Simple additive manufacturing of an osteoconductive ceramic using suspension melt extrusion.

PubMed

Slots, Casper; Jensen, Martin Bonde; Ditzel, Nicholas; Hedegaard, Martin A B; Borg, Søren Wiatr; Albrektsen, Ole; Thygesen, Torben; Kassem, Moustapha; Andersen, Morten Østergaard

2017-02-01

Craniofacial bone trauma is a leading reason for surgery at most hospitals. Large pieces of destroyed or resected bone are often replaced with non-resorbable and stock implants, and these are associated with a variety of problems. This paper explores the use of a novel fatty acid/calcium phosphate suspension melt for simple additive manufacturing of ceramic tricalcium phosphate implants. A wide variety of non-aqueous liquids were tested to determine the formulation of a storable 3D printable tricalcium phosphate suspension ink, and only fatty acid-based inks were found to work. A heated stearic acid-tricalcium phosphate suspension melt was then 3D printed, carbonized and sintered, yielding implants with controllable macroporosities. Their microstructure, compressive strength and chemical purity were analyzed with electron microscopy, mechanical testing and Raman spectroscopy, respectively. Mesenchymal stem cell culture was used to assess their osteoconductivity as defined by collagen deposition, alkaline phosphatase secretion and de-novo mineralization. After a rapid sintering process, the implants retained their pre-sintering shape with open pores. They possessed clinically relevant mechanical strength and were chemically pure. They supported adhesion of mesenchymal stem cells, and these were able to deposit collagen onto the implants, secrete alkaline phosphatase and further mineralize the ceramic. The tricalcium phosphate/fatty acid ink described here and its 3D printing may be sufficiently simple and effective to enable rapid, on-demand and in-hospital fabrication of individualized ceramic implants that allow clinicians to use them for treatment of bone trauma. Copyright © 2016 The Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Apatite glass-ceramics: a review

NASA Astrophysics Data System (ADS)

Duminis, Tomas; Shahid, Saroash; Hill, Robert Graham

2016-12-01

This article is a review of the published literature on apatite glass-ceramics (GCs). Topics covered include crystallization mechanisms of the various families of the apatite GCs and an update on research and development on apatite GCs for applications in orthopedics, dentistry, optoelectronics and nuclear waste management. Most apatite GCs crystallize through a homogenous nucleation and crystallization mechanism, which is aided by a prior liquid-liquid phase separation. Careful control of the base glass composition and heat-treatment conditions, which determine the nature and morphology of the crystal phases in the GC can produce GC materials with exceptional thermal, mechanical, optical and biological properties. The GCs reviewed for orthopedic applications exhibit suitable mechanical properties and can chemically bond to bone and stimulate its regeneration. The most commercially successful apatite GCs are those developed for dental veneering. These materials exhibit excellent translucency and clinical esthetics, and mimic the natural tooth mineral. Due to the ease of solid solution of the apatite lattice, rare earth doped apatite GCs are discussed for potential applications in optoelectronics and nuclear waste management. One of the drawbacks of the commercial apatite GCs used in orthopedics is the lack of resorbability, therefore the review provides a direction for future research in the field.

[Our experience about the use of resorbable plates in the treatment of craniostenosis].

PubMed

Grassiot, B; Delabar, V; Szathmari, A; Beuriat, P A; Paulus, C; Mottolese, C

2015-09-01

The use of resorbable plates increases for craniosynostosis surgery. This material, based on polymere (PLA, PGA) can replace steel wire and non resorbable plates. A few studies present surgical results about the use of this material with a long follow-up. We present our ten years experience of using resorbable material for craniosynostosis treatment in children. Between 2002 and 2012, we operated 283 craniosynostosis (98 scaphocephalies, 55 trigonocephalies, 79 plagiocephalies et 51 craniofaciostenoses). Among these surgeries, 211 were realized with resorbable material (plates and screws). Different criteria were observed: the esthetic result, the infection rate, the re-intervention, the bone defects and the inflammatory granuloma. Among the 211 craniosynostosis, we found 62 plagiocephalies, 66 scaphocephalies, 50 trigonocephalies, 33 craniofaciostenoses. All the reconstructions were realized with the same resorbable material (Macropore by Medtronic). The rate of complications was low: one scar infection without participation of material for two patients (0.9%), a pseudo-meningocele for two patients (0.9%), epilepsy for four children (1.8%) and bone defect for 15 (7%). We observed no granuloma for these patients. Our experience of ten years using resorbable material is very satisfactory. This material permits to realize solid and esthetic reconstructions with a low rate of infection without dangerous reaction for children in young age. Copyright © 2015 Elsevier Masson SAS. All rights reserved.

Resorbable bone fixation alloys, forming, and post-fabrication treatments.

PubMed

Ibrahim, Hamdy; Esfahani, Sajedeh Nasr; Poorganji, Behrang; Dean, David; Elahinia, Mohammad

2017-01-01

Metallic alloys have been introduced as biodegradable metals for various biomedical applications over the last decade owing to their gradual corrosion in the body, biocompatibility and superior strength compared to biodegradable polymers. Mg alloys possess advantageous properties that make them the most extensively studied biodegradable metallic material for orthopedic applications such as their low density, modulus of elasticity, close to that of the bone, and resorbability. Early resorption (i.e., <3months) and relatively inadequate strength are the main challenges that hinder the use of Mg alloys for bone fixation applications. The development of resorbable Mg-based bone fixation hardware with superior mechanical and corrosion performance requires a thorough understanding of the physical and mechanical properties of Mg alloys. This paper discusses the characteristics of successful Mg-based skeletal fixation hardware and the possible ways to improve its properties using different methods such as mechanical and heat treatment processes. We also review the most recent work pertaining to Mg alloys and surface coatings. To this end, this paper covers (i) the properties and development of Mg alloys and coatings with an emphasis on the Mg-Zn-Ca-based alloys; (ii) Mg alloys fabrication techniques; and (iii) strategies towards achieving Mg-based, resorbable, skeletal fixation devices. Copyright © 2016 Elsevier B.V. All rights reserved.

Inflammatory foreign body reaction caused by resorbable materials used for orbital fractures repair: A case report.

PubMed

He, Jie; Shi, Wodong

2017-12-01

Resorbable materials have been recommended for orbital fractures repair. Many literatures reported the advantages of resorbable materials in clinical applications, but few reports about complications. In this study, we encountered a 14-year-old boy treated for the orbital fracture by using resorbable plate, in whom inflammatory foreign body reaction was detected. In addition, this patient had repeated history of skin allergy and upper respiratory tract infection. Intraoperative observation showed that the resorbable material near the orbital rim was covered by granulation and inflammatory tissues, without purulent secretions. The histological examination revealed inflammatory foreign body reaction to the resorbable plate. Debridement was taken to remove the mass on the left lower eyelid. At the outpatient examination, a small amount of granulation tissue was found at the incision. Then, secondary surgery for exploration and removal of the resorbable material was carried, 9 months after the first surgery. One month after the surgery, the skin retraction, ectropion, and edema gradually improved. Inadequate degradation of resorbable materials and patient's medical history of allergies may cause an inflammatory foreign body reaction. Therefore, it is prudent to choose resorbable materials for patients.

Inflammatory foreign body reaction caused by resorbable materials used for orbital fractures repair

PubMed Central

He, Jie; Shi, Wodong

2017-01-01

Abstract Rationale: Resorbable materials have been recommended for orbital fractures repair. Many literatures reported the advantages of resorbable materials in clinical applications, but few reports about complications. Patient concerns: In this study, we encountered a 14-year-old boy treated for the orbital fracture by using resorbable plate, in whom inflammatory foreign body reaction was detected. In addition, this patient had repeated history of skin allergy and upper respiratory tract infection. Diagnoses: Intraoperative observation showed that the resorbable material near the orbital rim was covered by granulation and inflammatory tissues, without purulent secretions. The histological examination revealed inflammatory foreign body reaction to the resorbable plate. Interventions: Debridement was taken to remove the mass on the left lower eyelid. At the outpatient examination, a small amount of granulation tissue was found at the incision. Then, secondary surgery for exploration and removal of the resorbable material was carried, 9 months after the first surgery. Outcomes: One month after the surgery, the skin retraction, ectropion, and edema gradually improved. Lessons: Inadequate degradation of resorbable materials and patient's medical history of allergies may cause an inflammatory foreign body reaction. Therefore, it is prudent to choose resorbable materials for patients. PMID:29245243

21 CFR 888.3045 - Resorbable calcium salt bone void filler device.

Code of Federal Regulations, 2012 CFR

2012-04-01

... 21 Food and Drugs 8 2012-04-01 2012-04-01 false Resorbable calcium salt bone void filler device... salt bone void filler device. (a) Identification. A resorbable calcium salt bone void filler device is... entitled “Class II Special Controls Guidance: Resorbable Calcium Salt Bone Void Filler Device; Guidance for...

21 CFR 888.3045 - Resorbable calcium salt bone void filler device.

Code of Federal Regulations, 2014 CFR

2014-04-01

... 21 Food and Drugs 8 2014-04-01 2014-04-01 false Resorbable calcium salt bone void filler device... salt bone void filler device. (a) Identification. A resorbable calcium salt bone void filler device is... entitled “Class II Special Controls Guidance: Resorbable Calcium Salt Bone Void Filler Device; Guidance for...

21 CFR 888.3045 - Resorbable calcium salt bone void filler device.

Code of Federal Regulations, 2011 CFR

2011-04-01

... 21 Food and Drugs 8 2011-04-01 2011-04-01 false Resorbable calcium salt bone void filler device... salt bone void filler device. (a) Identification. A resorbable calcium salt bone void filler device is... entitled “Class II Special Controls Guidance: Resorbable Calcium Salt Bone Void Filler Device; Guidance for...

21 CFR 888.3045 - Resorbable calcium salt bone void filler device.

Code of Federal Regulations, 2010 CFR

2010-04-01

... 21 Food and Drugs 8 2010-04-01 2010-04-01 false Resorbable calcium salt bone void filler device... salt bone void filler device. (a) Identification. A resorbable calcium salt bone void filler device is... entitled “Class II Special Controls Guidance: Resorbable Calcium Salt Bone Void Filler Device; Guidance for...

21 CFR 888.3045 - Resorbable calcium salt bone void filler device.

Code of Federal Regulations, 2013 CFR

2013-04-01

... 21 Food and Drugs 8 2013-04-01 2013-04-01 false Resorbable calcium salt bone void filler device... salt bone void filler device. (a) Identification. A resorbable calcium salt bone void filler device is... entitled “Class II Special Controls Guidance: Resorbable Calcium Salt Bone Void Filler Device; Guidance for...

Use of a 3D Skull Model to Improve Accuracy in Cranioplasty for Autologous Flap Resorption in a 3-Year-Old Child.

PubMed

Maduri, Rodolfo; Viaroli, Edoardo; Levivier, Marc; Daniel, Roy T; Messerer, Mahmoud

2017-01-01

Cranioplasty is considered a simple reconstructive procedure, usually performed in a single stage. In some clinical conditions, such as in children with multifocal flap osteolysis, it could represent a surgical challenge. In these patients, the partially resorbed autologous flap should be removed and replaced with a precustomed prosthesis which should perfectly match the expected bone defect. We describe the technique used for a navigated cranioplasty in a 3-year-old child with multifocal autologous flap osteolysis. We decided to perform a cranioplasty using a custom-made hydroxyapatite porous ceramic flap. The prosthesis was produced with an epoxy resin 3D skull model of the patient, which included a removable flap corresponding to the planned cranioplasty. Preoperatively, a CT scan of the 3D skull model was performed without the removable flap. The CT scan images of the 3D skull model were merged with the preoperative 3D CT scan of the patient and navigated during the cranioplasty to define with precision the cranioplasty margins. After removal of the autologous resorbed flap, the hydroxyapatite prosthesis matched perfectly with the skull defect. The anatomical result was excellent. Thus, the implementation of cranioplasty with image merge navigation of a 3D skull model may improve cranioplasty accuracy, allowing precise anatomic reconstruction in complex skull defect cases. © 2017 S. Karger AG, Basel.

Silk-based resorbable electronic devices for remotely controlled therapy and in vivo infection abatement

PubMed Central

Tao, Hu; Hwang, Suk-Won; Marelli, Benedetto; An, Bo; Moreau, Jodie E.; Yang, Miaomiao; Brenckle, Mark A.; Kim, Stanley; Kaplan, David L.; Rogers, John A.; Omenetto, Fiorenzo G.

2014-01-01

A paradigm shift for implantable medical devices lies at the confluence between regenerative medicine, where materials remodel and integrate in the biological milieu, and technology, through the use of recently developed material platforms based on biomaterials and bioresorbable technologies such as optics and electronics. The union of materials and technology in this context enables a class of biomedical devices that can be optically or electronically functional and yet harmlessly degrade once their use is complete. We present here a fully degradable, remotely controlled, implantable therapeutic device operating in vivo to counter a Staphylococcus aureus infection that disappears once its function is complete. This class of device provides fully resorbable packaging and electronics that can be turned on remotely, after implantation, to provide the necessary thermal therapy or trigger drug delivery. Such externally controllable, resorbable devices not only obviate the need for secondary surgeries and retrieval, but also have extended utility as therapeutic devices that can be left behind at a surgical or suturing site, following intervention, and can be externally controlled to allow for infection management by either thermal treatment or by remote triggering of drug release when there is retardation of antibiotic diffusion, deep infections are present, or when systemic antibiotic treatment alone is insufficient due to the emergence of antibiotic-resistant strains. After completion of function, the device is safely resorbed into the body, within a programmable period. PMID:25422476

Silk-based resorbable electronic devices for remotely controlled therapy and in vivo infection abatement.

PubMed

Tao, Hu; Hwang, Suk-Won; Marelli, Benedetto; An, Bo; Moreau, Jodie E; Yang, Miaomiao; Brenckle, Mark A; Kim, Stanley; Kaplan, David L; Rogers, John A; Omenetto, Fiorenzo G

2014-12-09

A paradigm shift for implantable medical devices lies at the confluence between regenerative medicine, where materials remodel and integrate in the biological milieu, and technology, through the use of recently developed material platforms based on biomaterials and bioresorbable technologies such as optics and electronics. The union of materials and technology in this context enables a class of biomedical devices that can be optically or electronically functional and yet harmlessly degrade once their use is complete. We present here a fully degradable, remotely controlled, implantable therapeutic device operating in vivo to counter a Staphylococcus aureus infection that disappears once its function is complete. This class of device provides fully resorbable packaging and electronics that can be turned on remotely, after implantation, to provide the necessary thermal therapy or trigger drug delivery. Such externally controllable, resorbable devices not only obviate the need for secondary surgeries and retrieval, but also have extended utility as therapeutic devices that can be left behind at a surgical or suturing site, following intervention, and can be externally controlled to allow for infection management by either thermal treatment or by remote triggering of drug release when there is retardation of antibiotic diffusion, deep infections are present, or when systemic antibiotic treatment alone is insufficient due to the emergence of antibiotic-resistant strains. After completion of function, the device is safely resorbed into the body, within a programmable period.

Acceleration of Alveolar Ridge Augmentation Using a Low Dose of Recombinant Human Bone Morphogenetic Protein-2 Loaded on a Resorbable Bioactive Ceramic.

PubMed

Fahmy, Rania A; Mahmoud, Naguiba; Soliman, Samia; Nouh, Samir R; Cunningham, Larry; El-Ghannam, Ahmed

2015-12-01

The aim of the present study was to evaluate the effect of a porous silica-calcium phosphate composite (SCPC50) loaded with and without recombinant human bone morphogenetic protein-2 (rhBMP-2) on alveolar ridge augmentation in saddle-type defects. Micro-granules of SCPC50 resorbable bioactive ceramic were coated with rhBMP-2 10 mg and then implanted into a saddle-type defect (12 × 7 mm) in a dog mandible and covered with a collagen membrane. Control groups included defects grafted with SCPC50 granules without rhBMP-2 and un-grafted defects. Bone healing was evaluated at 8 and 16 weeks using histologic and histomorphometric techniques. The increase in bone height and total defect fill were assessed for each specimen using the ImageJ 1.46 program. The release kinetics of rhBMP-2 was determined in vitro. The height of the bone in the grafted defects and the total defect fill were statistically analyzed. SCPC50 enhanced alveolar ridge augmentation as indicated by the increased vertical bone height, bone surface area, and bone volume after 16 weeks. SCPC50-rhBMP-2 provided a sustained release profile of a low effective dose (BMP-2 4.6 ± 1.34 pg/mL per hour) during the 1- to 21-day period. The slow rate of release of rhBMP-2 from SCPC50 accelerated synchronized complete bone regeneration and graft material resorption in 8 weeks. Successful rapid reconstruction of the alveolar ridge by SCPC50 and SCPC50-rhBMP-2 occurred without any adverse excessive bone formation, inflammation, or fluid-filled voids. Results of this study suggest that SCPC50 is an effective graft material to preserve the alveolar ridge after tooth extraction. Coating SCPC50-rhBMP-2 further accelerated bone regeneration and a considerable increase in vertical bone height. These findings make SCPC50 the primary choice as a carrier for rhBMP-2. SCPC50-rhBMP-2 can serve as an alternative to autologous bone grafting. Published by Elsevier Inc.

Dilemma in pediatric mandible fractures: resorbable or metallic plates?

PubMed

Taylan Filinte, Gaye; Akan, İsmail Mithat; Ayçiçek Çardak, Gülçin Nujen; Özkaya Mutlu, Özay; Aköz, Tayfun

2015-12-01

The aim of this study was to compare the efficiency of resorbable and metallic plates in open reduction and internal fixation of mandible fractures in children. Thirty-one patients (mean age, 8.05 years; range 20 months-14 years) were operated on various fractures of the mandible (26 [60.4%] symphysis- parasymphysis, 12 [27.9%] condylar-subcondylar fractures, 5 [11.6%] angulus and ramus fractures). Twelve patients were treated with resorbable plates and 19 patients with metallic plates. Mean follow-up time was 41 months (11-74 months) in the metallic hardware group and was 22 months (8-35 months) in the resorbable plate group. Both groups were investigated for primary bone healing, complications, number of operations, and mandibular growth. The results were discussed below. Both groups demonstrated primary bone healing. Minor complications were similar in both groups. The metallic group involved secondary operations for plate removal. Mandibular growth was satisfactory in both groups. Resorbable plates cost more than the metallic ones; however, when the secondary operations are included in the total cost, resorbable plates were favourable. As mandibular growth and complication parameters are similar in both groups, resorbable plates are favored due to avoidance of potential odontogenic injury, elimination of long-term foreign body retention and provision of adequate stability for rapid bone healing. However, learning curve and concerns for decreased stability against heavy forces of mastication accompanied with the resorbable plates when compared to the metallic ones should be kept in mind.

High biocompatibility and improved osteogenic potential of novel Ca-P/titania composite scaffolds designed for regeneration of load-bearing segmental bone defects.

PubMed

Cunha, Carla; Sprio, Simone; Panseri, Silvia; Dapporto, Massimiliano; Marcacci, Maurilio; Tampieri, Anna

2013-06-01

Regeneration of load-bearing bone segments is still an open challenge due to the lack of biomaterials mimicking natural bone with a suitable chemicophysical and mechanical performance. This study proposes ceramic bone scaffolds made of β-tricalcium phosphate (β-TCP) and titania (TiO2 ), developed from hydroxyapatite (HA) and TiO2 starting nanopowders, which exhibit high and interconnected macroporosity (>70 vol %). The scaffold composition was designed to achieve a synergistic effect of bioactivity/resorbability and mechanical properties suitable for load-bearing regenerative applications. The analysis of the morphology, structure, and mechanical strength of the scaffolds resulted in compression strength nearly twice that of commercially available HA bone grafts with similar structure (Engipore(®)). Biological characterization was carried out for human MG-63 osteoblast-like cells proliferation, activity, attachment, and viability. β-TCP/TiO2 scaffolds show high proliferation rate, high viability, and high colonization rates. Moreover, an increased activity of the osteogenic marker alkaline phosphatase (ALP) was found. These results demonstrate that β-TCP/TiO2 scaffolds have good potential as osteogenically active load-bearing scaffolds; moreover, given the high and interconnected macroporosity as well as the resorbability properties of β-TCP, these scaffolds may enhance in vivo osteointegration and promote the formation of new organized bone, thus resulting in very promising biomimetic scaffolds for long bone regeneration. Copyright © 2012 Wiley Periodicals, Inc.

Orthopedic devices; classification for the resorbable calcium salt bone void filler device. Final rule.

PubMed

2003-06-02

The Food and Drug Administration (FDA) is classifying the resorbable calcium salt bone void filler device intended to fill bony voids or gaps of the extremities, spine, and pelvis that are caused by trauma or surgery and are not intrinsic to the stability of the bony structure into class II (special controls). Elsewhere in this issue of the Federal Register, FDA is announcing the availability of a class II special controls guidance entitled "Class II Special Controls Guidance Document: Resorbable Calcium Salt Bone Void Filler Device; Guidance for Industry and FDA." This action is being undertaken based on new information submitted in a classification proposal from Wright Medical Technology under the Federal Food, Drug, and Cosmetic Act as amended by the Medical Device Amendments of 1976, the Safe Medical Devices Act of 1990, and the Food and Drug Administration Modernization Act of 1997.

Design and Optimization of Resorbable Silk Internal Fixation Devices

NASA Astrophysics Data System (ADS)

Haas, Dylan S.

Limitations of current material options for internal fracture fixation devices have resulted in a large gap between user needs and hardware function. Metal systems offer robust mechanical strength and ease of implantation but require secondary surgery for removal and/or result in long-term complications (infection, palpability, sensitivity, etc.). Current resorbable devices eliminate the need for second surgery and long-term complications but are still associated with negative host response as well as limited functionality and more difficult implantation. There is a definitive need for orthopedic hardware that is mechanically capable of immediate fracture stabilization and fracture fixation during healing, can safely biodegrade while allowing complete bone remodeling, can be resterilized for reuse, and is easily implantable (self-tapping). Previous work investigated the use of silk protein to produce resorbable orthopedic hardware for non- load bearing fracture fixation. In this study, silk orthopedic hardware was further investigated and optimized in order to better understand the ability of silk as a fracture fixation system and more closely meet the unfulfilled market needs. Solvent-based and aqueous-based silk processing formulations were cross-linked with methanol to induce beta sheet structure, dried, autoclaved and then machined to the desired device/geometry. Silk hardware was evaluated for dry, hydrated and fatigued (cyclic) mechanical properties, in vitro degradation, resterilization, functionalization with osteoinductive molecules and implantation technique for fracture fixation. Mechanical strength showed minor improvements from previous results, but remains comparable to current resorbable fixation systems with the advantages of self-tapping ability for ease of implantation, full degradation in 10 months, ability to be resterilized and reused, and ability to release molecules for osteoinudction. In vivo assessment confirmed biocompatibility, showed improved bone deposition and remodeling with functionalization and showed promising feasibility of fracture fixations with minor adjustments to geometry. The proposed silk orthopedic hardware exhibits high potential as a resorbable fixation system that can bridge the gap between the current materials for internal fixation devices.

Biomechanical analysis of a newly designed bioabsorbable anterior cervical plate. Invited submission from the joint section meeting on disorders of the spine and peripheral nerves, March 2005.

PubMed

Ames, Christopher P; Acosta, Frank L; Chamberlain, Robert H; Larios, Adolfo Espinoza; Crawford, Neil R

2005-12-01

The authors present a biomechanical analysis of a newly designed bioabsorbable anterior cervical plate (ACP) for the treatment of one-level cervical degenerative disc disease. They studied anterior cervical discectomy and fusion (ACDF) in a human cadaveric model, comparing the stability of the cervical spine after placement of the bioabsorbable fusion plate, a bioabsorbable mesh, and a more traditional metallic ACP. Seven human cadaveric specimens underwent a C6-7 fibular graft-assisted ACDF placement. A one-level resorbable ACP was then placed and secured with bioabsorbable screws. Flexibility testing was performed on both intact and instrumented specimens using a servohydraulic system to create flexion-extension, lateral bending, and axial rotation motions. After data analysis, three parameters were calculated: angular range of motion, lax zone, and stiff zone. The results were compared with those obtained in a previous study of a resorbable fusion mesh and with those acquired using metallic fusion ACPs. For all parameters studied, the resorbable plate consistently conferred greater stability than the resorbable mesh. Moreover, it offered comparable stability with that of metallic fusion ACPs. Bioabsorbable plates provide better stability than resorbable mesh. Although the results of this study do not necessarily indicate that a resorbable plate confers equivalent stability to a metal plate, the resorbable ACP certainly yielded better results than the resorbable mesh. Bioabsorbable fusion ACPs should therefore be considered as alternatives to metal plates when a graft containment device is required.

Early-term and mid-term histologic events during single-level posterolateral intertransverse process fusion with rhBMP-2/collagen carrier and a ceramic bulking agent in a nonhuman primate model: implications for bone graft preparation.

PubMed

Khan, Safdar N; Toth, Jeffrey M; Gupta, Kavita; Glassman, Steven D; Gupta, Munish C

2014-06-01

We used a nonhuman primate lumbar intertransverse process arthrodesis model to evaluate biological cascade of bone formation using different carrier preparation methods with a single dose of recombinant human bone morphogenetic protein-2 (rhBMP-2) at early time points. To examine early-term/mid-term descriptive histologic and computerized tomographic events in single-level uninstrumented posterolateral nonhuman primate spinal fusions using rhBMP-2/absorbable collagen sponge (ACS) combined with ceramic bulking agents in 3 different configurations. rhBMP-2 on an ACS carrier alone leads to consistent posterolateral lumbar spine fusions in lower-order animals; however, these results have been difficult to replicate in nonhuman primates. Twelve skeletally mature, rhesus macaque monkeys underwent single-level posterolateral arthrodesis at L4-L5. A hydroxyapatite/β-tricalcium phosphate ceramic bulking agent in 3 formulations was used in the treatment groups (n=3). When used, rhBMP-2/ACS at 1.5 mg/cm (3.0 mg rhBMP-2) was combined with 2.5 cm of ceramic bulking agent per side. Animals were euthanized at 4 and 12 weeks postoperative. Computerized tomography scans were performed immediately postoperatively and every 4 weeks until they were euthanized. Sagittal histologic sections were evaluated for bone histogenesis and location, cellular infiltration of the graft/substitute, and bone remodeling activity. Significant histologic differences in the developing fusion appeared between the 3 rhBMP-2/ACS treatment groups at 4 and 12 weeks. At 4 weeks, bone formation appeared to originate at the transverse process and the intertransverse membrane. Cellular infiltration was greatest in granular ceramic groups compared with matrix ceramic group. Minimal to no residual ACS was identified at the early time point. At 12 weeks, marked ceramic remodeling was observed with continued bone formation noted in all carrier groups. At the early time period, histology showed that bone formation appeared to originate at the transverse processes and the intertransverse membrane, indicating that the dorsal muscle bed may not be the only location for bone formation. Histology also showed that the collagen carrier for rhBMP-2 is mostly resorbed by 4 weeks. Our results and previous literature indicate that ceramic bulking agents are needed to provide resistance to compression caused by paraspinal muscles on the fusion bed in the posterolateral environment. Histology showed that ceramic bulking agents may offer long-term scaffolding and a structure to supporting bone formation of the developing fusion mass.

Degradation and silicon excretion of the calcium silicate bioactive ceramics during bone regeneration using rabbit femur defect model.

PubMed

Lin, Kaili; Liu, Yong; Huang, Hai; Chen, Lei; Wang, Zhen; Chang, Jiang

2015-06-01

The investigation of the bone regeneration ability, degradation and excretion of the grafts is critical for development and application of the newly developed biomaterials. Herein, the in vivo bone-regeneration, biodegradation and silicon (Si) excretion of the new type calcium silicate (CaSiO3, CS) bioactive ceramics were investigated using rabbit femur defect model, and the results were compared with the traditional β-tricalcium phosphate [β-Ca3(PO4)2, β-TCP] bioceramics. After implantation of the scaffolds in rabbit femur defects for 4, 8 and 12 weeks, the bone regenerative capacity and degradation were evaluated by histomorphometric analysis. While urine and some organs such as kidney, liver, lung and spleen were resected for chemical analysis to determine the excretion of the ionic products from CS implants. The histomorphometric analysis showed that the bioresorption rate of CS was similar to that of β-TCP in femur defect model, while the CS grafts could significantly stimulate bone formation capacity as compared with β-TCP bioceramics (P < 0.05). The chemical analysis results showed that Si concentration in urinary of the CS group was apparently higher than that in control group of β-TCP. However, no significant increase of the Si excretion was found in the organs including kidney, which suggests that the resorbed Si element is harmlessly excreted in soluble form via the urine. The present studies show that the CS ceramics can be used as safe, bioactive and biodegradable materials for hard tissue repair and tissue engineering applications.

Polymer-ceramic nanocomposites for applications in the bone surgery

NASA Astrophysics Data System (ADS)

Stodolak, E.; Gadomska, K.; Lacz, A.; Bogun, M.

2009-01-01

The subject of this work was preparation and investigation of properties of a nanocomposite material based on polymer matrix modified with nanometric silica particles (SiO2). The composite matrix consisted of resorbable P(L/DL)LA polymer with certified biocompatibility. Nanometric silica was introduced into the matrix by means of ultrasonic homogenisation and/or mechanical stirring. The silica was introduced directly e.g. as nanoparticles or inside calcium alginate fibres which contained 3 wt.% of amorphous SiO2. Proper dispersion of nano-filliers was confirmed by means of thermal analysis (TG/DTA, DSC). It was observed, that the presence of inorganic nanoparticles influenced several surface parameters of the nanocomposites i.e. hydrophility (a decrease of surface energy) and topography (both in micro- and nano-scale). Additionally, the nanocomposites exhibited enhanced mechanical properties (Young's modulus, tensile strength) compared to the pure polymer. The nanocomposites were bioactive materials (SBF/3 days/37oC). Biological tests (MTT test) showed a good viability of human osteoblasts (hFOB 1.19) in contact with the nanocomposites surface. Results of preliminary biological tests carried out with the use of mother cells extracted from human bone marrow showed that the nanocomposites may provide differenation of bone cells.

Toward Smart Implant Synthesis: Bonding Bioceramics of Different Resorbability to Match Bone Growth Rates

PubMed Central

Comesaña, Rafael; Lusquiños, Fernando; del Val, Jesús; Quintero, Félix; Riveiro, Antonio; Boutinguiza, Mohamed; Jones, Julian R.; Hill, Robert G.; Pou, Juan

2015-01-01

Craniofacial reconstructive surgery requires a bioactive bone implant capable to provide a gradual resorbability and to adjust to the kinetics of new bone formation during healing. Biomaterials made of calcium phosphate or bioactive glasses are currently available, mainly as bone defect fillers, but it is still required a versatile processing technique to fabricate composition-gradient bioceramics for application as controlled resorption implants. Here it is reported the application of rapid prototyping based on laser cladding to produce three-dimensional bioceramic implants comprising of a calcium phosphate inner core, with moderate in vitro degradation at physiological pH, surrounded by a bioactive glass outer layer of higher degradability. Each component of the implant is validated in terms of chemical and physical properties, and absence of toxicity. Pre–osteoblastic cell adhesion and proliferation assays reveal the adherence and growth of new bone cells on the material. This technique affords implants with gradual-resorbability for restoration of low-load-bearing bone. PMID:26032983

Quickening: Translational design of resorbable synthetic vascular grafts.

PubMed

Stowell, Chelsea E T; Wang, Yadong

2018-08-01

Traditional tissue-engineered vascular grafts have yet to gain wide clinical use. The difficulty of scaling production of these cell- or biologic-based products has hindered commercialization. In situ tissue engineering bypasses such logistical challenges by using acellular resorbable scaffolds. Upon implant, the scaffolds become remodeled by host cells. This review describes the scientific and translational advantages of acellular, synthetic vascular grafts. It surveys in vivo results obtained with acellular synthetics over their fifty years of technological development. Finally, it discusses emerging principles, highlights strategic considerations for designers, and identifies questions needing additional research. Copyright © 2018 Elsevier Ltd. All rights reserved.

Characterization of a resorbable poly(ester urethane) with biodegradable hard segments.

PubMed

Dempsey, David K; Robinson, Jennifer L; Iyer, Ananth V; Parakka, James P; Bezwada, Rao S; Cosgriff-Hernandez, Elizabeth M

2014-01-01

The rapid growth of regenerative medicine and drug delivery fields has generated a strong need for improved polymeric materials that degrade at a controlled rate into safe, non-cytotoxic by-products. Polyurethane thermoplastic elastomers offer several advantages over other polymeric materials including tunable mechanical properties, excellent fatigue strength, and versatile processing. The variable segmental chemistry in developing resorbable polyurethanes also enables fine control over the degradation profile as well as the mechanical properties. Linear aliphatic isocyanates are most commonly used in biodegradable polyurethane formulations; however, these aliphatic polyurethanes do not match the mechanical properties of their aromatic counterparts. In this study, a novel poly(ester urethane) (PEsU) synthesized with biodegradable aromatic isocyanates based on glycolic acid was characterized for potential use as a new resorbable material in medical devices. Infrared spectral analysis confirmed the aromatic and phase-separated nature of the PEsU. Uniaxial tensile testing displayed stress-strain behavior typical of a semi-crystalline polymer above its Tg, in agreement with calorimetric findings. PEsU outperformed aliphatic PCL-based polyurethanes likely due to the enhanced cohesion of the aromatic hard domains. Accelerated degradation of the PEsU using 0.1 M sodium hydroxide resulted in hydrolysis of the polyester soft segment on the surface, reduced molecular weight, surface cracking, and a 30% mass loss after four weeks. Calorimetric studies indicated a disruption of the soft segment crystallinity after incubation which corresponded with a drop in initial modulus of the PEsU. Finally, cytocompatibility testing with 3T3 mouse fibroblasts exhibited cell viability on PEsU films comparable to a commercial poly(ether urethane urea) after 24 h followed by 85% cell viability at 72 h. Overall, this new resorbable polyurethane shows strong potential for use in wide range of biomedical applications.

Comparison of Resorbable Plating Systems: Complications During Degradation.

PubMed

Nguyen, Dennis C; Woo, Albert S; Farber, Scott J; Skolnick, Gary B; Yu, Jenny; Naidoo, Sybill D; Patel, Kamlesh B

2017-01-01

Several bioresorbable plating systems have become standard in pediatric craniosynostosis reconstruction. A comparison of these systems is needed to aid surgeons in the preoperative planning process. The authors aim to evaluate 1 institution's experience using Resorb-X by KLS Martin and Delta Resorbable Fixation System by Stryker (Stryker Craniomaxillofacial, Kalamazoo, MI). A sample of patients with single-suture nonsyndromic craniosynostosis treated at St Louis Children's Hospital between 2007 and 2014 using either Resorb-X or Delta bioresorbable plating systems were reviewed. Only patients with preoperative, immediate, and long-term 3-dimensional photographic images or computed tomography scans were included. A comparison of plating system outcomes was performed to determine the need for clinic and emergency room visits, imaging obtained, and incidence of subsequent surgical procedures due to complications. Forty-six patients (24 Resorb-X and 22 Delta) underwent open repair with bioabsorbable plating for single suture craniosynostosis. The mean age at each imaging time point was similar between the 2 plating systems (P > 0.717). Deformity-specific measures for sagittal (cranial index), metopic (interfrontotemporale), and unicoronal (frontal asymmetry) synostosis were equivalent between the systems at all time points (0.05 < P < 0.904). A single Delta patient developed bilateral scalp cellulitis and abscesses and subsequently required operative intervention and antibiotics. Bioabsorbable plating for craniosynostosis in children is effective and has low morbidity. In our experience, the authors did not find a difference between the outcomes and safety profiles between Resorb-X and Delta.

The effect of particle size on the in vivo degradation of poly(d,l-lactide-co-glycolide)/α-tricalcium phosphate micro- and nanocomposites.

PubMed

Bennett, Sarah M; Arumugam, Meera; Wilberforce, Samuel; Enea, Davide; Rushton, Neil; Zhang, Xiang C; Best, Serena M; Cameron, Ruth E; Brooks, Roger A

2016-11-01

This paper reports the effect of particle size within a resorbable composite on the in vivo degradation rate and host response. Resorbable composites based on poly(d,l-lactide-co-glycolide) (PLGA) reinforced with tricalcium phosphate (TCP) have shown suitable degradation, biological and mechanical properties for bone repair. Composites with nano-sized TCP particles degrade more homogenously in vitro than equivalent composites with micro-sized particles. In this study, PLGA and PLGA/TCP composites containing micro- or nano-sized α-TCP particles were implanted into an ovine distal femoral condyle defect and harvested at 6, 12, 18 and 24weeks. An intimate interface was observed between the new bone tissue and degrading implants. Visual scoring of histological images and semi-automated segmentation of X-ray images were used to quantify implant degradation and the growth of new bone tissue in the implant site. Bone growth into the implant site occurred at a similar rate for both composites and the PLGA control. However, the in vivo degradation rate of the nanocomposite was slower than that of the microcomposite and consequently more closely matched the rate of bone growth. For the first 6weeks, the rate of in vivo degradation matched that of in vitro degradation, but lagged significantly at longer time points. These results point to the potential use of ceramic particle size in controlling composite degradation whilst maintaining good bone formation. This paper concerns degradable composites for orthopaedic application. The effect of particle size on implant degradation in vivo is not yet well characterised and these results give the first opportunity to directly compare in vitro and in vivo degradation rates for composites with micro- and nano-sized particles. This type of data is vital for the validation of models of composite degradation behaviour, which will lead to the design and manufacture of composites with a tailored, predictable degradation profile. The trainable segmentation tool can be used for future studies where X-rays of partially degraded implants (which have complicated greyscales and morphologies) need to be quantified without bias. Copyright © 2016 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

A clinical evaluation of resorbable hydroxylapatite for the repair of human intra-osseous defects.

PubMed

Corsair, A

1990-01-01

One of the goals of periodontal therapy is actual hard- and soft-tissue regeneration or at least the functional repair of periodontal defects. Alloplastic materials used in the past included dense hydroxylapatite grafts which were non-resorbable and often exfoliated. A new resorbable hydroxylapatite biomaterial [OsteoGen (HA RESORB)] was used during flap surgery. After the usual initial therapy, full-thickness flaps were elevated. A through debridement of the roots and osseous defects was accomplished. The defects were measured and then filled with OsteoGen. The mean initial bone defect depth was 4.47 mm. These defects were re-evaluated by the probing of bone levels after a 4-6-month healing period. A mean of 2.26 mm of new bone fill was obtained. This represents an average fill of 51%. Seventeen of the 22 defects had 42% or more actual new bone fill. No foreign body reaction or exfoliation occurred.

Absorption machine with desorber-resorber

DOEpatents

Biermann, Wendell J.

1985-01-01

An absorption refrigeration system utilizing a low temperature desorber and intermediate temperature resorber. The system operates at three temperatures and three pressures to increase the efficiency of the system and is capable of utilizing a lower generator temperature than previously used.

Use of resorbable plates and screws in pediatric facial fractures.

PubMed

Eppley, Barry L

2005-03-01

The use of resorbable plates and screws for fixation of pediatric facial fractures is both well tolerated and effective. It enables realignment and stable positioning of rapidly healing fracture segments while obviating any future issues secondary to long-term metal retention. Forty-four pediatric facial fractures were treated over a 10-year period at our institution using differing techniques of polymeric bone fixation. Twenty-nine mandible fractures in patients under the age of 10 (age range, 6 months to 8 years) were treated. Displaced fractures of the symphysis, parasymphysis, body, and ramus underwent open reduction and either 1.5-mm or 2.0-mm plate and screw fixation in 14 patients. Subcondylar fractures were treated by a short period of maxillomandibular fixation (3 weeks) achieved with suture ligation between resorbable screws placed at the zygoma and symphysis or a circummandibular suture attached to a zygomatic screw. Fifteen patients (age range, 4 to 11 years) with isolated frontal, supraorbital, intraorbital, or orbitozygomatic fractures were treated by open reduction and internal fixation with 1.5-mm resorbable plates, mesh, and screws. No long-term implant-related complications were seen in any of the treated patients. Resorbable polylactic and polyglycolic acid plates and screws can be an effective fixation method for facial fractures in children in the primary and secondary dentition periods.

Resorbable Self-Locking Implant for Lung Lobectomy Through Video-Assisted Thoracoscopic Surgery: First Live Animal Application.

PubMed

Guedes, Rogério Luizari; Höglund, Odd Viking; Brum, Juliana Sperotto; Borg, Niklas; Dornbusch, Peterson Triches

2018-04-01

The aim of this pilot test was to test a new self-locking resorbable implant for hilum occlusion during a video-assisted thoracoscopic lung lobectomy in a surviving pig model. Once the thoracic cavity was assessed and structures identified, the right middle lobe and its respective hilum were exposed. The implant was introduced with a semiclosed loop through a working channel and positioned around the pulmonary lobe. Occlusion was performed with a conventional Crile forceps and a laparoscopic Kelly forceps. Lobe section was done with laparoscopic Metzenbaum scissors and tissue removal through the dorsal access. No signs of pneumothorax or bleeding were observed during a 60-day follow-up. Necropsy findings showed minimal pleuritis in caudal access and in the lobar stump. A granulomatous formation was found around a dense, amorphous material, which was identified as remains of a small part of the implant. Histopathological findings showed signs of a chronic healing process without other alterations. The resorbable implant LigaTie appears to exhibit similar handling and application characteristics during surgery as nonsurgical tie wraps. The resorbable implant avoids the uncontrolled substances not suitable for implants of conventional ties. The results of this pilot test suggested the resorbable implant's mechanical properties provided effective tissue support to complete the healing of the pulmonary hilum.

The cell biology and role of resorptive cells in diseases: A review.

PubMed

Babaji, Prashant; Devanna, Raghu; Jagtap, Kiran; Chaurasia, Vishwajit Rampratap; Jerry, Jeethu John; Choudhury, Basanta Kumar; Duhan, Dinesh

2017-01-01

Resorptive cells are responsible for the resorption of mineralized matrix of hard tissues. Bone-resorbing cells are called osteoclasts; however, they can resorb mineralized dental tissues or calcified cartilage and then they are called odontoclasts and chondroclasts, respectively. Resorptive cells form when mononuclear precursors derived from a monocyte-macrophage cell lineage are attracted to certain mineralized surfaces and subsequently fuse and adhere onto them for exerting their resorbing activity. These cells are responsible for degradation of calcified extracellular matrix composed of organic molecules and hydroxyapatite. The activity of these cells can be observed in both physiological and pathological processes throughout life and their activity is mainly required in bone turnover and growth, spontaneous and induced (orthodontic) tooth movement, tooth eruption, and bone fracture healing, as well as in pathological conditions such as osteoporosis, osteoarthritis, and bone metastasis. In addition, they are responsible for daily control of calcium homeostasis. Clastic cells also resorb the primary teeth for shedding before the permanent teeth erupt into the oral cavity.

Magmatic interactions as recorded in plagioclase phenocrysts of Chaos Crags, Lassen Volcanic Center, California

USGS Publications Warehouse

Tepley, F. J.; Davidson, J.P.; Clynne, M.A.

1999-01-01

The silicic lava domes of Chaos Crags in Lassen Volcanic National Park contain a suite of variably quenched, hybrid basaltic andesite magmatic inclusions. The inclusions represent thorough mixing between rhyodacite and basalt recharge liquids accompanied by some mechanical disaggregation of the inclusions resulting in crystals mixing into the rhyodacite host preserved by quenching on dome emplacement. 87Sr/86Sr ratios (~0.7037-0.7038) of the inclusions are distinctly lower than those of the host rhyodacite (~0.704-0.7041), which are used to fingerprint the origin of mineral components and to monitor the mixing and mingling process. Chemical, isotopic, and textural characteristics indicate that the inclusions are hybrid magmas formed from the mixing and undercooling of recharge basaltic magma with rhyodacitic magma. All the host magma phenocrysts (biotite, plagioclase, hornblende and quartz crystals) also occur in the inclusions, where they are rimmed by reaction products. Compositional and strontium isotopic data from cores of unresorbed plagioclase crystals in the host rhyodacite, partially resorbed plagioclase crystals enclosed within basaltic andesite inclusions, and partially resorbed plagioclase crystals in the rhyodacitic host are all similar. Rim 87Sr/86Sr ratios of the partially resorbed plagioclase crystals in both inclusions and host are lower and close to those of the whole-rock hybrid basaltic andesite values. This observation indicates that some crystals originally crystallized in the silicic host, were partially resorbed and subsequently overgrown in the hybrid basaltic andesite magma, and then some of these partially resorbed plagioclase crystals were recycled back into the host rhyodacite. Textural evidence, in the form of sieve zones and major dissolution boundaries of the resorbed plagioclase crystals, indicates immersion of crystals into a hotter, more calcic magma. The occurrence of partially resorbed plagioclase together with plagioclase microlites and olivine crystals reflects disaggregation of inclusions and mingling of this material into the silicic host. These processes are commonplace in some orogenic magma systems and may be elucidated by isotopic microsampling and analysis of the plagioclases crystallizing from them.

Resorbable versus titanium plates for orthognathic surgery.

PubMed

Fedorowicz, Z; Nasser, M; Newton, J T; Oliver, R J

2007-04-18

Recognition of some of the limitations of titanium plates and screws used for the fixation of bones has led to the development of plates manufactured from bioresorbable materials. Whilst resorbable plates appear to offer clinical advantages over metal plates in orthognathic surgery, concerns remain about the stability of fixation and the length of time required for their degradation and the possibility of foreign body reactions. To compare the effectiveness of bioresorbable fixation systems with titanium systems used during orthognathic surgery. We searched the following databases: Cochrane Oral Health Group Trials Register (to 26th January 2006); the Cochrane Central Register of Controlled Trials (CENTRAL) (The Cochrane Library 2005, Issue 4); MEDLINE (without filter) (from 1966 to 26th January 2006); and EMBASE (without filter) (from 1980 to 26th January 2006). Randomised controlled trials comparing resorbable versus titanium fixation systems used for orthognathic surgery. Clinical heterogeneity between the included trials precluded pooling of data, and only a descriptive summary is presented. This review included two trials, involving 103 participants, one compared titanium with resorbable plates and screws and the other titanium with resorbable screws, both provided very limited data for the primary outcomes of this review. All patients in one trial suffered mild to moderate postoperative discomfort with no statistically significant difference between the two plating groups at different follow-up times. Mean scores of patient satisfaction were 7.43 to 8.63 (range 0 to 10) with no statistically significant difference between the two groups throughout follow up. Adverse effects reported in one study were two plate exposures in each group occurring between the third and ninth months. Plate exposures occurred mainly in the posterior maxillary region, except for one titanium plate exposure in the mandibular premolar region. Known causes of infection were associated with loosened screws and wound dehiscence with no statistically significant difference in the infection rate between titanium (3/196), and resorbable (3/165) plates P = 0.83 (published as P = 0.67). This review provides some evidence to show that there is no statistically significant difference in postoperative discomfort, level of patient satisfaction, plate exposure or infection for plate and screw fixation using either titanium or resorbable materials in orthognathic surgery.

Treatment of calvarial defects by resorbable and non-resorbable sonic activated polymer pins and mouldable titanium mesh in two dogs: a case report.

PubMed

Langer, Pierre; Black, Cameron; Egan, Padraig; Fitzpatrick, Noel

2018-06-22

To date, calvarial defects in dogs have traditionally been addressed with different types of implants including bone allograft, polymethylmethacrylate and titanium mesh secured with conventional metallic fixation methods. This report describes the use of an absorbable and non absorbable novel polymer fixation method, Bonewelding® technology, in combination with titanium mesh for the repair of calvarial defects in two dogs. The clinical outcomes and comparative complication using resorbable and non-resorbable thermoplastic pins were compared. This report of two cases documents the repair of a traumatic calvarial fracture in an adult male Greyhound and a cranioplasty following frontal bone tumor resection in an adult female Cavalier King Charles Spaniel with the use of a commercially available titanium mesh secured with an innovative thermoplastic polymer screw system (Bonewelding®). The treatment combination aimed to restore cranial structure, sinus integrity and cosmetic appearance. A mouldable titanium mesh was cut to fit the bone defect of the frontal bone and secured with either resorbable or non-resorbable polymer pins using Bonewelding® technology. Gentamycin-impregnated collagen sponge was used intraoperatively to assist with sealing of the frontal sinuses. Calvarial fracture and post-operative implant positioning were advised using computed tomography. A satisfactory restoration of skull integrity and cosmetic result was achieved, and long term clinical outcome was deemed clinically adequate with good patient quality of life. Postoperative complications including rostral mesh uplift with minor associated clinical signs were encountered when resorbable pins were used. No postoperative complications were experienced in non-resorbable pins at 7 months follow-up, by contrast mesh uplift was noted 3 weeks post-procedure in the case treated using absorbable pins. The report demonstrates the innovative use of sonic-activated polymer pins (Bonewelding® technology) alongside titanium mesh is a suitable alternative technique for skull defect repair in dogs. The use of Bonewelding® may offer advantages in reduction of surgical time. Further, ultrasonic pin application may be less invasive than alternative metallic fixation and potentially reduces bone trauma. Polymer systems may offer enhanced mesh-bone integration when compared to traditional metallic implants. The use of polymer pins demonstrates initial potential as a fixation method in cranioplasty. Initial findings in a single case comparison indicate a possible advantage in the use of non-absorbable over the absorbable systems to circumvent complications associated with variable polymer degradation, further long term studies with higher patient numbers are required before reliable conclusions can be made.

Loss of trabeculae by mechano-biological means may explain rapid bone loss in osteoporosis.

PubMed

Mulvihill, Brianne M; McNamara, Laoise M; Prendergast, Patrick J

2008-10-06

Osteoporosis is characterized by rapid and irreversible loss of trabecular bone tissue leading to increased bone fragility. In this study, we hypothesize two causes for rapid loss of bone trabeculae; firstly, the perforation of trabeculae is caused by osteoclasts resorbing a cavity so deep that it cannot be refilled and, secondly, the increases in bone tissue elastic modulus lead to increased propensity for trabecular perforation. These hypotheses were tested using an algorithm that was based on two premises: (i) bone remodelling is a turnover process that repairs damaged bone tissue by resorbing and returning it to a homeostatic strain level and (ii) osteoblast attachment is under biochemical control. It was found that a mechano-biological algorithm based on these premises can simulate the remodelling cycle in a trabecular strut where damaged bone is resorbed to form a pit that is subsequently refilled with new bone. Furthermore, the simulation predicts that there is a depth of resorption cavity deeper than which refilling of the resorption pits is impossible and perforation inevitably occurs. However, perforation does not occur by a single fracture event but by continual removal of microdamage after it forms beneath the resorption pit. The simulation also predicts that perforations would occur more easily in trabeculae that are more highly mineralized (stiffer). Since both increased osteoclast activation rates and increased mineralization have been measured in osteoporotic bone, either or both may contribute to the rapid loss of trabecular bone mass observed in osteoporotic patients.

In vitro mechanical integrity of hydroxyapatite coated magnesium alloy.

PubMed

Kannan, M Bobby; Orr, Lynnley

2011-08-01

The mechanical integrity of resorbable implants during service, especially in load bearing orthopaedic applications, is critical. The high degradation rate of resorbable magnesium and magnesium-based implants in body fluid may potentially cause premature in-service failure. In this study, a magnesium alloy (AZ91) was potentiostatically coated with hydroxyapatite at different cathodic voltages in an attempt to enhance the mechanical integrity. The mechanical integrity of the uncoated and hydroxyapatite coated alloys was evaluated after in vitro testing of the coated samples in simulated body fluid (SBF). The uncoated alloy showed 40% loss in the mechanical strength after five days exposure to SBF. However, the hydroxyapatite coated alloy exposed to SBF showed 20% improvement in the mechanical strength as compared to that of the uncoated alloy. The alloy coated potentiostatically at -2 V performed better than the -3 V coated alloy. The cross-sectional analysis of the coatings revealed relatively uniform coating thickness for the -2 V coated alloy, whereas the -3 V coated alloy exhibited areas of uneven coating. This can be attributed to the increase in hydrogen evolution on the alloy during -3 V coating as compared to -2 V coating. The scanning electron micrographs of the in vitro tested alloy revealed that hydroxyapatite coating significantly reduced the localized corrosion of the alloy, which is critical for better in-service mechanical integrity. Thus, the study suggests that the in vitro mechanical integrity of resorbable magnesium-based alloy can be improved by potentiostatic hydroxyapatite coating. © 2011 IOP Publishing Ltd

Calcium Orthophosphate-Based Bioceramics

PubMed Central

Dorozhkin, Sergey V.

2013-01-01

Various types of grafts have been traditionally used to restore damaged bones. In the late 1960s, a strong interest was raised in studying ceramics as potential bone grafts due to their biomechanical properties. A bit later, such synthetic biomaterials were called bioceramics. In principle, bioceramics can be prepared from diverse materials but this review is limited to calcium orthophosphate-based formulations only, which possess the specific advantages due to the chemical similarity to mammalian bones and teeth. During the past 40 years, there have been a number of important achievements in this field. Namely, after the initial development of bioceramics that was just tolerated in the physiological environment, an emphasis was shifted towards the formulations able to form direct chemical bonds with the adjacent bones. Afterwards, by the structural and compositional controls, it became possible to choose whether the calcium orthophosphate-based implants remain biologically stable once incorporated into the skeletal structure or whether they were resorbed over time. At the turn of the millennium, a new concept of regenerative bioceramics was developed and such formulations became an integrated part of the tissue engineering approach. Now calcium orthophosphate scaffolds are designed to induce bone formation and vascularization. These scaffolds are often porous and harbor different biomolecules and/or cells. Therefore, current biomedical applications of calcium orthophosphate bioceramics include bone augmentations, artificial bone grafts, maxillofacial reconstruction, spinal fusion, periodontal disease repairs and bone fillers after tumor surgery. Perspective future applications comprise drug delivery and tissue engineering purposes because calcium orthophosphates appear to be promising carriers of growth factors, bioactive peptides and various types of cells. PMID:28788309

Bone generation in the reconstruction of a critical size calvarial defect in an experimental model.

PubMed

Por, Yong-Chen; Barceló, C Raul; Salyer, Kenneth E; Genecov, David G; Troxel, Karen; Gendler, El; Elsalanty, Mohammed E; Opperman, Lynne A

2008-03-01

This study was designed to investigate the optimal combination of known osteogenic biomaterials with shape conforming struts to achieve calvarial vault reconstruction, using a canine model. Eighteen adolescent beagles were divided equally into 6 groups. A critical-size defect of 6 x 2 cm traversed the sagittal suture. The biomaterials used for calvarial reconstruction were demineralized perforated bone matrix (DBM), recombinant human bone morphogenetic protein 2 (rhBMP2), and autogenous platelet-rich plasma (PRP). The struts used were cobalt chrome (metal) or resorbable plate. The groupings were as follows: 1) DBM + metal, 2) DBM + PRP + metal, 3) DBM + PRP + resorbable plate, 4) DBM + rhBMP2 + metal, 5) DBM + rhBMP2 + PRP + metal, and 6) DBM + rhBMP2 + resorbable plate. Animals were killed at 3 months after surgery. There was no mortality or major complications. Analysis was performed macroscopically and histologically and with computed tomography. There was complete bony regeneration in the rhBMP2 groups only. Non-rhBMP2 groups had minimal bony ingrowth from the defect edges and on the dural surface, a finding confirmed by computed tomographic scan and histology. Platelet-rich plasma did not enhance bone regeneration. Shape conformation was good with both metal and resorbable plate. rhBMP2, but not PRP, accelerated calvarial regeneration in 3 months. The DBMs in the rhBMP2 groups were substituted by new trabecular bone. Shape molding was good with both metal and resorbable plate.

Supercritical carbon dioxide-processed resorbable polymer nanocomposites for bone graft substitute applications

NASA Astrophysics Data System (ADS)

Baker, Kevin C.

Numerous clinical situations necessitate the use of bone graft materials to enhance bone formation. While autologous and allogenic materials are considered the gold standards in the setting of fracture healing and spine fusion, their disadvantages, which include donor site morbidity and finite supply have stimulated research and development of novel bone graft substitute materials. Among the most promising candidate materials are resorbable polymers, composed of lactic and/or glycolic acid. While the characteristics of these materials, such as predictable degradation kinetics and biocompatibility, make them an excellent choice for bone graft substitute applications, they lack mechanical strength when synthesized with the requisite porous morphology. As such, porous resorbable polymers are often reinforced with filler materials. In the presented work, we describe the use of supercritical carbon dioxide (scCO2) processing to create porous resorbable polymeric constructs reinforced by nanostructured, organically modified Montmorillonite clay (nanoclay). scCO2 processing simultaneously disperses the nanoclay throughout the polymeric matrix, while imparting a porous morphology to the construct conducive to facilitating cellular infiltration and neoangiogenesis, which are necessary components of bone growth. With the addition of as little as 2.5wt% of nanoclay, the compressive strength of the constructs nearly doubles putting them on par with human cortico-cancellous bone. Rheological measurements indicate that the dominant mode of reinforcement of the nanocomposite constructs is the restriction of polymer chain mobility. This restriction is a function of the positive interaction between polymer chains and the nanoclay. In vivo inflammation studies indicate biocompatibility of the constructs. Ectopic osteogenesis assays have determined that the scCO2-processed nanocomposites are capable of supporting growth-factor induced bone formation. scCO 2-processed resorbable polymer nanocomposites composed of resorbable polymers and nanocaly exhibit physical, mechanical and biologic properties that make them excellent candidate materials for structural bone graft substitute applications.

WITHDRAWN: Resorbable versus titanium plates for facial fractures.

PubMed

Dorri, Mojtaba; Oliver, Richard

2018-05-23

Rigid internal fixation of the jaw bones is a routine procedure for the management of facial fractures. Titanium plates and screws are routinely used for this purpose. The limitations of this system has led to the development of plates manufactured from bioresorbable materials which, in some cases, omits the necessity for the second surgery. However, concerns remain about the stability of fixation and the length of time required for their degradation and the possibility of foreign body reactions. To compare the effectiveness of bioresorbable fixation systems with titanium systems for the management of facial fractures. We searched the following databases: The Cochrane Oral Health Group's Trials Register (to 20th August 2008), the Cochrane Central Register of Controlled Trials (CENTRAL) (The Cochrane Library 2008, Issue 3), MEDLINE (1950 to 20th August 2008), EMBASE (from 1980 to 20th August 2008), http://www.clinicaltrials.gov/ and http://www.controlled-trials.com (to 20th August 2008). Randomised controlled trials comparing resorbable versus titanium fixation systems used for facial fractures. Retrieved studies were independently screened by two review authors. Results were to be expressed as random-effects models using mean differences for continuous outcomes and risk ratios for dichotomous outcomes with 95% confidence intervals. Heterogeneity was to be investigated including both clinical and methodological factors. The search strategy retrieved 53 potentially eligible studies. None of the retrieved studies met our inclusion criteria and all were excluded from this review. One study is awaiting classification as we failed to obtain the full text copy. Three ongoing trials were retrieved, two of which were stopped before recruiting the planned number of participants. In one study, the excess complications in the resorbable arm was declared as the reason for stopping the trial. This review illustrates that there are no published randomised controlled clinical trials relevant to this review question. There is currently insufficient evidence for the effectiveness of resorbable fixation systems compared with conventional titanium systems for facial fractures. The findings of this review, based on the results of the aborted trials, do not suggest that resorbable plates are as effective as titanium plates. In future, the results of ongoing clinical trials may provide high level reliable evidence for assisting clinicians and patients for decision making. Trialists should design their studies accurately and comprehensively to meet the aims and objectives defined for the study.

Crystal structures of CaSiO3 polymorphs control growth and osteogenic differentiation of human mesenchymal stem cells on bioceramic surfaces.

PubMed

Zhang, Nianli; Molenda, James A; Mankoci, Steven; Zhou, Xianfeng; Murphy, William L; Sahai, Nita

2013-10-01

The repair and replacement of damaged or diseased human bone tissue requires a stable interface between the orthopedic implant and living tissue. The ideal material should be both osteoconductive (promote bonding to bone) and osteoinductive (induce osteogenic differentiation of cells and generate new bone). Partially resorbable bioceramic materials with both properties are developed by expensive trial-and-error methods. Structure-reactivity relationships for predicting the osteoinductive properties of ceramics would significantly increase the efficiency of developing materials for bone tissue engineering. Here we propose the novel hypothesis that the crystal structure of a bioceramic controls the release rates, subsequent surface modifications due to precipitation of new phases, and thus, the concentrations of soluble factors, and ultimately, the attachment, viability and osteogenic differentiation of human Mesenchymal Stem Cells (hMSCs). To illustrate our hypothesis, we used two CaSiO 3 polymorphs, pseudo-wollastonite (psw, β-CaSiO 3 ) and wollastonite (wol, α-CaSiO 3 ) as scaffolds for hMSC culture. Polymorphs are materials which have identical chemical composition and stoichiometry, but different crystal structures. We combined the results of detailed surface characterizations, including environmental Scanning Electron Microscopy (SEM) back-scattered imaging, and spot-analysis and 2D elemental mapping by SEM-Energy Dispersive X-ray (SEM-EDX), High Resolution Transmission Electron Microscopy (HRTEM) and surface roughness analysis; culture medium solution analyses; and molecular/genetic assays from cell culture. Our results confirmed the hypothesis that the psw polymorph, which has a strained silicate ring structure, is more osteoinductive than the wol polymorph, which has a more stable, open silicate chain structure. The observations could be attributed to easier dissolution (resorption) of psw compared to wol, which resulted in concentration profiles that were more osteoinductive for the former. Thus, we showed that crystal structure is a fundamental parameter to be considered in the intelligent design of pro-osteogenic, partially resorbable bioceramics.

Bone Tumor Environment as a Potential Therapeutic Target in Ewing Sarcoma

PubMed Central

Redini, Françoise; Heymann, Dominique

2015-01-01

Ewing sarcoma is the second most common pediatric bone tumor, with three cases per million worldwide. In clinical terms, Ewing sarcoma is an aggressive, rapidly fatal malignancy that mainly develops not only in osseous sites (85%) but also in extra-skeletal soft tissue. It spreads naturally to the lungs, bones, and bone marrow with poor prognosis in the two latter cases. Bone lesions from primary or secondary (metastases) tumors are characterized by extensive bone remodeling, more often due to osteolysis. Osteoclast activation and subsequent bone resorption are responsible for the clinical features of bone tumors, including pain, vertebral collapse, and spinal cord compression. Based on the “vicious cycle” concept of tumor cells and bone resorbing cells, drugs, which target osteoclasts, may be promising agents as adjuvant setting for treating bone tumors, including Ewing sarcoma. There is also increasing evidence that cellular and molecular protagonists present in the bone microenvironment play a part in establishing a favorable “niche” for tumor initiation and progression. The purpose of this review is to discuss the potential therapeutic value of drugs targeting the bone tumor microenvironment in Ewing sarcoma. The first part of the review will focus on targeting the bone resorbing function of osteoclasts by means of bisphosphonates or drugs blocking the pro-resorbing cytokine receptor activator of NF-kappa B ligand. Second, the role of this peculiar hypoxic microenvironment will be discussed in the context of resistance to chemotherapy, escape from the immune system, or neo-angiogenesis. Therapeutic interventions based on these specificities could be then proposed in the context of Ewing sarcoma. PMID:26779435

Bone Tumor Environment as a Potential Therapeutic Target in Ewing Sarcoma.

PubMed

Redini, Françoise; Heymann, Dominique

2015-01-01

Ewing sarcoma is the second most common pediatric bone tumor, with three cases per million worldwide. In clinical terms, Ewing sarcoma is an aggressive, rapidly fatal malignancy that mainly develops not only in osseous sites (85%) but also in extra-skeletal soft tissue. It spreads naturally to the lungs, bones, and bone marrow with poor prognosis in the two latter cases. Bone lesions from primary or secondary (metastases) tumors are characterized by extensive bone remodeling, more often due to osteolysis. Osteoclast activation and subsequent bone resorption are responsible for the clinical features of bone tumors, including pain, vertebral collapse, and spinal cord compression. Based on the "vicious cycle" concept of tumor cells and bone resorbing cells, drugs, which target osteoclasts, may be promising agents as adjuvant setting for treating bone tumors, including Ewing sarcoma. There is also increasing evidence that cellular and molecular protagonists present in the bone microenvironment play a part in establishing a favorable "niche" for tumor initiation and progression. The purpose of this review is to discuss the potential therapeutic value of drugs targeting the bone tumor microenvironment in Ewing sarcoma. The first part of the review will focus on targeting the bone resorbing function of osteoclasts by means of bisphosphonates or drugs blocking the pro-resorbing cytokine receptor activator of NF-kappa B ligand. Second, the role of this peculiar hypoxic microenvironment will be discussed in the context of resistance to chemotherapy, escape from the immune system, or neo-angiogenesis. Therapeutic interventions based on these specificities could be then proposed in the context of Ewing sarcoma.

Method of coating a substrate with a calcium phosphate compound

DOEpatents

Gao, Yufei; Campbell, Allison A.

2000-01-01

The present invention is a method of coating a substrate with a calcium phosphate compound using plasma enhanced MOCVD. The substrate is a solid material that may be porous or non-porous, including but not limited to metal, ceramic, glass and combinations thereof. The coated substrate is preferably used as an implant, including but not limited to orthopaedic, dental and combinations thereof. Calcium phosphate compound includes but is not limited to tricalcium phosphate (TCP), hydroxyapatite (HA) and combinations thereof. TCP is preferred on a titanium implant when implant resorbability is desired. HA is preferred when the bone bonding of new bone tissue into the structure of the implant is desired. Either or both of TCP and/or HA coated implants may be placed into a solution with an agent selected from the group of protein, antibiotic, antimicrobial, growth factor and combinations thereof that can be adsorbed into the coating before implantation. Once implanted, the release of TCP will also release the agent to improve growth of new bone tissues and/or to prevent infection.

Do pregnant lizards resorb or abort inviable eggs and embryos? Morphological evidence from an Australian skink, Pseudemoia pagenstecheri.

PubMed

Blackburn, Daniel G; Weaber, Kera K; Stewart, James R; Thompson, Michael B

2003-05-01

Although pregnant viviparous squamates are sometimes claimed to be able to resorb inviable eggs and embryos from the uterus, definitive evidence for such resorption is not available. After placing pregnant female Pseudemoia pagenstecheri into conditions under which embryonic development is terminated, we periodically harvested the gravid oviducts and examined them histologically. Females contained abnormal and degenerating eggs and embryos that had died in various stages of development. Dead embryos had undergone extensive cytolysis, dissolution, and aseptic necrosis and vitelline masses showed signs of deterioration and passage down the oviduct. The uterine mucosa lay in direct contact with the vitelline material, with no intact shell membrane intervening between them. Yolk was sometimes displaced into the exocoelom and allantoic cavity due to rupture of the extraembryonic membranes. Histological examination revealed no evidence of the uptake of yolk by the uterine epithelium or its accumulation in the subepithelial connective tissue. In many specimens, the uterine epithelium showed minuscule, apical granules. The position, appearance, and staining properties of the granules suggests them to be secretory, a manifestation of placentotrophy. Our observations indicate that P. pagenstecheri females retain dead eggs and embryos for several weeks or longer, yet do not resorb them during that period. This lizard is the second placentotrophic skink species in which resorption has been suspected, but in which abortive eggs appear to be retained or extruded instead of being resorbed by the oviducts. Researchers should not assume that squamates can digest and resorb oviductal eggs without definitive morphological evidence. Copyright 2003 Wiley-Liss, Inc.

A resorbable and rapid method for maxillomandibular fixation in pediatric mandible fractures.

PubMed

Eppley, B L

2000-05-01

Maxillomandibular immobilization in pediatric mandible fractures is accomplished through a resorbable screw placed into the zygomatic body to which is attached a large, monofilament, circummandibular suture. Although the screw must be placed intraoperatively, this method of jaw immobilization is rapid, secure, does not damage the teeth, and can be removed in the office in the older child.

The use of resorbable hardware for fixation of pediatric mandible fracture. Case report.

PubMed

Poore, Matthew C; Penna, Kevin J

2008-01-01

The diagnosis and management of mandible fractures in the pediatric patient population can pose multiple challenges to the oral and maxillofacial surgeon. Resorbable plates and screws for fixation in this population are both well tolerated and effective. They enable realignment and stable positioning of rapidly healing fracture segments, while obviating any potential impediments to long-term metal retention.

Use of Resorbable Fixation System in Pediatric Facial Fractures.

PubMed

Wong, Frankie K; Adams, Saleigh; Hudson, Donald A; Ozaki, Wayne

2017-05-01

Resorbable fixation system (RFS) is an alternative to titanium in open reduction and internal fixation of pediatric facial fractures. This study retrospectively reviewed all medical records in a major metropolitan pediatric hospital in Cape Town, South Africa from September 2010 through May 2014. Inclusion criteria were children under the age of 13 with facial fractures who have undergone open reduction and internal fixation using RFS. Intraoperative and postoperative complications were reviewed. A total of 21 patients were included in this study. Twelve were males and 9 were females. Good dental occlusion was achieved in all patients and there were no complications intraoperatively. Three patients developed postoperative implanted-related complications: all 3 patients developed malocclusions and 1 developed an additional sterile abscess over the right zygomatic bone. For the latter, incision and drainage was performed and the problem resolved without additional operations. Resorbable fixation system is an alternative to titanium products in the setting of pediatric facial fractures without complications involving delayed union or malunion. The combination of intermaxillary fixation and RFS is not needed postoperatively for adequate fixation of mandible fractures. Resorbable fixation system is able to provide adequate internal fixation when both low-stress and high-stress craniofacial fractures occur simultaneously.

Posterior lumbar interbody fusion using non resorbable poly-ether-ether-ketone versus resorbable poly-L-lactide-co-D,L-lactide fusion devices. Clinical outcome at a minimum of 2-year follow-up.

PubMed

Jiya, Timothy U; Smit, T; van Royen, B J; Mullender, M

2011-04-01

Previous papers on resorbable poly-L-lactide-co-D,L-lactide (PLDLLA) cages in spinal fusion have failed to report adequately on patient-centred clinical outcome measures. Also comparison of PLDLLA cage with a traditionally applicable counterpart has not been previously reported. This is the first randomized prospective study that assesses clinical outcome of PLDLLA cage compared with a poly-ether-ether-ketone (PEEK) implant. Twenty-six patients were randomly assigned to undergo instrumented posterior lumbar interbody fusion (PLIF) whereby either a PEEK cage or a PLDLLA cage was implanted. Clinical outcome based on visual analogue scale scores for leg pain and back pain, as well as Oswestry Disability Index (ODI) and SF-36 questionnaires were documented and analysed. When compared with preoperative values, all clinical parameters have significantly improved in the PEEK group at 2 years after surgery with the exception of SF-36 general health, SF-36 mental health and SF-36 role emotional scores. No clinical parameter showed significant improvement at 2 years after surgery compared with preoperative values in the PLDLLA patient group. Only six patients (50%) in the PLDLLA group showed improvement in the VAS scores for leg and back pain as well as the ODI, as opposed to 10 patients (71%) in the PEEK group. One-third of the patients in the PLDLLA group actually reported worsening of their pain scores and ODI. Three cases of mild to moderate osteolysis were seen in the PLDLLA group. Following up on our preliminary report, these 2-year results confirm the superiority of the PEEK implant to the resorbable PLDLLA implant in aiding spinal fusion and alleviating symptoms following PLIF in patients with degenerative spondylolisthesis associated with either canal stenosis or foramen stenosis or both and emanating from a single lumbar segment.

Comparison of strains produced by titanium and poly D, L-lactide Acid plating systems to in vitro forces.

PubMed

Chacon, Guillermo E; Dillard, Frederick Matt; Clelland, Nancy; Rashid, Robert

2005-07-01

To determine if a specific resorbable plating system provides similar fixation, in terms of strain distribution under load, to a titanium system when the Champy technique is applied for the treatment of a mandibular angle fracture. A formalin-fixed cadaver mandible was harvested just before the study. A bicortical osteotomy was then made using a diamond disc extending in an oblique direction in the area of the angle. It was then passively fixated with a 4-hole 2.0-mm miniplate. Two stacked rosette strain gauges were bonded to the mandible on either side of the fracture. Each rosette had 3 strain gauges arranged in specific degrees relative to each other. The mandible was then placed on a dynanometer and 30 lb loads were delivered on the ipsilateral molar. Static resistance was placed in the condylar neck region to simulate the glenoid fossa. Loading was repeated 10 times with a period of 3 minutes between loads. Measurements were recorded for each strain gauge after loads were in place for 30 seconds. The same process was repeated using a 4-hole 2.1-mm resorbable miniplate. The strains were then used to calculate the maximum and minimum strains for each rosette. Hooke's law was used to calculate the principal stresses. Differences were observed between the strain gauges for each individual plating system. There was variability within the resorbable plate measurements as shown by the standard deviation. Using the REML ANOVA test, a significant difference was found between the 2 materials. In this in vitro study, there were significant biomechanical differences observed between a 2.0-mm titanium miniplate and a 2.1-mm resorbable miniplate when used to treat a mandibular angle fracture following Champy's principles. Based on our finding, both systems cannot be used interchangeably for the treatment of mandibular angle fractures under the same clinical conditions.

Holding fast.

PubMed

Gourville, John T

2005-06-01

CEO Peter Walsh faces a classic innovator's dilemma. His company, Crescordia, produces high-quality metal plates, pins, and screws that orthopedic surgeons use to repair broken bones. In fact, because the company has for decades refused to compromise on quality, there are orthopedic surgeons who use nothing but Crescordia hardware. And now these customers have begun to clamor for the next generation technology: resorbable hardware. Resorbables offer clear advantages over the traditional hardware. Like dissolving sutures, resorbable plates and screws are made of biodegradable polymers. They hold up long enough to support a healing bone, then gradually and harmlessly disintegrate in the patient's body. Surgeons are especially looking forward to using resorbables on children, so kids won't have to undergo a second operation to remove the old hardware after their bones heal, a common procedure in pediatrics. The new products, however, are not yet reliable; they fail about 8% of the time, sometimes disintegrating before the bone completely heals and sometimes not ever fully disintegrating. That's why Crescordia, mindful of its hard-earned reputation, has delayed launching a line using the new technology. But time is running out. A few competitors have begun to sell resorbables despite their imperfections, and these companies are picking up market share. Should Crescordia join the fray and risk tarnishing its brand? Or should the company sit tight until it can offer a perfect product? Commenting on this fictional case study are Robert A. Lutz, vice chairman of product development at General Motors; Clayton M. Christensen, the Robert and Jane Cizik Professor of Business Administration at Harvard Business School; Jason Wittes, a senior equity analyst covering medical supplies and devices at Leerink Swann; and Nick Galakatos, a general partner of MPM Capital.

Apical extrusion of debris in primary molar root canals using mechanical and manual systems.

PubMed

Buldur, B; Hascizmeci, C; Aksoy, S; Nur Aydin, M; Guvendi, O N

2018-03-01

Apical extrusion of debris in primary root canal treatment has not been well elucidated. The purpose of this study is to compare the amount of apically extruded debris during the preparation of primary molar root canals using ProTaper, ProTaper Next, Self-adjusting File (SAF) and hand files. One hundred sixty extracted primary mandibular molar teeth were assigned to 2 groups: Group 1: Resorbed (n=80) and Group 2: Non-resorbed (n=80) and randomly to four subgroups (n=20 teeth for each subgroup) according to the instruments used, ProTaper, ProTaper Next, SAF, and hand file. The apically extruded debris was collected and dried in preweighed Eppendof tubes. The dry weight was calculated by subtracting the preoperative weight from the postoperative weight. Data were analysed statistically using the ANOVA and the Bonferroni post hoc t-test. The amount of apically extruded debris was significantly less for the non-resorbed group compared to the resorbed group (P<0.05). Regardless of the resorption groups, ProTaper Next and SAF extruded significantly less debris than did the ProTaper and hand files (P<0.05), while no statistically significant difference was found between ProTaper Next and SAF (P>0.05). All instruments caused apically extruded debris in primary teeth.

Computer-assisted virtual technology in intracapsular condylar fracture with two resorbable long-screws.

PubMed

Wang, W H; Deng, J Y; Zhu, J; Li, M; Xia, B; Xu, B

2013-03-01

Our aim was to fix intracapsular condylar fractures (ICF) with two resorbable long screws using preoperative computer-assisted virtual technology. From February 2008 to July 2011, 19 patients with ICF were treated with two resorbable long screws. Preoperatively we took panoramic radiographs and spiral computed tomography (CT). Depending on their digital imaging and communications in medicine (DICOM) data, the dislocated condylar segments were restored using the SimPlant Pro™ software, version 11.04. The mean (SD) widths of the condylar head and neck from lateral to medial were 19.01 (1.28)mm and 13.84 (1.13)mm, respectively. In all patients, the mandibles and the ICF seen intraoperatively corresponded with the preoperative three-dimensional and virtual reposition. All patients were followed up for 6-46 months (mean 21). Occlusion and mouth opening had been restored completely in all but one patient, and absolute anatomical reduction was also achieved in most cases. Computer-assisted virtual technology plays an important part in the diagnosis of ICF, as well as in its preoperative design. Fixation with only two resorbable long screws is an effective and reliable method for fixing ICF. Copyright © 2012 The British Association of Oral and Maxillofacial Surgeons. Published by Elsevier Ltd. All rights reserved.

[Guided bone regeneration: general survey].

PubMed

Cosyn, Jan; De Bruyn, Hugo

2009-01-01

The principle of 'guided bone regeneration' was first described in 1988 on the basis of animal-experimental data. Six weeks after transmandibular defects had been created and protected by non-resorbable teflonmembranes, complete bone regeneration was found. The technique was based on the selective repopulation of the wound: every infiltration of cells outside the neighbouring bone tissue was prevented by the application of the membrane. Additional animal experiments showed that guided bone regeneration was a viable treatment option for local bone defects surrounding dental implants. Clinical practice, however, showed that premature membrane exposure was a common complication, which was responsible for a tremendous reduction in regenerated bone volume. In addition, a second surgical intervention was always necessary to remove the membrane. As a result, resorbable alternatives were developed. Since these are less rigid, bone fillers are usually used simultaneously. These comprise autogenous bone chips and bone substitutes from allogenic or xenogenic origine. Also alloplastic materials could be used for this purpose. Based on their characteristics this article provides an overview of the biomaterials that could be considered for guided bone regeneration. Specific attention goes to their application in clinical practice.

The friction and wear of ceramic/ceramic and ceramic/metal combinations in sliding contact

NASA Technical Reports Server (NTRS)

Sliney, Harold E.; Dellacorte, Christopher

1993-01-01

The tribological characteristics of ceramics sliding on ceramics are compared to those of ceramics sliding on a nickel based turbine alloy. The friction and wear of oxide ceramics and silicon-based ceramics in air at temperatures from room ambient to 900 C (in a few cases to 1200 C) were measured for a hemispherically-tipped pin on a flat sliding contact geometry. In general, especially at high temperature, friction and wear were lower for ceramic/metal combinations than for ceramic/ceramic combinations. The better tribological performance for ceramic/metal combinations is attributed primarily to the lubricious nature of the oxidized surface of the metal.

Enhanced Actuation Performance and Reduced Heat Generation in Shear-Bending Mode Actuator at High Temperature.

PubMed

Chen, Jianguo; Liu, Guoxi; Cheng, Jinrong; Dong, Shuxiang

2016-08-01

The actuation performance, strain hysteresis, and heat generation of the shear-bending mode actuators based on soft and hard BiScO3-PbTiO3 (BS-PT) ceramics were investigated under different thermal (from room temperature to 300 °C) and electrical loadings (from 2 to 10 kV/cm and from 1 to 1000 Hz). The actuator based on both soft and hard BS-PT ceramics worked stably at the temperature as high as 300 °C. The maximum working temperature of this shear-bending actuators is 150 °C higher than those of the traditional piezoelectric actuators based on commercial Pb(Zr, Ti)O3 materials. Furthermore, although the piezoelectric properties of soft-type ceramics based on BS-PT ceramics were superior to those of hard ceramics, the maximum displacement of the actuator based on hard ceramics was larger than that fabricated by soft ceramics at high temperature. The maximum displacement of the actuator based on hard ceramics was [Formula: see text] under an applied electric field of 10 kV/cm at 300 °C. The strain hysteresis and heat generation of the actuator based on hard ceramics was smaller than those of the actuator based on soft ceramics in the wide temperature range. These results indicated that the shear-bending actuator based on hard piezoelectric ceramics was more suitable for high-temperature piezoelectric applications.

Quantitative evaluation of bone resorption activity of osteoclast-like cells by measuring calcium phosphate resorbing area using incubator-facilitated and video-enhanced microscopy.

PubMed

Morimoto, Yoshitaka; Hoshino, Hironobu; Sakurai, Takashi; Terakawa, Susumu; Nagano, Akira

2009-04-01

Quantitative evaluation of the ability of bone resorption activity in live osteoclast-like cells (OCLs) has not yet been reported on. In this study, we observed the sequential morphological change of OCLs and measured the resorbing calcium phosphate (CP) area made by OCLs alone and with the addition of elcatonin utilizing incubator facilitated video-enhanced microscopy. OCLs, which were obtained from a coculture of ddy-mouse osteoblastic cells and bone marrow cells, were cultured on CP-coated quartz cover slips. The CP-free area increased constantly in the OCLs alone, whereas it did not increase after the addition of elcatonin. This study showed that analysis of the resorbed areas under the OCL body using this method enables the sequential quantitative evaluation of the bone resorption activity and the effect of several therapeutic agents on bone resorption in vitro.

Challenges and Opportunities in Design, Fabrication, and Testing of High Temperature Joints in Ceramics and Ceramic Composites

NASA Technical Reports Server (NTRS)

Singh, M.; Levine, S. R. (Technical Monitor)

2001-01-01

Ceramic joining has been recognized as an enabling technology for successful utilization of advanced ceramics and composite materials. A number of joint design and testing issues have been discussed for ceramic joints in silicon carbide-based ceramics and fiber-reinforced composites. These joints have been fabricated using an affordable, robust ceramic joining technology (ARCJoinT). The microstructure and good high temperature mechanical capability (compressive and flexural strengths) of ceramic joints in silicon carbide-based ceramics and composite materials are reported.

Ceramic Defects in Metal-Ceramic Fixed Dental Prostheses Made from Co-Cr and Au-Pt Alloys: A Retrospective Study.

PubMed

Mikeli, Aikaterini; Boening, Klaus W; Lißke, Benjamin

2015-01-01

Ceramic defects in porcelain-fused-to-metal (PFM) restorations may depend on framework alloy type. This study assessed ceramic defects on cobalt-chromium- (Co-Cr-) and gold-platinum- (Au-Pt-) based PFM restorations. In this study, 147 Co-Cr-based and 168 Au-Pt-based PFM restorations inserted between 1998 and 2010 (139 patients) were examined for ceramic defects. Detected defects were assigned to three groups according to clinical defect relevance. Ceramic defect rates (Co-Cr-based: 12.9%; Au-Pt-based: 7.2%) revealed no significant difference but a strong statistical trend (U test, P = .082). Most defects were of little clinical relevance. Co-Cr PFM restorations may be at higher risk for ceramic defects compared to Au-Pt-based restorations.

Clinically used adhesive ceramic bonding methods: a survey in 2007, 2011, and in 2015.

PubMed

Klosa, K; Meyer, G; Kern, M

2016-09-01

The objective of the study is to evaluate practices of dentists regarding adhesive cementation of all-ceramic restorations over a period of 8 years. The authors developed a questionnaire regarding adhesive cementation procedures for all-ceramic restorations. Restorations were distinguished between made out of silicate ceramic or oxide ceramic. The questionnaire was handed out to all dentists participating in a local annual dental meeting in Northern Germany. The returned questionnaires were analyzed to identify incorrect cementation procedures based upon current evidence-based technique from the scientific dental literature. The survey was conducted three times in 2007, 2011, and 2015 and their results were compared. For silicate ceramic restorations, 38-69 % of the participants used evidence-based bonding procedures; most of the incorrect bonding methods did not use a silane containing primer. In case of oxide ceramic restorations, most participants did not use air-abrasion prior to bonding. Only a relatively low rate (7-14 %) of dentists used evidence-based dental techniques for bonding oxide ceramics. In adhesive cementation of all-ceramic restorations, the practices of surveyed dentists in Northern Germany revealed high rates of incorrect bonding. During the observation period, the values of evidence-based bonding procedures for oxide ceramics improved while the values for silicate ceramics declined. Based on these results, some survey participants need additional education for adhesive techniques. Neglecting scientifically accepted methods for adhesive cementation of all-ceramic restorations may result in reduced longevity of all-ceramic restorations.

The use of resorbable plates in association with dental arch stabilization in the treatment of mandibular fractures in children.

PubMed

Li, Zhi; David, Ongodia; Li, Zu-Bing

2014-07-01

The purpose of this study was to investigate the effect of resorbable plate fixation in association with dental arch stabilization in the treatment of displaced mandibular fractures in children. Thirteen children (5 girls and 8 boys, age range 2 years 5 months to 12 years 2 months) with displaced mandibular fractures were included in this case series. Open reduction by intraoral approach was performed on these patients, and the fractures were fixed using resorbable plates and monocortical screws placed at the lower border of the mandible. At the same time, an arch bar or orthodontic wire splint was anchored using stainless steel wires or resin on the teeth to stabilize the whole mandibular dental arch. Postoperatively, follow-up was undertaken to evaluate the fracture healing, mandible movement, and mandible growth. Postoperatively, all patients achieved uneventful healing; premorbid occlusion restoration and wound healing were achieved, along with unimpaired function and normal growth and development of the mandible. Complications such as damage to tooth buds, infection, malunion, and nonunion were not encountered in these patients. Resorbable plates use in association with dental arch stabilization can provide good stabilization for mandibular fractures and is a promising approach for the treatment of displaced mandibular fractures in children. Copyright © 2013 European Association for Cranio-Maxillo-Facial Surgery. Published by Elsevier Ltd. All rights reserved.

The effect of osteotomy dimension on osseointegration to resorbable media-treated implants: a study in the sheep.

PubMed

Galli, Silvia; Jimbo, Ryo; Tovar, Nick; Yoo, Daniel Y; Anchieta, Rodolfo B; Yamaguchi, Satoshi; Coelho, Paulo G

2015-03-01

The drilling technique and the surface characteristics are known to influence the healing times of oral implants. The influence of osteotomy dimension on osseointegration of microroughned implant surfaces treated with resorbable blasting media was tested in an in vivo model. Ninety-six implants (ø4.5 mm, 8 mm in length) with resorbable blasting media-treated surfaces were placed in the ileum of six sheep. The final osteotomy diameters were 4.6 mm (reamer), 4.1 mm (loose), 3.7 mm (medium), and 3.2 mm (tight). After three and six weeks of healing, the implants were biomechanically tested and histologically evaluated. Statistical analysis was performed using Page L trend test for ordered and paired sample and linear regression, with significance level at p < 0.05. An overall increase in all dependent variables was observed with the reduction of osteotomy diameter. In addition, all osseointegration scores increased over time. At three weeks, the retention was significantly higher for smaller osteotomies. The histological sections depicted intimate contact of bone with all the implant surfaces and osteoblast lines were visible in all sections. The resorbable blasting media microroughed surfaces achieved successful osseointegration for all the instrumentation procedures tested, with higher osseointegration scores for the high insertion torque group. © The Author(s) 2014 Reprints and permissions: sagepub.co.uk/journalsPermissions.nav.

Laser-deposited thin films of biocompatible ceramic

NASA Astrophysics Data System (ADS)

Jelinek, Miroslav; Olsan, V.; Jastrabik, Lubomir; Dostalova, Tatjana; Himmlova, Lucia; Kadlec, Jaromir; Pospichal, M.; Simeckova, M.; Fotakis, Costas

1995-03-01

Thin films of biocompatible materials such as hydroxylapatite (HA) - Ca10 (PO4)6(OH)2 were deposited by laser ablation technique. The films of HA were created on Ti substrates by KrF laser. The layers were deposited in vacuum, in pure H2O vapors (pressure 2 X 10-3 mbar - 2 X 10-1 mbar), and in Ar/H2O vapor mixture. Influence of laser energy density ET (3 Jcm-2, 13 Jcm-2) and substrate temperature Tg (500 degree(s)C - 760 degree(s)C) on the film parameters was studied. Two different technological processes were used for HA target preparation. Films and targets were characterized by Rutherford backscattering analysis (RBS), particle induced x-ray emission (PIXE), x-ray diffraction (XRD), scanning electron microscopy (SEM) and by Knoop microhardness and scratch test. The best crystalline HA films were reached in the mixture of Ar/H2O. Higher Tg had to be used for such deposition. Higher Tg was also preferable from the point of film microhardness. Adhesion of films to the substrates in the range of tens of Newtons was measured. The preliminary results of in vitro experiments of films biotolerance and resorbability are also presented.

Silver-hafnium braze alloy

DOEpatents

Stephens, Jr., John J.; Hosking, F. Michael; Yost, Frederick G.

2003-12-16

A binary allow braze composition has been prepared and used in a bonded article of ceramic-ceramic and ceramic-metal materials. The braze composition comprises greater than approximately 95 wt % silver, greater than approximately 2 wt % hafnium and less than approximately 4.1 wt % hafnium, and less than approximately 0.2 wt % trace elements. The binary braze alloy is used to join a ceramic material to another ceramic material or a ceramic material, such as alumina, quartz, aluminum nitride, silicon nitride, silicon carbide, and mullite, to a metal material, such as iron-based metals, cobalt-based metals, nickel-based metals, molybdenum-based metals, tungsten-based metals, niobium-based metals, and tantalum-based metals. A hermetic bonded article is obtained with a strength greater than 10,000 psi.

Process for strengthening silicon based ceramics

DOEpatents

Kim, Hyoun-Ee; Moorhead, A. J.

1993-01-01

A process for strengthening silicon based ceramic monolithic materials and omposite materials that contain silicon based ceramic reinforcing phases that requires that the ceramic be exposed to a wet hydrogen atmosphere at about 1400.degree. C. The process results in a dense, tightly adherent silicon containing oxide layer that heals, blunts , or otherwise negates the detrimental effect of strength limiting flaws on the surface of the ceramic body.

Process for strengthening silicon based ceramics

DOEpatents

Kim, Hyoun-Ee; Moorhead, A. J.

1993-04-06

A process for strengthening silicon based ceramic monolithic materials and omposite materials that contain silicon based ceramic reinforcing phases that requires that the ceramic be exposed to a wet hydrogen atmosphere at about 1400.degree. C. The process results in a dense, tightly adherent silicon containing oxide layer that heals, blunts , or otherwise negates the detrimental effect of strength limiting flaws on the surface of the ceramic body.

Comparison of morphological changes in efferent lymph nodes after implantation of resorbable and non-resorbable implants in rabbits

PubMed Central

2011-01-01

Background Magnesium alloys as biodegradable implant materials received much interest in recent years. It is known that products of implant degradation can induce several types of immune response. Hence, the aim of this study was to examine the morphological changes of efferent lymph nodes after implantation of different resorbable magnesium alloys (MgCa0.8, LAE442) in comparison to commercially available resorbable (PLA) and non-resorbable (titanium) implant materials as well as control groups without implant material. Methods The different implant materials were inserted intramedullary into the rabbit tibia. After postoperative observation periods of three and six months, popliteal lymph nodes were examined histologically and immunhistologically and compared to lymph nodes of sham operated animals and animals without surgery. Haematoxylin and eosin staining was performed for cell differentiation. Mouse anti-CD79α and rat anti-CD3 monoclonal primary antibodies were used for B- and T-lymphocyte detection, mouse anti-CD68 primary antibodies for macrophage detection. Evaluation of all sections was performed applying a semi quantitative score. Results The histological evaluation demonstrated low and moderate levels of morphological changes for both magnesium alloys (LAE442 and MgCa0.8). Higher than moderate values were reached for titanium in sinus histiocytosis and histiocytic apoptosis (3 months) and for PLA in histiocytic apoptosis (3 and 6 months). The immune response to all investigated implants had a non-specific character and predominantly was a foreign-body reaction. LAE442 provoked the lowest changes which might be due to a lower degradation rate in comparison to MgCa0.8. Therewith it is a promising candidate for implants with low immunogenic potential. Conclusion Both examined magnesium alloys did not cause significantly increased morphological changes in efferent lymph nodes in comparison to the widely used implant materials titanium and PLA. LAE442 induced even lower immunological reactions. Therewith MgCa0.8 and especially LAE442 are appropriate candidates for biomedical use. PMID:21521497

Divergent Resorbability and Effects on Osteoclast Formation of Commonly Used Bone Substitutes in a Human In Vitro-Assay

PubMed Central

Busse, Björn; Schilling, Arndt F.; Schinke, Thorsten; Amling, Michael; Lange, Tobias

2012-01-01

Bioactive bone substitute materials are a valuable alternative to autologous bone transplantations in the repair of skeletal defects. However, clinical studies have reported varying success rates for many commonly used biomaterials. While osteoblasts have traditionally been regarded as key players mediating osseointegration, increasing evidence suggests that bone-resorbing osteoclasts are of crucial importance for the longevity of applied biomaterials. As no standardized data on the resorbability of biomaterials exists, we applied an in vitro-assay to compare ten commonly used bone substitutes. Human peripheral blood mononuclear cells (PBMCs) were differentiated into osteoclasts in the co-presence of dentin chips and biomaterials or dentin alone (control) for a period of 28 days. Osteoclast maturation was monitored on day 0 and 14 by light microscopy, and material-dependent changes in extracellular pH were assessed twice weekly. Mature osteoclasts were quantified using TRAP stainings on day 28 and their resorptive activity was determined on dentin (toluidin blue staining) and biomaterials (scanning electron microscopy, SEM). The analyzed biomaterials caused specific changes in the pH, which were correlated with osteoclast multinuclearity (r = 0.942; p = 0.034) and activity on biomaterials (r = 0.594; p = 0.041). Perossal led to a significant reduction of pH, nuclei per osteoclast and dentin resorption, whereas Tutogen bovine and Tutobone human strikingly increased all three parameters. Furthermore, natural biomaterials were resorbed more rapidly than synthetic biomaterials leading to differential relative resorption coefficients, which indicate whether bone substitutes lead to a balanced resorption or preferential resorption of either the biomaterial or the surrounding bone. Taken together, this study for the first time compares the effects of widely used biomaterials on osteoclast formation and resorbability in an unbiased approach that may now aid in improving the preclinical evaluation of bone substitute materials. PMID:23071629

Reconstructive periodontal therapy with simultaneous ridge augmentation. A clinical and histological case series report.

PubMed

Windisch, Péter; Szendroi-Kiss, Dóra; Horváth, Attila; Suba, Zsuzsanna; Gera, István; Sculean, Anton

2008-09-01

Treatment of intrabony periodontal defects with a combination of a natural bone mineral (NBM) and guided tissue regeneration (GTR) has been shown to promote periodontal regeneration in intrabony defects. In certain clinical situations, the teeth presenting intrabony defects are located at close vicinity of the resorbed alveolar ridge. In these particular cases, it is of clinical interest to simultaneously reconstruct both the intrabony periodontal defect and the resorbed alveolar ridge, thus allowing insertion of endosseous dental implants. The aim of the present study was to present the clinical and histological results obtained with a new surgical technique designed to simultaneously reconstruct the intrabony defect and the adjacently located resorbed alveolar ridge. Eight patients with chronic advanced periodontitis displaying intrabony defects located in the close vicinity of resorbed alveolar ridges were consecutively enrolled in the study. After local anesthesia, mucoperiosteal flaps were raised, the granulation tissue removed, and the roots meticulously scaled and planed. A subepithelial connective tissue graft was harvested from the palate and sutured to the oral flap. The intrabony defect and the adjacent alveolar ridge were filled with a NBM and subsequently covered with a bioresorbable collagen membrane (GTR). At 11-20 months (mean, 13.9+/-3.9 months) after surgery, implants were placed, core biopsies retrieved, and histologically evaluated. Mean pocket depth reduction measured 3.8+/-1.7 mm and mean clinical attachment level gain 4.3+/-2.2 mm, respectively. Reentry revealed in all cases a complete fill of the intrabony component and a mean additional vertical hard tissue gain of 1.8+/-1.8 mm. The histologic evaluation indicated that most NBM particles were surrounded by bone. Mean new bone and mean graft area measured 17.8+/-2.8% and 32.1+/-8.3%, respectively. Within their limits, the present findings indicate that the described surgical approach may be successfully used in certain clinical cases to simultaneously treat intrabony defects and to reconstruct the resorbed alveolar ridge.

Potassium Sodium Niobate-Based Lead-Free Piezoelectric Multilayer Ceramics Co-Fired with Nickel Electrodes.

PubMed

Kawada, Shinichiro; Hayashi, Hiroyuki; Ishii, Hideki; Kimura, Masahiko; Ando, Akira; Omiya, Suetake; Kubodera, Noriyuki

2015-11-03

Although lead-free piezoelectric ceramics have been extensively studied, many problems must still be overcome before they are suitable for practical use. One of the main problems is fabricating a multilayer structure, and one solution attracting growing interest is the use of lead-free multilayer piezoelectric ceramics. The paper reviews work that has been done by the authors on lead-free alkali niobate-based multilayer piezoelectric ceramics co-fired with nickel inner electrodes. Nickel inner electrodes have many advantages, such as high electromigration resistance, high interfacial strength with ceramics, and greater cost effectiveness than silver palladium inner electrodes. However, widely used lead zirconate titanate-based ceramics cannot be co-fired with nickel inner electrodes, and silver palladium inner electrodes are usually used for lead zirconate titanate-based piezoelectric ceramics. A possible alternative is lead-free ceramics co-fired with nickel inner electrodes. We have thus been developing lead-free alkali niobate-based multilayer ceramics co-fired with nickel inner electrodes. The normalized electric-field-induced thickness strain ( S max / E max ) of a representative alkali niobate-based multilayer ceramic structure with nickel inner electrodes was 360 pm/V, where S max denotes the maximum strain and E max denotes the maximum electric field. This value is about half that for the lead zirconate titanate-based ceramics that are widely used. However, a comparable value can be obtained by stacking more ceramic layers with smaller thicknesses. In the paper, the compositional design and process used to co-fire lead-free ceramics with nickel inner electrodes are introduced, and their piezoelectric properties and reliabilities are shown. Recent advances are introduced, and future development is discussed.

Potassium Sodium Niobate-Based Lead-Free Piezoelectric Multilayer Ceramics Co-Fired with Nickel Electrodes

PubMed Central

Kawada, Shinichiro; Hayashi, Hiroyuki; Ishii, Hideki; Kimura, Masahiko; Ando, Akira; Omiya, Suetake; Kubodera, Noriyuki

2015-01-01

Although lead-free piezoelectric ceramics have been extensively studied, many problems must still be overcome before they are suitable for practical use. One of the main problems is fabricating a multilayer structure, and one solution attracting growing interest is the use of lead-free multilayer piezoelectric ceramics. The paper reviews work that has been done by the authors on lead-free alkali niobate-based multilayer piezoelectric ceramics co-fired with nickel inner electrodes. Nickel inner electrodes have many advantages, such as high electromigration resistance, high interfacial strength with ceramics, and greater cost effectiveness than silver palladium inner electrodes. However, widely used lead zirconate titanate-based ceramics cannot be co-fired with nickel inner electrodes, and silver palladium inner electrodes are usually used for lead zirconate titanate-based piezoelectric ceramics. A possible alternative is lead-free ceramics co-fired with nickel inner electrodes. We have thus been developing lead-free alkali niobate-based multilayer ceramics co-fired with nickel inner electrodes. The normalized electric-field-induced thickness strain (Smax/Emax) of a representative alkali niobate-based multilayer ceramic structure with nickel inner electrodes was 360 pm/V, where Smax denotes the maximum strain and Emax denotes the maximum electric field. This value is about half that for the lead zirconate titanate-based ceramics that are widely used. However, a comparable value can be obtained by stacking more ceramic layers with smaller thicknesses. In the paper, the compositional design and process used to co-fire lead-free ceramics with nickel inner electrodes are introduced, and their piezoelectric properties and reliabilities are shown. Recent advances are introduced, and future development is discussed. PMID:28793646

A Novel Electro-Thermal Laminated Ceramic with Carbon-Based Layer

PubMed Central

Ji, Yi; Huang, Bin; Rao, Pinggen

2017-01-01

A novel electro-thermal laminated ceramic composed of ceramic tile, carbon-based layer, dielectric layer, and foaming ceramic layer was designed and prepared by tape casting. The surface temperature achieved at an applied voltage of 10 V by the laminated ceramics was 40.3 °C when the thickness of carbon-based suspension was 1.0 mm and the adhesive strength between ceramic tile and carbon-based layer was 1.02 ± 0.06 MPa. In addition, the thermal aging results at 100 °C up to 192 h confirmed the high thermal stability and reliability of the electro-thermal laminated ceramics. The development of this laminated ceramic with excellent electro-thermal properties and safety provides a new individual heating device which is highly expected to be widely applied in the field of indoor heat supply. PMID:28773006

A Novel Electro-Thermal Laminated Ceramic with Carbon-Based Layer.

PubMed

Ji, Yi; Huang, Bin; Rao, Pinggen

2017-06-12

A novel electro-thermal laminated ceramic composed of ceramic tile, carbon-based layer, dielectric layer, and foaming ceramic layer was designed and prepared by tape casting. The surface temperature achieved at an applied voltage of 10 V by the laminated ceramics was 40.3 °C when the thickness of carbon-based suspension was 1.0 mm and the adhesive strength between ceramic tile and carbon-based layer was 1.02 ± 0.06 MPa. In addition, the thermal aging results at 100 °C up to 192 h confirmed the high thermal stability and reliability of the electro-thermal laminated ceramics. The development of this laminated ceramic with excellent electro-thermal properties and safety provides a new individual heating device which is highly expected to be widely applied in the field of indoor heat supply.

Process for strengthening aluminum based ceramics and material

DOEpatents

Moorhead, Arthur J.; Kim, Hyoun-Ee

2000-01-01

A process for strengthening aluminum based ceramics is provided. A gaseous atmosphere consisting essentially of silicon monoxide gas is formed by exposing a source of silicon to an atmosphere consisting essentially of hydrogen and a sufficient amount of water vapor. The aluminum based ceramic is exposed to the gaseous silicon monoxide atmosphere for a period of time and at a temperature sufficient to produce a continuous, stable silicon-containing film on the surface of the aluminum based ceramic that increases the strength of the ceramic.

Resorbable versus titanium plates for orthognathic surgery.

PubMed

Agnihotry, Anirudha; Fedorowicz, Zbys; Nasser, Mona; Gill, Karanjot S

2017-10-04

Recognition of some of the limitations of titanium plates and screws used for the fixation of bones has led to the development of plates manufactured from bioresorbable materials. Whilst resorbable plates appear to offer clinical advantages over metal plates in orthognathic surgery, concerns remain about the stability of fixation and the length of time required for their degradation and the possibility of foreign body reactions. This review compares the use of titanium versus bioresorbable plates in orthognathic surgery and is an update of the Cochrane Review first published in 2007. To compare the effects of bioresorbable fixation systems with titanium systems used during orthognathic surgery. Cochrane Oral Health's Information Specialist searched the following databases: Cochrane Oral Health's Trials Register (to 20 January 2017); the Cochrane Central Register of Controlled Trials (CENTRAL; 2016, Issue 11) in the Cochrane Library (searched 20 January 2017); MEDLINE Ovid (1946 to 20 January 2017); and Embase Ovid (1980 to 20 January 2017). We searched the US National Institutes of Health Ongoing Trials Register ClinicalTrials.gov (clinicaltrials.gov; searched 20 January 2017), and the World Health Organization International Clinical Trials Registry Platform (searched 20 January 2017) for ongoing trials. No restrictions were placed on the language or date of publication when searching the electronic databases. Randomised controlled trials comparing bioresorbable versus titanium fixation systems used for orthognathic surgery in adults. Two review authors independently screened the results of the electronic searches, extracted data and assessed the risk of bias of the included studies. We resolved disagreement by discussion. Clinical heterogeneity between the included trials precluded pooling of data, and only a descriptive summary is presented. This review included two trials, involving 103 participants, one comparing titanium with resorbable plates and screws and the other titanium with resorbable screws. Both studies were at high risk of bias and provided very limited data for the primary outcomes of this review. All participants in one trial suffered mild to moderate postoperative discomfort with no statistically significant difference between the two plating groups at different follow-up times. Mean scores of patient satisfaction were 7.43 to 8.63 (range 0 to 10) with no statistically significant difference between the two groups throughout follow-up. Adverse effects reported in one study were two plate exposures in each group occurring between the third and ninth months. Plate exposures occurred mainly in the posterior maxillary region, except for one titanium plate exposure in the mandibular premolar region. Known causes of infection were associated with loosened screws and wound dehiscence with no statistically significant difference in the infection rate between titanium (3/196), and resorbable (3/165) plates. We do not have sufficient evidence to determine if titanium plates or resorbable plates are superior for fixation of bones after orthognathic surgery. This review provides insufficient evidence to show any difference in postoperative pain and discomfort, level of patient satisfaction, plate exposure or infection for plate and screw fixation using either titanium or resorbable materials.

Management of pediatric mandibular fractures using bioresorbable plating system - Efficacy, stability, and clinical outcomes: Our experiences and literature review.

PubMed

Singh, Mahinder; Singh, R K; Passi, Deepak; Aggarwal, Mohit; Kaur, Guneet

2016-01-01

The purpose of this study was to determine the efficacy and stability of the biodegradable fixation system for treatment of mandible fractures in pediatric patients by measuring the bite force. Sixty pediatric patients with mandibular fractures (36 males, 24 females) were included in this study. The 2.5-mm resorbable plates were adapted along Champy's line of ideal osteosynthesis and secured with four 2.5 mm diameter monocortical resorbable screws, 8 mm in length. All patients were followed for 10 months. Clinical parameters, such as soft tissue infection, nonunion, malunion, implant exposure, malocclusion, nerve injury, and bite force for stability, were prospectively assessed. Adequate fixation and primary bone healing was achieved in 100% of the cases. Six minor complications (10%) were observed: 2 soft tissue infections (3%), 1 plate dehiscence (2%), 1 malocclusion (2%), and 2 paresthesia (3%). 2.5-mm resorbable plating system along Champy's line of ideal osteosynthesis is a good treatment modality for mandible fractures in pediatric patients.

Comparison of resorbable poly-L-lactic acid-polyglycolic acid and internal Palmaz stents for the surgical correction of severe tracheomalacia.

PubMed

Sewall, Gregory K; Warner, Thomas; Connor, Nadine P; Hartig, Gregory K

2003-06-01

Tracheomalacia (TM) is associated with expiratory airway collapse and potentially fatal respiratory distress. Internal and external tracheal stents and, recently, resorbable biopolymers have been used to treat this condition. In this study, the efficacy and biocompatibility of internal Palmaz stents and external poly-L-lactic acid-polyglycolic acid (PLPG) stents were compared in a model of severe TM induced in piglets. The tracheas were repaired with one of two stenting methods, and the animals survived for up to 16 weeks. Weight gain, adverse respiratory signs and symptoms, tracheal or lung histopathologic changes, and internal and external tracheal diameters were measured. The animals in the PLPG group uniformly were free of respiratory distress and tracheal stenosis or inflammation, whereas all animals in the Palmaz group developed respiratory distress as a result of pneumonia or tracheal stenosis caused by intraluminal granulation tissue. In conclusion, superior efficacy of external, resorbable PLPG stents was found relative to internal Palmaz stents for the surgical repair of severe TM.

Method for producing chemically bonded phosphate ceramics and for stabilizing contaminants encapsulated therein utilizing reducing agents

DOEpatents

Singh, Dileep; Wagh, Arun S.; Jeong, Seung-Young

2000-01-01

Known phosphate ceramic formulations are improved and the ability to produce iron-based phosphate ceramic systems is enabled by the addition of an oxidizing or reducing step during the acid-base reactions that form the phosphate ceramic products. The additives allow control of the rate of the acid-base reactions and concomitant heat generation. In an alternate embodiment, waste containing metal anions are stabilized in phosphate ceramic products by the addition of a reducing agent to the phosphate ceramic mixture. The reduced metal ions are more stable and/or reactive with the phosphate ions, resulting in the formation of insoluble metal species within the phosphate ceramic matrix, such that the resulting chemically bonded phosphate ceramic product has greater leach resistance.

Laryngotracheal reconstruction with resorbable microplate buttressing.

PubMed

Javia, Luv R; Zur, Karen B

2012-04-01

In patients undergoing laryngotracheal reconstruction (LTR), malacic segments of trachea can pose challenges to successful reconstruction. Malacic segments may inadequately support cartilage grafts used in augmentation surgery, sometimes requiring cricotracheal or tracheal resections. We describe a novel technique of LTR with resorbable microplate buttressing of malacic lateral tracheal segments. Retrospective case series. Review of technique, treatment outcomes, and complications of seven children with subglottic stenosis and tracheomalacia requiring a microplate-augmented LTR technique. Seven infants ranging from 26 months to 9 years of age successfully underwent LTR for subglottic stenosis. Six children had a grade III subglottic stenosis. The seventh child had grade II subglottic stenosis, bilateral vocal fold paralysis, an elliptical cricoid, and an obstructing giant suprastomal fibroma. Five children underwent a double-stage LTR with resorbable microplates sutured bilaterally to support severely malacic lateral tracheal segments. A cricotracheal resection would not have been feasible in one child due to the resection length and inadequate tracheal mobilization. Two children underwent a single-stage LTR with unilateral application of a microplate. Six children were decannulated within 3 months and continue without airway symptoms or complications. One child, who is just over 2 months from reconstructive surgery, is being setup for decannulation. No complications were encountered. LTR with resorbable microplate buttressing of malacic lateral tracheal segments is technically feasible, safe, and can avoid more extensive surgery requiring tracheal resection. Further experience may support the use of this technique in challenging airway reconstructions. Copyright © 2012 The American Laryngological, Rhinological, and Otological Society, Inc.

Bioresorbable silicon electronic sensors for the brain.

PubMed

Kang, Seung-Kyun; Murphy, Rory K J; Hwang, Suk-Won; Lee, Seung Min; Harburg, Daniel V; Krueger, Neil A; Shin, Jiho; Gamble, Paul; Cheng, Huanyu; Yu, Sooyoun; Liu, Zhuangjian; McCall, Jordan G; Stephen, Manu; Ying, Hanze; Kim, Jeonghyun; Park, Gayoung; Webb, R Chad; Lee, Chi Hwan; Chung, Sangjin; Wie, Dae Seung; Gujar, Amit D; Vemulapalli, Bharat; Kim, Albert H; Lee, Kyung-Mi; Cheng, Jianjun; Huang, Younggang; Lee, Sang Hoon; Braun, Paul V; Ray, Wilson Z; Rogers, John A

2016-02-04

Many procedures in modern clinical medicine rely on the use of electronic implants in treating conditions that range from acute coronary events to traumatic injury. However, standard permanent electronic hardware acts as a nidus for infection: bacteria form biofilms along percutaneous wires, or seed haematogenously, with the potential to migrate within the body and to provoke immune-mediated pathological tissue reactions. The associated surgical retrieval procedures, meanwhile, subject patients to the distress associated with re-operation and expose them to additional complications. Here, we report materials, device architectures, integration strategies, and in vivo demonstrations in rats of implantable, multifunctional silicon sensors for the brain, for which all of the constituent materials naturally resorb via hydrolysis and/or metabolic action, eliminating the need for extraction. Continuous monitoring of intracranial pressure and temperature illustrates functionality essential to the treatment of traumatic brain injury; the measurement performance of our resorbable devices compares favourably with that of non-resorbable clinical standards. In our experiments, insulated percutaneous wires connect to an externally mounted, miniaturized wireless potentiostat for data transmission. In a separate set-up, we connect a sensor to an implanted (but only partially resorbable) data-communication system, proving the principle that there is no need for any percutaneous wiring. The devices can be adapted to sense fluid flow, motion, pH or thermal characteristics, in formats that are compatible with the body's abdomen and extremities, as well as the deep brain, suggesting that the sensors might meet many needs in clinical medicine.

Bioresorbable silicon electronic sensors for the brain

NASA Astrophysics Data System (ADS)

Kang, Seung-Kyun; Murphy, Rory K. J.; Hwang, Suk-Won; Lee, Seung Min; Harburg, Daniel V.; Krueger, Neil A.; Shin, Jiho; Gamble, Paul; Cheng, Huanyu; Yu, Sooyoun; Liu, Zhuangjian; McCall, Jordan G.; Stephen, Manu; Ying, Hanze; Kim, Jeonghyun; Park, Gayoung; Webb, R. Chad; Lee, Chi Hwan; Chung, Sangjin; Wie, Dae Seung; Gujar, Amit D.; Vemulapalli, Bharat; Kim, Albert H.; Lee, Kyung-Mi; Cheng, Jianjun; Huang, Younggang; Lee, Sang Hoon; Braun, Paul V.; Ray, Wilson Z.; Rogers, John A.

2016-02-01

Many procedures in modern clinical medicine rely on the use of electronic implants in treating conditions that range from acute coronary events to traumatic injury. However, standard permanent electronic hardware acts as a nidus for infection: bacteria form biofilms along percutaneous wires, or seed haematogenously, with the potential to migrate within the body and to provoke immune-mediated pathological tissue reactions. The associated surgical retrieval procedures, meanwhile, subject patients to the distress associated with re-operation and expose them to additional complications. Here, we report materials, device architectures, integration strategies, and in vivo demonstrations in rats of implantable, multifunctional silicon sensors for the brain, for which all of the constituent materials naturally resorb via hydrolysis and/or metabolic action, eliminating the need for extraction. Continuous monitoring of intracranial pressure and temperature illustrates functionality essential to the treatment of traumatic brain injury; the measurement performance of our resorbable devices compares favourably with that of non-resorbable clinical standards. In our experiments, insulated percutaneous wires connect to an externally mounted, miniaturized wireless potentiostat for data transmission. In a separate set-up, we connect a sensor to an implanted (but only partially resorbable) data-communication system, proving the principle that there is no need for any percutaneous wiring. The devices can be adapted to sense fluid flow, motion, pH or thermal characteristics, in formats that are compatible with the body’s abdomen and extremities, as well as the deep brain, suggesting that the sensors might meet many needs in clinical medicine.

Two dimensional alveolar ridge augmentation using particulate hydroxyapatite and collagen membrane: A case report

PubMed Central

Singh, Aparna; Daing, Anika; Anand, Vishal; Dixit, Jaya

2014-01-01

Background Ridge augmentation procedures require bone regeneration outside of the existing bony walls or housing and are therefore often considered to be the most challenging surgical procedures. The bony deficiencies can be managed with GBR techniques involving bone grafting material and membrane while vertical augmentation may require the use of space-creating support mechanisms. Non-degradable membranes have been used for ridge augmentation with encouraging results however; requirement of second surgery for its removal and associated infection on exposure may compromise the desired results. These problems can be overcome by employing resorbable collagen membranes. Different bone graft materials are also used in combination with resorbable membranes, for prevention of membrane collapse and maintenance of space, as they lack sufficient rigidity. Particulate hydroxyapatite bone graft may be better alternative, because it treats the underlying bone defect to restore the natural support of the tissue architecture. Moreover, its use avoids potential donor site complications associated with autogenous block grafts. Method Patient described in this report presented with missing right maxillary incisor with ridge deficiency. A treatment approach involving localised ridge augmentation with particulate hydroxyapatite and collagen membrane was used. Result Six month post-operative periapical radiograph demonstrated a significant vertical bone fill. Conclusion The clinical and radiographic findings of the present case suggests that HA in conjunction with a resorbable collagen membrane may be an acceptable alternative to the autogenous block graft and non-resorbable membrane in the treatment of compromised alveolar ridge deficiencies. PMID:25737935

Effect of an internal coating technique on tensile bond strengths of resin cements to zirconia ceramics.

PubMed

Kitayama, Shuzo; Nikaido, Toru; Maruoka, Rena; Zhu, Lei; Ikeda, Masaomi; Watanabe, Akihiko; Foxton, Richard M; Miura, Hiroyuki; Tagami, Junji

2009-07-01

This study was conducted to enhance the tensile bond strengths of resin cements to zirconia ceramics. Fifty-six zirconia ceramic specimens (Cercon Base) and twenty-eight silica-based ceramic specimens (GN-1, GN-1 Ceramic Block) were air-abraded using alumina. Thereafter, the zirconia ceramic specimens were divided into two subgroups of 28 each according to the surface pretreatment; no pretreatment (Zr); and the internal coating technique (INT). For INT, the surface of zirconia was coated by fusing silica-based ceramics (Cercon Ceram Kiss). Ceramic surfaces were conditioned with/without a silane coupling agent followed by bonding with one of two resin cements; Panavia F 2.0 (PF) and Superbond C&B (SB). After 24 hours storage in water, the tensile bond strengths were tested (n=7). For both PF and SB, silanization significantly improved the bond strength to GN-1 and INT (p<0.05). The INT coating followed by silanizaton demonstrated enhancement of bonding to zirconia ceramics.

Effect of ceramic thickness and composite bases on stress distribution of inlays--a finite element analysis.

PubMed

Durand, Letícia Brandão; Guimarães, Jackeline Coutinho; Monteiro Junior, Sylvio; Baratieri, Luiz Narciso

2015-01-01

The purpose of this study was to determine the effect of cavity depth, ceramic thickness, and resin bases with different elastic modulus on von Mises stress patterns of ceramic inlays. Tridimensional geometric models were developed with SolidWorks image software. The differences between the models were: depth of pulpal wall, ceramic thickness, and presence of composite bases with different thickness and elastic modulus. The geometric models were constrained at the proximal surfaces and base of maxillary bone. A load of 100 N was applied. The stress distribution pattern was analyzed with von Mises stress diagrams. The maximum von Mises stress values ranged from 176 MPa to 263 MPa and varied among the 3D-models. The highest von Mises stress value was found on models with 1-mm-thick composite resin base and 1-mm-thick ceramic inlay. Intermediate values (249-250 MPa) occurred on models with 2-mm-thick composite resin base and 1-mm-thick ceramic inlay and 1-mm-thick composite resin base and 2-mm-thick ceramic inlay. The lowest values were observed on models restored exclusively with ceramic inlay (176 MPa to 182 MPa). It was found that thicker inlays distribute stress more favorably and bases with low elastic modulus increase stress concentrations on the internal surface of the ceramic inlay. The increase of ceramic thickness tends to present more favorable stress distribution, especially when bonded directly onto the cavity without the use of supporting materials. When the use of a composite base is required, composite resin with high elastic modulus and reduced thickness should be preferred.

Affordable, Robust Ceramic Joining Technology (ARCJoinT) for High Temperature Applications

NASA Technical Reports Server (NTRS)

Singh, M.

1998-01-01

Ceramic joining is recognized as one of the enabling technologies for the successful utilization of silicon carbide-based monolithic ceramic and fiber reinforced composite components in a number of demanding and high temperature applications in aerospace and ground-based systems. An affordable, robust ceramic joining technology (ARCJoinT) for joining of silicon carbide-based ceramics and fiber reinforced composites has been developed. This technique is capable of producing joints with tailorable thickness and composition. A wide variety of silicon carbide-based ceramics and composites, in different shapes and sizes, have been joined using this technique. The room and high temperature mechanical properties and fractography of ceramic joints have been reported. In monolithic silicon carbide ceramics, these joints maintain their mechanical strength up to 1350 C in air. There is no change in the mechanical strength of joints in silicon carbide matrix composites up to 1200 C in air. In composites, simple butt joints yield only about 20% of the ultimate strength of the parent materials. This technology is suitable for the joining of large and complex shaped ceramic and composite components, and with certain modifications, can be applied to repair of ceramic components damaged in service.

Transosseous fixation of pediatric displaced mandibular fractures with polyglactin resorbable suture--a simplified technique.

PubMed

Chandan, Sanjay; Halli, Rajshekhar; Joshi, Samir; Chhabaria, Gaurav; Setiya, Sneha

2013-11-01

Management of pediatric mandibular fractures presents a unique challenge to surgeons in terms of its numerous variations compared to adults. Both conservative and open methods have been advocated with their obvious limitations and complications. However, conservative modalities may not be possible in grossly displaced fractures, which necessitate the open method of fixation. We present a novel and simplified technique of transosseous fixation of displaced pediatric mandibular fractures with polyglactin resorbable suture, which provides adequate stability without any interference with tooth buds and which is easy to master.

X-ray absorption fine structure analysis of molybdenum added to BaTiO3-based ceramics used for multilayer ceramic capacitors

NASA Astrophysics Data System (ADS)

Ogata, Yoichiro; Shimura, Tetsuo; Ryu, Minoru; Iwazaki, Yoshiki

2017-04-01

The effect of slight molybdenum doping of perovskite-type BaTiO3-based ceramics on the reliability of a multilayer ceramic capacitor (MLCC) and on the valence state of molybdenum in the BaTiO3-based ceramics has been investigated by highly accelerated lifetime tests and X-ray absorption fine structure analysis. The molybdenum added to the BaTiO3-based ceramics is located at Ti sites and improves the highly accelerated lifetime and lowers the initial dielectric resistivity in MLCCs. Through sintering in a reducing atmosphere, which is an important process in the fabrication of BaTiO3-based MLCCs, the oxidation state of the molybdenum added could be adjusted from +6 to a value close to +4.

Improved performance of diatomite-based dental nanocomposite ceramics using layer-by-layer assembly

PubMed Central

Lu, Xiaoli; Xia, Yang; Liu, Mei; Qian, Yunzhu; Zhou, Xuefeng; Gu, Ning; Zhang, Feimin

2012-01-01

To fabricate high-strength diatomite-based ceramics for dental applications, the layer-by-layer technique was used to coat diatomite particles with cationic [poly(allylamine hydrochloride)] and anionic [poly(sodium 4-styrenesulfonate)] polymers to improve the dispersion and adsorption of positively charged nano-ZrO2 (zirconia) as a reinforcing agent. The modified diatomite particles had reduced particle size, narrower size distribution, and were well dispersed, with good adsorption of nano-ZrO2. To determine the optimum addition levels for nano-ZrO2, ceramics containing 0, 20, 25, 30, and 35 wt% nano-ZrO2 were sintered and characterized by the three-point bending test and microhardness test. In addition to scanning electron microscopy, propagation phase-contrast synchrotron X-ray microtomography was used to examine the internal structure of the ceramics. The addition of 30 wt% nano-ZrO2 resulted in the highest flexural strength and fracture toughness with reduced porosity. Shear bond strength between the core and veneer of our diatomite ceramics and the most widely used dental ceramics were compared; the shear bond strength value for the diatomite-based ceramics was found to be significantly higher than for other groups (P < 0.05). Our results show that diatomite-based nanocomposite ceramics are good potential candidates for ceramic-based dental materials. PMID:22619551

Improved performance of diatomite-based dental nanocomposite ceramics using layer-by-layer assembly.

PubMed

Lu, Xiaoli; Xia, Yang; Liu, Mei; Qian, Yunzhu; Zhou, Xuefeng; Gu, Ning; Zhang, Feimin

2012-01-01

To fabricate high-strength diatomite-based ceramics for dental applications, the layer-by-layer technique was used to coat diatomite particles with cationic [poly(allylamine hydrochloride)] and anionic [poly(sodium 4-styrenesulfonate)] polymers to improve the dispersion and adsorption of positively charged nano-ZrO(2) (zirconia) as a reinforcing agent. The modified diatomite particles had reduced particle size, narrower size distribution, and were well dispersed, with good adsorption of nano-ZrO(2). To determine the optimum addition levels for nano-ZrO(2), ceramics containing 0, 20, 25, 30, and 35 wt% nano-ZrO(2) were sintered and characterized by the three-point bending test and microhardness test. In addition to scanning electron microscopy, propagation phase-contrast synchrotron X-ray microtomography was used to examine the internal structure of the ceramics. The addition of 30 wt% nano-ZrO(2) resulted in the highest flexural strength and fracture toughness with reduced porosity. Shear bond strength between the core and veneer of our diatomite ceramics and the most widely used dental ceramics were compared; the shear bond strength value for the diatomite-based ceramics was found to be significantly higher than for other groups (P < 0.05). Our results show that diatomite-based nanocomposite ceramics are good potential candidates for ceramic-based dental materials.

Effect of Ceramic Surface Treatments After Machine Grinding on the Biaxial Flexural Strength of Different CAD/CAM Dental Ceramics.

PubMed

Bagheri, Hossein; Hooshmand, Tabassom; Aghajani, Farzaneh

2015-09-01

This study aimed to evaluate the effect of different ceramic surface treatments after machining grinding on the biaxial flexural strength (BFS) of machinable dental ceramics with different crystalline phases. Disk-shape specimens (10mm in diameter and 1.3mm in thickness) of machinable ceramic cores (two silica-based and one zirconia-based ceramics) were prepared. Each type of the ceramic surfaces was then randomly treated (n=15) with different treatments as follows: 1) machined finish as control, 2) machined finish and sandblasting with alumina, and 3) machined finish and hydrofluoric acid etching for the leucite and lithium disilicate-based ceramics, and for the zirconia; 1) machined finish and post-sintered as control, 2) machined finish, post-sintered, and sandblasting, and 3) machined finish, post-sintered, and Nd;YAG laser irradiation. The BFS were measured in a universal testing machine. Data based were analyzed by ANOVA and Tukey's multiple comparisons post-hoc test (α=0.05). The mean BFS of machined finish only surfaces for leucite ceramic was significantly higher than that of sandblasted (P=0.001) and acid etched surfaces (P=0.005). A significantly lower BFS was found after sandblasting for lithium disilicate compared with that of other groups (P<0.05). Sandblasting significantly increased the BFS for the zirconia (P<0.05), but the BFS was significantly decreased after laser irradiation (P<0.05). The BFS of the machinable ceramics was affected by the type of ceramic material and surface treatment method. Sandblasting with alumina was detrimental to the strength of only silica-based ceramics. Nd:YAG laser irradiation may lead to substantial strength degradation of zirconia.

Effect of Ceramic Surface Treatments After Machine Grinding on the Biaxial Flexural Strength of Different CAD/CAM Dental Ceramics

PubMed Central

Bagheri, Hossein; Aghajani, Farzaneh

2015-01-01

Objectives: This study aimed to evaluate the effect of different ceramic surface treatments after machining grinding on the biaxial flexural strength (BFS) of machinable dental ceramics with different crystalline phases. Materials and Methods: Disk-shape specimens (10mm in diameter and 1.3mm in thickness) of machinable ceramic cores (two silica-based and one zirconia-based ceramics) were prepared. Each type of the ceramic surfaces was then randomly treated (n=15) with different treatments as follows: 1) machined finish as control, 2) machined finish and sandblasting with alumina, and 3) machined finish and hydrofluoric acid etching for the leucite and lithium disilicate-based ceramics, and for the zirconia; 1) machined finish and post-sintered as control, 2) machined finish, post-sintered, and sandblasting, and 3) machined finish, post-sintered, and Nd;YAG laser irradiation. The BFS were measured in a universal testing machine. Data based were analyzed by ANOVA and Tukey’s multiple comparisons post-hoc test (α=0.05). Results: The mean BFS of machined finish only surfaces for leucite ceramic was significantly higher than that of sandblasted (P=0.001) and acid etched surfaces (P=0.005). A significantly lower BFS was found after sandblasting for lithium disilicate compared with that of other groups (P<0.05). Sandblasting significantly increased the BFS for the zirconia (P<0.05), but the BFS was significantly decreased after laser irradiation (P<0.05). Conclusions: The BFS of the machinable ceramics was affected by the type of ceramic material and surface treatment method. Sandblasting with alumina was detrimental to the strength of only silica-based ceramics. Nd:YAG laser irradiation may lead to substantial strength degradation of zirconia. PMID:27148372

Crack tip fracture toughness of base glasses for dental restoration glass-ceramics using crack opening displacements.

PubMed

Deubener, J; Höland, M; Höland, W; Janakiraman, N; Rheinberger, V M

2011-10-01

The critical stress intensity factor, also known as the crack tip toughness K(tip), was determined for three base glasses, which are used in the manufacture of glass-ceramics. The glasses included the base glass for a lithium disilicate glass-ceramic, the base glass for a fluoroapatite glass-ceramic and the base glass for a leucite glass-ceramic. These glass-ceramic are extensively used in the form of biomaterials in restorative dental medicine. The crack tip toughness was established by using crack opening displacement profiles under experimental conditions. The crack was produced by Vickers indentation. The crack tip toughness parameters determined for the three glass-ceramics differed quite significantly. The crack tip parameters of the lithium disilicate base glass and the leucite base glass were higher than that of the fluoroapatite base glass. This last material showed glass-in-glass phase separation. The discussion of the results clearly shows that the droplet glass phase is softer than the glass matrix. Therefore, the authors conclude that a direct relationship exists between the chemical nature of the glasses and the crack tip parameter. Copyright © 2011 Elsevier Ltd. All rights reserved.

Cost Analysis of Cerebrospinal Fluid Leaks and Cerebrospinal Fluid Leak Prevention in Patients Undergoing Cerebellopontine Angle Surgery.

PubMed

Chern, Alexander; Hunter, Jacob B; Bennett, Marc L

2017-01-01

To determine if cranioplasty techniques following translabyrinthine approaches to the cerebellopontine angle are cost-effective. Retrospective case series. One hundred eighty patients with available financial data who underwent translabyrinthine approaches at a single academic referral center between 2005 and 2015. Cranioplasty with a dural substitute, layered fat graft, and a resorbable mesh plate secured with screws Main Outcome Measures: billing data was obtained for each patient's hospital course for translabyrinthine approaches and postoperative cerebrospinal fluid (CSF) leaks. One hundred nineteen patients underwent translabyrinthine approaches with an abdominal fat graft closure, with a median cost of $25759.89 (range, $15885.65-$136433.07). Sixty-one patients underwent translabyrinthine approaches with a dural substitute, abdominal fat graft, and a resorbable mesh for closure, with a median cost of $29314.97 (range, $17674.28-$111404.55). The median cost of a CSF leak was $50401.25 (range, $0-$384761.71). The additional cost of a CSF leak when shared by all patients who underwent translabyrinthine approaches is $6048.15. The addition of a dural substitute and a resorbable mesh plate after translabyrinthine approaches reduced the CSF leak from 12 to 1.9%, an 84.2% reduction, and a median savings per patient of $2932.23. Applying our cohort's billing data to previously published cranioplasty techniques, costs, and leak rate improvements after translabyrinthine approaches, all techniques were found to be cost-effective. Resorbable mesh cranioplasty is cost-effective at reducing CSF leaks after translabyrinthine approaches. Per our billing data and achieving the same CSF leak rate, cranioplasty costs exceeding $5090.53 are not cost-effective.

Use of Antibiotic Impregnated Resorbable Beads Reduces Pressure Ulcer Recurrence: A Retrospective Analysis.

PubMed

Khansa, Ibrahim; Barker, Jenny C; Ghatak, Piya Das; Sen, Chandan K; Gordillo, Gayle M

2018-05-17

Recurrence of pressure ulcers remains common. We have employed resorbable antibiotic beads as a therapeutic strategy to deliver high local antibiotic concentrations to the debridement site. Our objective was to determine whether the use of resorbable antibiotic- beads would reduce pressure ulcer recurrence. We reviewed all stage IV pressure ulcers treated with excision, partial ostectomy and flap coverage over 16 years. Baseline patient factors (location of ulcer, presence of osteomyelitis, preoperative prealbumin), surgical factors (type of flap, use of antibiotic beads, bone culture results) and postoperative outcomes (ulcer recurrence at 1 year, dehiscence, seroma, cellulitis) were collected. Outcomes of patients who received antibiotic-impregnated beads were compared to those who did not. 86 patients with 120 stage IV pressure ulcers underwent excision and flap coverage. This included 16 ulcers where antibiotic beads were used, and 104 where they were not. The overall ulcer recurrence rate at 12 months was 35.8%. The recurrence rate in the group treated with antibiotic beads was significantly lower than the group without beads (12.5% vs. 39.4%, p=0.03). Overall, complication rates between the two groups were similar (43.8% vs. 51.9%, p=0.54). No systemic or local toxicity from antibiotic beads occurred. Scanning electron microscopy images of sacral bone from one case showed bacterial biofilm even after debridement. Pressure ulcer recurrence at 1 year after excision and flap coverage decreased significantly with the use of resorbable antibiotic beads. This article is protected by copyright. All rights reserved. © 2018 by the Wound Healing Society.

Development and evaluation of magnesium oxide-based ceramics for chamber parts in mass-production plasma etching equipment

NASA Astrophysics Data System (ADS)

Kasashima, Yuji; Tsutsumi, Kota; Mitomi, Shinzo; Uesugi, Fumihiko

2017-06-01

In mass-production plasma etching equipment, the corrosion of ceramic chamber parts reduces the production yield of LSI and overall equipment effectiveness (OEE) owing to contamination, short useful life, and particle generation. Novel ceramics that can improve the production yield and OEE are highly required. We develop magnesium oxide (MgO)-based ceramics and evaluate them under mass-production plasma etching conditions. The results of this study indicate that the developed MgO-based ceramics with high mechanical properties and low electric resistivity have a higher resistance to corrosion in plasma etching using CF4 gas than Si and conventional ceramic materials such as aluminum oxide and yttrium oxide.

Ceramic Technology Project semiannual progress report, April 1992--September 1992

DOE Office of Scientific and Technical Information (OSTI.GOV)

Johnson, D.R.

1993-07-01

This project was developed to meet the ceramic technology requirements of the DOE Office of Transportation Systems` automotive technology programs. Significant progress in fabricating ceramic components for DOE, NASA, and DOE advanced heat engine programs show that operation of ceramic parts in high-temperature engines is feasible; however, addition research is needed in materials and processing, design, and data base and life prediction before industry will have a sufficient technology base for producing reliable cost-effective ceramic engine components commercially. A 5-yr project plan was developed, with focus on structural ceramics for advanced gas turbine and diesel engines, ceramic bearings and attachments,more » and ceramic coatings for thermal barrier and wear applications in these engines.« less

The development of bioresorbable composite polymeric implants with high mechanical strength

NASA Astrophysics Data System (ADS)

Sharma, Upma; Concagh, Danny; Core, Lee; Kuang, Yina; You, Changcheng; Pham, Quynh; Zugates, Greg; Busold, Rany; Webber, Stephanie; Merlo, Jonathan; Langer, Robert; Whitesides, George M.; Palasis, Maria

2018-01-01

Implants for the treatment of tissue defects should mimic the mechanical properties of the native tissue of interest and should be resorbable as well as biocompatible. In this work, we developed a scaffold from variants of poly(glycolic) acid which were braided and coated with an elastomer of poly(glycolide-co-caprolactone) and crosslinked. The coating of the scaffold with the elastomer led to higher mechanical strength in terms of compression, expansion and elasticity compared to braids without the elastomer coating. These composite scaffolds were found to have expansion properties similar to metallic stents, utilizing materials which are typically much weaker than metal. We optimized the mechanical properties of the implant by tuning the elastomer branching structure, crosslink density, and molecular weight. The scaffolds were shown to be highly resorbable following implantation in a porcine femoral artery. Biocompatibility was studied in vivo in an ovine model by implanting the scaffolds into femoral arteries. The scaffolds were able to support an expanded open lumen over 12 months in vivo and also fully resorbed by 18 months in the ovine model.

Management of pediatric mandibular fractures using bioresorbable plating system – Efficacy, stability, and clinical outcomes: Our experiences and literature review

PubMed Central

Singh, Mahinder; Singh, R.K.; Passi, Deepak; Aggarwal, Mohit; Kaur, Guneet

2015-01-01

Aims The purpose of this study was to determine the efficacy and stability of the biodegradable fixation system for treatment of mandible fractures in pediatric patients by measuring the bite force. Methods Sixty pediatric patients with mandibular fractures (36 males, 24 females) were included in this study. The 2.5-mm resorbable plates were adapted along Champy's line of ideal osteosynthesis and secured with four 2.5 mm diameter monocortical resorbable screws, 8 mm in length. All patients were followed for 10 months. Clinical parameters, such as soft tissue infection, nonunion, malunion, implant exposure, malocclusion, nerve injury, and bite force for stability, were prospectively assessed. Results Adequate fixation and primary bone healing was achieved in 100% of the cases. Six minor complications (10%) were observed: 2 soft tissue infections (3%), 1 plate dehiscence (2%), 1 malocclusion (2%), and 2 paresthesia (3%). Conclusion 2.5-mm resorbable plating system along Champy's line of ideal osteosynthesis is a good treatment modality for mandible fractures in pediatric patients. PMID:27195206

A study on (K, Na) NbO3 based multilayer piezoelectric ceramics micro speaker

NASA Astrophysics Data System (ADS)

Gao, Renlong; Chu, Xiangcheng; Huan, Yu; Sun, Yiming; Liu, Jiayi; Wang, Xiaohui; Li, Longtu

2014-10-01

A flat panel micro speaker was fabricated from (K, Na) NbO3 (KNN)-based multilayer piezoelectric ceramics by a tape casting and cofiring process using Ag-Pd alloys as an inner electrode. The interface between ceramic and electrode was investigated by scanning electron microscope (SEM) and transmission electron microscope (TEM). The acoustic response was characterized by a standard audio test system. We found that the micro speaker with dimensions of 23 × 27 × 0.6 mm3, using three layers of 30 μm thickness KNN-based ceramic, has a high average sound pressure level (SPL) of 87 dB, between 100 Hz-20 kHz under five voltage. This result was even better than that of lead zirconate titanate (PZT)-based ceramics under the same conditions. The experimental results show that the KNN-based multilayer ceramics could be used as lead free piezoelectric micro speakers.

Involvement of Receptor Activator of Nuclear Factor-κB Ligand (RANKL)-induced Incomplete Cytokinesis in the Polyploidization of Osteoclasts.

PubMed

Takegahara, Noriko; Kim, Hyunsoo; Mizuno, Hiroki; Sakaue-Sawano, Asako; Miyawaki, Atsushi; Tomura, Michio; Kanagawa, Osami; Ishii, Masaru; Choi, Yongwon

2016-02-12

Osteoclasts are specialized polyploid cells that resorb bone. Upon stimulation with receptor activator of nuclear factor-κB ligand (RANKL), myeloid precursors commit to becoming polyploid, largely via cell fusion. Polyploidization of osteoclasts is necessary for their bone-resorbing activity, but the mechanisms by which polyploidization is controlled remain to be determined. Here, we demonstrated that in addition to cell fusion, incomplete cytokinesis also plays a role in osteoclast polyploidization. In in vitro cultured osteoclasts derived from mice expressing the fluorescent ubiquitin-based cell cycle indicator (Fucci), RANKL induced polyploidy by incomplete cytokinesis as well as cell fusion. Polyploid cells generated by incomplete cytokinesis had the potential to subsequently undergo cell fusion. Nuclear polyploidy was also observed in osteoclasts in vivo, suggesting the involvement of incomplete cytokinesis in physiological polyploidization. Furthermore, RANKL-induced incomplete cytokinesis was reduced by inhibition of Akt, resulting in impaired multinucleated osteoclast formation. Taken together, these results reveal that RANKL-induced incomplete cytokinesis contributes to polyploidization of osteoclasts via Akt activation. © 2016 by The American Society for Biochemistry and Molecular Biology, Inc.

Involvement of Receptor Activator of Nuclear Factor-κB Ligand (RANKL)-induced Incomplete Cytokinesis in the Polyploidization of Osteoclasts*

PubMed Central

Takegahara, Noriko; Kim, Hyunsoo; Mizuno, Hiroki; Sakaue-Sawano, Asako; Miyawaki, Atsushi; Tomura, Michio; Kanagawa, Osami; Ishii, Masaru; Choi, Yongwon

2016-01-01

Osteoclasts are specialized polyploid cells that resorb bone. Upon stimulation with receptor activator of nuclear factor-κB ligand (RANKL), myeloid precursors commit to becoming polyploid, largely via cell fusion. Polyploidization of osteoclasts is necessary for their bone-resorbing activity, but the mechanisms by which polyploidization is controlled remain to be determined. Here, we demonstrated that in addition to cell fusion, incomplete cytokinesis also plays a role in osteoclast polyploidization. In in vitro cultured osteoclasts derived from mice expressing the fluorescent ubiquitin-based cell cycle indicator (Fucci), RANKL induced polyploidy by incomplete cytokinesis as well as cell fusion. Polyploid cells generated by incomplete cytokinesis had the potential to subsequently undergo cell fusion. Nuclear polyploidy was also observed in osteoclasts in vivo, suggesting the involvement of incomplete cytokinesis in physiological polyploidization. Furthermore, RANKL-induced incomplete cytokinesis was reduced by inhibition of Akt, resulting in impaired multinucleated osteoclast formation. Taken together, these results reveal that RANKL-induced incomplete cytokinesis contributes to polyploidization of osteoclasts via Akt activation. PMID:26670608

[Preliminary study of bonding strength between diatomite-based dental ceramic and veneering porcelains].

PubMed

Lu, Xiao-li; Gao, Mei-qin; Cheng, Yu-ye; Zhang, Fei-min

2015-04-01

In order to choose the best veneering porcelain for diatomite-based dental ceramic substrate, the bonding strength between diatomite-based dental ceramics and veneering porcelains was measured, and the microstructure and elements distribution of interface were analyzed. The coefficient of thermal expansion (CTE) of diatomite-based dental ceramics was detected by dilatometry. Three veneering porcelain materials were selected with the best CTE matching including alumina veneering porcelain (group A), titanium porcelain veneering porcelain (group B), and E-max veneering porcelain (group C). Shear bonding strength was detected. SEM and EDS were used to observe the interface microstructure and element distribution. Statistical analysis was performed using SPSS 17.0 software package. The CTE of diatomite-based dental ceramics at 25-500 degrees centigrade was 8.85×10-6K-1. The diatomite-based substrate ceramics combined best with group C. Shear bonding strength between group A and C and group B and C both showed significant differences(P<0.05). SEM and EDS showed that the interface of group C sintered tightly and elements permeated on both sides of the interface. The diatomite-based substrate ceramics combines better with E-max porcelain veneer.

Flight-vehicle materials, structures, and dynamics - Assessment and future directions. Vol. 3 - Ceramics and ceramic-matrix composites

NASA Technical Reports Server (NTRS)

Levine, Stanley R. (Editor)

1992-01-01

The present volume discusses ceramics and ceramic-matrix composites in prospective aerospace systems, monolithic ceramics, transformation-toughened and whisker-reinforced ceramic composites, glass-ceramic matrix composites, reaction-bonded Si3N4 and SiC composites, and chemical vapor-infiltrated composites. Also discussed are the sol-gel-processing of ceramic composites, the fabrication and properties of fiber-reinforced ceramic composites with directed metal oxidation, the fracture behavior of ceramic-matrix composites (CMCs), the fatigue of fiber-reinforced CMCs, creep and rupture of CMCs, structural design methodologies for ceramic-based materials systems, the joining of ceramics and CMCs, and carbon-carbon composites.

Novel Approach for Positioning Sensor Lead Wires on SiC-Based Monolithic Ceramic and FRCMC Components/Subcomponents Having Flat and Curved Surfaces

NASA Technical Reports Server (NTRS)

Kiser, J. Douglas; Singh, Mrityunjay; Lei, Jin-Fen; Martin, Lisa C.

1999-01-01

A novel attachment approach for positioning sensor lead wires on silicon carbide-based monolithic ceramic and fiber reinforced ceramic matrix composite (FRCMC) components has been developed. This approach is based on an affordable, robust ceramic joining technology, named ARCJoinT, which was developed for the joining of silicon carbide-based ceramic and fiber reinforced composites. The ARCJoinT technique has previously been shown to produce joints with tailorable thickness and good high temperature strength. In this study, silicon carbide-based ceramic and FRCMC attachments of different shapes and sizes were joined onto silicon carbide fiber reinforced silicon carbide matrix (SiC/ SiC) composites having flat and curved surfaces. Based on results obtained in previous joining studies. the joined attachments should maintain their mechanical strength and integrity at temperatures up to 1350 C in air. Therefore they can be used to position and secure sensor lead wires on SiC/SiC components that are being tested in programs that are focused on developing FRCMCs for a number of demanding high temperature applications in aerospace and ground-based systems. This approach, which is suitable for installing attachments on large and complex shaped monolithic ceramic and composite components, should enhance the durability of minimally intrusive high temperature sensor systems. The technology could also be used to reinstall attachments on ceramic components that were damaged in service.

Emerging Ceramic-based Materials for Dentistry

PubMed Central

Denry, I.; Kelly, J.R.

2014-01-01

Our goal is to give an overview of a selection of emerging ceramics and issues for dental or biomedical applications, with emphasis on specific challenges associated with full-contour zirconia ceramics, and a brief synopsis on new machinable glass-ceramics and ceramic-based interpenetrating phase composites. Selected fabrication techniques relevant to dental or biomedical applications such as microwave sintering, spark plasma sintering, and additive manufacturing are also reviewed. Where appropriate, the authors have added their opinions and guidance. PMID:25274751

The Effect of Water or Wax-based Binders on the Chemical and Morphological Characteristics of the Margin Ceramic-Framework Interface.

PubMed

Güler, Umut; de Queiroz, José Renato Cavalcanti; de Oliveira, Luiz Fernando Cappa; Canay, Senay; Ozcan, Mutlu

2015-09-01

This study evaluated the effect of binder choice in mixing ceramic powder on the chemical and morphological features between the margin ceramic-framework interfaces. Titanium and zirconia frameworks (15 x 5 x 0.5 mm3) were veneered with margin ceramics prepared with two different binders, namely a) water/conventional or b) wax-based. For each zirconia framework material, four different margin ceramics were used: a- Creation Zi (Creation Willi Geller International); b- GC Initial Zr (GC America); Triceram (Dentaurum); and d- IPS emax (voclar Vivadent). For the titanium framework, three different margin ceramics were used: a- Creation Ti (Creation Willi Geller International); b- Triceram (Dentaurum); and c- VITA Titaniumkeramik (Vita Zahnfabrik). The chemical composition of the framework-margin ceramic interface was analyzed using Energy Dispersive X-ray Spectroscopy (EDS) and porosity level was quantified within the margin ceramic using an image program (ImageJ) from four random areas (100 x 100 pixels) on each SEM image. EDS analysis showed the presence of Carbon at the margin ceramic-framework interface in the groups where wax-based binder technique was used with the concentration being the highest for the IPS emax ZirCAD group. While IPS system (IPS ZirCAD and IPS Emax) presented higher porosity concentration using wax binder, in the other groups wax-based binder reduced the porosity of margin ceramic, except for Titanium - Triceram combination.

The RIVET: a novel technique involving absorbable fixation for hydroxyapatite osteosynthesis.

PubMed

Shido, Hirokazu; Sakamoto, Yoshiaki; Miwa, Tomoru; Ohira, Takayuki; Yoshida, Kazunari; Kishi, Kazuo

2013-05-01

Cranioplasty using custom-made hydroxyapatite (HAP) ceramic implants is a common procedure for the repair of skull defects. The advantages of using HAP are that it is nonmetallic, unlike titanium; biocompatible; and osteoconductive. Furthermore, it can be molded to any complex shape that may be needed. A disadvantage is that titanium screws and plates are in development for its fixation. We developed a technique for implant fixation using bioabsorbable screws and plates, and named this technique RIVET: resorbable immobilization for vacuolar en bloc technique.Before each operation, the implant was customized for the patient in question on the basis of models prepared using computed tomography data. The bioabsorbable plates were attached to the implant by drilling, tapping, and screwing, as shown in the video (http://links.lww.com/SCS/A43). The interior portion of the screw was then melted to flatten it against the internal surface of the implant, forming a rivet to join the plate and HAP implant.We used this technique for cranial reconstruction in 2 patients, with satisfying and functional results. We did not encounter any complications.In conclusion, the technique described here allows surgeons to fix implants and plates together more rigidly, giving a better result than possible with previous methods.

Calcium Orthophosphates as Bioceramics: State of the Art

PubMed Central

Dorozhkin, Sergey V.

2010-01-01

In the late 1960s, much interest was raised in regard to biomedical applications of various ceramic materials. A little bit later, such materials were named bioceramics. This review is limited to bioceramics prepared from calcium orthophosphates only, which belong to the categories of bioactive and bioresorbable compounds. There have been a number of important advances in this field during the past 30–40 years. Namely, by structural and compositional control, it became possible to choose whether calcium orthophosphate bioceramics were biologically stable once incorporated within the skeletal structure or whether they were resorbed over time. At the turn of the millennium, a new concept of calcium orthophosphate bioceramics—which is able to promote regeneration of bones—was developed. Presently, calcium orthophosphate bioceramics are available in the form of particulates, blocks, cements, coatings, customized designs for specific applications and as injectable composites in a polymer carrier. Current biomedical applications include artificial replacements for hips, knees, teeth, tendons and ligaments, as well as repair for periodontal disease, maxillofacial reconstruction, augmentation and stabilization of the jawbone, spinal fusion and bone fillers after tumor surgery. Exploratory studies demonstrate potential applications of calcium orthophosphate bioceramics as scaffolds, drug delivery systems, as well as carriers of growth factors, bioactive peptides and/or various types of cells for tissue engineering purposes. PMID:24955932

TCP is hardly resorbed and not osteoconductive in a non-loading calvarial model.

PubMed

Handschel, Jörg; Wiesmann, Hans Peter; Stratmann, Udo; Kleinheinz, Johannes; Meyer, Ulrich; Joos, Ulrich

2002-04-01

Tricalciumphosphate (TCP) has been used as a ceramic bone substitute material in the orthopedic field as well as in craniofacial surgery. Some controversies exist concerning the osteoconductive potential of this material in different implantation sites. This study was designed to evaluate the biological response of calvarial bone towards TCP granules under non-loading conditions to assess the potential of TCP as a biodegredable and osteoconductive bone substitue material for the cranial vault. Full-thickness non-critical size defects were made bilaterally in the calvaria of 21 adult Wistar rats. One side was filled by TCP granules, the contralateral side was left empty and used as a control. Animals were sacrified in defined time intervals up to 6 months. Bone regeneration was analyzed with special respect toward the micromorphological and microanalytical features of the material-bone interaction by electron microscopy and electron diffraction analysis. Histologic examination revealed no TCP degradation even after 6 months of implantation. In contrast, a nearly complete bone regeneration of control defects was found after 6 months. At all times TCP was surrounded by a thin fibrous layer without presence of osteoblasts and features of regular mineralization. As far as degradation and substitution are concerned, TCP is a less favourable material tinder conditions of non-loading.

Reconstruction of irradiated bone segmental defects with a biomaterial associating MBCP+(R), microstructured collagen membrane and total bone marrow grafting: an experimental study in rabbits.

PubMed

Jégoux, Franck; Goyenvalle, Eric; Cognet, Ronan; Malard, Olivier; Moreau, Francoise; Daculsi, Guy; Aguado, Eric

2009-12-15

The bone tissue engineering models used today are still a long way from any oncologic application as immediate postimplantation irradiation would decrease their osteoinductive potential. The aim of this study was to reconstruct a segmental critical size defect in a weight-bearing bone irradiated after implantation. Six white New Zealand rabbits were immediately implanted with a biomaterial associating resorbable collagen membrane EZ(R) filled and micro-macroporous biphasic calcium phosphate granules (MBCP+(R)). After a daily schedule of radiation delivery, and within 4 weeks, a total autologous bone marrow (BM) graft was injected percutaneously into the center of the implant. All the animals were sacrificed at 16 weeks. Successful osseous colonization was found to have bridged the entire length of the defects. Identical distribution of bone ingrowth and residual ceramics at the different levels of the implant suggests that the BM graft plays an osteoinductive role in the center of the defect. Periosteum-like formation was observed at the periphery, with the collagen membrane most likely playing a role. This model succeeded in bridging a large segmental defect in weight-bearing bone with immediate postimplantation fractionated radiation delivery. This has significant implications for the bone tissue engineering approach to patients with cancer-related bone defects.

Biomaterials for craniofacial reconstruction

PubMed Central

Neumann, Andreas; Kevenhoerster, Kevin

2011-01-01

Biomaterials for reconstruction of bony defects of the skull comprise of osteosynthetic materials applied after osteotomies or traumatic fractures and materials to fill bony defects which result from malformation, trauma or tumor resections. Other applications concern functional augmentations for dental implants or aesthetic augmentations in the facial region. For ostheosynthesis, mini- and microplates made from titanium alloys provide major advantages concerning biocompatibility, stability and individual fitting to the implant bed. The necessity of removing asymptomatic plates and screws after fracture healing is still a controversial issue. Risks and costs of secondary surgery for removal face a low rate of complications (due to corrosion products) when the material remains in situ. Resorbable osteosynthesis systems have similar mechanical stability and are especially useful in the growing skull. The huge variety of biomaterials for the reconstruction of bony defects makes it difficult to decide which material is adequate for which indication and for which site. The optimal biomaterial that meets every requirement (e.g. biocompatibility, stability, intraoperative fitting, product safety, low costs etc.) does not exist. The different material types are (autogenic) bone and many alloplastics such as metals (mainly titanium), ceramics, plastics and composites. Future developments aim to improve physical and biological properties, especially regarding surface interactions. To date, tissue engineered bone is far from routine clinical application. PMID:22073101

Ceramic Integration Technologies for Advanced Energy Systems: Critical Needs, Technical Challenges, and Opportunities

NASA Technical Reports Server (NTRS)

Singh, Mrityunjay

2010-01-01

Advanced ceramic integration technologies dramatically impact the energy landscape due to wide scale application of ceramics in all aspects of alternative energy production, storage, distribution, conservation, and efficiency. Examples include fuel cells, thermoelectrics, photovoltaics, gas turbine propulsion systems, distribution and transmission systems based on superconductors, nuclear power generation and waste disposal. Ceramic integration technologies play a key role in fabrication and manufacturing of large and complex shaped parts with multifunctional properties. However, the development of robust and reliable integrated systems with optimum performance requires the understanding of many thermochemical and thermomechanical factors, particularly for high temperature applications. In this presentation, various needs, challenges, and opportunities in design, fabrication, and testing of integrated similar (ceramic ceramic) and dissimilar (ceramic metal) material www.nasa.gov 45 ceramic-ceramic-systems have been discussed. Experimental results for bonding and integration of SiC based Micro-Electro-Mechanical-Systems (MEMS) LDI fuel injector and advanced ceramics and composites for gas turbine applications are presented.

Environment Conscious Ceramics (Ecoceramics): An Eco-Friendly Route to Advanced Ceramic Materials

NASA Technical Reports Server (NTRS)

Singh, M.

2001-01-01

Environment conscious ceramics (Ecoceramics) are a new class of materials, which can be produced with renewable natural resources (wood) or wood wastes (wood sawdust). This technology provides an eco-friendly route to advanced ceramic materials. Ecoceramics have tailorable properties and behave like ceramic materials manufactured by conventional approaches. Silicon carbide-based ecoceramics have been fabricated by reactive infiltration of carbonaceous preforms by molten silicon or silicon-refractory metal alloys. The fabrication approach, microstructure, and mechanical properties of SiC-based ecoceramics are presented.

Characterization of glass-infiltrated alumina-based ceramics

PubMed Central

Bona, Alvaro Della; Mecholsky, John J; Barrett, Allyson A; Griggs, Jason A

2010-01-01

Objective characterize the microstructure, composition, and important properties of glass-infiltrated alumina-based ceramics similar to the In-Ceram system. Methods Materials used were: IA- In-Ceram Alumina (Vita); IAE- IA electrophoretically deposited (Vita); AEM- IA using a vacuum driven method (Vita); VC- Vitro-Ceram (Angelus); TC- Turkom-Cera (Turkom-Ceramic); CC- Ceramcap (Foto-Ceram); and AG- Alglass (EDG). Ceramic specimens were fabricated following manufacturers’ instructions and ISO6872 standard and polished successively through 1μm alumina abrasive. Semi-quantitative and qualitative analyses were performed using scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS), and stereology (Vv). The elastic modulus (E) and Poisson’s ratio (ν) were determined using time-of-flight data measured in an ultrasonic pulser/receiver and the density (ρ) was determined using a helium pycnometer. Vicker’s indentation was used to calculate hardness (H). Bar specimens (25×4×1.2mm3) were loaded in three-point bending to fracture using a universal testing machine with cross-head speed of 1mm/min. Flexural strength (σ3P) was calculated and statistically analyzed using ANOVA, Tukey (α=0.05) and Weibull (m= modulus, σ0= characteristic strength). Results SEM and EDS analyses revealed similar microstructure for all ceramics, except for a lead-based matrix in CC and a zirconia phase in VC. TC, AG and CC showed significantly lower mean σ3P values than the other ceramics (p 0.05). AEM showed the greatest m (16). Conclusion Despite few differences in microstructure and composition, the IA, IAE, AEM and VC ceramics have similar properties. Significance The glass-infiltrated alumina-based ceramics from different manufacturers presented distinct characteristics. It is necessary to characterize new commercially available materials to understand their properties. PMID:18692231

Ceramics Curriculum: What Has It Been? What Could it Be?

ERIC Educational Resources Information Center

Sessions, Billie

1999-01-01

Reviews the traditional approach to ceramics education that focuses on studio-based, formalist curriculum and Modernist concerns. Argues for a comprehensive, or contextual, ceramics education in high school classrooms that would include contextual information about ceramic objects. Discusses example ceramic objects by various artists. (CMK)

Oxidation and Corrosion of Ceramics and Ceramic Matrix Composites

NASA Technical Reports Server (NTRS)

Jacobson, Nathan S.; Opila, Elizabeth J.; Lee, Kang N.

2000-01-01

Ceramics and ceramic matrix composites are candidates for numerous applications in high temperature environments with aggressive gases and possible corrosive deposits. There is a growing realization that high temperature oxidation and corrosion issues must be considered. There are many facets to these studies, which have been extensively covered in some recent reviews. The focus of this paper is on current research, over the past two years. In the authors' view, the most important oxidation and corrosion studies have focused on four major areas during this time frame. These are; (I) Oxidation of precursor-based ceramics; (II) Studies of the interphase material in ceramic matrix composites; (III) Water vapor interactions with ceramics, particularly in combustion environments; and (IV) Development of refractory oxide coatings for silicon-based ceramics. In this paper, we shall explore the most current work in each of these areas.

Pre-form ceramic matrix composite cavity and a ceramic matrix composite component

DOE Office of Scientific and Technical Information (OSTI.GOV)

Monaghan, Philip Harold; Delvaux, John McConnell; Taxacher, Glenn Curtis

A pre-form CMC cavity and method of forming pre-form CMC cavity for a ceramic matrix component includes providing a mandrel, applying a base ply to the mandrel, laying-up at least one CMC ply on the base ply, removing the mandrel, and densifying the base ply and the at least one CMC ply. The remaining densified base ply and at least one CMC ply form a ceramic matrix component having a desired geometry and a cavity formed therein. Also provided is a method of forming a CMC component.

Crystallization behaviors and seal application of basalt based glass-ceramics

NASA Astrophysics Data System (ADS)

Ateş, A.; Önen, U.; Ercenk, E.; Yılmaz, Ş.

2017-02-01

Basalt based glass-ceramics were prepared by conventional melt-quenching technique and subsequently converted to glass-ceramics by a controlled nucleation and crystallization process. Glass materials were obtained by melt at 1500°C and quenched in cold water. The powder materials were made by milling and spin coating. The powders were applied on the 430 stainless steel interconnector material, and heat treatment was carried out. The interface characteristics between the glass-ceramic layer and interconnector were investigated by using X-ray diffraction analysis (XRD) and scanning electron microscopy (SEM). The results showed that the basalt base glass-ceramic sealant material exhibited promising properties to use for SOFC.

Light Weight Biomorphous Cellular Ceramics from Cellulose Templates

NASA Technical Reports Server (NTRS)

Singh, Mrityunjay; Yee, Bo-Moon; Gray, Hugh R. (Technical Monitor)

2003-01-01

Bimorphous ceramics are a new class of materials that can be fabricated from the cellulose templates derived from natural biopolymers. These biopolymers are abundantly available in nature and are produced by the photosynthesis process. The wood cellulose derived carbon templates have three- dimensional interconnectivity. A wide variety of non-oxide and oxide based ceramics have been fabricated by template conversion using infiltration and reaction-based processes. The cellular anatomy of the cellulose templates plays a key role in determining the processing parameters (pyrolysis, infiltration conditions, etc.) and resulting ceramic materials. The processing approach, microstructure, and mechanical properties of the biomorphous cellular ceramics (silicon carbide and oxide based) have been discussed.

Evaluating adhesion reduction efficacy of type I/III collagen membrane and collagen-GAG resorbable matrix in primary flexor tendon repair in a chicken model.

PubMed

Turner, John B; Corazzini, Rubina L; Butler, Timothy J; Garlick, David S; Rinker, Brian D

2015-09-01

Reduction of peritendinous adhesions after injury and repair has been the subject of extensive prior investigation. The application of a circumferential barrier at the repair site may limit the quantity of peritendinous adhesions while preserving the tendon's innate ability to heal. The authors compare the effectiveness of a type I/III collagen membrane and a collagen-glycosaminoglycan (GAG) resorbable matrix in reducing tendon adhesions in an experimental chicken model of a "zone II" tendon laceration and repair. In Leghorn chickens, flexor tendons were sharply divided using a scalpel and underwent repair in a standard fashion (54 total repairs). The sites were treated with a type I/III collagen membrane, collagen-GAG resorbable matrix, or saline in a randomized fashion. After 3 weeks, qualitative and semiquantitative histological analysis was performed to evaluate the "extent of peritendinous adhesions" and "nature of tendon healing." The data was evaluated with chi-square analysis and unpaired Student's t test. For both collagen materials, there was a statistically significant improvement in the degree of both extent of peritendinous adhesions and nature of tendon healing relative to the control group. There was no significant difference seen between the two materials. There was one tendon rupture observed in each treatment group. Surgical handling characteristics were subjectively favored for type I/III collagen membrane over the collagen-GAG resorbable matrix. The ideal method of reducing clinically significant tendon adhesions after injury remains elusive. Both materials in this study demonstrate promise in reducing tendon adhesions after flexor tendon repair without impeding tendon healing in this model.

Fisetin antagonizes cell fusion, cytoskeletal organization and bone resorption in RANKL-differentiated murine macrophages.

PubMed

Kim, Yun-Ho; Kim, Jung-Lye; Lee, Eun-Jung; Park, Sin-Hye; Han, Seon-Young; Kang, Soon Ah; Kang, Young-Hee

2014-03-01

Osteoclastogenesis is comprised of several stage s including progenitor survival, differentiation to mononuclear preosteoclasts, cell fusion to multinuclear mature osteoclasts, and activation to osteoclasts with bone resorbing activity. Botanical antioxidants are now being increasingly investigated for their health-promoting effects on bone. This study investigated that fisetin, a flavonol found naturally in many fruits and vegetables, suppressed osteoclastogenesis by disturbing receptor activator of nuclear factor (NF)-κB ligand (RANKL)-mediated signaling pathway and demoting osteoclastogenic protein induction. Nontoxic fisetin at ≤10 μM inhibited the induction of RANK, tumor necrosis factor receptor associated factor 6 (TRAF6) and the activation of NF-κB in RANKL-stimulated RAW 264.7 macrophages. In RANKL-differentiated osteoclasts cell fusion protein of E-cadherin was induced, which was dampened by fisetin. The formation of tartrate-resistance acid phosphatase-positive multinucleated osteoclasts was suppressed by adding fisetin to RANKL-exposed macrophages. It was also found that fisetin reduced actin ring formation and gelsolin induction of osteclasts enhanced by RANKL through disturbing c-Src-proline-rich tyrosine kinase 2 signaling. Fisetin deterred preosteoclasts from the cell-cell fusion and the organization of the cytoskeleton to seal the resorbing area and to secret protons for bone resorption. Consistently, the 5 day-treatment of fisetin diminished RANKL-induced cellular expression of carbonic anhydrase II and integrin β3 concurrently with a reduction of osteoclast bone-resorbing activity. Therefore, fisetin was a natural therapeutic agent retarding osteoclast fusion and cytoskeletal organization such as actin rings and ruffled boarder, which is a property of mature osteoclasts and is required for osteoclasts to resorb bone. Copyright © 2014 Elsevier Inc. All rights reserved.

Protective effects of myricitrin against osteoporosis via reducing reactive oxygen species and bone-resorbing cytokines

DOE Office of Scientific and Technical Information (OSTI.GOV)

Huang, Qiang; Gao, Bo; Wang, Long

Oxidative stress is a crucial pathogenic factor in the development of osteoporosis. Myricitrin, isolated from Myrica cerifera, is a potent antioxidant. We hypothesized that myricitrin possessed protective effects against osteoporosis by partially reducing reactive oxygen species (ROS) and bone-resorbing cytokines in osteoblastic MC3T3-E1 cells and human bone marrow stromal cells (hBMSCs). We investigated myricitrin on osteogenic differentiation under oxidative stress. Hydrogen peroxide (H{sub 2}O{sub 2}) was used to establish an oxidative cell injury model. Our results revealed that myricitrin significantly improved some osteogenic markers in these cells. Myricitrin decreased lipid production and reduced peroxisome proliferator-activated receptor gamma-2 (PPARγ2) expression inmore » hBMSCs. Moreover, myricitrin reduced the expression of receptor activator of nuclear factor kappa-B ligand (RANKL) and IL-6 and partially suppressed ROS production. In vivo, we established a murine ovariectomized (OVX) osteoporosis model. Our results demonstrated that myricitrin supplementation reduced serum malondialdehyde (MDA) activity and increased reduced glutathione (GSH) activity. Importantly, it ameliorated the micro-architecture of trabecular bones in the 4th lumbar vertebrae (L4) and distal femur. Taken together, these results indicated that the protective effects of myricitrin against osteoporosis are linked to a reduction in ROS and bone-resorbing cytokines, suggesting that myricitrin may be useful in bone metabolism diseases, particularly osteoporosis. - Highlights: • Myricitrin protects MC3T3-E1 cells and hBMSCs from oxidative stress. • It is accompanied by a decrease in oxidative stress and bone-resorbing cytokines. • Myricitrin decreases serum reactive oxygen species to some degree. • Myricitrin partly reverses ovariectomy effects in vivo. • Myricitrin may represent a beneficial anti-osteoporosis treatment method.« less

PLZT Ceramic Driving Rotary Micro-mirror Based on Photoelectric-electrostatic Mechanism

NASA Astrophysics Data System (ADS)

Tang, Yujuan; Yang, Zhong; Chen, Yusong; Wang, Xinjie

2017-12-01

Based on the anomalous photovoltaic effect of PLZT, a rotary micro-mirror driven by hybrid photoelectric-electrostatic actuation of PLZT ceramic is proposed. Firstly, the mathematical modelling of coupled multi-physics fields of PLZT ceramic is established during illumination and light off phases. Then, the relationship between the rotation angle and the photovoltage of PLZT ceramics is established. In addition, the feasibility of rotary micro-mirror with hybrid photoelectric-electrostatic driving is verified via closed-loop control for photo-induced voltage of PLZT ceramic. The experimental results show that the photo-induced voltage of PLZT ceramics has good dynamic control precision using on-off closed-loop control method.

In-situ formation of multiphase deposited thermal barrier coatings

DOEpatents

Subramanian, Ramesh

2004-01-13

A multiphase ceramic thermal barrier coating is provided. The coating is adapted for use in high temperature applications in excess of about 1200.degree. C., for coating superalloy components of a combustion turbine engine. The coating comprises a ceramic single or two oxide base layer disposed on the substrate surface; and a ceramic oxide reaction product material disposed on the base layer, the reaction product comprising the reaction product of the base layer with a ceramic single or two oxide overlay layer.

All-ceramic or metal-ceramic tooth-supported fixed dental prostheses (FDPs)? A systematic review of the survival and complication rates. Part I: Single crowns (SCs).

PubMed

Sailer, Irena; Makarov, Nikolay Alexandrovich; Thoma, Daniel Stefan; Zwahlen, Marcel; Pjetursson, Bjarni Elvar

2015-06-01

To assess the 5-year survival of metal-ceramic and all-ceramic tooth-supported single crowns (SCs) and to describe the incidence of biological, technical and esthetic complications. Medline (PubMed), Embase, Cochrane Central Register of Controlled Trials (CENTRAL) searches (2006-2013) were performed for clinical studies focusing on tooth-supported fixed dental prostheses (FDPs) with a mean follow-up of at least 3 years. This was complimented by an additional hand search and the inclusion of 34 studies from a previous systematic review [1,2]. Survival and complication rates were analyzed using robust Poisson's regression models to obtain summary estimates of 5-year proportions. Sixty-seven studies reporting on 4663 metal-ceramic and 9434 all-ceramic SCs fulfilled the inclusion criteria. Seventeen studies reported on metal-ceramic crowns, and 54 studies reported on all-ceramic crowns. Meta-analysis of the included studies indicated an estimated survival rate of metal-ceramic SCs of 94.7% (95% CI: 94.1-96.9%) after 5 years. This was similar to the estimated 5-year survival rate of leucit or lithium-disilicate reinforced glass ceramic SCs (96.6%; 95% CI: 94.9-96.7%), of glass infiltrated alumina SCs (94.6%; 95% CI: 92.7-96%) and densely sintered alumina and zirconia SCs (96%; 95% CI: 93.8-97.5%; 92.1%; 95% CI: 82.8-95.6%). In contrast, the 5-year survival rates of feldspathic/silica-based ceramic crowns were lower (p<0.001). When the outcomes in anterior and posterior regions were compared feldspathic/silica-based ceramic and zirconia crowns exhibited significantly lower survival rates in the posterior region (p<0.0001), the other crown types performed similarly. Densely sintered zirconia SCs were more frequently lost due to veneering ceramic fractures than metal-ceramic SCs (p<0.001), and had significantly more loss of retention (p<0.001). In total higher 5 year rates of framework fracture were reported for the all-ceramic SCs than for metal-ceramic SCs. Survival rates of most types of all-ceramic SCs were similar to those reported for metal-ceramic SCs, both in anterior and posterior regions. Weaker feldspathic/silica-based ceramics should be limited to applications in the anterior region. Zirconia-based SCs should not be considered as primary option due to their high incidence of technical problems. Copyright © 2015 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Measuring Fracture Times Of Ceramics

NASA Technical Reports Server (NTRS)

Shlichta, Paul J.; Bister, Leo; Bickler, Donald G.

1989-01-01

Electrical measurements complement or replace fast cinematography. Electronic system measures microsecond time intervals between impacts of projectiles on ceramic tiles and fracture tiles. Used in research on ceramics and ceramic-based composite materials such as armor. Hardness and low density of ceramics enable them to disintegrate projectiles more efficiently than metals. Projectile approaches ceramic tile specimen. Penetrating foil squares of triggering device activate display and recording instruments. As ceramic and resistive film break oscilloscope plots increase in electrical resistance of film.

Alumina-based ceramic composite

DOEpatents

Alexander, Kathleen B.; Tiegs, Terry N.; Becher, Paul F.; Waters, Shirley B.

1996-01-01

An improved ceramic composite comprising oxide ceramic particulates, nonoxide ceramic particulates selected from the group consisting of carbides, borides, nitrides of silicon and transition metals and mixtures thereof, and a ductile binder selected from the group consisting of metallic, intermetallic alloys and mixtures thereof is described. The ceramic composite is made by blending powders of the ceramic particulates and the ductile to form a mixture and consolidating the mixture of under conditions of temperature and pressure sufficient to produce a densified ceramic composite.

Unusual extension of the first branchial cleft anomaly.

PubMed

Ada, Mehmet; Korkut, Nazim; Güvenç, M Güven; Acioğlu, Engin; Yilmaz, Süleyman; Cevikbaş, Uğur

2006-03-01

First branchial cleft is the only branchial structure that persists as the external ear canal, while all other clefts are resorbed. Incomplete obliteration and the degree of closure cause the varied types of first branchial cleft anomalies. They were classified based on the anatomical and histological features. We present an unusual type of first branchial cleft anomaly involving the external auditory canal, the middle ear and the nasopharynx through the eustachian tube.

Internal coating of zirconia restoration with silica-based ceramic improves bonding of resin cement to dental zirconia ceramic.

PubMed

Kitayama, Shuzo; Nikaido, Toru; Ikeda, Masaomi; Alireza, Sadr; Miura, Hiroyuki; Tagami, Junji

2010-01-01

Resin bonding to zirconia ceramic cannot be established by standard methods that are utilized for conventional silica-based dental ceramics. This study was aimed to examine the tensile bond strength of resin cement to zirconia ceramic using a new laboratory technique. Sixty-four zirconia ceramic specimens were air-abraded using Al2O3 particles and divided into two groups; the control group with no pretreatment (Control), and the group pretreated using the internal coating technique (INT), in which the surface of the zirconia specimens were thinly coated by fusing silica-based ceramic and air-abraded in the same manner. The specimens in each group were further divided into two subgroups according to the silane coupling agents applied; a mixture of dentin primer/silane coupling agent (Clearfil SE Bond Primer/Porcelain Bond Activator) or a newly developed single-component silane coupling agent (Clearfil Ceramic Primer). After bonding with dual-cured resin cement (Panavia F 2.0), they were stored in water for 24 h and half of them were additionally subjected to thermal cycling. The tensile bond strengths were tested using a universal testing machine. ANOVAs revealed significant influence of ceramic surface pretreatment (p<0.001), silane coupling agent (p<0.001) and thermal cycling (p<0.001); the INT coating technique significantly increased the bond strengths of resin cement to zirconia ceramic, whereas thermal cycling significantly decreased the bond strengths. The use of a single-component silane coupling agent demonstrated significantly higher bond strengths than that of a mixture of dentin primer/silane coupling agent. The internal coating of zirconia dental restorations with silica-based ceramic followed by silanization may be indicated in order to achieve better bonding for the clinical success.

Characterization of composite materials based on cement-ceramic powder blended binder

NASA Astrophysics Data System (ADS)

Kulovaná, Tereza; Pavlík, Zbyšek

2016-06-01

Characterization of newly developed composite mortars with incorporated ceramic powder coming from precise brick cutting as partial Portland cement replacement up to 40 mass% is presented in the paper. Fine ceramic powder belongs to the pozzolanic materials. Utilization of pozzolanic materials is accompanied by lower request on energy needed for Portland clinker production which generally results in lower production costs of blended binder and lower CO2 emission. In this paper, the ceramic powder is used in cement based mortar composition in amount of 8, 16, 24, 32, and 40 mass% of cement. Chemical composition of ceramic powder is analyzed by X-Ray Fluorescence and X-Ray Diffraction. The particle size distribution of ceramics is accessed on laser diffraction principle. For 28 days cured mortar samples, basic physical and mechanical properties are experimentally determined. The obtained results demonstrate that ceramic powder has potential to replace a part of Portland cement in composition of cement based composites and to reduce negative environmental impact of their production.

Characterization of composite materials based on cement-ceramic powder blended binder

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kulovaná, Tereza; Pavlík, Zbyšek

Characterization of newly developed composite mortars with incorporated ceramic powder coming from precise brick cutting as partial Portland cement replacement up to 40 mass% is presented in the paper. Fine ceramic powder belongs to the pozzolanic materials. Utilization of pozzolanic materials is accompanied by lower request on energy needed for Portland clinker production which generally results in lower production costs of blended binder and lower CO{sub 2} emission. In this paper, the ceramic powder is used in cement based mortar composition in amount of 8, 16, 24, 32, and 40 mass% of cement. Chemical composition of ceramic powder is analyzedmore » by X-Ray Fluorescence and X-Ray Diffraction. The particle size distribution of ceramics is accessed on laser diffraction principle. For 28 days cured mortar samples, basic physical and mechanical properties are experimentally determined. The obtained results demonstrate that ceramic powder has potential to replace a part of Portland cement in composition of cement based composites and to reduce negative environmental impact of their production.« less

[Homeostasis and Disorder of Musculoskeletal System.Cellular dynamics in musculoskeletal system visualized by intravital imaging techniques.

PubMed

Kikuta, Junichi; Ishii, Masaru

Bone is continually remodeled by bone-resorbing osteoclasts and bone-forming osteoblasts. Although it has long been believed that bone homeostasis is tightly regulated by communication between osteoclasts and osteoblasts, the fundamental process and dynamics have remained elusive. We originally established an advanced imaging system to visualize living bone tissues using intravital two-photon microscopy. By means of this system, we revealed the in vivo behavior of bone-resorbing osteoclasts and bone-forming osteoblasts in bone tissues. This approach facilitates investigation of cellular dynamics in the pathogenesis of musculoskeletal disorders, and would thus be useful for evaluating the efficacy of novel therapeutic agents.

A Novel Procedure for the Immediate Reconstruction of Severely Resorbed Alveolar Sockets for Advanced Periodontal Disease.

PubMed

Aimetti, Mario; Manavella, Valeria; Cricenti, Luca; Romano, Federica

2017-01-01

Background. Several clinical techniques and a variety of biomaterials have been introduced over the years in an effort to overcome bone remodeling and resorption after tooth extraction. However, the predictability of these procedures in sockets with severely resorbed buccal/lingual plate due to periodontal disease is still unknown. Case Description. A patient with advanced periodontitis underwent extraction of upper right lateral and central incisors. The central incisor exhibited complete buccal bone plate loss and a 9 mm vertical bone deficiency on its palatal side. The alveolar sockets were filled with collagen sponge and covered with a nonresorbable high-density PTFE membrane. Primary closure was not attained and any rigid scaffold material was not used. Histologic analysis provided evidence of new bone formation. At 12 months a cone-beam computed tomographic scan revealed enough bone volume to insert two conventional dental implants in conjunction with minor horizontal bone augmentation procedures. Clinical Implications. This case report would seem to support the potential of the proposed reconstructive approach in changing the morphology of severely resorbed alveolar sockets, minimizing the need for advanced bone regeneration procedures during implant placement.

A Novel Procedure for the Immediate Reconstruction of Severely Resorbed Alveolar Sockets for Advanced Periodontal Disease

PubMed Central

2017-01-01

Background. Several clinical techniques and a variety of biomaterials have been introduced over the years in an effort to overcome bone remodeling and resorption after tooth extraction. However, the predictability of these procedures in sockets with severely resorbed buccal/lingual plate due to periodontal disease is still unknown. Case Description. A patient with advanced periodontitis underwent extraction of upper right lateral and central incisors. The central incisor exhibited complete buccal bone plate loss and a 9 mm vertical bone deficiency on its palatal side. The alveolar sockets were filled with collagen sponge and covered with a nonresorbable high-density PTFE membrane. Primary closure was not attained and any rigid scaffold material was not used. Histologic analysis provided evidence of new bone formation. At 12 months a cone-beam computed tomographic scan revealed enough bone volume to insert two conventional dental implants in conjunction with minor horizontal bone augmentation procedures. Clinical Implications. This case report would seem to support the potential of the proposed reconstructive approach in changing the morphology of severely resorbed alveolar sockets, minimizing the need for advanced bone regeneration procedures during implant placement. PMID:28250998

Development and characterisation of silver-doped bioactive glass-coated sutures for tissue engineering and wound healing applications.

PubMed

Blaker, J J; Nazhat, S N; Boccaccini, A R

2004-01-01

A novel silver-doped bioactive glass powder (AgBG) was used to coat resorbable Vicryl (polyglactin 910) and non-resorbable Mersilk surgical sutures, thereby imparting bioactive, antimicrobial and bactericidal properties to the sutures. Stable and homogeneous coatings on the surface of the sutures were achieved using an optimised aqueous slurry-dipping technique. Dynamic mechanical analysis (DMA) was used to investigate the viscoelastic parameters of storage modulus and tandelta and thermal transitions of the as-received and composite (coated) sutures. The results generally showed that the bioactive glass coating did not affect the dynamic mechanical and thermal properties of the sutures. The in vitro bioactivity of the sutures was tested by immersion in simulated body fluid (SBF). After only 3 days of immersion in SBF, bonelike hydroxyapatite formed on the coated suture surfaces, indicating their enhanced bioactive behaviour. Resorbable sutures with bioactive coatings as fabricated here, in conjunction with 3-D textile technology, may provide attractive materials for producing 3-D scaffolds with controlled porosities for tissue engineering applications. The bactericidal properties imparted by the Ag-containing glass coating open also new opportunities for use of the composite sutures in wound healing and body wall repair.

Pre-form ceramic matrix composite cavity and method of forming and method of forming a ceramic matrix composite component

DOEpatents

Monaghan, Philip Harold; Delvaux, John McConnell; Taxacher, Glenn Curtis

2015-06-09

A pre-form CMC cavity and method of forming pre-form CMC cavity for a ceramic matrix component includes providing a mandrel, applying a base ply to the mandrel, laying-up at least one CMC ply on the base ply, removing the mandrel, and densifying the base ply and the at least one CMC ply. The remaining densified base ply and at least one CMC ply form a ceramic matrix component having a desired geometry and a cavity formed therein. Also provided is a method of forming a CMC component.

Alumina-based ceramic composite

DOEpatents

Alexander, K.B.; Tiegs, T.N.; Becher, P.F.; Waters, S.B.

1996-07-23

An improved ceramic composite comprising oxide ceramic particulates, nonoxide ceramic particulates selected from the group consisting of carbides, borides, nitrides of silicon and transition metals and mixtures thereof, and a ductile binder selected from the group consisting of metallic, intermetallic alloys and mixtures thereof is described. The ceramic composite is made by blending powders of the ceramic particulates and the ductile to form a mixture and consolidating the mixture of under conditions of temperature and pressure sufficient to produce a densified ceramic composite. 5 figs.

Effect of surface acid etching on the biaxial flexural strength of two hot-pressed glass ceramics.

PubMed

Hooshmand, Tabassom; Parvizi, Shaghayegh; Keshvad, Alireza

2008-07-01

The purpose of this study was to assess the effect of surface acid etching on the biaxial flexural strength of two hot-pressed glass ceramics reinforced by leucite or lithium disilicate crystals. Forty glass ceramic disks (14-mm diameter, 2-mm thick) consisting of 20 leucite-based ceramic disks (IPS Empress) and 20 lithia disilicate-based ceramic (IPS Empress 2) were produced by hot-pressing technique. All specimens were polished and then cleaned ultrasonically in distilled water. Ten specimens of each ceramic group were then etched with 9% hydrofluoric (HF) acid gel for 2 minutes and cleaned ultrasonically again. The biaxial flexural strength was measured by the piston-on-three-ball test in a universal testing machine. Data based on ten specimens in each group were analyzed by two-way ANOVA (alpha= 0.05). Microstructure of ceramic surfaces before and after acid etching was also examined by a scanning electron microscope. The mean biaxial flexural strength values for each group tested were (in MPa): nonetched IPS Empress = 118.6 +/- 25.5; etched IPS Empress = 102.9 +/- 15.4; nonetched IPS Empress 2 = 283.0 +/- 48.5; and etched IPS Empress 2 = 250.6 +/- 34.6. The results showed that the etching process reduced the biaxial flexural strengths significantly for both ceramic types (p= 0.025). No significant interaction between the ceramic type and etching process was found (p= 0.407). From the results, it was concluded that surface HF acid etching could have a weakening effect on hot-pressed leucite or lithia disilicate-based glass ceramic systems.

Joining and Assembly of Silicon Carbide-based Advanced Ceramics and Composites for High Temperature Applications

NASA Technical Reports Server (NTRS)

Singh, M.

2004-01-01

Silicon carbide based advanced ceramics and fiber reinforced composites are under active consideration for use in wide variety of high temperature applications within the aeronautics, space transportation, energy, and nuclear industries. The engineering designs of ceramic and composite component require fabrication and manufacturing of large and complex shaped parts of various thicknesses. In many instances, it is more economical to build up complex shapes by joining simple geometrical shapes. In addition these components have to be joined or assembled with metallic sub-components. Thus, joining and attachment have been recognized as enabling technologies for successful utilization of ceramic components in various demanding applications. In this presentation, various challenges and opportunities in design, fabrication, and testing o high temperature joints in ceramic matrix composites will be presented. Silicon carbide based advanced ceramics (CVD and hot pressed), and C/SiC and SiC/SiC composites, in different shapes and sizes, have been joined using an affordable, robust ceramic joining technology (ARCJoinT). Microstructure and high temperature mechanical properties of joints in silicon carbide ceramics and CVI and melt infiltrated SiC matrix composites will,be reported. Various joint design philosophies and design issues in joining of ceramics and composites well be discussed.

Spacecraft ceramic protective shield

NASA Technical Reports Server (NTRS)

Larriva, Rene F. (Inventor); Nelson, Anne (M.); Czechanski, James G. (Inventor); Poff, Ray E. (Inventor)

1995-01-01

A low areal density protective shield apparatus, and method for making same, for protecting spacecraft structures from impact with hypervelocity objects, including a bumper member comprising a bumper ceramic layer, a bumper shock attenuator layer, and a bumper confining layer. The bumper ceramic layer can be SiC or B.sub.4 C; the bumper shock attenuator layer can be zirconia felt; and the bumper confining layer can be aluminum. A base armor member can be spaced from the bumper member and a ceramic fiber-based curtain can be positioned between the bumper and base armor members.

Time-dependent fracture probability of bilayer, lithium-disilicate-based, glass-ceramic, molar crowns as a function of core/veneer thickness ratio and load orientation.

PubMed

Anusavice, Kenneth J; Jadaan, Osama M; Esquivel-Upshaw, Josephine F

2013-11-01

Recent reports on bilayer ceramic crown prostheses suggest that fractures of the veneering ceramic represent the most common reason for prosthesis failure. The aims of this study were to test the hypotheses that: (1) an increase in core ceramic/veneer ceramic thickness ratio for a crown thickness of 1.6mm reduces the time-dependent fracture probability (Pf) of bilayer crowns with a lithium-disilicate-based glass-ceramic core, and (2) oblique loading, within the central fossa, increases Pf for 1.6-mm-thick crowns compared with vertical loading. Time-dependent fracture probabilities were calculated for 1.6-mm-thick, veneered lithium-disilicate-based glass-ceramic molar crowns as a function of core/veneer thickness ratio and load orientation in the central fossa area. Time-dependent fracture probability analyses were computed by CARES/Life software and finite element analysis, using dynamic fatigue strength data for monolithic discs of a lithium-disilicate glass-ceramic core (Empress 2), and ceramic veneer (Empress 2 Veneer Ceramic). Predicted fracture probabilities (Pf) for centrally loaded 1.6-mm-thick bilayer crowns over periods of 1, 5, and 10 years are 1.2%, 2.7%, and 3.5%, respectively, for a core/veneer thickness ratio of 1.0 (0.8mm/0.8mm), and 2.5%, 5.1%, and 7.0%, respectively, for a core/veneer thickness ratio of 0.33 (0.4mm/1.2mm). CARES/Life results support the proposed crown design and load orientation hypotheses. The application of dynamic fatigue data, finite element stress analysis, and CARES/Life analysis represent an optimal approach to optimize fixed dental prosthesis designs produced from dental ceramics and to predict time-dependent fracture probabilities of ceramic-based fixed dental prostheses that can minimize the risk for clinical failures. Copyright © 2013 Academy of Dental Materials. All rights reserved.

Time-dependent fracture probability of bilayer, lithium-disilicate-based glass-ceramic molar crowns as a function of core/veneer thickness ratio and load orientation

PubMed Central

Anusavice, Kenneth J.; Jadaan, Osama M.; Esquivel–Upshaw, Josephine

2013-01-01

Recent reports on bilayer ceramic crown prostheses suggest that fractures of the veneering ceramic represent the most common reason for prosthesis failure. Objective The aims of this study were to test the hypotheses that: (1) an increase in core ceramic/veneer ceramic thickness ratio for a crown thickness of 1.6 mm reduces the time-dependent fracture probability (Pf) of bilayer crowns with a lithium-disilicate-based glass-ceramic core, and (2) oblique loading, within the central fossa, increases Pf for 1.6-mm-thick crowns compared with vertical loading. Materials and methods Time-dependent fracture probabilities were calculated for 1.6-mm-thick, veneered lithium-disilicate-based glass-ceramic molar crowns as a function of core/veneer thickness ratio and load orientation in the central fossa area. Time-dependent fracture probability analyses were computed by CARES/Life software and finite element analysis, using dynamic fatigue strength data for monolithic discs of a lithium-disilicate glass-ceramic core (Empress 2), and ceramic veneer (Empress 2 Veneer Ceramic). Results Predicted fracture probabilities (Pf) for centrally-loaded 1,6-mm-thick bilayer crowns over periods of 1, 5, and 10 years are 1.2%, 2.7%, and 3.5%, respectively, for a core/veneer thickness ratio of 1.0 (0.8 mm/0.8 mm), and 2.5%, 5.1%, and 7.0%, respectively, for a core/veneer thickness ratio of 0.33 (0.4 mm/1.2 mm). Conclusion CARES/Life results support the proposed crown design and load orientation hypotheses. Significance The application of dynamic fatigue data, finite element stress analysis, and CARES/Life analysis represent an optimal approach to optimize fixed dental prosthesis designs produced from dental ceramics and to predict time-dependent fracture probabilities of ceramic-based fixed dental prostheses that can minimize the risk for clinical failures. PMID:24060349

Current Issues with Environmental Barrier Coatings for Ceramics and Ceramic Composites

NASA Technical Reports Server (NTRS)

Lee, Kang N.

2004-01-01

The environmental barrier coating (EBC) for SiC/SiC ceramic matrix composites and Si3N4 ceramics is an emerging field as the application of silicon-based ceramics in the gas turbine engine hot section is on the horizon, both for aero and industrial gas turbines. EBC is an enabling technology for silicon-based ceramics because these materials without an EBC cannot be used in combustion environments due to rapid surface recession. Significant progress in EBC development has been made during the last decade through various government-sponsored programs. Current EBCs are based on silicon, mullite (3Al2O3-2SiO2) and BSAS (barium strontium aluminum silicate with celsian structure). Volatility of BSAS, BSAS-silica chemical reaction, and low melting point of silicon limit temperature capability of current EBCs to about 1350 C for long-term applications. There is a need for higher temperature EBCs as the temperature capability of silicon-based ceramics continue to increase. Therefore, research is underway to develop EBCs with improved temperature capability compared to current EBCs. The current status and issues with the advanced EBC development efforts will be discussed.

Interfacial adhesion of dental ceramic-resin systems

NASA Astrophysics Data System (ADS)

Della Bona, Alvaro

The clinical success of resin bonding procedures for indirect ceramic restorations and ceramic repairs depends on the quality and durability of the bond between the ceramic and the resin. The quality of this bond will depend upon the bonding mechanisms that are controlled in part by the surface treatment that promotes micromechanical and/or chemical bonding to the substrate. The objective of this study is to correlate interfacial toughness (K A) with fracture surface morphological parameters of the dental ceramic-resin systems as a function of ceramic surface treatment. The analytical procedures focused on characterizing the microstructure and fracture properties of EmpressRTM ceramics (a leucite-based core ceramic, two lithia disilicate-based core ceramics, and a glass veneer) and determining the ceramic-resin adhesion zone bond strength characteristics. Microstructure and composition are controlling factors in the development of micromechanical retention produced by etching. Silane treated ceramics negated the effect of surface roughening produced by etching, inducing lower surface energy of the ceramic and, reduced bonding effectiveness. There was a positive correlation between WA, tensile bond strength (a), and KA, i.e., higher mean WA value, and higher mean sigma and KA values. This study suggests that (1) the sigma and KA values for ceramic bonded to resin are affected by the ceramic microstructure and the ceramic surface treatments; (2) the definition of the adhesion zone is essential to classify the modes of failure, which should be an integral component of all failure analyses; (3) the microtensile test may be preferable to conventional shear or flexural tests as an indicator of composite-ceramic bond quality; and (4) careful microscopic analysis of fracture surfaces and an x-ray dot map can produce a more consistent and complete description of the fracture process and interpretation of the modes of failure. The mode of failure and fractographic analyses provide important a more comprehensive assessment of mechanisms that control the survival times of dental adhesive systems. Thus, the quality of the bond should not be assessed based on bond strength data alone.

Ceramic applications in turbine engines

NASA Technical Reports Server (NTRS)

Helms, H. E.; Heitman, P. W.; Lindgren, L. C.; Thrasher, S. R.

1984-01-01

The application of ceramic components to demonstrate improved cycle efficiency by raising the operating temperature of the existing Allison IGI 404 vehicular gas turbine engine is discussed. This effort was called the Ceramic Applications in Turbine Engines (CATE) program and has successfully demonstrated ceramic components. Among these components are two design configurations featuring stationary and rotating caramic components in the IGT 404 engine. A complete discussion of all phases of the program, design, materials development, fabrication of ceramic components, and testing-including rig, engine, and vehicle demonstation test are presented. During the CATE program, a ceramic technology base was established that is now being applied to automotive and other gas turbine engine programs. This technology base is outlined and also provides a description of the CATE program accomplishments.

Three-year clinical evaluation of two ceramic crown systems: a preliminary study.

PubMed

Etman, Maged K; Woolford, M J

2010-02-01

The clinical performance and failure mechanisms of recently introduced ceramic crown systems used to restore posterior teeth have not been adequately examined. The purpose of this prospective clinical study was to evaluate and compare the clinical performance of 2 new ceramic crown systems with that of metal ceramic crowns using modified United States Public Health Services (USPHS) criteria. Ninety posterior teeth requiring crown restorations in 48 patients were randomized into 3 equal groups (n=30) for which different crown systems were used: an experimental hot-pressed glass ceramic based on a modified lithium disilicate ceramic (IPS e.max Press), an alumina-coping-based ceramic (Procera AllCeram), and a metal ceramic (Simidur S 2 veneered with IPS Classic Porcelain). The crowns were assessed over 3 years using the modified USPHS criteria. Crowns that developed visible cracks were sectioned and removed, and the surfaces were analyzed using a scanning electron microscope (SEM). The data were analyzed using the Kruskal-Wallis nonparametric statistical test, followed by the Mann-Whitney test with Bonferroni correction (alpha=.05). USPHS evaluation showed that the IPS e.max Press and metal ceramic crowns experienced fewer clinical changes than Procera AllCeram. Visible roughness, wear, and deformity were noticed in occlusal contact areas of Procera AllCeram crowns. SEM images showed well defined wear facets in both ceramic crown systems. Kruskal-Wallis tests showed a significant difference (P<.05) in Alpha scores among the 3 crown systems. Mann-Whitney tests showed significant differences among groups. IPS e.max Press crowns demonstrated clinical behavior comparable to Procera AllCeram and metal ceramic crowns, but the wear resistance of this crown type was superior to the Procera AllCeram crowns, according to modified USPHS criteria.

[Biodegradable fixation systems in pediatric craniofacial surgery: 10-year experience with 324 patients].

PubMed

Yasonov, S A; Lopatin, A V; Bel'chenko, V A; Vasil'ev, I G

Over the past 15 years, resorbable materials have been successfully used for osteosynthesis, but their high cost prevents widespread application. However, the use of resorbable systems could be a method of choice, especially in treatment of children in the active growth period. Obviously, biodegradable materials not only are highly competitive with known metal constructs in terms of fixation rigidity, biocompatibility, and a low risk of infection but also have an undeniable advantage, such as gradual resorption allowing quick return of damaged bones to the physiological conditions of functioning. A special feature of bioresorbable systems is that they can be assembled using ultrasonic welding, which greatly facilitates the fixation process and also provides necessary rigidity, even in cases of joining very thin bones when reliable fixation with screws is impossible. Over the past 10 years, we have used biodegradable systems in 324 patients. In 244 of them, we used traditional (plate/screw) systems; in 80 cases, an ultrasonic welding system was chosen for osteosynthesis. In the present work, we discuss, based on clinical evidence, the advantages and disadvantages of both fixation systems for reconstructive craniofacial surgery in children.

Ceramic Integration Technologies for Aerospace and Energy Systems: Technical Challenges and Opportunities

NASA Technical Reports Server (NTRS)

Singh, Mrityunjay

2007-01-01

Ceramic integration technology has been recognized as an enabling technology for the implementation of advanced ceramic systems in a number of high-temperature applications in aerospace, power generation, nuclear, chemical, and electronic industries. Various ceramic integration technologies (joining, brazing, attachments, repair, etc.) play a role in fabrication and manufacturing of large and complex shaped parts of various functionalities. However, the development of robust and reliable integrated systems with optimum performance requires the understanding of many thermochemical and thermomechanical factors, particularly for high temperature applications. In this presentation, various challenges and opportunities in design, fabrication, and testing of integrated similar (ceramic-ceramic) and dissimilar (ceramic-metal) material systems will be discussed. Experimental results for bonding and integration of SiC based LDI fuel injector, high conductivity C/C composite based heat rejection system, solid oxide fuel cells system, ultra high temperature ceramics for leading edges, and ceramic composites for thermostructural applications will be presented. Potential opportunities and need for the development of innovative design philosophies, approaches, and integrated system testing under simulated application conditions will also be discussed.

Environmental durability of ceramics and ceramic composites

NASA Technical Reports Server (NTRS)

Fox, Dennis S.

1992-01-01

An account is given of the current understanding of the environmental durability of both monolithic ceramics and ceramic-matrix composites, with a view to the prospective development of methods for the characterization, prediction, and improvement of ceramics' environmental durability. Attention is given to the environmental degradation behaviors of SiC, Si3N4, Al2O3, and glass-ceramic matrix compositions. The focus of corrosion prevention in Si-based ceramics such as SiC and Si3N4 is on the high and low sulfur fuel combustion-product effects encountered in heat engine applications of these ceramics; sintering additives and raw material impurities are noted to play a decisive role in ceramics' high temperature environmental response.

The Effect of Luting Agents and Ceramic Thickness on the Color Variation of Different Ceramics against a Chromatic Background

PubMed Central

de Azevedo Cubas, Gloria Beatriz; Camacho, Guilherme Brião; Demarco, Flávio Fernando; Pereira-Cenci, Tatiana

2011-01-01

Objectives: The aim of this study was to assess the influence of various ceramic thicknesses and luting agents on color variation in five ceramic systems. Methods: Fifteen disc-shaped ceramic specimens (11 mm diameter; shade A3) were fabricated with each of the six veneering ceramics tested, with 1, 1.5, or 2 mm thickness (n=5). Resin composite discs (Z-250, shade C4) were used as bases to simulate a chromatic background. The cementation of the veneers was carried out with an opaque resin-based cement (Enforce, shade C4), a resin-based cement (Enforce, shade A3), or without cement (C4, control group). Color differences (ΔE*) were determined using a colorimeter. Three-way ANOVA was used to analyze the data, followed by a Tukey post-hoc test (α=.05). Results: The L*a*b* values of the ceramic systems were affected by both the luting agent and the ceramic thickness (P<.05). In general, there was no difference between the control group and the group using the resin-based cement. The use of an opaque luting agent resulted in an increase of the color coordinates a*, b*, L*, producing differences in ΔE* values for all ceramics tested, regardless of the thickness (P<.05). For the 2-mm thick veneers, higher values in the color parameters were obtained for all ceramics and were independent of the luting agent used. Conclusions: The association of 2-mm thickness with opaque cement presented the strongest masking ability of a dark colored background when compared to a non- opaque luting agent and the other thicknesses tested. PMID:21769264

Preparation of affordable and multifunctional clay-based ceramic filter matrix for treatment of drinking water.

PubMed

Shivaraju, H Puttaiah; Egumbo, Henok; Madhusudan, P; Anil Kumar, K M; Midhun, G

2018-02-01

Affordable clay-based ceramic filters with multifunctional properties were prepared using low-cost and active ingredients. The characterization results clearly revealed well crystallinity, structural elucidation, extensive porosity, higher surface area, higher stability, and durability which apparently enhance the treatment efficiency. The filtration rates of ceramic filter were evaluated under gravity and the results obtained were compared with a typical gravity slow sand filter (GSSF). All ceramic filters showed significant filtration rates of about 50-180 m/h, which is comparatively higher than the typical GSSF. Further, purification efficiency of clay-based ceramic filters was evaluated by considering important drinking water parameters and contaminants. A significant removal potential was achieved by the clay-based ceramic filter with 25% and 30% activated carbon along with active agents. Desired drinking water quality parameters were achieved by potential removal of nitrite (98.5%), nitrate (80.5%), total dissolved solids (62%), total hardness (55%), total organic pollutants (89%), and pathogenic microorganisms (100%) using ceramic filters within a short duration. The remarkable purification and disinfection efficiencies were attributed to the extensive porosity (0.202 cm 3  g -1 ), surface area (124.61 m 2  g -1 ), stability, and presence of active nanoparticles such as Cu, TiO 2 , and Ag within the porous matrix of the ceramic filter.

Mechanical Properties and Microstructure of Biomorphic Silicon Carbide Ceramics Fabricated from Wood Precursors

NASA Technical Reports Server (NTRS)

Singh, Mrityunjay; Salem, J. A.; Gray, Hugh R. (Technical Monitor)

2002-01-01

Silicon carbide based, environment friendly, biomorphic ceramics have been fabricated by the pyrolysis and infiltration of natural wood (maple and mahogany) precursors. This technology provides an eco-friendly route to advanced ceramic materials. These biomorphic silicon carbide ceramics have tailorable properties and behave like silicon carbide based materials manufactured by conventional approaches. The elastic moduli and fracture toughness of biomorphic ceramics strongly depend on the properties of starting wood preforms and the degree of molten silicon infiltration. Mechanical properties of silicon carbide ceramics fabricated from maple wood precursors indicate the flexural strengths of 3441+/-58 MPa at room temperature and 230136 MPa at 1350C. Room temperature fracture toughness of the maple based material is 2.6 +/- 0.2 MPa(square root of)m while the mahogany precursor derived ceramics show a fracture toughness of 2.0 +/- 0.2 Mpa(square root of)m. The fracture toughness and the strength increase as the density of final material increases. Fractographic characterization indicates the failure origins to be pores and chipped pockets of silicon.

Short-term implantation effects of a DCPD-based calcium phosphate cement.

PubMed

Frayssinet, P; Gineste, L; Conte, P; Fages, J; Rouquet, N

1998-06-01

Calcium phosphate cements can be handled in paste form and set in a wet medium after precipitation of calcium phosphate crystals in the implantation site. Depending on the products entering into the chemical reaction leading to the precipitation of calcium phosphates, different phases can be obtained with different mechanical properties, setting times and injectability. We tested a cement composed of a powder, containing beta-tricalcium phosphate (beta-TCP) and sodium pyrophosphate mixed with a solution of phosphoric and sulphuric acids. The cement set under a dicalcium phosphate dihydrate (DCPD)-based matrix containing beta-TCP particles. This was injected with a syringe into a defect drilled in rabbit condyles, the control being an identical defect left empty in the opposite condyle. The condyles were analysed histologically 2, 6 and 18 weeks after implantation. After injection into the bone defect the cement set and formed a porous calcium phosphate structure. Two different calcium phosphate phases with different solubility rates could be identified by scanning electron microscopy (SEM) observation. The less-soluble fragments could be degraded by cell phagocytosis in cell compartments of low pH or integrated in the newly formed bone matrix. The degradation rate of the material was relatively high but compatible with the ingrowth of bone trabeculae within the resorbing material. The ossification process was different from the creeping substitution occurring at the ceramic contact. Bone did not form directly at the cement surface following the differentiation of osteoblasts at the material surface. The trabeculae came to the material surface from the edges of the implantation site. Bone formation in the implantation site was significantly higher than in the control region during the first week of implantation. In conclusion, this material set in situ was well tolerated, inducing a mild foreign-body reaction, which did not impair its replacement by newly formed bone within a few weeks.

Acellular dermal matrix allograft. The results of controlled randomized clinical studies.

PubMed

Novaes, Arthur Belém; de Barros, Raquel Rezende Martins

2008-10-01

The aim of this presentation was to discuss the effectiveness of the acellular dermal matrix in root coverage therapy and in alveolar ridge augmentation, based on three controlled randomized clinical trials conducted by our research team (Novaes Jr et al., 2001; Barros et al., 2005; Luczyszyn et al., 2005). The first and second studies highlight the allograft's performance in the treatment of gingival recession. In both studies, clinical parameters were assessed prior to surgery and 6 or 12 months post-surgery. The first one compared the use of the acellular dermal matrix with the subepithelial connective tissue graft and showed 1.83 and 2.10 mm of recession reduction, respectively. Because no statistically significant differences between the groups were observed, it was concluded that the allograft can be used as a substitute for the autograft. In the second study, a new surgical approach was compared to a conventional surgical procedure described by Langer and Langer in 1985. A statistically significant greater recession reduction favoring the test procedure was achieved. The percentage of root coverage was 82.5% and 62.3% for test and control groups. Thus the new technique was considered more suitable for the treatment of gingival recessions with the allograft. Finally, the third study evaluated the allograft as a membrane, associated or not with a resorbable hydroxyapatite in bone regeneration to prevent ridge deformities. In one group the extraction sockets were covered only by the allograft and in the other, the alveoli were also filled with the resorbable hydroxyapatite. After six months, both treatments were able to preserve ridge thickness, considering the pre-operative values. In conclusion, no adverse healing events were noted with the use of allograft in site preservation procedures, and sites treated with the combination of allograft plus resorbable hydroxyapatite showed significantly greater ridge thickness preservation at six months when compared to sites treated with allograft alone (6.8 +/- 1.26 and 5.53 +/- 1.06 respectively).

Randomized, Controlled Clinical Trial of Bilayer Ceramic and Metal-Ceramic Crown Performance

PubMed Central

Esquivel-Upshaw, Josephine; Rose, William; Oliveira, Erica; Yang, Mark; Clark, Arthur E.; Anusavice, Kenneth

2013-01-01

Purpose Analyzing the clinical performance of restorative materials is important, as there is an expectation that these materials and procedures will restore teeth and do no harm. The objective of this research study was to characterize the clinical performance of metal-ceramic crowns, core ceramic crowns, and core ceramic/veneer ceramic crowns based on 11 clinical criteria. Materials and Methods An IRB-approved, randomized, controlled clinical trial was conducted as a single-blind pilot study. The following three types of full crowns were fabricated: (1) metal-ceramic crown (MC) made from a Pd-Au-Ag-Sn-In alloy (Argedent 62) and a glass-ceramic veneer (IPS d.SIGN veneer); (2) non-veneered (glazed) lithium disilicate glass-ceramic crown (LDC) (IPS e.max Press core and e.max Ceram Glaze); and (3) veneered lithia disilicate glass-ceramic crown (LDC/V) with glass-ceramic veneer (IPS Empress 2 core and IPS Eris). Single-unit crowns were randomly assigned. Patients were recalled for each of 3 years and were evaluated by two calibrated clinicians. Thirty-six crowns were placed in 31 patients. A total of 12 crowns of each of the three crown types were studied. Eleven criteria were evaluated: tissue health, marginal integrity, secondary caries, proximal contact, anatomic contour, occlusion, surface texture, cracks/chips (fractures), color match, tooth sensitivity, and wear (of crowns and opposing enamel). Numerical rankings ranged from 1 to 4, with 4 being excellent, and 1 indicating a need for immediate replacement. Statistical analysis of the numerical rankings was performed using a Fisher’s exact test. Results There was no statistically significant difference between performance of the core ceramic crowns and the two veneered crowns at year 1 and year 2 (p > 0.05). All crowns were rated either as excellent or good for each of the clinical criteria; however, between years 2 and 3, gradual roughening of the occlusal surface occurred in some of the ceramic-ceramic crowns, possibly caused by dissolution and wear of the glaze. Statistically significant differences in surface texture (p = 0.0013) and crown wear (p = 0.0078) were found at year 3 between the metal-ceramic crowns and the lithium-disilicate-based crowns. Conclusion Based on the 11 criteria, the clinical performance of ceramic-ceramic crowns was comparable to that of the metal-ceramic crowns after 2 years; however, gradual roughening occurred between years 2 and 3, which resulted in differences in surface texture and wear. PMID:22978697

High resolution ceramic gun for projection CRT

NASA Astrophysics Data System (ADS)

Muchi, T.; Tagami, S.; Saito, T.

1995-08-01

A ceramic resistor with high-resistivity and a low thermal coefficient has been developed. The use of this ceramic material as a cylindrical electrode realizes an electrostatic lens with low spherical aberration. A ceramic electron gun based on a new concept has been developed for high resolution projection CRTs.

Geopolymer Porous Nanoceramics for Structural Smart and Thermal Shock Resistant Applications

DTIC Science & Technology

2011-02-02

porous membranes and foams, ceramic armor composites , iron-based geopolymer analogues, geopolymer composites reinforced with chopped polypropylene... geopolymers and geopolymer composites , as fabricated and upon conversion to ceramics with heating. The microstucture consisted of nanoporous...ceramic armore composites , iron-based geopolymer analogues, geopolymer composites reinforced with chopped polypropylene or basalt fibers and

Some developments on ceramic-to-metal and glass-ceramics-to-metal seals and related studies

NASA Astrophysics Data System (ADS)

Kothiyal, G. P.; Goswami, M.; Shrikhande, V. K.

2008-05-01

Seals and coatings based on ceramics and glass-ceramics find numerous applications in different disciplines of science and technology including space, accelerators, nuclear energy, chemical industry. Ceramic-to-metal (CM) seals based on conventional design (using brazing alloys) and glass-ceramics have been prepared. While Ag-Cu brazing alloy has been used in conventional CM seal, we have employed lithium zinc silicate (LZS) and lithium aluminum silicate (LAS) glass-ceramics for glass-ceramics-to-metal (GCM) seals. LZS glass-ceramics based on two different compositions; (a) LZSL composition (wt.%)- Li2O: 12.65, ZnO: 1.85, SiO2: 74.4, Al2O3: 3.8, K2O: 2.95, P2O5: 3.15, and B2O3: 1.2 (low ZnO) and (b) LZSH composition (wt.%)- Li2O: 8.9, ZnO: 24.03, SiO2: 53.7, Na2O: 5.42, P2O5: 2.95, and B2O3: 5.0 (high ZnO) were prepared with desired sealing characteristics for matched type seals. In addition, (wt.%) 12.6Li2O-71.7SiO2-5.1Al2O3-4.9K2O-3.2B2O3-2.5P2O5 (LAS-GC) was investigated for compressive type of seal. LZS glass-ceramics-to-Cu as well as SS-321 seals were found to withstand a vacuum of 10-6 Torr with leak rate 10-9 Torr. 1/s and LAS GC-to-SS304 seal showed high pressure endurance of 12000psi. In order to understand the mechanism of sealing, glass-ceramics-to-metal interface study has also been carried out.

A flexible, robust and antifouling asymmetric membrane based on ultra-long ceramic/polymeric fibers for high-efficiency separation of oil/water emulsions.

PubMed

Wang, Kui; Yiming, Wubulikasimu; Saththasivam, Jayaprakash; Liu, Zhaoyang

2017-07-06

Polymeric and ceramic asymmetric membranes have dominated commercial membranes for water treatment. However, polymeric membranes are prone to becoming fouled, while ceramic membranes are mechanically fragile. Here, we report a novel concept to develop asymmetric membranes based on ultra-long ceramic/polymeric fibers, with the combined merits of good mechanical stability, excellent fouling resistance and high oil/water selectivity, in order to meet the stringent requirements for practical oil/water separation. The ultra-long dimensions of ceramic nanofibers/polymeric microfibers endow this novel membrane with mechanical flexibility and robustness, due to the integrated and intertwined structure. This membrane is capable of separating oil/water emulsions with high oil-separation efficiency (99.9%), thanks to its nanoporous selective layer made of ceramic nanofibers. Further, this membrane also displays superior antifouling properties due to its underwater superoleophobicity and ultra-low oil adhesion of the ceramic-based selective layer. This membrane exhibits high water permeation flux (6.8 × 10 4 L m -2 h -1 bar -1 ) at low operation pressures, which is attributed to its 3-dimensional (3D) interconnected fiber-based structure throughout the membrane. In addition, the facile fabrication process and inexpensive materials required for this membrane suggest its significant potential for industrial applications.

Does implant coating with antibacterial-loaded hydrogel reduce bacterial colonization and biofilm formation in vitro?

PubMed

Drago, Lorenzo; Boot, Willemijn; Dimas, Kostantinos; Malizos, Kostantinos; Hänsch, Gertrud M; Stuyck, Jos; Gawlitta, Debby; Romanò, Carlo L

2014-11-01

Implant-related infections represent one of the most severe complications in orthopaedics. A fast-resorbable, antibacterial-loaded hydrogel may reduce or prevent bacterial colonization and biofilm formation of implanted biomaterials. We asked: (1) Is a fast-resorbable hydrogel able to deliver antibacterial compounds in vitro? (2) Can a hydrogel (alone or antibacterial-loaded) coating on implants reduce bacterial colonization? And (3) is intraoperative coating feasible and resistant to press-fit implant insertion? We tested the ability of Disposable Antibacterial Coating (DAC) hydrogel (Novagenit Srl, Mezzolombardo, Italy) to deliver antibacterial agents using spectrophotometry and a microbiologic assay. Antibacterial and antibiofilm activity were determined by broth microdilution and a crystal violet assay, respectively. Coating resistance to press-fit insertion was tested in rabbit tibias and human femurs. Complete release of all tested antibacterial compounds was observed in less than 96 hours. Bactericidal and antibiofilm effect of DAC hydrogel in combination with various antibacterials was shown in vitro. Approximately 80% of the hydrogel coating was retrieved on the implant after press-fit insertion. Implant coating with an antibacterial-loaded hydrogel reduces bacterial colonization and biofilm formation in vitro. A fast-resorbable, antibacterial-loaded hydrogel coating may help prevent implant-related infections in orthopaedics. However, further validation in animal models and properly controlled human studies is required.

A hybrid technique for sinus floor elevation in the severely resorbed posterior maxilla

PubMed Central

Jung, Ui-Won; Hong, Ji-Youn; Lee, Jung-Seok; Kim, Chang-Sung; Cho, Kyoo-Sung

2010-01-01

Purpose This study aimed to evaluate the effectiveness of the modified sinus floor elevation technique described hereafter as a "hybrid technique," in 11 patients with severely resorbed posterior maxillae. Methods Eleven patients who received 22 implants in the maxillary premolar and molar areas by the hybrid technique were enrolled in this study. A slot-shaped osteotomy for access was prepared on the lateral wall along the lower border of the sinus floor. The Schneiderian membrane was fully reflected through the lateral slot. Following drilling with the membrane protected by a periosteal elevator, the bone was grafted. All implants were placed simultaneously with sinus augmentation. The cumulative success rate was calculated and clinical parameters were recorded. Radiographic measurements were performed. Results All implants were well maintained at last follow up (cumulative success rate=100%). The mean residual bone height, augmented bone height, crown-to-implant ratio, and marginal bone loss were 4.1±1.64 mm, 8.76±1.77 mm, 1.21±0.33 mm, and 0.34±0.72 mm, respectively. Conclusions Simultaneous implant placement with sinus augmentation by hybrid technique showed successful clinical results over a 2-year observation period and may be a reliable modality for reconstruction of a severely resorbed posterior maxilla. PMID:20498764

A new classification system for all-ceramic and ceramic-like restorative materials.

PubMed

Gracis, Stefano; Thompson, Van P; Ferencz, Jonathan L; Silva, Nelson R F A; Bonfante, Estevam A

2015-01-01

Classification systems for all-ceramic materials are useful for communication and educational purposes and warrant continuous revisions and updates to incorporate new materials. This article proposes a classification system for ceramic and ceramic-like restorative materials in an attempt to systematize and include a new class of materials. This new classification system categorizes ceramic restorative materials into three families: (1) glass-matrix ceramics, (2) polycrystalline ceramics, and (3) resin-matrix ceramics. Subfamilies are described in each group along with their composition, allowing for newly developed materials to be placed into the already existing main families. The criteria used to differentiate ceramic materials are based on the phase or phases present in their chemical composition. Thus, an all-ceramic material is classified according to whether a glass-matrix phase is present (glass-matrix ceramics) or absent (polycrystalline ceramics) or whether the material contains an organic matrix highly filled with ceramic particles (resin-matrix ceramics). Also presented are the manufacturers' clinical indications for the different materials and an overview of the different fabrication methods and whether they are used as framework materials or monolithic solutions. Current developments in ceramic materials not yet available to the dental market are discussed.

Transient, biocompatible electronics and energy harvesters based on ZnO.

PubMed

Dagdeviren, Canan; Hwang, Suk-Won; Su, Yewang; Kim, Stanley; Cheng, Huanyu; Gur, Onur; Haney, Ryan; Omenetto, Fiorenzo G; Huang, Yonggang; Rogers, John A

2013-10-25

The combined use of ZnO, Mg, MgO, and silk provides routes to classes of thin-film transistors and mechanical energy harvesters that are soluble in water and biofluids. Experimental and theoretical studies of the operational aspects and dissolution properties of this type of transient electronics technology illustrate its various capabilities. Application opportunities range from resorbable biomedical implants, to environmentally dissolvable sensors, and degradable consumer electronics. Copyright © 2013 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Cement-based piezoelectric ceramic composites for sensor applications in civil engineering

NASA Astrophysics Data System (ADS)

Dong, Biqin

The objectives of this thesis are to develop and apply a new smart composite for the sensing and actuation application of civil engineering. Piezoelectric ceramic powder is incorporated into cement-based composite to achieve the sensing and actuation capability. The research investigates microstructure, polarization and aging, material properties and performance of cement-based piezoelectric ceramic composites both theoretically and experimentally. A hydrogen bonding is found at the interface of piezoelectric ceramic powder and cement phase by IR (Infrared Ray), XPS (X-ray Photoelectron Spectroscopy) and SIMS (Secondary Ion Mass Spectroscopy). It largely affects the material properties of composites. A simple first order model is introduced to explain the poling mechanism of composites and the dependency of polarization is discussed using electromechanical coupling coefficient kt. The mechanisms acting on the aging effect is explored in detail. Dielectrical, piezoelectric and mechanical properties of the cement-based piezoelectric ceramic composites are studied by experiment and theoretical calculation based on modified cube model (n=1) with chemical bonding . A complex circuit model is proposed to explain the unique feature of impedance spectra and the instinct of high-loss of cement-based piezoelectric ceramic composite. The sensing ability of cement-based piezoelectric ceramic composite has been evaluated by using step wave, sine wave, and random wave. It shows that the output of the composite can reflects the nature and characteristics of mechanical input. The work in this thesis opens a new direction for the current actuation/sensing technology in civil engineering. The materials and techniques, developed in this work, have a great potential in application of health monitoring of buildings and infrastructures.

The Recent Revolution in the Design and Manufacture of Cranial Implants: Modern Advancements and Future Directions

PubMed Central

Bonda, David J.; Manjila, Sunil; Selman, Warren R.; Dean, David

2015-01-01

Large format (i.e., > 25 cm2) cranioplasty is a challenging procedure not only from a cosmesis standpoint, but also in terms of ensuring that the patient's brain will be well-protected from direct trauma. Until recently, when a patient's own cranial flap was unavailable, these goals were unattainable. Recent advances in implant Computer Aided Design and 3-D printing are leveraging other advances in regenerative medicine. It is now possible to 3-D-print patient-specific implants from a variety of polymer, ceramic, or metal components. A skull template may be used to design the external shape of an implant that will become well integrated in the skull, while also providing beneficial distribution of mechanical force distribution in the event of trauma. Furthermore, an internal pore geometry can be utilized to facilitate the seeding of banked allograft cells. Implants may be cultured in a bioreactor along with recombinant growth factors to produce implants coated with bone progenitor cells and extracellular matrix that appear to the body as a graft, albeit a tissue-engineered graft. The growth factors would be left behind in the bioreactor and the graft would resorb as new host bone invades the space and is remodeled into strong bone. As we describe in this review, such advancements will lead to optimal replacement of cranial defects that are both patient-specific and regenerative. PMID:26171578

Geopolymer Porous Nanoceramics for Structural, for Smart and Thermal Shock Resistant Applications

DTIC Science & Technology

2011-02-02

porous membranes and foams, ceramic armor composites , iron-based geopolymer analogues, geopolymer composites reinforced with chopped polypropylene...the microstructure of geopolymers and geopolymer composites , as fabricated and upon conversion to ceramics with heating. The microstructure consisted...porous membranes and foams, ceramic armor composites , iron-based geopolymer analogues, geopolymer composites reinforced with chopped polypropylene or

A hybrid phenomenological model for ferroelectroelastic ceramics. Part II: Morphotropic PZT ceramics

NASA Astrophysics Data System (ADS)

Stark, S.; Neumeister, P.; Balke, H.

2016-10-01

In this part II of a two part series, the rate-independent hybrid phenomenological constitutive model introduced in part I is modified to account for the material behavior of morphotropic lead zirconate titanate ceramics (PZT ceramics). The modifications are based on a discussion of the available literature results regarding the micro-structure of these materials. In particular, a monoclinic phase and a highly simplified representation of the hierarchical structure of micro-domains and nano-domains observed experimentally are incorporated into the model. It is shown that experimental data for the commercially available morphotropic PZT material PIC151 (PI Ceramic GmbH, Lederhose, Germany) can be reproduced and predicted based on the modified hybrid model.

Light emitting ceramic device

DOEpatents

Valentine, Paul; Edwards, Doreen D.; Walker, Jr., William John; Slack, Lyle H.; Brown, Wayne Douglas; Osborne, Cathy; Norton, Michael; Begley, Richard

2010-05-18

A light-emitting ceramic based panel, hereafter termed "electroceramescent" panel, is herein claimed. The electroceramescent panel is formed on a substrate providing mechanical support as well as serving as the base electrode for the device. One or more semiconductive ceramic layers directly overlay the substrate, and electrical conductivity and ionic diffusion are controlled. Light emitting regions overlay the semiconductive ceramic layers, and said regions consist sequentially of a layer of a ceramic insulation layer and an electroluminescent layer, comprised of doped phosphors or the equivalent. One or more conductive top electrode layers having optically transmissive areas overlay the light emitting regions, and a multi-layered top barrier cover comprising one or more optically transmissive non-combustible insulation layers overlay said top electrode regions.

Bioactive ceramic-based materials with designed reactivity for bone tissue regeneration

PubMed Central

Ohtsuki, Chikara; Kamitakahara, Masanobu; Miyazaki, Toshiki

2009-01-01

Bioactive ceramics have been used clinically to repair bone defects owing to their biological affinity to living bone; i.e. the capability of direct bonding to living bone, their so-called bioactivity. However, currently available bioactive ceramics do not satisfy every clinical application. Therefore, the development of novel design of bioactive materials is necessary. Bioactive ceramics show osteoconduction by formation of biologically active bone-like apatite through chemical reaction of the ceramic surface with surrounding body fluid. Hence, the control of their chemical reactivity in body fluid is essential to developing novel bioactive materials as well as biodegradable materials. This paper reviews novel bioactive materials designed based on chemical reactivity in body fluid. PMID:19158015

On the influence of particle morphology on the post-impact ballistic response of ceramic armour materials

NASA Astrophysics Data System (ADS)

Hameed, Amer; Appleby-Thomas, Gareth; Wood, David; Jaansalu, Kevin

2015-06-01

Recent studies have shown evidence that the ballistic-resistance of fragmented (comminuted) ceramics is independent of the original strength of the material. In particular, experimental investigations into the ballistic behaviour of such fragmented ceramics have indicated that this response is correlated to shattered ceramic morphology. This suggests that careful control of ceramic microstructure - and therefore failure paths - might provide a route to optimise post-impact ballistic performance, thereby enhancing multi-hit capability. In this study, building on previous in-house work, ballistic tests were conducted using pre-formed `fragmented-ceramic' analogues based around three morphologically differing (but chemically identical) alumina feedstock materials compacted into target `pucks. In an evolution of previous work, variation of target thickness provided additional insight into an apparent morphology-based contribution to ballistic response.

Ceramic technology for advanced heat engines project. Semiannual progress report, April-September 1985

DOE Office of Scientific and Technical Information (OSTI.GOV)

Not Available

1986-05-01

An assessment of needs was completed, and a five-year project plan was developed with input from private industry. Objective is to develop the industrial technology base required for reliable ceramics for application in advanced automotive heat engines. Focus is on structural ceramics for advanced gas turbine and diesel engines, ceramic bearings and attachments, and ceramic coatings for thermal barrier and wear applications in these engines. The work described in this report is organized according to the following WBS project elements: management and coordination; materials and processing (monolithics, ceramic composites, thermal and wear coatings, joining); materials design methodology (contact interfaces, newmore » concepts); data base and life prediction (time-dependent behavior, environmental effects, fracture mechanics, NDE development); and technology transfer. This report includes contributions from all currently active project participants.« less

Ceramic Technology for Advanced Heat Engines Project

DOE Office of Scientific and Technical Information (OSTI.GOV)

Not Available

1989-08-01

The Ceramic Technology for Advanced Heat Engines Project was developed by the Department of Energy's Office of Transportation Systems (OTS) in Conservation and Renewable Energy. This project, part of the OTS's Advanced Materials Development Program, was developed to meet the ceramic technology requirements of the OTS's automotive technology programs. Significant accomplishments in fabricating ceramic components for the Department of Energy (DOE), National Aeronautics and Space Administration (NASA), and Department of Defense (DoD) advanced heat engine programs have provided evidence that the operation of ceramic parts in high-temperature engine environments is feasible. However, these programs have also demonstrated that additional researchmore » is needed in materials and processing development, design methodology, and data base and life prediction before industry will have a sufficient technology base from which to produce reliable cost-effective ceramic engine components commercially.« less

Ceramic Technology For Advanced Heat Engines Project

DOE Office of Scientific and Technical Information (OSTI.GOV)

Not Available

1990-12-01

Significant accomplishments in fabricating ceramic components for the Department of Energy (DOE), National Aeronautics and Space Administration (NASA), and Department of Defense (DoD) advanced heat engine programs have provided evidence that the operation of ceramic parts in high-temperature engine environments is feasible. However, these programs have also demonstrated that additional research is needed in materials and processing development, design methodology, and data base and life prediction before industry will have a sufficient technology base from which to produce reliable cost-effective ceramic engine components commercially. The objective of the project is to develop the industrial technology base required for reliable ceramicsmore » for application in advanced automotive heat engines. The project approach includes determining the mechanisms controlling reliability, improving processes for fabricating existing ceramics, developing new materials with increased reliability, and testing these materials in simulated engine environments to confirm reliability. Although this is a generic materials project, the focus is on the structural ceramics for advanced gas turbine and diesel engines, ceramic bearings and attachments, and ceramic coatings for thermal barrier and wear applications in these engines. This advanced materials technology is being developed in parallel and close coordination with the ongoing DOE and industry proof of concept engine development programs. To facilitate the rapid transfer of this technology to U.S. industry, the major portion of the work is being done in the ceramic industry, with technological support from government laboratories, other industrial laboratories, and universities. Abstracts prepared for appropriate papers.« less

Properties and Clinical Application of Three Types of Dental Glass-Ceramics and Ceramics for CAD-CAM Technologies

PubMed Central

Ritzberger, Christian; Apel, Elke; Höland, Wolfram; Peschke, Arnd; Rheinberger, Volker M.

2010-01-01

The main properties (mechanical, thermal and chemical) and clinical application for dental restoration are demonstrated for three types of glass-ceramics and sintered polycrystalline ceramic produced by Ivoclar Vivadent AG. Two types of glass-ceramics are derived from the leucite-type and the lithium disilicate-type. The third type of dental materials represents a ZrO2 ceramic. CAD/CAM technology is a procedure to manufacture dental ceramic restoration. Leucite-type glass-ceramics demonstrate high translucency, preferable optical/mechanical properties and an application as dental inlays, onlays and crowns. Based on an improvement of the mechanical parameters, specially the strength and toughness, the lithium disilicate glass-ceramics are used as crowns; applying a procedure to machine an intermediate product and producing the final glass-ceramic by an additional heat treatment. Small dental bridges of lithium disilicate glass-ceramic were fabricated using a molding technology. ZrO2 ceramics show high toughness and strength and were veneered with fluoroapatite glass-ceramic. Machining is possible with a porous intermediate product.

Wear properties of alumina/zirconia composite ceramics for joint prostheses measured with an end-face apparatus.

PubMed

Morita, Yusuke; Nakata, Kenichi; Kim, Yoon-Ho; Sekino, Tohru; Niihara, Koichi; Ikeuchi, Ken

2004-01-01

While only alumina is applied to all-ceramic joint prostheses at present, a stronger ceramic is required to prevent fracture and chipping due to impingement and stress concentration. Zirconia could be a potential substitute for alumina because it has high strength and fracture toughness. However, the wear of zirconia/zirconia combination is too high for clinical use. Although some investigations on composite ceramics revealed that mixing of different ceramics was able to improve the mechanical properties of ceramics, there are few reports about wear properties of composite ceramics for joint prosthesis. Since acetabular cup and femoral head of artificial hip joint are finished precisely, they indicate high geometric conformity. Therefore, wear test under flat contact was carried out with an end-face wear testing apparatus for four kinds of ceramics: alumina monolith, zirconia monolith, alumina-based composite ceramic, and zirconia based composite ceramic. Mean contact pressure was 10 MPa and sliding velocity was 40 mm/s. The wear test continued for 72 hours and total sliding distance was 10 km. After the test, the wear factor was calculated. Worn surfaces were observed with a scanning electron micrograph (SEM). The results of this wear test show that the wear factors of the both composite ceramics are similarly low and their mechanical properties are much better than those of the alumina monolith and the zirconia monolith. According to these results, it is predicted that joint prostheses of the composite ceramics are safer against break down and have longer lifetime compared with alumina/alumina joint prostheses.

Cost-effective method for determining the grindability of ceramics. Final report

DOE Office of Scientific and Technical Information (OSTI.GOV)

Guo, C.; Chand, R.H.

1997-02-01

The objective of this program was to develop a cost-effective method to determine the grindability of ceramics leading to cost-effective methods for machining such ceramics. In this first phase of activity, Chand Kare Technical Ceramics directed its efforts towards development of a definition for ceramic grindability, design of grindability-test experiments, and development of a ceramics-grindability test system (CGTS). The grindability study also included the establishment of the correlation between the grindability and conventional grinding practices. The above goals were achieved. A definition based on material removal rate under controlled force grinding was developed. Three prototypes CGTSs were developed and tested;more » suitable design was identified. Based on this, a fully automatic CGTS was developed and is ready for delivery to Oak Ridge National Laboratory. Comprehensive grindability tests for various commercially available engineering ceramics were conducted. Experimental results indicated that ceramics have significantly different grindabilities even though their mechanical properties were not significantly different. This implies that grindability of ceramics can be greatly improved. Further study is needed to establish correlations between microstructure and grindability. Therefore, grindability should be evaluated during the development of new ceramics or improvement of existing ones. In this report, the development of the ceramic-grindability definition, the development of CGTS, extensive grindability results, and the preliminary correlation between grindability and mechanical properties (such as flexural strength, hardness, elastic modulus, and fracture toughness) were summarized.« less

Histologic analysis of resorbable blasting media surface implants retrieved from humans: a report of two cases

PubMed Central

2016-01-01

The purpose of this study is to evaluate the degree of osseointegration of resorbable blasting media (RBM) surface implants retrieved from humans. Three implants in the mandibular molar region that were surface-treated with RBM were retrieved from two patients. The implants were used to manufacture specimens in order to measure the bone-implant contact (BIC) ratio. The BIC ratios of the three implants were found to be an average of 69.0%±9.1%. In conclusion, that RBM surface implants are integrated into the host environment with histological significance and the BIC ratio of the RBM surface-treated implant was not significantly different from that of other surface-treated implants. PMID:26904493

Resorbable poly(D,L)lactide plates and screws for osteosynthesis of condylar neck fractures in sheep.

PubMed

Rasse, Michael; Moser, Doris; Zahl, Christian; Gerlach, Klaus Louis; Eckelt, Uwe; Loukota, Richard

2007-01-01

We made osteotomies in the condylar neck in 12 adult sheep to simulate fractures, and joined the two ends with 2 poly(D,L)lactide (PDLLA) plates and 8 PDLLA screws 2mm in diameter. The animals were killed after 2, 6, and 12 months and bony healing was assessed macroscopically and histologically. The plates and screws remained intact and there was no displacement of the bony ends. The degrading plates, which were still visible in the specimens after 6 months, had been replaced by bone. At 12 months the PDLLA had been resorbed with no foreign body reaction and no resorption of underlying bone. The articular discs showed no signs of degeneration.

Dental rehabilitation using an implant-carrying plate system in a severely resorbed edentulous maxilla: a case report.

PubMed

Kurita, Hiroshi; Sakai, Hironori; Uehara, Shinobu; Kurashina, Kenji

2008-01-01

This clinical article describes a case of dental rehabilitation using an implant-carrying plate system (EPITEC) for a patient with severely resorbed edentulous maxilla and microstomia. In this case, the presence of microstomia prevented bone augmentation procedures through an intraoral approach. Treatment using 2 endosseous implants inserted in the canine regions and an implant-supported overdenture was planned. However, endosseous implants were not feasible on the right side because of insufficient available bone volume. An implant-carrying plate system was then utilized on the right side. Four months later, an implant-supported ball-attachment overdenture was fabricated. At the 2-year follow-up, the clinical course remained uneventful, and the patient remained satisfied with the treatment.

Analysis of Shear Bond Strength and Morphology of Er:YAG Laser-Recycled Ceramic Orthodontic Brackets.

PubMed

Han, Ruo-qiao; Yang, Kai; Ji, Ling-fei; Ling, Chen

2016-01-01

The aim of this study was to compare the recycling of deboned ceramic brackets via an Er:YAG laser or via the traditional chairside processing methods of flaming and sandblasting; shear bond strength and morphological changes were evaluated in recycled brackets versus new brackets. 3M Clarity Self-Ligating Ceramic Brackets with a microcrystalline base were divided into groups subjected to flaming, sandblasting, or exposure to an Er:YAG laser. New ceramic brackets served as a control group. Shear bond strengths were determined with an Electroforce test machine and tested for statistical significance through analysis of variance. Morphological examinations of the recycled ceramic bracket bases were conducted with scanning electron microscopy and confocal laser scanning microscopy. Residue on the bracket base was analyzed with Raman spectroscopy. Faded, dark adhesive was left on recycled bracket bases processed via flaming. Adhesive was thoroughly removed by both sandblasting and exposure to an Er:YAG laser. Compared with new brackets, shear bond strength was lower after sandblasting (p < 0.05), but not after exposure to an Er:YAG laser. The Er:YAG laser caused no damage to the bracket. Er:YAG lasers effectively remove adhesive from the bases of ceramic brackets without damaging them; thus, this method may be preferred over other recycling methods.

Achieving the desired colour in discoloured teeth, using leucite-based CAD-CAM laminate systems.

PubMed

Turgut, Sedanur; Bagis, Bora; Ayaz, Elif Aydogan

2014-01-01

To evaluate the cumulative effect of the abutment tooth and resin cement colour on the resultant optical properties of porcelain laminate veneers (PLVs) fabricated with leucite-based CAD/CAM blocks with different shades and thicknesses. A total of 224 ceramic specimens were prepared from the IPS Empress CAD with four different shades of HT-A1, LT-A1, MT-A1 and Bl-1. Resin composite discs were prepared with shade A3.5. For the cementation, 4 different shades of light-cure resin cements were chosen. L*, a*, and b* values, as well as the chroma (C) and hue (h) values of each cemented ceramic and the A1 shade table, were recorded. L*, Cab* and hab* values of the cemented ceramics were influenced by ceramic shade, ceramic thickness, cement shade, and interaction terms of the three variables. There were significant differences between the 1-mm-thick ceramic veneers that exhibited higher L* and lower Cab* values compared with veneers that were 0.5mm in thickness. Using the Tr shade cement resulted in lower L* and higher Cab* values for all thicknesses and ceramic shades, whereas the WO shade cement resulted in higher values. The selected colour of a laminate restoration is significantly affected by the ceramic shade, ceramic thickness and resin cement shade. Using the WO shade resin cement seems to be more effective in masking the discoloured abutment tooth. Clinicians should also select the translucency level of the ceramic block with the shade when a leucite-based CAD/CAM system is chosen to treat a discoloured tooth. Copyright © 2013 Elsevier Ltd. All rights reserved.

Er,Cr:YSGG Laser as a Novel Method for Rebonding Failed Ceramic Brackets.

PubMed

Sohrabi, Aydin; Jafari, Sanaz; Kimyai, Soodabeh; Rikhtehgaran, Sahand

2016-10-01

Since there is no standard method for rebonding loose ceramic brackets, the aim of this study was to evaluate the possibility of using Er,Cr:YSGG laser to eliminate the remaining composite materials from the base of ceramic brackets and to compare the bond strength of rebonded brackets with the new ones. Sixty-two extracted human premolars were mounted in acrylic cylinders. Thirty-one ceramic brackets were bonded, and shear bond strength was tested using Hounsfield testing machine. The remnants of the bonding material were removed from the bases of brackets using Er,Cr:YSGG laser. These brackets were rebonded to 31 fresh teeth and again shear bond strength was measured. Pattern of debonding was assessed in both cases under a stereomicroscope and graded according to ARI index. Data were analyzed with independent t-test and Fisher's exact test. Mean shear bond strength of the bond and rebond groups was 12.29 ± 5.46 and 10.58 ± 5.16 MPa, respectively. There were no significant differences between the two groups (p = 0.21). Pattern of bond failure was not statistically different between the two groups. Er,Cr:YSGG laser was effective in removing the remnants of bonding material from the base of ceramic brackets without any interference with the ceramic base itself, demonstrating that it might be a suitable method for rebonding ceramic brackets.

Shear bond strength of brackets on restorative materials: Comparison on various dental restorative materials using the universal primer Monobond® Plus.

PubMed

Ebert, Thomas; Elsner, Laura; Hirschfelder, Ursula; Hanke, Sebastian

2016-03-01

The purpose of this work was to analyze surfaces consisting of different restorative materials for shear bond strength (SBS) and failure patterns of metal and ceramic brackets. Bonding involved the use of a universal primer (Monobond® Plus, Ivoclar Vivadent). Six restorative materials were tested, including one composite resin (Clearfil Majesty™ Posterior, Kuraray Noritake Dental), one glass-ceramic material (IPS Empress® Esthetic, Ivoclar Vivadent), one oxide-ceramic material (CORiTEC Zr transpa Disc, imes-icore), two base-metal alloys (remanium® star, Dentaurum; Colado® CC, Ivoclar Vivadent), and one palladium-based alloy (Callisto® 75 Pd, Ivoclar Vivadent). Bovine incisors served as controls. Both metal and ceramic brackets (discovery®/discovery® pearl; Dentaurum) were bonded to the restorative surfaces after sandblasting and pretreatment with Monobond® Plus. A setup modified from DIN 13990-2 was used for SBS testing and adhesive remnant index (ARI)-based analysis of failure patterns. The metal brackets showed the highest mean SBS values on the glass-ceramic material (68.61 N/mm(2)) and the composite resin (67.58 N/mm(2)) and the lowest mean SBS on one of the base-metal alloys (Colado® CC; 14.01 N/mm(2)). The ceramic brackets showed the highest mean SBS on the glass-ceramic material (63.36 N/mm(2)) and the lowest mean SBS on the palladium-based alloy (38.48 N/mm(2)). Significant differences between the metal and ceramic brackets were observed in terms of both SBS values and ARI scores (p < 0.05). Under both bracket types, fractures of the composite-resin and the glass-ceramic samples were observed upon debonding. Opaque restorative materials under metal brackets were found to involve undercuring of the adhesive. Monobond® Plus succeeded in generating high bond strengths of both bracket types on all restorative surfaces. Given our observations of cohesive fracture (including cases of surface avulsion) of the composite-resin and the glass-ceramic samples, we recommend against using these material combinations in clinical practice.

Thermal behavior of silicone rubber-based ceramizable composites characterized by Fourier transform infrared (FT-IR) spectroscopy and microcalorimetry.

PubMed

Anyszka, Rafał; Bieliński, Dariusz M; Jędrzejczyk, Marcin

2013-12-01

Ceramizable (ceramifiable) silicone rubber-based composites are commonly used for cable insulation. These materials are able to create a protective ceramic layer during fire due to the ceramization process, which occurs at high temperature. When the temperature is increased, the polymer matrix is degraded and filler particles stick together by the fluxing agent, producing a solid, continuous ceramic phase that protects the copper wire from heat and mechanical stress. Despite increasing interest in these materials that has resulted in growing applications in the cable industry, their thermal behavior and ceramization process are still insufficiently described in the literature. In this paper, the thermal behavior of ceramizable silicone rubber-based composites is studied using microcalorimetry and Fourier transform infrared spectroscopy. The analysis of the experimental data made it possible to develop complete information on the mechanism of composite ceramization.

Magnetic Glass Ceramics by Sintering of Borosilicate Glass and Inorganic Waste.

PubMed

Ponsot, Inès M M M; Pontikes, Yiannis; Baldi, Giovanni; Chinnam, Rama K; Detsch, Rainer; Boccaccini, Aldo R; Bernardo, Enrico

2014-07-31

Ceramics and glass ceramics based on industrial waste have been widely recognized as competitive products for building applications; however, there is a great potential for such materials with novel functionalities. In this paper, we discuss the development of magnetic sintered glass ceramics based on two iron-rich slags, coming from non-ferrous metallurgy and recycled borosilicate glass. The substantial viscous flow of the glass led to dense products for rapid treatments at relatively low temperatures (900-1000 °C), whereas glass/slag interactions resulted in the formation of magnetite crystals, providing ferrimagnetism. Such behavior could be exploited for applying the obtained glass ceramics as induction heating plates, according to preliminary tests (showing the rapid heating of selected samples, even above 200 °C). The chemical durability and safety of the obtained glass ceramics were assessed by both leaching tests and cytotoxicity tests.

Ceramic Nanocomposites from Tailor-Made Preceramic Polymers

PubMed Central

Mera, Gabriela; Gallei, Markus; Bernard, Samuel; Ionescu, Emanuel

2015-01-01

The present Review addresses current developments related to polymer-derived ceramic nanocomposites (PDC-NCs). Different classes of preceramic polymers are briefly introduced and their conversion into ceramic materials with adjustable phase compositions and microstructures is presented. Emphasis is set on discussing the intimate relationship between the chemistry and structural architecture of the precursor and the structural features and properties of the resulting ceramic nanocomposites. Various structural and functional properties of silicon-containing ceramic nanocomposites as well as different preparative strategies to achieve nano-scaled PDC-NC-based ordered structures are highlighted, based on selected ceramic nanocomposite systems. Furthermore, prospective applications of the PDC-NCs such as high-temperature stable materials for thermal protection systems, membranes for hot gas separation purposes, materials for heterogeneous catalysis, nano-confinement materials for hydrogen storage applications as well as anode materials for secondary ion batteries are introduced and discussed in detail. PMID:28347023

Reconfigurable all-dielectric metamaterial frequency selective surface based on high-permittivity ceramics

NASA Astrophysics Data System (ADS)

Li, Liyang; Wang, Jun; Wang, Jiafu; Ma, Hua; Du, Hongliang; Zhang, Jieqiu; Qu, Shaobo; Xu, Zhuo

2016-04-01

Based on effective medium theory and dielectric resonator theory, we propose the design of reconfigurable all-dielectric metamaterial frequency selective surfaces (FSSs) using high-permittivity ceramics. The FSS is composed of ceramic resonators with different band stop responses under front and side incidences. By mechanically tuning the orientation of the ceramic resonators, reconfigurable electromagnetic (EM) responses between two adjacent stopbands can be achieved. The two broad stopbands originate from the first two resonant modes of the ceramic resonators. As an example, a reconfigurable FSS composed of cross-shaped ceramic resonators is demonstrated. Both numerical and experimental results show that the FSS can switch between two consecutive stopbands in 3.55-4.60 GHz and 4.54-4.94 GHz. The design method can be readily extended to the design of FSSs in other frequencies for high-power applications.

High-Temperature Dielectric Properties of Aluminum Nitride Ceramic for Wireless Passive Sensing Applications

PubMed Central

Liu, Jun; Yuan, Yukun; Ren, Zhong; Tan, Qiulin; Xiong, Jijun

2015-01-01

The accurate characterization of the temperature-dependent permittivity of aluminum nitride (AlN) ceramic is quite critical to the application of wireless passive sensors for harsh environments. Since the change of the temperature-dependent permittivity will vary the ceramic-based capacitance, which can be converted into the change of the resonant frequency, an LC resonator, based on AlN ceramic, is prepared by the thick film technology. The dielectric properties of AlN ceramic are measured by the wireless coupling method, and discussed within the temperature range of 12 °C (room temperature) to 600 °C. The results show that the extracted relative permittivity of ceramic at room temperature is 2.3% higher than the nominal value of 9, and increases from 9.21 to 10.79, and the quality factor Q is decreased from 29.77 at room temperature to 3.61 at 600 °C within the temperature range. PMID:26370999

Magnetic Glass Ceramics by Sintering of Borosilicate Glass and Inorganic Waste

PubMed Central

Ponsot, Inès M. M. M.; Pontikes, Yiannis; Baldi, Giovanni; Chinnam, Rama K.; Detsch, Rainer; Boccaccini, Aldo R.; Bernardo, Enrico

2014-01-01

Ceramics and glass ceramics based on industrial waste have been widely recognized as competitive products for building applications; however, there is a great potential for such materials with novel functionalities. In this paper, we discuss the development of magnetic sintered glass ceramics based on two iron-rich slags, coming from non-ferrous metallurgy and recycled borosilicate glass. The substantial viscous flow of the glass led to dense products for rapid treatments at relatively low temperatures (900–1000 °C), whereas glass/slag interactions resulted in the formation of magnetite crystals, providing ferrimagnetism. Such behavior could be exploited for applying the obtained glass ceramics as induction heating plates, according to preliminary tests (showing the rapid heating of selected samples, even above 200 °C). The chemical durability and safety of the obtained glass ceramics were assessed by both leaching tests and cytotoxicity tests. PMID:28788146

Reconfigurable all-dielectric metamaterial frequency selective surface based on high-permittivity ceramics

PubMed Central

Li, Liyang; Wang, Jun; Wang, Jiafu; Ma, Hua; Du, Hongliang; Zhang, Jieqiu; Qu, Shaobo; Xu, Zhuo

2016-01-01

Based on effective medium theory and dielectric resonator theory, we propose the design of reconfigurable all-dielectric metamaterial frequency selective surfaces (FSSs) using high-permittivity ceramics. The FSS is composed of ceramic resonators with different band stop responses under front and side incidences. By mechanically tuning the orientation of the ceramic resonators, reconfigurable electromagnetic (EM) responses between two adjacent stopbands can be achieved. The two broad stopbands originate from the first two resonant modes of the ceramic resonators. As an example, a reconfigurable FSS composed of cross-shaped ceramic resonators is demonstrated. Both numerical and experimental results show that the FSS can switch between two consecutive stopbands in 3.55–4.60 GHz and 4.54–4.94 GHz. The design method can be readily extended to the design of FSSs in other frequencies for high-power applications. PMID:27052098

Modified Ion-Conducting Ceramics Based on Lanthanum Gallate: Synthesis, Structure, and Properties

NASA Astrophysics Data System (ADS)

Kaleva, G. M.; Politova, E. D.; Mosunov, A. V.; Sadovskaya, N. V.

2018-06-01

A review is presented of the synthesis and complex investigation of modified ion-conducting ceramics based on heterosubstituted lanthanum gallate as a promising electrolyte material for solid oxide fuel cells. The effect the composition of multicomponent complex oxides has on the structure, microstructure, and electrophysical properties of ceramics is examined. Samples of ceramics with new compositions are produced via solid-state synthesis and modified with lithium fluoride. A drop is observed in the sintering temperature of the ceramics, caused by the liquid phase mechanism of sintering as a result of the low-melting superstoichiometric quantities of the additive. The effect lithium fluoride has on the process of phase formation, microstructure, and conductivity of the ceramics is investigated. It is found that samples modified with lithium fluoride display high density, dense grain packing, and high values of electrical conductivity at high temperatures.

Bioactive calcium silicate ceramics and coatings.

PubMed

Liu, Xuanyong; Morra, Marco; Carpi, Angelo; Li, Baoe

2008-10-01

CaO-SiO2 based ceramics have been regarded as potential candidates for artificial bone due to their excellent bone bioactivity and biocompatibility. However, they cannot be used as implants under a heavy load because of their poor mechanical properties, in particular low fracture toughness. Plasma spraying CaO-SiO2 based ceramic coatings onto titanium alloys can expand their application to the hard tissue replacement under a heavy load. Plasma sprayed wollastonite, dicalcium silicate and diopside coatings have excellent bone bioactivity and high bonding strength to titanium alloys. It is possible that these plasma sprayed CaO-SiO2 based ceramic coatings will be applied in clinic after they are widely and systematically researched.

Fuel cell integral bundle assembly including ceramic open end seal and vertical and horizontal thermal expansion control

DOEpatents

Zafred, Paolo R [Murrysville, PA; Gillett, James E [Greensburg, PA

2012-04-24

A plurality of integral bundle assemblies contain a top portion with an inlet fuel plenum and a bottom portion containing a base support, the base supports a dense, ceramic air exhaust manifold having four supporting legs, the manifold is below and connects to air feed tubes located in a recuperator zone, the air feed tubes passing into the center of inverted, tubular, elongated, hollow electrically connected solid oxide fuel cells having an open end above a combustion zone into which the air feed tubes pass and a closed end near the inlet fuel plenum, where the open end of the fuel cells rest upon and within a separate combination ceramic seal and bundle support contained in a ceramic support casting, where at least one flexible cushion ceramic band seal located between the recuperator and fuel cells protects and controls horizontal thermal expansion, and where the fuel cells operate in the fuel cell mode and where the base support and bottom ceramic air exhaust manifolds carry from 85% to all of the weight of the generator.

Ceramic processing: Experimental design and optimization

NASA Technical Reports Server (NTRS)

Weiser, Martin W.; Lauben, David N.; Madrid, Philip

1992-01-01

The objectives of this paper are to: (1) gain insight into the processing of ceramics and how green processing can affect the properties of ceramics; (2) investigate the technique of slip casting; (3) learn how heat treatment and temperature contribute to density, strength, and effects of under and over firing to ceramic properties; (4) experience some of the problems inherent in testing brittle materials and learn about the statistical nature of the strength of ceramics; (5) investigate orthogonal arrays as tools to examine the effect of many experimental parameters using a minimum number of experiments; (6) recognize appropriate uses for clay based ceramics; and (7) measure several different properties important to ceramic use and optimize them for a given application.

Method of making metal matrix composites reinforced with ceramic particulates

DOEpatents

Cornie, James A.; Kattamis, Theodoulos; Chambers, Brent V.; Bond, Bruce E.; Varela, Raul H.

1989-01-01

Composite materials and methods for making such materials are disclosed in which dispersed ceramic particles are at chemical equilibrium with a base metal matrix, thereby permitting such materials to be remelted and subsequently cast or otherwise processed to form net weight parts and other finished (or semi-finished) articles while maintaining the microstructure and mechanical properties (e.g. wear resistance or hardness) of the original composite. The composite materials of the present invention are composed of ceramic particles in a base metal matrix. The ceramics are preferably carbides of titanium, zirconium, tungsten, molybdenum or other refractory metals. The base metal can be iron, nickel, cobalt, chromium or other high temperature metal and alloys thereof. For ferrous matrices, alloys suitable for use as the base metal include cast iron, carbon steels, stainless steels and iron-based superalloys.

Method of making metal matrix composites reinforced with ceramic particulates

DOEpatents

Cornie, J.A.; Kattamis, T.; Chambers, B.V.; Bond, B.E.; Varela, R.H.

1989-08-01

Composite materials and methods for making such materials are disclosed in which dispersed ceramic particles are at chemical equilibrium with a base metal matrix, thereby permitting such materials to be remelted and subsequently cast or otherwise processed to form net weight parts and other finished (or semi-finished) articles while maintaining the microstructure and mechanical properties (e.g. wear resistance or hardness) of the original composite. The composite materials of the present invention are composed of ceramic particles in a base metal matrix. The ceramics are preferably carbides of titanium, zirconium, tungsten, molybdenum or other refractory metals. The base metal can be iron, nickel, cobalt, chromium or other high temperature metal and alloys thereof. For ferrous matrices, alloys suitable for use as the base metal include cast iron, carbon steels, stainless steels and iron-based superalloys. 2 figs.

Mechanical fatigue degradation of ceramics versus resin composites for dental restorations.

PubMed

Belli, Renan; Geinzer, Eva; Muschweck, Anna; Petschelt, Anselm; Lohbauer, Ulrich

2014-04-01

For posterior partial restorations an overlap of indication exists where either ceramic or resin-based composite materials can be successfully applied. The aim of this study was to compare the fatigue resistance of modern dental ceramic materials versus dental resin composites in order to address such conflicts. Bar specimens of five ceramic materials and resin composites were produced according to ISO 4049 and stored for 14 days in distilled water at 37°C. The following ceramic materials were selected for testing: a high-strength zirconium dioxide (e.max ZirCAD, Ivoclar), a machinable lithium disilicate (e.max CAD, Ivoclar), a pressable lithium disilicate ceramic (e-max Press, Ivoclar), a fluorapatite-based glass-ceramic (e.max Ceram, Ivoclar), and a machinable color-graded feldspathic porcelain (Trilux Forte, Vita). The composite materials selected were: an indirect machinable composite (Lava Ultimate, 3M ESPE) and four direct composites with varying filler nature (Clearfil Majesty Posterior, Kuraray; GrandioSO, Voco; Tetric EvoCeram, Ivoclar-Vivadent; and CeramX Duo, Dentsply). Fifteen specimens were tested in water for initial strength (σin) in 4-point bending. Using the same test set-up, the residual flexural fatigue strength (σff) was determined using the staircase approach after 10(4) cycles at 0.5 Hz (n=25). Weibull parameters σ0 and m were calculated for the σin specimens, whereas the σff and strength loss in percentage were obtained from the fatigue experiment. The zirconium oxide ceramic showed the highest σin and σff (768 and 440 MPa, respectively). Although both lithium disilicate ceramics were similar in the static test, the pressable version showed a significantly higher fatigue resistance after cyclic loading. Both the fluorapatite-based and the feldspathic porcelain showed equivalent initial and cyclic fatigue properties. From the composites, the highest filled direct material Clearfil Majesty Posterior showed superior fatigue performance. From all materials, e.max Press and Clearfil Majesty Posterior showed the lowest strength loss (29.6% and 32%, respectively), whereas the other materials lost between 41% and 62% of their flexural strength after cyclic loading. Dental ceramics and resin composite materials show equivalent fatigue strength degradation at loads around 0.5σin values. Apart from the zirconium oxide and the lithium disilicate ceramics, resin composites generally showed better σff after 10,000 cycles than the fluorapatite glass-ceramic and the feldspathic porcelain. Resin composite restorations may be used as an equivalent alternative to glass-rich-ceramic inlays regarding mechanical performance. Copyright © 2014 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Development of a low-permeability glass--ceramic to seal to molybdenum. [For long-life vacuum tubes

DOE Office of Scientific and Technical Information (OSTI.GOV)

Eagan, R. J.

1975-03-01

This report describes the development of low-permeability glass-ceramics which can be sealed directly to molybdenum for the purpose of producing long-life vacuum tubes. Low permeability to helium and thermal expansion match to molybdenum are the bases upon which particular glass-ceramic compositions were selected and developed. The fabrication of tube envelopes using glass-ceramics is simplified when compared to conventional ceramic/metal tubes and these melting and sealing techniques are presented.

Metal-ceramic joint assembly

DOEpatents

Li, Jian

2002-01-01

A metal-ceramic joint assembly in which a brazing alloy is situated between metallic and ceramic members. The metallic member is either an aluminum-containing stainless steel, a high chromium-content ferritic stainless steel or an iron nickel alloy with a corrosion protection coating. The brazing alloy, in turn, is either an Au-based or Ni-based alloy with a brazing temperature in the range of 9500 to 1200.degree. C.

Laser Surface Treatment of Sintered Alumina

NASA Astrophysics Data System (ADS)

Hagemann, R.; Noelke, C.; Kaierle, S.; Wesling, V.

Sintered alumina ceramics are used as refractory materials for industrial aluminum furnaces. In this environment the ceramic surface is in permanent contact with molten aluminum resulting in deposition of oxidic material on its surface. Consequently, a lower volume capacity as well as thermal efficiency of the furnaces follows. To reduce oxidic adherence of the ceramic material, two laser-based surface treatment processes were investigated: a powder- based single-step laser cladding and a laser surface remelting. Main objective is to achieve an improved surface quality of the ceramic material considering the industrial requirements as a high process speed.

Method of making multilayered titanium ceramic composites

DOEpatents

Fisher, G.T. II; Hansen, J.S.; Oden, L.L.; Turner, P.C.; Ochs, T.L.

1998-08-25

A method making a titanium ceramic composite involves forming a hot pressed powder body having a microstructure comprising at least one titanium metal or alloy layer and at least one ceramic particulate reinforced titanium metal or alloy layer and hot forging the hot pressed body followed by hot rolling to substantially reduce a thickness dimension and substantially increase a lateral dimension thereof to form a composite plate or sheet that retains in the microstructure at least one titanium based layer and at least one ceramic reinforced titanium based layer in the thickness direction of the composite plate or sheet. 3 figs.

Method of making multilayered titanium ceramic composites

DOEpatents

Fisher, George T., II; Hansen; Jeffrey S.; Oden; Laurance L.; Turner; Paul C.; Ochs; Thomas L.

1998-08-25

A method making a titanium ceramic composite involves forming a hot pressed powder body having a microstructure comprising at least one titanium metal or alloy layer and at least one ceramic particulate reinforced titanium metal or alloy layer and hot forging the hot pressed body follwed by hot rolling to substantially reduce a thickness dimension and substantially increase a lateral dimension thereof to form a composite plate or sheet that retains in the microstructure at least one titanium based layer and at least one ceramic reinforced titanium based layer in the thickness direction of the composite plate or sheet.

Method of making multilayered titanium ceramic composites

DOEpatents

Fisher, II, George T.; Hansen, Jeffrey S.; Oden, Laurance L.; Turner, Paul C.; Ochs, Thomas L.

1998-01-01

A method making a titanium ceramic composite involves forming a hot pressed powder body having a microstructure comprising at least one titanium metal or alloy layer and at least one ceramic particulate reinforced titanium metal or alloy layer and hot forging the hot pressed body follwed by hot rolling to substantially reduce a thickness dimension and substantially increase a lateral dimension thereof to form a composite plate or sheet that retains in the microstructure at least one titanium based layer and at least one ceramic reinforced titanium based layer in the thickness direction of the composite plate or sheet.

Evaluation of a novel multiple phase veneering ceramic.

PubMed

Sinthuprasirt, Pannapa; van Noort, Richard; Moorehead, Robert; Pollington, Sarah

2015-04-01

To produce a new veneering ceramic based on the production of a multiple phase glass-ceramic with improved performance in terms of strength and toughness. A composition of 60% leucite, 20% diopside and 20% feldspathic glass was prepared, blended and a heat treatment schedule of 930°C for 5 min was derived from differential thermal analysis (DTA) of the glasses. X-ray diffraction (XRD) and SEM analysis determined the crystalline phases and microstructure. Chemical solubility, biaxial flexural strength (BFS), fracture toughness, hardness, total transmittance and coefficient of thermal expansion (CTE) were all measured in comparison to a commercial veneering ceramic (VITA VM9). Thermal shock resistance of the leucite-diopside and VITA VM9 veneered onto a commercial high strength zirconia (Vita In-Ceram YZ) was also assessed. Statistical analysis was undertaken using Independent Samples t-test. Weibull analysis was employed to examine the reliability of the strength data. The mean chemical solubility was 6 μg/cm(2) for both ceramics (P=1.00). The mean BFS was 109 ± 8 MPa for leucite-diopside ceramic and 79 ± 11 MPa for VITA VM9 ceramic (P=0.01). Similarly, the leucite-diopside ceramic demonstrated a significantly higher fracture toughness and hardness. The average total transmittance was 46.3% for leucite-diopside ceramic and 39.8% for VITA VM9 (P=0.01). The leucite-diopside outperformed the VITA VM9 in terms of thermal shock resistance. Significance This novel veneering ceramic exhibits significant improvements in terms of mechanical properties, yet retains a high translucency and is the most appropriate choice as a veneering ceramic for a zirconia base core material. Copyright © 2015 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Ceramic strengthening by tuning the elastic moduli of resin-based luting agents.

PubMed

Spazzin, Aloísio O; Bacchi, Ataís; Alessandretti, Rodrigo; Santos, Mateus B; Basso, Gabriela R; Griggs, Jason; Moraes, Rafael R

2017-03-01

Resin-based luting agents (RBLAs) with tuned elastic moduli (E) were prepared and their influence on the strengthening, reliability, and mode of failure of luted feldspar ceramic was investigated. RBLAs with low E (2.6GPa), intermediate E (6.6GPa), and high E (13.3GPa) were prepared and used to coat acid-etched ceramic disks. Positive (untreated ceramic) and negative (acid-etched ceramic) control groups were tested. The response variables (n=30) were biaxial flexural strength (σ bf , MPa), characteristic strength (σ 0 , MPa), and Weibull modulus at the ceramic surface (z=0) and luting agent surface (z=-t 2 ). A 3D finite element analysis simulated the biaxial flexural test. Fractographic analysis and morphology of the bonded interfaces were analyzed using scanning electron microscopy. The RBLAs improved σ bf and σ 0 at z=0, particularly those with intermediate and high E, whereas the mechanical reliability was only affected in the negative control. At z=-t 2 , differences between all RBLAs were observed but the structural reliability was independent of the RBLA tested. Increasing E of the RBLA was associated with increased stress concentration at the RBLA and reduced stresses reaching the ceramic. Failures originated on the ceramic surface at the ceramic-cement interface. In the high E group, failure sometimes originated from the RBLA free surface. All RBLAs completely filled the ceramic irregularities. Increased E of the RBLA reduced the variability of strength, the stress reaching the ceramic structure, and sometimes altered the origin of failure. The use of high E RBLAs seems beneficial for luting feldspar ceramics. Copyright © 2017 The Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Construction Material And Method

DOEpatents

Wagh, Arun S.; Antink, Allison L.

2006-02-21

A structural material of a polystyrene base and the reaction product of the polystyrene base and a solid phosphate ceramic. The ceramic is applied as a slurry which includes one or more of a metal oxide or a metal hydroxide with a source of phosphate to produce a phosphate ceramic and a poly (acrylic acid or acrylate) or combinations or salts thereof and polystyrene or MgO applied to the polystyrene base and allowed to cure so that the dried aqueous slurry chemically bonds to the polystyrene base. A method is also disclosed of applying the slurry to the polystyrene base.

Method of binding structural material

DOEpatents

Wagh, Arun S.; Antink, Allison L.

2007-12-25

A structural material of a polystyrene base and the reaction product of the polystyrene base and a solid phosphate ceramic. The ceramic is applied as a slurry which includes one or more of a metal oxide or a metal hydroxide with a source of phosphate to produce a phosphate ceramic and a poly (acrylic acid or acrylate) or combinations or salts thereof and polystyrene or MgO applied to the polystyrene base and allowed to cure so that the dried aqueous slurry chemically bonds to the polystyrene base. A method is also disclosed of applying the slurry to the polystyrene base.

Osteoblasts Interaction with PLGA Membranes Functionalized with Titanium Film Nanolayer by PECVD. In vitro Assessment of Surface Influence on Cell Adhesion during Initial Cell to Material Interaction

PubMed Central

Terriza, Antonia; Vilches-Pérez, José I.; González-Caballero, Juan L.; de la Orden, Emilio; Yubero, Francisco; Barranco, Angel; Gonzalez-Elipe, Agustín R.; Vilches, José; Salido, Mercedes

2014-01-01

New biomaterials for Guided Bone Regeneration (GBR), both resorbable and non-resorbable, are being developed to stimulate bone tissue formation. Thus, the in vitro study of cell behavior towards material surface properties turns a prerequisite to assess both biocompatibility and bioactivity of any material intended to be used for clinical purposes. For this purpose, we have developed in vitro studies on normal human osteoblasts (HOB®) HOB® osteoblasts grown on a resorbable Poly (lactide-co-glycolide) (PLGA) membrane foil functionalized by a very thin film (around 15 nm) of TiO2 (i.e., TiO2/PLGA membranes), designed to be used as barrier membrane. To avoid any alteration of the membranes, the titanium films were deposited at room temperature in one step by plasma enhanced chemical vapour deposition. Characterization of the functionalized membranes proved that the thin titanium layer completely covers the PLGA foils that remains practically unmodified in their interior after the deposition process and stands the standard sterilization protocols. Both morphological changes and cytoskeletal reorganization, together with the focal adhesion development observed in HOB osteoblasts, significantly related to TiO2 treated PLGA in which the Ti deposition method described has revealed to be a valuable tool to increase bioactivity of PLGA membranes, by combining cell nanotopography cues with the incorporation of bioactive factors. PMID:28788538

Tetraspanin 7 regulates sealing zone formation and the bone-resorbing activity of osteoclasts

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kwon, Jun-Oh; Lee, Yong Deok; Kim, Haemin

Tetraspanin family proteins regulate morphology, motility, fusion, and signaling in various cell types. We investigated the role of the tetraspanin 7 (Tspan7) isoform in the differentiation and function of osteoclasts. Tspan7 was up-regulated during osteoclastogenesis. When Tspan7 expression was reduced in primary precursor cells by siRNA-mediated gene knock-down, the generation of multinuclear osteoclasts was not affected. However, a striking cytoskeletal abnormality was observed: the formation of the podosome belt structure was inhibited and the microtubular network were disrupted by Tspan7 knock-down. Decreases in acetylated microtubules and levels of phosphorylated Src and Pyk2 in Tspan7 knock-down cells supported the involvement ofmore » Tspan7 in cytoskeletal rearrangement signaling in osteoclasts. This cytoskeletal defect interfered with sealing zone formation and subsequently the bone-resorbing activity of mature osteoclasts on dentin surfaces. Our results suggest that Tspan7 plays an important role in cytoskeletal organization required for the bone-resorbing function of osteoclasts by regulating signaling to Src, Pyk2, and microtubules. - Highlights: • Tspan7 expression is up-regulated during osteoclastogenesis. • Tspan7 regulates podosome belt organization in osteoclasts. • Tspan7 is crucial for sealing zone formation and bone-resorption by osteoclasts. • Src and Pyk2 phosphorylation and microtubule acetylation mediate Tspan7 function.« less

Evaluation of carbonate apatite blocks fabricated from dicalcium phosphate dihydrate blocks for reconstruction of rabbit femoral and tibial defects.

PubMed

Kanazawa, Masayuki; Tsuru, Kanji; Fukuda, Naoyuki; Sakemi, Yuta; Nakashima, Yasuharu; Ishikawa, Kunio

2017-06-01

This study aimed to evaluate in vivo behavior of a carbonate apatite (CO 3 Ap) block fabricated by compositional transformation via a dissolution-precipitation reaction using a calcium hydrogen phosphate dihydrate [DCPD: CaHPO 4 ·2H 2 O] block as a precursor. These blocks were used to reconstruct defects in the femur and tibia of rabbits, using sintered dense hydroxyapatite (HAp) blocks as the control. Both the CO 3 Ap and HAp blocks showed excellent tissue response and good osteoconductivity. HAp block maintained its structure even after 24 weeks of implantation, so no bone replacement of the implant was observed throughout the post-implantation period in either femoral or tibial bone defects. In contrast, CO 3 Ap was resorbed with increasing time after implantation and replaced with new bone. The CO 3 Ap block was resorbed approximately twice as fast at the metaphysis of the proximal tibia than at the epiphysis of the distal femur. The CO 3 Ap block was resorbed at an approximately linear change over time, with complete resorption was estimated by extrapolation of data at approximately 1-1.5 years. Hence, the CO 3 Ap block fabricated in this study has potential value as an ideal artificial bone substitute because of its resorption and subsequent replacement by bone.

Evaluation of poly-L-lactic acid and polyglycolic acid resorbable stents for repair of tracheomalacia in a porcine model.

PubMed

Nalwa, S S; Hartig, G K; Warner, T; Connor, N P; Thielman, M J

2001-11-01

Poly-L-lactic acid and polyglycolic acid (PLPG) resorbable stents may offer a potential solution to the problem of tracheomalacia. Advantages of this material include its strength, its versatile shaping characteristics, and its resorbability, which would preclude surgical removal and allow for airway growth. The purpose of this pilot study was to examine the usefulness of PLPG stents for temporary external airway stenting of tracheomalacia in a porcine model. A severe tracheomalacia was created in 6 pigs by submucosal resection of segments of tracheal cartilage from 6 consecutive rings. The PLPG stent was then shaped to recreate the tracheal contour and sutured to the underlying airway. Endoscopic photodocumentation during spontaneous ventilation was obtained before and after reconstruction. After creation of the malacic tracheal segment, all animals developed stridor, retractions, and cyanosis during spontaneous ventilation. After repair, all animals were extubated without complication. All animals survived the follow-up period of 9 to 12 weeks without evidence of respiratory distress and with rapid weight gain. Repeat bronchoscopy showed no evidence of airway collapse during spontaneous ventilation. Tracheal measurements revealed growth of the stented segment with a mild narrowing within the repaired region. Histologic examination showed preservation of respiratory epithelium. These preliminary findings suggest that PLPG stents may serve a useful role in the surgical management of tracheomalacia.

Recombinant VSV G proteins reveal a novel raft-dependent endocytic pathway in resorbing osteoclasts

DOE Office of Scientific and Technical Information (OSTI.GOV)

Mulari, Mika T.K.; Centre for Military Medicine, Research Department, Lahti; Nars, Martin

2008-05-01

Transcytotic membrane flow delivers degraded bone fragments from the ruffled border to the functional secretory domain, FSD, in bone resorbing osteoclasts. Here we show that there is also a FSD-to-ruffled border trafficking pathway that compensates for the membrane loss during the matrix uptake process and that rafts are essential for this ruffled border-targeted endosomal pathway. Replacing the cytoplasmic tail of the vesicular stomatitis virus G protein with that of CD4 resulted in partial insolubility in Triton X-100 and retargeting from the peripheral non-bone facing plasma membrane to the FSD. Recombinant G proteins were subsequently endosytosed and delivered from the FSDmore » to the peripheral fusion zone of the ruffled border, which were both rich in lipid rafts as suggested by viral protein transport analysis and visualizing the rafts with fluorescent recombinant cholera toxin. Cholesterol depletion by methyl-{beta}-cyclodextrin impaired the ruffled border-targeted vesicle trafficking pathway and inhibited bone resorption dose-dependently as quantified by measuring the CTX and TRACP 5b secreted to the culture medium and by measuring the resorbed area visualized with a bi-phasic labeling method using sulpho-NHS-biotin and WGA-lectin. Thus, rafts are vital for membrane recycling from the FSD to the late endosomal/lysosomal ruffled border and bone resorption.« less

Microstructures and performance of CaO-based ceramic cores with different particle size distributions for investment casting

NASA Astrophysics Data System (ADS)

Zhou, P. P.; Wu, G. Q.; Tao, Y.; Cheng, X.; Zhao, J. Q.; Nan, H.

2018-02-01

A series of calcium-based ceramic cores for casting titanium alloy were prepared by mixing different amounts of coarse and fine powders through injection molding. The effects of particle size on the microstructures and properties of the ceramic cores were investigated using quantitative and statistical analysis methods. It is found that the shrinkage and room-temperature strength of the ceramic cores were enhanced as increasing the contents of fine particles. Moreover, the creep resistance of the ceramic cores increased initially and then decreased. The increase in the fine particle content of the cores reduced the number and mean diameter of pores after sintering. The grain boundary density decreased firstly and then increased. The flexural strength of the ceramic cores at room temperature decreased with increasing porosity of ceramic cores, whereas the creep resistance increased with decreasing grain boundary density. A core exhibiting the optimal property was obtained when mixing 65 wt% of coarse powders (75-150 μm) and 35 wt% of fine powders (25-48 μm).

Ceramic technology for advanced heat engines project. Semiannual progress report, October 1985-March 1986

DOE Office of Scientific and Technical Information (OSTI.GOV)

Not Available

1986-08-01

Significant accomplishments in fabricating cermaic components for the Department of Energy (DOE), National Aeronautics and Space Administration (NASA), and Department of Defense (DOD) advanced heat engine programs have provided evidence that the operation of ceramic parts in high-temperature engine environments is feasible. However, additional research is needed in materials and processing development, design methodology, and data base and life prediction. An assessment of needs was completed, and a five-year project plan was developed with extensive input from private industry. The objective of the project is to develop the industrial technology base required for reliable ceramics for application in advanced automotivemore » heat engines. The project approach includes determining the mechanisms controlling reliability, improving processes for fabricating existing ceramics, developing new materials with increased reliability, and testing these materials in simulated engine environments to confirm reliability. although this is a generic materials project, the focus is on structural ceramics for advanced gas turbine and diesel engines, ceramic bearings and attachments, and ceramic coatings for thermal barrier and wear applications in these engines.« less

Basic Research on Oxynitride Glasses.

DTIC Science & Technology

1982-07-01

The upsurge in interest in these glasses was originally motivated by their relevance to the processing of Si 3 1 4 -based ceramics (4, 5) when it was...are suggested by results obtained so far, among them refractory glass - ceramics , leach-resistant glasses , hardened optical windows, and Joining...compositions for ceramic - ceramic seals. Oxynitride Glass Synthesis The preparation of oxynitride glasses is more complex than preparation of conventional

Stability analysis of multipoint tool equipped with metal cutting ceramics

NASA Astrophysics Data System (ADS)

Maksarov, V. V.; Khalimonenko, A. D.; Matrenichev, K. G.

2017-10-01

The article highlights the issues of determining the stability of the cutting process by a multipoint cutting tool equipped with cutting ceramics. There were some recommendations offered on the choice of parameters of replaceable cutting ceramic plates for milling based of the conducted researches. Ceramic plates for milling are proposed to be selected on the basis of value of their electrical volume resistivity.

Light emitting ceramic device and method for fabricating the same

DOEpatents

Valentine, Paul; Edwards, Doreen D.; Walker Jr., William John; Slack, Lyle H.; Brown, Wayne Douglas; Osborne, Cathy; Norton, Michael; Begley, Richard

2004-11-30

A light-emitting ceramic based panel, hereafter termed "electroceramescent" panel, and alternative methods of fabrication for the same are claimed. The electroceramescent panel is formed on a substrate providing mechanical support as well as serving as the base electrode for the device. One or more semiconductive ceramic layers directly overlay the substrate, and electrical conductivity and ionic diffusion are controlled. Light emitting regions overlay the semiconductive ceramic layers, and said regions consist sequentially of a layer of a ceramic insulation layer and an electroluminescent layer, comprised of doped phosphors or the equivalent. One or more conductive top electrode layers having optically transmissive areas overlay the light emitting regions, and a multi-layered top barrier cover comprising one or more optically transmissive non-combustible insulation layers overlay said top electrode regions.

Analysis of Shear Bond Strength and Morphology of Er:YAG Laser-Recycled Ceramic Orthodontic Brackets

PubMed Central

Han, Ruo-qiao; Ji, Ling-fei; Ling, Chen

2016-01-01

Objective. The aim of this study was to compare the recycling of deboned ceramic brackets via an Er:YAG laser or via the traditional chairside processing methods of flaming and sandblasting; shear bond strength and morphological changes were evaluated in recycled brackets versus new brackets. Materials and Methods. 3M Clarity Self-Ligating Ceramic Brackets with a microcrystalline base were divided into groups subjected to flaming, sandblasting, or exposure to an Er:YAG laser. New ceramic brackets served as a control group. Shear bond strengths were determined with an Electroforce test machine and tested for statistical significance through analysis of variance. Morphological examinations of the recycled ceramic bracket bases were conducted with scanning electron microscopy and confocal laser scanning microscopy. Residue on the bracket base was analyzed with Raman spectroscopy. Results. Faded, dark adhesive was left on recycled bracket bases processed via flaming. Adhesive was thoroughly removed by both sandblasting and exposure to an Er:YAG laser. Compared with new brackets, shear bond strength was lower after sandblasting (p < 0.05), but not after exposure to an Er:YAG laser. The Er:YAG laser caused no damage to the bracket. Conclusion. Er:YAG lasers effectively remove adhesive from the bases of ceramic brackets without damaging them; thus, this method may be preferred over other recycling methods. PMID:27047964

Current progress in bioactive ceramic scaffolds for bone repair and regeneration.

PubMed

Gao, Chengde; Deng, Youwen; Feng, Pei; Mao, Zhongzheng; Li, Pengjian; Yang, Bo; Deng, Junjie; Cao, Yiyuan; Shuai, Cijun; Peng, Shuping

2014-03-18

Bioactive ceramics have received great attention in the past decades owing to their success in stimulating cell proliferation, differentiation and bone tissue regeneration. They can react and form chemical bonds with cells and tissues in human body. This paper provides a comprehensive review of the application of bioactive ceramics for bone repair and regeneration. The review systematically summarizes the types and characters of bioactive ceramics, the fabrication methods for nanostructure and hierarchically porous structure, typical toughness methods for ceramic scaffold and corresponding mechanisms such as fiber toughness, whisker toughness and particle toughness. Moreover, greater insights into the mechanisms of interaction between ceramics and cells are provided, as well as the development of ceramic-based composite materials. The development and challenges of bioactive ceramics are also discussed from the perspective of bone repair and regeneration.

Current Progress in Bioactive Ceramic Scaffolds for Bone Repair and Regeneration

PubMed Central

Gao, Chengde; Deng, Youwen; Feng, Pei; Mao, Zhongzheng; Li, Pengjian; Yang, Bo; Deng, Junjie; Cao, Yiyuan; Shuai, Cijun; Peng, Shuping

2014-01-01

Bioactive ceramics have received great attention in the past decades owing to their success in stimulating cell proliferation, differentiation and bone tissue regeneration. They can react and form chemical bonds with cells and tissues in human body. This paper provides a comprehensive review of the application of bioactive ceramics for bone repair and regeneration. The review systematically summarizes the types and characters of bioactive ceramics, the fabrication methods for nanostructure and hierarchically porous structure, typical toughness methods for ceramic scaffold and corresponding mechanisms such as fiber toughness, whisker toughness and particle toughness. Moreover, greater insights into the mechanisms of interaction between ceramics and cells are provided, as well as the development of ceramic-based composite materials. The development and challenges of bioactive ceramics are also discussed from the perspective of bone repair and regeneration. PMID:24646912

Tribology of ceramics: Report of the Committee on Tribology of Ceramics

NASA Technical Reports Server (NTRS)

1988-01-01

The current state of knowledge of ceramic surface structures, composition, and reactivity is reviewed. The tribological requirements of advanced mechanical systems now being deployed (in particular, heat engines) exceed the capabilities of traditional metallic-based materials because of the high temperatures encountered. Advanced ceramic materials for such applications are receiving intense scrutiny, but there is a lack of understanding of the properties and behavior of ceramic surfaces and the influence of processing on the properties of ceramics is described. The adequacy of models, ranging form atomic to macro, to describe and to predict ceramic friction and wear are discussed, as well as what is known about lubrication at elevated temperatures. From this analysis, recommendations are made for coordination, research, and development that will lead to better performance of ceramic materials in tribological systems.

The "in situ molding technique: " an accurate and simple way to fix resorbable plates to the facial skeleton.

PubMed

Sadigh, Parviz Lionel; Chang, Li-Ren; Feng, Kuan-Ming; Jeng, Seng-Feng

2014-09-01

Bioabsorbable plates developed for use in the facial skeleton have become an integral part of the craniomaxillofacial surgeon's reconstructive armamentarium. They avoid the problems associated with the retention of metal plates and can be easily contoured when heated in a thermobath. The technical process of molding and securing these devices, often through small access incisions, to achieve rigid fixation of facial fractures can be difficult. In this article, we describe a simple, novel technique that we have developed, using hot water suction irrigation, to achieve in situ molding of resorbable plates during facial fracture fixation. We used this technique to fix 123 facial fractures in 110 patients over a 4-year period. No complications secondary to the use of hot water suction irrigation were encountered.

Bioactive Glass Scaffolds for Dental Pulp and Dentin Tissue Engineering

NASA Astrophysics Data System (ADS)

Shawli, Hassan Talat

Current and historical endodontic "root canal" treatments employ inert obturating materials inserted into the teeth's pulp chambers and root canals, often saving teeth but without adequate function. Furthermore, the occurrence of pulpal necrosis in the immature permanent tooth is considered to be a challenging situation, clinically, in treatment because the thin and often short roots increase the risk of fracture. The ideal treatment would be to promote continued root development. This work demonstrated that endodontically-shaped and durable scaffolds of slowly resorbable fibrous (HT) glass and faster-resorbing small-particle Bioglass can be sintered at 900 degrees C for such placement, and that cell growth of osteoblasts in these scaffolds shows good early results. Retained bioactivity in the sintered specimen was revealed by Multiple Attenuated Internal Reflection Infrared Spectroscopy.

Translucency of zirconia-based pressable ceramics with different core and veneer thicknesses.

PubMed

Jeong, Il-Do; Bae, So-Yeon; Kim, Dong-Yeon; Kim, Ji-Hwan; Kim, Woong-Chul

2016-06-01

Little information is available on the translucency of zirconia-based pressable ceramic restorations with a pressed ceramic veneer and zirconia core in various thickness combinations. The purpose of this in vitro study was to assess the translucency of 3 types of zirconia-based pressable ceramics for different core-veneer thickness combinations. A bilayered ceramic specimen was prepared with a pressable ceramic (IPS e.max Zirpress, Initial IQ, Rosetta UltraPress) veneer over a zirconia core (Zenostar Zr). Three groups of specimens (n=7) were formed with the following core+veneer thicknesses: 1 +0.5 mm, 0.7 +0.8 mm, and 0.5 +1 mm. To obtain consistent thickness and high translucency, all specimens were subjected to surface grinding with a grinding machine. To eliminate the effect of differences in roughness on the translucency, the surface roughness of the ground specimens was measured with a scanning profiler, and the consistency of these measured values was verified through statistical analysis. The luminous transmittance of the specimens was measured with a spectrophotometer. The effects of the pressable ceramic type and core-veneer thickness combination on transmittance were assessed using a 2-way ANOVA (α=.05). The consistency of the surface roughness among the tested specimens was confirmed using a 1-way ANOVA and the Tukey HSD post hoc test (P<.05). The luminous transmittance exhibited a statistically significant dependence on both the type of pressable ceramic and the core-veneer thickness combination (P<.05). The type of pressable ceramic and core-veneer thickness combination affected the translucency of the restoration. Copyright © 2016 Editorial Council for the Journal of Prosthetic Dentistry. Published by Elsevier Inc. All rights reserved.

Transmission of Er:YAG laser through different dental ceramics.

PubMed

Sari, Tugrul; Tuncel, Ilkin; Usumez, Aslihan; Gutknecht, Norbert

2014-01-01

The aim of this study was to determine the erbium-doped yttrium aluminum garnet (Er:YAG) laser transmission ratio through different dental ceramics with different thicknesses. Laser debonding procedure of adhesively luted all-ceramic restorations is based on the transmission of laser energy through the ceramic and the ablation of resin cement, because of the transmitted laser energy. Five different dental ceramics were evaluated in this study: sintered zirconium-oxide core ceramic, monolithic zirconium-oxide ceramic, feldspathic ceramic, leucite-reinforced glass ceramic, and lithium disilicate-reinforced glass ceramic. Two ceramic discs with different thicknesses (0.5 and 1 mm) were fabricated for each group. Ceramic discs were placed between the sensor membrane of the laser power meter and the tip of the contact handpiece of an Er:YAG laser device with the aid of a custom- made acrylic holder. The transmission ratio of Er:YAG laser energy (500 mJ, 2 Hz, 1 W, 1000 μs) through different ceramic discs was measured with the power meter. Ten measurements were made for each group and the results were analyzed with two way analysis of variance (ANOVA) and Tukey honestly significant difference (HSD) tests. The highest transmission ratio was determined for lithium disilicate-reinforced ceramic with 0.5 mm thickness (88%) and the lowest was determined for feldspathic ceramic with 1 mm thickness (44%). The differences among the different ceramics and between the different thicknesses were significant (p<0.05). Ceramic type and thickness should be taken into consideration to adjust the laser irradiation parameters during laser debonding of adhesively luted all-ceramic restorations.

Reactive Processing of Environmentally Conscious, Biomorphic Ceramics from Natural Wood Precursors

NASA Technical Reports Server (NTRS)

Singh, M.; Yee, Bo-Moon

2003-01-01

Environmentally conscious, biomorphic ceramics (Ecoceramics) are a new class of materials that are manufactured from renewable resources and wastes. In this study, silicon carbide and oxide-based biomorphic ceramics have been fabricated from pine and jelutong wood precursors. A carbonaceous preform is produced through wood pyrolysis and subsequent infiltration with oxides (ZrO2 sols) and liquid silicon to form ceramics. These biomorphic ceramics show a wide variety of microstructures, densities, and hardness behavior that are determined by the type of wood and infiltrants selected.

Creep and Oxidation of Hafnium Diboride Based Ultra High Temperature Ceramics at 1500C

DTIC Science & Technology

2015-12-01

through experimentation. Although the Literature Review showed that some theories and models have been developed based on extensive experimental results...of Some Refractory Metals & Ceramics [Fahrenholtz] ........... 14 Figure 4: Creep Strain vs Time Based on Burgers Model ...

Fixation of fractures of the condylar head of the mandible with a new magnesium-alloy biodegradable cannulated headless bone screw.

PubMed

Leonhardt, H; Franke, A; McLeod, N M H; Lauer, G; Nowak, A

2017-07-01

It is difficult to fix fractures of the condylar head of the mandible. Several techniques have been described which show satisfactory outcomes, but stability can be questionable, and some can cause irritation of the soft tissues. We describe a technique and first results of treating such fractures with resorbable magnesium-based headless bone screws (Magnezix ® 2.7mm CS; Syntellix AG, Hanover, Germany). Copyright © 2017 The British Association of Oral and Maxillofacial Surgeons. Published by Elsevier Ltd. All rights reserved.

Optimization of the injection molding process for development of high performance calcium oxide -based ceramic cores

NASA Astrophysics Data System (ADS)

Zhou, P. P.; Wu, G. Q.; Tao, Y.; Cheng, X.; Zhao, J. Q.; Nan, H.

2018-02-01

The binder composition used for ceramic injection molding plays a crucial role on the final properties of sintered ceramic and to avoid defects on green parts. In this study, the effects of binder compositions on the rheological, microstructures and the mechanical properties of CaO based ceramic cores were investigated. It was found that the optimized formulation for dispersant, solid loading was 1.5 wt% and 84 wt%, respectively. The microstructures, such as porosity, pore size distribution and grain boundary density were closely related to the plasticizer contents. The decrease of plasticizer contents can enhance the strength of the ceramic cores but with decreased shrinkage. Meanwhile, the creep resistance of ceramic cores was enhanced by decreasing of plasticizer contents. The flexural strength of the core was found to decrease with the increase of the porosity, the improvement of creep resistance is closely related to the decrease of porosity and grain boundary density.

Hip Squeaking after Ceramic-on-ceramic Total Hip Arthroplasty

PubMed Central

Wu, Guo-Liang; Zhu, Wei; Zhao, Yan; Ma, Qi; Weng, Xi-Sheng

2016-01-01

Objective: The present study aimed to review the characteristics and influencing factors of squeaking after ceramic-on-ceramic (CoC) total hip arthroplasty (THA) and to analyze the possible mechanisms of the audible noise. Data Sources: The data analyzed in this review were based on articles from PubMed and Web of Science. Study Selection: The articles selected for review were original articles and reviews found based on the following search terms: “total hip arthroplasty”, “ceramic-on-ceramic”, “hip squeaking”, and “hip noise.” Results: The mechanism of the squeaking remains unknown. The possible explanations included stripe wear, edge loading, a third body, fracture of the ceramic liner, and resonance of the prosthesis components. Squeaking occurrence is influenced by patient, surgical, and implant factors. Conclusions: Most studies indicated that squeaking after CoC THA was the consequence of increasing wear or impingement, caused by prosthesis design, patient characteristics, or surgical factors. However, as conflicts exist among different articles, the major reasons for the squeaking remain to be identified. PMID:27453238

Structure and conductivity of nanostructured YBCO ceramics

NASA Astrophysics Data System (ADS)

Palchayev, D. K.; Gadzhimagomedov, S. Kh; Murlieva, Zh Kh; Rabadanov, M. Kh; Emirov, R. M.

2017-12-01

Superconducting nanostructured ceramics based on YBa2Cu3O7-δ were made of nanopowder obtained by burning nitrate-organic precursors. The structure, morphology, electrical resistivity, and density of ceramics were studied. Various porosity values of the ceramics were achieved by preliminary heat treatment of the nanopowder. The features of conductivity and the reason for increase of the of the superconducting transition temperature in these materials are discussed.

Formation of chemically bonded ceramics with magnesium dihydrogen phosphate binder

DOEpatents

Wagh, Arun S.; Jeong, Seung-Young

2004-08-17

A new method for combining magnesium oxide, MgO, and magnesium dihydrogen phosphate to form an inexpensive compactible ceramic to stabilize very low solubility metal oxides, ashes, swarfs, and other iron or metal-based additives, to create products and waste forms which can be poured or dye cast, and to reinforce and strengthen the ceramics formed by the addition of fibers to the initial ceramic mixture.

Structures and properties of alumina-based ceramic for reconstructive oncology

NASA Astrophysics Data System (ADS)

Grigoriev, M. V.; Kulkov, S. N.

2016-08-01

The microstructure of alumina ceramics based on powders with a varying grain size has been investigated. Both commercial alumina powders and those fabricated by denitration of aluminum salts in high-frequency discharge plasma were used. It is shown that the variation of the sintering temperature and morphology of the initial powders of the particles leads to a change of the pore structure of ceramics from pore isolated clusters to a structure consisting of a ceramic skeleton and a large pore space. Changing the type of pore structure occurs at about 50% of porosity. The ceramic pore size distribution is bimodal. Dependencies final density vs initial density are linear; at the same time with increasing temperature, inclination of changes from positive to negative, indicating the change of sealing mechanisms. Extrapolation of these curves showed that they intersect with the values of density of about 2 g/cm3, which indicates the possibility of producing non-shrink ceramics. It is shown that the strength increases with increasing nanocrystalline alumina content in powder mixture. A change in the character the pore structure is accompanied by a sharp decrease in strength, which corresponds to the percolation transition in ceramics. These results showed that it is possible to obtain ceramic materials with the structure and properties similar to natural bone.

A facile method to enhance the uniformity and adhesion properties of water-based ceramic coating layers on hydrophobic polyethylene separators

NASA Astrophysics Data System (ADS)

Lee, Hoogil; Jeon, Hyunkyu; Gong, Seokhyeon; Ryou, Myung-Hyun; Lee, Yong Min

2018-01-01

To enhance the uniformity and adhesion properties of water-based ceramic coating layers on hydrophobic polyethylene (PE) separators, their surfaces were treated with thin and hydrophilic polydopamine layers. As a result, an aqueous ceramic coating slurry consisting of Al2O3 particles, carboxyl methyl cellulose (CMC) binders, and water solvent was easily spread on the separator surface, and a uniform ceramic layer was formed after solvent drying. Moreover, the ceramic coating layer showed greatly improved adhesion properties to the PE separator surface. Whereas the adhesion strength within the bulk coating layer (Fmid) ranged from 43 to 86 N m-1 depending on the binder content of 1.5-3.0 wt%, the adhesion strength at the interface between the ceramic coating layer and PE separator (Fsepa-Al2O3) was 245-360 N m-1, a value equivalent to an increase of four or five times. Furthermore, an additional ceramic coating layer of approximately 7 μm did not degrade the ionic conductivity and electrochemical properties of the bare PE separators. Thus, all the LiMn2O4/graphite cells with ceramic-coated separators delivered an improved cycle life and rate capability compared with those of the control cells with bare PE separators.

Intercalated Nanocomposites Based on High-Temperature Superconducting Ceramics and Their Properties

PubMed Central

Tonoyan, Anahit; Schiсk, Christoph; Davtyan, Sevan

2009-01-01

High temperature superconducting (SC) nanocomposites based on SC ceramics and various polymeric binders were prepared. Regardless of the size of the ceramics’ grains, the increase of their amount leads to an increase of resistance to rupture and modulus and a decrease in limiting deformation, whereas an increase in the average ceramic grain size worsens resistance properties. The SC, thermo-chemical, mechanical and dynamic-mechanical properties of the samples were investigated. Superconducting properties of the polymer ceramic nanocomposites are explained by intercalation of macromolecule fragments into the interstitial layer of the ceramics’ grains. This phenomenon leads to a change in the morphological structure of the superconducting nanocomposites.

Considerations on Dop (Depth Of Penetration) Test for Evaluation of Ceramics Materials Used in Ballistic Protection

NASA Astrophysics Data System (ADS)

Popa, Ioan-Dan; Dobriţa, Florin

2017-12-01

Tremendous amount of funds and other resorces were invested in studying the response of ceramic materials under ballistic impact, the main goal being to find a way to increase the protection of soldiers and the vehicles used in the modern battlespace. Using of ceramic materials especially carbon based (carbides), nitrogen based (nitrides) and oxygen based (oxides) ceramics in order to increase the protection level of ballistic equipment could be, sometimes, a big challenge when trying to use the proper test in order to evaluate and compare their performances. The role of the tests is to provide a better understanding of their response in different situations and, as a consequence, to make them more efficient as armour components through future improvements. The paper presents shortly the main tests which are used and eventually standardised for evaluating the ballistic behaviour of the ceramics and other armour components, with a special focus to DOP (Depth of Penetration) Tests.

Joining of Silicon Carbide-Based Ceramics by Reaction Forming Method

NASA Technical Reports Server (NTRS)

Singh, M.; Kiser, J. D.

1997-01-01

Recently, there has been a surge of interest in the development and testing of silicon-based ceramics and composite components for a number of aerospace and ground based systems. The designs often require fabrication of complex shaped parts which can be quite expensive. One attractive way of achieving this goal is to build up complex shapes by joining together geometrically simple shapes. However, the joints should have good mechanical strength and environmental stability comparable to the bulk materials. These joints should also be able to maintain their structural integrity at high temperatures. In addition, the joining technique should be practical, reliable, and affordable. Thus, joining has been recognized as one of the enabling technologies for the successful utilization of silicon carbide based ceramic components in high temperature applications. Overviews of various joining techniques, i.e., mechanical fastening, adhesive bonding, welding, brazing, and soldering have been provided in recent publications. The majority of the techniques used today are based on the joining of monolithic ceramics with metals either by diffusion bonding, metal brazing, brazing with oxides and oxynitrides, or diffusion welding. These techniques need either very high temperatures for processing or hot pressing (high pressures). The joints produced by these techniques have different thermal expansion coefficients than the ceramic materials, which creates a stress concentration in the joint area. The use temperatures for these joints are around 700 C. Ceramic joint interlayers have been developed as a means of obtaining high temperature joints. These joint interlayers have been produced via pre-ceramic polymers, in-situ displacement reactions, and reaction bonding techniques. Joints produced by the pre-ceramic polymer approach exhibit a large amounts of porosity and poor mechanical properties. On the other hand, hot pressing or high pressures are needed for in-situ displacement reactions and reaction bonding techniques. Due to the equipment required, these techniques are impractical for joining large or complex shaped components.

Multiscale Modeling and Process Optimization for Engineered Microstructural Complexity

DTIC Science & Technology

2007-10-26

R. C. Rogan, E. Üstündag, M. R. Daymond and V. Knoblauch Ferroelastic Behavior of PZT -Based Ferroelectric Ceramics , Materials Science Forum, 404...Bhattacharya, Materials Science Seminar, University of Southern California, 2003. 42. R.C. Rogan, Texture and Strain Analysis of PZT by In-Situ...Annual Meeting of the American Ceramic Society, St. Louis, MO; May 2002. 44. R. Rogan, Ferroelastic Behavior of PZT -Based Ferroelectric Ceramics , 6th

CERAMIC: Case-Control Association Testing in Samples with Related Individuals, Based on Retrospective Mixed Model Analysis with Adjustment for Covariates

PubMed Central

Zhong, Sheng; McPeek, Mary Sara

2016-01-01

We consider the problem of genetic association testing of a binary trait in a sample that contains related individuals, where we adjust for relevant covariates and allow for missing data. We propose CERAMIC, an estimating equation approach that can be viewed as a hybrid of logistic regression and linear mixed-effects model (LMM) approaches. CERAMIC extends the recently proposed CARAT method to allow samples with related individuals and to incorporate partially missing data. In simulations, we show that CERAMIC outperforms existing LMM and generalized LMM approaches, maintaining high power and correct type 1 error across a wider range of scenarios. CERAMIC results in a particularly large power increase over existing methods when the sample includes related individuals with some missing data (e.g., when some individuals with phenotype and covariate information have missing genotype), because CERAMIC is able to make use of the relationship information to incorporate partially missing data in the analysis while correcting for dependence. Because CERAMIC is based on a retrospective analysis, it is robust to misspecification of the phenotype model, resulting in better control of type 1 error and higher power than that of prospective methods, such as GMMAT, when the phenotype model is misspecified. CERAMIC is computationally efficient for genomewide analysis in samples of related individuals of almost any configuration, including small families, unrelated individuals and even large, complex pedigrees. We apply CERAMIC to data on type 2 diabetes (T2D) from the Framingham Heart Study. In a genome scan, 9 of the 10 smallest CERAMIC p-values occur in or near either known T2D susceptibility loci or plausible candidates, verifying that CERAMIC is able to home in on the important loci in a genome scan. PMID:27695091

Light-weight ceramic insulation

NASA Technical Reports Server (NTRS)

Hsu, Ming-Ta S. (Inventor); Chen, Timothy S. (Inventor)

2002-01-01

Ultra-high temperature, light-weight, ceramic insulation such as ceramic tile is obtained by pyrolyzing a siloxane gel derived from the reaction of at least one organo dialkoxy silane and at least one tetralkoxy silane in an acid or base liquid medium. The reaction mixture of the tetra- and dialkoxy silanes may contain also an effective amount of a mono- or trialkoxy silane to obtain the siloxane gel. The siloxane gel is dried at ambient pressures to form a siloxane ceramic precursor without significant shrinkage. The siloxane ceramic precursor is subsequently pyrolyzed, in an inert atmosphere, to form the black ceramic insulation comprising atoms of silicon, carbon and oxygen. The ceramic insulation, can be characterized as a porous, uniform ceramic tile resistant to oxidation at temperatures ranging as high as 1700.degree. C. and is particularly useful as lightweight tiles for spacecraft and other high-temperature insulation applications.

Thermal barrier coatings

DOEpatents

Alvin, Mary Anne [Pittsburg, PA

2010-06-22

This disclosure addresses the issue of providing a metallic-ceramic overlay coating that potentially serves as an interface or bond coat layer to provide enhanced oxidation resistance to the underlying superalloy substrate via the formation of a diffusion barrier regime within the supporting base material. Furthermore, the metallic-ceramic coating is expected to limit the growth of a continuous thermally grown oxide (TGO) layer that has been primarily considered to be the principal cause for failure of existing TBC systems. Compositional compatibility of the metallic-ceramic with traditional yttria-stabilized zirconia (YSZ) top coats is provided to further limit debond or spallation of the coating during operational use. A metallic-ceramic architecture is disclosed wherein enhanced oxidation resistance is imparted to the surface of nickel-based superalloy or single crystal metal substrate, with simultaneous integration of the yttria stabilized zirconia (YSZ) within the metallic-ceramic overlayer.

Design of a dielectric resonator receive array at 7 Tesla using detunable ceramic resonators

NASA Astrophysics Data System (ADS)

Ruytenberg, Thomas; Webb, Andrew G.

2017-11-01

Ceramic-based dielectric resonators can be used for high frequency magnetic resonance imaging and microscopy. When used as elements in a transmit array, the intrinsically low inter-element coupling allows flexibility in designing different geometric arrangements for different regions-of-interest. However, without being able to detune such resonators, they cannot be used as elements in a receive-only array. Here, we propose and implement a method, based on mode-disruption, for detuning ceramic-based dielectric resonators to enable them to be used as receive-only elements.

Research and Development of High Energy 2 - Micron Lasers Based on TM: Doped Ceramic Laser Gain Media and TM: Doped Optical Fibers

DTIC Science & Technology

2016-07-20

AFRL-AFOSR-VA-TR-2016-0257 RESEARCH AND DEVELOPMENT OF HIGH ENERGY 2 - MICRON LASERS BASED ON TM: DOPED CERAMIC LASER GAIN MEDIA AND TM: DOPED...2010 to 01/03/2016 4. TITLE AND SUBTITLE RESEARCH AND DEVELOPMENT OF HIGH ENERGY 2 - MICRON LASERS BASED ON TM: DOPED CERAMIC LASER GAIN MEDIA AND...NOTES 14. ABSTRACT Our research and development of 2-μm femtosecond lasers has included development of mode-locked Tm:fiber lasers , super-continuum

Manufacture of a ceramic paper for art applications

NASA Astrophysics Data System (ADS)

Dölle, K.; Honig, A.; Piatkowski, J.; Kuempel, C.

2018-01-01

Ceramic paper products are mostly used as high temperature ceramic insulation products. They offer an effective solution for most demanding heat management and insulation applications. The objective for this research project was to create a ceramic paper like product that combines the advantages of paper fibers, ceramic filler, and a clay product into one product, which can be produced on a continuous base with a paper machine. The produced ceramic paper product had a ceramic filler level between 59.68% and 78.8% with a basis weight between 322.9 g/m² and 693.7 g/m², and a final moisture content of 58.6% to 44.7% respectively. The wooden fiber served as a support medium for the ceramic filler material during production on the paper machine and during the conversion process into art pieces. During firing in a kiln, the fiber material combusted and the ceramic filler material mixture acts as common pottery clay, holding the desired shape of the art pieces produced.

Radiopaque Strontium Fluoroapatite Glass-Ceramics.

PubMed

Höland, Wolfram; Schweiger, Marcel; Dittmer, Marc; Ritzberger, Christian

2015-01-01

The controlled precipitation of strontium fluoroapatite crystals was studied in four base glass compositions derived from the SiO2-Al2O3-Y2O3-SrO-Na2O-K2O/Rb2O/Cs2O-P2O5-F system. The crystal phase formation of these glasses and the main properties of the glass-ceramics, such as thermal and optical properties and radiopacity were compared with a fifth, a reference glass-ceramic. The reference glass-ceramic was characterized as Ca-fluoroapatite glass-ceramic. The four strontium fluoroapatite glass-ceramics showed the following crystal phases: (a) Sr5(PO4)3F - leucite, KAlSi2O6, (b) Sr5(PO4)3F - leucite, KAlSi2O6, and nano-sized NaSrPO4, (c) Sr5(PO4)3F - pollucite, CsAlSi2O6, and nano-sized NaSrPO4, and (d) Sr5(PO4)3F - Rb-leucite, RbAlSi2O6, and nano-sized NaSrPO4. The proof of crystal phase formation was possible by X-ray diffraction. The microstructures, which were studied using scanning electron microscopy, demonstrated a uniform distribution of the crystals in the glass matrix. The Sr-fluoroapatites were precipitated based on an internal crystallization process, and the crystals demonstrated a needle-like morphology. The study of the crystal growth of needle-like Sr-fluoroapatites gave a clear evidence of an Ostwald ripening mechanism. The formation of leucite, pollucite, and Rb-leucite was based on a surface crystallization mechanism. Therefore, a twofold crystallization mechanism was successfully applied to develop these types of glass-ceramics. The main focus of this study was the controlled development of glass-ceramics exhibiting high radiopacity in comparison to the reference glass-ceramic. This goal could be achieved with all four glass-ceramics with the preferred development of the Sr-fluoroapatite - pollucite-type glass-ceramic. In addition to this main development, it was possible to control the thermal properties. Especially the Rb-leucite containing glass-ceramic showed the highest coefficient of thermal expansion (CTE). These glass-ceramics allow optical properties, especially the translucency and color, to be tailored to the needs of biomaterials for dental applications. The authors conclude that it is possible to use twofold crystallization processes to develop glass-ceramic biomaterials featuring different properties, such as specific radiopacity values, CTEs, and optical characteristics.

Radiopaque Strontium Fluoroapatite Glass-Ceramics

PubMed Central

Höland, Wolfram; Schweiger, Marcel; Dittmer, Marc; Ritzberger, Christian

2015-01-01

The controlled precipitation of strontium fluoroapatite crystals was studied in four base glass compositions derived from the SiO2–Al2O3–Y2O3–SrO–Na2O–K2O/Rb2O/Cs2O–P2O5–F system. The crystal phase formation of these glasses and the main properties of the glass-ceramics, such as thermal and optical properties and radiopacity were compared with a fifth, a reference glass-ceramic. The reference glass-ceramic was characterized as Ca-fluoroapatite glass-ceramic. The four strontium fluoroapatite glass-ceramics showed the following crystal phases: (a) Sr5(PO4)3F – leucite, KAlSi2O6, (b) Sr5(PO4)3F – leucite, KAlSi2O6, and nano-sized NaSrPO4, (c) Sr5(PO4)3F – pollucite, CsAlSi2O6, and nano-sized NaSrPO4, and (d) Sr5(PO4)3F – Rb-leucite, RbAlSi2O6, and nano-sized NaSrPO4. The proof of crystal phase formation was possible by X-ray diffraction. The microstructures, which were studied using scanning electron microscopy, demonstrated a uniform distribution of the crystals in the glass matrix. The Sr-fluoroapatites were precipitated based on an internal crystallization process, and the crystals demonstrated a needle-like morphology. The study of the crystal growth of needle-like Sr-fluoroapatites gave a clear evidence of an Ostwald ripening mechanism. The formation of leucite, pollucite, and Rb-leucite was based on a surface crystallization mechanism. Therefore, a twofold crystallization mechanism was successfully applied to develop these types of glass-ceramics. The main focus of this study was the controlled development of glass-ceramics exhibiting high radiopacity in comparison to the reference glass-ceramic. This goal could be achieved with all four glass-ceramics with the preferred development of the Sr-fluoroapatite – pollucite-type glass-ceramic. In addition to this main development, it was possible to control the thermal properties. Especially the Rb-leucite containing glass-ceramic showed the highest coefficient of thermal expansion (CTE). These glass-ceramics allow optical properties, especially the translucency and color, to be tailored to the needs of biomaterials for dental applications. The authors conclude that it is possible to use twofold crystallization processes to develop glass-ceramic biomaterials featuring different properties, such as specific radiopacity values, CTEs, and optical characteristics. PMID:26528470

Ceramic-ceramic shell tile thermal protection system and method thereof

NASA Technical Reports Server (NTRS)

Riccitiello, Salvatore R. (Inventor); Smith, Marnell (Inventor); Goldstein, Howard E. (Inventor); Zimmerman, Norman B. (Inventor)

1986-01-01

A ceramic reusable, externally applied composite thermal protection system (TPS) is proposed. The system functions by utilizing a ceramic/ceramic upper shell structure which effectively separates its primary functions as a thermal insulator and as a load carrier to transmit loads to the cold structure. The composite tile system also prevents impact damage to the atmospheric entry vehicle thermal protection system. The composite tile comprises a structurally strong upper ceramic/ceramic shell manufactured from ceramic fibers and ceramic matrix meeting the thermal and structural requirements of a tile used on a re-entry aerospace vehicle. In addition, a lightweight high temperature ceramic lower temperature base tile is used. The upper shell and lower tile are attached by means effective to withstand the extreme temperatures (3000 to 3200F) and stress conditions. The composite tile may include one or more layers of variable density rigid or flexible thermal insulation. The assembly of the overall tile is facilitated by two or more locking mechanisms on opposing sides of the overall tile assembly. The assembly may occur subsequent to the installation of the lower shell tile on the spacecraft structural skin.

Characterizing ceramics and the interfacial adhesion to resin: I - The relationship of microstructure, composition, properties and fractography.

PubMed

Della Bona, Alvaro

2005-03-01

The appeal of ceramics as structural dental materials is based on their light weight, high hardness values, chemical inertness, and anticipated unique tribological characteristics. A major goal of current ceramic research and development is to produce tough, strong ceramics that can provide reliable performance in dental applications. Quantifying microstructural parameters is important to develop structure/property relationships. Quantitative microstructural analysis provides an association among the constitution, physical properties, and structural characteristics of materials. Structural reliability of dental ceramics is a major factor in the clinical success of ceramic restorations. Complex stress distributions are present in most practical conditions and strength data alone cannot be directly extrapolated to predict structural performance.

Ceramic Technology for Advanced Heat Engines Project. Semiannual progress report, October 1984-March 1985

DOE Office of Scientific and Technical Information (OSTI.GOV)

Not Available

1985-09-01

A five-year project plan was developed with extensive input from private industry. The objective of the project is to develop the industrial technology base required for reliable ceramics for application in advanced automotive heat engines. The project approach includes determining the mechanisms controlling reliability, improving processes for fabricating existing ceramics, developing new materials with increased reliability, and testing these materials in simulated engine environments to confirm reliability. Although this is a generic materials project, the focus is on structural ceramics for advanced gas turbine and diesel engines, ceramic bearings and attachments, and ceramic coatings for thermal barrier and wear applicationsmore » in these engines.« less

Ceramic technology for advanced heat engines project: Semiannual progress report for April through September 1986

DOE Office of Scientific and Technical Information (OSTI.GOV)

Not Available

1987-03-01

An assessment of needs was completed, and a five-year project plan was developed with extensive input from private industry. Objective is to develop the industrial technology base required for reliable ceramics for application in advanced automotive heat engines. The project approach includes determining the mechanisms controlling reliability, improving processes for fabricating existing ceramics, developing new materials with increased reliability, and testing these materials in simulated engine environments to confirm reliability. Although this is a generic materials project, the focus is on structural ceramics for advanced gas turbine and diesel engines, ceramic bearings and attachments, and ceramic coatings for thermal barriermore » and wear applications in these engines.« less

Wound Healing Complications Following Guided Bone Regeneration for Ridge Augmentation: A Systematic Review and Meta-Analysis.

PubMed

Lim, Glendale; Lin, Guo-Hao; Monje, Alberto; Chan, Hsun-Liang; Wang, Hom-Lay

The rate of developing soft tissue complications that accompany guided bone regeneration (GBR) procedures varies widely, from 0% to 45%. The present review was conducted to investigate the rate for resorbable versus nonresorbable membranes and the timing of soft tissue complications. Electronic and manual literature searches were conducted by two independent reviewers using several databases, including MEDLINE, EMBASE, Cochrane Central Register of Controlled Trials, and Cochrane Oral Health Group Trials Register, for articles published through July 2015, with no language restriction. Articles were included if they were clinical trials aimed at demonstrating the incidence of soft tissue complications following GBR procedures. Overall, 21 and 15 articles were included in the qualitative and quantitative synthesis, respectively. The weighted complication rate of the overall soft tissue complications, including membrane exposure, soft tissue dehiscence, and acute infection/abscess, into the calculation was 16.8% (95% CI = 10.6% to 25.4%). When considering the complication rate based on membrane type used, resorbable membrane was associated with a weighted complication rate of 18.3% (95% CI: 10.4% to 30.4%) and nonresorbable membrane with a rate of 17.6% (95% CI: 10.0% to 29.3%). Moreover, soft tissue lesions were reported as early as 1 week and as late as 6 months based on the included studies. Soft tissue complications after GBR are common (16.8%). Membrane type did not appear to significantly affect the complication rate, based on the limited number of data retrieved in this study. Technique sensitivity (ie, soft tissue management) may still be regarded as the main component to avoid soft tissue complications and, hence, to influence the success of bone regenerative therapy.

Fracture mode during cyclic loading of implant-supported single-tooth restorations.

PubMed

Hosseini, Mandana; Kleven, Erik; Gotfredsen, Klaus

2012-08-01

Fracture of veneering ceramics in zirconia-based restorations has frequently been reported. Investigation of the fracture mode of implant-supported ceramic restorations by using clinically relevant laboratory protocols is needed. This study compared the mode of fracture and number of cyclic loads until veneering fracture when ceramic and metal ceramic restorations with different veneering ceramics were supported by implants. Thirty-two implant-supported single-tooth restorations were fabricated. The test group was composed of 16 ceramic restorations of zirconia abutment-retained crowns with zirconia copings veneered with glass-ceramics (n=8) and feldspathic ceramics (n=8). The control group was composed of 16 metal ceramic restorations of titanium abutment-retained crowns with gold alloy copings veneered with glass (n=8) and feldspathic ceramics (n=8). The palatal surfaces of the crowns were exposed to cyclic loading of 800 N with a frequency of 2 Hz, which continued to 4.2 million cycles or until fracture of the copings, abutments, or implants. The number of cycles and the fracture modes were recorded. The fracture modes were analyzed by descriptive analysis and the Mann-Whitney test (α=.05). The differences in loading cycles until veneering fracture were estimated with the Cox proportional hazards analysis. Veneering fracture was the most frequently observed fracture mode. The severity of fractures was significantly more in ceramic restorations than in metal ceramic restorations. Significantly more loading cycles until veneering fracture were estimated with metal ceramic restorations veneered with glass-ceramics than with other restorations. The metal ceramic restorations demonstrated fewer and less severe fractures and resisted more cyclic loads than the ceramic restorations, particularly when the metal ceramic crowns were veneered with glass-ceramics. Copyright © 2012 The Editorial Council of the Journal of Prosthetic Dentistry. Published by Mosby, Inc. All rights reserved.

Reactive Processing of Environment Conscious, Biomorphic Ceramics: A Novel and Eco-friendly Route to Advanced Ceramic

NASA Technical Reports Server (NTRS)

Singh, M.

2002-01-01

Environment-conscious, biomorphic ceramics (Ecoceramics) are a new class of materials that can be produced with renewable resources (wood) and wood wastes (wood sawdust). These materials have tailorable properties with numerous potential applications. Silicon carbide-based ecoceramics have been fabricated by the infiltration of wood-derived carbonaceous preforms with oxide and silicon based materials. The wood-derived carbonaceous preforms have been shown to be quite useful in producing porous or dense materials with different microstructures and compositions. The microstructure and mechanical properties (flexural strength, fracture toughness, elastic modulus, and compressive strength) of a wide variety of Sic-based ecoceramics have been measured. Ecoceramics have tailorable properties and behave like ceramic materials manufactured by conventional approaches. In this presentation the fabrication approach, microstructure, and thermomechanical properties of a wide variety of Sic-based Ecoceramics will be reported.

[The effect of core veneer thickness ratio on the flexural strength of diatomite-based dental ceramic].

PubMed

Jiang, Jie; Zhang, Xin; Gao, Mei-qin; Zhang, Fei-min; Lu, Xiao-li

2015-06-01

To evaluate the effect of different core veneer thickness ratios on the flexural strength and failure mode of bilayered diatomite-based dental ceramics. Diatomite-based dental ceramics blocks (16 mm×5.4 mm×1 mm) were sintered with different thickness of veneer porcelains: 0 mm (group A), 0.6 mm (group B), 0.8 mm (group C) and 1.0 mm (group D). Flexural strength was detected and scanning electron microscope was used to observe the interface microstructure. Statistical analysis was performed using SPSS 17.0 software package. With the increase of the thickness of the veneer porcelain, flexural strength of group C showed highest flexural strength up to (277.24±5.47) MPa. Different core veneer thickness ratios can significantly influence the flexural strength of bilayered diatomite-based dental ceramics. Supported by Science and Technology Projects of Nantong City (HS2013010).

Effects of Ta2O5 Addition on Electrical Properties of ZnO-V2O5 Based Varistor Ceramics

NASA Astrophysics Data System (ADS)

Fan, J. W.; Zhao, H. J.; Zhang, X. L.

2018-05-01

ZnO varistors are widely used for the protection of electronic and electrical equipment against transient surges. ZnO–V2O5 based varistor system is a potential candidate which can co-fire with Ag, and avoids the use of expensive Pa and Pt as the inner electrode in making multilayer chip varistors. However, the study of ZnO–V2O5-based ceramics is still in the initial stage for practical applications. The current work reports the effects of Ta2O5 on the electrical properties of ZnO-V2O5 based varistor ceramics. It shows that within 850-925°C experimental sintering temperature, the addition of Ta2O5 (0.05-0.20 mol%) may not improve the nonlinear coefficient but reduces the breakdown field of ZnO–V2O5 varistor ceramics.

Base-metal saturation of refractory carbide coatings produced by enhanced ceramic jets in electrothermally exploded powder spray

NASA Astrophysics Data System (ADS)

Tamura, Hideki; Itaya, Masanobu

2000-09-01

Tungsten carbide and tantalum carbide were sprayed onto substrates of mild steel by the electrothermally exploded powder spray (ELTEPS) process. High-speed x-ray radiography revealed that tungsten-carbide jets of molten particles guided inside a nozzle exhibited denser flow than unguided jets at the substrate. The velocity of the jet was approximately 800 m/s at the early stage of jetting. The ceramic coatings obtained from the guided spray consisted of carbides of a few to tens of micrometers in size, which were saturated by the base metal up to the top of the coating. The coatings exhibited diffusion of the sprayed ceramics and base metal at the interface of the deposit and substrate. The enhancement of the jet flow formed a microstructure of the ceramic coating, which was saturated by the base metal even without post heat treatment.

High temperature (NaBi)0.48□0.04Bi2Nb2O9-based piezoelectric ceramics

NASA Astrophysics Data System (ADS)

Gai, Zhi-Gang; Wang, Jin-Feng; Zhao, Ming-Lei; Wang, Chun-Ming; Zang, Guo-Zhong; Ming, Bao-Quan; Qi, Peng; Zhang, Shujun; Shrout, Thomas R.

2006-07-01

The effect of (LiCe) substitution for A site on the properties of (NaBi)0.48◻0.04Bi2Nb2O9 (NB◻N)-based ceramics was investigated. The coercive fields (EC) of NB◻N)-based ceramics were significantly decreased from 61.0to32.5kV/cm and the Curie temperature (TC) gradually decreases from 820to803°C with increasing the (LiCe) modification. The piezoelectric coefficient d33, planar coupling factor kp, and mechanical quality factor Q of (NaBi)0.38(LiCe)0.05◻0.14Bi2Nb2O9 ceramic were found to be 27pC/N, 11.2%, and 2600, respectively, together with the high TC (˜809°C) and stable piezoelectric properties, demonstrating that the (LiCe) modified NB◻N-based material a promising candidate for high temperature applications.

Robust Joining and Integration of Advanced Ceramics and Composites: Challenges, Opportunities, and Realities

NASA Technical Reports Server (NTRS)

Singh, Mrityunjay

2006-01-01

Advanced ceramics and fiber reinforced composites are under active consideration for use in a wide variety of high temperature applications within the aeronautics, space transportation, energy, and nuclear industries. The engineering designs of ceramic and composite components require fabrication and manufacturing of large and complex shaped parts of various thicknesses. In many instances, it is more economical to build up complex shapes by joining simple geometrical shapes. In addition, these components have to be joined or assembled with metallic sub-components. Thus, joining and attachment have been recognized as enabling technologies for successful utilization of ceramic components in various demanding applications. In this presentation, various challenges and opportunities in design, fabrication, and testing of high temperature joints in advanced ceramics and ceramic matrix composites will be presented. Silicon carbide based advanced ceramics and fiber reinforced composites in different shapes and sizes, have been joined using an affordable, robust ceramic joining technology. In addition, some examples of metal-ceramic brazing will also be presented. Microstructure and high temperature mechanical properties of joints in silicon carbide ceramics and composites will be reported. Various joint design philosophies and design issues in joining of ceramics and composites will be discussed.

Production of porous Calcium Phosphate (CaP) ceramics with aligned pores using ceramic/camphene-based co-extrusion.

PubMed

Choi, Won-Young; Kim, Hyoun-Ee; Moon, Young-Wook; Shin, Kwan-Ha; Koh, Young-Hag

2015-01-01

Calcium phosphate (CaP) ceramics are one of the most valuable biomaterials for uses as the bone scaffold owing to their outstanding biocompatability, bioactivity, and biodegradation nature. In particular, these materials with an open porous structure can stimulate bone ingrowth into their 3-dimensionally interconnected pores. However, the creation of pores in bulk materials would inevitably cause a severe reduction in mechanical properties. Thus, it is a challenge to explore new ways of improving the mechanical properties of porous CaP scaffolds without scarifying their high porosity. Porous CaP ceramic scaffolds with aligned pores were successfully produced using ceramic/camphene-based co-extrusion. This aligned porous structure allowed for the achievement of high compressive strength when tested parallel to the direction of aligned pores. In addition, the overall porosity and mechanical properties of the aligned porous CaP ceramic scaffolds could be tailored simply by adjusting the initial CaP content in the CaP/camphene slurry. The porous CaP scaffolds showed excellent in vitro biocompatibility, suggesting their potential as the bone scaffold. Aligned porous CaP ceramic scaffolds with considerably enhanced mechanical properties and tailorable porosity would find very useful applications as the bone scaffold.

Integrated thick-film nanostructures based on spinel ceramics

PubMed Central

2014-01-01

Integrated temperature-humidity-sensitive thick-film structures based on spinel-type semiconducting ceramics of different chemical compositions and magnesium aluminate ceramics were prepared and studied. It is shown that temperature-sensitive thick-film structures possess good electrophysical characteristics in the region from 298 to 358 K. The change of electrical resistance in integrated thick-film structures is 1 order, but these elements are stable in time and can be successfully used for sensor applications. PMID:24670141

Ceramic Technology Project semiannual progress report, October 1992--March 1993

DOE Office of Scientific and Technical Information (OSTI.GOV)

Johnson, D.R.

1993-09-01

This project was developed to meet the ceramic technology requirements of the OTS`s automotive technology programs. Although progress has been made in developing reliable structural ceramics, further work is needed to reduce cost. The work described in this report is organized according to the following work breakdown structure project elements: Materials and processing (monolithics [Si nitride, carbide], ceramic composites, thermal and wear coatings, joining, cost effective ceramic machining), materials design methodology (contact interfaces, new concepts), data base and life prediction (structural qualification, time-dependent behavior, environmental effects, fracture mechanics, nondestructive evaluation development), and technology transfer.

Refractory Oxidative-Resistant Ceramic Carbon Insulation

NASA Technical Reports Server (NTRS)

Leiser, Daniel B. (Inventor); Hsu, Ming-Ta S. (Inventor); Chen, Timothy S. (Inventor)

2001-01-01

High-temperature, lightweight, ceramic carbon insulation is prepared by coating or impregnating a porous carbon substrate with a siloxane gel derived from the reaction of an organodialkoxy silane and an organotrialkoxy silane in an acid or base medium in the presence of the carbon substrate. The siloxane gel is subsequently dried on the carbon substrate to form a ceramic carbon precursor. The carbon precursor is pyrolyzed, in an inert atmosphere, to form the ceramic insulation containing carbon, silicon, and oxygen. The carbon insulation is characterized as a porous, fibrous, carbon ceramic tile which is particularly useful as lightweight tiles for spacecraft.

Masking ability of bi- and tri- laminate all-ceramic veneers on tooth-colored ceramic discs.

PubMed

Farhan, Daniel; Sukumar, Smitha; von Stein-Lausnitz, Axel; Aarabi, Ghazal; Alawneh, Ahmad; Reissmann, Daniel R

2014-01-01

A predictable esthetic outcome is imperative when placing ceramic veneers. Discolored teeth pose a major challenge as sufficient material thickness is required to achieve a good esthetic result. There is limited evidence in the literature that compares the masking ability of multi-laminate veneers. The aim of this in-vitro study was to compare the masking ability of bi-laminate (BL) and tri-laminate (TL) all-ceramic veneers cemented on tooth-colored ceramic discs. A total of 40 veneers (shade A1, 10-mm diameter, 0.8-mm thick) were manufactured-20 BL veneers (0.4-mm pressable ceramic coping veneered with 0.4-mm thick enamel layer) and 20 TL veneers (0.4-mm coping veneered with 0.2-mm thick opaque interlayer and 0.2-mm thick enamel layer). A bonding apparatus was utilized to adhesively cement all veneers on the ceramic discs (shade A1), simulating teeth of light and dark color. The resulting groups (N = 10 each) were the reference groups (shade A1 ceramic base) BL-1 and TL-1 veneers, and the test groups (shade A4 ceramic base) BL-4 and TL-4 veneers. The color of the cemented veneers was measured using a spectrophotometer. The data were converted to CIE L*a*b* coordinates, and ΔE* were calculated to allow for statistical analysis. The color differences between the samples with the A1 and A4 ceramic bases were significantly lower when covered with TL veneers (mean ΔE*: 3.2 units) than with BL veneers (mean ΔE*: 4.0 units: p < 0.001), indicating a better masking ability of the TL veneers. The 0.8-mm thick TL veneer was able to mask darker tooth-colored ceramic disc within clinically acceptable limits. Increased understanding of the masking ability of ceramics and of color science is necessary in these esthetically aware times. Providing tri-laminate veneers for darker colored teeth seems to result in more predictable esthetical results than when using bi-laminate veneers. Patients with discolored/darker teeth may benefit from a more predictable esthetic result when teeth restored with tri-laminate rather than bi-laminate veneers. © 2014 Wiley Periodicals, Inc.

Enhanced electrocaloric effect in La-based PZT antiferroelectric ceramics

NASA Astrophysics Data System (ADS)

Mendez-González, Y.; Peláiz-Barranco, A.; Yang, Tongqing; Guerra, J. D. S.

2018-03-01

The electrocaloric effect (ECE) has been investigated in (Pb0.98La0.02)(Zr0.95Ti0.05)0.995O3 antiferroelectric ceramics obtained via the solid-state reaction method. The results from indirect measurements across the temperature range considered reveal a large electrocaloric temperature change (ΔT) of approximately 5 K at 373 K. The enhanced ECE, which is significantly higher than those reported for some lead-free and lead-based electro-ceramics, was obtained by applying an electric field of 60 kV/cm lower than what has been reported for commonly studied ceramic systems. This result suggests that this system is a potential candidate for practical electrocaloric device applications.

Design, Fabrication and Characterization of High Temperature Joints in Ceramic Composites

NASA Technical Reports Server (NTRS)

Singh, M.

1999-01-01

Ceramic joining has been recognized as one of the enabling technologies for the successful utilization of ceramic components in a number of demanding, high temperature applications. Various joint design philosophies and design issues have been discussed along with an affordable, robust ceramic joining technology (ARCJoinT). A wide variety of silicon carbide-based composite materials, in different shapes and sizes, have been joined using this technology. This technique is capable of producing joints with tailorable thickness and composition. The room and high temperature mechanical properties and fractography of ceramic joints have been reported. These joints maintain their mechanical strength up to 1200 C in air. This technology is suitable for the joining of large and complex shaped ceramic composite components and with certain modifications, can be applied to repair of ceramic components damaged in service.

Design, Fabrication, and Characterization of High Temperature Joints in Ceramic Composites

NASA Technical Reports Server (NTRS)

Singh, M.

1999-01-01

Ceramic joining has been recognized as one of the enabling technologies for the successful utilization of ceramic components in a number of demanding, high temperature applications. Various joint design philosophies and design issues have been discussed along with an affordable, robust ceramic joining technology (ARCJoinT). A wide variety of silicon carbide-based composite materials, in different shapes and sizes, have been joined using this technology. This technique is capable of producing joints with tailorable thickness and composition. The room and high temperature mechanical properties and fractography of ceramic joints have been reported. These joints maintain their mechanical strength up to 1200C in air. This technology is suitable for the joining of large and complex shaped ceramic composite components and with certain modifications, can be applied to repair of ceramic components damaged in service.

A historical perspective of synthetic ceramic and traditional feldspathic porcelain.

PubMed

Chu, Stephen; Ahmad, Irfan

2005-10-01

Ceramics were invented by the Chinese during the T'ang Dynasty, where they quickly became a precious commodity. By the early 18th Century, ceramics found its way into dentistry due to its high strength, biocompatibility, and malleability. Today, ceramic materials are a staple in dentistry, available in both naturally based and partially synthetic formulas. Most recently they have become available as quartz-glass synthetic materials manufactured under controlled conditions to eliminate the inconsistencies and impurities inherent in the naturally based counterpart. This article details the discovery of porcelain and its role as a precious substance throughout the world and time, from its initial use as ornamental earthenware to its practical application in modern dentistry. Upon reading this article, the reader should: Understand the historical significance of porcelain. Recognize the fundamental constituents and physical properties of both natural feldspathic porcelains and fully synthetic ceramics used in dentistry.

Hydroxyapatite-based porous aggregates: physico-chemical nature, structure, texture and architecture.

PubMed

Fabbri, M; Celotti, G C; Ravaglioli, A

1995-02-01

At the request of medical teams from the maxillofacial sector, a highly porous ceramic support based on hydroxyapatite of around 70-80% porosity was produced with a pore size distribution similar to bone texture (< 10 microns, approximately 3 vol%; 10-150 microns, approximately 110 vol%; > 150 microns, approximately 86 vol%). The ceramic substrates were conceived not only as a fillers for bone cavities, but also for use as drug dispensers and as supports to host cells to produce particular therapeutic agents. A method is suggested to obtain a substrate of high porosity, exploiting the impregnation of spongy substrate with hydroxyapatite ceramic particles. X-ray and scanning electron microscopy analyses were carried out to evaluate the nature of the new ceramic support in comparison with the most common commercial product; pore size distribution and porosity were controlled to known hydroxyapatite ceramic architecture for the different possible uses.

Catalytic thermal barrier coatings

DOEpatents

Kulkarni, Anand A.; Campbell, Christian X.; Subramanian, Ramesh

2009-06-02

A catalyst element (30) for high temperature applications such as a gas turbine engine. The catalyst element includes a metal substrate such as a tube (32) having a layer of ceramic thermal barrier coating material (34) disposed on the substrate for thermally insulating the metal substrate from a high temperature fuel/air mixture. The ceramic thermal barrier coating material is formed of a crystal structure populated with base elements but with selected sites of the crystal structure being populated by substitute ions selected to allow the ceramic thermal barrier coating material to catalytically react the fuel-air mixture at a higher rate than would the base compound without the ionic substitutions. Precious metal crystallites may be disposed within the crystal structure to allow the ceramic thermal barrier coating material to catalytically react the fuel-air mixture at a lower light-off temperature than would the ceramic thermal barrier coating material without the precious metal crystallites.

Ceramic-Based 4D Components: Additive Manufacturing (AM) of Ceramic-Based Functionally Graded Materials (FGM) by Thermoplastic 3D Printing (T3DP).

PubMed

Scheithauer, Uwe; Weingarten, Steven; Johne, Robert; Schwarzer, Eric; Abel, Johannes; Richter, Hans-Jürgen; Moritz, Tassilo; Michaelis, Alexander

2017-11-28

In our study, we investigated the additive manufacturing (AM) of ceramic-based functionally graded materials (FGM) by the direct AM technology thermoplastic 3D printing (T3DP). Zirconia components with varying microstructures were additively manufactured by using thermoplastic suspensions with different contents of pore-forming agents (PFA), which were co-sintered defect-free. Different materials were investigated concerning their suitability as PFA for the T3DP process. Diverse zirconia-based suspensions were prepared and used for the AM of single- and multi-material test components. All of the samples were sintered defect-free, and in the end, we could realize a brick wall-like component consisting of dense (<1% porosity) and porous (approx. 5% porosity) zirconia areas to combine different properties in one component. T3DP opens the door to the AM of further ceramic-based 4D components, such as multi-color, multi-material, or especially, multi-functional components.

Ceramic-Based 4D Components: Additive Manufacturing (AM) of Ceramic-Based Functionally Graded Materials (FGM) by Thermoplastic 3D Printing (T3DP)

PubMed Central

Weingarten, Steven; Johne, Robert; Schwarzer, Eric; Richter, Hans-Jürgen; Michaelis, Alexander

2017-01-01

In our study, we investigated the additive manufacturing (AM) of ceramic-based functionally graded materials (FGM) by the direct AM technology thermoplastic 3D printing (T3DP). Zirconia components with varying microstructures were additively manufactured by using thermoplastic suspensions with different contents of pore-forming agents (PFA), which were co-sintered defect-free. Different materials were investigated concerning their suitability as PFA for the T3DP process. Diverse zirconia-based suspensions were prepared and used for the AM of single- and multi-material test components. All of the samples were sintered defect-free, and in the end, we could realize a brick wall-like component consisting of dense (<1% porosity) and porous (approx. 5% porosity) zirconia areas to combine different properties in one component. T3DP opens the door to the AM of further ceramic-based 4D components, such as multi-color, multi-material, or especially, multi-functional components. PMID:29182541

Subungual Hematoma

MedlinePlus

... Name: Category: Share: Yes No, Keep Private Subungual Hematoma Share | A subungual hematoma is a transient condition where blood and fluid ... bleeding underneath the nail. Regardless of treatment the hematoma will eventually be resorbed by the body and ...

Guided bone regeneration: A novel approach in the treatment of pediatric dentoalveolar trauma

PubMed Central

Murthy, Prashanth Sadashiva; Shivamallu, Avinash Bettahalli; Deshmukh, Seema; Nandlal, Bhojraj; Thotappa, Srilatha K.

2015-01-01

Traumatic injuries in the primary dentition pose major challenges for management. This emergency treatment requires proper planning so as to achieve favorable results. Trauma causing severe dentoalveolar injuries, especially in children, needs an interdisciplinary approach so as to retain normal functional anatomy for that age. This article describes a clinical innovative technique, which utilizes a resorbable membrane in management of pediatric dentoalveolar trauma. The membrane was shaped to cover the multiple alveolar bone fracture, thereby favoring the healing of the bone defects. The use of this resorbable membrane maintained a secluded space for the bone growth and prevented overgrowth of the soft tissue in the region of the defect. This resulted in uneventful healing leading to well-maintained functional bone contour, which further favored the esthetic rehabilitation as well as protected the underlying permanent tooth buds. PMID:26005471

Repair of giant postlaminectomy pseudomeningocele with fast-resorbing polymer mesh: technical report of 2 cases.

PubMed

Alvarez, Carlos M; Urakov, Timur M; Vanni, Steven

2018-03-01

Pseudomeningocele is a rare but well-known complication of lumbar spine surgery, which arises in 0.068%-0.1% of individuals in large series of patients undergoing laminectomy and in up to 2% of patients with postlaminectomy symptoms. In symptomatic pseudomeningoceles, surgical reexploration and repair of the dural defect are typically necessary. Whereas the goals of pseudomeningocele repair, which are extirpation of the pseudomeningocele cavity and elimination of extradural dead space, can typically be achieved by primary closure performed using nonabsorbable sutures, giant pseudomeningoceles (> 8 cm) can require more elaborate repair in which fibrin glues, dural substitute, myofascial flaps, or all of the above are used. The authors present 2 cases of postsurgical symptomatic giant pseudomeningoceles that were repaired using a fast-resorbing polymer mesh-supported reconstruction technique, which is described here for the first time.

Recent advances in fixation of the craniomaxillofacial skeleton.

PubMed

Meslemani, Danny; Kellman, Robert M

2012-08-01

Fixation of the craniomaxillofacial skeleton is an evolving aspect for facial plastic, oral and maxillofacial, and plastic surgery. This review looks at the recent advances that aid in reduction and fixation of the craniomaxillofacial skeleton. More surgeons are using resorbable plates for craniomaxillofacial fixation. A single miniplate on the inferior border of the mandible may be sufficient to reduce and fixate an angle fracture. Percutaneous K-wires may assist in plating angle fractures. Intraoperative computed tomography (CT) may prove to be useful for assessing reduction and fixation. Resorbable plates are becoming increasingly popular in orthognathic surgery and facial trauma surgery. There are newer operative techniques for fixating the angle of the mandible. Also, the utilization of the intraoperative CT provides immediate feedback for accurate reduction and fixation. Prebent surgical plates save operative time, decrease errors, and provide more accurate fixation.

A Retrospective Tomographic and Histologic Analysis of Horizontal Bone Augmentation in Maxillary Atrophic Ridges Using Resorbable Membrane with Anorganic Bovine Bone-Derived Mineral and Plasma Rich in Growth Factors.

PubMed

Lorenzetti, Massimo; Vono, Maurizio; Lorenzetti, Virginia

2018-02-16

A total of six patients treated from 2010 to 2014, having a knife-edge ridge (Cawood-Howell Class IV resorbed ridges) and requiring an implant-prosthetic rehabilitation, were selected. Tomographic measurement of the edentulous ridges was performed before grafting and after implant placement. At 6 months postgraft, a total of 41 implants had been inserted, 17 in the posterior region, 12 in the central region, and 12 in the anterior region. No surgical or healing complications were recorded, and the prostheses were loaded 6 to 9 months after implant placement. The tomographic measurements demonstrated an increased area in all the sites where bone augmentation had been performed, corresponding to 11.1% in the anterior region, 94.7% in the central region, and 760.2% in the posterior region. Histology was performed in 2 patients, one at 1 year and the other at 5 years postgrafting, and demonstrated the presence of mature lamellar bone tissue and newly formed bone without morphologic signs of necrosis or inflammation and a reduction of 50% to 30% of the grafted material. Although this study included a small number of clinical cases, it demonstrated how management of the atrophic maxillary ridge, with the goal of implant placement, may be handled using a technique that requires a single anorganic bovine bone-derived mineral treatment combined with a plasma rich in growth factors and resorbable collagen membrane.

Adenylate cyclase-stimulating, bone-resorbing and B TGF-like activities in canine apocrine cell adenocarcinoma of the anal sac.

PubMed

Weir, E C; Centrella, M; Matus, R E; Brooks, M L; Wu, T; Insogna, K L

1988-12-01

Canine apocrine cell adenocarcinoma of the anal sac (APO-AS) is a spontaneously occurring tumor that causes humorally mediated hypercalcemia in 90% of cases. To further define the nature of the responsible mediator in APO-AS, we examined tumor extracts from five APO-AS and four control tumors for adenylate cyclase-stimulating activity (ACSA). All extracts from APO-AS contained potent ACSA, whereas the four control tumors did not. The ACSA extracted from one tumor demonstrated a dose response curve parallel to that of synthetic bovinePTH-(1-34) and was 80% inhibited by Nle8,18,Tyr34 bPTH-(3-34)amide at a concentration of 10(-5) M. Extracts from three APO-AS and three control tumors were also examined for in vitro bone-resorbing activity (BRA). All APO-AS contained significant BRA, stimulating resorption 1.47 to 2.13-fold over basal, whereas none of the control tumors stimulated resorption. Purification of one extract using C18 reverse-phase high pressure liquid chromatography (RP-HPLC) resulted in a single sharp peak of ACSA which was 400-fold purified compared with the initial extract. This pool also contained significant bone-resorbing activity, whereas none of the adjacent pools did. Purification of a second extract using sequential CN and C18 RP-HPLC followed by size exclusion HPLC resulted in material that was at least 10,000-fold purified, and showed co-purification of ACSA and B TGF-like activity.

Osteoclasts prefer aged bone.

PubMed

Henriksen, K; Leeming, D J; Byrjalsen, I; Nielsen, R H; Sorensen, M G; Dziegiel, M H; Martin, T John; Christiansen, C; Qvist, P; Karsdal, M A

2007-06-01

We investigated whether the age of the bones endogenously exerts control over the bone resorption ability of the osteoclasts, and found that osteoclasts preferentially develop and resorb bone on aged bone. These findings indicate that the bone matrix itself plays a role in targeted remodeling of aged bones. Osteoclasts resorb aging bone in order to repair damage and maintain the quality of bone. The mechanism behind the targeting of aged bone for remodeling is not clear. We investigated whether bones endogenously possess the ability to control osteoclastic resorption. To biochemically distinguish aged and young bones; we measured the ratio between the age-isomerized betaCTX fragment and the non-isomerized alphaCTX fragment. By measurement of TRACP activity, CTX release, number of TRACP positive cells and pit area/pit number, we evaluated osteoclastogenesis as well as osteoclast resorption on aged and young bones. We found that the alphaCTX/betaCTX ratio is 3:1 in young compared to aged bones, and we found that both alpha and betaCTX are released by osteoclasts during resorption. Osteoclastogenesis was augmented on aged compared to young bones, and the difference was enhanced under low serum conditions. We found that mature osteoclasts resorb more on aged than on young bone, despite unchanged adhesion and morphology. These data indicate that the age of the bone plays an important role in controlling osteoclast-mediated resorption, with significantly higher levels of osteoclast differentiation and resorption on aged bones when compared to young bones.

A novel one-pot process for near-net-shape fabrication of open-porous resorbable hydroxyapatite/protein composites and in vivo assessment.

PubMed

Mueller, Berit; Koch, Dietmar; Lutz, Rainer; Schlegel, Karl A; Treccani, Laura; Rezwan, Kurosch

2014-09-01

We present a mild one-pot freeze gelation process for fabricating near-net, complex-shaped hydroxyapatite scaffolds and to directly incorporate active proteins during scaffold processing. In particular, the direct protein incorporation enables a simultaneous adjustment and control of scaffold microstructure, porosity, resorbability and enhancement of initial mechanical and handling stability. Two proteins, serum albumin and lysozyme, are selected and their effect on scaffold stability and microstructure investigated by biaxial strength tests, electron microscopy, and mercury intrusion porosimetry. The resulting hydroxyapatite/protein composites feature adjustable porosities from 50% to 70% and a mechanical strength ranging from 2 to 6 MPa comparable to that of human spongiosa without any sintering step. Scaffold degradation behaviour and protein release are assessed by in vitro studies. A preliminary in vivo assessment of scaffold biocompatibility and resorption behaviour in adult domestic pigs is discussed. After implantation, composites were resorbed up to 50% after only 4 weeks and up to 65% after 8 weeks. In addition, 14% new bone formation after 4 weeks and 37% after 8 weeks were detected. All these investigations demonstrate the outstanding suitability of the one-pot-process to create, in a customisable and reliable way, biocompatible scaffolds with sufficient mechanical strength for handling and surgical insertion, and for potential use as biodegradable bone substitutes and versatile platform for local drug delivery. Copyright © 2014 Elsevier B.V. All rights reserved.

Tribology of selected ceramics at temperatures to 900 C

NASA Technical Reports Server (NTRS)

Sliney, H. E.; Jacobson, T. P.; Deadmore, D.; Miyoshi, K.

1986-01-01

Results of fundamental and focused research on the tribological properties of ceramics are discussed. The basic friction and wear characteristics are given for ceramics of interest for use in gas turbine, adiabatic diesel, and Stirling engine applications. The importance of metal oxides in ceramic/metal sliding combinations is illustrated. The formulation and tribological additives are described. Friction and wear data are given for carbide and oxide-based composite coatings for temperatures to at least 900 C.

Effect of phase inversion on microporous structure development of Al 2O 3/poly(vinylidene fluoride-hexafluoropropylene)-based ceramic composite separators for lithium-ion batteries

NASA Astrophysics Data System (ADS)

Jeong, Hyun-Seok; Kim, Dong-Won; Jeong, Yeon Uk; Lee, Sang-Young

To improve the thermal shrinkage of the separators that are essential to securing the electrical isolation between electrodes in lithium-ion batteries, we develop a new separator based on a ceramic composite membrane. Introduction of microporous, ceramic coating layers onto both sides of a polyethylene (PE) separator allows such a progress. The ceramic coating layers consist of nano-sized alumina (Al 2O 3) powders and polymeric binders (PVdF-HFP). The microporous structure of the ceramic coating layers is observed to be crucial to governing the thermal shrinkage as well as the ionic transport of the ceramic composite separators. This microporous structure is determined by controlling the phase inversion, more specifically, nonsolvent (water) contents in the coating solutions. To provide a theoretical basis for this approach, a pre-investigation on the phase diagram for a ternary mixture comprising PVdF-HFP, acetone, and water is conducted. On the basis of this observation, the effect of phase inversion on the morphology and air permeability (i.e. Gurley value) of ceramic coating layers is systematically discussed. In addition, to explore the application of ceramic composite separators to lithium-ion batteries, the influence of the structural change in the coating layers on the thermal shrinkage and electrochemical performance of the separators is quantitatively identified.

High-Temperature Wettability and Interactions between Y-Containing Ni-Based Alloys and Various Oxide Ceramics.

PubMed

Li, Jinpeng; Zhang, Huarui; Gao, Ming; Li, Qingling; Bian, Weidong; Tao, Tongxiang; Zhang, Hu

2018-05-07

To obtain appropriate crucible materials for vacuum induction melting of MCrAlY alloys, four different oxide ceramics, including MgO, Y₂O₃, Al₂O₃, and ZrO₂, with various microstructures were designed and characterized. The high-temperature wettability and interactions between Ni-20Co-20Cr-10Al-1.5Y alloys and oxide ceramics were studied by sessile drop experiments under vacuum. The results showed that all the systems exhibited non-wetting behavior. The contact angles were stable during the melting process of alloys and the equilibrium contact angles were 140° (MgO), 148° (Y₂O₃), 154° (Al₂O₃), and 157° (ZrO₂), respectively. The interfacial reaction between the ceramic substrates and alloys occurred at high temperature. Though the ceramics had different microstructures, similar continuous Y₂O₃ reaction layer with thicknesses of about 25 μm at the alloy-ceramic interface in MgO, Al₂O₃, and ZrO₂ systems formed. The average area percentage of oxides in the alloy matrices were 0.59% (MgO), 0.11% (Al₂O₃), 0.09% (ZrO₂), and 0.02% (Y₂O₃), respectively. The alloys, after reacting with MgO ceramic, had the highest inclusion content, while those with the lowest content were in the Y₂O₃ system. Y₂O₃ ceramic was the most beneficial for vacuum induction melting of high-purity Y-containing Ni-based alloys.

Sliding durability of two carbide-oxide candidate high temperature fiber seal materials in air to 900 C

NASA Technical Reports Server (NTRS)

Dellacorte, Christopher; Steinetz, Bruce M.

1992-01-01

A test program to determine the friction and wear properties of two complex carbide oxide ceramic fibers for high temperature sliding seal applications is described. The fibers are based on Si, C, O, and Ti or Si, C, N, and O ceramic systems. Pin on disk tests using ceramic fiber covered pins and Inconel 718 disks, were conducted in air from 25 to 900 C to evaluate potential seal materials. This testing procedure was used in a previous study of oxide ceramic fibers which were found to exhibit wear behavior based predominantly on their mechanical properties. Like the oxide fibers tested previously, these carbide oxide ceramic fibers, show an increase in friction and wear with increased test temperature. At room temperature, the wear behavior seems to be based upon mechanical properties, namely tensile strength. At 500 and especially 900 C, the fibers wear by both mechanical fracture and by oxidative type wear. Based upon post test microscopic and x ray analyses, interaction between the fiber constituents and elements transferred from the counterface, namely Ni and Cr, may have occurred enhancing the tribochemical wear process. These results are interpreted.

Determination of the phase transition in Pb{sub 0.88}Ln{sub 0.08}Ti{sub 0.98}Mn{sub 0.02}O{sub 3} (Ln=La, Sm, Eu) piezoceramics based on the Stefan-Boltzmann law

DOE Office of Scientific and Technical Information (OSTI.GOV)

Suaste, Ernesto; Castillo, Victor; Gonzalez, Ruben

2004-07-15

A method for determination of the phase transition in piezoelectric ceramic based on the relationship expressed by the Stefan-Boltzmann law is reported, i.e., by means of the radiation that the piezoelectric ceramic emits when it is subjected to different temperatures. The experiment is performed in piezoelectric ceramic based on PbTiO{sub 3} modified by the partial substitution of rare earths for Pb in the Pb{sub 0.88}(Ln){sub 0.08}Ti{sub 0.98}Mn{sub 0.02}O{sub 3} system (Ln=La, Sm, Eu). From the measured emitted radiation, the value of the emissivity is calculated for each type of piezoelectric ceramic.

Progress report

NASA Technical Reports Server (NTRS)

Abhiraman, A.; Collard, D.; Cardelino, B.; Bhatia, S.; Desai, P.; Harruna, I.; Khan, I.; Mariam, Y.; Mensah, T.; Mitchell, M.

1992-01-01

The NASA funding allowed Clark Atlanta University (CAU) to establish a High Performance Polymers And Ceramics (HiPPAC) Research Center. The HiPPAC Center is consolidating and expanding the existing polymer and ceramic research capabilities at CAU through the development of interdepartmental and interinstitutional research in: (1) polymer synthesis; (2) polymer characterization and properties; (3) polymer processing; (4) polymer-based ceramic synthesis; and (5) ceramic characterization and properties. This Center has developed strong interactions between scientists and materials scientists of CAU and their counterparts from sister institutions in the Atlanta University Center (AUC) and the Georgia Institute of Technology. As a component of the center, we have started to develop strong collaborations with scientists from other universities and the HBCU's, national and federal agency laboratories, and the private sector during this first year. During this first year we have refined the focus of the research in the HiPPAC Center to three areas with seven working groups that will start programmatic activities on January 1, 1993, as follows: (1) nonlinear optical properties of chitosan derivatives; (2) polymeric electronic materials; (3) nondestructive characterization and prediction of polyimide performance; (4) solution processing of high-performance materials; (5) processable polyimides for composite applications; (6) sol-gel based ceramic materials processing; and (7) synthetic based processing of pre-ceramic polymers.

Assessing near infrared optical properties of ceramic orthodontic brackets using cross-polarization optical coherence tomography.

PubMed

Isfeld, Darren M; Aparicio, Conrado; Jones, Robert S

2014-04-01

Secondary decay (caries) under ceramic orthodontic brackets remains a significant dental problem and near infrared cross-polarization optical coherence tomography (CP-OCT) has the potential to detect underlying demineralization. The purpose of this study was to determine the effect of crystalline structure and chemical composition of ceramic brackets on CP-OCT imaging. Four ceramic brackets types, which were divided into monocrystalline and polycrystalline, were examined using CP-OCT. The results of this study demonstrated that the crystallinity of the ceramic brackets affected the 1310 nm CP-OCT imaging with the greatest attenuation seen in polycrystalline alumina brackets. The alumina polycrystalline bracket materials had significantly higher attenuation and scattering than alumina monocrystalline brackets (p < 0.05, ANOVA, Bonferroni). Additionally, bracket base morphology and composition affected NIR light attenuation. There was considerable attenuation in bracket bases that contained additive zirconium spheres (∼30 µm) and this alteration was significantly greater than the jagged alumina crystallographic alterations found in the other bracket systems (p < 0.05, ANOVA, Bonferroni). Noninvasive, near infrared (NIR) cross-polarization optical coherence tomography (CP-OCT) has potential to effectively image through portions of ceramic brackets; however, further investigation into the optical effects of resin integration in the base portion of the brackets is warranted. © 2013 Wiley Periodicals, Inc.

CaO-Al2O3 glass-ceramic as a joining material for SiC based components: A microstructural study of the effect of Si-ion irradiation

NASA Astrophysics Data System (ADS)

Casalegno, Valentina; Kondo, Sosuke; Hinoki, Tatsuya; Salvo, Milena; Czyrska-Filemonowicz, Aleksandra; Moskalewicz, Tomasz; Katoh, Yutai; Ferraris, Monica

2018-04-01

The aim of this work was to investigate and discuss the microstructure and interface reaction of a calcia-alumina based glass-ceramic (CA) with SiC. CA has been used for several years as a glass-ceramic for pressure-less joining of SiC based components. In the present work, the crystalline phases in the CA glass-ceramic and at the CA/SiC interface were investigated and the absence of any detectable amorphous phase was assessed. In order to provide a better understanding of the effect of irradiation on the joining material and on the joints, Si ion irradiation was performed both on bulk CA and CA joined SiC. CA glass-ceramic and CA joined SiC were both irradiated with 5.1 MeV Si2+ ions to 3.3 × 1020 ions/m2 at temperatures of 400 and 800 °C at DuET facility, Kyoto University. This corresponds to a damage level of 5 dpa for SiC averaged over the damage range. This paper presents the results of a microstructural analysis of the irradiated samples as well as an evaluation of the dimensional stability of the CA glass-ceramic and its irradiation temperature and/or damage dependence.

Fractographic features of glass-ceramic and zirconia-based dental restorations fractured during clinical function.

PubMed

Oilo, Marit; Hardang, Anne D; Ulsund, Amanda H; Gjerdet, Nils R

2014-06-01

Fractures during clinical function have been reported as the major concern associated with all-ceramic dental restorations. The aim of this study was to analyze the fracture features of glass-ceramic and zirconia-based restorations fractured during clinical use. Twenty-seven crowns and onlays were supplied by dentists and dental technicians with information about type of cement and time in function, if available. Fourteen lithium disilicate glass-ceramic restorations and 13 zirconia-based restorations were retrieved and analyzed. Fractographic features were examined using optical microscopy to determine crack initiation and crack propagation of the restorations. The material comprised fractured restorations from one canine, 10 incisors, four premolars, and 11 molars. One crown was not categorized because of difficulty in orientation of the fragments. The results revealed that all core and veneer fractures initiated in the cervical margin and usually from the approximal area close to the most coronally placed curvature of the margin. Three cases of occlusal chipping were found. The margin of dental all-ceramic single-tooth restorations was the area of fracture origin. The fracture features were similar for zirconia, glass-ceramic, and alumina single-tooth restorations. Design features seem to be of great importance for fracture initiation. © 2014 Eur J Oral Sci.

Detoxification and immobilization of chromite ore processing residue in spinel-based glass-ceramic.

PubMed

Liao, Chang-Zhong; Tang, Yuanyuan; Lee, Po-Heng; Liu, Chengshuai; Shih, Kaimin; Li, Fangbai

2017-01-05

A promising strategy for the detoxification and immobilization of chromite ore processing residue (COPR) in a spinel-based glass-ceramic matrix is reported in this study. In the search for a more chemically durable matrix for COPR, the most critical crystalline phase for Cr immobilization was found to be a spinel solid solution with a chemical composition of MgCr 1.32 Fe 0.19 Al 0.49 O 4 . Using Rietveld quantitative X-ray diffraction analysis, we identified this final product is with the phases of spinel (3.5wt.%), diopside (5.2wt.%), and some amorphous contents (91.2wt.%). The partitioning ratio of Cr reveals that about 77% of the Cr was incorporated into the more chemically durable spinel phase. The results of Cr K-edge X-ray absorption near-edge spectroscopy show that no Cr(VI) was observed after conversion of COPR into a glass-ceramic, which indicates successful detoxification of Cr(VI) into Cr(III) in the COPR-incorporated glass-ceramic. The leaching performances of Cr 2 O 3 and COPR-incorporated glass-ceramic were compared with a prolonged acid-leaching test, and the results demonstrate the superiority of the COPR-incorporated glass-ceramic matrix in the immobilization of Cr. The overall results suggest that the use of affordable additives has potential in more reliably immobilizing COPR with a spinel-based glass-ceramic for safer disposal of this hazardous waste. Copyright © 2016 Elsevier B.V. All rights reserved.

Pumpable/injectable phosphate-bonded ceramics

DOEpatents

Singh, Dileep; Wagh, Arun S.; Perry, Lamar; Jeong, Seung-Young

2001-01-01

A pumpable ceramic composition is provided comprising an inorganic oxide, potassium phosphate, and an oxide coating material. Also provided is a method for preparing pumpable ceramic-based waste forms comprising selecting inorganic oxides based on solubility, surface area and morphology criteria; mixing the selected oxides with phosphate solution and waste to form a first mixture; combining an additive to the first mixture to create a second mixture; adding water to the second mixture to create a reactive mixture; homogenizing the reactive mixture; and allowing the reactive mixture to cure.

Final Project Report CFA-14-6357: A New Paradigm for Understanding Multiphase Ceramic Waste Form Performance

DOE Office of Scientific and Technical Information (OSTI.GOV)

Brinkman, Kyle; Bordia, Rajendra; Reifsnider, Kenneth

This project fabricated model multiphase ceramic waste forms with processing-controlled microstructures followed by advanced characterization with synchrotron and electron microscopy-based 3D tomography to provide elemental and chemical state-specific information resulting in compositional phase maps of ceramic composites. Details of 3D microstructural features were incorporated into computer-based simulations using durability data for individual constituent phases as inputs in order to predict the performance of multiphase waste forms with varying microstructure and phase connectivity.

Plasma sprayed ceramic thermal barrier coating for NiAl-based intermetallic alloys

NASA Technical Reports Server (NTRS)

Miller, Robert A. (Inventor); Doychak, Joseph (Inventor)

1994-01-01

A thermal barrier coating system consists of two layers of a zirconia-yttria ceramic. The first layer is applied by low pressure plasma spraying. The second layer is applied by conventional atmospheric pressure plasma spraying. This facilitates the attachment of a durable thermally insulating ceramic coating directly to the surface of a highly oxidation resistant NiAl-based intermetallic alloy after the alloy has been preoxidized to promote the formation of a desirable Al2O3 scale.

SiC-Based Composite Materials Obtained by Siliconizing Carbon Matrices

NASA Astrophysics Data System (ADS)

Shikunov, S. L.; Kurlov, V. N.

2017-12-01

We have developed a method for fabrication of parts of complicated configuration from composite materials based on SiC ceramics, which employs the interaction of silicon melt with the carbon matrix having a certain composition and porosity. For elevating the operating temperatures of ceramic components, we have developed a method for depositing protective silicon-carbide coatings that is based on the interaction of the silicon melt and vapor with carbon obtained during thermal splitting of hydrocarbon molecules. The new structural ceramics are characterized by higher operating temperatures; chemical stability; mechanical strength; thermal shock, wear and radiation resistance; and parameters stability.

Fabrication of porous silicon nitride ceramics using binder jetting technology

NASA Astrophysics Data System (ADS)

Rabinskiy, L.; Ripetsky, A.; Sitnikov, S.; Solyaev, Y.; Kahramanov, R.

2016-07-01

This paper presents the results of the binder jetting technology application for the processing of the Si3N4-based ceramics. The difference of the developed technology from analogues used for additive manufacturing of silicon nitride ceramics is a method of the separate deposition of the mineral powder and binder without direct injection of suspensions/slurries. It is assumed that such approach allows reducing the technology complexity and simplifying the process of the feedstock preparation, including the simplification of the composite materials production. The binders based on methyl ester of acrylic acid with polyurethane and modified starch were studied. At this stage of the investigations, the technology of green body's fabrication is implemented using a standard HP cartridge mounted on the robotic arm. For the coordinated operation of the cartridge and robot the specially developed software was used. Obtained green bodies of silicon powder were used to produce the ceramic samples via reaction sintering. The results of study of ceramics samples microstructure and composition are presented. Sintered ceramics are characterized by fibrous α-Si3N4 structure and porosity up to 70%.

Aluminum alloy/alumina-based ceramic interactions

DOE Office of Scientific and Technical Information (OSTI.GOV)

Lebeau, T.; Strom-Olsen, J.O.; Gruzleski, J.E.

1995-07-01

Wetting experiments were performed on eutectic ZrO{sub 2}/Al{sub 2}O{sub 3} (ZA), ZrO{sub 2}/Al{sub 2}O{sub 3}/TiO{sub 2} (ZAT), and ZrO{sub 2}/Al{sub 2}O{sub 3}/SiO{sub 2} (ZAS) ceramic substrates with different Al alloys. Four major variables were tested to study the wetting behavior of the different ceramic-metal systems. Variable include holding time, melt temperature, ally, and ceramic compositions. An experimental setup was designed to measure in situ contact angles using the sessile drop method. For any ceramic substrate, a temperature over 950 C was necessary to observe an equilibrium wetting angle of less than 90{degree} with pure Al; by alloying the aluminum, wettingmore » could be observed at lower temperatures ({theta} = 76--86{degree} at 900 C for Al-10 wt. % Si, {theta} {approximately}72{degree} at 850 C for Al-2.4 wt. % Mg) forming clean interfaces. Finally, ZAS specimens reacted with molten Al alloys over 900 C to produce Zr-Al based intermetallics at the metal-ceramic interface.« less

[Microleakage of various cementing agents for casting ceramics].

PubMed

Weng, Wei-min; Zhang, Xiu-yin; Zhang, Fu-qiang

2009-12-01

To observe and compare the microleakage of different composite resin cement systems for IPS Empress 2 ceramics base. Sixteen healthy non-carious human molars were selected in the study. Class V ceramic inlay was prepared by IPS Empress 2 ceramics. The samples were divided into two groups, eight in each group. RelyX Unicem and Variolink 2 were used for bonding respectively in 2 groups. All specimens were stored in water at 37 degrees centigrade for 24 hours, then the specimens were subjected to 500 thermocycles ranging from 5 degrees centigrade to 55 degrees centigrade. Eight specimens in each group were evaluated by dye penetration. The microleakage was examined with light microscope. Statistical analysis was performed with SPSS11.0 software package. Enamel margins exhibited lower leakage than dentin margins by using two cementing agents for casting ceramics (P<0.05). The depth of dye for Variolink 2 and RelyX Unicem at enamel and dentin was not significantly different (P>0.05). The microleakage of Variolink 2 and RelyX Unicem for IPS Empress 2 ceramics base has similar sealing abilities.

Development of Novel Piezoelectric Biosensor Using PZT Ceramic Resonator for Detection of Cancer Markers.

PubMed

Su, Li; Fong, Chi-Chun; Cheung, Pik-Yuan; Yang, Mengsu

2017-01-01

A novel biosensor based on piezoelectric ceramic resonator was developed for direct detection of cancer markers in the study. For the first time, a commercially available PZT ceramic resonator with high resonance frequency was utilized as transducer for a piezoelectric biosensor. A dual ceramic resonators scheme was designed wherein two ceramic resonators were connected in parallel: one resonator was used as the sensing unit and the other as the control unit. This arrangement minimizes environmental influences including temperature fluctuation, while achieving the required frequency stability for biosensing applications. The detection of the cancer markers Prostate Specific Antigen (PSA) and α-Fetoprotein (AFP) was carried out through frequency change measurement. The device showed high sensitivity (0.25 ng/ml) and fast detection (within 30 min) with small samples (1 μl), which is compatible with the requirements of clinical measurements. The results also showed that the ceramic resonator-based piezoelectric biosensor platform could be utilized with different chemical interfaces, and had the potential to be further developed into biosensor arrays with different specificities for simultaneous detection of multiple analytes.

Fracture Mechanisms of Zirconium Diboride Ultra-High Temperature Ceramics under Pulse Loading

NASA Astrophysics Data System (ADS)

Skripnyak, Vladimir V.; Bragov, Anatolii M.; Skripnyak, Vladimir A.; Lomunov, Andrei K.; Skripnyak, Evgeniya G.; Vaganova, Irina K.

2015-06-01

Mechanisms of failure in ultra-high temperature ceramics (UHTC) based on zirconium diboride under pulse loading were studied experimentally by the method of SHPB and theoretically using the multiscale simulation method. The obtained experimental and numerical data are evidence of the quasi-brittle fracture character of nanostructured zirconium diboride ceramics under compression and tension at high strain rates and the room temperatures. Damage of nanostructured porous zirconium diboride -based UHTC can be formed under stress pulse amplitude below the Hugoniot elastic limit. Fracture of nanostructured ultra-high temperature ceramics under pulse and shock-wave loadings is provided by fast processes of intercrystalline brittle fracture and relatively slow processes of quasi-brittle failure via growth and coalescence of microcracks. A decrease of the shear strength can be caused by nano-voids clusters in vicinity of triple junctions between ceramic matrix grains and ultrafine-grained ceramics. This research was supported by grants from ``The Tomsk State University Academic D.I. Mendeleev Fund Program'' and also N. I. Lobachevski State University of Nizhny Novgorod (Grant of post graduate mobility).

Properties and Crystallization Phenomena in Li2Si2O5–Ca5(PO4)3F and Li2Si2O5–Sr5(PO4)3F Glass–Ceramics Via Twofold Internal Crystallization

PubMed Central

Rampf, Markus; Dittmer, Marc; Ritzberger, Christian; Schweiger, Marcel; Höland, Wolfram

2015-01-01

The combination of specific mechanical, esthetic, and chemical properties is decisive for the application of materials in prosthodontics. Controlled twofold crystallization provides a powerful tool to produce special property combinations for glass–ceramic materials. The present study outlines the potential of precipitating Ca5(PO4)3F as well as Sr5(PO4)3F as minor crystal phases in Li2Si2O5 glass–ceramics. Base glasses with different contents of CaO/SrO, P2O5, and F− were prepared within the glasses of the SiO2–Li2O–K2O–CaO/SrO–Al2O3–P2O5–F system. Preliminary studies of nucleation by means of XRD and scanning electron microscopy (SEM) of the nucleated base glasses revealed X-ray amorphous phase separation phenomena. Qualitative and quantitative crystal phase analyses after crystallization were conducted using XRD in combination with Rietveld refinement. As a main result, a direct proportional relationship between the content of apatite-forming components in the base glasses and the content of apatite in the glass–ceramics was established. The microstructures of the glass–ceramics were investigated using SEM. Microstructural and mechanical properties were found to be dominated by Li2Si2O5 crystals and quite independent of the content of the apatite present in the glass–ceramics. Biaxial strengths of up to 540 MPa were detected. Ca5(PO4)3F and Sr5(PO4)3F influence the translucency of the glass–ceramics and, hence, help to precisely tailor the properties of Li2Si2O5 glass–ceramics. The authors conclude that the twofold crystallization of Li2Si2O5–Ca5(PO4)3F or Li2Si2O5–Sr5(PO4)3F glass–ceramics involves independent solid-state reactions, which can be controlled via the chemical composition of the base glasses. The influence of the minor apatite phase on the optical properties helps to achieve new combinations of features of the glass–ceramics and, hence, displays new potential for dental applications. PMID:26389112

Properties and Crystallization Phenomena in Li2Si2O5-Ca5(PO4)3F and Li2Si2O5-Sr5(PO4)3F Glass-Ceramics Via Twofold Internal Crystallization.

PubMed

Rampf, Markus; Dittmer, Marc; Ritzberger, Christian; Schweiger, Marcel; Höland, Wolfram

2015-01-01

The combination of specific mechanical, esthetic, and chemical properties is decisive for the application of materials in prosthodontics. Controlled twofold crystallization provides a powerful tool to produce special property combinations for glass-ceramic materials. The present study outlines the potential of precipitating Ca5(PO4)3F as well as Sr5(PO4)3F as minor crystal phases in Li2Si2O5 glass-ceramics. Base glasses with different contents of CaO/SrO, P2O5, and F(-) were prepared within the glasses of the SiO2-Li2O-K2O-CaO/SrO-Al2O3-P2O5-F system. Preliminary studies of nucleation by means of XRD and scanning electron microscopy (SEM) of the nucleated base glasses revealed X-ray amorphous phase separation phenomena. Qualitative and quantitative crystal phase analyses after crystallization were conducted using XRD in combination with Rietveld refinement. As a main result, a direct proportional relationship between the content of apatite-forming components in the base glasses and the content of apatite in the glass-ceramics was established. The microstructures of the glass-ceramics were investigated using SEM. Microstructural and mechanical properties were found to be dominated by Li2Si2O5 crystals and quite independent of the content of the apatite present in the glass-ceramics. Biaxial strengths of up to 540 MPa were detected. Ca5(PO4)3F and Sr5(PO4)3F influence the translucency of the glass-ceramics and, hence, help to precisely tailor the properties of Li2Si2O5 glass-ceramics. The authors conclude that the twofold crystallization of Li2Si2O5-Ca5(PO4)3F or Li2Si2O5-Sr5(PO4)3F glass-ceramics involves independent solid-state reactions, which can be controlled via the chemical composition of the base glasses. The influence of the minor apatite phase on the optical properties helps to achieve new combinations of features of the glass-ceramics and, hence, displays new potential for dental applications.

Light-weight black ceramic insulation

NASA Technical Reports Server (NTRS)

Hsu, Ming-Ta S. (Inventor); Chen, Timothy S. (Inventor)

2003-01-01

Ultra-high temperature, light-weight, black ceramic insulation having a density ranging from about 0.12 g/cc. to 0.6 g/cc. such as ceramic tile is obtained by pyrolyzing siloxane gels derived from the reaction of at least one organo dialkoxy silane and at least one tetralkoxy silane in an acid or base liquid medium. The reaction mixture of the tetra- and dialkoxy silanes also may contain an effective amount of a mono- or trialkoxy silane to obtain the siloxane gels. The siloxane gels are dried at ambient temperatures and pressures to form siloxane ceramic precursors without significant shrinkage. The siloxane ceramic precursors are subsequently pyrolyzed, in an inert atmosphere, to form the black ceramic insulation comprising atoms of silicon, carbon and oxygen. The ceramic insulation can be characterized as a porous, uniform ceramic tile resistant to oxidation at temperatures ranging as high as 1700.degree. C., and particularly useful as lightweight tiles for spacecraft and other high-temperature insulation applications.

Osteoclastogenesis and Osteoclastic Resorption of Tricalcium Phosphate: Effect of Strontium and Magnesium Doping

PubMed Central

Roy, Mangal; Bose, Susmita

2012-01-01

Bone substitute materials are required to support the remodeling process, which consists of osteoclastic resorption and osteoblastic synthesis. Osteoclasts, the bone resorbing cells, generate from differentiation of hemopoietic mononuclear cells. In the present study we have evaluated the effects of 1.0 wt% strontium (Sr) and 1.0 wt% magnesium (Mg) doping in beta-tricalcium phosphate (β-TCP) on the differentiation of mononuclear cells into osteoclast-like cells and its resorptive activity. In vitro osteoclast-like cell formation, adhesion, and resorption were studied using osteoclast precursor RAW 264.7 cell, supplemented with receptor activator of nuclear factor κβ ligand (RANKL). Osteoclast-like cell formation was noticed on pure and Sr doped β-TCP samples at day 8 which was absent on Mg doped β-TCP samples indicating decrease in initial osteoclast differentiation due to Mg doping. After 21 days of culture, osteoclast-like cell formation was evident on all samples with osteoclastic markers such as actin ring, multiple nuclei, and presence of vitronectin receptor αvβ3 integrin. After osteoclast differentiation, all substrates showed osteoclast-like cell mediated degradation, however; significantly restricted for Mg doped β-TCP samples. Our present results indicated substrate chemistry controlled osteoclast differentiation and resorptive activity which can be used in designing TCP based resorbable bone substitutes with controlled degradation properties. PMID:22566212

Metals for bone implants. Part 1. Powder metallurgy and implant rendering.

PubMed

Andani, Mohsen Taheri; Shayesteh Moghaddam, Narges; Haberland, Christoph; Dean, David; Miller, Michael J; Elahinia, Mohammad

2014-10-01

New metal alloys and metal fabrication strategies are likely to benefit future skeletal implant strategies. These metals and fabrication strategies were looked at from the point of view of standard-of-care implants for the mandible. These implants are used as part of the treatment for segmental resection due to oropharyngeal cancer, injury or correction of deformity due to pathology or congenital defect. The focus of this two-part review is the issues associated with the failure of existing mandibular implants that are due to mismatched material properties. Potential directions for future research are also studied. To mitigate these issues, the use of low-stiffness metallic alloys has been highlighted. To this end, the development, processing and biocompatibility of superelastic NiTi as well as resorbable magnesium-based alloys are discussed. Additionally, engineered porosity is reviewed as it can be an effective way of matching the stiffness of an implant with the surrounding tissue. These porosities and the overall geometry of the implant can be optimized for strain transduction and with a tailored stiffness profile. Rendering patient-specific, site-specific, morphology-specific and function-specific implants can now be achieved using these and other metals with bone-like material properties by additive manufacturing. The biocompatibility of implants prepared from superelastic and resorbable alloys is also reviewed. Copyright © 2014 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

Osteoclastogenesis and osteoclastic resorption of tricalcium phosphate: effect of strontium and magnesium doping.

PubMed

Roy, Mangal; Bose, Susmita

2012-09-01

Bone substitute materials are required to support the remodeling process, which consists of osteoclastic resorption and osteoblastic synthesis. Osteoclasts, the bone-resorbing cells, generate from differentiation of hemopoietic mononuclear cells. In the present study, we have evaluated the effects of 1.0 wt % strontium (Sr) and 1.0 wt % magnesium (Mg) doping in beta-tricalcium phosphate (β-TCP) on the differentiation of mononuclear cells into osteoclast-like cells and its resorptive activity. In vitro osteoclast-like cell formation, adhesion, and resorption were studied using osteoclast precursor RAW 264.7 cell, supplemented with receptor activator of nuclear factor κβ ligand (RANKL). Osteoclast-like cell formation was noticed on pure and Sr-doped β-TCP samples at day 8, which was absent on Mg-doped β-TCP samples indicating decrease in initial osteoclast differentiation due to Mg doping. After 21 days of culture, osteoclast-like cell formation was evident on all samples with osteoclastic markers such as actin ring, multiple nuclei, and presence of vitronectin receptor α(v)β(3) integrin. After osteoclast differentiation, all substrates showed osteoclast-like cell-mediated degradation, however, significantly restricted for Mg-doped β-TCP samples. Our present results indicated that substrate chemistry controlled osteoclast differentiation and resorptive activity, which can be used in designing TCP-based resorbable bone substitutes with controlled degradation properties. Copyright © 2012 Wiley Periodicals, Inc.

Addition of a pontic to all-ceramic Turkom-Cera fixed partial denture restorations.

PubMed

Uludag, Bulent; Tokar, Emre; Polat, Serdar

2013-04-01

High-strength all-ceramic materials are commonly used in dentistry. When complications occur in an all-ceramic restoration, the restoration is usually replaced. This article describes the time-saving ability and cost-effectiveness of this novel technique for the addition of a pontic in two complicated clinical cases. Turkom-Cera(™) [Turkom-Ceramic (M) Sdn. Bhd.] with aluminum oxide (99.98%) is an all-ceramic system that offers the option of addition of a new pontic to the sintered framework. The new pontic was cut off from an alumina blank [Turkom-Ceramic (M) Sdn. Bhd.], moistened, and attached to the framework using alumina gel [Turkom-Ceramic (M) Sdn. Bhd.]. The framework was veneered with veneering porcelain (Vita VM 7; VITA Zahnfabrik). The two cases presented here involving the addition of a pontic to sintered framework were followed up for at least 1 year. No complication was detected or reported by the patients. Alumina- and zirconia-based ceramics are particularly suitable for for all-ceramic restorations in high-stress bearing areas. However, replacement of a failed all-ceramic restoration is not the most practical solution, considering both cost and tooth-related factors. This attractive feature of the Turkom-Cera allows the repair of a fractured ceramic coping or the addition of a new pontic to restorations.

Addition of a pontic to all-ceramic Turkom-Cera fixed partial denture restorations

PubMed Central

Uludag, Bulent; Tokar, Emre; Polat, Serdar

2013-01-01

High-strength all-ceramic materials are commonly used in dentistry. When complications occur in an all-ceramic restoration, the restoration is usually replaced. This article describes the time-saving ability and cost-effectiveness of this novel technique for the addition of a pontic in two complicated clinical cases. Turkom-Cera™ [Turkom-Ceramic (M) Sdn. Bhd.] with aluminum oxide (99.98%) is an all-ceramic system that offers the option of addition of a new pontic to the sintered framework. The new pontic was cut off from an alumina blank [Turkom-Ceramic (M) Sdn. Bhd.], moistened, and attached to the framework using alumina gel [Turkom-Ceramic (M) Sdn. Bhd.]. The framework was veneered with veneering porcelain (Vita VM 7; VITA Zahnfabrik). The two cases presented here involving the addition of a pontic to sintered framework were followed up for at least 1 year. No complication was detected or reported by the patients. Alumina- and zirconia-based ceramics are particularly suitable for for all-ceramic restorations in high-stress bearing areas. However, replacement of a failed all-ceramic restoration is not the most practical solution, considering both cost and tooth-related factors. This attractive feature of the Turkom-Cera allows the repair of a fractured ceramic coping or the addition of a new pontic to restorations. PMID:24883033

Porous ceramic scaffolds with complex architectures

NASA Astrophysics Data System (ADS)

Munch, E.; Franco, J.; Deville, S.; Hunger, P.; Saiz, E.; Tomsia, A. P.

2008-06-01

This work compares two novel techniques for the fabrication of ceramic scaffolds for bone tissue engineering with complex porosity: robocasting and freeze casting. Both techniques are based on the preparation of concentrated ceramic suspensions with suitable properties for the process. In robocasting, the computer-guided deposition of the suspensions is used to build porous materials with designed three dimensional geometries and microstructures. Freeze casting uses ice crystals as a template to form porous lamellar ceramic materials. Preliminary results on the compressive strengths of the materials are also reported.

Mechanical properties of a new mica-based machinable glass ceramic for CAD/CAM restorations.

PubMed

Thompson, J Y; Bayne, S C; Heymann, H O

1996-12-01

Machinable ceramics (Vita Mark II and Dicor MGC) exhibit good short-term clinical performance, but long-term in vivo fracture resistance is still being monitored. The relatively low fracture toughness of currently available machinable ceramics restricts their use to conservative inlays and onlays. A new machinable glass ceramic (MGC-F) has been developed (Corning Inc.) with enhanced fluorescence and machinability. The purpose of this study was to characterize and compare key mechanical properties of MGC-F to Dicor MGC-Light, Dicor MGC-Dark, and Vita Mark II glass ceramics. The mean fracture toughness and indented biaxial flexure strength of MGC-F were each significantly greater (p < or = 0.01) than that of Dicor MGC-Light, Dicor MGC-Dark, and Vita Mark II ceramic materials. The results of this study indicate the potential for better in vivo fracture resistance of MGC-F compared with existing machinable ceramic materials for CAD/CAM restorations.

Inverse analysis of giant macroscopic negative thermal expansion of Ca2RuO4‑ y ceramics based on elasticity and structural topology optimization

NASA Astrophysics Data System (ADS)

Takezawa, Akihiro; Takenaka, Koshi; Zhang, Xiaopeng

2018-05-01

Ca2RuO4‑ y ceramics exhibit a large volumetric negative thermal expansions (NTE), although the crystallographic volume contraction on heating is much smaller than the NTE. Therefore, we examine the differences in the mechanisms underlying the volumetric thermal expansion for ruthenate ceramics and crystals in the context of the elasticity. We identify the possible microstructure of ruthenate ceramics composed of crystal grains and cavities using structural topology optimization. We conclude that the measured large volumetric NTE of ruthenate ceramics is certainly possible via anisotropic crystallographic thermal expansion through an elastic mechanism.

Nd3+, Y3+-codoped SrF2 laser ceramics

NASA Astrophysics Data System (ADS)

Li, Weiwei; Mei, Bingchu; Song, Jinghong

2015-09-01

0.15 at.% Nd3+, 5 at.% Y3+-codoped SrF2 laser ceramic based on single crystal was prepared by extensive plastic deformation. Microstructure, optical and laser properties of the Nd3+, Y3+:SrF2 ceramic were investigated. The lasing of Nd3+, Y3+-codoped SrF2 ceramics with diode pumping have been observed and true CW laser operation around 1057 nm and 1050 nm was obtained with a slope efficiency of 31.9%. In particular, the fracture toughness of the ceramic is 0.98 MPa m1/2, which is approximately two times higher than that of single crystal.

Mo-Si-B-Based Coatings for Ceramic Base Substrates

NASA Technical Reports Server (NTRS)

Perepezko, John Harry (Inventor); Sakidja, Ridwan (Inventor); Ritt, Patrick (Inventor)

2015-01-01

Alumina-containing coatings based on molybdenum (Mo), silicon (Si), and boron (B) ("MoSiB coatings") that form protective, oxidation-resistant scales on ceramic substrate at high temperatures are provided. The protective scales comprise an aluminoborosilicate glass, and may additionally contain molybdenum. Two-stage deposition methods for forming the coatings are also provided.

Properties and Applications of High Emissivity Composite Films Based on Far-Infrared Ceramic Powder

PubMed Central

Xiong, Yabo; Huang, Shaoyun; Wang, Wenqi; Liu, Xinghai; Li, Houbin

2017-01-01

Polymer matrix composite materials that can emit radiation in the far-infrared region of the spectrum are receiving increasing attention due to their ability to significantly influence biological processes. This study reports on the far-infrared emissivity property of composite films based on far-infrared ceramic powder. X-ray fluorescence spectrometry, Fourier transform infrared spectroscopy, thermogravimetric analysis, and X-ray powder diffractometry were used to evaluate the physical properties of the ceramic powder. The ceramic powder was found to be rich in aluminum oxide, titanium oxide, and silicon oxide, which demonstrate high far-infrared emissivity. In addition, the micromorphology, mechanical performance, dynamic mechanical properties, and far-infrared emissivity of the composite were analyzed to evaluate their suitability for strawberry storage. The mechanical properties of the far-infrared radiation ceramic (cFIR) composite films were not significantly influenced (p ≥ 0.05) by the addition of the ceramic powder. However, the dynamic mechanical analysis (DMA) properties of the cFIR composite films, including a reduction in damping and shock absorption performance, were significant influenced by the addition of the ceramic powder. Moreover, the cFIR composite films showed high far-infrared emissivity, which has the capability of prolonging the storage life of strawberries. This research demonstrates that cFIR composite films are promising for future applications. PMID:29186047

Properties and Applications of High Emissivity Composite Films Based on Far-Infrared Ceramic Powder.

PubMed

Xiong, Yabo; Huang, Shaoyun; Wang, Wenqi; Liu, Xinghai; Li, Houbin

2017-11-29

Polymer matrix composite materials that can emit radiation in the far-infrared region of the spectrum are receiving increasing attention due to their ability to significantly influence biological processes. This study reports on the far-infrared emissivity property of composite films based on far-infrared ceramic powder. X-ray fluorescence spectrometry, Fourier transform infrared spectroscopy, thermogravimetric analysis, and X-ray powder diffractometry were used to evaluate the physical properties of the ceramic powder. The ceramic powder was found to be rich in aluminum oxide, titanium oxide, and silicon oxide, which demonstrate high far-infrared emissivity. In addition, the micromorphology, mechanical performance, dynamic mechanical properties, and far-infrared emissivity of the composite were analyzed to evaluate their suitability for strawberry storage. The mechanical properties of the far-infrared radiation ceramic (cFIR) composite films were not significantly influenced ( p ≥ 0.05) by the addition of the ceramic powder. However, the dynamic mechanical analysis (DMA) properties of the cFIR composite films, including a reduction in damping and shock absorption performance, were significant influenced by the addition of the ceramic powder. Moreover, the cFIR composite films showed high far-infrared emissivity, which has the capability of prolonging the storage life of strawberries. This research demonstrates that cFIR composite films are promising for future applications.

Integration Science and Technology of Silicon-Based Ceramics and Composites:Technical Challenges and Opportunities

NASA Technical Reports Server (NTRS)

Singh, M.

2013-01-01

Ceramic integration technologies enable hierarchical design and manufacturing of intricate ceramic and composite parts starting with geometrically simpler units that are subsequently joined to themselves and/or to metals to create components with progressively higher levels of complexity and functionality. However, for the development of robust and reliable integrated systems with optimum performance for high temperature applications, detailed understanding of various thermochemical and thermomechanical factors is critical. Different technical approaches are required for the integration of ceramic to ceramic and ceramic to metal systems. Active metal brazing, in particular, is a simple and cost-effective method to integrate ceramic to metallic components. Active braze alloys usually contain a reactive filler metal (e.g., Ti, Cr, V, Hf etc) that promotes wettability and spreading by inducing chemical reactions with the ceramics and composites. In this presentation, various examples of brazing of silicon nitride to themselves and to metallic systems are presented. Other examples of joining of ceramic composites (C/SiC and SiC/SiC) using ceramic interlayers and the resulting microstructures are also presented. Thermomechanical characterization of joints is presented for both types of systems. In addition, various challenges and opportunities in design, fabrication, and testing of integrated similar (ceramic-ceramic) and dissimilar (ceramic-metal) material systems will be discussed. Potential opportunities and need for the development of innovative design philosophies, approaches, and integrated system testing under simulated application conditions will also be presented.

Comparative characterization of a novel cad-cam polymer-infiltrated-ceramic-network

PubMed Central

Pascual, Agustín; Camps, Isabel; Grau-Benitez, María

2015-01-01

Background The field of dental ceramics for CAD-CAM is enriched with a new innovative material composition having a porous three-dimensional structure of feldspathic ceramic infiltrated with acrylic resins.The aim of this study is to determine the mechanical properties of Polymer-Infiltrated-Ceramic-Network (PICN) and compare its performance with other ceramics and a nano-ceramic resin available for CAD-CAM systems. Material and Methods In this study a total of five different materials for CAD-CAM were investigated. A polymer-infiltrated ceramic (Vita Enamic), a nano-ceramic resin (Lava Ultimate), a feldspathic ceramic (Mark II), a lithium disilicate ceramic (IPS-e max CAD) and finally a Leucite based ceramic (Empress - CAD). From CAD-CAM blocks, 120 bars (30 for each material cited above) were cut to measure the flexural strength with a three-point-bending test. Strain at failure, fracture stress and Weibull modulus was calculated. Vickers hardness of each material was also measured. Results IPS-EMAX presents mechanical properties significantly better from the other materials studied. Its strain at failure, flexural strength and hardness exhibited significantly higher values in comparison with the others. VITA ENAMIC and LAVA ULTIMATE stand out as the next most resistant materials. Conclusions The flexural strength, elastic modulus similar to a tooth as well as having less hardness than ceramics make PICN materials an option to consider as a restorative material. Key words:Ceramic infiltrated with resin, CAD-CAM, Weibull modulus, flexural strength, micro hardness. PMID:26535096

Comparison of the bacterial removal performance of silver nanoparticles and a polymer based quaternary amine functiaonalized silsesquioxane coated point-of-use ceramic water filters.

PubMed

Zhang, Hongyin; Oyanedel-Craver, Vinka

2013-09-15

This study compares the disinfection performance of ceramic water filters impregnated with two antibacterial compounds: silver nanoparticles and a polymer based quaternary amine functiaonalized silsesquioxane (poly(trihydroxysilyl) propyldimethyloctadecyl ammonium chloride (TPA)). This study evaluated these compounds using ceramic disks manufactures with clay obtained from a ceramic filter factory located in San Mateo Ixtatan, Guatemala. Instead of using full size ceramic water filters, manufactured 6.5 cm diameter ceramic water filter disks were used. Results showed that TPA can achieve a log bacterial reduction value of 10 while silver nanoparticles reached up to 2 log reduction using a initial concentration of bacteria of 10(10)-10(11)CFU/ml. Similarly, bacterial transport demonstrated that ceramic filter disks painted with TPA achieved a bacterial log reduction value of 6.24, which is about 2 log higher than the values obtained for disks painted with silver nanoparticles (bacterial log reduction value: 4.42). The release of both disinfectants from the ceramic materials to the treated water was determined measuring the effluent concentrations in each test performed. Regarding TPA, about 3% of the total mass applied to the ceramic disks was released in the effluent over 300 min, which is slightly lower than the release percentage for silver nanoparticles (4%). This study showed that TPA provides a comparable disinfection performance than silver nanoparticles in ceramic water filter. Another advantage of using TPA is the cost as the price of TPA is considerable lower than silver nanoparticles. In spite of the use of TPA in several medical related products, there is only partial information regarding the health risk associated with the ingestion of this compound. Additional long-term toxicological information for TPA should be evaluated before its future application in ceramic water filters. Copyright © 2013 Elsevier B.V. All rights reserved.

Homogeneity of Gd-based garnet transparent ceramic scintillators for gamma spectroscopy

NASA Astrophysics Data System (ADS)

Seeley, Z. M.; Cherepy, N. J.; Payne, S. A.

2013-09-01

Transparent polycrystalline ceramic scintillators based on the composition Gd1.49Y1.49Ce0.02Ga2.2Al2.8O12 are being developed for gamma spectroscopy detectors. Scintillator light yield and energy resolution depend on the details of various processing steps, including powder calcination, green body formation, and sintering atmosphere. We have found that gallium sublimation during vacuum sintering creates compositional gradients in the ceramic and can degrade the energy resolution. While sintering in oxygen produces ceramics with uniform composition and little afterglow, light yields are reduced, compared to vacuum sintering. By controlling the atmosphere during the various process steps, we were able to minimize the gallium sublimation, resulting in a more homogeneous composition and improved gamma spectroscopy performance.

Piezoelectric textured ceramics: Effective properties and application to ultrasonic transducers.

PubMed

Levassort, Franck; Pham Thi, Mai; Hemery, Henry; Marechal, Pierre; Tran-Huu-Hue, Louis-Pascal; Lethiecq, Marc

2006-12-22

Piezoelectric textured ceramics obtained by homo-template grain growth (HTGG) were recently demonstrated. A simple model with several assumptions has been used to calculate effective parameters of these new materials. Different connectivities have been simulated to show that spatial arrangements between the considered phases have little influence on the effective parameters, even through the 3-0 connectivity delivers the highest electromechanical thickness factor. A transducer based on a textured ceramic sample has been fabricated and characterised to show the efficiency of these piezoelectric materials. Finally, in a single element transducer configuration, simulation shows an improvement of 2 dB sensitivity for a transducer made with textured ceramic in comparison with a similar transducer design based on standard soft PZT (at equivalent bandwidths).

Ceramic materials of low-temperature synthesis for dielectric coating applied by 3D aerosol printing used in nano- and microelectronics, lighting engineering, and spacecraft control devices

NASA Astrophysics Data System (ADS)

Ivanov, A. A.; Tuev, V. I.; Nisan, A. V.; Potapov, G. N.

2016-11-01

A synthesis technique of low-temperature ceramic material based on aluminosilicates of dendrimer morphology capable to contain up to 80 wt % of nitrides and oxides of high-melting compounds as filler has been developed. The synthesis is based on a sol-gel method followed by mechanochemical treatment and ultrasonic dispersing. Dielectric ceramic layers with the layer thickness in the nanometer range and high thermal conductivity have been obtained for the first time by 3D aerosol printing of the synthesized material. The study of the obtained ceramic coating on the metal surface (Al) has proved its use prospects in microelectronics, light engineering, and devices for special purposes.

Non-destructive thermo-mechanical behavior assessment of glass-ceramics for dental applications

NASA Astrophysics Data System (ADS)

Kordatos, E. Z.; Abdulkadhim, Z.; Feteira, A. M.

2017-05-01

Every year millions of people seek dental treatment to either repair damaged, unaesthetic and dysfunctional teeth or replace missing natural teeth. Several dental materials have been developed to meet the stringent requirements in terms of mechanical properties, aesthetics and chemical durability in the oral environment. Glass-ceramics exhibit a suitable combination of these properties for dental restorations. This research is focused on the assessment of the thermomechanical behavior of bio-ceramics and particularly lithium aluminosilicate glass-ceramics (LAS glass-ceramics). Specifically, methodologies based on Infrared Thermography (IRT) have been applied in order the structure - property relationship to be evaluated. Non-crystallized, partially crystallized and fully crystallized glass-ceramic samples have been non-destructively assessed in order their thermo-mechanical behavior to be associated with their micro-structural features.

Experimental study of the fracture toughness of a ceramic/ceramic-matrix composite sandwich structure

DOE Office of Scientific and Technical Information (OSTI.GOV)

Li, Z.; Taya, M.; Dunn, M.L.

A hybrid experimental-numerical approach has been used to measure the fracture resistance of a sandwich structure consisting of a 304 stainless steel/partially stabilized zirconia ceramic-matrix composite crack-arresting layer embedded in a partially stabilized zirconia ceramic specimen. The mode 1 fracture toughness increases significantly when the crack propagates from the ceramic into the ceramic-matrix composite region. The increased toughening due to the stainless steel particles is explained reasonably well by a toughening model based on processing-induced thermal residual stresses. In addition, several experimental modifications were made to the chevron-notch wedge-loaded double cantilever beam specimen to overcome numerous problems encountered in generatingmore » a precrack in the small, brittle specimens used in this study.« less

Magnetohydrodynamic electrode

DOEpatents

Marchant, David D.; Killpatrick, Don H.

1978-01-01

An electrode capable of withstanding high temperatures and suitable for use as a current collector in the channel of a magnetohydrodynamic (MHD) generator consists of a sintered powdered metal base portion, the upper surface of the base being coated with a first layer of nickel aluminide, an intermediate layer of a mixture of nickel aluminide - refractory ceramic on the first layer and a third or outer layer of a refractory ceramic material on the intermediate layer. The sintered powdered metal base resists spalling by the ceramic coatings and permits greater electrode compliance to thermal shock. The density of the powdered metal base can be varied to allow optimization of the thermal conductivity of the electrode and prevent excess heat loss from the channel.

2014 NEPP Tasks Update for Ceramic and Tantalum Capacitors

NASA Technical Reports Server (NTRS)

Teverovsky, Alexander A.

2014-01-01

Presentation describes recent development in research on MnO2, wet, and polymer tantalum capacitors. Low-voltage failures in multilayer ceramic capacitors and techniques to reveal precious metal electrode (PME) and base metal electrode (BME) capacitors with cracks are discussed. A voltage breakdown technique is suggested to select high quality low-voltage BME ceramic capacitors.

Stochastic modeling of filtrate alkalinity in water filtration devices: Transport through micro/nano porous clay based ceramic materials

USDA-ARS?s Scientific Manuscript database

Clay and plant materials such as wood are the raw materials used in manufacture of ceramic water filtration devices around the world. A step by step manufacturing procedure which includes initial mixing, molding and sintering is used. The manufactured ceramic filters have numerous pores which help i...

Guanidine Soaps As Vehicles For Coating Ceramic Fibers

NASA Technical Reports Server (NTRS)

Philipp, Warren H.; Veitch, Lisa C.; Jaskowiak, Martha H.

1994-01-01

Soaps made from strong organic base guanidine and organic fatty acids serve as vehicles and binders for coating ceramic fibers, various smooth substrates, and other problematic surfaces with thin precious-metal or metal-oxide films. Films needed to serve as barriers to diffusion in fiber/matrix ceramic composite materials. Guanidine soaps entirely organic and burn off, leaving no residues.

A fractographic study of clinically retrieved zirconia-ceramic and metal-ceramic fixed dental prostheses.

PubMed

Pang, Zhen; Chughtai, Asima; Sailer, Irena; Zhang, Yu

2015-10-01

A recent 3-year randomized controlled trial (RCT) of tooth supported three- to five-unit zirconia-ceramic and metal-ceramic posterior fixed dental prostheses (FDPs) revealed that veneer chipping and fracture in zirconia-ceramic systems occurred more frequently than those in metal-ceramic systems [1]. This study seeks to elucidate the underlying mechanisms responsible for the fracture phenomena observed in this RCT using a descriptive fractographic analysis. Vinyl-polysiloxane impressions of 12 zirconia-ceramic and 6 metal-ceramic FDPs with veneer fractures were taken from the patients at the end of a mean observation of 40.3±2.8 months. Epoxy replicas were produced from these impressions [1]. All replicas were gold coated, and inspected under the optical microscope and scanning electron microscope (SEM) for descriptive fractography. Among the 12 zirconia-ceramic FDPs, 2 had small chippings, 9 had large chippings, and 1 exhibited delamination. Out of 6 metal-ceramic FDPs, 5 had small chippings and 1 had large chipping. Descriptive fractographic analysis based on SEM observations revealed that fracture initiated from the wear facet at the occlusal surface in all cases, irrespective of the type of restoration. Zirconia-ceramic and metal-ceramic FDPs all fractured from microcracks that emanated from occlusal wear facets. The relatively low fracture toughness and high residual tensile stress in porcelain veneer of zirconia restorations may contribute to the higher chipping rate and larger chip size in zirconia-ceramic FDPs relative to their metal-ceramic counterparts. The low veneer/core interfacial fracture energy of porcelain-veneered zirconia may result in the occurrence of delamination in zirconia-ceramic FDPs. Copyright © 2015 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

A fractographic study of clinically retrieved zirconia–ceramic and metal–ceramic fixed dental prostheses

PubMed Central

Pang, Zhen; Chughtai, Asima; Sailer, Irena; Zhang, Yu

2015-01-01

Objectives A recent 3-year randomized controlled trial (RCT) of tooth supported three- to five-unit zirconia–ceramic and metal–ceramic posterior fixed dental prostheses (FDPs) revealed that veneer chipping and fracture in zirconia–ceramic systems occurred more frequently than those in metal–ceramic systems [1]. This study seeks to elucidate the underlying mechanisms responsible for the fracture phenomena observed in this RCT using a descriptive fractographic analysis. Methods Vinyl-polysiloxane impressions of 12 zirconia–ceramic and 6 metal–ceramic FDPs with veneer fractures were taken from the patients at the end of a mean observation of 40.3 ± 2.8 months. Epoxy replicas were produced from these impressions [1]. All replicas were gold coated, and inspected under the optical microscope and scanning electron microscope (SEM) for descriptive fractography. Results Among the 12 zirconia–ceramic FDPs, 2 had small chippings, 9 had large chippings, and 1 exhibited delamination. Out of 6 metal–ceramic FDPs, 5 had small chippings and 1 had large chipping. Descriptive fractographic analysis based on SEM observations revealed that fracture initiated from the wear facet at the occlusal surface in all cases, irrespective of the type of restoration. Significance Zirconia–ceramic and metal–ceramic FDPs all fractured from microcracks that emanated from occlusal wear facets. The relatively low fracture toughness and high residual tensile stress in porcelain veneer of zirconia restorations may contribute to the higher chipping rate and larger chip size in zirconia–ceramic FDPs relative to their metal–ceramic counterparts. The low veneer/core interfacial fracture energy of porcelain-veneered zirconia may result in the occurrence of delamination in zirconia–ceramic FDPs. PMID:26233469

Ultrahigh Piezoelectric Properties in Textured (K,Na)NbO3 -Based Lead-Free Ceramics.

PubMed

Li, Peng; Zhai, Jiwei; Shen, Bo; Zhang, Shujun; Li, Xiaolong; Zhu, Fangyuan; Zhang, Xingmin

2018-02-01

High-performance lead-free piezoelectric materials are in great demand for next-generation electronic devices to meet the requirement of environmentally sustainable society. Here, ultrahigh piezoelectric properties with piezoelectric coefficients (d 33 ≈700 pC N -1 , d 33 * ≈980 pm V -1 ) and planar electromechanical coupling factor (k p ≈76%) are achieved in highly textured (K,Na)NbO 3 (KNN)-based ceramics. The excellent piezoelectric properties can be explained by the strong anisotropic feature, optimized engineered domain configuration in the textured ceramics, and facilitated polarization rotation induced by the intermediate phase. In addition, the nanodomain structures with decreased domain wall energy and increased domain wall mobility also contribute to the ultrahigh piezoelectric properties. This work not only demonstrates the tremendous potential of KNN-based ceramics to replace lead-based piezoelectrics but also provides a good strategy to design high-performance piezoelectrics by controlling appropriate phase and crystallographic orientation. © 2018 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Probabilistic Sizing and Verification of Space Ceramic Structures

NASA Astrophysics Data System (ADS)

Denaux, David; Ballhause, Dirk; Logut, Daniel; Lucarelli, Stefano; Coe, Graham; Laine, Benoit

2012-07-01

Sizing of ceramic parts is best optimised using a probabilistic approach which takes into account the preexisting flaw distribution in the ceramic part to compute a probability of failure of the part depending on the applied load, instead of a maximum allowable load as for a metallic part. This requires extensive knowledge of the material itself but also an accurate control of the manufacturing process. In the end, risk reduction approaches such as proof testing may be used to lower the final probability of failure of the part. Sizing and verification of ceramic space structures have been performed by Astrium for more than 15 years, both with Zerodur and SiC: Silex telescope structure, Seviri primary mirror, Herschel telescope, Formosat-2 instrument, and other ceramic structures flying today. Throughout this period of time, Astrium has investigated and developed experimental ceramic analysis tools based on the Weibull probabilistic approach. In the scope of the ESA/ESTEC study: “Mechanical Design and Verification Methodologies for Ceramic Structures”, which is to be concluded in the beginning of 2012, existing theories, technical state-of-the-art from international experts, and Astrium experience with probabilistic analysis tools have been synthesized into a comprehensive sizing and verification method for ceramics. Both classical deterministic and more optimised probabilistic methods are available, depending on the criticality of the item and on optimisation needs. The methodology, based on proven theory, has been successfully applied to demonstration cases and has shown its practical feasibility.

[Development of fluorescent probes for bone imaging in vivo ~Fluorescent probes for intravital imaging of osteoclast activity~.

PubMed

Minoshima, Masafumi; Kikuchi, Kazuya

Fluorescent molecules are widely used as a tool to directly visualize target biomolecules in vivo. Fluorescent probes have the advantage that desired function can be rendered based on rational design. For bone-imaging fluorescent probes in vivo, they should be delivered to bone tissue upon administration. Recently, a fluorescent probe for detecting osteoclast activity was developed. The fluorescent probe has acid-sensitive fluorescence property, specific delivery to bone tissue, and durability against laser irradiation, which enabled real-time intravital imaging of bone-resorbing osteoclasts for a long period of time.

Enhanced texture evolution and piezoelectric properties in CuO-doped Pb(In1/2Nb1/2)O3-Pb(Mg1/3Nb2/3)O3-PbTiO3 grain-oriented ceramics

NASA Astrophysics Data System (ADS)

Chang, Yunfei; Watson, Beecher; Fanton, Mark; Meyer, Richard J.; Messing, Gary L.

2017-12-01

In this work, both crystallographic texture and doping engineering strategies were integrated to develop relaxor-PbTiO3 (PT) based ternary ferroelectric ceramics with enhanced texture evolution and superior electromechanical properties. CuO-doped Pb(In1/2Nb1/2)O3-Pb(Mg1/3Nb2/3)O3-PbTiO3 (PIN-PMN-PT) piezoelectric ceramics with [001]c texture fraction ≥97% were synthesized by templated grain growth. The addition of CuO significantly promotes densification and oriented grain growth in the templated ceramics, leading to full texture development at dramatically reduced times and temperatures. Moreover, the CuO dopant remarkably enhances the piezoelectric properties of the textured ceramics while maintaining high phase transition temperatures and large coercive fields. Doping 0.125 wt. % CuO yields the electromechanical properties of d33 = 927 pC/N, d33* = 1510 pm/V, g33 = 43.2 × 10-3 Vm/N, Kp = 0.87, Ec=8.8 kV/cm, and tan δ = 1.3%, which are the best values reported so far in PIN-PMN-PT based ceramics. The high piezoelectric coefficient is mainly from the reversible piezoelectric response, with the irreversible contribution being on the order of 13.1%. We believe that this work not only facilitates closing the performance gap between ceramics and single crystals but also can expand relaxor-PT based piezoelectric application fields.

Ni-BaTiO3-Based Base-Metal Electrode (BME) Ceramic Capacitors for Space Applications

NASA Technical Reports Server (NTRS)

Liu, Donhang; Fetter, Lula; Meinhold, Bruce

2015-01-01

A multi-layer ceramic capacitor (MLCC) is a high-temperature (1350C typical) co-fired ceramic monolithic that is composed of many layers of alternately stacked oxide-based dielectric and internal metal electrodes. To make the dielectric layers insulating and the metal electrode layers conducting, only highly oxidation-resistant precious metals, such as platinum, palladium, and silver, can be used for the co-firing of insulating MLCCs in a regular air atmosphere. MLCCs made with precious metals as internal electrodes and terminations are called precious-metal electrode (PME) capacitors. Currently, all military and space-level applications only address the use of PME capacitors.

Effect of Light-Cured Resin Cement Application on Translucency of Ceramic Veneers and Light Transmission of LED Polymerization Units.

PubMed

Zhang, Lei; Luo, Xiao Ping; Tan, Ren Xiang

2018-05-31

To evaluate the effect of light-cured resin cement application based on etching and silanization on the translucent property of ceramic veneers in different thicknesses, testing the hypothesis that the surface treatment and subsequent resin cement application could influence the translucency of ceramic veneers. The relationship between translucency of ceramic veneers and light transmission irradiated by LED polymerization units was also determined. 40 specimens (10 mm diameter) were fabricated from IPS e.max Press HT A2 ceramic ingots, and polished to 0.3 ± 0.01 mm, 0.5 ± 0.01 mm, 0.7 ± 0.01 mm, 1.0 ± 0.01 mm, and 1.5 ± 0.01 mm thick (n = 8/group). One surface of each disc was etched with HF acid, silanized with Monobond-S, and applied with a light-cured resin cement (Variolink N Transparent Base). Before and after the above procedure, the total luminous transmittance (τ) of all specimens was assessed by a spectrophotometer in a wavelength range of 380-780 nm. A handheld radiometer was used to measure the light intensity irradiated by three LED polymerization units. Light transmission (LT) through ceramic specimens after resin cement application was calculated. Data were statistically analyzed using two-way ANOVA (p = 0.05) and Tukey's test. The correlation between translucency (τ) of ceramic veneers after resin cement application and light transmission (LT) of curing units was statistically evaluated using Spearman correlation test (p = 0.05). With the increase of ceramic thickness, the transmittance decreased significantly (p < 0.05). For the 0.3-mm, 0.5-mm, and 0.7-mm-thick groups, the transmittance of ceramic specimens was statistically significantly lower after resin cement application (p < 0.05). The r value of Bluephase C8 was 0.988, 0.977 for Bluphase, and 0.883 for Bluephase 20i, indicating that the light transmission (LT%) was positively correlated to the translucency of ceramic veneers, regardless of the type of curing units. After the light-cured resin cement application based on etching and silanization, the ceramic veneers (less than 0.7-mm thick) were less translucent, and the translucency decreased when the thickness increased. Because of the lower translucency of ceramic veneers, the light intensity of LED units transmitted to resin layer would decrease when curing. © 2018 by the American College of Prosthodontists.

Maintaining space in localized ridge augmentation using guided bone regeneration with tenting screw technology.

PubMed

Chasioti, Evdokia; Chiang, Tat Fai; Drew, Howard J

2013-01-01

Prosthetic guided implant surgery requires adequate ridge dimensions for proper implant placement. Various surgical procedures can be used to augment deficient alveolar ridges. Studies have examined new bone formation on deficient ridges, utilizing numerous surgical techniques and biomaterials. The goal is to develop time efficient techniques, which have low morbidity. A crucial factor for successful bone grafting procedures is space maintenance. The article discusses space maintenance tenting screws, used in conjunction with bone allografts and resorbable barrier membranes, to ensure uneventful guided bone regeneration (GBR) enabling optimal implant positioning. The technique utilized has been described in the literature to treat severely resorbed alveolar ridges and additionally can be considered in restoring the vertical and horizontal component of deficient extraction sites. Three cases are presented to illustrate the utilization and effectiveness of tenting screw technology in the treatment of atrophic extraction sockets and for deficient ridges.

The Use of Polymer Design in Resorbable Colloids

NASA Astrophysics Data System (ADS)

Finne-Wistrand, Anna; Albertsson, Ann-Christine

2006-08-01

During the past decade, researchers in the field of polymer chemistry have developed a wide range of very powerful procedures for constructing ever-more-sophisticated polymers. These methods subsequently have been used in suitable systems to solve specific medical problems. This is complicated, and many key factors such as mechanical properties, biocompatibility, biodegradation, stability, and degradation profile must be considered. Colloid particle systems can be used to solve many biomedical- and pharmaceutical-related problems, and it is expected that nanotechnology can be used to develop these materials, devices, and systems even further. For example, an injectible scaffold system with a defined release and degradation profile has huge potential for the repair and regeneration of damaged tissues. This short, nonexhaustive review presents examples of polymer architecture in resorbable particles that have been compared and tested in biomedical applications. We also discuss the design of polymers for core-shell structures.

Functional fixation of autotransplanted tooth germs by using bioresorbable membranes.

PubMed

Gérard, Eric; Membre, Hervé; Gaudy, Jean-François; Mahler, Patrick; Bravetti, Pierre

2002-12-01

The purpose of this study was to evaluate the contribution of a bioresorbable membrane placement to the healing of immature teeth after autotransplantation of tooth buds. Six cases were selected: 2 transplantations of wisdom teeth, 2 for premolar agenesis, 1 for ectopia, and 1 premolar in an incisor position. The crown of each tooth germ and the marginal alveolar bone were covered with a resorbable membrane. The radicular edification was nearly complete, neither ankylosis nor inflammatory resorption was observable, the pulp vitality was preserved, and the periodontal integration was identical to that of other teeth. The membrane ensured contention and stabilization of the transplant, allowed functional stimulation, permitted protection of the coagulum and periodontal cells, and kept the epithelium at a distance. The transplantations of immature teeth were improved by the use of a resorbable membrane, which caused an optimal functional fixation of the transplanted tooth.

Evidence that Resorption of Bone by Rat Peritoneal Macrophages Occurs in an Acidic Environment

NASA Technical Reports Server (NTRS)

Blair, H. C.

1985-01-01

Skeletal loss in space, like any form of osteoporosis, reflects a relative imbalance of the activities of cells resorbing (degrading) or forming bone. Consequently, prevention of weightlessness induced bone loss may theoretically be accomplished by (1) stimulating bone formation or (2) inhibiting bone resorption. This approach, however, requires fundamental understanding of the mechanisms by which cells form or degrade bone, information not yet at hand. An issue central to bone resorption is the pH at which resorption takes place. The pH dependent spectral shift of a fluorescent dye (fluorescein isothiocyanate) conjugated to bone matrix was used to determine the pH at the resorptive cell bone matrix interface. Devitalized rat bone was used as the substrate, and rat peritoneal macrophages were used as the bone resorbing cells. The results suggest that bone resorption is the result of generation of an acidic microenvironment at the cell matrix junction.

Structural design methodologies for ceramic-based material systems

NASA Technical Reports Server (NTRS)

Duffy, Stephen F.; Chulya, Abhisak; Gyekenyesi, John P.

1991-01-01

One of the primary pacing items for realizing the full potential of ceramic-based structural components is the development of new design methods and protocols. The focus here is on low temperature, fast-fracture analysis of monolithic, whisker-toughened, laminated, and woven ceramic composites. A number of design models and criteria are highlighted. Public domain computer algorithms, which aid engineers in predicting the fast-fracture reliability of structural components, are mentioned. Emphasis is not placed on evaluating the models, but instead is focused on the issues relevant to the current state of the art.

Developing porous ceramics on the base of zirconia oxide with thin and permeable pores by crystallization of organic additive method

NASA Astrophysics Data System (ADS)

Kamyshnaya, K. S.; Khabas, T. A.

2016-11-01

In this paper porous ceramics on the base of ZrO2 nanopowders and micropowders has been developed by freeze-casting method. A zirconia/carbamide slurry was frozen in mold and dehydrated in CaCl2 at room temperature. This simple process enabled the formation of porous ceramics with highly aligned pores as a replica of the carbamide crystals. The samples showed higher porosity of 47.9%. In addition, these materials could be used as membrane for air cleaning.

Phase assemblage study and cytocompatibility property of heat treated potassium magnesium phosphate-silicate ceramics.

PubMed

Kumar, Ravi; Kalmodia, Sushma; Nath, Shekhar; Singh, Dileep; Basu, Bikramjit

2009-08-01

This article reports the study on a new generation bioactive ceramic, based on MgKPO(4) (Magnesium Potassium Phosphate, abbreviated as MKP) for biomedical applications. A series of heat treatment experiments on the slip cast silica (SiO(2)) containing MKP ceramics were carried out at 900, 1,000 and 1,100 degrees C for 4 h in air. The density of the slip cast ceramic increases to 2.5 gm/cm(3) upon heat treatment at 900 degrees C. However, no significant change in density is measured upon heat treatment to higher temperature of 1,000 and 1,100 degrees C. On the basis of XRD results, the presence of K(2)MgSi(5)O(12) and dehydrated MgKPO(4) were confirmed and complementary information has also been obtained using FT-IR and Raman spectroscopy. In order to confirm the in vitro cytocompatibility property, the cell culture tests were carried out on selected samples and the results reveal good cell adhesion and spreading of L929 mouse fibroblast cells. MTT assay analysis with L929 cells confirmed non-cytotoxic behavior of MKP containing ceramics and the results are comparable with sintered HAp ceramics. It is expected that the newly developed MKP based materials could be a good substitute for hydroxyapatite (HAp or HA) based bioceramics.

Method for improving the toughness of silicon carbide-based ceramics

DOEpatents

Tein, Tseng-Ying; Hilmas, Gregory E.

1996-01-01

Method of improving the toughness of SiC-based ceramics. SiC, , AlN, Al.sub.2 O.sub.3 and optionally .alpha.-Si.sub.3 N.sub.4 are hot pressed to form a material which includes AlN polytypoids within its structure.

Method Using Water-Based Solvent to Prepare Li7La3Zr2O12 Solid Electrolytes.

PubMed

Huang, Xiao; Lu, Yang; Jin, Jun; Gu, Sui; Xiu, Tongping; Song, Zhen; Badding, Michael E; Wen, Zhaoyin

2018-05-09

Li-garnet Li 7 La 3 Zr 2 O 12 (LLZO) is a promising candidate of solid electrolytes for high-safety solid-state Li + ion batteries. However, because of its high reactivity to water, the preparation of LLZO powders and ceramics is not easy for large-scale amounts. Herein, a method applying water-based solvent is proposed to demonstrate a possible solution. Ta-doped LLZO, that is, Li 6.4 La 3 Zr 1.4 Ta 0.6 O 12 (LLZTO), and its LLZTO/MgO composite ceramics are made by attrition milling, followed by a spray-drying process using water-based slurries. The impacts of parameters of the method on the structure and properties of green and sintered pellets are studied. A relative density of ∼95%, a Li-ion conductivity of ∼3.5 × 10 -4 S/cm, and uniform grain size LLZTO/MgO garnet composite ceramics are obtained with an attrition-milled LLZTO/MgO slurry that contains 40 wt % solids and 2 wt % polyvinyl alcohol binder. Li-sulfur batteries based on these ceramics are fabricated and work under 25 °C for 20 cycles with a Coulombic efficiency of 100%. This research demonstrates a promising mass production method for the preparation of Li-garnet ceramics.

Environmental Barrier Coatings for Ceramics and Ceramic Composites

NASA Technical Reports Server (NTRS)

Lee, Kang N.; Fox, Dennis; Eldridge, Jeffrey; Robinson, R. Craig; Bansal, Narottam

2004-01-01

One key factor that limits the performance of current gas turbine engines is the temperature capability of hot section structural components. Silicon-based ceramics, such as SiC/SiC composites and monolithic Si3N4, are leading candidates to replace superalloy hot section components in the next generation gas turbine engines due to their excellent high temperature properties. A major stumbling block to realizing Si-based ceramic hot section components is the recession of Si-based ceramics in combustion environments due to the volatilization of silica scale by water vapor. An external environmental barrier coating (EBC) is the most promising approach to preventing the recession. Current EBCs are based on silicon, mullite (3A12O3-2SiO2) and BSAS (barium strontium aluminum silicate with celsian structure). Volatility of BSAS, BSAS-silica chemical reaction, and low melting point of silicon limit the durability and temperature capability of current EBCs. Research is underway to develop EBCs with longer life and enhanced temperature capability. Understanding key issues affecting the performance of current EBCs is necessary for successful development of advanced EBCs. These issues include stress, chemical compatibility, adherence, and water vapor stability. Factors that affect stress are thermal expansion mismatch, phase stability, chemical stability, elastic modulus, etc. The current understanding on these issues will be discussed.

Development of Al2O3 fiber-reinforced Al2O3-based ceramics.

PubMed

Tanimoto, Yasuhiro; Nemoto, Kimiya

2004-09-01

The purpose of this study was to use a tape casting technique to develop an Al2O3 fiber-reinforced Al2O3-based ceramic material (Al2O3-fiber/Al2O3 composite) into a new type of dental ceramic. The Al2O3-based ceramic used a matrix consisting of 60 wt% Al2O3 powder and 40 wt% SiO2-B2O3 powder. The prepreg sheets of Al2O3-fiber/Al2O3 composite (in which uniaxially aligned Al2O3 fibers were infiltrated with the Al2O3-based matrix) were fabricated continuously using tape casting technique with a doctor blade system. Multilayer preforms of Al2O3-fiber/Al2O3 composite sheets were then sintered at a maximum temperature of 1000 degrees C under an atmospheric pressure in a furnace. The results showed that the shrinkage and bending properties of Al2O3-fiber/Al2O3 composite exceeded those of unreinforced Al2O3--hence demonstrating the positive effects of fiber reinforcement. In conclusion, the tape casting technique has been utilized to successfully develop a new type of dental ceramic material.

In vivo biofilm formation on different dental ceramics.

PubMed

Bremer, Felicia; Grade, Sebastian; Kohorst, Philipp; Stiesch, Meike

2011-01-01

To investigate the formation of oral biofilm on various dental ceramics in vivo. Five different ceramic materials were included: a veneering glass- ceramic, a lithium disilicate glass-ceramic, a yttrium-stabilized zirconia (Y-TZP), a hot isostatically pressed (HIP) Y-TZP ceramic, and an HIP Y-TZP ceramic with 25% alumina. Test specimens were attached to individually designed acrylic appliances; five volunteers wore these appliances for 24 hours in the maxillary arch. After intraoral exposure, the samples were removed from the appliances and the adhering biofilms vitally stained. Then, the two-dimensional surface coating and thickness of the adhering biofilm were determined by confocal laser scanning microscopy. Statistical analysis was performed using one-way ANOVA with the level of significance set at .05. Significant differences (P < .001) in the bacterial surface coating and in the thickness of the biofilm were found between the various ceramic materials. The lowest surface coating (19.0%) and biofilm thickness (1.9 Μm) were determined on the HIP Y-TZP ceramic; the highest mean values were identified with the lithium disilicate glass-ceramic (46.8%, 12.6 Μm). Biofilm formation on various types of dental ceramics differed significantly; in particular, zirconia exhibited low plaque accumulation. In addition to its high strength, low plaque accumulation makes zirconia a promising material for various indications (including implant abutments and telescopic crowns) that previously were met only with metal-based materials.

Residual stress measurement in veneering ceramic by hole-drilling.

PubMed

Mainjot, Amélie K; Schajer, Gary S; Vanheusden, Alain J; Sadoun, Michaël J

2011-05-01

Mismatch in thermal expansion properties between veneering ceramic and metallic or high-strength ceramic cores can induce residual stresses and initiate cracks when combined with functional stresses. Knowledge of the stress distribution within the veneering ceramic is a key factor for understanding and predicting chipping failures, which are well-known problems with Yttria-tetragonal-zirconia-polycrystal based fixed partial dentures. The objectives of this study are to develop a method for measuring the stress profile in veneering ceramics and to compare ceramic-fused-to-metal compounds to veneered Yttria-tetragonal-zirconia-polycrystal ceramic. The hole-drilling method, often used for engineering measurements, was adapted for use with veneering ceramic. Because of the high sensitivity needed in comparison with industrial applications, a high sensitivity electrical measurement chain was developed. All samples exhibited the same type of stress vs. depth profile, starting with compressive at the ceramic surface, decreasing with depth and becoming tensile at 0.5-1.0mm from the surface, and then becoming slightly compressive again. The zirconia samples exhibited a stress depth profile of larger magnitude. The hole drilling method was shown be a practical tool for measuring residual stresses in veneering ceramics. Copyright © 2010 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Advanced Turbine Technology Applications Project (ATTAP) 1993 annual report

NASA Technical Reports Server (NTRS)

1994-01-01

This report summarizes work performed by AlliedSignal Engines, a unit of AlliedSignal Aerospace Company, during calendar year 1993, toward development and demonstration of structural ceramic technology for automotive gas turbine engines. This work was performed for the U.S. Department of Energy (DOE) under National Aeronautics and Space Administration (NASA) Contract DEN3-335, Advanced Turbine Technology Applications Project (ATFAP). During 1993, the test bed used to demonstrate ceramic technology was changed from the AlliedSignal Engines/Garrett Model AGT101 regenerated gas turbine engine to the Model 331-200(CT) engine. The 331-200(CT) ceramic demonstrator is a fully-developed test platform based on the existing production AlliedSignal 331-200(ER) gas turbine auxiliary power unit (APU), and is well suited to evaluating ceramic turbine blades and nozzles. In addition, commonality of the 331-200(CT) engine with existing gas turbine APU's in commercial service provides the potential for field testing of ceramic components. The 1993 ATTAP activities emphasized design modifications of the 331-200 engine test bed to accommodate ceramic first-stage turbine nozzles and blades, fabrication of the ceramic components, ceramic component proof and rig tests, operational tests of the test bed equipped with the ceramic components, and refinement of critical ceramic design technologies.

Fracture loads of all-ceramic crowns under wet and dry fatigue conditions.

PubMed

Borges, Gilberto A; Caldas, Danilo; Taskonak, Burak; Yan, Jiahau; Sobrinho, Lourenco Correr; de Oliveira, Wildomar José

2009-12-01

The aim of this study was to test the hypothesis that fracture loads of fatigued dental ceramic crowns are affected by testing environment and luting cement. One hundred and eighty crowns were prepared from bovine teeth using a lathe. Ceramic crowns were prepared from three types of ceramic systems: an alumina-infiltrated ceramic, a lithia-disilicate-based glass ceramic, and a leucite-reinforced ceramic. For each ceramic system, 30 crowns were cemented with a composite resin cement, and the remaining 30 with a resin-modified glass ionomer cement. For each ceramic system and cement, ten specimens were loaded to fracture without fatiguing. A second group (n = 10) was subjected to cyclic fatigue and fracture tested in a dry environment, and a third group (n = 10) was fatigued and fractured in distilled water. The results were statistically analyzed using one-way ANOVA and Tukey HSD test. The fracture loads of ceramic crowns decreased significantly after cyclic fatigue loading (p

Determination of elastic modulus of ceramics using ultrasonic testing

NASA Astrophysics Data System (ADS)

Sasmita, Firmansyah; Wibisono, Gatot; Judawisastra, Hermawan; Priambodo, Toni Agung

2018-04-01

Elastic modulus is important material property on structural ceramics application. However, bending test as a common method for determining this property require particular specimen preparation. Furthermore, elastic modulus of ceramics could vary because it depends on porosity content. For structural ceramics industry, such as ceramic tiles, this property is very important. This drives the development of new method to improve effectivity or verification method as well. In this research, ultrasonic testing was conducted to determine elastic modulus of soda lime glass and ceramic tiles. The experiment parameter was frequency of probe (1, 2, 4 MHz). Characterization of density and porosity were also done for analysis. Results from ultrasonic testing were compared with elastic modulus resulted from bending test. Elastic modulus of soda-lime glass based on ultrasonic testing showed excellent result with error 2.69% for 2 MHz probe relative to bending test result. Testing on red and white ceramic tiles were still contained error up to 41% and 158%, respectively. The results for red ceramic tile showed trend that 1 MHz probe gave better accuracy in determining elastic modulus. However, testing on white ceramic tile showed different trend. It was due to the presence of porosity and near field effect.

Marginal and Internal Discrepancies of Posterior Zirconia-Based Crowns Fabricated with Three Different CAD/CAM Systems Versus Metal-Ceramic.

PubMed

Ortega, Rocio; Gonzalo, Esther; Gomez-Polo, Miguel; Suárez, María J

2015-01-01

The aim of this study was to analyze the marginal and internal fit of metalceramic and zirconia-based crowns. Forty standardized steel specimens were prepared to receive posterior crowns and randomly divided into four groups (n = 10): (1) metal-ceramic, (2) NobelProcera Zirconia, (3) Lava Zirconia, and (4) VITA In-Ceram YZ. All crowns were cemented with glass-ionomer agent and sectioned buccolingually. A scanning electron microscope was used for measurements. Kruskal-Wallis and Wilcoxon signed rank test (α = .05) statistical analyses were conducted. Significant differences (P < .0001) in marginal discrepancies were observed between metal-ceramic and zirconia groups. No differences were found for the axial wall fit (P = .057). Significant differences were shown among the groups in discrepancies at the occlusal cusp (P = .0012) and at the fossa (P = .0062). No differences were observed between surfaces. All zirconia groups showed better values of marginal discrepancies than the metal-ceramic group. Procera Zirconia showed the lowest gaps.

FOREWORD: Focus on Advanced Ceramics Focus on Advanced Ceramics

NASA Astrophysics Data System (ADS)

Ohashi, Naoki

2011-06-01

Much research has been devoted recently to developing technologies for renewable energy and improving the efficiency of the processes and devices used in industry and everyday life. Efficient solutions have been found using novel materials such as platinum and palladium-based catalysts for car exhaust systems, samarium-cobalt and neodymium-iron-boron permanent magnets for electrical motors, and so on. However, their realization has resulted in an increasing demand for rare elements and in their deficit, the development of new materials based on more abundant elements and new functionalities of traditional materials. Moreover, increasing environmental and health concerns demand substitution of toxic or hazardous substances with nature-friendly alternatives. In this context, this focus issue on advanced ceramics aims to review current trends in ceramics science and technology. It is related to the International Conference on Science and Technology of Advanced Ceramics (STAC) held annually to discuss the emerging issues in the field of ceramics. An important direction of ceramic science is the collaboration between experimental and theoretical sciences. Recent developments in density functional theory and computer technology have enabled the prediction of physical and chemical properties of ceramics, thereby assisting the design of new materials. Therefore, this focus issue includes articles devoted to theory and advanced characterization techniques. As mentioned above, the potential shortage of rare elements is becoming critical to the industry and has resulted in a Japanese government initiative called the 'Ubiquitous Element Strategy'. This focus issue also includes articles related to this strategy and to the associated topics of energy conversion, such as phosphors for high-efficiency lighting and photocatalysts for solar-energy harvesting. We hope that this focus issue will provide a timely overview of current trends and problems in ceramics science and technology and promote new research and development in this field.

Methods of improving mechanical and biomedical properties of Ca-Si-based ceramics and scaffolds.

PubMed

Wu, Chengtie

2009-05-01

CaSiO3 ceramics and porous scaffolds are regarded as potential materials for bone tissue regeneration owing to their excellent bioactivity. However, their low mechanical strength and high dissolution limit their further biomedical application. In this report, we introduce three methods to improve the mechanical and biomedical properties of CaSiO3 ceramics and scaffolds. Positive ions and polymer modification are two promising ways to improve the mechanical and biomedical properties of CaSiO3 ceramics and scaffolds for bone tissue regeneration.

Dispersed metal-toughened ceramics and ceramic brazing

DOE Office of Scientific and Technical Information (OSTI.GOV)

Moorhead, A.J.; Tiegs, T.N.; Lauf, R.J.

1983-01-01

An alumina (Al/sub 2/O/sub 3/) based material that contains approximately 1 vol % finely dispersed platinum or chromium was developed for use in high temperature thermal-shock resistant electrical insulators. The work at ORNL is divided into two areas: (1) development of DMT ceramics; and (2) development of brazing filler metals suitable for making ceramic-to-ceramic and ceramic-to-metal brazements. The DMT ceramics and brazements are intended for service at elevated temperatures and at high stress levels in the dirty environments of advanced heat engines. The development and characterization of DMT ceramics includes processing (powder preparation, densification and heat treatment) and detailed measurementmore » of mechanical and physical properties (strength, fracture toughness, and thermal conductivity). The brazing work includes: (1) the formulation and melting of small quantities of experimental brazing filler metals; (2) evaluation of the wetting and bonding behavior of these filler metals on Al/sub 2/O/sub 3/, partially stabilized zirconia and ..cap alpha..-SiC in a sessile drop apparatus; and (3) determine the short-term strength and fracture toughness of brazements.« less

Engineering of III-Nitride Semiconductors on Low Temperature Co-fired Ceramics.

PubMed

Mánuel, J M; Jiménez, J J; Morales, F M; Lacroix, B; Santos, A J; García, R; Blanco, E; Domínguez, M; Ramírez, M; Beltrán, A M; Alexandrov, D; Tot, J; Dubreuil, R; Videkov, V; Andreev, S; Tzaneva, B; Bartsch, H; Breiling, J; Pezoldt, J; Fischer, M; Müller, J

2018-05-02

This work presents results in the field of advanced substrate solutions in order to achieve high crystalline quality group-III nitrides based heterostructures for high frequency and power devices or for sensor applications. With that objective, Low Temperature Co-fired Ceramics has been used, as a non-crystalline substrate. Structures like these have never been developed before, and for economic reasons will represent a groundbreaking material in these fields of Electronic. In this sense, the report presents the characterization through various techniques of three series of specimens where GaN was deposited on this ceramic composite, using different buffer layers, and a singular metal-organic chemical vapor deposition related technique for low temperature deposition. Other single crystalline ceramic-based templates were also utilized as substrate materials, for comparison purposes.

[Coloration of mica glass ceramic for use in dental CAD/CAM system].

PubMed

Sun, Ying; Wang, Zhong-yi; Tian, Jie-mo; Cao, Xiao-gang

2003-03-01

An intrinsically colored machinable glass-ceramic containing tetrasilicic fluormica as the predominant crystal phase was studied, which was used in molar crown in dental CAD/CAM system. Orthogonal design analysis was used to select appropriate base formula, coloration and heat treatment process. Factors influencing the color appearance of mica glass ceramic were nucleation agent and the ratio of Mg(2+) to K(+) in base formula; Cerium oxide (CeO(2)) was used as the main coloration; The preferred heat treatment was 650 degrees C for 1 h and 1,000 degrees C or 1,050 degrees C for 3 h - 4 h. This mica glass-ceramic could provide 4 to 5 color appearance for dental use, it showed excellent machinability which was eminently suitable for use in dental CAD/CAM system.

Adhesion/cementation to zirconia and other non-silicate ceramics: Where are we now?

PubMed Central

Thompson, Jeffrey Y; Stoner, Brian R.; Piascik, Jeffrey R.; Smith, Robert

2010-01-01

Non-silicate ceramics, especially zirconia, have become a topic of great interest in the field of prosthetic and implant dentistry. A clinical problem with use of zirconia-based components is the difficulty in achieving suitable adhesion with intended synthetic substrates or natural tissues. Traditional adhesive techniques used with silica-based ceramics do not work effectively with zirconia. Currently, several technologies are being utilized clinically to address this problem, and other approaches are under investigation. Most focus on surface modification of the inert surfaces of high strength ceramics. The ability to chemically functionalize the surface of zirconia appears to be critical in achieving adhesive bonding. This review will focus on currently available approaches as well as new advanced technologies to address this problem. PMID:21094526

Three-Dimensional Volumetric Changes in Severely Resorbed Alveolar Sockets After Ridge Augmentation with Bovine-Derived Xenograft and Resorbable Barrier: A Preliminary Study on CBCT Imaging.

PubMed

Manavella, Valeria; Romano, Federica; Corano, Lisa; Bignardi, Cristina; Aimetti, Mario

The primary aim of the study was to describe a novel technique to evaluate volumetric hard tissue dimensional changes after ridge augmentation procedures. The secondary aim was to apply this newly developed measuring method to compromised alveolar sockets grafted with a slowly resorbing biomaterial covered with a collagen membrane. Eleven patients (6 men and 5 women, mean age 52.7 ± 8.3 years) requiring extraction of one hopeless tooth for severe periodontitis in the maxillary anterior area were consecutively treated with a ridge augmentation procedure. All experimental sockets showed advanced buccal bone plate deficiency and were grafted with deproteinized bovine bone mineral with 10% collagen covered with a collagen membrane. Sockets healed by secondary intention. Three-dimensional volumetric alveolar bone changes were calculated by superimposing cone beam computed tomography scans obtained before and 12 months after the augmentation procedure. After 12 months, the alveolar mineralized tissue filled 91.20% ± 7.96% of the maximum volume for regeneration. The augmentation procedure appeared not only to compensate for bone remodeling in most alveolar regions but also to repair a significant portion of the buccal wall. The most significant ridge width changes occurred 1 mm apical to the bone crest (2.33 ± 1.46 mm, P < .001). Within present limitations, this radiographic measuring methodology can be a useful tool to evaluate changes in socket volume. A ridge preservation technique performed with collagenated bovine bone and a collagen membrane was able to improve ridge shape and dimensions in compromised alveolar sockets.

Long-Term Results of Mandibular Distraction Osteogenesis with a Resorbable Device in Infants with Robin Sequence: Effects on Developing Molars and Mandibular Growth.

PubMed

Paes, Emma C; Bittermann, Gerhard K P; Bittermann, Dirk; Muradin, Marvick M; van Hogezand, Rose; Etty, Erika; Mink van der Molen, Aebele B; Kon, Moshe; Breugem, Corstiaan C

2016-02-01

Mandibular distraction osteogenesis with a unidirectional resorbable device is an effective treatment option for severe upper airway obstruction in infants with Robin sequence. Long-term effects, especially with regard to tooth development and mandibular outgrowth, are not known. Robin sequence infants with a follow-up of greater than or equal to 5 years were included. Baseline characteristics were extracted from medical records. Panoramic and lateral cephalometric radiographs were analyzed and patients were recalled for physical examination. Ten infants underwent mandibular distraction osteogenesis at a mean age of 3.7 months (median, 19 months; range, 11 days to 27 months). Mean length of follow-up was 6.8 years (range, 5.0 to 7.9 years). Ten Robin sequence infants without mandibular distraction osteogenesis (mean length of follow-up, 7.4 years; range, 6.7 to 8.9 years) were the controls. Shape anomalies, positional changes, and root malformations of molars were seen significantly more often than in the control group (p = 0.007, p = 0.009, and p = 0.043, respectively). Mandibular length was shorter (p = 0.030), but mandibular ramus height was comparable (p = 0.838) with that of the non-mandibular distraction osteogenesis group. Compared with healthy controls, all Robin sequence infants had a significantly shorter mandible. Mandibular distraction osteogenesis with a resorbable system reveals overall good short- and long-term results, but the effects on developing molars and mandibular outgrowth likely necessitate secondary procedures. This factor should be considered when deciding on treatment options and counseling of parents. Therapeutic, III.

Fully-Enclosed Ceramic Micro-burners Using Fugitive Phase and Powder-based Processing

NASA Astrophysics Data System (ADS)

Do, Truong; Shin, Changseop; Kwon, Patrick; Yeom, Junghoon

2016-08-01

Ceramic-based microchemical systems (μCSs) are more suitable for operation under harsh environments such as high temperature and corrosive reactants compared to the more conventional μCS materials such as silicon and polymers. With the recent renewed interests in chemical manufacturing and process intensification, simple, inexpensive, and reliable ceramic manufacturing technologies are needed. The main objective of this paper is to introduce a new powder-based fabrication framework, which is a one-pot, cost-effective, and versatile process for ceramic μCS components. The proposed approach employs the compaction of metal-oxide sub-micron powders with a graphite fugitive phase that is burned out to create internal cavities and microchannels before full sintering. Pure alumina powder has been used without any binder phase, enabling more precise dimensional control and less structure shrinkage upon sintering. The key process steps such as powder compaction, graphite burnout during partial sintering, machining in a conventional machine tool, and final densification have been studied to characterize the process. This near-full density ceramic structure with the combustion chamber and various internal channels was fabricated to be used as a micro-burner for gas sensing applications.

Fully-Enclosed Ceramic Micro-burners Using Fugitive Phase and Powder-based Processing

PubMed Central

Do, Truong; Shin, Changseop; Kwon, Patrick; Yeom, Junghoon

2016-01-01

Ceramic-based microchemical systems (μCSs) are more suitable for operation under harsh environments such as high temperature and corrosive reactants compared to the more conventional μCS materials such as silicon and polymers. With the recent renewed interests in chemical manufacturing and process intensification, simple, inexpensive, and reliable ceramic manufacturing technologies are needed. The main objective of this paper is to introduce a new powder-based fabrication framework, which is a one-pot, cost-effective, and versatile process for ceramic μCS components. The proposed approach employs the compaction of metal-oxide sub-micron powders with a graphite fugitive phase that is burned out to create internal cavities and microchannels before full sintering. Pure alumina powder has been used without any binder phase, enabling more precise dimensional control and less structure shrinkage upon sintering. The key process steps such as powder compaction, graphite burnout during partial sintering, machining in a conventional machine tool, and final densification have been studied to characterize the process. This near-full density ceramic structure with the combustion chamber and various internal channels was fabricated to be used as a micro-burner for gas sensing applications. PMID:27546059

Design and Development for Capacitive Humidity Sensor Applications of Lead-Free Ca,Mg,Fe,Ti-Oxides-Based Electro-Ceramics with Improved Sensing Properties via Physisorption

PubMed Central

Tripathy, Ashis; Pramanik, Sumit; Manna, Ayan; Bhuyan, Satyanarayan; Azrin Shah, Nabila Farhana; Radzi, Zamri; Abu Osman, Noor Azuan

2016-01-01

Despite the many attractive potential uses of ceramic materials as humidity sensors, some unavoidable drawbacks, including toxicity, poor biocompatibility, long response and recovery times, low sensitivity and high hysteresis have stymied the use of these materials in advanced applications. Therefore, in present investigation, we developed a capacitive humidity sensor using lead-free Ca,Mg,Fe,Ti-Oxide (CMFTO)-based electro-ceramics with perovskite structures synthesized by solid-state step-sintering. This technique helps maintain the submicron size porous morphology of the developed lead-free CMFTO electro-ceramics while providing enhanced water physisorption behaviour. In comparison with conventional capacitive humidity sensors, the presented CMFTO-based humidity sensor shows a high sensitivity of up to 3000% compared to other materials, even at lower signal frequency. The best also shows a rapid response (14.5 s) and recovery (34.27 s), and very low hysteresis (3.2%) in a 33%–95% relative humidity range which are much lower values than those of existing conventional sensors. Therefore, CMFTO nano-electro-ceramics appear to be very promising materials for fabricating high-performance capacitive humidity sensors. PMID:27455263

Improving Erosion Resistance of Plasma-Sprayed Ceramic Coatings by Elevating the Deposition Temperature Based on the Critical Bonding Temperature

NASA Astrophysics Data System (ADS)

Yao, Shu-Wei; Yang, Guan-Jun; Li, Cheng-Xin; Li, Chang-Jiu

2018-01-01

Interlamellar bonding within plasma-sprayed coatings is one of the most important factors dominating the properties and performance of coatings. The interface bonding between lamellae significantly influences the erosion behavior of plasma-sprayed ceramic coatings. In this study, TiO2 and Al2O3 coatings with different microstructures were deposited at different deposition temperatures based on the critical bonding temperature concept. The erosion behavior of ceramic coatings was investigated. It was revealed that the coatings prepared at room temperature exhibit a typical lamellar structure with numerous unbonded interfaces, whereas the coatings deposited at the temperature above the critical bonding temperature present a dense structure with well-bonded interfaces. The erosion rate decreases sharply with the improvement of interlamellar bonding when the deposition temperature increases to the critical bonding temperature. In addition, the erosion mechanisms of ceramic coatings were examined. The unbonded interfaces in the conventional coatings act as pre-cracks accelerating the erosion of coatings. Thus, controlling interlamellar bonding formation based on the critical bonding temperature is an effective approach to improve the erosion resistance of plasma-sprayed ceramic coatings.

The development of heterogeneous materials based on Ni and B4C powders using a cold spray and stratified selective laser melting technologies

NASA Astrophysics Data System (ADS)

Filippov, A. A.; Fomin, V. M.; Buzyurkin, A. E.; Kosarev, V. F.; Malikov, A. G.; Orishich, A. M.; Ryashin, N. S.

2018-01-01

The work is dedicated to the creation of new ceramic-composite materials based on boron carbide, nickel and using a laser welding in order to obtain three dimensional objects henceforth. The perspective way of obtaining which has been suggested by the authors combined two methods: cold spray technology and subsequent laser post-treatment. At this stage, the authors focused on the interaction of the laser with the substance, regardless of the multi-layer object development. The investigated material of this work was the metal-ceramic mixture based on boron carbide, which has high physical and mechanical characteristics, such as hardness, elastic modulus, and chemical resistance. The nickel powder as a binder and different types of boron carbide were used. The ceramic content varied from 30 to 70% by mass. Thin ceramic layers were obtained by the combined method and cross-sections of different seams were studied. It was shown that the most perspective layers for additive manufacturing could be obtained from cold spray coatings with ceramic concentrations more than 50% by weight treated when laser beam was defocused (thermal-conductive laser mode).

Method for improving the toughness of silicon carbide-based ceramics

DOEpatents

Tein, T.Y.; Hilmas, G.E.

1996-12-03

Method of improving the toughness of SiC-based ceramics is disclosed. SiC, , AlN, Al{sub 2}O{sub 3} and optionally {alpha}-Si{sub 3}N{sub 4} are hot pressed to form a material which includes AlN polytypoids within its structure. 1 fig.

Affordable, Robust Ceramic Joining Technology (ARCJoint) Developed

NASA Technical Reports Server (NTRS)

Steele, Gynelle C.

2001-01-01

Affordable, Robust Ceramic Joining Technology (ARCJoint) is a method for joining high temperature- resistant ceramic pieces together, establishing joints that are strong, and allowing joining to be done in the field. This new way of joining allows complex shapes to be formed by joining together geometrically simple shapes. The joining technology at NASA is one of the enabling technologies for the application of silicon-carbide-based ceramic and composite components in demanding and high-temperature applications. The technology is being developed and tested for high-temperature propulsion parts for aerospace use. Commercially, it can be used for joining ceramic pieces used for high temperature applications in the power-generating and chemical industries, as well as in the microelectronics industry. This innovation could yield big payoffs for not only the power-generating industry but also the Silicon Valley chipmakers. This technology, which was developed at the NASA Glenn Research Center by Dr. Mrityunjay Singh, is a two-step process involving first using a paste to join together ceramic pieces and bonding them by heating the joint to 110 to 120 C for between 10 and 20 min. This makes the joint strong enough to be handled for the final joining. Then, a silicon-based substance is applied to the joint and heated to 1400 C for 10 to 15 min. The resulting joint is as strong as the original ceramic material and can withstand the same high temperatures.

Expansion of Bone Marrow Mesenchymal Stromal Cells in Perfused 3D Ceramic Scaffolds Enhances In Vivo Bone Formation.

PubMed

Hoch, Allison I; Duhr, Ralph; Di Maggio, Nunzia; Mehrkens, Arne; Jakob, Marcel; Wendt, David

2017-12-01

Bone marrow-derived mesenchymal stromal cells (BMSC), when expanded directly within 3D ceramic scaffolds in perfusion bioreactors, more reproducibly form bone when implanted in vivo as compared to conventional expansion on 2D polystyrene dishes/flasks. Since the bioreactor-based expansion on 3D ceramic scaffolds encompasses multiple aspects that are inherently different from expansion on 2D polystyrene, we aimed to decouple the effects of specific parameters among these two model systems. We assessed the effects of the: 1) 3D scaffold vs. 2D surface; 2) ceramic vs. polystyrene materials; and 3) BMSC niche established within the ceramic pores during in vitro culture, on subsequent in vivo bone formation. While BMSC expanded on 3D polystyrene scaffolds in the bioreactor could maintain their in vivo osteogenic potential, results were similar as BMSC expanded in monolayer on 2D polystyrene, suggesting little influence of the scaffold 3D environment. Bone formation was most reproducible when BMSC are expanded on 3D ceramic, highlighting the influence of the ceramic substrate. The presence of a pre-formed niche within the scaffold pores had negligible effects on the in vivo bone formation. The results of this study allow a greater understanding of the parameters required for perfusion bioreactor-based manufacturing of osteogenic grafts for clinical applications. © 2017 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Influence of CAD/CAM systems and cement selection on marginal discrepancy of zirconia-based ceramic crowns.

PubMed

Martínez-Rus, Francisco; Suárez, María J; Rivera, Begoña; Pradíes, Guillermo

2012-04-01

To analyze the effect of ceramic manufacturing technique and luting cement selection on the marginal adaptation of zirconium oxide-based all-ceramic crowns. An extracted mandibular first premolar was prepared for a complete coverage restoration and subsequently duplicated 40 times in a liquid crystal polymer (LCP). All-ceramic crowns (n = 10) were fabricated on LCP models using the following systems: glass-infiltrated zirconia-toughened alumina (In-Ceram Zirconia) and yttrium cation-doped tetragonal zirconia polycrystals (In-Ceram YZ, Cercon, and Procera Zirconia). The restorations (n = 5) were cemented on their respective dies with glass-ionomer cement (Ketac Cem Aplicap) and resin cement (Panavia 21). The absolute marginal discrepancy of the crowns was measured before and after cementation by scanning electronic microscopy at 160 points along the circumferential margin. The data were analyzed using one-way ANOVA for repeated measures and for independent samples, Scheffé's multiple range post hoc test, and Student's t-test (alpha = 0.05). There were statistical differences in the mean marginal openings among the four all-ceramic systems before and after luting (P < 0.0001). The Procera restorations had the lowest pre- and post-cementation values (P < 0.0001). A significant increase in the marginal gap size caused by luting media occurred in all tested groups (P < 0.0001). Resin cement resulted in larger marginal discrepancies than glass-ionomer cement (P < 0.0001).

Ceramics in Restorative and Prosthetic DENTISTRY1

NASA Astrophysics Data System (ADS)

Kelly, J. Robert

1997-08-01

This review is intended to provide the ceramic engineer with information about the history and current use of ceramics in dentistry, contemporary research topics, and potential research agenda. Background material includes intra-oral design considerations, descriptions of ceramic dental components, and the origin, composition, and microstructure of current dental ceramics. Attention is paid to efforts involving net-shape processing, machining as a forming method, and the analysis of clinical failure. A rationale is presented for the further development of all-ceramic restorative systems. Current research topics receiving attention include microstructure/processing/property relationships, clinical failure mechanisms and in vitro testing, wear damage and wear testing, surface treatments, and microstructural modifications. The status of the field is critically reviewed with an eye toward future work. Significant improvements seem possible in the clinical use of ceramics based on engineering solutions derived from the study of clinically failed restorations, on the incorporation of higher levels of "biomimicry" in new systems, and on the synergistic developments in dental cements and adhesive dentin bonding.

Method for sealing an oxygen transport membrane assembly

DOE Office of Scientific and Technical Information (OSTI.GOV)

Gonzalez, Javier E.; Grant, Arthur F.

An improved method of sealing a ceramic part to a solid part made of ceramic, metal, cermet or a ceramic coated metal is provided. The improved method includes placing a bond agent comprising an Al 2O 3 and SiO 2 based glass-ceramic material and organic binder material on adjoining surfaces of the ceramic part and the solid part. The assembly is heated to a first target temperature that removes or dissolves the organic binder material from the bond agent and the assembly is subjected to a second induction heating step at a temperature ramp rate of between about 100.degree. C.more » and 200.degree. C. per minute to temperatures where the glass-ceramic material flows and wets the interface between adjoining surfaces. The assembly is rapidly cooled at a cooling rate of about 140.degree. C. per minute or more to induce nucleation and re-crystallization of the glass-ceramic material to form a dense, durable and gas-tight seal.« less

Treatment of intrabony defects with resorbable materials, non-resorbable materials and flap debridement.

PubMed

Zybutz, M D; Laurell, L; Rapoport, D A; Persson, G R

2000-03-01

Different types of barriers are used in guided tissue regenerative procedures. This prospective study compared resorbable citric acid ester softened polylactic acid membranes (RM) and non-resorbable expanded polytetrafluoroethylene (ePTFE) barriers (NRM) in GTR treatment of intrabony defects. 29 subjects were randomly assigned to the RM group or NRM group. Each patient received one GTR procedure. An open flap debridement (FD) was performed at another site 2 weeks later to evaluate healing potential. Clinical treatment outcomes were finally evaluated 12 months after surgery for changes of pocket depth PD, probing attachment level PAL, and probing bone level PBL, and radiographically for bone change using standardised radiographs. No differences in healing patters after surgery were found between patients in the 2 study groups as evaluated from the FD surgical procedures. NRM treated sites showed less signs of post-surgical inflammation during the 1st 4 weeks of healing than did RM treated sites (p<0.05). GTR-treated defects in the RM group, initially 7.0+/-2.2 mm deep, showed PD reduction of 3.3+/-2.2 mm, PAL gain of 2.4+/-1.8 mm, PBL gain of 2.4+/-3.7 mm (28%) and a radiographic bone fill of 2.3+/-2.4 mm. Defects treated with the NRM exhibited PD reduction of 3.1+/-2.1 mm, PAL gain of 2.4+/-0.8 mm, PBL gain of 2.2+/-1.7 mm (25%) and a radiographic bone fill of 3.3+/-2.2 mm. All improvements were statistically significant (p<0.01) but there was no difference between RM and NRM treatments for any of the efficacy variables. The results of this study indicated that there was no clinically significant difference in treatment outcomes following GTR treatment of intrabony defects with citric acid ester softened polylactic acid membranes as compared to ePTFE barriers. The overall mean inter-proximal vertical bone defect fill at 12 months as assessed from intra-oral radiographs was 44% of the original mean defect depth. Thus, no clinically significant difference in treatment outcomes was observed following GTR treatment of intrabony defects with citric acid ester softened polylactic acid membranes or ePTFE barriers.

Grinding damage assessment for CAD-CAM restorative materials.

PubMed

Curran, Philippe; Cattani-Lorente, Maria; Anselm Wiskott, H W; Durual, Stéphane; Scherrer, Susanne S

2017-03-01

To assess surface/subsurface damage after grinding with diamond discs on five CAD-CAM restorative materials and to estimate potential losses in strength based on crack size measurements of the generated damage. The materials tested were: Lithium disilicate (LIT) glass-ceramic (e.max CAD), leucite glass-ceramic (LEU) (Empress CAD), feldspar ceramic (VM2) (Vita Mark II), feldspar ceramic-resin infiltrated (EN) (Enamic) and a composite reinforced with nano ceramics (LU) (Lava Ultimate). Specimens were cut from CAD-CAM blocs and pair-wise mirror polished for the bonded interface technique. Top surfaces were ground with diamond discs of respectively 75, 54 and 18μm. Chip damage was measured on the bonded interface using SEM. Fracture mechanics relationships were used to estimate fracture stresses based on average and maximum chip depths assuming these to represent strength limiting flaws subjected to tension and to calculate potential losses in strength compared to manufacturer's data. Grinding with a 75μm diamond disc induced on a bonded interface critical chips averaging 100μm with a potential strength loss estimated between 33% and 54% for all three glass-ceramics (LIT, LEU, VM2). The softer materials EN and LU were little damage susceptible with chips averaging respectively 26μm and 17μm with no loss in strength. Grinding with 18μm diamond discs was still quite detrimental for LIT with average chip sizes of 43μm and a potential strength loss of 42%. It is essential to understand that when grinding glass-ceramics or feldspar ceramics with diamond discs surface and subsurface damage are induced which have the potential of lowering the strength of the ceramic. Careful polishing steps should be carried out after grinding especially when dealing with glass-ceramics. Copyright © 2017 The Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Practice-based clinical evaluation of ceramic single crowns after at least five years.

PubMed

Dhima, Matilda; Paulusova, Vladimira; Carr, Alan B; Rieck, Kevin L; Lohse, Christine; Salinas, Thomas J

2014-02-01

Long-term practice-based clinical evaluations of various contemporary ceramic crown restorations from multiple practitioners are limited. The aims of this study were to evaluate the clinical performance of ceramic single crowns and to identify factors that influence their clinical performance. Ceramic single crowns that had been placed at the Mayo Clinic and in function since 2005 were identified and included in the study. The restorations were examined clinically, radiographically, and with photographs. Modified United States Public Health Services criteria were used for the clinical evaluation. The ceramic systems evaluated were bilayer and monolayer. Fifty-nine patients (41 women, 18 men) with 226 single teeth and implants restored with single ceramic crowns were identified. The mean duration from insertion date to study examination date was 6.1 years. Thirteen restorations (6%) were replaced at a mean 3.3 years after insertion date (range, 0.1-6.1 years). Estimated replacement-free survival rates (95% confidence interval [CI]; number of teeth/implants still at risk) at 5 years after insertion date were 95.1% (95% CI, 92.2-98.1; 153) and at 10 years were 92.8% (95% CI, 89.1-96.8; 8). The most common reason for replacement was fracture to the core of posterior layered ceramic crowns. The most commonly used luting agent was resin-modified ionomer cement. Most restorations exhibited clinically acceptable marginal integrity, shade, no caries recurrence, and no periapical pathology. The clinical performance of ceramic single crowns at 5 and 10 years supports their application in all areas of the mouth. With the majority of fractures to the core occurring early in the lifetime of layered ceramic posterior crowns, consideration of other monolithic ceramic systems for posterior crowns is advised. Copyright © 2014 Editorial Council for the Journal of Prosthetic Dentistry. Published by Mosby, Inc. All rights reserved.

High-Temperature Wettability and Interactions between Y-Containing Ni-Based Alloys and Various Oxide Ceramics

PubMed Central

Li, Jinpeng; Gao, Ming; Li, Qingling; Bian, Weidong; Tao, Tongxiang; Zhang, Hu

2018-01-01

To obtain appropriate crucible materials for vacuum induction melting of MCrAlY alloys, four different oxide ceramics, including MgO, Y2O3, Al2O3, and ZrO2, with various microstructures were designed and characterized. The high-temperature wettability and interactions between Ni-20Co-20Cr-10Al-1.5Y alloys and oxide ceramics were studied by sessile drop experiments under vacuum. The results showed that all the systems exhibited non-wetting behavior. The contact angles were stable during the melting process of alloys and the equilibrium contact angles were 140° (MgO), 148° (Y2O3), 154° (Al2O3), and 157° (ZrO2), respectively. The interfacial reaction between the ceramic substrates and alloys occurred at high temperature. Though the ceramics had different microstructures, similar continuous Y2O3 reaction layer with thicknesses of about 25 μm at the alloy-ceramic interface in MgO, Al2O3, and ZrO2 systems formed. The average area percentage of oxides in the alloy matrices were 0.59% (MgO), 0.11% (Al2O3), 0.09% (ZrO2), and 0.02% (Y2O3), respectively. The alloys, after reacting with MgO ceramic, had the highest inclusion content, while those with the lowest content were in the Y2O3 system. Y2O3 ceramic was the most beneficial for vacuum induction melting of high-purity Y-containing Ni-based alloys. PMID:29735958

Cervical and Incisal Marginal Discrepancy in Ceramic Laminate Veneering Materials: A SEM Analysis

PubMed Central

Ranganathan, Hemalatha; Ganapathy, Dhanraj M.; Jain, Ashish R.

2017-01-01

Context: Marginal discrepancy influenced by the choice of processing material used for the ceramic laminate veneers needs to be explored further for better clinical application. Aims: This study aimed to evaluate the amount of cervical and incisal marginal discrepancy associated with different ceramic laminate veneering materials. Settings and Design: This was an experimental, single-blinded, in vitro trial. Subjects and Methods: Ten central incisors were prepared for laminate veneers with 2 mm uniform reduction and heavy chamfer finish line. Ceramic laminate veneers fabricated over the prepared teeth using four different processing materials were categorized into four groups as Group I - aluminous porcelain veneers, Group II - lithium disilicate ceramic veneers, Group III - lithium disilicate-leucite-based veneers, Group IV - zirconia-based ceramic veneers. The cervical and incisal marginal discrepancy was measured using a scanning electron microscope. Statistical Analysis Used: ANOVA and post hoc Tukey honest significant difference (HSD) tests were used for statistical analysis. Results: The cervical and incisal marginal discrepancy for four groups was Group I - 114.6 ± 4.3 μm, 132.5 ± 6.5 μm, Group II - 86.1 ± 6.3 μm, 105.4 ± 5.3 μm, Group III - 71.4 ± 4.4 μm, 91.3 ± 4.7 μm, and Group IV - 123.1 ± 4.1 μm, 142.0 ± 5.4 μm. ANOVA and post hoc Tukey HSD tests observed a statistically significant difference between the four test specimens with regard to cervical marginal discrepancy. The cervical and incisal marginal discrepancy scored F = 243.408, P < 0.001 and F = 180.844, P < 0.001, respectively. Conclusion: This study concluded veneers fabricated using leucite reinforced lithium disilicate exhibited the least marginal discrepancy followed by lithium disilicate ceramic, aluminous porcelain, and zirconia-based ceramics. The marginal discrepancy was more in the incisal region than in the cervical region in all the groups. PMID:28839415

Novel Attrition-Resistant Fischer Tropsch Catalyst

DOE Office of Scientific and Technical Information (OSTI.GOV)

Weast, Logan, E.; Staats, William, R.

2009-05-01

There is a strong national interest in the Fischer-Tropsch synthesis process because it offers the possibility of making liquid hydrocarbon fuels from reformed natural gas or coal and biomass gasification products. This project explored a new approach that had been developed to produce active, attrition-resistant Fischer-Tropsch catalysts that are based on glass-ceramic materials and technology. This novel approach represented a promising solution to the problem of reducing or eliminating catalyst attrition and maximizing catalytic activity, thus reducing costs. The technical objective of the Phase I work was to demonstrate that glass-ceramic based catalytic materials for Fischer-Tropsch synthesis have resistance tomore » catalytic deactivation and reduction of particle size superior to traditional supported Fischer-Tropsch catalyst materials. Additionally, these novel glass-ceramic-based materials were expected to exhibit catalytic activity similar to the traditional materials. If successfully developed, the attrition-resistant Fischer-Tropsch catalyst materials would be expected to result in significant technical, economic, and social benefits for both producers and public consumers of Fischer-Tropsch products such as liquid fuels from coal or biomass gasification. This program demonstrated the anticipated high attrition resistance of the glass-ceramic materials. However, the observed catalytic activity of the materials was not sufficient to justify further development at this time. Additional testing documented that a lack of pore volume in the glass-ceramic materials limited the amount of surface area available for catalysis and consequently limited catalytic activity. However, previous work on glass-ceramic catalysts to promote other reactions demonstrated that commercial levels of activity can be achieved, at least for those reactions. Therefore, we recommend that glass-ceramic materials be considered again as potential Fischer-Tropsch catalysts if it can be demonstrated that materials with adequate pore volume can be produced. During the attrition resistance tests, it was learned that the glass-ceramic materials are very abrasive. Attention should be paid in any further developmental efforts to the potential for these hard, abrasive materials to damage reactors.« less

Cervical and Incisal Marginal Discrepancy in Ceramic Laminate Veneering Materials: A SEM Analysis.

PubMed

Ranganathan, Hemalatha; Ganapathy, Dhanraj M; Jain, Ashish R

2017-01-01

Marginal discrepancy influenced by the choice of processing material used for the ceramic laminate veneers needs to be explored further for better clinical application. This study aimed to evaluate the amount of cervical and incisal marginal discrepancy associated with different ceramic laminate veneering materials. This was an experimental, single-blinded, in vitro trial. Ten central incisors were prepared for laminate veneers with 2 mm uniform reduction and heavy chamfer finish line. Ceramic laminate veneers fabricated over the prepared teeth using four different processing materials were categorized into four groups as Group I - aluminous porcelain veneers, Group II - lithium disilicate ceramic veneers, Group III - lithium disilicate-leucite-based veneers, Group IV - zirconia-based ceramic veneers. The cervical and incisal marginal discrepancy was measured using a scanning electron microscope. ANOVA and post hoc Tukey honest significant difference (HSD) tests were used for statistical analysis. The cervical and incisal marginal discrepancy for four groups was Group I - 114.6 ± 4.3 μm, 132.5 ± 6.5 μm, Group II - 86.1 ± 6.3 μm, 105.4 ± 5.3 μm, Group III - 71.4 ± 4.4 μm, 91.3 ± 4.7 μm, and Group IV - 123.1 ± 4.1 μm, 142.0 ± 5.4 μm. ANOVA and post hoc Tukey HSD tests observed a statistically significant difference between the four test specimens with regard to cervical marginal discrepancy. The cervical and incisal marginal discrepancy scored F = 243.408, P < 0.001 and F = 180.844, P < 0.001, respectively. This study concluded veneers fabricated using leucite reinforced lithium disilicate exhibited the least marginal discrepancy followed by lithium disilicate ceramic, aluminous porcelain, and zirconia-based ceramics. The marginal discrepancy was more in the incisal region than in the cervical region in all the groups.

Electrostatic micromotor based on ferroelectric ceramics

NASA Astrophysics Data System (ADS)

Baginsky, I. L.; Kostsov, E. G.

2004-11-01

A new electrostatic micromotor is described that utilizes the electromechanical energy conversion principle earlier described by the authors. The electromechanical energy conversion is based on reversible electrostatic rolling of thin metallic films (petals) on a ferroelectric surface. The motor's active media are layers of ferroelectric ceramics (about 100 µm in thickness). The characteristics of the electrostatic rolling of the petals on different ceramic surfaces are studied, as well as the dynamic characteristics of the micromotors. It is shown that the use of antiferroelectric material allows one to reach a specific energy capacitance comparable to that of the micromotors based on ferroelectric films and to achieve a specific power of 30-300 µW mm-2.

Evaluation of self-adhesive resin cement bond strength to yttria-stabilized zirconia ceramic (Y-TZP) using four surface treatments.

PubMed

Miragaya, Luciana; Maia, Luciane Cople; Sabrosa, Carlos Eduardo; de Goes, Mário Fernando; da Silva, Eduardo Moreira

2011-10-01

To evaluate the influence of four surface treatments on the bond strength of a self-adhesive resin cement to an yttria-stabilized zirconia (Y-TZP) ceramic material (Lava Frame zirconia). Forty plates (8 x 6 x 1 mm) of a Y-TZP ceramic restorative material were randomly assigned to four groups (n = 10) according to the surface treatments: control, no treatment; airborne-particle abrasion with 50-μm Al2O3; coating with an MDP-based primer; conditioning with Rocatec System. The ceramic plates treated with each of the four methods were further divided into 2 subgroups according to the resin cement tested: RelyXTM ARC (ARC, conventional) and RelyXTM Unicem (Ucem, self-adhesive). The resin cements were put into PVC tubes (diameter 0.75 mm, 0.5 mm height) placed on the ceramic plate surfaces. After water storage at 37°C for 24 h, the specimens were submitted to a microshear bond strength (μSBS) test at a crosshead speed of 1.0 mm/min. The surface treatments significantly influenced the μSBS (p < 0.05). For the four surface treatments, UCem presented significantly higher μSBS than ARC (p < 0.05). For both resin cements, the best result was produced by the MDP-based primer: ARC 15.9 ± 5.0 MPa and UCem 36.2 ± 2.1 MPa. The highest μSBS values were presented by UCem on ceramic plates treated with the MDP-based primer (36.2 ± 2.1 MPa) and Rocatec system (37.4 ± 2.3 MPa). Irrespective of the surface treatment, the self-adhesive resin cement performed better in terms of bond strength to yttria-stabilized zirconia ceramic than did conventional resin cement.

Behavior of Aging, Micro-Void, and Self-Healing of Glass/Ceramic Materials and Its Effect on Mechanical Properties

DOE Office of Scientific and Technical Information (OSTI.GOV)

Liu, Wenning N.; Sun, Xin; Khaleel, Mohammad A.

This chapter first describes tests to investigate the temporal evolution of the volume fraction of ceramic phases, the evolution of micro-damage, and the self-healing behavior of the glass ceramic sealant used in SOFCs, then a phenomenological model based on mechanical analogs is developed to describe the temperature dependent Young’s modulus of glass ceramic seal materials. It was found that after the initial sintering process, further crystallization of the glass ceramic sealant does not stop, but slows down and reduces the residual glass content while boosting the ceramic crystalline content. Under the long-term operating environment, distinct fibrous and needle-like crystals inmore » the amorphous phase disappeared, and smeared/diffused phase boundaries between the glass phase and ceramic phase were observed. Meanwhile, the micro-damage was induced by the cooling-down process from the operating temperature to the room temperature, which can potentially degrade the mechanical properties of the glass/ceramic sealant. The glass/ceramic sealant self-healed upon reheating to the SOFC operating temperature, which can restore the mechanical performance of the glass/ceramic sealant. The phenomenological model developed here includes the effects of continuing aging and devitrification on the ceramic phase volume fraction and the resulted mechanical properties of glass ceramic seal material are considered. The effects of micro-voids and self-healing are also considered using a continuum damage mechanics (CDM) model. The formulation is for glass/ceramic seal in general, and it can be further developed to account for effects of various processing parameters. This model was applied to G18, and the temperature-dependent experimental measurements were used to calibrate the modeling parameters and to validate the model prediction.« less

Integration Science and Technology of Advanced Ceramics for Energy and Environmental Applications

NASA Technical Reports Server (NTRS)

Singh, M.

2012-01-01

The discovery of new and innovative materials has been known to culminate in major turning points in human history. The transformative impact and functional manifestation of new materials have been demonstrated in every historical era by their integration into new products, systems, assemblies, and devices. In modern times, the integration of new materials into usable products has a special relevance for the technological development and economic competitiveness of industrial societies. Advanced ceramic technologies dramatically impact the energy and environmental landscape due to potential wide scale applications in all aspects of energy production, storage, distribution, conservation, and efficiency. Examples include gas turbine propulsion systems, fuel cells, thermoelectrics, photovoltaics, distribution and transmission systems based on superconductors, nuclear power generation, and waste disposal. Robust ceramic integration technologies enable hierarchical design and manufacturing of intricate ceramic components starting with geometrically simpler units that are subsequently joined to themselves and/or to metals to create components with progressively higher levels of complexity and functionality. However, for the development of robust and reliable integrated systems with optimum performance under different operating conditions, the detailed understanding of various thermochemical and thermomechanical factors is critical. Different approaches are required for the integration of ceramic-metal and ceramic-ceramic systems across length scales (macro to nano). In this presentation, a few examples of integration of ceramic to metals and ceramic to ceramic systems will be presented. Various challenges and opportunities in design, fabrication, and testing of integrated similar (ceramic-ceramic) and dissimilar (ceramic-metal) material systems will be discussed. Potential opportunities and need for the development of innovative design philosophies, approaches, and integrated system testing under simulated application conditions will also be presented.

Development of chemically bonded phosphate ceramics for stabilizing low-level mixed wastes

NASA Astrophysics Data System (ADS)

Jeong, Seung-Young

1997-11-01

Novel chemically bonded phosphate ceramics have been developed by acid-base reactions between magnesium oxide and an acid phosphate at room temperature for stabilizing U.S. Department of Energy's low-level mixed waste streams that include hazardous chemicals and radioactive elements. Newberyite (MgHPOsb4.3Hsb2O)-rich magnesium phosphate ceramic was formed by an acid-base reaction between phosphoric acid and magnesium oxide. The reaction slurry, formed at room-temperature, sets rapidly and forms stable mineral phases of newberyite, lunebergite, and residual MgO. Rapid setting also generates heat due to exothermic acid-base reaction. The reaction was retarded by partially neutralizing the phosphoric acid solution by adding sodium or potassium hydroxide. This reduced the rate of reaction and heat generation and led to a practical way of producing novel magnesium potassium phosphate ceramic. This ceramic was formed by reacting stoichiometric amount of monopotassium dihydrogen phosphate crystals, MgO, and water, forming pure-phase of MgKPOsb4.6Hsb2O (MKP) with moderate exothermic reaction. Using this chemically bonded phosphate ceramic matrix, low-level mixed waste streams were stabilized, and superior waste forms in a monolithic structure were developed. The final waste forms showed low open porosity and permeability, and higher compression strength than the Land Disposal Requirements (LDRs). The novel MKP ceramic technology allowed us to develop operational size waste forms of 55 gal with good physical integrity. In this improved waste form, the hazardous contaminants such as RCRA heavy metals (Hg, Pb, Cd, Cr, Ni, etc) were chemically fixed by their conversion into insoluble phosphate forms and physically encapsulated by the phosphate ceramic. In addition, chemically bonded phosphate ceramics stabilized radioactive elements such U and Pu. This was demonstrated with a detailed stabilization study on cerium used as a surrogate (chemically equivalent but nonradioactive) of U and Pu as well as on actual U-contaminated waste water. In particular, the leaching level of mercury in the Toxicity Characteristic Leaching Procedure (TCLP) test was reduced from 5000 to 0.00085 ppm, and the leaching level of cerium in the long term leaching test (ANS 16.1 test) was below the detection limit. These results show that the chemically bonded phosphate ceramics process may be a simple, inexpensive, and efficient method for stabilizing low-level mixed waste streams.

Translucency of dental ceramics with different thicknesses.

PubMed

Wang, Fu; Takahashi, Hidekazu; Iwasaki, Naohiko

2013-07-01

The increased use of esthetic restorations requires an improved understanding of the translucent characteristics of ceramic materials. Ceramic translucency has been considered to be dependent on composition and thickness, but less information is available about the translucent characteristics of these materials, especially at different thicknesses. The purpose of this study was to investigate the relationship between translucency and the thickness of different dental ceramics. Six disk-shaped specimens of 8 glass ceramics (IPS e.max Press HO, MO, LT, HT, IPS e.max CAD LT, MO, AvanteZ Dentin, and Trans) and 5 specimens of 5 zirconia ceramics (Cercon Base, Zenotec Zr Bridge, Lava Standard, Lava Standard FS3, and Lava Plus High Translucency) were prepared following the manufacturers' instructions and ground to a predetermined thickness with a grinding machine. A spectrophotometer was used to measure the translucency parameters (TP) of the glass ceramics, which ranged from 2.0 to 0.6 mm, and of the zirconia ceramics, which ranged from 1.0 to 0.4 mm. The relationship between the thickness and TP of each material was evaluated using a regression analysis (α=.05). The TP values of the glass ceramics ranged from 2.2 to 25.3 and the zirconia ceramics from 5.5 to 15.1. There was an increase in the TP with a decrease in thickness, but the amount of change was material dependent. An exponential relationship with statistical significance (P<.05) between the TP and thickness was found for both glass ceramics and zirconia ceramics. The translucency of dental ceramics was significantly influenced by both material and thickness. The translucency of all materials increased exponentially as the thickness decreased. All of the zirconia ceramics evaluated in the present study showed some degree of translucency, which was less sensitive to thickness compared to that of the glass ceramics. Copyright © 2013 The Editorial Council of the Journal of Prosthetic Dentistry. Published by Mosby, Inc. All rights reserved.

Crystallization and dielectric properties of PbTiO3 based glass ceramics

NASA Astrophysics Data System (ADS)

Shankar, J.; Rani, G. Neeraja; Deshpande, V. K.

2018-04-01

Glass samples with composition (50 - X) PbO - (25 + X) TiO2 - 25 B2O3 (where X = 0, 5, 10 and 12.5 mol %) were prepared using conventional quenching technique. These glass samples were converted to glass ceramics by following two stage heat treatment schedule. The XRD results in the glass ceramics revealed the formation of tetragonal lead titanate as a major crystalline phase. The SEM results show rounded crystallite of lead titanate. The ferroelectric nature of all the glass ceramic samples is confirmed by P - E hysteresis measurements. The extended heat treatment of glass ceramic samples at 593K for 10 h exhibited saturated hysteresis loops with higher values of remnant polarization.

Methods of repairing a substrate

NASA Technical Reports Server (NTRS)

Riedell, James A. (Inventor); Easler, Timothy E. (Inventor)

2011-01-01

A precursor of a ceramic adhesive suitable for use in a vacuum, thermal, and microgravity environment. The precursor of the ceramic adhesive includes a silicon-based, preceramic polymer and at least one ceramic powder selected from the group consisting of aluminum oxide, aluminum nitride, boron carbide, boron oxide, boron nitride, hafnium boride, hafnium carbide, hafnium oxide, lithium aluminate, molybdenum silicide, niobium carbide, niobium nitride, silicon boride, silicon carbide, silicon oxide, silicon nitride, tin oxide, tantalum boride, tantalum carbide, tantalum oxide, tantalum nitride, titanium boride, titanium carbide, titanium oxide, titanium nitride, yttrium oxide, zirconium boride, zirconium carbide, zirconium oxide, and zirconium silicate. Methods of forming the ceramic adhesive and of repairing a substrate in a vacuum and microgravity environment are also disclosed, as is a substrate repaired with the ceramic adhesive.

Preparation of porous (Ba,Sr)TiO3 by adding corn-starch

NASA Astrophysics Data System (ADS)

Kim, J.-G.; Sim, J.-H.; Cho, W.-S.

2002-11-01

A new method of preparing porous (Ba,Sr)TiO3 ceramics has been introduced, using an ordinary ceramics processing technique. The effect of corn-starch on the positive temperature coefficient of resistivity characteristics and microstructure of the porous (Ba,Sr)TiO3 ceramics has been investigated. When the corn-starch addition was 1-20 wt%, the PTCR jump was over 106 and 1-2 orders higher than that of samples without corn-starch. Also, it was found that the (Ba,Sr)TiO3 ceramics had porous microstructure by the addition of corn-starch. The porosity of the ceramics with 20 wt% corn-starch was 44%. The electrical properties of the (Ba,Sr)TiO3 ceramics have been discussed, based on the microstructure, resistivity of grain boundaries, donor concentration of grains and the electrical potential barrier of grain boundaries.

Biomechanical behavior of a cemented ceramic knee replacement under worst case scenarios

NASA Astrophysics Data System (ADS)

Kluess, D.; Mittelmeier, W.; Bader, R.

2009-12-01

In connection with technological advances in the manufacturing of medical ceramics, a newly developed ceramic femoral component was introduced in total knee arthroplasty (TKA). The motivation to consider ceramics in TKA is based on the allergological and tribological benefits as proven in total hip arthroplasty. Owing to the brittleness and reduced fracture toughness of ceramic materials, the biomechanical performance has to be examined intensely. Apart from standard testing, we calculated the implant performance under different worst case scenarios including malposition, bone defects and stumbling. A finite-element-model was developed to calculate the implant performance in situ. The worst case conditions revealed principal stresses 12.6 times higher during stumbling than during normal gait. Nevertheless, none of the calculated principal stress amounts were above the critical strength of the ceramic material used. The analysis of malposition showed the necessity of exact alignment of the implant components.

Biomechanical behavior of a cemented ceramic knee replacement under worst case scenarios

NASA Astrophysics Data System (ADS)

Kluess, D.; Mittelmeier, W.; Bader, R.

2010-03-01

In connection with technological advances in the manufacturing of medical ceramics, a newly developed ceramic femoral component was introduced in total knee arthroplasty (TKA). The motivation to consider ceramics in TKA is based on the allergological and tribological benefits as proven in total hip arthroplasty. Owing to the brittleness and reduced fracture toughness of ceramic materials, the biomechanical performance has to be examined intensely. Apart from standard testing, we calculated the implant performance under different worst case scenarios including malposition, bone defects and stumbling. A finite-element-model was developed to calculate the implant performance in situ. The worst case conditions revealed principal stresses 12.6 times higher during stumbling than during normal gait. Nevertheless, none of the calculated principal stress amounts were above the critical strength of the ceramic material used. The analysis of malposition showed the necessity of exact alignment of the implant components.

The Influence of Pre-Heated Treatment to Improve Adhesion Bond Coating Strength of Fly Ash Based Geopolymer Ceramic

NASA Astrophysics Data System (ADS)

Jamaludin, L.; Abdullah, M. M. A. B.; Hussin, K.; Kadir, A. Abdul

2018-06-01

The study focus on effect of pre-heated ceramic surface on the adhesion bond strength between geopolymer coating coating and ceramic substrates. Ceramic substrates was pre-heated at different temperature (400 °C, 600 °C, 800 °C and 1000 °C). Fly ash geopolymer coating material potential used to protect surface used in exposure conditions after sintering at high temperature. Fly ash and alkali activator (Al2O3/Na2SiO3) were mixed with 2.0 solids-to-liquid ratios to prepare geopolymer coating material at constant NaOH concentration of 12M. Adhesion test was conducted to determine the adhesion bond between ceramic substrates and fly ash coating material. The results showed the pre-heated ceramic substrates effect the adhesion bond of coating compared with untreated substrates with increasing of strength up to 20 % for temperature 600 °C.

Ceramic material suitable for repair of a space vehicle component in a microgravity and vacuum environment, method of making same, and method of repairing a space vehicle component

NASA Technical Reports Server (NTRS)

Riedell, James A. (Inventor); Easler, Timothy E. (Inventor)

2009-01-01

A precursor of a ceramic adhesive suitable for use in a vacuum, thermal, and microgravity environment. The precursor of the ceramic adhesive includes a silicon-based, preceramic polymer and at least one ceramic powder selected from the group consisting of aluminum oxide, aluminum nitride, boron carbide, boron oxide, boron nitride, hafnium boride, hafnium carbide, hafnium oxide, lithium aluminate, molybdenum silicide, niobium carbide, niobium nitride, silicon boride, silicon carbide, silicon oxide, silicon nitride, tin oxide, tantalum boride, tantalum carbide, tantalum oxide, tantalum nitride, titanium boride, titanium carbide, titanium oxide, titanium nitride, yttrium oxide, zirconium diboride, zirconium carbide, zirconium oxide, and zirconium silicate. Methods of forming the ceramic adhesive and of repairing a substrate in a vacuum and microgravity environment are also disclosed, as is a substrate repaired with the ceramic adhesive.

Effect of soldering on the metal-ceramic bond strength of an Ni-Cr base alloy.

PubMed

Nikellis, Ioannis; Levi, Anna; Zinelis, Spiros

2005-11-01

Although soldering is a common laboratory procedure, the use of soldering alloys may adversely affect metal-ceramic bond strength and potentially decrease the longevity of metal-ceramic restorations. The purpose of this study was to investigate the effect of soldering on metal-ceramic bond strength of a representative Ni-Cr base metal alloy. Twenty-eight rectangular (25 x 3 x 0.5 mm) Ni-based alloy (Wiron 99) specimens were equally divided into soldering (S) and reference (R) groups. Soldering group specimens were covered with a 0.1-mm layer of the appropriate solder (Wiron-Lot) and reduced by 0.1 mm on the opposite side. Five specimens of each group were used for the measurement of surface roughness parameter (R(z)) and hardness, and 3 were used for measurement of the modulus of elasticity. Six specimens of each group were covered with porcelain (Ceramco 3) and subjected to a 3-point bending test for evaluation of the metal-ceramic bond strength according to the ISO 9693 specification. The data from surface roughness, hardness, modulus of elasticity, and metal-ceramic bond strength were analyzed statistically, using independent t tests (alpha=.05). Statistical analysis of the R(z) surface roughness parameter (S: 3.4 +/- 0.3 mum; R: 3.7 +/- 0.7 microm; P=.07) and bond strength (S: 46 +/- 3 MPa; R: 40 +/- 5 MPa; P=.057) failed to reveal any significant difference between the 2 groups. The specimens of the soldering group demonstrated significantly lower values both in hardness (S: 128 +/- 11 VHN; R: 217 +/- 4 VHN; P<.001) and in modulus of elasticity (S: 135 +/- 4 GPa; R: 183 +/- 6 GPa; P=.035) than the reference group. Under the conditions of the present study, the addition of solder to the base metal alloy did not affect the metal-ceramic bond strength.

Structural and Chemical Analysis of the Zirconia-Veneering Ceramic Interface.

PubMed

Inokoshi, M; Yoshihara, K; Nagaoka, N; Nakanishi, M; De Munck, J; Minakuchi, S; Vanmeensel, K; Zhang, F; Yoshida, Y; Vleugels, J; Naert, I; Van Meerbeek, B

2016-01-01

The interfacial interaction of veneering ceramic with zirconia is still not fully understood. This study aimed to characterize morphologically and chemically the zirconia-veneering ceramic interface. Three zirconia-veneering conditions were investigated: 1) zirconia-veneering ceramic fired on sandblasted zirconia, 2) zirconia-veneering ceramic on as-sintered zirconia, and 3) alumina-veneering ceramic (lower coefficient of thermal expansion [CTE]) on as-sintered zirconia. Polished cross-sectioned ceramic-veneered zirconia specimens were examined using field emission gun scanning electron microscopy (Feg-SEM). In addition, argon-ion thinned zirconia-veneering ceramic interface cross sections were examined using scanning transmission electron microscopy (STEM)-energy dispersive X-ray spectrometry (EDS) at high resolution. Finally, the zirconia-veneering ceramic interface was quantitatively analyzed for tetragonal-to-monoclinic phase transformation and residual stress using micro-Raman spectroscopy (µRaman). Feg-SEM revealed tight interfaces for all 3 veneering conditions. High-resolution transmission electron microscopy (HRTEM) disclosed an approximately 1.0-µm transformed zone at sandblasted zirconia, in which distinct zirconia grains were no longer observable. Straight grain boundaries and angular grain corners were detected up to the interface of zirconia- and alumina-veneering ceramic with as-sintered zirconia. EDS mapping disclosed within the zirconia-veneering ceramic a few nanometers thick calcium/aluminum-rich layer, touching the as-sintered zirconia base, with an equally thick silicon-rich/aluminum-poor layer on top. µRaman revealed t-ZrO2-to-m-ZrO2 phase transformation and residual compressive stress at the sandblasted zirconia surface. The difference in CTE between zirconia- and the alumina-veneering ceramic resulted in residual tensile stress within the zirconia immediately adjacent to its interface with the veneering ceramic. The rather minor chemical elemental shifts recorded in the veneering ceramic did not suffice to draw definitive conclusions regarding potential chemical interaction of the veneering ceramic with zirconia. Sandblasting damaged the zirconia surface and induced phase transformation that also resulted in residual compressive stress. Difference in CTE of zirconia versus that of the veneering ceramic resulted in an unfavorable residual tensile stress at the zirconia-veneering ceramic interface. © International & American Associations for Dental Research 2015.

Joining of Silicon Carbide-Based Ceramics for MEMS-LDI Fuel Injector Applications

NASA Technical Reports Server (NTRS)

Halbig, Michael C.; Singh, Mrityunjay

2012-01-01

Deliver the benefits of ceramics in turbine engine applications- increased efficiency, performance, horsepower, range, operating temperature, and payload and reduced cooling and operation and support costs for future engines.

Ceramic hemi-unicondylar arthroplasty in an adolescent patient with idiopathic tibial chondrolysis.

PubMed

Dombroski, Derek; Garino, Jonathan; Lee, Gwo-Chin

2009-06-01

Despite recent advances in cartilage regeneration and restoration procedures, isolated, large, full-thickness cartilage lesions in young patients continue to pose significant challenges to patients and orthopedic surgeons. Treatment options for this difficult problem have traditionally included arthrodesis, osteotomy, osteochondral allograft, and prosthetic reconstruction. We present a case of an adolescent patient with isolated idiopathic lateral tibial chondrolysis treated with a custom ceramic hemi-unicondylar hemiarthroplasty. Preoperatively, a 3-dimensional computed tomography scan of the patient's knee was obtained to begin manufacturing a conforming custom ceramic insert that would articulate between the tibial base plate and the patient's native lateral femoral cartilage. Through a lateral parapatellar approach, the tibial preparation was carried out using the Zimmer M/G unicompartmental knee system (Warsaw, Indiana), and the tibial base plate was cemented into position in the standard fashion. A custom, conforming, prefabricated ceramic insert (CeramTec, Memphis, Tennessee) was then inserted onto the tibial base plate. At 5-year follow-up, this salvage procedure was successful in relieving pain and restoring function in this young patient. There were no signs of implant loosening or lysis. Magnetic resonance imaging of the knee at last follow-up revealed that the cartilage thickness of the patient's lateral femoral condyle remained unchanged. Unicondylar hemiarthroplasty performed in patients with large unipolar lesions in the knee can provide durable and reliable pain relief. Ceramic is a viable material that can be considered for articulation with native cartilage.

Clinical performance of a lithia disilicate-based core ceramic for three-unit posterior FPDs.

PubMed

Esquivel-Upshaw, Josephine F; Anusavice, Kenneth J; Young, Henry; Jones, Jack; Gibbs, Charles

2004-01-01

The purpose of this research project was to determine the clinical success rate of a lithia disilicate-based core ceramic for use in posterior fixed partial dentures (FPD) as a function of bite force, cement type, connector height, and connector width. Thirty ceramic FPD core frameworks were prepared using a heat-pressing technique and a lithia disilicate-based core ceramic. The maximum clenching force was measured for each patient prior to tooth preparation. Connector height and width were measured for each FPD. Patients were recalled yearly after cementation for 2 years and evaluated using 11 clinical criteria. All FPDs were examined by two independent clinicians, and rankings from 1 to 4 were made for each criterion (4 = excellent; 1 = unacceptable). Two of the 30 ceramic FPDs fractured within the 2-year evaluation period, representing a 93% success rate. One fracture was associated with a low occlusal force and short connector height (2.9 mm). The other fracture was associated with the greatest occlusal force (1,031 N) and adequate connector height. All criteria were ranked good to excellent during the 2-year recall for all remaining FPDs. The performance of the experimental core ceramic in posterior FPDs was promising, with only a 7% fracture rate after 2 years. Because of the limited sample size, it is not possible to identify the maximum clenching force that is allowable to prevent fracture caused by interocclusal forces.

Miscellaneous Burial Recovery in Eastern Washington, 1981.

DTIC Science & Technology

1983-01-01

jaws. Specifically, an abscess associated with the maxillary left first premolar was present. The maxillary alveolar structures also exhibited...completely resorbed — evidence of periodontal disease. The general condition of the teeth and the periodontal bone suggests an old individual who

Effects of poling over the orthorhombic-tetragonal phase transition temperature in compositionally homogeneous (K,Na)NbO3-based ceramics

NASA Astrophysics Data System (ADS)

Morozov, M. I.; Kungl, H.; Hoffmann, M. J.

2011-03-01

Li-, Ta-, and Mn-modified (K,Na)NbO3 ceramics with various compositional homogeneity have been prepared by conventional and precursor methods. The homogeneous ceramic has demonstrated a sharper peak in temperature dependent piezoelectric response. The dielectric and piezoelectric properties of the homogeneous ceramics have been characterized at the experimental subcoercive electric fields near the temperature of the orthorhombic-tetragonal phase transition with respect to poling in both phases. Poling in the tetragonal phase is shown to enhance the low-signal dielectric and piezoelectric properties in the orthorhombic phase.

Optoenergy storage and random walks assisted broadband amplification in Er3+-doped (Pb,La)(Zr,Ti)O3 disordered ceramics.

PubMed

Xu, Long; Zhao, Hua; Xu, Caixia; Zhang, Siqi; Zou, Yingyin K; Zhang, Jingwen

2014-02-01

A broadband optical amplification was observed and investigated in Er3+-doped electrostrictive ceramics of lanthanum-modified lead zirconate titanate under a corona atmosphere. The ceramic structure change caused by UV light, electric field, and random walks originated from the diffusive process in intrinsically disordered materials may all contribute to the optical amplification and the associated energy storage. Discussion based on optical energy storage and diffusive equations was given to explain the findings. Those experiments performed made it possible to study random walks and optical amplification in transparent ceramics materials.

Development of highly porous scaffolds based on bioactive silicates for dental tissue engineering

DOE Office of Scientific and Technical Information (OSTI.GOV)

Goudouri, O.M., E-mail: menti.goudouri@ww.uni-erlangen.de; Department of Physics, Aristotle University of Thessaloniki, 54124 Thessaloniki; Theodosoglou, E.

Graphical abstract: - Highlights: • Synthesis of an Mg-based glass-ceramic via the sol–gel technique. • The heat treatment of the glass-ceramic promoted the crystallization of akermanite. • Akermanite scaffolds coated with gelatin were successfully fabricated. • An HCAp layer was developed on the surface of all scaffolds after 9 days in SBF. - Abstract: Various scaffolding materials, ceramics and especially Mg-based ceramic materials, including akermanite (Ca{sub 2}MgSi{sub 2}O{sub 7}) and diopside (CaMgSi{sub 2}O{sub 6}), have attracted interest for dental tissue regeneration because of their improved mechanical properties and controllable biodegradation. The aim of the present work was the synthesis ofmore » an Mg-based glass-ceramic, which would be used for the construction of workable akermanite scaffolds. The characterization of the synthesized material was performed by Fourier Transform Infrared Spectroscopy (FTIR) X-Ray Diffractometry (XRD) and Scanning Electron Microscopy (SEM). Finally, the apatite forming ability of the scaffolds was assessed by immersion in simulated body fluid. The scaffolds were fabricated by the foam replica technique and were subsequently coated with gelatin to provide a functional surface for increased cell attachment. Finally, SEM microphotographs and FTIR spectra of the scaffolds after immersion in SBF solution indicated the inorganic bioactive character of the scaffolds suitable for the intended applications in dental tissue engineering.« less

Inverted electro-mechanical behaviour induced by the irreversible domain configuration transformation in (K,Na)NbO3-based ceramics

PubMed Central

Huan, Yu; Wang, Xiaohui; Koruza, Jurij; Wang, Ke; Webber, Kyle G.; Hao, Yanan; Li, Longtu

2016-01-01

Miniaturization of domains to the nanometer scale has been previously reported in many piezoelectrics with two-phase coexistence. Despite the observation of nanoscale domain configuration near the polymorphic phase transition (PPT) regionin virgin (K0.5Na0.5)NbO3 (KNN) based ceramics, it remains unclear how this domain state responds to external loads and influences the macroscopic electro-mechanical properties. To this end, the electric-field-induced and stress-induced strain curves of KNN-based ceramics over a wide compositional range across PPT were characterized. It was found that the coercive field of the virgin samples was highest in PPT region, which was related to the inhibited domain wall motion due to the presence of nanodomains. However, the coercive field was found to be the lowest in the PPT region after electrical poling. This was related to the irreversible transformation of the nanodomains into micron-sized domains during the poling process. With the similar micron-sized domain configuration for all poled ceramics, the domains in the PPT region move more easily due to the additional polarization vectors. The results demonstrate that the poling process can give rise to the irreversible domain configuration transformation and then account for the inverted macroscopic piezoelectricity in the PPT region of KNN-based ceramics. PMID:26915972

Effect of zircon-based tricolor pigments on the color, microstructure, flexural strength and translucency of a novel dental lithium disilicate glass-ceramic.

PubMed

Yuan, Kun; Wang, Fu; Gao, Jing; Sun, Xiang; Deng, Zai-Xi; Wang, Hui; Jin, Lei; Chen, Ji-Hua

2014-01-01

The purpose of this study was to investigate the effect of zircon-based tricolor pigments (praseodymium zircon yellow, ferrum zircon red, and vanadium zircon blue) on the color, thermal property, crystalline phase composition, microstructure, flexural strength, and translucency of a novel dental lithium disilicate glass-ceramic. The pigments were added to the glass frit, milled, pressed, and sintered. Ninety monochrome samples were prepared and the colors were analyzed. The effect of the pigments on thermal property, crystalline phase composition, and microstructure were determined by differential scanning calorimetry (DSC), X-ray diffraction (XRD), and scanning electron microscopy (SEM), respectively. Addition of the pigments resulted in the acquisition of subtractive primary colors as well as tooth-like colors, and did not demonstrate significant effects on the thermal property, crystalline phase composition, microstructure, and flexural strength of the experimental glass-ceramic. Although significant differences (p < 0.01) were observed between the translucencies of the uncolored and 1.0 wt % zircon-based pigment colored ceramics, the translucencies of the latter were sufficient to fabricate dental restorations. These results indicate that the zircon-based tricolor pigments can be used with dental lithium disilicate glass-ceramic to produce abundant and predictable tooth-like colors without significant adverse effects, if mixed in the right proportions. Copyright © 2013 Wiley Periodicals, Inc.

The effect of variation in physical properties of porous bioactive glass on the expression and maintenance of the osteoblastic phenotype

NASA Astrophysics Data System (ADS)

Effah Kaufmann, Elsie Akosua Biraa

Revision surgery to replace failed hip implants is a significant health care issue that is expected to escalate as life expectancy increases. A major goal of revision surgery is to reconstruct femoral intramedullary bone-stock loss. To address this problem of bone loss, grafting techniques are widely used. Although fresh autografts remain the optimal material for all forms of surgery seeking to restore structural integrity to the skeleton, it is evident that the supply of such tissue is limited. In recent years, calcium phosphate ceramics have been studied as alternatives to autografts and allografts. The significant limitations associated with the use of biological and synthetic grafts have led to a growing interest in the in vitro synthesis of bone tissue. The approach is to synthesize bone tissue in vitro with the patient's own cells, and use this tissue for the repair of bony defects. Various substrates including metals, polymers, calcium phosphate ceramics and bioactive glasses, have been seeded with osteogenic cells. The selection of bioactive glass in this study is based on the fact that this material has shown an intense beneficial biological effect which has not been reproduced by other biomaterials. Even though the literature provides extensive data on the effect of pore size and porosity on in vivo bone tissue ingrowth into porous materials for joint prosthesis fixation, the data from past studies cannot be applied to the use of bioactive glass as a substrate for the in vitro synthesis of bone tissue. First, unlike the in vivo studies in the literature, this research deals with the growth of bone tissue in vitro. Second, unlike the implants used in past studies, bioactive glass is a degradable and resorbable material. Thus, in order to establish optimal substrate characteristics (porosity and pore size) for bioactive glass, it was important to study these parameters in an in vitro model. We synthesized porous bioactive glass substrates (BG) with varying pore sizes and porosity and determined the effect of substrate properties on the expression and maintenance of the osteoblastic phenotype, using an in vitro culture of osteoblast-like cells. Our data showed that porous bioactive glass substrates support the proliferation and maturation of osteoblast-like cells. Within the conditions of the experiment, we also found that at a given porosity of 44% the pore size of bioactive glass neither directs nor modulates the in vitro expression of the osteoblastic phenotype. On the other hand, at an average pore size of 92 mum, when cultures are maintained for 14 days, cell activity is greatly affected by the substrate porosity. As the porosity increases from 35% to 59%, osteoblast activity is adversely affected. (Abstract shortened by UMI.)

Current concepts review: Fractures of the patella

PubMed Central

Gwinner, Clemens; Märdian, Sven; Schwabe, Philipp; Schaser, Klaus-D.; Krapohl, Björn Dirk; Jung, Tobias M.

2016-01-01

Fractures of the patella account for about 1% of all skeletal injuries and can lead to profound impairment due to its crucial function in the extensor mechanism of the knee. Diagnosis is based on the injury mechanism, physical examination and radiological findings. While the clinical diagnosis is often distinct, there are numerous treatment options available. The type of treatment as well as the optimum timing of surgical intervention depends on the underlying fracture type, the associated soft tissue damage, patient factors (i.e. age, bone quality, activity level and compliance) and the stability of the extensor mechanism. Regardless of the treatment method an early rehabilitation is recommended in order to avoid contractures of the knee joint capsule and cartilage degeneration. For non-displaced and dislocated non-comminuted transverse patellar fractures (2-part) modified anterior tension band wiring is the treatment of choice and can be combined – due to its biomechanical superiority – with cannulated screw fixation. In severe comminuted fractures, open reduction and fixation with small fragment screws or new angular stable plates for anatomic restoration of the retropatellar surface and extension mechanism results in best outcome. Additional circular cerclage wiring using either typical metal cerclage wires or resorbable PDS/non-resorbable FiberWires increases fixation stability and decreases risk for re-dislocation. Distal avulsion fractures should be fixed with small fragment screws and should be protected by a transtibial McLaughlin cerclage. Partial or complete patellectomy should be regarded only as a very rare salvage operation due to its severe functional impairment. PMID:26816667

Dependences of microstructure on electromagnetic interference shielding properties of nano-layered Ti3AlC2 ceramics.

PubMed

Tan, Yongqiang; Luo, Heng; Zhou, Xiaosong; Peng, Shuming; Zhang, Haibin

2018-05-21

The microstructure dependent electromagnetic interference (EMI) shielding properties of nano-layered Ti 3 AlC 2 ceramics were presented in this study by comparing the shielding properties of various Ti 3 AlC 2 ceramics with distinct microstructures. Results indicate that Ti 3 AlC 2 ceramics with dense microstructure and coarse grains are more favourable for superior EMI shielding efficiency. High EMI shielding effectiveness over 40 dB at the whole Ku-band frequency range was achieved in Ti 3 AlC 2 ceramics by microstructure optimization, and the high shielding effectiveness were well maintained up to 600 °C. A further investigation reveals that only the absorption loss displays variations upon modifying microstructure by allowing more extensive multiple reflections in coarse layered grains. Moreover, the absorption loss of Ti 3 AlC 2 was found to be much higher than those of highly conductive TiC ceramics without layered structure. These results demonstrate that nano-layered MAX phase ceramics are promising candidates of high-temperature structural EMI shielding materials and provide insightful suggestions for achieving high EMI shielding efficiency in other ceramic-based shielding materials.

Zirconia in fixed prosthesis. A literature review

PubMed Central

Román-Rodríguez, Juan L.; Ferreiroa, Alberto; Solá-Ruíz, María F.; Fons-Font, Antonio

2014-01-01

Statement of problem: Evidence is limited on the efficacy of zirconia-based fixed dental prostheses. Objective: To carry out a literature review of the behavior of zirconium oxide dental restorations. Material and Methods: This literature review searched the Pubmed, Scopus, Medline and Cochrane Library databases using key search words “zirconium oxide,” “zirconia,” “non-metal restorations,” “ceramic oxides,” “veneering ceramic,” “zirconia-based fixed dental prostheses”. Both in vivo and in vitro studies into zirconia-based prosthodontic restoration behavior were included. Results: Clinical studies have revealed a high rate of fracture for porcelain-veneered zirconia-based restorations that varies between 6% and 15% over a 3- to 5-year period, while for ceramo-metallic restorations the fracture rate ranges between 4 and 10% over ten years. These results provoke uncertainty as to the long-term prognosis for this material in the oral medium. The cause of veneering porcelain fractures is unknown but hypothetically they could be associated with bond failure between the veneer material and the zirconia sub-structure. Key words:Veneering ceramic, zirconia-based ceramic restoration, crown, zirconia, tooth-supported fixed prosthesis. PMID:24596638

Different effects of a novel CaO-MgO-SiO₂-based multiphase glass-ceramic on cell behaviors of normal and cancer cells in vitro.

PubMed

Zhang, Mengjiao; Chen, Xianchun; Pu, Ximing; Liao, Xiaoming; Huang, Zhongbing; Yin, Guangfu

2014-04-01

The effects in vitro of a novel multiphase glass-ceramic (with nominal composition of 43.19% CaO, 7.68% MgO, and 49.13% SiO2 in weight percent) on cell adhesion, proliferation, differentiation and ultrastructure of human osteosarcoma cell line MG63, mouse fibroblasts L929, and human lung adenocarcinoma epithelial cell line A549 were investigated in this research. Scanning electron microscopy (SEM) micrographs revealed that the surface morphology of this glass-ceramic was beneficial to cell adhesion. The glass-ceramic extracts at certain concentrations could stimulate the proliferation and differentiation of MG63 and L929 cells, whereas inhibit A549 proliferation, which might be resulted from the released Si ions. In addition, when cultured with 0.1mg/mL glass-ceramic powder suspension, the cell ultrastructure of MG63 showed abundant organelles and L929 displayed the phenomena of cellular stress response. While more interestingly, A549 exhibited chromatin condensation, mitochondria swell and RER expansion, which was presumed to be early signs of apoptosis. These results suggest that this novel CaO-MgO-SiO2-based multiphase glass-ceramic has potential for bone regeneration and tissue engineering applications. Copyright © 2013 Elsevier B.V. All rights reserved.

A-Site (MCe) Substitution Effects on the Structures and Properties of CaBi4Ti4O15 Ceramics

NASA Astrophysics Data System (ADS)

Yan, Haixue; Li, Chengen; Zhou, Jiaguang; Zhu, Weimin; He, Lianxin; Song, Yuxin

2000-11-01

We investigated the effect of A-site compound substitution on the structures and properties of Ca0.8(MCe)0.1Bi4Ti4O15 (M denotes Li, Na and K) ceramics. The samples were prepared by the conventional ceramic technique. Sintering characteristics of Ca0.8(MCe)0.1Bi4Ti4O15 and CaBi4Ti4O15 ceramics were discussed. X-ray powder diffraction patterns of the three modified CBT-based compounds show a single phase of bismuth oxide layer type structure with m=4. The hysteresis loops of polarization versus electric field of the four compounds were also measured. A-site compound substitution improves the piezoelectric properties and the high-temperature resistivity of these materials. A-site (LiCe) and (KCe) substitution not only improves the Curie temperature but also decreases the temperature coefficient of dielectric constant (TK\\varepsilon). Among the three modified ceramics, only the Curie temperature of Ca0.8(NaCe)0.1Bi4Ti4O15 is lower than that of CaBi4Ti4O15; however, its TK\\varepsilon is the lowest. As a result, all the three modified CBT-based ceramics were found to be excellent high-temperature piezoelectric materials.

[Preparation of porous ceramics based on waste ceramics and its Ni2+ adsorption characteristics].

PubMed

Zhang, Yong-Li; Wang, Cheng-Zhi; Shi, Ce; Shang, Ling-Ling; Ma, Rui; Dong, Wan-Li

2013-07-01

The preparation conditions of porous ceramics were determined by SEM, XRD and FT-IR characterizations as well as the nickel removal ability of porous ceramics to be: the mass fraction w of sesbania powder doped was 4%, and the calcination temperature was 800 degrees C. SEM and pore structure characterization illustrated that calcination caused changes in the structure and morphology of waste ceramics. With the increase of calcination temperature, the specific surface area and pore volume decreased, while the aperture increased. EDS analyses showed that the main elements of both the original waste porcelain powder and the porous ceramics were Si, Al and O. The SEM, XRD and FT-IR characterization of porous ceramics illustrated that the structure of porous ceramics was stable before and after adsorption. The series of experiments of Ni2+ adsorption using these porous ceramics showed that when the dosage of porous ceramics was 10 g x L(-1), the adsorption time was 60 min, the pH value was 6.32, and the concentration of nickel-containing wastewater was below 100 mg x L(-1), the Ni2+ removal of wastewater reached 89.7%. Besides, the porous ceramics showed higher removal efficiency on nickel in the wastewater. The Ni(2+)-containing wastewater was processed by the porous ceramics prepared, and the adsorption dynamics and adsorption isotherms of Ni2+ in wastewater by porous ceramics were investigated. The research results showed that the Ni2+ adsorption process of porous ceramics was in accordance with the quasi second-order kinetic model (R2 = 0.999 9), with Q(e) of 9.09 mg x g(-1). The adsorption process can be described by the Freundlich equation and Langmuir equation, and when the temperature increased from 20 degrees C to 40 degrees C, the maximum adsorption capacity Q(m) increased from 14.49 mg x g(-1) to 15.38 mg x g(-1).

Fracture behaviors of ceramic tissue scaffolds for load bearing applications

NASA Astrophysics Data System (ADS)

Entezari, Ali; Roohani-Esfahani, Seyed-Iman; Zhang, Zhongpu; Zreiqat, Hala; Dunstan, Colin R.; Li, Qing

2016-07-01

Healing large bone defects, especially in weight-bearing locations, remains a challenge using available synthetic ceramic scaffolds. Manufactured as a scaffold using 3D printing technology, Sr-HT-Gahnite at high porosity (66%) had demonstrated significantly improved compressive strength (53 ± 9 MPa) and toughness. Nevertheless, the main concern of ceramic scaffolds in general remains to be their inherent brittleness and low fracture strength in load bearing applications. Therefore, it is crucial to establish a robust numerical framework for predicting fracture strengths of such scaffolds. Since crack initiation and propagation plays a critical role on the fracture strength of ceramic structures, we employed extended finite element method (XFEM) to predict fracture behaviors of Sr-HT-Gahnite scaffolds. The correlation between experimental and numerical results proved the superiority of XFEM for quantifying fracture strength of scaffolds over conventional FEM. In addition to computer aided design (CAD) based modeling analyses, XFEM was conducted on micro-computed tomography (μCT) based models for fabricated scaffolds, which took into account the geometric variations induced by the fabrication process. Fracture strengths and crack paths predicted by the μCT-based XFEM analyses correlated well with relevant experimental results. The study provided an effective means for the prediction of fracture strength of porous ceramic structures, thereby facilitating design optimization of scaffolds.

Durability and Design Issues of Thermal/environmental Barrier Coatings on Sic/sic Ceramic Matrix Composites Under 1650 C Test Conditions

NASA Technical Reports Server (NTRS)

Zhu, Dong-Ming; Choi, Sung R.; Ghosn, Louis J.; Miller, Robert A.

2004-01-01

Ceramic thermal/environmental barrier coatings for SiC-based ceramics will play an increasingly important role in future gas turbine engines because of their ability to effectively protect the engine components and further raise engine temperatures. However, the coating durability remains a major concern with the ever-increasing temperature requirements. Currently, advanced T/EBC systems, which typically include a high temperature capable zirconia- (or hahia-) based oxide top coat (thermal barrier) on a less temperature capable mullite/barium-strontium-aluminosilicate (BSAS)/Si inner coat (environmental barrier), are being developed and tested for higher temperature capability Sic combustor applications. In this paper, durability of several thermal/environmental barrier coating systems on SiC/SiC ceramic matrix composites was investigated under laser simulated engine thermal gradient cyclic, and 1650 C (3000 F) test conditions. The coating cracking and delamination processes were monitored and evaluated. The effects of temperature gradients and coating configurations on the ceramic coating crack initiation and propagation were analyzed using finite element analysis (FEA) models based on the observed failure mechanisms, in conjunction with mechanical testing results. The environmental effects on the coating durability will be discussed. The coating design approach will also be presented.

Facial fractures in children.

PubMed

Boyette, Jennings R

2014-10-01

Facial trauma in children differs from adults. The growing facial skeleton presents several challenges to the reconstructive surgeon. A thorough understanding of the patterns of facial growth and development is needed to form an individualized treatment strategy. A proper diagnosis must be made and treatment options weighed against the risk of causing further harm to facial development. This article focuses on the management of facial fractures in children. Discussed are common fracture patterns based on the development of the facial structure, initial management, diagnostic strategies, new concepts and old controversies regarding radiologic examinations, conservative versus operative intervention, risks of growth impairment, and resorbable fixation. Copyright © 2014 Elsevier Inc. All rights reserved.

Processing of polysiloxane-derived porous ceramics: a review

PubMed Central

Manoj Kumar, B V; Kim, Young-Wook

2010-01-01

Because of the unique combination of their attractive properties, porous ceramics are considered as candidate materials for several engineering applications. The production of porous ceramics from polysiloxane precursors offers advantages in terms of simple processing methodology, low processing cost, and easy control over porosity and other properties of the resultant ceramics. Therefore, considerable research has been conducted to produce various Si(O)C-based ceramics from polysiloxane precursors by employing different processing strategies. The complete potential of these materials can only be achieved when properties are tailored for a specific application, whereas the control over these properties is highly dependent on the processing route. This review deals with processing strategies of polysiloxane-derived porous ceramics. The essential features of processing strategies—replica, sacrificial template, direct foaming and reaction techniques—are explained and the available literature reports are thoroughly reviewed with particular regard to the critical issues that affect pore characteristics. A short note on the cross-linking methods of polysiloxanes is also provided. The potential of each processing strategy on porosity and strength of the resultant SiC or SiOC ceramics is outlined. PMID:27877344

Design and characterization of Yb and Nd doped transparent ceramics for high power laser applications: recent advancements

NASA Astrophysics Data System (ADS)

Lapucci, A.; Vannini, M.; Ciofini, M.; Pirri, A.; Nikl, M.; Li, J.; Esposito, L.; Biasini, V.; Hostasa, J.; Goto, T.; Boulon, G.; Maksimov, R.; Gizzi, L.; Labate, L.; Toci, G.

2017-01-01

We report a review on our recent developments in Yttebium and Neodymium doped laser ceramics, along two main research lines. The first is the design and development of Yb:YAG ceramics with non uniform doping distribution, for the management of thermo-mechanical stresses and for the mitigation of ASE: layered structures have been produced by solid state reactive sintering, using different forming processes (spray drying and cold press of the homogenized powders, tape cast of the slurry); samples have been characterized and compared to FEM analysis. The second is the investigation of Lutetium based ceramics (such as mixed garnets LuYAG and Lu2O3); this interest is mainly motivated by the favorable thermal properties of these hosts under high doping. We recently obtained for the first time high efficiency laser emission from Yb doped LuYAG ceramics. The investigation on sesquioxides has been focused on Nddoped Lu2O3 ceramics, fabricated with the Spark Plasma Sintering method (SPS). We recently achieved the first laser emission above 1 W from Nd doped Lu2O3 ceramics fabricated by SPS.

Nanoceramics for blood-borne virus removal.

PubMed

Zhao, Yufeng; Sugiyama, Sadahiro; Miller, Thomas; Miao, Xigeng

2008-05-01

The development of nanoscience and nanotechnology in the field of ceramics has brought new opportunities for the development of virus-removal techniques. A number of nanoceramics, including nanostructured alumina, titania and zirconia, have been introduced for the applications in virus removal or separation. Filtration or adsorption of viruses, and thus the removal of viruses through nanoceramics, such as nanoporous/mesoporous ceramic membranes, ceramic nanofibers and ceramic nanoparticles, will make it possible to produce an efficient system for virus removal from blood and one with excellent chemical/thermal stability. Currently, nanoceramic membranes and filters based on sol-gel alumina membranes and NanoCeram nanofiber filters have been commercialized and applied to remove viruses from the blood. Nevertheless, filtration using nanoporous filters is limited to the removal of only free viruses in the bloodstream.

Are PEEK-on-Ceramic Bearings an Option for Total Disc Arthroplasty? An In Vitro Tribology Study.

PubMed

Siskey, Ryan; Ciccarelli, Lauren; Lui, Melissa K C; Kurtz, Steven M

2016-11-01

Most contemporary total disc replacements (TDRs) use conventional orthopaedic bearing couples such as ultrahigh-molecular-weight polyethylene (polyethylene) and cobalt-chromium (CoCr). Cervical total disc replacements incorporating polyetheretherketone (PEEK) bearings (specifically PEEK-on-PEEK bearings) have been previously investigated, but little is known about PEEK-on-ceramic bearings for TDR. (1) What is the tribologic behavior of a PEEK-on-ceramic bearing for cervical TDR under idealized, clean wear test conditions? (2) How does the PEEK-on-ceramic design perform under impingement conditions? (3) How is the PEEK-on-ceramic bearing affected by abrasive wear? (4) Is the particle morphology from PEEK-on-ceramic bearings for TDRs affected by adverse wear scenarios? PEEK-on-ceramic cervical TDR bearings were subjected to a 10 million cycle ideal wear test based on ASTM F2423 and ISO 181912-1 using a six-station spine wear simulator (MTS, Eden Prairie, MN, USA) with 5 g/L bovine serum concentration at 23° ± 2° C (ambient temperature). Validated 1 million cycle impingement and 5 million cycle abrasive tests were conducted on the PEEK-on-ceramic bearings based, in part, on retrieval analysis of a comparable bearing design as well as finite element analyses. The ceramic-on-PEEK couple was characterized for damage modes, mass and volume loss, and penetration and the lubricant was subjected to particle analysis. The resulting mass wear rate, volumetric wear rate, based on material density, and particle analysis were compared with clinically available cervical disc bearing couples. The three modes of wear (idealized, impingement, and abrasive) resulted in mean mass wear rates of 0.9 ± 0.2 mg/MC, 1.9 ± 0.5 mg/MC, and 2.8 ± 0.6 mg/MC, respectively. The mass wear rates were converted to volumetric wear rates using density and found to be 0.7 ± 0.1 mm 3 /MC, 1.5 ± 0.4 mm 3 /MC, and 2.1 ± 0.5 mm 3 /MC, respectively. During each test, the PEEK endplates were the primary sources of wear and demonstrated an abrasive wear mechanism. Under idealized and impingement conditions, the ceramic core also demonstrated slight polishing of the articulating surface but the change in mass was unmeasurable. During abrasive testing, the titanium transfer on the core was shown to polish over 5 MC of testing. In all cases and consistent with previous studies of other PEEK bearing couples, the particle size was primarily < 2 µm and morphology was smooth and spheroidal. Overall, the idealized PEEK-on-ceramic wear rate (0.7 ± 0.1 mm 3 /MC) appears comparable to the published wear rates for other polymer-on-hard bearing couples (0.3-6.7 mm 3 /MC) and within the range of 0.2 to 1.9 mm 3 /MC reported for PEEK-on-PEEK cervical disc designs. The particles, based on size and morphology, also suggest the wear mechanism is comparable between the PEEK-on-ceramic couple and other polymer-on-ceramic orthopaedic couples. The PEEK-on-ceramic bearing considered in this study is a novel bearing couple for use in total disc arthroplasty devices and will require clinical evaluation to fully assess the bearing couple and total disc design. However, the wear rates under idealized and adverse conditions, and particle size and morphology, suggest that PEEK-on-ceramic bearings may be a reasonable alternative to polyethylene-on-CoCr and metal-on-metal bearings currently used in cervical TDRs.

Heat transfer fluids containing nanoparticles

DOEpatents

Singh, Dileep; Routbort, Jules; Routbort, A.J.; Yu, Wenhua; Timofeeva, Elena; Smith, David S.; France, David M.

2016-05-17

A nanofluid of a base heat transfer fluid and a plurality of ceramic nanoparticles suspended throughout the base heat transfer fluid applicable to commercial and industrial heat transfer applications. The nanofluid is stable, non-reactive and exhibits enhanced heat transfer properties relative to the base heat transfer fluid, with only minimal increases in pumping power required relative to the base heat transfer fluid. In a particular embodiment, the plurality of ceramic nanoparticles comprise silicon carbide and the base heat transfer fluid comprises water and water and ethylene glycol mixtures.

Ceramic Coatings for Clad (The C 3 Project): Advanced Accident-Tolerant Ceramic Coatings for Zr-Alloy Cladding

DOE Office of Scientific and Technical Information (OSTI.GOV)

Sickafus, Kurt E.; Wirth, Brian; Miller, Larry

The goal of this NEUP-IRP project is to develop a fuel concept based on an advanced ceramic coating for Zr-alloy cladding. The coated cladding must exhibit demonstrably improved performance compared to conventional Zr-alloy clad in the following respects: During normal service, the ceramic coating should decrease cladding oxidation and hydrogen pickup (the latter leads to hydriding and embrittlement). During a reactor transient (e.g., a loss of coolant accident), the ceramic coating must minimize or at least significantly delay oxidation of the Zr-alloy cladding, thus reducing the amount of hydrogen generated and the oxygen ingress into the cladding. The specific objectivesmore » of this project are as follows: To produce durable ceramic coatings on Zr-alloy clad using two possible routes: (i) MAX phase ceramic coatings or similar nitride or carbide coatings; and (ii) graded interface architecture (multilayer) ceramic coatings, using, for instance, an oxide such as yttria-stabilized zirconia (YSZ) as the outer protective layer. To characterize the structural and physical properties of the coated clad samples produced in 1. above, especially the corrosion properties under simulated normal and transient reactor operating conditions. To perform computational analyses to assess the effects of such coatings on fuel performance and reactor neutronics, and to perform fuel cycle analyses to assess the economic viability of modifying conventional Zr-alloy cladding with ceramic coatings. This project meets a number of the goals outlined in the NEUP-IRP call for proposals, including: Improve the fuel/cladding system through innovative designs (e.g. coatings/liners for zirconium-based cladding) Reduce or eliminate hydrogen generation Increase resistance to bulk steam oxidation Achievement of our goals and objectives, as defined above, will lead to safer light-water reactor (LWR) nuclear fuel assemblies, due to improved cladding properties and built-in accident resistance, as well as the possibilities for enhanced fuel/clad system performance and longevity.« less

[Study on high strength mica-based machinable glass-ceramic].

PubMed

Li, Hong; Ran, Junguo; Gou, Li; Wang, Fanghu

2004-02-01

The phase constitution, microstructure and properties of a new type of machinable glass-ceramics containing fluorophlogopite-type (FPT) Ca-mica for used in restorative dentistry were investigated. According to the results of X-ray diffraction (XRD) and energy-dispersive spectrometry(EDS), its main crystalline phases were FPT Ca-mica and t-ZrO2, together with few KxCa(1-x)/2Mg2Si4O10F2, m-ZrO2. The flexible strength was 235 MPa, which was nearly two times larger than that of the present mica-based dental materials, and the highest fracture toughness was 2.17 MPa.m1/2. The microstructure had a great effect on properties, the glass-ceramics contained a large volume, and the fine crystals showed higher strength. The material possessed typical microstructure of machinable glass-ceramics and displayed excellent machinability during drilling test and CAD/CAM.

Microscopical and functional aspects of calcium-transport and deposition in terrestrial isopods.

PubMed

Ziegler, Andreas; Fabritius, Helge; Hagedorn, Monica

2005-01-01

Terrestrial isopods (Crustacea) are excellent model organisms to study epithelial calcium-transport and the regulation of biomineralization processes. They molt frequently and resorb cuticular CaCO(3) before the molt to prevent excessive loss of Ca(2+) ions when the old cuticle is shed. The resorbed mineral is stored in CaCO(3) deposits within the ecdysial gap of the first four anterior sternites. After the molt, the deposits are quickly resorbed to mineralise the posterior part of the new cuticle. The deposits contain numerous small spherules composed of an organic matrix and amorphous CaCO(3), which has a high solubility and, therefore, facilitates quick mobilization of Ca(2+) and HCO(3)(-) ions. During the formation and resorption of the deposits large amounts of Ca(2+), HCO(3)(-) and H(+) are transported across the anterior sternal epithelial cells. Within the last years, various light and electron microscopical techniques have been used to characterize the CaCO(3) deposits and the cellular mechanisms involved in biomineralization. The work on the CaCO(3) deposits includes studies on the ultrastructure of the deposits, the sequence of events during deposit formation and dissolution, and the mineral composition of the sternal deposits. The differentiation of the anterior sternal epithelial cells and the mechanisms of epithelial ion transport required for the mineralization and demineralisation of the deposits was studied using various analytical light and electron microscopical techniques including polarized light microscopy, immunocytochemistry, electron microprobe analysis, electron energy loss spectroscopy and electron spectroscopic imaging. Comparative analysis of deposit morphology and the differentiation of the sternal epithelia provide information on the evolution of CaCO(3) deposit formation in relation to the degree of adaptation to terrestrial environments.

Vertical ridge augmentation with autogenous bone grafts 3 years after loading: resorbable barriers versus titanium-reinforced barriers. A randomized controlled clinical trial.

PubMed

Merli, Mauro; Lombardini, Francesco; Esposito, Marco

2010-01-01

To compare the efficacy of two different techniques for vertical bone regeneration at implant placement with particulated autogenous bone at 3 years after loading: resorbable collagen barriers supported by osteosynthesis plates and nonresorbable titanium-reinforced expanded polytetrafluoroethylene barriers. Twenty-two partially edentulous patients requiring vertical bone augmentation were randomly allocated to two treatment groups, each composed of 11 patients. Prosthetic and implant failures, complications, the amount of vertically regenerated bone, and peri-implant marginal bone levels were recorded by independent and blinded assessors. The implant site requiring the most vertical bone regeneration was selected in each patient for bone level assessment. The follow-up time ranged from provisional loading to 3 years after loading. Analysis of covariance and paired t tests were conducted to compare means at the .05 level of significance. No patient dropped out or was excluded at the 3-year follow-up. No prosthetic failures and no implant failures or complications occurred after loading. There was no statistically significant difference in bone loss between the two groups at either 1 year or 3 years. Both groups had gradually lost a statistically significant amount of peri-implant bone at 1 and 3 years (P < .05). After 3 years, patients treated with resorbable barriers had lost a mean of 0.55 mm of bone; patients who had received nonresorbable barriers showed a mean of 0.53 mm of bone loss. Up to 3 years after implant loading, no failures or complications occurred and peri-implant marginal bone loss was minimal. Vertically regenerated bone can be successfully maintained after functional loading.

Refixation of Osteochondral Fractures by an Ultrasound-Activated Pin System - An Ovine In Vivo Examination Using CT and Scanning Electron Microscope.

PubMed

H, Neumann; A P, Schulz; S, Breer; A, Unger; B, Kienast

2015-01-01

Osteochondral injuries, if not treated appropriately, often lead to severe osteoarthritis of the affected joint. Without refixation of the osteochondral fragment, human cartilage only repairs these defects imperfectly. All existing refixation systems for chondral defects have disadvantages, for instance bad MRI quality in the postoperative follow-up or low anchoring forces. To address the problem of reduced stability in resorbable implants, ultrasound-activated pins were developed. By ultrasound-activated melting of the tip of these implants a higher anchoring is assumed. Aim of the study was to investigate, if ultrasound-activated pins can provide a secure refixation of osteochondral fractures comparing to conventional screw and conventional, resorbable pin osteosynthesis. CT scans and scanning electron microscopy should proovegood refixation results with no further tissue damage by the melting of the ultrasound-activated pins in comparison to conventional osteosynthesis. Femoral osteochondral fragments in sheep were refixated with ultrasound-activated pins (SonicPin™), Ethipins(®) and screws (Asnis™). The quality of the refixated fragments was examined after three month of full weight bearing by CT scans and scanning electron microscopy of the cartilage surface. The CT examination found almost no statistically significant difference in the quality of refixation between the three different implants used. Concerning the CT morphology, ultrasound-activated pins demonstrated at least the same quality in refixation of osteochondral fragments as conventional resorbable pins or screws. The scanning electron microscopy showed no major surface damage by the three implants, especially any postulated cartilage damage induced by the heat of the ultrasound-activated pin. The screws protruded above the cartilage surface, which may affect the opposingtibial surface. Using CT scans and scanning electron microscopy, the SonicPin™, the Ethipin(®) and screws were at least equivalent in refixation quality of osteochondral fragments.

Application of biodegradable plates for treating pediatric mandibular fractures.

PubMed

An, Jingang; Jia, Pengcheng; Zhang, Yi; Gong, Xi; Han, Xiaodong; He, Yang

2015-05-01

We assessed the clinical results of a biodegradable plate system for the internal fixation of mandibular fractures in children, and observed the imaging features of fracture healing and bone changes around the biodegradable plates and screws during follow-up. We enrolled 39 patients (22 male, 17 female, average age 4 years 10 months) with different mandibular fractures. We used 2.0-mm resorbable plates to repair the fractures. Postoperative follow-up ranged from 6 months to 5 years; average follow-up was 1 year 2 months. The outcome measures identified and assessed included facial symmetry, mouth opening, occlusal relationship, infection, nonunion, malunion, and plate dehiscence. We fixed 42 fractures with 43 resorbable plates; the fracture site of one patient (aged 11 years 3 months) was fixed with two plates. Two patients developed small fistulas at the intraoral incision 2 months after surgery; the fistulas healed after 1 month without special treatment. In the other patients, the incision healed well, there was facial symmetry, mouth opening was >35 mm, and occlusion was good. Follow-up computed tomography examination data were available for 20 cases, and revealed different degrees of radiolucency indicating that osteolysis had occurred. Radiolucency was observed around the resorbable plates 1 month after the surgery. The extent and depth of the radiolucent region were obvious within 1 year of surgery. In the second year, there were obvious repairs, with the bony defect areas becoming shallower. After 2 years, the bony defect areas had almost disappeared. Biodegradable fixation devices are safe and efficient for treating pediatric mandibular fractures. Osteolysis commonly follows biodegradable fixation of pediatric mandibular fractures, and has no adverse effect on fracture healing. Copyright © 2015 European Association for Cranio-Maxillo-Facial Surgery. Published by Elsevier Ltd. All rights reserved.

Influence of bone affinity on the skeletal distribution of fluorescently labeled bisphosphonates in vivo.

PubMed

Roelofs, Anke J; Stewart, Charlotte A; Sun, Shuting; Błażewska, Katarzyna M; Kashemirov, Boris A; McKenna, Charles E; Russell, R Graham G; Rogers, Michael J; Lundy, Mark W; Ebetino, Frank H; Coxon, Fraser P

2012-04-01

Bisphosphonates are widely used antiresorptive drugs that bind to calcium. It has become evident that these drugs have differing affinities for bone mineral; however, it is unclear whether such differences affect their distribution on mineral surfaces. In this study, fluorescent conjugates of risedronate, and its lower-affinity analogues deoxy-risedronate and 3-PEHPC, were used to compare the localization of compounds with differing mineral affinities in vivo. Binding to dentine in vitro confirmed differences in mineral binding between compounds, which was influenced predominantly by the characteristics of the parent compound but also by the choice of fluorescent tag. In growing rats, all compounds preferentially bound to forming endocortical as opposed to resorbing periosteal surfaces in cortical bone, 1 day after administration. At resorbing surfaces, lower-affinity compounds showed preferential binding to resorption lacunae, whereas the highest-affinity compound showed more uniform labeling. At forming surfaces, penetration into the mineralizing osteoid was found to inversely correlate with mineral affinity. These differences in distribution at resorbing and forming surfaces were not observed at quiescent surfaces. Lower-affinity compounds also showed a relatively higher degree of labeling of osteocyte lacunar walls and labeled lacunae deeper within cortical bone, indicating increased penetration of the osteocyte canalicular network. Similar differences in mineralizing surface and osteocyte network penetration between high- and low-affinity compounds were evident 7 days after administration, with fluorescent conjugates at forming surfaces buried under a new layer of bone. Fluorescent compounds were incorporated into these areas of newly formed bone, indicating that "recycling" had occurred, albeit at very low levels. Taken together, these findings indicate that the bone mineral affinity of bisphosphonates is likely to influence their distribution within the skeleton. Copyright © 2012 American Society for Bone and Mineral Research.

Bioactive scaffold for bone tissue engineering: An in vivo study

NASA Astrophysics Data System (ADS)

Livingston, Treena Lynne

Massive bone loss of the proximal femur is a common problem in revision cases of total hip implants. Allograft is typically used to reconstruct the site for insertion of the new prosthesis. However, for long term fixation and function, it is desirable that the allograft becomes fully replaced by bone tissue and aids in the regeneration of bone to that site. However, allograft use is typically associated with delayed incorporation and poor remodeling. Due to these profound limitations, alternative approaches are needed. Tissue engineering is an attractive approach to designing improved graft materials. By combining osteogenic activity with a resorbable scaffold, bone formation can be stimulated while providing structure and stability to the limb during incorporation and remodeling of the scaffold. Porous, surface modified bioactive ceramic scaffolds (pSMC) have been developed which stimulate the expression of the osteoblastic phenotype and production of bone-like tissue in vitro. The scaffold and two tissue-engineered constructs, osteoprogenitor cells seeded onto scaffolds or cells expanded in culture to form bone tissue on the scaffolds prior to implantation, were investigated in a long bone defect model. The rate of incorporation was assessed. Both tissue-engineered constructs stimulated bone formation and comparable repair at 2 weeks. In a rat femoral window defect model, bone formation increased over time for all groups in concert with scaffold resorption, leading to a 40% increase in bone and 40% reduction of the scaffold in the defect by 12 weeks. Both tissue-engineered constructs enhanced the rate of mechanical repair of long bones due to better bony union with the host cortex. Long bones treated with tissue engineered constructs demonstrated a return in normal torsional properties by 4 weeks as compared to 12 weeks for long bones treated with pSMC. Culture expansion of cells to produce bone tissue in vitro did not accelerate incorporation over the treatment with cells seeded at the time of surgery. Porous, surface modified bioactive ceramic is a promising scaffold material for tissue-engineered bone repair. Bone formation and scaffold resorption act in concert for maintenance and improvement of the structural properties of the long bones over time. As determined histomorphometrically and mechanically, the rate of incorporation of the scaffold was enhanced with the tissue-engineered constructs.

Low cost silicon-on-ceramic photovoltaic solar cells

NASA Technical Reports Server (NTRS)

Koepke, B. G.; Heaps, J. D.; Grung, B. L.; Zook, J. D.; Sibold, J. D.; Leipold, M. H.

1980-01-01

A technique has been developed for coating low-cost mullite-based refractory substrates with thin layers of solar cell quality silicon. The technique involves first carbonizing one surface of the ceramic and then contacting it with molten silicon. The silicon wets the carbonized surface and, under the proper thermal conditions, solidifies as a large-grained sheet. Solar cells produced from this composite silicon-on-ceramic material have exhibited total area conversion efficiencies of ten percent.

Visualization and Analysis of Impact Damage in Sapphire

DTIC Science & Technology

2011-11-01

transparent armor materials like Starphire soda - lime and borosilicate glass [8], fused silica [9] and the transparent polycrystalline ceramic AlON...conventional glass -based armor when a transparent ceramic is used as strike face on a glass -polymer laminate [1, 2, 3]. Sapphire, i.e. single crystal aluminum...materials. Since part of transparent armor consists of brittle materials, the fragmentation of the ceramic and glass layers plays a key role in the

Static Fatigue of a Sintered Silicon Nitride.

DTIC Science & Technology

1984-10-01

Cost, Net Shape Ceramic Radial Turbine Program, Ninth Quarterly Progress Report, May 16, 1983. J. Smythe and K. Styhr, AiRcearch Garret Turbine Company ...Nijhoff Publishing Company , Boston, Massachusetts, 1983. p. 491-500. 4. SCHIOLER, L. J., QUINN. G. D., and KATZ. R. N. Tune-Temperature D(pendence of...properties and Fabrication of’Si.N4 + Y,03 Based Ceramics. Progress in Nitrogen Ceramics, I’. L. Riley, ed.. Martinus-Nijhoff Publishing Company , Boston

High efficiency tantalum-based ceramic composite structures

NASA Technical Reports Server (NTRS)

Stewart, David A. (Inventor); Leiser, Daniel B. (Inventor); DiFiore, Robert R. (Inventor); Katvala, Victor W. (Inventor)

2010-01-01

Tantalum-based ceramics are suitable for use in thermal protection systems. These composite structures have high efficiency surfaces (low catalytic efficiency and high emittance), thereby reducing heat flux to a spacecraft during planetary re-entry. These ceramics contain tantalum disilicide, molybdenum disilicide and borosilicate glass. The components are milled, along with a processing aid, then applied to a surface of a porous substrate, such as a fibrous silica or carbon substrate. Following application, the coating is then sintered on the substrate. The composite structure is substantially impervious to hot gas penetration and capable of surviving high heat fluxes at temperatures approaching 3000.degree. F. and above.

Interfacial microstructure and shear strength of reactive air brazed oxygen transport membrane ceramic-metal alloy joints

NASA Astrophysics Data System (ADS)

FR, Wahid Muhamad; Yoon, Dang-Hyok; Raju, Kati; Kim, Seyoung; Song, Kwang-sup; Yu, Ji Haeng

2018-01-01

To fabricate a multi-layered structure for maximizing oxygen production, oxygen transport membrane (OTM) ceramics need to be joined or sealed hermetically metal supports for interfacing with the peripheral components of the system. Therefore, in this study, Ag-10 wt% CuO was evaluated as an effective filler material for the reactive air brazing of dense Ce0.9Gd0.1O2-δ-La0.7Sr0.3MnO3±δ (GDC-LSM) OTM ceramics. Thermal decomposition in air and wetting behavior of the braze filler was performed. Reactive air brazing was performed at 1050 °C for 30 min in air to join GDC-LSM with four different commercially available high temperature-resistant metal alloys, such as Crofer 22 APU, Inconel 600, Fecralloy, and AISI 310S. The microstructure and elemental distribution of the ceramic-ceramic and ceramic-metal interfaces were examined from polished cross-sections. The mechanical shear strength at room temperature for the as-brazed and isothermally aged (800 °C for 24 h) joints of all the samples was compared. The results showed that the strength of the ceramic-ceramic joints was decreased marginally by aging; however, in the case of metal-ceramic joints, different decreases in strengths were observed according to the metal alloy used, which was explained based on the formation of different oxide layers at the interfaces.

The Micromorphological Research of the Internal Structure of Chairside CAD/CAM Materials by the Method of Scanning Impulse Acoustic Microscopy (SIAM).

PubMed

Goryainova, Kristina E; Morokov, Egor S; Retinskaja, Marina V; Rusanov, Fedor S; Apresyan, Samvel V; Lebedenko, Igor Yu

2018-01-01

The aim of the present work was to compare the elastic properties and internal structure of 4 different CAD/CAM chairside materials, by the method of Scanning Impulse Acoustic Microscopy (SIAM). Four chairside CAD/CAM materials with different structures from hybrid ceramic (VITA Enamic, VITA Zahnfabrik), feldspatic ceramic (VITABlocs Mark II, VITA Zahnfabrik), leucite glass-ceramic (IPS Empress CAD, Ivoclar Vivadent) and PMMA (Telio CAD, Ivoclar Vivadent) were examined by Scanning Impulse Acoustic Microscope (SIAM). The results of micromorphological research of CAD/CAM chairside materials using SIAM method showed differences between the internal structures of these materials. The internal structure of feldspatic and glass-ceramic samples revealed the presence of pores with different sizes, from 10 to 100 microns; the structure of polymer materials rendered some isolated defects, while in the structure of hybrid material, defects were not found. Based on the results obtained from the present study, in cases of chairside production of dental crowns, it would be advisable to give preference to the blocks of hybrid ceramics. Such ceramics devoid of quite large porosity, glazing for CAD/CAM crowns made from leucite glass-ceramic and feldspatic ceramic may be an option. For these purposes, commercially available special muffle furnace for clinical and laboratory individualization and glazing of ceramic prostheses were provided. Further studies are needed to confirm the evidence emerging from the present research.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Litvinova, Larisa, E-mail: larisalitvinova@yandex.ru, E-mail: vshupletsova@mail.ru, E-mail: leitsin@mail.ru; Shupletsova, Valeria, E-mail: larisalitvinova@yandex.ru, E-mail: vshupletsova@mail.ru, E-mail: leitsin@mail.ru; Leitsin, Vladimir, E-mail: larisalitvinova@yandex.ru, E-mail: vshupletsova@mail.ru, E-mail: leitsin@mail.ru

The work studies ZrO{sub 2}(Me{sub x}O{sub y})-based porous ceramics produced from the powders consisting of hollow spherical particles. It was shown that the structure is represented by a cellular framework with bimodal porosity consisting of sphere-like large pores and pores that were not filled with the powder particles during the compaction. For such ceramics, the increase of pore volume is accompanied by the increased strain in an elastic area. It was also shown that the porous ZrO{sub 2} ceramics had no acute or chronic cytotoxicity. At the same time, ceramics possess the following osteoconductive properties: adhesion support, spreading, proliferation andmore » osteogenic differentiation of MSCs.« less

The Particle Distribution in Liquid Metal with Ceramic Particles Mould Filling Process

NASA Astrophysics Data System (ADS)

Dong, Qi; Xing, Shu-ming

2017-09-01

Adding ceramic particles in the plate hammer is an effective method to increase the wear resistance of the hammer. The liquid phase method is based on the “with the flow of mixed liquid forging composite preparation of ZTA ceramic particle reinforced high chromium cast iron hammer. Preparation method for this system is using CFD simulation analysis the particles distribution of flow mixing and filling process. Taking the 30% volume fraction of ZTA ceramic composite of high chromium cast iron hammer as example, by changing the speed of liquid metal viscosity to control and make reasonable predictions of particles distribution before solidification.

Process for making ceramic insulation

DOEpatents

Akash, Akash [Salt Lake City, UT; Balakrishnan, G Nair [Sandy, UT

2009-12-08

A method is provided for producing insulation materials and insulation for high temperature applications using novel castable and powder-based ceramics. The ceramic components produced using the proposed process offers (i) a fine porosity (from nano-to micro scale); (ii) a superior strength-to-weight ratio; and (iii) flexibility in designing multilayered features offering multifunctionality which will increase the service lifetime of insulation and refractory components used in the solid oxide fuel cell, direct carbon fuel cell, furnace, metal melting, glass, chemical, paper/pulp, automobile, industrial heating, coal, and power generation industries. Further, the ceramic components made using this method may have net-shape and/or net-size advantages with minimum post machining requirements.

Evidence that failure of osteoid bone matrix resorption is caused by perturbation of osteoclast polarization.

PubMed

Yovich, S; Seydel, U; Papadimitriou, J M; Nicholson, G C; Wood, D J; Zheng, M H

1998-04-01

Osteoclasts resorb bone by a complex dynamic process that initially involves attachment, polarization and enzyme secretion, followed by their detachment and migration to new sites. In this study, we postulated that mineralized and osteoid bone matrix signal osteoclasts differently, resulting in the resorption of mineralized bone matrix only. We, therefore, compared the cytoplasmic distribution of cytoskeletal proteins F-actin and vinculin using confocal laser-scanning microscopy in osteoclasts cultured on mineralized and demineralized bone slices and correlated the observations with their functional activity. Our results have demonstrated significant differences in F-actin and vinculin staining patterns between osteoclasts cultured on mineralized bone matrix and those on demineralized bone matrix. In addition, the structural variations were accompanied by significant differences in bone resorbing activity between osteoclasts grown on mineralized bone matrix and those on demineralized bone matrix after 24 h of culture --resorption only occurring in mineralized bone but not in demineralized bone. These results indicated that failure of osteoid bone resorption is caused by perturbation of osteoclast polarization.

Use of the bioactive resorbable plate system for zygoma and zygomatic arch replacement and fixation with modified Crockett's method for maxillectomy: A technical note.

PubMed

Sukegawa, Shintaro; Kanno, Takahiro; Shibata, Akane; Matsumoto, Kenichi; Sukegawa-Takahashi, Yuka; Sakaida, Kyousuke; Furuki, Yoshihiko

2017-07-01

As a surgical approach targeting the pterygopalatine fossa following maxillary cancer due to tumor invasion, Crockett's method is conventional and useful. However, if the tumor is confined to the area between the maxilla and pterygopalatine fossa, it is not necessary to include the zygomatico-orbital in the access osteotomy, and the orbital floor may be preserved. Depending on the range of tumor invasion, the current study reports a more minimally invasive, modified Crockett's surgery that may be considered, which includes resection with modified osteotomy lines and repositioning with fixation of the zygoma and zygomatic arch following maxillary cancer ablation. In addition, the majority of patients with advanced maxillary cancer may require postoperative radiotherapy or chemoradiotherapy following maxillectomy according to several guidelines. Therefore, using a low-profile bioactive resorbable plate system as a method of repositioning and fixing the resected and preserved zygoma and zygomatic arch may be more effective in this modified Crockett's method for maxillectomy.

Continuous Digital Light Processing (cDLP): Highly Accurate Additive Manufacturing of Tissue Engineered Bone Scaffolds.

PubMed

Dean, David; Jonathan, Wallace; Siblani, Ali; Wang, Martha O; Kim, Kyobum; Mikos, Antonios G; Fisher, John P

2012-03-01

Highly accurate rendering of the external and internal geometry of bone tissue engineering scaffolds effects fit at the defect site, loading of internal pore spaces with cells, bioreactor-delivered nutrient and growth factor circulation, and scaffold resorption. It may be necessary to render resorbable polymer scaffolds with 50 μm or less accuracy to achieve these goals. This level of accuracy is available using Continuous Digital Light processing (cDLP) which utilizes a DLP(®) (Texas Instruments, Dallas, TX) chip. One such additive manufacturing device is the envisionTEC (Ferndale, MI) Perfactory(®). To use cDLP we integrate a photo-crosslinkable polymer, a photo-initiator, and a biocompatible dye. The dye attenuates light, thereby limiting the depth of polymerization. In this study we fabricated scaffolds using the well-studied resorbable polymer, poly(propylene fumarate) (PPF), titanium dioxide (TiO(2)) as a dye, Irgacure(®) 819 (BASF [Ciba], Florham Park, NJ) as an initiator, and diethyl fumarate as a solvent to control viscosity.

Biomaterials in search of a meniscus substitute.

PubMed

Rongen, Jan J; van Tienen, Tony G; van Bochove, Bas; Grijpma, Dirk W; Buma, Pieter

2014-04-01

The menisci fulfill key biomechanical functions in the tibiofemoral (knee) joint. Unfortunately meniscal injuries are quite common and most often treated by (partial) meniscectomy. However, some patients experience enduring symptoms, and, more importantly, it leads to an increased risk for symptomatic osteoarthritis. Over the past decades, researchers have put effort in developing a meniscal substitute able to prevent osteoarthritis and treat enduring clinical symptoms. Grossly, two categories of substitutes are observed: First, a resorbable scaffold mimicking biomechanical function which slowly degrades while tissue regeneration and organization is promoted. Second, a non resorbable, permanent implant which mimics the biomechanical function of the native meniscus. Numerous biomaterials with different (material) properties have been used in order to provide such a substitute. Nevertheless, a clinically applicable cartilage protecting material is not yet emerged. In the current review we provide an overview, and discuss, these different materials and extract recommendations regarding material properties for future developmental research. Copyright © 2014 Elsevier Ltd. All rights reserved.

Ultralight and fire-resistant ceramic nanofibrous aerogels with temperature-invariant superelasticity.

PubMed

Si, Yang; Wang, Xueqin; Dou, Lvye; Yu, Jianyong; Ding, Bin

2018-04-01

Ultralight aerogels that are both highly resilient and compressible have been fabricated from various materials including polymer, carbon, and metal. However, it has remained a great challenge to realize high elasticity in aerogels solely based on ceramic components. We report a scalable strategy to create superelastic lamellar-structured ceramic nanofibrous aerogels (CNFAs) by combining SiO 2 nanofibers with aluminoborosilicate matrices. This approach causes the random-deposited SiO 2 nanofibers to assemble into elastic ceramic aerogels with tunable densities and desired shapes on a large scale. The resulting CNFAs exhibit the integrated properties of flyweight densities of >0.15 mg cm -3 , rapid recovery from 80% strain, zero Poisson's ratio, and temperature-invariant superelasticity to 1100°C. The integral ceramic nature also provided the CNFAs with robust fire resistance and thermal insulation performance. The successful synthesis of these fascinating materials may provide new insights into the development of ceramics in a lightweight, resilient, and structurally adaptive form.

Ultralight and fire-resistant ceramic nanofibrous aerogels with temperature-invariant superelasticity

PubMed Central

Wang, Xueqin; Dou, Lvye; Yu, Jianyong

2018-01-01

Ultralight aerogels that are both highly resilient and compressible have been fabricated from various materials including polymer, carbon, and metal. However, it has remained a great challenge to realize high elasticity in aerogels solely based on ceramic components. We report a scalable strategy to create superelastic lamellar-structured ceramic nanofibrous aerogels (CNFAs) by combining SiO2 nanofibers with aluminoborosilicate matrices. This approach causes the random-deposited SiO2 nanofibers to assemble into elastic ceramic aerogels with tunable densities and desired shapes on a large scale. The resulting CNFAs exhibit the integrated properties of flyweight densities of >0.15 mg cm−3, rapid recovery from 80% strain, zero Poisson’s ratio, and temperature-invariant superelasticity to 1100°C. The integral ceramic nature also provided the CNFAs with robust fire resistance and thermal insulation performance. The successful synthesis of these fascinating materials may provide new insights into the development of ceramics in a lightweight, resilient, and structurally adaptive form. PMID:29719867

Synthesis and characterization of PbTiO3 based glass ceramics

NASA Astrophysics Data System (ADS)

Shankar, J.; Rani, G. Neeraja; Mamatha, B.; Deshpande, V. K.

2017-05-01

Glass samples with composition (50 - X) PbO - XCaO - 25 TiO2 - 25 B2O3 (where = 0, .5, 10 and 15 mol %) were prepared using conventional quenching technique. It was observed that with the addition of alkaline earth oxides to lead borate glass containing TiO2 alters the network (conversion of BO3 to BO4) increasing the rigidity of the glass which enhances the Tg. These glass samples were converted to glass ceramics by following two stage heat treatment schedule. The density values of glass ceramic samples are higher than those of corresponding glass samples. It was observed that there was good correlation between the density and CTE results of the glass-ceramics. The XRD results in the glass ceramics revealed the formation of tetragonal lead titanate as a major crystalline phase and Ca3Ti2O7 as minor crystalline phase. The ferroelectric nature of all the glass ceramic samples is confirmed by P - E hysteresis measurements.

Esthetic Rehabilitation of Anterior Teeth with Copy-Milled Restorations: A Report of Two Cases.

PubMed

Rani, Sapna; Devi, Jyoti; Jain, Chandan; Mutneja, Parul; Verma, Mahesh

2017-01-01

Digitalization has become part and parcel of contemporary prosthodontics with the probability of most of the procedures being based on the digital techniques in the near future. This digital revolution started in the latter half of the 20th century by converting analog objects/signals into digital bits and bytes. Recent developments in all-ceramic materials and systems of computer-aided designing and computer-aided manufacturing (CAD/CAM), copy milling, and so forth offer excellent esthetics and superb biocompatibility. Copy milling system for ceramics enables milling of the zirconia cores of all-ceramic restorations precisely and also if this system is properly used the procedure for fabricating all-ceramic restorations can be substantially simplified. This case report presents fabrication of all-ceramic Maryland Bridge and post-core with a copy milling system for esthetics and preservation of integrity of tooth. For both of the patients, the use of biologic, all-ceramic, copy-milled restorations resulted in clinical success and recovered function and esthetics.

SPS-RS technique for solid-phase “in situ” synthesis of biocompatible ZrO2 porous ceramics

NASA Astrophysics Data System (ADS)

Shichalin, O. O.; Medkov, M. A.; Grishchenko, D. N.; Mayorov, V. Yu; Fedorets, A. N.; Belov, A. A.; Golub, A. V.; Gridasova, E. A.; Papynov, E. K.

2018-02-01

The prospective method of spark plasma sintering-reaction synthesis (SPS-RS) for fabrication of ceramics based on ZrO2 and biocompatible with living tissue is presented. Nanostructured ceramics has high mechanical strength (more than 400 MPa) and controlled porosity depending on specified sintering conditions. Biocompatible phases Ca10(PO4)6(OH)2 are formed “in situ” during SPS sintering of ZrO2 powder due to chemical interaction of phosphate precursors preliminary introduced into the mixture. The effective method to improve (to develop) porous structure of bioceramics obtained by SPS or SPS-RS techniques using poreforming agent (carbon black) is proposed. Suggested original SPS-RS “in situ” technique provides fabrication of new ZrO2 ceramics containing biocompatible phosphate components and possessing unique structural and mechanical characteristics. Such ceramics is indispensable for bone-ceramic implants that are able to activate processes of osteogenesis during bone tissue recovery.

[Optical and spectral parameters in Ce3+ -doped gadolinium gallium aluminum garnet glass-ceramics].

PubMed

Gong, Hua; Zhao, Xin; Yu, Xiao-bo; Setsuhisa, Tanabe; Lin, Hai

2010-01-01

The crystalline phases of Ce3+ -doped gadolinium gallium aluminum garnet (GGAG) glass-ceramics were investigated by X-ray diffraction, and the fluorescence spectra were recorded under the pumping of blue light-emitting diode (LED) using an integrating sphere of 10-inch in diameter, which connected to a CCD detector. The spectral power distribution of the glass-ceramics was obtained from the measured spectra first, and then the quantum yield was derived based on the photon distribution. The quantum yield of Ce3+ emission in GGAG glass-ceramics is 29.2%, meanwhile, the color coordinates and the correlated color temperature (CCT) of combined white light were proved to be x = 0.319, y = 0.349 and 6086 K, respectively. Although the quantum yield is a little smaller than the value in Ce3+ -doped YAG glass-ceramics, the CCT of the combined white light is much smaller than that in the latter. The optical behavior of GGAG glass-ceramics provides new vision for developing comfortable LED lighting devices.

Esthetic Rehabilitation of Anterior Teeth with Copy-Milled Restorations: A Report of Two Cases

PubMed Central

Jain, Chandan; Mutneja, Parul; Verma, Mahesh

2017-01-01

Digitalization has become part and parcel of contemporary prosthodontics with the probability of most of the procedures being based on the digital techniques in the near future. This digital revolution started in the latter half of the 20th century by converting analog objects/signals into digital bits and bytes. Recent developments in all-ceramic materials and systems of computer-aided designing and computer-aided manufacturing (CAD/CAM), copy milling, and so forth offer excellent esthetics and superb biocompatibility. Copy milling system for ceramics enables milling of the zirconia cores of all-ceramic restorations precisely and also if this system is properly used the procedure for fabricating all-ceramic restorations can be substantially simplified. This case report presents fabrication of all-ceramic Maryland Bridge and post-core with a copy milling system for esthetics and preservation of integrity of tooth. For both of the patients, the use of biologic, all-ceramic, copy-milled restorations resulted in clinical success and recovered function and esthetics. PMID:28326203

Comparative assessment of marginal accuracy of grade II titanium and Ni–Cr alloy before and after ceramic firing: An in vitro study

PubMed Central

Patil, Abhijit; Singh, Kishan; Sahoo, Sukant; Suvarna, Suraj; Kumar, Prince; Singh, Anupam

2013-01-01

Objective: The aims of the study are to assess the marginal accuracy of base metal and titanium alloy casting and to evaluate the effect of repeated ceramic firing on the marginal accuracy of base metal and titanium alloy castings. Materials and Methods: Twenty metal copings were fabricated with each casting material. Specimens were divided into 4 groups of 10 each representing base metal alloys castings without (Group A) and with metal shoulder margin (Group B), titanium castings without (Group C) and with metal shoulder margin (Group D). The measurement of fit of the metal copings was carried out before the ceramic firing at four different points and the same was followed after porcelain build-up. Results: Significant difference was found when Ni–Cr alloy samples were compared with Grade II titanium samples both before and after ceramic firings. The titanium castings with metal shoulder margin showed highest microgap among all the materials tested. Conclusions: Based on the results that were found and within the limitations of the study design, it can be concluded that there is marginal discrepancy in the copings made from Ni–Cr and Grade II titanium. This marginal discrepancy increased after ceramic firing cycles for both Ni–Cr and Grade II titanium. The comparative statistical analysis for copings with metal-collar showed maximum discrepancy for Group D. The comparative statistical analysis for copings without metal-collar showed maximum discrepancy for Group C. PMID:24926205

Randomized clinical trial of implant-supported ceramic-ceramic and metal-ceramic fixed dental prostheses: preliminary results.

PubMed

Esquivel-Upshaw, Josephine F; Clark, Arthur E; Shuster, Jonathan J; Anusavice, Kenneth J

2014-02-01

The aim of this study was to determine the survival rates over time of implant-supported ceramic-ceramic and metal-ceramic prostheses as a function of core-veneer thickness ratio, gingival connector embrasure design, and connector height. An IRB-approved, randomized, controlled clinical trial was conducted as a single-blind pilot study involving 55 patients missing three teeth in either one or two posterior areas. These patients (34 women; 21 men; age range 52-75 years) were recruited for the study to receive a three-unit implant-supported fixed dental prosthesis (FDP). Two implants were placed for each of the 72 FDPs in the study. The implants (Osseospeed, Astra Tech), which were made of titanium, were grit blasted. A gold-shaded, custom-milled titanium abutment (Atlantis, Astra Tech), was secured to each implant body. Each of the 72 FDPs in 55 patients were randomly assigned based on one of the following options: (1) A. ceramic-ceramic (Yttria-stabilized zirconia core, pressable fluorapatite glass-ceramic, IPS e.max ZirCAD, and ZirPress, Ivoclar Vivadent) B. metal-ceramic (palladium-based noble alloy, Capricorn, Ivoclar Vivadent, with press-on leucite-reinforced glass-ceramic veneer, IPS InLine POM, Ivoclar Vivadent); (2) occlusal veneer thickness (0.5, 1.0, and 1.5 mm); (3) curvature of gingival embrasure (0.25, 0.5, and 0.75 mm diameter); and (4) connector height (3, 4, and 5 mm). FDPs were fabricated and cemented with dual-cure resin cement (RelyX, Universal Cement, 3M ESPE). Patients were recalled at 6 months, 1 year, and 2 years. FDPs were examined for cracks, fracture, and general surface quality. Recall exams of 72 prostheses revealed 10 chipping fractures. No fractures occurred within the connector or embrasure areas. Two-sided Fisher's exact tests showed no significant correlation between fractures and type of material system (p = 0.51), veneer thickness (p = 0.75), radius of curvature of gingival embrasure (p = 0.68), and connector height (p = 0.91). Although there were no significant associations between connector height, curvature of gingival embrasure, core/veneer thickness ratio, and material system and the survival probability of implant-supported FDPs with zirconia as a core material, the small number of fractures precludes a definitive conclusion on the dominant controlling factor. © 2013 by the American College of Prosthodontists.

Randomized Clinical Trial of Implant-Supported Ceramic-Ceramic and Metal-Ceramic Fixed Dental Prostheses: Preliminary Results

PubMed Central

Esquivel-Upshaw, Josephine F.; Clark, Arthur E.; Shuster, Jonathan J.; Anusavice, Kenneth J.

2013-01-01

Purpose The aim of this study was to determine the survival rates over time of implant-supported ceramic-ceramic and metal-ceramic prostheses as a function of core-veneer thickness ratio, gingival connector embrasure design, and connector height. Materials and Methods An IRB-approved, randomized, controlled clinical trial was conducted as a single-blind pilot study involving 55 patients missing three teeth in either one or two posterior areas. These patients (34 women; 21 men; age range 52–75 years) were recruited for the study to receive a 3-unit implant-supported fixed dental prosthesis (FDP). Two implants were placed for each of the 72 FDPs in the study. The implants (Osseospeed, Astra Tech), which were made of titanium, were grit blasted. A gold-shaded, custom-milled titanium abutment (Atlantis, Astra Tech), was secured to each implant body. Each of the 72 FDPs in 55 patients were randomly assigned based on one of the following options: (1) A. Material: ceramic-ceramic (Yttria-stabilized zirconia core, pressable fluorapatite glass-ceramic, IPS e.max ZirCAD and ZirPress, Ivoclar Vivadent) B. metal-ceramic (palladium-based noble alloy, Capricorn, Ivoclar Vivadent, with press-on leucite-reinforced glass-ceramic veneer, IPS InLine POM, Ivoclar Vivadent); (2) occlusal veneer thickness (0.5, 1.0, and 1.5 mm); (3) curvature of gingival embrasure (0.25, 0.5, and 0.75 mm diameter); and (4) connector height (3, 4, and 5 mm). FDPs were fabricated and cemented with dual-cure resin cement (RelyX, Universal Cement, 3M ESPE). Patients were recalled at 6 months, 1 year, and 2 years. FDPs were examined for cracks, fracture, and general surface quality. Results Recall exams of 72 prostheses revealed 10 chipping fractures. No fractures occurred within the connector or embrasure areas. Two-sided Fisher’s exact tests showed no significant correlation between fractures and type of material system (p = 0.51), veneer thickness (p = 0.75), radius of curvature of gingival embrasure (p = 0.68), and connector height (p = 0.91). Conclusions Although there were no significant associations between connector height, curvature of gingival embrasure, core/veneer thickness ratio, and material system and the survival probability of implant-supported FDPs with zirconia as a core material, the small number of fractures precludes a definitive conclusion on the dominant controlling factor. PMID:23758092

Reduction-oxidation Enabled Glass-ceramics to Stainless Steel Bonding Part I: screening of doping oxidants

DOE Office of Scientific and Technical Information (OSTI.GOV)

Dai, Steve Xunhu

Lithium silicate-based glass-ceramics with high coefficients of thermal expansion, designed to form matched hermetic seals in 304L stainless steel housing, show little evidence of interfacial chemical bonding, despite extensive inter-diffusion at the glass-ceramic-stainless steel (GC-SS) interface. A series of glass-ceramic compositions modified with a variety of oxidants, AgO, FeO, NiO, PbO, SnO, CuO, CoO, MoO 3 and WO 3, are examined for the feasibility of forming bonding oxides through reduction-oxidation (redox) at the GC-SS interface. The oxidants were selected according to their Gibbs free energy to allow for oxidation of Cr/Mn/Si from stainless steel, and yet to prevent a reductionmore » of P2O5 in the glass-ceramic where the P 2O 5 is to form Li 3PO 4 nuclei for growth of high expansion crystalline SiO 2 phases. Other than the CuO and CoO modified glass-ceramics, bonding from interfacial redox reactions were not achieved in the modified glass-ceramics, either because of poor wetting on the stainless steel or a reduction of the oxidants at the surface of glass-ceramic specimens rather than the GC-SS interface.« less

Advanced Ceramic Technology for Space Applications at NASA MSFC

NASA Technical Reports Server (NTRS)

Alim, Mohammad A.

2003-01-01

The ceramic processing technology using conventional methods is applied to the making of the state-of-the-art ceramics known as smart ceramics or intelligent ceramics or electroceramics. The sol-gel and wet chemical processing routes are excluded in this investigation considering economic aspect and proportionate benefit of the resulting product. The use of ceramic ingredients in making coatings or devices employing vacuum coating unit is also excluded in this investigation. Based on the present information it is anticipated that the conventional processing methods provide identical performing ceramics when compared to that processed by the chemical routes. This is possible when sintering temperature, heating and cooling ramps, peak temperature (sintering temperature), soak-time (hold-time), etc. are considered as variable parameters. In addition, optional calcination step prior to the sintering operation remains as a vital variable parameter. These variable parameters constitute a sintering profile to obtain a sintered product. Also it is possible to obtain identical products for more than one sintering profile attributing to the calcination step in conjunction with the variables of the sintering profile. Overall, the state-of-the-art ceramic technology is evaluated for potential thermal and electrical insulation coatings, microelectronics and integrated circuits, discrete and integrated devices, etc. applications in the space program.

Synthesis, characterization and potential utility of doped ceramics based catalysts

NASA Astrophysics Data System (ADS)

Sharma, Ritika; Yadav, Deepshikha; Singh, G. P.; Vyas, G.; Bhojak, N.

2018-05-01

Excessive utilization of petrol, diesel and other fossil fuels, continuous increase in their prices, and the big problem of carbon dioxide mission have encouraged scientists and technologist to find either new sources of energy or to develop technologies for the sustainable utilization of fuel. Biofuels are the only energy technologies that can resolve the problem of carbon dioxide emission in the atmosphere as well as reduce the amount of fossil fuel burned. Bio ethanol and biodiesel are the most common types of biofuel which are being used at present. Biodiesel has become more interesting for all the researchers in present scenario. Various feedstock viz. edible, nonedible oils, waste cooking oil, animal fat, algae etc, are using for the production of biodiesel worldwide according to their availability. Selection of efficient heterogeneous catalysts for biodiesel preparation still needs more attention of researchers. The present investigation deals with determination of synthesis, characterization and applications of doped ceramic based materials in different medium. Two of doped ceramic based catalysts which has been potentially used for the production of biodiesel. The Engine performance of biodiesel samples, made from industrial waste oils and ceramic based catalyst, have also been investigated and found up to satisfactory levels.

Volatile Reaction Products From Silicon-Based Ceramics in Combustion Environments Identified

NASA Technical Reports Server (NTRS)

Opila, Elizabeth J.

1997-01-01

Silicon-based ceramics and composites are prime candidates for use as components in the hot sections of advanced aircraft engines. These materials must have long-term durability in the combustion environment. Because water vapor is always present as a major product of combustion in the engine environment, its effect on the durability of silicon-based ceramics must be understood. In combustion environments, silicon-based ceramics react with water vapor to form a surface silica (SiO2) scale. This SiO2 scale, in turn, has been found to react with water vapor to form volatile hydroxides. Studies to date have focused on how water vapor reacts with high-purity silicon carbide (SiC) and SiO2 in model combustion environments. Because the combustion environment in advanced aircraft engines is expected to contain about 10-percent water vapor at 10-atm total pressure, the durability of SiC and SiO2 in gas mixtures containing 0.1- to 1-atm water vapor is of interest. The reactions of SiC and SiO2 with water vapor were monitored by measuring weight changes of sample coupons in a 0.5-atm water vapor/0.5-atm oxygen gas mixture with thermogravimetric analysis.

Large actuation strain over 0.3% in periodically orthogonal poled BaTiO3 ceramics and multilayer actuators via reversible domain switching

NASA Astrophysics Data System (ADS)

Wang, Qiangzhong; Li, Faxin

2018-06-01

Lead titanate zirconate (PZT) ceramics based piezoelectric actuators always suffer from small output strains (typically 0.1%–0.15%) and have recently been criticized for the toxicity problem of the high-concentration lead. In our recent work (Li et al 2017 J. Appl. Phys. 122 074103), we realized large local actuation strain nearly 0.6% in a periodically orthogonal poled (POP) PZT ceramics via reversible domain switching. In this work, we applied the POP method to barium titanate (BT) ceramics and proposed a specially designed multilayer actuator which can output large uniform strain. The simple tetragonal structure of BT ceramics makes it easier to understand the mechanism of reversible domain switching in POP ceramics and its lead-free characteristic is more promising. Firstly, a POP BT ceramic piece was fabricated and the actuation testing results show that local large actuation strain of 0.36% can be obtained under a field of 2 kV mm‑1 at 0.1 Hz. However, the actuation strain is non-uniform along the period direction, varying from 0.22% to 0.36%. Then, to output uniform large strain, a four-layer actuator based on the POP BT ceramics was designed and fabricated in which only the in-plane poled regions of the adjacent layers were bonded. Results show that the output strain turns to be uniform in this way, which is 0.34% under 2 kV mm‑1, resulting in a very high large-signal (=S max/E max) of 1700 pm V‑1. The large actuation strain is very stable and keeps unchanged after 20k cycles of operation. It drops quickly with the increasing frequency and is stabilized at 0.18% above 1.0 Hz. Finally, bipolar field testing was conducted on the POP BT based actuator. Results show that the actuator shows electrostriction-like symmetric bipolar actuation behavior with the repeatable actuation strain of 0.3% under 2 kV mm‑1. This work may provide a feasible solution to low frequency, large-strain lead-free piezoelectric actuation.

Influence of cooling rate on residual stress profile in veneering ceramic: measurement by hole-drilling.

PubMed

Mainjot, Amélie K; Schajer, Gary S; Vanheusden, Alain J; Sadoun, Michaël J

2011-09-01

The manufacture of dental crowns and bridges generates residual stresses within the veneering ceramic and framework during the cooling process. Residual stress is an important factor that control the mechanical behavior of restorations. Knowing the stress distribution within the veneering ceramic as a function of depth can help the understanding of failures, particularly chipping, a well-known problem with Yttria-tetragonal-zirconia-polycrystal based fixed partial dentures. The objective of this study is to investigate the cooling rate dependence of the stress profile in veneering ceramic layered on metal and zirconia frameworks. The hole-drilling method, often used for engineering measurements, was adapted for use with veneering ceramic. The stress profile was measured in bilayered disc samples 20 mm in diameter, with a 0.7 mm thick metal or Yttria-tetragonal-zirconia-polycrystal framework and a 1.5mm thick veneering ceramic. Three different cooling procedures were investigated. The magnitude of the stresses in the surface of the veneering ceramic was found to increase with cooling rate, while the interior stresses decreased. At the surface, compressive stresses were observed in all samples. In the interior, compressive stresses were observed in metal samples and tensile in zirconia samples. Cooling rate influences the magnitude of residual stresses. These can significantly influence the mechanical behavior of metal-and zirconia-based bilayered systems. The framework material influenced the nature of the interior stresses, with zirconia samples showing a less favorable stress profile than metal. Copyright © 2011 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Bioactive calcium pyrophosphate glasses and glass-ceramics.

PubMed

Kasuga, Toshihiro

2005-01-01

Calcium phosphate glass-based materials in the pyrophosphate region are briefly reviewed. Calcium pyrophosphate glasses can be prepared by including a small amount of TiO(2) (

A novel method for isolation and recovery of ceramic nanoparticles and metal wear debris from serum lubricants at ultra-low wear rates.

PubMed

Lal, S; Hall, R M; Tipper, J L

2016-09-15

Ceramics have been used to deliver significant improvements in the wear properties of orthopaedic bearing materials, which has made it challenging to isolate wear debris from simulator lubricants. Ceramics such as silicon nitride, as well as ceramic-like surface coatings on metal substrates have been explored as potential alternatives to conventional implant materials. Current isolation methods were designed for isolating conventional metal, UHMWPE and ceramic wear debris. In this paper, we describe a methodology for isolation and recovery of ceramic or ceramic-like coating particles and metal wear particles from serum lubricants under ultra-low and low wear performance. Enzymatic digestion was used to digest the serum proteins and sodium polytungstate was used as a novel density gradient medium to isolate particles from proteins and other contaminants by ultracentrifugation. This method demonstrated over 80% recovery of particles and did not alter the size or morphology of ceramic and metal particles during the isolation process. Improvements in resistance to wear and mechanical damage of the articulating surfaces have a large influence on longevity and reliability of joint replacement devices. Modern ceramics have demonstrated ultra-low wear rates for hard-on-hard total hip replacements. Generation of very low concentrations of wear debris in simulator lubricants has made it challenging to isolate the particles for characterisation and further analysis. We have introduced a novel method to isolate ceramic and metal particles from serum-based lubricants using enzymatic digestion and novel sodium polytungstate gradients. This is the first study to demonstrate the recovery of ceramic and metal particles from serum lubricants at lowest detectable in vitro wear rates reported in literature. Copyright © 2016. Published by Elsevier Ltd.

Low Cost Fabrication of Silicon Carbide Based Ceramics and Fiber Reinforced Composites

NASA Technical Reports Server (NTRS)

Singh, M.; Levine, S. R.

1995-01-01

A low cost processing technique called reaction forming for the fabrication of near-net and complex shaped components of silicon carbide based ceramics and composites is presented. This process consists of the production of a microporous carbon preform and subsequent infiltration with liquid silicon or silicon-refractory metal alloys. The microporous preforms are made by the pyrolysis of a polymerized resin mixture with very good control of pore volume and pore size thereby yielding materials with tailorable microstructure and composition. Mechanical properties (elastic modulus, flexural strength, and fracture toughness) of reaction-formed silicon carbide ceramics are presented. This processing approach is suitable for various kinds of reinforcements such as whiskers, particulates, fibers (tows, weaves, and filaments), and 3-D architectures. This approach has also been used to fabricate continuous silicon carbide fiber reinforced ceramic composites (CFCC's) with silicon carbide based matrices. Strong and tough composites with tailorable matrix microstructure and composition have been obtained. Microstructure and thermomechanical properties of a silicon carbide (SCS-6) fiber reinforced reaction-formed silicon carbide matrix composites are discussed.

Fine platinum nanoparticles supported on a porous ceramic membrane as efficient catalysts for the removal of benzene.

PubMed

Liu, Hui; Li, Chengyin; Ren, Xiaoyong; Liu, Kaiqi; Yang, Jun

2017-11-29

It would be desirable to remove volatile organic compounds (VOCs) while we eliminate the dusts using silicon carbide (SiC)-based porous ceramics from the hot gases. Aiming at functionalizing SiC-based porous ceramics with catalytic capability, we herein report a facile strategy to integrate high efficient catalysts into the porous SiC substrates for the VOC removal. We demonstrate an aqueous salt method for uniformly distributing fine platinum (Pt) particles on the alumina (Al 2 O 3 ) layers, which are pre-coated on the SiC substrates as supports for VOC catalysts. We confirm that at a Pt mass loading as low as 0.176% and a weight hourly space velocity of 6000 mL g -1 h -1 , the as-prepared Pt/SiC@Al 2 O 3 catalysts can convert 90% benzene at a temperature of ca. 215 °C. The results suggest a promising way to design ceramics-based bi-functional materials for simultaneously eliminating dusts and harmful VOCs from various hot gases.

Ceramic matrix composite behavior -- Computational simulation

DOE Office of Scientific and Technical Information (OSTI.GOV)

Chamis, C.C.; Murthy, P.L.N.; Mital, S.K.

Development of analytical modeling and computational capabilities for the prediction of high temperature ceramic matrix composite behavior has been an ongoing research activity at NASA-Lewis Research Center. These research activities have resulted in the development of micromechanics based methodologies to evaluate different aspects of ceramic matrix composite behavior. The basis of the approach is micromechanics together with a unique fiber substructuring concept. In this new concept the conventional unit cell (the smallest representative volume element of the composite) of micromechanics approach has been modified by substructuring the unit cell into several slices and developing the micromechanics based equations at themore » slice level. Main advantage of this technique is that it can provide a much greater detail in the response of composite behavior as compared to a conventional micromechanics based analysis and still maintains a very high computational efficiency. This methodology has recently been extended to model plain weave ceramic composites. The objective of the present paper is to describe the important features of the modeling and simulation and illustrate with select examples of laminated as well as woven composites.« less

Department of Defense Advisory Group on Electron Devices. Special Technology Area Review on Microwave Packaging Technology. Appendix

DTIC Science & Technology

1993-02-01

sintered in hydrogen furnace at very high temperatures . Multiple furnace firing occurs until the binders are removed and part density is achieved "* Process...and base Low temperature co-fired ceramic - Metallized for shielding and grounding - Low resistance thick-film metallization - High thermal resistance...ESPECIALLY LOW TEMPERATURE COFIRED CERAMIC CERAMICS HIGH THERMAL CONDUCTIVITY,MATCHED GaAS AND SILICON SUBSTRATE MATERIALS I I,1Z#A,17Mr1 J, TI

Rapid Prototyping

NASA Technical Reports Server (NTRS)

1999-01-01

Javelin, a Lone Peak Engineering Inc. Company has introduced the SteamRoller(TM) System as a commercial product. The system was designed by Javelin during a Phase II NASA funded small commercial product. The purpose of the invention was to allow automated-feed of flexible ceramic tapes to the Laminated Object Manufacturing rapid prototyping equipment. The ceramic material that Javelin was working with during the Phase II project is silicon nitride. This engineered ceramic material is of interest for space-based component.

Porous ceramic membrane with superhydrophobic and superoleophilic surface for reclaiming oil from oily water

NASA Astrophysics Data System (ADS)

Su, Changhong; Xu, Youqian; Zhang, Wei; Liu, Yang; Li, Jun

2012-01-01

A porous ceramic tube with superhydrophobic and superoleophilic surface was fabricated by sol-gel and then surface modification with polyurethane-polydimethysiloxane, and an oil-water separator based on the porous ceramic tube was erected to characterize superhydrophobic and superoleophilic surface's separation efficiency and velocity when being used to reclaim oil from oily water and complex oily water containing clay particle. The separator is fit for reclaiming oil from oily water.

Battery utilizing ceramic membranes

DOEpatents

Yahnke, Mark S.; Shlomo, Golan; Anderson, Marc A.

1994-01-01

A thin film battery is disclosed based on the use of ceramic membrane technology. The battery includes a pair of conductive collectors on which the materials for the anode and the cathode may be spin coated. The separator is formed of a porous metal oxide ceramic membrane impregnated with electrolyte so that electrical separation is maintained while ion mobility is also maintained. The entire battery can be made less than 10 microns thick while generating a potential in the 1 volt range.

Challenges and Opportunities in Reactive Processing and Applications of Advanced Ceramic Materials

NASA Technical Reports Server (NTRS)

Singh, Mrityunjay

2003-01-01

Recently, there has been a great deal of interest in the research, development, and commercialization of innovative synthesis and processing technologies for advanced ceramics and composite materials. Reactive processing approaches have been actively considered due to their robustness, flexibility, and affordability. A wide variety of silicon carbide-based advanced ceramics and composites are currently being fabricated using the processing approaches involving reactive infiltration of liquid and gaseous species into engineered fibrous or microporous carbon performs. The microporous carbon performs have been fabricated using the temperature induced phase separation and pyrolysis of two phase organic (resin-pore former) mixtures and fiber reinforcement of carbon and ceramic particulate bodies. In addition, pyrolyzed native plant cellulose tissues also provide unique carbon templates for manufacturing of non-oxide and oxide ceramics. In spite of great interest in this technology due to their affordability and robustness, there is a lack of scientific basis for process understanding and many technical challenges still remain. The influence of perform properties and other parameters on the resulting microstructure and properties of final material is not well understood. In this presentation, mechanism of silicon-carbon reaction in various systems and the effect of perform microstructure on the mechanical properties of advanced silicon carbide based materials will be discussed. Various examples of applications of reactively processed advanced silicon carbide ceramics and composite materials will be presented.

Electrostatic Assembly Preparation of High-Toughness Zirconium Diboride-Based Ceramic Composites with Enhanced Thermal Shock Resistance Performance.

PubMed

Zhang, Baoxi; Zhang, Xinghong; Hong, Changqing; Qiu, Yunfeng; Zhang, Jia; Han, Jiecai; Hu, PingAn

2016-05-11

The central problem of using ceramic as a structural material is its brittleness, which associated with rigid covalent or ionic bonds. Whiskers or fibers of strong ceramics such as silicon carbide (SiC) or silicon nitride (Si3N4) are widely embedded in a ceramic matrix to improve the strength and toughness. The incorporation of these insulating fillers can impede the thermal flow in ceramic matrix, thus decrease its thermal shock resistance that is required in some practical applications. Here we demonstrate that the toughness and thermal shock resistance of zirconium diboride (ZrB2)/SiC composites can be improved simultaneously by introducing graphene into composites via electrostatic assembly and subsequent sintering treatment. The incorporated graphene creates weak interfaces of grain boundaries (GBs) and optimal thermal conductance paths inside composites. In comparison to pristine ZrB2-SiC composites, the toughness of (2.0%) ZrB2-SiC/graphene composites exhibited a 61% increasing (from 4.3 to 6.93 MPa·m(1/2)) after spark plasma sintering (SPS); the retained strength after thermal shock increased as high as 74.8% at 400 °C and 304.4% at 500 °C. Present work presents an important guideline for producing high-toughness ceramic-based composites with enhanced thermal shock properties.

The dynamic properties of sandwich structures based on metal-ceramic foams.

DOT National Transportation Integrated Search

2014-01-01

The present research program has studied the fracture properties of closed pore metal-ceramic foams for their potential applications as core systems in sandwich structures. The composite foams were created at Fireline, Inc. (Youngstown, OH) using the...

Structural Transition and Electrical Properties of (1 - x)(Na0.4K0.1Bi0.5)TiO3- xSrTiO3 Lead-Free Piezoceramics

NASA Astrophysics Data System (ADS)

Liu, Xing; Zhai, Jiwei; Shen, Bo; Li, Feng; Li, Peng

2017-10-01

(1 - x)(Na0.4K0.1Bi0.5)TiO3- xSrTiO3 (NKBT- xST) ceramics with x = 0 mol.%, 3 mol.%, and 5 mol.% (0ST, 3ST, and 5ST) have been prepared by a conventional solid-state reaction method and their ferroelectric, electrostrictive, and pyroelectric properties investigated. Addition of ST considerably disrupted the long-range ferroelectric order of NKBT- xST ceramics, and the 5ST ceramic exhibited ergodic relaxor phase structure. T FR shifted to near or below room temperature for 5ST ceramic, accompanied by a significant decline of ferroelectricity and enhanced strain. As the temperature approached T FR, the NKBT- xST ceramics exhibited predominantly electrostrictive effect, and the 5ST ceramic presented relatively high electrostrictive coefficient Q 33 of 0.0193 m4/C2. High pyroelectric response was observed for 0ST, 3ST, and 5ST ceramics in the vicinity of T FR due to the large polarization release during the ferroelectric-relaxor structural transition. The 5ST ceramic exhibited high and frequency-insensitive (100 Hz to 10 kHz) room-temperature pyroelectric properties with pyroelectric coefficient p of 656 μC m-2 K-1 and figures of merit F i, F v, and F d reaching 233 pm/V, 0.013 m2/C, and 7.61 μPa-1/2, respectively, indicating that 5ST ceramic is a promising candidate to replace PZT-based ceramics.

Fracture resistance of aluminium oxide and lithium disilicate-based crowns using different luting cements: an in vitro study.

PubMed

Al-Wahadni, Ahed M; Hussey, David L; Grey, Nicholas; Hatamleh, Muhanad M

2009-03-01

The aim of this study was to investigate the fracture resistance of two types of ceramic crowns cemented with two different cements. Forty premolar crowns were fabricated using lithium-disilicate (IPS Empress-2) and glass-infiltrated aluminium-oxide (In-Ceram) ceramic systems. The crowns were divided into four groups (n=10) with Group 1 (IPS Empress-2) and Group 2 (In-Ceram) cemented with glass ionomer cement. Group 3 (IPS Empress-2) and Group 4 (In-Ceram) were cemented with resin cement. Crowns were tested in a universal testing machine at a compressive-load speed of 10 mm/min. Fracture modes were grouped into five categories. One way analysis of variance (ANOVA) and Bonferroni post-hoc tests were used to detect statistical significances (p<0.05). The mean (SD) fracture resistance (Newtons) for Groups 1 to 4 were: 245.35 (82.69), 390.48 (67.03), 269.69 (10.33), and 418.36 (26.24). The cement type had no statistical significant effect (p>0.05) on fracture resistance within each ceramic system tested. In-Ceram crowns cemented with either glass ionomer or resin cements exhibited a statistically significantly higher fracture-resistance than IPS Empress-2 crowns (p<0.05). Minimal fracture in the test crowns was the common mode exhibited. Fracture resistance of IPS Empress-2 and In-Ceram crowns was not affected by the type of cement used for luting. Both In-Ceram and IPS Empress-2 crowns can be successfully luted with the cements tested with In-Ceram exhibiting higher fracture resistance than IPS Empress-2.

Three- to nine-year survival estimates and fracture mechanisms of zirconia- and alumina-based restorations using standardized criteria to distinguish the severity of ceramic fractures.

PubMed

Moráguez, Osvaldo D; Wiskott, H W Anselm; Scherrer, Susanne S

2015-12-01

The aims of this study were set as follows: 1. To provide verifiable criteria to categorize the ceramic fractures into non-critical (i.e., amenable to polishing) or critical (i.e., in need of replacement) 2. To establish the corresponding survival rates for alumina and zirconia restorations 3. To establish the mechanism of fracture using fractography Fifty-eight patients restored with 115 alumina-/zirconia-based crowns and 26 zirconia-based fixed dental prostheses (FDPs) were included. Ceramic fractures were classified into four types and further subclassified into "critical" or "non-critical." Kaplan-Meier survival estimates were calculated for "critical fractures only" and "all fractures." Intra-oral replicas were taken for fractographic analyses. Kaplan-Meier survival estimates for "critical fractures only" and "all fractures" were respectively: Alumina single crowns: 90.9 and 68.3 % after 9.5 years (mean 5.71 ± 2.6 years). Zirconia single crowns: 89.4 and 80.9 % after 6.3 years (mean 3.88 ± 1.2 years). Zirconia FDPs: 68.6 % (critical fractures) and 24.6 % (all fractures) after 7.2 and 4.6 years respectively (FDP mean observation time 3.02 ± 1.4 years). No core/framework fractures were detected. Survival estimates varied significantly depending on whether "all" fractures were considered as failures or only those deemed as "critical". For all restorations, fractographic analyses of failed veneering ceramics systematically demonstrated heavy occlusal wear at the failure origin. Therefore, the relief of local contact pressures on unsupported ceramic is recommended. Occlusal contacts on mesial or distal ridges should systematically be eliminated. A classification standard for ceramic fractures into four categories with subtypes "critical" and "non-critical" provides a differentiated view of the survival of ceramic restorations.

Additive Manufacturing of Silicon Carbide-Based Ceramic Matrix Composites: Technical Challenges and Opportunities

NASA Technical Reports Server (NTRS)

Singh, Mrityunjay; Halbig, Michael C.; Grady, Joseph E.

2016-01-01

Advanced SiC-based ceramic matrix composites offer significant contributions toward reducing fuel burn and emissions by enabling high overall pressure ratio (OPR) of gas turbine engines and reducing or eliminating cooling air in the hot-section components, such as shrouds, combustor liners, vanes, and blades. Additive manufacturing (AM), which allows high value, custom designed parts layer by layer, has been demonstrated for metals and polymer matrix composites. However, there has been limited activity on additive manufacturing of ceramic matrix composites (CMCs). In this presentation, laminated object manufacturing (LOM), binder jet process, and 3-D printing approaches for developing ceramic composite materials are presented. For the laminated object manufacturing (LOM), fiber prepreg laminates were cut into shape with a laser and stacked to form the desired part followed by high temperature heat treatments. For the binder jet, processing optimization was pursued through silicon carbide powder blending, infiltration with and without SiC nano powder loading, and integration of fibers into the powder bed. Scanning electron microscopy was conducted along with XRD, TGA, and mechanical testing. Various technical challenges and opportunities for additive manufacturing of ceramics and CMCs will be presented.

Development of ASTM Standard for SiC-SiC Joint Testing Final Scientific/Technical Report

DOE Office of Scientific and Technical Information (OSTI.GOV)

Jacobsen, George; Back, Christina

2015-10-30

As the nuclear industry moves to advanced ceramic based materials for cladding and core structural materials for a variety of advanced reactors, new standards and test methods are required for material development and licensing purposes. For example, General Atomics (GA) is actively developing silicon carbide (SiC) based composite cladding (SiC-SiC) for its Energy Multiplier Module (EM2), a high efficiency gas cooled fast reactor. Through DOE funding via the advanced reactor concept program, GA developed a new test method for the nominal joint strength of an endplug sealed to advanced ceramic tubes, Fig. 1-1, at ambient and elevated temperatures called themore » endplug pushout (EPPO) test. This test utilizes widely available universal mechanical testers coupled with clam shell heaters, and specimen size is relatively small, making it a viable post irradiation test method. The culmination of this effort was a draft of an ASTM test standard that will be submitted for approval to the ASTM C28 ceramic committee. Once the standard has been vetted by the ceramics test community, an industry wide standard methodology to test joined tubular ceramic components will be available for the entire nuclear materials community.« less

XRD investigation of the Effect of MgO Additives on ZTA-TiO2 Ceramic Composites

NASA Astrophysics Data System (ADS)

Azhar, Ahmad Zahirani Ahmad; Manshor, Hanisah; Ali, Afifah Mohd

2018-01-01

Alumina (Al2O3) based ceramics possess good mechanical properties and suitable for the application of cutting inserts. However, this monolithic ceramics suffer from lack of toughness. Hence, there are some modification were made such as the addition of yttria stabilized zirconia (YSZ) to the Al2O3 helps in increasing the toughness of the Al2O3 ceramics. Some additives such as MgO and TiO2 were used to further improve the mechanical properties of ZTA. In this study, high purity raw materials which consist of ZTA-TiO2 were mixed with different amount of MgO (0.0 - 1.0 wt %). The mixture of materials was going through wet mixing, compaction and pressureless sintering at 1600°C for one hour. The samples were characterized for phase analysis, microstructure, shrinkage rate, bulk density, Vickers hardness and fracture toughness. Based on the XRD analysis results, the secondary phase (MgAl2O4) was detected in the sample with 0.5 wt% of MgO onwards which leads to grains refinement, thus improve the density and hardness of ZTA-TiO2-MgO ceramics composites.

Dental cutting behaviour of mica-based and apatite-based machinable glass-ceramics.

PubMed

Taira, M; Wakasa, K; Yamaki, M; Matsui, A

1990-09-01

Some recently developed industrial ceramics have excellent machinability properties. The objective of this study was to evaluate the dental cutting behaviour of two machinable glass-ceramics, mica-containing Macor-M and apatite- and diopside-containing Bioram-M, and to compare them with the cutting behaviour of a composite resin typodont tooth enamel and bovine enamel. Weight-load cutting tests were conducted, using a diamond point driven by an air-turbine handpiece, While the transverse load applied on the point was varied, the handpiece speed during cutting and the volume of removal upon cutting were measured. In general, an increase in the applied load caused a decrease in cutting speed and an increase in cutting volume. However, the intensity of this trend was found to differ between four workpieces. Cutting Macor-M resulted in the second-most reduced cutting speed and the maximum cutting volume. Cutting Bioram-M gave the least reduced cutting speed and the minimum cutting volume. It was suggested that two machinable glass-ceramics could be employed as typodont teeth. This study may also contribute to the development of new restorative dental ceramic materials, prepared by machining.

Thick-film nickel-metal-hydride battery based on porous ceramic substrates

NASA Astrophysics Data System (ADS)

Do, Jing-Shan; Yu, Sen-Hao; Cheng, Suh-Fen

Nickel-metal-hydride (Ni-MH) batteries are prepared with thick-film and thin-film technologies based on porous ceramic substrates. The porosity and the mean pore diameter of BP ceramic substrates prepared from the argils increases from 19.81% and 0.0432 μm to 29.81% and 0.224 μm, respectively, upon increasing the ethyl cellulose content in the BP argil from 0 to 0.79%. The pore diameter of Al 2O 3 substrates prepared from Al 2O 3 powder is mainly distributed in the range 0.01-0.5 μm. The distribution of the pore diameters of BP ceramic substrates lies in two ranges, namely: 0.04-2 μm and 10-300 μm. Using BP ceramic plates and Al 2O 3 plates as substrates to fabricate thick-film Ni-MH batteries, the optimal electroactive material utilization in the batteries is 77.0 and 71.1%, respectively. On increasing the screen-printing number for preparing the cathode (Ni(OH) 2) from 1 to 3, the discharge capacity of the thick-film battery increases from 0.2917 to 0.7875 mAh, and the utilization in the battery decreases from 71.0 to 53.0%.

Ceramic-like open-celled geopolymer foam as a porous substrate for water treatment catalyst

NASA Astrophysics Data System (ADS)

Kovářík, T.; Křenek, T.; Pola, M.; Rieger, D.; Kadlec, J.; Franče, P.

2017-02-01

This paper presents results from experimental study on microstructural and mechanical properties of geopolymer-based foam filters. The process for making porous ceramic-like geopolymer body was experimentally established, consists of (a) geopolymer paste synthesis, (b) ceramic filler incorporation, (c) coating of open-celled polyurethane foam with geopolymer mixture, (d) rapid setting procedure, (e) thermal treatment. Geopolymer paste was based on potassium silicate solution n(SiO2)/n(K2O)=1.6 and powder mixture of calcined kaolin and precipitated silica. Various types of ceramic granular filler (alumina, calcined schistous clay and cordierite) were tested in relation to aggregate gradation design and particle size distribution. The small amplitude oscillatory rheometry in strain controlled regime 0.01% with angular frequency 10 rad/s was applied for determination of rheology behavior of prepared mixtures. Thermal treatment conditions were applied in the temperature range 1100 - 1300 °C. The developed porous ceramic-like foam effectively served as a substrate for highly active nanoparticles of selected Fe+2 spinels. Such new-type of nanocomposite was tested as a heterogeneous catalyst for technological process of advanced oxidative degradation of resistive antibiotics occurring in waste waters.

Modeling the Nonlinear, Strain Rate Dependent Deformation of Woven Ceramic Matrix Composites With Hydrostatic Stress Effects Included

NASA Technical Reports Server (NTRS)

Goldberg, Robert K.; Carney, Kelly S.

2004-01-01

An analysis method based on a deformation (as opposed to damage) approach has been developed to model the strain rate dependent, nonlinear deformation of woven ceramic matrix composites with a plain weave fiber architecture. In the developed model, the differences in the tension and compression response have also been considered. State variable based viscoplastic equations originally developed for metals have been modified to analyze the ceramic matrix composites. To account for the tension/compression asymmetry in the material, the effective stress and effective inelastic strain definitions have been modified. The equations have also been modified to account for the fact that in an orthotropic composite the in-plane shear stiffness is independent of the stiffness in the normal directions. The developed equations have been implemented into a commercially available transient dynamic finite element code, LS-DYNA, through the use of user defined subroutines (UMATs). The tensile, compressive, and shear deformation of a representative plain weave woven ceramic matrix composite are computed and compared to experimental results. The computed values correlate well to the experimental data, demonstrating the ability of the model to accurately compute the deformation response of woven ceramic matrix composites.

Shear Bond Strength of Ceramic Brackets with Different Base Designs: Comparative In-vitro Study

PubMed Central

Ansari, Mohd. Younus; Agarwal, Deepak K; Bhattacharya, Preeti; Ansar, Juhi; Bhandari, Ravi

2016-01-01

Introduction Knowledge about the Shear Bond Strength (SBS) of ceramic brackets with different base design is essential as it affects bond strength to enamel. Aim The aim of the present study was to evaluate and compare the effect of base designs of different ceramic brackets on SBS, and to determine the fracture site after debonding. Materials and Methods Four groups of ceramic brackets and one group of metal brackets with different base designs were used. Adhesive precoated base of Clarity Advanced (APC Flash-free) (Unitek/3M, Monrovia, California), microcrystalline base of Clarity Advanced (Unitek/3M, Monrovia, California), polymer mesh base of InVu (TP Orthodontics, Inc., La Porte, IN, United States), patented bead ball base of Inspire Ice (Ormco, Glendora, California), and a mechanical mesh base of Gemini Metal bracket (Unitek/3M, Monrovia, California). Ten brackets of each type were bonded to 50 maxillary premolars with Transbond XT (Unitek/3M). Samples were stored in distilled water at room temperature for 24 hours and subsequently tested in shear mode on a universal testing machine (Model 3382; Instron Corp., Canton, Massachusetts, USA) at a cross head speed of 1mm/minute with the help of a chisel. The debonded interface was recorded and analyzed to determine the predominant bond failure site under an optical microscope (Stereomicroscope) at 10X magnification. One way analysis of variance (ANOVA) was used to compare SBS. Tukey’s significant differences tests were used for post-hoc comparisons. The Adhesive Remnant Index (ARI) scores were compared by chi-square test. Results Mean SBS of microcrystalline base (27.26±1.73), was the highest followed by bead ball base (23.45±5.09), adhesive precoated base (20.13±5.20), polymer mesh base (17.54±1.91), and mechanical mesh base (17.50±2.41) the least. Comparing the frequency (%) of ARI Score among the groups, chi-square test showed significantly different ARI scores among the groups (χ2 = 34.07, p<0.001). Conclusion Different base designs of metal and ceramic brackets influence SBS to enamel and all were clinically acceptable. PMID:28050507

Method of processing "BPS" glass ceramic and seals made therewith

DOEpatents

Reed, Scott T.; Stone, Ronald G.; McCollister, Howard L.; Wengert, deceased, Paul R.

1998-01-01

A glass ceramic composition, a glass ceramic-to-metal seal, and more specifically a hermetic glass ceramic-to-metal seal prepared by subjecting a glass composition comprising, by weight percent, SiO.sub.2 (65-80%), LiO.sub.2 (8-16%), Al.sub.2 O.sub.3 (2-8%), K.sub.2 O (1-8%), P.sub.2 O.sub.5 (1-5%), B.sub.2 O.sub.3 (0.5-7%), and ZnO (0-5%) to the following processing steps: 1) heating the glass composition in a belt furnace to a temperature sufficient to melt the glass and crystallize lithium phosphate, 2) holding at a temperature and for a time sufficient to create cristobalite nuclei, 3) cooling at a controlled rate and to a temperature to cause crystallization of lithium silicates and growth of cristobalite, and 4) still further cooling in stages to ambient temperature. This process produces a glass ceramic whose high coefficient of thermal expansion (up to 200.times.10.sup.-7 in/in/.degree.C.) permits the fabrication of glass ceramic-to-metal seals, and particularly hermetic glass ceramic seals to nickel-based and stainless steel alloys and copper.

Ga2O3 doping and vacancy effect in KNN—LT lead-free piezoceramics

NASA Astrophysics Data System (ADS)

Tan, Zhi; Xing, Jie; Jiang, Laiming; Zhu, Jianguo; Wu, Bo

2017-12-01

Ga2O3 was doped into 0.95(K0.48Na0.52)NbO3—0.05LiTaO3 (KNN—LT) ceramics and its influences on the sintering behavior, phase structure and electrical properties of ceramics were studied. Firstly, SEM observation exhibits that more and more glass phase appears in ceramics with the gradual addition of Ga2O3, which determines the continuous decrease in sintering temperatures. And the addition of Ga2O3 is also found to increase the orthorhombic—tetragonal transition temperature ( T O—T) of system to a higher level. Secondly, both the density and the coercive field ( E C) of ceramics increase firstly and then decrease with increasing the Ga2O3 content, and the KNN—LT— xGa sample at x = 0.004 shows a pinched P— E hysteresis loop. Finally, the impedance characteristics of KNN—LT— xGa ceramics were investigated at different temperatures, revealing a typical vacancy related conduction mechanism. This work demonstrates that Ga2O3 is a good sintering aid for KNN-based ceramics, and the vacancy plays an important role in the sintering and electrical behaviors of ceramics.

Laboratory evaluations on thermal debonding of ceramic brackets.

PubMed

Sernetz, F; Kraut, J

1991-01-01

The purpose of this laboratory study was to define the working parameters and physiological safety and efficacy of the Dentaurum Ceramic Debonding Unit. Extracted mandibular incisors were utilized because of their low thermal mass and low heat sensitivity. The teeth were embedded in plastic and placed on a turning force measuring apparatus. An electrothermal element was placed in the pulp chamber (filled with a conducting paste). The thermoelement temperature was registered on y-t recorder as was the turning momentum required to remove the ceramic brackets with the Dentaurum Ceramic Debonding Unit. Ceramic brackets from GAC (Allure III), Unitek (Transcend) and Dentaurum (Fascination) using one and two component adhesives (Monolok, Concise), were tested. Scanning electron microscopic views taken after debonding showed predictable (and favorable) adhesive failure at the bracket base/resin interface. No enamel damage was demonstrated. All brackets were removable under three seconds with a clinically reproducible turning force of 85-100 Nmm allowing for intrapulpal temperature increases under the 5 degrees C biocompatible threshold. The Dentaurum Ceramic Debonding Unit provided a safe, reliable, efficient modality of removing ceramic brackets while maintaining a physiologically acceptable rise in pulpal temperature without damage to tooth enamel or pulpal tissue.