The influence of SrO and CaO in silicate and phosphate bioactive glasses on human gingival fibroblasts.

PubMed

Massera, J; Kokkari, A; Närhi, T; Hupa, L

2015-06-01

In this paper, we investigate the effect of substituting SrO for CaO in silicate and phosphate bioactive glasses on the human gingival fibroblast activity. In both materials the presence of SrO led to the formation of a CaP layer with partial Sr substitution for Ca. The layer at the surface of the silicate glass consisted of HAP whereas at the phosphate glasses it was close to the DCPD composition. In silicate glasses, SrO gave a faster initial dissolution and a thinner reaction layer probably allowing for a continuous ion release into the solution. In phosphate glasses, SrO decreased the dissolution process and gave a more strongly bonded reaction layer. Overall, the SrO-containing silicate glass led to a slight enhancement in the activity of the gingival fibroblasts cells when compared to the SrO-free reference glass, S53P4. The cell activity decreased up to 3 days of culturing for all phosphate glasses containing SrO. Whereas culturing together with the SrO-free phosphate glass led to complete cell death at 7 days. The glasses containing SrO showed rapid cell proliferation and growth between 7 and 14 days, reaching similar activity than glass S53P4. The addition of SrO in both silicate and phosphate glasses was assumed beneficial for proliferation and growth of human gingival fibroblasts due to Sr incorporation in the reaction layer at the glass surface and released in the cell culture medium.

Intermediate-range order in simple metal-phosphate glasses: The effect of metal cations on the phosphate anion distribution

DOE Office of Scientific and Technical Information (OSTI.GOV)

Sales, B.C.; Boatner, L.A.; Ramey, J.O.

1997-06-01

The technique of high-performance liquid chromatography (HPLC) has been used to probe the phosphate anion distribution in a variety of metal phosphate glasses including glasses made with trivalent metal cations (Al, In, Ga, La). The composition of each glass was chosen so that the average phosphate chain length was between 2 and 4 PO{sub 4} tetrahedra. The widths of the resulting phosphate anion distributions were determined directly from an analysis of the HPLC chromatograms. Literature values for the free energy of formation of the crystalline metal-orthophosphate compounds with respect to P{sub 2}O{sub 5} and the metal oxide, were compared tomore » the chromatogram widths. It was found that the smaller the energy of formation, the wider the distribution of phosphate chains, and the greater the ease of glass formation.« less

Phosphate glasses for radioactive, hazardous and mixed waste immobilization

DOEpatents

Cao, H.; Adams, J.W.; Kalb, P.D.

1999-03-09

Lead-free phosphate glass compositions are provided which can be used to immobilize low level and/or high level radioactive wastes in monolithic waste forms. The glass composition may also be used without waste contained therein. Lead-free phosphate glass compositions prepared at about 900 C include mixtures from about 1 mole % to about 6 mole % iron (III) oxide, from about 1 mole % to about 6 mole % aluminum oxide, from about 15 mole % to about 20 mole % sodium oxide or potassium oxide, and from about 30 mole % to about 60 mole % phosphate. The invention also provides phosphate, lead-free glass ceramic glass compositions which are prepared from about 400 C to about 450 C and which includes from about 3 mole % to about 6 mole % sodium oxide, from about 20 mole % to about 50 mole % tin oxide, from about 30 mole % to about 70 mole % phosphate, from about 3 mole % to about 6 mole % aluminum oxide, from about 3 mole % to about 8 mole % silicon oxide, from about 0.5 mole % to about 2 mole % iron (III) oxide and from about 3 mole % to about 6 mole % potassium oxide. Method of making lead-free phosphate glasses are also provided. 8 figs.

Phosphate glasses for radioactive, hazardous and mixed waste immobilization

DOEpatents

Cao, Hui; Adams, Jay W.; Kalb, Paul D.

1998-11-24

Lead-free phosphate glass compositions are provided which can be used to immobilize low level and/or high level radioactive wastes in monolithic waste forms. The glass composition may also be used without waste contained therein. Lead-free phosphate glass compositions prepared at about 900.degree. C. include mixtures from about 1 mole % to about 6 mole % iron (III) oxide, from about 1 mole % to about 6 mole % aluminum oxide, from about 15 mole % to about 20 mole % sodium oxide or potassium oxide, and from about 30 mole % to about 60 mole % phosphate. The invention also provides phosphate, lead-free glass ceramic glass compositions which are prepared from about 400.degree. C. to about 450.degree. C. and which includes from about 3 mole % to about 6 mole % sodium oxide, from about 20 mole % to about 50 mole % tin oxide, from about 30 mole % to about 70 mole % phosphate, from about 3 mole % to about 6 mole % aluminum oxide, from about 3 mole % to about 8 mole % silicon oxide, from about 0.5 mole % to about 2 mole % iron (III) oxide and from about 3 mole % to about 6 mole % potassium oxide. Method of making lead-free phosphate glasses are also provided.

Phosphate glasses for radioactive, hazardous and mixed waste immobilization

DOEpatents

Cao, Hui; Adams, Jay W.; Kalb, Paul D.

1999-03-09

Lead-free phosphate glass compositions are provided which can be used to immobilize low level and/or high level radioactive wastes in monolithic waste forms. The glass composition may also be used without waste contained therein. Lead-free phosphate glass compositions prepared at about 900.degree. C. include mixtures from about 1 mole % to about 6 mole %.iron (III) oxide, from about 1 mole % to about 6 mole % aluminum oxide, from about 15 mole % to about 20 mole % sodium oxide or potassium oxide, and from about 30 mole % to about 60 mole % phosphate. The invention also provides phosphate, lead-free glass ceramic glass compositions which are prepared from about 400.degree. C. to about 450.degree. C. and which includes from about 3 mole % to about 6 mole % sodium oxide, from about 20 mole % to about 50 mole % tin oxide, from about 30 mole % to about 70 mole % phosphate, from about 3 mole % to about 6 mole % aluminum oxide, from about 3 mole % to about 8 mole % silicon oxide, from about 0.5 mole % to about 2 mole % iron (III) oxide and from about 3 mole % to about 6 mole % potassium oxide. Method of making lead-free phosphate glasses are also provided.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Joseph, Kitheri; Stennett, Martin C.; Hyatt, Neil C.

Bulk properties such as glass transition temperature, density and thermal expansion of iron phosphate glass compositions, with replacement of Cs by Ba, are investigated as a surrogate for the transmutation of 137Cs to 137Ba, relevant to the immobilisation of Cs in glass. These studies are required to establish the appropriate incorporation rate of 137Cs in iron phosphate glass. Density and glass transition temperature increases with the addition of BaO indicating the shrinkage and reticulation of the iron phosphate glass network. The average thermal expansion coefficient reduces from 19.8 × 10-6 K-1 to 13.4 × 10-6 K-1, when 25 wt. %more » of Cs2O was replaced by 25 wt. % of BaO in caesium loaded iron phosphate glass. In addition to the above bulk properties, the role of Ba as a network modifier in the structure of iron phosphate glass is examined using various spectroscopic techniques. The FeII content and average coordination number of iron in the glass network was estimated using Mössbauer spectroscopy. The FeII content in the un-doped iron phosphate glass and barium doped iron phosphate glasses was 20, 21 and 22 ± 1% respectively and the average Fe coordination varied from 5.3 ± 0.2 to 5.7 ± 0.2 with increasing Ba content. The atomic scale structure was further probed by Fe K-edge X-ray absorption spectroscopy. The average coordination number provided by extended X-ray absorption fine structure spectroscopy and X-ray absorption near edge structure was in good agreement with that given by the Mössbauer data.« less

Glass formation and crystallization in the alumina-silica-lanthanum phosphate system for ceramics composites

NASA Astrophysics Data System (ADS)

Guo, Shuling

The formation, structure, and dynamics of glasses in the alumina-silica-lanthanum phosphate system and their crystallization were investigated as a function of composition. These are of interest because of their potential as precursors for synthesizing ceramic-matrix-composites via co-crystallization of lanthanum monazite and either mullite or alumina into finely mixed microstructures. The glasses were characterized by X-Ray Diffraction (XRD), Raman spectroscopy, Differential Scanning Calorimetry (DSC), Nuclear Magnetic Resonance (NMR), Scanning Electron Microscopy (SEM), Transmission Electron Microscopy (TEM), and Electron Energy Loss Spectrometry (EELS). Glass formation from rapidly quenched liquids was easiest and most consistent for compositions containing silica, such as for mullitemonazite compositions, and more difficult for alumina-monazite compositions. For mullite-monazite glasses, the glass transition temperatures increased linearly from 845°C to 906°C with increasing mullite content. An analysis of the glass structure indicated a network consisting of corner-linked aluminate, silicate and phosphate tetrahedra where aluminum played a central role of separating silicon and phosphorous. It was hypothesized that the glass network consisted of domains of aluminum silicate network edged by phosphate tetrahedra. A maximum in the crystallization temperature was attributed to the complexity of the glass network. At relatively mullite-rich compositions, simultaneous and cooperative crystallization of lanthanum phosphate and mullite correlated with the highest crystallization temperatures, and the lowest activation energies of crystallization. This was preceded by amorphous phase segregation in the glass at lower temperatures. An intermediate phase of lanthanum phosphate was discovered with an orthorhombic unit cell. For compositions of high phosphate contents, lanthanum phosphate precipitated first at about 900°C leaving an essentially pure mullite glass. Mullite crystallized at about 1000°C, matching the conditions for crystallizing pure mullite glass. The phosphate phase transformed to monazite at even higher temperatures. No amorphous phase segregation was observed in these cases. Microstructures were correlated with nucleation and growth conditions such that the continuous and isolated phases could be manipulated. Optimum nucleation temperatures were close to the glass transition temperature. Conditions were identified for forming a continuous boundary phase of monazite that isolated mullite grains, which is desired for fabricating ceramic-matrix-composites.

Ammonia-treated phosphate glasses useful for sealing to metals metals

DOEpatents

Brow, Richard K.; Day, Delbert E.

1991-01-01

A method of improving surface-dependent properties of phosphate glass such as durability and wear resistance without significantly affecting its thermal expansion coefficient is provided which comprises annealing the glass in a dry ammonia atmosphere at temperatures approximating the transition temperature of the glass. The ammonia annealing treatment of the present invention is carried out for a time sufficient to allow incorporation of a thin layer of nitrogen into the surface of the phosphate glass, and the treatment improves the durability of the glass without the reduction in the thermal expansion coefficient that has restricted the effectiveness of prior ammonia treatments. The improved phosphate glass resulting from this method is superior in wear resistance, yet maintains suitable thermal expansion properties so that it may be used effectively in a variety of applications requiring hermetic glass-metal seals.

Ammonia-treated phosphate glasses useful for sealing to metals

DOEpatents

Brow, R.K.; Day, D.E.

1991-09-03

A method of improving surface-dependent properties of phosphate glass such as durability and wear resistance without significantly affecting its thermal expansion coefficient is provided which comprises annealing the glass in a dry ammonia atmosphere at temperatures approximating the transition temperature of the glass. The ammonia annealing treatment of the present invention is carried out for a time sufficient to allow incorporation of a thin layer of nitrogen into the surface of the phosphate glass, and the treatment improves the durability of the glass without the reduction in the thermal expansion coefficient that has restricted the effectiveness of prior ammonia treatments. The improved phosphate glass resulting from this method is superior in wear resistance, yet maintains suitable thermal expansion properties so that it may be used effectively in a variety of applications requiring hermetic glass-metal seals.

DOE Office of Scientific and Technical Information (OSTI.GOV)

ALAM,TODD M.

Monte Carlo simulations of phosphate tetrahedron connectivity distributions in alkali and alkaline earth phosphate glasses are reported. By utilizing a discrete bond model, the distribution of next-nearest neighbor connectivities between phosphate polyhedron for random, alternating and clustering bonding scenarios was evaluated as a function of the relative bond energy difference. The simulated distributions are compared to experimentally observed connectivities reported for solid-state two-dimensional exchange and double-quantum NMR experiments of phosphate glasses. These Monte Carlo simulations demonstrate that the polyhedron connectivity is best described by a random distribution in lithium phosphate and calcium phosphate glasses.

Ultraviolet optical absorptions of semiconducting copper phosphate glasses

NASA Technical Reports Server (NTRS)

Bae, Byeong-Soo; Weinberg, Michael C.

1993-01-01

Results are presented of a quantitative investigation of the change in UV optical absorption in semiconducting copper phosphate glasses with batch compositions of 40, 50, and 55 percent CuO, as a function of the Cu(2+)/Cu(total) ratio in the glasses for each glass composition. It was found that optical energy gap, E(opt), of copper phosphate glass is a function of both glass composition and Cu(2+)/Cu(total) ratio in the glass. E(opt) increases as the CuO content for fixed Cu(2+)/Cu(total) ratio and the Cu(2+)/Cu(total) ratio for fixed glass composition are reduced.

Lead-iron phosphate glass as a containment medium for the disposal of high-level nuclear wastes

DOEpatents

Boatner, L.A.; Sales, B.C.

1984-04-11

Disclosed are lead-iron phosphate glasses containing a high level of Fe/sub 2/O/sub 3/ for use as a storage medium for high-level radioactive nuclear waste. By combining lead-iron phosphate glass with various types of simulated high-level nuclear waste

Modelling aqueous corrosion of nuclear waste phosphate glass

NASA Astrophysics Data System (ADS)

Poluektov, Pavel P.; Schmidt, Olga V.; Kascheev, Vladimir A.; Ojovan, Michael I.

2017-02-01

A model is presented on nuclear sodium alumina phosphate (NAP) glass aqueous corrosion accounting for dissolution of radioactive glass and formation of corrosion products surface layer on the glass contacting ground water of a disposal environment. Modelling is used to process available experimental data demonstrating the generic inhibiting role of corrosion products on the NAP glass surface.

Further damage induced by water in micro-indentations in phosphate laser glass

NASA Astrophysics Data System (ADS)

Yu, Jiaxin; Jian, Qingyun; Yuan, Weifeng; Gu, Bin; Ji, Fang; Huang, Wen

2014-02-01

Using a microhardness tester, artificial flaws were made by micro-indentation in N31 Nd-doped phosphate laser glass. Indentation fracture toughness, KIC, was estimated as 0.45-0.53 MPa m1/2 from these indentations. The glasses with indentations were then immersed in ultrapure water to investigate further water-induced damage of these indentations. Stress-enhanced hydrolysis leads to the propagations of radial crack, lateral cracks and microcracks in the subsurface. These crack propagations therefore cause deformation in subsurface to form annular reflections regions around the indentations and further material collapse within imprints. After the residual stresses are exhausted, the leaching plays a more dominated role in glass corrosion in the further immersion. After immersion, the material structure slackens around micro-indentation, which decreases the contact stiffness and results in a lower nano-hardness. For the surface far away from flaws, water immersion presents a weak effect on the near-surface mechanical since the matrix leaching in phosphate glass restricts the formation of hydration layer. During first 20 min immersion, due to higher chemical activity and lower fracture toughness, the radial cracks show a faster propagation in phosphate glass compared with that in K9 silicate glass. For further immersion, crack healing occurs in silicate glass but not in phosphate glass. Analysis shows that the formation of hydration layer on crack walls plays an important role in crack healing in glasses.

Magnesium-phosphate-glass cements with ceramic-type properties

DOEpatents

Sugama, T.; Kukacka, L.E.

1982-09-23

Rapid setting magnesium phosphate (Mg glass) cementitious materials consisting of magnesium phosphate cement paste, polyborax and water-saturated aggregate, exhibits rapid setting and high early strength characteristics. The magnesium glass cement is prepared from a cation-leachable powder and a bivalent metallic ion-accepting liquid such as an aqueous solution of diammonium phosphate and ammonium polyphosphate. The cation-leachable powder includes a mixture of two different magnesium oxide powders processed and sized differently which when mixed with the bivalent metallic ion-accepting liquid provides the magnesium glass cement consisting primarily of magnesium ortho phosphate tetrahydrate, with magnesium hydroxide and magnesium ammonium phosphate hexahydrate also present. The polyborax serves as a set-retarder. The resulting magnesium mono- and polyphosphate cements are particularly suitable for use as a cementing matrix in rapid repair systems for deteriorated concrete structures as well as construction materials and surface coatings for fireproof structures.

Magnesium phosphate glass cements with ceramic-type properties

DOEpatents

Sugama, Toshifumi; Kukacka, Lawrence E.

1984-03-13

Rapid setting magnesium phosphate (Mg glass) cementitious materials consisting of magnesium phosphate cement paste, polyborax and water-saturated aggregate exhibiting rapid setting and high early strength characteristics. The magnesium glass cement is prepared from a cation-leachable powder and a bivalent metallic ion-accepting liquid such as an aqueous solution of diammonium phosphate and ammonium polyphosphate. The cation-leachable powder includes a mixture of two different magnesium oxide powders processed and sized differently which when mixed with the bivalent metallic ion-accepting liquid provides the magnesium glass cement consisting primarily of magnesium ortho phosphate tetrahydrate, with magnesium hydroxide and magnesium ammonium phosphate hexahydrate also present. The polyborax serves as a set-retarder. The resulting magnesium mono- and polyphosphate cements are particularly suitable for use as a cementing matrix in rapid repair systems for deteriorated concrete structures as well as construction materials and surface coatings for fireproof structures.

CADMIUM PHOSPHATE GLASS

DOEpatents

Carpenter, H.W.; Johnson, P.D.

1963-04-01

A method of preparing a cadmium phosphate glass that comprises providing a mixture of solid inorganic compounds of cadmuim and phosphate having vaporizable components and heating the resulting composition to a temperature of at least 850 un. Concent 85% C is presented. (AEC)

Alkaline resistant phosphate glasses and method of preparation and use thereof

DOEpatents

Brow, Richard K.; Reis, Signo T.; Velez, Mariano; Day, Delbert E.

2010-01-26

A substantially alkaline resistant calcium-iron-phosphate (CFP) glass and methods of making and using thereof. In one application, the CFP glass is drawn into a fiber and dispersed in cement to produce glass fiber reinforced concrete (GFRC) articles having the high compressive strength of concrete with the high impact, flexural and tensile strength associated with glass fibers.

Structural features of silver-doped phosphate glasses in zone of femtosecond laser-induced modification

DOE Office of Scientific and Technical Information (OSTI.GOV)

Vasileva, A.A., E-mail: anvsilv@gmail.com; Nazarov, I.A.; Olshin, P.K.

2015-10-15

Femtosecond (fs) laser writing of two-dimensional microstructures (waveguides) is demonstrated in bulk phosphate glasses doped with silver ions. Silver-content phosphate and silver-content niobium–phosphate glasses with high concentration of silver oxide 55 mol% were used as samples for fs laser writing. The chemical network structure of the synthesized samples is analyzed through Raman spectroscopy and was found to be strongly sensitive to Nb incorporation. It was found that the direct laser writing process enables not only reorganization of glass network, but also formation of color centers and silver nanoparticles that are revealed in appearance of luminescence signal and plasmon absorption. Themore » process of NPs' formation is more efficient for Nb-phosphate glass, while color centers are preferably formed in phosphate glass. - Graphical abstract: Formation of silver NPs on the surface of 0.5Ag{sub 2}O–0.4P{sub 2}O{sub 5}–0,1Nb{sub 2}O{sub 5} glass induced by CW laser irradiation. - Highlights: • The structure of 0.5Ag{sub 2}O–0.1Nb{sub 2}O{sub 5}–0.4P{sub 2}O{sub 5} and 0.55Ag{sub 2}O–0.45P{sub 2}O{sub 5} glasses was investigated by Raman spectroscopy. • Fs laser writing induces formation of silver NPs in investigated glasses. • Surface plasmon resonance in the absorption spectra confirms the formation of NP. • The possibility of CW laser induced formation of silver NPs on the surface of sample with niobium is shown.« less

Tb3+ and Eu3+ doped zinc phosphate glasses for solid state lighting applications

NASA Astrophysics Data System (ADS)

Jha, Kaushal; Vishwakarma, Amit K.; Jayasimhadri, M.; Haranath, D.; Jang, Kiwan

2018-04-01

Tb3+ and Eu3+ doped zinc phosphate (ZP) glasses were prepared by conventional melt-quenching technique and their photoluminescence properties were investigated in detail. For, Tb3+ doped glasses the intense emission was at 545 nm corresponding to 5D4→7F5 transition under 377 nm n-UV excitation. The optimized concentration for Tb3+ doped zinc phosphate glass was 3 mol% and above this concentration quenching takes place. The Eu3+ doped zinc phosphate glass revealed intense emission at 613 nm attributed to the 5D0→7F2 transition under intense 392 nm n-UV excitation. The concentration quenching phenomenon was not observed in the Eu3+ doped ZP glasses. The CIE chromaticity coordinates for 3 mol% Tb3+ and 5 mol% Eu3+ doped ZP glasses were found to (0.283, 0.615) and (0.652, 0.331) lying in the green and red regions, respectively. The above mentioned results indicate that the prepared glass are suitable for application in the field of lighting and display devices.

Contrasting two different interpretations of the dynamics in binary glass forming mixtures

NASA Astrophysics Data System (ADS)

Valenti, S.; Capaccioli, S.; Ngai, K. L.

2018-02-01

In a series of papers on binary glass-forming mixtures of tripropyl phosphate (TPP) with polystyrene (PS), Kahlau et al. [J. Chem. Phys. 140, 044509 (2014)] and Bock et al. [J. Chem. Phys. 139, 064508 (2013); J. Chem. Phys. 140, 094505 (2014); and J. Non-Cryst. Solids 407, 88-97 (2015)] presented the data on the dynamics of the two components studied over the entire composition range by several experimental methods. From these sets of data, obtained by multiple experimental techniques on mixtures with a large difference ΔTg ≈ 200 K between the glass transition temperatures of two starting glass formers, they obtained two α-relaxations, α1 and α2. The temperature dependence of the slower α1 is Vogel-Fulcher like, but the faster α2 is Arrhenius. We have re-examined their data and show that their α2-relaxation is the Johari-Goldstein (JG) β-relaxation with Arrhenius T-dependence admixed with a true α2-relaxation having a stronger temperature dependence. In support of our interpretation of their data, we made dielectric measurements at elevated pressures P to show that the ratio of the α1 and α2 relaxation times, τα1(T,P)/τα2(T,P), is invariant to variations of T and P, while τα1(T,P) is kept constant. This property proves unequivocally that the α2-relaxation is the JG β-relaxation, the precursor of the α1-relaxation. Subsequently, the true but unresolved α2-relaxation is recovered, and its relaxation times with much stronger temperature dependence are deduced, as expected for the α-relaxation of the TPP component. The results are fully compatible with those found in another binary mixture of methyltetrahydrofuran with tristyrene and PS with ΔTg ≈ 283 K, even larger than ΔTg ≈ 200 K of the mixture of TPP with PS, and in several polymer blends. The contrast between the two very different interpretations brought out in this paper is deemed beneficial for further progress in this research area.

Ultraviolet and infrared absorption spectra of Cr2O3 doped-sodium metaphosphate, lead metaphosphate and zinc metaphosphate glasses and effects of gamma irradiation: a comparative study.

PubMed

Marzouk, M A; ElBatal, F H; Abdelghany, A M

2013-10-01

The effects of gamma irradiation on spectral properties of Cr2O3-doped phosphate glasses of three varieties, namely sodium metaphosphate, lead metaphosphate and zinc metaphosphate have been investigated. Optical spectra of the undoped samples reveal strong UV absorption bands which are attributed to the presence of trace iron impurities in both the sodium and zinc phosphate glasses while the lead phosphate glass exhibits broad UV near visible bands due to combined absorption of both trace iron impurities and divalent lead ions. The effect of chromium oxide content has been investigated. The three different Cr2O3-doped phosphate glasses reveal spectral visible bands varying in their position and intensity and splitting due to the different field strengths of the Na(+), Pb(2+), Zn(2+) cations, together with the way they are housed in the network and their effects on the polarisability of neighboring oxygens ligands. The effects of gamma irradiation on the optical spectral properties of the various glasses have been compared. The different effects for lead and zinc phosphate are related to the ability of Pb(2+), and Zn(2+) to form additional structural units causing stability of the network towards gamma irradiation. Also, the introduction of the transition metal chromium ions reveals some shielding behavior towards irradiation. Infrared absorption spectra of the three different base phosphate glasses show characteristic vibrations due to various phosphate groups depending on the type of glass and Cr2O3 is observed to slightly affect the IR spectra. Gamma irradiation causes minor variations in some of the intensities of the IR spectra but the main characteristic bands due to phosphate groups remain in their number and position. Copyright © 2013 Elsevier B.V. All rights reserved.

X-ray absorption studies of gamma irradiated Nd doped phosphate glass

NASA Astrophysics Data System (ADS)

Rai, V. N.; Rajput, Parasmani; Jha, S. N.; Bhattacharyya, D.

2015-06-01

This paper presents the X-ray absorption near edge structure (XANES) studies of Nd doped phosphate glasses before and after gamma irradiation. The intensity and location of LIII edge white line peak of Nd changes depending on its concentration as well as on the ratio of O/Nd in the glass matrix. The decrease in the peak intensity of white line after gamma irradiation indicates towards reduction of Nd3+ to Nd2+ in the glass matrix, which increases with an increase in the doses of gamma irradiation. Similarity in the XANES spectra of Nd doped phosphate glasses and Nd2O3 suggests that coordination geometry around Nd3+ in glass samples may be identical to that of Nd2O3.

Potential use of gallium-doped phosphate-based glass material for periodontitis treatment.

PubMed

Sahdev, Rohan; Ansari, Tahera I; Higham, Susan M; Valappil, Sabeel P

2015-07-01

This study aimed at evaluating the potential effect of gallium-incorporated phosphate-based glasses towards periodontitis-associated bacteria, Porphyromonas gingivalis, and matrix metalloproteinase-13. Periodontitis describes a group of inflammatory diseases of the gingiva and supporting structures of the periodontium. They are initiated by the accumulation of plaque bacteria, such as the putative periodontal pathogen Porphyromonas gingivalis, but the host immune response such as elevated matrix metalloproteinases are the major contributing factor for destruction of periodontal tissues. Antibacterial assays of gallium-incorporated phosphate-based glasses were conducted on Porphyromonas gingivalis ATCC 33277 using disc diffusion assay on fastidious anaerobe agar and liquid broth assay in a modified tryptic soy broth. In vitro study investigated the effect of gallium on purified recombinant human matrix metalloproteinase-13 activity using matrix metalloproteinase assay kit. In vivo biocompatibility of gallium-incorporated phosphate-based glass was evaluated in rats as subcutaneous implants. Antibacterial assay of gallium displayed activity against Porphyromonas gingivalis (inhibition zone of 22 ± 0.5 mm compared with 0 mm for control glass, c-PBG). Gallium in the glass contributed to growth inhibitory effect on Porphyromonas gingivalis (up to 1.30 reductions in log 10 values of the viable counts compared with control) in a modified tryptic soy broth. In vitro study showed gallium-incorporated phosphate-based glasses inhibited matrix metalloproteinase activity significantly (p ≤ 0.01) compared with c-PBG. Evaluation of in vivo biocompatibility of gallium-incorporated phosphate-based glasses in rats showed a non-toxic and foreign body response after 2 weeks of implantation. The results indicate that gallium ions might act on multiple targets of biological mechanisms underlying periodontal disease. Moreover, gallium-incorporated phosphate-based glasses are biocompatible in a rat model. The findings warrant further investigation and will have important clinical implications in the future treatment and management of periodontitis. © The Author(s) 2015 Reprints and permissions: sagepub.co.uk/journalsPermissions.nav.

In vitro bioactivity behavior of modified multicomponent borate glasses containing dopants of Ag2O, CuO, CeO2 or V2O5

NASA Astrophysics Data System (ADS)

Marzouk, M. A.; ElBatal, F. H.; Ghoneim, N. A.

2018-02-01

Some multi-component borate glasses containing dopants of Ag2O, CuO, CeO2 or V2O5 were prepared. Multi-characterization techniques were carried out to investigate their bioactivity, corrosion weight loss after immersion in phosphate solution. Controlled thermal heat-treatment by two-step technique was done to convert the prepared glasses to their corresponding glass-ceramic derivatives. X-ray diffraction analysis was performed to identify the crystalline phases formed by thermal treatment. Infrared absorption of glasses and glass-ceramics reveal vibrational bands due to combined main triangular and tetrahedral borate groups in their specific wavenumbers besides some sharing of phosphate group. After immersion in the phosphate solution, two extra characteristic peaks are generated indicating the bioactivity of the studied glasses and glass-ceramics through the formation of calcium phosphate (hydroxyapatite). X-ray diffraction data indicate the formation of crystalline phases which are variable with the introduced dopants. The main crystalline phase identified is calcium borate together with some other phases some of which contain phosphate ions. These data indicate that the presence of CaO and P2O5 initiates phase separation and subsequent crystallization of the parent and doped glasses. Weight loss data indicate that glass-ceramics are obviously durable than the parent glasses. SEM micrographs of glass-ceramics before immersion show multiconstituent crystalline phases due to the basic chemical composition consisting of multicomponent mixed alkali and alkaline earth oxides beside P2O5 and with the main B2O3 constituent. After immersion, the crystalline phases are identified to be more distinct in different shapes because of the multi-composition involved.

Structure-solubility relationships in fluoride-containing phosphate based bioactive glasses

NASA Astrophysics Data System (ADS)

Shaharyar, Yaqoot

The dissolution of fluoride-containing bioactive glasses critically affects their biomedical applications. Most commercial fluoride-releasing bioactive glasses have been designed in the soda-lime-silica system. However, their relatively slow chemical dissolution and the adverse effect of fluoride on their bioactivity are stimulating the study of novel biodegradable materials with higher bioactivity, such as biodegradable phosphate-based bioactive glasses, which can be a viable alternative for applications where a fast release of active ions is sought. In order to design new biomaterials with controlled degradability and high bioactivity, it is essential to understand the connection between chemical composition, molecular structure, and solubility in physiological fluids.Accordingly, in this work we have combined the strengths of various experimental techniques with Molecular Dynamics (MD) simulations, to elucidate the impact of fluoride ions on the structure and chemical dissolution of bioactive phosphate glasses in the system: 10Na2O - (45-x) CaO - 45P2O5 - xCaF2, where x varies between 0 -- 10 mol.%. NMR and MD data reveal that the medium-range atomic-scale structure of thse glasses is dominated by Q2 phosphate units followed by Q1 units, and the MD simulations further show that fluoride tends to associate with network modifier cations to form alkali/alkaline-earth rich ionic aggregates. On a macroscopic scale, we find that incorporating fluoride in phosphate glasses does not affect the rate of apatite formation on the glass surface in simulated body fluid (SBF). However, fluoride has a marked favorable impact on the glass dissolution in deionized water. Similarly, fluoride incorporation in the glasses results in significant weight gain due to adsorption of water (in the form of OH ions). These macroscopic trends are discussed on the basis of the F effect on the atomistic structure of the glasses, such as the F-induced phosphate network re-polymerization, in a first attempt to establish composition-structure-property relationships for these biomaterials.

Ferric oxide quantum dots in stable phosphate glass system and their magneto-optical study

DOE Office of Scientific and Technical Information (OSTI.GOV)

Garaje, Sunil N.; Apte, Sanjay K.; Kumar, Ganpathy

2013-02-15

Graphical abstract: We report synthesis of ferric oxide embedded low melting phosphate glass nanocomposite and also the effect of ferric oxide nanoparticles (NCs) content on the optical and magneto-optical properties of the glasses. Faraday rotation of the glass nanocomposites was measured and showed variation in Verdet constant with concentration of ferric oxide. Interestingly, the host glass itself showed fairly good Verdet constant (11.5°/T cm) and there is a threefold enhancement in the Verdet constant of ferric oxide quantum dot-glass nanocomposite. Highlights: ► We synthesize ferric oxide embedded low melting stable phosphate glass nanocomposite. ► Glasses doped with 0.25 and 2%more » ferric oxide show particle size in the range of 4–12 nm. ► The host phosphate glass itself shows fairly good Verdet constant (11.5°/T cm). ► Glasses doped with 0.25% ferric oxide show high Verdet constant (30.525°/T cm). ► The as synthesis glasses may have potential application in magneto optical devices. -- Abstract: Herein, we report the synthesis of ferric oxide embedded low melting phosphate glass nanocomposite and also the effect of ferric oxide nanoparticles content on the optical and magneto-optical properties of the glasses. The optical study clearly showed red shift in optical cut off with increasing ferric oxide concentration. The band gap of the host glass was observed to be 3.48 eV and it shifted to 3.14 eV after doping with ferric oxide. The glasses doped with 0.25 and 2% ferric oxide showed particle size of 4–6 nm and 8–12 nm, respectively. Faraday rotation of the glass nanocomposites was measured and showed variation in the Verdet constant as per increasing concentration of ferric oxide. Interestingly, the host glass itself showed fairly good Verdet constant (11.5°/T cm) and threefold enhancement was observed in the Verdet constant of ferric oxide quantum dot-glass nanocomposite.« less

Bioactive calcium phosphate-based glasses and ceramics and their biomedical applications: A review.

PubMed

Islam, Md Towhidul; Felfel, Reda M; Abou Neel, Ensanya A; Grant, David M; Ahmed, Ifty; Hossain, Kazi M Zakir

2017-01-01

An overview of the formation of calcium phosphate under in vitro environment on the surface of a range of bioactive materials (e.g. from silicate, borate, and phosphate glasses, glass-ceramics, bioceramics to metals) based on recent literature is presented in this review. The mechanism of bone-like calcium phosphate (i.e. hydroxyapatite) formation and the test protocols that are either already in use or currently being investigated for the evaluation of the bioactivity of biomaterials are discussed. This review also highlights the effect of chemical composition and surface charge of materials, types of medium (e.g. simulated body fluid, phosphate-buffered saline and cell culture medium) and test parameters on their bioactivity performance. Finally, a brief summary of the biomedical applications of these newly formed calcium phosphate (either in the form of amorphous or apatite) is presented.

Strong emission in Yb3+/Er3+ co-doped phosphate glass ceramics

NASA Astrophysics Data System (ADS)

Liu, Yanling; Song, Feng; Jia, Guozhi; Zhang, Yanbang; Tang, Yi

Yb3+/Er3+ co-doped phosphate glass and glass ceramics were prepared by high-temperature melting method. The X-ray diffraction, transmission electron micrographs, up-conversion and infrared emissions, photothermal conversion properties of the samples have been measured. The results showed the annealing time had a great impact on the microstructure and luminous performance of the phosphate glass. At the beginning of annealing, the metaphosphate crystals were firstly dissolved out. The metaphosphate crystals gradually turned into the orthophosphate with the increasing of annealing time. The emission intensity of the sample was obviously improved after the precursor glass was annealed. The up-conversion and infrared emissions of the sample annealed at 600 °C for 24 h, reached the maximum intensity. Compared with the photothermal properties of glass, the lower photothermal conversion efficiency of the glass ceramics testified the strong emission.

Spectroscopic and laser properties of Er{sup 3+} doped fluoro-phosphate glasses as promising candidates for broadband optical fiber lasers and amplifiers

DOE Office of Scientific and Technical Information (OSTI.GOV)

Babu, S.; Seshadri, M.; Reddy Prasad, V.

2015-10-15

Highlights: • Erbium doped different fluoro-phosphate glasses are prepared and characterized. • Spectroscopic properties have been determined using Judd–Ofelt and Mc-Cumber theory. • Prominent laser transition Er{sup 3+}:{sup 4}I{sub 13/2} → {sup 4}I{sub 15/2} is observed at 1.53 μm. - Abstract: Different fluoro-phosphate glasses doped with 0.5 mol% Er{sup 3+} doped are prepared by melt quenching method. Both structural and spectroscopic properties have been characterized in order to evaluate their potential as both laser source and amplifier materials. Optical absorption measurements are carried out and analyzed through Judd–Ofelt and Mc-Cumber theories where spectroscopic parameters such as intensity parameters Ω{sub l}more » (λ = 2,4,6), transition probabilities, radiative lifetimes, stimulated absorption cross-sections and emission cross-sections at 1.5 μm have been evaluated for Er{sup 3+} doped different fluorophosphate glasses. The various luminescence and gain properties are explained from photoluminescence studies. The decay curve analysis have been done for obtaining the decay time constants of Er{sup 3+} excited level {sup 4}I{sub 13/2} in all the fluoro-phosphate glasses. The obtained results of each glass matrix are compared with the equivalent parameters for several other host glasses. These fluoro-phosphate glasses are found to be suitable candidates for laser and amplifier applications.« less

Chemically durable nitrogen containing phosphate glasses useful for sealing to metals

DOEpatents

Day, Delbert E.; Wilder, Jr., James A.

1984-01-01

The chemical durability of alkali phosphate glasses is improved by incorporation of up to 23 weight percent of nitrogen. A typical phosphate glass contains: 10 to 60 mole % of Li.sub.2 O, Na.sub.2 O or K.sub.2 O; 5-40 mole % of BaO or CAO; 0-1 to 10 mole % of Al.sub.2 O.sub.3 ; and 40-70 mole % of P.sub.2 O.sub.5. Nitrides, such as AlN, are the favored additives.

Spectroscopic study of biologically active glasses

NASA Astrophysics Data System (ADS)

Szumera, M.; Wacławska, I.; Mozgawa, W.; Sitarz, M.

2005-06-01

It is known that the chemical activity phenomenon is characteristic for some inorganic glasses and they are able to participate in biological processes of living organisms (plants, animals and human bodies). An example here is the selective removal of silicate-phosphate glass components under the influence of biological solutions, which has been applied in designing glasses acting as ecological fertilizers of controlled release rate of the nutrients for plants. The structure of model silicate-phosphate glasses containing the different amounts of the glass network formers, i.e. Ca 2+ and Mg 2+, as a binding components were studied. These elements besides other are indispensable of the normal growth of plants. In order to establish the function and position occupied by the particular components in the glass structure, the glasses were examined by FTIR spectroscopy (with spectra decomposition) and XRD methods. It has been found that the increasing amount of MgO in the structure of silicate-phosphate glasses causes the formation of domains the structure of which changes systematically from a structure of the cristobalite type to a structure corresponding to forsterite type. Whilst the increasing content of CaO in the structure of silicate-phosphate glasses causes the formation of domains the structure of which changes from a structure typical for cristobalite through one similar to the structure of calcium orthophosphate, to a structure corresponding to calcium silicates. The changing character of domains structure is the reason of different chemical activity of glasses.

Thermophysical and structural studies on some glass-ceramics and role of nano size crystallites

NASA Astrophysics Data System (ADS)

Kothiyal, G. P.; Arvind, A.; Kumar, Rakesh; Dixit, Anupam; Sharma, Kuldeep; Goswami, Madhumita

2009-07-01

In this paper, we present some studies on structure and thermophysical properties of glass and glass-ceramics with possible bio-medical and sealing applications. The glass-ceramics prepared for bio-medical applications include phosphate as well as silico-phosphate compositions. In vitro bio-compatibility/activity of these materials is discussed. The glass-ceramics used for the sealing application are lithium aluminium silicate (LAS) and lithium zinc silicate (LZS). The phase formation and some aspects of thermophysical properties and sealing are discussed.

Effects of rare-earth co-doping on the local structure of rare-earth phosphate glasses using high and low energy X-ray diffraction.

PubMed

Cramer, Alisha J; Cole, Jacqueline M; FitzGerald, Vicky; Honkimaki, Veijo; Roberts, Mark A; Brennan, Tessa; Martin, Richard A; Saunders, George A; Newport, Robert J

2013-06-14

Rare-earth co-doping in inorganic materials has a long-held tradition of facilitating highly desirable optoelectronic properties for their application to the laser industry. This study concentrates specifically on rare-earth phosphate glasses, (R2O3)x(R'2O3)y(P2O5)(1-(x+y)), where (R, R') denotes (Ce, Er) or (La, Nd) co-doping and the total rare-earth composition corresponds to a range between metaphosphate, RP3O9, and ultraphosphate, RP5O14. Thereupon, the effects of rare-earth co-doping on the local structure are assessed at the atomic level. Pair-distribution function analysis of high-energy X-ray diffraction data (Q(max) = 28 Å(-1)) is employed to make this assessment. Results reveal a stark structural invariance to rare-earth co-doping which bears testament to the open-framework and rigid nature of these glasses. A range of desirable attributes of these glasses unfold from this finding; in particular, a structural simplicity that will enable facile molecular engineering of rare-earth phosphate glasses with 'dial-up' lasing properties. When considered together with other factors, this finding also demonstrates additional prospects for these co-doped rare-earth phosphate glasses in nuclear waste storage applications. This study also reveals, for the first time, the ability to distinguish between P-O and P[double bond, length as m-dash]O bonding in these rare-earth phosphate glasses from X-ray diffraction data in a fully quantitative manner. Complementary analysis of high-energy X-ray diffraction data on single rare-earth phosphate glasses of similar rare-earth composition to the co-doped materials is also presented in this context. In a technical sense, all high-energy X-ray diffraction data on these glasses are compared with analogous low-energy diffraction data; their salient differences reveal distinct advantages of high-energy X-ray diffraction data for the study of amorphous materials.

Survey and research on up-conversion emission character and energy transition of Yb3+/Er3+/Tm3+ co-doped phosphate glass and glass ceramic

NASA Astrophysics Data System (ADS)

Yu, Yin; Song, Feng; Ming, Chengguo; Liu, Jiadong; Li, Wei; Liu, Yanling; Zhao, Hongyan

2012-11-01

By conventional high-temperature melting method, Yb3+/Er3+/Tm3+ co-doped phosphate glass was synthesized. After annealing the precursor glass, the phosphate glass ceramic (GC) was obtained. By measuring the X-ray diffraction (XRD) spectrum, it is proved that the LiYbP4O12 and Li6P6O18 nano-crystals have existed in the phosphate GC. The up-conversion (UC) emission intensity of the GC is obvious stronger compared to that of the glass. The reason is that the shorter distance between rare earth ions in the glass ceramic increases the energy transitions from the sensitized ions (Yb3+) to the luminous ions (Er3+ and Tm3+). By studying the dependence of UC emissions on the pump power, the 523 and 546 nm green emissions of Er3+ ions in the glass are two-photon processes. But in the glass ceramic, they are two/three-photon processes. The phenomenon implies that a three-photon process has participated in the population of the two green emissions. Using Dexter theory, we discuss the energy transitions of Er3+ and Tm3+. The results indicate the energy transition of Tm3+ to Er3+ is very strong in the GC, which changes the population mechanism of UC emissions of Er3+.

[In vitro drug release behavior of carrier made of porous glass ceramics].

PubMed

Wang, De-ping; Huang, Wen-hai; Zhou, Nai

2002-09-01

To conduct the in vitro test on drug release of rifampin encapsulated in a carrier made of porous phosphate glass ceramics and to analyze main factors which affect the drug release rate. A certain quantitative of rifampin was sealed in a hollow cylindrical capsule which consisted of chopped calcium phosphate crystal fiber obtained from glass crystallization. The rifampin concentration was measured in the simulated physiological solution in which the capsule soaked. Rifampin could be released in a constant rate from the porous glass ceramic carrier in a long time. The release rate was dependent on the size of crystal fiber and the wall thickness of the capsule. This kind of calcium phosphate glass ceramics can be a candidate of the carrier materials used as long term drug therapy after osteotomy surgery.

Chemically durable phosphate glasses and a method for their preparation

DOEpatents

Day, D.E.; Wilder, J.A. Jr.

The chemical durability of alkali phosphate glasses is improved by incorporation of up to 23 weight percent of nitrogen. A typical phosphate glass contains: 10 to 60 mole % of Li/sub 2/O, Na/sub 2/O or K/sub 2/O; 5 to 40 mole % of BaO or CaO; 0 to 1 to 10 mole % of Al/sub 2/O/sub 3/; and 40 to 70 mole % of P/sub 2/O/sub 5/. Nitrides, such as AlN, are the favored additives.

Kinetics and mechanisms of the conversion of silicate (45S5), borate, and borosilicate glasses to hydroxyapatite in dilute phosphate solutions.

PubMed

Huang, Wenhai; Day, Delbert E; Kittiratanapiboon, Kanisa; Rahaman, Mohamed N

2006-07-01

Bioactive glasses with controllable conversion rates to hydroxyapatite (HA) may provide a novel class of scaffold materials for bone tissue engineering. The objective of the present work was to comprehensively characterize the conversion of a silicate bioactive glass (45S5), a borate glass, and two intermediate borosilicate glass compositions to HA in a dilute phosphate solution at 37 degrees Celsius. The borate glass and the borosilicate glasses were derived from the 45S5 glass by fully or partially replacing the SiO(2) with B(2)O(3). Higher B(2)O(3) content produced a more rapid conversion of the glass to HA and a lower pH value of the phosphate solution. Whereas the borate glass was fully converted to HA in less than 4 days, the silicate (45S5) and borosilicate compositions were only partially converted even after 70 days, and contained residual SiO(2) in a Na-depleted core. The concentration of Na(+) in the phosphate solution increased with reaction time whereas the PO(4) (3-) concentration decreased, both reaching final limiting values at a rate that increased with the B(2)O(3) content of the glass. However, the Ca(2+) concentration in the solution remained low, below the detection limit of atomic absorption, throughout the reaction. Immersion of the glasses in a mixed solution of K(2)HPO(4) and K(2)CO(3) produced a carbonate-substituted HA but the presence of the K(2)CO(3) had little effect on the kinetics of conversion to HA. The kinetics and mechanisms of the conversion process of the four glasses to HA are compared and used to develop a model for the process.

Dynamics of asymmetric binary glass formers. I. A dielectric and nuclear magnetic resonance spectroscopy study

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kahlau, R.; Bock, D.; Schmidtke, B.

2014-01-28

Dielectric spectroscopy as well as {sup 2}H and {sup 31}P nuclear magnetic resonance spectroscopy (NMR) are applied to probe the component dynamics of the binary glass former tripropyl phosphate (TPP)/polystyrene (PS/PS-d{sub 3}) in the full concentration (c{sub TPP}) range. In addition, depolarized light scattering and differential scanning calorimetry experiments are performed. Two glass transition temperatures are found: T{sub g1}(c{sub TPP}) reflects PS dynamics and shows a monotonic plasticizer effect, while the lower T{sub g2}(c{sub TPP}) exhibits a maximum and is attributed to (faster) TPP dynamics, occurring in a slowly moving or immobilized PS matrix. Dielectric spectroscopy probing solely TPP identifiesmore » two different time scales, which are attributed to two sub-ensembles. One of them, again, shows fast TPP dynamics (α{sub 2}-process), the other (α{sub 1}-process) displays time constants identical with those of the slow PS matrix. Upon heating the α{sub 1}-fraction of TPP decreases until above some temperature T{sub c} only a single α{sub 2}-population exists. Inversely, below T{sub c} a fraction of the TPP molecules is trapped by the PS matrix. At low c{sub TPP} the α{sub 2}-relaxation does not follow frequency-temperature superposition (FTS), instead it is governed by a temperature independent distribution of activation energies leading to correlation times which follow Arrhenius laws, i.e., the α{sub 2}-relaxation resembles a secondary process. Yet, {sup 31}P NMR demonstrates that it involves isotropic reorientations of TPP molecules within a slowly moving or rigid matrix of PS. At high c{sub TPP} the super-Arrhenius temperature dependence of τ{sub 2}(T), as well as FTS are recovered, known as typical of the glass transition in neat systems.« less

Simple views on critical binary liquid mixtures in porous glass

NASA Astrophysics Data System (ADS)

Tremblay, L.; Socol, S. M.; Lacelle, S.

2000-01-01

A simple scenario, different from previous attempts, is proposed to resolve the problem of the slow phase separation dynamics of binary liquid mixtures confined in porous Vycor glass. We demonstrate that simply mutual diffusion, renormalized by critical composition fluctuations and geometrical hindrance of the porous glass, accounts for the slow phase separation kinetics. Capillary invasion studies of porous Vycor glass by the critical isobutyric acid-water mixture, close to the consolute solution temperature, corroborate our analysis.

Effect of PbO on the spectral and thermo-optical properties of Nd3+-doped phosphate laser glass

NASA Astrophysics Data System (ADS)

Yin, Qianwen; Kang, Shuai; Wang, Xue; Li, Shunguang; He, Dongbing; Hu, Lili

2017-04-01

Nd3+-doped P2O5-K2O-Al2O3-BaO-PbO phosphate glasses with various PbO/BaO ratios were synthesized using the melt quenching technique. Raman, absorption, and emission spectra were measured to investigate the effects of PbO/BaO ratios on the structures and spectroscopic properties of the glasses. The emission cross-sections of the Nd3+-doped phosphate glasses were calculated using the Judd-Ofelt theory, and were found to increase from 4.37 × 10-20 to 4.50 × 10-20 cm2 as the PbO/BaO ratio increased. In addition, thermo-optical properties were measured using an interferometric technique. The thermo-optical coefficients, which were -1.49 × 10-6, -1.65 × 10-6, and -1.64 × 10-6 K-1, respectively, were all largely negative values. The thermal expansion coefficients of the three glass samples varied within a small range. The results showed that increasing the PbO/BaO ratio of phosphate glasses can improve the laser properties while maintaining their good thermo-optical properties.

Thermal properties and surface reactivity in simulated body fluid of new strontium ion-containing phosphate glasses.

PubMed

Massera, J; Petit, L; Cardinal, T; Videau, J J; Hupa, M; Hupa, L

2013-06-01

In this paper, we investigate the effect of SrO substitution for CaO in 50P₂O₅-10Na₂-(40-x)CaO-xSrO glass system (x from 0 to 40) on the thermal and structural properties and also on the glass reactivity in simulated body fluid (SBF) in order to find new glass candidates for biomedical glass fibers. The addition of SrO at the expense of CaO seems to restrain the leaching of phosphate ions in the solution limiting the reduction of the solution pH. We observed the formation of an apatite layer at the surface of the glasses when in contact with SBF. SrO and MgO were found in the apatite layer of the strontium ion-containing glasses, the concentration of which increases with an increase of SrO content. We think that it is the presence of MgO and SrO in the layer which limits the leaching of phosphate in the solution and thus the glass dissolution in SBF.

A Review of Iron Phosphate Glasses and Recommendations for Vitrifying Hanford Waste

DOE Office of Scientific and Technical Information (OSTI.GOV)

Delbert E. Ray; Chandra S. Ray

2013-11-01

This report contains a comprehensive review of the research conducted, world-wide, on iron phosphate glass over the past ~30 years. Special attention is devoted to those iron phosphate glass compositions which have been formulated for the purpose of vitrifying numerous types of nuclear waste, with special emphasis on the wastes stored in the underground tanks at Hanford WA. Data for the structural, chemical, and physical properties of iron phosphate waste forms are reviewed for the purpose of understanding their (a) outstanding chemical durability which meets all current DOE requirements, (b) high waste loadings which can exceed 40 wt% (up tomore » 75 wt%) for several Hanford wastes, (c) low melting temperatures, can be as low as 900°C for certain wastes, and (d) high tolerance for “problem” waste components such as sulfates, halides, and heavy metals (chromium, actinides, noble metals, etc.). Several recommendations are given for actions that are necessary to smoothly integrate iron phosphate glass technology into the present waste treatment plans and vitrification facilities at Hanford.« less

Detection algorithm for glass bottle mouth defect by continuous wavelet transform based on machine vision

NASA Astrophysics Data System (ADS)

Qian, Jinfang; Zhang, Changjiang

2014-11-01

An efficient algorithm based on continuous wavelet transform combining with pre-knowledge, which can be used to detect the defect of glass bottle mouth, is proposed. Firstly, under the condition of ball integral light source, a perfect glass bottle mouth image is obtained by Japanese Computar camera through the interface of IEEE-1394b. A single threshold method based on gray level histogram is used to obtain the binary image of the glass bottle mouth. In order to efficiently suppress noise, moving average filter is employed to smooth the histogram of original glass bottle mouth image. And then continuous wavelet transform is done to accurately determine the segmentation threshold. Mathematical morphology operations are used to get normal binary bottle mouth mask. A glass bottle to be detected is moving to the detection zone by conveyor belt. Both bottle mouth image and binary image are obtained by above method. The binary image is multiplied with normal bottle mask and a region of interest is got. Four parameters (number of connected regions, coordinate of centroid position, diameter of inner cycle, and area of annular region) can be computed based on the region of interest. Glass bottle mouth detection rules are designed by above four parameters so as to accurately detect and identify the defect conditions of glass bottle. Finally, the glass bottles of Coca-Cola Company are used to verify the proposed algorithm. The experimental results show that the proposed algorithm can accurately detect the defect conditions of the glass bottles and have 98% detecting accuracy.

Fiberglass goes green: Developing phosphate glass for use in biodegradable composites

NASA Astrophysics Data System (ADS)

Arendt, Christina Lee

Composite materials, such as the glass fiber reinforced polyester thermosets known as "fiberglass," are used in many applications. However, recycling processes for these materials are inefficient and not widely available. Specially engineered degradable polymers offer an opportunity to redesign these composites. Additionally, the composite could be tailored to be multi-use, such that upon degradation, the resulting products could be used as part of a zeoponic substrate (artificial soil) for growing plants. Such a material would be beneficial for long-duration space missions, terraforming, or in other agricultural applications. The research presented in this dissertation focuses on developing phosphate glass for use as the fiber reinforcement for such a composite. Due to the under-utilization of phosphate systems, there is a lack of thermodynamic data on these systems. The modified associate species method of phase diagram calculation was used in an attempt to gain more information about the desired system, as it is a good predictor of the phase relations in oxide melts, slags, and glasses and requires less data than other methods. Further research into the thermodynamic properties of phosphates is still needed to develop accurate phase diagrams and melting temperatures for this system. Seventeen glass formulations were developed and melted. Six of these formulations were chosen for dissolution testing. Of these six, Glass 17 was chosen for intensive testing and characterization. This glass was tested in water, hydrochloric acid solutions, and citric acid solutions. The weight loss was measured and ICP-OES was performed on the leachate solution. Scanning electron microscopy (SEM) and X-ray diffraction were performed on the tested specimens. Shrinking-core models were fit to the dissolution data. Fibers were drawn from the glass and characterized using SEM. The data shows that this glass is not dissolving congruently, as is expected of phosphate glasses. Instead, selective leaching is occurring, leading to the development of a non-protective surface layer during dissolution.

Lead and aluminum bonding in Pb-AI metaphosphate glasses.

PubMed

Tsuchida, J E; Schneider, J; Pizani, P S; Oliveira, S L

2008-01-21

The bonding properties of cations in phosphate glasses determine many short- and medium-range structural features in the glass network, hence influencing bulk properties. In this work, Pb-Al-metaphosphate glasses (1 - x)Pb(PO(3))(2).xAI(PO(3))(3) with 0 < or = x < or = 1 were analyzed to determine the effect of the substitution of Pb by AI on the glass structure in the metaphosphate composition. The glass transition temperature and density were measured as a function of the Al concentration. The vibrational and structural properties were probed by Raman spectroscopy and nuclear magnetic resonance of (31)P, (27)AI, and (207)Pb. Aluminum incorporates homogeneously in the glass creating a stiffer and less packed network. The average coordination number for AI decreases from 5.9 to 5.0 as x increases from 0.1 to 1, indicating more covalent AI-O bonds. The coordination number of Pb in these glasses is greater than 8, showing an increasing ionic behavior for compositions richer in AI. A quantitative analysis of the phosphate speciation shows definite trends in the bonding of AIO(n) groups and phosphate tetrahedra. In glasses with x < 0.48, phosphate groups share preferentially only one nonbridging O corner with an AIO(n) coordination polyhedron. For x > 0.48 more than one nonbridging O can be linked to AIO(n) polyhedra. There is no corner sharing of O between AIO(n) and PbO(n) polyhedra nor between AIO(n) themselves throughout the compositional range. The PbO(n) coordination polyhedra show considerable nonbridging O sharing, with each O participating in the coordination sphere of at least two Pb. The bonding preferences determined for Al are consistent with the behavior observed in Na-AI and Ca-AI metaphosphates, indicating this may be a general behavior for ternary phosphate glasses.

Analysis of radiophotoluminescence center formation mechanism in Ag-doped phosphate glasses

NASA Astrophysics Data System (ADS)

Kawamoto, Hiroki; Fujimoto, Yutaka; Koshimizu, Masanori; Okada, Go; Yanagida, Takayuki; Asai, Keisuke

2018-06-01

Ag-doped phosphate glasses have widely been used as radiophotoluminescence (RPL) dosimeters. However, the RPL center formation process is not fully understood. In this study, we investigated the RPL center formation process in Ag-doped Na–Al phosphate glasses. We observed that two RPL centers (Ag0 and Ag2+) were formed at temperatures higher than 100 and 250 K, respectively. In addition, activation energies of their formation were estimated to be 20 and 267 meV, respectively. These results suggest that the electron transfer process is not a simple thermally activated process.

Framework influence of erbium doped oxyfluoride glasses on their optical properties

NASA Astrophysics Data System (ADS)

Środa, Marcin; Cholewa-Kowalska, Katarzyna; Różański, Marek; Nocuń, Marek

2011-01-01

Glasses of different matrix (phosphate, borate, silicate and lead-silicate) were studied for their optical properties. The effect of Er dopant on transmittance and luminescence properties was presented. The significant “red shift” and “blue shift” of UV edge absorption were discussed based on the changes in the framework of the borate and phosphate glasses, respectively. It was showed that the integral intensity of the two main optical absorption transitions monotonically increases with the order: phosphate < borate < silicate < lead-silicate. Ellipsometric measurement was applied to obtain the refractive index of the glasses. The correlation between the shift of edge absorption and the change of refractive index was presented. Effect of glassy matrix on luminescence of Er3+ was discussed.

Novel lead-iron phosphate glass

DOEpatents

Boatner, Lynn A.; Sales, Brian C.

1989-01-01

The invention described and claimed in the specification relates to the discovery that effective addition of Fe.sub.2 O.sub.3 to a lead phosphate glass results in a glass having enhanced chemical durability and physical stability, and consists essentially of the glass resulting from melting a mixture consisting essentially of, in weight percent, 40-66 percent PbO, 30-55 percent P.sub.2 O.sub.5 and an effective concentration up to 12 percent Fe.sub.2 O.sub.3.

Novel lead-iron phosphate glass

DOEpatents

Boatner, L.A.; Sales, B.C.

1989-07-11

The invention described and claimed in the specification relates to the discovery that effective addition of Fe[sub 2]O[sub 3] to a lead phosphate glass results in a glass having enhanced chemical durability and physical stability, and consists essentially of the glass resulting from melting a mixture consisting essentially of, in weight percent, 40--66 percent PbO, 30--55 percent P[sub 2]O[sub 5] and an effective concentration up to 12 percent Fe[sub 2]O[sub 3].

Bioactive calcium phosphate–based glasses and ceramics and their biomedical applications: A review

PubMed Central

Islam, Md Towhidul; Felfel, Reda M; Abou Neel, Ensanya A; Grant, David M; Ahmed, Ifty; Hossain, Kazi M Zakir

2017-01-01

An overview of the formation of calcium phosphate under in vitro environment on the surface of a range of bioactive materials (e.g. from silicate, borate, and phosphate glasses, glass-ceramics, bioceramics to metals) based on recent literature is presented in this review. The mechanism of bone-like calcium phosphate (i.e. hydroxyapatite) formation and the test protocols that are either already in use or currently being investigated for the evaluation of the bioactivity of biomaterials are discussed. This review also highlights the effect of chemical composition and surface charge of materials, types of medium (e.g. simulated body fluid, phosphate-buffered saline and cell culture medium) and test parameters on their bioactivity performance. Finally, a brief summary of the biomedical applications of these newly formed calcium phosphate (either in the form of amorphous or apatite) is presented. PMID:28794848

Cerium doped glasses: search for a new scintillator

NASA Astrophysics Data System (ADS)

Kielty, Matthew William

Single crystals have been the standard material when it comes to scintillators, but with the ability to easily be produced at a considerably lower cost and fabricated into tailored sizes and shapes there is increasing interest in the development of glass scintillators as an alternative. Ce-doped borosilicate and phosphate glasses were investigated focusing on the effect of different modifiers on their optical properties and luminescence. The borosilicate glasses were prepared aiming at the detection of thermal neutrons, utilizing B-10, while the phosphate glasses were targeting the detection of gamma-rays taking advantage of high Z elements such as, Ba, Bi, Ta, Pb and W. Structural characteristics determined by Raman spectroscopy were coupled with results from photoluminescence and UV-visible transmission measurements, while the index of refraction was estimated using the Gladstone-Dale relation using experimentally obtained density values. This work revealed barium, with its superior optical transmission and luminescent properties, to be the best high Z element for inclusion in the phosphate glasses studied.

Novel selenium containing boro-phosphate glasses: preparation and structural study.

PubMed

Ciceo-Lucacel, R; Radu, T; Ponta, O; Simon, V

2014-06-01

We synthesized a new boro-phosphate glass system with different %mol SeO2 content by conventional melt quenching technique. All samples were obtained in a glassy state with the vitreous structure confirmed by X-ray diffraction analysis. Scanning electron microscopy (SEM) revealed some non-homogeneous domains on the glasses surface, and their tendency to link each other once the selenium oxide content increases. Energy-dispersive X-ray analysis (EDAX) indicated similar elemental composition in different regions of each sample. X-ray photoelectron spectroscopy (XPS) was used to determine the nature of chemical bonding and the elemental composition at the sample surfaces, and Fourier transform infrared (FT-IR) spectroscopy was used to determine the structural groups in the obtained glass structure. Based on FT-IR results, the glass structure at short range order consists mainly of small phosphate units such as pyrophosphate (i.e. P2O7(4-) dimmers or terminating groups at the end of phosphate chains) and some metaphosphate (i.e. PO3(-) middle groups in the phosphate chains) units. The boron atoms are mainly placed in three-coordinated sites in BØ3 or BØ2O(-) units. A small contribution of BØ4(-) units was also detected from the FT-IR spectra of glasses. For SeO2 content higher than 5mol%, the modifier role of selenium ions is strongly reflected on the local structure dominated in this case by pyrophosphate units. Copyright © 2014 Elsevier B.V. All rights reserved.

Fabrication of planar optical waveguides by 6.0 MeV silicon ion implantation in Nd-doped phosphate glasses

NASA Astrophysics Data System (ADS)

Shen, Xiao-Liang; Dai, Han-Qing; Zhang, Liao-Lin; Wang, Yue; Zhu, Qi-Feng; Guo, Hai-Tao; Li, Wei-Nan; Liu, Chun-Xiao

2018-04-01

We report the fabrication of a planar optical waveguide by silicon ion implantation into Nd-doped phosphate glass at an energy of 6.0 MeV and a dose of 5.0 × 1014 ions/cm2. The change in the surface morphology of the glass after the implantation can be clearly observed by scanning electron microscopy. The measurement of the dark mode spectrum of the waveguide is conducted using a prism coupler at 632.8 nm. The refractive index distribution of the waveguide is reconstructed by the reflectivity calculation method. The near-field optical intensity profile of the waveguide is measured using an end-face coupling system. The waveguide with good optical properties on the glass matrix may be valuable for the application of the Nd-doped phosphate glass in integrated optical devices.

Radiation-induced polymerization of glass-forming systems. V. Initial polymerization rate in binary glass-forming systems

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kaetsu, Isao; Okubo, Hiroshi; Ito, Akihiko

1973-06-01

The radiation-induced polymerization of binary systems consisting of glass-forming monomer and glass-forming solvent in supercooled phase was studied. The initial polymerization rates were markedly affected by T/sub g/ (glass transition temperature) and T/sub v/ of the system (30-50 deg C higher than T/sub g/), which are functions of the composition. The composition and temperature dependence of initial polymerization rate in binary glass-forming systems were much affected by homogeneity of the polymerization system and the T of the glass- forming solvent. The composition and temperature dependences in the glycidyl methacrylate --triacetin system as a typical homogeneous polymerization system were studied inmore » detail, and the polymerizations of hydroxyethyl methacrylate triacetln and hydroxyethyl methacrylate --isoamyl acetate systems were studied for the heterogeneous polymerization systems; the former illustrates the combination of lower T/sub g/ monomer and higher T/sub g/ solvent and the latter typifies a system consisting of higher T/sub g/ monomer and lower T/sub g/ solvent. All experimental results for the composition and temperature dependence of initial polymerization rate in binary glass-forming systems could be explained by considering the product of the effect of the physical effect relating to T/sub v/ and T/sub g/ of the system and the effect of composition in normal solution polymerization at higher temperature, which was also the product of a dilution effect and a chemical or physical acceleration effect. (auth)« less

Study on surface roughness evolvement of Nd-doped phosphate glass after IBF

NASA Astrophysics Data System (ADS)

Li, Furen; Xie, Xuhui; Zhou, Lin; Tie, Guipeng; Hu, Hao

2016-10-01

Nd doped phosphate glass is widely used as gain media in high power laser system. It is traditionally polished with the annular polishing technology. The edge effect is inevitable in annular polishing process and it results in the low manufacturing efficiency. Ion Beam Figuring (IBF) is a highly deterministic, non-contact method for the ultra-precision optics fabrication. So the edge effect is avoided. Nanometer and sub-nanometer precision is realizable in IBF. In this paper, Nd doped phosphate glass was polished with IBF, and the evolvement of surface roughness was emphasized. The roughness of surface polished with ion beam at normal and oblique incidence was researched. The oblique incident angle was 45°. The surface roughness was measured with the white light interferometer. No evident change was observed. This means that the pre-finish roughness can be preserved in IBF. The results denote that IBF is a feasible method to correct the contour errors of Nd doped phosphate glass, and the roughness will not be coarsened.

Optical absorption and photoluminescence properties of Nd3+ doped mixed alkali phosphate glasses-spectroscopic investigations.

PubMed

Ratnakaram, Y C; Srihari, N V; Kumar, A Vijaya; Naidu, D Thirupathi; Chakradhar, R P S

2009-02-01

Spectroscopic investigations were performed on 68NH(4)H(2)PO(4).xLi(2)CO(3)(30-x)K(2)CO(3) and 68NH(4)H(2)PO(4).xNa(2)CO(3)(30-x)K(2)CO(3) (where x=5, 10, 15, 20 and 25) glasses containing 2 mol% Nd(2)O(3). Various spectroscopic parameters (Racah (E(1), E(2), E(3)), spin-orbit (xi(4f)) and configuration interaction (alpha)) are reported. Judd-Ofelt intensity parameters (Omega(2), Omega(4), Omega(6)) are calculated for Nd(3+) doped two mixed alkali phosphate glass matrices. From the magnitude of Judd-Ofelt parameters, covalency is studied as a function of x in the glass matrix. Using Judd-Ofelt intensity parameters, total radiative transition probabilities (A(T)), radiative lifetimes (tau(R)), branching ratios (beta) and integrated absorption cross sections (Sigma) have been computed for certain excited states of Nd(3+) in these mixed alkali phosphate glasses. Emission cross sections (sigma(P)) are calculated for the two transitions, (4)G(7/2)-->(4)I(11/2) and (4)G(7/2)-->(4)I(13/2) of Nd(3+) in these mixed alkali phosphate glasses. Optical band gaps (E(opt)) for direct and indirect transitions are reported.

Nanoscale mechanochemical wear of phosphate laser glass against a CeO2 particle in humid air

NASA Astrophysics Data System (ADS)

Yu, Jiaxin; He, Hongtu; Zhang, Yafeng; Hu, Hailong

2017-01-01

Using an atomic force microscope, the friction and wear of phosphate laser glass against a CeO2 particle were quantitatively studied both in humid air and in vacuum, to reveal the water molecules induced mechanochemical wear mechanism of phosphate laser glass. The friction coefficient of the glass/CeO2 pair in air was found to be 5-7 times higher than that in vacuum due to the formation of a capillary water bridge at the friction interface, with a contribution of the capillary-related friction to the total friction coefficient as high as 65-79%. The capillary water bridge further induced a serious material removal of glass and CeO2 particle surfaces, while supplying both a local liquid water environment to corrode the glass surface and a high shearing force to assist the stretching of the Cesbnd Osbnd P bond, accelerating the reaction between water and the glass/CeO2 pair. In vacuum, however, no discernable wear phenomena were observed, but the phase images captured by AFM tapping mode suggested the occurrence of potential strain hardening in the friction area of the glass surface.

New Er3+-doped phosphate glass for ion-exchanged waveguide amplifiers

NASA Astrophysics Data System (ADS)

Jiang, Shibin; Luo, Tao; Hwang, Bor-Chyuan; Nunzi Conti, Gualtiero; Myers, Michael J.; Rhonehouse, Daniel L.; Honkanen, Seppo; Peyghambarian, Nasser

1998-12-01

A new Er(superscript 3+)-doped phosphate glass exhibiting an excellent durability in both boiling water and NaNO(subscript 3) molten salt is developed. The ion-exchange process of this glass is investigated by treating glass samples in a variety of salt baths with various exposure times. A planar waveguide with one mode at 1.54 micrometers and three modes at 632.8 nm is demonstrated. The spectral properties of Er(superscript 3+) in this glass are characterized by measuring absorption and emission spectra and fluorescence lifetimes. The emission cross section of Er(superscript 3+) in this glass is calculated to be 0.76 X 10(superscript 20) cm(superscript 2) using McCumber theory.

Bioactive calcium pyrophosphate glasses and glass-ceramics.

PubMed

Kasuga, Toshihiro

2005-01-01

Calcium phosphate glass-based materials in the pyrophosphate region are briefly reviewed. Calcium pyrophosphate glasses can be prepared by including a small amount of TiO(2) (

Spectroscopic properties of Eu3+/Nd3+ co-doped phosphate glasses and opaque glass-ceramics

NASA Astrophysics Data System (ADS)

Narro-García, R.; Desirena, H.; López-Luke, T.; Guerrero-Contreras, J.; Jayasankar, C. K.; Quintero-Torres, R.; De la Rosa, E.

2015-08-01

This paper reports the fabrication and characterization of Eu3+/Nd3+ co-doped phosphate (PNE) glasses and glass-ceramics as a function of Eu3+ concentration. The precursor glasses were prepared by the conventional melt quenching technique and the opaque glass-ceramics were obtained by heating the precursor glasses at 450 °C for 30 h. The structural and optical properties of the glass and glass-ceramics were analyzed by means of X-ray diffraction, Raman spectroscopy, UV-VIS-IR absorption spectroscopy, photoluminescence spectra and lifetimes. The amorphous and crystalline structures of the precursor glass and opaque glass-ceramic were confirmed by X-ray diffraction respectively. The Raman spectra showed that the maximum phonon energy decreased from 1317 cm-1 to 1277 cm-1 with the thermal treatment. The luminescence spectra of the glass and glass-ceramic samples were studied under 396 nm and 806 nm excitation. The emission intensity of the bands observed in opaque glass-ceramic is stronger than that of the precursor glass. The luminescence spectra show strong dependence on the Eu3+ ion concentration in the Nd3+ ion photoluminescence (PL) intensity, which suggest the presence of energy transfer (ET) and cross-relaxation (CR) processes. The lifetimes of the 4F3/2 state of Nd3+ ion in Eu3+/Nd3+ co-doped phosphate glasses and glass-ceramics under 806 nm excitation were measured. It was observed that the lifetimes of the 4F3/2 level of Nd3+ of both glasses and glass-ceramics decrease with the increasing Eu3+ concentration. However in the case of opaque glass-ceramics the lifetimes decrease only 16%.

Synthesis, characterization and bioactivity of a calcium-phosphate glass-ceramics obtained by the sol-gel processing method.

PubMed

Jmal, Nouha; Bouaziz, Jamel

2017-02-01

In this work, a calcium-phosphate glass-ceramics was successfully obtained by heat treatment of a mixture of 26.52 in wt.% of fluorapatite (Fap) and 73.48 in wt.% of 77S (77 SiO 2 14 CaO9 P 2 O 5 in wt.%) gel. The calcium phosphate-glass-ceramics was prepared by sol-gel process with tetraethyl orthosilicate (TEOS), triethyl phosphate (TEP), calcium nitrate and fluorapatite. The synthesized powders were characterized by some commonly used tools such as X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), 31 P magic angle spinning nuclear magnetic resonance (MAS-NMR), scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS), and thin-film X-ray diffraction (TF-XRD). The obtained results seemed to confirm the nucleation and growth of hydroxyapatite (Hap) nano-phase in the glass. Moreover, an in-vitro evaluation of the glass-ceramic was performed. In addition, to assess its bioactive capacity, it was soaked in simulated body fluid (SBF) at different time intervals. The SEM, EDS and TF-XRD analyses showed the deposition of hydroxyapatite on the surface of the specimens after three days of immersion in SBF solution. The mechanical properties of the obtained material such as rupture strength, Vickers hardness and elastic modulus were measured. In addition, the friction coefficient of calcium phosphate-glass-ceramics was tested. The values of the composite of rupture strength (24MPa), Vickers hardness (214Hv), Young's modulus (52.3GPa), shear modulus (19GPa) and friction coefficient (0.327) were obtained. This glass-ceramics can have useful applications in dental prostheses. Indeed, this material may have promising applications for implants because of its content of fluorine, the effective protector against dental caries. Copyright © 2016 Elsevier B.V. All rights reserved.

Mechanical behaviour of degradable phosphate glass fibres and composites-a review.

PubMed

Colquhoun, R; Tanner, K E

2015-12-23

Biodegradable materials are potentially an advantageous alternative to the traditional metallic fracture fixation devices used in the reconstruction of bone tissue defects. This is due to the occurrence of stress shielding in the surrounding bone tissue that arises from the absence of mechanical stimulus to the regenerating bone due to the mismatch between the elastic modulus of bone and the metal implant. However although degradable polymers may alleviate such issues, these inert materials possess insufficient mechanical properties to be considered as a suitable alternative to current metallic devices at sites of sufficient mechanical loading. Phosphate based glasses are an advantageous group of materials for tissue regenerative applications due to their ability to completely degrade in vivo at highly controllable rates based on the specific glass composition. Furthermore the release of the glass's constituent ions can evoke a therapeutic stimulus in vivo (i.e. osteoinduction) whilst also generating a bioactive response. The processing of these materials into fibres subsequently allows them to act as reinforcing agents in degradable polymers to simultaneously increase its mechanical properties and enhance its in vivo response. However despite the various review articles relating to the compositional influences of different phosphate glass systems, there has been limited work summarising the mechanical properties of different phosphate based glass fibres and their subsequent incorporation as a reinforcing agent in degradable composite materials. As a result, this review article examines the compositional influences behind the development of different phosphate based glass fibre compositions intended as composite reinforcing agents along with an analysis of different potential composite configurations. This includes variations in the fibre content, matrix material and fibre architecture as well as other novel composites designs.

Glass microspheres for medical applications

NASA Astrophysics Data System (ADS)

Conzone, Samuel David

Radioactive dysprosium lithium borate glass microspheres have been developed as biodegradable radiation delivery vehicles for the radiation synovectomy treatment of rheumatoid arthritis. Once injected into a diseased joint, the microspheres deliver a potent dose of radiation to the diseased tissue, while a non-uniform chemical reaction converts the glass into an amorphous, porous, hydrated dysprosium phosphate reaction product. The non-radioactive, lithium-borate component is dissolved from the glass (up to 94% weight loss), while the radioactive 165Dy reacts with phosphate anions in the body fluids, and becomes "chemically" trapped in a solid, dysprosium phosphate reaction product that has the same size as the un-reacted glass microsphere. Ethylene diamine tetraacetate (EDTA) chelation therapy can be used to dissolve the dysprosium phosphate reaction product after the radiation delivery has subsided. The dysprosium phosphate reaction product, which formed in vivo in the joint of a Sprague-Dawley rat, was dissolved by EDTA chelation therapy in <1 week, without causing any detectable joint damage. The combination of dysprosium lithium borate glass microspheres and EDTA chelation therapy provides an unique "tool" for the medical community, which can deliver a large dose (>100 Gy) of localized beta radiation to a treatment site within the body, followed by complete biodegradability. The non-uniform reaction process is a desirable characteristic for a biodegradable radiation delivery vehicle, but it is also a novel material synthesis technique that can convert a glass to a highly porous materials with widely varying chemical composition by simple, low-temperature, glass/solution reaction. The reaction product formed by nonuniform reaction occupies the same volume as the un-reacted glass, and after drying for 1 h at 300°C, has a specific surface area of ≈200 m2/g, a pore size of ≈30 nm, and a nominal crushing strength of ≈10 MPa. Finally, rhenium glass microspheres, composed of micron-sized, metallic rhenium particles dispersed within a magnesium alumino borate glass matrix were produced by sintering ReO2 powder and glass frit at 1050°C. A 50 mg injection of radioactive rhenium glass microspheres containing 3.7 GBq of 186Re and 8.5 GBq of 188Re could be used to deliver a 100 Gy dose to a cancerous tumor, while limiting the total body dose caused by rhenium dissolution to approximately 1 mGy.

Cell adhesion to borate glasses by colloidal probe microscopy.

PubMed

Wiederhorn, Sheldon M; Chae, Young-Hun; Simon, Carl G; Cahn, Jackson; Deng, Yan; Day, Delbert

2011-05-01

The adhesion of osteoblast-like cells to silicate and borate glasses was measured in cell growth medium using colloidal probe microscopy. The probes consisted of silicate and borate glass spheres, 25-50 μm in diameter, attached to atomic force microscope cantilevers. Variables of the study included glass composition and time of contact of the cell to the glasses. Increasing the time of contact from 15 to 900 s increased the force of adhesion. The data could be plotted linearly on a log-log plot of adhesive force versus time. Of the seven glasses tested, five had slopes close to 0.5, suggesting a square root dependence of the adhesive force on the contact time. Such behavior can be interpreted as a diffusion limited process occurring during the early stages of cell attachment. We suggest that the rate limiting step in the adhesion process is the diffusion of integrins resident in the cell membrane to the area of cell attachment. Data presented in this paper support the hypothesis of Hench et al. that strong adhesion depends on the formation of a calcium phosphate reaction layer on the surfaces of the glass. Glasses that did not form a calcium phosphate layer exhibited a weaker adhesive force relative to those glasses that did form a calcium phosphate layer. Published by Elsevier Ltd.

ROLE OF THE NETWORK FORMER IN SEMICONDUCTING OXIDE GLASSES.

DTIC Science & Technology

SEMICONDUCTOR DEVICES, * GLASS ), (*ELECTRICAL NETWORKS, GLASS ), ELECTRICAL PROPERTIES, SEEBECK EFFECT, BORATES, PHOSPHATES, ELECTRICAL RESISTANCE, X RAY DIFFRACTION, ANNEALING, OXIDATION, OXIDES, ELECTRODES, VANADIUM

Erbium-doped phosphate glass waveguide on silicon with 4.1 dB/cm gain at 1.535 µm

NASA Astrophysics Data System (ADS)

Yan, Y. C.; Faber, A. J.; de Waal, H.; Kik, P. G.; Polman, A.

1997-11-01

Erbium-doped multicomponent phosphate glass waveguides were deposited by rf sputtering techniques. The Er concentration was 5.3×1020cm-3. By pumping the waveguide at 980 nm with a power of ˜21 mW, a net optical gain of 4.1 dB at 1.535 μm was achieved. This high gain per unit length at low pump power could be achieved because the Er-Er cooperative upconversion interactions in this heavily Er-doped phosphate glass are very weak [the upconversion coefficient is (2.0±0.5)×10-18 cm3/s], presumably due to the homogeneous distribution of Er in the glass and due to the high optical mode confinement in the waveguide which leads to high pump power density at low pump power.

Aluminum elution and precipitation in glass vials: effect of pH and buffer species.

PubMed

Ogawa, Toru; Miyajima, Makoto; Wakiyama, Naoki; Terada, Katsuhide

2015-02-01

Inorganic extractables from glass vials may cause particle formation in the drug solution. In this study, the ability of eluting Al ion from borosilicate glass vials, and tendencies of precipitation containing Al were investigated using various pHs of phosphate, citrate, acetate and histidine buffer. Through heating, all of the buffers showed that Si and Al were eluted from glass vials in ratios almost the same as the composition of borosilicate glass, and the amounts of Al and Si from various buffer solutions at pH 7 were in the following order: citrate > phosphate > acetate > histidine. In addition, during storage after heating, the Al concentration at certain pHs of phosphate and acetate buffer solution decreased, suggesting the formation of particles containing Al. In citrate buffer, Al did not decrease in spite of the high elution amount. Considering that the solubility profile of aluminum oxide and the Al eluting profile of borosilicate glass were different, it is speculated that Al ion may be forced to leach into the buffer solution according to Si elution on the surface of glass vials. When Al ions were added to the buffer solutions, phosphate, acetate and histidine buffer showed a decrease of Al concentration during storage at a neutral range of pHs, indicating the formation of particles containing Al. In conclusion, it is suggested that phosphate buffer solution has higher possibility of forming particles containing Al than other buffer solutions.

Novel method for early investigation of bioactivity in different borate bio-glasses

NASA Astrophysics Data System (ADS)

Abdelghany, A. M.

Some ternary borate glasses were prepared and corrosion behavior of such ternary borate glasses after immersion in aqueous dilute phosphate solution was studied using different immersion times. Fourier transform infrared (FTIR) absorption spectral measurements were done before and after immersion in the mentioned solution for extended times up to 2 days to justify the appearance of the characteristic FTIR bands due to calcium phosphate (hydroxyapatite (HA)) which is considered as the potential indication of bioactivity. Experimental IR data confirm the beginning of the appearance of FTIR bands at about 580 and 620 cm-1 after 3 days and the complete resolution with its characteristic split form after 1 week and more. Deconvolution analysis technique (DAT) of the FTIR spectrum was employed to investigate the bioactivity of such ternary borate system after a short period of immersion. The corrosion behavior of such glasses is explained in relation to a suggested hydrolysis followed by direct dissolution mechanism. The ease of dissolution of all the borate glasses constituents explains the formation of calcium phosphate and conversion to crystalline hydroxyapatite within the borate glass matrix. X-ray diffraction may be used to retrace the structural changes and degree of crystallinity of the prepared glasses.

Influence of temperature and frequency on ionic conductivity of Li{sub 3}PO{sub 4}–Pb{sub 3}(PO{sub 4}){sub 2}–BiPO{sub 4} phosphate glasses

DOE Office of Scientific and Technical Information (OSTI.GOV)

El Moudane, M., E-mail: m.elmoudane@gmail.com; El Maniani, M.; Sabbar, A.

2015-12-15

Highlights: • Results of ionic conductivities of Li{sub 3}PO{sub 4}–Pb{sub 3}(PO{sub 4}){sub 2}–BiPO{sub 4} phosphate glasses. • Determination of glass transition temperature using DSC method. • Study of temperature and frequency on ionic conductivity of Li{sub 3}PO{sub 4}–Pb{sub 3}(PO{sub 4}){sub 2}–BiPO{sub 4} phosphate glasses. - Abstract: Lithium–Lead–Bismuth phosphates glasses having, a composition 30Li{sub 3}PO{sub 4}–(70 − x)Pb{sub 3}(PO{sub 4}){sub 2}–xBiPO{sub 4} (45 ≤ x ≤ 60 mol%) were prepared by using the melt quenching method 1000 °C. The thermal stability of theses glasses increases with the substitution of Bi{sub 2}O{sub 3} with PbO. The ionic conductivity of all compositions havemore » been measured over a wide temperature (200–500 °C) and frequency range (1–106 Hz). The ionic conductivity data below and above T{sub g} follows Arrhenius and Vogel–Tamman–Fulcher (VTF) relationship, respectively. The activation energies are estimated and discussed. The dependence in frequency of AC conductivity is found to obey Jonscher’s relation.« less

Parameters optimization for the fabrication of phosphate glass/hydroxyapatite nanocomposite scaffold

NASA Astrophysics Data System (ADS)

Govindan, R.; Girija, E. K.

2015-06-01

Three-dimensional, highly porous, bioactive and biodegradable phosphate glass and nanohydroxyapatite (n-HA) composite scaffolds was fabricated by the polymer foam replication technique. Polyurethane foam (PU) and polyvinyl alcohol (PVA) were used as template and binder, respectively. Optimization of composition and sintering temperature is carried out for tissue engineering scaffold fabrication.

A comparative study of retentive strengths of zinc phosphate, polycarboxylate and glass ionomer cements with stainless steel crowns--an in vitro study.

PubMed

Reddy, R; Basappa, N; Reddy, V V

1998-03-01

This study was conducted on 30 extracted human primary molars to assess the retentive strengths of zinc phosphate, polycarboxylate and glass ionomer cements. The teeth were embedded in resin blocks and were randomly divided into 3 groups of 10 each. The occlusal surfaces of all teeth were reduced uniformly by 1.0 to 1.5 mm. All mesial, distal undercuts were removed and sharp angles rounded. This was followed by cementing pretrimmed and precontoured stainless steel crowns on each tooth with hand pressure and storing in artificial saliva at 37 degrees C for 24 hours. Retentive strength was tested using Instron Universal Testing Machine. The load was applied starting from a zero reading and gradually increased until the cemented stainless steel crowns showed signs of movement and then the readings were recorded. It was found that retentive strengths of zinc phosphate and glass ionomer cements were statistically better (P < 0.05) when compared to the polycarboxylate cement. Negligible difference (0. 59 kg/cm2) was however observed between zinc phosphate and glass ionomer cements.

X-ray-induced fluorescent centers formation in zinc- phosphate glasses doped with Ag and Cu ions

NASA Astrophysics Data System (ADS)

Klyukin, D. A.; Pshenova, A. S.; Sidorov, A. I.; Stolyarchuk, M. V.

2016-08-01

Fluorescent properties of silver and copper doped zinc-phosphate glasses were studied. By X-ray irradiation of silver and copper co-doped glasses we could create and identify new emission centers which do not exist in single-doped samples. Doping of the glass with both silver and copper ions leads to the increase of quantum yield by 2.7 times. The study was complemented by quantum chemical calculations using the time-dependent density functional theory. It was shown that fluorescence may be attributed to the formation of mixed Ag-Cu molecular clusters.

Effect of Partial Crystallization on the Structural and Luminescence Properties of Er3+-Doped Phosphate Glasses

PubMed Central

Lopez-Iscoa, Pablo; Salminen, Turkka; Hakkarainen, Teemu; Petit, Laeticia; Janner, Davide; Boetti, Nadia G.; Lastusaari, Mika; Pugliese, Diego; Paturi, Petriina; Milanese, Daniel

2017-01-01

Er-doped phosphate glass ceramics were fabricated by melt-quenching technique followed by a heat treatment. The effect of the crystallization on the structural and luminescence properties of phosphate glasses containing Al2O3, TiO2, and ZnO was investigated. The morphological and structural properties of the glass ceramics were characterized by Field Emission-Scanning Electron Microscopy (FE-SEM), X-ray Diffraction (XRD), and micro-Raman spectroscopy. Additionally, the luminescence spectra and the lifetime values were measured in order to study the influence of the crystallization on the spectroscopic properties of the glasses. The volume ratio between the crystal and the glassy phases increased along with the duration of the heat treatment. The crystallization of the glass ceramics was confirmed by the presence of sharp peaks in the XRD patterns and different crystal phases were identified depending on the glass composition. Sr(PO3)2 crystals were found to precipitate in all the investigated glasses. As evidenced by the spectroscopic properties, the site of the Er3+ ions was not strongly affected by the heat treatment except for the fully crystallized glass ceramic which does not contain Al2O3, TiO2, and ZnO. An increase of the lifetime was also observed after the heat treatment of this glass. Therefore, we suspect that the Er3+ ions are incorporated in the precipitated crystals only in this glass ceramic. PMID:28772833

Cyclic growth and dissolution of camphor crystals in quinary, ternary, and binary solutions: A study on crystal behavior in storm glass

NASA Astrophysics Data System (ADS)

Mitsuya, Takuro; Takahashi, Kyohei; Nagashima, Kazushige

2014-09-01

"Storm glass" is a hermetically sealed glass tube containing a solution of camphor. In 19th-century England, the pattern and quantity of the crystals were observed and interpreted as a weather forecasting tool. In the present study, the appearance of camphor crystals under cyclic temperature change was studied in three sample solutions, the storm glass solution (quinary system), camphor-ethanol-water (ternary system), and camphor-ethanol (binary system), to elucidate the effect of components in the storm glass on the appearance of camphor crystals. Equilibrium temperatures of camphor crystals as a function of the camphor concentration were also obtained to estimate the quantity of camphor crystals precipitated in the solutions. During the temperature cycles, the crystal height increased and decreased. The ranges (local maxima and minima) of crystal heights gradually decreased to approximately a constant range. Not only the crystal height but also the amplitude of the height variation in the quinary and ternary systems were much larger than those in the binary system, although the estimated weights of crystals precipitated in the quinary and ternary systems were smaller than that in the binary system. This fact resulted from the formation of dendrites in the quinary and ternary systems, which caused high porosity of sedimented crystals.

Antibacterial effect of gallium and silver on Pseudomonas aeruginosa treated with gallium-silver-phosphate-based glasses.

PubMed

Valappil, Sabeel P; Higham, Susan M

2014-01-01

Gallium and silver incorporated phosphate-based glasses were evaluated for antibacterial effect on the growth of Pseudomonas aeruginosa, which is a leading cause of opportunistic infections. The glasses were produced by conventional melt quenching methods at 1100°C for 1 h. Glass degradation studies were conducted by weight loss method. Disc diffusion assay and cell viability assay displayed statistically significant (p ≤ 0.0005) effect on P. aeruginosa growth which increased with decreasing calcium content in the glasses. The gallium ion release rates (1.83, 0.69 and 0.48 ppm·h(-1)) and silver ion release rates (2.97, 2.84 and 2.47 ppm·h(-1)) were found to account for this variation. Constant depth film fermentor was used to evaluate the anti-biofilm properties of the glasses. Both gallium and silver in the glass contributed to biofilm growth inhibitory effect on P. aeruginosa (up to 2.68 reduction in log 10 values of the viable counts compared with controls). The glasses were found to deliver gallium and silver in a controlled way and exerted cumulative antibacterial action on planktonic and biofilm growth of P. aeruginosa. The antibacterial, especially anti-biofilm, properties of the gallium and silver incorporated phosphate-based glasses make them a potential candidate to combat infections caused by P. aeruginosa.

Tunable luminescence mediated by energy transfer in Tm3+/Dy3+ co-doped phosphate glasses under UV excitation

NASA Astrophysics Data System (ADS)

Chen, Yong; Chen, Guohua; Liu, Xiangyu; Yuan, Changlai; Zhou, Changrong

2017-11-01

Tm3+/Dy3+ co-doped phosphate glasses for white light-emitting diodes were synthesized by a conventional melting-quenching method. A spectroscopic research based on optical, photoluminescence spectrum and decay time curves in Tm3+/Dy3+ co-doped phosphate glasses was carried out. The color of luminescence could be tuned by altering the concentrations of Tm3+ ions. Under UV light excitation, the CIE chromaticity coordinates (0.3471, 0.3374) and color correlate temperature (CCT = 4866.21 K) close to the standard white-light illumination (0.333, 0.333 and CCT = 5454.12 K) could be achieved in 0.4 Tm3+/0.6 Dy3+ (mol %) co-doped glass sample. The decrease of the Dy3+ emission decay time in existence of Tm3+ ascertained that non-radiative energy transfer from Dy3+ to Tm3+ occurred. Moreover, the research of energy transfers between Dy3+ and Tm3+ based on the Inokuti-Hirayama model revealed that an electric quadrupole-quadrupole interaction might be the predominant mechanism participated in the energy transfer. This finding suggests that the as-prepared Tm3+/Dy3+ co-doped phosphate glasses may be promising candidate for white LEDs and other display devices.

Development and characterization of a new Er3+-doped phosphate glass for planar waveguide lasers and amplifiers

NASA Astrophysics Data System (ADS)

Jiang, Shibin; Honkanen, Seppo; Luo, Tao; Hwang, Bor-Chyuan; Nunzi Conti, Gualtiero; Myers, Michael J.; Rhonehouse, Daniel L.; Peyghambarian, Nasser

1998-04-01

A new Er3+ doped phosphate glass exhibiting an excellent durability in both boiling water and NaNO3 molten salt was developed. Ion-exchange process of this glass was investigated by treating glass samples in a variety of salt bathes with various exposure times. Planar waveguide with one mode at 1.54 micrometers and three modes at 632.8 nm was demonstrated. Spectral properties of Er3+ in this glass were characterized by measuring absorption and emission spectra, and fluorescence lifetimes. Emission cross section of Er3+ in this glass was calculated to be 0.76 X 10-20 cm2 using McCumber theory. Our preliminary experimental results indicate this new Er3+ doped glass is an excellent material for ion-exchanged waveguide lasers and amplifiers.

Effect of pyrophosphate ions on the conversion of calcium-lithium-borate glass to hydroxyapatite in aqueous phosphate solution.

PubMed

Fu, Hailuo; Rahaman, Mohamed N; Day, Delbert E; Huang, Wenhai

2010-10-01

The conversion of glass to a hydroxyapatite (HA) material in an aqueous phosphate solution is used as an indication of the bioactive potential of the glass, as well as a low temperature route for preparing biologically useful materials. In this work, the effect of varying concentrations of pyrophosphate ions in the phosphate solution on the conversion of a calcium-lithium-borate glass to HA was investigated. Particles of the glass (150-355 μm) were immersed for up to 28 days in 0.25 M K(2)HPO(4) solution containing 0-0.1 M K(4)P(2)O(7). The kinetics of degradation of the glass particles and their conversion to HA were monitored by measuring the weight loss of the particles and the ionic concentration of the solution. The structure and composition of the conversion products were analyzed using X-ray diffraction, scanning electron microscopy, and Fourier transform infrared spectroscopy. For K(4)P(2)O(7) concentrations of up to 0.01 M, the glass particles converted to HA, but the time for complete conversion increased from 2 days (no K(4)P(2)O(7)) to 10 days (0.01 M K(4)P(2)O(7)). When the K(4)P(2)O(7) concentration was increased to 0.1 M, the product consisted of an amorphous calcium phosphate material, which eventually crystallized to a pyrophosphate product (predominantly K(2)CaP(2)O(7) and Ca(2)P(2)O(7)). The consequences of the results for the formation of HA materials and devices by the glass conversion route are discussed.

Effect of pyrophosphate ions on the conversion of calcium–lithium–borate glass to hydroxyapatite in aqueous phosphate solution

PubMed Central

Fu, Hailuo; Day, Delbert E.; Huang, Wenhai

2010-01-01

The conversion of glass to a hydroxyapatite (HA) material in an aqueous phosphate solution is used as an indication of the bioactive potential of the glass, as well as a low temperature route for preparing biologically useful materials. In this work, the effect of varying concentrations of pyrophosphate ions in the phosphate solution on the conversion of a calcium–lithium–borate glass to HA was investigated. Particles of the glass (150–355 µm) were immersed for up to 28 days in 0.25 M K2HPO4 solution containing 0–0.1 M K4P2O7. The kinetics of degradation of the glass particles and their conversion to HA were monitored by measuring the weight loss of the particles and the ionic concentration of the solution. The structure and composition of the conversion products were analyzed using X-ray diffraction, scanning electron microscopy, and Fourier transform infrared spectroscopy. For K4P2O7 concentrations of up to 0.01 M, the glass particles converted to HA, but the time for complete conversion increased from 2 days (no K4P2O7) to 10 days (0.01 M K4P2O7). When the K4P2O7 concentration was increased to 0.1 M, the product consisted of an amorphous calcium phosphate material, which eventually crystallized to a pyrophosphate product (predominantly K2CaP2O7 and Ca2P2O7). The consequences of the results for the formation of HA materials and devices by the glass conversion route are discussed. PMID:20680413

Two-photon excited microscale colour centre patterns in Ag-activated phosphate glass written using a focused proton beam

NASA Astrophysics Data System (ADS)

Kurobori, Toshio; Kada, Wataru; Shirao, Taichi; Satoh, Takahiro

2018-02-01

We report a demonstration of microscale patterns in Ag-activated phosphate glass fabricated using a focused proton beam with an energy range of 1-3 MeV. Various microscale patterns are based on blue and orange radiophotoluminescent (RPL) centres. Two- and three-dimensional (2D and 3D) microstructures are visualised by combining two-photon confocal microscopy with femtosecond (fs) laser pulses generated from a mode-locked Ti:sapphire laser operating at 700 nm. The reconstructed images are analytically evaluated using lateral/axial dose mapping and RPL spectra. In addition, the advantages of two-photon excitation applied to Ag-activated phosphate glass are discussed, and this method is compared with single-photon excitation.

Effect of nanosecond UV laser irradiation on luminescence and absorption in silver- and copper-containing phosphate glasses

NASA Astrophysics Data System (ADS)

Murashov, A. A.; Sidorov, A. I.; Stoliarchuk, M. V.

2018-03-01

Experimental evidence is presented that nanosecond UV laser irradiation of silver- and copper-containing barium phosphate glasses leads to luminescence quenching in the visible range. Subsequent heat treatment induces an absorption in the range 350–500 nm. These effects are due to the ionisation and fragmentation of subnanometre molecular clusters by laser radiation and subsequent (heat treatment-induced) formation of nanoparticles possessing plasmon resonance. Our numerical modelling results demonstrate the feasibility of producing stable AgnCum hybrid molecular clusters in glass. Local modification of the optical properties of glass by laser light can be used for optical information recording.

Evidence of phase transition in Nd3+ doped phosphate glass determined by thermal lens spectrometry.

PubMed

Andrade, Acácio A; Lourenço, Sidney A; Pilla, Viviane; Silva, Anielle C Almeida; Dantas, Noelio O

2014-01-28

Thermal lens spectroscopy (TLS), differential scanning calorimetry (DSC) and Fourier transform infrared (FTIR) techniques were applied to the thermo-optical property analysis of a new phosphate glass matrix PANK with nominal composition 40P2O5·20Al2O3·35Na2O·5K2O (mol%), doped with different Nd(3+) compositions. This glass system, synthesized by the fusion protocol, presents high transparency from UV to the near infrared, excellent thermo-optical properties at room temperature and high fluorescence quantum efficiency. Thermal lens phase shift parameters, thermal diffusivity and the DSC signal present pronounced changes at about 61 °C for the PANK glass system. This anomalous behavior was associated with a phase transition in the nanostructured glass materials. The FTIR signal confirms the presence of isolated PO4 tetrahedron groups connected to different cations in PANK glass. As a main result, our experimental data suggest that these tetrahedron groups present a structural phase transition, paraelectric-ferroelectric phase transition, similar to that in potassium dihydrogen phosphate, KH2PO4, nanocrystals and which TLS technique can be used as a sensitive method to investigate changes in the structural level of nanostructured materials.

Novel method for early investigation of bioactivity in different borate bio-glasses.

PubMed

Abdelghany, A M

2013-01-01

Some ternary borate glasses were prepared and corrosion behavior of such ternary borate glasses after immersion in aqueous dilute phosphate solution was studied using different immersion times. Fourier transform infrared (FTIR) absorption spectral measurements were done before and after immersion in the mentioned solution for extended times up to 2 days to justify the appearance of the characteristic FTIR bands due to calcium phosphate (hydroxyapatite (HA)) which is considered as the potential indication of bioactivity. Experimental IR data confirm the beginning of the appearance of FTIR bands at about 580 and 620 cm(-1) after 3 days and the complete resolution with its characteristic split form after 1 week and more. Deconvolution analysis technique (DAT) of the FTIR spectrum was employed to investigate the bioactivity of such ternary borate system after a short period of immersion. The corrosion behavior of such glasses is explained in relation to a suggested hydrolysis followed by direct dissolution mechanism. The ease of dissolution of all the borate glasses constituents explains the formation of calcium phosphate and conversion to crystalline hydroxyapatite within the borate glass matrix. X-ray diffraction may be used to retrace the structural changes and degree of crystallinity of the prepared glasses. Copyright © 2012 Elsevier B.V. All rights reserved.

Sodium aluminum-iron phosphate glass-ceramics for immobilization of lanthanide oxide wastes from pyrochemical reprocessing of spent nuclear fuel

NASA Astrophysics Data System (ADS)

Stefanovsky, S. V.; Stefanovsky, O. I.; Kadyko, M. I.; Nikonov, B. S.

2018-03-01

Sodium aluminum (iron) phosphate glass ceramics containing of up to 20 wt.% rare earth (RE) oxides simulating pyroprocessing waste were produced by melting at 1250 °C followed by either quenching or slow cooling to room temperature. The iron-free glass-ceramics were composed of major glass and minor phosphotridymite and monazite. The iron-bearing glass-ceramics were composed of major glass and minor monazite and Na-Al-Fe orthophosphate at low waste loadings (5-10 wt.%) and major orthophosphate and minor monazite as well as interstitial glass at high waste loadings (15-20 wt.%). Slowly cooled samples contained higher amount of crystalline phases than quenched ones. Monazite is major phase for REs. Leach rates from the materials of major elements (Na, Al, Fe, P) are 10-5-10-7 g cm-2 d-1, RE elements - lower than 10-5 g cm-2 d-1.

Influence of silver and copper doping on luminescent properties of zinc-phosphate glasses after x-ray irradiation

NASA Astrophysics Data System (ADS)

Murashov, Alexander A.; Sidorov, Alexander I.; Shakhverdov, Teimur A.; Stolyarchuk, Maxim V.

2017-11-01

It is shown, experimentally, that in silver- and copper-containing zinc-phosphate glasses, metal molecular clusters are formed during the glass synthesis. X-ray irradiation of these glasses led to the considerable increase of its luminescence in visible spectral range. This effect is caused by the transformation of the charged metal molecular clusters into the neutral state. Luminescence and excitation spectra of the glass, doped with silver and copper simultaneously, change significantly in comparison with the spectra of glasses doped with one metal. The reason for this can be the formation of hybrid AgnCum molecular clusters. The computer simulation of the structure and optical properties of such clusters by the time-dependent density functional theory method is presented. It is shown that the optimal luminescent material for photonics application, in comparison with other studied materials, is glass, containing hybrid molecular clusters.

Optical Spectra Tuning of All-Glass Photonic Bandgap Fiber Infiltrated with Silver Fast-Ion-Conducting Glasses.

PubMed

Konidakis, Ioannis; Pissadakis, Stavros

2014-08-07

Silver iodide metaphosphate glasses of the x AgI + (1- x )AgPO₃ family are embedded inside the air capillaries of a commercial silica photonic crystal fiber (PCF) by means of vacuum-assisted infiltration technique. In this paper, we report on tuning the photonic bandgap (PBG) guidance characteristics of the fabricated all-glass photonic bandgap fibers, by varying the composition of the fast-ion-conducting phosphate glass infiltration medium. Doping AgPO₃ metaphosphate glass with AgI significantly alters the PBG guidance patterns in the examined range between 350 and 1750 nm, as it leads to the introduction of numerous additional transmission stop-bands, while affecting scattering dependant losses. The effect of phosphate glass cooling method during sample fabrication on the transmission behavior of the x AgI + (1- x )AgPO₃/PCFs is also considered.

Structural aspects of calcium iron phosphate glass containing neodymium oxide

NASA Astrophysics Data System (ADS)

Li, Haijian; Liang, Xiaofeng; Wang, Cuiling; Yu, Huijun; Li, Zhen; Yang, Shiyuan

2014-06-01

Homogeneous glasses of the xNd2O3sbnd (100 - x)(12CaOsbnd 20Fe2O3sbnd 68P2O5) system were obtained within the 0 ⩽ x ⩽ 10 mol% composition range. The density and molar volume measurements helped to understand the structural changes occurring in these glasses. Vickers-hardness results showed that addition of Nd2O3 strengthened the crosslinking of the glass network. Spectra analysis indicated that Nd2O3 enters in the structure of the phosphate glasses as a network modifier. The depolymerization of the glass network by the addition of Nd2O3 is characterized by the increase in the concentration of pyrophosphate. The decrease of the Q1 terminal oxygen with increasing Nd2O3 content indicated that Psbnd Osbnd Nd bonds participated in the pyrophosphate glass structure, determined from the Raman spectra.

Surface or internal nucleation and crystallization of glass-ceramics

NASA Astrophysics Data System (ADS)

Höland, W.; Rheinberger, V. M.; Ritzberger, C.; Apel, E.

2013-07-01

Fluoroapatite (Ca5(PO4)3F) was precipitated in glass-ceramics via internal crystallization of base glasses. The crystals grew with a needle-like morphology in the direction of the crystallographic c-axis. Two different reaction mechanisms were analyzed: precipitation via a disordered primary apatite crystals and a solid state parallel reaction to rhenanite (NaCaPO4) precipitation. In contrast to the internal nucleation used in the formation of fluoroapatite, surface crystallization was induced to precipitate a phosphate-free oxyapatite of NaY9(SiO4)6O2-type. Internal nucleation and crystallization have been shown to be a very useful tool for developing high-strength lithium disilicate (Li2Si2O5) glass-ceramics. A very controlled process was conducted to transform the lithium metasilicate glass-ceramic precursor material into the final product of the lithium disilicate glass-ceramic without the major phase of the precursor material. The combination of all these methods allowed the driving forces of the internal nucleation and crystallization mechanisms to be explained. An amorphous phosphate primary phase was discovered in the process. Nucleation started at the interface between the amorphous phosphate phase and the glass matrix. The final products of all these glass-ceramics are biomaterials for dental restoration showing special optical properties, e.g. translucence and color close to dental teeth.

Structural and spectroscopic investigations on deuteron glasses belonging to the potassium dihydrogen phosphate family

DOE Office of Scientific and Technical Information (OSTI.GOV)

Choudhury, Rajul Ranjan, E-mail: rajul@barc.gov.in; Chitra, R.; Abraham, Geogy J.

2015-06-24

X-ray powder diffraction and Raman measurements were performed on the mixed crystals of deuterated potassium dihydrogen phosphate (DKDP) and deuterated ammonium dihydrogen phosphate (DADP) grown at our lab. These crystals are known to behave like deuteron glasses due to frustration between ferroelectric and antiferroelectric ordering. Both spectral as well as structural studies indicate that crystals belonging to the glassy regions of the crystal composition have stronger O-D-O hydrogen bonds as compared to those belong to the ferroelectric or antiferroelectric regions of the crystal composition.

Phosphate-core silica-clad Er/Yb-doped optical fiber and cladding pumped laser.

PubMed

Egorova, O N; Semjonov, S L; Velmiskin, V V; Yatsenko, Yu P; Sverchkov, S E; Galagan, B I; Denker, B I; Dianov, E M

2014-04-07

We present a composite optical fiber with a Er/Yb co-doped phosphate-glass core in a silica glass cladding as well as cladding pumped laser. The fabrication process, optical properties, and lasing parameters are described. The slope efficiency under 980 nm cladding pumping reached 39% with respect to the absorbed pump power and 28% with respect to the coupled pump power. Due to high doping level of the phosphate core optimal length was several times shorter than that of silica core fibers.

[Influence of adhesion on the color of glass infiltrated alumina ceramic restorations].

PubMed

Jiang, Li; Yang, Liu; Xu, Qiang; Guan, Hong-Yu; Wan, Qian-Bing

2006-10-01

To investigate the effects of luting agent on the final color of glass infiltrated alumina ceramic restorations. 12 plate-shaped specimens with 12.5 mm in diameter and 0.5 mm thickness were fabricated from GI-II (color IG2). Vitadur alpha veneering porcelain (color A2) with 1.0 mm thickness was fired to GI- II glass/alumina composite. 12 plate-shaped background specimens simulating the metal alloy post-and-core 12.5 mm in diameter and 2 mm thickness were also made from Ni-Cr alloy. All-ceramic specimens were luted to the metal alloy by Zinc Phosphate cement, glass ionomer cement and composite resin. The color shifts of the specimens were measured by colorimeter. Luting agents had effect on the final color of restorations. The influence of composite resin was least, followed by glass ionomer cement and Zinc Phosphate cement. The color difference between with and without Zinc Phosphate cement could be identified by the eye. To reduce the effect of luting agents, composite resin is recommended to all-ceramic restorations' adhesion.

Multi-layer porous fiber-reinforced composites for implants: in vitro calcium phosphate formation in the presence of bioactive glass.

PubMed

Nganga, Sara; Zhang, Di; Moritz, Niko; Vallittu, Pekka K; Hupa, Leena

2012-11-01

Glass-fiber-reinforced composites (FRCs), based on bifunctional methacrylate resin, have recently shown their potential for use as durable cranioplasty, orthopedic and oral implants. In this study we suggest a multi-component sandwich implant structure with (i) outer layers out of porous FRC, which interface the cortical bone, and (ii) inner layers encompassing bioactive glass granules, which interface with the cancellous bone. The capability of Bioglass(®) 45S5 granules (100-250μm) to induce calcium phosphate formation on the surface of the FRC was explored by immersing the porous FRC-Bioglass laminates in simulated body fluid (SBF) for up to 28d. In both static (agitated) and dynamic conditions, bioactive glass granules induced precipitation of calcium phosphate at the laminate surfaces as confirmed by scanning electron microscopy. The proposed dynamic flow system is useful for the in vitro simulation of bone-like apatite formation on various new porous implant designs containing bioactive glass and implant material degradation. Copyright © 2012 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

A Solid-State NMR Experiment: Analysis of Local Structural Environments in Phosphate Glasses

ERIC Educational Resources Information Center

Anderson, Stanley E.; Saiki, David; Eckert, Hellmut; Meise-Gresch, Karin

2004-01-01

An experiment that can be used to directly study the local chemical environments of phosphorus in solid amorphous materials is demonstrated. The experiment aims at familiarizing the students of chemistry with the principles of solid-state NMR, by having them synthesize a simple phosphate glass, and making them observe the (super 31)P NMR spectrum,…

Visible emission in Sm3+ and Tb3+ doped phosphate glass excited by UV radiation

NASA Astrophysics Data System (ADS)

Zmojda, Jacek; Dorosz, Dominik; Kochanowicz, Marcin; Miluski, Piotr; Czajkowski, Karol; Ragin, Tomasz

2013-10-01

In the article analysis of UV absorption and visible fluorescence of Sm3+ and Tb3+ ions doped phosphate glass with molar composition: 65P2O5 + 8Al2O3 + 10BaO + 17(Na2O + MgO + ZnO) have been investigated. As a result of optical pumping fabricated glass with radiation from a deuterium lamp four luminescence bands were observed near to the wavelength of 600 nm for Sm3+ ions and 550 nm for Tb3+ ions. It was found that larger energy gap between laser and ground levels leads to the strongest emission in the visible range in terbium doped glasses than in glasses doped with samarium ions. Both fabricated glasses are characterized by the ability to selectively detect the radiation in the UV range.

Anneal-induced enhancement of refractive index and hardness of silicophosphate glasses containing six-fold coordinated silicon

DOE Office of Scientific and Technical Information (OSTI.GOV)

Zeng, Huidan, E-mail: hdzeng@ecust.edu.cn; Jiang, Qi; Li, Xiang

2015-01-12

A considerable number of optical devices have significantly benefited from the development of phosphate glasses as substrate materials. Introducing silica into sodium phosphate is an effective method to enhance its mechanical and optical properties. Through annealing treatment, the tetrahedral silicon oxide network structure (Si{sup (4)}) can be transformed into an octahedral structure (Si{sup (6)}) with more constraints. Here, we use high-temperature Raman and Nuclear Magnetic Resonance to reveal the mechanism of transformation between the Si{sup (4)} and Si{sup (6)} silicon oxide structures. The increase of the Si{sup (6)} content results in the phosphate glasses having higher refractive index and hardness.more » Based on this, the refractive index contribution of SiO{sub 6} is obtained.« less

Effect of composition and temperature on the second harmonic generation in silver phosphate glasses

NASA Astrophysics Data System (ADS)

Konidakis, I.; Psilodimitrakopoulos, S.; Kosma, K.; Lemonis, A.; Stratakis, E.

2018-01-01

We herein employ nonlinear laser imaging microscopy to explicitly study the dynamics of second harmonic generation (SHG) in silver iodide phosphate glasses. While glasses of this family have gained extensive scientific attention over the years due to their superior conducting properties, considerably less attention has been paid to their unique nonlinear optical characteristics. In the present study, firstly, it is demonstrated that SHG signal intensity is enhanced upon increasing silver content due to the random formation of silver microstructures within the glass network. Secondly, the SHG temperature dynamics were explored near the glass transition temperature (Tg) regime, where significant glass relaxation phenomena occur. It is found that heating towards the Tg improves the SHG efficiency, whereas above Tg, the capacity of glasses to generate second harmonic radiation is drastically suppressed. The novel findings of this work are considered important in terms of the potential employment of these glasses for the realization of advanced photonic applications like optical-switches and wavelength conversion devices.

Phytic acid derived bioactive CaO-P2O5-SiO2 gel-glasses.

PubMed

Li, Ailing; Qiu, Dong

2011-12-01

The possibility of using phytic acid as a precursor to synthesize CaO-P(2)O(5)-SiO(2) glasses by sol-gel method has been explored and the pseudo ternary phase diagram has been established. It was shown that gel-glasses over a broader range of compositions could be prepared compared to other phosphorus precursors or melt-quenching method. Furthermore, phytic acid was found to assist calcium being incorporated into glass networks. In vitro tests in simulated body fluid (SBF) were performed on the above gel-glasses and it was found that they were bioactive over a much broader compositional range especially at high phosphate content, thus enabling one to design bioactive materials with various degradation rates by adjusting the phosphate content.

Spectroscopic identification of rare earth elements in phosphate glass

NASA Astrophysics Data System (ADS)

Devangad, Praveen; Tamboli, Maktum; Muhammed Shameem, K. M.; Nayak, Rajesh; Patil, Ajeetkumar; Unnikrishnan, V. K.; Santhosh, C.; Kumar, G. A.

2018-01-01

In this work, rare earth-doped phosphate glasses were synthesized and characterized using three different spectroscopic techniques. The absorption spectra of the prepared praseodymium (Pr) and samarium (Sm) doped glasses, recorded by a UV-VIS-NIR spectrophotometer, show the characteristic absorption bands of these elements. To confirm this inference, laser-induced fluorescence spectra of Pr and Sm were obtained at a laser excitation of 442 nm. Their emission bands are reported here. The elemental analysis of these samples was carried out using a laser-induced breakdown spectroscopy (LIBS) system. Characteristic emission lines of Pr and Sm have been identified and reported by the recorded LIBS spectra of glass samples. Results prove that using these three complimentary spectroscopic techniques (absorption, fluorescence and LIBS), we can meaningfully characterize rare earth-doped glass samples.

Polaronic conductivity and scaling behavior of lithium iron phosphate glass

NASA Astrophysics Data System (ADS)

Banday, Azeem; Murugavel, Sevi

2018-05-01

Charge transport properties of the Lithium Iron Phosphate (LFP) glass has been investigated in a wide frequency and temperature range by means of broadband dielectric spectroscopy. The conductivity spectra has been studied on the basis of Jonscher power law for characterizing the hopping dynamics of charge carriers. The ac conductivity and scaling behavior of the LFP glass has been studied in the temperature range from 333K to 573K and frequency range from 100 mHz to 1 MHz. The conductivity isotherms of LFP glass do not superimpose upon each other by using Summerfield scaling. The structural peculiarities in the material could result in different conduction pathways giving rise to the deviation from Summerfield scaling.

Development, characterisation and biocompatibility testing of a cobalt-containing titanium phosphate-based glass for engineering of vascularized hard tissues.

PubMed

Lee, In-Ho; Yu, Hye-sun; Lakhkar, Nilay J; Kim, Hae-Won; Gong, Myoung-Seon; Knowles, Jonathan C; Wall, Ivan B

2013-05-01

There is a continuing need to develop scaffold materials that can promote vascularisation throughout the tissue engineered construct. This study investigated the effect of cobalt oxide (CoO) doped into titanium phosphate glasses on material properties, biocompatibility and vascular endothelial growth factor (VEGF) secretion by osteoblastic MG63 cells. Glasses composed of (P2O5)45(Na2O)20(TiO2)05(CaO)30-x(CoO)x(x=0, 5, 10, and 15 mol%) were fabricated and the effect of Co on physicochemical properties including density, glass transition temperature (Tg), degradation rate, ion release, and pH changes was assessed. The results showed that incorporation of CoO into the glass system produced an increase in density with little change in Tg. It was then confirmed that the pH did not change significantly when CoO was incorporated in the glass, and stayed constant at around 6.5-7.0 throughout the dissolution study period of 336 h. Ion release results followed a specific pattern with increasing amounts of CoO. In general, although incorporation of CoO into a titanium phosphate glass increased its density, other bulk and surface properties of the glass did not show any significant changes. Cell culture studies performed using MG63 cells over a 7-day period indicated that the glasses provide a stable surface for cell attachment and are biocompatible. Furthermore, VEGF secretion was significantly enhanced on all glasses compared with standard tissue culture plastic and Co doping enhanced this effect further. In conclusion, the developed Co-doped glasses are stable and biocompatible and thus offer enhanced potential for engineering vascularized tissue. Crown Copyright © 2013. Published by Elsevier B.V. All rights reserved.

Multiple Doped Erbium Glasses,

DTIC Science & Technology

GLASS, LASERS, ERBIUM, ERBIUM COMPOUNDS, DOPING, OXIDES, OPTIMIZATION, ATOMIC ENERGY LEVELS, PHOSPHATES , YTTERBIUM COMPOUNDS, NEODYMIUM COMPOUNDS, OPTICAL PUMPING, FLUORESCENCE, LIFE EXPECTANCY(SERVICE LIFE), BAND SPECTRA.

Phosphorus solubility in basaltic glass: Limitations for phosphorus immobilization in glass and glass-ceramics.

PubMed

Tarrago, M; Garcia-Valles, M; Martínez, S; Neuville, D R

2018-05-11

The composition of sewage sludge from urban wastewater treatment plants is simulated using P-doped basalts. Electron microscopy analyses show that the solubility of P in the basaltic melt is limited by the formation of a liquid-liquid immiscibility in the form of an aluminosilicate phase and a Ca-Mg-Fe-rich phosphate phase. The rheological behavior of these compositions is influenced by both phase separation and nanocrystallization. Upon a thermal treatment, the glasses will crystallize into a mixture of inosilicates and spinel-like phases at low P contents and into Ca-Mg-Fe phosphate at high P contents. Hardness measurements yield values between 5.41 and 7.66 GPa, inside the range of commercial glasses and glass-ceramics. Leaching affects mainly unstable Mg 2+ -PO 4 3- complexes. Copyright © 2018 Elsevier Ltd. All rights reserved.

Influence of CuO and ZnO addition on the multicomponent phosphate glasses: Spectroscopic studies

NASA Astrophysics Data System (ADS)

Szumera, Magdalena; Wacławska, Irena; Sułowska, Justyna

2016-06-01

The spectra of phosphate-silicate glasses from the P2O5-SiO2-K2O-MgO-CaO system modified with the addition of CuO or ZnO have been studied by means of FTIR, Raman and 31P MAS NMR spectroscopy. All glasses were synthesized by the conventional melt-quenching technique and their homogeneous chemical composition was controlled and confirmed. By using the aforementioned research techniques, the presence of structural units with various degrees of polymerization was shown in the structure of analyzed phosphate-silicate glasses: Q3, Q2, Q1 and Q0. It was found that an increase in the content of CuO or ZnO in the composition of analyzed glasses, which are introduced at the expense of decreasing amounts of CaO and MgO, has a different influence on the phospho-oxygen network. It was shown that copper ions cause its gradual polymerization, while zinc ions cause its depolymerization. At the same time, polymerization of the silico-oxygen subnetwork was found. Additionally, in the case of glasses containing increasing amounts of ZnO, a change of the role of zinc ions in the vitreous matrix was confirmed (from the modifier to a structure-forming component).

A comparative study of retentive strengths of zinc phosphate, polycarboxylate and glass ionomer cements with stainless steel crowns - an in vitro study.

PubMed

Raghunath Reddy, M H; Subba Reddy, V V; Basappa, N

2010-01-01

An in vitro study was conducted to compare the retentive strengths of zinc phosphate, polycarboxylate and glass ionomer cements using Instron universal testing machine. Thirty preformed and pretrimmed stainless steel crowns were used for cementation on 30 extracted human primary molars which were divided into three groups of 10 teeth in each group. Then the teeth were stored in artificial saliva and incubated at 37°C for 24 h. A load was applied on to the crown and was gradually increased till the crown showed dislodgement, and then the readings were recorded using Instron recorder and analyzed for statistical significance. The surface area of crown was measured by graphical method. The retentive strength was expressed in terms of kg/cm 2 , which was calculated by the equation load divided by area. Retentive strengths of zinc phosphate (ranged from a minimum of 16.93 to amaximum of 28.13 kg/cm 2 with mean of 21.28 kg/cm 2 ) and glass ionomer cement (minimum of 13.69 - 28.15 kg/cm 2 with mean of 20.69 kg/cm 2 ) were greater than that of polycarboxylate cement (minimum of 13.26 - 22.69 kg/cm 2 with mean of 16.79 kg/cm 2 ). Negligible difference (0.59 kg/cm 2 ) of retentive strength was observed between zinc phosphate (21.28 kg/cm 2 ) and glass ionomer cements (20.69 kg/cm 2 ). Glass ionomer cements can be recommended for cementation of stainless steel crowns because of its advantages and the retentive strength was almost similar to that of zinc phosphate cement.

Experimental evidence for excess entropy discontinuities in glass-forming solutions.

PubMed

Lienhard, Daniel M; Zobrist, Bernhard; Zuend, Andreas; Krieger, Ulrich K; Peter, Thomas

2012-02-21

Glass transition temperatures T(g) are investigated in aqueous binary and multi-component solutions consisting of citric acid, calcium nitrate (Ca(NO(3))(2)), malonic acid, raffinose, and ammonium bisulfate (NH(4)HSO(4)) using a differential scanning calorimeter. Based on measured glass transition temperatures of binary aqueous mixtures and fitted binary coefficients, the T(g) of multi-component systems can be predicted using mixing rules. However, the experimentally observed T(g) in multi-component solutions show considerable deviations from two theoretical approaches considered. The deviations from these predictions are explained in terms of the molar excess mixing entropy difference between the supercooled liquid and glassy state at T(g). The multi-component mixtures involve contributions to these excess mixing entropies that the mixing rules do not take into account. © 2012 American Institute of Physics

Chemical composition and binary mixture of human urinary stones using FT-Raman spectroscopy method.

PubMed

Selvaraju, R; Raja, A; Thiruppathi, G

2013-10-01

In the present study the human urinary stones were observed in their different chemical compositions of calcium oxalate monohydrate, calcium oxalate dihydrate, calcium phosphate, struvite (magnesium ammonium phosphate), uric acid, cystine, oxammite (ammonium oxalate monohydrate), natroxalate (sodium oxalate), glushinkite (magnesium oxalate dihydrate) and moolooite (copper oxalate) were analyzed using Fourier Transform-Raman (FT-Raman) spectroscopy. For the quantitative analysis, various human urinary stone samples are used for ratios calculation of binary mixtures compositions such as COM/COD, HAP/COD, HAP/COD, Uric acid/COM, uric acid/COD and uric acid/HAP. The calibration curve is used for further analysis of binary mixture of human urinary stones. For the binary mixture calculation the various intensities bands at 1462 cm(-1) (I(COM)), 1473 cm(-1) (I(COD)), 961 cm(-1) (I(HAP)) and 1282 cm(-1) (I(UA)) were used. Copyright © 2013 Elsevier B.V. All rights reserved.

Iron Phosphate Glass-Containing Hanford Waste Simulant

DOE Office of Scientific and Technical Information (OSTI.GOV)

Sevigny, Gary J.; Kimura, Marcia L.; Fischer, Christopher M.

2012-01-18

Resolution of the nation's high-level tank waste legacy requires the design, construction, and operation of large and technically complex one-of-a-kind processing waste treatment and vitrification facilities. While the ultimate limits for waste loading and melter efficiency have yet to be defined or realized, significant reductions in glass volumes for disposal and mission life may be possible with advancements in melter technologies and/or glass formulations. This test report describes the experimental results from a small-scale test using the research-scale melter (RSM) at Pacific Northwest National Laboratory (PNNL) to demonstrate the viability of iron-phosphate-based glass with a selected waste composition that ismore » high in sulfate (4.37 wt% SO3). The primary objective of the test was to develop data to support a cost-benefit analysis related to the implementation of phosphate-based glasses for Hanford low-activity waste (LAW) and/or other high-level waste streams within the U.S. Department of Energy complex. The testing was performed by PNNL and supported by Idaho National Laboratory, Savannah River National Laboratory, Missouri University of Science and Technology, and Mo-Sci Corporation.« less

DOE Office of Scientific and Technical Information (OSTI.GOV)

Yao, Aihua, E-mail: aihyao@126.com; Ai, Fanrong; Liu, Xin

Hollow hydroxyapatite microspheres, consisting of a hollow core and a porous shell, were prepared by converting Li{sub 2}O-CaO-B{sub 2}O{sub 3} glass microspheres in dilute phosphate solution at 37 {sup o}C. The results confirmed that Li{sub 2}O-CaO-B{sub 2}O{sub 3} glass was transformed to hydroxyapatite without changing the external shape and dimension of the original glass object. Scanning electron microscopy images showed the shell wall of the microsphere was built from hydroxyapatite particles, and these particles spontaneously align with one another to form a porous sphere with an interior cavity. Increase in phosphate concentration resulted in an increase in the reaction rate,more » which in turn had an effect on shell wall structure of the hollow hydroxyapatite microsphere. For the Li{sub 2}O-CaO-B{sub 2}O{sub 3} glass microspheres reacted in low-concentration K{sub 2}HPO{sub 4} solution, lower reaction rate and a multilayered microstructure were observed. On the other hand, the glass microspheres reacted in higher phosphate solution converted more rapidly and produced a single hydroxyapatite layer. Furthermore, the mechanism of forming hydroxyapatite hollow microsphere was described.« less

Spatially selective Au nanoparticle growth in laser-quality glass controlled by UV-induced phosphate-chain cross-linkage

NASA Astrophysics Data System (ADS)

Sigaev, Vladimir N.; Savinkov, Vitaly I.; Lotarev, Sergey V.; Shakhgildyan, Georgiy Yu; Lorenzi, Roberto; Paleari, Alberto

2013-06-01

Herein we describe how UV excitation of localized electronic states in phosphate glasses can activate structural rearrangements that influence the kinetics of Au nanoparticle (NP) thermal growth in Au-doped glass. The results suggest a novel strategy to address the problem of controlling nano-assembly processes of metal NP patterns in fully inorganic and chemically stable hard materials, such as laser-quality glasses. We show that the mechanism is promoted by opening and subsequent cross-linkage of phosphate chains under UV excitation of non-bridging groups in the amorphous network of the glass, with a consequent modification of Au diffusion and metal NP growth. Importantly, the micro-Raman mapping of the UV-induced modifications demonstrates that the process is restricted within the beam waist region of the focused UV laser beam. This fact is consistent with the need for more than one excitation event, close in time and in space, in order to promote structural cross-linkage and Au diffusion confinement. The stability of the photo-induced modifications makes it possible to design new metal patterning approaches for the fabrication of three-dimensional metal structures in laser-quality materials for high-power nonlinear applications.

Spatially selective Au nanoparticle growth in laser-quality glass controlled by UV-induced phosphate-chain cross-linkage.

PubMed

Sigaev, Vladimir N; Savinkov, Vitaly I; Lotarev, Sergey V; Shakhgildyan, Georgiy Yu; Lorenzi, Roberto; Paleari, Alberto

2013-06-07

Herein we describe how UV excitation of localized electronic states in phosphate glasses can activate structural rearrangements that influence the kinetics of Au nanoparticle (NP) thermal growth in Au-doped glass. The results suggest a novel strategy to address the problem of controlling nano-assembly processes of metal NP patterns in fully inorganic and chemically stable hard materials, such as laser-quality glasses. We show that the mechanism is promoted by opening and subsequent cross-linkage of phosphate chains under UV excitation of non-bridging groups in the amorphous network of the glass, with a consequent modification of Au diffusion and metal NP growth. Importantly, the micro-Raman mapping of the UV-induced modifications demonstrates that the process is restricted within the beam waist region of the focused UV laser beam. This fact is consistent with the need for more than one excitation event, close in time and in space, in order to promote structural cross-linkage and Au diffusion confinement. The stability of the photo-induced modifications makes it possible to design new metal patterning approaches for the fabrication of three-dimensional metal structures in laser-quality materials for high-power nonlinear applications.

Computational studies of the glass-forming ability of model bulk metallic glasses

NASA Astrophysics Data System (ADS)

Zhang, Kai; Wang, Minglei; Papanikolaou, Stefanos; Liu, Yanhui; Schroers, Jan; Shattuck, Mark D.; O'Hern, Corey S.

2013-09-01

Bulk metallic glasses (BMGs) are produced by rapidly thermally quenching supercooled liquid metal alloys below the glass transition temperature at rates much faster than the critical cooling rate Rc below which crystallization occurs. The glass-forming ability of BMGs increases with decreasing Rc, and thus good glass-formers possess small values of Rc. We perform molecular dynamics simulations of binary Lennard-Jones (LJ) mixtures to quantify how key parameters, such as the stoichiometry, particle size difference, attraction strength, and heat of mixing, influence the glass-formability of model BMGs. For binary LJ mixtures, we find that the best glass-forming mixtures possess atomic size ratios (small to large) less than 0.92 and stoichiometries near 50:50 by number. In addition, weaker attractive interactions between the smaller atoms facilitate glass formation, whereas negative heats of mixing (in the experimentally relevant regime) do not change Rc significantly. These results are tempered by the fact that the slowest cooling rates achieved in our simulations correspond to ˜1011 K/s, which is several orders of magnitude higher than Rc for typical BMGs. Despite this, our studies represent a first step in the development of computational methods for quantitatively predicting glass-formability.

Q-Speciation and Network Structure Evolution in Invert Calcium Silicate Glasses.

PubMed

Kaseman, Derrick C; Retsinas, A; Kalampounias, A G; Papatheodorou, G N; Sen, S

2015-07-02

Binary silicate glasses in the system CaO-SiO2 are synthesized over an extended composition range (42 mol % ≤ CaO ≤ 61 mol %), using container-less aerodynamic levitation techniques and CO2-laser heating. The compositional evolution of Q speciation in these glasses is quantified using (29)Si and (17)O magic angle spinning nuclear magnetic resonance spectroscopy. The results indicate progressive depolymerization of the silicate network upon addition of CaO and significant deviation of the Q speciation from the binary model. The equilibrium constants for the various Q species disproportionation reactions for these glasses are found to be similar to (much smaller than) those characteristic of Li (Mg)-silicate glasses, consistent with the corresponding trends in the field strengths of these modifier cations. Increasing CaO concentration results in an increase in the packing density and structural rigidity of these glasses and consequently in their glass transition temperature Tg. This apparent role reversal of conventional network-modifying cations in invert alkaline-earth silicate glasses are compared and contrasted with that in their alkali silicate counterparts.

Analysis of Nd3+:glass, solar-pumped, high-powr laser systems

NASA Technical Reports Server (NTRS)

Zapata, L. E.; Williams, M. D.

1989-01-01

The operating characteristics of Nd(3+):glass lasers energized by a solar concentrator were analyzed for the hosts YAG, silicate glass, and phosphate glass. The modeling is based on the slab zigzag laser geometry and assumes that chemical hardening methods for glass are successful in increasing glass hardness by a factor of 4. On this basis, it was found that a realistic 1-MW solar-pumped laser might be constructed from phosphate glass 4 sq m in area and 2 mm thick. If YAG were the host medium, a 1-MW solar-pumped laser need only be 0.5 sq m in area and 0.5 cm thick, which is already possible. In addition, Nd(3+) doped glass fibers were found to be excellent solar-pumped laser candidates. The small diameter of fibers eliminates thermal stress problems, and if their diameter is kept small (10 microns), they propagate a Gaussian single mode which can be expanded and transmitted long distances in space. Fiber lasers could then be used for communications in space or could be bundled and the individual beams summed or phase-matched for high-power operation.

Glass transition in ferroic glass K x (ND4)1-x D2PO4: a complete x-ray diffraction line shape analysis

NASA Astrophysics Data System (ADS)

Ranjan Choudhury, Rajul; Chitra, R.; Jayakrishnan, V. B.

2016-03-01

Quenching of dynamic disorder in glassy systems is termed as the glass transition. Ferroic glasses belong to the class of paracrystalline materials having crystallographic order in-between that of a perfect crystal and amorphous material, a classic example of ferroic glass is the solid solution of ferroelectric deuterated potassium dihydrogen phosphate and antiferroelectric deuterated ammonium dihydrogen phosphate. Lowering temperature of this ferroic glass can lead to a glass transition to a quenched disordered state. The subtle atomic rearrangement that takes place at such a glass transition can be revealed by careful examination of the temperature induced changes occurring in the x-ray powder diffraction (XRD) patterns of these materials. Hence we report here results of a complete diffraction line shape analysis of the XRD patterns recorded at different temperatures from deuterated mixed crystals DK x A1-x DP with mixing concentration x ranging as 0 < x < 1. Changes observed in diffraction peak shapes have been explained on the basis of structural rearrangements induced by changing O-D-O hydrogen bond dynamics in these paracrystals.

Electronic polarizability, optical basicity and interaction parameter for Nd2O3 doped lithium-zinc-phosphate glasses

NASA Astrophysics Data System (ADS)

Algradee, M. A.; Sultan, M.; Samir, O. M.; Alwany, A. Elwhab B.

2017-08-01

The Nd3+-doped lithium-zinc-phosphate glasses were prepared by means of conventional melt quenching method. X-ray diffraction results confirmed the glassy nature of the studied glasses. The physical parameters such as the density, molar volume, ion concentration, polaron radius, inter-ionic distance, field strength and oxygen packing density were calculated using different formulae. The transmittance and reflectance spectra of glasses were recorded in the wavelength range 190-1200 nm. The values of optical band gap and Urbach energy were determined based on Mott-Davis model. The refractive indices for the studied glasses were evaluated from optical band gap values using different methods. The average electronic polarizability of the oxide ions, optical basicity and an interaction parameter were investigated from the calculated values of the refractive index and the optical band gap for the studied glasses. The variations in the different physical and optical properties of glasses with Nd2O3 content were discussed in terms of different parameters such as non-bridging oxygen and different concentrations of Nd cation in glass system.

Nd- And Er-Doped Phosphate Glass For Fiber Laser.

NASA Astrophysics Data System (ADS)

Yamashita, Toshiharu T.

1990-02-01

Laser fibers prepared from Nd- and Er-doped phosphate glass possessing a large stimulated emission cross section have been investigated both in a single fiber and in a fiber bundle. In the single fiber, continuous wave oscillations were successfully obtained at 1.054 p.m and 1.366 µm on a high Nd-doped single-mode fiber of 10 mm in length and also at 1.535 pm in a Er-doped single-mode fiber, sensitized by Nd, Yb. Especially, a low threshold of 1 mw and a high slope-efficiency of 50% were achieved in 1.054 pm laser oscillation on a Nd-doped fiber, end-pumped with a laser diode. A fiber bundle of phosphate glass doped with 8 wt% Nd2O3 yielded an average output power of 100 W at 50 pps where the bundle was 4.6 mm in diameter and was side-pumped with flash lamps.

Structural and spectroscopic characteristics of Eu3+-doped tungsten phosphate glasses

NASA Astrophysics Data System (ADS)

Dousti, M. Reza; Poirier, Gael Yves; de Camargo, Andrea Simone Stucchi

2015-07-01

Tungsten based phosphate glasses are interesting non-crystalline materials, commonly known for photochromic and electrochromic effects, but also promising hosts for luminescent trivalent rare earth ions. Despite very few reports in the literature, association of the host´s functionalities with the efficient emissions of the dopant ions in the visible and near-infrared spectra could lead to novel applications. This work reports the preparation and characterization of glasses with the new composition 4(Sb2O3)96-x(50WO3 50NaPO3)xEu2O3 where x = 0, 0.1, 0.25, 0.5 and 1.0 mol%, obtained by the melt quenching technique. The glasses present large density (∼4.6 g cm-3), high glass transition temperature (∼480 °C) and high thermal stability against crystallization. Upon excitation at 464 nm, the characteristic emissions of Eu3+ ions in the red spectral region are observed with high intensity. The Judd-Ofelt intensity parameters Ω2 = 6.86 × 10-20, Ω4 = 3.22 × 10-20 and Ω6 = 8.2 × 10-20 cm2 were calculated from the emission spectra and found to be higher than those reported for other phosphate glass compositions. An average excited state lifetime value of 1.2 ms, was determined by fitting the luminescence decay curves with single exponential functions and it is comparable or higher than those of other oxide glasses.

Fracture toughness and fractography of dental cements, lining, build-up, and filling materials.

PubMed

Mueller, H J

1990-06-01

The plane strain fracture toughness (K1c) at 23 degrees C and the fractography of zinc phosphate and zinc polycarboxylate cements, buffered glass ionomer liner, amalgam alloy admixed glass ionomer build-up material, and glass ionomer, microfilled and conventionally filled bis-GMA resin composite filling materials were analyzed by elastic-plastic short-rod and scanning electron microscopy methodologies. Results indicated that significant differences occurred in their K1c's from the lowest to the highest in the following groups of materials, (i) buffered glass ionomer, (ii) zinc phosphate, glass ionomer, zinc polycarboxylate, and alloy mixed glass ionomer, (iii) microfilled resin, and (iv) conventionally filled resin. All materials except the microfilled resin, which fractured via crack jumping, fractured via smooth crack advance. Filler debonding without any crack inhibiting process was related to materials with low K1c values. The incorporation of either buffering compounds or alloy particles into glass ionomer had no beneficial effect upon fracture toughness. This was in contrast to microfilled and conventionally filled resins where either crack blunting or crack pinning processes, respectively, were likely involved with their increased K1c's. For microfilled resin, distinct radial zones positioned around the chevron apex and characterized by plastically deformed deposited material were related to distinct crack jumps that occurred in the load versus displacement behavior. Finally, for the two remaining materials of zinc phosphate and polycarboxylate, particle cleavage and matrix debonding for the former and shear yielding for the latter occurred.

Silicon-Induced UV Transparency in Phosphate Glasses and Its Application to the Enhancement of the UV Type B Emission of Gd3.

PubMed

Jiménez, José A

2017-05-10

The silicon route to improve the ultraviolet (UV) transparency in phosphate glasses is investigated and further exploited to enhance the UV type B (280-320 nm) emission of gadolinium(III) relevant for biomedical applications. The glasses were synthesized with a barium phosphate composition by melt-quenching in ambient atmosphere and the optical properties investigated by optical absorption and photoluminescence (PL) spectroscopy including emission decay kinetics. An improvement in the UV transparency was gradually developed for the glasses melted merely with increasing amounts of Si powder. A particular PL in the visible was also exhibited for such glasses under excitation at 275 nm, consistent with the presence of Si-induced defects. For Si-Gd codoped glasses, the UV transparency was likewise manifested, while the UV emission from Gd 3+ around 312 nm was enhanced with the increase in Si concentration (up to ∼6.7 times). Moreover, along with the Gd 3+ PL intensity enhancement, a linear correlation was revealed between the increase in decay times for the Gd 3+6 P 7/2 -emitting state and the amount of silicon. It is then suggested that the improved PL properties of gadolinium(III) originate from the increased UV transparency of the host and the consequent precluding of a nonradiative energy transfer from Gd 3+ to the matrix. Accordingly, a role of Si as PL quenching inhibitor is supported. The demonstrated efficacy of the Si-Gd codoping concept realized by a facile glass synthesis procedure may appeal to the application of the UV-emitting glasses for phototherapy lamps.

Physical and absorption properties of titanium nanoparticles incorporated into zinc magnesium phosphate glass

DOE Office of Scientific and Technical Information (OSTI.GOV)

Ismail, S.F.; Sahar, M.R., E-mail: mrahim057@gmail.com; Ghoshal, S.K.

We report the influences of Titania (TiO{sub 2}) nanoparticles (NPs) on the physical and optical properties of melt quench synthesized zinc magnesium phosphate glasses. Five glass samples with composition (42 − x)P{sub 2}O{sub 5}–50ZnO–8MgO–xTiO{sub 2}, where x = 0, 1, 2, 3, 4 mol% are prepared and characterized. XRD pattern verified the amorphous nature of all samples. TEM images manifested the growth of Ti NPs of average size ≈ 5.78 nm. TiO{sub 2} NP concentration dependent variation in the physical properties including glass density, molar volume, molar refractivity, electronic polarizability and ionic packing density are determined. The values of glassmore » refractive indices, density and ionic packing density are increased with the increase of TiO{sub 2} NP contents. Conversely, the Urbach energy, direct and indirect optical band gap are found to decrease with the increase of TiO{sub 2} NP concentration. These glass compositions may be potential for various solid state devices including laser. - Highlights: • TiO{sub 2} NP embedded self-cleaning phosphate glass are synthesized for the first time. • Well dispersed and uniform sized TiO{sub 2} NPs are grown. • Absorption spectra revealed prominent peak in the UV region. • TiO{sub 2} NPs strongly influenced the physical and absorption features of synthesized glasses. • The effects of TiO{sub 2} NPs on the physical and optical properties of these glasses are determined.« less

Dental glass-reinforced composite for caries inhibition: Calcium phosphate ion release and mechanical properties

PubMed Central

Xu, Hockin H. K.; Moreau, Jennifer L.

2010-01-01

The two main challenges facing dental composite restorations are secondary caries and bulk fracture. Previous studies developed whisker-reinforced Ca-PO4 composites that were relatively opaque. The objective of this study was to develop an esthetic glass particle-reinforced, photo-cured calcium phosphate composite. Tetracalcium phosphate (TTCP) particles were incorporated into a resin for Ca and PO4 release, while glass particles provided reinforcement. Ion release and mechanical properties were measured after immersion in solutions with pH of 7, 5.5, and 4. For the composite containing 40% mass fraction of TTCP, incorporating glass fillers increased the strength (p < 0.05). Flexural strength (mean ± sd; n = 6) at 30% glass was (99 ± 18) MPa, higher than (54 ± 20) MPa at 0% glass (p < 0.05). Elastic modulus was 11 GPa at 30% glass, compared to 2 GPa without glass. At 28 d, the released Ca ion concentration was (4.61 ± 0.18) mmol/L at pH of 4, much higher than (1.14 ± 0.07) at pH of 5.5, and (0.27 ± 0.01) at pH of 7 (p < 0.05). PO4 release was also dramatically increased at cariogenic, acidic pH. The TTCP-glass composite had strength 2-3 fold that of a resin-modified glass ionomer control. In conclusion, the photo-cured TTCP-glass composite was “smart” and substantially increased the Ca and PO4 release when the pH was reduced from neutral to a cariogenic pH of 4, when these ions are most needed to inhibit tooth caries. Its mechanical properties were significantly higher than previous Ca, PO4 and fluoride releasing restoratives. Hence, the photo-cured TTCP-glass composite may have potential to provide the necessary combination of load-bearing and caries-inhibiting capabilities. PMID:19810118

XPS and 31P NMR inquiry of Eu3+-induced structural modification in SnO-containing phosphate glass

NASA Astrophysics Data System (ADS)

Jiménez, José A.; Fachini, Esteban Rosim; Zhao, Chunqing

2018-07-01

The influence of Eu3+ doping on the structural properties of SnO-containing phosphate glass has been investigated by X-ray photoelectron spectroscopy (XPS) and 31P nuclear magnetic resonance (NMR) spectroscopy. Oxygen 1s XPS data indicates that the Eu3+ doping results in a higher concentration of non-bridging oxygens in the glass matrix, whereas 31P NMR shows an increase in the terminal phosphate chain tetrahedral units, i.e. the amount of Q1 sites with only one bridging oxygen. Accordingly, both techniques agree with a depolymerization effect induced by the Eu3+ ions. Further, XPS reveals that together with the Eu3+ doping, the presence of Sn4+ is supported while the presence of Eu2+ is also indicated. The structural changes are then indicated to be a consequence of redox chemistry between Sn2+ and Eu3+ promoting a transition of tin from Sn2+ with a role as network former to Sn4+ acting as network modifier in the glass system.

The effects of crystallization and residual glass on the chemical durability of iron phosphate waste forms containing 40 wt% of a high MoO3 Collins-CLT waste

NASA Astrophysics Data System (ADS)

Hsu, Jen-Hsien; Bai, Jincheng; Kim, Cheol-Woon; Brow, Richard K.; Szabo, Joe; Zervos, Adam

2018-03-01

The effects of cooling rate on the chemical durability of iron phosphate waste forms containing up to 40 wt% of a high MoO3 Collins-CLT waste simulant were determined at 90 °C using the product consistency test (PCT). The waste form, designated 40wt%-5, meets appropriate Department of Energy (DOE) standards when rapidly quenched from the melt (as-cast) and after slow cooling following the CCC (canister centerline cooling)-protocol, although the quenched glass is more durable. The analysis of samples from the vapor hydration test (VHT) and the aqueous corrosion test (differential recession test) reveals that rare earth orthophosphate (monazite) and Zr-pyrophosphate crystals that form on cooling are more durable than the residual glass in the 40wt%-5 waste form. The residual glass in the CCC-treated samples has a greater average phosphate chain length and a lower Fe/P ratio, and those contribute to its faster corrosion kinetics.

The influence of different alkaline earth oxides on the structural and optical properties of undoped, Ce-doped, Sm-doped, and Sm/Ce co-doped lithium alumino-phosphate glasses

NASA Astrophysics Data System (ADS)

Othman, H. A.; Arzumanyan, G. M.; Möncke, D.

2016-12-01

Undoped, singly Sm doped, Ce doped, and Sm/Ce co-doped lithium alumino-phosphate glasses with different alkaline earth modifiers were prepared by melt quenching. The structure of the prepared glasses was investigated by FT-IR and Raman, as well as by optical spectroscopy. The effect of the optical basicity of the host glass matrix on the added active dopants was studied, as was the effect doping had on the phosphate structural units. The optical edge shifts toward higher wavelengths with an increase in the optical basicity due to the increased polarizability of the glass matrix, but also with increasing CeO2 concentration as a result of Ce3+/Ce4+ inter valence charge transfer (IV-CT) absorption. The optical band gap for direct and indirect allowed transitions was calculated for the undoped glasses. The glass sample containing Mg2+ modifier ions is found to have the highest value (4.16 eV) for the optical band gap while Ba2+ has the lowest value (3.61 eV). The change in the optical band gap arises from the structural changes and the overall polarizability (optical basicity). Refractive index, molar refractivity Rm and molar polarizability αm values increase with increasing optical basicity of the glasses. The characteristic absorption peaks of Sm3+ were also investigated. For Sm/Ce co-doped glasses, especially at high concentration of CeO2, the absorption of Ce3+ hinders the high energy absorption of Sm3+ and this effect becomes more obvious with increasing optical basicity.

Reaction of sodium calcium borate glasses to form hydroxyapatite.

PubMed

Han, Xue; Day, Delbert E

2007-09-01

This study investigated the transformation of two sodium calcium borate glasses to hydroxyapatite (HA). The chemical reaction was between either 1CaO . 2Na(2)O . 6B(2)O(3) or 2CaO . 2Na(2)O . 6B(2)O(3) glass and a 0.25 M phosphate (K(2)HPO(4)) solution at 37, 75 and 200 degrees C. Glass samples in the form of irregular particles (125-180 microm) and microspheres (45-90 and 125-180 microm) were used in order to understand the reaction mechanism. The effect of glass composition (calcium content) on the weight loss rate and reaction temperature on crystal size, crystallinity and grain shape of the reaction products were studied. Carbonated HA was made by dissolving an appropriate amount of carbonate (K(2)CO(3)) in the 0.25 M phosphate solution. X-ray diffraction, Fourier transform infrared spectroscopy, and scanning electron microscopy were used to characterize the reaction products. The results show that sodium calcium borate glasses can be transformed to HA by reacting with a phosphate solution. It is essentially a process of dissolution of glass and precipitation of HA. The transformation begins from an amorphous state to calcium-deficient HA without changing the size and shape of the original glass sample. Glass with a lower calcium content (1CaO . 2Na(2)O . 6B(2)O(3)), or reacted at an elevated temperature (75 degrees C), has a higher reaction rate. The HA crystal size increases and grain shape changes from spheroidal to cylindrical as temperature increases from 37 to 200 degrees C. Increase in carbonate concentration can also decrease the crystal size and yield a more needle-like grain shape.

Multiple rare-earth ion environments in amorphous ( G d 2 O 3 ) 0.230 ( P 2 O 5 ) 0.770 revealed by gadolinium K -edge anomalous x-ray scattering

DOE Office of Scientific and Technical Information (OSTI.GOV)

Cole, Jacqueline M.; Cramer, Alisha J.; Shastri, Sarvjit D.

A Gd K-edge anomalous X-ray scattering (AXS) study is performed on the rare-earth (R) phosphate glass, (Gd2O3)0.230(P2O5)0.770, in order to determine Gd…Gd separations in its local structure. The minimum rare-earth separation is of particular interest given that the optical properties of these glasses can quench when rare-earth ions become too close to each other. To this end, a weak Gd…Gd pairwise correlation is located at 4.2(1) Å which is representative of a meta-phosphate R…R separation. More intense first neighbor Gd…Gd pairwise correlations are found at the larger radial distributions, 4.8(1) Å, 5.1(1) Å and 5.4(1) Å. These reflect a mixedmore » ultra-phosphate and meta-phosphate structural character, respectively. A second neighbor Gd…Gd pairwise correlation lies at 6.6(1) Å which is indicative of meta-phosphate structures. Meta- and ultra-phosphate classifications are made by comparing the R…R separations against those of rare-earth phosphate crystal structures, R(PO3)3 and RP5O14 respectively, or difference pair distribution function (ΔPDF) features determined on similar glasses using difference neutron scattering methods. The local structure of this glass is therefore found to display multiple rare-earth ion environments, presumably because its composition lies between these two stoichiometric formulae. These Gd…Gd separations are well resolved in the ΔPDFs that represent the AXS signal. Indeed, the spatial resolution is so good that it also enables the identification of R…X (X = R, P, O) pairwise correlations up to r ~ 9 Å; their average separations lie at r ~ 7.1(1) Å, 7.6(1) Å 7.9(1) Å, 8.4(1) Å and 8.7(1) Å. This is the first report of a Gd K-edge AXS study on an amorphous material. Its demonstrated ability to characterize the local structure of a glass up to such a long-range of r, heralds exciting prospects for AXS studies on other ternary non-crystalline materials. However, the technical challenge of such an experiment should not be underestimated, as is highlighted in this work where probing AXS signal near the Gd K-edge is found to produce inelastic X-ray scattering that precludes the normal AXS methods of data processing. Nonetheless, it is shown that AXS results are not only tractable but they also reveal local structure of rare-earth phosphate glasses that is important from a materials-centered perspective and which could not be obtained by other materials characterization methods.« less

Radioluminescence and optical studies of gadolinium calcium phosphate oxyfluoride glasses doped with Sm3+

NASA Astrophysics Data System (ADS)

Meejitpaisan, P.; Insiripong, S.; Kedkaew, C.; Kim, H. J.; Kaewkhao, J.

2017-08-01

Sm3+-doped gadolinium calcium phosphate oxyfluoride glasses have been synthesized and investigated their optical, photo and radioluminescence properties. The glasses were prepared by melt quenching technique at 1400 °C. The characteristic absorption bands of Sm3+ ions originating from the 6H5/2 ground state and occurring absorbed photon in visible light (VIS) and near-infrared (NIR) region with clearly observed from absorption spectra. From the photoluminescence (PL), the glasses showed the emission at 561 (4G5/2→6H5/2), 598 (4G5/2→6H7/2), 644 (4G5/2→6H9/2) and 705 nm (4G5/2→6H11/2). The radioluminescence (RL), emission spectra were corresponding to those from PL measurements. From RL measurement, the integral scintillation efficiency of developed glass was determined at 43% when compared with BGO crystal.

Optical absorption spectra and energy band gap in manganese containing sodium zinc phosphate glasses

NASA Astrophysics Data System (ADS)

Sardarpasha, K. R.; Hanumantharaju, N.; Gowda, V. C. Veeranna

2018-05-01

Optical band gap energy in the system 25Na2O-(75-x)[0.6P2O5-0.4ZnO]-xMnO2 (where x = 0.5,1,5,10 and 20 mol.%) have been studied. The intensity of the absorption band found to increase with increase of MnO2 content. The decrease in the optical band gap energy with increase in MnO2 content in the investigated glasses is attributed to shifting of absorption edge to a longer wavelength region. The obtained results were discussed in view of the structure of phosphate glass network.

In vitro behaviour of three biocompatible glasses in composite implants.

PubMed

Varila, Leena; Lehtonen, Timo; Tuominen, Jukka; Hupa, Mikko; Hupa, Leena

2012-10-01

Poly(L,DL-lactide) composites containing filler particles of bioactive glasses 45S5 and S53P4 were compared with a composite containing a slowly dissolving glass S68. The in vitro reactivity of the composites was studied in simulated body fluid, Tris-buffered solution, and phosphate buffered saline. The high processing temperature induced thermal degradation giving cavities in the composites containing 45S5 and S53P4, while good adhesion of S68 to the polymer was observed. The cavities partly affected the in vitro reactivity of the composites. The degradation of the composites containing the bioactive glasses was faster in phosphate buffered saline than in the two other solutions. Hydroxyapatite precipitation suggesting bone tissue bonding capability was observed on these two composites in all three solutions. The slower dissolution of S68 glass particles and the limited hydroxyapatite precipitation suggested that this glass has potential as a reinforcing composition with the capability to guide bone tissue growth in biodegradable polymer composites.

Fluorescence properties of Yb3+-Er3+ co-doped phosphate glasses containing silver nanoparticles

NASA Astrophysics Data System (ADS)

Martínez Gámez, Ma A.; Vallejo H, Miguel A.; Kiryanov, A. V.; Licea-Jiménez, L.; Lucio M, J. L.; Pérez-García, S. A.

2018-04-01

Er3+-Yb3+ co-doped phosphate glasses containing silver nitrate (SN), were fabricated. Transmission electron microscopy (TEM) and x-ray photoelectron spectroscopy (XPS) analyses were used to evidence the nucleation and presence of silver nanoparticles (SNP). The basic parameters of the glasses were inspected by means of absorption and fluorescence spectra, and fluorescence lifetimes under excitation at 916 nm (in-band of Yb3+), and at 406 nm (in-band of surface plasmon resonance given by the presence of SNP). The spectra as well as estimates for the basic parameters defining the lasing/amplifying potential of the glasses were studied as a function of SN concentration. The experimental results indicate that by increasing the SN content an enhancement of Er3+/Yb3+ fluorescence takes place.

Investigation of Refractive Index Profile Induced with Femtosecond Pulses into Neodymium Doped Phosphate Glass for the Purposes of Hybrid Waveguiding Structures Formation

NASA Astrophysics Data System (ADS)

Bukharin, M.; Khudakov, D.; Vartapetov, S.

The technique of writing depressed cladding waveguides into Nd:phosphate glass with relatively large mode field diameter in 2-line geometry was reported for the purposes of waveguiding structures formation. The easy to use and accurate technique of induced refractive index measurement was proposed, and it was shown the inefficiency of widespread indirect (numerical aperture) technique of refractive index measurement for such femtosecond written waveguides.

Effect of lead fluoride incorporation on the structure and luminescence properties of tungsten sodium phosphate glasses

NASA Astrophysics Data System (ADS)

Nardi, Rachel Prado Russo Delorenzo; Braz, Celso Eduardo; de Camargo, Andrea S. S.; Ribeiro, Sidney J. L.; Rocha, Lucas A.; Cassanjes, Fábia Castro; Poirier, Gael

2015-11-01

Tungsten phosphate glasses are known to be promising materials for several applications in optics such as non linear optical properties, lower phonon energy or photochromic effects related with tungsten oxide incorporation inside the phosphate network. In this study, lead fluoride has been incorporated in a 60NaPO3-40WO3 glass composition according to the ternary molar compositions (100 - x)[0.6NaPO3-0.4WO3]-xPbF2 with x varying from 0 to 60 mol%. The structural changes as a function of composition were investigated by thermal analysis, UV-visible absorption, Raman spectroscopy, X-ray diffraction of the crystallized samples, and Eu3+ emission in the visible. While DSC analyzes points out a strong decrease in the glass network connectivity and higher crystallization tendency with increasing PbF2 contents, Raman spectra clearly identify a progressive incorporation of PbF2 in the phosphate network with the formation of terminal Psbnd F and Wsbnd F bonds. These results are also in agreement with the crystallization of β-PbF2 observed for the most lead fluoride concentrated samples. Investigation of Eu3+ emission data in the visible showed longer 5D0 excited state lifetime values and higher quantum efficiencies. These results are discussed in terms of the assumption of higher local symmetry around Eu3+ with increasing PbF2 contents.

Structural and optical properties of CuO in zinc phosphate glasses and effects of gamma irradiation

NASA Astrophysics Data System (ADS)

Ouis, M. A.; ElBatal, H. A.; Abdelghany, A. M.; Hammad, Ahmed H.

2016-01-01

Collective optical and infrared measurements have been employed to investigate the state of increasing copper ions in host 0.5ZnO-0.5P2O5 glass composition. The same spectral measurements were repeated after gamma irradiation with a dose of 20 and 80 KGy. Optical absorption spectra reveal strong UV absorption due to trace ferric ions present as unavoidable impurities within the chemicals used in the preparation of the glasses. Copper containing glasses show an additional broad visible-near infrared band due to distorted octahedrally coordinated Cu2+ ions which at high CuO contents exhibit splitting to several component absorption peaks. Gamma irradiation causes several variations between the response of the base host zinc phosphate glass and effect of increasing CuO. These changes are correlated with both the formation of induced defects through suggested photochemical reactions in the UV region and some shielding effects with increasing CuO in the visible-near infrared spectrum. Infrared absorption spectra reveal repetitive vibrational bands due to phosphate groups mainly from metaphosphate units and the spectra show some variations with the increase of CuO content visualize by the increase of the intensity of the mid broad band extending in the range 800-1500 cm-1.

Use of Raman microscopy and multivariate data analysis to observe the biomimetic growth of carbonated hydroxyapatite on bioactive glass.

PubMed

Seah, Regina K H; Garland, Marc; Loo, Joachim S C; Widjaja, Effendi

2009-02-15

In the present contribution, the biomimetic growth of carbonated hydroxyapatite (HA) on bioactive glass were investigated by Raman microscopy. Bioactive glass samples were immersed in simulated body fluid (SBF) buffered solution at pH 7.40 up to 17 days at 37 degrees C. Raman microscopy mapping was performed on the bioglass samples immersed in SBF solution for different periods of time. The collected data was then analyzed using the band-target entropy minimization technique to extract the observable pure component Raman spectral information. In this study, the pure component Raman spectra of the precursor amorphous calcium phosphate, transient octacalcium phosphate, and matured HA were all recovered. In addition, pure component Raman spectra of calcite, silica glass, and some organic impurities were also recovered. The resolved pure component spectra were fit to the normalized measured Raman data to provide the spatial distribution of these species on the sample surfaces. The current results show that Raman microscopy and multivariate data analysis provide a sensitive and accurate tool to characterize the surface morphology, as well as to give more specific information on the chemical species present and the phase transformation of phosphate species during the formation of HA on bioactive glass.

P2O5-doping in waste glasses: evolution of viscosity and crystallization processes

NASA Astrophysics Data System (ADS)

Tarrago, Mariona; Espuñes, Alex; Garcia-Valles, Maite; Martinez, Salvador

2015-04-01

Current concern for environmental preservation is the main motive for the study of new, more sustainable materials. Increasing amounts of sewage sludge are produced in wastewater treatment plants over the world every day. This fact represents a major problem for the municipalities and industries due to the volume of waste and also to the contaminant elements it may bear, which require expensive conditions for disposal in landfills. Vitrification is an established technique in the inertization of different types of toxic wastes (such as nuclear wastes and contaminated soils) that has been used successfully for sewage sludge. Glasses of basaltic composition (43.48SiO2-14.00Al2O3-12.86Fe2O3-10.00CaO-9.94MgO-3.27Na2O-1.96K2O-0.17MnO-0.55P2O5-2.48TiO2) are used as a laboratory analogous of wastes such as sewage sludge and galvanic sludge to study the properties of the inertization matrix. This basaltic matrix is doped by adding 1%, 2%, 3%, 4% and 20% of P5O5 in order to cover the compositional range of phosphate in sewage sludge encountered in the literature. In this study, the focus has been placed in the effect of the concentration of phosphate (P2O5) in glass stability, thermal properties and evolution of viscosity with temperature. The dependence of viscosity on temperature and the thermal behaviour of these glasses are critical parameters in the design of their production process. Regarding the compositional limits of the mixture, it has been observed that melt reactivity is much increased when P2O5 content is over 4%, hindering the glass conformation process. Moreover, stanfieldite (calcium and magnesium phosphate) crystallized during glass making when phosphate concentration approached 20%, hence establishing the upper limit for glass stability. Viscosity is also dramatically increased in this range, hence requiring production amends. Differential thermal analysis has provided nucleation and crystallization temperatures of the glasses around 915°C and 1050°C respectively at phosphate contents up to 4%. Subsequent analysis by X-Ray Diffraction has proved that newly formed phases are iron oxides, Ca - Mg silicates and feldspars. Glass transition temperature (Tg; approximately 635°C) obtained by dilatometry remains almost constant until very high phosphate contents; even then, the increase is not large (650°C at 20% P2O5). Hot-Stage microscopy (HSM) has shown the evolution of viscosity with temperature through the analysis of the morphological evolution of cylindrical probes of glass according to German standard DIN 51730. The annealing range (viscosity between 1013.5 and 1012 is reached at temperatures between 600 and 700°C. The temperatures of the lower limit of the working range (viscosity under 103 Pa-s) are between 1325 and 1375°C; decreasing slightly with the addition of P2O5.

Influence of F- on stark splitting of Yb3+ and the thermal expansion of silica glass

NASA Astrophysics Data System (ADS)

Cao, Yabin; Chen, Si; Shao, Chongyun; Yu, Chunlei

2018-06-01

A local phosphate/fluoride environment of Yb3+ was created in silica glass using a multi-step method. The influence of F- on the Stark splitting of Yb3+ in Al3+/P5+/F- co-doped silica glass was studied at room-temperature, in addition to its effect on the thermal expansion performance of the glass matrix. The results indicate that Yb3+ ions in Al3+/P5+/F- co-doped silica glass have a larger Stark splitting energy of 2F7/2 compared to Al3+/P5+ co-doped silica glass. Moreover, a larger integrated absorption cross-section (34.58 pm2 × nm), stimulated emission cross-section (0.63 pm2), and better thermal expansion performance (1.3062 × 10-6 K- at 100 °C) are achieved in Al3+/P5+/F- co-doped silica glass. Finally, different function mechanisms of F- in silica and phosphate glasses were analyzed and the F-Si bond was used to explain the results in silica glass. The combination of low refractive index, large Stark splitting energy of 2F7/2, and small thermal expansion makes Al3+/P5+/F- co-doped silica glass a preferred material for large mode area fibers for high-power laser applications.

Effect of boron oxide addition on fibre drawing, mechanical properties and dissolution behaviour of phosphate-based glass fibres with fixed 40, 45 and 50 mol% P2O5

PubMed Central

Sharmin, Nusrat; Parsons, Andrew J; Rudd, Chris D

2014-01-01

Previous studies investigating manufacture of phosphate-based glass fibres from glasses fixed with P2O5 content less than 50 mol% showed that continuous manufacture without breakage was very difficult. In this study, nine phosphate-based glass formulations from the system P2O5-CaO-Na2O-MgO-B2O3 were prepared with P2O5 contents fixed at 40, 45 and 50 mol%, where Na2O was replaced by 5 and 10 mol% B2O3 and MgO and CaO were fixed to 24 and 16 mol%, respectively. The effect of B2O3 addition on the fibre drawing, fibre mechanical properties and dissolution behaviour was investigated. It was found that addition of 5 and 10 mol% B2O3 enabled successful drawing of continuous fibres from glasses with phosphate (P2O5) contents fixed at 40, 45 and 50 mol%. The mechanical properties of the fibres were found to significantly increase with increasing B2O3 content. The highest tensile strength (1200 ± 130 MPa) was recorded for 45P2O5-16CaO-5Na2O-24MgO-10B2O3 glass fibres. The fibres were annealed, and a comparison of the mechanical properties and mode of degradation of annealed and non-annealed fibres were investigated. A decrease in tensile strength and an increase in tensile modulus were observed for the annealed fibres. An assessment of the change in mechanical properties of both the annealed and non-annealed fibres was performed in phosphate-buffered saline (PBS) at 37℃ for 28 and 60 days, respectively. Initial loss of mechanical properties due to annealing was found to be recovered with degradation. The B2O3-containing glass fibres were found to degrade at a much slower rate as compared to the non-B2O3-containing fibres. Both annealed and non-annealed fibres exhibited a peeling effect of the fibre's outer layer during degradation. PMID:24939962

Effect of boron oxide addition on fibre drawing, mechanical properties and dissolution behaviour of phosphate-based glass fibres with fixed 40, 45 and 50 mol% P2O5.

PubMed

Sharmin, Nusrat; Parsons, Andrew J; Rudd, Chris D; Ahmed, Ifty

2014-11-01

Previous studies investigating manufacture of phosphate-based glass fibres from glasses fixed with P2O5 content less than 50 mol% showed that continuous manufacture without breakage was very difficult. In this study, nine phosphate-based glass formulations from the system P2O5-CaO-Na2O-MgO-B2O3 were prepared with P2O5 contents fixed at 40, 45 and 50 mol%, where Na2O was replaced by 5 and 10 mol% B2O3 and MgO and CaO were fixed to 24 and 16 mol%, respectively. The effect of B2O3 addition on the fibre drawing, fibre mechanical properties and dissolution behaviour was investigated. It was found that addition of 5 and 10 mol% B2O3 enabled successful drawing of continuous fibres from glasses with phosphate (P2O5) contents fixed at 40, 45 and 50 mol%. The mechanical properties of the fibres were found to significantly increase with increasing B2O3 content. The highest tensile strength (1200 ± 130 MPa) was recorded for 45P2O5-16CaO-5Na2O-24MgO-10B2O3 glass fibres. The fibres were annealed, and a comparison of the mechanical properties and mode of degradation of annealed and non-annealed fibres were investigated. A decrease in tensile strength and an increase in tensile modulus were observed for the annealed fibres. An assessment of the change in mechanical properties of both the annealed and non-annealed fibres was performed in phosphate-buffered saline (PBS) at 37℃ for 28 and 60 days, respectively. Initial loss of mechanical properties due to annealing was found to be recovered with degradation. The B2O3-containing glass fibres were found to degrade at a much slower rate as compared to the non-B2O3-containing fibres. Both annealed and non-annealed fibres exhibited a peeling effect of the fibre's outer layer during degradation. © The Author(s) 2014 Reprints and permissions: sagepub.co.uk/journalsPermissions.nav.

Fragility and glass transition for binary mixtures of 1,2-propanediol and LiBF4

NASA Astrophysics Data System (ADS)

Terashima, Y.; Mori, M.; Sugimoto, N.; Takeda, K.

2014-04-01

The fragility and glass transition for binary mixtures of 1,2-propanediol and LiBF4 were investigated by measuring the heating rate dependence of glass transition temperature (Tg) using differential scanning calorimetry. With increasing LiBF4 mole fraction, x, up to 0.25, fragility, m, increased rapidly from 53 to 85, and then remained approximately unchanged for x > 0.25. The concentration dependences of Tg and heat capacity jump at Tg also showed anomalies around x = 0.25. We suggest this mixture transformed from a moderate to quite fragile liquid at x = 0.25 because of a structural change from a hydrogen-bonding- to ionic-interaction-dominant system.

Mechanical, degradation and cytocompatibility properties of magnesium coated phosphate glass fibre reinforced polycaprolactone composites.

PubMed

Liu, Xiaoling; Hasan, Muhammad S; Grant, David M; Harper, Lee T; Parsons, Andrew J; Palmer, Graham; Rudd, Chris D; Ahmed, Ifty

2014-11-01

Retention of mechanical properties of phosphate glass fibre reinforced degradable polyesters such as polycaprolactone and polylactic acid in aqueous media has been shown to be strongly influenced by the integrity of the fibre/polymer interface. A previous study utilising 'single fibre' fragmentation tests found that coating with magnesium improved the fibre and matrix interfacial shear strength. Therefore, the aim of this study was to investigate the effects of a magnesium coating on the manufacture and characterisation of a random chopped fibre reinforced polycaprolactone composite. Short chopped strand non-woven phosphate glass fibre mats were sputter coated with degradable magnesium to manufacture phosphate glass fibre/polycaprolactone composites. The degradation behaviour (water uptake, mass loss and pH change of the media) of these polycaprolactone composites as well as of pure polycaprolactone was investigated in phosphate buffered saline. The Mg coated fibre reinforced composites revealed less water uptake and mass loss during degradation compared to the non-coated composites. The cations released were also explored and a lower ion release profile for all three cations investigated (namely Na(+), Mg(2+) and Ca(2+)) was seen for the Mg coated composite samples. An increase of 17% in tensile strength and 47% in tensile modulus was obtained for the Mg coated composite samples. Both flexural and tensile properties were investigated and a higher retention of mechanical properties was obtained for the Mg coated fibre reinforced composite samples up to 10 days immersion in PBS. Cytocompatibility study showed both composite samples (coated and non-coated) had good cytocompatibility with human osteosarcoma cell line. © The Author(s) 2014 Reprints and permissions: sagepub.co.uk/journalsPermissions.nav.

Investigations on the effects of the Stark splitting on the fluorescence behaviors in Yb3+-doped silicate, tellurite, germanate, and phosphate glasses

NASA Astrophysics Data System (ADS)

Zhang, Liaolin; Xia, Yu; Shen, Xiao; Yang, Runlan; Wei, Wei

2018-01-01

In this work, we systematically studied the spectroscopic characteristics of Yb3+ doped germanate, phosphate, silicate, and tellurite glasses. The emission peak beyond 976 nm showed irregular shift from 1001 nm to 1023 nm when Yb3+ in different glass matrices. It was associated with the Stark splitting of 2F7/2 and the emission intensities ratio between the transition from the lowest Stark splitting energy level of 2F5/2 to the Stark splitting energy levels of 2F7/2, e to b and that of e to d. Larger Stark splitting of 2F7/2 results in the red-shift of the near infrared emission band at room temperature and larger ratio results in the blue-shift of emission band. The fluorescence lifetimes of Yb3+ doped germanate, phosphate, silicate, and tellurite glasses were measured to be 0.94, 0.82, 1.51, and 0.66 ms, respectively. The fluorescence lifetime was associated with the reabsorption of Yb3+, which larger absorption cross section at the emission band results in larger reabsorption, then leads to the shorter near infrared fluorescence lifetime.

Optical evaluation on Nd3+-doped phosphate glasses for O-band amplification.

PubMed

Lei, Weihong; Chen, Baojie; Zhang, Xiangling; Pun, Edwin Yun Bun; Lin, Hai

2011-02-20

We have fabricated and characterized optically Nd3+-doped phosphate [Li2O-CaO-BaO-Al2O3-La2O3-P2O5 (LCBALP)] glasses for drawing single-mode glass fiber. The 4F3/2→4I13/2 transition emission from the Nd3+ is at the 1.327 μm wavelength with a full width at half-maximum of 43 nm, and the spontaneous transition probability and quantum efficiency are calculated to be 1836 s-1 and 52%, respectively. The maximum stimulated emission cross sections for 4F3/2→4I11/2 and 4F3/2→4I13/2 transitions are derived to be 1.82×10(-20) cm2 and 6.97×10(-21) cm2, respectively, and the theoretical gain coefficient at the 1.327 μm wavelength is evaluated to be 0.182 dB/cm when the fractional factor of the excited neodymium ions equals 0.6, which indicates that Nd3+-doped LCBALP phosphate glasses are potential candidates in developing O-band optical fiber amplifiers.

Biodegradable ceramic-polymer composites for biomedical applications: A review.

PubMed

Dziadek, Michal; Stodolak-Zych, Ewa; Cholewa-Kowalska, Katarzyna

2017-02-01

The present work focuses on the state-of-the-art of biodegradable ceramic-polymer composites with particular emphasis on influence of various types of ceramic fillers on properties of the composites. First, the general needs to create composite materials for medical applications are briefly introduced. Second, various types of polymeric materials used as matrices of ceramic-containing composites and their properties are reviewed. Third, silica nanocomposites and their material as well as biological characteristics are presented. Fourth, different types of glass fillers including silicate, borate and phosphate glasses and their effect on a number of properties of the composites are described. Fifth, wollastonite as a composite modifier and its effect on composite characteristics are discussed. Sixth, composites containing calcium phosphate ceramics, namely hydroxyapatite, tricalcium phosphate and biphasic calcium phosphate are presented. Finally, general possibilities for control of properties of composite materials are highlighted. Copyright © 2016 Elsevier B.V. All rights reserved.

Random gauge models of the superconductor-insulator transition in two-dimensional disordered superconductors

NASA Astrophysics Data System (ADS)

Granato, Enzo

2017-11-01

We study numerically the superconductor-insulator transition in two-dimensional inhomogeneous superconductors with gauge disorder, described by four different quantum rotor models: a gauge glass, a flux glass, a binary phase glass, and a Gaussian phase glass. The first two models describe the combined effect of geometrical disorder in the array of local superconducting islands and a uniform external magnetic field, while the last two describe the effects of random negative Josephson-junction couplings or π junctions. Monte Carlo simulations in the path-integral representation of the models are used to determine the critical exponents and the universal conductivity at the quantum phase transition. The gauge- and flux-glass models display the same critical behavior, within the estimated numerical uncertainties. Similar agreement is found for the binary and Gaussian phase-glass models. Despite the different symmetries and disorder correlations, we find that the universal conductivity of these models is approximately the same. In particular, the ratio of this value to that of the pure model agrees with recent experiments on nanohole thin-film superconductors in a magnetic field, in the large disorder limit.

Alkali-resistant calcium iron phosphate glass fibers for concrete reinforcement

DOT National Transportation Integrated Search

2008-02-01

The physical properties and alkaline corrosion resistant properties of calcium-ironphosphate glasses were studied. Iron addition decreases the thermal expansion coefficient and increases the Youngs modulus in comparison with the addition of calciu...

Physical and optical properties of calcium sulfate ultra-phosphate glass-doped Er2O3

NASA Astrophysics Data System (ADS)

Aliyu, Aliyu Mohammed; Hussin, R.; Deraman, Karim; Ahmad, N. E.; Danmadami, Amina M.; Yamusa, Y. A.

2018-03-01

The influence of erbium on physical and optical properties of calcium sulfate ultra-phosphate glass was investigated using conventional melt quench process. Selected samples of composition 20CaSO4 (80 - x) P2O5- xEr2O3 with 0.1 ≤x ≤ 0.9 mol.% were prepared and assessed. X-ray diffraction (XRD) techniques were used to confirm the amorphous nature of the said samples. The structural units of phosphate-based glass were assessed from Raman spectra as ultra-(Q3), meta-(Q2), pyro-(Q1) and orthophosphate (Q0) units. Depolymerization process of the glasses was testified for higher calcium oxide content and UV-visible for optical measurement. Thermal analysis have been investigated by means of thermogravimetric analysis. The results show the decomposition of materials in the temperature range of 25∘C-1000∘C. Er3+ absorption spectra were measured in the range of 400-1800nm. PL measurement was carried out in order to obtain the excitation and emission spectra of the samples. The emission spectra excited at 779nm comprises of 518nm, 550nm and 649nm of transition 4F9/2, 4S3/2 and 2H11/2 excited states to 4I15/2 ground state. In physical properties, the density calculated using Archimedes method is inversely proportional to molar volume with increase in Er3+ ions. Optical bandgap (Eg) were determined using Tauc’s plots for direct transitions where Eg (direct) decreases with increase in erbium content. The refractive index increases with decreasing molar volume; this may have a tendency for larger optical bandgap. The result obtained from the glass matrix indicates that erbium oxide-doped calcium sulfate ultra-phosphate may give important information for wider development of functional glasses.

In situ fabrication of hollow hydroxyapatite microspheres by phosphate solution immersion

NASA Astrophysics Data System (ADS)

Wang, Yingchun; Yao, Aihua; Huang, Wenhai; Wang, Deping; zhou, Jun

2011-07-01

Hollow hydroxyapatite (HAP) microspheres with pores on their surfaces were prepared by converting Li 2O-CaO-B 2O 3 (LCB) glass microspheres in phosphate solution. The structure, phase composition, surface morphology, and porosity of the hollow HAP microspheres were characterized by SEM, SEM-EDS, XRD, FTIR, ICP-AES, and N 2 adsorption-desorption techniques. The formation and conversion mechanism of the hollow HAP microspheres during immersion process were discussed. The as-prepared microspheres consisted of calcium deficient carbonated hydroxyapatite, which is biomimetic. FTIR spectra indicated that the resulting apatite were B-type CO 3HAP, in which carbonate ions occupied the phosphate sites. After 600 °C heating treatment, hollow microspheres were completely composed of calcium deficient hydroxyapatite crystals including CO32-. The pore size distribution of the as-prepared hollow HAP microspheres were mainly the mesopores in the range of 2-40 nm with the pore volume 0.5614 cm 3/g, and the mean pore size 10.5 nm, respectively. The results confirmed that LCB glass were transformed to hydroxyapatite without changing the external shape and dimension of the original glass object and the resulting microspheres possessed good hollow structures. Once immersed in phosphate solution, Ca-P-OH hydrates were in situ formed on the surface of the glass and precipitated in the position occupied by Ca 2+, while the pores were formed in the position occupied by Li + and B 3+. These hollow HAP microspheres with such structures may be used as promising drug delivery devices.

An advanced NMR protocol for the structural characterization of aluminophosphate glasses.

PubMed

van Wüllen, Leo; Tricot, Grégory; Wegner, Sebastian

2007-10-01

In this work a combination of complementary advanced solid-state nuclear magnetic resonance (NMR) strategies is employed to analyse the network organization in aluminophosphate glasses to an unprecedented level of detailed insight. The combined results from MAS, MQMAS and (31)P-{(27)Al}-CP-heteronuclear correlation spectroscopy (HETCOR) NMR experiments allow for a detailed speciation of the different phosphate and aluminate species present in the glass. The interconnection of these local building units to an extended three-dimensional network is explored employing heteronuclear dipolar and scalar NMR approaches to quantify P-O-Al connectivity by (31)P{(27)Al}-heteronuclear multiple quantum coherence (HMQC), -rotational echo adiabatic passage double resonance (REAPDOR) and -HETCOR NMR as well as (27)Al{(31)P}-rotational echo double resonance (REDOR) NMR experiments, complemented by (31)P-2D-J-RESolved MAS NMR experiments to probe P-O-P connectivity utilizing the through bond scalar J-coupling. The combination of the results from the various NMR approaches enables us to not only quantify the phosphate units present in the glass but also to identify their respective structural environments within the three-dimensional network on a medium length scale employing a modified Q notation, Q(n)(m),(AlO)(x), where n denotes the number of connected tetrahedral phosphate, m gives the number of aluminate species connected to a central phosphate unit and x specifies the nature of the bonded aluminate species (i.e. 4, 5 or 6 coordinate aluminium).

Ytterbium-Phosphate Glass for Microstructured Fiber Laser

PubMed Central

Stępień, Ryszard; Franczyk, Marcin; Pysz, Dariusz; Kujawa, Ireneusz; Klimczak, Mariusz; Buczyński, Ryszard

2014-01-01

In the paper, we report on the development of a synthesis and melting method of phosphate glasses designed for active microstructured fiber manufacturing. Non-doped glass synthesized in a P2O5-Al2O3-BaO-ZnO-MgO-Na2O oxide system served as the matrix material; meanwhile, the glass was doped with 6 mol% (18 wt%) of Yb2O3, as fiber core. The glasses were well-fitted in relation to optical (refractive index) and thermal proprieties (thermal expansion coefficient, rheology). The fiber with the Yb3+-doped core, with a wide internal photonic microstructure for a laser pump, as well as with a high relative hole size in the photonic outer air-cladding, was produced. The laser built on the basis of this fiber enabled achieving 8.07 W of output power with 20.5% slope efficiency against the launched pump power, in single-mode operation M2 = 1.59, from a 53 cm-long cavity. PMID:28788702

The role of troublesome components in plutonium vitrification

DOE Office of Scientific and Technical Information (OSTI.GOV)

Li, Hong; Vienna, J.D.; Peeler, D.K.

1996-05-01

One option for immobilizing surplus plutonium is vitrification in a borosilicate glass. Two advantages of the glass form are (1) high tolerance to feed variability and, (2) high solubility of some impurity components. The types of plutonium-containing materials in the United States inventory include: pits, metals, oxides, residues, scrap, compounds, and fuel. Many of them also contain high concentrations of carbon, chloride, fluoride, phosphate, sulfate, and chromium oxide. To vitrify plutonium-containing scrap and residues, it is critical to understand the impact of each component on glass processing and chemical durability of the final product. This paper addresses glass processing issuesmore » associated with these troublesome components. It covers solubility limits of chlorine, fluorine, phosphate, sulfate, and chromium oxide in several borosilicate based glasses, and the effect of each component on vitrification (volatility, phase segregation, crystallization, and melt viscosity). Techniques (formulation, pretreatment, removal, and/or dilution) to mitigate the effect of these troublesome components are suggested.« less

Preparation and properties of porous microspheres made from borate glass.

PubMed

Conzone, Samuel D; Day, Delbert E

2009-02-01

Dysprosium lithium-borate glass microspheres and particles, ranging from 45 to 150 microm in diameter, were reacted with a 0.25 M phosphate solution at 37 degrees C, whose pH was either 3 or 8.8. The glass reacted nonuniformly and was converted into a porous, amorphous, hydrated, dysprosium phosphate reaction product. The amorphous product had the same volume and shape (pseudomorphic) as the unreacted glass, and could be dried without cracking. After heating at 300 degrees C for 1 h, the amorphous reaction product had a specific surface area of approximately 200 m(2)/g, a pore size of approximately 30 nm, and nominal crushing strength of approximately 10 MPa. When the reaction product was heated to 600 degrees C for 15 min, the specific surface area decreased to approximately 90 m(2)/g and the nominal crushing strength increased to 35 MPa. Heating above 615 degrees C converted the amorphous dysprosium phosphate product into crystalline DyPO(4), which contained open porosity until heated above 800 degrees C for 15 min. Highly porous materials of different chemical composition can be prepared by chemically reacting a borate-based glass with an aqueous solution at low-temperature (<100 degrees C). These highly porous materials are easy to process, and are considered candidates for controlled drug delivery, catalysis, chromatographic separation, filtration, and as bioactive materials.

Phosphorus doping a semiconductor particle

DOEpatents

Stevens, G.D.; Reynolds, J.S.

1999-07-20

A method of phosphorus doping a semiconductor particle using ammonium phosphate is disclosed. A p-doped silicon sphere is mixed with a diluted solution of ammonium phosphate having a predetermined concentration. These spheres are dried with the phosphorus then being diffused into the sphere to create either a shallow or deep p-n junction. A good PSG glass layer is formed on the surface of the sphere during the diffusion process. A subsequent segregation anneal process is utilized to strip metal impurities from near the p-n junction into the glass layer. A subsequent HF strip procedure is then utilized to removed the PSG layer. Ammonium phosphate is not a restricted chemical, is inexpensive, and does not pose any special shipping, handling, or disposal requirement. 1 fig.

Phosphorous doping a semiconductor particle

DOEpatents

Stevens, Gary Don; Reynolds, Jeffrey Scott

1999-07-20

A method (10) of phosphorus doping a semiconductor particle using ammonium phosphate. A p-doped silicon sphere is mixed with a diluted solution of ammonium phosphate having a predetermined concentration. These spheres are dried (16, 18), with the phosphorus then being diffused (20) into the sphere to create either a shallow or deep p-n junction. A good PSG glass layer is formed on the surface of the sphere during the diffusion process. A subsequent segregation anneal process is utilized to strip metal impurities from near the p-n junction into the glass layer. A subsequent HF strip procedure is then utilized to removed the PSG layer. Ammonium phosphate is not a restricted chemical, is inexpensive, and does not pose any special shipping, handling, or disposal requirement.

FTIR spectra and properties of iron borophosphate glasses containing simulated nuclear wastes

NASA Astrophysics Data System (ADS)

Liao, Qilong; Wang, Fu; Chen, Kuiru; Pan, Sheqi; Zhu, Hanzhen; Lu, Mingwei; Qin, Jianfa

2015-07-01

30 wt.% simulated nuclear wastes were successfully immobilized by B2O3-doped iron phosphate base glasses. The structure and thermal stability of the prepared wasteforms were characterized by Fourier transform infrared spectroscopy and differential thermal analysis, respectively. The subtle structural variations attributed to different B2O3 doping modes have been discussed in detail. The results show that the thermal stability and glass forming tendency of the iron borophosphate glass wasteforms are faintly affected by different B2O3 doping modes. The main structural networks of iron borophosphate glass wasteforms are PO43-, P2O74-, [BO4] groups. Furthermore, for the wasteform prepared by using 10B2O3-36Fe2O3-54P2O5 as base glass, the distributions of Fe-O-P bonds, [BO4], PO43- and P2O74- groups are optimal. In general, the dissolution rate (DR) values of the studied iron borophosphate wasteforms are about 10-8 g cm-2 min-1. The obtained conclusions can offer some useful information for the disposal of high-level radioactive wastes using boron contained phosphate glasses.

Phosphate-based glass fiber vs. bulk glass: Change in fiber optical response to probe in vitro glass reactivity.

PubMed

Massera, J; Ahmed, I; Petit, L; Aallos, V; Hupa, L

2014-04-01

This paper investigates the effect of fiber drawing on the thermal and structural properties as well as on the glass reactivity of a phosphate glass in tris(hydroxymethyl)aminomethane-buffered (TRIS) solution and simulated body fluid (SBF). The changes induced in the thermal properties suggest that the fiber drawing process leads to a weakening and probable re-orientation of the POP bonds. Whereas the fiber drawing did not significantly impact the release of P and Ca, an increase in the release of Na into the solution was noticed. This was probably due to small structural reorientations occurring during the fiber drawing process and to a slight diffusion of Na to the fiber surface. Both the powders from the bulk and the glass fibers formed a Ca-P surface layer when immersed in SBF and TRIS. The layer thickness was higher in the calcium and phosphate supersaturated SBF than in TRIS. This paper for the first time presents the in vitro reactivity and optical response of a phosphate-based bioactive glass (PBG) fiber when immersed in SBF. The light intensity remained constant for the first 48h after which a decrease with three distinct slopes was observed: the first decrease between 48 and 200h of immersion could be correlated to the formation of the Ca-P layer at the fiber surface. After this a faster decrease in light transmission was observed from 200 to ~425h in SBF. SEM analysis suggested that after 200h, the surface of the fiber was fully covered by a thin Ca-P layer which is likely to scatter light. For immersion times longer than ~425h, the thickness of the Ca-P layer increased and thus acted as a barrier to the dissolution process limiting further reduction in light transmission. The tracking of light transmission through the PBG fiber allowed monitoring of the fiber dissolution in vitro. These results are essential in developing new bioactive fiber sensors that can be used to monitor bioresponse in situ. Copyright © 2014 Elsevier B.V. All rights reserved.

Kinetics of copper nanoparticle precipitation in phosphate glass: an isothermal plasmonic approach.

PubMed

Sendova, Mariana; Jiménez, José A; Smith, Robert; Rudawski, Nicholas

2015-01-14

The kinetics of copper nanoparticle (NP) precipitation in melt-quenched barium-phosphate glass has been studied by in situ isothermal optical micro-spectroscopy. A spectroscopically based approximation technique is proposed to obtain information about the activation energies of nucleation and growth in a narrow temperature range (530-570 °C). Pre-plasmonic and plasmonic NP precipitation stages are identified separated in time. The process as a whole is discussed employing classical nucleation/growth theory and the Kolmogorov-Johnson-Mehl-Avrami phase change model. Activation energies of 3.9(7) eV and 2.6(5) eV have been estimated for the pre-plasmonic and plasmonic spectroscopically assessed stages, respectively. High resolution transmission electron microscopy, differential scanning calorimetry, and Raman spectroscopy were used as complementary techniques for studying the nanoparticulate phase and glass host structure. An empirical linear dependence of the diffusion activation energy on the glass transition temperature with broad applicability is suggested.

Phosphate glass useful in high power lasers

DOEpatents

Hayden, Joseph S.; Sapak, David L.; Ward, Julia M.

1990-01-01

A low- or no-silica phosphate glass useful as a laser medium and having a high thermal conductivity, K.sub.90.degree. C. >0.8 W/mK, and a low coefficient of thermal expansion, .alpha..sub.20.degree.-40.degree. C. <80.times.10.sup.-7 /.degree.C., consists essentially of (on a batch composition basis): the amounts of Li.sub.2 O and Na.sub.2 O providing an average alkali metal ionic radius sufficiently low whereby said glass has K.sub.90.degree. C. >0.8 W/mK and .alpha..sub.20.degree.-40.degree. C. <80.times.10.sup.-7 /.degree.C., and wherein, when the batch composition is melted in contact with a silica-containing surface, the final glass composition contains at most about 3.5 mole % of additional silica derived from such contact during melting. The Nd.sub.2 O.sub.3 can be replaced by other lasing species.

Low phonon energies and wideband optical windows of La2O3-Ga2O3 glasses prepared using an aerodynamic levitation technique.

PubMed

Yoshimoto, Kohei; Masuno, Atsunobu; Ueda, Motoi; Inoue, Hiroyuki; Yamamoto, Hiroshi; Kawashima, Tastunori

2017-03-30

xLa 2 O 3 -(100 - x)Ga 2 O 3 binary glasses were synthesized by an aerodynamic levitation technique. The glass-forming region was found to be 20 ≤ x ≤ 57. The refractive indices were greater than 1.92 and increased linearly with increasing x. The polarizabilities of oxide ions were estimated to be 2.16-2.41 Å 3 , indicating that the glasses were highly ionic. The glasses were transparent over a very wide range from the ultraviolet to the mid-infrared region. The widest transparent window among the oxide glasses was from 270 nm to 10 μm at x = 55. From the Raman scattering spectra, a decrease in bridging oxide ions and an increase in non-bridging oxide ions were confirmed to occur with increasing La 2 O 3 content. The maximum phonon energy was found to be approximately 650 cm -1 , being one of the lowest among oxide glasses. These results show that La 2 O 3 -Ga 2 O 3 binary glasses should be promising host materials for optical applications such as lenses, windows, and filters over a very wide wavelength range.

Low phonon energies and wideband optical windows of La2O3-Ga2O3 glasses prepared using an aerodynamic levitation technique

PubMed Central

Yoshimoto, Kohei; Masuno, Atsunobu; Ueda, Motoi; Inoue, Hiroyuki; Yamamoto, Hiroshi; Kawashima, Tastunori

2017-01-01

xLa2O3-(100 − x)Ga2O3 binary glasses were synthesized by an aerodynamic levitation technique. The glass-forming region was found to be 20 ≤ x ≤ 57. The refractive indices were greater than 1.92 and increased linearly with increasing x. The polarizabilities of oxide ions were estimated to be 2.16–2.41 Å3, indicating that the glasses were highly ionic. The glasses were transparent over a very wide range from the ultraviolet to the mid-infrared region. The widest transparent window among the oxide glasses was from 270 nm to 10 μm at x = 55. From the Raman scattering spectra, a decrease in bridging oxide ions and an increase in non-bridging oxide ions were confirmed to occur with increasing La2O3 content. The maximum phonon energy was found to be approximately 650 cm−1, being one of the lowest among oxide glasses. These results show that La2O3-Ga2O3 binary glasses should be promising host materials for optical applications such as lenses, windows, and filters over a very wide wavelength range. PMID:28358112

Low phonon energies and wideband optical windows of La2O3-Ga2O3 glasses prepared using an aerodynamic levitation technique

NASA Astrophysics Data System (ADS)

Yoshimoto, Kohei; Masuno, Atsunobu; Ueda, Motoi; Inoue, Hiroyuki; Yamamoto, Hiroshi; Kawashima, Tastunori

2017-03-01

xLa2O3-(100 - x)Ga2O3 binary glasses were synthesized by an aerodynamic levitation technique. The glass-forming region was found to be 20 ≤ x ≤ 57. The refractive indices were greater than 1.92 and increased linearly with increasing x. The polarizabilities of oxide ions were estimated to be 2.16-2.41 Å3, indicating that the glasses were highly ionic. The glasses were transparent over a very wide range from the ultraviolet to the mid-infrared region. The widest transparent window among the oxide glasses was from 270 nm to 10 μm at x = 55. From the Raman scattering spectra, a decrease in bridging oxide ions and an increase in non-bridging oxide ions were confirmed to occur with increasing La2O3 content. The maximum phonon energy was found to be approximately 650 cm-1, being one of the lowest among oxide glasses. These results show that La2O3-Ga2O3 binary glasses should be promising host materials for optical applications such as lenses, windows, and filters over a very wide wavelength range.

Chemistry of uranium in aluminophosphate glasses

NASA Technical Reports Server (NTRS)

Schreiber, H. D.; Balazs, G. B.; Williams, B. J.

1982-01-01

The U(VI)-U(V)-U(IV) redox equilibria are investigated in two sodium aluminophosphate base compositions at a variety of melt temperatures, imposed oxygen fugacities, and uranium contents. Results show that the higher redox states of uranium are quite soluble in the phosphate glasses, although U(IV) readily precipitates from the melts as UO2. In addition, comparisons of the uranium redox equilibria established in phosphate melts versus those in silicate melts shows that the coordination sites of the individual uranium species are generally the same in both solvent systems although they differ in detail.

Preparation, mechanical property and cytocompatibility of freeze-cast porous calcium phosphate ceramics reinforced by phosphate-based glass.

PubMed

Yang, Yanqiu; He, Fupo; Ye, Jiandong

2016-12-01

In this study, phosphate-based glass (PG) was used as a sintering aid for freeze-cast porous biphasic calcium phosphate (BCP) ceramic, which was sintered under a lower temperature (1000°C). The phase composition, pore structure, compressive strength, and cytocompatibility of calcium phosphate composite ceramics (PG-BCP) were evaluated. The results indicated that PG additive reacted with calcium phosphate during the sintering process, forming β-Ca2P2O7; the ions of sodium and magnesium from PG partially substituted the calcium sites of β-calcium phosphate in BCP. The PG-BCP showed good cytocompatibility. The pore width of the porous PG-BCP ceramics was around 50μm, regardless of the amount of PG sintering aid. As the content of PG increased from 0wt.% to 15wt.%, the compressive strength of PG-BCP increased from 0.02 MP to 0.28MPa. When the PG additive was 17.5wt.%, the compressive strength of PG-BCP dramatically increased to 5.66MPa. Addition of 15wt.% PG was the critical point for the properties of PG-BCP. PG is considered as an effective sintering aid for freeze-cast porous bioceramics. Copyright © 2016 Elsevier B.V. All rights reserved.

Fe-Mn binary oxide incorporated into diatomite as an adsorbent for arsenite removal: preparation and evaluation.

PubMed

Chang, Fangfang; Qu, Jiuhui; Liu, Huijuan; Liu, Ruiping; Zhao, Xu

2009-10-15

Fe-Mn binary oxide incorporated into diatomite (FMBO-diatomite) was prepared by a simple coating method, and exhibited high oxidation and adsorption ability for arsenite [As(III)]. After being incorporated by Fe-Mn binary oxide, the surface area of diatomite increased 36%, and the pore volume increased five times. The pHzpc of FMBO-diatomite was determined to be 8.1. These characteristics are responsible for the increased As(III) adsorption efficiency. The adsorption equilibria of As(III) on FMBO-diatomite were described well by a Langmuir isotherm model due to the homogeneous distribution of Fe-Mn binary oxide on a diatomite surface. As(III) was oxidized into As(V), and then adsorbed by FMBO-diatomite. The oxidation and adsorption efficiencies for As(III) depended deeply on the pH of solution. When the pH was raised to 8.1, the As(III) adsorption efficiency of FMBO-diatomite was almost equal to the As(III) oxidation efficiency. Silicate and phosphate had negative effects on As(III) adsorption. Also the influence of silicate and phosphate with the pH variation was different.

Real-time dissolution measurement of sized and unsized calcium phosphate glass fibers.

PubMed

Rinehart, J D; Taylor, T D; Tian, Y; Latour, R A

1999-01-01

The objective of this study was to develop an efficient "real time" measurement system able to directly measure, with microgram resolution, the dissolution rate of absorbable glass fibers, and utilize the system to evaluate the effectiveness of silane-based sizing as a means to delay the fiber dissolution process. The absorbable glass fiber used was calcium phosphate (CaP), with tetramethoxysilane selected as the sizing agent. E-glass fiber was used as a relatively nondegrading control. Both the unsized-CaP and sized-CaP degraded linearly at both the 37 degrees C and 60 degrees C test temperature levels used. No significant decrease in weight-loss rate was recorded when the CaP fiber tows were pretreated, using conventional application methods, with the tetramethoxysilane sizing for either temperature condition. The unsized-CaP and sized-CaP weight loss rates were each significantly higher at 60 than at 37 degrees C (both p < 0.02), as expected from dissolution kinetics. In terms of actual weight loss rate measured using our system for phosphate glass fiber, the unsized-CaP fiber we studied dissolved at a rate of 10.90 x 10(-09) and 41.20 x 10(-09) g/min-cm(2) at 37 degrees C and 60 degrees C, respectively. Considering performance validation of the developed system, the slope of the weight loss vs. time plot for the tested E-glass fiber was not significantly different compared to a slope equal to zero for both test temperatures. Copyright 1999 John Wiley & Sons, Inc.

Bioactivity of gel-glass powders in the CaO-SiO2 system: a comparison with ternary (CaO-P2O5-SiO2) and quaternary glasses (SiO2-CaO-P2O5-Na2O).

PubMed

Saravanapavan, Priya; Jones, Julian R; Pryce, Russell S; Hench, Larry L

2003-07-01

Bioactive glasses react chemically with body fluids in a manner that is compatible with the repair processes of the tissues. This results in the formation of an interfacial bond between the glasses and living tissue. Bioactive glasses also stimulate bone-cell proliferation. This behavior is dependent on the chemical composition as well as the surface texture of the glasses. It has been recently reported that gel-derived monolith specimens in the binary SiO2 - CaO are bioactive over a similar molar range of SiO2 content as the previously studied ternary CaO-P2O5-SiO2 system. In this report, the preparation and bioactivity of the binary gel-glass powder with 70 mol % SiO2 is discussed and its bioactivity is compared with the melt-derived 45S5 (quaternary) Bioglass and sol-gel-derived 58S (ternary) bioactive gel-glass compositions. Dissolution kinetic parameters K(1) and K(2) were also computed based on the silicon release for all glass powders. It was shown that the simple two-component SiO2-CaO gel-glass powder is bioactive with comparable dissolution rates as the clinically used melt-derived 45S5 Bioglass powder and extensively studied sol-gel-derived 58S gel-glass powder. Copyright 2003 Wiley Periodicals, Inc.

Structural investigation of new vanadium-bismuth-phosphate glasses by IR and ESR spectroscopy

NASA Astrophysics Data System (ADS)

Vedeanu, N.; Cozar, O.; Stanescu, R.; Cozar, I. B.; Ardelean, I.

2013-07-01

IR spectra changes of the xV2O5(1 - x)[0.8P2O5ṡ0.2Bi2O3] glass system with 0 ⩽ x ⩽ 50 mol% show that vanadium oxide acts as a network modifier at low concentration (x ⩽ 5 mol%), affecting especially the Bi2O3 network. In the same time the phosphate groups (structures) impose their presence by themselves, fact which is illustrated by the increasing of the intensity of characteristic 910, 1040, 1230 cm-1 bands. The IR bands belonging to the phosphate groups are strongly reduced for x ⩾ 10 mol% due to the phosphate network depolymerization and to the appearance of new vibrations characteristic for POV and VOV linkages, showing the network former role of V2O5. In the same time the changes observed in the ESR spectra of these glasses are explained supposing the superposition of two signals, one with a well-resolved hyperfine structure typical for isolated V4+ ions and a broad line characteristic for clustered ions. The line width dependence versus V2O5 content shows that dipole-dipole interactions exist between vanadium ions until x = 5 mol% and the superexchange interactions prevail at high content (x ⩾ 10 mol%).

Conversion of D-ribulose 5-phosphate to D-xylulose 5-phosphate : new insights from structural and biochemical studies on human RPE.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Liang, W.; Ouyang, S.; Shaw, N.

2011-02-01

The pentose phosphate pathway (PPP) confers protection against oxidative stress by supplying NADPH necessary for the regeneration of glutathione, which detoxifies H{sub 2}O{sub 2} into H{sub 2}O and O{sub 2}. RPE functions in the PPP, catalyzing the reversible conversion of D-ribulose 5-phosphate to D-xylulose 5-phosphate and is an important enzyme for cellular response against oxidative stress. Here, using structural, biochemical, and functional studies, we show that human D-ribulose 5-phosphate 3-epimerase (hRPE) uses Fe{sup 2+} for catalysis. Structures of the binary complexes of hRPE with D-ribulose 5-phosphate and D-xylulose 5-phosphate provide the first detailed molecular insights into the binding mode ofmore » physiological ligands and reveal an octahedrally coordinated Fe{sup 2+} ion buried deep inside the active site. Human RPE folds into a typical ({beta}/{alpha}){sub 8} triosephosphate isomerase (TIM) barrel with a loop regulating access to the active site. Two aspartic acids are well positioned to carry out the proton transfers in an acid-base type of reaction mechanism. Interestingly, mutating Ser-10 to alanine almost abolished the enzymatic activity, while L12A and M72A mutations resulted in an almost 50% decrease in the activity. The binary complexes of hRPE reported here will aid in the design of small molecules for modulating the activity of the enzyme and altering flux through the PPP.« less

Protein-adsorption and Ca-phosphate formation on chitosan-bioactive glass composite coatings

NASA Astrophysics Data System (ADS)

Wagener, V.; Boccaccini, A. R.; Virtanen, S.

2017-09-01

In the last years, chitosan-bioactive glass (BG) composites have been developed and investigated as bioactive coatings for orthopedic applications. The increase of bioactivity occurs due to the stimulation of calcium-phosphate/hydroxyapatite formation on the surface while the coating is degrading. In the present work, protein adsorption and its influence on calcium-phosphate precipitation was studied for the first time on such composite coatings. The experiments involved coating of 316L stainless steel substrates with chitosan (Ch) and chitosan-bioactive glass (Ch-BG) and immersion of the coated samples in two different bovine serum albumin (BSA) containing solutions, namely DI H2O (with pH adjusted to about 7.2 with diluted NaOH) and simulated body fluid (SBF). In order to investigate the influence of protein adsorption on calcium-phosphate precipitation, samples were also immersed in DI H2O and in SBF without BSA. Samples were analyzed by scanning electron microscopy (SEM), X-ray photoelectron spectroscopy (XPS) and time-of-flight secondary ion mass spectrometry (ToF-SIMS). Surface analysis revealed that adsorption of BSA takes place on all studied samples and that protein adsorption is influenced by the presence of Ca2+ and PO43- ions. Bioactivity in the form of hydroxyapatite pre-stage formation is significantly increased on Ch-BG composite coating as compared with bare stainless steel surface. However, calcium-phosphate precipitation in SBF is reduced by the presence of BSA.

Impact effects of gamma irradiation on the optical and FT infrared absorption spectra of some Nd3+-doped soda lime phosphate glasses

NASA Astrophysics Data System (ADS)

Marzouk, M. A.; Elkashef, I. M.; Elbatal, H. A.

2018-04-01

The main aim of the present work is to study by two collective optical and FTIR spectral measurements some prepared Nd2O3-doped soda lime phosphate glasses before and after gamma irradiation with dose (9 Mrad). The spectral data reveal two strong UV absorption peaks which are correlated with unavoidable trace iron impurities beside extended additional characteristic bands due to Nd3+ ions. Gamma irradiation on the undoped glass produces slight decrease of the intensity of the UV absorption and the generation of an induced visible band and these effects are controlled with two photochemical reduction of some Fe3+ ions to Fe2+ ions together with the formation of nonbridging oxygen hole center (NBOHC) or phosphorous oxygen hole center (POHC). The impact effect of gamma irradiation on the spectra of Nd2O3-doped glasses is limited due to suggested shielding behavior of neodymium ions. FT-infrared spectra show vibrational modes due to main Q2-Q3 phosphate groups and the response of gamma irradiation of the IR spectra is low and the limited variations are related to suggested changes in some bond angles and bond lengths which cause the observed decrease to the intensities of some IR bands.

Vitrified metal finishing wastes I. Composition, density and chemical durability.

PubMed

Bingham, P A; Hand, R J

2005-03-17

Durable phosphate glasses were formed by vitrifying waste filter cakes from two metal finishing operations. Some melts formed crystalline components during cooling. Compositional analysis of dried, heat treated and vitrified samples was made using energy-dispersive X-ray spectroscopy, X-ray fluorescence spectroscopy, inductively-coupled plasma spectroscopy and Leco induction furnace combustion analysis. Hydrolytic dissolution, measured by an adapted product consistency test, was reduced by up to 3 orders of magnitude upon heat treatment or vitrification, surpassing the performance of borosilicate glass in some cases. This was attributed to the high levels of iron and zinc in the wastes, which greatly improve the durability of phosphate glasses. One of the wastes arose from a metal phosphating process and was particularly suitable for vitrification due to its high P2O5 content and favourable melting behaviour. The other waste, which arose from a number of processes, was less suitable as it had a low P2O5 content and during heating it emitted harmful corrosive gases and underwent violent reactions. Substantial volume reductions were obtained by heat treatment and vitrification of both wastes. Compositions and performances of some vitrified wastes were comparable with those of glasses which are under consideration for the immobilisation of toxic and nuclear wastes.

Incorporation of casein phosphopeptide-amorphous calcium phosphate into a glass-ionomer cement.

PubMed

Mazzaoui, S A; Burrow, M F; Tyas, M J; Dashper, S G; Eakins, D; Reynolds, E C

2003-11-01

Casein phosphopeptide-amorphous calcium phosphate (CPP-ACP) nanocomplexes have been shown to prevent demineralization and promote remineralization of enamel subsurface lesions in animal and in situ caries models. The aim of this study was to determine the effect of incorporating CPP-ACP into a self-cured glass-ionomer cement (GIC). Incorporation of 1.56% w/w CPP-ACP into the GIC significantly increased microtensile bond strength (33%) and compressive strength (23%) and significantly enhanced the release of calcium, phosphate, and fluoride ions at neutral and acidic pH. MALDI mass spectrometry also showed casein phosphopeptides from the CPP-ACP nanocomplexes to be released. The release of CPP-ACP and fluoride from the CPP-ACP-containing GIC was associated with enhanced protection of the adjacent dentin during acid challenge in vitro.

Investigating the addition of SiO₂-CaO-ZnO-Na₂O-TiO₂ bioactive glass to hydroxyapatite: Characterization, mechanical properties and bioactivity.

PubMed

Yatongchai, Chokchai; Placek, Lana M; Curran, Declan J; Towler, Mark R; Wren, Anthony W

2015-11-01

Hydroxyapatite (Ca10(PO4)6(OH)2) is widely investigated as an implantable material for hard tissue restoration due to its osteoconductive properties. However, hydroxyapatite in bulk form is limited as its mechanical properties are insufficient for load-bearing orthopedic applications. Attempts have been made to improve the mechanical properties of hydroxyapatite, by incorporating ceramic fillers, but the resultant composite materials require high sintering temperatures to facilitate densification, leading to the decomposition of hydroxyapatite into tricalcium phosphate, tetra-calcium phosphate and CaO phases. One method of improving the properties of hydroxyapatite is to incorporate bioactive glass particles as a second phase. These typically have lower softening points which could possibly facilitate sintering at lower temperatures. In this work, a bioactive glass (SiO2-CaO-ZnO-Na2O-TiO2) is incorporated (10, 20 and 30 wt%) into hydroxyapatite as a reinforcing phase. X-ray diffraction confirmed that no additional phases (other than hydroxyapatite) were formed at a sintering temperature of 560 ℃ with up to 30 wt% glass addition. The addition of the glass phase increased the % crystallinity and the relative density of the composites. The biaxial flexural strength increased to 36 MPa with glass addition, and there was no significant change in hardness as a function of maturation. The pH of the incubation media increased to pH 10 or 11 through glass addition, and ion release profiles determined that Si, Na and P were released from the composites. Calcium phosphate precipitation was encouraged in simulated body fluid with the incorporation of the bioactive glass phase, and cell culture testing in MC-3T3 osteoblasts determined that the composite materials did not significantly reduce cell viability. © The Author(s) 2015.

Effect of boron oxide addition on the viscosity-temperature behaviour and structure of phosphate-based glasses.

PubMed

Sharmin, Nusrat; Hasan, Muhammad S; Rudd, Chris D; Boyd, Daniel; Werner-Zwanziger, Ulrike; Ahmed, Ifty; Parsons, Andrew J

2017-05-01

In this study, nine phosphate-based glass formulations from the system P 2 O 5 -CaO-Na 2 O-MgO-B 2 O 3 were prepared with P 2 O 5 content fixed as 40, 45 and 50 mol%, where Na 2 O was replaced by 5 and 10 mol% B 2 O 3 and MgO and CaO were fixed to 24 and 16 mol%, respectively. The effect of B 2 O 3 addition on the viscosity-temperature behaviour, fragility index and structure of the glasses was investigated. The composition of the glasses was confirmed by ICP-AES. The viscosity-temperature behaviour of the glasses were measured using beam-bending and parallel -plate viscometers. The viscosity of the glasses investigated was found to shift to higher temperature with increasing B 2 O 3 content. The kinetic fragility parameter, m and F 1/2 , estimated from the viscosity curve were found to decease with increasing B 2 O 3 content. The structural analysis was achieved by a combination of Fourier transform infrared spectroscopy and solid state nuclear magnetic resonance. 31 P solid-state magic-angle-spinning nuclear magnetic resonance (MAS-NMR) showed that the local structure of the glasses changes with increasing B 2 O 3 content. As B 2 O 3 was added to the glass systems, the phosphate connectivity increases as the as the Q 1 units transforms into Q 2 units. The 11 B NMR results confirmed the presence of tetrahedral boron (BO 4 ) units for all the compositions investigated. Structural analysis indicates an increasing level of cross-linking with increasing B 2 O 3 content. Evidence of the presence of P-O-B bonds was also observed from the FTIR and 31 P NMR analysis. © 2016 Wiley Periodicals, Inc. J Biomed Mater Res Part B: Appl Biomater, 105B: 764-777, 2017. © 2016 Wiley Periodicals, Inc.

The decoupling of the glass transitions in the two-component p-spin spherical model

NASA Astrophysics Data System (ADS)

Ikeda, Harukuni; Ikeda, Atsushi

2016-07-01

Binary mixtures of large and small particles with a disparate size ratio exhibit a rich phenomenology at their glass transition points. In order to gain insights on such systems, we introduce and study a two-component version of the p-spin spherical spin glass model. We employ the replica method to calculate the free energy and the phase diagram. We show that when the strengths of the interactions of each component are not widely separated, the model has only one glass phase characterized by the conventional one-step replica symmetry breaking. However when the strengths of the interactions are well separated, the model has three glass phases depending on the temperature and component ratio. One is the ‘single’ glass phase in which only the spins of one component are frozen while the spins of the other component remain mobile. This phase is characterized by the one-step replica symmetry breaking. The second is the ‘double’ glass phase obtained by cooling the single glass phase further, in which the spins of the remaining mobile component are also frozen. This phase is characterized by the two-step replica symmetry breaking. The third is also the ‘double’ glass phase, which, however, is formed by the simultaneous freezing of the spins of both components at the same temperatures and is characterized by the one-step replica symmetry breaking. We discuss the implications of these results for the glass transitions of binary mixtures.

Kinetics of UV laser radiation defects in high performance glasses

NASA Astrophysics Data System (ADS)

Natura, U.; Feurer, T.; Ehrt, D.

2000-05-01

High purity fluoride phosphate glasses are attractive candidates as UV transmitting materials. The calculated values for the ultraviolet resonance wavelength are comparable with those of pure silica glass or fluoride single crystal CaF2. The formation of radiation-induced defect centers leads to additional absorption bands in the VUV-UV-vis range. The damage and the healing behavior by lamps and lasers are investigated in dependence on phosphate content and the content of impurities, mainly transition metals. Experiments were carried out using pulsed lasers with a duration of femto- and nanoseconds at a wavelength of 248 nm. The initial slope of the induced absorption shows a nonlinear dependence on the pulse energy density. Resonant and non-resonant two-photon mechanisms were observed. Two-photon-absorption coefficients at 248 nm for samples with different phosphate contents were measured. Models of the kinetics of the radiation-induced defects were developed. The inclusion of energy transfer was necessary to explain the difference in the damage behavior for nanosecond (248 nm, 193 nm) and femtosecond (248 nm) laser pulses.

Magnesium coated bioresorbable phosphate glass fibres: investigation of the interface between fibre and polyester matrices.

PubMed

Liu, Xiaoling; Grant, David M; Parsons, Andrew J; Harper, Lee T; Rudd, Chris D; Ahmed, Ifty

2013-01-01

Bioresorbable phosphate glass fibre reinforced polyester composites have been investigated as replacement for some traditional metallic orthopaedic implants, such as bone fracture fixation plates. However, composites tested revealed loss of the interfacial integrity after immersion within aqueous media which resulted in rapid loss of mechanical properties. Physical modification of fibres to change fibre surface morphology has been shown to be an effective method to improve fibre and matrix adhesion in composites. In this study, biodegradable magnesium which would gradually degrade to Mg(2+) in the human body was deposited via magnetron sputtering onto bioresorbable phosphate glass fibres to obtain roughened fibre surfaces. Fibre surface morphology after coating was observed using scanning electron microscope (SEM). The roughness profile and crystalline texture of the coatings were determined via atomic force microscope (AFM) and X-ray diffraction (XRD) analysis, respectively. The roughness of the coatings was seen to increase from 40 ± 1 nm to 80 ± 1 nm. The mechanical properties (tensile strength and modulus) of fibre with coatings decreased with increased magnesium coating thickness.

Magnesium Coated Bioresorbable Phosphate Glass Fibres: Investigation of the Interface between Fibre and Polyester Matrices

PubMed Central

Liu, Xiaoling; Grant, David M.; Parsons, Andrew J.; Harper, Lee T.; Rudd, Chris D.; Ahmed, Ifty

2013-01-01

Bioresorbable phosphate glass fibre reinforced polyester composites have been investigated as replacement for some traditional metallic orthopaedic implants, such as bone fracture fixation plates. However, composites tested revealed loss of the interfacial integrity after immersion within aqueous media which resulted in rapid loss of mechanical properties. Physical modification of fibres to change fibre surface morphology has been shown to be an effective method to improve fibre and matrix adhesion in composites. In this study, biodegradable magnesium which would gradually degrade to Mg2+ in the human body was deposited via magnetron sputtering onto bioresorbable phosphate glass fibres to obtain roughened fibre surfaces. Fibre surface morphology after coating was observed using scanning electron microscope (SEM). The roughness profile and crystalline texture of the coatings were determined via atomic force microscope (AFM) and X-ray diffraction (XRD) analysis, respectively. The roughness of the coatings was seen to increase from 40 ± 1 nm to 80 ± 1 nm. The mechanical properties (tensile strength and modulus) of fibre with coatings decreased with increased magnesium coating thickness. PMID:24066297

Study of electrical conductivity and memory switching in the zinc-vanadium-phosphate glasses

NASA Astrophysics Data System (ADS)

Mirzayi, M.; Hekmatshoar, M. H.

2013-07-01

Vanadium zinc phosphate glasses were prepared by the conventional melt quenching technique and effect of V2O5 concentration on d.c. conductivity of prepared samples were investigated. X-ray diffraction patterns confirmed the glassy character of the samples. The d.c. conductivity increased with increase in V2O5 content. Results showed that activation energy has a single value in the investigated range of temperature, which can be explained in accordance with Mott small pollaron hopping model. I-V characteristics at high electric field showed that switching in these glasses was memory type. The threshold field of switching was found to decrease with increase in V2O5 content. Non-linear behavior and switching phenomenon was explained by Pool-Frenkel effect and thermal model.

Solar pumping of solid state lasers for space mission: a novel approach

NASA Astrophysics Data System (ADS)

Boetti, N. G.; Lousteau, J.; Negro, D.; Mura, E.; Scarpignato, G. C.; Perrone, G.; Milanese, D.; Abrate, S.

2017-11-01

Solar pumped laser (SPL) can find wide applications in space missions, especially for long lasting ones. In this paper a new technological approach for the realization of a SPL based on fiber laser technology is proposed. We present a preliminary study, focused on the active material performance evaluation, towards the realization of a Nd3+ -doped fiber laser made of phosphate glass materials, emitting at 1.06 μm. For this research several Nd3+ -doped phosphate glass samples were fabricated, with concentration of Nd3+ up to 10 mol%. Physical and thermal properties of the glasses were measured and their spectroscopic properties are described. The effect of Nd3+ doping concentration on emission spectra and lifetimes was investigated in order to study the concentration quenching effect on luminescence performance.

Determination of nonlinear optical properties by time resolved Z-scan in Nd-doped phosphate glass

NASA Astrophysics Data System (ADS)

de Souza, J. M.; de Lima, W. J.; Pilla, V.; Andrade, A. A.; Dantas, N. O.; Messias, D. N.

2017-02-01

In this work, we have used a Ti3+:Safira laser tuned at 803nm to performed time-resolved measurements using the Z-scan technique to characterize the nonlinear optical properties of phosphate glasses. The glass matrices, labeled PAN (P2O5-Al2O3-Na2CO3) and PANK (P2O5-Al2O3- Na2O-K2O), were doped with increasing Nd3+ concentration, ranging from 0.5 to 5 wt%. For both systems, we have seen that the optical nonlinearity has a linear dependence with the doping ion concentration. Therefore, we propose a new approach to obtain the parameters Δα and Δσ. All results obtained are in good agreement with others found in the literature.

Studies of structure of calcium-iron phosphate glasses by infrared, Raman and UV-Vis spectroscopies

NASA Astrophysics Data System (ADS)

Li, H. J.; Liang, X. F.; Yu, H. J.; Yang, D. Q.; Yang, S. Y.

2016-06-01

Glasses in the ternary CaO-Fe2O3-P2O5 system were prepared and studied by means of density, differential scanning calorimetry, infrared, Raman and UV-Vis spectroscopies. The results showed that density and molar volume in the glass system decreased with increasing substitution of CaO for Fe2O3. The variation of glass transition temperature and thermal stability was strictly related to the nature of bonding in the vitreous network. Spectroscopic analysis showed that substitution of CaO for Fe2O3 induced an evolution of structural units from pyrophosphate to metaphosphate species indicating the polymerization of phosphate chains and the decrease of non-bridging oxygen concentrations. With increasing substitution of CaO for Fe2O3 The P-O-Ca linkage and (P-O- Ca2+ -O-P) chains participated in the glass network by replacing P-O-Fe bonds. The absorption band of the P-O-Ca stretching mode in the glasses with high CaO content (≥32 mol%) was assigned at around 1084 cm-1. The absorption edge would fall in the region between 332 and 420 nm which are the absorption bands of Fe3+ ions.

Structural investigation of phosphate - bismuth glasses with vanadium

NASA Astrophysics Data System (ADS)

Stǎnescu, R.; Vedeanu, N.; Cozar, I. B.; Mǎgdaş, A.

2013-11-01

The xV2O5(1-dx)[0.5P2O5ṡ0.5Bi2O3] glass system with 0 ≤ x ≤ 50 mol% is investigated by IR and Raman spectroscopy. Both P2O5 and Bi2O3 oxides are known as network formers, but Bi2O3 is an unconventional one. At low content of vanadium oxide (x ≤ 5 mol%), both IR and Raman spectra are dominated by vibration bands characteristics to structural groups of phosphate and bismuthate lattices. Due to the network modifier role, vanadium oxide acts mainly on the Bi2O3 network allowing the phosphate groups to impose their characteristics absorption bands in spectra. These bands are strongly reduced for x ≥ 20 mol% due to the phosphate network depolymerization and the appearance of new vibrations characteristic to P-O-V, Bi-O-V and V-O-V groups showing the network former role of V2O5.

Stressed waveguides with tubular depressed-cladding inscribed in phosphate glasses by femtosecond hollow laser beams.

PubMed

Long, Xuewen; Bai, Jing; Zhao, Wei; Stoian, Razvan; Hui, Rongqing; Cheng, Guanghua

2012-08-01

We report on the single-step fabrication of stressed optical waveguides with tubular depressed-refractive-index cladding in phosphate glasses by the use of focused femtosecond hollow laser beams. Tubelike low index regions appear under direct exposure due to material rarefaction following expansion. Strained compacted zones emerged in domains neighboring the tubular track of lower refractive index, and waveguiding occurs mainly within the tube core fabricated by the engineered femtosecond laser beam. The refractive index profile of the optical waveguide was reconstructed from the measured transmitted near-field intensity.

Ultrafast pulsed laser utilizing broad bandwidth laser glass

DOEpatents

Payne, Stephen A.; Hayden, Joseph S.

1997-01-01

An ultrafast laser uses a Nd-doped phosphate laser glass characterized by a particularly broad emission bandwidth to generate the shortest possible output pulses. The laser glass is composed primarily of P.sub.2 O.sub.5, Al.sub.2 O.sub.3 and MgO, and possesses physical and thermal properties that are compatible with standard melting and manufacturing methods. The broad bandwidth laser glass can be used in modelocked oscillators as well as in amplifier modules.

Comprehensive thermal and structural characterization of antimony-phosphate glass

NASA Astrophysics Data System (ADS)

Moustafa, S. Y.; Sahar, M. R.; Ghoshal, S. K.

For the first time, we prepare new ternary glass systems of composition (95-x)Sb2O3-xP2O5-5MgO, where x = 45, 40, 35 mol%; (85-x)Sb2O3-xP2O5-15MgO, where x = 55, 35, 25 mol%; (75-x)Sb2O3-xP2O5-25MgO, where x = 45, 35, 25 mol%; and 60Sb2O3-(40-x)P2O5-xMgO, where x = 10, 20 mol% via melt-quenching method. Synthesized glasses are characterized using XRD, FESEM, EDX, and TG/DTA measurements. The influence of varying modifier concentrations on their thermal properties is evaluated. The XRD patterns confirmed the amorphous nature of samples. SEM images demonstrated interesting phase formation with ribbons-like texture. Five crystalline phases are evidenced in the ternary diagram which are antimony phosphate and antimony orthophosphate as major phases as well as magnesium phosphate, magnesium cyclo-tetraphosphate and cervantite as minor phases. EDX spectra detected the right elemental traces. Detailed thermal analysis of these glasses revealed their high-molecular polymer character for Sb2O3 content greater than 50 mol%. Three different glass transition temperatures are achieved around 276, 380-381 and 422-470 °C depending on the composition. Furthermore, the solidus and liquidus temperature are found to decrease with increasing Sb2O3 and increases for MgO contents till 15 mol% and then decrease, where the lowest recorded solidus temperature is 426 °C. This observation may open up new research avenues for antimony based ternary glasses and an exploitation of the derived results for optoelectronics applications, photonic devices and non-linear optical devices.

Towards modular bone tissue engineering using Ti-Co-doped phosphate glass microspheres: cytocompatibility and dynamic culture studies.

PubMed

Peticone, Carlotta; De Silva Thompson, David; Owens, Gareth J; Kim, Hae-Won; Micheletti, Martina; Knowles, Jonathan C; Wall, Ivan

2017-09-01

The production of large quantities of functional vascularized bone tissue ex vivo still represent an unmet clinical challenge. Microcarriers offer a potential solution to scalable manufacture of bone tissue due to their high surface area-to-volume ratio and the capacity to be assembled using a modular approach. Microcarriers made of phosphate bioactive glass doped with titanium dioxide have been previously shown to enhance proliferation of osteoblast progenitors and maturation towards functional osteoblasts. Furthemore, doping with cobalt appears to mimic hypoxic conditions that have a key role in promoting angiogenesis. This characteristic could be exploited to meet the clinical requirement of producing vascularized units of bone tissue. In the current study, the human osteosarcoma cell line MG-63 was cultured on phosphate glass microspheres doped with 5% mol titanium dioxide and different concentrations of cobalt oxide (0%, 2% and 5% mol), under static and dynamic conditions (150 and 300 rpm on an orbital shaker). Cell proliferation and the formation of aggregates of cells and microspheres were observed over a period of two weeks in all glass compositions, thus confirming the biocompatibility of the substrate and the suitability of this system for the formation of compact micro-units of tissue. At the concentrations tested, cobalt was not found to be cytotoxic and did not alter cell metabolism. On the other hand, the dynamic environment played a key role, with moderate agitation having a positive effect on cell proliferation while higher agitation resulting in impaired cell growth. Finally, in static culture assays, the capacity of cobalt doping to induce vascular endothelial growth factor (VEGF) upregulation by osteoblastic cells was observed, but was not found to increase linearly with cobalt oxide content. In conclusion, Ti-Co phosphate glasses were found to support osteoblastic cell growth and aggregate formation that is a necessary precursor to tissue formation and the upregaulation of VEGF production can potentially support vascularization.

Gamma rays shielding and sensing application of some rare earth doped lead-alumino-phosphate glasses

NASA Astrophysics Data System (ADS)

Kaur, Preet; Singh, Devinder; Singh, Tejbir

2018-03-01

Seven rare earth (Sm3+, Eu3+ and Nd3+) doped lead alumino phosphate glasses were prepared. The protective and sensing measures from gamma rays were analysed in terms of parameters viz. density (ρ), refractive index, energy band gap (Eg), mean free path (mfp), effective atomic number (Zeff) and buildup factors (energy absorption EABF as well as exposure buildup factor EBF). The energy dependent parameters (mfp, Zeff, EABF and EBF) were investigated in the energy region from 15 keV to 15 MeV. EABF and EBF values were observed to be maximum in the intermediate energy region. Besides, the EABF and EBF values for the prepared samples are shown to have strong dependence on chemical composition of the glass at lower energy, whereas, it is almost independent of chemical composition in higher energy region. The prepared glass samples are found to have potential applications in radiation shielding as well as radiation sensing, which further find numerous applications in the field of medicine and industry.

Influence of silver nanoparticles on the spectroscopic properties of Sm{sup 3+} doped boro-phosphate glasses

DOE Office of Scientific and Technical Information (OSTI.GOV)

Suthanthirakumar, P.; Marimuthu, K., E-mail: emari-ram2000@yahoo.com

The Sm{sup 3+} doped novel boro-phosphate glasses containing silver nanoparticles (NPs) (SmBPxA) have been prepared following the melt quenching technique and their structural and spectroscopic behavior were studied through HR-TEM, optical absorption and photoluminescence spectral measurements. The TEM analysis validates the existence of Ag NPs with an average diameter of ~8 nm. The Surface plasmon resonance (SPR) band of silver NPs was found at around 600 nm from the absorption spectrum of the Sm{sup 3+} ions free glass sample. The optical band gap energy (E{sub opt}) corresponding to the direct and indirect allowed transitions and the Urbach energy (ΔE) valuesmore » were determined from the absorption spectral measurements. The luminescence intensity is found to get enhance when the Ag NPs were embedded along with the Sm{sup 3+} ions in the prepared glasses due to the local electric field effect around the rare earth (RE) ion site produced by the SPR of Ag NPs.« less

Microwave Crystallization of Lithium Aluminum Germanium Phosphate Solid-State Electrolyte.

PubMed

Mahmoud, Morsi M; Cui, Yuantao; Rohde, Magnus; Ziebert, Carlos; Link, Guido; Seifert, Hans Juergen

2016-06-23

Lithium aluminum germanium phosphate (LAGP) glass-ceramics are considered as promising solid-state electrolytes for Li-ion batteries. LAGP glass was prepared via the regular conventional melt-quenching method. Thermal, chemical analyses and X-ray diffraction (XRD) were performed to characterize the prepared glass. The crystallization of the prepared LAGP glass was done using conventional heating and high frequency microwave (MW) processing. Thirty GHz microwave (MW) processing setup were used to convert the prepared LAGP glass into glass-ceramics and compared with the conventionally crystallized LAGP glass-ceramics that were heat-treated in an electric conventional furnace. The ionic conductivities of the LAGP samples obtained from the two different routes were measured using impedance spectroscopy. These samples were also characterized using XRD and scanning electron microscopy (SEM). Microwave processing was successfully used to crystallize LAGP glass into glass-ceramic without the aid of susceptors. The MW treated sample showed higher total, grains and grain boundary ionic conductivities values, lower activation energy and relatively larger-grained microstructure with less porosity compared to the corresponding conventionally treated sample at the same optimized heat-treatment conditions. The enhanced total, grains and grain boundary ionic conductivities values along with the reduced activation energy that were observed in the MW treated sample was considered as an experimental evidence for the existence of the microwave effect in LAGP crystallization process. MW processing is a promising candidate technology for the production of solid-state electrolytes for Li-ion battery.

Pathways for diffusion in the potential energy landscape of the network glass former SiO2

NASA Astrophysics Data System (ADS)

Niblett, S. P.; Biedermann, M.; Wales, D. J.; de Souza, V. K.

2017-10-01

We study the dynamical behaviour of a computer model for viscous silica, the archetypal strong glass former, and compare its diffusion mechanism with earlier studies of a fragile binary Lennard-Jones liquid. Three different methods of analysis are employed. First, the temperature and time scale dependence of the diffusion constant is analysed. Negative correlation of particle displacements influences transport properties in silica as well as in fragile liquids. We suggest that the difference between Arrhenius and super-Arrhenius diffusive behaviour results from competition between the correlation time scale and the caging time scale. Second, we analyse the dynamics using a geometrical definition of cage-breaking transitions that was proposed previously for fragile glass formers. We find that this definition accurately captures the bond rearrangement mechanisms that control transport in open network liquids, and reproduces the diffusion constants accurately at low temperatures. As the same method is applicable to both strong and fragile glass formers, we can compare correlation time scales in these two types of systems. We compare the time spent in chains of correlated cage breaks with the characteristic caging time and find that correlations in the fragile binary Lennard-Jones system persist for an order of magnitude longer than those in the strong silica system. We investigate the origin of the correlation behaviour by sampling the potential energy landscape for silica and comparing it with the binary Lennard-Jones model. We find no qualitative difference between the landscapes, but several metrics suggest that the landscape of the fragile liquid is rougher and more frustrated. Metabasins in silica are smaller than those in binary Lennard-Jones and contain fewer high-barrier processes. This difference probably leads to the observed separation of correlation and caging time scales.

Novel Synthesis of Calcium Oxide-Aluminum Oxide Glasses

NASA Astrophysics Data System (ADS)

Weber, J. K. Richard; Tangeman, Jean A.; Key, Thomas S.; Hiera, Kirsten J.; Paradis, Paul-Francois; Ishikawa, Takehiko; Yu, Jianding; Yoda, Shinichi

2002-05-01

Binary Al2O3:CaO glasses containing 36-50 mole% Al2O3 were synthesized by containerless processing of liquids in nitrogen using aerodynamic and a pressurized electrostatic-aerodynamic levitator. The critical cooling rate for glass formation RC under containerless conditions was ca. 70 K/s. The Vickers hardness of the glasses was 775-785; and the infrared transmission extended to approximately 5500 nm. The work function of the 36 mole% Al2O3 composition was 3.7 eV at 1100 K.

Single-longitudinal mode distributed-feedback fiber laser with low-threshold and high-efficiency

NASA Astrophysics Data System (ADS)

Jiang, Man; Zhou, Pu; Gu, Xijia

2018-01-01

Single-frequency fiber laser has attracted a lot of interest in recent years due to its numerous application potentials in telecommunications, LIDAR, high resolution sensing, atom frequency standard, etc. Phosphate glass fiber is one of the candidates for building compact high gain fiber lasers because of its capability of high-concentration of rare-earth ions doping in fiber core. Nevertheless, it is challenging for the integration of UV-written intra-core fiber Bragg gratings into the fiber laser cavity due to the low photosensitivity of phosphate glass fiber. The research presented in this paper will focus on demonstration of UV-written Bragg gratings in phosphate glass fiber and its application in direct-written short monolithic single-frequency fiber lasers. Strong π-phase shift Bragg grating structure is direct-inscribed into the Er/Yb co-doped gain fiber using an excimer laser, and a 5-cm-long phase mask is used to inscribe a laser cavity into the Er/Yb co-doped phosphate glass fibers. The phase mask is a uniform mask with a 50 μm gap in the middle. The fiber laser device emits output power of 10.44 mW with a slope efficiency of 21.5% and the threshold power is about 42.8 mW. Single-longitudinal mode operation is validated by radio frequency spectrum measurement. Moreover, the output spectrum at the highest power shows an excellent optical signal to noise ratio of about 70 dB. These results, to the best of our knowledge, show the lowest power threshold and highest efficiency among the reports that using the same structure to achieve single-longitudinal mode laser output.

Ultrafast pulsed laser utilizing broad bandwidth laser glass

DOEpatents

Payne, S.A.; Hayden, J.S.

1997-09-02

An ultrafast laser uses a Nd-doped phosphate laser glass characterized by a particularly broad emission bandwidth to generate the shortest possible output pulses. The laser glass is composed primarily of P{sub 2}O{sub 5}, Al{sub 2}O{sub 3} and MgO, and possesses physical and thermal properties that are compatible with standard melting and manufacturing methods. The broad bandwidth laser glass can be used in modelocked oscillators as well as in amplifier modules. 7 figs.

Structural and dynamical studies of molecular and network forming chalcogenide glasses and supercooled liquids with NMR and Raman spectroscopy

NASA Astrophysics Data System (ADS)

Gjersing, Erica Lee

The techniques of Nuclear Magnetic Resonance (NMR) and Raman spectroscopy have been employed to study structure and dynamics in Ge-Se, Ge/As-Te, and As-S binary and complex Ge-As-Te and P-As-S ternary chalcogenide glasses. Structural studies were conducted on Ge-Se glasses and on binary Ge/As-Te and ternary Ge-As-Te systems. The structure of the GexSe100-x glass series, with 5≤x≤33, is investigated with 77Se Magic Angle Spinning (MAS) NMR and then compared with three different proposed structural models. For the binary Ge-Te and As-Te and ternary Ge-As-Te glass systems the structure is studied using Raman spectroscopy and correlated with physical properties such as molar volume, viscosity, optical band gap and thermophysical properties. Studies on glass transition dynamics were conducted on systems with a range of structural features including an As4S3 inorganic molecular glass former, an As-P-S system where molecules are bonded to the As-S network, and network glasses in the Ge-Se system. Timescales of the rotational dynamics of As4S3 cage molecules in the molecular As-sulfide glass and supercooled liquid show remarkably large decoupling from the timescales of viscous flow and shear relaxation at temperatures below and near Tg (312K). Next, the dynamic behavior of a (As 2S3)90(P2S5)10 glass, which is proposed to consist of As2P2S8 molecular structures which are connected to an As-S network, is investigated with 31P NMR. The rotational dynamics of selenium chains in network forming GexSe100-x glasses and supercooled liquids with 5≤x≤23 are investigated with variable temperature 77Se NMR spectroscopy to determine the relationship between rigidity percolation and dynamic behavior. The timescale of the motion of the Se atoms is observed to be nearly identical for x≤17 and ≤2.36. However, for the x=20 and 23 compositions where ≤2.4, above the rigidity percolation threshold, the timescale slows down abruptly. Finally, the Ge20Se 80 glass and supercooled liquid have been the focus of a variable temperature Raman spectroscopy study to investigate the vibrational mode softening behavior and the importance of vibrational entropy in glass transition.

Composition Dependence of the Na(+) Ion Conductivity in 0.5Na2S + 0.5[xGeS2 + (1 - x)PS5/2] Mixed Glass Former Glasses: A Structural Interpretation of a Negative Mixed Glass Former Effect.

PubMed

Martin, Steve W; Bischoff, Christian; Schuller, Katherine

2015-12-24

A negative mixed glass former effect (MGFE) in the Na(+) ion conductivity of glass has been found in 0.5Na2S + 0.5[xGeS2 + (1 - x)PS5/2] glasses where the Na(+) ion conductivity is significantly smaller for all of the ternary glasses than either of the binary end-member glasses. The minimum conductivity of ∼0.4 × 10(-6) (Ω cm)(-1) at 25 °C occurs for the x = 0.7 glass. Prior to this observation, the alkali ion conductivity of sulfide glasses at constant alkali concentration, but variable ratio of one glass former for another (x) ternary mixed glass former (MGF) glasses, has always produced a positive MGFE in the alkali ion conductivity; that is, the ternary glasses have always had higher ion conductivities that either of the end-member binary glasses. While the Na(+) ion conductivity exhibits a single global minimum value, the conductivity activation energy exhibits a bimodal double maximum at x ≈ 0.4 and x ≈ 0.7. The modified Christensen-Martin-Anderson-Stuart (CMAS) model of the activation energies reveals the origin of the negative MGFE to be due to an increase in the dielectric stiffness (a decrease in relative dielectric permittivity) of these glasses. When coupled with an increase in the average Na(+) ion jump distance and a slight increase in the mechanical stiffness of the glass, this causes the activation energy to go through maximum values and thereby produce the negative MGFE. The double maximum in the conductivity activation energy is coincident with double maximums in CMAS calculated strain, ΔES, and Coulombic, ΔEC, activation energies. In these ternary glasses, the increase in the dielectric stiffness of the glass arises from a negative deviation of the limiting high frequency dielectric permittivity as compared to the binary end-member glasses. While the CMAS calculated total activation energies ΔEact = ΔES + ΔEC are found to reproduce the overall shape of the composition dependence of the measured ΔEact values, they are consistently smaller than the measured values for all compositions x. The new concept of an effective Madelung constant for the Na(+) ions in glass is introduced, MD(Na(+)), to account for the difference. Calculated MD(Na(+)) values necessary to bring the CMAS and experimental ΔEact values into agreement are in excellent agreement with nominal values for typical oxide crystals containing Na(+). New MD simulations of oxide glasses were performed and were used to calculate MD(Na(+)) values for Na2O + SiO2 glasses for the first time and were found to agree quite well with the values for the sulfide glasses studied here. Insights from the current study have been used to predict and design new MGF systems that may lead to a positive MGFE in the ionic conductivity.

Non-polymeric asymmetric binary glass-formers. II. Secondary relaxation studied by dielectric, 2H NMR, and 31P NMR spectroscopy

NASA Astrophysics Data System (ADS)

Pötzschner, B.; Mohamed, F.; Bächer, C.; Wagner, E.; Lichtinger, A.; Bock, D.; Kreger, K.; Schmidt, H.-W.; Rössler, E. A.

2017-04-01

We investigate the secondary (β-) relaxations of an asymmetric binary glass former consisting of a spirobichroman derivative (SBC; Tg = 356 K) as the high-Tg component and the low-Tg component tripropyl phosphate (TPP; Tg = 134 K). The main relaxations are studied in Paper I [B. Pötzschner et al., J. Chem. Phys. 146, 164503 (2017)]. A high Tg contrast of ΔTg = 222 K is put into effect in a non-polymeric system. Component-selective studies are carried out by combining results from dielectric spectroscopy (DS) for mass concentrations cTPP ≥ 60% and those from different methods of 2H and 31P NMR spectroscopy. In the case of NMR, the full concentration range (10% ≤ cTPP ≤ 100%) is covered. The neat components exhibit a β-relaxation (β1 (SBC) and β2 (TPP)). The latter is rediscovered by DS in the mixtures for all concentrations with unchanged time constants. NMR spectroscopy identifies the β-relaxations as being alike to those in neat glasses. A spatially highly restricted motion with angular displacement below ±10° encompassing all molecules is involved. In the low temperature range, where TPP shows the typical 31P NMR echo spectra of the β2-process, very similar spectral features are observed for the (deuterated) SBC component by 2H NMR, in addition to its "own" β1-process observed at high temperatures. Apparently, the small TPP molecules enslave the large SBC molecules to perform a common hindered reorientation. The temperature dependence of the spin-lattice relaxation time of both components is the same and reveals an angular displacement of the SBC molecules somewhat smaller than that of TPP, though the time constants τβ2 are the same. Furthermore, T1(T) of TPP in the temperature region of the β2-process is absolutely the same as in the mixture TPP/polystyrene investigated previously. It appears that the manifestations of the β-process introduced by one component are essentially independent of the second component. Finally, at cTPP ≤ 20% one finds indications that the β2-process starts to disintegrate. More and more TPP molecules get immobilized upon decreasing cTPP. We conclude that the β-process is a cooperative process.

Novel High Temperature and Radiation Resistant Infrared Glasses and Optical Fibers for Sensing in Advanced Small Modular Reactors

DOE Office of Scientific and Technical Information (OSTI.GOV)

Ballato, John

One binary and three series of ternary non-oxide pure sulfide glasses compositions were investigated with the goal of synthesizing new glasses that exhibit high glass transition (Tg) and crystallization (Tc) temperatures, infrared transparency, and reliable glass formability. The binary glass series consisted of Ges 2 and La 2S 3 and the three glass series in the x(nBaS + mLa2S3) + (1-2x)GeS2 ternary system have BaS:La2S3 modifier ratios of 1:1, 1:2, and 2:1 with . With these glasses, new insights were realized as to how ionic glasses form and how glass modifiers affect both structure and glass formability. All synthesized compositionsmore » were characterized by Infrared (IR) and Raman spectroscopies and differential thermal analysis (DTA) to better understand the fundamental structure, optical, and thermal characteristics of the glasses. After a range of these glasses were synthesized, optimal compositions were formed into glass disks and subjected to gamma irradiation. Glass disks were characterized both before and after irradiation by microscope imaging, measuring the refractive index, density, and UV-VIS-IR transmission spectra. The final total dose the samples were subjected to was ~2.5 MGy. Ternary samples showed a less than 0.4% change in density and refractive index and minimal change in transmission window. The glasses also resisted cracking as seen in microscope images. Overall, many glass compositions were developed that possess operating temperatures above 500 °C, where conventional chalcogenide glasses such as As2S3 and have T gs from ~200-300 °C, and these glasses have a greater than Tc – Tg values larger than 100 °C and this shows that these glasses have good thermal stability of Tg such that they can be fabricated into optical fibers and as such can be considered candidates for high temperature infrared fiber optics. Initial fiber fabrication efforts showed that selected glasses could be drawn but larger samples would be needed for further development and optimization« less

Synthesis and characterization of chitosan-polyvinyl alcohol-bioactive glass hybrid membranes.

PubMed

Dias, Luisa L S; Mansur, Herman S; Donnici, Claudio Luis; Pereira, Marivalda M

2011-01-01

The tissue engineering strategy is a new approach for the regeneration of cementum, which is essential for the regeneration of the periodontal tissue. This strategy involves the cell cultures present in this tissue, called cementoblasts, and located on an appropriate substrate for posterior implantation in the regeneration site. Prior studies from our research group have shown that the proliferation and viability of cementoblasts increase in the presence of the ionic dissolution products of bioactive glass particles. Therefore, one possible approach to obtaining adequate substrates for cementoblast cultures is the development of composite membranes containing bioactive glass. In the present study, composite films of chitosan-polyvinyl alcohol-bioactive glass containing different glass contents were developed. Glutaraldehyde was also added to allow for the formation of cross-links and changes in the degradation rate. The glass phase was introduced in the material by a sol-gel route, leading to an organic-inorganic hybrid. The films were characterized by Fourier-transformed infrared spectroscopy (FTIR), scanning electron microscopy (SEM) with electron dispersive spectroscopy (EDS) and X-ray diffraction (XRD) analysis. Bioactivity tests were also conducted by immersion of the films in simulated body fluid (SBF). Films containing up to 30% glass phase could be obtained. The formation of calcium phosphate was observed after the immersion of the films. A calcium phosphate layer formed more quickly on materials containing higher bioactive glass contents. In the hybrid containing 23% bioactive glass, a complete layer was formed after 24 h immersion, showing the high bioactivity of this material. However, despite the higher in vitro bioactivity, the film with 23% glass showed lower mechanical properties compared with films containing up to 17% glass.

Bent channel design in buried Er3+/Yb3+ codoped phosphate glass waveguide fabricated by field-assisted annealing

NASA Astrophysics Data System (ADS)

Zhao, Ruitu; Wang, Mu; Chen, Baojie; Liu, Ke; Pun, Edwin Yue-Bun; Lin, Hai

2011-04-01

Bent waveguide structures (S-, U-, and F-bend) based on buried Er3+/Yb3+ codoped phosphate glass waveguide channel fabricated by field-assisted annealing have been designed to achieve high-gain C-band integrated amplification. Using a simulated-bend method, the optimal radius for the curved structure is derived to be 0.90 cm with loss coefficient of 0.02 dB/cm, as the substrate size is schemed to be 4×3 cm2. In the wavelength range of 1520 to 1575 nm, obvious gain enhancement for the bent structure waveguides is anticipated, and for the F-bend waveguide, the internal gain at 1534-nm wavelength is derived to be 41.61 dB, which is much higher than the value of 26.22 and 13.81 dB in the U- and S-bend waveguides, respectively, and over three times higher than that of the straight one. The simulation results indicate that the bent structure design is beneficial in obtaining high signal gain in buried Er3+/Yb3+ codoped phosphate glass waveguides, which lays the foundation for further design and fabrication of integrated devices.

Novel Optical Fiber Materials With Engineered Brillouin Gain Coefficients SSL 1: Novel Fiber Lasers

DTIC Science & Technology

2015-12-29

strontium aluminosilicate glasses . A zero-p12 composition is calculated to be at a SiO2 content of about 41.5 mol%, SrO content of about 22.5 mol...ternary, glasses that are needed for this program. These include the BaO- SiO2 system as an example binary glass , and the MgO-Al2O3- SiO2 and BaO-Al2O3... SiO2 systems as example ternary glasses (with the addition of a rare earth 16 resulting in a quaternary glass ). Complex ternary compositions were

Crystal Nucleation and Growth in Undercooled Melts of Pure Zr, Binary Zr-Based and Ternary Zr-Ni-Cu Glass-Forming Alloys

NASA Astrophysics Data System (ADS)

Herlach, Dieter M.; Kobold, Raphael; Klein, Stefan

2018-03-01

Glass formation of a liquid undercooled below its melting temperature requires the complete avoidance of crystal nucleation and subsequent crystal growth. Even though they are not part of the glass formation process, a detailed knowledge of both processes involved in crystallization is mandatory to determine the glass-forming ability of metals and metallic alloys. In the present work, methods of containerless processing of drops by electrostatic and electromagnetic levitation are applied to undercool metallic melts prior to solidification. Heterogeneous nucleation on crucible walls is completely avoided giving access to large undercoolings. A freely suspended drop offers the additional benefit of showing the rapid crystallization process of an undercooled melt in situ by proper diagnostic means. As a reference, crystal nucleation and dendrite growth in the undercooled melt of pure Zr are experimentally investigated. Equivalently, binary Zr-Cu, Zr-Ni and Zr-Pd and ternary Zr-Ni-Cu alloys are studied, whose glass-forming abilities differ. The experimental results are analyzed within classical nucleation theory and models of dendrite growth. The findings give detailed knowledge about the nucleation-undercooling statistics and the growth kinetics over a large range of undercooling.

White light emission of dysprosium doped lanthanum calcium phosphate oxide and oxyfluoride glasses

NASA Astrophysics Data System (ADS)

Luewarasirikul, N.; Kim, H. J.; Meejitpaisan, P.; Kaewkhao, J.

2017-04-01

Lanthanum calcium phosphate oxide and oxyfluoride glasses doped with dysprosium oxide were prepared by melt-quenching technique with chemical composition 20La2O3:10CaO:69P2O5:1Dy2O3 and 20La2O3:10CaF2:69P2O5:1Dy2O3. The physical, optical and luminescence properties of the glass samples were studied to evaluate their potential to using as luminescence materials for solid-state lighting applications. The density, molar volume and refractive index of the glass samples were carried out. The optical and luminescence properties were studied by investigating absorption, excitation, and emission spectra of the glass samples. The absorption spectra were investigated in the UV-Vis-NIR region from 300 to 2000 nm. The excitation spectra observed under 574 nm emission wavelength showed the highest peak centered at 349 nm (6H15/2 → 6P7/2). The emission spectra, excited with 349 nm excitation wavelength showed two major peaks corresponding to 482 nm blue emission (4F9/2 → 6H15/2) and 574 nm yellow emission (4F9/2 → 6H13/2). The experimental lifetime were found to be 0.539 and 0.540 for oxide and oxyfluoride glass sample, respectively. The x,y color coordinates under 349 nm excitation wavelength were (0.38, 0.43) for both glass samples, that be plotted in white region of CIE 1931 chromaticity diagram. The CCT values obtained from the glass samples are 4204 K for oxide glass and 4228 K for oxyfluoride glass corresponding to the commercial cool white light (3100-4500 K). Judd-Ofelt theory had also been employed to obtain the J-O parameters (Ω2, Ω4 and Ω6), oscillator strength, radiative transition possibility, stimulated emission cross section and branching ratio. The Ω2 > Ω4 > Ω6 trend of J-O parameters of both glass samples may indicate the good quality of a glass host for using as optical device application. Temperature dependence of emission spectra was studied from 300 K to 10 K and found that the intensity of the emission peak was found to be increased with decreasing of the temperature. The results of the investigations in this work confirmed that the present Dy-doped lanthanum calcium phosphate oxide and oxyfluoride glasses perform high potential for using as efficient luminescence materials for solid-state lighting applications, especially for white LEDs. Furthermore, the oxyfluoride glass sample provides more luminescence potential than the oxide glass sample.

Mixed polyanion glass cathodes: Glass-state conversion reactions

DOE PAGES

Kercher, Andrew K.; Kolopus, James A.; Carroll, Kyler; ...

2015-11-10

Mixed polyanion (MP) glasses can undergo glass-state conversion (GSC) reactions to provide an alternate class of high-capacity cathode materials. GSC reactions have been demonstrated in phosphate/vanadate glasses with Ag, Co, Cu, Fe, and Ni cations. These MP glasses provided high capacity and good high power performance, but suffer from moderate voltages, large voltage hysteresis, and significant capacity fade with cycling. Details of the GSC reaction have been revealed by x-ray absorption spectroscopy, electron microscopy, and energy dispersive x-ray spectroscopy of ex situ cathodes at key states of charge. Using the Open Quantum Materials Database (OQMD), a computational thermodynamic model hasmore » been developed to predict the near-equilibrium voltages of glass-state conversion reactions in MP glasses.« less

Effect of alkaline earth modifier on the optical and structural properties of Cu2+ doped phosphate glasses as a bandpass filter

NASA Astrophysics Data System (ADS)

Farouk, M.; Samir, A.; El Okr, M.

2018-02-01

Glasses of composition [16RO-3Al2O3sbnd 6CuOsbnd 20Na2Osbnd 55P2O5], where R is the alkaline earth (R = Mg, Ca, Sr and Ba mol. %), were prepared by conventional melt quenching technique. The glass samples were characterized by X-ray diffraction, infrared spectroscopy, and spectrophotometer. XRD patterns show no sharp peaks indicating the non-crystalline nature of the prepared glasses. The density and molar volume of the glass systems were determined in order to study their structures. These results revealed that addition of alkaline earth elements leads to the formation of non-bridging oxygens (NBOs) and expands (opens up) the structure. The infrared spectra were analyzed to quantify the present phosphate groups. The optical absorption spectra of Cu2+ ions show the characteristic broadband single of Cu2+ ions in octahedral symmetry. The band gap was estimated following two methodologies. The first method considers the band edge of the transmission, while the second approach relays on the estimated values of the optical constants. A decent agreement for the band gap values using the two methods was obtained.

Structural and luminescence studies of Ho{sup 3+}-doped zinc-aluminium-sodium-phosphate (ZANP) glasses

DOE Office of Scientific and Technical Information (OSTI.GOV)

Brahmachary, K.; Rajesh, D.; Ratnakaram, Y. C., E-mail: ratnakaramsvu@gmail.com

Trivalent holmium doped zinc-aluminium-sodium-phosphate (ZANP) glasses were prepared by conventional melt-quenching technique and characterized for their structural and luminescence properties. The amorphous nature, elemental analysis and thermal stability of the glasses were studied by using X-ray diffraction, energy dispersive spectrum and differential scanning calorimetry analysis, respectively. The absorption and fluorescence spectra have been recorded at room temperature. Based on the absorption spectra, the Judd-Ofelt parameters and radiative parameters such as spontaneous transition probabilities (A{sub R}), branching ratios (β{sub R}), radiative lifetimes (τ{sub R}) were calculated and discussed. From the emission spectra emission peak positions (λ{sub P}), effective bandwidths (Δλ{sub eff})more » and stimulated emission cross-sections (σ{sub P}) were calculated for the observed emission transitions,{sup 5}S{sub 2} ({sup 5}F{sub 4}→{sup 5}I{sub 8}) and {sup 5}F{sub 5}→{sup 5}I{sub 8} in all the glass samples. The stimulated emission cross-section is higher for ZANPHo10 glass matrix and so it may be useful for laser excitation.« less

Towards a selective adsorbent for arsenate and selenite in the presence of phosphate: Assessment of adsorption efficiency, mechanism, and binary separation factors of the chitosan-copper complex.

PubMed

Yamani, Jamila S; Lounsbury, Amanda W; Zimmerman, Julie B

2016-01-01

The potential for a chitosan-copper polymer complex to select for the target contaminants in the presence of their respective competitive ions was evaluated by synthesizing chitosan-copper beads (CCB) for the treatment of (arsenate:phosphate), (selenite:phosphate), and (selenate:sulfate). Based on work by Rhazi et al., copper (II) binds to the amine moiety on the chitosan backbone as a monodentate complex (Type I) and as a bidentate complex crosslinking two polymer chains (Type II), depending on pH and copper loading. In general, the Type I complex exists alone; however, beyond threshold conditions of pH 5.5 during synthesis and a copper loading of 0.25 mol Cu(II)/mol chitosan monomer, the Type I and Type II complexes coexist. Subsequent chelation of this chitosan-copper ligand to oxyanions results in enhanced and selective adsorption of the target contaminants in complex matrices with high background ion concentrations. With differing affinities for arsenate, selenite, and phosphate, the Type I complex favors phosphate chelation while the Type II complex favors arsenate chelation due to electrostatic considerations and selenite chelation due to steric effects. No trend was exhibited for the selenate:sulfate system possibly due to the high Ksp of the corresponding copper salts. Binary separation factors, α12, were calculated for the arsenate-phosphate and selenite-phosphate systems, supporting the mechanistic hypothesis. While, further research is needed to develop a synthesis method for the independent formation of the Type II complexes to select for target contaminants in complex matrices, this work can provide initial steps in the development of a selective adsorbent. Copyright © 2015 Elsevier Ltd. All rights reserved.

Optical studies on alkali-alkaline Dy3+-doped lead-alumino-boro-phosphate glasses for white LED's application

NASA Astrophysics Data System (ADS)

Joseph, P. Arun Jeganatha; Vinothini, J. Jemma; Maheshvaran, K.; Rayappan, I. Arul

2018-04-01

A new series 34B2O3+20NH4H2PO4+10Al2O3+10PbO+25MCO3+1Dy2O3, where (M= K2 and Mg) of Dy3+ doped lead-alumino-boro-phosphate glasses have been prepared by conventional melt quenching technique. The prepared glass samples were characterized through Optical absorption and photoluminescence spectra. The bonding parameter, Oscillator strength and Judd-Oflet (JO) parameter have been calculated and investigated through optical absorption spectra. The excitation and emission wavelength have been obtained through the photoluminescence spectra. The emission spectra exhibit two visible bands as 4F9/2→6H15/2 (Blue) and 4F9/2→6H13/2 (Yellow). Yellow to blue (Y/B) intensity ratio and chromaticity coordinates have been estimated for the stimulation of WLED applications.

Spontaneous and stimulated emission spectroscopy of a Nd(3+)-doped phosphate glass under wavelength selective pumping.

PubMed

Iparraguirre, I; Azkargorta, J; Balda, R; Venkata Krishnaiah, K; Jayasankar, C K; Al-Saleh, M; Fernández, J

2011-09-26

The influence of the host matrix on the spectroscopic and laser properties of Nd(3+) in a K-Ba-Al phosphate glass has been investigated as a function of rare-earth concentration. Site-selective time resolved laser spectroscopy and stimulated emission experiments under selective wavelength laser pumping show the existence of a very complex crystal field site distribution of Nd(3+) ions in this glass. The peak of the broad stimulated (4)F(3/2)→(4)I(11/2) emission shifts in a non monotonous way up to 3 nm as a function of the excitation wavelength. This behavior can be explained by the relatively moderate inter-site energy transfer among Nd(3+) ions found in this system and measured by using fluorescence line narrowing spectroscopy. The best slope efficiency obtained for the laser emission was 40%. © 2011 Optical Society of America

Investigation of the local environment of Eu3+ in a silicophosphate glass using site-selective spectroscopy and Molecular Dynamics simulations

NASA Astrophysics Data System (ADS)

Ben Slimen, F.; Haouari, M.; Ben Ouada, H.; Guichaoua, D.; Raso, P.; Bidault, X.; Turlier, J.; Gaumer, N.; Chaussedent, S.

2017-02-01

Silicophosphate glasses (SiO2-P2O5) doped with Eu3+ ions were synthesized by the sol-gel process. Optical properties of these glasses were investigated by means of emission spectra and lifetime measurements. The Fluorescence Line Narrowing (FLN) technique was also used to explore the local structure around the Eu3+ ions in this host and to understand the role of phosphate as a codopant. As it is the case for aluminum, the ability of phosphate to avoid the rare earth clustering was investigated, and the role of this codopant in modifying the local order around the rare earth ion was evidenced. The analysis of the FLN spectra and lifetime measurements is consistent with this interpretation. Molecular Dynamics simulations were performed to evaluate and confirm these structural features. Two classes of europium sites were distinguished in agreement with the experimental characterization.

SnO-containing oxide glasses emitting in 1.0–2.0 µm spectral range

NASA Astrophysics Data System (ADS)

Denker, B. I.; Galagan, B. I.; Sverchkov, S. E.; Dianov, E. M.

2018-06-01

Different SnO-containing oxide glasses with various net formers (silicate, phosphate, germanate, borate, and a number of mixed compositions) were investigated for the presence of near-infrared photoluminescence. It was found that SnO-containing silicate and germanate, and also a plurality of mixed glass compositions, exhibit wideband photoluminescence peaking at 1.5–1.6 µm and with lifetimes in the order of 100 µs. These glasses are interesting as promising active materials for widely tunable fiber lasers and wideband amplifiers.

Structure and properties of strontium-doped phosphate-based glasses

PubMed Central

Abou Neel, Ensanya A.; Chrzanowski, Wojciech; Pickup, David M.; O'Dell, Luke A.; Mordan, Nicola J.; Newport, Robert J.; Smith, Mark E.; Knowles, Jonathan C.

2008-01-01

Owing to similarity in both ionic size and polarity, strontium (Sr2+) is known to behave in a comparable way to calcium (Ca2+), and its role in bone metabolism has been well documented as both anti-resorptive and bone forming. In this study, novel quaternary strontium-doped phosphate-based glasses, containing 1, 3 and 5 mol% SrO, were synthesized and characterized. 31P magic angle spinning (MAS) nuclear magnetic resonance results showed that, as the Sr2+ content is increased in the glasses, there is a slight increase in disproportionation of Q2 phosphorus environments into Q1 and Q3 environments. Moreover, shortening and strengthening of the phosphorus to bridging oxygen distance occurred as obtained from FTIR. The general broadening of the spectral features with Sr2+ content is most probably due to the increased variation of the phosphate–cation bonding interactions caused by the introduction of the third cation. This increased disorder may be the cause of the increased degradation of the Sr-containing glasses relative to the Sr-free glass. As confirmed from elemental analysis, all Sr-containing glasses showed higher Na2O than expected and this also could be accounted for by the higher degradation of these glasses compared with Sr-free glasses. Measurements of surface free energy (SFE) showed that incorporation of strontium had no effect on SFE, and samples had relatively higher fractional polarity, which is not expected to promote high cell activity. From viability studies, however, the incorporation of Sr2+ showed better cellular response than Sr2+-free glasses, but still lower than the positive control. This unfavourable cellular response could be due to the high degradation nature of these glasses and not due to the presence of Sr2+. PMID:18826914

Mechanism for converting Al2O3-containing borate glass to hydroxyapatite in aqueous phosphate solution.

PubMed

Zhao, Di; Huang, Wenhai; Rahaman, Mohamed N; Day, Delbert E; Wang, Deping

2009-05-01

The effect of replacing varying amounts (0-2.5 mol.%) of B2O3 with Al2O3 in a borate glass on (1) the conversion of the glass to HA in an aqueous phosphate solution and (2) the compressive strength of the as-formed HA product was investigated. Samples of each glass (10 x 10 x 8 mm) were placed in 0.25 M K2HPO4 solution at 60 degrees C, and the conversion kinetics to HA were determined from the weight loss of the glass and the pH of the solution. The structure and composition of the solid reaction products were characterized using X-ray diffraction, Fourier transform infrared spectroscopy and scanning electron microscopy. While the conversion rate of the glass to HA decreased considerably with increasing Al2O3 content, the microstructure of the HA product became denser and the compressive strength of the HA product increased. The addition of SiO2 to the Al2O3-containing borate glass reversed the deterioration of the conversion rate, and produced a further improvement in the strength of the HA product. The compressive strength of the HA formed from the borate glass with 2.5 mol.% Al2O3 and 5 mol.% SiO2 was 11.1 +/- 0.2 MPa, which is equal to the highest strengths reported for trabecular bone. The results indicated that simultaneous additions of Al2O3 and SiO2 could be used to control the bioactivity of the borate glass and to enhance the mechanical strength of the HA product. Furthermore, the HA product formed from the glass containing both SiO2 and Al2O3 could be applied to bone repair.

Nd : glass rod laser with an output energy of 500 J

NASA Astrophysics Data System (ADS)

Shaykin, A. A.; Kuzmin, A. A.; Shaikin, I. A.; Burdonov, K. F.; Khazanov, E. A.

2016-04-01

The energy of two orthogonally polarised pulses injected into an available multistage amplifier based on neodymium phosphate glass rods was increased from 300 to 500 J (in both pulses). The second output pulse with an energy of 200 J will be used to pump an additional parametric amplifier of a petawatt laser.

Influence of europium (Eu3+) ions on the optical properties of lithium zinc phosphate glasses

NASA Astrophysics Data System (ADS)

Shwetha, M.; Eraiah, B.

2018-02-01

Europium doped lithium zinc phosphate glasses with composition xEu2O3-(15-x) Li2O-45ZnO-40P2O5 (where x=0, 0.1, 0.3 and 0.5 mol %) named as EP0, EP1, EP3 and EP5 respectively, are prepared by melt-quenching method and the influence of Eu3+ ions on physical and optical properties of these glasses has been studied. Optical properties were studied using optical absorption spectra which was recorded at room temperature in the UV-Visible region. Optical direct band gap and indirect band gap energies were measured and their values range from 3.167 to 4.23eV and 2.08 to 3.02eV, respectively. Refractive indices have been measured with respect to different concentration of europium ions. Fluorescence spectroscopy measurements have been performed by excitation in the UV-Visible range, which resulted in the significant fluorescence peaks. The luminescence color of the glass system is characterized using Commission International de l’Eclairage de France 1931 standards.

A study of the formation of amorphous calcium phosphate and hydroxyapatite on melt quenched Bioglass using surface sensitive shallow angle X-ray diffraction.

PubMed

Martin, R A; Twyman, H; Qiu, D; Knowles, J C; Newport, R J

2009-04-01

Melt quenched silicate glasses containing calcium, phosphorous and alkali metals have the ability to promote bone regeneration and to fuse to living bone. These glasses, including 45S5 Bioglass((R)) [(CaO)(26.9)(Na(2)O)(24.4)(SiO(2))(46.1)(P(2)O(5))(2.6)], are routinely used as clinical implants. Consequently there have been numerous studies on the structure of these glasses using conventional diffraction techniques. These studies have provided important information on the atomic structure of Bioglass((R)) but are of course intrinsically limited in the sense that they probe the bulk material and cannot be as sensitive to thin layers of near-surface dissolution/growth. The present study therefore uses surface sensitive shallow angle X-ray diffraction to study the formation of amorphous calcium phosphate and hydroxyapatite on Bioglass((R)) samples, pre-reacted in simulated body fluid (SBF). Unreacted Bioglass((R)) is dominated by a broad amorphous feature around 2.2 A(-1) which is characteristic of sodium calcium silicate glass. After reacting Bioglass((R)) in SBF a second broad amorphous feature evolves ~1.6 A(-1) which is attributed to amorphous calcium phosphate. This feature is evident for samples after only 4 h reacting in SBF and by 8 h the amorphous feature becomes comparable in magnitude to the background signal of the bulk Bioglass((R)). Bragg peaks characteristic of hydroxyapatite form after 1-3 days of reacting in SBF.

Phosphate base laser glasses

DOE Office of Scientific and Technical Information (OSTI.GOV)

Izumitani, T.; Tsuru, M.

1980-12-16

A phosphate base laser glass comprising 55-70% P2O5, 1-15% Al2O3, 0-25% Li2O, 0-25% Na2O, 0-8% K2O, the total proportion of Li2O, Na2O, and K2O being 10-25%, 0-15% BaO, 0-15% ZnO, 0-15% CaO , 0-15%, sro, 0-15% MgO, the total proportion of BaO, ZnO, CaO, SrO, and MgO being 5-15%, 0-5% Y2O3, 0-5% La2O3, 0-5% GeO2, 0-5% CeO2, 0-3% Nb2O5, 0-3% MnO2, 0-2% Ta2O5, 0-1% Sb2O3, and 0.01-5% Nd2O3, all % being mole %. The phosphate base laser glass of this invention has a high induced emission cross section, a low non-linear refractive index coefficient, and excellent acid resistance and divitrificationmore » resistance. By replacing partially or wholely one or more of LiO2, Na2O, K2O, BaO, ZnO, CaO, SrO, MgO or Al2O3 by LiF, NaF, KF , BaF2ZnF2, CaF2, SrF2, MgF2 or AlF3, respectively, the above properties of the laser glass are further improved.« less

Analyses of kinetic glass transition in short-range attractive colloids based on time-convolutionless mode-coupling theory.

PubMed

Narumi, Takayuki; Tokuyama, Michio

2017-03-01

For short-range attractive colloids, the phase diagram of the kinetic glass transition is studied by time-convolutionless mode-coupling theory (TMCT). Using numerical calculations, TMCT is shown to recover all the remarkable features predicted by the mode-coupling theory for attractive colloids: the glass-liquid-glass reentrant, the glass-glass transition, and the higher-order singularities. It is also demonstrated through the comparisons with the results of molecular dynamics for the binary attractive colloids that TMCT improves the critical values of the volume fraction. In addition, a schematic model of three control parameters is investigated analytically. It is thus confirmed that TMCT can describe the glass-glass transition and higher-order singularities even in such a schematic model.

Optical ridge waveguides in Er3+/Yb3+ co-doped phosphate glass produced by ion irradiation combined with femtosecond laser ablation for guided-wave green and red upconversion emissions

NASA Astrophysics Data System (ADS)

Chen, Chen; He, Ruiyun; Tan, Yang; Wang, Biao; Akhmadaliev, Shavkat; Zhou, Shengqiang; de Aldana, Javier R. Vázquez; Hu, Lili; Chen, Feng

2016-01-01

This work reports on the fabrication of ridge waveguides in Er3+/Yb3+ co-doped phosphate glass by the combination of femtosecond laser ablation and following swift carbon ion irradiation. The guiding properties of waveguides have been investigated at 633 and 1064 nm through end face coupling arrangement. The refractive index profile on the cross section of the waveguide has been constructed. The propagation losses can be reduced considerably after annealing treatment. Under the optical pump laser at 980 nm, the upconversion emission of both green and red fluorescence has been realized through the ridge waveguide structures.

Alkali-lead-iron phosphate glass and associated method

DOEpatents

Boatner, Lynn A.; Sales, Brian C.; Franco, Sofia C. S.

1994-01-01

A glass composition and method of preparation utilizes a mixture consisting of phosphorus oxide within the range of about 40 to 49 molar percent, lead oxide within the range of about 10 to 25 molar percent, iron oxide within the range of about 10 to 17 molar percent and an alkali oxide within the range of about 23 to 30 molar percent. The glass resulting from the melting and subsequent solidifying of the mixture possesses a high degree of durability and a coefficient of thermal expansion as high as that of any of a number of metals. Such features render this glass highly desirable in glass-to-metal seal applications.

European Conference on Thermophysical Properties (11th) Held on 13-16 June 1988, University of Umea, Sweden. Abstracts

DTIC Science & Technology

1988-06-16

University of Urnea 901 87 UMEA SWEDEN E Karawacki Dept of Physics 48 Chalmers Tekniska Hogskola 412 96 GOTEBORG SWEDEN S Klarsfeld Glass Properties...Saunders, Electrical Conductivity and Dielectric Constant of Samarium Phosphate Glasses © 0 Andersson, P Andersson, R G Ross & G Backstrcm. Thermophysical...delivers extinction coefficients of about 50 m-/kg for pure (conventional) glass fiber insulations. We have thoroughly studied the potentials for a

Study of structural, electrical, and dielectric properties of phosphate-borate glasses and glass-ceramics

NASA Astrophysics Data System (ADS)

Melo, B. M. G.; Graça, M. P. F.; Prezas, P. R.; Valente, M. A.; Almeida, A. F.; Freire, F. N. A.; Bih, L.

2016-08-01

In this work, phosphate-borate based glasses with molar composition 20.7P2O5-17.2Nb2O5-13.8WO3-34.5A2O-13.8B2O3, where A = Li, Na, and K, were prepared by the melt quenching technique. The as-prepared glasses were heat-treated in air at 800 °C for 4 h, which led to the formation of glass-ceramics. These high chemical and thermal stability glasses are good candidates for several applications such as fast ionic conductors, semiconductors, photonic materials, electrolytes, hermetic seals, rare-earth ion host solid lasers, and biomedical materials. The present work endorses the analysis of the electrical conductivity of the as-grown samples, and also the electrical, dielectric, and structural changes established by the heat-treatment process. The structure of the samples was analyzed using X-Ray powder Diffraction (XRD), Raman spectroscopy, and density measurements. Both XRD and Raman analysis confirmed crystals formation through the heat-treatment process. The electrical ac and dc conductivities, σac and σdc, respectively, and impedance spectroscopy measurements as function of the temperature, varying from 200 to 380 K, were investigated for the as-grown and heat-treated samples. The impedance spectroscopy was measured in the frequency range of 100 Hz-1 MHz.

Relaxation dynamics in a binary hard-ellipse liquid.

PubMed

Xu, Wen-Sheng; Sun, Zhao-Yan; An, Li-Jia

2015-01-21

Structural relaxation in binary hard spherical particles has been shown recently to exhibit a wealth of remarkable features when size disparity or mixture composition is varied. In this paper, we test whether or not similar dynamical phenomena occur in glassy systems composed of binary hard ellipses. We demonstrate via event-driven molecular dynamics simulation that a binary hard-ellipse mixture with an aspect ratio of two and moderate size disparity displays characteristic glassy dynamics upon increasing density in both the translational and the rotational degrees of freedom. The rotational glass transition density is found to be close to the translational one for the binary mixtures investigated. More importantly, we assess the influence of size disparity and mixture composition on the relaxation dynamics. We find that an increase of size disparity leads, both translationally and rotationally, to a speed up of the long-time dynamics in the supercooled regime so that both the translational and the rotational glass transition shift to higher densities. By increasing the number concentration of the small particles, the time evolution of both translational and rotational relaxation dynamics at high densities displays two qualitatively different scenarios, i.e., both the initial and the final part of the structural relaxation slow down for small size disparity, while the short-time dynamics still slows down but the final decay speeds up in the binary mixture with large size disparity. These findings are reminiscent of those observed in binary hard spherical particles. Therefore, our results suggest a universal mechanism for the influence of size disparity and mixture composition on the structural relaxation in both isotropic and anisotropic particle systems.

Photoluminescence quenching by OH in Er- and Pr-doped glasses for 1.5 and 1.3 μm optical amplifiers

NASA Astrophysics Data System (ADS)

Faber, Anne J.; Simons, Dennis R.; Yan, Yingchao; de Waal, Henk

1994-09-01

In this paper we report on the effect of hydroxyl (OH) groups on the photoluminescence in the near IR (1.5 and 1.3 micrometers ) in rare earth (Er, Pr)-doped glasses. The 1.5 micrometers emission of Er-doped phosphate glasses was studied, before and after a special heat treatment. The luminescent lifetime of the 1.5 micrometers emission increases substantially, typically from 3 ms up to 7.2 ms for a 2 mole% Er2O3-doped phosphate glass, due to the controlled heat treatment. The increase in lifetime is ascribed to a decrease in OH- concentration, which is confirmed by IR-absorption spectroscopy. The quenching by OH is described by a simplified quenching model, which predicts the 1.5 micrometers emission lifetime as a function of Er- concentration with the OH-concentration as parameter. It appears that the larger part of the OH groups is coupled to Er ions and thus acts as quenching center. Photoluminescence quenching by OH groups is also reported for the 1.3 micrometers emission of Pr in GeS2-glasses: In pure OH-free GeS2 glass the 1.3 micrometers emission lifetime is as high as 350 microsecond(s) , for a 400 ppm dopant level. In GeS2 glasses containing only small amounts of OH (approximately 100 ppm), this lifetime is less than 200 microsecond(s) . Both examples demonstrate that for the fabrication of efficient glass optical amplifiers at the telecommunication windows 1.3 and 1.5 micrometers , the OH-impurity level of the host glass must be kept as low as possible.

Novel resorbable glass-ceramic scaffolds for hard tissue engineering: from the parent phosphate glass to its bone-like macroporous derivatives.

PubMed

Bretcanu, Oana; Baino, Francesco; Verné, Enrica; Vitale-Brovarone, Chiara

2014-05-01

One of the major challenges of hard tissue engineering research focuses on the development of scaffolds that can match the mechanical properties of the host bone and resorb at the same rate as the bone is repaired. The aim of this work was the synthesis and characterization of a resorbable phosphate glass, as well as its application for the fabrication of three dimensional (3-D) scaffolds for bone regeneration. The glass microstructure and behaviour upon heating were analysed by X-ray diffraction, differential scanning calorimetry and hot stage microscopy. The glass solubility was investigated according to relevant ISO standards using distilled water, simulated body fluid (SBF) and Tris-HCl as testing media. The glass underwent progressive dissolution over time in all three media but the formation of a hydroxyapatite-like layer was also observed on the samples soaked in SBF and Tris-HCl, which demonstrated the bioactivity of the material. The glass powder was used to fabricate 3-D macroporous bone-like glass-ceramic scaffolds by adopting polyethylene particles as pore formers: during thermal treatment, the polymer additive was removed and the sintering of glass particles was allowed. The obtained scaffolds exhibited high porosity (87 vol.%) and compressive strength around 1.5 MPa. After soaking for 4 months in SBF, the scaffolds mass loss was 76 wt.% and the pH of the solution did not exceed the 7.55 value, thereby remaining in a physiological range. The produced scaffolds, being resorbable, bioactive, architecturally similar to trabecular bone and exhibiting interesting mechanical properties, can be proposed as promising candidates for bone repair applications.

Controlled delivery of antimicrobial gallium ions from phosphate-based glasses.

PubMed

Valappil, S P; Ready, D; Abou Neel, E A; Pickup, D M; O'Dell, L A; Chrzanowski, W; Pratten, J; Newport, R J; Smith, M E; Wilson, M; Knowles, J C

2009-05-01

Gallium-doped phosphate-based glasses (PBGs) have been recently shown to have antibacterial activity. However, the delivery of gallium ions from these glasses can be improved by altering the calcium ion concentration to control the degradation rate of the glasses. In the present study, the effect of increasing calcium content in novel gallium (Ga2O3)-doped PBGs on the susceptibility of Pseudomonas aeruginosa is examined. The lack of new antibiotics in development makes gallium-doped PBG potentially a highly promising new therapeutic agent. The results show that an increase in calcium content (14, 15 and 16 mol.% CaO) cause a decrease in degradation rate (17.6, 13.5 and 7.3 microg mm(-2) h(-1)), gallium ion release and antimicrobial activity against planktonic P. aeruginosa. The most potent glass composition (containing 14 mol.% CaO) was then evaluated for its ability to prevent the growth of biofilms of P. aeruginosa. Gallium release was found to reduce biofilm growth of P. aeruginosa with a maximum effect (0.86 log(10) CFU reduction compared to Ga2O3-free glasses) after 48 h. Analysis of the biofilms by confocal microscopy confirmed the anti-biofilm effect of these glasses as it showed both viable and non-viable bacteria on the glass surface. Results of the solubility and ion release studies show that this glass system is suitable for controlled delivery of Ga3+. 71Ga NMR and Ga K-edge XANES measurements indicate that the gallium is octahedrally coordinated by oxygen atoms in all samples. The results presented here suggest that PBGs may be useful in controlled drug delivery applications, to deliver gallium ions in order to prevent infections due to P. aeruginosa biofilms.

Effect of Boron Addition on the Thermal, Degradation, and Cytocompatibility Properties of Phosphate-Based Glasses

PubMed Central

Hasan, Muhammad S.; Parsons, Andrew J.; Furniss, David; Scotchford, Colin A.; Ahmed, Ifty; Rudd, Chris D.

2013-01-01

In this study eight different phosphate-based glass compositions were prepared by melt-quenching: four in the (P2O5)45-(CaO)16-(Na2O)15-x -(MgO)24-(B2O3)x system and four in the system (P2O5)50-(CaO)16-(Na2O)10-x-(MgO)24-(B2O3)x, where x = 0,1, 5 and 10 mol%. The effect of B2O3 addition on the thermal properties, density, molar volume, dissolution rates, and cytocompatibility were studied for both glass systems. Addition of B2O3 increased the glass transition (T g), crystallisation (T c), melting (T m), Liquidus (T L) and dilatometric softening (T d) temperature and molar volume (V m). The thermal expansion coefficient (α) and density (ρ) were seen to decrease. An assessment of the thermal stability of the glasses was made in terms of their processing window (crystallisation onset, T c,ons minus glass transition temperature, T g), and an increase in the processing window was observed with increasing B2O3 content. Degradation studies of the glasses revealed that the rates decreased with increasing B2O3 content and a decrease in degradation rates was also observed as the P2O5 content reduced from 50 to 45 mol%. MG63 osteoblast-like cells cultured in direct contact with the glass samples for 14 days revealed comparative data to the positive control for the cell metabolic activity, proliferation, ALP activity, and morphology for glasses containing up to 5 mol% of B2O3. PMID:23991425

Presence of global and local α-relaxations in an alkyl phosphate glass former

NASA Astrophysics Data System (ADS)

Wu, Tao; Jin, Xiao; Saini, Manoj K.; Liu, Ying Dan; Ngai, K. L.; Wang, Li-Min

2017-10-01

The dynamics of a molecular glass former, tributyl phosphate (TBP), with an alkyl phosphate structure (three alkyl branches emanating from a polar core of PO4) is studied in the supercooled regime by dielectric and thermal (or enthalpic) relaxations. The dielectric fragility index md and the stretching exponent βd of the Kohlrausch-Williams-Watts correlation function are determined. Analyses of the enthalpic relaxation data by the Tool-Narayanaswamy-Moynihan-Hodge formalism yield the enthalpic fragility index mH and stretching exponent βH. The large difference between the dielectric md and the enthalpic mH, as well as between βd and βH, is a remarkable finding. The differences are interpreted by the formation of molecular self-assemblies. The interpretation is supported by the quite comparable fragility determined by viscosity and the enthalpic relaxation. The Kirkwood factor calculated at low temperatures is also consistent with the interpretation. The results suggest that the enthalpic relaxation involving the motions of all parts of TBP is global, while the dielectric relaxation detects the local rotation, which might originate from the rotation of the dipole moment of the core. The presence of two structural α-relaxations, one global and one local, with a large difference in dynamics is revealed for the first time in a molecular glass former.

Luminescence in the fluoride-containing phosphate-based glasses: A possible origin of their high resistance to nanosecond pulse laser-induced damage

PubMed Central

Wang, Pengfei; Lu, Min; Gao, Fei; Guo, Haitao; Xu, Yantao; Hou, Chaoqi; Zhou, Zhiwei; Peng, Bo

2015-01-01

Fusion power offers the prospect of an almost inexhaustible source of energy for future generations. It was reported that fusion fuel gains exceeding unity on the National Ignition Facility (NIF) were achieved, but so far great deal of scientific and engineering challenges have to be overcome for realizing fusion power generation. There is a bottleneck for color-separation gratings in NIF and other similar inertial confinement fusion (ICF) lasers. Here we show a series of high performance phosphate-based glasses that can transmit the third harmonic frequency (3ω) laser light with high efficiency meanwhile filter the fundamental (1ω) and the second harmonic frequency (2ω) laser lights through direct absorption, and especially they exhibit excellent damage threshold induced by nanosecond pulse laser compared with that of the fused silica used in NIF. Yellowish-orange fluorescence emits during the laser-material interaction process, and it can be tailored through regulating the glass structure. Study on its structural origin suggests that the fluorescence emission is a key factor that conduces to the high laser-induced damage resistance of these glasses. The results also indicated the feasibility of utilizing these high performance glasses in novel color separation optics, allowing novel design for the final optics assembly in ICF lasers. PMID:25716328

Luminescence in the fluoride-containing phosphate-based glasses: a possible origin of their high resistance to nanosecond pulse laser-induced damage.

PubMed

Wang, Pengfei; Lu, Min; Gao, Fei; Guo, Haitao; Xu, Yantao; Hou, Chaoqi; Zhou, Zhiwei; Peng, Bo

2015-02-26

Fusion power offers the prospect of an almost inexhaustible source of energy for future generations. It was reported that fusion fuel gains exceeding unity on the National Ignition Facility (NIF) were achieved, but so far great deal of scientific and engineering challenges have to be overcome for realizing fusion power generation. There is a bottleneck for color-separation gratings in NIF and other similar inertial confinement fusion (ICF) lasers. Here we show a series of high performance phosphate-based glasses that can transmit the third harmonic frequency (3ω) laser light with high efficiency meanwhile filter the fundamental (1ω) and the second harmonic frequency (2ω) laser lights through direct absorption, and especially they exhibit excellent damage threshold induced by nanosecond pulse laser compared with that of the fused silica used in NIF. Yellowish-orange fluorescence emits during the laser-material interaction process, and it can be tailored through regulating the glass structure. Study on its structural origin suggests that the fluorescence emission is a key factor that conduces to the high laser-induced damage resistance of these glasses. The results also indicated the feasibility of utilizing these high performance glasses in novel color separation optics, allowing novel design for the final optics assembly in ICF lasers.

Chinese Journal of Lasers (Selected Articles),

DTIC Science & Technology

1986-04-22

properties We first investigated silicate based glasses, then the other inorganic glasses such as borate, phosphate, germanate. tellurate ...of the growth of high melting temperature I.~ oxides, several upward pulling single crystal furnaces with nigh precision mechanical movement and high...automatic electronic weighting systems, and programmable automatic movement correction systems. The reliability of most of these control systems

Enhanced phosphate selectivity from wastewater using copper-loaded chelating resin functionalized with polyethylenimine.

PubMed

An, Byungryul; Nam, Juhee; Choi, Jae-Woo; Hong, Seok-Won; Lee, Sang-Hyup

2013-11-01

In water and wastewater, phosphate is considered a critical contaminant due to cause algae blooms and eutrophication. To meet the stringent regulation of phosphate in water, a new commercial chelating resin functionalized with polyethylenimine was tested for phosphate removal by loading Cu(2+) and Fe(2+)/Fe(3+) to enhance selectivity for phosphate. Batch and column experiments showed that CR20-Cu exhibited high selectivity for phosphate over other strong anions such as sulfate. The average binary phosphate/nitrate and phosphate/sulfate factors for CR20-Cu were calculated to be 7.3 and 4.8, respectively, which were more than 0.97 and 0.22 for a commercial anion exchanger (AMP16). The optimal pH for the phosphate removal efficiency was determined to be 7. According to the fixed-bed column test, the breakthrough sequence for multiple ions was HPO4(2-)>SO4(2-)>NO3(-)>Cl(-). Saturated CR20-Cu can be regenerated using 4% NaCl at pH 7. More than 95% of the phosphate from CR20-Cu was recovered, and the phosphate uptake capacity for CR20-Cu was not reduced after 7 regeneration cycles. Copyright © 2013 Elsevier Inc. All rights reserved.

Ion transport mechanism in glasses: non-Arrhenius conductivity and nonuniversal features.

PubMed

Murugavel, S; Vaid, C; Bhadram, V S; Narayana, C

2010-10-28

In this article, we report non-Arrhenius behavior in the temperature-dependent dc conductivity of alkali ion conducting silicate glasses well below their glass transition temperature. In contrast to the several fast ion-conducting and binary potassium silicate glasses, these glasses show a positive deviation in the Arrhenius plot. The observed non-Arrhenius behavior is completely reproducible in nature even after prolonged annealing close to the glass transition temperature of the respective glass sample. These results are the manifestation of local structural changes of the silicate network with temperature and give rise to different local environments into which the alkali ions hop, revealed by in situ high-temperature Raman spectroscopy. Furthermore, the present study provides new insights into the strong link between the dynamics of the alkali ions and different sites associated with it in the glasses.

Liquid-glass transition in equilibrium

NASA Astrophysics Data System (ADS)

Parisi, G.; Seoane, B.

2014-02-01

We show in numerical simulations that a system of two coupled replicas of a binary mixture of hard spheres undergoes a phase transition in equilibrium at a density slightly smaller than the glass transition density for an unreplicated system. This result is in agreement with the theories that predict that such a transition is a precursor of the standard ideal glass transition. The critical properties are compatible with those of an Ising system. The relations of this approach to the conventional approach based on configurational entropy are briefly discussed.

An Assessment of Binary Metallic Glasses: Correlations Between Structure, Glass Forming Ability and Stability (Preprint)

DTIC Science & Technology

2009-04-01

Cu, germanium and tellurium ," J. Mat. Sci., vol. 9, pp. 707-717, 1974. [29] A. Inoue, T. Zhang, K. Kita, and T. Masumoto, "Mechanical strengths...Toribuchi, K. Aoki, and T. Masumoto, "Formation of La-M- Cu (M=Ca, Sr or Ba) amorphous alloys and their oxidization and superconductivity," Trans. JIM...structure of Pd- Ge alloys glasses by pulsed neutron total scattering," presented at Proc. 4 th International Conference on Rapidly Quenched Metals

Broad-spectrum neodymium-doped laser glasses for high-energy chirped-pulse amplification.

PubMed

Hays, Greg R; Gaul, Erhard W; Martinez, Mikael D; Ditmire, Todd

2007-07-20

We have investigated two novel laser glasses in an effort to generate high-energy, broad-spectrum pulses from a chirped-pulse amplification Nd:glass laser. Both glasses have significantly broader spectra (>38 nm FWHM) than currently available Nd:phosphate and Nd:silicate glasses. We present calculations for small signal pulse amplification to simulate spectral gain narrowing. The technique of spectral shaping using mixed-glass architecture with an optical parametric chirped-pulse amplification front end is evaluated. Our modeling shows that amplified pulses with energies exceeding 10 kJ with sufficient bandwidth to achieve 120 fs pulsewidths are achievable with the use of the new laser glasses. With further development of current technologies, a laser system could be scaled to generate one exawatt in peak power.

Thermal transport in binary colloidal glasses: Composition dependence and percolation assessment

NASA Astrophysics Data System (ADS)

Ruckdeschel, Pia; Philipp, Alexandra; Kopera, Bernd A. F.; Bitterlich, Flora; Dulle, Martin; Pech-May, Nelson W.; Retsch, Markus

2018-02-01

The combination of various types of materials is often used to create superior composites that outperform the pure phase components. For any rational design, the thermal conductivity of the composite as a function of the volume fraction of the filler component needs to be known. When approaching the nanoscale, the homogeneous mixture of various components poses an additional challenge. Here, we investigate binary nanocomposite materials based on polymer latex beads and hollow silica nanoparticles. These form randomly mixed colloidal glasses on a sub-μ m scale. We focus on the heat transport properties through such binary assembly structures. The thermal conductivity can be well described by the effective medium theory. However, film formation of the soft polymer component leads to phase segregation and a mismatch between existing mixing models. We confirm our experimental data by finite element modeling. This additionally allowed us to assess the onset of thermal transport percolation in such random particulate structures. Our study contributes to a better understanding of thermal transport through heterostructured particulate assemblies.

[Quantitative determination of glass content in monazite glass-ceramics by IR technique].

PubMed

He, Yong; Zhang, Bao-min

2003-04-01

Monazite glass-ceramics consist of both monazite and metaphoshate glass phases. The absorption bands of both phases do not overlap each other, and the absorption intensities of bands 1,275 and 616 cm-1 vary with the glass contents. The correlation coefficient between logarithmic absorbance ratio of the two bands and glass contents was r = 0.9975 and its regression equation was y = 48.356 + 25.93x. The absorbance ratio of bands 952 and 616 cm-1 also varied with different ratios of Ce2O3/La2O3 in synthetic monazites, with r = 0.9917 and a regression equation y = 0.2211 exp (0.0221x). High correlation coefficients show that the IR technique could find new application in the quantitative analysis of glass content in phosphate glass-ceramics.

Predict the glass transition temperature of glycerol-water binary cryoprotectant by molecular dynamic simulation.

PubMed

Li, Dai-Xi; Liu, Bao-Lin; Liu, Yi-shu; Chen, Cheng-lung

2008-04-01

Vitrification is proposed to be the best way for the cryopreservation of organs. The glass transition temperature (T(g)) of vitrification solutions is a critical parameter of fundamental importance for cryopreservation by vitrification. The instruments that can detect the thermodynamic, mechanical and dielectric changes of a substance may be used to determine the glass transition temperature. T(g) is usually measured by using differential scanning calorimetry (DSC). In this study, the T(g) of the glycerol-aqueous solution (60%, wt/%) was determined by isothermal-isobaric molecular dynamic simulation (NPT-MD). The software package Discover in Material Studio with the Polymer Consortium Force Field (PCFF) was used for the simulation. The state parameters of heat capacity at constant pressure (C(p)), density (rho), amorphous cell volume (V(cell)) and specific volume (V(specific)) and radial distribution function (rdf) were obtained by NPT-MD in the temperature range of 90-270K. These parameters showed a discontinuity at a specific temperature in the plot of state parameter versus temperature. The temperature at the discontinuity is taken as the simulated T(g) value for glycerol-water binary solution. The T(g) values determined by simulation method were compared with the values in the literatures. The simulation values of T(g) (160.06-167.51K) agree well with the DSC results (163.60-167.10K) and the DMA results (159.00K). We drew the conclusion that molecular dynamic simulation (MDS) is a potential method for investigating the glass transition temperature (T(g)) of glycerol-water binary cryoprotectants and may be used for other vitrification solutions.

Optical characterisation of hydroxide catalysed bonds applied to phosphate glass

NASA Astrophysics Data System (ADS)

Lacaille, Grégoire; Mangano, Valentina; van Veggel, Anna-Maria A.; Killow, Christian J.; MacKay, Peter E.; Rowan, Sheila; Hough, James

2017-10-01

We apply the Hydroxide Catalysis Bonding (HCB) technique to phosphate glass and measure the reflectivity and Light Induced Damage Threshold (LITD) of the newly formed interface. HCB is a room temperature, high performing process which was designed for astronomical research glass assemblies and played a key role in the detection of gravitational waves, a breakthrough in contemporary science. The bonds have numerous assets including mechanical strength, stability, no outgassing and resistance to contamination which are of high interest in the precision optics industry. However only little research has been done on their optical properties and mostly on silica based materials. In this paper, we use HCB to bond phosphate glass at room temperature with the goal of designing composite components for solid state laser gain media. We change the solution parameters to identify how they influence the final properties of the bonds: the LIDT at 1535 nm in long pulse regime and the reflectivity at 532 nm are investigated. The measurement of the incidence dependent reflectance allows estimating the thickness and refractive index of the bond in a non destructive process. The best performing set of parameters yields a LIDT of 1.6 GW/cm2 (16 J/cm2) and a reflectivity below 0.03 % which makes it suitable for use in high power lasers. The bond thickness is derived both from Scanning Electron Microscopy and the reflectivity measurements and is in the range of 50-150 nm depending on the parameters. Finally, the bonds survive cutting and polishing which is promising for manufacturing purpose.

Effects of Composites Containing Bioactive Glasses on Demineralized Dentin.

PubMed

Tezvergil-Mutluay, A; Seseogullari-Dirihan, R; Feitosa, V P; Cama, G; Brauer, D S; Sauro, S

2017-08-01

The aim of this study was to evaluate the degradation of completely demineralized dentin specimens in contact with a filler-free or 2 ion-releasing resins containing micrometer-sized particles of Bioglass 45S5 (BAG) or fluoride-containing phosphate-rich bioactive glass (BAG-F). Fourier transform infrared spectroscopy (FTIR) and scanning electron microscopy (SEM) were also used to evaluate the remineralization induced by the experimental ion-releasing resin-based materials. Dentin beams were totally demineralized in H 3 PO 4 (10%) and placed in direct contact with a filler-free (RESIN) or 2 experimental ion-releasing resins (BAG or BAG-F) and immersed in artificial saliva (AS) up to 30 d. Further specimens were also processed and submitted to FTIR and SEM analysis to evaluate the remineralization induced by such ion-releasing resins before and after AS immersion. BAG and BAG-F alkalinized the incubation media. A significant decrease of the dry mass was observed between the specimens of all groups stored for 3 and 30 d in AS. However, the fluoride-containing phosphate-rich bioactive glass incorporated into a resin-based material (BAG-F) showed greater ability in reducing the solubilization of C-terminal cross-linked telopeptide (ICTP) and C-terminal telopeptide (CTX) after prolonged AS storage. Moreover, after 30 d of AS storage, BAG-F showed the greatest remineralizing effect on the stiffness of the completely demineralized dentin matrices. In conclusion, fluoride-containing phosphate-rich bioactive glass incorporated as micrometer-sized filler in dental composites may offer greater beneficial effects than Bioglass 45S5 in reducing the enzyme-mediated degradation and remineralization of demineralized dentin.

An in vitro radiographic analysis of the density of dental luting cements as measured by CCD-based digital radiography.

PubMed

Antonijevic, Djordje; Jevremovic, Danimir; Jovanovic, Svetlana; Obradovic-Djuricic, Kosovka

2012-05-01

According to the ISO, the radiopacity of luting cements should be equal to or greater than that of aluminum. The aim of this in vitro study was to determine the radiopacity of 13 commercially available dental luting cements and compare them with human enamel and dentin. Five classes of luting cements were evaluated: zinc phosphate (Cegal N and Harvard Zinc Phosphate), zinc polycarboxylate (Harvard Polycarboxylate and Hoffmann's Carboxylate), glass ionomers (Ketac Cem Easymix, Ketac Cem Radiopaque, and Fuji I), resin-modified glass ionomer (Rely X Luting), and resin cements (Multilink Automix, Variolink II, Speed CEM, Rely X Unicem Automix, and three shades of Variolink Veneer). Tooth slices served as controls. Five specimens of each material measuring 8 mm in diameter and 1 mm thick were prepared and radiographed alongside tooth slices and an aluminum stepwedge using a Trophy RVG sensor. The radiopacity values were expressed in mm Al and analyzed by the ANOVA and Tukey tests (P < .05). All the cements examined except Variolink Veneer had significantly higher radiopacities than that of dentin. Rely X Unicem Automix, glass ionomer, and resin-modified glass-ionomer cements demonstrated radiopacities that were not significantly different with respect to enamel. Zinc phosphate, zinc polycarboxylate, and three of the resin cements presented radiopacity values that were significantly greater than that of enamel. Almost all the investigated materials presented an acceptable radiopacity. Radiopacity of dental cements seems to depend more on the presence of elements with high atomic numbers than on the type of the material.

Viscosity measurements of metallic melts using the oscillating drop technique

NASA Astrophysics Data System (ADS)

Heintzmann, P.; Yang, F.; Schneider, S.; Lohöfer, G.; Meyer, A.

2016-06-01

By means of benchmarking reduced gravity experiments, we have verified the measured viscosity of binary Zr-Ni glass forming liquids utilizing the oscillating drop technique combined with ground-based electrostatic levitation (ESL). Reliable viscosity data can be obtained as long as internal viscous damping of a single oscillation mode of a levitated drop dominates external perturbations. This can be verified by the absence of a sample mass dependence of the results. Hence, ESL is an excellent tool for studying the viscosity of metallic glass forming melts in the range of about 10-250 mPa s, with sample masses below 100 mg. To this end, we show that, for binary Zr-Ni melts, the viscosity is qualitatively controlled by the packing density.

Binary rare earth element-Ni/Co metallic glasses with distinct β-relaxation behaviors

DOE Office of Scientific and Technical Information (OSTI.GOV)

Zhu, Z. G.; Wang, Z.; Wang, W. H., E-mail: whw@iphy.ac.cn

2015-10-21

We report the formation of a series of rare earth element (RE)-Ni/Co binary metallic glasses (MGs) with unusual distinct β-relaxation peak compared with that of most of the reported MGs which usually exhibit as an excess wing or a shoulder. The β-relaxation behavior of RE-Ni/Co MGs is sensitive to the composition and the atomic radii of the RE and can be tuned through changing the fraction of RE-Ni (or Co) atomic pairs. The novel RE-Ni/Co MGs with distinct β-relaxation can serve as model system to investigate the nature of the β-relaxation as well as its relations with other physical andmore » mechanical properties of MGs.« less

Extremal Optimization for Quadratic Unconstrained Binary Problems

NASA Astrophysics Data System (ADS)

Boettcher, S.

We present an implementation of τ-EO for quadratic unconstrained binary optimization (QUBO) problems. To this end, we transform modify QUBO from its conventional Boolean presentation into a spin glass with a random external field on each site. These fields tend to be rather large compared to the typical coupling, presenting EO with a challenging two-scale problem, exploring smaller differences in couplings effectively while sufficiently aligning with those strong external fields. However, we also find a simple solution to that problem that indicates that those external fields apparently tilt the energy landscape to a such a degree such that global minima become more easy to find than those of spin glasses without (or very small) fields. We explore the impact of the weight distribution of the QUBO formulation in the operations research literature and analyze their meaning in a spin-glass language. This is significant because QUBO problems are considered among the main contenders for NP-hard problems that could be solved efficiently on a quantum computer such as D-Wave.

Alkali-lead-iron phosphate glass and associated method

DOEpatents

Boatner, L.A.; Sales, B.C.; Franco, S.C.S.

1994-03-29

A glass composition and method of preparation utilizes a mixture consisting of phosphorus oxide within the range of about 40 to 49 molar percent, lead oxide within the range of about 10 to 25 molar percent, iron oxide within the range of about 10 to 17 molar percent and an alkali oxide within the range of about 23 to 30 molar percent. The glass resulting from the melting and subsequent solidifying of the mixture possesses a high degree of durability and a coefficient of thermal expansion as high as that of any of a number of metals. Such features render this glass highly desirable in glass-to-metal seal applications. 6 figures.

Selenium semiconductor core optical fibers

DOE Office of Scientific and Technical Information (OSTI.GOV)

Tang, G. W.; Qian, Q., E-mail: qianqi@scut.edu.cn; Peng, K. L.

2015-02-15

Phosphate glass-clad optical fibers containing selenium (Se) semiconductor core were fabricated using a molten core method. The cores were found to be amorphous as evidenced by X-ray diffraction and corroborated by Micro-Raman spectrum. Elemental analysis across the core/clad interface suggests that there is some diffusion of about 3 wt % oxygen in the core region. Phosphate glass-clad crystalline selenium core optical fibers were obtained by a postdrawing annealing process. A two-cm-long crystalline selenium semiconductor core optical fibers, electrically contacted to external circuitry through the fiber end facets, exhibit a three times change in conductivity between dark and illuminated states. Suchmore » crystalline selenium semiconductor core optical fibers have promising utility in optical switch and photoconductivity of optical fiber array.« less

Gradient-index elements made from phosphate glasses in the system Al(PO3)3 - Na2O - Ag2O by ion-exchange process

NASA Astrophysics Data System (ADS)

Staronski, Leszek R.; Wychowaniec, Marek; Wasylak, Jan

1994-10-01

Silver aluminum phosphate glassed have been tested as a material for gradient index (GRIN) elements fabrication by exchange of Na+ ions from mixed molten salt baths by the Ag+ ones. The annealing technique was used to control the final gradient and GRIN rod elements with radial index profile were prepared with n(r) equals no(1 - A/2 (DOT) rn) where 2

Study of the thermal-optics parameters of Nd3+-doped phosphate glass as a function of temperature

NASA Astrophysics Data System (ADS)

Filho, J. C.; Pilla, V.; Messias, D. N.; Lourenço, S. A.; Silva, A. C. A.; Dantas, N. O.; Andrade, A. A.

2017-02-01

The spectroscopic properties of rare earth ions in many different hosts have been investigated, including surveys of Nd3+ in silicate, phosphate, fluorophosphates and fluoride glasses. Some of the thermal-optical properties of materials are influenced by temperature change, such as thermal diffusivity, specific heat and luminescence quantum efficiency. In this work the luminescence quantum efficiency of PANK: Nd3+, as a function of temperature (80- 480 K), was investigated using the normalized lifetime thermal lens technique. This system presents high quantum efficiency at low Nd3+ concentration and at ambient temperature, 100%, which decrease as temperature increase. Below room temperature the effects are not in accord with the maximum value of η, which must be unity.

Damage resistant optics for a mega-joule solid-state laser

NASA Astrophysics Data System (ADS)

Campbell, J. H.; Rainer, F.; Kozlowski, M. R.; Wolfe, C. R.; Thomas, I.; Milanovich, F.

1990-12-01

Research on Inertial Confinement Fusion (ICF) has progressed rapidly in the past several years. As a consequence, LLNL is developing plans to upgrade the current 120 kJ solid state (Nd3+ phosphate glass) Nova laser to a 1.5 to 2 megajoule system with the goal of achieving fusion ignition. The design of the planned Nova Upgrade is briefly discussed. Because of recent improvements in the damage resistance of optical materials it is now technically and economically feasible to build a megajoule-class solid state laser. Specifically, the damage threshold of Nd(+3)-doped phosphate laser glass, multilayer dielectric coatings, and non-linear optical crystals (e.g., KDP) have been dramatically improved. These materials now meet the fluence requirements for a 1.5 to 2 MJ Nd(+3)-glass laser operating at 1054 and 351 nm and at a pulse length of 3 ns. The recent improvements in damage thresholds are reviewed; threshold data at both 1064 and 355 nm and the measured pulse length scaling are presented.

Damage resistant optics for a megajoule solid state laser

NASA Astrophysics Data System (ADS)

Campbell, Jack H.; Rainer, Frank; Kozlowski, Mark R.; Wolfe, C. Robert; Thomas, Ian M.; Milanovich, Fred P.

1991-06-01

Research on Inertial Confinement Fusion (ICF) has progressed rapidly in the past several years. As a consequence LLNL is developing plans to upgrade the current 120 kJ solid state (Nd3-phosphate glass) Nova laser to a 1 . 5 to 2 megajoule system with the goal of achieving fusion ignition. The design of the planned Nova Upgrade is briefly discussed. Because of recent improvements in the damage resistance of optical materials it is now technically and economically feasible to build a megajoule-class solid state laser. Specifically the damage threshold of Nd3- doped phosphate laser glass muliilayer dielectric coatings and non-linear optical crystals (e. g. KDP) have been dramatically improved. These materials now meet the fluence requirements for a 1. 5-2 MJ Nd3-glass laser operating at 1054 and 351 nm and at a pulse length of 3 ns. The recent improvements in damage thresholds are reviewed threshold data at both 1064 and 355 nm and the measured pulse length scaling are presented. 1.

Composition formulas of Fe-based transition metals-metalloid bulk metallic glasses derived from dual-cluster model of binary eutectics.

PubMed

Naz, Gul Jabeen; Dong, Dandan; Geng, Yaoxiang; Wang, Yingmin; Dong, Chuang

2017-08-22

It is known that bulk metallic glasses follow simple composition formulas [cluster](glue atom) 1 or 3 with 24 valence electrons within the framework of the cluster-plus-glue-atom model. Though the relevant nearest-neighbor cluster can be readily identified from a devitrification phase, the glue atoms remains poorly defined. The present work is devoted to understanding the composition rule of Fe-(B,P,C) based multi-component bulk metallic glasses, by introducing a cluster-based eutectic liquid model. This model regards a eutectic liquid to be composed of two stable liquids formulated respectively by cluster formulas for ideal metallic glasses from the two eutectic phases. The dual cluster formulas are first established for binary Fe-(B,C,P) eutectics: [Fe-Fe 14 ]B 2 Fe + [B-B 2 Fe 8 ]Fe ≈ Fe 83.3 B 16.7 for eutectic Fe 83 B 17 , [P-Fe 14 ]P + [P-Fe 9 ]P 2 Fe≈Fe 82.8 P 17.2 for Fe 83 P 17 , and [C-Fe 6 ]Fe 3  + [C-Fe 9 ]C 2 Fe ≈ Fe 82.6 C 17.4 for Fe 82.7 C 17.3 . The second formulas in these dual-cluster formulas, being respectively relevant to devitrification phases Fe 2 B, Fe 3 P, and Fe 3 C, well explain the compositions of existing Fe-based transition metals-metalloid bulk metallic glasses. These formulas also satisfy the 24-electron rule. The proposition of the composition formulas for good glass formers, directly from known eutectic points, constitutes a new route towards understanding and eventual designing metallic glasses of high glass forming abilities.

Fragility, network adaptation, rigidity- and stress- transitions in homogenized binary GexS100-x glasses

NASA Astrophysics Data System (ADS)

Chakraborty, Shibalik; Boolchand, Punit

2014-03-01

Binary GexS100-x glasses reveal elastic and chemical phase transitions driven by network topology. With increasing Ge content x, well defined rigidity (xc(1) =19.3%) and stress(xc(2) =24.85%) transitions and associated optical elasticity power-laws are observed in Raman scattering. Calorimetric measurements reveal a square-well like minimum with window walls that coincide with the two elastic phase transitions. Molar volumes show a trapezoidal-like minimum with edges that nearly coincide with the reversibility window. These results are signatures of the isostatically rigid nature of the elastic phase formed between the rigidity and stress transitions. Complex Cp measurements show melt fragility index, m(x) to also show a global minimum in the reversibility window, underscoring that melt dynamics encode the elastic behavior of the glass formed at Tg. The strong nature of melts formed in the IP has an important practical consequence; they lead to slow homogenization of non-stoichiometric batch compositions reacted at high temperatures. Homogenization of chalcogenides melts/glasses over a scale of a few microns is a pre-requisite to observe the intrinsic physical properties of these materials. Supported by NSF Grant DMR 0853957.

New laser glass for short pulsed laser applications: the BLG80 (Conference Presentation)

NASA Astrophysics Data System (ADS)

George, Simi A.

2017-03-01

For achieving highest peak powers in a solid state laser (SSL) system, significant energy output and short pulses are necessary. For mode-locked lasers, it is well-known from the Fourier theorem that the largest gain bandwidths produce the narrowest pulse-widths; thus are transform limited. For an inhomogeneously broadened line width of a laser medium, if the intensity of pulses follow a Gaussian function, then the resulting mode-locked pulse will have a Gaussian shape with the emission bandwidth/pulse duration relationship of pulse ≥ 0.44?02/c. Thus, for high peak power SSL systems, laser designers incorporate gain materials capable of broad emission bandwidths. Available energy outputs from a phosphate glass host doped with rare-earth ions are unparalleled. Unfortunately, the emission bandwidths achievable from glass based gain materials are typically many factors smaller when compared to the Ti:Sapphire crystal. In order to overcome this limitation, a hybrid "mixed" laser glass amplifier - OPCPA approach was developed. The Texas petawatt laser that is currently in operation at the University of Texas-Austin and producing high peak powers uses this hybrid architecture. In this mixed-glass laser design, a phosphate and a silicate glass is used in series to achieve a broader bandwidth required before compression. Though proven, this technology is still insufficient for the future compact petawatt and exawatt systems capable of producing high energies and shorter pulse durations. New glasses with bandwidths that are two and three times larger than what is now available from glass hosts is needed if there is to be an alternative to Ti:Sapphire for laser designers. In this paper, we present new materials that may meet the necessary characteristics and demonstrate the laser and emission characteristics these through the internal and external studies.

Synthesis of Ag doped calcium phosphate particles and their antibacterial effect as additives in dental glass ionomer cements.

PubMed

Chen, Song; Gururaj, Satwik; Xia, Wei; Engqvist, Håkan

2016-11-01

Developing dental restorations with enhanced antibacterial properties has been a constant quest for materials scientists. The aim of this study was to synthesize silver doped calcium phosphate particles and use them to improve antibacterial properties of conventional glass ionomer cement. The Ag doped monetite (Ag-DCPA) and hydroxyapatite (Ag-HA) were synthesized by precipitation method and characterized using X-ray diffraction, scanning electron microscope and X-ray fluorescence spectroscopy. The antibacterial properties of the cements aged for 1 day and 7 days were evaluated by direct contact measurement using staphylococcus epidermis Xen 43. Ion concentrations (F - and Ag + ) and pH were measured to correlate to the results of the antibacterial study. The compressive strength of the cements was evaluated with a crosshead speed of 1 mm/min. The glass ionomer cements containing silver doped hydroxyapatite or monetite showed improved antibacterial properties. Addition of silver doped hydroxyapatite or monetite did not change the pH and ion release of F - . Concentration of Ag + was under the detection limit (0.001 mg/L) for all samples. Silver doped hydroxyapatite or monetite had no effect on the compressive strength of glass ionomer cement.

Luminescence performance of Eu{sup 3+} doped lead free zinc phosphate glasses for red emission

DOE Office of Scientific and Technical Information (OSTI.GOV)

Prasad, V. Reddy; Babu, S.; Ratnakaram, Y. C., E-mail: ratnakaramsvu@gmail.com

2016-05-06

Luminescence performance of zinc phosphate glasses containing Eu{sup 3+} ion with the chemical compositions (60-x)NH{sub 4}H{sub 2}PO{sub 4}-20ZnO-10BaF{sub 2}-10NaF-x Eu{sub 2}O{sub 3} (where x = 0.2, 0.5, 1.0 and 1.5 mol%) has been studied. The Fourier Transform Infrared Spectroscopy (FT-IR) shows several vibrations bands. Luminescence spectra of these glasses exhibit characteristic emission of Eu{sup 3+} ion with an intense and most prominent red emission (614 nm) which is attributed to {sup 5}D{sub 0}→{sup 7}F{sub 2} transition. Judd-Ofelt (Ω{sub 2}, Ω{sub 4}) parameters have been evaluated from the luminescence intensity ratios of {sup 5}D{sub 0}→{sup 7}F{sub J} (where J = 2 and 4)more » to {sup 5}D{sub 0}→{sup 7}F{sub 1} transition as well as absorption spectra under different constraints. Using J-O parameters and excitation spectra, the radiative parameters are calculated for different Eu{sup 3+} doped glasses.« less

Conversion of borate-based glass scaffold to hydroxyapatite in a dilute phosphate solution.

PubMed

Liu, Xin; Pan, Haobo; Fu, Hailuo; Fu, Qiang; Rahaman, Mohamed N; Huang, Wenhai

2010-02-01

Porous scaffolds of a borate-based glass (composition in mol%: 6Na2O, 8K2O, 8MgO, 22CaO, 36B2O3, 18SiO2, 2P2O5), with interconnected porosity of approximately 70% and pores of size 200-500 microm, were prepared by a polymer foam replication technique. The degradation of the scaffolds and conversion to a hydroxyapatite-type material in a 0.02 M K2HPO4 solution (starting pH = 7.0) at 37 degrees C were studied by measuring the weight loss of the scaffolds, as well as the pH and the boron concentration of the solution. X-ray diffraction, scanning electronic microscopy and energy dispersive x-ray analysis showed that a hydroxyapatite-type material was formed on the glass surface within 7 days of immersion in the phosphate solution. Cellular response to the scaffolds was assessed using murine MLO-A5 cells, an osteogenic cell line. Scanning electron microscopy showed that the scaffolds supported cell attachment and proliferation during the 6 day incubation. The results indicate that this borate-based glass could provide a promising degradable scaffold material for bone tissue engineering applications.

Femtosecond laser-induced refractive index modification in multicomponent glasses

NASA Astrophysics Data System (ADS)

Bhardwaj, V. R.; Simova, E.; Corkum, P. B.; Rayner, D. M.; Hnatovsky, C.; Taylor, R. S.; Schreder, B.; Kluge, M.; Zimmer, J.

2005-04-01

We present a comprehensive study on femtosecond laser-induced refractive index modification in a wide variety of multicomponent glasses grouped as borosilicate, aluminum-silicate, and heavy-metal oxide glasses along with lanthanum-borate and sodium-phosphate glasses. By using high-spatial resolution refractive index profiling techniques, we demonstrate that under a wide range of writing conditions the refractive index modification in multicomponent glasses can be positive, negative, or nonuniform, and exhibits a strong dependence on the glass composition. With the exception of some aluminum-silicate glasses all other glasses exhibited a negative/nonuniform index change. We also demonstrate direct writing of waveguides in photosensitive Foturan® glass with a femtosecond laser without initiating crystallization by thermal treatment. Upon ceramization of lithium-aluminum-silicate glasses such as Foturan®, Zerodur®, and Robax® we observe switching of laser-induced refractive index change from being positive to negative. The measured transmission losses in the waveguides at 1550nm agree with the index profile measurements in alkali-free aluminum-silicate glasses.

Study of structural, electrical, and dielectric properties of phosphate-borate glasses and glass-ceramics

DOE Office of Scientific and Technical Information (OSTI.GOV)

Melo, B. M. G.; Graça, M. P. F., E-mail: mpfg@ua.pt; Prezas, P. R.

2016-08-07

In this work, phosphate-borate based glasses with molar composition 20.7P{sub 2}O{sub 5}–17.2Nb{sub 2}O{sub 5}–13.8WO{sub 3}–34.5A{sub 2}O–13.8B{sub 2}O{sub 3}, where A = Li, Na, and K, were prepared by the melt quenching technique. The as-prepared glasses were heat-treated in air at 800 °C for 4 h, which led to the formation of glass-ceramics. These high chemical and thermal stability glasses are good candidates for several applications such as fast ionic conductors, semiconductors, photonic materials, electrolytes, hermetic seals, rare-earth ion host solid lasers, and biomedical materials. The present work endorses the analysis of the electrical conductivity of the as-grown samples, and also the electrical, dielectric,more » and structural changes established by the heat-treatment process. The structure of the samples was analyzed using X-Ray powder Diffraction (XRD), Raman spectroscopy, and density measurements. Both XRD and Raman analysis confirmed crystals formation through the heat-treatment process. The electrical ac and dc conductivities, σ{sub ac} and σ{sub dc}, respectively, and impedance spectroscopy measurements as function of the temperature, varying from 200 to 380 K, were investigated for the as-grown and heat-treated samples. The impedance spectroscopy was measured in the frequency range of 100 Hz–1 MHz.« less

Structural and luminescence studies on Dy3+ doped lead boro-telluro-phosphate glasses

NASA Astrophysics Data System (ADS)

Selvi, S.; Venkataiah, G.; Arunkumar, S.; Muralidharan, G.; Marimuthu, K.

2014-12-01

This paper reports results obtained on the structural and luminescence properties of Dy3+doped lead boro-telluro-phosphate glasses prepared following the melt quenching technique. FTIR spectra exhibit the presence of B-O vibrations, P-O-P symmetric vibrations and Te-O stretching modes of TeO3 and TeO6 units. The metal-ligand bond was identified through UV-vis-NIR absorption spectra and to determine the band tailing parameter, direct and indirect band gap energy of the prepared glasses. The Judd-Ofelt (JO) intensity parameters (Ω2, Ω4 and Ω6), experimental and theoretical oscillator strengths were also determined and reported. Luminescence measurements were made to determine the transition probability (A), stimulated emission cross-section (σPE) and branching ratio (βR) for the transitions that include 4F9/2→6H11/2, 6H13/2 and 6H15/2 bands. The effect of Dy3+ ion concentration on the intensity ratio of yellow to blue emission bands has also been studied and reported. The lifetime corresponding to the 4F9/2 level of the title glasses has been found to decrease with the increase in Dy3+ ion concentration. The chromaticity coordinates (x,y) have been estimated from the luminescence spectra and the suitability of title glasses for white light applications has been analyzed using CIE chromaticity diagram. The variation of optical properties with the concentration of dysprosium oxide content in the glasses have been studied and reported.

Lithium-aluminum-zinc phosphate glasses activated with Tb3+ and Tb3+/Eu3+ for green laser medium, reddish-orange and white phosphor applications

NASA Astrophysics Data System (ADS)

Francisco-Rodriguez, H. I.; Lira, A.; Soriano-Romero, O.; Meza-Rocha, A. N.; Bordignon, S.; Speghini, A.; Lozada-Morales, R.; Caldiño, U.

2018-05-01

A spectroscopic analysis of Tb3+ and Tb3+/Eu3+ doped lithium-aluminum-zinc phosphate glasses is performed through their absorbance and photoluminescence spectra, and decay time profiles. Laser parameter values (stimulated emission cross section, effective bandwidth, gain bandwidth and optical gain) were obtained for the terbium 5D4 → 7F5 green emission from the Tb3+ singly-doped glass (LAZT) excited at 350 nm to judge the suitability of the glass phosphor for fiber lasers. A quantum yield of (47.68 ± 0.49)% was measured for the 5D4 level luminescence. Upon 350 nm excitation the LAZT glass phosphor emits green light with a color purity of 65.6% and chromaticity coordinates (0.285, 0.585) very close to those (0.29, 0.60) of European Broadcasting Union illuminant green. The Tb3+/Eu3+codoped glass emission color can be tuned from reddish-orange of 1865 K upon 318 nm excitation to warm white of 3599 K and neutral white of 4049 K upon 359 and 340 nm excitations, respectively. Upon Tb3+ excitation at 340 nm Eu3+ is sensitized by Tb3+ through a non-radiative energy transfer with an efficiency of 0.23-0.26. An electric dipole-dipole interaction might be the dominant mechanism in the Tb3+ to Eu3+ energy transfer taking place into Tb3+ - Eu3+ clusters.

Cooling rate dependence of structural order in Al90Sm10 metallic glass

NASA Astrophysics Data System (ADS)

Sun, Yang; Zhang, Yue; Zhang, Feng; Ye, Zhuo; Ding, Zejun; Wang, Cai-Zhuang; Ho, Kai-Ming

2016-07-01

The atomic structure of Al90Sm10 metallic glass is studied using molecular dynamics simulations. By performing a long sub-Tg annealing, we developed a glass model closer to the experiments than the models prepared by continuous cooling. Using the cluster alignment method, we found that "3661" cluster is the dominating short-range order in the glass samples. The connection and arrangement of "3661" clusters, which define the medium-range order in the system, are enhanced significantly in the sub-Tg annealed sample as compared with the fast cooled glass samples. Unlike some strong binary glass formers such as Cu64.5Zr35.5, the clusters representing the short-range order do not form an interconnected interpenetrating network in Al90Sm10, which has only marginal glass formability.

A predictive structural model for bulk metallic glasses

PubMed Central

Laws, K. J.; Miracle, D. B.; Ferry, M.

2015-01-01

Great progress has been made in understanding the atomic structure of metallic glasses, but there is still no clear connection between atomic structure and glass-forming ability. Here we give new insights into perhaps the most important question in the field of amorphous metals: how can glass-forming ability be predicted from atomic structure? We give a new approach to modelling metallic glass atomic structures by solving three long-standing problems: we discover a new family of structural defects that discourage glass formation; we impose efficient local packing around all atoms simultaneously; and we enforce structural self-consistency. Fewer than a dozen binary structures satisfy these constraints, but extra degrees of freedom in structures with three or more different atom sizes significantly expand the number of relatively stable, ‘bulk' metallic glasses. The present work gives a new approach towards achieving the long-sought goal of a predictive capability for bulk metallic glasses. PMID:26370667

The roles of phosphate and tungstate species in surface acidities of TiO2-ZrO2 binary oxides - A comparison study

NASA Astrophysics Data System (ADS)

Chaudhary, Manchal; Shen, Po-fan; Chang, Sue-min

2018-05-01

Porous tungstated and phosphated TiO2-ZrO2 (TZ) binary oxides with high and strong acidity were successfully prepared by means of sol-gel or impregnation approaches. In addition, the influences of the two types of modifiers on the microstructures and acidity were systematically examined, compared, and clarified. The TZ oxide derived from a surfactant-templating method exhibited a high surface area of 195 m2/g with a pore size of 6.3 nm. Moreover, it had a high acidity of 859 μmol/g with a density of 4.4 μmol/nm2 because of defective surface. Phosphation significantly increased the acidity to 1547 μmol/g and showed the highest acid density of 6.7 μmol/nm2 at a surface P density of 22.7P/nm2. On the other hand, tungstated compounds just showed the highest acidity of 972 μmol/g and the highest acid density of 4.8 μmol/nm2 at 4.7 W/nm2. Compared to tungstate species, phosphate anions are more capable of promoting the acidity because they are able to distort the host network and inhibit elemental rearrangement. While Lewis acidity prevailed in the tungstated compounds, Brønsted acidity was dominant in the phosphated oxides. The Wdbnd O and Psbnd OH groups were responsible for strong acidity in the modified compounds. Phosphated compounds formed strong Brønsted acid sites on the Psbnd OH groups with a particular strength, and tungstation produced Lewis acid sites with a continuous strength on the metal ions adjacent to the tungstate moieties. Cyclic NH3 adsorption-desorption processes revealed that the active sites for NH3 adsorption were stable in both the tungstate and phosphate modified compounds, revealing that these solid acids are promising as the adsorbents for removal of base gases.

In vitro characterization of a novel polymeric system for preparation of amorphous solid drug dispersions.

PubMed

Mahmoudi, Zahra N; Upadhye, Sampada B; Ferrizzi, David; Rajabi-Siahboomi, Ali R

2014-07-01

Preparation of amorphous solid dispersions using polymers is a commonly used formulation strategy for enhancing the solubility of poorly water-soluble drugs. However, often a single polymer may not bring about a significant enhancement in solubility or amorphous stability of a poorly water-soluble drug. This study describes application of a unique and novel binary polymeric blend in preparation of solid dispersions. The objective of this study was to investigate amorphous solid dispersions of glipizide, a BCS class II model drug, in a binary polymeric system of polyvinyl acetate phthalate (PVAP) and hypromellose (hydroxypropyl methylcellulose, HPMC). The solid dispersions were prepared using two different solvent methods: rotary evaporation (rotavap) and fluid bed drug layering on sugar spheres. The performance and physical stability of the dispersions were evaluated with non-sink dissolution testing, powder X-ray diffraction (PXRD), and modulated differential scanning calorimetry (mDSC). PXRD analysis demonstrated an amorphous state for glipizide, and mDSC showed no evidence of phase separation. Non-sink dissolution testing in pH 7.5 phosphate buffer indicated more than twofold increase in apparent solubility of the drug with PVAP-HPMC system. The glipizide solid dispersions demonstrated a high glass transition temperature (Tg) and acceptable chemical and physical stability during the stability period irrespective of the manufacturing process. In conclusion, the polymeric blend of PVAP-HPMC offers a unique formulation approach for developing amorphous solid dispersions with the flexibility towards the use of these polymers in different ratios and combined quantities depending on drug properties.

Crack-resistant Al2O3-SiO2 glasses.

PubMed

Rosales-Sosa, Gustavo A; Masuno, Atsunobu; Higo, Yuji; Inoue, Hiroyuki

2016-04-07

Obtaining "hard" and "crack-resistant" glasses have always been of great important in glass science and glass technology. However, in most commercial glasses both properties are not compatible. In this work, colorless and transparent xAl2O3-(100-x)SiO2 glasses (30 ≤ x ≤ 60) were fabricated by the aerodynamic levitation technique. The elastic moduli and Vickers hardness monotonically increased with an increase in the atomic packing density as the Al2O3 content increased. Although a higher atomic packing density generally enhances crack formation in conventional oxide glasses, the indentation cracking resistance increased by approximately seven times with an increase in atomic packing density in binary Al2O3-SiO2 glasses. In particular, the composition of 60Al2O3 • 40SiO2 glass, which is identical to that of mullite, has extraordinary high cracking resistance with high elastic moduli and Vickers hardness. The results indicate that there exist aluminosilicate compositions that can produce hard and damage-tolerant glasses.

The Effect of Single, Binary and Ternary Anions of Chloride, Carbonate and Phosphate on the Release of 2,4-Dichlorophenoxyacetate Intercalated into the Zn-Al-layered Double Hydroxide Nanohybrid

NASA Astrophysics Data System (ADS)

Hussein, Mohd Zobir; Jaafar, Adila Mohamad; Yahaya, Asmah Hj.; Zainal, Zulkarnain

2009-11-01

Intercalation of beneficial anion into inorganic host has lead to an opportunity to synthesize various combinations of new organic-inorganic nanohybrids with various potential applications; especially, for the controlled release formulation and storage purposes. Investigation on the release behavior of 2,4-dichlorophenoxyacetate (2,4-D) intercalated into the interlayer of Zn-Al-layered double hydroxide (ZAN) have been carried out using single, binary and ternary aqueous systems of chloride, carbonate and phosphate. The release behavior of the active agent 2,4-D from its double-layered hydroxide nanohybrid ZANDI was found to be of controlled manner governed by pseudo-second order kinetics. It was found that carbonate medium yielded the highest accumulated release of 2,4-D, while phosphate in combination with carbonate and/or nitrate speeds up the release rate of 2,4-D. These results indicate that it is possible to design and develop new delivery system of latex stimulant compound with controlled release property based on 2,4-D that is known as a substance to increase latex production of rubber tree, Hevea brasiliensis.

A New Biocompatible and Antibacterial Phosphate Free Glass-Ceramic for Medical Applications

NASA Astrophysics Data System (ADS)

Cabal, Belén; Alou, Luís; Cafini, Fabio; Couceiro, Ramiro; Sevillano, David; Esteban-Tejeda, Leticia; Guitián, Francisco; Torrecillas, Ramón; Moya, José S.

2014-06-01

In the attempt to find valid alternatives to classic antibiotics and in view of current limitations in the efficacy of antimicrobial-coated or loaded biomaterials, this work is focused on the development of a new glass-ceramic with antibacterial performance together with safe biocompatibility. This bactericidal glass-ceramic composed of combeite and nepheline crystals in a residual glassy matrix has been obtained using an antimicrobial soda-lime glass as a precursor. Its inhibitory effects on bacterial growth and biofilm formation were proved against five biofilm-producing reference strains. The biocompatibility tests by using mesenchymal stem cells derived from human bone indicate an excellent biocompatibility.

A New Biocompatible and Antibacterial Phosphate Free Glass-Ceramic for Medical Applications

PubMed Central

Cabal, Belén; Alou, Luís; Cafini, Fabio; Couceiro, Ramiro; Sevillano, David; Esteban-Tejeda, Leticia; Guitián, Francisco; Torrecillas, Ramón; Moya, José S.

2014-01-01

In the attempt to find valid alternatives to classic antibiotics and in view of current limitations in the efficacy of antimicrobial-coated or loaded biomaterials, this work is focused on the development of a new glass-ceramic with antibacterial performance together with safe biocompatibility. This bactericidal glass-ceramic composed of combeite and nepheline crystals in a residual glassy matrix has been obtained using an antimicrobial soda-lime glass as a precursor. Its inhibitory effects on bacterial growth and biofilm formation were proved against five biofilm-producing reference strains. The biocompatibility tests by using mesenchymal stem cells derived from human bone indicate an excellent biocompatibility. PMID:24961911

Magnesium coated phosphate glass fibers for unidirectional reinforcement of polycaprolactone composites.

PubMed

Liu, Xiaoling; Grant, David M; Palmer, Graham; Parsons, Andrew J; Rudd, Chris D; Ahmed, Ifty

2015-10-01

Bioresorbable composites have shown much potential for bone repair applications, as they have the ability to degrade completely over time and their degradation and mechanical properties can be tailored to suit the end application. In this study, phosphate glass fiber (from the system 45% P2 O5-16% CaO-24% MgO-11% Na2 O-4% Fe2 O3 (given in mol%)) were used to reinforce polycaprolactone (PCL) with approximately 20% fiber volume fraction. The glass fiber surfaces were coated with magnesium (Mg) through magnetron sputtering to improve the fiber-matrix interfacial properties. The Mg coating provided a rough fiber surface (roughness (Ra) of about 44nm). Both noncoated and Mg-coated fiber-reinforced composites were assessed. The water uptake and mass loss properties for the composites were assessed in phosphate-buffered saline (PBS) at 37°C for up to 28 days, and ion release profiles were also investigated in both water and PBS media. Inhibition of media influx was observed for the Mg-coated composites. The composite mechanical properties were characterized on the basis of both tensile and flexural tests and their retention in PBS media at 37°C was also investigated. A higher retention of the mechanical properties was observed for the Mg-coated composites over the 28 days degradation period. © 2014 Wiley Periodicals, Inc.

Heat accumulation regime of femtosecond laser writing in fused silica and Nd:phosphate glass

NASA Astrophysics Data System (ADS)

Bukharin, M. A.; Khudyakov, D. V.; Vartapetov, S. K.

2015-04-01

We investigated refractive index induced by direct femtosecond laser writing inside fused silica and Nd:phosphate glass in heat accumulation regime. Spatial profile and magnitude of induced refractive index were investigated at various pulse repetition rates and translation velocities. It was shown that the magnitude of induced refractive index significantly rises with decreasing in time interval between successive laser pulses below the time for thermal diffusion. Going from nonthermal regime to heat accumulation regime, we achieved induced refractive index growth from 4 × 10-3 up to 6.5 × 10-3 in fused silica and from -6 × 10-3 to -9 × 10-3 in Nd:phosphate glass. Aspect ratio of treated area decreased from 2.1 down to less than 1.5 without correcting optical elements. It was shown that in heat accumulation regime, the treated area was surrounded by region of alternatively changed refractive index with significant magnitude up to -2 × 10-3. Wide regions of decreased refractive index enable fabrication of depressed cladding waveguides. We demonstrated low-loss (0.3 dB/cm) tubular waveguide inside fused silica. For orthogonal polarizations of guiding light, we achieved a small difference between losses as 0.1 dB/cm using highly symmetric written tracks forming the cladding. The desired structure was simulated with the beam propagation method, and the results were in good agreement with experiment data.

Ultrapure glass optical waveguide: Development in microgravity by the sol gel process

NASA Technical Reports Server (NTRS)

Mukherjee, S. P.; Debsikdar, J. C.; Beam, T.

1983-01-01

The sol-gel process for the preparation of homogeneous gels in three binary oxide systems was investigated. The glass forming ability of certain compositions in the selected oxide systems (SiO-GeO2, GeO2-PbO, and SiO2-TiO2) were studied based on their potential importance in the design of optical waveguide at longer wavelengths.

Optical Properties of Bismuth Tellurite Based Glass

PubMed Central

Oo, Hooi Ming; Mohamed-Kamari, Halimah; Wan-Yusoff, Wan Mohd Daud

2012-01-01

A series of binary tellurite based glasses (Bi2O3)x (TeO2)100−x was prepared by melt quenching method. The density, molar volume and refractive index increase when bismuth ions Bi3+ increase, this is due to the increased polarization of the ions Bi3+ and the enhanced formation of non-bridging oxygen (NBO). The Fourier transform infrared spectroscopy (FTIR) results show the bonding of the glass sample and the optical band gap, Eopt decreases while the refractive index increases when the ion Bi3+ content increases. PMID:22605999

There Is Still Room for Improvement: Presentation of a Neutral Borosilicate Glass with Improved Chemical Stability for Parenteral Packaging.

PubMed

Boltres, Bettine; Tratzky, Stephan; Kass, Christof; Eichholz, Rainer; Naß, Peter

2016-01-01

For pharmaceutical parenteral packaging the glass compositions have always been either Type I borosilicate or Type III soda-lime glass. As both the compositions and certain chemical and physical properties are mandated by international standards, there has not been room for any changes. However, by applying only minor adjustments, a borosilicate glass was developed that showed improved chemical stability. The chemical composition is still in the range of currently used borosilicate glasses, which makes it a Type I glass according to all current pharmacopeia. A study was performed on glass vials comparing the new glass with the standard FIOLAX(®) and two other publicly available glasses. In an extraction study with water at 121 °C the new glass showed the highest chemical stability with the lowest amount of extractables. In an accelerated ageing study, which was done with water, phosphate, and carbonate buffer at 40 °C for 12 months, the new glass also proved to have the lowest amount of leachables. In this article the new glass and the results from the studies are presented, showing the reader how much of an effect can be attained with only minor adjustments if the scientific fundamentals are clear. The pharmaceutical market has been quite constant and risk-oriented due to the high impact on the safety of the patient. As any change necessitates a complicated change process, this has, in consequence, lead the industry to resist changing the parenteral primary packaging material for decades. The main glasses have either been Type I borosilicate or Type III soda-lime glass. On the other hand, a combination of improved inspection systems and the development of more sensitive biologically based drugs has elevated the standards for parental packaging materials. For example, the measurement of extractables and leachables from the packaging material steadily came into focus. In this article, a new glass is presented that still belongs to the group of Type I borosilicate glasses according to all pharmacopeia. However, with some minor adjustments in the chemical composition it was possible to increase the chemical stability measurably. To prove this several studies were performed, of which the extraction study with water at 121 °C and the accelerated ageing study with water, phosphate, and carbonate buffer at 40 °C for 12 months are presented here. © PDA, Inc. 2016.

Laboratory strength of glass ionomer and zinc phosphate cements.

PubMed

Piwowarczyk, A; Ottl, P; Lauer, H C

2001-09-01

The present in vitro study examined 3 mechanical properties, namely compressive, flexural, and diametral tensile strength, of various commercially available cements and core materials as a function of time after mixing. The examined materials were 2 cermet cements (Ketac Silver [ESPE, Seefeld, Germany] and Chelon Silver [ESPE]), 1 metal-reinforced glass ionomer cement (Miracle Mix [GC Dental Industrial Corp, Tokyo, Japan]), 2 conventional glass ionomer cements (Ketac Bond [ESPE] and Ketac Cem [ESPE]), 1 standard cure zinc phosphate cement (Harvard Cement [Richter and Hoffmann, Berlin, Germany]), and 1 zinc phosphate cement with the addition of 30% silver amalgam alloy powder (Harvard Cement 70% with Dispersalloy 30% [Richter and Hoffmann/Johnson and Johnson, East Windsor, NJ]). Properties were measured using a universal testing machine at 15 minutes, 1 hour, and 24 hours after first mixing. Compressive strengths varied widely between the 3 times of measurement from 5.8 +/- 6.6 MPa for Ketac Cem to 144.3 +/- 10.2 MPa for Ketac Silver. Twenty-four hours after mixing, the Bonferroni test showed significant (p

Flowing Air-Water Cooled Slab Nd: Glass Laser

NASA Astrophysics Data System (ADS)

Lu, Baida; Cai, Bangwei; Liao, Y.; Xu, Shifa; Xin, Z.

1989-03-01

A zig-zag optical path slab geometry Nd: glass laser cooled through flowing air-water is developed by us. Theoretical studies on temperature distribution of slab and rod configurations in the unsteady state clarify the advantages of the slab geometry laser. The slab design and processing are also reported. In our experiments main laser output characteristics, e. g. laser efficiency, polarization, far-field divergence angle as well as resonator misalignment are investigated. The slab phosphate glass laser in combination with a crossed Porro-prism resonator demonstrates a good laser performance.

Transition and post-transition metal ions in borate glasses: Borate ligand speciation, cluster formation, and their effect on glass transition and mechanical properties.

PubMed

Möncke, D; Kamitsos, E I; Palles, D; Limbach, R; Winterstein-Beckmann, A; Honma, T; Yao, Z; Rouxel, T; Wondraczek, L

2016-09-28

A series of transition and post-transition metal ion (Mn, Cu, Zn, Pb, Bi) binary borate glasses was studied with special consideration of the cations impact on the borate structure, the cations cross-linking capacity, and more generally, structure-property correlations. Infrared (IR) and Raman spectroscopies were used for the structural characterization. These complementary techniques are sensitive to the short-range order as in the differentiation of tetrahedral and trigonal borate units or regarding the number of non-bridging oxygen ions per unit. Moreover, vibrational spectroscopy is also sensitive to the intermediate-range order and to the presence of superstructural units, such as rings and chains, or the combination of rings. In order to clarify band assignments for the various borate entities, examples are given from pure vitreous B 2 O 3 to meta-, pyro-, ortho-, and even overmodified borate glass compositions. For binary metaborate glasses, the impact of the modifier cation on the borate speciation is shown. High field strength cations such as Zn 2+ enhance the disproportionation of metaborate to polyborate and pyroborate units. Pb 2+ and Bi 3+ induce cluster formation, resulting in PbO n - and BiO n -pseudophases. Both lead and bismuth borate glasses show also a tendency to stabilize very large superstructural units in the form of diborate polyanions. Far-IR spectra reflect on the bonding states of modifier cations in glasses. The frequency of the measured cation-site vibration band was used to obtain the average force constant for the metal-oxygen bonding, F M-O . A linear correlation between glass transition temperature (T g ) and F M-O was shown for the metaborate glass series. The mechanical properties of the glasses also correlate with the force constant F M-O , though for cations of similar force constant the fraction of tetrahedral borate units (N 4 ) strongly affects the thermal and mechanical properties. For paramagnetic Cu- and Mn-borate glasses, N 4 was determined from the IR spectra after deducing the relative absorption coefficient of boron tetrahedral versus boron trigonal units, α = α 4 /α 3 , using NMR literature data of the diamagnetic glasses.

Laser characteristics at 1535 nm and thermal effects of an Er:Yb phosphate glass microchip pumped by Ti:sapphire laser

NASA Astrophysics Data System (ADS)

Cai, Zhiping; Chardon, Alain; Xu, Huiying; Féron, Patrice; Michel Stéphan, Guy

2002-03-01

An Er:Yb codoped phosphate glass microchip laser has been studied under pumping with a Ti:sapphire laser ranging from 945 to 990 nm. The characteristics (threshold, slope efficiency) are first described for an optimized laser. The gain spectrum is calculated for the transition 4I13/2→ 4I15/2 around 1535 nm from fundamental spectroscopic data and from experimental results. Red-shift effect on the frequency of a single mode is experimentally observed when the pump power is increased, originating from thermal effects. Temperature inside the microchip cavity and thermal expansion coefficient were determined by employing the intensity ratio of two green upconversion emission line centered at 530 and 554 nm, respectively, which quantitatively explain this red shift.

Retentive [correction of Preventive] efficacy of glass ionomer, zinc phosphate and zinc polycarboxylate luting cements in preformed stainless steel crowns: a comparative clinical study.

PubMed

Khinda, V I S; Grewal, N

2002-06-01

This study was undertaken to assess the efficacy of three luting cements, namely, glass ionomer, zinc phosphate and zinc polycarboxylate in retainng the preformed stainless steel crowns in-vivo. Twenty subjects, with an indication for restoration of three primary molars with stainless steel crowns, were selected. Sixty teeth were taken up for the study, and twenty crowns were cemented with each of the three luting cements. After an eight month follow up the crowns were assessed for their presence/ absence or "rocking". Statistical analysis was done using Chi-square test. The results have shown no significant difference in retentivity of stainless steel crowns with the use of either of the three luting agents.

Nd3+-doped soft glass double-clad fibers with a hexagonal inner cladding

NASA Astrophysics Data System (ADS)

Wang, Longfei; He, Dongbing; Hu, Lili; Chen, Danping

2015-04-01

The stack-and-draw technique was used to fabricate Nd3+-doped silicate and phosphate glass double-clad step-index fibers with a non-circular inner cladding. For the silicate fiber, a maximum output power of 7.7 W was obtained from a 94 cm fiber. An output power of 1.25 W was also realized with a short length fiber of 8 cm, confirming the application potential of this fiber in single frequency lasers and pulsed amplifiers where an efficient rare-earth-doped fiber with short length is desirable. For the phosphate fiber, a maximum output power of 2.78 W was obtained from a single-mode fiber with a core diameter of up to 35 μm.

Transmission performance analysis of WDM systems based on bismuth-doped phosphate glass fiber amplifiers

NASA Astrophysics Data System (ADS)

Ji, Jianhua; Huang, Qian; Wang, Ke; Xu, Ming; Jiang, Chun

2018-01-01

In this paper transmission performance of Allwave fiber WDM systems cascaded by bismuth-doped phosphate glass fiber amplifiers pumped by 808 nm lasers is analyzed for the first time, to the best of our knowledge. The rate and power propagation equations of a three-level system are used to model the signal amplification and noise figure in the doped fibers. The simulation results show that the channels in the 1460-1470 nm wavelength region in 32 × 40 Gbit/s WDM system with 10 nm channel space can reach a BER less than 1 × 10-9 with the transmission distance more than 600 km, but when the channel space is reduced to 1 nm, the performance of the system is degraded greatly.

On the structure and radiation chemistry of iron phosphate glasses: New insights from electron spin resonance, Mössbauer, and evolved-gas mass spectroscopy

NASA Astrophysics Data System (ADS)

Griscom, D. L.; Merzbacher, C. I.; Bibler, N. E.; Imagawa, H.; Uchiyama, S.; Namiki, A.; Marasinghe, G. K.; Mesko, M.; Karabulut, M.

1998-05-01

Several vitreous forms for immobilization of plutonium and/or high-level nuclear wastes have been surveyed by electron spin resonance (ESR) to gain insights into their atomic-scale structures and to look for signs of radiolytic decomposition resulting from exposures to γ-ray doses of 30 MGy. While preliminary results are reported for Defense Waste Processing Facility (DWPF) borosilicate compositions and an experimental lanthanum-silicate glass, this paper focusses primarily on a class of glasses containing 40-75 mol% P 2O 5 and up to 40 mol% Fe 2O 3. Each of the six diverse compositions investigated displayed characteristic ESR signals (not resembling those of the iron-containing phosphorus-free glasses) comprising combinations of an extremely broad "X resonance" and a narrow "Z resonance", both centered near g=2.00 and both displaying nearly perfect Lorentzian line shapes (peak-to-peak derivative widths ˜300-600 mT and ˜30 mT, respectively, at 300 K). The X-resonance intensities in the air-melted glasses correlated linearly with Fe:P ratio up to [Fe 2O 3]/[P 2O 5] ≈ 0.6, where intensity values ˜1 spin/phosphorus were reached. Mössbauer studies showed that the [Fe 3+]/[Fe] tot ratio could be varied from 0.82 to 0.49 by raising the melting temperature in air from 1150°C to 1450°C and/or by employing mildly reducing atmospheres. The combined X + Z-resonance intensities were reduced to zero for [Fe 3+]/[Fe] tot less than ˜0.6, leaving only a much weaker spectrum attributable to Fe 3+ ions. The X and Z ESR signals of the iron phosphate glasses resemble nothing else in the literature except the correspondingly denoted signals in an iron-free amorphous peroxyborate (APB) preparation. The X and Z resonances in the latter are deemed to arise from superoxide ions (O 2-) in the borate network and in a separated Na 2O 2 phase, respectively. An asymmetric Z resonance signal attributable to interstitial O 2- species was a radiation-induced manifestation in phosphate glass of composition 50P 2O 5-20Fe 2O 3-23Li 2O-7CeO 2. Irradiated and unirradiated samples of this same glass were studied by ESR isochronal annealing and differential thermal analysis, revealing a one-for-one conversion of X to Z upon partial crystallization near 670°C and a Z → X reconversion upon partial remelting near 970°C. Heating to 1070°C in dry Ar resulted in a weight loss of ˜5 wt%, while quadrupole mass spectrometry (QMS) during ramped heating to 1550°C at a pressure of 10 -5 Pa revealed the evolution of O 2 molecules with (radiation sensitive) ion-current peaks near 1170°C and 1350-1400°C. To account for the totality of these and other results, it is suggested that air-melted iron phosphate glasses may contain macroscopic numbers of superoxide ions as an intrinsic chemical feature of their as-quenched structures. A specific four-connected phosphorus-oxygen glass network incorporating O 2- ions is proposed.

Distinctly Different Glass Transition Behaviors of Trehalose Mixed with Na2HPO 4 or NaH 2PO 4: Evidence for its Molecular Origin.

PubMed

Weng, Lindong; Elliott, Gloria D

2015-07-01

The present study is aimed at understanding how the interactions between sugar molecules and phosphate ions affect the glass transition temperature of their mixtures, and the implications for pharmaceutical formulations. The glass transition temperature (Tg) and the α-relaxation temperature (Tα) of dehydrated trehalose/sodium phosphate mixtures (monobasic or dibasic) were determined by differential scanning calorimetry and dynamic mechanical analysis, respectively. Molecular dynamics simulations were also conducted to investigate the microscopic interactions between sugar molecules and phosphate ions. The hydrogen-bonding characteristics and the self-aggregation features of these mixtures were quantified and compared. Thermal analysis measurements demonstrated that the addition of NaH2PO4 decreased both the glass transition temperature and the α-relaxation temperature of the dehydrated trehalose/NaH2PO4 mixture compared to trehalose alone while both Tg and Tα were increased by adding Na2HPO4 to pure trehalose. The hydrogen-bonding interactions between trehalose and HPO4(2-) were found to be stronger than both the trehalose-trehalose hydrogen bonds and those formed between trehalose and H2PO4(-). The HPO4(2-) ions also aggregated into smaller clusters than H2PO4(-) ions. The trehalose/Na2HPO4 mixture yielded a higher T g than pure trehalose because marginally self-aggregated HPO4(2-) ions established a strengthened hydrogen-bonding network with trehalose molecules. In contrast H2PO4(-) ions served only as plasticizers, resulting in a lower Tg of the mixtures than trehalose alone, creating large-sized ionic pockets, weakening interactions, and disrupting the original hydrogen-bonding network amongst trehalose molecules.

Distinctly Different Glass Transition Behaviors of Trehalose Mixed with Na2HPO4 or NaH2PO4: Evidence for its Molecular Origin

PubMed Central

Weng, Lindong; Elliott, Gloria D.

2015-01-01

Purpose The present study is aimed at understanding how the interactions between sugar molecules and phosphate ions affect the glass transition temperature of their mixtures, and the implications for pharmaceutical formulations. Methods The glass transition temperature (Tg) and the α-relaxation temperature (Tα) of dehydrated trehalose/sodium phosphate mixtures (monobasic or dibasic) were determined by differential scanning calorimetry and dynamic mechanical analysis, respectively. Molecular dynamics simulations were also conducted to investigate the microscopic interactions between sugar molecules and phosphate ions. The hydrogen-bonding characteristics and the self-aggregation features of these mixtures were quantified and compared. Results Thermal analysis measurements demonstrated that the addition of NaH2PO4 decreased both the glass transition temperature and the α-relaxation temperature of the dehydrated trehalose/NaH2PO4 mixture compared to trehalose alone while both Tg and Tα were increased by adding Na2HPO4 to pure trehalose. The hydrogen-bonding interactions between trehalose and HPO42− were found to be stronger than both the trehalose-trehalose hydrogen bonds and those formed between trehalose and H2PO4−. The HPO42− ions also aggregated into smaller clusters than H2PO4− ions. Conclusions The trehalose/Na2HPO4 mixture yielded a higher Tg than pure trehalose because marginally self-aggregated HPO42− ions established a strengthened hydrogen-bonding network with trehalose molecules. In contrast H2PO4− ions served only as plasticizers, resulting in a lower Tg of the mixtures than trehalose alone, creating large-sized ionic pockets, weakening interactions, and disrupting the original hydrogen-bonding network amongst trehalose molecules. PMID:25537342

Influence of storage vial material on measurement of organophosphate flame retardant metabolites in urine.

PubMed

Carignan, Courtney C; Butt, Craig M; Stapleton, Heather M; Meeker, John D; Minguez-Alarcón, Lidia; Williams, Paige L; Hauser, Russ

2017-08-01

Use of organophosphate flame retardants (PFRs) has increased over the past decade with the phase out of polybrominated diphenyl ethers. Urinary metabolites of PFRs are used as biomarkers of exposure in epidemiologic research, which typically uses samples collected and stored in polypropylene plastic cryovials. However, a small study suggested that the storage vial material may influence reported concentrations. Therefore, we aimed to examine the influence of the storage vial material on analytical measurement of PFR urinary metabolites. Using urine samples collected from participants in the Environment and Reproductive Health (EARTH) Study, we analyzed the PFR metabolites in duplicate aliquots that were stored in glass and plastic vials (n = 31 pairs). Bis(1,3-dichloro-2-propyl) phosphate (BDCIPP), diphenyl phosphate (DPHP) and isopropyl-phenyl phenyl phosphate (ip-PPP) were detected in 98%, 97% and 87% of duplicates. We observed high correlations between glass-plastic duplicates for BDCIPP (r s  = 0.95), DPHP (r s  = 0.79) and ip-PPP (r s  = 0.82) (p < 0.0001). Urinary ip-PPP was an average of 0.04 ng/ml (p = 0.04) higher among samples stored in glass, with a mean relative difference of 14%. While this difference is statistically significant, it is small in magnitude. No differences were observed for BDCIPP or DPHP, however future research should seek to reduce the potential for type II error (false negatives). We conclude that storing urine samples in polypropylene plastic cryovials may result in slightly reduced concentrations of urinary ip-PPP relative to storage in glass vials and future research should seek to increase the sample size, reduce background variability and consider the material of the urine collection cup. Copyright © 2017 Elsevier Ltd. All rights reserved.

Effect of vital tooth bleaching on solubility and roughness of dental cements.

PubMed

Londono, Jimmy; Abreu, Amara; Nelson, Steve; Hernandez, Jorge; Torres, Carlos; Mettenburg, Donald; Looney, Stephen; Rueggeberg, Frederick

2009-09-01

Vital tooth bleaching may affect properties of dental cements used for fixed prostheses. The purpose of this study was to examine the effect of a combined in-office and at-home bleaching regimen on changes in surface roughness and depth loss of a variety of commercially available dental cements. Five cement classifications were tested: glass ionomer, resin-modified glass ionomer, resin,self-adhesive resin cement, and zinc phosphate. Cements were placed in multiple wells in plastic blocks. After setting,the surface profile of each block was determined, and average roughness and vertical height of cement surface from the specimen holder were recorded. Blocks were water stored (control) or subjected to in-office and at-home bleaching(n=12). Surfaces were rescanned and pre- and posttest parameter changes were calculated. Statistical analysis consisted of Mann-Whitney-Wilcoxon Rank Sum and Student t tests applied to control and bleaching parameterc hanges within the same cements. A family-wise alpha of .05 was maintained by using a Bonferroni-adjusted level of significance preset to .01 per test. Zinc phosphate showed the only significant depth increase (P=.004) from bleaching: 0.9 +/- 0.7 microm deeper than the water-control group. Only resin-modified glass ionomer showed a significant (P=.004) increase in roughness from bleaching; values increased by 0.05 +/- 0.03 microm over the water-control group. In-office and at-home bleaching significantly increased depth loss of zinc phosphate and increased resinmodified glass ionomer roughness. However, the absolute values of differences observed, as compared to the wateronly control, were considered to be clinically insignificant. (J Prosthet Dent 2009;102:148-154)

Cooling rate dependence of structural order in Al 90Sm 10 metallic glass

DOE Office of Scientific and Technical Information (OSTI.GOV)

Sun, Yang; Zhang, Yue; Zhang, Feng

2016-07-07

Here, the atomic structure of Al 90Sm 10 metallic glass is studied using molecular dynamics simulations. By performing a long sub-T g annealing, we developed a glass model closer to the experiments than the models prepared by continuous cooling. Using the cluster alignment method, we found that “3661” cluster is the dominating short-range order in the glass samples. The connection and arrangement of “3661” clusters, which define the medium-range order in the system, are enhanced significantly in the sub-T g annealed sample as compared with the fast cooled glass samples. Unlike some strong binary glass formers such as Cu 64.5Zrmore » 35.5, the clusters representing the short-range order do not form an interconnected interpenetrating network in Al 90Sm 10, which has only marginal glass formability.« less

Cooling rate dependence of structural order in Al{sub 90}Sm{sub 10} metallic glass

DOE Office of Scientific and Technical Information (OSTI.GOV)

Sun, Yang; Ames Laboratory, US Department of Energy, Ames, Iowa 50011; Zhang, Yue

2016-07-07

The atomic structure of Al{sub 90}Sm{sub 10} metallic glass is studied using molecular dynamics simulations. By performing a long sub-T{sub g} annealing, we developed a glass model closer to the experiments than the models prepared by continuous cooling. Using the cluster alignment method, we found that “3661” cluster is the dominating short-range order in the glass samples. The connection and arrangement of “3661” clusters, which define the medium-range order in the system, are enhanced significantly in the sub-T{sub g} annealed sample as compared with the fast cooled glass samples. Unlike some strong binary glass formers such as Cu{sub 64.5}Zr{sub 35.5},more » the clusters representing the short-range order do not form an interconnected interpenetrating network in Al{sub 90}Sm{sub 10,} which has only marginal glass formability.« less

Impact of vanadium ions in barium borate glass

NASA Astrophysics Data System (ADS)

Abdelghany, A. M.; Hammad, Ahmed H.

2015-02-01

Combined optical and infrared spectral measurements of prepared barium borate glasses containing different concentrations of V2O5 were carried out. Vanadium containing glasses exhibit extended UV-visible (UV/Vis.) bands when compared with base binary borate glass. UV/Vis. spectrum shows the presence of an unsymmetrical strong UV broad band centered at 214 nm attributed to the presence of unavoidable trace iron impurities within the raw materials used for the preparation of such glass. The calculated direct and indirect optical band gaps are found to decrease with increasing the vanadium content (2.9:137 for indirect and 3.99:2.01 for direct transition). This change was discussed in terms of structural changes in the glass network. Infrared absorption spectra of the glasses reveal the appearance of both triangular and tetrahedral borate units. Electron spin resonance analyses indicate the presence of unpaired species in sufficient quantity to be identified and to confirm the spectral data.

Modifier constraint in alkali borophosphate glasses using topological constraint theory

NASA Astrophysics Data System (ADS)

Li, Xiang; Zeng, Huidan; Jiang, Qi; Zhao, Donghui; Chen, Guorong; Wang, Zhaofeng; Sun, Luyi; Chen, Jianding

2016-12-01

In recent years, composition-dependent properties of glasses have been successfully predicted using the topological constraint theory. The constraints of the glass network are derived from two main parts: network formers and network modifiers. The constraints of the network formers can be calculated on the basis of the topological structure of the glass. However, the latter cannot be accurately calculated in this way, because of the existing of ionic bonds. In this paper, the constraints of the modifier ions in phosphate glasses were thoroughly investigated using the topological constraint theory. The results show that the constraints of the modifier ions are gradually increased with the addition of alkali oxides. Furthermore, an improved topological constraint theory for borophosphate glasses is proposed by taking the composition-dependent constraints of the network modifiers into consideration. The proposed theory is subsequently evaluated by analyzing the composition dependence of the glass transition temperature in alkali borophosphate glasses. This method is supposed to be extended to other similar glass systems containing alkali ions.

Low-temperature vibrational dynamics of fused silica and binary silicate glasses

NASA Astrophysics Data System (ADS)

Cai, Ling; Shi, Ying; Hrdina, Ken; Moore, Lisa; Wu, Jingshi; Daemen, Luke L.; Cheng, Yongqiang

2018-02-01

Inelastic neutron scattering was used to study the vibrational dynamics of fused silica and its mixed binary glasses that were doped with either TiO2 or K2O . The energy transfer was measured from zero to 180 meV where the so-called Boson peaks (BP) at low energy and molecular vibrations at high energy are included. Although most of the vibrational spectra at the high energy resemble those reported in earlier literature, a defect-mode-like peak is observed for the doped binary systems near 120 meV . At very low temperature, the BP intensity increases rapidly with temperature and then, at higher temperature, the peak intensity decreases. As a result, a maximum is observed in the temperature dependence of the BP intensity. This maximum was shown in all four samples, but the pure SiO2 sample shows the highest intensity peak and the lowest temperature for peak position. Broadband energy spectra reveal a shift of intensity from BP to the more localized modes at higher energy. Temperature evolution of BP and its relationship with heat conduction and thermal expansion are discussed.

Multilayer Choline Phosphate Molecule Modified Surface with Enhanced Cell Adhesion but Resistance to Protein Adsorption.

PubMed

Chen, Xingyu; Yang, Ming; Liu, Botao; Li, Zhiqiang; Tan, Hong; Li, Jianshu

2017-08-22

Choline phosphate (CP), which is a new zwitterionic molecule, and has the reverse order of phosphate choline (PC) and could bind to the cell membrane though the unique CP-PC interaction. Here we modified a glass surface with multilayer CP molecules using surface-initiated atom-transfer radical polymerization (SI-ATRP) and the ring-opening method. Polymeric brushes of (dimethylamino)ethyl methacrylate (DMAEMA) were synthesized by SI-ATRP from the glass surface. Then the grafted PDMAEMA brushes were used to introduce CP groups to fabricate the multilayer CP molecule modified surface. The protein adsorption experiment and cell culture test were used to evaluate the biocompatibility of the modified surfaces by using human umbilical veinendothelial cells (HUVECs). The protein adsorption results demonstrated that the multilayer CP molecule decorated surface could prevent the adsorption of fibrinogen and serum protein. The adhesion and proliferation of cells were improved significantly on the multilayer CP molecule modified surface. Therefore, the biocompatibility of the material surface could be improved by the modified multilayer CP molecule, which exhibits great potential for biomedical applications, e.g., scaffolds in tissue engineering.

Biocorrosion Evaluation on a Zr-Cu-Ag-Ti Metallic Glass

NASA Astrophysics Data System (ADS)

Kumar, Shresh; Anwar, Rebin; Ryu, Wookha; Park, E. S.; Vincent, S.

2018-04-01

Metallic glasses are in high demand for fabrication of variety of innovative products, in particular surgical and biomedical tools and devices owing to its excellent biocompatible properties. In the present investigation, a novel Zr39.5Cu50.5Ag4Ti6 metallic glass composition was synthesized using melt spinning technique. Potentiodynamic polarization studies were conducted to investigate bio-corrosion behaviour of Zr39.5Cu50.5Ag4Ti6 metallic glass. The test were conducted in various simulated artificial body conditions such as artificial saliva solution, phosphate-buffered saline solution, artificial blood plasma solution, and Hank’s balanced saline solution. The bio-corrosion results of metallic glass were compared with traditional biomaterials. The study aims to provide bio-compatible properties of Zr39.5Cu50.5Ag4Ti6 metallic glass.

Doped Calcium Silicate Ceramics: A New Class of Candidates for Synthetic Bone Substitutes

PubMed Central

No, Young Jung; Li, Jiao Jiao; Zreiqat, Hala

2017-01-01

Doped calcium silicate ceramics (DCSCs) have recently gained immense interest as a new class of candidates for the treatment of bone defects. Although calcium phosphates and bioactive glasses have remained the mainstream of ceramic bone substitutes, their clinical use is limited by suboptimal mechanical properties. DCSCs are a class of calcium silicate ceramics which are developed through the ionic substitution of calcium ions, the incorporation of metal oxides into the base binary xCaO–ySiO2 system, or a combination of both. Due to their unique compositions and ability to release bioactive ions, DCSCs exhibit enhanced mechanical and biological properties. Such characteristics offer significant advantages over existing ceramic bone substitutes, and underline the future potential of adopting DCSCs for clinical use in bone reconstruction to produce improved outcomes. This review will discuss the effects of different dopant elements and oxides on the characteristics of DCSCs for applications in bone repair, including mechanical properties, degradation and ion release characteristics, radiopacity, and biological activity (in vitro and in vivo). Recent advances in the development of DCSCs for broader clinical applications will also be discussed, including DCSC composites, coated DCSC scaffolds and DCSC-coated metal implants. PMID:28772513

EPR, optical absorption and luminescence studies of Cr3+-doped antimony phosphate glasses

NASA Astrophysics Data System (ADS)

De Vicente, F. S.; Santos, F. A.; Simões, B. S.; Dias, S. T.; Siu Li, M.

2014-12-01

Antimony phosphate glasses (SbPO) doped with 3 and 6 mol% of Cr3+ were studied by Electron Paramagnetic Resonance (EPR), UV-VIS optical absorption and luminescence spectroscopy. The EPR spectra of Cr3+-doped glasses showed two principal resonance signals with effective g values at g = 5.11 and g = 1.97. UV-VIS optical absorption spectra of SbPO:Cr3+ presented four characteristics bands at 457, 641, 675, and 705 nm related to the transitions from 4A2(F) to 4T1(F), 4T2(F), 2T1(G), and 2E(G), respectively, of Cr3+ ions in octahedral symmetry. Optical absorption spectra of SbPO:Cr3+ allowed evaluating the crystalline field Dq, Racah parameters (B and C) and Dq/B. The calculated value of Dq/B = 2.48 indicates that Cr3+ ions in SbPO glasses are in strong ligand field sites. The optical band gap for SbPO and SbPO:Cr3+ were evaluated from the UV optical absorption edges. Luminescence measurements of pure and Cr3+-doped glasses excited with 350 nm revealed weak emission bands from 400 to 600 nm due to the 3P1 → 1S0 electronic transition from Sb3+ ions. Cr3+-doped glasses excited with 415 nm presented Cr3+ characteristic luminescence spectra composed by two broad bands, one band centered at 645 nm (2E → 4A2) and another intense band from 700 to 850 nm (4T2 → 4A2).

Network-Forming Nanoclusters in Binary As-S/Se Glasses: From Ab Initio Quantum Chemical Modeling to Experimental Evidences.

PubMed

Hyla, M

2017-12-01

Network-forming As 2 (S/Se) m nanoclusters are employed to recognize expected variations in a vicinity of some remarkable compositions in binary As-Se/S glassy systems accepted as signatures of optimally constrained intermediate topological phases in earlier temperature-modulated differential scanning calorimetry experiments. The ab initio quantum chemical calculations performed using the cation-interlinking network cluster approach show similar oscillating character in tendency to local chemical decomposition but obvious step-like behavior in preference to global phase separation on boundary chemical compounds (pure chalcogen and stoichiometric arsenic chalcogenides). The onsets of stability are defined for chalcogen-rich glasses, these being connected with As 2 Se 5 (Z = 2.29) and As 2 S 6 (Z = 2.25) nanoclusters for As-Se and As-S glasses, respectively. The physical aging effects result preferentially from global phase separation in As-S glass system due to high localization of covalent bonding and local demixing on neighboring As 2 Se m+1 and As 2 Se m-1 nanoclusters in As-Se system. These nanoclusters well explain the lower limits of reversibility windows in temperature-modulated differential scanning calorimetry, but they cannot be accepted as signatures of topological phase transitions in respect to the rigidity theory.

Complex magnetic behaviour and evidence of a superspin glass state in the binary intermetallic compound Er5Pd2

NASA Astrophysics Data System (ADS)

Sharma, Mohit K.; Yadav, Kavita; Mukherjee, K.

2018-05-01

The binary intermetallic compound Er5Pd2 has been investigated using dc and ac magnetic susceptibilities, magnetic memory effect, isothermal magnetization, non-linear dc susceptibility, heat capacity and magnetocaloric effect studies. Interestingly, even though the compound does not show geometrical frustration it undergoes glassy magnetic phase transition below 17.2 K. Investigation of dc magnetization and heat capacity data divulged absence of long-ranged magnetic ordering. Through the magnetic memory effect, time dependent magnetization and ac susceptibility studies it was revealed that the compound undergoes glass-like freezing below 17.2 K. Analysis of frequency dependence of this transition temperature through scaling and Arrhenius law; along with the Mydosh parameter indicate, that the dynamics in Er5Pd2 are due to the presence of strongly interacting superspins rather than individual spins. This phase transition was further investigated by non-linear dc susceptibility and was characterized by static critical exponents γ and δ. Our results indicate that this compound shows the signature of superspin glass at low temperature. Additionally, both conventional and inverse magnetocaloric effect was observed with a large value of magnetic entropy change and relative cooling power. Our results suggest that Er5Pd2 can be classified as a superspin glass system with large magnetocaloric effect.

Photon Dosimetry by Luminescence Methods

ERIC Educational Resources Information Center

Raeside, D. E.

1973-01-01

Discusses the fundamentals of two personnel dosimeters: the lithium fluoride thermoluminescent dosimeter and the silver-activated phosphate glass radiophotoluminescent dosimeter, and indicates the usefulness of this presentation for both teachers and students. (CC)

In vitro microleakage of luting cements and crown foundation material.

PubMed

Lindquist, T J; Connolly, J

2001-03-01

Microleakage is a concern for the long-term prognosis of a cemented crown and foundation. The aims of this investigation were, first, to evaluate microleakage of zinc phosphate cement and resin-reinforced glass ionomer cement under ideal (dry) versus contaminated (wet) conditions, and second, to compare 3 foundations under both ideal and contaminated conditions. One hundred forty extracted molar teeth were cleaned and mounted. Tooth preparations for complete veneer cast crowns were completed with a chamfer finish line. A mesial surface class II cavity preparation 4 mm wide buccolingually and 2 mm deep was made in each tooth. Seven restorative groups were formed: amalgam/cavity varnish, amalgam/dentinal bonding agent, and composite/dentinal bonding agent, each with dry and contaminated groups, and a seventh group of class II cavity preparations without foundations. Finish lines for crown margins were refined 1.5 mm gingival to the restoration. Artificial crowns were cast in type III gold. Treatment groups were divided into 4 cement groups: dry and contaminated zinc phosphate cement and dry and contaminated resin-reinforced glass ionomer cement. The specimens were thermocycled and immersed in erythrosine B solution for 24 hours. Subsequently, they were rinsed, and their coronal portions were embedded in clear resin. Teeth were sectioned mesiodistally, and standard photomicrographs were made. The microleakage of each restoration and crown was measured. The least foundation microleakage was recorded for amalgam/dentinal bonding agents (ideal group) and composite/dentinal bonding agents (ideal group). The most microleakage was observed within the group without a foundation. In cement groups, the control and experiment sides were evaluated separately but displayed the same order of finding. The least leakage was recorded with resin-reinforced glass ionomer cement (ideal group); the most microleakage was noted with zinc phosphate cement (ideal group). An interaction was demonstrated on the experimental side between cements and the foundations (P=.0001). Within the experimental conditions of this study, less microleakage was recorded with resin-reinforced glass ionomer cement (ideal or contaminated) than with zinc phosphate cement (ideal or contaminated). There also was less microleakage evident with a foundation of silver amalgam or composite when a dentinal bonding agent was used under ideal conditions.

Perfluorooctane sulfonate adsorption on powder activated carbon: Effect of phosphate (P) competition, pH, and temperature.

PubMed

Qian, Jin; Shen, Mengmeng; Wang, Peifang; Wang, Chao; Li, Kun; Liu, Jingjing; Lu, Bianhe; Tian, Xin

2017-09-01

Powdered activated carbon (PAC), as an adsorbent, was applied to remove perfluorooctane sulfonate (PFOS) from aqueous solution. Laboratory batch experiments were performed to investigate the influences of phosphate (P) competition, temperature, and pH for PFOS adsorption onto PAC. The results showed that higher temperature favored PFOS adsorption in single and binary systems. The kinetic data fitted very well to the pseudo second-order kinetic model. Thermodynamically, the endothermic enthalpy of the PFOS adsorption in single and binary systems were 125.07 and 21.25 kJ mol -1 , respectively. The entropy of the PFOS adsorption in single and binary systems were 0.479 and 0.092 kJ mol -1  K -1 , respectively. And the Gibbs constants were negative. These results indicated that the adsorption processes were spontaneous. The adsorption isotherms of PFOS agreed well with the Langmuir model. In the single system, PFOS adsorption decreased with increased pH value. The difference in the amount of PFOS adsorption between the single and binary systems increased at higher pH. Frustrated total internal reflection (FTIR) demonstrated that P competition increased the hydrophilicity of the PAC and the electrostatic repulsion between PFOS and PAC, then the PFOS adsorption amount decreased. It also demonstrated that, at higher temperature, increased PFOS adsorption was mainly due to the higher diffusion rate of PFOS molecules and greater number of active sites opened on the PAC surface. Copyright © 2017 Elsevier Ltd. All rights reserved.

Extended Abstracts. International Symposium on Halide Glasses (2nd), Rensselaer Polytechnic Institute, Troy, New York, USA, 2-5 August 1983.

DTIC Science & Technology

1983-08-02

Research and Development in ’" T. Miyashita and i.. . nabe 34 "Environmental Effects on the Strength of Fluoride Glass Fibers" A. Nakata, J. Lau, and J...continuous optical window. Ujnfortunately YVP3 ony permit’s thin samiples (1 mm) to be synthesized. Vitrco&us domnain ina the ternary sys ~tem TIT "Zni - YbF 4...synthesis methods, quenched glasses have been obtained in the CdF2-ZnF 2-BaF2 and CdF2-MnF2-BaF 2 ternary sys - tems. Binary glasses (Cd0 .5Ba0 .5 )F2 have

Fluorescence properties and white light generation from Dy3+-doped niobium phosphate glasses

NASA Astrophysics Data System (ADS)

Srihari, T.; Jayasankar, C. K.

2017-07-01

Niobium phosphate glasses (P2O5+Nb2O5+K2O + Al2O3+Dy2O3) doped with different concentrations of Dy3+ ions have been synthesized by melt quenching technique and characterized through structural and optical measurements to evaluate the fluorescence properties and find their suitability for white light emitting diodes (LEDs). Phonon energy and vibrational groups of the host matrix have been analyzed from Raman spectra. Judd-Ofelt analysis has been applied for 1.0 mol% Dy2O3-doped glass and inturn radiative properties have been evaluated for excited states of the Dy3+ ion. The higher value of stimulated emission cross-section (σe = 6.4 × 10-21 cm2) for the 4F9/2 → 6H13/2 level confirms its potentiality to be used as yellow laser. The decay curves exhibit non-exponential nature at higher concentrations (≥1 mol %) of Dy3+ ion. From the decay curve analysis, the quantum efficiency for the 4F9/2 level of 1.0 mol % Dy3+-doped glass is found to be 92%. The yellow to blue intensity ratios and chromaticity color co-ordinates are found to vary with Dy3+ ion concentrations/excitation wavelengths and are within the white light region.

Thermal analysis and in vitro bioactivity of bioactive glass-alumina composites

DOE Office of Scientific and Technical Information (OSTI.GOV)

Chatzistavrou, Xanthippi, E-mail: x.chatzistavrou@imperial.ac.uk; Kantiranis, Nikolaos, E-mail: kantira@geo.auth.gr; Kontonasaki, Eleana, E-mail: kont@dent.auth.gr

2011-01-15

Bioactive glass-alumina composite (BA) pellets were fabricated in the range 95/5-60/40 wt.% respectively and were heat-treated under a specific thermal treatment up to 950 {sup o}C. Control (unheated) and heat-treated pellets were immersed in Simulated Body Fluid (SBF) for bioactivity testing. All pellets before and after immersion in SBF were studied by Fourier Transform Infrared spectroscopy (FTIR), Scanning Electron Microscopy (SEM-EDS) and X-ray Diffraction (XRD) analysis. All composite pellets presented bioactive response. On the surface of the heat-treated pellets the development of a rich biological hydroxyapatite (HAp) layer was delayed for one day, compared to the respective control pellets. Independentmore » of the proportion of the two components, all composites of each group (control and heat-treated) presented the same bioactive response as a function of immersion time in SBF. It was found that by the applied methodology, Al{sub 2}O{sub 3} can be successfully applied in bioactive glass composites without obstructing their bioactive response. - Research Highlights: {yields} Isostatically pressed glass-alumina composites presented apatite-forming ability. {yields} The interaction with SBF resulted in an aluminium phosphate phase formation. {yields} The formation of an aluminium phosphate phase enhanced the in vitro apatite growth.« less

Glass formation and structure of calcium antimony phosphate glasses and those doped with tellurium oxide

NASA Astrophysics Data System (ADS)

Li, Jun; Zhang, Yin; Nian, Shangjiu; Wu, Zhenning; Cao, Weijing; Zhou, Nianying; Wang, Danian

2017-03-01

An approximate glass-forming region in the P2O5-Sb2O3-CaO ternary system was determined. The properties and structure of two compositional series of (A) (75- x)P2O5- xSb2O3-25CaO ( x = 20, 25, 30, 35 mol%) and (B) 45P2O5-30Sb2O3-(25- x)CaO- xTeO2 ( x = 5, 10, 15, 20 mol%) were studied systematically. Thermal properties were investigated by means of differential scanning calorimetry (DSC). The densities of all samples were measured by Archimedes' method using distilled water as the immersion liquid. The water durability of the glasses was described by their dissolution rate (DR) in the distilled water at 90 °C for some time periods. Density, thermal stability and water durability were improved with the addition of Sb2O3 and TeO2. Structural studies were carried out by X-ray diffraction (XRD), infrared spectroscopy and Raman spectroscopy. The phosphate chain depolymerization occurred with the increase of Sb2O3 and the Q2 structural units transformed to the Q1 and Q0 structural units with the addition of TeO2.

Mixed polyanion glass cathodes: Effect of polyanion content

DOE PAGES

Kercher, Andrew K.; Kolopus, James A.; Sacci, Robert L.; ...

2017-02-18

Mixed polyanion glass cathodes in lithium-ion batteries have very high capacities (200-500 mAh/g), but currently these materials have fundamental problems with 1 st-cycle irreversible loss, cycling efficiency, and capacity fade. It is well established that polyanion substitutions into glasses can dramatically affect their physical properties, but the effect of polyanion content on the electrochemical performance has not been previously established. The proper amount of lithium and borate substitution in copper phosphate/vanadate glasses was shown to nearly eliminate 1 st-cycle irreversible loss and improve cycling efficiency. As a result, Raman and IR spectroscopy were used to identify polyanions that correlated withmore » electrochemical performance changes.« less

Degradable phosphate glass fiber reinforced polymer matrices: mechanical properties and cell response.

PubMed

Brauer, Delia S; Rüssel, Christian; Vogt, Sebastian; Weisser, Jürgen; Schnabelrauch, Matthias

2008-01-01

The development of biodegradable materials for internal fracture fixation is of great interest, as they would both eliminate the problem of stress shielding and obviate the need for a second operation to remove fixation devices. Preliminary investigations for the production of degradable fiber reinforced polymer composite materials are detailed. Composites were produced of phosphate invert glass fibers of the glass system P(2)O(5)-CaO-MgO-Na(2)O-TiO(2), which showed a low solubility in previous work. The fibers were embedded into a matrix of a degradable organic polymer network based on methacrylate-modified oligolactide. Fracture behavior, bending strength and elastic modulus were evaluated during 3-point bending tests and the fracture surface of the composites was investigated using a scanning electron microscope. Short-term biocompatibility was tested in an FDA/EtBr viability assay using MC3T3-E1 murine pre-osteoblast cells and showed a good cell compatibility of the composite materials. Results suggested that these composite materials are biocompatible and show mechanical properties which are of interest for the production of degradable bone fixation devices.

Fabrication and characterization of carbon/oxygen-implanted waveguides in Nd3+-doped phosphate glasses

NASA Astrophysics Data System (ADS)

Liu, Chun-Xiao; Xu, Jun; Fu, Li-Li; Zheng, Rui-Lin; Zhou, Zhi-Guang; Li, Wei-Nan; Guo, Hai-Tao; Lin, She-Bao; Wei, Wei

2015-06-01

Optical planar waveguides in Nd3+-doped phosphate glasses are fabricated by a 6.0-MeV carbon ion implantation with a dose of 6.0×1014 ions/cm2 and a 6.0-MeV oxygen ion implantation at a fluence of 6.0×1014 ions/cm2, respectively. The guided modes and the corresponding effective refractive indices were measured by a modal 2010 prism coupler. The refractive index profiles of the waveguides were analyzed based on the stopping and range of ions in matter and the RCM reflectivity calculation method. The near-field light intensity distributions were measured and simulated by an end-face coupling method and a finite-difference beam propagation method, respectively. The comparison of optical properties between the carbon-implanted waveguide and the oxygen-implanted waveguide was carried out. The microluminescence and Raman spectroscopy investigations reveal that fluorescent properties of Nd3+ ions and glass microstructure are well preserved in the waveguide region, which suggests that the carbon/oxygen-implanted waveguide is a good candidate for integrated photonic devices.

Aging of a Binary Colloidal Glass

NASA Astrophysics Data System (ADS)

Lynch, Jennifer M.; Cianci, Gianguido C.; Weeks, Eric R.

2008-03-01

After having undergone a glass transition, a glass is in a non-equilibrium state, and its properties depend on the time elapsed since vitrification. We study this phenomenon, known as aging. In particular, we study a colloidal suspension consisting of micron-sized particles in a liquid --- a good model system for studying the glass transition. In this system, the glass transition is approached by increasing the particle concentration, instead of decreasing the temperature. We observe samples composed of particles of two sizes (d1= 1.0μm and d2= 2.0μm) using fast laser scanning confocal microscopy, which yields real-time, three-dimensional movies deep inside the colloidal glass. We then analyze the trajectories of several thousand particles as the glassy suspension ages. Specifically, we look at how the size, motion and structural organization of the particles relate to the overall aging of the glass. We find that areas richer in small particles are more mobile and therefore contribute more to the structural changes found in aging glasses.

Structural investigation of MO ṡ P2O5ṡ Li2O (MO = Fe2O3 or V2O5) glass systems by FTIR spectroscopy

NASA Astrophysics Data System (ADS)

Andronache, Constantin I.; Racolta, Dania

2014-11-01

Glasses from the systems xMO ṡ(100-x )[ P2O5ṡ Li2O ] (MO = Fe2O3 or V2O5) with 0 ≤ x ≤ mol % were prepared in the same conditions and characterized by IR spectroscopy. It was established the mode in which both Fe2O3 and V2O5 influences the local structure of these glasses. The iron ions generally modify in a different way the local structure of these glasses then vanadium ions. The results shown that phosphate units are the main structural units of glass system and the iron and vanadium ions are located in the network.

Damage Resistant Optical Glasses for High Power Lasers: A Continuing Glass Science and Technology Challenge

DOE Office of Scientific and Technical Information (OSTI.GOV)

Campbell, J H

2002-08-28

A major challenge in the development of optical glasses for high-power lasers is reducing or eliminating laser-induced damage to the interior (bulk) and the polished surface of the glass. Bulk laser damage in glass generally originates from inclusions. With the development of novel glass melting and forming processes it is now possible to make both fused silica and a suit of meta-phosphate laser glasses in large sizes ({approx}>0.5-lm diameter), free of inclusions and with high optical homogeneity ({approx} 10{sup -6}). Considerable attention also has been focused on improving the laser damage resistance to polished optical glass surfaces. Studies have shownmore » that laser-induced damage to surfaces grows exponentially with the number of shots when illuminated with nano-second pulses at 351-nm above a given fluence threshold. A new approach for reducing and eliminating laser-induced surface damage relies on a series of post-polishing treatment steps. This damage improvement method is briefly reviewed.« less

Preparation, structural characterization, and in vitro cell studies of three-dimensional SiO2-CaO binary glass scaffolds built ofultra-small nanofibers.

PubMed

Luo, Honglin; Li, Wei; Ao, Haiyong; Li, Gen; Tu, Junpin; Xiong, Guangyao; Zhu, Yong; Wan, Yizao

2017-07-01

Three-dimensional (3D) nanofibrous scaffolds hold great promises in tissue engineering and regenerative medicine. In this work, for the first time, 3D SiO 2 -CaO binary glass nanofibrous scaffolds have been fabricated via a combined method of template-assisted sol-gel and calcination by using bacterial cellulose as the template. SEM with EDS, TEM, and AFM confirm that the molar ratio of Ca to Si and fiber diameter of the resultant SiO 2 -CaO nanofibers can be controlled by immersion time in the solution of tetraethyl orthosilicate and ethanol. The optimal immersion time was 6h which produced the SiO 2 -CaO binary glass containing 60at.% Si and 40at.% Ca (named 60S40C). The fiber diameter of 60S40C scaffold is as small as 29nm. In addition, the scaffold has highly porous 3D nanostructure with dominant mesopores at 10.6nm and macropores at 20μm as well as a large BET surface area (240.9m 2 g -1 ), which endow the 60S40C scaffold excellent biocompatibility and high ALP activity as revealed by cell studies using osteoblast cells. These results suggest that the 60S40C scaffold has great potential in bone tissue regeneration. Copyright © 2017 Elsevier B.V. All rights reserved.

Crack-resistant Al2O3–SiO2 glasses

PubMed Central

Rosales-Sosa, Gustavo A.; Masuno, Atsunobu; Higo, Yuji; Inoue, Hiroyuki

2016-01-01

Obtaining “hard” and “crack-resistant” glasses have always been of great important in glass science and glass technology. However, in most commercial glasses both properties are not compatible. In this work, colorless and transparent xAl2O3–(100–x)SiO2 glasses (30 ≤ x ≤ 60) were fabricated by the aerodynamic levitation technique. The elastic moduli and Vickers hardness monotonically increased with an increase in the atomic packing density as the Al2O3 content increased. Although a higher atomic packing density generally enhances crack formation in conventional oxide glasses, the indentation cracking resistance increased by approximately seven times with an increase in atomic packing density in binary Al2O3–SiO2 glasses. In particular, the composition of 60Al2O3•40SiO2 glass, which is identical to that of mullite, has extraordinary high cracking resistance with high elastic moduli and Vickers hardness. The results indicate that there exist aluminosilicate compositions that can produce hard and damage-tolerant glasses. PMID:27053006

Crack-resistant Al2O3-SiO2 glasses

NASA Astrophysics Data System (ADS)

Rosales-Sosa, Gustavo A.; Masuno, Atsunobu; Higo, Yuji; Inoue, Hiroyuki

2016-04-01

Obtaining “hard” and “crack-resistant” glasses have always been of great important in glass science and glass technology. However, in most commercial glasses both properties are not compatible. In this work, colorless and transparent xAl2O3-(100-x)SiO2 glasses (30 ≤ x ≤ 60) were fabricated by the aerodynamic levitation technique. The elastic moduli and Vickers hardness monotonically increased with an increase in the atomic packing density as the Al2O3 content increased. Although a higher atomic packing density generally enhances crack formation in conventional oxide glasses, the indentation cracking resistance increased by approximately seven times with an increase in atomic packing density in binary Al2O3-SiO2 glasses. In particular, the composition of 60Al2O3•40SiO2 glass, which is identical to that of mullite, has extraordinary high cracking resistance with high elastic moduli and Vickers hardness. The results indicate that there exist aluminosilicate compositions that can produce hard and damage-tolerant glasses.

Glass transition behavior of ternary disaccharide-ethylene glycol-water solutions

NASA Astrophysics Data System (ADS)

Yu, Tongxu; Zhao, Lishan; Wang, Qiang; Cao, Zexian

2017-06-01

Glass transition behavior of ternary disaccharide-ethylene glycol-water solutions, in reference to that of the binary combinations, has been investigated towards a better understanding of their cryoprotective ability. In water-deficient solutions, the disaccharides, including trehalose, sucrose and maltose, can associate with more than 100 ethylene glycol molecules to form amorphous complex, one order of magnitude larger than the corresponding hydration numbers. In water-rich solutions, a second glass transition emerges with increasing molar fraction of ethylene glycol, indicating the possible synergy of disaccharides and ethylene glycol in vitrification of the ternary aqueous solution.

Crystal-chemistry of alteration products of vitrified wastes: Implications on the retention of polluting elements

DOE Office of Scientific and Technical Information (OSTI.GOV)

Sterpenich, Jerome

2008-07-01

Alteration products of vitrified wastes coming from the incineration of household refuse (MSW) are described. Two vitrified wastes containing 50% and 70% of fly ash and a synthetic stained-glass with a composition close to that of an ancient glass (medieval stained-glass) were altered under different pH conditions (1, 5.5 corresponding to demineralized water and 10) during 181 days. Under acidic condition, the alteration layer is made of an amorphous hydrated silica gel impoverished in most of the initial elements. A minor phase MPO{sub 4} . nH{sub 2}O, where M represents Fe, Ti, Al, Ca and K cations, also constitutes themore » altered layer of the synthetic stained-glass. Under neutral and basic conditions, the altered layer is made of an amorphous hydrated silica gel and a crystallized calcium phosphate phase. The silica gel is depleted in alkalis and alkali-earth elements but contains significant amounts of aluminium, magnesium and transition elements, whereas the calcium phosphate is a hydroxylapatite-like phase with P-Si substitutions and a Ca/P ratio depending on the pH of the solution. This study shows: (i) the strong influence of pH conditions on the crystal-chemistry of alteration products and thus on the mechanisms of weathering resulting in different trapping of polluting elements, and (ii) that glass alteration does not necessary produce thermodynamically stable phases which has to be taken into account for the prediction of the long-term behavior.« less

Effect of surface condition of dental zirconia ceramic (Denzir) on bonding.

PubMed

Uo, Motohiro; Sjögren, Göran; Sundh, Anders; Goto, Mitsunari; Watari, Fumio; Bergman, Maud

2006-09-01

Yttria partially stabilized zirconia (YPSZ) ceramics are suitable for dental and medical use because of their high fracture toughness and chemical durability. The purpose of this study was to examine the bonding behavior of a dental YPSZ ceramic, Denzir. After being subjected to various surface treatments, Denzir specimens were bonded to each other using an adhesive resin composite, glass ionomer, or zinc phosphate cement. Bonding strength was then determined by the shearing test. No significant differences (p>0.05) were observed between SiC- and Al2O3-blasted specimens. In all surface treatments, the shear bond strength significantly (p<0.05) increased in the order of adhesive resin composite cement > glass ionomer cement > zinc phosphate cement. Moreover, silanization with methacryloxy propyl trimethoxysilane slightly increased the bonding strength of the adhesive resin composite cement.

Porosity of different dental luting cements.

PubMed

Milutinović-Nikolić, Aleksandra D; Medić, Vesna B; Vuković, Zorica M

2007-06-01

The aim of this in vitro study was to compare open porosity and pore size distribution of different types of luting cements (zinc phosphate and polycarboxylate produced by Harvard Cement, Great Britain, glass-ionomer product GC Fuji I, GC Corporation, Japan, and Panavia F, resin based composite cement, Kurraray Co. Ltd. Japan) using mercury intrusion porosimetry and use it as an additional parameter for ranging the quality of cements used in prosthetics. Samples were hand mixed in accordance with the manufacturer's instructions and formed in cylindrical test specimens. Density of samples was determined using a pycnometer while porous structure was estimated using high pressure mercury intrusion porosimeter enabling estimation of pore diameters in interval 7.5-15,000 nm. The polycarboxylate cement posses the highest porosity and specific pore volume among investigated cements. By comparison of the results obtained for zinc phosphate and glass-ionomer cement, it can be observed that according to some textural properties zinc phosphate cement is better choice (smaller specific pore volume and absence of macropores larger than 1 microm) while according to other textural properties the glass-ionomer has advantage (smaller porosity). The resin based composite cement poses the most desired porous structure for prosthetic application among the investigated cements (the lowest porosity and specific pore volume and all identified pores are smaller than 20 nm). Based on results of this study, it is possible to estimate the efficiency of luting cements to protect the interior of tooth from penetration of oral fluids, bacteria and bacterial toxins into unprotected dentine.

Electron-impact total ionization cross sections of DNA sugar-phosphate backbone and an additivity principle

NASA Technical Reports Server (NTRS)

Huo, Winifred M.; Dateo, Christopher E.

2005-01-01

The improved binary-encounter dipole (iBED) model [W.M. Huo, Phys. Rev. A64, 042719-1 (2001)l is used to study the total ionization cross sections of the DNA sugar-phosphate backbone by electron impact. Calculations using neutral fragments found that the total ionization cross sections of C3' - and C5', -deoxyribose-phospate, two conformers of the sugar-phosphate backbone, are close to each other. Furthermore, the sum of the ionization cross sections of the separate deoxyribose and phosphate fragments is in close agreement with the C3' - and C5" -deoxyribose-phospate cross sections, differing by less than 10%. The result implies that certain properties of the-DNA, like the total singly ionization cross section, are localized properties and a building-up or additivity principle may apply. This allows us to obtain accurate properties of larger molecular systems built up from the results of smaller subsystem fragments. Calculations are underway using a negatively charged sugar-phosphate backbone with a metal counter-ion.

[Microstructure and mechanical property of a new IPS-Empress 2 dental glass-ceramic].

PubMed

Luo, Xiao-ping; Watts, D C; Wilson, N H F; Silsons, N; Cheng, Ya-qin

2005-03-01

To investigate the microstructure and mechanical properties of a new IPS-Empress 2 dental glass-ceramic. AFM, SEM and XRD were used to analyze the microstructure and crystal phase of IPS-Empress 2 glass-ceramic. The flexural strength and fracture toughness were tested using 3-point bending method and indentation method respectively. IPS-Empress 2 glass-ceramic mainly consisted of lithium disilicate crystal, lithium phosphate and glass matrix, which formed a continuous interlocking structure. The crystal phases were not changed before and after hot-pressed treatment. AFM showed nucleating agent particles of different sizes distributed on the highly polished ceramic surface. The strength and fracture toughness were 300 MPa and 3.1 MPam(1/2). The high strength and fracture toughness of IPS-Empress 2 glass ceramic are attributed to the fine lithium disilicate crystalline, interlocking microstructure and crack deflection.

Glass viscosity calculation based on a global statistical modelling approach

DOE Office of Scientific and Technical Information (OSTI.GOV)

Fluegel, Alex

2007-02-01

A global statistical glass viscosity model was developed for predicting the complete viscosity curve, based on more than 2200 composition-property data of silicate glasses from the scientific literature, including soda-lime-silica container and float glasses, TV panel glasses, borosilicate fiber wool and E type glasses, low expansion borosilicate glasses, glasses for nuclear waste vitrification, lead crystal glasses, binary alkali silicates, and various further compositions from over half a century. It is shown that within a measurement series from a specific laboratory the reported viscosity values are often over-estimated at higher temperatures due to alkali and boron oxide evaporation during the measurementmore » and glass preparation, including data by Lakatos et al. (1972) and the recently published High temperature glass melt property database for process modeling by Seward et al. (2005). Similarly, in the glass transition range many experimental data of borosilicate glasses are reported too high due to phase separation effects. The developed global model corrects those errors. The model standard error was 9-17°C, with R^2 = 0.985-0.989. The prediction 95% confidence interval for glass in mass production largely depends on the glass composition of interest, the composition uncertainty, and the viscosity level. New insights in the mixed-alkali effect are provided.« less

Effectiveness of Flame Retardants in TufFoam.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Abelow, Alexis Elizabeth; Nissen, April; Massey, Lee Taylor

An investigation of polyurethane foam filled with known flame retardant fillers including hydroxides, melamine, phosphate-containing compounds, and melamine phosphates was carried out to produce a low-cost material with high flame retardant efficiency. The impact of flame retardant fillers on the physical properties such a s composite foam density, glass transition temperature, storage modulus, and thermal expansion of composite foams was investigated with the goal of synthesizing a robust rigid foam with excellent flame retardant properties.

Influence of gel/LED-laser application on cervical microleakage of two barrier materials used for endodontically treated teeth whitening

NASA Astrophysics Data System (ADS)

Marchesan, Melissa Andréia; Barros, Felipe; Porto, Saulo; Zaitter, Suellen; Brugnera, Aldo, Jr.; Sousa-Neto, Manoel D.

2007-02-01

This study evaluated ex vivo the influence of the number of gel/LED-laser applications/activations on cervical microleakage of two different barrier materials used for protection during whitening of endodontically treated teeth. Eighty-four canines were instrumented and obturated with epoxy resin sealer. The seal was removed 2 mm beyond the cemento-enamel junction for barrier placement and the teeth were divided into two groups of 40 teeth each: G1, zinc phosphate cement; G2, glass ionomer cement. The two groups were subdivided into 4 subgroups (n=10 each): I) no gel or LED-laser application; II) one gel application and two LED-laser activations; III) two gel applications and four LED-laser activations; IV) three gel applications and six LED-laser activations. The teeth were immersed in India ink for 7 days, decalcified and cleared. Cervical microleakage was quantified with a measurement microscope. Statistical analysis showed that zinc phosphate caused significantly lower microleakage than glass ionomer cement (presented microleakage in all subgroups). However, after two (p<0.01) and three (p<0.001) applications of gel, there was statistially significant microleakage in zinc phosphate barriers. Based on the present results, it can be concluded that cervical barriers with zinc phosphate cement show less cervical microleakage and that two or more applications/activations of gel/LED-laser significantly increase microleakage.

Suppression of phosphate liberation from eutrophic lake sediment by using fly ash and ordinary Portland cement

DOE Office of Scientific and Technical Information (OSTI.GOV)

Heng-Peng Ye; Fan-Zhong Chen; Yan-Qing Sheng

2006-08-15

In this study, the effect of suppression on phosphate liberation from eutrophic lake sediment by using fly ash and ordinary Portland cement (OPC) was investigated by small scale experiment. A system including sediment, lake water, and several kinds of capping materials was designed to clarify the suppression of phosphate liberation from sediment under the anaerobic condition. The suppression efficiencies of fly ash, OPC and glass bead used as control material were also determined, and these effects were discussed. The suppression efficiency of glass bead was 44.4%, and those of fly ash and OPC were 84.4%, 94.9%, respectively. The suppression bymore » fly ash and OPC was mainly carried out by the adsorption effect, in addition to the covering effect. The suppression efficiency depended on the amounts of the material used, and about 90% of liberated phosphate was suppressed by fly ash of 10.0 Kg m{sup -2}, and OPC of 6.0 Kg m{sup -2}. The concentrations of heavy metals, such as mercury, cadmium, lead, copper, zinc, chromium, silver, arsenic and nickel, in fly ash and OPC were lower than those in the environmental materials. And it was considered that the concentrations of heavy metals in fly ash and OPC were too low to influence the ecosystem in natural water region.« less

Glassy nature and glass-to-crystal transition in the binary metallic glass CuZr

NASA Astrophysics Data System (ADS)

Wei, Zi-Yang; Shang, Cheng; Zhang, Xiao-Jie; Liu, Zhi-Pan

2017-06-01

The prediction for the stability of glassy material is a key challenge in physical science. Here, we report a theoretical framework to predict the glass stability based on stochastic surface walking global optimization and reaction pathway sampling. This is demonstrated by revealing for the first time the global potential energy surface (PES) of two systems, CuZr binary metallic glass and nonglassy pure Cu systems, and establishing the lowest energy pathways linking glassy/amorphous structures with crystalline structures. The CuZr system has a significant number of glassy structures on PES that are ˜0.045 eV /atom above the crystal structure. Two clear trends are identified from global PES in the glass-to-crystal transition of the CuZr system: (i) the local Zr-Cu coordination (nearest neighbor) increases, and (ii) the local Zr bonding environment becomes homogeneous. This allows us to introduce quantitative structural and energetics conditions to distinguish the glassy structures from the crystalline structures. Because of the local Zr-Cu exchange in the glass-to-crystal transition, a high reaction barrier (>0.048 eV /atom ) is present to separate the glassy structures and the crystals in CuZr. By contrast, the Cu system, although it does possess amorphous structures that appear at much higher energy (˜0.075 eV /atom ) with respect to the crystal structure, has very low reaction barriers for the crystallization of amorphous structures, i.e. <0.011 eV /atom . The quantitative data on PES now available from global optimization techniques deepens our understanding on the microscopic nature of glassy material and might eventually facilitate the design of stable glassy materials.

Role of gallium and silver from phosphate-based glasses on in vitro dual species oral biofilm models of Porphyromonas gingivalis and Streptococcus gordonii.

PubMed

Valappil, Sabeel P; Coombes, Marc; Wright, Lucy; Owens, Gareth J; Lynch, Richard J M; Hope, Christopher K; Higham, Susan M

2012-05-01

Phosphate-based glasses (PBGs) are excellent controlled delivery agents for antibacterial ions such as silver and gallium. The aim of this study was to assess the potential utility of novel PBGs combining both gallium and silver for use in periodontal therapy. To this end, an in vitro biofilm model with the putative periodontal pathogen, Porphyromonas gingivalis, and an initial colonizer, Streptococcus gordonii, was established. The effect of increasing calcium content in gallium-silver-doped PBG on the susceptibility of P. gingivalis was examined. A decrease in degradation rates (30.34, 25.19, 21.40 μg mm(-2) h(-1)) with increasing PBG calciumcontent (10, 11, 12 mol.% respectively) was observed, correlating well with gallium and silver ion release and antimicrobial activity against planktonic P. gingivalis (approximately 5.4log(10) colony-forming units (CFU) reduction after 24h by the C10 glass compared with controls) and S. gordonii (total growth inhibition after 32h by C10, C11 and C12 glasses compared with controls). The most potent PBG (C10) was evaluated for its ability to inhibit the biofilm growth of P. gingivalis in a newly established constant-depth film fermentor model. The simultaneous release of silver and gallium from the glass reduced P. gingivalis biofilm growth with a maximum effect (1.92log(10) CFU reduction) after 168 h. Given the emergence of antibiotic-resistant bacteria and dearth of new antibiotics in development, the glasses, especially C10, would offer effective alternatives to antibiotics or may complement current therapies through controlled, localized delivery of gallium and silver ions at infected sites in the oral cavity. Copyright © 2012 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

Conversion of melt-derived microfibrous borate (13-93B3) and silicate (45S5) bioactive glass in a simulated body fluid.

PubMed

Liu, Xin; Rahaman, Mohamed N; Day, Delbert E

2013-03-01

Microfibrous bioactive glasses are showing a considerable capacity to heal soft tissue wounds, but little information is available on the mechanism of healing. In the present study, the conversion of microfibrous borate bioactive glass (diameter = 0.2-5 μm) with the composition designated 13-93B3 (5.5 Na2O, 11.1 K2O, 4.6 MgO, 18.5 CaO, 3.7 P2O5, 56.6 B2O3 wt%) was evaluated in vitro as a function of immersion time in a simulated body fluid (SBF) at 37 °C using structural and chemical techniques. Silicate 45S5glass microfibers (45 SiO2, 24.5 Na2O, 24.5 CaO, 6 P2O5 wt%) were also studied for comparison. Microfibrous 13-93B3 glass degraded almost completely and converted to a calcium phosphate material within 7-14 days in SBF, whereas >85 % of the silica remained in the 45S5 microfibers, forming a silica gel phase. An amorphous calcium phosphate (ACP) product that formed on the 13-93B3 microfibers crystallized at a slower rate to hydroxyapatite (HA) when compared to the ACP that formed on the 45S5 fibers. For immersion times >3 days, the 13-93B3 fibers released a higher concentration of Ca into the SBF than the 45S5 fibers. The fast and more complete degradation, slow crystallization of the ACP product, and higher concentration of dissolved Ca in SBF could contribute to the capacity of the microfibrous borate 13-93B3 glass to heal soft tissue wounds.

Float processing of high-temperature complex silicate glasses and float baths used for same

NASA Technical Reports Server (NTRS)

Cooper, Reid Franklin (Inventor); Cook, Glen Bennett (Inventor)

2000-01-01

A float glass process for production of high melting temperature glasses utilizes a binary metal alloy bath having the combined properties of a low melting point, low reactivity with oxygen, low vapor pressure, and minimal reactivity with the silicate glasses being formed. The metal alloy of the float medium is exothermic with a solvent metal that does not readily form an oxide. The vapor pressure of both components in the alloy is low enough to prevent deleterious vapor deposition, and there is minimal chemical and interdiffusive interaction of either component with silicate glasses under the float processing conditions. Alloys having the desired combination of properties include compositions in which gold, silver or copper is the solvent metal and silicon, germanium or tin is the solute, preferably in eutectic or near-eutectic compositions.

Impact of vanadium ions in barium borate glass.

PubMed

Abdelghany, A M; Hammad, Ahmed H

2015-02-25

Combined optical and infrared spectral measurements of prepared barium borate glasses containing different concentrations of V2O5 were carried out. Vanadium containing glasses exhibit extended UV-visible (UV/Vis.) bands when compared with base binary borate glass. UV/Vis. spectrum shows the presence of an unsymmetrical strong UV broad band centered at 214 nm attributed to the presence of unavoidable trace iron impurities within the raw materials used for the preparation of such glass. The calculated direct and indirect optical band gaps are found to decrease with increasing the vanadium content (2.9:137 for indirect and 3.99:2.01 for direct transition). This change was discussed in terms of structural changes in the glass network. Infrared absorption spectra of the glasses reveal the appearance of both triangular and tetrahedral borate units. Electron spin resonance analyses indicate the presence of unpaired species in sufficient quantity to be identified and to confirm the spectral data. Copyright © 2014 Elsevier B.V. All rights reserved.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Helfferich, Julian; Lyubimov, Ivan; Reid, Daniel

Glasses produced via physical vapor deposition can display greater kinetic stability and lower enthalpy than glasses prepared by liquid cooling. While the reduced enthalpy has often been used as a measure of the stability, it is not obvious whether dynamic measures of stability provide the same view. Here, we study dynamics in vapor-deposited and liquid-cooled glass films using molecular simulations of a bead-spring polymer model as well as a Lennard-Jones binary mixture in two and three dimensions. We confirm that the dynamics in vapor-deposited glasses is indeed slower than in ordinary glasses. We further show that the inherent structure energymore » is a good reporter of local dynamics, and that aged systems and glasses prepared by cooling at progressively slower rates exhibit the same behavior as vapor-deposited materials when they both have the same inherent structure energy. These findings suggest that the stability inferred from measurements of the energy is also manifested in dynamic observables, and they strengthen the view that vapor deposition processes provide an effective strategy for creation of stable glasses.« less

Silver metaphosphate glass wires inside silica fibers--a new approach for hybrid optical fibers.

PubMed

Jain, Chhavi; Rodrigues, Bruno P; Wieduwilt, Torsten; Kobelke, Jens; Wondraczek, Lothar; Schmidt, Markus A

2016-02-22

Phosphate glasses represent promising candidates for next-generation photonic devices due to their unique characteristics, such as vastly tunable optical properties, and high rare earth solubility. Here we show that silver metaphosphate wires with bulk optical properties and diameters as small as 2 µm can be integrated into silica fibers using pressure-assisted melt filling. By analyzing two types of hybrid metaphosphate-silica fibers, we show that the filled metaphosphate glass has only negligible higher attenuation and a refractive index that is identical to the bulk material. The presented results pave the way towards new fiber-type optical devices relying on metaphosphate glasses, which are promising materials for applications in nonlinear optics, sensing and spectral filtering.

Particle tracking experiments in match-index-refraction porous media.

PubMed

Lachhab, Ahmed; Zhang, You-Kuan; Muste, Marian V I

2008-01-01

A low-cost, noninvasive, three-dimensional (3D), particle tracking velocimetry system was designed and built to investigate particle movement in match-index-refraction porous media. Both a uniform load of the glass beads of the same diameter and a binary load of the glass beads of two diameters were used. The purpose of the experiments is to study the effect of the two loads on the trajectories, velocity distribution, and spreading of small physical particles. A total of 35 particles were released and tracked in the uniform load and 46 in the binary load. The 3D trajectory of each particle was recorded with two video camcorders and analyzed. It is found that the particle's velocity, trajectory, and spreading are very sensitive to its initial location and that the smaller pore size or heterogeneity in the binary load increases the particles' velocity and enhances their spreading as compared with the uniform load. The experiments also verified the previous finding that the distribution of the particle velocities are lognormal in the longitudinal direction and Gaussian in two transverse directions and that the particle spreading is much larger along the longitudinal direction than along the traverse directions.

Corrosion resistance and in-vitro bioactivity of BaO containing Na2O-CaO-P2O5 phosphate glass-ceramic coating prepared on 316 L, duplex stainless steel 2205 and Ti6Al4V

NASA Astrophysics Data System (ADS)

Edathazhe, Akhila B.; Shashikala, H. D.

2018-03-01

The phosphate glass with composition 11Na2O-15BaO-29CaO-45P2O5 was coated on biomedical implant materials such as stainless steel 316 L, duplex stainless steel (DSS) 2205 and Ti6Al4V alloy by thermal enamelling method. The structural properties and composition of glass coated substrates were studied by x-ray diffraction (XRD), Scanning electron microscopy (SEM) and Energy dispersive x-ray spectroscopy (EDS) analysis. The coatings were partially crystalline in nature with porous structure and pore size varied from micro to nanometer range. The polarization curve was obtained for uncoated and coated substrates from electrochemical corrosion test which was conducted at 37 °C in Hank’s balanced salt solution (HBSS). The corrosion resistance of 316 L substrate increased after coating, whereas it decreased in case of DSS 2205 and Ti6Al4V. The XRD and SEM/EDS studies indicated the bioactive hydroxyapatite (HAp) layer formation on all the coated surfaces after electrochemical corrosion test, which improved the corrosion resistance. The observed electrochemical corrosion behavior can be explained based on protective HAp layer formation, composition and diffusion of ions on glass coated surfaces. The in-vitro bioactivity test was carried out at 37 °C in HBS solution for 14 days under static conditions for uncoated and coated substrates. pH and ion release rate measurements from the coated samples were conducted to substantiate the electrochemical corrosion test. The lower ion release rates of Na+ and Ca2+ from coated 316 L supported its higher electrochemical corrosion resistance among coated samples. Among the uncoated substrates, DSS showed higher electrochemical corrosion resistance. Amorphous calcium-phosphate (ACP) layer formation on all the coated substrates after in-vitro bioactivity test was confirmed by XRD, SEM/EDS and ion release measurements. The present work is a comparative study of corrosion resistance and bioactivity of glass coated and uncoated biomedical implants such as 316 L, DSS and Ti6Al4V.

Phosphate glass useful in high power lasers

DOEpatents

Hayden, J.S.; Sapak, D.L.; Ward, J.M.

1990-05-29

A low- or no-silica phosphate glass useful as a laser medium and having a high thermal conductivity, K[sub 90 C] > 0.8 W/mK, and a low coefficient of thermal expansion, [alpha][sub 20--40 C] < 80[times]10[sup [minus]7]/C, consists essentially of (on a batch composition basis Mole %): P[sub 2]O[sub 5], 45-70; Li[sub 2]O, 15-35; Na[sub 2]O, 0-10; Al[sub 2]O[sub 3], 10-15; Nd[sub 2]O[sub 3], 0.01-6; La[sub 2]O[sub 3], 0-6; SiO[sub 2], 0-8; B[sub 2]O[sub 3], 0-8; MgO, 0-18; CaO, 0-15; SrO, 0-9; BaO, 0-9; ZnO, 0-15; the amounts of Li[sub 2]O and Na[sub 2]O providing an average alkali metal ionic radius sufficiently low whereby said glass has K[sub 90 C] > 0.8 W/mK and [alpha][sub 20--40 C] < 80[times]10[sup [minus]7]/C, and wherein, when the batch composition is melted in contact with a silica-containing surface, the final glass composition contains at most about 3.5 mole % of additional silica derived from such contact during melting. The Nd[sub 2]O[sub 3] can be replaced by other lasing species. 3 figs.

The influence of different cementation modes on the fracture resistance of feldspathic ceramic crowns.

PubMed

Groten, M; Pröbster, L

1997-01-01

One hundred twenty pressed feldspathic ceramic crowns were luted to 20 steel dies using six different cementation modes. Fracture resistance was tested under an angle of 45 degrees and was determined as the maximal fracture load. Crowns were tested with luting agent only (groups A and C) and after etching with hydrofluoric acid, silanating, and the application of a bonding agent (groups B, D, E, and F). The resulting means were: phosphate cement 294.3 (A) and 282.2 (B); glass-ionomer cement 217.2 (C) and 255.4 (D); resin composite 382.2 (E) and 687.6 (F). Statistical analysis revealed significantly greater fracture resistance (P < .01) of resin luted crowns. Bonding to the die almost doubled the fracture resistance. Conditioning of the inner surfaces of the crowns did not improve the fracture resistance of crowns luted using zinc phosphate or glass-ionomer cements.

Wavefront correction by target-phase-locking technology in a 500 TW laser facility

NASA Astrophysics Data System (ADS)

Wang, D. E.; Dai, W. J.; Zhou, K. N.; Su, J. Q.; Xue, Q.; Yuan, Q.; Zhang, X.; Deng, X. W.; Yang, Y.; Wang, Y. C.; Xie, N.; Sun, L.; Hu, D. X.; Zhu, Q. H.

2017-03-01

We demonstrate a novel approach termed target-phase-locking that could improve the entire beam wavefront quality of a 500 TW Nd3+:phosphate glass laser facility. The thermal and static wavefront from front-end to target is corrected by using one deformable mirror that receives feedback from both the focal-spot sensor and wavefront sensor, and only the main laser of the laser system is employed in the correction process, with auxiliary calibration light no longer necessary. As a result, a static focal spot with full width at half maximum of 8.87  ×  5.74 µm is achieved, the thermal wavefront induced by flash-lamp-pumped Nd3+:phosphate glass is compensated with PV from 3.54-0.43 µm, and a dynamic focal spot with intensity exceeding 1020 W cm-2 is precisely predicted at the target with such an approach.

Optical spectroscopy, 1.06 μm emission properties of Nd3 +-doped phosphate based glasses

NASA Astrophysics Data System (ADS)

Sk. Nayab, Rasool; Sasikala, T.; Mohan Babu, A.; Rama Moorthy, L.; C. K., Jayasankar

2017-06-01

Neodymium doped phosphate based glasses with composition of (P2O5 + K2O + Al2O3 + CaF2) were prepared. The samples were analysed through differential thermal analysis (DTA), Fourier transform infrared (FTIR), absorption, emission and decay measurements. Judd-Ofelt parameters (Ωλ) have been determined from the spectral intensities of absorption bands in order to calculate the radiative parameters like radiative transition probabilities (AR), radiative lifetime (τR) and branching ratios (βR) for the 4F3/2 → 4I11/2 laser transition of Nd3 + ion. The effective emission bandwidths (Δλeff), experimental branching ratios (βexp) and stimulated emission cross-sections (σe) have been determined from the emission spectrum. The decay curves of the 4F3/2 level exhibited almost single exponential nature for all the Nd3 + ion concentrations.

In Vitro Comparison of Zinc Phosphate and Glass Ionomers Ability to Inhibit Decalcification under and Adjacent to Orthodontic Bands.

DTIC Science & Technology

1985-08-01

confer the ability to leach fluoride ions into the surrounding tooth enamel . Kidd 3 7 using an artifical caries tec- hnique with a diffusion controlled...5 - Enamel Changes Scoring System- 1. NONE: No color change evident 2. MILD: Slight change in enamel color 3.MODERATE: Definate whitening of enamel ...to adhere to stainless steel and to tooth enamel with a chemical bond 51 . Zinc phosphate, on the other hand, does not chemically adhere to enamel or

Effect of bioglass 45S5 addition on properties, microstructure and cellular response of tetracalcium phosphate/monetite cements

DOE Office of Scientific and Technical Information (OSTI.GOV)

Stulajterova, R., E-mail: rstulajterova@saske.sk

Tetracalcium phosphate/nanomonetite (TTCPMH) cement composites with 7.5 and 15 wt% addition of melt-derived 45S5 bioactive glass were prepared by mechanical homogenization of powder components and 2% NaH{sub 2}PO{sub 4} solution was used as a hardening liquid. The properties of composites with the acidic (Ca/P ratio equal 1.5) or basic (Ca/P ratio equal 1.67) TTCPMH component were compared. Addition of glass component caused rapid rise in pH of composites up to 10. In microstructure of basic cement composite, the large bioglass particles weakly bounded to surrounding cement matrix were found contrary to a more compact microstructure of acidic cement composites withmore » the high number of spherical silica particles. Both the significant refinement of hydroxyapatite particles and the change to needle-like morphology with rise in the content of bioglass were identified in hydroxyapatite coatings created during soaking of composites in phosphate buffered saline. In acidic cement mixtures, the increase of compressive strength with an amount of bioglass was found whereas the opposite tendency was revealed in the case of basic cement mixtures. The higher concentrations of ions were verified in solutions after immersion of acidic cement composites. The severe cytotoxicity of extracts and composite cement substrates containing 15 wt% of bioglass demonstrated adverse effects of both the ionic concentrations and unappropriate surface texture on proliferation of mesenchymal stem cells. The enhanced ALP activities of cells cultured on composite cements confirmed the positive effect of bioactive glass addition on differentiation of mesenchymal stem cells. - Highlights: • Novel B45S5 bioglass/tetracalcium phosphate/nanomonetite cement composites • Cement basicity negatively affected their microstructure. • Acid composite cements had higher compressive strengths than basic composites. • Fast differentiation of MSC to osteoblast line on composite with 7.5 wt% of bioglass • Severe cytotoxicity of 24 h extracts from composites with 15 wt% of bioglass.« less

Dense proton injection into phosphate glasses using corona discharge treatment

NASA Astrophysics Data System (ADS)

Kinoshita, Takuya; Miyazaki, Atsushi; Kawaguchi, Keiga; Sakai, Daisuke; Yamaguchi, Takuya; Omata, Takahisa; Ishiyama, Tomohiro; Fujioka, Masaya; Kaiju, Hideo; Nishii, Junji

2018-01-01

Sodium ions in 25NaO1/2-6LaO3/2-6GeO2-63PO5/2 (mol%) glasses were substituted with protons using corona discharge treatment (CDT) under a H2 atmosphere. The substitution of sodium ion to proton proceeded from the anode side to the cathode side with constant current flow during the CDT. A crystalline free and transparent glass plate of 0.3 mm thickness was obtained after CDT for 96 h. The maximum decrease rate from sodium ion to proton was 78 ± 10%. The proton conductivity of 8.5 × 10-4 S/cm was attained at 400 °C.

Network structure and concentration fluctuations in a series of elemental, binary, and tertiary liquids and glasses.

PubMed

Soper, Alan K

2010-10-13

Liquids and glasses continue to produce a lively debate about the nature of the disordered structure in these materials, and whether it is driven by longer range concentration or density fluctuations. One factor often lacking in these studies is an overview of a wide range of structures from which common features of and differences between materials can be identified. Here I examine the structure of a wide range of chain and network, elemental, binary and tertiary liquids and glasses, using available x-ray and neutron diffraction data and combining them with empirical potential structure refinement. Calculation of the Bhatia-Thornton number-number and concentration-concentration structure factors and distribution functions highlights common structural motifs that run through many of the series. It is found that the greatest structural overlap occurs where the nearest-neighbour and second-neighbour coordination numbers are similar for different materials. As these coordination numbers increase, so the structures undergo a sequence of characteristic changes involving increasingly bent bond angle distributions and increased packing fractions. In these regards liquid and amorphous phosphorus appear to be in a structural class of their own, combining both chain-like and network-like characteristics.

Toward a Rational Design of Bioactive Glasses with Optimal Structural Features: Composition–Structure Correlations Unveiled by Solid-State NMR and MD Simulations

PubMed Central

2013-01-01

The physiological responses of silicate-based bioactive glasses (BGs) are known to depend critically on both the P content (nP) of the glass and its silicate network connectivity (N̅BOSi). However, while the bioactivity generally displays a nonmonotonic dependence on nP itself, recent work suggest that it is merely the net orthophosphate content that directly links to the bioactivity. We exploit molecular dynamics (MD) simulations combined with 31P and 29Si solid-state nuclear magnetic resonance (NMR) spectroscopy to explore the quantitative relationships between N̅BOSi, nP, and the silicate and phosphate speciations in a series of Na2O–CaO–SiO2–P2O5 glasses spanning 2.1 ≤ N̅BOSi ≤ 2.9 and variable P2O5 contents up to 6.0 mol %. The fractional population of the orthophosphate groups remains independent of nP at a fixed N̅BOSi-value, but is reduced slightly as N̅BOSi increases. Nevertheless, P remains predominantly as readily released orthophosphate ions, whose content may be altered essentially independently of the network connectivity, thereby offering a route to optimize the glass bioactivity. We discuss the observed composition-structure links in relation to known composition-bioactivity correlations, and define how Na2O–CaO–SiO2–P2O5 compositions exhibiting an optimal bioactivity can be designed by simultaneously altering three key parameters: the silicate network connectivity, the (ortho)phosphate content, and the nNa/nCa molar ratio. PMID:24364818

Development of electro-conductive silver phosphate-based glass optrodes for in vivo optogenetics

NASA Astrophysics Data System (ADS)

Desjardins, Mathieu; Roudjane, Mourad; Ledemi, Yannick; Gagnon-Turcotte, Gabriel; Maghsoudloo, Esmaeel; Filion, Guillaume; Gosselin, Benoit; Messaddeq, Younès.

2018-02-01

Multifunctional fibers are developed worldwide for enabling many new advanced applications. Among the multiple new functionalities that such fibers can offer according to their design, chemical composition and materials combination, the co-transmission of light and electrical signals is of first interest for sensing applications, in particular for optogenetics and electrophysiology. Multifunctional fibers offer an all-solid approach relying on new ionic conducting glasses for the design and manufacturing of next generation optrodes, which represents a tremendous upgrade compared to conventional techniques that requires the utilization of liquid electrolytes to carry the electrical signal generated by genetically encoded neuronal gated ion channels after optical excitation. After a systematic study conducted on different ion-conductive glass systems, silver phosphate-based glasses belonging to the AgI-AgPO3-WO3 and AgI-AgPO3-Ag2WO4 systems were found to be very promising materials for the target application. Several types of fibers, including single-core step-index fibers, multimaterial fibers made of inorganic and optical polymeric glasses have been then fabricated and characterized. Light transmission ranging from 400 to 1000 nm and electrical conductivity ranging from 10-3 and 10-1 S·cm-1 at room temperature (AC frequencies from 1 Hz to 1 MHz) were demonstrated with these fibers. Very sharp fiber tapers were then produced with high repeatability by using a CO2 laser optical setup, allowing a significant shrinking from the fiber (300 μm diameter) to the taper tip (25-30 μm diameter).

Method of processing "BPS" glass ceramic and seals made therewith

DOEpatents

Reed, Scott T.; Stone, Ronald G.; McCollister, Howard L.; Wengert, deceased, Paul R.

1998-01-01

A glass ceramic composition, a glass ceramic-to-metal seal, and more specifically a hermetic glass ceramic-to-metal seal prepared by subjecting a glass composition comprising, by weight percent, SiO.sub.2 (65-80%), LiO.sub.2 (8-16%), Al.sub.2 O.sub.3 (2-8%), K.sub.2 O (1-8%), P.sub.2 O.sub.5 (1-5%), B.sub.2 O.sub.3 (0.5-7%), and ZnO (0-5%) to the following processing steps: 1) heating the glass composition in a belt furnace to a temperature sufficient to melt the glass and crystallize lithium phosphate, 2) holding at a temperature and for a time sufficient to create cristobalite nuclei, 3) cooling at a controlled rate and to a temperature to cause crystallization of lithium silicates and growth of cristobalite, and 4) still further cooling in stages to ambient temperature. This process produces a glass ceramic whose high coefficient of thermal expansion (up to 200.times.10.sup.-7 in/in/.degree.C.) permits the fabrication of glass ceramic-to-metal seals, and particularly hermetic glass ceramic seals to nickel-based and stainless steel alloys and copper.

In vitro bioactivity and antimicrobial tuning of bioactive glass nanoparticles added with neem (Azadirachta indica) leaf powder.

PubMed

Prabhu, M; Ruby Priscilla, S; Kavitha, K; Manivasakan, P; Rajendran, V; Kulandaivelu, P

2014-01-01

Silica and phosphate based bioactive glass nanoparticles (58SiO2-33CaO-9P2O5) with doping of neem (Azadirachta indica) leaf powder and silver nanoparticles were prepared and characterised. Bioactive glass nanoparticles were produced using sol-gel technique. In vitro bioactivity of the prepared samples was investigated using simulated body fluid. X-ray diffraction (XRD) pattern of prepared glass particles reveals amorphous phase and spherical morphology with a particle size of less than 50 nm. When compared to neem doped glass, better bioactivity was attained in silver doped glass through formation of hydroxyapatite layer on the surface, which was confirmed through XRD, Fourier transform infrared (FTIR), and scanning electron microscopy (SEM) analysis. However, neem leaf powder doped bioactive glass nanoparticles show good antimicrobial activity against Staphylococcus aureus and Escherichia coli and less bioactivity compared with silver doped glass particles. In addition, the biocompatibility of the prepared nanocomposites reveals better results for neem doped and silver doped glasses at lower concentration. Therefore, neem doped bioactive glass may act as a potent antimicrobial agent for preventing microbial infection in tissue engineering applications.

Method of processing ``BPS`` glass ceramic and seals made therewith

DOEpatents

Reed, S.T.; Stone, R.G.; McCollister, H.L.; Wengert, P.R.

1998-10-13

A glass ceramic composition, a glass ceramic-to-metal seal, and more specifically a hermetic glass ceramic-to-metal seal prepared by subjecting a glass composition comprising, by weight percent, SiO{sub 2} (65--80%), LiO{sub 2} (8--16%), Al{sub 2}O{sub 3} (2--8%), K{sub 2}O (1--8%), P{sub 2}O{sub 5} (1--5%), B{sub 2}O{sub 3} (0.5--7%), and ZnO (0--5%) to the following processing steps: (1) heating the glass composition in a belt furnace to a temperature sufficient to melt the glass and crystallize lithium phosphate, (2) holding at a temperature and for a time sufficient to create cristobalite nuclei, (3) cooling at a controlled rate and to a temperature to cause crystallization of lithium silicates and growth of cristobalite, and (4) still further cooling in stages to ambient temperature. This process produces a glass ceramic whose high coefficient of thermal expansion (up to 200{times}10{sup {minus}7} in/in/C) permits the fabrication of glass ceramic-to-metal seals, and particularly hermetic glass ceramic seals to nickel-based and stainless steel alloys and copper. 5 figs.

In Vitro Bioactivity and Antimicrobial Tuning of Bioactive Glass Nanoparticles Added with Neem (Azadirachta indica) Leaf Powder

PubMed Central

Prabhu, M.; Ruby Priscilla, S.; Kavitha, K.; Manivasakan, P.; Rajendran, V.; Kulandaivelu, P.

2014-01-01

Silica and phosphate based bioactive glass nanoparticles (58SiO2-33CaO-9P2O5) with doping of neem (Azadirachta indica) leaf powder and silver nanoparticles were prepared and characterised. Bioactive glass nanoparticles were produced using sol-gel technique. In vitro bioactivity of the prepared samples was investigated using simulated body fluid. X-ray diffraction (XRD) pattern of prepared glass particles reveals amorphous phase and spherical morphology with a particle size of less than 50 nm. When compared to neem doped glass, better bioactivity was attained in silver doped glass through formation of hydroxyapatite layer on the surface, which was confirmed through XRD, Fourier transform infrared (FTIR), and scanning electron microscopy (SEM) analysis. However, neem leaf powder doped bioactive glass nanoparticles show good antimicrobial activity against Staphylococcus aureus and Escherichia coli and less bioactivity compared with silver doped glass particles. In addition, the biocompatibility of the prepared nanocomposites reveals better results for neem doped and silver doped glasses at lower concentration. Therefore, neem doped bioactive glass may act as a potent antimicrobial agent for preventing microbial infection in tissue engineering applications. PMID:25276834

Fluorescence properties of Nd3+-doped tellurite glasses.

PubMed

Kumar, K Upendra; Prathyusha, V A; Babu, P; Jayasankar, C K; Joshi, A S; Speghini, A; Bettinelli, M

2007-07-01

The compositional and concentration dependence of luminescence of the (4)F(3/2)-->(4)I(J) (J=13/2, 11/2 and 9/2) transitions in four Nd(3+)-doped tellurite based glasses has been studied. The free-ion energy levels obtained for 60TeO(2)+39ZnO(2)+1.0Nd(2)O(3) (TZN10) glass have been analysed using the free-ion Hamiltonian model and compared with similar results obtained for Nd(3+):glass systems. The absorption spectrum of TZN10 glass has been analysed using the Judd-Ofelt theory. Relatively longer decay rates have been obtained for Nd(3+)-doped phosphotellurite glasses. The emission characteristics of the (4)F(3/2)-->(4)I(11/2) transition, of the Nd(3+):TZN10 glass, are found to be comparable to those obtained for Nd(3+):phosphate laser glasses. The non-exponential shape of the emission decay curves for the (4)F(3/2)-->(4)I(11/2) transition is attributed to the presence of energy transfer processes between the Nd(3+) ions.

Independent control of beam astigmatism and ellipticity using a SLM for fs-laser waveguide writing.

PubMed

Ruiz de la Cruz, A; Ferrer, A; Gawelda, W; Puerto, D; Sosa, M Galván; Siegel, J; Solis, J

2009-11-09

We have used a low repetition rate (1 kHz), femtosecond laser amplifier in combination with a spatial light modulator (SLM) to write optical waveguides with controllable cross-section inside a phosphate glass sample. The SLM is used to induce a controllable amount of astigmatism in the beam wavefront while the beam ellipticity is controlled through the propagation distance from the SLM to the focusing optics of the writing set-up. The beam astigmatism leads to the formation of two separate disk-shaped foci lying in orthogonal planes. Additionally, the ellipticity has the effect of enabling control over the relative peak irradiances of the two foci, making it possible to bring the peak irradiance of one of them below the material transformation threshold. This allows producing a single waveguide with controllable cross-section. Numerical simulations of the irradiance distribution at the focal region under different beam shaping conditions are compared to in situ obtained experimental plasma emission images and structures produced inside the glass, leading to a very satisfactory agreement. Finally, guiding structures with controllable cross-section are successfully produced in the phosphate glass using this approach.

Enhanced 1.53 μm emission of Er{sup 3+} ions in phosphate glass via energy transfer from Cu{sup +} ions

DOE Office of Scientific and Technical Information (OSTI.GOV)

Jiménez, José A., E-mail: jose.jimenez@unf.edu; Sendova, Mariana

2014-07-21

Optimizing the efficiency of Er{sup 3+} emission in the near-infrared telecommunication window in glass matrices is currently a subject of great interest in photonics research. In this work, Cu{sup +} ions are shown to be successfully stabilized at a high concentration in Er-containing phosphate glass by a single-step melt-quench method, and demonstrated to transfer energy to Er{sup 3+} thereby enhancing the near-infrared emission about 15 times. The spectroscopic data indicate an energy conversion process where Cu{sup +} ions first absorb photons broadly around 360 nm and subsequently transfer energy from the Stokes-shifted emitting states to resonant Er{sup 3+} absorption transitions inmore » the visible. Consequently, the Er{sup 3+} electronic excited states decay and the {sup 4}I{sub 3/2} metastable state is populated, leading to the enhanced emission at 1.53 μm. Monovalent copper ions are thus recognized as sensitizers of Er{sup 3+} ions, suggesting the potential of Cu{sup +} co-doping for applications in the telecommunications, solar cells, and solid-state lasing realizable under broad band near-ultraviolet optical pumping.« less

Dry silver electromigration process for optical glass waveguide fabrication and fluxless bonding technology for photonics and MEMS packaging

NASA Astrophysics Data System (ADS)

Chuang, Ricky Wenkuei

2001-07-01

An effectively simple dry silver electromigration technology without the need of evaporating separate gold or aluminum film electrodes onto both sides of glass is reported to fabricate low-loss deep multimode planar and channel waveguides on BK7 and BF450 glass substrates. A relatively high electrical field ranging from 440 to 545 V/mm was applied to the glass to speed up the migration, while at the same time preventing silver ions that were driven into the glass from reducing into silver atom; a major contributor to waveguide loss. The deep planar and channel waveguides thus fabricated showed no discolors or cracks, of which the attenuation losses of less than 2dB/cm and 0.1dB/cm were later measured from channel waveguides constructed on the BK7 and BF450 glass substrates, respectively, using our 0.6328mum He-Ne laser edge-coupling setup. To complete the waveguide studies, the scanning electron microscope (SEM) equipped with energy-dispersive X-ray (EDX) detector was adopted to obtain the concentration profiles of silver and sodium ions distributed in a waveguiding region after the exchange. The EDX measurements acquired hereafter were then utilized along with the Gladstone-Dale relation altogether to deduce the refractive index profile; of which a nearly step-like profile was consistently deduced from every deep planar and channel waveguides fabricated. Finally, a numerical model utilizing the space charge approach was devised to explain the nonlinear current effect often observed during the actual waveguide fabrication. The simulation results have confirmed that the nonlinear current-versus-time profile obtained is mainly attributed to the inhomogeneous distribution of the electric field in the glass substrate due to a space charge region created by the separation between silver- and sodium-ion migration fronts as a result of their unequal mobilities; a phenomenon which is ultimately responsible for the eventual slow down in the ion exchange rate as monitored during the actual electromigration process. A fluxless oxidation-free bonding technology using multilayer composite solders based on the non eutectic binary alloys of indium-tin (In-Sn), silver-indium (Ag-In), gold-tin (Au-Sn), and bismuth-tin (Bi-Sn) has been established and studied to determine its applicability to photonics and MEMS packaging. The scanning acoustic microscopy (SAM) conducted on these solder samples has consistently shown that a nearly void-free joint fabricated from each non-eutectic binary alloy system can be reliably achieved. In addition, the scanning electron microscopy (SEM) equipped with the energy dispersive X-ray (EDX) detector was also performed on the cross section of each sample to determine its joint composition, especially of any sign of intermetallic compounds. These results will demonstrate that any intermetallic compound or phase present in a joint fabricated with a pre-determined multilayer composition based on a specific binary alloy system can be well understood and fully justified by correlating the experimental outcome with its respective binary phase diagram.

Erosion of water-based cements evaluated by volumetric and gravimetric methods.

PubMed

Nomoto, Rie; Uchida, Keiko; Momoi, Yasuko; McCabe, John F

2003-05-01

To compare the erosion of glass ionomer, zinc phosphate and polycarboxylate cements using volumetric and gravimetric methods. For the volumetric method, the eroded depth of cement placed in a cylindrical cavity in PMMA was measured using a dial gauge after immersion in an eroding solution. For the gravimetric method, the weight of the residue of a solution in which a cylindrical specimen had been immersed was measured. 0.02 M lactic acid solution (0.02 M acid) and 0.1 M lactic acid/sodium lactate buffer solution (0.1 M buffer) were used as eroding solutions. The pH of both solutions was 2.74 and the test period was 24 h. Ranking of eroded depth and weight of residue was polycarboxylate>zinc phosphate>glass ionomers. Differences in erosion were more clearly defined by differences in eroded depth than differences in weight of residue. In 0.02 M acid, the erosion of glass ionomer using the volumetric method was effected by the hygroscopic expansion. In 0.1 M buffer, the erosion for polycarboxylate and zinc phosphate using the volumetric method was much greater than that using the gravimetric method. This is explained by cryo-SEM images which show many holes in the surface of specimens after erosion. It appears that zinc oxide is dissolved leaving a spongy matrix which easily collapses under the force applied to the dial gauge during measurement. The volumetric method that employs eroded depth of cement using a 0.1 M buffer solution is able to quantify erosion and to make material comparisons.

Dynamics of asymmetric non-polymeric binary glass formers—A nuclear magnetic resonance and dielectric spectroscopy study

DOE Office of Scientific and Technical Information (OSTI.GOV)

Pötzschner, B.; Mohamed, F.; Lichtinger, A.

2015-10-21

We study a dynamically asymmetric binary glass former with the low-T{sub g} component m-tri-cresyl phosphate (m-TCP: T{sub g} = 206 K) and a spirobichroman derivative as a non-polymeric high-T{sub g} component (T{sub g} = 382 K) by means of {sup 1}H nuclear magnetic resonance (NMR), {sup 31}P NMR, and dielectric spectroscopy which allow component-selectively probing the dynamics. The entire concentration range is covered, and two main relaxation processes with two T{sub g} are identified, T{sub g1} and T{sub g2}. The slower one is attributed to the high-T{sub g} component (α{sub 1}-process), and the faster one is related to the m-TCPmore » molecules (α{sub 2}-process). Yet, there are indications that a small fraction of m-TCP is associated also with the α{sub 1}-process. While the α{sub 1}-relaxation only weakly broadens upon adding m-TCP, the α{sub 2}-relaxation becomes extremely stretched leading to quasi-logarithmic correlation functions at low m-TCP concentrations—as probed by {sup 31}P NMR stimulated echo experiments. Frequency-temperature superposition does not apply for the α{sub 2}-process and it reflects an isotropic, liquid-like motion which is observed even below T{sub g1}, i.e., in the matrix of the arrested high-T{sub g} molecules. As proven by 2D {sup 31}P NMR, the corresponding dynamic heterogeneities are of transient nature, i.e., exchange occurs within the distribution G(lnτ{sub α2}). At T{sub g1} a crossover is found for the temperature dependence of (mean) τ{sub α2}(T) from non-Arrhenius above to Arrhenius below T{sub g1} which is attributed to intrinsic confinement effects. This “fragile-to-strong” transition also leads to a re-decrease of T{sub g2}(c{sub m−TCP}) at low concentration c{sub m−TCP}, i.e., a maximum is observed in T{sub g2}(c{sub m−TCP}) while T{sub g1}(c{sub m−TCP}) displays the well-known plasticizer effect. Although only non-polymeric components are involved, we re-discover essentially all features previously reported for polymer-plasticizer systems.« less

Judd-Ofelt analysis and energy transfer processes of Er3+ and Nd3+ doped fluoroaluminate glasses with low phosphate content

NASA Astrophysics Data System (ADS)

Huang, Feifei; Zhang, Yu; Hu, Lili; Chen, Danping

2014-12-01

Spectroscopic property and energy transfer processes of singly doped and codoped Er3+ and Nd3+ fluoroaluminate glasses with low phosphate content are systematically analyzed. The absorption spectra of these glasses are tested, and the Judd-Ofelt (J-O) and radiative parameters are discussed based on J-O theory and the parameters changes substantially because of the other codoping ions. As for Nd3+: the main emission bands at 0.9 and 1.05 μm decrease in the codoped sample under the excitation of an 800 nm laser diode from the emission spectra because the Er3+: 4I11/2 level reduces the Nd3+: 4F3/2 level effectively through the energy transfer process Nd3+: 4F3/2 → Er3+: 4I11/2. For Er3+, the emission at 1.5 μm is restrained by codoping with Nd3+ ions from the energy transfer process Er3+: 4I13/2 → Nd3+: 4I15/2. The emission at 2.7 μm is enhanced because the Nd3+ ions deplete the lower level and exert a positive effect on the upper laser level. The microparameters of the energy transfer between the Er3+ and Nd3+ ions are calculated and discussed using Forster-Dexter theory. The energy transfer efficiencies of the Nd3+: 4F3/2 to the Er3+: 4I11/2 and the Er3+: 4I13/2 to the Nd3+: 4I15/2 are 28.8% and 74.5%, respectively. These results indicate that Nd3+ can be an efficient sensitizer for Er3+ to obtain Mid-infrared (Mid-IR) emission and the codoped Er3+/Nd3+ fluoroaluminate glass with low phosphate content is suitable to be used as the fiber optical gain media for 2.7 μm laser generation.

Development of an Agrobacterium-based transformation system for Rhizoctonia solani

USDA-ARS?s Scientific Manuscript database

A 8.7 kb binary vector containing the 1.9 kb hygromycin B phosphortransferase (hyg) gene was constructed with promoter and terminator regions from the glyceraldehyde-3-phosphate- dehydrogenase (gpd) gene of Rhizoctonia solani anastomosis group 3 (AG-3) at the 5'- and 3'- gene termini of hyg. Promot...

Vitrified chemically bonded phosphate ceramics for immobilization of radioisotopes

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wagh, Arun S.

2016-04-05

A method of immobilizing a radioisotope and vitrified chemically bonded phosphate ceramic (CBPC) articles formed by the method are described. The method comprises combining a radioisotope-containing material, MgO, a source of phosphate, and optionally, a reducing agent, in water at a temperature of less than 100.degree. C. to form a slurry; curing the slurry to form a solid intermediate CBPC article comprising the radioisotope therefrom; comminuting the intermediate CBPC article, mixing the comminuted material with glass frits, and heating the mixture at a temperature in the range of about 900 to about 1500.degree. C. to form a vitrified CBPC articlemore » comprising the radioisotope immobilized therein.« less

Elastic moduli of a Brownian colloidal glass former

NASA Astrophysics Data System (ADS)

Fritschi, S.; Fuchs, M.

2018-01-01

The static, dynamic and flow-dependent shear moduli of a binary mixture of Brownian hard disks are studied by an event-driven molecular dynamics simulation. Thereby, the emergence of rigidity close to the glass transition encoded in the static shear modulus G_∞ is accessed by three methods. Results from shear stress auto-correlation functions, elastic dispersion relations, and the elastic response to strain deformations upon the start-up of shear flow are compared. This enables one to sample the time-dependent shear modulus G(t) consistently over several decades in time. By that a very precise specification of the glass transition point and of G_∞ is feasible. Predictions by mode coupling theory of a finite shear modulus at the glass transition, of α-scaling in fluid states close to the transition, and of shear induced decay in yielding glass states are tested and broadly verified.

A pseudopotential approach to the superconducting state properties of Cu Zr metallic glasses

NASA Astrophysics Data System (ADS)

Sharma, Smita; Sharma, K. S.; Khan, Haniph

2004-03-01

The superconducting state properties of the nine metallic glasses of Cu1-cZrc system have been investigated in the BCS-Eliashberg-McMillan framework by extending this theory to the binary metallic glasses. The values of superconducting state parameters, namely, the electron-phonon coupling strength (lgr), Coulomb pseudopotential (mgr*), transition temperature (Tc), isotope effect exponent (agr) and interaction strength (NoV) of Cu-Zr metallic glasses in the range 0.40 \\le c \\le 0.75 of Zr in Cu have been worked out using Ashcroft's potential along with the RPA form of the dielectric screening. The present results for Tc show an excellent agreement with the experimental data. The values of Tc, agr and NoV are found to decrease continuously with increase of the Cu concentration in Zr, showing that Zr rich Cu-Zr glasses are favoured materials for superconductivity.

Effect of surface treatment on the corrosion properties of magnesium-based fibre metal laminate

NASA Astrophysics Data System (ADS)

Zhang, X.; Zhang, Y.; Ma, Q. Y.; Dai, Y.; Hu, F. P.; Wei, G. B.; Xu, T. C.; Zeng, Q. W.; Wang, S. Z.; Xie, W. D.

2017-02-01

The surface roughness, weight of phosphating film and wettability of magnesium alloy substrates after abrasion and phosphating treatment were investigated in this work. The interfacial bonding and corrosion properties of a magnesium-based fibre metal laminate (MgFML) were analysed. The results showed that the wettability of the magnesium alloy was greatly influenced by the surface roughness, and the rough surface possessed a larger surface energy and better wettability. The surface energy and wettability of the magnesium alloy were significantly improved by the phosphating treatment. After phosphating for 5 min, a phosphating film with a double-layer structure was formed on the magnesium substrate, and the weight of the phosphating film and the surface energy reached their maximum values. The surface energies of the phosphated substrate after abrasion with #120 and #3000 grit abrasive papers were 84.31 mJ/m2 and 83.65 mJ/m2, respectively. The wettability of the phosphated magnesium was significantly better than the abraded magnesium. The phosphated AZ31B sheet had a better corrosion resistance than the abraded AZ31B sheet within short times. The corrosion resistance of the magnesium alloy was greatly increased by being composited with glass fibre/epoxy prepregs.

The effect of solute on the homogeneous crystal nucleation frequency in metallic melts

NASA Technical Reports Server (NTRS)

Thompson, C. V.; Spaepen, F.

1982-01-01

A complete calculation that extends the classical theory for crystal nucleation in pure melts to binary alloys has been made. Using a regular solution model, approximate expressions have been developed for the free energy change upon crystallization as a function of solute concentration. They are used, together with model-based estimates of the interfacial tension, to calculate the nucleation frequency. The predictions of the theory for the maximum attainable undercooling are compared with existing experimental results for non-glass forming alloys. The theory is also applied to several easy glass-forming alloys (Pd-Si, Au-Si, Fe-B) for qualitative comparison with the present experimental experience on the ease of glass formation, and for assessment of the potential for formation of the glass in bulk.

FTIR of binary lead borate glass: Structural investigation

NASA Astrophysics Data System (ADS)

Othman, H. A.; Elkholy, H. S.; Hager, I. Z.

2016-02-01

The glass samples were prepared according to the following formula: (100-x) B2O3 - x PbO, where x = 20-80 mol% by melt quenching method. The density of the prepared samples was measured and molar volume was calculated. IR spectra were measured for the prepared samples to investigate the glass structure. The IR spectra were deconvoluted using curves of Gaussian shape at approximately the same frequencies. The deconvoluted data were used to study the effect of PbO content on all the structural borate groups. Some structural parameters such as density, packing density, bond length and bond force constant were theoretically calculated and were compared to the obtained experimental results. Deviation between the experimental and theoretically calculated parameters reflects the dual role of PbO content on the network of borate glass.

Structural studies of gels and gel-glasses in the SiO2-GeO2 system using vibrational spectroscopy

NASA Technical Reports Server (NTRS)

Mukherjee, Shyama P.; Sharma, Shiv K.

1986-01-01

GeO2 gel and gels in the SiO2-GeO2 system synthesized by the hydrolytic polycondensation of metal alkoxides have been studied by infrared and Raman spectroscopic techniques. The molecular structures, hydroxyl contents, and crystallinity of gels and gel-glasses in relation to the thermal history and GeO2 concentration were investigated. The binary compositions having up to 70 mol percent GeO2 were examined.

Structural investigation of MO⋅P{sub 2}O{sub 5}⋅Li{sub 2}O (MO = Fe{sub 2}O{sub 3} or V{sub 2}O{sub 5}) glass systems by FTIR spectroscopy

DOE Office of Scientific and Technical Information (OSTI.GOV)

Andronache, Constantin I., E-mail: androtin03@yahoo.com; Racolta, Dania, E-mail: androtin03@yahoo.com

2014-11-24

Glasses from the systems xMO⋅(100−x)[P{sub 2}O{sub 5}⋅Li{sub 2}O] (MO = Fe{sub 2}O{sub 3} or V{sub 2}O{sub 5}) with 0 ≤ x ≤ mol % were prepared in the same conditions and characterized by IR spectroscopy. It was established the mode in which both Fe{sub 2}O{sub 3} and V{sub 2}O{sub 5} influences the local structure of these glasses. The iron ions generally modify in a different way the local structure of these glasses then vanadium ions. The results shown that phosphate units are the main structural units of glass system and the iron and vanadium ions are located in the network.

LASERS: Ultimate energy parameters of the radiation emitted from neodymium-glass laser systems

NASA Astrophysics Data System (ADS)

Eshmemet'eva, E. V.; Korolev, V. I.; Mesnyankin, E. P.; Serebryakov, V. A.; Shashkin, V. V.; Yashin, V. E.

1992-09-01

An experimental investigation was made of the energy conversion efficiency and of the effects of stimulated Brillouin scattering and of optical breakdown, limiting the maximum energy density obtained from several phosphate and silicate neodymium glasses when the duration of the output pulses was 50-150 ns. The experimental results were used to develop a numerical model for calculation of the gain allowing for these processes. A design was developed for an amplifier with ultimate radiation characteristics.

Passive mode locking of 2.09 microm Cr,Tm,Ho:Y3Sc2Al3O12 laser using PbS quantum-dot-doped glass.

PubMed

Denisov, Igor A; Skoptsov, Nikolai A; Gaponenko, Maxim S; Malyarevich, Alexander M; Yumashev, Konstantin V; Lipovskii, Andrei A

2009-11-01

Passive Q-switched mode locking of a 2.09 microm flashlamp-pumped Cr(3+),Tm(3+),Ho(3+):Y(3)Sc(2)Al(3)O(12) laser by use of a phosphate glass doped with PbS quantum dots of 5 nm in radius was demonstrated. Mode-locked pulses of 290 ps in duration and up to 0.5 mJ in energy were registered.

Annealing dynamics of waveguide Bragg gratings: evidence of femtosecond laser induced colour centres.

PubMed

Dekker, P; Ams, M; Marshall, G D; Little, D J; Withford, M J

2010-02-15

There is still significant speculation regarding the nature of femtosecond laser induced index change in bulk glasses with colour centre formation and densification the main candidates. In the work presented here, we fabricated waveguide Bragg gratings in doped and undoped phosphate glasses and use these as a diagnostic for monitoring subtle changes in the induced refractive index during photo- and thermal annealing experiments. Reductions in grating strengths during such experiments were attributed to the annihilation of colour centres.

Biocompatible Zr-Al-Fe bulk metallic glasses with large plasticity

NASA Astrophysics Data System (ADS)

Hua, NengBin; Li, Ran; Wang, JianFeng; Zhang, Tao

2012-09-01

In the present study, high-zirconium ternary Zr-Al-Fe bulk metallic glasses (BMGs) with low Young's modulus and good plasticity were developed. Zr75Al7.5Fe17.5 BMG exhibits a low Young's modulus of 70 GPa and high Poisson's ratio of 0.403. Pronounced plasticity was demonstrated under both compression and bending conditions for the BMGs. Furthermore, the alloys show high corrosion resistance in phosphate buffered solution. The combination of desirable mechanical and chemical properties implies potential for biomedical applications.

Effect of sub-Tg annealing on CuZr and AlSm glasses: A molecular dynamics study

NASA Astrophysics Data System (ADS)

Sun, Yang; Zhang, Feng; Zhang, Yue; Ye, Zhuo; Mendelev, Mikhail; Wang, Cai-Zhuang; Ho, Kai-Ming

Cu65Zr35 and Al90Sm10 glasses, which represent strong and marginal binary metallic glass formers, respectively, were developed with a sub-Tg annealing method using Molecular Dynamics simulations. The short-range order (SRO) in both systems was characterized based on the concept of ``crystal gene'' that we established recently. Furthermore, we found that while the local clusters representing the dominant short-range order form an ever-more pronounced interpenetrating network with slower cooling rates in Cu65Zr35 glasses, the interpenetration of SRO in Al90Sm10 glasses only shows a weak dependence on the cooling rate. This clear difference in the connectivity of the SRO, which can characterize the medium-range order (MRO), could contribute to the different glass forming abilities of both systems. Work at Ames Laboratory was supported by the U.S. Department of Energy, Basic Energy Sciences, Materials Science and Engineering Division, under Contract No. DE-AC02-07CH11358.

Improvement in degradability of 58s glass scaffolds by ZnO and β-TCP modification

PubMed Central

Shuai, Cijun; Cao, Yiyuan; Dan, Gao; Gao, Chengde; Feng, Pei; Wu, Ping

2016-01-01

ABSTRACT 58s bioactive glass shows great potential for bone defects repair. However, at early repairing stage, the degradation rate of 58s glass is too fast due to the fast ion-exchange. At later repairing stage, the degradation rate of 58s glass is too slow due to the high dense mineral layer. In this work, Zinc oxide (ZnO) and β-tricalcium phosphate (β-TCP) were introduced into 58s glass bone scaffolds to improve the degradability. The results showed that ZnO could decrease the degradation rate and promote the stability of 58s glass at early repairing stage. Moreover, the presence of β-TCP appeared to increase the degradation rate at a later stage of repairing. Furthermore, in vitro biocompatibility study, carried out using human osteoblast-like cells (MG63), demonstrated that ZnO and β-TCP enhanced cell attachment and proliferation. The study provided a reference for further research in bone tissue engineering. PMID:27710432

Molybdenum modified phosphate glasses studied by 31P MAS NMR and Raman spectroscopy.

PubMed

Szumera, Magdalena

2015-02-25

Glasses have been synthesized in the system P2O5-SiO2-K2O-MgO-CaO modified by addition of MoO3. Glasses were prepared by conventional fusion method from 40 g batches. The influence of Mo-cations on the analysed glass structure was investigated by means of Raman and (31)P MAS-NMR techniques. It has been found that molybdate units can form Mo[MoO4/MoO6]-O-P and/or Mo[MoO4/MoO6]-O-Si bonds with non-bridging oxygens atoms of Q2 methaphosphate units, resulting in the transformation of chain methaphosphate structure into pyrophosphate and finally into orthophosphate structure. It has been also found that increasing amount of MoO3 in the structure of investigated glasses causes their gradual depolymerization and molybdenum ions in the analysed glass matrix act as modifying cations. Copyright © 2014 Elsevier B.V. All rights reserved.

Preparation and application of nanoglued binary titania-silica aerogel.

PubMed

Luo, Liang; Cooper, Adrienne T; Fan, Maohong

2009-01-15

Nanoglued binary titania (TiO2)-silica (SiO2) aerogel, as a novel type of photocatalyst, has been synthesized on glass substrates. Using an about-to-gel SiO2 sol as nanoglue, anatase TiO2 aerogel was immobilized into a three-dimensional mesoporous network of the SiO2. Factorial designs were employed to optimize both TiO2 aerogel and binary TiO2-SiO2 aerogel synthesis. Characterization of the as-prepared TiO2 and binary samples by surface area, porosity, and surface chemical composition showed that the photocatalysts were high-surface-area nanoporous materials, with a Ti4+ valency. The binary aerogel exhibited high photocatalytic activity for the degradation of methylene blue (MB) under simulated solar light; the reaction followed the pseudo first-order Langmuir-Hinshelwood (L-H) kinetic model. Fluorescence spectroscopy revealed that the hydroxyl (*OH) radical was formed during the illumination of the binary TiO2-SiO2 aerogel in a solution of probe molecules, which corroborates the probable mechanism of hydroxyl radical oxidation of contaminants in photocatalytic reactions.

The kinetics of crystallization of molten binary and ternary oxide systems and their application to the origination of high modulus glass fibers

NASA Technical Reports Server (NTRS)

Bacon, J. F.

1971-01-01

Emphasis on the consideration of glass formation on a kinetic process made it possible to think of glass compositions different from those normally employed in the manufacture of glass fibers. Approximately 450 new glass compositions were prepared and three dozen of these compositions have values for Young's modulus measured on bulk specimens greater than nineteen million pounds per square inch. Of the new glasses about a hundred could be drawn into fibers by mechanical methods at high speeds. The fiber which has a Young's modulus measured on the fiber of 18.6 million pounds per square inch and has been prepared in quantity as a monofilament (to date more than 150 million lineal feet of 0.2 to 0.4 mil fiber have been produced). This fiber has also been successfully incorporated both in epoxy and polyimide matrices. The epoxy resin composite has shown a modulus forty percent better than that achievable using the most common grade of competitive glass fiber, and twenty percent better than that obtainable with the best available grade of competitive glass fiber. Other glass fibers of even higher modulus have been developed.

Functionally graded bioactive glass coating on magnesia partially stabilized zirconia (Mg-PSZ) for enhanced biocompatibility.

PubMed

Rahaman, Mohamed N; Li, Yadong; Bal, B Sonny; Huang, Wenhai

2008-06-01

The coating of magnesia partially stabilized zirconia (Mg-PSZ) with a bioactive glass was investigated for enhancing the bioactivity and bone-bonding ability of Mg-PSZ orthopedic implants. Individual coatings of three different bioactive glasses were prepared by depositing a concentrated suspension of the glass particles on Mg-PSZ substrates, followed by sintering at temperatures between 750 degrees C and 850 degrees C. Two silicate-based glass compositions (designated 13-93 and 6P68), and a borosilicate glass composition (H12) were investigated. The microstructure and adhesive strength of the coatings were characterized, and the in vitro bioactivity of the glasses was compared by measuring their conversion kinetics to hydroxyapatite in an aqueous phosphate solution at 37 degrees C. The 6P68 glass provided the highest adhesive strength (40 +/- 2 MPa) but showed very limited bioactivity, whereas the H12 glass had lower adhesive strength (18 +/- 2 MPa) but the highest bioactivity. A functionally graded coating, consisting of a 6P68 interfacial layer and an H12 surface layer, was developed to provide a coating with high adhesive strength coupled with rapid in vitro bioactivity.

Acid Vapor Weathering of Apatite and Implications for Mars

NASA Technical Reports Server (NTRS)

Hausrath, E. M.; Golden, D. C.; Morris, R. V.; Ming, D. W.

2008-01-01

Phosphorus is an essential nutrient for terrestrial life, and therefore may be important in characterizing habitability on Mars. In addition, phosphate mobility on Mars has been postulated as an indicator of early aqueous activity [1]. Rock surfaces analyzed by the Spirit Mars Exploration Rover indicate elemental concentrations consistent with the loss of a phosphate-containing mineral [2], and the highly altered Paso Robles deposit contains 5% P2O5, modeled as 8-10 % phosphate [3]. Depending on the pH of the solution, phosphate can exist as one of four charge states, which can affect its solubility, reactivity and mobility. Phosphate may therefore prove a useful and interesting tracer of alteration conditions on Mars. Acid vapor weathering has been previously studied as a potentially important process on Mars [4-6], and Paso Robles may have been formed by reaction of volcanic vapors with phosphate-bearing rock [3, 7]. Here we present preliminary results of acid vapor reactions in a Parr vessel [6] using fluorapatite, olivine and glass as single phases and in a mixture.

OXIDATION-RESISTANT COATING ON ARTICLES OF YTTRIUM METAL

DOEpatents

Wilder, D.R.; Wirkus, C.D.

1963-11-01

A process for protecting yttrium metal from oxidation by applying thereto and firing thereon a liquid suspension of a fritted ground silicate or phosphate glass plus from 5 to 35% by weight of CeO/sub 2/ is presented. (AEC)

Beyond packing of hard spheres: The effects of core softness, non-additivity, intermediate-range repulsion, and many-body interactions on the glass-forming ability of bulk metallic glasses

DOE Office of Scientific and Technical Information (OSTI.GOV)

Zhang, Kai; Fan, Meng; Liu, Yanhui

When a liquid is cooled well below its melting temperature at a rate that exceeds the critical cooling rate R{sub c}, the crystalline state is bypassed and a metastable, amorphous glassy state forms instead. R{sub c} (or the corresponding critical casting thickness d{sub c}) characterizes the glass-forming ability (GFA) of each material. While silica is an excellent glass-former with small R{sub c} < 10{sup −2} K/s, pure metals and most alloys are typically poor glass-formers with large R{sub c} > 10{sup 10} K/s. Only in the past thirty years have bulk metallic glasses (BMGs) been identified with R{sub c} approachingmore » that for silica. Recent simulations have shown that simple, hard-sphere models are able to identify the atomic size ratio and number fraction regime where BMGs exist with critical cooling rates more than 13 orders of magnitude smaller than those for pure metals. However, there are a number of other features of interatomic potentials beyond hard-core interactions. How do these other features affect the glass-forming ability of BMGs? In this manuscript, we perform molecular dynamics simulations to determine how variations in the softness and non-additivity of the repulsive core and form of the interatomic pair potential at intermediate distances affect the GFA of binary alloys. These variations in the interatomic pair potential allow us to introduce geometric frustration and change the crystal phases that compete with glass formation. We also investigate the effect of tuning the strength of the many-body interactions from zero to the full embedded atom model on the GFA for pure metals. We then employ the full embedded atom model for binary BMGs and show that hard-core interactions play the dominant role in setting the GFA of alloys, while other features of the interatomic potential only change the GFA by one to two orders of magnitude. Despite their perturbative effect, understanding the detailed form of the intermetallic potential is important for designing BMGs with cm or greater casting thickness.« less

Phosphorus-31, sup 15 N, and sup 13 C NMR of glyphosate: Comparison of pH titrations to the herbicidal dead-end complex with 5-enolpyruvoylshikimate-3-phosphate synthase

DOE Office of Scientific and Technical Information (OSTI.GOV)

Castellino, S.; Leo, G.C.; Sammons, R.D.

1989-05-02

The herbicidal dead-end ternary complex (E{sup S3P}{sub Glyph}) of glyphosate (N-(phosphonomethyl)glycine) with 5-enolpyruvoylshikimate-3-phosphate synthase (EPSPS) and the substrate shikimate 3-phosphate (S3P) has been characterized by {sup 31}P, {sup 15}N, and {sup 13}C NMR. The NMR spectra of EPSPS-bound glyphosate show unique chemical shifts ({delta}) for each of the three nuclei. By {sup 31}P NMR, glyphosate in the dead-end complex is a distinct species 3.5 ppm downfield from free glyphosate. The {sup 13}C signal of glyphosate in the dead-end complex is shifted 4 ppm downfield from that of free glyphosate. The {sup 15}N signal for glyphosate (99%) in the dead-end complexmore » is 5 ppm further downfield than that of any free zwitterionic species and 10 ppm downfield from that of the average free species at pH 10.1. The structures of each ionic state of glyphosate are modeled with force field calculations by using MacroModel. A correlation is made for the {sup 31}P {delta} and the C-P-O bond angle, and the {sup 13}C and {sup 15}N {delta} values are postulated to be related to C-C-O and C-N-C bond angles, respectively. The downfield {sup 31}P chemical shift perturbation for S3P in the EPSPS binary complex is consistent with ionization of the 3-phosphate of S3P upon binding. Comparison with the S3P {sup 31}P {delta} vs pH titration curve specifies predominantly the dianion of the 3-phosphate in the E{sup S3P} binary complex, while the E{sup S3P}{sub Glyph} complex indicates net protonation at the 3-phosphate. Chemical shift perturbations of this latter type may be explained by changes in the O-P-O bond angle.« less

Direct observation of molecular cooperativity near the glass transition.

PubMed

Russell, E V; Israeloff, N E

2000-12-07

The increasingly sluggish response of a supercooled liquid as it nears its glass transition (for example, refrigerated honey) is prototypical of glassy dynamics found in proteins, neural networks and superconductors. The notion that molecules rearrange cooperatively has long been postulated to explain diverging relaxation times and broadened (non-exponential) response functions near the glass transition. Recently, cooperativity was observed and analysed in colloid glasses and in simulations of binary liquids well above the glass transition. But nanometre-scale studies of cooperativity at the molecular glass transition are lacking. Important issues to be resolved include the precise form of the cooperativity and its length scale, and whether the broadened response is intrinsic to individual cooperative regions, or arises only from heterogeneity in an ensemble of such regions. Here we describe direct observations of molecular cooperativity near the glass transition in polyvinylacetate (PVAc), using nanometre-scale probing of dielectric fluctuations. Molecular clusters switched spontaneously among two to four distinct configurations, producing random telegraph noise. Our analysis of these noise signals and their power spectra reveals that individual clusters exhibit transient dynamical heterogeneity and non-exponential kinetics.

Structure-composition trends in multicomponent borosilicate-based glasses deduced from molecular dynamics simulations with improved B-O and P-O force fields.

PubMed

Stevensson, Baltzar; Yu, Yang; Edén, Mattias

2018-03-28

We present a comprehensive molecular dynamics (MD) simulation study of composition-structure trends in a set of 25 glasses of widely spanning compositions from the following four systems of increasing complexity: Na 2 O-B 2 O 3 , Na 2 O-B 2 O 3 -SiO 2 , Na 2 O-CaO-SiO 2 -P 2 O 5 , and Na 2 O-CaO-B 2 O 3 -SiO 2 -P 2 O 5 . The simulations involved new B-O and P-O potential parameters developed within the polarizable shell-model framework, thereby combining the beneficial features of an overall high accuracy and excellent transferability among different glass systems and compositions: this was confirmed by the good accordance with experimental data on the relative BO 3 /BO 4 populations in borate and boro(phospho)silicate networks, as well as with the orthophosphate fractions in bioactive (boro)phosphosilicate glasses, which is believed to strongly influence their bone-bonding properties. The bearing of the simulated melt-cooling rate on the borate/phosphate speciations is discussed. Each local {BO 3 , BO 4 , SiO 4 , PO 4 } coordination environment remained independent of the precise set of co-existing network formers, while all trends observed in bond-lengths/angles mainly reflected the glass-network polymerization, i.e., the relative amounts of bridging oxygen (BO) and non-bridging oxygen (NBO) species. The structural roles of the Na + /Ca 2+ cations were also probed, targeting their local coordination environments and their relative preferences to associate with the various borate, silicate, and phosphate moieties. We evaluate and discuss the common classification of alkali/alkaline-earth metal ions as charge-compensators of either BO 4 tetrahedra or NBO anions in borosilicate glasses, also encompassing the less explored NBO-rich regime: the Na + /Ca 2+ cations mainly associate with BO/NBO species of SiO 4 /BO 3 groups, with significant relative Na-BO 4 contacts only observed in B-rich glass networks devoid of NBO species, whereas NBO-rich glass networks also reveal substantial amounts of NBO-bearing BO 4 tetrahedra.

A unified in vitro evaluation for apatite-forming ability of bioactive glasses and their variants.

PubMed

Maçon, Anthony L B; Kim, Taek B; Valliant, Esther M; Goetschius, Kathryn; Brow, Richard K; Day, Delbert E; Hoppe, Alexander; Boccaccini, Aldo R; Kim, Ill Yong; Ohtsuki, Chikara; Kokubo, Tadashi; Osaka, Akiyoshi; Vallet-Regí, Maria; Arcos, Daniel; Fraile, Leandro; Salinas, Antonio J; Teixeira, Alexandra V; Vueva, Yuliya; Almeida, Rui M; Miola, Marta; Vitale-Brovarone, Chiara; Verné, Enrica; Höland, Wolfram; Jones, Julian R

2015-02-01

The aim of this study was to propose and validate a new unified method for testing dissolution rates of bioactive glasses and their variants, and the formation of calcium phosphate layer formation on their surface, which is an indicator of bioactivity. At present, comparison in the literature is difficult as many groups use different testing protocols. An ISO standard covers the use of simulated body fluid on standard shape materials but it does not take into account that bioactive glasses can have very different specific surface areas, as for glass powders. Validation of the proposed modified test was through round robin testing and comparison to the ISO standard where appropriate. The proposed test uses fixed mass per solution volume ratio and agitated solution. The round robin study showed differences in hydroxyapatite nucleation on glasses of different composition and between glasses of the same composition but different particle size. The results were reproducible between research facilities. Researchers should use this method when testing new glasses, or their variants, to enable comparison between the literature in the future.

Very high numerical aperture light transmitting device

DOEpatents

Allison, Stephen W.; Boatner, Lynn A.; Sales, Brian C.

1998-01-01

A new light-transmitting device using a SCIN glass core and a novel calcium sodium cladding has been developed. The very high index of refraction, radiation hardness, similar solubility for rare earths and similar melt and viscosity characteristics of core and cladding materials makes them attractive for several applications such as high-numerical-aperture optical fibers and specialty lenses. Optical fibers up to 60 m in length have been drawn, and several simple lenses have been designed, ground, and polished. Preliminary results on the ability to directly cast optical components of lead-indium phosphate glass are also discussed as well as the suitability of these glasses as a host medium for rare-earth ion lasers and amplifiers.

Emission characteristics of holmium ions in fluoro-phosphate glasses for photonic applications

DOE Office of Scientific and Technical Information (OSTI.GOV)

Babu, S.; Ratnakaram, Y. C., E-mail: ratnakaramsvu@gmail.com

2016-05-23

Optical properties of Ho{sup 3+} doped different fluorophosphate (FP) glasses have been synthesized and discussed. Thermal properties have been studied through differential scanning calorimetry (DSC).The Judd-Ofelt (J-O) intensity parameters Ω{sub λ} (λ= 2, 4, 6) from absorption spectra have been evaluated. Various radiative parameters have been obtained for the different excited states using J-O theory. From the emission spectra, different laser properties have been studied and discussed. The nature of decay curve analysis was performed for the {sup 5}F{sub 4}({sup 5}S{sub 2}) level. These glasses are expected to give interesting application in the field of photonic applications.

Radiophotoluminescent and Tenebrescent Glasses

DTIC Science & Technology

1951-11-24

Mineral Industries | Pennsylvania State College State College, Pennsylvania -j-- Copy No. 42 < Dr; G. Monk Senior Physicist , Remote Control...the quaternary system A^Og-ELO-? P2Oc-BaO, In order to better understand this fact stapler binary and ternary compositions were considered, The

Scintillation properties of phosphate-borate-fluoride glass doped with Tb3+/Pr3+

NASA Astrophysics Data System (ADS)

Valiev, D.; Stepanov, S.; Polisadova, E.; Yao, G.

2018-06-01

Scintillation glass doped with Tb3+ and Pr3+ ions with different concentrations were prepared by the melt-quenching method. Optical, photoluminescence and decay kinetic characteristics of the pulse cathodoluminescence (PCL) were investigated. It was shown that the absorption coefficient of the induced absorption in the visible range of the spectrum decreases significantly with the increase of the Pr2O3 content starting from 0.2 to 1 wt%. There was the difference in the luminescence spectra of the glass at a selective and non-selective type of excitation. The "green" emission (λem= 542 nm, 5D4→7F5 radiative transition of Tb3+ ions) was excited an electron beam. The "red" emission (λem= 600 nm, 3P0→3H6 radiative transition of Pr3+ ion) was observed under selective excitation action (λexc= 450 nm). It was demonstrated that decreasing of intensity the main bands of Tb3+ ions at 487, 544, 622 nm connected with increases of concentration Pr3+ ions. The luminescence decay time of terbium ions at 487, 544, 622 nm emission bands depend on Pr3+ concentration. The tendency of reducing the luminescence decay time in the main luminescence bands of Tb3+ ions at increasing the Pr3+ concentration was presented. The results showed that Tb3+/ Pr3+ co-doped phosphate-borate-fluoride glasses are promising non-crystalline scintillation materials.

Separating and stabilizing phosphate from high-level radioactive waste: process development and spectroscopic monitoring.

PubMed

Lumetta, Gregg J; Braley, Jenifer C; Peterson, James M; Bryan, Samuel A; Levitskaia, Tatiana G

2012-06-05

Removing phosphate from alkaline high-level waste sludges at the Department of Energy's Hanford Site in Washington State is necessary to increase the waste loading in the borosilicate glass waste form that will be used to immobilize the highly radioactive fraction of these wastes. We are developing a process which first leaches phosphate from the high-level waste solids with aqueous sodium hydroxide, and then isolates the phosphate by precipitation with calcium oxide. Tests with actual tank waste confirmed that this process is an effective method of phosphate removal from the sludge and offers an additional option for managing the phosphorus in the Hanford tank waste solids. The presence of vibrationally active species, such as nitrate and phosphate ions, in the tank waste processing streams makes the phosphate removal process an ideal candidate for monitoring by Raman or infrared spectroscopic means. As a proof-of-principle demonstration, Raman and Fourier transform infrared (FTIR) spectra were acquired for all phases during a test of the process with actual tank waste. Quantitative determination of phosphate, nitrate, and sulfate in the liquid phases was achieved by Raman spectroscopy, demonstrating the applicability of Raman spectroscopy for the monitoring of these species in the tank waste process streams.

Study of hydraulic properties of binary beads mixture as porous media in sustainable urban drainage system

NASA Astrophysics Data System (ADS)

Abdullah, Muhammad Faiz; Puay, How Tion; Zakaria, Nor Azazi

2017-10-01

Sustainable Urban Drainage System (SuDS) such as swales and rain gardens is showing growing popularity as a green technology for stormwater management and it can be used in all types of development to provide a natural approach to managing drainage. Soil permeability is a critical factor in selecting the right SuDS technique for a site. On this basis, we have set up a laboratory experiment to investigate the porosity and saturated hydraulic conductivity of single size and binary (two sizes) mixture using column-test as a preliminary investigation with two sets of glass beads with different sizes are used in this study. The porosity and saturated hydraulic conductivity for varies volume fraction of the course and fine glass beads were measured. It was found that the porosity of the binary mixture does not increase with the increment of the ratio of coarse to fine beads until the volume fraction of fine particles is equal to the coarse component. Saturated hydraulic conductivity result shows that the assumption of random packing was not achieved at the higher coarse ratio where most of the fine particles tend to sit at the bottom of the column forming separate layers which lower the overall hydraulic conductivity value.

Time-domain diffuse optics using bioresorbable fibers: a proof-of-principle study

NASA Astrophysics Data System (ADS)

Di Sieno, Laura; Boetti, Nadia G.; Dalla Mora, Alberto; Pugliese, Diego; Farina, Andrea; Konugolu Venkata Sekar, Sanathana; Ceci-Ginistrelli, Edoardo; Janner, Davide; Pifferi, Antonio; Milanese, Daniel

2017-07-01

We show for the first time the aptness of Calcium Phosphate Glass-based bioresorbable fibers for time-domain diffuse optics using tests described by a standardized protocol and we also present a spectroscopic measurement on a chicken breast.

Long-term conversion of 45S5 bioactive glass-ceramic microspheres in aqueous phosphate solution.

PubMed

Fu, Hailuo; Rahaman, Mohamed N; Day, Delbert E; Huang, Wenhai

2012-05-01

The conversion of 45S5 glass and glass-ceramics to a hydroxyapatite (HA)-like material in vitro has been studied extensively, but only for short reaction times (typically <3 months). In this paper, we report for the first time on the long-term conversion of 45S5 glass-ceramic microspheres (designated 45S5c) in an aqueous phosphate solution. Microspheres of 45S5c (75-150 μm) were immersed for 10 years at room temperature (~25 °C) in K(2)HPO(4) solution with a concentration of 0.01 M or 1.0 M, and with a starting pH of 7.0 or 9.5. The reacted 45S5c microspheres and solutions were analyzed using structural and analytical techniques. Only 25-45 vol% of the 45S5c microspheres were converted to an HA-like material after the 10 year reaction. In solutions with a starting pH of 9.5, an increase in the K(2)HPO(4) concentration from 0.01 to 1.0 M resulted in a doubling of the volume of the microspheres converted to an HA-like material but had little effect on the composition of the HA-like product. In comparison, reaction of the 45S5c microspheres in the solution with a starting pH of 7.0 resulted in an HA-like product in the 0.01 M K(2)HPO(4) solution but a calcium pyrophosphate product, Ca(10)K(4)(P(2)O(7))(6).9H(2)O, in the 1.0 M solution. The consequences of these results for the long-term use of 45S5 glass-ceramics in biomedical applications are discussed.

Heavily Yb-doped phosphate large-mode area all-solid photonic crystal fiber operating at 990 nm

NASA Astrophysics Data System (ADS)

Wang, Longfei; He, Dongbing; Feng, Suya; Yu, Chunlei; Hu, Lili; Qiu, Jianrong; Chen, Danping

2015-07-01

We demonstrate, for the first time to our knowledge, a 16 wt.% Yb-doped phosphate large-mode area all-solid photonic crystal fiber (AS-PCF) laser operating at 990 nm. By carefully tailoring the absorption and emission properties of the active glass and designing the structure of AS-PCF, the excitation of the 990 nm laser and the depression of the laser above 1 µm can be easily realized even without any wavelength-selective optics. The single-mode behavior of PCF with a 35 µm doped core, the largest core diameter of approximately 1 µm in phosphate fiber, is theoretically investigated by finite-difference time-domain method and experimentally confirmed.

Predictions of glass transition temperature for hydrogen bonding biomaterials.

PubMed

van der Sman, R G M

2013-12-19

We show that the glass transition of a multitude of mixtures containing hydrogen bonding materials correlates strongly with the effective number of hydroxyl groups per molecule, which are available for intermolecular hydrogen bonding. This correlation is in compliance with the topological constraint theory, wherein the intermolecular hydrogen bonds constrain the mobility of the hydrogen bonded network. The finding that the glass transition relates to hydrogen bonding rather than free volume agrees with our recent finding that there is little difference in free volume among carbohydrates and polysaccharides. For binary and ternary mixtures of sugars, polyols, or biopolymers with water, our correlation states that the glass transition temperature is linear with the inverse of the number of effective hydroxyl groups per molecule. Only for dry biopolymer/sugar or sugar/polyol mixtures do we find deviations due to nonideal mixing, imposed by microheterogeneity.

Spectroscopic and thermal study of a new glass from TeO2sbnd Ga2O3sbnd GeO2 system

NASA Astrophysics Data System (ADS)

Marczewska, Agnieszka; Środa, Marcin

2018-07-01

Tellurium oxide and germanium oxide based glasses are classified as the heavy metal oxide glasses, with phonon energies below 880 cm-1. These glasses transmit to longer wavelengths when compared to borate, phosphate and silicate glasses because of the heavier mass of germanium. In this paper we present a new promising TeO2sbnd Ga2O3sbnd GeO2 glasses with high thermal stability and good optical properties in the near and mid-IR regions. The glass can be easily obtained for the wide range of Te/Ge ratio, which gives opportunity to engineering desirable properties. Based on the FT-IR spectra it could be stated that the tellurite network is monotonically transformed into germanate one as the GeO2 content increases. Admixtures of GeO2 into the network of tellurite glass causes the conversion of [TeO4] to [TeO3] units. Thus, the network of the glass could be consider as a mixture of the [TeO4], [TeO3] and [GeO4] units and with Ga3+ ions playing the role of its modifier. The glasses demonstrate high transmittance in mid-IR up to 6 μm what makes these materials suitable for mid-IR applications.

X-ray Absorption Fine Structure (XAFS) Studies of Oxide Glasses—A 45-Year Overview

PubMed Central

Zanotto, Edgar Dutra

2018-01-01

X-ray Absorption Fine Structure (XAFS) spectroscopy has been widely used to characterize the short-range order of glassy materials since the theoretical basis was established 45 years ago. Soon after the technique became accessible, mainly due to the existence of Synchrotron laboratories, a wide range of glassy materials was characterized. Silicate glasses have been the most studied because they are easy to prepare, they have commercial value and are similar to natural glasses, but borate, germanate, phosphate, tellurite and other less frequent oxide glasses have also been studied. In this manuscript, we review reported advances in the structural characterization of oxide-based glasses using this technique. A focus is on structural characterization of transition metal ions, especially Ti, Fe, and Ni, and their role in different properties of synthetic oxide-based glasses, as well as their important function in the formation of natural glasses and magmas, and in nucleation and crystallization. We also give some examples of XAFS applications for structural characterization of glasses submitted to high pressure, glasses used to store radioactive waste and medieval glasses. This updated, comprehensive review will likely serve as a useful guide to clarify the details of the short-range structure of oxide glasses. PMID:29382102

A review of bioactive glasses: Their structure, properties, fabrication and apatite formation.

PubMed

Kaur, Gurbinder; Pandey, Om P; Singh, Kulvir; Homa, Dan; Scott, Brian; Pickrell, Gary

2014-01-01

Bioactive glass and glass-ceramics are used in bone repair applications and are being developed for tissue engineering applications. Bioactive glasses/Bioglass are very attractive materials for producing scaffolds devoted to bone regeneration due to their versatile properties, which can be properly designed depending on their composition. An important feature of bioactive glasses, which enables them to work for applications in bone tissue engineering, is their ability to enhance revascularization, osteoblast adhesion, enzyme activity and differentiation of mesenchymal stem cells as well as osteoprogenitor cells. An extensive amount of research work has been carried out to develop silicate, borate/borosilicate bioactive glasses and phosphate glasses. Along with this, some metallic glasses have also been investigated for biomedical and technological applications in tissue engineering. Many trace elements have also been incorporated in the glass network to obtain the desired properties, which have beneficial effects on bone remodeling and/or associated angiogenesis. The motivation of this review is to provide an overview of the general requirements, composition, structure-property relationship with hydroxyapatite formation and future perspectives of bioglasses.Attention has also been given to developments of metallic glasses and doped bioglasses along with the techniques used for their fabrication. Copyright © 2013 Wiley Periodicals, Inc., a Wiley Company.

Investigation of bone formation using calcium phosphate glass cement in beagle dogs

PubMed Central

Lee, Seung-Bum; Jung, Ui-Won; Choi, Youna; Jamiyandorj, Otgonbold; Kim, Chang-Sung; Lee, Yong-Keun; Chai, Jung-Kiu

2010-01-01

Purpose Among available biomaterials, bioceramics have drawn special interest due to their bioactivity and the possibility of tailoring their composition. The degradation rate and formulation of bioceramics can be altered to mimic the compositions of the mineral phase of bone. The aim of this study was to investigate the bone formation effect of amorphous calcium phosphate glass cement (CPGC) synthesized by a melting and quenching process. Methods In five male beagle dogs, 4 × 4 mm 1-wall intrabony defects were created bilaterally at the mesial or distal aspect of the mandibular second and fourth premolars. Each of the four defects was divided according to graft materials: CPGC with collagen membrane (CM), biphasic calcium phosphate (BCP) with CM, CM alone, or a surgical flap operation only. The dogs were sacrificed 8 weeks post-surgery, and block sections of the defects were collected for histologic and histometric analysis. Results There were significant differences in bone formation and cementum regeneration between the experimental and control groups. In particular, the CPGC and BCP groups showed greater bone formation than the CM and control groups. Conclusions In conclusion, CPGC was replaced rapidly with an abundant volume of new bone; CPGC also contributed slightly to regeneration of the periodontal apparatus. PMID:20607057

Evaluation of retentive strength of four luting cements with stainless steel crowns in primary molars: An in vitro study.

PubMed

Parisay, Iman; Khazaei, Yegane

2018-01-01

Stainless steel crown (SSC) is the most reliable restoration for primary teeth with extensive caries. Retention is of great importance for a successful restoration and is provided by various factors such as luting cements. The aim of this study was to evaluate the retentive strength of SSC cemented with four different luting cements. In this in vitro study, A total of 55 extracted primary first molars were selected. Following crown selection and cementation (one with no cement and four groups cemented with resin, glass ionomer, zinc phosphate, and polycarboxylate), all the specimens were incubated and thermocycled in 5°C-55°C. Retentive properties of SSCs were tested with a mechanical test machine. First dislodgement of each specimen and full crown removal were recorded. One-way ANOVA test followed by least significant difference test and Kruskal-Wallis test was used for retentive strength comparison at the level of significance of P < 0.05. The results of the study showed that the specimens cemented with zinc phosphate exhibited higher retentive strength as compared to glass ionomer and polycarboxylate ( P < 0.001 and P = 0.023, respectively). Zinc phosphate cement showed the most promising results; thus, it can be preferably used for cementation of the teeth with no grossly broken down crowns.

Na/Ca Intermixing around Silicate and Phosphate Groups in Bioactive Phosphosilicate Glasses Revealed by Heteronuclear Solid-State NMR and Molecular Dynamics Simulations.

PubMed

Mathew, Renny; Stevensson, Baltzar; Edén, Mattias

2015-04-30

We characterize the intermixing of network-modifying Na(+)/Ca(2+) ions around the silicate (QSi(n)) and phosphate (QP(n)) tetrahedra in a series of 16 Na2O–CaO–SiO2–P2O5 glasses, whose P content and silicate network connectivity were varied independently. The set includes both bioactive and bioinactive compositions and also encompasses two soda-lime-silicate members devoid of P, as well as two CaO–SiO2 glasses and one Na2O–SiO2–P2O5 glass. The various Si/P↔Na/Ca contacts were probed by molecular dynamics (MD) simulations together with heteronuclear magic-angle-spinning (MAS) nuclear magnetic resonance (NMR) experimentation utilizing (23)Na{(31)P} and (23)Na{(29)Si} REDOR, as well as (31)P{ (23)Na} and (29)Si{(23)Na} REAPDOR. We introduce an approach for quantifying the extent of Na(+)/Ca(2+) ordering around a given QP(n) or QSi(n) group, encoded by the preference factor 0⩽ PM ⩽ 1 conveying the relative weights of a random cation intermixing (PM = 0) and complete preference/ordering (PM = 1) for one of the species M, which represents either Na(+) or Ca(2+). The MD-derived preference factors reveal phosphate and silicate species surrounded by Na(+)/Ca(2+) ions intermixed nearly randomly (PM ≲ 0.15), except for the QSi(4) and QSi(1) groups, which manifest more significant cation ordering with preference for Na+ and Ca2+, respectively. The overall weak preferences are essentially independent of the Si and P contents of the glass, whereas PM primarily correlates with the total amount of network modifiers: as the latter is increased, the Na/Ca distribution around the {QP(0), QSi(1), QSi(2)} groups with preference for Ca2(+ )tend to randomize (i.e., PCa decreases), while the PNa-values grow slightly for the {QP(1), QSi(3), QSi(4)} species already preferring coordination of Na. The set of experimental preference factors {PCa} for the orthophosphate (QP(0)) groups extracted from (31)P{(23)Na} REAPDOR NMR-derived M2(P–Na) dipolar second moments agrees well with the MD-generated counterparts. Our results on the Na/Ca intermixing in soda-lime-silicate glasses are discussed in relation to previous reports, highlighting the dependence of the conclusion on the approach to data evaluation.

Preparation and characterization of Tb3+ ions doped zincborophosphate glasses for green emission

NASA Astrophysics Data System (ADS)

Bindu, S. Hima; Raju, D. Siva; Krishna, V. Vinay; Raju, Ch. Linga

2017-06-01

The present study reports the preparation of various concentrations of Tb3+ ions doped zincborophosphate glasses and analysis by XRD, FTIR, optical, emission and decay curve spectras. The effect of borate groups on the phosphate was evidenced by FTIR spectroscopy. The JO intensity parameters was calculated using Judd-Offlet theory. The fluroscence spectra of Tb3+ doped zincborophosphate glasses revealed the efficient blue and green emissions due to 5D3 and 5D4 excited levels to 7Fj ground state respectively. The decay curves exhibits single exponential curves for all the Tb3+ ion concentrations. Various radiative and fluorescence parameters are calculated using JO intensity parameters. Based on the results obtained in the present study, the Tb3+ ions doped zincborophosphate glasses behaves as a efficient laser active materials for highintensity emissions in the green region.

Mechanical properties and ion release from bioactive restorative composites containing glass fillers and calcium phosphate nano-structured particles.

PubMed

Chiari, Marina D S; Rodrigues, Marcela C; Xavier, Tathy A; de Souza, Eugen M N; Arana-Chavez, Victor E; Braga, Roberto R

2015-06-01

To evaluate the effect of the replacement of barium glass by dicalcium phosphate dihydrate (DCPD) particles on the mechanical properties and degree of conversion (DC) of composites. Additionally, calcium and hydrogen phosphate (HPO4(2-)) release were followed for 28 days. Nine composites containing equal parts (in mols) of BisGMA and TEGDMA and 40, 50 or 60 vol% of total filler were manipulated. Filler phase was constituted by silanated barium glass and 0%, 10% or 20% of DCPD particles. DC was determined by near-FTIR. Biaxial flexural strength (BFS) and modulus (E) were tested using the "piston on three balls" method, while fracture toughness (KIc) used the "single edge notched beam" method. Specimens were tested after 24h and 28 days in water. Ion release was determined using inductively coupled plasma optical emission spectrometry (ICP-OES). Data were analyzed by ANOVA/Tukey (DC and ion release) or Kruskal-Wallis/Mann-Whitney (mechanical properties; alpha: 5%). DC was not affected by DCPD. The presence of DCPD reduced BFS for both storage times, while differences in E became evident after 28 days. After 24h, KIc increased with the addition of DCPD; after 28 days, however, KIc decreased only for DCPD-containing composites. Calcium release was similar for both DCPD contents and remained fairly constant during the 28-day period. Overall, HPO4(2-) release was higher at 7 days and did not decrease after 14 days. The composite with the highest filler level and 10% DCPD represented the best compromise between mechanical properties after aging in water and ion release. Copyright © 2015 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Characterization of aqueous interactions of copper-doped phosphate-based glasses by vapour sorption.

PubMed

Stähli, Christoph; Shah Mohammadi, Maziar; Waters, Kristian E; Nazhat, Showan N

2014-07-01

Owing to their adjustable dissolution properties, phosphate-based glasses (PGs) are promising materials for the controlled release of bioinorganics, such as copper ions. This study describes a vapour sorption method that allowed for the investigation of the kinetics and mechanisms of aqueous interactions of PGs of the formulation 50P2O5-30CaO-(20-x)Na2O-xCuO (x=0, 1, 5 and 10mol.%). Initial characterization was performed using (31)P magic angle spinning nuclear magnetic resonance and attenuated total reflectance-Fourier transform infrared spectroscopy. Increasing CuO content resulted in chemical shifts of the predominant Q(2) NMR peak and of the (POP)as and (PO(-)) Fourier transform infrared absorptions, owing to the higher strength of the POCu bond compared to PONa. Vapour sorption and desorption were gravimetrically measured in PG powders exposed to variable relative humidity (RH). Sorption was negligible below 70% RH and increased exponentially with RH from 70 to 90%, where it exhibited a negative correlation with CuO content. Vapour sorption in 0% and 1% CuO glasses resulted in phosphate chain hydration and hydrolysis, as evidenced by protonated Q(0)(1H) and Q(1)(1H) species. Dissolution rates in deionized water showed a linear correlation (R(2)>0.99) with vapour sorption. Furthermore, cation release rates could be predicted based on dissolution rates and PG composition. The release of orthophosphate and short polyphosphate species corroborates the action of hydrolysis and was correlated with pH changes. In conclusion, the agreement between vapour sorption and routine characterization techniques in water demonstrates the potential of this method for the study of PG aqueous reactions. Copyright © 2014 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

Effects of Cement, Abutment Surface Pretreatment, and Artificial Aging on the Force Required to Detach Cantilever Fixed Dental Prostheses from Dental Implants.

PubMed

Kappel, Stefanie; Chepura, Taras; Schmitter, Marc; Rammelsberg, Peter; Rues, Stefan

To examine the in vitro effects of different cements, abutment surface preconditioning, and artificial aging on the maximum tensile force needed to detach cantilever fixed dental prostheses (FDPs) from dental implants with titanium abutments. A total of 32 tissue-level implants were combined with standardized titanium abutments. For each test group, eight cantilever FDPs were fabricated using selective laser melting (cobalt-chromium [CoCr] alloy). The inner surfaces of the cantilever FDPs and half of the abutments were sandblasted and then joined by use of four different cements (two permanent and two semi-permanent) in two different amounts per cement. Subgroups were tested after either artificial aging (thermocycling and chewing simulation) or 3 days of water storage. Finally, axial pull off-tests were performed for each abutment separately. Cement type and surface pretreatment significantly affected decementation behavior. The highest retention forces (approximately 1,200 N) were associated with sandblasted abutments and permanent cements. With unconditioned abutments, temporary cements (Fu < 100 N), as well as glass-ionomer cement (Fu ≈ 100 N), resulted in rather low retention forces. Zinc phosphate cement guaranteed high retention forces. After aging, retention was sufficient only for cementation with zinc phosphate cement and for the combination of sandblasted abutments and glass-ionomer cement. When glass-ionomer cement is used to fix cantilever FDPs on implants, sandblasting of standard titanium abutments may help prevent loss of retention. Retention forces were still high for FDPs fixed with zinc phosphate cement, even when the abutments were not pretreated. Use of permanent cements only, however, is recommended to prevent unwanted loosening of cantilever FDPs.

Formation of surface reaction products on bioactive glass and their effects on the expression of the osteoblastic phenotype and the deposition of mineralized extracellular matrix.

PubMed

el-Ghannam, A; Ducheyne, P; Shapiro, I M

1997-02-01

The objective of the study was to examine the effect of alkali ion release, pH control and buffer capacity on the expression of the osteoblastic phenotype. In addition we determined the importance of modifications of the surface of porous bioactive glass (BG) on the activity of rat calvaria osteoblasts in vitro. We found that at a low tissue culture medium (TCM) volume to BG surface area (Vol/SA) ratio, the products of glass corrosion elevated the pH of the TCM to a value that adversely affected cellular activity; thus, the matrix synthesized by the cells was non-mineralized. On the other hand, when the Vol/SA was high and the buffer capacity of the medium was not exceeded, the cells generated a mineralized extracellular matrix. Addressing the second issue, we observed that modification of the composition of the BG surface markedly influenced osteoblast activity. BG that was coated with either a calcium phosphate-rich layer only or a serum protein layer changed the phenotypic characteristics of the osteoblasts. The presence of either of these surfaces lowered the alkaline phosphatase activity of the attached cells; this finding indicated that the osteoblast phenotype was not conserved. However, when the BG was coated with a bilayer of calcium phosphate and serum proteins, the alkaline phosphatase (AP) activity was elevated and the extracellular matrix contained characteristic bone markers. Our findings indicate that the calcium phosphate-rich layer promotes adsorption and concentration of proteins from the TCM, and it is utilized by the osteoblasts to form the mineralized extracellular matrix.

Finite-connectivity spin-glass phase diagrams and low-density parity check codes.

PubMed

Migliorini, Gabriele; Saad, David

2006-02-01

We obtain phase diagrams of regular and irregular finite-connectivity spin glasses. Contact is first established between properties of the phase diagram and the performance of low-density parity check (LDPC) codes within the replica symmetric (RS) ansatz. We then study the location of the dynamical and critical transition points of these systems within the one step replica symmetry breaking theory (RSB), extending similar calculations that have been performed in the past for the Bethe spin-glass problem. We observe that the location of the dynamical transition line does change within the RSB theory, in comparison with the results obtained in the RS case. For LDPC decoding of messages transmitted over the binary erasure channel we find, at zero temperature and rate , an RS critical transition point at while the critical RSB transition point is located at , to be compared with the corresponding Shannon bound . For the binary symmetric channel we show that the low temperature reentrant behavior of the dynamical transition line, observed within the RS ansatz, changes its location when the RSB ansatz is employed; the dynamical transition point occurs at higher values of the channel noise. Possible practical implications to improve the performance of the state-of-the-art error correcting codes are discussed.

Chromatic characterization of ion-exchanged glass binary phase plates for mode-division multiplexing.

PubMed

Prieto-Blanco, Xesús; Montero-Orille, Carlos; Moreno, Vicente; Mateo, Eduardo F; Liñares, Jesús

2015-04-10

Mode-division multiplexing (MDM) in few-mode fibers is regarded as a promising candidate to increase optical network capacity. A fundamental element for MDM is a modal transformer to LP modes which can be implemented in a free-space basis by using multiregion phase plates, that is, LP plates. Likewise, several wavelengths have to be used due to wavelength multiplexing purposes, optical amplification tasks, and so on. In this work we show that efficient monolithic binary phase plates for different wavelengths can be fabricated by ion-exchange in glass and used for MDM tasks. We introduce an optical characterization method of the chromatic properties of such phase plates which combines the inverse Wentzel-Kramers-Brillouin (IWKB) together with Mach-Zehnder and Michelson-based interferometric techniques. The interferometric method provides a measurement of the phase step for several wavelengths, which characterizes the chromatic properties of the phase plate. Consequently, it is shown that the IWKB method allows us to design and characterize the phase plates in an easy and fast way.

SEPARATION OF PROTACTINIUM FROM THORIUM IN NITRIC ACID SOLUTIONS BY SOLVENT EXTRACTION WITH TRIBUTYL PHOSPHATE OR BY ADSORPTION ON PULVERIZED UNFIRED VYCOR GLASS OR SILICA GEL

DOE Office of Scientific and Technical Information (OSTI.GOV)

Moore, J.G.; Rainey, R.H.

1963-04-01

Two methods were investigated for the separation and recovery of Pa from short-decayed Th fuel in HNO/sub 3/ solutions. The Pa/sub 233/, Th, and U may be coextracted from highly acidic feed solutions with 30% tributyl phosphate, or the Pa may be preferentially adsorbed on pulverized unfired Vycor glass or silica gel. Major effort has been on the adsorption method. Adsorption experiments with tracer concentrations of Pa/sup 233/ in HNO/sub 3/ solutions showed distribution coefficient maxima for Pa of about 1000, 325, and 175 from 6 to 10 M HNO/sub 3/ for laboratory-prepared silica gel, unfired Vycor, and commercial silicamore » gel, respectively. Unfired Vycor, a commercial, leached borosilicate glass containing 96% SiO/sub 2/ and about 3% B/sub 2/O/sub 3/, was used for most of the studies. Fired Vycor glass adsorbed little or no Pa. The adsorption coefficient of Pa by unfired Vycor glass from HNO/sub 3/ solutions increased as the contact time increased or as the particle size of the glass decreased and was dependent on the concentration of salt or HNO/sub 3/ in the solution. The adsorbed Pa may be eluted with oxalic or tartaric acids. Although optimum conditions for column operations were not determined, decontamination factors of Pa from Th, U, Ru, Zr- Nb and total rare earths of 6x 10/sup 3/, 1.6 x 101,4 x 10/sup 3/, 3, and 5.8 x 10/sup 5/, respectively, were obtained in tracer experiments. Batch countercurrent scouting experiments with tracer Pa showed that about 90% of the Pa was extracted with the Th and U from 5 M HNO/sub 3/-1 M Al(NO/sub 3/)/sub 3/ solutions, with a decontamination factor of 70 from Ru and about 10/sup 5/ from rare earths. (P.C.H.)« less

Effect of phosphate-based glass fibre surface properties on thermally produced poly(lactic acid) matrix composites.

PubMed

Mohammadi, Maziar Shah; Ahmed, Ifty; Muja, Naser; Rudd, Christopher D; Bureau, Martin N; Nazhat, Showan N

2011-12-01

Incorporation of soluble bioactive glass fibres into biodegradable polymers is an interesting approach for bone repair and regeneration. However, the glass composition and its surface properties significantly affect the nature of the fibre-matrix interface and composite properties. Herein, the effect of Si and Fe on the surface properties of calcium containing phosphate based glasses (PGs) in the system (50P(2)O(5)-40CaO-(10-x)SiO(2)-xFe(2)O(3), where x = 0, 5 and 10 mol.%) were investigated. Contact angle measurements revealed a higher surface energy, and surface polarity as well as increased hydrophilicity for Si doped PG which may account for the presence of surface hydroxyl groups. Two PG formulations, 50P(2)O(5)-40CaO-10Fe(2)O(3) (Fe10) and 50P(2)O(5)-40CaO-5Fe(2)O(3)-5SiO(2) (Fe5Si5), were melt drawn into fibres and randomly incorporated into poly(lactic acid) (PLA) produced by melt processing. The ageing in deionised water (DW), mechanical property changes in phosphate buffered saline (PBS) and cytocompatibility properties of these composites were investigated. In contrast to Fe10 and as a consequence of the higher surface energy and polarity of Fe5Si5, its incorporation into PLA led to increased inorganic/organic interaction indicated by a reduction in the carbonyl group of the matrix. PLA chain scission was confirmed by a greater reduction in its molecular weight in PLA-Fe5Si5 composites. In DW, the dissolution rate of PLA-Fe5Si5 was significantly higher than that of PLA-Fe10. Dissolution of the glass fibres resulted in the formation of channels within the matrix. Initial flexural strength was significantly increased through PGF incorporation. After PBS ageing, the reduction in mechanical properties was greater for PLA-Fe5Si5 compared to PLA-Fe10. MC3T3-E1 preosteoblasts seeded onto PG discs, PLA and PLA-PGF composites were evaluated for up to 7 days indicating that the materials were generally cytocompatible. In addition, cell alignment along the PGF orientation was observed showing cell preference towards PGF.

The Feasibility and Functional Performance of Ternary Borate-Filled Hydrophilic Bone Cements: Targeting Therapeutic Release Thresholds for Strontium

PubMed Central

MacDonald, Kathleen; Price, Richard B.; Boyd, Daniel

2017-01-01

We examine the feasibility and functionality of hydrophilic modifications to a borate glass reinforced resin composite; with the objective of meeting and maintaining therapeutic thresholds for Sr release over time, as a potential method of incorporating antiosteoporotic therapy into a vertebroplasty material. Fifteen composites were formulated with the hydrophilic agent hydroxyl ethyl methacrylate (HEMA, 15, 22.5, 30, 37.5 or 45 wt% of resin phase) and filled with a borate glass (55, 60 or 65 wt% of total cement) with known Sr release characteristics. Cements were examined with respect to degree of cure, water sorption, Sr release, and biaxial flexural strength over 60 days of incubation in phosphate buffered saline. While water sorption and glass degradation increased with increasing HEMA content, Sr release peaked with the 30% HEMA compositions, scanning electron microscope (SEM) imaging confirmed the surface precipitation of a Sr phosphate compound. Biaxial flexural strengths ranged between 16 and 44 MPa, decreasing with increased HEMA content. Degree of cure increased with HEMA content (42 to 81%), while no significant effect was seen on setting times (209 to 263 s). High HEMA content may provide a method of increasing monomer conversion without effect on setting reaction, providing sustained mechanical strength over 60 days. PMID:28708123

SOLID-STATE DOSIMETERS BASED ON OPTICAL THEORY (in Hungarian)

DOE Office of Scientific and Technical Information (OSTI.GOV)

Patko, J.

1962-01-01

A comparison is made of applications of various dosimeters based on solid materials, and their comparative merits are described. Characteristics of the following types of dosimeters effective at various radiation intensities are discussed: condensation chambers for measurements over the range 10/sup -4/-10/ sup 2/ rad, film dosimeters 10/sup -1/-10/sup 5/ rad, thermoluminescent types 10/ sup -3/ - 10/sup 4/ rad, photoluminescent dosimeters 10/sup 1/-- 10/sup 4/ rad, crystal types 10/sup 1/- 10/sup 4/ rad, glass dosimeters 10/sup 3/- 10/sup 7/ rad, synthetic material types 10/sup 5/- 10/sup 9/ rad, and luminescent degradation dosimeters 10/sup 5/-10/sup 8/ rad. Special attention ismore » given to the thermoluminescent dosimeter, which utilizes Mn-activated Ca phosphate. This dosimeter utilizes a glass ampulla instead of a glass vacuum tube and polarography is used to determine the luminescence curve. Simple evaluation equipment is being developed to be used with this dosimeter. Such thermoluminescent dosimeters are generally small in size. Its high sensitivity makes it applicable to low intensity radiation aad after calibration it can again be utilized. Manganese-activated Ca phosphate dosimeters do not show any fading of response in the first hour after use. Use of solid dosimeters, for high- energy measurements« less

Mechanical, structural and dissolution properties of heat treated thin-film phosphate based glasses

NASA Astrophysics Data System (ADS)

Stuart, Bryan W.; Gimeno-Fabra, Miquel; Segal, Joel; Ahmed, Ifty; Grant, David M.

2017-09-01

Here we show the deposition of 2.7 μm thick phosphate based glass films produced by magnetron sputtering, followed by post heat treatments at 500 °C. Variations in degradation properties pre and post heat treatment were attributed to the formation of Hematite crystals within a glass matrix, iron oxidation and the depletion of hydrophilic P-O-P bonds within the surface layer. As deposited and heat treated coatings showed interfacial tensile adhesion in excess of 73.6 MPa; which surpassed ISO and FDA requirements for HA coatings. Scratch testing of coatings on polished substrates revealed brittle failure mechanisms, amplified due to heat treatment and interfacial failure occurring from 2.3 to 5.0 N. Coatings that were deposited onto sandblasted substrates to mimic commercial implant surfaces, did not suffer from tensile cracking or trackside delamination showing substantial interfacial improvements to between 8.6 and 11.3 N. An exponential dissolution rate was observed from 0 to 2 h for as deposited coatings, which was eliminated via heat treatment. From 2 to 24 h ion release rates ordered P > Na > Mg > Ca > Fe whilst all coatings exhibited linear degradation rates, which reduced by factors of 2.4-3.0 following heat treatments.

The Feasibility and Functional Performance of Ternary Borate-Filled Hydrophilic Bone Cements: Targeting Therapeutic Release Thresholds for Strontium.

PubMed

MacDonald, Kathleen; Price, Richard B; Boyd, Daniel

2017-07-14

We examine the feasibility and functionality of hydrophilic modifications to a borate glass reinforced resin composite; with the objective of meeting and maintaining therapeutic thresholds for Sr release over time, as a potential method of incorporating antiosteoporotic therapy into a vertebroplasty material. Fifteen composites were formulated with the hydrophilic agent hydroxyl ethyl methacrylate (HEMA, 15, 22.5, 30, 37.5 or 45 wt% of resin phase) and filled with a borate glass (55, 60 or 65 wt% of total cement) with known Sr release characteristics. Cements were examined with respect to degree of cure, water sorption, Sr release, and biaxial flexural strength over 60 days of incubation in phosphate buffered saline. While water sorption and glass degradation increased with increasing HEMA content, Sr release peaked with the 30% HEMA compositions, scanning electron microscope (SEM) imaging confirmed the surface precipitation of a Sr phosphate compound. Biaxial flexural strengths ranged between 16 and 44 MPa, decreasing with increased HEMA content. Degree of cure increased with HEMA content (42 to 81%), while no significant effect was seen on setting times (209 to 263 s). High HEMA content may provide a method of increasing monomer conversion without effect on setting reaction, providing sustained mechanical strength over 60 days.

Crystallization, fluoridation and some properties of apatite thin films prepared through rf-sputtering from CaO-P2O5 glasses.

PubMed

Yamashita, K; Matsuda, M; Arashi, T; Umegaki, T

1998-07-01

Using calcium phosphate glass targets with the CaO/P2O5 molar ratios of 1.50-0.50, much lower than the stoichiometric value of 3.3 for hydroxyapatite, thin films of stoichiometric hydroxy-, nonstoichiometric oxyhydroxy- and Ca-deficient oxyhydroxy-apatites were prepared on alumina ceramic substrates by rf-sputtering followed by post-annealing. Based on the present results, a phase diagram for CaO-P2O5 at low temperatures in the ambience of air was depicted for thin films. The ambient H2O vapor had an influence on the phase diagram: Tricalcium phosphate was changed to apatite in the presence of H2O vapor. Dense fluorohydroxyapatite thin films were prepared by fluoridation of those apatite thin films at a low temperature such as 200 degrees C. In the present report, some functional properties of thin films thus prepared were also shown.

Er3+ phosphate glass optical waveguide amplifiers at 1.5 μm on silicon

NASA Astrophysics Data System (ADS)

Yan, Yingchao; Faber, Anne J.; de Waal, Henk

1996-01-01

RF-sputtering techniques were employed to produce Er-doped phosphate glass films on thermally oxidized silicon wafers. Film compositions were characterized by X-ray photoelectron spectroscopy. As-deposited films showed very low Er luminescence lifetimes. By postannealing of deposited films in pure oxygen, Er photoluminescence emission lifetime of the 4I13/2 - 4I15/2 transition could be increased from 1 - 2 ms to 8 - 9 ms. The long Er lifetime of the deposited films is very promising for achieving an optical gain. A dependence of measured lifetimes on pump power was observed which are related to a up-conversion quenching process. After postannealing, the sputtered waveguides showed relatively low attenuation loss at the potential pumping and signaling wavelengths. The loss spectrum from 700 nm to 1600 nm was measured by two-prism coupling. The films were easy to be patterned by lithography and ridge channel waveguides were developed by argon plasma etching.

Optical spectroscopy, 1.06μm emission properties of Nd3+-doped phosphate based glasses.

PubMed

Sk Nayab, Rasool; T, Sasikala; A, Mohan Babu; L, Rama Moorthy; C K, Jayasankar

2017-06-05

Neodymium doped phosphate based glasses with composition of (P 2 O 5 +K 2 O+Al 2 O 3 +CaF 2 ) were prepared. The samples were analysed through differential thermal analysis (DTA), Fourier transform infrared (FTIR), absorption, emission and decay measurements. Judd-Ofelt parameters (Ω λ ) have been determined from the spectral intensities of absorption bands in order to calculate the radiative parameters like radiative transition probabilities (A R ), radiative lifetime (τ R ) and branching ratios (β R ) for the 4 F 3/2 → 4 I 11/2 laser transition of Nd 3+ ion. The effective emission bandwidths (Δλ eff ), experimental branching ratios (β exp ) and stimulated emission cross-sections (σ e ) have been determined from the emission spectrum. The decay curves of the 4 F 3/2 level exhibited almost single exponential nature for all the Nd 3+ ion concentrations. Copyright © 2017 Elsevier B.V. All rights reserved.

Antibacterial activity evaluation of bioactive glass and biphasic calcium phosphate nanopowders mixtures

NASA Astrophysics Data System (ADS)

Nazemi, Zahra; Mehdikhani-Nahrkhalaji, Mehdi; Haghbin-Nazarpak, Masoumeh; Staji, Hamid; Kalani, Mohammad Mehdi

2016-12-01

The aim of this work was to evaluate the antibacterial activity of bioactive glass (BG) and biphasic calcium phosphate (BCP) nanopowders mixtures for the first time. 37S BG and BCP (50% HA-50% β-TCP) nanopowders were prepared via sol-gel technique. Characterization techniques such as X-ray diffraction, scanning electron microscopy, transition electron microscopy, and X-ray fluorescent. The antibacterial activity was studied using Escherichia coli and Salmonella typhi as gram-negative, and Staphylococcus aureus as gram-positive bacteria. The antibacterial effect of BG, BCP nanopowders, and their mixtures was evaluated at different concentrations. The 37S BG nanopowders showed minimum bactericidal concentration at 25 mg/ml. At broth concentrations below 300 mg/ml, BCP showed no antibacterial activity. BCP and BG nanopowders mixture (M2) with 60/40 ratio of BCP/BG showed noticeable antibacterial effect. It was concluded that BCP and 37S BG nanopowders mixture could be used as a good candidate for dental and orthopedic applications.

Toward Smart Implant Synthesis: Bonding Bioceramics of Different Resorbability to Match Bone Growth Rates

PubMed Central

Comesaña, Rafael; Lusquiños, Fernando; del Val, Jesús; Quintero, Félix; Riveiro, Antonio; Boutinguiza, Mohamed; Jones, Julian R.; Hill, Robert G.; Pou, Juan

2015-01-01

Craniofacial reconstructive surgery requires a bioactive bone implant capable to provide a gradual resorbability and to adjust to the kinetics of new bone formation during healing. Biomaterials made of calcium phosphate or bioactive glasses are currently available, mainly as bone defect fillers, but it is still required a versatile processing technique to fabricate composition-gradient bioceramics for application as controlled resorption implants. Here it is reported the application of rapid prototyping based on laser cladding to produce three-dimensional bioceramic implants comprising of a calcium phosphate inner core, with moderate in vitro degradation at physiological pH, surrounded by a bioactive glass outer layer of higher degradability. Each component of the implant is validated in terms of chemical and physical properties, and absence of toxicity. Pre–osteoblastic cell adhesion and proliferation assays reveal the adherence and growth of new bone cells on the material. This technique affords implants with gradual-resorbability for restoration of low-load-bearing bone. PMID:26032983

Fabrication of a Biomass-Based Hydrous Zirconium Oxide Nanocomposite for Preferable Phosphate Removal and Recovery.

PubMed

Qiu, Hui; Liang, Chen; Zhang, Xiaolin; Chen, Mindong; Zhao, Yunxia; Tao, Tao; Xu, Zhengwen; Liu, Gang

2015-09-23

Advanced removal of phosphate by low-cost adsorbents from municipal wastewater or industrial effluents is an effective and economic way to prevent the occurrence of eutrophication. Here, we proposed a novel method to immobilize hydrous zirconium oxide nanoparticle within quaternary-aminated wheat straw, and obtained an inexpensive, eco-friendly nanocomposite Ws-N-Zr. The biomass-based Ws-N-Zr exhibited higher preference toward phosphate than commercial anion exchanger IRA-900 when competing sulfate ions coexisted at relatively high levels. Such excellent performance of Ws-N-Zr resulted from its specific hybrid structure, the quaternary ammonium groups bonded on the host favor the preconcentration of phosphate ions inside the wheat straw based on Donnan effect, and the encapsulated HZO nanoparticle exhibits preferable sequestration of phosphate ions through specific interaction, as further demonstrated by FTIR and X-ray photoelectron spectroscopy. Cycle adsorption and regeneration experiments demonstrated that Ws-N-Zr could be employed for repeated use without significant capacity loss, when the binary NaOH-NaCl solution was employed as the regenerant. The influence of solution pH and contact time was also examined. The results suggested that Ws-N-Zr has a great potential in efficient removal of phosphate in contaminated waters.

Investigation on gamma and neutron radiation shielding parameters for BaO/SrO‒Bi2O3‒B2O3 glasses

NASA Astrophysics Data System (ADS)

Sayyed, M. I.; Lakshminarayana, G.; Dong, M. G.; Ersundu, M. Çelikbilek; Ersundu, A. E.; Kityk, I. V.

2018-04-01

In this work, mass attenuation coefficients (μ/ρ), effective atomic number (Zeff), electron density (Ne), mean free path (MFP), and half-value layer (HVL) of 20 BaO/SrO‒(x) Bi2O3‒(80‒x) B2O3 glasses (where x=10, 20, 30, 40, 50 and 60 mol%) were calculated using WinXCom program and MCNP5 code. The obtained (μ/ρ) results using both MCNP5 code and WinXCom program were in good agreement. It is found that the addition of Bi2O3 leads to increase the Zeff values in both BaO/SrO‒Bi2O3‒B2O3 glass systems. However, the Zeff values of the BaO‒Bi2O3‒B2O3 glass system are higher than those of the SrO‒Bi2O3‒B2O3 glasses. The fast neutrons effective removal cross sections (ΣR) for 20 SrO‒40 Bi2O3‒40 B2O3 glass is the highest among all studied glasses. The calculated half-value layer values were compared with different glass systems and it was found that the shielding properties of the selected glasses are comparable or even better than other glass systems such as phosphate glasses.

Complexing Agents and pH Influence on Chemical Durability of Type I Molded Glass Containers.

PubMed

Biavati, Alberto; Poncini, Michele; Ferrarini, Arianna; Favaro, Nicola; Scarpa, Martina; Vallotto, Marta

2017-01-01

Among the factors that affect the glass surface chemical durability, pH and complexing agents present in aqueous solution have the main role. Glass surface attack can be also related to the delamination issue causing glass particles' appearance in the pharmaceutical preparation. A few methods to check for glass containers delamination propensity and some control guidelines have been proposed. The present study emphasizes the possible synergy between a few complexing agents with pH on borosilicate glass chemical durability.Hydrolytic attack was performed in small-volume 23 mL type I glass containers autoclaved according to the European Pharmacopoeia or United States Pharmacopeia for 1 h at 121 °C, in order to enhance the chemical attack due to time, temperature, and the unfavorable surface/volume ratio. Solutions of 0.048 M or 0.024 M (M/L) of the acids citric, glutaric, acetic, EDTA (ethylenediaminetetraacetic acid), together with sodium phosphate with water for comparison, were used for the trials. The pH was adjusted ±0.05 units at fixed values 5.5, 6.6, 7, 7.4, 8, and 9 by LiOH diluted solution.Because silicon is the main glass network former, silicon release into the attack solutions was chosen as the main index of the glass surface attack and analysed by inductively coupled plasma atomic emission spectrophotometry. The work was completed by the analysis of the silicon release in the worst attack conditions of molded glass, soda lime type II glass, and tubing borosilicate glass vials to compare different glass compositions and forming technologies. Surface analysis by scanning electron microscopy was finally performed to check for the surface status after the worst chemical attack condition by citric acid. LAY ABSTRACT: Glass, like every packaging material, can have some usage limits, mainly in basic pH solutions. The issue of glass surface degradation particles that appear in vials (delamination) has forced a number of drug product recalls in recent years. To prevent such situations, pharmaceutical and biopharmaceutical manufacturers need to understand the reasons for accelerate surface glass corrosion mainly in the case of injectables.Some drugs can contain active components with known ability to corrode glass silica networks. Sometimes these ingredients are dissolved in an alkaline medium that dramatically increases the glass corrosion and potentially causes the issue. As this action is strongly affected by time and temperature, flaking may become visible only after a long storage time. The purpose of this investigation is to verify the borosilicate glass chemical durability during controlled conditions of time and temperature when in contact with testing solutions containing different complexing agents by varying the pH. Si concentration in the extract solution is taken as an index of glass dissolution during constant autoclaving conditions for 1 h at 121 °C, which simulates approximately five years of contact at room temperature.Acetate, citrate, ethylenediaminetetraacetic acid (EDTA), phosphate, and glutarate 0.048 M or 0.024 M solutions were used at increasing pH from 5.5 to 9.0. The chemical durability of two borosilicate tubing glass vials of different glass compositions were compared with the molded one in the worst attack conditions by citric acid. Even if no delamination issue has been experienced by this study in type I molded and tubing containers, the conclusions developed can provide pharmaceutical manufacturers with useful information to prevent glass delamination risk in their processes. © PDA, Inc. 2017.

Interfacial free energy controlling glass-forming ability of Cu-Zr alloys.

PubMed

Kang, Dong-Hee; Zhang, Hao; Yoo, Hanbyeol; Lee, Hyun Hwi; Lee, Sooheyong; Lee, Geun Woo; Lou, Hongbo; Wang, Xiaodong; Cao, Qingping; Zhang, Dongxian; Jiang, Jianzhong

2014-06-04

Glass is a freezing phase of a deeply supercooled liquid. Despite its simple definition, the origin of glass forming ability (GFA) is still ambiguous, even for binary Cu-Zr alloys. Here, we directly study the stability of the supercooled Cu-Zr liquids where we find that Cu64Zr36 at a supercooled temperature shows deeper undercoolability and longer persistence than other neighbouring compositions with an equivalent driving Gibbs free energy. This observation implies that the GFA of the Cu-Zr alloys is significantly affected by crystal-liquid interfacial free energy. In particular, the crystal-liquid interfacial free energy of Cu64Zr36 in our measurement was higher than that of other neighbouring liquids and, coincidently a molecular dynamics simulation reveals a larger glass-glass interfacial energy value at this composition, which reflects more distinct configuration difference between liquid and crystal phase. The present results demonstrate that the higher crystal-liquid interfacial free energy is a prerequisite of good GFA of the Cu-Zr alloys.

Electrospun Polyhydroxybutyrate/Poly(ε-caprolactone)/58S Sol-Gel Bioactive Glass Hybrid Scaffolds with Highly Improved Osteogenic Potential for Bone Tissue Engineering.

PubMed

Ding, Yaping; Li, Wei; Müller, Teresa; Schubert, Dirk W; Boccaccini, Aldo R; Yao, Qingqing; Roether, Judith A

2016-07-13

Electrospinning of biopolymer and inorganic substances is one of the efficient ways to combine various advantageous properties in one single fibrous structure with potential for tissue engineering applications. In the present study, to integrate the high stiffness of polyhydroxybutyrate (PHB), the flexibility of poly(ε-caprolactone) (PCL) and the bioactivity of 58S bioactive glass, PHB/PCL/58S sol-gel bioactive glass hybrid scaffolds were fabricated using combined electrospinning and sol-gel method. Physical features such as fiber diameter distribution, mechanical strength and Young's modulus were characterized thoroughly. FTIR analysis demonstrated the successful incorporation of 58S bioactive glass into the blend polymers, which greatly improved the hydrophilicity of PHB/PCL fibermats. The primary biological response of MG-63 osteoblast-like cells on the prepared fibrous scaffolds was evaluated, proving that the 58S glass sol containing hybrid scaffold were not only favorable to MG-63 cell adhesion but also slightly enhanced cell viability and significantly increased alkaline phosphate activity .

Relaxation dynamics in AgI-doped silver vanadate superionic glasses.

PubMed

Bhattacharya, S; Ghosh, A

2005-09-22

Relaxation dynamics of Ag+ ions in several series of AgI-Ag2O-V2O5 superionic glasses has been studied in the frequency range from 10 Hz to 2 MHz and in the temperature range from 93 to 323 K. The composition dependence of the dc conductivity and the activation energy of these glasses has been compared with those of AgI-doped silver phosphate and borate glasses. The frequency-dependent electrical data have been analyzed in the framework of conductivity formalism. We have obtained the mobile ion concentration and the power-law exponent from the analysis of the conductivity spectra. We have observed that the concentration of Ag+ ions is independent of temperature and the conductivity is primarily determined by the mobility. A fraction of the Ag+ ions in the glass compositions are involved in the dynamic process. We have also shown that the power-law exponent is independent of temperature. The results are also supported by the temperature and composition independence of the scaling of the conductivity spectra.

Biological Impact of Bioactive Glasses and Their Dissolution Products.

PubMed

Hoppe, Alexander; Boccaccini, Aldo R

2015-01-01

For many years, bioactive glasses (BGs) have been widely considered for bone tissue engineering applications due to their ability to bond to hard as well as soft tissue (a property termed bioactivity) and for their stimulating effects on bone formation. Ionic dissolution products released during the degradation of the BG matrix induce osteogenic gene expression leading to enhanced bone regeneration. Recently, adding bioactive metallic ions (e.g. boron, copper, cobalt, silver, zinc and strontium) to silicate (or phosphate and borate) glasses has emerged as a promising route for developing novel BG formulations with specific therapeutic functionalities, including antibacterial, angiogenic and osteogenic properties. The degradation behaviour of BGs can be tailored by adjusting the glass chemistry making these glass matrices potential carrier systems for controlled therapeutic ion release. This book chapter summarises the fundamental aspects of the effect of ionic dissolution products from BGs on osteogenesis and angiogenesis, whilst discussing novel BG compositions with controlled therapeutic ion release. © 2015 S. Karger AG, Basel.

Dynamics and structure of an aging binary colloidal glass

NASA Astrophysics Data System (ADS)

Lynch, Jennifer M.; Cianci, Gianguido C.; Weeks, Eric R.

2008-09-01

We study aging in a colloidal suspension consisting of micron-sized particles in a liquid. This system is made glassy by increasing the particle concentration. We observe samples composed of particles of two sizes, with a size ratio of 1:2.1 and a volume fraction ratio 1:6, using fast laser scanning confocal microscopy. This technique yields real-time, three-dimensional movies deep inside the colloidal glass. Specifically, we look at how the size, motion, and structural organization of the particles relate to the overall aging of the glass. Particles move in spatially heterogeneous cooperative groups. These mobile regions tend to be richer in small particles, and these small particles facilitate the motion of nearby particles of both sizes.

Characterization and electrical properties of V 2O 5-CuO-P 2O 5 glasses

NASA Astrophysics Data System (ADS)

Al-Assiri, M. S.

2008-08-01

Characterization and electrical properties of vanadium-copper-phosphate glasses of compositions xV 2O 5-(40- x)CuO-60P 2O 5 have been reported. X-ray diffraction (XRD) confirms the amorphous nature of these glasses. It was observed that, the density ( d) decreases gradually while the molar volume ( Vm) increases with the increase of the vanadium oxide content in such glasses. This may be due to the effect of the polarizing power strength, PPS, which is a measure of ratio of the cation valance to its diameter. The dc conductivity increases while the activation energy decreases with the increase of the V 2O 5 content. The dc conductivity in the present glasses is electronic and depends strongly upon the average distance, R, between the vanadium ions. Analysis of the electrical properties has been made in the light of small polaron hopping model. The parameters obtained from the fits of the experimental data to this model are reasonable and consistent with glass composition. The conduction is attributed to non-adiabatic hopping of small polaron.

Spectroscopy of Yb-doped tungsten-tellurite glass and assessment of its lasing properties

NASA Astrophysics Data System (ADS)

Merzliakov, M. A.; Kouhar, V. V.; Malashkevich, G. E.; Pestryakov, E. V.

2018-01-01

Glasses of the TeO2-WO3-Yb2O3 system are synthesized for wide range of Yb3+ concentrations of up to 6.0 × 1021 ions/cm3. The spectral-luminescent properties of lightly doped samples are investigated at room temperature and at the boiling point of liquid nitrogen. The energies of the Stark levels of the ground and excited states of Yb3+ ions incorporated into tungsten-tellurite glass are determined by analyzing the low-temperature spectra. The absorption, emission, and gain cross section spectra are obtained. The excess of the measured fluorescence decay time over the radiative lifetime ∼0.3 ms derived from the absorption spectra is attributed to the reabsorption effect in bulk samples. Measurements of lightly doped glass powder in the immersion liquid are made to reduce the effect of reabsorption. The fluorescence decay time of the powder is very close to the calculated radiative lifetime. Compared with phosphate, silicate, and other Yb3+-doped glasses, the tungsten-tellurite glass has a promising potential as a gain medium for lasers and amplifiers.

SOLIDIFICATION OF THE HANFORD LAW WASTE STREAM PRODUCED AS A RESULT OF NEAR-TANK CONTINUOUS SLUDGE LEACHING AND SODIUM HYDROXIDE RECOVERY

DOE Office of Scientific and Technical Information (OSTI.GOV)

Reigel, M.; Johnson, F.; Crawford, C.

2011-09-20

The U.S. Department of Energy (DOE), Office of River Protection (ORP), is responsible for the remediation and stabilization of the Hanford Site tank farms, including 53 million gallons of highly radioactive mixed wasted waste contained in 177 underground tanks. The plan calls for all waste retrieved from the tanks to be transferred to the Waste Treatment Plant (WTP). The WTP will consist of three primary facilities including pretreatment facilities for Low Activity Waste (LAW) to remove aluminum, chromium and other solids and radioisotopes that are undesirable in the High Level Waste (HLW) stream. Removal of aluminum from HLW sludge canmore » be accomplished through continuous sludge leaching of the aluminum from the HLW sludge as sodium aluminate; however, this process will introduce a significant amount of sodium hydroxide into the waste stream and consequently will increase the volume of waste to be dispositioned. A sodium recovery process is needed to remove the sodium hydroxide and recycle it back to the aluminum dissolution process. The resulting LAW waste stream has a high concentration of aluminum and sodium and will require alternative immobilization methods. Five waste forms were evaluated for immobilization of LAW at Hanford after the sodium recovery process. The waste forms considered for these two waste streams include low temperature processes (Saltstone/Cast stone and geopolymers), intermediate temperature processes (steam reforming and phosphate glasses) and high temperature processes (vitrification). These immobilization methods and the waste forms produced were evaluated for (1) compliance with the Performance Assessment (PA) requirements for disposal at the IDF, (2) waste form volume (waste loading), and (3) compatibility with the tank farms and systems. The iron phosphate glasses tested using the product consistency test had normalized release rates lower than the waste form requirements although the CCC glasses had higher release rates than the quenched glasses. However, the waste form failed to meet the vapor hydration test criteria listed in the WTP contract. In addition, the waste loading in the phosphate glasses were not as high as other candidate waste forms. Vitrification of HLW waste as borosilicate glass is a proven process; however the HLW and LAW streams at Hanford can vary significantly from waste currently being immobilized. The ccc glasses show lower release rates for B and Na than the quenched glasses and all glasses meet the acceptance criterion of < 4 g/L. Glass samples spiked with Re{sub 2}O{sub 7} also passed the PCT test. However, further vapor hydration testing must be performed since all the samples cracked and the test could not be performed. The waste loading of the iron phosphate and borosilicate glasses are approximately 20 and 25% respectively. The steam reforming process produced the predicted waste form for both the high and low aluminate waste streams. The predicted waste loadings for the monolithic samples is approximately 39%, which is higher than the glass waste forms; however, at the time of this report, no monolithic samples were made and therefore compliance with the PA cannot be determined. The waste loading in the geopolymer is approximately 40% but can vary with the sodium hydroxide content in the waste stream. Initial geopolymer mixes revealed compressive strengths that are greater than 500 psi for the low aluminate mixes and less than 500 psi for the high aluminate mixes. Further work testing needs to be performed to formulate a geopolymer waste form made using a high aluminate salt solution. A cementitious waste form has the advantage that the process is performed at ambient conditions and is a proven process currently in use for LAW disposal. The Saltstone/Cast Stone formulated using low and high aluminate salt solutions retained at least 97% of the Re that was added to the mix as a dopant. While this data is promising, additional leaching testing must be performed to show compliance with the PA. Compressive strength tests must also be performed on the Cast Stone monoliths to verify PA compliance. Based on testing performed for this report, the borosilicate glass and Cast Stone are the recommended waste forms for further testing. Both are proven technologies for radioactive waste disposal and the initial testing using simulated Hanford LAW waste shows compliance with the PA. Both are resistant to leaching and have greater than 25% waste loading.« less

Polaronic Transport in Phosphate Glasses Containing Transition Metal Ions

NASA Astrophysics Data System (ADS)

Henderson, Mark

The goal of this dissertation is to characterize the basic transport properties of phosphate glasses containing various amounts of TIs and to identify and explain any electronic phase transitions which may occur. The P2 O5-V2O5-WO3 (PVW) glass system will be analyzed to find the effect of TI concentration on conduction. In addition, the effect of the relative concentrations of network forming ions (SiO2 and P2O5) on transport will be studied in the P2O5-SiO2-Fe2O 3 (PSF) system. Also presented is a numerical study on a tight-binding model adapted for the purposes of modelling Gaussian traps, mimicking TI's, which are arranged in an extended network. The results of this project will contribute to the development of fundamental theories on the electronic transport in glasses containing mixtures of transition oxides as well as those containing multiple network formers without discernible phase separation. The present study on the PVW follows up on previous investigation into the effect on mixed transition ions in oxide glasses. Past research has focused on glasses containing transition metal ions from the 3d row. The inclusion of tungsten, a 5d transition metal, adds a layer of complexity through the mismatch of the energies of the orbitals contributing to localized states. The data have indicated that a transition reminiscent of a metal-insulator transition (MIT) occurs in this system as the concentration of tungsten increases. As opposed to some other MIT-like transitions found in phosphate glass systems, there seems to be no polaron to bipolaron conversion. Instead, the individual localization parameter for tungsten noticeably decreases dramatically at the transition point as well as the adiabaticity. Another distinctive feature of this project is the study of the PSF system, which contains two true network formers, phosphorous pentoxide (P2O 5) and silicon dioxide (SiO2). It is not usually possible to do a reliable investigation of the conduction properties of such glasses because the two network formers will tend to separate into different phases, making it difficult to obtain homogenous samples. The PSF system proved easier to study than other systems. The hopping in this system seems to be dominated by the Greaves mid-range mechanism. In addition, in samples containing the same proportion of iron, conductivities were found to not depend noticeably on composition, supporting the use of models focusing on the transition metal ions in calculating conductivity. Despite ostensibly changing the structural and metrical properties of the network, the ratio of the concentration of the network formers only appears to have an effect on the conductivity through changing the inter-atomic distance of iron. The numerical model adds to the evidence for the dominating contribution on the nearest-neighbor ordering of TI ions on the electrical properties of a glass; especially interesting is the reproducibility of the mixed-transition ion effect (MTE) in a numerical model where ensemble averages are taken over possible arrangements. It was also determined that the disorder arising from the spread between two types of traps can lead to a MIT as function of population. Finally, an outline of the notion of invariance in TI glasses is extended from work done by other authors, creating an opportunity for further research.

Alternate methods of applying diffusants to silicon solar cells. [screen printing of thick-film paste materials and vapor phase transport from solid sources

NASA Technical Reports Server (NTRS)

Brock, T. W.; Field, M. B.

1979-01-01

Low-melting phosphate and borate glasses were screen printed on silicon wafers and heated to form n and p junctions. Data on surface appearance, sheet resistance and junction depth are presented. Similar data are reported for vapor phase transport from sintered aluminum metaphosphate and boron-containing glass-ceramic solid sources. Simultaneous diffusion of an N(+) layer with screen-printed glass and a p(+) layer with screen-printed Al alloy paste was attempted. No p(+) back surface field formation was achieved. Some good cells were produced but the heating in an endless-belt furnace caused a large scatter in sheet resistance and junction depth for three separate lots of wafers.

Effects of titanium nanoparticles on self-cleaning and structural features of zinc-magnesium-phosphate glass

DOE Office of Scientific and Technical Information (OSTI.GOV)

Ismail, S.F.; Sahar, M.R., E-mail: mrahim057@gmail.com; Ghoshal, S.K.

Graphical abstract: Water contact angle for sample S2, S3, S4 and S5. The water contact angle increased with increased the titanium NPs content (mol%). - Highlights: • ZnO–MgO–P{sub 2}O{sub 5} embedded TiO{sub 2} NPs prepared by conventional melt-quenching method. • The amorphous nature is confirmed by X-ray diffraction spectroscopy. • The structural characteristics of glasses is investigated using FTIR and Raman. • Wettability of the glasses surface by water contact angle. - Abstract: The loss of glass transparency on surface pollutants contamination unless inhibited not only causes vision obscurity but also responsible for major aesthetic damages of cultural heritage. Itmore » is due to the sticking of fine dirt particles on wetting layers, a complex process with several possible ramifications still to be clarified. We report the influence of titanium dioxide or titania (TiO{sub 2}) nanoparticles (NPs) on the structural and self-cleaning properties of zinc–magnesium–phosphate glasses. Following melt-quenching method glass samples of optimized composition (42 − x)P{sub 2}O{sub 5}–8MgO–50ZnO–xTiO{sub 2} with x = 0, 1, 2, 3 and 4 mol% are prepared. XRD patterns verified their amorphous nature and TEM images revealed the nucleation of TiO{sub 2} NPs of average diameter ≈4.05 ± 0.01 nm. Fourier transform infrared (FTIR) spectra displayed four absorption band centred at 1618–3438 cm{sup −1}, 902– 931 cm{sup −1}, 757–762 cm{sup −1} and 531–560 cm{sup −1}. Raman spectra exhibited four peaks each accompanied by a blue-shift. Water contact angle is found to increase with the increase of titanium NPs concentration into the amorphous matrix. This knowledge can be used to set up strategies and selective treatments to preventing glass transparency loss via the modification of self-cleaning attributes.« less

The Syntheses and Structure of the First Vanadium(IV) and Vanadium(V) Binary Azides, V(N3)4, [V(N3)6]2- and [V(N3)6]- (Preprint)

DTIC Science & Technology

2009-11-17

V(N3)3(N3S2)] 2- , [22] have been reported, and no binary vanadium(V) compounds had been known except for VF5, VF6 - and V2O5 . By analogy with...valves. Volatile materials were handled in a Pyrex glass or stainless steel/Teflon-FEP vacuum line. [31] All reaction vessels were passivated with ClF3...successful synthesis of the [V(N3)6] - anion, the only binary vanadium(V) compound known besides VF5, VF6 - and V2O5 . N1’ N8 N9 N1 N2 N3 V N4 N5 N6 N2

Nonflammable potting, encapsulating and/or conformal coating compound

NASA Technical Reports Server (NTRS)

Kline, H. F.; Dawn, F.

1972-01-01

Compound formed from dimethylpolysiloxane, ammonium phosphate, and ground glass is nonflammable in air environment and self-extingushing in atmosphere of 60 percent oxygen and 40 percent nitrogen. Material may have applications for reducing industrial fire hazards and should interest aircraft industry, machinery manufacturers, and automotive industry.

Destructive Clustering of Metal Nanoparticles in Chalcogenide and Oxide Glassy Matrices.

PubMed

Shpotyuk, M V; Shpotyuk, O I; Cebulski, J; Kozyukhin, S

2016-12-01

The energetic χ-criterion is developed to parameterize difference in the origin of high-order optical non-linearity associated with metallic atoms (Cu, Ag, Au) embedded destructively in oxide- and chalcogenide glasses. Within this approach, it is unambiguously proved that covalent-bonded networks of soft semiconductor chalcogenides exemplified by binary As(Ge)-S(Se) glasses differ essentially from those typical for hard dielectric oxides like vitreous silica by impossibility to accommodate pure agglomerates of metallic nanoparticles. In an excellence according to known experimental data, it is suggested that destructive clustering of nanoparticles is possible in Cu-, Ag-, and Au-ion-implanted dielectric oxide glass media, possessing a strongly negative χ-criterion. Some recent speculations trying to ascribe equally this ability to soft chalcogenide glasses despite an obvious difference in the corresponding bond dissociation energies have been disclosed and criticized as inconclusive.

Redox equilibria of multivalent ions in silicate glasses

NASA Technical Reports Server (NTRS)

Lauer, H. V., Jr.; Morris, R. V.

1977-01-01

Experimental studies were made on the compositional dependence of the redox equilibrium of Eu in synthetic silicate liquids, together with an empirical model describing the observed compositional dependence. Electron paramagnetic resonance (EPR) was used to measure the concentration ratio of Eu(2+) to Eu(3+) in various glasses formed by rapidly quenching silicate liquids. The compositional field studied comprised mixtures of SiO2, TiO2, Al2O3, CaO, MgO, and Na2O. The proposed model describes the Eu(2+)/Eu(3+) ratio over the entire compositional field in terms of parameters easily related to each glass composition. The general applicability and utility of the model is further demonstrated by its application to the Fe(2+)-Fe(3+), Ce(3+)-Ce(4+), and Cr(3+)-Cr(6+) redox reactions in binary alkali oxide silicate glasses of Li, Na, and K.

Column Experiments to Interpret Weathering in Columbia Hills

NASA Technical Reports Server (NTRS)

Hausrath, E. M.; Morris, R.V.; Ming, D.W.; Golden, D.C.; Galindo, C.; Sutter, B.

2009-01-01

Phosphate mobility has been postulated as an indicator of early aqueous activity on Mars. In addition, rock surfaces analyzed by the Mars Exploration Rover Spirit are consistent with the loss of a phosphate- containing mineral To interpret phosphate alteration behavior on Mars, we performed column dissolution experiments leaching the primary phases Durango fluorapatite, San Carlos olivine, and basalt glass (Stapafjell Volcano, courtesy of S. Gislason, University of Iceland) [3,4]) with acidic solutions. These phases were chosen to represent quickly dissolving phases likely present in Columbia Hills. Column dissolution experiments are closer to natural dissolution conditions than batch experiments, although they can be difficult to interpret. Acidic solutions were used because the leached layers on the surfaces of these rocks have been interpreted as resulting from acid solutions [5].

UV-visible, Raman and E.S.R. studies of gamma-irradiated NiO-doped sodium metaphosphate glasses.

PubMed

ElBatal, Fatma H; Morsi, Reham M; Ouis, Mona A; Marzouk, Samir Y

2010-11-01

UV-visible spectroscopic measurements of Ni-doped sodium phosphate glasses were carried out before and after successive gamma irradiation. The undoped glass reveals strong UV absorption originating from trace iron impurities. NiO-doped glasses show characteristic absorption bands due mainly to octahedral coordination of Ni(2+) ions. Gamma irradiation produces induced bands generated from intrinsic defects and extrinsic defects. The changes in the spectroscopic data are discussed in relation to the structural evolution caused by the changes in composition and coordination state of nickel ions. The change in the growth behaviour of the induced bands is related to the annihilation or approach saturation of these characteristic induced bands. Raman and E.S.R. spectroscopic measurements confirm the presence of nickel as Ni(2+) ions in octahedral state. Copyright © 2010 Elsevier B.V. All rights reserved.

Optical transitions of Er3+/Yb3+ codoped TeO2-WO3-Bi2O3 glass.

PubMed

Shen, Xiang; Nie, Qiuhua; Xu, Tiefeng; Gao, Yuan

2005-10-01

Optical absorption and emission properties of the Er3+/Yb3+ codoped TeO2-WO3-Bi2O3 (TWB) glass has been investigated. The transition probabilities, excited state lifetimes, and the branching ratios have been predicted for Er3+ based on the Judd-Ofelt theory. The broad 1.5 microm fluorescence was observed under 970 nm excitation, and its full width at half maximum (FWHM) is 77 nm. The emission cross-section is calculated using the McCumber theory, and the peak emission cross-section is 1.03 x 10(-21) cm2 at 1.531 microm. This value is much larger than those of the silicate and phosphate glasses. Efficient green and weak red upconversion luminescence from Er3+ centers in the glass sample was observed at room temperature, and the upconversion excitation processes have been analyzed.

Putty-like bone fillers based on CaP ceramics or Biosilicate® combined with carboxymethylcellulose: Characterization, optimization, and evaluation.

PubMed

Gabbai-Armelin, Paulo R; Renno, Ana Cm; Crovace, Murilo C; Magri, Angela Mp; Zanotto, Edgar D; Peitl, Oscar; Leeuwenburgh, Sander Cg; Jansen, John A; van den Beucken, Jeroen Jjp

2017-08-01

Calcium phosphates and bioactive glass ceramics have been considered promising biomaterials for use in surgeries. However, their moldability should be further enhanced. We here thereby report the handling, physicochemical features, and morphological characteristics of formulations consisting of carboxymethylcellulose-glycerol and hydroxyapatite-tricalcium phosphate or Biosilicate® particles. We hypothesized that combining either material with carboxymethylcellulose-glycerol would improve handling properties, retaining their bioactivity. In addition to scanning electron microscopy, cohesion, mineralization, pH, and viscoelastic properties of the novel formulations, cell culture experiments were performed to evaluate the cytotoxicity and cell proliferation. Putty-like formulations were obtained with improved cohesion and moldability. Remarkably, mineralization in simulated body fluid of hydroxyapatite-tricalcium phosphate/carboxymethylcellulose-glycerol formulations was enhanced compared to pure hydroxyapatite-tricalcium phosphate. Cell experiments showed that all formulations were noncytotoxic and that HA-TCP60 and BGC50 extracts led to an increased cell proliferation. We conclude that combining carboxymethylcellulose-glycerol with either hydroxyapatite-tricalcium phosphate or Biosilicate® allows for the generation of moldable putties, improves handling properties, and retains the ceramic bioactivity.

Effect of Water-Glass Coating on HA and HA-TCP Samples for MSCs Adhesion, Proliferation, and Differentiation.

PubMed

Bajpai, Indu; Kim, Duk Yeon; Kyong-Jin, Jung; Song, In-Hwan; Kim, Sukyoung

2016-01-01

Ca-P and silicon based materials have become very popular as bone tissue engineering materials. In this study, water-glass (also known as sodium silicate glass) was coated on sintered hydroxyapatite (HA) and HA-TCP (TCP stands for tricalcium phosphate) samples and subsequently heat-treated at 600°C for 2 hrs. X-rays diffraction showed the presence of β- and α-TCP phases along with HA in the HA-TCP samples. Samples without coating, with water-glass coating, and heat-treated after water-glass coating were used to observe the adhesion and proliferation response of bone marrow derived-mesenchymal stem cells (MSCs). Cell culture was carried out for 4 hrs, 1 day, and 7 days. Interestingly, all samples showed similar response for cell adhesion and proliferation up to 7-day culture but fibronectin, E-cadherin, and osteogenic differentiation related genes (osteocalcin and osteopontin) were significantly induced in heat-treated water-glass coated HA-TCP samples. A water-glass coating on Ca-P samples was not found to influence the cell proliferation response significantly but activated some extracellular matrix genes and induced osteogenic differentiation in the MSCs.

Structure-property relations in lanthanide borate glasses

NASA Technical Reports Server (NTRS)

Chakraborty, I. N.; Day, D. E.; Lapp, J. C.; Shelby, J. E.

1985-01-01

Glass formation in the system Ln2O3-B2O3 (Ln = Nd, Sm) was studied. Glasses could be formed in the range from 0 to 28 mol pct rare-earth oxide (Ln2O3), but liquid immiscibility in these systems limits the range of homogeneous glasses to 0 to 1.5 and 25 to 28 mol pct Ln2O3. The infrared spectra indicate that the rare-earth-rich glasses are structurally similar to rare-earth metaborates (LnB3O6) which contain (B3O6)-infinity chains. The variation in density, transformation temperature, thermal expansion coefficient, and transformation-range viscosity of these glasses with the size of the rare-earth ion is discussed. Glasses near the metaborate composition have a transformation temperature of about 700 C, which is high for binary borate glasses. Glasses could not be formed in the systems Eu2O3-, Gd2O3-, Ho2O3-, and Er2O3-B2O3, even by quenching at 1300 C/s. The sudden lack of glass formation in the system Ln2O3-B2O3 with Ln(3+) ions smaller than Sm(3+) is explained on the basis of the size effect of the Ln(3+) ion on the stability of (B3O6)-infinity chains in these metaborates.

Compositional dependence of bioactivity of glasses in the system Na2O-K2O-MgO-CaO-B2O3-P2O5-SiO2.

PubMed

Brink, M; Turunen, T; Happonen, R P; Yli-Urpo, A

1997-10-01

The bioactivity, i.e., bone-bonding ability, of 26 glasses in the system Na2O-K2O-MgO-CaO-B2O3-P2O5-SiO2 was studied in vivo. This investigation of bioactivity was performed to establish the compositional dependence of bioactivity, and enabled a model to be developed that describes the relation between reactions in vivo and glass composition. Reactions in vivo were investigated by inserting glass implants into rabbit tibia for 8 weeks. The glasses and the surrounding tissue were examined using scanning electron microscopy (SEM), light microscopy, and energy-dispersive X-ray analysis (EDXA). For most of the glasses containing < 59 mol % SiO2, SEM and EDXA showed two distinct layers at the glass surface after implantation, one silica-rich and another containing calcium phosphate. The build-up of these layers in vivo was taken as a sign of bioactivity. The in vivo experiments showed that glasses in the investigated system are bioactive when they contain 14-30 mol % alkali oxides, 14-30 mol % alkaline earth oxides, and < 59 mol % SiO2. Glasses containing potassium and magnesium bonded to bone in a similar way as bioactive glasses developed so far.

Intensity fluctuations of erbium-doped whispering gallery mode lasers (Conference Presentation)

NASA Astrophysics Data System (ADS)

Féron, Patrice; Ceppe, Jean-Baptiste; Dumeige, Yannick; Mortier, Michel S.

2017-02-01

Micro spherical resonators have attracted significant attention in recent years due to their interesting optical properties and the range of applications for which they can be used. Most of the publications dedicated to micro spherical Laser are devoted to lasing effects in different materials where the spectral properties of the emission depends on (i) the choice of dopant (e.g. Er3+, Yb3+, Tm3+) and (ii) the host matrix (e.g. silica, fluoride, phosphate or telluride glass) in which the dopant is embedded. Yet, the dynamics of theses Lasers are still to be studied. This paper shows experimental results on the amplitude fluctuations of a Whispering Gallery Mode Laser, also known as relative intensity noise (RIN). It gives information about the dynamics inside the cavity, such as photon lifetime, effective pumping rate and noise sources. We use as active medium Er3+ doped fluoride ZBLALiP glass and also industrial IOG-1 Yb3+- Er3+ co-doped phosphate glass. Theses glasses are well adapted to the development of micro spherical Laser operating in the infrared region, in particular with emission wavelengths falling respectively in the C-band and C+L band. We have observed that the RIN can provide insurance about the emission of the Laser. Moreover, we have shown that a single-mode emission comes with the presence of multiple harmonics of the relaxation frequency, which is the signature of a Laser with high noise levels. In this particular case, the second and higher orders of intensity fluctuations cannot be neglected any longer in the small-signal analysis.

Concentration-dependent studies of Nd3+ -doped zinc phosphate glasses for NIR photoluminescence at 1.05 μm.

PubMed

Reddy Prasad, V; Seshadri, M; Babu, S; Ratnakaram, Y C

2017-05-01

Nd 3 + -doped lead-free zinc phosphate glasses with the chemical compositions (60-x) NH 4 H 2 PO 4  + 20ZnO + 10BaF 2  + 10NaF + xNd 2 O 3 (where x = 0.5, 1.0, 1.5, 2.0 and 2.5 mol%) were prepared using a melt quenching technique. Vibrational bands were assigned and clearly elucidated by Raman spectral profiles for all the glass samples. Judd-Ofelt (J-O) intensity parameters (Ω λ : λ = 2, 4, 6) were obtained from the spectral intensities of different absorption bands of Nd 3 + ions. Radiative properties such as radiative transition probabilities (A R ), radiative lifetimes (τ R ) and branching ratios (β R ) for different excited states were calculated using J-O parameters. The near infrared (NIR) photoluminescence spectra exhibited three emission bands ( 4 F 3 /2 level to 4 I 13 /2 , 4 I 11 /2 and 4 I 9 /2 states) for all the concentrations of Nd 3 + ions. Various luminescence properties were studied by varying the Nd 3 + concentration for the three spectral profiles. Fluorescence decay curves of the 4 F 3 /2 level were recorded. The energy transfer mechanism that leads to quenching of the 4 F 3 /2 state lifetimes was discussed at higher concentration of Nd 3 + ions. These glasses are suggested as suitable hosts to produce efficient lasing action in NIR region at 1.05 μm. Copyright © 2016 John Wiley & Sons, Ltd.

High-beam quality, high-efficiency laser based on fiber with heavily Yb(3+)-doped phosphate core and silica cladding.

PubMed

Egorova, O N; Semjonov, S L; Medvedkov, O I; Astapovich, M S; Okhrimchuk, A G; Galagan, B I; Denker, B I; Sverchkov, S E; Dianov, E M

2015-08-15

We have fabricated and tested a composite fiber with an Yb(3+)-doped phosphate glass core and silica cladding. Oscillation with a slope efficiency of 74% was achieved using core pumping at 976 nm with fiber lengths of 48-90 mm in a simple laser configuration, where the cavity was formed by a high-reflectivity Bragg grating and the cleaved fiber end. The measured M(2) factors were as low as 1.05-1.22 even though the fiber was multimode at the lasing wavelength.

Effect of biochar type on macronutrient retention and release from soilless substrate

USDA-ARS?s Scientific Manuscript database

A series of column studies were conducted to determine the influence of three different biochar types on nitrate, phosphate, and potassium retention and leaching in a typical greenhouse soilless substrate. Glass columns were filled with 85 sphagnum peat moss : 15 perlite (v:v) and amended with 10% ...

Crystal genes in a marginal glass-forming system of Ni 50Zr 50

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wen, T. Q.; Tang, L.; Sun, Y.

Glass-forming motifs with B2 traits are found. A perfect Ni-centered B33 motif deteriorates the glass-forming ability of Ni 50Zr 50. The marginal glass-forming ability (GFA) of binary Ni-Zr system is an issue to be explained considering the numerous bulk metallic glasses (BMGs) found in the Cu-Zr system. Using molecular dynamics, the structures and dynamics of Ni 50Zr 50 metallic liquid and glass are investigated at the atomistic level. To achieve a well-relaxed glassy sample, sub-T g annealing method is applied and the final sample is closer to the experiments than the models prepared by continuous cooling. With the state-of-the-art structuralmore » analysis tools such as cluster alignment and pair-wise alignment methods, two glass-forming motifs with some mixed traits of the metastable B2 crystalline phase and the crystalline Ni-centered B33 motif are found to be dominant in the undercooled liquid and glass samples. A new chemical order characterization on each short-range order (SRO) structure is accomplished based on the cluster alignment method. The significant amount of the crystalline motif and the few icosahedra in the glassy sample deteriorate the GFA.« less

Crystal genes in a marginal glass-forming system of Ni 50Zr 50

DOE PAGES

Wen, T. Q.; Tang, L.; Sun, Y.; ...

2017-10-17

Glass-forming motifs with B2 traits are found. A perfect Ni-centered B33 motif deteriorates the glass-forming ability of Ni 50Zr 50. The marginal glass-forming ability (GFA) of binary Ni-Zr system is an issue to be explained considering the numerous bulk metallic glasses (BMGs) found in the Cu-Zr system. Using molecular dynamics, the structures and dynamics of Ni 50Zr 50 metallic liquid and glass are investigated at the atomistic level. To achieve a well-relaxed glassy sample, sub-T g annealing method is applied and the final sample is closer to the experiments than the models prepared by continuous cooling. With the state-of-the-art structuralmore » analysis tools such as cluster alignment and pair-wise alignment methods, two glass-forming motifs with some mixed traits of the metastable B2 crystalline phase and the crystalline Ni-centered B33 motif are found to be dominant in the undercooled liquid and glass samples. A new chemical order characterization on each short-range order (SRO) structure is accomplished based on the cluster alignment method. The significant amount of the crystalline motif and the few icosahedra in the glassy sample deteriorate the GFA.« less

In vitro stimulation of vascular endothelial growth factor by borate-based glass fibers under dynamic flow conditions.

PubMed

Chen, Sisi; Yang, Qingbo; Brow, Richard K; Liu, Kun; Brow, Katherine A; Ma, Yinfa; Shi, Honglan

2017-04-01

Bioactive borate glass has been recognized to have both hard and soft tissue repair and regeneration capabilities through stimulating both osteogenesis and angiogenesis. However, the underlying biochemical and cellular mechanisms remain unclear. In this study, dynamic flow culturing modules were designed to simulate the micro-environment near the vascular depletion and hyperplasia area in wound-healing regions, thus to better investigate the mechanisms underlying the biocompatibility and functionality of borate-based glass materials. Glass fibers were dosed either upstream or in contact with the pre-seeded cells in the dynamic flow module. Two types of borate glasses, doped with (1605) or without (13-93B3) CuO and ZnO, were studied along with the silicate-based glass, 45S5. Substantial fiber dissolution in cell culture medium was observed, leading to the release of ions (boron, sodium and potassium) and the deposition of a calcium phosphate phase. Different levels of vascular endothelial growth factor secretion were observed from cells exposed to these three glass fibers, and the copper/zinc containing borate 1605 fibers exhibited the most positive influence. These results indicate that dynamic studies of in vitro bioactivity provide useful information to understand the in vivo response to bioactive borate glasses. Copyright © 2016 Elsevier B.V. All rights reserved.

Effect of cryogenic temperature on spectroscopic and laser properties of Er, Yb-doped potassium-lanthanum phosphate glass

NASA Astrophysics Data System (ADS)

Švejkar, Richard; Šulc, Jan; Němec, Michal; Jelínková, Helena; Nitsch, Karel; Cihlář, Antonín.; Král, Robert; Nejezchleb, Karel; Nikl, Martin

2017-05-01

Glass matrix doped with rare-earth ions is a promising laser active medium for high power laser systems. Due to amorphous structure of glasses the absorption and emission spectra lines are broader in comparison with crystalline materials thus pumping radiation can be absorbed efficiently, moreover much broader gain bandwidth is suitable for generation of ultra-short pulses. Another advantage of the glass matrix is the possibility to fabricate large volume ingots and simultaneously preservation of sufficient optical quality. The lower thermal conductivity of glasses can be compensated by geometry of the active medium for instance shaped into fibres or discs. We present temperature dependence of spectroscopic and laser properties of newly developed Er, Yb - doped potassium-lanthanum phosphate glass, which is appropriate for generation of radiation at 1.53 μm. The sample of Er,Yb:KLaP glassy mixture was cut into disc shape with dimensions of 2.5 mm (thickness) and 5 mm (diameter) and its faces were polished plan-parallelly without being anti-reflection coated. The temperature dependence of the transmission and emission spectra Er,Yb:KLaP together with the fluorescence decay time were measured the temperature range from 80 to 400 K. The fluorescence lifetime of manifold 4I13/2 (upper laser level) prolonged and the intensity of up-conversion radiation decreased with decreasing temperature. The longitudinal excitation of Er,Yb:KLaP was carried out by a fibre-coupled laser diode (pulse duration 2 ms, repetition rate 10 Hz, pump wavelength 969 nm). Laser resonator was hemispherical, with flat pumping mirror (HR @ 1.5 μm) and spherical output coupler (R = 98 % @ 1.5 - 1.6 μm). The Er,Yb:KLaP glass laser properties were investigated in the temperature range 80 - 300 K. The highest slope efficiency with respect to absorbed pumped power was 6.1 % at 80 K. The maximum output of peak amplitude power was 0.71 W at 80 K, i.e. 1.2 times higher than at 300 K. Tunability of laser wavelength at 80 K in range 1528 - 1552 nm was obtained using MgF2 birefringent filter. From our measurement it can be concluded, that spectroscopic and laser properties of newly developed Er,Yb:KLaP glass are slightly temperature dependent.

Investigation of focusing and correcting aberrations with binary amplitude and polarization modulation

DOE PAGES

Fiala, Peter; Li, Yunqi; Dorrer, Christophe

2018-01-29

Here, we investigate the focusing and correcting wavefront aberration of an optical wave using binary amplitude and polarization modulation. Focusing is performed by selectively modulating the field in different zones of the pupil to obtain on-axis constructive interference at a given distance. The conventional Soret zone plate (binary amplitude profile) is expanded to a polarization Soret zone plate with twice the focusing efficiency. Binary pixelated devices that approximate the sinusoidal transmission profile of a Gabor zone plate by spatial dithering are also investigated with amplitude and polarization modulation. Wavefront aberrations are corrected by modulation of the field in the pupilmore » plane to prevent destructive interference in the focal plane of an ideal focusing element. Polarization modulation improves the efficiency obtained by amplitude-only modulation, with a gain that depends on the aberration. Experimental results obtained with Cr-on-glass devices for amplitude modulation and liquid crystal devices operating in the Mauguin condition for polarization modulation are in very good agreement with simulations.« less

Investigation of focusing and correcting aberrations with binary amplitude and polarization modulation

DOE Office of Scientific and Technical Information (OSTI.GOV)

Fiala, Peter; Li, Yunqi; Dorrer, Christophe

Here, we investigate the focusing and correcting wavefront aberration of an optical wave using binary amplitude and polarization modulation. Focusing is performed by selectively modulating the field in different zones of the pupil to obtain on-axis constructive interference at a given distance. The conventional Soret zone plate (binary amplitude profile) is expanded to a polarization Soret zone plate with twice the focusing efficiency. Binary pixelated devices that approximate the sinusoidal transmission profile of a Gabor zone plate by spatial dithering are also investigated with amplitude and polarization modulation. Wavefront aberrations are corrected by modulation of the field in the pupilmore » plane to prevent destructive interference in the focal plane of an ideal focusing element. Polarization modulation improves the efficiency obtained by amplitude-only modulation, with a gain that depends on the aberration. Experimental results obtained with Cr-on-glass devices for amplitude modulation and liquid crystal devices operating in the Mauguin condition for polarization modulation are in very good agreement with simulations.« less

Evaluation of retentive strength of four luting cements with stainless steel crowns in primary molars: An in vitro study

PubMed Central

Parisay, Iman; Khazaei, Yegane

2018-01-01

Background: Stainless steel crown (SSC) is the most reliable restoration for primary teeth with extensive caries. Retention is of great importance for a successful restoration and is provided by various factors such as luting cements. The aim of this study was to evaluate the retentive strength of SSC cemented with four different luting cements. Materials and Methods: In this in vitro study, A total of 55 extracted primary first molars were selected. Following crown selection and cementation (one with no cement and four groups cemented with resin, glass ionomer, zinc phosphate, and polycarboxylate), all the specimens were incubated and thermocycled in 5°C–55°C. Retentive properties of SSCs were tested with a mechanical test machine. First dislodgement of each specimen and full crown removal were recorded. One-way ANOVA test followed by least significant difference test and Kruskal–Wallis test was used for retentive strength comparison at the level of significance of P < 0.05. Results: The results of the study showed that the specimens cemented with zinc phosphate exhibited higher retentive strength as compared to glass ionomer and polycarboxylate (P < 0.001 and P = 0.023, respectively). Conclusion: Zinc phosphate cement showed the most promising results; thus, it can be preferably used for cementation of the teeth with no grossly broken down crowns. PMID:29922339

Atomic-Level Structure Studies of Rare-Earth Doped Sodium Phosphate Glasses Using High Energy X-Ray Diffraction and Complementary Techniques

NASA Astrophysics Data System (ADS)

Amir, Faisal

The atomic-scale structure of a series of (RE2 O3)x ( Na2O)y ( P2O5)1- x-y glasses (RE = Pr, Nd, Er) where has been characterized by high-energy X-ray diffraction technique (HEXRD). In addition, differential thermal analysis (DTA), Fourier transform infrared (FTIR) spectroscopy, and absorption and emission spectroscopy in visible and near IR ranges have been used as supplementary tools to validate structural features obtained from HEXRD techniques.Structural features such as inter-atomic distances and coordination numbers and their dependence on the concentration of RE 2 O3 have been obtained by analyzing pair distribution functions (PDF) extracted from diffraction data. Coordination numbers for P-O, Na-O, O-O, and P-P were found to be independent of the RE 2 O3 concentration. In contrast, the RE-O coordination number varies between ≈ 8 and 7.2 as the RE2 O3 concentration increases from 0.005 to 0.05. The variation of the bond distance between large rare-earth ions (Pr, Nd) and small rare-earth ion (Er) is approximately 0.2 A, which is attributed to lanthanide contraction. The Na-O coordination number in these glasses was observed to ≈ 5.0 as the RE2 O 3 content increases. The overlapping correlation of RE-O, Na-O, and O-O in the same vicinity makes it difficult to calculate these coordination numbers. DTA measurements were used for the investigation of thermal characteristics of glasses. From these measurements, it is evident that the glass transition temperature increases with increasing the RE2 O3 (RE=Pr, Er) content. FTIR was used to inspect the structural changes of the glasses. The doping of RE 2 O3 (RE=Pr, Er) induces depolymerization of the glasses at the Q3 tetrahedral sites. The forming of the ionic linkages between phosphate chains is attributed to the increase in non-bridging oxygen (NBO). The cross-linkages density (CLD) increases with the RE2 O3 (RE=Pr, Er) concentrations. Absorption spectra for x = 0.01 of Er 3+ and 0.005-0.05 for Nd3+ doped glasses have been analyzed using Judd-Ofelt (JO) theory. The JO parameters have been used to predict radiative properties of luminescent levels of Er3+ and Nd3+ ions. Comparatively large photoluminescence lifetime 13.76 msec (x = 0.01) for Er3+ and 476 microsec ( x = 0.005) for Nd3+ for the laser transition was observed. However, the quantum efficiency of the erbium doped glasses is ≈70 %. The influence of RE 3+ (RE = Er, Nd) doping concentration on the emission spectra and lifetimes was investigated wit the model proposed by Auzel's limited diffusion model, in order to study the concentration quenching effect on luminescence. In this model, the fitting of the fluorescence lifetime experimental data gives us a radiative lifetime (tau0) and quenching concentration (N0). For Neodymium glasses, tau0 = 467 microsec and N0 = 5.98 x 1020 ions/cm3 Nd3+ ion, and in erbium glasses, tau0 = 12.4 ms at N0= 1.57 x 1020 ions/cm3 for Er3+ ion. The Inokuti-Hirayama (IH) model has been applied to the non-exponential behavior of the decay profiles to investigate the mechanism involved in the energy transfer between the donors and acceptors. Emission spectra of rare earth phosphate glasses show that their fluorescence efficiency decreases with increasing rare-earth content even at relatively at low concentrations (0.005 < x < 0.05), suggesting that concentration quenching of lasing action may be present even at these concentrations.

Structure, biodegradation behavior and cytotoxicity of alkali-containing alkaline-earth phosphosilicate glasses.

PubMed

Kansal, Ishu; Reddy, AlluAmarnath; Muñoz, Francisco; Choi, Seong-Jun; Kim, Hae-Won; Tulyaganov, Dilshat U; Ferreira, José M F

2014-11-01

We report on the effect of sodium on the structure, chemical degradation and bioactivity of glasses in the CaO-MgO-SiO2-P2O5-CaF2 system. The (29)Si and (31)P magic angle spinning-nuclear magnetic resonance spectroscopy of melt-quenched glasses with varying Na2O/MgO ratios exhibit a silicate glass network with the dominance of Q(2)(Si) units and phosphorus mainly forming orthophosphate species. Sodium incorporation in the glasses did not induce a significant structural change in the silicate network, while it did influence the phosphate environment due to its lower ionic field strength in comparison with that of magnesium. The apatite forming ability of glasses has been investigated by immersion of glass powders in simulated body fluid (SBF) for time durations varying between 1h and 7 days while their chemical degradation has been studied in Tris-HCl in accordance with ISO-10993-14. Increasing Na(+)/Mg(2+) ratio caused a decrease in the chemical durability of glasses and in the apatite forming ability especially during initial steps of interaction between glass and SBF solution. The cellular responses were observed in vitro on bulk glass samples using mouse-derived pre-osteoblastic MC3T3-E1 cell line. The preliminary study suggested that the increasing alkali-concentration in glasses led to cytotoxicity in the cell culture medium. Copyright © 2014 Elsevier B.V. All rights reserved.

Preparation and antifouling properties of 2-(meth-acryloyloxy)ethyl cholinephosphate based polymers modified surface with different molecular architectures by ATRP.

PubMed

Jiang, Yuchen; Su, Yuling; Zhao, Lili; Meng, Fancui; Wang, Quanxin; Ding, Chunmei; Luo, Jianbin; Li, Jianshu

2017-08-01

Choline phosphate (CP) containing polymers modified surfaces have been shown good resist to the adhesion of proteins while prompt the attaching of mammalian cells due to the dipole pairing between the CP groups of the polymer and the phosphorylcholine (PC) groups on the cell membrane. However, the antifouling activities of CP modified surface against microbes have not been investigated at present. In addition, CP containing polymers modified surface with different molecular architectures has not been prepared and studied. To this end, glass slides surface modified with two different 2-(meth-acryloyloxy)ethyl cholinephosphate (MCP) containing polymer (PMCP) structures, i.e. brush-like (Glass-PMCP) and bottle brush-like (Glass-PHEMA-g-PMCP) architectures, were prepared in this work by surface-initiated atom transfer radical polymerization (SI-ATRP). The surface physichemical and antifouling properties of the prepared surfaces were characterized and studied. The Glass-PMCP shows improved antifouling properties against proteins and bacteria as compared to pristine glass slides (Glass-OH) and glass slides grafted with poly(2-hydroxyethyl methacrylate) (Glass-PHEMA). Notably, a synergetic fouling resistant properties of PHEMA and PMCP is presented for Glass-PHEMA-g-PMCP, which shows superior antifouling activities over Glass-PHEMA and Glass-PMCP. Furthermore, glass slides containing PMCP, i.e. Glass-PMCP and Glas-PHEMA-g-PMCP, decrease platelet adhesion and prevent their activation significantly. Therefore, the combination of antifouling PHEMA and PMCP into one system holds potential for prevention of bacterial fouling and biomaterial-centered infections. Copyright © 2017 Elsevier B.V. All rights reserved.

Effects of cooling rate on particle rearrangement statistics: Rapidly cooled glasses are more ductile and less reversible.

PubMed

Fan, Meng; Wang, Minglei; Zhang, Kai; Liu, Yanhui; Schroers, Jan; Shattuck, Mark D; O'Hern, Corey S

2017-02-01

Amorphous solids, such as metallic, polymeric, and colloidal glasses, display complex spatiotemporal response to applied deformations. In contrast to crystalline solids, during loading, amorphous solids exhibit a smooth crossover from elastic response to plastic flow. In this study, we investigate the mechanical response of binary Lennard-Jones glasses to athermal, quasistatic pure shear as a function of the cooling rate used to prepare them. We find several key results concerning the connection between strain-induced particle rearrangements and mechanical response. We show that the energy loss per strain dU_{loss}/dγ caused by particle rearrangements for more rapidly cooled glasses is larger than that for slowly cooled glasses. We also find that the cumulative energy loss U_{loss} can be used to predict the ductility of glasses even in the putative linear regime of stress versus strain. U_{loss} increases (and the ratio of shear to bulk moduli decreases) with increasing cooling rate, indicating enhanced ductility. In addition, we characterized the degree of reversibility of particle motion during a single shear cycle. We find that irreversible particle motion occurs even in the linear regime of stress versus strain. However, slowly cooled glasses, which undergo smaller rearrangements, are more reversible during a single shear cycle than rapidly cooled glasses. Thus, we show that more ductile glasses are also less reversible.

Preferable removal of phosphate from water using hydrous zirconium oxide-based nanocomposite of high stability.

PubMed

Chen, Liang; Zhao, Xin; Pan, Bingcai; Zhang, Weixian; Hua, Ming; Lv, Lu; Zhang, Weiming

2015-03-02

In this study, we employed a new nanocomposite adsorbent HZO-201, which featured high stability under varying solution chemistry, for preferable removal of phosphate from synthetic solution and a real effluent. An anion exchange resin (D-201) was employed as the host of HZO-201, where nano-hydrous zirconium oxide (HZO) was encapsulated as the active species. D-201 binds phosphate through nonspecific electrostatic affinity, whereas the loaded HZO nanoparticles capture phosphate through formation of the inner-sphere complexes. Quantitative contribution of both species to phosphate adsorption was predicted based on the double-Langmuir model. Preferable removal of phosphate by HZO-201 was observed in the presence of the competing anions at higher levels (Cl(-), NO3(-), SO4(2-), HCO3(-)). Fixed-bed adsorption indicated that the effective volume capacity of a synthetic water (2.0 mg P-PO4(3-)/L) by using HZO-201 was ∼1600 BV in the first run (<0.5mg P-PO4(3-)/L), comparable to Fe(III)-based nanocomposite HFO-201 (∼1500 BV) and much larger than D-201 (<250 BV). The exhausted HZO-201 can be in situ regenerated by using a binary NaOH-NaCl solution for cyclic runs, whether fed with the synthetic solution or real effluent. In general, HZO-201 is a promising alternative to Fe(III)-based adsorbents for trace phosphate removal from effluent particularly at acidic pH. Copyright © 2014 Elsevier B.V. All rights reserved.

Neodymium glass laser with a phase conjugate mirror producing 220 J pulses at 0.02 Hz repetition rate.

PubMed

Kuzmin, A A; Khazanov, E A; Kulagin, O V; Shaykin, A A

2014-08-25

For pumping multipetawatt Ti:sapphire laser facilities we developed a compact repetitively pulsed laser based on neodymium phosphate glass with pulse energy of 220 J, pulse repetition rate of 0.02 Hz, beam diameter of 43 mm, aperture fill factor of 0.8, and FWHM pulse duration of 30 ns. The phase distortions of laser radiation were compensated by optical phase conjugation via stimulated Brillouin scattering. The depolarization was reduced to 0.4% using linear compensation methods. The beam quality was 2.5 x diffraction limit (150 µrad).

Characterization of a Shiga-Like Toxin Converting Phage Isolated from an Escherichia coli Strain Responsible for Hemorrhagic Colitis in Humans

DTIC Science & Technology

1985-01-01

filled with 20X SSPE (salt-sodium phosphate-EDTA) (Maniatis, 1982) and air bubbles trapped under the 3 ýM paper were pressed out with a glass rod. Next...nitrocellulose filter moist ned with 20X SSPE was placed on top of the gel and air bubbles were again pressed out with a glass rod. Two pieces of 3 M paper were...then soaked in 5X SSPE 27 for 10 minutes, dried at room temperature, and baked for 2 hours at 800 C under vacuum (Maniatis et al., 1982

Multiple rare-earth ion environments in amorphous (Gd2O3 ) 0.230(P2O5) 0.770 revealed by gadolinium K -edge anomalous x-ray scattering

NASA Astrophysics Data System (ADS)

Cole, Jacqueline M.; Cramer, Alisha J.; Shastri, Sarvjit D.; Mukaddem, Karim T.; Newport, Robert J.

2018-04-01

A Gd K -edge anomalous x-ray scattering (AXS) study is performed on the rare-earth (R ) phosphate glass, (Gd2O3 ) 0.230(P2O5) 0.770 , in order to determine Gd ⋯Gd separations in its local structure. The minimum rare-earth separation is of particular interest given that the optical properties of these glasses can quench when rare-earth ions become too close to each other. To this end, a weak Gd ⋯Gd pairwise correlation is located at 4.2 (1 )Å , which is representative of a metaphosphate R ⋯R separation. More intense first-neighbor Gd ⋯Gd pairwise correlations are found at the larger radial distributions, 4.8(1), 5.1(1), and 5.4 (1 )Å . These reflect a mixed ultraphosphate and metaphosphate structural character, respectively. A second-neighbor Gd ⋯Gd pairwise correlation lies at 6.6 (1 )Å which is indicative of metaphosphate structures. Meta- and ultraphosphate classifications are made by comparing the R ⋯R separations against those of rare-earth phosphate crystal structures, R (PO3) 3 and R P5O14 , respectively, or difference pair-distribution function (Δ PDF ) features determined on similar glasses using difference neutron-scattering methods. The local structure of this glass is therefore found to display multiple rare-earth ion environments, presumably because its composition lies between these two stoichiometric formulae. These Gd ⋯Gd separations are well-resolved in Δ PDFs that represent the AXS signal. Indeed, the spatial resolution is so good that it also enables the identification of R ⋯X (X =R , P, O) pairwise correlations up to r ˜9 Å ; their average separations lie at r ˜7.1 (1 ) , 7.6(1), 7.9(1), 8.4(1), and 8.7 (1 )Å . This is a report of a Gd K -edge AXS study on an amorphous material. Its demonstrated ability to characterize the local structure of a glass up to such a long range of r heralds exciting prospects for AXS studies on other ternary noncrystalline materials. However, the technical challenge of such an experiment should not be underestimated, as is highlighted in this work where probing AXS signal near the Gd K edge is found to produce inelastic x-ray scattering that precludes the normal AXS methods of data processing. Nonetheless, it is shown that AXS results are not only tractable but they also reveal local structure of rare-earth phosphate glasses that is important from a materials-centered perspective and which could not be obtained by other materials characterization methods.

Influence of sodium content on the properties of bioactive glasses for use in air abrasion.

PubMed

Farooq, Imran; Tylkowski, Maxi; Müller, Steffen; Janicki, Tomasz; Brauer, Delia S; Hill, Robert G

2013-12-01

Air abrasion is used in minimally invasive dentistry for preparing cavities, while removing no or little sound dentine or enamel, and the use of bioactive glass (rather than alumina) as an abrasive could aid in tooth remineralization. Melt-derived bioactive glasses (SiO2-P2O5-CaO-CaF2-Na2O) with low sodium content (0 to 10 mol% Na2O in exchange for CaO) for increased hardness, high phosphate content for high bioactivity and fluoride content for release of fluoride and formation of fluorapatite were produced, and particles between 38 and 80 µm in size were used for cutting soda-lime silicate glass microscope slides and human enamel. Vickers hardness increased with decreasing Na2O content, owing to a more compact silicate network in low sodium content glasses, resulting in shorter cutting times. Cutting times using bioactive glass were significantly longer than using the alumina control (29 µm) when tested on microscope slides; however, glasses showed more comparable results when cutting human enamel. The bioactive glasses formed apatite in Tris buffer within 6 h, which was significantly faster than Bioglass® 45S5 (24 h), suggesting that the hardness of the glasses makes them suitable for air abrasion application, while their high bioactivity and fluoride content make them of interest for tooth remineralization.

Theoretical Studies of the Spin Hamiltonian Parameters and Local Distortions for Cu2+ in Alkaline Earth Lead Zinc Phosphate Glasses

NASA Astrophysics Data System (ADS)

Wang, Bo-Kun; Wu, Shao-Yi; Yuan, Zi-Yi; Liu, Zi-Xuan; Jiang, Shi-Xin; Liu, Zheng; Yao, Zi-Jian; Teng, Bao-Hua; Wu, Ming-He

2016-08-01

The spin Hamiltonian parameters and local structures are theoretically studied for Cu2+-doped alkaline earth lead zinc phosphate (RPPZ, R=Mg, Ca, Sr, and Ba) glasses based on the high-order perturbation calculations for a tetragonally elongated octahedral 3d9 cluster. The relative elongation ratios are found to be ρ≈3.2%, 4.4%, 4.6%, and 3.3% for R=Mg, Ca, Sr, and Ba, respectively, because of the Jahn-Teller effect. The whole decreasing crystal-field strength Dq and orbital reduction factor k from Mg to Sr are ascribed to the weakening electrostatic coulombic interactions and the increasing probability of productivity of nonbridge oxygen (and hence increasing Cu2+-O2- electron cloud admixtures) under PbO addition, respectively, with increasing alkali earth ionic radius. The anomalies (the largest Dq and the next highest k among the systems) for R=Ba are attributed to the cross linkage of this large cation in the network. The overall increasing order (Mg≤Ba

Impact Chemistry and the Origin of Life

NASA Astrophysics Data System (ADS)

Melosh, H. J.; Pasek, M.

2012-12-01

Most discussions of global environmental effects of large impacts focus on changes deleterious to extant life. However, impacts may also produce changes that enhance or even create conditions beneficial to the origin of life. Many other authors have discussed impact delivery of organic molecules, and some have shown the shock synthesis of prebiotic molecules such as amino acids during impact. Our past work on the chemistry of impacts demonstrated that strong chemical reduction occurs in impact melt ejecta (spherules and melt droplets; tektites). Here we focus on the element phosphorus (P), whose role is crucial in biology as the backbone of DNA and RNA, and in metabolic biochemical energy transfer. Pasek previously showed that reduced P readily enters into interesting biological compounds with organic molecules in aqueous solution, and that these reduced P compounds may generate structures similar to sugar phosphates, which are critical to life as we know it. In this talk we argue that impact reduction of P transforms terrestrial and meteoritic phosphates bearing an oxidation state of +5 to the lower redox states of +3 (phosphites) and 0 as an alloy with metal (phosphides). We base this argument on studies of fulgurites—glasses formed by cloud-to-ground lightning—that bear phosphides and phosphites as major carriers of P. Fulgurite chemistry frequently parallels that of impact glasses. Additionally, thermodynamic calculations show that separation of an O-rich vapor from a melt readily results in the transformation of phosphate to phosphites and metal phosphides. These results are confirmed by the presence of metal phosphides within tektites. The impact reduction of phosphates followed by global dispersal of reduced P in the form of glassy droplets likely played a major role in the origin of life on Earth and perhaps on other young planets.

Boson peak, heterogeneity and intermediate-range order in binary SiO2-Al2O3 glasses.

PubMed

Ando, Mariana F; Benzine, Omar; Pan, Zhiwen; Garden, Jean-Luc; Wondraczek, Katrin; Grimm, Stephan; Schuster, Kay; Wondraczek, Lothar

2018-03-29

In binary aluminosilicate liquids and glasses, heterogeneity on intermediate length scale is a crucial factor for optical fiber performance, determining the lower limit of optical attenuation and Rayleigh scattering, but also clustering and precipitation of optically active dopants, for example, in the fabrication of high-power laser gain media. Here, we consider the low-frequency vibrational modes of such materials for assessing structural heterogeneity on molecular scale. We determine the vibrational density of states VDoS g(ω) using low-temperature heat capacity data. From correlation with low-frequency Raman spectroscopy, we obtain the Raman coupling coefficient. Both experiments allow for the extraction of the average dynamic correlation length as a function of alumina content. We find that this value decreases from about 3.9 nm to 3.3 nm when mildly increasing the alumina content from zero (vitreous silica) to 7 mol%. At the same time, the average inter-particle distance increases slightly due to the presence of oxygen tricluster species. In accordance with Loewensteinian dynamics, this proves that mild alumina doping increases structural homogeneity on molecular scale.

Adsorption of perfluorooctane sulfonate on soils: Effects of soil characteristics and phosphate competition.

PubMed

Qian, Jin; Shen, Mengmeng; Wang, Peifang; Wang, Chao; Hou, Jun; Ao, Yanhui; Liu, Jingjing; Li, Kun

2017-02-01

Perfluorooctane sulfonate (PFOS) is an emerging contaminant, whose presence has been detected in different compartments of the environment in many countries. In this study, the effects of soil characteristics and phosphate competition on the adsorption of PFOS on soils were investigated. Results from batch sorption experiments showed that all the adsorption isotherms of PFOS on three tested soils were nonlinear. In experiments without the addition of phosphate (P) to the soil solution, the Freundlich sorption affinity (K f ) of PFOS on S (original soil), S1 (soil from which soil organic matter (SOM) had been removed), and S2 (soil from which both SOM and ferric oxides had been removed) were 23.13, 10.37 and 15.95, respectively. The results suggested that a high amount of SOM in soil can increase the sorption affinity of PFOS on soils and that a greater amount of ferric oxides can reduce it. The addition of P in the soil solution reduced the K f of PFOS on S, S1, and S2 by approximately 25%, 50%, and 15%, respectively. For the binary system of PFOS and P, soil with higher ferric oxide content showed greater K f reduction after P addition; whereas soil with higher SOM content showed less K f reduction. Our results suggest that for soils dominated by ferric oxides, P is a more effective competitor than PFOS for the adsorption sites in the binary system; whereas in soils containing more SOM, P is a weak competitor. Copyright © 2016 Elsevier Ltd. All rights reserved.

Structure of high alumina content Al2O3-SiO2 composition glasses.

PubMed

Weber, Richard; Sen, Sabyasachi; Youngman, Randall E; Hart, Robert T; Benmore, Chris J

2008-12-25

The structure of binary aluminosilicate glasses containing 60-67 mol % Al2O3 were investigated using high-resolution 27Al NMR and X-ray and neutron diffraction. The glasses were made by aerodynamic levitation of molten oxides. The 67% alumina composition required a cooling rate of approximately 1600 degrees C s(1-) to form glass from submillimeter sized samples. NMR results show that the glasses contain aluminum in 4-, 5-, and 6-fold coordination in the approximate ratio 4:5:1. The average Al coordination increases from 4.57 to 4.73 as the fraction of octahedral Al increases with alumina content. The diffraction results on the 67% composition are consistent with a disordered Al framework with Al ions in a range of coordination environments that are substantially different from those found in the equilibrium crystalline phases. Analysis of the neutron and X-ray structure factors yields an average bond angle of 125 +/- 4 degrees between an Al ion and the adjoining cation via a bridging oxygen. We propose that the structure of the glass is a "transition state" between the alumina-rich liquid and the equilibrium mullite phase that are dominated by 4- and 6-coordinated aluminum ions, respectively.

Experimental study on cesium immobilization in struvite structures.

PubMed

Wagh, Arun S; Sayenko, S Y; Shkuropatenko, V A; Tarasov, R V; Dykiy, M P; Svitlychniy, Y O; Virych, V D; Ulybkina, Е А

2016-01-25

Ceramicrete, a chemically bonded phosphate ceramic, was developed for nuclear waste immobilization and nuclear radiation shielding. Ceramicrete products are fabricated by an acid-base reaction between magnesium oxide and mono potassium phosphate that has a struvite-K mineral structure. In this study, we demonstrate that this crystalline structure is ideal for incorporating radioactive Cs into a Ceramicrete matrix. This is accomplished by partially replacing K by Cs in the struvite-K structure, thus forming struvite-(K, Cs) mineral. X-ray diffraction and thermo-gravimetric analyses are used to confirm such a replacement. The resulting product is non-leachable and stable at high temperatures, and hence it is an ideal matrix for immobilizing Cs found in high-activity nuclear waste streams. The product can also be used for immobilizing secondary waste streams generated during glass vitrification of spent fuel, or the method described in this article can be used as a pretreatment method during glass vitrification of high level radioactive waste streams. Furthermore, it suggests a method of producing safe commercial radioactive Cs sources. Copyright © 2015 Elsevier B.V. All rights reserved.

Phosphate glass useful in high energy lasers

DOEpatents

Hayden, Yuiko T.; Guesto-Barnak, Donna

1992-01-01

A low-or no-silica, low- or no-alkali phosphate glass useful as a laser amplifier in a multiple pass, high energy laser system having a high thermal conductivity, K.sub.90.degree. C. >0.85 W/mK, a low coefficient of thermal expansion, .alpha..sub.20.degree.-300.degree. C. <80.times.10.sup.-7 /.degree.C., low emission cross section, .sigma.<2.5.times.10.sup.-20 cm.sup.2, and a high fluorescence lifetime, .tau.>325 .mu.secs at 3 wt. % Nd doping, consisting essentially of (on an oxide composition basis): wherein Ln.sub.2 O.sub.3 is the sum of lanthanide oxides; .SIGMA.R.sub.2 O is <5, R being Li, Na, K, Cs, and Rb; the sum of Al.sub.2 O.sub.3 and MgO is <24 unless .SIGMA.R.sub.2 O is 0, then the sum of Al.sub.2 O.sub.3 and MgO is <42; and the ratio of MgO to B.sub.2 O.sub.3 is 0.48-4.20.

Corrosion of dental amalgam and mercury vapor emission in vitro.

PubMed

Moberg, L E

1988-10-01

Amalgam specimens were immersed for 30 days in 1) water, 2) 0.9% NaCl in water, 3) 0.9% NaCl and 10 mM phosphate buffer in water, and 4) 0.9% NaCl, 7.7 mM phosphate, and 6.1 mM citric acid in water. The solutions were stored in stoppered glass tubes. Hg-drops were immersed in solutions 1, 2, and 3. The concentration of mercury vapor in the air above the solutions was measured once a day. After 30 days the amounts of Cu, Zn, Hg, and Ag in the solutions were analyzed by atomic absorption spectrophotometry. The results showed that 0.9% NaCl alone or in combination with the additives increased the amounts of elements released into the solutions. The concentration of Hg0 in the glass tubes increased with the amount of Hg in the solutions, with the exception of solution No. 3, from which significantly less Hg0 evaporated. The results indicate that the composition of the saliva, oral hygiene and dietary factors may be determinants of Hg0 emission from amalgams in the oral cavity.

Behavior of soluble and immobilized acid phosphatase in hydro-organic media.

PubMed

Wan, H; Horvath, C

1975-11-20

The hydrolysis of p-nitrophenyl phosphate by wheat germ acid phosphatase (orthophosphoric monoester phosphohydrolase, EC 3.1.3.2) has been investigated in mixtures of aqueous buffers with acetone, dioxane and acetonitrile. The enzyme was either in free solution or immobilized on a pellicular support which consisted of a porous carbonaceous layer on solid glass beads. The highest enzyme activity was obtained in acetone and acetonitrile mixed with citrate buffer over a wide range of organic solvent concentration. In 50% (v/v) acetone both V and Km of the immobilized enzyme were about half of the values in the neat aqueous buffer, but the Ki for inorganic phosphate was unchanged. In 50% (v/v) mixtures of various solvents and citrate buffers of different pH, the enzymic activity was found to depend on the pH of the aqueous buffer component rather than the pH of the hydro-organic mixture as measured with the glass-calomel electrode. The relatively high rates of p-nitrophenol liberation in the presence of glucose even at high organic solvent concentrations suggest that transphosphorylation is facilitated at low water activity.

Mineral stimulation of subsurface microorganisms: release of limiting nutrients from silicates

USGS Publications Warehouse

Roger, Jennifer Roberts; Bennett, Philip C.

2004-01-01

Microorganisms play an important role in the weathering of silicate minerals in many subsurface environments, but an unanswered question is whether the mineral plays an important role in the microbial ecology. Silicate minerals often contain nutrients necessary for microbial growth, but whether the microbial community benefits from their release during weathering is unclear. In this study, we used field and laboratory approaches to investigate microbial interactions with minerals and glasses containing beneficial nutrients and metals. Field experiments from a petroleum-contaminated aquifer, where silicate weathering is substantially accelerated in the contaminated zone, revealed that phosphorus (P) and iron (Fe)-bearing silicate glasses were preferentially colonized and weathered, while glasses without these elements were typically barren of colonizing microorganisms, corroborating previous studies using feldspars. In laboratory studies, we investigated microbial weathering of silicates and the release of nutrients using a model ligand-promoted pathway. A metal-chelating organic ligand 3,4 dihydroxybenzoic acid (3,4 DHBA) was used as a source of chelated ferric iron, and a carbon source, to investigate mineral weathering rate and microbial metabolism.In the investigated aquifer, we hypothesize that microbes produce organic ligands to chelate metals, particularly Fe, for metabolic processes and also form stable complexes with Al and occasionally with Si. Further, the concentration of these ligands is apparently sufficient near an attached microorganism to destroy the silicate framework while releasing the nutrient of interest. In microcosms containing silicates and glasses with trace phosphate mineral inclusions, microbial biomass increased, indicating that the microbial community can use silicate-bound phosphate inclusions. The addition of a native microbial consortium to microcosms containing silicates or glasses with iron oxide inclusions correlated to accelerated weathering and release of Si into solution as well as the accelerated degradation of the model substrate 3,4 DHBA. We propose that silicate-bound P and Fe inclusions are bioavailable, and microorganisms may use organic ligands to dissolve the silicate matrix and access these otherwise limiting nutrients.

Development and validation of a microchip pulsed laser for ESA space altimeters

NASA Astrophysics Data System (ADS)

Couto, Bruno; Abreu, Hernâni; Gordo, Paulo; Amorim, António

2016-10-01

The development and validation of small size laser sources for space based range finding is of crucial importance to the development of miniature LIDAR devices for European space missions, particularly for planet lander probes. In this context, CENTRA-SIM is developing a passively q-switched microchip laser in the 1.5μm wavelength range. Pulses in the order of 2 ns and 100μJ were found to be suitable for range finding for small landing platforms. Both glass and crystalline Yb-Er doped active media are commonly available. Crystalline media present higher thermal conductivity and hardness, which allows for higher pumping intensities. However, glass laser media present longer laser upper-state lifetime and 99% Yb-Er transfer efficiency make phosphate glasses the typically preferred host for this type of application. In addition to this, passively q-switched microchip lasers with Yb-Er doped phosphate glass have been reported to output >100μJ pulses while their crystalline host counterparts achieve a few tens of μJ at best. Two different types of rate equation models have been found: microscopic quantities based models and macroscopic quantities based models. Based on the works of Zolotovskaya et al. and Spühler et al, we have developed a computer model that further exploits the equivalence between the two types of approaches. The simulation studies, using commercial available components allowed us to design a compact laser emitting 80μJ pulses with up to 30kW peak power and 1 to 2 ns pulse width. We considered EAT14 Yb-Er doped glass as active medium and Co2+:MgAl2O4 as saturable absorber. The active medium is pumped by a 975nm semiconductor laser focused into a 200μm spot. Measurements on an experimental test bench to validate the numerical model were carried out. Several different combinations of, saturable absorber length and output coupling were experimented.

Intense red photoluminescence from Mn2+-doped (Na+; Zn2+) sulfophosphate glasses and glass ceramics as LED converters.

PubMed

Da, Ning; Peng, Mingying; Krolikowski, Sebastian; Wondraczek, Lothar

2010-02-01

We report on intense red fluorescence from Mn(2+)-doped sulfophosphate glasses and glass ceramics of the type ZnO-Na(2)O-SO(3)-P(2)O(5). As a hypothesis, controlled internal crystallization of as-melted glasses is achieved on the basis of thermally-induced bimodal separation of an SO(3)-rich phase. Crystal formation is then confined to the relict structure of phase separation. The whole synthesis procedure is performed in air at

Alkali-free bioactive glasses for bone regeneration =

NASA Astrophysics Data System (ADS)

Kapoor, Saurabh

Bioactive glasses and glass-ceramics are a class of third generation biomaterials which elicit a special response on their surface when in contact with biological fluids, leading to strong bonding to living tissues. The purpose of the present study was to develop diopside based alkali-free bioactive glasses in order to achieve good sintering behaviour, high bioactivity, and a dissolution/ degradation rates compatible with the target applications in bone regeneration and tissue engineering. Another aim was to understand the structure-property relationships in the investigated bioactive glasses. In this quest, various glass compositions within the Diopside (CaMgSi2O6) - Fluorapatite (Ca5(PO4)3F) - Tricalcium phosphate (3CaO•P2O5) system have been investigated. All the glasses were prepared by melt-quenching technique and characterized by a wide array of complementary characterization techniques. The glass-ceramics were produced by sintering of glass powders compacts followed by a suitable heat treatment to promote the nucleation and crystallization phenomena. Furthermore, selected parent glass compositions were doped with several functional ions and an attempt to understand their effects on the glass structure, sintering ability and on the in vitro bio-degradation and biomineralization behaviours of the glasses was made. The effects of the same variables on the devitrification (nucleation and crystallization) behaviour of glasses to form bioactive glass-ceramics were also investigated. Some of the glasses exhibited high bio-mineralization rates, expressed by the formation of a surface hydroxyapatite layer within 1-12 h of immersion in a simulated body fluid (SBF) solution. All the glasses showed relatively lower degradation rates in comparison to that of 45S5 Bioglass. Some of the glasses showed very good in vitro behaviour and the glasses co-doped with zinc and strontium showed an in vitro dose dependent behaviour. The as-designed bioactive glasses and glass-ceramic materials are excellent candidates for applications in bone regeneration and for the fabrication of scaffolds for tissue engineering.

What is the origin of concentration quenching of Cu+ luminescence in glass?

NASA Astrophysics Data System (ADS)

Jiménez, José A.

2016-10-01

Monovalent copper-doped luminescent glasses are attractive materials for white light-emitting devices, photonic waveguides, and solar spectral conversion in photovoltaic cells. However, the occurrence of concentration quenching in such is not fully understood at present. In this work, calcium-phosphate glasses with high concentrations of luminescent Cu+ ions have been prepared by a simple melt-quench method via CuO and SnO co-doping. The aim is to elucidate the origin of concentration quenching of Cu+ light emission. A spectroscopic characterization was carried out by optical absorption and photoluminescence (PL) spectroscopy including emission decay dynamics. The concentrations of both CuO and SnO dopants were varied as 5, 10 and 15 mol%. Monovalent copper content is estimated in the CuO/SnO-containing glasses following the assessment of the concentration dependence of Cu2+ absorption in the visible for CuO singly-doped glasses. Contrary to the conventionally acknowledged direct Cu+→Cu2+ transfer, the data supports a Cu+-Cu+ energy migration channel at the origin of the PL quenching.

3D FEA of cemented glass fiber and cast posts with various dental cements in a maxillary central incisor.

PubMed

Madfa, Ahmed A; Al-Hamzi, Mohsen A; Al-Sanabani, Fadhel A; Al-Qudaimi, Nasr H; Yue, Xiao-Guang

2015-01-01

This study aimed to analyse and compare the stability of two dental posts cemented with four different luting agents by examining their shear stress transfer through the FEM. Eight three-dimensional finite element models of a maxillary central incisor restored with glass fiber and Ni-Cr alloy cast dental posts. Each dental post was luted with zinc phosphate, Panavia resin, super bond C&B resin and glass ionomer materials. Finite element models were constructed and oblique loading of 100 N was applied. The distribution of shear stress was investigated at posts and cement/dentine interfaces using ABAQUS/CAE software. The peak shear stress for glass fiber post models minimized approximately three to four times of those for Ni-Cr alloy cast post models. There was negligible difference in peak of shear stress when various cements were compared, irrespective of post materials. The shear stress had same trend for all cement materials. This study found that the glass fiber dental post reduced the shear stress concentration at interfacial of post and cement/dentine compared to Ni-Cr alloy cast dental post.

Bio-corrosion and cytotoxicity studies on novel Zr 55Co 30Ti 15 and Cu 60Zr 20Ti 20 metallic glasses

DOE PAGES

Vincent, S.; Daiwile, A.; Devi, S. S.; ...

2014-09-26

Metallic glasses are a potential and compatible implant candidate for biomedical applications. In the present investigation, a comparative study between novel Zr 55Co 30Ti 15 and Cu 60Zr 20Ti 20 metallic glasses is carried out to evaluate in vitro biocompatibility using simulated body fluids. The bio-corrosion behavior of Zr- and Cu-based metallic glasses in different types of artificial body fluids such as artificial saliva solution, phosphate-buffered saline solution, artificial blood plasma solution, and Hank’s balanced saline solution is evaluated using potentiodynamic polarization studies at a constant body temperature of 310.15 K (37 °C). Surface morphology of samples after bio-corrosion experimentsmore » was observed by scanning electron microscopy. In vitro cytotoxicity test on glassy alloys were performed using human osteosarcoma cell line as per 10993-5 guidelines from International Organization for Standardization. As a result, the comparative study between Zr- and Cu-based glassy alloys provides vital information about the effect of elemental composition on biocompatibility of metallic glasses.« less

Characterization and spectroscopic studies of multi-component calcium zinc bismuth phosphate glass ceramics doped with iron ions

NASA Astrophysics Data System (ADS)

Kumar, A. Suneel; Narendrudu, T.; Suresh, S.; Ram, G. Chinna; Rao, M. V. Sambasiva; Tirupataiah, Ch.; Rao, D. Krishna

2018-04-01

Glass ceramics with the composition 10CaF2-20ZnO-(15-x)Bi2O3-55P2O5:x Fe2O3(0≤x≤2.5) were synthesized by melt-quenching technique and heat treatment. These glass ceramics were characterized by XRD and SEM. Spectroscopic studies such as optical absorption, EPR were also carried out on these glass ceramics. From the absorption spectra the observed bands around 438 and 660nm are the octahedral transitions of Fe3+ (d5) ions and another band at about 536 nm is the tetrahedral transition of Fe3+ (d5) ions. The absorption spectrum also consist of a band around 991 nm and is attributed to the octahedral transition of Fe2+ ions. The EPR spectra of the prepared glass ceramics have exhibited two resonance signals one at g1=4.32 and another signal at g2=2.008. The observed decrease in band gap energy up to 2 mol% Fe2O3 doped glass ceramics is an evidence for the change of environment around iron ions and ligands from more covalent to less covalent (ionic) and induces higher concentration of NBOs which causes the depolymerization of the glass ceramic network.

Efficient Nd3+→Yb3+ energy transfer processes in high phonon energy phosphate glasses for 1.0 μm Yb3+ laser

NASA Astrophysics Data System (ADS)

Rivera-López, F.; Babu, P.; Basavapoornima, Ch.; Jayasankar, C. K.; Lavín, V.

2011-06-01

Efficient Nd3+→Yb3+ resonant and phonon-assisted energy transfer processes have been observed in phosphate glasses and have been studied using steady-state and time-resolved optical spectroscopies. Results indicate that the energy transfer occurs via nonradiative electric dipole-dipole processes and is enhanced with the concentration of Yb3+ acceptor ions, having an efficiency higher than 75% for the glass doped with 1 mol% of Nd2O3 and 4 mol% of Yb2O3. The luminescence decay curves show a nonexponential character and the energy transfer microscopic parameter calculated with the Inokuti-Hirayama model gives a value of 240 × 10-40 cm6 s-1, being one of the highest reported in the literature for Nd3+-Yb3+ co-doped matrices. From the steady-state experimental absorption and emission cross-sections, a general expression for estimating the microscopic energy transfer parameter is proposed based upon the theoretical methods developed by Miyakawa and Dexter and Tarelho et al. This expression takes into account all the resonant mechanisms involved in an energy transfer processes together with other phonon-assisted nonvanishing overlaps. The value of the Nd3+→Yb3+ energy transfer microscopic parameter has been calculated to be 200 × 10-40 cm6 s-1, which is in good agreement with that obtained from the Inokuti-Hirayama fitting. These results show the importance of the nonresonant phonon-assisted Nd3+→Yb3+ energy transfer processes and the great potential of these glasses as active matrices in the development of multiple-pump-channel Yb3+ lasers.

The role of Bi2O3 on the thermal, structural, and optical properties of tungsten-phosphate glasses.

PubMed

Manzani, Danilo; de Araújo, Cid B; Boudebs, Georges; Messaddeq, Younès; Ribeiro, Sidney J L

2013-01-10

Glasses in the ternary system (70 - x)NaPO(3)-30WO(3)-xBi(2)O(3), with x = 0-30 mol %, were prepared by the conventional melt-quenching technique. X-ray diffraction (XRD) measurements were performed to confirm the noncrystalline nature of the samples. The influence of the Bi(2)O(3) on the thermal, structural, and optical properties was investigated. Differential scanning calorimetry analysis showed that the glass transition temperature, T(g), increases from 405 to 440 °C for 0 ≤ x ≤ 15 mol % and decreases to 417 °C for x = 30 mol %. The thermal stability against devitrification decreases from 156 to 67 °C with the increase of the Bi(2)O(3) content. The structural modifications were studied by Raman scattering, showing a bismuth insertion into the phosphate chains by Bi-O-P linkage. Furthermore, up to 15 mol % of Bi(2)O(3) formation of BiO(6) clusters is observed, associated with Bi-O-Bi linkage, resulting in a progressive break of the linear phosphate chains that leads to orthophosphate Q(0) units. The linear refractive index, n(0), was measured using the prism-coupler technique at 532, 633, and 1550 nm, whereas the nonlinear (NL) refractive index, n(2) was measured at 1064 nm using the Z-scan technique. Values of 1.58 ≤ n(0) ≤ 1.88, n(2) ≥ 10(-15) cm(2)/W and NL absorption coefficient, α(2) ≤ 0.01 cm/GW, were determined. The linear and NL refractive indices increase with the increase of the Bi(2)O(3) concentration. The large values of n(0) and n(2), as well as the very small α(2), indicate that these materials have large potential for all-optical switching applications in the near-infrared.

Bismuth silicate glass containing heavy metal oxide as a promising radiation shielding material

NASA Astrophysics Data System (ADS)

Elalaily, Nagia A.; Abou-Hussien, Eman M.; Saad, Ebtisam A.

2016-12-01

Optical and FTIR spectroscopic measurements and electron paramagnetic resonance (EPR) properties have been utilized to investigate and characterize the given compositions of binary bismuth silicate glasses. In this work, it is aimed to study the possibility of using the prepared bismuth silicate glasses as a good shielding material for γ-rays in which adding bismuth oxide to silicate glasses causes distinguish increase in its density by an order of magnitude ranging from one to two more than mono divalent oxides. The good thermal stability and high density of the bismuth-based silicate glass encourage many studies to be undertaken to understand its radiation shielding efficiency. For this purpose a glass containing 20% bismuth oxide and 80% SiO2 was prepared using the melting-annealing technique. In addition the effects of adding some alkali heavy metal oxides to this glass, such as PbO, BaO or SrO, were also studied. EPR measurements show that the prepared glasses have good stability when exposed to γ-irradiation. The changes in the FTIR spectra due to the presence of metal oxides were referred to the different housing positions and physical properties of the respective divalent Sr2+, Ba2+ and Pb2+ ions. Calculations of optical band gap energies were presented for some selected glasses from the UV data to support the probability of using these glasses as a gamma radiation shielding material. The results showed stability of both optical and magnetic spectra of the studied glasses toward gamma irradiation, which validates their irradiation shielding behavior and suitability as the radiation shielding candidate materials.

Sol-gel derived lithium-releasing glass for cartilage regeneration.

PubMed

Li, Siwei; Maçon, Anthony L B; Jacquemin, Manon; Stevens, Molly M; Jones, Julian R

2017-07-01

Wnt-signalling cascade is one of the crucial pathways involved in the development and homeostasis of cartilage. Influencing this pathway can potentially contribute to improved cartilage repair or regeneration. One key molecular regulator of the Wnt pathway is the glycogen synthase kinase-3 enzyme, the inhibition of which allows initiation of the signalling pathway. This study aims to utilise a binary SiO 2 -Li 2 O sol-gel derived glass for controlled delivery of lithium, a known glycogen synthase kinase-3 antagonist. The effect of the dissolution products of the glass on chondrogenic differentiation in an in vitro 3D pellet culture model is reported. Dissolution products that contained 5 mM lithium and 3.5 mM silicon were capable of inducing chondrogenic differentiation and hyaline cartilaginous matrix formation without the presence of growth factors such as TGF-β3. The results suggest that sol-gel derived glass has the potential to be used as a delivery vehicle for therapeutic lithium ions in cartilage regeneration applications.

[Raman spectroscopic study of binary PbO-TeO2 glasses].

PubMed

Huang, Li; You, Jing-Lin; Chen, Hui; Jiang, Guo-Chang

2008-07-01

Raman spectra of lead tellurite glasses and their melts were measured. Results show that four coordinate tellurite units convert into three coordinate units with increasing the concentration of PbO, and the number of non-bridging oxygen bonds (NBO) increases accordingly in this system. Three spectral peaks in the high frequency range were assigned to stretching vibration of bridging oxygen in four coordinate tellurite units (Q(b)), stretching vibration of non-bridging oxygen in four coordinate tellurite units (Q(nb)) and in three coordinate tellurite units (T(nb)). The relative density of four coordinate structure units decreases and the three coordinate tellurite units considerably exist in tellurite glasses when the concentration of PbO > 50%. Besides, the Raman frequencies of the three species' peaks become blue-shifted because of the temperature induced crystallization at high temperature, and the peak intensities increase and the peaks sharpen. The peaks merge together and become much broader while the glass is heated above the melting point because of multiple microstructure units coexisting.