graphene oxide and/or graphene sheets are dispersed.

Magneto-optical characterizations of FeTe₀̣₅Se₀̣₅ thin films with critical current density over 1 MA/cm²

DOE PAGES

Sun, Yue; Li, Qiang; Tsuchiya, Yuji; ...

2014-12-03

We performed magneto-optical (MO) measurements on FeTe₀̣₅Se₀̣₅ thin films grown on LaAlO₃ (LAO) and Yttria-stabilized zirconia (YSZ) single-crystalline substrates. These thin films show superconducting transition temperature T c ~19 K, 4 K higher than the bulk sample. Typical roof-top patterns can be observed in the MO images of thin films grown on LAO and YSZ, from which a large and homogeneous critical current density J c ~ 3 - 4 x 10⁶ A/cm² at 5 K was obtained. In this study, magnetic flux penetration measurement reveals that the current is almost isotropically distributed in the two thin films. Compared withmore » bulk crystals, FeTe₀̣₅Se₀̣₅ thin film demonstrates not only higher T c, but also much larger J c, which is attractive for applications.« less

Low Temperature Chemical Vapor Deposition Of Thin Film Magnets

DOEpatents

Miller, Joel S.; Pokhodnya, Kostyantyn I.

2003-12-09

A thin-film magnet formed from a gas-phase reaction of tetracyanoetheylene (TCNE) OR (TCNQ), 7,7,8,8-tetracyano-P-quinodimethane, and a vanadium-containing compound such as vanadium hexcarbonyl (V(CO).sub.6) and bis(benzene)vanalium (V(C.sub.6 H.sub.6).sub.2) and a process of forming a magnetic thin film upon at least one substrate by chemical vapor deposition (CVD) at a process temperature not exceeding approximately 90.degree. C. and in the absence of a solvent. The magnetic thin film is particularly suitable for being disposed upon rigid or flexible substrates at temperatures in the range of 40.degree. C. and 70.degree. C. The present invention exhibits air-stable characteristics and qualities and is particularly suitable for providing being disposed upon a wide variety of substrates.

The influence of sequence of precursor films on CZTSe thin films prepared by ion-beam sputtering deposition

NASA Astrophysics Data System (ADS)

Zhao, Jun; Liang, Guangxing; Zeng, Yang; Fan, Ping; Hu, Juguang; Luo, Jingting; Zhang, Dongping

2017-02-01

The CuZnSn (CZT) precursor thin films are grown by ion-beam sputtering Cu, Zn, Sn targets with different orders and then sputtering Se target to fabricate Cu2ZnSnSe4 (CZTSe) absorber thin films on molybdenum substrates. They are annealed in the same vacuum chamber at 400 °C. The characterization methods of CZTSe thin films include X-ray diffraction (XRD), energy dispersive spectroscopy (EDS), scanning electron microscopy (SEM), and X-ray photoelectron spectra (XPS) in order to study the crystallographic properties, composition, surface morphology, electrical properties and so on. The results display that the CZTSe thin films got the strongest diffraction peak intensity and were with good crystalline quality and its morphology appeared smooth and compact with a sequence of Cu/Zn/Sn/Se, which reveals that the expected states for CZTSe are Cu1+, Zn2+, Sn4+, Se2+. With the good crystalline quality and close to ideal stoichiometric ratio the resistivity of the CZTSe film with the sequence of Cu/Zn/Sn/Se is lower, whose optical band gap is about 1.50 eV. Project supported by the National Natural Science Foundation of China (No. 61404086), the Basical Research Program of Shenzhen (Nos. JCYJ20150324140036866, JCYJ20150324141711581), and the Natural Science Foundation of SZU (No. 2014017).

Oxygen Vacancy-Tuned Physical Properties in Perovskite Thin Films with Multiple B-site Valance States

DOE Office of Scientific and Technical Information (OSTI.GOV)

Enriquez, Erik; Chen, Aiping; Harrell, Zach

Controlling oxygen content in perovskite oxides with ABO 3 structure is one of most critical steps for tuning their functionality. Notably, there have been tremendous efforts to understand the effect of changes in oxygen content on the properties of perovskite thin films that are not composed of cations with multiple valance states. Here, we study the effect of oxygen vacancies on structural and electrical properties in epitaxial thin films of SrFeO 3-δ (SFO), where SFO is a compound with multiple valance states at the B site. Various annealing treatments are used to produce different oxygen contents in the films, whichmore » has resulted in significant structural changes in the fully strained SFO films. The out-of-plane lattice parameter and tetragonality increase with decreasing oxygen concentration, indicating the crystal structure is closely related to the oxygen content. Importantly, variation of the oxygen content in the films significantly affects the dielectric properties, leakage conduction mechanisms, and the resistive hysteresis of the materials. These results establish the relationship between oxygen content and structural and functional properties for a range of multivalent transition metal oxides.« less

Oxygen Vacancy-Tuned Physical Properties in Perovskite Thin Films with Multiple B-site Valance States

DOE PAGES

Enriquez, Erik; Chen, Aiping; Harrell, Zach; ...

2017-04-18

Controlling oxygen content in perovskite oxides with ABO 3 structure is one of most critical steps for tuning their functionality. Notably, there have been tremendous efforts to understand the effect of changes in oxygen content on the properties of perovskite thin films that are not composed of cations with multiple valance states. Here, we study the effect of oxygen vacancies on structural and electrical properties in epitaxial thin films of SrFeO 3-δ (SFO), where SFO is a compound with multiple valance states at the B site. Various annealing treatments are used to produce different oxygen contents in the films, whichmore » has resulted in significant structural changes in the fully strained SFO films. The out-of-plane lattice parameter and tetragonality increase with decreasing oxygen concentration, indicating the crystal structure is closely related to the oxygen content. Importantly, variation of the oxygen content in the films significantly affects the dielectric properties, leakage conduction mechanisms, and the resistive hysteresis of the materials. These results establish the relationship between oxygen content and structural and functional properties for a range of multivalent transition metal oxides.« less

Effect on the properties of ITO thin films in Gamma environment

NASA Astrophysics Data System (ADS)

Sofi, A. H.; Shah, M. A.; Asokan, K.

2018-04-01

The present study reports the effect of gamma irradiation of varying doses (0-200 kGy) on the physical properties of the indium tin oxide (ITO) thin films. The films were fabricated by thermal evaporation method using indium-tin (InSn) ingots followed by an oxidation in atmosphere at a temperature of 550 °C. X-ray diffraction analysis confirmed the body-centered cubic (BCC) structure corresponds to the ITO thin films, high phase purity and a variation in crystallite size between 30-44 nm. While the optical studies revealed an increase in transmission as well as variation in optical band gap, the electrical studies confirmed n-type semiconductive behavior of the thin films, increase in mobility and a decrease in resistivity from 2.33×10-2 - 9.31×10-4 Ωcm with the increase in gamma dose from 0-200 kGy. The gamma irradiation caused totally electronic excitation and resulted in this modifications. The degenerate electron gas model was considered when attempting to understand the prevalent scattering mechanism in gamma irradiated ITO thin films.

Thin film heterojunction photovoltaic cells and methods of making the same

DOEpatents

Basol, Bulent M.; Tseng, Eric S.; Rod, Robert L.

1983-06-14

A method of fabricating a thin film heterojunction photovoltaic cell which comprises depositing a film of a near intrinsic or n-type semiconductor compound formed of at least one of the metal elements of Class II B of the Periodic Table of Elements and at least tellurium and then heating said film at a temperature between about 250.degree. C. and 500.degree. C. for a time sufficient to convert said film to a suitably low resistivity p-type semiconductor compound. Such film may be deposited initially on the surface of an n-type semiconductor substrate. Alternatively, there may be deposited on the converted film a layer of n-type semiconductor compound different from the film semiconductor compound. The resulting photovoltaic cell exhibits a substantially increased power output over similar cells not subjected to the method of the present invention.

Structure and magnetic properties of Fe-Co-B alloy thin films prepared on cubic (001) single-crystal substrates

NASA Astrophysics Data System (ADS)

Ohtake, Mitsuru; Serizawa, Kana; Futamoto, Masaaki; Kirino, Fumiyoshi; Inaba, Nobuyuki

2018-04-01

Fe70Co30 and (Fe70Co30)0.95B5 (at. %) alloy films of 5 nm thickness are prepared by sputtering on cubic (001) oxide substrates at 200 °C. The lattice mismatch between film and substrate is varied from -4.2%, 0%, to +3.5% by employing MgO, MgAl2O4, and SrTiO3 substrates, respectively. Fe70Co30 and (Fe70Co30)0.95B5 single-crystal films with bcc structure grow epitaxially on all the substrates in the orientation relationship of (001)[110]film || (001)[100]substrate. The in-plane and out-of-plane lattice constants, a and c, are in agreement within small differences ranging between +1.1% and -0.9% with the value of bulk bcc-Fe70Co30 crystal, even though there exist the lattice mismatches of -4.2% and +3.5%. The result indicates that misfit dislocations are introduced around the film/substrate interface when films are deposited on MgO and SrTiO3 substrates. The single-crystal films show in-plane magnetic anisotropies with the easy magnetization direction of bcc[100], which are reflecting the magnetocrystalline anisotropy of bulk Fe70Co30 crystal.

AC impedance analysis of polypyrrole thin films

NASA Technical Reports Server (NTRS)

Penner, Reginald M.; Martin, Charles R.

1987-01-01

The AC impedance spectra of thin polypyrrole films were obtained at open circuit potentials from -0.4 to 0.4 V vs SCE. Two limiting cases are discussed for which simplified equivalent circuits are applicable. At very positive potentials, the predominantly nonfaradaic AC impedance of polypyrrole is very similar to that observed previously for finite porous metallic films. Modeling of the data with the appropriate equivalent circuit permits effective pore diameter and pore number densities of the oxidized film to be estimated. At potentials from -0.4 to -0.3 V, the polypyrrole film is essentially nonelectronically conductive and diffusion of polymer oxidized sites with their associated counterions can be assumed to be linear from the film/substrate electrode interface. The equivalent circuit for the polypyrrole film at these potentials is that previously described for metal oxide, lithium intercalation thin films. Using this model, counterion diffusion coefficients are determined for both semi-infinite and finite diffusion domains. In addition, the limiting low frequency resistance and capacitance of the polypyrrole thin fims was determined and compared to that obtained previously for thicker films of the polymer. The origin of the observed potential dependence of these low frequency circuit components is discussed.

YSZ thin films with minimized grain boundary resistivity

DOE Office of Scientific and Technical Information (OSTI.GOV)

Mills, Edmund M.; Kleine-Boymann, Matthias; Janek, Juergen

2016-03-31

In recent years, interface engineering of solid electrolytes has been explored to increase their ionic conductivity and improve the performance of solid oxide fuel cells and other electrochemical power sources. It has been observed that the ionic conductivity of epitaxially grown thin films of some electrolytes is dramatically enhanced, which is often attributed to effects (e. g. strain-induced mobility changes) at the heterophase boundary with the substrate. Still largely unexplored is the possibility of manipulation of grain boundary resistivity in polycrystalline solid electrolyte films, clearly a limiting factor in their ionic conductivity. Here we report that the ionic conductivity ofmore » yttria stabilized zirconia thin films with nano-­ columnar grains grown on a MgO substrate nearly reaches that of the corresponding single crystal when the thickness of the films becomes less than roughly 8 nm (smaller by a factor of three at 500°C). Using impedance spectroscopy, the grain boundary resistivity was probed as a function of film thickness. The resistivity of the grain boundaries near the film- substrate interface and film surface (within 4 nm of each) was almost entirely eliminated. This minimization of grain boundary resistivity is attributed to Mg2+ diffusion from the MgO substrate into the YSZ grain boundaries, which is supported by time of flight secondary ion mass spectroscopy measurements. We suggest grain boundary “design” as an attractive method to obtain highly conductive solid electrolyte thin films.« less

Domain switching kinetics in ferroelectric-resistive BiFeO3 thin film memories

NASA Astrophysics Data System (ADS)

Meng, Jianwei; Jiang, Jun; Geng, Wenping; Chen, Zhihui; Zhang, Wei; Jiang, Anquan

2015-02-01

We fabricated (00l) BiFeO3 (BFO) thin films in different growth modes on SrRuO3/SrTiO3 substrates using a pulsed laser deposition technique. X-ray diffraction patterns show an out-of-plane lattice constant of 4.03 Å and ferroelectric polarization of 82 µC/cm2 for the BFO thin film in a layer-by-layer growth mode (2D-BFO), larger than 3.96 Å and 51 µC/cm2 for the thin film in the 3D-island formation growth mode (3D-BFO). The 2D-BFO thin film at 300 K shows switchable on/off diode currents upon polarization flipping near a negative coercive voltage, which is nevertheless absent from the above 3D-BFO thin film. From a positive-up-negative-down pulse characterization technique, we measured domain switching current transients as well as polarization-voltage (Pf-Vf) hysteresis loops in both semiconducting thin films. Pf-Vf hysteresis loops after 1 µs-retention time show the preferred domain orientation pointing to bottom electrodes in a 3D-BFO thin film. The poor retention of the domains pointing to top electrodes can be improved considerably in a 2D-BFO thin film. From these measurements, we extracted domain switching time dependence of coercive voltage at temperatures of 78-300 K. From these dependences, we found coercive voltages in semiconducting ferroelectric thin films much higher than those in insulating thin films, disobeying the traditional Merz equation. Finally, an equivalent resistance model in description of free-carrier compensation of the front domain boundary charge is developed to interpret this difference. This equivalent resistance can be coincidently extracted either from domain switching time dependence of coercive voltage or from applied voltage dependence of domain switching current, which drops almost linearly with the temperature until down to 0 in a ferroelectric insulator at 78 K.