Natural graphene microsheets/sulfur as Li-S battery cathode towards >99% coulombic efficiency of long cycles

NASA Astrophysics Data System (ADS)

Zhang, Yan; Duan, Xiaoyong; Wang, Jie; Wang, Congwei; Wang, Junying; Wang, Jianlong; Wang, Junzhong

2018-02-01

Lithium-sulfur battery receives intense attention owing to its high theoretical energy density. However, poor electrical conductivity of sulfur and poor cycle stability of the battery hinder its application. Here, we report that graphene microsheets prepared from microcrystalline graphite minerals by an electrochemical & mechanical approach work as a special conductive support to load sulfur as the cathode of lithium-sulfur battery. The graphene microsheets have the features of excellent conductivity and low defect, small sheet sizes of <1 μm2 and ≤6 atomic layers as well as natural silicate residue covered. Li-S batteries of graphene microsheets/S as cathode exhibit long-term cyclability and high coulombic efficiency. At 1 C for 2000 cycles, average coulombic efficiency of 99.7% is reached.

Small quaternary alkyl phosphonium bis(fluorosulfonyl)imide ionic liquid electrolytes for sodium-ion batteries with P2- and O3-Na2/3[Fe2/3Mn1/3]O2 cathode material

NASA Astrophysics Data System (ADS)

Hilder, Matthias; Howlett, Patrick C.; Saurel, Damien; Gonzalo, Elena; Armand, Michel; Rojo, Teófilo; Macfarlane, Douglas R.; Forsyth, Maria

2017-05-01

A saturated solution of 2.3 M sodium bis(fluorosulfonyl)imide in trimethyl iso-butyl phosphonium bis(fluorosulfonyl)imide ionic liquid shows a high conductivity (0.94 mScm-1 at 50 °C), low ion association, and a wide operational temperature window (-71 °C-305 °C) making it a promising electrolyte for sodium battery applications. Cycling with P2- and O3-Na2/3[Fe2/3Mn1/3]O2 cathode display excellent performance at 50 °C outperforming conventional organic solvent based electrolytes in terms of capacities (at C/10) and long term cycle stability (at C/2). Post analysis of the electrolyte shows no measurable changes while the sodium metal anode and the cathode surface shows the presence of electrolyte specific elements after cycling, suggesting the formation of a stabilizing solid electrolyte interface. Additionally, cycling changes the topography and particle morphology of the cathode. Thus, the electrolyte properties and cell performance match or outperform previously reported results with the additional benefit of replacing the hazardous and flammable organic solvent solutions commonly employed.

High performance planar p-i-n perovskite solar cells with crown-ether functionalized fullerene and LiF as double cathode buffer layers

NASA Astrophysics Data System (ADS)

Liu, Xiaodong; Lei, Ming; Zhou, Yi; Song, Bo; Li, Yongfang

2015-08-01

Double cathode buffer layers (CBLs) composed of fullerene derivative functionalized with a crown-ether end group in its side chain (denoted as PCBC) and a LiF layer were introduced between the PCBM acceptor layer and the top cathode in planar p-i-n perovskite solar cells (pero-SCs) based on CH3NH3PbI3-XClX. The devices with the PCBC/LiF double CBLs showed significant improvements in power conversion efficiency (PCE) and long-term stability when compared to the device with LiF single CBL. Through optimizing the spin-coating speed of PCBC, a maximum PCE of 15.53% has been achieved, which is approximately 15% higher than that of the device with single LiF CBL. The remarkable improvement in PCE can be attributed to the formation of a better ohmic contact in the CBL between PCBC and LiF/Al electrode arising from the dipole moment of PCBC, leading to the enhanced fill factor and short-circuit current density (Jsc). Besides the PCE, the long-term stability of the devices with PCBC interlayer is also superior to that of the device with LiF single CBL, which is due to the more effective protection for the perovskite/PCBM interface.

Effects of cathode electrolyte interfacial (CEI) layer on long term cycling of all-solid-state thin-film batteries

DOE PAGES

Wang, Ziying; Lee, Jungwoo Z.; Xin, Huolin L.; ...

2016-05-30

All-solid-state lithium-ion batteries have the potential to not only push the current limits of energy density by utilizing Li metal, but also improve safety by avoiding flammable organic electrolyte. However, understanding the role of solid electrolyte – electrode interfaces will be critical to improve performance. In this paper, we conducted long term cycling on commercially available lithium cobalt oxide (LCO)/lithium phosphorus oxynitride (LiPON)/lithium (Li) cells at elevated temperature to investigate the interfacial phenomena that lead to capacity decay. STEM-EELS analysis of samples revealed a previously unreported disordered layer between the LCO cathode and LiPON electrolyte. This electrochemically inactive layer grewmore » in thickness leading to loss of capacity and increase of interfacial resistance when cycled at 80 °C. Finally, the stabilization of this layer through interfacial engineering is crucial to improve the long term performance of thin-film batteries especially under thermal stress.« less

3D Interconnected Carbon Fiber Network-Enabled Ultralong Life Na3 V2 (PO4 )3 @Carbon Paper Cathode for Sodium-Ion Batteries.

PubMed

Kretschmer, Katja; Sun, Bing; Zhang, Jinqiang; Xie, Xiuqiang; Liu, Hao; Wang, Guoxiu

2017-03-01

Sodium-ion batteries (NIBs) are an emerging technology, which can meet increasing demands for large-scale energy storage. One of the most promising cathode material candidates for sodium-ion batteries is Na 3 V 2 (PO 4 ) 3 due to its high capacity, thermal stability, and sodium (Na) Superionic Conductor 3D (NASICON)-type framework. In this work, the authors have significantly improved electrochemical performance and cycling stability of Na 3 V 2 (PO 4 ) 3 by introducing a 3D interconnected conductive network in the form of carbon fiber derived from ordinary paper towel. The free-standing Na 3 V 2 (PO 4 ) 3 -carbon paper (Na 3 V 2 (PO 4 ) 3 @CP) hybrid electrodes do not require a metallic current collector, polymeric binder, or conducting additives to function as a cathode material in an NIB system. The Na 3 V 2 (PO 4 ) 3 @CP cathode demonstrates extraordinary long term cycling stability for 30 000 deep charge-discharge cycles at a current density of 2.5 mA cm -2 . Such outstanding cycling stability can meet the stringent requirements for renewable energy storage. © 2016 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

All ceramic structure for molten carbonate fuel cell

DOEpatents

Smith, James L.; Kucera, Eugenia H.

1992-01-01

An all-ceramic molten carbonate fuel cell having a composition formed of a multivalent metal oxide or oxygenate such as an alkali metal, transition metal oxygenate. The structure includes an anode and cathode separated by an electronically conductive interconnect. The electrodes and interconnect are compositions ceramic materials. Various combinations of ceramic compositions for the anode, cathode and interconnect are disclosed. The fuel cell exhibits stability in the fuel gas and oxidizing environments. It presents reduced sealing and expansion problems in fabrication and has improved long-term corrosion resistance.

Inhibition of microbial growth on air cathodes of single chamber microbial fuel cells by incorporating enrofloxacin into the catalyst layer.

PubMed

Liu, Weifeng; Cheng, Shaoan; Sun, Dan; Huang, Haobin; Chen, Jie; Cen, Kefa

2015-10-15

The inevitable growth of aerobic bacteria on the surface of air cathodes is an important factor reducing the performance stability of air cathode single-chamber membrane-free microbial fuel cells (MFCs). Thus searching for effective methods to inhibit the cathodic microbial growth is critical for the practical application of MFCs. In this study, enrofloxacin (ENR), a broad spectrum fluoroquinolone antibiotic, was incorporated into the catalyst layer of activated carbon air cathodes (ACACs) to inhibit the cathodic microbial growth. The biomass content on ACACs was substantially reduced by 60.2% with ENR treatment after 91 days of MFCs operation. As a result of the inhibited microbial growth, the oxygen reduction catalytic performance of the ENR treated ACACs was much stable compared to the fast performance decline of the untreated control. Consequently, a quite stable electricity production was obtained for the MFCs with the ENR treated ACACs, in contrast with a 22.5% decrease in maximum power density of the MFCs with the untreated cathode. ENR treatment of ACACs showed minimal effects on the anode performance. These results indicate that incorporating antibiotics into ACACs should be a simple and effective strategy to inhibit the microbial growth and improve the long-term stability of the performance of air cathode and the electricity production of MFCs. Copyright © 2015 Elsevier B.V. All rights reserved.

The orientation construction of S and N dual-doped discoid-like graphene with high-rate electrode property

NASA Astrophysics Data System (ADS)

Song, Xinyu; Ma, Xinlong; Ning, Guoqing; Gao, Daowei; Yu, Zhiqing; Xiao, Zhihua

2018-06-01

The orientation construction of S and N dual-doped discoid-like graphene (labeled as SNDG) is achieved by regular arrangement of the polycyclic aromatics in pitch molecules using natural diatomites as templates. The superior electrochemical energy storage ability of SNDG is demonstrated by cathode and anode tests, respectively. The synergistic effects of the robust scaffold coupled with the hollow structure, unique porous structure, the excellent structural stability and the dual-doping of S and N lead to the electrode property enhancement in terms of rate capability and durability. The Li ion hybrid capacitor using SNDG as both anode and cathode, presents excellent long-term cycling stability and markedly energy and power densities (up to 143 Wh kg-1 and 13,548 W kg-1). This work provides a novel pathway to realize the mass production of high-rate electrode materials via the high value-added utilization of pitch.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Mancini, Alessandro; Felice, Valeria; Natali Sora, Isabella

Chemical reactivity between cathodes and electrolytes is a crucial issue for long term SOFCs stability and performances. In this study, chemical reactivity between selected cathodic materials and the ionic conducting melilite La{sub 1.50}Sr{sub 0.50}Ga{sub 3}O{sub 7.25} has been extensively investigated by X-ray powder diffraction in a wide temperature range (up to 1573 K). Perovskite-type La{sub 0.8}Sr{sub 0.2}MnO{sub 3−d} and La{sub 0.8}Sr{sub 0.2}Fe{sub 0.8}Cu{sub 0.2}O{sub 3−d} and K{sub 2}NiF{sub 4}-type La{sub 2}NiO{sub 4+d} were selected as cathode materials. The results of this study allow identifying the most suitable electrode material to be used in combination with the melilite-type gallate electrolyte andmore » set the basis for future work on this novel system. - Graphical abstract: Chemical reactivity between cathodes and electrolytes is a crucial issue for long term SOFCs stability and performances. In this study, chemical reactivity between selected cathodic materials and the ionic conducting melilite La{sub 1.50}Sr{sub 0.50}Ga{sub 3}O{sub 7.25} has been extensively investigated by means of X-ray powder diffraction. - Highlights: • Chemical compatibility between melilite-type gallate and cathodes for SOFCs up to 1573 K. • No reactivity observed between La{sub 0.8}Sr{sub 0.2}Fe{sub 0.8}Cu{sub 0.2}O{sub 3−d} and La{sub 1.50}Sr{sub 0.50}Ga{sub 3}O{sub 7.25}. • Reactivity observed between La{sub 0.80}Sr{sub 0.20}MnO{sub 3−d} and La{sub 1.50}Sr{sub 0.50}Ga{sub 3}O{sub 7.25}. • Significant reactivity observed between La{sub 2}NiO{sub 4+d} and La{sub 1.50}Sr{sub 0.50}Ga{sub 3}O{sub 7.25}.« less

Degradation analysis of anode-supported intermediate temperature-solid oxide fuel cells under various failure modes

NASA Astrophysics Data System (ADS)

Lee, Tae-Hee; Park, Ka-Young; Kim, Ji-Tae; Seo, Yongho; Kim, Ki Buem; Song, Sun-Ju; Park, Byoungnam; Park, Jun-Young

2015-02-01

This study focuses on mechanisms and symptoms of several simulated failure modes, which may have significant influences on the long-term durability and operational stability of intermediate temperature-solid oxide fuel cells (IT-SOFCs), including fuel/oxidation starvation by breakdown of fuel/air supply components and wet and dry cycling atmospheres. Anode-supported IT-SOFCs consisting of a Ba0.5Sr0.5Co0.8Fe0.2O3-δ (BSCF)-Nd0.1Ce0.9O2-δ (NDC) composite cathode with an NDC electrolyte on a Ni-NDC anode substrate are fabricated via dry-pressings followed by the co-firing method. Comprehensive and systematic research based on the failure mode and effect analysis (FMEA) of anode-supported IT-SOFCs is conducted using various electrochemical and physiochemical analysis techniques to extend our understanding of the major mechanisms of performance deterioration under SOFC operating conditions. The fuel-starvation condition in the fuel-pump failure mode causes irreversible mechanical degradation of the electrolyte and cathode interface by the dimensional expansion of the anode support due to the oxidation of Ni metal to NiO. In contrast, the BSCF cathode shows poor stability under wet and dry cycling modes of cathode air due to the strong electroactivity of SrO with H2O. On the other hand, the air-depletion phenomena under air-pump failure mode results in the recovery of cell performance during the long-term operation without the visible microstructural transformation through the reduction of anode overvoltage.

A stable lithiated silicon-chalcogen battery via synergetic chemical coupling between silicon and selenium.

PubMed

Eom, KwangSup; Lee, Jung Tae; Oschatz, Martin; Wu, Feixiang; Kaskel, Stefan; Yushin, Gleb; Fuller, Thomas F

2017-01-05

Li-ion batteries dominate portable energy storage due to their exceptional power and energy characteristics. Yet, various consumer devices and electric vehicles demand higher specific energy and power with longer cycle life. Here we report a full-cell battery that contains a lithiated Si/graphene anode paired with a selenium disulfide (SeS 2 ) cathode with high capacity and long-term stability. Selenium, which dissolves from the SeS 2 cathode, was found to become a component of the anode solid electrolyte interphase (SEI), leading to a significant increase of the SEI conductivity and stability. Moreover, the replacement of lithium metal anode impedes unwanted side reactions between the dissolved intermediate products from the SeS 2 cathode and lithium metal and eliminates lithium dendrite formation. As a result, the capacity retention of the lithiated silicon/graphene-SeS 2 full cell is 81% after 1,500 cycles at 268 mA g SeS2 -1 . The achieved cathode capacity is 403 mAh g SeS2 -1 (1,209 mAh cm SeS2 -3 ).

High performance planar p-i-n perovskite solar cells with crown-ether functionalized fullerene and LiF as double cathode buffer layers

DOE Office of Scientific and Technical Information (OSTI.GOV)

Liu, Xiaodong; Zhou, Yi, E-mail: yizhou@suda.edu.cn, E-mail: songbo@suda.edu.cn, E-mail: liyf@iccas.ac.cn; Song, Bo, E-mail: yizhou@suda.edu.cn, E-mail: songbo@suda.edu.cn, E-mail: liyf@iccas.ac.cn

2015-08-10

Double cathode buffer layers (CBLs) composed of fullerene derivative functionalized with a crown-ether end group in its side chain (denoted as PCBC) and a LiF layer were introduced between the PCBM acceptor layer and the top cathode in planar p-i-n perovskite solar cells (pero-SCs) based on CH{sub 3}NH{sub 3}PbI{sub 3−X}Cl{sub X}. The devices with the PCBC/LiF double CBLs showed significant improvements in power conversion efficiency (PCE) and long-term stability when compared to the device with LiF single CBL. Through optimizing the spin-coating speed of PCBC, a maximum PCE of 15.53% has been achieved, which is approximately 15% higher than thatmore » of the device with single LiF CBL. The remarkable improvement in PCE can be attributed to the formation of a better ohmic contact in the CBL between PCBC and LiF/Al electrode arising from the dipole moment of PCBC, leading to the enhanced fill factor and short-circuit current density (J{sub sc}). Besides the PCE, the long-term stability of the devices with PCBC interlayer is also superior to that of the device with LiF single CBL, which is due to the more effective protection for the perovskite/PCBM interface.« less

Development and Long-Term Stability of a Novel Microbial Fuel Cell BOD Sensor with MnO2 Catalyst

PubMed Central

Kharkwal, Shailesh; Tan, Yi Chao; Lu, Min; Ng, How Yong

2017-01-01

A novel microbial fuel cell (MFC)-based biosensor was designed for continuous monitoring of biochemical oxygen demand (BOD) in real wastewater. To lower the material cost, manganese dioxide (MnO2) was tested as an innovative cathode catalyst for oxygen reduction in a single chamber air-cathode MFC, and two different crystalline structures obtained during synthesis of MnO2 (namely β- and γ-MnO2) were compared. The BOD sensor was studied in a comprehensive way, using both sodium acetate solution and real domestic wastewater (DWW). The optimal performance of the sensor was obtained with a β-MnO2 catalyst, with R2 values of 0.99 and 0.98 using sodium acetate solution and DWW, respectively. The BOD values predicted by the β-MnO2 biosensor for DWW were in agreement with the BOD5 values, determined according to standard methods, with slight variations in the range from 3% to 12%. Finally, the long-term stability of the BOD biosensor was evaluated over 1.5 years. To the best of our knowledge, this is the first report of an MFC BOD sensor using an MnO2 catalyst at the cathode; the feasibility of using a low-cost catalyst in an MFC for online measurement of BOD in real wastewater broadens the scope of applications for such devices. PMID:28134838

DMSO-Li2O2 Interface in the Rechargeable Li-O2 Battery Cathode: Theoretical and Experimental Perspectives on Stability.

PubMed

Schroeder, Marshall A; Kumar, Nitin; Pearse, Alexander J; Liu, Chanyuan; Lee, Sang Bok; Rubloff, Gary W; Leung, Kevin; Noked, Malachi

2015-06-03

One of the greatest obstacles for the realization of the nonaqueous Li-O2 battery is finding a solvent that is chemically and electrochemically stable under cell operating conditions. Dimethyl sulfoxide (DMSO) is an attractive candidate for rechargeable Li-O2 battery studies; however, there is still significant controversy regarding its stability on the Li-O2 cathode surface. We performed multiple experiments (in situ XPS, FTIR, Raman, and XRD) which assess the stability of the DMSO-Li2O2 interface and report perspectives on previously published studies. Our electrochemical experiments show long-term stable cycling of a DMSO-based operating Li-O2 cell with a platinum@carbon nanotube core-shell cathode fabricated via atomic layer deposition, specifically with >45 cycles of 40 h of discharge per cycle. This work is complemented by density functional theory calculations of DMSO degradation pathways on Li2O2. Both experimental and theoretical evidence strongly suggests that DMSO is chemically and electrochemically stable on the surface of Li2O2 under the reported operating conditions.

Inkjet-Printed Porous Silver Thin Film as a Cathode for a Low-Temperature Solid Oxide Fuel Cell.

PubMed

Yu, Chen-Chiang; Baek, Jong Dae; Su, Chun-Hao; Fan, Liangdong; Wei, Jun; Liao, Ying-Chih; Su, Pei-Chen

2016-04-27

In this work we report a porous silver thin film cathode that was fabricated by a simple inkjet printing process for low-temperature solid oxide fuel cell applications. The electrochemical performance of the inkjet-printed silver cathode was studied at 300-450 °C and was compared with that of silver cathodes that were fabricated by the typical sputtering method. Inkjet-printed silver cathodes showed lower electrochemical impedance due to their porous structure, which facilitated oxygen gaseous diffusion and oxygen surface adsorption-dissociation reactions. A typical sputtered nanoporous silver cathode became essentially dense after the operation and showed high impedance due to a lack of oxygen supply. The results of long-term fuel cell operation show that the cell with an inkjet-printed cathode had a more stable current output for more than 45 h at 400 °C. A porous silver cathode is required for high fuel cell performance, and the simple inkjet printing technique offers an alternative method of fabrication for such a desirable porous structure with the required thermal-morphological stability.

Power Conversion Efficiency and Device Stability Improvement of Inverted Perovskite Solar Cells by Using a ZnO:PFN Composite Cathode Buffer Layer.

PubMed

Jia, Xiaorui; Zhang, Lianping; Luo, Qun; Lu, Hui; Li, Xueyuan; Xie, Zhongzhi; Yang, Yongzhen; Li, Yan-Qing; Liu, Xuguang; Ma, Chang-Qi

2016-07-20

We have demonstrated in this article that both power conversion efficiency (PCE) and performance stability of inverted planar heterojunction perovskite solar cells can be improved by using a ZnO:PFN nanocomposite (PFN: poly[(9,9-bis(3'-(N,N-dimethylamion)propyl)-2,7-fluorene)-alt-2,7-(9,9-dioctyl)-fluorene]) as the cathode buffer layer (CBL). This nanocomposite could form a compact and defect-less CBL film on the perovskite/PC61BM surface (PC61BM: phenyl-C61-butyric acid methyl ester). In addition, the high conductivity of the nanocomposite layer makes it works well at a layer thickness of 150 nm. Both advantages of the composite layer are helpful in reducing interface charge recombination and improving device performance. The power conversion efficiency (PCE) of the best ZnO:PFN CBL based device was measured to be 12.76%, which is higher than that of device without CBL (9.00%), or device with ZnO (7.93%) or PFN (11.30%) as the cathode buffer layer. In addition, the long-term stability is improved by using ZnO:PFN composite cathode buffer layer when compare to that of the reference cells. Almost no degradation of open circuit voltage (VOC) and fill factor (FF) was found for the device having ZnO:PFN, suggesting that ZnO:PFN is able to stabilize the interface property and consequently improve the solar cell performance stability.

Fundamental Investigations and Rational Design of Durable High-Performance SOFC Cathodes

DOE Office of Scientific and Technical Information (OSTI.GOV)

Chen, Yu; Ding, Dong; Wei, Tao

The main objective of this project is to unravel the degradation mechanism of LSCF cathodes under realistic operating conditions with different types of contaminants, aiming towards the rational design of cathodes with high-performance and enhanced durability by combining a porous backbone (such as LSCF) with a thin catalyst coating. The mechanistic understanding will help us to optimize the composition and morphology of the catalyst layer and microstructure of the LSCF backbone for better performance and durability. More specifically, the technical objectives include: (1) to unravel the degradation mechanism of LSCF cathodes under realistic operating conditions with different types of contaminantsmore » using in situ and ex situ measurements performed on specially-designed cathodes; (2) to examine the microstructural and compositional evolution of LSCF cathodes as well as the cathode/electrolyte interfaces under realistic operating conditions; (3) to correlate the fuel cell performance instability and degradation with the microstructural and morphological evolution and surface chemistry change of the cathode under realistic operating conditions; (4) to explore new catalyst materials and electrode structures to enhance the stability of the LSCF cathode under realistic operating conditions; and (5) to validate the long term stability of the modified LSCF cathode in commercially available cells under realistic operating conditions. We have systematically evaluated LSCF cathodes in symmetrical cells and anode supported cells under realistic conditions with different types of contaminants such as humidity, CO 2, and Cr. Electrochemical models for the design of test cells and understanding of mechanisms have been developed for the exploration of fundamental properties of electrode materials. It is demonstrated that the activity and stability of LSCF cathodes can be degraded by the introduction of contaminants. The microstructural and compositional evolution of LSCF cathodes as well as the cathode/electrolyte interfaces under realistic operating conditions has been studied. It is found that SrO readily segregated/enriched on the LSCF surface. More severe contamination conditions cause more SrO on surface. Novel catalyst coatings through particle depositions (PrOx) or continuous thin films (PNM) were successfully developed to improve the activity and stability of LSCF cathodes. Finally, we have demonstrated enhanced activity and stability of LSCF cathodes over longer periods of time in homemade and commercially available cells by an optimized PNM (dense film and particles) infiltration process, under clean air and realistic operating conditions (3% H 2O, 5% CO 2 and direct Crofer contact). Both performance and durability of single cells with PNM coating has been enhanced compared with those without coating. Raman analysis of cathodes surface indicated that the intensity of SrCrO 4 was significantly decreased.« less

Selecting the Best Graphite for Long-Life, High-Energy Li-Ion Batteries

DOE Office of Scientific and Technical Information (OSTI.GOV)

Mao, Chengyu; Wood, Marissa; David, Lamuel Abraham

Here, most lithium-ion batteries still rely on intercalation-type graphite materials for anodes, so it is important to consider their role in full cells for applications in electric vehicles. Here, we systematically evaluate the chemical and physical properties of six commercially-available natural and synthetic graphites to establish which factors have the greatest impact on the cycling stability of full cells with nickel-rich LiNi0.8Mn0.1Co0.1O2 (NMC811) cathodes. Electrochemical data and post-mortem characterization explain the origin of capacity fade. The NMC811 cathode shows large irreversible capacity loss and impedance growth, accounting for much of full cell degradation. However, six graphite anodes demonstrate significant differencesmore » with respect to structural change, surface area, impedance growth, and SEI chemistry, which impact overall capacity retention. We found long cycle life correlated most strongly with stable graphite crystallite size. In addition, graphites with lower surface area generally had higher coulombic efficiencies during formation cycles, which led to more stable long-term cycling. The best graphite screened here enables a capacity retention around 90% in full pouch cells over extensive long-term cycling compared to only 82% for cells with the lowest performing graphite. The results show that optimal graphite selection improves cycling stability of high energy lithium-ion cells.« less

Selecting the Best Graphite for Long-Life, High-Energy Li-Ion Batteries

DOE PAGES

Mao, Chengyu; Wood, Marissa; David, Lamuel Abraham; ...

2018-06-16

Here, most lithium-ion batteries still rely on intercalation-type graphite materials for anodes, so it is important to consider their role in full cells for applications in electric vehicles. Here, we systematically evaluate the chemical and physical properties of six commercially-available natural and synthetic graphites to establish which factors have the greatest impact on the cycling stability of full cells with nickel-rich LiNi0.8Mn0.1Co0.1O2 (NMC811) cathodes. Electrochemical data and post-mortem characterization explain the origin of capacity fade. The NMC811 cathode shows large irreversible capacity loss and impedance growth, accounting for much of full cell degradation. However, six graphite anodes demonstrate significant differencesmore » with respect to structural change, surface area, impedance growth, and SEI chemistry, which impact overall capacity retention. We found long cycle life correlated most strongly with stable graphite crystallite size. In addition, graphites with lower surface area generally had higher coulombic efficiencies during formation cycles, which led to more stable long-term cycling. The best graphite screened here enables a capacity retention around 90% in full pouch cells over extensive long-term cycling compared to only 82% for cells with the lowest performing graphite. The results show that optimal graphite selection improves cycling stability of high energy lithium-ion cells.« less

Performance and Structural Evolution of Nano-Scale Infiltrated Solid Oxide Fuel Cell Cathodes

NASA Astrophysics Data System (ADS)

Call, Ann Virginia

Nano-structured mixed ionic and electronic conducting (MIEC) materials have garnered intense interest in electrode development for solid oxide fuel cells due to their high surface areas which allow for effective catalytic activity and low polarization resistances. In particular, composite solid oxide fuel cell (SOFC) cathodes consisting of ionic conducting scaffolds infiltrated with MIEC nanoparticles have exhibited some of the lowest reported polarization resistances. In order for cells utilizing nanostructured moRPhologies to be viable for commercial implementation, more information on their initial performance and long term stability is necessary. In this study, symmetric cell cathodes were prepared via wet infiltration of Sr0.5Sm 0.5CoO3 (SSC) nano-particles via a nitrate process into porous Ce0.9Gd0.1O1.95 (GDC) scaffolds to be used as a model system to investigate performance and structural evolution. Detailed analysis of the cells and cathodes was carried out using electrochemical impedance spectroscopy (EIS). Initial polarization resistances (RP) as low as 0.11 O cm2 at 600ºC were obtained for these SSC-GDC cathodes, making them an ideal candidate for studying high performance nano-structured electrodes. The present results show that the infiltrated cathode microstructure has a direct impact on the initial performance of the cell. Small initial particle sizes and high infiltration loadings (up to 30 vol% SSC) improved initial RP. A simple microstructure-based electrochemical model successfully explained these trends in RP. Further understanding of electrode performance was gleaned from fitting EIS data gathered under varying temperatures and oxygen partial pressures to equivalent circuit models. Both RQ and Gerischer impedance elements provided good fits to the main response in the EIS data, which was associated with the combination of oxygen surface exchange and oxygen diffusion in the electrode. A gas diffusion response was also observed at relatively low pO2. The cells were subjected to life testing at temperatures between 650°C and 800°C for as long as 1500 h. EIS measurements, carried out periodically during the life tests, were done in air at 600°C, a typical expected intermediate-temperature SOFC operating temperature. These were accelerated tests because the aging temperatures > 600ºC should accelerate most degradation processes such as nano-particle coarsening. Long-term RP versus time data was fitted to a combined surface resistance and coarsening kinetics model, and a t0.25 power law coarsening model was found to provide the best fits to the data, suggesting that surface diffusion is the dominant mass transport pathway in SSC-GDC infiltrated cathodes. That is, cathode degradation was due primarily to the coarsening-induced decrease in active SSC surface area. Scanning electron microscopy (SEM) performed after electrochemical life testing confirmed the extent of coarsening of the SSC nanoparticles. The model is used to make predictions regarding long-term stability of infiltrated SSC electrodes, and is also compared with prior results on a similar perovskite MIEC electrode, LSCF. An important new finding is that increasing infiltration loadings yields a marked decrease in the long term degradation rate. Predictions based on accelerated life tests found the lowest possible operating temperature while achieving a degradation rate of 0.5% per kh is 595°C, corresponding to an initial particle size of 40 nm.

High-Thermal- and Air-Stability Cathode Material with Concentration-Gradient Buffer for Li-Ion Batteries.

PubMed

Shi, Ji-Lei; Qi, Ran; Zhang, Xu-Dong; Wang, Peng-Fei; Fu, Wei-Gui; Yin, Ya-Xia; Xu, Jian; Wan, Li-Jun; Guo, Yu-Guo

2017-12-13

Delivery of high capacity with high thermal and air stability is a great challenge in the development of Ni-rich layered cathodes for commercialized Li-ion batteries (LIBs). Herein we present a surface concentration-gradient spherical particle with varying elemental composition from the outer end LiNi 1/3 Co 1/3 Mn 1/3 O 2 (NCM) to the inner end LiNi 0.8 Co 0.15 Al 0.05 O 2 (NCA). This cathode material with the merit of NCM concentration-gradient protective buffer and the inner NCA core shows high capacity retention of 99.8% after 200 cycles at 0.5 C. Furthermore, this cathode material exhibits much improved thermal and air stability compared with bare NCA. These results provide new insights into the structural design of high-performance cathodes with high energy density, long life span, and storage stability materials for LIBs in the future.

A stable lithiated silicon–chalcogen battery via synergetic chemical coupling between silicon and selenium

PubMed Central

Eom, KwangSup; Lee, Jung Tae; Oschatz, Martin; Wu, Feixiang; Kaskel, Stefan; Yushin, Gleb; Fuller, Thomas F.

2017-01-01

Li-ion batteries dominate portable energy storage due to their exceptional power and energy characteristics. Yet, various consumer devices and electric vehicles demand higher specific energy and power with longer cycle life. Here we report a full-cell battery that contains a lithiated Si/graphene anode paired with a selenium disulfide (SeS2) cathode with high capacity and long-term stability. Selenium, which dissolves from the SeS2 cathode, was found to become a component of the anode solid electrolyte interphase (SEI), leading to a significant increase of the SEI conductivity and stability. Moreover, the replacement of lithium metal anode impedes unwanted side reactions between the dissolved intermediate products from the SeS2 cathode and lithium metal and eliminates lithium dendrite formation. As a result, the capacity retention of the lithiated silicon/graphene—SeS2 full cell is 81% after 1,500 cycles at 268 mA gSeS2−1. The achieved cathode capacity is 403 mAh gSeS2−1 (1,209 mAh cmSeS2−3). PMID:28054543

Exceptional power density and stability at intermediate temperatures in protonic ceramic fuel cells

NASA Astrophysics Data System (ADS)

Choi, Sihyuk; Kucharczyk, Chris J.; Liang, Yangang; Zhang, Xiaohang; Takeuchi, Ichiro; Ji, Ho-Il; Haile, Sossina M.

2018-03-01

Over the past several years, important strides have been made in demonstrating protonic ceramic fuel cells (PCFCs). Such fuel cells offer the potential of environmentally sustainable and cost-effective electric power generation. However, their power outputs have lagged behind predictions based on their high electrolyte conductivities. Here we overcome PCFC performance and stability challenges by employing a high-activity cathode, PrBa0.5Sr0.5Co1.5Fe0.5O5+δ (PBSCF), in combination with a chemically stable electrolyte, BaZr0.4Ce0.4Y0.1Yb0.1O3 (BZCYYb4411). We deposit a thin dense interlayer film of the cathode material onto the electrolyte surface to mitigate contact resistance, an approach which is made possible by the proton permeability of PBSCF. The peak power densities of the resulting fuel cells exceed 500 mW cm-2 at 500 °C, while also offering exceptional, long-term stability under CO2.

Aromatic Polyimide/Graphene Composite Organic Cathodes for Fast and Sustainable Lithium-Ion Batteries

DOE Office of Scientific and Technical Information (OSTI.GOV)

Lyu, Hailong; Li, Peipei; Liu, Jiurong

A composite organic cathode material based on aromatic polyimide (PI) and highly conductive graphene was prepared through a facile in situ polymerization method for application in lithium-ion batteries. The in situ polymerization generated intimate contact between PI and electronically conductive graphene, resulting in conductive composites with highly reversible redox reactions and good structure stability. The synergistic effect between PI and graphene enabled not only a high reversible capacity of 232.6 mAh g -1 at a charge–discharge rate of C/10 but also exceptionally high-rate cycling stability, that is, a high capacity of 108.9 mAh g -1 at a very high charge–dischargemore » rate of 50C with a capacity retention of 80 % after 1000 cycles. This improved electrochemical performance resulted from the combination of stable redox reversibility of PI and high electronic conductivity of the graphene additive. In conclusion, the graphene-based composite also exhibited much better performance than composites based on multi-walled carbon nanotubes and the conductive carbon black C45 in terms of specific capacity and long-term cycling stability under the same charge–discharge rates.« less

Aromatic Polyimide/Graphene Composite Organic Cathodes for Fast and Sustainable Lithium-Ion Batteries

DOE PAGES

Lyu, Hailong; Li, Peipei; Liu, Jiurong; ...

2018-01-24

A composite organic cathode material based on aromatic polyimide (PI) and highly conductive graphene was prepared through a facile in situ polymerization method for application in lithium-ion batteries. The in situ polymerization generated intimate contact between PI and electronically conductive graphene, resulting in conductive composites with highly reversible redox reactions and good structure stability. The synergistic effect between PI and graphene enabled not only a high reversible capacity of 232.6 mAh g -1 at a charge–discharge rate of C/10 but also exceptionally high-rate cycling stability, that is, a high capacity of 108.9 mAh g -1 at a very high charge–dischargemore » rate of 50C with a capacity retention of 80 % after 1000 cycles. This improved electrochemical performance resulted from the combination of stable redox reversibility of PI and high electronic conductivity of the graphene additive. In conclusion, the graphene-based composite also exhibited much better performance than composites based on multi-walled carbon nanotubes and the conductive carbon black C45 in terms of specific capacity and long-term cycling stability under the same charge–discharge rates.« less

A tripolar-electrode ionization gas sensor using a carbon nanotube cathode for NO detection

NASA Astrophysics Data System (ADS)

Song, Hui; Li, Kun; Li, Quanfu

2018-06-01

Nitric oxide accounts for more than 95% of the total NO X emission from power plants, which is a major air pollutant. Therefore, it is imperative to accurately detect NO for environmental protection. A tripolar-electrode ionization sensor with a carbon nanotube (CNT) cathode is proposed for NO detection. The non-self-sustaining discharge state and the tripolar-electrode configuration ensures a long nanotube life, which ensures a good stability and fast response of the sensor. Experimental results demonstrate that the tripolar-electrode ionization sensor with 120 µm separations has an intrinsic monotonously decreasing response to NO and exhibits a fast response time of 7 s and recovery time of 8 s. More consumption of the two metastable states N2(A3  ∑  u +) and N2(aʹ1  ∑  u +) of N2 with the increasing of NO concentration is responsible for this. The tripolar-electrode ionization sensor also shows excellent long-term stability of at least one month due to the long CNT life. In addition, the weak effect of SO2 introduction on NO response indicates a good selectivity of the sensor to NO.

Strategies to curb structural changes of lithium/transition metal oxide cathode materials & the changes' effects on thermal & cycling stability

DOE PAGES

Yu, Xiqian; Hu, Enyuan; Bak, Seongmin; ...

2015-12-07

Structural transformation behaviors of several typical oxide cathode materials during a heating process are reviewed in detail to provide in-depth understanding of the key factors governing the thermal stability of these materials. Furthermore, we also discuss applying the information about heat induced structural evolution in the study of electrochemically induced structural changes. All these discussions are expected to provide valuable insights for designing oxide cathode materials with significantly improved structural stability for safe, long-life lithium ion batteries, as the safety of lithium-ion batteries is a critical issue. As a result, it is widely accepted that the thermal instability of themore » cathodes is one of the most critical factors in thermal runaway and related safety problems.« less

A new high-energy cathode for a Na-ion battery with ultrahigh stability.

PubMed

Park, Young-Uk; Seo, Dong-Hwa; Kwon, Hyung-Soon; Kim, Byoungkook; Kim, Jongsoon; Kim, Haegyeom; Kim, Inkyung; Yoo, Han-Ill; Kang, Kisuk

2013-09-18

Large-scale electric energy storage is a key enabler for the use of renewable energy. Recently, the room-temperature Na-ion battery has been rehighlighted as an alternative low-cost technology for this application. However, significant challenges such as energy density and long-term stability must be addressed. Herein, we introduce a novel cathode material, Na1.5VPO4.8F0.7, for Na-ion batteries. This new material provides an energy density of ~600 Wh kg(-1), the highest value among cathodes, originating from both the multielectron redox reaction (1.2 e(-) per formula unit) and the high potential (~3.8 V vs Na(+)/Na) of the tailored vanadium redox couple (V(3.8+)/V(5+)). Furthermore, an outstanding cycle life (~95% capacity retention for 100 cycles and ~84% for extended 500 cycles) could be achieved, which we attribute to the small volume change (2.9%) upon cycling, the smallest volume change among known Na intercalation cathodes. The open crystal framework with two-dimensional Na diffusional pathways leads to low activation barriers for Na diffusion, enabling excellent rate capability. We believe that this new material can bring the low-cost room-temperature Na-ion battery a step closer to a sustainable large-scale energy storage system.

Reinvigorating Reverse-Osmosis Membrane Technology to Stabilize the V 2 O 5 Lithium-Ion Battery Cathode

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wu, Ji; Byrd, Ian; Jin, Congrui

V 2O 5 is deemed as one of the most promising cathode materials for next-generation high-capacity lithium-ion batteries (LIBs). It possesses a theoretical capacity of 294 mAh g -1, which is much higher than conventional cathodes. But, there are many issues to be solved before its practical use, including poor cycle life and unsatisfactory rate performance, mainly owing to its low electronic conductivity and ionic diffusivity, as well as structural instability. Our work reports three types of V 2O 5 asymmetric membranes synthesized by using an adapted reverse-osmosis membrane technology combined with sol-gel chemistry, aiming to stabilize the cyclability andmore » improve the rate performance. V 2O 5 asymmetric membrane cathodes prepared using graphene as the conductive additives have a specific capacity of approximately 160 mAh g -1 at a current density of 100 mA g -1 with no capacity degradation after 380 cycles. It is also found that the annealing temperature and the choice of conductive additives can affect the morphology of V 2O 5 nanoparticles and the overall electrode cyclability. Furthermore, we find that a lower annealing temperature (300 vs. 400 °C) and the addition of graphene are beneficial to long-term cycling performance.« less

Reinvigorating Reverse-Osmosis Membrane Technology to Stabilize the V 2 O 5 Lithium-Ion Battery Cathode

DOE PAGES

Wu, Ji; Byrd, Ian; Jin, Congrui; ...

2017-02-27

V 2O 5 is deemed as one of the most promising cathode materials for next-generation high-capacity lithium-ion batteries (LIBs). It possesses a theoretical capacity of 294 mAh g -1, which is much higher than conventional cathodes. But, there are many issues to be solved before its practical use, including poor cycle life and unsatisfactory rate performance, mainly owing to its low electronic conductivity and ionic diffusivity, as well as structural instability. Our work reports three types of V 2O 5 asymmetric membranes synthesized by using an adapted reverse-osmosis membrane technology combined with sol-gel chemistry, aiming to stabilize the cyclability andmore » improve the rate performance. V 2O 5 asymmetric membrane cathodes prepared using graphene as the conductive additives have a specific capacity of approximately 160 mAh g -1 at a current density of 100 mA g -1 with no capacity degradation after 380 cycles. It is also found that the annealing temperature and the choice of conductive additives can affect the morphology of V 2O 5 nanoparticles and the overall electrode cyclability. Furthermore, we find that a lower annealing temperature (300 vs. 400 °C) and the addition of graphene are beneficial to long-term cycling performance.« less

Fabrication of three-dimensional buckypaper catalyst layer with Pt nanoparticles supported on polyelectrolyte functionalized carbon nanotubes for proton exchange membrane fuel cells

NASA Astrophysics Data System (ADS)

Zhu, Shiyao; Zheng, Junsheng; Huang, Jun; Dai, Ningning; Li, Ping; Zheng, Jim P.

2018-07-01

Polyelectrolyte poly(diallyldimethylammonium chloride) (PDDA) functionalized carbon nanotubes (CNTs) supported Pt electrocatalyst was synthesized as a substitute for commonly used Pt/C and Pt/CNTs (modified by harsh acid-oxidation treatment) catalysts. In addition, this catalyst was fabricated as the cathode catalyst layer (CL) with a unique double-layered structure for proton exchange membrane fuel cells (PEMFCs). Thermogravimetric analysis shows an enhanced thermal stability of Pt/PDDA-CNTs. The Pt/PDDA-CNTs catalyst with an average Pt particle size of ∼3.1 nm exhibits the best electrocatalytic activity and a significantly enhanced electrochemical stability. Scanning electron microscope, energy dispersive spectrometer and mercury intrusion porosimetry results demonstrate the gradient distribution of Pt content and pore size along the thickness of buckypaper catalyst layer (BPCL). The accelerated degradation test results of BPCLs indicate that this gradient structure can ensure a high Pt utilization in the BPCLs (up to 90%) and further improve the catalyst durability. In addition, the membrane electrode assembly (MEA) fabricated with cathode BPCL-PDDA shows the best single cell performance and long-term stability, and a reduction of Pt loading can be achieved. The feasibility of BPCL for improving the Pt utilization is also demonstrated by the cathode cyclic voltammetry in MEA.

Monitoring local redox processes in LiNi0.5Mn1.5O4 battery cathode material by in operando EPR spectroscopy.

PubMed

Niemöller, Arvid; Jakes, Peter; Eurich, Svitlana; Paulus, Anja; Kungl, Hans; Eichel, Rüdiger-A; Granwehr, Josef

2018-01-07

Despite the multitude of analytical methods available to characterize battery cathode materials, identifying the factors responsible for material aging is still challenging. We present the first investigation of transient redox processes in a spinel cathode during electrochemical cycling of a lithium ion battery by in operando electron paramagnetic resonance (EPR). The battery contains a LiNi 0.5 Mn 1.5 O 4 (LNMO) spinel cathode, which is a material whose magnetic interactions are well understood. The evolution of the EPR signal in combination with electrochemical measurements shows the impact of Mn 3+ on the Li + motion inside the spinel. Moreover, state of charge dependent linewidth variations confirm the formation of a solid solution for slow cycling, which is taken over by mixed models of solid solution and two-phase formation for fast cycling due to kinetic restrictions and overpotentials. Long-term measurements for 480 h showed the stability of the investigated LNMO, but also small amounts of cathode degradation products became visible. The results point out how local, exchange mediated magnetic interactions in cathode materials are linked with battery performance and can be used for material characterization.

Monitoring local redox processes in LiNi0.5Mn1.5O4 battery cathode material by in operando EPR spectroscopy

NASA Astrophysics Data System (ADS)

Niemöller, Arvid; Jakes, Peter; Eurich, Svitlana; Paulus, Anja; Kungl, Hans; Eichel, Rüdiger-A.; Granwehr, Josef

2018-01-01

Despite the multitude of analytical methods available to characterize battery cathode materials, identifying the factors responsible for material aging is still challenging. We present the first investigation of transient redox processes in a spinel cathode during electrochemical cycling of a lithium ion battery by in operando electron paramagnetic resonance (EPR). The battery contains a LiNi0.5Mn1.5O4 (LNMO) spinel cathode, which is a material whose magnetic interactions are well understood. The evolution of the EPR signal in combination with electrochemical measurements shows the impact of Mn3+ on the Li+ motion inside the spinel. Moreover, state of charge dependent linewidth variations confirm the formation of a solid solution for slow cycling, which is taken over by mixed models of solid solution and two-phase formation for fast cycling due to kinetic restrictions and overpotentials. Long-term measurements for 480 h showed the stability of the investigated LNMO, but also small amounts of cathode degradation products became visible. The results point out how local, exchange mediated magnetic interactions in cathode materials are linked with battery performance and can be used for material characterization.

Long-term evaluation of solid oxide fuel cell candidate materials in a 3-cell generic stack test fixture, part III: Stability and microstructure of Ce-(Mn,Co)-spinel coating, AISI441 interconnect, alumina coating, cathode and anode

NASA Astrophysics Data System (ADS)

Chou, Yeong-Shyung; Stevenson, Jeffry W.; Choi, Jung-Pyung

2014-07-01

A generic solid oxide fuel cell stack test fixture was developed to evaluate candidate materials and processing under realistic conditions. Part III of the work investigated the stability of Ce-(Mn,Co) spinel coating, AISI441 metallic interconnect, alumina coating, and cell's degradation. After 6000 h test, the spinel coating showed densification with some diffusion of Cr. At the metal interface, segregation of Si and Ti was observed, however, no continuous layer formed. The alumina coating for perimeter sealing areas appeared more dense and thick at the air side than the fuel side. Both the spinel and alumina coatings remained bonded. EDS analysis of Cr within the metal showed small decrease in concentration near the coating interface and would expect to cause no issue of Cr depletion. Inter-diffusion of Ni, Fe, and Cr between spot-welded Ni wire and AISI441 interconnect was observed and Cr-oxide scale formed along the circumference of the weld. The microstructure of the anode and cathode was discussed relating to degradation of the top and middle cells. Overall, the Ce-(Mn,Co) spinel coating, alumina coating, and AISI441 steel showed the desired long-term stability and the developed generic stack fixture proved to be a useful tool to validate candidate materials for SOFC.

Strategies to curb structural changes of lithium/transition metal oxide cathode materials & the changes’ effects on thermal & cycling stability

NASA Astrophysics Data System (ADS)

Xiqian, Yu; Enyuan, Hu; Seongmin, Bak; Yong-Ning, Zhou; Xiao-Qing, Yang

2016-01-01

Structural transformation behaviors of several typical oxide cathode materials during a heating process are reviewed in detail to provide in-depth understanding of the key factors governing the thermal stability of these materials. We also discuss applying the information about heat induced structural evolution in the study of electrochemically induced structural changes. All these discussions are expected to provide valuable insights for designing oxide cathode materials with significantly improved structural stability for safe, long-life lithium ion batteries, as the safety of lithium-ion batteries is a critical issue; it is widely accepted that the thermal instability of the cathodes is one of the most critical factors in thermal runaway and related safety problems. Project supported by the U.S. Department of Energy, the Assistant Secretary for Energy Efficiency and Renewable Energy, Office of Vehicle Technologies (Grant No. DE-SC0012704).

Facile Fabrication of Ethoxy-Functional Polysiloxane Wrapped LiNi0.6Co0.2Mn0.2O2 Cathode with Improved Cycling Performance for Rechargeable Li-Ion Battery.

PubMed

Wang, Hao; Ge, Wujie; Li, Wen; Wang, Feng; Liu, Wenjing; Qu, Mei-Zhen; Peng, Gongchang

2016-07-20

Dealing with the water molecule on the surface of LiNi0.6Co0.2Mn0.2O2 (NCM) cathode and hydrogen fluoride in the electrolyte is one of the most difficult challenges in Li-ion battery research. In this paper, the surface polymerization of tetraethyl orthosilicate (TEOS) on NCM to generate ethoxy-functional polysiloxane (EPS) wrapped NCM (E-NCM) cathode under mild conditions and without any additions is utilized to solve this intractable problem. The differential scanning calorimetry, transmission electron microscopy, and X-ray photoelectron spectroscopy results show that the formed amorphous coating can provide a protective shell to improve the NCM thermal stability, suppress the thickening of the solid electrolyte interphase (SEI) layer, and scavenge HF in the electrolyte. The E-NCM composite with 2 mol % EPS delivers a high discharge capacity retention of 84.9% after 100 cycles at a 1 C discharge rate in the 2.8-4.3 V potential range at 55 °C. Moreover, electrochemical impedance spectroscopy measurements reveal that the EPS coating could alleviate the impedance rise during cycling especially at an elevated temperature. Therefore, the fabricated E-NCM cathode with long-term cycling and thermal stability is a promising candidate for use in a high-energy Li-ion battery.

Preliminary Results of Field Emission Cathode Tests

NASA Technical Reports Server (NTRS)

Sovey, James S.; Kovaleski, Scott D.

2001-01-01

Preliminary screening tests of field emission cathodes such as chemical vapor deposited (CVD) diamond, textured pyrolytic graphite, and textured copper were conducted at background pressures typical of electric thruster test facilities to assess cathode performance and stability. Very low power electric thrusters which provide tens to hundreds micronewtons of thrust may need field emission neutralizers that have a capability of tens to hundreds of microamperes. From current voltage characteristics, it was found that the CVD diamond and textured metals cathodes clearly satisfied the Fowler-Nordheim emission relation. The CVD diamond and a textured copper cathode had average current densities of 270 and 380 mA/sq cm, respectively, at the beginning-of-life. After a few hours of operation the cathode emission currents degraded by 40 to 75% at background pressures in the 10(exp -5) Pa to 10(exp -4) Pa range. The textured pyrolytic graphite had a modest current density at beginning-of-life of 84 mA/sq cm, but this cathode was the most stable of all. Extended testing of the most promising cathodes is warranted to determine if current degradation is a burn-in effect or whether it is a long-term degradation process. Preliminary experiments with ferroelectric emission cathodes, which are ceramics with spontaneous electric polarization, were conducted. Peak current densities of 30 to 120 mA/sq cm were obtained for pulse durations of about 500 ns in the 10(exp -4) Pa pressure range.

Effect of current ripple on cathode erosion in 30 kWe class arcjets

NASA Technical Reports Server (NTRS)

Harris, William J.; O'Hair, Edgar A.; Hatfield, Lynn L.; Kristiansen, M.; Grimes, Montgomery D.

1991-01-01

An investigation was conducted to study the effect of current ripple on cathode erosion in 30 kWe class arcjets to determine the change in the cathode erosion rate for high (11 percent) and low (4 percent) current ripple. The measurements were conducted using a copper-tungsten cathode material to accelerate the cathode erosion process. It is shown that the high ripple erosion rate was initially higher than the low ripple erosion rate, but decreased asymptotically with time to a level less than half that of the low ripple value. Results suggest that high ripple extends the cathode lifetime for long duration operation, and improves arc stability by increasing the cathode attachment area.

Durability and regeneration of activated carbon air-cathodes in long-term operated microbial fuel cells

NASA Astrophysics Data System (ADS)

Zhang, Enren; Wang, Feng; Yu, Qingling; Scott, Keith; Wang, Xu; Diao, Guowang

2017-08-01

The performance of activated carbon catalyst in air-cathodes in microbial fuel cells was investigated over one year. A maximum power of 1722 mW m-2 was produced within the initial one-month microbial fuel cell operation. The air-cathodes produced a maximum power >1200 mW m-2 within six months, but gradually became a limiting factor for the power output in prolonged microbial fuel cell operation. The maximum power decreased by 55% when microbial fuel cells were operated over one year due to deterioration in activated carbon air-cathodes. While salt/biofilm removal from cathodes experiencing one-year operation increased a limiting performance enhancement in cathodes, a washing-drying-pressing procedure could restore the cathode performance to its original levels, although the performance restoration was temporary. Durable cathodes could be regenerated by re-pressing activated carbon catalyst, recovered from one year deteriorated air-cathodes, with new gas diffusion layer, resulting in ∼1800 mW m-2 of maximum power production. The present study indicated that activated carbon was an effective catalyst in microbial fuel cell cathodes, and could be recovered for reuse in long-term operated microbial fuel cells by simple methods.

Long-term cathode performance and the microbial communities that develop in microbial fuel cells fed different fermentation endproducts.

PubMed

Kiely, Patrick D; Rader, Geoffrey; Regan, John M; Logan, Bruce E

2011-01-01

To better understand how cathode performance and substrates affected communities that evolved in these reactors over long periods of time, microbial fuel cells were operated for more than 1 year with individual endproducts of lignocellulose fermentation (acetic acid, formic acid, lactic acid, succinic acid, or ethanol). Large variations in reactor performance were primarily due to the specific substrates, with power densities ranging from 835 ± 21 to 62 ± 1mW/m(3). Cathodes performance degraded over time, as shown by an increase in power of up to 26% when the cathode biofilm was removed, and 118% using new cathodes. Communities that developed on the anodes included exoelectrogenic families, such as Rhodobacteraceae, Geobacteraceae, and Peptococcaceae, with the Deltaproteobacteria dominating most reactors. Pelobacter propionicus was the predominant member in reactors fed acetic acid, and it was abundant in several other MFCs. These results provide valuable insights into the effects of long-term MFC operation on reactor performance. Copyright © 2010 Elsevier Ltd. All rights reserved.

Treatment with direct-current stimulation against cingulate seizure-like activity induced by 4-aminopyridine and bicuculline in an in vitro mouse model.

PubMed

Chang, Wei-Pang; Lu, Hsiang-Chin; Shyu, Bai-Chuang

2015-03-01

Clinical studies have shown that cathodal transcranial direct-current stimulation (tDCS) application can produce long-term suppressive effects on drug-resistant seizures. Whether this long-term effect produced by cathodal tDCS can counterbalance the enhancement of synaptic transmission during seizures requires further investigation. Our hypothesis was that the long-term effects of DCS on seizure suppression by the application of cathodal DCS occur through a long-term depression (LTD)-like mechanism. We used a thalamocingulate brain slice preparation combined with a multielectrode array and patch recording to investigate the underlying mechanism of the suppressive effect of DCS on anterior cingulate cortex (ACC) seizures. Patch-clamp recordings showed that cathodal DCS significantly decreased spontaneous excitatory postsynaptic currents (EPSCs) and epileptic EPSCs caused by the 4-aminopyridine. Fifteen minutes of DCS application reliably induced LTD, and the synaptic activation frequency was an important factor in LTD formation. The application of DCS alone without continuous synaptic activation did not induce LTD. Direct-current stimulation-induced LTD appeared to be N-methyl-d-aspartate (NMDA)-dependent, in which the application of the NMDA receptor antagonist D-1-2-amino-5-phosphonopentanoic acid (APV) abolished DCS-induced LTD, and the immediate effect remained. Direct-current stimulation-induced LTD and the long-term effects of DCS on seizure-like activities were also abolished by okadaic acid, a protein phosphatase 1 inhibitor. The long-term effects of DCS on seizures were not influenced by the depotentiation blocker FK-506. Therefore, we conclude that the long-term effects of DCS on seizure-like activities in brain slice occur through an LTD-like mechanism. Copyright © 2015 Elsevier Inc. All rights reserved.

Highly Durable Na2V6O16·1.63H2O Nanowire Cathode for Aqueous Zinc-Ion Battery.

PubMed

Hu, Ping; Zhu, Ting; Wang, Xuanpeng; Wei, Xiujuan; Yan, Mengyu; Li, Jiantao; Luo, Wen; Yang, Wei; Zhang, Wencui; Zhou, Liang; Zhou, Zhiqiang; Mai, Liqiang

2018-03-14

Rechargeable aqueous zinc-ion batteries are highly desirable for grid-scale applications due to their low cost and high safety; however, the poor cycling stability hinders their widespread application. Herein, a highly durable zinc-ion battery system with a Na 2 V 6 O 16 ·1.63H 2 O nanowire cathode and an aqueous Zn(CF 3 SO 3 ) 2 electrolyte has been developed. The Na 2 V 6 O 16 ·1.63H 2 O nanowires deliver a high specific capacity of 352 mAh g -1 at 50 mA g -1 and exhibit a capacity retention of 90% over 6000 cycles at 5000 mA g -1 , which represents the best cycling performance compared with all previous reports. In contrast, the NaV 3 O 8 nanowires maintain only 17% of the initial capacity after 4000 cycles at 5000 mA g -1 . A single-nanowire-based zinc-ion battery is assembled, which reveals the intrinsic Zn 2+ storage mechanism at nanoscale. The remarkable electrochemical performance especially the long-term cycling stability makes Na 2 V 6 O 16 ·1.63H 2 O a promising cathode for a low-cost and safe aqueous zinc-ion battery.

Cathode material for lithium ion accumulators prepared by screen printing for Smart Textile applications

NASA Astrophysics Data System (ADS)

Syrový, T.; Kazda, T.; Syrová, L.; Vondrák, J.; Kubáč, L.; Sedlaříková, M.

2016-03-01

The presented study is focused on the development of LiFePO4 based cathode for thin and flexible screen printed secondary lithium based accumulators. An ink formulation was developed for the screen printing technique, which enabled mass production of accumulator's cathode for Smart Label and Smart Textile applications. The screen printed cathode was compared with an electrode prepared by the bar coating technique using an ink formulation based on the standard approach of ink composition. Obtained LiFePO4 cathode layers were characterized by scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDS) and galvanostatic charge/discharge measurements at different loads. The discharge capacity, capacity retention and stability at a high C rate of the LiFePO4 cathode were improved when Super P and PVDF were replaced by conductive polymers PEDOT:PSS. The achieved capacity during cycling at various C rates was approximately the same at the beginning and at the end, and it was about 151 mAh/g for cycling under 1C. The obtained results of this novelty electrode layer exceed the parameters of several electrode layers based on LiFePO4 published in literature in terms of capacity, cycling stability and overcomes them in terms of simplicity/industrial process ability of cathode layer fabrication and electrode material preparation.

Activity and Stability of (Pr 1-xNd x) 2NiO 4+δ as Cathodes for Oxide Fuel Cells: Part VI. The Role of Cu Dopant on the Structure and Electrochemical Properties

DOE Office of Scientific and Technical Information (OSTI.GOV)

Dogdibegovic, Emir; Yan, Jingbo; Cai, Qinsheng

Phase instability in praseodymium nickelates is a major concern for the long-term operations of solid oxide fuel cells since it may lead to the performance degradation. In this work, praseodymium nickelates (ex. Pr 2NiO 4+δ) have been stabilized via substitution on both Pr- and Ni-sites. Systematic studies over a wide range of compositions were conducted via long-term thermal annealing studies (T ≤ 870°C) and electrochemical tests in full cells. Proposed (Pr 0.50Nd 0.50) 2Ni 1-yCu yO 4+δ compositions (y = 0.05, 0.10, 0.20, and 0.30) showed the most promising results and serve as a comprehensive extension to our previous studiesmore » in this series of papers. A stable long-term performance was obtained for temperatures up to 790°C for 500 hours at 0.80 V with a minimal tradeoff between the activity (power density of 0.8–1.0 W cm -2 at 850°C) and performance stability. A preserved parent phase and suppressed performance degradation, when compared to Pr 2NiO 4+δ, make newly developed electrodes attractive candidates for the state-of-the-art solid oxide fuel cell applications.« less

Activity and Stability of (Pr 1-xNd x) 2NiO 4+δ as Cathodes for Oxide Fuel Cells: Part VI. The Role of Cu Dopant on the Structure and Electrochemical Properties

DOE PAGES

Dogdibegovic, Emir; Yan, Jingbo; Cai, Qinsheng; ...

2017-08-12

Phase instability in praseodymium nickelates is a major concern for the long-term operations of solid oxide fuel cells since it may lead to the performance degradation. In this work, praseodymium nickelates (ex. Pr 2NiO 4+δ) have been stabilized via substitution on both Pr- and Ni-sites. Systematic studies over a wide range of compositions were conducted via long-term thermal annealing studies (T ≤ 870°C) and electrochemical tests in full cells. Proposed (Pr 0.50Nd 0.50) 2Ni 1-yCu yO 4+δ compositions (y = 0.05, 0.10, 0.20, and 0.30) showed the most promising results and serve as a comprehensive extension to our previous studiesmore » in this series of papers. A stable long-term performance was obtained for temperatures up to 790°C for 500 hours at 0.80 V with a minimal tradeoff between the activity (power density of 0.8–1.0 W cm -2 at 850°C) and performance stability. A preserved parent phase and suppressed performance degradation, when compared to Pr 2NiO 4+δ, make newly developed electrodes attractive candidates for the state-of-the-art solid oxide fuel cell applications.« less

Building Honeycomb-Like Hollow Microsphere Architecture in a Bubble Template Reaction for High-Performance Lithium-Rich Layered Oxide Cathode Materials.

PubMed

Chen, Zhaoyong; Yan, Xiaoyan; Xu, Ming; Cao, Kaifeng; Zhu, Huali; Li, Lingjun; Duan, Junfei

2017-09-13

In the family of high-performance cathode materials for lithium-ion batteries, lithium-rich layered oxides come out in front because of a high reversible capacity exceeding 250 mAh g -1 . However, the long-term energy retention and high energy densities for lithium-rich layered oxide cathode materials require a stable structure with large surface areas. Here we propose a "bubble template" reaction to build "honeycomb-like" hollow microsphere architecture for a Li 1.2 Mn 0.52 Ni 0.2 Co 0.08 O 2 cathode material. Our material is designed with ca. 8-μm-sized secondary particles with hollow and highly exposed porous structures that promise a large flexible volume to achieve superior structure stability and high rate capability. Our preliminary electrochemical experiments show a high capacity of 287 mAh g -1 at 0.1 C and a capacity retention of 96% after 100 cycles at 1.0 C. Furthermore, the rate capability is superior without any other modifications, reaching 197 mAh g -1 at 3.0 C with a capacity retention of 94% after 100 cycles. This approach may shed light on a new material engineering for high-performance cathode materials.

Behavior of Lithium Metal Anodes under Various Capacity Utilization and High Current Density in Lithium Metal Batteries

DOE Office of Scientific and Technical Information (OSTI.GOV)

Jiao, Shuhong; Zheng, Jianming; Li, Qiuyan

Lithium (Li) metal batteries (LMBs) are regarded as the most promising power sources for electric vehicles. Besides the Li dendrite growth and low Li Coulombic efficiency, how to well match Li metal anode with a high loading (normally over 3.0 mAh cm-2) cathode is another key challenge to achieve the real high energy density battery. In this work, we systematically investigate the effects of the Li metal capacity usage in each cycle, manipulated by varying the cathode areal loading, on the stability of Li metal anode and the cycling performance of LMBs using the LiNi1/3Mn1/3Co1/3O2 (NMC) cathode and an additive-containingmore » dual-salt/carbonate-solvent electrolyte. It is demonstrated that the Li||NMC cells show decent long-term cycling performance even with NMC areal capacity loading up to ca. 4.0 mAh cm-2 and at a charge current density of 1.0 mA cm-2. The increase of the Li capacity usage in each cycle causes variation in the components of the solid electrolyte interphase (SEI) layer on Li metal anode and generates more ionic conductive species from this electrolyte. Further study reveals for the first time that the degradation of Li metal anode and the thickness of SEI layer on Li anode show linear relationship with the areal capacity of NMC cathode. Meanwhile, the expansion rate of consumed Li and the ratio of SEI thickness to NMC areal loading are kept almost the same value with increasing cathode loading, respectively. These fundamental findings provide new perspectives on the rational evaluation of Li metal anode stability for the development of rechargeable LMBs.« less

On stabilization of field emission and increase in the current density of planar nanostructures with DLC films

NASA Astrophysics Data System (ADS)

Yakunin, Alexander N.; Aban'shin, Nikolay P.; Avetisyan, Yuri A.; Akchurin, Georgy G.; Loginov, Alexander P.; Mosiyash, Denis S.; Akchurin, Garif G.

2018-04-01

The paper provides a justification and a comparative analysis of the scaling directions of the developed and investigated planar triode field emission cathode unit with the aim of increasing the maximum field current density up to 0.75 A-cm-2 without sacrificing durability. The design features of the vacuum device with a planar structure provided low-voltage control - at 150 V in the mode of long-term durability and not more than 250 V in the mode of the maximum permissible emission current.

A new design of indirectly heated cathode based strip type electron gun.

PubMed

Maiti, Namita; Lijeesh, K; Barve, U D; Quadri, Nishad; Tembhare, G U; Mukherjee, S; Thakur, K B; Das, A K

2013-08-01

A new design of indirectly heated solid cathode based electron gun (200 kW, 45 kV, 270° bent strip type electron gun) has been presented. The design issue addressed is the uniformity of temperature on the solid cathode using (a) a multi-segmented filament with variable height as the primary heat source and (b) trapezoidal shaped single long filament as the primary heat source. The proposed design in this paper is based on computer simulation and validated by extensive experimentations. The design emphasis is on maintaining uniform temperature on the solid cathode. The designed multi-segment filament and the single long filament provide a temperature uniformity on the solid cathode of about 250 K and 110 K, respectively. The better temperature uniformity inspite of the thermal expansion, in case of a single long filament tightly clamped at two ends, has been possible due to shaping of the single filament with a number of constituent sections such that the thermal expansion of different sections forming the actual filament takes care of not only the mechanical stability but also does not affect the emitting surface of the filament. Experiments show that the modified design achieves a one to one correspondence of the solid cathode length and the electron beam length emitted from the solid cathode.

Electrospun single crystalline fork-like K2V8O21 as high-performance cathode materials for lithium-ion batteries

NASA Astrophysics Data System (ADS)

Hao, Pengfei; Zhu, Ting; Su, Qiong; Lin, Jiande; Cui, Rong; Cao, Xinxin; Wang, Yaping; Pan, Anqiang

2018-06-01

Single crystalline fork-like potassium vanadate (K2V8O21) has been successfully prepared through electrospinning combined with a subsequent annealing process. The as-obtained K2V8O21 forks show a unique layer-by-layer stacked structure with conductive carbon. When used as cathode materials for lithium-ion batteries, the as-prepared fork-like materials exhibit high specific discharge capacity and excellent cyclic stability. High specific discharge capacity of 200.2 mA h g-1 and 131.5 mA h g-1 can be delivered at the current densities of 50 mA g-1 and 500 mA g-1, respectively. Furthermore, the K2V8O21 electrodes exhibit excellent long-term cycling stability that maintain a capacity of 108.3 mA h g-1 after 300 cycles at 500 mA g-1 with a fading rate of only 0.054% per cycle, revealing their potential applications in next generation high-performance lithium-ion batteries.

Aligned Li+ Tunnels in Core-Shell Li(NixMnyCoz)O2@LiFePO4 Enhances Its High Voltage Cycling Stability as Li-ion Battery Cathode.

PubMed

Wu, Zhongzhen; Ji, Shunping; Liu, Tongchao; Duan, Yandong; Xiao, Shu; Lin, Yuan; Xu, Kang; Pan, Feng

2016-10-12

Layered transition-metal oxides (Li[Ni x Mn y Co z ]O 2 , NMC, or NMCxyz) due to their poor stability when cycled at a high operating voltage (>4.5 V) have limited their practical applications in industry. Earlier researches have identified Mn(II)-dissolution and some parasitic reactions between NMC surface and electrolyte, especially when NMC is charged to a high potential, as primarily factors responsible for the fading. In our previous work, we have achieved a capacity of NMC active material close to theoretical value and optimized its cycling performance by a depolarized carbon nanotubes (CNTs) network and an unique "pre-lithiation process" that generates an in situ organic coating (∼40 nm) to prevent Mn(II) dissolution and minimize the parasitic reactions. Unfortunately, this organic coating is not durable enough during a long-term cycling when the cathode operates at a high potential (>4.5 V). This work attempts to improve the surface protection of the NMC532 particles by applying an active inorganic coating consisting of nanosized- and crystal-orientated LiFePO 4 (LFP) (about 50 nm, exposed (010) face) to generate a core-shell nanostructure of Li(Ni x Mn y Co z )O 2 @LiFePO 4 . Transmission electron microscopy (TEM) and etching X-ray photoelectron spectroscopy have confirmed an intimate contact coating (about 50 nm) between the original structure of NMC and LFP single-particle with atomic interdiffusion at the core-shell interface, and an array of interconnected aligned Li + tunnels are observed at the interface by cross-sectional high-resolution TEM, which were formed by ball-milling and then strictly controlling the temperature below 100 °C. Batteries based on this modified NMC cathode material show a high reversible capacity when cycled between 3.0 and 4.6 V during a long-term cycling.

Influence of memory effect on the state-of-charge estimation of large-format Li-ion batteries based on LiFePO4 cathode

NASA Astrophysics Data System (ADS)

Shi, Wei; Wang, Jiulin; Zheng, Jianming; Jiang, Jiuchun; Viswanathan, Vilayanur; Zhang, Ji-Guang

2016-04-01

In this work, we systematically investigated the influence of the memory effect of LiFePO4 cathodes in large-format full batteries. The electrochemical performance of the electrodes used in these batteries was also investigated separately in half-cells to reveal their intrinsic properties. We noticed that the memory effect of LiFePO4/graphite cells depends not only on the maximum state of charge reached during the memory writing process, but is also affected by the depth of discharge reached during the memory writing process. In addition, the voltage deviation in a LiFePO4/graphite full battery is more complex than in a LiFePO4/Li half-cell, especially for a large-format battery, which exhibits a significant current variation in the region near its terminals. Therefore, the memory effect should be taken into account in advanced battery management systems to further extend the long-term cycling stabilities of Li-ion batteries using LiFePO4 cathodes.

Activity and Stability of (Pr 1-xNd x) 2NiO 4 as Cathodes for Solid Oxide Fuel Cells: Part V. In Situ Studies of Phase Evolution

DOE PAGES

Dogdibegovic, Emir; Alabri, Nawf S.; Wright, Christopher J.; ...

2017-08-12

This study is to complement an early report (the manuscript is attached for review purpose) on the role of interlayer on activity and performance stability in praseodymium nickelates. The aforementioned report showed a remarkable 48% increase in power density while switching from common GDC interlayer to a new interlayer chemistry (PGCO). Furthermore, a stable long-term performance was linked with suppressed reaction between the cathode and PGCO interlayer. In this article, we report in situ studies of the phase evolution. The high energy XRD studies at a synchrotron source showed fully suppressed phase transition in praseodymium nickelates with PGCO interlayer, whilemore » the electrodes on the GDC interlayer undergo substantial phase transformation. Furthermore, in operando and post-test XRD analyses shown fully suppressed structural changes in electrodes operated in full cells at 750°C and 0.80 V for 500 hours. SEM-EDS analysis showed that the formation of PrO x at the cathode-interlayer interface may play a role in a decrease of mechanical integrity of the interfaces, due to thermal expansion mismatch, leading to a local stress between the two phases. Furthermore, phase evolution at a narrow interface may propagate toward the electrode bulk, leading to structural changes Q1 and performance degradation.« less

Activity and Stability of (Pr 1-xNd x) 2NiO 4 as Cathodes for Solid Oxide Fuel Cells: Part V. In Situ Studies of Phase Evolution

DOE Office of Scientific and Technical Information (OSTI.GOV)

Dogdibegovic, Emir; Alabri, Nawf S.; Wright, Christopher J.

This study is to complement an early report (the manuscript is attached for review purpose) on the role of interlayer on activity and performance stability in praseodymium nickelates. The aforementioned report showed a remarkable 48% increase in power density while switching from common GDC interlayer to a new interlayer chemistry (PGCO). Furthermore, a stable long-term performance was linked with suppressed reaction between the cathode and PGCO interlayer. In this article, we report in situ studies of the phase evolution. The high energy XRD studies at a synchrotron source showed fully suppressed phase transition in praseodymium nickelates with PGCO interlayer, whilemore » the electrodes on the GDC interlayer undergo substantial phase transformation. Furthermore, in operando and post-test XRD analyses shown fully suppressed structural changes in electrodes operated in full cells at 750°C and 0.80 V for 500 hours. SEM-EDS analysis showed that the formation of PrO x at the cathode-interlayer interface may play a role in a decrease of mechanical integrity of the interfaces, due to thermal expansion mismatch, leading to a local stress between the two phases. Furthermore, phase evolution at a narrow interface may propagate toward the electrode bulk, leading to structural changes Q1 and performance degradation.« less

Physical model and experimental results of cathode erosion related to power supply ripple

NASA Technical Reports Server (NTRS)

Harris, W. J.; O'Hair, E. A.; Hatfield, L. L.; Kristiansen, M.

1992-01-01

This paper discusses the physical effects of power supply ripple on cathode erosion and cathode arc attachment in a water-cooled, 30 kW nitrogen arcjet. Experimental results are presented for 2 percent thoriated tungsten, which show that the long-term cathode erosion rate is a decreasing function of current ripple over the range 1-13 percent. Above this range, the cathode discharge becomes unstable, and the erosion rate rapidly increases. A qualitative model of this effect is given in terms of a magnetically induced radial motion of the arc column, and an overall increase in the cathode spot radius due to the higher peak current associated with higher ripple. The most important effect of power supply ripple is therefore shown to be its ability to collectively drive the cathode attachment away from the cathode center. This leads to an increase in the cathode attachment area, and a subsequent decrease in the cathode erosion rate.

A Hollow-Structured Manganese Oxide Cathode for Stable Zn-MnO₂ Batteries.

PubMed

Guo, Xiaotong; Li, Jianming; Jin, Xu; Han, Yehu; Lin, Yue; Lei, Zhanwu; Wang, Shiyang; Qin, Lianjie; Jiao, Shuhong; Cao, Ruiguo

2018-05-05

Aqueous rechargeable zinc-manganese dioxide (Zn-MnO₂) batteries are considered as one of the most promising energy storage devices for large scale-energy storage systems due to their low cost, high safety, and environmental friendliness. However, only a few cathode materials have been demonstrated to achieve stable cycling for aqueous rechargeable Zn-MnO₂ batteries. Here, we report a new material consisting of hollow MnO₂ nanospheres, which can be used for aqueous Zn-MnO₂ batteries. The hollow MnO₂ nanospheres can achieve high specific capacity up to ~405 mAh g −1 at 0.5 C. More importantly, the hollow structure of birnessite-type MnO₂ enables long-term cycling stability for the aqueous Zn-MnO₂ batteries. The excellent performance of the hollow MnO₂ nanospheres should be due to their unique structural properties that enable the easy intercalation of zinc ions.

Na2MnSiO4 as an attractive high capacity cathode material for sodium-ion battery

NASA Astrophysics Data System (ADS)

Law, Markas; Ramar, Vishwanathan; Balaya, Palani

2017-08-01

Here we report a polyanion-based cathode material for sodium-ion batteries, Na2MnSiO4, registering impressive sodium storage performances with discharge capacity of 210 mAh g-1 at an average voltage of 3 V at 0.1 C, along with excellent long-term cycling stability (500 cycles at 1 C). Insertion/extraction of ∼1.5 mol of sodium ion per formula unit of the silicate-based compound is reported and the utilisation of Mn2+ ⇋ Mn4+ redox couple is also demonstrated by ex-situ XPS. Besides, this study involves a systematic investigation of influence of the electrolyte additive (with different content) on the sodium storage performance of Na2MnSiO4. The electrolyte additive forms an optimum protective passivation film on the electrode surface, successfully reducing manganese dissolution.

Highly Rechargeable Lithium-CO2 Batteries with a Boron- and Nitrogen-Codoped Holey-Graphene Cathode.

PubMed

Qie, Long; Lin, Yi; Connell, John W; Xu, Jiantie; Dai, Liming

2017-06-06

Metal-air batteries, especially Li-air batteries, have attracted significant research attention in the past decade. However, the electrochemical reactions between CO 2 (0.04 % in ambient air) with Li anode may lead to the irreversible formation of insulating Li 2 CO 3 , making the battery less rechargeable. To make the Li-CO 2 batteries usable under ambient conditions, it is critical to develop highly efficient catalysts for the CO 2 reduction and evolution reactions and investigate the electrochemical behavior of Li-CO 2 batteries. Here, we demonstrate a rechargeable Li-CO 2 battery with a high reversibility by using B,N-codoped holey graphene as a highly efficient catalyst for CO 2 reduction and evolution reactions. Benefiting from the unique porous holey nanostructure and high catalytic activity of the cathode, the as-prepared Li-CO 2 batteries exhibit high reversibility, low polarization, excellent rate performance, and superior long-term cycling stability over 200 cycles at a high current density of 1.0 A g -1 . Our results open up new possibilities for the development of long-term Li-air batteries reusable under ambient conditions, and the utilization and storage of CO 2 . © 2017 Wiley-VCH Verlag GmbH & Co. KGaA, Weinheim.

Substantial Humic Acid Adsorption to Activated Carbon Air Cathodes Produces a Small Reduction in Catalytic Activity.

PubMed

Yang, Wulin; Watson, Valerie J; Logan, Bruce E

2016-08-16

Long-term operation of microbial fuel cells (MFCs) can result in substantial degradation of activated carbon (AC) air-cathode performance. To examine a possible role in fouling from organic matter in water, cathodes were exposed to high concentrations of humic acids (HA). Cathodes treated with 100 mg L(-1) HA exhibited no significant change in performance. Exposure to 1000 mg L(-1) HA decreased the maximum power density by 14% (from 1310 ± 30 mW m(-2) to 1130 ± 30 mW m(-2)). Pore blocking was the main mechanism as the total surface area of the AC decreased by 12%. Minimization of external mass transfer resistances using a rotating disk electrode exhibited only a 5% reduction in current, indicating about half the impact of HA adsorption was associated with external mass transfer resistance and the remainder was due to internal resistances. Rinsing the cathodes with deionized water did not restore cathode performance. These results demonstrated that HA could contribute to cathode fouling, but the extent of power reduction was relatively small in comparison to large mass of humics adsorbed. Other factors, such as biopolymer attachment, or salt precipitation, are therefore likely more important contributors to long-term fouling of MFC cathodes.

Alcohol-soluble interfacial fluorenes for inverted polymer solar cells: sequence induced spatial conformation dipole moment.

PubMed

Chen, Lie; Liu, Xiangfu; Wei, Yingkai; Wu, Feiyan; Chen, Yiwang

2016-01-21

Three fluorene-based alcohol-soluble organic small molecule electrolytes (SMEs) with different conjugated backbones, namely, TFTN-Br, FTFN-Br and FTTFN-Br, were designed as cathode interfacial layers for inverted polymer solar cells (i-PSCs). The insertion of SMEs to the ITO/active layer interfaces effectively lowered the energy barrier for electron transport and improved the inherent compatibility between the hydrophilic ITO and hydrophobic active layers. Due to these advantages, the device based on poly(3-hexylthiophene) (P3HT):(6,6)-phenyl-C61 butyric acid methyl ester (PC61BM) with TFTN-Br as the cathode interfacial layer achieved an improved power conversion efficiency (PCE) of 3.8%, which is a 26% improvement when compared to the standard device comprising ZnO cathode interfacial layers (PCE = 3.0%). Devices with FTFN-Br and FTTFN-Br also showed an improved PCE of 3.1% and 3.5%, respectively. The variation in device performance enhancement was found to be primarily correlated with the different conformation of their assembly onto the electrode caused by the joint sequence of the polar group of the SMEs, consequently impacting the dipole moment and interface morphology. In addition, introducing SMEs as the cathode interfacial layer also produced devices with long-term stability.

Alkaline anion exchange membrane water electrolysis: Effects of electrolyte feed method and electrode binder content

NASA Astrophysics Data System (ADS)

Cho, Min Kyung; Park, Hee-Young; Lee, Hye Jin; Kim, Hyoung-Juhn; Lim, Ahyoun; Henkensmeier, Dirk; Yoo, Sung Jong; Kim, Jin Young; Lee, So Young; Park, Hyun S.; Jang, Jong Hyun

2018-04-01

Herein, we investigate the effects of catholyte feed method and anode binder content on the characteristics of anion exchange membrane water electrolysis (AEMWE) to construct a high-performance electrolyzer, revealing that the initial AEMWE performance is significantly improved by pre-feeding 0.5 M aqueous KOH to the cathode. The highest long-term activity during repeated voltage cycling is observed for AEMWE operation in the dry cathode mode, for which the best long-term performance among membrane electrode assemblies (MEAs) featuring polytetrafluoroethylene (PTFE) binder-impregnated (5-20 wt%) anodes is detected for a PTFE content of 20 wt%. MEAs with low PTFE content (5 and 9 wt%) demonstrate high initial performance, rapid performance decay, and significant catalyst loss from the electrode during long-term operation, whereas the MEA with 20 wt% PTFE allows stable water electrolysis for over 1600 voltage cycles. Optimization of cell operating conditions (i.e., operation in dry cathode mode at an optimum anode binder content following an initial solution feed) achieves an enhanced water splitting current density (1.07 A cm-2 at 1.8 V) and stable long-term AEMWE performance (0.01% current density reduction per voltage cycle).

Nanostructured high-energy cathode materials for advanced lithium batteries

NASA Astrophysics Data System (ADS)

Sun, Yang-Kook; Chen, Zonghai; Noh, Hyung-Joo; Lee, Dong-Ju; Jung, Hun-Gi; Ren, Yang; Wang, Steve; Yoon, Chong Seung; Myung, Seung-Taek; Amine, Khalil

2012-11-01

Nickel-rich layered lithium transition-metal oxides, LiNi1-xMxO2 (M = transition metal), have been under intense investigation as high-energy cathode materials for rechargeable lithium batteries because of their high specific capacity and relatively low cost. However, the commercial deployment of nickel-rich oxides has been severely hindered by their intrinsic poor thermal stability at the fully charged state and insufficient cycle life, especially at elevated temperatures. Here, we report a nickel-rich lithium transition-metal oxide with a very high capacity (215 mA h g-1), where the nickel concentration decreases linearly whereas the manganese concentration increases linearly from the centre to the outer layer of each particle. Using this nano-functional full-gradient approach, we are able to harness the high energy density of the nickel-rich core and the high thermal stability and long life of the manganese-rich outer layers. Moreover, the micrometre-size secondary particles of this cathode material are composed of aligned needle-like nanosize primary particles, resulting in a high rate capability. The experimental results suggest that this nano-functional full-gradient cathode material is promising for applications that require high energy, long calendar life and excellent abuse tolerance such as electric vehicles.

Nanostructured high-energy cathode materials for advanced lithium batteries.

PubMed

Sun, Yang-Kook; Chen, Zonghai; Noh, Hyung-Joo; Lee, Dong-Ju; Jung, Hun-Gi; Ren, Yang; Wang, Steve; Yoon, Chong Seung; Myung, Seung-Taek; Amine, Khalil

2012-11-01

Nickel-rich layered lithium transition-metal oxides, LiNi(1-x)M(x)O(2) (M = transition metal), have been under intense investigation as high-energy cathode materials for rechargeable lithium batteries because of their high specific capacity and relatively low cost. However, the commercial deployment of nickel-rich oxides has been severely hindered by their intrinsic poor thermal stability at the fully charged state and insufficient cycle life, especially at elevated temperatures. Here, we report a nickel-rich lithium transition-metal oxide with a very high capacity (215 mA h g(-1)), where the nickel concentration decreases linearly whereas the manganese concentration increases linearly from the centre to the outer layer of each particle. Using this nano-functional full-gradient approach, we are able to harness the high energy density of the nickel-rich core and the high thermal stability and long life of the manganese-rich outer layers. Moreover, the micrometre-size secondary particles of this cathode material are composed of aligned needle-like nanosize primary particles, resulting in a high rate capability. The experimental results suggest that this nano-functional full-gradient cathode material is promising for applications that require high energy, long calendar life and excellent abuse tolerance such as electric vehicles.

Solid oxide membrane (SOM) process for ytterbium and silicon production from their oxides

NASA Astrophysics Data System (ADS)

Jiang, Yihong

The Solid oxide membrane (SOM) electrolysis is an innovative green technology that produces technologically important metals directly from their respective oxides. A yttria-stabilized zirconia (YSZ) tube, closed at one end is employed to separate the molten salt containing dissolved metal oxides from the anode inside the YSZ tube. When the applied electric potential between the cathode in the molten salt and the anode exceeds the dissociation potential of the desired metal oxides, oxygen ions in the molten salt migrate through the YSZ membrane and are oxidized at the anode while the dissolved metal cations in the flux are reduced to the desired metal at the cathode. Compared with existing metal production processes, the SOM process has many advantages such as one unit operation, less energy consumption, lower capital costs and zero carbon emission. Successful implementation of the SOM electrolysis process would provide a way to mitigate the negative environmental impact of the metal industry. Successful demonstration of producing ytterbium (Yb) and silicon (Si) directly from their respective oxides utilizing the SOM electrolysis process is presented in this dissertation. During the SOM electrolysis process, Yb2O3 was reduced to Yb metal on an inert cathode. The melting point of the supporting electrolyte (LiF-YbF3-Yb2O3) was determined by differential thermal analysis (DTA). Static stability testing confirmed that the YSZ tube was stable with the flux at operating temperature. Yb metal deposit on the cathode was confirmed by scanning electron microscopy (SEM) and energy dispersive x-ray spectroscopy (EDS). During the SOM electrolysis process for silicon production, a fluoride based flux based on BaF2, MgF2, and YF3 was engineered to serve as the liquid electrolyte for dissolving silicon dioxide. YSZ tube was used to separate the molten salt from an anode current collector in the liquid silver. Liquid tin was chosen as cathode to dissolve the reduced silicon during SOM electrolysis. After electrolysis, upon cooling, silicon crystals precipitated out from the Si-Sn liquid alloy. The presence of high-purity silicon crystals in the liquid tin cathode was confirmed by SEM/EDS. The fluoride based flux was also optimized to improve YSZ membrane stability for long-term use.

Long-term Effectiveness of Cathodic Protection Systems on Highway Structures

DOT National Transportation Integrated Search

2003-07-01

The Federal Highway Administration (FHWA) has concluded, on the basis of extensive research, that cathodic protection (CP), the technology used to mitigate corrosion of metals embedded in concrete, is the only rehabilitation technique that has proven...

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wang, Ziying; Lee, Jungwoo Z.; Xin, Huolin L.

All-solid-state lithium-ion batteries have the potential to not only push the current limits of energy density by utilizing Li metal, but also improve safety by avoiding flammable organic electrolyte. However, understanding the role of solid electrolyte – electrode interfaces will be critical to improve performance. In this paper, we conducted long term cycling on commercially available lithium cobalt oxide (LCO)/lithium phosphorus oxynitride (LiPON)/lithium (Li) cells at elevated temperature to investigate the interfacial phenomena that lead to capacity decay. STEM-EELS analysis of samples revealed a previously unreported disordered layer between the LCO cathode and LiPON electrolyte. This electrochemically inactive layer grewmore » in thickness leading to loss of capacity and increase of interfacial resistance when cycled at 80 °C. Finally, the stabilization of this layer through interfacial engineering is crucial to improve the long term performance of thin-film batteries especially under thermal stress.« less

Perfluorinated ionomer-enveloped sulfur cathodes for lithium-sulfur batteries.

PubMed

Song, Jongchan; Choo, Min-Ju; Noh, Hyungjun; Park, Jung-Ki; Kim, Hee-Tak

2014-12-01

Nafion is known to suppress the polysulfide (PS) shuttle effect, a major obstacle to achieving high capacity and long cycle life for lithium-sulfur batteries. However, elaborate control of the layer's configuration is required for high performance. In this regard, we designed a Nafion-enveloped sulfur cathode, where the Nafion layer is formed on the skin of the cathode, covering its surface and edge while not restricting the porosity. Discharge capacity and efficiency were enhanced with the enveloping configuration, demonstrating suppression of shuttle. The edge protection exhibited better cycling stability than an edge-open configuration. In the absence of the Nafion envelope, charged sulfur concentrated on the top region of the cathode because of the relatively lower PS concentration at the cathode surface. Surprisingly, for the Nafion-enveloped cathode, sulfur was evenly distributed along the cathode, indicating that the configuration imparts a uniform PS concentration within the cathode. © 2014 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

A High‐Voltage and High‐Capacity Li1+xNi0.5Mn1.5O4 Cathode Material: From Synthesis to Full Lithium‐Ion Cells

PubMed Central

Mancini, Marilena; Gabrielli, Giulio; Kinyanjui, Michael; Kaiser, Ute; Wohlfahrt‐Mehrens, Margret

2016-01-01

Abstract We report Co‐free, Li‐rich Li1+xNi0.5Mn1.5O4 (0

UV-Vis-NIR spectroelectrochemical and in situ conductance studies of unusual stability of n- and p-doped poly(dimethyldioctylquaterthiophene-alt-oxadiazole) under high cathodic and anodic polarizations.

PubMed

Pomerantz, Z; Levi, M D; Salitra, G; Demadrille, R; Fisyuk, A; Zaban, A; Aurbach, D; Pron, A

2008-02-21

Combined CV studies and UV-Vis-NIR spectroelectrochemical investigations revealed an unusual stability of the p- and n-doped PMOThOD in the wide potential window of 4 V. The n-doping process occurs in this polymer down to -2.7 V (vs. Ag/Ag+) in a non-destructive way with the characteristic development of the omega3 transition as a function of the doping level. In situ electronic transport studies revealed a high conductivity of the n-doped polymer which implies high mobility of the negatively charged carriers in the freshly doped PMOThOD film electrodes. An increase in the cathodic polarization, long-term cycling of the film electrodes, especially of higher thickness, results in a growing contribution of the negatively charged carriers trapping to the redox properties of the PMOThOD. The trapping of the charged carriers reduces gradually the electronic conductance of the PMOThOD film, but its effect on the redox-capacity of the film (in a typical scan rates range up to 50 mV s(-1)) is only minor.

Understanding the role of different conductive polymers in improving the nanostructured sulfur cathode performance.

PubMed

Li, Weiyang; Zhang, Qianfan; Zheng, Guangyuan; Seh, Zhi Wei; Yao, Hongbin; Cui, Yi

2013-01-01

Lithium sulfur batteries have brought significant advancement to the current state-of-art battery technologies because of their high theoretical specific energy, but their wide-scale implementation has been impeded by a series of challenges, especially the dissolution of intermediate polysulfides species into the electrolyte. Conductive polymers in combination with nanostructured sulfur have attracted great interest as promising matrices for the confinement of lithium polysulfides. However, the roles of different conductive polymers on the electrochemical performances of sulfur electrode remain elusive and poorly understood due to the vastly different structural configurations of conductive polymer-sulfur composites employed in previous studies. In this work, we systematically investigate the influence of different conductive polymers on the sulfur cathode based on conductive polymer-coated hollow sulfur nanospheres with high uniformity. Three of the most well-known conductive polymers, polyaniline (PANI), polypyrrole (PPY), and poly(3,4-ethylenedioxythiophene) (PEDOT), were coated, respectively, onto monodisperse hollow sulfur nanopsheres through a facile, versatile, and scalable polymerization process. The sulfur cathodes made from these well-defined sulfur nanoparticles act as ideal platforms to study and compare how coating thickness, chemical bonding, and the conductivity of the polymers affected the sulfur cathode performances from both experimental observations and theoretical simulations. We found that the capability of these three polymers in improving long-term cycling stability and high-rate performance of the sulfur cathode decreased in the order of PEDOT > PPY > PANI. High specific capacities and excellent cycle life were demonstrated for sulfur cathodes made from these conductive polymer-coated hollow sulfur nanospheres.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Chung, Sheng-Heng; Chang, Chi-Hao; Manthiram, Arumugam

Sulfur is an appealing cathode material for establishing advanced lithium batteries as it offers a high theoretical capacity of 1675 mA h g -1 at low material and operating costs. However, the lithium–sulfur (Li–S) electrochemical cells face several formidable challenges arising from both the materials chemistry (e.g., low electrochemical utilization of sulfur and severe polysulfide diffusion) and battery chemistry (e.g., dynamic and static instability and low sulfur loadings). Here in this study, we present the design of a core–shell cathode with a pure sulfur core shielded within a conductive shell-shaped electrode. The new electrode configuration allows Li–S cells to loadmore » with a high amount of sulfur (sulfur loadings of up to 30 mg cm -2 and sulfur content approaching 70 wt%). The core–shell cathodes demonstrate a superior dynamic and static electrochemical stability in Li–S cells. The high-loading cathodes exhibit (i) a high sulfur utilization of up to 97% at C/20–C/2 rates and (ii) a low self-discharge during long-term cell storage for a three-month rest period and at different cell-storage conditions. Finally, a polysulfide-trap cell configuration is designed to evidence the eliminations of polysulfide diffusion and to investigate the relationship between the electrode configuration and electrochemical characteristics. Finally, the comprehensive analytical results based on the high-loading cathodes suggest that (i) the core–shell cathode is a promising solution for designing highly reversible Li–S cells and (ii) the polysulfide-trap cell configuration is a viable approach to qualitatively evaluating the presence or absence of polysulfide diffusion.« less

The performance and long-term stability of low-cost separators in single-chamber bottle-type microbial fuel cells.

PubMed

Kondaveeti, Sanath; Kakarla, Ramesh; Kim, Hong Suck; Kim, Byung-Goon; Min, Booki

2018-02-01

This study evaluates long-term stability of low-cost separators in single-chamber bottle-type microbial fuel cells with domestic wastewater. Low-cost separators tested in this study were nonwoven fabrics (NWF) of polypropylene (PP80, PP100), textile fabrics of polyphenylene sulfide (PPS), sulfonated polyphenylene sulfide (SPPS), and cellulose esters. NWF PP80 separator generated the highest power density of 280 mW/m 2 , which was higher than with ion-exchange membranes (cation exchange membrane; CEM = 271 mW/m 2 , cation exchange membrane; CMI = 196 mW/m 2 , Nafion = 260 mW/m 2 ). MFC operations with other size-selective separators such as SPPS, PPS, and cellulose esters exhibited power densities of 261, 231, and 250 mW/m 2 , respectively. During a 280-day operation, initial power density of PP80 (278 mW/m 2 ) was decreased to 257 mW/m 2 , but this decrease was smaller than with others (Nafion: 265-230 mW/m 2 ; PP100: 220-126 mW/m 2 ). The anode potential of around -430 mV did not change much with all separators in the long-term operation, but the initial cathode potential gradually decreased. Fouling analysis suggested that the presence of carbonaceous substance on Nafion and PP80 after 280 days of operation and Nafion was subject to be more biofouling.

Atomic to Nanoscale Investigation of Functionalities of Al2O3 Coating Layer on Cathode for Enhanced Battery Performance

DOE Office of Scientific and Technical Information (OSTI.GOV)

Yan, Pengfei; Zheng, Jianming; Zhang, Xiaofeng

2016-01-06

Surface coating of cathode has been identified as an effective approach for enhancing the capacity retention of layered structure cathode. However, the underlying operating mechanism of such a thin layer of coating, in terms of surface chemical functionality and capacity retention, remains unclear. In this work, we use aberration corrected scanning transmission electron microscopy and high efficient spectroscopy to probe the delicate functioning mechanism of Al2O3 coating layer on Li1.2Ni0.2Mn0.6O2 cathode. We discovered that in terms of surface chemical function, the Al2O3 coating suppresses the side reaction between cathode and the electrolyte upon the battery cycling. At the same time,more » the Al2O3 coating layer also eliminates the chemical reduction of Mn from the cathode particle surface, therefore avoiding the dissolution of the reduced Mn into the electrolyte. In terms of structural stability, we found that the Al2O3 coating layer can mitigate the layer to spinel phase transformation, which otherwise will initiate from the particle surface and propagate towards the interior of the particle with the progression of the battery cycling. The atomic to nanoscale effects of the coating layer observed here provide insight for optimized design of coating layer on cathode to enhance the battery properties.« less

Cation-Deficient Spinel ZnMn2O4 Cathode in Zn(CF3SO3)2 Electrolyte for Rechargeable Aqueous Zn-Ion Battery.

PubMed

Zhang, Ning; Cheng, Fangyi; Liu, Yongchang; Zhao, Qing; Lei, Kaixiang; Chen, Chengcheng; Liu, Xiaosong; Chen, Jun

2016-10-05

Rechargeable aqueous Zn-ion batteries are attractive cheap, safe and green energy storage technologies but are bottlenecked by limitation in high-capacity cathode and compatible electrolyte to achieve satisfactory cyclability. Here we report the application of nonstoichiometric ZnMn 2 O 4 /carbon composite as a new Zn-insertion cathode material in aqueous Zn(CF 3 SO 3 ) 2 electrolyte. In 3 M Zn(CF 3 SO 3 ) 2 solution that enables ∼100% Zn plating/stripping efficiency with long-term stability and suppresses Mn dissolution, the spinel/carbon hybrid exhibits a reversible capacity of 150 mAh g -1 and a capacity retention of 94% over 500 cycles at a high rate of 500 mA g -1 . The remarkable electrode performance results from the facile charge transfer and Zn insertion in the structurally robust spinel featuring small particle size and abundant cation vacancies, as evidenced by combined electrochemical measurements, XRD, Raman, synchrotron X-ray absorption spectroscopy, FTIR, and NMR analysis. The results would enlighten and promote the use of cation-defective spinel compounds and trifluoromethanesulfonic electrolyte to develop high-performance rechargeable zinc batteries.

A sodium–aluminum hybrid battery

DOE PAGES

Sun, Xiao-Guang; Zhang, Zhizhen; Guan, Hong Yu; ...

2017-03-07

We present novel hybrid batteries that are fabricated using an aluminum anode, a sodium intercalation cathode Na 3V 2(PO 4) 3 (NVP), and a sodium/aluminum dual salt electrolyte based on NaAlCl 4 and an eutectic mixture of 1-ethyl-3-methylimidazolium chloride (EMImC) and aluminum chloride. Cyclic voltammograms indicate that increasing the molar concentration of AlCl 3 in the electrolyte is beneficial to high coulombic efficiency of aluminum deposition/stripping, which, unfortunately, results in lower coulombic efficiency of sodium extraction/insertion in the cathode. Therefore, EMImC–AlCl 3 with a molar ratio of 1–1.1 is used for battery evaluation. The hybrid battery with 1.0 M NaAlClmore » 4 exhibits a discharge voltage of 1.25 V and a cathodic capacity of 99 mA h g -1 at a current rate of C/10. In addition, the hybrid battery exhibits good rate performance and long-term cycling stability while maintaining a high coulombic efficiency of 98%. It is also demonstrated that increasing salt concentration can further enhance the cycling performance of the hybrid battery. X-ray diffraction analysis of the NVP electrodes under different conditions confirms that the main cathode reaction is indeed Na extraction/insertion. Based on all earth-abundant elements, the new Na–Al hybrid battery is very attractive for stationary and grid energy storage applications.« less

A sodium–aluminum hybrid battery

DOE Office of Scientific and Technical Information (OSTI.GOV)

Sun, Xiao-Guang; Zhang, Zhizhen; Guan, Hong Yu

We present novel hybrid batteries that are fabricated using an aluminum anode, a sodium intercalation cathode Na 3V 2(PO 4) 3 (NVP), and a sodium/aluminum dual salt electrolyte based on NaAlCl 4 and an eutectic mixture of 1-ethyl-3-methylimidazolium chloride (EMImC) and aluminum chloride. Cyclic voltammograms indicate that increasing the molar concentration of AlCl 3 in the electrolyte is beneficial to high coulombic efficiency of aluminum deposition/stripping, which, unfortunately, results in lower coulombic efficiency of sodium extraction/insertion in the cathode. Therefore, EMImC–AlCl 3 with a molar ratio of 1–1.1 is used for battery evaluation. The hybrid battery with 1.0 M NaAlClmore » 4 exhibits a discharge voltage of 1.25 V and a cathodic capacity of 99 mA h g -1 at a current rate of C/10. In addition, the hybrid battery exhibits good rate performance and long-term cycling stability while maintaining a high coulombic efficiency of 98%. It is also demonstrated that increasing salt concentration can further enhance the cycling performance of the hybrid battery. X-ray diffraction analysis of the NVP electrodes under different conditions confirms that the main cathode reaction is indeed Na extraction/insertion. Based on all earth-abundant elements, the new Na–Al hybrid battery is very attractive for stationary and grid energy storage applications.« less

DOE Office of Scientific and Technical Information (OSTI.GOV)

Hu, Enyuan; Wang, Xuelong; Yu, Xiqian

The rechargeable lithium-ion battery (LIB) is the most promising energy storage system to power electric vehicles with high energy density and long cycling life. However, in order to meet customers’ demands for fast charging, the power performances of current LIBs need to be improved. From the cathode aspect, layer-structured cathode materials are widely used in today’s market and will continue to play important roles in the near future. The high rate capability of layered cathode materials during charging and discharging is critical to the power performance of the whole cell and the thermal stability is closely related to the safetymore » issues. Therefore, the in-depth understanding of structural changes of layered cathode materials during high rate charging/discharging and the thermal stability during heating are essential in developing new materials and improving current materials. Since structural changes take place from the atomic level to the whole electrode level, combination of characterization techniques covering multilength scales is quite important. Finally, in many cases, this means using comprehensive tools involving diffraction, spectroscopy, and imaging to differentiate the surface from the bulk and to obtain structural/chemical information with different levels of spatial resolution.« less

Strong Capillarity, Chemisorption, and Electrocatalytic Capability of Crisscrossed Nanostraws Enabled Flexible, High-Rate, and Long-Cycling Lithium-Sulfur Batteries.

PubMed

Ma, Lianbo; Zhang, Wenjun; Wang, Lei; Hu, Yi; Zhu, Guoyin; Wang, Yanrong; Chen, Renpeng; Chen, Tao; Tie, Zuoxiu; Liu, Jie; Jin, Zhong

2018-05-22

The development of flexible lithium-sulfur (Li-S) batteries with high energy density and long cycling life are very appealing for the emerging flexible, portable, and wearable electronics. However, the progress on flexible Li-S batteries was limited by the poor flexibility and serious performance decay of existing sulfur composite cathodes. Herein, we report a freestanding and highly flexible sulfur host that can simultaneously meet the flexibility, stability, and capacity requirements of flexible Li-S batteries. The host consists of a crisscrossed network of carbon nanotubes reinforced CoS nanostraws (CNTs/CoS-NSs). The CNTs/CoS-NSs with large inner space and high conductivity enable high loading and efficient utilization of sulfur. The strong capillarity effect and chemisorption of CNTs/CoS-NSs to sulfur species were verified, which can efficiently suppress the shuttle effect and promote the redox kinetics of polysulfides. The sulfur-encapsulated CNTs/CoS-NSs (S@CNTs/CoS-NSs) cathode in Li-S batteries exhibits superior performance, including high discharge capacity, rate capability (1045 mAh g -1 at 0.5 C and 573 mAh g -1 at 5.0 C), and cycling stability. Intriguingly, the soft-packed Li-S batteries based on S@CNTs/CoS-NSs cathode show good flexibility and stability upon bending.

Development of advanced fuel cell system, phase 3

NASA Technical Reports Server (NTRS)

Handley, L. M.; Meyer, A. P.; Bell, W. F.

1975-01-01

A multiple task research and development program was performed to improve the weight, life, and performance characteristics of hydrogen-oxygen alkaline fuel cells for advanced power systems. Gradual wetting of the anode structure and subsequent long-term performance loss was determined to be caused by deposition of a silicon-containing material on the anode. This deposit was attributed to degradation of the asbestos matrix, and attention was therefore placed on development of a substitute matrix of potassium titanate. An 80 percent gold 20 percent platinum catalyst cathode was developed which has the same performance and stability as the standard 90 percent gold - 10 percent platinum cathode but at half the loading. A hybrid polysulfone/epoxy-glass fiber frame was developed which combines the resistance to the cell environment of pure polysulfone with the fabricating ease of epoxy-glass fiber laminate. These cell components were evaluated in various configurations of full-size cells. The ways in which the baseline engineering model system would be modified to accommodate the requirements of the space tug application are identified.

A core–shell electrode for dynamically and statically stable Li–S battery chemistry

DOE PAGES

Chung, Sheng-Heng; Chang, Chi-Hao; Manthiram, Arumugam

2016-08-17

Sulfur is an appealing cathode material for establishing advanced lithium batteries as it offers a high theoretical capacity of 1675 mA h g -1 at low material and operating costs. However, the lithium–sulfur (Li–S) electrochemical cells face several formidable challenges arising from both the materials chemistry (e.g., low electrochemical utilization of sulfur and severe polysulfide diffusion) and battery chemistry (e.g., dynamic and static instability and low sulfur loadings). Here in this study, we present the design of a core–shell cathode with a pure sulfur core shielded within a conductive shell-shaped electrode. The new electrode configuration allows Li–S cells to loadmore » with a high amount of sulfur (sulfur loadings of up to 30 mg cm -2 and sulfur content approaching 70 wt%). The core–shell cathodes demonstrate a superior dynamic and static electrochemical stability in Li–S cells. The high-loading cathodes exhibit (i) a high sulfur utilization of up to 97% at C/20–C/2 rates and (ii) a low self-discharge during long-term cell storage for a three-month rest period and at different cell-storage conditions. Finally, a polysulfide-trap cell configuration is designed to evidence the eliminations of polysulfide diffusion and to investigate the relationship between the electrode configuration and electrochemical characteristics. Finally, the comprehensive analytical results based on the high-loading cathodes suggest that (i) the core–shell cathode is a promising solution for designing highly reversible Li–S cells and (ii) the polysulfide-trap cell configuration is a viable approach to qualitatively evaluating the presence or absence of polysulfide diffusion.« less

Atomic to Nanoscale Investigation of Functionalities of an Al2O3 Coating Layer on a Cathode for Enhanced Battery Performance

DOE Office of Scientific and Technical Information (OSTI.GOV)

Yan, Pengfei; Zheng, Jianming; Zhang, Xiaofeng

2016-02-09

Surface coating has been identified as an effective approach for enhancing the capacity retention of layered structure cathode. However, the underlying operating mechanism of such a thin coating layer, in terms of surface chemical functionality and capacity retention, remains unclear. In this work, we use aberration-corrected scanning transmission electron microscopy and high-efficiency spectroscopy to probe the delicate functioning mechanism of an Al2O3 coating layer on a Li1.2Ni0.2Mn0.6O2 cathode. We discovered that in terms of surface chemical function, the Al2O3 coating suppresses the side reaction between the cathode and the electrolyte during battery cycling. At the same time, the Al2O3 coatingmore » layer also eliminates the chemical reduction of Mn from the cathode particle surface, therefore preventing the dissolution of the reduced Mn into the electrolyte. In terms of structural stability, we found that the Al2O3 coating layer can mitigate the layer to spinel phase transformation, which otherwise will be initiated from the particle surface and propagate toward the interior of the particle with the progression of battery cycling. The atomic to nanoscale effects of the coating layer observed here provide insight into the optimized design of a coating layer on a cathode to enhance the battery properties.« less

Characterization of the NEXT Hollow Cathode Inserts After Long-Duration Testing

NASA Technical Reports Server (NTRS)

Mackey, J.; Shastry, R.; Soulas, G.

2017-01-01

Hollow dispenser cathode inserts are a critical element of electric propulsion systems, and should therefore be well understood during long term operation to ensure reliable system performance. This work destructively investigated cathode inserts from the NEXT long-duration test which demonstrated 51,184 hours of high-voltage operation, 918 kg of propellant throughput, and 35.5 MN-s of total impulse. The characterization methods used include scanning electron microscopy with energy dispersive spectroscopy and X-ray diffraction. Microscopy analysis has been performed on fractured surfaces, emission surfaces, and metallographically polished cross-sections of post-test inserts and unused inserts. Impregnate distribution, etch region thickness, impregnate chemical content, emission surface topography, and emission surface phase identification are the primary factors investigated.

Probing the Complexities of Structural Changes in Layered Oxide Cathode Materials for Li-Ion Batteries during Fast Charge–Discharge Cycling and Heating

DOE PAGES

Hu, Enyuan; Wang, Xuelong; Yu, Xiqian; ...

2018-01-19

The rechargeable lithium-ion battery (LIB) is the most promising energy storage system to power electric vehicles with high energy density and long cycling life. However, in order to meet customers’ demands for fast charging, the power performances of current LIBs need to be improved. From the cathode aspect, layer-structured cathode materials are widely used in today’s market and will continue to play important roles in the near future. The high rate capability of layered cathode materials during charging and discharging is critical to the power performance of the whole cell and the thermal stability is closely related to the safetymore » issues. Therefore, the in-depth understanding of structural changes of layered cathode materials during high rate charging/discharging and the thermal stability during heating are essential in developing new materials and improving current materials. Since structural changes take place from the atomic level to the whole electrode level, combination of characterization techniques covering multilength scales is quite important. Finally, in many cases, this means using comprehensive tools involving diffraction, spectroscopy, and imaging to differentiate the surface from the bulk and to obtain structural/chemical information with different levels of spatial resolution.« less

High Energy Density Li-ion Cells for EV’s Based on Novel, High Voltage Cathode Material Systems

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kepler, Keith D.; Slater, Michael

This Li-ion cell technology development project had three objectives: to develop advanced electrode materials and cell components to enable stable high-voltage operation; to design and demonstrate a Li-ion cell using these materials that meets the PHEV40 performance targets; and to design and demonstrate a Li-ion cell using these materials that meets the EV performance targets. The major challenge to creating stable high energy cells with long cycle life is system integration. Although materials that can give high energy cells are known, stabilizing them towards long-term cycling in the presence of other novel cell components is a major challenge. The majormore » technical barriers addressed by this work include low cathode specific energy, poor electrolyte stability during high voltage operation, and insufficient capacity retention during deep discharge for Si-containing anodes. Through the course of this project, Farasis was able to improve capacity retention of NCM materials for 4.4+ V operation, through both surface treatment and bulk-doping approaches. Other material advances include increased rate capability and of HE-NCM materials through novel synthesis approach, doubling the relative capacity at 1C over materials synthesized using standard methods. Silicon active materials proved challenging throughout the project and ultimately were the limiting factor in the energy density vs. cycle life trade off. By avoiding silicon anodes for the lower energy PHEV design, we manufactured cells with intermediate energy density and long cycle life under high voltage operation for PHEV applications. Cells with high energy density for EV applications were manufactured targeting a 300 Wh/kg design and were able to achieve > 200 cycles.« less

Mosaic-shaped cathode for highly durable solid oxide fuel cell under thermal stress

NASA Astrophysics Data System (ADS)

Joo, Jong Hoon; Jeong, Jaewon; Kim, Se Young; Yoo, Chung-Yul; Jung, Doh Won; Park, Hee Jung; Kwak, Chan; Yu, Ji Haeng

2014-02-01

In this study, we propose a novel "mosaic structure" for a SOFC (solid oxide fuel cell) cathode with high thermal expansion to improve the stability against thermal stress. Self-organizing mosaic-shaped cathode has been successfully achieved by controlling the amount of binder in the dip-coating solution. The anode-supported cell with mosaic-shaped cathode shows itself to be highly durable performance for rapid thermal cycles, however, the performance of the cell with a non-mosaic cathode exhibits severe deterioration originated from the delamination at the cathode/electrolyte interface after 7 thermal cycles. The thermal stability of an SOFC cathode can be evidently improved by controlling the surface morphology. In view of the importance of the thermal expansion properties of the cathode, the effects of cathode morphology on the thermal stress stability are discussed.

First-Principles Study on the Thermal Stability of LiNiO2 Materials Coated by Amorphous Al2O3 with Atomic Layer Thickness.

PubMed

Kang, Joonhee; Han, Byungchan

2015-06-03

Using first-principles calculations, we study how to enhance thermal stability of high Ni compositional cathodes in Li-ion battery application. Using the archetype material LiNiO2 (LNO), we identify that ultrathin coating of Al2O3 (0001) on LNO(012) surface, which is the Li de-/intercalation channel, substantially improves the instability problem. Density functional theory calculations indicate that the Al2O3 deposits show phase transition from the corundum-type crystalline (c-Al2O3) to amorphous (a-Al2O3) structures as the number of coating layers reaches three. Ab initio molecular dynamic simulations on the LNO(012) surface coated by a-Al2O3 (about 0.88 nm) with three atomic layers oxygen gas evolution is strongly suppressed at T=400 K. We find that the underlying mechanism is the strong contacting force at the interface between LNO(012) and Al2O3 deposits, which, in turn, originated from highly ionic chemical bonding of Al and O at the interface. Furthermore, we identify that thermodynamic stability of the a-Al2O3 is even more enhanced with Li in the layer, implying that the protection for the LNO(012) surface by the coating layer is meaningful over the charging process. Our approach contributes to the design of innovative cathode materials with not only high-energy capacity but also long-term thermal and electrochemical stability applicable for a variety of electrochemical energy devices including Li-ion batteries.

Niobium Doped Lanthanum Strontium Ferrite as A Redox-Stable and Sulfur-Tolerant Anode for Solid Oxide Fuel Cells.

PubMed

Li, Jingwei; Wei, Bo; Cao, Zhiqun; Yue, Xing; Zhang, Yaxin; Lü, Zhe

2018-01-10

The Nb-doped lanthanum strontium ferrite perovskite oxide La 0.8 Sr 0.2 Fe 0.9 Nb 0.1 O 3-δ (LSFNb) is evaluated as an anode material in a solid oxide fuel cell (SOFC). The effects of Nb partial substitution in the crystal structure, the electrical conductivity, and the valence of Fe ions are studied. LSFNb exhibits good structural stability in a severe reducing atmosphere at 800 °C, suggesting that high-valent Nb can effectively promote the stability of the lattice structure. The concentration of Fe 2+ increases after Nb doping, as confirmed by X-ray photoelectron spectroscopy. The maximum power density of a thick Sc-stabilized zirconia (ScSZ) electrolyte-supported single cell reached 241.6 mW cm -2 at 800 °C with H 2 as fuel. The cell exhibited excellent stability for 100 h continuous operation without detectable degeneration. Scanning electron microscopy clearly revealed exsolution on the LSFNb surface after operation. Meanwhile, LSFNb particles agglomerated significantly during long-term stability testing. Impedance spectra suggested that both the LSFNb anode and the (La 0.75 Sr 0.25 ) 0.95 MnO 3-δ /ScSZ cathode underwent an activation process during long-term testing, through which the charge transfer ability increased significantly. Meanwhile, low-frequency resistance (R L ) mainly attributed to the anode (80 %) significantly increased, probably due to the agglomeration of LSFNb particles. The LSFNb anode exhibits excellent anti-sulfuring poisoning ability and redox stability. These results demonstrate that LSFNb is a promising anode material for SOFCs. © 2018 Wiley-VCH Verlag GmbH & Co. KGaA, Weinheim.

Zirconia coating stabilized super-iron alkaline cathodes

NASA Astrophysics Data System (ADS)

Yu, Xingwen; Licht, Stuart

A low-level zirconia coating significantly stabilizes high energy alkaline super-iron cathodes, and improves the energy storage capacity of super-iron batteries. Zirconia coating is derived from ZrCl 4 in an organic medium through the conversion of ZrCl 4 to ZrO 2. In alkaline battery system, ZrO 2 provides an intact shield for the cathode materials and the hydroxide shuttle through the coating sustains alkaline cathode redox chemistry. Most super-iron cathodes are solid-state stable, such as K 2FeO 4 and Cs 2FeO 4, but tend to be passivated in alkaline electrolyte due to the formation of Fe(III) over layer. Zirconia coating effectively enhances the stability of these super-iron cathodes. However, for solid-state unstable super-iron cathode (e.g. BaFeO 4), only a little stabilization effect of zirconia coating is observed.

Molybdenum Carbide Nanoparticles on Carbon Nanotubes and Carbon Xerogel: Low-Cost Cathodes for Hydrogen Production by Alkaline Water Electrolysis.

PubMed

Šljukić, Biljana; Santos, Diogo M F; Vujković, Milica; Amaral, Luís; Rocha, Raquel P; Sequeira, César A C; Figueiredo, José L

2016-05-23

Low-cost molybdenum carbide (Mo2 C) nanoparticles supported on carbon nanotubes (CNTs) and on carbon xerogel (CXG) were prepared and their activity for the hydrogen evolution reaction (HER) was evaluated in 8 m KOH aqueous electrolyte at 25-85 °C. Measurements of the HER by linear scan voltammetry allowed us to determine Tafel slopes of 71 and 74 mV dec(-1) at 25 °C for Mo2 C/CNT and Mo2 C/CXG, respectively. Stability tests were also performed, which showed the steady performance of the two electrocatalysts. Moreover, the HER kinetics at Mo2 C/CNT was enhanced significantly after the long-term stability tests. The specific activity of both materials was high, and a higher stability was obtained for the activated Mo2 C/CNT (40 A g(-1) at -0.40 V vs. the reversible hydrogen electrode). © 2016 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Enhanced oxygen reduction activity and solid oxide fuel cell performance with a nanoparticles-loaded cathode.

PubMed

Zhang, Xiaomin; Liu, Li; Zhao, Zhe; Tu, Baofeng; Ou, Dingrong; Cui, Daan; Wei, Xuming; Chen, Xiaobo; Cheng, Mojie

2015-03-11

Reluctant oxygen-reduction-reaction (ORR) activity has been a long-standing challenge limiting cell performance for solid oxide fuel cells (SOFCs) in both centralized and distributed power applications. We report here that this challenge has been tackled with coloading of (La,Sr)MnO3 (LSM) and Y2O3 stabilized zirconia (YSZ) nanoparticles within a porous YSZ framework. This design dramatically improves ORR activity, enhances fuel cell output (200-300% power improvement), and enables superior stability (no observed degradation within 500 h of operation) from 600 to 800 °C. The improved performance is attributed to the intimate contacts between nanoparticulate YSZ and LSM particles in the three-phase boundaries in the cathode.

Achieving high capacity and rate capability in layered lithium transition metal oxide cathodes for lithium-ion batteries

NASA Astrophysics Data System (ADS)

Ahn, Juhyeon; Susanto, Dieky; Noh, Jae-Kyo; Ali, Ghulam; Cho, Byung Won; Chung, Kyung Yoon; Kim, Jong Hak; Oh, Si Hyoung

2017-08-01

In this study, we target to find a new composition for a layered mixed metal oxide, which has a high structural stability and a good electrochemical performance. Our strategy is to alter the transition metal composition focusing on the relative amounts of redox active Ni and Co to the inactive Mn, based on highly-stabilized LiNi1/3Co1/3Mn1/3O2. X-ray absorption near-edge structure and X-ray diffraction analyses show that the degree of cation disorder decreases on increasing the ratio of Ni and Co to Mn, by the presence of Ni3+, suggesting that slightly higher Ni and Co contents lead to improved structural stability. Electrochemical studies demonstrate that LiNi0.4Co0.4Mn0.2O2 cathodes exhibit considerable improvements in both the reversible capacity and the rate capabilities at a voltage range of 2.5-4.6 V. In situ XRD measurements reveal that LiNi0.4Co0.4Mn0.2O2 maintains a single-phase and undergoes lesser structural variations compared to controlled compositions during a delithiation process up to 4.6 V, while achieving a high reversible capacity over 200 mAh g-1. As a result, LiNi0.4Co0.4Mn0.2O2 experiences fewer structural degradations during electrochemical cycling, which explains the excellent long-term cycling performance.

FePO4 based single chamber air-cathode microbial fuel cell for online monitoring levofloxacin.

PubMed

Zeng, Libin; Li, Xinyong; Shi, Yueran; Qi, Yefei; Huang, Daqiong; Tadé, Moses; Wang, Shaobin; Liu, Shaomin

2017-05-15

A bio-electrochemical strategy was developed for constructing a simple and sensitive levofloxacin (LEV) sensor based on a single chamber microbial fuel cell (SC-MFC) using FePO 4 nanoparticles (NPs) as the cathode catalyst instead of traditional Pt/C. In this assembled sensor device, FePO 4 NPs dramatically promoted the electrooxidation of oxygen on the cathode, which helps to accelerate the voltage output from SC-MFC and can provide a powerful guarantee for LEV detection. Scanning electron microscopy (SEM), X-ray diffraction (XRD), Fourier transform infrared (FTIR) and X-ray photoelectron spectroscopy (XPS) were used to fully characterize the FePO 4 NPs. Under the optimized COD condition (3mM), the LEV with a concentration range of 0.1-1000µg/L could be detected successfully, and exhibited the excellent linear interval in the concentration range of 0.1-100µg/L. During this range of concentrations of LEV, a temporary effect on the anode of exoelectrogenic bacterial in less than 10min could occur, and then came back to the normal. It exhibited a long-term stability, maintaining the stable electricity production for 14 months of continuous running. Besides, the detection mechanism was investigated by quantum chemical calculation using density functional theory (DFT). Copyright © 2016. Published by Elsevier B.V.

Probing the Complexities of Structural Changes in Layered Oxide Cathode Materials for Li-Ion Batteries during Fast Charge-Discharge Cycling and Heating.

PubMed

Hu, Enyuan; Wang, Xuelong; Yu, Xiqian; Yang, Xiao-Qing

2018-02-20

The rechargeable lithium-ion battery (LIB) is the most promising energy storage system to power electric vehicles with high energy density and long cycling life. However, in order to meet customers' demands for fast charging, the power performances of current LIBs need to be improved. From the cathode aspect, layer-structured cathode materials are widely used in today's market and will continue to play important roles in the near future. The high rate capability of layered cathode materials during charging and discharging is critical to the power performance of the whole cell and the thermal stability is closely related to the safety issues. Therefore, the in-depth understanding of structural changes of layered cathode materials during high rate charging/discharging and the thermal stability during heating are essential in developing new materials and improving current materials. Since structural changes take place from the atomic level to the whole electrode level, combination of characterization techniques covering multilength scales is quite important. In many cases, this means using comprehensive tools involving diffraction, spectroscopy, and imaging to differentiate the surface from the bulk and to obtain structural/chemical information with different levels of spatial resolution. For example, hard X-ray spectroscopy can yield the bulk information and soft X-ray spectroscopy can give the surface information; X-ray based imaging techniques can obtain spatial resolution of tens of nanometers, and electron-based microcopy can go to angstroms. In addition to challenges associated with different spatial resolution, the dynamic nature of structural changes during high rate cycling and heating requires characterization tools to have the capability of collecting high quality data in a time-resolved fashion. Thanks to the advancement in synchrotron based techniques and high-resolution electron microscopy, high temporal and spatial resolutions can now be achieved. In this Account, we focus on the recent works studying kinetic and thermal properties of layer-structured cathode materials, especially the structural changes during high rate cycling and the thermal stability during heating. Advanced characterization techniques relating to the rate capability and thermal stability will be introduced. The different structure evolution behavior of cathode materials cycled at high rate will be compared with that cycled at low rate. Different response of individual transition metals and the inhomogeneity in chemical distribution will be discussed. For the thermal stability, the relationship between structural changes and oxygen release will be emphatically pointed out. In all these studies being reviewed, advanced characterization techniques are critically applied to reveal complexities at multiscale in layer-structured cathode materials.

O3-type layered transition metal oxide Na(NiCoFeTi) 1/4O 2 as a high rate and long cycle life cathode material for sodium ion batteries

DOE PAGES

Yue, Ji -Li; Yang, Xiao -Qing; Zhou, Yong -Ning; ...

2015-10-09

High rate capability and long cycle life are challenging goals for the development of room temperature sodium-ion batteries. Here we report a new single phase quaternary O3-type layer-structured transition metal oxide Na(NiCoFeTi) 1/4O 2 synthesized by a simple solid-state reaction as a new cathode material for sodium-ion batteries. It can deliver a reversible capacity of 90.6 mA h g –1 at a rate as high as 20C. At 5C, 75.0% of the initial specific capacity can be retained after 400 cycles with a capacity-decay rate of 0.07% per cycle, demonstrating a superior long-term cyclability at high current density. X-ray diffractionmore » and absorption characterization revealed reversible phase transformations and electronic structural changes during the Na + deintercalation/intercalation process. Ni, Co and Fe ions contribute to charge compensation during charge and discharge. Although Ti ions do not contribute to the charge transfer, they play a very important role in stabilizing the structure during charge and discharge by suppressing the Fe migration. Additionally, Ti substitution can also smooth the charge–discharge plateaus effectively, which provides a potential advantage for the commercialization of this material for room temperature sodium-ion batteries.« less

Advanced technology lightweight fuel cell program

NASA Technical Reports Server (NTRS)

Martin, R. E.

1981-01-01

The potential of the alkaline electrolyte fuel cell as the power source in a multi hundred kilowatt orbital energy storage system was studied. The total system weight of an electrolysis cell energy storage system was determined. The tests demonstrated: (1) the performance stability of a platinum on carbon anode catalyst configuration after 5000 hours of testing has no loss in performance; (2) capability of the alkaline fuel cell to operate to a cyclical load profile; (3) suitability of a lightweight graphite electrolyte reservoir plate for use in the alkaline fuel cell; (4) long life potential of a hybrid polysulfone cell edge frame construction; and (5) long term stability of a fiber reinforced potassium titanate matrix structure. The power section tested operates with passive water removal eliminating the requirement for a dynamic hydrogen pump water separator thereby allowing a powerplant design with reduced weight, lower parasite power, and a potential for high reliability and extended endurance. It is concluded that two perovskites are unsuitable for use as a catalyst or as a catalyst support at the cathode of an alkaline fuel cell.

Habit plane-driven P2-type manganese-based layered oxide as long cycling cathode for Na-ion batteries

NASA Astrophysics Data System (ADS)

Luo, Rui; Wu, Feng; Xie, Man; Ying, Yao; Zhou, Jiahui; Huang, Yongxin; Ye, Yusheng; Li, Li; Chen, RenJie

2018-04-01

Layered transition metal oxides are considered to be promising candidates as cathode materials for sodium-ion batteries. Herein, a facile solid-state reaction is developed to synthesize hexagons plate-like Na0.67Ni0.25Mn0.75O2+δ (denoted as P2-NNM) material with habit plane formed. The structure of this layered oxide is characterized by XRD, HR-TEM and SAED. The layered material delivers a high reversible capacity of 91.8 mAh g-1 at 0.2 C with a capacity retention of 94.4 % after 280 cycles, superior rate capability and long cycle life (84.2 % capacity retention after 1000 cycle). Ni2+ is an active ion and Ni doping alleviates the Jahn-Teller distortion, and Mn3+/Mn4+ coexist as Mn4+ is desired from the stability perspective. Particularly, CV and XPS results confirm these results. Moreover, the electrode exhibits a quasi-solid-solution reaction during the sodium extraction and insertion. This contribution demonstrates that P2-NNM is a promising cathode electrode for rechargeable long-life sodium-ion batteries.

Interfacial reaction dependent performance of hollow carbon nanosphere - sulfur composite as a cathode for Li-S battery

DOE PAGES

Zheng, Jianming; Yan, Pengfei; Gu, Meng; ...

2015-05-26

Lithium-sulfur (Li-S) battery is a promising energy storage system due to its high energy density, cost effectiveness and environmental friendliness of sulfur. However, there are still a number of challenges, such as low Coulombic efficiency and poor long-term cycling stability, impeding the commercialization of Li-S battery. The electrochemical performance of Li-S battery is closely related with the interfacial reactions occurring between hosting substrate and active sulfur species which are poorly conducting at fully oxidized and reduced states. Here, we correlate the relationship between the performance and interfacial reactions in the Li-S battery system, using a hollow carbon nanosphere (HCNS) withmore » highly graphitic character as hosting substrate for sulfur. With an appropriate amount of sulfur loading, HCNS/S composite exhibits excellent electrochemical performance because of the fast interfacial reactions between HCNS and the polysulfides. However, further increase of sulfur loading leads to increased formation of highly resistive insoluble reaction products (Li 2S 2/Li 2S) which limits the reversibility of the interfacial reactions and results in poor electrochemical performance. In conclusion, these findings demonstrate the importance of the interfacial reaction reversibility in the whole electrode system on achieving high capacity and long cycle life of sulfur cathode for Li-S batteries.« less

A New CuO-Fe2 O3 -Mesocarbon Microbeads Conversion Anode in a High-Performance Lithium-Ion Battery with a Li1.35 Ni0.48 Fe0.1 Mn1.72 O4 Spinel Cathode.

PubMed

Di Lecce, Daniele; Verrelli, Roberta; Campanella, Daniele; Marangon, Vittorio; Hassoun, Jusef

2017-04-10

A ternary CuO-Fe 2 O 3 -mesocarbon microbeads (MCMB) conversion anode was characterized and combined with a high-voltage Li 1.35 Ni 0.48 Fe 0.1 Mn 1.72 O 4 spinel cathode in a lithium-ion battery of relevant performance in terms of cycling stability and rate capability. The CuO-Fe 2 O 3 -MCMB composite was prepared by using high-energy milling, a low-cost pathway that leads to a crystalline structure and homogeneous submicrometrical morphology as revealed by XRD and electron microscopy. The anode reversibly exchanges lithium ions through the conversion reactions of CuO and Fe 2 O 3 and by insertion into the MCMB carbon. Electrochemical tests, including impedance spectroscopy, revealed a conductive electrode/electrolyte interface that enabled the anode to achieve a reversible capacity value higher than 500 mAh g -1 when cycled at a current of 120 mA g -1 . The remarkable stability of the CuO-Fe 2 O 3 -MCMB electrode and the suitable characteristics in terms of delivered capacity and voltage-profile retention allowed its use in an efficient full lithium-ion cell with a high-voltage Li 1.35 Ni 0.48 Fe 0.1 Mn 1.72 O 4 cathode. The cell had a working voltage of 3.6 V and delivered a capacity of 110 mAh g cathode -1 with a Coulombic efficiency above 99 % after 100 cycles at 148 mA g cathode -1 . This relevant performances, rarely achieved by lithium-ion systems that use the conversion reaction, are the result of an excellent cell balance in terms of negative-to-positive ratio, favored by the anode composition and electrochemical features. © 2017 Wiley-VCH Verlag GmbH & Co. KGaA, Weinheim.

Nature of the Electrochemical Properties of Sulphur Substituted LiMn2O4 Spinel Cathode Material Studied by Electrochemical Impedance Spectroscopy

PubMed Central

Bakierska, Monika; Świętosławski, Michał; Dziembaj, Roman; Molenda, Marcin

2016-01-01

In this work, nanostructured LiMn2O4 (LMO) and LiMn2O3.99S0.01 (LMOS1) spinel cathode materials were comprehensively investigated in terms of electrochemical properties. For this purpose, electrochemical impedance spectroscopy (EIS) measurements as a function of state of charge (SOC) were conducted on a representative charge and discharge cycle. The changes in the electrochemical performance of the stoichiometric and sulphur-substituted lithium manganese oxide spinels were examined, and suggested explanations for the observed dependencies were given. A strong influence of sulphur introduction into the spinel structure on the chemical stability and electrochemical characteristic was observed. It was demonstrated that the significant improvement in coulombic efficiency and capacity retention of lithium cell with LMOS1 active material arises from a more stable solid electrolyte interphase (SEI) layer. Based on EIS studies, the Li ion diffusion coefficients in the cathodes were estimated, and the influence of sulphur on Li+ diffusivity in the spinel structure was established. The obtained results support the assumption that sulphur substitution is an effective way to promote chemical stability and the electrochemical performance of LiMn2O4 cathode material. PMID:28773819

Scalable and template-free synthesis of nanostructured Na{sub 1.08}V{sub 6}O{sub 15} as high-performance cathode material for lithium-ion batteries

DOE Office of Scientific and Technical Information (OSTI.GOV)

Zheng, Shili, E-mail: slzheng@ipe.ac.cn; Wang, Xinran; Yan, Hong

2016-09-15

Highlights: • Nanostructured Na{sub 1.08}V{sub 6}O{sub 15} was synthesized through additive-free sol-gel process. • Prepared Na{sub 1.08}V{sub 6}O{sub 15} demonstrated high capacity and sufficient cycling stability. • The reaction temperature was optimized to allow scalable Na{sub 1.08}V{sub 6}O{sub 15} fabrication. - Abstract: Developing high-capacity cathode material with feasibility and scalability is still challenging for lithium-ion batteries (LIBs). In this study, a high-capacity ternary sodium vanadate compound, nanostructured NaV{sub 6}O{sub 15}, was template-free synthesized through sol-gel process with high producing efficiency. The as-prepared sample was systematically post-treated at different temperature and the post-annealing temperature was found to determine the cycling stabilitymore » and capacity of NaV{sub 6}O{sub 15}. The well-crystallized one exhibited good electrochemical performance with a high specific capacity of 302 mAh g{sup −1} when cycled at current density of 0.03 mA g{sup −1}. Its relatively long-term cycling stability was characterized by the cell performance under the current density of 1 A g{sup −1}, delivering a reversible capacity of 118 mAh g{sup −1} after 300 cycles with 79% capacity retention and nearly 100% coulombic efficiency: all demonstrating its significant promise of proposed strategy for large-scale synthesis of NaV{sub 6}O{sub 15} as cathode with high-capacity and high energy density for LIBs.« less

Sustainable water desalination and electricity generation in a separator coupled stacked microbial desalination cell with buffer free electrolyte circulation.

PubMed

Chen, Xi; Liang, Peng; Wei, Zhimou; Zhang, Xiaoyuan; Huang, Xia

2012-09-01

A separator coupled circulation stacked microbial desalination cell (c-SMDC-S) was constructed to stabilize the pH imbalances in MDCs without buffer solution and achieved the stable desalination. The long-term operation of c-SMDC-S, regular stacked MDC (SMDC) and no separator coupled circulation SMDC (c-SMDC) were tested. The SMDC and c-SMDC could only stably operate for 1 week and 1 month owing to dramatic anolyte pH decrease and serious biofilm growth on the air cathode, respectively. The c-SMDC-S gained in anolyte alkalinity and operated stably for about 60 days without the thick biofilm growth on cathode. Besides, the chemical oxygen demand removal and coulombic efficiency were 64 ± 6% and 30 ± 2%, higher than that of SMDC and c-SMDC, respectively. It was concluded that the circulation of alkalinity could remove pH imbalance while the separator could expand the operation period and promote the conversion of organic matter to electricity. Copyright © 2012 Elsevier Ltd. All rights reserved.

High-Rate and Long-Term Cycle Stability of Li-S Batteries Enabled by Li2S/TiO2-Impregnated Hollow Carbon Nanofiber Cathodes.

PubMed

Wang, Xinran; Bi, Xuanxuan; Wang, Shaona; Zhang, Yi; Du, Hao; Lu, Jun

2018-05-16

The high theoretical energy density of lithium-sulfur (Li-S) batteries makes them an alternative battery technology to lithium ion batteries. However, Li-S batteries suffer from low sulfur loading, poor charge transport, and dissolution of lithium polysulfide. In our study, we use the lithiated S, Li 2 S, as the cathode material, coupled with electrospun TiO 2 -impregnated hollow carbon nanofibers (TiO 2 -HCFs), which serve as the conductive agent and protective barrier for Li 2 S in Li-S batteries. TiO 2 -HCFs provide much improved electron/ionic conductivity and serve as a physical barrier, which prevents the dissolution of lithium polysulfides. The Li 2 S/TiO 2 -HCF composite delivers a discharge capacity of 851 mA h g Li 2 S -1 at 0.1C and the bilayer TiO 2 -HCFs/Li 2 S/TiO 2 -HCF composite delivers a high specific capacity of 400 mA h g Li 2 S -1 at 5C.

Controllable Preparation of V2O5/Graphene Nanocomposites as Cathode Materials for Lithium-Ion Batteries

NASA Astrophysics Data System (ADS)

Liu, Yanglin; Wang, Yaping; Zhang, Yifang; Liang, Shuquan; Pan, Anqiang

2016-12-01

Transition metal oxides and graphene composites have been widely reported in energy storage and conversion systems. However, the controllable synthesis of graphene-based nanocomposites with tunable morphologies is far less reported. In this work, we report the fabrication of V2O5 and reduced graphene oxide composites with nanosheet or nanoparticle-assembled subunits by adjusting the solvothermal solution. As cathode materials for lithium-ion batteries, the nanosheet-assembled V2O5/graphene composite exhibits better rate capability and long-term cycling stability. The V2O5/graphene composites can deliver discharge capacities of 133, 131, and 122 mAh g-1 at 16 C, 32 C, and 64 C, respectively, in the voltage range of 2.5-4.0 V vs. Li/Li+. Moreover, the electrodes can retain 85% of their original capacity at 1C rate after 500 cycles. The superior electrochemical performances are attributed to the porous structures created by the connected V2O5 nanosheets and the electron conductivity improvement by graphene.

Reconstruction of multidimensional carbon hosts with combined 0D, 1D and 2D networks for enhanced lithium-sulfur batteries

NASA Astrophysics Data System (ADS)

Li, S. H.; Xia, X. H.; Wang, Y. D.; Wang, X. L.; Tu, J. P.

2017-02-01

It is a core task to find solutions to suppress the "shuttle effect" of polysulfides and improve high rate capability at the sulfur cathode of lithium sulfur batteries. Herein we first time propose a concept of multileveled blocking "dams" to suppress the diffusion of polysulfides. We report a facile and effective strategy to construct multidimensional conductive carbon hosts for accommodation of active sulfur. Multidimensional ternary carbon networks (MTCNs) with 0D nanospheres, 1D nanotubes and 2D nanoflakes are organically combined together to provide multileveled conductive channels to reserve active sulfur and promote stable sustained reactions. In the light of enhanced conductivity and multileveled blocking "dams" for polysulfides, the designed MTCNs/S cathode has been demonstrated with noticeable improvement in discharge capacity (1472 mAh g-1 at 0.l C) and long-term cycling stability (65% retention at 5.0 C after 500 cycles). Our research may provide a new insight in the gradient blocking of polysulfides with the help of multidimensional carbon networks.

3D-hybrid material design with electron/lithium-ion dual-conductivity for high-performance Li-sulfur batteries

NASA Astrophysics Data System (ADS)

Zhao, Yan; Tan, Rui; Yang, Jie; Wang, Kai; Gao, Rongtan; Liu, Dong; Liu, Yidong; Yang, Jinlong; Pan, Feng

2017-02-01

We report a novel 3D-hybrid cathode material with three-dimensional (3D) N-GO/CNT framework to load sulfur (77.6 wt %), and sulfonated polyaniline (SPANI) of coating layer. Used as a cathode material, it possesses a high capacity (1196 mAh g-1@0.3 A g-1@1.6 mg cm-2), excellent charging-discharging rate (680 mAh g-1@7.5 A g-1) and long-life performance (maintaining 71.1% capacity over 450 cycles), which is mainly attributed to the benefits of excellent electronic/Li-ionic dual-conductivity and confinement effect of the 3D-hybrid N-GO/CNT framework coated by self-doping conducting polymer SPANI. Thus, a 3D sulfur cathode modified with electronic/Li-ionic dual-conduction network can significantly enhance the electrochemical performance and stability, and this novel type of material is very promising for commercial applications that require high energy and power density, long life, and excellent abuse tolerance.

One-Pot Synthesis of Lithium-Rich Cathode Material with Hierarchical Morphology.

PubMed

Luo, Kun; Roberts, Matthew R; Hao, Rong; Guerrini, Niccoló; Liberti, Emanuela; Allen, Christopher S; Kirkland, Angus I; Bruce, Peter G

2016-12-14

Lithium-rich transition metal oxides, Li 1+x TM 1-x O 2 (TM, transition metal), have attracted much attention as potential candidate cathode materials for next generation lithium ion batteries because their high theoretical capacity. Here we present the synthesis of Li[Li 0.2 Ni 0.2 Mn 0.6 ]O 2 using a facile one-pot resorcinol-formaldehyde method. Structural characterization indicates that the material adopts a hierarchical porous morphology consisting of uniformly distributed small pores and disordered large pore structures. The material exhibits excellent electrochemical cycling stability and a good retention of capacity at high rates. The material has been shown to be both advantageous in terms of gravimetric and volumetric capacities over state of the art commercial cathode materials.

Hybrid lithium-ion capacitor with LiFePO4/AC composite cathode - Long term cycle life study, rate effect and charge sharing analysis

NASA Astrophysics Data System (ADS)

Shellikeri, A.; Yturriaga, S.; Zheng, J. S.; Cao, W.; Hagen, M.; Read, J. A.; Jow, T. R.; Zheng, J. P.

2018-07-01

Energy storage devices, which can combine the advantages of lithium-ion battery with that of electric double layer capacitor, are of prime interest. Recently, composite cathodes, which combine a battery material with capacitor material, have shown promise in enhancing life cycle and energy/power performances. Lithium-ion capacitor (LIC), with unique charge storage mechanism of combining a pre-lithiated battery anode with a capacitor cathode, is one such device which has the potential to synergistically incorporate the composite cathode to enhance capacity and cycle life. We report here a hybrid LIC consisting of a lithium iron phosphate (LiFePO4-LFP)/Activated Carbon composite cathode in combination with a hard carbon anode, by integrating the cycle life and capacity enhancing strategies of a dry method of electrode fabrication, anode pre-lithiation and a 3:1 anode to cathode capacity ratio, demonstrating a long cycle life, while elaborating on the charge sharing between the faradaic and non-faradaic mechanism in the battery and capacitor materials, respectively in the composite cathode. An excellent cell capacity retention of 94% (1000 cycles at 1C) and 92% (100,000 cycles at 60C) were demonstrated, while retaining 78% (over 6000 cycles at 2.7C) and 67% (over 70,000 cycles at 43C) of the LFP capacity in the composite cathode.

Bioelectrochemical desalination and electricity generation in microbial desalination cell with dewatered sludge as fuel.

PubMed

Meng, Fanyu; Jiang, Junqiu; Zhao, Qingliang; Wang, Kun; Zhang, Guodong; Fan, Qingxin; Wei, Liangliang; Ding, Jing; Zheng, Zhen

2014-04-01

Microbial desalination cells (MDCs) with common liquid anodic substrate exhibit a slow startup and destructive pH drop, and abiotic cathodes have high cost and low sustainability. A biocathode MDC with dewatered sludge as fuel was developed for synergistic desalination, electricity generation and sludge stabilization. Experimental results indicated that the startup period was reduced to 3d, anodic pH was maintained between 6.6 and 7.6, and high stability was shown under long-term operation (300d). When initial NaCl concentrations were 5 and 10g/L, the desalinization rates during stable operation were 46.37±1.14% and 40.74±0.89%, respectively. The maximum power output of 3.178W/m(3) with open circuit voltage (OCV) of 1.118V was produced on 130d. After 300d, 25.71±0.15% of organic matter was removed. These results demonstrated that dewatered sludge was an appropriate anodic substrate to enhance MDC stability for desalination and electricity generation. Copyright © 2014 Elsevier Ltd. All rights reserved.

Application of M-type cathodes to high-power cw klystrons

NASA Astrophysics Data System (ADS)

Isagawa, S.; Higuchi, T.; Kobayashi, K.; Miyake, S.; Ohya, K.; Yoshida, M.

1999-05-01

Two types of high-power cw klystrons have been widely used at KEK in both TRISTAN and KEKB e +e - collider projects: one is a 0.8 MW/1.0 MW tube, called YK1302/YK1303 (Philips); the other is a 1.2 MW tube, called E3786/E3732 (Toshiba). Normally, the dispenser cathodes of the `B-type' and the `S-type' have been used, respectively, but for improved versions they have been replaced by low-temperature cathodes, called the `M-type'. An Os/Ru coating was applied to the former, whereas an Ir one was applied to the latter. Until now, all upgraded tubes installing M-type cathodes, 9 and 8 in number, respectively, have worked successfully without any dropout. A positive experience concerning the lifetime under real operation conditions has been obtained. M-type cathodes are, however, more easily poisoned. One tube installing an Os/Ru-coated cathode showed a gradual, and then sudden decrease in emission during an underheating test, although the emission could fortunately be recovered by aging at the KEK test field. Once sufficiently aged, the emission of an Ir-coated cathode proved to be very high and stable, and its lifetime is expected to be very long. One disadvantage of this cathode is, however, susceptibility to gas poisoning and the necessity of long-term initial aging. New techniques, like ion milling and fine-grained tungsten top layers, were not as successful as expected from their smaller scale applications to shorten the initial aging period. A burn-in process at higher cathode loading was efficient to make the poisoned cathode active and to decrease unwanted Wehnelt emission. On top of that, the emission cooling, and thus thermal conductivity near the emitting layer could play an important role in such large-current cathodes as ours.

Lithium-Polymer battery based on polybithiophene as cathode material

NASA Astrophysics Data System (ADS)

Chen, J.; Wang, J.; Wang, C.; Too, C. O.; Wallace, G. G.

Stainless-steel mesh electrodes coated with polybithiophene, obtained by electrochemical polymerization (constant potential and constant current), have been investigated as cathode materials in a lithium-polybithiophene rechargeable battery by cyclic voltammetry, electrochemical impedance spectroscopy and long-term charge-discharge cycling process. The effects of different growth methods on the surface morphology of the films and the charge-discharge capacity are discussed in detail. The results show that polybithiophene-hexafluorophosphate is a very promising cathode material for manufacturing lithium-polymer rechargeable batteries with a highly stable discharge capacity of 81.67 mAh g -1 after 50 cycles.

Recent Progress in Iron-Based Electrode Materials for Grid-Scale Sodium-Ion Batteries.

PubMed

Fang, Yongjin; Chen, Zhongxue; Xiao, Lifen; Ai, Xinping; Cao, Yuliang; Yang, Hanxi

2018-03-01

Grid-scale energy storage batteries with electrode materials made from low-cost, earth-abundant elements are needed to meet the requirements of sustainable energy systems. Sodium-ion batteries (SIBs) with iron-based electrodes offer an attractive combination of low cost, plentiful structural diversity and high stability, making them ideal candidates for grid-scale energy storage systems. Although various iron-based cathode and anode materials have been synthesized and evaluated for sodium storage, further improvements are still required in terms of energy/power density and long cyclic stability for commercialization. In this Review, progress in iron-based electrode materials for SIBs, including oxides, polyanions, ferrocyanides, and sulfides, is briefly summarized. In addition, the reaction mechanisms, electrochemical performance enhancements, structure-composition-performance relationships, merits and drawbacks of iron-based electrode materials for SIBs are discussed. Such iron-based electrode materials will be competitive and attractive electrodes for next-generation energy storage devices. © 2018 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

An air-breathing enzymatic cathode with extended lifetime by continuous laccase supply.

PubMed

Kipf, Elena; Sané, Sabine; Morse, Daniel; Messinger, Thorsten; Zengerle, Roland; Kerzenmacher, Sven

2018-04-22

We present a novel concept of an air-breathing enzymatic biofuel cell cathode combined with continuous supply of unpurified laccase-containing supernatant of the white-rot fungus Trametes versicolor for extended lifetime. The air-breathing cathode design obviates the need for energy-intensive active aeration. In a corresponding long-term experiment at a constant current density of 50 µA cm -2 , we demonstrated an increased lifetime of 33 days (cathode potential above 0.430 V vs. SCE), independent of enzyme degradation. The obtained data suggest that theoretically a longer lifetime is feasible. However, further engineering efforts are required to prevent clogging and fouling of the supply tubes. These results represent an important step towards the realization of enzymatic biofuel cell cathodes with extended lifetime and enhanced performance. Copyright © 2018 Elsevier Ltd. All rights reserved.

Enhancement of Combustion and Flame Stabilization Using Transient Non-Equilibrium Plasma

DTIC Science & Technology

2007-03-31

cathode spot D = diameter of MGA device D= diffusivity of i’h species d = diameter of arc dcoected= diametrically corrected diameter of arc d.rwwd... cathode and anode, stabilization (4) respectively (Fig. 1). A wire was attached to the cathode , which was separated from the outer anode by 2 mm at the...smallest gap (point (1) in Fig. 1). The wire spiraled progressively closer to the cathode , where it was attached at the largest gap between the two

Carbon-nanotube-doped Pd-Ni bimetallic three-dimensional electrode for electrocatalytic hydrodechlorination of 4-chlorophenol: Enhanced activity and stability.

PubMed

Wu, Yifan; Gan, Ling; Zhang, Shupeng; Song, Haiou; Lu, Chang; Li, Wentao; Wang, Zheng; Jiang, Bicun; Li, Aimin

2018-08-15

A novel composite bimetallic electrode, palladium-nickel/multi-walled carbon nanotubes/graphite felt (Pd-Ni/MWCNTs/GF), was synthesized for the electrocatalytic hydrodechlorination of 4-chlorophenol (4-CP). GF with a three-dimensional structure was used as the electrode substrate, and doped with MWCNTs, which can improve the GF conductivity and serve as a skeleton for metal loading. Ni and Pd were deposited on the electrode surface stepwise to obtain a well-aligned, highly active and stable Pd-Ni/MWCNTs/GF electrode. The Pd-Ni/MWCNTs/GF cathode showed a high reactivity for the electrocatalytic hydrodechlorination of 4-CP; up to 100% removal of 4-CP was achieved within 30 min, and followed pseudo-first-order kinetics with a rate constant of 0.162 min -1 . Compared with other cathodes, the Pd-Ni/MWCNTs/GF electrode showed superior performance in 4-CP reduction. Excessive current will lower the reaction efficiency and current efficiency because of hydrogen evolution, and acidic solution conditions are more conducive to electrocatalytic reactions. Experiments confirmed that the Ni had a small amount of loss under acidic conditions but remained stable under neutral and alkaline conditions, whereas the loss of Pd for different pH values was constantly low. In cycle tests, the bimetallic electrode exhibits a better reactivity and stability than the single-metal Pd electrode in the long-term. Copyright © 2018 Elsevier B.V. All rights reserved.

Electrolyte additive enabled fast charging and stable cycling lithium metal batteries

DOE Office of Scientific and Technical Information (OSTI.GOV)

Zheng, Jianming; Engelhard, Mark H.; Mei, Donghai

2017-03-01

Lithium (Li) metal battery is an attractive energy storage system owing to the ultrahigh specific capacity and the lowest redox potential of Li metal anode. However, safety concern associated with dendrite growth and limited cycle life especially at a high charge current density are two critical challenges hindering the practical applications of rechargeable Li metal batteries. Here, we report for the first time that an optimal amount (0.05 M) of LiPF6 as additive in the LiTFSI-LiBOB dual-salt/carbonate-based electrolyte can significantly enhance the charging capability and the long-term cycle life of Li metal batteries with a moderately high cathode loading ofmore » 1.75 mAh cm-2. Unprecedented stable-cycling (97.1% capacity retention after 500 cycles) along with very limited increase in electrode over-potential has been achieved at a high current density of 1.75 mA cm-2. This unparalleled fast charging and stable cycling performance is contributed from both the stabilized Al cathode current collector, and, more importantly, the robust and conductive SEI layer formed on Li metal anode in the presence of the LiPF6 additive.« less

Unveiling the Structural Evolution of Ag 1.2Mn 8O 16 under Coulombically Controlled (De)Lithiation

DOE Office of Scientific and Technical Information (OSTI.GOV)

Huang, Jianping; Hu, Xiaobing; Brady, Alexander B.

MnO 2 materials are considered promising cathode materials for rechargeable lithium, sodium, and magnesium batteries due to their earth abundance and environmental friendliness. One polymorph of MnO 2, α-MnO 2, has 2 × 2 tunnels (4.6 Å × 4.6 Å) in its structural framework, which provide facile diffusion pathways for guest ions. In this work, a silver-ion-containing α-MnO 2 (Ag 1.2Mn 8O 16) is examined as a candidate cathode material for Li based batteries. Electrochemical stability of Ag 1.2Mn 8O 16 is investigated through Coulombically controlled reduction under 2 or 4 molar electron equivalents (e.e.). Terminal discharge voltage remains almostmore » constant under 2 e.e. of cycling, whereas it continuously decreases under repetitive reduction by 4 e.e. Thus, detailed structural analyses were utilized to investigate the structural evolution upon lithiation. Significant increases in lattice a (17.7%) and atomic distances (~4.8%) are observed when x in Li xAg 1.2Mn 8O 16 is >4. Ag metal forms at this level of lithiation concomitant with a large structural distortion to the Mn–O framework. In contrast, lattice a only expands by 2.2% and Mn–O/Mn-Mn distances show minor changes (~1.4%) at x < 2. The structural deformation (tunnel breakage) at x > 4 inhibits the recovery of the original structure, leading to poor cycle stability at high lithiation levels. This report establishes the correlation among local structure changes, amorphization processes, formation of Ag 0, and long-term cycle stability for this silver-containing α-MnO 2 type material at both low and high lithiation levels.« less

Unveiling the Structural Evolution of Ag 1.2Mn 8O 16 under Coulombically Controlled (De)Lithiation

DOE Office of Scientific and Technical Information (OSTI.GOV)

Huang, Jianping; Hu, Xiaobing; Brady, Alexander B.

MnO 2 materials are considered promising cathode materials for rechargeable lithium, sodium, and magnesi-um batteries due to their earth abundance and environmental friendliness. One polymorph of MnO 2, α-MnO 2, has 2×2 tunnels (4.6 Å × 4.6 Å) in its structural framework, which provide facile diffusion pathways for guest ions. In this work, a silver ion containing α-MnO 2 (Ag 1.2Mn 8O 16) is examined as a candidate cathode material for Li based batteries. Electro-chemical stability of Ag 1.2Mn 8O 16 is investigated through Coulombically controlled reduction under 2 or 4 molar electron equivalents (e.e.). Terminal discharge voltage remains almostmore » constant under 2 e.e. of cycling, whereas it continuously decreases under repetitive reduction by 4 e.e. Thus, detailed structural analyses were utilized to investigate the structural evolution upon lithiation. Significant increases in lattice a (17.7 %) and atomic distances (~4.8 %) are observed when x in Li xAg 1.2Mn 8O 16 is >4. Ag metal forms at this level of lithiation concomitant with a large structural distortion to the Mn-O framework. In contrast, lattice a only expands by 2.2 % and Mn-O/Mn-Mn distances show minor changes (~1.4 %) at x <2. The structural deformation (tunnel breakage) at x >4 inhibits the recovery of the original structure, leading to poor cycle stability at high lithiation levels. This report establishes the correlation among local structure changes, amorphization processes, formation of Ag 0 and long term cycle stability for this silver containing α-MnO 2 type material at both low and high lithiation levels.« less

Unveiling the Structural Evolution of Ag 1.2Mn 8O 16 under Coulombically Controlled (De)Lithiation

DOE PAGES

Huang, Jianping; Hu, Xiaobing; Brady, Alexander B.; ...

2017-12-17

MnO 2 materials are considered promising cathode materials for rechargeable lithium, sodium, and magnesi-um batteries due to their earth abundance and environmental friendliness. One polymorph of MnO 2, α-MnO 2, has 2×2 tunnels (4.6 Å × 4.6 Å) in its structural framework, which provide facile diffusion pathways for guest ions. In this work, a silver ion containing α-MnO 2 (Ag 1.2Mn 8O 16) is examined as a candidate cathode material for Li based batteries. Electro-chemical stability of Ag 1.2Mn 8O 16 is investigated through Coulombically controlled reduction under 2 or 4 molar electron equivalents (e.e.). Terminal discharge voltage remains almostmore » constant under 2 e.e. of cycling, whereas it continuously decreases under repetitive reduction by 4 e.e. Thus, detailed structural analyses were utilized to investigate the structural evolution upon lithiation. Significant increases in lattice a (17.7 %) and atomic distances (~4.8 %) are observed when x in Li xAg 1.2Mn 8O 16 is >4. Ag metal forms at this level of lithiation concomitant with a large structural distortion to the Mn-O framework. In contrast, lattice a only expands by 2.2 % and Mn-O/Mn-Mn distances show minor changes (~1.4 %) at x <2. The structural deformation (tunnel breakage) at x >4 inhibits the recovery of the original structure, leading to poor cycle stability at high lithiation levels. This report establishes the correlation among local structure changes, amorphization processes, formation of Ag 0 and long term cycle stability for this silver containing α-MnO 2 type material at both low and high lithiation levels.« less

Tape Casting of High-Performance Low-Temperature Solid Oxide Cells with Thin La0.8Sr0.2Ga0.8Mg0.2O3-δ Electrolytes and Impregnated Nano Anodes.

PubMed

Gao, Zhan; Wang, Hongqian; Miller, Elizabeth; Liu, Qinyuan; Senn, Daniel; Barnett, Scott

2017-03-01

Low-temperature solid oxide cells (LT-SOCs), operating at 400 to 650 °C, have great potential for commercialization since they can provide lower cost and improved long-term durability. Low operating temperature can also enable high round-trip efficiency of SOCs as reversible energy storage devices. This paper describes Sr 0.8 La 0.2 TiO 3-α (SLT) anode supported LT-SOC with thin La 0.8 Sr 0.2 Ga 0.8 Mg 0.2 O 3-δ (LSGM) electrolyte made by tape casting, with screen printed La 0.6 Sr 0.4 Fe 0.8 Co 0.2 O 3-δ (LSCF) cathode and impregnated Ni anode. Optimization of the anode functional layers is described; the best anodes had 68 vol % LSGM and 12.3 vol % Ni and yielded maximum power density of 1.6 Wcm -2 with a cell area specific resistance (ASR) of 0.21 Ωcm 2 at 650 °C. Most of the cell ASR was associated with the cathode. Reversible electrolysis and fuel cell operation yielded similar characteristics with both 50% H 2 -50% H 2 O and syngas fuel. Life testing over 500 h showed that the cathode impedance stabilized after an initial break-in period; the ohmic and anode resistances, though relatively small, increased slightly with time.

A Carbon-Cotton Cathode with Ultrahigh-Loading Capability for Statically and Dynamically Stable Lithium–Sulfur Batteries

DOE PAGES

Chung, Sheng-Heng; Chang, Chi-Hao; Manthiram, Arumugam

2016-10-26

Sulfur exhibits a high theoretical capacity of 1675 mA h g -1 via a distinct conversion reaction, which is different from the insertion reactions in commercial lithium-ion batteries. In consideration of its conversion reaction battery chemistry, a custom design for electrode materials could establish the way for attaining high-loading capability while simultaneously maintaining high electrochemical utilization and stability. In this study, this process is undertaken by introducing carbon cotton as an attractive electrode-containment material for enhancing the dynamic and static stabilities of lithium-sulfur (Li-S) batteries. The carbon cotton possessing a hierarchical macro-/microporous architecture exhibits a high surface area of 805more » m 2 g -1 and high microporosity with a micropore area of 557 m 2 g -1. The macroporous channels allow the carbon cotton to load and stabilize a high amount of active material. The abundant microporous reaction sites spread throughout the carbon cotton facilitate the redox chemistry of the high-loading/content Li-S system. As a result, the high-loading carbon-cotton cathode exhibits (i) enhanced cycle stability with a good dynamic capacity retention of 70% after 100 cycles and (ii) improved cellstorage stability with a high static capacity retention of above 93% and a low time-dependent self-discharge rate of 0.12% per day after storing for a long period of 60 days. In conclusion, these carbon-cotton cathodes with the remarkably highest values reported so far of both sulfur loading (61.4 mg cm -2) and sulfur content (80 wt %) demonstrate enhanced electrochemical utilization with the highest areal, volumetric, and gravimetric capacities simultaneously.« less

A Carbon-Cotton Cathode with Ultrahigh-Loading Capability for Statically and Dynamically Stable Lithium–Sulfur Batteries

DOE Office of Scientific and Technical Information (OSTI.GOV)

Chung, Sheng-Heng; Chang, Chi-Hao; Manthiram, Arumugam

Sulfur exhibits a high theoretical capacity of 1675 mA h g -1 via a distinct conversion reaction, which is different from the insertion reactions in commercial lithium-ion batteries. In consideration of its conversion reaction battery chemistry, a custom design for electrode materials could establish the way for attaining high-loading capability while simultaneously maintaining high electrochemical utilization and stability. In this study, this process is undertaken by introducing carbon cotton as an attractive electrode-containment material for enhancing the dynamic and static stabilities of lithium-sulfur (Li-S) batteries. The carbon cotton possessing a hierarchical macro-/microporous architecture exhibits a high surface area of 805more » m 2 g -1 and high microporosity with a micropore area of 557 m 2 g -1. The macroporous channels allow the carbon cotton to load and stabilize a high amount of active material. The abundant microporous reaction sites spread throughout the carbon cotton facilitate the redox chemistry of the high-loading/content Li-S system. As a result, the high-loading carbon-cotton cathode exhibits (i) enhanced cycle stability with a good dynamic capacity retention of 70% after 100 cycles and (ii) improved cellstorage stability with a high static capacity retention of above 93% and a low time-dependent self-discharge rate of 0.12% per day after storing for a long period of 60 days. In conclusion, these carbon-cotton cathodes with the remarkably highest values reported so far of both sulfur loading (61.4 mg cm -2) and sulfur content (80 wt %) demonstrate enhanced electrochemical utilization with the highest areal, volumetric, and gravimetric capacities simultaneously.« less

Carbon Disulfide Cosolvent Electrolytes for High-Performance Lithium Sulfur Batteries.

PubMed

Gu, Sui; Wen, Zhaoyin; Qian, Rong; Jin, Jun; Wang, Qingsong; Wu, Meifen; Zhuo, Shangjun

2016-12-21

Development of lithium sulfur (Li-S) batteries with high Coulombic efficiency and long cycle stability remains challenging due to the dissolution and shuttle of polysulfides in electrolyte. Here, a novel additive, carbon disulfide (CS 2 ), to the organic electrolyte is reported to improve the cycling performance of Li-S batteries. The cells with the CS 2 -additive electrolyte exhibit high Coulombic efficiency and long cycle stability, showing average Coulombic efficiency >99% and a capacity retention of 88% over the entire 300 cycles. The function of the CS 2 additive is 2-fold: (1) it inhibits the migration of long-chain polysulfides to the anode by forming complexes with polysulfides and (2) it passivates electrode surfaces by inducing the protective coatings on both the anode and the cathode.

Fabricating Ir/C Nanofiber Networks as Free-Standing Air Cathodes for Rechargeable Li-CO2 Batteries.

PubMed

Wang, Chengyi; Zhang, Qinming; Zhang, Xin; Wang, Xin-Gai; Xie, Zhaojun; Zhou, Zhen

2018-06-07

Li-CO 2 batteries are promising energy storage systems by utilizing CO 2 at the same time, though there are still some critical barriers before its practical applications such as high charging overpotential and poor cycling stability. In this work, iridium/carbon nanofibers (Ir/CNFs) are prepared via electrospinning and subsequent heat treatment, and are used as cathode catalysts for rechargeable Li-CO 2 batteries. Benefitting from the unique porous network structure and the high activity of ultrasmall Ir nanoparticles, Ir/CNFs exhibit excellent CO 2 reduction and evolution activities. The Li-CO 2 batteries present extremely large discharge capacity, high coulombic efficiency, and long cycling life. Moreover, free-standing Ir/CNF films are used directly as air cathodes to assemble Li-CO 2 batteries, which show high energy density and ultralong operation time, demonstrating great potential for practical applications. © 2018 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

A passive microfluidic hydrogen-air fuel cell with exceptional stability and high performance.

PubMed

Mitrovski, Svetlana M; Nuzzo, Ralph G

2006-03-01

We describe an advanced microfluidic hydrogen-air fuel cell (FC) that exhibits exceptional durability and high performance, most notably yielding stable output power (>100 days) without the use of an anode-cathode separator membrane. This FC embraces an entirely passive device architecture and, unlike conventional microfluidic designs that exploit laminar hydrodynamics, no external pumps are used to sustain or localize the reagent flow fields. The devices incorporate high surface area/porous metal and metal alloy electrodes that are embedded and fully immersed in liquid electrolyte confined in the channels of a poly(dimethylsiloxane) (PDMS)-based microfluidic network. The polymeric network also serves as a self-supporting membrane through which oxygen and hydrogen are supplied to the cathode and alloy anode, respectively, by permeation. The operational stability of the device and its performance is strongly dependent on the nature of the electrolyte used (5 M H2SO4 or 2.5 M NaOH) and composition of the anode material. The latter choice is optimized to decrease the sensitivity of the system to oxygen cross-over while still maintaining high activity towards the hydrogen oxidation reaction (HOR). Three types of high surface area anodes were tested in this work. These include: high-surface area electrodeposited Pt (Pt); high-surface area electrodeposited Pd (Pd); and thin palladium adlayers supported on a "porous" Pt electrode (Pd/Pt). The FCs display their best performance in 5 M H2SO4 using the Pd/Pt anode. This exceptional stability and performance was ascribed to several factors, namely: the high permeabilities of O2, H2, and CO2 in PDMS; the inhibition of the formation of insoluble carbonate species due to the presence of a highly acidic electrolyte; and the selectivity of the Pd/Pt anode toward the HOR. The stability of the device for long-term operation was modeled using a stack of three FCs as a power supply for a portable display that otherwise uses a 3 V battery.

Evaluation of a LED-based flatbed document scanner for radiochromic film dosimetry in transmission mode.

PubMed

Lárraga-Gutiérrez, José Manuel; García-Garduño, Olivia Amanda; Treviño-Palacios, Carlos; Herrera-González, José Alfredo

2018-03-01

Flatbed scanners are the most frequently used reading instrument for radiochromic film dosimetry because its low cost, high spatial resolution, among other advantages. These scanners use a fluorescent lamp and a CCD array as light source and detector, respectively. Recently, manufacturers of flatbed scanners replaced the fluorescent lamp by light emission diodes (LED) as a light source. The goal of this work is to evaluate the performance of a commercial flatbed scanner with LED based source light for radiochromic film dosimetry. Film read out consistency, response uniformity, film-scanner sensitivity, long term stability and total dose uncertainty was evaluated. In overall, the performance of the LED flatbed scanner is comparable to that of a cold cathode fluorescent lamp (CCFL). There are important spectral differences between LED and CCFL lamps that results in a higher sensitivity of the LED scanner in the green channel. Total dose uncertainty, film response reproducibility and long-term stability of LED scanner are slightly better than those of the CCFL. However, the LED based scanner has a strong non-uniform response, up to 9%, that must be adequately corrected for radiotherapy dosimetry QA. The differences in light emission spectra between LED and CCFL lamps and its potential impact on film-scanner sensitivity suggest that the design of a dedicated flat-bed scanner with LEDs may improve sensitivity and dose uncertainty in radiochromic film dosimetry. Copyright © 2018 Associazione Italiana di Fisica Medica. Published by Elsevier Ltd. All rights reserved.

Self-stabilized discharge filament in plane-parallel barrier discharge configuration: formation, breakdown mechanism, and memory effects

NASA Astrophysics Data System (ADS)

Tschiersch, R.; Nemschokmichal, S.; Bogaczyk, M.; Meichsner, J.

2017-10-01

Single self-stabilized discharge filaments were investigated in the plane-parallel electrode configuration. The barrier discharge was operated inside a gap of 3 mm shielded by glass plates to both electrodes, using helium-nitrogen mixtures and a square-wave feeding voltage at a frequency of 2 kHz. The combined application of electrical measurements, ICCD camera imaging, optical emission spectroscopy and surface charge diagnostics via the electro-optic Pockels effect allowed the correlation of the discharge development in the volume and on the dielectric surfaces. The formation criteria and existence regimes were found by systematic variation of the nitrogen admixture to helium, the total pressure and the feeding voltage amplitude. Single self-stabilized discharge filaments can be operated over a wide parameter range, foremost, by significant reduction of the voltage amplitude after the operation in the microdischarge regime. Here, the outstanding importance of the surface charge memory effect on the long-term stability was pointed out by the recalculated spatio-temporally resolved gap voltage. The optical emission revealed discharge characteristics that are partially reminiscent of both the glow-like barrier discharge and the microdischarge regime, such as a Townsend pre-phase, a fast cathode-directed ionization front during the breakdown and radially propagating surface discharges during the afterglow.

A hollow cathode ion source for production of primary ions for the BNL electron beam ion source.

PubMed

Alessi, James; Beebe, Edward; Carlson, Charles; McCafferty, Daniel; Pikin, Alexander; Ritter, John

2014-02-01

A hollow cathode ion source, based on one developed at Saclay, has been modified significantly and used for several years to produce all primary 1+ ions injected into the Relativistic Heavy Ion Collider Electron Beam Ion Source (EBIS) at Brookhaven. Currents of tens to hundreds of microamperes have been produced for 1+ ions of He, C, O, Ne, Si, Ar, Ti, Fe, Cu, Kr, Xe, Ta, Au, and U. The source is very simple, relying on a glow discharge using a noble gas, between anode and a solid cathode containing the desired species. Ions of both the working gas and ionized sputtered cathode material are extracted, and then the desired species is selected using an ExB filter before being transported into the EBIS trap for charge breeding. The source operates pulsed with long life and excellent stability for most species. Reliable ignition of the discharge at low gas pressure is facilitated by the use of capacitive coupling from a simple toy plasma globe. The source design, and operating experience for the various species, is presented.

Cathodic and anodic biofilms in Single Chamber Microbial Fuel Cells.

PubMed

Cristiani, P; Carvalho, M L; Guerrini, E; Daghio, M; Santoro, C; Li, B

2013-08-01

The oxygen reduction due to microaerophilic biofilms grown on graphite cathodes (biocathodes) in Single Chamber Microbial Fuel Cells (SCMFCs) is proved and analysed in this paper. Pt-free cathode performances are compared with those of different platinum-loaded cathodes, before and after the biofilm growth. Membraneless SCMFCs were operating in batch-mode, filled with wastewater. A substrate (fuel) of sodium acetate (0.03 M) was periodically added and the experiment lasted more than six months. A maximum of power densities, up to 0.5 W m(-2), were reached when biofilms developed on the electrodes and the cathodic potential decreased (open circuit potential of 50-200 mV vs. SHE). The power output was almost constant with an acetate concentration of 0.01-0.05 M and it fell down when the pH of the media exceeded 9.5, independently of the Pt-free/Pt-loading at the cathodes. Current densities varied in the range of 1-5 Am(-2) (cathode area of 5 cm(2)). Quasi-stationary polarization curves performed with a three-electrode configuration on cathodic and anodic electrodes showed that the anodic overpotential, more than the cathodic one, may limit the current density in the SCMFCs for a long-term operation. Copyright © 2012 Elsevier B.V. All rights reserved.

The stability of the international oil trade network from short-term and long-term perspectives

NASA Astrophysics Data System (ADS)

Sun, Qingru; Gao, Xiangyun; Zhong, Weiqiong; Liu, Nairong

2017-09-01

To examine the stability of the international oil trade network and explore the influence of countries and trade relationships on the trade stability, we construct weighted and unweighted international oil trade networks based on complex network theory using oil trading data between countries from 1996 to 2014. We analyze the stability of international oil trade network (IOTN) from short-term and long-term aspects. From the short-term perspective, we find that the trade volumes play an important role on the stability. Moreover, the weighted IOTN is stable; however, the unweighted networks can better reflect the actual evolution of IOTN. From the long-term perspective, we identify trade relationships that are maintained during the whole sample period to reveal the situation of the whole international oil trade. We provide a way to quantitatively measure the stability of complex network from short-term and long-term perspectives, which can be applied to measure and analyze trade stability of other goods or services.

Acute and chronic effects of noradrenergic enhancement on transcranial direct current stimulation-induced neuroplasticity in humans.

PubMed

Kuo, Hsiao-I; Paulus, Walter; Batsikadze, Giorgi; Jamil, Asif; Kuo, Min-Fang; Nitsche, Michael A

2017-02-15

Chronic administration of the selective noradrenaline reuptake inhibitor (NRI) reboxetine (RBX) increased and prolonged the long-term potentiation-like plasticity induced by anodal transcranial direct current stimulation (tDCS) for over 24 h. Chronic administration of RBX converted cathodal tDCS-induced long-term depression-like plasticity into facilitation for 120 min. Chronic noradrenergic activity enhancement on plasticity of the human brain might partially explain the delayed therapeutic impact of selective NRIs in depression and other neuropsychiatric diseases. Noradrenaline affects cognition and motor learning processes via its impact on long-term potentiation (LTP) and depression (LTD). We aimed to explore the impact of single dose and chronic administration of the selective noradrenaline reuptake inhibitor (NRI) reboxetine (RBX) on plasticity induced by transcranial direct current stimulation (tDCS) in healthy humans via a double-blinded, placebo-controlled, randomized crossover study. Sixteen healthy volunteers received placebo or single dose RBX (8 mg) before anodal or cathodal tDCS of the primary motor cortex. Afterwards, the same subjects took RBX (8 mg day -1 ) consecutively for 21 days. During this period, two additional interventions were performed (RBX with anodal or cathodal tDCS), to explore the impact of chronic RBX treatment on plasticity. Plasticity was monitored by motor-evoked potential amplitudes elicited by transcranial magnetic stimulation. Chronic administration of RBX increased and prolonged the LTP-like plasticity induced by anodal tDCS for over 24 h. Chronic RBX significantly converted cathodal tDCS-induced LTD-like plasticity into facilitation, as compared to the single dose condition, for 120 min after stimulation. The results show a prominent impact of chronic noradrenergic enhancement on plasticity of the human brain that might partially explain the delayed therapeutic impact of selective NRIs in depression and other neuropsychiatric diseases. © 2016 The Authors. The Journal of Physiology © 2016 The Physiological Society.

Laser frequency stabilization by combining modulation transfer and frequency modulation spectroscopy.

PubMed

Zi, Fei; Wu, Xuejian; Zhong, Weicheng; Parker, Richard H; Yu, Chenghui; Budker, Simon; Lu, Xuanhui; Müller, Holger

2017-04-01

We present a hybrid laser frequency stabilization method combining modulation transfer spectroscopy (MTS) and frequency modulation spectroscopy (FMS) for the cesium D₂ transition. In a typical pump-probe setup, the error signal is a combination of the DC-coupled MTS error signal and the AC-coupled FMS error signal. This combines the long-term stability of the former with the high signal-to-noise ratio of the latter. In addition, we enhance the long-term frequency stability with laser intensity stabilization. By measuring the frequency difference between two independent hybrid spectroscopies, we investigate the short-and long-term stability. We find a long-term stability of 7.8 kHz characterized by a standard deviation of the beating frequency drift over the course of 10 h and a short-term stability of 1.9 kHz characterized by an Allan deviation of that at 2 s of integration time.

Mesoporous LiFeBO3/C hollow spheres for improved stability lithium-ion battery cathodes

NASA Astrophysics Data System (ADS)

Chen, Zhongxue; Cao, Liufei; Chen, Liang; Zhou, Haihui; Zheng, Chunman; Xie, Kai; Kuang, Yafei

2015-12-01

Polyanionic compounds are regarded as one of the most promising cathode materials for the next generation lithium-ion batteries due to their abundant resource and thermal stability. LiFeBO3 has a relatively higher capacity than olivine LiFePO4, however, moisture sensitivity and low conductivity hinder its further development. Here, we design and synthesize mesoporous LiFeBO3/C (LFB/C) hollow spheres to enhance its structural stability and electric conductivity, two LiFeBO3/C electrodes with different carbon content are prepared and tested. The experimental results show that mesoporous LiFeBO3/C hollow spheres with higher carbon content exhibit superior lithium storage capacity, cycling stability and rate capability. Particularly, the LFB/C electrode with higher carbon content demonstrates good structural stability, which can maintain its original crystal structure and Li storage properties even after three months of air exposure at room temperature. The exceptional structural stability and electrochemical performance may justify their potential use as high-performance cathode materials for advanced lithium-ion batteries. In addition, the synthesis strategy demonstrated herein is simple and versatile for the fabrication of other polyanionic cathode materials with mesoporous hollow spherical structure.

A review of blended cathode materials for use in Li-ion batteries

NASA Astrophysics Data System (ADS)

Chikkannanavar, Satishkumar B.; Bernardi, Dawn M.; Liu, Lingyun

2014-02-01

Several commercial automotive battery suppliers have developed lithium ion cells which use cathodes that consist of a mixture of two different active materials. This approach is intended to take advantage of the unique properties of each material and optimize the performance of the battery with respect to the automotive operating requirements. Certain cathode materials have high coulombic capacity and good cycling characteristics, but are costly and exhibit poor thermal stability (e.g., LiNixCo1-x-yAlyO2). Alternately, other cathode materials exhibit good thermal stability, high voltage and high rate capability, but have low capacity (e.g., LiMn2O4). By blending two cathode materials the shortcomings of the parent materials could be minimized and the resultant blend can be tailored to have a higher energy or power density coupled with enhanced stability and lower cost. In this review, we survey the developing field of blended cathode materials from a new perspective. Targeting a range of cathode materials, we survey the advances in the field in the current review. Limitations, such as capacity decay due to metal dissolution are also discussed, as well as how the appropriate balance of characteristics of the blended materials can be optimized for hybrid- and electric-vehicle applications.

Facet Dependent Disorder in the Pristine High Voltage Lithium-Manganese-Rich Cathode Material

DOE PAGES

Dixit, Hemant M.; Zhou, Wu; Idrobo Tapia, Juan Carlos; ...

2014-11-21

Defects and surface reconstructions are thought to be crucial for the long term stability of high-voltage lithium-manganese-rich cathodes. Unfortunately, many of these defects arise only after electrochemical cycling which occur under harsh conditions making it difficult to fully comprehend the role they play in degrading material performance. Recently, it has been observed that defects are present even in the pristine material. This study, therefore, focuses on examining the nature of the disorder observed in pristine Limore » $$_{1.2}$$Ni$$_{0.175}$$Mn$$_{0.525}$$Co$$_{0.1}$$O$$_2$$ (LNMCO) particles. Using atomic resolution Z-contrast imaging and electron energy-loss spectroscopy measurements we show that there are indeed a significant amount of anti-site defects present in this material; with transition metals substituting on Li metal sites. Furthermore, we find a strong tendency of segregation of these types of defects towards open facets (surfaces perpendicular to the layered arrangement of atoms), rather than closed facets (surfaces parallel to the layered arrangement of atoms). First principles calculations identify anti-site defect pairs of Ni swapping with Li ions as the predominant defect in the material. Furthermore, energetically favorable swapping of Ni on the Mn sites were observed to lead to Mn depletion at open facets. Relatively, low Ni migration barriers also support the notion that Ni are the predominant cause of disorder. These insights suggests that certain facets of the LNMCO particles may be more useful for inhibiting surface reconstruction and improving the stability of these materials through careful consideration of the exposed surface.« less

Electricity generation and brewery wastewater treatment from sequential anode-cathode microbial fuel cell.

PubMed

Wen, Qing; Wu, Ying; Zhao, Li-xin; Sun, Qian; Kong, Fan-ying

2010-02-01

A sequential anode-cathode double-chamber microbial fuel cell (MFC), in which the effluent of anode chamber was used as a continuous feed for an aerated cathode chamber, was constructed in this experiment to investigate the performance of brewery wastewater treatment in conjugation with electricity generation. Carbon fiber was used as anode and plain carbon felt with biofilm as cathode. When hydraulic retention time (HRT) was 14.7 h, a relatively high chemical oxygen demand (COD) removal efficiency of 91.7%-95.7% was achieved under long-term stable operation. The MFC displayed an open circuit voltage of 0.434 V and a maximum power density of 830 mW/m(3) at an external resistance of 300 Omega. To estimate the electrochemical performance of the MFC, electrochemical measurements were carried out and showed that polarization resistance of anode was the major limiting factor in the MFC. Since a high COD removal efficiency was achieved, we conclude that the sequential anode-cathode MFC constructed with bio-cathode in this experiment could provide a new approach for brewery wastewater treatment.

Electricity generation and brewery wastewater treatment from sequential anode-cathode microbial fuel cell*

PubMed Central

Wen, Qing; Wu, Ying; Zhao, Li-xin; Sun, Qian; Kong, Fan-ying

2010-01-01

A sequential anode-cathode double-chamber microbial fuel cell (MFC), in which the effluent of anode chamber was used as a continuous feed for an aerated cathode chamber, was constructed in this experiment to investigate the performance of brewery wastewater treatment in conjugation with electricity generation. Carbon fiber was used as anode and plain carbon felt with biofilm as cathode. When hydraulic retention time (HRT) was 14.7 h, a relatively high chemical oxygen demand (COD) removal efficiency of 91.7%–95.7% was achieved under long-term stable operation. The MFC displayed an open circuit voltage of 0.434 V and a maximum power density of 830 mW/m3 at an external resistance of 300 Ω. To estimate the electrochemical performance of the MFC, electrochemical measurements were carried out and showed that polarization resistance of anode was the major limiting factor in the MFC. Since a high COD removal efficiency was achieved, we conclude that the sequential anode-cathode MFC constructed with bio-cathode in this experiment could provide a new approach for brewery wastewater treatment. PMID:20104642

Analysis of the aging/stability process of organic solar cells based on PTB7:[70]PCBM and an alternative free-vacuum deposited cathode: the effect of active layer scaling

NASA Astrophysics Data System (ADS)

Barreiro-Argüelles, Denisse; Ramos-Ortiz, Gabriel; Maldonado, José-Luis L.; Romero-Borja, Daniel; Meneses-Nava, Marco-Antonio; Pérez-Gutiérrez, Enrique

2017-08-01

The PV performance and aging/stability of organic photovoltaic (OPV) devices based on the well-known system PTB7:[70]PCBM and an alternative air-stable electrode deposited at room conditions are fully studied when the active area is scaled by a factor of 25. On the other hand, the aging/stability processes were also studied through single diode model, impedance spectroscopy and light-beam induced current (LBIC) measurements in accordance with the established ISOS-D1 (dark storage) and ISOS-L1 (illumination conditions) protocols. Results are a good indication that the alternative cathode Field's metal (FM) cathode works as an encapsulating material and provides excellent PV performance comparable with the common and costly high-vacuum evaporated Al cathode.

Li-air batteries: Decouple to stabilize

NASA Astrophysics Data System (ADS)

Xu, Ji-Jing; Zhang, Xin-Bo

2017-09-01

The utilization of porous carbon cathodes in lithium-air batteries is hindered by their severe decomposition during battery cycling. Now, dual redox mediators are shown to decouple the complex electrochemical reactions at the cathode, avoiding cathode passivation and decomposition.

Ni nanotube array-based electrodes by electrochemical alloying and de-alloying for efficient water splitting.

PubMed

Teng, Xue; Wang, Jianying; Ji, Lvlv; Lv, Yaokang; Chen, Zuofeng

2018-05-17

The design of cost-efficient earth-abundant catalysts with superior performance for the hydrogen evolution reaction (HER) and oxygen evolution reaction (OER) is extremely important for future renewable energy production. Herein, we report a facile strategy for constructing Ni nanotube arrays (NTAs) on a Ni foam (NF) substrate through cathodic deposition of NiCu alloy followed by anodic stripping of metallic Cu. Based on Ni NTAs, the as-prepared NiSe2 NTA electrode by NiSe2 electrodeposition and the NiFeOx NTA electrode by dipping in Fe3+ solution exhibit excellent HER and OER performance in alkaline conditions. In these systems, Ni NTAs act as a binder-free multifunctional inner layer to support the electrocatalysts, offer a large specific surface area and serve as a fast electron transport pathway. Moreover, an alkaline electrolyzer has been constructed using NiFeOx NTAs as the anode and NiSe2 NTAs as the cathode, which only demands a cell voltage of 1.78 V to deliver a water-splitting current density of 500 mA cm-2, and demonstrates remarkable stability during long-term electrolysis. This work provides an attractive method for the design and fabrication of nanotube array-based catalyst electrodes for highly efficient water-splitting.

Operation of a long-pulse backward-wave oscillator using a disk cathode

NASA Astrophysics Data System (ADS)

Hahn, Kelly; Fuks, Mikhail I.; Schamiloglu, Edl

2001-08-01

Recent work at the University of New Mexico has studied the use of a circular disk cathode as the electron source in a long-pulse Backward Wave Oscillator (BWO) experiment. The use of this cathode was motivated by recent studies by Loza and Strelkov of the General Physics Institute in Russia that demonstrated that a relativistic electron beam with stable cross section could be sustained for over one microsecond. In our first investigations using this new cathode configuration we found that the microwave pulse length generated from a long pulse BWO increased somewhat compared to the case when a traditional annular `cookie-cutter' cathode was used. We attribute this pulse lengthening to the hypothesis that the disk cathode generates a relativistic electron beam that is less likely to radially expand, thereby minimizing wall interception and the generation of unwanted plasma. In this paper we describe details of work- in-progress relating to a comparison of microwave generation from a disk cathode and annular cathode in a long-pulse BWO.

Magnetic-cusp, cathodic-arc source

DOEpatents

Falabella, S.

1995-11-21

A magnetic-cusp for a cathodic-arc source wherein the arc is confined to the desired cathode surface, provides a current path for electrons from the cathode to the anode, and utilizes electric and magnetic fields to guide ions from the cathode to a point of use, such as substrates to be coated. The magnetic-cusp insures arc stability by an easy magnetic path from anode to cathode, while the straight-through arrangement leads to high ion transmission. 3 figs.

Recent progress in degradation and stabilization of organic solar cells

NASA Astrophysics Data System (ADS)

Cao, Huanqi; He, Weidong; Mao, Yiwu; Lin, Xiao; Ishikawa, Ken; Dickerson, James H.; Hess, Wayne P.

2014-10-01

Stability is of paramount importance in organic semiconductor devices, especially in organic solar cells (OSCs). Serious degradation in air limits wide applications of these flexible, light-weight and low-cost power-generation devices. Studying the stability of organic solar cells will help us understand degradation mechanisms and further improve the stability of these devices. There are many investigations into the efficiency and stability of OSCs. The efficiency and stability of devices even of the same photoactive materials are scattered in different papers. In particular, the extrinsic degradation that mainly occurs near the interface between the organic layer and the cathode is a major stability concern. In the past few years, researchers have developed many new cathodes and cathode buffer layers, some of which have astonishingly improved the stability of OSCs. In this review article, we discuss the recent developments of these materials and summarize recent progresses in the study of the degradation/stability of OSCs, with emphasis on the extrinsic degradation/stability that is related to the intrusion of oxygen and water. The review provides detailed insight into the current status of research on the stability of OSCs and seeks to facilitate the development of highly-efficient OSCs with enhanced stability.

Sulfur-impregnated disordered carbon nanotubes cathode for lithium-sulfur batteries.

PubMed

Guo, Juchen; Xu, Yunhua; Wang, Chunsheng

2011-10-12

The commercialization of lithium-sulfur batteries is hindered by low cycle stability and low efficiency, which are induced by sulfur active material loss and polysulfide shuttle reaction through dissolution into electrolyte. In this study, sulfur-impregnated disordered carbon nanotubes are synthesized as cathode material for the lithium-sulfur battery. The obtained sulfur-carbon tube cathodes demonstrate superior cyclability and Coulombic efficiency. More importantly, the electrochemical characterization indicates a new stabilization mechanism of sulfur in carbon induced by heat treatment.

“Ni-Less” Cathodes for High Energy Density, Intermediate Temperature Na-NiCl 2 Batteries

DOE Office of Scientific and Technical Information (OSTI.GOV)

Chang, Hee-Jung; Lu, Xiaochuan; Bonnett, Jeffery F.

Among various battery technologies being considered for stationary energy storage applications, sodium-metal halide (Na-MH) batteries have become one of the most attractive candidates because of the abundance of raw materials, long cycle life, high energy density, and superior safety. However, one of issues limiting its practical application is the relatively expensive nickel (Ni) used in the cathode. In the present work, we focus on of efforts to develop new Ni-based cathodes, and demonstrate that a much higher specific energy density of 405 Wh/kg (23% higher than state-of-the-art Na-MH batteries) can be achieved at an operating temperature of 190oC. Furthermore, 15%more » less Ni is used in the new cathode than that in conventional Na-NiCl2 batteries. Long-term cycling tests also show stable electrochemical performance for over 300 cycles with excellent capacity retention (~100%). The results in this work indicate that these advances can significantly reduce the raw material cost associated with Ni (a 31% reduction) and promote practical applications of Na-MH battery technologies in stationary energy storage systems.« less

Degradation Mechanisms at the Li10GeP2S12/LiCoO2 Cathode Interface in an All-Solid-State Lithium-Ion Battery.

PubMed

Zhang, Wenbo; Richter, Felix H; Culver, Sean P; Leichtweiss, Thomas; Lozano, Juan G; Dietrich, Christian; Bruce, Peter G; Zeier, Wolfgang G; Janek, Jürgen

2018-06-20

All-solid-state batteries (ASSBs) show great potential for providing high power and energy densities with enhanced battery safety. While new solid electrolytes (SEs) have been developed with high enough ionic conductivities, SSBs with long operational life are still rarely reported. Therefore, on the way to high-performance and long-life ASSBs, a better understanding of the complex degradation mechanisms, occurring at the electrode/electrolyte interfaces is pivotal. While the lithium metal/solid electrolyte interface is receiving considerable attention due to the quest for high energy density, the interface between the active material and solid electrolyte particles within the composite cathode is arguably the most difficult to solve and study. In this work, multiple characterization methods are combined to better understand the processes that occur at the LiCoO 2 cathode and the Li 10 GeP 2 S 12 solid electrolyte interface. Indium and Li 4 Ti 5 O 12 are used as anode materials to avoid the instability problems associated with Li-metal anodes. Capacity fading and increased impedances are observed during long-term cycling. Postmortem analysis with scanning transmission electron microscopy, electron energy loss spectroscopy, X-ray diffraction, and X-ray photoelectron spectroscopy show that electrochemically driven mechanical failure and degradation at the cathode/solid electrolyte interface contribute to the increase in internal resistance and the resulting capacity fading. These results suggest that the development of electrochemically more stable SEs and the engineering of cathode/SE interfaces are crucial for achieving reliable SSB performance.

In-situ synthesis of monodisperse micro-nanospherical LiFePO4/carbon cathode composites for lithium-ion batteries

NASA Astrophysics Data System (ADS)

Gong, Hao; Xue, Hairong; Wang, Tao; He, Jianping

2016-06-01

The LiFePO4 is recognized as the promising cathode material, due to its high specific capacity, excellent, structural stability and environmental benignity. However, it is blamed for the low tap density and poor rate performance when served as the cathode materials for a long time. Here, the microspheric LiFePO4/C composites are successfully synthesized through a one-step in-situ solvothermal method combined with carbothermic reduction. These LiFePO4/C microspheres are assembled by LiFePO4 nanoparticles (∼100 nm) and uniformly coated by the carbon, which show a narrow diameter distribution of 4 μm. As a cathode material for lithium ion batteries, the LiFePO4/C composites can deliver an initiate charge capacity of 155 mAh g-1 and retain 90% of initial capacity after 200 cycles at 0.1 C. When cycled at high current densities up to 20 C, it shows a discharge capacity of ∼60 mAh g-1, exhibiting superior rate performance. The significantly improved electrochemical performance of LiFePO4/C composites material can be attributed to its special micro-nano hierarchical structure. Microspheric LiFePO4/C composites exhibit a high tap density about 1.3 g cm-3. What's more, the well-coated carbon insures the high electrical conductivity and the nano-sized LiFePO4/C particles shorten lithium ion transport, thus exhibiting the high specific capacity, high cycling stability and good rate performance.

Polysulfide Binding to Several Nanoscale Magnéli Phases Synthesized in Carbon for Long-Life Lithium-Sulfur Battery Cathodes.

PubMed

Zubair, Usman; Amici, Julia; Francia, Carlotta; McNulty, David; Bodoardo, Silvia; O'Dwyer, Colm

2018-06-11

In Li-S batteries, it is important to ensure efficient reversible conversion of sulfur to lithium polysulfide (LiPS). Shuttling effects caused by LiPS dissolution can lead to reduced performance and cycle life. Although carbon materials rely on physical trapping of polysulfides, polar oxide surfaces can chemically bind LiPS to improve the stability of sulfur cathodes. We show a simple synthetic method that allows high sulfur loading into mesoporous carbon preloaded with spatially localized nanoparticles of several Magnéli-phase titanium oxide (Ti n O 2n-1 ). This material simultaneously suppresses polysulfide shuttling phenomena by chemically binding Li polysulfides onto several Magnéli-phase surfaces in a single cathode and ensures physical confinement of sulfur and LiPS. The synergy between chemical immobilization of significant quantities of LiPS at the surface of several Ti n O 2n-1 phases and physical entrapment results in coulombically efficient high-rate cathodes with long cycle life and high capacity. These cathodes function efficiently at low electrolyte-to-sulfur ratios to provide high gravimetric and volumetric capacities in comparison with their highly porous carbon counterparts. Assembled coin cells have an initial discharge capacity of 1100 mAh g -1 at 0.1C and maintain a reversible capacity of 520 mAh g -1 at 0.2C for more than 500 cycles. Even at 1C, the cell loses only 0.06 % per cycle for 1000 cycles with a coulombic efficiency close to 99 %. © 2018 Wiley-VCH Verlag GmbH & Co. KGaA, Weinheim.

Reduced Kalman Filters for Clock Ensembles

NASA Technical Reports Server (NTRS)

Greenhall, Charles A.

2011-01-01

This paper summarizes the author's work ontimescales based on Kalman filters that act upon the clock comparisons. The natural Kalman timescale algorithm tends to optimize long-term timescale stability at the expense of short-term stability. By subjecting each post-measurement error covariance matrix to a non-transparent reduction operation, one obtains corrected clocks with improved short-term stability and little sacrifice of long-term stability.

Advanced intermediate temperature sodium-nickel chloride batteries with ultra-high energy density

DOE PAGES

Li, Guosheng; Lu, Xiaochuan; Kim, Jin Yong; ...

2016-02-11

Here we demonstrate for the first time that planar Na-NiCl 2 batteries can be operated at an intermediate temperature of 190°C with ultra-high energy density. A specific energy density of 350 Wh/kg, which is 3 times higher than that of conventional tubular Na-NiCl 2 batteries operated at 280°C, was obtained for planar Na-NiCl 2 batteries operated at 190°C over a long-term cell test (1000 cycles). The high energy density and superior cycle stability are attributed to the slower particle growth of the cathode materials (NaCl and Ni) at 190°C. The results reported in this work demonstrate that planar Na-NiCl 2more » batteries operated at an intermediate temperature could greatly benefit this traditional energy storage technology by improving battery energy density, cycle life and reducing material costs.« less

Biological Fuel Cells and Membranes.

PubMed

Ghassemi, Zahra; Slaughter, Gymama

2017-01-17

Biofuel cells have been widely used to generate bioelectricity. Early biofuel cells employ a semi-permeable membrane to separate the anodic and cathodic compartments. The impact of different membrane materials and compositions has also been explored. Some membrane materials are employed strictly as membrane separators, while some have gained significant attention in the immobilization of enzymes or microorganisms within or behind the membrane at the electrode surface. The membrane material affects the transfer rate of the chemical species (e.g., fuel, oxygen molecules, and products) involved in the chemical reaction, which in turn has an impact on the performance of the biofuel cell. For enzymatic biofuel cells, Nafion, modified Nafion, and chitosan membranes have been used widely and continue to hold great promise in the long-term stability of enzymes and microorganisms encapsulated within them. This article provides a review of the most widely used membrane materials in the development of enzymatic and microbial biofuel cells.

Optically transparent cathode for Co(III/II) mediated dye-sensitized solar cells based on graphene oxide.

PubMed

Kavan, Ladislav; Yum, Jun-Ho; Graetzel, Michael

2012-12-01

Thin semitransparent films were fabricated on F-doped SnO(2) (FTO) from single-layer graphene oxide (GO) either pure or in a composite with graphene nanoplatelets. Electrocatalytic activity of prepared films was tested for the Co(bpy)(3)(3+/2+) redox couple in acetonitrile electrolyte solution. Pristine GO showed almost no activity, resembling the properties of basal plane pyrolytic graphite. However, electrochemical performance of graphene oxide improved dramatically upon chemical reduction with hydrazine and/or heat treatment. All GO-containing films were firmly bonded to FTO, which contrasted with the poor adhesion of sole graphene nanoplatelets to this support. The activity loss during long-term aging was considerably improved, too. Enhanced stability of GO-containing films together with high electrocatalytic activity is beneficial for application in a new generation of dye-sensitized solar cells employing Co(bpy)(3)(3+/2+) as the redox shuttle.

Template-directed fabrication of porous gas diffusion layer for magnesium air batteries

NASA Astrophysics Data System (ADS)

Xue, Yejian; Miao, He; Sun, Shanshan; Wang, Qin; Li, Shihua; Liu, Zhaoping

2015-11-01

The uniform micropore distribution in the gas diffusion layers (GDLs) of the air-breathing cathode is very important for the metal air batteries. In this work, the super-hydrophobic GDL with the interconnected regular pores is prepared by a facile silica template method, and then the electrochemical properties of the Mg air batteries containing these GDLs are investigated. The results indicate that the interconnected and uniform pore structure, the available water-breakout pressure and the high gas permeability coefficient of the GDL can be obtained by the application of 30% silica template. The maximum power density of the Mg air battery containing the GDL with 30% regular pores reaches 88.9 mW cm-2 which is about 1.2 times that containing the pristine GDL. Furthermore, the GDL with 30% regular pores exhibits the improved the long term hydrophobic stability.

Biological Fuel Cells and Membranes

PubMed Central

Ghassemi, Zahra; Slaughter, Gymama

2017-01-01

Biofuel cells have been widely used to generate bioelectricity. Early biofuel cells employ a semi-permeable membrane to separate the anodic and cathodic compartments. The impact of different membrane materials and compositions has also been explored. Some membrane materials are employed strictly as membrane separators, while some have gained significant attention in the immobilization of enzymes or microorganisms within or behind the membrane at the electrode surface. The membrane material affects the transfer rate of the chemical species (e.g., fuel, oxygen molecules, and products) involved in the chemical reaction, which in turn has an impact on the performance of the biofuel cell. For enzymatic biofuel cells, Nafion, modified Nafion, and chitosan membranes have been used widely and continue to hold great promise in the long-term stability of enzymes and microorganisms encapsulated within them. This article provides a review of the most widely used membrane materials in the development of enzymatic and microbial biofuel cells. PMID:28106711

Chemical Immobilization Effect on Lithium Polysulfides for Lithium-Sulfur Batteries.

PubMed

Li, Caixia; Xi, Zhucong; Guo, Dexiang; Chen, Xiangju; Yin, Longwei

2018-01-01

Despite great progress in lithium-sulfur batteries (LSBs), great obstacles still exist to achieve high loading content of sulfur and avoid the loss of active materials due to the dissolution of the intermediate polysulfide products in the electrolyte. Relationships between the intrinsic properties of nanostructured hosts and electrochemical performance of LSBs, especially, the chemical interaction effects on immobilizing polysulfides for LSB cathodes, are discussed in this Review. Moreover, the principle of rational microstructure design for LSB cathode materials with strong chemical interaction adsorbent effects on polysulfides, such as metallic compounds, metal particles, organic polymers, and heteroatom-doped carbon, is mainly described. According to the chemical immobilizing mechanism of polysulfide on LSB cathodes, three kinds of chemical immobilizing effects, including the strong chemical affinity between polar host and polar polysulfides, the chemical bonding effect between sulfur and the special function groups/atoms, and the catalytic effect on electrochemical reaction kinetics, are thoroughly reviewed. To improve the electrochemical performance and long cycling life-cycle stability of LSBs, possible solutions and strategies with respect to the rational design of the microstructure of LSB cathodes are comprehensively analyzed. © 2017 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Long-Life and High-Power Binder-Free Cathode Based on One-Step Synthesis of Radical Polymers with Multi-Pendant Groups.

PubMed

Chen, Yaoguang; Zhang, Yangfan; Liu, Xiu; Fan, Xuliang; Bai, Bing; Yang, Kang; Liang, Zhongxin; Zhang, Zishou; Mai, Kancheng

2018-05-16

The main bottlenecks for the widespread application of radical polymers in organic radical batteries are poor cycling stability, due to the dissolution of radical polymers into the electrolyte, and the low efficiency of multi-step synthesis strategies. Herein, a kind of electrolyte-resistant radical polymer bearing multi-pendant groups (poly(ethylene-alt-TEMPO maleate) (PETM)) is designed and synthesized through a one-step esterification reaction to graft 4-hydroxy-2,2,6,6-teramethylpiperidinyl-1-oxy into the commercially available poly(ethylene-alt-maleic anhydride). Interestingly, PETM is hardly soluble in the ethylene carbonate/dimethyl carbonate/ethyl methyl carbonate-based electrolyte, showing an extremely low solubility of 0.59 mg mL -1 , but is easily soluble in tetrahydrofuran and N-Methyl pyrrolidone. The derived binder-free PETM cathode exhibits nearly 100% utilization of the grafted nitroxide radicals (88 mA h g -1 ) and excellent rate capability with almost invariant capacitance from 10 C to 40 C. Significantly, the PETM cathodes retain 94% of the initial capacity after 1000 cycles, outperforming most reported radical polymer-based cathodes. © 2018 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Intraindividual stability of cortisol and cortisone and the ratio of cortisol to cortisone in saliva, urine and hair.

PubMed

Zhang, Quan; Chen, Zheng; Chen, Shenghuo; Xu, Youyun; Deng, Huihua

2017-02-01

Cortisol, cortisone and the ratio of cortisol to cortisone in saliva, urine and hair are acute, short-term and long-term biomarkers to reliably assess the activity of hypothalamic-pituitary-adrenal (HPA) axis and 11β-hydroxysteroid dehydrogenase (11β-HSD). One key issue is whether these biomarkers have intraindividual relative stability. Salivary, urinary and hair cortisol was proven to show considerable long-term intraindividual relative stability. However, currently unknown is whether cortisone and the ratio in saliva, urine and hair show intraindividual relative stability. The present study utilized a longitudinal design to validate long-term stability within two weeks of three biomarkers in saliva and urine, and long-term stability within twelve months of three hair biomarkers. Salivary, urinary and hair steroids were measured with high performance liquid chromatography tandem mass spectrometry. Three biomarkers in urine and hair showed moderate test-retest correlations with coefficient (r) ranging between 0.22 and 0.56 and good multiple-test consistencies with coefficient of intraclass correlation (ICC) ranging between 0.42 and 0.67. Three single-point salivary biomarkers showed weak to moderate test-retest correlations (r's between 0.01 and 0.38) and poor to fair multiple-test consistencies (ICC's between 0.29 and 0.53) within two weeks. Three single-day salivary biomarkers showed moderate test-retest correlations (r's between 0.23 and 0.53) and good multiple-test consistencies (ICC's between 0.56 and 0.66) within two weeks. Three biomarkers in urine and hair showed moderate long-term intraindividual relative stability. Three single-point salivary biomarkers showed weak to moderate short-term and long-term intraindividual relative stability, but three single-day salivary biomarkers showed moderate short-term and long-term intraindividual relative stability. Copyright © 2016 Elsevier Inc. All rights reserved.

Unprecedented long-term frequency stability with a microwave resonator oscillator.

PubMed

Grop, Serge; Schafer, Wolfgang; Bourgeois, Pierre-Yves; Kersale, Yann; Oxborrow, Mark; Rubiola, Enrico; Giordano, Vincent

2011-08-01

This article reports on the long-term frequency stability characterization of a new type of cryogenic sapphire oscillator using an autonomous pulse-tube cryocooler as its cold source. This new design enables a relative frequency stability of better than 4.5 x 10(-15) over one day of integration. To the best of our knowledge, this represents the best long-term frequency stability ever obtained with a signal source based on a macroscopic resonator.

Solid State Li-ion Batteries

DTIC Science & Technology

2013-10-23

sulfur (FeS + S) cathode (26). The pairing of a lithium free FeS + S cathode and a lithium free STN anode presents an easily overcome obstacle. Our...upon the combined mass of both the composite anode and cathode. To realize this full cell, we pair an iron sulfide and sulfur composite cathode with a...capacity reported to date. To utilize both a lithium free anode and cathode, we adopt a pre-lithiation technique involving stabilized lithium metal

NON-BLOCKING STABILIZED FEED BACK AMPLIFIER

DOEpatents

Fairstein, E.

1960-03-01

A plural stuge nonblocking degenerative feed-back amplifier was designed particularly suitable for counting circuits because of the stability and linearity in operation, characterized by the fact that the inltial stage employs a cathode coupled input circuit fed from a cathode follower and the final stage has a tline constant greater than those of the other stages.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Tan, Guoqiang; Wu, Feng; Zhan, Chun

The development of safe, stable, and long-life Li-ion batteries is being intensively pursued to enable the electrification of transportation and intelligent grid applications. Here, we report a new solid-state Li-ion battery technology, using a solid nanocomposite electrolyte composed of porous silica matrices with in situ immobilizing Li+ conducting ionic liquid, anode material of MCMB, and cathode material of LiCoO 2, LiNi 1/3Co 1/3Mn 1/3O 2, or LiFePO 4. An injection printing method is used for the electrode/electrolyte preparation. Solid nanocomposite electrolytes exhibit superior performance to the conventional organic electrolytes with regard to safety and cycle-life. They also have a transparentmore » glassy structure with high ionic conductivity and good mechanical strength. Solid-state full cells tested with the various cathodes exhibited high specific capacities, long cycling stability, and excellent high temperature performance. This solid-state battery technology will provide new avenues for the rational engineering of advanced Li-ion batteries and other electrochemical devices.« less

Dynamic Octahedral Breathing in Oxygen-Deficient Ba(0.9)Co(0.7)Fe(0.2)Nb(0.1)O(3-δ) Perovskite Performing as a Cathode in Intermediate-Temperature SOFC.

PubMed

Gong, Yudong; Sun, Chunwen; Huang, Qiu-an; Alonso, Jose Antonio; Fernández-Díaz, Maria Teresa; Chen, Liquan

2016-03-21

Ba(0.9)Co(0.7)Fe(0.2)Nb(0.1)O(3-δ) outperforms as a cathode in solid-oxide fuel cells (SOFC), at temperatures as low as 700-750 °C. The microscopical reason for this performance was investigated by temperature-dependent neutron powder diffraction (NPD) experiments. In the temperature range of 25-800 °C, Ba(0.9)Co(0.7)Fe(0.2)Nb(0.1)O(3-δ) shows a perfectly cubic structure (a = a0), with a significant oxygen deficiency in a single oxygen site, that substantially increases at the working temperatures of a SOFC. The anisotropic thermal motion of oxygen atoms considerably rises with T, reaching B(eq) ≈ 5 Å(2) at 800 °C, with prolate cigar-shaped, anisotropic vibration ellipsoids that suggest a dynamic breathing of the octahedra as oxygen ions diffuse across the structure by a vacancies mechanism, thus implying a significant ionic mobility that could be described as a molten oxygen sublattice. The test cell with a La(0.8)Sr(0.2)Ga(0.83)Mg(0.17)O(3-δ) electrolyte (∼300 μm in thickness)-supported configuration yields a peak power density of 0.20 and 0.40 W cm(-2) at temperatures of 700 and 750 °C, respectively, with pure H2 as fuel and ambient air as oxidant. The electrochemical impedance spectra (EIS) evolution with time of the symmetric cathode fuel cell measured at 750 °C shows that the Ba(0.9)Co(0.7)Fe(0.2)Nb(0.1)O(3-δ) cathode possesses a superior ORR catalytic activity and long-term stability. The mixed electronic-ionic conduction properties of Ba(0.9)Co(0.7)Fe(0.2)Nb(0.1)O(3-δ) account for its good performance as an oxygen-reduction catalyst.

Promoting Healthy Weight with "Stability Skills First": A Randomized Trial

ERIC Educational Resources Information Center

Kiernan, Michaela; Brown, Susan D.; Schoffman, Danielle E.; Lee, Katherine; King, Abby C.; Taylor, C. Barr; Schleicher, Nina C.; Perri, Michael G.

2013-01-01

Objective: Although behavioral weight-loss interventions produce short-term weight loss, long-term maintenance remains elusive. This randomized trial examined whether learning a novel set of "stability skills" before losing weight improved long-term weight management. Stability skills were designed to optimize individuals' current…

A hermetic self-sustained microbial solar cell based on Chlorella vulgaris and a versatile charge transfer chain

NASA Astrophysics Data System (ADS)

Pan, Keliang; Zhou, Peijiang

2015-10-01

A hermetic noble-metal-free membrane-less microbial solar cell (MSC) is established. The substances decomposition and regeneration in this MSC are carried out only by Chlorella vulgaris simultaneously. The conversion of metabolism types of C. vulgaris is controlled only by illumination. By using a pleiotropic redox mediator and a cupric hexacyanoferrate modified cathode, a two-phase three-stage charge transfer chain is formed. Through this pathway, the one microorganism self-sustained system gets a long-term power output up to 0.04773 mW/cm2 at 0.423 V without any material exchange with external, which is 50 times higher than that obtained from the original system. Benefiting from this electron buffer system, the battery will achieve an electricity generation in both light and dark conditions. There is almost no consumption of any substrates throughout the stabilized process, and no more additions are required. This maintenance-free and extremely inexpensive reactor with a simple structure and a long service life demonstrates the possibility of combining the microbial, chemical and photo cells.

Final Scientific/Technical Report for Low Cost, High Capacity Non- Intercalation Chemistry Automotive Cells

DOE Office of Scientific and Technical Information (OSTI.GOV)

Berdichevsky, Gene

Commercial Li-ion batteries typically use Ni- and Co-based intercalation cathodes. As the demand for improved performance from batteries increases, these cathode materials will no longer be able to provide the desired energy storage characteristics since they are currently approaching their theoretical limits. Conversion cathode materials are prime candidates for improvement of Li-ion batteries. On both a volumetric and gravimetric basis they have higher theoretical capacity than intercalation cathode materials. Metal fluoride (MFx) cathodes offer higher specific energy density and dramatically higher volumetric energy density. Challenges associated with metal fluoride cathodes were addressed through nanostructured material design and synthesis. A majormore » goal of this project was to develop and demonstrate Li-ion cells based on Si-comprising anodes and metal fluoride (MFx) comprising cathodes. Pairing the high-capacity MFx cathode with a high-capacity anode, such as an alloying Si anode, allows for the highest possible energy density on a cell level. After facing and overcoming multiple material synthesis and electrochemical instability challenges, we succeeded in fabrication of MFx half cells with cycle stability in excess of 500 cycles (to 20% or smaller degradation) and full cells with MFx-based cathodes and Si-based anodes with cycle stability in excess of 200 cycles (to 20% or smaller degradation).« less

Degradation Study by Start-Up/Shut-Down Cycling of Superhydrophobic Electrosprayed Catalyst Layers Using a Localized Reference Electrode Technique.

PubMed

Ferreira-Aparicio, Paloma; Chaparro, Antonio M; Folgado, M Antonia; Conde, Julio J; Brightman, Edward; Hinds, Gareth

2017-03-29

Degradation of a polymer electrolyte membrane fuel cell (PEMFC) with electrosprayed cathode catalyst layers is investigated during cyclic start-up and shut-down events. The study is carried out within a single cell incorporating an array of reference electrodes that enables measurement of cell current as a function of local cathode potential (localized polarization curves). Accelerated degradation of the cell by start-up/shut-down cycling gives rise to inhomogeneous performance loss, which is more severe close to the gas outlet and occurs predominantly during start-up. The degradation consists primarily of loss of cathode catalyst activity and increase in cell internal resistance, which is attributed to carbon corrosion and Pt aggregation in both anode and cathode. Cells with an electrosprayed cathode catalyst layer show lower degradation rates during the first 100 cycles, compared with those of a conventional gas diffusion electrode. This difference in behavior is attributed to the high hydrophobicity of the electrosprayed catalyst layer microstructure, which retards the kinetics of corrosion of the carbon support. In the long term, however, the degradation rate is dominated by the Pt/C ratio in the cathode catalyst layer.

Degradation of oxygen reduction reaction kinetics in porous La0.6Sr0.4Co0.2Fe0.8O3-δ cathodes due to aging-induced changes in surface chemistry

NASA Astrophysics Data System (ADS)

Baqué, Laura C.; Soldati, Analía L.; Teixeira-Neto, Erico; Troiani, Horacio E.; Schreiber, Anja; Serquis, Adriana C.

2017-01-01

The modification of surface composition after long-term operation is one of the most reported degradation mechanisms of (La,Sr)(Co,Fe)O3-δ (LSCFO) cathodes for Solid Oxide Fuel Cells (SOFCs). Nevertheless, its effect on the oxygen reduction reaction kinetics of porous LSCFO cathodes has not been yet reliably established. In this work, La- and Sr-enrichment at the LSCFO surface of porous cathodes has been induced after 50 h aging at 800 °C under air. Such cation redistribution can extend up to ∼400 nm depth under the LSCFO surface as detected by high resolution Scanning Transmission Electron Microscopy-Energy Dispersive Spectroscopy maps acquired inside the cathode pores. The observed surface chemical changes hamper the oxygen surface exchange reaction at the LSCFO/gas interface. Accordingly, a suitable Electrochemical Impedance Spectroscopy analysis revealed that the oxygen ion conductivity remains practically unaltered during the aging treatment while the oxygen surface exchange resistance increases up to 1.8 times. As a result, the cathode impedance response deteriorates within the 10-0.1 Hz frequency range during the aging treatment, resulting in a total cathode area specific resistance increase of 150%. The methodology adopted has demonstrated to be very valuable for studying the degradation of SOFC cathodes produced by the modification of surface composition.

High performance C/S composite cathodes with conventional carbonate-based electrolytes in Li-S battery.

PubMed

Zheng, Shiyou; Han, Pan; Han, Zhuo; Zhang, Huijuan; Tang, Zhihong; Yang, Junhe

2014-04-29

High stable C/S composites are fabricated by a novel high-temperature sulfur infusion into micro-mesoporous carbon method following with solvent cleaning treatment. The C/S composite cathodes show high Coulombic efficiency, long cycling stability and good rate capability in the electrolyte of 1.0 M LiPF6 + EC/DEC (1:1 v/v), for instance, the reversible capacity of the treated C/S-50 (50% S) cathode retains around 860 mAh/g even after 500 cycles and the Coulombic efficiency is close to 100%, which demonstrates the best electrochemical performance of carbon-sulfur composite cathodes using the carbonate-based electrolyte reported to date. It is believed that the chemical bond of C-S is responsible for the superior electrochemical properties in Li-S battery, that is, the strong interaction between S and carbon matrix significantly improves the conductivity of S, effectively buffers the structural strain/stress caused by the large volume change during lithiation/delithiation, completely eliminates the formation of high-order polysulfide intermediates, and substantially avoids the shuttle reaction and the side reaction between polysulfide anions and carbonate solvent, and thus enables the C/S cathode to use conventional carbonate-based electrolytes and achieve outstanding electrochemical properties in Li-S battery. The results may substantially contribute to the progress of the Li-S battery technology.

Stabilizing the Electrode/Electrolyte Interface of LiNi0.8Co0.15Al0.05O2 through Tailoring Aluminum Distribution in Microspheres as Long-Life, High-Rate, and Safe Cathode for Lithium-Ion Batteries.

PubMed

Hou, Peiyu; Zhang, Hongzhou; Deng, Xiaolong; Xu, Xijin; Zhang, Lianqi

2017-09-06

The unstable electrode/electrolyte interface of high-capacity LiNi 0.8 Co 0.15 Al 0.05 O 2 (NCA) cathodes, especially at a highly delithiated state, usually leads to the transformation of layered to spinel and/or rock-salt phases, resulting in drastic capacity fade and poor thermal stability. Herein, the Al-increased and Ni-,Co-decreased electrode surface is fabricated through tailoring element distribution in micrometer-sized spherical NCA secondary particles via coprecipitation and solid-state reactions, aimed at stabilizing the electrode/electrolyte interface during continuous cycles. As expected, it shows much extended cycle life, 93.6% capacity retention within 100 cycles, compared with that of 78.5% for the normal NCA. It also delivers large reversible capacity of about 140 mAh g -1 even at 20 C, corresponding to energy density of around 480 Wh kg -1 , which is enhanced by 45% compared to that of the normal NCA (about 330 Wh kg -1 ). Besides, the delayed heat emission temperature and reduced heat generation mean remarkably improved thermal stability. These foregoing improvements are ascribed to the Al-increased spherical secondary particle surface that stabilizes the electrode/electrolyte interface by protecting inner components from directly contacting with electrolyte and suppressing the side reaction on electrode surface between high oxidizing Ni 4+ and electrolyte.

Facile synthesis of lithium sulfide nanocrystals for use in advanced rechargeable batteries

DOE PAGES

Li, Xuemin; Wolden, Colin A.; Ban, Chunmei; ...

2015-12-03

This work reports a new method of synthesizing anhydrous lithium sulfide (L i2S) nanocrystals and demonstrates their potential as cathode materials for advanced rechargeable batteries. Li 2S is synthesized by reacting hydrogen sulfide (H 2S) with lithium naphthalenide (Li-NAP), a thermodynamically spontaneous reaction that proceeds to completion rapidly at ambient temperature and pressure. The process completely removes H 2S, a major industrial waste, while cogenerating 1,4-dihydronaphthalene, itself a value-added chemical that can be used as liquid fuel. The phase purity, morphology, and homogeneity of the resulting nanopowders were confirmed by X-ray diffraction and scanning electron microscopy. The synthesized Li 2Smore » nanoparticles (100 nm) were assembled into cathodes, and their performance was compared to that of cathodes fabricated using commercial Li 2S micropowders (1–5 μm). As a result, electrochemical analyses demonstrated that the synthesized Li 2S were superior in terms of (dis)charge capacity, cycling stability, output voltage, and voltage efficiency.« less

Durability of nickel-metal hydride (Ni-MH) battery cathode using nickel-aluminum layered double hydroxide/carbon (Ni-Al LDH/C) composite

NASA Astrophysics Data System (ADS)

Béléké, Alexis Bienvenu; Higuchi, Eiji; Inoue, Hiroshi; Mizuhata, Minoru

2014-02-01

We report the durability of the optimized nickel-aluminum layered double hydroxide/carbon (Ni-Al LDH/C) composite prepared by liquid phase deposition (LPD) as cathode active materials in nickel metal hydride (Ni-MH) secondary battery. The positive electrode was used for charge-discharge measurements under two different current: 5 mA for 300 cycles in half-cell conditions, and 5.8 mA for 569 cycles in battery regime, respectively. The optimized Ni-Al LDH/C composite exhibits a good lifespan and stability with the capacity retention above 380 mA h gcomp-1 over 869 cycles. Cyclic voltammetry shows that the α-Ni(OH)2/γ-NiOOH redox reaction is maintained even after 869 cycles, and the higher current regime is beneficial in terms of materials utilization. X-ray diffraction (XRD) patterns of the cathode after charge and discharge confirms that the α-Ni(OH)2/γ-NiOOH redox reaction occurs without any intermediate phase.

Long term stability following genioplasty: a cephalometric study.

PubMed

Kumar, B Lakshman; Raju, G Kranthi Praveen; Kumar, N Dilip; Reddy, G Vivek; Naik, B Ravindra; Achary, C Ravindranath

2015-04-01

A receding chin associated with an orthognathic mandible is a common situation and surgical changes in chin position are often required to improve the overall harmony of the face. Genioplasty is one such procedure. Stability of hard and soft tissue changes following genioplasty on a long term basis needs to be assessed. Studies on the stability of hard and soft tissue changes following genioplasty on a short term basis have revealed it as a procedure with good stability. This study is done to assess the stability of hard and soft tissue changes following genioplasty on a long term basis. Pre-surgical, postsurgical and long term post-surgical cephalograms of 15 cases treated by vertical reduction augmentation genioplasty were obtained. Paired t-test was used to compare the changes between pre-surgical, postsurgical and long term postsurgical cephalograms. Findings of this study demonstrated that genioplasty is a stable procedure. After long term follow-up period, there was a relapse of 1.5 mm at the pogonion accounting for 24% of the surgical advancement. This is attributed to the remodeling that occurs at the surgical site, but not the instability due to the surgical procedure. With the present study, it can be concluded that vertical reduction and advancement genioplasty can be considered as an adjunctive procedure that produces predictable results and the bony and soft tissue stability were generally very good.

Long Term Stability Following Genioplasty: A Cephalometric Study

PubMed Central

Kumar, B Lakshman; Raju, G Kranthi Praveen; Kumar, N Dilip; Reddy, G Vivek; Naik, B Ravindra; Achary, C Ravindranath

2015-01-01

Background: A receding chin associated with an orthognathic mandible is a common situation and surgical changes in chin position are often required to improve the overall harmony of the face. Genioplasty is one such procedure. Stability of hard and soft tissue changes following genioplasty on a long term basis needs to be assessed. Studies on the stability of hard and soft tissue changes following genioplasty on a short term basis have revealed it as a procedure with good stability. This study is done to assess the stability of hard and soft tissue changes following genioplasty on a long term basis. Materials and Methods: Pre-surgical, postsurgical and long term post-surgical cephalograms of 15 cases treated by vertical reduction augmentation genioplasty were obtained. Paired t-test was used to compare the changes between pre-surgical, postsurgical and long term postsurgical cephalograms. Results: Findings of this study demonstrated that genioplasty is a stable procedure. After long term follow-up period, there was a relapse of 1.5 mm at the pogonion accounting for 24% of the surgical advancement. This is attributed to the remodeling that occurs at the surgical site, but not the instability due to the surgical procedure. Conclusion: With the present study, it can be concluded that vertical reduction and advancement genioplasty can be considered as an adjunctive procedure that produces predictable results and the bony and soft tissue stability were generally very good. PMID:25954070

A Mössbauer spectral study of degradation in La 0.58Sr 0.4Fe 0.5Co 0.5O 3–x after long-term operation in solid oxide electrolysis cells

DOE Office of Scientific and Technical Information (OSTI.GOV)

Mahmoud, Abdelfattah; Daroukh, Mahmoud Al; Lipinska-Chwalek, Marta

Here, degradation processes of oxygen electrodes in solid oxide electrolysis cells (SOECs) were studied by X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM) and Mössbauer spectroscopy. La 0.58Sr 0.4Fe 0.5Co 0.5O 3–x (LSCF) anodes (oxygen electrode) were analyzed after different long-term operations durations of 1774, 6100 and 9000 h. The results were compared with a cell in the initial state. Besides the LSCF anode, the SOECs were composed of a Ce 0.8Gd 0.2O 1.9 barrier layer between the anode and electrolyte, yttria-stabilized zirconia (YSZ) as electrolyte and Ni-YSZ as cathode (hydrogen electrode). Mössbauer spectra of the iron-containingmore » anode were acquired in order to determine the alteration of the iron oxidation state and its local environment during operation. Mössbauer spectroscopy yields indirect information about the degradation mechanism, especially in combination with SEM, TEM, and XRD. XRD and TEM revealed the appearance of Co 3O 4 during the SOEC operation and SEM analyses confirmed the formation of SrZrO 3 at the electrode/electrolyte interface. The spectral analysis confirmed the reduction of iron from Fe(IV) to Fe(III) in LSCF after long-term operation. The fraction of Fe(IV) in the electrode decreased with time and 18, 15, 13 and 11% were obtained for 0, 1774, 6100, and 9000 h of operation, respectively.« less

A Mössbauer spectral study of degradation in La 0.58Sr 0.4Fe 0.5Co 0.5O 3–x after long-term operation in solid oxide electrolysis cells

DOE PAGES

Mahmoud, Abdelfattah; Daroukh, Mahmoud Al; Lipinska-Chwalek, Marta; ...

2017-10-21

Here, degradation processes of oxygen electrodes in solid oxide electrolysis cells (SOECs) were studied by X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM) and Mössbauer spectroscopy. La 0.58Sr 0.4Fe 0.5Co 0.5O 3–x (LSCF) anodes (oxygen electrode) were analyzed after different long-term operations durations of 1774, 6100 and 9000 h. The results were compared with a cell in the initial state. Besides the LSCF anode, the SOECs were composed of a Ce 0.8Gd 0.2O 1.9 barrier layer between the anode and electrolyte, yttria-stabilized zirconia (YSZ) as electrolyte and Ni-YSZ as cathode (hydrogen electrode). Mössbauer spectra of the iron-containingmore » anode were acquired in order to determine the alteration of the iron oxidation state and its local environment during operation. Mössbauer spectroscopy yields indirect information about the degradation mechanism, especially in combination with SEM, TEM, and XRD. XRD and TEM revealed the appearance of Co 3O 4 during the SOEC operation and SEM analyses confirmed the formation of SrZrO 3 at the electrode/electrolyte interface. The spectral analysis confirmed the reduction of iron from Fe(IV) to Fe(III) in LSCF after long-term operation. The fraction of Fe(IV) in the electrode decreased with time and 18, 15, 13 and 11% were obtained for 0, 1774, 6100, and 9000 h of operation, respectively.« less

A High-Energy-Density Potassium Battery with a Polymer-Gel Electrolyte and a Polyaniline Cathode.

PubMed

Gao, Hongcai; Xue, Leigang; Xin, Sen; Goodenough, John B

2018-05-04

A safe, rechargeable potassium battery of high energy density and excellent cycling stability has been developed. The anion component of the electrolyte salt is inserted into a polyaniline cathode upon charging and extracted from it during discharging while the K + ion of the KPF 6 salt is plated/stripped on the potassium-metal anode. The use of a p-type polymer cathode increases the cell voltage. By replacing the organic-liquid electrolyte in a glass-fiber separator with a polymer-gel electrolyte of cross-linked poly(methyl methacrylate), a dendrite-free potassium anode can be plated/stripped, and the electrode/electrolyte interface is stabilized. The potassium anode wets the polymer, and the cross-linked architecture provides small pores of adjustable sizes to stabilize a solid-electrolyte interphase formed at the anode/electrolyte interface. This alternative electrolyte/cathode strategy offers a promising new approach to low-cost potassium batteries for the stationary storage of electric power. © 2018 Wiley-VCH Verlag GmbH & Co. KGaA, Weinheim.

Long lifetime hollow cathodes for 30-cm mercury ion thrusters

NASA Technical Reports Server (NTRS)

Mirtich, M. J.; Kerslake, W. R.

1976-01-01

An experimental investigation of hollow cathodes for 30-cm Hg bombardment thrusters was carried out. Both main and neutralizer cathode configurations were tested with both rolled foil inserts coated with low work function material and impregnated porous tungsten inserts. Temperature measurements of an impregnated insert at various positions in the cathode were made. These, along with the cathode thermal profile are presented. A theory for rolled foil and impregnated insert operation and lifetime in hollow cathodes is developed. Several endurance tests, as long as 18000 hours at emission currents of up to 12 amps were attained with no degradation in performance.

Construction of a biocathode using the multicopper oxidase from the hyperthermophilic archaeon, Pyrobaculum aerophilum: towards a long-life biobattery.

PubMed

Sakamoto, Hiroaki; Uchii, Toshiki; Yamaguchi, Kayo; Koto, Ayako; Takamura, Ei-Ichiro; Satomura, Takenori; Sakuraba, Haruhiko; Ohshima, Toshihisa; Suye, Shin-Ichiro

2015-07-01

The life of biobatteries remains an issue due to loss of enzyme activity over time. In this study, we sought to develop a biobattery with a long life using a hyperthermophilic enzyme. We hypothesized that use of such hyperthermophilic enzymes would allow for the biofuel cells to have a long battery life. Using pyrroloquinoline quinone-glucose dehydrogenase and the multicopper oxidase from Pyrobaculum aerophilum, we constructed an anode and cathode. The maximum output was 11 μW at 0.2 V, and the stability of the both electrode was maintained at 70 % after 14 days. The biofuel cells that use hyperthermophilic enzymes may prolong their life.

Prospects for spinel-stabilized, high-capacity lithium-ion battery cathodes

DOE Office of Scientific and Technical Information (OSTI.GOV)

Croy, Jason R.; Park, Joong Sun; Shin, Youngho

Herein we report early results on efforts to optimize the electrochemical performance of a cathode composed of a lithium- and manganese-rich “layered-layered-spinel” material for lithium-ion battery applications. Pre-pilot scale synthesis leads to improved particle properties compared with lab-scale efforts, resulting in high capacities (≳200 mAh/g) and good energy densities (>700 Wh/kg) in tests with lithium-ion cells. Subsequent surface modifications give further improvements in rate capabilities and high-voltage stability. These results bode well for advances in the performance of this class of lithium- and manganese-rich cathode materials.

Prospects for spinel-stabilized, high-capacity lithium-ion battery cathodes

DOE PAGES

Croy, Jason R.; Park, Joong Sun; Shin, Youngho; ...

2016-10-13

Herein we report early results on efforts to optimize the electrochemical performance of a cathode composed of a lithium- and manganese-rich “layered-layered-spinel” material for lithium-ion battery applications. Pre-pilot scale synthesis leads to improved particle properties compared with lab-scale efforts, resulting in high capacities (≳200 mAh/g) and good energy densities (>700 Wh/kg) in tests with lithium-ion cells. Subsequent surface modifications give further improvements in rate capabilities and high-voltage stability. These results bode well for advances in the performance of this class of lithium- and manganese-rich cathode materials.

In situ engineering of the electrode-electrolyte interface for stabilized overlithiated cathodes

DOE PAGES

Evans, Tyler; Piper, Daniela Molina; Sun, Huaxing; ...

2017-01-05

Here, the first-ever demonstration of stabilized Si/lithium-manganese-rich full cells, capable of retaining >90% energy over early cycling and >90% capacity over more than 750 cycles at the 1C rate (100% depth-of-discharge), is made through the utilization of a modified ionic liquid electrolyte capable of forming a favorable cathode-electrolyte interface.

Stability and predictors of change in salivary cortisol measures over six years: MESA.

PubMed

Wang, Xu; Sánchez, Brisa N; Golden, Sherita Hill; Shrager, Sandi; Kirschbaum, Clemens; Karlamangla, Arun S; Seeman, Teresa E; Roux, Ana V Diez

2014-11-01

A major challenge in characterizing features of the daily cortisol curve is variability in features over time. Few studies have examined the stability of daily features of the cortisol curve over long periods or the predictors of long term changes. Repeated salivary cortisol measures on 580 adults from the MESA Stress study were used to examine the stability of various features of the daily cortisol curve (wakeup value, the cortisol awakening response (CAR), the early and late decline slope and the area under the curve (AUC)), over short periods (several days) and long periods (approximately 6-years) and to investigate the association of demographic factors with the changes. Intraclass correlation coefficients (ICCs) were used to estimate the short and long term stability. Piecewise linear mixed models were used to assess factors associated with changes in features over time. For most features, short term stability (ICCs: 0.17-0.74) was higher than long term stability (ICCs: 0.05-0.42), and long term stability was highest when several days were averaged for each time point. The decline over the day showed the highest long term stability: when several days for each wave were averaged the stability of the daily decline slope across 6 years was similar (or higher) than the stability across short periods. AUC had high stability over short periods (ICCs: 0.65-0.74) but much lower stability across long periods (ICC: 0.05). All features of daily cortisol curve investigated changed significantly over the approximately 6 year follow-up period. The wakeup cortisol became higher; the CAR became smaller; both the early and late decline became flatter; and the AUC became larger. Hispanics experienced significantly larger increases in the wakeup value; and African-Americans and Hispanics showed less flattening over time of the early decline slope than Non-Hispanic Whites. Our findings have implications for characterization of features in studies linking cortisol to health outcomes. The presence of variability over time suggests opportunities for future investigation of the predictors of changes over time as well as the links between these changes and health outcomes. Copyright © 2014 Elsevier Ltd. All rights reserved.

Advanced Li-Ion Hybrid Supercapacitors Based on 3D Graphene-Foam Composites.

PubMed

Liu, Wenwen; Li, Jingde; Feng, Kun; Sy, Abel; Liu, Yangshuai; Lim, Lucas; Lui, Gregory; Tjandra, Ricky; Rasenthiram, Lathankan; Chiu, Gordon; Yu, Aiping

2016-10-05

Li-ion hybrid supercapacitors (LIHSs) have recently attracted increasing attention as a new and promising energy storage device. However, it is still a great challenge to construct novel LIHSs with high-performance due to the majority of battery-type anodes retaining the sluggish kinetics of Li-ion storage and most capacitor-type cathodes with low specific capacitance. To solve this problem, 3D graphene-wrapped MoO 3 nanobelt foam with the unique porous network structure has been designed and prepared as anode material, which delivers high capacity, improved rate performance, and enhanced cycle stability. First-principles calculation reveals that the combination of graphene dramatically reduces the diffusion energy barrier of Li + adsorbed on the surface of MoO 3 nanobelt, thus improving its electrochemical performance. Furthermore, 3D graphene-wrapped polyaniline nanotube foam derived carbon is employed as a new type of capacitor-type cathode, demonstrating high specific capacitance, good rate performance, and long cycle stability. Benefiting from these two graphene foam-enhanced materials, the constructed LIHSs show a wide operating voltage range (3.8 V), a long stable cycle life (90% capacity retention after 3000 cycles), a high energy density (128.3 Wh·kg -1 ), and a high power density (13.5 kW·kg -1 ). These encouraging performances indicate that the obtained LIHSs may have promising prospect as next-generation energy-storage devices.

Active water management at the cathode of a planar air-breathing polymer electrolyte membrane fuel cell using an electroosmotic pump

NASA Astrophysics Data System (ADS)

Fabian, T.; O'Hayre, R.; Litster, S.; Prinz, F. B.; Santiago, J. G.

In a typical air-breathing fuel cell design, ambient air is supplied to the cathode by natural convection and dry hydrogen is supplied to a dead-ended anode. While this design is simple and attractive for portable low-power applications, the difficulty in implementing effective and robust water management presents disadvantages. In particular, excessive flooding of the open-cathode during long-term operation can lead to a dramatic reduction of fuel cell power. To overcome this limitation, we report here on a novel air-breathing fuel cell water management design based on a hydrophilic and electrically conductive wick in conjunction with an electroosmotic (EO) pump that actively pumps water out of the wick. Transient experiments demonstrate the ability of the EO-pump to "resuscitate" the fuel cell from catastrophic flooding events, while longer term galvanostatic measurements suggest that the design can completely eliminate cathode flooding using less than 2% of fuel cell power, and lead to stable operation with higher net power performance than a control design without EO-pump. This demonstrates that active EO-pump water management, which has previously only been demonstrated in forced-convection fuel cell systems, can also be applied effectively to miniaturized (<5 W) air-breathing fuel cell systems.

A highly active hybrid catalyst modified (La0.60Sr0.40)0.95Co0.20Fe0.80O3-δ cathode for proton conducting solid oxide fuel cells

NASA Astrophysics Data System (ADS)

Lei, Libin; Tao, Zetian; Hong, Tao; Wang, Xiaoming; Chen, Fanglin

2018-06-01

The sluggish reaction kinetics in the cathode usually leads to considerable cathode polarization resistance, hindering the development of proton conducting solid oxide fuel cells (H-SOFCs) operated at intermediate temperatures (400-650 °C). To address this problem, for the first time, a novel hybrid catalyst consisting of PrNi0.5Mn0.5O3 and PrOx is impregnated in the (La0.60Sr0.40)0.95Co0.20Fe0.80O3-δ (LSCF) cathode of H-SOFCs, resulting in significant enhancement of the cathode reaction kinetics. Single cells with impregnated LSCF cathode and BaZr0.8Y0.2O3 (BZY) electrolyte yield a maximum power density (MPD) of 0.198 W cm-2 at 600 °C, more than doubled of that with blank LSCF cathode (0.083 W cm-2). ECR and EIS studies reveal that the hybrid catalyst can substantially accelerate the oxygen-ion transfer and oxygen dissociation-absorption processes in the cathode, resulting in significantly lower polarization resistance and higher MPD. In addition, the hybrid catalyst possesses good chemical and microstructural stability at 600 °C. Consequently, the single cells with impregnated LSCF cathode show excellent durability. This study shows that the impregnation of this novel hybrid catalyst in the cathode could be a promising approach to improve the performance and stability of H-SOFCs.

Few Atomic Layered Lithium Cathode Materials to Achieve Ultrahigh Rate Capability in Lithium-Ion Batteries.

PubMed

Tai, Zhixin; Subramaniyam, Chandrasekar M; Chou, Shu-Lei; Chen, Lingna; Liu, Hua-Kun; Dou, Shi-Xue

2017-09-01

The most promising cathode materials, including LiCoO 2 (layered), LiMn 2 O 4 (spinel), and LiFePO 4 (olivine), have been the focus of intense research to develop rechargeable lithium-ion batteries (LIBs) for portable electronic devices. Sluggish lithium diffusion, however, and unsatisfactory long-term cycling performance still limit the development of present LIBs for several applications, such as plug-in/hybrid electric vehicles. Motivated by the success of graphene and novel 2D materials with unique physical and chemical properties, herein, a simple shear-assisted mechanical exfoliation method to synthesize few-layered nanosheets of LiCoO 2 , LiMn 2 O 4 , and LiFePO 4 is used. Importantly, these as-prepared nanosheets with preferred orientations and optimized stable structures exhibit excellent C-rate capability and long-term cycling performance with much reduced volume expansion during cycling. In particular, the zero-strain insertion phenomenon could be achieved in 2-3 such layers of LiCoO 2 electrode materials, which could open up a new way to the further development of next-generation long-life and high-rate batteries. © 2017 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Construction of Hierarchical CNT/rGO-Supported MnMoO4 Nanosheets on Ni Foam for High-Performance Aqueous Hybrid Supercapacitors.

PubMed

Mu, Xuemei; Du, Jingwei; Zhang, Yaxiong; Liang, Zhilin; Wang, Huan; Huang, Baoyu; Zhou, Jinyuan; Pan, Xiaojun; Zhang, Zhenxing; Xie, Erqing

2017-10-18

Rationally designed conductive hierarchical nanostructures are highly desirable for supporting pseudocapacitive materials to achieve high-performance electrodes for supercapacitors. Herein, manganese molybdate nanosheets were hydrothermally grown with graphene oxide (GO) on three-dimensional nickel foam-supported carbon nanotube structures. Under the optimal graphene oxide concentration, the obtained carbon nanotubes/reduced graphene oxide/MnMoO 4 composites (CNT/rGO/MnMoO 4 ) as binder-free supercapacitor cathodes perform with a high specific capacitance of 2374.9 F g -1 at the scan rate of 2 mV s -1 and good long-term stability (97.1% of the initial specific capacitance can be maintained after 3000 charge/discharge cycles). The asymmetric device with CNT/rGO/MnMoO 4 as the cathode electrode and the carbon nanotubes/activated carbon on nickel foam (CNT-AC) as the anode electrode can deliver an energy density of 59.4 Wh kg -1 at the power density of 1367.9 W kg -1 . These superior performances can be attributed to the synergistic effects from each component of the composite electrodes: highly pseudocapacitive MnMoO 4 nanosheets and three-dimensional conductive Ni foam/CNTs/rGO networks. These results suggest that the fabricated asymmetric supercapacitor can be a promising candidate for energy storage devices.

Single-layer nano-carbon film, diamond film, and diamond/nano-carbon composite film field emission performance comparison

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wang, Xiaoping, E-mail: wxpchina64@aliyun.com, E-mail: wxpchina@sohu.com; Shanghai Key Laboratory of Modern Optical System, Shanghai 200093; Wang, Jinye

A series of single-layer nano-carbon (SNC) films, diamond films, and diamond/nano-carbon (D/NC) composite films have been prepared on the highly doped silicon substrate by using microwave plasma chemical vapor deposition techniques. The films were characterised by scanning electron microscopy, Raman spectroscopy, and field emission I-V measurements. The experimental results indicated that the field emission maximum current density of D/NC composite films is 11.8–17.8 times that of diamond films. And the field emission current density of D/NC composite films is 2.9–5 times that of SNC films at an electric field of 3.0 V/μm. At the same time, the D/NC composite film exhibitsmore » the advantage of improved reproducibility and long term stability (both of the nano-carbon film within the D/NC composite cathode and the SNC cathode were prepared under the same experimental conditions). And for the D/NC composite sample, a high current density of 10 mA/cm{sup 2} at an electric field of 3.0 V/μm was obtained. Diamond layer can effectively improve the field emission characteristics of nano-carbon film. The reason may be due to the diamond film acts as the electron acceleration layer.« less

[Stabilization and long-term effect of chromium contaminated soil].

PubMed

Wang, Jing; Luo, Qi-Shi; Zhang, Chang-Bo; Tan, Liang; Li, Xu

2013-10-01

Short-term (3 d and 28 d) and long-term (1 a) stabilization effects of Cr contaminated soil were investigated through nature curing, using four amendments including ferrous sulfide, ferrous sulfate, zero-valent iron and sodium dithionite. The results indicated that ferrous sulfide and zero-valent iron were not helpful for the stabilization of Cr(VI) when directly used because of their poor solubility and immobility. Ferrous sulfate could effectively and rapidly decrease total leaching Cr and Cr(VI) content. The stabilization effect was further promoted by the generation of iron hydroxides after long-term curing. Sodium dithionite also had positive effect on soil stabilization. Appropriate addition ratio of the two chemicals could help maintain the soil pH in range of 6-8.

Long-Term Stability of Oxide Nanowire Sensors via Heavily Doped Oxide Contact.

PubMed

Zeng, Hao; Takahashi, Tsunaki; Kanai, Masaki; Zhang, Guozhu; He, Yong; Nagashima, Kazuki; Yanagida, Takeshi

2017-12-22

Long-term stability of a chemical sensor is an essential quality for long-term collection of data related to exhaled breath, environmental air, and other sources in the Internet of things (IoT) era. Although an oxide nanowire sensor has shown great potential as a chemical sensor, the long-term stability of sensitivity has not been realized yet due to electrical degradation under harsh sensing conditions. Here, we report a rational concept to accomplish long-term electrical stability of metal oxide nanowire sensors via introduction of a heavily doped metal oxide contact layer. Antimony-doped SnO 2 (ATO) contacts on SnO 2 nanowires show much more stable and lower electrical contact resistance than conventional Ti contacts for high temperature (200 °C) conditions, which are required to operate chemical sensors. The stable and low contact resistance of ATO was confirmed for at least 1960 h under 200 °C in open air. This heavily doped oxide contact enables us to realize the long-term stability of SnO 2 nanowire sensors while maintaining the sensitivity for both NO 2 gas and light (photo) detections. The applicability of our method is confirmed for sensors on a flexible polyethylene naphthalate (PEN) substrate. Since the proposed fundamental concept can be applied to various oxide nanostructures, it will give a foundation for designing long-term stable oxide nanomaterial-based IoT sensors.

Effect of Si on DC arc plasma generation from Al-Cr and Al-Cr-Si cathodes used in oxygen

NASA Astrophysics Data System (ADS)

Zhirkov, I.; Landälv, L.; Göthelid, E.; Ahlgren, M.; Eklund, P.; Rosen, J.

2017-02-01

Al2O3 alloyed with Cr is an important material for the tooling industry. It can be synthesized from an arc discharge using Al-Cr cathodes in an oxygen atmosphere. Due to formation of Al-rich oxide islands on the cathode surface, the arc process stability is highly sensitive to oxygen pressure. For improved stability, the use of Al0.70Cr0.25Si0.05 cathodes has previously been suggested, where Si may reduce island formation. Here, we have investigated the effect of Si by comparing plasma generation and thin film deposition from Al0.7Cr0.3 and Al0.7Cr0.25Si0.05 cathodes. Plasma ion composition, ion energies, ion charge states, neutral species, droplet formation, and film composition have been characterized at different O2 flow rates for arc currents of 60 and 90 A. Si and related compounds are detected in plasma ions and in plasma neutrals. Scanning electron microscopy and energy dispersive X-ray analysis show that the cathode composition and the film composition are the same, with Si present in droplets as well. The effect of Si on the process stability, ion energies, and ion charge states is found to be negligible compared to that of the arc current. The latter is identified as the most relevant parameter for tuning the properties of the reactive discharge. The present work increases the fundamental understanding of plasma generation in a reactive atmosphere, and provides input for the choice of cathode composition and process parameters in reactive DC arc synthesis.

Polyethylenimine Interfacial Layers in Inverted Organic Photovoltaic Devices: Effects of Ethoxylation and Molecular Weight on Efficiency and Temporal Stability.

PubMed

Courtright, Brett A E; Jenekhe, Samson A

2015-12-02

We report a comparative study of polyethylenimine (PEI) and ethoxylated-polyethylenimine (PEIE) cathode buffer layers in high performance inverted organic photovoltaic devices. The work function of the indium-tin oxide (ITO)/zinc oxide (ZnO) cathode was reduced substantially (Δφ = 0.73-1.09 eV) as the molecular weight of PEI was varied from 800 g mol(-1) to 750 000 g mol(-1) compared with the observed much smaller reduction when using a PEIE thin film (Δφ = 0.56 eV). The reference inverted polymer solar cells based on the small band gap polymer PBDTT-FTTE (ITO/ZnO/PBDTT-FTTE:PC70BM/MoO3/Ag), without a cathode buffer layer, had an average power conversion efficiency (PCE) of 6.06 ± 0.22%. Incorporation of a PEIE cathode buffer layer in the same PBDTT-FTTE:PC70BM blend devices gave an enhanced performance with a PCE of 7.37 ± 0.53%. In contrast, an even greater photovoltaic efficiency with a PCE of 8.22 ± 0.10% was obtained in similar PBDTT-FTTE:PC70BM blend solar cells containing a PEI cathode buffer layer. The temporal stability of the inverted polymer solar cells was found to increase with increasing molecular weight of the cathode buffer layer. The results show that PEI is superior to PEIE as a cathode buffer layer in high performance organic photovoltaic devices and that the highest molecular weight PEI interlayer provides the highest temporal stability.

An ionization gauge for ultrahigh vacuum measurement based on a carbon nanotube cathode

NASA Astrophysics Data System (ADS)

Zhang, Huzhong; Cheng, Yongjun; Sun, Jian; Wang, Yongjun; Xi, Zhenhua; Dong, Meng; Li, Detian

2017-10-01

This work reports on the complete design and the properties of an ionization gauge based on a carbon nanotube cathode, which can measure ultrahigh vacuum without thermal effects. The gauge is composed of a pressure sensor and an electronic controller. This pressure sensor is constructed based on a hot-cathode ionization gauge, where the traditional hot filament is replaced by an electron source prepared with multi-wall nanotubes. Besides, an electronic controller was developed for bias voltage supply, low current detection, and pressure indication. The gauge was calibrated in the pressure range of 10-8 to 10-4 Pa in a XHV/UHV calibration apparatus. The gauge shows good linear characteristics in different gases. The calibrated sensitivity is 0.035 Pa-1 in N2, and the standard deviation of the sensitivity is about 1.1%. In addition, the stability of the sensitivity was learned in a long period. The standard deviation of the sensitivity factor "S" during one year is 2.0% for Ar and 1.6% for N2.

Mixed cellulose ester filter as a separator for air-diffusion cathode microbial fuel cells.

PubMed

Wang, Zejie; Lim, Bongsu

2017-04-01

Separator is important to prevent bio-contamination of the catalyst layer of air-diffusion cathode microbial fuel cells (MFCs). Mixed cellulose ester filter (MCEF) was examined as a separator for an air-cathode MFC in the present study. The MCEF-MFC produced a maximum power density of 780.7 ± 18.7 mW/m 2 , which was comparable to 770.9 ± 35.9 mW/m 2 of MFC with Nafion membrane (NFM) as a separator. Long-term examination demonstrated a more stable performance of the MCEF-MFC than NFM-MFC. After 25 cycles, the maximum voltage of the MCEF-MFC decreased by only 1.3% from 425.1 ± 4.3 mV (initial 5 cycles) to 419.5 ± 2.3 mV (last 5 cycles). However, it was decreased by 9.1% from 424.8 ± 5.7 to 386 ± 2.5 mV for the NFM-MFC. The coulombic efficiency (CE) of the MCEF-MFC did not change (from 3.11 ± 0.09% to 3.13 ± 0.02%), while it decreased by 9.12% from 3.18 ± 0.04% to 2.89 ± 0.02% for the NFM-MFC. The MCEF separator was with less biofouling than the NFM separator over 60 days' operation, which might be the reason for the more table long-term performance of the MCEF-MFC. The results demonstrated that MCEF was feasible as a separator to set up good-performing and cost-effective air-diffusion cathode MFC.

Long lifetime hollow cathodes for 30-cm mercury ion thrusters

NASA Technical Reports Server (NTRS)

Mirtich, M. J.; Kerslake, W. R.

1976-01-01

An experimental investigation of hollow cathodes for 30-cm Hg bombardment thrusters was carried out. Both main and neutralizer cathode configurations were tested with both rolled foil inserts coated with low work function material and impregnated porous tungsten inserts. Temperature measurements of an impregnated insert at various positions in the cathode were made. These, along with the cathode thermal profile are presented. A theory for rolled foil and impregnated insert operation and lifetime in hollow cathodes is developed. Several endurance tests, as long as 18,000 hours at emission currents of up to 12 amps were attained with no degradation in performance.

Nitrogen, Fluorine, and Boron Ternary Doped Carbon Fibers as Cathode Electrocatalysts for Zinc-Air Batteries.

PubMed

Wang, Lei; Wang, Yueqing; Wu, Mingguang; Wei, Zengxi; Cui, Chunyu; Mao, Minglei; Zhang, Jintao; Han, Xiaopeng; Liu, Quanhui; Ma, Jianmin

2018-05-01

Zinc-air batteries with high-density energy are promising energy storage devices for the next generation of energy storage technologies. However, the battery performance is highly dependent on the efficiency of oxygen electrocatalyst in the air electrode. Herein, the N, F, and B ternary doped carbon fibers (TD-CFs) are prepared and exhibited higher catalytic properties via the efficient 4e - transfer mechanism for oxygen reduction in comparison with the single nitrogen doped CFs. More importantly, the primary and rechargeable Zn-air batteries using TD-CFs as air-cathode catalysts are constructed. When compared to batteries with Pt/C + RuO 2 and Vulcan XC-72 carbon black catalysts, the TD-CFs catalyzed batteries exhibit remarkable battery reversibility and stability over long charging/discharging cycles. © 2018 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Enhanced ambient stability of efficient perovskite solar cells by employing a modified fullerene cathode interlayer

DOE PAGES

Zhu, Zonglong; Chueh, Chu -Chen; Lin, Francis; ...

2016-03-22

A novel fullerene cathode interlayer is employed to facilitate the fabrication of stable and efficient perovskite solar cells. Here, this modified fullerene surfactant significantly increases air stability of the derived devices due to its hydrophobic characteristics to enable 80% of the initial PCE to be retained after being exposed in ambient condition with 20% relative humidity for 14 days.

Evaluation of the Long-Term Stability and Temperature Coefficient of Dew-Point Hygrometers

NASA Astrophysics Data System (ADS)

Benyon, R.; Vicente, T.; Hernández, P.; De Rivas, L.; Conde, F.

2012-09-01

The continuous quest for improved specifications of optical dew-point hygrometers has raised customer expectations on the performance of these devices. In the absence of a long calibration history, users with a limited prior experience in the measurement of humidity, place reliance on manufacturer specifications to estimate long-term stability. While this might be reasonable in the case of measurement of electrical quantities, in humidity it can lead to optimistic estimations of uncertainty. This article reports a study of the long-term stability of some hygrometers and the analysis of their performance as monitored through regular calibration. The results of the investigations provide some typical, realistic uncertainties associated with the long-term stability of instruments used in calibration and testing laboratories. Together, these uncertainties can help in establishing initial contributions in uncertainty budgets, as well as in setting the minimum calibration requirements, based on the evaluation of dominant influence quantities.

Free-Standing Porous Carbon Nanofiber/Carbon Nanotube Film as Sulfur Immobilizer with High Areal Capacity for Lithium-Sulfur Battery.

PubMed

Zhang, Ye-Zheng; Zhang, Ze; Liu, Sheng; Li, Guo-Ran; Gao, Xue-Ping

2018-03-14

Low sulfur utilization and poor cycle life of the sulfur cathode with high sulfur loadings remain a great challenge for lithium-sulfur (Li-S) battery. Herein, the free-standing carbon film consisting of porous carbon nanofibers (PCNFs) and carbon nanotubes (CNTs) is successfully fabricated by the electrospinning technology. The PCNF/CNT film with three-dimensional and interconnected structure is promising for the uniformity of the high-loading sulfur, good penetration of the electrolyte, and reliable accommodation of volumetric expansion of the sulfur cathode. In addition, the abundant N/O-doped elements in PCNF/CNT film are helpful to chemically trap soluble polysulfides in the charge-discharge processes. Consequently, the obtained monolayer S/PCNF/CNT film as the cathode shows high specific capacity, excellent cycle stability, and rate stability with the sulfur loading of 3.9 mg cm -2 . Moreover, the high areal capacity of 13.5 mA h cm -2 is obtained for the cathode by stacking three S/PCNF/CNT layers with the high sulfur loading of 12 mg cm -2 . The stacking-layered cathode with high sulfur loading provides excellent cycle stability, which is beneficial to fabricate high-energy-density Li-S battery in future.

Nb and Pd co-doped La0.57Sr0.38Co0.19Fe0.665Nb0.095Pd0.05O3-δ as a stable, high performance electrode for barrier-layer-free Y2O3-ZrO2 electrolyte of solid oxide fuel cells

NASA Astrophysics Data System (ADS)

Chen, Kongfa; He, Shuai; Li, Na; Cheng, Yi; Ai, Na; Chen, Minle; Rickard, William D. A.; Zhang, Teng; Jiang, San Ping

2018-02-01

La0.6Sr0.2Co0.2Fe0.8O3-δ (LSCF) is the most intensively investigated high performance cathode for intermediate temperature solid oxide fuel cells (IT-SOFCs), but strontium segregation and migration at the electrode/electrolyte interface is a critical issue limiting the electrocatalytic activity and stability of LSCF based cathodes. Herein, we report a Nb and Pd co-doped LSCF (La0.57Sr0.38Co0.19Fe0.665Nb0.095Pd0.05O3-δ, LSCFNPd) perovskite as stable and active cathode on a barrier-layer-free anode-supported yttria-stabilized zirconia (YSZ) electrolyte cell using direct assembly method without pre-sintering at high temperatures. The cell exhibits a peak power density of 1.3 W cm-2 at 750 °C and excellent stability with no degradation during polarization at 500 mA cm-2 and 750 °C for 175 h. Microscopic and spectroscopic analysis show that the electrochemical polarization promotes the formation of electrode/electrolyte interface in operando and exsolution of Pd/PdO nanoparticles. The Nb doping in the B-site of LSCF significantly reduces the Sr surface segregation, enhancing the stability of the cathode, while the exsoluted Pd/PdO nanoparticles increases the electrocatalytic activity for the oxygen reduction reaction. The present study opens up a new route for the development of cobaltite-based perovskite cathodes with high activity and stability for barrier-layer-free YSZ electrolyte based IT-SOFCs.

Theory, Investigation and Stability of Cathode Electrocatalytic Activity

DOE Office of Scientific and Technical Information (OSTI.GOV)

Ding, Dong; Liu, Mingfei; Lai, Samson

2012-09-30

The main objective of this project is to systematically characterize the surface composition, morphology, and electro-catalytic properties of catalysts coated on LSCF, aiming to establish the scientific basis for rational design of high-performance cathodes by combining a porous backbone (such as LSCF) with a thin catalyst coating. The understanding gained will help us to optimize the composition and morphology of the catalyst layer and microstructure of the LSCF backbone for better performance. More specifically, the technical objectives include: (1) to characterize the surface composition, morphology, and electro-catalytic properties of catalysts coated on LSCF; (2) to characterize the microscopic details andmore » stability of the LSCF-catalyst (e.g., LSM) interfaces; (3) to establish the scientific basis for rational design of high-performance cathodes by combining a porous backbone (such as LSCF) with a thin catalyst coating; and (4) to demonstrate that the performance and stability of porous LSCF cathodes can be enhanced by the application of a thin-film coating of LSM through a solution infiltration process in small homemade button cells and in commercially available cells of larger dimension. We have successfully developed dense, conformal LSM films with desired structure, composition, morphology, and thickness on the LSCF surfaces by two different infiltration processes: a non-aqueous and a water-based sol-gel process. It is demonstrated that the activity and stability of LSCF cathodes can be improved by the introduction of a thin-film LSM coating through an infiltration process. Surface and interface of the LSM-coated LSCF cathode were systematically characterized using advanced microscopy and spectroscopy techniques. TEM observation suggests that a layer of La and Sr oxide was formed on LSCF surfaces after annealing. With LSM infiltration, in contrast, we no longer observe such La/Sr oxide layer on the LSM-coated LSCF samples after annealing under similar conditions. This was also confirmed by x-ray analyses. For example, soft x-ray XANES data reveal that Co cations displace the Mn cations as being more favored to be reduced. Variations in the Sr-O in the annealed LSCF Fourier-transformed (FT) EXAFS suggest that some Sr segregation is occurring, but is not present in the annealed LSM-infiltrated LSCF cathode materials. Further, a surface enhanced Raman technique was also developed into to probe and map LSM and LSCF phase on underlying YSZ substrate, enabling us to capture important chemical information of cathode surfaces under practical operating conditions. Electrochemical models for the design of test cells and understanding of mechanism have been developed for the exploration of fundamental properties of electrode materials. Novel catalyst coatings through particle depositions (SDC, SSC, and LCC) or continuous thin films (PSM and PSCM) were successfully developed to improve the activity and stability of LSCF cathodes. Finally, we have demonstrated enhanced activity and stability of LSCF cathodes over longer periods of time in homemade and commercially available cells by an optimized LSM infiltration process. Microstructure examination of the tested cells did not show obvious differences between blank and infiltrated cells, suggesting that the infiltrated LSM may form a coherent film on the LSCF cathodes. There was no significant change in the morphology or microstructure of the LSCF cathode due to the structural similarity of LSCF and LSM. Raman analysis of the tested cells indicated small peaks emerging on the blank cells that correspond to trace amounts of secondary phase formation during operation (e.g., CoO{sub x}). The formation of this secondary phase might be attributed to performance degradation. In contrast, there was no such secondary phase observed in the LSM infiltrated cells, indicating that the LSM modification staved off secondary phase formation and thus improved the stability.« less

Structural Transformations in High-Capacity Li 2 Cu 0.5 Ni 0.5 O 2 Cathodes

DOE Office of Scientific and Technical Information (OSTI.GOV)

Ruther, Rose E.; Samuthira Pandian, Amaresh; Yan, Pengfei

2017-03-21

Cathode materials that can cycle > 1 Li+ per transition metal are of substantial interest to increase the overall energy density of lithium-ion batteries. Li2Cu0.5Ni0.5O2 has a very high theoretical capacity of ~ 500 mAh/g assuming both Li+ are cycled reversibly. The Cu2+/3+ and Ni2+/3+/4+ redox couples are also at high voltage, which could further boost the energy density of this system. Despite such promise, Li2Cu0.5Ni0.5O2 undergoes irreversible phase changes during charge (delithiation) that result in large first-cycle irreversible loss and poor long-term cycling stability. Oxygen is evolved before the Cu2+/3+ or Ni3+/4+ transitions are accessed. In this contribution, XRD,more » TEM, and TXM-XANES are used to follow the chemical and structural changes that occur in Li2Cu0.5Ni0.5O2 during electrochemical cycling. Li2Cu0.5Ni0.5O2 is a solid solution of orthorhombic Li2CuO2 and Li2NiO2, but the structural changes more closely mimic the Li2NiO2 endmember. Li2Cu0.5Ni0.5O2 loses long-range order during charge, but TEM analysis provides clear evidence for particle exfoliation and the transformation from orthorhombic to a partially layered structure. Linear combination fitting and principal component analysis of TXM-XANES are used to map the different phases that emerge during cycling ex situ and in situ. Significant changes in the XANES at the Cu and Ni K-edges correlate with the onset of oxygen evolution.« less

Annual Summary Report on Thermionic Cathode Project.

DTIC Science & Technology

1986-01-09

Voltage Operation The electron gun cathode is driven negative by a high voltageRadiation pulse modulator in the circuit of Figure 3-1. Typical current...tungsten filament. The bombardment heating system is stabilized by a feed- back control circuit . The power required to heat tne cathode is 315 W bom...project. The primary purpose of the first phase was to develop the bombardment heating circuit used to heat the LaB 6 cathode, and to test the beam

Self aligning electron beam gun having enhanced thermal and mechanical stability

DOEpatents

Scarpetti, Jr., Raymond D.; Parkison, Clarence D.; Switzer, Vernon A.; Lee, Young J.; Sawyer, William C.

1995-01-01

A compact, high power electron gun having enhanced thermal and mechanical stability which incorporates a mechanically coupled, self aligning structure for the anode and cathode. The enhanced stability, and reduced need for realignment of the cathode to the anode and downstream optics during operation are achieved by use of a common support structure for the cathode and anode which requires no adjustment screws or spacers. The electron gun of the present invention also incorporates a modular design for the cathode, in which the electron emitter, its support structure, and the hardware required to attach the emitter assembly to the rest of the gun are a single element. This modular design makes replacement of the emitter simpler and requires no realignment after a new emitter has been installed. Compactness and a reduction in the possibility of high voltage breakdown are achieved by shielding the "triple point" where the electrode, insulator, and vacuum meet. The use of electric discharge machining (EDM) for fabricating the emitter allows for the accurate machining of the emitter into intricate shapes without encountering the normal stresses developed by standard emitter fabrication techniques.

A highly active hybrid catalyst modified (La 0.60Sr 0.40) 0.95Co 0.20Fe 0.80O 3-δ cathode for proton conducting solid oxide fuel cells

DOE Office of Scientific and Technical Information (OSTI.GOV)

Lei, Libin; Tao, Zetian; Hong, Tao

The sluggish reaction kinetics in the cathode usually leads to considerable cathode polarization resistance, hindering the development of proton conducting solid oxide fuel cells (H-SOFCs) operated at intermediate temperatures (400–650 °C). In this paper, to address this problem, for the first time, a novel hybrid catalyst consisting of PrNi 0.5Mn 0.5O 3 and PrOx is impregnated in the (La 0.60Sr 0.40) 0.95Co 0.20Fe 0.80O 3-δ (LSCF) cathode of H-SOFCs, resulting in significant enhancement of the cathode reaction kinetics. Single cells with impregnated LSCF cathode and BaZr 0.8Y 0.2O 3 (BZY) electrolyte yield a maximum power density (MPD) of 0.198 Wmore » cm -2 at 600 °C, more than doubled of that with blank LSCF cathode (0.083 W cm -2). ECR and EIS studies reveal that the hybrid catalyst can substantially accelerate the oxygen-ion transfer and oxygen dissociation-absorption processes in the cathode, resulting in significantly lower polarization resistance and higher MPD. In addition, the hybrid catalyst possesses good chemical and microstructural stability at 600 °C. Consequently, the single cells with impregnated LSCF cathode show excellent durability. Finally, this study shows that the impregnation of this novel hybrid catalyst in the cathode could be a promising approach to improve the performance and stability of H-SOFCs.« less

A highly active hybrid catalyst modified (La 0.60Sr 0.40) 0.95Co 0.20Fe 0.80O 3-δ cathode for proton conducting solid oxide fuel cells

DOE PAGES

Lei, Libin; Tao, Zetian; Hong, Tao; ...

2018-04-06

The sluggish reaction kinetics in the cathode usually leads to considerable cathode polarization resistance, hindering the development of proton conducting solid oxide fuel cells (H-SOFCs) operated at intermediate temperatures (400–650 °C). In this paper, to address this problem, for the first time, a novel hybrid catalyst consisting of PrNi 0.5Mn 0.5O 3 and PrOx is impregnated in the (La 0.60Sr 0.40) 0.95Co 0.20Fe 0.80O 3-δ (LSCF) cathode of H-SOFCs, resulting in significant enhancement of the cathode reaction kinetics. Single cells with impregnated LSCF cathode and BaZr 0.8Y 0.2O 3 (BZY) electrolyte yield a maximum power density (MPD) of 0.198 Wmore » cm -2 at 600 °C, more than doubled of that with blank LSCF cathode (0.083 W cm -2). ECR and EIS studies reveal that the hybrid catalyst can substantially accelerate the oxygen-ion transfer and oxygen dissociation-absorption processes in the cathode, resulting in significantly lower polarization resistance and higher MPD. In addition, the hybrid catalyst possesses good chemical and microstructural stability at 600 °C. Consequently, the single cells with impregnated LSCF cathode show excellent durability. Finally, this study shows that the impregnation of this novel hybrid catalyst in the cathode could be a promising approach to improve the performance and stability of H-SOFCs.« less

The thermomechanical stability of micro-solid oxide fuel cells fabricated on anodized aluminum oxide membranes

NASA Astrophysics Data System (ADS)

Kwon, Chang-Woo; Lee, Jae-Il; Kim, Ki-Bum; Lee, Hae-Weon; Lee, Jong-Ho; Son, Ji-Won

2012-07-01

The thermomechanical stability of micro-solid oxide fuel cells (micro-SOFCs) fabricated on an anodized aluminum oxide (AAO) membrane template is investigated. The full structure consists of the following layers: AAO membrane (600 nm)/Pt anode/YSZ electrolyte (900 nm)/porous Pt cathode. The utilization of a 600-nm-thick AAO membrane significantly improves the thermomechanical stability due to its well-known honeycomb-shaped nanopore structure. Moreover, the Pt anode layer deposited in between the AAO membrane and the YSZ electrolyte preserves its integrity in terms of maintaining the triple-phase boundary (TPB) and electrical conductivity during high-temperature operation. Both of these results guarantee thermomechanical stability of the micro-SOFC and extend the cell lifetime, which is one of the most critical issues in the fabrication of freestanding membrane-type micro-SOFCs.

Carbon-Stabilized Interlayer-Expanded Few-Layer MoSe2 Nanosheets for Sodium Ion Batteries with Enhanced Rate Capability and Cycling Performance.

PubMed

Tang, Yongchao; Zhao, Zongbin; Wang, Yuwei; Dong, Yanfeng; Liu, Yang; Wang, Xuzhen; Qiu, Jieshan

2016-11-30

Sodium ion batteries (SIBs) have been considered as a promising alternative to lithium ion batteries, owing to the abundant reserve and low-cost accessibility of the sodium source. To date, the pursuit of high-performance anode materials remains a great challenge for the SIBs. In this work, carbon-stabilized interlayer-expanded few-layer MoSe 2 nanosheets (MoSe 2 @C) have been fabricated by an oleic acid (OA) functionalized synthesis-polydopamine (PDA) stabilization-carbonization strategy, and their structural, morphological, and electrochemical properties have been carefully characterized and compared with the carbon-free MoSe 2 . When evaluated as anode for sodium ion half batteries, the MoSe 2 @C exhibits a remarkably enhanced rate capability of 367 mA h g -1 at 5 A g -1 , a high reversible discharge capacity of 445 mA h g -1 at 1 A g -1 , and a long-term cycling stability over 100 cycles. To further explore the potential applications, the MoSe 2 @C is assembled into sodium ion full batteries with Na 3 V 2 (PO 4 ) 3 (NVP) as cathode materials, showing an impressively high reversible capacity of 421 mA h g -1 at 0.2 A g -1 after 100 cycles. Such results are primarily attributed to the unique carbon-stabilized interlayer-expanded few-layer MoSe 2 nanosheets structure, which facilitates the permeation of electrolyte into the inner of MoSe 2 nanosheets, promoting charge transfer efficiency among MoSe 2 nanosheets, and accommodating the volume change from discharge-charge cycling.

Ferrocene-Promoted Long-Cycle Lithium-Sulfur Batteries.

PubMed

Mi, Yingying; Liu, Wen; Yang, Ke R; Jiang, Jianbing; Fan, Qi; Weng, Zhe; Zhong, Yiren; Wu, Zishan; Brudvig, Gary W; Batista, Victor S; Zhou, Henghui; Wang, Hailiang

2016-11-14

Confining lithium polysulfide intermediates is one of the most effective ways to alleviate the capacity fade of sulfur-cathode materials in lithium-sulfur (Li-S) batteries. To develop long-cycle Li-S batteries, there is an urgent need for material structures with effective polysulfide binding capability and well-defined surface sites; thereby improving cycling stability and allowing study of molecular-level interactions. This challenge was addressed by introducing an organometallic molecular compound, ferrocene, as a new polysulfide-confining agent. With ferrocene molecules covalently anchored on graphene oxide, sulfur electrode materials with capacity decay as low as 0.014 % per cycle were realized, among the best of cycling stabilities reported to date. With combined spectroscopic studies and theoretical calculations, it was determined that effective polysulfide binding originates from favorable cation-π interactions between Li + of lithium polysulfides and the negatively charged cyclopentadienyl ligands of ferrocene. © 2016 Wiley-VCH Verlag GmbH & Co. KGaA, Weinheim.

Synergistic Effect between LiNi0.5Co0.2Mn0.3O2 and LiFe0.15Mn0.85PO4/C on Rate and Thermal Performance for Lithium Ion Batteries.

PubMed

Sun, Guiyan; Lai, Shaobo; Kong, Xiangbang; Chen, Zhiqiang; Li, Kun; Zhou, Rong; Wang, Jing; Zhao, Jinbao

2018-05-16

A blend cathode has been prepared by mixing both LiNi 0.5 Co 0.2 Mn 0.3 O 2 (NCM523) of high energy density and high specific capacity and LiFe 0.15 Mn 0.85 PO 4 /C (LFMP/C) of excellent thermal stability via a low-speed ball-milling method. The lithium ion batteries using the blend cathode with LFMP/C of optimum percent exhibit better capacity retention after 100 cycles than those using only single NCM523 or LFMP/C. Both theoretical simulation and experimental rate performances demonstrate that the electrochemical property of blend cathode materials is predictable and economical. In addition, the thermal behaviors of blend cathodes are studied by using differential scanning calorimetry analysis. The thermal stability of blend cathode materials behaves better than that of the bare NCM523 accompanied with an electrolyte. It is found that the outstanding rate and thermal performance of the blend cathode is due to the prominent synergistic effect between NCM523 and LFMP/C, and 10% LFMP/C in the blend cathode materials is the most adaptable as considering both electrochemical and thermal properties simultaneously.

Understanding the effect of an in situ generated and integrated spinel phase on a layered Li-rich cathode material using a non-stoichiometric strategy.

PubMed

Zhang, Jicheng; Gao, Rui; Sun, Limei; Li, Zhengyao; Zhang, Heng; Hu, Zhongbo; Liu, Xiangfeng

2016-09-14

Recently, spinel-layered integrated Li-rich cathode materials have attracted great interest due to the large enhancement of their electrochemical performances. However, the modification mechanism and the effect of the integrated spinel phase on Li-rich layered cathode materials are still not very clear. Herein, we have successfully synthesized the spinel-layered integrated Li-rich cathode material using a facile non-stoichiometric strategy (NS-LNCMO). The rate capability (84 mA h g -1 vs. 28 mA h g -1 , 10 C), cycling stability (92.4% vs. 80.5%, 0.2 C), low temperature electrochemical capability (96.5 mA h g -1 vs. 59 mA h g -1 , -20 °C), initial coulomb efficiency (92% vs. 79%) and voltage fading (2.77 V vs. 3.02 V, 200 cycles@1 C) of spinel-layered integrated Li-rich cathode materials have been significantly improved compared with a pure Li-rich phase cathode. Some new insights into the effect of the integrated spinel phase on a layered Li-rich cathode have been proposed through a comparison of the structure evolution of the integrated and Li-rich only materials before and after cycling. The Li-ion diffusion coefficient of NS-LNCMO has been enlarged by about 3 times and almost does not change even after 100 cycles indicating an enhanced structure stability. The integration of the spinel phase not only enhances the structure stability of the layered Li-rich phase during charging-discharging but also expands the interslab spacing of the Li-ion diffusion layer, and elongates TM-O covalent bond lengths, which lowers the activation barrier of Li + -transportation, and alleviates the structure strain during the cycling procedure.

Application of vitreous and graphitic large-area carbon surfaces as field-emission cathodes

NASA Astrophysics Data System (ADS)

Hunt, Charles E.; Wang, Yu

2005-09-01

Numerous carbon bulk or thin-film materials have been used as field-emission cathodes. Most of these can be made into large-area and high-current field-emission cathodes without the use of complex IC fabrication techniques. Some of these exhibit low-extraction field, low work-function, high ruggedness, chemical stability, uniform emission, and low-cost manufacturability. A comparison of all of these materials is presented. Two viable cathode materials, reticulated vitreous carbon (RVC) and graphite paste are examined here and compared.

Long-term stability of diurnal salivary cortisol and alpha-amylase secretion patterns.

PubMed

Skoluda, Nadine; La Marca, Roberto; Gollwitzer, Mario; Müller, Andreas; Limm, Heribert; Marten-Mittag, Birgitt; Gündel, Harald; Angerer, Peter; Nater, Urs M

2017-06-01

This study aimed to investigate long-term stability and variability of diurnal cortisol and alpha-amylase patterns. Diurnal cortisol and alpha-amylase secretion patterns were assessed on a single workday with three waves of measurement across a total time period of 24months in 189 participants. Separate hierarchical linear models were analyzed, with and without a number of potential predictor variables (age, BMI, smoking, chronic stress, stress reactivity). While low long-term stability was found in diurnal cortisol, the stability of diurnal alpha-amylase was moderate across the time period of 24months. Several predictor variables had a positive impact on diurnal cortisol and alpha-amylase secretion patterns averaged across waves. Our findings underpin the notion that long-term stability is not necessarily warranted in longitudinal studies. It is important to choose an appropriate study design when attempting to disentangle clinically and biologically relevant changes from naturally occurring variations in diurnal cortisol and alpha-amylase. Copyright © 2017 Elsevier Inc. All rights reserved.

Cathodic electrochemical activation of Co3O4 nanoarrays: a smart strategy to significantly boost the hydrogen evolution activity.

PubMed

Yang, Li; Zhou, Huang; Qin, Xin; Guo, Xiaodong; Cui, Guanwei; Asiri, Abdullah M; Sun, Xuping

2018-02-22

Co(hydro)oxides show unsatisfactory catalytic activity for the hydrogen evolution reaction (HER) in alkaline media, and it is thus highly desirable but still remains a challenge to design and develop Co(hydro)oxide derived materials as superb hydrogen-evolving catalysts using a facile, rapid and less energy-intensive method. Here, we propose a cathodic electrochemical activation strategy toward greatly boosted HER activity of a Co 3 O 4 nanoarray via room-temperature cathodic polarization in sodium hypophosphite solution. After activation, the overpotential significantly decreases from 260 to 73 mV to drive a geometrical catalytic current density of 10 mA cm -2 in 1.0 M KOH. Notably, this activated electrode also shows strong long-term electrochemical durability with the retention of its catalytic activity at 100 mA cm -2 for at least 40 h.

Some Thoughts on Stability in Nonlinear Periodic Focusing Systems

DOE R&D Accomplishments Database

McMillan, E. M.

1967-09-05

A brief discussion is given of the long-term stability of particle motions through periodic focusing structures containing lumped nonlinear elements. A method is presented whereby one can specify the nonlinear elements in such a way as to generate a variety of structures in which the motion has long-term stability.

Long-term stability of sodium caseinate-stabilized nanoemulsions.

PubMed

Yerramilli, Manispuritha; Ghosh, Supratim

2017-01-01

Oil-in-water (5 wt%) nanoemulsions were prepared with different concentration (2.5-10 wt%) of sodium caseinate as a sole emulsifier and their long-term storage stability was investigated for 6 months. Previous studies associated with sodium caseinate looked only into nanoemulsion formation; hence the challenges with long-term stability were not addressed. All nanoemulsions displayed an average droplet size <200 nm, which remained unchanged over 6 months. However, all of them displayed rapid creaming due to unabsorbed protein induced depletion flocculation, whose extent increased with protein concentration, although the cream layer formed was weak and re-dispersible upon gentle mixing. Microstructural analysis of the cream layer showed compaction of flocculated nanodroplet network with time leaving the aqueous phase out. Calculation of depletion interaction energy showed an increase in inter-droplet attraction with protein concentration and decrease with a reduction in droplet size, making the nanoemulsions more resistant to flocculation than conventional emulsions. This work aids in understanding the dependence of protein concentration on long-term stability of sodium caseinate-stabilized nanoemulsions.

Enhanced electrochromic and energy storage performance in mesoporous WO3 film and its application in a bi-functional smart window.

PubMed

Wang, Wei-Qi; Wang, Xiu-Li; Xia, Xin-Hui; Yao, Zhu-Jun; Zhong, Yu; Tu, Jiang-Ping

2018-05-03

Construction of multifunctional photoelectrochemical energy devices is of great importance to energy saving. In this study, we have successfully prepared a mesoporous WO3 film on FTO glass via a facile dip-coating sol-gel method; the designed mesoporous WO3 film exhibited advantages including high transparency, good adhesion and high porosity. Also, multifunctional integrated energy storage and optical modulation ability are simultaneously achieved by the mesoporous WO3 film. Impressively, the mesoporous WO3 film exhibits a noticeable electrochromic energy storage performance with a large optical modulation up to 75.6% at 633 nm, accompanied by energy storage with a specific capacity of 75.3 mA h g-1. Furthermore, a full electrochromic energy storage window assembled with the mesoporous WO3 anode and PANI nanoparticle cathode is demonstrated with large optical modulation and good long-term stability. Our research provides a new route to realize the coincident utilization of optical-electrochemical energy.

Reconstruction of TiO2/MnO2-C nanotube/nanoflake core/shell arrays as high-performance supercapacitor electrodes

NASA Astrophysics Data System (ADS)

Xiong, Qinqin; Zheng, Cun; Chi, Hongzhong; Zhang, Jun; Ji, Zhenguo

2017-02-01

Construction of electrodes with fast reaction kinetics is of great importance for achieving advanced supercapacitors. Herein we report a facile combined synthetic strategy with atomic layer deposition (ALD) and electrodeposition to rationally fabricate nanotube/nanoflake core/shell arrays. ALD-TiO2 nanotubes are used as the skeleton core for assembly of electrodeposited MnO2-C nanoflake shells forming a core/shell structure. Highly porous architecture and good electrical conductivity are combined in this unique core/shell structure, resulting in fast ion/electron transfer. In tests of electrochemical performance, the TiO2/MnO2-C core/shell arrays are characterized as cathode for asymmetric supecapacitors and exhibit high specific capacitance (880 F g-1 at 2.5 A g-1), excellent rate properties (735 F g-1 at 30 A g-1) and good long-term cycling stability (94.3% capacitance retention after 20 000 cycles). The proposed electrode construction strategy is favorable for fabrication of other advanced supercapacitor electrodes.

Reconstruction of TiO2/MnO2-C nanotube/nanoflake core/shell arrays as high-performance supercapacitor electrodes.

PubMed

Xiong, Qinqin; Zheng, Cun; Chi, Hongzhong; Zhang, Jun; Ji, Zhenguo

2017-02-03

Construction of electrodes with fast reaction kinetics is of great importance for achieving advanced supercapacitors. Herein we report a facile combined synthetic strategy with atomic layer deposition (ALD) and electrodeposition to rationally fabricate nanotube/nanoflake core/shell arrays. ALD-TiO 2 nanotubes are used as the skeleton core for assembly of electrodeposited MnO 2 -C nanoflake shells forming a core/shell structure. Highly porous architecture and good electrical conductivity are combined in this unique core/shell structure, resulting in fast ion/electron transfer. In tests of electrochemical performance, the TiO 2 /MnO 2 -C core/shell arrays are characterized as cathode for asymmetric supecapacitors and exhibit high specific capacitance (880 F g -1 at 2.5 A g -1 ), excellent rate properties (735 F g -1 at 30 A g -1 ) and good long-term cycling stability (94.3% capacitance retention after 20 000 cycles). The proposed electrode construction strategy is favorable for fabrication of other advanced supercapacitor electrodes.

Achieving High-Energy-High-Power Density in a Flexible Quasi-Solid-State Sodium Ion Capacitor.

PubMed

Li, Hongsen; Peng, Lele; Zhu, Yue; Zhang, Xiaogang; Yu, Guihua

2016-09-14

Simultaneous integration of high-energy output with high-power delivery is a major challenge for electrochemical energy storage systems, limiting dual fine attributes on a device. We introduce a quasi-solid-state sodium ion capacitor (NIC) based on a battery type urchin-like Na2Ti3O7 anode and a capacitor type peanut shell derived carbon cathode, using a sodium ion conducting gel polymer as electrolyte, achieving high-energy-high-power characteristics in solid state. Energy densities can reach 111.2 Wh kg(-1) at power density of 800 W kg(-1), and 33.2 Wh kg(-1) at power density of 11200 W kg(-1), which are among the best reported state-of-the-art NICs. The designed device also exhibits long-term cycling stability over 3000 cycles with capacity retention ∼86%. Furthermore, we demonstrate the assembly of a highly flexible quasi-solid-state NIC and it shows no obvious capacity loss under different bending conditions.

A novel high pressure, high temperature vessel used to conduct long-term stability measurements of silicon MEMS pressure transducers

NASA Astrophysics Data System (ADS)

Wisniewiski, David

2014-03-01

The need to quantify and to improve long-term stability of pressure transducers is a persistent requirement from the aerospace sector. Specifically, the incorporation of real-time pressure monitoring in aircraft landing gear, as exemplified in Tire Pressure Monitoring Systems (TPMS), has placed greater demand on the pressure transducer for improved performance and increased reliability which is manifested in low lifecycle cost and minimal maintenance downtime through fuel savings and increased life of the tire. Piezoresistive (PR) silicon MEMS pressure transducers are the primary choice as a transduction method for this measurement owing to their ability to be designed for the harsh environment seen in aircraft landing gear. However, these pressure transducers are only as valuable as the long-term stability they possess to ensure reliable, real-time monitoring over tens of years. The "heart" of the pressure transducer is the silicon MEMS element, and it is at this basic level where the long-term stability is established and needs to be quantified. A novel High Pressure, High Temperature (HPHT) vessel has been designed and constructed to facilitate this critical measurement of the silicon MEMS element directly through a process of mechanically "floating" the silicon MEMS element while being subjected to the extreme environments of pressure and temperature, simultaneously. Furthermore, the HPHT vessel is scalable to permit up to fifty specimens to be tested at one time to provide a statistically significant data population on which to draw reasonable conclusions on long-term stability. With the knowledge gained on the silicon MEMS element, higher level assembly to the pressure transducer envelope package can also be quantified as to the build-effects contribution to long-term stability in the same HPHT vessel due to its accommodating size. Accordingly, a HPHT vessel offering multiple levels of configurability and robustness in data measurement is presented, along with 10 year long-term stability results.

Correlation of Electrolyte Volume and Electrochemical Performance in Lithium-Ion Pouch Cells with Graphite Anodes and NMC532 Cathodes

DOE Office of Scientific and Technical Information (OSTI.GOV)

An, Seong Jin; Li, Jianlin; Mohanty, Debasish

2017-01-01

The work herein reports on studies aimed at exploring the correlation between electrolyte volume and electrochemical performance of full cell, pouch-cells consisting of graphite/ Li 1.02Ni 0.50Mn 0.29Co 0.19O 2 (NMC-532) as the electrodes and 1.2 M LiPF6 in ethylene carbonate:ethylmethyl carbonate (EC:EMC) as the electrolyte. It is demonstrated that a minimum electrolyte volume factor of 1.9 times the total pore volume of cell components (cathode, anode, and separator) is needed for long-term cyclability and low impedance. Less electrolyte results in an increase of the measured ohmic resistances. Increased resistance ratios for charge transfer and passivation layers at cathode, relativemore » to initial values, were 1.5–2.0 after 100 cycles. At the cathode, the resistance from charge transfer was 2–3 times higher than for passivation layers. Differential voltage analysis showed that anodes were less delithiated after discharging as the cells were cycled.« less

Correlation of Electrolyte Volume and Electrochemical Performance in Lithium-Ion Pouch Cells with Graphite Anodes and NMC532 Cathodes

DOE PAGES

An, Seong Jin; Li, Jianlin; Mohanty, Debasish; ...

2017-04-07

The work herein reports on studies aimed at exploring the correlation between electrolyte volume and electrochemical performance of full cell, pouch-cells consisting of graphite/ Li 1.02Ni 0.50Mn 0.29Co 0.19O 2 (NMC-532) as the electrodes and 1.2 M LiPF 6 in ethylene carbonate:ethylmethyl carbonate (EC:EMC) as the electrolyte. In addition, it is demonstrated that a minimum electrolyte volume factor of 1.9 times the total pore volume of cell components (cathode, anode, and separator) is needed for long-term cyclability and low impedance. Less electrolyte results in an increase of the measured Ohmic resistances. Increased resistance ratios for charge transfer and passivation layersmore » at cathode, relative to initial values, were 1.5 2.0 after 100 cycles. At the cathode, the resistance from charge transfer was 2-3 times higher than for passivation layers. Lastly, differential voltage analysis showed that anodes were less delithiated after discharging as the cells were cycled.« less

Long-term stability and properties of zirconia ceramics for heavy duty diesel engine components

NASA Technical Reports Server (NTRS)

Larsen, D. C.; Adams, J. W.

1985-01-01

Physical, mechanical, and thermal properties of commercially available transformation-toughened zirconia are measured. Behavior is related to the material microstructure and phase assemblage. The stability of the materials is assessed after long-term exposure appropriate for diesel engine application. Properties measured included flexure strength, elastic modulus, fracture toughness, creep, thermal shock, thermal expansion, internal friction, and thermal diffusivity. Stability is assessed by measuring the residual property after 1000 hr/1000C static exposure. Additionally static fatigue and thermal fatigue testing is performed. Both yttria-stabilized and magnesia-stabilized materials are compared and contrasted. The major limitations of these materials are short term loss of properties with increasing temperature as the metastable tetragonal phase becomes more stable. Fine grain yttria-stabilized material (TZP) is higher strength and has a more stable microstructure with respect to overaging phenomena. The long-term limitation of Y-TZP is excessive creep deformation. Magnesia-stabilized PSZ has relatively poor stability at elevated temperature. Overaging, decomposition, and/or destabilization effects are observed. The major limitation of Mg-PSZ is controlling unwanted phase changes at elevated temperature.

Insight into the structure and functional application of the Sr0.95Ce0.05CoO3-δ cathode for solid oxide fuel cells.

PubMed

Yang, Wei; Zhang, Huairuo; Sun, Chunwen; Liu, Lilu; Alonso, J A; Fernández-Díaz, M T; Chen, Liquan

2015-04-06

A new perovskite cathode, Sr0.95Ce0.05CoO3-δ, performs well for oxygen-reduction reactions in solid oxide fuel cells (SOFCs). We gain insight into the crystal structure of Sr1-xCexCoO3-δ (x = 0.05, 0.1) and temperature-dependent structural evolution of Sr0.95Ce0.05CoO3-δ by X-ray diffraction, neutron powder diffraction, and scanning transmission electron microscopy experiments. Sr0.9Ce0.1CoO3-δ shows a perfectly cubic structure (a = a0), with a large oxygen deficiency in a single oxygen site; however, Sr0.95Ce0.05CoO3-δ exhibits a tetragonal perovskite superstructure with a double c axis, defined in the P4/mmm space group, that contains two crystallographically different cobalt positions, with distinct oxygen environments. The structural evolution of Sr0.95Ce0.05CoO3-δ at high temperatures was further studied by in situ temperature-dependent NPD experiments. At 1100 K, the oxygen atoms in Sr0.95Ce0.05CoO3-δ show large and highly anisotropic displacement factors, suggesting a significant ionic mobility. The test cell with a La0.8Sr0.2Ga0.83Mg0.17O3-δ-electrolyte-supported (∼300 μm thickness) configuration yields peak power densities of 0.25 and 0.48 W cm(-2) at temperatures of 1023 and 1073 K, respectively, with pure H2 as the fuel and ambient air as the oxidant. The electrochemical impedance spectra evolution with time of the symmetric cathode fuel cell measured at 1073 K shows that the Sr0.95Ce0.05CoO3-δ cathode possesses superior ORR catalytic activity and long-term stability. Mixed ionic-electronic conduction properties of Sr0.95Ce0.05CoO3-δ account for its good performance as an oxygen-reduction catalyst.

Control of electrochemical properties of nickel-rich layered cathode materials for lithium ion batteries by variation of the manganese to cobalt ratio

NASA Astrophysics Data System (ADS)

Sun, Ho-Hyun; Choi, Wonchang; Lee, Joong Kee; Oh, In-Hwan; Jung, Hun-Gi

2015-02-01

Various Ni-rich layered oxide cathodes (above 0.80 Ni content), such as LiNi1-y-zCoyAlzO2 (NCA), are used in electric vehicles (EVs) due to their high capacity (∼200 mAh g-1 for NCA). However, to improve cycle performance and thermal stability and to ensure longer and safer usage, numerous studies have investigated surface modification, coating, and doping of cathode materials. In this study, we have investigated the characteristics of Li[Ni0.85CoxMn0.15-x]O2 with various Mn to Co ratios (x = 0-0.15) synthesized by a coprecipitation method. The discharge capacities of the Li[Ni0.85CoxMn0.15-x]O2 cathodes are similar at around 206 mAh g-1 at room temperature and 213.8 mAh g-1 at 55 °C between 2.7 and 4.3 V at a 0.2C rate, while the cyclability, thermal stability, and rate capability of all samples differ according to the Mn and Co ratio. The Li[Ni0.85Co0.05Mn0.10]O2 cathode shows the most promising electrochemical properties under different conditions among the various cathodes evaluated; it displays a high rate capacity (approximately 163 mAh g-1 at 5C rate) at 25 °C and good thermal stability (main exothermic temperature of 233.7 °C and relatively low heat evolution of 857.3 J g-1).

Controlled phase stability of highly Na-active triclinic structure in nanoscale high-voltage Na2-2xCo1+xP2O7 cathode for Na-ion batteries

NASA Astrophysics Data System (ADS)

Song, Hee Jo; Kim, Jae-Chan; Dar, Mushtaq Ahmad; Kim, Dong-Wan

2018-02-01

With the increasing demand for high energy density in energy-storage systems, a high-voltage cathode is essential in rechargeable Li-ion and Na-ion batteries. The operating voltage of a triclinic-polymorph Na2CoP2O7, also known as the rose form, is above 4.0 V (vs. Na/Na+), which is relatively high compared to that of other cathode materials. Thus, it can be employed as a potential high-voltage cathode material in Na-ion batteries. However, it is difficult to synthesize a pure rose phase because of its low phase stability, thus limiting its use in high-voltage applications. Herein, compositional-engineered, rose-phase Na2-2xCo1+xP2O7/C (x = 0, 0.1 and 0.2) nanopowder are prepared using a wet-chemical method. The Na2-2xCo1+xP2O7/C cathode shows high electrochemical reactivity with Na ions at 4.0 V, delivering high capacity and high energy density.

Delithiated states of layered cathode materials: doping and dispersion interaction effects on the structure

NASA Astrophysics Data System (ADS)

Eremin, Roman; Zolotarev, Pavel; Bobrikov, Ivan

2018-04-01

Here we present results of density functional theory (DFT) study of delithiated structures of layered LiNiO2 (LNO, Li12Ni12O24 model) cathode material and its doped analogue LiNi0.833Co0.083Al0.083O2 (N10C1A1, Li12Ni10CoAlO24 model). The paper is aimed at independent elucidation of doping and dispersion interaction effects on the structural stability of cathode materials studied. For this purpose, the LNO and N10C1A1 configurational spaces consisting of 87 and 4512 crystallographically independent configurations (obtained starting from 2×2×1 supercell of R-3m structure of LNO) are optimized within a number of DFT models. Based on a comparison of the calculated dependencies for the lattice parameters with the results of in situ neutron diffraction experiments, the most pronounced effect of cathode material stabilization is due to the dispersion interaction. In turn, the doping effect is found to affect cathode structure behavior at the latest stages of delithiation only.

Related Studies in Long Term Lithium Battery Stability

NASA Technical Reports Server (NTRS)

Horning, R. J.; Chua, D. L.

1984-01-01

The continuing growth of the use of lithium electrochemical systems in a wide variety of both military and industrial applications is primarily a result of the significant benefits associated with the technology such as high energy density, wide temperature operation and long term stability. The stability or long term storage capability of a battery is a function of several factors, each important to the overall storage life and, therefore, each potentially a problem area if not addressed during the design, development and evaluation phases of the product cycle. Design (e.g., reserve vs active), inherent material thermal stability, material compatibility and self-discharge characteristics are examples of factors key to the storability of a power source.

Atomic-Scale Origin of Long-Term Stability and High Performance of p-GaN Nanowire Arrays for Photocatalytic Overall Pure Water Splitting.

PubMed

Kibria, Md Golam; Qiao, Ruimin; Yang, Wanli; Boukahil, Idris; Kong, Xianghua; Chowdhury, Faqrul Alam; Trudeau, Michel L; Ji, Wei; Guo, Hong; Himpsel, F J; Vayssieres, Lionel; Mi, Zetian

2016-10-01

The atomic-scale origin of the unusually high performance and long-term stability of wurtzite p-GaN oriented nanowire arrays is revealed. Nitrogen termination of both the polar (0001¯) top face and the nonpolar (101¯0) side faces of the nanowires is essential for long-term stability and high efficiency. Such a distinct atomic configuration ensures not only stability against (photo) oxidation in air and in water/electrolyte but, as importantly, also provides the necessary overall reverse crystal polarization needed for efficient hole extraction in p-GaN. © 2016 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Enhanced electro-Fenton Mineralization of Acid Orange 7 Using a Carbon Nanotube Fiber Based Cathode

NASA Astrophysics Data System (ADS)

Huong Le, Thi Xuan; Alemán, Belén; Vilatela, Juan J.; Bechelany, Mikhael; Cretin, Marc

2018-02-01

A new cathodic material for electro-Fenton (EF) process was prepared based on a macroscopic fiber (CNTF) made of mm long carbon nanotubes directly spun from the gas phase by floating catalyst CVD, on a carbon fiber (CF) substrate. CNTF@CF electrode is a highly graphitic material combining a high surface area ( 260 m2/g) with high electrical conductivity and electrochemical stability . One kind of azo dye, acid orange 7 (AO7), was used as model bio-refractory pollutant to be treated at CNTF@CF cathode in acidic aqueous medium (pH 3.0). The experimental results pointed out that AO7 and its organic intermediate compounds were totally mineralized by hydroxyl radical generated from Fenton reaction. In fact, 96.7 % of the initial TOC was eliminated in 8h of electrolysis by applying a current of -25 mA and ferrous ions as catalyst at concentration of 0.2 mM. At the same electrolysis time, only 23.7 % of TOC removal found on CF support which proved the high mineralization efficiency of new material thanks to CNTs deposition. The CNTF@CF cathode maintained stable its activity during five experimental cycles of EF set-up. The results indicated that CNTF@CF material could be a potential choice for wastewater treatment containing bio-refractory by electrochemical advanced oxidation processes (EAOPs).

Equilibrium high entropy alloy phase stability from experiments and thermodynamic modeling

DOE Office of Scientific and Technical Information (OSTI.GOV)

Saal, James E.; Berglund, Ida S.; Sebastian, Jason T.

Long-term stability of high entropy alloys (HEAs) is a critical consideration for the design and practical application of HEAs. It has long been assumed that many HEAs are a kinetically-stabilized metastable structure, and recent experiments have confirmed this hypothesis by observing HEA ecomposition after long-termequilibration. In the presentwork,we demonstrate the use of the CALculation of PHAse Diagrams (CALPHAD) approach to predict HEA stability and processing parameters, comparing experimental long-term annealing observations to CALPHAD phase diagrams from a commercially-available HEA database. As a result, we find good agreement between single- and multi-phase predictions and experiments.

Equilibrium high entropy alloy phase stability from experiments and thermodynamic modeling

DOE PAGES

Saal, James E.; Berglund, Ida S.; Sebastian, Jason T.; ...

2017-10-29

Long-term stability of high entropy alloys (HEAs) is a critical consideration for the design and practical application of HEAs. It has long been assumed that many HEAs are a kinetically-stabilized metastable structure, and recent experiments have confirmed this hypothesis by observing HEA ecomposition after long-termequilibration. In the presentwork,we demonstrate the use of the CALculation of PHAse Diagrams (CALPHAD) approach to predict HEA stability and processing parameters, comparing experimental long-term annealing observations to CALPHAD phase diagrams from a commercially-available HEA database. As a result, we find good agreement between single- and multi-phase predictions and experiments.

Self aligning electron beam gun having enhanced thermal and mechanical stability

DOEpatents

Scarpetti, R.D. Jr.; Parkison, C.D.; Switzer, V.A.; Lee, Y.J.; Sawyer, W.C.

1995-05-16

A compact, high power electron gun is disclosed having enhanced thermal and mechanical stability which incorporates a mechanically coupled, self aligning structure for the anode and cathode. The enhanced stability, and reduced need for realignment of the cathode to the anode and downstream optics during operation are achieved by use of a common support structure for the cathode and anode which requires no adjustment screws or spacers. The electron gun of the present invention also incorporates a modular design for the cathode, in which the electron emitter, its support structure, and the hardware required to attach the emitter assembly to the rest of the gun are a single element. This modular design makes replacement of the emitter simpler and requires no realignment after a new emitter has been installed. Compactness and a reduction in the possibility of high voltage breakdown are achieved by shielding the ``triple point`` where the electrode, insulator, and vacuum meet. The use of electric discharge machining (EDM) for fabricating the emitter allows for the accurate machining of the emitter into intricate shapes without encountering the normal stresses developed by standard emitter fabrication techniques. 12 Figs.

A combined theoretical and experimental study on the oxygenated graphitic carbon nitride as a promising sulfur host for lithium-sulfur batteries

NASA Astrophysics Data System (ADS)

He, Feng; Li, Kai; Yin, Cong; Ding, Yingchun; Tang, Hao; Wang, Ying; Wu, Zhijian

2018-01-01

To effectively restrain the dissolution of soluble polysulfides and fully utilize the active sulfur materials in lithium-sulfur (Li-S) batteries, host materials with unique compositions and porous structures have been pursued. Herein, we have investigated the mechanism of the excellent activity of oxygenated g-C3N4 for Li-S batteries from theoretical perspective, and the further experiment confirms that our O-g-C3N4-S cathode exhibits much better electrochemical performance compared with those in previous reports. Our DFT calculations reveal that the oxygenated material has better electrical conductivity and stronger adsorption ability with the Li2Sx species compared with the pristine g-C3N4 and other two-dimensional (2D) materials. Furthermore, we have confirmed experimentally that the O-g-C3N4-S composite cathode exhibits excellent electrochemical performance in Li-S batteries with high reversible discharge capacity of 1030 mAh g-1 after 100 cycles at 0.2 C, great rate capability with the discharge capacity of 364 mAh g-1 even at 5.0 C, and outstanding long-term cyclic stability with the discharge capacity of 465 mAh g-1 after 1000 cycles at 1.0 C (capacity decay was only 0.046% per cycle). Our results also suggest that theoretical study will play a significant role in predicting and screening novel materials with better performance.

Sustainability Impact of Nanomaterial Enhanced Lithium Ion Batteries

NASA Astrophysics Data System (ADS)

Ganter, Matthew

Energy storage devices are becoming an integral part of sustainable energy technology adoption, particularly, in alternative transportation (electric vehicles) and renewable energy technologies (solar and wind which are intermittent). The most prevalent technology exhibiting near-term impact are lithium ion batteries, especially in portable consumer electronics and initial electric vehicle models like the Chevy Volt and Nissan Leaf. However, new technologies need to consider the full life-cycle impacts from material production and use phase performance to the end-of-life management (EOL). This dissertation investigates the impacts of nanomaterials in lithium ion batteries throughout the life cycle and develops strategies to improve each step in the process. The embodied energy of laser vaporization synthesis and purification of carbon nanotubes (CNTs) was calculated to determine the environmental impact of the novel nanomaterial at beginning of life. CNTs were integrated into lithium ion battery electrodes as conductive additives, current collectors, and active material supports to increase power, energy, and thermal stability in the use phase. A method was developed to uniformly distribute CNT conductive additives in composites. Cathode composites with CNT additives had significant rate improvements (3x the capacity at a 10C rate) and higher thermal stability (40% reduction in exothermic energy released upon overcharge). Similar trends were also measured with CNTs in anode composites. Advanced free-standing anodes incorporating CNTs with high capacity silicon and germanium were measured to have high capacities where surface area reduction improved coulombic efficiencies and thermal stability. A thermal stability plot was developed that compares the safety of traditional composites with free-standing electrodes, relating the results to thermal conductivity and surface area effects. The EOL management of nanomaterials in lithium ion batteries was studied and a novel recycling technique, referred to as refunctionalization , for lithium ion cathode materials was developed. Refunctionalization is the treatment of active materials in order to regain electrochemical performance at EOL which eliminates the need to recycle to the elemental level and can lead to greater environmental and economic savings. The lithium ion capacity of EOL lithium iron phosphate (LiFePO4) nanomaterial cathode was regained through chemical and electrochemical re-lithiation techniques. The embodied energy of refunctionalized LiFePO4 was calculated to be 50% less than cathode synthesized from virgin materials. Overall, these results contribute to an improved understanding of the life cycle impacts for nanomaterials in batteries. The CNT embodied energy calculation established the first life cycle inventory for laser vaporization CNTs, whereas the novel refunctionalization strategies established a new EOL pathway to recover cathodes at a higher value state than traditional recycling. At the same time, CNT enhanced battery electrodes increased power and energy in the use phase while demonstrating the unique ability to engineer electrodes to control thermal stability, which enables better performing and safer batteries.

Miniature Reservoir Cathode: An Update

NASA Technical Reports Server (NTRS)

Vancil, Bernard K.; Wintucky, Edwin G.

2002-01-01

We report on recent work to produce a small low power, low cost reservoir cathode capable of long life (more than 100,000 hours) at high loading (> 5 A/sq cm). Our objective is a highly manufacturable, commercial device costing less than $30. Small highly loaded cathodes are needed, especially for millimeter wave tubes, where focusing becomes difficult when area convergence ratios are too high. We currently have 3 models ranging from .060-inch diameter to. 125-inch diameter. Reservoir type barium dispenser cathodes have a demonstrated capability for simultaneous high emission density and long life. Seven reservoir cathodes continue to operate on the cathode life test facility at NSWC, Crane, Indiana at 2 and 4 amps/sq cm. They have accumulated nearly 100,000 hours with practically no change in emission levels or knee temperature.

PULSE AMPLIFIER

DOEpatents

Johnstone, C.W.

1958-06-17

The improvement of pulse amplifiers used with scintillation detectors is described. The pulse amplifier circuit has the advantage of reducing the harmful effects of overloading cause by large signal inputs. In general the pulse amplifier circuit comprises two amplifier tubes with the input pulses applied to one amplifier grid and coupled to the second amplifier tube through a common cathode load. The output of the second amplifier is coupled from the plate circuit to a cathode follower tube grid and a diode tube in connected from grid to cathode of the cathode follower tube. Degenerative feedback is provided in the second amplifier by coupling a signal from the cathode follower cathode to the second amplifier grid. The circuit proqides moderate gain stability, and overload protection for subsequent pulse circuits.

Binder-free LiCoO2/carbon nanotube cathodes for high-performance lithium ion batteries.

PubMed

Luo, Shu; Wang, Ke; Wang, Jiaping; Jiang, Kaili; Li, Qunqing; Fan, Shoushan

2012-05-02

Binder-free LiCoO(2) -SACNT cathodes with excellent flexibility and conductivity are obtained by constructing a continuous three-dimensional super-aligned carbon nanotube (SACNT) framework with embedded LiCoO(2) particles. These binder-free cathodes display much better cycling stability, greater rate performance, and higher energy density than classical cathodes with binder. Various functional binder-free SACNT composites can be mass produced by the ultrasonication and co-deposition method described in this paper. Copyright © 2012 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Power-Efficient, High-Current-Density, Long-Life Thermionic Cathode Developed for Microwave Amplifier Applications

NASA Technical Reports Server (NTRS)

Wintucky, Edwin G.

2002-01-01

A power-efficient, miniature, easily manufactured, reservoir-type barium-dispenser thermionic cathode has been developed that offers the significant advantages of simultaneous high electron-emission current density (>2 A/sq cm) and very long life (>100,000 hr of continuous operation) when compared with the commonly used impregnated-type barium-dispenser cathodes. Important applications of this cathode are a wide variety of microwave and millimeter-wave vacuum electronic devices, where high output power and reliability (long life) are essential. We also expect it to enable the practical development of higher purveyance electron guns for lower voltage and more reliable device operation. The low cathode heater power and reduced size and mass are expected to be particularly beneficial in traveling-wave-tube amplifiers (TWTA's) for space communications, where future NASA mission requirements include smaller onboard spacecraft systems, higher data transmission rates (high frequency and output power) and greater electrical efficiency.

Multiscale Transient and Steady-State Study of the Influence of Microstructure Degradation and Chromium Oxide Poisoning on Solid Oxide Fuel Cell Cathode Performance

NASA Astrophysics Data System (ADS)

Li, Guanchen; von Spakovsky, Michael R.; Shen, Fengyu; Lu, Kathy

2018-01-01

Oxygen reduction in a solid oxide fuel cell cathode involves a nonequilibrium process of coupled mass and heat diffusion and electrochemical and chemical reactions. These phenomena occur at multiple temporal and spatial scales, making the modeling, especially in the transient regime, very difficult. Nonetheless, multiscale models are needed to improve the understanding of oxygen reduction and guide cathode design. Of particular importance for long-term operation are microstructure degradation and chromium oxide poisoning both of which degrade cathode performance. Existing methods are phenomenological or empirical in nature and their application limited to the continuum realm with quantum effects not captured. In contrast, steepest-entropy-ascent quantum thermodynamics can be used to model nonequilibrium processes (even those far-from equilibrium) at all scales. The nonequilibrium relaxation is characterized by entropy generation, which can unify coupled phenomena into one framework to model transient and steady behavior. The results reveal the effects on performance of the different timescales of the varied phenomena involved and their coupling. Results are included here for the effects of chromium oxide concentrations on cathode output as is a parametric study of the effects of interconnect-three-phase-boundary length, oxygen mean free path, and adsorption site effectiveness. A qualitative comparison with experimental results is made.

Tris(trimethylsilyl) Phosphite as an Efficient Electrolyte Additive To Improve the Surface Stability of Graphite Anodes.

PubMed

Yim, Taeeun; Han, Young-Kyu

2017-09-27

Tris(trimethylsilyl) phosphite (TMSP) has received considerable attention as a functional additive for various cathode materials in lithium-ion batteries, but the effect of TMSP on the surface stability of a graphite anode has not been studied. Herein, we demonstrate that TMSP serves as an effective solid electrolyte interphase (SEI)-forming additive for graphite anodes in lithium-ion batteries (LIBs). TMSP forms SEI layers by chemical reactions between TMSP and a reductively decomposed ethylene carbonate (EC) anion, which is strikingly different from the widely known mechanism of the SEI-forming additives. TMSP is stable under cathodic polarization, but it reacts chemically with radical anion intermediates derived from the electrochemical reduction of the carbonate solvents to generate a stable SEI layer. These TMSP-derived SEI layers improve the interfacial stability of the graphite anode, resulting in a retention of 96.8% and a high Coulombic efficiency of 95.2%. We suggest the use of TMSP as a functional additive that effectively stabilizes solid electrolyte interfaces of both the anode and cathode in lithium-ion batteries.

Evaluation of Laser Stabilization and Imaging Systems for LCLS-II - Final Paper

DOE Office of Scientific and Technical Information (OSTI.GOV)

Barry, Matthew

2015-08-20

By combining the top performing commercial laser beam stabilization system with the most ideal optical imaging configuration, the beamline for the Linear Accelerator Coherent Light Source II (LCLS-II) will deliver the highest quality and most stable beam to the cathode. To determine the optimal combination, LCLS-II beamline conditions were replicated and the systems tested with a He-Ne laser. The Guidestar-II and MRC active laser beam stabilization systems were evaluated for their ideal positioning and stability. Both a two and four lens optical imaging configuration was then evaluated for beam imaging quality, magnification properties, and natural stability. In their best performancesmore » when tested over fifteen hours, Guidestar-II kept the beam stable over approximately 70-110um while the MRC system kept it stable over approximately 90-100um. During short periods of time, Guidestar-II kept the beam stable between 10-20um, but was more susceptible to drift over time, while the MRC system maintained the beam between 30-50um with less overall drift. The best optical imaging configuration proved to be a four lens system that images to the iris located in the cathode room and from there, imaged to the cathode. The magnification from the iris to the cathode was 2:1, within an acceptable tolerance to the expected 2.1:1 magnification. The two lens configuration was slightly more stable in small periods of time (less than 10 minutes) without the assistance of a stability system, approximately 55um compared to approximately 70um, but the four lens configurations beam image had a significantly flatter intensity distribution compared to the two lens configuration which had a Gaussian distribution. A final test still needs to be run with both stability systems running at the same time through the four lens system. With this data, the optimal laser beam stabilization system can be determined for the beamline of LCLS-II.« less

Excellent rate capability and cycling stability in Li+-conductive Li2SnO3-coated LiNi0.5Mn1.5O4 cathode materials for lithium-ion batteries.

PubMed

Mou, Jirong; Deng, Yunlong; Song, Zhicui; Zheng, Qiaoji; Lam, Kwok Ho; Lin, Dunmin

2018-05-22

High-voltage LiNi0.5Mn1.5O4 is a promising cathode candidate for lithium-ion batteries (LIBs) due to its considerable energy density and power density, but the material generally undergoes serious capacity fading caused by side reactions between the active material and organic electrolyte. In this work, Li+-conductive Li2SnO3 was coated on the surface of LiNi0.5Mn1.5O4 to protect the cathode against the attack of HF, mitigate the dissolution of Mn ions during cycling and improve the Li+ diffusion coefficient of the materials. Remarkable improvement in cycling stability and rate performance has been achieved in Li2SnO3-coated LiNi0.5Mn1.5O4. The 1.0 wt% Li2SnO3-coated LiNi0.5Mn1.5O4 cathode exhibits excellent cycling stability with a capacity retention of 88.2% after 150 cycles at 0.1 C and rate capability at high discharge rates of 5 C and 10 C, presenting discharge capacities of 119.5 and 112.2 mAh g-1, respectively. In particular, a significant improvement in cycling stability at 55 °C is obtained after the coating of 1.0 wt% Li2SnO3, giving a capacity retention of 86.8% after 150 cycles at 1 C and 55 °C. The present study provides a significant insight into the effective protection of Li-conductive coating materials for a high-voltage LiNi0.5Mn1.5O4 cathode material.

Long-Term Stability of Scores on the Wechsler Intelligence Scale for Children-Fourth Edition in Children with Learning Disabilities

ERIC Educational Resources Information Center

Lander, Jenny

2010-01-01

The present investigation explored the stability of scores on the Wechsler Intelligence Scale for Children-IV (WISC-IV) over approximately a three-year period. Previous research has suggested that some children with Learning Disabilities (LD) do not demonstrate long-term stability of intelligence. Legally, school districts are no longer required…

AFM as an analysis tool for high-capacity sulfur cathodes for Li–S batteries

PubMed Central

Sörgel, Seniz; Costa, Rémi; Carlé, Linus; Galm, Ines; Cañas, Natalia; Pascucci, Brigitta; Friedrich, K Andreas

2013-01-01

Summary In this work, material-sensitive atomic force microscopy (AFM) techniques were used to analyse the cathodes of lithium–sulfur batteries. A comparison of their nanoscale electrical, electrochemical, and morphological properties was performed with samples prepared by either suspension-spraying or doctor-blade coating with different binders. Morphological studies of the cathodes before and after the electrochemical tests were performed by using AFM and scanning electron microscopy (SEM). The cathodes that contained polyvinylidene fluoride (PVDF) and were prepared by spray-coating exhibited a superior stability of the morphology and the electric network associated with the capacity and cycling stability of these batteries. A reduction of the conductive area determined by conductive AFM was found to correlate to the battery capacity loss for all cathodes. X-ray diffraction (XRD) measurements of Li2S exposed to ambient air showed that insulating Li2S hydrolyses to insulating LiOH. This validates the significance of electrical ex-situ AFM analysis after cycling. Conductive tapping mode AFM indicated the existence of large carbon-coated sulfur particles. Based on the analytical findings, the first results of an optimized cathode showed a much improved discharge capacity of 800 mA·g(sulfur)−1 after 43 cycles. PMID:24205455

75 FR 33769 - Manufacturing Extension Partnership (MEP) Availability of Funds for Projects To Develop and...

Federal Register 2010, 2011, 2012, 2013, 2014

2010-06-15

... to the long-term economic stability of the region. Please see the NIST MEP Web site, http://www.nist... region, and contribute to the long-term economic stability of the region. Competitive projects will use...

Modified High-Nickel Cathodes with Stable Surface Chemistry Against Ambient Air for Lithium-Ion Batteries.

PubMed

You, Ya; Celio, Hugo; Li, Jianyu; Dolocan, Andrei; Manthiram, Arumugam

2018-03-30

High-Ni layered oxides are promising next-generation cathodes for lithium-ion batteries owing to their high capacity and lower cost. However, as the Ni content increases over 70 %, they have a high dynamic affinity towards moisture and CO 2 in ambient air, primarily reacting to form LiOH, Li 2 CO 3 , and LiHCO 3 on the surface, which is commonly termed "residual lithium". Air exposure occurs after synthesis as it is common practice to handle and store them under ambient conditions. The air exposure leads to significant performance losses, and hampers the electrode fabrication, impeding their practical viability. Herein, we show that substituting a small amount of Al for Ni in the crystal lattice notably improves the chemical stability against air by limiting the formation of LiOH, Li 2 CO 3 , LiHCO 3 , and NiO in the near-surface region. The Al-doped high-Ni oxides display a high capacity retention with excellent rate capability and cycling stability after being exposed to air for 30 days. © 2018 Wiley-VCH Verlag GmbH & Co. KGaA, Weinheim.

Long-term effect of set potential on biocathodes in microbial fuel cells: electrochemical and phylogenetic characterization.

PubMed

Xia, Xue; Sun, Yanmei; Liang, Peng; Huang, Xia

2012-09-01

The long-term effect of set potential on oxygen reducing biocathodes was investigated in terms of electrochemical and biological characteristics. Three biocathodes were poised at 200, 60 and -100 mV vs. saturated calomel electrode (SCE) for 110 days, including the first 17 days for startup. Electrochemical analyses showed that 60 mV was the optimum potential during long-term operation. The performance of all the biocathodes kept increasing after startup, suggesting a period longer than startup time needed to make potential regulation more effective. The inherent characteristics without oxygen transfer limitation were studied. Different from short-term regulation, the amounts of biomass were similar while the specific electrochemical activity was significantly influenced by potential. Moreover, potential showed a strong selection for cathode bacteria. Clones 98% similar with an uncultured Bacteroidetes bacterium clone CG84 accounted for 75% to 80% of the sequences on the biocathodes that showed higher electrochemical activity (60 and -100 mV). Copyright © 2012 Elsevier Ltd. All rights reserved.

Size-Controlled Synthesis of Sub-10 nm PtNi3 Alloy Nanoparticles and their Unusual Volcano-Shaped Size Effect on ORR Electrocatalysis.

PubMed

Gan, Lin; Rudi, Stefan; Cui, Chunhua; Heggen, Marc; Strasser, Peter

2016-06-01

Dealloyed Pt bimetallic core-shell catalysts derived from low-Pt bimetallic alloy nanoparticles (e.g, PtNi3 ) have recently shown unprecedented activity and stability on the cathodic oxygen reduction reaction (ORR) under realistic fuel cell conditions and become today's catalyst of choice for commercialization of automobile fuel cells. A critical step toward this breakthrough is to control their particle size below a critical value (≈10 nm) to suppress nanoporosity formation and hence reduce significant base metal (e.g., Ni) leaching under the corrosive ORR condition. Fine size control of the sub-10 nm PtNi3 nanoparticles and understanding their size dependent ORR electrocatalysis are crucial to further improve their ORR activity and stability yet still remain unexplored. A robust synthetic approach is presented here for size-controlled PtNi3 nanoparticles between 3 and 10 nm while keeping a constant particle composition and their size-selected growth mechanism is studied comprehensively. This enables us to address their size-dependent ORR activities and stabilities for the first time. Contrary to the previously established monotonic increase of ORR specific activity and stability with increasing particle size on Pt and Pt-rich bimetallic nanoparticles, the Pt-poor PtNi3 nanoparticles exhibit an unusual "volcano-shaped" size dependence, showing the highest ORR activity and stability at the particle sizes between 6 and 8 nm due to their highest Ni retention during long-term catalyst aging. The results of this study provide important practical guidelines for the size selection of the low Pt bimetallic ORR electrocatalysts with further improved durably high activity. © 2016 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Structural changes and thermal stability of charged LiNixMnyCozO₂ cathode materials studied by combined in situ time-resolved XRD and mass spectroscopy.

PubMed

Bak, Seong-Min; Hu, Enyuan; Zhou, Yongning; Yu, Xiqian; Senanayake, Sanjaya D; Cho, Sung-Jin; Kim, Kwang-Bum; Chung, Kyung Yoon; Yang, Xiao-Qing; Nam, Kyung-Wan

2014-12-24

Thermal stability of charged LiNixMnyCozO2 (NMC, with x + y + z = 1, x:y:z = 4:3:3 (NMC433), 5:3:2 (NMC532), 6:2:2 (NMC622), and 8:1:1 (NMC811)) cathode materials is systematically studied using combined in situ time-resolved X-ray diffraction and mass spectroscopy (TR-XRD/MS) techniques upon heating up to 600 °C. The TR-XRD/MS results indicate that the content of Ni, Co, and Mn significantly affects both the structural changes and the oxygen release features during heating: the more Ni and less Co and Mn, the lower the onset temperature of the phase transition (i.e., thermal decomposition) and the larger amount of oxygen release. Interestingly, the NMC532 seems to be the optimized composition to maintain a reasonably good thermal stability, comparable to the low-nickel-content materials (e.g., NMC333 and NMC433), while having a high capacity close to the high-nickel-content materials (e.g., NMC811 and NMC622). The origin of the thermal decomposition of NMC cathode materials was elucidated by the changes in the oxidation states of each transition metal (TM) cations (i.e., Ni, Co, and Mn) and their site preferences during thermal decomposition. It is revealed that Mn ions mainly occupy the 3a octahedral sites of a layered structure (R3̅m) but Co ions prefer to migrate to the 8a tetrahedral sites of a spinel structure (Fd3̅m) during the thermal decomposition. Such element-dependent cation migration plays a very important role in the thermal stability of NMC cathode materials. The reasonably good thermal stability and high capacity characteristics of the NMC532 composition is originated from the well-balanced ratio of nickel content to manganese and cobalt contents. This systematic study provides insight into the rational design of NMC-based cathode materials with a desired balance between thermal stability and high energy density.

Structural changes and thermal stability of charged LiNi xMn yCo zO 2 cathode materials studied by combined in situ time-resolved XRD and mass spectroscopy

DOE PAGES

Bak, Seong -Min; Hu, Enyuan; Zhou, Yongning; ...

2014-11-24

Thermal stability of charged LiNi xMn yCo zO 2 (NMC, with x + y + z = 1, x:y:z = 4:3:3 (NMC433), 5:3:2 (NMC532), 6:2:2 (NMC622), and 8:1:1 (NMC811)) cathode materials is systematically studied using combined in situ time- resolved X-ray diffraction and mass spectroscopy (TR-XRD/MS) techniques upon heating up to 600 °C. The TR-XRD/MS results indicate that the content of Ni, Co, and Mn significantly affects both the structural changes and the oxygen release features during heating: the more Ni and less Co and Mn, the lower the onset temperature of the phase transition (i.e., thermal decomposition) and themore » larger amount of oxygen release. Interestingly, the NMC532 seems to be the optimized composition to maintain a reasonably good thermal stability, comparable to the low-nickel-content materials (e.g., NMC333 and NMC433), while having a high capacity close to the high-nickel-content materials (e.g., NMC811 and NMC622). The origin of the thermal decomposition of NMC cathode materials was elucidated by the changes in the oxidation states of each transition metal (TM) cations (i.e., Ni, Co, and Mn) and their site preferences during thermal decomposition. It is revealed that Mn ions mainly occupy the 3a octahedral sites of a layered structure (R3¯m) but Co ions prefer to migrate to the 8a tetrahedral sites of a spinel structure (Fd3¯m) during the thermal decomposition. Such element-dependent cation migration plays a very important role in the thermal stability of NMC cathode materials. The reasonably good thermal stability and high capacity characteristics of the NMC532 composition is originated from the well-balanced ratio of nickel content to manganese and cobalt contents. As a result, this systematic study provides insight into the rational design of NMC-based cathode materials with a desired balance between thermal stability and high energy density.« less

Tunable Core-Shell Single-Walled Carbon Nanotube-Cu2S Networked Nanocomposites as High-Performance Cathodes for Lithium-ion Batteries

DOE PAGES

Meng, Xiangbo; Riha, Shannon C.; Libera, Joseph A.; ...

2015-01-24

In this study, nanoscale copper(I) sulfide (n-Cu2S) was deposited over networks of single-walled carbon nanotubes (SWCNTs) by atomic layer deposition (ALD). This synthetic route provides a high degree of control for tuning the materials properties. The resulting core shell SWCNT-n-Cu2S composite structure ensures an intimate contact between the two components while maintaining a high porosity for efficient transport of charges. Indeed, electrochemical testing demonstrates that these nanocomposites are promising as cathodes in lithium-ion batteries (LIBs), exhibiting excellent stability over 200 discharge-charge cycles with a sustainable, high capacity of 260 mAh g(-1) (92% of the theoretical value in terms of Cu2S)more » and >99% Coulombic efficiency. This work establishes a general strategy for developing high-performance nanoscale electrode materials.« less

Outstanding Li-storage performance of LiFePO4@MWCNTs cathode material with 3D network structure for lithium-ion batteries

NASA Astrophysics Data System (ADS)

Sun, Xiaodong; Zhang, Le

2018-05-01

In this work, the MWCNTs-decorated LiFePO4 microspheres (LiFePO4@MWCNTs) with a 3D network structure have been synthesized by a facile and efficient spray-drying approach followed by solid-state reaction in a reduction atmosphere. In the as-prepared composite, the MWCNTs around LiFePO4 nanoparticles can provide 3D conductive networks which greatly facilitate the transport of Li+-ion and electron during the electrochemical reaction. Compared to the pure LiFePO4 material, the LiFePO4@MWCNTs composite as cathode for lithium-ion batteries exhibits significantly improved Li-storage performance in terms of rate capability and cyclic stability. Therefore, we can speculate that the spray-drying approach is a promising route to prepare the high-performance electrode materials with 3D network structure for electrochemical energy storage.

In Situ Encapsulating α-MnS into N,S-Codoped Nanotube-Like Carbon as Advanced Anode Material: α → β Phase Transition Promoted Cycling Stability and Superior Li/Na-Storage Performance in Half/Full Cells.

PubMed

Liu, Dai-Huo; Li, Wen-Hao; Zheng, Yan-Ping; Cui, Zheng; Yan, Xin; Liu, Dao-Sheng; Wang, Jiawei; Zhang, Yu; Lü, Hong-Yan; Bai, Feng-Yang; Guo, Jin-Zhi; Wu, Xing-Long

2018-04-02

Incorporation of N,S-codoped nanotube-like carbon (N,S-NTC) can endow electrode materials with superior electrochemical properties owing to the unique nanoarchitecture and improved kinetics. Herein, α-MnS nanoparticles (NPs) are in situ encapsulated into N,S-NTC, preparing an advanced anode material (α-MnS@N,S-NTC) for lithium-ion/sodium-ion batteries (LIBs/SIBs). It is for the first time revealed that electrochemical α → β phase transition of MnS NPs during the 1st cycle effectively promotes Li-storage properties, which is deduced by the studies of ex situ X-ray diffraction/high-resolution transmission electron microscopy and electrode kinetics. As a result, the optimized α-MnS@N,S-NTC electrode delivers a high Li-storage capacity (1415 mA h g -1 at 50 mA g -1 ), excellent rate capability (430 mA h g -1 at 10 A g -1 ), and long-term cycling stability (no obvious capacity decay over 5000 cycles at 1 A g -1 ) with retained morphology. In addition, the N,S-NTC-based encapsulation plays the key roles on enhancing the electrochemical properties due to its high conductivity and unique 1D nanoarchitecture with excellent protective effects to active MnS NPs. Furthermore, α-MnS@N,S-NTC also delivers high Na-storage capacity (536 mA h g -1 at 50 mA g -1 ) without the occurrence of such α → β phase transition and excellent full-cell performances as coupling with commercial LiFePO 4 and LiNi 0.6 Co 0.2 Mn 0.2 O 2 cathodes in LIBs as well as Na 3 V 2 (PO 4 ) 2 O 2 F cathode in SIBs. © 2018 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

BDNF-Val66Met-Polymorphism Impact on Cortical Plasticity in Schizophrenia Patients: A Proof-of-Concept Study

PubMed Central

Nitsche, Michael A.; Wobrock, Thomas; Bunse, Tilmann; Rein, Bettina; Herrmann, Maximiliane; Schmitt, Andrea; Nieratschker, Vanessa; Witt, Stephanie H.; Rietschel, Marcella; Falkai, Peter; Hasan, Alkomiet

2015-01-01

Background: Brain-derived neurotrophic factor (BDNF) has been shown to be a moderator of neuroplasticity. A frequent BDNF-polymorphism (Val66Met) is associated with impairments of cortical plasticity. In patients with schizophrenia, reduced neuroplastic responses following non-invasive brain stimulation have been reported consistently. Various studies have indicated a relationship between the BDNF-Val66Met-polymorphism and motor-cortical plasticity in healthy individuals, but schizophrenia patients have yet to be investigated. The aim of this proof-of-concept study was, therefore, to test the impact of the BDNF-Val66Met-polymorphism on inhibitory and facilitatory cortical plasticity in schizophrenia patients. Methods: Cortical plasticity was investigated in 22 schizophrenia patients and 35 healthy controls using anodal and cathodal transcranial direct-current stimulation (tDCS) applied to the left primary motor cortex. Animal and human research indicates that excitability shifts following anodal and cathodal tDCS are related to molecular long-term potentiation and long-term depression. To test motor-cortical excitability before and after tDCS, well-established single- and paired-pulse transcranial magnetic stimulation protocols were applied. Results: Our analysis revealed increased glutamate-mediated intracortical facilitation in met-heterozygotes compared to val-homozygotes at baseline. Following cathodal tDCS, schizophrenia met-heterozygotes had reduced gamma-amino-butyric-acid-mediated short-interval intracortical inhibition, whereas healthy met-heterozygotes displayed the opposite effect. The BDNF-Val66Met-polymorphism did not influence single-pulse motor-evoked potential amplitudes after tDCS. Conclusions: These preliminary findings support the notion of an association of the BDNF-Val66Met-polymorphism with observable alterations in plasticity following cathodal tDCS in schizophrenia patients. This indicates a complex interaction between inhibitory intracortical interneuron-networks, cortical plasticity, and the BDNF-Val66Met-polymorphism. Further replication and validation need to be dedicated to this question to confirm this relationship. PMID:25612896

An Insoluble Titanium-Lead Anode for Sulfate Electrolytes

DOE Office of Scientific and Technical Information (OSTI.GOV)

Ferdman, Alla

2005-05-11

The project is devoted to the development of novel insoluble anodes for copper electrowinning and electrolytic manganese dioxide (EMD) production. The anodes are made of titanium-lead composite material produced by techniques of powder metallurgy, compaction of titanium powder, sintering and subsequent lead infiltration. The titanium-lead anode combines beneficial electrochemical behavior of a lead anode with high mechanical properties and corrosion resistance of a titanium anode. In the titanium-lead anode, the titanium stabilizes the lead, preventing it from spalling, and the lead sheathes the titanium, protecting it from passivation. Interconnections between manufacturing process, structure, composition and properties of the titanium-lead compositemore » material were investigated. The material containing 20-30 vol.% of lead had optimal combination of mechanical and electrochemical properties. Optimal process parameters to manufacture the anodes were identified. Prototypes having optimized composition and structure were produced for testing in operating conditions of copper electrowinning and EMD production. Bench-scale, mini-pilot scale and pilot scale tests were performed. The test anodes were of both a plate design and a flow-through cylindrical design. The cylindrical anodes were composed of cylinders containing titanium inner rods and fitting over titanium-lead bushings. The cylindrical design allows the electrolyte to flow through the anode, which enhances diffusion of the electrolyte reactants. The cylindrical anodes demonstrate higher mass transport capabilities and increased electrical efficiency compared to the plate anodes. Copper electrowinning represents the primary target market for the titanium-lead anode. A full-size cylindrical anode performance in copper electrowinning conditions was monitored over a year. The test anode to cathode voltage was stable in the 1.8 to 2.0 volt range. Copper cathode morphology was very smooth and uniform. There was no measurable anode weight loss during this time period. Quantitative chemical analysis of the anode surface showed that the lead content after testing remained at its initial level. No lead dissolution or transfer from the anode to the product occurred.A key benefit of the titanium-lead anode design is that cobalt additions to copper electrolyte should be eliminated. Cobalt is added to the electrolyte to help stabilize the lead oxide surface of conventional lead anodes. The presence of the titanium intimately mixed with the lead should eliminate the need for cobalt stabilization of the lead surface. The anode should last twice as long as the conventional lead anode. Energy savings should be achieved due to minimizing and stabilizing the anode-cathode distance in the electrowinning cells. The anode is easily substitutable into existing tankhouses without a rectifier change.The copper electrowinning test data indicate that the titanium-lead anode is a good candidate for further testing as a possible replacement for a conventional lead anode. A key consideration is the cost. Titanium costs have increased. One of the ways to get the anode cost down is manufacturing the anodes with fewer cylinders. Additional prototypes having different number of cylinders were constructed for a long-term commercial testing in a circuit without cobalt. The objective of the testing is to evaluate the need for cobalt, investigate the effect of decreasing the number of cylinders on the anode performance, and to optimize further the anode design in order to meet the operating requirements, minimize the voltage, maximize the life of the anode, and to balance this against a reasonable cost for the anode. It is anticipated that after testing of the additional prototypes, a whole cell commercial test will be conducted to complete evaluation of the titanium-lead anode costs/benefits.« less

Some Thoughts on Stability in Nonlinear Periodic Focusing Systems [Addendum

DOE R&D Accomplishments Database

McMillan, Edwin M.

1968-03-29

Addendum to September 5, 1967 report with the same title and with the abstract: A brief discussion is given of the long-term stability of particle motions through periodic focusing structures containing lumped nonlinear elements. A method is presented whereby one can specify the nonlinear elements in such a way as to generate a variety of structures in which the motion has long-term stability.

Understanding the interdiffusion behavior and determining the long term stability of tungsten fiber reinforced niobium-base matrix composite systems

NASA Technical Reports Server (NTRS)

Tien, John K.

1990-01-01

The long term interdiffusional stability of tungsten fiber reinforced niobium alloy composites is addressed. The matrix alloy that is most promising for use as a high temperature structural material for reliable long-term space power generation is Nb1Zr. As an ancillary project to this program, efforts were made to assess the nature and kinetics of interphase reaction between selected beryllide intermetallics and nickel and iron aluminides.

Nickel Hydroxide-Modified Sulfur/Carbon Composite as a High-Performance Cathode Material for Lithium Sulfur Battery.

PubMed

Niu, Xiao-Qing; Wang, Xiu-Li; Xie, Dong; Wang, Dong-Huang; Zhang, Yi-Di; Li, Yi; Yu, Ting; Tu, Jiang-Ping

2015-08-05

Tailored sulfur cathode is vital for the development of a high performance lithium-sulfur (Li-S) battery. A surface modification on the sulfur/carbon composite would be an efficient strategy to enhance the cycling stability. Herein, we report a nickel hydroxide-modified sulfur/conductive carbon black composite (Ni(OH)2@S/CCB) as the cathode material for the Li-S battery through the thermal treatment and chemical precipitation method. In this composite, the sublimed sulfur is stored in the CCB, followed by a surface modification of Ni(OH)2 nanoparticles with size of 1-2 nm. As a cathode for the Li-S battery, the as-prepared Ni(OH)2@S/CCB electrode exhibits better cycle stability and higher rate discharge capacity, compared with the bare S/CCB electrode. The improved performance is largely due to the introduction of Ni(OH)2 surface modification, which can effectively suppress the "shuttle effect" of polysulfides, resulting in enhanced cycling life and higher capacity.

Electro-peroxone degradation of diethyl phthalate: Cathode selection, operational parameters, and degradation mechanisms.

PubMed

Hou, Meifang; Chu, Yaofei; Li, Xiang; Wang, Huijiao; Yao, Weikun; Yu, Gang; Murayama, Seiichi; Wang, Yujue

2016-12-05

This study compares the degradation of diethyl phthalate (DEP) by the electro-peroxone (E-peroxone) process with three different carbon-based cathodes, namely, carbon-polytetrafluorethylene (carbon-PTFE), carbon felt, and reticulated vitreous carbon (RVC). Results show that the three cathodes had different electrocatalytic activity for converting sparged O2 to H2O2, which increased in order of carbon felt, RVC, and carbon-PTFE. The in-situ generated H2O2 then reacts with sparged O3 to yield OH, which can in turn oxidize ozone-refractory DEP toward complete mineralization. In general, satisfactory total organic carbon removal yields (76.4-91.8%) could be obtained after 60min of the E-peroxone treatment with the three carbon-based cathodes, and the highest yield was obtained with the carbon-PTFE cathode due to its highest activity for H2O2 generation. In addition, the carbon-PTFE and carbon felt cathodes exhibited excellent stability over six cycles of the E-peroxone treatment of DEP solutions. Based on the intermediates (e.g., monoethyl phthalate, phthalic acid, phenolics, and carboxylic acids) identified by HPLC-UV, plausible reaction pathways were proposed for DEP mineralization by the E-peroxone process. The results of this study indicate that carbon-based cathodes generally have good electrocatalytic activity and stability for application in extended E-peroxone operations to effectively remove phthalates from water. Copyright © 2015 Elsevier B.V. All rights reserved.

Mn-Based Cathode with Synergetic Layered-Tunnel Hybrid Structures and Their Enhanced Electrochemical Performance in Sodium Ion Batteries.

PubMed

Wu, Zhen-Guo; Li, Jun-Tao; Zhong, Yan-Jun; Guo, Xiao-Dong; Huang, Ling; Zhong, Ben-He; Agyeman, Daniel-Adjei; Lim, Jin-Myoung; Kim, Du-Ho; Cho, Maeng-Hyo; Kang, Yong-Mook

2017-06-28

A synergistic approach for advanced cathode materials is proposed. Sodium manganese oxide with a layered-tunnel hybrid structure was designed, synthesized, and subsequently investigated. The layered-tunnel hybrid structure provides fast Na ion diffusivity and high structural stability thanks to the tunnel phase, enabling high rate capability and greatly improved cycling stability compared to that of the pure P2 layered phase while retaining the high specific capacity of the P2 layered phase. The hybrid structure provided a decent discharge capacity of 133.4 mAh g -1 even at 8 C, which exceeds the reported best rate capability for Mn-based cathodes. It also displayed an impressive cycling stability, maintaining 83.3 mAh g -1 after 700 cycles at 10 C. Theoretical calculation and the potentiostatic intermittent titration technique (PITT) demonstrated that this hybrid structure helps enhance Na ion diffusivity during charge and discharge, attaining, as a result, an unprecendented electrochemical performance.

Superior Blends Solid Polymer Electrolyte with Integrated Hierarchical Architectures for All-Solid-State Lithium-Ion Batteries.

PubMed

Zhang, Dechao; Zhang, Long; Yang, Kun; Wang, Hongqiang; Yu, Chuang; Xu, Di; Xu, Bo; Wang, Li-Min

2017-10-25

Exploration of advanced solid electrolytes with good interfacial stability toward electrodes is a highly relevant research topic for all-solid-state batteries. Here, we report PCL/SN blends integrating with PAN-skeleton as solid polymer electrolyte prepared by a facile method. This polymer electrolyte with hierarchical architectures exhibits high ionic conductivity, large electrochemical windows, high degree flexibility, good flame-retardance ability, and thermal stability (workable at 80 °C). Additionally, it demonstrates superior compatibility and electrochemical stability toward metallic Li as well as LiFePO 4 cathode. The electrolyte/electrode interfaces are very stable even subjected to 4.5 V at charging state for long time. The LiFePO 4 /Li all-solid-state cells based on this electrolyte deliver high capacity, outstanding cycling stability, and superior rate capability better than those based on liquid electrolyte. This solid polymer electrolyte is eligible for next generation high energy density all-solid-state batteries.

From Cell to Module: Fabrication and Long-term Stability of Dye-sensitized Solar Cells

NASA Astrophysics Data System (ADS)

Nursam, N. M.; Hidayat, J.; Muliani, L.; Anggraeni, P. N.; Retnaningsih, L.; Idayanti, N.

2017-07-01

Dye-sensitized solar cell (DSSC), which has been firstly developed by Graetzel et al back in 1991, has attracted a considerable interest since its discovery. However, two of the main challenges that the DSSC technology will have to overcome towards commercialization involve device scale-up and long-term stability. In our group, the fabrication technology of DSSC has been developed from laboratory to module scale over the past few years, nevertheless, the long-term stability has still became a major concern. In this contribution, the long-term DSSC performance in relation to their scale-up from cell to module is investigated. The photoelectrode of the DSSCs were fabricated using nanocrystalline titanium dioxide materials that were subsequently sensitized using ruthenium-based dye. Additionally, TiCl4 pre- and post-treatment were carried out to enhance the overall device efficiency. When fabricated as cells, the DSSC prototypes showed relatively stable performance during repeated tests over three months. In order to increase the output power of the solar cells, the DSSCs were then connected in a Z-type series connection to obtain sub-module panels. The DSSC sub-modules exhibit poor stability, particularly as indicated by the significant decrease in the short circuit current (ISC ). Herein, the effect of photoelectrode and sealant materials as well as module design are investigated, highlighting their profound influence upon the DSSC efficiency and long-term stability.

High sulfur-containing carbon polysulfide polymer as a novel cathode material for lithium-sulfur battery.

PubMed

Zhang, Yiyong; Peng, Yueying; Wang, Yunhui; Li, Jiyang; Li, He; Zeng, Jing; Wang, Jing; Hwang, Bing Joe; Zhao, Jinbao

2017-09-12

The lithium-sulfur battery, which offers a high energy density and is environmental friendly, is a promising next generation of rechargeable energy storage system. However, despite these attractive attributes, the commercialization of lithium-sulfur battery is primarily hindered by the parasitic reactions between the Li metal anode and dissolved polysulfide species from the cathode during the cycling process. Herein, we synthesize the sulfur-rich carbon polysulfide polymer and demonstrate that it is a promising cathode material for high performance lithium-sulfur battery. The electrochemical studies reveal that the carbon polysulfide polymer exhibits superb reversibility and cycle stability. This is due to that the well-designed structure of the carbon polysulfide polymer has several advantages, especially, the strong chemical interaction between sulfur and the carbon framework (C-S bonds) inhibits the shuttle effect and the π electrons of the carbon polysulfide compound enhance the transfer of electrons and Li + . Furthermore, as-prepared carbon polysulfide polymer-graphene hybrid cathode achieves outstanding cycle stability and relatively high capacity. This work highlights the potential promise of the carbon polysulfide polymer as the cathode material for high performance lithium-sulfur battery.

Activity and Stability of (Pr 1-xNd x) 2NiO 4 as Cathodes for Solid Oxide Fuel Cells: II. Electrochemical Performance and Performance Durability

DOE PAGES

Dogdibegovic, Emir; Guan, Wanbing; Yan, Jingbo; ...

2016-09-21

Single phase (Pr 1-xNd x) 2NiO 4 cathode powders (x = 0, 0.25, 0.50, 0.75, and 1.0) were synthesized via a glycine-nitrate combustion and high temperature calcination. Anode supported cells were used to investigate the cathode property. A reproducible performance, within 9% for each cathode composition, was observed providing a wealth of data for quantitative studies. Area specific resistance analysis and i-V measurements between 650 and 850°C showed a decrease in the cell performance with increasing Nd content. Impedance spectrum analysis suggests that the decline in performance results from an increase in electrode polarization. While Pr 2NiO 4 cells showedmore » significant performance degradation of 6.40%/1,000 hours, the degradation rate for (Pr 0.75Nd 0.25) 2NiO 4 cells was reduced by an order of magnitude (0.56%/1,000 hours) with a 7% lower power output. Furthermore, the cathodes with a higher Nd content showed further improvement in performance stability with a marginal degradation rate of 0.06%/1,000 hours.« less

STABILIZED FEEDBACK AMPLIFIER

DOEpatents

Fishbine, H.L.; Sewell, C. Jr.

1957-08-01

Negative feedback amplifiers, and particularly a negative feedback circuit which is economical on amode power consumption, are described. Basically, the disclosed circuit comprises two tetrode tubes where the output of the first tube is capacitamce coupled to the grid of the second tube, which in turn has its plate coupled to the cathode of the first tube to form a degenerative feedback circuit. Operating potential for screen of the second tube is supplied by connecting the cathode resistor of the first tube to the screen, while the screen is by-passed to the cathode of its tube for the amplified frequencies. Also, the amplifier incorporates a circuit to stabilize the transconductance of the tubes by making the grid potential of each tube interdependent on anode currents of both lubes by voltage divider circuitry.

Thermal abuse performance of high-power 18650 Li-ion cells

NASA Astrophysics Data System (ADS)

Roth, E. P.; Doughty, D. H.

High-power 18650 Li-ion cells have been developed for hybrid electric vehicle applications as part of the DOE Advanced Technology Development (ATD) program. The thermal abuse response of two advanced chemistries (Gen1 and Gen2) were measured and compared with commercial Sony 18650 cells. Gen1 cells consisted of an MCMB graphite based anode and a LiNi 0.85Co 0.15O 2 cathode material while the Gen2 cells consisted of a MAG10 anode graphite and a LiNi 0.80Co 0.15 Al 0.05O 2 cathode. Accelerating rate calorimetry (ARC) and differential scanning calorimetry (DSC) were used to measure the thermal response and properties of the cells and cell materials up to 400 °C. The MCMB graphite was found to result in increased thermal stability of the cells due to more effective solid electrolyte interface (SEI) formation. The Al stabilized cathodes were seen to have higher peak reaction temperatures that also gave improved cell thermal response. The effects of accelerated aging on cell properties were also determined. Aging resulted in improved cell thermal stability with the anodes showing a rapid reduction in exothermic reactions while the cathodes only showed reduced reactions after more extended aging.

'Enzyme Test Bench': A biochemical application of the multi-rate modeling

NASA Astrophysics Data System (ADS)

Rachinskiy, K.; Schultze, H.; Boy, M.; Büchs, J.

2008-11-01

In the expanding field of 'white biotechnology' enzymes are frequently applied to catalyze the biochemical reaction from a resource material to a valuable product. Evolutionary designed to catalyze the metabolism in any life form, they selectively accelerate complex reactions under physiological conditions. Modern techniques, such as directed evolution, have been developed to satisfy the increasing demand on enzymes. Applying these techniques together with rational protein design, we aim at improving of enzymes' activity, selectivity and stability. To tap the full potential of these techniques, it is essential to combine them with adequate screening methods. Nowadays a great number of high throughput colorimetric and fluorescent enzyme assays are applied to measure the initial enzyme activity with high throughput. However, the prediction of enzyme long term stability within short experiments is still a challenge. A new high throughput technique for enzyme characterization with specific attention to the long term stability, called 'Enzyme Test Bench', is presented. The concept of the Enzyme Test Bench consists of short term enzyme tests conducted under partly extreme conditions to predict the enzyme long term stability under moderate conditions. The technique is based on the mathematical modeling of temperature dependent enzyme activation and deactivation. Adapting the temperature profiles in sequential experiments by optimum non-linear experimental design, the long term deactivation effects can be purposefully accelerated and detected within hours. During the experiment the enzyme activity is measured online to estimate the model parameters from the obtained data. Thus, the enzyme activity and long term stability can be calculated as a function of temperature. The results of the characterization, based on micro liter format experiments of hours, are in good agreement with the results of long term experiments in 1L format. Thus, the new technique allows for both: the enzyme screening with regard to the long term stability and the choice of the optimal process temperature. The presented article gives a successful example for the application of multi-rate modeling, experimental design and parameter estimation within biochemical engineering. At the same time, it shows the limitations of the methods at the state of the art and addresses the current problems to the applied mathematics community.

Long-Term Cr Poisoning Effect on LSCF-GDC Composite Cathodes Sintered at Different Temperatures

DOE PAGES

Xiong, Chunyan; Taillon, Joshua A.; Pellegrinelli, Christopher; ...

2016-07-19

Here, the impact of sintering temperature on Cr-poisoning of solid oxide fuel cell (SOFC) cathodes was systematically studied. La 0.6Sr 0.4Fe 0.8Co 0.2O 3-δ - Ce 0.9Gd 0.1O 2-δ symmetric cells were aged at 750°C in synthetic air with the presence of Crofer 22 APU, a common high temperature interconnect, over 200 hours and electrochemical impedance spectroscopy (EIS) was used to determine the degradation process. Both the ohmic resistance (R Ω) and polarization resistance (R P) of LSCF-GDC cells, extracted from EIS spectra, for different sintering temperatures increase as a function of aging time. Furthermore, the Cr-related degradation rate increasesmore » with decreased cathode sintering temperature. The polarization resistance of cathode sintered at lower temperature (950°C) increases dramatically while aging with the presence of Cr and also significantly decreases the oxygen partial pressure dependence after aging. The degradation rate shows a positive correlation to the concentration of Cr. The results indicate that decreased sintering temperature increases the total surface area, leading to more available sites for Sr-Cr-O nucleation and thus greater Cr degradation.« less

Sea water magnesium fuel cell power supply

NASA Astrophysics Data System (ADS)

Hahn, Robert; Mainert, Jan; Glaw, Fabian; Lang, K.-D.

2015-08-01

An environmentally friendly magnesium fuel cell system using seawater electrolyte and atmospheric oxygen was tested under practical considerations for use as maritime power supply. The hydrogen rate and therefore the power density of the system were increased by a factor of two by using hydrogen evolution cathodes with a gas separation membrane instead of submerged cathodes without gas separation. Commercial magnesium AZ31 rolled sheet anodes can be dissolved in seawater for hydrogen production, down to a thickness below 100 μm thickness, resulting in hydrogen generation efficiency of the anode of over 80%. A practical specific energy/energy density of the alloy of more than 1200 Wh/kg/3000 Wh/l was achieved when coupled to a fuel cell with atmospheric air breathing cathode. The performance of several AZ31 alloy anodes was tested as well as the influence of temperature, electrolyte concentration and anode - cathode separation. The excess hydrogen produced by the magnesium hydrogen evolving cell, due to the negative difference effect, is proportional to the cell current in case of the AZ31 alloys, which simplifies system control considerably. Stable long-term operation of the system was demonstrated at low pressures which can be maintained in an open-seawater-submerged hydrogen generator.

Evaluation of Cation Migration in Lanthanum Strontium Cobalt Ferrite Solid Oxide Fuel Cell Cathodes via In-operando X-ray Diffraction

DOE Office of Scientific and Technical Information (OSTI.GOV)

Hardy, John S.; Coyle, Christopher A.; Bonnett, Jeff F.

2018-01-28

Anode-supported SOFCs with LSCF-6428 cathodes were operated at various temperatures for hundreds of hours in dry or humid (~3% water) cathode air with continuous cathode XRD. Additionally, one cell in dry air was held at OCV and another had 12% CO2 added to the humid air. Long cumulative XRD count times allowed identification of minor phases at <0.1 wt%. In humid air, performance improved during the first couple of hundred hours and Fe-rich Fe,Co spinel XRD peaks gradually shifted to lower angles while nano-nodules formed on LSCF surfaces. With 12% CO2 added, performance degraded after initial activation, unlike without CO2,more » where stability followed activation. In CO2, LSCF XRD peaks shifted indicating gradual decomposition. In dry air, fast initial degradation that decelerated over time occurred at constant current while the cell at OCV was stable. At OCV and 750°C or at constant current and 700°C in dry air, Fe-rich spinel XRD peaks shifted more slowly than in humid air tests; Co-rich Fe,Co spinel peaks shifted to higher angles; and SEM discovered smaller nano-nodules on LSCF than after humid air tests. At constant current at 750°C and 800°C in dry air, no nano-nodules or gradual changes in the XRD patterns were discovered.« less

Stabilizing platinum in phosphoric acid fuel cells

NASA Technical Reports Server (NTRS)

Remick, R. J.

1982-01-01

Platinum sintering on phosphoric acid fuel cell cathodes is discussed. The cathode of the phosphoric acid fuel cell uses a high surface area platinum catalyst dispersed on a conductive carbon support to minimize both cathode polarization and fabrication costs. During operation, however, the active surface area of these electrodes decreases, which in turn leads to decreased cell performance. This loss of active surface area is a major factor in the degradation of fuel cell performance over time.

Stability of Electrons in the Virtual Cathode Region of an IEC

NASA Astrophysics Data System (ADS)

Kim, Hyng-Jin; Miley, George; Momota, Hiromu

2003-04-01

In the Inertial Electrostatic Confinement (IEC) device, electrons are confined inside a virtual anode that in turn confines ions. Prior stability studies [1, 2] have considered systems in which one species is electrostatically confined by the other, and either or both species are out of local thermal equilibrium. In the present research, electron stability in the virtual cathode region of an ion injected IEC is being studied. The ion density in an IEC is non-uniform due to the radial electrostatic potential, and increases toward the center region. The potential near the virtual cathode is assumed to have a parabolic shape and is determined assuming that the net space charge density is constant in that region. The corresponding ion distribution function is assumed to have the form f = C [sigma] (H W) /L^0.5 and the electron response is taken to be diabatic. Then using a variational principle after linearizing the hydrodynamic equations, stability properties of the electron layer are determined. Results will be presented as a function of injected ion/electron current ratios. 1. L. Chacon and D. C. Barnes, Phys. Plasma 7, 4774 (2000). 2. D. C. Barnes, L. Chacon, and J. M. Finn, Phys. Plasmas 9, 4448 (2002).

Effects of binders on the electrochemical performance of rechargeable magnesium batteries

NASA Astrophysics Data System (ADS)

Wang, Nan; NuLi, Yanna; Su, Shuojian; Yang, Jun; Wang, Jiulin

2017-02-01

A comparative study on the effects of different binders on the electrochemical performance of rechargeable magnesium batteries with Mo6S8 cathode is conducted for the first time. The selected binders are commercial organic-soluble polyvinylidene fluoride (PVDF), water-soluble poly(acrylic acid) (PAA), poly(vinyl alcohol) (PVA), gelatin, sodium alginate (SA) and Beta-cyclodextrin (β-CD). The binders significantly affect the physical properties, thus the electrochemical performance of Mo6S8 cathode. Compared with those using traditional PVDF binder, Mo6S8 electrodes with PAA and PVA exhibit enhanced cycling stabilities and rate capabilities, which are attributed to the improved cohesion among the electrode constituents and adhesion between the electrode laminate and the current collector. In addition, the anodic stability of these binders is not only related to the chemical structure of binders, but also to the uniformity of electrode surface. SA binder shows low anodic stability duo to containing easily oxidized groups. Non-uniform electrode surface decreases the anodic stability of PVDF based Mo6S8 electrode. Gelatin can be used as a binder in the formulation of high voltage cathodes for rechargeable magnesium batteries.

Limitations and possibilities of green synthesis and long-term stability of colloidal Ag nanoparticles

NASA Astrophysics Data System (ADS)

Velgosová, Oksana; Mražíková, Anna

2017-12-01

In this paper the influence of algae life cycle and the solutions pH on the green synthesis of colloidal Ag nanoparticles (AgNPs) as well as effect of different storage conditions on AgNPs long-term stability was investigated. Silver nanoparticles were biologically synthesized using extracts of Parachlorella kessleri algae cultivated 1, 2, 3 and 4 weeks. The formation of AgNPs was monitored using a UV-vis spectrophotometer and verified by TEM observation. The results confirmed formation of polyhedron and/or near polyhedron AgNPs, ranging between 5 and 60 nm in diameter. The age of algae influenced the synthesis rate and an amount of AgNPs in solution. The best results were obtained using tree weeks old algae. UV-vis analysis and TEM observation also revealed that the size and the stability of AgNPs depend on the pH of solution. AgNPs formed in solutions of higher pH (8 and 10) are polyhedron, fine, with narrow size interval and stabile. Nanoparticles formed in solutions of low pH (2, 4 and 6) started to lose their stability on 10th day of experiment, and the particle size interval was wide. The long-term stability of AgNPs can be influenced by light and temperature conditions. The most significant stability loss was observed at day light and room temperature (21°C). After 200-days significant amount of agglomerated particles settled on the bottom of the Erlenmeyer flask. AgNPs stored at dark and room temperature showed better long-term stability, weak particles agglomeration was observed. AgNPs stored at dark and at temperature 5°C showed the best long-term stability. Such AgNPs remained spherical, fine (5-20 nm), with narrow size interval and stable (no agglomeration) even after more than six months.

In situ probing of the active site geometry of ultrathin nanowires for the oxygen reduction reaction

DOE PAGES

Liu, Haiqing; Wong, Stanislaus S.; An, Wei; ...

2015-09-24

To create truly effective electrocatalysts for the cathodic reaction governing proton exchange membrane fuel cells (PEMFC), namely the oxygen reduction reaction (ORR), necessitates an accurate and detailed structural understanding of these electrocatalysts, especially at the nanoscale, and to precisely correlate that structure with demonstrable performance enhancement. To address this key issue, we have combined and interwoven theoretical calculations with experimental, spectroscopic observations in order to acquire useful structural insights into the active site geometry with implications for designing optimized nanoscale electrocatalysts with rationally predicted properties. Specifically, we have probed ultrathin (~2 nm) core–shell Pt~Pd 9Au nanowires, which have been previouslymore » shown to be excellent candidates for ORR in terms of both activity and long-term stability, from the complementary perspectives of both DFT calculations and X-ray absorption spectroscopy (XAS). The combination and correlation of data from both experimental and theoretical studies has revealed for the first time that the catalytically active structure of our ternary nanowires can actually be ascribed to a PtAu~Pd configuration, comprising a PtAu binary shell and a pure inner Pd core. Moreover, we have plausibly attributed the resulting structure to a specific synthesis step, namely the Cu underpotential deposition (UPD) followed by galvanic replacement with Pt. Thus, the fundamental insights gained into the performance of our ultrathin nanowires from our demonstrated approach will likely guide future directed efforts aimed at broadly improving upon the durability and stability of nanoscale electrocatalysts in general.« less

A frequency-stabilized light source at 399 nm using an Yb hollow-cathode lamp

NASA Astrophysics Data System (ADS)

Tanabe, Takehiko; Akamatsu, Daisuke; Inaba, Hajime; Okubo, Sho; Kobayashi, Takumi; Yasuda, Masami; Hosaka, Kazumoto; Hong, Feng-Lei

2018-06-01

We demonstrate a diode laser system operating at 399 nm that is stabilized to the 6s2 1S0–6s6p 1P1 electric dipole transition in ytterbium (Yb) atoms in a hollow-cathode lamp. The frequency stability of the laser reached 1.1 × 10‑11 at an averaging time of τ = 1 s. We performed an absolute frequency measurement using an optical frequency comb and determined that the absolute frequency of the laser stabilized to the 1S0–1P1 transition in 174Yb was 751 526 522.26(9) MHz. We also investigated several systematic frequency shifts while changing some of the light source parameters and measured several isotope shifts. The measured laser frequency will provide useful information regarding the practical use of the frequency-stabilized light source at 399 nm.

Cu2+ Dual-Doped Layer-Tunnel Hybrid Na0.6Mn1- xCu xO2 as a Cathode of Sodium-Ion Battery with Enhanced Structure Stability, Electrochemical Property, and Air Stability.

PubMed

Chen, Ting-Ru; Sheng, Tian; Wu, Zhen-Guo; Li, Jun-Tao; Wang, En-Hui; Wu, Chun-Jin; Li, Hong-Tai; Guo, Xiao-Dong; Zhong, Ben-He; Huang, Ling; Sun, Shi-Gang

2018-03-28

Sodium-ion batteries (SIBs) have been regarded as a promising candidate for large-scale renewable energy storage system. Layered manganese oxide cathode possesses the advantages of high energy density, low cost and natural abundance while suffering from limited cycling life and poor rate capacity. To overcome these weaknesses, layer-tunnel hybrid material was developed and served as the cathode of SIB, which integrated high capacity, superior cycle ability, and rate performance. In the current work, the doping of copper was adopted to suppress the Jahn-Teller effect of Mn 3+ and to affect relevant structural parameters. Multifunctions of the Cu 2+ doping were carefully investigated. It was found that the structure component ratio is varied with the Cu 2+ doping amount. Results demonstrated that Na + /vacancy rearrangement and phase transitions were suppressed during cycling without sacrificing the reversible capacity and enhanced electrochemical performances evidenced with 96 mA h g -1 retained after 250 cycles at 4 C and 85 mA h g -1 at 8 C. Furthermore, ex situ X-ray diffraction has demonstrated high reversibility of the Na 0.6 Mn 0.9 Cu 0.1 O 2 cathode during Na + extraction/insertion processes and superior air stability that results in better storage properties. This study reveals that the Cu 2+ doping could be an effective strategy to tune the properties and related performances of Mn-based layer-tunnel hybrid cathode.

A high-rate and long cycle life aqueous electrolyte battery for grid-scale energy storage.

PubMed

Pasta, Mauro; Wessells, Colin D; Huggins, Robert A; Cui, Yi

2012-01-01

New types of energy storage are needed in conjunction with the deployment of solar, wind and other volatile renewable energy sources and their integration with the electric grid. No existing energy storage technology can economically provide the power, cycle life and energy efficiency needed to respond to the costly short-term transients that arise from renewables and other aspects of grid operation. Here we demonstrate a new type of safe, fast, inexpensive, long-life aqueous electrolyte battery, which relies on the insertion of potassium ions into a copper hexacyanoferrate cathode and a novel activated carbon/polypyrrole hybrid anode. The cathode reacts rapidly with very little hysteresis. The hybrid anode uses an electrochemically active additive to tune its potential. This high-rate, high-efficiency cell has a 95% round-trip energy efficiency when cycled at a 5C rate, and a 79% energy efficiency at 50C. It also has zero-capacity loss after 1,000 deep-discharge cycles.

In Vivo Integrity and Biological Fate of Chelator-Free Zirconium-89-Labeled Mesoporous Silica Nanoparticles

PubMed Central

2015-01-01

Traditional chelator-based radio-labeled nanoparticles and positron emission tomography (PET) imaging are playing vital roles in the field of nano-oncology. However, their long-term in vivo integrity and potential mismatch of the biodistribution patterns between nanoparticles and radio-isotopes are two major concerns for this approach. Here, we present a chelator-free zirconium-89 (89Zr, t1/2 = 78.4 h) labeling of mesoporous silica nanoparticle (MSN) with significantly enhanced in vivo long-term (>20 days) stability. Successful radio-labeling and in vivo stability are demonstrated to be highly dependent on both the concentration and location of deprotonated silanol groups (−Si–O–) from two types of silica nanoparticles investigated. This work reports 89Zr-labeled MSN with a detailed labeling mechanism investigation and long-term stability study. With its attractive radio-stability and the simplicity of chelator-free radio-labeling, 89Zr-MSN offers a novel, simple, and accurate way for studying the in vivo long-term fate and PET image-guided drug delivery of MSN in the near future. PMID:26213260

In Vivo Integrity and Biological Fate of Chelator-Free Zirconium-89-Labeled Mesoporous Silica Nanoparticles.

PubMed

Chen, Feng; Goel, Shreya; Valdovinos, Hector F; Luo, Haiming; Hernandez, Reinier; Barnhart, Todd E; Cai, Weibo

2015-08-25

Traditional chelator-based radio-labeled nanoparticles and positron emission tomography (PET) imaging are playing vital roles in the field of nano-oncology. However, their long-term in vivo integrity and potential mismatch of the biodistribution patterns between nanoparticles and radio-isotopes are two major concerns for this approach. Here, we present a chelator-free zirconium-89 ((89)Zr, t1/2 = 78.4 h) labeling of mesoporous silica nanoparticle (MSN) with significantly enhanced in vivo long-term (>20 days) stability. Successful radio-labeling and in vivo stability are demonstrated to be highly dependent on both the concentration and location of deprotonated silanol groups (-Si-O(-)) from two types of silica nanoparticles investigated. This work reports (89)Zr-labeled MSN with a detailed labeling mechanism investigation and long-term stability study. With its attractive radio-stability and the simplicity of chelator-free radio-labeling, (89)Zr-MSN offers a novel, simple, and accurate way for studying the in vivo long-term fate and PET image-guided drug delivery of MSN in the near future.

Endurance testing of downstream cathodes on a low-power MPD thruster

NASA Technical Reports Server (NTRS)

Burkhart, J. A.; Rose, J. R.

1974-01-01

A low-power MPD thruster with downstream cathode was tested for endurance with a series of hollow cathode designs. Failure modes and failure mechanisms were identified. A new hollow cathode (with rod inserts) has emerged which shows promise for long life. The downstream positioning of the cathode was also changed from an on-axis location to an off-axis location. Data are presented for a 1332-hour life test of this new hollow cathode located at the new off-axis location. Xenon propellant was used.

High performance and durability of order-structured cathode catalyst layer based on TiO2@PANI core-shell nanowire arrays

NASA Astrophysics Data System (ADS)

Chen, Ming; Wang, Meng; Yang, Zhaoyi; Wang, Xindong

2017-06-01

In this paper, an order-structured cathode catalyst layer consisting of Pt-TiO2@PANI core-shell nanowire arrays that in situ grown on commercial gas diffusion layer (GDL) are prepared and applied to membrane electrode assembly (MEA) of proton exchange membrane fuel cell (PEMFC). In order to prepare the TiO2@PANI core-shell nanowire arrays with suitable porosity and prominent conductivity, the morphologies of the TiO2 nanoarray and electrochemical polymerization process of aniline are schematically investigated. The MEA with order-structured cathode catalyst layer is assembled in the single cell to evaluate the electrochemical performance and durability of PEMFC. As a result, the PEMFC with order-structured cathode catalyst layer shows higher peak power density (773.54 mW cm-2) than conventional PEMFC (699.30 mW cm-2). Electrochemically active surface area (ECSA) and charge transfer impedance (Rct) are measured before and after accelerated degradation test (ADT), and the corresponding experimental results indicate the novel cathode structure exhibits a better stability with respect to conventional cathode. The enhanced electrochemical performance and durability toward PEMFC can be ascribed to the order-structured cathode nanoarray structure with high specific surface area increases the utilization of catalyst and reduces the tortuosity of transport pathways, and the synergistic effect between TiO2@PANI support and Pt nanoparticles promotes the high efficiency of electrochemical reaction and improves the stability of catalyst. This research provides a facile and controllable method to prepare order-structured membrane electrode with lower Pt loading for PEMFC in the future.

Stability of Chronic Hepatitis-Related Parameters in Serum Samples After Long-Term Storage.

PubMed

Yu, Rentao; Dan, Yunjie; Xiang, Xiaomei; Zhou, Yi; Kuang, Xuemei; Yang, Ge; Tang, Yulan; Liu, Mingdong; Kong, Weilong; Tan, Wenting; Deng, Guohong

2017-06-01

Serum samples are widely used in clinical research, but a comprehensive research of the stability of parameters relevant to chronic hepatitis and the effect of a relatively long-term (up to 10 years) storage on the stability have rarely been studied. To investigate the stability of chronic hepatitis-related parameters in serum samples after long-term storage. The storage stability of common clinical parameters such as total bile acid (TBA), total bilirubin (TBIL), potassium, cholesterol, and protein parameters such as alanine aminotransferase (ALT), creatine kinase (CK), γ-glutamyltransferase (GGT), albumin, high-density lipoprotein (HDL) and also hepatitis B virus (HBV) DNA, hepatitis C virus (HCV) RNA, hepatitis B surface antigen (HBsAg), and chemokine (C-X-C motif) ligand 10 (CXCL10) were tested in serum samples after storing at -20°C or -70°C for 1, 2, 3, 7, 8, and 10 years. Levels of TBA, TBIL, and protein parameters such as ALT, CK, GGT, HDL, and HBsAg decreased significantly, but levels of potassium and cholesterol increased significantly after long-term storage, whereas blood glucose and triglycerides were stable during storage. HBV DNA remained stable at -70°C but changed at -20°C, whereas HCV RNA was stable after 1-, 2-, and 3-year storage. CXCL10 was still detectable after 8-year storage. Low temperatures (-70°C/80°C) are necessary for storage of serum samples in chronic hepatitis B research after long-term storage.

Organic light emitting diodes with structured electrodes

DOEpatents

Mao, Samuel S.; Liu, Gao; Johnson, Stephen G.

2012-12-04

A cathode that contain nanostructures that extend into the organic layer of an OLED has been described. The cathode can have an array of nanotubes or a layer of nanoclusters extending out from its surface. In another arrangement, the cathode is patterned and etched to form protruding nanostructures using a standard lithographic process. Various methods for fabricating these structures are provided, all of which are compatible with large-scale manufacturing. OLEDs made with these novel electrodes have greatly enhanced electron injection, have good environmental stability.

Carbon with hierarchical pores from carbonized metal-organic frameworks for lithium sulphur batteries.

PubMed

Xi, Kai; Cao, Shuai; Peng, Xiaoyu; Ducati, Caterina; Kumar, R Vasant; Cheetham, Anthony K

2013-03-18

This paper presents a novel method and rationale for utilizing carbonized MOFs for sulphur loading to fabricate cathode structures for lithium-sulphur batteries. Unique carbon materials with differing hierarchical pore structures were synthesized from four types of zinc-containing metal-organic frameworks (MOFs). It is found that cathode materials made from MOFs-derived carbons with higher mesopore (2-50 nm) volumes exhibit increased initial discharge capacities, whereas carbons with higher micropore (<2 nm) volumes lead to cathode materials with better cycle stability.

A study to assess the long-term stability of the ionization chamber reference system in the LNMRI

NASA Astrophysics Data System (ADS)

Trindade Filho, O. L.; Conceição, D. A.; da Silva, C. J.; Delgado, J. U.; de Oliveira, A. E.; Iwahara, A.; Tauhata, L.

2018-03-01

Ionization chambers are used as secondary standard in order to maintain the calibration factors of radionuclides in the activity measurements in metrology laboratories. Used as radionuclide calibrator in nuclear medicine clinics to control dose in patients, its long-term performance is not evaluated systematically. A methodology for long-term evaluation for its stability is monitored and checked. Historical data produced monthly of 2012 until 2017, by an ionization chamber, electrometer and 226Ra, were analyzed via control chart, aiming to follow the long-term performance. Monitoring systematic errors were consistent within the limits of control, demonstrating the quality of measurements in compliance with ISO17025.

Electrochemical study of highly durable cathode with Pt supported on ITO-CNT composite for proton exchange membrane fuel cells

DOE Office of Scientific and Technical Information (OSTI.GOV)

Park, Sehkyu; Shao, Yuyan; Viswanathan, Vilayanur V.

2016-10-01

In this paper, we describe a highly stable cathode containing a Pt catalyst supported on an indium tin oxide (ITO) and carbon nanotube (CNT) composite. The dependence of cathode performance and durability on the ITO content and the diameter of the CNTs were investigated by electrochemical techniques. The cathode with 30 wt% ITO and CNTs with diameters 10–20 nm in the composite offered preferred locations for Pt stabilization and was very resistant to carbon corrosion (i.e., 82.7% ESA retention and 105.7% mass activity retention after an accelerated stress test for 400 h).

Rational Design of Statically and Dynamically Stable Lithium-Sulfur Batteries with High Sulfur Loading and Low Electrolyte/Sulfur Ratio.

PubMed

Chung, Sheng-Heng; Manthiram, Arumugam

2018-02-01

The primary challenge with lithium-sulfur battery research is the design of sulfur cathodes that exhibit high electrochemical efficiency and stability while keeping the sulfur content and loading high and the electrolyte/sulfur ratio low. With a systematic investigation, a novel graphene/cotton-carbon cathode is presented here that enables sulfur loading and content as high as 46 mg cm -2 and 70 wt% with an electrolyte/sulfur ratio of as low as only 5. The graphene/cotton-carbon cathodes deliver peak capacities of 926 and 765 mA h g -1 , respectively, at C/10 and C/5 rates, which translate into high areal, gravimetric, and volumetric capacities of, respectively, 43 and 35 mA h cm -2 , 648 and 536 mA h g -1 , and 1067 and 881 mA h cm -3 with a stable cyclability. They also exhibit superior cell-storage capability with 95% capacity-retention, a low self-discharge constant of just 0.0012 per day, and stable poststorage cyclability after storing over a long period of six months. This work demonstrates a viable approach to develop lithium-sulfur batteries with practical energy densities exceeding that of lithium-ion batteries. © 2017 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

High-performance spinel-rich Li1.5MnTiO4+δ ultralong nanofibers as cathode materials for Li-ion batteries

NASA Astrophysics Data System (ADS)

Hung Vu, Ngoc; Arunkumar, Paulraj; Bin Im, Won

2017-03-01

Recently, composite materials based on Li-Mn-Ti-O system were developed to target low cost and environmentally benign cathodes for Li-ion batteries. The spinel-layered Li1.5MnTiO4+δ bulk particles showed excellent cycle stability but poor rate performance. To address this drawback, ultralong nanofibers of a Li1.5MnTiO4+δ spinel-layered heterostructure were synthesized by electrospinning. Uniform nanofibers with diameters of about 80 nm were formed of tiny octahedral particles wrapped together into 30 μm long fibers. The Li1.5MnTiO4+δ nanofibers exhibited an improved rate capability compared to both Li1.5MnTiO4+δ nanoparticles and bulk particles. The uniform one-dimensional nanostructure of the composite cathode exhibited enhanced capacities of 235 and 170 mAh g-1 at C/5 and 1 C rates, respectively. Its unique structure provided a large effective contact area for Li+ diffusion, and low charge transfer resistance. Moreover, the layered phase contributed to its capacity in over 3 V region, which increased specific energy (726 Wh kg-1) compared to the bulk particles (534 Wh kg-1).

Interfacial Engineering of Perovskite Solar Cells by Employing a Hydrophobic Copper Phthalocyanine Derivative as Hole-Transporting Material with Improved Performance and Stability.

PubMed

Jiang, Xiaoqing; Yu, Ze; Lai, Jianbo; Zhang, Yuchen; Hu, Maowei; Lei, Ning; Wang, Dongping; Yang, Xichuan; Sun, Licheng

2017-04-22

In high-performance perovskite solar cells (PSCs), hole-transporting materials (HTMs) play an important role in extracting and transporting the photo-generated holes from the perovskite absorber to the cathode, thus reducing unwanted recombination losses and enhancing the photovoltaic performance. Herein, solution-processable tetra-4-(bis(4-tert-butylphenyl)amino)phenoxy-substituted copper phthalocyanine (CuPc-OTPAtBu) was synthesized and explored as a HTM in PSCs. The optical, electrochemical, and thermal properties were fully characterized for this organic metal complex. The photovoltaic performance of PSCs employing this CuPc derivative as a HTM was further investigated, in combination with a mixed-ion perovskite as a light absorber and a low-cost vacuum-free carbon as cathode. The optimized devices [doped with 6 % (w/w) tetrafluoro-tetracyano-quinodimethane (F4TCNQ)] showed a decent power conversion efficiency of 15.0 %, with an open-circuit voltage of 1.01 V, a short-circuit current density of 21.9 mA cm -2 , and a fill factor of 0.68. Notably, the PSC devices studied also exhibited excellent long-term durability under ambient condition for 720 h, mainly owing to the introduction of the hydrophobic HTM interlayer, which prevents moisture penetration into the perovskite film. The present work emphasizes that solution-processable CuPc holds a great promise as a class of alternative HTMs that can be further explored for efficient and stable PSCs in the future. © 2017 Wiley-VCH Verlag GmbH & Co. KGaA, Weinheim.

Atomistic Modeling of Cation Diffusion in Transition Metal Perovskites La1-xSrxMnO3+/-δfor Solid Oxide Fuel Cell Cathodes Applications

NASA Astrophysics Data System (ADS)

Lee, Yueh-Lin; Duan, Yuhua; Morgan, Dane; Sorescu, Dan; Abernathy, Harry

Cation diffusion in La1-xSrxMnO3+/-δ (LSM) and in related perovskite materials play an important role in controlling long term performance and stability of solid oxide fuel cell (SOFCs) cathodes. Due to sluggish rates of cation diffusion and complex coupling between defect chemistry and cation diffusion pathways, currently there is still lack of quantitative theoretical model predictions on cation diffusivity vs. T and P(O2) to describe experimental cation tracer diffusivities. In this work, based on ab initio modeling of LSM defect chemistry and migration barriers of the possible cation diffusion pathways, we assess the rates of A-site and B-site cation diffusion in a wide range of T and P(O2) at x =0.0 and 0.2 for SOFC applications. We demonstrate the active cation diffusion pathways in LSM involve cation defect clusters as cation transport carriers, where reduction in the cation migration barriers, which are governed by the steric effect associated with the metal-oxygen cage in the perovskite lattice, is much greater than the penalty of repulsive interaction in the A-site and B-site cation vacancy clusters, leading to higher cation diffusion rates as compared to those of single cation vacancy hopping mechanisms. The predicted Mn and La/Sr cation self-diffusion coefficients of LSM at at x =0.0 and 0.2 along with their 1/T and P(O2) dependences, are in good agreement with the experimental tracer diffusion coefficients.

Characterization of a High Current, Long Life Hollow Cathode

NASA Technical Reports Server (NTRS)

VanNoord, Jonathan L.; Kamhawi, Hani; McEwen, Heather K.

2006-01-01

The advent of higher power spacecraft makes it desirable to use higher power electric propulsion thrusters such as ion thrusters or Hall thrusters. Higher power thrusters require cathodes that are capable of producing higher currents. One application of these higher power spacecraft is deep-space missions that require tens of thousands of hours of operation. This paper presents the approach used to design a high current, long life hollow cathode assembly for that application, along with test results from the corresponding hollow cathode. The design approach used for the candidate hollow cathode was to reduce the temperature gradient in the insert, yielding a lower peak temperature and allowing current to be produced more uniformly along the insert. The lower temperatures result in a hollow cathode with increased life. The hollow cathode designed was successfully operated at currents from 10 to 60 A with flow rates of 5 to 19 sccm with a maximum orifice temperature measured of 1100 C. Data including discharge voltage, keeper voltage, discharge current, flow rates, and orifice plate temperatures are presented.

Design, construction and long life endurance testing of cathode assemblies for use in microwave high-power transmitting tubes

NASA Technical Reports Server (NTRS)

Batra, R.; Marino, D.

1986-01-01

The cathode life test program sponsored by NASA Lewis Research Center at Watkins-Johnson Company has been in continuous operation since 1972. Its primary objective has been to evaluate the long life capability of barium dispenser cathodes to produce emission current densities of 2 A sq. cm. or more in an operational environment simulating that of a highpower microwave tube. The life test vehicles were equipped with convergent flow electron guns, drift space tubes with solenoid magnets for electron beam confinement and water-cooled depressed collectors. A variety of cathode types has been tested, including GE Tungstate, Litton Impregnated, Philips Type B and M, Semicon types S and M, and Spectra-Mat Type M. Recent emphasis has been on monitoring the performance of Philips Type M cathodes at 2 A sq. cm. and Sprectra-Mat and Semicon Type M cathodes at 4 A sq. cm. These cathodes have been operated at a constant current of 616 mA and a cathode anode voltage on the order of 10 kV. Cathode temperatures were maintained at 1010 C true as measured from black body holes in the backs of the cathodes. This report presents results of the cathode life test program from July l982 through April l986. The results include hours of operation and performance data in the form of normalized emission current density versus temperature curves (Miram plots).

Competitive migration behaviors of multiple ions and their impacts on ion-exchange resin packed microbial desalination cell.

PubMed

Zuo, Kuichang; Yuan, Lulu; Wei, Jincheng; Liang, Peng; Huang, Xia

2013-10-01

Mixed ion-exchange resins packed microbial desalination cell (R-MDC) could stabilize the internal resistance, however, the impacts of multiple ions on R-MDC performance was unclear. This study investigated the desalination performance, multiple ions migration behaviors and their impacts on R-MDCs fed with salt solution containing multiple anions and cations. Results showed that R-MDC removed multiple anions better than multiple cations with desalination efficiency of 99% (effluent conductivity <0.05 ms/cm) at hydraulic retention time of 50 h. Competitive migration order was SO4(2-)>NO3(-)>Cl(-) for anions and Ca(2+)≈Mg(2+)>NH4(+)>Na(+) for cations, jointly affected by both their molar conductivity and exchange selectivity on resins. After long-term operation, the existence of higher concentration Ca(2+) and Mg(2+) caused the electric conductivity of mixed resins decrease and scaling on the surface of cation-exchange membrane adjoined with cathode chamber, suggesting that R-MDC would be more suitable for desalination of water with lower hardness. Copyright © 2013 Elsevier Ltd. All rights reserved.

Surface-oxidized cobalt phosphide used as high efficient electrocatalyst in activated carbon air-cathode microbial fuel cell

NASA Astrophysics Data System (ADS)

Yang, Tingting; Wang, Zhong; Li, Kexun; Liu, Yi; Liu, Di; Wang, Junjie

2017-09-01

Herein, we report a simplistic method to fabricate the surface-oxidized cobalt phosphide (CoP) nanocrystals (NCs), which is used as electrocatalyst for oxygen reduction reaction (ORR) in microbial fuel cell (MFC) for the first time. The corallite-like CoP NCs are successfully prepared by a hydrothermal reaction following a phosphating treatment in N2 atmosphere. When used as an ORR catalyst, cobalt phosphide shows comparable onset potential, inferior resistance, as well as a small Tafel slope with long-term stability in neutral media. The maximum power density of MFC embellished with 10% CoP reached 1914.4 ± 59.7 mW m-2, which is 108.5% higher than the control. The four-electron pathway, observed by the RDE, plays a crucial role in electrochemical catalytic activity. In addition, material characterizations indicate that the surface oxide layer (CoOx) around the metallic CoP core is important and beneficial for ORR. Accordingly, it can be expected that the as-synthesized CoP will be a promising candidate of the non-precious metal ORR electrocatalysts for electrochemical energy applications.

The Effect of a Short-Term and Long-Term Whole-Body Vibration in Healthy Men upon the Postural Stability

PubMed Central

Piecha, Magdalena; Juras, Grzegorz; Król, Piotr; Sobota, Grzegorz; Polak, Anna; Bacik, Bogdan

2014-01-01

The study aimed to establish the short-term and long-term effects of whole-body vibration on postural stability. The sample consisted of 28 male subjects randomly allocated to four comparative groups, three of which exercised on a vibration platform with parameters set individually for the groups. The stabilographic signal was recorded before the test commenced, after a single session of whole-body vibration, immediately after the last set of exercises of the 4-week whole-body vibration training, and one week after the training ended. The subjects were exposed to vibrations 3 times a week for 4 weeks. Long-term vibration training significantly shortened the rambling and trembling paths in the frontal plane. The path lengths were significantly reduced in the frontal plane one week after the training end date. Most changes in the values of the center of pressure (COP) path lengths in the sagittal and frontal plane were statistically insignificant. We concluded that long-term vibration training improves the postural stability of young healthy individuals in the frontal plane. PMID:24520362

ESTABLISHING SUSTAINABLE US HEV/PHEV MANUFACTURING BASE: STABILIZED LITHIUM METAL POWDER, ENABLING MATERIAL AND REVOLUTIONARY TECHNOLOGY FOR HIGH ENERGY LI-ION BATTERIES

DOE Office of Scientific and Technical Information (OSTI.GOV)

Yakovleva, Marina

2012-12-31

FMC Lithium Division has successfully completed the project “Establishing Sustainable US PHEV/EV Manufacturing Base: Stabilized Lithium Metal Powder, Enabling Material and Revolutionary Technology for High Energy Li-ion Batteries”. The project included design, acquisition and process development for the production scale units to 1) produce stabilized lithium dispersions in oil medium, 2) to produce dry stabilized lithium metal powders, 3) to evaluate, design and acquire pilot-scale unit for alternative production technology to further decrease the cost, and 4) to demonstrate concepts for integrating SLMP technology into the Li- ion batteries to increase energy density. It is very difficult to satisfy safety,more » cost and performance requirements for the PHEV and EV applications. As the initial step in SLMP Technology introduction, industry can use commercially available LiMn2O4 or LiFePO4, for example, that are the only proven safer and cheaper lithium providing cathodes available on the market. Unfortunately, these cathodes alone are inferior to the energy density of the conventional LiCoO2 cathode and, even when paired with the advanced anode materials, such as silicon composite material, the resulting cell will still not meet the energy density requirements. We have demonstrated, however, if SLMP Technology is used to compensate for the irreversible capacity in the anode, the efficiency of the cathode utilization will be improved and the cost of the cell, based on the materials, will decrease.« less

Nanoprocess and nanoscale surface functionalization on cathode materials for advanced lithium-ion batteries.

PubMed

Alaboina, Pankaj Kumar; Uddin, Md-Jamal; Cho, Sung-Jin

2017-10-26

Nanotechnology-driven development of cathode materials is an essential part to revolutionize the evolution of the next generation lithium ion batteries. With the progress of nanoprocess and nanoscale surface modification investigations on cathode materials in recent years, the advanced battery technology future seems very promising - Thanks to nanotechnology. In this review, an overview of promising nanoscale surface deposition methods and their significance in surface functionalization on cathodes is extensively summarized. Surface modified cathodes are provided with a protective layer to overcome the electrochemical performance limitations related to side reactions with electrolytes, reduce self-discharge reactions, improve thermal and structural stability, and further enhance the overall battery performance. The review addresses the importance of nanoscale surface modification on battery cathodes and concludes with a comparison of the different nanoprocess techniques discussed to provide a direction in the race to build advanced lithium-ion batteries.

Emission characteristics of dispenser cathodes with a fine-grained tungsten top layer

NASA Astrophysics Data System (ADS)

Kimura, S.; Higuchi, T.; Ouchi, Y.; Uda, E.; Nakamura, O.; Sudo, T.; Koyama, K.

1997-02-01

In order to improve the emission stability of the Ir-coated dispenser cathode under ion bombardment, a fine-grained tungsten top layer was applied on the substrate porous tungsten plug before Ir coating. The emission characteristics were studied after being assembled in a CRT gun. Cathode current was measured under pulse operation in a range of 0.1-9% duty. Remarkable anti-ion bombardment characteristics were observed over the range of 1-6% duty. The improved cathode showed 1.5 times higher emission current than that of a conventional Ir-coated dispenser cathode at 4% duty. AES analysis showed that the recovering rates of surface Ba and O atoms after ion bombardment were 2.5 times higher. From these results it is confirmed that the Ir coated cathode with a fine-grained tungsten top layer is provided with a good tolerance against the ion bombardment.

Structural transformations in high-capacity Li 2Cu 0.5Ni 0.5O 2 cathodes

DOE PAGES

Ruther, Rose E.; Pandian, Amaresh Samuthira; Yan, Pengfei; ...

2017-03-09

Cathode materials that can cycle >1 Li + per transition metal are of substantial interest for increasing the overall energy density of lithium-ion batteries. Li 2Cu 0.5Ni 0.5O 2 has a very high theoretical capacity of ~500 mAh/g assuming both Li+ ions are cycled reversibly. The Cu 2+/3+ and Ni 2+/3+/4+ redox couples are also at high voltage, which could further boost the energy density of this system. Despite such promise, Li 2Cu 0.5Ni 0.5O 2 undergoes irreversible phase changes during charge (delithiation) that result in large first-cycle irreversible loss and poor long-term cycling stability. Oxygen evolves before the Cumore » 2+/3+ or Ni 3+/4+ transitions are accessed. In this contribution, X-ray diffraction, transmission electron microscopy (TEM), and transmission X-ray microscopy combined with X-ray absorption near edge structure (TXM–XANES) are used to follow the chemical and structural changes that occur in Li 2Cu 0.5Ni 0.5O 2 during electrochemical cycling. Li 2Cu 0.5Ni 0.5O 2 is a solid solution of orthorhombic Li2CuO2 and Li2NiO2, but the structural changes more closely mimic the changes that the Li 2NiO 2 endmember undergoes. Li 2Cu 0.5Ni 0.5O 2 loses long-range order during charge, but TEM analysis provides clear evidence of particle exfoliation and the transformation from orthorhombic to a partially layered structure. Linear combination fitting and principal component analysis of TXM–XANES are used to map the different phases that emerge during cycling ex situ and in situ. Lastly, significant changes in the XANES at the Cu and Ni K-edges correlate with the onset of oxygen evolution.« less

High-Energy/Power and Low-Temperature Cathode for Sodium-Ion Batteries: In Situ XRD Study and Superior Full-Cell Performance.

PubMed

Guo, Jin-Zhi; Wang, Peng-Fei; Wu, Xing-Long; Zhang, Xiao-Hua; Yan, Qingyu; Chen, Hong; Zhang, Jing-Ping; Guo, Yu-Guo

2017-09-01

Sodium-ion batteries (SIBs) are still confronted with several major challenges, including low energy and power densities, short-term cycle life, and poor low-temperature performance, which severely hinder their practical applications. Here, a high-voltage cathode composed of Na 3 V 2 (PO 4 ) 2 O 2 F nano-tetraprisms (NVPF-NTP) is proposed to enhance the energy density of SIBs. The prepared NVPF-NTP exhibits two high working plateaux at about 4.01 and 3.60 V versus the Na + /Na with a specific capacity of 127.8 mA h g -1 . The energy density of NVPF-NTP reaches up to 486 W h kg -1 , which is higher than the majority of other cathode materials previously reported for SIBs. Moreover, due to the low strain (≈2.56% volumetric variation) and superior Na transport kinetics in Na intercalation/extraction processes, as demonstrated by in situ X-ray diffraction, galvanostatic intermittent titration technique, and cyclic voltammetry at varied scan rates, the NVPF-NTP shows long-term cycle life, superior low-temperature performance, and outstanding high-rate capabilities. The comparison of Ragone plots further discloses that NVPF-NTP presents the best power performance among the state-of-the-art cathode materials for SIBs. More importantly, when coupled with an Sb-based anode, the fabricated sodium-ion full-cells also exhibit excellent rate and cycling performances, thus providing a preview of their practical application. © 2017 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Nasicon-Type Surface Functional Modification in Core-Shell LiNi0.5Mn0.3Co0.2O2@NaTi2(PO4)3 Cathode Enhances Its High-Voltage Cycling Stability and Rate Capacity toward Li-Ion Batteries.

PubMed

Liang, Longwei; Sun, Xuan; Wu, Chen; Hou, Linrui; Sun, Jinfeng; Zhang, Xiaogang; Yuan, Changzhou

2018-02-14

Surface modifications are established well as efficient methodologies to enhance comprehensive Li-storage behaviors of the cathodes and play a significant role in cutting edge innovations toward lithium-ion batteries (LIBs). Herein, we first logically devised a pilot-scale coating strategy to integrate solid-state electrolyte NaTi 2 (PO 4 ) 3 (NTP) and layered LiNi 0.5 Mn 0.3 Co 0.2 O 2 (NMC) for smart construction of core-shell NMC@NTP cathodes. The Nasicon-type NTP nanoshell with exceptional ion conductivity effectively suppressed gradual encroachment and/or loss of electroactive NMC, guaranteed stable phase interfaces, and meanwhile rendered small sur-/interfacial electron/ion-diffusion resistance. By benefiting from immanently promoting contributions of the nano-NTP coating, the as-fabricated core-shell NMC@NTP architectures were competitively endowed with superior high-voltage cyclic stabilities and rate capacities within larger electrochemical window from 3.0 to 4.6 V when utilized as advanced cathodes for advanced LIBs. More meaningfully, the appealing electrode design concept proposed here will exert significant impact upon further constructing other high-voltage Ni-based cathodes for high-energy/power LIBs.

Pluronic F127 as auxiliary template for preparing nitrogen and oxygen dual doped mesoporous carbon cathode of lithium-oxygen batteries

NASA Astrophysics Data System (ADS)

Wu, Junwei; Liu, Yanchen; Cui, Yanhui; Ouyang, Jue; Baker, Andrew P.; Li, Zuohua; Zhang, Huayu

2018-02-01

Two mesoporous carbon foam (MCF) with nitrogen and oxygen dual doped are fabricated through facile templated hydrothermal process. One using fumed silica as single template is named S-MCF, and another using fumed silica and Pluronic F127 as double templates is named D-MCF. When using Pluronic F127 as an auxiliary template, the D-MCF shows different porous architecture and surface chemical nature from S-MCF, thus they behave differently as cathode materials in Li-O2 batteries. The D-MCF electrode exhibits a slight lower discharge capacity and an increased overpotential than that of S-SCF due to the decreased surface area and oxygen content. However, a better cycle stability was proved for the D-MCF electrode because of its higher nitrogen and lower oxygen content. When further composited with RuO2 nanoparticles, the RuO2/D-MCF cathode can operate 160 cycles with capacity cutoff of 500 mAh g-1, and this prolonged cycle life, compared to the 102 cycles of S-MCF cathode, verifies the superior electrochemical stability of D-MCF further and illuminates the crucial role of carbon substrate in the cathodes of Li-O2 batteries.

Tuning Li2MO3 phase abundance and suppressing migration of transition metal ions to improve the overall performance of Li- and Mn-rich layered oxide cathode

NASA Astrophysics Data System (ADS)

Zhang, Shiming; Tang, Tian; Ma, Zhihua; Gu, Haitao; Du, Wubing; Gao, Mingxia; Liu, Yongfeng; Jian, Dechao; Pan, Hongge

2018-03-01

The poor cycling stability of Li- and Mn-rich layered oxide cathodes used in lithium-ion batteries (LIBs) has severely limited their practical application. Unfortunately, current strategies to improve their lifecycle sacrifice initial capacity. In this paper, we firstly report the synergistic improvement of the electrochemical performance of a Li1.2Ni0.13Co0.13Mn0.54O2 (LNCMO) cathode material, including gains for capacity, cycling stability, and rate capability, by the partial substitution of Li+ ions by Mg2+ ions. Electrochemical performance is evaluated by a galvanostatic charge and discharge test and electrochemical impedance spectroscopy (EIS). Structure and morphology are characterized by X-ray diffraction (XRD) and high-resolution transmission electron microscopy (HRTEM). Compared with the substitution of transition metal (TM) ions with Mg2+ ions reported previously, the substitution of Li+ ions by Mg2+ ions not only drastically ameliorates the capacity retention and rate performance challenges of LNCMO cathodes but also markedly suppresses their voltage fading, due to the inhibition of the migration of TM ions during cycling, while also increasing the capacity of the cathode due to an increased abundance of the Li2MO3 phase.

Overcoming bottlenecks of enzymatic biofuel cell cathodes: crude fungal culture supernatant can help to extend lifetime and reduce cost.

PubMed

Sané, Sabine; Jolivalt, Claude; Mittler, Gerhard; Nielsen, Peter J; Rubenwolf, Stefanie; Zengerle, Roland; Kerzenmacher, Sven

2013-07-01

Enzymatic biofuel cells (BFCs) show great potential for the direct conversion of biochemically stored energy from renewable biomass resources into electricity. However, enzyme purification is time-consuming and expensive. Furthermore, the long-term use of enzymatic BFCs is hindered by enzyme degradation, which limits their lifetime to only a few weeks. We show, for the first time, that crude culture supernatant from enzyme-secreting microorganisms (Trametes versicolor) can be used without further treatment to supply the enzyme laccase to the cathode of a mediatorless BFC. Polarization curves show that there is no significant difference in the cathode performance when using crude supernatant that contains laccase compared to purified laccase in culture medium or buffer solution. Furthermore, we demonstrate that the oxygen reduction activity of this enzymatic cathode can be sustained over a period of at least 120 days by periodic resupply of crude culture supernatant. This is more than five times longer than control cathodes without the resupply of culture supernatant. During the operation period of 120 days, no progressive loss of potential is observed, which suggests that significantly longer lifetimes than shown in this work may be possible. Our results demonstrate the possibility to establish simple, cost efficient, and mediatorless enzymatic BFC cathodes that do not require expensive enzyme purification procedures. Furthermore, they show the feasibility of an enzymatic BFC with an extended lifetime, in which self-replicating microorganisms provide the electrode with catalytically active enzymes in a continuous or periodic manner. Copyright © 2013 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Qin, Fen; Key Laboratory on High Power Microwave Technology, Institute of Applied Electronics, China Academy of Engineering Physics, Mianyang 621900; Wang, Dong, E-mail: mr20001@sina.com

We present the repetitive operation research results of an L-band magnetically insulated transmission line oscillator with metal array cathode (MAC-MILO) in this paper. To ensure a more uniform emission of electrons emitted from the cathode, metal plates with different outer radii and thicknesses are periodically arranged in longitudinal direction on the cathode substrate to act as emitters. The higher order mode depressed MILO (HDMILO) structure is applied to ensure stability of the tube. Comparison experiments are carried out between velvet cathode and MAC MILO driven by a 20 GW/40 Ω/40 ns/20 Hz pulse power system. Experimental results reveal that themore » MAC has much lower outgassing rate, much longer life time, and higher repetitive stability. The MAC-MILO could work stably with a rep-rate up to 20 Hz at a power level of 550 MW when employing a 350 kV/35 kA electric pulse. The TE{sub 11} mode radiation pattern in the farfield region reveals the tube works steadily on the dominant mode. More than 2000 shots have been tested in repetitive mode without any obvious degradation of the detected microwave parameters.« less

Pressurized air cathodes for enhanced stability and power generation by microbial fuel cells

NASA Astrophysics Data System (ADS)

He, Weihua; Yang, Wulin; Tian, Yushi; Zhu, Xiuping; Liu, Jia; Feng, Yujie; Logan, Bruce E.

2016-11-01

Large differences between the water and air pressure in microbial fuel cells (MFCs) can deform and damage cathodes. To avoid deformation, the cathode air pressure was controlled to balance pressure differences between the air and water. Raising the air pressures from 0 to 10 kPa at a set cathode potential of -0.3 V (versus Ag/AgCl) enhanced cathode performance by 17%, but pressures ≥25 kPa decreased current and resulted in air leakage into the solution. Matching the air pressure with the water pressure avoided cathode deformation and improved performance. The maximum power density increased by 15%, from 1070 ± 20 to 1230 ± 70 mW m-2, with balanced air and water pressures of 10-25 kPa. Oxygen partial pressures ≥12.5 kPa in the cathode compartment maintained the oxygen reduction rate to be within 92 ± 1% of that in ambient air. The use of pressurized air flow through the cathode compartments can enable closer spacing of the cathodes compared to passive gas transfer systems, which could make the reactor design more compact. The energy cost of pressurizing the cathodes was estimated to be smaller than the increase in power that resulted from the use of pressurized cathodes.

Emission and evaporation properties of 75 at.% Re-25 at.% W mixed matrix impregnated cathode

NASA Astrophysics Data System (ADS)

Lai, Chen; Wang, Jinshu; Zhou, Fan; Liu, Wei; den Engelsen, Daniel; Miao, Naihua

2018-01-01

We present a comprehensive study on the phase, emission performance, surface composition, chemical states and evaporation properties of a 75 at.% Re-25 at.% W (75Re) mixed matrix impregnated cathode by several modern analyzers, including XRD, electron emission test device, in situ AES, XPS and Quartz Crystal Oscillation Instrument (QCOI). On the basis of experimental results, the adsorption energy and charge transfer of the Ba-O dipole adsorbed on cathode surface was investigated by the first-principles density functional theory calculations. The in situ AES analyses indicate that the atomic ratio of Ba:O of the active emission layer on the cathode surface converged to 3:2 for a conventional Ba-W cathode and to about 3:1 for the 75Re cathode. Due to the larger adsorption energy of Ba and Ba-O on 75Re cathode surface, the total evaporation rate of Ba and BaO in the 75Re cathode is much lower than that for the Ba-W cathode, which is agreed favorably with the experimental evaporation data. Our characterizations and calculations suggest that rhenium in the matrix of impregnated cathodes improves the stability of Ba-O dipole on the cathode surface and enhances the emission capability substantially.

Surface Modification Technique of Cathode Materials for LI-ION Battery

NASA Astrophysics Data System (ADS)

Jia, Yongzhong; Han, Jinduo; Jing, Yan; Jin, Shan; Qi, Taiyuan

Cathode materials for Li-ion battery LiMn2O4 and LiCo0.1Mn1.9O4 were prepared by soft chemical method. Carbon, which was made by decomposing organic compounds, was used as modifying agent. Cathode material matrix was mixed with water solution that had contained organic compound such as cane sugar, soluble amylum, levulose et al. These mixture were reacted at 150 200 °C for 0.5 4 h in a Teflon-lined autoclave to get a series of homogeneously C-coated cathode materials. The new products were analyzed by X-ray diffraction (XRD) and infrared (IR). Morphology of cathode materials was characterized by scanning electron microscope (SEM) and transition electron microscope (TEM). The new homogeneously C-coated products that were used as cathode materials of lithium-ion battery had good electrochemical stability and cycle performance. This technique has free-pollution, low cost, simpleness and easiness to realize the industrialization of the cathode materials for Li-ion battery.

Multicore-shell nanofiber architecture of polyimide/polyvinylidene fluoride blend for thermal and long-term stability of lithium ion battery separator.

PubMed

Park, Sejoon; Son, Chung Woo; Lee, Sungho; Kim, Dong Young; Park, Cheolmin; Eom, Kwang Sup; Fuller, Thomas F; Joh, Han-Ik; Jo, Seong Mu

2016-11-11

Li-ion battery, separator, multicoreshell structure, thermal stability, long-term stability. A nanofibrous membrane with multiple cores of polyimide (PI) in the shell of polyvinylidene fluoride (PVdF) was prepared using a facile one-pot electrospinning technique with a single nozzle. Unique multicore-shell (MCS) structure of the electrospun composite fibers was obtained, which resulted from electrospinning a phase-separated polymer composite solution. Multiple PI core fibrils with high molecular orientation were well-embedded across the cross-section and contributed remarkable thermal stabilities to the MCS membrane. Thus, no outbreaks were found in its dimension and ionic resistance up to 200 and 250 °C, respectively. Moreover, the MCS membrane (at ~200 °C), as a lithium ion battery (LIB) separator, showed superior thermal and electrochemical stabilities compared with a widely used commercial separator (~120 °C). The average capacity decay rate of LIB for 500 cycles was calculated to be approximately 0.030 mAh/g/cycle. This value demonstrated exceptional long-term stability compared with commercial LIBs and with two other types (single core-shell and co-electrospun separators incorporating with functionalized TiO 2 ) of PI/PVdF composite separators. The proper architecture and synergy effects of multiple PI nanofibrils as a thermally stable polymer in the PVdF shell as electrolyte compatible polymers are responsible for the superior thermal performance and long-term stability of the LIB.

Multicore-shell nanofiber architecture of polyimide/polyvinylidene fluoride blend for thermal and long-term stability of lithium ion battery separator

PubMed Central

Park, Sejoon; Son, Chung Woo; Lee, Sungho; Kim, Dong Young; Park, Cheolmin; Eom, Kwang Sup; Fuller, Thomas F.; Joh, Han-Ik; Jo, Seong Mu

2016-01-01

Li-ion battery, separator, multicoreshell structure, thermal stability, long-term stability. A nanofibrous membrane with multiple cores of polyimide (PI) in the shell of polyvinylidene fluoride (PVdF) was prepared using a facile one-pot electrospinning technique with a single nozzle. Unique multicore-shell (MCS) structure of the electrospun composite fibers was obtained, which resulted from electrospinning a phase-separated polymer composite solution. Multiple PI core fibrils with high molecular orientation were well-embedded across the cross-section and contributed remarkable thermal stabilities to the MCS membrane. Thus, no outbreaks were found in its dimension and ionic resistance up to 200 and 250 °C, respectively. Moreover, the MCS membrane (at ~200 °C), as a lithium ion battery (LIB) separator, showed superior thermal and electrochemical stabilities compared with a widely used commercial separator (~120 °C). The average capacity decay rate of LIB for 500 cycles was calculated to be approximately 0.030 mAh/g/cycle. This value demonstrated exceptional long-term stability compared with commercial LIBs and with two other types (single core-shell and co-electrospun separators incorporating with functionalized TiO2) of PI/PVdF composite separators. The proper architecture and synergy effects of multiple PI nanofibrils as a thermally stable polymer in the PVdF shell as electrolyte compatible polymers are responsible for the superior thermal performance and long-term stability of the LIB. PMID:27833132

Electrolytic trichloroethene degradation using mixed metal oxide coated titanium mesh electrodes.

PubMed

Petersen, Matthew A; Sale, Thomas C; Reardon, Kenneth F

2007-04-01

Electrochemical systems provide a low cost, versatile, and controllable platform to potentially treat contaminants in water, including chlorinated solvents. Relative to bare metal or noble metal amended materials, dimensionally stable electrode materials such as mixed metal oxide coated titanium (Ti/MMO) have advantages in terms of stability and cost, important factors for sustainable remediation solutions. Here, we report the use of Ti/MMO as an effective cathode substrate for treatment of trichloroethene (TCE). TCE degradation in a batch reactor was measured as the decrease of TCE concentration over time and the corresponding evolution of chloride; notably, this occurred without the formation of commonly encountered chlorinated intermediates. The reaction was initiated when Ti/MMO cathode potentials were less than -0.8 V vs. the standard hydrogen electrode, and the rate of TCE degradation increased linearly with progressively more negative potentials. The maximum pseudo-first-order heterogeneous rate constant was approximately 0.05 cm min(-1), which is comparable to more commonly used cathode materials such as nickel. In laboratory-scale flow-though column reactors designed to simulate permeable reactive barriers (PRBs), TCE concentrations were reduced by 80-90%. The extent of TCE flux reduction increased with the applied potential difference across the electrodes and was largely insensitive to the spacing distance between the electrodes. This is the first report of the electrochemical reduction of a chlorinated organic contaminant at a Ti/MMO cathode, and these results support the use of this material in PRBs as a possible approach to manage TCE plume migration.

Long Term Stability of Learning Outcomes in Undergraduates after an Open-Inquiry Instruction on Thermal Science

ERIC Educational Resources Information Center

Adorno, Dominique Persano; Pizzolato, Nicola; Fazio, Claudio

2018-01-01

This paper investigates the efficacy of an open-inquiry approach to achieve a long term stability of physics instruction. This study represents the natural continuation of a research project started four years ago when a sample of thirty engineering undergraduates, having already attended traditional university physics instruction, were involved…

Development of side-chain NLO polymer materials with high electro-optic activity and long-term stability

NASA Astrophysics Data System (ADS)

Huang, Diyun; Parker, Timothy; Guan, Hann Wen; Cong, Shuxin; Jin, Danliang; Dinu, Raluca; Chen, Baoquan; Tolstedt, Don; Wolf, Nick; Condon, Stephen

2005-01-01

The electro-optic coefficient and long-term dipole alignment stability are two major factors in the development of high performance NLO materials for the application of high-speed EO devices. We have developed a high performance non-linear organic chromophore and incorporated it into a crosslinkable side-chain polyimide system. The polymer was synthesized through stepwise grafting of the crosslinker followed by the chromophore onto the polyimide backbone via esterification. Different chromophore loading levels were achieved by adjusting the crosslinker/chromophore feeding ratio. The polyimides films were contact-poled with second-harmonic generation monitoring. A large EO coefficient value was obtained and good long-term thermal stability at 85°C was observed.

Revealing Anisotropic Spinel Formation on Pristine Li- and Mn-Rich Layered Oxide Surface and Its Impact on Cathode Performance

DOE PAGES

Kuppan, Saravanan; Shukla, Alpesh Khushalchand; Membreno, Daniel; ...

2017-01-06

Surface properties of cathode particles play important roles in the transport of ions and electrons and they may ultimately dominate cathode's performance and stability in lithium-ion batteries. Through the use of carefully prepared Li 1.2Ni 0.13Mn 0.54Co 0.13O 2 crystal samples with six distinct morphologies, surface transition-metal redox activities and crystal structural transformation are investigated as a function of surface area and surface crystalline orientation. Complementary depth-profiled core-level spectroscopy, namely, X-ray absorption spectroscopy, electron energy loss spectroscopy, and atomic-resolution scanning transmission electron microscopy, are applied in the study, presenting a fine example of combining advanced diagnostic techniques with a well-definedmore » model system of battery materials. Here, we report the following findings: (1) a thin layer of defective spinel with reduced transition metals, similar to what is reported on cycled conventional secondary particles in the literature, is found on pristine oxide surface even before cycling, and (2) surface crystal structure and chemical composition of both pristine and cycled particles are facet dependent. Oxide structural and cycling stabilities improve with maximum expression of surface facets stable against transition-metal reduction. Finally, the intricate relationships among morphology, surface reactivity and structural transformation, electrochemical performance, and stability of the cathode materials are revealed.« less

A High Capacity, Good Safety and Low Cost Na2FeSiO4-Based Cathode for Rechargeable Sodium-Ion Battery.

PubMed

Guan, Wenhao; Pan, Bin; Zhou, Peng; Mi, Jinxiao; Zhang, Dan; Xu, Jiacheng; Jiang, Yinzhu

2017-07-12

Rechargeable sodium-ion batteries (SIBs) are receiving intense interest because the resource abundance of sodium and its lithium-like chemistry make them low cost alternatives to the prevailing lithium-ion batteries in large-scale energy storage devices. Two typical classes of materials including transition metal oxides and polyanion compounds have been under intensive investigation as cathodes for SIBs; however, they are still limited to poor stability or low capacity of the state-of-art. Herein, we report a low cost carbon-coated Na 2 FeSiO 4 with simultaneous high capacity and good stability, owing to the highly pure Na-rich triclinic phase and the carbon-incorporated three-dimensional network morphology. The present carbon-coated Na 2 FeSiO 4 demonstrates the highest reversible capacity of 181.0 mAh g -1 to date with multielectron redox reaction that occurred among various polyanion-based SIBs cathodes, which achieves a close-to-100% initial Coulombic efficiency and a stable cycling with 88% capacity retention up to 100 cycles. In addition, such an electrode shows excellent stability either charged at a high voltage of 4.5 V or heated up to 800 °C. The present work might open up the possibility for developing high capacity, good safety and low cost polyanion-based cathodes for rechargeable SIBs.

Modification of polymer velvet cathode via metallic Mo coating for enhancement of high-current electron emission performances

DOE Office of Scientific and Technical Information (OSTI.GOV)

Xiong, Ying; Wang, Bing; Yi, Yong

2013-09-15

The effect of surface Mo coating on the high-current electron emission performances for polymer velvet cathode has been investigated in a diode with A-K gap of 11.5 cm by the combination of time-resolved electrical diagnostic and temporal pressure variation. Compared with uncoated polymer velvet cathode under the single-pulsed emission mode, the Mo-coated one shows lower outgassing levels (∼0.40 Pa L), slower cathode plasma expansion velocity (∼2.30 cm/μs), and higher emission stability as evidences by the change in cathode current, temporal pressure variation, and diode perveance. Moreover, after Mo coating, the emission consistency of the polymer velvet cathode between two adjacentmore » pulses is significantly improved in double-pulsed emission mode with ∼500 ns interval between two pulses, which further confirms the effectiveness of Mo coating for enhancement of electron emission performance of polymer velvet cathodes. These results should be of interest to the high-repetitive high-power microwave systems with cold cathodes.« less

High performance polymer solar cells with as-prepared zirconium acetylacetonate film as cathode buffer layer

PubMed Central

Tan, Zhan'ao; Li, Shusheng; Wang, Fuzhi; Qian, Deping; Lin, Jun; Hou, Jianhui; Li, Yongfang

2014-01-01

Low-work-function active metals are commonly used as cathode in polymer solar cells (PSCs), but sensitivity of the active metals towards moisture and oxygen results in poor stability of the devices. Therefore, solution-proceessable and stable cathode buffer layer is of great importance for the application of PSCs. Here we demonstrate high performance PSCs by employing as-prepared zirconium acetylacetonate (a-ZrAcac) film spin-cast from its ethanol solution as cathode buffer layer. The PSCs based on a low bandgap polymer PBDTBDD as donor and PC60BM as acceptor with a-ZrAcac/Al cathode demonstrated an average power conversion efficiency (PCE) of 8.75% which is significantly improved than that of the devices with traditional Ca/Al cathode. The improved photovoltaic performance is benefitted from the decreased series resistance and enhanced light harvest of the PSCs with the a-ZrAcac/Al cathode. The results indicate that a-ZrAcac is a promising high performance cathode buffer layer for fabricating large area flexible PSCs. PMID:24732976

Long-term stability of FeSO4 and H2SO4 treated chromite ore processing residue (COPR): Importance of H+ and SO42.

PubMed

Wang, Xin; Zhang, Jingdong; Wang, Linling; Chen, Jing; Hou, Huijie; Yang, Jiakuan; Lu, Xiaohua

2017-01-05

In this study, the long-term stability of Cr(VI) in the FeSO 4 and H 2 SO 4 (FeSO 4 -H 2 SO 4 ) treated chromite ore processing residue (COPR) after 400 curing days and the stabilization mechanisms were investigated. FeSO 4 -H 2 SO 4 treatment significantly reduced toxicity characteristic leaching procedure (TCLP) and synthetic precipitation leaching procedure (SPLP) Cr(VI) concentrations to lower than the regulatory limit of 1.5mgL -1 (HJ/T 301-2007, China EPA) even for the samples curing 400days, achieving an outstanding long-term stability. Our independent leaching tests revealed that H + and SO 4 2- have synergistic effect on promoting the release of Cr(VI), which would make Cr(VI) easier accessed by Fe(II) during stabilization. The contributions of H + and SO 4 2- to Cr(VI) release ratio were 25%-44% and 19%-38%, respectively, as 5mol H 2 SO 4 per kg COPR was used. X-ray powder diffraction (XRD), X-ray photoelectron spectroscopy (XPS) and alkaline digestion analyses were also employed to interpret the possible stabilization mechanism. Cr(VI) released from COPR solid was reduced to Cr(III) by Fe(II), and then formed stable Fe x Cr (1-x) (OH) 3 precipitate. This study provides a facile and reliable scheme for COPR stabilization, and verifies the excellent long-term stability of the FeSO 4 -H 2 SO 4 treated COPR. Copyright © 2016 Elsevier B.V. All rights reserved.

Extended test of a xenon hollow cathode for a space plasma contactor

NASA Technical Reports Server (NTRS)

Sarver-Verhey, Timothy R.

1994-01-01

Implementation of a hollow cathode plasma contactor for charge control on the Space Station has required validation of long-life hollow cathodes. A test series of hollow cathodes and hollow cathode plasma contactors was initiated as part of the plasma contactor development program. An on-going wear-test of a hollow cathode has demonstrated cathode operation in excess of 4700 hours with small changes in operating parameters. The discharge experienced 4 shutdowns during the test, all of which were due to test facility failures or expellant replenishment. In all cases, the cathode was reignited at approximately 42 volts and resumed typical operation. This test represents the longest demonstrated stable operation of a high current (greater than 1A) xenon hollow cathode reported to date.

Continuing life test of a xenon hollow cathode for a space plasma contactor

NASA Technical Reports Server (NTRS)

Sarver-Verhey, Timothy R.

1994-01-01

Implementation of a hollow cathode plasma contactor for charge control on the Space Station has required validation of long-life hollow cathodes. A test series of hollow cathodes and hollow cathode plasma contactors was initiated as part of the plasma contactor development program. An on-going wear-test of a hollow cathode has demonstrated cathode operation in excess of 10,000 hours with small changes in operating parameters. The discharge has experienced 10 shutdowns during the test, all of which were due to test facility failures or expellant replenishment. In all cases, the cathode was re-ignited at approximately 42 volts and resumed typical operation. This test represents the longest demonstrated stable operation of a high current (greater than 1 A) xenon hollow cathode reported to date.

Toward a stable solid-electrolyte-interfaces on nickel-rich cathodes: LiPO2F2 salt-type additive and its working mechanism for LiNi0.5Mn0.25Co0.25O2 cathodes

NASA Astrophysics Data System (ADS)

Zhao, Weimin; Zheng, Guorui; Lin, Min; Zhao, Wengao; Li, Dongjiang; Guan, Xiaoyun; Ji, Yajuan; Ortiz, Gregorio F.; Yang, Yong

2018-03-01

Although the LiNi0.5Mn0.25Co0.25O2 holds the merits of high theoretical capacities and a relatively high operating voltage, the battery performance suffers from the severe cycling decay due to the unstable solid electrolyte interface on the cathode. Herein, we present LiPO2F2 as a salt-type electrolyte additive to enhance the cycling stability of large-size crystallite LiNi0.5Mn0.25Co0.25O2 cathodes. Results demonstrate that 1 wt% LiPO2F2 can significantly improve not only the initial coulombic efficiency by 3%, but also the cycling stability and rate capability at 25 °C. Furthermore, the discharge capacity of LiNi0.5Mn0.25Co0.25O2 cathodes still maintain 156 mAh g-1 after 100 cycles even when the temperature increases to 55 °C. In-depth experimental characterization and theoretical calculation indicate that a new stable and thin (e.g. 15-20 nm) film formed on the surface of the cathodes, with composition of LiPO2F2, LiF, etc., which significantly reduces charge transfer impedance of the electrodes, and therefore significantly improves the cycling and rate performance of LiNi0.5Mn0.25Co0.25O2.

An impressive approach to solving the ongoing stability problems of LiCoPO4 cathode: Nickel oxide surface modification with excellent core-shell principle

NASA Astrophysics Data System (ADS)

Örnek, Ahmet

2017-07-01

Nanoscale and NiO-coated LiCoPO4 cathode materials were prepared for the first time by a newly designed three-step synthesis route, which is a combined technique including advantages of the Stöber, hydrothermal and microwave synthesis methods. Using this extraordinary technique, LiCoPO4 particles are coated with a thin NiO layer with a perfect core-shell morphology and the technique's positive contribution to electrochemistry is elucidated in detail. The samples are interpreted using opto-analytical techniques and galvanostatic charge-discharge tests. The high-resolution transmission electron microscopy analysis proves that this well-elaborated technique makes it possible to achieve a continuous NiO surface coverage of 8-10 nm, a result that contributes towards solving the chronic electrochemical problems of 4.8 V cathode material. Our data reveal that NiO-coated LiCoPO4 cathode demonstrates superior cycle stability and specific capacity at relatively low rates. The 2.5% wt. NiO-coated cathode exhibits the best electrochemical property, which reaches a discharge capacity of 159 mAh g-1 at 0.l C current rate and shows almost 85% capacity retention after 80 charge-discharge cycles. It therefore achieves partial success in improving the electrochemical properties of the LiCoPO4 cathode material, which is especially crucial for energy storage to be applied in electric vehicles and plug-in hybrid electric applications.

Active screen cage pulsed dc discharge for implanting copper in polytetrafluoroethylene (PTFE)

NASA Astrophysics Data System (ADS)

Zaka-ul-Islam, Mujahid; Naeem, Muhammad; Shafiq, Muhammad; Sitara; Jabbar Al-Rajab, Abdul; Zakaullah, Muhammad

2017-07-01

Polymers such as polytetrafluoroethylene (PTFE) are widely used in artificial organs where long-term anti-bacterial properties are required to avoid bacterial proliferation. Copper or silver ion implantation on the polymer surface is known as a viable method to generate long-term anti-bacterial properties. Here, we have tested pulsed DC plasma with copper cathodic cage for the PTFE surface treatment. The surface analysis of the treated specimens suggests that the surface, structural properties, crystallinity and chemical structure of the PTFE have been changed, after the plasma treatment. The copper release tests show that copper ions are released from the polymer at a slow rate and quantity of the released copper increases with the plasma treatment time.

Synthesis of hierarchical porous δ-MnO2 nanoboxes as an efficient catalyst for rechargeable Li-O2 batteries

NASA Astrophysics Data System (ADS)

Zhang, Jian; Luan, Yanping; Lyu, Zhiyang; Wang, Liangjun; Xu, Leilei; Yuan, Kaidi; Pan, Feng; Lai, Min; Liu, Zhaolin; Chen, Wei

2015-09-01

A rechargeable lithium-oxygen (Li-O2) battery with a remarkably high theoretical energy storage capacity has attracted enormous research attention. However, the poor oxygen reduction and oxygen evolution reaction (ORR and OER) activities in discharge and charge processes cause low energy efficiency, poor electrolyte stability and short cycle life. This requires the development of efficient cathode catalysts to dramatically improve the Li-O2 battery performances. MnO2-based materials are recognized as efficient and low-cost catalysts for a Li-O2 battery cathode. Here, we report a controllable approach to synthesize hierarchical porous δ-MnO2 nanoboxes by using Prussian blue analogues as the precursors. The obtained products possess hierarchical pore size and an extremely large surface area (249.3 m2 g-1), which would favour oxygen transportation and provide more catalytically active sites to promote ORR and OER as the Li-O2 battery cathode. The battery shows enhanced discharge capacity (4368 mA h g-1@0.08 mA cm-2), reduced overpotential (270 mV), improved rate performance and excellent cycle stability (248 cycles@500 mA h g-1 and 112 cycles@1000 mA h g-1), in comparison with the battery with a VX-72 carbon cathode. The superb performance of the hierarchical porous δ-MnO2 nanoboxes, together with a convenient fabrication method, presents an alternative to develop advanced cathode catalysts for the Li-O2 battery.A rechargeable lithium-oxygen (Li-O2) battery with a remarkably high theoretical energy storage capacity has attracted enormous research attention. However, the poor oxygen reduction and oxygen evolution reaction (ORR and OER) activities in discharge and charge processes cause low energy efficiency, poor electrolyte stability and short cycle life. This requires the development of efficient cathode catalysts to dramatically improve the Li-O2 battery performances. MnO2-based materials are recognized as efficient and low-cost catalysts for a Li-O2 battery cathode. Here, we report a controllable approach to synthesize hierarchical porous δ-MnO2 nanoboxes by using Prussian blue analogues as the precursors. The obtained products possess hierarchical pore size and an extremely large surface area (249.3 m2 g-1), which would favour oxygen transportation and provide more catalytically active sites to promote ORR and OER as the Li-O2 battery cathode. The battery shows enhanced discharge capacity (4368 mA h g-1@0.08 mA cm-2), reduced overpotential (270 mV), improved rate performance and excellent cycle stability (248 cycles@500 mA h g-1 and 112 cycles@1000 mA h g-1), in comparison with the battery with a VX-72 carbon cathode. The superb performance of the hierarchical porous δ-MnO2 nanoboxes, together with a convenient fabrication method, presents an alternative to develop advanced cathode catalysts for the Li-O2 battery. Electronic supplementary information (ESI) available. See DOI: 10.1039/c5nr02983j

Long-Life/Low-Power Ion-Gun Cathode

NASA Technical Reports Server (NTRS)

Fitzgerald, D. J.

1982-01-01

New cathode has form of hollow tube through which gas enters region of high electron density, produced by electric discharge with auxiliary electrode referred to as "keeper." Ion-gun cathode emits electrons that bombard gas in chamber. Ions accelerated out of source are used to dope semiconductor material.

Synthesis of ceria based superhydrophobic coating on Ni20Cr substrate via cathodic electrodeposition.

PubMed

Pedraza, F; Mahadik, S A; Bouchaud, B

2015-12-21

In this work, superhydrophobic cerium oxide coating surface (111) with dual scale texture on Ni20Cr substrate is obtained by combination of electropolishing the substrate and subsequent cathodic electrodeposition and long-term UVH surface relaxation. To form hierarchical structures of CeO2 is controllable by varying the substrate roughness, and electropolishing period. The results indicated that at the optimal condition, the surface of the cerium oxide coating showed a superhydrophobicity with a great water contact angle (151.0 ± 1.4°) with Gecko state. An interface model for electropolishing of substrate surface in cerium nitrate medium is proposed. We expect that this facile process can be readily and widely adopted for the design of superhydrophobic coating on engineering materials.

ELECTRICAL CIRCUITS USING COLD-CATHODE TRIODE VALVES

DOEpatents

Goulding, F.S.

1957-11-26

An electrical circuit which may be utilized as a pulse generator or voltage stabilizer is presented. The circuit employs a cold-cathode triode valve arranged to oscillate between its on and off stages by the use of selected resistance-capacitance time constant components in the plate and trigger grid circuits. The magnitude of the d-c voltage applied to the trigger grid circuit effectively controls the repetition rate of the output pulses. In the voltage stabilizer arrangement the d-c control voltage is a portion of the supply voltage and the rectified output voltage is substantially constant.

Precise and long-term stabilization of the carrier-envelope phase of femtosecond laser pulses using an enhanced direct locking technique.

PubMed

Yu, Tae Jun; Hong, Kyung-Han; Choi, Hyun-Gyug; Sung, Jae Hee; Choi, Il Woo; Ko, Do-Kyeong; Lee, Jongmin; Kim, Junwon; Kim, Dong Eon; Nam, Chang Hee

2007-06-25

We demonstrate a long-term operation with reduced phase noise in the carrier-envelope-phase (CEP) stabilization process by employing a double feedback loop and an improved signal detection in the direct locking technique [Opt. Express 13, 2969 (2005)]. A homodyne balanced detection method is employed for efficiently suppressing the dc noise in the f-2f beat signal, which is converted into the CEP noise in the direct locking loop working at around zero carrier-envelope offset frequency (f(ceo)). In order to enhance the long-term stability, we have used the double feedback scheme that modulates both the oscillator pump power for a fast control and the intracavity-prism insertion depth for a slow and high-dynamic-range control. As a result, the in-loop phase jitter is reduced from 50 mrad of the previous result to 29 mrad, corresponding to 13 as in time scale, and the long-term stable operation is achieved for more than 12 hours.

Paper Microzone Plates as Analytical Tools for Studying Enzyme Stability: A Case Study on the Stabilization of Horseradish Peroxidase Using Trehalose and SU-8 Epoxy Novolac Resin.

PubMed

Ganaja, Kirsten A; Chaplan, Cory A; Zhang, Jingyi; Martinez, Nathaniel W; Martinez, Andres W

2017-05-16

Paper microzone plates in combination with a noncontact liquid handling robot were demonstrated as tools for studying the stability of enzymes stored on paper. The effect of trehalose and SU-8 epoxy novolac resin (SU-8) on the stability of horseradish peroxidase (HRP) was studied in both a short-term experiment, where the activity of various concentrations of HRP dried on paper were measured after 1 h, and a long-term experiment, where the activity of a single concentration of HRP dried and stored on paper was monitored for 61 days. SU-8 was found to stabilize HRP up to 35 times more than trehalose in the short-term experiment for comparable concentrations of the two reagents, and a 1% SU-8 solution was found to stabilize HRP approximately 2 times more than a 34% trehalose solution in both short- and long-term experiments. The results suggest that SU-8 is a promising candidate for use as an enzyme-stabilizing reagent for paper-based diagnostic devices and that the short-term experiment could be used to quickly evaluate the capacity of various reagents for stabilizing enzymes to identify and characterize new enzyme-stabilizing reagents.

Stabilizing nanostructured solid oxide fuel cell cathode with atomic layer deposition.

PubMed

Gong, Yunhui; Palacio, Diego; Song, Xueyan; Patel, Rajankumar L; Liang, Xinhua; Zhao, Xuan; Goodenough, John B; Huang, Kevin

2013-09-11

We demonstrate that the highly active but unstable nanostructured intermediate-temperature solid oxide fuel cell cathode, La0.6Sr0.4CoO3-δ (LSCo), can retain its high oxygen reduction reaction (ORR) activity with exceptional stability for 4000 h at 700 °C by overcoating its surfaces with a conformal layer of nanoscale ZrO2 films through atomic layer deposition (ALD). The benefits from the presence of the nanoscale ALD-ZrO2 overcoats are remarkable: a factor of 19 and 18 reduction in polarization area-specific resistance and degradation rate over the pristine sample, respectively. The unique multifunctionality of the ALD-derived nanoscaled ZrO2 overcoats, that is, possessing porosity for O2 access to LSCo, conducting both electrons and oxide-ions, confining thermal growth of LSCo nanoparticles, and suppressing surface Sr-segregation is deemed the key enabler for the observed stable and active nanostructured cathode.

Frequency stability of maser oscillators operated with cavity Q. [hydrogen and rubidium masers

NASA Technical Reports Server (NTRS)

Tetu, M.; Tremblay, P.; Lesage, P.; Petit, P.; Audoin, C.

1982-01-01

The short term frequency stability of masers equipped with an external feedback loop to increase the cavity quality factor was studied. The frequency stability of a hydrogen and a rubidium maser were measured and compared with theoretical evaluation. It is shown that the frequency stability passes through an optimum when the cavity Q is varied. Long term fluctuations are discussed and the optimum mid term frequency stability achievably by small size active and passive H-masers is considered.

Long-term effect of lime-fly ash treated soils.

DOT National Transportation Integrated Search

2003-12-01

In October of 2000 MDOT initiated State Study No. 147, entitled "Long-Term Effect of Lime-Fly Ash Treated Soils." The purpose of this study : was to evaluate the long-term performance of LFA stabilized soil as a base course material. Part of the impe...

Clinical characteristics and long-term response to mood stabilizers in patients with bipolar disorder and different age at onset

PubMed Central

Dell’Osso, Bernardo; Buoli, Massimiliano; Riundi, Riccardo; D’Urso, Nazario; Pozzoli, Sara; Bassetti, Roberta; Mundo, Emanuela; Altamura, A Carlo

2009-01-01

Introduction Bipolar disorder (BD) is a prevalent, comorbid, and impairing condition. Potential predictors of response to pharmacological treatment are object of continuous investigation in patients with BD. The present naturalistic study was aimed to assess clinical features and long-term response to mood stabilizers in a sample of bipolar subjects with different ages at onset. Methods The study sample included 108 euthymic patients, diagnosed as affected by BD, either type I or II, according to the DSM-IV-TR, who were started on mood stabilizer treatment. Patients were followed-up for 24 months and the occurrence of any mood episode collected. At the end of the follow-up, patients were divided in 3 subgroups according to the age at onset (early-onset ≤30 years, middle-onset >30–≤45 years, and late-onset >45 years, respectively) and the long-term response to mood stabilizers was compared between them along with other clinical features. Results The three subgroups showed significant differences in terms of clinical and demographic features and, with respect to long-term response to mood stabilizers, the early-onset subgroup showed a better outcome in terms of reduction of major depressive episodes during the 24-month follow-up compared to the other subgroups (one way ANOVA, F = 3.57, p = 0.032). Conclusions Even though further controlled studies are needed to clarify the relationship between age at onset and outcome in BD, the present follow-up study suggests clinical peculiarities and different patterns of response to mood stabilizers across distinct subgroups of patients with BD and different ages at onset. PMID:19649214

LONG TERM STABILITY STUDY AT FNAL AND SLAC USING BINP DEVELOPED HYDROSTATIC LEVEL SYSTEM

DOE Office of Scientific and Technical Information (OSTI.GOV)

Seryi, Andrei

2003-05-28

Long term ground stability is essential for achieving the performance goals of the Next Linear Collider. To characterize ground motion on relevant time scales, measurements have been performed at three geologically different locations using a hydrostatic level system developed specifically for these studies. Comparative results from the different sites are presented in this paper.

Long-term Stability of a Camouflage Retreatment of an Asymmetric Class III/Posterior Open Bite Using Sliding Jigs.

PubMed

Oliveira, Dauro Douglas; de Oliveira, Bruno Franco; Figueiredo, Daniel Santos Fonseca; Antunes, Alberto Nogueira da Gama; Seraidarian, Paulo Isaías

2017-10-01

This article reports the camouflage retreatment of an adult patient presenting an asymmetric Class III malocclusion and posterior open bite. Sliding jigs (SJs) associated with intermaxillary elastics were used. The long-term stability of the excellent results suggests that the use of SJs to correct asymmetric posterior occlusions may be effective.

Application of long-term simulation programs for analysis of system islanding

DOE Office of Scientific and Technical Information (OSTI.GOV)

Sancha, J.L.; Llorens, M.L.; Moreno, J.M.

1997-02-01

This paper describes the main results and conclusions from the application of two different long-term stability programs to the analysis of a system islanding scenario for a study case developed by Red Electrica de Espana (REE), based on the Spanish system. Two main goals were to evaluate the performance of both the influence of some important control and protection elements (tie-line loss-of-synchronism relays, underfrequency load-shedding, load-frequency control, and power plant dynamics). Conclusions about modeling and computational requirements for system islanding (frequency) scenarios and use of long-term stability programs are presented.

Long Term Stability and Relapse Following Mandibular Advancement and Mandibular Setback Surgeries: A Cephalometric Study

PubMed Central

Darshan, S Vinay; Ronad, Yusuf Ahammed; Kishore, M S V; Shetty, K Sadashiva; Rajesh, M; Suman, S D

2014-01-01

Background: The aim was to evaluate the long-term hard and soft tissue changes following mandibular advancement and setback surgeries. Materials and Methods: A total of 16 subjects each were selected who underwent bilateral sagittal split osteotomy mandibular advancement and mandibular setback groups. Pre-surgical (T1), immediate post-surgical (T2) and long-term post-surgical (T3) cephalograms were compared for hard and soft tissue changes. After cephalometric measurements, the quantity of changes between T1-T2 and T1-T3 were determined for each patient. The mean difference between T1-T2 and T1-T3 was compared with assess the long-term changes and stability. Results: In mandibular advancement the mean difference between immediate post-surgical and long term post-surgical is 7%, which accounts for a relapse of 7%. In mandibular setback, the mean difference between immediate post-surgical and long-term post-surgical is 29%, which accounts for a relapse of 29%. Conclusion: Mandibular advancement remained stable over the long period when compared to mandibular setback. PMID:25395792

Long term stability and relapse following mandibular advancement and mandibular setback surgeries: a cephalometric study.

PubMed

Darshan, S Vinay; Ronad, Yusuf Ahammed; Kishore, M S V; Shetty, K Sadashiva; Rajesh, M; Suman, S D

2014-09-01

The aim was to evaluate the long-term hard and soft tissue changes following mandibular advancement and setback surgeries. A total of 16 subjects each were selected who underwent bilateral sagittal split osteotomy mandibular advancement and mandibular setback groups. Pre-surgical (T1), immediate post-surgical (T2) and long-term post-surgical (T3) cephalograms were compared for hard and soft tissue changes. After cephalometric measurements, the quantity of changes between T1-T2 and T1-T3 were determined for each patient. The mean difference between T1-T2 and T1-T3 was compared with assess the long-term changes and stability. In mandibular advancement the mean difference between immediate post-surgical and long term post-surgical is 7%, which accounts for a relapse of 7%. In mandibular setback, the mean difference between immediate post-surgical and long-term post-surgical is 29%, which accounts for a relapse of 29%. Mandibular advancement remained stable over the long period when compared to mandibular setback.

Electrical characteristics of a free-burning direct-current argon arc operating between 90 and 563 kilowatts with two types of cathodes

NASA Technical Reports Server (NTRS)

Curtis, H. B.; Decker, A. J.

1975-01-01

The electrical characteristics of a high-power, long-lived, free-burning dc argon arc are presented. Empirical formulas relating voltage to current, electrode separation, and operating pressure are given for two types of cathodes: a typical point tip cathode and a cathode with a 1.27-cm-(0.5-in.-) diameter crater in the tip. Power was varied from 90 to 563 kW. A discussion of the cathode with the crater tip is given.

Unraveling micro- and nanoscale degradation processes during operation of high-temperature polymer-electrolyte-membrane fuel cells

NASA Astrophysics Data System (ADS)

Hengge, K.; Heinzl, C.; Perchthaler, M.; Varley, D.; Lochner, T.; Scheu, C.

2017-10-01

The work in hand presents an electron microscopy based in-depth study of micro- and nanoscale degradation processes that take place during the operation of high-temperature polymer-electrolyte-membrane fuel cells (HT-PEMFCs). Carbon supported Pt particles were used as cathodic catalyst material and the bimetallic, carbon supported Pt/Ru system was applied as anode. As membrane, cross-linked polybenzimidazole was used. Scanning electron microscopy analysis of cross-sections of as-prepared and long-term operated membrane-electrode-assemblies revealed insight into micrometer scale degradation processes: operation-caused catalyst redistribution and thinning of the membrane and electrodes. Transmission electron microscopy investigations were performed to unravel the nanometer scale phenomena: a band of Pt and Pt/Ru nanoparticles was detected in the membrane adjacent to the cathode catalyst layer. Quantification of the elemental composition of several individual nanoparticles and the overall band area revealed that they stem from both anode and cathode catalyst layers. The results presented do not demonstrate any catastrophic failure but rather intermediate states during fuel cell operation and indications to proceed with targeted HT-PEMFC optimization.

A chemically activated graphene-encapsulated LiFePO4 composite for high-performance lithium ion batteries.

PubMed

Ha, Jeonghyun; Park, Seung-Keun; Yu, Seung-Ho; Jin, Aihua; Jang, Byungchul; Bong, Sungyool; Kim, In; Sung, Yung-Eun; Piao, Yuanzhe

2013-09-21

A composite of modified graphene and LiFePO4 has been developed to improve the speed of charging-discharging and the cycling stability of lithium ion batteries using LiFePO4 as a cathode material. Chemically activated graphene (CA-graphene) has been successfully synthesized via activation by KOH. The as-prepared CA-graphene was mixed with LiFePO4 to prepare the composite. Microscopic observation and nitrogen sorption analysis have revealed the surface morphologies of CA-graphene and the CA-graphene/LiFePO4 composite. Electrochemical properties have also been investigated after assembling coin cells with the CA-graphene/LiFePO4 composite as a cathode active material. Interestingly, the CA-graphene/LiFePO4 composite has exhibited better electrochemical properties than the conventional graphene/LiFePO4 composite as well as bare LiFePO4, including exceptional speed of charging-discharging and excellent cycle stability. That is because the CA-graphene in the composite provides abundant porous channels for the diffusion of lithium ions. Moreover, it acts as a conducting network for easy charge transfer and as a divider, preventing the aggregation of LiFePO4 particles. Owing to these properties of CA-graphene, LiFePO4 could demonstrate enhanced and stably long-lasting electrochemical performance.

New kind of injection-locked oscillator and its corresponding long-term stability control.

PubMed

Hong, Jun; Liu, An; Wang, Xiao-hu; Yao, Sheng-xing; Li, Zu-ling

2015-09-20

A new type of opto-electronic hybrid oscillator is proposed for the first time, to the best of our knowledge, and verified by experiments in this paper. Typical electronic oscillator-dielectric resonator oscillator as the first injection source is used to injection lock the first long-fiber loop-based opto-electronic oscillator (OEO); then its output is used to injection lock the second long-fiber opto-electronic oscillator. Using this method, low-phase noise output signal can be obtained. Experiments show that single side-band (SSB) phase noise of a 9.5 GHz oscillation signal at 10 kHz offset frequency decreases from -123 to -135  dBc/Hz after the first injection, then, through the second injection, the SSB phase noise drops down to -146  dBc/Hz. In order to solve the long-term stability problem of the above oscillator, a new stability-control circuit also is designed and verified by experiments. Experiments show that the Allan deviation decreases from 9.0×10(-11) to 2.2×10(-12) during 1 s after the long-term stability-control circuit being used.

A high-performance, cobalt-free cathode for intermediate-temperature solid oxide fuel cells with excellent CO2 tolerance

NASA Astrophysics Data System (ADS)

Bu, Yun-fei; Zhong, Qin; Chen, Dong-Chang; Chen, Yu; Lai, Samson Yuxiu; Wei, Tao; Sun, Hai-bin; Ding, Dong; Liu, Meilin

2016-07-01

Compared with some cobalt-rich cathodes which have been proven to yield high performance in SOFCs, interest in cobalt-free cathodes has increased due to their reduced thermal expansion coefficients (TECs), high structural stability, and CO2 tolerance. In this report, a new robust Co-free complex perovskite oxide PrLa0.4Ba0.6Fe0.8Zn0.2O5+δ (PLBFZ) has been synthesized and evaluated. The TEC is 14.4 × 10-6 K-1. With the introduction of Sm0.2Ce0.8O2 (SDC), the composite cathode PLBFZ-SDC with a mass ratio of 7:3 (PLBFZ-SDC 73) exhibited the best electrocatalytic activity for oxygen reduction under OCV conditions, with polarization values of 0.044, 0.079, 0.124, 0.251, 0.572, and 1.297 Ω cm-2 at 800, 750, 700, 650, 600, and 550 °C, respectively. The power densities of the cell were 1309, 1079, 788 and 586 mW cm-2 at 750, 700, 650, and 600 °C, respectively. Moreover, it appears to have good stability in air containing 1% CO2 (volume ratio) for 150 h based on Raman and polarization resistance (Rp) analysis. These results suggest that PLBFZ and its SDC composite are promising cathodes for IT-SOFCs.

Highly ordered and ultra-long carbon nanotube arrays as air cathodes for high-energy-efficiency Li-oxygen batteries

NASA Astrophysics Data System (ADS)

Yu, Ruimin; Fan, Wugang; Guo, Xiangxin; Dong, Shaoming

2016-02-01

Carbonaceous air cathodes with rational architecture are vital for the nonaqueous Li-O2 batteries to achieve large energy density, high energy efficiency and long cycle life. In this work, we report the cathodes made of highly ordered and vertically aligned carbon nanotubes grown on permeable Ta foil substrates (VACNTs-Ta) via thermal chemical vapour deposition. The VACNTs-Ta, composed of uniform carbon nanotubes with approximately 240 μm in superficial height, has the super large surface area. Meanwhile, the oriented carbon nanotubes provide extremely outstanding passageways for Li ions and oxygen species. Electrochemistry tests of VACNTs-Ta air cathodes show enhancement in discharge capacity and cycle life compared to those made from short-range oriented and disordered carbon nanotubes. By further combining with the LiI redox mediator that is dissolved in the tetraethylene dimethyl glycol based electrolytes, the batteries exhibit more than 200 cycles at the current density of 200 mA g-1 with a cut-off discharge capacity of 1000 mAh g-1, and their energy efficiencies increase from 50% to 82%. The results here demonstrate the importance of cathode construction for high-energy-efficiency and long-life Li-O2 batteries.

Materials Challenges and Opportunities of Lithium-ion Batteries for Electrical Energy Storage

NASA Astrophysics Data System (ADS)

Manthiram, Arumugam

2011-03-01

Electrical energy storage has emerged as a topic of national and global importance with respect to establishing a cleaner environment and reducing the dependence on foreign oil. Batteries are the prime candidates for electrical energy storage. They are the most viable near-term option for vehicle applications and the efficient utilization of intermittent energy sources like solar and wind. Lithium-ion batteries are attractive for these applications as they offer much higher energy density than other rechargeable battery systems. However, the adoption of lithium-ion battery technology for vehicle and stationary storage applications is hampered by high cost, safety concerns, and limitations in energy, power, and cycle life, which are in turn linked to severe materials challenges. This presentation, after providing an overview of the current status, will focus on the physics and chemistry of new materials that can address these challenges. Specifically, it will focus on the design and development of (i) high-capacity, high-voltage layered oxide cathodes, (ii) high-voltage, high-power spinel oxide cathodes, (iii) high-capacity silicate cathodes, and (iv) nano-engineered, high-capacity alloy anodes. With high-voltage cathodes, a critical issue is the instability of the electrolyte in contact with the highly oxidized cathode surface and the formation of solid-electrolyte interfacial (SEI) layers that degrade the performance. Accordingly, surface modification of cathodes with nanostructured materials and self-surface segregation during the synthesis process to suppress SEI layer formation and enhance the energy, power, and cycle life will be emphasized. With the high-capacity alloy anodes, a critical issue is the huge volume change occurring during the charge-discharge process and the consequent poor cycle life. Dispersion of the active alloy nanoparticles in an inactive metal oxide-carbon matrix to mitigate this problem and realize long cycle life will be presented.

Enhanced lifetime for thin-dielectric microdischarge-arrays operating in DC

NASA Astrophysics Data System (ADS)

Dussart, Remi; Felix, Valentin; Overzet, Lawrence; Aubry, Olivier; Stolz, Arnaud; Lefaucheux, Philippe; Gremi-Univ Orleans-Cnrs Collaboration; University Of Texas At Dallas Collaboration

2016-09-01

Micro-hollow cathode discharge arrays using silicon as the cathode have a very limited lifetime because the silicon bubbles and initiates micro-arcing. To avoid this destructive behavior, the same configuration was kept but, another material was selected for the cathode. Using micro and nanotechnologies ordinarily used in microelectronic and MEMS device fabrication, we made arrays of cathode boundary layer (CBL)-type microreactors consisting of nickel electrodes separated by a 6 µm thick SiO2 layer. Microdischarges were ignited in arrays of 100 µm diameter holes at different pressures (200750 Torr) in different gases. Electrical and optical measurements were made to characterize the arrays. Unlike the microdischarges produced using silicon cathodes, the Ni cathode discharges remain very stable with essentially no micro-arcing. DC currents between 50 and 900 µA flowed through each microreactor with a discharge voltage of typically 200 V. Stable V-I characteristics showing both the normal and abnormal regimes were observed and are consistent with the spread of the plasma over the cathode area. Due to their stability and lifetime, new applications of these DC, CBL-type microreactors can now be envisaged.

Surface modification of cathode material 0.5Li2MnO3·0.5LiMn1/3Ni1/3Co1/3O2 by alumina for lithium-ion batteries

NASA Astrophysics Data System (ADS)

Li, Yonghu; Chang, Xingping; Xu, Qunjie; Lai, Chunyan; Liu, Xinnuan; Yuan, Xiaolei; Liu, Haimei; Min, Yulin

2018-02-01

In an attempt to overcome the irreversible capacity loss occurred during the first cycle and stabilize the surface structure, an alumina coating layer has been triumphantly prepared on the surface of 0.5Li2MnO3·0.5LiMn1/3Ni1/3Co1/3O2 cathode material with different amounts (1, 2, and 3 wt%) through a simple hydrolysis reaction, followed by an annealing process. The results reveal that the coated materials have a higher crystallinity and the particles are evenly distributed. As a cathode material for lithium-ion batteries, the 2-wt% coated sample delivers initial discharge specific capacity of 211.7 mAh g-1 at a rate of 1 C between 2.0 and 4.8 V with an initial columbic efficiency of 73.2%. Meanwhile, it exhibits the highest discharge specific capacity of 206.2 mAh g-1 with 97.4% capacity retention after 100 cycles at and much elevated rate capability compared to uncoated material. The excellent cycling stability and more superior rate property can be ascribed to alumina coating layer, which has a surface stabilization effect on these cathode materials, lessening the dissolution of metal ions. The electrochemical impedance and cyclic voltammetry studies indicate that coated by alumina improved the kinetic performance for lithium-rich layered materials, showing a prospect for practical lithium battery application.

Electrochemical performance of La2O3/Li2O/TiO2 nano-particle coated cathode material LiFePO4.

PubMed

Wang, Hong; Yang, Chi; Liu, Shu-Xin

2014-09-01

Cathode material, LiFePO4 was modified by coating with a thin layer of La2O3/Li2O/TiO2 nano-particles for improving its performance for lithium ion batteries. The morphology and structure of the modified cathode material were characterized by powder X-ray diffraction, scanning electron microcopy and AES. The performance of the battery with the modified cathode material, including cycling stability, C-rate discharge was examined. The results show that the battery composed of the coated cathode materials can discharge at a large current density and show stable cycling performance in the range from 2.5 to 4.0 V. The rate of Li ion diffusion increases in the battery with the La2O3/Li2O/TiO2-coated LiFePO4 as a cathode and the coating layer may acts as a faster ion conductor (La(2/3-x)Li(3x)TiO3).

Nickel-based electrodeposits as potential cathode catalysts for hydrogen production by microbial electrolysis

NASA Astrophysics Data System (ADS)

Mitov, M.; Chorbadzhiyska, E.; Nalbandian, L.; Hubenova, Y.

2017-07-01

The development of cost-effective cathodes, operating at neutral pH and ambient temperatures, is a crucial challenge for the practical application of microbial electrolysis cell (MEC) technology. In this study, NiW and NiMo co-deposits produced by electroplating on Ni-foam are explored as cathodes in MEC. The fabricated electrodes exhibit higher corrosion stability and enhanced electrocatalytic activity towards hydrogen evolution reaction in neutral electrolyte compared to the bare Ni-foam. NiW/Ni-foam electrodes possess six times higher intrinsic catalytic activity, estimated from data obtained by linear voltammetry and chronoamperometry. The newly developed electrodes are applied as cathodes in single-chamber membrane-free MEC reactors, inoculated with wastewater and activated sludge from a municipal wastewater treatment plant. Cathodic hydrogen recovery of 79% and 89% by using NiW and NiMo cathodes, respectively, is achieved at applied voltage of 0.6 V. The obtained results reveal potential for practical application of used catalysts in MEC.

La0.3Sr0.2Mn0.1Zn0.4 oxide-Sm0.2Ce0.8O1.9 (LSMZ-SDC) nanocomposite cathode for low temperature SOFCs.

PubMed

Raza, Rizwan; Abbas, Ghazanfar; Liu, Qinghua; Patel, Imran; Zhu, Bin

2012-06-01

Nanocomposite based cathode materials compatible for low temperature solid oxide fuel cells (LTSOFCs) are being developed. In pursuit of compatible cathode, this research aims to synthesis and investigation nanocomposite La0.3Sr0.2Mn0.1Zn0.4 oxide-Sm0.2Ce0.8O1.9 (LSMZ-SDC) based system. The material was synthesized through wet chemical method and investigated for oxide-ceria composite based electrolyte LTSOFCs. Electrical property was studied by AC electrochemical impedance spectroscopy (EIS). The microstructure, thermal properties, and elemental analysis of the samples were characterized by TGA/DSC, XRD, SEM, respectively. The AC conductivity of cathode was obtained for 2.4 Scm(-1) at 550 degrees C in air. This cathode is compatible with ceria-based composite electrolytes and has improved the stability of the material in SOFC cathode environment.

Air breathing lithium power cells

DOEpatents

Farmer, Joseph C.

2014-07-15

A cell suitable for use in a battery according to one embodiment includes a catalytic oxygen cathode; a stabilized zirconia electrolyte for selective oxygen anion transport; a molten salt electrolyte; and a lithium-based anode. A cell suitable for use in a battery according to another embodiment includes a catalytic oxygen cathode; an electrolyte; a membrane selective to molecular oxygen; and a lithium-based anode.

Site-dependent effects of tDCS uncover dissociations in the communication network underlying the processing of visual search.

PubMed

Ball, Keira; Lane, Alison R; Smith, Daniel T; Ellison, Amanda

2013-11-01

The right posterior parietal cortex (rPPC) and the right frontal eye field (rFEF) form part of a network of brain areas involved in orienting spatial attention. Previous studies using transcranial magnetic stimulation (TMS) have demonstrated that both areas are critically involved in the processing of conjunction visual search tasks, since stimulation of these sites disrupts performance. This study investigated the effects of long term neuronal modulation to rPPC and rFEF using transcranial direct current stimulation (tDCS) with the aim of uncovering sharing of these resources in the processing of conjunction visual search tasks. Participants completed four blocks of conjunction search trials over the course of 45 min. Following the first block they received 15 min of either cathodal or anodal stimulation to rPPC or rFEF, or sham stimulation. A significant interaction between block and stimulation condition was found, indicating that tDCS caused different effects according to the site (rPPC or rFEF) and type of stimulation (cathodal, anodal, or sham). Practice resulted in a significant reduction in reaction time across the four blocks in all conditions except when cathodal tDCS was applied to rPPC. The effects of cathodal tDCS over rPPC are subtler than those seen with TMS, and no effect of tDCS was evident at rFEF. This suggests that rFEF has a more transient role than rPPC in the processing of conjunction visual search and is robust to longer-term methods of neuro-disruption. Our results may be explained within the framework of functional connectivity between these, and other, areas. Copyright © 2013 Elsevier Inc. All rights reserved.

An experimental investigation of cathode erosion in high current magnetoplasmadynamic arc discharges

NASA Astrophysics Data System (ADS)

Codron, Douglas A.

Since the early to mid 1960's, laboratory studies have demonstrated the unique ability of magnetoplasmadynamic (MPD) thrusters to deliver an exceptionally high level of specific impulse and thrust at large power processing densities. These intrinsic advantages are why MPD thrusters have been identified as a prime candidate for future long duration space missions, including piloted Mars, Mars cargo, lunar cargo, and other missions beyond low Earth orbit (LEO). The large total impulse requirements inherent of the long duration space missions demand the thruster to operate for a significant fraction of the mission burn time while requiring the cathodes to operate at 50 to 10,000 kW for 2,000 to 10,000 hours. The high current levels lead to high operational temperatures and a corresponding steady depletion of the cathode material by evaporation. This mechanism has been identified as the life-limiting component of MPD thrusters. In this research, utilizing subscale geometries, time dependent cathode axial temperature profiles under varying current levels (20 to 60 A) and argon gas mass flow rates (450 to 640 sccm) for both pure and thoriated solid tungsten cathodes were measured by means of both optical pyrometry and charged-coupled (CCD) camera imaging. Thoriated tungsten cathode axial temperature profiles were compared against those of pure tungsten to demonstrate the large temperature reducing effect lowered work function imparts by encouraging increased thermionic electron emission from the cathode surface. Also, Langmuir probing was employed to measure the electron temperature, electron density, and plasma potential near the "active zone" (the surface area of the cathode responsible for approximately 70% of the emitted current) in order to characterize the plasma environment and verify future model predictions. The time changing surface microstructure and elemental composition of the thoriated tungsten cathodes were analyzed using a scanning electron microscope (SEM) in conjunction with energy-dispersive X-ray spectroscopy (EDS). Such studies have provided a qualitative understanding of the typical pathways in which thorium diffuses and how it is normally redistributed along the cathode surface. Lastly, the erosion rates of both pure and thoriated tungsten cathodes were measured after various run times by use of an analytical scale. These measurements have revealed the ability of thoriated tungsten cathodes to run as long as that of pure tungsten but with significantly less material erosion.

Vertically aligned diamond-graphite hybrid nanorod arrays with superior field electron emission properties

NASA Astrophysics Data System (ADS)

Ramaneti, R.; Sankaran, K. J.; Korneychuk, S.; Yeh, C. J.; Degutis, G.; Leou, K. C.; Verbeeck, J.; Van Bael, M. K.; Lin, I. N.; Haenen, K.

2017-06-01

A "patterned-seeding technique" in combination with a "nanodiamond masked reactive ion etching process" is demonstrated for fabricating vertically aligned diamond-graphite hybrid (DGH) nanorod arrays. The DGH nanorod arrays possess superior field electron emission (FEE) behavior with a low turn-on field, long lifetime stability, and large field enhancement factor. Such an enhanced FEE is attributed to the nanocomposite nature of the DGH nanorods, which contain sp2-graphitic phases in the boundaries of nano-sized diamond grains. The simplicity in the nanorod fabrication process renders the DGH nanorods of greater potential for the applications as cathodes in field emission displays and microplasma display devices.

Long term in vitro stability of fully integrated wireless neural interfaces based on Utah slant electrode array

NASA Astrophysics Data System (ADS)

Sharma, Asha; Rieth, Loren; Tathireddy, Prashant; Harrison, Reid; Solzbacher, Florian

2010-02-01

We herein report in vitro functional stability and recording longevity of a fully integrated wireless neural interface (INI). The INI uses biocompatible Parylene-C as an encapsulation layer, and was immersed in phosphate buffered saline (PBS) for a period of over 150 days. The full functionality (wireless radio-frequency power, command, and signal transmission) and the ability of INI to record artificial action potentials even after 150 days of PBS soaking without any change in signal/noise amplitude constitutes a major milestone in long term stability, and evaluate the encapsulation reliability, functional stability, and potential usefulness for future chronic implants.

Optimization of scintillator loading with the tellurium-130 isotope for long-term stability

NASA Astrophysics Data System (ADS)

Duhamel, Lauren; Song, Xiaoya; Goutnik, Michael; Kaptanoglu, Tanner; Klein, Joshua; SNO+ Collaboration

2017-09-01

Tellurium-130 was selected as the isotope for the SNO + neutrinoless double beta decay search, as 130Te decays to 130Xe via double beta decay. Linear alkyl benzene(LAB) is the liquid scintillator for the SNO + experiment. To load tellurium into scintillator, it is combined with 1,2-butanediol to form an organometallic complex, commonly called tellurium butanediol (TeBD). This study focuses on maximizing the percentage of tellurium loaded into scintillator and evaluates the complex's long-term stability. Studies on the effect of nucleation due to imperfections in the detector's surface and external particulates were employed by filtration and induced nucleation. The impact of water on the stability of TeBD complex was evaluated by liquid-nitrogen sparging, variability in pH and induced humidity. Alternative loading methods were evaluated, including the addition of stability-inducing organic compounds. Samples of tellurium-loaded scintillator were synthesized, treated, and consistently monitored in a controlled environment. It was found that the hydronium ions cause precipitation in the loaded scintillator, demonstrating that water has a detrimental effect on long-term stability. Optimization of loaded scintillator stability can contribute to the SNO + double beta decay search.

The role of silica nanoparticles on long-term room-temperature stabilization of water-in-oil emulsions containing microalgae.

PubMed

Fernández, L; Scher, H; VanderGheynst, J S

2015-12-01

Prior research has demonstrated that microalgae can be stored for extended periods of time at room temperature in water-in-oil (W/O) emulsions stabilized by surface modified silica nanoparticles. However, little research has been done to examine the impact of nanoparticle concentration on emulsion stability. Such information is important for large-scale production of emulsions for microalgae storage and delivery. Studies were done to examine the impact of silica nanoparticle concentration on emulsion stability and identify the lower limit for nanoparticle concentration. Emulsion physical stability was determined using internal phase droplet size measurements and biological stability was evaluated using cell density measurements. The results demonstrate that nanoparticle concentrations as low as 0·5wt% in the oil phase can be used without significant losses in emulsion stability and microalgae viability. Stabilization technologies are needed for long-term storage and application of microalgae in agricultural-scale systems. While prior work has demonstrated that water-in-oil emulsions containing silica nanoparticles offer a promising solution for long-term microalgae storage at room temperature, little research has been done to examine the impact of nanoparticle concentration on emulsion stability. Here, we show the effects of silica nanoparticle concentration on maintaining physical stability of emulsions and sustaining viable cells. The results enable informed decisions to be made regarding production of emulsions containing silica nanoparticles and associated impacts on stabilization of microalgae. © 2015 The Society for Applied Microbiology.

Thermal Stability of FeS2 Cathode Material in "Thermal" Batteries: Effect of Dissolved Oxides in Molten Salt Electrolytes

NASA Astrophysics Data System (ADS)

Masset, Patrick J.

2008-09-01

The thermal stability of FeS2 cathode material for thermal batteries is investigated in the LiCl-KCl eutectic containing up to 10 wt% Li2O (used as anti-peak). The results show that the decomposition of pyrite shifts to higher temperatures in the presence of molten salts as the S2 gas is repressed by the liquid phase. For high lithium oxide contents the decomposition temperature of pyrite decreases by 100 °C. In addition Li2FeS2 as reaction product is evidenced whereas Li3Fe2S4 is expected from literature data.

Stability study of cermet-supported solid oxide fuel cells with bi-layered electrolyte

NASA Astrophysics Data System (ADS)

Zhang, Xinge; Gazzarri, Javier; Robertson, Mark; Decès-Petit, Cyrille; Kesler, Olivera

Performance and stability of five cermet-supported button-type solid oxide fuel cells featuring a bi-layered electrolyte (SSZ/SDC), an SSC cathode, and a Ni-SSZ anode, were analyzed using polarization curves, impedance spectroscopy, and post-mortem SEM observation. The cell performance degradation at 650 °C in H 2/air both with and without DC bias conditions was manifested primarily as an increase in polarization resistance, approximately at a rate of 2.3 mΩ cm 2 h -1 at OCV, suggesting a decrease in electrochemical kinetics as the main phenomenon responsible for the performance decay. In addition, the initial series resistance was about ten times higher than the calculated resistance corresponding to the electrolyte, reflecting a possible inter-reaction between the electrolyte layers that occurred during the sintering stage. In situ and ex situ sintered cathodes showed no obvious difference in cell performance or decay rate. The stability of the cells with and without electrical load was also investigated and no significant influence of DC bias was recorded. Based on the experimental results presented, we preliminarily attribute the performance degradation to electrochemical and microstructural degradation of the cathode.

Towards Synergistic Electrode-Electrolyte Design Principles for Nonaqueous Li-O[Formula: see text] batteries.

PubMed

Khetan, Abhishek; Krishnamurthy, Dilip; Viswanathan, Venkatasubramanian

2018-03-20

One route toward sustainable land and aerial transportation is based on electrified vehicles. To enable electrification in transportation, there is a need for high-energy-density batteries, and this has led to an enormous interest in lithium-oxygen batteries. Several critical challenges remain with respect to realizing a practical lithium-oxygen battery. In this article, we present a detailed overview of theoretical efforts to formulate design principles for identifying stable electrolytes and electrodes with the desired functionality and stability. We discuss design principles relating to electrolytes and the additional stability challenges that arise at the cathode-electrolyte interface. Based on a thermodynamic analysis, we discuss two important requirements for the cathode: the ability to nucleate the desired discharge product, Li[Formula: see text]O[Formula: see text], and the ability to selectively activate only this discharge product while suppressing lithium oxide, the undesired secondary discharge product. We propose preliminary guidelines for determining the chemical stability of the electrode and illustrate the challenge associated with electrode selection using the examples of carbon cathodes and transition metals. We believe that a synergistic design framework for identifying electrolyte-electrode formulations is needed to realize a practical Li-O[Formula: see text] battery.

Enhanced electrochemical performance and storage property of LiNi0.815Co0.15Al0.035O2 via Al gradient doping

NASA Astrophysics Data System (ADS)

Duan, Jianguo; Hu, Guorong; Cao, Yanbing; Tan, Chaopu; Wu, Ceng; Du, Ke; Peng, Zhongdong

2016-09-01

LiNi1-x-yCoxAlyO2 is a commonly used Ni-rich cathode material because of its relatively low cost, excellent rate capability and high gravimetric energy density. Surface modification is an efficient way to overcome the shortcomings of Ni-rich cathodes such as poor cycling stability and poor thermal stability. A high-powered concentration-gradient cathode material with an average composition of LiNi0.815Co0.15Al0.035O2 (LGNCAO) has been successfully synthesized by using spherical concentration-gradient Ni0.815Co0.15Al0.035(OH)2 (GNCA)as the starting material. An efficient design of the Al3+ precipitation method is developed, which enables obtaining spherical GNCA with ∼10 μm particle size and high tap density. In LGNCAO, the nickel and cobalt concentration decreases gradually whereas the aluminum concentration increases from the centre to the outer layer of each particle. Electrochemical performance and storage properties of LGNCAO have been investigated comparatively. The LGNCAO displays better electrochemical performance and improved storage stability than LNCAO.

Cathodal transcranial direct current stimulation can stabilize perception of movement: Evidence from the two-thirds power law illusion.

PubMed

Scocchia, Lisa; Bolognini, Nadia; Convento, Silvia; Stucchi, Natale

2015-11-16

Human movements conform to specific kinematic laws of motion. One of such laws, the "two-thirds power law", describes the systematic co-variation between curvature and velocity of body movements. Noticeably, the same law also influences the perception of moving stimuli: the velocity of a dot moving along a curvilinear trajectory is perceived as uniform when the dot kinematics complies with the two-thirds power law. Instead, if the dot moves at constant speed, its velocity is perceived as highly non-uniform. This dynamic visual illusion points to a strong coupling between action and perception; however, how this coupling is implemented in the brain remains elusive. In this study, we tested whether the premotor cortex (PM) and the primary visual cortex (V1) play a role in the illusion by means of transcranial Direct Current Stimulation (tDCS). All participants underwent three tDCS sessions during which they received active or sham cathodal tDCS (1.5mA) over PM or V1 of the left hemisphere. During tDCS, participants were required to adjust the velocity of a dot moving along an elliptical trajectory until it looked uniform across the whole trajectory. Results show that occipital tDCS decreases the illusion variability both within and across participants, as compared to sham tDCS. This means that V1 stimulation increases individual sensitivity to the illusory motion and also increases coherence across different observers. Conversely, the illusion seems resistant to tDCS in terms of its magnitude, with cathodal stimulation of V1 or PM not affecting the amount of the illusory effect. Our results provide evidence for strong visuo-motor coupling in visual perception: the velocity of a dot moving along an elliptical trajectory is perceived as uniform only when its kinematics closely complies to the same law of motion that constrains human movement production. Occipital stimulation by cathodal tDCS can stabilize such illusory percept. Copyright © 2015 Elsevier Ireland Ltd. All rights reserved.

Multimodal Characterization of the Morphology and Functional Interfaces in Composite Electrodes for Li-S Batteries by Li Ion and Electron Beams.

PubMed

Oleshko, Vladimir P; Herzing, Andrew A; Twedt, Kevin A; Griebel, Jared J; McClelland, Jabez J; Pyun, Jeffrey; Soles, Christopher L

2017-09-19

We report the characterization of multiscale 3D structural architectures of novel poly[sulfur-random-(1,3-diisopropenylbenzene)] copolymer-based cathodes for high-energy-density Li-S batteries capable of realizing discharge capacities >1000 mAh/g and long cycling lifetimes >500 cycles. Hierarchical morphologies and interfacial structures have been investigated by a combination of focused Li ion beam (LiFIB) and analytical electron microscopy in relation to the electrochemical performance and physicomechanical stability of the cathodes. Charge-free surface topography and composition-sensitive imaging of the electrodes was performed using recently introduced low-energy scanning LiFIB with Li + probe sizes of a few tens of nanometers at 5 keV energy and 1 pA probe current. Furthermore, we demonstrate that LiFIB has the ability to inject a certain number of Li cations into the material with nanoscale precision, potentially enabling control of the state of discharge in the selected area. We show that chemical modification of the cathodes by replacing the elemental sulfur with organosulfur copolymers significantly improves its structural integrity and compositional homogeneity down to the sub-5-nm length scale, resulting in the creation of (a) robust functional interfaces and percolated conductive pathways involving graphitic-like outer shells of aggregated nanocarbons and (b) extended micro- and mesoscale porosities required for effective ion transport.

Oxygen Release Induced Chemomechanical Breakdown of Layered Cathode Materials

DOE PAGES

Mu, Linqin; Lin, Ruoqian; Xu, Rong; ...

2018-04-18

Chemical and mechanical properties interplay on the nanometric scale and collectively govern the functionalities of battery materials. Understanding the relationship between the two can inform the design of battery materials with optimal chemomechanical properties for long-life lithium batteries. Herein, we report a mechanism of nanoscale mechanical breakdown in layered oxide cathode materials, originating from oxygen release at high states of charge under thermal abuse conditions. Here, we observe that the mechanical breakdown of charged Li 1-xNi 0.4Mn 0.4Co 0.2O 2 materials proceeds via a two-step pathway involving intergranular and intragranular crack formation. Owing to the oxygen release, sporadic phase transformationsmore » from the layered structure to the spinel and/or rocksalt structures introduce local stress, which initiates microcracks along grain boundaries and ultimately leads to the detachment of primary particles; i.e., intergranular crack formation. Furthermore, intragranular cracks (pores and exfoliations) form, likely due to the accumulation of oxygen vacancies and continuous phase transformations at the surfaces of primary particles. Finally, finite element modeling confirms our experimental observation that the crack formation is attributable to formation of oxygen vacancies, oxygen release, and phase transformations. This study is designed to directly observe the chemomechanical behavior of layered oxide cathode materials and provides a chemical basis for strengthening primary and secondary particles by stabilizing the oxygen anions in the lattice.« less

Oxygen Release Induced Chemomechanical Breakdown of Layered Cathode Materials

DOE Office of Scientific and Technical Information (OSTI.GOV)

Mu, Linqin; Lin, Ruoqian; Xu, Rong

Chemical and mechanical properties interplay on the nanometric scale and collectively govern the functionalities of battery materials. Understanding the relationship between the two can inform the design of battery materials with optimal chemomechanical properties for long-life lithium batteries. Herein, we report a mechanism of nanoscale mechanical breakdown in layered oxide cathode materials, originating from oxygen release at high states of charge under thermal abuse conditions. Here, we observe that the mechanical breakdown of charged Li 1-xNi 0.4Mn 0.4Co 0.2O 2 materials proceeds via a two-step pathway involving intergranular and intragranular crack formation. Owing to the oxygen release, sporadic phase transformationsmore » from the layered structure to the spinel and/or rocksalt structures introduce local stress, which initiates microcracks along grain boundaries and ultimately leads to the detachment of primary particles; i.e., intergranular crack formation. Furthermore, intragranular cracks (pores and exfoliations) form, likely due to the accumulation of oxygen vacancies and continuous phase transformations at the surfaces of primary particles. Finally, finite element modeling confirms our experimental observation that the crack formation is attributable to formation of oxygen vacancies, oxygen release, and phase transformations. This study is designed to directly observe the chemomechanical behavior of layered oxide cathode materials and provides a chemical basis for strengthening primary and secondary particles by stabilizing the oxygen anions in the lattice.« less

Impact of ALD Coating on Mn-rich Cathode Materials (Presentation)

DOE Office of Scientific and Technical Information (OSTI.GOV)

Santhanagopalan, S.

2013-06-01

LG Chem Power Inc. (LGCPI) and NREL have collaborated to demonstrate the scalability of the atomic layer deposition (ALD) coating process over the last 6 months, and the benefits of ALD coatings for long-term cycling and calendar life are being quantified. The objectives of this work are two-fold: 1) to evaluate the scalability of the process to coat LGCPI cathodes with alumina using the ALD technique, and 2) to demonstrate improvements in rate capability and life of ALD-coated LGCPI electrodes. NREL received samples of baseline material to be coated from LGCPI. NREL carried out ALD coating of the samples withmore » help from a subcontractor, ALD Nanosolutions. NREL fabricated cells from those samples for quick screening and feedback to ALD Nanosolutions. LGCPI is currently fabricating larger-format cells for further evaluation.« less

SERT II thrusters - Still ticking after eleven years

NASA Technical Reports Server (NTRS)

Kerslake, W. R.

1981-01-01

The Space Electric Rocket Test II (SERT II) spacecraft was launched in 1970 with a primary objective of demonstrating long-term operation of a space electric thruster system. An overview is presented of all the SERT II testing conducted during the time from 1970 to 1981. Thruster testing and interaction results are considered, taking into account ion beam thrusting, distant neutralization, and the plasma beam thrust. In a discussion of durability testing, attention is given to the main cathodes, the neutralizer cathodes, the main keeper insulator, the H.V. grid insulators, the neutralizer propellant tanks, and the main propellant tanks. The most important result of the study is related to the confidence gained that mercury bombardment ion thruster systems can be built and operated in space on a routine basis with the same lifetime and performance as measured in ground testing.

Full scale phosphoric acid fuel cell stack technology development

NASA Technical Reports Server (NTRS)

Christner, L.; Faroque, M.

1984-01-01

The technology development for phosphoric acid fuel cells is summarized. The preparation, heat treatment, and characterization of carbon composites used as bipolar separator plates are described. Characterization included resistivity, porosity, and electrochemical corrosion. High density glassy carbon/graphite composites performed well in long-term fuel cell endurance tests. Platinum alloy cathode catalysts and low-loaded platinum electrodes were evaluated in 25 sq cm cells. Although the alloys displayed an initial improvement, some of this improvement diminished after a few thousand hours of testing. Low platinum loading (0.12 mg/sq cm anodes and 0.3 mg/sq cm cathodes) performed nearly as well as twice this loading. A selectively wetproofed anode backing paper was tested in a 5 by 15 inch three-cell stack. This material may provide for acid volume expansion, acid storage, and acid lateral distribution.

Large variability of biochar stability and biochar properties

NASA Astrophysics Data System (ADS)

Lehmann, J.; Nguyen, B.; Hanley, K.; Enders, A.

2008-12-01

In general, charring or purposeful pyrolysis increases the stability of biomass. It is less clear, however, to what extent biochar properties influence its stability. Chemical and physical properties of biochars and biomass-derived black carbons (BC) vary greatly as a function of the type of biomass it was generated from and of the production temperature. We show that these properties greatly affect the stability of BC is a function of both these factors, with highly significant interactions. BC produced from corn stalks produced at 350°C decomposed much quicker when incubated at field capacity at 30°C for one year than those produced at 600°C. In contrast, there was hardly a difference noted between those two temperatures if oak was the precursor biomass. Such differences in labile carbon not only affect the proportion of stable carbon in BC, but also influence the quantification of long-term stability. Extrapolation from short-term decay to long-term stability may require prior knowledge about the decay rate of the labile fraction of BC. Some indications are provided for the short-term oxidation of BC.

Development of a High-Stability Microstrip-based L-band Radiometer for Ocean Salinity Measurements

NASA Technical Reports Server (NTRS)

Pellerano, Fernando A.; Horgan, Kevin A.; Wilson, William J.; Tanner, Alan B.

2004-01-01

The development of a microstrip-based L-band Dicke radiometer with the long-term stability required for future ocean salinity measurements to an accuracy of 0.1 psu is presented. This measurement requires the L-band radiometers to have calibration stabilities of less than or equal to 0.05 K over 2 days. This research has focused on determining the optimum radiometer requirements and configuration to achieve this objective. System configuration and component performance have been evaluated with radiometer test beds at both JPL and GSFC. The GSFC testbed uses a cryogenic chamber that allows long-term characterization at radiometric temperatures in the range of 70 - 120 K. The research has addressed several areas including component characterization as a function of temperature and DC bias, system linearity, optimum noise diode injection calibration, and precision temperature control of components. A breadboard radiometer, utilizing microstrip-based technologies, has been built to demonstrate this long-term stability.

Using the Sonoran Desert test site to monitor the long-term radiometric stability of the Landsat TM/ETM+ and Terra MODIS sensors

USGS Publications Warehouse

Angal, A.; Xiong, X.; Choi, T.; Chander, G.; Wu, A.

2009-01-01

Pseudo-invariant ground targets have been extensively used to monitor the long-term radiometric calibration stability of remote sensing instruments. The NASA MODIS Characterization Support Team (MCST), in collaboration with members from the U.S. Geological Survey (USGS) Earth Resources Observation and Science (EROS) Center, has previously demonstrated the use of pseudo-invariant ground sites for the long-term stability monitoring of Terra MODIS and Landsat 7 ETM+ sensors. This paper focuses on the results derived from observations made over the Sonoran Desert. Additionally, Landsat 5 TM data over the Sonoran Desert site were used to evaluate the temporal stability of this site. Top-ofatmosphere (TOA) reflectances were computed for the closely matched TM, ETM+, and MODIS spectral bands over selected regions of interest. The impacts due to different viewing geometries, or the effect of test site Bi-directional Reflectance Distribution Function (BRDF), are also presented. ?? 2009 SPIE.

Long-term maintenance of the carrier-envelope phase coherence of a femtosecond laser.

PubMed

Kim, Eok Bong; Lee, Jae-Hwan; Lee, Won-Kyu; Luu, Tran Trung; Nam, Chang Hee

2010-12-06

The long-term carrier-envelope phase (CEP) coherence of a femtosecond laser with same pulse-to-pulse CEP value, obtained using the direct locking method, is demonstrated by employing a quasi-common-path interferometer (QPI). For the evaluation of the CEP stability, the phase noise properties of a femtosecond laser with the CEP stabilized using a QPI are compared with those obtained using a Mach-Zehnder f-2f interferometer, for which the phase power spectral density and the Allan deviation were calculated from the beat signals of the interferometers. With the improved CEP stability, the long-term CEP coherent signal with an accumulated phase noise well below 1 radian can be maintained for more than 56 hours, i.e., the CEP coherence is preserved without a phase cycle slip for more than 1.6 × 10(13) pulses at a repetition rate of 80 MHz. The relative stability is also estimated to be approximately 1.4 × 10(-22) at a central wavelength of 790 nm.

Influence of the dynamic Stark effect on long-term frequency stability of a self-oscillating magnetometer with laser-pumped alkali atoms

NASA Astrophysics Data System (ADS)

Baranov, A. A.; Ermak, S. V.; Kulachenkov, N. K.; Petrenko, M. V.; Sagitov, E. A.; Semenov, V. V.

2017-11-01

This paper presents the results of investigation Stark shift effect influence on the long-term stability of a dual scheme of quantum magnetometers. Such scheme allows suppressing Stark shift components when a certain pumping light polarization is applied. As a result, long-term stability of a quantum sensor increases. However, when low-frequency (LF) and microwave fields are attached to a single vapor cell a coherence circulation in hyperfine structure of alkali atoms takes place. Physical origin of this effect is associated with the so called “dressed” atom theory, when atom is “dressed” by LF field. It yields in multiphoton absorption and resonance frequency shift. First estimates for this shift based on density matrix evolution formalism are provided in the paper.

Ab initio investigation of barium-scandium-oxygen coatings on tungsten for electron emitting cathodes

NASA Astrophysics Data System (ADS)

Vlahos, Vasilios; Booske, John H.; Morgan, Dane

2010-02-01

Microwave, x-ray, and radio-frequency radiation sources require a cathode emitting electrons into vacuum. Thermionic B-type dispenser cathodes consist of BaxOz coatings on tungsten (W), where the surface coatings lower the W work function and enhance electron emission. The new and promising class of scandate cathodes modifies the B-type surface through inclusion of Sc, and their superior emissive properties are also believed to stem from the formation of a low work function surface alloy. In order to better understand these cathode systems, density-functional theory (DFT)-based ab initio modeling is used to explore the stability and work function of BaxScyOz on W(001) monolayer-type surface structures. It is demonstrated how surface depolarization effects can be calculated easily using ab initio calculations and fitted to an analytic depolarization equation. This approach enables the rapid extraction of the complete depolarization curve (work function versus coverage relation) from relatively few DFT calculations, useful for understanding and characterizing the emitting properties of novel cathode materials. It is generally believed that the B-type cathode has some concentration of Ba-O dimers on the W surface, although their structure is not known. Calculations suggest that tilted Ba-O dimers are the stable dimer surface configuration and can explain the observed work function reduction corresponding to various dimer coverages. Tilted Ba-O dimers represent a new surface coating structure not previously proposed for the activated B-type cathode. The thermodynamically stable phase of Ba and O on the W surface was identified to be the Ba0.25O configuration, possessing a significantly lower Φ value than any of the Ba-O dimer configurations investigated. The identification of a more stable Ba0.25O phase implies that if Ba-O dimers cover the surface of emitting B-type cathodes, then a nonequilibrium steady state must dominate the emitting surface. The identification of a stable and low work function Ba0.25Sc0.25O structure suggests that addition of Sc to the B-type cathode surface could form this alloy structure under operating conditions, leading to improved cathode performance and stability. Detailed comparison to previous experimental results of BaxScyOz on W surface coatings are made to both validate the modeling and aid in interpretation of experimental data. The studies presented here demonstrate that ab initio methods are powerful for understanding the fundamental physics of electron emitting materials systems and can potentially aid in the development of improved cathodes.

Long-term stable active mount for reflective optics

NASA Astrophysics Data System (ADS)

Reinlein, C.; Brady, A.; Damm, C.; Mohaupt, M.; Kamm, A.; Lange, N.; Goy, M.

2016-07-01

We report on the development of an active mount with an orthogonal actuator matrix offering a stable shape optimization for gratings or mirrors. We introduce the actuator distribution and calculate the accessible Zernike polynomials from their actuator influence function. Experimental tests show the capability of the device to compensate for aberrations of grating substrates as we report measurements of a 110x105 mm2 and 220x210 mm2 device With these devices, we evaluate the position depending aberrations, long-term stability shape results, and temperature-induced shape variations. Therewith we will discuss potential applications in space telescopes and Earth-based facilities where long-term stability is mandatory.

Highly Stable Sr-Free Cobaltite-Based Perovskite Cathodes Directly Assembled on a Barrier-Layer-Free Y2 O3 -ZrO2 Electrolyte of Solid Oxide Fuel Cells.

PubMed

Ai, Na; Li, Na; Rickard, William D A; Cheng, Yi; Chen, Kongfa; Jiang, San Ping

2017-03-09

Direct assembly is a newly developed technique in which a cobaltite-based perovskite (CBP) cathode can be directly applied to a barrier-layer-free Y 2 O 3 -ZrO 2 (YSZ) electrolyte with no high-temperature pre-sintering steps. Solid oxide fuel cells (SOFCs) based on directly assembled CBPs such as La 0.6 Sr 0.4 Co 0.2 Fe 0.8 O 3-δ show high performance initially but degrade rapidly under SOFC operation conditions at 750 °C owing to Sr segregation and accumulation at the electrode/electrolyte interface. Herein, the performance and interface of Sr-free CBPs such as LaCoO 3-δ (LC) and Sm 0.95 CoO 3-δ (SmC) and their composite cathodes directly assembled on YSZ electrolyte was studied systematically. The LC electrode underwent performance degradation, most likely owing to cation demixing and accumulation of La on the YSZ electrolyte under polarization at 500 mA cm -2 and 750 °C. However, the performance and stability of LC electrodes could be substantially enhanced by the formation of LC-gadolinium-doped ceria (GDC) composite cathodes. Replacement of La by Sm increased the cell stability, and doping of 5 % Pd to form Sm 0.95 Co 0.95 Pd 0.05 O 3-δ (SmCPd) significantly improved the electrode activity. An anode-supported YSZ-electrolyte cell with a directly assembled SmCPd-GDC composite electrode exhibited a peak power density of 1.4 W cm -2 at 750 °C, and an excellent stability at 750 °C for over 240 h. The higher stability of SmC as compared to that of LC is most likely a result of the lower reactivity of SmC with YSZ. This study demonstrates the new opportunities in the design and development of intermediate-temperature SOFCs based on the directly assembled high-performance and durable Sr-free CBP cathodes. © 2017 Wiley-VCH Verlag GmbH & Co. KGaA, Weinheim.

Development of porous carbon foam polymer electrolyte membrane fuel cell

NASA Astrophysics Data System (ADS)

Kim, Jin; Cunningham, Nicolas

In order to prove the feasibility of using porous carbon foam material in a polymer electrolyte membrane fuel cell (PEMFC), a single PEMFC is constructed with a piece of 80PPI (pores per linear inch) Reticulated Vitreous Carbon (RVC) foam at a thickness of 3.5 mm employed in the cathode flow-field. The cell performance of such design is compared with that of a conventional fuel cell with serpentine channel design in the cathode and anode flow-fields. Experimental results show that the RVC foam fuel cell not only produces comparative power density to, but also offers interesting benefits over the conventional fuel cell. A 250 h long term test conducted on a RVC foam fuel cell shows that the durability and performance stability of the material is deemed to be acceptable. Furthermore, a parametric study is conducted on single RVC foam fuel cells. Effect of geometrical and material parameters of the RVC foam such as PPI and thickness and operating conditions such as pressure, temperature, and stoichiometric ratio of the reactant gases on the cell performance is experimentally investigated in detail. The single cell with the 80PPI RVC foam exhibits the best performance, especially if the thinnest foam (3.5 mm) is used. The cell performance improves with increasing the operating gauge pressure from 0 kPa to 80 kPa and the operating temperature from 40 °C to 60 °C, but deteriorates as it further increases to 80 °C. The cell performance improves as the stoichiometric ratio of air increases from 1.5 to 4.5; however, the improvement becomes marginal when it is raised above 3.0. On the other hand, changing the stoichiometric ratio of hydrogen does not have a significant impact on the cell performance.

Note: Improving long-term stability of hot-wire anemometer sensors by means of annealing

DOE Office of Scientific and Technical Information (OSTI.GOV)

Lundström, H., E-mail: hans.lundstrom@hig.se

2015-08-15

Annealing procedures for hot-wire sensors of platinum and platinum-plated tungsten have been investigated experimentally. It was discovered that the two investigated sensor metals behave quite differently during the annealing process, but for both types annealing may improve long-term stability considerably. Measured drift of sensors both without and with prior annealing is presented. Suggestions for suitable annealing temperatures and times are given.

Long-term Stabilization of Disturbed Slopes Resulting from Construction Operations

DOT National Transportation Integrated Search

2018-01-01

Highway construction disturbs soil, which must be stabilized to prevent migration of soil particles into water bodies. Stabilization is enforced by law, regulation, and a permit system. Stabilization is most efficiently attained by reestablishment of...

Calcium cation enhanced cathode/electrolyte interface property of Li2FeSiO4/C cathode for lithium-ion batteries with long-cycling life

NASA Astrophysics Data System (ADS)

Qu, Long; Li, Mingtao; Tian, Xiaolu; Liu, Pei; Yi, Yikun; Yang, Bolun

2018-03-01

Currently, the cycle performance at low rate is one of the most critical factor for realizing practical applications of Li2FeSiO4/C as a cathode of the lithium-ion batteries. To meet this challenge, calcium (Ca)-doped Li2FeSiO4/C is prepared by using the sol-gel method with soluble Li, Fe, Si and Ca sources. X-ray diffraction, scanning electron microscopy, energy dispersive X-ray spectroscopy, transmission electron microscopy and X-ray photoelectron spectroscopy measurements are carried out to determine the crystal structures, morphologies, particle sizes and chemical valence states of the resulting products. Rietveld refinement confirms that Ca-doped Li2FeSiO4 has a monoclinic P21/n structure and that a Ca cation occupies the Fe site in the Li2FeSiO4 lattice. The grain size of Ca-doped Li2FeSiO4 is approximately 20 nm and the nanoparticles are interconnected tightly with amorphous carbon layer. As a cathode material for the lithium-ion batteries, Li2Fe0.97Ca0.03SiO4/C delivers a high discharge capacity of 186 mAh g-1 at a 0.5 C rate. Its capacity retention after the 100th cycle reaches 87%, which increases by 25 percentage points compared with Li2FeSiO4/C. The Li2Fe0.97Ca0.03SiO4/C cathode exhibits good rate performance, with corresponding discharge capacities of 170, 157, 144 and 117 mAh g-1 at 1 C, 2 C, 5 C and 10 C rates, respectively. In summary, the improvement of the electrochemical performance can be attributed to a coefficient of the strengthened crystal structure stability during Li+ deintercalation-intercalation and restrained side reactions between electrode and electrolyte.

The development and characterization of a first generation carbon nanotube x-ray based microbeam radiation therapy system

NASA Astrophysics Data System (ADS)

Hadsell, Michael John, Jr.

Microbeam radiation therapy (MRT) is a new type of cancer treatment currently being studied at scattered synchrotron sites throughout the world. It has been shown to be capable of ablating aggressive brain tumors in rats while almost completely sparing the surrounding normal tissue. This promising technique has yet to find its way to the clinic, however, because the radiobiological mechanisms behind its efficacy are still largely unknown. This is partly due to the lack of a compact device that could facilitate more large scale research. The challenges inherent to creating a compact device lie within the structure of MRT, which uses parallel arrays of ultra high-dose, orthovoltage, microplanar beams on the order of 100mum thick and separated by four to ten times their width. Because of focal spot limitations, current commercial orthovoltage devices are simply not capable of creating such arrays at dose rates high enough for effective treatment while maintaining the microbeam pattern necessary to retain the high therapeutic ratio of the technique. Therefore, the development of a compact MRT device using carbon nanotube (CNT) cathode based X-ray technology is presented here. CNT cathodes have been shown to be capable of creating novel focal spot arrays on a single anode while being robust enough for long-term use in X-ray tubes. Using these cathodes, an X-ray tube with a single focal line has been created for the delivery of MRT dose distributions in radiobiological studies on small animals. In this work, the development process and final design of this specialized device will be detailed, along with the optimization and stabilization of its use for small animal studies. In addition, a detailed characterization of its final capabilities will be given; including a comprehensive measurement of its X-ray focal line dimensions, a description and evaluation of its collimator alignment and microbeam dimensions, and a full-scale phantom-based quantification of its dosimetric output. Finally, future project directions will be described briefly along with plans for a second generation device. Based on the results of this work, it is the author's belief that compact CNT MRT devices have definite commercialization potential for radiobiological research.

A High-Performance Lithium-Ion Capacitor Based on 2D Nanosheet Materials.

PubMed

Li, Shaohui; Chen, Jingwei; Cui, Mengqi; Cai, Guofa; Wang, Jiangxin; Cui, Peng; Gong, Xuefei; Lee, Pooi See

2017-02-01

Lithium-ion capacitors (LICs) are promising electrical energy storage systems for mid-to-large-scale applications due to the high energy and large power output without sacrificing long cycle stability. However, due to the different energy storage mechanisms between anode and cathode, the energy densities of LICs often degrade noticeably at high power density, because of the sluggish kinetics limitation at the battery-type anode side. Herein, a high-performance LIC by well-defined ZnMn 2 O 4 -graphene hybrid nanosheets anode and N-doped carbon nanosheets cathode is presented. The 2D nanomaterials offer high specific surface areas in favor of a fast ion transport and storage with shortened ion diffusion length, enabling fast charge and discharge. The fabricated LIC delivers a high specific energy of 202.8 Wh kg -1 at specific power of 180 W kg -1 , and the specific energy remains 98 Wh kg -1 even when the specific power achieves as high as 21 kW kg -1 . © 2016 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Na2.5Fe1.75(SO4)3/Ketjen/rGO: An advanced cathode composite for sodium ion batteries

NASA Astrophysics Data System (ADS)

Goñi, A.; Iturrondobeitia, A.; Gil de Muro, I.; Lezama, L.; Rojo, T.

2017-11-01

An advanced cathode composite Na2.5Fe1.75(SO4)3/Ketjen/rGO for sodium ion batteries has been prepared, joining together the excellent electrochemical properties of the three components: off stoichiometric iron sulfate alluaudite, Ketjen Black carbon and reduced graphene oxide (rGO). This electrode material has been exhaustively characterized by XRD, thermogravimetric analysis, Raman spectroscopy and SEM and TEM microscopy. The study has demonstrated that a high quality electrode material has been designed containing a porous sulfate core properly coated by interweaved rGO fibers and Ketjen Black nanoparticles. The electrochemical study has revealed an excellent performance providing specific capacities close to the theoretical one at 1C. Additionally, this composite has shown a very good rate capability and a great cycling stability for at least 200 cycles maintaining a coulombic efficiency of 96%. The post mortem analysis, which includes EPR and XPS measurements, has demonstrated that the carbonaceous coating on the composite generates a stable and protective SEI layer over the active material guaranteeing a successful performance during a long cycle life.

An Integrated, Layered-Spinel Composite Cathode for Energy Storage Applications

NASA Technical Reports Server (NTRS)

Hagh, Nader; Skandan, Ganesh

2012-01-01

At low operating temperatures, commercially available electrode materials for lithium-ion batteries do not fully meet the energy and power requirements for NASA fs exploration activities. The composite cathode under development is projected to provide the required energy and power densities at low temperatures and its usage will considerably reduce the overall volume and weight of the battery pack. The newly developed composite electrode material can provide superior electrochemical performance relative to a commercially available lithium cobalt system. One advantage of using a composite cathode is its higher energy density, which can lead to smaller and lighter battery packs. In the current program, different series of layered-spinel composite materials with at least two different systems in an integrated structure were synthesized, and the volumetric and gravimetric energy densities were evaluated. In an integrated network of a composite electrode, the effect of the combined structures is to enhance the capacity and power capabilities of the material to levels greater than what is possible in current state-of-the-art cathode systems. The main objective of the current program is to implement a novel cathode material that meets NASA fs low temperature energy density requirements. An important feature of the composite cathode is that it has at least two components (e.g., layered and spinel) that are structurally integrated. The layered material by itself is electrochemically inactive; however, upon structural integration with a spinel material, the layered material can be electrochemically activated, thereby delivering a large amount of energy with stable cycling. A key aspect of the innovation has been the development of a scalable process to produce submicronand micron-scale particles of these composite materials. An additional advantage of using such a composite electrode material is its low irreversible loss (.5%), which is primarily due to the unique activation of the composite. High columbic efficiency (greater than 99%) upon cycling may indicate the formation of a stable SEI (solid-electrolyte interface) layer, which can contribute to long cycle life. The innovation in the current program, when further developed, will enable the system to maintain high energy and power densities at low temperatures, improve efficiency, and further stabilize and enhance the safety of the cell.

A Gel-Polymer Sn-C/LiMn0.5Fe0.5PO4 Battery Using a Fluorine-Free Salt.

PubMed

Di Lecce, Daniele; Fasciani, Chiara; Scrosati, Bruno; Hassoun, Jusef

2015-09-30

Safety and environmental issues, because of the contemporary use of common liquid electrolytes, fluorinated salts, and LiCoO2-based cathodes in commercial Li-ion batteries, might be efficiently mitigated by employing alternative gel-polymer battery configurations and new electrode materials. Herein we study a lithium-ion polymer cell formed by combining a LiMn0.5Fe0.5PO4 olivine cathode, prepared by simple solvothermal pathway, a nanostructured Sn-C anode, and a LiBOB-containing PVdF-based gel electrolyte. The polymer electrolyte, here analyzed in terms of electrochemical stability by impedance spectroscopy (EIS) and voltammetry, reveals full compatibility for cell application. The LiBOB electrolyte salt and the electrochemically delithiaded Mn0.5Fe0.5PO4 have a higher thermal stability compared to conventional LiPF6 and Li0.5CoO2, as confirmed by thermogravimetric analysis (TGA) and by galvanostatic cycling at high temperature. LiMn0.5Fe0.5PO4 and Sn-C, showing in lithium half-cell a capacity of about 120 and 350 mAh g(-1), respectively, within the gelled electrolyte configuration are combined in a full Li-ion polymer battery delivering a stable capacity of about 110 mAh g(-1), with working voltage ranging from 2.8 to 3.6 V.

Long-term lithium-ion battery performance improvement via ultraviolet light treatment of the graphite anode

DOE PAGES

An, Seong Jin; Li, Jianlin; Sheng, Yangping; ...

2016-01-01

Effects of ultraviolet (UV) light on dried graphite anodes were investigated in terms of the cycle life of lithium ion batteries. The time variations for the UV treatment were 0 (no treatment), 20, 40, and 60 minutes. UV-light-treated graphite anodes were assembled for cycle life tests in pouch cells with pristine Li 1.02Ni 0.50Mn 0.29Co 0.19O 2 (NMC 532) cathodes. UV treatment for 40 minutes resulted in the highest capacity retention and the lowest resistance after the cycle life testing. X-ray photoelectron spectroscopy (XPS) and contact angle measurements on the graphite anodes showed changes in surface chemistry and wetting aftermore » the UV treatment. XPS also showed increases in solvent products and decreases in salt products on the SEI surface when UV-treated anodes were used. In conclusion, the thickness of the surface films and their compositions on the anodes and cathodes were also estimated using survey scans and snapshots from XPS depth profiles.« less

Modulating Memory Performance in Healthy Subjects with Transcranial Direct Current Stimulation Over the Right Dorsolateral Prefrontal Cortex.

PubMed

Smirni, Daniela; Turriziani, Patrizia; Mangano, Giuseppa Renata; Cipolotti, Lisa; Oliveri, Massimiliano

2015-01-01

The role of the Dorsolateral Prefrontal Cortex (DLPFC) in recognition memory has been well documented in lesion, neuroimaging and repetitive Transcranial Magnetic Stimulation (rTMS) studies. The aim of the present study was to investigate the effects of transcranial Direct Current Stimulation (tDCS) over the left and the right DLPFC during the delay interval of a non-verbal recognition memory task. 36 right-handed young healthy subjects participated in the study. The experimental task was an Italian version of Recognition Memory Test for unknown faces. Study included two experiments: in a first experiment, each subject underwent one session of sham tDCS and one session of left or right cathodal tDCS; in a second experiment each subject underwent one session of sham tDCS and one session of left or right anodal tDCS. Cathodal tDCS over the right DLPFC significantly improved non verbal recognition memory performance, while cathodal tDCS over the left DLPFC had no effect. Anodal tDCS of both the left and right DLPFC did not modify non verbal recognition memory performance. Complementing the majority of previous studies, reporting long term memory facilitations following left prefrontal anodal tDCS, the present findings show that cathodal tDCS of the right DLPFC can also improve recognition memory in healthy subjects.

Capacity fade of LiNi(1-x-y)CoxAlyO2 cathode for lithium-ion batteries during accelerated calendar and cycle life test. I. Comparison analysis between LiNi(1-x-y)CoxAlyO2 and LiCoO2 cathodes in cylindrical lithium-ion cells during long term storage test

NASA Astrophysics Data System (ADS)

Watanabe, Shoichiro; Kinoshita, Masahiro; Nakura, Kensuke

2014-02-01

Ni-based LiNi(1-x-y)CoxAlyO2 (NCA) and LiCoO2 (LCO) cathode materials taken out of lithium-ion cells after storage for 2 years at 45 °C were analyzed by various spectroscopic techniques. X-ray photoelectron spectroscopy exhibited that there was no difference between NCA and LCO. On the other hand, scanning transmission electron microscopy-electron energy-loss spectroscopy demonstrated there was a remarkably large difference between the two cathode materials. Ni-L2,3 energy-loss near-edge structure (ELNES) spectra of the NCA showed a peak at about 856.5 eV, which was assigned to trivalent nickel, was maintained even after storage, indicating that the NCA had no significant change in its surface structure during storage. On the other hand, in the Co-L2,3 ELNES spectra of the LCO a peak at about 782.5 eV, which was assigned to trivalent cobalt, significantly shifted to the lower energies after storage. These results suggest that crystal structure change of the active material surface is a predominant reason of deterioration during the storage test.

Microbial fuel cells with highly active aerobic biocathodes

NASA Astrophysics Data System (ADS)

Milner, Edward M.; Popescu, Dorin; Curtis, Tom; Head, Ian M.; Scott, Keith; Yu, Eileen H.

2016-08-01

Microbial fuel cells (MFCs), which convert organic waste to electricity, could be used to make the wastewater infrastructure more energy efficient and sustainable. However, platinum and other non-platinum chemical catalysts used for the oxygen reduction reaction (ORR) at the cathode of MFCs are unsustainable due to their high cost and long-term degradation. Aerobic biocathodes, which use microorganisms as the biocatalysts for cathode ORR, are a good alternative to chemical catalysts. In the current work, high-performing aerobic biocathodes with an onset potential for the ORR of +0.4 V vs. Ag/AgCl were enriched from activated sludge in electrochemical half-cells poised at -0.1 and + 0.2 V vs. Ag/AgCl. Gammaproteobacteria, distantly related to any known cultivated gammaproteobacterial lineage, were identified as dominant in these working electrode biofilms (23.3-44.3% of reads in 16S rRNA gene Ion Torrent libraries), and were in very low abundance in non-polarised control working electrode biofilms (0.5-0.7%). These Gammaproteobacteria were therefore most likely responsible for the high activity of biologically catalysed ORR. In MFC tests, a high-performing aerobic biocathode increased peak power 9-fold from 7 to 62 μW cm-2 in comparison to an unmodified carbon cathode, which was similar to peak power with a platinum-doped cathode at 70 μW cm-2.

Thin film passivation of laser generated 3D micro patterns in lithium manganese oxide cathodes

NASA Astrophysics Data System (ADS)

Pröll, J.; Kohler, R.; Bruns, M.; Oberst, V.; Weidler, P. G.; Heißler, S.; Kübel, C.; Scherer, T.; Prang, R.; Seifert, H. J.; Pfleging, W.

2013-03-01

The increasing need for long-life lithium-ion batteries requires the further development of electrode materials. Especially on the cathode side new materials or material composites are needed to increase the cycle lifetime. On the one hand, spinel-type lithium manganese oxide is a promising candidate to be used as cathode material due to its non-toxicity, low cost and good thermal stability. On the other hand, the spinel structure suffers from change in the oxidation state of manganese during cycling which is also accompanied by loss of active material into the liquid electrolyte. The general trend is to enhance the active surface area of the cathode in order to increase lithium-ion mobility through the electrode/electrolyte interface, while an enhanced surface area will also promote chemical degradation. In this work, laser microstructuring of lithium manganese oxide thin films was applied in a first step to increase the active surface area. This was done by using 248 nm excimer laser radiation and chromium/quartz mask imaging techniques. In a second step, high power diode laser-annealing operating at a wavelength of 940 nm was used for forming a cubic spinel-like battery phase. This was verified by means of Raman spectroscopy and cyclic voltammetric measurements. In a last step, the laser patterned thin films were coated with indium tin oxide (ITO) layers with a thickness of 10 nm to 50 nm. The influence of the 3D surface topography as well as the ITO thickness on the electrochemical performance was studied by cyclic voltammetry. Post-mortem studies were carried out by using scanning electron microscopy and focused ion beam analysis.

Comprehensive characterization and understanding of micro-fuel cells operating at high methanol concentrations.

PubMed

Gago, Aldo S; Esquivel, Juan-Pablo; Sabaté, Neus; Santander, Joaquín; Alonso-Vante, Nicolas

2015-01-01

We report on the analysis of the performance of each electrode of an air-breathing passive micro-direct methanol fuel cell (µDMFC) during polarization, stabilization and discharge, with CH3OH (2-20 M). A reference electrode with a microcapillary was used for separately measuring the anode the cathode potential. Information about the open circuit potential (OCP), the voltage and the mass transport related phenomena are available. Using 2 M CH3OH, the anode showed mass transport problems. With 4 and 6 M CH3OH both electrodes experience this situation, whereas with 10 and 20 M CH3OH the issue is attributed to the cathode. The stabilization and fuel consumption time depends mainly on the cathode performance, which is very sensitive to fuel crossover. The exposure to 20 M CH3OH produced a loss in performance of more than 75% of the highest power density (16.3 mW·cm(-2)).

In Situ-Formed Hierarchical Metal-Organic Flexible Cathode for High-Energy Sodium-Ion Batteries.

PubMed

Huang, Ying; Fang, Chun; Zeng, Rui; Liu, Yaojun; Zhang, Wang; Wang, Yanjie; Liu, Qingju; Huang, Yunhui

2017-12-08

Metal-organic compounds are a family of electrode materials with structural diversity and excellent thermal stability for rechargeable batteries. Here, we fabricated a hierarchical nanocomposite with metal-organic cuprous tetracyanoquinodimethane (CuTCNQ) in a 3 D conductive carbon nanofibers (CNFs) network by in situ growth, and evaluated it as flexible cathode for sodium-ion batteries (SIBs). CuTCNQ in such flexible composite electrode is able to exhibit a high capacity of 252 mAh g -1 at 0.1 C and highly reversible stability for 1200 cycles within the voltage range of 2.5-4.1 V (vs. Na + /Na). A high specific energy of 762 Wh kg -1 was obtained with high average potential of 3.2 V (vs. Na + /Na). The in situ-formed electroactive metal-organic composites with tailored nanoarchitecture provide a promising alternative choice for high-performance cathode materials in SIBs with high energy. © 2017 Wiley-VCH Verlag GmbH & Co. KGaA, Weinheim.

Cathodic electrodeposition of ceramic and organoceramic materials. Fundamental aspects.

PubMed

Zhitomirsky, I

2002-03-29

Electrodeposition of ceramic materials can be performed by electrophoretic (EPD) or electrolytic (ELD) deposition. Electrophoretic deposition is achieved via motion of charged particles towards an electrode under an applied electric field. Electrolytic deposition produces colloidal particles in cathodic reactions for subsequent deposition. Various electrochemical strategies and deposition mechanisms have been developed for electrodeposition of ceramic and organoceramic films, and are discussed in the present article. Electrode-position of ceramic and organoceramic materials includes mass transport, accumulation of particles near the electrode and their coagulation to form a cathodic deposit. Various types of interparticle forces that govern colloidal stability in the absence and presence of processing additives are discussed. Novel theoretical contributions towards an interpretation of particle coagulation near the electrode surface are reviewed. Background information is given on the methods of particle charging, stabilization of colloids in aqueous and non-aqueous media, electrophoretic mobility of ceramic particles and polyelectrolytes, and electrode reactions. This review also covers recent developments in the electrodeposition of ceramic and organoceramic materials.

Effect of an InxGa1-xAs-GaAs blocking heterocathode metal contact on the GaAs TED operation

NASA Astrophysics Data System (ADS)

Arkusha, Yu. V.; Prokhorov, E. D.; Storozhenko, I. P.

2004-09-01

The frequency dependence of the generation efficiency of an mm- -nn:In:InxGaGa1-1-xAs- As-nn:GaAs-:GaAs-nn++:GaAs TED with the 2.5-mm long active region is calculated. The optimum values - which yield the diode maximum generation efficiency - for the :GaAs TED with the 2.5-mm long active region is calculated. The optimum values - which yield the diode maximum generation efficiency - for the nn:In:InxGaGa1-1-xAs cathode length, the cathode concentration of ionized impurities, and the height of the potential barrier on metal contact are determined.As cathode length, the cathode concentration of ionized impurities, and the height of the potential barrier on metal contact are determined.

Long-term stability of radiotherapy dosimeters calibrated at the Polish Secondary Standard Dosimetry Laboratory.

PubMed

Ulkowski, Piotr; Bulski, Wojciech; Chełmiński, Krzysztof

2015-10-01

Unidos 10001, Unidos E (10008/10009) and Dose 1 electrometers from 14 radiotherapy centres were calibrated 3-4 times over a long period of time, together with Farmer type (PTW 30001, 30013, Nuclear Enterprises 2571 and Scanditronix-Wellhofer FC65G) cylindrical ionization chambers and plane-parallel type chambers (PTW Markus 23343 and Scanditronix-Wellhofer PPC05). On the basis of the long period of repetitive establishing of calibration coefficients for the same electrometers and ionization chambers, the accuracy of electrometers and the long-term stability of ionization chambers were examined. All measurements were carried out at the same laboratory, by the same staff, according to the same IAEA recommendations. A good accuracy and long-term stability of the dosimeters used in Polish radiotherapy centres was observed. These values were within 0.1% for electrometers and 0.2% for the chambers with electrometers. Furthermore, these values were not observed to vary over time. The observations confirm the opinion that the requirement of calibration of the dosimeters more often than every 2 years is not justified. Copyright © 2015 Elsevier Ltd. All rights reserved.

Development of a high-performance composite cathode for LT-SOFC

NASA Astrophysics Data System (ADS)

Lee, Byung Wook

Solid Oxide Fuel Cell (SOFC) has drawn considerable attention for decades due to its high efficiency and low pollution, which is made possible since chemical energy is directly converted to electrical energy through the system without combustion. However, successful commercialization of SOFC has been delayed due to its high production cost mainly related with using high cost of interconnecting materials and the other structural components required for high temperature operation. This is the reason that intermediate (IT) or low temperature (LT)-SOFC operating at 600~800°C or 650°C and below, respectively, is of particular significance because it allows the wider selection of cheaper materials such as stainless steel for interconnects and the other structural components. Also, extended lifetime and system reliability are expected due to less thermal stress through the system with reduced temperature. More rapid start-up/shut-down procedure is another advantage of lowering the operating temperatures. As a result, commercialization of SOFC will be more viable. However, there exists performance drop with reduced operating temperature due to increased polarization resistances from the electrode electrochemical reactions and decreased electrolyte conductivity. Since ohmic polarization of the electrolyte can be significantly reduced with state-of-the art thin film technology and cathode polarization has more drastic effect on total SOFC electrochemical performance than anode polarization as temperature decreases, development of the cathode with high performance operating at IT or LT range is thus essential. On the other hand, chemical stability of the cathode and its chemical compatibility with the electrolyte should also be considered for cathode development since instability and incompatibility of the cathode will also cause substantial performance loss. Based on requirements of the cathode mentioned above, in this study, several chemico-physical approaches were carried out to develop a high-performance composite cathode, in particular, for LT-SOFC operating 650°C and below since stability and compatibility of the materials in interest are secured at low temperatures. First, a nano-sized pyrochlore bismuth ruthenate (Bi2Ru 2O7 or BRO7 shortly), one of the promising cathode materials, was successfully synthesized using glycine-nitrate combustion (GNC) route. Stoichiometric Bi2Ru2O7 without any impurity phase was achieved with considerably improved processing condition, leading to the crystallite size of ~24nm in diameter. Even though the resulting powder tends to agglomerate, resulting in overall 200~400nm size range, it still showed better quality than the one prepared by solid state (SS) reaction route followed by extra milling steps such as vibro-milling and sonication for further particle size reduction. Glycine-to-nitrate (G/N) ratio was found to play a critical role in determining the reaction temperature and reaction duration, thus phase purity and particle morphology (particle size, shape, and agglomeration etc). Composite cathodes of such prepared BRO7 (GNC BRO7) combined with SS erbia-stabilized bismuth oxide, Bi1.6Er0.4O3 or ESB, showed better electrochemical performance than vibro-milled BRO7 (VM BRO7)-SS ESB. ASR values of 0.123Ocm2 at 700°C and 4.59cOm 2 at 500°C, respectively, were achieved, which follows well the trend of particle size effect on performance of composite cathodes. Additionally, the number of processing steps (thus time) was reduced by GNC route. Several issues in regard to synthesis process and characteristics of BRO7 material itself will be addressed in this dissertation. Secondly, a unique in-situ composite cathode synthesis was successfully developed and applied for BRO7-ESB composite cathodes to improve percolation and to reduce agglomeration of each phase inside the cathode so that the effective triple phase boundary (TPB) length was extended. To disperse and stabilize ESB powder in de-ionized (DI) water, zeta potential profile of ESB powder in DI water as a function of pH was first achieved. The effect of a dispersant (ammonium citrate dibasic) on the stability of ESB powder dispersed in DI water was also investigated. Knowledge of BRO7 wet chemical synthesis from previous study was utilized for final product of in-situ BRO7-ESB composite cathodes. Such prepared composite particles were characterized and the electrochemical performance of in-situ BRO7-ESB composite cathodes was examined as well. Performance enhancement was observed so that ASR values of 0.097Ocm2 and 3.58Ocm2 were achieved at 700°C and 500°C, respectively, which were 19% and 22% improvement, respectively compared to those of conventionally mixed composite cathodes of BRO7-ESB. Finally, a highly controlled nanostructured BRO7-ESB composite cathode was developed by infiltration of BRO7 onto ESB scaffolds to maximize the effective TPB length, to improve the connectivity of ESB phase inside the cathode for better oxygen-ion diffusion, and to minimize delamination between the electrolyte and cathode layers. ESB scaffolds were first established by adding a graphite pore-former and controlling heat treatment condition. Nano-sized BRO7 particles were successfully created on the surface of previously formed ESB scaffold by infiltration of concentrated (Bi, Ru) nitrate solution followed by the optimized heat treatment. Such prepared composite cathodes exhibited superior electrochemical performance to conventionally made BRO7-ESB composite cathodes and even better than GNC BRO7-SS ESB developed in this dissertation, e.g. 0.073Ocm2 at 700°C and 1.82Ocm2 at 500°C, respectively. This cathode system was revealed to be highly competitive among all the reported composite cathodes consisting of the same or different materials prepared by various processing techniques. It was demonstrated that the extended TPB length from continuous network of BRO7 nanoparticles and better connectivity of ESB scaffolds enabled the outstanding performance. Moreover, de-lamination of cathode from the electrolyte was prevented thanks to improved adhesion between ESB scaffolds and ESB electrolyte. Dissociative adsorption of oxygen gas were proposed to be the dominant rate-determining process for the overall oxygen reduction reaction at low temperatures (500-600°C) whereas all of the constituting sub-reactions such as oxygen gas dissociative adsorption, oxygen ion diffusion towards TPB region, and oxygen ion incorporation were found to play roles competitively in the overall reaction at relatively high operating temperature (650-700°C) based on analysis of impedance spectra.

Long term stability of Oligo (dT) 25 magnetic beads for the expression analysis of Euglena gracilis for long term space projects

NASA Astrophysics Data System (ADS)

Becker, Ina; Strauch, Sebastian M.; Hauslage, Jens; Lebert, Michael

2017-05-01

The unicellular freshwater flagellate Euglena gracilis has a highly developed sensory system. The cells use different stimuli such as light and gravity to orient themselves in the surrounding medium to find areas for optimal growth. Due to the ability to produce oxygen and consume carbon dioxide, Euglena is a suitable candidate for life support systems. Participation in a long-term space experiment would allow for the analysis of changes and adaptations to the new environment, and this could bring new insights into the mechanism of perception of gravity and the associated signal transduction chain. For a molecular analysis of transcription patterns, an automated system is necessary, capable of performing all steps from taking a sample, processing it and generating data. One of the developmental steps is to find long-term stable reagents and materials and test them for stability at higher-than-recommended temperature conditions during extended storage time. We investigated the usability of magnetic beads in an Euglena specific lysis buffer after addition of the RNA stabilizer Dithiothreitol over 360 days and the lysis buffer with the stabilizer alone over 455 days at the expected storage temperature of 19 °C. We can claim that the stability is not impaired at all after an incubation period of over one year. This might be an interesting result for researchers who have to work under non-standard lab conditions, as in biological or medicinal fieldwork.

Effect of desliming of sulphide-rich mill tailings on the long-term strength of cemented paste backfill.

PubMed

Ercikdi, Bayram; Baki, Hakan; İzki, Muhammet

2013-01-30

This paper presents the effect of desliming on the short- and long-term strength, stability and rheological properties of cemented paste backfill (CPB) produced from two different mill tailings. A 28-day unconfined compressive strength (UCS) of ≥1.0 MPa and the maintenance of stability over 224 days of curing were selected as the design criteria for the evaluation of paste backfill performance. Desliming induced some changes in the physical, chemical, mineralogical and rheological properties of the tailings. CPB mixture of the deslimed tailings achieved the required consistency at a lower water to cement ratio. The short-term UCSs of CPB samples of the deslimed tailings were found to be 30-100% higher than those samples of the reference tailings at all the binder dosages and curing times. CPB samples of the deslimed tailings achieved the long-term stability at relatively low binder dosages (e.g. 5 wt% c.f. ≥6.1% for the reference tailings). It was also estimated that desliming could allow a 13.4-23.1% reduction in the binder consumption depending apparently on the inherent characteristics of the tailings. Over the curing period, generation of sulphate and acid by the oxidation of pyrite present in the tailings was also monitored to correlate with the strength losses observed in the long term. Scanning electron microscope (SEM) and Mercury Intrusion Porosimetry (MIP) analyses provided an insight into the microstructure of CPB and the formation of secondary mineral phases (i.e. gypsum) confirming the beneficial effect of desliming. These findings suggest that desliming can be suitably exploited for CPB of sulphide-rich mill tailings to improve the strength and stability particularly in the long term and to reduce binder consumption. Copyright © 2012 Elsevier Ltd. All rights reserved.

Development of a Hard X-ray Beam Position Monitor for Insertion Device Beams at the APS

NASA Astrophysics Data System (ADS)

Decker, Glenn; Rosenbaum, Gerd; Singh, Om

2006-11-01

Long-term pointing stability requirements at the Advanced Photon Source (APS) are very stringent, at the level of 500 nanoradians peak-to-peak or better over a one-week time frame. Conventional rf beam position monitors (BPMs) close to the insertion device source points are incapable of assuring this level of stability, owing to mechanical, thermal, and electronic stability limitations. Insertion device gap-dependent systematic errors associated with the present ultraviolet photon beam position monitors similarly limit their ability to control long-term pointing stability. We report on the development of a new BPM design sensitive only to hard x-rays. Early experimental results will be presented.

A highly conductive poly(3,4-ethylenedioxythiophene):poly(styrene sulfonate) film with the solvent bath treatment by dimethyl sulfoxide as cathode for polymer tantalum capacitor

NASA Astrophysics Data System (ADS)

Ma, Xiaopin; Wang, Xiuyu; Li, Mingxiu; Chen, Tongning; Zhang, Hao; Chen, Qiang; Ding, Bonan; Liu, Yanpeng

2016-06-01

The highly conductive poly(3,4-ethylenedioxythiophene):poly(styrene sulfonate) (PEDOT:PSS) films were prepared on porous tantalum pentoxide surface as cathode for polymer tantalum capacitors (PTC). The electrical performances of PTC with PEDOT:PSS films as cathode were optimized by dimethyl sulfoxide (DMSO) bath treatment. With the DMSO-bath treatment of PTC, the equivalent series resistance (ESR) of PTC decreased from 25 mΩ to 9 mΩ. The ultralow ESR led to better capacitance-frequency performance. The device reliability investigation revealed the enhanced environmental stability of PTC. The enhanced performances were attributed to the conductivity improvement of PEDOT:PSS cathode films and the removal of excess PSS from PEDOT:PSS films.

An Aurivillius Oxide Based Cathode with Excellent CO2 Tolerance for Intermediate-Temperature Solid Oxide Fuel Cells.

PubMed

Zhu, Yinlong; Zhou, Wei; Chen, Yubo; Shao, Zongping

2016-07-25

The Aurivillius oxide Bi2 Sr2 Nb2 MnO12-δ (BSNM) was used as a cobalt-free cathode for intermediate-temperature solid oxide fuel cells (IT-SOFCs). To the best of our knowledge, the BSNM oxide is the only alkaline-earth-containing cathode material with complete CO2 tolerance that has been reported thus far. BSNM not only shows favorable activity in the oxygen reduction reaction (ORR) at intermediate temperatures but also exhibits a low thermal expansion coefficient, excellent structural stability, and good chemical compatibility with the electrolyte. These features highlight the potential of the new BSNM material as a highly promising cathode material for IT-SOFCs. © 2016 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Insights into the structural effects of layered cathode materials for high voltage sodium-ion batteries

DOE PAGES

Xu, Gui -Liang; Amine, Rachid; Xu, Yue -Feng; ...

2017-06-08

Cathode materials are critical to the energy density, power density and safety of sodium-ion batteries (SIBs). Herein, we performed a comprehensive study to elucidate and exemplify the interplay mechanism between phase structures, interfacial microstrain and electrochemical properties of layered-structured Na xNi 1/3Co 1/3Mn 1/3O 2 cathode materials for high voltage SIBs. The electrochemical test results showed that Na xNi 1/3Co 1/3Mn 1/3O 2 with an intergrowth P2/O3/O1 structure demonstrates better electrochemical performance and better thermal stability than Na xNi 1/3Co 1/3Mn 1/3O 2 with P2/O3 binary-phase integration and Na xNi 1/3Co 1/3Mn 1/3O 2 where only the P phase ismore » dominant. This result is caused by the distinct interfacial microstrain development during the synthesis and cycling of the P2/O3/O1 phase. In operando high energy X-ray diffraction further revealed that the intergrowth P2/O1/O3 cathode can inhibit the irreversible P2–O2 phase transformation and simultaneously improve the structure stability of the O3 and O1 phases during cycling. Here, we believe that interfacial microstrain can serve as an indispensable bridge to guide future design and synthesis of high performance SIB cathode materials and other high energy battery materials.« less

Spatially resolved surface valence gradient and structural transformation of lithium transition metal oxides in lithium-ion batteries.

PubMed

Liu, Hanshuo; Bugnet, Matthieu; Tessaro, Matteo Z; Harris, Kristopher J; Dunham, Mark J R; Jiang, Meng; Goward, Gillian R; Botton, Gianluigi A

2016-10-26

Layered lithium transition metal oxides are one of the most important types of cathode materials in lithium-ion batteries (LIBs) that possess high capacity and relatively low cost. Nevertheless, these layered cathode materials suffer structural changes during electrochemical cycling that could adversely affect the battery performance. Clear explanations of the cathode degradation process and its initiation, however, are still under debate and not yet fully understood. We herein systematically investigate the chemical evolution and structural transformation of the LiNi x Mn y Co 1-x-y O 2 (NMC) cathode material in order to understand the battery performance deterioration driven by the cathode degradation upon cycling. Using high-resolution electron energy loss spectroscopy (HR-EELS) we clarify the role of transition metals in the charge compensation mechanism, particularly the controversial Ni 2+ (active) and Co 3+ (stable) ions, at different states-of-charge (SOC) under 4.6 V operation voltage. The cathode evolution is studied in detail from the first-charge to long-term cycling using complementary diagnostic tools. With the bulk sensitive 7 Li nuclear magnetic resonance (NMR) measurements, we show that the local ordering of transition metal and Li layers (R3[combining macron]m structure) is well retained in the bulk material upon cycling. In complement to the bulk measurements, we locally probe the valence state distribution of cations and the surface structure of NMC particles using EELS and scanning transmission electron microscopy (STEM). The results reveal that the surface evolution of NMC is initiated in the first-charging step with a surface reduction layer formed at the particle surface. The NMC surface undergoes phase transformation from the layered structure to a poor electronic and ionic conducting transition-metal oxide rock-salt phase (R3[combining macron]m → Fm3[combining macron]m), accompanied by irreversible lithium and oxygen loss. In addition to the electrochemical cycling effect, electrolyte exposure also shows non-negligible influence on cathode surface degradation. These chemical and structural changes of the NMC cathode could contribute to the first-cycle coulombic inefficiency, restrict the charge transfer characteristics and ultimately impact the cell capacity.

Robust Low-Cost Cathode for Commercial Applications

NASA Technical Reports Server (NTRS)

Patterson, Michael J.

2007-01-01

Under funding from the NASA Commercial Technology Office, a cathode assembly was designed, developed, fabricated, and tested for use in plasma sources for ground-based materials processing applications. The cathode development activity relied on the large prior NASA investment and successful development of high-current, high-efficiency, long-life hollow cathodes for use on the International Space Station Plasma Contactor System. The hollow cathode was designed and fabricated based on known engineering criteria and manufacturing processes for compatibility with the requirements of the plasma source. The transfer of NASA GRC-developed hollow cathode technology for use as an electron emitter in the commercial plasma source is anticipated to yield a significant increase in process control, while eliminating the present issues of electron emitter lifetime and contamination.

On the nanostructuring and catalytic promotion of intermediate temperature solid oxide fuel cell (IT-SOFC) cathodes

NASA Astrophysics Data System (ADS)

Serra, José M.; Buchkremer, Hans-Peter

Solid oxide fuel cells (SOFCs) are highly efficient energy converters for both stationary and mobile purposes. However, their market introduction still demands the reduction of manufacture costs and one possible way to reach this goal is the decrease of the operating temperatures, which entails the improvement of the cathode electrocatalytic properties. An ideal cathode material may have mixed ionic and electronic conductivity as well as proper catalytic properties. Nanostructuring and catalytic promotion of mixed conducting perovskites (e.g. La 0.58Sr 0.4Fe 0.8Co 0.2O 3- δ) seem to be promising approaches to overcoming cathode polarization problems and are briefly illustrated here. The preparation of nanostructured cathodes with relatively high surface area and enough thermal stability enables to improve the oxygen exchange rate and therefore the overall SOFC performance. A similar effect was obtained by catalytic promoting the perovskite surface, allowing decoupling the catalytic and ionic-transport properties in the cathode design. Noble metal incorporation may improve the reversibility of the reduction cycles involved in the oxygen reduction. Under the cathode oxidizing conditions, Pd seems to be partially dissolved in the perovskite structure and as a result very well dispersed.

The electrochemical exploration of double carbon-wrapped Na3V2(PO4)3: Towards long-time cycling and superior rate sodium-ion battery cathode

NASA Astrophysics Data System (ADS)

Li, Sijie; Ge, Peng; Zhang, Chenyang; Sun, Wei; Hou, Hongshuai; Ji, Xiaobo

2017-10-01

Na3V2(PO4)3 (NVP) is a very promising cathode material in sodium ion battery for rapidly emerging large-scale energy storage with its classical 3D NASCION structure. However, the cycling life and rate performances are restricted its low electronic conductivity. To overcome these, the double carbon-wrapped Na3V2(PO4)3 composite is firstly designed through rheological phase approach, delivering enhanced electrochemical properties. The unique double carbon layers are composed of uniform amorphous carbons as protecting framework for stabilizing the structure, as well as the graphitized carbon sheets playing the role of conductive network for better electronic conductivity. This double carbon-wrapped Na3V2(PO4)3 composite exhibits a high reversible capacity of 99.8 mAh g-1 over 500 cycles at 1 C (110 mA g-1), yielding the coulombic efficiency of ∼99.8%. Meanwhile, it displays an initial capacity of 73 mAh g-1 at 100 C and remains 55 mAh g-1 at an ultra-rate of 200 C. Even after cycling at 200 C over 12 000 cycles, the Na+-storage capacity of 40 mAh g-1 with a retention of 72.7% is still obtained, highlighting its excellent long cycling life and remarkable rate performances.

Direct-current cathodic vacuum arc system with magnetic-field mechanism for plasma stabilization.

PubMed

Zhang, H-S; Komvopoulos, K

2008-07-01

Filtered cathodic vacuum arc (FCVA) deposition is characterized by plasma beam directionality, plasma energy adjustment via substrate biasing, macroparticle filtering, and independent substrate temperature control. Between the two modes of FCVA deposition, namely, direct current (dc) and pulsed arc, the dc mode yields higher deposition rates than the pulsed mode. However, maintaining the dc arc discharge is challenging because of its inherent plasma instabilities. A system generating a special configuration of magnetic field that stabilizes the dc arc discharge during film deposition is presented. This magnetic field is also part of the out-of-plane magnetic filter used to focus the plasma beam and prevent macroparticle film contamination. The efficiency of the plasma-stabilizing magnetic-field mechanism is demonstrated by the deposition of amorphous carbon (a-C) films exhibiting significantly high hardness and tetrahedral carbon hybridization (sp3) contents higher than 70%. Such high-quality films cannot be produced by dc arc deposition without the plasma-stabilizing mechanism presented in this study.

CW injection locking for long-term stability of frequency combs

NASA Astrophysics Data System (ADS)

Williams, Charles; Quinlan, Franklyn; Delfyett, Peter J.

2009-05-01

Harmonically mode-locked semiconductor lasers with external ring cavities offer high repetition rate pulse trains while maintaining low optical linewidth via long cavity storage times. Continuous wave (CW) injection locking further reduces linewidth and stabilizes the optical frequencies. The output can be stabilized long-term with the help of a modified Pound-Drever-Hall feedback loop. Optical sidemode suppression of 36 dB has been shown, as well as RF supermode noise suppression of 14 dB for longer than 1 hour. In addition to the injection locking of harmonically mode-locked lasers requiring an external frequency source, recent work shows the viability of the injection locking technique for regeneratively mode-locked lasers, or Coupled Opto-Electronic Oscillators (COEO).

Facile preparation of MnO2 nanorods and evaluation of their supercapacitive characteristics

NASA Astrophysics Data System (ADS)

Aghazadeh, Mustafa; Asadi, Maryam; Maragheh, Mohammad Ghannadi; Ganjali, Mohammad Reza; Norouzi, Parviz; Faridbod, Farnoush

2016-02-01

The first time pulsed base (OH-) electrogeneration to the cathodic electrodeposition of MnO2 in nitrate bath was applied and MnO2 nanorods were obtained. The deposition experiments were performed under a pulse current mode with typical on-times and off-times (ton = 10 ms and toff = 50 ms) and a peak current density of 2 mA cm-2 (Ia = 2 mA cm-2). The structural characterization with XRD and FTIR revealed that the prepared MnO2 is composed of both α and γ phases. Morphological evaluations through SEM and TEM revealed that the prepared MnO2 contains nanorods of relative uniform structures (with an average diameter of 50 nm). The electrochemical measurements through cyclic voltammetry and charge-discharge techniques revealed that the prepared MnO2 nanostructures reveal an excellent capacitive behavior with specific capacitance values of 242, 167 and 98 F g-1 under the applied current densities of 2, 5 and 10 A g-1, respectively. Also, excellent long-term cycling stabilities of 94.8%, 89.1%, and 76.5% were observed after 1000 charge-discharge cycles at the current densities of 2, 5 and 10 A g-1.

Synthesis of TiC Nanoparticles Anchored on Hollow Carbon Nanospheres for Enhanced Polysulfide Adsorption in Li-S Batteries.

PubMed

Cao, Bokai; Chen, Yong; Li, De; Yin, Lihong; Mo, Yan

2016-12-08

A novel spatial confinement strategy based on a carbon/TiO 2 /carbon sandwich structure is proposed to synthesize TiC nanoparticles anchored on hollow carbon nanospheres (TiC@C) through a carbothermal reduction reaction. During the synthesis process, two carbon layers not only serve as reductant to convert TiO 2 into TiC nanoparticles, but also create a spatial confinement to suppress the aggregation of TiO 2 , resulting in the formation of well-dispersed TiC nanoparticles. This unique TiC@C structure shows an outstanding long-term cycling stability at high rates owing to the strong physical and chemical adsorption of lithium polysulfides (i.e., a high capacity of 732.6 mA h g -1 at 1600 mA g -1 ) and it retains a capacity of 443.2 mA h g -1 after 1000 cycles, corresponding to a decay rate of only 0.0395 % per cycle. Therefore, this unique TiC@C composite could be considered as an important candidate for the cathode material in Li-S batteries. © 2016 Wiley-VCH Verlag GmbH & Co. KGaA, Weinheim.

Evaluation of Polymer Hermetically Sealed Tantalum Capacitors

NASA Technical Reports Server (NTRS)

Teverovsky, Alexander A.

2014-01-01

Polymer cathode tantalum capacitors have lower ESR (equivalent series resistance) compared to other types of tantalum capacitors and for this reason have gained popularity in the electronics design community. Their use allows improved performance of power supply systems along with substantial reduction of size and weight of the components used. However, these parts have poor thermal stability and can degrade in humid environments. Polymer hermetically sealed (PHS) capacitors avoid problems related to environmental degradation of molded case parts and can potentially replace current wet and solid hermetically sealed capacitors. In this work, PHS capacitors manufactured per DLA LAM DWG#13030 are evaluated for space applications. Several lots of capacitors manufactured over period from 2010 to 2014 were tested for the consistency of performance, electrical and thermal characteristics, highly accelerated life testing, and robustness under reverse bias and random vibration conditions. Special attention was given to analysis of leakage currents and the effect of long-term high temperature storage on capacitors in as is condition and after hermeticity loss. The results show that PHS capacitors might be especially effective for low-temperature applications or for system requiring a cold start-up. Additional screening and qualification testing have been recommended to assure the necessary quality of capacitors for space projects.

Facile formation of 2D Co2P@Co3O4 microsheets through in-situ toptactic conversion and surface corrosion: Bifunctional electrocatalysts towards overall water splitting

NASA Astrophysics Data System (ADS)

Yao, Lihua; Zhang, Nan; Wang, Yin; Ni, Yuanman; Yan, Dongpeng; Hu, Changwen

2018-01-01

Exploring efficient non-precious electrocatalysts for both the hydrogen evolution reaction (HER) and oxygen evolution reaction (OER) is crucial for many renewable energy conversion processes. In this work, we report that 2D Co2P@Co3O4 microsheets can be prepared through an in-situ toptactic conversion from single-crystal β-Co(OH)2 microplatelets, associated with a surface phosphatization and corrosion process. The resultant Co2P@Co3O4 2D hybrid materials can further serve as self-supported bifunctional catalytic electrodes to drive the overall water splitting for HER and OER simultaneously, with low overpotentials and high long-term stability. Furthermore, a water electrolyzer based on Co2P@Co3O4 hybrid as both anode and cathode is fabricated, which achieves 10 mA cm-2 current at only 1.57 V during water splitting process. Therefore, this work provides a facile strategy to obtain 2D Co2P-based micro/nanostructures, which act as low-cost and highly active electrocatalysts towards overall water splitting application.

Polyanion-Type Electrode Materials for Sodium-Ion Batteries.

PubMed

Ni, Qiao; Bai, Ying; Wu, Feng; Wu, Chuan

2017-03-01

Sodium-ion batteries, representative members of the post-lithium-battery club, are very attractive and promising for large-scale energy storage applications. The increasing technological improvements in sodium-ion batteries (Na-ion batteries) are being driven by the demand for Na-based electrode materials that are resource-abundant, cost-effective, and long lasting. Polyanion-type compounds are among the most promising electrode materials for Na-ion batteries due to their stability, safety, and suitable operating voltages. The most representative polyanion-type electrode materials are Na 3 V 2 (PO 4 ) 3 and NaTi 2 (PO 4 ) 3 for Na-based cathode and anode materials, respectively. Both show superior electrochemical properties and attractive prospects in terms of their development and application in Na-ion batteries. Carbonophosphate Na 3 MnCO 3 PO 4 and amorphous FePO 4 have also recently emerged and are contributing to further developing the research scope of polyanion-type Na-ion batteries. However, the typical low conductivity and relatively low capacity performance of such materials still restrict their development. This paper presents a brief review of the research progress of polyanion-type electrode materials for Na-ion batteries, summarizing recent accomplishments, highlighting emerging strategies, and discussing the remaining challenges of such systems.

Glucose oxidase bioanodes for glucose conversion and H2O2 production for horseradish peroxidase biocathodes in a flow through glucose biofuel cell design

NASA Astrophysics Data System (ADS)

Abreu, Caroline; Nedellec, Yannig; Ondel, Olivier; Buret, Francois; Cosnier, Serge; Le Goff, Alan; Holzinger, Michael

2018-07-01

Bioelectrocatalytic carbon nanotube pellets comprising glucose oxidase (GOx) at the anode and horseradish peroxidase (HRP) at the cathode were integrated in a glucose/H2O2 flow-through fuel cell setup. The porous bioelectrodes, separated with a cellulose membrane, were assembled in a design allowing the fuel/electrolyte flow through the entire fuel cell with controlled direction. An air saturated 5 mmol L-1 glucose solution was directed through the anode where glucose is used for power conversion and for the enzymatic generation of hydrogen peroxide supplying the HRP biocathode with its substrate. This configuration showed an open circuit voltage (OCV) of 0.6 V and provided 0.7 ± 0.035 mW at 0.41 V. Furthermore, different charge/discharge cycles at 500 Ω and 3 kΩ were applied to show the long term stability of this setup producing 290 μW h (1.04 J) of energy after 48 h. The biofuel cell design further allows a convenient assembly of several glucose biofuel cells in reduced volumes and its connection in parallel or in series.

A nanoporous PdCo alloy as a highly active electrocatalyst for the oxygen-reduction reaction and formic acid electrooxidation.

PubMed

Xu, Caixia; Liu, Yunqing; Zhang, Huan; Geng, Haoran

2013-11-01

A nanoporous (NP) PdCo alloy with uniform structure size and controllable bimetallic ratio was fabricated simply by one-step mild dealloying of a PdCoAl precursor alloy. The as-made alloy consists of a nanoscaled bicontinuous network skeleton with interconnected hollow channels that extend in all three dimensions. With a narrow ligament size distribution around 5 nm, the NP PdCo alloy exhibits much higher electrocatalytic activity towards the oxygen-reduction reaction (ORR) with enhanced specific and mass activities relative to NP Pd and commercial Pt/C catalysts. A long-term stability test demonstrated that NP PdCo has comparable catalytic durability with less loss of ORR activity and electrochemical surface area than Pt/C. The NP PdCo alloy also shows dramatically enhanced catalytic activity towards formic acid electrooxidation relative to NP Pd and Pd/C catalysts. The as-made NP PdCo holds great application potential as a promising cathode as well as an anode electrocatalyst in fuel cells with the advantages of superior catalytic performance and easy preparation. Copyright © 2013 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Metal Doping to Enhance the Photoelectrochemical Behavior of LaFeO3 Photocathodes.

PubMed

Díez-García, María Isabel; Gómez, Roberto

2017-06-09

The development of tandem devices for water photosplitting requires the preparation of photocathodic materials based on earth-abundant elements that show long-term stability in aqueous electrolytes. Ternary metal oxides seem to be a viable option, among which perovskites stand out. In this context, transparent and compact LaFeO 3 thin-film electrodes have been prepared by a sol-gel process, both undoped and doped with metals (M) such as Mg or Zn. Pristine electrodes support the development of cathodic photocurrents in 0.1 m NaOH aqueous solutions, particularly in the presence of oxygen, with an onset potential as high as 1.4 V versus the reversible hydrogen electrode. Doping with Mg or Zn leads to an important enhancement of the photocurrent, which peaks for a stoichiometry of LaFe 0.95 M 0.05 O 3 with a sixfold enhancement with respect to the pristine material. Such an improvement is attributed to an increase in both the density and mobility of the majority carriers, although a contribution of surface passivation cannot be excluded. © 2017 Wiley-VCH Verlag GmbH & Co. KGaA, Weinheim.

Perovskite Sr2Fe1.5Mo0.5O6-δ as electrode materials for symmetrical solid oxide electrolysis cells

DOE Office of Scientific and Technical Information (OSTI.GOV)

Liu, Qiang; Yang, Chenghao; Dong, Xihui

2010-10-01

Perovskite Sr2Fe1.5Mo0.5O6-δ (SFM) has been successfully prepared by a microwave-assisted combustion method in air and employed as both anode and cathode in symmetrical solid oxide electrolysis cells (SOECs) for hydrogen production for the first time in this work. Influence of cell operating temperature, absolute humidity (AH) as well as applied direct current (DC) on the impedance of single cells with the configuration of SFM|La0.9Sr0.1Ga0.8Mg0.2O3 (LSGM)|SFM has been evaluated. Under open circuit conditions and 60 vol.% AH, the cell polarization resistance, RP is as low as 0.26 Ω cm2 at 900 °C. An electrolysis current of 0.88 A cm-2 and amore » hydrogen production rate as high as 380 mL cm-2 h have been achieved at 900 °C with an electrolysis voltage of 1.3 V and 60 vol.% AH. Further, the cell has demonstrated good stability in the long-term steam electrolysis test. The results showed that the cell electrolysis performance was even better than that of the reported strontium doped lanthanum manganite (LSM) – yttria stabilized zirconia (YSZ)|YSZ|Ni–YSZ cell, indicating that SFM could be a very promising electrode material for the practical application of SOEC technology.« less

STABILIZED OSCILLATOR

DOEpatents

Jessen, P.L.; Price, H.J.

1958-03-18

This patent relates to sine-wave generators and in particular describes a generator with a novel feedback circuit resulting in improved frequency stability. The generator comprises two triodes having a common cathode circuit connected to oscillate at a frequency and amplitude at which the loop galn of the circutt ls unity, and another pair of triodes having a common cathode circuit arranged as a conventional amplifier. A signal is conducted from the osciliator through a frequency selective network to the amplifier and fed back to the osciliator. The unique feature of the feedback circuit is the amplifier operates in the nonlinear portion of its tube characteristics thereby providing a relatively constant feedback voltage to the oscillator irrespective of the amplitude of its input signal.

Insight into Ca-Substitution Effects on O3-Type NaNi1/3 Fe1/3 Mn1/3 O2 Cathode Materials for Sodium-Ion Batteries Application.

PubMed

Sun, Liqi; Xie, Yingying; Liao, Xiao-Zhen; Wang, Hong; Tan, Guoqiang; Chen, Zonghai; Ren, Yang; Gim, Jihyeon; Tang, Wan; He, Yu-Shi; Amine, Khalil; Ma, Zi-Feng

2018-04-18

O3-type NaNi 1/3 Fe 1/3 Mn 1/3 O 2 (NaNFM) is well investigated as a promising cathode material for sodium-ion batteries (SIBs), but the cycling stability of NaNFM still needs to be improved by using novel electrolytes or optimizing their structure with the substitution of different elements sites. To enlarge the alkali-layer distance inside the layer structure of NaNFM may benefit Na + diffusion. Herein, the effect of Ca-substitution is reported in Na sites on the structural and electrochemical properties of Na 1- x Ca x /2 NFM (x = 0, 0.05, 0.1). X-ray diffraction (XRD) patterns of the prepared Na 1- x Ca x /2 NFM samples show single α-NaFeO 2 type phase with slightly increased alkali-layer distance as Ca content increases. The cycling stabilities of Ca-substituted samples are remarkably improved. The Na 0.9 Ca 0.05 Ni 1/3 Fe 1/3 Mn 1/3 O 2 (Na 0.9 Ca 0.05 NFM) cathode delivers a capacity of 116.3 mAh g -1 with capacity retention of 92% after 200 cycles at 1C rate. In operando XRD indicates a reversible structural evolution through an O3-P3-P3-O3 sequence of Na 0.9 Ca 0.05 NFM cathode during cycling. Compared to NaNMF, the Na 0.9 Ca 0.05 NFM cathode shows a wider voltage range in pure P3 phase state during the charge/discharge process and exhibits better structure recoverability after cycling. The superior cycling stability of Na 0.9 Ca 0.05 NFM makes it a promising material for practical applications in sodium-ion batteries. © 2018 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Plant Line Trial Evaluation of Viable Non-Chromium Passivation Systems for Electrolytin Tinplate, ETP (TRP 9911)

DOE Office of Scientific and Technical Information (OSTI.GOV)

John A. Sinsel

2003-06-30

Plant trial evaluations have been completed for two zirconium-based, non-chromium passivation systems previously identified as possible alternatives to cathodic dichromate (CDC) passivation for electrolytic tinplate (ETP). These trials were done on a commercial electrolytic tin plating line at Weirton Steel and extensive evaluations of the materials resulting from these trials have been completed. All this was accomplished as a collaborative effort under the AISI Technology Roadmap Program and was executed by seven North American Tin Mill Products producers [Bethlehem Steel (now acquired by International Steel Group (ISG)), Dofasco Inc., National Steel (now acquired by U.S. Steel), U.S. Steel, USS-Posco, Weirtonmore » Steel, and Wheeling-Pittsburgh Steel] with funding partially from the Department of Energy (DOE) and partially on an equal cost sharing basis among project participants. The initial phases of this project involved optimization of application procedures for the non-chromium systems in the laboratories at Bethlehem Steel and Betz Dearborn followed by extensive testing with various lacquer formulations and food simulants in the laboratories at Valspar and PPG. Work was also completed at Dofasco and Weirton Steel to develop methods to prevent precipitation of insoluble solids as a function of time from the zirconate system. The results of this testing indicated that sulfide staining characteristics for the non-chromium passivation systems could be minimized but not totally eliminated and neither system was found to perform quite as good, in this respect, as the standard CDC system. As for the stability of zirconate treatment, a method was developed to stabilize this system for a sufficient period of time to conduct plant trial evaluations but, working with a major supplier of zirconium orthosulfate, a method for long term stabilization is still under development.« less

Long-term evaluation of solid oxide fuel cell candidate materials in a 3-cell generic short stack fixture, Part II: sealing glass stability, microstructure and interfacial reactions.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Chou, Y. S.; Stevenson, Jeffry W.; Choi, Jung-Pyung

2014-03-15

A generic solid oxide fuel cell stack test fixture was developed to evaluate candidate materials and processing methods under realistic conditions. Part I of the work addressed the stack fixture, seal system and cell performance of a 3-cell short stack tested at 800oC for 6000h. Commercial NiO-YSZ anode-supported thin YSZ electrolyte cells with LSM cathodes were used for assessment and were tested in constant current mode with dilute (~50% H2) fuel versus air. Part II of the work examined the sealing glass stability, microstructure development, interfacial reactions, and volatility issues. Part III of the work investigated the stability of Ce-(Mn,Co)more » spinel coating, AISI441 metallic interconnect, alumina coating, and cell degradation. After 6000h of testing, the refractory sealing glass YSO77 (Ba-Sr-Y-B-Si) showed desirable chemical compatibility with YSZ electrolyte in that no discernable interfacial reaction was identified, consistent with thermodynamic calculations. In addition, no glass penetration into the thin electrolyte was observed. At the aluminized AISI441 interface, the protective alumina coating appeared to be corroded by the sealing glass. Air side interactions appeared to be more severe than fuel side interactions. Metal species such as Cr, Mn, and Fe were detected in the glass, but were limited to the vicinity of the interface. No alkaline earth chromates were found at the air side. Volatility was also studied in a similar glass and weight loss in a wet reducing environment was determined. Using the steady-state volatility data, the life time (40,000h) weight loss of refractory sealing glass YSO77 was estimated to be less than 0.1 wt%.« less

Multiple Hollow Cathode Wear Testing for the Space Station Plasma Contactor

NASA Technical Reports Server (NTRS)

Soulas, George C.

1994-01-01

A wear test of four hollow cathodes was conducted to resolve issues associated with the Space Station plasma contactor. The objectives of this test were to evaluate unit-to-unit dispersions, verify the transportability of contamination control protocols developed by the project, and to evaluate cathode contamination control and activation procedures to enable simplification of the gas feed system and heater power processor. These objectives were achieved by wear testing four cathodes concurrently to 2000 hours. Test results showed maximum unit-to-unit deviations for discharge voltages and cathode tip temperatures to be +/-3 percent and +/-2 percent, respectively, of the nominal values. Cathodes utilizing contamination control procedures known to increase cathode lifetime showed no trends in their monitored parameters that would indicate a possible failure, demonstrating that contamination control procedures had been successfully transferred. Comparisons of cathodes utilizing and not utilizing a purifier or simplified activation procedure showed similar behavior during wear testing and pre- and post-test performance characterizations. This behavior indicates that use of simplified cathode systems and procedures is consistent with long cathode lifetimes.

Long-term stability of GOES-8 and -9 attitude control

NASA Astrophysics Data System (ADS)

Carr, James L.

1996-10-01

An independent audit of the in-orbit behavior of the GOES-8 and GOES-9 satellites has been conducted for the NASA/GSFC. This audit utilized star and landmark observations from the GOES imager to determine long-term histories for spacecraft attitude, orbital position, and instrument internal misalignments. The paper presents results from this audit. Long-term drifts are found in the attitude histories, whereas the misalignment histories are shown to be diurnally stable. The GOES image navigation and registration system is designed to compensate for instrument internal misalignments, and both the diurnally repeatable and drift components of the attitude. Correlations between GOES-8 and GOES-9 long-term roll and pitch drifts implicate the Earth sensor as the origin of these observed drifts. This results clearly demonstrates the enhanced registration stability to be obtained with stellar inertial attitude determination replacing or supplementing Earth sensor control on future GOES missions.

Metal-Free Carbon-Based Materials: Promising Electrocatalysts for Oxygen Reduction Reaction in Microbial Fuel Cells

PubMed Central

Sawant, Sandesh Y.; Han, Thi Hiep; Cho, Moo Hwan

2016-01-01

Microbial fuel cells (MFCs) are a promising green approach for wastewater treatment with the simultaneous advantage of energy production. Among the various limiting factors, the cathodic limitation, with respect to performance and cost, is one of the main obstacles to the practical applications of MFCs. Despite the high performance of platinum and other metal-based cathodes, their practical use is limited by their high cost, low stability, and environmental toxicity. Oxygen is the most favorable electron acceptor in the case of MFCs, which reduces to water through a complicated oxygen reduction reaction (ORR). Carbon-based ORR catalysts possessing high surface area and good electrical conductivity improve the ORR kinetics by lowering the cathodic overpotential. Recently, a range of carbon-based materials have attracted attention for their exceptional ORR catalytic activity and high stability. Doping the carbon texture with a heteroatom improved their ORR activity remarkably through the favorable adsorption of oxygen and weaker molecular bonding. This review provides better insight into ORR catalysis for MFCs and the properties, performance, and applicability of various metal-free carbon-based electrocatalysts in MFCs to find the most appropriate cathodic catalyst for the practical applications. The approaches for improvement, key challenges, and future opportunities in this field are also explored. PMID:28029116

Nanoscale Polysulfides Reactors Achieved by Chemical Au-S Interaction: Improving the Performance of Li-S Batteries on the Electrode Level.

PubMed

Fan, Chao-Ying; Xiao, Pin; Li, Huan-Huan; Wang, Hai-Feng; Zhang, Lin-Lin; Sun, Hai-Zhu; Wu, Xing-Long; Xie, Hai-Ming; Zhang, Jing-Ping

2015-12-23

In this work, the chemical interaction of cathode and lithium polysulfides (LiPSs), which is a more targeted approach for completely preventing the shuttle of LiPSs in lithium-sulfur (Li-S) batteries, has been established on the electrode level. Through simply posttreating the ordinary sulfur cathode in atmospheric environment just for several minutes, the Au nanoparticles (Au NPs) were well-decorated on/in the surface and pores of the electrode composed of commercial acetylene black (CB) and sulfur powder. The Au NPs can covalently stabilize the sulfur/LiPSs, which is advantageous for restricting the shuttle effect. Moreover, the LiPSs reservoirs of Au NPs with high conductivity can significantly control the deposition of the trapped LiPSs, contributing to the uniform distribution of sulfur species upon charging/discharging. The slight modification of the cathode with <3 wt % Au NPs has favorably prospered the cycle capacity and stability of Li-S batteries. Moreover, this cathode exhibited an excellent anti-self-discharge ability. The slight decoration for the ordinary electrode, which can be easily accessed in the industrial process, provides a facile strategy for improving the performance of commercial carbon-based Li-S batteries toward practical application.

Mechanistic Study of Electrolyte Additives to Stabilize High-Voltage Cathode-Electrolyte Interface in Lithium-Ion Batteries.

PubMed

Gao, Han; Maglia, Filippo; Lamp, Peter; Amine, Khalil; Chen, Zonghai

2017-12-27

Current developments of electrolyte additives to stabilize electrode-electrolyte interface in lithium-ion batteries highly rely on a trial-and-error search, which involves repetitive testing and intensive amount of resources. The lack of understandings on the fundamental protection mechanisms of the additives significantly increases the difficulty for the transformational development of new additives. In this study, we investigated two types of individual protection routes to build a robust cathode-electrolyte interphase at high potentials: (i) a direct reduction in the catalytic decomposition of the electrolyte solvent; and (ii) formation of a "corrosion inhibitor film" that prevents severely attack and passivation from protons that generated from the solvent oxidation, even the decomposition of solvent cannot be mitigated. Effect of two exemplary electrolyte additives, lithium difluoro(oxalato)borate (LiDFOB) and 3-hexylthiophene (3HT), on LiNi 0.6 Mn 0.2 Co 0.2 O 2 (NMC 622) cathode were investigated to validate our hypothesis. It is demonstrated that understandings of both electrolyte additives and solvent are essential and careful balance between the cathode protection mechanism of additives and their side effects is critical to obtain optimum results. More importantly, this study opens up new directions of rational design of functional electrolyte additives for the next-generation high-energy-density lithium-ion chemistries.

Comparison analysis on the thermal runaway of lithium-ion battery under two heating modes.

PubMed

Wu, Tangqin; Chen, Haodong; Wang, Qingsong; Sun, Jinhua

2018-02-15

The thermal stability evaluation of materials in a soft-pack commercial cell is tested using C80 calorimeter, including anode, cathode, separator and full cell (mixing of the three materials including additional electrolyte). Thermal runaway characteristic of the commercial cell is tested on the accelerating rate calorimeter (ARC) with two heating modes, including internal heating mode and external heating mode. The results show that the thermal stability of internal material for tested cell follows the below order: anode

Experimental test of 200 W Hall thruster with titanium wall

NASA Astrophysics Data System (ADS)

Ding, Yongjie; Sun, Hezhi; Peng, Wuji; Xu, Yu; Wei, Liqiu; Li, Hong; Li, Peng; Su, Hongbo; Yu, Daren

2017-05-01

We designed a 200 W Hall thruster based on the technology of pushing down a magnetic field with two permanent magnetic rings. Boron nitride (BN) is an important insulating wall material for Hall thrusters. The discharge characteristics of the designed Hall thruster were studied by replacing BN with titanium (Ti). Experimental results show that the designed Hall thruster can discharge stably for a long time under a Ti channel. Experiments were performed to determine whether the channel and cathode are electrically connected. When the channel wall and cathode are insulated, the divergence angle of the plume increases, but the performance of the Hall thruster is improved in terms of thrust, specific impulse, anode efficiency, and thrust-to-power ratio. Ti exhibits a powerful antisputtering capability, a low emanation rate of gas, and a large structural strength, making it a potential candidate wall material in the design of low-power Hall thrusters.

Co-modification of nitrogen-doped graphene and carbon on Li3V2(PO4)3 particles with excellent long-term and high-rate performance for lithium storage

NASA Astrophysics Data System (ADS)

Ren, Manman; Yang, Mingzhi; Liu, Weiliang; Li, Mei; Su, Liwei; Wu, Xianbin; Wang, Yuanhao

2016-09-01

In this work, N-doped graphene and carbon co-modified Li3V2(PO4)3 composites (LVP/NGC) are successfully fabricated through a xerogel method for the first time. The obtained architecture combines two types of electronic contact with Li3V2(PO4)3 particles: the point-to-face contact of N-doped graphene and the face-to-face contact of N-doped carbon coating layers. Profiting from the favorable complex structure, graphene and carbon coating layers offer an extraordinary network for electron transfer and hence an excellent long-term and high-rate performance. Even tested at the rate of 40 C, the reversible capacity still maintains 86.9 mAh g-1 after 800 cycles without any fading. This work provides a promising route to improve the long-term and high-rate performance of cathodes for LIBs and enlightens us on exploring preferable strategies to develop advanced electrode materials for other energy storage devices.

Application of Millisecond Pulsar Timing to the Long-Term Stability of Clock Ensembles

NASA Technical Reports Server (NTRS)

Foster, Roger S.; Matsakis, Demetrios N.

1996-01-01

We review the application of millisecond pulsars to define a precise long-term standard and positional reference system in a nearly inertial reference frame. We quantify the current timing precision of the best millisecond pulsars and define the required precise time and time interval (PTTI) accuracy and stability to enable time transfer via pulsars. Pulsars may prove useful as independent standards to examine decade-long timing stability and provide an independent natural system within which to calibrate any new, perhaps vastly improved atomic time scale. Since pulsar stability appears to be related to the lifetime of the pulsar, the new millisecond pulsar J173+0747 is projected to have a 100-day accuracy equivalent to a single HP5071 cesium standard. Over the last five years, dozens of new millisecond pulsars have been discovered. A few of the new millisecond pulsars may have even better timing properties.

Sustainable Hypersaline Microbial Fuel Cells: Inexpensive Recyclable Polymer Supports for Carbon Nanotube Conductive Paint Anodes.

PubMed

Grattieri, Matteo; Shivel, Nelson D; Sifat, Iram; Bestetti, Massimiliano; Minteer, Shelley D

2017-05-09

Microbial fuel cells are an emerging technology for wastewater treatment, but to be commercially viable and sustainable, the electrode materials must be inexpensive, recyclable, and reliable. In this study, recyclable polymeric supports were explored for the development of anode electrodes to be applied in single-chamber microbial fuel cells operated in field under hypersaline conditions. The support was covered with a carbon nanotube (CNT) based conductive paint, and biofilms were able to colonize the electrodes. The single-chamber microbial fuel cells with Pt-free cathodes delivered a reproducible power output after 15 days of operation to achieve 12±1 mW m -2 at a current density of 69±7 mA m -2 . The decrease of the performance in long-term experiments was mostly related to inorganic precipitates on the cathode electrode and did not affect the performance of the anode, as shown by experiments in which the cathode was replaced and the fuel cell performance was regenerated. The results of these studies show the feasibility of polymeric supports coated with CNT-based paint for microbial fuel cell applications. © 2017 Wiley-VCH Verlag GmbH & Co. KGaA, Weinheim.

Study of the long-term operation of a vanadium/oxygen fuel cell

NASA Astrophysics Data System (ADS)

Noack, Jens; Cognard, Gwenn; Oral, Meryem; Küttinger, Michael; Roznyatovskaya, Nataliya; Pinkwart, Karsten; Tübke, Jens

2016-09-01

A vanadium/oxygen fuel cell (VOFC) with a geometrically active area of 51 cm2 and two membranes was discontinuously operated over a period of over 676 h with 47 successive tests at room temperature with a current density of 19.6 mA/cm2 in order to investigate signs of ageing. As well as measuring cell voltages, the test setup was also used to measure anode and redox potentials as well as cell and half-cell impedances. The performance data of the VOFC fluctuated widely over the course of the test period, due to different V2+ concentrations and instabilities of the starting solutions on the one hand and complex changes in cathode conditions on the other. The desired behaviour of the anode reactions was achieved primarily through improved methods for producing the V2+ solutions, and remained stable at the end of the experiments. The kinetics of the cathode reactions were temporarily increased by purging with 2 M H2SO4, however their performance decreased over time. The VOFC had symptoms of ageing by complex and overlaid changes in the cathode's triple phase boundary layer and in the special conditions between the two electrodes and membranes.

Performance of the FOS and GHRS Pt/(Cr)-Ne Hollow-cathode Lamps after their Return from Space and Comparison with Archival Data

NASA Technical Reports Server (NTRS)

Kerber, Florian; Lindler, Don; Bristow, Paul; Lembke, Dominik; Nave, Gillian; Reader, Joseph; Sansonetti, Craig J.; Heap, Sara R.; Rosa, Michael R.; Wood, H. John

2006-01-01

The Space Telescope European Coordinating Facility (ST-ECF) and National Institute of Standards and Technology (NIST) are collaborating to study hollow cathode calibration lamps as used onboard the Hubble Space Telescope (HST). As part of the STIS Calibration Enhancement (STIS-CE) Project we are trying to improve our understanding of the performance of hollow cathode lamps and the physical processes involved in their long term operation. The original flight lamps from the Faint Object Spectrograph (FOS) and the Goddard High Resolution Spectrograph (GHRS) are the only lamps that have ever been returned to Earth after extended operation in space. We have taken spectra of all four lamps using NIST s 10.7-m normal-incidence spectrograph and Fourier transform spectrometer (FTS) optimized for use in the ultraviolet (UV). These spectra, together with spectra archived from six years of on-orbit operations and pre-launch spectra, provide a unique data set - covering a period of about 20 years - for studying aging effects in these lamps. Our findings represent important lessons for the choice and design of calibration sources and their operation in future UV and optical spectrographs in space.

Surface Chemistry in Cobalt Phosphide-Stabilized Lithium-Sulfur Batteries.

PubMed

Zhong, Yiren; Yin, Lichang; He, Peng; Liu, Wen; Wu, Zishan; Wang, Hailiang

2018-01-31

Chemistry at the cathode/electrolyte interface plays an important role for lithium-sulfur batteries in which stable cycling of the sulfur cathode requires confinement of the lithium polysulfide intermediates and their fast electrochemical conversion on the electrode surface. While many materials have been found to be effective for confining polysulfides, the underlying chemical interactions remain poorly understood. We report a new and general lithium polysulfide-binding mechanism enabled by surface oxidation layers of transition-metal phosphide and chalcogenide materials. We for the first time find that CoP nanoparticles strongly adsorb polysulfides because their natural oxidation (forming Co-O-P-like species) activates the surface Co sites for binding polysulfides via strong Co-S bonding. With a surface oxidation layer capable of confining polysulfides and an inner core suitable for conducting electrons, the CoP nanoparticles are thus a desirable candidate for stabilizing and improving the performance of sulfur cathodes in lithium-sulfur batteries. We demonstrate that sulfur electrodes that hold a high mass loading of 7 mg cm -2 and a high areal capacity of 5.6 mAh cm -2 can be stably cycled for 200 cycles. We further reveal that this new surface oxidation-induced polysulfide-binding scheme applies to a series of transition-metal phosphide and chalcogenide materials and can explain their stabilizing effects for lithium-sulfur batteries.

Effectiveness of Career Counseling: A One-Year Follow-Up

ERIC Educational Resources Information Center

Perdrix, Sophie; Stauffer, Sarah; Masdonati, Jonas; Massoudi, Koorosh; Rossier, Jerome

2012-01-01

The short-term effectiveness of career counseling is well supported in the literature. However, the long-term impact is often overlooked. This study quantitatively investigated the long-term stability of the positive effects gained through the career counseling process and qualitatively observed participants' levels of career project…

Where Is the “Optimal” Fontan Hemodynamics?

PubMed Central

2017-01-01

Fontan circulation is generally characterized by high central venous pressure, low cardiac output, and slightly low arterial oxygen saturation, and it is quite different from normal biventricular physiology. Therefore, when a patient with congenital heart disease is selected as a candidate for this type of circulation, the ultimate goals of therapy consist of 2 components. One is a smooth adjustment to the new circulation, and the other is long-term circulatory stabilization after adjustment. When either of these goals is not achieved, the patient is categorized as having “failed” Fontan circulation, and the prognosis is dismal. For the first goal of smooth adjustment, a lot of effort has been made to establish criteria for patient selection and intensive management immediately after the Fontan operation. For the second goal of long-term circulatory stabilization, there is limited evidence of successful strategies for long-term hemodynamic stabilization. Furthermore, there have been no data on optimal hemodynamics in Fontan circulation that could be used as a reference for patient management. Although small clinical trials and case reports are available, the results cannot be generalized to the majority of Fontan survivors. We recently reported the clinical and hemodynamic characteristics of early and late failing Fontan survivors and their association with all-cause mortality. This knowledge could provide insight into the complex Fontan pathophysiology and might help establish a management strategy for long-term hemodynamic stabilization. PMID:29035429

Optical frequency locked loop for long-term stabilization of broad-line DFB laser frequency difference

NASA Astrophysics Data System (ADS)

Lipka, Michał; Parniak, Michał; Wasilewski, Wojciech

2017-09-01

We present an experimental realization of the optical frequency locked loop applied to long-term frequency difference stabilization of broad-line DFB lasers along with a new independent method to characterize relative phase fluctuations of two lasers. The presented design is based on a fast photodiode matched with an integrated phase-frequency detector chip. The locking setup is digitally tunable in real time, insensitive to environmental perturbations and compatible with commercially available laser current control modules. We present a simple model and a quick method to optimize the loop for a given hardware relying exclusively on simple measurements in time domain. Step response of the system as well as phase characteristics closely agree with the theoretical model. Finally, frequency stabilization for offsets within 4-15 GHz working range achieving <0.1 Hz long-term stability of the beat note frequency for 500 s averaging time period is demonstrated. For these measurements we employ an I/Q mixer that allows us to precisely and independently measure the full phase trace of the beat note signal.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Lill, R.; Sereno, N.; Yang, B.

The Advanced Photon Source (APS) is currently in the preliminary design phase for the multi-bend achromat (MBA) lattice upgrade. Beam stability is critical for the MBA and will require long term drift defined as beam mo-tion over a seven-day timescale to be no more than 1 mi-cron at the insertion device locations and beam angle change no more than 0.25 micro-radian. Mechanical stabil-ity of beam position monitor (BPM) pickup electrodes mounted on insertion device vacuum chambers place a fun-damental limitation on long-term beam stability for inser-tion device beamlines. We present the design and imple-mentation of prototype mechanical motion system (MMS)more » instrumentation for quantifying this type of motion specif-ically in the APS accelerator tunnel and experiment hall floor under normal operating conditions. The MMS pres-ently provides critical position information on the vacuum chamber and BPM support systems. Initial results of the R&D prototype systems have demonstrated that the cham-ber movements far exceed the long-term drift tolerance specified for the APS Upgrade MBA storage ring.« less

Stability characterization and modeling of robust distributed benthic microbial fuel cell (DBMFC) system.

PubMed

Karra, Udayarka; Huang, Guoxian; Umaz, Ridvan; Tenaglier, Christopher; Wang, Lei; Li, Baikun

2013-09-01

A novel and robust distributed benthic microbial fuel cell (DBMFC) was developed to address the energy supply issues for oceanographic sensor network applications, especially under scouring and bioturbation by aquatic life. Multi-anode/cathode configuration was employed in the DBMFC system for enhanced robustness and stability in the harsh ocean environment. The results showed that the DBMFC system achieved peak power and current densities of 190mW/m(2) and 125mA/m(2) respectively. Stability characterization tests indicated the DBMFC with multiple anodes achieved higher power generation over the systems with single anode. A computational model that integrated physical, electrochemical and biological factors of MFCs was developed to validate the overall performance of the DBMFC system. The model simulation well corresponded with the experimental results, and confirmed the hypothesis that using a multi anode/cathode MFC configuration results in reliable and robust power generation. Published by Elsevier Ltd.

Long-Term Stability of the SGA-WZ Strapdown Airborne Gravimeter

PubMed Central

Cai, Shaokun; Zhang, Kaidong; Wu, Meiping; Huang, Yangming

2012-01-01

Accelerometers are one of the most important sensors in a strapdown airborne gravimeter. The accelerometer's drift determines the long-term accuracy of the strapdown inertial navigation system (SINS), which is the primary and most critical component of the strapdown airborne gravimeter. A long-term stability test lasting 104 days was conducted to determine the characteristics of the strapdown airborne gravimeter's long-term drift. This stability test was based on the first set of strapdown airborne gravimeters built in China, the SGA-WZ. The test results reveal a quadratic drift in the strapdown airborne gravimeter data. A drift model was developed using the static data in the two end sections, and then this model was used to correct the test data. After compensating for the drift, the drift effect improved from 70 mGal to 3.46 mGal with a standard deviation of 0.63 mGal. The quadratic curve better reflects the drift's real characteristics. In comparison with other methodologies, modelling the drift as a quadratic curve was shown to be more appropriate. Furthermore, this method allows the drift to be adjusted throughout the course of the entire campaign. PMID:23112647

Preventing the dissolution of lithium polysulfides in lithium-sulfur cells by using Nafion-coated cathodes.

PubMed

Oh, Soo Jung; Lee, Jun Kyu; Yoon, Woo Young

2014-09-01

The principal drawback of lithium-sulfur batteries is the dissolution of long-chain lithium polysulfides into the electrolyte, which limits cycling performance. To overcome this problem, we focused on the development of a novel cathode as well as anode material and designed Nafion-coated NiCrAl/S as a cathode and lithium powder as an anode. Nafion-coated NiCrAl/S cathode was synthesized using a two-step dip-coating technique. The lithium-powder anode was used instead of a lithium-foil anode to prohibit dendrite growth and to improve on the electrochemical behaviors. The cells showed an initial discharge capacity of about 900 mA g(-1) and a final discharge capacity of 772 mA g(-1) after 100 cycles at 0.1 C-rate. Scanning electron microscopy (SEM) and X-ray photoelectron spectroscopy (XPS) demonstrate that using the Nafion-coated NiCrAl/S cathode can suppress the dissolution of long-chain lithium polysulfides. © 2014 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Synthesis and structural stability of Cr-doped Li2MnSiO4/C cathode materials by solid-state method

NASA Astrophysics Data System (ADS)

Cheng, Hong-Mei; Zhao, Shi-Xi; Wu, Xia; Zhao, Jian-Wei; Wei, Lei; Nan, Ce-Wen

2018-03-01

The crystal structure of the Li2MnSiO4 cathode material would collapse during the charge and discharge process because of that the Mn-O coordination polyhedron changed from [MnO4] into [MnO6] in the process of Mn+2 to Mn+4, but the Cr element could remain [CrO4] crystal ligand from Cr+2 to Cr+4, so Cr element substitution was used to improve the structural stability of the Li2MnSiO4 cathode material. In this work, Li2Mn1-xCrxSiO4/C nanocomposites were synthesized by solid-state method. XRD, SEM and TEM observations show that the as-prepared Li2Mn1-xCrxSiO4/C materials presents an orthorhombic crystal structure (S.G. Pmn21), the particle size of Li2Mn1-xCrxSiO4/C powder ranges from 50 to 100 nm. The XRD and XPS results indicate that Cr+2 is successfully doped into Li2MnSiO4 lattice and has well compatibility with Li2MnSiO4. The electrochemical results display that Li2Mn92.5%Cr7.5%SiO4/C exhibits significantly enhanced cycle stability and discharge capability. The initial discharge capacity of the Li2Mn92.5%Cr7.5%SiO4/C sample is 255 mAh g-1, and the discharge capacity was still about 60 mAh g-1 after 50 cycles. Furthermore, the XRD patterns, TEM images and Raman analysis reveal that the Cr doping enhances the structural stability of Li2Mn1-xCrxSiO4/C and improves the electrochemical activity of the cathode. Thus, the Li2Mn92.5%Cr7.5%SiO4/C have shown potential applications for lithium ion batteries.

Alkaline polymer electrolyte fuel cells stably working at 80 °C

NASA Astrophysics Data System (ADS)

Peng, Hanqing; Li, Qihao; Hu, Meixue; Xiao, Li; Lu, Juntao; Zhuang, Lin

2018-06-01

Alkaline polymer electrolyte fuel cells are a new class of polymer electrolyte fuel cells that fundamentally enables the use of nonprecious metal catalysts. The cell performance mostly relies on the quality of alkaline polymer electrolytes, including the ionic conductivity and the chemical/mechanical stability. For a long time, alkaline polymer electrolytes are thought to be too weak in stability to allow the fuel cell to be operated at elevated temperatures, e.g., above 60 °C. In the present work, we report a progress in the state-of-the-art alkaline polymer electrolyte fuel cell technology. By using a newly developed alkaline polymer electrolyte, quaternary ammonia poly (N-methyl-piperidine-co-p-terphenyl), which simultaneously possesses high ionic conductivity and excellent chemical/mechanical stability, the fuel cell can now be stably operated at 80 °C with high power density. The peak power density reaches ca. 1.5 W/cm2 at 80 °C with Pt/C catalysts used in both the anode and the cathode. The cell works stably in a period of study over 100 h.

Degradation of aniline by electrochemical activation of peroxydisulfate at MWCNT cathode: The proofed concept of nonradical oxidation process.

PubMed

Nie, Chunyang; Ao, Zhimin; Duan, Xiaoguang; Wang, Chengying; Wang, Shaobin; An, Taicheng

2018-05-07

Enhanced elimination of aniline in aqueous solution was achieved by coupling electrosorption of aniline and electrochemical activation of peroxydisulfate (PDS) at multi-walled carbon nanotube (MWCNT) cathode, in which a synergistic effect occurred. It was found that PDS could be effectively activated under a small voltage at MWCNT cathode owing to the specific pore structures of MWCNTs. A nonradical oxidation pathway instead of radical-based oxidation was proposed from the cathodic activation of PDS, wherein PDS molecules with a modified electronic structure was suggested to be the principal reactive species. Meanwhile, the influences of various operation parameters such as electrode potential, PDS concentration, presence of chloride ions on the elimination efficiency, and the stability of MWCNT electrode were also attempted. Therefore, the electrochemical activation of PDS by MWCNT cathode is a promising energy-saving method for the treatment of organic pollutants in wastewater. Copyright © 2018 Elsevier Ltd. All rights reserved.

Novel Approach to Strengthening Ceramic Cathode Contact and Validation in a Generic Stack Test Fixture

DOE Office of Scientific and Technical Information (OSTI.GOV)

Chou, Yeong-Shyung; Bonnett, Jeff F.; Stevenson, Jeffry W.

The ceramic contact material at the cathode side has been identified as the weakest mechanical link in solid oxide fuel cells, due to poor sintering at low stack fabrication temperatures. In this work, a novel approach of mechanical interlocking with an engineered surface was proposed to strengthen LSM-type contacts. The engineered cathode surface was made by depositing large LSM20 granules onto a wet cathode print, followed by sintering. Granules of three sizes were tested (mesh #35, #60, and #100). Small coupons of anode-supported YSZ electrolyte with LSM cathode were joined at 850 and 950oC for 2h with LSM contact usingmore » either the engineered surface or plain surfaces. The results of contact strength measurements showed about 14 times increase with engineered surface compared to plain surfaces. Validation with a 2”x2” LSM-based cell in a generic stack fixture showed good thermal cycle stability with minimal change in ohmic impedance over ten cycles.« less

Recent advances on the understanding of structural and composition evolution of LMR cathodes for Li-ion batteries

DOE PAGES

Yan, Pengfei; Zheng, Jianming; Xiao, Jie; ...

2015-06-08

Lithium-rich, magnesium-rich (LMR) cathode materials have been regarded as one of the very promising cathodes for Li-ion battery applications. However, their practical application is still limited by several challenges, especially by their limited electrochemical stability rate capability. In this work, we present recent progresses on the understanding of the structural and composition evolution of LMR cathode materials with emphasis being placed on the correlation between structural/chemical evolution and electrochemical properties. In particular, using Li [Li 0.2Ni 0.2Mn 0.6O 2 as a typical example, we clearly illustrate the structural characteristics of the pristine materials and their dependence on the materials processingmore » history, cycling induced structural degradation/chemical partition and their correlation with degradation of electrochemical performance. The fundamental understanding obtained in this work may also guide the design and preparation of new cathode materials based on ternary system of transitional metal oxide.« less

Frequency standard stability for Doppler measurements on-board the shuttle

NASA Technical Reports Server (NTRS)

Harton, P. L.

1974-01-01

The short and long term stability characteristics of crystal and atomic standards are described. Emphasis is placed on crystal oscillators because of the selection which was made for the shuttle baseline and the complexities which are introduced by the shuttle environment. Attention is given, first, to the definitions of stability and the application of these definitions to the shuttle system and its mission. Data from time domain measurements are used to illustrate the definitions. Results of a literature survey to determine environmental effects on frequency reference sources are then presented. Finally, methods of standard frequency dissemination over radio frequency carriers are noted as a possible means of measuring absolute accuracy and long term stability characteristics during on one way Doppler equipment.

Spectrally narrow, long-term stable optical frequency reference based on a Eu3+:Y2SiO5 crystal at cryogenic temperature.

PubMed

Chen, Qun-Feng; Troshyn, Andrei; Ernsting, Ingo; Kayser, Steffen; Vasilyev, Sergey; Nevsky, Alexander; Schiller, Stephan

2011-11-25

Using an ultrastable continuous-wave laser at 580 nm we performed spectral hole burning of Eu(3+):Y(2)SiO(5) at a very high spectral resolution. The essential parameters determining the usefulness as a macroscopic frequency reference, linewidth, temperature sensitivity, and long-term stability, were characterized using a H-maser stabilized frequency comb. Spectral holes with a linewidth as low as 6 kHz were observed and the upper limit of the drift of the hole frequency was determined to be 5±3 mHz/s. We discuss the necessary requirements for achieving ultrahigh stability in laser frequency stabilization to these spectral holes.

Facile Synthesis of V₂O₅ Hollow Spheres as Advanced Cathodes for High-Performance Lithium-Ion Batteries.

PubMed

Zhang, Xingyuan; Wang, Jian-Gan; Liu, Huanyan; Liu, Hongzhen; Wei, Bingqing

2017-01-18

Three-dimensional V₂O₅ hollow structures have been prepared through a simple synthesis strategy combining solvothermal treatment and a subsequent thermal annealing. The V₂O₅ materials are composed of microspheres 2-3 μm in diameter and with a distinct hollow interior. The as-synthesized V₂O₅ hollow microspheres, when evaluated as a cathode material for lithium-ion batteries, can deliver a specific capacity as high as 273 mAh·g -1 at 0.2 C. Benefiting from the hollow structures that afford fast electrolyte transport and volume accommodation, the V₂O₅ cathode also exhibits a superior rate capability and excellent cycling stability. The good Li-ion storage performance demonstrates the great potential of this unique V₂O₅ hollow material as a high-performance cathode for lithium-ion batteries.

Explaining Variance in Long-Term Recall in 3- and 4-Year-Old Children: The Importance of Post-Encoding Processes

ERIC Educational Resources Information Center

Bauer, Patricia J.; Larkina, Marina; Doydum, Ayzit O.

2012-01-01

Long-term recall is influenced by what originally was encoded as well as by the efficacy of retrieval processes. The possible explanatory role of post-encoding processes by which initially labile memory traces are stabilized and integrated into long-term memory (i.e., consolidated) has received relatively less research attention. In the current…

Stabilization of dynamics of oscillatory systems by nonautonomous perturbation.

PubMed

Lucas, Maxime; Newman, Julian; Stefanovska, Aneta

2018-04-01

Synchronization and stability under periodic oscillatory driving are well understood, but little is known about the effects of aperiodic driving, despite its abundance in nature. Here, we consider oscillators subject to driving with slowly varying frequency, and investigate both short-term and long-term stability properties. For a phase oscillator, we find that, counterintuitively, such variation is guaranteed to enlarge the Arnold tongue in parameter space. Using analytical and numerical methods that provide information on time-variable dynamical properties, we find that the growth of the Arnold tongue is specifically due to the growth of a region of intermittent synchronization where trajectories alternate between short-term stability and short-term neutral stability, giving rise to stability on average. We also present examples of higher-dimensional nonlinear oscillators where a similar stabilization phenomenon is numerically observed. Our findings help support the case that in general, deterministic nonautonomous perturbation is a very good candidate for stabilizing complex dynamics.

Stabilization of dynamics of oscillatory systems by nonautonomous perturbation

NASA Astrophysics Data System (ADS)

Lucas, Maxime; Newman, Julian; Stefanovska, Aneta

2018-04-01

Synchronization and stability under periodic oscillatory driving are well understood, but little is known about the effects of aperiodic driving, despite its abundance in nature. Here, we consider oscillators subject to driving with slowly varying frequency, and investigate both short-term and long-term stability properties. For a phase oscillator, we find that, counterintuitively, such variation is guaranteed to enlarge the Arnold tongue in parameter space. Using analytical and numerical methods that provide information on time-variable dynamical properties, we find that the growth of the Arnold tongue is specifically due to the growth of a region of intermittent synchronization where trajectories alternate between short-term stability and short-term neutral stability, giving rise to stability on average. We also present examples of higher-dimensional nonlinear oscillators where a similar stabilization phenomenon is numerically observed. Our findings help support the case that in general, deterministic nonautonomous perturbation is a very good candidate for stabilizing complex dynamics.

Long term stability of Oligo (dT) 25 magnetic beads for the expression analysis of Euglena gracilis for long term space projects.

PubMed

Becker, Ina; Strauch, Sebastian M; Hauslage, Jens; Lebert, Michael

2017-05-01

The unicellular freshwater flagellate Euglena gracilis has a highly developed sensory system. The cells use different stimuli such as light and gravity to orient themselves in the surrounding medium to find areas for optimal growth. Due to the ability to produce oxygen and consume carbon dioxide, Euglena is a suitable candidate for life support systems. Participation in a long-term space experiment would allow for the analysis of changes and adaptations to the new environment, and this could bring new insights into the mechanism of perception of gravity and the associated signal transduction chain. For a molecular analysis of transcription patterns, an automated system is necessary, capable of performing all steps from taking a sample, processing it and generating data. One of the developmental steps is to find long-term stable reagents and materials and test them for stability at higher-than-recommended temperature conditions during extended storage time. We investigated the usability of magnetic beads in an Euglena specific lysis buffer after addition of the RNA stabilizer Dithiothreitol over 360 days and the lysis buffer with the stabilizer alone over 455 days at the expected storage temperature of 19 °C. We can claim that the stability is not impaired at all after an incubation period of over one year. This might be an interesting result for researchers who have to work under non-standard lab conditions, as in biological or medicinal fieldwork. Copyright © 2017 The Committee on Space Research (COSPAR). Published by Elsevier Ltd. All rights reserved.

Ultradispersed Nanoarchitecture of LiV3O8 Nanoparticle/Reduced Graphene Oxide with High-Capacity and Long-Life Lithium-Ion Battery Cathodes

NASA Astrophysics Data System (ADS)

Mo, Runwei; Du, Ying; Rooney, David; Ding, Guqiao; Sun, Kening

2016-01-01

Lack of high-performance cathode materials has become the major barriers to lithium-ion battery applications in advanced communication equipment and electric vehicles. In this paper, we report a versatile interfacial reaction strategy, which is based on the idea of space confinement, for the synthesis of ultradispersed LiV3O8 nanoparticles (~10 nm) on graphene (denoted as LVO NPs-GNs) with an unprecedented degree of control on the separation and manipulation of the nucleation, growth, anchoring, and crystallization of nanoparticles in a water-in-oil emulsion system over free growth in solution. The prepared LVO NPs-GNs composites displayed high performance as an cathode material for lithium-ion battery, including high reversible lithium storage capacity (237 mA h g-1 after 200 cycles), high Coulombic efficiency (about 98%), excellent cycling stability and high rate capability (as high as 176 mA h g-1 at 0.9 A g-1, 128 mA h g-1 at 1.5 A g-1, 91 mA h g-1 at 3 A g-1 and 59 mA h g-1 at 6 A g-1, respectively). Very significantly, the preparation method employed can be easily adapted and may opens the door to complex hybrid materials design and engineering with graphene for advanced energy storage.

Basic Research on Plasma Cathode for HPM Sources (NE - Luginsland)

DTIC Science & Technology

2011-11-30

to NEPP Vacuum Pump for Mock Magnetron 12 (b) Borosilicate glass (Insulator)  Anode Cathode Vacuum chamber Ion gauge controller Charge...channeling may be one physical mechanism that can explain the stability of the pinch in the discharge. (a) Scroll Pump High Voltage Power Supply DC... vacuum and/or low vacuum slow wave devices and cross field devices) in burst mode? Here, burst mode effectively implies an impulse-like (short pulse

Thin-film Rechargeable Lithium Batteries

DOE R&D Accomplishments Database

Dudney, N. J.; Bates, J. B.; Lubben, D.

1995-06-01

Thin film rechargeable lithium batteries using ceramic electrolyte and cathode materials have been fabricated by physical deposition techniques. The lithium phosphorous oxynitride electrolyte has exceptional electrochemical stability and a good lithium conductivity. The lithium insertion reaction of several different intercalation materials, amorphous V{sub 2}O{sub 5}, amorphous LiMn{sub 2}O{sub 4}, and crystalline LiMn{sub 2}O{sub 4} films, have been investigated using the completed cathode/electrolyte/lithium thin film battery.

Secondary battery material and synthesis method

DOEpatents

Liu, Hongjian; Kepler, Keith Douglas; Wang, Yu

2013-10-22

A composite Li.sub.1+xMn.sub.2-x-yM.sub.yO.sub.4 cathode material stabilized by treatment with a second transition metal oxide phase that is highly suitable for use in high power and energy density Li-ion cells and batteries. A method for treating a Li.sub.1+xMn.sub.2-x-yM.sub.yO.sub.4 cathode material utilizing a dry mixing and firing process.

Long-term stability of crystal-stabilized water-in-oil emulsions.

PubMed

Ghosh, Supratim; Pradhan, Mamata; Patel, Tejas; Haj-Shafiei, Samira; Rousseau, Dérick

2015-12-15

The impact of cooling rate and mixing on the long-term kinetic stability of wax-stabilized water-in-oil emulsions was investigated. Four cooling/mixing protocols were investigated: cooling from 45°C to either 25°C or 4°C with/without stirring and two cooling rates - slow (1°C/min) and fast (5°C/min). The sedimentation behaviour of the emulsions was significantly affected by cooling protocol. Stirring was critical to the stability of all emulsions, with statically-cooled (no stirring) emulsions suffering from extensive aqueous phase separation. Emulsions stirred while cooling showed sedimentation of a waxy emulsion layer leaving a clear oil layer at the top, with a smaller separation and droplet size distribution at 4°C compared to 25°C, indicating the importance of the amount of crystallized wax on emulsion stability. Light microscopy revealed that crystallized wax appeared both on the droplet surface and in the continuous phase, suggesting that stirring ensured dispersibility of the water droplets during cooling as the wax was crystallizing. Wax crystallization on the droplet surface provided stability against droplet coalescence while continuous phase wax crystals minimized inter-droplet collisions. The key novel aspect of this research is in the simplicity to tailor the spatial distribution of wax crystals, i.e., either at the droplet surface or in the continuous phase via use of a surfactant and judicious stirring and/or cooling. Knowledge gained from this research can be applied to develop strategies for long-term storage stability of crystal-stabilized W/O emulsions. Copyright © 2015 Elsevier Inc. All rights reserved.

DARHT Axis II Cathode 16 (S/N 22) History as Recorded in the Historian and Shot Data Databases

DOE Office of Scientific and Technical Information (OSTI.GOV)

Smith, H. Vernon; Barraza, Juan; Harrison, James F.

2014-01-10

Long DARHT II injector cathode operating lifetimes are desirable for flash radiography of hydrodynamic tests at the dual-axis radiographic hydrotest facility (DARHT). The specification for cathode operating lifetime given to Spectra-Mat in the purchase orders for the 311X-M cathodes is ≥ 1000 hours at full operating temperature (~1120 oC). Of the five most-recent cathodes operated on DARHT II, only two have met this specification. It is desirable to have cathodes lifetimes considerably longer than the specified 1000 hours. In this report we present the thermal and vacuum history of cathode 16 (serial no. [S/N] 22), a 311X-M cathode, as recordedmore » in the historian database and the shot data database. The hope is that by examining this history we can identify the parameter (or parameters) that are limiting the DARHT II 311X-M cathode lifetimes. This is the fifth in a series of 5 DARHT Tech Notes in which recent cathode thermal and vacuum histories are examined. The other tech notes in this series are DARHT Tech Notes Nos. 501 (cathode 12, S/N 15), 502 (cathode 13, S/N 19), 503 (cathode 14, S/N 20), and 504 (cathode 15, S/N 21). In DARHT Tech Note No. 506 we will compare the recorded thermal and vacuum histories of cathodes 12-16 and attempt to understand the cathode lifetime limitations based on the stored cathode data presented in DARHT Tech Notes 501-505 and other relevant information.« less

On the long-term stability of calibration standards in different matrices.

PubMed

Kandić, A; Vukanac, I; Djurašević, M; Novković, D; Šešlak, B; Milošević, Z

2012-09-01

In order to assure Quality Control in accordance with ISO/IEC 17025, it was important, from metrological point of view, to examine the long-term stability of calibration standards previously prepared. Comprehensive reconsideration on efficiency curves with respect to the ageing of calibration standards is presented in this paper. The calibration standards were re-used after a period of 5 years and analysis of the results showed discrepancies in efficiency values. Copyright © 2012 Elsevier Ltd. All rights reserved.

Polymer Latex Stability Modification by Exposure to Hydrophobic Solvents.

PubMed

de Oliveira Cardoso A; Galembeck

1998-08-01

The stability of latex particles toward coagulation in the presence of salt is modified by swelling the latex with toluene and chloroform vapors. Short-term stability was determined by turbidimetric titrations, and the long-term stability was evaluated by adding latex and salt solutions, allowing the mixture to age for 24 or 48 h and determining the characteristics of the supernatant and of the sediment. Nine different latexes were examined, with variable results: in some cases, both apolar solvents stabilize the latex; in other cases, increased stability is induced by only one of the solvents, either toluene or chloroform. There is also coherence, but not a strict correlation, between the solvent effects on short- and long-term stability. For instance, in the case of a core-and-shell styrene-butyl methacrylate latex, chloroform has a small stabilizing effect in the titration experiment, but it prevents the formation of a coagulated latex sediment even 48 h after mixing latex and salt. Two hypotheses are discussed to account for these observations: (i) swelling solvents decrease the particles ability to dissipate the collision kinetic energy, so that particles collide but without joining each other; (ii) the solvents induce the release of trapped charged groups from the particle interior to the interface, enhancing the usual (electrostatic, steric, hydration) stability factors. Copyright 1998 Academic Press.

Understanding the impact of operational conditions on performance of microbial peroxide producing cells

NASA Astrophysics Data System (ADS)

Young, Michelle N.; Chowdhury, Nadrat; Garver, Emily; Evans, Patrick J.; Popat, Sudeep C.; Rittmann, Bruce E.; Torres, César I.

2017-07-01

Microbial peroxide producing cells (MPPCs) are microbial electrochemical cells used to synthesize hydrogen peroxide (H2O2) in the cathode chamber. Catholyte hydraulic retention time (HRT), different catholytes and their concentrations, and a ferrochelating stabilizer are varied in a continuous-flow cathode MPPC to evaluate their impacts on performance. Using NaCl catholytes, the MPPC produced as high as 3.1 ± 0.37 g H2O2 L-1 at a 4-h HRT with as little as 1.13 W-h g-1 H2O2 energy input and with up to 57 g Lcathode-1 d-1 at a 1-h HRT. For these conditions, the H2O2 production rate provides more than 3 times the H2O2 required for disinfection or micro-pollutant removal while using 5-25% of the power used in conventional H2O2 production processes. Attempts to improve H2O2-production by adding weak acid buffers or H2O2-stabilizing EDTA fail for different reasons. The addition of the ferrochelator EDTA to prevent H2O2 auto-decay deteriorates MPPC performance, because EDTA diffuses from the cathode to the anode, inhibiting iron utilization by anode-respiring bacteria. Weak acid buffers failed to reduce cathode concentration overpotentials. Buffering catholytes lowered the H2O2 yield due to large pH gradients at the cathode chamber entrance, causing the formation of H2O instead of H2O2 or O2 re-formation from H2O2 auto-decay.

A nickel-foam@carbon-shell with a pie-like architecture as an efficient polysulfide trap for high-energy Li–S batteries

DOE PAGES

Luo, Liu; Chung, Sheng-Heng; Chang, Chi-Hao; ...

2017-07-06

A high-loading sulfur cathode is critical for establishing rechargeable lithium–sulfur (Li–S) batteries with the anticipated high energy density. However, its fabrication as well as realizing high electrochemical utilization and stability with high-loading sulfur cathodes is a daunting challenge. Here, we present a new pie-like electrode that consists of an electrocatalytic nickel-foam as a “filling” to adsorb and store polysulfide catholytes and an outer carbon shell as a “crust” for facilitating high-loading sulfur cathodes with superior electrochemical and structural stabilities. The inner electrocatalytic nickel-foam is configured to adsorb polysulfides and facilitate their redox reactions. The intertwined carbon shell assists to shieldmore » the polysulfides within the cathode region of the cell. Both the nickel-foam and the carbon shell have high conductivity and porous space, which serve simultaneously as interconnected current collectors to enhance the redox kinetics and as polysulfide reservoirs to confine the active material. The effectiveness of such a pie-like structure in improving the electrochemical efficiency enables the cathode to host an ultrahigh sulfur loading of 40 mg cm -2 and attain a high areal capacity of over 40 mA h cm -2 at a low electrolyte/sulfur (E/S) ratio of 7. The enhanced cyclability is reflected in a high reversible areal capacity approaching 30 mA h cm -2 at C/5 rate after 100 cycles and excellent rate capability up to 2C rate.« less

A nickel-foam@carbon-shell with a pie-like architecture as an efficient polysulfide trap for high-energy Li–S batteries

DOE Office of Scientific and Technical Information (OSTI.GOV)

Luo, Liu; Chung, Sheng-Heng; Chang, Chi-Hao

A high-loading sulfur cathode is critical for establishing rechargeable lithium–sulfur (Li–S) batteries with the anticipated high energy density. However, its fabrication as well as realizing high electrochemical utilization and stability with high-loading sulfur cathodes is a daunting challenge. Here, we present a new pie-like electrode that consists of an electrocatalytic nickel-foam as a “filling” to adsorb and store polysulfide catholytes and an outer carbon shell as a “crust” for facilitating high-loading sulfur cathodes with superior electrochemical and structural stabilities. The inner electrocatalytic nickel-foam is configured to adsorb polysulfides and facilitate their redox reactions. The intertwined carbon shell assists to shieldmore » the polysulfides within the cathode region of the cell. Both the nickel-foam and the carbon shell have high conductivity and porous space, which serve simultaneously as interconnected current collectors to enhance the redox kinetics and as polysulfide reservoirs to confine the active material. The effectiveness of such a pie-like structure in improving the electrochemical efficiency enables the cathode to host an ultrahigh sulfur loading of 40 mg cm -2 and attain a high areal capacity of over 40 mA h cm -2 at a low electrolyte/sulfur (E/S) ratio of 7. The enhanced cyclability is reflected in a high reversible areal capacity approaching 30 mA h cm -2 at C/5 rate after 100 cycles and excellent rate capability up to 2C rate.« less

The stability of liquid-filled matrix ionization chamber electronic portal imaging devices for dosimetry purposes.

PubMed

Louwe, R J W; Tielenburg, R; van Ingen, K M; Mijnheer, B J; van Herk, M B

2004-04-01

This study was performed to determine the stability of liquid-filled matrix ionization chamber (LiFi-type) electronic portal imaging devices (EPID) for dosimetric purposes. The short- and long-term stability of the response was investigated, as well as the importance of factors influencing the response (e.g., temperature fluctuations, radiation damage, and the performance of the electronic hardware). It was shown that testing the performance of the electronic hardware as well as the short-term stability of the imagers may reveal the cause of a poor long-term stability of the imager response. In addition, the short-term stability was measured to verify the validity of the fitted dose-response curve immediately after beam startup. The long-term stability of these imagers could be considerably improved by correcting for room temperature fluctuations and gradual changes in response due to radiation damage. As a result, the reproducibility was better than 1% (1 SD) over a period of two years. The results of this study were used to formulate recommendations for a quality control program for portal dosimetry. The effect of such a program was assessed by comparing the results of portal dosimetry and in vivo dosimetry using diodes during the treatment of 31 prostate patients. The improvement of the results for portal dosimetry was consistent with the deviations observed with the reproducibility tests in that particular period. After a correction for the variation in response of the imager, the average difference between the measured and prescribed dose during the treatment of prostate patients was -0.7%+/-1.5% (1 SD), and -0.6%+/-1.1% (1 SD) for EPID and diode in vivo dosimetry, respectively. It can be concluded that a high stability of the response can be achieved for this type of EPID by applying a rigorous quality control program.

Modeling and validation of single-chamber microbial fuel cell cathode biofilm growth and response to oxidant gas composition

NASA Astrophysics Data System (ADS)

Ou, Shiqi; Zhao, Yi; Aaron, Douglas S.; Regan, John M.; Mench, Matthew M.

2016-10-01

This work describes experiments and computational simulations to analyze single-chamber, air-cathode microbial fuel cell (MFC) performance and cathodic limitations in terms of current generation, power output, mass transport, biomass competition, and biofilm growth. Steady-state and transient cathode models were developed and experimentally validated. Two cathode gas mixtures were used to explore oxygen transport in the cathode: the MFCs exposed to a helium-oxygen mixture (heliox) produced higher current and power output than the group of MFCs exposed to air or a nitrogen-oxygen mixture (nitrox), indicating a dependence on gas-phase transport in the cathode. Multi-substance transport, biological reactions, and electrochemical reactions in a multi-layer and multi-biomass cathode biofilm were also simulated in a transient model. The transient model described biofilm growth over 15 days while providing insight into mass transport and cathodic dissolved species concentration profiles during biofilm growth. Simulation results predict that the dissolved oxygen content and diffusion in the cathode are key parameters affecting the power output of the air-cathode MFC system, with greater oxygen content in the cathode resulting in increased power output and fully-matured biomass.

Modeling and validation of single-chamber microbial fuel cell cathode biofilm growth and response to oxidant gas composition

DOE PAGES

Ou, Shiqi; Zhao, Yi; Aaron, Douglas S.; ...

2016-08-15

This work describes experiments and computational simulations to analyze single-chamber, air-cathode microbial fuel cell (MFC) performance and cathodic limitations in terms of current generation, power output, mass transport, biomass competition, and biofilm growth. Steady-state and transient cathode models were developed and experimentally validated. Two cathode gas mixtures were used to explore oxygen transport in the cathode: the MFCs exposed to a helium-oxygen mixture (heliox) produced higher current and power output than the group of MFCs exposed to air or a nitrogen-oxygen mixture (nitrox), indicating a dependence on gas-phase transport in the cathode. Multi-substance transport, biological reactions, and electrochemical reactions inmore » a multi-layer and multi-biomass cathode biofilm were also simulated in a transient model. The transient model described biofilm growth over 15 days while providing insight into mass transport and cathodic dissolved species concentration profiles during biofilm growth. Lastly, simulation results predict that the dissolved oxygen content and diffusion in the cathode are key parameters affecting the power output of the air-cathode MFC system, with greater oxygen content in the cathode resulting in increased power output and fully-matured biomass.« less

Investigating the stability of cathode materials for rechargeable lithium ion batteries

NASA Astrophysics Data System (ADS)

Huang, Yiqing

Lithium ion batteries are widely used in portable electronic devices and electric vehicles. However, safety is one of the most important issues for the Li-ion batteries' use. Some cathode materials, such as LiCoO 2, are thermally unstable in the charged state. Upon decomposition these cathode materials release O2, which could react with organic electrolyte, leading to a thermal runaway. Thus understanding the stability of the cathode materials is critical to the safety of lithium ion batteries. Olivine-type LiMnPO4 is a promising cathode material for lithium ion batteries because of its high energy density. We have revealed the critical role of carbon in the stability and thermal behaviour of olivine MnPO 4 obtained by chemical delithiation of LiMnPO4. (Li)MnPO 4 samples with various particle sizes and carbon contents were studied. Carbon-free LiMnPO4 obtained by solid state synthesis in O 2 becomes amorphous upon delithiation. Small amounts of carbon (0.3 wt.%) help to stabilize the olivine structure, so that completely delithiated crystalline olivine MnPO4 can be obtained. Larger amount of carbon (2 wt.%) prevents full delithiation. Heating in air, O2, or N 2 results in structural disorder (< 300 °C), formation of an intermediate sarcopside Mn3(PO4)2 phase (350 -- 450 °C), and complete decomposition to Mn2P2O 7 on extended heating at 400 °C. Carbon protects MnPO4 from reacting with environmental water, which is detrimental to its structural stability. We not only studied the crystalline olivine MnPO4, but also investigated the amorphous products obtained from carbon-free LiMnPO 4. We have revealed the Mn dissolution phenomenon during chemical delithiation of LiMnPO4, which causes the amorphization of olivine MnPO 4. Properties of crystalline-MnPO4 obtained from carbon-coated LiMnPO4 and of amorphous product resulting from the delithiation of pure LiMnPO4 were studied and compared. The P-rich amorphous phases in the latter are considered to be MnHP2O7 and MnH2P2O7 from XAS and XPS analysis. Safety of batteries not only depends on the stability of the active materials, but also the interactions between the active materials and electrolyte. Thus we study the stability between the cathode materials and the electrolyte. The thermal stability of electrochemically delithiated Li0.1N 0.8C0.15Al0.05O2 (NCA), FePO4 (FP), Mn0.8Fe0.2PO4 (MFP), hydrothermally synthesized VOPO4, LiVOPO4 and electrochemically lithiated Li2VOPO4 is investigated by differential scanning calorimetry (DSC) and thermogravimetric analysis, coupled with mass spectrometry (TGA-MS). The thermal stability is found in the order: NCA< VOPO4< MFP< FP=LiVOPO4=Li2VOPO4. Sealed capsule high pressure experiments show a phase transformation of VOPO4 → HVOPO4 → H2VOPO4 when VOPO4 reacts with electrolyte (1 M LiPF6 in EC: DMC=1:1) between 200 and 300 °C. Finally, we characterize the lithium storage and release mechanism of V2O5 aerogels by x-ray photoelectron spectroscopy (XPS). We study the influence of n--butyllithium (n--BuLi) treatments on the electrochemical performance of the aerogel. In addition to fully reversible V reduction and oxidation due to the intercalation reaction, we observe the formation of LiOH species that are only partially reversible. This is attributed to reaction with the interlayer water and is considered responsible for the gradual capacity fade. The n--BuLi treated aerogels display a higher capacity than those without and our XPS analysis reveals an additional reversible formation of Li2O.

High-voltage positive electrode materials for lithium-ion batteries

DOE Office of Scientific and Technical Information (OSTI.GOV)

Li, Wangda; Song, Bohang; Manthiram, Arumugam

The ever-growing demand for advanced rechargeable lithium-ion batteries in portable electronics and electric vehicles has spurred intensive research efforts over the past decade. The key to sustaining the progress in Li-ion batteries lies in the quest for safe, low-cost positive electrode (cathode) materials with desirable energy and power capabilities. One approach to boost the energy and power densities of batteries is to increase the output voltage while maintaining a high capacity, fast charge–discharge rate, and long service life. Here, this review gives an account of the various emerging high-voltage positive electrode materials that have the potential to satisfy these requirementsmore » either in the short or long term, including nickel-rich layered oxides, lithium-rich layered oxides, high-voltage spinel oxides, and high-voltage polyanionic compounds. The key barriers and the corresponding strategies for the practical viability of these cathode materials are discussed along with the optimization of electrolytes and other cell components, with a particular emphasis on recent advances in the literature. Finally, a concise perspective with respect to plausible strategies for future developments in the field is also provided.« less

High-voltage positive electrode materials for lithium-ion batteries

DOE PAGES

Li, Wangda; Song, Bohang; Manthiram, Arumugam

2017-04-25

The ever-growing demand for advanced rechargeable lithium-ion batteries in portable electronics and electric vehicles has spurred intensive research efforts over the past decade. The key to sustaining the progress in Li-ion batteries lies in the quest for safe, low-cost positive electrode (cathode) materials with desirable energy and power capabilities. One approach to boost the energy and power densities of batteries is to increase the output voltage while maintaining a high capacity, fast charge–discharge rate, and long service life. Here, this review gives an account of the various emerging high-voltage positive electrode materials that have the potential to satisfy these requirementsmore » either in the short or long term, including nickel-rich layered oxides, lithium-rich layered oxides, high-voltage spinel oxides, and high-voltage polyanionic compounds. The key barriers and the corresponding strategies for the practical viability of these cathode materials are discussed along with the optimization of electrolytes and other cell components, with a particular emphasis on recent advances in the literature. Finally, a concise perspective with respect to plausible strategies for future developments in the field is also provided.« less

Surface transformation by a “cocktail” solvent enables stable cathode materials for sodium ion batteries

DOE Office of Scientific and Technical Information (OSTI.GOV)

Mu, Linqin; Rahman, Muhammad Mominur; Zhang, Yan

Coating the surfaces of active materials has become an effective and indispensable path towards the stable operation of practical rechargeable batteries. Improving the affordability of coating processes can bring enormous manufacturing advantages to battery applications. Here in this paper, we report a cheap, simple and efficient method to create conformal coating layers on the primary particles of sodium layered oxide materials for improving battery performance. Mimicking the cathode–electrolyte interfacial reaction in practical cells, we create conformal coating layers via the spontaneous reaction between the oxidative cathode surfaces and a cocktail of reductive organic solvents. The conformal coating layers consist ofmore » metal–organic compounds with reduced transition metal cations, i.e., artificial cathode–electrolyte interphases (CEIs). The cells containing these coated cathode materials deliver much improved cycle life while maintaining reasonably high reversible capacity and rate capability. Furthermore, the structural stability and water resistance are enhanced, which can practically help simplify the storage protocol of cathode powders prior to battery manufacturing. The surfaces of most oxide cathode materials (e.g., lithium cathodes and sodium cathodes) are highly oxidative, and thus we expect that the present method, with tailored experimental parameters, can be readily applied to most battery systems.« less

Exploring Lithium Deficiency in Layered Oxide Cathode for Li-Ion Battery

DOE Office of Scientific and Technical Information (OSTI.GOV)

Cho, Sung-Jin; Uddin, Md-Jamal; Alaboina, Pankaj K.

Abstract or short description: The ever-growing demand for high capacity cathode materials is on the rise since the futuristic applications are knocking on the door. Conventional approach to developing such cathode relies on the lithium-excess materials to operate the cathode at high voltage and extract more lithium-ion. Yet, they fail to satiate the needs because of their unresolved issues upon cycling such as, for lithium manganese-rich layered oxides – their voltage fading, and for as nickel-based layered oxides – the structural transition. Here, in contrast, lithium-deficient ratio is demonstrated as a new approach to attain high capacity at high voltagemore » for layered oxide cathodes. Rapid and cost effective lithiation of a porous hydroxide precursor with lithium deficient ratio acted as a driving force to partially convert the layered material to spinel phase yielding in a multiphase structure (MPS) cathode material. Upon cycling, MPS revealed structural stability at high voltage and high temperature and resulted in fast lithium-ion diffusion by providing a distinctive SEI chemistry – MPS displayed minimum lithium loss in SEI and formed a thinner SEI. MPS thus offer high energy and high power applications and provides a new perspective compared to the conventional layered cathode materials denying the focus for lithium excess material.« less

High-performance electrodes for reduced temperature solid oxide fuel cells with doped lanthanum gallate electrolyte. II. La(Sr)CoO 3 cathode

NASA Astrophysics Data System (ADS)

Inagaki, Toru; Miura, Kazuhiro; Yoshida, Hiroyuki; Maric, Radenka; Ohara, Satoshi; Zhang, Xinge; Mukai, Kazuo; Fukui, Takehisa

The reduced temperature solid oxide fuel cell (SOFC) with 0.5 mm thick La 0.9Sr 0.1Ga 0.8Mg 0.2O 3- α (LSGM) electrolyte, La 0.6Sr 0.4CoO 3- δ (LSCo) cathode, and Ni-(CeO 2) 0.8(SmO 1.5) 0.2 (SDC) cermet anode showed an excellent initial performance, and high maximum power density, 0.47 W/cm 2, at 800°C. The results were comparable to those for the conventional SOFC with yttria-stabilized zirconia (YSZ) electrolyte, La(Sr)MnO 3-YSZ cathode and Ni-YSZ cermet anode at 1000°C. Using an LSCo powder prepared by spray pyrolysis, and selecting appropriate sintering temperatures, the lowest cathodic polarization of about 25 mV at 300 mA/cm 2 was measured for a cathode prepared by sintering at 1000°C. Life time cell test results, however, showed that the polarization of the LSCo cathode increased with operating time. From EPMA results, this behavior was considered to be related to the interdiffusion of the elements at the cathode/electrolyte interface. Calcination of LSCo powder could be a possible way to suppress this interdiffusion at the interface.

Surface transformation by a “cocktail” solvent enables stable cathode materials for sodium ion batteries

DOE PAGES

Mu, Linqin; Rahman, Muhammad Mominur; Zhang, Yan; ...

2018-01-09

Coating the surfaces of active materials has become an effective and indispensable path towards the stable operation of practical rechargeable batteries. Improving the affordability of coating processes can bring enormous manufacturing advantages to battery applications. Here in this paper, we report a cheap, simple and efficient method to create conformal coating layers on the primary particles of sodium layered oxide materials for improving battery performance. Mimicking the cathode–electrolyte interfacial reaction in practical cells, we create conformal coating layers via the spontaneous reaction between the oxidative cathode surfaces and a cocktail of reductive organic solvents. The conformal coating layers consist ofmore » metal–organic compounds with reduced transition metal cations, i.e., artificial cathode–electrolyte interphases (CEIs). The cells containing these coated cathode materials deliver much improved cycle life while maintaining reasonably high reversible capacity and rate capability. Furthermore, the structural stability and water resistance are enhanced, which can practically help simplify the storage protocol of cathode powders prior to battery manufacturing. The surfaces of most oxide cathode materials (e.g., lithium cathodes and sodium cathodes) are highly oxidative, and thus we expect that the present method, with tailored experimental parameters, can be readily applied to most battery systems.« less

Co3O4 nanoparticles decorated carbon nanofiber mat as binder-free air-cathode for high performance rechargeable zinc-air batteries

NASA Astrophysics Data System (ADS)

Li, Bing; Ge, Xiaoming; Goh, F. W. Thomas; Hor, T. S. Andy; Geng, Dongsheng; Du, Guojun; Liu, Zhaolin; Zhang, Jie; Liu, Xiaogang; Zong, Yun

2015-01-01

An efficient, durable and low cost air-cathode is essential for a high performance metal-air battery for practical applications. Herein, we report a composite bifunctional catalyst, Co3O4 nanoparticles-decorated carbon nanofibers (CNFs), working as an efficient air-cathode in high performance rechargeable Zn-air batteries (ZnABs). The particles-on-fibers nanohybrid materials were derived from electrospun metal-ion containing polymer fibers followed by thermal carbonization and a post annealing process in air at a moderate temperature. Electrochemical studies suggest that the nanohybrid material effectively catalyzes oxygen reduction reaction via an ideal 4-electron transfer process and outperforms Pt/C in catalyzing oxygen evolution reactions. Accordingly, the prototype ZnABs exhibit a low discharge-charge voltage gap (e.g. 0.7 V, discharge-charge at 2 mA cm-2) with higher stability and longer cycle life compared to their counterparts constructed using Pt/C in air-cathode. Importantly, the hybrid nanofiber mat readily serves as an integrated air-cathode without the need of any further modification. Benefitting from its efficient catalytic activities and structural advantages, particularly the 3D architecture of highly conductive CNFs and the high loading density of strongly attached Co3O4 NPs on their surfaces, the resultant ZnABs show significantly improved performance with respect to the rate capability, cycling stability and current density, promising good potential in practical applications.An efficient, durable and low cost air-cathode is essential for a high performance metal-air battery for practical applications. Herein, we report a composite bifunctional catalyst, Co3O4 nanoparticles-decorated carbon nanofibers (CNFs), working as an efficient air-cathode in high performance rechargeable Zn-air batteries (ZnABs). The particles-on-fibers nanohybrid materials were derived from electrospun metal-ion containing polymer fibers followed by thermal carbonization and a post annealing process in air at a moderate temperature. Electrochemical studies suggest that the nanohybrid material effectively catalyzes oxygen reduction reaction via an ideal 4-electron transfer process and outperforms Pt/C in catalyzing oxygen evolution reactions. Accordingly, the prototype ZnABs exhibit a low discharge-charge voltage gap (e.g. 0.7 V, discharge-charge at 2 mA cm-2) with higher stability and longer cycle life compared to their counterparts constructed using Pt/C in air-cathode. Importantly, the hybrid nanofiber mat readily serves as an integrated air-cathode without the need of any further modification. Benefitting from its efficient catalytic activities and structural advantages, particularly the 3D architecture of highly conductive CNFs and the high loading density of strongly attached Co3O4 NPs on their surfaces, the resultant ZnABs show significantly improved performance with respect to the rate capability, cycling stability and current density, promising good potential in practical applications. Electronic supplementary information (ESI) available: TGA curves of as electrospun Co(ii)-PAN fiber and C-CoPAN900 EDX and XPS spectra of the C-CoPAN900 photo of a home-built Zn-air cell and the preparation method of conventional catalyst electrode; polarization curves and corresponding power density plots of the battery using conventional type cathode of C-CoPN900 and commercial Pt/C catalyst; the electrocatalytic properties of hybrid CNFs obtained from varied weight ratios of PAN to cobalt acetate, e.g. 16 : 1 and 8 : 1, and their corresponding TGA curves; a comparison of the Zn-air battery performance of this work with recent literatures. See DOI: 10.1039/c4nr05988c

Humidity-corrected Arrhenius equation: The reference condition approach.

PubMed

Naveršnik, Klemen; Jurečič, Rok

2016-03-16

Accelerated and stress stability data is often used to predict shelf life of pharmaceuticals. Temperature, combined with humidity accelerates chemical decomposition and the Arrhenius equation is used to extrapolate accelerated stability results to long-term stability. Statistical estimation of the humidity-corrected Arrhenius equation is not straightforward due to its non-linearity. A two stage nonlinear fitting approach is used in practice, followed by a prediction stage. We developed a single-stage statistical procedure, called the reference condition approach, which has better statistical properties (less collinearity, direct estimation of uncertainty, narrower prediction interval) and is significantly easier to use, compared to the existing approaches. Our statistical model was populated with data from a 35-day stress stability study on a laboratory batch of vitamin tablets and required mere 30 laboratory assay determinations. The stability prediction agreed well with the actual 24-month long term stability of the product. The approach has high potential to assist product formulation, specification setting and stability statements. Copyright © 2016 Elsevier B.V. All rights reserved.

3D printed cellular solid outperforms traditional stochastic foam in long-term mechanical response

DOE PAGES

Maiti, A.; Small, W.; Lewicki, J.; ...

2016-04-27

3D printing of polymeric foams by direct-ink-write is a recent technological breakthrough that enables the creation of versatile compressible solids with programmable microstructure, customizable shapes, and tunable mechanical response including negative elastic modulus. However, in many applications the success of these 3D printed materials as a viable replacement for traditional stochastic foams critically depends on their mechanical performance and micro-architectural stability while deployed under long-term mechanical strain. To predict the long-term performance of the two types of foams we employed multi-year-long accelerated aging studies under compressive strain followed by a time-temperature-superposition analysis using a minimum-arc-length-based algorithm. The resulting master curvesmore » predict superior long-term performance of the 3D printed foam in terms of two different metrics, i.e., compression set and load retention. To gain deeper understanding, we imaged the microstructure of both foams using X-ray computed tomography, and performed finite-element analysis of the mechanical response within these microstructures. As a result, this indicates a wider stress variation in the stochastic foam with points of more extreme local stress as compared to the 3D printed material, which might explain the latter’s improved long-term stability and mechanical performance.« less

3D printed cellular solid outperforms traditional stochastic foam in long-term mechanical response

DOE Office of Scientific and Technical Information (OSTI.GOV)

Maiti, A.; Small, W.; Lewicki, J.

3D printing of polymeric foams by direct-ink-write is a recent technological breakthrough that enables the creation of versatile compressible solids with programmable microstructure, customizable shapes, and tunable mechanical response including negative elastic modulus. However, in many applications the success of these 3D printed materials as a viable replacement for traditional stochastic foams critically depends on their mechanical performance and micro-architectural stability while deployed under long-term mechanical strain. To predict the long-term performance of the two types of foams we employed multi-year-long accelerated aging studies under compressive strain followed by a time-temperature-superposition analysis using a minimum-arc-length-based algorithm. The resulting master curvesmore » predict superior long-term performance of the 3D printed foam in terms of two different metrics, i.e., compression set and load retention. To gain deeper understanding, we imaged the microstructure of both foams using X-ray computed tomography, and performed finite-element analysis of the mechanical response within these microstructures. As a result, this indicates a wider stress variation in the stochastic foam with points of more extreme local stress as compared to the 3D printed material, which might explain the latter’s improved long-term stability and mechanical performance.« less