DOE Office of Scientific and Technical Information (OSTI.GOV)

Han,W.Q.

Boron nitride (BN) is a synthetic binary compound located between III and V group elements in the Periodic Table. However, its properties, in terms of polymorphism and mechanical characteristics, are rather close to those of carbon compared with other III-V compounds, such as gallium nitride. BN crystallizes into a layered or a tetrahedrally linked structure, like those of graphite and diamond, respectively, depending on the conditions of its preparation, especially the pressure applied. Such correspondence between BN and carbon readily can be understood from their isoelectronic structures [1, 2]. On the other hand, in contrast to graphite, layered BN ismore » transparent and is an insulator. This material has attracted great interest because, similar to carbon, it exists in various polymorphic forms exhibiting very different properties; however, these forms do not correspond strictly to those of carbon. Crystallographically, BN is classified into four polymorphic forms: Hexagonal BN (h-BN) (Figure 1(b)); rhombohedral BN (r-BN); cubic BN (c-BN); and wurtzite BN (w-BN). BN does not occur in nature. In 1842, Balmain [3] obtained BN as a reaction product between molten boric oxide and potassium cyanide under atmospheric pressure. Thereafter, many methods for its synthesis were reported. h-BN and r-BN are formed under ambient pressure. c-BN is synthesized from h-BN under high pressure at high temperature while w-BN is prepared from h-BN under high pressure at room temperature [1]. Each BN layer consists of stacks of hexagonal plate-like units of boron and nitrogen atoms linked by SP{sup 2} hybridized orbits and held together mainly by Van der Waals force (Fig 1(b)). The hexagonal polymorph has two-layered repeating units: AA'AA'... that differ from those in graphite: ABAB... (Figure 1(a)). Within the layers of h-BN there is coincidence between the same phases of the hexagons, although the boron atoms and nitrogen atoms are alternatively located along the c-axis. The rhombohedral system consists of three-layered units: ABCABC..., whose honeycomb layers are arranged in a shifted phase, like as those of graphite. Reflecting its weak interlayer bond, the h-BN can be cleaved easily along its layers, and hence, is widely used as a lubricant material. The material is stable up to a high temperature of 2300 C before decomposition sets in [2] does not fuse a nitrogen atmosphere of 1 atm, and thus, is applicable as a refractory material. Besides having such properties, similar to those of graphite, the material is transparent, and acts as a good electric insulator, especially at high temperatures (10{sup 6} {Omega}m at 1000 C) [1]. c-BN and w-BN are tetrahedrally linked BN. The former has a cubic sphalerite-type structure, and the latter has a hexagonal wurtzite-type structure. c-BN is the second hardest known material (the hardest is diamond), the so-called white diamond. It is used mainly for grinding and cutting industrial ferrous materials because it does not react with molten iron, nickel, and related alloys at high temperatures whereas diamond does [1]. It displays the second highest thermal conductivity (6-9 W/cm.deg) after diamond. This chapter focuses principally upon information about h-BN nanomaterials, mainly BN nanotubes (BNNTs), porous BN, mono- and few-layer-BN sheets. There are good reviews book chapters about c-BN in [1, 4-6].« less

Core-level photoabsorption study of defects and metastable bonding configurations in boron nitride

DOE Office of Scientific and Technical Information (OSTI.GOV)

Jimenez, I.; Jankowski, A.F.; Terminello, L.J.

1997-04-01

Boron nitride is an interesting material for technological applications and for fundamental solid state physics investigations. It is a compound isoelectronic with carbon and, like carbon can possess sp{sup 2} and sp{sup 3} bonded phases resembling graphite and diamond. BN crystallizes in the sp{sup 2}-bonded hexagonal (h-BN), rhombohedral (r-BN) and turbostratic phases, and in the sp{sup 3}-bonded cubic (c-BN) and wurtzite (w-BN) phases. A new family of materials is obtained when replacing C-C pairs in graphite with isoelectronic B-N pairs, resulting in C{sub 2}BN compounds. Regarding other boron compounds, BN is exceptional in the sense that it has standard two-centermore » bonds with conventional coordination numbers, while other boron compounds (e.g. B{sub 4}C) are based on the boron icosahedron unit with three-center bonds and high coordination numbers. The existence of several allotropic forms and fullerene-like structures for BN suggests a rich variety of local bonding and poses the questions of how this affects the local electronic structure and how the material accommodates the stress induced in the transition regions between different phases. One would expect point defects to play a crucial role in stress accommodation, but these must also have a strong influence in the electronic structure, since the B-N bond is polar and a point defect will thus be a charged structure. The study of point defects in relationship to the electronic structure is of fundamental interest in these materials. Recently, the authors have shown that Near-Edge X-ray Absorption Fine Structure (NEXAFS) is sensitive to point defects in h-BN, and to the formation of metastable phases even in amorphous materials. This is significant since other phase identification techniques like vibrational spectroscopies or x-ray diffraction yield ambiguous results for nanocrystalline and amorphous samples. Serendipitously, NEXAFS also combines chemical selectivity with point defect sensitivity.« less

Understanding the Scalability of Bayesian Network Inference using Clique Tree Growth Curves

NASA Technical Reports Server (NTRS)

Mengshoel, Ole Jakob

2009-01-01

Bayesian networks (BNs) are used to represent and efficiently compute with multi-variate probability distributions in a wide range of disciplines. One of the main approaches to perform computation in BNs is clique tree clustering and propagation. In this approach, BN computation consists of propagation in a clique tree compiled from a Bayesian network. There is a lack of understanding of how clique tree computation time, and BN computation time in more general, depends on variations in BN size and structure. On the one hand, complexity results tell us that many interesting BN queries are NP-hard or worse to answer, and it is not hard to find application BNs where the clique tree approach in practice cannot be used. On the other hand, it is well-known that tree-structured BNs can be used to answer probabilistic queries in polynomial time. In this article, we develop an approach to characterizing clique tree growth as a function of parameters that can be computed in polynomial time from BNs, specifically: (i) the ratio of the number of a BN's non-root nodes to the number of root nodes, or (ii) the expected number of moral edges in their moral graphs. Our approach is based on combining analytical and experimental results. Analytically, we partition the set of cliques in a clique tree into different sets, and introduce a growth curve for each set. For the special case of bipartite BNs, we consequently have two growth curves, a mixed clique growth curve and a root clique growth curve. In experiments, we systematically increase the degree of the root nodes in bipartite Bayesian networks, and find that root clique growth is well-approximated by Gompertz growth curves. It is believed that this research improves the understanding of the scaling behavior of clique tree clustering, provides a foundation for benchmarking and developing improved BN inference and machine learning algorithms, and presents an aid for analytical trade-off studies of clique tree clustering using growth curves.

Initial stages of growth and the influence of temperature during chemical vapor deposition of sp{sup 2}-BN films

DOE Office of Scientific and Technical Information (OSTI.GOV)

Chubarov, Mikhail; Pedersen, Henrik; Högberg, Hans

2015-11-15

Knowledge of the structural evolution of thin films, starting by the initial stages of growth, is important to control the quality and properties of the film. The authors present a study on the initial stages of growth and the temperature influence on the structural evolution of sp{sup 2} hybridized boron nitride (BN) thin films during chemical vapor deposition (CVD) with triethyl boron and ammonia as precursors. Nucleation of hexagonal BN (h-BN) occurs at 1200 °C on α-Al{sub 2}O{sub 3} with an AlN buffer layer (AlN/α-Al{sub 2}O{sub 3}). At 1500 °C, h-BN grows with a layer-by-layer growth mode on AlN/α-Al{sub 2}O{sub 3} upmore » to ∼4 nm after which the film structure changes to rhombohedral BN (r-BN). Then, r-BN growth proceeds with a mixed layer-by-layer and island growth mode. h-BN does not grow on 6H-SiC substrates; instead, r-BN nucleates and grows directly with a mixed layer-by-layer and island growth mode. These differences may be caused by differences in substrate surface temperature due to different thermal conductivities of the substrate materials. These results add to the understanding of the growth process of sp{sup 2}-BN employing CVD.« less

Novel 3D metallic boron nitride containing only sp2 bonds

NASA Astrophysics Data System (ADS)

Wang, Hao; Zhang, Wei; Huai, Ping

2017-09-01

As the closest isoelectronic analogue of carbon, boron nitride (BN) shares a similar structure with carbon from 1D nanotubes, 2D nanosheets, and 3D diamond structures. However, most BN structures are insulators, which limits their application. In this work, under the inspiration of the sp2 hybridized carbon honeycomb, we propose a hexagonal phase of BN consisting of only sp2 bonds, which exhibits intriguingly intrinsic metallicity. First-principles calculations confirm that this phase is both thermally and dynamically stable. Moreover, the calculations on the band structure, partial density states and electron localization function suggest that the metallic behavior is attributable to the delocalized B-2p electrons, leading to second-neighbor interaction between the p z states of sp2-bonded B atoms in adjacent layers. Our findings not only enrich the BN allotrope family with 3D structures but also stimulate further experimental interest in applications of metallic BN in electronic devices.

Ultralight boron nitride aerogels via template-assisted chemical vapor deposition

PubMed Central

Song, Yangxi; Li, Bin; Yang, Siwei; Ding, Guqiao; Zhang, Changrui; Xie, Xiaoming

2015-01-01

Boron nitride (BN) aerogels are porous materials with a continuous three-dimensional network structure. They are attracting increasing attention for a wide range of applications. Here, we report the template-assisted synthesis of BN aerogels by catalyst-free, low-pressure chemical vapor deposition on graphene-carbon nanotube composite aerogels using borazine as the B and N sources with a relatively low temperature of 900 °C. The three-dimensional structure of the BN aerogels was achieved through the structural design of carbon aerogel templates. The BN aerogels have an ultrahigh specific surface area, ultralow density, excellent oil absorbing ability, and high temperature oxidation resistance. The specific surface area of BN aerogels can reach up to 1051 m2 g−1, 2-3 times larger than the reported BN aerogels. The mass density can be as low as 0.6 mg cm−3, much lower than that of air. The BN aerogels exhibit high hydrophobic properties and can absorb up to 160 times their weight in oil. This is much higher than porous BN nanosheets reported previously. The BN aerogels can be restored for reuse after oil absorption simply by burning them in air. This is because of their high temperature oxidation resistance and suggests broad utility as water treatment tools. PMID:25976019

Ultralight boron nitride aerogels via template-assisted chemical vapor deposition.

PubMed

Song, Yangxi; Li, Bin; Yang, Siwei; Ding, Guqiao; Zhang, Changrui; Xie, Xiaoming

2015-05-15

Boron nitride (BN) aerogels are porous materials with a continuous three-dimensional network structure. They are attracting increasing attention for a wide range of applications. Here, we report the template-assisted synthesis of BN aerogels by catalyst-free, low-pressure chemical vapor deposition on graphene-carbon nanotube composite aerogels using borazine as the B and N sources with a relatively low temperature of 900 (°)C. The three-dimensional structure of the BN aerogels was achieved through the structural design of carbon aerogel templates. The BN aerogels have an ultrahigh specific surface area, ultralow density, excellent oil absorbing ability, and high temperature oxidation resistance. The specific surface area of BN aerogels can reach up to 1051 m(2) g(-1), 2-3 times larger than the reported BN aerogels. The mass density can be as low as 0.6 mg cm(-3), much lower than that of air. The BN aerogels exhibit high hydrophobic properties and can absorb up to 160 times their weight in oil. This is much higher than porous BN nanosheets reported previously. The BN aerogels can be restored for reuse after oil absorption simply by burning them in air. This is because of their high temperature oxidation resistance and suggests broad utility as water treatment tools.

Linking Structural Equation Modelling with Bayesian Network and Coastal Phytoplankton Dynamics in Bohai Bay

NASA Astrophysics Data System (ADS)

Chu, Jiangtao; Yang, Yue

2018-06-01

Bayesian networks (BN) have many advantages over other methods in ecological modelling and have become an increasingly popular modelling tool. However, BN are flawed in regard to building models based on inadequate existing knowledge. To overcome this limitation, we propose a new method that links BN with structural equation modelling (SEM). In this method, SEM is used to improve the model structure for BN. This method was used to simulate coastal phytoplankton dynamics in Bohai Bay. We demonstrate that this hybrid approach minimizes the need for expert elicitation, generates more reasonable structures for BN models and increases the BN model's accuracy and reliability. These results suggest that the inclusion of SEM for testing and verifying the theoretical structure during the initial construction stage improves the effectiveness of BN models, especially for complex eco-environment systems. The results also demonstrate that in Bohai Bay, while phytoplankton biomass has the greatest influence on phytoplankton dynamics, the impact of nutrients on phytoplankton dynamics is larger than the influence of the physical environment in summer. Furthermore, despite the Redfield ratio indicating that phosphorus should be the primary nutrient limiting factor, our results indicate that silicate plays the most important role in regulating phytoplankton dynamics in Bohai Bay.

Structural analysis of graphene and h-BN: A molecular dynamics approach

DOE Office of Scientific and Technical Information (OSTI.GOV)

Thomas, Siby; Ajith, K. M., E-mail: ajith@nitk.ac.in; Valsakumar, M. C.

2016-05-06

Classical molecular dynamics simulation is employed to analyze pair correlations in graphene and h-BN at various temperatures to explore the integrity of their respective structures. As the temperature increases, the height fluctuations in the out-of-plane direction of both graphene and h-BN are found to increase. The positional spread of atoms also increases with temperature. Thus the amplitude of the peak positions in the radial distribution function (RDF) decreases with temperature. It is found that FWHM of peaks in the RDF of h-BN is smaller as compared to those of graphene which implies that the structure of h-BN is more robustmore » as compared to that of graphene with respect to their respective empirical potential.« less

High-Yield Synthesis of Stoichiometric Boron Nitride Nanostructures

DOE PAGES

Nocua, José E.; Piazza, Fabrice; Weiner, Brad R.; ...

2009-01-01

Boron nimore » tride (BN) nanostructures are structural analogues of carbon nanostructures but have completely different bonding character and structural defects. They are chemically inert, electrically insulating, and potentially important in mechanical applications that include the strengthening of light structural materials. These applications require the reliable production of bulk amounts of pure BN nanostructures in order to be able to reinforce large quantities of structural materials, hence the need for the development of high-yield synthesis methods of pure BN nanostructures. Using borazine ( B 3 N 3 H 6 ) as chemical precursor and the hot-filament chemical vapor deposition (HFCVD) technique, pure BN nanostructures with cross-sectional sizes ranging between 20 and 50 nm were obtained, including nanoparticles and nanofibers. Their crystalline structure was characterized by (XRD), their morphology and nanostructure was examined by (SEM) and (TEM), while their chemical composition was studied by (EDS), (FTIR), (EELS), and (XPS). Taken altogether, the results indicate that all the material obtained is stoichiometric nanostructured BN with hexagonal and rhombohedral crystalline structure.« less

Electronic Properties of Curved and Defective 2-D BN Nanostructures

NASA Astrophysics Data System (ADS)

Beach, Kory; Terrones, Humberto; Raeliarijaona, Aldo; Siegel, Ross; Florio, Fred

Density functional theory (DFT) with local density approximation (LDA) pseudopotentials is used to calculate the band structure and density of states of various novel 2-D BN nanostructures. Three types of systems are studied: Schwarzites, a Haeckelite, and an h-BN monolayer. Schwarzites are negatively curved structures in which the curvature is due to the introduction of octagonal rings of alternating boron and nitrogen atoms. In particular, three families of Schwarzites are analyzed: P, G and IWP. The Haeckelites on the other hand, are flat layers composed of squares and octagons of BN. It is found that all these BN allotropes are metastable in which the band gap is direct and smaller than the most stable system, h-BN. National Science Foundation (EFRI-1433311).

Tribological properties of epoxy composite coatings reinforced with functionalized C-BN and H-BN nanofillers

NASA Astrophysics Data System (ADS)

Yu, Jingjing; Zhao, Wenjie; Wu, Yinghao; Wang, Deliang; Feng, Ruotao

2018-03-01

A series of epoxy resin (EP) composite coatings reinforced with functionalized cubic boron nitride (FC-BN) and functionalized hexagonal boron nitride (FH-BN) were fabricated successfully on 316L stainless steel by hand lay-up technique. The structure properties were characterized by Fourier transform infrared spectroscopy (FTIR), X-ray photoelectron spectroscopy (XPS) and X-ray diffraction (XRD). The morphologies were characterized by atomic force microscopy (AFM), scanning electron microscopy (SEM) and transmission electron microscopy (TEM). Moreover, UMT-3 tribometer and surface profiler were used to investigate tribological behaviors of as-prepared composite coatings under dry friction and seawater conditions respectively. The results demonstrated that the presence of FC-BN or FH-BN fillers could greatly decrease the friction coefficient (COF) and wear rate of epoxy, in addition, composite coatings possess better tribological properties under seawater condition which was attributed to the lubricating effect of seawater. Moreover, FC-BN endows the composite coatings the highest wear resistance, and FH-BN /EP composite coatings exhibited the best friction reduction performance which is attributed to the self-lubricating performance of lamella structure for FH-BN sheet.

Flexible metal-semiconductor-metal device prototype on wafer-scale thick boron nitride layers grown by MOVPE.

PubMed

Li, Xin; Jordan, Matthew B; Ayari, Taha; Sundaram, Suresh; El Gmili, Youssef; Alam, Saiful; Alam, Muhbub; Patriarche, Gilles; Voss, Paul L; Paul Salvestrini, Jean; Ougazzaden, Abdallah

2017-04-11

Practical boron nitride (BN) detector applications will require uniform materials over large surface area and thick BN layers. To report important progress toward these technological requirements, 1~2.5 µm-thick BN layers were grown on 2-inch sapphire substrates by metal-organic vapor phase epitaxy (MOVPE). The structural and optical properties were carefully characterized and discussed. The thick layers exhibited strong band-edge absorption near 215 nm. A highly oriented two-dimensional h-BN structure was formed at the film/sapphire interface, which permitted an effective exfoliation of the thick BN film onto other adhesive supports. And this structure resulted in a metal-semiconductor-metal (MSM) device prototype fabricated on BN membrane delaminating from the substrate. MSM photodiode prototype showed low dark current of 2 nA under 100 V, and 100 ± 20% photoconductivity yield for deep UV light illumination. These wafer-scale MOVPE-grown thick BN layers present great potential for the development of deep UV photodetection applications, and even for flexible (opto-) electronics in the future.

Catalytically-etched hexagonal boron nitride flakes and their surface activity

NASA Astrophysics Data System (ADS)

Kim, Do-Hyun; Lee, Minwoo; Ye, Bora; Jang, Ho-Kyun; Kim, Gyu Tae; Lee, Dong-Jin; Kim, Eok-Soo; Kim, Hong Dae

2017-04-01

Hexagonal boron nitride (h-BN) is a ceramic compound which is thermally stable up to 1000 °C in air. Due to this, it is a very challenging task to etch h-BN under air atmosphere at low temperature. In this study, we report that h-BN flakes can be easily etched by oxidation at 350 °C under air atmosphere in the presence of transition metal (TM) oxide. After selecting Co, Cu, and Zn elements as TM precursors, we simply oxidized h-BN sheets impregnated with the TM precursors at 350 °C in air. As a result, microscopic analysis revealed that an etched structure was created on the surface of h-BN flakes regardless of catalyst type. And, X-ray diffraction patterns indicated that the air oxidation led to the formation of Co3O4, CuO, and ZnO from each precursor. Thermogravimetric analysis showed a gradual weight loss in the temperature range where the weight of h-BN flakes increased by air oxidation. As a result of etching, pore volume and pore area of h-BN flakes were increased after catalytic oxidation in all cases. In addition, the surface of h-BN flakes became highly active when the h-BN samples were etched by Co3O4 and CuO catalysts. Based on these results, we report that h-BN flakes can be easily oxidized in the presence of a catalyst, resulting in an etched structure in the layered structure.

Effect of different thickness h-BN coatings on interface shear strength of quartz fiber reinforced Sisbnd Osbnd Csbnd N composite

NASA Astrophysics Data System (ADS)

Wang, Shubin; Zheng, Yu

2014-02-01

Hexagonal boron nitride (h-BN) coatings with different thickness were prepared on quartz fibers to improve mechanical properties of quartz fiber reinforced Sisbnd Osbnd Csbnd N composite. Scanning electron microscopy (SEM), push-out test and single edge notched beam (SENB) in three point bending test were employed to study morphology, interface shear strength and fracture toughness of the composite. The results showed that h-BN coatings changed the crack growth direction and weaken the interface shear strength efficiently. When the h-BN coating was 308.2 nm, the interface shear strength was about 5.2 MPa, which was about one-quarter of that of the sample without h-BN coatings. After the heating process for obtaining composite, the h-BN nanometer-sized grains would grow up to micron-sized hexagonal grains. Different thickness h-BN coatings had different structure. When the coatings were relatively thin, the hexagonal grains were single layer structure, and when the coatings were thicker, the hexagonal grains were multiple layer structure. This multiple layer interface phase would consume more power of cracks, thus interface shear strength of the composite decreased steadily with the increasing of h-BN coatings thickness. When the coating thickness was 238.8 nm, KIC reaches the peak value 3.8 MPa m1/2, which was more than two times of that of composites without h-BN coatings.

Novel Crystal Structure C60 Nanowire

NASA Astrophysics Data System (ADS)

Mickelson, William; Aloni, Shaul; Han, Weiqiang; Cumings, John; Zettl, Alex

2003-03-01

We have created insulated C60 nanowire by packing C60 molecules into the interior of insulating boron nitride (BN) nanotubes. For small-diameter BN tubes, the wire consists of a linear chain of C60's. With increasing BN tube inner diameter, novel C60 stacking configurations are obtained (including helical, hollow core, and incommensurate) which are unknown for bulk or thin film forms of C60. C60 in BN nanotubes presents a model system for studying the properties of new dimensionally-constrained "silo" crystal structures.

Pnma-BN: Another Boron Nitride Polymorph with Interesting Physical Properties

PubMed Central

Ma, Zhenyang; Han, Zheng; Liu, Xuhong; Yu, Xinhai; Wang, Dayun; Tian, Yi

2016-01-01

Structural, mechanical, electronic properties, and stability of boron nitride (BN) in Pnma structure were studied using first-principles calculations by Cambridge Serial Total Energy Package (CASTEP) plane-wave code, and the calculations were performed with the local density approximation and generalized gradient approximation in the form of Perdew–Burke–Ernzerhof. This BN, called Pnma-BN, contains four boron atoms and four nitrogen atoms buckled through sp3-hybridized bonds in an orthorhombic symmetry unit cell with Space group of Pnma. Pnma-BN is energetically stable, mechanically stable, and dynamically stable at ambient pressure and high pressure. The calculated Pugh ratio and Poisson’s ratio revealed that Pnma-BN is brittle, and Pnma-BN is found to turn brittle to ductile (~94 GPa) in this pressure range. It shows a higher mechanical anisotropy in Poisson’s ratio, shear modulus, Young’s modulus, and the universal elastic anisotropy index AU. Band structure calculations indicate that Pnma-BN is an insulator with indirect band gap of 7.18 eV. The most extraordinary thing is that the band gap increases first and then decreases with the increase of pressure from 0 to 60 GPa, and from 60 to 100 GPa, the band gap increases first and then decreases again. PMID:28336837

Neurocircuit function in eating disorders.

PubMed

Friederich, Hans-Christoph; Wu, Mudan; Simon, Joe J; Herzog, Wolfgang

2013-07-01

Eating disorders are serious psychosomatic disorders with high morbidity and lifetime mortality. Inadequate response to current therapeutic interventions constitutes a challenging clinical problem. A better understanding of the underlying neurobiological mechanisms could improve psychotherapeutic and drug treatment strategies. A review highlighting the current state of brain imaging in eating disorders related to the anxiety and pathological fear learning model of anorexia nervosa (AN) and the impulsivity model of binge eating in bulimia nervosa (BN). Available neuroimaging studies in patients with acute AN primarily suggest a hyper-responsive emotional and fear network to food, but not necessarily to eating disorder-unrelated, salient stimuli. Furthermore, patients with AN show decreased activation in the ventral fronto-striatal circuits during the performance of a cognitive flexibility task. Results in patients with BN primarily suggest a hypo-responsive reward system to food stimuli, especially to taste reward. Additionally, patients with BN exhibit impaired brain activation in the inhibitory control network during the performance of general response-inhibition tasks. Anxiety and pathological fear learning may lead to conditioned neural stimulus-response patterns to food stimuli and increased cognitive rigidity, which could account for the phobic avoidance of food intake in patients with acute AN. However, further neurobiological studies are required to investigate pathological fear learning in patients with AN. Patients with BN may binge eat to compensate for a hypo-responsive reward system. The impaired brain activation in the inhibitory control network may facilitate the loss of control over food intake in patients with BN. Copyright © 2013 Wiley Periodicals, Inc.

Electronic structure, stability and magnetic properties of small M1-4(M = Fe, Co, Ni) clusters encapsulated inside a (BN)48 cage

NASA Astrophysics Data System (ADS)

Liang, Wenjuan; Jia, Jianfeng; Lv, Jin; Wu, Haishun

2015-02-01

The geometrical structure and magnetic properties of M1-4(M = Fe, Co and Ni) clusters within a (BN)48 cage were calculated at the BPW91/LanL2DZ level. The small M1-4 clusters generally prefer an off-centered position near the hexagonal rings in the (BN)48 cages. The (BN)48 cages can increase the stability of these small magnetic clusters while protecting the magnetic nature of M and M2 clusters.

Stability, Elastic Properties, and Deformation of LiBN2: A Potential High-Energy Material.

PubMed

Zhu, Chunye; Zhu, Wenjun; Yang, Yanqiang

2018-05-15

Searching for high-energy-density materials is of great interest in scientific research and for industrial applications. Using an unbiased structure prediction method and first-principles calculations, we investigated the phase stability of LiBN 2 from 0 to100 GPa. Two new structures with space groups P4̅2 1 m and Pnma were discovered. The theoretical calculations revealed that Pnma LiBN 2 is stable with respect to a mixture of 1 / 3 Li 3 N, BN, and 1 / 3 N 2 above 22 GPa. The electronic band structure revealed that Pnma LiBN 2 has an indirect band gap of 2.3 eV, which shows a nonmetallic feature. The Pnma phase has a high calculated bulk modulus and shear modulus, indicating its incompressible nature. The microscopic mechanism of the structural deformation was demonstrated by ideal tensile shear strength calculations. It is worth mentioning that Pnma LiBN 2 is dynamically stable under ambient conditions. The decomposition of this phase is exothermic, releasing an energy of approximately 1.23 kJ/g at the PBE level. The results provide new thoughts for designing and synthesizing novel high-energy compounds in ternary systems.

Tunable thermal rectification in graphene/hexagonal boron nitride hybrid structures

NASA Astrophysics Data System (ADS)

Chen, Xue-Kun; Hu, Ji-Wen; Wu, Xi-Jun; Jia, Peng; Peng, Zhi-Hua; Chen, Ke-Qiu

2018-02-01

Using non-equilibrium molecular dynamics simulations, we investigate thermal rectification (TR) in graphene/hexagonal boron nitride (h-BN) hybrid structures. Two different structural models, partially substituting graphene into h-BN (CBN) and partially substituting h-BN into graphene (BNC), are considered. It is found that CBN has a significant TR effect while that of BNC is very weak. The observed TR phenomenon can be attributed to the resonance effect between out-of-plane phonons of graphene and h-BN domains in the low-frequency region under negative temperature bias. In addition, the influences of ambient temperature, system size, defect number and substrate interaction are also studied to obtain the optimum conditions for TR. More importantly, the TR ratio could be effectively tuned through chemical and structural diversity. A moderate C/BN ratio and parallel arrangement are found to enhance the TR ratio. Detailed phonon spectra analyses are conducted to understand the thermal transport behavior. This work extends hybrid engineering to 2D materials for achieving TR.

Nano Electronics on Atomically Controlled van der Waals Quantum Heterostructures

DTIC Science & Technology

2015-03-30

for the structural of the atomically sharp interface between hBN and Bi2Te3. Finally, we have developed unprecedentedly clean graphene supercoductor...crystals by MBE method. We also use transmission electron microscopy (TEM) analysis for the structural of the atomically sharp interface between hBN and...by MBE method. We also use transmission electron microscopy (TEM) analysis for the structural of the atomically sharp interface between hBN and Bi2Te3

Bulimia nervosa-nonpurging subtype: closer to the bulimia nervosa-purging subtype or to binge eating disorder?

PubMed

Jordan, Jennifer; McIntosh, Virginia V W; Carter, Janet D; Rowe, Sarah; Taylor, Kathryn; Frampton, Christopher M A; McKenzie, Janice M; Latner, Janet; Joyce, Peter R

2014-04-01

DSM-5 has dropped subtyping of bulimia nervosa (BN), opting to continue inclusion of the somewhat contentious diagnosis of BN-nonpurging subtype (BN-NP) within a broad BN category. Some contend however that BN-NP is more like binge eating disorder (BED) than BN-P. This study examines clinical characteristics, eating disorder symptomatology, and Axis I comorbidity in BN-NP, BN-P, and BED groups to establish whether BN-NP more closely resembles BN-P or BED. Women with BN-P (n = 29), BN-NP (n = 29), and BED (n = 54) were assessed at baseline in an outpatient psychotherapy trial for those with binge eating. Measures included the Structured Clinical Interviews for DSM-IV, Eating Disorder Examination, and Eating Disorder Inventory-2. The BN-NP subtype had BMIs between those with BN-P and BED. Both BN subtypes had higher Restraint and Drive for Thinness scores than BED. Body Dissatisfaction was highest in BN-NP and predicted BN-NP compared to BN-P. Higher Restraint and lower BMI predicted BN-NP relative to BED. BN-NP resembled BED with higher lifetime BMIs; and weight-loss clinic than eating disorder clinic attendances relative to the BN-P subtype. Psychiatric comorbidity was comparable except for higher lifetime cannabis use disorder in the BN-NP than BN-P subtype These results suggest that BN-NP sits between BN-P and BED however the high distress driving inappropriate compensatory behaviors in BN-P requires specialist eating disorder treatment. These results support retaining the BN-NP group within the BN category. Further research is needed to determine whether there are meaningful differences in outcome over follow-up. Copyright © 2013 Wiley Periodicals, Inc.

Synthesis and processing of nanostructured BN and BN/Ti composites

NASA Astrophysics Data System (ADS)

Horvath, Robert Steven

Superhard materials, such as cubic-BN, are widely used in machine tools, grinding wheels, and abrasives. Low density combined with high hardness makes c-BN and its composites attractive candidate materials for personnel and vehicular armor. However, improvements in toughness, and ballistic-impact performance, are needed to meet anticipated performance requirements. To achieve such improvements, we have targeted for development nanostructured c-BN, and its composites with Ti. Current research utilizes an experimental high pressure/high temperature (HPHT) method to produce these materials on a laboratory scale. Results from this work should transfer well into the industrial arena, utilizing high-tonnage presses used in the production of synthetic diamond and c-BN. Progress has been made in: (1) HPHT synthesis of cBN powder using Mg as catalyst; (2) HPHT consolidation of cBN powder to produce nanostructured cBN; (3) reactive-HPHT consolidation of mixed cBN/Ti powder to produce nanostructured Ti- or TiB2/TiN-bonded cBN; and (4) reactive-HPHT consolidation of mixed hBN/Ti powder to produce nanostructured Ti-bonded TiB2/TiN or TiB2/TiN. Even so, much remains to be done to lay a firm scientific foundation to enable the reproducible fabrication of large-area panels for armor applications. To this end, Rutgers has formed a partnership with a major producer of hard and superhard materials. The ability to produce hard and superhard nanostructured composites by reacting cBN or hBN with Ti under high pressure also enables multi-layered structures to be developed. Such structures may be designed to satisfy impedance-mismatch requirements for high performance armor, and possibly provide a multi-hit capability. A demonstration has been made of reactive-HPHT processing of multi-layered composites, consisting of alternating layers of superhard Ti-bonded cBN and tough Ti. It is noteworthy that the pressure requirements for processing Ti-bonded cBN, Ti-bonded TiB2/TiN, and their corresponding multi-layered structures are in the 0.1-1.0 GPa range, well within the capabilities of today's hot-pressing technologies; thus scaling this new reactive-HPHT processing technology seems assured. Future research will focus on establishing mechanisms and kinetics of the various phase transformations observed during reactive-HPHT processing, with the objective of being able to optimize processing parameters to generate nanostructured cBN-based and TiB2/TiN-based composites that display superior mechanical properties, particularly under high-strain-rate conditions.

Electrical transport and capacitance characteristics of metal-insulator-metal structures using hexagonal and cubic boron nitride films as dielectrics

NASA Astrophysics Data System (ADS)

Teii, Kungen; Kawamoto, Shinsuke; Fukui, Shingo; Matsumoto, Seiichiro

2018-04-01

Metal-insulator-metal capacitor structures using thick hexagonal and cubic boron nitride (hBN and cBN) films as dielectrics are produced by plasma jet-enhanced chemical vapor deposition, and their electrical transport and capacitance characteristics are studied in a temperature range of 298 to 473 K. The resistivity of the cBN film is of the order of 107 Ω cm at 298 K, which is lower than that of the hBN film by two orders of magnitude, while it becomes the same order as the hBN film above ˜423 K. The dominant current transport mechanism at high fields (≥1 × 104 V cm-1) is described by the Frenkel-Poole emission and thermionic emission models for the hBN and cBN films, respectively. The capacitance of the hBN film remains stable for a change in alternating-current frequency and temperature, while that of the cBN film has variations of at most 18%. The dissipation factor as a measure of energy loss is satisfactorily low (≤5%) for both films. The origin of leakage current and capacitance variation is attributed to a high defect density in the film and a transition interlayer between the substrate and the film, respectively. This suggests that cBN films with higher crystallinity, stoichiometry, and phase purity are potentially applicable for dielectrics like hBN films.

Improved Performance of h-BN Encapsulated Double Gate Graphene Nanomesh Field Effect Transistor for Short Channel Length

NASA Astrophysics Data System (ADS)

Tiwari, Durgesh Laxman; Sivasankaran, K.

This paper presents improved performance of Double Gate Graphene Nanomesh Field Effect Transistor (DG-GNMFET) with h-BN as substrate and gate oxide material. The DC characteristics of 0.95μm and 5nm channel length devices are studied for SiO2 and h-BN substrate and oxide material. For analyzing the ballistic behavior of electron for 5nm channel length, von Neumann boundary condition is considered near source and drain contact region. The simulated results show improved saturation current for h-BN encapsulated structure with two times higher on current value (0.375 for SiO2 and 0.621 for h-BN) as compared to SiO2 encapsulated structure. The obtained result shows h-BN to be a better substrate and oxide material for graphene electronics with improved device characteristics.

Influence of BN fiber coatings on the interfacial structure of sapphire fiber reinforced NiAl composites

NASA Astrophysics Data System (ADS)

Reichert, K.; Wen, K.; Cremer, R.; Hu, W.; Neuschütz, D.; Gottstein, G.

2001-07-01

A new concept for a tailored fiber-matrix interface for sapphire fiber reinforced NiAl matrix composites is proposed, consisting of an initial hexagonal boron nitride (hBN) fiber coating. For this, single crystal Al 2O 3 fibers were coated with hBN by chemical vapor deposition (CVD). Following a comprehensive characterization of the CVD coating as to composition and structure by means of X-ray photoelectron spectroscopy (XPS) and grazing incidence X-ray diffraction (GIXRD), the fiber reinforced NiAl matrix composites were fabricated by diffusion bonding at 1400°C. The interfaces NiAl/BN and BN/Al 2O 3 were analyzed by scanning electron microscopy (SEM), analytical transmission electron microscopy (TEM), and selected area diffraction (SAD). An interfacial reaction between NiAl and hBN to form AlN was revealed using these analytical techniques.

Electronic structure, stability and magnetic properties of small M1-2Cr (M = Fe, Co, and Ni) alloy encapsulated inside a (BN)48 cage

NASA Astrophysics Data System (ADS)

Liang, Wenjuan; Jia, Jianfeng; Lv, Jin; Wu, Haishun

2015-09-01

The geometrical structure and magnetic properties of M1-2Cr (M = Fe, Co, and Ni) alloy clusters inside a (BN)48 cage were calculated at the BPW91/LANL2DZ level of theory. The doping with Cr significantly changed the magnetic properties of the transition-metal clusters. When M1-2Cr alloys were placed inside a (BN)48 cage, the alloy clusters interacted strongly with the cage, and the M1-2Cr@(BN)48 clusters showed high stability. Moreover, Cr-doped magnetic metal clusters preferably occupied positions off-center and near the hexagonal rings of (BN)48 cages. Thus, the (BN)48 cages can be used to increase the stability of M1-2Cr alloys, and retain their magnetic nature, except for CoCr and Ni2Cr clusters.

Electronic structure and STM images simulation of defects on hBN/ black-phosphorene heterostructures: A theoretical study

NASA Astrophysics Data System (ADS)

Ospina, D. A.; Cisternas, E.; Duque, C. A.; Correa, J. D.

2018-03-01

By first principles calculations which include van der Waals interactions, we studied the electronic structure of hexagonal boron-nitride/black-phosphorene heterostructures (hBN/BP). In particular the role of several kind of defects on the electronic properties of black-phosphorene monolayer and hBN/BP heterostructure was analyzed. The defects under consideration were single and double vacancies, as well Stone-Wale type defects, all of them present in the phosphorene layer. In this way, we found that the electronic structure of the hBN/BP is modified according the type of defect that is introduced. As a remarkable feature, our results show occupied states at the Fermi Level introduced by a single vacancy in the energy gap of the hBN/BP heterostructure. Additionally, we performed simulations of scanning tunneling microscopy images. These simulations show that is possible to discriminate the kind of defect even when the black-phosphorene monolayer is part of the heterostructure hBN/BP. Our results may help to discriminate among several kind of defects during experimental characterization of these novel materials.

Boron nitride nanotubes and nanosheets.

PubMed

Golberg, Dmitri; Bando, Yoshio; Huang, Yang; Terao, Takeshi; Mitome, Masanori; Tang, Chengchun; Zhi, Chunyi

2010-06-22

Hexagonal boron nitride (h-BN) is a layered material with a graphite-like structure in which planar networks of BN hexagons are regularly stacked. As the structural analogue of a carbon nanotube (CNT), a BN nanotube (BNNT) was first predicted in 1994; since then, it has become one of the most intriguing non-carbon nanotubes. Compared with metallic or semiconducting CNTs, a BNNT is an electrical insulator with a band gap of ca. 5 eV, basically independent of tube geometry. In addition, BNNTs possess a high chemical stability, excellent mechanical properties, and high thermal conductivity. The same advantages are likely applicable to a graphene analogue-a monatomic layer of a hexagonal BN. Such unique properties make BN nanotubes and nanosheets a promising nanomaterial in a variety of potential fields such as optoelectronic nanodevices, functional composites, hydrogen accumulators, electrically insulating substrates perfectly matching the CNT, and graphene lattices. This review gives an introduction to the rich BN nanotube/nanosheet field, including the latest achievements in the synthesis, structural analyses, and property evaluations, and presents the purpose and significance of this direction in the light of the general nanotube/nanosheet developments.

Pulsed laser deposition of single layer, hexagonal boron nitride (white graphene, h-BN) on fiber-oriented Ag(111)/SrTiO3(001)

NASA Astrophysics Data System (ADS)

Velázquez, Daniel; Seibert, Rachel; Man, Hamdi; Spentzouris, Linda; Terry, Jeff

2016-03-01

We report on the growth of 1-10 ML films of hexagonal boron nitride (h-BN), also known as white graphene, on fiber-oriented Ag buffer films on SrTiO3(001) by pulsed laser deposition. The Ag buffer films of 40 nm thickness were used as substitutes for expensive single crystal metallic substrates. In-situ, reflection high-energy electron diffraction was used to monitor the surface structure of the Ag films and to observe the formation of the characteristic h-BN diffraction pattern. Further evidence of the growth of h-BN was provided by attenuated total reflectance spectroscopy, which showed the characteristic h-BN peaks at ˜780 cm-1 and 1367.4 cm-1. Ex-situ photoelectron spectroscopy showed that the surface of the h-BN films is stoichiometric. The physical structure of the films was confirmed by scanning electron microscopy. The h-BN films grew as large, sub-millimeter sheets with nano- and micro-sheets scattered on the surface. The h-BN sheets can be exfoliated by the micromechanical adhesive tape method. Spectral analysis was performed by energy dispersive spectroscopy in order to identify the h-BN sheets after exfoliation. The use of thin film Ag allows for reduced use of Ag and makes it possible to adjust the surface morphology of the thin film prior to h-BN growth.

Hazard Screening Methods for Nanomaterials: A Comparative Study

PubMed Central

Murphy, Finbarr; Mullins, Martin; Furxhi, Irini; Costa, Anna L.; Simeone, Felice C.

2018-01-01

Hazard identification is the key step in risk assessment and management of manufactured nanomaterials (NM). However, the rapid commercialisation of nano-enabled products continues to out-pace the development of a prudent risk management mechanism that is widely accepted by the scientific community and enforced by regulators. However, a growing body of academic literature is developing promising quantitative methods. Two approaches have gained significant currency. Bayesian networks (BN) are a probabilistic, machine learning approach while the weight of evidence (WoE) statistical framework is based on expert elicitation. This comparative study investigates the efficacy of quantitative WoE and Bayesian methodologies in ranking the potential hazard of metal and metal-oxide NMs—TiO2, Ag, and ZnO. This research finds that hazard ranking is consistent for both risk assessment approaches. The BN and WoE models both utilize physico-chemical, toxicological, and study type data to infer the hazard potential. The BN exhibits more stability when the models are perturbed with new data. The BN has the significant advantage of self-learning with new data; however, this assumes all input data is equally valid. This research finds that a combination of WoE that would rank input data along with the BN is the optimal hazard assessment framework. PMID:29495342

Surface functionalization of hexagonal boron nitride and its effect on the structure and performance of composites

NASA Astrophysics Data System (ADS)

Jin, Wenqin; Zhang, Wei; Gao, Yuwen; Liang, Guozheng; Gu, Aijuan; Yuan, Li

2013-04-01

A new organized hexagonal boron nitride (OhBN) with significantly increased amount of amine groups was synthesized, and characterized by Fourier Transform Infrared (FTIR), X-ray Photoelectron Spectroscopy (XPS), Thermogravimetric (TG) analysis, UV-vis Transmittance Spectra, Transmission Electron Microscope (TEM) and the potentiometric titration. The content of amine groups for OhBN is about 5 times of that for original hexagonal boron nitride (hBN). Based on the preparation of OhBN, new composites consisting of OhBN and bismaleimide (BD) resin were developed, which show greatly improved integrated performance (including dynamic mechanical, dielectric and thermal properties) compared with BD resin and the hBN/BD composites. In the case of the OhBN/BD composite with 15 wt% OhBN, its storage modulus, dielectric loss, thermal conductivity and coefficient of thermal expansion are about 1.2, 0.56, 1.11 and 0.92 times of the corresponding values of hBN/BD composite, respectively; moreover, the glass transition temperature of the former is 15 °C higher than that of the latter. These interesting results suggest that the integrated performance of the composites is closely related to the surface nature of the fillers because the change in the surface nature not only varies the chemical structure, free volume and crosslinking density of the composite, but also determines the interfacial nature between inorganic fillers and the resin matrix. This investigation demonstrates that the method proposed herein provides a new approach to prepare organized inorganic fillers as well as corresponding composites with controlled structure and expected performances for cutting-edge industries.

Neuropsychological function in patients with anorexia nervosa or bulimia nervosa.

PubMed

Weider, Siri; Indredavik, Marit Saebø; Lydersen, Stian; Hestad, Knut

2015-05-01

This study explored the neuropsychological performance of patients diagnosed with anorexia nervosa (AN) or bulimia nervosa (BN) compared with healthy controls (HCs). An additional aim was to investigate the effect of several possible mediators on the association between eating disorders (EDs) and cognitive function. Forty patients with AN, 39 patients with BN, and 40 HCs who were comparable in age and education were consecutively recruited to complete a standardized neuropsychological test battery covering the following cognitive domains: verbal learning and memory, visual learning and memory, speed of information processing, visuospatial ability, working memory, executive function, verbal fluency, attention/vigilance, and motor function. The AN group scored significantly below the HCs on eight of the nine measured cognitive domains. The BN group also showed inferior performance on six cognitive domains. After adjusting for possible mediators, the nadir body mass index (lowest lifetime BMI) and depressive symptoms explained all findings in the BN group. Although this adjustment reduced the difference between the AN and HC groups, the AN group still performed worse than the HCs regarding verbal learning and memory, visual learning and memory, visuospatial ability, working memory, and executive functioning. Patients with EDs scored below the HCs on several cognitive function measures, this difference being most pronounced for the AN group. The nadir BMI and depressive symptoms had strong mediating effects. Longitudinal studies are needed to identify the importance of weight restoration and treatment of depressive symptoms in the prevention of a possible cognitive decline. © 2014 Wiley Periodicals, Inc.

Suppression of Lateral Diffusion and Surface Leakage Currents in nBn Photodetectors Using an Inverted Design

NASA Astrophysics Data System (ADS)

Du, X.; Savich, G. R.; Marozas, B. T.; Wicks, G. W.

2018-02-01

Surface leakage and lateral diffusion currents in InAs-based nBn photodetectors have been investigated. Devices fabricated using a shallow etch processing scheme that etches through the top contact and stops at the barrier exhibited large lateral diffusion current but undetectably low surface leakage. Such large lateral diffusion current significantly increased the dark current, especially in small devices, and causes pixel-to-pixel crosstalk in detector arrays. To eliminate the lateral diffusion current, two different approaches were examined. The conventional solution utilized a deep etch process, which etches through the top contact, barrier, and absorber. This deep etch processing scheme eliminated lateral diffusion, but introduced high surface current along the device mesa sidewalls, increasing the dark current. High device failure rate was also observed in deep-etched nBn structures. An alternative approach to limit lateral diffusion used an inverted nBn structure that has its absorber grown above the barrier. Like the shallow etch process on conventional nBn structures, the inverted nBn devices were fabricated with a processing scheme that only etches the top layer (the absorber, in this case) but avoids etching through the barrier. The results show that inverted nBn devices have the advantage of eliminating the lateral diffusion current without introducing elevated surface current.

Abnormal fronto-striatal activation as a marker of threshold and subthreshold Bulimia Nervosa.

PubMed

Cyr, Marilyn; Yang, Xiao; Horga, Guillermo; Marsh, Rachel

2018-04-01

This study aimed to determine whether functional disturbances in fronto-striatal control circuits characterize adolescents with Bulimia Nervosa (BN) spectrum eating disorders regardless of clinical severity. FMRI was used to assess conflict-related brain activations during performance of a Simon task in two samples of adolescents with BN symptoms compared with healthy adolescents. The BN samples differed in the severity of their clinical presentation, illness duration and age. Multi-voxel pattern analyses (MVPAs) based on machine learning were used to determine whether patterns of fronto-striatal activation characterized adolescents with BN spectrum disorders regardless of clinical severity, and whether accurate classification of less symptomatic adolescents (subthreshold BN; SBN) could be achieved based on patterns of activation in adolescents who met DSM5 criteria for BN. MVPA classification analyses revealed that both BN and SBN adolescents could be accurately discriminated from healthy adolescents based on fronto-striatal activation. Notably, the patterns detected in more severely ill BN compared with healthy adolescents accurately discriminated less symptomatic SBN from healthy adolescents. Deficient activation of fronto-striatal circuits can characterize BN early in its course, when clinical presentations are less severe, perhaps pointing to circuit-based disturbances as useful biomarker or risk factor for the disorder, and a tool for understanding its developmental trajectory, as well as the development of early interventions. © 2018 Wiley Periodicals, Inc.

Hydrogenation and hydrogen intercalation of hexagonal boron nitride on Ni(1 1 1): reactivity and electronic structure

NASA Astrophysics Data System (ADS)

Späth, F.; Gebhardt, J.; Düll, F.; Bauer, U.; Bachmann, P.; Gleichweit, C.; Görling, A.; Steinrück, H.-P.; Papp, C.

2017-09-01

We investigate the reactivity of hexagonal boron nitride (h-BN) on a Ni(1 1 1) single crystal towards atomic hydrogen over a wide exposure range. Near edge x-ray absorption fine structure and x-ray photoelectron spectroscopy (XPS) show that for low hydrogen exposures hydrogenation of the h-BN sheet is found. In contrast, intercalation of hydrogen between h-BN and the Ni(1 1 1) substrate occurs for high exposures. For intermediate regimes, a mixture of intercalation and hydrogenation is observed. From temperature-programmed desorption and temperature-programmed XPS experiments, we conclude that the hydrogen covalently bound to h-BN is rather stable with a desorption temperature of 600 K, while intercalated hydrogen is desorbing already at 390 K. Further insight into the structural arrangements and the thermodynamics of the system is obtained by comparing our experimental results with extensive density-functional theory calculations. Together with ultraviolet photoelectron spectroscopy measurements, the calculations provide detailed insight into the influence of hydrogenation on the electronic structure of h-BN.

Extended Tersoff potential for boron nitride: Energetics and elastic properties of pristine and defective h -BN

NASA Astrophysics Data System (ADS)

Los, J. H.; Kroes, J. M. H.; Albe, K.; Gordillo, R. M.; Katsnelson, M. I.; Fasolino, A.

2017-11-01

We present an extended Tersoff potential for boron nitride (BN-ExTeP) for application in large scale atomistic simulations. BN-ExTeP accurately describes the main low energy B, N, and BN structures and yields quantitatively correct trends in the bonding as a function of coordination. The proposed extension of the bond order, added to improve the dependence of bonding on the chemical environment, leads to an accurate description of point defects in hexagonal BN (h -BN) and cubic BN (c -BN). We have implemented this potential in the molecular dynamics LAMMPS code and used it to determine some basic properties of pristine 2D h -BN and the elastic properties of defective h -BN as a function of defect density at zero temperature. Our results show that there is a strong correlation between the size of the static corrugation induced by the defects and the weakening of the in-plane elastic moduli.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Velázquez, Daniel; Seibert, Rachel; Spentzouris, Linda

We report on the growth of 1–10 ML films of hexagonal boron nitride (h-BN), also known as white graphene, on fiber-oriented Ag buffer films on SrTiO{sub 3}(001) by pulsed laser deposition. The Ag buffer films of 40 nm thickness were used as substitutes for expensive single crystal metallic substrates. In-situ, reflection high-energy electron diffraction was used to monitor the surface structure of the Ag films and to observe the formation of the characteristic h-BN diffraction pattern. Further evidence of the growth of h-BN was provided by attenuated total reflectance spectroscopy, which showed the characteristic h-BN peaks at ∼780 cm{sup −1} and 1367.4 cm{supmore » −1}. Ex-situ photoelectron spectroscopy showed that the surface of the h-BN films is stoichiometric. The physical structure of the films was confirmed by scanning electron microscopy. The h-BN films grew as large, sub-millimeter sheets with nano- and micro-sheets scattered on the surface. The h-BN sheets can be exfoliated by the micromechanical adhesive tape method. Spectral analysis was performed by energy dispersive spectroscopy in order to identify the h-BN sheets after exfoliation. The use of thin film Ag allows for reduced use of Ag and makes it possible to adjust the surface morphology of the thin film prior to h-BN growth.« less

High hardness BaCb-(BxOy/BN) composites with 3D mesh-like fine grain-boundary structure by reactive spark plasma sintering.

PubMed

Vasylkiv, Oleg; Borodianska, Hanna; Badica, Petre; Grasso, Salvatore; Sakka, Yoshio; Tok, Alfred; Su, Liap Tat; Bosman, Michael; Ma, Jan

2012-02-01

Boron carbide B4C powders were subject to reactive spark plasma sintering (also known as field assisted sintering, pulsed current sintering or plasma assisted sintering) under nitrogen atmosphere. For an optimum hexagonal BN (h-BN) content estimated from X-ray diffraction measurements at approximately 0.4 wt%, the as-prepared BaCb-(BxOy/BN) ceramic shows values of Berkovich and Vickers hardness of 56.7 +/- 3.1 GPa and 39.3 +/- 7.6 GPa, respectively. These values are higher than for the vacuum SPS processed B4C pristine sample and the h-BN -mechanically-added samples. XRD and electronic microscopy data suggest that in the samples produced by reactive SPS in N2 atmosphere, and containing an estimated amount of 0.3-1.5% h-BN, the crystallite size of the boron carbide grains is decreasing with the increasing amount of N2, while for the newly formed lamellar h-BN the crystallite size is almost constant (approximately 30-50 nm). BN is located at the grain boundaries between the boron carbide grains and it is wrapped and intercalated by a thin layer of boron oxide. BxOy/BN forms a fine and continuous 3D mesh-like structure that is a possible reason for good mechanical properties.

Spectroscopic and structural studies of the first complex formed between salinomycin and organic amine

NASA Astrophysics Data System (ADS)

Antoszczak, Michał; Janczak, Jan; Brzezinski, Bogumił; Huczyński, Adam

2017-02-01

For the first time, the crystalline complex of salinomycin with benzylamine was obtained and its molecular structure was studied using single crystal X-ray diffraction, FT-IR, 1H NMR, 13C NMR, 2D NMR and ESI MS methods. These studies provided evidence that the proton from the carboxylic group of salinomycin (SAL) is transferred to the amine group of benzylamine (BnA) forming the host-guest complex (SAL-BnA). It was shown that the SAL-BnA complex both in solid state and in chloroform solution is stabilized by the intramolecular O-H⋯O hydrogen bonds and also by the intermolecular hydrogen bonding interactions of the carboxylate, ketone and/or hydroxyl groups of SAL with water molecules present in the investigated system. The solvated acetonitrile molecules are additionally located in the voids between the SAL-BnA complex molecules in the crystal structure, while water molecules involved in the dihydrated crystalline SAL-BnA complex partially move into the solvent upon dissolution in chloroform.

Phase stability limit of c-BN under hydrostatic and non-hydrostatic pressure conditions

NASA Astrophysics Data System (ADS)

Xiao, Jianwei; Du, Jinglian; Wen, Bin; Melnik, Roderick; Kawazoe, Yoshiyuki; Zhang, Xiangyi

2014-04-01

Phase stability limit of cubic boron nitride (c-BN) has been investigated by the crystal structure search technique. It indicated that this limit is ˜1000 GPa at hydrostatic pressure condition. Above this pressure, c-BN turns into a metastable phase with respect to rocksalt type boron nitride (rs-BN). However, rs-BN cannot be retained at 0 GPa owing to its instability at pressure below 250 GPa. For non-hydrostatic pressure conditions, the phase stability limit of c-BN is substantially lower than that under hydrostatic pressure conditions and it is also dramatically different for other pressure mode.

Phase stability limit of c-BN under hydrostatic and non-hydrostatic pressure conditions

DOE Office of Scientific and Technical Information (OSTI.GOV)

Xiao, Jianwei; Du, Jinglian; Wen, Bin, E-mail: wenbin@ysu.edu.cn

2014-04-28

Phase stability limit of cubic boron nitride (c-BN) has been investigated by the crystal structure search technique. It indicated that this limit is ∼1000 GPa at hydrostatic pressure condition. Above this pressure, c-BN turns into a metastable phase with respect to rocksalt type boron nitride (rs-BN). However, rs-BN cannot be retained at 0 GPa owing to its instability at pressure below 250 GPa. For non-hydrostatic pressure conditions, the phase stability limit of c-BN is substantially lower than that under hydrostatic pressure conditions and it is also dramatically different for other pressure mode.

Activated boron nitride as an effective adsorbent for metal ions and organic pollutants

PubMed Central

Li, Jie; Xiao, Xing; Xu, Xuewen; Lin, Jing; Huang, Yang; Xue, Yanming; Jin, Peng; Zou, Jin; Tang, Chengchun

2013-01-01

Novel activated boron nitride (BN) as an effective adsorbent for pollutants in water and air has been reported in the present work. The activated BN was synthesized by a simple structure-directed method that enabled us to control the surface area, pore volume, crystal defects and surface groups. The obtained BN exhibits an super high surface area of 2078 m2/g, a large pore volume of 1.66 cm3/g and a special multimodal microporous/mesoporous structure located at ~ 1.3, ~ 2.7, and ~ 3.9 nm, respectively. More importantly, the novel activated BN exhibits an excellent adsorption performance for various metal ions (Cr3+, Co2+, Ni2+, Ce3+, Pb2+) and organic pollutants (tetracycline, methyl orange and congo red) in water, as well as volatile organic compounds (benzene) in air. The excellent reusability of the activated BN has also been confirmed. All the features render the activated BN a promising material suitable for environmental remediation. PMID:24220570

Graphene/h-BN/GaAs sandwich diode as solar cell and photodetector.

PubMed

Li, Xiaoqiang; Lin, Shisheng; Lin, Xing; Xu, Zhijuan; Wang, Peng; Zhang, Shengjiao; Zhong, Huikai; Xu, Wenli; Wu, Zhiqian; Fang, Wei

2016-01-11

In graphene/semiconductor heterojunction, the statistic charge transfer between graphene and semiconductor leads to decreased junction barrier height and limits the Fermi level tuning effect in graphene, which greatly affects the final performance of the device. In this work, we have designed a sandwich diode for solar cells and photodetectors through inserting 2D hexagonal boron nitride (h-BN) into graphene/GaAs heterostructure to suppress the static charge transfer. The barrier height of graphene/GaAs heterojunction can be increased from 0.88 eV to 1.02 eV by inserting h-BN. Based on the enhanced Fermi level tuning effect with interface h-BN, through adopting photo-induced doping into the device, power conversion efficiency (PCE) of 10.18% has been achieved for graphene/h-BN/GaAs compared with 8.63% of graphene/GaAs structure. The performance of graphene/h-BN/GaAs based photodetector is also improved with on/off ratio increased by one magnitude compared with graphene/GaAs structure.

Anisotropic Effective Mass, Optical Property, and Enhanced Band Gap in BN/Phosphorene/BN Heterostructures.

PubMed

Hu, Tao; Hong, Jisang

2015-10-28

Phosphorene is receiving great research interests because of its peculiar physical properties. Nonetheless, the phosphorus has a trouble of degradation due to oxidation. Hereby, we propose that the electrical and optical anisotropic properties can be preserved by encapsulating into hexagonal boron nitride (h-BN). We found that the h-BN contributed to enhancing the band gap of the phosphorene layer. Comparing the band gap of the pristine phosphorene layer, the band gap of the phosphorene/BN(1ML) system was enhanced by 0.15 eV. It was further enhanced by 0.31 eV in the BN(1ML)/phosphorene/BN(1ML) trilayer structure. However, the band gap was not further enhanced when we increased the thickness of the h-BN layers even up to 4 MLs. Interestingly, the anisotropic effective mass and optical property were still preserved in BN/phosphorene/BN heterostructures. Overall, we predict that the capping of phosphorene by the h-BN layers can be an excellent solution to protect the intrinsic properties of the phosphorene.

Structure and luminescence properties of 10-BN sheets

NASA Astrophysics Data System (ADS)

Han, Wei-Qiang; Liu, Lijia; Sham, T. K.; Liu, Zhenxian

2012-10-01

Isotopic 10BN sheets were first prepared using graphene sheets as templates to react with 10B2O3. The edge-areas of BN sheets have much higher oxygen-doping ratios compared to other areas. The emission peak of X-ray excited optical luminescence spectra of the 10BN-sheets is broader and red-shifted because of the isotopic effect. A broad violet-blue emission at a wavelength centered at ~400 nm is assigned to the defect emission due to oxygen-doping and defects in the BN network.

Facile synthesis, microstructure and photophysical properties of core-shell nanostructured (SiCN)/BN nanocomposites

PubMed Central

Zhang, Qian; Jia, Dechang; Yang, Zhihua; Cai, Delong; Laine, Richard M.; Li, Qian; Zhou, Yu

2017-01-01

Increasing structural complexity at nanoscale can permit superior control over photophysical properties in the precursor-derived semiconductors. We demonstrate here the synthesis of silicon carbonitride (SiCN)/boron nitride (BN) nanocomposites via a polymer precursor route wherein the cobalt polyamine complexes used as the catalyst, exhibiting novel composite structures and photophysical properties. High Resolution Transmission Electron Microscopy (HRTEM) analysis shows that the diameters of SiCN−BN core−shell nanocomposites and BN shells are 50‒400 nm and 5‒25 nm, respectively. BN nanosheets (BNNSs) are also observed with an average sheet size of 5‒15 nm. The photophysical properties of these nanocomposites are characterized using the UV-Vis and photoluminescence (PL) analyses. The as-produced composites have emission behavior including an emission lifetime of 2.5 ns (±20 ps) longer observed in BN doped SiCN than that seen for SiC nanoparticles. Our results suggest that the SiCN/BN nanocomposites act as semiconductor displaying superior width photoluminescence at wavelengths spanning the visible to near-infrared (NIR) spectral range (400‒700 nm), owing to the heterojunction of the interface between the SiC(N) nanowire core and the BN nanosheet shell. PMID:28084300

Synergic nitrogen source route to inorganic fullerene-like boron nitride with vessel, hollow sphere, onion, and peanut nanostructures.

PubMed

Xu, Fen; Xie, Yi; Zhang, Xu; Zhang, Shuyuan; Liu, Xianming; Tian, Xiaobo

2004-01-26

In this paper we describe the large-scale synthesis of inorganic fullerene-like (IF-like) hexagonal boron nitride with vessel, hollow sphere, peanut, and onion structures by reacting BBr(3) with the synergic nitrogen sources NaNH(2) and NH(4)Cl at 400-450 degrees C for 6-12 h. The composition of products could be confirmed to be pure boron nitride with hexagonal structures by the XRD patterns and FT-IR, XPS, and EDXA spectra. The representative HRTEM images clearly reveal the layerlike features of the products. Here, the peanut-like structure of the IF-like BN is reported for the first time, and added to the list as one kind of new morphology of BN nanomaterials. The similarity in the structure between h-BN and graphite is responsible for the formation of IF-like BN with nanostructures of vessels, hollow spheres, peanuts, and onions.

Boron doped GaN and InN: Potential candidates for spintronics

NASA Astrophysics Data System (ADS)

Fan, S. W.; Huang, X. N.; Yao, K. L.

2017-02-01

The full potential linearized augmented plane wave method together with the Tran-Blaha modified Becke-Johnson potential is utilized to investigate the electronic structures and magnetism for boron doped GaN and InN. Calculations show the boron substituting nitrogen (BN defects) could induce the GaN and InN to be half-metallic ferromagnets. The magnetic moments mainly come from the BN defects, and each BN defect would produce the 2.00 μB total magnetic moment. The electronic structures indicate the carriers-mediated double exchange interaction plays a crucial role in forming the ferromagnetism. Positive chemical pair interactions imply the BN defects would form the homogeneous distribution in GaN and InN matrix. Moderate formation energies suggest that GaN and InN with BN defects could be fabricated experimentally.

Structural and electronic properties of multilayer graphene on monolayer hexagonal boron nitride/nickel (111) interface system: A van der Waals density functional study

NASA Astrophysics Data System (ADS)

Yelgel, Celal

2016-02-01

The structural and electronic properties of multilayer graphene adsorbed on monolayer hexagonal boron nitride (h-BN)/Ni(111) interface system are investigated using the density functional theory with a recently developed non-local van der Waals density functional (rvv10). The most energetically favourable configuration for a monolayer h-BN/Ni(111) interface is found to be N atom atop the Ni atoms and B atom in fcc site with the interlayer distance of 2.04 Å and adsorption energy of 302 meV/BN. Our results show that increasing graphene layers on a monolayer h-BN/Ni(111) interface leads to a weakening of the interfacial interaction between the monolayer h-BN and Ni(111) surface. The adsorption energy of graphene layers on the h-BN/Ni(111) interface is found to be in the range of the 50-120 meV/C atom as the vertical distance from h-BN to the bottommost graphene layers decreases. With the adsorption of a multilayer graphene on the monolayer h-BN/Ni(111) interface system, the band gap of 0.12 eV and 0.25 eV opening in monolayer graphene and bilayer graphene near the K point is found with an upward shifting of the Fermi level. However, a stacking-sensitive band gap is opened in trilayer graphene. We obtain the band gap of 0.35 eV close to the K point with forming a Mexican hat band structure for ABC-stacked trilayer graphene.

Logical Differential Prediction Bayes Net, improving breast cancer diagnosis for older women.

PubMed

Nassif, Houssam; Wu, Yirong; Page, David; Burnside, Elizabeth

2012-01-01

Overdiagnosis is a phenomenon in which screening identities cancer which may not go on to cause symptoms or death. Women over 65 who develop breast cancer bear the heaviest burden of overdiagnosis. This work introduces novel machine learning algorithms to improve diagnostic accuracy of breast cancer in aging populations. At the same time, we aim at minimizing unnecessary invasive procedures (thus decreasing false positives) and concomitantly addressing overdiagnosis. We develop a novel algorithm. Logical Differential Prediction Bayes Net (LDP-BN), that calculates the risk of breast disease based on mammography findings. LDP-BN uses Inductive Logic Programming (ILP) to learn relational rules, selects older-specific differentially predictive rules, and incorporates them into a Bayes Net, significantly improving its performance. In addition, LDP-BN offers valuable insight into the classification process, revealing novel older-specific rules that link mass presence to invasive, and calcification presence and lack of detectable mass to DCIS.

Image analysis of representative food structures: application of the bootstrap method.

PubMed

Ramírez, Cristian; Germain, Juan C; Aguilera, José M

2009-08-01

Images (for example, photomicrographs) are routinely used as qualitative evidence of the microstructure of foods. In quantitative image analysis it is important to estimate the area (or volume) to be sampled, the field of view, and the resolution. The bootstrap method is proposed to estimate the size of the sampling area as a function of the coefficient of variation (CV(Bn)) and standard error (SE(Bn)) of the bootstrap taking sub-areas of different sizes. The bootstrap method was applied to simulated and real structures (apple tissue). For simulated structures, 10 computer-generated images were constructed containing 225 black circles (elements) and different coefficient of variation (CV(image)). For apple tissue, 8 images of apple tissue containing cellular cavities with different CV(image) were analyzed. Results confirmed that for simulated and real structures, increasing the size of the sampling area decreased the CV(Bn) and SE(Bn). Furthermore, there was a linear relationship between the CV(image) and CV(Bn) (.) For example, to obtain a CV(Bn) = 0.10 in an image with CV(image) = 0.60, a sampling area of 400 x 400 pixels (11% of whole image) was required, whereas if CV(image) = 1.46, a sampling area of 1000 x 100 pixels (69% of whole image) became necessary. This suggests that a large-size dispersion of element sizes in an image requires increasingly larger sampling areas or a larger number of images.

Common quandaries and their practical solutions in Bayesian network modeling

Treesearch

Bruce G. Marcot

2017-01-01

Use and popularity of Bayesian network (BN) modeling has greatly expanded in recent years, but many common problems remain. Here, I summarize key problems in BN model construction and interpretation,along with suggested practical solutions. Problems in BN model construction include parameterizing probability values, variable definition, complex network structures,...

Wafer-scale controlled exfoliation of metal organic vapor phase epitaxy grown InGaN/GaN multi quantum well structures using low-tack two-dimensional layered h-BN

DOE Office of Scientific and Technical Information (OSTI.GOV)

Ayari, Taha; Li, Xin; Voss, Paul L.

Recent advances in epitaxial growth have led to the growth of III-nitride devices on 2D layered h-BN. This advance has the potential for wafer-scale transfer to arbitrary substrates, which could improve the thermal management and would allow III-N devices to be used more flexibly in a broader range of applications. We report wafer scale exfoliation of a metal organic vapor phase epitaxy grown InGaN/GaN Multi Quantum Well (MQW) structure from a 5 nm thick h-BN layer that was grown on a 2-inch sapphire substrate. The weak van der Waals bonds between h-BN atomic layers break easily, allowing the MQW structure tomore » be mechanically lifted off from the sapphire substrate using a commercial adhesive tape. This results in the surface roughness of only 1.14 nm on the separated surface. Structural characterizations performed before and after the lift-off confirm the conservation of structural properties after lift-off. Cathodoluminescence at 454 nm was present before lift-off and 458 nm was present after. Electroluminescence near 450 nm from the lifted-off structure has also been observed. These results show that the high crystalline quality ultrathin h-BN serves as an effective sacrificial layer—it maintains performance, while also reducing the GaN buffer thickness and temperature ramps as compared to a conventional two-step growth method. These results support the use of h-BN as a low-tack sacrificial underlying layer for GaN-based device structures and demonstrate the feasibility of large area lift-off and transfer to any template, which is important for industrial scale production.« less

Ion beam modification of the structure and properties of hexagonal boron nitride: An infrared and X-ray diffraction study

NASA Astrophysics Data System (ADS)

Aradi, E.; Naidoo, S. R.; Billing, D. G.; Wamwangi, D.; Motochi, I.; Derry, T. E.

2014-07-01

The vibrational mode for the cubic symmetry of boron nitride (BN) has been produced by boron ion implantation of hexagonal boron nitride (h-BN). The optimum fluence at 150 keV was found to be 5 × 1014 ions/cm2. The presence of the c-BN phase was inferred using glancing incidence XRD (GIXRD) and Fourier Transform Infrared Spectroscopy (FTIR). After implantation, Fourier Transform Infrared Spectroscopy indicated a peak at 1092 cm-1 which corresponds to the vibrational mode for nanocrystalline BN (nc-BN). The glancing angle XRD pattern after implantation exhibited c-BN diffraction peaks relative to the implantation depth of 0.4 μm.

Hexagonal boron nitride nanomechanical resonators with spatially visualized motion

DOE Office of Scientific and Technical Information (OSTI.GOV)

Zheng, Xu-Qian; Lee, Jaesung; Feng, Philip X. -L.

Atomic layers of hexagonal boron nitride (h-BN) crystal are excellent candidates for structural materials as enabling ultrathin, two-dimensional (2D) nanoelectromechanical systems (NEMS) due to the outstanding mechanical properties and very wide bandgap (5.9 eV) of h-BN. In this work, we report the experimental demonstration of h-BN 2D nanomechanical resonators vibrating at high and very high frequencies (from ~ 5 to ~ 70 MHz), and investigations of the elastic properties of h-BN by measuring the multimode resonant behavior of these devices. First, we demonstrate a dry-transferred doubly clamped h-BN membrane with ~ 6.7 nm thickness, the thinnest h-BN resonator known tomore » date. In addition, we fabricate circular drumhead h-BN resonators with thicknesses ranging from ~ 9 to 292 nm, from which we measure up to eight resonance modes in the range of ~ 18 to 35 MHz. Combining measurements and modeling of the rich multimode resonances, we resolve h-BN’s elastic behavior, including the transition from membrane to disk regime, with built-in tension ranging from 0.02 to 2 N m -1. The Young’s modulus of h-BN is determined to be EY≈392 GPa from the measured resonances. The ultrasensitive measurements further reveal subtle structural characteristics and mechanical properties of the suspended h-BN diaphragms, including anisotropic built-in tension and bulging, thus suggesting guidelines on how these effects can be exploited for engineering multimode resonant functions in 2D NEMS transducers.« less

Hexagonal boron nitride nanomechanical resonators with spatially visualized motion

DOE PAGES

Zheng, Xu-Qian; Lee, Jaesung; Feng, Philip X. -L.

2017-07-31

Atomic layers of hexagonal boron nitride (h-BN) crystal are excellent candidates for structural materials as enabling ultrathin, two-dimensional (2D) nanoelectromechanical systems (NEMS) due to the outstanding mechanical properties and very wide bandgap (5.9 eV) of h-BN. In this work, we report the experimental demonstration of h-BN 2D nanomechanical resonators vibrating at high and very high frequencies (from ~ 5 to ~ 70 MHz), and investigations of the elastic properties of h-BN by measuring the multimode resonant behavior of these devices. First, we demonstrate a dry-transferred doubly clamped h-BN membrane with ~ 6.7 nm thickness, the thinnest h-BN resonator known tomore » date. In addition, we fabricate circular drumhead h-BN resonators with thicknesses ranging from ~ 9 to 292 nm, from which we measure up to eight resonance modes in the range of ~ 18 to 35 MHz. Combining measurements and modeling of the rich multimode resonances, we resolve h-BN’s elastic behavior, including the transition from membrane to disk regime, with built-in tension ranging from 0.02 to 2 N m -1. The Young’s modulus of h-BN is determined to be EY≈392 GPa from the measured resonances. The ultrasensitive measurements further reveal subtle structural characteristics and mechanical properties of the suspended h-BN diaphragms, including anisotropic built-in tension and bulging, thus suggesting guidelines on how these effects can be exploited for engineering multimode resonant functions in 2D NEMS transducers.« less

Shame and guilt as shared vulnerability factors: Shame, but not guilt, prospectively predicts both social anxiety and bulimic symptoms.

PubMed

Levinson, Cheri A; Byrne, Meghan; Rodebaugh, Thomas L

2016-08-01

Social anxiety disorder (SAD) and bulimia nervosa (BN) are highly comorbid. However, little is known about the shared vulnerability factors that prospectively predict both SA and BN symptoms. Two potential factors that have not yet been tested are shame and guilt. In the current study we tested if shame and guilt were shared vulnerability factors for SA and BN symptoms. Women (N=300) completed measures of SA symptoms, BN symptoms, state shame and guilt, and trait negative affect at two time points, two months apart. Utilizing structural equation modeling we tested a cross-sectional and prospective model of SA and BN vulnerability. We found that shame prospectively predicted both SA and BN symptoms. We did not find that guilt prospectively predicted SA or BN symptoms. However, higher levels of both BN and SA symptoms predicted increased guilt over time. We found support for shame as a shared prospective vulnerability factor between BN and SA symptoms. Interventions that focus on decreasing shame could potentially alleviate symptoms of BN and SA in one protocol. Copyright © 2016 Elsevier Ltd. All rights reserved.

New two-dimensional boron nitride allotropes with attractive electronic and optical properties

NASA Astrophysics Data System (ADS)

Shahrokhi, Masoud; Mortazavi, Bohayra; Berdiyorov, Golibjon R.

2017-03-01

Using first principles calculations, structural, electronic and optical properties of five new 2D boron nitride (BN) allotropes have been studied. The results exhibit that the cohesive energy for all these five new allotrope is positive such as all these systems are stable; therefore, it is possible to synthesize these structures in experiments. It is found that the band gap of all new 2D BN allotropes is smaller than the h-BN sheet. In our calculations the dielectric tensor is derived within the random phase approximation (RPA). Specifically, the dielectric function, refraction index and the loss function, of the 2D BN allotropes are calculated for both parallel and perpendicular electric field polarizations. The results show that the optical spectra are anisotropic along these two polarizations. The results obtained from our calculations are beneficial to practical applications of these 2D BN allotropes in optoelectronics and electronics.

Electrophoretic deposition of hydroxyapatite-hexagonal boron nitride composite coatings on Ti substrate.

PubMed

Göncü, Yapıncak; Geçgin, Merve; Bakan, Feray; Ay, Nuran

2017-10-01

In this study, commercial pure titanium samples were coated with nano hydroxyapatite-nano hexagonal boron nitride (nano HA-nano hBN) composite by electrophoretic deposition (EPD). The effect of process parameters (applied voltage, deposition time and solid concentration) on the coating morphology, thickness and the adhesion behavior were studied systematically and crack free nano hBN-nano HA composite coating production was achieved for developing bioactive coatings on titanium substrates for orthopedic applications. For the examination of structural and morphological characteristics of the coating surfaces, various complementary analysis methods were performed. For the structural characterization, XRD and Raman Spectroscopy were used while, Scanning Electron Microscopy (SEM) equipped with an energy dispersive spectrometer (EDS) and Transmission Electron Microscopy (TEM) techniques were carried out for revealing the morphological characterization. The results showed that nano HA-nano hBN were successfully deposited on Ti surface with uniform, crack-free coating by EPD. The amounts of hBN in suspension are considered to have no effect on coating thickness. By adding hBN into HA, the morphology of HA did not change and hBN has no significant effect on porous structure. These nanostructured surfaces are expected to be suitable for proliferation of cells and have high potential for bioactive materials. Copyright © 2017 Elsevier B.V. All rights reserved.

Negative Refraction with Superior Transmission in Graphene-Hexagonal Boron Nitride (hBN) Multilayer Hyper Crystal

PubMed Central

Sayem, Ayed Al; Rahman, Md. Masudur; Mahdy, M. R. C.; Jahangir, Ifat; Rahman, Md. Saifur

2016-01-01

In this article, we have theoretically investigated the performance of graphene-hexagonal Boron Nitride (hBN) multilayer structure (hyper crystal) to demonstrate all angle negative refraction along with superior transmission. hBN, one of the latest natural hyperbolic materials, can be a very strong contender to form a hyper crystal with graphene due to its excellence as a graphene-compatible substrate. Although bare hBN can exhibit negative refraction, the transmission is generally low due to its high reflectivity. Whereas due to graphene’s 2D nature and metallic characteristics in the frequency range where hBN behaves as a type-I hyperbolic material, we have found graphene-hBN hyper-crystals to exhibit all angle negative refraction with superior transmission. Interestingly, superior transmission from the whole structure can be fully controlled by the tunability of graphene without hampering the negative refraction originated mainly from hBN. We have also presented an effective medium description of the hyper crystal in the low-k limit and validated the proposed theory analytically and with full wave simulations. Along with the current extensive research on hybridization of graphene plasmon polaritons with (hyperbolic) hBN phonon polaritons, this work might have some substantial impact on this field of research and can be very useful in applications such as hyper-lensing. PMID:27146561

Electronic structure properties of deep defects in hBN

NASA Astrophysics Data System (ADS)

Dev, Pratibha; Prdm Collaboration

In recent years, the search for room-temperature solid-state qubit (quantum bit) candidates has revived interest in the study of deep-defect centers in semiconductors. The charged NV-center in diamond is the best known amongst these defects. However, as a host material, diamond poses several challenges and so, increasingly, there is an interest in exploring deep defects in alternative semiconductors such as hBN. The layered structure of hBN makes it a scalable platform for quantum applications, as there is a greater potential for controlling the location of the deep defect in the 2D-matrix through careful experiments. Using density functional theory-based methods, we have studied the electronic and structural properties of several deep defects in hBN. Native defects within hBN layers are shown to have high spin ground states that should survive even at room temperature, making them interesting solid-state qubit candidates in a 2D matrix. Partnership for Reduced Dimensional Material (PRDM) is part of the NSF sponsored Partnerships for Research and Education in Materials (PREM).

Electronic theoretical study on the influence of torsional deformation on the electronic structure and optical properties of BN-doped graphene

NASA Astrophysics Data System (ADS)

Fan, Dazhi; Liu, Guili; Wei, Lin

2018-06-01

Based on the density functional theory, the effect of torsional deformation on the electronic structure and optical properties of boron nitride (BN)-doped graphene is studied by using the first-principles calculations. The band structure calculations show that the intrinsic graphene is a semi-metallic material with zero band gap and the torsional deformation has a large effect on its band gap, opening its band gap and turning it from the semi-metal to the medium band gap semiconductor. The doping of BN in graphene makes its band gap open and becomes a medium band gap semiconductor. When it is subjected to a torsional effect, it is found to have a weak influence on its band gap. In other words, the doping of BN makes the changes of the band gap of graphene no longer sensitive to torsional deformation. Optical properties show that the doping of BN leads to a significant decrease in the light absorption coefficient and reflectivity of the graphene at the characteristic peak and that of BN-doped graphene system is also weakened by torsional deformation at the characteristic peak. In the absorption spectrum, the absorption peaks of the doping system of the torsion angle of 2-20∘ are redshifted compared with that of the BN-doped system (the torsion angle is 0∘). In the reflection spectrum, the two reflection peaks are all redshifted relative to that of the BN-doped system (the torsion angle is 0∘) and when the torsion angle exceeds 12∘, the size relationship between the two peaks is interchanged. The results of this paper are of guiding significance for the study of graphene-based nanotube devices in terms of deformation.

Geometric and electronic structures of monolayer hexagonal boron nitride with multi-vacancy

NASA Astrophysics Data System (ADS)

Kim, Do-Hyun; Kim, Hag-Soo; Song, Min Woo; Lee, Seunghyun; Lee, Sang Yun

2017-05-01

Hexagonal boron nitride (h-BN) is an electrical insulator with a large band gap of 5 eV and a good thermal conductor of which melting point reaches about 3000 °C. Due to these properties, much attention was given to the thermal stability rather than the electrical properties of h-BN experimentally and theoretically. In this study, we report calculations that the electronic structure of monolayer h-BN can be influenced by the presence of a vacancy defect which leads to a geometric deformation in the hexagonal lattice structure. The vacancy was varied from mono- to tri-vacancy in a supercell, and different defective structures under the same vacancy density were considered in the case of an odd number of vacancies. Consequently, all cases of vacancy defects resulted in a geometric distortion in monolayer h-BN, and new energy states were created between valence and conduction band with the Fermi level shift. Notably, B atoms around vacancies attracted one another while repulsion happened between N atoms around vacancies, irrespective of vacancy density. The calculation of formation energy revealed that multi-vacancy including more B-vacancies has much lower formation energy than vacancies with more N-vacancies. This work suggests that multi-vacancy created in monolayer h-BN will have more B-vacancies and that the presence of multi-vacancy can make monolayer h-BN electrically conductive by the new energy states and the Fermi level shift.

Geometric and electronic structures of monolayer hexagonal boron nitride with multi-vacancy.

PubMed

Kim, Do-Hyun; Kim, Hag-Soo; Song, Min Woo; Lee, Seunghyun; Lee, Sang Yun

2017-01-01

Hexagonal boron nitride (h-BN) is an electrical insulator with a large band gap of 5 eV and a good thermal conductor of which melting point reaches about 3000 °C. Due to these properties, much attention was given to the thermal stability rather than the electrical properties of h-BN experimentally and theoretically. In this study, we report calculations that the electronic structure of monolayer h-BN can be influenced by the presence of a vacancy defect which leads to a geometric deformation in the hexagonal lattice structure. The vacancy was varied from mono- to tri-vacancy in a supercell, and different defective structures under the same vacancy density were considered in the case of an odd number of vacancies. Consequently, all cases of vacancy defects resulted in a geometric distortion in monolayer h-BN, and new energy states were created between valence and conduction band with the Fermi level shift. Notably, B atoms around vacancies attracted one another while repulsion happened between N atoms around vacancies, irrespective of vacancy density. The calculation of formation energy revealed that multi-vacancy including more B-vacancies has much lower formation energy than vacancies with more N-vacancies. This work suggests that multi-vacancy created in monolayer h-BN will have more B-vacancies and that the presence of multi-vacancy can make monolayer h-BN electrically conductive by the new energy states and the Fermi level shift.

Tuning the electronic and optical properties of hexagonal boron-nitride nanosheet by inserting graphene quantum dots

NASA Astrophysics Data System (ADS)

Ding, Yi-Min; Shi, Jun-Jie; Zhang, Min; Wu, Meng; Wang, Hui; Cen, Yu-Lang; Pan, Shu-Hang; Guo, Wen-Hui

2018-02-01

It is difficult to integrate two-dimensional (2D) graphene and hexagonal boron-nitride (h-BN) in optoelectronic nanodevices, due to the semi-metal and insulator characteristic of graphene and h-BN, respectively. Using the state-of-the-art first-principles calculations based on many-body perturbation theory, we investigate the electronic and optical properties of h-BN nanosheet embedded with graphene dots. We find that C atom impurities doped in h-BN nanosheet tend to phase-separate into graphene quantum dots (QD), and BNC hybrid structure, i.e. a graphene dot within a h-BN background, can be formed. The band gaps of BNC hybrid structures have an inverse relationship with the size of graphene dot. The calculated optical band gaps for BNC structures vary from 4.71 eV to 3.77 eV, which are much smaller than that of h-BN nanosheet. Furthermore, the valence band maximum is located in C atoms bonded to B atoms and conduction band minimum is located in C atoms bonded to N atoms, which means the electron and hole wave functions are closely distributed around the graphene dot. The bound excitons, localized around the graphene dot, determine the optical spectra of the BNC hybrid structures, in which the exciton binding energies decrease with increase in the size of graphene dots. Our results provide an important theoretical basis for the design and development of BNC-based optoelectronic nanodevices.

FAST TRACK COMMUNICATION: Electronic structure of a graphene/hexagonal-BN heterostructure grown on Ru(0001) by chemical vapor deposition and atomic layer deposition: extrinsically doped graphene

NASA Astrophysics Data System (ADS)

Bjelkevig, Cameron; Mi, Zhou; Xiao, Jie; Dowben, P. A.; Wang, Lu; Mei, Wai-Ning; Kelber, Jeffry A.

2010-08-01

A significant BN-to-graphene charge donation is evident in the electronic structure of a graphene/h-BN(0001) heterojunction grown by chemical vapor deposition and atomic layer deposition directly on Ru(0001), consistent with density functional theory. This filling of the lowest unoccupied state near the Brillouin zone center has been characterized by combined photoemission/k vector resolved inverse photoemission spectroscopies, and Raman and scanning tunneling microscopy/spectroscopy. The unoccupied σ*(Γ1 +) band dispersion yields an effective mass of 0.05 me for graphene in the graphene/h-BN(0001) heterostructure, in spite of strong perturbations to the graphene conduction band edge placement.

In Situ Formation of Carbon Nanotubes Encapsulated within Boron Nitride Nanotubes via Electron Irradiation

DOE Office of Scientific and Technical Information (OSTI.GOV)

Arenal, Raul; Lopez-Bezanilla, Alejandro

2014-07-25

We report experimental evidence of the formation by in situ electron-irradiation of single-walled carbon nanotubes (C NT) confined within boron nitride nanotubes (BN-NT). The electron radiation stemming from the microscope supplies the energy required by the amorphous carbonaceous structures to crystallize in a tubular form in a catalyst free procedure, at room temperature and high vacuum. The structural defects resulting from the interaction of the shapeless carbon with the BN nanotube are corrected in a self-healing process throughout the crystallinization. Structural changes developed during the irradiation process such as defects formation and evolution, shrinkage, and shortness of the BN-NT weremore » in situ monitored. The outer BN wall provides a protective and insulating shell against environmental Perturbations to the inner C-NT without affecting their electronic properties, as demonstrated by first principles calculations.« less

Modification of the electronic properties of hexagonal boron-nitride in BN/graphene vertical heterostructures

DOE PAGES

Pan, Minghu; Liang, Liangbo; Lin, Wenzhi; ...

2016-09-28

Van der Waals (vdW) heterostructures consist of isolated atomic planar structures, assembled layer- by-layer into desired structures in a well-defined sequence. Graphene deposited on hexagonal boron nitride (h-BN) has been first considered as a testbed system for vdW heterostructures, and many others have been demonstrated both theoretically and experimentally, revealing many attractive properties and phenomena. However, much less emphasis has been placed on how graphene actively affects h-BN properties. Here, we perform local probe measurements on single-layer h-BN grown over graphene and highlight the manifestation of a proximity effect that significantly affects the electronic properties of h-BN due to itsmore » coupling with the underlying graphene. We find electronic states originating from the graphene layer and the Cu substrate to be injected into the wide electronic gap of the h-BN top layer. Such proximity effect is further confirmed in a study of the variation of h-BN in-gap states with interlayer couplings, elucidated using a combination of topographical/ spectroscopic measurements and first-principles density functional theory calculations. In conclusion, the findings of this work indicate the potential of mutually engineering electronic properties of the components of vdW heterostructures.« less

Unsupported platinum nanoparticles as effective sensors of neurotransmitters and possible drug curriers

NASA Astrophysics Data System (ADS)

Tąta, Agnieszka; Gralec, Barbara; Proniewicz, Edyta

2018-03-01

Herein, surface-enhanced Raman scattering (SERS) activity of positively charged unsupported platinum nanoparticles (PtNPs) with ∼12 nm size and narrow size distribution, in an aqueous solution, towards neurotransmitters was monitored at 785 nm excitation wavelength. The pure PtNPs were synthetized by polyol method. Their morphology and structure were checked by scanning electron microscopy (SEM) and X-ray diffraction spectroscopy (XRD) measurements. As a neurotransmitter bombesin (BN), which exhibits autocrine effect on the growth of normal and tumour tissues, and its fragments from the C-terminal end: BN13-14, BN12-14, BN11-14, BN10-14, BN9-14, and BN8-14 (X-14 fragments of the BN amino acid sequence) were chosen. The collected spectra were interpreted and discussed. This is to determine the adsorption mode of bombesin onto the PtNPs surface and changes in this mode as a result of the bombesin backbone shortening from the N-terminal end. This is important from the point of using PtNPs as potential BN carrier into the cancerous tissue and antitumor drug.

Strain, stabilities and electronic properties of hexagonal BN bilayers

NASA Astrophysics Data System (ADS)

Fujimoto, Yoshitaka; Saito, Susumu

Hexagonal boron nitride (h-BN) atomic layers have been regarded as fascinating materials both scientifically and technologically due to the sizable band gap. This sizable band-gap nature of the h-BN atomic layers would provide not only new physical properties but also novel nano- and/or opto-electronics applications. Here, we study the first-principles density-functional study that clarifies the biaxial strain effects on the energetics and the electronic properties of h-BN bilayers. We show that the band gaps of the h-BN bilayers are tunable by applying strains. Furthermore, we show that the biaxial strains can produce a transition from indirect to direct band gaps of the h-BN bilayer. We also discuss that both AA and AB stacking patterns of h-BN bilayer become feasible structures because h-BN bilayers possess two different directions in the stacking patterns. Supported by MEXT Elements Strategy Initiative to Form Core Research Center through Tokodai Institute for Element Strategy, JSPS KAKENHI Grant Numbers JP26390062 and JP25107005.

Utilizing boron nitride sheets as thin supports for high resolution imaging of nanocrystals.

PubMed

Wu, Yimin A; Kirkland, Angus I; Schäffel, Franziska; Porfyrakis, Kyriakos; Young, Neil P; Briggs, G Andrew D; Warner, Jamie H

2011-05-13

We demonstrate the use of thin BN sheets as supports for imaging nanocrystals using low voltage (80 kV) aberration-corrected high resolution transmission electron microscopy. This provides an alternative to the previously utilized 2D crystal supports of graphene and graphene oxide. A simple chemical exfoliation method is applied to get few layer boron nitride (BN) sheets with micrometer-sized dimensions. This generic approach of using BN sheets as supports is shown by depositing Mn doped ZnSe nanocrystals directly onto the BN sheets and resolving the atomic structure from both the ZnSe nanocrystals and the BN support. Phase contrast images reveal moiré patterns of interference between the beams diffracted by the nanocrystals and the BN substrate that are used to determine the relative orientation of the nanocrystals with respect to the BN sheets and interference lattice planes. Double diffraction is observed and has been analyzed.

Bilayered graphene/h-BN with folded holes as new nanoelectronic materials: modeling of structures and electronic properties

PubMed Central

Chernozatonskii, Leonid A.; Demin, Viсtor A.; Bellucci, Stefano

2016-01-01

The latest achievements in 2-dimensional (2D) material research have shown the perspective use of sandwich structures in nanodevices. We demonstrate the following generation of bilayer materials for electronics and optoelectronics. The atomic structures, the stability and electronic properties of Moiré graphene (G)/h-BN bilayers with folded nanoholes have been investigated theoretically by ab-initio DFT method. These perforated bilayers with folded hole edges may present electronic properties different from the properties of both graphene and monolayer nanomesh structures. The closing of the edges is realized by C-B(N) bonds that form after folding the borders of the holes. Stable ≪round≫ and ≪triangle≫ holes organization are studied and compared with similar hole forms in single layer graphene. The electronic band structures of the considered G/BN nanomeshes reveal semiconducting or metallic characteristics depending on the sizes and edge terminations of the created holes. This investigation of the new types of G/BN nanostructures with folded edges might provide a directional guide for the future of this emerging area. PMID:27897237

Constructing a clinical decision-making framework for image-guided radiotherapy using a Bayesian Network

NASA Astrophysics Data System (ADS)

Hargrave, C.; Moores, M.; Deegan, T.; Gibbs, A.; Poulsen, M.; Harden, F.; Mengersen, K.

2014-03-01

A decision-making framework for image-guided radiotherapy (IGRT) is being developed using a Bayesian Network (BN) to graphically describe, and probabilistically quantify, the many interacting factors that are involved in this complex clinical process. Outputs of the BN will provide decision-support for radiation therapists to assist them to make correct inferences relating to the likelihood of treatment delivery accuracy for a given image-guided set-up correction. The framework is being developed as a dynamic object-oriented BN, allowing for complex modelling with specific subregions, as well as representation of the sequential decision-making and belief updating associated with IGRT. A prototype graphic structure for the BN was developed by analysing IGRT practices at a local radiotherapy department and incorporating results obtained from a literature review. Clinical stakeholders reviewed the BN to validate its structure. The BN consists of a sub-network for evaluating the accuracy of IGRT practices and technology. The directed acyclic graph (DAG) contains nodes and directional arcs representing the causal relationship between the many interacting factors such as tumour site and its associated critical organs, technology and technique, and inter-user variability. The BN was extended to support on-line and off-line decision-making with respect to treatment plan compliance. Following conceptualisation of the framework, the BN will be quantified. It is anticipated that the finalised decision-making framework will provide a foundation to develop better decision-support strategies and automated correction algorithms for IGRT.

Characterizing structural association alterations within brain networks in normal aging using Gaussian Bayesian networks.

PubMed

Guo, Xiaojuan; Wang, Yan; Chen, Kewei; Wu, Xia; Zhang, Jiacai; Li, Ke; Jin, Zhen; Yao, Li

2014-01-01

Recent multivariate neuroimaging studies have revealed aging-related alterations in brain structural networks. However, the sensory/motor networks such as the auditory, visual and motor networks, have obtained much less attention in normal aging research. In this study, we used Gaussian Bayesian networks (BN), an approach investigating possible inter-regional directed relationship, to characterize aging effects on structural associations between core brain regions within each of these structural sensory/motor networks using volumetric MRI data. We then further examined the discriminability of BN models for the young (N = 109; mean age =22.73 years, range 20-28) and old (N = 82; mean age =74.37 years, range 60-90) groups. The results of the BN modeling demonstrated that structural associations exist between two homotopic brain regions from the left and right hemispheres in each of the three networks. In particular, compared with the young group, the old group had significant connection reductions in each of the three networks and lesser connection numbers in the visual network. Moreover, it was found that the aging-related BN models could distinguish the young and old individuals with 90.05, 73.82, and 88.48% accuracy for the auditory, visual, and motor networks, respectively. Our findings suggest that BN models can be used to investigate the normal aging process with reliable statistical power. Moreover, these differences in structural inter-regional interactions may help elucidate the neuronal mechanism of anatomical changes in normal aging.

Manipulation of enhanced absorption with tilted hexagonal boron nitride slabs

NASA Astrophysics Data System (ADS)

Wu, Xiaohu; Fu, Ceji

2018-04-01

The wavevector of electromagnetic wave propagation in a hexagonal boron nitride (hBN) slab can be controlled by tilting its optical axis. This property can be used to manipulate the absorption in a hBN slab. By carefully analyzing the dependence of the absorptivity of a thin hBN slab on the tilted angle of its optical axis, we propose a structure that can realize great absorptivity enhancement in a band by stacking hBN slabs of different tilted angles. Our numerical results show that the absorptivity of a structure made of 91 stacked hBN slabs can be achieved higher than 0.94 in the wavenumber range from 1367 to 1580 cm-1 when the tilted angles of the slabs are properly arranged. The strong absorption is attributed to the combination of impedance matching at the slab interfaces and enlarged wavevectors in the slabs. This work reveals a novel way to realize strong absorption with anisotropic materials for applications in areas such as thermal radiative energy harvesting and conversion.

Microstructures of BN/SiC coatings on nicalon fibers

NASA Technical Reports Server (NTRS)

Dickerson, R. M.; Singh, M.

1995-01-01

The microstructures of Nicalon silicon carbide (SiC) fibers and layered coatings of boron nitride (BN) followed by chemical vapor infiltrated silicon carbide (CVI-SiC) were characterized using optical and electron microscopy. Two different precursors and reactions were used to produce the BN layers while the deposition of CVI silicon carbide was nearly identical. Coated tows were examined in cross-section to characterize the chemistry and structures of the constituents and the interfaces. One BN precursor yielded three sublayers while the other gave a relatively homogeneous nanocrystalline layer.

Progress on BN and Doped-BN Coatings on Woven Fabrics

NASA Technical Reports Server (NTRS)

Hurwitz, Frances I.; Scott, John M.; Chayka, Paul V.

2001-01-01

A novel, multistep process for applying interface coatings to woven structures using a pulsed CVD process is being evaluated. Borazine (B3N3H6), a neat liquid, and several Si precursors are used in the process to produce BN and SiBN coatings on Hi- Nicalon fabrics and preforms. A three variable, two level, full factorial matrix is proposed to define the influence of processing parameters. Coating morphology, uniformity and chemistry are characterized by field emission scanning electron microscopy (FESEM), energy dispersive (EDS) and Auger spectroscopies.

Study of electronic and magnetic properties of h-BN on Ni surfaces: A DFT approach

NASA Astrophysics Data System (ADS)

Sahoo, M. R.; Sahu, S.; Kushwaha, A. K.; Nayak, S.

2018-04-01

Hexagonal boron nitride (h-BN) is a promising material for implementation in spintronics due to large band gap, low spin-orbit coupling, and a small lattice mismatch to graphene and close-packedsurfaces of fcc-Ni(111). Electronic and magnetic properties of single layer hexagonal Boron Nitride (h-BN) on Ni (111) surface have been studied with density functional calculation. Since lattice constants of nickel surfaces are very close to that of h-BN, nickel acts as a good substrate. We found that the interaction between 2Pz - 3dz2 orbitals leads to change in electronic band structure as well as density of states which results spin polarization in h-BN.

Single Crystalline Film of Hexagonal Boron Nitride Atomic Monolayer by Controlling Nucleation Seeds and Domains

PubMed Central

Wu, Qinke; Park, Ji-Hoon; Park, Sangwoo; Jung, Seong Jun; Suh, Hwansoo; Park, Noejung; Wongwiriyapan, Winadda; Lee, Sungjoo; Lee, Young Hee; Song, Young Jae

2015-01-01

A monolayer hexagonal boron nitride (h-BN) film with controllable domain morphology and domain size (varying from less than 1 μm to more than 100 μm) with uniform crystalline orientation was successfully synthesized by chemical vapor deposition (CVD). The key for this extremely large single crystalline domain size of a h-BN monolayer is a decrease in the density of nucleation seeds by increasing the hydrogen gas flow during the h-BN growth. Moreover, the well-defined shape of h-BN flakes can be selectively grown by controlling Cu-annealing time under argon atmosphere prior to h-BN growth, which provides the h-BN shape varies in triangular, trapezoidal, hexagonal and complex shapes. The uniform crystalline orientation of h-BN from different nucleation seeds can be easily confirmed by polarized optical microscopy (POM) with a liquid crystal coating. Furthermore, seamlessly merged h-BN flakes without structural domain boundaries were evidence by a selective hydrogen etching after a full coverage of a h-BN film was achieved. This seamless large-area and atomic monolayer of single crystalline h-BN film can offer as an ideal and practical template of graphene-based devices or alternative two-dimensional materials for industrial applications with scalability. PMID:26537788

Single Crystalline Film of Hexagonal Boron Nitride Atomic Monolayer by Controlling Nucleation Seeds and Domains

NASA Astrophysics Data System (ADS)

Wu, Qinke; Park, Ji-Hoon; Park, Sangwoo; Jung, Seong Jun; Suh, Hwansoo; Park, Noejung; Wongwiriyapan, Winadda; Lee, Sungjoo; Lee, Young Hee; Song, Young Jae

2015-11-01

A monolayer hexagonal boron nitride (h-BN) film with controllable domain morphology and domain size (varying from less than 1 μm to more than 100 μm) with uniform crystalline orientation was successfully synthesized by chemical vapor deposition (CVD). The key for this extremely large single crystalline domain size of a h-BN monolayer is a decrease in the density of nucleation seeds by increasing the hydrogen gas flow during the h-BN growth. Moreover, the well-defined shape of h-BN flakes can be selectively grown by controlling Cu-annealing time under argon atmosphere prior to h-BN growth, which provides the h-BN shape varies in triangular, trapezoidal, hexagonal and complex shapes. The uniform crystalline orientation of h-BN from different nucleation seeds can be easily confirmed by polarized optical microscopy (POM) with a liquid crystal coating. Furthermore, seamlessly merged h-BN flakes without structural domain boundaries were evidence by a selective hydrogen etching after a full coverage of a h-BN film was achieved. This seamless large-area and atomic monolayer of single crystalline h-BN film can offer as an ideal and practical template of graphene-based devices or alternative two-dimensional materials for industrial applications with scalability.

Direct growth of hexagonal boron nitride/graphene heterostructures on cobalt foil substrates by plasma-assisted molecular beam epitaxy

DOE Office of Scientific and Technical Information (OSTI.GOV)

Xu, Zhongguang; Khanaki, Alireza; Tian, Hao

2016-07-25

Graphene/hexagonal boron nitride (G/h-BN) heterostructures have attracted a great deal of attention because of their exceptional properties and wide variety of potential applications in nanoelectronics. However, direct growth of large-area, high-quality, and stacked structures in a controllable and scalable way remains challenging. In this work, we demonstrate the synthesis of h-BN/graphene (h-BN/G) heterostructures on cobalt (Co) foil by sequential deposition of graphene and h-BN layers using plasma-assisted molecular beam epitaxy. It is found that the coverage of h-BN layers can be readily controlled on the epitaxial graphene by growth time. Large-area, uniform-quality, and multi-layer h-BN films on thin graphite layersmore » were achieved. Based on an h-BN (5–6 nm)/G (26–27 nm) heterostructure, capacitor devices with Co(foil)/G/h-BN/Co(contact) configuration were fabricated to evaluate the dielectric properties of h-BN. The measured breakdown electric field showed a high value of ∼2.5–3.2 MV/cm. Both I-V and C-V characteristics indicate that the epitaxial h-BN film has good insulating characteristics.« less

One-pot synthesis of h-BN fullerenes usinsg a graphene oxide template

NASA Astrophysics Data System (ADS)

Kim, Sang Sub; Khai, Tran Van; Kwon, Yong Jung; Katoch, Akash; Wu, Ping; Kim, Hyoun Woo

2015-09-01

Hexagonal-boron nitride ( h-BN) fullerenes were synthesized from a graphene oxide (GO) template by simultaneously heating the GO and B2O3 in the presence of NH3 gas. Transmission electron microscopy (TEM) observations revealed that a considerable amount of product had a fullerene-like nanostructure. Typical BN fullerenes have a polyhedral shape, being hollow nanocages. Lattice-resolved TEM and X-ray diffraction consistently demonstrated the formation of h-BN fullerenes. The FTIR spectrum exhibited absorption bands at approximately 800 and 1378 cm-1, which were related to the h-BN structure. The Raman spectra exhibited peaks at 1368 and 1399 cm-1, which can be related to BN sheets and BN fullerenes, respectively. The photoluminescence spectrum of the h-BN fullerenes taken at 8 K exhibited intense white-light emission. To reveal the origin of the broad emission band, which could be a superimposition of several peaks, we used a deconvolution procedure based on Gaussian functions. We proposed a growth mechanism of the h-BN fullerenes and verified it with a thermodynamic calculation. This work provides a cost-effective approach to synthesize fullerene-type boron nitride on a production scale.

Diamond- cBN alloy: A universal cutting material

DOE PAGES

Wang, Pei; He, Duanwei; Wang, Liping; ...

2015-09-08

Diamond and cubic boron nitride ( cBN) as conventional superhard materials have found widespread industrial applications, but both have inherent limitations. Diamond is not suitable for high-speed cutting of ferrous materials due to its poor chemical inertness, while cBN is only about half as hard as diamond. Because of their affinity in structural lattices and covalent bonding character, diamond and cBN could form alloys that can potentially fill the performance gap. However, the idea has never been demonstrated because samples obtained in the previous studies were too small to be tested for their practical performance. Here, we report the synthesismore » and characterization of transparent bulk diamond- cBN alloy compacts whose diameters (3 mm) are sufficiently large for them to be processed into cutting tools. The testing results show that the diamond- cBN alloy has superior chemical inertness over polycrystalline diamond and higher hardness than single crystal cBN. In conclusion, high-speed cutting tests on hardened steel and granite suggest that diamond- cBN alloy is indeed a universal cutting material.« less

Diamond-cBN alloy: A universal cutting material

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wang, Pei; High Pressure Science and Engineering Center and Department of Physics and Astronomy, University of Nevada Las Vegas, Las Vegas, Nevada 89154; He, Duanwei, E-mail: duanweihe@scu.edu.cn

Diamond and cubic boron nitride (cBN) as conventional superhard materials have found widespread industrial applications, but both have inherent limitations. Diamond is not suitable for high-speed cutting of ferrous materials due to its poor chemical inertness, while cBN is only about half as hard as diamond. Because of their affinity in structural lattices and covalent bonding character, diamond and cBN could form alloys that can potentially fill the performance gap. However, the idea has never been demonstrated because samples obtained in the previous studies were too small to be tested for their practical performance. Here, we report the synthesis andmore » characterization of transparent bulk diamond-cBN alloy compacts whose diameters (3 mm) are sufficiently large for them to be processed into cutting tools. The testing results show that the diamond-cBN alloy has superior chemical inertness over polycrystalline diamond and higher hardness than single crystal cBN. High-speed cutting tests on hardened steel and granite suggest that diamond-cBN alloy is indeed a universal cutting material.« less

Diamond- cBN alloy: A universal cutting material

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wang, Pei; He, Duanwei; Wang, Liping

Diamond and cubic boron nitride ( cBN) as conventional superhard materials have found widespread industrial applications, but both have inherent limitations. Diamond is not suitable for high-speed cutting of ferrous materials due to its poor chemical inertness, while cBN is only about half as hard as diamond. Because of their affinity in structural lattices and covalent bonding character, diamond and cBN could form alloys that can potentially fill the performance gap. However, the idea has never been demonstrated because samples obtained in the previous studies were too small to be tested for their practical performance. Here, we report the synthesismore » and characterization of transparent bulk diamond- cBN alloy compacts whose diameters (3 mm) are sufficiently large for them to be processed into cutting tools. The testing results show that the diamond- cBN alloy has superior chemical inertness over polycrystalline diamond and higher hardness than single crystal cBN. In conclusion, high-speed cutting tests on hardened steel and granite suggest that diamond- cBN alloy is indeed a universal cutting material.« less

Microstructural, Chemical and Mechanical Characterization of Polymer-Derived Hi-Nicalon Fibers with Surface Coatings

NASA Technical Reports Server (NTRS)

Bansal, Narottam P.; Chen, Yuan L.

1998-01-01

Room temperature tensile strengths of as-received Hi-Nicalon fibers and those having BN/SiC, p-BN/SiC, and p-B(Si)N/SiC surface coatings, deposited by chemical vapor deposition, were measured using an average fiber diameter of 13.5 microns. The Weibull statistical parameters were determined for each fiber. The average tensile strength of uncoated Hi-Nicalon on was 3.19 +/- 0.73 GPa with a Weibull modulus of 5.41. Strength of fibers coated with BN/SiC did not change. However, coat with p-BN/SiC and p-B(Si)N/SiC surface layers showed strength loss of approx. 10 and 35 percent, respectively, compared with as-received fibers. The elemental compositions of the fibers and the coatings were analyzed using scanning Auger microprobe and energy dispersive x-ray spectroscopy. The BN coating was contaminated with a large concentration of carbon and some oxygen. In contrast, p-BN, p-B(Si)N, and SiC coatings did not show any contamination. Microstructural analyses of the fibers and the coatings were done by scanning electron microscopy (SEM), transmission electron microscopy (TEM), and selected area electron diffraction. Hi-Nicalon fiber consists of the P-SIC nanocrystals ranging in size from 1 to 30 nm embedded in an amorphous matrix. TEM analysis of the BN coating revealed four distinct layers with turbostatic structure. The p-BN layer was turbostratic and showed considerable preferred orientation. The p-B(Si)N was glassy and the silicon and boron were uniformly distributed. The silicon carbide coating was polycrystalline with a columnar structure along the growth direction. The p-B(Si)N/SiC coatings were more uniform, less defective and of better quality than the BN/SiC or the p-BN/SiC coatings.

Preparation of high-content hexagonal boron nitride composite film and characterization of atomic oxygen erosion resistance

NASA Astrophysics Data System (ADS)

Zhang, Yu; Li, Min; Gu, Yizhuo; Wang, Shaokai; Zhang, Zuoguang

2017-04-01

Space aircrafts circling in low earth orbit are suffered from highly reactive atomic oxygen (AO). To shield AO, a flexible thin film with 80 wt.% hexagonal boron nitride (h-BN) and h-BN/epoxy film were fabricated through vacuum filtration and adding nanofibrillated cellulose fibers. H-BN nanosheets were hydroxylated for enhancing interaction in the films. Mass loss and erosion yield at accumulated AO fluence about 3.04 × 1020 atoms/cm2 were adopted to evaluate the AO resistance properties of the films. A carpet-like rough surface, chemical oxidations and change in crystal structure of h-BN were found after AO treatment, and the degrading mechanism was proposed. The mass loss and erosion yield under AO attack were compared between h-BN film and h-BN/epoxy film, and the comparison was also done for various types of shielding AO materials. Excellent AO resistance property of h-BN film is shown, and the reasons are analyzed.

Layer speciation and electronic structure investigation of freestanding hexagonal boron nitride nanosheets

NASA Astrophysics Data System (ADS)

WangEqual Contribution To This Work., Jian; Wang, Zhiqiang; Cho, Hyunjin; Kim, Myung Jong; Sham, T. K.; Sun, Xuhui

2015-01-01

Chemical imaging, thickness mapping, layer speciation and polarization dependence have been performed on single and multilayered (up to three layers and trilayered nanosheets overlapping to form 6 and 9 layers) hexagonal boron nitride (hBN) nanosheets by scanning transmission X-ray microscopy. Spatially-resolved XANES directly from freestanding regions of different layers has been extracted and compared with sample normal and 30° tilted configurations. Notably a double feature σ* excitonic state and a stable high energy σ* state were observed at the boron site in addition to the intense π* excitonic state. The boron projected σ* DOS, especially the first σ* exciton, is sensitive to surface modification, particularly in the single layered hBN nanosheet which shows more significant detectable contaminants and defects such as tri-coordinated boron/nitrogen oxide. The nitrogen site has shown very weak or no excitonic character. The distinct excitonic effect on boron and nitrogen was interpreted to the partly ionic state of hBN. Bulk XANES of hBN nanosheets was also measured to confirm the spectro-microscopic STXM result. Finally, the unoccupied electronic structures of hBN and graphene were compared.Chemical imaging, thickness mapping, layer speciation and polarization dependence have been performed on single and multilayered (up to three layers and trilayered nanosheets overlapping to form 6 and 9 layers) hexagonal boron nitride (hBN) nanosheets by scanning transmission X-ray microscopy. Spatially-resolved XANES directly from freestanding regions of different layers has been extracted and compared with sample normal and 30° tilted configurations. Notably a double feature σ* excitonic state and a stable high energy σ* state were observed at the boron site in addition to the intense π* excitonic state. The boron projected σ* DOS, especially the first σ* exciton, is sensitive to surface modification, particularly in the single layered hBN nanosheet which shows more significant detectable contaminants and defects such as tri-coordinated boron/nitrogen oxide. The nitrogen site has shown very weak or no excitonic character. The distinct excitonic effect on boron and nitrogen was interpreted to the partly ionic state of hBN. Bulk XANES of hBN nanosheets was also measured to confirm the spectro-microscopic STXM result. Finally, the unoccupied electronic structures of hBN and graphene were compared. Electronic supplementary information (ESI) available. See DOI: 10.1039/c4nr04445b

Electron affinity of cubic boron nitride terminated with vanadium oxide

NASA Astrophysics Data System (ADS)

Yang, Yu; Sun, Tianyin; Shammas, Joseph; Kaur, Manpuneet; Hao, Mei; Nemanich, Robert J.

2015-10-01

A thermally stable negative electron affinity (NEA) for a cubic boron nitride (c-BN) surface with vanadium-oxide-termination is achieved, and its electronic structure was analyzed with in-situ photoelectron spectroscopy. The c-BN films were prepared by electron cyclotron resonance plasma-enhanced chemical vapor deposition employing BF3 and N2 as precursors. Vanadium layers of ˜0.1 and 0.5 nm thickness were deposited on the c-BN surface in an electron beam deposition system. Oxidation of the metal layer was achieved by an oxygen plasma treatment. After 650 °C thermal annealing, the vanadium oxide on the c-BN surface was determined to be VO2, and the surfaces were found to be thermally stable, exhibiting an NEA. In comparison, the oxygen-terminated c-BN surface, where B2O3 was detected, showed a positive electron affinity of ˜1.2 eV. The B2O3 evidently acts as a negatively charged layer introducing a surface dipole directed into the c-BN. Through the interaction of VO2 with the B2O3 layer, a B-O-V layer structure would contribute a dipole between the O and V layers with the positive side facing vacuum. The lower enthalpy of formation for B2O3 is favorable for the formation of the B-O-V layer structure, which provides a thermally stable surface dipole and an NEA surface.

Differential impairments underlying decision making in anorexia nervosa and bulimia nervosa: a cognitive modeling analysis.

PubMed

Chan, Trista Wai Sze; Ahn, Woo-Young; Bates, John E; Busemeyer, Jerome R; Guillaume, Sebastien; Redgrave, Graham W; Danner, Unna N; Courtet, Philippe

2014-03-01

This study examined the underlying processes of decision-making impairments in individuals with anorexia nervosa (AN) and bulimia nervosa (BN). We deconstructed their performance on the widely used decision task, the Iowa Gambling Task (IGT) into cognitive, motivational, and response processes using cognitive modeling analysis. We hypothesized that IGT performance would be characterized by impaired memory functions and heightened punishment sensitivity in AN, and by elevated sensitivity to reward as opposed to punishment in BN. We analyzed trial-by-trial data of IGT obtained from 224 individuals: 94 individuals with AN, 63 with BN, and 67 healthy comparison individuals (HC). The prospect valence learning model was used to assess cognitive, motivational, and response processes underlying IGT performance. Individuals with AN showed marginally impaired IGT performance compared to HC. Their performance was characterized by impairments in memory functions. Individuals with BN showed significantly impaired IGT performance compared to HC. They showed greater relative sensitivity to gains as opposed to losses than HC. Memory functions in AN were positively correlated with body mass index. This study identified differential impairments underlying IGT performance in AN and BN. Findings suggest that impaired decision making in AN might involve impaired memory functions. Impaired decision making in BN might involve altered reward and punishment sensitivity. Copyright © 2013 Wiley Periodicals, Inc.

Molecular Beam Epitaxial Growth and Characterization of Graphene and Hexagonal Boron Nitride Two-Dimensional Layers

NASA Astrophysics Data System (ADS)

Zheng, Renjing

Van der Waals (vdW) materials (also called as two-dimensional (2D) material in some literature) systems have received extensive attention recently due to their potential applications in next-generation electronics platform. Exciting properties have been discovered in this field, however, the performance and properties of the systems rely on the materials' quality and interface significantly, leading to the urgent need for scalable synthesis of high-quality vdW crystals and heterostructures. Toward this direction, this dissertation is devoted on the study of Molecular Beam Epitaxy (MBE) growth and various characterization of vdW materials and heterostructures, especially graphene and hexagonal boron nitride (h-BN). The goal is to achieve high-quality vdW materials and related heterostructures. There are mainly four projects discussed in this dissertation. The first project (Chapter 2) is about MBE growth of large-area h-BN on copper foil. After the growth, the film was transferred onto SiO2 substrate for characterization. It is observed that as-grown film gives evident h-BN Raman spectrum; what's more, h-BN peak intensity and position is dependent on film thickness. N-1s and B-1s XPS peaks further suggest the formation of h-BN. AFM and SEM images show the film is flat and continuous over large area. Our synthesis method shows it's possible to use MBE to achieve h-BN growth and could also pave a way for some unique structure, such as h-BN/graphene heterostructures and doped h-BN films by MBE. The second project (Chapter 3) is focused on establishment of grapehene/h-BN heterostructure on cobalt (Co) film. In-situ epitaxial growth of graphene/h-BN heterostructures on Co film substrate was achieved by using plasma-assisted MBE. The direct graphene/h-BN vertical stacking structures were demonstrated and further confirmed by various characterizations, such as Raman spectroscopy, SEM, XPS and TEM. Large area heterostructures consisting of single- /bilayer graphene and multilayer h-BN were achieved. The mismatch angle between graphene and h-BN is below 1º. The third project (Chapter 4) is about graphene growth on Fe by MBE at low temperature. Temperature-dependent growth of graphene on Fe using MBE is studied. Two-dimensional (2D), large-area graphene samples were grown on Fe thin films, and characterized by Raman, X-ray photoelectron spectroscopy, X-ray diffraction, optical microscopy, transmission electron microscopy and atomic force microscopy. Graphene is achieved on Fe at a wide growth temperature range and as low as 400 °C. The growth mechanism is studied and shows graphene growth is associated with formation and decomposition of iron carbide. The forth part is about a convenient way to produce vdW heterostructures: graphene growth of exfoliated h-BN on Co. We demonstrated graphene/h-BN heterostructures by growing graphene onto the substrates which consist of exfoliated h-BN on Co thin film using MBE. The heterostructure samples grown at different temperatures and growth durations were characterized by Raman, optical microscopy, atomic force microscopy, microwave impedance microscopy and scanning tunneling microscopy. It is found that the graphene/h-BN heterostructures were formed by the formation of graphene underneath rather than on top of the h-BN flakes. The growth mechanism is discussed. In summary, we develop and optimize growth of vdW materials (h-BN and graphene), and vdW heterostructures by MBE. Various characterization has been carried out to evaluate properties of the films in structural, optical and electrical aspects. Our results reveal that MBE can provide an excellent alternative way for reliable growth of high-quality and large-size vdW materials and related heterostructures, which will attract more attention for the utilization of MBE in vdW materials research.

System Analysis by Mapping a Fault-tree into a Bayesian-network

NASA Astrophysics Data System (ADS)

Sheng, B.; Deng, C.; Wang, Y. H.; Tang, L. H.

2018-05-01

In view of the limitations of fault tree analysis in reliability assessment, Bayesian Network (BN) has been studied as an alternative technology. After a brief introduction to the method for mapping a Fault Tree (FT) into an equivalent BN, equations used to calculate the structure importance degree, the probability importance degree and the critical importance degree are presented. Furthermore, the correctness of these equations is proved mathematically. Combining with an aircraft landing gear’s FT, an equivalent BN is developed and analysed. The results show that richer and more accurate information have been achieved through the BN method than the FT, which demonstrates that the BN is a superior technique in both reliability assessment and fault diagnosis.

Electronic structure of graphene- and BN-supported phosphorene

NASA Astrophysics Data System (ADS)

Davletshin, Artur R.; Ustiuzhanina, Svetlana V.; Kistanov, Andrey A.; Saadatmand, Danial; Dmitriev, Sergey V.; Zhou, Kun; Korznikova, Elena A.

2018-04-01

By using first-principles calculations, the effects of graphene and boron nitride (BN) substrates on the electronic properties of phosphorene are studied. Graphene-supported phosphorene is found to be metallic, while the BN-supported phosphorene is a semiconductor with a moderate band gap of 1.02 eV. Furthermore, the effects of the van der Waals interactions between the phosphorene and graphene or BN layers by means of the interlayer distance change are investigated. It is shown that the interlayer distance change leads to significant band gap size modulations and direct-indirect band gap transitions in the phosphorene-BN heterostructure. The presented band gap engineering of phosphorene may be a powerful technique for the fabrication of high-performance phosphorene-based nanodevices.

Exploring the effect of oxygen coverage on the electronic, magnetic and chemical properties of Ni(111) supported h-BN sheet: A density functional study

NASA Astrophysics Data System (ADS)

Wasey, A. H. M. Abdul; Das, G. P.; Majumder, C.

2017-05-01

Traditionally, h-BN is used as coating material to prevent corrosion on the metal surface. In sharp contrast to this, here we show catalytic behavior of h-BN monolayer deposited on Ni(111) surface, clearly demonstrating the influence of the support in modulation of h-BN electronic structure. Using first principles density functional theory we have studied the interaction of O2 molecules with the h-BN/Ni(111) surface. The activation of Osbnd O bond, which is the most important step for oxidative catalysis, showed dependence on the O2 coverage. Thus this study is extremely important to predict the optimum O2 pressure in reaction chamber for efficient catalysis.

Decoupled electron and phonon transports in hexagonal boron nitride-silicene bilayer heterostructure

DOE Office of Scientific and Technical Information (OSTI.GOV)

Cai, Yongqing; Pei, Qing-Xiang, E-mail: peiqx@ihpc.a-star.edu.sg, E-mail: zhangg@ihpc.a-star.edu.sg; Zhang, Gang, E-mail: peiqx@ihpc.a-star.edu.sg, E-mail: zhangg@ihpc.a-star.edu.sg

2016-02-14

Calculations based on the density functional theory and empirical molecular dynamics are performed to investigate interlayer interaction, electronic structure and thermal transport of a bilayer heterostructure consisting of silicene and hexagonal boron nitride (h-BN). In this heterostructure, the two layers are found to interact weakly via a non-covalent binding. As a result, the Dirac cone of silicene is preserved with the Dirac cone point being located exactly at the Fermi level, and only a small amount of electrons are transferred from h-BN to silicene, suggesting that silicene dominates the electronic transport. Molecular dynamics calculation results demonstrate that the heat currentmore » along h-BN is six times of that along silicene, suggesting that h-BN dominates the thermal transport. This decoupled role of h-BN and silicene in thermal and electronic transport suggests that the BN-silicene bilayer heterostructure is promising for thermoelectric applications.« less

A platform for large-scale graphene electronics--CVD growth of single-layer graphene on CVD-grown hexagonal boron nitride.

PubMed

Wang, Min; Jang, Sung Kyu; Jang, Won-Jun; Kim, Minwoo; Park, Seong-Yong; Kim, Sang-Woo; Kahng, Se-Jong; Choi, Jae-Young; Ruoff, Rodney S; Song, Young Jae; Lee, Sungjoo

2013-05-21

Direct chemical vapor deposition (CVD) growth of single-layer graphene on CVD-grown hexagonal boron nitride (h-BN) film can suggest a large-scale and high-quality graphene/h-BN film hybrid structure with a defect-free interface. This sequentially grown graphene/h-BN film shows better electronic properties than that of graphene/SiO2 or graphene transferred on h-BN film, and suggests a new promising template for graphene device fabrication. Copyright © 2013 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Is the diagnostic threshold for bulimia nervosa clinically meaningful?

PubMed

Chapa, Danielle A N; Bohrer, Brittany K; Forbush, Kelsie T

2018-01-01

The DSM-5 differentiates full- and sub-threshold bulimia nervosa (BN) according to average weekly frequencies of binge eating and inappropriate compensatory behaviors. This study was the first to evaluate the modified frequency criterion for BN published in the DSM-5. The purpose of this study was to test whether community-recruited adults (N=125; 83.2% women) with current full-threshold (n=77) or sub-threshold BN (n=48) differed in comorbid psychopathology and eating disorder (ED) illness duration, symptom severity, and clinical impairment. Participants completed the Clinical Impairment Assessment and participated in semi-structured clinical interviews of ED- and non-ED psychopathology. Differences between the sub- and full-threshold BN groups were assessed using MANOVA and Chi-square analyses. ED illness duration, age-of-onset, body mass index (BMI), alcohol and drug misuse, and the presence of current and lifetime mood or anxiety disorders did not differ between participants with sub- and full-threshold BN. Participants with full-threshold BN had higher levels of clinical impairment and weight concern than those with sub-threshold BN. However, minimal clinically important difference analyses suggested that statistically significant differences between participants with sub- and full-threshold BN on clinical impairment and weight concern were not clinically significant. In conclusion, sub-threshold BN did not differ from full-threshold BN in clinically meaningful ways. Future studies are needed to identify an improved frequency criterion for BN that better distinguishes individuals in ways that will more validly inform prognosis and effective treatment planning for BN. Copyright © 2017 Elsevier Ltd. All rights reserved.

Exceptionally large migration length of carbon and topographically-facilitated self-limiting molecular beam epitaxial growth of graphene on hexagonal boron nitride

DOE Office of Scientific and Technical Information (OSTI.GOV)

Plaut, Annette S.; Wurstbauer, Ulrich; Wang, Sheng

We demonstrate growth of single-layer graphene (SLG) on hexagonal boron nitride (h-BN) by molecular beam epitaxy (MBE), only limited in area by the finite size of the h-BN flakes. Using atomic force microscopy and micro-Raman spectroscopy, we show that for growth over a wide range of temperatures (500 °C – 1000 °C) the deposited carbon atoms spill off the edge of the h-BN flakes. We attribute this spillage to the very high mobility of the carbon atoms on the BN basal plane, consistent with van der Waals MBE. The h-BN flakes vary in size from 30 μm to 100 μm,more » thus demonstrating that the migration length of carbon atoms on h-BN is greater than 100 μm. When sufficient carbon is supplied to compensate for this loss, which is largely due to this fast migration of the carbon atoms to and off the edges of the h-BN flake, we find that the best growth temperature for MBE SLG on h-BN is ~950 °C. Self-limiting graphene growth appears to be facilitated by topographic h-BN surface features: We have thereby grown MBE self-limited SLG on an h-BN ridge. This opens up future avenues for precisely tailored fabrication of nano- and hetero-structures on pre-patterned h-BN surfaces for device applications.« less

Large-area growth of multi-layer hexagonal boron nitride on polished cobalt foils by plasma-assisted molecular beam epitaxy

PubMed Central

Xu, Zhongguang; Tian, Hao; Khanaki, Alireza; Zheng, Renjing; Suja, Mohammad; Liu, Jianlin

2017-01-01

Two-dimensional (2D) hexagonal boron nitride (h-BN), which has a similar honeycomb lattice structure to graphene, is promising as a dielectric material for a wide variety of potential applications based on 2D materials. Synthesis of high-quality, large-size and single-crystalline h-BN domains is of vital importance for fundamental research as well as practical applications. In this work, we report the growth of h-BN films on mechanically polished cobalt (Co) foils using plasma-assisted molecular beam epitaxy. Under appropriate growth conditions, the coverage of h-BN layers can be readily controlled by growth time. A large-area, multi-layer h-BN film with a thickness of 5~6 nm is confirmed by Raman spectroscopy, scanning electron microscopy, X-ray photoelectron spectroscopy and transmission electron microscopy. In addition, the size of h-BN single domains is 20~100 μm. Dielectric property of as-grown h-BN film is evaluated by characterization of Co(foil)/h-BN/Co(contact) capacitor devices. Breakdown electric field is in the range of 3.0~3.3 MV/cm, which indicates that the epitaxial h-BN film has good insulating characteristics. In addition, the effect of substrate morphology on h-BN growth is discussed regarding different domain density, lateral size, and thickness of the h-BN films grown on unpolished and polished Co foils. PMID:28230178

Theoretical analysis of nBn infrared photodetectors

NASA Astrophysics Data System (ADS)

Ting, David Z.; Soibel, Alexander; Khoshakhlagh, Arezou; Gunapala, Sarath D.

2017-09-01

The depletion and surface leakage dark current suppression properties of unipolar barrier device architectures such as the nBn have been highly beneficial for III-V semiconductor-based infrared detectors. Using a one-dimensional drift-diffusion model, we theoretically examine the effects of contact doping, minority carrier lifetime, and absorber doping on the dark current characteristics of nBn detectors to explore some basic aspects of their operation. We found that in a properly designed nBn detector with highly doped excluding contacts the minority carriers are extracted to nonequilibrium levels under reverse bias in the same manner as the high operating temperature (HOT) detector structure. Longer absorber Shockley-Read-Hall (SRH) lifetimes result in lower diffusion and depletion dark currents. Higher absorber doping can also lead to lower diffusion and depletion dark currents, but the benefit should be weighted against the possibility of reduced diffusion length due to shortened SRH lifetime. We also briefly examined nBn structures with unintended minority carrier blocking barriers due to excessive n-doping in the unipolar electron barrier, or due to a positive valence band offset between the barrier and the absorber. Both types of hole blocking structures lead to higher turn-on bias, although barrier n-doping could help suppress depletion dark current.

Investigation of structure and mechanical properties of plasma vapor deposited nanocomposite TiBN films

NASA Astrophysics Data System (ADS)

Han, Bin; Neena, D.; Wang, Zesong; Kondamareddy, K. k.; Li, Na; Zuo, Wenbin; Yan, Shaojian; Liu, Chuansheng; Fu, Dejun

2017-04-01

TiBN coatings have huge potential applications as they have excellent properties with increasing modern industrial requirements. Nanocomposite TiBN coatings were synthesized on cemented carbide, high speed steel and Si substrates by using cathodic arc plasma ion plating from pure TiB2 ceramic targets. The structure and mechanical properties of the TiBN coatings were significantly influenced by the nitrogen partial pressure. Rutherford backscattering spectrometry demonstrates that the nitrogen content of the coating varied from 2.8% to 34.5% and high-resolution electron microscopy images reveal that all coatings have the characteristic of nanocrystals embedded in an amorphous matrix. The root-mean-square roughness of the coatings increases from 3.73 to 14.64 nm and the coefficients of friction of the coatings at room temperature vary from 0.54 to 0.73 with increasing nitrogen partial pressure. The microhardness of the coating increases up to 35.7 GPa at 10 sccm N2 flow rate. The smallest wear rate is 2.65 × 10-15 m3 N-1 m-1 which indicates that TiBN coatings have excellent wear resistance. The adhesion test revealed that the TiBN coatings have good adhesion at low nitrogen partial pressure.

Electrophoretic Deposition of Chitosan/h-BN and Chitosan/h-BN/TiO₂ Composite Coatings on Stainless Steel (316L) Substrates.

PubMed

Raddaha, Namir S; Cordero-Arias, Luis; Cabanas-Polo, Sandra; Virtanen, Sannakaisa; Roether, Judith A; Boccaccini, Aldo R

2014-03-04

This article presents the results of an experimental investigation designed to deposit chitosan/hexagonal boron nitride (h-BN) and chitosan/h-BN/titania (TiO₂) composites on SS316L substrates using electrophoretic deposition (EPD) for potential antibacterial applications. The influence of EPD parameters (voltage and deposition time) and relative concentrations of chitosan, h-BN and TiO₂ in suspension on deposition yield was studied. The composition and structure of deposited coatings were investigated by FTIR, XRD and SEM. It was observed that h-BN and TiO₂ particles were dispersed in the chitosan matrix through simultaneous deposition. The adhesion between the electrophoretic coatings and the stainless steel substrates was tested by using tape test technique, and the results showed that the adhesion strength corresponded to 3B and 4B classes. Corrosion resistance was evaluated by electrochemical polarization curves, indicating enhanced corrosion resistance of the chitosan/h-BN/TiO₂ and chitosan/h-BN coatings compared to the bare stainless steel substrate. In order to investigate the in-vitro inorganic bioactivity, coatings were immersed in simulated body fluid (SBF) for 28 days. FTIR and XRD results showed no formation of hydroxyapatite on the surface of chitosan/h-BN/TiO₂ and chitosan/h-BN coatings, which are therefore non bioactive but potentially useful as antibacterial coatings.

Electrophoretic Deposition of Chitosan/h-BN and Chitosan/h-BN/TiO2 Composite Coatings on Stainless Steel (316L) Substrates

PubMed Central

Raddaha, Namir S.; Cordero-Arias, Luis; Cabanas-Polo, Sandra; Virtanen, Sannakaisa; Roether, Judith A.; Boccaccini, Aldo R.

2014-01-01

This article presents the results of an experimental investigation designed to deposit chitosan/hexagonal boron nitride (h-BN) and chitosan/h-BN/titania (TiO2) composites on SS316L substrates using electrophoretic deposition (EPD) for potential antibacterial applications. The influence of EPD parameters (voltage and deposition time) and relative concentrations of chitosan, h-BN and TiO2 in suspension on deposition yield was studied. The composition and structure of deposited coatings were investigated by FTIR, XRD and SEM. It was observed that h-BN and TiO2 particles were dispersed in the chitosan matrix through simultaneous deposition. The adhesion between the electrophoretic coatings and the stainless steel substrates was tested by using tape test technique, and the results showed that the adhesion strength corresponded to 3B and 4B classes. Corrosion resistance was evaluated by electrochemical polarization curves, indicating enhanced corrosion resistance of the chitosan/h-BN/TiO2 and chitosan/h-BN coatings compared to the bare stainless steel substrate. In order to investigate the in-vitro inorganic bioactivity, coatings were immersed in simulated body fluid (SBF) for 28 days. FTIR and XRD results showed no formation of hydroxyapatite on the surface of chitosan/h-BN/TiO2 and chitosan/h-BN coatings, which are therefore non bioactive but potentially useful as antibacterial coatings. PMID:28788541

Functional Identification and Characterization of the Brassica Napus Transcription Factor Gene BnAP2, the Ortholog of Arabidopsis Thaliana APETALA2

PubMed Central

Xiong, Zhiyong; Chen, Chunli; Wang, Lijun; Yu, Jingyin; Lu, Changming; Wei, Wenhui

2012-01-01

BnAP2, an APETALA2 (AP2)-like gene, has been isolated from Brassica napus cultivar Zhongshuang 9. The cDNA of BnAP2, with 1, 299 bp in length, encoded a transcription factor comprising of 432 amino acid residues. Results from complementary experiment indicated that BnAP2 was completely capable of restoring the phenotype of Arabidopsis ap2-11 mutant. Together with the sequence and expression data, the complementation data suggested that BnAP2 encodes the ortholog of AtAP2. To address the transcriptional activation of BnAP2, we performed transactivation assays in yeast. Fusion protein of BnAP2 with GAL4 DNA binding domain strongly activated transcription in yeast, and the transactivating activity of BnAP2 was localized to the N-terminal 100 amino acids. To further study the function of BnAP2 involved in the phenotype of B. napus, we used a transgenic approach that involved targeted RNA interference (RNAi) repression induced by ihp-RNA. Floral various phenotype defectives and reduced female fertility were observed in B. napus BnAP2-RNAi lines. Loss of the function of BnAP2 gene also resulted in delayed sepal abscission and senescence with the ethylene-independent pathway. In the strong BnAP2-RNAi lines, seeds showed defects in shape, structure and development and larger size. Strong BnAP2-RNAi and wild-type seeds initially did not display a significant difference in morphology at 10 DAF, but the development of BnAP2-RNAi seeds was slower than that of wild type at 20 DAF, and further at 30 DAF, wild-type seeds were essentially at their final size, whereas BnAP2-RNAi seeds stopped growing and developing and gradually withered. PMID:22479468

Functional identification and characterization of the Brassica napus transcription factor gene BnAP2, the ortholog of Arabidopsis thaliana APETALA2.

PubMed

Yan, Xiaohong; Zhang, Lei; Chen, Bo; Xiong, Zhiyong; Chen, Chunli; Wang, Lijun; Yu, Jingyin; Lu, Changming; Wei, Wenhui

2012-01-01

BnAP2, an APETALA2 (AP2)-like gene, has been isolated from Brassica napus cultivar Zhongshuang 9. The cDNA of BnAP2, with 1, 299 bp in length, encoded a transcription factor comprising of 432 amino acid residues. Results from complementary experiment indicated that BnAP2 was completely capable of restoring the phenotype of Arabidopsis ap2-11 mutant. Together with the sequence and expression data, the complementation data suggested that BnAP2 encodes the ortholog of AtAP2. To address the transcriptional activation of BnAP2, we performed transactivation assays in yeast. Fusion protein of BnAP2 with GAL4 DNA binding domain strongly activated transcription in yeast, and the transactivating activity of BnAP2 was localized to the N-terminal 100 amino acids. To further study the function of BnAP2 involved in the phenotype of B. napus, we used a transgenic approach that involved targeted RNA interference (RNAi) repression induced by ihp-RNA. Floral various phenotype defectives and reduced female fertility were observed in B. napus BnAP2-RNAi lines. Loss of the function of BnAP2 gene also resulted in delayed sepal abscission and senescence with the ethylene-independent pathway. In the strong BnAP2-RNAi lines, seeds showed defects in shape, structure and development and larger size. Strong BnAP2-RNAi and wild-type seeds initially did not display a significant difference in morphology at 10 DAF, but the development of BnAP2-RNAi seeds was slower than that of wild type at 20 DAF, and further at 30 DAF, wild-type seeds were essentially at their final size, whereas BnAP2-RNAi seeds stopped growing and developing and gradually withered.

Substitutional carbon doping of free-standing and Ru-supported BN sheets: a first-principles study

NASA Astrophysics Data System (ADS)

Berseneva, N.; Komsa, H.-P.; Vierimaa, V.; Björkman, T.; Fan, Z.; Harju, A.; Todorović, M.; Krasheninnikov, A. V.; Nieminen, R. M.

2017-10-01

The development of spatially homogeneous mixed structures with boron (B), nitrogen (N) and carbon (C) atoms arranged in a honeycomb lattice is highly desirable, as they open the possibility of creating stable two-dimensional materials with tunable band gaps. However, at least in the free-standing form, the mixed BCN system is energetically driven towards phase segregation to graphene and hexagonal BN. It is possible to overcome the segregation when BCN material is grown on a particular metal substrate, for example Ru(0 0 0 1), but the stabilization mechanism is still unknown. With the use of density-functional theory we study the energetics of BN/Ru slabs, with different types of configurations of C substitutional defects introduced to the h-BN overlayer. The results are compared to the energetics of free-standing BCN materials. We found that the substrate facilitates the C substitution process in the h-BN overlayer. Thus, more homogeneous BCN material can be grown, overcoming the segregation into graphene and h-BN. In addition, we investigate the electronic and transport gaps in free-standing BCN structures, and assess their mechanical properties and stability. The band gap in mixed BCN free-standing material depends on the concentration of the constituent elements and ranges from zero in pristine graphene to nearly 5 eV in free-standing h-BN. This makes BCN attractive for application in modern electronics.

CGBayesNets: Conditional Gaussian Bayesian Network Learning and Inference with Mixed Discrete and Continuous Data

PubMed Central

Weiss, Scott T.

2014-01-01

Bayesian Networks (BN) have been a popular predictive modeling formalism in bioinformatics, but their application in modern genomics has been slowed by an inability to cleanly handle domains with mixed discrete and continuous variables. Existing free BN software packages either discretize continuous variables, which can lead to information loss, or do not include inference routines, which makes prediction with the BN impossible. We present CGBayesNets, a BN package focused around prediction of a clinical phenotype from mixed discrete and continuous variables, which fills these gaps. CGBayesNets implements Bayesian likelihood and inference algorithms for the conditional Gaussian Bayesian network (CGBNs) formalism, one appropriate for predicting an outcome of interest from, e.g., multimodal genomic data. We provide four different network learning algorithms, each making a different tradeoff between computational cost and network likelihood. CGBayesNets provides a full suite of functions for model exploration and verification, including cross validation, bootstrapping, and AUC manipulation. We highlight several results obtained previously with CGBayesNets, including predictive models of wood properties from tree genomics, leukemia subtype classification from mixed genomic data, and robust prediction of intensive care unit mortality outcomes from metabolomic profiles. We also provide detailed example analysis on public metabolomic and gene expression datasets. CGBayesNets is implemented in MATLAB and available as MATLAB source code, under an Open Source license and anonymous download at http://www.cgbayesnets.com. PMID:24922310

CGBayesNets: conditional Gaussian Bayesian network learning and inference with mixed discrete and continuous data.

PubMed

McGeachie, Michael J; Chang, Hsun-Hsien; Weiss, Scott T

2014-06-01

Bayesian Networks (BN) have been a popular predictive modeling formalism in bioinformatics, but their application in modern genomics has been slowed by an inability to cleanly handle domains with mixed discrete and continuous variables. Existing free BN software packages either discretize continuous variables, which can lead to information loss, or do not include inference routines, which makes prediction with the BN impossible. We present CGBayesNets, a BN package focused around prediction of a clinical phenotype from mixed discrete and continuous variables, which fills these gaps. CGBayesNets implements Bayesian likelihood and inference algorithms for the conditional Gaussian Bayesian network (CGBNs) formalism, one appropriate for predicting an outcome of interest from, e.g., multimodal genomic data. We provide four different network learning algorithms, each making a different tradeoff between computational cost and network likelihood. CGBayesNets provides a full suite of functions for model exploration and verification, including cross validation, bootstrapping, and AUC manipulation. We highlight several results obtained previously with CGBayesNets, including predictive models of wood properties from tree genomics, leukemia subtype classification from mixed genomic data, and robust prediction of intensive care unit mortality outcomes from metabolomic profiles. We also provide detailed example analysis on public metabolomic and gene expression datasets. CGBayesNets is implemented in MATLAB and available as MATLAB source code, under an Open Source license and anonymous download at http://www.cgbayesnets.com.

Neutral line chaos and phase space structure

NASA Technical Reports Server (NTRS)

Burkhart, Grant R.; Speiser, Theodore W.; Martin, Richard F., Jr.; Dusenbery, Paul B.

1991-01-01

Phase space structure and chaos near a neutral line are studied with numerical surface-of-section (SOS) techniques and analytic methods. Results are presented for a linear neutral line model with zero crosstail electric field. It was found that particle motion can be divided into three regimes dependening on the value of the conserved canonical momentum, Py, and the conserved Hamiltonian, h. The phase space structure, using Poincare SOS plots, is highly sensitive to bn = Bn/B0 variations, but not to h variations. It is verified that the slow motion preserves the action, Jz, as evaluated by Sonnerup (1971), when the period of the fast motion is smaller than the time scale of the slow motion. Results show that the phase space structure and particle chaos depend sensitively upon Py and bn, but are independent of h.

Unipolar Barrier Dual-Band Infrared Detectors

NASA Technical Reports Server (NTRS)

Ting, David Z. (Inventor); Soibel, Alexander (Inventor); Khoshakhlagh, Arezou (Inventor); Gunapala, Sarath (Inventor)

2017-01-01

Dual-band barrier infrared detectors having structures configured to reduce spectral crosstalk between spectral bands and/or enhance quantum efficiency, and methods of their manufacture are provided. In particular, dual-band device structures are provided for constructing high-performance barrier infrared detectors having reduced crosstalk and/or enhance quantum efficiency using novel multi-segmented absorber regions. The novel absorber regions may comprise both p-type and n-type absorber sections. Utilizing such multi-segmented absorbers it is possible to construct any suitable barrier infrared detector having reduced crosstalk, including npBPN, nBPN, pBPN, npBN, npBP, pBN and nBP structures. The pBPN and pBN detector structures have high quantum efficiency and suppresses dark current, but has a smaller etch depth than conventional detectors and does not require a thick bottom contact layer.

Inter-layer potential for hexagonal boron nitride

NASA Astrophysics Data System (ADS)

Leven, Itai; Azuri, Ido; Kronik, Leeor; Hod, Oded

2014-03-01

A new interlayer force-field for layered hexagonal boron nitride (h-BN) based structures is presented. The force-field contains three terms representing the interlayer attraction due to dispersive interactions, repulsion due to anisotropic overlaps of electron clouds, and monopolar electrostatic interactions. With appropriate parameterization, the potential is able to simultaneously capture well the binding and lateral sliding energies of planar h-BN based dimer systems as well as the interlayer telescoping and rotation of double walled boron-nitride nanotubes of different crystallographic orientations. The new potential thus allows for the accurate and efficient modeling and simulation of large-scale h-BN based layered structures.

Hexagonal boron nitride intercalated multi-layer graphene: a possible ultimate solution to ultra-scaled interconnect technology

NASA Astrophysics Data System (ADS)

Li, Yong-Jun; Sun, Qing-Qing; Chen, Lin; Zhou, Peng; Wang, Peng-Fei; Ding, Shi-Jin; Zhang, David Wei

2012-03-01

We proposed intercalation of hexagonal boron nitride (hBN) in multilayer graphene to improve its performance in ultra-scaled interconnects for integrated circuit. The effect of intercalated hBN layer in bilayer graphene is investigated using non-equilibrium Green's functions. We find the hBN intercalated bilayer graphene exhibit enhanced transport properties compared with pristine bilayer ones, and the improvement is attributed to suppression of interlayer scattering and good planar bonding condition of inbetween hBN layer. Based on these results, we proposed a via structure that not only benefits from suppressed interlayer scattering between multilayer graphene, but also sustains the unique electrical properties of graphene when many graphene layers are stacking together. The ideal current density across the structure can be as high as 4.6×109 A/cm2 at 1V, which is very promising for the future high-performance interconnect.

Well-defined N-heterocyclic carbene silver halides of 1-cyclohexyl-3-arylmethylimidazolylidenes: synthesis, structure and catalysis in A3-reaction of aldehydes, amines and alkynes.

PubMed

Li, Yanbo; Chen, Xiaofeng; Song, Yin; Fang, Ling; Zou, Gang

2011-03-07

Structurally well-defined N-heterocyclic carbene silver chlorides and bromides supported by 1-cyclohexyl-3-benzylimidazolylidene (CyBn-NHC) or 1-cyclohexyl-3-naphthalen-2-ylmethylimidazolylidene (CyNaph-NHC) were synthesized by reaction of the corresponding imidazolium halides with silver(I) oxide while cationic bis(CyBn-NHC) silver nitrate was isolated under similar conditions using imidazolium iodide in the presence of sodium nitrate. Single-crystal X-ray diffraction revealed a dimeric structure through a nonpolar weak-hydrogen-bond supported Ag-Ag bond for 1-cyclohexyl-3-benzylimidazolylidene silver halides [(CyBn-NHC)AgX](2) (X = Cl, 1; Br, 2) but a monomeric structure for N-heterocyclic carbene silver halides with the more sterically demanding 1-cyclohexyl-3-naphthalen-2-ylmethylimidazolylidene ligand (CyNaph-NHC)AgX (X = Cl, 4; Br, 5). Cationic biscarbene silver nitrate [(CyBn-NHC)(2)Ag](+)NO(3)(-)3 assumed a cis orientation with respect to the two carbene ligands. The monomeric complexes (CyNaph-NHC)AgX 4 and 5 showed higher catalytic activity than the dimeric [(CyBn-NHC)AgX](2)1 and 2 as well as the cationic biscarbene silver nitrate 3 in the model three component reaction of 3-phenylpropionaldehyde, phenylacetylene and piperidine with chloride 4 performing best and giving product in almost quantitative yield within 2 h at 100 °C. An explanation for the structure-activity relationship in N-heterocyclic carbene silver halide catalyzed three component reaction is given based on a slightly modified mechanism from the one in literature.

Near-field heat transfer between graphene/hBN multilayers

NASA Astrophysics Data System (ADS)

Zhao, Bo; Guizal, Brahim; Zhang, Zhuomin M.; Fan, Shanhui; Antezza, Mauro

2017-06-01

We study the radiative heat transfer between multilayer structures made by a periodic repetition of a graphene sheet and a hexagonal boron nitride (hBN) slab. Surface plasmons in a monolayer graphene can couple with hyperbolic phonon polaritons in a single hBN film to form hybrid polaritons that can assist photon tunneling. For periodic multilayer graphene/hBN structures, the stacked metallic/dielectric array can give rise to a further effective hyperbolic behavior, in addition to the intrinsic natural hyperbolic behavior of hBN. The effective hyperbolicity can enable more hyperbolic polaritons that enhance the photon tunneling and hence the near-field heat transfer. However, the hybrid polaritons on the surface, i.e., surface plasmon-phonon polaritons, dominate the near-field heat transfer between multilayer structures when the topmost layer is graphene. The effective hyperbolic regions can be well predicted by the effective medium theory (EMT), thought EMT fails to capture the hybrid surface polaritons and results in a heat transfer rate much lower compared to the exact calculation. The chemical potential of the graphene sheets can be tuned through electrical gating and results in an additional modulation of the heat transfer. We found that the near-field heat transfer between multilayer structures does not increase monotonously with the number of layers in the stack, which provides a way to control the heat transfer rate by the number of graphene layers in the multilayer structure. The results may benefit the applications of near-field energy harvesting and radiative cooling based on hybrid polaritons in two-dimensional materials.

Activation of CO and CO2 on homonuclear boron bonds of fullerene-like BN cages: first principles study

NASA Astrophysics Data System (ADS)

Sinthika, S.; Kumar, E. Mathan; Surya, V. J.; Kawazoe, Y.; Park, Noejung; Iyakutti, K.; Thapa, Ranjit

2015-12-01

Using density functional theory we investigate the electronic and atomic structure of fullerene-like boron nitride cage structures. The pentagonal ring leads to the formation of homonuclear bonds. The homonuclear bonds are also found in other BN structures having pentagon line defect. The calculated thermodynamics and vibrational spectra indicated that, among various stable configurations of BN-60 cages, the higher number of homonuclear N-N bonds and lower B:N ratio can result in the more stable structure. The homonuclear bonds bestow the system with salient catalytic properties that can be tuned by modifying the B atom bonding environment. We show that homonuclear B-B (B2) bonds can anchor both oxygen and CO molecules making the cage to be potential candidates as catalyst for CO oxidation via Langmuir-Hinshelwood (LH) mechanism. Moreover, the B-B-B (B3) bonds are reactive enough to capture, activate and hydrogenate CO2 molecules to formic acid. The observed trend in reactivity, viz B3 > B2 > B1 is explained in terms of the position of the boron defect state relative to the Fermi level.

Activation of CO and CO2 on homonuclear boron bonds of fullerene-like BN cages: first principles study

PubMed Central

Sinthika, S.; Kumar, E. Mathan; Surya, V. J.; Kawazoe, Y.; Park, Noejung; Iyakutti, K.; Thapa, Ranjit

2015-01-01

Using density functional theory we investigate the electronic and atomic structure of fullerene-like boron nitride cage structures. The pentagonal ring leads to the formation of homonuclear bonds. The homonuclear bonds are also found in other BN structures having pentagon line defect. The calculated thermodynamics and vibrational spectra indicated that, among various stable configurations of BN-60 cages, the higher number of homonuclear N-N bonds and lower B:N ratio can result in the more stable structure. The homonuclear bonds bestow the system with salient catalytic properties that can be tuned by modifying the B atom bonding environment. We show that homonuclear B-B (B2) bonds can anchor both oxygen and CO molecules making the cage to be potential candidates as catalyst for CO oxidation via Langmuir–Hinshelwood (LH) mechanism. Moreover, the B-B-B (B3) bonds are reactive enough to capture, activate and hydrogenate CO2 molecules to formic acid. The observed trend in reactivity, viz B3 > B2 > B1 is explained in terms of the position of the boron defect state relative to the Fermi level. PMID:26626147

Activation of CO and CO2 on homonuclear boron bonds of fullerene-like BN cages: first principles study.

PubMed

Sinthika, S; Kumar, E Mathan; Surya, V J; Kawazoe, Y; Park, Noejung; Iyakutti, K; Thapa, Ranjit

2015-12-02

Using density functional theory we investigate the electronic and atomic structure of fullerene-like boron nitride cage structures. The pentagonal ring leads to the formation of homonuclear bonds. The homonuclear bonds are also found in other BN structures having pentagon line defect. The calculated thermodynamics and vibrational spectra indicated that, among various stable configurations of BN-60 cages, the higher number of homonuclear N-N bonds and lower B:N ratio can result in the more stable structure. The homonuclear bonds bestow the system with salient catalytic properties that can be tuned by modifying the B atom bonding environment. We show that homonuclear B-B (B2) bonds can anchor both oxygen and CO molecules making the cage to be potential candidates as catalyst for CO oxidation via Langmuir-Hinshelwood (LH) mechanism. Moreover, the B-B-B (B3) bonds are reactive enough to capture, activate and hydrogenate CO2 molecules to formic acid. The observed trend in reactivity, viz B3 > B2 > B1 is explained in terms of the position of the boron defect state relative to the Fermi level.

Peptide-modified liposomes for selective targeting of bombesin receptors overexpressed by cancer cells: a potential theranostic agent

PubMed Central

Accardo, Antonella; Salsano, Giuseppina; Morisco, Anna; Aurilio, Michela; Parisi, Antonio; Maione, Francesco; Cicala, Carla; Tesauro, Diego; Aloj, Luigi; De Rosa, Giuseppe; Morelli, Giancarlo

2012-01-01

Objectives Drug delivery systems consisting of liposomes displaying a cell surface receptor-targeting peptide are being developed to specifically deliver chemotherapeutic drugs to tumors overexpressing a target receptor. This study addresses novel liposome composition approaches to specifically target tissues overexpressing bombesin (BN) receptors. Methods A new amphiphilic peptide derivative (MonY-BN) containing the BN(7–14) peptide, the DTPA (diethylenetriaminepentaacetate) chelating agent, a hydrophobic moiety with two C18 alkyl chains, and polyethylene glycol spacers, has been synthesized by solid-phase methods. Liposomes have been generated by co-aggregation of MonY-BN with 1,2-distearoyl-sn-glycero-3-phosphocholine (DSPC). The structural and biological properties of these new target-selective drug-delivery systems have been characterized. Results Liposomes with a DSPC/MonY-BN (97/3 molar ratio) composition showed a diameter of 145.5 ± 31.5 nm and a polydispersity index of 0.20 ± 0.05. High doxorubicin (Dox) loading was obtained with the remote pH gradient method using citrate as the inner buffer. Specific binding to PC-3 cells of DSPC/MonY-BN liposomes was obtained (2.7% ± 0.3%, at 37°C), compared with peptide-free DSPC liposomes (1.4% ± 0.2% at 37°C). Incubation of cells with DSPC/ MonY-BN/Dox showed significantly lower cell survival compared with DSPC/Dox-treated cells, in the presence of 100 ng/mL and 300 ng/mL drug amounts, in cytotoxicity experiments. Intravenous treatment of PC-3 xenograft-bearing mice with DSPC/MonY-BN/Dox at 10 mg/kg Dox dose produced higher tumour growth inhibition (60%) compared with nonspecific DSPC/ Dox liposomes (36%) relative to control animals. Conclusion The structural and loading properties of DSPC/MonY-BN liposomes along with the observed in-vitro and in-vivo activity are encouraging for further development of this approach for target-specific cancer chemotherapy. PMID:22619538

Synthesis and Characterization of Quenched and Crystalline Phases: Q-Carbon, Q-BN, Diamond and Phase-Pure c-BN

NASA Astrophysics Data System (ADS)

Bhaumik, Anagh; Narayan, Jagdish

2018-04-01

We report the synthesis and characterization of quenched (Q-carbon and Q-BN) and crystalline (diamond and c-BN) phases using a non-equilibrium technique. These phases are formed as a result of the melting and subsequent quenching of amorphous carbon and nanocrystalline h-BN in a super undercooled state by using high-power nanosecond laser pulses. Pulsed laser annealing also leads to the formation of nanoneedles, microneedles and single-crystal thin films of diamond and c-BN. This formation is dependent on the nucleation and growth times, which are controlled by laser energy density and thermal conductivities of substrate and as-deposited thin film. The diamond nuclei present in the Q-carbon structure ( 80% sp 3) can also be grown to larger sizes using the equilibrium hot filament chemical vapor deposition process. The texture of diamond and c-BN crystals is <111> under epitaxial growth and <110> under rapid unseeded crystallization. Our nanosecond laser processing opens up a roadmap to the fabrication of novel phases on heat-sensitive substrates.

Inhibition of serotonin release by bombesin-like peptides in rat hypothalamus in vitro.

PubMed

Saporito, M S; Warwick, R O

1989-01-01

We investigated the activity of bombesin (BN), neuromedin-C (NM-C) and neuromedin-B (NM-B) on serotonin (5-HT) release and reuptake in rat hypothalamus (HYP) in vitro. BN and NM-C but not NM-B (all 1 microM) decreased K+ evoked 3H-5-HT release from superfused HYP slices by 25%. Bacitracin (BCN, 2 micrograms/ml), a nonspecific peptidase inhibitor, reversed the inhibitory effect of BN on K+ evoked 3H-5-HT release. Phosphoramidon (PAN, 10 microM) an endopeptidase 24.11 inhibitor, abolished the inhibitory effect of BN, but not NM-C, on K+ evoked 3H-5-HT release. The peptidyl dipeptidase A inhibitor enalaprilat (ENP, 10 microM), enhanced both BN and NM-C inhibition of 3H-5-HT release. Bestatin (BST, 10 microM) had no effect on BN or NM-C inhibitory activity on 3H-5-HT release. Neither BN, NM-C nor NM-B affected reuptake of 3H-5-HT into HYP synaptosomes alone or in combination with any of the peptidase inhibitors, nor did these peptides alter the ability of fluoxetine to inhibit 3H-5-HT uptake. These data suggest: a) that BN-like peptides may alter neurotransmission in the HYP by acting presynaptically on the 5-HT release mechanism; b) a similarity in the structural requirements for the BN induced inhibition of 5-HT release and BN evoked thermoregulatory disturbances; and c) that peptidases may selectively augment or reduce pharmacologic activity of BN-like peptides upon CNS administration.

Formation of graphene on BN substrate by vapor deposition method and size effects on its structure

NASA Astrophysics Data System (ADS)

Giang, Nguyen Hoang; Hanh, Tran Thi Thu; Ngoc, Le Nhu; Nga, Nguyen To; Van Hoang, Vo

2018-04-01

We report MD simulation of the growth of graphene by the vapor deposition on a two-dimensional hBN substrate. The systems (containing carbon vapor and hBN substrate) are relaxed at high temperature (1500 K), and then it is cooled down to room one (300 K). Carbon atoms interact with the substrate via the Lennard-Jones potential while the interaction between carbon atoms is computed via the Tersoff potential. Depending on the size of the model, different crystalline honeycomb structures have been found. Structural properties of the graphene obtained at 300 K are studied by analyzing radial distribution functions (RDFs), coordination numbers, ring statistics, interatomic distances, bond-angle distributions and 2D visualization of atomic configurations. We find that the models containing various numbers of atoms have a honeycomb structure. Besides, differences in structural properties of graphene formed by the vapor deposition on the substrate and free standing one are found. Moreover, the size effect on the structure is significant.

A comparative DFT study on the interaction of cathinone drug with BN nanotubes, nanocages, and nanosheets

NASA Astrophysics Data System (ADS)

Nejati, Kamellia; Hosseinian, Akram; Vessally, Esmail; Bekhradnia, Ahmadreza; Edjlali, Ladan

2017-11-01

Cathinone is an organic stimulant which is classified as psychoactive drug and its abuse has been linked to many deaths worldwide. Here, we studied the electronic sensitivity of a BN cage, a zigzag (6, 0) BN nanotube, and a BN nanosheet toward cathinone using density functional theory calculations. The B3LYP-D functional predicts that the order of magnitude of electrical conductivity of BN nanostructures is as follows tube > sheet > cage. The cathinone drug prefers to be adsorbed on the BN nanostructures via its sbnd NH2 group rather than O-head with adsorption energy about -16.1, -14.0 and -5.0 kcal/mol for cage, tube, and sheet, respectively. Our results indicate that by increasing the p-character of the hybridization of the adsorbing B atom in the BN nanostructures, the interaction is strengthened. Based on the density of states analysis, it was demonstrated that the electrical conductivity of the BN nanostructures is decreased by the drug adsorption, indicating that they can be used in the cathinone sensors. The order of magnitude of the sensitivity is as follows: SCage > STube > SSheet. This trend corresponds to the decrease of the structural curvature in the BN nanostructures. Finally, a short recovery time of about 0.54 s, 0.02 s and 4.4 ns is predicted for cage, tube and sheet, respectively, at 298 K.

Epitaxial hexagonal boron nitride on Ir(111): A work function template

NASA Astrophysics Data System (ADS)

Schulz, Fabian; Drost, Robert; Hämäläinen, Sampsa K.; Demonchaux, Thomas; Seitsonen, Ari P.; Liljeroth, Peter

2014-06-01

Hexagonal boron nitride (h-BN) is a prominent member in the growing family of two-dimensional materials with potential applications ranging from being an atomically smooth support for other two-dimensional materials to templating growth of molecular layers. We have studied the structure of monolayer h-BN grown by chemical vapor deposition on Ir(111) by low-temperature scanning tunneling microscopy (STM) and spectroscopy (STS) experiments and state-of-the-art density functional theory (DFT) calculations. The lattice mismatch between the h-BN and Ir(111) surface results in the formation of a moiré superstructure with a periodicity of ˜29 Å and a corrugation of ˜0.4 Å. By measuring the field emission resonances above the h-BN layer, we find a modulation of the work function within the moiré unit cell of ˜0.5 eV. DFT simulations for a 13-on-12 h-BN/Ir(111) unit cell confirm our experimental findings and allow us to relate the change in the work function to the subtle changes in the interaction between boron and nitrogen atoms and the underlying substrate atoms within the moiré unit cell. Hexagonal boron nitride on Ir(111) combines weak topographic corrugation with a strong work function modulation over the moiré unit cell. This makes h-BN/Ir(111) a potential substrate for electronically modulated thin film and heterosandwich structures.

HIV-1 broadly neutralizing antibody precursor B cells revealed by germline-targeting immunogen

DOE PAGES

Jardine, Joseph G.; Kulp, Daniel W.; Havenar-Daughton, Colin; ...

2016-03-25

Induction of broadly neutralizing antibodies (bnAbs) is a major HIV vaccine goal. Germline-targeting immunogens aim to initiate bnAb induction by activating bnAb germline precursor B cells. Critical unmet challenges are to determine whether bnAb precursor naïve B cells bind germline-targeting immunogens and occur at sufficient frequency in humans for reliable vaccine responses. We employed deep mutational scanning and multi-target optimization to develop a germline-targeting immunogen (eOD-GT8) for diverse VRC01-class bnAbs. We then used the immunogen to isolate VRC01-class precursor naïve B cells from HIV-uninfected donors. Frequencies of true VRC01-class precursors, their structures, and their eOD-GT8 affinities support this immunogen asmore » a candidate human vaccine prime. Lastly, these methods could be applied to germline targeting for other classes of HIV bnAbs and for Abs to other pathogens.« less

In-plane heterostructures of graphene and hexagonal boron nitride with controlled domain sizes

NASA Astrophysics Data System (ADS)

Liu, Zheng; Ma, Lulu; Shi, Gang; Zhou, Wu; Gong, Yongji; Lei, Sidong; Yang, Xuebei; Zhang, Jiangnan; Yu, Jingjiang; Hackenberg, Ken P.; Babakhani, Aydin; Idrobo, Juan-Carlos; Vajtai, Robert; Lou, Jun; Ajayan, Pulickel M.

2013-02-01

Graphene and hexagonal boron nitride (h-BN) have similar crystal structures with a lattice constant difference of only 2%. However, graphene is a zero-bandgap semiconductor with remarkably high carrier mobility at room temperature, whereas an atomically thin layer of h-BN is a dielectric with a wide bandgap of ~5.9 eV. Accordingly, if precise two-dimensional domains of graphene and h-BN can be seamlessly stitched together, hybrid atomic layers with interesting electronic applications could be created. Here, we show that planar graphene/h-BN heterostructures can be formed by growing graphene in lithographically patterned h-BN atomic layers. Our approach can create periodic arrangements of domains with size ranging from tens of nanometres to millimetres. The resulting graphene/h-BN atomic layers can be peeled off the growth substrate and transferred to various platforms including flexible substrates. We also show that the technique can be used to fabricate two-dimensional devices, such as a split closed-loop resonator that works as a bandpass filter.

Multifunctional cyanate ester nanocomposites reinforced by hexagonal boron nitride after noncovalent biomimetic functionalization.

PubMed

Wu, Hongchao; Kessler, Michael R

2015-03-18

Boron nitride (BN) reinforced polymer nanocomposites have attracted a growing research interest in the microelectronic industry for their uniquely thermal conductive but electrical insulating properties. To overcome the challenges in surface functionalization, in this study, hexagonal boron nitride (h-BN) nanoparticles were noncovalently modified with polydopamine in a solvent-free aqueous condition. The strong π-π interaction between the hexagonal structural BN and aromatic dopamine molecules facilitated 15 wt % polydopamine encapsulating the nanoparticles. High-performance bisphenol E cyanate ester (BECy) was incorporated by homogeneously dispersed h-BN at different loadings and functionalities to investigate their effects on thermo-mechanical, dynamic-mechanical, and dielectric properties, as well as thermal conductivity. Different theoretical and empirical models were successfully applied to predict thermal and dielectric properties of h-BN/BECy nanocomposites. Overall, the prepared h-BN/BECy nanocomposites exhibited outstanding performance in dimensional stability, dynamic-mechanical properties, and thermal conductivity, together with the controllable dielectric property and preserved thermal stability for high-temperature applications.

Effect of substrate temperature and gas flow ratio on the nanocomposite TiAlBN coating

NASA Astrophysics Data System (ADS)

Rosli, Z. M.; Kwan, W. L.; Juoi, J. M.

2016-07-01

Nanocomposite TiAlBN (nc-TiAlBN) coatings were successfully deposited via RF magnetron sputtering by varying the nitrogen-to-total gas flow ratio (RN), and substrate temperature (TS). All coatings were deposited on AISI 316 substrates using single Ti-Al-BN hot-pressed disc as a target. The grain size, phases, and chemical composition of the coatings were evaluated using glancing angle X-ray diffraction analysis (GAXRD) and X-ray photoelectron spectroscopy (XPS). Results showed that the grains size of the deposited nc-TiAlBN coatings were in the range of 3.5 to 5.7 nm and reached a nitride saturation state as early as 15 % RN. As the nitrogen concentration decreases, boron concentration increased from 9 at.% to 16.17 at.%. and thus, increase the TiB2 phase within the coatings. The TS, however, showed no significant effect either on the crystallographic structure, grain size, or in the chemical composition of the deposited nc-TiAlBN coating.

HIV-1 broadly neutralizing antibody precursor B cells revealed by germline-targeting immunogen

DOE Office of Scientific and Technical Information (OSTI.GOV)

Jardine, Joseph G.; Kulp, Daniel W.; Havenar-Daughton, Colin

Induction of broadly neutralizing antibodies (bnAbs) is a major HIV vaccine goal. Germline-targeting immunogens aim to initiate bnAb induction by activating bnAb germline precursor B cells. Critical unmet challenges are to determine whether bnAb precursor naïve B cells bind germline-targeting immunogens and occur at sufficient frequency in humans for reliable vaccine responses. We employed deep mutational scanning and multi-target optimization to develop a germline-targeting immunogen (eOD-GT8) for diverse VRC01-class bnAbs. We then used the immunogen to isolate VRC01-class precursor naïve B cells from HIV-uninfected donors. Frequencies of true VRC01-class precursors, their structures, and their eOD-GT8 affinities support this immunogen asmore » a candidate human vaccine prime. Lastly, these methods could be applied to germline targeting for other classes of HIV bnAbs and for Abs to other pathogens.« less

HIV-1 broadly neutralizing antibody precursor B cells revealed by germline-targeting immunogen.

PubMed

Jardine, Joseph G; Kulp, Daniel W; Havenar-Daughton, Colin; Sarkar, Anita; Briney, Bryan; Sok, Devin; Sesterhenn, Fabian; Ereño-Orbea, June; Kalyuzhniy, Oleksandr; Deresa, Isaiah; Hu, Xiaozhen; Spencer, Skye; Jones, Meaghan; Georgeson, Erik; Adachi, Yumiko; Kubitz, Michael; deCamp, Allan C; Julien, Jean-Philippe; Wilson, Ian A; Burton, Dennis R; Crotty, Shane; Schief, William R

2016-03-25

Induction of broadly neutralizing antibodies (bnAbs) is a major HIV vaccine goal. Germline-targeting immunogens aim to initiate bnAb induction by activating bnAb germline precursor B cells. Critical unmet challenges are to determine whether bnAb precursor naïve B cells bind germline-targeting immunogens and occur at sufficient frequency in humans for reliable vaccine responses. Using deep mutational scanning and multitarget optimization, we developed a germline-targeting immunogen (eOD-GT8) for diverse VRC01-class bnAbs. We then used the immunogen to isolate VRC01-class precursor naïve B cells from HIV-uninfected donors. Frequencies of true VRC01-class precursors, their structures, and their eOD-GT8 affinities support this immunogen as a candidate human vaccine prime. These methods could be applied to germline targeting for other classes of HIV bnAbs and for Abs to other pathogens. Copyright © 2016, American Association for the Advancement of Science.

Tunable and Memory Metamaterials

DTIC Science & Technology

2015-12-02

THz beams [APL   102,   224103   (2013)]. In 2014 our group reported for the first time an observation of propagating phonon polaritons in a...Finally, we have fabricated hybrid graphene/hBN structures and proposed a new concept of a van der Walls polaritonic metamaterial. In these...structures plasmon polaritons of graphene hybridize with phonon polaritons of hBN. The hybrid polaritons DISTRIBUTION A: Distribution approved for public

The Structure and Stability of Bn(+) Clusters

NASA Technical Reports Server (NTRS)

Ricca, Alessandra; Bauschlicher, Charles W., Jr.; Langhoff, Stephen R. (Technical Monitor)

1995-01-01

The geometries of B+n clusters for n less than 14 have been optimized using density functional theory with the B3LYP functional. The most stable structure for each cluster is planar or quasi-planar. The B3LYP fragmentation energies are calibrated using coupled cluster theory. Overall, our corrected fragmentation energies are in reasonable agreement with experiment. Our results are compared with previous theoretical results.

Molecular level assessment of thermal transport and thermoelectricity in materials: From bulk alloys to nanostructures

NASA Astrophysics Data System (ADS)

Kinaci, Alper

The ability to manipulate material response to dynamical processes depends on the extent of understanding of transport properties and their variation with chemical and structural features in materials. In this perspective, current work focuses on the thermal and electronic transport behavior of technologically important bulk and nanomaterials. Strontium titanate is a potential thermoelectric material due to its large Seebeck coefficient. Here, first principles electronic band structure and Boltzmann transport calculations are employed in studying the thermoelectric properties of this material in doped and deformed states. The calculations verified that excessive carrier concentrations are needed for this material to be used in thermoelectric applications. Carbon- and boron nitride-based nanomaterials also offer new opportunities in many applications from thermoelectrics to fast heat removers. For these materials, molecular dynamics calculations are used to evaluate lattice thermal transport. To do this, first, an energy moment term is reformulated for periodic boundary conditions and tested to calculate thermal conductivity from Einstein relation in various systems. The influences of the structural details (size, dimensionality) and defects (vacancies, Stone-Wales defects, edge roughness, isotopic disorder) on the thermal conductivity of C and BN nanostructures are explored. It is observed that single vacancies scatter phonons stronger than other type of defects due to unsatisfied bonds in their structure. In pristine states, BN nanostructures have 4-6 times lower thermal conductivity compared to C counterparts. The reason of this observation is investigated on the basis of phonon group velocities, life times and heat capacities. The calculations show that both phonon group velocities and life times are smaller in BN systems. Quantum corrections are also discussed for these classical simulations. The chemical and structural diversity that could be attained by mixing hexagonal boron nitride and graphene provide further avenues for tuning thermal and electronic properties. In this work, the thermal conductivity of hybrid graphene/hexagonal-BN structures: stripe superlattices and BN (graphene) dots embedded in graphene (BN) are studied. The largest reduction in thermal conductivity is observed at 50% chemical mixture in dot superlattices. The dot radius appears to have little effect on the magnitude of reduction around large concentrations while smaller dots are more influential at dilute systems.

Development of a Probabilistic Decision-Support Model to Forecast Coastal Resilience

NASA Astrophysics Data System (ADS)

Wilson, K.; Safak, I.; Brenner, O.; Lentz, E. E.; Hapke, C. J.

2016-02-01

Site-specific forecasts of coastal change are a valuable management tool in preparing for and assessing storm-driven impacts in coastal areas. More specifically, understanding the likelihood of storm impacts, recovery following events, and the alongshore variability of both is central in evaluating vulnerability and resiliency of barrier islands. We introduce a probabilistic modeling framework that integrates hydrodynamic, anthropogenic, and morphologic components of the barrier system to evaluate coastal change at Fire Island, New York. The model is structured on a Bayesian network (BN), which utilizes observations to learn statistical relationships between system variables. In addition to predictive ability, probabilistic models convey the level of confidence associated with a prediction, an important consideration for coastal managers. Our model predicts the likelihood of morphologic change on the upper beach based on several decades of beach monitoring data. A coupled hydrodynamic BN combines probabilistic and deterministic modeling approaches; by querying nearly two decades of nested-grid wave simulations that account for both distant swells and local seas, we produce scenarios of event and seasonal wave climates. The wave scenarios of total water level - a sum of run up, surge and tide - and anthropogenic modification are the primary drivers of morphologic change in our model structure. Preliminary results show the hydrodynamic BN is able to reproduce time series of total water levels, a critical validation process before generating scenarios, and forecasts of geomorphic change over three month intervals are up to 70% accurate. Predictions of storm-induced change and recovery are linked to evaluate zones of persistent vulnerability or resilience and will help managers target restoration efforts, identify areas most vulnerable to habitat degradation, and highlight resilient zones that may best support relocation of critical infrastructure.

Review—hexagonal boron nitride epilayers: Growth, optical properties and device applications

DOE PAGES

Jiang, H. X.; Lin, Jing Yu

2016-09-07

This paper provides a brief overview on recent advances made in authors’ laboratory in epitaxial growth and optical studies of hexagonal boron nitride (h-BN) epilayers and heterostructures. Photoluminescence spectroscopy has been employed to probe the optical properties of h-BN. It was observed that the near band edge emission of h-BN is unusually high and is more than two orders of magnitude higher than that of high quality AlN epilayers. It was shown that the unique quasi-2D nature induced by the layered structure of h-BN results in high optical absorption and emission. The impurity related and near band-edge transitions in h-BNmore » epilayers were probed for materials synthesized under varying ammonia flow rates. Our results have identified that the most dominant impurities and deep level defects in h-BN epilayers are related to nitrogen vacancies. By growing h-BN under high ammonia flow rates, nitrogen vacancy related defects can be eliminated and epilayers exhibiting pure free exciton emission have been obtained. Deep UV and thermal neutron detectors based on h-BN epilayers were shown to possess unique features. Lastly, it is our belief that h-BN will lead to many potential applications from deep UV emitters and detectors, radiation detectors, to novel 2D photonic and electronic devices.« less

Review—hexagonal boron nitride epilayers: Growth, optical properties and device applications

DOE Office of Scientific and Technical Information (OSTI.GOV)

Jiang, H. X.; Lin, Jing Yu

This paper provides a brief overview on recent advances made in authors’ laboratory in epitaxial growth and optical studies of hexagonal boron nitride (h-BN) epilayers and heterostructures. Photoluminescence spectroscopy has been employed to probe the optical properties of h-BN. It was observed that the near band edge emission of h-BN is unusually high and is more than two orders of magnitude higher than that of high quality AlN epilayers. It was shown that the unique quasi-2D nature induced by the layered structure of h-BN results in high optical absorption and emission. The impurity related and near band-edge transitions in h-BNmore » epilayers were probed for materials synthesized under varying ammonia flow rates. Our results have identified that the most dominant impurities and deep level defects in h-BN epilayers are related to nitrogen vacancies. By growing h-BN under high ammonia flow rates, nitrogen vacancy related defects can be eliminated and epilayers exhibiting pure free exciton emission have been obtained. Deep UV and thermal neutron detectors based on h-BN epilayers were shown to possess unique features. Lastly, it is our belief that h-BN will lead to many potential applications from deep UV emitters and detectors, radiation detectors, to novel 2D photonic and electronic devices.« less

Self-Assembly of Porous Boron Nitride Microfibers into Ultralight Multifunctional Foams of Large Sizes.

PubMed

Lin, Jing; Yuan, Xiaohai; Li, Gen; Huang, Yang; Wang, Weijia; He, Xin; Yu, Chao; Fang, Yi; Liu, Zhenya; Tang, Chengchun

2017-12-27

As a kind of macroscopic boron nitride (BN) architectures, ultralight BN cellular materials with high porosity and great resilience would have a broad range of applications in energy and environment areas. However, creating such BN cellular materials in large sizes has still been proven challenging. Here, we report on the unique self-assembly of one-dimensional porous BN microfibers into an integral three-dimensional BN foam with open-cell cellular architectures. An ultrasonic-assisted self-assembly, freeze-drying, and high-temperature pyrolysis process has been developed for the preparation of cellular BN foam with a large size and desired shape. The developed BN foam has low density, high porosity (∼99.3%), great resilience, and excellent hydrophobic-lipophilic nature. The foam also exhibits excellent absorption capacities for a wide range of organic solvents and oils (wt % of ∼5130-7820%), as well as a high recovery efficiency (∼94%). Moreover, the unique hierarchical porous structure enables the foam to demonstrate a very low thermal conductivity (∼0.035 W/K/m). The excellent thermal insulation performance, superior mechanical property, and superb chemical and thermal stability enable the developed BN foam as an integrating multifunctional material in a broad range of high-end applications.

From complex questionnaire and interviewing data to intelligent Bayesian Network models for medical decision support

PubMed Central

Constantinou, Anthony Costa; Fenton, Norman; Marsh, William; Radlinski, Lukasz

2016-01-01

Objectives 1) To develop a rigorous and repeatable method for building effective Bayesian network (BN) models for medical decision support from complex, unstructured and incomplete patient questionnaires and interviews that inevitably contain examples of repetitive, redundant and contradictory responses; 2) To exploit expert knowledge in the BN development since further data acquisition is usually not possible; 3) To ensure the BN model can be used for interventional analysis; 4) To demonstrate why using data alone to learn the model structure and parameters is often unsatisfactory even when extensive data is available. Method The method is based on applying a range of recent BN developments targeted at helping experts build BNs given limited data. While most of the components of the method are based on established work, its novelty is that it provides a rigorous consolidated and generalised framework that addresses the whole life-cycle of BN model development. The method is based on two original and recent validated BN models in forensic psychiatry, known as DSVM-MSS and DSVM-P. Results When employed with the same datasets, the DSVM-MSS demonstrated competitive to superior predictive performance (AUC scores 0.708 and 0.797) against the state-of-the-art (AUC scores ranging from 0.527 to 0.705), and the DSVM-P demonstrated superior predictive performance (cross-validated AUC score of 0.78) against the state-of-the-art (AUC scores ranging from 0.665 to 0.717). More importantly, the resulting models go beyond improving predictive accuracy and into usefulness for risk management purposes through intervention, and enhanced decision support in terms of answering complex clinical questions that are based on unobserved evidence. Conclusions This development process is applicable to any application domain which involves large-scale decision analysis based on such complex information, rather than based on data with hard facts, and in conjunction with the incorporation of expert knowledge for decision support via intervention. The novelty extends to challenging the decision scientists to reason about building models based on what information is really required for inference, rather than based on what data is available and hence, forces decision scientists to use available data in a much smarter way. PMID:26830286

From complex questionnaire and interviewing data to intelligent Bayesian network models for medical decision support.

PubMed

Constantinou, Anthony Costa; Fenton, Norman; Marsh, William; Radlinski, Lukasz

2016-02-01

(1) To develop a rigorous and repeatable method for building effective Bayesian network (BN) models for medical decision support from complex, unstructured and incomplete patient questionnaires and interviews that inevitably contain examples of repetitive, redundant and contradictory responses; (2) To exploit expert knowledge in the BN development since further data acquisition is usually not possible; (3) To ensure the BN model can be used for interventional analysis; (4) To demonstrate why using data alone to learn the model structure and parameters is often unsatisfactory even when extensive data is available. The method is based on applying a range of recent BN developments targeted at helping experts build BNs given limited data. While most of the components of the method are based on established work, its novelty is that it provides a rigorous consolidated and generalised framework that addresses the whole life-cycle of BN model development. The method is based on two original and recent validated BN models in forensic psychiatry, known as DSVM-MSS and DSVM-P. When employed with the same datasets, the DSVM-MSS demonstrated competitive to superior predictive performance (AUC scores 0.708 and 0.797) against the state-of-the-art (AUC scores ranging from 0.527 to 0.705), and the DSVM-P demonstrated superior predictive performance (cross-validated AUC score of 0.78) against the state-of-the-art (AUC scores ranging from 0.665 to 0.717). More importantly, the resulting models go beyond improving predictive accuracy and into usefulness for risk management purposes through intervention, and enhanced decision support in terms of answering complex clinical questions that are based on unobserved evidence. This development process is applicable to any application domain which involves large-scale decision analysis based on such complex information, rather than based on data with hard facts, and in conjunction with the incorporation of expert knowledge for decision support via intervention. The novelty extends to challenging the decision scientists to reason about building models based on what information is really required for inference, rather than based on what data is available and hence, forces decision scientists to use available data in a much smarter way. Copyright © 2016 Elsevier B.V. All rights reserved.

High energy density and efficiency achieved in nanocomposite film capacitors via structure modulation

NASA Astrophysics Data System (ADS)

Zeng, Yi; Shen, Zhong-Hui; Shen, Yang; Lin, Yuanhua; Nan, Ce-Wen

2018-03-01

Flexible dielectric polymer films with high energy storage density and high charge-discharge efficiency have been considered as promising materials for electrical power applications. Here, we design hierarchical structured nanocomposite films using nonlinear polymer poly(vinylidene fluoride-HFP) [P(VDF-HFP)] with inorganic h-boron nitride (h-BN) nanosheets by electrospinning and hot-pressing methods. Our results show that the addition of h-BN nanosheets and the design of the hierarchical multilayer structure in the nanocomposites can remarkably enhance the charge-discharge efficiency and energy density. A high charge-discharge efficiency of 78% and an energy density of 21 J/cm3 can be realized in the 12-layered PVDF/h-BN nanocomposite films. Phase-field simulation results reveal that the spatial distribution of the electric field in these hierarchical structured films affects the charge-discharge efficiency and energy density. This work provides a feasible route, i.e., structure modulation, to improve the energy storage performances for nanocomposite films.

Ni foam assisted synthesis of high quality hexagonal boron nitride with large domain size and controllable thickness

NASA Astrophysics Data System (ADS)

Ying, Hao; Li, Xiuting; Li, Deshuai; Huang, Mingqiang; Wan, Wen; Yao, Qian; Chen, Xiangping; Wang, Zhiwei; Wu, Yanqing; Wang, Le; Chen, Shanshan

2018-04-01

The scalable synthesis of two-dimensional (2D) hexagonal boron nitride (h-BN) is of great interest for its numerous applications in novel electronic devices. Highly-crystalline h-BN films, with single-crystal sizes up to hundreds of microns, are demonstrated via a novel Ni foam assisted technique reported here for the first time. The nucleation density of h-BN domains can be significantly reduced due to the high boron solubility, as well as the large specific surface area of the Ni foam. The crystalline structure of the h-BN domains is found to be well aligned with, and therefore strongly dependent upon, the underlying Pt lattice orientation. Growth-time dependent experiments confirm the presence of a surface mediated self-limiting growth mechanism for monolayer h-BN on the Pt substrate. However, utilizing remote catalysis from the Ni foam, bilayer h-BN films can be synthesized breaking the self-limiting effect. This work provides further understanding of the mechanisms involved in the growth of h-BN and proposes a facile synthesis technique that may be applied to further applications in which control over the crystal alignment, and the numbers of layers is crucial.

Thin-walled boron nitride microtubes exhibiting intense band-edge UV emission at room temperature.

PubMed

Huang, Yang; Bando, Yoshio; Tang, Chengchun; Zhi, Chunyi; Terao, Takeshi; Dierre, Benjamin; Sekiguchi, Takashi; Golberg, Dmitri

2009-02-25

Boron nitride (BN) microtubes were synthesized in a vertical induction furnace using Li(2)CO(3) and B reactants. Their structures and morphologies were investigated using x-ray diffraction, scanning and transmission electron microscopy, and energy-dispersive x-ray spectroscopy. The microtubes have diameters of 1-3 microm, lengths of up to hundreds of micrometers, and well-structured ultrathin walls only approximately 50 nm thick. A mechanism combining the vapor-liquid-solid (VLS) and template self-sacrificing processes is proposed to explain the formation of these novel one-dimensional microstructures, in which the Li(2)O-B(2)O(3) eutectic reaction plays an important role. Cathodoluminescence studies show that even at room temperature the thin-walled BN microtubes can possess an intense band-edge emission at approximately 216.5 nm, which is distinct compared with other BN nanostructures. The study suggests that the thin-walled BN microtubes should be promising for constructing compact deep UV devices and find potential applications in microreactors and microfluidic and drug delivery systems.

Fundamental Discovery of New Phases and Direct Conversion of Carbon into Diamond and hBN into cBN and Properties

NASA Astrophysics Data System (ADS)

Narayan, Jagdish; Bhaumik, Anagh

2016-04-01

We review the discovery of new phases of carbon (Q-carbon) and BN (Q-BN) and address critical issues related to direct conversion of carbon into diamond and hBN into cBN at ambient temperatures and pressures in air without any need for catalyst and the presence of hydrogen. The Q-carbon and Q-BN are formed as a result of quenching from super undercooled state by using high-power nanosecond laser pulses. We discuss the equilibrium phase diagram ( P vs T) of carbon, and show that by rapid quenching, kinetics can shift thermodynamic graphite/diamond/liquid carbon triple point from 5000 K/12 GPa to super undercooled carbon at atmospheric pressure in air. Similarly, the hBN-cBN-Liquid triple point is shifted from 3500 K/9.5 GPa to as low as 2800 K and atmospheric pressure. It is shown that nanosecond laser heating of amorphous carbon and nanocrystalline BN on sapphire, glass, and polymer substrates can be confined to melt in a super undercooled state. By quenching this super undercooled state, we have created a new state of carbon (Q-carbon) and BN (Q-BN) from which nanocrystals, microcrystals, nanoneedles, microneedles, and thin films are formed depending upon the nucleation and growth times allowed and the presence of growth template. The large-area epitaxial diamond and cBN films are formed, when appropriate planar matching or lattice matching template is provided for growth from super undercooled liquid. The Q-phases have unique atomic structure and bonding characteristics as determined by high-resolution SEM and backscatter diffraction, HRTEM, STEM-Z, EELS, and Raman spectroscopy, and exhibit new and improved mechanical hardness, electrical conductivity, and chemical and physical properties, including room-temperature ferromagnetism and enhanced field emission. The Q-carbon exhibits robust bulk ferromagnetism with estimated Curie temperature of about 500 K and saturation magnetization value of 20 emu g-1. We have also deposited diamond on cBN by using a novel pulsed laser evaporation of carbon and obtained cBN/diamond composites, where cBN acts as template for diamond growth. Both diamond and cBN grown from super undercooled liquid can be alloyed with both p- and n-type dopants. This process allows carbon to diamond and hBN to cBN conversions and formation of useful nanostructures and microstructures at ambient temperatures in air at atmospheric pressure on practical and heat-sensitive substrates in a controlled way without need for any catalysts and hydrogen to stabilize sp3 bonding for diamond and cBN phases.

Structural instabilities and wrinkles at the grain boundaries in 2-D h-BN: a first-principles analysis.

PubMed

Singh, Anjali; Waghmare, Umesh V

2014-10-21

The structure of grain boundaries (GBs) or interfaces between nano-forms of carbon determines their evolution into 3-D forms with nano-scale architecture. Here, we present a general framework for the construction of interfaces in 2-D h-BN and graphene in terms of (a) stacking faults and (b) growth faults, using first-principles density functional theoretical analysis. Such interfaces or GBs involve deviation from their ideal hexagonal lattice structure. We show that a stacking fault involves a linkage of rhombal and octagonal rings (4 : 8), and a growth fault involves a linkage of paired pentagonal and octagonal rings (5 : 5 : 8). While a growth fault is energetically more stable than a stacking fault in graphene, the polarity of B and N leads to the reversal of their relative stability in h-BN. We show that the planar structure of these interfacing grains exhibits instability with respect to buckling (out-of-plane deformation), which results in the formation of a wrinkle at the grain boundary (GB) and rippling of the structure. Our analysis leads to prediction of new types of low-energy GBs of 2-D h-BN and graphene. Our results for electronic and vibrational signatures of these interfaces and an STM image of the most stable interface will facilitate their experimental characterization, particularly of the wrinkles forming spontaneously at these interfaces.

Observed Connection and Individuation: Relation to Symptoms in Families of Adolescents with Bulimia Nervosa

PubMed Central

Thomas, Sarah A.; Hoste, Renee Rienecke; Le Grange, Daniel

2012-01-01

Objective To examine the relation between observed familial connection and individuation and adolescent bulimia nervosa (BN) symptoms. Method As part of a treatment study for adolescent BN, adolescents (n = 54) and their parents participated in a videotaped semi-structured interview. Participants were rated on observed connection and individuation from these interviews using the Scale of Intergenerational Relationship Quality and two measures of connection. Results There was a significant negative relation between individuation from parents and adolescent BN symptoms. Connection both to and from mothers and adolescents was negatively associated with BN symptoms. Increased eating concern was significantly associated with a greater likelihood of expressing a desire for more connection with the family. Discussion Investigating and understanding family factors present at the time of adolescent BN may assist in providing treatment specific to the needs of the family to best aid the adolescent’s recovery process. PMID:22593023

Observed connection and individuation: relation to symptoms in families of adolescents with bulimia nervosa.

PubMed

Thomas, Sarah A; Hoste, Renee Rienecke; Le Grange, Daniel

2012-11-01

To examine the relation between observed familial connection and individuation and adolescent bulimia nervosa (BN) symptoms. As part of a treatment study for adolescent BN, adolescents (n = 54) and their parents participated in a videotaped semi-structured interview. Participants were rated on observed connection and individuation from these interviews using the Scale of Intergenerational Relationship Quality and two measures of connection. There was a significant negative relation between individuation from parents and adolescent BN symptoms. Connection both to and from mothers and adolescents was negatively associated with BN symptoms. Increased eating concern was significantly associated with a greater likelihood of expressing a desire for more connection with the family. Investigating and understanding family factors present at the time of adolescent BN may assist in providing treatment specific to the needs of the family to best aid the adolescent's recovery process. Copyright © 2012 Wiley Periodicals, Inc.

Effect of substrate temperature in the synthesis of BN nanostructures

NASA Astrophysics Data System (ADS)

Sajjad, M.; Zhang, H. X.; Peng, X. Y.; Feng, P. X.

2011-06-01

Boron nitride (BN) nanostructures were grown on molybdenum discs at different substrate temperatures using the short-pulse laser plasma deposition technique. Large numbers of randomly oriented nanorods of fiber-like structures were obtained. The variation in the length and diameter of the nanorods as a function of the substrate temperature was systematically studied. The surface morphologies of the samples were studied using scanning electron microscopy. Energy dispersive x-ray spectroscopy confirmed that both the elements boron and nitrogen are dominant in the nanostructure. The x-ray diffraction (XRD) technique was used to analyse BN phases. The XRD peak that appeared at 26° showed the presence of hexagonal BN phase, whereas the peak at 44° was related to cubic BN content in the samples. Raman spectroscopic analysis showed vibrational modes of sp2- and sp3-type bonding in the sample. The Raman spectra agreed well with XRD results.

Rapid Changes in the Structure of the BN Object

NASA Technical Reports Server (NTRS)

Danchi, William C.; Gezari, D. Y.; Greenhill, L. J.; Najita, J.; Monnier, J. D.; Tuthill, P. G.; Wishnow, E. H.; Townes, C. H.; Fisher, Richard R. (Technical Monitor)

2001-01-01

The BN/KL region in Orion is the archetypal region of high-mass star formation, radiating approx. 10(sup)5 Lsun and displaying promininent bulk outflows. In particular, there is no certain identification of the sources responsible for the high luminosity and outflows, and is the origin of a major explosive event (Shultz et al. 1999, ApJ, 511, 282). Using 18.7 and 12.5 micron data from observations in December 1999 and October 2000 made at the Keck I telescope, we discovered that the BN Object has a companion previously seen only at radio wavelengths (Menten & Reid 1995, ApJ, 445, L157). We call this companion B2 and it is about 1.5 arcsec West of the bright component. We also see changes in the shape of BN and the emission of "blobs" or "bullets" of material. While B2 remains unchanged and in the same place between the two epochs, there is an additional structure in BN to the South-South-East and the North-East, as well as a finger of material pointing North from B2 itself. Such a change has not been seen before in the infrared. We have looked very carefully at these images, calibrator images taken within a few minutes of the source images, as well as our previous images and cannot find any technical faults with the data. We explore the implications of these results, in particular, can these features be connected with previously observed "bullets" or "fingers" (see Allen & Burton 1993, for example), making BN a source for the bullets, implying they are not from IRc2 as previously thought? Or could they be produced by an interaction between material from BN and other sources such as IRc2?

Competition between landmarks in spatial learning: the role of proximity to the goal.

PubMed

Chamizo, V D; Manteiga, R D; Rodrigo, T; Mackintosh, N J

2006-01-10

In two experiments, rats were trained to find a hidden platform in a Morris pool in the presence of two landmarks. Landmark B was present on all training trials, on half the trials accompanied by landmark A, on the remainder by landmark C. For rats in Group Bn, B was near the location of the platform; for those in Group Bf, B was far from the platform. Group Bn performed better than Group Bf on test trials to B alone, but significantly worse on test trials to a new configuration formed by A and C. Thus, the spatial proximity of B to the platform affected not only how well it could be used to locate the platform, but also its ability to prevent learning about other landmarks.

Genome-Wide Survey of Flavonoid Biosynthesis Genes and Gene Expression Analysis between Black- and Yellow-Seeded Brassica napus

PubMed Central

Qu, Cunmin; Zhao, Huiyan; Fu, Fuyou; Wang, Zhen; Zhang, Kai; Zhou, Yan; Wang, Xin; Wang, Rui; Xu, Xinfu; Tang, Zhanglin; Lu, Kun; Li, Jia-Na

2016-01-01

Flavonoids, the compounds that impart color to fruits, flowers, and seeds, are the most widespread secondary metabolites in plants. However, a systematic analysis of these loci has not been performed in Brassicaceae. In this study, we isolated 649 nucleotide sequences related to flavonoid biosynthesis, i.e., the Transparent Testa (TT) genes, and their associated amino acid sequences in 17 Brassicaceae species, grouped into Arabidopsis or Brassicaceae subgroups. Moreover, 36 copies of 21 genes of the flavonoid biosynthesis pathway were identified in Arabidopsis thaliana, 53 were identified in Brassica rapa, 50 in Brassica oleracea, and 95 in B. napus, followed the genomic distribution, collinearity analysis and genes triplication of them among Brassicaceae species. The results showed that the extensive gene loss, whole genome triplication, and diploidization that occurred after divergence from the common ancestor. Using qRT-PCR methods, we analyzed the expression of 18 flavonoid biosynthesis genes in 6 yellow- and black-seeded B. napus inbred lines with different genetic background, found that 12 of which were preferentially expressed during seed development, whereas the remaining genes were expressed in all B. napus tissues examined. Moreover, 14 of these genes showed significant differences in expression level during seed development, and all but four of these (i.e., BnTT5, BnTT7, BnTT10, and BnTTG1) had similar expression patterns among the yellow- and black-seeded B. napus. Results showed that the structural genes (BnTT3, BnTT18, and BnBAN), regulatory genes (BnTTG2 and BnTT16) and three encoding transfer proteins (BnTT12, BnTT19, and BnAHA10) might play an crucial roles in the formation of different seed coat colors in B. napus. These data will be helpful for illustrating the molecular mechanisms of flavonoid biosynthesis in Brassicaceae species. PMID:27999578

Wetting and interfacial properties of water nanodroplets in contact with graphene and monolayer boron-nitride sheets.

PubMed

Li, Hui; Zeng, Xiao Cheng

2012-03-27

Born-Oppenheim quantum molecular dynamics (QMD) simulations are performed to investigate wetting, diffusive, and interfacial properties of water nanodroplets in contact with a graphene sheet or a monolayer boron-nitride (BN) sheet. Contact angles of the water nanodroplets on the two sheets are computed for the first time using QMD simulations. Structural and dynamic properties of the water droplets near the graphene or BN sheet are also studied to gain insights into the interfacial interaction between the water droplet and the substrate. QMD simulation results are compared with those from previous classic MD simulations and with the experimental measurements. The QMD simulations show that the graphene sheet yields a contact angle of 87°, while the monolayer BN sheet gives rise to a contact angle of 86°. Hence, like graphene, the monolayer BN sheet is also weakly hydrophobic, even though the BN bonds entail a large local dipole moment. QMD simulations also show that the interfacial water can induce net positive charges on the contacting surface of the graphene and monolayer BN sheets, and such charge induction may affect electronic structure of the contacting graphene in view that graphene is a semimetal. Contact angles of nanodroplets of water in a supercooled state on the graphene are also computed. It is found that under the supercooled condition, water nanodroplets exhibit an appreciably larger contact angle than under the ambient condition. © 2012 American Chemical Society

Application of Bayesian networks in a hierarchical structure for environmental risk assessment: a case study of the Gabric Dam, Iran.

PubMed

Malekmohammadi, Bahram; Tayebzadeh Moghadam, Negar

2018-04-13

Environmental risk assessment (ERA) is a commonly used, effective tool applied to reduce adverse effects of environmental risk factors. In this study, ERA was investigated using the Bayesian network (BN) model based on a hierarchical structure of variables in an influence diagram (ID). ID facilitated ranking of the different alternatives under uncertainty that were then used to evaluate comparisons of the different risk factors. BN was used to present a new model for ERA applicable to complicated development projects such as dam construction. The methodology was applied to the Gabric Dam, in southern Iran. The main environmental risk factors in the region, presented by the Gabric Dam, were identified based on the Delphi technique and specific features of the study area. These included the following: flood, water pollution, earthquake, changes in land use, erosion and sedimentation, effects on the population, and ecosensitivity. These risk factors were then categorized based on results from the output decision node of the BN, including expected utility values for risk factors in the decision node. ERA was performed for the Gabric Dam using the analytical hierarchy process (AHP) method to compare results of BN modeling with those of conventional methods. Results determined that a BN-based hierarchical structure to ERA present acceptable and reasonable risk assessment prioritization in proposing suitable solutions to reduce environmental risks and can be used as a powerful decision support system for evaluating environmental risks.

The dynamic programming high-order Dynamic Bayesian Networks learning for identifying effective connectivity in human brain from fMRI.

PubMed

Dang, Shilpa; Chaudhury, Santanu; Lall, Brejesh; Roy, Prasun Kumar

2017-06-15

Determination of effective connectivity (EC) among brain regions using fMRI is helpful in understanding the underlying neural mechanisms. Dynamic Bayesian Networks (DBNs) are an appropriate class of probabilistic graphical temporal-models that have been used in past to model EC from fMRI, specifically order-one. High-order DBNs (HO-DBNs) have still not been explored for fMRI data. A fundamental problem faced in the structure-learning of HO-DBN is high computational-burden and low accuracy by the existing heuristic search techniques used for EC detection from fMRI. In this paper, we propose using dynamic programming (DP) principle along with integration of properties of scoring-function in a way to reduce search space for structure-learning of HO-DBNs and finally, for identifying EC from fMRI which has not been done yet to the best of our knowledge. The proposed exact search-&-score learning approach HO-DBN-DP is an extension of the technique which was originally devised for learning a BN's structure from static data (Singh and Moore, 2005). The effectiveness in structure-learning is shown on synthetic fMRI dataset. The algorithm reaches globally-optimal solution in appreciably reduced time-complexity than the static counterpart due to integration of properties. The proof of optimality is provided. The results demonstrate that HO-DBN-DP is comparably more accurate and faster than currently used structure-learning algorithms used for identifying EC from fMRI. The real data EC from HO-DBN-DP shows consistency with previous literature than the classical Granger Causality method. Hence, the DP algorithm can be employed for reliable EC estimates from experimental fMRI data. Copyright © 2017 Elsevier B.V. All rights reserved.

Semiconductor-Insulator-Semiconductor Diode Consisting of Monolayer MoS2, h-BN, and GaN Heterostructure.

PubMed

Jeong, Hyun; Bang, Seungho; Oh, Hye Min; Jeong, Hyeon Jun; An, Sung-Jin; Han, Gang Hee; Kim, Hyun; Kim, Ki Kang; Park, Jin Cheol; Lee, Young Hee; Lerondel, Gilles; Jeong, Mun Seok

2015-10-27

We propose a semiconductor-insulator-semiconductor (SIS) heterojunction diode consisting of monolayer (1-L) MoS2, hexagonal boron nitride (h-BN), and epitaxial p-GaN that can be applied to high-performance nanoscale optoelectronics. The layered materials of 1-L MoS2 and h-BN, grown by chemical vapor deposition, were vertically stacked by a wet-transfer method on a p-GaN layer. The final structure was verified by confocal photoluminescence and Raman spectroscopy. Current-voltage (I-V) measurements were conducted to compare the device performance with that of a more classical p-n structure. In both structures (the p-n and SIS heterojunction diode), clear current-rectifying characteristics were observed. In particular, a current and threshold voltage were obtained for the SIS structure that was higher compared to that of the p-n structure. This indicated that tunneling is the predominant carrier transport mechanism. In addition, the photoresponse of the SIS structure induced by the illumination of visible light was observed by photocurrent measurements.

Synthesis and Characterization of Nano Boron Nitride Reinforced Magnesium Composites Produced by the Microwave Sintering Method

PubMed Central

Seetharaman, Sankaranarayanan; Subramanian, Jayalakshmi; Tun, Khin Sandar; Hamouda, Abdelmagid S.; Gupta, Manoj

2013-01-01

In this study, magnesium composites with nano-size boron nitride (BN) particulates of varying contents were synthesized using the powder metallurgy (PM) technique incorporating microwave-assisted two-directional sintering followed by hot extrusion. The effect of nano-BN addition on the microstructural and the mechanical behavior of the developed Mg/BN composites were studied in comparison with pure Mg using the structure-property correlation. Microstructural characterization revealed uniform distribution of nano-BN particulates and marginal grain refinement. The coefficient of thermal expansion (CTE) value of the magnesium matrix was improved with the addition of nano-sized BN particulates. The results of XRD studies indicate basal texture weakening with an increase in nano-BN addition. The composites showed improved mechanical properties measured under micro-indentation, tension and compression loading. While the tensile yield strength improvement was marginal, a significant increase in compressive yield strength was observed. This resulted in the reduction of tension-compression yield asymmetry and can be attributed to the weakening of the strong basal texture. PMID:28809252

Modulation of band gap by an applied electric field in BN-based heterostructures

NASA Astrophysics Data System (ADS)

Luo, M.; Xu, Y. E.; Zhang, Q. X.

2018-05-01

First-principles density functional theory (DFT) calculations are performed on the structural and electronic properties of the SiC/BN van der Waals (vdW) heterostructures under an external electric field (E-field). Our results reveal that the SiC/BN vdW heterostructure has a direct band gap of 2.41 eV in the raw. The results also imply that electrons are likely to transfer from BN to SiC monolayer due to the deeper potential of BN monolayer. It is also observed that, by applying an E-field, ranging from -0.50 to +0.65 V/Å, the band gap decreases from 2.41 eV to zero, which presents a parabola-like relationship around 0.0 V/Å. Through partial density of states (PDOS) plots, it is revealed that, p orbital of Si, C, B, and N atoms are responsible for the significant variations of band gap. These obtained results predict that, the electric field tunable band gap of the SiC/BN vdW heterostructures carries potential applications for nanoelectronics and spintronic device applications.

Graphene-like boron nitride modified bismuth phosphate materials for boosting photocatalytic degradation of enrofloxacin.

PubMed

Chen, Zhigang; Chen, Xiaoliu; Di, Jun; Liu, Yiling; Yin, Sheng; Xia, Jiexiang; Li, Huaming

2017-04-15

A novel graphene-like BN modified BiPO 4 material was prepared for the first time via a simple solvothermal process with the assistance of reactable ionic liquid 1-decyl-3-methylimidazolium dihydrogen phosphate ([Omim]H 2 PO 4 ). The as-prepared photocatalyst was characterized by XRD, FT-IR, Raman, XPS, TEM, DRS, BET, PL, EIS and ESR to investigate the structure, morphology, optical property, surface area, electrical property and active species. The photocatalytic activities of graphene-like BN/BiPO 4 materials were evaluated by the degradation of antibiotic enrofloxacin (ENR) under UV light irradiation and the 1wt% graphene-like BN/BiPO 4 displayed the best activity among the BN/BiPO 4 composites. The enhanced photocatalytic activity for the removal of enrofloxacin was attributed to higher separation efficiency of photogenerated electron-hole pairs, and the generated more O 2 - and OH radicals when the BN was modified on BiPO 4 . Moreover, a probable degradation mechanism was proposed for the improved photocatalytic activity of BN modified BiPO 4 . Copyright © 2016 Elsevier Inc. All rights reserved.

Structural Evolution of Silicon Oxynitride Fiber Reinforced Boron Nitride Matrix Composite at High Temperatures

NASA Astrophysics Data System (ADS)

Zou, Chunrong; Li, Bin; Zhang, Changrui; Wang, Siqing; Xie, Zhengfang; Shao, Changwei

2016-02-01

The structural evolution of a silicon oxynitride fiber reinforced boron nitride matrix (Si-N-Of/BN) wave-transparent composite at high temperatures was investigated. When heat treated at 1600 °C, the composite retained a favorable bending strength of 55.3 MPa while partially crystallizing to Si2N2O and h-BN from the as-received amorphous structure. The Si-N-O fibers still performed as effective reinforcements despite the presence of small pores due to fiber decomposition. Upon heat treatment at 1800 °C, the Si-N-O fibers already lost their reinforcing function and rough hollow microstructure formed within the fibers because of the accelerated decomposition. Further heating to 2000 °C led to the complete decomposition of the reinforcing fibers and only h-BN particles survived. The crystallization and decomposition behaviors of the composite at high temperatures are discussed.

Magnetic and Electronic Properties of h-BN Nanosheets with Nonmetal Atoms Adsorbed: an Ab Initio Study

NASA Astrophysics Data System (ADS)

Luo, M.; Yin, H. H.; Chu, J. H.

2018-04-01

The magnetic properties of the h-BN monolayer with nonmetal atoms are studied by ab initio methods. Different dopants (C, Cl, F, and O) and doping sites are considered. Magnetic behavior is observed in the two-dimensional (2D) BN system with C, Cl, and O atoms. On the other hand, the O adsorbed system shows a more stable formed structure among above three magnetic materials, we study the ferromagnetic (FM) interaction in 2D-BN system with two O adatoms. Interestingly, as the O-O distance increases, the interaction between two O adatoms prefers to a long-range FM coupling. This phenomenon could be well described by a simple Heisenberg model.

Optical, photonic and optoelectronic properties of graphene, h-NB and their hybrid materials

NASA Astrophysics Data System (ADS)

Wang, Jingang; Ma, Fengcai; Liang, Wenjie; Wang, Rongming; Sun, Mengtao

2017-06-01

Because of the linear dispersion relation and the unique structure of graphene's Dirac electrons, which can be tuned the ultra-wide band, this enables more applications in photonics, electronics and plasma optics. As a substrate, hexagonal boron nitride (h-BN) has an atomic level flat surface without dangling bonds, a weak doping effect and a response in the far ultraviolet area. So the graphene/h-BN heterostructure is very attractive due to its unique optical electronics characteristics. Graphene and h-BN which are stacked in different ways could open the band gap of graphene, and form a moiré pattern for graphene on h-BN and the superlattice in the Brillouin zone, which makes it possible to build photoelectric devices.

Metal-free spin and spin-gapless semiconducting heterobilayers: monolayer boron carbonitrides on hexagonal boron nitride.

PubMed

Pan, Hongzhe; Zhang, Hongyu; Sun, Yuanyuan; Ding, Yingchun; Chen, Jie; Du, Youwei; Tang, Nujiang

2017-06-07

The interfaces between monolayer boron carbonitrides and hexagonal boron nitride (h-BN) play an important role in their practical applications. Herein, we respectively investigate the structural and electronic properties of two metal-free heterobilayers constructed by vertically stacking two-dimensional (2D) spintronic materials (B 4 CN 3 and B 3 CN 4 ) on a h-BN monolayer from the viewpoints of lattice match and lattice mismatch models using density functional calculations. It is found that both B 4 CN 3 and B 3 CN 4 monolayers can be stably adsorbed on the h-BN monolayer due to the van der Waals interactions. Intriguingly, we demonstrate that the bipolar magnetic semiconductor (BMS) behavior of the B 4 CN 3 layer and the spin gapless semiconductor (SGS) property of the B 3 CN 4 layer can be well preserved in the B 4 CN 3 /BN and B 3 CN 4 /BN heterobilayers, respectively. The magnetic moments and spintronic properties of the two systems originate mainly from the 2p z electrons of the carbon atoms in the B 4 CN 3 and B 3 CN 4 layers. Furthermore, the BMS behavior of the B 4 CN 3 /BN bilayer is very robust while the electronic property of the B 3 CN 4 /BN bilayer is sensitive to interlayer couplings. These theoretical results are helpful both in understanding the interlayer coupling between B 4 CN 3 or B 3 CN 4 and h-BN monolayers and in providing a possibility of fabricating 2D composite B 4 CN 3 /BN and B 3 CN 4 /BN metal-free spintronic materials theoretically.

Adsorption and possible dissociation of glucose by the [BN fullerene-B6]- magnetic nanocomposite. In silico studies

NASA Astrophysics Data System (ADS)

Anota, E. Chigo; Villanueva, M. Salazar; Shakerzadeh, E.; Castro, M.

2018-02-01

The adsorption, activation and possible dissociation of the glucose molecule on the magnetic [BN fullerene-B6]- system is performed by means of density functional theory calculations. Three models of magnetic nanocomposites were inspected: i) pristine BN fullerene, BN fullerene functionalized with a magnetic B6 cluster which generates two structures: ii) pyramidal (P) and iii) triangular (T). Chemical interactions of glucose appear for all these cases; however, for the BNF:B6(T)—glucose system, the interaction generates an effect of dissociation on glucose, due to the magnetic effects, since it has high spin multiplicity. The latter nanocomposite shows electronic behavior like-conductor and like-semi-conductor for the P and T geometries, respectively. Intrinsic magnetism associated to values of 1.0 magneton bohr (µB) for the pyramidal and 5.0 µB for the triangular structure, high polarity, and low-chemical reactivity are found for these systems. These interesting properties make these functionalized fullerenes a good option for being used as nano-vehicles for drug delivery. These quantum descriptors remain invariant when the [BN]-fullerene and [BNF:B6 (P) or (T)]- nanocomposites are interacting with the glucose molecule. According to the determined adsorption energy, chemisorption regimes occur in both the phases: gas and aqueous medium.

Intelligent judgements over health risks in a spatial agent-based model.

PubMed

Abdulkareem, Shaheen A; Augustijn, Ellen-Wien; Mustafa, Yaseen T; Filatova, Tatiana

2018-03-20

Millions of people worldwide are exposed to deadly infectious diseases on a regular basis. Breaking news of the Zika outbreak for instance, made it to the main media titles internationally. Perceiving disease risks motivate people to adapt their behavior toward a safer and more protective lifestyle. Computational science is instrumental in exploring patterns of disease spread emerging from many individual decisions and interactions among agents and their environment by means of agent-based models. Yet, current disease models rarely consider simulating dynamics in risk perception and its impact on the adaptive protective behavior. Social sciences offer insights into individual risk perception and corresponding protective actions, while machine learning provides algorithms and methods to capture these learning processes. This article presents an innovative approach to extend agent-based disease models by capturing behavioral aspects of decision-making in a risky context using machine learning techniques. We illustrate it with a case of cholera in Kumasi, Ghana, accounting for spatial and social risk factors that affect intelligent behavior and corresponding disease incidents. The results of computational experiments comparing intelligent with zero-intelligent representations of agents in a spatial disease agent-based model are discussed. We present a spatial disease agent-based model (ABM) with agents' behavior grounded in Protection Motivation Theory. Spatial and temporal patterns of disease diffusion among zero-intelligent agents are compared to those produced by a population of intelligent agents. Two Bayesian Networks (BNs) designed and coded using R and are further integrated with the NetLogo-based Cholera ABM. The first is a one-tier BN1 (only risk perception), the second is a two-tier BN2 (risk and coping behavior). We run three experiments (zero-intelligent agents, BN1 intelligence and BN2 intelligence) and report the results per experiment in terms of several macro metrics of interest: an epidemic curve, a risk perception curve, and a distribution of different types of coping strategies over time. Our results emphasize the importance of integrating behavioral aspects of decision making under risk into spatial disease ABMs using machine learning algorithms. This is especially relevant when studying cumulative impacts of behavioral changes and possible intervention strategies.

Boolean network inference from time series data incorporating prior biological knowledge.

PubMed

Haider, Saad; Pal, Ranadip

2012-01-01

Numerous approaches exist for modeling of genetic regulatory networks (GRNs) but the low sampling rates often employed in biological studies prevents the inference of detailed models from experimental data. In this paper, we analyze the issues involved in estimating a model of a GRN from single cell line time series data with limited time points. We present an inference approach for a Boolean Network (BN) model of a GRN from limited transcriptomic or proteomic time series data based on prior biological knowledge of connectivity, constraints on attractor structure and robust design. We applied our inference approach to 6 time point transcriptomic data on Human Mammary Epithelial Cell line (HMEC) after application of Epidermal Growth Factor (EGF) and generated a BN with a plausible biological structure satisfying the data. We further defined and applied a similarity measure to compare synthetic BNs and BNs generated through the proposed approach constructed from transitions of various paths of the synthetic BNs. We have also compared the performance of our algorithm with two existing BN inference algorithms. Through theoretical analysis and simulations, we showed the rarity of arriving at a BN from limited time series data with plausible biological structure using random connectivity and absence of structure in data. The framework when applied to experimental data and data generated from synthetic BNs were able to estimate BNs with high similarity scores. Comparison with existing BN inference algorithms showed the better performance of our proposed algorithm for limited time series data. The proposed framework can also be applied to optimize the connectivity of a GRN from experimental data when the prior biological knowledge on regulators is limited or not unique.

Study of vibrational modes and specific heat of wurtzite phase of BN

DOE Office of Scientific and Technical Information (OSTI.GOV)

Singh, Daljit, E-mail: daljit.jt@gmail.com; Sinha, M. M.

2016-05-06

In these days of nanotechnology the materials like BN is of utmost importance as in hexagonal phase it is among hardest materials. The phonon mode study of the materials is most important factor to find structural and thermodynamcal properties. To study the phonons de launey angular force (DAF) constant model is best suited as it involves many particle interactions. Therefore in this presentation we have studied the lattice dynamical properties and specific heat of BN in wurtzite phase using DAF model. The obtained results are in excellent agreement with existing results.

Plasma synthesis and HPHT consolidation of BN nanoparticles, nanospheres, and nanotubes to produce nanocrystalline cubic boron nitride

NASA Astrophysics Data System (ADS)

Stout, Christopher

Plasma methods offer a variety of advantages to nanomaterials synthesis. The process is robust, allowing varying particle sizes and phases to be generated simply by modifying key parameters. The work here demonstrates a novel approach to nanopowder synthesis using inductively-coupled plasma to decompose precursor, which are then quenched to produce a variety of boron nitride (BN)-phase nanoparticles, including cubic phase, along with short-range-order nanospheres (e.g., nano-onions) and BN nanotubes. Cubic BN (c-BN) powders can be generated through direct deposition onto a chilled substrate. The extremely-high pyrolysis temperatures afforded by the equilibrium plasma offer a unique particle growth environment, accommodating long deposition times while exposing resulting powders to temperatures in excess of 5000K without any additional particle nucleation and growth. Such conditions can yield short-range ordered amorphous BN structures in the form of 20nm diameter nanospheres. Finally, when introducing a rapid-quenching counter-flow gas against the plasma jet, high aspect ratio nanotubes are synthesized, which are collected on substrate situated radially. The benefits of these morphologies are also evident in high-pressure/high-temperature consolidation experiments, where nanoparticle phases can offer a favorable conversion route to super-hard c-BN while maintaining nanocrystallinity. Experiments using these morphologies are shown to begin to yield c-BN conversion at conditions as low as 2.0 GPa and 1500°C when using micron sized c-BN seeding to create localized regions of high pressures due to Hertzian forces acting on the nanoparticles.

Fabrication of AlN/BN bishell hollow nanofibers by electrospinning and atomic layer deposition

DOE Office of Scientific and Technical Information (OSTI.GOV)

Haider, Ali; Kayaci, Fatma; Uyar, Tamer

2014-09-01

Aluminum nitride (AlN)/boron nitride (BN) bishell hollow nanofibers (HNFs) have been fabricated by successive atomic layer deposition (ALD) of AlN and sequential chemical vapor deposition (CVD) of BN on electrospun polymeric nanofibrous template. A four-step fabrication process was utilized: (i) fabrication of polymeric (nylon 6,6) nanofibers via electrospinning, (ii) hollow cathode plasma-assisted ALD of AlN at 100 °C onto electrospun polymeric nanofibers, (iii) calcination at 500 °C for 2 h in order to remove the polymeric template, and (iv) sequential CVD growth of BN at 450 °C. AlN/BN HNFs have been characterized for their chemical composition, surface morphology, crystal structure, and internal nanostructuremore » using X-ray photoelectron spectroscopy, scanning electron microscopy, transmission electron microscopy, energy dispersive X-ray spectroscopy, and selected area electron diffraction. Measurements confirmed the presence of crystalline hexagonal BN and AlN within the three dimensional (3D) network of bishell HNFs with relatively low impurity content. In contrast to the smooth surface of the inner AlN layer, outer BN coating showed a highly rough 3D morphology in the form of BN nano-needle crystallites. It is shown that the combination of electrospinning and plasma-assisted low-temperature ALD/CVD can produce highly controlled multi-layered bishell nitride ceramic hollow nanostructures. While electrospinning enables easy fabrication of nanofibrous template, self-limiting reactions of plasma-assisted ALD and sequential CVD provide control over the wall thicknesses of AlN and BN layers with sub-nanometer accuracy.« less

An interoceptive model of bulimia nervosa: A neurobiological systematic review.

PubMed

Klabunde, Megan; Collado, Danielle; Bohon, Cara

2017-11-01

The objective of our study was to examine the neurobiological support for an interoceptive sensory processing model of bulimia nervosa (BN). To do so, we conducted a systematic review of interoceptive sensory processing in BN, using the PRISMA guidelines. We searched PsychInfo, Pubmed, and Web of Knowledge databases to identify biological and behavioral studies that examine interoceptive detection in BN. After screening 390 articles for inclusion and conducting a quality assessment of articles that met inclusion criteria, we reviewed 41 articles. We found that global interoceptive sensory processing deficits may be present in BN. Specifically there is evidence of abnormal brain function, structure and connectivity in the interoceptive neural network, in addition to gastric and pain processing disturbances. These results suggest that there may be a neurobiological basis for global interoceptive sensory processing deficits in BN that remain after recovery. Data from taste and heart beat detection studies were inconclusive; some studies suggest interoceptive disturbances in these sensory domains. Discrepancies in findings appear to be due to methodological differences. In conclusion, interoceptive sensory processing deficits may directly contribute to and explain a variety of symptoms present in those with BN. Further examination of interoceptive sensory processing deficits could inform the development of treatments for those with BN. Copyright © 2017 Elsevier Ltd. All rights reserved.

A behavioral-genetic investigation of bulimia nervosa and its relationship with alcohol use disorder

PubMed Central

Trace, Sara Elizabeth; Thornton, Laura Marie; Baker, Jessica Helen; Root, Tammy Lynn; Janson, Lauren Elizabeth; Lichtenstein, Paul; Pedersen, Nancy Lee; Bulik, Cynthia Marie

2013-01-01

Bulimia nervosa (BN) and alcohol use disorder (AUD) frequently co-occur and may share genetic factors; however, the nature of their association is not fully understood. We assessed the extent to which the same genetic and environmental factors contribute to liability to BN and AUD. A bivariate structural equation model using a Cholesky decomposition was fit to data from 7,241 women who participated in the Swedish Twin study of Adults: Genes and Environment. The proportion of variance accounted for by genetic and environmental factors for BN and AUD and the genetic and environmental correlations between these disorders were estimated. In the best-fitting model, the heritability estimates were 0.55 (95% CI: 0.37; 0.70) for BN and 0.62 (95% CI: 0.54; 0.70) for AUD. Unique environmental factors accounted for the remainder of variance for BN. The genetic correlation between BN and AUD was 0.23 (95% CI: 0.01; 0.44), and the correlation between the unique environmental factors for the two disorders was 0.35 (95% CI: 0.08; 0.61), suggesting moderate overlap in these factors. Findings from this investigation provide additional support that some of the same genetic factors may influence liability to both BN and AUD. PMID:23790978

Mobility enhancement in graphene transistors on low temperature pulsed laser deposited boron nitride

DOE Office of Scientific and Technical Information (OSTI.GOV)

Uddin, Md Ahsan, E-mail: uddin2@email.sc.edu, E-mail: gkoley@clemson.edu; Koley, Goutam, E-mail: uddin2@email.sc.edu, E-mail: gkoley@clemson.edu; Department of Electrical Engineering, University of South Carolina, Columbia, South Carolina 29208

2015-11-16

Low temperature pulsed laser deposited (PLD) ultrathin boron nitride (BN) on SiO{sub 2} was investigated as a dielectric for graphene electronics, and a significant enhancement in electrical transport properties of graphene/PLD BN compared to graphene/SiO{sub 2} has been observed. Graphene synthesized by chemical vapor deposition and transferred on PLD deposited and annealed BN exhibited up to three times higher field effect mobility compared to graphene on the SiO{sub 2} substrate. Graphene field effect transistor devices fabricated on 5 nm BN/SiO{sub 2} (300 nm) yielded maximum hole and electron mobility of 4980 and 4200 cm{sup 2}/V s, respectively. In addition, significant improvement in carriermore » homogeneity and reduction in extrinsic doping in graphene on BN has been observed. An average Dirac point of 3.5 V and residual carrier concentration of 7.65 × 10{sup 11 }cm{sup −2} was observed for graphene transferred on 5 nm BN at ambient condition. The overall performance improvement on PLD BN can be attributed to dielectric screening of charged impurities, similar crystal structure and phonon modes, and reduced substrate induced doping.« less

Hyperbolic phonon polaritons in hexagonal boron nitride (Conference Presentation)

NASA Astrophysics Data System (ADS)

Dai, Siyuan; Ma, Qiong; Fei, Zhe; Liu, Mengkun; Goldflam, Michael D.; Andersen, Trond; Garnett, William; Regan, Will; Wagner, Martin; McLeod, Alexander S.; Rodin, Alexandr; Zhu, Shou-En; Watanabe, Kenji; Taniguchi, T.; Dominguez, Gerado; Thiemens, Mark; Castro Neto, Antonio H.; Janssen, Guido C. A. M.; Zettl, Alex; Keilmann, Fritz; Jarillo-Herrero, Pablo; Fogler, Michael M.; Basov, Dmitri N.

2016-09-01

Uniaxial materials whose axial and tangential permittivities have opposite signs are referred to as indefinite or hyperbolic media. While hyperbolic responses are normally achieved with metamaterials, hexagonal boron nitride (hBN) naturally possesses this property due to the anisotropic phonons in the mid-infrared. Using scattering-type scanning near-field optical microscopy, we studied polaritonic phenomena in hBN. We performed infrared nano-imaging of highly confined and low-loss hyperbolic phonon polaritons in hBN. The polariton wavelength was shown to be governed by the hBN thickness according to a linear law persisting down to few atomic layers [1]. Additionally, we carried out the modification of hyperbolic response in meta-structures comprised of a mononlayer graphene deposited on hBN [2]. Electrostatic gating of the top graphene layer allows for the modification of wavelength and intensity of hyperbolic phonon polaritons in bulk hBN. The physics of the modification originates from the plasmon-phonon coupling in the hyperbolic medium. Furthermore, we demonstrated the "hyperlens" for subdiffractional focusing and imaging using a slab of hBN [3]. References [1] S. Dai et al., Science, 343, 1125 (2014). [2] S. Dai et al., Nature Nanotechnology, 10, 682 (2015). [3] S. Dai et al., Nature Communications, 6, 6963 (2015).

DOE Office of Scientific and Technical Information (OSTI.GOV)

Mitrani, J

Bayesian networks (BN) are an excellent tool for modeling uncertainties in systems with several interdependent variables. A BN is a directed acyclic graph, and consists of a structure, or the set of directional links between variables that depend on other variables, and conditional probabilities (CP) for each variable. In this project, we apply BN's to understand uncertainties in NIF ignition experiments. One can represent various physical properties of National Ignition Facility (NIF) capsule implosions as variables in a BN. A dataset containing simulations of NIF capsule implosions was provided. The dataset was generated from a radiation hydrodynamics code, and itmore » contained 120 simulations of 16 variables. Relevant knowledge about the physics of NIF capsule implosions and greedy search algorithms were used to search for hypothetical structures for a BN. Our preliminary results found 6 links between variables in the dataset. However, we thought there should have been more links between the dataset variables based on the physics of NIF capsule implosions. Important reasons for the paucity of links are the relatively small size of the dataset, and the sampling of the values for dataset variables. Another factor that might have caused the paucity of links is the fact that in the dataset, 20% of the simulations represented successful fusion, and 80% didn't, (simulations of unsuccessful fusion are useful for measuring certain diagnostics) which skewed the distributions of several variables, and possibly reduced the number of links. Nevertheless, by illustrating the interdependencies and conditional probabilities of several parameters and diagnostics, an accurate and complete BN built from an appropriate simulation set would provide uncertainty quantification for NIF capsule implosions.« less

High-Temperature Corrosion Behavior of SiBCN Fibers for Aerospace Applications.

PubMed

Ji, Xiaoyu; Wang, Shanshan; Shao, Changwei; Wang, Hao

2018-06-13

Amorphous SiBCN fibers possessing superior stability against oxidation have become a desirable candidate for high-temperature aerospace applications. Currently, investigations on the high-temperature corrosion behavior of these fibers for the application in high-heat engines are insufficient. Here, our polymer-derived SiBCN fibers were corroded at 1400 °C in air and simulated combustion environments. The fibers' structural evolution after corrosion in two different conditions and the potential mechanisms are investigated. It shows that the as-prepared SiBCN fibers mainly consist of amorphous networks of SiN 3 C, SiN 4 , B-N hexatomic rings, free carbon clusters, and BN 2 C units. High-resolution transmission electron microscopy cross-section observations combined with energy-dispersive spectrometry/electron energy-loss spectroscopy analysis exhibit a trilayer structure with no detectable cracks for fibers after corrosion, including the outermost SiO 2 layer, the h-BN grain-contained interlayer, and the uncorroded fiber core. A high percentage of water vapor contained in the simulated combustion environment triggers the formation of abundant α-cristobalite nanoparticles dispersing in the amorphous SiO 2 phase, which are absent in fibers corroded in air. The formation of h-BN grains in the interlayer could be ascribed to the sacrificial effects of free carbon clusters, Si-C, and Si-N units reacting with oxygen diffusing inward, which protects h-BN grains formed by networks of B-N hexatomic rings in original SiBCN fibers. These results improve our understanding of the corrosion process of SiBCN fibers in a high-temperature oxygen- and water-rich atmosphere.

Rhodium-Catalyzed Boron Arylation of 1,2-Azaborines**

PubMed Central

Rudebusch, Gabriel E.; Zakharov, Lev N.; Liu, Shih-Yuan

2013-01-01

A Sn-phony in B! BN isosteres of biphenyl compounds are prepared through Rh-catalyzed cross-coupling between 2-chloro-1,2-azaborines and arylstannanes (see scheme). The synthetic method should enable investigations of structure–activity relationships (SARs) by expanding the chemical space of the pharmaceutically relevant biphenyl structure through BN/CC isosterism. PMID:23832871

Temperature dependent structural properties and bending rigidity of pristine and defective hexagonal boron nitride

NASA Astrophysics Data System (ADS)

Thomas, Siby; Ajith, K. M.; Chandra, Sharat; Valsakumar, M. C.

2015-08-01

Structural and thermodynamical properties of monolayer pristine and defective boron nitride sheets (h-BN) have been investigated in a wide temperature range by carrying out atomistic simulations using a tuned Tersoff-type inter-atomic empirical potential. The temperature dependence of lattice parameter, radial distribution function, specific heat at constant volume, linear thermal expansion coefficient and the height correlation function of the thermally excited ripples on pristine as well as defective h-BN sheet have been investigated. Specific heat shows considerable increase beyond the Dulong-Petit limit at high temperatures, which is interpreted as a signature of strong anharmonicity present in h-BN. Analysis of the height fluctuations, < {{h}2}> , shows that the bending rigidity and variance of height fluctuations are strongly temperature dependent and this is explained using the continuum theory of membranes. A detailed study of the height-height correlation function shows deviation from the prediction of harmonic theory of membranes as a consequence of the strong anharmonicity in h-BN. It is also seen that the variance of the height fluctuations increases with defect concentration.

Impulsivity and test meal intake among women with bulimia nervosa

PubMed Central

Sysko, Robyn; Ojserkis, Rachel; Schebendach, Janet; Evans, Suzette M.; Hildebrandt, Tom; Walsh, B. Timothy

2017-01-01

Many patients with bulimia nervosa (BN) also meet criteria for a lifetime alcohol use disorder (AUD). In order to understand possible mechanisms contributing to the co-occurrence and perpetuation of these disorders, this study investigated the importance of impulsivity and test meal intake among patients with BN by comparing women with BN only (n = 18), BN and current/past AUDs (n = 13), and healthy controls (n = 12). All participants completed assessments of eating disorder symptoms, frequency of alcohol use, binge eating, and purging via questionnaires and semi-structured interviews over two sessions. Measures of impulsivity consisted of computerized and self-report measures, and laboratory test meals. Significant differences between individuals with BN with/without comorbid AUDs were not found for test meal intake, impulsivity measures, or self-reported psychological symptoms. As hypothesized, compared to healthy controls, individuals with BN had significantly higher scores on two subscales and the total score of the Barratt Impulsiveness Scale, a trait measure of impulsivity, and consumed significantly more calories in the binge instruction meal. Total Barratt Impulsiveness Scale scores were also significantly related to kcal consumed during the laboratory test meal when individuals were instructed to binge eat (BN groups). Data from this study add to the existing literature implicating impulsivity in the psychopathology of disorders of binge eating, including BN, and also support the use of laboratory meals as a symptom-specific measure of this trait in eating disorder populations. PMID:28077307

Impulsivity and test meal intake among women with bulimia nervosa.

PubMed

Sysko, Robyn; Ojserkis, Rachel; Schebendach, Janet; Evans, Suzette M; Hildebrandt, Tom; Walsh, B Timothy

2017-05-01

Many patients with bulimia nervosa (BN) also meet criteria for a lifetime alcohol use disorder (AUD). In order to understand possible mechanisms contributing to the co-occurrence and perpetuation of these disorders, this study investigated the importance of impulsivity and test meal intake among patients with BN by comparing women with BN only (n = 18), BN and current/past AUDs (n = 13), and healthy controls (n = 12). All participants completed assessments of eating disorder symptoms, frequency of alcohol use, binge eating, and purging via questionnaires and semi-structured interviews over two sessions. Measures of impulsivity consisted of computerized and self-report measures, and laboratory test meals. Significant differences between individuals with BN with/without comorbid AUDs were not found for test meal intake, impulsivity measures, or self-reported psychological symptoms. As hypothesized, compared to healthy controls, individuals with BN had significantly higher scores on two subscales and the total score of the Barratt Impulsiveness Scale, a trait measure of impulsivity, and consumed significantly more calories in the binge instruction meal. Total Barratt Impulsiveness Scale scores were also significantly related to kcal consumed during the laboratory test meal when individuals were instructed to binge eat (BN groups). Data from this study add to the existing literature implicating impulsivity in the psychopathology of disorders of binge eating, including BN, and also support the use of laboratory meals as a symptom-specific measure of this trait in eating disorder populations. Copyright © 2017 Elsevier Ltd. All rights reserved.

Recent advances in preparation, properties and device applications of two-dimensional h-BN and its vertical heterostructures

NASA Astrophysics Data System (ADS)

Yang, Huihui; Gao, Feng; Dai, Mingjin; Jia, Dechang; Zhou, Yu; Hu, Pingan

2017-03-01

Two-dimensional (2D) layered materials, such as graphene, hexagonal boron nitride (h-BN), molybdenum disulfide (MoS{}2 ), have attracted tremendous interest due to their atom-thickness structures and excellent physical properties. h-BN has predominant advantages as the dielectric substrate in FET devices due to its outstanding properties such as chemically inert surface, being free of dangling bonds and surface charge traps, especially the large-band-gap insulativity. h-BN involved vertical heterostructures have been widely exploited during the past few years. Such heterostructures adopting h-BN as dielectric layers exhibit enhanced electronic performance, and provide further possibilities for device engineering. Besides, a series of intriguing physical phenomena are observed in certain vertical heterostructures, such as superlattice potential induced replication of Dirac points, band gap tuning, Hofstadter butterfly states, gate-dependent pseudospin mixing. Herein we focus on the rapid developments of h-BN synthesis and fabrication of vertical heterostructures devices based on h-BN, and review the novel properties as well as the potential applications of the heterostructures composed of h-BN. Project supported by the National Natural Science Foundation of China (Nos. 61390502, 21373068), the National Basic Research Program of China (No. 2013CB632900), the Foundation for Innovative Research Groups of the National Natural Science Foundation of China (No. 51521003), and the Self-Planned Task of State Key Laboratory of Robotics and System (No. SKLRS201607B).

New bifunctional chelator for 64Cu-immuno-positron emission tomography.

PubMed

Pandya, Darpan N; Bhatt, Nikunj; Dale, Ajit V; Kim, Jung Young; Lee, Hochun; Ha, Yeong Su; Lee, Ji-Eun; An, Gwang Il; Yoo, Jeongsoo

2013-08-21

A new tetraazamacrocyclic bifunctional chelator, TE2A-Bn-NCS, was synthesized in high overall yield from cyclam. An extra functional group (NCS) was introduced to the N-atom of TE2A for specific conjugation with antibody. The Cu complex of TE2A-Bn-NCS showed high kinetic stability in acidic decomplexation and cyclic voltammetry studies. X-ray structure determination of the Cu-TE2A-Bn-NH2 complex confirmed octahedral geometry, in which copper atom is strongly coordinated by four macrocyclic nitrogens in equatorial positions and two carboxylate oxygen atoms occupy the elongated axial positions. Trastuzumab was conjugated with TE2A-Bn-NCS and then radiolabeled with 64Cu quantitatively at room temperature within 10 min. Biodistribution studies showed that the 64Cu-labeled TE2A-Bn-NCS-trastuzumab conjugates maintain high stability in physiological conditions, and NIH3T6.7 tumors were clearly visualized up to 3 days by 64Cu-immuno-positron emission tomography imaging in animal models.

Graphene nanoribbons epitaxy on boron nitride

DOE Office of Scientific and Technical Information (OSTI.GOV)

Lu, Xiaobo; Wang, Shuopei; Wu, Shuang

2016-03-14

In this letter, we report a pilot study on epitaxy of monolayer graphene nanoribbons (GNRs) on hexagonal boron nitride (h-BN). We found that GNRs grow preferentially from the atomic steps of h-BN, forming in-plane heterostructures. GNRs with well-defined widths ranging from ∼15 nm to ∼150 nm can be obtained reliably. As-grown GNRs on h-BN have high quality with a carrier mobility of ∼20 000 cm{sup 2} V{sup −1} s{sup −1} for ∼100-nm-wide GNRs at a temperature of 1.7 K. Besides, a moiré pattern induced quasi-one-dimensional superlattice with a periodicity of ∼15 nm for GNR/h-BN was also observed, indicating zero crystallographic twisting angle between GNRs and h-BNmore » substrate. The superlattice induced band structure modification is confirmed by our transport results. These epitaxial GNRs/h-BN with clean surfaces/interfaces and tailored widths provide an ideal platform for high-performance GNR devices.« less

A first principles approach to magnetic and optical properties in single-layer graphene sandwiched between boron nitride monolayers

NASA Astrophysics Data System (ADS)

Das, Ritwika; Chowdhury, Suman; Jana, Debnarayan

2015-07-01

The dependence of the stability of single-layer graphene (SLG) sandwiched between hexagonal boron nitride bilayers (h-BN) has been described and investigated for different types of stacking in order to provide the fingerprint of the stacking order which affects the optical properties of such trilayer systems. Considering the four stacking models AAA-, AAB-, ABA-, and ABC-type stacking, the static dielectric functions (in case of parallel polarizations) for AAB-type stacking possesses maximum values, and minimum values are noticed for AAA. However, AAA-type stacking structures contribute the maximum magnetic moment while vanishing magnetic moments are observed for ABA and ABC stacking. The observed optical anisotropy and magnetic properties of these trilayer heterostructures (h-BN/SLG/h-BN) can be understood from the crystallographic stacking order and inherent crystal lattice symmetry. These optical and magnetic results suggest that the h-BN/SLG/h-BN could provide a viable route to graphene-based opto-electronic and spintronic devices.

Hexagonal boron nitride cover on Pt(111): a new route to tune molecule-metal interaction and metal-catalyzed reactions.

PubMed

Zhang, Yanhong; Weng, Xuefei; Li, Huan; Li, Haobo; Wei, Mingming; Xiao, Jianping; Liu, Zhi; Chen, Mingshu; Fu, Qiang; Bao, Xinhe

2015-05-13

In heterogeneous catalysis molecule-metal interaction is often modulated through structural modifications at the surface or under the surface of the metal catalyst. Here, we suggest an alternative way toward this modulation by placing a two-dimensional (2D) cover on the metal surface. As an illustration, CO adsorption on Pt(111) surface has been studied under 2D hexagonal boron nitride (h-BN) overlayer. Dynamic imaging data from surface electron microscopy and in situ surface spectroscopic results under near ambient pressure conditions confirm that CO molecules readily intercalate monolayer h-BN sheets on Pt(111) in CO atmosphere but desorb from the h-BN/Pt(111) interface even around room temperature in ultrahigh vacuum. The interaction of CO with Pt has been strongly weakened due to the confinement effect of the h-BN cover, and consequently, CO oxidation at the h-BN/Pt(111) interface was enhanced thanks to the alleviated CO poisoning effect.

Exfoliation of Hexagonal Boron Nitride via Ferric Chloride Intercalation

NASA Technical Reports Server (NTRS)

Hung, Ching-cheh; Hurst, Janet; Santiago, Diana; Rogers, Richard B.

2014-01-01

Sodium fluoride (NaF) was used as an activation agent to successfully intercalate ferric chloride (FeCl3) into hexagonal boron nitride (hBN). This reaction caused the hBN mass to increase by approx.100 percent, the lattice parameter c to decrease from 6.6585 to between 6.6565 and 6.6569 ?, the x-ray diffraction (XRD) (002) peak to widen from 0.01deg to 0.05deg of the full width half maximum value, the Fourier transform infrared (FTIR) spectrum's broad band (1277/cm peak) to change shape, and new FTIR bands to emerge at 3700 to 2700 and 1600/cm. This indicates hBN's structural and chemical properties are significantly changed. The intercalated product was hygroscopic and interacted with moisture in the air to cause further structural and chemical changes (from XRD and FTIR). During a 24-h hold at room temperature in air with 100 percent relative humidity, the mass increased another 141 percent. The intercalated product, hydrated or not, can be heated to 750 C in air to cause exfoliation. Exfoliation becomes significant after two intercalation-air heating cycles, when 20-nm nanosheets are commonly found. Structural and chemical changes indicated by XRD and FTIR data were nearly reversed after the product was placed in hydrochloric acid (HCl), resulting in purified, exfoliated, thin hBN products.

Dynamic consolidation of cubic boron nitride and its admixtures

DOE Office of Scientific and Technical Information (OSTI.GOV)

Tan, H.; Ahrens, T.J.

1988-09-01

Cubic boron nitride (C-BN) powders admixed with graphite-structured boron nitride powder (g-BN), silicon carbide whisker (SCW), or silicon nitride whisker (SNW) were shock compacted to pressures up to 22 GPa. Unlike previous work with diamond and graphite (D. K. Potter and T. J. Ahrens, J. Appl. Phys. 63, 910 (1987)) it was found that the addition of g-BN inhibited dynamic consolidation. Good consolidation was achieved with a 4--8 ..mu..m particle size C-BN powder admixed with 15 wt.% SNW or 20 wt.% SCW. Whereas a 37--44 ..mu..m particle size C-BN mixture was only poorly consolidated. Scanning electron microscopy (SEM) analysis demonstratemore » that SCW and SNW in the mixtures were highly deformed and indicated melt textures. A skin heating model was used to describe the physics of consolidation. Model calculations are consistent with SEM analysis images that indicate plastic deformation of SCW and SNW. Micro-Vickers hardness values as high as 50 GPa were obtained for consolidated C-BN and SNW mixtures. This compares to 21 GPa for single-crystal Al/sub 2/O/sub 3/ and 120 GPa for diamond.« less

Cross-cultural examination of beliefs about the causes of bulimia nervosa among Australian and Japanese females.

PubMed

Dryer, Rachel; Uesaka, Yuri; Manalo, Emmanuel; Tyson, Graham

2015-03-01

To identify similarities and differences in beliefs about the causes of Bulimia Nervosa (BN) held by Asian (Japanese) women and Western (Australian) women, and hence, to examine the applicability of belief models of eating disorders (ED) across different cultures. Four hundred three Japanese and 256 Australian female university students (aged 17-35 years) completed a questionnaire that gauged beliefs about the causes of BN. Among the Australian women, the four-component structure of perceived causes (dieting and eating practices, family dynamics, socio-cultural pressure, and psychological vulnerability) found in Dryer et al. (2012) was replicated. Among the Japanese women, however, a three-component structure (without the psychological vulnerability component) was obtained. The groups also differed in the causal component they most strongly endorsed, that being socio-cultural pressure for the Australian women, and dieting and eating practices for the Japanese women. The Japanese participants were found to endorse three out of the four Western-based causal explanations for BN, but the relative importance they placed on those explanations differed from that of the Australian participants. Further research is needed, particularly to establish whether Japanese women simply fail to see psychological vulnerability as a viable cause of BN, or there are in fact cultural differences in the extent to which such vulnerability causes BN. © 2014 Wiley Periodicals, Inc.

Multilayered BN Coatings Processed by a Continuous LPCVD Treatment onto Hi-Nicalon Fibers

NASA Astrophysics Data System (ADS)

Jacques, S.; Vincent, H.; Vincent, C.; Lopez-Marure, A.; Bouix, J.

2001-12-01

Boron nitride coatings were deposited onto SiC fibers by means of continuous low-pressure chemical vapor deposition (LPCVD) treatment from BF3/NH3 mixtures. This process lies in unrolling the fiber in the reactor axis. The relationships between the processing parameters and the structure of the BN deposits are presented. Thanks to a temperature gradient present in the reactor, multilayered BN films can be performed by stacking successive isotropic and anisotropic sublayers. Tensile tests show that when the temperature profile is well adapted, the SiC fibers are not damaged by the LPCVD treatment.

Anisotropic Nanomechanics of Boron Nitride Nanotubes: Nanostructured "Skin" Effect

NASA Technical Reports Server (NTRS)

Srivastava, Deepak; Menon, Madhu; Cho, KyeongJae

2000-01-01

The stiffness and plasticity of boron nitride nanotubes are investigated using generalized tight-binding molecular dynamics and ab-initio total energy methods. Due to boron-nitride BN bond buckling effects, compressed zigzag BN nanotubes are found to undergo novel anisotropic strain release followed by anisotropic plastic buckling. The strain is preferentially released towards N atoms in the rotated BN bonds. The tubes buckle anisotropically towards only one end when uniaxially compressed from both. A "skin-effect" model of smart nanocomposite materials is proposed which will localize the structural damage towards the 'skin' or surface side of the material.

Research Review: Two Pathways toward impulsive action: an integrative risk model for bulimic behavior in youth

PubMed Central

Pearson, Carolyn M.; Riley, Elizabeth N.; Davis, Heather A.; Smith, Gregory T.

2014-01-01

Background This paper provides an integrative review of existing risk factors and models for bulimia nervosa (BN) in young girls. We offer a new model for BN that describes two pathways of risk that may lead to the initial impulsive act of binge eating and purging in children and adolescents. Scope We conducted a selective literature review, focusing on existing and new risk processes for BN in this select population. Findings We identify two ways in which girls increase their risk to begin engaging in the impulsive behavior of binge eating and purging. The first is state based: the experience of negative mood, in girls attempting to restrain eating, leads to the depletion of self-control and thus increased risk for loss of control eating. The second is personality-based: elevations on the trait of negative urgency, or the tendency to act rashly when distressed, increase risk, particularly in conjunction with high-risk psychosocial learning. We then briefly discuss how these behaviors are reinforced, putting girls at further risk for developing BN. Conclusions We highlight several areas in which further inquiry is necessary, and we discuss the clinical implications of the new risk model we described. PMID:24673546

[Study of cubic boron nitride crystal UV absorption spectroscopy].

PubMed

Liu, Hai-Bo; Jia, Gang; Chen, Gang; Meng, Qing-Ju; Zhang, Tie-Chen

2008-07-01

UV absorption spectroscopy of artificial cubic boron nitride (cBN) single crystal flake, synthesized under high-temperature and high-pressure, was studied in the present paper. UV WINLAB spectrometer was used in the experiments, and MOLECULAR SPECTROSCOPY software was used for data analysis. The UV-cBN limit of 198 nm was showed in this test by a special fixture quartz sample. We calculated the energy gap by virtue of the formula: lambda0 = 1.24/E(g) (microm). The energy gap is 6. 26 eV. There are many viewpoints about the gap of cBN. By using the first-principles theory to calculate energy band structure and density of electronic states of cBN, an indirect transition due to electronics in valence band jumping into conduction band by absorbing photon can be confirmed. That leads to UV absorption. The method of calculation was based on the quantum mechanics of CASTEP in the commercial software package of Cerius2 in the Co. Accerlrys in the United States. The theory of CASTEP is based on local density approximation or gradient corrected LDA. The crystal parameter of cBN was input to the quantum mechanics of CASTEP in order to construct the crystal parameter model of cBN. We calculated the energy gap of cBN by the method of gradient corrected LDA. The method underestimates the value of nonconductor by about 1 to 2 eV. We gaot some opinions as follows: cBN is indirect band semiconductor. The energy gap is 4.76 eV, less than our experiment. The reason may be defect that we ignored in calculating process. It was reported that the results by first principles method of calculation of the band generally was less than the experimental results. This paper shows good UV characteristics of cBN because of the good agreement of experimental results with the cBN band width. That is a kind of development prospect of UV photo-electronic devices and high-temperature semiconductor devices.

Electronic structure of boron based single and multi-layer two dimensional materials

NASA Astrophysics Data System (ADS)

Miyazato, Itsuki; Takahashi, Keisuke

2017-09-01

Two dimensional nanosheets based on boron and Group VA elements are designed and characterized using first principles calculations. B-N, B-P, B-As, B-Sb, and B-Bi are found to possess honeycomb structures where formation energies indicate exothermic reactions. Contrary to B-N, the cases of B-P, B-As, B-Sb, and B-Bi nanosheets are calculated to possess narrow band gaps. In addition, calculations reveal that the electronegativity difference between B and Group VA elements in the designed materials is a good indicator to predict the charge transfer and band gap of the two dimensional materials. Hydrogen adsorption over defect-free B-Sb and B-Bi results in exothermic reactions, while defect-free B-N, B-P, and B-As result in endothermic reactions. The layerability of the designed two dimensional materials is also investigated where the electronic structure of two-layered two dimensional materials is strongly coupled with how the two dimensional materials are layered. Thus, one can consider that the properties of two dimensional materials can be controlled by the composition of two dimensional materials and the structure of layers.

Nanomechanics of Carbon and CxByNz Nanotubes: Via a Quantum Molecular Dynamics Method

NASA Technical Reports Server (NTRS)

Srivastava, Deepak; Menon, M.; Cho, Kyeong Jae; Saini, Subhash (Technical Monitor)

1999-01-01

Nanomechanics of single-wall C, BN and BC$_3$ and B doped C nanotubes under axial compression and tension are investigated through a generalized tight-binding molecular dynamics (GTBMD) and {\\it ab-initio} electronic structure methods. The dynamic strength of BN, BC$_3$ and B doped C nanotubes for small axial strain are comparable to each other. The main difference is in the critical strain at which structural collapse occurs. For example, even a shallow doping with B lowers the value of critical strain for C nanotubes. The critical strain for BN nanotube is found to be more than that for the similar C nanotube. Once the structural collapse starts to occur we find that carbon nanotubes irreversibly go into plastic deformation regime via the formation of tetrahedral (four-fold coordinated) bonds at the location of sharp pinches or kinks. This finding is considerably different from the classical MD (molecular dynamics) simulation results known so far. The energetics and electronic densities of states of the collapsed structures, investigated with {\\it ab-initio) methods, will also be discussed.

Clinical learning experiences of nursing students using an innovative clinical partnership model: A non-randomized controlled trial.

PubMed

Chan, Aileen W K; Tang, Fiona W K; Choi, Kai Chow; Liu, Ting; Taylor-Piliae, Ruth E

2018-06-05

Clinical practicum is a major learning component for pre-registration nursing students. Various clinical practicum models have been used to facilitate students' clinical learning experiences, employing both university-based and hospital-based clinical teachers. Considering the strengths and limitations of these clinical practicum models, along with nursing workforce shortages, we developed and tested an innovative clinical partnership model (CPM) in Hong Kong. To evaluate an innovative CPM among nursing students actual and preferred clinical learning environment, compared with a conventional facilitation model (CFM). A non-randomized controlled trial examining students' clinical experiences, comparing the CPM (supervised by hospital clinical teacher) with the CFM (supervised by university clinical teacher). One university in Hong Kong. Pre-registration nursing students (N = 331), including bachelor of nursing (n = 246 year three-BN) and masters-entry nursing (n = 85 year one-MNSP). Students were assigned to either the CPM (n = 48 BN plus n = 85 MNSP students) or the CFM (n = 198 BN students) for their clinical practice experiences in an acute medical-surgical ward. Clinical teachers supervised between 6 and 8 students at a time, during these clinical practicums (duration = 4-6 weeks). At the end of the clinical practicum, students were invited to complete the Clinical Learning Environment Inventory (CLEI). Analysis of covariance was used to compare groups; adjusted for age, gender and prior work experience. A total of 259 students (mean age = 22 years, 76% female, 81% prior work experience) completed the CLEI (78% response rate). Students had higher scores on preferred versus actual experiences, in all domains of the CLEI. CPM student experiences indicated a higher preferred task orientation (p = 0.004), while CFM student experiences indicated a higher actual (p < 0.001) and preferred individualization (p = 0.005). No significant differences were noted in the other domains. The CPM draws on the strengths of existing clinical learning models and provides complementary methods to facilitate clinical learning for pre-registration nursing students. Additional studies examining this CPM with longer duration of clinical practicum are recommended. Copyright © 2018 Elsevier Ltd. All rights reserved.

Specific comorbidity between bulimia nervosa and personality disorders.

PubMed

Carroll, J M; Touyz, S W; Beumont, P J

1996-03-01

The present study investigates the comorbidity between bulimia nervosa (BN) and the entire range of American Psychiatric Association's Diagnostic and Statistical Manual of Mental Disorders, 3rd rev. ed. (DSM-III-R) personality disorders and controls for the presence of coexisting depression. The Personality Disorders Examination (PDE), a structured interview that encompasses all 13 (provisional) DSM-III-R personality disorders, was administered to three groups of subjects: depressed BN patients (n = 15), nondepressed BN patients (n = 15), and nonpsychiatric controls (n = 15). The BN patients were referrals to a dieting disorder unit affiliated with the University of Sydney. They all met DSM-III-R criteria and all had body mass indexes (BMIs) greater than 19. The nonpsychiatric control group were recruited from an undergraduate psychology course. All subjects were given the Bulimic Investigatory Test, Edinburgh (BITE), the Eating Disorders Inventory-2 (EDI-2), the Hamilton Depression Rating Scale (HDRS), and the PDE. 46.7% of depressed BN patients met the criteria for at least one Axis II diagnosis, as assessed by the PDE, and 33.3% of nondepressed BN patients received such a diagnosis, whereas only 6.7% of nonpsychiatric control subjects met this criterion (p < .05). The results of the present study provide support for an increased comorbidity between personality disorders and BN that cannot be attributed to the confounding influence of coexisting depression. This finding enables the identification of subgroups of individuals with BN, enabling them to be compared and contrasted. The identification of differences between subgroups may provide information regarding prognosis and differential response to treatment, which could enable more appropriate treatment decisions to be made.

Posttraumatic stress disorder as a moderator of the association between negative affect and bulimic symptoms: an ecological momentary assessment study.

PubMed

Karr, Trisha M; Crosby, Ross D; Cao, Li; Engel, Scott G; Mitchell, James E; Simonich, Heather; Wonderlich, Stephen A

2013-01-01

The purpose of this study was to examine the potential moderating effect of posttraumatic stress disorder (PTSD) on the emotion-behavior relationship in individuals with bulimia nervosa (BN). A total of 119 women with BN were involved in the study. Participants were divided into 2 groups: those with BN and PTSD (n = 20) and those with BN only (n = 99). Ecological momentary assessment procedures were used for the examination of affect, frequency of bulimic behaviors, and the relationship of affect and bulimic behavior over time. The Structured Clinical Interview for Diagnostic and Statistical Manual of Mental Disorders, Fourth Edition, Axis I Disorders was conducted for the diagnosis of BN, PTSD, mood disorders, anxiety disorders, and substance use disorders. Mood disorders, anxiety disorders, and substance use disorders functioned as covariates in all analyses. Statistical models showed that those in the PTSD group reported a greater daily mean level of negative affect (NA) and a greater daily frequency of bulimic behaviors than those in the BN-only group. Moderation was found for the association between NA and time in that the PTSD group showed a faster acceleration in NA before purging and faster deceleration in NA after purging. The association between positive affect and time was also moderated by group, indicating that the PTSD group had a faster acceleration in positive affect after purging than the BN-only group. These findings highlight the importance of recognizing PTSD when interpreting the emotion-behavior relationship in individuals with BN. Published by Elsevier Inc.

Genome-Wide Analysis and Expression Profiling of the SUC and SWEET Gene Families of Sucrose Transporters in Oilseed Rape (Brassica napus L.)

PubMed Central

Jian, Hongju; Lu, Kun; Yang, Bo; Wang, Tengyue; Zhang, Li; Zhang, Aoxiang; Wang, Jia; Liu, Liezhao; Qu, Cunmin; Li, Jiana

2016-01-01

Sucrose is the principal transported product of photosynthesis from source leaves to sink organs. SUTs/SUCs (sucrose transporters or sucrose carriers) and SWEETs (Sugars Will Eventually be Exported Transporters) play significant central roles in phloem loading and unloading. SUTs/SUCs and SWEETs are key players in sucrose translocation and are associated with crop yields. The SUT/SUC and SWEET genes have been characterized in several plant species, but a comprehensive analysis of these two gene families in oilseed rape has not yet been reported. In our study, 22 and 68 members of the SUT/SUCs and SWEET gene families, respectively, were identified in the oilseed rape (Brassica napus) genome through homology searches. An analysis of the chromosomal distribution, phylogenetic relationships, gene structures, motifs and the cis-acting regulatory elements in the promoters of BnSUC and BnSWEET genes were analyzed. Furthermore, we examined the expression of the 18 BnSUC and 16 BnSWEET genes in different tissues of “ZS11” and the expression of 9 BnSUC and 7 BnSWEET genes in “ZS11” under various conditions, including biotic stress (Sclerotinia sclerotiorum), abiotic stresses (drought, salt and heat), and hormone treatments (abscisic acid, auxin, cytokinin, brassinolide, gibberellin, and salicylic acid). In conclusion, our study provides the first comprehensive analysis of the oilseed rape SUC and SWEET gene families. Information regarding the phylogenetic relationships, gene structure and expression profiles of the SUC and SWEET genes in the different tissues of oilseed rape helps to identify candidates with potential roles in specific developmental processes. Our study advances our understanding of the important roles of sucrose transport in oilseed rape. PMID:27733861

Ab-initio study of structural and electronic properties of WS2/h-BN van der Waals heterostructure

NASA Astrophysics Data System (ADS)

Ghasemi majd, Zahra; Amiri, Peiman; Taghizadeh, Seyed Fardin

2018-06-01

First-principle calculations with different exchange-correlation functionals, including LDA, GGA, semi-empirical and ab-initio van der Waals in the forms of vdW-DF2B86R and vdW-DF2 were performed to evaluate the performance of different functionals in describing the bonding mechanism, adsorption energy and interlayer distance of WS2 monolayer on and between h-BN layers. The finding was that the vdW-DF2B86R seems to be the approach best lending itself to this purpose. In order to include the van der Waals (vdW) interactions in our calculations, we used the DFT-D2 and vdW methods, which gave rise to a physical adsorption with no net charge transfer between the WS2 layer and the corresponding substrates. In addition, we investigated the electronic and structural properties of WS2 and h-BN heterolayers, using vdW-DF2B86R functional. Based on density functional theory calculations, WS2 on and between h-BN layers showed a direct band gap at the K-point, which was experimentally observed.

Performance analysis of boron nitride embedded armchair graphene nanoribbon metal-oxide-semiconductor field effect transistor with Stone Wales defects

NASA Astrophysics Data System (ADS)

Chanana, Anuja; Sengupta, Amretashis; Mahapatra, Santanu

2014-01-01

We study the performance of a hybrid Graphene-Boron Nitride armchair nanoribbon (a-GNR-BN) n-MOSFET at its ballistic transport limit. We consider three geometric configurations 3p, 3p + 1, and 3p + 2 of a-GNR-BN with BN atoms embedded on either side (2, 4, and 6 BN) on the GNR. Material properties like band gap, effective mass, and density of states of these H-passivated structures are evaluated using the Density Functional Theory. Using these material parameters, self-consistent Poisson-Schrodinger simulations are carried out under the Non Equilibrium Green's Function formalism to calculate the ballistic n-MOSFET device characteristics. For a hybrid nanoribbon of width ˜5 nm, the simulated ON current is found to be in the range of 265 μA-280 μA with an ON/OFF ratio 7.1 × 106-7.4 × 106 for a VDD = 0.68 V corresponding to 10 nm technology node. We further study the impact of randomly distributed Stone Wales (SW) defects in these hybrid structures and only 2.5% degradation of ON current is observed for SW defect density of 3.18%.

First principles-based moiré model for incommensurate graphene on BN

NASA Astrophysics Data System (ADS)

Spataru, Catalin; Thurmer, Konrad

Various properties of supported graphene films depend strongly on the exact positions of carbon atoms with respect to the underlying substrate. While density functional theory (DFT) can predict atom position in many systems, it cannot be applied straightforwardly to systems that are incommensurate or have large unit cells, such as graphene on a BN surface. We address these limitations by developing a simple moiré model with parameters derived from DFT calculations for systems strained into commensurate structures with manageable unit cell sizes. Our moiré model, which takes into account the flexural rigidity of graphene and includes the influence of the substrate, is able to reproduce the DFT-relaxed carbon positions with an accuracy of <0.01 Å. We then apply this model to the unstrained C/BN system and predict how structure and energy vary with azimuthal orientation of the graphene sheet with respect to the BN substrate. Work supported by the Laboratory Directed Research and Development program at Sandia National Laboratories, a multi-program laboratory operated by Sandia Corporation, a Lockheed Martin Co., for the U.S. DOE under Contract DE-AC04-94AL85000.

Multifunctional tunneling devices based on graphene/h-BN/MoSe2 van der Waals heterostructures

NASA Astrophysics Data System (ADS)

Cheng, Ruiqing; Wang, Feng; Yin, Lei; Xu, Kai; Ahmed Shifa, Tofik; Wen, Yao; Zhan, Xueying; Li, Jie; Jiang, Chao; Wang, Zhenxing; He, Jun

2017-04-01

The vertically stacked devices based on van der Waals heterostructures (vdWHs) of two-dimensional layered materials (2DLMs) have attracted considerable attention due to their superb properties. As a typical structure, graphene/hexagonal boron nitride (h-BN)/graphene vdWH has been proved possible to make tunneling devices. Compared with graphene, transition metal dichalcogenides possess intrinsic bandgap, leading to high performance of electronic devices. Here, tunneling devices based on graphene/h-BN/MoSe2 vdWHs are designed for multiple functions. On the one hand, the device shows a typical tunneling field-effect transistor behavior. A high on/off ratio of tunneling current (5 × 103) and an ultrahigh current rectification ratio (7 × 105) are achieved, which are attributed to relatively small electronic affinity of MoSe2 and optimized thickness of h-BN. On the other hand, the same structure also realizes 2D non-volatile memory with a high program/erase current ratio (>105), large memory window (˜150 V from ±90 V), and good retention characteristic. These results could enhance the fundamental understanding of tunneling behavior in vdWHs and contribute to the design of ultrathin rectifiers and memory based on 2DLMs.

Harnessing expert knowledge: Defining a Bayesian network decision model with limited data-Model structure for the vibration qualification problem

DOE Office of Scientific and Technical Information (OSTI.GOV)

Rizzo, Davinia B.; Blackburn, Mark R.

As systems become more complex, systems engineers rely on experts to inform decisions. There are few experts and limited data in many complex new technologies. This challenges systems engineers as they strive to plan activities such as qualification in an environment where technical constraints are coupled with the traditional cost, risk, and schedule constraints. Bayesian network (BN) models provide a framework to aid systems engineers in planning qualification efforts with complex constraints by harnessing expert knowledge and incorporating technical factors. By quantifying causal factors, a BN model can provide data about the risk of implementing a decision supplemented with informationmore » on driving factors. This allows a systems engineer to make informed decisions and examine “what-if” scenarios. This paper discusses a novel process developed to define a BN model structure based primarily on expert knowledge supplemented with extremely limited data (25 data sets or less). The model was developed to aid qualification decisions—specifically to predict the suitability of six degrees of freedom (6DOF) vibration testing for qualification. The process defined the model structure with expert knowledge in an unbiased manner. Finally, validation during the process execution and of the model provided evidence the process may be an effective tool in harnessing expert knowledge for a BN model.« less

Harnessing expert knowledge: Defining a Bayesian network decision model with limited data-Model structure for the vibration qualification problem

DOE PAGES

Rizzo, Davinia B.; Blackburn, Mark R.

2018-03-30

As systems become more complex, systems engineers rely on experts to inform decisions. There are few experts and limited data in many complex new technologies. This challenges systems engineers as they strive to plan activities such as qualification in an environment where technical constraints are coupled with the traditional cost, risk, and schedule constraints. Bayesian network (BN) models provide a framework to aid systems engineers in planning qualification efforts with complex constraints by harnessing expert knowledge and incorporating technical factors. By quantifying causal factors, a BN model can provide data about the risk of implementing a decision supplemented with informationmore » on driving factors. This allows a systems engineer to make informed decisions and examine “what-if” scenarios. This paper discusses a novel process developed to define a BN model structure based primarily on expert knowledge supplemented with extremely limited data (25 data sets or less). The model was developed to aid qualification decisions—specifically to predict the suitability of six degrees of freedom (6DOF) vibration testing for qualification. The process defined the model structure with expert knowledge in an unbiased manner. Finally, validation during the process execution and of the model provided evidence the process may be an effective tool in harnessing expert knowledge for a BN model.« less

Characterization of two-dimensional hexagonal boron nitride using scanning electron and scanning helium ion microscopy

NASA Astrophysics Data System (ADS)

Guo, Hongxuan; Gao, Jianhua; Ishida, Nobuyuki; Xu, Mingsheng; Fujita, Daisuke

2014-01-01

Characterization of the structural and physical properties of two-dimensional (2D) materials, such as layer number and inelastic mean free path measurements, is very important to optimize their synthesis and application. In this study, we characterize the layer number and morphology of hexagonal boron nitride (h-BN) nanosheets on a metallic substrate using field emission scanning electron microscopy (FE-SEM) and scanning helium ion microscopy (HIM). Using scanning beams of various energies, we could analyze the dependence of the intensities of secondary electrons on the thickness of the h-BN nanosheets. Based on the interaction between the scanning particles (electrons and helium ions) and h-BN nanosheets, we deduced an exponential relationship between the intensities of secondary electrons and number of layers of h-BN. With the attenuation factor of the exponential formula, we calculate the inelastic mean free path of electrons and helium ions in the h-BN nanosheets. Our results show that HIM is more sensitive and consistent than FE-SEM for characterizing the number of layers and morphology of 2D materials.

Ab Initio Molecular Dynamics and Lattice Dynamics-Based Force Field for Modeling Hexagonal Boron Nitride in Mechanical and Interfacial Applications.

PubMed

Govind Rajan, Ananth; Strano, Michael S; Blankschtein, Daniel

2018-04-05

Hexagonal boron nitride (hBN) is an up-and-coming two-dimensional material, with applications in electronic devices, tribology, and separation membranes. Herein, we utilize density-functional-theory-based ab initio molecular dynamics (MD) simulations and lattice dynamics calculations to develop a classical force field (FF) for modeling hBN. The FF predicts the crystal structure, elastic constants, and phonon dispersion relation of hBN with good accuracy and exhibits remarkable agreement with the interlayer binding energy predicted by random phase approximation calculations. We demonstrate the importance of including Coulombic interactions but excluding 1-4 intrasheet interactions to obtain the correct phonon dispersion relation. We find that improper dihedrals do not modify the bulk mechanical properties and the extent of thermal vibrations in hBN, although they impact its flexural rigidity. Combining the FF with the accurate TIP4P/Ice water model yields excellent agreement with interaction energies predicted by quantum Monte Carlo calculations. Our FF should enable an accurate description of hBN interfaces in classical MD simulations.

Bandgap renormalization and work function tuning in MoSe2/hBN/Ru(0001) heterostructures.

PubMed

Zhang, Qiang; Chen, Yuxuan; Zhang, Chendong; Pan, Chi-Ruei; Chou, Mei-Yin; Zeng, Changgan; Shih, Chih-Kang

2016-12-14

The van der Waals interaction in vertical heterostructures made of two-dimensional (2D) materials relaxes the requirement of lattice matching, therefore enabling great design flexibility to tailor novel 2D electronic systems. Here we report the successful growth of MoSe 2 on single-layer hexagonal boron nitride (hBN) on the Ru(0001) substrate using molecular beam epitaxy. Using scanning tunnelling microscopy and spectroscopy, we found that the quasi-particle bandgap of MoSe 2 on hBN/Ru is about 0.25 eV smaller than those on graphene or graphite substrates. We attribute this result to the strong interaction between hBN/Ru, which causes residual metallic screening from the substrate. In addition, the electronic structure and the work function of MoSe 2 are modulated electrostatically with an amplitude of ∼0.13 eV. Most interestingly, this electrostatic modulation is spatially in phase with the Moiré pattern of hBN on Ru(0001) whose surface also exhibits a work function modulation of the same amplitude.

The role of depression and impulsivity in the psychopathology of bulimia nervosa.

PubMed

Vaz-Leal, Francisco J; Rodríguez-Santos, Laura; García-Herráiz, M Angustias; Chimpén-López, Carlos A; Rojo-Moreno, Luís; Beato-Fernández, Luís; Ramos-Fuentes, María Isabel

2014-01-01

The study aimed to analyze the role of depression and impulsivity in the psychopathology of bulimia nervosa (BN). Seventy female patients with DSM-IV BN, purging subtype, were assessed for eating-related symptoms, body dissatisfaction, affective symptoms, impulsivity, and personality traits. Factor analysis and structural equation modeling methods were used for statistical analysis. BN appeared as a condition which incorporated 5 general dimensions: a) binge eating and compensatory behaviours; b) restrictive eating; c) body dissatisfaction; d) dissocial personality traits; and e) a cluster of features which was called «emotional instability» The 5 obtained dimensions can be grouped into 2 basic factors: body dissatisfaction/eating behaviour and personality traits/psychopathology. The first one contains the clinical items used for the definition of BN as a clinical condition in the DSM-V and the International Classification of Diseases 10, and reflects the morphology and the severity of the eating-related symptoms. The second dimension includes a cluster of symptoms (depressive symptoms, impulsivity, and borderline, self-defeating and dissocial personality traits) which could be regarded as the «psychopathological core» of BN and may be able to condition the course and the prognosis of BN. Copyright © 2013 SEP y SEPB. Published by Elsevier España. All rights reserved.

Magnetization distribution and spin transport of graphene/h-BN/graphene nanoribbon-based magnetic tunnel junction

NASA Astrophysics Data System (ADS)

Zhang, Y.; Yan, X. H.; Guo, Y. D.; Xiao, Y.

2017-09-01

Motivated by recent electronic transport measurement of boron nitride-graphene hybrid atomic layers, we studied magnetization distribution, transmission and current-bias relation of graphene/h-BN/graphene (C/BN/C) nanoribbon-based magnetic tunnel junctions (MTJ) based on density functional theory and non-equilibrium Green's function methods. Three types of MTJs, i.e. asymmetric, symmetric (S) and symmetric (SS), and two types of lead magnetization alignment, i.e. parallel (PC) and antiparallel (APC), are considered. The results show that the magnetization distribution is closely related to the interface structure. Especially for asymmetric MTJ, the B/N atoms at the C/BN interface are spin-polarized and give finite magnetic moments. More interesting, it is found that the APC transmission of asymmetric MTJ with the thinnest barrier dominates over the PC one. By analyzing the projected density of states, one finds that the unusual higher APC transmission than PC is due to the coupling of electronic states of left ZGNR and right ZGNR. By integrating transmission, we calculate the current-bias voltage relation and find that the APC current is larger than PC current at small bias voltage and therefore reproduces a negative tunnel magnetoresistance. The results reported here will be useful and important for the design of C/BN/C-based MTJ.

Computational simulation of subatomic-resolution AFM and STM images for graphene/hexagonal boron nitride heterostructures with intercalated defects

NASA Astrophysics Data System (ADS)

Lee, Junsu; Kim, Minjung; Chelikowsky, James R.; Kim, Gunn

2016-07-01

Using ab initio density functional calculations, we predict subatomic-resolution atomic force microscopy (AFM) and scanning tunneling microscopy (STM) images of vertical heterostructures of graphene/hexagonal boron nitride (h-BN) with an intercalated metal atom (Li, K, Cr, Mn, Co, or Cu), and study the effects of the extrinsic metal defect on the interfacial coupling. We find that the structural deformation of the graphene/h-BN layer caused by the metal defect strongly affects the AFM images, whereas orbital hybridization between the metal defect and the graphene/h-BN layer characterizes the STM images.

Core structure and dynamics of non-Abelian vortices in a biaxial nematic spinor Bose-Einstein condensate

NASA Astrophysics Data System (ADS)

Borgh, Magnus O.; Ruostekoski, Janne

2016-05-01

We demonstrate that multiple interaction-dependent defect core structures as well as dynamics of non-Abelian vortices can be realized in the biaxial nematic (BN) phase of a spin-2 atomic Bose-Einstein condensate (BEC). An experimentally simple protocol may be used to break degeneracy with the uniaxial nematic phase. We show that a discrete spin-space symmetry in the core may be reflected in a breaking of its spatial symmetry. The discrete symmetry of the BN order parameter leads to non-commuting vortex charges. We numerically simulate reconnection of non-Abelian vortices, demonstrating formation of the obligatory rung vortex. In addition to atomic BECs, non-Abelian vortices are theorized in, e.g., liquid crystals and cosmic strings. Our results suggest the BN spin-2 BEC as a prime candidate for their realization. We acknowledge financial support from the EPSRC.

Quantum interference on electron scattering in graphene by carbon impurities in underlying h -BN

NASA Astrophysics Data System (ADS)

Kaneko, Tomoaki; Koshino, Mikito; Saito, Riichiro

2017-03-01

Electronic structures and transport properties of graphene on h -BN with carbon impurities are investigated by first-principles calculation and the tight-binding model. We show that the coupling between the impurity level and the graphene's Dirac cone sensitively depends on the impurity position, and in particular, it nearly vanishes when the impurity is located right below the center of the six membered ring of graphene. The Bloch phase factor at the Brillouin zone edge plays a decisive role in the cancellation of the hopping integrals. The impurity position dependence on the electronic structures of graphene on h -BN is investigated by the first-principles calculation, and its qualitative feature is well explained by a tight-binding model with graphene and a single impurity site. We also propose a simple one-dimensional chain-impurity model to analytically describe the role of the quantum interference in the position-dependent coupling.

Cytotoxicity and Efflux Pump Inhibition Induced by Molybdenum Disulfide and Boron Nitride Nanomaterials with Sheetlike Structure.

PubMed

Liu, Su; Shen, Zhuoyan; Wu, Bing; Yu, Yue; Hou, Hui; Zhang, Xu-Xiang; Ren, Hong-Qiang

2017-09-19

Sheetlike molybdenum disulfide (MoS 2 ) and boron nitride (BN) nanomaterials have attracted attention in the past few years due to their unique material properties. However, information on adverse effects and their underlying mechanisms for sheetlike MoS 2 and BN nanomaterials is rare. In this study, cytotoxicities of sheetlike MoS 2 and BN nanomaterials on human hepatoma HepG2 cells were systematically investigated at different toxic end points. Results showed that MoS 2 and BN nanomaterials decreased cell viability at 30 μg/mL and induced adverse effects on intracellular ROS generation (≥2 μg/mL), mitochondrial depolarization (≥4 μg/mL), and membrane integrity (≥8 μg/mL for MoS 2 and ≥2 μg/mL for BN). Furthermore, this study first found that low exposure concentrations (0.2-2 μg/mL) of MoS 2 and BN nanomaterials could increase plasma membrane fluidity and inhibit transmembrane ATP binding cassette (ABC) efflux transporter activity, which make both nanomaterials act as a chemosensitizer (increasing arsenic toxicity). Damage to plasma membrane and release of soluble Mo or B species might be two reasons that both nanomaterials inhibit efflux pump activities. This study provides a systematic understanding of the cytotoxicity of sheetlike MoS 2 and BN nanomaterials at different exposure levels, which is important for their safe use.

The economic-impact fallacy

NASA Astrophysics Data System (ADS)

Moriarty, Philip

2009-06-01

Before the UK budget was announced in April, there had been excited expectations of an "Obama-style" £1bn stimulus package for science. That prospect prompted research councils and learned societies in the UK to rush to identify "shovel-ready" projects that could benefit from a fresh injection of funds. However, their efforts were in vain - the stimulus did not arrive. Instead, John Denham, secretary of state for Innovation, Universities and Skills, has had to put a brave face on an immensely disappointing budget settlement for science. The Department for Innovation, Universities and Skills (DIUS), which Denham runs, must now make £0.5bn in savings over the next two years.

Electron transport in polycyclic aromatic hydrocarbons/boron nitride hybrid structures: density functional theory combined with the nonequilibrium Green's function.

PubMed

Panahi, S F K S; Namiranian, Afshin; Soleimani, Maryam; Jamaati, Maryam

2018-02-07

We investigate the electronic transport properties of two types of junction based on single polyaromatic hydrocarbons (PAHs) and PAHs embedded in boron nitride (h-BN) nanoribbons, using nonequilibrium Green's functions (NEGF) and density functional theory (DFT). In the PAH junctions, a Fano resonance line shape at the Fermi energy in the transport feature can be clearly seen. In hybrid junctions, structural asymmetries enable interactions between the electronic states, leading to observation of interface-based transport. Our findings reveal that the interface of PAH/h-BN strongly affects the transport properties of the structures.

On the structure of transition metals complexes with the new tridentate dye of thiazole series: Theoretical and experimental studies

NASA Astrophysics Data System (ADS)

Fizer, Maksym; Sidey, Vasyl; Tupys, Andrii; Ostapiuk, Yurii; Tymoshuk, Oleksandr; Bazel, Yaroslav

2017-12-01

The 1-[(5-Benzyl-1,3-thiazol-2-yl)diazenyl]naphthalene-2-ol (BnTAN) is a recently synthesized azo dye that can act as a tridentate ligand in complexes with transition metals. In a series of previous works, this analytical reagent was shown to be applicable for selective, reliable, express and relatively inexpensive determination of heavy metals in different objects through the spectrophotometric technique. Although the action of 1-(2-thiazolylazo)-2-naphthol (TAN) dyes as tridentate ligands has been suggested in the literature long time ago, due to the lack of experimental data, it was necessary to investigate the mechanism of formation and the structure of BnTAN complexes with the such transition metals as Cu(II), Zn(II) and Cd(II). Furthermore, the reactivity and properties of different acidity forms and conformers of BnTAN and related TAN dyes were not fully defined, so the determination of these properties by analysis of wavefunction was also necessary. Two standard spectrophotometric methods and voltammetric technique were used to determine the composition of complex of BnTAN with metals ions. All three experimental methods indicate that coordination ratio of metal:dye is equal to 1:2. Moreover, this study reports the stability and geometry of conformers of different forms (anionic/neutral/cationic) of BnTAN, along with a detailed analysis of electronic properties, reactivity and aromaticity of the most stable conformers of BnTAN forms. Each of the above forms has some difference in position of benzyl ring against the thiazole moiety, which is explained in terms of attraction and repulsion of these two fragments induced by partial atomic charges. The crucial influence of hydrogen bond and weak non-covalent interactions between naphthyl, aza- and thiazolyl fragments has been established. The quantum chemical calculations have shown that partial atomic charges of anionic, neutral and cationic forms can explain the reactivity of each BnTAN form, and have also clarified the mechanism of formation of metal complex through the connection of metal with phenol oxygen, thiazolyl nitrogen and one nitrogen of aza group - thus giving two five-membered metal-containing cycles and confirming that BnTAN acts as a tridentate ligand. The obtained results introduce novel and crucial information which can assist in understanding the mechanism of complex formation of BnTAN and display the strength and level of detail of applying quantum chemical methods to reveal the reactivity, energy properties, and electronic properties of this new dye.

Multiple NUCLEAR FACTOR Y transcription factors respond to abiotic stress in Brassica napus L.

PubMed

Xu, Li; Lin, Zhongyuan; Tao, Qing; Liang, Mingxiang; Zhao, Gengmao; Yin, Xiangzhen; Fu, Ruixin

2014-01-01

Members of the plant NUCLEAR FACTOR Y (NF-Y) family are composed of the NF-YA, NF-YB, and NF-YC subunits. In Brassica napus (canola), each of these subunits forms a multimember subfamily. Plant NF-Ys were reported to be involved in several abiotic stresses. In this study, we demonstrated that multiple members of thirty three BnNF-Ys responded rapidly to salinity, drought, or ABA treatments. Transcripts of five BnNF-YAs, seven BnNF-YBs, and two BnNF-YCs were up-regulated by salinity stress, whereas the expression of thirteen BnNF-YAs, ten BnNF-YBs, and four BnNF-YCs were induced by drought stress. Under NaCl treatments, the expression of one BnNF-YA10 and four NF-YBs (BnNF-YB3, BnNF-YB7, BnNF-YB10, and BnNF-YB14) were greatly increased. Under PEG treatments, the expression levels of four NF-YAs (BnNF-YA9, BnNF-YA10, BnNF-YA11, and BnNF-YA12) and five NF-YBs (BnNF-YB1, BnNF-YB8, BnNF-YB10, BnNF-YB13, and BnNF-YB14) were greatly induced. The expression profiles of 20 of the 27 salinity- or drought-induced BnNF-Ys were also affected by ABA treatment. The expression levels of six NF-YAs (BnNF-YA1, BnNF-YA7, BnNF-YA8, BnNF-YA9, BnNF-YA10, and BnNF-YA12) and seven BnNF-YB members (BnNF-YB2, BnNF-YB3, BnNF-YB7, BnNF-YB10, BnNF-YB11, BnNF-YB13, and BnNF-YB14) and two NF-YC members (BnNF-YC2 and BnNF-YC3) were greatly up-regulated by ABA treatments. Only a few BnNF-Ys were inhibited by the above three treatments. Several NF-Y subfamily members exhibited collinear expression patterns. The promoters of all stress-responsive BnNF-Ys harbored at least two types of stress-related cis-elements, such as ABRE, DRE, MYB, or MYC. The cis-element organization of BnNF-Ys was similar to that of Arabidopsis thaliana, and the promoter regions exhibited higher levels of nucleotide sequence identity with Brassica rapa than with Brassica oleracea. This work represents an entry point for investigating the roles of canola NF-Y proteins during abiotic stress responses and provides insight into the genetic evolution of Brassica NF-Ys.

Controllable poly-crystalline bilayered and multilayered graphene film growth by reciprocal chemical vapor deposition

NASA Astrophysics Data System (ADS)

Wu, Qinke; Jung, Seong Jun; Jang, Sung Kyu; Lee, Joohyun; Jeon, Insu; Suh, Hwansoo; Kim, Yong Ho; Lee, Young Hee; Lee, Sungjoo; Song, Young Jae

2015-06-01

We report the selective growth of large-area bilayered graphene film and multilayered graphene film on copper. This growth was achieved by introducing a reciprocal chemical vapor deposition (CVD) process that took advantage of an intermediate h-BN layer as a sacrificial template for graphene growth. A thin h-BN film, initially grown on the copper substrate using CVD methods, was locally etched away during the subsequent graphene growth under residual H2 and CH4 gas flows. Etching of the h-BN layer formed a channel that permitted the growth of additional graphene adlayers below the existing graphene layer. Bilayered graphene typically covers an entire Cu foil with domain sizes of 10-50 μm, whereas multilayered graphene can be epitaxially grown to form islands a few hundreds of microns in size. This new mechanism, in which graphene growth proceeded simultaneously with h-BN etching, suggests a potential approach to control graphene layers for engineering the band structures of large-area graphene for electronic device applications.We report the selective growth of large-area bilayered graphene film and multilayered graphene film on copper. This growth was achieved by introducing a reciprocal chemical vapor deposition (CVD) process that took advantage of an intermediate h-BN layer as a sacrificial template for graphene growth. A thin h-BN film, initially grown on the copper substrate using CVD methods, was locally etched away during the subsequent graphene growth under residual H2 and CH4 gas flows. Etching of the h-BN layer formed a channel that permitted the growth of additional graphene adlayers below the existing graphene layer. Bilayered graphene typically covers an entire Cu foil with domain sizes of 10-50 μm, whereas multilayered graphene can be epitaxially grown to form islands a few hundreds of microns in size. This new mechanism, in which graphene growth proceeded simultaneously with h-BN etching, suggests a potential approach to control graphene layers for engineering the band structures of large-area graphene for electronic device applications. Electronic supplementary information (ESI) available: The growth conditions, statistical studies of OM images and high-resolution STM/TEM measurements for multi-/bi-layered graphene are discussed in detail. See DOI: 10.1039/c5nr02716k

A Risk and Maintenance Model for Bulimia Nervosa: From Impulsive Action to Compulsive Behavior

PubMed Central

Pearson, Carolyn M.; Wonderlich, Stephen A.; Smith, Gregory T.

2015-01-01

This paper offers a new model for bulimia nervosa (BN) that explains both the initial impulsive nature of binge eating and purging as well as the compulsive quality of the fully developed disorder. The model is based on a review of advances in research on BN and advances in relevant basic psychological science. It integrates transdiagnostic personality risk, eating disorder specific risk, reinforcement theory, cognitive neuroscience, and theory drawn from the drug addiction literature. We identify both a state-based and a trait-based risk pathway, and we then propose possible state-by-trait interaction risk processes. The state-based pathway emphasizes depletion of self-control. The trait-based pathway emphasizes transactions between the trait of negative urgency (the tendency to act rashly when distressed) and high-risk psychosocial learning. We then describe a process by which initially impulsive BN behaviors become compulsive over time, and we consider the clinical implications of our model. PMID:25961467

nBn Infrared Detector Containing Graded Absorption Layer

NASA Technical Reports Server (NTRS)

Gunapala, Sarath D.; Ting, David Z.; Hill, Cory J.; Bandara, Sumith V.

2009-01-01

It has been proposed to modify the basic structure of an nBn infrared photodetector so that a plain electron-donor- type (n-type) semiconductor contact layer would be replaced by a graded n-type III V alloy semiconductor layer (i.e., ternary or quarternary) with appropriate doping gradient. The abbreviation nBn refers to one aspect of the unmodified basic device structure: There is an electron-barrier ("B" ) layer between two n-type ("n" ) layers, as shown in the upper part of the figure. One of the n-type layers is the aforementioned photon-absorption layer; the other n-type layer, denoted the contact layer, collects the photocurrent. The basic unmodified device structure utilizes minority-charge-carrier conduction, such that, for reasons too complex to explain within the space available for this article, the dark current at a given temperature can be orders of magnitude lower (and, consequently, signal-to-noise ratios can be greater) than in infrared detectors of other types. Thus, to obtain a given level of performance, less cooling (and, consequently, less cooling equipment and less cooling power) is needed. [In principle, one could obtain the same advantages by means of a structure that would be called pBp because it would include a barrier layer between two electron-acceptor- type (p-type) layers.] The proposed modifications could make it practical to utilize nBn photodetectors in conjunction with readily available, compact thermoelectric coolers in diverse infrared- imaging applications that could include planetary exploration, industrial quality control, monitoring pollution, firefighting, law enforcement, and medical diagnosis.

A triallelic genetic male sterility locus in Brassica napus: an integrative strategy for its physical mapping and possible local chromosome evolution around it

PubMed Central

Lu, Wei; Liu, Jun; Xin, Qiang; Wan, Lili; Hong, Dengfeng; Yang, Guangsheng

2013-01-01

Background and Aims Spontaneous male sterility is an advantageous trait for both constructing efficient pollination control systems and for understanding the developmental process of the male reproductive unit in many crops. A triallelic genetic male-sterile locus (BnMs5) has been identified in Brassica napus; however, its complicated genome structure has greatly hampered the isolation of this locus. The aim of this study was to physically map BnMs5 through an integrated map-based cloning strategy and analyse the local chromosomal evolution around BnMs5. Methods A large F2 population was used to integrate the existing genetic maps around BnMs5. A map-based cloning strategy in combination with comparative mapping among B. napus, Arabidopsis, Brassica rapa and Brassica oleracea was employed to facilitate the identification of a target bacterial artificial chromosome (BAC) clone covering the BnMs5 locus. The genomic sequences from the Brassica species were analysed to reveal the regional chromosomal evolution around BnMs5. Key Results BnMs5 was finally delimited to a 0·3-cM genetic fragment from an integrated local genetic map, and was anchored on the B. napus A8 chromosome. Screening of a B. napus BAC clone library and identification of the positive clones validated that JBnB034L06 was the target BAC clone. The closest flanking markers restrict BnMs5 to a 21-kb region on JBnB034L06 containing six predicted functional genes. Good collinearity relationship around BnMs5 between several Brassica species was observed, while violent chromosomal evolutionary events including insertions/deletions, duplications and single nucleotide mutations were also found to have extensively occurred during their divergence. Conclusions This work represents major progress towards the molecular cloning of BnMs5, as well as presenting a powerful, integrative method to mapping loci in plants with complex genomic architecture, such as the amphidiploid B. napus. PMID:23243189

Transition metal atoms absorbed on MoS2/h-BN heterostructure: stable geometries, band structures and magnetic properties.

PubMed

Wu, Yanbing; Huang, Zongyu; Liu, Huating; He, Chaoyu; Xue, Lin; Qi, Xiang; Zhong, Jianxin

2018-06-15

We have studied the stable geometries, band structures and magnetic properties of transition-metal (V, Cr, Mn, Fe, Co and Ni) atoms absorbed on MoS2/h-BN heterostructure systems by first-principles calculations. By comparing the adsorption energies, we find that the adsorbed transition metal (TM) atoms prefer to stay on the top of Mo atoms. The results of the band structure without spin-orbit coupling (SOC) interaction indicate that the Cr-absorbed systems behave in a similar manner to metals, and the Co-absorbed system exhibits a half-metallic state. We also deduce that the V-, Mn-, Fe-absorbed systems are semiconductors with 100% spin polarization at the HOMO level. The Ni-absorbed system is a nonmagnetic semiconductor. In contrast, the Co-absorbed system exhibits metallic state, and the bandgap of V-absorbed system decreases slightly according to the SOC calculations. In addition, the magnetic moments of all the six TM atoms absorbed on the MoS2/h-BN heterostructure systems decrease when compared with those of their free-standing states.

Assessment of personality disorders in anorexia nervosa and bulimia nervosa. A comparison of self-report and structured interview methods.

PubMed

Kennedy, S H; Katz, R; Rockert, W; Mendlowitz, S; Ralevski, E; Clewes, J

1995-06-01

Interest in assessing Personality Disorders (PDs) in association with anorexia nervosa (AN) and bulimia nervosa (BN) has been accompanied by the development of several structured interview and self-report measures. In an attempt to see how the self-report Millon Clinical Multiaxial Inventory (MCMI-II) compared with the Structured Clinical Interview for DSM-III-R (SCID-II) in the assessment of PDs, we gave both instruments to 43 inpatients with a diagnosis of AN or BN. Correlation coefficient values for both categorical and dimensional comparisons were generally less than .4. Although comparable rates of positive PDs occurred for each of the three clusters (A: 30.2% vs. 34.9%, B: 25.6% vs. 18.6%, and C: 62.8% vs. 81.4% for SCID-II vs. MCMI-II), agreement for individual diagnosis and individual subjects was poor. In conclusion, the MCMI-II did not prove to be a reliable instrument for assessing axis II PDs in patients with AN and BN when compared with the SCID-II.

Structural characterization of viral epitopes recognized by broadly cross-reactive antibodies.

PubMed

Lee, Peter S; Wilson, Ian A

2015-01-01

Influenza hemagglutinin (HA) is the major surface glycoprotein on influenza viruses and mediates viral attachment and subsequent fusion with host cells. The HA is the major target of the immune response, but due to its high level of variability, as evidenced by substantial antigenic diversity, it had been historically considered to elicit only a narrow, strain-specific antibody response. However, a recent explosion in the discovery of broadly neutralizing antibodies (bnAbs) to influenza virus has identified two major supersites of vulnerability on the HA through structural characterization of HA-antibody complexes. These commonly targeted epitopes are involved with receptor binding as well as the fusion machinery and, hence, are functionally conserved and less prone to mutation. These bnAbs can neutralize viruses by blocking infection or the spread of infection by preventing progeny release. Structural analyses of these bnAbs show they exhibit striking similarities and trends in recognition of the HA and use recurring recognition motifs, despite substantial differences in their germline genes. This information can be utilized in design of novel therapeutics as well as in immunogens for improved vaccines with greater breadth and efficacy.

A template for constructing Bayesian networks in forensic biology cases when considering activity level propositions.

PubMed

Taylor, Duncan; Biedermann, Alex; Hicks, Tacha; Champod, Christophe

2018-03-01

The hierarchy of propositions has been accepted amongst the forensic science community for some time. It is also accepted that the higher up the hierarchy the propositions are, against which the scientist are competent to evaluate their results, the more directly useful the testimony will be to the court. Because each case represents a unique set of circumstances and findings, it is difficult to come up with a standard structure for evaluation. One common tool that assists in this task is Bayesian networks (BNs). There is much diversity in the way that BN can be constructed. In this work, we develop a template for BN construction that allows sufficient flexibility to address most cases, but enough commonality and structure that the flow of information in the BN is readily recognised at a glance. We provide seven steps that can be used to construct BNs within this structure and demonstrate how they can be applied, using a case example. Copyright © 2017 The Authors. Published by Elsevier B.V. All rights reserved.

Recognition of O6-benzyl-2′-deoxyguanosine by a perimidinone-derived synthetic nucleoside: a DNA interstrand stacking interaction

PubMed Central

Kowal, Ewa A.; Lad, Rahul R.; Pallan, Pradeep S.; Dhummakupt, Elizabeth; Wawrzak, Zdzislaw; Egli, Martin; Sturla, Shana J.; Stone, Michael P.

2013-01-01

The 2′-deoxynucleoside containing the synthetic base 1-[(2R,4S,5R)-4-hydroxy-5-(hydroxymethyl)-tetrahydrofuran-2-yl)-1H-perimidin-2(3H)-one] (dPer) recognizes in DNA the O6-benzyl-2′-deoxyguanosine nucleoside (O6-Bn-dG), formed by exposure to N-benzylmethylnitrosamine. Herein, we show how dPer distinguishes between O6-Bn-dG and dG in DNA. The structure of the modified Dickerson–Drew dodecamer (DDD) in which guanine at position G4 has been replaced by O6-Bn-dG and cytosine C9 has been replaced with dPer to form the modified O6-Bn-dG:dPer (DDD-XY) duplex [5′-d(C1G2C3X4A5A6T7T8Y9G10C11G12)-3′]2 (X = O6-Bn-dG, Y = dPer) reveals that dPer intercalates into the duplex and adopts the syn conformation about the glycosyl bond. This provides a binding pocket that allows the benzyl group of O6-Bn-dG to intercalate between Per and thymine of the 3′-neighbor A:T base pair. Nuclear magnetic resonance data suggest that a similar intercalative recognition mechanism applies in this sequence in solution. However, in solution, the benzyl ring of O6-Bn-dG undergoes rotation on the nuclear magnetic resonance time scale. In contrast, the structure of the modified DDD in which cytosine at position C9 is replaced with dPer to form the dG:dPer (DDD-GY) [5′-d(C1G2C3G4A5A6T7T8Y9G10C11G12)-3′]2 duplex (Y = dPer) reveals that dPer adopts the anti conformation about the glycosyl bond and forms a less stable wobble pairing interaction with guanine. PMID:23748954

Magnitude of the current in 2D interlayer tunneling devices.

PubMed

Feenstra, Randall M; de la Barrera, Sergio C; Li, Jun; Nie, Yifan; Cho, Kyeongjae

2018-01-15

Using the Bardeen tunneling method with first-principles wave functions, computations are made of the tunneling current in graphene/hexagonal-boron-nitride/graphene (G/h-BN/G) vertical structures. Detailed comparison with prior experimental results is made, focusing on the magnitude of the achievable tunnel current. With inclusion of the effects of translational and rotational misalignment of the graphene and the h-BN, predicted currents are found to be about 15×  larger than experimental values. A reduction in this discrepancy, to a factor of 2.5×, is achieved by utilizing a realistic size for the band gap of the h-BN, hence affecting the exponential decay constant for the tunneling.

Magnitude of the Current in Two-Dimensional Interlayer Tunneling Devices.

PubMed

Feenstra, Randall; de la Barrera, Sergio; Li, Jun; Nie, Yifan; Cho, Kyeongjae

2018-01-02

Using the Bardeen tunneling method with first-principles wave functions, computations are made of the tunneling current in graphene / hexagonal-boron-nitride / graphene (G/h-BN/G) vertical structures. Detailed comparison with prior experimental results is made, focusing on the magnitude of the achievable tunnel current. With inclusion of the effects of translational and rotational misalignment of the graphene and the h-BN, predicted currents are found to be about 15x larger than experimental values. A reduction in this discrepancy, to a factor of 2.5x, is achieved by utilizing a realistic size for the band gap of the h-BN, hence affecting the exponential decay constant for the tunneling. © 2018 IOP Publishing Ltd.

Solution properties and spectroscopic characterization of polymeric precursors to SiNCB and BN ceramic materials

NASA Astrophysics Data System (ADS)

Cortez, E.; Remsen, E.; Chlanda, V.; Wideman, T.; Zank, G.; Carrol, P.; Sneddon, L.

1998-06-01

Boron Nitride, BN, and composite SiNCB ceramic fibers are important structural materials because of their excellent thermal and oxidative stabilities. Consequently, polymeric materials as precursors to ceramic composites are receiving increasing attention. Characterization of these materials requires the ability to evaluate simultaneous molecular weight and compositional heterogeneity within the polymer. Size exclusion chromatography equipped with viscometric and refractive index detection as well as coupled to a LC-transform device for infrared absorption analysis has been employed to examine these heterogeneities. Using these combined approaches, the solution properties and the relative amounts of individual functional groups distributed through the molecular weight distribution of SiNCB and BN polymeric precursors were characterized.

Seasonal patterns of birth for subjects with bulimia nervosa, binge eating, and purging: results from the National Women's Study.

PubMed

Brewerton, Timothy D; Dansky, Bonnie S; O'Neil, Patrick M; Kilpatrick, Dean G

2012-01-01

Studies of birth patterns in anorexia nervosa have shown relative increases between March and August, while studies in Bulimia Nervosa (BN) have been negative. Since there are no studies using representative, nonclinical samples, we looked for seasonal birth patterns in women with BN and in those who ever endorsed bingeing or purging. A national, representative sample of 3,006 adult women completed structured telephone interviews including screenings for bulimia nervosa (BN) and questions about month, date, and year of birth. Season of birth was calculated using traditional definitions. Differences across season of birth between subjects with (n = 85) and without BN (n = 2,898), those with (n = 749) and without bingeing (n = 2,229), and those with (n = 267) and without any purging (n = 2,715) were compared using chi-square analyses. There were significant differences across season of birth between subjects: (1) with and without BN (p = 0.033); (2) with and without bingeing (p = 0.034), and; (3) with and without purging (p = 0.001). Fall had the highest relative number of births for all categories, while spring had the lowest. In a national representative study of nontreatment seeking subjects significant differences in season of birth were found for subjects with lifetime histories of BN, binge eating and purging. © 2011 by Wiley Periodicals, Inc. (Int J Eat Disord 2012). Copyright © 2011 Wiley Periodicals, Inc.

The direct exchange mechanism of induced spin polarization of low-dimensional π-conjugated carbon- and h-BN fragments at LSMO(001) MnO-terminated interfaces

NASA Astrophysics Data System (ADS)

Kuklin, Artem V.; Kuzubov, Alexander A.; Kovaleva, Evgenia A.; Lee, Hyosun; Sorokin, Pavel B.; Sakai, Seiji; Entani, Shiro; Naramoto, Hiroshi; Avramov, Paul

2017-10-01

Induced spin polarization of π-conjugated carbon and h-BN low dimensional fragments at the interfaces formed by deposition of pentacene molecule and narrow zigzag graphene and h-BN nanoribbons on MnO2-terminated LSMO(001) thin film was studied using GGA PBE+U PAW D3-corrected approach. Induced spin polarization of π-conjugated low-dimensional fragments is caused by direct exchange with Mn ions of LSMO(001) MnO-derived surface. Due to direct exchange, the pentacene molecule changes its diamagnetic narrow-band gap semiconducting nature to the ferromagnetic semiconducting state with 0.15 eV energy shift between spin-up and spin-down valence bands and total magnetic moment of 0.11 μB. Direct exchange converts graphene nanoribbon to 100% spin-polarized half-metal with large amplitude of spin-up electronic density at the Fermi level. The direct exchange narrows the h-BN nanoribbon band gap from 4.04 to 1.72 eV in spin-up channel and converts the h-BN ribbon semiconducting diamagnetic nature to a semiconducting magnetic one. The electronic structure calculations demonstrate a possibility to control the spin properties of low-dimensional π-conjugated carbon and h-BN fragments by direct exchange with MnO-derived LSMO(001) surface for spin-related applications.

Effect of eating rate on binge size in Bulimia Nervosa

PubMed Central

Kissileff, Harry R; Zimmerli, Ellen J; Torres, Migdalia I; Devlin, Michael J; Walsh, B Timothy

2008-01-01

Effect of eating rate on binge size in bulimia nervosa. Bulimia Nervosa (BN) is an eating disorder characterized by recurrent episodes of binge eating. During binge eating episodes, patients often describe the rapid consumption of food, and laboratory studies have shown that during binges patients with BN eat faster than normal controls (NC), but the hypothesis that a rapid rate of eating contributes to the excessive intake of binge meals has not yet been experimentally tested. The aim of this study was to assess the effect of eating rate on binge size in BN, in order to determine whether binge size is mediated, in part, by rate of eating. Thirteen BN and 14 NC subjects were asked to binge eat a yogurt shake that was served at a fast rate (140g/min) on one occasion and at a slow rate (70g/min) on another. NC subjects consumed 169 g more when eating at the fast rate than when eating at the slow rate. In contrast, consumption rates failed to influence binge size in patients with BN (fast: 1205 g; slow: 1195 g). Consequently, there was a significant group by rate interaction. As expected, patients with BN consumed more overall than NC subjects (1200 g vs. 740 g). When instructed to binge in the eating laboratory, patients with BN ate equally large amounts of food at a slow rate as at a fast rate. NC subjects ate less at a slow rate. These findings indicate that in a structured laboratory meal paradigm binge size is not affected by rate of eating. PMID:17996257

Genome-Wide Identification and Expression Profiling of Cytokinin Oxidase/Dehydrogenase (CKX) Genes Reveal Likely Roles in Pod Development and Stress Responses in Oilseed Rape (Brassica napus L.).

PubMed

Liu, Pu; Zhang, Chao; Ma, Jin-Qi; Zhang, Li-Yuan; Yang, Bo; Tang, Xin-Yu; Huang, Ling; Zhou, Xin-Tong; Lu, Kun; Li, Jia-Na

2018-03-16

Cytokinin oxidase/dehydrogenases (CKXs) play a critical role in the irreversible degradation of cytokinins, thereby regulating plant growth and development. Brassica napus is one of the most widely cultivated oilseed crops worldwide. With the completion of whole-genome sequencing of B. napus , genome-wide identification and expression analysis of the BnCKX gene family has become technically feasible. In this study, we identified 23 BnCKX genes and analyzed their phylogenetic relationships, gene structures, conserved motifs, protein subcellular localizations, and other properties. We also analyzed the expression of the 23 BnCKX genes in the B. napus cultivar Zhong Shuang 11 ('ZS11') by quantitative reverse-transcription polymerase chain reaction (qRT-PCR), revealing their diverse expression patterns. We selected four BnCKX genes based on the results of RNA-sequencing and qRT-PCR and compared their expression in cultivated varieties with extremely long versus short siliques. The expression levels of BnCKX5-1 , 5-2 , 6-1 , and 7-1 significantly differed between the two lines and changed during pod development, suggesting they might play roles in determining silique length and in pod development. Finally, we investigated the effects of treatment with the synthetic cytokinin 6-benzylaminopurine (6-BA) and the auxin indole-3-acetic acid (IAA) on the expression of the four selected BnCKX genes. Our results suggest that regulating BnCKX expression is a promising way to enhance the harvest index and stress resistance in plants.

Optoelectronic tuning of organoborylazadipyrromethenes via effective electronegativity at the metalloid center.

PubMed

Berhe, Seare A; Rodriguez, Marco T; Park, Eunsol; Nesterov, Vladimir N; Pan, Hongjun; Youngblood, W Justin

2014-03-03

Organoborylazadipyrromethenes were synthesized from free base and fluoroborylazadipyrromethenes and characterized with regard to their structural and electronic properties. B-N bond lengths, along with photophysical and redox behavior, appear dependent on the effective electronegativity at the boron atom as tuned by its substituents, with stronger electronegativity correlating to a shorter B-N bond length, red-shifted absorbance, enhanced fluorescence lifetime and yield, and positively shifted redox potentials.

Assessment and Classification of Service Learning: A Case Study of CS/EE Students

PubMed Central

Wang, Yu-Tseng; Lai, Pao-Lien; Chen, Jen-Yeu

2014-01-01

This study investigates the undergraduate students in computer science/electric engineering (CS/EE) in Taiwan to measure their perceived benefits from the experiences in service learning coursework. In addition, the confidence of their professional disciplines and its correlation with service learning experiences are examined. The results show that students take positive attitudes toward service learning and their perceived benefits from service learning are correlated with their confidence in professional disciplines. Furthermore, this study designs the knowledge model by Bayesian network (BN) classifiers and term frequency-inverse document frequency (TFIDF) for counseling students on the optimal choice of service learning. PMID:25295294

Performance analysis of boron nitride embedded armchair graphene nanoribbon metal–oxide–semiconductor field effect transistor with Stone Wales defects

DOE Office of Scientific and Technical Information (OSTI.GOV)

Chanana, Anuja; Sengupta, Amretashis; Mahapatra, Santanu

2014-01-21

We study the performance of a hybrid Graphene-Boron Nitride armchair nanoribbon (a-GNR-BN) n-MOSFET at its ballistic transport limit. We consider three geometric configurations 3p, 3p + 1, and 3p + 2 of a-GNR-BN with BN atoms embedded on either side (2, 4, and 6 BN) on the GNR. Material properties like band gap, effective mass, and density of states of these H-passivated structures are evaluated using the Density Functional Theory. Using these material parameters, self-consistent Poisson-Schrodinger simulations are carried out under the Non Equilibrium Green's Function formalism to calculate the ballistic n-MOSFET device characteristics. For a hybrid nanoribbon of widthmore » ∼5 nm, the simulated ON current is found to be in the range of 265 μA–280 μA with an ON/OFF ratio 7.1 × 10{sup 6}–7.4 × 10{sup 6} for a V{sub DD} = 0.68 V corresponding to 10 nm technology node. We further study the impact of randomly distributed Stone Wales (SW) defects in these hybrid structures and only 2.5% degradation of ON current is observed for SW defect density of 3.18%.« less

Genome-wide analysis and expression profiling of the GRF gene family in oilseed rape (Brassica napus L.).

PubMed

Ma, Jin-Qi; Jian, Hong-Ju; Yang, Bo; Lu, Kun; Zhang, Ao-Xiang; Liu, Pu; Li, Jia-Na

2017-07-15

Growth regulating-factors (GRFs) are plant-specific transcription factors that help regulate plant growth and development. Genome-wide identification and evolutionary analyses of GRF gene families have been performed in Arabidopsis thaliana, Zea mays, Oryza sativa, and Brassica rapa, but a comprehensive analysis of the GRF gene family in oilseed rape (Brassica napus) has not yet been reported. In the current study, we identified 35 members of the BnGRF family in B. napus. We analyzed the chromosomal distribution, phylogenetic relationships (Bayesian Inference and Neighbor Joining method), gene structures, and motifs of the BnGRF family members, as well as the cis-acting regulatory elements in their promoters. We also analyzed the expression patterns of 15 randomly selected BnGRF genes in various tissues and in plant varieties with different harvest indices and gibberellic acid (GA) responses. The expression levels of BnGRFs under GA treatment suggested the presence of possible negative feedback regulation. The evolutionary patterns and expression profiles of BnGRFs uncovered in this study increase our understanding of the important roles played by these genes in oilseed rape. Copyright © 2017. Published by Elsevier B.V.

[The affective pathology in patients with adolescent bulimia nervosa].

PubMed

Grachev, V V

To investigate affective pathology in patients with adolescent bulimia nervosa (BN) and to analyze comorbid mutual influences of these clinical entities. A sample consisted of 52 young female patients, aged from 13.9 to 17.4 years, who simultaneously meet ICD-10 criteria of F50.2 - typical BN and F30-F39 - mood disorders. The Eating Attitudes Test (EAT-26) and the Beck Depression Inventory were used for psychometric assessment. Duration of follow-up ranged from 1 to 7 years. The common forms of affective disorders comorbid with adolescent BN were dysthymia and bipolar affective disorder (BAD) type II. Less often BN manifested in association with psychogenic endoform depressions. And the less typical was comorbidity of BN with endogenous recurrent unipolar depression. The normalization of mood and transition depression to hypomania contributed to the remission of eating disorders. Worst clinical and social outcome was detected in patients with long-term persistent hypothymia caused by dysthymia or protracted depressive episodes of recurrent depressive disorder. A more favorable outcome was seen in patients with alternation of depression and hypomania in the structure of the BAD type II and the best outcome in patients with single episode of psychogenic endoform depression.

Polymer-Derived Boron Nitride: A Review on the Chemistry, Shaping and Ceramic Conversion of Borazine Derivatives

PubMed Central

Bernard, Samuel; Miele, Philippe

2014-01-01

Boron nitride (BN) is a III-V compound which is the focus of important research since its discovery in the early 19th century. BN is electronic to carbon and thus, in the same way that carbon exists as graphite, BN exists in the hexagonal phase. The latter offers an unusual combination of properties that cannot be found in any other ceramics. However, these properties closely depend on the synthesis processes. This review states the recent developments in the preparation of BN through the chemistry, shaping and ceramic conversion of borazine derivatives. This concept denoted as Polymer-Derived Ceramics (PDCs) route allows tailoring the chemistry of precursors to elaborate complex BN shapes which cannot be obtained by conventional process. The effect of the chemistry of the molecular precursors, i.e., borazine and trichloroborazine, and their polymeric derivatives i.e., polyborazylene and poly[tri(methylamino)borazine], in which the specific functional groups and structural motifs determine the shaping potential by conventional liquid-phase process and plastic-forming techniques is discussed. Nanotubes, nano-fibers, coatings, monoliths and fiber-reinforced matrix composites are especially described. This leads to materials which are of significant engineering interest. PMID:28788257

Polymer-Derived Boron Nitride: A Review on the Chemistry, Shaping and Ceramic Conversion of Borazine Derivatives.

PubMed

Bernard, Samuel; Miele, Philippe

2014-11-21

Boron nitride (BN) is a III-V compound which is the focus of important research since its discovery in the early 19th century. BN is electronic to carbon and thus, in the same way that carbon exists as graphite, BN exists in the hexagonal phase. The latter offers an unusual combination of properties that cannot be found in any other ceramics. However, these properties closely depend on the synthesis processes. This review states the recent developments in the preparation of BN through the chemistry, shaping and ceramic conversion of borazine derivatives. This concept denoted as Polymer-Derived Ceramics (PDCs) route allows tailoring the chemistry of precursors to elaborate complex BN shapes which cannot be obtained by conventional process. The effect of the chemistry of the molecular precursors, i.e. , borazine and trichloroborazine, and their polymeric derivatives i.e. , polyborazylene and poly[tri(methylamino)borazine], in which the specific functional groups and structural motifs determine the shaping potential by conventional liquid-phase process and plastic-forming techniques is discussed. Nanotubes, nano-fibers, coatings, monoliths and fiber-reinforced matrix composites are especially described. This leads to materials which are of significant engineering interest.

Effect of BN coating on the strength of a mullite type fiber

NASA Astrophysics Data System (ADS)

Chawla, K. K.; Xu, Z. R.; Ha, J.-S.; Schmücker, M.; Schneider, H.

1997-09-01

Nextel 480 is a polycrystalline essentially mullite fiber (70 wt.-% Al2O3+28 wt.-% SiO2+2 wt.-% B2O3). Different thicknesses of BN were applied as coatings on this fiber. Optical, scanning electron, and transmission electron microscopy were used to characterize the microstructure of the coatings and fibers. The effects of coating and high temperature exposure on the fiber strength were investigated using two-parameter Weibull distribution. TEM examination showed that the BN coating has a turbostratic structure, with the basal planes lying predominantly parallel to the fiber surface. Such an orientation of coating is desirable for easy crack deflection and subsequent fiber pullout in a composite. The BN coated Nextel 480 fiber showed that Weibull mean strength increased first and then decreased with increasing coating thickness. This was due to the surface flaw healing effect of the coating (up to 0.3 μm) while in the case of thick BN coating (1 μm), the soft nature of the coating material had a more dominant effect and resulted in a decrease of the fiber strength. High temperature exposure of Nextel 480 resulted in grain growth, which led to a strength loss.

Pure & crystallized 2D Boron Nitride sheets synthesized via a novel process coupling both PDCs and SPS methods

PubMed Central

Yuan, Sheng; Linas, Sébastien; Journet, Catherine; Steyer, Philippe; Garnier, Vincent; Bonnefont, Guillaume; Brioude, Arnaud; Toury, Bérangère

2016-01-01

Within the context of emergent researches linked to graphene, it is well known that h-BN nanosheets (BNNSs), also referred as 2D BN, are considered as the best candidate for replacing SiO2 as dielectric support or capping layers for graphene. As a consequence, the development of a novel alternative source for highly crystallized h-BN crystals, suitable for a further exfoliation, is a prime scientific issue. This paper proposes a promising approach to synthesize pure and well-crystallized h-BN flakes, which can be easily exfoliated into BNNSs. This new accessible production process represents a relevant alternative source of supply in response to the increasing need of high quality BNNSs. The synthesis strategy to prepare pure h-BN is based on a unique combination of the Polymer Derived Ceramics (PDCs) route with the Spark Plasma Sintering (SPS) process. Through a multi-scale chemical and structural investigation, it is clearly shown that obtained flakes are large (up to 30 μm), defect-free and well crystallized, which are key-characteristics for a subsequent exfoliation into relevant BNNSs. PMID:26843122

Understanding the Scalability of Bayesian Network Inference Using Clique Tree Growth Curves

NASA Technical Reports Server (NTRS)

Mengshoel, Ole J.

2010-01-01

One of the main approaches to performing computation in Bayesian networks (BNs) is clique tree clustering and propagation. The clique tree approach consists of propagation in a clique tree compiled from a Bayesian network, and while it was introduced in the 1980s, there is still a lack of understanding of how clique tree computation time depends on variations in BN size and structure. In this article, we improve this understanding by developing an approach to characterizing clique tree growth as a function of parameters that can be computed in polynomial time from BNs, specifically: (i) the ratio of the number of a BN s non-root nodes to the number of root nodes, and (ii) the expected number of moral edges in their moral graphs. Analytically, we partition the set of cliques in a clique tree into different sets, and introduce a growth curve for the total size of each set. For the special case of bipartite BNs, there are two sets and two growth curves, a mixed clique growth curve and a root clique growth curve. In experiments, where random bipartite BNs generated using the BPART algorithm are studied, we systematically increase the out-degree of the root nodes in bipartite Bayesian networks, by increasing the number of leaf nodes. Surprisingly, root clique growth is well-approximated by Gompertz growth curves, an S-shaped family of curves that has previously been used to describe growth processes in biology, medicine, and neuroscience. We believe that this research improves the understanding of the scaling behavior of clique tree clustering for a certain class of Bayesian networks; presents an aid for trade-off studies of clique tree clustering using growth curves; and ultimately provides a foundation for benchmarking and developing improved BN inference and machine learning algorithms.

78 FR 64894 - Airworthiness Directives; B-N Group Ltd. Airplanes

Federal Register 2010, 2011, 2012, 2013, 2014

2013-10-30

... requires a one-time inspection and functional test of the engine control cables and, depending on findings... Airworthiness Directives; B-N Group Ltd. Airplanes AGENCY: Federal Aviation Administration (FAA), Department of... airworthiness directive (AD) for B-N Group Ltd. Models BN-2, BN-2A, BN-2A-2, BN-2A-3, BN-2A-6, BN-2A-8, BN- 2A-9...

A novel in situ synthesis of SiBCN-Zr composites prepared by a sol-gel process and spark plasma sintering.

PubMed

Miao, Yang; Yang, Zhihua; Liang, Bin; Li, Quan; Chen, Qingqing; Jia, Dechang; Cheng, Yi-Bing; Zhou, Yu

2016-08-09

In the work reported here, SiBCN amorphous powders were first prepared by a mechanical alloying technique, employing cubic silicon, graphite and hexagonal boron nitride powders as raw materials. Zirconia was then introduced via sol-gel methods. The resulting powder composite was then consolidated via SPS sintering. The SPS sintering sample was evaluated using XRD, SEM and TEM. XRD reveals a chemical transformation wherein amorphous BN(C) and ZrO2 form the primary ZrC and ZrB2 phases after SPS processing along with SiC and BN(C). Thereafter ZrC reacts with BN(C) completely to form ZrB2. The reaction starts at the temperature of 1500 °C and is complete at the temperature of 1900 °C. The fracture toughness of the sintered composites reaches 4.9 ± 0.2 MPa m(1/2) due to the presence of the laminated structure of the BN(C) phase.

All-optical control and super-resolution imaging of quantum emitters in layered materials.

PubMed

Kianinia, Mehran; Bradac, Carlo; Sontheimer, Bernd; Wang, Fan; Tran, Toan Trong; Nguyen, Minh; Kim, Sejeong; Xu, Zai-Quan; Jin, Dayong; Schell, Andreas W; Lobo, Charlene J; Aharonovich, Igor; Toth, Milos

2018-02-28

Layered van der Waals materials are emerging as compelling two-dimensional platforms for nanophotonics, polaritonics, valleytronics and spintronics, and have the potential to transform applications in sensing, imaging and quantum information processing. Among these, hexagonal boron nitride (hBN) is known to host ultra-bright, room-temperature quantum emitters, whose nature is yet to be fully understood. Here we present a set of measurements that give unique insight into the photophysical properties and level structure of hBN quantum emitters. Specifically, we report the existence of a class of hBN quantum emitters with a fast-decaying intermediate and a long-lived metastable state accessible from the first excited electronic state. Furthermore, by means of a two-laser repumping scheme, we show an enhanced photoluminescence and emission intensity, which can be utilized to realize a new modality of far-field super-resolution imaging. Our findings expand current understanding of quantum emitters in hBN and show new potential ways of harnessing their nonlinear optical properties in sub-diffraction nanoscopy.

Processing and Structural Advantages of the Sylramic-iBN SiC Fiber for SiC/SiC Components

NASA Technical Reports Server (NTRS)

Yun, H. M.; Dicarlo, J. A.; Bhatt, R. T.; Hurst, J. B.

2008-01-01

The successful high-temperature application of complex-shaped SiC/SiC components will depend on achieving as high a fraction of the as-produced fiber strength as possible during component fabrication and service. Key issues center on a variety of component architecture, processing, and service-related factors that can reduce fiber strength, such as fiber-fiber abrasion during architecture shaping, surface chemical attack during interphase deposition and service, and intrinsic flaw growth during high-temperature matrix formation and composite creep. The objective of this paper is to show that the NASA-developed Sylramic-iBN SiC fiber minimizes many of these issues for state-of-the-art melt-infiltrated (MI) SiC/BN/SiC composites. To accomplish this, data from various mechanical tests are presented that compare how different high performance SiC fiber types retain strength during formation of complex architectures, during processing of BN interphases and MI matrices, and during simulated composite service at high temperatures.

The effect of SiO 2-doped boron nitride multiple coatings on mechanical properties of quartz fibers

NASA Astrophysics Data System (ADS)

Zheng, Yu; Wang, Shubin

2012-01-01

SiO2-doped boron nitride multiple coatings (SiO2/BN multiple coatings) were prepared on quartz fibers surface at 700 °C. Single fiber tensile test was employed to evaluate fiber tensile strength; Scanning Electron Microscopy (SEM) and Transmission Electron Microscopy (TEM) were employed to evaluate morphology and structure of the fibers. Fiber tensile test results indicated that the strength of quartz fibers with SiO2/BN multiple coatings was about twice of the fibers with BN coatings and original fibers which were heated at 700 °C for 10 h. The SiO2/BN multiple coatings would provide compressive stress on quartz fibers, which would help to seal the defects on fiber surface. Furthermore, TEM images showed that the nano-SiO2 powders crystallized in advance of quartz fibers, which would suppress crystallization of quartz fibers and reduce damage from crystallization. Thus, nano-SiO2 powders would help to keep mechanical properties of quartz fibers.

Interface-induced perpendicular magnetic anisotropy of Co nanoparticles on single-layer h-BN/Pt(111)

NASA Astrophysics Data System (ADS)

Watanabe, Takahiro; Yamada, Yoichi; Koide, Akihiro; Entani, Shiro; Li, Songtian; Popov, Zakhar I.; Sorokin, Pavel B.; Naramoto, Hiroshi; Sasaki, Masahiro; Amemiya, Kenta; Sakai, Seiji

2018-01-01

Ferromagnetism with perpendicular magnetic anisotropy (PMA) was observed at room temperature in cobalt nanoparticles (NPs) grown on hexagonal boron nitride (h-BN) on a Pt(111) surface. It was shown that the Co NPs have planar hexagonal shapes with a mean diameter of ˜20 nm and a mean height of ˜1.6 nm. The depth-resolved analysis of X-ray magnetic circular dichroism at the Co L2,3-edges revealed that in the ferromagnetic Co NPs, the ratio of the orbital magnetic moment to the spin magnetic moment in the out-of-plane direction becomes larger at the Co NP/h-BN interface than the ratio in bulk Co. The B and N K-edge near edge X-ray absorption fine structures showed the orbital hybridization between the π orbitals of h-BN and d orbitals of Co at the interface, as an origin of the orbital magnetic moment enhancement possibly giving rise to PMA in the Co NPs.

A Nano-sized Supramolecule Beyond the Fullerene Topology**

PubMed Central

Dielmann, Fabian; Heindl, Claudia; Hastreiter, Florian; Peresypkina, Eugenia V; Virovets, Alexander V; Gschwind, Ruth M; Scheer, Manfred

2014-01-01

The reaction of [CpBnFe(η5-P5)] (1) (CpBn=η5-C5(CH2Ph)5) with CuI selectively yields a novel spherical supramolecule (CH2Cl2)3.4@[(CpBnFeP5)12{CuI}54(MeCN)1.46] (2) showing a linkage of the scaffold atoms which is beyond the Fullerene topology. Its extended CuI framework reveals an outer diameter of 3.7 nm—a size that has not been reached before using five-fold symmetric building blocks. Furthermore, 2 shows a remarkable solubility in CH2Cl2, and NMR spectroscopy reveals that the scaffold of the supramolecule remains intact in solution. In addition, a novel 2D polymer [{CpBnFe(η5-P5)}2{Cu6(μ-I)2(μ3-I)4}]n (3) with an uncommon structural motif was isolated. Its formation can be avoided by using a large excess of CuI in the reaction with 1. PMID:25288480

Eating disorder symptomatology among ballet dancers.

PubMed

Ringham, Rebecca; Klump, Kelly; Kaye, Walter; Stone, David; Libman, Steven; Stowe, Susan; Marcus, Marsha

2006-09-01

The current study sought to compare eating disorder symptomatology among ballet dancers and individuals with restricting anorexia nervosa (RAN), bulimia nervosa (BN), and no eating pathology. Twenty-nine female ballet dancers completed assessments and were compared with an archival dataset of 26 women with RAN, 47 women with BN, and 44 women with no eating pathology. Eating disorder diagnoses and behaviors were assessed with a semi-structured clinical interview, the Eating Disorder Inventory (EDI), and a weight history interview. Eighty-three percent of dancers met lifetime criteria for AN (6.9%), BN (10.3%), AN+BN (10.3%), or EDNOS (55.0%). Moreover, dancers looked more similar to eating-disordered individuals than to control individuals on measures of eating pathology. Despite previous emphasis on the pathology AN, the current findings suggest that dancers frequently engage in binge eating and purging behaviors. Moreover, it appears that their pathology is as severe as that of non-dancing women with eating disorders. Copyright (c) 2006 by Wiley Periodicals, Inc.

78 FR 21072 - Airworthiness Directives; B-N Group Ltd. Airplanes

Federal Register 2010, 2011, 2012, 2013, 2014

2013-04-09

... Airworthiness Directives; B-N Group Ltd. Airplanes AGENCY: Federal Aviation Administration (FAA), Department of... airworthiness directive (AD) for B-N Group Ltd. Models BN-2, BN-2A, BN2A MK. III, BN2A MK. III-2, BN2A MK. III-3... further information by examining the MCAI in the AD docket. Relevant Service Information B-N Group Limited...

Self-harm and suicidal behavior in borderline personality disorder with and without bulimia nervosa.

PubMed

Reas, Deborah L; Pedersen, Geir; Karterud, Sigmund; Rø, Øyvind

2015-06-01

Few studies have investigated whether a diagnosis of Bulimia nervosa (BN) confers additional risk of life-threatening behaviors such as self-harm and suicidal behavior in borderline personality disorder (BPD). Participants were 483 treatment-seeking women diagnosed with BPD according to the Structured Clinical Interview for DSM-IV Axis II Personality Disorders (SCID-II; First, Gibbon, Spitzer, Williams, & Benjamin, 1997; Diagnostic and Statistical Manual of Mental Disorders, 4th ed.; APA, 1994) and admitted to the Norwegian Network of Psychotherapeutic Day Hospitals between 1996 and 2009. Of these, 57 (11.8%) women met DSM-IV diagnostic criteria for BN according to the Mini-International Neuropsychiatric Interview (M.I.N.I.; Sheehan et al., 1998) and they were compared with women with BPD and other Axis I disorders. We found that comorbid BN is uniquely and significantly associated with increased risk of suicidal behavior among women being treated for BPD. Findings underscore the importance of routinely screening for BN among women seeking treatment for BPD, as co-occurring bulimia appears to be a significant marker for immediate life-threatening behaviors in this already high-risk population, which is a significant public health issue. A significantly greater proportion of women with BPD-BN reported suicidal ideation at intake (past 7 days), engaged in self-harm behavior during treatment, and attempted suicide during treatment. All bivariate associations remained significant in the logistic regression models after controlling for mood, anxiety, and substance-related disorders. The presence of a concurrent diagnosis of BN among women with BPD is significantly and uniquely associated with recent suicidal ideation, and self-harm behavior and suicide attempts during treatment after controlling for major classes of mental disorders. Co-occurring BN appears to represent a significant marker for immediate life-threatening behaviors in women seeking treatment for BPD. Extra vigilance and careful monitoring of suicidal behavior during treatment is important for these individuals, and routine screening for BN is warranted. (c) 2015 APA, all rights reserved).

The Natural Course of Bulimia Nervosa and Eating Disorder not Otherwise Specified is not Influenced by Personality Disorders

PubMed Central

Grilo, Carlos M.; Sanislow, Charles A.; Shea, M. Tracie; Skodol, Andrew E.; Stout, Robert L.; Pagano, Maria E.; Yen, Shirley; McGlashan, Thomas H.

2013-01-01

Objective To examine prospectively the natural course of bulimia nervosa (BN) and eating disorder not otherwise specified (EDNOS) and to test the effects of personality disorder (PD) comorbidity on the outcomes. Method Ninety-two female patients with current BN (N = 23) or EDNOS (N = 69) were evaluated at baseline enrollment in the Collaborative Longitudinal Personality Disorders Study (CLPS). Eating disorders (EDs) were assessed with the Structured Clinical Interview for DSM-IV Axis I Disorders. Personality disorders (PDs) were assessed with the Diagnostic Interview for DSM-IV PD (DIPD-IV). The course of BN and EDNOS was assessed with the Longitudinal Interval Follow-up Evaluation and the course of PDs was evaluated with the Follow-Along version of the DIPD-IV at 6, 12, and 24 months. Results Probability of remission at 24 months was 40% for BN and 59% for EDNOS. To test the effects of PD comorbidity on course, ED patients were divided into groups with no, one, and two or more PDs. Cox proportional regression analyses revealed that BN had a longer time to remission than EDNOS (p < .05). The number of PDs was not a significant predictor of time to remission, nor was the presence of Axis I psychiatric comorbidity or Global Assessment of Functioning scores. Analyses using proportional hazards regression with time-varying covariates revealed that PD instability was unrelated to changes in ED. Conclusions BN has a worse 24-month course (longer time to remission) than EDNOS. The natural course of BN and EDNOS is not influenced significantly by the presence, severity, or time-varying changes of co-occurring PDs, co-occurring Axis I disorders, or by global functioning. PMID:12949923

Detection and Characterization of Conjugative Degradative Plasmids in Xenobiotic-Degrading Sphingomonas Strains

PubMed Central

Basta, Tamara; Keck, Andreas; Klein, Joachim; Stolz, Andreas

2004-01-01

A systematic survey for the presence of plasmids in 17 different xenobiotic-degrading Sphingomonas strains was performed. In almost all analyzed strains, two to five plasmids with sizes of about 50 to 500 kb were detected by using pulsed-field gel electrophoresis. A comparison of plasmid preparations untreated or treated with S1 nuclease suggested that, in general, Sphingomonas plasmids are circular. Hybridization experiments with labeled gene probes suggested that large plasmids are involved in the degradation of dibenzo-p-dioxin, dibenzofuran, and naphthalenesulfonates in S. wittichii RW1, Sphingomonas sp. HH69, and S. xenophaga BN6, respectively. The plasmids which are responsible for the degradation of naphthalene, biphenyl, and toluene by S. aromaticivorans F199 (pNL1) and of naphthalenesulfonates by S. xenophaga BN6 (pBN6) were site-specifically labeled with a kanamycin resistance cassette. The conjugative transfer of these labeled plasmids was attempted with various bacterial strains as putative recipient strains. Thus, a conjugative transfer of plasmid pBN6 from S. xenophaga BN6 to a cured mutant of strain BN6 and to Sphingomonas sp. SS3 was observed. The conjugation experiments with plasmid pNL1 suggested a broader host range of this plasmid, because it was transferred without any obvious structural changes to S. yanoikuyae B1, Sphingomonas sp. SS3, and S. herbicidovorans. In contrast, major plasmid rearrangements were observed in the transconjugants after the transfer of plasmid pNL1 to Sphingomonas sp. HH69 and of pBN6 to Sphingomonas sp. SS3. No indications for the transfer of a Sphingomonas plasmid to bacteria outside of the Sphingomonadaceae were obtained. PMID:15175300

The validity and utility of subtyping bulimia nervosa.

PubMed

van Hoeken, Daphne; Veling, Wim; Sinke, Sjoukje; Mitchell, James E; Hoek, Hans W

2009-11-01

To review the evidence for the validity and utility of subtyping bulimia nervosa (BN) into a purging (BN-P) and a nonpurging subtype (BN-NP), and of distinguishing BN-NP from binge eating disorder (BED), by comparing course, complications, and treatment. A literature search of psychiatry databases for studies published in peer-reviewed journals that used the DSM-definitions of BN and BED, and included both individuals with BN-NP and individuals with BN-P and/or BED. Twenty-three studies compared individuals with BN-NP (N = 671) to individuals with BN-P (N = 1795) and/or individuals with BED (N = 1921), two of which reported on course, 12 on comorbidity and none on treatment response-the indicators for validity and clinical utility. The differences found were mainly quantitative rather than qualitative, suggesting a gradual difference in severity from BN-P (most severe) through BN-NP to BED (least severe). None of the comparisons provided convincing evidence for the validity or utility of the BN-NP diagnosis. Three options for the position of BN-NP in DSM-V were suggested: (1) maintaining the BN-NP subtype, (2) dropping nonpurging compensatory behavior as a criterion for BN, so that individuals currently designated as having BN-NP would be designated as having BED, and (3) including BN-NP in a broad BN category.

An open canvas--2D materials with defects, disorder, and functionality.

PubMed

Zou, Xiaolong; Yakobson, Boris I

2015-01-20

CONSPECTUS: While some exceptional properties are unique to graphene only (its signature Dirac-cone gapless dispersion, carrier mobility, record strength), other features are common to other two-dimensional materials. The broader family "beyond graphene" offers greater choices to be explored and tailored for various applications. Transition metal dichalcogenides (TMDCs), hexagonal boron nitride (h-BN), and 2D layers of pure elements, like phosphorus or boron, can complement or even surpass graphene in many ways and uses, ranging from electronics and optoelectronics to catalysis and energy storage. Their availability greatly relies on chemical vapor deposition growth of large samples, which are highly polycrystalline and include interfaces such as edges, heterostructures, and grain boundaries, as well as dislocations and point defects. These imperfections do not always degrade the material properties, but they often bring new physics and even useful functionality. It turns particularly interesting in combination with the sheer openness of all 2D sheets, fully exposed to the environment, which, as we show herein, can change and tune the defect structures and consequently all their qualities, from electronic levels, conductivity, magnetism, and optics to structural mobility of dislocations and catalytic activities. In this Account, we review our progress in understanding of various defects. We begin by expressing the energy of an arbitrary graphene edge analytically, so that the environment is regarded by "chemical phase shift". This has profound implications for graphene and carbon nanotube growth. Generalization of this equation to heteroelemental BN gives a method to determine the energy for arbitrary edges of BN, depending on the partial chemical potentials. This facilitates the tuning of the morphology and electronic and magnetic properties of pure BN or hybrid BN|C systems. Applying a similar method to three-atomic-layer TMDCs reveals more diverse edge structures for thermodynamically stable flakes. Moreover, CVD samples show new types of edge reconstruction, providing insight into the nonequilibrium growth process. Combining dislocation theory with first-principles computations, we could predict the dislocation cores for BN and TMDC and reveal their variable chemical makeup. This lays the foundation for the unique sensitivity to ambient conditions. For example, partial occupation of the defect states for dislocations in TMDCs renders them intrinsically magnetic. The exchange coupling between electrons from neighboring dislocations in grain boundaries further makes them half-metallic, which may find its applications in spintronics. Finally, brief discussion of monoelemental 2D-layer phosphorus and especially the structures and growth routes of 2D boron shows how theoretical assessment can help the quest for new synthetic routes.

Deep Learning Identifies High-z Galaxies in a Central Blue Nugget Phase in a Characteristic Mass Range

NASA Astrophysics Data System (ADS)

Huertas-Company, M.; Primack, J. R.; Dekel, A.; Koo, D. C.; Lapiner, S.; Ceverino, D.; Simons, R. C.; Snyder, G. F.; Bernardi, M.; Chen, Z.; Domínguez-Sánchez, H.; Lee, C. T.; Margalef-Bentabol, B.; Tuccillo, D.

2018-05-01

We use machine learning to identify in color images of high-redshift galaxies an astrophysical phenomenon predicted by cosmological simulations. This phenomenon, called the blue nugget (BN) phase, is the compact star-forming phase in the central regions of many growing galaxies that follows an earlier phase of gas compaction and is followed by a central quenching phase. We train a convolutional neural network (CNN) with mock “observed” images of simulated galaxies at three phases of evolution— pre-BN, BN, and post-BN—and demonstrate that the CNN successfully retrieves the three phases in other simulated galaxies. We show that BNs are identified by the CNN within a time window of ∼0.15 Hubble times. When the trained CNN is applied to observed galaxies from the CANDELS survey at z = 1–3, it successfully identifies galaxies at the three phases. We find that the observed BNs are preferentially found in galaxies at a characteristic stellar mass range, 109.2–10.3 M ⊙ at all redshifts. This is consistent with the characteristic galaxy mass for BNs as detected in the simulations and is meaningful because it is revealed in the observations when the direct information concerning the total galaxy luminosity has been eliminated from the training set. This technique can be applied to the classification of other astrophysical phenomena for improved comparison of theory and observations in the era of large imaging surveys and cosmological simulations.

Chemical and Bandgap Engineering in Monolayer Hexagonal Boron Nitride

PubMed Central

Ba, Kun; Jiang, Wei; Cheng, Jingxin; Bao, Jingxian; Xuan, Ningning; Sun, Yangye; Liu, Bing; Xie, Aozhen; Wu, Shiwei; Sun, Zhengzong

2017-01-01

Monolayer hexagonal boron nitride (h-BN) possesses a wide bandgap of ~6 eV. Trimming down the bandgap is technically attractive, yet poses remarkable challenges in chemistry. One strategy is to topological reform the h-BN’s hexagonal structure, which involves defects or grain boundaries (GBs) engineering in the basal plane. The other way is to invite foreign atoms, such as carbon, to forge bizarre hybrid structures like hetero-junctions or semiconducting h-BNC materials. Here we successfully developed a general chemical method to synthesize these different h-BN derivatives, showcasing how the chemical structure can be manipulated with or without a graphene precursor, and the bandgap be tuned to ~2 eV, only one third of the pristine one’s. PMID:28367992

Neuroimaging in bulimia nervosa and binge eating disorder: a systematic review.

PubMed

Donnelly, Brooke; Touyz, Stephen; Hay, Phillipa; Burton, Amy; Russell, Janice; Caterson, Ian

2018-01-01

In recent decades there has been growing interest in the use of neuroimaging techniques to explore the structural and functional brain changes that take place in those with eating disorders. However, to date, the majority of research has focused on patients with anorexia nervosa. This systematic review addresses a gap in the literature by providing an examination of the published literature on the neurobiology of individuals who binge eat; specifically, individuals with bulimia nervosa (BN) and binge eating disorder (BED). A systematic review was conducted in accordance with PRISMA guidelines using PubMed, PsycInfo, Medline and Web of Science, and additional hand searches through reference lists. 1,003 papers were identified in the database search. Published studies were included if they were an original research paper written in English; studied humans only; used samples of participants with a diagnosed eating disorder characterised by recurrent binge eating; included a healthy control sample; and reported group comparisons between clinical groups and healthy control groups. Thirty-two papers were included in the systematic review. Significant heterogeneity in the methods used in the included papers coupled with small sample sizes impeded the interpretation of results. Twenty-one papers utilised functional Magnetic Resonance Imaging (fMRI); seven papers utilized Magnetic Resonance Imaging (MRI) with one of these using both MRI and Positron Emission Technology (PET); three studies used Single-Photon Emission Computed Tomography (SPECT) and one study used PET only. A small number of consistent findings emerged in individuals in the acute phase of illness with BN or BED including: volume reduction and increases across a range of areas; hypoactivity in the frontostriatal circuits; and aberrant responses in the insula, amygdala, middle frontal gyrus and occipital cortex to a range of different stimuli or tasks; a link between illness severity in BN and neural changes; diminished attentional capacity and early learning; and in SPECT studies, increased rCBF in relation to disorder-related stimuli. Studies included in this review are heterogenous, preventing many robust conclusions from being drawn. The precise neurobiology of BN and BED remains unclear and ongoing, large-scale investigations are required. One clear finding is that illness severity, exclusively defined as the frequency of binge eating or bulimic episodes, is related to greater neural changes. The results of this review indicate additional research is required, particularly extending findings of reduced cortical volumes and diminished activity in regions associated with self-regulation (frontostriatal circuits) and further exploring responses to disorder-related stimuli in people with BN and BED.

Multifunctional Nanofluids with 2D Nanosheets for thermal management and tribological applications

NASA Astrophysics Data System (ADS)

Taha Tijerina, Jose Jaime

Conventional heat-transfer fluids such as water, ethylene glycol, standard oils and other lubricants are typically low-efficiency heat-transfer fluids. Thermal management plays a critical factor in many applications where these fluids can be used, such as in motors/engines, solar cells, biopharmaceuticals, fuel cells, high voltage power transmission systems, micro/nanoelectronics mechanical systems (MEMS/NEMS), and nuclear cooling among others. These insulating fluids require superb filler dispersion, high thermal conduction, and for certain applications as in electrical/electronic devices also electrical insulation. The miniaturization and high efficiency of electrical/electronic devices in these fields demand successful heat management and energy-efficient fluid-based heat-transfer systems. Recent advances in layered materials enable large scale synthesis of various two-dimensional (2D) structures. Some of these 2D materials are good choices as nanofillers in heat transfer fluids; mainly due to their inherent high thermal conductivity (TC) and high surface area available for thermal energy transport. Among various 2D-nanostructures, hexagonal boron nitride (h-BN) and graphene (G) exhibit versatile properties such as outstanding TC, excellent mechanical stability, and remarkable chemical inertness. The following research, even though investigate various conventional fluids, will focus on dielectric insulating nanofluids (mineral oil -- MO) with significant thermal performance. It is presented the plan for synthesis and characterization of stable high-thermal conductivity nanofluids using 2D-nanostructures of h-BN, which will be further incorporated at diverse filler concentrations to conventional fluids for cooling applications, without compromising its electrical insulating property. For comparison, properties of h-BN based fluids are compared with conductive fillers such as graphene; where graphene has similar crystal structure of h-BN and also has similar bulk thermal conductivity. Moreover, bot h-BN and graphene are exfoliated through the same method. In essence, this project, for the first time, unravels the behavior of the exfoliated h-BN effect on reinforced conventional fluids under the influence of atomistic scale structures (particularly, electrically insulating and lubricant/cutting fluids), thereby linking the physical, electrical and mechanical properties of these nanoscale materials. The innovative experimental approach is expected to result in de novo strategies for introducing these systems for new concepts and variables to engineer nanofluid properties suitable for very promising industrial applications.

Static structure of a pointed charged drop

NASA Astrophysics Data System (ADS)

Fernandez de La Mora, Juan

2017-11-01

The static equilibrium structure of an equipotential drop with two symmetric Taylor cones is computed by assigning a charge distribution along the z axis q (z) = ∑Bn (L2 -z2)n + 1 / 2 . Taylor's local equilibrium at the poles z = L , - L fixes two of the Bn coefficients as a function of the other, determined by minimizing stress imbalance. Just two optimally chosen terms in the Bn expansion yield imperceptible errors. Prior work has argued that an exploding drop initially carrying Rayleigh's charge qR is quasi static. Paradoxically, quasi-static predictions on the size of the progeny drops emitted during a Coulombic explosion disagree with observations. The static drop structure found here also models poorly a Coulomb explosion having an equatorial over polar length ratio (0.42) and the a drop charge exceeding those observed (0.28-0.36 and qR / 2). Our explanation for this paradox is that, while the duration tc of a Coulomb explosion is much larger than the charge relaxation time, the dynamic time scale for drop elongation is typically far longer than tc. Therefore, the pressure distribution within the exploding drop is not uniform. A similar analysis for a drop in an external field fits well the experimental shape.

Advances in 2D boron nitride nanostructures: nanosheets, nanoribbons, nanomeshes, and hybrids with graphene.

PubMed

Lin, Yi; Connell, John W

2012-11-21

The recent surge in graphene research has stimulated interest in the investigation of various 2-dimensional (2D) nanomaterials. Among these materials, the 2D boron nitride (BN) nanostructures are in a unique position. This is because they are the isoelectric analogs to graphene structures and share very similar structural characteristics and many physical properties except for the large band gap. The main forms of the 2D BN nanostructures include nanosheets (BNNSs), nanoribbons (BNNRs), and nanomeshes (BNNMs). BNNRs are essentially BNNSs with narrow widths in which the edge effects become significant; BNNMs are also variations of BNNSs, which are supported on certain metal substrates where strong interactions and the lattice mismatch between the substrate and the nanosheet result in periodic shallow regions on the nanosheet surface. Recently, the hybrids of 2D BN nanostructures with graphene, in the form of either in-plane hybrids or inter-plane heterolayers, have also drawn much attention. In particular, the BNNS-graphene heterolayer architectures are finding important electronic applications as BNNSs may serve as excellent dielectric substrates or separation layers for graphene electronic devices. In this article, we first discuss the structural basics, spectroscopic signatures, and physical properties of the 2D BN nanostructures. Then, various top-down and bottom-up preparation methodologies are reviewed in detail. Several sections are dedicated to the preparation of BNNRs, BNNMs, and BNNS-graphene hybrids, respectively. Following some more discussions on the applications of these unique materials, the article is concluded with a summary and perspectives of this exciting new field.

Effect of the SiCl₄ Flow Rate on SiBN Deposition Kinetics in SiCl₄-BCl₃-NH₃-H₂-Ar Environment.

PubMed

Li, Jianping; Qin, Hailong; Liu, Yongsheng; Ye, Fang; Li, Zan; Cheng, Laifei; Zhang, Litong

2017-06-07

To improve the thermal and mechanical stability of SiC f /SiC or C/SiC composites with SiBN interphase, SiBN coating was deposited by low pressure chemical vapor deposition (LPCVD) using SiCl₄-BCl₃-NH₃-H₂-Ar gas system. The effect of the SiCl₄ flow rate on deposition kinetics was investigated. Results show that deposition rate increases at first and then decreases with the increase of the SiCl₄ flow rate. The surface of the coating is a uniform cauliflower-like structure at the SiCl₄ flow rate of 10 mL/min and 20 mL/min. The surface is covered with small spherical particles when the flow rate is 30 mL/min. The coatings deposited at various SiCl₄ flow rates are all X-ray amorphous and contain Si, B, N, and O elements. The main bonding states are B-N, Si-N, and N-O. B element and B-N bonding decrease with the increase of SiCl₄ flow rate, while Si element and Si-N bonding increase. The main deposition mechanism refers to two parallel reactions of BCl₃+NH₃ and SiCl₄+NH₃. The deposition process is mainly controlled by the reaction of BCl₃+NH₃.

The effect of incorporated self-lubricated BN(h) particles on the tribological properties of Ni-P/BN(h) composite coatings

NASA Astrophysics Data System (ADS)

Hsu, Chih-I.; Hou, Kung-Hsu; Ger, Ming-Der; Wang, Gao-Liang

2015-12-01

Ni-P/BN(h) composite coatings are prepared by means of the conventional electroless plating from the bath containing up to 10.0 g/l of hexagonal boron nitride particles with size 0.5 μm. The Ni-P coating is also prepared as a comparison. Cationic surfactant cetyltrimethylammonium bromide (CTAB) is used to stabilize the electrolyte, and the optimum CTAB concentration resulting in a nonagglomerated dispersion of particles is obtained using a dispersion stability analyzer. Morphology of the coatings and the effect of incorporated particles on coating structure and composition are investigated via scanning electron microscopy, field emission electron probe micro-analyzer and X-ray diffraction analysis. Hardness, roughness, friction coefficient and wear resistance of the coatings are also evaluated using Vickers microhardness tester, atomic force microscopy and ball-on disk machine. The presence of CTAB in the depositing bath has a positive effect on the surface roughness and performance of Ni-P/BN(h) composite coatings. The friction and wear tests results show that incorporation of 14.5 vol% BN(h) particles into the Ni-P coating lowers the coating friction coefficient by about 75% and the wear resistance of the Ni-P composites is approximately 10 times higher than Ni-P coating.

Hexagonal Boron Nitride: A Promising Substrate for Graphene with High Heat Dissipation

NASA Astrophysics Data System (ADS)

Zhang, Zhongwei; Hu, Shiqian; Chen, Jie; Li, Baowen

Supported graphene on standard SiO2 substrate exhibits unsatisfactory heat dissipation performance that is far inferior to the ultrahigh thermal conductivity of suspended case. A suitable substrate for enhancing the thermal transport in supported graphene is highly desirable. By using molecular dynamics simulations, we have studied thermal conductivity of sing-layer graphene (SLG) supported on bulk hexagonal boron nitride (h-BN) substrate. Notable length dependence and high thermal conductivity are observed in h-BN supported SLG, suggesting thermal transport properties are close to that in suspended SLG. At room temperature, thermal conductivity of h-BN supported SLG is as high as 1347.3+/-20.5 W/mK, which is about 77% of suspended case and more than twice of SiO2 supported SLG. Furthermore, the h-BN substrate gives rise to a regular and weak stress distribution in graphene, which results in less suppressed phonon relaxation time and phonon mean free path. We also find stacking and rotation have significant impacts on structure dynamics and thermal conductivity of h-BN supported graphene. Our study provides valuable insights towards the design of realistic supported graphene devices with high performance heat dissipation. Acknowledges the supports from the National Natural Science Foundation of China (Grant No. 51506153 and No. 11334007) and the National Youth 1000 Talents Program in China.

Synergistic Behavior of Tubes, Junctions, and Sheets Imparts Mechano-Mutable Functionality in 3D Porous Boron Nitride Nanostructures

PubMed Central

2015-01-01

One-dimensional (1D) boron nitride nanotube (BNNT) and 2D hexagonal BN (h-BN) are attractive for demonstrating fundamental physics and promising applications in nano-/microscale devices. However, there is a high anisotropy associated with these BN allotropes as their excellent properties are either along the tube axis or in-plane directions, posing an obstacle in their widespread use in technological and industrial applications. Herein, we report a series of 3D BN prototypes, namely, pillared boron nitride (PBN), by fusing single-wall BNNT and monolayer h-BN aimed at filling this gap. We use density functional theory and molecular dynamics simulations to probe the diverse mechano-mutable properties of PBN prototypes. Our results demonstrate that the synergistic effect of the tubes, junctions, and sheets imparts cooperative deformation mechanisms, which overcome the intrinsic limitations of the PBN constituents and provide a number of superior characteristics including 3D balance of strength and toughness, emergence of negative Poisson’s ratio, and elimination of strain softening along the armchair orientation. These features, combined with the ultrahigh surface area and lightweight structure, render PBN as a 3D multifunctional template for applications in graphene-based nanoelectronics, optoelectronics, gas storage, and functional composites with fascinating in-plane and out-of-plane tailorable properties. PMID:25289114

A latent profile analysis of childhood trauma in women with bulimia nervosa: Associations with borderline personality disorder psychopathology.

PubMed

Utzinger, Linsey M; Haukebo, Justine E; Simonich, Heather; Wonderlich, Stephen A; Cao, Li; Lavender, Jason M; Mitchell, James E; Engel, Scott G; Crosby, Ross D

2016-07-01

The aim of this study was to empirically examine naturally occurring groups of individuals with bulimia nervosa (BN) based on their childhood trauma (CT) histories and to compare these groups on a clinically relevant external validator, borderline personality disorder (BPD) psychopathology. This study examined the relationship between CT and BPD psychopathology among 133 women with BN using latent profile analysis (LPA) to classify participants based on histories of CT. Participants completed the Structured Clinical Interview for DSM-IV Axis I Disorders (SCID-I/P), the Diagnostic Interview for Borderlines-Revised (DIB-R), and the Childhood Trauma Questionnaire (CTQ). The LPA revealed four trauma profiles: low/no trauma, emotional trauma, sexual trauma, and polytrauma. Results indicated that the sexual and polytrauma profiles displayed significantly elevated scores on the DIB-R and that the low/no and emotional trauma profiles did not differ significantly on the DIB-R. Secondary analyses revealed elevated levels of a composite CT score among those with both BN and BPD psychopathology compared to those with BN only. These findings suggest that both childhood sexual abuse and the additive effects of childhood polytrauma may be linked to BPD psychopathology in BN. © 2016 Wiley Periodicals, Inc. (Int J Eat Disord 2016; 49:689-694). © 2016 Wiley Periodicals, Inc.

Stressful Life Events Predict Eating Disorder Relapse Following Remission: Six-Year Prospective Outcomes

PubMed Central

Grilo, Carlos M.; Pagano, Maria E.; Stout, Robert L.; Markowitz, John C.; Ansell, Emily B.; Pinto, Anthony; Zanarini, Mary C.; Yen, Shirley; Skodol, Andrew E.

2012-01-01

Objective To examine prospectively the natural course of bulimia nervosa (BN) and eating disorder not-otherwise-specified (EDNOS) and test for the effects of stressful life events (SLE) on relapse after remission from these eating disorders. Method 117 female patients with BN (N = 35) or EDNOS (N = 82) were prospectively followed for 72 months using structured interviews performed at baseline, 6- and 12-months, and then yearly thereafter. ED were assessed with the structured clinical interview for DSM-IV, and monitored over time with the longitudinal interval follow-up evaluation. Personality disorders were assessed with the diagnostic interview for DSM-IV-personality-disorders, and monitored over time with the follow-along-version. The occurrence and specific timing of SLE were assessed with the life events assessment interview. Cox proportional-hazard-regression-analyses tested associations between time-varying levels of SLE and ED relapse, controlling for comorbid psychiatric disorders, ED duration, and time-varying personality-disorder status. Results ED relapse probability was 43%; BN and EDNOS did not differ in time to relapse. Negative SLE significantly predicted ED relapse; elevated work and social stressors were significant predictors. Psychiatric comorbidity, ED duration, and time-varying personality-disorder status were not significant predictors. Discussion Higher work and social stress represent significant warning signs for triggering relapse for women with remitted BN and EDNOS. PMID:21448971

Social networking as a learning tool: nursing students' perception of efficacy.

PubMed

Tower, Marion; Latimer, Sharon; Hewitt, Jayne

2014-06-01

The pedagogical use of social networking technology in education is of growing interest to academics as a potential teaching and learning tool. However, the educational use of social networking sites such as Facebook is still under explored. Nursing students often perceive bioscience subjects as difficult and lack self-efficacy in their ability to be successful. In this case, as the final assessment for a bioscience related subject approached, students became increasingly anxious about their ability to perform in the assessment item. To better support students, a Facebook group was formed. The aim of the study was to examine students' perceptions of the efficacy of using Facebook as a tool to support study. A convenience sample of BN students (n=533 across 3 campuses), enrolled in the subject Medications and Safe Administration, were invited to join. 373 BN students joined the group (70% of the student cohort). A solution-focussed orientation underpinned the management of the group. A descriptive, online survey was administered following release of students' results for the final assessment item to assess students' perceptions of how effective the group had been in helping them learn. The survey contained both quantitative and qualitative questions. Responses were received from 89 students (24%). Survey data were analysed descriptively and qualitative data were analysed thematically by the academic team. Students perceived the group to be an innovative method of study support that guided learning by enhancing self-efficacy in their learning. Students also described how it was useful in promoting peer learning and engaging with academics. Social media platforms such as Facebook have the potential to enhance students' self-efficacy in learning and can support students to develop their learning to a deeper level. Copyright © 2013 Elsevier Ltd. All rights reserved.

Direct conversion of h-BN into c-BN and formation of epitaxial c-BN/diamond heterostructures

DOE Office of Scientific and Technical Information (OSTI.GOV)

Narayan, Jagdish, E-mail: narayan@ncsu.edu; Bhaumik, Anagh; Xu, Weizong

2016-05-14

We have created a new state of BN (named Q-BN) through rapid melting and super undercooling and quenching by using nanosecond laser pulses. Phase pure c-BN is formed either by direct quenching of super undercooled liquid or by nucleation and growth from Q-BN. Thus, a direct conversion of hexagonal boron nitride (h-BN) into phase-pure cubic boron nitride (c-BN) is achieved by nanosecond pulsed laser melting at ambient temperatures and atmospheric pressure in air. According to the P-T phase diagram, the transformation from h-BN into c-BN under equilibrium processing can occur only at high temperatures and pressures, as the hBN-cBN-Liquid triplemore » point is at 3500 K/9.5 GPa or 3700 K/7.0 GPa with a recent theoretical refinement. Using nonequilibrium nanosecond laser melting, we have created super undercooled state and shifted this triple point to as low as 2800 K and atmospheric pressure. The rapid quenching from super undercooled state leads to the formation of a new phase, named as Q-BN. We present detailed characterization of Q-BN and c-BN layers by using Raman spectroscopy, high-resolution scanning electron microscopy, electron-back-scatter diffraction, high-resolution TEM, and electron energy loss spectroscopy, and discuss the mechanism of formation of nanodots, nanoneedles, microneedles, and single-crystal c-BN on sapphire substrate. We have also deposited diamond by pulsed laser deposition of carbon on c-BN and created c-BN/diamond heterostructures, where c-BN acts as a template for epitaxial diamond growth. We discuss the mechanism of epitaxial c-BN and diamond growth on lattice matching c-BN template under pulsed laser evaporation of amorphous carbon, and the impact of this discovery on a variety of applications.« less

How lithium atoms affect the first hyperpolarizability of BN edge-doped graphene.

PubMed

Song, Yao-Dong; Wu, Li-Ming; Chen, Qiao-Ling; Liu, Fa-Kun; Tang, Xiao-Wen

2016-01-01

How do lithium atoms affect the first hyperpolarizability (β0) of boron-nitrogen (BN) edge-doped graphene. In this work, using pentacene as graphene model, Lin@BN-1 edge-doped pentacene and Lin@BN-2 edge-doped pentacene (n = 1, 5) were designed to study this problem. First, two models (BN-1 edge-doped pentacene, and BN-2 edge-doped pentacene ) were formed by doping the BN into the pentacene with different order, and then Li@BN-1 edge-doped pentacene and Li@ BN-2 edge-doped pentacene were obtained by substituting the H atom in BN edge-doped pentacene with a Li atom. The results show that the first hyperpolarizabilities of BN-1 edge-doped pentacene and Li@BN-1 edge-doped pentacene were 4059 a.u. and 6249 a.u., respectively; the first hyperpolarizabilities of BN-2 edge-doped pentacene and Li@BN-2 edge-doped pentacene were 2491 a.u. and 4265 a.u., respectively. The results indicate that the effect of Li substitution is to greatly increase the β0 value. To further enhance the first hyperpolarizability, Li5@ BN-1 edge-doped pentacene and Li5@BN-2 edge-doped pentacene were designed, and were found to exhibit considerably larger first hyperpolarizabilities (β0) (12,112 a.u. and 7921a.u., respectively). This work may inspire further study of the nonlinear properties of BN edge-doped graphene.

Dynamical effects in x-ray absorption spectra of graphene and monolayered h -BN on Ni(111)

NASA Astrophysics Data System (ADS)

Rusz, J.; Preobrajenski, A. B.; Ng, May Ling; Vinogradov, N. A.; Mårtensson, N.; Wessely, O.; Sanyal, B.; Eriksson, O.

2010-02-01

We present first-principles calculations of x-ray absorption spectra of graphene and hexagonal BN monolayer on the Ni(111) substrate. Including dynamical core-hole screening effects according to the theory of Mahan-Nozières-de Dominics (MND) results in an overall good agreement with previously published experimental data and our new observations. This approach provides a unified first-principles description of the electronic structure and core excitations in the sp2 -bonded materials on metal surfaces and a better insight into the dynamics of screening effects. We demonstrate in particular that the observed spectral features of graphene and hexagonal BN can be well reproduced with the MND theory, and that they are determined by a delicate balance between initial and final-state effects.

BN Bonded BN fiber article and method of manufacture

DOEpatents

Hamilton, Robert S.

1981-08-18

A boron nitride bonded boron nitride fiber article and the method for its manufacture which comprises forming a shaped article with a composition comprising a bonding compound selected from boron oxide and boric acid and a structural fiber selected from the group consisting of boron oxide, boron nitride and partially nitrided boron oxide fibers, heating the composition in an anhydrous gas to a temperature above the melting point of the compound and nitriding the resulting article in ammonia gas.

Single photon emission from plasma treated 2D hexagonal boron nitride.

PubMed

Xu, Zai-Quan; Elbadawi, Christopher; Tran, Toan Trong; Kianinia, Mehran; Li, Xiuling; Liu, Daobin; Hoffman, Timothy B; Nguyen, Minh; Kim, Sejeong; Edgar, James H; Wu, Xiaojun; Song, Li; Ali, Sajid; Ford, Mike; Toth, Milos; Aharonovich, Igor

2018-05-03

Artificial atomic systems in solids are becoming increasingly important building blocks in quantum information processing and scalable quantum nanophotonic networks. Amongst numerous candidates, 2D hexagonal boron nitride has recently emerged as a promising platform hosting single photon emitters. Here, we report a number of robust plasma and thermal annealing methods for fabrication of emitters in tape-exfoliated hexagonal boron nitride (hBN) crystals. A two-step process comprising Ar plasma etching and subsequent annealing in Ar is highly robust, and yields an eight-fold increase in the concentration of emitters in hBN. The initial plasma-etching step generates emitters that suffer from blinking and bleaching, whereas the two-step process yields emitters that are photostable at room temperature with emission wavelengths greater than ∼700 nm. Density functional theory modeling suggests that the emitters might be associated with defect complexes that contain oxygen. This is further confirmed by generating the emitters via annealing hBN in air. Our findings advance the present understanding of the structure of quantum emitters in hBN and enhance the nanofabrication toolkit needed to realize integrated quantum nanophotonic circuits.

Cellulose nanobiocomposites with reinforcement of boron nitride: study of thermal, oxygen barrier and chemical resistant properties.

PubMed

Swain, Sarat K; Dash, Satyabrata; Behera, Chandini; Kisku, Sudhir K; Behera, Lingaraj

2013-06-20

A series of cellulose based nanobiocomposites (cellulose/BN) were prepared with incorporation of various percentage of nano boron nitride (BN). The interaction between cellulose and boron nitride was studied by Fourier transform infrared spectroscopy (FTIR). The structure of cellulose/BN nanobiocomposites was investigated by XRD, FESEM, and HRTEM. It was observed that the boron nitride nanoparticles were dispersed within cellulose matrix due to intercalation and partial exfoliation. The quantitative identification of nanobiocomposites was investigated by selected area electron diffraction (SAED). Thermal stabilities of the prepared nanobiocomposites were measured by thermo gravimetric analysis (TGA) and it was found that thermal stability of the nanobiocomposites was higher than the virgin cellulose. The oxygen barrier property of cellulose/BN nanobiocomposites was measured using a gas permeameter and a substantial reduction in oxygen permeability due to increase in boron nitride loading was observed. Further it was noticed that the chemical resistance of the nanobiocomposites was more than the virgin cellulose. Hence, the prepared nanobiocomposite may be widely used for insulating and temperature resistant packaging materials. Copyright © 2013 Elsevier Ltd. All rights reserved.

Template growth of Au, Ni and Ni–Au nanoclusters on hexagonal boron nitride/Rh(111): a combined STM, TPD and AES study

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wu, Fanglue; Huang, Dali; Yue, Yuan

In this study, the template growth of Au, Ni, and Ni–Au bimetallic nanoclusters on hexagonal boron nitride/Rh(111), i.e. h-BN/Rh(111), was investigated via scanning tunneling microscopy (STM), temperature programmed-desorption (TPD), and Auger electron spectroscopy (AES). STM study shows that template growth of Au clusters on h-BN/Rh(111) forms mainly well-dispersed monolayer clusters. In contrast, Ni forms large multilayer clusters showing a relatively high diffusivity on h-BN/Rh(111) substrate. Ni–Au bimetallic clusters are effectively formed first by Au deposition followed by Ni deposition, with the Au clusters functioning as nucleation sites for the subsequently deposited Ni. Further structural analysis was carried out via TPDmore » and AES. The resulting TPD and AES data show the surface composition and charge transfer between Au and Ni of the bimetallic clusters. These results suggest that the h-BN/Rh(111) substrate represents a unique candidate for supporting Ni–Au bimetallic clusters in further catalytic reactions.« less

Template growth of Au, Ni and Ni–Au nanoclusters on hexagonal boron nitride/Rh(111): a combined STM, TPD and AES study

DOE PAGES

Wu, Fanglue; Huang, Dali; Yue, Yuan; ...

2017-09-12

In this study, the template growth of Au, Ni, and Ni–Au bimetallic nanoclusters on hexagonal boron nitride/Rh(111), i.e. h-BN/Rh(111), was investigated via scanning tunneling microscopy (STM), temperature programmed-desorption (TPD), and Auger electron spectroscopy (AES). STM study shows that template growth of Au clusters on h-BN/Rh(111) forms mainly well-dispersed monolayer clusters. In contrast, Ni forms large multilayer clusters showing a relatively high diffusivity on h-BN/Rh(111) substrate. Ni–Au bimetallic clusters are effectively formed first by Au deposition followed by Ni deposition, with the Au clusters functioning as nucleation sites for the subsequently deposited Ni. Further structural analysis was carried out via TPDmore » and AES. The resulting TPD and AES data show the surface composition and charge transfer between Au and Ni of the bimetallic clusters. These results suggest that the h-BN/Rh(111) substrate represents a unique candidate for supporting Ni–Au bimetallic clusters in further catalytic reactions.« less

Surface-enhanced Raman difference between bombesin and its modified analogues on the colloidal and electrochemically roughen silver surfaces.

PubMed

Podstawka, Edyta; Ozaki, Yukihiro

2008-10-01

In this article, surface-enhanced Raman scattering (SERS) spectra of bombesin (BN) and its six modified analogues ([D-Phe(12)]BN, [Tyr(4)]BN, [Tyr(4),D-Phe(12)]BN, [D-Phe(12),Leu(14)]BN, [Leu(13)-(R)-Leu(14)]BN, and [Lys(3)]BN) on a colloidal silver surface are reported and compared with SERS spectra of these species immobilized onto an ellectrochemically roughen silver electrode. Changes in enhancement and wavenumber of proper bands upon adsorption on different silver surfaces are consistent with BN and its analogues adsorption primarily through Trp(8). Slightly different adsorption states of these molecules are observed depending upon natural amino acids substitution. For example, the indole ring in all the peptides interacts with silver nanoparticles in a edge-on orientation. It is additionally coordinated to the silver through the N(1)--H bond for all the peptides, except [Phe(12)]BN. This is in contrary to the results obtained for the silver roughen electrode that show direct but not strong N(1)--H/Ag interaction for all peptides except [D-Phe(12),Leu(14)]BN and [Leu(13)-(R)-Leu(14)]BN. For BN only C==O is not involved in the chemical coordination with the colloidal surface. [Lys(3)]BN and BN also adsorb with the C--N bond of NH(2) group normal and horizontal, respectively, to the colloidal surface, whereas C--NH(2) in other peptides is tilted to this surface. Also, the Trp(8) --CH(2)-- moiety of only [Tyr(4)]BN, [Lys(3)]BN, and [Tyr(4),D-Phe(12)]BN coordinates to Ag, whereas the Phe(12) ring of [Phe(12)]BN, [Tyr(4),D-Phe(12)]BN, and [D-Phe(12),Leu(14)]BN assists in the peptides binding only on the colloidal silver. (c) 2008 Wiley Periodicals, Inc.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Nash, David J.; Restrepo, David T.; Parra, Natalia S.

Catalytic hydrogenation is an important process used for the production of everything from foods to fuels. Current heterogeneous implementations of this process utilize metals as the active species. Until recently, catalytic heterogeneous hydrogenation over a metal-free solid was unknown; implementation of such a system would eliminate the health, environmental, and economic concerns associated with metal-based catalysts. We report good hydrogenation rates and yields for a metal-free heterogeneous hydrogenation catalyst as well as its unique hydrogenation mechanism. We achieved catalytic hydrogenation of olefins over defect-laden h-BN (dh-BN) in a reactor designed to maximize the defects in h-BN sheets. Good yields (>90%)more » and turnover frequencies (6 × 10 –5–4 × 10 –3) were obtained for the hydrogenation of propene, cyclohexene, 1,1-diphenylethene, (E)- and (Z)-1,2-diphenylethene, octadecene, and benzylideneacetophenone. Temperature-programmed desorption of ethene over processed h-BN indicates the formation of a highly defective structure. Solid-state NMR (SSNMR) measurements of dh-BN with high and low propene surface coverages show four different binding modes. The introduction of defects into h-BN creates regions of electronic deficiency and excess. Density functional theory calculations show that both the alkene and hydrogen-bond order are reduced over four specific defects: boron substitution for nitrogen (B N), vacancies (V B and V N), and Stone–Wales defects. SSNMR and binding-energy calculations show that V N are most likely the catalytically active sites. Our work shows that catalytic sites can be introduced into a material previously thought to be catalytically inactive through the production of defects.« less

APCVD hexagonal boron nitride thin films for passive near-junction thermal management of electronics

NASA Astrophysics Data System (ADS)

KC, Pratik; Rai, Amit; Ashton, Taylor S.; Moore, Arden L.

2017-12-01

The ability of graphene to serve as an ultrathin heat spreader has been previously demonstrated with impressive results. However, graphene is electrically conductive, making its use in contact with electronic devices problematic from a reliability and integration perspective. As an alternative, hexagonal boron nitride (h-BN) is a similarly structured material with large in-plane thermal conductivity but which possesses a wide band gap, thereby giving it potential to be utilized for directing contact, near-junction thermal management of electronics without shorting or the need for an insulating intermediate layer. In this work, the viability of using large area, continuous h-BN thin films as direct contact, near-junction heat spreaders for electronic devices is experimentally evaluated. Thin films of h-BN several square millimeters in size were synthesized via an atmospheric pressure chemical vapor deposition (APCVD) method that is both simple and scalable. These were subsequently transferred onto a microfabricated test device that simulated a multigate transistor while also allowing for measurements of the device temperature at various locations via precision resistance thermometry. Results showed that these large-area h-BN films with thicknesses of 77-125 nm are indeed capable of significantly lowering microdevice temperatures, with the best sample showing the presence of the h-BN thin film reduced the effective thermal resistance by 15.9% ± 4.6% compared to a bare microdevice at the same power density. Finally, finite element simulations of these experiments were utilized to estimate the thermal conductivity of the h-BN thin films and identify means by which further heat spreading performance gains could be attained.

Psychodynamic profile and reflective functioning in patients with bulimia nervosa.

PubMed

Mathiesen, Birgit Bork; Pedersen, Signe Holm; Sandros, Charlotte; Katznelson, Hannah; Wilczek, Alexander; Poulsen, Stig; Lunn, Susanne

2015-10-01

The aim of this study was to examine the general psychological functioning of patients suffering from bulimia nervosa (BN) using the Karolinska Psychodynamic Profile (KAPP). Furthermore, KAPP data and data from the Reflective Functioning scale (RF), measuring the ability to mentalize, were combined in order to examine differences in alexithymia, impulse control and affect regulation in patients with high or low RF. Seventy patients with BN were interviewed with both the KAPP and the Adult Attachment Interview (AAI) from which RF is coded. Differences in KAPP scores of patients with high or low RF were analyzed. Most of the patients with BN were found to have a personality structure within the normal or neurotic range (n=50 of 70). BN patients with a high RF had significantly lower scores on KAPP's alexithymia scale than patients with a low RF score, demonstrating that poor mentalizing is related to alexithymia. Concurrently, patients with high RF showed problems with impulse control and coping with aggressive affects according to KAPP scores. Although BN patients with high RF showed good capacities for describing their mental states, they still had difficulties regulating the emotions and impulses related to these states. Among patients suffering from BN, patients with high RF were significantly less alexithymic than low RF patients. The findings of this study are limited by the relatively small numbers of participants especially in the RF subgroups, posing a danger of not finding as significant existing differences in character pathology between high and low RF groups. Copyright © 2015 Elsevier Inc. All rights reserved.

WE-AB-207B-02: A Bayesian Network Approach for Joint Prediction of Tumor Control and Radiation Pneumonitis (RP) in Non-Small-Cell Lung Cancer (NSCLC)

DOE Office of Scientific and Technical Information (OSTI.GOV)

Luo, Y; McShan, D; Matuszak, M

Purpose: NSCLC radiotherapy treatment is a trade-off between controlling the tumor while limiting radiation-induced toxicities. Here we identify hierarchical biophysical relationships that could simultaneously influence both local control (LC) and RP by using an integrated Bayesian Networks (BN) approach. Methods: We studied 79 NSCLC patients treated on prospective protocol with 56 cases of LC and 21 events of RP. Beyond dosimetric information, each patient had 193 features including 12 clinical factors, 60 circulating blood cytokines before and during radiotherapy, 62 microRNAs, and 59 single-nucleotide polymorphisms (SNPs). The most relevant biophysical predictors for both LC and RP were identified using amore » Markov blanket local discovery algorithm and the corresponding BN was constructed using a score-learning algorithm. The area under the free-response receiver operating characteristics (AU-FROC) was used for performance evaluation. Cross-validation was employed to guard against overfitting pitfalls. Results: A BN revealing the biophysical interrelationships jointly in terms of LC and RP was developed and evaluated. The integrated BN included two SNPs, one microRNA, one clinical factor, three pre-treatment cytokines, relative changes of two cytokines between pre and during-treatment, and gEUDs of the GTV (a=-20) and lung (a=1). On cross-validation, the AUC prediction of independent LC was 0.85 (95% CI: 0.75–0.95) and RP was 0.83 (0.73–0.92). The AU-FROC of the integrated BN to predict both LC/RP was 0.81 (0.71–0.90) based on 2000 stratified bootstrap, indicating minimal loss in joint prediction power. Conclusions: We developed a new approach for multiple outcome utility application in radiotherapy based on integrated BN techniques. The BN developed from large-scale retrospective data is able to simultaneously predict LC and RP in NSCLC treatments based on individual patient characteristics. The joint prediction is only slightly compromised compared to independent predictions. Our approach shows promise for use in clinical decision support system for personalized radiotherapy subject to multiple endpoints. These studies were supported by a grant from the NCI/NIH P01-CA59827.« less

Theoretical study of adsorption of amino acids on graphene and BN sheet in gas and aqueous phase with empirical DFT dispersion correction.

PubMed

Singla, Preeti; Riyaz, Mohd; Singhal, Sonal; Goel, Neetu

2016-02-21

Understanding interactions of biomolecules with nanomaterials at the molecular level is crucial to design new materials for practical use. In the present study, adsorption of three distinct types of amino acids, namely, valine, arginine and aspartic acid, over the surface of structurally analogous but chemically different graphene and BN nanosheets has been explored within the formalism of DFT. The explicit dispersion correction incorporated in the computational methodology improves the accuracy of the results by accounting for long range van der Waals interactions and is essential for agreement with experimental values. The real biological environment has been mimicked by re-optimizing all the model structures in an aqueous medium. The study provides ample evidence in terms of adsorption energy, solvation energy, separation distance and charge analysis to conclude that both the nano-surfaces adsorb the amino acids with release of energy and there are no bonded interactions between the two. The polarity of the BN nanosheet provides it an edge over the graphene surface to have more affinity towards amino acids.

Theory of proximity-induced exchange coupling in graphene on hBN/(Co, Ni)

NASA Astrophysics Data System (ADS)

Zollner, Klaus; Gmitra, Martin; Frank, Tobias; Fabian, Jaroslav

2016-10-01

Graphene, being essentially a surface, can borrow some properties of an insulating substrate (such as exchange or spin-orbit couplings) while still preserving a great degree of autonomy of its electronic structure. Such derived properties are commonly labeled as proximity. Here we perform systematic first-principles calculations of the proximity exchange coupling, induced by cobalt (Co) and nickel (Ni) in graphene, via a few (up to three) layers of hexagonal boron nitride (hBN). We find that the induced spin splitting of the graphene bands is of the order of 10 meV for a monolayer of hBN, decreasing in magnitude but alternating in sign by adding each new insulating layer. We find that the proximity exchange can be giant if there is a resonant d level of the transition metal close to the Dirac point. Our calculations suggest that this effect could be present in Co heterostructures, in which a d level strongly hybridizes with the valence-band orbitals of graphene. Since this hybridization is spin dependent, the proximity spin splitting is unusually large, about 10 meV even for two layers of hBN. An external electric field can change the offset of the graphene and transition-metal orbitals and can lead to a reversal of the sign of the exchange parameter. This we predict to happen for the case of two monolayers of hBN, enabling electrical control of proximity spin polarization (but also spin injection) in graphene/hBN/Co structures. Nickel-based heterostructures show weaker proximity effects than cobalt heterostructures. We introduce two phenomenological models to describe the first-principles data. The minimal model comprises the graphene (effective) pz orbitals and can be used to study transport in graphene with proximity exchange, while the pz-d model also includes hybridization with d orbitals, which is important to capture the giant proximity exchange. Crucial to both models is the pseudospin-dependent exchange coupling, needed to describe the different spin splittings of the valence and conduction bands.

First-principles calculated decomposition pathways for LiBH4 nanoclusters

PubMed Central

Huang, Zhi-Quan; Chen, Wei-Chih; Chuang, Feng-Chuan; Majzoub, Eric H.; Ozoliņš, Vidvuds

2016-01-01

We analyze thermodynamic stability and decomposition pathways of LiBH4 nanoclusters using grand-canonical free-energy minimization based on total energies and vibrational frequencies obtained from density-functional theory (DFT) calculations. We consider (LiBH4)n nanoclusters with n = 2 to 12 as reactants, while the possible products include (Li)n, (B)n, (LiB)n, (LiH)n, and Li2BnHn; off-stoichiometric LinBnHm (m ≤ 4n) clusters were considered for n = 2, 3, and 6. Cluster ground-state configurations have been predicted using prototype electrostatic ground-state (PEGS) and genetic algorithm (GA) based structural optimizations. Free-energy calculations show hydrogen release pathways markedly differ from those in bulk LiBH4. While experiments have found that the bulk material decomposes into LiH and B, with Li2B12H12 as a kinetically inhibited intermediate phase, (LiBH4)n nanoclusters with n ≤ 12 are predicted to decompose into mixed LinBn clusters via a series of intermediate clusters of LinBnHm (m ≤ 4n). The calculated pressure-composition isotherms and temperature-pressure isobars exhibit sloping plateaus due to finite size effects on reaction thermodynamics. Generally, decomposition temperatures of free-standing clusters are found to increase with decreasing cluster size due to thermodynamic destabilization of reaction products. PMID:27189731

Effect of the SiCl4 Flow Rate on SiBN Deposition Kinetics in SiCl4-BCl3-NH3-H2-Ar Environment

PubMed Central

Li, Jianping; Qin, Hailong; Liu, Yongsheng; Ye, Fang; Li, Zan; Cheng, Laifei; Zhang, Litong

2017-01-01

To improve the thermal and mechanical stability of SiCf/SiC or C/SiC composites with SiBN interphase, SiBN coating was deposited by low pressure chemical vapor deposition (LPCVD) using SiCl4-BCl3-NH3-H2-Ar gas system. The effect of the SiCl4 flow rate on deposition kinetics was investigated. Results show that deposition rate increases at first and then decreases with the increase of the SiCl4 flow rate. The surface of the coating is a uniform cauliflower-like structure at the SiCl4 flow rate of 10 mL/min and 20 mL/min. The surface is covered with small spherical particles when the flow rate is 30 mL/min. The coatings deposited at various SiCl4 flow rates are all X-ray amorphous and contain Si, B, N, and O elements. The main bonding states are B-N, Si-N, and N-O. B element and B-N bonding decrease with the increase of SiCl4 flow rate, while Si element and Si-N bonding increase. The main deposition mechanism refers to two parallel reactions of BCl3+NH3 and SiCl4+NH3. The deposition process is mainly controlled by the reaction of BCl3+NH3. PMID:28772986

The interface between ferroelectric and 2D material for a Ferroelectric Field-Effect Transistor

NASA Astrophysics Data System (ADS)

Park, Nahee; Kang, Haeyong; Lee, Sang-Goo; Lee, Young Hee; Suh, Dongseok

We have studied electrical property of ferroelectric field-effect transistor which consists of graphene on hexagonal Boron-Nitride (h-BN) gated by a ferroelectric, PMN-PT (i.e. (1-x)Pb(Mg1/3Nb2/3) O3-xPbTiO3) single-crystal substrate. The PMN-PT was expected to have an effect on polarization field into the graphene channel and to induce a giant amount of surface charge. The hexagonal Boron-Nitride (h-BN) flake was directly exfoliated on the PMN-PT substrate for preventing graphene from directly contacting on the PMN-PT substrate. It can make us to observe the effect of the interface between ferroelectric and 2D material on the device operation. Monolayer graphene as 2D channel material, which was confirmed by Raman spectroscopy, was transferred on top of the hexagonal Boron-Nitride (h-BN) by using the conventional dry-transfer method. Here, we can demonstrate that the structure of graphene/hexagonal-BN/ferroelectric field-effect transistor makes us to clearly understand the device operation as well as the interface between ferroelectric and 2D materials by inserting h-BN between them. The phenomena such as anti-hysteresis, current saturation behavior, and hump-like increase of channel current, will be discussed by in terms of ferroelectric switching, polarization-assisted charge trapping.

Prediction of a new graphenelike Si2BN solid

NASA Astrophysics Data System (ADS)

Andriotis, Antonis N.; Richter, Ernst; Menon, Madhu

2016-02-01

While the possibility to create a single-atom-thick two-dimensional layer from any material remains, only a few such structures have been obtained other than graphene and a monolayer of boron nitride. Here, based upon ab initio theoretical simulations, we propose a new stable graphenelike single-atomic-layer Si2BN structure that has all of its atoms with s p2 bonding with no out-of-plane buckling. The structure is found to be metallic with a finite density of states at the Fermi level. This structure can be rolled into nanotubes in a manner similar to graphene. Combining first- and second-row elements in the Periodic Table to form a one-atom-thick material that is also flat opens up the possibility for studying new physics beyond graphene. The presence of Si will make the surface more reactive and therefore a promising candidate for hydrogen storage.

Regional grey matter volume abnormalities in bulimia nervosa and binge-eating disorder.

PubMed

Schäfer, Axel; Vaitl, Dieter; Schienle, Anne

2010-04-01

This study investigated whether bulimia nervosa (BN) and binge-eating disorder (BED) are associated with structural brain abnormalities. Both disorders share the main symptom binge-eating, but are considered differential diagnoses. We attempted to identify alterations in grey matter volume (GMV) that are present in both psychopathologies as well as disorder-specific GMV characteristics. Such information can help to improve neurobiological models of eating disorders and their classification. A total of 50 participants (patients suffering from BN (purge type), BED, and normal-weight controls) underwent structural MRI scanning. GMV for specific brain regions involved in food/reinforcement processing was analyzed by means of voxel-based morphometry. Both patient groups were characterized by greater volumes of the medial orbitofrontal cortex (OFC) compared to healthy controls. In BN patients, who had increased ventral striatum volumes, body mass index and purging severity were correlated with striatal grey matter volume. Altogether, our data implicate a crucial role of the medial OFC in the studied eating disorders. The structural abnormality might be associated with dysfunctions in food reward processing and/or self-regulation. The bulimia-specific volume enlargement of the ventral striatum is discussed in the framework of negative reinforcement through purging and associated weight regulation. Copyright 2009 Elsevier Inc. All rights reserved.

Quantum transport through MoS2 constrictions defined by photodoping.

PubMed

Epping, Alexander; Banszerus, Luca; Güttinger, Johannes; Krückeberg, Luisa; Watanabe, Kenji; Taniguchi, Takashi; Hassler, Fabian; Beschoten, Bernd; Stampfer, Christoph

2018-05-23

We present a device scheme to explore mesoscopic transport through molybdenum disulfide (MoS 2 ) constrictions using photodoping. The devices are based on van-der-Waals heterostructures where few-layer MoS 2 flakes are partially encapsulated by hexagonal boron nitride (hBN) and covered by a few-layer graphene flake to fabricate electrical contacts. Since the as-fabricated devices are insulating at low temperatures, we use photo-induced remote doping in the hBN substrate to create free charge carriers in the MoS 2 layer. On top of the device, we place additional metal structures, which define the shape of the constriction and act as shadow masks during photodoping of the underlying MoS 2 /hBN heterostructure. Low temperature two- and four-terminal transport measurements show evidence of quantum confinement effects.

Rod-like polyaniline supported on three-dimensional boron and nitrogen-co-doped graphene frameworks for high-performance supercapacitors

NASA Astrophysics Data System (ADS)

Liao, Kexuan; Gao, Jialu; Fan, Jinchen; Mo, Yao; Xu, Qunjie; Min, Yulin

2017-12-01

In this work, novel three-dimensional (3D) boron and nitrogen-co-doped three-dimensional (3D) graphene frameworks (BN-GFs) supporting rod-like polyaniline (PANI) are facilely prepared and used as electrodes for high-performance supercapacitors. The results demonstrated that BN-GFs with tuned electronic structure can not only provide a large surface area for rod-like PANI to anchor but also effectively facilitate the ion transfer and charge storage in the electrode. The PANI/BN-GF composite with wrinkled boron and nitrogen-co-doped graphene sheets interconnected by rod-like PANI exhibits excellent capacitive properties with a maximum specific capacitance of 596 F/g at a current density of 0.5 A/g. Notably, they also show excellent cycling stability with more than 81% capacitance retention after 5000 charge-discharge cycles.

Quantum transport through MoS2 constrictions defined by photodoping

NASA Astrophysics Data System (ADS)

Epping, Alexander; Banszerus, Luca; Güttinger, Johannes; Krückeberg, Luisa; Watanabe, Kenji; Taniguchi, Takashi; Hassler, Fabian; Beschoten, Bernd; Stampfer, Christoph

2018-05-01

We present a device scheme to explore mesoscopic transport through molybdenum disulfide (MoS2) constrictions using photodoping. The devices are based on van-der-Waals heterostructures where few-layer MoS2 flakes are partially encapsulated by hexagonal boron nitride (hBN) and covered by a few-layer graphene flake to fabricate electrical contacts. Since the as-fabricated devices are insulating at low temperatures, we use photo-induced remote doping in the hBN substrate to create free charge carriers in the MoS2 layer. On top of the device, we place additional metal structures, which define the shape of the constriction and act as shadow masks during photodoping of the underlying MoS2/hBN heterostructure. Low temperature two- and four-terminal transport measurements show evidence of quantum confinement effects.

Patterning monolayer graphene with zigzag edges on hexagonal boron nitride by anisotropic etching

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wang, Guole; Wu, Shuang; Zhang, Tingting

2016-08-01

Graphene nanostructures are potential building blocks for nanoelectronic and spintronic devices. However, the production of monolayer graphene nanostructures with well-defined zigzag edges remains a challenge. In this paper, we report the patterning of monolayer graphene nanostructures with zigzag edges on hexagonal boron nitride (h-BN) substrates by an anisotropic etching technique. We found that hydrogen plasma etching of monolayer graphene on h-BN is highly anisotropic due to the inert and ultra-flat nature of the h-BN surface, resulting in zigzag edge formation. The as-fabricated zigzag-edged monolayer graphene nanoribbons (Z-GNRs) with widths below 30 nm show high carrier mobility and width-dependent energy gaps atmore » liquid helium temperature. These high quality Z-GNRs are thus ideal structures for exploring their valleytronic or spintronic properties.« less

Normal brain tissue volumes after long-term recovery in anorexia and bulimia nervosa.

PubMed

Wagner, Angela; Greer, Phil; Bailer, Ursula F; Frank, Guido K; Henry, Shannan E; Putnam, Karen; Meltzer, Carolyn C; Ziolko, Scott K; Hoge, Jessica; McConaha, Claire; Kaye, Walter H

2006-02-01

Individuals who are ill with anorexia (AN) and bulimia nervosa (BN) often have increased cerebrospinal fluid (CSF) volumes and decreased total gray and white matter volumes. It is unclear whether such disturbances persist after recovery from an eating disorder. Magnetic resonance imaging was performed on 40 women who were long-term recovered (>1 year no binging, purging, or restricting behaviors, normal weight, and menstrual cycles, not on medication) from restricting or binge/purging type AN or BN and 31 healthy control women (CW). Voxel-based morphometry (VBM) was used for data analysis. Recovered AN and BN subgroups were similar to CW in terms of cerebrospinal fluid (CSF) volume as well as total or regional gray or white matter volume. These findings suggest that structural brain abnormalities are reversible in individuals with eating disorders after long-term recovery.

Engineering of hydrogenated two-dimensional h-BN/C superlattices as electrostatic substrates.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Liu, Zhun; Zhong, Xiaoliang; Yan, Hui

2016-01-14

Hybridized two-dimensional materials incorporating domains from the hexagonal boron nitride (h-BN) and graphene is an interesting branch of materials science due to their highly tunable electronic properties. In the present study, we investigate the hydrogenated two-dimensional (2D) h-BN/C superlattices (SLs) with zigzag edges using first-principles calculations. We found that the domain width, the phase ratio, and the vertical dipole orientation all have significant influence on the stability of SLs. The electronic reconstruction is associated with the lateral polar discontinuities at the zigzag edges and the vertically polarized (B2N2H4)(m) domains, which modifies the electronic structures and the spatial potential of themore » SLs significantly. Furthermore, we demonstrate that the hydrogenated 2D h-BN/C SLs can be applied in engineering the electronic structure of graphene: laterally-varying doping can be achieved by taking advantage of the spatial variation of the surface potential of the SLs. By applying an external vertical electric field on these novel bidirectional heterostructures, graphene doping levels and band offsets can be tuned to a wide range, such that the graphene doping profile can be switched from the bipolar (p-n junction) to unipolar (n(+)-n junction) mode. It is expected that such bidirectional heterostructures provide an effective approach for developing novel nanoscale electronic devices and improving our understanding of the fundamentals of low-dimensional materials.« less

PREFACE: Ultrathin layers of graphene, h-BN and other honeycomb structures Ultrathin layers of graphene, h-BN and other honeycomb structures

NASA Astrophysics Data System (ADS)

Geber, Thomas; Oshima, Chuhei

2012-08-01

Since ancient times, pure carbon materials have been familiar in human society—not only diamonds in jewellery and graphite in pencils, but also charcoal and coal which have been used for centuries as fuel for living and industry. Carbon fibers are stronger, tougher and lighter than steel and increase material efficiency because of their lower weight. Today, carbon fibers and related composite materials are used to make the frames of bicycles, cars and even airplane parts. The two-dimensional allotrope, now called graphene, is just a single layer of carbon atoms, locked together in a strongly bonded honeycomb lattice. In plane, graphene is stiffer than diamond, but out-of-plane it is soft, like rubber. It is virtually invisible, may conduct electricity (heat) better than copper and weighs next to nothing. Carbon compounds with two carbon atoms as a base, such as graphene, graphite or diamond, have isoelectronic sister compounds made of boron-nitrogen pairs: hexagonal and cubic boron nitride, with almost the same lattice constant. Although the two 2D sisters, graphene and h-BN, have the same number of valence electrons, their electronic properties are very different: freestanding h-BN is an insulator, while charge carriers in graphene are highly mobile. The past ten years have seen a great expansion in studies of single-layer and few-layer graphene. This activity has been concerned with the π electron transport in graphene, in electric and magnetic fields. More than 30 years ago, however, single-layer graphene and h-BN on solid surfaces were widely investigated. It was noted that they drastically changed the chemical reactivity of surfaces, and they were known to 'poison' heterogeneous catalysts, to passivate surfaces, to prevent oxidation of surfaces and to act as surfactants. Also, it was realized that the controlled growth of h-BN and graphene on substrates yields the formation of mismatch driven superstructures with peculiar template functionality on the nanometer scale. This special section contains interesting papers on graphene, h-BN and related 'honeycomb' compounds on solid surfaces, which are currently in development. Interfacial interaction strongly modifies the electronic and atomic structures of these overlayer systems and substrate surfaces. In addition, one can recognize a variety of growth phenomena by changing the surface and growth conditions, which are promising as regards fabricating those noble nanosystems. We have great pleasure in acknowledging the enthusiastic response and participation of our invited authors and their diligent preparation of the manuscripts. Ultrathin layers of graphene, h-BN and other honeycomb structures contents Ultrathin layers of graphene, h-BN and other honeycomb structuresThomas Geber and Chuhei Oshima Templating of arrays of Ru nanoclusters by monolayer graphene/Ru Moirés with different periodicitiesEli Sutter, Bin Wang, Peter Albrecht, Jayeeta Lahiri, Marie-Laure Bocquet and Peter Sutter Controllable p-doping of graphene on Ir(111) by chlorination with FeCl3N A Vinogradov, K A Simonov, A V Generalov, A S Vinogradov, D V Vyalikh, C Laubschat, N Mårtensson and A B Preobrajenski Optimizing long-range order, band gap, and group velocities for graphene on close-packed metal surfacesF D Natterer, S Rusponi, M Papagno, C Carbone and H Brune Epitaxial growth of graphene on transition metal surfaces: chemical vapor deposition versus liquid phase depositionSamuel Grandthyll, Stefan Gsell, Michael Weinl, Matthias Schreck, Stefan Hüfner and Frank Müller High-yield boron nitride nanosheets from 'chemical blowing': towards practical applications in polymer compositesXuebin Wang, Amir Pakdel, Chunyi Zhi, Kentaro Watanabe, Takashi Sekiguchi, Dmitri Golberg and Yoshio Bando BCx layers with honeycomb lattices on an NbB2(0001) surfaceChuhei Oshima Epitaxial growth of boron-doped graphene by thermal decomposition of B4CWataru Norimatsu, Koichiro Hirata, Yuta Yamamoto, Shigeo Arai and Michiko Kusunoki Mechanical exfoliation of epitaxial graphene on Ir(111) enabled by Br2 intercalationCharlotte Herbig, Markus Kaiser, Nedjma Bendiab, Stefan Schumacher, Daniel F Förster, Johann Coraux, Klaus Meerholz, Thomas Michely and Carsten Busse Low energy electron microscopy and photoemission electron microscopy investigation of grapheneK L Man and M S Altman Periodic overlayers and moiré patterns: theoretical studies of geometric propertiesKlaus Hermann Silicene structures on silver surfacesHanna Enriquez, Sébastien Vizzini, Abdelkader Kara, Boubekeur Lalmi and Hamid Oughaddou Contrast inversion of the h-BN nanomesh investigated by nc-AFM and Kelvin probe force microscopyS Koch, M Langer, S Kawai, E Meyer and Th Glatzel Probing the electronic structure and optical response of a graphene quantum disk supported on monolayer grapheneWu Zhou, Stephen J Pennycook and Juan-Carlos Idrobo Multi-oriented moiré superstructures of graphene on Ir(111): experimental observations and theoretical modelsLei Meng, Rongting Wu, Lizhi Zhang, Linfei Li, Shixuan Du, Yeliang Wang and H-J Gao The physics of epitaxial graphene on SiC(0001)H Kageshima, H Hibino and S Tanabe

Low molecular weight fucan prevents transplant coronaropathy in rat cardiac allograft model.

PubMed

Alkhatib, Bassam; Freguin-Bouilland, Caroline; Lallemand, Françoise; Henry, Jean Paul; Litzler, Pierre-Yves; Marie, Jean Paul; Richard, Vincent; Thuillez, Christian; Plissonnier, Didier

2006-06-01

Transplant arteriosclerosis is the main cause of long-term failure after cardiac transplantation. Vascular rejection is thought to be due to intimal proliferation occurring in response to arterial wall immune-mediated injury. A low molecular weight fucan (LMWF) compound, a sulfated polysaccharide, has been demonstrated to increase plasma levels of stromal cell-derived factor 1 (SDF-1) and consequently to mobilize bone marrow-derived vascular progenitor cells (BMVPC). The aim of this study was to evaluate the capacity of LMWF to prevent coronary intimal proliferation in a rat cardiac allograft model. Heterotopic abdominal cardiac graftings were performed in Brown Norway (BN) and Lewis (LEW) rats. Animals were divided into 4 groups of 10 rats. Two groups were treated intramuscularly with LMWF (5 mg/kg/day) (one BN to BN isograft group, and one BN to LEW allograft group); and two control groups were LMWF-untreated (one BN to BN isograft group and one BN to LEW allograft group). All animals were treated by cyclosporin (15 mg/kg/day) sub-cutaneously and sacrificed at day 30. The cardiac grafts were assessed by morphometry of structural parameters and by histological and immunohistochemical analyses. All cardiac isografts were devoid of any coronary and parenchymal lesions. In contrast, the majority of untreated allografts developed coronary intimal proliferation in close association with intimal and adventitial inflammatory CD68(+) cell infiltration. Further, the parenchyma exhibited large areas of actin(+) cells (myofibroblasts) of recipient origin colocalized with the CD68(+) infiltrating cells. Interestingly, all LMWF-treated allografts were well protected against coronary and parenchymal lesions and the coronary arteries exhibited an intimal monolayer of flat cells, which however were CD34 negative. treatment with LMWF appeared very effective in this rat cardiac allograft model to prevent arterial and parenchymal lesions occurring in response to alloimmune injury. However this protective effect does not appear to depend on mobilization of bone marrow-derived cells.

Beyond where to how: a machine learning approach for sensing mobility contexts using smartphone sensors.

PubMed

Guinness, Robert E

2015-04-28

This paper presents the results of research on the use of smartphone sensors (namely, GPS and accelerometers), geospatial information (points of interest, such as bus stops and train stations) and machine learning (ML) to sense mobility contexts. Our goal is to develop techniques to continuously and automatically detect a smartphone user's mobility activities, including walking, running, driving and using a bus or train, in real-time or near-real-time (<5 s). We investigated a wide range of supervised learning techniques for classification, including decision trees (DT), support vector machines (SVM), naive Bayes classifiers (NB), Bayesian networks (BN), logistic regression (LR), artificial neural networks (ANN) and several instance-based classifiers (KStar, LWLand IBk). Applying ten-fold cross-validation, the best performers in terms of correct classification rate (i.e., recall) were DT (96.5%), BN (90.9%), LWL (95.5%) and KStar (95.6%). In particular, the DT-algorithm RandomForest exhibited the best overall performance. After a feature selection process for a subset of algorithms, the performance was improved slightly. Furthermore, after tuning the parameters of RandomForest, performance improved to above 97.5%. Lastly, we measured the computational complexity of the classifiers, in terms of central processing unit (CPU) time needed for classification, to provide a rough comparison between the algorithms in terms of battery usage requirements. As a result, the classifiers can be ranked from lowest to highest complexity (i.e., computational cost) as follows: SVM, ANN, LR, BN, DT, NB, IBk, LWL and KStar. The instance-based classifiers take considerably more computational time than the non-instance-based classifiers, whereas the slowest non-instance-based classifier (NB) required about five-times the amount of CPU time as the fastest classifier (SVM). The above results suggest that DT algorithms are excellent candidates for detecting mobility contexts in smartphones, both in terms of performance and computational complexity.

Beyond Where to How: A Machine Learning Approach for Sensing Mobility Contexts Using Smartphone Sensors †

PubMed Central

Guinness, Robert E.

2015-01-01

This paper presents the results of research on the use of smartphone sensors (namely, GPS and accelerometers), geospatial information (points of interest, such as bus stops and train stations) and machine learning (ML) to sense mobility contexts. Our goal is to develop techniques to continuously and automatically detect a smartphone user's mobility activities, including walking, running, driving and using a bus or train, in real-time or near-real-time (<5 s). We investigated a wide range of supervised learning techniques for classification, including decision trees (DT), support vector machines (SVM), naive Bayes classifiers (NB), Bayesian networks (BN), logistic regression (LR), artificial neural networks (ANN) and several instance-based classifiers (KStar, LWLand IBk). Applying ten-fold cross-validation, the best performers in terms of correct classification rate (i.e., recall) were DT (96.5%), BN (90.9%), LWL (95.5%) and KStar (95.6%). In particular, the DT-algorithm RandomForest exhibited the best overall performance. After a feature selection process for a subset of algorithms, the performance was improved slightly. Furthermore, after tuning the parameters of RandomForest, performance improved to above 97.5%. Lastly, we measured the computational complexity of the classifiers, in terms of central processing unit (CPU) time needed for classification, to provide a rough comparison between the algorithms in terms of battery usage requirements. As a result, the classifiers can be ranked from lowest to highest complexity (i.e., computational cost) as follows: SVM, ANN, LR, BN, DT, NB, IBk, LWL and KStar. The instance-based classifiers take considerably more computational time than the non-instance-based classifiers, whereas the slowest non-instance-based classifier (NB) required about five-times the amount of CPU time as the fastest classifier (SVM). The above results suggest that DT algorithms are excellent candidates for detecting mobility contexts in smartphones, both in terms of performance and computational complexity. PMID:25928060

BnSGS3 Has Differential Effects on the Accumulation of CMV, ORMV and TuMV in Oilseed Rape

PubMed Central

Chen, Quan; Wang, Jie; Hou, Mingsheng; Liu, Shengyi; Huang, Junyan; Cai, Li

2015-01-01

Virus diseases greatly affect oilseed rape (Brassica napus) production. Investigating antiviral genes may lead to the development of disease-resistant varieties of oilseed rape. In this study, we examined the effects of the suppressor of gene silencing 3 in Brassica napus (BnSGS3, a putative antiviral gene) with different genus viruses by constructing BnSGS3-overexpressing (BnSGS3-Ov) and BnSGS3-silenced (BnSGS3-Si) oilseed rape (cv. Zhongshuang No. 6) plants. These three viruses are Oilseed rape mosaic virus (ORMV), Turnip mosaic virus (TuMV) and Cucumber mosaic virus (CMV). The native BnSGS3 expressed in all examined tissues with the highest expression in siliques. All three viruses induced BnSGS3 expression, but ORMV induced a dramatic increase in the BnSGS3-Ov plants, followed by TuMV and CMV. Upon inoculation with three different viruses, transcript abundance of BnSGS3 gene follows: BnSGS3-Ov > non-transgenic plants > BnSGS3-Si. The accumulation quantities of ORMV and TuMV exhibited a similar trend. However, CMV accumulation showed an opposite trend where virus accumulations were negatively correlated with BnSGS3 expression. The results suggest that BnSGS3 selectively inhibits CMV accumulation but promotes ORMV and TuMV accumulation. BnSGS3 should be used in different ways (up- and down-regulation) for breeding virus-resistant oilseed rape varieties. PMID:26225990

Trait-level and momentary correlates of bulimia nervosa with a history of anorexia nervosa.

PubMed

Goldschmidt, Andrea B; Peterson, Carol B; Wonderlich, Stephen A; Crosby, Ross D; Engel, Scott G; Mitchell, James E; Crow, Scott J; Cao, Li; Berg, Kelly C

2013-03-01

Some investigators have suggested subtyping bulimia nervosa (BN) by anorexia nervosa (AN) history. We examined trait-level and momentary eating-related and psychosocial factors in BN with and without an AN history. Interview, questionnaire, and ecological momentary assessment data of eating-related and psychological symptoms were collected from 122 women with BN, including 43 with (BN+) and 79 without an AN history (BN-). Body mass index (kg/m(2) ) was lower in BN+ than BN- (p = 0.001). Groups did not differ on trait-level anxiety, shape/weight concerns, psychiatric comorbidity, or dietary restraint; or on momentary anxiety, dietary restriction, binge eating, purging, or exercise frequency, or affective patterns surrounding binge/purge behaviors. Negative affect increased prior to exercise and decreased thereafter in BN+ but not BN-, although groups did not statistically differ. Results do not support formally subtyping BN by AN history. Exercise in BN+ may modulate negative affect, which could have important treatment implications. Copyright © 2012 Wiley Periodicals, Inc.

75 FR 79990 - Airworthiness Directives; B-N Group Ltd. Model BN-2, BN-2A, BN-2A-2, BN-2A-3, BN-2A-6, BN-2A-8...

Federal Register 2010, 2011, 2012, 2013, 2014

2010-12-21

... service information. We might also have proposed different actions in this AD from those in the MCAI in...--AIRWORTHINESS DIRECTIVES 1. The authority citation for part 39 continues to read as follows: Authority: 49 U.S.C... inspect for deformation of shape and signs of concavity the elevator tip assemblies (top and bottom...

Investigation on two abnormal phenomena about thermal conductivity enhancement of BN/EG nanofluids.

PubMed

Li, Yanjiao; Zhou, Jing'en; Luo, Zhifeng; Tung, Simon; Schneider, Eric; Wu, Jiangtao; Li, Xiaojing

2011-07-09

The thermal conductivity of boron nitride/ethylene glycol (BN/EG) nanofluids was investigated by transient hot-wire method and two abnormal phenomena was reported. One is the abnormal higher thermal conductivity enhancement for BN/EG nanofluids at very low-volume fraction of particles, and the other is the thermal conductivity enhancement of BN/EG nanofluids synthesized with large BN nanoparticles (140 nm) which is higher than that synthesized with small BN nanoparticles (70 nm). The chain-like loose aggregation of nanoparticles is responsible for the abnormal increment of thermal conductivity enhancement for the BN/EG nanofluids at very low particles volume fraction. And the difference in specific surface area and aspect ratio of BN nanoparticles may be the main reasons for the abnormal difference between thermal conductivity enhancements for BN/EG nanofluids prepared with 140- and 70-nm BN nanoparticles, respectively.

Pressure sensing element based on the BN-graphene-BN heterostructure

NASA Astrophysics Data System (ADS)

Li, Mengwei; Wu, Chenggen; Zhao, Shiliang; Deng, Tao; Wang, Junqiang; Liu, Zewen; Wang, Li; Wang, Gao

2018-04-01

In this letter, we report a pressure sensing element based on the graphene-boron nitride (BN) heterostructure. The heterostructure consists of monolayer graphene sandwiched between two layers of vertically stacked dielectric BN nanofilms. The BN layers were used to protect the graphene layer from oxidation and pollution. Pressure tests were performed to investigate the characteristics of the BN-graphene-BN pressure sensing element. A sensitivity of 24.85 μV/V/mmHg is achieved in the pressure range of 130-180 kPa. After exposing the BN-graphene-BN pressure sensing element to the ambient environment for 7 days, the relative resistance change in the pressure sensing element is only 3.1%, while that of the reference open-faced graphene device without the BN protection layers is 15.7%. Thus, this strategy is promising for fabricating practical graphene pressure sensors with improved performance and stability.

Hexagonal boron nitride neutron detectors with high detection efficiencies

DOE Office of Scientific and Technical Information (OSTI.GOV)

Maity, A.; Grenadier, S. J.; Li, J.

Here, neutron detectors fabricated from 10B enriched hexagonal boron nitride (h- 10BN or h-BN) epilayers have demonstrated the highest thermal neutron detection efficiency among solid-state neutron detectors to date at about 53%. In this work, photoconductive-like vertical detectors with a detection area of 1 × 1 mm 2 were fabricated from 50 μm thick free-standing h-BN epilayers using Ni/Au and Ti/Al bilayers as ohmic contacts. Leakage currents, mobility-lifetime (μτ) products under UV photoexcitation, and neutron detection efficiencies have been measured for a total of 16 different device configurations. The results have unambiguously identified that detectors incorporating the Ni/Au bilayer onmore » both surfaces as ohmic contacts and using the negatively biased top surface for neutron irradiation are the most desired device configurations. It was noted that high growth temperatures of h- 10BN epilayers on sapphire substrates tend to yield a higher concentration of oxygen impurities near the bottom surface, leading to a better device performance by the chosen top surface for irradiation than by the bottom. Preferential scattering of oxygen donors tends to reduce the mobility of holes more than that of electrons, making the biasing scheme with the ability of rapidly extracting holes at the irradiated surface while leaving the electrons to travel a large average distance inside the detector at a preferred choice. When measured against a calibrated 6LiF filled micro-structured semiconductor neutron detector, it was shown that the optimized configuration has pushed the detection efficiency of h-BN neutron detectors to 58%. These detailed studies also provided a better understanding of growth-mediated impurities in h-BN epilayers and their effects on the charge collection and neutron detection efficiencies.« less

Hexagonal boron nitride neutron detectors with high detection efficiencies

NASA Astrophysics Data System (ADS)

Maity, A.; Grenadier, S. J.; Li, J.; Lin, J. Y.; Jiang, H. X.

2018-01-01

Neutron detectors fabricated from 10B enriched hexagonal boron nitride (h-10BN or h-BN) epilayers have demonstrated the highest thermal neutron detection efficiency among solid-state neutron detectors to date at about 53%. In this work, photoconductive-like vertical detectors with a detection area of 1 × 1 mm2 were fabricated from 50 μm thick free-standing h-BN epilayers using Ni/Au and Ti/Al bilayers as ohmic contacts. Leakage currents, mobility-lifetime (μτ) products under UV photoexcitation, and neutron detection efficiencies have been measured for a total of 16 different device configurations. The results have unambiguously identified that detectors incorporating the Ni/Au bilayer on both surfaces as ohmic contacts and using the negatively biased top surface for neutron irradiation are the most desired device configurations. It was noted that high growth temperatures of h-10BN epilayers on sapphire substrates tend to yield a higher concentration of oxygen impurities near the bottom surface, leading to a better device performance by the chosen top surface for irradiation than by the bottom. Preferential scattering of oxygen donors tends to reduce the mobility of holes more than that of electrons, making the biasing scheme with the ability of rapidly extracting holes at the irradiated surface while leaving the electrons to travel a large average distance inside the detector at a preferred choice. When measured against a calibrated 6LiF filled micro-structured semiconductor neutron detector, it was shown that the optimized configuration has pushed the detection efficiency of h-BN neutron detectors to 58%. These detailed studies also provided a better understanding of growth-mediated impurities in h-BN epilayers and their effects on the charge collection and neutron detection efficiencies.

Heterogeneous Metal-Free Hydrogenation over Defect-Laden Hexagonal Boron Nitride

DOE PAGES

Nash, David J.; Restrepo, David T.; Parra, Natalia S.; ...

2016-12-21

Catalytic hydrogenation is an important process used for the production of everything from foods to fuels. Current heterogeneous implementations of this process utilize metals as the active species. Until recently, catalytic heterogeneous hydrogenation over a metal-free solid was unknown; implementation of such a system would eliminate the health, environmental, and economic concerns associated with metal-based catalysts. We report good hydrogenation rates and yields for a metal-free heterogeneous hydrogenation catalyst as well as its unique hydrogenation mechanism. We achieved catalytic hydrogenation of olefins over defect-laden h-BN (dh-BN) in a reactor designed to maximize the defects in h-BN sheets. Good yields (>90%)more » and turnover frequencies (6 × 10 –5–4 × 10 –3) were obtained for the hydrogenation of propene, cyclohexene, 1,1-diphenylethene, (E)- and (Z)-1,2-diphenylethene, octadecene, and benzylideneacetophenone. Temperature-programmed desorption of ethene over processed h-BN indicates the formation of a highly defective structure. Solid-state NMR (SSNMR) measurements of dh-BN with high and low propene surface coverages show four different binding modes. The introduction of defects into h-BN creates regions of electronic deficiency and excess. Density functional theory calculations show that both the alkene and hydrogen-bond order are reduced over four specific defects: boron substitution for nitrogen (B N), vacancies (V B and V N), and Stone–Wales defects. SSNMR and binding-energy calculations show that V N are most likely the catalytically active sites. Our work shows that catalytic sites can be introduced into a material previously thought to be catalytically inactive through the production of defects.« less

Hexagonal boron nitride neutron detectors with high detection efficiencies

DOE PAGES

Maity, A.; Grenadier, S. J.; Li, J.; ...

2018-01-23

Here, neutron detectors fabricated from 10B enriched hexagonal boron nitride (h- 10BN or h-BN) epilayers have demonstrated the highest thermal neutron detection efficiency among solid-state neutron detectors to date at about 53%. In this work, photoconductive-like vertical detectors with a detection area of 1 × 1 mm 2 were fabricated from 50 μm thick free-standing h-BN epilayers using Ni/Au and Ti/Al bilayers as ohmic contacts. Leakage currents, mobility-lifetime (μτ) products under UV photoexcitation, and neutron detection efficiencies have been measured for a total of 16 different device configurations. The results have unambiguously identified that detectors incorporating the Ni/Au bilayer onmore » both surfaces as ohmic contacts and using the negatively biased top surface for neutron irradiation are the most desired device configurations. It was noted that high growth temperatures of h- 10BN epilayers on sapphire substrates tend to yield a higher concentration of oxygen impurities near the bottom surface, leading to a better device performance by the chosen top surface for irradiation than by the bottom. Preferential scattering of oxygen donors tends to reduce the mobility of holes more than that of electrons, making the biasing scheme with the ability of rapidly extracting holes at the irradiated surface while leaving the electrons to travel a large average distance inside the detector at a preferred choice. When measured against a calibrated 6LiF filled micro-structured semiconductor neutron detector, it was shown that the optimized configuration has pushed the detection efficiency of h-BN neutron detectors to 58%. These detailed studies also provided a better understanding of growth-mediated impurities in h-BN epilayers and their effects on the charge collection and neutron detection efficiencies.« less

Phonon Transport at the Interfaces of Vertically Stacked Graphene and Hexagonal Boron Nitride Heterostructures

DOE PAGES

Yan, Zhequan; Chen, Liang; Yoon, Mina; ...

2016-01-12

Hexagonal boron nitride (h-BN) is a substrate for graphene based nano-electronic devices. We investigate the ballistic phonon transport at the interface of vertically stacked graphene and h-BN heterostructures using first principles density functional theory and atomistic Green's function simulations considering the influence of lattice stacking. We compute the frequency and wave-vector dependent transmission function and observe distinct stacking-dependent phonon transmission features for the h-BN/graphene/h-BN sandwiched systems. We find that the in-plane acoustic modes have the dominant contributions to the phonon transmission and thermal boundary conductance (TBC) for the interfaces with the carbon atom located directly on top of the boronmore » atom (C–B matched) because of low interfacial spacing. The low interfacial spacing is a consequence of the differences in the effective atomic volume of N and B and the difference in the local electron density around N and B. For the structures with the carbon atom directly on top of the nitrogen atom (C–N matched), the spatial distance increases and the contribution of in-plane modes to the TBC decreases leading to higher contributions by out-of-plane acoustic modes. We find that the C–B matched interfaces have stronger phonon–phonon coupling than the C–N matched interfaces, which results in significantly higher TBC (more than 50%) in the C–B matched interface. The findings in this study will provide insights to understand the mechanism of phonon transport at h-BN/graphene/h-BN interfaces, to better explain the experimental observations and to engineer these interfaces to enhance heat dissipation in graphene based electronic devices.« less

Cellulose nanofibrils (CNF) filled boron nitride (BN) nanocomposites

DOE Office of Scientific and Technical Information (OSTI.GOV)

Sulaiman, Hanisah Syed; Hua, Chia Chin; Zakaria, Sarani

In this study, nanocomposite using cellulose nanofibrils filled with different percentage of boron nitride (CNF-BN) were prepared. The objective of this research is to study the effect of different percentage of BN to the thermal conductivity of the nanocomposite produced. The CNF-BN nanocomposite were characterization by FT-IR, SEM and thermal conductivity. The FT-IR analysis of the CNF-BN nanocomposite shows all the characteristic peaks of cellulose and BN present in all samples. The dispersion of BN in CNF were seen through SEM analysis. The effect of different loading percentage of BN to the thermal conductivity of the nanocomposite were also investigated.

Clinician Beliefs and Attitudes about Buprenorphine/Naloxone Diversion

PubMed Central

Schuman-Olivier, Zev; Connery, Hilary; Griffin, Margaret L.; Wyatt, Steve A.; Wartenberg, Alan A.; Borodovsky, Jacob; Renner, John A.; Weiss, Roger D.

2013-01-01

Background and Objectives Concern about diversion of buprenorphine/naloxone (B/N) in the U.S. may affect prescribing patterns and policy decisions. This study examines addiction treatment clinician beliefs and attitudes regarding B/N diversion. Methods Participants (n=369) completed a 34-item survey in 2010 during two national symposia on opioid dependence. We conducted multivariable regression, examining the relationship of perceived danger from B/N diversion with clinician characteristics and their beliefs about B/N treatment and diversion. We compared causal beliefs about diversion among clinicians with and without B/N treatment experience. Results Forty percent of clinicians believed that B/N diversion is a dangerous problem. The belief that B/N diversion increases accidental overdoses in the community was strongly associated with perceived danger from B/N diversion. Conclusions and Scientific Significance Attitudes and beliefs, not education level, were associated with clinician’s perceived danger from B/N diversion. Clinicians with greater B/N patient experience were more likely to believe treatment access barriers are the major cause of B/N diversion. PMID:24131165

Comparison of MWIR unipolar barrier structures based on strained layer superlattices (Conference Presentation)

NASA Astrophysics Data System (ADS)

Ramirez, David A.; Myers, Stephen A.; Kuznetsova, Yuliya; Mathews, Sen; Schuler-Sandy, Theodore; Steenbergen, Elizabeth H.; Morath, Christian P.; Cowan, Vicent M.; Krishna, Sanjay

2016-09-01

In this work, we compare the performance of three MWIR unipolar barrier structures based on the InAs/GaSb Type-2 strained layer superlattice material system. We have designed, fabricated, and characterized pBiBn, pBn, and pBp detector structures. All the structures have been designed so that the cut off wavelength is around 5 microns at 100 K. We fabricated single-pixel devices and characterize their radiometric performance. In addition, we have characterized the degradation of the performance of the devices after exposing the devices to 63 MeV proton radiation to total ionizing dose of 100 kRad (Si). In this report, we compare the performance of the different structures with the objective of determining the advantages and disadvantages of the different designs. This work was supported by the Small Business Innovation Research (SBIR) program under the contract FA9453-14-C-0032, sponsored by the Air Force Research Laboratory (AFRL).

Nonequilibrium BN-ZnO: Optical properties and excitonic effects from first principles

NASA Astrophysics Data System (ADS)

Zhang, Xiao; Schleife, André

2018-03-01

The nonequilibrium boron nitride (BN) phase of zinc oxide (ZnO) has been reported for thin films and nanostructures, however, its properties are not well understood due to a persistent controversy that prevents reconciling experimental and first-principles results for its atomic coordinates. We use first-principles theoretical spectroscopy to accurately compute electronic and optical properties, including single-quasiparticle and excitonic effects: Band structures and densities of states are computed using density functional theory, hybrid functionals, and the G W approximation. Accurate optical absorption spectra and exciton binding energies are computed by solving the Bethe-Salpeter equation for the optical polarization function. Using this data we show that the band-gap difference between BN-ZnO and wurtzite (WZ) ZnO agrees very well with experiment when the theoretical lattice geometry is used, but significantly disagrees for the experimental atomic coordinates. We also show that the optical anisotropy of BN-ZnO differs significantly from that of WZ-ZnO, allowing us to optically distinguish both polymorphs. By using the transfer-matrix method to solve Maxwell's equations for thin films composed of both polymorphs, we illustrate that this opens up a promising route for tuning optical properties.

Deposition of BN interphase coatings from B-trichloroborazine and its effects on the mechanical properties of SiC/SiC composites

NASA Astrophysics Data System (ADS)

Wu, Haitang; Chen, Mingwei; Wei, Xi; Ge, Min; Zhang, Weigang

2010-12-01

Boron nitride thin films were deposited on silicon carbide fibers by chemical vapor deposition at atmospheric pressure from the single source precursor B-trichloroborazine (Cl 3B 3N 3H 3, TCB). The film growth and structure, as a function of deposition temperature, hydrogen gas flow rate, and deposition time, were discussed. The deposition rate reaches a maximum at 1000 °C, then decreases with the increasing of temperature, and the apparent activation energy of the reaction is 127 kJ/mol. Above 1000 °C, gas-phase nucleation determines the deposition process. The deposited BN films were characterized by Raman spectroscopy, X-ray diffraction (XRD) and scanning electron microscopy (SEM). The effect of BN interphase on the mechanical properties of the unidirectional SiC fiber-reinforced SiC matrix (SiC/SiC) composites was also investigated. The results show that the flexural strength of SiC/SiC composites with and without coating is 276 MPa and 70 MPa, respectively, which indicates that BN interphase coating deposited from B-trichloroborazine precursor can effectively adjust the fiber/matrix interface, thus causing a dramatic increase in the mechanical properties of the composites.

Zinc complexes supported by methyl salicylato ligands: synthesis, structure, and application in ring-opening polymerization of L-lactide.

PubMed

Petrus, Rafał; Sobota, Piotr

2013-10-14

Two novel zinc alkoxides supported by chelating methyl salicylato (MesalO; MesalOH = methyl salicylate) ligands were successfully synthesized and characterized. Reaction of MesalOH with ZnEt2 (2:1) gives a tetranuclear cluster [Zn(MesalO)2]4 (1), which by addition of pyridine is transformed to the mononuclear compound [Zn(MesalO)2(py)2] (2). Compounds 1 and 2 were characterized by elemental analysis, NMR, IR, and single crystal X-ray diffraction. The catalytic activity of both compounds was tested for the ring-opening polymerization (ROP) of L-lactide (L-LA). It was found that compounds 1 and 2 are efficient initiators of the ROP of L-LA, yielding cyclic PLLA with weight average molecular weights up to 100 kDa for 2. The treatment of 2 with 1 equiv. of BnOH in toluene afforded a dimeric compound [Zn(OBn)(MesalO)(py)]2 (3). The addition of L-LA to a combination of 1 and 4 equiv. of BnOH in THF or 2 and 1 equiv. of BnOH in toluene led to the rapid and efficient generation of PLLA with end-capped BnO groups.

Molecular Dynamics implementation of BN2D or 'Mercedes Benz' water model

NASA Astrophysics Data System (ADS)

Scukins, Arturs; Bardik, Vitaliy; Pavlov, Evgen; Nerukh, Dmitry

2015-05-01

Two-dimensional 'Mercedes Benz' (MB) or BN2D water model (Naim, 1971) is implemented in Molecular Dynamics. It is known that the MB model can capture abnormal properties of real water (high heat capacity, minima of pressure and isothermal compressibility, negative thermal expansion coefficient) (Silverstein et al., 1998). In this work formulas for calculating the thermodynamic, structural and dynamic properties in microcanonical (NVE) and isothermal-isobaric (NPT) ensembles for the model from Molecular Dynamics simulation are derived and verified against known Monte Carlo results. The convergence of the thermodynamic properties and the system's numerical stability are investigated. The results qualitatively reproduce the peculiarities of real water making the model a visually convenient tool that also requires less computational resources, thus allowing simulations of large (hydrodynamic scale) molecular systems. We provide the open source code written in C/C++ for the BN2D water model implementation using Molecular Dynamics.

Introducing Overlapping Grain Boundaries in Chemical Vapor Deposited Hexagonal Boron Nitride Monolayer Films

PubMed Central

2017-01-01

We demonstrate the growth of overlapping grain boundaries in continuous, polycrystalline hexagonal boron nitride (h-BN) monolayer films via scalable catalytic chemical vapor deposition. Unlike the commonly reported atomically stitched grain boundaries, these overlapping grain boundaries do not consist of defect lines within the monolayer films but are composed of self-sealing bilayer regions of limited width. We characterize this overlapping h-BN grain boundary structure in detail by complementary (scanning) transmission electron microscopy techniques and propose a catalytic growth mechanism linked to the subsurface/bulk of the process catalyst and its boron and nitrogen solubilities. Our data suggest that the overlapping grain boundaries are comparatively resilient against deleterious pinhole formation associated with grain boundary defect lines and thus may reduce detrimental breakdown effects when polycrystalline h-BN monolayer films are used as ultrathin dielectrics, barrier layers, or separation membranes. PMID:28410557

Recent Advances in Azaborine Chemistry

PubMed Central

Campbell, Patrick G.; Marwitz, Adam J. V.

2013-01-01

The chemistry of organoboron compounds has been primarily dominated by their use as powerful reagents in synthetic organic chemistry. Recently, the incorporation of boron as part of a functional target structure has emerged as a useful way to generate diversity in organic compounds. A commonly applied strategy is the replacement of a CC unit with its isoelectronic BN unit. In particular, the BN/CC isosterism of the ubiquitous arene motif has undergone a renaissance in the past decade. The parent molecule of the 1,2-dihydro-1,2-azaborine family has now been isolated. New mono- and polycyclic BN heterocycles have been synthesized for potential use in biomedical and materials science applications. This review is a tribute to Dewar's first synthesis of a monocyclic 1,2-dihydro-1,2-azaborine 50 years ago and discusses recent advances in the synthesis and characterization of carbon(C)-boron(B)-nitrogen(N)-containing heterocycles. PMID:22644658

Diagnosis of Cognitive Impairment Compatible with Early Diagnosis of Alzheimer's Disease. A Bayesian Network Model based on the Analysis of Oral Definitions of Semantic Categories.

PubMed

Guerrero, J M; Martínez-Tomás, R; Rincón, M; Peraita, H

2016-01-01

Early detection of Alzheimer's disease (AD) has become one of the principal focuses of research in medicine, particularly when the disease is incipient or even prodromic, because treatments are more effective in these stages. Lexical-semantic-conceptual deficit (LSCD) in the oral definitions of semantic categories for basic objects is an important early indicator in the evaluation of the cognitive state of patients. The objective of this research is to define an economic procedure for cognitive impairment (CI) diagnosis, which may be associated with early stages of AD, by analysing cognitive alterations affecting declarative semantic memory. Because of its low cost, it could be used for routine clinical evaluations or screenings, leading to more expensive and selective tests that confirm or rule out the disease accurately. It should necessarily be an explanatory procedure, which would allow us to study the evolution of the disease in relation to CI, the irregularities in different semantic categories, and other neurodegenerative diseases. On the basis of these requirements, we hypothesise that Bayesian networks (BNs) are the most appropriate tool for this purpose. We have developed a BN for CI diagnosis in mild and moderate AD patients by analysing the oral production of semantic features. The BN causal model represents LSCD in certain semantic categories, both of living things (dog, pine, and apple) and non-living things (chair, car, and trousers), as symptoms of CI. The model structure, the qualitative part of the model, uses domain knowledge obtained from psychology experts and epidemiological studies. Further, the model parameters, the quantitative part of the model, are learnt automatically from epidemiological studies and Peraita and Grasso's linguistic corpus of oral definitions. This corpus was prepared with an incidental sampling and included the analysis of the oral linguistic production of 81 participants (42 cognitively healthy elderly people and 39 mild and moderate AD patients) from Madrid region's hospitals. Experienced neurologists diagnosed these cases following the National Institute of Neurological and Communicative Disorders and Stroke/Alzheimer's Disease and Related Disorders Association (NINCDS-ADRDA)'s Alzheimer's criteria, performing, among other explorations and tests, a minimum neuropsychological exploration that included the Mini-Mental State Examination test. BN's classification performance is remarkable compared with other machine learning methods, achieving 91% accuracy and 94% precision in mild and moderate AD patients. Apart from this, the BN model facilitates the explanation of the reasoning process and the validation of the conclusions and allows the study of uncommon declarative semantic memory impairments. Our method is able to analyse LSCD in a wide set of semantic categories throughout the progression of CI, being a valuable first screening method in AD diagnosis in its early stages. Because of its low cost, it can be used for routine clinical evaluations or screenings to detect AD in its early stages. Besides, due to its knowledge-based structure, it can be easily extended to provide an explanation of the diagnosis and to the study of other neurodegenerative diseases. Further, this is a key advantage of BNs over other machine learning methods with similar performance: it is a recognisable and explanatory model that allows one to study irregularities in different semantic categories.

Ultrahard stitching of nanotwinned diamond and cubic boron nitride in C 2-BN composite

DOE PAGES

Liu, Xiaobing; Chen, Xin; Ma, Hong-An; ...

2016-07-27

Materials combining the hardness and strength of diamond with the higher thermal stability of cubic boron nitride (cBN) have broad potential value in science and engineering. Reacting nanodiamond with cBN at moderate pressures and high temperatures provides a pathway to such materials. Here we report the fabrication of C x-BN nanocomposites, measuring up to 10 mm in longest dimension, by reacting nanodiamond with pre-synthesized cBN in a large-volume press. The nanocomposites consist of randomly-oriented diamond and cBN domains stitched together by sp 3-hybridized C-B and C-N bonds, leading to p-type semiconductivity. Dislocations near the sutures accommodate lattice mismatch between diamondmore » and cBN. Nanotwinning within both diamond and cBN domains further contributes to a bulk hardness ~50% higher than sintered cBN. We find the nanocomposite of C 2-BN exhibits p-type semiconductivity with low activation energy and high thermal stability, making it a functional,ultrahard substance.« less

Oxidation of Boron Nitride in Composites

NASA Technical Reports Server (NTRS)

Jacobson, Nathan S.

1998-01-01

Boron nitride (BN) is a prime candidate for fiber coatings in silicon carbide (SiC) fiber-reinforced SiC matrix composites. The properties of BN allow the fiber to impart beneficial composite properties to the matrix, even at elevated temperatures. The problem with BN is that it is readily attacked by oxygen. Although BN is an internal component of the composite, a matrix crack or pore can create a path for hot oxygen to attack the BN. This type of attack is not well understood. A variety of phenomena have been observed. These include borosilicate glass formation, volatilization of the BN, and under some conditions, preservation of the BN. In this study at the NASA Lewis Research Center, a series of BN materials and BN-containing model composites were methodically examined to understand the various issues dealing with the oxidation of BN in composites. Initial studies were done with a series of monolithic BN materials prepared by hot pressing and chemical vapor deposition (CVD). From these studies, we found that BN showed a strong orientation effect in oxidation and was extremely sensitive to the presence of water vapor in the environment. In addition, CVD material deposited at a high temperature showed much better oxidation behavior than CVD material deposited at a lower temperature.

Coupling of Bayesian Networks with GIS for wildfire risk assessment on natural and agricultural areas of the Mediterranean

NASA Astrophysics Data System (ADS)

Scherb, Anke; Papakosta, Panagiota; Straub, Daniel

2014-05-01

Wildfires cause severe damages to ecosystems, socio-economic assets, and human lives in the Mediterranean. To facilitate coping with wildfire risks, an understanding of the factors influencing wildfire occurrence and behavior (e.g. human activity, weather conditions, topography, fuel loads) and their interaction is of importance, as is the implementation of this knowledge in improved wildfire hazard and risk prediction systems. In this project, a probabilistic wildfire risk prediction model is developed, with integrated fire occurrence and fire propagation probability and potential impact prediction on natural and cultivated areas. Bayesian Networks (BNs) are used to facilitate the probabilistic modeling. The final BN model is a spatial-temporal prediction system at the meso scale (1 km2 spatial and 1 day temporal resolution). The modeled consequences account for potential restoration costs and production losses referred to forests, agriculture, and (semi-) natural areas. BNs and a geographic information system (GIS) are coupled within this project to support a semi-automated BN model parameter learning and the spatial-temporal risk prediction. The coupling also enables the visualization of prediction results by means of daily maps. The BN parameters are learnt for Cyprus with data from 2006-2009. Data from 2010 is used as validation data set. A special focus is put on the performance evaluation of the BN for fire occurrence, which is modeled as binary classifier and thus, could be validated by means of Receiver Operator Characteristic (ROC) curves. With the final best models, AUC values of more than 70% for validation could be achieved, which indicates potential for reliable prediction performance via BN. Maps of selected days in 2010 are shown to illustrate final prediction results. The resulting system can be easily expanded to predict additional expected damages in the mesoscale (e.g. building and infrastructure damages). The system can support planning of preventive measures (e.g. state resources allocation for wildfire prevention and preparedness) and assist recuperation plans of damaged areas.

Two-Dimensional Graphene-Gold Interfaces Serve as Robust Templates for Dielectric Capacitors.

PubMed

Teshome, Tamiru; Datta, Ayan

2017-10-04

The electronic structures of novel heterostructures, namely, graphene-Au van der Waals (vdW) interfaces, have been studied using density functional theory. Dispersion-corrected PBE-D2 functionals are used to describe the phonon spectrum and binding energies. Ab initio molecular dynamics simulations reveal that the vdW framework is preserved till 1200 K. Beyond T = 1200 K, a transition of the quasiplanar Au into the three-dimensional cluster-like structure is observed. A dielectric capacitor is designed by placing 1-4 hexagonal boron nitride (h-BN) monolayers between graphene and Au conductive plates. Charge separation between the Au and graphene plates is carried out under the effect of an external field normal to the graphene-h-BN-Au interface. The gravimetric capacitances are computed as C 1 = 7.6 μF/g and C 2 = 3.2 μF/g for h-BN bilayers with the Au-graphene heterostructures. The capacitive behavior shows strong deviations from the classical charging models and exemplifies the importance of quantum phenomenon at short contacts, which eventually nullifies at large interelectrode distances. The graphene-Au interface is predicted to be an exciting vdW heterostructure with a potential application as a dielectric capacitor.

In vitro and in vivo evaluation of a 64Cu-labeled NOTA-Bn-SCN-Aoc-bombesin analogue in gastrin-releasing peptide receptor expressing prostate cancer.

PubMed

Craft, Jeffrey M; De Silva, Ravindra A; Lears, Kimberly A; Andrews, Rebecca; Liang, Kexian; Achilefu, Samuel; Rogers, Buck E

2012-07-01

Bombesin (BN) is an amphibian peptide that binds to the gastrin-releasing peptide receptor (GRPR). It has been demonstrated that BN analogues can be radiolabeled for potential diagnosis and treatment of GRPR-expressing malignancies. Previous studies have conjugated various chelators to the eight C-terminal amino acids of BN [BN(7-14)] for radiolabeling with 64Cu. Recently, (1,4,7-triazacyclononane-1,4,7-triacetic acid) (NOTA) has been evaluated as the five-coordinate 64Cu complex, with results indicating GRPR-specific tumor uptake. This study aimed to conjugate S-2-(4-isothiocyanatobenzyl)-NOTA (p-SCN-Bn-NOTA) to BN(7-14) such that it could form a six-coordinate complex with 64Cu and to evaluate the resulting peptide. p-SCN-NOTA was conjugated to 8-aminooctanoic acid (Aoc)-BN(7-14) in solution to yield NOTA-Bn-SCN-Aoc-BN(7-14). The unlabeled peptide was evaluated in a cell binding assay using PC-3 prostate cancer cells and 125I-Tyr4-BN to determine the IC50 value. The peptide was radiolabeled with 64Cu and evaluated for internalization into PC-3 cells and for tumor uptake in mice bearing PC-3 xenografts using biodistribution and micro-positron emission tomography imaging studies. The binding assay demonstrated that NOTA-Bn-SCN-Aoc-BN(7-14) bound with high affinity to GRPR with an IC50 of 1.4 nM. The radiolabeled peptide demonstrated time-dependent internalization into PC-3 cells. In vivo, the peptide demonstrated tumor-specific uptake and imaging that were comparable to those of previously reported 64Cu-labeled BN analogues. These studies demonstrate that 64Cu-NOTA-Bn-SCN-Aoc-BN(7-14) binds to GRPR-expressing cells and that it can be used for imaging of GRPR-expressing prostate cancer. Copyright © 2012 Elsevier Inc. All rights reserved.

Overexpression of BnWRKY33 in oilseed rape enhances resistance to Sclerotinia sclerotiorum.

PubMed

Wang, Zheng; Fang, Hedi; Chen, Yu; Chen, Keping; Li, Guanying; Gu, Shoulai; Tan, Xiaoli

2014-09-01

Sclerotinia sclerotiorum causes a devastating disease in oilseed rape (Brassica napus) resulting in a tremendous yield loss worldwide. Studies on various host-pathogen interactions have shown that plant WRKY transcription factors are essential for defence. For the B. napus-S. sclerotiorum interaction, little direct evidence has been found with regard to the biological roles of specific WRKY genes in host resistance. In this study, we isolated a B. napus WRKY gene, BnWRKY33, and found that the gene is highly responsive to S. sclerotiorum infection. Transgenic B. napus plants overexpressing BnWRKY33 showed markedly enhanced resistance to S. sclerotiorum, constitutive activation of the expression of BnPR1 and BnPDF1.2, and inhibition of H2 O2 accumulation in response to pathogen infection. Further, we isolated a mitogen-activated protein (MAP) kinase substrate gene, BnMKS1, and found that not only can BnWRKY33 interact with BnMKS1, which can also interact with BnMPK4, using the yeast two-hybrid assay, consistent with their collective nuclear localization, but also BnWRKY33, BnMKS1 and BnMPK4 are substantially and synergistically expressed in response to S. sclerotiorum infection. In contrast, the three genes showed differential expression in response to phytohormone treatments. Together, these results suggest that BnWRKY33 plays an important role in B. napus defence to S. sclerotiorum, which is most probably associated with the activation of the salicylic acid (SA)- and jasmonic acid (JA)-mediated defence response and inhibition of H2 O2 accumulation, and we propose a potential mechanism in which BnMPK4-BnMKS1-BnWRKY33 exist in a nuclear localized complex to regulate resistance to S. sclerotiorum in oilseed rape. © 2014 BSPP AND JOHN WILEY & SONS LTD.

Tool wear of (Ti, Al) N-coated polycrystalline cubic boron nitride compact in cutting of hardened steel

NASA Astrophysics Data System (ADS)

Wada, Tadahiro; Hanyu, Hiroyuki

2017-11-01

Polycrystalline cubic boron nitride compact (cBN) is effective tool material for cutting hardened steel. In addition to coated high speed steel and coated cemented carbide that has long been used for cutting materials, more recently, coated cBN has also been used. In this study, to verify the effectiveness of the (Ti,Al)N-coated cBN, which is formed on the substrate of cBN by the physical vapor deposition method, the hardened steel was turned with the (Ti,Al)N-coated cBN tool at a cutting speed of 3.33, 5.00 m/s, a feed rate of 0.3 mm/rev and a depth of cut of 0.1 mm. Furthermore, the uncoated cBN, which was the substrate of the (Ti,Al)N-coated, was also used. The tool wear of the cBN tools was experimentally investigated. The following results were obtained: (1) The contact area between the rake face and the chip of the (Ti,.Al)N-coated cBN tool was smaller than that of the uncoated cBN tool. (2) The tool wear of the (Ti,Al)N-coated cBN was smaller than that of uncoated cBN. (3) The wear progress of the (Ti,Al)N-coated cBN with the main element phase of the TiCN-Al, was slower than that of the (Ti,Al)N-coated cBN with the main element phase of the TiN-Al. (4) In the case of the high cutting speed of 5.00 m/s, the tool wear of the (Ti,Al)N-coated cBN was also smaller than that of uncoated cBN. The above results clarify that the (Ti,Al)N-coated cBN can be used as a tool material in high feed cutting of hardened steel.

Enhanced adsorption of Co atoms on grain boundary of boron nitride

NASA Astrophysics Data System (ADS)

Zhang, Tingting; Chen, Guibin; Zhu, Liyan

2017-11-01

Structural, energetic, electronic, and magnetic properties of Co monomer, dimer, and trimer adsorbed on a single-layer boron nitride (BN) with a grain boundary (GB) consisting of tetragons and octagons ( 4|8) are theoretically explored via density functional calculations. Due to the presence of 4|8 GB, the adsorption energies (EAs) of small Co clusters are generally enhanced by 10% as compared with those adsorbed on pristine BN, e.g., the EA of Co monomer, and dimer increase by 0.1 eV on a global amount of 0.87 eV, and 0.2 eV for the case of Co trimer. Most interestingly, the increase in adsorption energy exhibits a strong correlation to the number of atoms directly bonded to the substrate. The enhanced binding of Co adatom on the BN with 4|8 GBs ( BN 48 ) is due to the strong hybridization of d orbitals of Co adatom and the localized defect states at the 4|8 GBs. However, the GBs have negligible influence on the electronic and magnetic properties of adsorbates. Hence, the two-dimensional (2D) nanosheets with linear GBs might be a better candidate for anchoring the transition metal atoms than pristine BN. Such a strategy may also be applied to other 2D materials, e.g., MoS2 and phosphorene, to enhance the binding of adatom on them, or to utilize them as 1D templates to assemble transition metal atoms into nanowires.

Satiation deficits and binge eating: Probing differences between bulimia nervosa and purging disorder using an ad lib test meal.

PubMed

Keel, Pamela K; Haedt-Matt, Alissa A; Hildebrandt, Britny; Bodell, Lindsay P; Wolfe, Barbara E; Jimerson, David C

2018-08-01

Purging disorder (PD) has been included as a named condition within the DSM-5 category of Other Specified Feeding or Eating Disorder and differs from bulimia nervosa (BN) in the absence of binge-eating episodes. The current study evaluated satiation through behavioral and self-report measures to understand how this construct may explain distinct symptom presentations for bulimia nervosa (BN) and purging disorder (PD). Women (N = 119) were recruited from the community if they met DSM-5 criteria for BN (n = 57), PD (n = 31), or were free of eating pathology (n = 31 controls). Participants completed structured clinical interviews and questionnaires and an ad lib test meal during which they provided reports of subjective states. Significant group differences were found on self-reported symptoms, ad lib test meal intake, and subjective responses to food intake between individuals with eating disorders and controls and between BN and PD. Further, ad lib intake was associated with self-reported frequency and size of binge episodes. In a multivariable model, the amount of food consumed during binges as reported during clinical interviews predicted amount of food consumed during the ad lib test meal, controlling for other binge-related variables. Satiation deficits distinguish BN from PD and appear to be specifically linked to the size of binge episodes. Future work should expand exploration of physiological bases of these differences to contribute to novel interventions. Copyright © 2018 Elsevier Ltd. All rights reserved.

Mild, moderate, meaningful? Examining the psychological and functioning correlates of DSM-5 eating disorder severity specifiers.

PubMed

Gianini, Loren; Roberto, Christina A; Attia, Evelyn; Walsh, B Timothy; Thomas, Jennifer J; Eddy, Kamryn T; Grilo, Carlos M; Weigel, Thomas; Sysko, Robyn

2017-08-01

This study evaluated the DSM-5 severity specifiers for treatment-seeking groups of participants with anorexia nervosa (AN), the purging form of bulimia nervosa (BN), and binge-eating disorder (BED). Hundred and sixty-two participants with AN, 93 participants with BN, and 343 participants with BED were diagnosed using semi-structured interviews, sub-categorized using DSM-5 severity specifiers and compared on demographic and cross-sectional clinical measures. In AN, the number of previous hospitalizations and the duration of illness increased with severity, but there was no difference across severity groups on measures of eating pathology, depression, or measures of self-reported physical or emotional functioning. In BN, the level of eating concerns increased across the severity groups, but the groups did not differ on measures of depression, self-esteem, and most eating pathology variables. In BN, support was also found for an alternative severity classification scheme based upon number of methods of purging. In BED, levels of several measures of eating pathology and self-reported physical and emotional functioning increased across the severity groups. For BED, however, support was also found for an alternative severity classification scheme based upon overvaluation of shape and weight. Preliminary evidence was also found for a transdiagnostic severity index based upon overvaluation of shape and weight. Overall, these data show limited support for the DSM-5 severity specifiers for BN and modest support for the DSM-5 severity specifiers for AN and BED. © 2017 Wiley Periodicals, Inc.

The relationship of bulimia and anorexia nervosa with bipolar disorder and its temperamental foundations.

PubMed

Lunde, Anna V; Fasmer, Ole B; Akiskal, Kareen K; Akiskal, Hagop S; Oedegaard, Ketil J

2009-06-01

Earlier studies have suggested a relationship between bipolar disorder (BP) and eating disorders (ED), more specifically, bulimia nervosa (BN) and bipolar II disorder (BP-II). In the present report we extend this relationship to broader definitions of bipolarity. Semi-structured interview of 201 patients with DSM-IV criteria for major affective disorders combined with Akiskal and Mallya criteria for Affective temperaments. To diagnose lifetime comorbid eating disorders DSM-IV criteria for eating disorders (Bulimia Nervosa, BN, Anorexia, AN) were used. 33 patients had an eating disorder. When compared to patients without ED the patients with ED had a higher prevalence of bipolar disorders. Using strict DSM-IV criteria, this association was only significant for BN (OR) 4.5 (95% CI 1.1-17.6). When using a broader index of bipolarity including patients having affective temperaments, a significant relation was found for BN (OR) 9.1 (95% CI 1.1-73.6), and for patients with a lifetime history of both BN and AN (OR) 8.6 (95% CI 1.1-70.2).We also found patients with ED to have a significantly higher prevalence of affective temperaments, an earlier onset of major affective disorder and to have more depressive episodes. Non-blind evaluation of diagnosis for mood, eating disorders and affective temperaments. In line with previous reports we describe an association between bulimia nervosa and bipolar disorder. Furthermore we report a relationship between lifetime bulimia and anorexia and cyclothymic and related affective temperaments.

Whole-Genome Sequences of DA and F344 Rats with Different Susceptibilities to Arthritis, Autoimmunity, Inflammation and Cancer

PubMed Central

Guo, Xiaosen; Brenner, Max; Zhang, Xuemei; Laragione, Teresina; Tai, Shuaishuai; Li, Yanhong; Bu, Junjie; Yin, Ye; Shah, Anish A.; Kwan, Kevin; Li, Yingrui; Jun, Wang; Gulko, Pércio S.

2013-01-01

DA (D-blood group of Palm and Agouti, also known as Dark Agouti) and F344 (Fischer) are two inbred rat strains with differences in several phenotypes, including susceptibility to autoimmune disease models and inflammatory responses. While these strains have been extensively studied, little information is available about the DA and F344 genomes, as only the Brown Norway (BN) and spontaneously hypertensive rat strains have been sequenced to date. Here we report the sequencing of the DA and F344 genomes using next-generation Illumina paired-end read technology and the first de novo assembly of a rat genome. DA and F344 were sequenced with an average depth of 32-fold, covered 98.9% of the BN reference genome, and included 97.97% of known rat ESTs. New sequences could be assigned to 59 million positions with previously unknown data in the BN reference genome. Differences between DA, F344, and BN included 19 million positions in novel scaffolds, 4.09 million single nucleotide polymorphisms (SNPs) (including 1.37 million new SNPs), 458,224 short insertions and deletions, and 58,174 structural variants. Genetic differences between DA, F344, and BN, including high-impact SNPs and short insertions and deletions affecting >2500 genes, are likely to account for most of the phenotypic variation between these strains. The new DA and F344 genome sequencing data should facilitate gene discovery efforts in rat models of human disease. PMID:23695301

Assessment of liquefaction-induced hazards using Bayesian networks based on standard penetration test data

NASA Astrophysics Data System (ADS)

Tang, Xiao-Wei; Bai, Xu; Hu, Ji-Lei; Qiu, Jiang-Nan

2018-05-01

Liquefaction-induced hazards such as sand boils, ground cracks, settlement, and lateral spreading are responsible for considerable damage to engineering structures during major earthquakes. Presently, there is no effective empirical approach that can assess different liquefaction-induced hazards in one model. This is because of the uncertainties and complexity of the factors related to seismic liquefaction and liquefaction-induced hazards. In this study, Bayesian networks (BNs) are used to integrate multiple factors related to seismic liquefaction, sand boils, ground cracks, settlement, and lateral spreading into a model based on standard penetration test data. The constructed BN model can assess four different liquefaction-induced hazards together. In a case study, the BN method outperforms an artificial neural network and Ishihara and Yoshimine's simplified method in terms of accuracy, Brier score, recall, precision, and area under the curve (AUC) of the receiver operating characteristic (ROC). This demonstrates that the BN method is a good alternative tool for the risk assessment of liquefaction-induced hazards. Furthermore, the performance of the BN model in estimating liquefaction-induced hazards in Japan's 2011 Tōhoku earthquake confirms its correctness and reliability compared with the liquefaction potential index approach. The proposed BN model can also predict whether the soil becomes liquefied after an earthquake and can deduce the chain reaction process of liquefaction-induced hazards and perform backward reasoning. The assessment results from the proposed model provide informative guidelines for decision-makers to detect the damage state of a field following liquefaction.

Whole-genome sequences of DA and F344 rats with different susceptibilities to arthritis, autoimmunity, inflammation and cancer.

PubMed

Guo, Xiaosen; Brenner, Max; Zhang, Xuemei; Laragione, Teresina; Tai, Shuaishuai; Li, Yanhong; Bu, Junjie; Yin, Ye; Shah, Anish A; Kwan, Kevin; Li, Yingrui; Jun, Wang; Gulko, Pércio S

2013-08-01

DA (D-blood group of Palm and Agouti, also known as Dark Agouti) and F344 (Fischer) are two inbred rat strains with differences in several phenotypes, including susceptibility to autoimmune disease models and inflammatory responses. While these strains have been extensively studied, little information is available about the DA and F344 genomes, as only the Brown Norway (BN) and spontaneously hypertensive rat strains have been sequenced to date. Here we report the sequencing of the DA and F344 genomes using next-generation Illumina paired-end read technology and the first de novo assembly of a rat genome. DA and F344 were sequenced with an average depth of 32-fold, covered 98.9% of the BN reference genome, and included 97.97% of known rat ESTs. New sequences could be assigned to 59 million positions with previously unknown data in the BN reference genome. Differences between DA, F344, and BN included 19 million positions in novel scaffolds, 4.09 million single nucleotide polymorphisms (SNPs) (including 1.37 million new SNPs), 458,224 short insertions and deletions, and 58,174 structural variants. Genetic differences between DA, F344, and BN, including high-impact SNPs and short insertions and deletions affecting >2500 genes, are likely to account for most of the phenotypic variation between these strains. The new DA and F344 genome sequencing data should facilitate gene discovery efforts in rat models of human disease.

Electronic properties of T graphene-like C-BN sheets: A density functional theory study

NASA Astrophysics Data System (ADS)

Majidi, R.

2015-11-01

We have used density functional theory to study the electronic properties of T graphene-like C, C-BN and BN sheets. The planar T graphene with metallic property has been considered. The results show that the presence of BN has a considerable effect on the electronic properties of T graphene. The T graphene-like C-BN and BN sheets show semiconducting properties. The energy band gap is increased by enhancing the number of BN units. The possibility of opening and controlling band gap opens the door for T graphene in switchable electronic devices.

Localized emission from laser-irradiated defects in 2D hexagonal boron nitride

NASA Astrophysics Data System (ADS)

Hou, Songyan; Danang Birowosuto, Muhammad; Umar, Saleem; Ange Anicet, Maurice; Yingjie Tay, Roland; Coquet, Philippe; Tay, Beng Kang; Wang, Hong; Teo, Edwin Hang Tong

2018-01-01

Hexagonal boron nitride (hBN) has emerged as a promising two-dimensional (2D) material for photonics device due to its large bandgap and flexibility in nanophotonic circuits. Here, we report bright and localized luminescent centres can be engineered in hBN monolayers and flakes using laser irradiation. The transition from hBN to cBN emerges in laser irradiated hBN large monolayers while is absent in processed hBN flakes. Remarkably, the colour centres in hBN flakes exhibit room temperature cleaner single photon emissions with g 2(0) ranging from 0.20 to 0.42, a narrower line width of 1.4 nm and higher brightness compared with monolayers. Our results pave the way to engineering deterministic defects in hBN induced by laser pulse and show great prospect for application of defects in hBN used as nano-size light source in photonics.

Tribological properties of boron nitride synthesized by ion beam deposition

NASA Technical Reports Server (NTRS)

Miyoshi, K.; Buckley, D. H.; Spalvins, T.

1985-01-01

The adhesion and friction behavior of boron nitride films on 440 C bearing stainless steel substrates was examined. The thin films containing the boron nitride were synthesized using an ion beam extracted from a borazine plasma. Sliding friction experiments were conducted with BN in sliding contact with itself and various transition metals. It is indicated that the surfaces of atomically cleaned BN coating film contain a small amount of oxides and carbides, in addition to boron nitride. The coefficients of friction for the BN in contact with metals are related to the relative chemical activity of the metals. The more active the metal, the higher is the coefficient of friction. The adsorption of oxygen on clean metal and BN increases the shear strength of the metal - BN contact and increases the friction. The friction for BN-BN contact is a function of the shear strength of the elastic contacts. Clean BN surfaces exhibit relatively strong interfacial adhesion and high friction. The presence of adsorbates such as adventitious carbon contaminants on the BN surfaces reduces the shear strength of the contact area. In contrast, chemically adsorbed oxygen enhances the shear strength of the BN-BN contact and increases the friction.

Interhemispheric functional connectivity in anorexia and bulimia nervosa.

PubMed

Canna, Antonietta; Prinster, Anna; Monteleone, Alessio Maria; Cantone, Elena; Monteleone, Palmiero; Volpe, Umberto; Maj, Mario; Di Salle, Francesco; Esposito, Fabrizio

2017-05-01

The functional interplay between hemispheres is fundamental for behavioral, cognitive, and emotional control. Anorexia nervosa (AN) and bulimia nervosa (BN) have been largely studied with brain magnetic resonance imaging (MRI) in relation to the functional mechanisms of high-level processing, but not in terms of possible inter-hemispheric functional connectivity anomalies. Using resting-state functional MRI (fMRI), voxel-mirrored homotopic connectivity (VMHC) and regional inter-hemispheric spectral coherence (IHSC) were studied in 15 AN and 13 BN patients and 16 healthy controls (HC). Using T1-weighted and diffusion tensor imaging MRI scans, regional VMHC values were correlated with the left-right asymmetry of corresponding homotopic gray matter volumes and with the white matter callosal fractional anisotropy (FA). Compared to HC, AN patients exhibited reduced VMHC in cerebellum, insula, and precuneus, while BN patients showed reduced VMHC in dorso-lateral prefrontal and orbito-frontal cortices. The regional IHSC analysis highlighted that the inter-hemispheric functional connectivity was higher in the 'Slow-5' band in all regions except the insula. No group differences in left-right structural asymmetries and in VMHC vs. callosal FA correlations were significant in the comparisons between cohorts. These anomalies, not explained by structural changes, indicate that AN and BN, at least in their acute phase, are associated with a loss of inter-hemispheric connectivity in regions implicated in self-referential, cognitive control and reward processing. These findings may thus gather novel functional markers to explore aberrant features of these eating disorders. © 2016 Federation of European Neuroscience Societies and John Wiley & Sons Ltd.

Synthesis and Characterization of Three Dimensional Nanostructures Based on Interconnected Carbon Nanomaterials

NASA Astrophysics Data System (ADS)

Koizumi, Ryota

This thesis addresses various types of synthetic methods for novel three dimensional nanomaterials and nanostructures based on interconnected carbon nanomaterials using solution chemistry and chemical vapor deposition (CVD) methods. Carbon nanotube (CNT) spheres with porous and scaffold structures consisting of interconnected CNTs were synthesized by solution chemistry followed by freeze-drying, which have high elasticity under nano-indentation tests. This allows the CNT spheres to be potentially applied to mechanical dampers. CNTs were also grown on two dimensional materials--such as reduced graphene oxide (rGO) and hexagonal boron nitride (h-BN)--by CVD methods, which are chemically interconnected. CNTs on rGO and h-BN interconnected structures performed well as electrodes for supercapacitors. Furthermore, unique interconnected flake structures of alpha-phase molybdenum carbide were developed by a CVD method. The molybdenum carbide can be used for a catalyst of hydrogen evolution reaction activity as well as an electrode for supercapacitors.

Theoretical study of porous surfaces derived from graphene and boron nitride

NASA Astrophysics Data System (ADS)

Fabris, G. S. L.; Marana, N. L.; Longo, E.; Sambrano, J. R.

2018-02-01

Porous graphene (PG), graphenylene (GP), inorganic graphenylene (IGP-BN), and porous boron nitride (PBN) single-layer have been studied via periodic density functional theory with a modified B3LYP functional and an all-electron Gaussian basis set. The structural, elastic, electronic, vibrational, and topological properties of the surfaces were investigated. The analysis showed that all porous structures had a nonzero band gap, and only PG exhibited a non-planar shape. All porous structures seem to be more susceptible to longitudinal deformation than their pristine counterparts, and GP exhibits a higher strength than graphene in the transversal direction. In addition, the electron densities of GP and IGP-BN are localized closer to the atoms, in contrast with PG and PBN, whose charge density is shifted towards the pore center; this property could find application in various fields, such as gas adsorption.

Preparation and characterization of boron nitride coatings on carbon fibers from borazine by chemical vapor deposition

NASA Astrophysics Data System (ADS)

Li, Jun-Sheng; Zhang, Chang-Rui; Li, Bin

2011-06-01

Boron nitride (BN) coatings were deposited on carbon fibers by chemical vapor deposition (CVD) using borazine as single source precursor. The deposited coatings were characterized by scanning electron microscopy (SEM), Auger electron spectroscopy (AES), X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR) and Raman spectroscopy. The effect of temperatures on growth kinetics, morphology, composition and structure of the coatings was investigated. In the low temperature range of 900 °C-1000 °C, the growth rate increased with increasing temperature complying with Arrhenius law, and an apparent active energy of 72 kJ/mol was calculated. The coating surface was smooth and compact, and the coatings uniformly deposited on individual fibers of carbon fiber bundles. The growth was controlled by surface reaction. At 1000 °C, the deposition rate reached a maximum (2.5 μm/h). At the same time, the limiting step of the growth translated to be mass-transportation. Above 1100 °C, the growth rate decreased drastically due to the occurrence of gas-phase nucleation. Moreover, the coating surface became loose and rough. Composition and structure examinations revealed that stoichiometric BN coatings with turbostratic structure were obtained below 1000 °C, while hexagonal BN coatings were deposited above 1100 °C. A penetration of carbon element from the fibers to the coatings was observed.

Elevated total plasma-adiponectin is stable over time in young women with bulimia nervosa.

PubMed

Syk, M; Ramklint, M; Fredriksson, R; Ekselius, L; Cunningham, J L

2017-03-01

Bulimia nervosa (BN) is characterized by dysregulated eating behaviour and present data suggest adipokines may regulate food intake. We investigated a possible association between BN and adipokine levels and hypothesized that plasma (P)-adiponectin would be elevated and P-leptin and P-leptin-adiponectin-ratio would be reduced in women with BN. The study was designed as a cross-sectional study with a longitudinal arm for patients with BN. Plasma-adiponectin and leptin was measured in 148 female patients seeking psychiatric ambulatory care and 45 female controls. Fifteen patients were diagnosed with BN and the remaining with other affective and anxiety disorders. P-adiponectin and P-leptin levels were compared between patients with BN, patients without BN and controls. At follow-up 1-2years later, adipokines were reassessed in patients with BN and the Eating Disorder Examination Questionnaire was used to assess symptom severity. P-adiponectin was elevated in patients with BN at baseline and at follow-up when compared to patients without BN and controls (P<0.004 and <0.008 respectively). The difference remained significant after controlling for body mass index. P-adiponectin was correlated to symptom severity at follow-up in patients with BN without morbid obesity (ρ=0.72, P<0.04). P-leptin-adiponectin-ratio was significantly lower in patients with BN compared to controls (P<0.04) and P-leptin non-significantly lower. Findings indicate a stable elevation of P-adiponectin in women with BN. P-adiponectin at follow-up correlates to eating disorder symptom severity in patients without morbid obesity, indicating that P-adiponectin should be further investigated as a possible potential prognostic biomarker for BN. Copyright © 2016 Elsevier Masson SAS. All rights reserved.

Depressed expression of FAE1 and FAD2 genes modifies fatty acid profiles and storage compounds accumulation in Brassica napus seeds.

PubMed

Shi, Jianghua; Lang, Chunxiu; Wang, Fulin; Wu, Xuelong; Liu, Renhu; Zheng, Tao; Zhang, Dongqing; Chen, Jinqing; Wu, Guanting

2017-10-01

In plants, the enzymes fatty acid dehydrogenase 2 (FAD2) and fatty acid elongase 1 (FAE1) have been shown in previous studies to play important roles in the de novo biosynthesis of fatty acids. However, the effects of depressed expression of FAD2 and FAE1 on seed storage compounds accumulation remains to be elucidated. In this study, we produced RNA interfering transgenic rapeseeds lines, BnFAD2-Ri, BnFAE1-Ri and BnFAD2/BnFAE1-Ri, which exhibited depressed expression of the BnFAD2 and BnFAE1 genes under the control of seed-specific napin A promoter. These transgenic rapeseeds showed normal growth and development as compared with the wild type (CY2). Depressed expression of BnFAD2 and BnFAE1 genes modified fatty acid profiles, leading to increased oleic acid and decreased erucic acid contents in transgenic seeds. Consistent with these results, the ratios of C18:1/C18:2 and C18:1/C18:3 in C18 unsaturated fatty acids were greatly increased due to increased oleic acid content in transgenic seeds. Moreover, depressed expression of BnFAD2 and BnFAE1 genes resulted in slightly decreased oil contents and increased protein contents in transgenic seeds. Our results demonstrated that depressed expression of BnFAD2 and BnFAE1 greatly improves seed nutritional quality by modulating the fatty acid metabolism and storage products accumulation and that BnFAD2 and BnFAE1 are reliable targets for genetic improvement of rapeseed in seed nutritional quality. Copyright © 2017 Elsevier B.V. All rights reserved.

Boron nitride composites

DOEpatents

Kuntz, Joshua D.; Ellsworth, German F.; Swenson, Fritz J.; Allen, Patrick G.

2016-02-16

According to one embodiment, a composite product includes hexagonal boron nitride (hBN), and a plurality of cubic boron nitride (cBN) particles, wherein the plurality of cBN particles are dispersed in a matrix of the hBN. According to another embodiment, a composite product includes a plurality of cBN particles, and one or more borate-containing binders.

Nanostructured BN-Mg composites: features of interface bonding and mechanical properties.

PubMed

Kvashnin, Dmitry G; Krasheninnikov, Arkady V; Shtansky, Dmitry; Sorokin, Pavel B; Golberg, Dmitri

2016-01-14

Magnesium (Mg) is one of the lightest industrially used metals. However, wide applications of Mg-based components require a substantial enhancement of their mechanical characteristics. This can be achieved by introducing small particles or fibers into the metal matrix. Using first-principles calculations, we investigate the stability and mechanical properties of a nanocomposite made of magnesium reinforced with boron nitride (BN) nanostructures (BN nanotubes and BN monolayers). We show that boron vacancies at the BN/Mg interface lead to a substantial increase in BN/Mg bonding establishing an efficient route towards the development of BN/Mg composite materials with enhanced mechanical properties.

Raman spectroscopy and time-resolved photoluminescence of BN and BxCyNz nanotubes

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wu, J.; Han, Wei-Qiang; Walukiewicz, W.

2004-01-21

We report Raman and time-resolved photoluminescence spectroscopic studies of multiwalled BN and B{sub x}C{sub y}N{sub z} nanotubes. The Raman spectroscopy shows that the as-grown B{sub x}C{sub y}N{sub z} charge recombination, respectively. Comparison of the photoluminescence of BN nanotubes to that decay process is characterized by two time constants that are attributed to intra- and inter-BN sheet nanotubes as predicted by theory. nanotubes are radially phase separated into BN shells and carbon shells. The photoluminescence of hexagonal BN is consistent with the existence of a spatially indirect band gap in multi-walled BN.

(Fuzzy) Ideals of BN-Algebras

PubMed Central

Walendziak, Andrzej

2015-01-01

The notions of an ideal and a fuzzy ideal in BN-algebras are introduced. The properties and characterizations of them are investigated. The concepts of normal ideals and normal congruences of a BN-algebra are also studied, the properties of them are displayed, and a one-to-one correspondence between them is presented. Conditions for a fuzzy set to be a fuzzy ideal are given. The relationships between ideals and fuzzy ideals of a BN-algebra are established. The homomorphic properties of fuzzy ideals of a BN-algebra are provided. Finally, characterizations of Noetherian BN-algebras and Artinian BN-algebras via fuzzy ideals are obtained. PMID:26125050

The Evolution of "Enhanced" Cognitive Behavior Therapy for Eating Disorders: Learning from Treatment Nonresponse

ERIC Educational Resources Information Center

Cooper, Zafra; Fairburn, Christopher G.

2011-01-01

In recent years there has been widespread acceptance that cognitive behavior therapy (CBT) is the treatment of choice for bulimia nervosa. The cognitive behavioral treatment of bulimia nervosa (CBT-BN) was first described in 1981. Over the past decades the theory and treatment have evolved in response to a variety of challenges. The treatment has…

Genome-Wide Analysis of the PYL Gene Family and Identification of PYL Genes That Respond to Abiotic Stress in Brassica napus

PubMed Central

Di, Feifei; Jian, Hongju; Wang, Tengyue; Chen, Xueping; Ding, Yiran; Du, Hai; Li, Jiana; Liu, Liezhao

2018-01-01

Abscisic acid (ABA) is an endogenous phytohormone that plays important roles in the regulation of plant growth, development, and stress responses. The pyrabactin resistance 1-like (PYR/PYL) protein is a core regulatory component of ABA signaling networks in plants. However, no details regarding this family in Brassica napus are available. Here, 46 PYLs were identified in the B. napus genome. Based on phylogenetic analysis, BnPYR1 and BnPYL1-3 belong to subfamily I, BnPYL7-10 belong to subfamily II, and BnPYL4-6 and BnPYL11-13 belong to subfamily III. Analysis of BnPYL conserved motifs showed that every subfamily contained four common motifs. By predicting cis-elements in the promoters, we found that all BnPYL members contained hormone- and stress-related elements and that expression levels of most BnPYLs were relatively higher in seeds at the germination stage than those in other organs or at other developmental stages. Gene Ontology (GO) enrichment showed that BnPYL genes mainly participate in responses to stimuli. To identify crucial PYLs mediating the response to abiotic stress in B. napus, expression changes in 14 BnPYL genes were determined by quantitative real-time RT-PCR after drought, heat, and salinity treatments, and identified BnPYR1-3, BnPYL1-2, and BnPYL7-2 in respond to abiotic stresses. The findings of this study lay a foundation for further investigations of PYL genes in B. napus. PMID:29534558

Influence of hydrogen on the structure and stability of ultra-thin ZnO on metal substrates

DOE Office of Scientific and Technical Information (OSTI.GOV)

Bieniek, Bjoern; Hofmann, Oliver T.; Institut für Festkörperphysik, TU Graz, 8010 Graz

2015-03-30

We investigate the atomic and electronic structure of ultra-thin ZnO films (1 to 4 layers) on the (111) surfaces of Ag, Cu, Pd, Pt, Ni, and Rh by means of density-functional theory. The ZnO monolayer is found to adopt an α-BN structure on the metal substrates with coincidence structures in good agreement with experiment. Thicker ZnO layers change into a wurtzite structure. The films exhibit a strong corrugation, which can be smoothed by hydrogen (H) adsorption. An H over-layer with 50% coverage is formed at chemical potentials that range from low to ultra-high vacuum H{sub 2} pressures. For the Agmore » substrate, both α-BN and wurtzite ZnO films are accessible in this pressure range, while for Cu, Pd, Pt, Rh, and Ni wurtzite films are favored. The surface structure and the density of states of these H passivated ZnO thin films agree well with those of the bulk ZnO(0001{sup ¯})-2×1-H surface.« less

Bulimia nervosa in overweight and normal-weight women.

PubMed

Masheb, Robin; White, Marney A

2012-02-01

The aim of the present study was to examine overweight bulimia nervosa (BN) in a community sample of women. Volunteers (n = 1964) completed self-report questionnaires of weight, binge eating, purging, and cognitive features. Participants were classified as overweight (body mass index ≥25) or normal weight (body mass index <25). Rates of BN within the overweight and normal-weight classes did not differ (6.4% vs 7.9%). Of the 131 participants identified as BN, 64% (n = 84) were classified as overweight BN and 36% (n = 47) as normal-weight BN. The overweight BN group had a greater proportion of ethnic minorities and reported significantly less restraint than the normal-weight BN group. Otherwise, the 2 groups reported similarly, even in terms of purging and depression. In summary, rates of BN did not differ between overweight and normal-weight women. Among BN participants, the majority (two thirds) were overweight. Differences in ethnicity and restraint, but little else, were found between overweight and normal-weight BN. Findings from the present study should serve to increase awareness of the weight range and ethnic diversity of BN, and highlight the need to address weight and cultural sensitivity in the identification and treatment of eating disorders. Copyright © 2012 Elsevier Inc. All rights reserved.

Fracture toughness and sliding properties of magnetron sputtered CrBC and CrBCN coatings

NASA Astrophysics Data System (ADS)

Wang, Qianzhi; Zhou, Fei; Ma, Qiang; Callisti, Mauro; Polcar, Tomas; Yan, Jiwang

2018-06-01

CrBC and CrBCN coatings with low and high B contents were deposited on 316L steel and Si wafers using an unbalanced magnetron sputtering system. Mechanical properties including hardness (H), elastic modulus (E) and fracture toughness (KIc) as well as residual stresses (σ) were quantified. A clear correlation between structural, mechanical and tribological properties of coatings was found. In particular, structural analyses indicated that N incorporation in CrBC coatings with high B content caused a significant structural evolution of the nanocomposite structure (crystalline grains embedded into an amorphous matrix) from nc-CrB2/(a-CrBx, a-BCx) to nc-CrN/(a-BCx, a-BN). As a result, the hardness of CrBC coating with high B content decreased from 23.4 to 16.3 GPa but the fracture toughness was enhanced. Consequently, less cracks initiated on CrBCN coatings during tribological tests, which combined with the shielding effect of a-BN on wear debris, led to a low friction coefficient and wear rate.

Structural Constraints of Vaccine-Induced Tier-2 Autologous HIV Neutralizing Antibodies Targeting the Receptor-Binding Site.

PubMed

Bradley, Todd; Fera, Daniela; Bhiman, Jinal; Eslamizar, Leila; Lu, Xiaozhi; Anasti, Kara; Zhang, Ruijung; Sutherland, Laura L; Scearce, Richard M; Bowman, Cindy M; Stolarchuk, Christina; Lloyd, Krissey E; Parks, Robert; Eaton, Amanda; Foulger, Andrew; Nie, Xiaoyan; Karim, Salim S Abdool; Barnett, Susan; Kelsoe, Garnett; Kepler, Thomas B; Alam, S Munir; Montefiori, David C; Moody, M Anthony; Liao, Hua-Xin; Morris, Lynn; Santra, Sampa; Harrison, Stephen C; Haynes, Barton F

2016-01-05

Antibodies that neutralize autologous transmitted/founder (TF) HIV occur in most HIV-infected individuals and can evolve to neutralization breadth. Autologous neutralizing antibodies (nAbs) against neutralization-resistant (Tier-2) viruses are rarely induced by vaccination. Whereas broadly neutralizing antibody (bnAb)-HIV-Envelope structures have been defined, the structures of autologous nAbs have not. Here, we show that immunization with TF mutant Envs gp140 oligomers induced high-titer, V5-dependent plasma neutralization for a Tier-2 autologous TF evolved mutant virus. Structural analysis of autologous nAb DH427 revealed binding to V5, demonstrating the source of narrow nAb specificity and explaining the failure to acquire breadth. Thus, oligomeric TF Envs can elicit autologous nAbs to Tier-2 HIVs, but induction of bnAbs will require targeting of precursors of B cell lineages that can mature to heterologous neutralization. Copyright © 2016 The Authors. Published by Elsevier Inc. All rights reserved.

Most effective way to improve the hydrogen storage abilities of Na-decorated BN sheets: applying external biaxial strain and an electric field.

PubMed

Tang, Chunmei; Zhang, Xue; Zhou, Xiaofeng

2017-02-15

Density functional calculations were used to investigate the hydrogen storage abilities of Na-atoms-decorated BN sheets under both external biaxial strain and a vertical electric field. The Na atom generally has the weakest binding strength to a given substrate compared with the other elements in the periodic table [PANS, 2016, 113, 3735]. Consequently, it is understudied in comparison to other elements and there are few reports about the hydrogen storage abilities of Na-decorated nanomaterials. We calculated that the average binding energy (E b ) of Na atoms to the pure BN sheet is 1.08 eV, which is smaller than the cohesive energy of bulk Na (1.11 eV). However, the E b can be increased to 1.15 eV under 15% biaxial strain, and further up to 1.53 eV with the control of both 15% biaxial strain and a 5.14 V nm -1 electric field (E-field). Therefore, the application of biaxial strain and an external upward E-field can prevent clustering of the Na atoms on the surface of a BN sheet, which is crucial for the hydrogen storage. Each Na atom on the surface of a BN sheet can adsorb only one H 2 molecule when no strain or E-field is applied; however, the absorption increases to five H 2 molecules under 15% biaxial strain and six H 2 molecules under both 15% biaxial strain combined with a 5.14 V nm -1 E-field. The average adsorption energies for H 2 of BN-(Na-mH 2 ) (m = 1-6) are within the range of practical applications (0.2-0.6 eV). The hydrogen gravimetric density of the periodic BN-(Na-6H 2 ) 4 structure is 9 wt%, which exceeds the 5.5 wt% value that should be met by 2017 as specified by the US Department of Energy. On the other side, removal of the biaxial strain and E-field can help to desorb the H 2 molecule. These findings suggest a new route to design hydrogen storage materials under near-ambient conditions.

Measurement of the Elastic Modulus of a Single Boron Nitride Nanotube

NASA Astrophysics Data System (ADS)

Chopra, Nasreen G.; Cohen, Marvin L.; Louie, Steven G.; Zettl, A.

1997-03-01

In situ transmission electron microscope (TEM) measurements of thermally-excited vibrational characteristics of boron nitride (BN) nanotubes are used to extract the elastic modulus. We find BN nanotubes to have a higher axial Young's modulus, 1.2 TPa, than any other insulating fiber. This value is consistent with theoretical predictions and confirms previous TEM observations of the high degree of crystallinity of these structures. This work was supported by the U. S. Department of Energy under contract No. DE-AC03-76-SF00098 and the Office of Naval Research, Order No. N00014-95-F-0099

Hole polarons and p -type doping in boron nitride polymorphs

NASA Astrophysics Data System (ADS)

Weston, L.; Wickramaratne, D.; Van de Walle, C. G.

2017-09-01

Boron nitride polymorphs hold great promise for integration into electronic and optoelectronic devices requiring ultrawide band gaps. We use first-principles calculations to examine the prospects for p -type doping of hexagonal (h -BN ), wurtzite (w z -BN ), and cubic (c -BN ) boron nitride. Group-IV elements (C, Si) substituting on the N site result in a deep acceptor, as the atomic levels of the impurity species lie above the BN valence-band maximum. On the other hand, group-II elements (Be, Mg) substituting on the B site do not give impurity states in the band gap; however, these dopants lead to the formation of small hole polarons. The tendency for polaron formation is far more pronounced in h -BN compared to w z -BN or c -BN . Despite forming small hole polarons, Be acceptors enable p -type doping, with ionization energies of 0.31 eV for w z -BN and 0.24 eV for c -BN ; these values are comparable to the Mg ionization energy in GaN.

Magnetic tunnel junctions with monolayer hexagonal boron nitride tunnel barriers

DOE Office of Scientific and Technical Information (OSTI.GOV)

Piquemal-Banci, M.; Galceran, R.; Bouzehouane, K.

We report on the integration of atomically thin 2D insulating hexagonal boron nitride (h-BN) tunnel barriers into Co/h-BN/Fe magnetic tunnel junctions (MTJs). The h-BN monolayer is directly grown by chemical vapor deposition on Fe. The Conductive Tip Atomic Force Microscopy (CT-AFM) measurements reveal the homogeneity of the tunnel behavior of our h-BN layers. As expected for tunneling, the resistance depends exponentially on the number of h-BN layers. The h-BN monolayer properties are also characterized through integration into complete MTJ devices. A Tunnel Magnetoresistance of up to 6% is observed for a MTJ based on a single atomically thin h-BN layer.

Bayesian network prior: network analysis of biological data using external knowledge

PubMed Central

Isci, Senol; Dogan, Haluk; Ozturk, Cengizhan; Otu, Hasan H.

2014-01-01

Motivation: Reverse engineering GI networks from experimental data is a challenging task due to the complex nature of the networks and the noise inherent in the data. One way to overcome these hurdles would be incorporating the vast amounts of external biological knowledge when building interaction networks. We propose a framework where GI networks are learned from experimental data using Bayesian networks (BNs) and the incorporation of external knowledge is also done via a BN that we call Bayesian Network Prior (BNP). BNP depicts the relation between various evidence types that contribute to the event ‘gene interaction’ and is used to calculate the probability of a candidate graph (G) in the structure learning process. Results: Our simulation results on synthetic, simulated and real biological data show that the proposed approach can identify the underlying interaction network with high accuracy even when the prior information is distorted and outperforms existing methods. Availability: Accompanying BNP software package is freely available for academic use at http://bioe.bilgi.edu.tr/BNP. Contact: hasan.otu@bilgi.edu.tr Supplementary Information: Supplementary data are available at Bioinformatics online. PMID:24215027

Staged induction of HIV-1 glycan–dependent broadly neutralizing antibodies

DOE PAGES

Bonsignori, Mattia; Kreider, Edward F.; Fera, Daniela; ...

2017-03-15

A preventive HIV-1 vaccine should induce HIV-1–specific broadly neutralizing antibodies (bnAbs). However, bnAbs generally require high levels of somatic hypermutation (SHM) to acquire breadth, and current vaccine strategies have not been successful in inducing bnAbs. Because bnAbs directed against a glycosylated site adjacent to the third variable loop (V3) of the HIV-1 envelope protein require limited SHM, the V3-glycan epitope is an attractive vaccine target. By studying the cooperation among multiple V3-glycan B cell lineages and their coevolution with autologous virus throughout 5 years of infection, we identify key events in the ontogeny of a V3- glycan bnAb. Two autologousmore » neutralizing antibody lineages selected for virus escape mutations and consequently allowed initiation and affinity maturation of a V3-glycan bnAb lineage. The nucleotide substitution required to initiate the bnAb lineage occurred at a low-probability site for activation-induced cytidine deaminase activity. Cooperation of B cell lineages and an improbable mutation critical for bnAb activity defined the necessary events leading to breadth in this V3- glycan bnAb lineage. These findings may, in part, explain why initiation of V3-glycan bnAbs is rare, and suggest an immunization strategy for inducing similar V3-glycan bnAbs.« less

The Core Symptoms of Bulimia Nervosa, Anxiety, and Depression: A Network Analysis

PubMed Central

Levinson, Cheri A.; Zerwas, Stephanie; Calebs, Benjamin; Forbush, Kelsie; Kordy, Hans; Watson, Hunna; Hofmeier, Sara; Levine, Michele; Crosby, Ross D.; Peat, Christine; Runfola, Cristin D.; Zimmer, Benjamin; Moesner, Markus; Marcus, Marsha D.; Bulik, Cynthia M.

2017-01-01

Bulimia nervosa (BN) is characterized by symptoms of binge eating and compensatory behavior, and overevaluation of weight and shape, which often co-occur with symptoms of anxiety and depression. However, there is little research identifying which specific BN symptoms maintain BN psychopathology and how they are associated with symptoms of depression and anxiety. Network analyses represent an emerging method in psychopathology research to examine how symptoms interact and may become self-reinforcing. In the current study of adults with a DSM-IV diagnosis of BN (N = 196), we used network analysis to identify the central symptoms of BN, as well as symptoms that may bridge the association between BN symptoms and anxiety and depression symptoms. Results showed that fear of weight gain was central to BN psychopathology, whereas binge eating, purging, and restriction were less central in the symptom network. Symptoms related to sensitivity to physical sensations (e.g., changes in appetite, feeling dizzy, wobbly) were identified as bridge symptoms between BN, and anxiety and depressive symptoms. We discuss our findings with respect to cognitive-behavioral treatment approaches for BN. These findings suggest that treatments for BN should focus on fear of weight gain, perhaps through exposure therapies. Further, interventions focusing on exposure to physical sensations may also address BN psychopathology, as well as co-occurring anxiety and depressive symptoms. PMID:28277735

Differences and similarities between bulimia nervosa, compulsive buying and gambling disorder.

PubMed

Jiménez-Murcia, Susana; Granero, Roser; Moragas, Laura; Steiger, Howard; Israel, Mimi; Aymamí, Neus; Gómez-Peña, Mónica; Sauchelli, Sarah; Agüera, Zaida; Sánchez, Isabel; Riesco, Nadine; Penelo, Eva; Menchón, José M; Fernández-Aranda, Fernando

2015-03-01

The objective of the study was to analyse shared commonalities and differences between bulimia nervosa (BN) and certain impulse-related disorders, namely compulsive buying (CB) and gambling disorder (GD), with respect to general psychopathology and personality traits. A total of 188 female patients [50 BN without comorbid CB (BN-CB), 49 BN with comorbid CB (BN+CB), 53 GD and 36 CB] and 50 comparison non-psychiatric women participated in the current study. All patients were diagnosed using the Diagnostic and Statistical Manual of Mental Disorders, Fourth revised edition, the Temperament and Character Inventory-Revised, and other clinical indices. A positive-growing trend was observed in psychopathology and personality traits across the four clinical groups. Comorbid BN with CB was associated with highest eating psychopathology and social anxiety. On Novelty Seeking, the CB, GD and BN+CB were similar to each other, whereas BN-CB presented a distinct profile. Moreover, the BN+CB group displayed more dysfunctional personality traits and higher general psychopathology. The clinical groups demonstrated overall higher levels of psychopathology compared with the control group. The results of this study demonstrate that disorders with impulsive traits (CB, GD, BN+CB and BN-CB) follow a linear trend in general psychopathology and specific personality traits, but differ along specific personality and psychopathological dimensions. Copyright © 2014 John Wiley & Sons, Ltd and Eating Disorders Association.

Staged induction of HIV-1 glycan–dependent broadly neutralizing antibodies

DOE Office of Scientific and Technical Information (OSTI.GOV)

Bonsignori, Mattia; Kreider, Edward F.; Fera, Daniela

A preventive HIV-1 vaccine should induce HIV-1–specific broadly neutralizing antibodies (bnAbs). However, bnAbs generally require high levels of somatic hypermutation (SHM) to acquire breadth, and current vaccine strategies have not been successful in inducing bnAbs. Because bnAbs directed against a glycosylated site adjacent to the third variable loop (V3) of the HIV-1 envelope protein require limited SHM, the V3-glycan epitope is an attractive vaccine target. By studying the cooperation among multiple V3-glycan B cell lineages and their coevolution with autologous virus throughout 5 years of infection, we identify key events in the ontogeny of a V3- glycan bnAb. Two autologousmore » neutralizing antibody lineages selected for virus escape mutations and consequently allowed initiation and affinity maturation of a V3-glycan bnAb lineage. The nucleotide substitution required to initiate the bnAb lineage occurred at a low-probability site for activation-induced cytidine deaminase activity. Cooperation of B cell lineages and an improbable mutation critical for bnAb activity defined the necessary events leading to breadth in this V3- glycan bnAb lineage. These findings may, in part, explain why initiation of V3-glycan bnAbs is rare, and suggest an immunization strategy for inducing similar V3-glycan bnAbs.« less

Interpreting genetics in the context of eating disorders: Evidence of disease, not diversity

PubMed Central

Easter, Michele

2013-01-01

How is genetic involvement interpreted for disorders whose medicalisation is contested? Framing psychiatric and behavioral disorders in terms of genetics is expected to make them seem “more medical.” Yet, genetic etiology can also be used to frame behavior as acceptable human variation, rather than a medical problem (e.g., sexual orientation). I analyze responses to the idea of a genetic component in anorexia and bulimia nervosa (AN/BN) via semi-structured interviews with a sample of 50 women diagnosed with an eating disorder (25 recovered). All but three volunteered that genetics would medicalise AN/BN, by (1) making eating disorders seem more like “real” diseases; (2) implying a need for professional treatment; or (3) for biologically-based treatment. Results also indicate several “counter-logics,” by which genetic framing could support non-medical definitions of AN/BN. I argue that genetic framing reduces perceived individual responsibility, which can support definitions of behavior as either a reflection of disease (which entails intervention) or a reflection of normal human diversity (which does not). In the context of public skepticism as to the “reality” of AN/BN, genetic involvement was taken as evidence of disease in ongoing negotiations about the medical and moral status of people with eating disorders. PMID:24286479

Oxidation of SiC/BN/SiC Composites in Reduced Oxygen Partial Pressures

NASA Technical Reports Server (NTRS)

Opila, Elizabeth J.; Boyd, Meredith

2010-01-01

SiC fiber-reinforced SiC composites with a BN interphase are proposed for use as leading edge structures of hypersonic vehicles. The durability of these materials under hypersonic flight conditions is therefore of interest. Thermogravimetric analysis was used to characterize the oxidation kinetics of both the constituent fibers and composite coupons at four temperatures: 816, 1149, 1343, and 1538 C (1500, 2100, 2450, and 2800 F) and in oxygen partial pressures between 5% and 0.1% (balance argon) at 1 atm total pressure. One edge of the coupons was ground off so the effects of oxygen ingress into the composite could be monitored by post-test SEM and EDS. Additional characterization of the oxidation products was conducted by XPS and TOF-SIMS. Under most conditions, the BN oxidized rapidly, leading to the formation of borosilicate glass. Rapid initial oxidation followed by volatilization of boria lead to protective oxide formation and further oxidation was slow. At 1538C in 5% oxygen, both the fibers and coupons exhibited borosilicate glass formation and bubbling. At 1538C in 0.1% oxygen, active oxidation of both the fibers and the composites was observed leading to rapid SiC degradation. BN oxidation at 1538C in 0.1% oxygen was not significant.

Adsorption of various types of amino acids on the graphene and boron-nitride nano-sheet, a DFT-D3 study

NASA Astrophysics Data System (ADS)

Zhiani, Rahele

2017-07-01

The binding properties of the adsorption of five different classes of amino acids, namely, alanine (Ala), arginine (Arg), asparagine (Asn), histidine (His) and cysteine (Cys) on the surface of the graphene (Gra) and the born-nitride (BN) nano-sheet structures were studied from molecular viewpoint using quantum mechanics methods. Density functional theory (DFT) and DFT-D3 calculations were carried out to investigate the electronic properties and the dispersion interaction of the amino acid/adsorbent complexes. Several parameters affecting the interactions between the amino acids and the adsorbent surfaces such as solvent effect, adsorption energy and separation distance were investigated. Findings show that Arg forms the most stable complexes with the graphene and the BN nano-sheet compare to the other amino acids used in this study. The observed frequency results which were related to the band gap energies were consistent with the above statement. Results exhibit that adsorption of the amino acids on the surface of the BN nano-sheet and the graphene accompanied with the release of the energy. Calculations show that there are no bonded interactions between the amino acids and adsorbent surfaces. The polarity of the BN nano-sheet provides the more affinity towards the amino acids. These results were proved by the quantum chemistry studies.

Stability and electronic properties of Gex(BN)y monolayers

NASA Astrophysics Data System (ADS)

Freitas, A.; Machado, L. D.; Tromer, R. M.; Bezerra, C. G.; Azevedo, S.

2017-10-01

In this work, we employ ab initio simulations to propose a new class of monolayers with stoichiometry Gex(BN)y . These monolayers belong to a family of 2D materials combining B, N and group IV atoms, such as BxCyNz and SixByNz . We calculated the formation energy for ten atomic arrangements, and found that it increases when the number of Bsbnd Ge and Nsbnd Ge bonds increases, and decreases when the number of Bsbnd N and Gesbnd Ge bonds increases. We found that the lowest energy monolayer presented a Ge2 BN stoichiometry, and maximized the number of Bsbnd N and Gesbnd Ge bonds. This structure also presented mixed sp2 and sp3 bonds and out-of-plane buckling. Moreover, it remained stable in our ab initio molecular dynamics simulations carried out at T = 300 K. The calculated electronic properties revealed that Gex(BN)y monolayers might present conductor or semiconductor behavior, with band gaps ranging from 0.0 to 0.74 eV, depending on atomic arrangement. Tunable values of band gap can be useful in applications. In optoelectronics, for instance, this property might be employed to control absorbed light wavelengths. Our calculations add a new class of monolayers to the increasing library of 2D materials.

Eating disorder symptoms and comorbid psychopathology among male and female veterans.

PubMed

Litwack, Scott D; Mitchell, Karen S; Sloan, Denise M; Reardon, Annemarie F; Miller, Mark W

2014-01-01

Eating disorder (ED) symptoms have gone mostly unexamined among veterans. The current study assessed rates of bulimia nervosa (BN) and binge eating disorder (BED) symptoms and diagnoses and their associations with common comorbidities among male and female veterans. Participants were US military veterans who screened positive for trauma histories and/or a probable Diagnostic and Statistical Manual of Mental Disorders 4th Edition (DSM-IV) posttraumatic stress disorder (PTSD) diagnosis (n=499). Symptoms of PTSD were assessed using the Clinician-Administered PTSD Scale, and symptoms of EDs, mood, and substance use disorders were assessed using the Structured Clinical Interview for the DSM-IV. Lifetime rates of BN and BED diagnoses were comparable to civilian populations, and a considerable range of lifetime and current BN and BED symptoms were identified. In multivariate models, PTSD and depression severity were most consistently associated with BN and BED symptom severity, with depression most strongly associated with EDs for women. Findings highlight the importance of screening for ED symptoms among male and female veterans, particularly those that present with PTSD and depression symptomatology. Future examinations of the temporal order of such relationships and the degree to which ED symptoms and associated symptoms impact veteran functioning are warranted. Published by Elsevier Inc.

Evolution of structural features and mechanical properties during the conversion of poly[(methylamino)borazine] fibers into boron nitride fibers

NASA Astrophysics Data System (ADS)

Bernard, Samuel; Ayadi, Khaled; Berthet, Marie-Paule; Chassagneux, Fernand; Cornu, David; Letoffe, Jean-Marie; Miele, Philippe

2004-06-01

Poly[(methylamino)borazine] (PolyMAB) green fibers of a mean diameter of 15 μm have been pyrolyzed under ammonia up to 1000°C and heat treated under nitrogen up to 2000°C to prepare boron nitride (BN) fibers. During the polymer-to-ceramic conversion, the mechanical properties of the green fibers increase within the 25-400°C temperature range owing to the formation of a preceramic material and remain almost constant up to 1000°C. Both the crystallinity and the mechanical properties slightly increase within the 1000-1400°C range, in association with the consolidation of the fused-B 3N 3 basal planes. A rapid increase in tensile strength ( σR) and elastic modulus (Young's modulus E) is observed in relation with crystallization of the BN phase for fibers treated between 1400°C and 1800°C. At 2000°C, "meso-hexagonal" BN fibers of 7.5 μm in diameter are finally obtained, displaying values of σR=1.480 GPa and E=365 GPa. The obtention of both high mechanical properties and fine diameter for the as-prepared BN fibers is a consequence of the stretching of the green fibers on a spool which is used during their conversion into ceramic.

Patterns of expressed emotion in adolescent eating disorders.

PubMed

Rienecke, Renee D; Sim, Leslie; Lock, James; Le Grange, Daniel

2016-12-01

This goal of this study was to understand the patterns of expressed emotions (EEs) in adolescent eating disorders. As such, this study compared EE among families of adolescents with anorexia nervosa (AN), bulimia nervosa (BN), and a psychiatric control group, major depressive disorder (MDD). This study also examined the influence of family status (intact vs. nonintact) and the presence of siblings on EE. Two-hundred and fifteen adolescents (ages 12-19) and their families were recruited for this study including 121 adolescents with AN, 54 adolescents with BN, and 40 adolescents with MDD. Adolescents with at least one parent completed the Standardized Clinical Family Interview. Adolescents completed structured diagnostic interviews to assess eligibility for the study, as well as a standardized questionnaire to assess depression. Analyses revealed that fathers showed higher levels of critical comments to adolescents with BN or MDD than those with AN, whereas mothers made more critical comments toward patients with BN. Mothers made the least number of positive remarks toward patients with MDD. In terms of the influence of family status, fathers from intact families showed more expressions of warmth and were less critical than fathers from nonintact families, whereas mothers from intact families were less critical but also made fewer positive remarks than mothers from nonintact families. The presence of siblings appeared to reduce mothers' expression of warmth and emotional overinvolvement. Unique patterns of EE were found to characterize AN, BN, and MDD. Family status and the presence of siblings exert an influence on EE that should be taken into consideration in future research. © 2016 Association for Child and Adolescent Mental Health.

Evidence for disks at an early stage in class 0 protostars?

NASA Astrophysics Data System (ADS)

Gerin, M.; Pety, J.; Commerçon, B.; Fuente, A.; Cernicharo, J.; Marcelino, N.; Ciardi, A.; Lis, D. C.; Roueff, E.; Wootten, H. A.; Chapillon, E.

2017-10-01

Aims: The formation epoch of protostellar disks is debated because of the competing roles of rotation, turbulence, and magnetic fields in the early stages of low-mass star formation. Magnetohydrodynamics simulations of collapsing cores predict that rotationally supported disks may form in strongly magnetized cores through ambipolar diffusion or misalignment between the rotation axis and the magnetic field orientation. Detailed studies of individual sources are needed to cross check the theoretical predictions. Methods: We present 0.06-0.1'' resolution images at 350 GHz toward B1b-N and B1b-S, which are young class 0 protostars, possibly first hydrostatic cores. The images have been obtained with ALMA, and we compare these data with magnetohydrodynamics simulations of a collapsing turbulent and magnetized core. Results: The submillimeter continuum emission is spatially resolved by ALMA. Compact structures with optically thick 350 GHz emission are detected toward both B1b-N and B1b-S, with 0.2 and 0.35'' radii (46 and 80 au at the Perseus distance of 230 pc), within a more extended envelope. The flux ratio between the compact structure and the envelope is lower in B1b-N than in B1b-S, in agreement with its earlier evolutionary status. The size and orientation of the compact structure are consistent with 0.2'' resolution 32 GHz observations obtained with the Very Large Array as a part of the VANDAM survey, suggesting that grains have grown through coagulation. The morphology, temperature, and densities of the compact structures are consistent with those of disks formed in numerical simulations of collapsing cores. Moreover, the properties of B1b-N are consistent with those of a very young protostar, possibly a first hydrostatic core. These observations provide support for the early formation of disks around low-mass protostars. The reduced images and datacubes are only available at the CDS via anonymous ftp to http://cdsarc.u-strasbg.fr (http://130.79.128.5) or via http://cdsarc.u-strasbg.fr/viz-bin/qcat?J/A+A/606/A35

Loneliness mediates the relationship between emotion dysregulation and bulimia nervosa/binge eating disorder psychopathology in a clinical sample

PubMed Central

Christensen, Kara A.; Fettich, Karla C.; Weissman, Jessica; Berona, Johnny; Chen, Eunice Y.

2017-01-01

Emotion dysregulation has been linked to binge eating disorder (BED) and bulimia nervosa (BN) although the mechanisms by which it affects BN/BED psychopathology are unclear. This study tested loneliness as a mediator between emotion dysregulation and BN/BED psychopathology. A treatment-seeking sample of 107 women with BN or BED was assessed for loneliness (UCLA Loneliness Scale), emotion dysregulation (Difficulties in Emotion Regulation Scale), and BN/BED psychopathology (Eating Disorder Examination) before treatment. Hierarchical linear regressions and bootstrapping mediation models were run. Greater overall emotion dysregulation was associated with greater BN/BED psychopathology, mediated by loneliness (95 % CI 0.03, 0.09). Emotion dysregulation, however, did not mediate between loneliness and BN/BED psychopathology (95 % CI −0.01, 0.01). Targeting loneliness may effectively treat emotional aspects of BN/BED in women. PMID:24235091

Shock compression behavior of a mixture of cubic and hexagonal boron nitride

NASA Astrophysics Data System (ADS)

Hu, Xiaojun; Yang, Gang; Zhao, Bin; Li, Peiyun; Yang, Jun; Leng, Chunwei; Liu, Hanyu; Huang, Haijun; Fei, Yingwei

2018-05-01

We report Hugoniot measurements on a mixture of cubic boron nitride (cBN) and hexagonal boron nitride (hBN, ˜10% in weight) to investigate the shock compression behavior of BN at Hugoniot stresses up to 110 GPa. We observed a discontinuity at ˜77 GPa along the Hugoniot and interpreted it as the manifestation of the shock-induced phase transition of hBN to cBN. The experimental stress at 77-110 GPa shows significant deviation from the hydrodynamic Hugoniot of cBN calculated using the Mie-Grüneisen model coupled with the reported 300 K-isotherms of cBN. Our investigation reveals that material strength in cBN increases with the experimental stress at least up to 110 GPa. The material strength might be preserved at higher stress if we consider the previously reported high stress data.

Diamidophosphines with six-membered chelates and their coordination chemistry with group 4 metals: development of a trimethylene-methane-tethered [PN2]-type "molecular claw".

PubMed

Batke, S; Kothe, T; Haas, M; Wadepohl, H; Ballmann, J

2016-02-28

The coordination chemistry of the phosphine-tethered diamidophosphine ligands PhP(CH2CH2CH2NHPh)2 (pr[NPN]H2) and PhP(1,2-CH2-C6H4-NHSiMe3)2 (bn[NPN]H2) featuring six-membered N–C3–P chelates was explored with group 4 metals, which allowed for the consecutive development of a new trimethylene-methane-tethered [PN2] scaffold. In the case of the propylene-linked system pr[NPN]H2, access to the sparingly soluble dibenzyl derivative pr[NPN]ZrBn2 (3-Zr) was gained, while thermally sensitive zirconium and hafnium diiodo complexes bn[NPN]MI2 (5-M, M = Zr, Hf) were isolated in the case of the benzylene-linked derivative bn[NPN]H2. Despite the related phosphine-tethered backbone architectures of both of these ligands, their group 4 complexes were found to exhibit either C1-symmetric (bn[NPN]MX2) or averaged CS-symmetric (pr[NPN]MX2) structures in solution. To restrain the overall flexibility of these systems and thereby control the properties of the resulting complexes without disrupting the six-membered chelates, the new trimethylene-methane-tethered N,N′-di-(tert-butyl)-substituted [PN2]H2 protioligand was designed. This tripodal ligand system was prepared on a gram scale and its CS-symmetric dichloro complexes [PN2]MCl2 (6-M, M = Ti, Zr, Hf) were isolated subsequently. The benzene-soluble dibenzyl derivative [PN2]ZrBn2 (7-Zr) was synthesised as well and characterised by X-ray diffraction. These results are discussed not only in conjunction with the known [NPN]-coordinated group 4 complexes incorporating five-membered chelates, but also in the context of “molecular claws” that are related to the new [PN2] tripod.

Antimicrobial (BN/PE) film combined with modified atmosphere packaging extends the shelf life of minimally processed fresh-cut iceberg lettuce.

PubMed

Kang, Sun-Chul; Kim, Min-Jeong; Park, In-Sik; Choi, Ung-Kyu

2008-03-01

This study was conducted to investigate the effect of modified atmosphere packaging (MAP) in combination with BN/PE film on the shelf life and quality of fresh-cut iceberg lettuce during cold storage. The total mesophilic population in the sample packed in BN/PE film under MAP conditions was dramatically reduced in comparison with that of PE film, PE film under MAP conditions, and BN/PE film. The O2 concentration in the BN/PE film under MAP conditions decreased slightly as the storage period progressed. The coloration of the iceberg lettuce progressed the slowest when it was packaged in BN/PE film under MAP conditions, followed by BN/PE film, PE film, and PE film under MAP conditions. The shelf life of fresh-cut iceberg lettuce packaged in the BN/PE film under MAP conditions was extended by more than 2 days at 10 degrees as compared with that of the BN/PE film in which the extension effect was more than 2 days longer than that of PE, PET, and OPP films.

Boron Nitride Obtained from Molecular Precursors: Aminoboranes Used as a BN Source for Coatings, Matrix, and Si 3N 4-BN Composite Ceramic Preparation

NASA Astrophysics Data System (ADS)

Thévenot, F.; Doche, C.; Mongeot, H.; Guilhon, F.; Miele, P.; Cornu, D.; Bonnetot, B.

1997-10-01

Aminoboranes, pure or partially converted into aminoborazines using thermal or aminolysis polymerization, have been used as boron nitride precursors. An amorphous BN preceramic is obtained when pyrolysed up to 1000°C that can be stabilized using further annealing up to 1400°C or crystallized into h-BN above 1700°C. These molecular precursors have been used to prepare carbon fiber/BN matrix microcomposites to get an efficient BN coating on graphite and as a BN source in Si3N4/BN composite ceramic. The properties of these new types of samples have been compared with those obtained by classical processes. The boron nitride obtained from these precursors is a good sintering agent during the hot-pressing of the samples. However, the crystallinity of BN, even sintered up to 1800°C, remains poor. In fact, most of the mechanical properties of the composite ceramic (density, porosity, hardness) are clearly improved and the aminoboranes can be considered as convenient boron nitride sources and helpful sintering agents in hot-pressing technology.

CBT4BN versus CBTF2F: Comparison of Online versus Face-To-FaceTreatment for Bulimia Nervosa

PubMed Central

Bulik, Cynthia M.; Marcus, Marsha D.; Zerwas, Stephanie; Levine, Michele D.; Hofmeier, Sara; Trace, Sara E.; Hamer, Robert M.; Zimmer, Benjamin; Moessner, Markus; Kordy, Hans

2012-01-01

Cognitive-behavioral therapy (CBT) is currently the “gold standard” for treatment of bulimia nervosa (BN), and is effective for approximately 40–60% of individuals receiving treatment; however, the majority of individuals in need of care do not have access to CBT. New strategies for service delivery of CBT and for maximizing maintenance of treatment benefits are critical for improving our ability to treat BN. This clinical trial is comparing an Internet-based version of CBT (CBT4BN) in which group intervention is conducted via therapeutic chat group with traditional group CBT (CBTF2F) for BN conducted via face-to-face therapy group. The purpose of the trial is to determine whether manualized CBT delivered via the Internet is not inferior to the gold standard of manualized group CBT. In this two-site randomized controlled trial, powered for non-inferiority analyses, 180 individuals with BN are being randomized to either CBT4BN or CBTF2F. We hypothesize that CBT4BN will not be inferior to CBTF2F and that participants will value the convenience of an online intervention. If not inferior, CBT4BN may be a cost-effective approach to service delivery for individuals requiring treatment for BN. PMID:22659072

In situ synthesis of Fe-based alloy clad coatings containing TiB2-TiN-(h-BN)

NASA Astrophysics Data System (ADS)

Jiang, Shao-qun; Wang, Gang; Ren, Qing-wen; Yang, Chuan-duo; Wang, Ze-hua; Zhou, Ze-hua

2015-06-01

Fe-based alloy coatings containing TiB2-TiN-(h-BN) were synthesized in situ on Q235 steel substrates by a plasma cladding process using the powders of Fe901 alloy, Ti, and h-BN as raw materials. The effects of Ti/h-BN mass ratio on interfacial bonds between the coating and substrate along with the microstructures and microhardnesses of the coatings were investigated. The results show that the Ti/h-BN mass ratio is a vital factor in the formation of the coatings. Free h-BN can be introduced into the coatings by adding an excess amount of h-BN into the precursor. Decreases in the Ti/h-BN mass ratio improve the microstructural uniformity and compactness and enhance the interfacial bonds of the coatings. At a Ti/h-BN mass ratio of 10/20, the coating is free of cracks and micropores, and mainly consists of Fe-Cr, Fe3B, TiB2, TiN, Ti2N, TiB, FeN, FeB, Fe2B, and h-BN phases. Its average microhardness in the zone between 0.1-2.8 mm from the coating surface is about Hv0.2 551.5.

On the Stability of c-BN-Reinforcing Particles in Ceramic Matrix Materials

PubMed Central

Wolfrum, Anne-Kathrin; Michaelis, Alexander; Herrmann, Mathias

2018-01-01

Cubic boron nitride (c-BN) composites produced at high pressures and temperatures are widely used as cutting tool materials. The advent of new, effective pressure-assisted densification methods, such as spark plasma sintering (SPS), has stimulated attempts to produce these composites at low pressures. Under low-pressure conditions, however, transformation of c-BN to the soft hexagonal BN (h-BN) phase can occur, with a strong deterioration in hardness and wear. In the present work, the influence of secondary phases (B2O3, Si3N4, and oxide glasses) on the transformation of c-BN was studied in the temperature range between 1100 °C and 1575 °C. The different heat treated c-BN particles and c-BN composites were analyzed by SEM, X-ray diffraction, and Raman spectroscopy. The transformation mechanism was found to be kinetically controlled solution–diffusion–precipitation. Given a sufficiently low liquid phase viscosity, the transformation could be observed at temperatures as low as 1200 °C for the c-BN–glass composites. In contrast, no transformation was found at temperatures up to 1575 °C when no liquid oxide phase is present in the composite. The results were compared with previous studies concerning the c-BN stability and the c-BN phase diagram. PMID:29414847

Toxicity evaluation of boron nitride nanospheres and water-soluble boron nitride in Caenorhabditis elegans

PubMed Central

Wang, Ning; Wang, Hui; Tang, Chengchun; Lei, Shijun; Shen, Wanqing; Wang, Cong; Wang, Guobin; Wang, Zheng; Wang, Lin

2017-01-01

Boron nitride (BN) nanomaterials have been increasingly explored for potential biological applications. However, their toxicity remains poorly understood. Using Caenorhabditis elegans as a whole-animal model for toxicity analysis of two representative types of BN nanomaterials – BN nanospheres (BNNSs) and highly water-soluble BN nanomaterial (named BN-800-2) – we found that BNNSs overall toxicity was less than soluble BN-800-2 with irregular shapes. The concentration thresholds for BNNSs and BN-800-2 were 100 µg·mL−1 and 10 µg·mL−1, respectively. Above this concentration, both delayed growth, decreased life span, reduced progeny, retarded locomotion behavior, and changed the expression of phenotype-related genes to various extents. BNNSs and BN-800-2 increased oxidative stress levels in C. elegans by promoting reactive oxygen species production. Our results further showed that oxidative stress response and MAPK signaling-related genes, such as GAS1, SOD2, SOD3, MEK1, and PMK1, might be key factors for reactive oxygen species production and toxic responses to BNNSs and BN-800-2 exposure. Together, our results suggest that when concentrations are lower than 10 µg·mL−1, BNNSs are more biocompatible than BN-800-2 and are potentially biocompatible material. PMID:28860759

Toxicity evaluation of boron nitride nanospheres and water-soluble boron nitride in Caenorhabditis elegans.

PubMed

Wang, Ning; Wang, Hui; Tang, Chengchun; Lei, Shijun; Shen, Wanqing; Wang, Cong; Wang, Guobin; Wang, Zheng; Wang, Lin

2017-01-01

Boron nitride (BN) nanomaterials have been increasingly explored for potential biological applications. However, their toxicity remains poorly understood. Using Caenorhabditis elegans as a whole-animal model for toxicity analysis of two representative types of BN nanomaterials - BN nanospheres (BNNSs) and highly water-soluble BN nanomaterial (named BN-800-2) - we found that BNNSs overall toxicity was less than soluble BN-800-2 with irregular shapes. The concentration thresholds for BNNSs and BN-800-2 were 100 µg·mL -1 and 10 µg·mL -1 , respectively. Above this concentration, both delayed growth, decreased life span, reduced progeny, retarded locomotion behavior, and changed the expression of phenotype-related genes to various extents. BNNSs and BN-800-2 increased oxidative stress levels in C. elegans by promoting reactive oxygen species production. Our results further showed that oxidative stress response and MAPK signaling-related genes, such as GAS1 , SOD2 , SOD3 , MEK1 , and PMK1 , might be key factors for reactive oxygen species production and toxic responses to BNNSs and BN-800-2 exposure. Together, our results suggest that when concentrations are lower than 10 µg·mL -1 , BNNSs are more biocompatible than BN-800-2 and are potentially biocompatible material.

Boride Formation Induced by pcBN Tool Wear in Friction-Stir-Welded Stainless Steels

NASA Astrophysics Data System (ADS)

Park, Seung Hwan C.; Sato, Yutaka S.; Kokawa, Hiroyuki; Okamoto, Kazutaka; Hirano, Satoshi; Inagaki, Masahisa

2009-03-01

The wear of polycrystalline cubic boron nitride (pcBN) tool and its effect on second phase formation were investigated in stainless steel friction-stir (FS) welds. The nitrogen content and the flow stress were analyzed in these welds to examine pcBN tool wear. The nitrogen content in stir zone (SZ) was found to be higher in the austenitic stainless steel FS welds than in the ferritic and duplex stainless steel welds. The flow stress of austenitic stainless steels was almost 1.5 times larger than that of ferritic and duplex stainless steels. These results suggest that the higher flow stress causes the severe tool wear in austenitic stainless steels, which results in greater nitrogen pickup in austenitic stainless steel FS welds. From the microstructural observation, a possibility was suggested that Cr-rich borides with a crystallographic structure of Cr2B and Cr5B3 formed through the reaction between the increased boron and nitrogen and the matrix during FS welding (FSW).

New Cu(TiBN x ) copper alloy films for industrial applications

NASA Astrophysics Data System (ADS)

Lin, Chon-Hsin

2016-06-01

In this study, I explore a new type of copper alloy, Cu(TiBN x ), films by cosputtering Cu and TiB within an Ar/N2 gas atmosphere on Si substrates. The films are then annealed for 1 h in a vacuum environment at temperatures up to 700 °C. The annealed films exhibit not only excellent thermal stability and low resistivity but also little leakage current and strong adhesion to the substrates while no Cu/Si interfacial interactions are apparent. Within a Sn/Cu(TiBN x )/Si structure at 200 °C, the new alloy exhibits a minute dissolution rate, which is lower than that of pure Cu by at least one order of magnitude. Furthermore, the new alloy’s consumption rate is comparable to that of Ni commonly used in solder joints. The new films appear suitable for some industrial applications, such as barrierless Si metallization and new wetting and diffusion barrier layers required in flip-chip solder joints.

Two sides of the same coin? A new instrument to assess body checking and avoidance behaviors in eating disorders.

PubMed

Legenbauer, Tanja; Martin, Franziska; Blaschke, Ariane; Schwenzfeier, Anne; Blechert, Jens; Schnicker, Katja

2017-06-01

Body checking (BC) and avoidance behaviors (BA) are the dominant behavioral features of body image disturbances (BID) that characterize most individuals with eating disorders (EDs). Whereas BC can be reliably assessed, a valid assessment tool for BA is lacking, preventing an adequate assessment of BID differences across different EDs (anorexia nervosa, AN; bulimia nervosa, BN; binge eating disorder, BED). A total of 310 women with EDs and 112 nonclinical controls completed measures of BC-, BA- and ED-related symptoms. BA did not differentiate between EDs, whereas BC did: it was highest in AN and BN, and lowest in BED. Multivariate analyses also discriminated AN from BN based on BC. Given that results are of preliminary nature, evidence is promising that EDs can be discriminated from healthy controls and that differential BID profiles for the behavioral component among ED subgroups exist. However, replication of the factor structure remains open within ED subsamples. Copyright © 2017 Elsevier Ltd. All rights reserved.

Efficient Gate-tunable light-emitting device made of defective boron nitride nanotubes: from ultraviolet to the visible

PubMed Central

Attaccalite, Claudio; Wirtz, Ludger; Marini, Andrea; Rubio, Angel

2013-01-01

Boron nitride is a promising material for nanotechnology applications due to its two-dimensional graphene-like, insulating, and highly-resistant structure. Recently it has received a lot of attention as a substrate to grow and isolate graphene as well as for its intrinsic UV lasing response. Similar to carbon, one-dimensional boron nitride nanotubes (BNNTs) have been theoretically predicted and later synthesised. Here we use first principles simulations to unambiguously demonstrate that i) BN nanotubes inherit the highly efficient UV luminescence of hexagonal BN; ii) the application of an external perpendicular field closes the electronic gap keeping the UV lasing with lower yield; iii) defects in BNNTS are responsible for tunable light emission from the UV to the visible controlled by a transverse electric field (TEF). Our present findings pave the road towards optoelectronic applications of BN-nanotube-based devices that are simple to implement because they do not require any special doping or complex growth. PMID:24060843

Approaching quantum anomalous Hall effect in proximity-coupled YIG/graphene/h-BN sandwich structure

NASA Astrophysics Data System (ADS)

Tang, Chi; Cheng, Bin; Aldosary, Mohammed; Wang, Zhiyong; Jiang, Zilong; Watanabe, K.; Taniguchi, T.; Bockrath, Marc; Shi, Jing

2018-02-01

Quantum anomalous Hall state is expected to emerge in Dirac electron systems such as graphene under both sufficiently strong exchange and spin-orbit interactions. In pristine graphene, neither interaction exists; however, both interactions can be acquired by coupling graphene to a magnetic insulator as revealed by the anomalous Hall effect. Here, we show enhanced magnetic proximity coupling by sandwiching graphene between a ferrimagnetic insulator yttrium iron garnet (YIG) and hexagonal-boron nitride (h-BN) which also serves as a top gate dielectric. By sweeping the top-gate voltage, we observe Fermi level-dependent anomalous Hall conductance. As the Dirac point is approached from both electron and hole sides, the anomalous Hall conductance reaches ¼ of the quantum anomalous Hall conductance 2e2/h. The exchange coupling strength is determined to be as high as 27 meV from the transition temperature of the induced magnetic phase. YIG/graphene/h-BN is an excellent heterostructure for demonstrating proximity-induced interactions in two-dimensional electron systems.

Development of scanning graphene Hall probes for magnetic microscopy

NASA Astrophysics Data System (ADS)

Schaefer, Brian T.; Wang, Lei; McEuen, Paul L.; Nowack, Katja C.

We discuss our progress on developing scanning Hall probes fabricated from hexagonal boron nitride (hBN)-encapsulated graphene, with the goal to image magnetic fields with submicron resolution. In contrast to scanning superconducting quantum interference device (SQUID) microscopy, this technique is compatible with a large applied magnetic field and not limited to cryogenic temperatures. The field sensitivity of a Hall probe depends inversely on carrier density, while the primary source of noise in the measurement is Johnson noise originating from the device resistance. hBN-encapsulated graphene demonstrates high carrier mobility at low carrier densities, therefore making it an ideal material for sensitive Hall probes. Furthermore, engineering the dielectric environment of graphene by encapsulating in hBN reduces low-frequency charge noise and disorder from the substrate. We outline our plans for adapting these devices for scanning, including characterization of the point spread function with a scanned current loop and fabrication of a deep-etched structure that enables positioning the sensitive area within 100 nanometers of the sample surface.

A probabilistic model for accidental cargo oil outflow from product tankers in a ship-ship collision.

PubMed

Goerlandt, Floris; Montewka, Jakub

2014-02-15

In risk assessment of maritime transportation, estimation of accidental oil outflow from tankers is important for assessing environmental impacts. However, there typically is limited data concerning the specific structural design and tank arrangement of ships operating in a given area. Moreover, there is uncertainty about the accident scenarios potentially emerging from ship encounters. This paper proposes a Bayesian network (BN) model for reasoning under uncertainty for the assessment of accidental cargo oil outflow in a ship-ship collision where a product tanker is struck. The BN combines a model linking impact scenarios to damage extent with a model for estimating the tank layouts based on limited information regarding the ship. The methodology for constructing the model is presented and output for two accident scenarios is shown. The discussion elaborates on the issue of model validation, both in terms of the BN and in light of the adopted uncertainty/bias-based risk perspective. Copyright © 2013 The Authors. Published by Elsevier Ltd.. All rights reserved.

Integrated network modelling for identifying microbial mechanisms of particulate organic carbon accumulation in coastal marine systems

NASA Astrophysics Data System (ADS)

McDonald, Karlie; Turk, Valentina; Mozetič, Patricija; Tinta, Tinkara; Malfatti, Francesca; Hannah, David; Krause, Stefan

2016-04-01

Accumulation of particulate organic carbon (POC) has the potential to change the structure and function of marine ecosystems. High abidance of POC can develop into aggregates, known as marine snow or mucus aggregates that can impair essential marine ecosystem functioning and services. Currently marine POC formation, accumulation and sedimentation processes are being explored as potential pathways to remove CO2 from the atmosphere by CO2 sequestration via fixation into biomass by phytoplankton. However, the current ability of scientists, environmental managers and regulators to analyse and predict high POC concentrations is restricted by the limited understanding of the dynamic nature of the microbial mechanisms regulating POC accumulation events in marine environments. We present a proof of concept study that applies a novel Bayesian Networks (BN) approach to integrate relevant biological and physical-chemical variables across spatial and temporal scales in order to identify the interactions of the main contributing microbial mechanisms regulating POC accumulation in the northern Adriatic Sea. Where previous models have characterised only the POC formed, the BN approach provides a probabilistic framework for predicting the occurrence of POC accumulation by linking biotic factors with prevailing environmental conditions. In this paper the BN was used to test three scenarios (diatom, nanoflagellate, and dinoflagellate blooms). The scenarios predicted diatom blooms to produce high chlorophyll a at the water surface while nanoflagellate blooms were predicted to occur at lower depths (> 6m) in the water column and produce lower chlorophyll a concentrations. A sensitivity analysis identified the variables with the greatest influence on POC accumulation being the enzymes protease and alkaline phosphatase, which highlights the importance of microbial community interactions. The developed proof of concept BN model allows for the first time to quantify the impacts of biological, chemical and physical parameters influencing microbial community interactions mechanisms that regulate POC accumulation in marine environments. The dynamic modular nature of the developed BN will allow successive updating and improvement of the model structure as new data are emerging, thus, providing a powerful interactive framework for the investigation, prediction and mitigation of future POC accumulation events.

The core symptoms of bulimia nervosa, anxiety, and depression: A network analysis.

PubMed

Levinson, Cheri A; Zerwas, Stephanie; Calebs, Benjamin; Forbush, Kelsie; Kordy, Hans; Watson, Hunna; Hofmeier, Sara; Levine, Michele; Crosby, Ross D; Peat, Christine; Runfola, Cristin D; Zimmer, Benjamin; Moesner, Markus; Marcus, Marsha D; Bulik, Cynthia M

2017-04-01

Bulimia nervosa (BN) is characterized by symptoms of binge eating and compensatory behavior, and overevaluation of weight and shape, which often co-occur with symptoms of anxiety and depression. However, there is little research identifying which specific BN symptoms maintain BN psychopathology and how they are associated with symptoms of depression and anxiety. Network analyses represent an emerging method in psychopathology research to examine how symptoms interact and may become self-reinforcing. In the current study of adults with a Diagnostic and Statistical Manual for Mental Disorders-Fourth Edition ( DSM-IV ) diagnosis of BN (N = 196), we used network analysis to identify the central symptoms of BN, as well as symptoms that may bridge the association between BN symptoms and anxiety and depression symptoms. Results showed that fear of weight gain was central to BN psychopathology, whereas binge eating, purging, and restriction were less central in the symptom network. Symptoms related to sensitivity to physical sensations (e.g., changes in appetite, feeling dizzy, and wobbly) were identified as bridge symptoms between BN, and anxiety and depressive symptoms. We discuss our findings with respect to cognitive-behavioral treatment approaches for BN. These findings suggest that treatments for BN should focus on fear of weight gain, perhaps through exposure therapies. Further, interventions focusing on exposure to physical sensations may also address BN psychopathology, as well as co-occurring anxiety and depressive symptoms. (PsycINFO Database Record (c) 2017 APA, all rights reserved).

Chemical shielding properties for BN, BP, AlN, and AlP nanocones: DFT studies

NASA Astrophysics Data System (ADS)

Mirzaei, Mahmoud; Yousefi, Mohammad; Meskinfam, Masoumeh

2012-06-01

The properties of boron nitride (BN), boron phosphide (BP), aluminum nitride (AlN), and aluminum phosphide (AlP) nanocones were investigated by density functional theory (DFT) calculations. The investigated structures were optimized and chemical shielding (CS) properties including isotropic and anisotropic CS parameters were calculated for the atoms of the optimized structures. The magnitudes of CS parameters were observed to be mainly dependent on the bond lengths of considered atoms. The results indicated that the atoms could be divided into atomic layers due to the similarities of their CS properties for the atoms of each layer. The trend means that the atoms of each layer detect almost similar electronic environments. Moreover, the atoms at the apex and mouth of nanocones exhibit different properties with respect to the other atomic layers.

Influence of point defects on the near edge structure of hexagonal boron nitride

NASA Astrophysics Data System (ADS)

McDougall, Nicholas L.; Partridge, Jim G.; Nicholls, Rebecca J.; Russo, Salvy P.; McCulloch, Dougal G.

2017-10-01

Hexagonal boron nitride (hBN) is a wide-band-gap semiconductor with applications including gate insulation layers in graphene transistors, far-ultraviolet light emitting devices and as hydrogen storage media. Due to its complex microstructure, defects in hBN are challenging to identify. Here, we combine x-ray absorption near edge structure (XANES) spectroscopy with ab initio theoretical modeling to identify energetically favorable defects. Following annealing of hBN samples in vacuum and oxygen, the B and N K edges exhibited angular-dependent peak modifications consistent with in-plane defects. Theoretical calculations showed that the energetically favorable defects all produce signature features in XANES. Comparing these calculations with experiments, the principle defects were attributed to substitutional oxygen at the nitrogen site, substitutional carbon at the boron site, and hydrogen passivated boron vacancies. Hydrogen passivation of defects was found to significantly affect the formation energies, electronic states, and XANES. In the B K edge, multiple peaks above the major 1 s to π* peak occur as a result of these defects and the hydrogen passivated boron vacancy produces the frequently observed doublet in the 1 s to σ* transition. While the N K edge is less sensitive to defects, features attributable to substitutional C at the B site were observed. This defect was also calculated to have mid-gap states in its band structure that may be responsible for the 4.1-eV ultraviolet emission frequently observed from this material.

How should DSM-V classify eating disorder not otherwise specified (EDNOS) presentations in women with lifetime anorexia or bulimia nervosa?

PubMed Central

Eddy, K. T.; Swanson, S. A.; Crosby, R. D.; Franko, D. L.; Engel, S.; Herzog, D. B.

2013-01-01

Objective Anorexia nervosa (AN) and bulimia nervosa (BN) are marked by longitudinal symptom fluctuations. DSM-IV-TR does not address how to classify eating disorder (ED) presentations in individuals who no longer meet full criteria for these disorders. To consider this issue, we examined subthreshold presentations in women with initial diagnoses of AN and BN. Method A total of 246 women with AN or BN were followed for a median of 9 years; weekly symptom data were collected at frequent intervals using the Longitudinal Interval Follow-up Evaluation of Eating Disorders (LIFE-EAT-II). Outcomes were ED presentations that were subthreshold for ≥3 months, including those narrowly missing full criteria for AN or BN, along with binge eating disorder (BED) and purging disorder. Results During follow-up, most women (77.6%) experienced a subthreshold presentation. Subthreshold presentation was related to intake diagnosis (Wald χ2 = 8.065, df = 2, p = 0.018). Individuals with AN most often developed subthreshold presentations resembling AN; those with BN were more likely to develop subthreshold BN. Purging disorder was experienced by half of those with BN and one-quarter of those with AN binge/purge type (ANBP); BED occurred in 20% with BN. Transition from AN or BN to most subthreshold types was associated with improved psychosocial functioning (p < 0.001). Conclusions Subthreshold presentations in women with lifetime AN and BN were common, resembled the initial diagnosis, and were associated with modest improvements in psychosocial functioning. For most with lifetime AN and BN, subthreshold presentations seem to represent part of the course of illness and to fit within the original AN or BN diagnosis. PMID:20047706

Humanized immunoglobulin mice: models for HIV vaccine testing and studying the broadly neutralizing antibody problem

PubMed Central

Verkoczy, Laurent

2018-01-01

A vaccine that can effectively prevent HIV-1 transmission remains paramount to ending the HIV pandemic, but to do so, will likely need to induce broad neutralizing antibody (bnAb) responses. A major technical hurdle towards achieving this goal has been a shortage of animal models with the ability to systematically pinpoint roadblocks to bnAb induction and to rank vaccine strategies based on their ability to stimulate bnAb development. Over the past six years, immunoglobulin (Ig) knock-in (KI) technology has been leveraged to express bnAbs in mice, an approach that has enabled elucidation of various B-cell tolerance mechanisms limiting bnAb production and evaluation of strategies to circumvent such processes. From these studies, in conjunction with the wealth of information recently obtained regarding the evolutionary pathways and paratopes/epitopes of multiple bnAbs, it has become clear that the very features of bnAbs desired for their function will be problematic to elicit by traditional vaccine paradigms, necessitating more iterative testing of new vaccine concepts. To meet this need, novel bnAb KI models have now been engineered to express either inferred pre-rearranged V(D)J exons (or unrearranged germline V, D, or J segments that can be assembled into functional rearranged V(D)J exons) encoding predecessors of mature bnAbs One encouraging approach that has materialized from studies using such newer models is sequential administration of immunogens designed to bind progressively more mature bnAb predecessors. In this review, insights into the regulation and induction of bnAbs based on the use of KI models will be discussed, as will new Ig KI approaches for higher-throughput production and/or altering expression of bnAbs in vivo, so as to further enable vaccine-guided bnAb induction studies. PMID:28413022

Polypropylene Biocomposites with Boron Nitride and Nanohydroxyapatite Reinforcements

PubMed Central

Chan, Kai Wang; Wong, Hoi Man; Yeung, Kelvin Wai Kwok; Tjong, Sie Chin

2015-01-01

In this study, we develop binary polypropylene (PP) composites with hexagonal boron nitride (hBN) nanoplatelets and ternary hybrids reinforced with hBN and nanohydroxyapatite (nHA). Filler hybridization is a sound approach to make novel nanocomposites with useful biological and mechanical properties. Tensile test, osteoblastic cell culture and dimethyl thiazolyl diphenyl tetrazolium (MTT) assay were employed to investigate the mechanical performance, bioactivity and biocompatibility of binary PP/hBN and ternary PP/hBN-nHA composites. The purpose is to prepare biocomposite nanomaterials with good mechanical properties and biocompatibility for replacing conventional polymer composites reinforced with large hydroxyapatite microparticles at a high loading of 40 vol%. Tensile test reveals that the elastic modulus of PP composites increases, while tensile elongation decreases with increasing hBN content. Hybridization of hBN with nHA further enhances elastic modulus of PP. The cell culture and MTT assay show that osteoblastic cells attach and proliferate on binary PP/hBN and ternary PP/hBN-20%nHA nanocomposites. PMID:28787984

What Are the Primary Limitations in B-Cell Affinity Maturation, and How Much Affinity Maturation Can We Drive with Vaccination?

PubMed Central

2017-01-01

A key goal of HIV-1 vaccine development is the induction of broadly neutralizing antibodies (bnAbs) targeted to the vulnerable regions of the HIV envelope. BnAbs develop overtime in ∼50%of HIV-1-infected individuals. However, to date, no vaccines have induced bnAbs and few or none of these vaccine-elicited HIV-1 antibodies carry the high frequencies of V(D)J mutations characteristic of bnAbs. Do the high frequencies of mutations characteristic of naturally induced bnAbs represent a fundamental barrier to the induction of bnAbs by vaccines? Recent studies suggest that high frequencies of V(D)J mutations can be achieved by serial vaccination strategies. Rather, it appears that, in the absence of HIV-1 infection, physiologic immune tolerance controls, including a germinal center process termed affinity reversion, may limit vaccine-driven bnAb development by clonal elimination or selecting for mutations incompatible with bnAb activity. PMID:28630077

Functional Relevance of Improbable Antibody Mutations for HIV Broadly Neutralizing Antibody Development.

PubMed

Wiehe, Kevin; Bradley, Todd; Meyerhoff, R Ryan; Hart, Connor; Williams, Wilton B; Easterhoff, David; Faison, William J; Kepler, Thomas B; Saunders, Kevin O; Alam, S Munir; Bonsignori, Mattia; Haynes, Barton F

2018-06-13

HIV-1 broadly neutralizing antibodies (bnAbs) require high levels of activation-induced cytidine deaminase (AID)-catalyzed somatic mutations for optimal neutralization potency. Probable mutations occur at sites of frequent AID activity, while improbable mutations occur where AID activity is infrequent. One bottleneck for induction of bnAbs is the evolution of viral envelopes (Envs) that can select bnAb B cell receptors (BCR) with improbable mutations. Here we define the probability of bnAb mutations and demonstrate the functional significance of key improbable mutations in three bnAb B cell lineages. We show that bnAbs are enriched for improbable mutations, which implies that their elicitation will be critical for successful vaccine induction of potent bnAb B cell lineages. We discuss a mutation-guided vaccine strategy for identification of Envs that can select B cells with BCRs that have key improbable mutations required for bnAb development. Copyright © 2018 The Authors. Published by Elsevier Inc. All rights reserved.

Chemically stabilized epitaxial wurtzite-BN thin film

NASA Astrophysics Data System (ADS)

Vishal, Badri; Singh, Rajendra; Chaturvedi, Abhishek; Sharma, Ankit; Sreedhara, M. B.; Sahu, Rajib; Bhat, Usha; Ramamurty, Upadrasta; Datta, Ranjan

2018-03-01

We report on the chemically stabilized epitaxial w-BN thin film grown on c-plane sapphire by pulsed laser deposition under slow kinetic condition. Traces of no other allotropes such as cubic (c) or hexagonal (h) BN phases are present. Sapphire substrate plays a significant role in stabilizing the metastable w-BN from h-BN target under unusual PLD growth condition involving low temperature and pressure and is explained based on density functional theory calculation. The hardness and the elastic modulus of the w-BN film are 37 & 339 GPa, respectively measured by indentation along <0001> direction. The results are extremely promising in advancing the microelectronic and mechanical tooling industry.

BnNHL18A shows a localization change by stress-inducing chemical treatments

DOE Office of Scientific and Technical Information (OSTI.GOV)

Lee, Suk-Bae; Ham, Byung-Kook; Park, Jeong Mee

2006-01-06

The two genes, named BnNHL18A and BnNHL18B, showing sequence homology with Arabidopsis NDR1/HIN1-like (NHL) genes, were isolated from cDNA library prepared with oilseed rape (Brassica napus) seedlings treated with NaCl. The transcript level of BnNHL18A was increased by sodium chloride, ethephon, hydrogen peroxide, methyl jasmonate, or salicylic acid treatment. The coding regions of BnNHL18A and BnNHL18B contain a sarcolipin (SLN)-like sequence. Analysis of the localization of smGFP fusion proteins showed that BnNHL18A is mainly localized to endoplasmic reticulum (ER). This result suggests that the SLN-like sequence plays a role in retaining proteins in ER membrane in plants. In response tomore » NaCl, hydrogen peroxide, ethephon, and salicylic acid treatments, the protein localization of BnNHL18A was changed. Our findings suggest a common function of BnNHL18A in biotic and abiotic stresses, and demonstrate the presence of the shared mechanism of protein translocalization between the responses to plant pathogen and to osmotic stress.« less

Analysis of audiometric notch as a noise-induced hearing loss phenotype in US youth: data from the National Health And Nutrition Examination Survey, 2005-2010.

PubMed

Bhatt, Ishan S; Guthrie, O'neil

2017-06-01

Bilateral audiometric notch (BN) at 4000-6000 Hz was identified as a noise-induced hearing loss (NIHL) phenotype for genetic association analysis in college-aged musicians. This study analysed BN in a sample of US youth. Prevalence of the BN within the study sample was determined and logistic-regression analyses were performed to identify audiologic and other demographic factors associated with BN. Computer-simulated "flat" audiograms were used to estimate potential influence of false-positive rates in estimating the prevalence of the BN. 2348 participants (12-19 years) following the inclusion criteria were selected from the National Health and Nutrition Examination Survey data (2005-2010). The prevalence of BN was 16.6%. Almost 55.6% of the participants showed notch in at least one ear. Noise exposure, gender, ethnicity and age showed significant relationship with the BN. Computer simulation revealed that 5.5% of simulated participants with "flat" audiograms showed BN. Association of noise exposure with BN suggests that it is a useful NIHL phenotype for genetic association analyses. However, further research is necessary to reduce false-positive rates in notch identification.

I-V characteristics of graphene nanoribbon/h-BN heterojunctions and resonant tunneling.

PubMed

Wakai, Taiga; Sakamoto, Shoichi; Tomiya, Mitsuyoshi

2018-07-04

We present the first principle calculations of the electrical properties of graphene sheet/h-BN heterojunction (GS/h-BN) and 11-armchair graphene nanoribbon/h-BN heterojunction (11-AGNR/h-BN), which are carried out using the density functional theory (DFT) method and the non-equilibrium Green's function (NEGF) technique. Since 11-AGNR belongs to the conductive (3n-1)-family of AGNR, both are metallic nanomaterials with two transverse arrays of h-BN, which is a wide-gap semi-conductor. The two h-BN arrays act as double barriers. The transmission functions (TF) and I-[Formula: see text] characteristics of GS/h-BN and 11-AGNR/h-BN are calculated by DFT and NEGF, and they show that quantum double barrier tunneling occurs. The TF becomes very spiky in both materials, and it leads to step-wise I-[Formula: see text] characteristics rather than negative resistance, which is the typical behavior of double barriers in semiconductors. The results of our first principle calculations are also compared with 1D Dirac equation model for the double barrier system. The model explains most of the peaks of the transmission functions nearby the Fermi energy quite well. They are due to quantum tunneling.

Process-Induced Carbon and Sub-Layer in SiC/BN/SiC Composites: Characterization and Consequences

NASA Technical Reports Server (NTRS)

Ogbuji, L. U. J. T; Wheeler, D. R.; McCue, T. R.

2001-01-01

Following our detection of films of elemental carbon in the Hi-Nicalon TM/BN/SiC composite and its deleterious effect on oxidative durability, we have examined other SiC/BN/SiC systems. The problem is pervasive, and significant residues of free carbon are confirmed in Sylramic /BN/SiC materials. Effective techniques for routine detection and characterization of adventitious carbon in SiC/BN/SiC composites are discussed.

Bombesin related peptides/receptors and their promising therapeutic roles in cancer imaging, targeting and treatment

PubMed Central

Moreno, Paola; Ramos-Álvarez, Irene; Moody, Terry W.; Jensen, Robert T.

2016-01-01

Introduction Despite remarkable advances in tumor treatment, many patients still die from common tumors (breast, prostate, lung, CNS, colon, and pancreas), and thus, new approaches are needed. Many of these tumors synthesize bombesin (Bn)-related peptides and over-express their receptors (BnRs), hence functioning as autocrine-growth-factors. Recent studies support the conclusion that Bn-peptides/BnRs are well-positioned for numerous novel antitumor treatments, including interrupting autocrine-growth via the use of over-expressed receptors for imaging and targeting cytotoxic-compounds, either by direct-coupling or combined with nanoparticle-technology. Areas covered The unique ability of common neoplasms to synthesize, secrete, and show a growth/proliferative/differentiating response due to BnR over-expression, is reviewed, both in general and with regard to the most frequently investigated neoplasms (breast, prostate, lung, and CNS). Particular attention is paid to advances in the recent years. Also considered are the possible therapeutic approaches to the growth/differentiation effect of Bn-peptides, as well as the therapeutic implication of the frequent BnR over-expression for tumor-imaging and/or targeted-delivery. Expert opinion Given that Bn-related-peptides/BnRs are so frequently ectopically-expressed by common tumors, which are often malignant and become refractory to conventional treatments, therapeutic interventions using novel approaches to Bn-peptides and receptors are being explored. Of particular interest is the potential of reproducing BnRs in common tumors, such as the recent success of utilizing overexpression of somatostatin-receptors by neuroendocrine-tumors to provide the most sensitive imaging methods and targeted delivery of cytotoxic-compounds. PMID:26981612

Structural impact on the eigenenergy renormalization for carbon and silicon allotropes and boron nitride polymorphs

NASA Astrophysics Data System (ADS)

Tutchton, Roxanne; Marchbanks, Christopher; Wu, Zhigang

2018-05-01

The phonon-induced renormalization of electronic band structures is investigated through first-principles calculations based on the density functional perturbation theory for nine materials with various crystal symmetries. Our results demonstrate that the magnitude of the zero-point renormalization (ZPR) of the electronic band structure is dependent on both crystal structure and material composition. We have performed analysis of the electron-phonon-coupling-induced renormalization for two silicon (Si) allotropes, three carbon (C) allotropes, and four boron nitride (BN) polymorphs. Phonon dispersions of each material were computed, and our analysis indicates that materials with optical phonons at higher maximum frequencies, such as graphite and hexagonal BN, have larger absolute ZPRs, with the exception of graphene, which has a considerably smaller ZPR despite having phonon frequencies in the same range as graphite. Depending on the structure and material, renormalizations can be comparable to the GW many-body corrections to Kohn-Sham eigenenergies and, thus, need to be considered in electronic structure calculations. The temperature dependence of the renormalizations is also considered, and in all materials, the eigenenergy renormalization at the band gap and around the Fermi level increases with increasing temperature.

Pycup – A bifunctional, cage-like ligand for 64Cu radiolabeling

PubMed Central

Boros, Eszter; Rybak-Akimova, Elena; Holland, Jason P.; Rietz, Tyson; Rotile, Nicholas; Blasi, Francesco; Day, Helen; Latifi, Reza; Caravan, Peter

2014-01-01

In developing targeted probes for positron emission tomography (PET) based on 64Cu, stable complexation of the radiometal is key, and a flexible handle for bioconjugation is highly advantageous. Here, we present the synthesis and characterization of the chelator pycup and 4 derivatives. Pycup is a cross-bridged cyclam derivative with a pyridyl donor atom integrated into the cross-bridge resulting in a pentadentate ligand. The pycup platform provides kinetic inertness toward 64Cu de-chelation and offers versatile bioconjugation chemistry. We varied the number and type of additional donor atoms by alkylation of the remaining two secondary amines, providing three model ligands, pycup2A, pycup1A1Bn and pycup2Bn in 3–4 synthetic steps from cyclam. All model copper complexes displayed very slow decomplexation in 5 M HCl and 90 °C (t1/2: 1.5 h for pycup1A1Bn, 2.7 h for pycup2A, 20.3 h for pycup2Bn). The single crystal crystal X-ray structure of the [Cu(pycup2Bn)]2+ complex showed that the copper was coordinated in a trigonal, bi-pyramidal manner. The corresponding radiochemical complexes were at least 94% stable in rat plasma after 24 h. Biodistribution studies conducted in Balb/c mice at 2 h post-injection of 64Cu labeled pycup2A revealed low residual activity in kidney, liver and blood pool with predominantly renal clearance observed. Pycup2A was readily conjugated to a fibrin-targeted peptide and labeled with 64Cu for successful PET imaging of arterial thrombosis in a rat model, demonstrating the utility of our new chelator in vivo. PMID:24294970

Employment of Adaptive Learning Techniques for the Discrimination of Acoustic Emissions.

DTIC Science & Technology

1983-11-01

Dereverberation Simulations ... ............ .. 96 Ŗ 4. ARRAY OPTIMIZATION ......... ...................... . 115 * 4.1 Phased Array Fundamentals... 115 4.2 Phased Array Diffraction Suboptimization ......... ... 121 , .i Page s 4.3 Diffraction Pattern Simulations of Phased Arrays...by differentiating (2.13.14) with respect to z and • -- equating equal powers of z , giving n-i c n bn + I/n kckbn-k (2.13.15)nk= This is very

Temperature Dependence of Raman-Active In-Plane E2g Phonons in Layered Graphene and h-BN Flakes

NASA Astrophysics Data System (ADS)

Li, Xiaoli; Liu, Jian; Ding, Kai; Zhao, Xiaohui; Li, Shuai; Zhou, Wenguang; Liang, Baolai

2018-01-01

Thermal properties of sp2 systems such as graphene and hexagonal boron nitride (h-BN) have attracted significant attention because of both systems being excellent thermal conductors. This research reports micro-Raman measurements on the in-plane E2g optical phonon peaks ( 1580 cm-1 in graphene layers and 1362 cm-1 in h-BN layers) as a function of temperature from - 194 to 200 °C. The h-BN flakes show higher sensitivity to temperature-dependent frequency shifts and broadenings than graphene flakes. Moreover, the thermal effect in the c direction on phonon frequency in h-BN layers is more sensitive than that in graphene layers but on phonon broadening in h-BN layers is similar as that in graphene layers. These results are very useful to understand the thermal properties and related physical mechanisms in h-BN and graphene flakes for applications of thermal devices.

Immune perturbations in HIV–1-infected individuals who make broadly reactive neutralizing antibodies

PubMed Central

Moody, M. Anthony; Pedroza-Pacheco, Isabela; Vandergrift, Nathan A.; Chui, Cecilia; Lloyd, Krissey E.; Parks, Robert; Soderberg, Kelly A.; Ogbe, Ane T.; Cohen, Myron S.; Liao, Hua-Xin; Gao, Feng; McMichael, Andrew J.; Montefiori, David C.; Verkoczy, Laurent; Kelsoe, Garnett; Huang, Jinghe; Shea, Patrick R.; Connors, Mark; Borrow, Persephone; Haynes, Barton F.

2017-01-01

Induction of broadly neutralizing antibodies (bnAbs) is a goal of HIV-1 vaccine development. BnAbs occur in some HIV-1-infected individuals and frequently have characteristics of autoantibodies. Here we have studied cohorts of HIV-1-infected individuals that made bnAbs and compared them to those who did not do so, and determined immune traits associated with the ability to produce bnAbs. HIV-1-infected individuals with bnAbs had a higher frequency of blood autoantibodies, a lower frequency of regulatory CD4+ T cells, a higher frequency of circulating memory T follicular helper CD4+ cells and a higher T regulatory cell level of programmed cell death-1 expression compared to HIV-1-infected individuals without bnAbs. Thus, induction of HIV-1 bnAbs may require vaccination regimens that transiently mimic immunologic perturbations in HIV-1-infected individuals. PMID:28783677

78 FR 38544 - Airworthiness Directives; B-N Group Ltd. Airplanes

Federal Register 2010, 2011, 2012, 2013, 2014

2013-06-27

... Airworthiness Directives; B-N Group Ltd. Airplanes AGENCY: Federal Aviation Administration (FAA), Department of Transportation (DOT). ACTION: Final rule. SUMMARY: We are adopting a new airworthiness directive (AD) for all B-N... adding the following new AD: 2013-13-02 B-N Group Ltd.: Amendment 39-17490; Docket No. FAA-2013- 0314...

A prospective study of the influence of the UPPS model of impulsivity on the co-occurrence of bulimic symptoms and non-suicidal self-injury.

PubMed

Peterson, Claire M; Fischer, Sarah

2012-12-01

Individuals with bulimia nervosa (BN) often report co-morbid symptoms of non suicidal self-injury (NSSI). This study examined the influence of (lack of) perseverance, (lack of) premeditation, sensation seeking, and negative urgency (the tendency to act rashly when experiencing negative affect) on these two behavior patterns. We hypothesized that negative urgency influences vulnerability to multiple maladaptive behavior patterns, thus influencing the co-occurrence of NSSI and BN symptoms. 489 young adult women completed baseline assessments, and 209 completed an eight month follow-up assessment. Structural equation modeling was used to examine the influence of four personality pathways to impulsive behavior simultaneously on both behaviors at baseline, and the incremental predictive utility of traits on both behaviors at eight month follow up. Additionally, we examined the influence of NSSI at baseline on symptoms of BN at follow up, and symptoms of BN at baseline on NSSI at follow up. Negative urgency accounted for significant variance in NSSI and eating pathology. Baseline (lack of) perseverance contributed significantly to binge eating frequency at follow-up, when accounting for baseline symptoms. NSSI at baseline was associated with increased purging at follow-up. Individual differences in impulsivity appear to influence both NSSI and eating pathology. Copyright © 2012 Elsevier Ltd. All rights reserved.

Elasticity and inelasticity of silicon nitride/boron nitride fibrous monoliths.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Smirnov, B. I.; Burenkov, Yu. A.; Kardashev, B. K.

A study is reported on the effect of temperature and elastic vibration amplitude on Young's modulus E and internal friction in Si{sub 3}N{sub 4} and BN ceramic samples and Si{sub 3}N{sub 4}/BN monoliths obtained by hot pressing of BN-coated Si{sub 3}N{sub 4} fibers. The fibers were arranged along, across, or both along and across the specimen axis. The E measurements were carried out under thermal cycling within the 20-600 C range. It was found that high-modulus silicon-nitride specimens possess a high thermal stability; the E(T) dependences obtained under heating and cooling coincide well with one another. The low-modulus BN ceramicmore » exhibits a considerable hysteresis, thus indicating evolution of the defect structure under the action of thermoelastic (internal) stresses. Monoliths demonstrate a qualitatively similar behavior (with hysteresis). This behavior of the elastic modulus is possible under microplastic deformation initiated by internal stresses. The presence of microplastic shear in all the materials studied is supported by the character of the amplitude dependences of internal friction and the Young's modulus. The experimental data obtained are discussed in terms of a model in which the temperature dependences of the elastic modulus and their features are accounted for by both microplastic deformation and nonlinear lattice-atom vibrations, which depend on internal stresses.« less

Chemical Vapor-Deposited Hexagonal Boron Nitride as a Scalable Template for High-Performance Organic Field-Effect Transistors

DOE PAGES

Lee, Tae Hoon; Kim, Kwanpyo; Kim, Gwangwoo; ...

2017-02-27

Organic field-effect transistors have attracted much attention because of their potential use in low-cost, large-area, flexible electronics. High-performance organic transistors require a low density of grain boundaries in their organic films and a decrease in the charge trap density at the semiconductor–dielectric interface for efficient charge transport. In this respect, the role of the dielectric material is crucial because it primarily determines the growth of the film and the interfacial trap density. Here, we demonstrate the use of chemical vapor-deposited hexagonal boron nitride (CVD h-BN) as a scalable growth template/dielectric for high-performance organic field-effect transistors. The field-effect transistors based onmore » C60 films grown on single-layer CVD h-BN exhibit an average mobility of 1.7 cm 2 V –1 s –1 and a maximal mobility of 2.9 cm 2 V –1 s –1 with on/off ratios of 10 7. The structural and morphology analysis shows that the epitaxial, two-dimensional growth of C 60 on CVD h-BN is mainly responsible for the superior charge transport behavior. In conclusion, we believe that CVD h-BN can serve as a growth template for various organic semiconductors, allowing the development of large-area, high-performance flexible electronics.« less

Chemical Vapor-Deposited Hexagonal Boron Nitride as a Scalable Template for High-Performance Organic Field-Effect Transistors

DOE Office of Scientific and Technical Information (OSTI.GOV)

Lee, Tae Hoon; Kim, Kwanpyo; Kim, Gwangwoo

Organic field-effect transistors have attracted much attention because of their potential use in low-cost, large-area, flexible electronics. High-performance organic transistors require a low density of grain boundaries in their organic films and a decrease in the charge trap density at the semiconductor–dielectric interface for efficient charge transport. In this respect, the role of the dielectric material is crucial because it primarily determines the growth of the film and the interfacial trap density. Here, we demonstrate the use of chemical vapor-deposited hexagonal boron nitride (CVD h-BN) as a scalable growth template/dielectric for high-performance organic field-effect transistors. The field-effect transistors based onmore » C60 films grown on single-layer CVD h-BN exhibit an average mobility of 1.7 cm 2 V –1 s –1 and a maximal mobility of 2.9 cm 2 V –1 s –1 with on/off ratios of 10 7. The structural and morphology analysis shows that the epitaxial, two-dimensional growth of C 60 on CVD h-BN is mainly responsible for the superior charge transport behavior. In conclusion, we believe that CVD h-BN can serve as a growth template for various organic semiconductors, allowing the development of large-area, high-performance flexible electronics.« less

High-performance polyimide nanocomposites with core-shell AgNWs@BN for electronic packagings

DOE Office of Scientific and Technical Information (OSTI.GOV)

Zhou, Yongcun; Liu, Feng, E-mail: liufeng@nwpu.edu.cn

2016-08-22

The increasing density of electronic devices underscores the need for efficient thermal management. Silver nanowires (AgNWs), as one-dimensional nanostructures, possess a high aspect ratio and intrinsic thermal conductivity. However, high electrical conductivity of AgNWs limits their application for electronic packaging. We synthesized boron nitride-coated silver nanowires (AgNWs@BN) using a flexible and fast method followed by incorporation into synthetic polyimide (PI) for enhanced thermal conductivity and dielectric properties of nanocomposites. The thinner boron nitride intermediate nanolayer on AgNWs not only alleviated the mismatch between AgNWs and PI but also enhanced their interfacial interaction. Hence, the maximum thermal conductivity of an AgNWs@BN/PImore » composite with a filler loading up to 20% volume was increased to 4.33 W/m K, which is an enhancement by nearly 23.3 times compared with that of the PI matrix. The relative permittivity and dielectric loss were about 9.89 and 0.015 at 1 MHz, respectively. Compared with AgNWs@SiO{sub 2}/PI and Ag@BN/PI composites, boron nitride-coated core-shell structures effectively increased the thermal conductivity and reduced the permittivity of nanocomposites. The relative mechanism was studied and discussed. This study enables the identification of appropriate modifier fillers for polymer matrix nanocomposites.« less

On the fluctuations of sums of independent random variables.

PubMed

Feller, W

1969-07-01

If X(1), X(2),... are independent random variables with zero expectation and finite variances, the cumulative sums S(n) are, on the average, of the order of magnitude S(n), where S(n) (2) = E(S(n) (2)). The occasional maxima of the ratios S(n)/S(n) are surprisingly large and the problem is to estimate the extent of their probable fluctuations.Specifically, let S(n) (*) = (S(n) - b(n))/a(n), where {a(n)} and {b(n)}, two numerical sequences. For any interval I, denote by p(I) the probability that the event S(n) (*) epsilon I occurs for infinitely many n. Under mild conditions on {a(n)} and {b(n)}, it is shown that p(I) equals 0 or 1 according as a certain series converges or diverges. To obtain the upper limit of S(n)/a(n), one has to set b(n) = +/- epsilon a(n), but finer results are obtained with smaller b(n). No assumptions concerning the under-lying distributions are made; the criteria explain structurally which features of {X(n)} affect the fluctuations, but for concrete results something about P{S(n)>a(n)} must be known. For example, a complete solution is possible when the X(n) are normal, replacing the classical law of the iterated logarithm. Further concrete estimates may be obtained by combining the new criteria with some recently developed limit theorems.

Wetting Behavior and Reactivity of Molten Silicon with h-BN Substrate at Ultrahigh Temperatures up to 1750 °C

NASA Astrophysics Data System (ADS)

Polkowski, Wojciech; Sobczak, Natalia; Nowak, Rafał; Kudyba, Artur; Bruzda, Grzegorz; Polkowska, Adelajda; Homa, Marta; Turalska, Patrycja; Tangstad, Merete; Safarian, Jafar; Moosavi-Khoonsari, Elmira; Datas, Alejandro

2017-12-01

For a successful implementation of newly proposed silicon-based latent heat thermal energy storage systems, proper ceramic materials that could withstand a contact heating with molten silicon at temperatures much higher than its melting point need to be developed. In this regard, a non-wetting behavior and low reactivity are the main criteria determining the applicability of ceramic as a potential crucible material for long-term ultrahigh temperature contact with molten silicon. In this work, the wetting of hexagonal boron nitride (h-BN) by molten silicon was examined for the first time at temperatures up to 1750 °C. For this purpose, the sessile drop technique combined with contact heating procedure under static argon was used. The reactivity in Si/h-BN system under proposed conditions was evaluated by SEM/EDS examinations of the solidified couple. It was demonstrated that increase in temperature improves wetting, and consequently, non-wetting-to-wetting transition takes place at around 1650 °C. The contact angle of 90° ± 5° is maintained at temperatures up to 1750 °C. The results of structural characterization supported by a thermodynamic modeling indicate that the wetting behavior of the Si/h-BN couple during heating to and cooling from ultrahigh temperature of 1750 °C is mainly controlled by the substrate dissolution/reprecipitation mechanism.

Binge Eating, Purging, or Both: Eating Disorder Psychopathology Findings from an Internet Community Survey

PubMed Central

Roberto, Christina A.; Grilo, Carlos M.; Masheb, Robin M.; White, Marney A.

2010-01-01

Objective This study aimed to compare bulimia nervosa (BN), binge eating disorder (BED), and purging disorder (PD) on clinically significant variables and examine the utility of once versus twice-weekly diagnostic thresholds for disturbed eating behaviors. Method 234 women with BN, BED, or PD were identified through self-report measures via an online survey and categorized based on either once-weekly or twice-weekly disturbed eating behaviors. Results BN emerged as a more severe disorder than BED and PD. The three groups differed significantly in self-reported restraint and disinhibition and the BN and BED groups reported higher levels of depression than PD. For BN, those engaging in behaviors twice-weekly versus once-weekly were more symptomatic. Discussion The BN, BED, and PD groups differed in clinically meaningful ways. Future research need to clarify the relationship between mood disturbances and eating behaviors. Reducing the twice-weekly behavior threshold for BN would capture individuals with clinically significant eating disorders, though the twice-weekly threshold may provide important information about disorder severity for both BN and BED. PMID:19862702

What Are the Primary Limitations in B-Cell Affinity Maturation, and How Much Affinity Maturation Can We Drive with Vaccination? Breaking through Immunity's Glass Ceiling.

PubMed

Kelsoe, Garnett; Haynes, Barton F

2018-05-01

A key goal of HIV-1 vaccine development is the induction of broadly neutralizing antibodies (bnAbs) targeted to the vulnerable regions of the HIV envelope. BnAbs develop over time in ∼50% of HIV-1-infected individuals. However, to date, no vaccines have induced bnAbs and few or none of these vaccine-elicited HIV-1 antibodies carry the high frequencies of V(D)J mutations characteristic of bnAbs. Do the high frequencies of mutations characteristic of naturally induced bnAbs represent a fundamental barrier to the induction of bnAbs by vaccines? Recent studies suggest that high frequencies of V(D)J mutations can be achieved by serial vaccination strategies. Rather, it appears that, in the absence of HIV-1 infection, physiologic immune tolerance controls, including a germinal center process termed affinity reversion, may limit vaccine-driven bnAb development by clonal elimination or selecting for mutations incompatible with bnAb activity. Copyright © 2018 Cold Spring Harbor Laboratory Press; all rights reserved.

Synthesis of large-area multilayer hexagonal boron nitride for high material performance.

PubMed

Kim, Soo Min; Hsu, Allen; Park, Min Ho; Chae, Sang Hoon; Yun, Seok Joon; Lee, Joo Song; Cho, Dae-Hyun; Fang, Wenjing; Lee, Changgu; Palacios, Tomás; Dresselhaus, Mildred; Kim, Ki Kang; Lee, Young Hee; Kong, Jing

2015-10-28

Although hexagonal boron nitride (h-BN) is a good candidate for gate-insulating materials by minimizing interaction from substrate, further applications to electronic devices with available two-dimensional semiconductors continue to be limited by flake size. While monolayer h-BN has been synthesized on Pt and Cu foil using chemical vapour deposition (CVD), multilayer h-BN is still absent. Here we use Fe foil and synthesize large-area multilayer h-BN film by CVD with a borazine precursor. These films reveal strong cathodoluminescence and high mechanical strength (Young's modulus: 1.16 ± 0.1 TPa), reminiscent of formation of high-quality h-BN. The CVD-grown graphene on multilayer h-BN film yields a high carrier mobility of ∼ 24,000 cm(2) V(-1) s(-1) at room temperature, higher than that (∼ 13,000 (2) V(-1) s(-1)) with exfoliated h-BN. By placing additional h-BN on a SiO2/Si substrate for a MoS2 (WSe2) field-effect transistor, the doping effect from gate oxide is minimized and furthermore the mobility is improved by four (150) times.

Temperature-triggered chemical switching growth of in-plane and vertically stacked graphene-boron nitride heterostructures

PubMed Central

Gao, Teng; Song, Xiuju; Du, Huiwen; Nie, Yufeng; Chen, Yubin; Ji, Qingqing; Sun, Jingyu; Yang, Yanlian; Zhang, Yanfeng; Liu, Zhongfan

2015-01-01

In-plane and vertically stacked heterostructures of graphene and hexagonal boron nitride (h-BN-G and G/h-BN, respectively) are both recent focuses of graphene research. However, targeted synthesis of either heterostructure remains a challenge. Here, via chemical vapour deposition and using benzoic acid precursor, we have achieved the selective growth of h-BN-G and G/h-BN through a temperature-triggered switching reaction. The perfect in-plane h-BN-G is characterized by scanning tunnelling microscopy (STM), showing atomically patched graphene and h-BN with typical zigzag edges. In contrast, the vertical alignment of G/h-BN is confirmed by unique lattice-mismatch-induced moiré patterns in high-resolution STM images, and two sets of aligned selected area electron diffraction spots, both suggesting a van der Waals epitaxial mechanism. The present work demonstrates the chemical designability of growth process for controlled synthesis of graphene and h-BN heterostructures. With practical scalability, high uniformity and quality, our approach will promote the development of graphene-based electronics and optoelectronics. PMID:25869236

Vibrational Properties of h-BN and h-BN-Graphene Heterostructures Probed by Inelastic Electron Tunneling Spectroscopy

PubMed Central

Jung, Suyong; Park, Minkyu; Park, Jaesung; Jeong, Tae-Young; Kim, Ho-Jong; Watanabe, Kenji; Taniguchi, Takashi; Ha, Dong Han; Hwang, Chanyong; Kim, Yong-Sung

2015-01-01

Inelastic electron tunneling spectroscopy is a powerful technique for investigating lattice dynamics of nanoscale systems including graphene and small molecules, but establishing a stable tunnel junction is considered as a major hurdle in expanding the scope of tunneling experiments. Hexagonal boron nitride is a pivotal component in two-dimensional Van der Waals heterostructures as a high-quality insulating material due to its large energy gap and chemical-mechanical stability. Here we present planar graphene/h-BN-heterostructure tunneling devices utilizing thin h-BN as a tunneling insulator. With much improved h-BN-tunneling-junction stability, we are able to probe all possible phonon modes of h-BN and graphite/graphene at Γ and K high symmetry points by inelastic tunneling spectroscopy. Additionally, we observe that low-frequency out-of-plane vibrations of h-BN and graphene lattices are significantly modified at heterostructure interfaces. Equipped with an external back gate, we can also detect high-order coupling phenomena between phonons and plasmons, demonstrating that h-BN-based tunneling device is a wonderful playground for investigating electron-phonon couplings in low-dimensional systems. PMID:26563740

Vibrational Properties of h-BN and h-BN-Graphene Heterostructures Probed by Inelastic Electron Tunneling Spectroscopy.

PubMed

Jung, Suyong; Park, Minkyu; Park, Jaesung; Jeong, Tae-Young; Kim, Ho-Jong; Watanabe, Kenji; Taniguchi, Takashi; Ha, Dong Han; Hwang, Chanyong; Kim, Yong-Sung

2015-11-13

Inelastic electron tunneling spectroscopy is a powerful technique for investigating lattice dynamics of nanoscale systems including graphene and small molecules, but establishing a stable tunnel junction is considered as a major hurdle in expanding the scope of tunneling experiments. Hexagonal boron nitride is a pivotal component in two-dimensional Van der Waals heterostructures as a high-quality insulating material due to its large energy gap and chemical-mechanical stability. Here we present planar graphene/h-BN-heterostructure tunneling devices utilizing thin h-BN as a tunneling insulator. With much improved h-BN-tunneling-junction stability, we are able to probe all possible phonon modes of h-BN and graphite/graphene at Γ and K high symmetry points by inelastic tunneling spectroscopy. Additionally, we observe that low-frequency out-of-plane vibrations of h-BN and graphene lattices are significantly modified at heterostructure interfaces. Equipped with an external back gate, we can also detect high-order coupling phenomena between phonons and plasmons, demonstrating that h-BN-based tunneling device is a wonderful playground for investigating electron-phonon couplings in low-dimensional systems.

Preparation and Characterization of Ni Spines Grown on the Surface of Cubic Boron Nitride Grains by Electroplating Method

PubMed Central

Gui, Yanghai; Zhao, Jianbo; Chen, Jingbo; Jiang, Yuanli

2016-01-01

Cubic boron nitride (cBN) is widely applied in cutting and grinding tools. cBN grains plated by pure Ni and Ni/SiC composite were produced under the same conditions from an additive-free nickel Watts type bath. The processed electroplating products were characterized by the techniques of scanning electron microscopy (SEM), X-ray diffraction (XRD) and thermoanalysis (TG-DTA). Due to the presence of SiC particles, there are some additional nodules on the surface of Ni/SiC plated cBN compared with the pure Ni plated cBN. The unique morphology of Ni/SiC plated cBN should attain greater retention force in resin bond. Moreover, the coating weight of cBN grains could be controlled by regulating the plating time. cBN grains with 60% coating weight possess the optimum grinding performance due to their roughest and spiniest surface. In addition, Ni spines plated cBN grains show good thermal stability when temperature is lower than 464 °C. Therefore, the plated cBN grains are more stable and suitable for making resin bond abrasive tools below 225 °C. Finally, the formation mechanism of electroplating products is also discussed. PMID:28773283

Nickel cobaltite nanosheets strongly anchored on boron and nitrogen co-doped graphene for high-performance asymmetric supercapacitors

NASA Astrophysics Data System (ADS)

Jiao, Xinyan; Xia, Xifeng; Liu, Peng; Lei, Wu; Ouyang, Yu; Hao, Qingli

2017-08-01

Strongly coupled boron and nitrogen co-doped graphene (BN-G) hybrids with nickel cobaltite (NiCo2O4) nanosheets (NCO/BN-G) were fabricated by a facile soft-chemical method for asymmetric supercapacitors with high-performance. The strong interaction between BN-G and NiCo2O4 nanosheets are explored by various techniques. The effect of heteroatom doping on electrochemical properties of the hybrids is systematically investigated. The strong synergistic effect between NiCo2O4 and BN-G leads to a specific capacitance of 106.5 mA h g-1 at the current density of 0.5 A g-1 and capacitance retention of 96.8% after 10 000 cycles at 5 A g-1, much better than those of the pure NiCo2O4 and its hybrid with N-doped graphene. Moreover, an asymmetric supercapacitor device, assembled with NCO/BN-G and activated carbon (NCO/BN-G//AC), exhibits a maximum energy density of 45.6 Wh kg-1 and an excellent cycling stability. The improved electrochemical performance of the NCO/BN-G hybrid is attributed to the good conductivity of BN-G and the synergistic effect between NiCo2O4 nanosheets and BN-G combined together through a plane-to-plane contact mode.

Bulimia nervosa: friend or foe? The pros and cons of bulimia nervosa.

PubMed

Serpell, Lucy; Treasure, Janet

2002-09-01

The aim of the current study was to use a qualitative approach to investigate the attitude of people with bulimia nervosa (BN) to their illness. Patients with BN were asked to write two letters to their bulimia, one addressing it as a friend and the other addressing it as an enemy. We used a coding scheme to classify themes in letters of people with anorexia nervosa (AN) to group together themes expressed by those with BN. We revised the coding scheme to include themes that were not present in the letters of people with AN. There were both similarities and differences in the themes described by AN and BN patients. Two positive themes (BN allowing the individuals to eat and not get fat and BN as a way of dealing with boredom) and two negative themes (shame or low self-esteem resulting from BN and obsessive thoughts of weight and shape) were added to the coding scheme to account for these differences. The positive and negative aspects of BN differ in some important ways from those expressed by patients with AN. The meaning of these differences is discussed with reference to the wider symptom pattern of BN compared with AN and their importance with reference to motivation for change is outlined. Copyright 2002 by Wiley Periodicals, Inc.

Multilayer Regulation of Atomic Boron Nitride Films to Improve Oxidation and Corrosion Resistance of Cu.

PubMed

Ren, Siming; Cui, Mingjun; Pu, Jibin; Xue, Qunji; Wang, Liping

2017-08-16

The boron nitride (BN) monolayer (1L) with high impermeability and resistivity seems to hold promise as a long-term corrosion barrier for Cu under ambient condition, which is supported by recent researches. Here, we perform a complete study of the alternating temperature tests (the sample is exposed in air for 30 days and subsequently heated at 200 °C for 2 h) and electrochemical measurements on 1L and multilayer BN-coated Cu foils. Results imply that the BN-coated Cu foils are less oxidized than uncoated Cu foils after alternating temperature tests, regardless of the layers of BN. Particularly, the oxidation process proceeds slowly in multilayers because most of the underlying defects are covered with BN layers to suppress the oxygen diffusion in the vertical direction and the oxidation mainly occurs on the wrinkled region of BN films. Electrochemical analyses reveal that the BN layers provide an effective physical barrier against the corrosive medium and inhibit the electron diffusion because of their high electrical insulating behavior and the corrosion resistance of the samples increases with increasing BN layers. These findings indicate that BN films with adequate layers are good candidates for oxidation and corrosion protection at the atomic level, which is vital to many industrial and academic applications.

A twin study of specific bulimia nervosa symptoms.

PubMed

Mazzeo, S E; Mitchell, K S; Bulik, C M; Aggen, S H; Kendler, K S; Neale, M C

2010-07-01

Twin studies have suggested that additive genetic factors significantly contribute to liability to bulimia nervosa (BN). However, the diagnostic criteria for BN remain controversial. In this study, an item-factor model was used to examine the BN diagnostic criteria and the genetic and environmental contributions to BN in a population-based twin sample. The validity of the equal environment assumption (EEA) for BN was also tested. Participants were 1024 female twins (MZ n=614, DZ n=410) from the population-based Mid-Atlantic Twin Registry. BN was assessed using symptom-level (self-report) items consistent with DSM-IV and ICD-10 diagnostic criteria. Items assessing BN were included in an item-factor model. The EEA was measured by items assessing similarity of childhood and adolescent environment, which have demonstrated construct validity. Scores on the EEA factor were used to specify the degree to which twins shared environmental experiences in this model. The EEA was not violated for BN. Modeling results indicated that the majority of the variance in BN was due to additive genetic factors. There was substantial variability in additive genetic and environmental contributions to specific BN symptoms. Most notably, vomiting was very strongly influenced by additive genetic factors, while other symptoms were much less heritable, including the influence of weight on self-evaluation. These results highlight the importance of assessing eating disorders at the symptom level. Refinement of eating disorder phenotypes could ultimately lead to improvements in treatment and targeted prevention, by clarifying sources of variation for specific components of symptomatology.

Controlled Gas Exfoliation of Boron Nitride into Few-Layered Nanosheets

DOE PAGES

Zhu, Wenshuai; Gao, Xiang; Li, Qian; ...

2016-07-22

The controlled exfoliation of hexagonal boron nitride (h-BN) into single- or few-layered nanosheets remains a grand challenge and becomes the bottleneck to essential studies and applications of h-BN. Here, we present an efficient strategy for the scalable synthesis of few-layered h-BN nanosheets (BNNS) via a novel gas exfoliation of bulk h-BN in liquid N 2 (L-N 2). The essence of this strategy lies in the combination of a high temperature triggered expansion of bulk h-BN and the cryogenic L-N 2 gasification to exfoliate the h-BN. The produced BNNS after ten cycles (BNNS-10) consisted primarily of fewer than five atomic layersmore » with high a mass yield of 16~20%. N 2 sorption and desorption isotherms show that the BNNS-10 exhibited a much higher specific surface area of 278 m 2/g –1 than that of bulk BN (10 m 2/g –1). Through the investigation of the exfoliated intermediates combined with a theoretical calculation, we found that the huge temperature variation initiates the expansion and curling of the bulk h-BN. Subseqently, the L-N 2 penetrates into the interlayers of h-BN along the curling edge, followed by an immediate drastic gasification of L-N 2, further peeling off h-BN. In conclusion, this novel gas exfoliation of high surface area BNNS not only opens up potential opportunities for wide applications, but also can be extended to produce other layered materials with high yeilds.« less

Association of Betel Nut with Carcinogenesis: Revisit with a Clinical Perspective

PubMed Central

Sharan, Rajeshwar N.; Mehrotra, Ravi; Choudhury, Yashmin; Asotra, Kamlesh

2012-01-01

Abstract Betel nut (BN), betel quid (BQ) and products derived from them are widely used as a socially endorsed masticatory product. The addictive nature of BN/BQ has resulted in its widespread usage making it the fourth most abused substance by humans. Progressively, several additives, including chewing tobacco, got added to simple BN preparations. This addictive practice has been shown to have strong etiological correlation with human susceptibility to cancer, particularly oral and oropharyngeal cancers. The PUBMED database was searched to retrieve all relevant published studies in English on BN and BQ, and its association with oral and oropharyngeal cancers. Only complete studies directly dealing with BN/BQ induced carcinogenesis using statistically valid and acceptable sample size were analyzed. Additional relevant information available from other sources was also considered. This systematic review attempts to put in perspective the consequences of this widespread habit of BN/BQ mastication, practiced by approximately 10% of the world population, on oral cancer with a clinical perspective. BN/BQ mastication seems to be significantly associated with susceptibility to oral and oropharyngeal cancers. Addition of tobacco to BN has been found to only marginally increase the cancer risk. Despite the widespread usage of BN/BQ and its strong association with human susceptibility to cancer, no serious strategy seems to exist to control this habit. The review, therefore, also looks at various preventive efforts being made by governments and highlights the multifaceted intervention strategies required to mitigate and/or control the habit of BN/BQ mastication. PMID:22912735

Reduced Inferior and Orbital Frontal Thickness in Adolescent Bulimia Nervosa Persists Over Two-Year Follow-Up.

PubMed

Cyr, Marilyn; Kopala-Sibley, Daniel C; Lee, Seonjoo; Chen, Chen; Stefan, Mihaela; Fontaine, Martine; Terranova, Kate; Berner, Laura A; Marsh, Rachel

2017-10-01

Cross-sectional data suggest functional and anatomical disturbances in inferior and orbital frontal regions in bulimia nervosa (BN). Using longitudinal data, we investigated whether reduced cortical thickness (CT) in these regions arises early and persists over adolescence in BN, independent of symptom remission, and whether CT reductions are markers of BN symptoms. A total of 33 adolescent females with BN symptoms (BN or other specified feeding or eating disorder) and 28 healthy adolescents participated in this study. Anatomical magnetic resonance imaging and clinical data were acquired at 3 time points within 2-year intervals over adolescence, with 31% average attrition between assessments. Using a region-of-interest approach, we assessed group differences in CT at baseline and over time, and tested whether between- and within-subject variations in CT were associated with the frequency of BN symptoms. Reduced CT in the right inferior frontal gyrus persisted over adolescence in BN compared to healthy adolescents, even in those who achieved full or partial remission. Within the BN group, between-subject variations in CT in the inferior and orbital frontal regions were inversely associated with specific BN symptoms, suggesting, on average over time, greater CT reductions in individuals with more frequent BN symptoms. Reduced CT in inferior frontal regions may contribute to illness persistence into adulthood. Reductions in the thickness of the inferior and orbital frontal regions may be markers of specific BN symptoms. Because our sample size precluded correcting for multiple comparisons, these findings should be replicated in a larger sample. Future study of functional changes in associated fronto-striatal circuits could identify potential circuit-based intervention targets. Copyright © 2017 American Academy of Child and Adolescent Psychiatry. Published by Elsevier Inc. All rights reserved.

Pharmacogenomic Strain Differences in Cardiovascular Sensitivity to Propofol

PubMed Central

Stekiel, Thomas A.; Contney, Stephen J.; Roman, Richard J.; Weber, Craig A.; Stadnicka, Anna; Bosnjak, Zeljko J.; Greene, Andrew S; Moreno, Carol

2011-01-01

Introduction A pharmacogenomic approach was used to further localize the genetic region responsible for previously observed enhanced cardiovascular sensitivity to propofol in Dahl Salt Sensitive (SS) vs. control Brown Norway (BN) rats. Methods Propofol infusion levels that decreased blood pressure by 50% were measured in BN.13SS rats (substitution of SS chromosome 13 into BN) and in 5 congenic (partial substitution) strains of SS.13BN. The effect of superfused 2,6 diisopropylphenol on small mesenteric arterial vascular smooth muscle transmembrane potential was measured in congenic strains before and during superfusion with Rp-cAMPS and Rp-8-pCPT-cGMPS, inhibitors of protein kinase A and G respectively. The genetic locus and potential role of the renin gene in mediating VSM sensitivity to propofol were determined in three selected sub-congenic SS.BN13 strains. Results A 30 – 32% smaller propofol infusion rate reduced blood pressure by 50% in BN.13SS compared to BN and the SS.13BN congenic containing a 80 BN gene substitution. Compared to the latter, SS exhibited greater protein kinase A dependent vascular smooth muscle hyperpolarization in response to propofol. Using sub-congenics, the increased propofol-induced cardiovascular sensitivity and hyperpolarization was further localized to an 8-gene region (containing the BN renin gene). Blockade of angiotensin (AT1) receptors with losartan in this sub-congenic, elevated propofol-induced hyperpolarization by 3 fold, to that observed in SS. Conclusions Enhanced cardiovascular sensitivity to propofol in SS (compared to BN) is caused by an altered renin gene. Through modified second messenger function, this differentially regulates VSM contractile state and reduces vascular tone exacerbating cardiovascular depression by propofol. PMID:22020141

High Temperature Si-doped BN Interphases for Woven SiC/SiC Composites

NASA Technical Reports Server (NTRS)

Morscher, Gregory N.; Hurwitz, Frances; Yun, Hee Mann; Gray, Hugh R. (Technical Monitor)

2002-01-01

The hydrolytic stability of high-temperature deposited Si-doped BN has been shown in the past to be superior in comparison to "pure" BN processed at similar or even higher temperatures. This type of material would be very desirable as a SiC/SiC composite interphase that is formed by chemical infiltration into multi-ply woven preform. However, due to rapid deposition on the preform outer surface at the high processing temperature, this has proven very difficult. To overcome this issue, single plies of woven fabric were infiltrated with Si-doped BN. Three composite panels of different SiC fiber types were fabricated with Si-doped BN interphases including Sylramic, Hi-Nicalon Type S and Sylramic-iBN fiber-types. The latter fiber-type possesses a thin in-situ grown BN layer on the fiber surface. High Si contents (approx. 7 to 10 a/o) and low oxygen contents (less than 1 a/o) were achieved. All three composite systems demonstrated reasonable debonding and sliding properties. The coated Sylramic fabric and composites were weak due to fiber degradation apparently caused during interphase processing by the formation of TiN crystals on the fiber surface. The Hi-Nicalon Type S composites with Si-doped BN interphase were only slightly weaker than Hi-Nicalon Type S composites with conventional BN when the strength on the load-bearing fibers at failure was compared. On the other hand, the Sylramic-iBN fabric and composites with Si-doped BN showed excellent composite and intermediate temperature stress-rupture properties. Most impressive was the lack of any significant interphase oxidation on the fracture surface of stress-ruptured specimens tested well above matrix cracking at 815C.

The prevalence and correlates of binge eating disorder in the WHO World Mental Health Surveys

PubMed Central

Kessler, Ronald C.; Berglund, Patricia A.; Chiu, Wai Tat; Deitz, Anne C.; Hudson, James I.; Shahly, Victoria; Aguilar-Gaxiola, Sergio; Alonso, Jordi; Angermeyer, Matthias C.; Benjet, Corina; Bruffaerts, Ronny; de Girolamo, Giovanni; de Graaf, Ron; Haro, Josep Maria; Kovess-Masfety, Viviane; O’Neill, Siobhan; Posada-Villa, Jose; Sasu, Carmen; Scott, Kate; Viana, Maria Carmen; Xavier, Miguel

2013-01-01

Background Little population-based data exist outside the United States on the epidemiology of binge eating disorder (BED). Cross-national data on BED are presented and compared to bulimia nervosa (BN) based on the WHO World Mental Health Surveys. Methods Community surveys with 24,124 respondents (ages 18+) across 14 mostly upper-middle and high income countries assessed lifetime and 12-month DSM-IV mental disorders with the WHO Composite International Diagnostic Interview. Physical disorders were assessed with a chronic conditions checklist. Results Country-specific lifetime prevalence estimates are consistently (median; inter-quartile range) higher for BED (1.4%;0.8–1.9%) than BN (0.8%;0.4–1.0%). Median age-of-onset is in the late teens to early 20s for both disorders but slightly younger for BN. Persistence is slightly higher for BN (6.5 years; 2.2–15.4) than BED (4.3 years; 1.0–11.7). Lifetime risk of both disorders is elevated for women and recent cohorts. Retrospective reports suggest that comorbid anxiety, mood, and disruptive behavior disorders predict subsequent onset of BN somewhat more strongly than BED and that BN predicts subsequent comorbid psychiatric disorders somewhat more strongly than does BED. Significant comorbidities with physical conditions are due almost entirely to BN and BED predicting subsequent onset of these conditions, again with BN somewhat stronger than BED. Role impairments are similar for BN and BED. Fewer than half of lifetime BN or BED cases receive treatment. Conclusions BED represents a public health problem at least equal to BN. Low treatment rates highlight the clinical importance of questioning patients about eating problems even when not included among presenting complaints. PMID:23290497

Study of Structural, Optical and Electrical Properties of InAs/InAsSb Superlattices Using Multiple Characterization Techniques

NASA Astrophysics Data System (ADS)

Shen, Xiaomeng

InAs/InAsSb type-II superlattices (T2SLs) can be considered as potential alternatives for conventional HgCdTe photodetectors due to improved uniformity, lower manufacturing costs with larger substrates, and possibly better device performance. This dissertation presents a comprehensive study on the structural, optical and electrical properties of InAs/InAsSb T2SLs grown by Molecular Beam Epitaxy. The effects of different growth conditions on the structural quality were thoroughly investigated. Lattice-matched condition was successfully achieved and material of exceptional quality was demonstrated. After growth optimization had been achieved, structural defects could hardly be detected, so different characterization techniques, including etch-pit-density (EPD) measurements, cathodoluminescence (CL) imaging and X-ray topography (XRT), were explored, in attempting to gain better knowledge of the sparsely distributed defects. EPD revealed the distribution of dislocation-associated pits across the wafer. Unfortunately, the lack of contrast in images obtained by CL imaging and XRT indicated their inability to provide any quantitative information about defect density in these InAs/InAsSb T2SLs. The nBn photodetectors based on mid-wave infrared (MWIR) and long-wave infrared (LWIR) InAs/InAsSb T2SLs were fabricated. The significant difference in Ga composition in the barrier layer coupled with different dark current behavior, suggested the possibility of different types of band alignment between the barrier layers and the absorbers. A positive charge density of 1.8 x 1017/cm3 in the barrier of MWIR nBn photodetector, as determined by electron holography, confirmed the presence of a potential well in its valence band, thus identifying type-II alignment. In contrast, the LWIR nBn photodetector was shown to have type-I alignment because no sign of positive charge was detected in its barrier. Capacitance-voltage measurements were performed to investigate the temperature dependence of carrier densities in a metal-oxide-semiconductor (MOS) structure based on MWIR InAs/InAsSb T2SLs, and a nBn structure based on LWIR InAs/InAsSb T2SLs. No carrier freeze-out was observed in either sample, indicating very shallow donor levels. The decrease in carrier density when temperature increased was attributed to the increased density of holes that had been thermally excited from localized states near the oxide/semiconductor interface in the MOS sample. No deep-level traps were revealed in deep-level transient spectroscopy temperature scans.

BnLATE, a Cys2/His2-Type Zinc-Finger Protein, Enhances Silique Shattering Resistance by Negatively Regulating Lignin Accumulation in the Silique Walls of Brassica napus

PubMed Central

Tao, Zhangsheng; Huang, Yi; Zhang, Lida; Wang, Xinfa; Liu, Guihua; Wang, Hanzhong

2017-01-01

Silique shattering resistance is one of the most important agricultural traits in oil crop breeding. Seed shedding from siliques prior to and during harvest causes devastating losses in oilseed yield. Lignin biosynthesis in the silique walls is thought to affect silique-shattering resistance in oil crops. Here, we identified and characterized B. napus LATE FLOWERING (BnLATE), which encodes a Cys2/His2-type zinc-finger protein. Heterologous expression of BnLATE under the double enhanced CaMV 35S promoter (D35S) in wild-type Arabidopsis plants resulted in a marked decrease in lignification in the replum, valve layer (carpel) and dehiscence zone. pBnLATE::GUS activity was strong in the yellowing silique walls of transgenic lines. Furthermore, the expression pattern of BnLATE and the lignin content gradient in the silique walls at 48 days after pollination (DAP) of 73290, a B. napus silique shattering-resistant line, are similar to those in transgenic Arabidopsis lines expressing BnLATE. Transcriptome sequencing of the silique walls revealed that genes encoding peroxidases, which polymerize monolignols and lignin in the phenylpropanoid pathway, were down-regulated at least two-fold change in the D35S::BnLATE transgenic lines. pBnLATE::BnLATE transgenic lines were further used to identify the function of BnLATE, and the results showed that lignification in the carpel and dehiscence zone of yellowing silique also remarkably decreased compared with the wild-type control, the silique shattering-resistance and expression pattern of peroxidase genes are very similar to results with D35S::BnLATE. These results suggest that BnLATE is a negative regulator of lignin biosynthesis in the yellowing silique walls, and promotes silique-shattering resistance in B. napus through restraining the polymerization of monolignols and lignin. PMID:28081140

Capacity of Broadly Neutralizing Antibodies to Inhibit HIV-1 Cell-Cell Transmission Is Strain- and Epitope-Dependent

PubMed Central

Reh, Lucia; Magnus, Carsten; Schanz, Merle; Weber, Jacqueline; Uhr, Therese; Rusert, Peter; Trkola, Alexandra

2015-01-01

An increasing number of broadly neutralizing antibodies (bnAbs) are considered leads for HIV-1 vaccine development and novel therapeutics. Here, we systematically explored the capacity of bnAbs to neutralize HIV-1 prior to and post-CD4 engagement and to block HIV-1 cell-cell transmission. Cell-cell spread is known to promote a highly efficient infection with HIV-1 which can inflict dramatic losses in neutralization potency compared to free virus infection. Selection of bnAbs that are capable of suppressing HIV irrespective of the transmission mode therefore needs to be considered to ascertain their in vivo activity in therapeutic use and vaccines. Employing assay systems that allow for unambiguous discrimination between free virus and cell-cell transmission to T cells, we probed a panel of 16 bnAbs for their activity against 11 viruses from subtypes A, B and C during both transmission modes. Over a wide range of bnAb-virus combinations tested, inhibitory activity against HIV-1 cell-cell transmission was strongly decreased compared to free virus transmission. Activity loss varied considerably between virus strains and was inversely associated with neutralization of free virus spread for V1V2- and V3-directed bnAbs. In rare bnAb-virus combinations, inhibition for both transmission modes was comparable but no bnAb potently blocked cell-cell transmission across all probed virus strains. Mathematical analysis indicated an increased probability of bnAb resistance mutations to arise in cell-cell rather than free virus spread, further highlighting the need to block this pathway. Importantly, the capacity to efficiently neutralize prior to CD4 engagement correlated with the inhibition efficacy against free virus but not cell-cell transmitted virus. Pre-CD4 attachment activity proved strongest amongst CD4bs bnAbs and varied substantially for V3 and V1V2 loop bnAbs in a strain-dependent manner. In summary, bnAb activity against divergent viruses varied depending on the transmission mode and differed depending on the window of action during the entry process, underscoring that powerful combinations of bnAbs are needed for in vivo application. PMID:26158270

Nanotubes from Inorganic Materials

NASA Astrophysics Data System (ADS)

Tenne, Reshef; Zettl, Alex K.

The inorganic analogs of carbon fullerenes and nanotubes, like MoS2 and BN, are reviewed. It is argued that nanoparticles of 2D layered compounds are inherently unstable in the planar configuration and prefer to form closed cage structures. The progress in the synthesis of these nanomaterials, and, in particular, the large-scale synthesis of BN, WS2 and V2O5 nanotubes, are described. Some of the electronic, optical and mechanical properties of these nanostructures are reviewed. The red-shift of the energy gap with shrinking nanotube diameter is discussed as well as the suggestion that zigzag nanotubes exhibit a direct gap rather than an indirect gap, as is prevalent in many of the bulk 2D materials. Some potential applications of these nanomaterials are presented as well, most importantly the superior tribological properties of WS2 and MoS2 nested fullerene-like structures (onions).

Wear Resistance of Austempered Ductile Iron with Nanosized Additives

NASA Astrophysics Data System (ADS)

Kaleicheva, J. K.; Mishev, V.

2018-01-01

The wear resistance, microstructure and mechanical properties of austempered ductile iron (ADI) with nanosized additives of cubic boron nitride cBN are investigated. Samples of ductile iron are put under austhempering at the following conditions: heating at 900°С, 1 h and isothermal retention at 280оС, 2 h and 380°С, 2 h with the aim to achieve a lower bainitic structure and an upper bainitic structure. The experimental wear testing of austempered ductile irons is performed in friction conditions of a fixed abrasive by a cinematic scheme „pin - disc” using an accelerated testing method and device. The microstructure of the ADI is investigated by metallographic and X-Ray analyses. The Vickers hardness testing and impact strength examination are carried out. The influence of the nanosized additives of cBN on the wear resistance, microstructure, impact strength and hardness of the ADI is investigated.

BN-C Hybrid Nanoribbons as Gas Sensors

NASA Astrophysics Data System (ADS)

Darvishi Gilan, Mahdi; Chegel, Raad

2018-02-01

The effects of carbon monoxide (CO) and ammonia (NH3) molecules adsorption on the various composites of boron nitride and graphene BN-C hybrid nanoribbons are investigated using the non-equilibrium Green's function (NEGF) technique based on density functional theory (DFT). The effects of adsorption with possible random configurations on the average of the density of states (DOS), transmission coefficient, and the current-voltage ( I- V) characteristics are calculated. The results indicate that, by embedding armchair graphene nanoribbon (AGNR) with boron nitride nanoribbon (BNNR), the various electronic properties can be observed after gas molecule adsorption. The electronic structure and gap of hybrids system is modified due to gas adsorption, and the systems act like the n-type semiconductor by NH3 molecule adsorption. The hybrid structures due to their tunable band gap are better candidates for gas detecting compared to the pristine BNNRs and AGNRs.

Inferring Toxicological Responses of HepG2 Cells from ...

EPA Pesticide Factsheets

Understanding the dynamic perturbation of cell states by chemicals can aid in for predicting their adverse effects. High-content imaging (HCI) was used to measure the state of HepG2 cells over three time points (1, 24, and 72 h) in response to 976 ToxCast chemicals for 10 different concentrations (0.39-200µM). Cell state was characterized by p53 activation (p53), c-Jun activation (SK), phospho-Histone H2A.x (OS), phospho-Histone H3 (MA), alpha tubulin (Mt), mitochondrial membrane potential (MMP), mitochondrial mass (MM), cell cycle arrest (CCA), nuclear size (NS) and cell number (CN). Dynamic cell state perturbations due to each chemical concentration were utilized to infer coarse-grained dependencies between cellular functions as Boolean networks (BNs). BNs were inferred from data in two steps. First, the data for each state variable were discretized into changed/active (> 1 standard deviation), and unchanged/inactive values. Second, the discretized data were used to learn Boolean relationships between variables. In our case, a BN is a wiring diagram between nodes that represent 10 previously described observable phenotypes. Functional relationships between nodes were represented as Boolean functions. We found that inferred BN show that HepG2 cell response is chemical and concentration specific. We observed presence of both point and cycle BN attractors. In addition, there are instances where Boolean functions were not found. We believe that this may be either

Adaptive cyber-attack modeling system

NASA Astrophysics Data System (ADS)

Gonsalves, Paul G.; Dougherty, Edward T.

2006-05-01

The pervasiveness of software and networked information systems is evident across a broad spectrum of business and government sectors. Such reliance provides an ample opportunity not only for the nefarious exploits of lone wolf computer hackers, but for more systematic software attacks from organized entities. Much effort and focus has been placed on preventing and ameliorating network and OS attacks, a concomitant emphasis is required to address protection of mission critical software. Typical software protection technique and methodology evaluation and verification and validation (V&V) involves the use of a team of subject matter experts (SMEs) to mimic potential attackers or hackers. This manpower intensive, time-consuming, and potentially cost-prohibitive approach is not amenable to performing the necessary multiple non-subjective analyses required to support quantifying software protection levels. To facilitate the evaluation and V&V of software protection solutions, we have designed and developed a prototype adaptive cyber attack modeling system. Our approach integrates an off-line mechanism for rapid construction of Bayesian belief network (BN) attack models with an on-line model instantiation, adaptation and knowledge acquisition scheme. Off-line model construction is supported via a knowledge elicitation approach for identifying key domain requirements and a process for translating these requirements into a library of BN-based cyber-attack models. On-line attack modeling and knowledge acquisition is supported via BN evidence propagation and model parameter learning.

Modelling heat conduction in polycrystalline hexagonal boron-nitride films

PubMed Central

Mortazavi, Bohayra; Pereira, Luiz Felipe C.; Jiang, Jin-Wu; Rabczuk, Timon

2015-01-01

We conducted extensive molecular dynamics simulations to investigate the thermal conductivity of polycrystalline hexagonal boron-nitride (h-BN) films. To this aim, we constructed large atomistic models of polycrystalline h-BN sheets with random and uniform grain configuration. By performing equilibrium molecular dynamics (EMD) simulations, we investigated the influence of the average grain size on the thermal conductivity of polycrystalline h-BN films at various temperatures. Using the EMD results, we constructed finite element models of polycrystalline h-BN sheets to probe the thermal conductivity of samples with larger grain sizes. Our multiscale investigations not only provide a general viewpoint regarding the heat conduction in h-BN films but also propose that polycrystalline h-BN sheets present high thermal conductivity comparable to monocrystalline sheets. PMID:26286820

X-ray absorption fine structure of artificial antigens for cadmium

NASA Astrophysics Data System (ADS)

Lu, Liang; Liu, Aiping; Chen, Fusheng; Wang, Xiaohong

2011-11-01

Immunoassay technology as a quick and large-scale screening method to detect metal ions in foods and environmental samples has rapidly been developed due to several advantages over conventional instrument-intensive methods. Unlike biomacromolecule, metal ions are haptens without immunogenicity, so successful preparation of artificial antigens is the first critical step for establishing immunoassay methods for them. In the current paper, cadmium ions were conjugated to BSA and OVA, respectively, using bifunctional chelator, p-SCN-Bn-DTPA. The ultraviolet analysis indicated that the maximum absorption peak of Cd-p-SCN-DTPA-BSA and Cd-p-SCN-DTPA-OVA had a small peak shift and an apparent absorbance increase compared to that of BSA and OVA, and the extents of substitution of ɛ-amino in both conjugates were 51.2% and 58.6%, respectively. In addition, the EXAFS of conjugates implied that Cd 2+ coordinated with N and O atoms of DTPA in artificial antigens, the coordination type and number of Cd-DTPA, Cd-p-SCN-Bn-DTPA-BSA, Cd-p-SCN-Bn-DTPA-OVA were the same. XANES region and geometries of the three compounds were also same. These results implied that the three antigens had the similar local structure and atomic geometry. This was the first time that the XAFS was attempted for the identification of artificial heavy metal ion antigens.

Bombesin receptors and transplanted stem cells in rat brain: High-resolution scan with 99mTc BN1.1

NASA Astrophysics Data System (ADS)

Scopinaro, F.; Paschali, E.; Di Santo, G.; Antonellis, T.; Massari, R.; Trotta, C.; Gourni, H.; Bouziotis, P.; David, V.; Soluri, A.; Varvarigou, A. D.

2006-12-01

The aim of this work is to detect the presence of transplanted stem cells (TSC) in rat brain with high-resolution (HR) scintigraphy and labelled bombesin (BN). BN is a morphogen for Central Nervous System (CNS) as well as for other organs: CNS-oriented TSC over-express BN Receptors (BNR). BN is also a neurotransmitter and modulates several functions of CNS. 99mTc labelled BN-like peptide scan of CNS is the ideal method to detect growing TSC once knowing normal distribution of BNRs in CNS. HR Planar and single photon emission computerized tomography (SPECT) images of rat brain were performed with new HR detectors (Li-tech, Italy). Pertechnetate, 99mTc HMPAO and the new 99mTc BN1.1 (patented) were i.v. administered in five rats. HR SPECT of 99mTc BN1.1 detected olfactory tract, fronto-lateral cortex, cerebellum, basal ganglia and amygdale. Results of SPECT were confirmed by bio-distribution study performed after autopsy of three of the five rats. The remaining two rats underwent cerebral lesions followed by transplant of TSC. Three months later, HR scintigraphy was repeated and showed images completely different from previous basal study, with hot spot of 99mTc BN1.1 corresponding to the site of TSC transplant. Immuno-histochemistry confirmed the presence of viable TSC. Not only 99mTc BN1.1 HR scan showed viability of transplanted TSC but also the "background brain" was the still now unknown map of BNR in mammalian brain.

Understanding the Relation between Anorexia Nervosa and Bulimia Nervosa in a Swedish National Twin Sample

PubMed Central

Bulik, Cynthia M; Thornton, Laura; Root, Tammy L.; Pisetsky, Emily M.; Lichtenstein, Paul; Pedersen, Nancy L.

2010-01-01

Background We present a bivariate twin analysis of anorexia nervosa (AN) and bulimia nervosa (BN) to determine the extent to which shared genetic and environmental factors contribute to liability to these disorders. Method Focusing on females from the Swedish Twin study of Adults: Genes and Environment (STAGE) (N=7000), we calculated heritability estimates for narrow and broad AN and BN and estimated their genetic correlation. Results In the full model, the heritability estimate for narrow AN was (a2 = .57; 95% CI: .00, .81) and for narrow BN (a2 = .62; 95% CI: .08, .70) with the remaining variance accounted for by unique environmental factors. Shared environmental factors estimates were (c2 = .00; 95% CI: .00, .67) for AN and (c2 = .00; 95% CI: .00, .40) for BN. Moderate additive genetic (.46) and unique environmental (.42) correlations between AN and BN were observed. Heritability estimates for broad AN were lower (a2 = .29; 95% CI: .04, .43) than for narrow AN, but estimates for broad BN were similar to narrow BN. The genetic correlation for broad AN and BN was .79 and the unique environmental correlation was .44. Conclusions We highlight the contribution of additive genetic factors to both narrow and broad AN and BN and demonstrate a moderate overlap of both genetic and unique environmental factors that influence the two conditions. Common concurrent and sequential comorbidity of AN and BN can in part be accounted for by shared genetic and environmental influences on liability although independent factors also operative. PMID:19828139

A systematic review of the health-related quality of life and economic burdens of anorexia nervosa, bulimia nervosa, and binge eating disorder.

PubMed

Ágh, Tamás; Kovács, Gábor; Supina, Dylan; Pawaskar, Manjiri; Herman, Barry K; Vokó, Zoltán; Sheehan, David V

2016-09-01

To perform a systematic review of the health-related quality of life (HRQoL) and economic burdens of anorexia nervosa (AN), bulimia nervosa (BN), and binge eating disorder (BED). A systematic literature search of English-language studies was performed in Medline, Embase, PsycINFO, PsycARTICLES, Academic Search Complete, CINAHL Plus, Business Source Premier, and Cochrane Library. Cost data were converted to 2014 Euro. Sixty-nine studies were included. Data on HRQoL were reported in 41 studies (18 for AN, 17 for BN, and 18 for BED), on healthcare utilization in 20 studies (14 for AN, 12 for BN, and 8 for BED), and on healthcare costs in 17 studies (9 for AN, 11 for BN, and only 2 for BED). Patients' HRQoL was significantly worse with AN, BN, and BED compared with healthy populations. AN, BN, and BED were associated with a high rate of hospitalization, outpatient care, and emergency department visits. However, patients rarely received specific treatment for their eating disorder. The annual healthcare costs for AN, BN, and BED were €2993 to €55,270, €888 to €18,823, and €1762 to €2902, respectively. AN, BN, and BED have a serious impact on patient's HRQoL and are also associated with increased healthcare utilization and healthcare costs. The burden of BED should be examined separately from that of BN. The limited evidence suggests that further research is warranted to better understand the differences in long-term HRQoL and economic burdens of AN, BN, and BED.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Du Frane, W. L.; Cervantes, O.; Ellsworth, G. F.

When we Consolidate cubic boron nitride (cBN) it typically requires either a matrix of metal bearing materials that are undesirable for certain applications, or very high pressures within the cBN phase stability field that are prohibitive to manufacturing size and cost. We present new methodology for consolidating high stiffness cBN composites within a hexagonal boron nitride (hBN) matrix (15–25 vol%) with the aid of a binder phase (0–6 vol%) at moderate pressures (0.5–1.0 GPa) and temperatures (900–1300 °C). The composites are demonstrated to be highly tailorable with a range of compositions and resulting physical/mechanical properties. Ultrasonic measurements indicate that inmore » some cases these composites have elastic mechanical properties that exceed those of the highest strength steel alloys. Moreover, two methods were identified to prevent phase transformation of the metastable cBN phase into hBN during consolidation: 1. removal of hydrocarbons, and 2. increased cBN particle size. Lithium tetraborate worked better as a binder than boron oxide, aiding consolidation without enhancing cBN to hBN phase transformation kinetics. These powder mixtures consolidated within error of their full theoretical mass densities at 1 GPa, and had only slightly lower densities at 0.5 GPa. This shows potential for consolidation of these composites into larger parts, in a variety of shapes, at even lower pressures using more conventional manufacturing methods, such as hot-pressing.« less

Fluoxetine augments ventilatory CO2 sensitivity in Brown Norway but not Sprague Dawley rats.

PubMed

Hodges, Matthew R; Echert, Ashley E; Puissant, Madeleine M; Mouradian, Gary C

2013-04-01

The Brown Norway (BN; BN/NHsdMcwi) rat exhibits a deficit in ventilatory CO2 sensitivity and a modest serotonin (5-HT) deficiency. Here, we tested the hypothesis that the selective serotonin reuptake inhibitor fluoxetine would augment CO2 sensitivity in BN but not Sprague Dawley (SD) rats. Ventilation during room air or 7% CO2 exposure was measured before, during and after 3 weeks of daily injections of saline or fluoxetine (10mg/(kgday)) in adult male BN and SD rats. Fluoxetine had minimal effects on room air breathing in BN and SD rats (p>0.05), although tidal volume (VT) was reduced in BN rats (p<0.05). There were also minimal effects of fluoxetine on CO2 sensitivity in SD rats, but fluoxetine increased minute ventilation, breathing frequency and VT during hypercapnia in BN rats (p<0.05). The augmented CO2 response was reversible upon withdrawal of fluoxetine. Brain levels of biogenic amines were largely unaffected, but 5-HIAA and the ratio of 5-HIAA/5-HT were reduced (p<0.05) consistent with selective and effective 5-HT reuptake inhibition. Thus, fluoxetine increases ventilatory CO2 sensitivity in BN but not SD rats, further suggesting altered 5-HT system function may contribute to the inherently low CO2 sensitivity in the BN rat. Copyright © 2013 Elsevier B.V. All rights reserved.

Thick c-BN films deposited by radio frequency magnetron sputtering in argon/nitrogen gas mixture with additional hydrogen gas

NASA Astrophysics Data System (ADS)

Zhao, Yan; Gao, Wei; Xu, Bo; Li, Ying-Ai; Li, Hong-Dong; Gu, Guang-Rui; Yin, Hong

2016-10-01

The excellent physical and chemical properties of cubic boron nitride (c-BN) film make it a promising candidate for various industry applications. However, the c-BN film thickness restricts its practical applications in many cases. Thus, it is indispensable to develop an economic, simple and environment-friend way to synthesize high-quality thick, stable c-BN films. High-cubic-content BN films are prepared on silicon (100) substrates by radio frequency (RF) magnetron sputtering from an h-BN target at low substrate temperature. Adhesions of the c-BN films are greatly improved by adding hydrogen to the argon/nitrogen gas mixture, allowing the deposition of a film up to 5-μm thick. The compositions and the microstructure morphologies of the c-BN films grown at different substrate temperatures are systematically investigated with respect to the ratio of H2 gas content to total working gas. In addition, a primary mechanism for the deposition of thick c-BN film is proposed. Project supported by the National Natural Science Foundation of China (Grant Nos. 51572105, 61504046, and 51272224), the Scientific Research Foundation for the Returned Overseas Chinese Scholars, State Education Ministry, China, the Development and Reform Commission of Jilin Province, China (Grant No. 2015Y050), and the Scientific Research Foundation for the Returned Overseas of Jilin Province, China.

A pilot study examining diagnostic differences among exercise and weight suppression in bulimia nervosa and binge eating disorder.

PubMed

Cook, Brian J; Steffen, Kristine J; Mitchell, James E; Otto, Maxwell; Crosby, Ross D; Cao, Li; Wonderlich, Stephen A; Crow, Scott; Hill, Laura; Le Grange, Daniel; Powers, Pauline

2015-05-01

The objective of this study was to investigate diagnostic differences in weight suppression (e.g., the difference between one's current body weight and highest non-pregnancy adult body weight) and exercise among Bulimia Nervosa (BN) and Binge Eating Disorder (BED). Because exercise may be a key contributor to weight suppression in BN, we were interested in examining the potential moderating effect of exercise on weight suppression in BN or BED. Participants with BN (n = 774) and BED (n = 285) completed self-report surveys of weight history, exercise and eating disorder symptoms. Generalised linear model analyses were used to examine the associations among diagnosis, exercise frequency and their interaction on weight suppression. Exercise frequency and BN/BED diagnosis were both associated with weight suppression. Additionally, exercise frequency moderated the relationship between diagnosis and weight suppression. Specifically, weight suppression was higher in BN than in BED among those with low exercise frequency but comparable in BN and BED among those with high exercise frequency. Our results suggest that exercise frequency may contribute to different weight suppression outcomes among BN and BED. This may inform clinical implications of exercise in these disorders. Specifically, much understanding of the differences among exercise frequency and the compensatory use of exercise in BN and BED is needed. Copyright © 2015 John Wiley & Sons, Ltd and Eating Disorders Association.

Anticorrosive performance of waterborne epoxy coatings containing water-dispersible hexagonal boron nitride (h-BN) nanosheets

NASA Astrophysics Data System (ADS)

Cui, Mingjun; Ren, Siming; Chen, Jia; Liu, Shuan; Zhang, Guangan; Zhao, Haichao; Wang, Liping; Xue, Qunji

2017-03-01

Homogenous dispersion of hexagonal boron nitride (h-BN) nanosheets in solvents or in the polymer matrix is crucial to initiate their many applications. Here, homogeneous dispersion of hexagonal boron nitride (h-BN) in epoxy matrix was achieved with a water-soluble carboxylated aniline trimer derivative (CAT-) as a dispersant, which was attributed to the strong π-π interaction between h-BN and CAT-, as proved by Raman and UV-vis spectra. Transmission electron microscopy (TEM) analysis confirmed a random dispersion of h-BN nanosheets in the waterborne epoxy coatings. The deterioration process of water-borne epoxy coating with and without h-BN nanosheets during the long-term immersion in 3.5 wt% NaCl solution was investigated by electrochemical measurements and water absorption test. Results implied that the introduction of well dispersed h-BN nanosheets into waterborne epoxy system remarkably improved the corrosion protection performance to substrate. Moreover, 1 wt% BN/EP composite coated substrate exhibited higher impedance modulus (1.3 × 106 Ω cm2) and lower water absorption (4%) than those of pure waterborne epoxy coating coated electrode after long-term immersion in 3.5 wt% NaCl solution, demonstrating its superior anticorrosive performance. This enhanced anticorrosive performance was mainly ascribed to the improved water barrier property of epoxy coating via incorporating homogeneously dispersed h-BN nanosheets.

BnDGAT1s Function Similarly in Oil Deposition and Are Expressed with Uniform Patterns in Tissues of Brassica napus.

PubMed

Zhao, Cuizhu; Li, Huan; Zhang, Wenxue; Wang, Hailan; Xu, Aixia; Tian, Jianhua; Zou, Jitao; Taylor, David C; Zhang, Meng

2017-01-01

As an allotetraploid oilcrop, Brassica napus contains four duplicated Acyl-CoA:diacylglycerol acyltransferase 1 ( DGAT1 ) genes, which catalyze one of the rate-limiting steps in triacylglycerol (TAG) biosynthesis in plants. While all four BnDGAT1 s have been expressed functionally in yeast, their expression patterns in different germplasms and tissues and also consequent contribution to seed oil accumulation in planta remain to be elucidated. In this study, the coding regions of the four BnDGAT1s were expressed in an Arabidopsis dgat1 mutant. All four BnDGAT1s showed similar effects on oil content and fatty acid composition, a result which is different from that observed in previous studies of their expression in yeast. Expression patterns of BnDGAT1s were analyzed in developing seeds of 34 B. napus inbred lines and in different tissues of 14 lines. Different expression patterns were observed for the four BnDGAT1 s, which suggests that they express independently or randomly in different germplasm sources. Higher expression of BnDGAT1s was correlated with higher seed oil content lines. Tissue-specific analyses showed that the BnDGAT1 s were expressed in a uniform pattern in different tissues. Our results suggest that it is important to maintain expression of the four BnDGAT1s for maximum return on oil content.

Evaluation of Intestinal Absorption and Bioavailability of a Bergenin-Phospholipid Complex Solid Dispersion in Rats.

PubMed

Gao, Haoshi; Wei, Yue; Xi, Long; Sun, Yuanyuan; Zhang, Tianhong

2018-05-01

Bergenin (BN) is a Biopharmaceutics Classification System class IV (BCS IV) drug with poor hydrophilicity and lipophilicity and is potentially eliminated by the efflux function of P-glycoprotein (P-gp). These factors may explain its low oral bioavailability. In the present study, a BN-phospholipid complex solid dispersion (BNPC-SD) was prepared by solvent evaporation and characterized based on differential scanning calorimetry, powder X-ray diffraction, scanning electron microscopy, infrared diffraction, solubility, octanol-water partition coefficient, and in vitro dissolution. To investigate how P-gp can inhibit BN absorption in vivo, the P-gp inhibitor verapamil was co-administered with BNPC-SD to Sprague Dawley rats. By in situ single-pass intestinal perfusion, the membrane permeability of BN from BNPC-SD was higher than that of BN given alone and was improved further by co-administered verapamil. A pharmacokinetics study was done in Sprague Dawley rats, with plasma BN levels estimated by high-performance liquid chromatography. C max and AUC 0 → t values for BN were significantly higher for BNPC-SD than for BN given alone and were increased further by verapamil. Thus, the relative oral bioavailability of BNPC-SD as well as BNPC-SD co-administered with verapamil was 156.33 and 202.46%, respectively, compared with the value for BN given alone. These results showed that BNPC-SD can increase the oral bioavailability of BCS IV drugs.

Energetics and formation mechanism of borders between hexagonal boron nitride and graphene

NASA Astrophysics Data System (ADS)

Sawahata, Hisaki; Yamanaka, Ayaka; Maruyama, Mina; Okada, Susumu

2018-06-01

We studied the energetics of two-dimensional heterostructures consisting of hexagonal boron nitride (h-BN) and graphene with respect to the border structure and heterobond species using density functional theory. A BC heterobond is energetically preferable at the border between h-BN and graphene. We also found that the polarization at the zigzag border increases the total energy of the heterostructures. Competition between the bond formation energy and the polarization energy leads to chiral borders at which BC heterobonds are dominant. By taking the formation process of the heterostructures into account, the zigzag border with BC heterobonds is found to be preferentially synthesized from graphene edges under hydrogen-rich conditions.

Anomalous Topological Currents in Graphene Superlattices

NASA Astrophysics Data System (ADS)

Samutpraphoot, Polnop; Song, Justin; Levitov, Leonid

2014-03-01

Berry's phases naturally arise from the spinor structure of Dirac systems, yet observation of non-trivial Berry's phase effects in the transport characteristics of Dirac systems, such as the Valley Hal effect, has proved elusive. Recently, layered graphene heterostructures have emerged as a promising setting to observe novel electron dynamics. We will discuss how novel features in Berry's curvature arise in Graphene/h-BN superlattices to allow long range topological currents to develop. Non-intuitively, we find superlattice mini-bands that have non-trivial Valley Chern number even though the sub-lattice asymmetric potential oscillates in sign. This results in clear non-local transport signatures for the topological character of the bands formed in Graphene/h-BN heterostructures.

Born Lucky: The Institutional Sources behind the Third United States Army Headquarters’ Procedures in Northwest Europe, 1944-45

DTIC Science & Technology

2014-05-22

Engineer Bn., Co. B, 942nd Engineer Avn . Bn., Third US Army, 1 August 1944- 9 May 1945: Vol. I, The Operations, After Action Report (Germany...practitioners are willing to investigate the possibilities. 69 BIBLIOGRAPHY 652nd Engineer Bn., Co. B, 942nd Engineer Avn . Bn. Third US Army, 1 August

Micrometric BN powders used as catalyst support: influence of the precursor on the properties of the BN ceramic

NASA Astrophysics Data System (ADS)

Perdigon-Melon, José Antonio; Auroux, Aline; Guimon, Claude; Bonnetot, Bernard

2004-02-01

Thin powders and foams of boron nitride have been prepared from molecular precursors for use as noble metal supports in the catalytic conversion of methane. Different precursors originating from borazines have been tested. The best results were obtained using a precursor derived from trichloroborazine (TCB) which, after reacting with ammonia at room temperature and then thermolyzing up to 1800°C, led to BN powders with a specific area of more than 300 m 2 g -1 and a micrometric spherical texture. Comparable results were obtained using polyborazylene under similar conditions. Aminoborazine-derived precursors did not yield such high specific area ceramics but the BN microstructure resembled a foam with a crystallized skin and amorphous internal part. These differences were related to the chemical mechanism of the conversion of the precursor into BN. Polyhaloborazines and polyborazines yielded BN through gas-solid reactions whereas aminoborazine polymers could be kept waxy up to high temperatures, which favored the glassy foam. Catalysts composed of BN support and platinum have been prepared using two routes: from a mixture of precursor or by impregnation of a BN powder leading to very different catalysts.

BnEPFL6, an EPIDERMAL PATTERNING FACTOR-LIKE (EPFL) secreted peptide gene, is required for filament elongation in Brassica napus.

PubMed

Huang, Yi; Tao, Zhangsheng; Liu, Qiong; Wang, Xinfa; Yu, Jingyin; Liu, Guihua; Wang, Hanzhong

2014-07-01

Inflorescence architecture, pedicel length and stomata patterning in Arabidopsis thaliana are specified by inter-tissue communication mediated by ERECTA and its signaling ligands in the EPIDERMAL PATTERNING FACTOR-LIKE (EPFL) family of secreted cysteine-rich peptides. Here, we identified and characterized BnEPFL6 from Brassica napus. Heterologous expression of this gene under the double enhanced CaMV promoter (D35S) in Arabidopsis resulted in shortened stamen filaments, filaments degradation, and reduced filament cell size that displayed down-regulated expression of AHK2, in which phenotypic variation of ahk2-1 mutant presented highly consistent with that of BnEPFL6 transgenic lines. Especially, the expression level of BnEPFL6 in the shortened filaments of four B. napus male sterile lines (98A, 86A, SA, and Z11A) was similar to that of BnEPFL6 in the transgenic Arabidopsis lines. The activity of pBnEPFL6.2::GUS was intensive in the filaments of transgenic lines. These observations reveal that BnEPFL6 plays an important role in filament elongation and may also affect organ morphology and floral organ specification via a BnEPFL6-mediated cascade.

Hybrid boron nitride-natural fiber composites for enhanced thermal conductivity.

PubMed

Xia, Changlei; Garcia, Andres C; Shi, Sheldon Q; Qiu, Ying; Warner, Nathaniel; Wu, Yingji; Cai, Liping; Rizvi, Hussain R; D'Souza, Nandika A; Nie, Xu

2016-10-05

Thermal conductivity was dramatically increased after adding natural fiber into hexagonal boron nitride (hBN)/epoxy composites. Although natural fiber does not show high-thermal conductivity itself, this study found that the synergy of natural fiber with hBN could significantly improve thermal conductivity, compared with that solely using hBN. A design of mixtures approach using constant fibers with increasing volume fractions of hBN was examined and compared. The thermal conductivity of the composite containing 43.6% hBN, 26.3% kenaf fiber and 30.1% epoxy reached 6.418 W m -1 K -1 , which was 72.3% higher than that (3.600 W m -1 K -1 ) of the 69.0% hBN and 31.0% epoxy composite. Using the scanning electron microscope (SEM) and micro computed tomography (micro-CT), it was observed that the hBN powders were well distributed and ordered on the fiber surfaces enhancing the ceramic filler's interconnection, which may be the reason for the increase in thermal conductivity. Additionally, the results from mechanical and dynamic mechanical tests showed that performances dramatically improved after adding kenaf fibers into the hBN/epoxy composite, potentially benefiting the composite's use as an engineered material.

Hybrid boron nitride-natural fiber composites for enhanced thermal conductivity

NASA Astrophysics Data System (ADS)

Xia, Changlei; Garcia, Andres C.; Shi, Sheldon Q.; Qiu, Ying; Warner, Nathaniel; Wu, Yingji; Cai, Liping; Rizvi, Hussain R.; D'Souza, Nandika A.; Nie, Xu

2016-10-01

Thermal conductivity was dramatically increased after adding natural fiber into hexagonal boron nitride (hBN)/epoxy composites. Although natural fiber does not show high-thermal conductivity itself, this study found that the synergy of natural fiber with hBN could significantly improve thermal conductivity, compared with that solely using hBN. A design of mixtures approach using constant fibers with increasing volume fractions of hBN was examined and compared. The thermal conductivity of the composite containing 43.6% hBN, 26.3% kenaf fiber and 30.1% epoxy reached 6.418 W m-1 K-1, which was 72.3% higher than that (3.600 W m-1 K-1) of the 69.0% hBN and 31.0% epoxy composite. Using the scanning electron microscope (SEM) and micro computed tomography (micro-CT), it was observed that the hBN powders were well distributed and ordered on the fiber surfaces enhancing the ceramic filler’s interconnection, which may be the reason for the increase in thermal conductivity. Additionally, the results from mechanical and dynamic mechanical tests showed that performances dramatically improved after adding kenaf fibers into the hBN/epoxy composite, potentially benefiting the composite’s use as an engineered material.

Comorbid depressive symptoms and self-esteem improve after either cognitive-behavioural therapy or family-based treatment for adolescent bulimia nervosa.

PubMed

Valenzuela, Fabiola; Lock, James; Le Grange, Daniel; Bohon, Cara

2018-05-01

This study examined the effect of family-based treatment for bulimia nervosa (FBT-BN) and cognitive behavioral therapy for adolescents (CBT-A) on depressive symptoms and self-esteem in adolescents with BN. Data were collected from 110 adolescents, ages 12-18, who met Diagnostic and Statistical Manual of Mental Disorders-Fourth Edition, text revision criteria for BN or partial BN. Participants were randomly assigned to FBT-BN or CBT-A and completed measures of depressive symptoms and self-esteem before and after treatment and at 6- and 12-month follow-up assessments. Depressive symptoms and self-esteem significantly improved in both treatments, and neither treatment appeared superior on these clinical outcomes. Parents often worry whether FBT-BN addresses comorbid depressive symptoms and low self-esteem. Our findings address this concern, as they demonstrate that FBT-BN does not differ from CBT-A in improving depressive symptoms and self-esteem, and both treatments result in symptom improvement. These findings can help clinicians guide families to choose a treatment that addresses BN and depressive symptoms and low self-esteem. Copyright © 2018 John Wiley & Sons, Ltd and Eating Disorders Association.

Large-scale synthesis of high-quality hexagonal boron nitride nanosheets for large-area graphene electronics.

PubMed

Lee, Kang Hyuck; Shin, Hyeon-Jin; Lee, Jinyeong; Lee, In-yeal; Kim, Gil-Ho; Choi, Jae-Young; Kim, Sang-Woo

2012-02-08

Hexagonal boron nitride (h-BN) has received a great deal of attention as a substrate material for high-performance graphene electronics because it has an atomically smooth surface, lattice constant similar to that of graphene, large optical phonon modes, and a large electrical band gap. Herein, we report the large-scale synthesis of high-quality h-BN nanosheets in a chemical vapor deposition (CVD) process by controlling the surface morphologies of the copper (Cu) catalysts. It was found that morphology control of the Cu foil is much critical for the formation of the pure h-BN nanosheets as well as the improvement of their crystallinity. For the first time, we demonstrate the performance enhancement of CVD-based graphene devices with large-scale h-BN nanosheets. The mobility of the graphene device on the h-BN nanosheets was increased 3 times compared to that without the h-BN nanosheets. The on-off ratio of the drain current is 2 times higher than that of the graphene device without h-BN. This work suggests that high-quality h-BN nanosheets based on CVD are very promising for high-performance large-area graphene electronics. © 2012 American Chemical Society

Synthesis of large-area multilayer hexagonal boron nitride for high material performance

PubMed Central

Kim, Soo Min; Hsu, Allen; Park, Min Ho; Chae, Sang Hoon; Yun, Seok Joon; Lee, Joo Song; Cho, Dae-Hyun; Fang, Wenjing; Lee, Changgu; Palacios, Tomás; Dresselhaus, Mildred; Kim, Ki Kang; Lee, Young Hee; Kong, Jing

2015-01-01

Although hexagonal boron nitride (h-BN) is a good candidate for gate-insulating materials by minimizing interaction from substrate, further applications to electronic devices with available two-dimensional semiconductors continue to be limited by flake size. While monolayer h-BN has been synthesized on Pt and Cu foil using chemical vapour deposition (CVD), multilayer h-BN is still absent. Here we use Fe foil and synthesize large-area multilayer h-BN film by CVD with a borazine precursor. These films reveal strong cathodoluminescence and high mechanical strength (Young's modulus: 1.16±0.1 TPa), reminiscent of formation of high-quality h-BN. The CVD-grown graphene on multilayer h-BN film yields a high carrier mobility of ∼24,000 cm2 V−1 s−1 at room temperature, higher than that (∼13,000 2 V−1 s−1) with exfoliated h-BN. By placing additional h-BN on a SiO2/Si substrate for a MoS2 (WSe2) field-effect transistor, the doping effect from gate oxide is minimized and furthermore the mobility is improved by four (150) times. PMID:26507400

Interplay between intercalated oxygen superstructures and monolayer h -BN on Cu(100)

DOE PAGES

Ma, Chuanxu; Park, Jewook; Liu, Lei; ...

2016-08-18

The confinement effect of intercalated atoms in van der Waals heterostructures can lead to interesting interactions between the confined atoms or molecules and the overlaying two-dimensional (2D) materials. In this paper, we report the formation of ordered Cu(100) p(2×2) oxygen superstructures by oxygen intercalation under the monolayer hexagonal boron nitride (h-BN) on Cu after annealing. By using scanning tunneling microscopy and x-ray photoelectron spectroscopy, we identify the superstructure and reveal its roles in passivating the exposed Cu surfaces, decoupling h-BN and Cu, and disintegrating h-BN monolayers. The oxygen superstructure appears as a 2D pattern on the exposed Cu surface ormore » quasi-1D stripes of paired oxygen intercalated in the interface of h-BN and Cu predominantly oriented along the moiré modulations. The oxygen superstructure is shown to etch the overlaying h-BN monolayer in a thermal annealing process. After extended annealing, the h-BN monolayer disintegrates into nanoislands with zigzag edges. Finally, we discuss the implications of these findings on the stability and oxidation resistance of h-BN and relate them to challenges in process integration and 2D heterostructures.« less

An antagonistic monoclonal antibody (B-N6) specific for the human neurotensin receptor-1.

PubMed

Ovigne, J M; Vermot-Desroches, C; Lecron, J C; Portier, M; Lupker, J; Pecceu, F; Wijdenes, J

1998-06-01

The neuropeptide neurotensin (NT) interacts with two types of human receptors (hNTR) termed hNTR-1 and hNTR-2. This study describes a monoclonal antibody (MAb) specific for hNTR-1, B-N6. This MAb binds specifically to hNTR-1, but not to hNTR-2 transfected CHO cells. B-N6 and NT display a reciprocal competition and react in a similar way to trypsin, suggesting that the B-N6 epitope is at or close to the NT binding site on the third extracellular loop. Unlike B-N6, NT induces hNTR-1 internalization. Although neither NT-FITC nor B-N6 binding was detected by flow cytometry on different human cells, specific mRNA expression for hNTR-1 was detected in these cells. In CHO cells expressing hNTR-1 and a luciferase gene coupled to the krox24 reporter, B-N6 and the antagonist SR 48692 inhibited NT-induced intracellular activation of krox24 in a dose-dependent manner. From these results it is concluded that B-N6 is an antagonistic anti-hNTR-1 MAb.

Materials Data on NaSr4(BN2)3 (SG:229) by Materials Project

DOE Data Explorer

Kristin Persson

2014-11-02

Computed materials data using density functional theory calculations. These calculations determine the electronic structure of bulk materials by solving approximations to the Schrodinger equation. For more information, see https://materialsproject.org/docs/calculations

Materials Data on Sr2BN2F (SG:62) by Materials Project

DOE Data Explorer

Kristin Persson

2014-11-02

Computed materials data using density functional theory calculations. These calculations determine the electronic structure of bulk materials by solving approximations to the Schrodinger equation. For more information, see https://materialsproject.org/docs/calculations

Materials Data on Ca2BN2F (SG:62) by Materials Project

DOE Data Explorer

Kristin Persson

2014-11-02

Computed materials data using density functional theory calculations. These calculations determine the electronic structure of bulk materials by solving approximations to the Schrodinger equation. For more information, see https://materialsproject.org/docs/calculations

Fermentation product of soybean, black bean, and green bean mixture induces apoptosis in a wide variety of cancer cells.

PubMed

Chia, Jean-San; Du, Jia-Ling; Wu, Ming-Shiou; Hsu, Wei-Bin; Chiang, Chun-Pin; Sun, Andy; Lu, John Jenn-Yenn; Wang, Won-Bo

2013-05-01

Previous studies have shown that soybean fermentation products can act as cancer chemoprevention or therapeutic agents. In this study, the anticancer activities of a fermentation product of soybean, black bean, and green bean mixture (BN999) were investigated. We found that BN999 inhibited the growth of human breast cancer AU565 cells and prostate adenocarcinoma PC-3 cells but not that of normal human cells. BN999 induced apoptosis in various human cancer cells but not in normal human cells. BN999 treatment of AU565 cancer cells resulted in activation of calpain and caspase-8, -9, and -3, suggesting that BN999 induces apoptosis via receptor-, mitochondria-, and endoplasmic reticulum-mediated pathways. Finally, we showed that BN999 inhibited the growth of mouse CT-26 colon cancer xenografts in syngenic BALB/c mice without causing obvious side effects. Together, these data suggest that BN999 has potential to be used as a cancer chemoprevention or therapeutic agent.

Brain responses to body image stimuli but not food are altered in women with bulimia nervosa

PubMed Central

2013-01-01

Background Research into the neural correlates of bulimia nervosa (BN) psychopathology remains limited. Methods In this functional magnetic resonance imaging study, 21 BN patients and 23 healthy controls (HCs) completed two paradigms: 1) processing of visual food stimuli and 2) comparing their own appearance with that of slim women. Participants also rated food craving and anxiety levels. Results Brain activation patterns in response to food cues did not differ between women with and without BN. However, when evaluating themselves against images of slim women, BN patients engaged the insula more and the fusiform gyrus less, compared to HCs, suggesting increased self-focus among women with BN whilst comparing themselves to a ‘slim ideal’. In these BN patients, exposure to food and body image stimuli increased self-reported levels of anxiety, but not craving. Conclusions Our findings suggest that women with BN differ from HCs in the way they process body image, but not in the way they process food stimuli. PMID:24238299

The improvement of wave-absorbing ability of silicon carbide fibers by depositing boron nitride coating

NASA Astrophysics Data System (ADS)

Ye, Fang; Zhang, Litong; Yin, Xiaowei; Liu, Yongsheng; Cheng, Laifei

2013-04-01

This work investigated electromagnetic wave (EMW) absorption and mechanical properties of silicon carbide (SiC) fibers with and without boron nitride (BN) coating by chemical vapor infiltration (CVI). The dielectric property and EM shielding effectiveness of SiC fiber bundles before and after being coated by BN were measured by wave guide method. The EM reflection coefficient of SiC fiber laminates with and without BN coating was determined by model calculation and NRL-arc method, respectively. Tensile properties of SiC fiber bundles with and without BN coating were tested at room temperature. Results show that SiC fibers with BN coating had a great improvement of EMW absorbing property because the composites achieved the impedance matching. BN with the low permittivity and dielectric loss contributed to the enhancive introduction and reduced reflection of EMW. The tensile strength and Weibull modulus of SiC fiber bundles coated by BN increased owing to the decrease of defects in SiC fibers and the protection of coating during loading.

A methodology to model causal relationships on offshore safety assessment focusing on human and organizational factors.

PubMed

Ren, J; Jenkinson, I; Wang, J; Xu, D L; Yang, J B

2008-01-01

Focusing on people and organizations, this paper aims to contribute to offshore safety assessment by proposing a methodology to model causal relationships. The methodology is proposed in a general sense that it will be capable of accommodating modeling of multiple risk factors considered in offshore operations and will have the ability to deal with different types of data that may come from different resources. Reason's "Swiss cheese" model is used to form a generic offshore safety assessment framework, and Bayesian Network (BN) is tailored to fit into the framework to construct a causal relationship model. The proposed framework uses a five-level-structure model to address latent failures within the causal sequence of events. The five levels include Root causes level, Trigger events level, Incidents level, Accidents level, and Consequences level. To analyze and model a specified offshore installation safety, a BN model was established following the guideline of the proposed five-level framework. A range of events was specified, and the related prior and conditional probabilities regarding the BN model were assigned based on the inherent characteristics of each event. This paper shows that Reason's "Swiss cheese" model and BN can be jointly used in offshore safety assessment. On the one hand, the five-level conceptual model is enhanced by BNs that are capable of providing graphical demonstration of inter-relationships as well as calculating numerical values of occurrence likelihood for each failure event. Bayesian inference mechanism also makes it possible to monitor how a safety situation changes when information flow travel forwards and backwards within the networks. On the other hand, BN modeling relies heavily on experts' personal experiences and is therefore highly domain specific. "Swiss cheese" model is such a theoretic framework that it is based on solid behavioral theory and therefore can be used to provide industry with a roadmap for BN modeling and implications. A case study of the collision risk between a Floating Production, Storage and Offloading (FPSO) unit and authorized vessels caused by human and organizational factors (HOFs) during operations is used to illustrate an industrial application of the proposed methodology.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Zhang, Jingchao, E-mail: zhang@unl.edu, E-mail: yyue@whu.edu.cn; Hong, Yang; Yue, Yanan, E-mail: zhang@unl.edu, E-mail: yyue@whu.edu.cn

As the dimensions of nanocircuits and nanoelectronics shrink, thermal energies are being generated in more confined spaces, making it extremely important and urgent to explore for efficient heat dissipation pathways. In this work, the phonon energy transport across graphene and hexagonal boron-nitride (h-BN) interface is studied using classic molecular dynamics simulations. Effects of temperature, interatomic bond strength, heat flux direction, and functionalization on interfacial thermal transport are investigated. It is found out that by hydrogenating graphene in the hybrid structure, the interfacial thermal resistance (R) between graphene and h-BN can be reduced by 76.3%, indicating an effective approach to manipulatemore » the interfacial thermal transport. Improved in-plane/out-of-plane phonon couplings and broadened phonon channels are observed in the hydrogenated graphene system by analyzing its phonon power spectra. The reported R results monotonically decrease with temperature and interatomic bond strengths. No thermal rectification phenomenon is observed in this interfacial thermal transport. Results reported in this work give the fundamental knowledge on graphene and h-BN thermal transport and provide rational guidelines for next generation thermal interface material designs.« less

Antibodies to a conformational epitope on gp41 neutralize HIV-1 by destabilizing the Env spike

PubMed Central

Lee, Jeong Hyun; Leaman, Daniel P.; Kim, Arthur S.; Torrents de la Peña, Alba; Sliepen, Kwinten; Yasmeen, Anila; Derking, Ronald; Ramos, Alejandra; de Taeye, Steven W.; Ozorowski, Gabriel; Klein, Florian; Burton, Dennis R.; Nussenzweig, Michel C.; Poignard, Pascal; Moore, John P.; Klasse, Per Johan; Sanders, Rogier W.; Zwick, Michael B.; Wilson, Ian A.; Ward, Andrew B.

2015-01-01

The recent identification of three broadly neutralizing antibodies (bnAbs) against gp120–gp41 interface epitopes has expanded the targetable surface on the HIV-1 envelope glycoprotein (Env) trimer. By using biochemical, biophysical and computational methods, we map the previously unknown trimer epitopes of two related antibodies, 3BC315 and 3BC176. A cryo-EM reconstruction of a soluble Env trimer bound to 3BC315 Fab at 9.3 Å resolution reveals that the antibody binds between two gp41 protomers, and neutralizes the virus by accelerating trimer decay. In contrast, bnAb 35O22 binding to a partially overlapping quaternary epitope at the gp120–gp41 interface does not induce decay. A conserved gp41-proximal glycan at N88 was also shown to play a role in the binding kinetics of 3BC176 and 3BC315. Finally, our data suggest that the dynamic structure of the Env trimer influences exposure of bnAb epitopes. PMID:26404402

Self-Discrepancy and Eating Disorder Symptoms Across Eating Disorder Diagnostic Groups.

PubMed

Mason, Tyler B; Lavender, Jason M; Wonderlich, Stephen A; Crosby, Ross D; Engel, Scott G; Strauman, Timothy J; Mitchell, James E; Crow, Scott J; Le Grange, Daniel; Klein, Marjorie H; Smith, Tracey L; Peterson, Carol B

2016-11-01

This study examined self-discrepancy, a construct of theoretical relevance to eating disorder (ED) psychopathology, across different types of EDs. Individuals with anorexia nervosa (AN; n = 112), bulimia nervosa (BN; n = 72), and binge eating disorder (BED; n = 199) completed semi-structured interviews assessing specific types of self-discrepancies. Results revealed that actual:ideal (A:I) discrepancy was positively associated with AN, actual:ought (A:O) discrepancy was positively associated with BN and BED, and self-discrepancies did not differentiate BN from BED. Across diagnoses, A:O discrepancy was positively associated with severity of purging, binge eating, and global ED psychopathology. Further, there were significant interactions between diagnosis and A:O discrepancy for global ED psychopathology and between diagnosis and A:I discrepancy for binge eating and driven exercise. These results support the importance of self-discrepancy as a potential causal and maintenance variable in EDs that differentiates among different types of EDs and symptom severity. Copyright © 2016 John Wiley & Sons, Ltd and Eating Disorders Association. Copyright © 2016 John Wiley & Sons, Ltd and Eating Disorders Association.

Identity impairment and the eating disorders: content and organization of the self-concept in women with anorexia nervosa and bulimia nervosa.

PubMed

Stein, Karen Farchaus; Corte, Colleen

2007-01-01

The cognitive model of the self-concept was used to test the theoretical proposition that disturbances in overall identity development are a core vulnerability that lead to formation of a fat body weight self-definition and eating disorder symptomatology. Structural properties of the self-concept, availability in memory of a fat body weight self-schema, and eating disordered attitudes and behaviours were measured in women with anorexia nervosa (AN) (n = 26), bulimia nervosa (BN) (n = 53) and controls (n = 32). Women with (AN) and (BN) had fewer positive and more negative and highly interrelated self-schemas compared to controls, and women with BN showed information processing evidence of a fat self-schema available in memory. These self-concept properties predicted eating disordered attitudes and behaviour. Disturbances in the overall collection of identities--an impoverished self--is an important contributor to eating disorder symptomatology. The development of new positive selves may be an important factor in recovery. 2006 John Wiley & Sons, Ltd and Eating Disorders Association

Using robust Bayesian network to estimate the residuals of fluoroquinolone antibiotic in soil.

PubMed

Li, Xuewen; Xie, Yunfeng; Li, Lianfa; Yang, Xunfeng; Wang, Ning; Wang, Jinfeng

2015-11-01

Prediction of antibiotic pollution and its consequences is difficult, due to the uncertainties and complexities associated with multiple related factors. This article employed domain knowledge and spatial data to construct a Bayesian network (BN) model to assess fluoroquinolone antibiotic (FQs) pollution in the soil of an intensive vegetable cultivation area. The results show: (1) The relationships between FQs pollution and contributory factors: Three factors (cultivation methods, crop rotations, and chicken manure types) were consistently identified as predictors in the topological structures of three FQs, indicating their importance in FQs pollution; deduced with domain knowledge, the cultivation methods are determined by the crop rotations, which require different nutrients (derived from the manure) according to different plant biomass. (2) The performance of BN model: The integrative robust Bayesian network model achieved the highest detection probability (pd) of high-risk and receiver operating characteristic (ROC) area, since it incorporates domain knowledge and model uncertainty. Our encouraging findings have implications for the use of BN as a robust approach to assessment of FQs pollution and for informing decisions on appropriate remedial measures.

Stability, elastic and electronic properties of a novel BN2 sheet with extended hexagons with N-N bonds

NASA Astrophysics Data System (ADS)

Waters, Kevin; Pandey, Ravindra

2018-04-01

A new B-N monolayer material (BN2) consisting of a network of extended hexagons is predicted using density functional theory. The distinguishable nature of this 2D material is found to be the presence of the bonded N atoms (N-N) in the lattice. Analysis of the phonon dispersion curves show this phase of BN2 to be stable. The calculated elastic properties exhibit anisotropic mechanical properties that surpass graphene in the armchair direction. The BN2 monolayer is metallic with in-plane p states dominating the Fermi level. Novel applications resulting from a strong anisotropic mechanical strength together with the metallic properties of the BN2 sheet with the extended hexagons with N-N bonds may enable future innovation at the nanoscale.

What If You Ran Your Bookstore Like a Library? The Troubled Book Business Can Learn from Libraries' Willingness to Share

ERIC Educational Resources Information Center

Fister, Barbara

2008-01-01

Ten years ago, stories like "B&N: The New College Library" (LJ 2/1/98) and "What If You Ran Your Library Like a Bookstore?" (American Libraries, 3/98) kicked up a controversy about the viability of libraries. Ironically, these days it's the book business that has an aura of crisis and gloom, while visits to libraries are surging. Over two billion…

Quality of Life in Patients With Brain Metastases Using the EORTC QLQ-BN20+2 and QLQ-C15-PAL

DOE Office of Scientific and Technical Information (OSTI.GOV)

Caissie, Amanda; Nguyen, Janet; Chen, Emily

Purpose: The 20-item European Organisation for Research and Treatment of Cancer Quality of Life Questionnaire-Brain Neoplasm (QLQ-BN20) is a validated quality-of-life (QOL) questionnaire for patients with primary brain tumors. The European Organisation for Research and Treatment of Cancer Quality of Life Questionnaire-Core 15 Palliative (QLQ-C15-PAL) core palliative questionnaire is a 15-item version of the core 30-item QLQ-C30 and was developed to decrease the burden on patients with advanced cancer. The combination of the QLQ-BN20 and QLQ-C30 to assess QOL may be too burdensome for patients. The primary aim of this study was to assess QOL in patients before and aftermore » treatment for brain metastases using the QLQ-BN20+2 and QLQ-C15-PAL, a version of the QLQ-BN20 questionnaire with 2 additional questions assessing cognitive functioning that were not addressed in the QLQ-C15-PAL. Methods and Materials: Patients with brain metastases completed the QLQ-C15-PAL and QLQ-BN20+2 questionnaires to assess QOL before and 1 month after radiation. Linear regression analysis was used to assess changes in QOL scores over time, as well as to explore associations between the QLQ-BN20+2 and QLQ-C15-PAL scales, patient demographics, and clinical variables. Spearman correlation assessed associations between the QLQ-BN20+2 and QLQ-C15-PAL scales. Results: Among 108 patients, the majority (55%) received whole-brain radiotherapy only, with 65% of patients completing follow-up at 1 month after treatment. The most prominent symptoms at baseline were future uncertainty (QLQ-BN20+2) and fatigue (QLQ-C15-PAL). After treatment, significant improvement was seen for the QLQ-C15-PAL insomnia scale, as well as the QLQ-BN20+2 scales of future uncertainty, visual disorder, and concentration difficulty. Baseline Karnofsky Performance Status was negatively correlated to QLQ-BN20+2 motor dysfunction but positively related to QLQ-C15-PAL physical functioning and QLQ-BN20+2 cognitive functioning at baseline and follow-up. QLQ-BN20+2 scales of future uncertainty and motor dysfunction correlated with the most QLQ-C15-PAL scales, including overall QOL (negative association) at baseline and follow-up. Conclusion: After radiation, the questionnaires showed maintenance of QOL and improvement of QOL scores such as future uncertainty, which featured prominently in this patient population. It is proposed that the 37-item QLQ-BN20+2 and QLQ-C15-PAL, as opposed to the 50-item QLQ-BN20 and QLQ-C30, may be used together as a universal QOL assessment tool in this setting.« less

44Sc-DOTA-BN[2-14]NH2 in comparison to 68Ga-DOTA-BN[2-14]NH2 in pre-clinical investigation. Is 44Sc a potential radionuclide for PET?

PubMed

Koumarianou, E; Loktionova, N S; Fellner, M; Roesch, F; Thews, O; Pawlak, D; Archimandritis, S C; Mikolajczak, R

2012-12-01

In the present study we demonstrate the in vitro and in vivo comparison of the (44)Sc and (68)Ga labeled DOTA-BN[2-14]NH(2). (44)Sc is a positron emitter with a half life of 3.92 h. Hence it could be used for PET imaging with ligands requiring longer observation time than in the case of (68)Ga. The binding affinity of (nat)Sc-DOTA-BN[2-14]NH(2) and (nat)Ga-DOTA-BN[2-14]NH(2) to GRP receptors was studied in competition to [(125)I-Tyr(4)]-Bombesin in the human prostate cancer cell line PC-3. A preliminary biodistribution in normal rats was performed, while first microPET images were assessed in male Copenhagen rats bearing the androgen-independent Dunning R-3327-AT-1 prostate cancer tumor. The affinity to GRP receptors in the PC-3 cell line was higher for (nat)Ga-DOTA-BN[2-14]NH(2) (IC(50)(nM)=0.85 ± 0.06) than that of (nat)Sc-DOTA-BN[2-14]NH(2) (IC(50) (nM)=6.49 ± 0.13). The internalization rate of (68)Ga labeled DOTA-BN[2-14]NH(2) was slower than that of (44)Sc, but their final internalization percents were comparable. (68)Ga-DOTA-BN[2-14]NH(2) was externalized faster than (44)Sc-DOTA-BN[2-14]NH(2). The biodistribution of (44)Sc-DOTA-BN[2-14]NH(2) and (68)Ga-DOTA-BN[2-14]NH(2) in normal rats revealed a higher uptake in target organs and tissues of the first one while both excreted mainly through urinary tract. In microPET images both tracers were accumulated in the tumor with similar uptake patterns. Despite the differences in the receptor affinity both the (68)Ga- and the (44)Sc-labeled DOTA-BN[2-14]NH(2) tracers showed comparable distribution and similar time constants of uptake and elimination. Moreover no differences in tumor accumulation (neither in the overall uptake nor in the dynamics) were observed from the microPet imaging. From that perspective the use of either (44)Sc or (68)Ga for detecting tumors with GRP receptors is equivalent. Copyright © 2012 Elsevier Ltd. All rights reserved.

Comparison of machine learning techniques to predict all-cause mortality using fitness data: the Henry ford exercIse testing (FIT) project.

PubMed

Sakr, Sherif; Elshawi, Radwa; Ahmed, Amjad M; Qureshi, Waqas T; Brawner, Clinton A; Keteyian, Steven J; Blaha, Michael J; Al-Mallah, Mouaz H

2017-12-19

Prior studies have demonstrated that cardiorespiratory fitness (CRF) is a strong marker of cardiovascular health. Machine learning (ML) can enhance the prediction of outcomes through classification techniques that classify the data into predetermined categories. The aim of this study is to present an evaluation and comparison of how machine learning techniques can be applied on medical records of cardiorespiratory fitness and how the various techniques differ in terms of capabilities of predicting medical outcomes (e.g. mortality). We use data of 34,212 patients free of known coronary artery disease or heart failure who underwent clinician-referred exercise treadmill stress testing at Henry Ford Health Systems Between 1991 and 2009 and had a complete 10-year follow-up. Seven machine learning classification techniques were evaluated: Decision Tree (DT), Support Vector Machine (SVM), Artificial Neural Networks (ANN), Naïve Bayesian Classifier (BC), Bayesian Network (BN), K-Nearest Neighbor (KNN) and Random Forest (RF). In order to handle the imbalanced dataset used, the Synthetic Minority Over-Sampling Technique (SMOTE) is used. Two set of experiments have been conducted with and without the SMOTE sampling technique. On average over different evaluation metrics, SVM Classifier has shown the lowest performance while other models like BN, BC and DT performed better. The RF classifier has shown the best performance (AUC = 0.97) among all models trained using the SMOTE sampling. The results show that various ML techniques can significantly vary in terms of its performance for the different evaluation metrics. It is also not necessarily that the more complex the ML model, the more prediction accuracy can be achieved. The prediction performance of all models trained with SMOTE is much better than the performance of models trained without SMOTE. The study shows the potential of machine learning methods for predicting all-cause mortality using cardiorespiratory fitness data.

New High-Performance SiC Fiber Developed for Ceramic Composites

NASA Technical Reports Server (NTRS)

DiCarlo, James A.; Yun, Hee Mann

2002-01-01

Sylramic-iBN fiber is a new type of small-diameter (10-mm) SiC fiber that was developed at the NASA Glenn Research Center and was recently given an R&D 100 Award for 2001. It is produced by subjecting commercially available Sylramic (Dow Corning, Midland, MI) SiC fibers, fabrics, or preforms to a specially designed high-temperature treatment in a controlled nitrogen environment for a specific time. It can be used in a variety of applications, but it currently has the greatest advantage as a reinforcement for SiC/SiC ceramic composites that are targeted for long-term structural applications at temperatures higher than the capability of metallic superalloys. The commercial Sylramic SiC fiber, which is the precursor for the Sylramic-iBN fiber, is produced by Dow Corning, Midland, Michigan. It is derived from polymers at low temperatures and then pyrolyzed and sintered at high temperatures using boron-containing sintering aids (ref. 1). The sintering process results in very strong fibers (>3 GPa) that are dense, oxygen-free, and nearly stoichiometric. They also display an optimum grain size that is beneficial for high tensile strength, good creep resistance, and good thermal conductivity (ref. 2). The NASA-developed treatment allows the excess boron in the bulk to diffuse to the fiber surface where it reacts with nitrogen to form an in situ boron nitride (BN) coating on the fiber surface (thus the product name of Sylramic-iBN fiber). The removal of boron from the fiber bulk allows the retention of high tensile strength while significantly improving creep resistance and electrical conductivity, and probably thermal conductivity since the grains are slightly larger and the grain boundaries cleaner (ref. 2). Also, as shown in the graph, these improvements allow the fiber to display the best rupture strength at high temperatures in air for any available SiC fiber. In addition, for CMC applications under oxidizing conditions, the formation of an in situ BN surface layer creates a more environmentally durable fiber surface not only because a more oxidation-resistant BN is formed, but also because this layer provides a physical barrier between contacting fibers with oxidation-prone SiC surface layers (refs. 3 and 4). This year, Glenn demonstrated that the in situ BN treatment can be applied simply to Sylramic fibers located within continuous multifiber tows, within woven fabric pieces, or even assembled into complex product shapes (preforms). SiC/SiC ceramic composite panels have been fabricated from Sylramic-iBN fabric and then tested at Glenn within the Ultra-Efficient Engine Technology Program. The test conditions were selected to simulate those experienced by hot-section components in advanced gas turbine engines. The results from testing at Glenn demonstrate all the benefits expected for the Sylramic-iBN fibers. That is, the composites displayed the best thermostructural performance in comparison to composites reinforced by Sylramic fibers and by all other currently available high-performance SiC fiber types (refs. 3 and 5). For these reasons, the Ultra-Efficient Engine Technology Program has selected the Sylramic-iBN fiber for ongoing efforts aimed at SiC/SiC engine component development.