Strength of a Ceramic Sectored Flexure Specimen

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wereszczak, Andrew A; Duffy, Stephen F; Baker, E. H.

2008-01-01

A new test specimen, defined here as the "sectored flexure strength specimen", was developed to measure the strength of ceramic tubes specifically for circumstances when flaws located at the tube's outer diameter are the strength-limiter and subjected to axial tension. The understanding of such strength-limitation is relevant for when ceramic tubes are subjected to bending or when the internal temperature is hotter than the tube's exterior (e.g., heat exchangers). The specimen is both economically and statistically attractive because eight specimens (eight in the case of this project - but the user is not necessarily limited to eight) were extracted outmore » of each length of tube. An analytic expression for maximum or failure stress, and relationships portraying effective area and effective volume as a function of Weibull modulus were developed. Lastly, it was proven from the testing of two ceramics that the sectored flexure specimen was very effective at producing failures caused by strength-limiting flaws located on the tube's original outer diameter. Keywords: ceramics, strength, sectored flexure specimen, effective area, effective volume, finite-element analysis, Weibull distribution, and fractography.« less

In vivo and in vitro assessment of an intraoral dental colorimeter.

PubMed

Karaagaclioglu, Lale; Terzioglu, Hakan; Yilmaz, Burak; Yurdukoru, Bengul

2010-06-01

The purpose of this study was to assess the performance of an intraoral dental colorimeter. In vivo repeatability of an intraoral colorimeter was assessed by performing color measurements of 30 individuals' right maxillary central incisor. Three consecutive measurements from each individual were made. In the in vitro part of the study, 25 metal-ceramic and 25 all-ceramic specimens were prepared. Five shades of metal-ceramic and all-ceramic specimens were selected for color determination. A widely recognized in vitro colorimeter was used as the control group for the in vitro performance assessment of the in vivo colorimeter. The color differentiation capability of two colorimeters was compared with the readings obtained from ceramic specimens. DeltaE values between shade groups of ceramic specimens were calculated and statistically analyzed with Student's t-test. The repeatability of the intraoral instrument was evaluated statistically with Intraclass correlation coefficient. The in vivo evaluation results showed that the overall repeatability coefficient values of L*, a*, and b* notations of the intraoral colorimeter were "excellent." The color differences (DeltaE) calculated between the colorimeters were significant only between shades A(1)-B(1) for metal-ceramic specimens (p= 0.002); however, from 5 of 10 shade couples of all-ceramic specimens, the color differences obtained from the readings of the in vivo colorimeter were significantly different from that of the in vitro colorimeter (p < 0.001). For all specimens, the differences between DeltaE values were within clinically acceptable limits (<3.5). Within the limitations of this study, the intraoral colorimeter exhibited successful in vivo repeatability; however, the color difference detection performance of the device varied depending on the translucency of the specimens.

[Effect of core: dentin thickness ratio on the flexure strength of IPS Empress II heat-pressed all-ceramic restorative material].

PubMed

Liu, Yi-hong; Feng, Hai-lan; Bao, Yi-wang; Qiu, Yan

2007-02-18

To evaluate the effect of core:dentin thickness ratio on the flexure strength, fracture mode and origin of bilayered IPS Empress II ceramic composite specimens. IPS Empress II core ceramic, dentin porcelain and bilayered composite specimens with core:dentin thickness ratio of 2:1 and 1:1 were tested in three-point flexure strength. Mean strengths and standard deviations were determined. The optical microscopy was employed for identification of the fracture mode and origin. The flexure strength of dentin porcelain was the smallest(62.7 MPa), and the strength of bilayered composite specimens was smaller than single-layered core ceramic(190.2 MPa). The core: dentin ratio did not influence the strength of bilayered composite specimens. The frequency of occurrence of bilayered specimen delaminations was higher in the group of core: dentin thickness ratio of 1:1 than in the group of 2:1. IPS Empress II core ceramic was significantly stronger than veneering dentin porcelain. Core:dentin thickness ratio could significantly influence the fracture mode and origin, and bilayered IPS Empress II ceramic composite specimens showed little influence in the fracture strength.

XCT Study of Cone Crack Damage in Multilayered Transparent Panel Structures and Comparison to Modeling

DTIC Science & Technology

2012-08-01

Radiography Scans Each of the two specimens consists of three 14- × 14-in transparent ceramic plates with adhesive between them to bond them...vertically close to the centerline. The depth of the impact cavity in specimen 741-2 is beyond the relatively thin front ceramic plate . Figure 2...The points defining the corners of the ceramic plates in both specimens were also determined. Figure 5. Centerline XCT scan of specimen 740-1

Effect of an internal coating technique on tensile bond strengths of resin cements to zirconia ceramics.

PubMed

Kitayama, Shuzo; Nikaido, Toru; Maruoka, Rena; Zhu, Lei; Ikeda, Masaomi; Watanabe, Akihiko; Foxton, Richard M; Miura, Hiroyuki; Tagami, Junji

2009-07-01

This study was conducted to enhance the tensile bond strengths of resin cements to zirconia ceramics. Fifty-six zirconia ceramic specimens (Cercon Base) and twenty-eight silica-based ceramic specimens (GN-1, GN-1 Ceramic Block) were air-abraded using alumina. Thereafter, the zirconia ceramic specimens were divided into two subgroups of 28 each according to the surface pretreatment; no pretreatment (Zr); and the internal coating technique (INT). For INT, the surface of zirconia was coated by fusing silica-based ceramics (Cercon Ceram Kiss). Ceramic surfaces were conditioned with/without a silane coupling agent followed by bonding with one of two resin cements; Panavia F 2.0 (PF) and Superbond C&B (SB). After 24 hours storage in water, the tensile bond strengths were tested (n=7). For both PF and SB, silanization significantly improved the bond strength to GN-1 and INT (p<0.05). The INT coating followed by silanizaton demonstrated enhancement of bonding to zirconia ceramics.

Effects of silicon coating on bond strength of two different titanium ceramic to titanium.

PubMed

Ozcan, Isil; Uysal, Hakan

2005-08-01

This study investigated the effect of silicon coating (SiO2) by magnetron sputtering on bond strength of two different titanium ceramics to titanium. Sixty cast titanium specimens were prepared following the protocol ISO 9693. Titanium specimens were divided into two test and control groups with 15 specimens in each. Test groups were silicon coated by the magnetron sputtering technique. Two titanium ceramics (Triceram and Duceratin) were applied on both test (coated) and control (uncoated) metal specimens. The titanium-ceramic specimens were subjected to a three point flexural test. The groups were compared for their bond strength. SEM and SEM/EDS analyses were performed on the delaminated titanium surfaces to ascertain bond failure. The mean bond strength of Ti-Duceratin, Ti-Triceram, Si-coated Ti-Duceratin and Si-coated Ti-Triceram were 17.22+/-2.43, 23.31+/-3.18, 23.21+/-3.81 and 24.91+/-3.70 MPa, respectively. While the improvement in bond strength was 30% for Duceratin, it was statistically insignificant for Triceram. An adhesive mode of failure was observed in the Duceratin control group. In the silicoated Duceratin specimen, the bonded ceramic boundaries were wider but less than in the silicoated Triceram specimen. In the coated Triceram specimen, the ceramic retained areas were frequent and the failure mode was generally cohesive. Silicon coating was significantly effective in both preventing titanium oxide layer formation and in improving bond strength for Duceratin. However, it was of less value for Triceram.

Translucency of zirconia-based pressable ceramics with different core and veneer thicknesses.

PubMed

Jeong, Il-Do; Bae, So-Yeon; Kim, Dong-Yeon; Kim, Ji-Hwan; Kim, Woong-Chul

2016-06-01

Little information is available on the translucency of zirconia-based pressable ceramic restorations with a pressed ceramic veneer and zirconia core in various thickness combinations. The purpose of this in vitro study was to assess the translucency of 3 types of zirconia-based pressable ceramics for different core-veneer thickness combinations. A bilayered ceramic specimen was prepared with a pressable ceramic (IPS e.max Zirpress, Initial IQ, Rosetta UltraPress) veneer over a zirconia core (Zenostar Zr). Three groups of specimens (n=7) were formed with the following core+veneer thicknesses: 1 +0.5 mm, 0.7 +0.8 mm, and 0.5 +1 mm. To obtain consistent thickness and high translucency, all specimens were subjected to surface grinding with a grinding machine. To eliminate the effect of differences in roughness on the translucency, the surface roughness of the ground specimens was measured with a scanning profiler, and the consistency of these measured values was verified through statistical analysis. The luminous transmittance of the specimens was measured with a spectrophotometer. The effects of the pressable ceramic type and core-veneer thickness combination on transmittance were assessed using a 2-way ANOVA (α=.05). The consistency of the surface roughness among the tested specimens was confirmed using a 1-way ANOVA and the Tukey HSD post hoc test (P<.05). The luminous transmittance exhibited a statistically significant dependence on both the type of pressable ceramic and the core-veneer thickness combination (P<.05). The type of pressable ceramic and core-veneer thickness combination affected the translucency of the restoration. Copyright © 2016 Editorial Council for the Journal of Prosthetic Dentistry. Published by Elsevier Inc. All rights reserved.

Microwave processing of a dental ceramic used in computer-aided design/computer-aided manufacturing.

PubMed

Pendola, Martin; Saha, Subrata

2015-01-01

Because of their favorable mechanical properties and natural esthetics, ceramics are widely used in restorative dentistry. The conventional ceramic sintering process required for their use is usually slow, however, and the equipment has an elevated energy consumption. Sintering processes that use microwaves have several advantages compared to regular sintering: shorter processing times, lower energy consumption, and the capacity for volumetric heating. The objective of this study was to test the mechanical properties of a dental ceramic used in computer-aided design/computer-aided manufacturing (CAD/CAM) after the specimens were processed with microwave hybrid sintering. Density, hardness, and bending strength were measured. When ceramic specimens were sintered with microwaves, the processing times were reduced and protocols were simplified. Hardness was improved almost 20% compared to regular sintering, and flexural strength measurements suggested that specimens were approximately 50% stronger than specimens sintered in a conventional system. Microwave hybrid sintering may preserve or improve the mechanical properties of dental ceramics designed for CAD/CAM processing systems, reducing processing and waiting times.

Acousto-Ultrasonic analysis of failure in ceramic matrix composite tensile specimens

NASA Technical Reports Server (NTRS)

Kautz, Harold E.; Chulya, Abhisak

1993-01-01

Three types of acousto-ultrasonic (AU) measurements, stress-wave factor (SWF), lowest antisymmetric plate mode group velocity (VS), and lowest symmetric plate mode group velocity (VL), were performed on specimens before and after tensile failure. Three different Nicalon fiber architectures with ceramic matrices were tested. These composites were categorized as 1D (unidirectional fiber orientation) SiC/CAS glass ceramic, and 2D and 3D woven SiC/SiC ceramic matrix materials. SWF was found to be degraded after tensile failure in all three material categories. VS was found to be degraded only in the 1D SiC/CAS. VL was difficult to determine on the irregular specimen surfaces but appeared unchanged on all failed specimens. 3D woven specimens with heat-treatment at high temperature exhibited degradation only in SWF.

Experimental study of the fracture toughness of a ceramic/ceramic-matrix composite sandwich structure

DOE Office of Scientific and Technical Information (OSTI.GOV)

Li, Z.; Taya, M.; Dunn, M.L.

A hybrid experimental-numerical approach has been used to measure the fracture resistance of a sandwich structure consisting of a 304 stainless steel/partially stabilized zirconia ceramic-matrix composite crack-arresting layer embedded in a partially stabilized zirconia ceramic specimen. The mode 1 fracture toughness increases significantly when the crack propagates from the ceramic into the ceramic-matrix composite region. The increased toughening due to the stainless steel particles is explained reasonably well by a toughening model based on processing-induced thermal residual stresses. In addition, several experimental modifications were made to the chevron-notch wedge-loaded double cantilever beam specimen to overcome numerous problems encountered in generatingmore » a precrack in the small, brittle specimens used in this study.« less

Analysis of Subcritical Crack Growth in Dental Ceramics Using Fracture Mechanics and Fractography

PubMed Central

Taskonak, Burak; Griggs, Jason A.; Mecholsky, John J.; Yan, Jia-Hau

2008-01-01

Objectives The aim of this study was to test the hypothesis that the flexural strengths and critical flaw sizes of dental ceramic specimens will be affected by the testing environment and stressing rate even though their fracture toughness values will remain the same. Methods Ceramic specimens were prepared from an aluminous porcelain (Vitadur Alpha; VITA Zahnfabrik, Bad Säckingen, Germany) and an alumina-zirconia-glass composite (In-Ceram® Zirconia; VITA Zahnfabrik). Three hundred uniaxial flexure specimens (150 of each material) were fabricated to dimensions of 25 mm × 4 mm × 1.2 mm according to the ISO 6872 standard. Each group of 30 specimens was fractured in water using one of four different target stressing rates ranging on a logarithmic scale from 0.1 to 100 MPa/s for Vitadur Alpha and from 0.01 to 10 MPa/s for In-Ceram® Zirconia. The fifth group was tested in inert environment (oil) with a target stressing rate of 100 MPa/s for Vitadur Alpha and 1000 MPa/s for In-Ceram® Zirconia. The effects of stressing rate and environment on flexural strength, critical flaw size, and fracture toughness were analyzed statistically by Kruskal-Wallis one-way ANOVA on ranks followed by post-hoc comparisons using Dunn’s test (α=0.05). In addition, 20 Vitadur Alpha specimens were fabricated with controlled flaws to simplify fractography. Half of these specimens were fracture tested in water and half in oil at a target stressing rate of 100 MPa/s, and the results were compared using Mann-Whitney rank sum tests (α=0.05). A logarithmic regression model was used to determine the fatigue parameters for each material. Results For each ceramic composition, specimens tested in oil had significantly higher strength (P≤0.05) and smaller critical flaw size (significant for Vitadur Alpha, P≤0.05) than those tested in water but did not have significantly different fracture toughness (P>0.05). Specimens tested at faster stressing rates had significantly higher strength (P≤0.05) but did not have significantly different fracture toughness (P>0.05). Regarding critical flaw size, stressing rate had a significant effect for In-Ceram® Zirconia specimens (P≤0.05) but not for Vitadur Alpha specimens (P>0.05). Fatigue parameters, n and ln B, were 38.4 and −12.7 for Vitadur Alpha and were 13.1 and 10.4 for In-Ceram® Zirconia. Significance Moisture assisted subcritical crack growth had a more deleterious effect on In-Ceram® Zirconia core ceramic than on Vitadur Alpha porcelain. Fracture surface analysis identified fracture surface features that can potentially mislead investigators into misidentifying the critical flaw. PMID:17845817

Analysis of subcritical crack growth in dental ceramics using fracture mechanics and fractography.

PubMed

Taskonak, Burak; Griggs, Jason A; Mecholsky, John J; Yan, Jia-Hau

2008-05-01

The aim of this study was to test the hypothesis that the flexural strengths and critical flaw sizes of dental ceramic specimens will be affected by the testing environment and stressing rate even though their fracture toughness values will remain the same. Ceramic specimens were prepared from an aluminous porcelain (Vitadur Alpha; VITA Zahnfabrik, Bad Säckingen, Germany) and an alumina-zirconia-glass composite (In-Ceram Zirconia; VITA Zahnfabrik). Three hundred uniaxial flexure specimens (150 of each material) were fabricated to dimensions of 25 mmx4 mmx1.2 mm according to the ISO 6872 standard. Each group of 30 specimens was fractured in water using one of four different target stressing rates ranging on a logarithmic scale from 0.1 to 100 MPa/s for Vitadur Alpha and from 0.01 to 10 MPa/s for In-Ceram Zirconia. The fifth group was tested in inert environment (oil) with a target stressing rate of 100 MPa/s for Vitadur Alpha and 1000 MPa/s for In-Ceram Zirconia. The effects of stressing rate and environment on flexural strength, critical flaw size, and fracture toughness were analyzed statistically by Kruskal-Wallis one-way ANOVA on ranks followed by post hoc comparisons using Dunn's test (alpha=0.05). In addition, 20 Vitadur Alpha specimens were fabricated with controlled flaws to simplify fractography. Half of these specimens were fracture tested in water and half in oil at a target stressing rate of 100 MPa/s, and the results were compared using Mann-Whitney rank sum tests (alpha=0.05). A logarithmic regression model was used to determine the fatigue parameters for each material. For each ceramic composition, specimens tested in oil had significantly higher strength (P0.05). Specimens tested at faster stressing rates had significantly higher strength (P0.05). Regarding critical flaw size, stressing rate had a significant effect for In-Ceram Zirconia specimens (P0.05). Fatigue parameters, n and lnB, were 38.4 and -12.7 for Vitadur Alpha and were 13.1 and 10.4 for In-Ceram Zirconia. Moisture assisted subcritical crack growth had a more deleterious effect on In-Ceram Zirconia core ceramic than on Vitadur Alpha porcelain. Fracture surface analysis identified fracture surface features that can potentially mislead investigators into misidentifying the critical flaw.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Thangadurai, P.; Lumelsky, Yulia; Silverstein, Michael S.

Transmission electron microscopy (TEM) cross-section specimens of PMMA in contact with gold and Si were prepared by focused ion beam (FIB) and compared with plan-view PMMA specimens prepared by a dip-coating technique. The specimens were characterized by TEM and electron energy loss spectroscopy (EELS). In the cross-section specimens, the thin films of PMMA were located in a Si-PMMA-Au multilayer. Different thicknesses of PMMA films were spin-coated on the Si substrates. The thickness of the TEM specimens prepared by FIB was estimated using EELS to be 0.65 of the plasmon mean-free-path. Along the PMMA-Au interface, Au particle diffusion into the PMMAmore » was observed, and the size of the Au particles was in the range of 2-4 nm. Dip-coating of PMMA directly on Cu TEM grids resulted in thin specimens with a granular morphology, with a thickness of 0.58 of the plasmon mean-free-path. The dip-coated specimens were free from ion milling induced artifacts, and thus serve as control specimens for comparison with the cross-sectioned specimens prepared by FIB.« less

Influence of implant abutment material and ceramic thickness on optical properties.

PubMed

Jirajariyavej, Bundhit; Wanapirom, Peeraphorn; Anunmana, Chuchai

2018-05-01

Anterior shade matching is an essential factor influencing the esthetics of a ceramic restoration. Dentists face a challenge when the color of an implant abutment creates an unsatisfactory match with the ceramic restoration or neighboring teeth. The purpose of this in vitro study was to evaluate the influence of abutment material and ceramic thickness on the final color of different ceramic systems. Four experimental and control ceramic specimens in shade A3 were cut from IPS e.max CAD, IPS Empress CAD, and VITA Suprinity PC blocks. These specimens had thicknesses of 1.0 mm, 1.5 mm, 2.0 mm, and 2.5 mm, respectively, for the experimental groups, and 4 mm for the controls. Background abutment specimens were fabricated to yield 3 different shades: white zirconia, yellow zirconia, and titanium at a 3-mm thickness. All 3 ceramic specimens in each thickness were placed in succession on different abutment backgrounds with glycerin optical fluid in between, and the color was measured. A digital spectrophotometer was used to record the specimen color value in the Commission Internationale De L'éclairage (CIELab) color coordinates system and to calculate the color difference (ΔE) between the control and experimental groups. The Kruskal-Wallis test was used to analyze the effect of ceramic thickness on different abutments, and the pair-wise test was used to evaluate within the group (α=.05). The color differences between the test groups and the control decreased with increasing ceramic thickness for every background material. In every case, significant differences were found between 1.0- and 2.5-mm ceramic thicknesses. Only certain 2.5-mm e.max CAD, VITA Suprinity PC, and Empress CAD specimens on yellow-shade zirconia or VITA Suprinity PC on titanium were identified as clinically acceptable (ΔE<3). Increasing ceramic restoration thickness over the abutment background decreased the color mismatch. Increasing the thickness of ceramic on a yellow-shaded zirconia abutment rather than on titanium or white zirconia yielded a more esthetic color for the whole restoration. Copyright © 2017 Editorial Council for the Journal of Prosthetic Dentistry. Published by Elsevier Inc. All rights reserved.

Shear Bond Strength of Resin Buttons to Lithium Disilicate and Leucite Reinforced Feldspathic Restorations

DTIC Science & Technology

2016-05-01

Hydrofluoric acid, silane coupling agent, light cured composite and ceramic restoration specimens (10 of each IPS e.max and Empress). The surface treatment...cured composite and ceramic restoration specimens (10 of each IPS e.max and Empress). The surface treatment in group C was applied to all specimens...and light cured for 20 seconds. 4) Group D: 5% Hydrofluoric acid, silane coupling agent, light cured composite and ceramic restoration (10 of

Giant strain with ultra-low hysteresis and high temperature stability in grain oriented lead-free K0.5Bi0.5TiO3-BaTiO3-Na0.5Bi0.5TiO3 piezoelectric materials

PubMed Central

Maurya, Deepam; Zhou, Yuan; Wang, Yaojin; Yan, Yongke; Li, Jiefang; Viehland, Dwight; Priya, Shashank

2015-01-01

We synthesized grain-oriented lead-free piezoelectric materials in (K0.5Bi0.5TiO3-BaTiO3-xNa0.5Bi0.5TiO3 (KBT-BT-NBT) system with high degree of texturing along the [001]c (c-cubic) crystallographic orientation. We demonstrate giant field induced strain (~0.48%) with an ultra-low hysteresis along with enhanced piezoelectric response (d33 ~ 190pC/N) and high temperature stability (~160°C). Transmission electron microscopy (TEM) and piezoresponse force microscopy (PFM) results demonstrate smaller size highly ordered domain structure in grain-oriented specimen relative to the conventional polycrystalline ceramics. The grain oriented specimens exhibited a high degree of non-180° domain switching, in comparison to the randomly axed ones. These results indicate the effective solution to the lead-free piezoelectric materials. PMID:25716551

Giant strain with ultra-low hysteresis and high temperature stability in grain oriented lead-free K₀̣₅Bi₀̣₅TiO₃-BaTiO₃-Na₀̣₅Bi₀̣₅TiO₃ piezoelectric materials

DOE Office of Scientific and Technical Information (OSTI.GOV)

Maurya, Deepam; Zhou, Yuan; Wang, Yaojin

2015-02-26

We synthesized grain-oriented lead-free piezoelectric materials in (K₀̣₅Bi₀̣₅TiO₃-BaTiO₃-xNa₀̣₅Bi₀̣₅TiO₃ (KBT-BT-NBT) system with high degree of texturing along the [001]c (c-cubic) crystallographic orientation. We demonstrate giant field induced strain (~0.48%) with an ultra-low hysteresis along with enhanced piezoelectric response (d₃₃ ~ 190pC/N) and high temperature stability (~160°C). Transmission electron microscopy (TEM) and piezoresponse force microscopy (PFM) results demonstrate smaller size highly ordered domain structure in grain-oriented specimen relative to the conventional polycrystalline ceramics. The grain oriented specimens exhibited a high degree of non-180° domain switching, in comparison to the randomly axed ones. These results indicate the effective solution to the lead-free piezoelectricmore » materials.« less

Shear bond strength comparison between conventional porcelain fused to metal and new functionally graded dental restorations after thermal-mechanical cycling.

PubMed

Henriques, B; Gonçalves, S; Soares, D; Silva, F S

2012-09-01

The aim of this study was to evaluate the effect of thermo-mechanical cycling on the metal-ceramic bond strength of conventional porcelain fused to metal restorations (PFM) and new functionally graded metal-ceramic dental restorations (FGMR). Two types of specimens were produced: PFM and FGMR specimens. PFM specimens were produced by conventional PFM technique. FGMR specimens were hot pressed and prepared with a metal/ceramic composite interlayer (50 M, vol%) at the metal-ceramic interface. They were manufactured and standardized in cylindrical format and then submitted to thermal (3000, 6000 and 12,000 cycles; between 5 °C and 60 °C; dwell time: 30s) and mechanical (25,000, 50,000 and 100,000 cycles under a load of 50 N; 1.6 Hz) cycling. The shear bond strength tests were performed in a universal testing machine (crosshead speed: 0.5mm/min), using a special device to concentrate the tension at the metal-ceramic interface and the load was applied until fracture. The metal-ceramic interfaces were examined with SEM/EDS prior to and after shear tests. The Young's modulus and hardness were measured across the interfaces of both types of specimens using nanoindentation tests. Data was analyzed with Shapiro-Wilk test to test the assumption of normality. The 2-way ANOVA was used to compare shear bond strength results (p<0.05). FGMR specimens showed significantly (p<0.001) higher shear bond strength results than PFM specimens, irrespective of fatigue conditions. Fatigue conditions significantly (p<0.05) affected the shear bond strength results. The analysis of surface fracture revealed adhesive fracture type for PFM specimens and mixed fracture type for FGMR specimens. Nanoindentation tests showed differences in mechanical properties measured across the metal-ceramic interface for the two types of specimens, namely Young's Modulus and hardness. This study showed significantly better performance of the new functionally graded restorations relative to conventional PFM restorations, under fatigue testing conditions and for the materials tested. Copyright © 2012 Elsevier Ltd. All rights reserved.

Influences of multiple firings and aging on surface roughness, strength and hardness of veneering ceramics for zirconia frameworks.

PubMed

Tang, Xuehua; Luo, Huinan; Bai, Yang; Tang, Hui; Nakamura, Takashi; Yatani, Hirofumi

2015-09-01

To evaluate the effects of multiple firings and aging on surface roughness, strength, and hardness of veneering ceramics for zirconia frameworks. Five different veneering ceramics for zirconia frameworks were used: Vintage ZR (ZR), Cerabien ZR (CZR), VitaVM9 (VM9), Cercon ceram KISS (KISS), and IPS e.max ceram (e.max). Specimens were fired 2 or 10 times in order to accelerate aging. Surface roughness was evaluated using laser profilometry. Flexural strength and Vickers hardness were also measured. Surface topography was observed using scanning electron microscopy. After accelerated aging, the surface roughness of all specimens fired 10 times was significantly lower than that of the same specimens fired 2 times (P=0.000). Except for VM9, the flexural strength of all specimens fired 10 times was greater than that of the same specimens fired 2 times, and the differences were significant for ZR and CZR (P<0.01). The flexural strength of VM9 fired 10 times was significantly lower than that of VM9 fired 2 times (P=0.034). The Vickers hardness of ZR and VM9 fired 10 times was significantly higher than that of the same specimens fired 2 times (P<0.05), but that of KISS fired 10 times was significantly lower than that of KISS fired 2 times (P=0.000). Multiple firings had a positive effect on the surface roughness of all aged veneering ceramics used for zirconia restorations and on the strength and hardness of many aged veneering ceramics used for zirconia restorations. Copyright © 2015 Elsevier Ltd. All rights reserved.

The strength of sintered and adhesively bonded zirconia/veneer-ceramic bilayers.

PubMed

Costa, Anna Karina F; Borges, Alexandre Luiz S; Fleming, Garry James P; Addison, Owen

2014-10-01

Recently all-ceramic restorative systems have been introduced that use CAD/CAM technology to fabricate both the Y-TZP core and veneer-ceramic layers. The aim was to identify whether the CAD/CAM approach resulted in more favourable stressing patterns in the veneer-ceramic when compared with a conventionally sintered Y-TZP core/veneer-ceramic. Nominally identical Vita VM9 veneer-ceramic disc-shaped specimens (0.7mm thickness, 12mm diameter) were fabricated. 20 specimens received a surface coating of resin-cement (Panavia 21); 20 specimens were bonded with the resin-cement to fully sintered Y-TZP (YZ Vita Inceram Vita) discs (0.27mm thickness, 12mm diameter). A final series of 20 Y-TZP core/veneer-ceramic specimens were manufactured using a conventional sintering route. Biaxial flexure strength was determined in a ball-on-ring configuration and stress at the fracture origin calculated using multilayer closed-form analytical solutions. Fractography was undertaken using scanning electron microscopy. The experimental test was simulated using Finite Element Analysis. Group mean BFS were compared using a one-way ANOVA and post hoc Tukey tests at a 95% significance level. Resin cement application resulted in significant strengthening of the veneer-ceramic and further significant strengthening of the veneer-ceramic (p<0.01) occurred following bonding to the Y-TZP core. The BFS calculated at the failure origin for conventionally sintered specimens was significantly reduced when compared with the adhesively bonded Y-TZP/veneer-ceramic. Under the test conditions employed adhesive cementation between CAD/CAM produced Y-TZP/veneer-ceramic layers appears to offer the potential to induce more favourable stress states within the veneer-ceramic when compared with conventional sintered manufacturing routes. The current investigation suggests that the stressing patterns that arise in all-ceramic restorations fabricated using CAD/CAM for both the core and veneer-ceramic layers differ from those that occur in conventionally sintered bilayer restorations. Further work is required to ascertain whether such differences will translate into improved clinical outcomes. Copyright © 2014 Elsevier Ltd. All rights reserved.

Effect of abutment shade, ceramic thickness, and coping type on the final shade of zirconia all-ceramic restorations: in vitro study of color masking ability.

PubMed

Oh, Seon-Hee; Kim, Seok-Gyu

2015-10-01

The aim of the study was to evaluate the effect of abutment shade, ceramic thickness, and coping type on the final shade of zirconia all-ceramic restorations. Three different types of disk-shaped zirconia coping specimens (Lava, Cercon, Zirkonzahn: ø10 mm × 0.4 mm) were fabricated and veneered with IPS e.max Press Ceram (shade A2), for total thicknesses of 1 and 1.5 mm. A total of sixty zirconia restoration specimens were divided into six groups based on their coping types and thicknesses. The abutment specimens (ø10 mm × 7 mm) were prepared with gold alloy, base metal (nickel-chromium) alloy, and four different shades (A1, A2, A3, A4) of composite resins. The average L*, a*, b* values of the zirconia specimens on the six abutment specimens were measured with a dental colorimeter, and the statistical significance in the effects of three variables was analyzed by using repeated measures analysis of variance (α=.05).The average shade difference (ΔE) values of the zirconia specimens between the A2 composite resin abutment and other abutments were also evaluated. The effects of zirconia specimen thickness (P<.001), abutment shade (P<.001), and type of zirconia copings (P<.003) on the final shade of the zirconia restorations were significant. The average ΔE value of Lava specimens (1 mm) between the A2 composite resin and gold alloy abutments was higher (close to the acceptability threshold of 5.5 ΔE) than th ose between the A2 composite resin and other abutments. This in-vitro study demonstrated that abutment shade, ceramic thickness, and coping type affected the resulting shade of zirconia restorations.

Effect of two-step and one-step surface conditioning of glass ceramic on adhesion strength of orthodontic bracket and effect of thermo-cycling on adhesion strength.

PubMed

Asiry, Moshabab A; AlShahrani, Ibrahim; Alaqeel, Samer M; Durgesh, Bangalore H; Ramakrishnaiah, Ravikumar

2018-08-01

The adhesion strength of orthodontic brackets bonded to dental glass ceramics was evaluated after ceramic surface was treated with two-step and one-step surface conditioning systems, and subjecting to thermo-cycling. A total of forty specimens were fabricated from silica based glass ceramic (lithium disilicate) by duplicating the buccal surface of maxillary first premolar. The specimens were randomly assigned to two experimental groups (n = 20), group one specimens were treated with two-step surface conditioning system (IPS ceramic etching gel™ and Monobond plus™) and group two specimens were treated with one-step surface conditioning system (Monobond etch and prime™). The surface roughness of the specimens after treatment with two-step and one-step surface conditioning system was measured using non-contact surface profilometer. Ten randomly selected specimens from each group were subjected to thermo-cycling and the remaining ten served as baseline. The shear bond strength of the specimens was measured using universal material testing machine. The adhesive remnant index score was calculated, and the results of surface roughness and bond strength were tabulated and subjected to analysis of variance and post hoc tukey's test at a significance level of p < 0.05. The results of the study showed that the specimens treated with two-step conditioning system had higher surface roughness and bond strength than one-step conditioning system. The majority of the specimens treated with both two-step and one-step conditioned specimens showed adhesive failure after subjecting thermo-cycling. Traditional two-step conditioning provides better bond strength. The clinical importance of the study is that, the silane promoted adhesion significantly reduces on exposure to thermo-cycling. Copyright © 2018 Elsevier Ltd. All rights reserved.

Illuminating light-dependent color shifts in core and veneer layers of dental all-ceramics.

PubMed

Lee, Yong-Keun; Cha, Hyun-Suk; Yu, Bin

2014-09-01

The color of an object is perceived differently depending on the ambient light conditions. Since dental all-ceramic restorations are fabricated by building up several layers to reproduce the tooth shade, the optical properties of each layer should be optimized for successful shade reproduction. This study aimed to determine the separate contributions of the color shifts in each of the core and veneer layers of all-ceramics by switching the illuminating lights on the color shifts of layered ceramics. Specimens of seven kinds of core ceramics and the corresponding veneer ceramics for each core were fabricated with a layered thickness of 1.5 mm. A sintering ceramic was used as a reference core material. The Commission Internationale de l’Eclairage (CIE) color coordinates of core, veneer, and layered specimens were measured with a spectroradiometer under the CIE illuminant D65 (daylight), A (incandescent lamp), and F9 (fluorescent lamp) simulating lights. Color shifts of the layered specimens were primarily determined by the CIE a shifts (D65 to A switch) or by the CIE b shifts (D65 to F9 switch) of the veneer layer. The color coordinates shifts in the constituent layers differentially influenced those of the layered specimens by the kind of switched lights. Therefore, the optical properties of the constituent layers of all-ceramics should be controlled to reflect these findings.

Illuminating light-dependent color shifts in core and veneer layers of dental all-ceramics

NASA Astrophysics Data System (ADS)

Lee, Yong-Keun; Cha, Hyun-Suk; Yu, Bin

2014-09-01

The color of an object is perceived differently depending on the ambient light conditions. Since dental all-ceramic restorations are fabricated by building up several layers to reproduce the tooth shade, the optical properties of each layer should be optimized for successful shade reproduction. This study aimed to determine the separate contributions of the color shifts in each of the core and veneer layers of all-ceramics by switching the illuminating lights on the color shifts of layered ceramics. Specimens of seven kinds of core ceramics and the corresponding veneer ceramics for each core were fabricated with a layered thickness of 1.5 mm. A sintering ceramic was used as a reference core material. The Commission Internationale de l'Eclairage (CIE) color coordinates of core, veneer, and layered specimens were measured with a spectroradiometer under the CIE illuminant D65 (daylight), A (incandescent lamp), and F9 (fluorescent lamp) simulating lights. Color shifts of the layered specimens were primarily determined by the CIE a* shifts (D65 to A switch) or by the CIE b* shifts (D65 to F9 switch) of the veneer layer. The color coordinates shifts in the constituent layers differentially influenced those of the layered specimens by the kind of switched lights. Therefore, the optical properties of the constituent layers of all-ceramics should be controlled to reflect these findings.

The influence of cutting speed and cutting initiation location in specimen preparation for the microtensile bond strength test.

PubMed

Abreu, Celina Wanderley; Santosb, Jarbas F; Passos, Sheila Pestana; Michida, Silvia Masae; Takahashi, Fernando Eidi; Bottino, Marco Antonio

2011-06-01

This study evaluated the effect of cutting initiation location and cutting speed on the bond strength between resin cement and feldspathic ceramic. Thirty-six blocks (6.4 x 6.4 x 4.8 mm) of ceramic (Vita VM7) were produced. The ceramic surfaces were etched with 10% hydrofluoric acid gel for 60 s and then silanized. Each ceramic block was placed in a silicon mold with the treated surface exposed. A resin cement (Variolink II) was injected into the mold over the treated surface and polymerized. The resin cement-ceramic blocks were divided into two groups according to experimental conditions: a) cutting initiation location - resin cement, ceramic and interface; and b) cutting speed - 10,000, 15,000, and 20,000 rpm. The specimens were sectioned to achieve non-trimmed bar specimens. The microtensile test was performed in a universal testing machine (1 mm/min). The failure modes were examined using an optical light microscope and SEM. Bond strength results were analyzed using one-way ANOVA and Tukey's test (α = 0.05). Significant influences of cutting speed and initiation location on bond strength (p < 0.05) were observed. The highest mean was achieved for specimens cut at 15,000 rpm at the interface (15.12 ± 5.36 MPa). The lowest means were obtained for specimens cut at the highest cutting speed in resin cement (8.50 ± 3.27 MPa), and cut at the lowest cutting speed in ceramic (8.60 ± 2.65 MPa). All groups showed mainly mixed failure (75% to 100%). The cutting speed and initiation location are important factors that should be considered during specimen preparation for microtensile bond strength testing, as both may influence the bond strength results.

[In vitro study on shear bond strength of veneering ceramics to zirconia].

PubMed

Hu, Xiaoping; Zhu, Hongshui; Zeng, Liwei

2012-12-01

To investigate the shear bond strength between veneering ceramic and zirconia core in different all-ceramic systems. Twenty disk-shaped specimens with 8 mm in diameter and 3 mm in height for each zirconia system (Lava, Cercon, IPS e.max ZirCAD, Procera) were fabricated respectively and divided into four groups: Lava group, Cercon group, IPS e.max ZirCAD group, Procera group. For each group, 10 specimens were sintered with 1 mm corresponding veneering ceramic, while the other were sintered with 2 mm corresponding veneering ceramic respectively. The shear bond strength and fracture mode of specimens were observed and determined. The values of shear bond strength for Lava, Cercon, IPS e.max ZirCAD and Procera were (13.82 +/- 3.71), (13.24 +/- 2.09), (6.37 +/- 4.15), (5.19 +/- 5.31) MPa in the group of 1 mm thicked veneering ceramics, respectively, while the values in the group of 2mm thicked veneering ceramics were (38.77 +/- 1.69), (21.67 +/- 3.34), (12.70 +/- 4.24), (9.94 +/- 6.67) MPa. The values of Lava and Cercon groups were significantly higher than that of IPS e.max ZirCAD and Procera groups (P < 0.05). And the values of 2 mm thicked veneering ceramic group were significantly higher than that in 1 mm thicked groups (P < 0.05). Adhesive fracture between core and veneering ceramics were observed in the fracture modes of most specimens. The shear bond strength of veneering ceramic to the zirconia framework are different from the zirconia system we chose, and the thickness of veneering ceramic has a great impact on its shear bond strength.

Ceramic Matrix Composite Vane Subelement Burst Testing

NASA Technical Reports Server (NTRS)

Brewer, David N.; Verrilli, Michael; Calomino, Anthony

2006-01-01

Burst tests were performed on Ceramic Matrix Composite (CMC) vane specimens, manufactured by two vendors, under the Ultra Efficient Engine Technology (UEET) project. Burst specimens were machined from the ends of 76mm long vane sub-elements blanks and from High Pressure Burner Rig (HPBR) tested specimens. The results of burst tests will be used to compare virgin specimens with specimens that have had an Environmental Barrier Coating (EBC) applied, both HPBR tested and untested, as well as a comparison between vendors.

Static and Dynamic Electron Microscopy Investigations at the Atomic and Ultrafast Scales

NASA Astrophysics Data System (ADS)

Suri, Pranav Kumar

Advancements in the electron microscopy capabilities - aberration-corrected imaging, monochromatic spectroscopy, direct-electron detectors - have enabled routine visualization of atomic-scale processes with millisecond temporal resolutions in this decade. This, combined with progress in the transmission electron microscopy (TEM) specimen holder technology and nanofabrication techniques, allows comprehensive experiments on a wide range of materials in various phases via in situ methods. The development of ultrafast (sub-nanosecond) time-resolved TEM with ultrafast electron microscopy (UEM) has further pushed the envelope of in situ TEM to sub-nanosecond temporal resolution while maintaining sub-nanometer spatial resolution. A plethora of materials phenomena - including electron-phonon coupling, phonon transport, first-order phase transitions, bond rotation, plasmon dynamics, melting, and dopant atoms arrangement - are not yet clearly understood and could be benefitted with the current in situ TEM capabilities having atomic-level and ultrafast precision. Better understanding of these phenomena and intrinsic material dynamics (e.g. how phonons propagate in a material, what time-scales are involved in a first-order phase transition, how fast a material melts, where dopant atoms sit in a crystal) in new-generation and technologically important materials (e.g. two-dimensional layered materials, semiconductor and magnetic devices, rare-earth-element-free permanent magnets, unconventional superconductors) could bring a paradigm shift in their electronic, structural, magnetic, thermal and optical applications. Present research efforts, employing cutting-edge static and dynamic in situ electron microscopy resources at the University of Minnesota, are directed towards understanding the atomic-scale crystallographic structural transition and phonon transport in an iron-pnictide parent compound LaFeAsO, studying the mechanical stability of fast moving hard-drive heads in heat-assisted magnetic recording (HAMR) technology, exploring the possibility of ductile ceramics in magnesium oxide (MgO) nanomaterials, and revealing the atomic-structure of newly discovered rare-earth-element-free iron nitride (FeN) magnetic materials. Via atomic-resolution imaging and electron diffraction coupled with in situ TEM cooling on LaFeAsO, it was found that additional effects not related to the structural transition, namely dynamical scattering and electron channeling, can give signatures reminiscent of those typically associated with the symmetry change. UEM studies on LaFeAsO revealed direct, real-space imaging of the emergence and evolution of acoustic phonons and resolved dispersion behavior during propagation and scattering. Via UEM bright-field imaging, megahertz vibrational frequencies were observed upon laser-illumination in TEM specimens made out of HAMR devices which could be detrimental to their long-term thermal and structural reliability. Compression testing of 100-350 nm single-crystal MgO nanocubes shows size-dependent stresses and engineering strains of 4-13.8 GPa and 0.046-0.221 respectively at the first signs of yield accompanied by an absence of brittle fracture, which is a significant increase in plasticity of a brittle ceramic material. Atomic-scale characterization of FeN phases show that it is possible to detect interstitial locations of low atomic-number nitrogen atoms in iron crystal and hints at a development of novel routes (without involving rare-earth elements) for bulk permanent magnet synthesis.

Acousto-ultrasonic evaluation of ceramic matrix composite materials

NASA Technical Reports Server (NTRS)

Dosreis, Henrique L. M.

1991-01-01

Acousto-ultrasonic nondestructive evaluation of ceramic composite specimens with a lithium-alumino-silicate glass matrix reinforced with unidirectional silicon carbide (NICALON) fibers was conducted to evaluate their reserve of strength. Ceramic composite specimens with different amount of damage were prepared by four-point cyclic fatigue loading of the specimens at 500 C for a different number of cycles. The reserve of strength of the specimens was measured as the maximum bending stress recorded during four-pointed bending test with the load monotonically increased until failure occurs. It was observed that the reserve of strength did not correlate with the number of fatigue cycles. However, it was also observed that higher values of the stress wave factor measurements correspond to higher values of the reserve of strength test data. Therefore, these results show that the acousto-ultrasonic approach has the potential of being used to monitor damage and to estimate the reserve of strength of ceramic composites.

Flexural strength and failure modes of layered ceramic structures.

PubMed

Borba, Márcia; de Araújo, Maico D; de Lima, Erick; Yoshimura, Humberto N; Cesar, Paulo F; Griggs, Jason A; Della Bona, Alvaro

2011-12-01

To evaluate the effect of the specimen design on the flexural strength (σ(f)) and failure mode of ceramic structures, testing the hypothesis that the ceramic material under tension controls the mechanical performance of the structure. Three ceramics used as framework materials for fixed partial dentures (YZ--Vita In-Ceram YZ; IZ--Vita In-Ceram Zirconia; AL--Vita In-Ceram AL) and two veneering porcelains (VM7 and VM9) were studied. Bar-shaped specimens were produced in three different designs (n=10): monolithic, two layers (porcelain-framework) and three layers (TRI) (porcelain-framework-porcelain). Specimens were tested for three-point flexural strength at 1MPa/s in 37°C artificial saliva. For bi-layered design, the specimens were tested in both conditions: with porcelain (PT) or framework ceramic (FT) layer under tension. Fracture surfaces were analyzed using stereomicroscope and scanning electron microscopy (SEM). Young's modulus (E) and Poisson's ratio (ν) were determined using ultrasonic pulse-echo method. Results were statistically analyzed by Kruskal-Wallis and Student-Newman-Keuls tests. Except for VM7 and VM9, significant differences were observed for E values among the materials. YZ showed the highest ν value followed by IZ and AL. YZ presented the highest σ(f). There was no statistical difference in the σ(f) value between IZ and IZ-FT and between AL and AL-FT. σ(f) values for YZ-PT, IZ-PT, IZ-TRI, AL-PT, AL-TRI were similar to the results obtained for VM7 and VM9. Two types of fracture mode were identified: total and partial failure. The mechanical performance of the specimens was determined by the material under tension during testing, confirming the study hypothesis. Copyright © 2011 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Effect of different aging methods on the mechanical behavior of multi-layered ceramic structures.

PubMed

Borba, Márcia; de Araújo, Maico D; Fukushima, Karen A; Yoshimura, Humberto N; Griggs, Jason A; Della Bona, Álvaro; Cesar, Paulo F

2016-12-01

To evaluate the effect of two aging methods (mechanical cycling and autoclave) on the mechanical behavior of veneer and framework ceramic specimens with different configurations (monolithic, two and three-layers). Three ceramics used as framework for fixed dental prostheses (YZ-Vita In-Ceram YZ; IZ-Vita In-Ceram Zirconia; AL-Vita In-Ceram AL) and two veneering porcelains (VM7 and VM9) were studied. Bar-shaped specimens were produced in three different designs: monolithic, two layers (porcelain-framework) and three layers (porcelain-framework-porcelain). Specimens were tested for three-point flexural strength at 1MPa/s in 37°C artificial saliva. Three different experimental conditions were evaluated (n=10): control; mechanical cycling (2Hz, 37°C artificial saliva); and autoclave aging (134°C, 2 bars, 5h). Bi-layered specimens were tested in both conditions: with porcelain or framework ceramic under tension. Fracture surfaces were analyzed using stereomicroscope and scanning electron microscopy. Results were statistically analyzed using Kruskal-Wallis and Student-Newman-Keuls tests. Only for AL group, mechanical cycling and autoclave aging significantly decreased the flexural strength values in comparison to the control (p<0.01). YZ, AL, VM7 and VM9 monolithic groups showed no strength degradation. For multi-layered specimens, when the porcelain layer was tested in tension (bi and tri-layers), the aging methods evaluated also had no effect on strength (p≥0.05). Total and partial failure modes were identified. Mechanical cycling and autoclave aging protocols had no effect on the flexural strength values and failure behavior of YZ and IZ ceramic structures. Yet, AL monolithic structures showed a significant decrease in flexural strength with any of the aging methods. Copyright © 2016. Published by Elsevier Ltd.

Optimum Design of a Ceramic Tensile Creep Specimen Using a Finite Element Method

PubMed Central

Wang, Z.; Chiang, C. K.; Chuang, T.-J.

1997-01-01

An optimization procedure for designing a ceramic tensile creep specimen to minimize stress concentration is carried out using a finite element method. The effect of pin loading and the specimen geometry are considered in the stress distribution calculations. A growing contact zone between the pin and the specimen has been incorporated into the problem solution scheme as the load is increased to its full value. The optimization procedures are performed for the specimen, and all design variables including pinhole location and pinhole diameter, head width, neck radius, and gauge length are determined based on a set of constraints imposed on the problem. In addition, for the purpose of assessing the possibility of delayed failure outside the gage section, power-law creep in the tensile specimen is considered in the analysis. Using a particular grade of advanced ceramics as an example, it is found that if the specimen is not designed properly, significant creep deformation and stress redistribution may occur in the head of the specimen resulting in undesirable (delayed) head failure of the specimen during the creep test. PMID:27805126

Optical properties of pre-colored dental monolithic zirconia ceramics.

PubMed

Kim, Hee-Kyung; Kim, Sung-Hun

2016-12-01

The purposes of this study were to evaluate the optical properties of recently marketed pre-colored monolithic zirconia ceramics and to compare with those of veneered zirconia and lithium disilicate glass ceramics. Various shades of pre-colored monolithic zirconia, veneered zirconia, and lithium disilicate glass ceramic specimens were tested (17.0×17.0×1.5mm, n=5). CIELab color coordinates were obtained against white, black, and grey backgrounds with a spectrophotometer. Color differences of the specimen pairs were calculated by using the CIEDE2000 (ΔE 00 ) formula. The translucency parameter (TP) was derived from ΔE 00 of the specimen against a white and a black background. X-ray diffraction was used to determine the crystalline phases of monolithic zirconia specimens. Data were analyzed with 1-way ANOVA, Scheffé post hoc, and Pearson correlation testing (α=0.05). For different shades of the same ceramic brand, there were significant differences in L * , a * , b * , and TP values in most ceramic brands. With the same nominal shade (A2), statistically significant differences were observed in L * , a * , b * , and TP values among different ceramic brands and systems (P<0.001). The color differences between pre-colored monolithic zirconia and veneered zirconia or lithium disilicate glass ceramics of the corresponding nominal shades ranged beyond the acceptability threshold. Due to the high L * values and low a * and b * values, pre-colored monolithic zirconia ceramics can be used with additional staining to match neighboring restorations or natural teeth. Due to their high value and low chroma, unacceptable color mismatch with adjacent ceramic restorations might be expected. Copyright © 2016 Elsevier Ltd. All rights reserved.

Effect of abutment shade, ceramic thickness, and coping type on the final shade of zirconia all-ceramic restorations: in vitro study of color masking ability

PubMed Central

Oh, Seon-Hee

2015-01-01

PURPOSE The aim of the study was to evaluate the effect of abutment shade, ceramic thickness, and coping type on the final shade of zirconia all-ceramic restorations. MATERIALS AND METHODS Three different types of disk-shaped zirconia coping specimens (Lava, Cercon, Zirkonzahn: ø10 mm × 0.4 mm) were fabricated and veneered with IPS e.max Press Ceram (shade A2), for total thicknesses of 1 and 1.5 mm. A total of sixty zirconia restoration specimens were divided into six groups based on their coping types and thicknesses. The abutment specimens (ø10 mm × 7 mm) were prepared with gold alloy, base metal (nickel-chromium) alloy, and four different shades (A1, A2, A3, A4) of composite resins. The average L*, a*, b* values of the zirconia specimens on the six abutment specimens were measured with a dental colorimeter, and the statistical significance in the effects of three variables was analyzed by using repeated measures analysis of variance (α=.05).The average shade difference (ΔE) values of the zirconia specimens between the A2 composite resin abutment and other abutments were also evaluated. RESULTS The effects of zirconia specimen thickness (P<.001), abutment shade (P<.001), and type of zirconia copings (P<.003) on the final shade of the zirconia restorations were significant. The average ΔE value of Lava specimens (1 mm) between the A2 composite resin and gold alloy abutments was higher (close to the acceptability threshold of 5.5 ΔE) than th ose between the A2 composite resin and other abutments. CONCLUSION This in-vitro study demonstrated that abutment shade, ceramic thickness, and coping type affected the resulting shade of zirconia restorations. PMID:26576252

Performance of universal adhesives on bonding to leucite-reinforced ceramic.

PubMed

Kim, Ryan Jin-Young; Woo, Jung-Soo; Lee, In-Bog; Yi, Young-Ah; Hwang, Ji-Yun; Seo, Deog-Gyu

2015-01-01

This study aimed to investigate the microshear bond strength of universal bonding adhesives to leucite-reinforced glass-ceramic. Leucite-reinforced glass-ceramic blocks were polished and etched with 9.5% hydrofluoric acid for 1 min. The specimens were assigned to one of four groups based on their surface conditioning (n = 16): 1) NC: negative control with no further treatment; 2) SBU: Single Bond Universal (3M ESPE); 3) ABU: ALL-BOND Universal (Bisco); and 4) PC: RelyX Ceramic Primer and Adper Scotchbond Multi-Purpose Adhesive (3M ESPE) as a positive control. RelyX Ultimate resin cement (3M ESPE) was placed on the pretreated ceramic and was light cured. Eight specimens from each group were stored in water for 24 h, and the remaining eight specimens were thermocycled 10,000 times prior to microshear bond strength evaluation. The fractured surfaces were examined by stereomicroscopy and scanning electron microscopy (SEM). After water storage and thermocycling, the microshear bond strength values decreased in the order of PC > SBU and ABU > NC (P < 0.05). Thermocycling significantly reduced the microshear bond strength, regardless of the surface conditioning used (P < 0.05). Cohesive failure in the ceramic and mixed failure in the ceramic and resin cement were observed in the fractured specimens. The percentage of specimens with cohesive failure after 24 h of water storage was: NC (50%), SBU (75%), ABU (75%), and PC (87%). After thermocycling, the percentage of cohesive failure in NC decreased to 25%; however, yet the percentages of the other groups remained the same. Although the bond strength between resin and hydrofluoric acid-etched glass ceramic was improved when universal adhesives were used, conventional surface conditioning using a separate silane and adhesive is preferable to a simplified procedure that uses only a universal adhesive for cementation of leucite-reinforced glass-ceramic.

Residual interface tensile strength of ceramic bonded to dentin after cyclic loading and aging.

PubMed

Hernandez, Alfredo I; Roongruangphol, Thasanai; Katsube, Noriko; Seghi, Robert R

2008-03-01

To guard against the potential risk of cusp fracture, esthetic onlay restorations have been advocated for teeth with large restorations. The influence of the adhesive resin cement is believed to play a role in strengthening these restorations. The durability of this tooth/adhesive/ceramic interface is critical to ensure clinical longevity. The purpose of this study was to assess the effects of cyclic loading and environmental aging on the residual interface strength of a ceramic bonded to dentin structure. Eighteen simple trilayer specimens were fabricated, consisting of a 1.5-mm-thick ceramic plate (ProCAD) bonded to a flattened human molar tooth with exposed coronal dentin. The ceramic plates were bonded using resin cement (Nexus 2) and manufacturer-recommended bonding techniques. The specimens were divided into 3 equal groups and were stored in water at 37 degrees C for 10 weeks as a control group (CT), 9 months as an aging group (AG), or placed in water at 37 degrees C while being subjected to 10 million vertical loading cycles between 20 N to 200 N, as a fatigue group (FG). After the specimens were subjected to the experimental conditions, they were sectioned perpendicular to the flat ceramic surface into 1 x 1-mm sticks. The mean residual interface microtensile bond (MTB) strength was determined for each specimen using only those sticks which contained ceramic bonded to dentin. The MTB strength data were analyzed using Weibull analysis methods to determine differences between groups. All subsequent failed specimen surfaces were evaluated under a stereomicroscope at x10 magnification to determine the apparent failure modes. Some specimens were selected from each failure mode category for surface evaluation under a scanning electron microscope (SEM). The characteristic Weibull means for the 3 groups were CT, 19.2, FG, 14.7, and AG, 11.7. The bond strength of group CT was significantly greater than both AG (P=.007) and FG (P=.014). Light microscopic categorization of the failure modes suggests that adhesive failure at the ceramic/cement interface was the most common (65%) for all 3 groups. SEM evaluation of failed surfaces of select specimens from each group could not distinguish any interface appearance differences. For indirect adhesive-retained ceramic restorations, both cyclic masticatory loading and hydrolytic degradation may contribute to a weakening of the interface bond. The ceramic/resin interface may be more susceptible to these changes over the time frame of this investigation than the dentin/resin interface.

Repair bond strength of resin composite to bilayer dental ceramics

PubMed Central

2018-01-01

PURPOSE The purpose of this study was to investigate the effect of various surface treatments (ST) on the shear bond strength of resin composite to three bilayer dental ceramics made by CAD/CAM and two veneering ceramics. MATERIALS AND METHODS Three different bilayer dental ceramics and two different veneering ceramics were used (Group A: IPS e.max CAD+IPS e.max Ceram; Group B: IPS e.max ZirCAD+IPS e.max Ceram, Group C: Vita Suprinity+Vita VM11; Group D: IPS e.max Ceram; Group E: Vita VM11). All groups were divided into eight subgroups according to the ST. Then, all test specimens were repaired with a nano hybrid resin composite. Half of the test specimens were subjected to thermocycling procedure and the other half was stored in distilled water at 37℃. Shear bond strength tests for all test specimens were carried out with a universal testing machine. RESULTS There were statistically significant differences among the tested surface treatments within the all tested fracture types (P<.005). HF etching showed higher bond strength values in Groups A, C, D, and E than the other tested ST. However, bonding durability of all the surface-treated groups were similar after thermocycling (P>.00125). CONCLUSION This study revealed that HF etching for glass ceramics and sandblasting for zirconia ceramics were adequate for repair of all ceramic restorations. The effect of ceramic type exposed on the fracture area was not significant on the repair bond strength of resin composites to different ceramic types. PMID:29713430

Effect of etching with distinct hydrofluoric acid concentrations on the flexural strength of a lithium disilicate-based glass ceramic.

PubMed

Prochnow, Catina; Venturini, Andressa B; Grasel, Rafaella; Bottino, Marco C; Valandro, Luiz Felipe

2017-05-01

This study examined the effects of distinct hydrofluoric acid concentrations on the mechanical behavior of a lithium disilicate-based glass ceramic. Bar-shaped specimens were produced from ceramic blocks (e.max CAD, Ivoclar Vivadent). The specimens were polished, chamfered, and sonically cleaned in distilled water. The specimens were randomly divided into five groups (n = 23). The HF1, HF3, HF5, and HF10 specimens were etched for 20 s with acid concentrations of 1%, 3%, 5%, and 10%, respectively, while the SC (control) sample was untreated. The etched surfaces were evaluated using a scanning electron microscope and an atomic force microscope. Finally, the roughness was measured, and 3-point bending flexural tests were performed. The data were analyzed using one-way analysis of variance (ANOVA) and Tukey's test (α = 0.05). The Weibull modulus and characteristic strength were also determined. No statistical difference in the roughness and flexural strength was determined among the groups. The structural reliabilities (Weilbull moduli) were similar for the tested groups; however, the characteristic strength of the HF1 specimen was greater than that of the HF10 specimen. Compared with the untreated ceramic, the surface roughness and flexural strength of the ceramic were unaffected upon etching, regardless of the acid concentration. © 2016 Wiley Periodicals, Inc. J Biomed Mater Res Part B: Appl Biomater, 105B: 885-891, 2017. © 2016 Wiley Periodicals, Inc.

Changes to Glazed Dental Ceramic Shade, Roughness, and Microhardness after Bleaching and Simulated Brushing.

PubMed

Rodrigues, Carlos Roberto Teixeira; Turssi, Cecilia Pedroso; Amaral, Flávia Lucisano Botelho; Basting, Roberta Tarkany; França, Fabiana Mantovani Gomes

2017-09-05

To evaluate shade stability, surface roughness, microhardness, and compressive strength of a glazed feldspathic ceramic subjected to bleaching and simulated brushing. Eighty-eight glazed feldspathic ceramic specimens were made from microparticulate leucite and divided into eight groups (n = 10). The whitening products used were: Opalescence Trèswhite Supreme (Ultradent), Opalescence®\\ PF 15% (Ultradent), and Oral-B 3D White Whitestrips. All substances for whitening were used for 4 hours/day for a period of 14 days; the control group was not bleached. Next, half of the specimens were individually brushed. Microhardness and surface roughness data were subjected to three-way ANOVA and Tukey test. The diametrical tensile strength data were subjected to two-way ANOVA. The shade change data were analyzed using Kruskal-Wallis, Mann-Whitney, and the Student-Newman-Keuls test. The significance level was set at 5%. Glazed feldspathic ceramic surface microhardness was significantly affected by bleaching agents (p = 0.007). Initially, glazed ceramic microhardness was significantly higher than that observed after contact with the bleaching agents, whether or not brushing was performed. The specimens submitted to bleaching in preloaded trays presented lower surface roughness values after brushing (p = 0.037). The surface roughness was significantly lower in the brushed specimens (p = 0.044). The diametrical tensile strength was not significantly affected by the application of bleaching agents (p = 0.563) or by brushing (p = 0.477). When the specimens were brushed, however, shade change was significantly influenced by the bleaching agent used (p = 0.041). Bleaching agents associated with brushing cycles can alter surface properties and shade stability of glazed feldspathic ceramics, though such findings may not reflect the performance of unglazed feldspathic ceramics. © 2017 by the American College of Prosthodontists.

Plastic damage induced fracture behaviors of dental ceramic layer structures subjected to monotonic load.

PubMed

Wang, Raorao; Lu, Chenglin; Arola, Dwayne; Zhang, Dongsheng

2013-08-01

The aim of this study was to compare failure modes and fracture strength of ceramic structures using a combination of experimental and numerical methods. Twelve specimens with flat layer structures were fabricated from two types of ceramic systems (IPS e.max ceram/e.max press-CP and Vita VM9/Lava zirconia-VZ) and subjected to monotonic load to fracture with a tungsten carbide sphere. Digital image correlation (DIC) and fractography technology were used to analyze fracture behaviors of specimens. Numerical simulation was also applied to analyze the stress distribution in these two types of dental ceramics. Quasi-plastic damage occurred beneath the indenter in porcelain in all cases. In general, the fracture strength of VZ specimens was greater than that of CP specimens. The crack initiation loads of VZ and CP were determined as 958 ± 50 N and 724 ± 36 N, respectively. Cracks were induced by plastic damage and were subsequently driven by tensile stress at the elastic/plastic boundary and extended downward toward to the veneer/core interface from the observation of DIC at the specimen surface. Cracks penetrated into e.max press core, which led to a serious bulk fracture in CP crowns, while in VZ specimens, cracks were deflected and extended along the porcelain/zirconia core interface without penetration into the zirconia core. The rupture loads for VZ and CP ceramics were determined as 1150 ± 170 N and 857 ± 66 N, respectively. Quasi-plastic deformation (damage) is responsible for crack initiation within porcelain in both types of crowns. Due to the intrinsic mechanical properties, the fracture behaviors of these two types of ceramics are different. The zirconia core with high strength and high elastic modulus has better resistance to fracture than the e.max core. © 2013 by the American College of Prosthodontists.

A comparison of the fracture resistance of three machinable ceramics after thermal and mechanical fatigue.

PubMed

Yang, Rui; Arola, Dwayne; Han, Zhihui; Zhang, Xiuyin

2014-10-01

Mechanical and thermal fatigue may affect ceramic restorations in the oral environment. The purpose of this study was to determine the influence of thermal and mechanical cycling on the fracture load and fracture patterns of 3 machinable ceramics. Seventy-two human third molar teeth were prepared for bonding ceramic specimens of Sirona CEREC Blocs, IPS e.maxCAD, or inCoris ZI meso blocks. The 24 specimens of each ceramic were divided into 4 groups (n=6), which underwent no preloading (control), thermocycling (5°C-55°C, 2000 cycles), mechanical cycling (10(5) cycles, 100 N), and thermocycling (5°C-55°C, 2000 cycles) plus mechanical cycling (10(5) cycles, 100 N). The specimens were subsequently loaded to failure, and both stereomicroscopy and scanning electron microscopy were used to investigate the fracture patterns. The data were analyzed with 2-way ANOVA and the Fisher exact probability test (α=.05). Mechanical and thermal cycling had a significant influence on the critical load to failure of the 3 ceramics. No significant difference was found between mechanical cycling for 10(5) times and thermocycling for 2000 times within the same ceramic. The specimens of inCoris ZI experienced significantly higher fracture loads for all the groups. The fracture patterns of the 3 machinable ceramics showed that failure mainly occurred at the cement-dentin interface. The effects of combined thermal and mechanical cycling on the fracture load of ceramics were more significant than any individual mode of cyclic fatigue. Overall, the inCoris ZI resisted thermal and mechanical fatigue better than the Sirona CEREC and IPS e.maxCAD. Copyright © 2014 Editorial Council for the Journal of Prosthetic Dentistry. Published by Elsevier Inc. All rights reserved.

Effects of silica coating and silane surface conditioning on the bond strength of metal and ceramic brackets to enamel.

PubMed

Atsü, Saadet Sağlam; Gelgör, Ibrahim Erhan; Sahin, Volkan

2006-09-01

To evaluate the effect of tribochemical silica coating and silane surface conditioning on the bond strength of metal and ceramic brackets bonded to enamel surfaces with light-cured composite resin. Twenty metal and 20 ceramic brackets were divided into four groups (n = 10 for each group). The specimens were randomly assigned to one of the following treatment conditions of the metal and ceramic brackets' surface: (1) tribochemical silica coating combined with silane and (2) no treatment. Brackets were bonded to the enamel surface on the labial and lingual sides of human maxillary premolars (20 total) with a light-polymerized resin composite. All specimens were stored in water for 1 week at 37 degrees C and then thermocycled (5000 cycles, 5 degrees C to 55 degrees C, 30 seconds). The shear bond strength values were measured on a universal testing machine. Student's t-test was used to compare the data (alpha = 0.05). The types of failures were observed using a stereomicroscope. Metal and ceramic brackets treated with silica coating with silanization had significantly greater bond strength values (metal brackets: 14.2 +/- 1.7 MPa, P < .01; ceramic brackets: 25.9 +/- 4.4 MPa, P < .0001) than the control groups (metal brackets: 11.9 +/- 1.3 MPa; ceramic brackets: 15.6 +/- 4.2 MPa). Treated specimens of metal and ceramic exhibited cohesive failures in resin and adhesive failures at the enamel-adhesive interface, whereas control specimens showed mixed types of failures. Silica coating with aluminum trioxide particles coated with silica followed by silanization gave higher bond strengths in both metal and ceramic brackets than in the control group.

A new oxidation based technique for artifact free TEM specimen preparation of nuclear graphite

NASA Astrophysics Data System (ADS)

Johns, Steve; Shin, Wontak; Kane, Joshua J.; Windes, William E.; Ubic, Rick; Karthik, Chinnathambi

2018-07-01

Graphite is a key component in designs of current and future nuclear reactors whose in-service lifetimes are dependent upon the mechanical performance of the graphite. Irradiation damage from fast neutrons creates lattice defects which have a dynamic effect on the microstructure and mechanical properties of graphite. Transmission electron microscopy (TEM) can offer real-time monitoring of the dynamic atomic-level response of graphite subjected to irradiation; however, conventional TEM specimen-preparation techniques, such as argon ion milling itself, damage the graphite specimen and introduce lattice defects. It is impossible to distinguish these defects from the ones created by electron or neutron irradiation. To ensure that TEM specimens are artifact-free, a new oxidation-based technique has been developed. Bulk nuclear grades of graphite (IG-110 and NBG-18) and highly oriented pyrolytic graphite (HOPG) were initially mechanically thinned to ∼60 μm. Discs 3 mm in diameter were then oxidized at temperatures between 575 °C and 625 °C in oxidizing gasses using a new jet-polisher-like set-up in order to achieve optimal oxidation conditions to create self-supporting electron-transparent TEM specimens. The quality of these oxidized specimens were established using optical and electron microscopy. Samples oxidized at 575 °C exhibited large areas of electron transparency and the corresponding lattice imaging showed no apparent damage to the graphite lattice.

A new oxidation based technique for artifact free TEM specimen preparation of nuclear graphite

DOE Office of Scientific and Technical Information (OSTI.GOV)

Johns, Steve; Shin, Wontak; Kane, Joshua J.

Graphite is a key component in designs of current and future nuclear reactors whose in-service lifetimes are dependent upon the mechanical performance of the graphite. Irradiation damage from fast neutrons creates lattice defects which have a dynamic effect on the microstructure and mechanical properties of graphite. Transmission electron microscopy (TEM) can offer real-time monitoring of the dynamic atomic-level response of graphite subjected to irradiation; however, conventional TEM specimen-preparation techniques, such as argon ion milling itself, damage the graphite specimen and introduce lattice defects. It is impossible to distinguish these defects from the ones created by electron or neutron irradiation. Thus,tomore » ensure that TEM specimens are artifact-free, a new oxidation-based technique has been developed. Bulk nuclear grades of graphite (IG-110 and NBG-18) and highly oriented pyrolytic graphite (HOPG) were initially mechanically thinned to ~60μm. Discs 3mm in diameter were then oxidized at temperatures between 575°C and 625°C in oxidizing gasses using a new jet-polisher-like set-up in order to achieve optimal oxidation conditions to create self-supporting electron-transparent TEM specimens. The quality of these oxidized specimens were established using optical and electron microscopy. Samples oxidized at 575°C exhibited large areas of electron transparency and the corresponding lattice imaging showed no apparent damage to the graphite lattice.« less

A new oxidation based technique for artifact free TEM specimen preparation of nuclear graphite

DOE PAGES

Johns, Steve; Shin, Wontak; Kane, Joshua J.; ...

2018-04-03

Graphite is a key component in designs of current and future nuclear reactors whose in-service lifetimes are dependent upon the mechanical performance of the graphite. Irradiation damage from fast neutrons creates lattice defects which have a dynamic effect on the microstructure and mechanical properties of graphite. Transmission electron microscopy (TEM) can offer real-time monitoring of the dynamic atomic-level response of graphite subjected to irradiation; however, conventional TEM specimen-preparation techniques, such as argon ion milling itself, damage the graphite specimen and introduce lattice defects. It is impossible to distinguish these defects from the ones created by electron or neutron irradiation. Thus,tomore » ensure that TEM specimens are artifact-free, a new oxidation-based technique has been developed. Bulk nuclear grades of graphite (IG-110 and NBG-18) and highly oriented pyrolytic graphite (HOPG) were initially mechanically thinned to ~60μm. Discs 3mm in diameter were then oxidized at temperatures between 575°C and 625°C in oxidizing gasses using a new jet-polisher-like set-up in order to achieve optimal oxidation conditions to create self-supporting electron-transparent TEM specimens. The quality of these oxidized specimens were established using optical and electron microscopy. Samples oxidized at 575°C exhibited large areas of electron transparency and the corresponding lattice imaging showed no apparent damage to the graphite lattice.« less

Evaluation of Ceramic Honeycomb Core Compression Behavior at Room Temperature

NASA Technical Reports Server (NTRS)

Bird, Richard K.; Lapointe, Thomas S.

2013-01-01

Room temperature flatwise compression tests were conducted on two varieties of ceramic honeycomb core specimens that have potential for high-temperature structural applications. One set of specimens was fabricated using strips of a commercially-available thin-gage "ceramic paper" sheet molded into a hexagonal core configuration. The other set was fabricated by machining honeycomb core directly from a commercially available rigid insulation tile material. This paper summarizes the results from these tests.

[Microleakage of various cementing agents for casting ceramics].

PubMed

Weng, Wei-min; Zhang, Xiu-yin; Zhang, Fu-qiang

2009-12-01

To observe and compare the microleakage of different composite resin cement systems for IPS Empress 2 ceramics base. Sixteen healthy non-carious human molars were selected in the study. Class V ceramic inlay was prepared by IPS Empress 2 ceramics. The samples were divided into two groups, eight in each group. RelyX Unicem and Variolink 2 were used for bonding respectively in 2 groups. All specimens were stored in water at 37 degrees centigrade for 24 hours, then the specimens were subjected to 500 thermocycles ranging from 5 degrees centigrade to 55 degrees centigrade. Eight specimens in each group were evaluated by dye penetration. The microleakage was examined with light microscope. Statistical analysis was performed with SPSS11.0 software package. Enamel margins exhibited lower leakage than dentin margins by using two cementing agents for casting ceramics (P<0.05). The depth of dye for Variolink 2 and RelyX Unicem at enamel and dentin was not significantly different (P>0.05). The microleakage of Variolink 2 and RelyX Unicem for IPS Empress 2 ceramics base has similar sealing abilities.

An evaluation of the effects of handpiece speed, abrasive characteristics, and polishing load on the flexural strength of polished ceramics.

PubMed

Ahmad, Rohana; Morgano, Steven M; Wu, Benjamin M; Giordano, Russell A

2005-11-01

Many studies on the strengthening effects of grinding and polishing, as well as heat treatment on ceramics, are not well standardized or use commercially available industrial polishing systems. The reported effectiveness of these strengthening mechanisms on ceramics may not be applicable to clinical dentistry. The purpose of this study was to evaluate the effects of controlled polishing on the flexural strength of dental ceramics by using a custom-made machine that applied standardized loads and speeds that coincided with the mean loads and speeds used by experienced prosthodontists. A total of 140 aluminous dental ceramic bar-shaped specimens (Vitadur Alpha Enamel) measuring 1.5 x 2.0 x 25 mm were fabricated and divided into 12 groups (for most groups, n=10). Specimens were untreated, polished with different polishing systems, polished at different speeds, ground and autoglazed, polished and autoglazed, autoglazed and polished, polished with loose (paste) and bonded abrasives, or overglazed. Simulated clinical polishing was performed on the ceramic specimens by using a customized polishing apparatus that allowed independent control over the relevant polishing parameters (abrasive hardness, applied load, linear speed, rotational velocity, and wheel stiffness). Flexural strength (MPa) was measured with a 4-point bending test, and subjective surface roughness was assessed with scanning electron microscopy. Autoglazing was performed at various stages of the polishing sequence to determine the effects of polishing on surface stresses. Mean values, standard deviations, independent-sample t tests, 1-way and 2-way analyses of variance, Dunnett t tests and Kruskal-Wallis tests were applied to the data (alpha=.05). Under a clinical load of 0.6 N for a coarse polishing wheel, 1.0 N for a medium polishing wheel, and 1.3 N for a fine polishing wheel, a linear speed of 499 mm/min, and a rotational velocity of 10,000 rpm, the use of clinical polishing instruments did not affect the flexural strength of the aluminous ceramics studied (P=.274). At higher rotational velocity (20,000 rpm), specimens polished with the diamond polishing system produced statistically weaker specimens compared with those that had been polished at 10,000 rpm (P=.019). Autoglazing treatment of the diamond-polished specimens did not reverse the strength degradation (P=.125). Conversely, diamond polishing of the autoglazed specimens resulted in significant flexural strength reduction (P=.029). Fine-diamond-bonded abrasive significantly reduced flexural strength (P=.025). Simulated clinical polishing at 10,000 rpm did not appear to substantially strengthen or weaken the ceramic specimens. Polishing at 20,000 rpm reduced flexural strength of the ceramic bars.

The effect of different shades of specific luting agents and IPS empress ceramic thickness on overall color.

PubMed

Terzioğlu, Hakan; Yilmaz, Burak; Yurdukoru, Bengul

2009-10-01

The color stability of both porcelain and luting materials is very important for the esthetics of laminate veneers and all-ceramic crowns. The purpose of this study was to determine the effect of different shades of resin-based luting cement and the thickness of IPS Empress ceramics on the final color of the restorations. Resin-based dual-polymerized composite cement in two different shades (RelyX ARC) and ceramic disks of different thicknesses were selected for the study. Forty specimens (ten each of four different thicknesses: 0.5 mm, 1 mm, 2 mm, and 3 mm) were used for the evaluation. Initial specimen color parameters were determined in a Commission Internationale de l'Eclairage L*a*b* color order system with a colorimeter. Two different shades of the cement were prepared as polymerized layers and applied to one face of the specimens in order. Color changes were calculated between baseline color measurements and measurements after cementation. Color difference data were analyzed statistically. All specimens showed a significant color shift (DE > 3.7) after cementation regardless of the cement shade. However, the differences in the cement shade did not significantly affect the final color of the ceramic specimens for any thickness, and color shifts were not perceivable between the different shades of cement. (Int J Periodontics Restorative Dent 2009;29:499-505.).

Strength degradation and lifetime prediction of dental zirconia ceramics under cyclic normal loading.

PubMed

Li, Wanzhong; Xu, Yingqiang; He, Huiming; Zhao, Haidan; Sun, Jian; Hou, Yue

2015-01-01

Clinical cases show that zirconia restoration could happen fracture by accident under overloading after using a period of time. The purpose of this study is to research mechanical behavior and predict lifetime of dental zirconia ceramics under cyclic normal contact loading with experiments. Cyclic normal contact loading test and three point bending test are carried on specimens made of two brands of dental zirconia ceramic to obtain flexure strength and damage degree after different number of loading cycles. By means of damage mechanics model, damage degree under different number of contact loading cycles are calculated according to flexure strength, and verified by SEM photographs of cross section morphology of zirconia ceramics specimen phenomenologically. Relation curve of damage degree and number of cycles is fitted by polynomial fitting, then the number of loading cycles can be concluded when the specimen is complete damage. Strength degradation of two brands dental zirconia ceramics are researched in vitro, and prediction method of contact fatigue lifetime is established.

Effect of different grinding burs on the physical properties of zirconia

PubMed Central

2016-01-01

PURPOSE Grinding with less stress on 3Y-TZP through proper selection of methods and instruments can lead to a long-term success of prosthesis. The purpose of this study was to compare the phase transformation and physical properties after zirconia surface grinding with 3 different grinding burs. MATERIALS AND METHODS Forty disc-shaped zirconia specimens were fabricated. Each Ten specimens were ground with AllCeramic SuperMax (NTI, Kahla, Germany), Dura-Green DIA (Shofu Inc., Kyoto, Japan), and Dura-Green (Shofu Inc., Kyoto, Japan). Ten specimens were not ground and used as a control group. After the specimen grinding, XRD analysis, surface roughness test, FE-SEM imaging, and biaxial flexural strength test were performed. RESULTS After surface grinding, small amount of monoclinic phase in all experimental groups was observed. The phase change was higher in specimens, which were ground with Dura-Green DIA and AllCeramic SuperMax burs. The roughness of surfaces increased in specimens, which were ground with Dura-Green DIA and AllCeramic SuperMax burs than control groups and ground with Dura-Green. All experimental groups showed lower flexural strength than control group, but there was no statistically significant difference between control group and ground with Dura-Green DIA and AllCeramic SuperMax burs. The specimens, which were ground with Dura- Green showed the lowest strength. CONCLUSION The use of dedicated zirconia-specific grinding burs such as Dura-Green DIA and AllCeramic SuperMax burs decreases the grinding time and did not significantly affect the flexural strength of zirconia, and therefore, they may be recommended. However, a fine polishing process should be accompanied to reduce the surface roughness after grinding. PMID:27141258

Effect of different grinding burs on the physical properties of zirconia.

PubMed

Lee, Kyung-Rok; Choe, Han-Cheol; Heo, Yu-Ri; Lee, Jang-Jae; Son, Mee-Kyoung

2016-04-01

Grinding with less stress on 3Y-TZP through proper selection of methods and instruments can lead to a long-term success of prosthesis. The purpose of this study was to compare the phase transformation and physical properties after zirconia surface grinding with 3 different grinding burs. Forty disc-shaped zirconia specimens were fabricated. Each Ten specimens were ground with AllCeramic SuperMax (NTI, Kahla, Germany), Dura-Green DIA (Shofu Inc., Kyoto, Japan), and Dura-Green (Shofu Inc., Kyoto, Japan). Ten specimens were not ground and used as a control group. After the specimen grinding, XRD analysis, surface roughness test, FE-SEM imaging, and biaxial flexural strength test were performed. After surface grinding, small amount of monoclinic phase in all experimental groups was observed. The phase change was higher in specimens, which were ground with Dura-Green DIA and AllCeramic SuperMax burs. The roughness of surfaces increased in specimens, which were ground with Dura-Green DIA and AllCeramic SuperMax burs than control groups and ground with Dura-Green. All experimental groups showed lower flexural strength than control group, but there was no statistically significant difference between control group and ground with Dura-Green DIA and AllCeramic SuperMax burs. The specimens, which were ground with Dura- Green showed the lowest strength. The use of dedicated zirconia-specific grinding burs such as Dura-Green DIA and AllCeramic SuperMax burs decreases the grinding time and did not significantly affect the flexural strength of zirconia, and therefore, they may be recommended. However, a fine polishing process should be accompanied to reduce the surface roughness after grinding.

Life prediction methodology for ceramic components of advanced heat engines. Phase 1: Volume 2, Appendices

DOE Office of Scientific and Technical Information (OSTI.GOV)

NONE

1995-03-01

This volume presents the following appendices: ceramic test specimen drawings and schematics, mixed-mode and biaxial stress fracture of structural ceramics for advanced vehicular heat engines (U. Utah), mode I/mode II fracture toughness and tension/torsion fracture strength of NT154 Si nitride (Brown U.), summary of strength test results and fractography, fractography photographs, derivations of statistical models, Weibull strength plots for fast fracture test specimens, and size functions.

Light transmittance and surface roughness of a feldspathic ceramic CAD-CAM material as a function of different surface treatments.

PubMed

Ural, Çağrı; Duran, İbrahim; Evmek, Betül; Kavut, İdris; Cengiz, Seda; Yuzbasioglu, Emir

2016-07-15

The aim of the present study was to determine the effect of different surface treatments on light transmission of aesthetic feldspathic ceramics used in CAD-CAM chairside restorations. Forty eight feldspatic ceramic test specimens were prepared from prefabricated CAD-CAM blocks by using a slow speed diamond saw. Test specimens were prepared and divided into 4 groups (n = 12). In the control group, no surface treatments were applied on the feldspathic ceramic surfaces. In the hydrofluoric acid group, the bonding surfaces of feldspathic ceramics were etched with 9.5 % hydrofluoric acid. In the sandblasting group the feldspathic ceramic surfaces were air-abraded with 30-μm alumium oxide (Al2O3) particles and Er:YAG laser was used to irradiate the ceramic surfaces. The incident light power given by the LED device and the transmitted light power through each ceramic sample was registered using a digital LED radiometer device. Each polymerization light had a light guide with 8-mm-diameter tips. Light transmission of feldspathic ceramic samples was determined by placing it on the radiometer and irradiating the specimen for 10 s at the highest setting for each light polymerization. All specimens were coated with gold using a sputter coater and examined under a field emission scanning electron microscope. Surface roughness measurement each group were evaluated with 3D optical surface and tactile profilometers. One-way ANOVA test results revealed that both surface conditioning method significantly affect the light transmittance (F:412.437; p < 0.001) and the surface roughness values (F:16.386; p < 0.001). Al2O3 and Er-YAG laser application reduced the light transmission significantly (p < 0.05). The laser and Al2O3 applications reduced the light transmission of 1.5 mm thickness feldspathic ceramic material below the value of 400 mW/cm(2) which is critical limit for safe polymerization.

Effect of colouring green stage zirconia on the adhesion of veneering ceramics with different thermal expansion coefficients

PubMed Central

Aktas, Guliz; Sahin, Erdal; Vallittu, Pekka; Özcan, Mutlu; Lassila, Lippo

2013-01-01

This study evaluated the adhesion of zirconia core ceramics with their corresponding veneering ceramics, having different thermal expansion coefficients (TECs), when zirconia ceramics were coloured at green stage. Zirconia blocks (N=240; 6 mm×7 mm×7 mm) were manufactured from two materials namely, ICE Zirconia (Group 1) and Prettau Zirconia (Group 2). In their green stage, they were randomly divided into two groups. Half of the specimens were coloured with colouring liquid (shade A2). Three different veneering ceramics with different TEC (ICE Ceramic, GC Initial Zr and IPS e.max Ceram) were fired on both coloured and non-coloured zirconia cores. Specimens of high noble alloys (Esteticor Plus) veneered with ceramic (VM 13) (n=16) acted as the control group. Core–veneer interface of the specimens were subjected to shear force in the Universal Testing Machine (0.5 mm⋅min−1). Neither the zirconia core material (P=0.318) nor colouring (P=0.188) significantly affected the results (three-way analysis of variance, Tukey's test). But the results were significantly affected by the veneering ceramic (P=0.000). Control group exhibited significantly higher mean bond strength values (45.7±8) MPa than all other tested groups ((27.1±4.1)−(39.7±4.7) and (27.4±5.6)−(35.9±4.7) MPa with and without colouring, respectively) (P<0.001). While in zirconia–veneer test groups, predominantly mixed type of failures were observed with the veneering ceramic covering <1/3 of the substrate surface, in the metal–ceramic group, veneering ceramic was left adhered >1/3 of the metal surface. Colouring zirconia did not impair adhesion of veneering ceramic, but veneering ceramic had a significant influence on the core–veneer adhesion. Metal–ceramic adhesion was more reliable than all zirconia–veneer ceramics tested. PMID:24158142

Effect of colouring green stage zirconia on the adhesion of veneering ceramics with different thermal expansion coefficients.

PubMed

Aktas, Guliz; Sahin, Erdal; Vallittu, Pekka; Ozcan, Mutlu; Lassila, Lippo

2013-12-01

This study evaluated the adhesion of zirconia core ceramics with their corresponding veneering ceramics, having different thermal expansion coefficients (TECs), when zirconia ceramics were coloured at green stage. Zirconia blocks (N=240; 6 mm×7 mm×7 mm) were manufactured from two materials namely, ICE Zirconia (Group 1) and Prettau Zirconia (Group 2). In their green stage, they were randomly divided into two groups. Half of the specimens were coloured with colouring liquid (shade A2). Three different veneering ceramics with different TEC (ICE Ceramic, GC Initial Zr and IPS e.max Ceram) were fired on both coloured and non-coloured zirconia cores. Specimens of high noble alloys (Esteticor Plus) veneered with ceramic (VM 13) (n=16) acted as the control group. Core-veneer interface of the specimens were subjected to shear force in the Universal Testing Machine (0.5 mm⋅min(-1)). Neither the zirconia core material (P=0.318) nor colouring (P=0.188) significantly affected the results (three-way analysis of variance, Tukey's test). But the results were significantly affected by the veneering ceramic (P=0.000). Control group exhibited significantly higher mean bond strength values (45.7±8) MPa than all other tested groups ((27.1±4.1)-(39.7±4.7) and (27.4±5.6)-(35.9±4.7) MPa with and without colouring, respectively) (P<0.001). While in zirconia-veneer test groups, predominantly mixed type of failures were observed with the veneering ceramic covering <1/3 of the substrate surface, in the metal-ceramic group, veneering ceramic was left adhered >1/3 of the metal surface. Colouring zirconia did not impair adhesion of veneering ceramic, but veneering ceramic had a significant influence on the core-veneer adhesion. Metal-ceramic adhesion was more reliable than all zirconia-veneer ceramics tested.

Influence of glass particle size of resin cements on bonding to glass ceramic: SEM and bond strength evaluation.

PubMed

Valentini, Fernanda; Moraes, Rafael R; Pereira-Cenci, Tatiana; Boscato, Noéli

2014-05-01

This study investigated the effect of the filler particle size (micron or submicron) of experimental resin cements on the microtensile bond strength to a glass-ceramic pretreated with hydrofluoric acid (HFA) etching or alumina airborne-particle abrasion (AA). Cements were obtained from a Bis-GMA/TEGDMA mixture filled with 60 mass% micron-sized (1 ± 0.2 µm) or submicron-sized (180 ± 30 µm) Ba-Si-Al glass particles. Ceramic blocks (PM9; VITA) were treated with 10% HFA for 60 s or AA for 15 s. Silane and adhesive were applied. Ceramic blocks were bonded to resin composite blocks (Z250; 3M ESPE) using one of the cements. Bonded specimens were sectioned into beams (n = 20/group) and subjected to microtensile bond strength tests. Data were analyzed using ANOVA and Student-Newman-Keuls' tests (5%). Failure modes were classified under magnification. Morphologies of the treated ceramic surfaces and bonded interfaces were evaluated by scanning electron microscopy. The HFA-submicron group had lower bond strengths than the other groups. All AA-submicron specimens debonded prematurely. Mixed failures were predominant for HFA groups, whereas interfacial failures predominated for AA groups. SEM revealed a honeycomb-like aspect in the HFA-treated ceramic, whereas the AA-treated groups showed an irregular retentive pattern. Continuity of cement infiltration along the bonded interface was more uniform for HFA-treated compared to AA-treated specimens. Cracks toward the bulk of the ceramic were observed in AA-treated specimens. Particle size significantly influenced the ceramic bond strength, whereas surface treatment had a minor effect. Copyright © 2014 Wiley Periodicals, Inc.

Artifacts introduced by ion milling in Al-Li-Cu alloys.

PubMed

Singh, A K; Imam, M A; Sadananda, K

1988-04-01

Ion milling is commonly used to prepare specimens for observation under transmission electron microscope (TEM). This technique sometimes introduces artifacts in specimens contributing to misleading interpretation of TEM results as observed in the present investigation of Al-Li-Cu alloys. This type of alloy, in general, contains several kinds of precipitates, namely delta', T1, and theta'. It is found that ion milling even for a short time produces drastic changes in the precipitate characteristics as compared to standard electropolishing methods of specimen preparation for TEM. Careful analysis of selected area diffraction patterns and micrographs shows that after ion milling delta' precipitates are very irregular, whereas other precipitates coarsen and they are surrounded by misfit dislocations. In situ hot-stage TEM experiments were performed to relate the microstructure to that observed in the ion-milled specimen. Results and causes of ion milling effects on the microstructure are discussed in relation to standard electropolishing techniques and in situ hot-stage experiment.

Fracture strength of all-ceramic lithium disilicate and porcelain-fused-to-metal bridges for molar replacement after dynamic loading.

PubMed

Chitmongkolsuk, Somsak; Heydecke, Guido; Stappert, Christian; Strub, Joerg R

2002-03-01

The replacement of missing posterior teeth using all-ceramic bridges remains a challenge. This study compares the fracture resistance of all-ceramic 3-unit bridges for the replacement of first molars to conventional porcelain-fused-to-metal bridges. Human premolars and molars were used to create two test groups and one control group of 16 specimens each. To simulate clinical parameters, the specimens were exposed to cyclic fatigue loading in an artificial mouth with simultaneous thermocycling. All samples were thereafter exposed to fracture strength testing. Porcelain-fused-to-metal bridges showed significantly higher fracture strengths than all-ceramic bridges. However, the fracture strength of the all-ceramic bridges was higher than peak physiological chewing forces.

Apparatus for tensile testing plate-type ceramic specimens

DOEpatents

Liu, Kenneth C.

1993-01-01

Apparatus for tensile testing plate-type ceramic specimens having dogbone- or T-shaped end sections without introducing bending stresses in the specimens during the application of a dynamic tensile loading on the specimens is described. A pair of elongated pull rods disposed in a side-by-side relationship are used to grip the shoulders on each T-shaped end section. The pull rods are pivotally attached to a piston-displaceable, disk-shaped member so as to be longitudinally movable with respect to one another effecting the self-alignment thereof with the shoulders on the T-shaped end sections of the specimen to compensate for shoulders being located in different longitudinal positions.

Thermal compatibility of dental ceramic systems using cylindrical and spherical geometries.

PubMed

DeHoff, Paul H; Barrett, Allyson A; Lee, Robert B; Anusavice, Kenneth J

2008-06-01

To test the hypothesis that bilayer ceramic cylinders and spheres can provide valid confirmation of thermal incompatibility stresses predicted by finite element analyses. A commercial core ceramic and an experimental core ceramic were used to fabricate open-ended cylinders and core ceramic spheres. The core cylinders and spheres were veneered with one of four commercial dental ceramics representing four thermally compatible groups and four thermally incompatible groups. Axisymmetric thermal and viscoelastic elements in the ANSYS finite element program were used to calculate temperatures and stresses for each geometry and ceramic combination. This process required a transient heat transfer analysis for each combination to determine input temperatures for the structural model. After fabrication, each specimen was examined visually using fiberoptic transillumination for evidence of cracking. There were 100% failures of the thermally incompatible cylinders while none of the thermally compatible combinations failed. Among the spheres, 100% of the thermally incompatible systems failed, 16% of one of the thermally compatible systems failed, and none of the remaining compatible combinations failed. The calculated stress values were in general agreement with the experimental observations, i.e., low residual stresses for the specimens that did not fail and high residual stresses for the specimens that did fail. Simple screening geometries can be used to identify highly incompatible ceramic combinations, but they do not identify marginally incompatible systems.

Thermal compatibility of dental ceramic systems using cylindrical and spherical geometries

PubMed Central

DeHoff, Paul H.; Barrett, Allyson A.; Lee, Robert B.; Anusavice, Kenneth J.

2009-01-01

Objective To test the hypothesis that bilayer ceramic cylinders and spheres can provide valid confirmation of thermal incompatibility stresses predicted by finite element analyses. Methods A commercial core ceramic and an experimental core ceramic were used to fabricate open-ended cylinders and core ceramic spheres. The core cylinders and spheres were veneered with one of four commercial dental ceramics representing four thermally compatible groups and four thermally incompatible groups. Axisymmetric thermal and viscoelastic elements in the ANSYS finite element program were used to calculate temperatures and stresses for each geometry and ceramic combination. This process required a transient heat transfer analysis for each combination to determine input temperatures for the structural model. Results After fabrication, each specimen was examined visually using fiberoptic transillumination for evidence of cracking. There were 100% failures of the thermally incompatible cylinders while none of the thermally compatible combinations failed. Among the spheres, 100% of the thermally incompatible systems failed, 16% of one of the thermally compatible systems failed, and none of the remaining compatible combinations failed. The calculated stress values were in general agreement with the experimental observations, i.e., low residual stresses for the specimens that did not fail and high residual stresses for the specimens that did fail. Significance Simple screening geometries can be used to identify highly incompatible ceramic combinations, but they do not identify marginally incompatible systems. PMID:17949805

Rolling contact fatigue strengths of shot-peened and crack-healed ceramics

NASA Astrophysics Data System (ADS)

Takahashi, K.; Oki, T.

2018-06-01

The effects of shot-peening (SP) and crack-healing on the rolling contact fatigue (RCF) strengths of Al2O3/SiC composite ceramics were investigated. Non-shot-peened, shot- peened, and shot-peened + crack-healed specimens were prepared. SP was performed using ZrO2 beads. The shot-peened + crack-healed specimen was crack-healed after SP. X-ray diffraction clearly showed that SP induced a compressive residual stress up to 300 MPa at the specimen surfaces. Furthermore, the shot-peened + crack-healed specimen retained a compressive residual stress of 200 MPa. The apparent surface fracture toughness of the shot- peened specimens increased owing to the positive effects of the compressive residual stress. RCF tests were performed using a thrust load-bearing test device. The RCF lives of the shot- peened specimens did not improve compared to that of the non-shot-peened specimen, because the numerous SP-introduced surface cracks could act as crack initiation sites during the RCF tests. However, the RCF life of the shot-peened + crack-healed specimen did improve compared to those of non-shot-peened and shot-peened specimens, implying that combining SP and crack-healing was an effective strategy for improving the RCF lives of Al2O3/SiC composite ceramics.

Effect of various intermediate ceramic layers on the interfacial stability of zirconia core and veneering ceramics.

PubMed

Yoon, Hyung-In; Yeo, In-Sung; Yi, Yang-Jin; Kim, Sung-Hun; Lee, Jai-Bong; Han, Jung-Suk

2015-01-01

The purposes of this study were to evaluate the effects of intermediate ceramics on the adhesion between the zirconia core and veneer ceramics. The polished surfaces of fully sintered Y-TZP blocks received three different treatments: (1) connector (C), (2) liner (L) or (3) wash layer (W). All the treated zirconia blocks were veneered with either (a) fluorapatite glass-ceramic (E) or (b) feldspathic porcelain (V) and divided into four groups (CE, CV, LE and WV). For the control group, the testing surfaces of metal blocks were veneered with feldspathic porcelain (VM). A half of the samples in each group (n = 21) were exposed to thermocycling, while the other half of the specimens were stored at room temperature under dry conditions. All specimens were subjected to the shear test and the failed surfaces were microscopically examined. The elemental distribution at the zirconia core/veneer interface was analyzed. The specimens in Groups CE and CV exhibited significantly greater mean bond strength values than those in Groups LE and WV, respectively (p < 0.05). However, the mean bond strengths significantly decreased in the connector groups (CE and CV) after thermal cycling (p < 0.05). The elemental analysis suggested diffusion of ceramic substances into the zirconia surface. A glass-ceramic based connector is significantly more favorable to core/veneer adhesion than the other intermediate ceramics evaluated in the study. However, thermal cycling affected the bond strength at the core/veneer interface differently according to the intermediate ceramics.

[Influence of adhesion on the color of glass infiltrated alumina ceramic restorations].

PubMed

Jiang, Li; Yang, Liu; Xu, Qiang; Guan, Hong-Yu; Wan, Qian-Bing

2006-10-01

To investigate the effects of luting agent on the final color of glass infiltrated alumina ceramic restorations. 12 plate-shaped specimens with 12.5 mm in diameter and 0.5 mm thickness were fabricated from GI-II (color IG2). Vitadur alpha veneering porcelain (color A2) with 1.0 mm thickness was fired to GI- II glass/alumina composite. 12 plate-shaped background specimens simulating the metal alloy post-and-core 12.5 mm in diameter and 2 mm thickness were also made from Ni-Cr alloy. All-ceramic specimens were luted to the metal alloy by Zinc Phosphate cement, glass ionomer cement and composite resin. The color shifts of the specimens were measured by colorimeter. Luting agents had effect on the final color of restorations. The influence of composite resin was least, followed by glass ionomer cement and Zinc Phosphate cement. The color difference between with and without Zinc Phosphate cement could be identified by the eye. To reduce the effect of luting agents, composite resin is recommended to all-ceramic restorations' adhesion.

Manifestation of Crystal Lattice Distortions in the IR Reflection Spectra of Abrasion-Treated ZnSe Ceramics

NASA Astrophysics Data System (ADS)

Sitnikova, V. E.; Dunaev, A. A.; Mamalimov, R. I.; Pakhomov, P. M.; Khizhnyak, S. D.; Chmel, A. E.

2017-07-01

The Fourier IR reflection spectra of ZnSe ceramics prepared by hot pressing (HP), physical vapor deposition (PVD), and PVD combined with hot isostatic pressing (HIP) are presented. The optical constants of polished and dry-ground specimens were used for comparison. The grinding treatment simulated the erosion of the outer surface of optical elements made of zinc selenide under the influence of solid dust particles and deposits. In the polished specimens residual stresses showed up in the IR reflection spectra of the ZnSePVD and ZnSeHIP ceramics, which had well-defined orientation of grains, but were not present in the spectra of the ZnSeHIP ceramics as a result of mutual compensation of the stresses in the randomly oriented grains of the material. The stresses, which appeared as a shift of the absorption bands calculated by the Kramers-Kronig method, increased significantly after abrasive treatment of the specimens. For all the treated ceramics the intensity of the absorption bands resulting from the anharmonicity of the vibrations in the distorted crystal lattice increased by several times. The last effect also depends on the production prehistory of the ceramics.

Effect of surface acid etching on the biaxial flexural strength of two hot-pressed glass ceramics.

PubMed

Hooshmand, Tabassom; Parvizi, Shaghayegh; Keshvad, Alireza

2008-07-01

The purpose of this study was to assess the effect of surface acid etching on the biaxial flexural strength of two hot-pressed glass ceramics reinforced by leucite or lithium disilicate crystals. Forty glass ceramic disks (14-mm diameter, 2-mm thick) consisting of 20 leucite-based ceramic disks (IPS Empress) and 20 lithia disilicate-based ceramic (IPS Empress 2) were produced by hot-pressing technique. All specimens were polished and then cleaned ultrasonically in distilled water. Ten specimens of each ceramic group were then etched with 9% hydrofluoric (HF) acid gel for 2 minutes and cleaned ultrasonically again. The biaxial flexural strength was measured by the piston-on-three-ball test in a universal testing machine. Data based on ten specimens in each group were analyzed by two-way ANOVA (alpha= 0.05). Microstructure of ceramic surfaces before and after acid etching was also examined by a scanning electron microscope. The mean biaxial flexural strength values for each group tested were (in MPa): nonetched IPS Empress = 118.6 +/- 25.5; etched IPS Empress = 102.9 +/- 15.4; nonetched IPS Empress 2 = 283.0 +/- 48.5; and etched IPS Empress 2 = 250.6 +/- 34.6. The results showed that the etching process reduced the biaxial flexural strengths significantly for both ceramic types (p= 0.025). No significant interaction between the ceramic type and etching process was found (p= 0.407). From the results, it was concluded that surface HF acid etching could have a weakening effect on hot-pressed leucite or lithia disilicate-based glass ceramic systems.

Impact of Gastric Acid Induced Surface Changes on Mechanical Behavior and Optical Characteristics of Dental Ceramics.

PubMed

Kulkarni, Aditi; Rothrock, James; Thompson, Jeffery

2018-01-14

To test the impact of exposure to artificial gastric acid combined with toothbrush abrasion on the properties of dental ceramics. Earlier research has indicated that immersion in artificial gastric acid has caused increased surface roughness of dental ceramics; however, the combined effects of acid immersion and toothbrush abrasion and the impact of increased surface roughness on mechanical strength and optical properties have not been studied. Three commercially available ceramics were chosen for this study: feldspathic porcelain, lithium disilicate glass-ceramic, and monolithic zirconium oxide. The specimens (10 × 1 mm discs) were cut, thermally treated as required, and polished. Each material was divided into four groups (n = 8 per group): control (no exposure), acid only, brush only, acid + brush. The specimens were immersed in artificial gastric acid (50 ml of 0.2% [w/v] sodium chloride in 0.7% [v/v] hydrochloric acid mixed with 0.16 g of pepsin powder, pH = 2) for 2 minutes and rinsed with deionized water for 2 minutes. The procedure was repeated 6 times/day × 9 days, and specimens were stored in deionized water at 37°C. Toothbrush abrasion was performed using an ISO/ADA design brushing machine for 100 cycles/day × 9 days. The acid + brush group received both treatments. Specimens were examined under SEM and an optical microscope for morphological changes. Color and translucency were measured using spectrophotometer CIELAB coordinates (L*, a*, b*). Surface gloss was measured using a gloss meter. Surface roughness was measured using a stylus profilometer. Biaxial flexural strength was measured using a mechanical testing machine. The data were analyzed by one-way ANOVA followed by Tukey's HSD post hoc test (p < 0.05). Statistically significant changes were found for color, gloss, and surface roughness for porcelain and e.max specimens. No statistically significant changes were found for any properties of zirconia specimens. The acid treatment affected the surface roughness, color, and gloss of porcelain and e.max ceramics. The changes in translucency and mechanical strength for all materials were not statistically significant. Zirconia ceramic showed resistance to all treatments. © 2018 by the American College of Prosthodontists.

Method and apparatus for radio frequency ceramic sintering

DOEpatents

Hoffman, Daniel J.; Kimrey, Jr., Harold D.

1993-01-01

Radio frequency energy is used to sinter ceramic materials. A coaxial waveguide resonator produces a TEM mode wave which generates a high field capacitive region in which a sample of the ceramic material is located. Frequency of the power source is kept in the range of radio frequency, and preferably between 60-80 MHz. An alternative embodiment provides a tunable radio frequency circuit which includes a series input capacitor and a parallel capacitor, with the sintered ceramic connected by an inductive lead. This arrangement permits matching of impedance over a wide range of dielectric constants, ceramic volumes, and loss tangents.

Method and apparatus for radio frequency ceramic sintering

DOEpatents

Hoffman, D.J.; Kimrey, H.D. Jr.

1993-11-30

Radio frequency energy is used to sinter ceramic materials. A coaxial waveguide resonator produces a TEM mode wave which generates a high field capacitive region in which a sample of the ceramic material is located. Frequency of the power source is kept in the range of radio frequency, and preferably between 60-80 MHz. An alternative embodiment provides a tunable radio frequency circuit which includes a series input capacitor and a parallel capacitor, with the sintered ceramic connected by an inductive lead. This arrangement permits matching of impedance over a wide range of dielectric constants, ceramic volumes, and loss tangents. 6 figures.

Effect of soldering on the metal-ceramic bond strength of an Ni-Cr base alloy.

PubMed

Nikellis, Ioannis; Levi, Anna; Zinelis, Spiros

2005-11-01

Although soldering is a common laboratory procedure, the use of soldering alloys may adversely affect metal-ceramic bond strength and potentially decrease the longevity of metal-ceramic restorations. The purpose of this study was to investigate the effect of soldering on metal-ceramic bond strength of a representative Ni-Cr base metal alloy. Twenty-eight rectangular (25 x 3 x 0.5 mm) Ni-based alloy (Wiron 99) specimens were equally divided into soldering (S) and reference (R) groups. Soldering group specimens were covered with a 0.1-mm layer of the appropriate solder (Wiron-Lot) and reduced by 0.1 mm on the opposite side. Five specimens of each group were used for the measurement of surface roughness parameter (R(z)) and hardness, and 3 were used for measurement of the modulus of elasticity. Six specimens of each group were covered with porcelain (Ceramco 3) and subjected to a 3-point bending test for evaluation of the metal-ceramic bond strength according to the ISO 9693 specification. The data from surface roughness, hardness, modulus of elasticity, and metal-ceramic bond strength were analyzed statistically, using independent t tests (alpha=.05). Statistical analysis of the R(z) surface roughness parameter (S: 3.4 +/- 0.3 mum; R: 3.7 +/- 0.7 microm; P=.07) and bond strength (S: 46 +/- 3 MPa; R: 40 +/- 5 MPa; P=.057) failed to reveal any significant difference between the 2 groups. The specimens of the soldering group demonstrated significantly lower values both in hardness (S: 128 +/- 11 VHN; R: 217 +/- 4 VHN; P<.001) and in modulus of elasticity (S: 135 +/- 4 GPa; R: 183 +/- 6 GPa; P=.035) than the reference group. Under the conditions of the present study, the addition of solder to the base metal alloy did not affect the metal-ceramic bond strength.

Biaxial flexural strength of Turkom-Cera core compared to two other all-ceramic systems.

PubMed

Al-Makramani, Bandar Mohammed Abdullah; Razak, Abdul Aziz Abdul; Abu-Hassan, Mohamed Ibrahim

2010-12-01

Advances in all-ceramic systems have established predictable means of providing metal-free aesthetic and biocompatible materials. These materials must have sufficient strength to be a practical treatment alternative for the fabrication of crowns and fixed partial dentures. The aim of this study was to compare the biaxial flexural strength of three core ceramic materials. Three groups of 10 disc-shaped specimens (16 mm diameter x 1.2 mm thickness - in accordance with ISO-6872, 1995) were made from the following ceramic materials: Turkom-Cera Fused Alumina [(Turkom-Ceramic (M) Sdn Bhd, Puchong, Selangor, Malaysia)], In-Ceram (Vita Zahnfabrik, Bad Säckingen, Baden-Württemberg, Germany) and Vitadur-N (Vita Zahnfabrik, Bad Säckingen, Baden-Württemberg, Germany), which were sintered according to the manufacturer's recommendations. The specimens were subjected to biaxial flexural strength test in an universal testing machine at a crosshead speed of 0.5 mm/min. The definitive fracture load was recorded for each specimen and the biaxial flexural strength was calculated from an equation in accordance with ISO-6872. The mean biaxial flexural strength values were: Turkom-Cera: 506.8 ± 87.01 MPa, In-Ceram: 347.4 ± 28.83 MPa and Vitadur-N: 128.7 ± 12.72 MPa. The results were analyzed by the Levene's test and Dunnett's T3 post-hoc test (SPSS software V11.5.0 for Windows, SPSS, Chicago, IL, USA ) at a preset significance level of 5% because of unequal group variances (P<0.001). There was statistically significant difference between the three core ceramics (P<0.05). Turkom-Cera showed the highest biaxial flexural strength, followed by In-Ceram and Vitadur-N. Turkom-Cera core had significantly higher flexural strength than In-Ceram and Vitadur-N ceramic core materials.

Internal coating of zirconia restoration with silica-based ceramic improves bonding of resin cement to dental zirconia ceramic.

PubMed

Kitayama, Shuzo; Nikaido, Toru; Ikeda, Masaomi; Alireza, Sadr; Miura, Hiroyuki; Tagami, Junji

2010-01-01

Resin bonding to zirconia ceramic cannot be established by standard methods that are utilized for conventional silica-based dental ceramics. This study was aimed to examine the tensile bond strength of resin cement to zirconia ceramic using a new laboratory technique. Sixty-four zirconia ceramic specimens were air-abraded using Al2O3 particles and divided into two groups; the control group with no pretreatment (Control), and the group pretreated using the internal coating technique (INT), in which the surface of the zirconia specimens were thinly coated by fusing silica-based ceramic and air-abraded in the same manner. The specimens in each group were further divided into two subgroups according to the silane coupling agents applied; a mixture of dentin primer/silane coupling agent (Clearfil SE Bond Primer/Porcelain Bond Activator) or a newly developed single-component silane coupling agent (Clearfil Ceramic Primer). After bonding with dual-cured resin cement (Panavia F 2.0), they were stored in water for 24 h and half of them were additionally subjected to thermal cycling. The tensile bond strengths were tested using a universal testing machine. ANOVAs revealed significant influence of ceramic surface pretreatment (p<0.001), silane coupling agent (p<0.001) and thermal cycling (p<0.001); the INT coating technique significantly increased the bond strengths of resin cement to zirconia ceramic, whereas thermal cycling significantly decreased the bond strengths. The use of a single-component silane coupling agent demonstrated significantly higher bond strengths than that of a mixture of dentin primer/silane coupling agent. The internal coating of zirconia dental restorations with silica-based ceramic followed by silanization may be indicated in order to achieve better bonding for the clinical success.

New and unconventional approaches for advancing resolution in biological transmission electron microscopy by improving macromolecular specimen preparation and preservation.

PubMed

Massover, William H

2011-02-01

Resolution in transmission electron microscopy (TEM) now is limited by the properties of specimens, rather than by those of instrumentation. The long-standing difficulties in obtaining truly high-resolution structure from biological macromolecules with TEM demand the development, testing, and application of new ideas and unconventional approaches. This review concisely describes some new concepts and innovative methodologies for TEM that deal with unsolved problems in the preparation and preservation of macromolecular specimens. The selected topics include use of better support films, a more protective multi-component matrix surrounding specimens for cryo-TEM and negative staining, and, several quite different changes in microscopy and micrography that should decrease the effects of electron radiation damage; all these practical approaches are non-traditional, but have promise to advance resolution for specimens of biological macromolecules beyond its present level of 3-10 Å (0.3-1.0 nm). The result of achieving truly high resolution will be a fulfillment of the still unrealized potential of transmission electron microscopy for directly revealing the structure of biological macromolecules down to the atomic level. Published by Elsevier Ltd.

Tensile bond strength of metal bracket bonding to glazed ceramic surfaces with different surface conditionings.

PubMed

Akhoundi, Ms Ahmad; Kamel, M Rahmati; Hashemi, Sh Mahmood; Imani, M

2011-01-01

The objective of this study was to compare the tensile bond strength of metal brackets bonding to glazed ceramic surfaces using three various surface treatments. Forty two glazed ceramic disks were assigned to three groups. In the first and second groups the specimens were etched with 9.5% hydrofluoric acid (HFA). Subsequently in first group, ceramic primer and adhesive were applied, but in second group a bonding agent alone was used. In third group, specimens were treated with 35% phosphoric acid followed by ceramic primer and adhesive application. Brackets were bonded with light cure composites. The specimens were stored in distilled water in the room temperature for 24 hours and thermocycled 500 times between 5°C and 55°C. The universal testing machine was used to test the tensile bond strength and the adhesive remenant index scores between three groups was evaluated. The data were subjected to one-way ANOVA, Tukey and Kruskal-Wallis tests respectively. The tensile bond strength was 3.69±0.52 MPa forfirst group, 2.69±0.91 MPa for second group and 3.60±0.41 MPa for third group. Group II specimens showed tensile strength values significantly different from other groups (P<0.01). In spite of limitations in laboratory studies it may be concluded that in application of Scotch bond multipurpose plus adhesive, phosphoric acid can be used instead of HFA for bonding brackets to the glazed ceramic restorations with enough tensile bond strength.

Effect of Acidic Agents on Surface Roughness of Dental Ceramics

PubMed Central

Kukiattrakoon, Boonlert; Hengtrakool, Chanothai; Kedjarune-Leggat, Ureporn

2011-01-01

Background: An increase in surface roughness of ceramics may decrease strength and affect the clinical success of ceramic restorations. However, little is known about the effect of acidic agents on ceramic restorations. The aim of this study was to evaluate the surface roughness of dental ceramics after being immersed in acidic agents. Methods: Eighty-three ceramic disk specimens (12.0 mm in diameter and 2.0 mm in thickness) were made from four types of ceramics (VMK 95, Vitadur Alpha, IPS Empress Esthetic, and IPS e.max Ceram). Baseline data of surface roughness were recorded by profilometer. The specimens were then immersed in acidic agents (citrate buffer solution, pineapple juice and green mango juice) and deionized water (control) at 37°C for 168 hours. One group was immersed in 4% acetic acid at 80°C for 168 hours. After immersion, surface roughness was evaluated by a profilometer at intervals of 24, 96, and 168 hours. Surface characteristics of specimens were studied using scanning electron microscopy (SEM). Data were analyzed using two-way repeated ANOVA and Tukey's multiple comparisons (α = 0.05). Results: For all studied ceramics, all surface roughness parameters were significantly increased after 168 hours immersion in all acidic agents (P < 0.05). After 168 hours in 4% acetic acid, there were significant differences for all roughness parameters from other acidic agents of all evaluated ceramics. Among all studied ceramics, Vitadur Alpha showed significantly the greatest values of all surface roughness parameters after immersion in 4% acetic acid (P < 0.001). SEM photomicrographs also presented surface destruction of ceramics in varying degrees. Conclusion: Acidic agents used in this study negatively affected the surface of ceramic materials. This should be considered when restoring the eroded tooth with ceramic restorations in patients who have a high risk of erosive conditions. PMID:22132009

Wear of ceramic and antagonist--a systematic evaluation of influencing factors in vitro.

PubMed

Heintze, S D; Cavalleri, A; Forjanic, M; Zellweger, G; Rousson, V

2008-04-01

(1) To systematically review the existing literature on in vitro assessments of antagonist wear of ceramic materials; (2) To systematically evaluate possible influencing factors on material and antagonist wear of ceramic specimens. The database MEDLINE was searched with the terms "enamel," "wear" and "antagonist." The selected studies were analyzed with regard to wear parameters, type of antagonist and outcome. In the laboratory study, three ceramic materials were selected with different compositions and physical properties: IPS d.SIGN low-fusing metal ceramic, IPS Empress leucite ceramic, e.max Press lithium disilicate ceramic. These materials were subjected to the Ivoclar wear method (Willytec chewing simulator, 120,000cycles, 5kg weight) by systematically modifying the following variables which resulted in 36 tests with 8 specimens in each group: (1) configuration (flat, crown specimen), (2) surface treatment (polish, glaze), (3) type of antagonist (ceramic, two types of enamel stylus). Furthermore, the enamel styluses were cut to measure the enamel thickness and cusp width. Wear of both the material and the antagonist was quantified by scanning plaster replicas of the specimens with a laser scanner (etkon es1) and matching baseline and follow-up data with the Match 3D software (Willytec). The data were log-transformed to stabilize the variance and achieve near normality. To test the influence of specific test parameters, a four-way ANOVA with post hoc tests and Bonferroni correction was applied. The systematic review revealed 20 in vitro studies in which a material and the antagonist wear of the same material was examined. However, the results were inconsistent mainly due to the fact that the test parameters differed widely. Most studies used prepared enamel from extracted molars as the antagonist and flat polished ceramic specimens. The test chamber was filled with water and some sort of sliding movement was integrated in the wear generating process. However, there was a huge variation in relation to the applied force, the used force actuator, the number of cycles, and the frequency of cycles per time as well as the number of specimens. The results of the systematic laboratory tests revealed that the following factors strongly influence the wear: configuration (more material wear of flat versus crown specimens), surface treatment (more antagonist wear of glazed versus polished specimens), the antagonist system (more material wear and less antagonist wear for ceramic stylus versus enamel stylus), and enamel thickness (less wear for thicker enamel). Material wear was not very much different between the materials. However, e.max Press generally caused more antagonist wear than the other two materials, which were quite similar. However, the main influencing factors did not yield consistent results for all the subgroups and there was a huge variability of results within the subgroups especially in those groups that used enamel as antagonist. As far as consistency and correlation with clinical studies is concerned, the set-up that consists of unprepared enamel of molar cusps against glazed crowns seems to be the most appropriate method to evaluate a ceramic material with regard to antagonist wear. However, due to the high variability of results large sample sizes are necessary to differentiate between materials, which calls the whole in vitro approach into question.

In vitro evaluation of marginal adaptation in five ceramic restoration fabricating techniques.

PubMed

Ural, Cağri; Burgaz, Yavuz; Saraç, Duygu

2010-01-01

To compare in vitro the marginal adaptation of crowns manufactured using ceramic restoration fabricating techniques. Fifty standardized master steel dies simulating molars were produced and divided into five groups, each containing 10 specimens. Test specimens were fabricated with CAD/CAM, heat-press, glass-infiltration, and conventional lost-wax techniques according to manufacturer instructions. Marginal adaptation of the test specimens was measured vertically before and after cementation using SEM. Data were statistically analyzed by one-way ANOVA with Tukey HSD tests (a = .05). Marginal adaptation of ceramic crowns was affected by fabrication technique and cementation process (P < .001). The lowest marginal opening values were obtained with Cerec-3 crowns before and after cementation (P < .001). The highest marginal discrepancy values were obtained with PFM crowns before and after cementation. Marginal adaptation values obtained in the compared systems were within clinically acceptable limits. Cementation causes a significant increase in the vertical marginal discrepancies of the test specimens.

Adaptation of the chevron-notch beam fracture toughness method to specimens harvested from diesel particulate filters

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wereszczak, Andrew; Jadaan, Osama; Modugno, Max

In this paper, the apparent fracture toughness of a porous cordierite ceramic was estimated using a large specimen whose geometry was inspired by the ASTM-C1421-standardized chevron-notch beam. In this paper, using the same combination of experiment and analysis used to develop the standardized chevron-notch test for small, monolithic ceramic bend bars, an apparent fracture toughness of 0.6 and 0.9 MPa√m were estimated for an unaged and aged cordierite diesel particulate filter structure, respectively. Finally, the effectiveness and simplicity of this adapted specimen geometry and test method lends itself to the evaluation of (macroscopic) apparent fracture toughness of an entire porous-ceramic,more » diesel particulate filter structure.« less

Adaptation of the chevron-notch beam fracture toughness method to specimens harvested from diesel particulate filters

DOE PAGES

Wereszczak, Andrew; Jadaan, Osama; Modugno, Max; ...

2017-01-18

In this paper, the apparent fracture toughness of a porous cordierite ceramic was estimated using a large specimen whose geometry was inspired by the ASTM-C1421-standardized chevron-notch beam. In this paper, using the same combination of experiment and analysis used to develop the standardized chevron-notch test for small, monolithic ceramic bend bars, an apparent fracture toughness of 0.6 and 0.9 MPa√m were estimated for an unaged and aged cordierite diesel particulate filter structure, respectively. Finally, the effectiveness and simplicity of this adapted specimen geometry and test method lends itself to the evaluation of (macroscopic) apparent fracture toughness of an entire porous-ceramic,more » diesel particulate filter structure.« less

[In vitro evaluation of low-temperature aging effects of Y2O3 stabilized tetragonal zirconia polycrystals dental ceramics].

PubMed

Yi, Yuan-fu; Liu, Hong-chen; Wang, Chen; Tian, Jie-mo; Wen, Ning

2008-03-01

To investigate the influence of in vitro low-temperature degradation (LTD) treatment on the structural stability of 5 kinds of Y2O3 stabilized tetragonal zirconia polycrystals (Y-TZP) dental ceramics. TZ-3YS powder was compacted at 200 MPa using cold isostatic pressure and pre-sintered at 1050 degrees C for 2 h forming presintered blocks. Specimens were sectioned into 15 mm x 15 mm x 1.5 mm slices from blocks of TZ-3YS, Vita In-Ceram YZ, Ivoclar, Cercon Smart, and Kavo Y-TZP presintered blocks, 18 slices for each brand, and then densely sintered. Specimens were divided into 6 groups and subjected to an accelerated aging test carried out in an autoclave in steam at 134 degrees C, 0.2 MPa, for 0, 1, 2, 3, 4, and 5 h. X-ray diffraction (XRD) was used to identify crystal phases and relative content of monoclinic phase was calculated. Specimens for three-point bending test were fabricated using TZ-3YS ceramics according to the ISO 6872 standard and bending strength was tested before and after aging. The polished and aging specimens of TZ-3YS and Cercon Smart zirconia ceramics were observed by atomic force microscopy (AFM) to evaluate surface microstructure. Tetragonal-to-monoclinic phase transformation was detected for specimens of TZ-3YS, Vita In-Ceram YZ, Ivoclar, and Kavo zirconia ceramics except for Cercon Smart ceramics after aging, and the relative content of monoclinic phase was increasing with the prolonged aging time. TZ-3YS was the most affected material, Kavo took the second, and Vita and Ivoclar were similar. Aging had no significant negative effects on flexural strength of TZ-3YS with average bending strength being over 1100 MPa. The nucleation and growth of monoclinic phase were detected by AFM in surface of Cercon Smart zirconia in which monoclinic phase was not detected by XRD. The results suggest that LTD of dental Y-TZP is time dependent, but the aging test does not reduce the flexural strength of TZ-3YS. The long-term clinical serviceability of dental Y-TZP needs further observation.

The bonding effectiveness of five luting resin cements to the IPS Empress 2 all ceramic system.

PubMed

Bookhan, V; Essop, A R M; Du Preez, I C

2005-04-01

Variolink II is the only resin cement used for bonding IPS (Ivoclar Porcelain System) Empress 2 ceramic restorations. Alternative luting resin cements need to be investigated for their bonding effectiveness with the IPS Empress 2 ceramic. To determine the shear bond strength (SBS) and the effect of thermocycling, on the bonding effectiveness, of five resin cements to IPS Empress 2 ceramic. The projecting surfaces of one hundred ceramic discs were ground wet on silicone carbide paper. The specimens were divided into 5 groups of 20. The resin cements were bonded to the prepared ceramic surfaces, in the form of a stub. The specimens were stored under distilled water at 37 degrees C in an oven for 24 hours. Ten specimens in each group were thermocycled for 300 cycles between 5 degrees C and 55 degrees C. All the specimens were stressed to failure in an Instron Materials Testing Machine. The results were subjected to a one-way analysis of variance (ANOVA). Statistically similar mean SBS values were grouped using the Bonferroni (Dunn) multiple comparison test. The means for the non-thermocycled group were: 26.21, 19.41, 17.69, 17.43, and 15.76. The means for the thermocycled group were: 22.90, 15.72, 14.34, 13.96 and 13.45. The differences between the means were highly significant (p < 0.0125). The shear bond strength of Variolink II and Rely XARC to IPS Empress 2 ceramic was effective. Thermocycling had a significant effect on the mean SBS values of Calibra. Thermocycling had no significant effect on the mean SBS values of the other resin cements.

Crack Branching and Fracture Mirror Data of Glasses and Advanced Ceramics

NASA Technical Reports Server (NTRS)

Choi, Sung R.; Gyekenyesi, John P.

1998-01-01

The fracture mirror and crack branching constants were determined from three glasses and nine advanced ceramics tested under various loading and specimen configurations in an attempt to use the constants as a data base for fractography. The ratios of fracture mirror or crack branching constant to fracture toughness were found to be approximately two for most ceramic materials tested. A demonstration of how to use the two constants as a tool for verifying stress measurements was presented for silicon nitride disk specimens subjected to high-temperature, constant stress-rate biaxial flexure testing.

Net shaped high performance oxide ceramic parts by selective laser melting

NASA Astrophysics Data System (ADS)

Yves-Christian, Hagedorn; Jan, Wilkes; Wilhelm, Meiners; Konrad, Wissenbach; Reinhart, Poprawe

An additive manufacturing technique (AM) for ceramics, based on Al2O3-ZrO2 powder by means of Selective Laser Melting (SLM) is presented. Pure ceramic powder is completely melted by a laser beam yielding net-shaped specimens of almost 100% densities without any post-processing. Possible crack formation during the build-up process due to thermal stresses is prevented by a high-temperature preheating of above 1600 ∘C. Specimens with fine-grained nano-sized microstructures and flexural strengths of above 500 MPa are produced. The new technology allows for rapid freeform manufacture of complex net-shaped ceramics, thus, exploiting the outstanding mechanical and thermal properties for high-end medical and engineering disciplines.

Effect of Er:YAG laser irradiation on bonding property of zirconia ceramics to resin cement.

PubMed

Lin, Yihua; Song, Xiaomeng; Chen, Yaming; Zhu, Qingping; Zhang, Wei

2013-12-01

This study aimed to investigate whether or not an erbium: yttrium-aluminum-garnet (Er:YAG) laser could improve the bonding property of zirconia ceramics to resin cement. Surface treatments can improve the bonding properties of dental ceramics. However, little is known about the effect of Er:YAG laser irradiated on zirconia ceramics. Specimens of zirconia ceramic pieces were made, and randomly divided into 11 groups according to surface treatments, including one control group (no treatment), one air abrasion group, and nine Er:YAG laser groups. The laser groups were subdivided by applying different energy intensities (100, 200, or 300 mJ) and irradiation times (5, 10, or 15 sec). After surface treatments, ceramic pieces had their surface morphology observed, and their surface roughness was measured. All specimens were bonded to resin cement. Shear bond strength was measured after the bonded specimens were stored in water for 24 h, and additionally aged by thermocycling. Statistical analyses were performed using one way analysis of variance (ANOVA) and Tukey's test for shear bond strength, and Dunnett's t test for surface roughness, with α=0.05. Er:YAG laser irradiation changed the morphological characteristics of zirconia ceramics. Higher energy intensities (200, 300 mJ) could roughen the ceramics, but also caused surface cracks. There were no significant differences in the bond strength between the control group and the laser groups treated with different energy intensities or irradiation times. Air abrasion with alumina particles induced highest surface roughness and shear bond strength. Er:YAG laser irradiation cannot improve the bonding property of zirconia ceramics to resin cement. Enhancing irradiation intensities and extending irradiation time have no benefit on the bond of the ceramics, and might cause material defect.

Wear of human enamel opposing monolithic zirconia, glass ceramic, and composite resin: an in vitro study.

PubMed

Sripetchdanond, Jeerapa; Leevailoj, Chalermpol

2014-11-01

Demand is increasing for ceramic and composite resin posterior restorations. However, ceramics are recognized for their high abrasiveness to opposing dental structure. The purpose of this study was to investigate the wear of enamel as opposed to dental ceramics and composite resin. Twenty-four test specimens (antagonists), 6 each of monolithic zirconia, glass ceramic, composite resin, and enamel, were prepared into cylindrical rods. Enamel specimens were prepared from 24 extracted human permanent molar teeth. Enamel specimens were abraded against each type of antagonist with a pin-on-disk wear tester under a constant load of 25 N at 20 rpm for 4800 cycles. The maximum depth of wear (Dmax), mean depth of wear (Da), and mean surface roughness (Ra) of the enamel specimens were measured with a profilometer. All data were statistically analyzed by 1-way ANOVA, followed by the Tukey test (α=.05). A paired t test was used to compare the Ra of enamel at baseline and after testing. The wear of both the enamel and antagonists was evaluated qualitatively with scanning electron microscopic images. No significant differences were found in enamel wear depth (Dmax, Da) between monolithic zirconia (2.17 ±0.80, 1.83 ±0.75 μm) and composite resin (1.70 ±0.92, 1.37 ±0.81 μm) or between glass ceramic (8.54 ±2.31, 7.32 ±2.06 μm) and enamel (10.72 ±6.31, 8.81 ±5.16 μm). Significant differences were found when the enamel wear depth caused by monolithic zirconia and composite resin was compared with that of glass ceramic and enamel (P<.001). The Ra of enamel specimens increased significantly after wear tests with monolithic zirconia, glass ceramic, and enamel (P<.05); however, no difference was found among these materials. Within the limitations of this in vitro study, monolithic zirconia and composite resin resulted in less wear depth to human enamel compared with glass ceramic and enamel. All test materials except composite resin similarly increased the enamel surface roughness after wear testing. Copyright © 2014 Editorial Council for the Journal of Prosthetic Dentistry. Published by Elsevier Inc. All rights reserved.

Effect of the silicone disclosing procedure on the shear bond strength of composite cements to ceramic restorations.

PubMed

Szep, Susanne; Schmid, Claudia; Weigl, Paul; Hahn, Lothar; Heidemann, Detlef

2003-01-01

There is no evidence-based information on how ceramic restorations with an adhesive bond between restoration material and composite cement may be influenced by a silicone disclosing agent. The aim of this study was to determine the effects of the silicone disclosing procedure on the shear bond strength of composite cements in the luting of industrial sintered and laboratory sintered ceramic restorations. Thirty standardized (15 x 10 x 9 mm) prefabricated ceramic specimens (Groups 1, 3, 5) and 30 standardized (15 x10 x 9 mm) conventionally sintered ceramic specimens (Groups 2, 4, 6) were roughened with sandpaper (800-grit). Each group contained 10 specimens. Groups 3 and 4 were conditioned with hydrofluoric acid and primed with silane solution after the use of a silicone disclosing procedure. Groups 1 and 2 served as the control groups, where no silicone disclosing procedure was performed. Groups 5 and 6 were insulated with glycerine before the silicone disclosing procedure. A glass tube (4.5 mm in diameter) was used to apply a cylinder of dual-polymerized composite cement to the conditioned surfaces. All specimens were submitted to 5000 thermocycles (5 degrees to 55 degrees C) to simulate the in vivo situation. The specimens were subjected to a shear-pull test at a constant crosshead speed of 5 mm/min with a universal testing machine. The comparative shear bond strengths were analyzed by use of Duncan's test (alpha=0.05). Shear bond strength values for Groups 1 (9.86 +/- 4.97 MPa) and 2 (9.56 +/- 4.47 Mpa) were obtained with no significant differences. Lower but significantly undifferent values were obtained for Groups 3 (7.49 +/- 4.67 MPa) and 4 (7.62 +/- 3.49 MPa) after the use of a silicone disclosing procedure. In Groups 5 (8.21 +/- 4.75 MPa) and 6 (8.22 +/- 3.59 MPa), including insulation with glycerine before the silicone disclosing procedure, no significant differences were obtained. Within the limitations of this study, the use of silicone disclosing procedures before conditioning the ceramic surface did not lead to a significant reduction of the shear bond strength between ceramic and composite cement. The ceramic materials used (industrial-sintered versus laboratory-sintered ceramic) had no significant influence on adhesion.

Measuring Fracture Times Of Ceramics

NASA Technical Reports Server (NTRS)

Shlichta, Paul J.; Bister, Leo; Bickler, Donald G.

1989-01-01

Electrical measurements complement or replace fast cinematography. Electronic system measures microsecond time intervals between impacts of projectiles on ceramic tiles and fracture tiles. Used in research on ceramics and ceramic-based composite materials such as armor. Hardness and low density of ceramics enable them to disintegrate projectiles more efficiently than metals. Projectile approaches ceramic tile specimen. Penetrating foil squares of triggering device activate display and recording instruments. As ceramic and resistive film break oscilloscope plots increase in electrical resistance of film.

[Effect of hydrofluoric acid concentration on the surface morphology and bonding effectiveness of lithium disilicate glass ceramics to resin composites].

PubMed

Hailan, Qian; Lingyan, Ren; Rongrong, Nie; Xiangfeng, Meng

2017-12-01

This study aimed at determining the influence of hydrofluoric acid (HF) in varied concentrations on the surface morphology of lithium disilicate glass ceramics and bond durability between resin composites and post-treated lithium disilicate glass ceramics. After being sintered, ground, and washed, 72 as-prepared specimens of lithium disilicate glass ceramics with dimensions of 11 mm×13 mm×2 mm were randomly divided into three groups. Each group was treated with acid solution [32% phosphoric acid (PA) or 4% or 9.5% HF] for 20 s. Then, four acidified specimens from each group were randomly selected. One of the specimens was used to observe the surface morphology using scanning electron microscopy, and the others were used to observe the surface roughness using a surface roughness meter (including Ra, Rz, and Rmax). After treatment with different acid solutions in each group, 20 samples were further treated with silane coupling agent/resin adhesive/resin cement (Monobond S/Multilink Primer A&B/Multilink N), followed by bonding to a composite resin column (Filtek™ Z350) with a diameter of 3 mm. A total of 20 specimens in each group were randomly divided into two subgroups, which were used for measuring the microshear bond strength, with one of them subjected to cool-thermal cycle for 20 000 times. The surface roughness (Ra, Rz, and Rmax) of lithium disilicate glass ceramics treated with 4% or 9.5% HF was significantly higher than that of the ceramic treated with PA (P<0.05). The lithium disilicate glass ceramics treated with 9.5% HF also demonstrated better surface roughness (Rz and Rmax) than that of the ceramics treated with 4% HF. Cool-thermal cycle treatment reduced the bond strength of lithium disilicate glass ceramics in all groups (P<0.05). After cool-thermal cycle, the lithium disilicate glass ceramics treated with HF had higher bond strength than that of the ceramics treated with PA. The lithium disilicate glass ceramics treated with 4% HF had higher bond strength than that of the ceramics treated with 9.5% HF (P<0.05). During cool-thermal cycle, the lithium disilicate glass ceramics treated with 4% HF demonstrated higher reduction in bond strength than that of the samples treated with 9.5% HF (P<0.05). The concentration of HF significantly affected the surface morphology of lithium disilicate glass ceramics and the bond durability between resin composites and post-treated lithium disilicate glass ceramics. The bond strength between resin composites and post-treated lithium disilicate glass ceramic was more efficiently maintained by treatment with 9.5% HF.

Behavior of osteoblast-like cells on calcium-deficient hydroxyapatite ceramics composed of particles with different shapes and sizes.

PubMed

Kamitakahara, Masanobu; Uno, Yuika; Ioku, Koji

2014-01-01

In designing the biomaterials, it is important to control their surface morphologies, because they affect the interactions between the materials and cells. We previously reported that porous calcium-deficient hydroxyapatite (HA) ceramics composed of rod-like particles had advantages over sintered porous HA ceramics; however, the effects of the surface morphology of calcium-deficient HA ceramics on cell behavior have remained unclear. Using a hydrothermal process, we successfully prepared porous calcium-deficient HA ceramics with different surface morphologies, composed of plate-like particles of 200-300, 500-800 nm, or 2-3 μm in width and rod-like particles of 1 or 3-5 μm in width, respectively. The effects of these surface morphologies on the behavior of osteoblast-like cells were examined. Although the numbers of cells adhered to the ceramic specimens did not differ significantly among the specimens, the proliferation rates of cells on the ceramics decreased with decreasing particle size. Our results reveal that controlling the surface morphology that is governed by particle shape and size is important for designing porous calcium-deficient HA ceramics.

Modified PZT ceramics as a material that can be used in micromechatronics

NASA Astrophysics Data System (ADS)

Zachariasz, Radosław; Bochenek, Dariusz

2015-11-01

Results on investigations of the PZT type ceramics with the following chemical composition: Pb0.94Sr0.06(Zr0.50 Ti0.50)0.99 Cr0.01O3 (PSZTC) which belongs to a group of multicomponent ceramic materials obtained on basis of the PZT type solid solution, are presented in this work. Ceramics PSZTC was obtained by a free sintering method under the following conditions: Tsint = 1250 °C and tsint = 2 h. Ceramic compacts of specimens for the sintering process were made from the ceramic mass consisting of a mixture of the synthesized PSZTC powder and 3% polyvinyl alcohol while wet. The PSZTC ceramic specimens were subjected to poling by two methods: low temperature and high temperature. On the basis of the examinations made it has been found that the ceramics obtained belongs to ferroelectric-hard materials and that is why it may be used to build resonators, filters and ultrasonic transducers. Contribution to the Topical Issue "Materials for Dielectric Applications" edited by Maciej Jaroszewski and Sabu Thomas.

Development of Processing Techniques for Advanced Thermal Protection Materials

NASA Technical Reports Server (NTRS)

Selvaduray, Guna; Cox, Michael; Srinivasan, Vijayakumar

1997-01-01

Thermal Protection Materials Branch (TPMB) has been involved in various research programs to improve the properties and structural integrity of the existing aerospace high temperature materials. Specimens from various research programs were brought into the analytical laboratory for the purpose of obtaining and refining the material characterization. The analytical laboratory in TPMB has many different instruments which were utilized to determine the physical and chemical characteristics of materials. Some of the instruments that were utilized by the SJSU students are: Scanning Electron Microscopy (SEM), Energy Dispersive X-ray analysis (EDX), X-ray Diffraction Spectrometer (XRD), Fourier Transform-Infrared Spectroscopy (FTIR), Ultra Violet Spectroscopy/Visible Spectroscopy (UV/VIS), Particle Size Analyzer (PSA), and Inductively Coupled Plasma Atomic Emission Spectrometer (ICP-AES). The above mentioned analytical instruments were utilized in the material characterization process of the specimens from research programs such as: aerogel ceramics (I) and (II), X-33 Blankets, ARC-Jet specimens, QUICFIX specimens and gas permeability of lightweight ceramic ablators. In addition to analytical instruments in the analytical laboratory at TPMB, there are several on-going experiments. One particular experiment allows the measurement of permeability of ceramic ablators. From these measurements, physical characteristics of the ceramic ablators can be derived.

Influence of contamination on bonding to zirconia ceramic.

PubMed

Yang, Bin; Scharnberg, Michael; Wolfart, Stefan; Quaas, Anne C; Ludwig, Klaus; Adelung, Rainer; Kern, Matthias

2007-05-01

The purpose of this study was to investigate the influences of contaminations and cleaning methods on bonding to dental zirconia ceramic. After saliva immersion and using silicone disclosing agent, airborne-particle abraded ceramic specimens were cleaned with isopropanol (AL), acetone (AC), 37% phosphoric acid (PA), additional airborne-particle abrasion (AA), or only with water rinsing (SS). Airborne-particle abraded specimens without contaminations (CL) were used as control group. For chemical analysis specimens of all groups were examined with X-ray photoelectron spectroscopy (XPS). Plexiglas tubes filled with composite resin were bonded to ceramic specimens using a phosphate-monomer containing composite luting resin. After 3-day water storage, tensile bond strengths (TBS) were tested. XPS analysis of group SS showed the presence of saliva and silicone (Si) contamination on the surface. The ratios of carbon/zirconium and oxygen/zirconium for groups PA and AA were comparable to those ratios obtained for group CL, indicating the removal of the organic saliva contamination. Airborne-particle abrasion and acetone completely removed Si contamination from ceramic surfaces. Isopropanol had little cleaning effect on the two contaminants. TBS (median +/- standard deviation) in MPa of the groups SS (11.6 +/- 3.1), AL (10.0 +/- 2.9), and AC (13.0 +/- 2.8) were statistically lower than those of groups PA (33.6 +/- 5.5), AA (40.1 +/- 3.6), and CL (47.0 +/- 8.1) (p < 0.001), while no differences were found in TBS between groups AA and CL (p > 0.5). Contamination significantly reduced bond strengths to zirconia ceramic. Airborne-particle abrasion was the most effective cleaning method.

The influences of accelerated aging on mechanical properties of veneering ceramics used for zirconia restorations.

PubMed

Luo, Huinan; Tang, Xuehua; Dong, Zhen; Tang, Hui; Nakamura, Takashi; Yatani, Hirofumi

2016-01-01

This study evaluated the influences of accelerated aging on the mechanical properties of veneering ceramics used for zirconia frameworks. Five different veneering ceramics for zirconia frameworks were used. Twenty specimens were fabricated for each veneering ceramic. All specimens were divided into two groups. One was subjected to accelerated aging and the other was used as a control. Accelerated aging was performed in distilled water for 5 h at 200ºC and 2 atm. The density, open porosity, surface roughness, three-point flexural strength, and Vickers hardness were measured. The results showed that the density, open porosity, and surface roughness of all examined veneering ceramics were changed by the accelerated aging process. Accelerated aging was also found to have a positive effect on strength and a negative effect on the hardness.

Effect of etching and airborne particle abrasion on the microstructure of different dental ceramics.

PubMed

Borges, Gilberto Antonio; Sophr, Ana Maria; de Goes, Mario Fernando; Sobrinho, Lourenço Correr; Chan, Daniel C N

2003-05-01

The ceramic composition and microstructure surface of all-ceramic restorations are important components of an effective bonding substrate. Both hydrofluoric acid etching and airborne aluminum oxide particle abrasion produce irregular surfaces necessary for micromechanical bonding. Although surface treatments of feldspathic and leucite porcelains have been studied previously, the high alumina-containing and lithium disilicate ceramics have not been fully investigated. The purpose of this study was to assess the surface topography of 6 different ceramics after treatment with either hydrofluoric acid etching or airborne aluminum oxide particle abrasion. Five copings each of IPS Empress, IPS Empress 2 (0.8 mm thick), Cergogold (0.7 mm thick), In-Ceram Alumina, In-Ceram Zirconia, and Procera (0.8 mm thick) were fabricated following the manufacturer's instructions. Each coping was longitudinally sectioned into 4 equal parts by a diamond disk. The resulting sections were then randomly divided into 3 groups depending on subsequent surface treatments: Group 1, specimens without additional surface treatments, as received from the laboratory (control); Group 2, specimens treated by use of airborne particle abrasion with 50-microm aluminum oxide; and Group 3, specimens treated with 10% hydrofluoric acid etching (20 seconds for IPS Empress 2; 60 seconds for IPS Empress and Cergogold; and 2 minutes for In-Ceram Alumina, In-Ceram Zirconia, and Procera). Airborne particle abrasion changed the morphologic surface of IPS Empress, IPS Empress 2, and Cergogold ceramics. The surface topography of these ceramics exhibited shallow irregularities not evident in the control group. For Procera, the 50-microm aluminum oxide airborne particle abrasion produced a flattened surface. Airborne particle abrasion of In-Ceram Alumina and In-Ceram Zirconia did not change the morphologic characteristics and the same shallows pits found in the control group remained. For IPS Empress 2, 10% hydrofluoric acid etching produced elongated crystals scattered with shallow irregularities. For IPS Empress and Cergogold, the morphologic characteristic was honeycomb-like on the ceramic surface. The surface treatment of In-Ceram Alumina, In-Ceram Zirconia, and Procera did not change their superficial structure. Hydrofluoric acid etching and airborne particle abrasion with 50-microm aluminum oxide increased the irregularities on the surface of IPS Empress, IPS Empress 2, and Cergogold ceramics. Similar treatment of In-Ceram Alumina, In-Ceram Zirconia, and Procera did not change their morphologic microstructure.

High temperature composites. Status and future directions

NASA Technical Reports Server (NTRS)

Signorelli, R. A.

1982-01-01

A summary of research investigations of manufacturing methods, fabrication methods, and testing of high temperature composites for use in gas turbine engines is presented. Ceramic/ceramic, ceramic/metal, and metal/metal composites are considered. Directional solidification of superalloys and eutectic alloys, fiber reinforced metal and ceramic composites, ceramic fibers and whiskers, refractory coatings, metal fiber/metal composites, matrix metal selection, and the preparation of test specimens are discussed.

Initial polishing time affects gloss retention in resin composites.

PubMed

Waheeb, Nehal; Silikas, Nick; Watts, David

2012-10-01

To determine the effect of finishing and polishing time on the surface gloss of various resin-composites before and after simulated toothbrushing. Eight representative resin-composites (Ceram X mono, Ceram X duo, Tetric EvoCeram, Venus Diamond, EsteliteSigma Quick, Esthet.X HD, Filtek Supreme XT and Spectrum TPH) were used to prepare 80 disc-shaped (12 mm x 2 mm) specimens. The two step system Venus Supra was used for polishing the specimens for 3 minutes (Group A) and 10 minutes (Group B). All specimens were subjected to 16,000 cycles of simulated toothbrushing. The surface gloss was measured after polishing and after brushing using the gloss meter. Results were evaluated using one way ANOVA, two ways ANOVA and Dennett's post hoc test (P = 0.05). Group B (10-minute polishing) resulted in higher gloss values (GV) for all specimens compared to Group A (3 minutes). Also Group B showed better gloss retention compared to Group A after simulated toothbrushing. In each group, there was a significant difference between the polished composite resins (P < 0.05). For all specimens there was a decrease in gloss after the simulated toothbrushing.

Durability of feldspathic veneering ceramic on glass-infiltrated alumina ceramics after long-term thermocycling.

PubMed

Mesquita, A M M; Ozcan, M; Souza, R O A; Kojima, A N; Nishioka, R S; Kimpara, E T; Bottino, M A

2010-01-01

This study compared the bond strength durability of a feldspathic veneering ceramic to glass-infiltrated reinforced ceramics in dry and aged conditions. Disc shaped (thickness: 4 mm, diameter: 4 mm) of glass-infiltrated alumina (In-Ceram Alumina) and glass-infiltrated alumina reinforced by zirconia (In-Ceram Zirconia) core ceramic specimens (N=48, N=12 per groups) were constructed according to the manufacturers' recommendations. Veneering ceramic (VITA VM7) was fired onto the core ceramics using a mold. The core-veneering ceramic assemblies were randomly divided into two conditions and tested either immediately after specimen preparation (Dry) or following 30000 thermocycling (5-55 ºC±1; dwell time: 30 seconds). Shear bond strength test was performed in a universal testing machine (cross-head speed: 1 mm/min). Failure modes were analyzed using optical microscope (x20). The bond strength data (MPa) were analyzed using ANOVA (α=0.05). Thermocycling did not decrease the bond strength results for both In-Ceram Alumina (30.6±8.2 MPa; P=0.2053) and In-Ceram zirconia (32.6±9 MPa; P=0.3987) core ceramic-feldspathic veneering ceramic combinations when compared to non-aged conditions (28.1±6.4 MPa, 29.7±7.3 MPa, respectively). There were also no significant differences between adhesion of the veneering ceramic to either In-Ceram Alumina or In-Ceram Zirconia ceramics (P=0.3289). Failure types were predominantly a mixture of adhesive failure between the veneering and the core ceramic together with cohesive fracture of the veneering ceramic. Long-term thermocycling aging conditions did not impair the adhesion of the veneering ceramic to the glass-infiltrated alumina core ceramics tested.

Biaxial flexural strength of Turkom-Cera core compared to two other all-ceramic systems

PubMed Central

AL-MAKRAMANI, Bandar Mohammed Abdullah; RAZAK, Abdul Aziz Abdul; ABU-HASSAN, Mohamed Ibrahim

2010-01-01

Advances in all-ceramic systems have established predictable means of providing metal-free aesthetic and biocompatible materials. These materials must have sufficient strength to be a practical treatment alternative for the fabrication of crowns and fixed partial dentures. Objectives The aim of this study was to compare the biaxial flexural strength of three core ceramic materials. Material and methods Three groups of 10 disc-shaped specimens (16 mm diameter x 1.2 mm thickness - in accordance with ISO-6872, 1995) were made from the following ceramic materials: Turkom-Cera Fused Alumina [(Turkom-Ceramic (M) Sdn Bhd, Puchong, Selangor, Malaysia)], In-Ceram (Vita Zahnfabrik, Bad Säckingen, Baden-Württemberg, Germany) and Vitadur-N (Vita Zahnfabrik, Bad Säckingen, Baden-Württemberg, Germany), which were sintered according to the manufacturer's recommendations. The specimens were subjected to biaxial flexural strength test in a universal testing machine at a crosshead speed of 0.5 mm/min. The definitive fracture load was recorded for each specimen and the biaxial flexural strength was calculated from an equation in accordance with ISO-6872. Results The mean biaxial flexural strength values were: Turkom-Cera: 506.8±87.01 MPa, In-Ceram: 347.4±28.83 MPa and Vitadur-N: 128.7±12.72 MPa. The results were analyzed by the Levene's test and Dunnett's T3 post-hoc test (SPSS software V11.5.0 for Windows, SPSS, Chicago, IL, USA ) at a preset significance level of 5% because of unequal group variances (P<0.001). There was statistically significant difference between the three core ceramics (P<0.05). Turkom-Cera showed the highest biaxial flexural strength, followed by In-Ceram and Vitadur-N. Conclusions Turkom-Cera core had significantly higher flexural strength than In-Ceram and Vitadur-N ceramic core materials. PMID:21308292

Evidence of yttrium silicate inclusions in YSZ-porcelain veneers.

PubMed

Stoner, Brian R; Griggs, Jason A; Neidigh, John; Piascik, Jeffrey R

2014-04-01

This report introduces the discovery of crystalline defects that can form in the porcelain veneering layer when in contact with yttria-stabilized zirconia (YSZ). The focus was on dental prostheses and understanding the defects that form in the YSZ/porcelain system; however the data reported herein may have broader implications toward the use and stability of YSZ-based ceramics in general. Specimens were cut from fully sintered YSZ plates and veneering porcelain was applied (<1 mm thick) to one surface and fired under manufacturer's recommended protocol. Scanning electron microscopy (SEM) with integrated electron dispersive X-ray (EDAX) was used for microstructural and elemental analysis. EDAX, for chemical analysis and transmission electron diffraction (TED) for structural analysis were both performed in the transmission electron microscope (TEM). Additionally, in order to spatially resolve Y-rich precipitates, micro-CT scans were conducted at varying depths within the porcelain veneer. Local EDAX (SEM) was performed in the regions of visible inclusions and showed significant increases in yttrium concentration. TEM specimens also showed apparent inclusions in the porcelain and selected area electron diffraction was performed on these regions and found the inclusions to be crystalline and identified as either yttrium-silicate (Y2 SiO5 ) or yttrium-disilicate (Y2 Si2 O7 ). Micro-CT data showed that yttrium-silicate precipitates were distributed throughout the thickness of the porcelain veneer. Future studies are needed to determine whether many of the premature failures associated with this materials system may be the result of crystalline flaws that form as a result of high temperature yttrium diffusion near the surfaces of YSZ. © 2013 Wiley Periodicals, Inc.

Gloss and Stain Resistance of Ceramic-Polymer CAD/CAM Restorative Blocks.

PubMed

Lawson, Nathaniel C; Burgess, John O

2016-03-01

To evaluate the gloss and stain resistance of several new ceramic-polymer CAD/CAM blocks Specimens (4 mm) were sectioned from: Enamic (polymer-infused ceramic), LAVA Ultimate (nano-ceramic reinforced polymer), e.max (lithium disilicate), Paradigm C (porcelain), and Paradigm MZ100 (composite). Specimens were wet polished on a polishing wheel to either 320 grit silicon paper (un-polished, N = 8) or 2000 grit silicon carbide papers followed by a 0.05 μm alumina slurry (polished, N = 8). Initial gloss and color (L*a*b*) values were measured. Specimens were stored in a staining solution at 37°C in darkness for 12 days (simulating 1 year). After storage, L*a*b* values re-measured. Change in color was reported as ΔE00 based on the CIEDE2000 formula. Gloss and ΔE00 were analyzed by two-way analysis of variance (ANOVA) (alpha = .05). Separate one-way ANOVA and Tukey post-hoc analyses were performed for both polish conditions and all materials. Two-way ANOVA showed that factors material, polish and their interaction were significant for both gloss and ΔE00 (p < .01). Post-hoc analysis reveals that polished specimens had significantly less color change than un-polished specimens for Paradigm C and LAVA Ultimate. E.max had significantly higher gloss and less color change than all other materials. The composition and polish of CAD/CAM materials affects gloss and stain resistance. Ceramic-polymer hybrid materials can achieve the high gloss required for esthetic restorations. These materials should be polished in order to minimize staining. If polished, all of the tested materials exhibited clinically acceptable color changes at 1 year of simulated staining. (J Esthet Restor Dent 28:S40-S45, 2016). © 2015 Wiley Periodicals, Inc.

Thermal debonding of ceramic brackets: an in vitro study.

PubMed

Crooks, M; Hood, J; Harkness, M

1997-02-01

Thermal debonding has been developed to overcome the problems of enamel damage and high forces when debonding ceramic orthodontic brackets. However, the temperature changes with thermal debonding have the potential to damage the tooth tissues. The principal aims of this study are, first, to investigate the effects of resin type, resin thickness, and debonding force on the temperature changes in human premolars during thermal debonding of ceramic brackets and, second, to record the sites of bond failure and damage to the tooth surface. Ceramic brackets were attached to each specimen by using one of four types of bonding resin in a controlled thick or thin resin layer. The ceramic debonding unit (Dentaurum, Pforzheim, Germany) was used to thermally debond the brackets with either a 40 or 80 Nmm torsional force. Higher temperature changes at the pulpal wall (> 10 degrees C in some 40 Nmm torsional force specimens) always occurred with Concise (3M Dental Products, St. Paul, Minn.) and Transbond (Unitek/3M Dental Products, Monrovia, Calif.) resins, and lower temperature changes (< 5 degrees C) with Quasar (Rocky Mountain Orthodontics, Denver, Colo.) and Ortho. B.S. (Dentaurum, Pforzheim, Germany) resins. In general, resin thickness was not significantly associated with buccal surface or pulpal wall temperature changes. However, temperature changes at the pulpal wall were significantly associated with the temperature changes at the buccal surface (r = 0.76), with the temperature of the thermal debonder blade for thin resin layer specimens (r = 0.50), and the time required to debond the bracket for both thick (r = 0.74) and thin (r = 0.63) resin layer specimens. In most specimens, the site of bond failure occurred at the bracket-resin interface. There was no evidence of enamel damage after bracket removal.

Polypropylenes foam consisting of thermally expandable microcapsule as blowing agent

NASA Astrophysics Data System (ADS)

Jeoung, Sun Kyung; Hwang, Ye Jin; Lee, Hyun Wook; Kwak, Sung Bok; Han, In-Soo; Ha, Jin Uk

2016-03-01

The structure of thermally expandable microcapsule (TEMs) is consisted of a thermoplastic shell which is filled with liquid hydrocarbon at core. The shell of TEMs becomes soft when the temperature is higher than boiling temperature of liquid hydrocarbon. The shell of TEMs is expanded under the high temperature because the inner pressure of TEMs is increased by vaporization of hydrocarbon core. Therefore, the TEMs are applicable for blowing agents and light weight fillers. In this research, we fabricated the polypropylene (PP) foam by using the TEMs and chemical blowing agents and compared to their physical properties. The density of the specimen was decreased when the contents of chemical blowing agents and TEMs were increased. In addition, the mechanical properties (i.e. tensile strength and impact strength) of specimens were deteriorated with increasing amount of chemical blowing agents and TEMs. However, PP foam produced with TEMs showed higher impact strength than the one with the chemical blowing agent. In order to clarify the dependence of impact strength of PP foam as the blowing agent, the morphology difference of the PP foams was investigated. Expanding properties of PP foams produced with TEMs was changed with TEMs content of PP foams. Processing conditions also influenced the mechanical properties of PP foam containing TEMs.

Effective Size Analysis of the Diametral Compression (Brazil) Test Specimen

DOE Office of Scientific and Technical Information (OSTI.GOV)

Jadaan, Osama M.; Wereszczak, Andrew A

2009-04-01

This study considers the finite element analysis (FEA) simulation and Weibull effective size analysis for the diametral compression (DC) or Brazil specimen loaded with three different push-rod geometries. Those geometries are a flat push-rod, a push-rod whose radius of curvature is larger than that for the DC specimen, and a push-rod whose radius of curvature matches that of the DC specimen. Such established effective size analysis recognizes that the tensile strength of structural ceramics is typically one to two orders of magnitude less than its compressive strength. Therefore, because fracture is much more apt to result from a tensile stressmore » than a compressive one, this traditional analysis only considers the first principal tensile stress field in the mechanically loaded ceramic component for the effective size analysis. The effective areas and effective volumes were computed as function of Weibull modulus using the CARES/Life code. Particular attention was devoted to the effect of mesh sensitivity and localized stress concentration. The effect of specimen width on the stress state was also investigated. The effects of push-rod geometry, the use of steel versus WC push-rods, and considering a frictionless versus no-slip interface between push-rod and specimen on the maximum stresses, where those stresses are located, and the effective area and effective volume results are described. Of the three push-rod geometries, it is concluded that the push-rod (made from WC rather than steel) whose radius of curvature matches that of the DC specimen is the most apt to cause fracture initiation within the specimen's bulk rather than at the loading interface. Therefore, its geometry is the most likely to produce a valid diametral compression strength test. However, the DC specimen remains inefficient in terms of its area and volume efficiencies; namely, the tensile strength of only a few percent of the specimen's entire area or volume is sampled. Given the high probability that a valid (or invalid) test can be proven by ceramic fractographic practices suggests that this test method and specimen is questionable for use with relatively strong structural ceramics.« less

Spotiton: A prototype for an integrated inkjet dispense and vitrification system for cryo-TEM

PubMed Central

Jain, Tilak; Sheehan, Patrick; Crum, John; Carragher, Bridget; Potter, Clinton S.

2012-01-01

Over the last three decades, Cryo-TEM has developed into a powerful technique for high-resolution imaging of biological macromolecules in their native vitrified state. However, the technique for vitrifying specimens onto EM grids is essentially unchanged – application of ~ 3 µL sample to a grid, followed by blotting and rapid plunge freezing into liquid ethane. Several trials are often required to obtain suitable thin (few hundred nanometers or less) vitrified layers amenable for cryo-TEM imaging, which results in waste of precious sample and resources. While commercially available instruments provide some level of automation to control the vitrification process in an effort to increase quality and reproducibility, obtaining satisfactory vitrified specimens remains a bottleneck in the Cryo-TEM pipeline. We describe here a completely novel method for EM specimen preparation based on small volume (picoliter to nanoliter) dispensing using inkjet technology. A first prototype system (Spotiton v0.5) demonstrates feasibility of this new approach for specimen vitrification. A piezo-electric inkjet dispenser is integrated with optical real-time cameras (100 Hz frame rate) to analyze picoliter to nanoliter droplet profiles in-flight and spreading dynamics on the grid, and thus provides a method to optimize timing of the process. Using TEM imaging and biochemical assays we demonstrate that the piezo-electric inkjet mechanism does not disrupt the structural or functional integrity of macromolecules. These preliminary studies provide insight into the factors and components that will need further development to enable a robust and repeatable technique for specimen vitrification using this novel approach. PMID:22569522

Thermal barrier coating life prediction model development, phase 2

NASA Technical Reports Server (NTRS)

Meier, Susan Manning; Sheffler, Keith D.; Nissley, David M.

1991-01-01

The objective of this program was to generate a life prediction model for electron-beam-physical vapor deposited (EB-PVD) zirconia thermal barrier coating (TBC) on gas turbine engine components. Specific activities involved in development of the EB-PVD life prediction model included measurement of EB-PVD ceramic physical and mechanical properties and adherence strength, measurement of the thermally grown oxide (TGO) growth kinetics, generation of quantitative cyclic thermal spallation life data, and development of a spallation life prediction model. Life data useful for model development was obtained by exposing instrumented, EB-PVD ceramic coated cylindrical specimens in a jet fueled burner rig. Monotonic compression and tensile mechanical tests and physical property tests were conducted to obtain the EB-PVD ceramic behavior required for burner rig specimen analysis. As part of that effort, a nonlinear constitutive model was developed for the EB-PVD ceramic. Spallation failure of the EB-PVD TBC system consistently occurred at the TGO-metal interface. Calculated out-of-plane stresses were a small fraction of that required to statically fail the TGO. Thus, EB-PVD spallation was attributed to the interfacial cracking caused by in-plane TGO strains. Since TGO mechanical properties were not measured in this program, calculation of the burner rig specimen TGO in-plane strains was performed by using alumina properties. A life model based on maximum in-plane TGO tensile mechanical strain and TGO thickness correlated the burner rig specimen EB-PVD ceramic spallation lives within a factor of about plus or minus 2X.

Development of plane strain fracture toughness test for ceramics using Chevron notched specimens

NASA Technical Reports Server (NTRS)

Bubsey, R. T.; Shannon, J. L., Jr.; Munz, D.

1983-01-01

Chevron-notched four-point-bend and short-bar specimens have been used to determine the fracture toughness of sintered aluminum oxide and hot-pressed silicon nitride ceramics. The fracture toughness for Si3N4 is found to be essentially independent of the specimen size and chevron notch configuration, with values ranging from 4.6 to 4.9 MNm exp -3/2. In contrast, significant specimen size and notch geometry effects have been observed for Al2O3, with the fracture toughness ranging from 3.1 to 4.7 MNm exp -3/2. These effects are attributed to a rising crack growth resistance curve for the Al2O3 tested.

Post-ion beam induced degradation of copper layers in transmission electron microscopy specimens

NASA Astrophysics Data System (ADS)

Seidel, F.; Richard, O.; Bender, H.; Vandervorst, W.

2015-11-01

Copper containing transmission electron microscopy (TEM) specimens frequently show corrosion after focused ion beam (FIB) preparation. This paper reveals that the corrosion product is a Cu-S phase growing over the specimen surface. The layer is identified by energy-dispersive x-ray spectroscopy, and lattice spacing indexing of power spectra patterns. The corrosion process is further studied by TEM on cone-shaped specimens, which are intentionally stored after FIB preparation with S flakes for short time. Furthermore, a protective method against corrosion is developed by varying the time in the FIB vacuum and the duration of a subsequent plasma cleaning.

[A study of bone-like apatite formation on calcium phosphate ceramics in different kinds of animals in vivo].

PubMed

Duan, Yourong; Wu, Yao; Wang, Chaoyuan; Chen, Jiyong; Zhang, Xingdong

2003-03-01

Bone-like apatite formation on the surface of calcium phosphate ceramics has been believed to be necessary for new bone to grow on the ceramics and to be related to the osteoinductivity of the material. The research of bone-like apatite formation is a great help to understanding the mechanism of osteoinduction. Synthetic porous calcium phosphate ceramics (HA/TCP = 70/30) were implanted intramuscularly in pigs, dogs, rabbits and rats to make a comparative study of the bone-like apatite formation onto the porous HA/TCP ceramics in different animals. Specimens were harvested at 14 days after implantation. Samples were detected for the surface morphology with SEM. The chemical composition of the sample surface after implantation was analyzed with reflection infrared (R-IR). Obvious bone-like apatite formation could be detected in the sections of porous specimens harvested from all animals after 14 days intramuscular implantation. Crystal deposition could be only observed on the surface of the concave regions of the samples collected from dogs, rabbits and rat. On the contrary, evenly distributed flake-shaped crystal could be found on the pore surface and also on the outer surface of the materials implanted in pigs. The morphology of bone-like apatite in pigs was different from that in the others animals. Bone-like apatite was not observed in dense specimen implanted intramuscularly. Bone-like apatite formed faster on specimens implanted in rabbit than that in other animals. This formation sequence is different from the sequence of osteoinductivity of biphasic calcium phosphate ceramics implanted in these animals. The results demonstrated that the formation of bone-like apatite on materials is a prerequisite condition to their osteoinduction but other factors also play important roles in osteoinduction.

Contact thermal shock test of ceramics

NASA Technical Reports Server (NTRS)

Rogers, W. P.; Emery, A. F.

1992-01-01

A novel quantitative thermal shock test of ceramics is described. The technique employs contact between a metal-cooling rod and hot disk-shaped specimen. In contrast with traditional techniques, the well-defined thermal boundary condition allows for accurate analyses of heat transfer, stress, and fracture. Uniform equibiaxial tensile stresses are induced in the center of the test specimen. Transient specimen temperature and acoustic emission are monitored continuously during the thermal stress cycle. The technique is demonstrated with soda-lime glass specimens. Experimental results are compared with theoretical predictions based on a finite-element method thermal stress analysis combined with a statistical model of fracture. Material strength parameters are determined using concentric ring flexure tests. Good agreement is found between experimental results and theoretical predictions of failure probability as a function of time and initial specimen temperature.

Wear characteristics of polished and glazed lithium disilicate ceramics opposed to three ceramic materials.

PubMed

Saiki, Osamu; Koizumi, Hiroyasu; Akazawa, Nobutaka; Kodaira, Akihisa; Okamura, Kentaro; Matsumura, Hideo

2016-01-01

This study compared the wear characteristics of a heat-pressed lithium disilicate ceramic material opposed to feldspathic porcelain, a lithium disilicate glass ceramic, and zirconia materials. Ceramic plate specimens were prepared from feldspathic porcelain (EX-3 nA1B), lithium disilicate glass ceramics (e.max CAD MO1/C14), and zirconia (Katana KT 10) and then ground or polished. Rounded rod specimens were fabricated from heat-pressed lithium disilicate glass ceramic (e.max press LT A3) and then glazed or polished. A sliding wear testing apparatus was used for wear testing. Wear of glazed rods was greater than that of polished rods when they were abraded with ground zirconia, ground porcelain, polished porcelain, or polished lithium disilicate ceramics. For both glazed and polished rods, wear was greater when the rods were abraded with ground plates. The findings indicate that application of a polished surface rather than a glazed surface is recommended for single restorations made of heat-pressed lithium disilicate material. In addition, care must be taken when polishing opposing materials, especially those used in occlusal contact areas. (J Oral Sci 58, 117-123, 2016).

Effect of Light-Cured Resin Cement Application on Translucency of Ceramic Veneers and Light Transmission of LED Polymerization Units.

PubMed

Zhang, Lei; Luo, Xiao Ping; Tan, Ren Xiang

2018-05-31

To evaluate the effect of light-cured resin cement application based on etching and silanization on the translucent property of ceramic veneers in different thicknesses, testing the hypothesis that the surface treatment and subsequent resin cement application could influence the translucency of ceramic veneers. The relationship between translucency of ceramic veneers and light transmission irradiated by LED polymerization units was also determined. 40 specimens (10 mm diameter) were fabricated from IPS e.max Press HT A2 ceramic ingots, and polished to 0.3 ± 0.01 mm, 0.5 ± 0.01 mm, 0.7 ± 0.01 mm, 1.0 ± 0.01 mm, and 1.5 ± 0.01 mm thick (n = 8/group). One surface of each disc was etched with HF acid, silanized with Monobond-S, and applied with a light-cured resin cement (Variolink N Transparent Base). Before and after the above procedure, the total luminous transmittance (τ) of all specimens was assessed by a spectrophotometer in a wavelength range of 380-780 nm. A handheld radiometer was used to measure the light intensity irradiated by three LED polymerization units. Light transmission (LT) through ceramic specimens after resin cement application was calculated. Data were statistically analyzed using two-way ANOVA (p = 0.05) and Tukey's test. The correlation between translucency (τ) of ceramic veneers after resin cement application and light transmission (LT) of curing units was statistically evaluated using Spearman correlation test (p = 0.05). With the increase of ceramic thickness, the transmittance decreased significantly (p < 0.05). For the 0.3-mm, 0.5-mm, and 0.7-mm-thick groups, the transmittance of ceramic specimens was statistically significantly lower after resin cement application (p < 0.05). The r value of Bluephase C8 was 0.988, 0.977 for Bluphase, and 0.883 for Bluephase 20i, indicating that the light transmission (LT%) was positively correlated to the translucency of ceramic veneers, regardless of the type of curing units. After the light-cured resin cement application based on etching and silanization, the ceramic veneers (less than 0.7-mm thick) were less translucent, and the translucency decreased when the thickness increased. Because of the lower translucency of ceramic veneers, the light intensity of LED units transmitted to resin layer would decrease when curing. © 2018 by the American College of Prosthodontists.

Effects of different etching methods and bonding procedures on shear bond strength of orthodontic metal brackets applied to different CAD/CAM ceramic materials.

PubMed

Buyuk, S Kutalmış; Kucukekenci, Ahmet Serkan

2018-03-01

To investigate the shear bond strength (SBS) of orthodontic metal brackets applied to different types of ceramic surfaces treated with different etching procedures and bonding agents. Monolithic CAD/CAM ceramic specimens (N = 120; n = 40 each group) of feldspathic ceramic Vita Mark II, resin nanoceramic Lava Ultimate, and hybrid ceramic Vita Enamic were fabricated (14 × 12 × 3 mm). Ceramic specimens were separated into four subgroups (n = 10) according to type of surface treatment and bonding onto the ceramic surface. Within each group, four subgroups were prepared by phosphoric acid, hydrofluoric acid, Transbond XT primer, and Clearfill Ceramic primer. Mandibular central incisor metal brackets were bonded with light-cure composite. The SBS data were analyzed using three-way analysis of variance (ANOVA) and Tukey HSD tests. The highest SBS was found in the Vita Enamic group, which is a hybrid ceramic, etched with hydrofluoric acid and applied Transbond XT Adhesive primer (7.28 ± 2.49 MPa). The lowest SBS was found in the Lava Ultimate group, which is a resin nano-ceramic etched with hydrofluoric acid and applied Clearfill ceramic primer (2.20 ± 1.21 MPa). CAD/CAM material types and bonding procedures affected bond strength ( P < .05), but the etching procedure did not ( P > .05). The use of Transbond XT as a primer bonding agent resulted in higher SBS.

Effect finishing and polishing procedures on the surface roughness of IPS Empress 2 ceramic.

PubMed

Boaventura, Juliana Maria Capelozza; Nishida, Rodrigo; Elossais, André Afif; Lima, Darlon Martins; Reis, José Mauricio Santos Nunes; Campos, Edson Alves; de Andrade, Marcelo Ferrarezi

2013-01-01

To evaluate the surface roughness of IPS Empress 2 ceramic when treated with different finishing/polishing protocols. Sixteen specimens of IPS Empress 2 ceramic were made from wax patterns obtained using a stainless steel split mold. The specimens were glazed (Stage 0-S0, control) and divided into two groups. The specimens in Group 1 (G1) were finished/polished with a KG Sorensen diamond point (S1), followed by KG Sorensen siliconized points (S2) and final polishing with diamond polish paste (S3). In Group 2 (G2), the specimens were finished/polished using a Shofu diamond point (S1), as well as Shofu siliconized points (S2) and final polishing was performed using Porcelize paste (S3). After glazing (S0) and following each polishing procedure (S1, S2 or S3), the surface roughness was measured using TALYSURF Series 2. The average surface roughness results were analyzed using ANOVA followed by Tukey post-hoc tests (α = 0.01) RESULTS: All of the polishing procedures yielded higher surface roughness values when compared to the control group (S0). S3 yielded lower surface roughness values when compared to S1 and S2. The proposed treatments negatively affected the surface roughness of the glazed IPS Empress 2 ceramic.

Glass-ceramic coating material for the CO2 laser based sintering of thin films as caries and erosion protection.

PubMed

Bilandžić, Marin Dean; Wollgarten, Susanne; Stollenwerk, Jochen; Poprawe, Reinhart; Esteves-Oliveira, Marcella; Fischer, Horst

2017-09-01

The established method of fissure-sealing using polymeric coating materials exhibits limitations on the long-term. Here, we present a novel technique with the potential to protect susceptible teeth against caries and erosion. We hypothesized that a tailored glass-ceramic material could be sprayed onto enamel-like substrates to create superior adhesion properties after sintering by a CO 2 laser beam. A powdered dental glass-ceramic material from the system SiO 2 -Na 2 O-K 2 O-CaO-Al 2 O 3 -MgO was adjusted with individual properties suitable for a spray coating process. The material was characterized using X-ray fluorescence analysis (XRF), heating microscopy, dilatometry, scanning electron microscopy (SEM), grain size analysis, biaxial flexural strength measurements, fourier transform infrared spectroscopy (FTIR), and gas pycnometry. Three different groups of samples (each n=10) where prepared: Group A, powder pressed glass-ceramic coating material; Group B, sintered hydroxyapatite specimens; and Group C, enamel specimens (prepared from bovine teeth). Group B and C where spray coated with glass-ceramic powder. All specimens were heat treated using a CO 2 laser beam process. Cross-sections of the laser-sintered specimens were analyzed using laser scanning microscopy (LSM), energy dispersive X-ray analysis (EDX), and SEM. The developed glass-ceramic material (grain size d50=13.1mm, coefficient of thermal expansion (CTE)=13.310 -6 /K) could be spray coated on all tested substrates (mean thickness=160μm). FTIR analysis confirmed an absorption of the laser energy up to 95%. The powdered glass-ceramic material was successfully densely sintered in all sample groups. The coating interface investigation by SEM and EDX proved atomic diffusion and adhesion of the glass-ceramic material to hydroxyapatite and to dental enamel. A glass-ceramic material with suitable absorption properties was successfully sprayed and laser-sintered in thin films on hydroxyapatite as well as on bovine enamel. The presented novel technique of tooth coating with a dental glass-ceramic using a CO 2 -laser holds a great potential as a possible method to protect susceptible teeth against caries and erosion. Copyright © 2017 The Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Influence of a cellulosic ether carrier on the structure of biphasic calcium phosphate ceramic particles in an injectable composite material.

PubMed

Dupraz, A; Nguyen, T P; Richard, M; Daculsi, G; Passuti, N

1999-04-01

An injectable composite material based on biphasic calcium phosphate (BCP) and a nonionic cellulose ether has been elaborated for use in percutaneous surgery for spine fusion. This paper reports the characterization results of this material by spectroscopic techniques including X-ray diffraction (XRD), infrared spectroscopy (FTIR), X-ray photoelectron spectroscopy (XPS), scanning electron microscopy (SEM) fitted with an energy dispersive X-Ray analysis system and high-resolution transmission electron microscopy (HR-TEM). From FTIR and XPS results, it was observed that the adhesion between the polymer and the ceramic might be insured by oxygen bridging developed through an ionic bonding between calcium ions and (C-O) groups of the polymer. Moreover, XPS showed attraction of Ca2+ ions in the polymer matrix, while the ceramic surface was modified in a HPO4(2-) -rich layer. These results suggest a possible dissolution/precipitation process at the interface ceramic/polymer. HR-TEM observations supported this hypothesis, showing a light contrasted fringe at the surface of the ceramic grains in the composite paste. As well, changes in the XRD spectra could indicate a small decrease in the crystal size of the BCP powder through the contact to polymer solution. In addition, SEM observation showed a decrease of the initial BCP granulometry. Aggregates of 80-200 microm seemed to be mostly dissociated in micrograins. The ceramic grains were coated with and bonded between each other by the polymer matrix, which acted as spacer in between the ceramic grains, creating a macroporous-like material structure.

Reliability of scanning laser acoustic microscopy for detecting internal voids in structural ceramics

NASA Technical Reports Server (NTRS)

Roth, D. J.; Baaklini, G. Y.

1986-01-01

The reliability of 100 MHz scanning laser acoustic microscopy (SLAM) for detecting internal voids in sintered specimens of silicon nitride and silicon carbide was evaluated. The specimens contained artificially implanted voids and were positioned at depths ranging up to 2 mm below the specimen surface. Detection probability of 0.90 at a 0.95 confidence level was determined as a function of material, void diameter, and void depth. The statistical results presented for void detectability indicate some of the strengths and limitations of SLAM as a nondestructive evaluation technique for structural ceramics.

Magnetic Resonance Imaging of Gel-cast Ceramic Composites

DOE R&D Accomplishments Database

Dieckman, S. L.; Balss, K. M.; Waterfield, L. G.; Jendrzejczyk, J. A.; Raptis, A. C.

1997-01-16

Magnetic resonance imaging (MRI) techniques are being employed to aid in the development of advanced near-net-shape gel-cast ceramic composites. MRI is a unique nondestructive evaluation tool that provides information on both the chemical and physical properties of materials. In this effort, MRI imaging was performed to monitor the drying of porous green-state alumina - methacrylamide-N.N`-methylene bisacrylamide (MAM-MBAM) polymerized composite specimens. Studies were performed on several specimens as a function of humidity and time. The mass and shrinkage of the specimens were also monitored and correlated with the water content.

[Preparation and chromaticity properties of colored dental 3Y-TZP ceramics].

PubMed

Yi, Yuan-fu; Wang, Chen; Tian, Jie-mo; Liu, Hong-chen; Wen, Ning

2008-10-01

To obtain and investigate the chromaticity properties of colored dental 3Y-TZP ceramics with different colorant combinations. Colorant combinations were mixed with TZ-3Y-S powder, then the mixtures were compacted at 200 MPa using cold isostatic pressure, densely sintered at 1500 degrees C for 2 h forming 5 graded colored dental zirconia ceramics. Specimen were sectioned into 10 mm x 10 mm x 0.5 mm and 10 mm x l0 mmx 1 mm slices from the sintered blocks. Color measurement was performed under black background using spectrophotometer. The chromaticity properties were compared with that of the VITA In-Ceram YZ shade guide. Five colored dental zirconia ceramics were obtained. The lightness decreased gradually, and the chroma value increased gradually. The color differences of the two thickness specimens were little. The parameters of the color space were L*: 67.76-77.78; a*: -2.19-3.80; b*: 12.13-25.01, which was similar with that of the VITA In-Ceram YZ shade guide, while the lowest value of lightness was relatively higher than that of the VITA In-Ceram YZ shade guide. Colored 3Y-TZP dental ceramics are suitable for clinical use. There is a need to develop more darkness shaded zirconia dental ceramics.

Room temperature degradation of YBa2Cu3O(7-x) superconductors in varying relative humidity environments

NASA Technical Reports Server (NTRS)

Hooker, M. W.; Wise, S. A.; Carlberg, I. A.; Stephens, R. M.; Simchick, R. T.; Farjami, A.

1993-01-01

An aging study was performed to determine the stability of YBa2Cu3O(7-x) ceramics in humid environments at 20 C. In this study, fired ceramic specimens were exposed to humidity levels ranging from 30.5 to 100 percent for 2-, 4-, and 6-week time intervals. After storage under these conditions, the specimens were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), and electrical resistance measurements. At every storage condition evaluated, the fired ceramics were found to interact with H2O present in the surrounding environment, resulting in the decomposition of the YBa2Cu3O(7-x) phase. XRD data showed that BaCO3, CuO, and Y2BaCuO5 were present after aging and that the peak intensities of these impurity phases increased both with increasing humidity level and with increasing time of exposure. Additionally, SEM analyses of the ceramic microstructures after aging revealed the development of needle-like crystallites along the surface of the test specimens after aging. Furthermore, the superconducting transition temperature T(sub c) was found to decrease both with increasing humidity level and with increasing time of exposure. All the specimens aged at 30.5, 66, and 81 percent relative humidity exhibited superconducting transitions above 80 K, although these values were reduced by the exposure to the test conditions. Conversely, the specimens stored in direct contact with water (100 percent relative humidity) exhibited no superconducting transitions.

Effect of Silanization on Microtensile Bond Strength of Different Resin Cements to a Lithium Disilicate Glass Ceramic.

PubMed

Gré, Cristina Parise; de Ré Silveira, Renan C; Shibata, Shizuma; Lago, Carlo Tr; Vieira, Luiz Cc

2016-02-01

This study evaluated the influence of a silane-coupling agent on the bond strength of a self-adhesive cement and a conventional resin cement to a lithium disilicate glass ceramic. A total of eight ceramic blocks were fabricated and divided into four groups (n = 2). In groups 1 and 3, ceramic surfaces were etched with hydrofluoric acid 10% for 20 seconds, rinsed for 30 seconds, and air-dried. One layer of a silane agent was applied onto all ceramic specimens and air-dried for 30 seconds. In groups 2 and 4, ceramic surfaces were etched with hydrofluoric acid, rinsed, and air-dried without application of the silane-coupling agent. The ceramic blocks were bonded to a block of composite with a self-adhesive resin cement or with a conventional resin cement, according to the manufacturer's instructions. After 24 hours in distilled water at 37°C, the specimens were sectioned perpendicular to the bonding interface area to obtain beams with a bonding area of 0.8 mm(2) and submitted to a microtensile bond strength test at a crosshead speed of 0.5 mm/min. Data were statistically analyzed with one-way analysis of variance and the Games-Howell post hoc test (p = 0.05). Fractured specimens were examined under optical microscopy at 40x magnification. Silanization resulted in higher microtensile bond strength compared to groups without silane. No significant differences were found between the conventional resin cement and the self-adhesive resin cement with silane agent (p = 0.983), and without silane agent (p = 0.877). Silanization appears to be crucial for resin bonding to a lithium disilicate-based ceramic, regardless of the resin cement used. The self-adhesive resin cement performed as well as the conventional resin cement. Applying one layer of a silane-coupling agent after etching the ceramic surface with hydrofluoric acid 10% enhanced the bond strength between resin cements and a glass ceramic.

A comparative study of progressive wear of four dental monolithic, veneered glass-ceramics.

PubMed

Zhang, Zhenzhen; Yi, Yuanping; Wang, Xuesong; Guo, Jiawen; Li, Ding; He, Lin; Zhang, Shaofeng

2017-10-01

This study evaluated the wear performance and wear mechanisms of four dental glass-ceramics, based on the microstructure and mechanical properties in the progressive wear process. Bar (N = 40, n = 10) and disk (N = 32, n = 8) specimens were prepared from (A) lithium disilicate glass-ceramic (LD), (B) leucite reinforced glass-ceramic (LEU), (C) feldspathic glass-ceramic (FEL), and (D) fluorapatite glass-ceramic (FLU). The bar specimens were tested for three-point flexural strength, hardness, fracture toughness and elastic modulus. The disk specimens paired with steatite antagonists were tested in a pin-on-disk tribometer with 10N up to 1000,000 wear cycles. The wear analysis of glass-ceramics was performed using a 3D profilometer after every 200,000 wear cycles. Wear loss of steatite antagonists was calculated by measuring the weight and density using sensitive balance and Archimedes' method. Wear morphologies and microstructures were analyzed by scanning electron microscopy (SEM). The crystalline phase compositions were determined using X-ray diffraction (XRD). One-way analysis of variance (ANOVA) was used to analyze the data. Multiple pair-wise comparison of means was performed by Tukey's post-hoc test. LD showed the highest fracture toughness, flexural strength, elastic modulus and crystallinity, followed by LEU and FEL, and FLU showed the lowest. However, the hardness of LD was lower than all the other three types of ceramics. For steatite antagonists, LD produced the least wear loss of antagonist, followed by LEU and FEL, and FLU had the most wear loss. For glass-ceramic materials, LD exhibited similar wear loss as LEU, but more than FLU and FEL did. Moreover, fracture occurred on the wear surface of FLU. In the progressive wear process, veneering porcelains showed better wear resistance but fluorapatite veneering porcelains appeared fracture surface. Monolithic lithium disilicate glass-ceramics with higher mechanical properties showed more wear loss, however, they did not fracture and produced less wear loss of antagonists. Copyright © 2017 Elsevier Ltd. All rights reserved.

Fracture loads of all-ceramic crowns under wet and dry fatigue conditions.

PubMed

Borges, Gilberto A; Caldas, Danilo; Taskonak, Burak; Yan, Jiahau; Sobrinho, Lourenco Correr; de Oliveira, Wildomar José

2009-12-01

The aim of this study was to test the hypothesis that fracture loads of fatigued dental ceramic crowns are affected by testing environment and luting cement. One hundred and eighty crowns were prepared from bovine teeth using a lathe. Ceramic crowns were prepared from three types of ceramic systems: an alumina-infiltrated ceramic, a lithia-disilicate-based glass ceramic, and a leucite-reinforced ceramic. For each ceramic system, 30 crowns were cemented with a composite resin cement, and the remaining 30 with a resin-modified glass ionomer cement. For each ceramic system and cement, ten specimens were loaded to fracture without fatiguing. A second group (n = 10) was subjected to cyclic fatigue and fracture tested in a dry environment, and a third group (n = 10) was fatigued and fractured in distilled water. The results were statistically analyzed using one-way ANOVA and Tukey HSD test. The fracture loads of ceramic crowns decreased significantly after cyclic fatigue loading (p

In-situ High Temperature Phase Transformations in Ceramics

DTIC Science & Technology

2009-07-28

microscopy - SEM and transmission electron microscopy - TEM), have identified important microstructural considerations, such as the critical ...particularly with judicial design of the critical particle size and microstructure.12, 47, 48 Likewise, preliminary work indicates the possibility of high...toughening of fiber reinforced, fibrous monolithic or laminated ceramic matrix composites.49, 50 enstatite was above a 7 μm critical grain size

Hexagonal OsB 2: Sintering, microstructure and mechanical properties

DOE PAGES

Xie, Zhilin; Lugovy, Mykola; Orlovskaya, Nina; ...

2015-02-07

In this study, the metastable high pressure ReB 2-type hexagonal OsB 2 bulk ceramics was produced by spark plasma sintering. The phase composition, microstructure, and mechanical behavior of the sintered OsB 2 were studied by X-ray diffraction, optical microscopy, TEM, SEM, EDS, and nanoindentation. The produced ceramics was rather porous and contained a mixture of hexagonal (~80 wt.%) and orthorhombic (~20 wt.%) phases as identified by X-ray diffraction and EBSD analysis. Two boron-rich phases, which do not contain Os, were also identified by TEM and SEM/EDS analysis. Nanoindentation measurements yielded a hardness of 31 ± 9 GPa and Young’s modulusmore » of 574 ± 112 GPa, indicating that the material is rather hard and very stiff; but, it is very prone to crack formation and propagation, which is indicative of a very brittle nature of this material. Improvements in the sintering regime are required in order to produce dense, homogeneous and single phase hexagonal OsB 2 bulk ceramics.« less

The plasma electrolytic oxidation micro-discharge channel model and its microstructure characteristic based on Ti tracer

NASA Astrophysics Data System (ADS)

Gao, Fangyuan; Hao, Li; Li, Guang; Xia, Yuan

2018-02-01

This study focuses on the individual discharge channel of ceramic coating prepared by plasma electrolytic oxidation (PEO), and attempts to reveal the mechanism of breakdown discharge at low voltage. Titanium (Ti) was employed as a substrate with the layer of aluminum deposited on it (aluminized Ti). The shape and microstructure of the discharge channels in PEO coatings were investigated using transmission electron microscope (TEM) and scanning electron microscopy (SEM). A schematic model of the individual discharge channel was proposed based on Ti tracer method. The shape of the discharge channel was mainly cylinder-shaped in the compact coating, with a groove-like oxidation region existed at the coating/substrate interface. In the groove-like oxidation region, the phase composition mainly composed of amorphous and mixed polycrystalline (aluminum titanate and mullite). β-Al2O3 was found in the ceramic coating. TEM morphology showed that nanometer sized micro channels existed in the ceramic coatings.

Spectrophotometric evaluation of the influence of different backgrounds on the color of glass-infiltrated ceramic veneers.

PubMed

Charisis, Dimitrios; Koutayas, Spiridon-Oumvertos; Kamposiora, Photini; Doukoudakis, Asterios

2006-08-01

The purpose of this spectrophotometric study was to evaluate the influence of different color backgrounds on Vita In-Ceram (Vident) glass-infiltrated ceramic veneers. A total of 50 color background disks were fabricated from Vitadur Alpha 2M2 (n=30) and 5M1 (n=20) dentin porcelain (Vi-dent). Ceramic veneer disks were fabricated from In-Ceram Spinell (n=20) or In-Ceram Alumina (n=20) glass-infiltrated core veneered using Vitadur Alpha 2M2 dentin porcelain. In addition, 10 ceramic veneer disks were fabricated from feldspathic dentin porcelain Vitadur Alpha 2M2. The ceramic veneer specimens were bonded onto the color background specimens using dual-curing luting composite cement, creating the following groups (each n=10): S2M2 (Spinell/2M2), S5M1 (Spinell/5M1), A2M2 (Alumina/2M2), A5M1 (Alumina/5M1), and control (Vitadur Alpha/2M2). L*a*b* color coordinates were measured five times for each specimen using a Vita Easyshade (Vident) spectrophotometer. Mean color differences (deltaE) between each study group and the control group were: 3.79 for S2M2; 7.24 for S5M1; 5.86 for A2M2, and 7.32 for A5M1. Two-way ANOVA showed statistically significant differences in deltaE between all groups. However, a t test revealed that the statistically significant differences only existed between groups S2M2/S5M1, A2M2/A5M1, and S2M2/A2M2. The results suggest that vacuum infiltration with a translucent glass provides the Spinell and Alumina ceramic veneers with increased semi-translucency, which makes them highly influenced by discolored backgrounds. In-Ceram Spinell glass-infiltrated ceramic veneers could be considered as an alternative to conventional feldspathic veneers for the restoration of nondiscolored teeth. Although Spinell and Alumina ceramic veneers could enhance the final color establishment of discolored teeth, the results would not be clinically acceptable.

Proceedings of the Asilomar Conference on Polymers (9th) Held on February 9-12, 1986 at Asilomar, California.

DTIC Science & Technology

1986-06-01

reticulated vitreous carbon material r ~ y n uniformity anc. material distribution. The material s * -p~s~Oro prismatic specimens. Four specimens had...with carbon fiber, hydroxylapatite ceramic (HA), tri-calcium phosphate ceramic (TCP), various organic acids, and calcium sulphate, we have been able to...filamentous carbon device coated with an absorbable polymer to prevent * premature fragmentation of the carbon fiber. Fracture repair has been effected

CARES/Life Software for Designing More Reliable Ceramic Parts

NASA Technical Reports Server (NTRS)

Nemeth, Noel N.; Powers, Lynn M.; Baker, Eric H.

1997-01-01

Products made from advanced ceramics show great promise for revolutionizing aerospace and terrestrial propulsion, and power generation. However, ceramic components are difficult to design because brittle materials in general have widely varying strength values. The CAPES/Life software eases this task by providing a tool to optimize the design and manufacture of brittle material components using probabilistic reliability analysis techniques. Probabilistic component design involves predicting the probability of failure for a thermomechanically loaded component from specimen rupture data. Typically, these experiments are performed using many simple geometry flexural or tensile test specimens. A static, dynamic, or cyclic load is applied to each specimen until fracture. Statistical strength and SCG (fatigue) parameters are then determined from these data. Using these parameters and the results obtained from a finite element analysis, the time-dependent reliability for a complex component geometry and loading is then predicted. Appropriate design changes are made until an acceptable probability of failure has been reached.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kawasaki, Tadahiro; PRESTO-JST, 4-1-8 Honcho, Kawaguchi, Saitama 332-0012; Ueda, Kouta

We have developed an improved, windowed type environmental-cell (E-cell) transmission electron microscope (TEM) for in situ observation of gas-solid interactions, such as catalytic reactions at atmospheric pressure. Our E-cell TEM includes a compact E-cell specimen holder with mechanical stability, resulting in smoother introduction of the desired gases compared with previous E-cell TEMs. In addition, the gas control unit was simplified by omitting the pressure control function of the TEM pre-evacuation chamber. This simplification was due to the successful development of remarkably tough thin carbon films as the window material. These films, with a thickness of <10 nm, were found tomore » withstand pressure differences >2 atm. Appropriate arrangement of the specimen position inside the E-cell provided quantitatively analyzable TEM images, with no disturbances caused by the windowed films. As an application, we used this E-cell TEM to observe the dynamic shape change in a catalytic gold nanoparticle supported on TiO{sub 2} during the oxidation of CO gas.« less

An ultrahigh vacuum multipurpose specimen chamber with sample introduction system for in situ transmission electron microscopy investigations

NASA Technical Reports Server (NTRS)

Heinemann, K.; Poppa, H.

1986-01-01

A commercial transmission electron microscope (TEM), with flat-plate upper pole piece configuration of the objective lens, and top-entry specimen introduction was modified by introducing an ultrahigh vacuum (UHV) specimen chamber for in situ TEM experimentation. The pumping and design principles and special features of this UHV chamber, which makes it possible to obtain 5 x 10 to the -10th mbar pressure at the site of the specimen, while maintaining the airlock system that allows operation in the 10 to the -10th mbar range within 15 min after specimen change, are described. Design operating pressures and image quality (resolution of metal particles smaller than 1 nm in size) were achieved. Schematic drawings and design dimensions are included.

Improved Tensile Test for Ceramics

NASA Technical Reports Server (NTRS)

Osiecki, R. A.

1982-01-01

For almost-nondestructive tensile testing of ceramics, steel rod is bonded to sample of ceramic. Assembly is then pulled apart in conventional tensile-test machine. Test destroys only shallow surface layer which can be machined away making specimen ready for other uses. Method should be useful as manufacturing inspection procedure for low-strength brittle materials.

Comparative analysis of two measurement methods for marginal fit in metal-ceramic and zirconia posterior FPDs.

PubMed

Gonzalo, Esther; Suárez, María J; Serrano, Benjamin; Lozano, José F L

2009-01-01

The purpose of this study was to compare two measurement methods for the external marginal fit of zirconia posterior fixed partial dentures (FPDs) fabricated using computer-aided design/manufacturing technology and metal-ceramic posterior FPDs fabricated using the conventional lost-wax technique. The null hypothesis was that there would be no differences between the measurement methods. Forty standardized steel specimens were prepared to receive posterior three-unit FPDs. Specimens were divided into four groups (n = 10): (1) metal-ceramic, (2) Procera Bridge Zirconia, (3) Lava AllCeramic System, and (4) Vita In-Ceram YZ 2000. All FPDs were luted with glass-ionomer cement (Ketac Cem EasyMix, 3M ESPE). Two measurement methods were used to analyze marginal fit: an image analysis (IA) program and a scanning electron microscope (SEM) (JEOL JSM-6400) with magnifications of 340 and 31,000, respectively. Marginal fit was measured at the same point on each abutment. Significant interaction was observed between measurement method and material (P = .0019). Therefore, the measurement method is not independent of the restoration material. Differences among groups were observed for IA (P = .0001) and SEM (P = .0013). Significant differences were observed for the Procera (P = .0050) and metal-ceramic (P = .0039) specimen groups when both measurement methods were evaluated separately. Accuracy of fit achieved by the four groups analyzed was within the range of clinical acceptance, yielding Procera Bridge Zirconia to have the best marginal fit using both measurement methods.

Synthesis and Characterization of BiCaSrCuO and BiSnCaSrCuO superconducting Ceramics

DTIC Science & Technology

1988-09-20

0-1-2-2 2 2-1-1-2-2 3 1-0-1-1-2 4 2-0-1-2-2 SUPERCONDUCTING CERAMICS Magnetic Measurements Quantitative magnetic measurements were made using a...Transition TemPerature and Superconducting Volume Fractions The magnetic data for the four samples studied show J. H. MILLER, JR., ET. AL. relatively broad... SUPERCONDUCTING CERAMICS TABLE II Transition temperatures and percent bulk diamagnetism Sample Tc(ZFC) Tc (FC) T,(onset) T.(zero) %(ZFC) %(f C) 1 77.6

Confocal examination of subsurface cracking in ceramic materials.

PubMed

Etman, Maged K

2009-10-01

The original ceramic surface finish and its microstructure may have an effect on crack propagation. The purpose of this study was to investigate the relation between crack propagation and ceramic microstructure following cyclic fatigue loading, and to qualitatively evaluate and quantitatively measure the surface and subsurface crack depths of three types of ceramic restorations with different microstructures using a Confocal Laser Scanning Microscope (CLSM) and Scanning Electron Microscope (SEM). Twenty (8 x 4 x 2 mm(3)) blocks of AllCeram (AC), experimental ceramic (EC, IPS e.max Press), and Sensation SL (SSL) were prepared, ten glazed and ten polished of each material. Sixty antagonist enamel specimens were made from the labial surfaces of permanent incisors. The ceramic abraders were attached to a wear machine, so that each enamel specimen presented at 45 degrees to the vertical movement of the abraders, and immersed in artificial saliva. Wear was induced for 80K cycles at 60 cycles/min with a load of 40 N and 2-mm horizontal deflection. The specimens were examined for cracks at baseline, 5K, 10K, 20K, 40K, and 80K cycles. Twenty- to 30-microm deep subsurface cracking appeared in SSL, with 8 to 10 microm in AC, and 7 microm close to the margin of the wear facets in glazed EC after 5K cycles. The EC showed no cracks with increasing wear cycles. Seventy-microm deep subsurface cracks were detected in SSL and 45 microm in AC after 80K cycles. Statistically, there was significant difference among the three materials (p < 0.05). Bonferroni multiple comparison of means test confirmed the ANOVA test and showed that there was no statistical difference (p > 0.05) in crack depth within the same ceramic material with different surface finishes. The ceramic materials with different microstructures showed different patterns of subsurface cracking.

[Comparative study of 4 types of luting cements on shear bond strength of Zirconia ceramics to dentin].

PubMed

Yin, Bao-di; Zhang, Xian-fang; Zheng, Hu; Han, Dong-wei

2010-04-01

To investigate the adequate luting cements for zirconia ceramics to dentin. Blocks of sintered zirconia ceramics were randomly divided into 4 groups with 8 slices in each. After saliva immersion,airborne-particle abraded ceramic specimens were cleaned with phosphoric acid gel(containing 35% phosphoric acid) and then bonded to dentin with these four kinds of luting cements. After preserved in 37 degrees centigrade distilled water for 24 hours, the shear bonding strength of these specimens was tested and the data was analyzed with SPSS12.0 software package. The Multilink Automix could attain the highest shear bonding strength and the 3M RelyXTM Unicem AplicapTM could attain higher shear bonding strength, which were both significantly higher than in the Tokuso Ionomer and Shofu Polycarboxylate Cement groups(P<0.05). Total etching resin luting cement is an ideal option to the bonding of zirconia ceramics and can provide a strong bonding.

Characterization of the bioactive and mechanical behavior of dental ceramic/sol-gel derived bioactive glass mixtures.

PubMed

Abbasi, Zahra; Bahrololoum, Mohammad E; Bagheri, Rafat; Shariat, Mohammad H

2016-02-01

Dental ceramics can be modified by bioactive glasses in order to develop apatite layer on their surface. One of the benefits of such modification is to prolong the lifetime of the fixed dental prosthesis by preventing the formation of secondary caries. Dental ceramic/sol-gel derived bioactive glass mixture is one of the options for this modification. In the current study, mixtures of dental ceramic/bioactive glass with different compositions were successfully produced. To evaluate their bioactive behavior, prepared samples were immersed in a simulated body fluid at various time intervals. The prepared and soaked specimens were characterized using Fourier transform infrared spectroscopy, X-ray diffractometry and scanning electron microscopy. Since bioactive glasses have deleterious effects on the mechanical properties of dental ceramics, 3-point bending tests were used to evaluate the flexural strength, flexural strain, tangent modulus of elasticity and Weibull modulus of the specimens in order to find the optimal relationship between mechanical and bioactive properties. Copyright © 2015 Elsevier Ltd. All rights reserved.

Effect of Home Bleaching on the Translucency of CAD/CAM Systems.

PubMed

Karci, Muhammet; Demir, Necla

2017-11-10

To evaluate the effect of a home bleaching agent (Opalescence PF) on the translucency of CAD/CAM ceramic systems. The 28 sintered ceramic specimens (IPS Empress CAD and IPS e.max CAD; 15 mm long, 10 mm wide, 1 mm thick) were divided into two subgroups as control and bleaching groups (n = 7). Carbamide peroxide (CP), 16%, home bleaching agent was applied onto the surface of each specimen for 6 hours per day for 7 days. A spectrophotometer (VITA Easyshade Advance) was used to measure the CIE L * a * b * coordinates and the reflectance value (Y) of the specimens on white and black backgrounds. The translucency parameter (TP), contrast ratio (CR), and opalescence parameter (OP) of the specimens were calculated. The data were statistically analyzed using Kolmogorov-Smirnov, one-way ANOVA, Tukey's test, and Pearson's correlation. Statistically significant differences in the TP values after 16% CP bleaching treatment were observed (p ˂ 0.05); however, no significant differences were found in the OP and CR values after the surface treatment (p ˃ 0.05). According to our study, patients who have all-ceramic restorations in their mouths should be careful when using home bleaching agents, because whitening agents can affect the translucency of all-ceramic restorations such as e.max CAD and Empress CAD. © 2017 by the American College of Prosthodontists.

Effect finishing and polishing procedures on the surface roughness of IPS Empress 2 ceramic

PubMed Central

Nishida, Rodrigo; Elossais, André Afif; Lima, Darlon Martins; Reis, José Mauricio Santos Nunes; Campos, Edson Alves; de Andrade, Marcelo Ferrarezi

2013-01-01

Objective. To evaluate the surface roughness of IPS Empress 2 ceramic when treated with different finishing/polishing protocols. Materials and methods. Sixteen specimens of IPS Empress 2 ceramic were made from wax patterns obtained using a stainless steel split mold. The specimens were glazed (Stage 0–S0, control) and divided into two groups. The specimens in Group 1 (G1) were finished/polished with a KG Sorensen diamond point (S1), followed by KG Sorensen siliconized points (S2) and final polishing with diamond polish paste (S3). In Group 2 (G2), the specimens were finished/polished using a Shofu diamond point (S1), as well as Shofu siliconized points (S2) and final polishing was performed using Porcelize paste (S3). After glazing (S0) and following each polishing procedure (S1, S2 or S3), the surface roughness was measured using TALYSURF Series 2. The average surface roughness results were analyzed using ANOVA followed by Tukey post-hoc tests (α = 0.01) Results. All of the polishing procedures yielded higher surface roughness values when compared to the control group (S0). S3 yielded lower surface roughness values when compared to S1 and S2. Conclusions. The proposed treatments negatively affected the surface roughness of the glazed IPS Empress 2 ceramic. PMID:22724660

Effects of soldering and laser welding on bond strength of ceramic to metal.

PubMed

Aladağ, Akin; Cömlekoğlu, M Erhan; Dündar, Mine; Güngör, M Ali; Artunç, Celal

2011-01-01

Welding or soldering of metal frameworks negatively affects the overall bond strength between the veneering ceramic and metal. The purpose of this study was to evaluate the effect of soldering and laser-welding procedures on the bond strength between ceramic and metal. Thirty Ni-based metal specimens (Wiron 99) (8 × 4 × 4 mm) were fabricated and divided into 3 groups; soldered (S), laser welded (L), and control (untreated cast alloy) (n=10). In S and L specimens, a notch (1 × 1.5 mm) was prepared longitudinally on the surface of each specimen and filled with compatible alloy (Wiron soldering rods and Wiroweld NC, respectively). Vickers hardness measurements were made after polishing the surfaces with a metallographic polishing kit. A veneering ceramic (VITA VMK 95) was vibrated, condensed in a mold, and fired on the metal frameworks. The specimens were sectioned in 2 axes to obtain nontrimmed bar specimens with a bonding area of approximately 1 mm². Forty bars per block were obtained. Each bar was subjected to microtensile bond strength (μTBS) testing with a crosshead speed of 1 mm/min. The μTBS data (MPa) were recorded, and SEM was used for failure analysis of the tested bars. The measurements were statistically analyzed using a 1-way ANOVA and Tamhane tests (α=.05). The mean differences in μTBS of veneering ceramic to soldered (10.4 ±2.4 MPa) and laser-welded (11.7 ±1.3 MPa) metal surfaces were not significantly different and were significantly lower than that of the cast alloy (25.4 ±3.6 MPa) (P<.05). The mean Vickers hardness of cast alloy was significantly higher (236 ±17 HV) than soldered (114 ±9 HV) and laser-welded groups (129 ±11 HV) (P<.05). Soldering and laser welding significantly decreased the μTBS of a veneering ceramic to a base metal alloy. Copyright © 2011 The Editorial Council of the Journal of Prosthetic Dentistry. Published by Mosby, Inc. All rights reserved.

Effect of surface modifications on the bond strength of zirconia ceramic with resin cement resin.

PubMed

Hallmann, Lubica; Ulmer, Peter; Lehmann, Frank; Wille, Sebastian; Polonskyi, Oleksander; Johannes, Martina; Köbel, Stefan; Trottenberg, Thomas; Bornholdt, Sven; Haase, Fabian; Kersten, Holger; Kern, Matthias

2016-05-01

Purpose of this in vitro study was to evaluate the effect of surface modifications on the tensile bond strength between zirconia ceramic and resin. Zirconia ceramic surfaces were treated with 150-μm abrasive alumina particles, 150-μm abrasive zirconia particles, argon-ion bombardment, gas plasma, and piranha solution (H2SO4:H2O2=3:1). In addition, slip casting surfaces were examined. Untreated surfaces were used as the control group. Tensile bond strengths (TBS) were measured after water storage for 3 days or 150 days with additional 37,500 thermal cycling for artificial aging. Statistical analyses were performed with 1-way and 3-way ANOVA, followed by comparison of means with the Tukey HSD test. After storage in distilled water for three days at 37 °C, the highest mean tensile bond strengths (TBS) were observed for zirconia ceramic surfaces abraded with 150-μm abrasive alumina particles (TBS(AAP)=37.3 MPa, TBS(CAAP)=40.4 MPa), and 150-μm abrasive zirconia particles (TBS(AZP)=34.8 MPa, TBS(CAZP)=35.8 MPa). Also a high TBS was observed for specimens treated with argon-ion bombardment (TBS(BAI)=37.8 MPa). After 150 days of storage, specimens abraded with 150-μm abrasive alumina particles and 150-μm abrasive zirconia particles revealed high TBS (TBS(AAP)=37.6 MPa, TBS(CAAP)=33.0 MPa, TBS(AZP)=22.1 MPa and TBS(CAZP)=22.8 MPa). A high TBS was observed also for specimens prepared with slip casting (TBS(SC)=30.0 MPa). A decrease of TBS was observed for control specimens (TBS(UNT)=12.5 MPa, TBS(CUNT)=9.0 MPa), specimens treated with argon-ion bombardment (TBS(BAI)=10.3 MPa) and gas plasma (TBS(GP)=11.0 MPa). A decrease of TBS was observed also for specimens treated with piranha solution (TBS(PS)=3.9 MPa, TBS(CPS)=4.1 MPa). A significant difference in TBS after three days storage was observed for specimens treated with different methods (p<0.001). Thermal cycling significantly reduced TBS for all groups (p<0.001) excluding groups: AAP(p>0.05), CAAP(p>0.05) and SC(p>0.05). However, the failure patterns of debonded specimens prepared with 150-μm abrasive zirconia particles were 96.7% cohesive. Treatment of zirconia ceramic surfaces with abrasive zirconia particles is a promising method to increase the tensile bond strength without significant damage of the ceramic surface itself. An alternative promising method is slip casting. Copyright © 2016 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

An in vitro study of the effect of different restorative materials on the reliability of a veneering porcelain.

PubMed

Anderson, Matthew R; Chung, Kwok-Hung; Flinn, Brian D; Raigrodski, Ariel J

2013-12-01

Implant-supported, porcelain veneered restorations experience a greater rate of porcelain fracture than tooth-supported restorations. For completely edentulous patients, one approach to minimizing porcelain fracture is to use acrylic resin in the mandible, although its efficacy is unknown. The purpose of this study was to evaluate the reliability of a veneering porcelain fatigued with different restorative materials in vitro. Fifty-nine veneering porcelain disk specimens were fabricated by layering veneering porcelain on nickel-chromium base metal alloy disks. Four groups of different indenter materials fatigued the porcelain specimens: group WC, tungsten carbide served as a control; group FC, pressed leucite glass ceramic; group NHC, nanohybrid composite resin denture tooth; and group AR, unfilled acrylic resin denture tooth. Porcelain specimens were randomly divided into 4 groups (n=14). A step-stress accelerated life-testing model was used. Use-level probability Weibull plots were generated, and the reliability of each group was estimated for a theoretical completion of 50 000 cycles at 150 N. Nanohybrid composite resin and unfilled acrylic resin denture tooth groups had higher reliability than tungsten carbide and leucite glass ceramic groups. No significant differences existed between the reliability of the tungsten carbide and leucite glass ceramic groups and the nanohybrid composite resin and acrylic resin denture tooth groups. Veneering porcelain disk specimens fatigued with the unfilled acrylic resin and nanohybrid composite resin denture tooth indenters exhibited higher reliability than the specimens fatigued with either the tungsten carbide or leucite glass ceramic indenters. All of the veneering porcelain disk specimens failed with the same mode of fracture, although the surface posttest exhibited different fracture characteristics among specimens fatigued with the 4 different materials. Copyright © 2013 Editorial Council for the Journal of Prosthetic Dentistry. Published by Mosby, Inc. All rights reserved.

Mechanical fatigue degradation of ceramics versus resin composites for dental restorations.

PubMed

Belli, Renan; Geinzer, Eva; Muschweck, Anna; Petschelt, Anselm; Lohbauer, Ulrich

2014-04-01

For posterior partial restorations an overlap of indication exists where either ceramic or resin-based composite materials can be successfully applied. The aim of this study was to compare the fatigue resistance of modern dental ceramic materials versus dental resin composites in order to address such conflicts. Bar specimens of five ceramic materials and resin composites were produced according to ISO 4049 and stored for 14 days in distilled water at 37°C. The following ceramic materials were selected for testing: a high-strength zirconium dioxide (e.max ZirCAD, Ivoclar), a machinable lithium disilicate (e.max CAD, Ivoclar), a pressable lithium disilicate ceramic (e-max Press, Ivoclar), a fluorapatite-based glass-ceramic (e.max Ceram, Ivoclar), and a machinable color-graded feldspathic porcelain (Trilux Forte, Vita). The composite materials selected were: an indirect machinable composite (Lava Ultimate, 3M ESPE) and four direct composites with varying filler nature (Clearfil Majesty Posterior, Kuraray; GrandioSO, Voco; Tetric EvoCeram, Ivoclar-Vivadent; and CeramX Duo, Dentsply). Fifteen specimens were tested in water for initial strength (σin) in 4-point bending. Using the same test set-up, the residual flexural fatigue strength (σff) was determined using the staircase approach after 10(4) cycles at 0.5 Hz (n=25). Weibull parameters σ0 and m were calculated for the σin specimens, whereas the σff and strength loss in percentage were obtained from the fatigue experiment. The zirconium oxide ceramic showed the highest σin and σff (768 and 440 MPa, respectively). Although both lithium disilicate ceramics were similar in the static test, the pressable version showed a significantly higher fatigue resistance after cyclic loading. Both the fluorapatite-based and the feldspathic porcelain showed equivalent initial and cyclic fatigue properties. From the composites, the highest filled direct material Clearfil Majesty Posterior showed superior fatigue performance. From all materials, e.max Press and Clearfil Majesty Posterior showed the lowest strength loss (29.6% and 32%, respectively), whereas the other materials lost between 41% and 62% of their flexural strength after cyclic loading. Dental ceramics and resin composite materials show equivalent fatigue strength degradation at loads around 0.5σin values. Apart from the zirconium oxide and the lithium disilicate ceramics, resin composites generally showed better σff after 10,000 cycles than the fluorapatite glass-ceramic and the feldspathic porcelain. Resin composite restorations may be used as an equivalent alternative to glass-rich-ceramic inlays regarding mechanical performance. Copyright © 2014 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Effects of surface-finishing protocols on the roughness, color change, and translucency of different ceramic systems.

PubMed

Akar, Gülcan Coşkun; Pekkan, Gürel; Çal, Ebru; Eskitaşçıoğlu, Gürcan; Özcan, Mutlu

2014-08-01

Surface-finishing protocols have a mechanical impact on ceramic surfaces that could eventually affect surface topography and light scattering. An optimum protocol is needed to avoid damaging the optical properties of ceramics. The purpose of this study was to determine the effects of different surface-finishing protocols on the surface roughness, color change, and translucency of ceramic and metal ceramic restorations. Standardized disk-shaped specimens (1.5 × 10 mm, n=128) were fabricated from 3 different ceramic core materials (aluminum oxide [Al2O3]-AL, zirconium oxide [ZrO2]-ZR, lithium disilicate [Li2Si2O5]-LIT), veneered (V) with dentin ceramics (n=32 per group), and placed in the following groups: ALV, ZRV, and LITV. The metal ceramic group acted as the control (n=32). Four different surface-finishing methods were tested. Airborne-particle abrasion with 50 μm Al2O3, polishing with adjustment kit, polishing with adjustment kit plus diamond polishing paste, and autoglazing (n=8 subgroup) were applied on the veneering ceramics. The specimens were analyzed with a profilometer for surface roughness, and color change and translucency were measured with a clinical spectrophotometer. Statistical analyses were performed with 1-way ANOVA and the Tukey honest significant difference tests (α=.05). Specimens treated with the airborne particle abrasion method showed significantly higher mean profilometer for surface roughness values in all groups (P<.05). The polishing with adjustment kit and autoglazing methods revealed statistically similar surface roughness values in all groups (P>.05). With the diamond polishing paste method, lower surface roughness values were achieved in the ZRV and metal ceramic groups acted as the control groups. Different surface-finishing methods affected the color change of the ceramic systems, except for ZRV. Surface-finishing protocols significantly affected the translucency values of the ALV, LITV, and metal ceramic groups (P<.05). No single surface-finishing protocol can be recommended to obtain the smoothest surface and the least color change without affecting translucency for the ceramics tested. The airborne-particle abrasion protocol created rougher surfaces and decreased translucency, and color change in zirconia was not affected by the finishing protocols. Copyright © 2014 Editorial Council for the Journal of Prosthetic Dentistry. Published by Elsevier Inc. All rights reserved.

Characterization of BOR-60 Irradiated 14YWT-NFA1 Tubes

DOE Office of Scientific and Technical Information (OSTI.GOV)

Saleh, Tarik A.; Maloy, Stuart Andrew; Aydogan, Eda

2017-02-15

Tubes of FCRD 14YWT-NFA1 Alloy were placed in the BOR-60 reactor and irradiated under a fast flux neutron environment to two conditions: 7 dpa at 360-370 °C and 6 dpa at 385-430 °C. Small sections of the tube were cut and sent to UC Berkeley for nanohardness testing and focused ion beam (FIB) milling of TEM specimens. FIB specimens were sent back to LANL for final FIB milling and TEM imaging. Hardness data and TEM images are presented in this report. This is the first fast reactor neutron irradiated information on the 14YWT-NFA1 alloy.

Examination of ceramic/enamel interfacial debonding using acoustic emission and optical coherence tomography.

PubMed

Lin, Chun-Li; Kuo, Wen-Chuan; Chang, Yen-Hsiang; Yu, Jin-Jie; Lin, Yun-Chu

2014-08-01

This study investigates monitored micro-crack growth and damage in the ceramic/enamel adhesive interface using the acoustic emission (AE) technique with optical coherence tomography (OCT) under fatigue shear testing. Shear bond strength (SBS) was measured first with eight prepared ceramic/enamel adhesive specimens under static loads. The fatigue shear testing was performed with three specimens at each cyclic load according to a modified ISO14801 method, applying at 80%, 75%, 70%, and 65% of the SBS to monitor interface debonding. The number of cycles at each load was recorded until ceramic/enamel adhesive interface debonding occurred. The AE technique was used to detect micro-crack signals in static and fatigue shear bond tests. The results showed that the average SBS value in the static tests was 18.07 ± 1.72 MPa (mean ± standard deviation), expressed in Newton's at 56.77 ± 5.40N. The average number of fatigue cycles in which ceramic/enamel interface damage was detected in 80%, 75%, 70% and 65% of the SBS were 41, 410, 8141 and 76,541, respectively. The acoustic behavior varied according to the applied load level. Events were emitted during 65% and 70% fatigue tests. A good correlation was observed between the crack location in OCT images and the number of AE signal hits. The AE technique combined with OCT images as a pre-clinical assessment tool to determine the integrity of cemented load bearing restored ceramic material. Sustainable cyclic load stresses in ceramic/enamel bonded specimens were substantially lower than the measured SBS. Predicted S-N curve showed that the maximum endured load was 10.98 MPa (about 34.48 N) passing 10(6) fatigue cyclic. Copyright © 2014 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Effect of annealing procedure on the bonding of ceramic to cobalt-chromium alloys fabricated by rapid prototyping.

PubMed

Tulga, Ayca

2018-04-01

An annealing procedure is a heat treatment process to improve the mechanical properties of cobalt-chromium (Co-Cr) alloys. However, information is lacking about the effect of the annealing process on the bonding ability of ceramic to Co-Cr alloys fabricated by rapid prototyping. The purpose of this in vitro study was to evaluate the effects of the fabrication techniques and the annealing procedure on the shear bond strength of ceramic to Co-Cr alloys fabricated by different techniques. Ninety-six cylindrical specimens (10-mm diameter, 10-mm height) made of Co-Cr alloy were prepared by casting (C), milling (M), direct process powder-bed (LaserCUSING) with and without annealing (CL+, CL), and direct metal laser sintering (DMLS) with annealing (EL+) and without annealing (EL). After the application of ceramic to the metal specimens, the metal-ceramic bond strength was assessed using a shear force test at a crosshead speed of 0.5 mm/min. Shear bond strength values were statistically analyzed by 1-way ANOVA and Tukey multiple comparison tests (α=.05). Although statistically significant differences were found among the 3 groups (M, 29.87 ±2.06; EL, 38.92 ±2.04; and CL+, 40.93 ±2.21; P=.002), no significant differences were found among the others (P>.05). The debonding surfaces of all specimens exhibited mixed failure mode. These results showed that the direct process powder-bed method is promising in terms of metal-ceramic bonding ability. The manufacturing technique of Co-Cr alloys and the annealing process influence metal-ceramic bonding. Copyright © 2017 Editorial Council for the Journal of Prosthetic Dentistry. Published by Elsevier Inc. All rights reserved.

Veneer Ceramic to Y-TZP Bonding: Comparison of Different Surface Treatments.

PubMed

Kirmali, Omer; Kapdan, Alper; Kustarci, Alper; Er, Kursat

2016-06-01

The purpose of this study was to evaluate the effects of various surface-treatment techniques for enhancing the bond strength between veneering ceramic and yttria-stabilized tetragonal zirconia polycrystals (Y-TZP). Pre-sintered Y-TZP specimens were divided into eight groups (n = 10) according to the surface-treatment technique used: (a) untreated (control); (b) air abrasion with aluminum oxide particles; (c) erbium, chromium:yttrium-scandium-gallium-garnet (Er,Cr:YSGG) laser irradiation at different energy intensities (1 to 6 W). All specimens were then sintered and veneered with veneering ceramic according to the manufacturer's instructions. The obtained zirconia-ceramic specimens were immersed in 37°C distilled water for 24 hours before a shear bond strength test using a universal testing device at a 1 mm/min crosshead speed. The average values were calculated. After debonding, the Y-TZP surfaces were examined under a stereomicroscope to determine their fracture pattern, and the surface topography was evaluated with scanning electron microscopy after surface treatments. The bond strength ranged from 13.24 to 20.54 MPa. All surface treatments increased the bond strength between the veneering ceramic and Y-TZP; however, the value for the 6 W irradiation group was significantly different from the values for other groups (p ˂ 0.05). The present study's findings showed that higher energy densities were needed for the laser irradiation to improve the bond strength between the veneering ceramic and zirconia. Y-TZP is commonly used as a core material in fixed restorations. The bond strength between zirconia and the veneering ceramic can be affected by various surface treatments. © 2015 by the American College of Prosthodontists.

Effect of intra-oral aging on t→m phase transformation, microstructure, and mechanical properties of Y-TZP dental ceramics.

PubMed

Miragaya, Luciana Meireles; Guimarães, Renato Bastos; Souza, Rodrigo Othávio de Assunção E; Santos Botelho, Glauco Dos; Antunes Guimarães, José Guilherme; da Silva, Eduardo Moreira

2017-08-01

The aim of the present study was to evaluate the influence of intra-oral aging on the tetragonal-to-monoclinic (t→m) phase transformation of two Y-TZP dental ceramics - Lava Frame (Frame) and Lava Plus (Plus) - and determine the impact of this response on their microstructures and mechanical properties: flexural strength, Young's modulus, microhardness and fracture toughness. Standardized ceramic specimens were analyzed by X-ray diffraction (XRD), scanning electron microscopy (SEM) and atomic force microscopy (AFM). After the baseline analysis, the specimens were attached to personalized intra-oral resin appliances and exposed to the oral cavity of 20 subjects for 60 days and then analyzed again. Specimens produced for mechanical properties evaluation were also analyzed before and after the 60-day intra-oral aging. The data were analyzed using two-way ANOVA and Tukey HSD's post hoc test (α=0.05). Weibull analysis was used to evaluate the strength reliability. Both Y-TZP ceramics suffered t→m phase transformation after 60-day intra-oral aging (Plus=4.7%/Frame=7.7%). SEM and AFM analyses showed dislodgement of ZrO 2 grains and a significant increase in roughness after intra-oral aging for both ceramics. Both Y-TZP ceramics suffered a decrease on flexural strength, Young's modulus and fracture toughness after intra-oral aging (p<0.05). Only Plus presented a decrease of microhardness after intra-oral aging (p<0.05). Intra-oral aging for 60 days produced t→m phase transformation, changed the microstructure and decreased the mechanical properties of two Y-TZP dental ceramics. Copyright © 2017 Elsevier Ltd. All rights reserved.

Cryo-FIB specimen preparation for use in a cartridge-type cryo-TEM.

PubMed

He, Jie; Hsieh, Chyongere; Wu, Yongping; Schmelzer, Thomas; Wang, Pan; Lin, Ying; Marko, Michael; Sui, Haixin

2017-08-01

Cryo-electron tomography (cryo-ET) is a well-established technique for studying 3D structural details of subcellular macromolecular complexes and organelles in their nearly native context in the cell. A primary limitation of the application of cryo-ET is the accessible specimen thickness, which is less than the diameters of almost all eukaryotic cells. It has been shown that focused ion beam (FIB) milling can be used to prepare thin, distortion-free lamellae of frozen biological material for high-resolution cryo-ET. Commercial cryosystems are available for cryo-FIB specimen preparation, however re-engineering and additional fixtures are often essential for reliable results with a particular cryo-FIB and cryo-transmission electron microscope (cryo-TEM). Here, we describe our optimized protocol and modified instrumentation for cryo-FIB milling to produce thin lamellae and subsequent damage-free cryotransfer of the lamellae into our cartridge-type cryo-TEM. Published by Elsevier Inc.

Influence of Different Ceramic Systems on Marginal Misfit.

PubMed

Vargas, S P; Neves, A C C; Vitti, R; Amaral, M; Henrique, M N; Silva-Concílio, L R

2017-09-01

the aim of this study was to evaluate the marginal misfit at the interface between a ceramic coping and its abutment. Twenty-four specimens were made with solid abutments. The specimens were divided into 3 groups according to the ceramic system (n = 8): Lava (zirconia), IPS e.max Press (lithium disilicate), and IPS Empress Esthetic (leucite). All copings were cemented with resin luting agent (RelyX U200) and the marginal misfit were evaluated at 3 different times: initial, after cementation, and after mechanical cycling using a linear measuring microscope (Measuring Microscope STM-Olympus) at a magnification of 40x. All specimens were subjected to mechanical cycling (1 million cycles) by an universal testing machine (Instron 8800). The results were statistically analyzed using Analysis of Variance and Student's t-test (α = 0.05). all groups showed an increase in the marginal misfit after cementation. The lithium disilicate group demonstrated the lowest interacial gap values at each evaluation (p = 0.001). The zirconia and leucite groups showed similar interfacial gap values (initial, p = 0.244; and post cementation, p = 0.751). the cementation increase the marginal misfit, but the mechanical cycling did not influence the marginal misfit of the ceramics systems evaluated. Copyright© 2017 Dennis Barber Ltd.

TEM and XAS investigation of fission gas behaviors in U-Mo alloy fuels through ion beam irradiation

NASA Astrophysics Data System (ADS)

Zang, Hang; Yun, Di; Mo, Kun; Wang, Kunpeng; Mohamed, Walid; Kirk, Marquis A.; Velázquez, Daniel; Seibert, Rachel; Logan, Kevin; Terry, Jeffrey; Baldo, Peter; Yacout, Abdellatif M.; Liu, Wenbo; Zhang, Bo; Gao, Yedong; Du, Yang; Liu, Jing

2017-10-01

In this study, smaller-grained (hundred nano-meter size grain) and larger-grained (micro-meter size grain) U-10Mo specimens have been irradiated (implanted) with 250 keV Xe+ beam and were in situ characterized by TEM. Xe bubbles were not seen in the specimen after an implantation fluence of 2 × 1020 ions/m2 at room temperature. Nucleation of Xe bubbles happened during heating of the specimen to a final temperature of 300 °C. By comparing measured Xe bubble statistics, the nucleation and growth behaviors of Xe bubbles were investigated in smaller-grained and larger-grained U-10Mo specimens. A multi-atom kind of nucleation mechanism has been observed in both specimens. X-ray Absorption spectroscopy showed the edge position in the bubbles to be the same as that of Xe gas. The size of Xe bubbles has been shown to be bigger in larger-grained specimens than in smaller-grained specimens at the same implantation conditions.

Surface Modifications of Dental Ceramic Implants with Different Glass Solder Matrices: In Vitro Analyses with Human Primary Osteoblasts and Epithelial Cells

PubMed Central

Mick, Enrico

2014-01-01

Ceramic materials show excellent esthetic behavior, along with an absence of hypersensitivity, making them a possible alternative implant material in dental surgery. However, their surface properties enable only limited osseointegration compared to titanium implants. Within this study, a novel surface coating technique for enhanced osseointegration was investigated biologically and mechanically. Specimens of tetragonal zirconia polycrystal (TZP) and aluminum toughened zirconia (ATZ) were modified with glass solder matrices in two configurations which mainly consisted of SiO2, Al2O3, K2O, and Na2O. The influence on human osteoblastic and epithelial cell viability was examined by means of a WST-1 assay as well as live/dead staining. A C1CP-ELISA was carried out to verify procollagen type I production. Uncoated/sandblasted ceramic specimens and sandblasted titanium surfaces were investigated as a reference. Furthermore, mechanical investigations of bilaterally coated pellets were conducted with respect to surface roughness and adhesive strength of the different coatings. These tests could demonstrate a mechanically stable implant coating with glass solder matrices. The coated ceramic specimens show enhanced osteoblastic and partly epithelial viability and matrix production compared to the titanium control. Hence, the new glass solder matrix coating could improve bone cell growth as a prerequisite for enhanced osseointegration of ceramic implants. PMID:25295270

Surface modifications of dental ceramic implants with different glass solder matrices: in vitro analyses with human primary osteoblasts and epithelial cells.

PubMed

Markhoff, Jana; Mick, Enrico; Mitrovic, Aurica; Pasold, Juliane; Wegner, Katharina; Bader, Rainer

2014-01-01

Ceramic materials show excellent esthetic behavior, along with an absence of hypersensitivity, making them a possible alternative implant material in dental surgery. However, their surface properties enable only limited osseointegration compared to titanium implants. Within this study, a novel surface coating technique for enhanced osseointegration was investigated biologically and mechanically. Specimens of tetragonal zirconia polycrystal (TZP) and aluminum toughened zirconia (ATZ) were modified with glass solder matrices in two configurations which mainly consisted of SiO2, Al2O3, K2O, and Na2O. The influence on human osteoblastic and epithelial cell viability was examined by means of a WST-1 assay as well as live/dead staining. A C1CP-ELISA was carried out to verify procollagen type I production. Uncoated/sandblasted ceramic specimens and sandblasted titanium surfaces were investigated as a reference. Furthermore, mechanical investigations of bilaterally coated pellets were conducted with respect to surface roughness and adhesive strength of the different coatings. These tests could demonstrate a mechanically stable implant coating with glass solder matrices. The coated ceramic specimens show enhanced osteoblastic and partly epithelial viability and matrix production compared to the titanium control. Hence, the new glass solder matrix coating could improve bone cell growth as a prerequisite for enhanced osseointegration of ceramic implants.

Fatigue failure load of two resin-bonded zirconia-reinforced lithium silicate glass-ceramics: Effect of ceramic thickness.

PubMed

Monteiro, Jaiane Bandoli; Riquieri, Hilton; Prochnow, Catina; Guilardi, Luís Felipe; Pereira, Gabriel Kalil Rocha; Borges, Alexandre Luiz Souto; de Melo, Renata Marques; Valandro, Luiz Felipe

2018-06-01

To evaluate the effect of ceramic thickness on the fatigue failure load of two zirconia-reinforced lithium silicate (ZLS) glass-ceramics, adhesively cemented to a dentin analogue material. Disc-shaped specimens were allocated into 8 groups (n=25) considering two study factors: ZLS ceramic type (Vita Suprinity - VS; and Celtra Duo - CD), and ceramic thickness (1.0; 1.5; 2.0; and 2.5mm). A trilayer assembly (ϕ=10mm; thickness=3.5mm) was designed to mimic a bonded monolithic restoration. The ceramic discs were etched, silanized and luted (Variolink N) into a dentin analogue material. Fatigue failure load was determined using the Staircase method (100,000 cycles at 20Hz; initial fatigue load ∼60% of the mean monotonic load-to-failure; step size ∼5% of the initial fatigue load). A stainless-steel piston (ϕ=40mm) applied the load into the center of the specimens submerged in water. Fractographic analysis and Finite Element Analysis (FEA) were also performed. The ceramic thickness influenced the fatigue failure load for both ZLS materials: Suprinity (716N up to 1119N); Celtra (404N up to 1126N). FEA showed that decreasing ceramic thickness led to higher stress concentration on the cementing interface. Different ZLS glass-ceramic thicknesses influenced the fatigue failure load of the bonded system (i.e. the thicker the glass ceramic is, the higher the fatigue failure load will be). Different microstructures of the ZLS glass-ceramics might affect the fatigue behavior. FEA showed that the thicker the glass ceramic is, the lower the stress concentration at the tensile surface will be. Copyright © 2018 The Academy of Dental Materials. Published by Elsevier Inc. All rights reserved.

Hydrogen defects in α-Al2O3 and water weakening of sapphire and alumina ceramics between 600 and 1000°C: I. Infrared characterization of defects

USGS Publications Warehouse

Kronenberg, A.K.; Castaing, J.; Mitchell, T.E.; Kirby, S.H.

2000-01-01

Hydrogen impurities in materials influence their properties, including flow strength. α-Al2O3 single crystals and polycrystalline ceramics were annealed in supercritical water between 850 and 1025°C, under pressures in the range 1500–2000 MPa. A few specimens were further subjected to plastic deformation. Hydrogen penetration was examined using infrared absorption measurements of O–H bond vibrations, which revealed two kinds of hydrogen defects. In single crystals, defects are characterized by sharp O–H absorption bands assigned to interstitial protons. Hydrogen impurities of hydrothermally annealed ceramics and of all hydrothermally deformed specimens are characterized by broad O–H bands assigned to molecular water. The grain boundaries of hydrothermally annealed ceramics are severely damaged. The kinetics of hydrogen penetration is consistent with diffusion data.

Fatigue Behavior of Crystalline-Reinforced Glass-Ceramics.

PubMed

Vicari, Carolina Barbosa; Magalhães, Bárbara de Oliveira; Griggs, Jason Alan; Borba, Márcia

2018-01-03

To evaluate the fatigue behavior of two crystalline-reinforced ceramics: leucite-reinforced (VL) and lithium disilicate-based (VD) glass-ceramics. Bar-shaped specimens (16 × 4 × 1.2 mm) were produced for each ceramic using prefabricated CAD/CAM blocks. For each group, 30 specimens were subjected to a three-point flexural strength test in a universal testing machine. For VL and VD, 36 and 41 specimens were subjected to a cyclic fatigue test, respectively. The cyclic fatigue test was performed with a pneumatic mechanical cycling machine (1 Hz; 37°C distilled water). Specimens were tested at two stress levels for each preset lifetime (10 3 and 10 4 cycles for VL; 10 4 and 10 5 cycles for VD) following the boundary technique. Fractography was performed with a scanning electron microscope. Data were analyzed with Weibull analysis. There were significant differences among groups for characteristic strength (σ 0 ) and Weibull modulus (m), as the confidence intervals did not overlap. The VD group presented the highest values of σ 0 , but the lowest Weibull modulus. Both groups showed a reduction of approximately 60% of the initial flexural strength (σ f ) after cycling for 10 4 cycles. For VD tested in fatigue, there was no degradation of σ f when the number of cycles was increased from 10 4 to 10 5 . The VL group showed an 18% decrease in σ f when the number of cycles increased from 10 3 to 10 4 . Flexural strength values estimated for a 5% probability of failure were 36 MPa for VL and 55 MPa for VD, after 10 4 cycles. Both glass-ceramics showed similar strength degradation (60%) after a lifetime of 10 4 cycles, despite their distinct mechanical properties. Mechanical cycling in humid conditions proved to be an important factor for the degradation of the mechanical properties of crystalline-reinforced glass-ceramics. © 2018 by the American College of Prosthodontists.

Two-body wear rate of CAD/CAM resin blocks and their enamel antagonists.

PubMed

Stawarczyk, Bogna; Özcan, Mutlu; Trottmann, Albert; Schmutz, Felix; Roos, Malgorzata; Hämmerle, Christoph

2013-05-01

Computer-aided design and computer-aided manufacturing (CAD/CAM) resins exhibit good mechanical properties and can be used as long-term restorations. The wear rate of such resins and their enamel antagonists is unknown. The purpose of this study was to test and compare the 2-body wear rate of CAD/CAM resin blocks. Wear specimens (N=42, n=6) were made from 5 CAD/CAM resins: ZENO PMMA (ZP), artBloc Temp (AT), Telio CAD (TC), Blanc High-class (HC), CAD-Temp (CT); 1 manually polymerized resin: Integral esthetic press (negative control group, IEP); and 1 glass-ceramic: VITA Mark II (positive control group, VM2). The specimens for the wear resistance were aged in a thermomechanical loading machine (49 N, 1.67 Hz, 5/50°C) with human enamel antagonists. The material loss of all specimens before, during, and after aging was evaluated with a 3DS profilometer. The measured material loss data of all tested groups were statistically evaluated with linear mixed model analysis (a=.05). Manually polymerized resin showed significantly higher material wear (P<.001) than all other tested groups. Glass-ceramic showed significantly lower wear values (P<.001) than CAD/CAM resins ZP, AT, HC, CT, and IES. CAD/CAM resin TC was not significantly different from the positive control group. Glass-ceramic showed the highest enamel wear values (P<.001) of all tested resins. No differences were found in the enamel wear among all resins. The glass-ceramic group showed damage in the form of cracks on the worn enamel surface in 50% of specimens. CAD/CAM resins showed lower wear rates than those conventionally polymerized. Only one CAD/CAM resin, TC, presented material wear values comparable with glass-ceramic. The tested glass-ceramic developed cracks in the enamel antagonist and showed the highest enamel wear values of all other tested groups. Copyright © 2013 The Editorial Council of the Journal of Prosthetic Dentistry. Published by Mosby, Inc. All rights reserved.

Influence of abutment material and luting cements color on the final color of all ceramics.

PubMed

Dede, Dogu Ömür; Armaganci, Arzu; Ceylan, Gözlem; Cankaya, Soner; Celik, Ersan

2013-11-01

The purpose of this study is to evaluate the effects of different abutment materials and luting cements color on the final color of implant-supported all-ceramic restorations. Ten A2 shade IPS e.max Press disc shape all-ceramic specimens were prepared (11 × 1.5 mm). Three different shades (translucent, universal and white opaque) of disc shape luting cement specimens were prepared (11 × 0.2 mm). Three different (zirconium, gold-palladium and titanium) implant abutments and one composite resin disc shape background specimen were prepared at 11 mm diameter and appropriate thicknesses. All ceramic specimens colors were measured with each background and luting cement samples on a teflon mold. A digital spectrophotometer used for measurements and data recorded as CIE L*a*b* color co-ordinates. An optical fluid applied on to the samples to provide a good optical connection and measurements on the composite resin background was saved as the control group. ΔE values were calculated from the ΔL, Δa and Δb values between control and test groups and data were analyzed with one-way variance analysis (ANOVA) and mean values were compared by the Tukey HSD test (α = 0.05). One-way ANOVA of ΔL, Δa, Δb and ΔE values of control and test groups revealed significant differences for backgrounds and seldom for cement color groups (p the 0.05). Only zirconium implant abutment groups and gold palladium abutment with universal shade cement group were found to be clinically acceptable (ΔE ≤ 3.0). Using titanium or gold-palladium abutments for implant supported all ceramics will be esthetically questionable and white opaque cement will be helpful to mask the dark color of titanium abutment.

[Comparison of wear resistance and flexural strength of three kinds of bulk-fill composite resins].

PubMed

Zhang, Huan; Zhang, Meng-Long; Qiu, Li-Hong; Yu, Jing-Tao; Zhan, Fu-Liang

2016-06-01

To compare the abrasion resistance and flexure strength of three bulk-fill resin composites with an universal nano-hybrid composite resins. The specimens were prepared with three kinds of bulk fill composites (SDR , sonicfill, Tetric N-Ceram Bulk Fill) and an universal nano-hybrid composite resins(Herculite Precis). 10 mm in diameter × 2mm in height specimens were prepared for abrasion resistance, while 2 mm in width × 2 mm in depth×25 mm in length specimens were prepared for flexure strength. The specimens were mounted in a bal1-on-disc wear testing machine and abraded with the media artificial saliva(50 N loads, 10000 cycles).Flexural test was performed with an Universal Testing Machine at a cross-head speed of 1mm/min. One-way variance analysis was used to determine the statistical differences of volume loss and flexural strength among groups with SPSS 13.0 software package(P<0.05). The volume loss was as follows: SDR (1.2433±0.11) mm30.05). With regard to wear resistance and flexural strength, Tetric N-Ceram Bulk Fill is recommended as an alternative for posterior restorations.

Comparison of Shade of Ceramic with Three Different Zirconia Substructures using Spectrophotometer.

PubMed

Habib, Syed Rashid; Shiddi, Ibraheem F Al

2015-02-01

This study assessed how changing the Zirconia (Zr) substructure affected the color samples after they have been overlaid by the same shade of veneering ceramic. Three commercial Zr materials were tested in this study: Prettau(®) Zirconia (ZirKonZahn, Italy), Cercon (Dentsply, Germany) and InCoris ZI (Sirona, Germany). For each system, 15 disk-shaped specimens (10 × 1 mm) were fabricated. Three shades of A1, A2 and A3.5 of porcelain (IPS e.MaxCeram, IvoclarVivadent, USA) were used for layering the specimens. Five specimens from each type of Zr were layered with same shade of ceramic. Color measurements were recorderd by a spectrophotometer Color-Eye(®) 7000A (X-Rite, Grand Rapids, MI). Mean values of L, a, b color coordinates and ΔE were recorded and comparisons were made. Differences in the ΔE were recorded for the same porcelain shade with different Zr substructures and affected the color of the specimens (p < 0.01, ANOVA). The maximum difference between the ΔE values for the A1, A2 and A3.5 shades with three types of Zr substructures was found to be 1.59, 1.69 and 1.45 respectively. Multiple comparisons of the ΔE with PostHoc Tukey test revealed a statistically significant difference (p < 0.05) between the three types of Zr, except between Type 2 Zr and Type 3 Zr for the Shade A1. The mean values of L, a, b and ΔE for the Prettau(®) Zirconia substructure were found to be the least among the three types. The brand of Zr used influences the final color of the all ceramic Zr based restorations and this has clinical significance.

Step-stress analysis for predicting dental ceramic reliability

PubMed Central

Borba, Márcia; Cesar, Paulo F.; Griggs, Jason A.; Bona, Álvaro Della

2013-01-01

Objective To test the hypothesis that step-stress analysis is effective to predict the reliability of an alumina-based dental ceramic (VITA In-Ceram AL blocks) subjected to a mechanical aging test. Methods Bar-shaped ceramic specimens were fabricated, polished to 1µm finish and divided into 3 groups (n=10): (1) step-stress accelerating test; (2) flexural strength- control; (3) flexural strength- mechanical aging. Specimens from group 1 were tested in an electromagnetic actuator (MTS Evolution) using a three-point flexure fixture (frequency: 2Hz; R=0.1) in 37°C water bath. Each specimen was subjected to an individual stress profile, and the number of cycles to failure was recorded. A cumulative damage model with an inverse power law lifetime-stress relation and Weibull lifetime distribution were used to fit the fatigue data. The data were used to predict the stress level and number of cycles for mechanical aging (group 3). Groups 2 and 3 were tested for three-point flexural strength (σ) in a universal testing machine with 1.0 s in 37°C water. Data were statistically analyzed using Mann-Whitney Rank Sum test. Results Step-stress data analysis showed that the profile most likely to weaken the specimens without causing fracture during aging (95% CI: 0–14% failures) was: 80 MPa stress amplitude and 105 cycles. The median σ values (MPa) for groups 2 (493±54) and 3 (423±103) were statistically different (p=0.009). Significance The aging profile determined by step-stress analysis was effective to reduce alumina ceramic strength as predicted by the reliability estimate, confirming the study hypothesis. PMID:23827018

Step-stress analysis for predicting dental ceramic reliability.

PubMed

Borba, Márcia; Cesar, Paulo F; Griggs, Jason A; Della Bona, Alvaro

2013-08-01

To test the hypothesis that step-stress analysis is effective to predict the reliability of an alumina-based dental ceramic (VITA In-Ceram AL blocks) subjected to a mechanical aging test. Bar-shaped ceramic specimens were fabricated, polished to 1μm finish and divided into 3 groups (n=10): (1) step-stress accelerating test; (2) flexural strength-control; (3) flexural strength-mechanical aging. Specimens from group 1 were tested in an electromagnetic actuator (MTS Evolution) using a three-point flexure fixture (frequency: 2Hz; R=0.1) in 37°C water bath. Each specimen was subjected to an individual stress profile, and the number of cycles to failure was recorded. A cumulative damage model with an inverse power law lifetime-stress relation and Weibull lifetime distribution were used to fit the fatigue data. The data were used to predict the stress level and number of cycles for mechanical aging (group 3). Groups 2 and 3 were tested for three-point flexural strength (σ) in a universal testing machine with 1.0MPa/s stress rate, in 37°C water. Data were statistically analyzed using Mann-Whitney Rank Sum test. Step-stress data analysis showed that the profile most likely to weaken the specimens without causing fracture during aging (95% CI: 0-14% failures) was: 80MPa stress amplitude and 10(5) cycles. The median σ values (MPa) for groups 2 (493±54) and 3 (423±103) were statistically different (p=0.009). The aging profile determined by step-stress analysis was effective to reduce alumina ceramic strength as predicted by the reliability estimate, confirming the study hypothesis. Copyright © 2013 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Dynamic Behavior and Optimization of Advanced Armor Ceramics: January-December 2011 Annual Report

DTIC Science & Technology

2015-03-01

however, under conventional methods of processing. To develop plasticity in ceramic like SiC, new fracture mechanisms and interesting behaviors need...and new fracture mechanisms . These improvements, in turn, could offer the potential for improved ballistic performance. Co-precipitation has been...experiments, the following deformed fragments were recovered for extensive SEM and TEM study.  A fracture mechanism map has been constructed in

Fracture strength of three all-ceramic systems: Top-Ceram compared with IPS-Empress and In-Ceram.

PubMed

Quran, Firas Al; Haj-Ali, Reem

2012-03-01

The purpose of this study was to investigate the fracture loads and mode of failure of all-ceramic crowns fabricated using Top-Ceram and compare it with all-ceramic crowns fabricated from well-established systems: IPS-Empress II, In-Ceram. Thirty all-ceramic crowns were fabricated; 10 IPS-Empress II, 10 In-Ceram alumina and 10 Top-Ceram. Instron testing machine was used to measure the loads required to introduce fracture of each crown. Mean fracture load for In-Ceram alumina [941.8 (± 221.66) N] was significantly (p > 0.05) higher than those of Top-Ceram and IPS-Empress II. There was no statistically significant difference between Top-Ceram and IPS-Empress II mean fracture loads; 696.20 (+222.20) and 534 (+110.84) N respectively. Core fracture pattern was highest seen in Top- Ceram specimens.

A study on (K, Na) NbO3 based multilayer piezoelectric ceramics micro speaker

NASA Astrophysics Data System (ADS)

Gao, Renlong; Chu, Xiangcheng; Huan, Yu; Sun, Yiming; Liu, Jiayi; Wang, Xiaohui; Li, Longtu

2014-10-01

A flat panel micro speaker was fabricated from (K, Na) NbO3 (KNN)-based multilayer piezoelectric ceramics by a tape casting and cofiring process using Ag-Pd alloys as an inner electrode. The interface between ceramic and electrode was investigated by scanning electron microscope (SEM) and transmission electron microscope (TEM). The acoustic response was characterized by a standard audio test system. We found that the micro speaker with dimensions of 23 × 27 × 0.6 mm3, using three layers of 30 μm thickness KNN-based ceramic, has a high average sound pressure level (SPL) of 87 dB, between 100 Hz-20 kHz under five voltage. This result was even better than that of lead zirconate titanate (PZT)-based ceramics under the same conditions. The experimental results show that the KNN-based multilayer ceramics could be used as lead free piezoelectric micro speakers.

Probability of detection of internal voids in structural ceramics using microfocus radiography

NASA Technical Reports Server (NTRS)

Baaklini, G. Y.; Roth, D. J.

1986-01-01

The reliability of microfocous X-radiography for detecting subsurface voids in structural ceramic test specimens was statistically evaluated. The microfocus system was operated in the projection mode using low X-ray photon energies (20 keV) and a 10 micro m focal spot. The statistics were developed for implanted subsurface voids in green and sintered silicon carbide and silicon nitride test specimens. These statistics were compared with previously-obtained statistics for implanted surface voids in similar specimens. Problems associated with void implantation are discussed. Statistical results are given as probability-of-detection curves at a 95 precent confidence level for voids ranging in size from 20 to 528 micro m in diameter.

Probability of detection of internal voids in structural ceramics using microfocus radiography

NASA Technical Reports Server (NTRS)

Baaklini, G. Y.; Roth, D. J.

1985-01-01

The reliability of microfocus x-radiography for detecting subsurface voids in structural ceramic test specimens was statistically evaluated. The microfocus system was operated in the projection mode using low X-ray photon energies (20 keV) and a 10 micro m focal spot. The statistics were developed for implanted subsurface voids in green and sintered silicon carbide and silicon nitride test specimens. These statistics were compared with previously-obtained statistics for implanted surface voids in similar specimens. Problems associated with void implantation are discussed. Statistical results are given as probability-of-detection curves at a 95 percent confidence level for voids ranging in size from 20 to 528 micro m in diameter.

Interlaboratory round robin study on axial tensile properties of SiC-SiC CMC tubular test specimens [Interlaboratory round robin study on axial tensile properties of SiC/SiC tubes

DOE Office of Scientific and Technical Information (OSTI.GOV)

Singh, Gyanender P.; Gonczy, Steve T.; Deck, Christian P.

An interlaboratory round robin study was conducted on the tensile strength of SiC–SiC ceramic matrix composite (CMC) tubular test specimens at room temperature with the objective of expanding the database of mechanical properties of nuclear grade SiC–SiC and establishing the precision and bias statement for standard test method ASTM C1773. The mechanical properties statistics from the round robin study and the precision statistics and precision statement are presented herein. The data show reasonable consistency across the laboratories, indicating that the current C1773–13 ASTM standard is adequate for testing ceramic fiber reinforced ceramic matrix composite tubular test specimen. Furthermore, it wasmore » found that the distribution of ultimate tensile strength data was best described with a two–parameter Weibull distribution, while a lognormal distribution provided a good description of the distribution of proportional limit stress data.« less

Interlaboratory round robin study on axial tensile properties of SiC-SiC CMC tubular test specimens [Interlaboratory round robin study on axial tensile properties of SiC/SiC tubes

DOE PAGES

Singh, Gyanender P.; Gonczy, Steve T.; Deck, Christian P.; ...

2018-04-19

An interlaboratory round robin study was conducted on the tensile strength of SiC–SiC ceramic matrix composite (CMC) tubular test specimens at room temperature with the objective of expanding the database of mechanical properties of nuclear grade SiC–SiC and establishing the precision and bias statement for standard test method ASTM C1773. The mechanical properties statistics from the round robin study and the precision statistics and precision statement are presented herein. The data show reasonable consistency across the laboratories, indicating that the current C1773–13 ASTM standard is adequate for testing ceramic fiber reinforced ceramic matrix composite tubular test specimen. Furthermore, it wasmore » found that the distribution of ultimate tensile strength data was best described with a two–parameter Weibull distribution, while a lognormal distribution provided a good description of the distribution of proportional limit stress data.« less

Engine materials characterization and damage monitoring by using x ray technologies

NASA Technical Reports Server (NTRS)

Baaklini, George Y.

1993-01-01

X ray attenuation measurement systems that are capable of characterizing density variations in monolithic ceramics and damage due to processing and/or mechanical testing in ceramic and intermetallic matrix composites are developed and applied. Noninvasive monitoring of damage accumulation and failure sequences in ceramic matrix composites is used during room-temperature tensile testing. This work resulted in the development of a point-scan digital radiography system and an in situ x ray material testing system. The former is used to characterize silicon carbide and silicon nitride specimens, and the latter is used to image the failure behavior of silicon-carbide-fiber-reinforced, reaction-bonded silicon nitride matrix composites. State-of-the-art x ray computed tomography is investigated to determine its capabilities and limitations in characterizing density variations of subscale engine components (e.g., a silicon carbide rotor, a silicon nitride blade, and a silicon-carbide-fiber-reinforced beta titanium matrix rod, rotor, and ring). Microfocus radiography, conventional radiography, scanning acoustic microscopy, and metallography are used to substantiate the x ray computed tomography findings. Point-scan digital radiography is a viable technique for characterizing density variations in monolithic ceramic specimens. But it is very limited and time consuming in characterizing ceramic matrix composites. Precise x ray attenuation measurements, reflecting minute density variations, are achieved by photon counting and by using microcollimators at the source and the detector. X ray computed tomography is found to be a unique x ray attenuation measurement technique capable of providing cross-sectional spatial density information in monolithic ceramics and metal matrix composites. X ray computed tomography is proven to accelerate generic composite component development. Radiographic evaluation before, during, and after loading shows the effect of preexisting volume flaws on the fracture behavior of composites. Results from one-, three-, five-, and eight-ply ceramic composite specimens show that x ray film radiography can monitor damage accumulation during tensile loading. Matrix cracking, fiber-matrix debonding, fiber bridging, and fiber pullout are imaged throughout the tensile loading of the specimens. In situ film radiography is found to be a practical technique for estimating interfacial shear strength between the silicon carbide fibers and the reaction-bonded silicon nitride matrix. It is concluded that pretest, in situ, and post-test x ray imaging can provide greater understanding of ceramic matrix composite mechanical behavior.

Polymerization of a dual-cured cement through ceramic: LED curing light vs halogen lamp.

PubMed

Lopes, Lawrence Gonzaga; Franco, Eduardo Batista; Name Neto, Abrão; Herrera, Francyle S; Kurachi, Cristina; Castañeda-Espinosa, Juan C; Lauris, José Roberto Pereira

2004-12-01

The aim of this study was to investigate the influence of light source, LED unit and halogen lamp (HL), on the effectiveness of Enforce dual-cured cement cured under a ceramic disc. Three exposure times (60, 80 and 120 s) were also evaluated. Two experimental groups, in which the polymerization of the dual-cured cement was performed through a ceramic disc, and two control groups, in which the polymerization of the dual-cured cement was performed directly without presence of ceramic disc were subdivided into three subgroups (three different exposure times), with five specimens each: G1A- HL 60s; G1B- HL 80s; G1C- HL 120s; G2A- LED 60s; G2B- LED 80s; G2C- LED 120s; and control groups: G3A- HL 60s; G3B- HL 80s; G3C- HL 120s; G4A- LED 60s; G4B- LED 80s and G4C- LED 120s. Cement was applied in a steel matrix (4mm diameter, 1.2mm thickness). In the experimental groups, a ceramic disc was placed on top. The cement was light-cured through the ceramic by a HL and LED, however, the control groups were cured without the ceramic disc. The specimens were stored in a light-proof container at 37ºC for 24 hours, then Vickers hardness was determined. A four-way ANOVA and Tukey test (p£ 0.05) were performed. All specimens cured by LED for 60s showed inferior values compared with the halogen groups. In general, light-curing by LED for 80s and 120s was comparable to halogen groups (60s and 80s) and their control groups. LED technology can be viable for light-curing through conventional ceramic indirect restorations, when curing time is increased in relation to HL curing time.

Edge chipping and flexural resistance of monolithic ceramics☆

PubMed Central

Zhang, Yu; Lee, James J.-W.; Srikanth, Ramanathan; Lawn, Brian R.

2014-01-01

Objective Test the hypothesis that monolithic ceramics can be developed with combined esthetics and superior fracture resistance to circumvent processing and performance drawbacks of traditional all-ceramic crowns and fixed-dental-prostheses consisting of a hard and strong core with an esthetic porcelain veneer. Specifically, to demonstrate that monolithic prostheses can be produced with a much reduced susceptibility to fracture. Methods Protocols were applied for quantifying resistance to chipping as well as resistance to flexural failure in two classes of dental ceramic, microstructurally-modified zirconias and lithium disilicate glass–ceramics. A sharp indenter was used to induce chips near the edges of flat-layer specimens, and the results compared with predictions from a critical load equation. The critical loads required to produce cementation surface failure in monolithic specimens bonded to dentin were computed from established flexural strength relations and the predictions validated with experimental data. Results Monolithic zirconias have superior chipping and flexural fracture resistance relative to their veneered counterparts. While they have superior esthetics, glass–ceramics exhibit lower strength but higher chip fracture resistance relative to porcelain-veneered zirconias. Significance The study suggests a promising future for new and improved monolithic ceramic restorations, with combined durability and acceptable esthetics. PMID:24139756

Characterization of glass-infiltrated alumina-based ceramics

PubMed Central

Bona, Alvaro Della; Mecholsky, John J; Barrett, Allyson A; Griggs, Jason A

2010-01-01

Objective characterize the microstructure, composition, and important properties of glass-infiltrated alumina-based ceramics similar to the In-Ceram system. Methods Materials used were: IA- In-Ceram Alumina (Vita); IAE- IA electrophoretically deposited (Vita); AEM- IA using a vacuum driven method (Vita); VC- Vitro-Ceram (Angelus); TC- Turkom-Cera (Turkom-Ceramic); CC- Ceramcap (Foto-Ceram); and AG- Alglass (EDG). Ceramic specimens were fabricated following manufacturers’ instructions and ISO6872 standard and polished successively through 1μm alumina abrasive. Semi-quantitative and qualitative analyses were performed using scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS), and stereology (Vv). The elastic modulus (E) and Poisson’s ratio (ν) were determined using time-of-flight data measured in an ultrasonic pulser/receiver and the density (ρ) was determined using a helium pycnometer. Vicker’s indentation was used to calculate hardness (H). Bar specimens (25×4×1.2mm3) were loaded in three-point bending to fracture using a universal testing machine with cross-head speed of 1mm/min. Flexural strength (σ3P) was calculated and statistically analyzed using ANOVA, Tukey (α=0.05) and Weibull (m= modulus, σ0= characteristic strength). Results SEM and EDS analyses revealed similar microstructure for all ceramics, except for a lead-based matrix in CC and a zirconia phase in VC. TC, AG and CC showed significantly lower mean σ3P values than the other ceramics (p 0.05). AEM showed the greatest m (16). Conclusion Despite few differences in microstructure and composition, the IA, IAE, AEM and VC ceramics have similar properties. Significance The glass-infiltrated alumina-based ceramics from different manufacturers presented distinct characteristics. It is necessary to characterize new commercially available materials to understand their properties. PMID:18692231

New nano-sized Al2O3-BN coating 3Y-TZP ceramic composites for CAD/CAM-produced all-ceramic dental restorations. Part I. Fabrication of powders.

PubMed

Yang, Se Fei; Yang, Li Qiang; Jin, Zhi Hao; Guo, Tian Wen; Wang, Lei; Liu, Hong Chen

2009-06-01

Partially sintered 3 mol % yttria-stabilized tetragonal zirconium dioxide (ZrO(2), zirconia) polycrystal (3Y-TZP) ceramics are used in dental posterior restorations with computer-aided design-computer-aided manufacturing (CAD/CAM) techniques. High strength is acquired after sintering, but shape distortion of preshaped compacts during their sintering is inevitable. The aim of this study is to fabricate new machinable ceramic composites with strong mechanical properties that are fit for all-ceramic dental restorations. Aluminum oxide (Al(2)O(3))-coated 3Y-TZP powders were first prepared by the heterogeneous precipitation method starting with 3Y-TZP, Al(NO(3))(3) . 9H(2)O, and ammonia, then amorphous boron nitride (BN) was produced and the as-received composite powders were coated via in situ reaction with boric acid and urea. Transmission electron microscopy (TEM) and X-ray diffraction (XRD) were used to analyze the status of Al(2)O(3)-BN on the surface of the 3Y-TZP particles. TEM micrographs show an abundance of Al(2)O(3) particles and amorphous BN appearing uniformly on the surface of the 3Y-TZP particles after the coating process. The size of the Al(2)O(3) particles is about 20 nm. The XRD pattern shows clearly the peak of amorphous BN among the peaks of ZrO(2).

Fracture Strength of Single-Crystal Silicon Carbide Microspecimens at Room and Elevated Temperature

NASA Technical Reports Server (NTRS)

Nemeth, Noel N.; Sharpe, William N., Jr.; Beheim, Glenn M.; Evans, Laura J.; Jadaan, Osama M.

2007-01-01

Three shapes of tensile specimens were tested--curved with a very low stress concentration factor and straight with either a circular hole or an elliptical hole. The nominal thickness was 125 micron with a net section 100 micron wide; the overall length of these microspecimens was 3.1 mm. They were fabricated by an improved version of deep reactive ion etching, which produced specimens with smooth sidewalls and cross-sections having a slightly trapezoidal shape that was exaggerated inside the holes. The novel test setup used a vertical load train extending into a resistance furnace. The specimens had wedge-shaped ends which fit into ceramic grips. The fixed grip was mounted on a ceramic post, and the movable grip was connected to a load cell and actuator outside the furnace with a ceramic-encased nichrome wire. The same arrangement was used for tests at 24 and at 1000 C. The strengths of the curved specimens for two batches of material (made with slightly different processes) were 0.66+/-0.12 GPa and 0.45+/-0.20 GPa respectively at 24 C with identical values at 1000 C. The fracture strengths of the circular-hole and elliptical-hole specimens (computed from the stress concentration factors and measured loads at failure) were approximately 1.2 GPa with slight decreases at the higher temperature. Fractographic examinations showed failures initiating on the surface--primarily at corners. Weibull predictions of fracture strengths for the hole specimens based on the properties of the curved specimens were reasonably effective for the circular holes, but not for the elliptical holes.

Flexural strength and reliability of monolithic and trilayer ceramic structures obtained by the CAD-on technique.

PubMed

Basso, G R; Moraes, R R; Borba, M; Griggs, J A; Della Bona, A

2015-12-01

To evaluate the flexural strength, Weibull modulus, fracture toughness, and failure behavior of ceramic structures obtained by the CAD-on technique, testing the null hypothesis that trilayer structures show similar properties to monolithic structures. Bar-shaped (1.8mm×4mm×16mm) monolithic specimens of zirconia (IPS e.max ZirCAD - Ivoclar Vivadent) and trilayer specimens of zirconia/fusion ceramic/lithium dissilicate (IPS e.max ZirCAD/IPS e.max CAD Crystall./Connect/IPS e.max CAD, Ivoclar Vivadent) were fabricated (n=30). Specimens were tested in flexure in 37°C deionized water using a universal testing machine at a crosshead speed of 0.5mm/min. Failure loads were recorded, and the flexural strength values were calculated. Fractography principles were used to examine the fracture surfaces under optical and scanning electron microscopy. Data were statistically analyzed using Student's t-test and Weibull statistics (α=0.05). Monolithic and trilayer specimens showed similar mean flexural strengths, characteristic strengths, and Weibull moduli. Trilayer structures showed greater mean critical flaw and fracture toughness values than monolithic specimens (p<0.001). Most critical flaws in the trilayer groups were located on the Y-TZP surface subjected to tension and propagated catastrophically. Trilayer structures showed no flaw deflection at the interface. Considering the CAD-on technique, the trilayer structures showed greater fracture toughness than the monolithic zirconia specimens. Copyright © 2015 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Specimen Preparation

NASA Astrophysics Data System (ADS)

Williams, David B.; Carter, C. Barry

Specimen preparation is a very broad subject; there are books devoted to this topic alone. The intention here is to summarize the techniques, suggest routes that you might follow, and above all to emphasize that there are many ways to produce a TEM specimen; the one you choose will depend on the information you need, time constraints, availability of equipment, your skill, and the material. So we’ll concentrate on the ‘principles of cooking,’ but won’t try to list all the possible ‘recipes.’ One important point to bear in mind is that your technique must not affect what you see or measure, or if it does, then you must know how. Specimen preparation artifacts may be interesting but they are not usually what you want to study. Incidentally, we’ll make ‘specimens’ from the ‘sample’ we’re investigating so we’ll look at ‘TEM specimens,’ but sometimes we, and everyone else, will interchange the two words.

In situ sputter cleaning of thin film metal substrates for UHV-TEM corrosion studies.

NASA Technical Reports Server (NTRS)

Heinemann, K.; Poppa, H.

1973-01-01

A prerequisite for conducting valid corrosion experiments by in situ electron microscopy techniques is not only the achievement of UHV background pressure conditions at the site of the specimen but also the ability to clean the surface of the thin metal substrate specimen before initiation of the corrosive interaction. A miniaturized simple ion gun has been constructed for this purpose. The gun is small enough to be incorporated into an UHV electron microscope specimen chamber with hot stage in such a way as to permit bombardment of the substrate specimen while observing it by transmission electron microscopy TEM. It is shown that the ion beam generated is confined well enough to cause a sputtering removal of substrate material at a rate of approximately 5-10 A/min and to prevent the sputter deposition of contaminating material from the specimen holder.

Translucency of dental ceramics with different thicknesses.

PubMed

Wang, Fu; Takahashi, Hidekazu; Iwasaki, Naohiko

2013-07-01

The increased use of esthetic restorations requires an improved understanding of the translucent characteristics of ceramic materials. Ceramic translucency has been considered to be dependent on composition and thickness, but less information is available about the translucent characteristics of these materials, especially at different thicknesses. The purpose of this study was to investigate the relationship between translucency and the thickness of different dental ceramics. Six disk-shaped specimens of 8 glass ceramics (IPS e.max Press HO, MO, LT, HT, IPS e.max CAD LT, MO, AvanteZ Dentin, and Trans) and 5 specimens of 5 zirconia ceramics (Cercon Base, Zenotec Zr Bridge, Lava Standard, Lava Standard FS3, and Lava Plus High Translucency) were prepared following the manufacturers' instructions and ground to a predetermined thickness with a grinding machine. A spectrophotometer was used to measure the translucency parameters (TP) of the glass ceramics, which ranged from 2.0 to 0.6 mm, and of the zirconia ceramics, which ranged from 1.0 to 0.4 mm. The relationship between the thickness and TP of each material was evaluated using a regression analysis (α=.05). The TP values of the glass ceramics ranged from 2.2 to 25.3 and the zirconia ceramics from 5.5 to 15.1. There was an increase in the TP with a decrease in thickness, but the amount of change was material dependent. An exponential relationship with statistical significance (P<.05) between the TP and thickness was found for both glass ceramics and zirconia ceramics. The translucency of dental ceramics was significantly influenced by both material and thickness. The translucency of all materials increased exponentially as the thickness decreased. All of the zirconia ceramics evaluated in the present study showed some degree of translucency, which was less sensitive to thickness compared to that of the glass ceramics. Copyright © 2013 The Editorial Council of the Journal of Prosthetic Dentistry. Published by Mosby, Inc. All rights reserved.

Internal strain analysis of ceramics using scanning laser acoustic microscopy

NASA Technical Reports Server (NTRS)

Kent, Renee M.

1993-01-01

Quantitative studies of material behavior characteristics are essential for predicting the functionality of a material under its operating conditions. A nonintrusive methodology for measuring the in situ strain of small dimeter (to 11 microns) ceramic fibers under uniaxial tensile loading and the local internal strains of ceramics and ceramic composites under flexural loading is introduced. The strain measurements and experimentally observed mechanical behavior are analyzed in terms of the microstructural development and fracture behavior of each test specimen evaluated. Measurement and analysis of Nicalon silicon carbide (SiC) fiber (15 microns diameter) indicate that the mean elastic modulus of the individual fiber is 185.3 GPa. Deviations observed in the experimentally determined elastic modulus values between specimens were attributed to microstructural variations which occur during processing. Corresponding variations in the fracture surface morphology were also observed. The observed local mechanical behavior of a lithium alumino-silicate (LAS) glass ceramic, a LAS/SiC monofilament composite, and a calcium alumino-silicate (CAS)/SiC fully reinforced composite exhibits nonlinearities and apparent hysteresis due to the subcritical mechanical loading. Local hysteresis in the LAS matrices coincided with the occurrence of multiple fracture initiation sites, localized microcracking, and secondary cracking. The observed microcracking phenomenon was attributed to stress relaxation of residual stresses developed during processing, and local interaction of the crack front with the microstructure. The relaxation strain and stress predicted on apparent mechanical hysteresis effects were defined and correlated with the magnitude of the measured fracture stress for each specimen studied. This quantitative correlation indicated a repeatable measure of the stress at which matrix microcracking occurred for stress relief of each material system. Stress relaxation occurred prior to the onset of steady state cracking conditions. The relaxation stress occurred at 18.5 percent of the fracture stress in LAS and 11.0 percent of the yield stress in CAS/SiC. The relaxation stress ratio was dependent upon the dominant fracture mode of the LAS/SiC specimens. Relaxation stress ratios greater than 0.30 were observed for specimens which fractured due to shear at the fiber matrix interface; specimens which fracture due to tensile cracking had relaxation stress ratios less than 0.30. The stress relaxation ratio appeared to be a specific characteristic of the glass ceramic material. The measured stress relaxation for LAS indicated a measure of the inherent residual stresses in the material due to processing and suggested localized toughening mechanisms for brittle material structures.

Eccentric loading of microtensile specimens

NASA Technical Reports Server (NTRS)

Trapp, Mark A.

2004-01-01

Ceramic materials have a lower density than most metals and are capable of performing at extremely high temperatures. The utility of these materials is obvious; however, the fracture strength of brittle materials is not easily predicted and often varies greatly. Characteristically, brittle materials lack ductility and do not yield as other materials. Ceramics materials are naturally populated with microscopic cracks due to fabrication techniques. Upon application of a load, stress concentration occurs at the root of these cracks and fracture will eventually occur at some not easily predicted strength. In order to use ceramics in any application some design methodology must exist from which a component can be placed into service. This design methodology is CARES/LIFE (Ceramics Analysis and Reliability Evaluation of Structures) which has been developed and refined at NASA over the last several decades. The CARES/LIFE computer program predicts the probability of failure of a ceramic component over its service life. CARES combines finite element results from a commercial FE (finite element) package such as ANSYS and experimental results to compute the abovementioned probability of failure. Over the course of several tests CARES has had great success in predicting the life of various ceramic components and has been used throughout industry. The latest challenge is to verify that CARES is valid for MEMS (Micro-Electro Mechanical Systems). To investigate a series of microtensile specimens were fractured in the laboratory. From this data, material parameters were determined and used to predict a distribution of strength for other specimens that exhibit a known stress concentration. If the prediction matches the experimental results then these parameters can be applied to a desired component outside of the laboratory. During testing nearly half of the tensile Specimens fractured at a location that was not expected and hence not captured in the FE model. It has been my duty to investigate the nature of this phenomenon in hopes of finding a better correlation between theory and empirical results. To investigate I built complete FE models of all of the tensile specimens using ANSYS. It is suspected that some misalignment naturally occurs during testing and thus additional bending stresses are present in the specimens. I modeled this eccentric loading and ran several FE trials using ANSYS/PDS (a probabilistic design system in ANSYS). My objective this summer has been familiarize myself with the CARES/LIFE program in hopes of using it in conjunction with ANSYS to help verify that CARES is applicable to MEMS-scale (greater that 1 micron, less than 1 millimeter) components.

In vitro adherence of oral streptococci to zirconia core and veneering glass-ceramics.

PubMed

Rosentritt, Martin; Behr, Michael; Bürgers, Ralf; Feilzer, Albert J; Hahnel, Sebastian

2009-10-01

Plaque formation on dental ceramics may cause gingival inflammation and secondary caries. This in vitro study compared the susceptibility of various dental ceramics to adhere oral streptococci, and verified the influence of substratum surface roughness and surface hydrophobicity. Three zirconia ceramic materials and three veneering glass-ceramics were investigated. Fifteen test specimens were prepared for each material, polished, and surface roughness and hydrophobicity were determined. After incubation with artificial saliva (2 h, 37 degrees C) for pellicle formation, specimens were incubated with suspensions of Streptococcus gordonii DSMZ 6777, Streptococcus mutans DSMZ 20523, Streptococcus oralis DSMZ 20627, or Streptococcus sanguinis DSMZ 20068, respectively, for 2.5 h at 37 degrees C. Adherent bacteria were quantified using a fluorescence dye for viable cell quantification (Alamar Blue/Resazurin). Statistical analysis was performed using one- and two-way ANOVA and the Tukey-Kramer multiple comparison test for post hoc analysis (alpha < 0.05). Surface roughness and surface hydrophobicity differed significantly among the various ceramics; protein coating hydrophilized the surfaces, and led to a homogenization of the surface hydrophobicity of the various ceramics. Before protein coating, almost similar relative fluorescence intensities indicating similar adhesion of streptococci were found for the various ceramics; more distinct differences were observed after protein coating. Correlations between surface parameters and streptococcal adhesion were poor. Within the limitations of these experiments, the findings of this in vitro study indicate only little differences between zirconia and glass ceramic with regard to streptococcal adhesion. Judging from these results, it is unlikely that exposed zirconia surfaces yield more plaque than glass ceramic surfaces in vivo. (c) 2009 Wiley Periodicals, Inc.

Characteristics of solder joints under fatigue loads using piezomechanical actuation

NASA Astrophysics Data System (ADS)

Shim, Dong-Jin; Spearing, S. Mark

2003-07-01

Crack initiation and growth characteristics of solder joints under fatigue loads are investigated using piezomechanical actuation. Cracks in solder joints, which can cause failure in microelectronics components, are induced via piezoelectricity in piezo-ceramic bonded joints. Lead-zirconate-titanate ceramic plates and eutectic Sn-Pb solder bonded in a double-lap shear configuration are used in the investigation. Electric field across each piezo-ceramic plate is applied such that shear stresses/strains are induced in the solder joints. The experiments show that cracks initiate in the solder joints around defects such as voids and grow in length until they coalesce with other cracks from adjacent voids. These observations are compared with the similar thermal cycling tests from the literature to show feasibility and validity of the current method in investigating the fatigue characteristics of solder joints. In some specimens, cracks in the piezo-ceramic plates are observed, and failure in the specimens generally occurred due to piezo-ceramic plate fracture. The issues encountered in implementing this methodology such as low actuation and high processing temperatures are further discussed.

Comparative study of flexural strength test methods on CAD/CAM Y-TZP dental ceramics

PubMed Central

Xu, Yongxiang; Han, Jianmin; Lin, Hong; An, Linan

2015-01-01

Clinically, fractures are the main cause of computer-aided design and computer-aided manufacturing (CAD/CAM) 3 mol%-yttria-stabilized tetragonal zirconia polycrystal (Y-TZP) all-ceramic dental restorations failure because of repetitive occlusal loading. The goal of this work is to study the effect of test methods and specimen’s size on the flexural strength of five ceramic products. Both bi-axial flexure test (BI) and uni-axial flexure tests (UNI), including three-point flexure test (3PF) and four-point flexure test (4PF), are used in this study. For all five products, the flexural strength is as follows: BI > 3PF > 4PF. Furthermore, specimens with smaller size (3PF-s) have higher values than the bigger ones (3PF). The difference between BI and UNI resulted from the edge flaws in ceramic specimens. The relationship between different UNI (including 3PF-s, 3PF and 4PF) can be explained according to Weibull statistical fracture theory. BI is recommended to evaluate the flexural strength of CAD/CAM Y-TZP dental ceramics. PMID:26816646

Effect of Contact Damage on the Strength of Ceramic Materials.

DTIC Science & Technology

1982-10-01

variables that are important to erosion, and a multivariate , linear regression analysis is used to fit the data to the dimensional analysis. The...of Equations 7 and 8 by a multivariable regression analysis (room tem- perature data) Exponent Regression Standard error Computed coefficient of...1980) 593. WEAVER, Proc. Brit. Ceram. Soc. 22 (1973) 125. 39. P. W. BRIDGMAN, "Dimensional Analaysis ", (Yale 18. R. W. RICE, S. W. FREIMAN and P. F

[Interface bond and compatibility between Mark II machining ceramic and vita VM9 veneering porcelain].

PubMed

Liu, Tian-Shuang; Li, Zhen-Chun; Chen, Xiao-Dong

2009-04-01

To investigate the interface bond and thermal compatibility between Mark II machining ceramic and Vita VM9 veneering porcelain. A bar shaped specimen (30 mm x 15 mm x 1 mm in size) of Mark II block was prepared, with 0.5 mm-deep notch (vertical to the long axis of specimen) at the middle of the bottom surface. The upper surface was veneered with 0.3 mm VM9 dentin base porcelain. Then the specimen was fractured from the notching site and the fracture surface was examined under scanning electron microscope (SEM) and electron microprobe analyzer (EMPA) with electron beam of 1 microm in diameter. Another ten specimens (30 mm x 15 mm x 1.5 mm in size) were fabricated and the temperature of thermal shock resistance were tested. SEM observation showed tight bond between these two materials and EMPA results showed penetration of Al element from Mark II block into veneering porcelain and Ca element from veneering porcelain into Mark II block occurred after sintering baking. The average temperature of thermal shock resistance for specimens in this study was (194.0+/-10.3) degrees C. Cracks were mainly distributed in veneering porcelain. Chemical bond exists between the Mark II machining ceramic and Vita VM9 veneering porcelain, and there is good thermal compatibility between them.

Bone bonding in bioactive glass ceramics combined with a new synthesized agent TAK-778.

PubMed

Kato, H; Neo, M; Tamura, J; Nakamura, T

2001-11-01

We studied the stimulatory effects of TAK-778, a new synthetic 3-benzothiepin derivative that promotes osteoblast differentiation, in the bonding of bone to bioactive glass ceramic implants in rabbit tibiae. Smooth-surfaced, rectangular plates (15 x 10 x 2 mm) made of apatite-wollastonite-containing glass ceramic were implanted bilaterally into the proximal metaphyses of rabbit tibiae. Sustained-release microcapsules containing TAK-778 were packed into the medullary cavity in one limb and untreated microcapsules were packed into the contralateral limb to serve as a paired control. At 4, 8, and 16 weeks after implantation, bonding at the bone/implant interfaces was evaluated using a detaching test and histological examination of undecalcified specimens. The tensile failure load increased during weeks 4 to 16 in both groups; the tensile failure load in the TAK-778-treated group was significantly greater than that in the control group at each interval after implantation. Histologically, the TAK-778-treated specimens showed greater active new bone formation mainly in the medullary cavity and more extensive bonding between the implant and bone than the untreated specimens. The results of this study suggest that adding the bone formation-promoting TAK-778 to bioactive glass ceramic implants may significantly accelerate bone apposition to the implants and improve the bonding process at the interface. This would help to establish earlier and stronger bonding of orthopedic ceramic implants to the surrounding bone tissue. Copyright 2001 John Wiley & Sons, Inc.

Fabrication of Silicon Nitride Dental Core Ceramics with Borosilicate Veneering material

NASA Astrophysics Data System (ADS)

Wananuruksawong, R.; Jinawath, S.; Padipatvuthikul, P.; Wasanapiarnpong, T.

2011-10-01

Silicon nitride (Si3N4) ceramic is a great candidate for clinical applications due to its high fracture toughness, strength, hardness and bio-inertness. This study has focused on the Si3N4 ceramic as a dental core material. The white Si3N4 was prepared by pressureless sintering at relative low sintering temperature of 1650 °C in nitrogen atmosphere. The coefficient of thermal expansion (CTE) of Si3N4 ceramic is lower than that of Zirconia and Alumina ceramic which are popular in this field. The borosilicate glass veneering was employed due to its compatibility in thermal expansion. The sintered Si3N4 specimens represented the synthetic dental core were paintbrush coated by a veneer paste composed of borosilicate glass powder (<150 micrometer, Pyrex) with 5 wt% of zirconia powder (3 wt% Y2O3 - partial stabilized zirconia) and 30 wt% of polyvinyl alcohol (5 wt% solution). After coating the veneer on the Si3N4 specimens, the firing was performed in electric tube furnace between 1000-1200°C. The veneered specimens fired at 1100°C for 15 mins show good bonding, smooth and glossy without defect and crazing. The veneer has thermal expansion coefficient as 3.98×10-6 °C-1, rather white and semi opaque, due to zirconia addition, the Vickers hardness as 4.0 GPa which is closely to the human teeth.

Shockless spalling damage of alumina ceramic

NASA Astrophysics Data System (ADS)

Erzar, B.; Buzaud, E.

2012-05-01

Ceramic materials are commonly used to build multi-layer armour. However reliable test data is needed to identify correctly models and to be able to perform accurate numerical simulation of the dynamic response of armour systems. In this work, isentropic loading waves have been applied to alumina samples to induce spalling damage. The technique employed allows assessing carefully the strain-rate at failure and the dynamic strength. Moreover, specimens have been recovered and analysed using SEM. In a damaged but unbroken specimen, interactions between cracks has been highlighted illustrating the fragmentation process.

Surface degradation of glass ceramics after exposure to acidulated phosphate fluoride.

PubMed

Ccahuana, Vanessa Zulema S; Ozcan, Mutlu; Mesquita, Alfredo Mikail Melo; Nishioka, Renato Sussumo; Kimpara, Estevão Tomomitsu; Bottino, Marco Antonio

2010-01-01

This study evaluated the surface degradation effect of acidulated phosphate fluoride (APF) gel exposure on the glassy matrix ceramics as a function of time. Disc-shaped ceramic specimens (N = 120, 10/per ceramic material) were prepared in stainless steel molds (inner diameter: 5 mm, height: 2 mm) using 6 dental ceramics: 3 indicated for ceramic-fused-to-metal (Vita Omega 900, Carmen and Vita Titankeramik), 2 for all-ceramic (Vitadur Alpha and Finesse Low Fusing) and 1 for both types of restorations (IPS d.SIGN). The specimens were wet ground finished, ultrasonically cleaned and auto-glazed. All specimens were subjected to calculation of percentage of mass loss, surface roughness analysis and topographical description by scanning electron microscopy (SEM) before (0 min) and after exposure to 1.23 % APF gel for 4 min and 60 min representing short- and long-term etching effect, respectively. The data were analyzed using two-way ANOVA with repeated measures and Tukey's test (a=0.05). Significant effect of the type of the ceramics (p=0.0000, p=0.0031) and exposure time (p=0.0000) was observed in both surface roughness and percentage of mass loss values, respectively. The interaction factor between both parameters was also significant for both parameters (p=0.0904, p=0.0258). Both 4 min (0.44+/-0.1 - 0.81+/-0.2 microm) and 60 min (0.66+/-0.1 - 1.04+/-0.3 microm) APF gel exposure created significantly more surface roughness for all groups when compared to the control groups (0.33+/-0.2 - 0.68+/-0.2 microm) (p<0.05). There were no significant differences in percentage of mass loss between the ceramics at 4 min (p>0.05) but at 60 min exposure, IPS d.SIGN showed the highest percentage of mass loss (0.1151+/-0.11). The mean surface roughness for Vita Titankeramik (0.84+/-0.2 microm) and Finesse Low Fusing (0.74.+/-0.2 microm) was significantly higher than those of the other ceramics (0.59+/-0.1 microm - 0.49+/-0.1 microm) and Vita Titankeramik (p<0.05) regardless of the exposure time. A positive correlation was found between surface roughness and percentage of mass loss for all ceramic materials [(r=0.518 (Vitadur Alpha), r=0.405 (Vita Omega 900), r=0.580 (Carmen), r=0.687 (IPS d.SIGN), r=0.442 (Finesse Low Fusing), r=0.572 (Vita Titankeramik), Pearson's correlation coefficient)]. The qualitative SEM analysis showed evidence of corrosive attack on all of ceramics at varying degrees. The ceramics indicated for either metal-ceramic or all-ceramic restorations were all vulnerable to surface texture changes and mass loss after short-term and long-term APF gel exposure.

A high temperature testing system for ceramic composites

NASA Technical Reports Server (NTRS)

Hemann, John

1994-01-01

Ceramic composites are presently being developed for high temperature use in heat engine and space power system applications. The operating temperature range is expected to be 1090 to 1650 C (2000 F to 3000 F). Very little material data is available at these temperatures and, therefore, it is desirable to thoroughly characterize the basic unidirectional fiber reinforced ceramic composite. This includes testing mainly for mechanical material properties at high temperatures. The proper conduct of such characterization tests requires the development of a tensile testing system includes unique gripping, heating, and strain measuring devices which require special considerations. The system also requires an optimized specimen shape. The purpose of this paper is to review various techniques for measuring displacements or strains, preferably at elevated temperatures. Due to current equipment limitations it is assumed that the specimen is to be tested at a temperature of 1430 C (2600F) in an oxidizing atmosphere. For the most part, previous high temperature material characterization tests, such as flexure and tensile tests, have been performed in inert atmospheres. Due to the harsh environment in which the ceramic specimen is to be tested, many conventional strain measuring techniques can not be applied. Initially a brief description of the more commonly used mechanical strain measuring techniques is given. Major advantages and disadvantages with their application to high temperature tensile testing of ceramic composites are discussed. Next, a general overview is given for various optical techniques. Advantages and disadvantages which are common to these techniques are noted. The optical methods for measuring strain or displacement are categorized into two sections. These include real-time techniques. Finally, an optical technique which offers optimum performance with the high temperature tensile testing of ceramic composites is recommended.

Bonding of Resin Cement to Zirconia with High Pressure Primer Coating

PubMed Central

Wang, Ying-jie; Jiao, Kai; Liu, Yan; Zhou, Wei; Shen, Li-juan; Fang, Ming; Li, Meng; Zhang, Xiang; Tay, Franklin R.; Chen, Ji-hua

2014-01-01

Objectives To investigate the effect of air-drying pressure during ceramic primer coating on zirconia/resin bonding and the surface characteristics of the primed zirconia. Methods Two ceramic primers (Clearfil Ceramic Primer, CCP, Kuraray Medical Inc. and Z-Prime Plus, ZPP, Bisco Inc.) were applied on the surface of air-abraded zirconia (Katana zirconia, Noritake) and dried at 4 different air pressures (0.1–0.4 MPa). The primed zirconia ceramic specimens were bonded with a resin-based luting agent (SA Luting Cement, Kuraray). Micro-shear bond strengths of the bonded specimens were tested after 3 days of water storage or 5,000× thermocycling (n = 12). Failure modes of the fractured specimens were examined with scanning electron miscopy. The effects of air pressure on the thickness of the primer layers and the surface roughness (Sa) of primed zirconia were evaluated using spectroscopic ellipsometry (n = 6), optical profilometry and environmental scanning electron microscopy (ESEM) (n = 6), respectively. Results Clearfil Ceramic Primer air-dried at 0.3 and 0.4 MPa, yielding significantly higher µSBS than gentle air-drying subgroups (p<0.05). Compared to vigorous drying conditions, Z-Prime Plus air-dried at 0.2 MPa exhibited significantly higher µSBS (p<0.05). Increasing air-drying pressure reduced the film thickness for both primers. Profilometry measurements and ESEM showed rougher surfaces in the high pressure subgroups of CCP and intermediate pressure subgroup of ZPP. Conclusion Air-drying pressure influences resin/zirconia bond strength and durability significantly. Higher air-drying pressure (0.3-0.4 MPa) for CCP and intermediate pressure (0.2 MPa) for ZPP are recommended to produce strong, durable bonds between resin cement and zirconia ceramics. PMID:24992678

Cross-sectional TEM specimen preparation for W/B{sub 4}C multilayer sample using FIB

DOE Office of Scientific and Technical Information (OSTI.GOV)

Mondal, Puspen, E-mail: puspen@rrcat.gov.in; Pradhan, P. C.; Tiwari, Pragya

2016-05-23

A recent emergence of a cross-beam scanning electron microscopy (SEM)/focused-ion-beam (FIB) system have given choice to fabricate cross-sectional transmission electron microscopy (TEM) specimen of thin film multilayer sample. A 300 layer pair thin film multilayer sample of W/B{sub 4}C was used to demonstrate the specimen lift-out technique in very short time as compared to conventional cross-sectional sample preparation technique. To get large area electron transparent sample, sample prepared by FIB is followed by Ar{sup +} ion polishing at 2 kV with grazing incident. The prepared cross-sectional sample was characterized by transmission electron microscope.

Dynamic fracture responses of alumina and two ceramic composites

NASA Technical Reports Server (NTRS)

Yang, Kwan-Ho; Kobayashi, Albert S.

1990-01-01

A hybrid experimental-numerical procedure was used to characterize the dynamic fracture response of Al2O3 and TiB2-particulate/SiC-matrix and SiC-whisker/Al2O3-matrix composites. Unlike metals and polymers, dynamic arrest stress intensity factors (SIFs) did not exist in the monolithic ceramics and the two ceramic composites considered. Thus a running crack in these materials cannot be arrested by lowering the driving force, i.e., the dynamic SIF. Fractography study of the alumina specimens showed that the area of transgranular failure varied from about 3 percent to about 16 percent for rapid crack extensions in statically and impact loaded specimens, respectively. The influence of kinematic constraints which enforces transgranular flat crack extension, despite the higher fracture energy of transgranular fracture, is discussed.

Influence of curing protocol and ceramic composition on the degree of conversion of resin cement.

PubMed

Lanza, Marcos Daniel Septimio; Andreeta, Marcello Rubens Barsi; Pegoraro, Thiago Amadei; Pegoraro, Luiz Fernando; Carvalho, Ricardo Marins De

2017-01-01

Due to increasing of aesthetic demand, ceramic crowns are widely used in different situations. However, to obtain long-term prognosis of restorations, a good conversion of resin cement is necessary. To evaluate the degree of conversion (DC) of one light-cure and two dual-cure resin cements under a simulated clinical cementation of ceramic crowns. Prepared teeth were randomly split according to the ceramic's material, resin cement and curing protocol. The crowns were cemented as per manufacturer's directions and photoactivated either from occlusal suface only for 60 s; or from the buccal, occlusal and lingual surfaces, with an exposure time of 20 s on each aspect. After cementation, the specimens were stored in deionized water at 37°C for 7 days. Specimens were transversally sectioned from occlusal to cervical surfaces and the DC was determined along the cement line with three measurements taken and averaged from the buccal, lingual and approximal aspects using micro-Raman spectroscopy (Alpha 300R/WITec®). Data were analyzed by 3-way ANOVA and Tukey test at =5%. Statistical analysis showed significant differences among cements, curing protocols and ceramic type (p<0.001). The curing protocol 3x20 resulted in higher DC for all tested conditions; lower DC was observed for Zr ceramic crowns; Duolink resin cement culminated in higher DC regardless ceramic composition and curing protocol. The DC of resin cement layers was dependent on the curing protocol and type of ceramic.

Stress and Reliability Analysis of a Metal-Ceramic Dental Crown

NASA Technical Reports Server (NTRS)

Anusavice, Kenneth J; Sokolowski, Todd M.; Hojjatie, Barry; Nemeth, Noel N.

1996-01-01

Interaction of mechanical and thermal stresses with the flaws and microcracks within the ceramic region of metal-ceramic dental crowns can result in catastrophic or delayed failure of these restorations. The objective of this study was to determine the combined influence of induced functional stresses and pre-existing flaws and microcracks on the time-dependent probability of failure of a metal-ceramic molar crown. A three-dimensional finite element model of a porcelain fused-to-metal (PFM) molar crown was developed using the ANSYS finite element program. The crown consisted of a body porcelain, opaque porcelain, and a metal substrate. The model had a 300 Newton load applied perpendicular to one cusp, a load of 30ON applied at 30 degrees from the perpendicular load case, directed toward the center, and a 600 Newton vertical load. Ceramic specimens were subjected to a biaxial flexure test and the load-to-failure of each specimen was measured. The results of the finite element stress analysis and the flexure tests were incorporated in the NASA developed CARES/LIFE program to determine the Weibull and fatigue parameters and time-dependent fracture reliability of the PFM crown. CARES/LIFE calculates the time-dependent reliability of monolithic ceramic components subjected to thermomechanical and/Or proof test loading. This program is an extension of the CARES (Ceramics Analysis and Reliability Evaluation of Structures) computer program.

Utilization of Electric Arc Furnace Dust as raw material for the production of ceramic and concrete building products.

PubMed

Sikalidis, Constantine; Mitrakas, Manassis

2006-01-01

The up to 20 wt% addition of the Electric Arc Furnace Dust (EAFD) hazardous waste on the properties of extruded clay-based ceramic building products fired at various temperatures (850 to 1050 degrees C), as well as of dolomite-concrete products was investigated. Chemical, mineralogical and particle size distribution analyses were performed in order to characterize the used EAFD. The results showed that the ceramic specimens prepared had water absorption, firing shrinkage, apparent density, mechanical strength, colour and leaching behaviour within accepted limits. Addition of 7.5 to 15 wt% EAFD presented improved properties, while 20 wt% seems to be the upper limit. Dolomite-concrete specimens were prepared by vibration and press-forming of mixtures containing cement, sand, dolomite, EAFD and water. Modulus of rupture values were significantly increased by the addition of EAFD. The leaching tests showed stabilization of all toxic metals within the sintered ceramic structure, while the leaching behaviour of lead in dolomite-concrete products needs further detailed study.

Characterization of TiN coating layers using ultrasonic backward radiation.

PubMed

Song, Sung-Jin; Yang, Dong-Joo; Kim, Hak-Joon; Kwon, Sung D; Lee, Young-Ze; Kim, Ji-Yoon; Choi, Song-Chun

2006-12-22

Since ceramic layers coated on machinery components inevitably experience the changes in their properties it is necessary to evaluate the characteristics of ceramic coating layers nondestructively for the reliable use of coated components and the remaining life prediction. To address such a need, in the present study, the ultrasonic backward radiation technique is applied to examine the very thin TiN ceramic layers coated on AISI 1045 steel or austenitic 304 steel substrate. Specifically, the ultrasonic backward radiation profiles have been measured with variations in specimen preparation conditions such as coating layer thickness and sliding loading. In the experiments performed in the current study, the peak angle and the peak amplitude of ultrasonic backward radiation profile varied sensitively according to two specimen preparation conditions. In fact, this result demonstrates a high possibility of the ultrasonic backward radiation as an effective tool for the nondestructive characterization of the TiN ceramic coating layers even in such a thin regime.

Effects of Different Surface Treatment Methods and MDP Monomer on Resin Cementation of Zirconia Ceramics an In Vitro Study.

PubMed

Tanış, Merve Çakırbay; Akçaboy, Cihan

2015-01-01

Resin cements are generally preferred for cementation of zirconia ceramics. Resin bonding of zirconia ceramics cannot be done with the same methods of traditional ceramics because zirconia is a silica-free material. In recent years, many methods have been reported in the literature to provide the resin bonding of zirconia ceramics. The purpose of this in vitro study is to evaluate effects of different surface treatments and 10-metacryloxydecyl dihydrogen phosphate (MDP) monomer on shear bond strength between zirconia and resin cement. 120 zirconia specimens were treated as follows: Group I: sandblasting, group II: sandblasting + tribochemical silica coating + silane, group III: sandblasting + Nd:YAG (neodymium: yttrium-aluminum-garnet) laser. One specimen from each group was evaluated under scanning electron microscope (SEM). Specimens in each group were bonded either with conventional resin cement Variolink II or with a MDP containing resin cement Panavia F2.0. Subgroups of bonded specimens were stored in distilled water (37°C) for 24 hours or 14 days. Following water storage shear bond strength test was performed at a crosshead speed of 1 mm/min in a universal test machine. Then statistical analyses were performed. Highest shear bond strength values were observed in group II. No significant difference between group I and III was found when Panavia F2.0 resin cement was used. When Variolink II resin cement was used group III showed significantly higher bond strength than group I. In group I, Panavia F2.0 resin cement showed statistically higher shear bond strength than Variolink II resin cement. In group II no significant difference was found between resin cements. No significant difference was found between specimens stored in 37°C distilled water for 24 hours and 14 days. In group I surface irregularities with sharp edges and grooves were observed. In group II less roughened surface was observed with silica particles. In group III surface microcracks connecting each other were observed. Tribochemical silica coating is an effective method for achieving an acceptable bond between zirconia and resin cement. Use of a MDP monomer containing resin cement increases the bond strength of sandblasted zirconia.

Effect of ceramic thickness and shade on mechanical properties of a resin luting agent.

PubMed

Passos, Sheila Pestana; Kimpara, Estevão Tomomitsu; Bottino, Marco Antonio; Rizkalla, Amin S; Santos, Gildo Coelho

2014-08-01

This study aimed to investigate the influence of ceramic thickness and shade on the Knoop hardness and dynamic elastic modulus of a dual-cured resin cement. Six ceramic shades (Bleaching, A1, A2, A3, A3.5, B3) and two ceramic thicknesses (1 mm, 3 mm) were evaluated. Disk specimens (diameter: 7 mm; thickness: 2 mm) of the resin cement were light cured under a ceramic block. Light-cured specimens without the ceramic block at distances of 1 and 3 mm were also produced. The Knoop hardness number (KHN), density, and dynamic Young's moduli were determined. Statistical analysis was conducted using ANOVA and a Tukey B rank order test (p = 0.05). The bleaching 1-mm-thick group exhibited significantly higher dynamic Young's modulus. Lower dynamic Young's moduli were observed for the 3-mm-thick ceramic groups compared to bleaching 3-mm-thick group, and no difference was found among the other 3-mm groups. For the KHN, when A3.5 3-mm-thick was used, the KHN was significantly lower than bleaching and A1 1-mm-thick ceramic; however, no difference was exhibited between the thicknesses of the same shade. The dual-cured resin cement studied irradiated through the 1-mm-thick ceramic with the lightest shade (bleaching ceramic) exhibited a better elastic modulus, and there was no effect in KHN of the resin cement when light cured under different ceramic shades and thicknesses (1 and 3 mm), except when the A3.5 3-mm-thick ceramic was used. Variolink II irradiated through ceramic with the lowest chroma exhibited the highest elastic modulus; therefore, the light activation method might not be the same for all clinical situations. © 2014 by the American College of Prosthodontists.

Influence of implant abutment material on the color of different ceramic crown systems.

PubMed

Dede, Doğu Ömür; Armağanci, Arzu; Ceylan, Gözlem; Celik, Ersan; Cankaya, Soner; Yilmaz, Burak

2016-11-01

Ceramics are widely used for anterior restorations; however, clinical color reproduction still constitutes a challenge particularly when the ceramic crowns are used on titanium implant abutments. The purpose of this in vitro study was to investigate the effect of implant abutment material on the color of different ceramic material systems. Forty disks (11×1.5 mm, shade A2) were fabricated from medium-opacity (mo) and high-translucency (ht) lithium disilicate (IPS e.max) blocks, an aluminous ceramic (VITA In-Ceram Alumina), and a zirconia (Zirkonzahn) ceramic system. Disks were fabricated to represent 3 different implant abutments (zirconia, gold-palladium, and titanium) and dentin (composite resin, A2 shade) as background (11×2 mm). Disk-shaped composite resin specimens in A2 shade were fabricated to represent the cement layer. The color measurements of ceramic specimens were made on composite resin abutment materials using a spectrophotometer. CIELab color coordinates were recorded, and the color coordinates measured on composite resin background served as the control group. Color differences (ΔE 00 ) between the control and test groups were calculated. The data were analyzed with 2-way analysis of variance (ANOVA) and compared with the Tukey HSD test (α=.05). The ceramics system, abutment material, and their interaction were significant for ΔE 00 values (P<.001). Clinically unacceptable results (ΔE 00 >2.25) were observed for lithium disilicate ceramics on titanium abutments (2.46-2.50). The ΔE 00 values of lithium disilicate ceramics for gold-palladium and titanium abutments were significantly higher than for other groups (P<.05). The color results (ΔE 00 >2.25) of an implant-supported lithium disilicate ceramic restoration may be clinically unacceptable if it is fabricated over a titanium abutment. Zirconia may be a more suitable abutment material for implant-supported ceramic restorations. Copyright © 2016 Editorial Council for the Journal of Prosthetic Dentistry. Published by Elsevier Inc. All rights reserved.

In vitro study of fracture load and fracture pattern of ceramic crowns: a finite element and fractography analysis.

PubMed

Campos, Roberto Elias; Soares, Carlos José; Quagliatto, Paulo S; Soares, Paulo Vinícius; de Oliveira, Osmir Batista; Santos-Filho, Paulo Cesar Freitas; Salazar-Marocho, Susana M

2011-08-01

This in vitro study investigated the null hypothesis that metal-free crowns induce fracture loads and mechanical behavior similar to metal ceramic systems and to study the fracture pattern of ceramic crowns under compressive loads using finite element and fractography analyses. Six groups (n = 8) with crowns from different systems were compared: conventional metal ceramic (Noritake) (CMC); modified metal ceramic (Noritake) (MMC); lithium disilicate-reinforced ceramic (IPS Empress II) (EMP); leucite-reinforced ceramic (Cergogold) (CERG); leucite fluoride-apatite reinforced ceramic (IPS d.Sign) (SIGN); and polymer crowns (Targis) (TARG). Standardized crown preparations were performed on bovine roots containing NiCr metal dowels and resin cores. Crowns were fabricated using the ceramics listed, cemented with dual-cure resin cement, and submitted to compressive loads in a mechanical testing machine at a 0.5-mm/min crosshead speed. Data were submitted to one-way ANOVA and Tukey tests, and fractured specimens were visually inspected under a stereomicroscope (20×) to determine the type of fracture. Maximum principal stress (MPS) distributions were calculated using finite element analysis, and fracture origin and the correlation with the fracture type were determined using fractography. Mean values of fracture resistance (N) for all groups were: CMC: 1383 ± 298 (a); MMC: 1691 ± 236 (a); EMP: 657 ± 153 (b); CERG: 546 ± 149 (bc); SIGN: 443 ± 126 (c); TARG: 749 ± 113 (b). Statistical results showed significant differences among groups (p < 0.05) represented by different lowercase letters. Metal ceramic crowns presented fracture loads significantly higher than the others. Ceramic specimens presented high incidence of fractures involving either the core or the tooth, and all fractures of polymer crown specimens involved the tooth in a catastrophic way. Based on stress and fractographic analyses it was determined that fracture occurred from the occlusal to the cervical direction. Within the limitations of this study, the results indicated that the use of ceramic and polymer crowns without a core reinforcement should be carefully evaluated before clinical use due to the high incidence of failure with tooth involvement. This mainly occurred for the polymer crown group, although the fracture load was higher than normal occlusal forces. High tensile stress concentrations were found around and between the occlusal loading points. Fractographic analysis indicated fracture originating from the load point and propagating from the occlusal surface toward the cervical area, which is the opposite direction of that observed in clinical situations. © 2011 by The American College of Prosthodontists.

Soviet Developments in High Temperature Ceramics No. 1, January-December 1975

DTIC Science & Technology

1976-02-25

in microstructure and granulometric composition of silicon nitride in the process of hot pressing were studied by optical and electron micrographic...and on the laboratory-made a-alumina specimens^have shown that densely- sintered ceramics can be produced by a simplified process using a- Al -O...dusting of the powdered ceramic materials, spinel slurry deposition and subsequent fusion by a plasma jet traveling along the coated surface at

Comparison of fracture resistance of pressable metal ceramic custom implant abutment with a commercially fabricated CAD/CAM zirconia implant abutment.

PubMed

Protopapadaki, Maria; Monaco, Edward A; Kim, Hyeong-Il; Davis, Elaine L

2013-11-01

The predictable nature of the hot pressing ceramic technique has several applications, but no study was identified that evaluated its application to the fabrication of custom implant abutments. The purpose of this study was to compare the fracture resistance of an experimentally designed pressable metal ceramic custom implant abutment (PR) with that of a duplicate zirconia abutment (ZR). Two groups of narrow platform (NP) (Nobel Replace) implant abutment specimens were fabricated (n=10). The experimental abutment (PR) had a metal substructure cast with ceramic alloy (Lodestar) and veneered with leucite pressable glass ceramic (InLine PoM). Each PR abutment was individually scanned and 10 duplicate CAD/CAM ZR abutments were fabricated for the control group. Ceramic crowns (n=20) with the average dimensions of a human lateral incisor were pressed with lithium disilicate glass ceramic (IPS e.max Press) and bonded on the abutments with a resin luting agent (Multilink Automix). The specimens were subjected to thermocycling, cyclic loading, and finally static loading to failure with a computer-controlled Universal Testing Machine. An independent t test (1 sided) determined whether the mean values of the fracture load differed significantly (α=.05) between the 2 groups. No specimen failed during cyclic loading. Upon static loading, the mean (SD) load to failure was significantly higher for the PR group (525.89 [143.547] N) than for the ZR group (413.70 [35.515] N) for internal connection narrow platform bone-level implants (P=.025). Failure was initiated at the screw and internal connection level for both groups. It is possible to fabricate PR abutments that are stronger than ZR abutments for Nobel Biocare internal connection NP bone-level implants. The screw and the internal connection are the weak links for both groups. Copyright © 2013 Editorial Council for the Journal of Prosthetic Dentistry. Published by Mosby, Inc. All rights reserved.

Wear properties of dental ceramics and porcelains compared with human enamel.

PubMed

D'Arcangelo, Camillo; Vanini, Lorenzo; Rondoni, Giuseppe D; De Angelis, Francesco

2016-03-01

Contemporary pressable and computer-aided design/manufacturing (CAD/CAM) ceramics exhibit good mechanical and esthetic properties. Their wear resistance compared with human enamel and traditional gold based alloys needs to be better investigated. The purpose of this in vitro study was to compare the 2-body wear resistance of human enamel, gold alloy, and 5 different dental ceramics, including a recently introduced zirconia-reinforced lithium silicate ceramic (Celtra Duo). Cylindrical specimens were fabricated from a Type III gold alloy (Aurocast8), 2 hot pressed ceramics (Imagine PressX, IPS e.max Press), 2 CAD/CAM ceramics (IPS e.max CAD, Celtra Duo), and a CAD/CAM feldspathic porcelain (Vitablocs Mark II) (n=10). Celtra Duo was tested both soon after grinding and after a subsequent glaze firing cycle. Ten flat human enamel specimens were used as the control group. All specimens were subjected to a 2-body wear test in a dual axis mastication simulator for 120000 loading cycles against yttria stabilized tetragonal zirconia polycrystal cusps. The wear resistance was analyzed by measuring the vertical substance loss (mm) and the volume loss (mm(3)). Antagonist wear (mm) was also recorded. Data were statistically analyzed with 1-way ANOVA tests (α=.05). The wear depth (0.223 mm) of gold alloy was the closest to that of human enamel (0.217 mm), with no significant difference (P>.05). The greatest wear was recorded on the milled Celtra Duo (wear depth=0.320 mm), which appeared significantly less wear resistant than gold alloy or human enamel (P<.05). The milled and not glazed Celtra Duo showed a small but significantly increased wear depth compared with Aurocast8 and human enamel. Wear depth and volumetric loss for the glaze-fired Celtra Duo and for the other tested ceramics did not statistically differ in comparison with the human enamel. Copyright © 2016 Editorial Council for the Journal of Prosthetic Dentistry. Published by Elsevier Inc. All rights reserved.

The effect of silane applied to glass ceramics on surface structure and bonding strength at different temperatures

PubMed Central

Eraslan, Oguz

2016-01-01

PURPOSE To evaluate the effect of various surface treatments on the surface structure and shear bond strength (SBS) of different ceramics. MATERIALS AND METHODS 288 specimens (lithium-disilicate, leucite-reinforced, and glass infiltrated zirconia) were first divided into two groups according to the resin cement used, and were later divided into four groups according to the given surface treatments: G1 (hydrofluoric acid (HF)+silane), G2 (silane alone-no heat-treatment), G3 (silane alone-then dried with 60℃ heat-treatment), and G4 (silane alone-then dried with 100℃ heat-treatment). Two different adhesive luting systems were applied onto the ceramic discs in all groups. SBS (in MPa) was calculated from the failure load per bonded area (in N/mm2). Subsequently, one specimen from each group was prepared for SEM evaluation of the separated-resin–ceramic interface. RESULTS SBS values of G1 were significantly higher than those of the other groups in the lithium disilicate ceramic and leucite reinforced ceramic, and the SBS values of G4 and G1 were significantly higher than those of G2 and G3 in glass infiltrated zirconia. The three-way ANOVA revealed that the SBS values were significantly affected by the type of resin cement (P<.001). FIN ceramics had the highest rate of cohesive failure on the ceramic surfaces than other ceramic groups. AFM images showed that the surface treatment groups exhibited similar topographies, except the group treated with HF. CONCLUSION The heat treatment was not sufficient to achieve high SBS values as compared with HF acid etching. The surface topography of ceramics was affected by surface treatments. PMID:27141250

Fracture Resistance and Mode of Failure of Ceramic versus Titanium Implant Abutments and Single Implant-Supported Restorations.

PubMed

Sghaireen, Mohd G

2015-06-01

The material of choice for implant-supported restorations is affected by esthetic requirements and type of abutment. This study compares the fracture resistance of different types of implant abutments and implant-supported restorations and their mode of failure. Forty-five Oraltronics Pitt-Easy implants (Oraltronics Dental Implant Technology GmbH, Bremen, Germany) (4 mm diameter, 10 mm length) were embedded in clear autopolymerizing acrylic resin. The implants were randomly divided into three groups, A, B and C, of 15 implants each. In group A, titanium abutments and metal-ceramic crowns were used. In group B, zirconia ceramic abutments and In-Ceram Alumina crowns were used. In group C, zirconia ceramic abutments and IPS Empress Esthetic crowns were used. Specimens were tested to failure by applying load at 130° from horizontal plane using an Instron Universal Testing Machine. Subsequently, the mode of failure of each specimen was identified. Fracture resistance was significantly different between groups (p < .05). The highest fracture loads were associated with metal-ceramic crowns supported by titanium abutments (p = .000). IPS Empress crowns supported by zirconia abutments had the lowest fracture loads (p = .000). Fracture modes of metal-ceramic crowns supported by titanium abutments included screw fracture and screw bending. Fracture of both crown and abutment was the dominant mode of failure of In-Ceram/IPS Empress crowns supported by zirconia abutments. Metal-ceramic crowns supported by titanium abutments were more resistant to fracture than In-Ceram crowns supported by zirconia abutments, which in turn were more resistant to fracture than IPS Empress crowns supported by zirconia abutments. In addition, failure modes of restorations supported by zirconia abutments were more catastrophic than those for restorations supported by titanium abutments. © 2013 Wiley Periodicals, Inc.

Internal adaptation, marginal accuracy and microleakage of a pressable versus a machinable ceramic laminate veneers.

PubMed

Aboushelib, Moustafa Nabil; Elmahy, Waleed AbdelMeguid; Ghazy, Mohammed Hamed

2012-08-01

The aim of this study was to evaluate the internal adaptation and marginal properties of ceramic laminate veneers fabricated using pressable and machinable CAD/CAM techniques. 40 ceramic laminate veneers were fabricated by either milling ceramic blocks using a CAD/CAM system (group 1 n=20) or press-on veneering using lost wax technique (group 2 n=20). The veneers were acid etched using hydrofluoric acid, silanated, and cemented on their corresponding prepared teeth. All specimens were stored under water (37 °C) for 60 days, then received thermocycling (15,000 cycles between 5 and 55 °C and dwell time of 90 s) followed by cyclic loading (100,000 cycles between 50 and 100 N) before immersion in basic fuchsine dye for 24 h. Half of the specimens in each group were sectioned in labio-lingual direction and the rest were horizontally sectioned using precision cutting machine (n=10). Dye penetration, internal cement film thickness, and vertical and horizontal marginal gaps at the incisal and cervical regions were measured (α=0.05). Pressable ceramic veneers demonstrated significantly lower (F=8.916, P<0.005) vertical and horizontal marginal gaps at the cervical and incisal margins and lower cement film thickness (F=50.921, P<0.001) compared to machinable ceramic veneers. The inferior marginal properties of machinable ceramic veneers were associated with significantly higher microleakage values. Pressable ceramic laminate veneers produced higher marginal adaptation, homogenous and thinner cement film thickness, and improved resistance to microleakage compared to machinable ceramic veneers. The manufacturing process influences internal and marginal fit of ceramic veneers. Therefore, dentist and laboratory technicians should choose a manufacturing process with careful consideration. Copyright © 2012 Elsevier Ltd. All rights reserved.

Effects of sol-gel processed silica coating on bond strength of resin cements to glass-infiltrated alumina ceramic.

PubMed

Xie, Haifeng; Wang, Xiaozu; Wang, Yu; Zhang, Feimin; Chen, Chen; Xia, Yang

2009-02-01

The aim of this study was to verify the effects of sol-gel processed silica coating on the bond strength between resin cement and glass-infiltrated aluminum oxide ceramic. Silica coatings were prepared on glass-infiltrated aluminum oxide ceramic surface via the sol-gel process. Atomic Force Microscope (AFM), Fourier Transmission Infrared spectrum (FTIR), and Energy Dispersive X-ray Spectroscopy (EDS) were used for coating characterization. Forty-eight blocks of glass-infiltrated aluminum oxide ceramic were fabricated. The ceramic surfaces were polished following sandblasting. Three groups of specimens (16 for each group) with different surface treatment were prepared. Group P: no treatment; group PO: treated with silane solution; group PTO: silica coating via sol-gel process, followed by silane application. Composite cylinders were luted with resin cement to the test specimens. Half of the specimens in each group were stored in distilled water for 24 h and the other half were stored in distilled water for 30 days before shear loading in a universal testing machine until failure. Selected ceramic surfaces were analyzed to identify the failure mode using a scanning electron microscopy (SEM). Nanostructured silica coatings were prepared on glass-infiltrated aluminum oxide ceramic surfaces by the sol-gel process. The silicon element on the ceramic surface increased significantly after the coating process. The mean shear bond strength values (standard deviation) before artificial aging were: group P: 1.882 +/- 0.156 MPa; group PO: 2.177 +/- 0.226 MPa; group PTO: 3.574 +/- 0.671 MPa. Statistically significant differences existed between group PTO and group P, and group PTO and groups PO. The failure mode for group P and group PO was adhesive, while group PTO was mixed. The mean shear bond strength values (standard deviation) after artificial aging were: group P: 1.594 +/- 0.111 MPa; group PO: 2.120 +/- 0.339 MPa; group PTO: 2.955 +/- 0.113 MPa. Statistically significant differences existed between each two groups after artificial aging, group P had the lowest bond durability, and group PTO had the highest bond durability. The sol-gel process is an effective way to prepare silica coating on dental glass-infiltrated alumina ceramic. Sol-gel processed silica coating can improve the resin bond strength of glass-infiltrated alumina ceramic.

Contrast ratios and masking ability of three types of ceramic veneers.

PubMed

Chu, Frederick C S; Chow, Tak W; Chai, John

2007-11-01

Although ceramic veneers have been proven to be clinically successful in longevity studies, there is little information on the contrast ratios and masking ability of the available ceramic systems because dental laboratory technology and expensive experimental equipment are required for the investigation. Moreover, the complexity in understanding how to evaluate translucent ceramic materials may also explain why information in this area is limited. The purpose of this study was to determine the contrast ratios and masking abilities of 3 types of all-ceramic veneers by measuring their luminance and color difference over white and black backgrounds. Disk-shaped specimens (8-mm diameter x 0.7-mm thickness) of Shade A2 (Vita Lumin) of 3 types of all-ceramic systems: Procera (n=8), Empress 2 (n=8), and Vitadur Alpha (n=10) were fabricated. The luminance (as Y) and color (as CIE L*a*b*) of the specimens were measured with a colorimeter. The contrast ratio (CR=Yb/Yw), defined as the ratio of illuminance (Y) of the test material when it is placed on the black background (Yb) to the illuminance of the same material when it is placed over a white background (Yw), was determined. The masking ability of a specimen was evaluated by calculating the color difference (DeltaE) of the veneers over white and black backgrounds. Both CR and DeltaE* data were analyzed with 1-way ANOVA and the Tukey HSD test (alpha=.05). The mean contrast ratios (SD) of Procera, Empress 2, and Vitadur Alpha specimens were 0.50 (0.02), 0.46 (0.05), and 0.39 (0.02), respectively. CR values were significantly different among the 3 materials (P<.001). Procera veneers had a significantly higher CR compared to Empress 2 (P=.01) or Vitadur Alpha (P=.01), whereas the CR of Empress 2 was significantly higher than that of Vitadur Alpha (P=.046). Color difference (DeltaE*) (SD) of Procera, Empress 2, and Vitadur Alpha specimens over black and white backgrounds were 24.46 (1.03), 25.80 (1.03), and 31.08 (1.19), respectively. DeltaE* values were statistically different among the 3 materials (P<.001). Vitadur Alpha specimens had significantly higher DeltaE* when compared with Procera (P<.001) or Empress 2 (P<.001), whereas DeltaE* values between Procera and Empress 2 were not significantly different (P=.331). Vitadur Alpha had significantly lower contrast ratio and poorer masking ability compared to Procera or Empress 2. The clinical application of Vitadur Alpha as a veneer material over discolored teeth is cautioned. Although the contrast ratio of Procera was significantly higher than that of Empress 2, the masking abilities of these materials were not significantly different. The clinical application of these 2 ceramics as a veneer material may still be limited when applied over intense tooth discoloration because neither can fully mask the color of a black background.

Synthesis, characterization, bioactivity and antibacterial studies of silver doped calcium borosilicate glass-ceramics

NASA Astrophysics Data System (ADS)

Kumar, Alesh; Mariappan, C. R.

2018-04-01

Bioactive glass-ceramics 45.8 mol% SiO- 45.8 CaO - 8.4 B2O3 doped with Ag2O were synthesized by sol-gel method. The glass-ceramic nature of samples was confirmed by X-ray diffraction (XRD) and transmission electron microscopy (TEM) analysis. Fourier transform infrared (FT-IR) spectra reveal the probable stretching and bending vibration modes of silicate and borate groups. UV-Visible spectra reveal the presence of Ag+ ions and metallic Ag in the glass matrix for Ag2O doped ceramic sample. Biocompatibility of the glass nature of samples was studied by soaking of samples in Dulbecco's Modified Eagle's Medium (DMEM) with subsequent XRD studies. It was found that bone-like apatite formation on the glasses after soaked in DMEM. Antibacterial studies of glass ceramics powder against gram positive and negative microorganisms were carried out.

Characterization of a polymer-infiltrated ceramic-network material

PubMed Central

Corazza, Pedro H.; Zhang, Yu

2015-01-01

Objectives To characterize the microstructure and determine some mechanical properties of a polymer-ingfiltrated ceramic-network (PICN) material (Vita Enamic, Vita Zahnfabrik) available for CAD–CAM systems. Methods Specimens were fabricated to perform quantitative and qualitative analyses of the material’s microstructure and to determine the fracture toughness (KIc), density (ρ), Poisson’s ratio (v) and Young’s modulus (E). KIc was determined using V-notched specimens and the short beam toughness method, where bar-shaped specimens were notched and 3-point loaded to fracture. ρ was calculated using Archimedes principle, and v and E were measured using an ultrasonic thickness gauge with a combination of a pulse generator and an oscilloscope. Results Microstructural analyses showed a ceramic- and a polymer-based interpenetrating network. Mean and standard deviation values for the properties evaluated were: KIc = 1.09 ± 0.05 MPa m1/2, ρ = 2.09 ± 0.01 g/cm3, v = 0.23 ± 0.002 and E = 37.95 ± 0.34 GPa. Significance The PICN material showed mechanical properties between porcelains and resin-based composites, reflecting its microstructural components. PMID:24656471

Characterization of a polymer-infiltrated ceramic-network material.

PubMed

Della Bona, Alvaro; Corazza, Pedro H; Zhang, Yu

2014-05-01

To characterize the microstructure and determine some mechanical properties of a polymer-infiltrated ceramic-network (PICN) material (Vita Enamic, Vita Zahnfabrik) available for CAD-CAM systems. Specimens were fabricated to perform quantitative and qualitative analyses of the material's microstructure and to determine the fracture toughness (KIc), density (ρ), Poisson's ratio (ν) and Young's modulus (E). KIc was determined using V-notched specimens and the short beam toughness method, where bar-shaped specimens were notched and 3-point loaded to fracture. ρ was calculated using Archimedes principle, and ν and E were measured using an ultrasonic thickness gauge with a combination of a pulse generator and an oscilloscope. Microstructural analyses showed a ceramic- and a polymer-based interpenetrating network. Mean and standard deviation values for the properties evaluated were: KIc=1.09±0.05MPam(1/2), ρ=2.09±0.01g/cm(3), ν=0.23±0.002 and E=37.95±0.34GPa. The PICN material showed mechanical properties between porcelains and resin-based composites, reflecting its microstructural components. Copyright © 2014 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Formation of Ca/P ceramic coatings by Plasma Electrolytic Oxidation (PEO) on Ti6Al4V ELI alloy

NASA Astrophysics Data System (ADS)

Rodriguez-Jaimes, Y.; Naranjo, D. I.; Blanco, S.; García-Vergara, S. J.

2017-12-01

The formation of PEO ceramic coatings on Ti6Al4V ELI alloy was investigated using a phosphate/calcium containing electrolyte at 300 and 400V at 310K for different times. The Plasma Electrolytic Oxidation (PEO) coated specimens were then heat treated at 873 and 1073K for 2 hours. Scanning electron microscopy, Energy Dispersive X-Ray Spectroscopy (EDS) and X-ray diffraction analysis were used to study the composition and the morphology of the ceramic coatings. The corrosion behaviour of the coatings was studied by Electrochemical Impedance Spectroscopy (EIS) in Simulated Body Fluid (SBF). The PEO-treated specimens primarily revealed a porous structure with thickness between 4 and 12μm, according to the voltage and process time used. The coatings are mainly composed of hydroxyapatite; however, as the voltage and anodizing time increase, the Ca/P ratio decreases. Generally, the corrosion resistance of the alloy was improved by the PEO-treated coatings, although the specimens treated at 1073K showed the presence of cracks that reduced the protective effect of the coatings.

Effect of different surface treatments on adhesion of In-Ceram Zirconia to enamel and dentin substrates.

PubMed

Saker, Samah; Ibrahim, Fatma; Ozcan, Mutlu

2013-08-01

Resin bonding of In-Ceram Zirconia (ICZ) ceramics is still a challenge, especially for minimally invasive applications. This study evaluated the adhesion of ICZ to enamel and dentin after different surface treatments of the ceramic. ICZ ceramic specimens (diameter: 6 mm; thickness: 2 mm) (N = 100) were fabricated following the manufacturer's instructions and randomly assigned to 5 groups (n = 20), according to the surface treatment methods applied. The groups were as follows: group C: no treatment; group SB: sandblasting; group SCS-S: CoJet+silane; group SCS-P: CoJet+Alloy Primer; group GE-S: glaze+ hydrofluoric acid etching (9.6%) for 60 s+silane. Each group was randomly divided into two subgroups to be bonded to either enamel or dentin (n = 10 per group) using MDP-based resin cement (Panavia F2.0). All the specimens were subjected to thermocycling (5000x, 5°C-55°C). The specimens were mounted in a universal testing machine and tensile force was applied to the ceramic/cement interface until failure occurred (1 mm/min). After evaluating all the debonded specimens under SEM, the failure types were defined as either "adhesive" with no cement left on the ceramic surface (score 0) or "mixed" with less than 1/2 of the cement left adhered to the surface with no cohesive failure of the substrate (score 1). The data were statistically evaluated using 2-way ANOVA and Tukey's tests (α = 0.05). The highest tensile bond strength for the enamel surfaces was obtained in group GE-S (18.1 ± 2 MPa) and the lowest in group SB (7.1 ± 1.4 MPa). Regarding dentin, group CSC-P showed the highest (12 ± 1.3 MPa) and SB the lowest tensile bond strength (5.7 ± 0.4 MPa). Groups SB, CSC-S, CSC-P, and GE-S did not show significant differences between the different surface treatments on either enamel or dentin surfaces (p < 0.05, p < 0.001, respectively). Groups CSC-P and GE-S presented similar bond strength for both the enamel and dentin substrates (p < 0.8 and p < 0.9), respectively. While on enamel substrates, exclusively adhesive failures from ICZ (score 0) were found, on dentin exclusively mixed failures were observed (score 1). Adhesion of ICZ to both enamel and dentin can be improved when ceramics are glazed, etched, and silanized, or sandblasted, primed, and cemented with an MDP-based cement.

MICROSTRUCTURAL AND MECHANICAL CHARACTERIZATION OF 2-D AND 3-D SiC/SiNC CERAMIC MATRIX COMPOSITES

DTIC Science & Technology

2018-02-23

48 5.2 Residual Strength of Test Specimens Reaching Run -Out ...........................................48 5.3 Fracture...46 Table 10. Residual Strength Tension Test Results for Creep Rupture Specimens Reaching Run - Out...Residual Strength Tension Test Results for Fatigue Specimens Reaching Run -Out . 49 vii Distribution Statement A. Approved for public release

Evaluation of five CAD/CAM materials by microstructural characterization and mechanical tests: a comparative in vitro study.

PubMed

Sonmez, Nesrin; Gultekin, Pinar; Turp, Volkan; Akgungor, Gokhan; Sen, Deniz; Mijiritsky, Eitan

2018-01-08

Polymer infiltrated ceramics and nano-ceramic resins are the new restorative materials which have been developed in order to enhance the adverse properties of glass-matrix ceramics and resin composites. The aim of the present in vitro study was to evaluate the characteristics of various CAD/CAM materials through mechanical, microstructural, and SEM analysis. Five test groups (n = 22) were formed by using the indicated CAD/CAM blocks: VITA Enamic (VITA Zahnfabrik), Lava Ultimate (3 M ESPE), IPS e.max CAD (Ivoclar Vivadent), IPS Empress CAD (Ivoclar Vivadent), and VITA Mark II (VITA Zahnfabrik). Two specimens from each test group were used for XRD and EDS analysis. Remaining samples were divided into two subgroups (n = 10). One subgroup specimens were thermocycled (5 °C to 55 °C, 30s, 10,000 cycles) whereas the other were not. All of the specimens were evaluated in terms of flexural strength, Vickers hardness, and fracture toughness. Results were statistically analyzed using two-way ANOVA, one-way ANOVA, Tukey's HSD, and Student's t tests (α = .05). Fractured specimens were evaluated using SEM. The highest Vickers microhardness value was found for VITA Mark II (p < .001), however flexural strength and fracture toughness results were lowest conversely (p < .05). IPS e.max CAD was found to have the highest flexural strength (p < .001). Fracture toughness of IPS e.max CAD was also higher than other tested block materials (p < .001). Lava Ultimate and VITA Enamic's mechanical properties were affected negatively from thermocycling (p < .05). Microhardness, flexural strength, and fracture toughness values of Lava Ultimate and VITA Enamic were found to be similar to VITA Mark II and IPS Empress CAD groups. It should be realised that simulated aging process seem to affect ceramic-polymer composite materials more significantly than glass ceramics.

New Coating Technique of Ceramic Implants with Different Glass Solder Matrices for Improved Osseointegration-Mechanical Investigations.

PubMed

Mick, Enrico; Markhoff, Jana; Mitrovic, Aurica; Jonitz, Anika; Bader, Rainer

2013-09-11

Ceramics are a very popular material in dental implant technology due to their tribological properties, their biocompatibility and their esthetic appearance. However, their natural surface structure lacks the ability of proper osseointegration, which constitutes a crucial process for the stability and, thus, the functionality of a bone implant. We investigated the application of a glass solder matrix in three configurations-consisting mainly of SiO₂, Al₂O₃, K₂O and Na₂O to TZP-A ceramic specimens. The corresponding adhesive strength and surface roughness of the coatings on ceramic specimens have been analyzed. Thereby, high adhesive strength (70.3 ± 7.9 MPa) was found for the three different coatings. The obtained roughness (R z ) amounted to 18.24 ± 2.48 µm in average, with significant differences between the glass solder configurations. Furthermore, one configuration was also tested after additional etching which did not lead to significant increase of surface roughness (19.37 ± 1.04 µm) or adhesive strength (57.2 ± 5.8 MPa). In conclusion, coating with glass solder matrix seems to be a promising surface modification technique that may enable direct insertion of ceramic implants in dental and orthopaedic surgery.

Effects of crystal refining on wear behaviors and mechanical properties of lithium disilicate glass-ceramics.

PubMed

Zhang, Zhenzhen; Guo, Jiawen; Sun, Yali; Tian, Beimin; Zheng, Xiaojuan; Zhou, Ming; He, Lin; Zhang, Shaofeng

2018-05-01

The purpose of this study is to improve wear resistance and mechanical properties of lithium disilicate glass-ceramics by refining their crystal sizes. After lithium disilicate glass-ceramics (LD) were melted to form precursory glass blocks, bar (N = 40, n = 10) and plate (N = 32, n = 8) specimens were prepared. According to the differential scanning calorimetry (DSC) of precursory glass, specimens G1-G4 were designed to form lithium disilicate glass-ceramics with different crystal sizes using a two-step thermal treatment. In the meantime, heat-pressed lithium disilicate glass-ceramics (GC-P) and original ingots (GC-O) were used as control groups. Glass-ceramics were characterized using X-ray diffraction (XRD) and were tested using flexural strength test, nanoindentation test and toughness measurements. The plate specimens were dynamically loaded in a chewing simulator with 350 N up to 2.4 × 10 6 loading cycles. The wear analysis of glass-ceramics was performed using a 3D profilometer after every 300,000 wear cycles. Wear morphologies and microstructures were analyzed by scanning electron microscopy (SEM). One-way analysis of variance (ANOVA) was used to analyze the data. Multiple pairwise comparisons of means were performed by Tukey's post-hoc test. Materials with different crystal sizes (p < 0.05) exhibited different properties. Specifically, G3 with medium-sized crystals presented the highest flexural strength, hardness, elastic modulus and fracture toughness. G1 and G2 with small-sized crystals showed lower flexural strength, whereas G4, GC-P, and GC-O with large-sized crystals exhibited lower hardness and elastic modulus. The wear behaviors of all six groups showed running-in wear stage and steady wear stage. G3 showed the best wear resistance while GC-P and GC-O exhibited the highest wear volume loss. After crystal refining, lithium disilicate glass-ceramic with medium-sized crystals showed the highest wear resistance and mechanical properties. Copyright © 2018 Elsevier Ltd. All rights reserved.

In Vitro Comparison of the Bond Strength between Ceramic Repair Systems and Ceramic Materials and Evaluation of the Wettability.

PubMed

Kocaağaoğlu, Hasan; Manav, Taha; Albayrak, Haydar

2017-04-01

When fracture of an all-ceramic restoration occurs, it can be necessary to repair without removing the restoration. Although there are many studies about the repair of metal-ceramic restorations, there are few about all-ceramic restorations. The aim of this study was to evaluate the shear bond strength between ceramic repair systems and esthetic core materials and to evaluate the wettability of all-ceramic core materials. Disk-like specimens (N = 90) made of three dental ceramic infrastructure materials (zirconia ceramic, alumina ceramic, glass ceramic) were polished with silicon carbide paper, prepared for bonding (abrasion with 30 μm diamond rotary cutting instrument). Thirty specimens of each infrastructure were obtained. Each infrastructure group was divided into three subgroups; they were bonded using 3 repair systems: Bisco Intraoral Repair Kit, Cimara & Cimara Zircon Repair System, and Clearfil Repair System. After 1200 thermocycles, shear bond strength was measured in a universal testing machine at a 0.5 mm/min crosshead speed. In addition, the contact angle values of the infrastructures after surface treatments were examined for wettability. Data were analyzed by using ANOVA and Tukey post hoc tests. Although there were no significant differences among the repair systems (p > 0.05) in the glass ceramic and zirconia groups, a significant difference was found among the repair systems in alumina infrastructure (p < 0.001). There were no statistically significant differences among the infrastructures (p > 0.05); however, a statistically significant difference was found among the repair systems (p < 0.05). No difference was found among the infrastructures and repair systems in terms of contact angle values. Cimara & Cimara Zircon Repair System had higher bond strength values than the other repair systems. Although no difference was found among the infrastructures and repair systems, contact wettability angle was decreased by surface treatments compared with polished surfaces. © 2015 by the American College of Prosthodontists.

Strength, fracture toughness and microstructure of a selection of all-ceramic materials. Part I. Pressable and alumina glass-infiltrated ceramics.

PubMed

Guazzato, Massimiliano; Albakry, Mohammad; Ringer, Simon P; Swain, Michael V

2004-06-01

The present study, divided into two parts, aimed to compare the strength, fracture toughness and microstructure of a range of all-ceramic materials. In part I, three hot-pressed glass-ceramics (IPS-Empress, Empress 2 and a new experimental ceramic) and alumina glass-infiltrated ceramics (In-Ceram Alumina), processed by both slip casting and dry pressing, were compared. Tensile strength was appraised on 10 bar-shaped specimens (20 x 4 x 1.2 mm3) for each material with the three-point bending method; the fracture toughness was measured from 20 specimens (20 x 4 x 2 mm3), by using the indentation strength technique. Data were compared with ANOVA and the Sheffé post hoc test (p = 0.05). The volume fraction of each phase, the dimensions and shapes of the grains, porosity and the crack patterns were investigated using SEM. The average and standard deviation in strength (MPa) and fracture toughness (MPa m(1/2)) were: IPS-Empress 106(17)1, 1.2(0.14)1; Empress 2 306(29)2, 2.9(0.51)2, new experimental ceramic 303(49)2, 3.0(0.65)2, In-Ceram Alumina dry-pressed 440(50)2, 3.6(0.26)2, In-Ceram Alumina slip 594(52)3, 4.4(0.48)3. Values with the same superscript number showed no significant statistical difference. Microscopy revealed the relationship between the glass matrix and the crystalline phase and the characteristics of the latter were correlated to the strengthening and toughening mechanisms of these glass-ceramics. The mechanical properties and microstructure of core materials have been advocated as crucial to the clinical long-term performance of all-ceramic dental restorations. This investigation provides the clinician with data regarding strength, fracture toughness and microstructure of a broad range of current materials. Copyright 2003 Academy of Dental Materials

Effect of sandblasting, silica coating, and laser treatment on the microtensile bond strength of a dental zirconia ceramic to resin cements.

PubMed

Mahmoodi, Nasrin; Hooshmand, Tabassom; Heidari, Solmaz; Khoshro, Kimia

2016-02-01

The purpose of this in vitro study was to evaluate the effect of laser irradiation as well as other surface treatment methods on the microtensile bond strength of a dental zirconia ceramic to the two types of resin cements. Zirconia ceramic blocks (ICE Zirkon) were sintered according to the manufacturer's instructions and duplicated in resin composites. The ceramic specimens were divided into four groups according to the following surface treatments: no surface treatment (control), sandblasting with alumina, silica coating plus silanization, and Nd:YAG laser irradiation. The specimens were divided equally and then bonded with Panavia F2.0 (self-etching resin cement) and Clearfil SA Luting (self-adhesive resin cement) to the composite blocks. The bonded ceramic-composite blocks were stored in distilled water at 37 °C for 72 h, cut to prepare bar-shaped specimens with a bonding area of approximately 1 mm(2), and thermocycled for 3000 cycles between 5 and 55 °C, and the microtensile bond strengths were measured using a universal testing machine. The data were analyzed by ANOVA and Tukey post hoc test. The results showed that the self-adhesive resin cement used in this study did not improve the microtensile bond strength when the zirconia surface was sandblasted by alumina. The use of the Nd:YAG laser did not enhance the bond strength between the zirconia and both types of resin cements. In addition, silica coating of the zirconia surfaces plus silane application significantly improved the bond strength regardless of the type of resin cement utilized.

Effect of bending on the room-temperature tensile strengths of structural ceramics

DOE Office of Scientific and Technical Information (OSTI.GOV)

Jenkins, M.G.

1992-01-01

Results for nearly fifty, room-temperature tensile tests conducted on two advanced, monolithic silicon nitride ceramics are evaluated for the effects of bending and application of various Weibull statistical analyses. Two specimen gripping systems (straight collet and tapered collet) were evaluated for both success in producing gage section failures and tendency to minimize bending at failure. Specimen fabrication and grinding technique consderations are briefly reviewed and related to their effects on successful tensile tests. Ultimate tensile strengths are related to the bending measured at specimen failure and the effects of the gripping system on bending are discussed. Finally, comparisons are mademore » between the use of censored and uncensored data sample sets for determining the maximum likelihood estimates of the Weibull parameters from the tensile strength distributions.« less

Effect of bending on the room-temperature tensile strengths of structural ceramics

DOE Office of Scientific and Technical Information (OSTI.GOV)

Jenkins, M.G.

1992-07-01

Results for nearly fifty, room-temperature tensile tests conducted on two advanced, monolithic silicon nitride ceramics are evaluated for the effects of bending and application of various Weibull statistical analyses. Two specimen gripping systems (straight collet and tapered collet) were evaluated for both success in producing gage section failures and tendency to minimize bending at failure. Specimen fabrication and grinding technique consderations are briefly reviewed and related to their effects on successful tensile tests. Ultimate tensile strengths are related to the bending measured at specimen failure and the effects of the gripping system on bending are discussed. Finally, comparisons are mademore » between the use of censored and uncensored data sample sets for determining the maximum likelihood estimates of the Weibull parameters from the tensile strength distributions.« less

An evaluation of strain measuring devices for ceramic composites

NASA Technical Reports Server (NTRS)

Gyekenyesi, John Z.; Bartolotta, Paul A.

1991-01-01

A series of tensile tests was conducted on SiC/reaction bonded silicon nitrides (RBSN) composites using different methods of strain measurement. The tests were used to find the optimum strain sensing device for use with continuous fiber reinforced ceramic matrix composites in ambient and high temperature environments. Bonded resistance gages were found to offer excellent performance for room temperature tests. The clip-on gage offers the same performance, but less time is required for mounting it to the specimen. Low contact force extensometers track the strain with acceptable results at high specimen temperatures. Silicon carbide rods with knife edges are preferred. The edges must be kept sharp. The strain measuring devices should be mounted on the flat side of the specimen. This is in contrast to mounting on the rough thickness side.

An evaluation of strain measuring devices for ceramic composites

NASA Technical Reports Server (NTRS)

Gyekenyesi, John Z.; Bartolotta, Paul A.

1992-01-01

A series of tensile tests were conducted on SiC/RBSN composites using different methods of strain measurement. The tests were used to find the optimum strain sensing device for use with continuous fiber reinforced ceramic matrix composites in ambient and high temperature environments. Bonded resistance strain gages were found to offer excellent performance for room temperature tests. The clip-on gage offers the same performance but significantly less time is required for mounting it to the specimen. Low contact force extensometers track the strain with acceptable results at high specimen temperatures. Silicon carbide rods with knife edges are preferred. The edges must be kept sharp. The strain measuring devices should be mounted on the flat side of the specimen. This is in contrast to mounting on the rough thickness side.

Effect of surface condition of dental zirconia ceramic (Denzir) on bonding.

PubMed

Uo, Motohiro; Sjögren, Göran; Sundh, Anders; Goto, Mitsunari; Watari, Fumio; Bergman, Maud

2006-09-01

Yttria partially stabilized zirconia (YPSZ) ceramics are suitable for dental and medical use because of their high fracture toughness and chemical durability. The purpose of this study was to examine the bonding behavior of a dental YPSZ ceramic, Denzir. After being subjected to various surface treatments, Denzir specimens were bonded to each other using an adhesive resin composite, glass ionomer, or zinc phosphate cement. Bonding strength was then determined by the shearing test. No significant differences (p>0.05) were observed between SiC- and Al2O3-blasted specimens. In all surface treatments, the shear bond strength significantly (p<0.05) increased in the order of adhesive resin composite cement > glass ionomer cement > zinc phosphate cement. Moreover, silanization with methacryloxy propyl trimethoxysilane slightly increased the bonding strength of the adhesive resin composite cement.

The effect of core material, veneering porcelain, and fabrication technique on the biaxial flexural strength and weibull analysis of selected dental ceramics.

PubMed

Lin, Wei-Shao; Ercoli, Carlo; Feng, Changyong; Morton, Dean

2012-07-01

The objective of this study was to compare the effect of veneering porcelain (monolithic or bilayer specimens) and core fabrication technique (heat-pressed or CAD/CAM) on the biaxial flexural strength and Weibull modulus of leucite-reinforced and lithium-disilicate glass ceramics. In addition, the effect of veneering technique (heat-pressed or powder/liquid layering) for zirconia ceramics on the biaxial flexural strength and Weibull modulus was studied. Five ceramic core materials (IPS Empress Esthetic, IPS Empress CAD, IPS e.max Press, IPS e.max CAD, IPS e.max ZirCAD) and three corresponding veneering porcelains (IPS Empress Esthetic Veneer, IPS e.max Ceram, IPS e.max ZirPress) were selected for this study. Each core material group contained three subgroups based on the core material thickness and the presence of corresponding veneering porcelain as follows: 1.5 mm core material only (subgroup 1.5C), 0.8 mm core material only (subgroup 0.8C), and 1.5 mm core/veneer group: 0.8 mm core with 0.7 mm corresponding veneering porcelain with a powder/liquid layering technique (subgroup 0.8C-0.7VL). The ZirCAD group had one additional 1.5 mm core/veneer subgroup with 0.7 mm heat-pressed veneering porcelain (subgroup 0.8C-0.7VP). The biaxial flexural strengths were compared for each subgroup (n = 10) according to ISO standard 6872:2008 with ANOVA and Tukey's post hoc multiple comparison test (p≤ 0.05). The reliability of strength was analyzed with the Weibull distribution. For all core materials, the 1.5 mm core/veneer subgroups (0.8C-0.7VL, 0.8C-0.7VP) had significantly lower mean biaxial flexural strengths (p < 0.0001) than the other two subgroups (subgroups 1.5C and 0.8C). For the ZirCAD group, the 0.8C-0.7VL subgroup had significantly lower flexural strength (p= 0.004) than subgroup 0.8C-0.7VP. Nonetheless, both veneered ZirCAD groups showed greater flexural strength than the monolithic Empress and e.max groups, regardless of core thickness and fabrication techniques. Comparing fabrication techniques, Empress Esthetic/CAD, e.max Press/CAD had similar biaxial flexural strength (p= 0.28 for Empress pair; p= 0.87 for e.max pair); however, e.max CAD/Press groups had significantly higher flexural strength (p < 0.0001) than Empress Esthetic/CAD groups. Monolithic core specimens presented with higher Weibull modulus with all selected core materials. For the ZirCAD group, although the bilayer 0.8C-0.7VL subgroup exhibited significantly lower flexural strength, it had highest Weibull modulus than the 0.8C-0.7VP subgroup. The present study suggests that veneering porcelain onto a ceramic core material diminishes the flexural strength and the reliability of the bilayer specimens. Leucite-reinforced glass-ceramic cores have lower flexural strength than lithium-disilicate ones, while fabrication techniques (heat-pressed or CAD/CAM) and specimen thicknesses do not affect the flexural strength of all glass ceramics. Compared with the heat-pressed veneering technique, the powder/liquid veneering technique exhibited lower flexural strength but increased reliability with a higher Weibull modulus for zirconia bilayer specimens. Zirconia-veneered ceramics exhibited greater flexural strength than monolithic leucite-reinforced and lithium-disilicate ceramics regardless of zirconia veneering techniques (heat-pressed or powder/liquid technique). © 2012 by the American College of Prosthodontists.

Size determination of Acipenser ruthenus spermatozoa in different types of electron microscopy.

PubMed

Psenicka, Martin; Tesarová, Martina; Tesitel, Jakub; Nebesárová, Jana

2010-07-01

In this study three types of scanning electron microscopes were used for the size determination of spermatozoa of sterlet Acipenser ruthenus - high vacuum scanning electron microscope (SEM, JEOL 6300), environmental scanning electron microscope (ESEM, Quanta 200 FEG), field emission scanning electron microscope (FESEM, JEOL 7401F) with cryoattachment Alto 2500 (Gatan) and transmission electron microscope (TEM, JEOL 1010). The use of particular microscopes was tied with different specimen preparation techniques. The aim of this study was to evaluate to what degree the type of used electron microscope can influence the size of different parts of spermatozoa. For high vacuum SEM the specimen was prepared using two slightly different procedures. After chemical fixation with 2.5% glutaraldehyde in 0.1M phosphate buffer and post-fixation by 1% osmium tetroxide, the specimen was dehydrated by acetone series and dried either by critical point method or by means of t-butylalcohol. For ESEM fresh, unfixed material was used, which was dropped on microscopic copper grids. In FESEM working in cryo-mode the specimen was observed in a frozen state. Ultrathin sections from chemically fixed and Epon embedded specimens were prepared for TEM observation. Distinct parts of sterlet spermatozoa were measured in each microscope and the data obtained was statistically processed. Results confirmed that the classical chemical procedure of specimen preparation for SEM including critical point drying method led to a significant contraction of all measured values, which could deviate up to 30% in comparison with values measured on the fresh chemically untreated specimen in ESEM. Surprisingly sperm dimensions determinated on ultrathin sections by TEM are comparable with values obtained in ESEM or FESEM. Copyright 2010 Elsevier Ltd. All rights reserved.

Functionalization of Ceramic Metal Oxide Powders and Ceramic Membranes by Perfluoroalkylsilanes and Alkylsilanes Possessing Different Reactive Groups: Physicochemical and Tribological Properties.

PubMed

Kujawa, Joanna; Kujawski, Wojciech

2016-03-23

The functionalization of ceramic materials, metal oxide powders (TiO2 and ZrO2), and ceramic membranes (5 kD TiO2 and 300 kD TiO2) was performed and thoroughly discussed. The objective of the functionalization was to change the natively hydrophilic character to the hydrophobic. The hydrophilic character of the ceramics generates limitations in wider application of such materials. Material functionalization was performed using perfluoroalkylsilanes and trifunctional(octyl)silanes possessing three different reactive functional groups: -Cl, -OMe, and -OEt. The characterization of functionalized metal oxide powders and ceramic membranes was assessed by a combination of various analytical methods and techniques: NMR, TGA, HR-TEM, FT-IR, SEM-EDX, AFM, and contact goniometry. The impact of molecular structure of grafting agents (type of reactive group), time of functionalization process (5-15 min), and type of membrane morphology on the material, physicochemical, and tribological properties was studied. Effectiveness of hydrophobization was confirmed by HR-TEM technique. The thickness of the attached hydrophobic nanolayer on the surface of ceramics was around 2.2 nm. It was found that the stable hydrophobic surfaces were obtained by functionalization with both fluorinated and nonfluorinated modifiers. The materials modified with perfluoroalkylsilanes (FC6OEt3) and trichloro(octyl)silanes (C6Cl3) during 15 min hydrophobization possess comparable properties: contact angle (CA) equal to 130° and 133°; roughness RMS of 10.2 and 12 nm; adhesive force of 4.1 and 5.7 nN; and Young modulus of 135 and 130 GPa, respectively. The relation between hydrophobicity level and ceramic membrane roughness was discussed applying the Kao diagram concept. (29)Si NMR results show that type of modifier has an important influence on grafting efficiency and on the mode of the grafting molecules attachment. In case of grafting with n-octyltrichlorosilane (C6OCl3) and n-octyltrimethoxysilane (C6OMe3), an increase of lateral polymerization across the octylsilane layer was observed.

Surface degradation of glass ceramics after exposure to acidulated phosphate fluoride

PubMed Central

CCAHUANA, Vanessa Zulema S.; ÖZCAN, Mutlu; MESQUITA, Alfredo Mikail Melo; NISHIOKA, Renato Sussumo; KIMPARA, Estevão Tomomitsu; BOTTINO, Marco Antonio

2010-01-01

Objective This study evaluated the surface degradation effect of acidulated phosphate fluoride (APF) gel exposure on the glassy matrix ceramics as a function of time. Material and methods Disc-shaped ceramic specimens (N = 120, 10/per ceramic material) were prepared in stainless steel molds (inner diameter: 5 mm, height: 2 mm) using 6 dental ceramics: 3 indicated for ceramic-fused-to-metal (Vita Omega 900, Carmen and Vita Titankeramik), 2 for all-ceramic (Vitadur Alpha and Finesse® Low Fusing) and 1 for both types of restorations (IPS d.SIGN). The specimens were wet ground finished, ultrasonically cleaned and auto-glazed. All specimens were subjected to calculation of percentage of mass loss, surface roughness analysis and topographical description by scanning electron microscopy (SEM) before (0 min) and after exposure to 1.23 % APF gel for 4 min and 60 min representing short- and long-term etching effect, respectively. The data were analyzed using two-way ANOVA with repeated measures and Tukey`s test (α=0.05). Results Significant effect of the type of the ceramics (p=0.0000, p=0.0031) and exposure time (p=0.0000) was observed in both surface roughness and percentage of mass loss values, respectively. The interaction factor between both parameters was also significant for both parameters (p=0.0904, p=0.0258). Both 4 min (0.44±0.1 - 0.81±0.2 µm) and 60 min (0.66±0.1 - 1.04±0.3 µm) APF gel exposure created significantly more surface roughness for all groups when compared to the control groups (0.33±0.2 - 0.68±0.2 µm) (p<0.05). There were no significant differences in percentage of mass loss between the ceramics at 4 min (p>0.05) but at 60 min exposure, IPS d.SIGN showed the highest percentage of mass loss (0.1151±0.11). The mean surface roughness for Vita Titankeramik (0.84±0.2 µm) and Finesse® Low Fusing (0.74.±0.2 µm) was significantly higher than those of the other ceramics (0.59±0.1 µm - 0.49±0.1 µm) and Vita Titankeramik (p<0.05) regardless of the exposure time. A positive correlation was found between surface roughness and percentage of mass loss for all ceramic materials [(r=0.518 (Vitadur Alpha), r=0.405 (Vita Omega 900), r=0.580 (Carmen), r=0.687 (IPS d.SIGN), r=0.442 (Finesse® Low Fusing), r=0.572 (Vita Titankeramik), Pearson`s correlation coefficient)]. The qualitative SEM analysis showed evidence of corrosive attack on all of ceramics at varying degrees. Conclusions The ceramics indicated for either metal-ceramic or all-ceramic restorations were all vulnerable to surface texture changes and mass loss after short-term and long-term APF gel exposure. PMID:20485927

Recycling of residual IGCC slags and their benefits as degreasers in ceramics.

PubMed

Iglesias Martín, I; Acosta Echeverría, A; García-Romero, E

2013-11-15

This work studies the evolution of IGCC slag grains within a ceramic matrix fired at different temperatures to investigate the effect of using IGCC slag as a degreaser. Pressed ceramic specimens from two clay mixtures are used in this study. The M1 mixture is composed of standard clays, whereas the M2 mixture is composed of the same clay mixture as M1 mixture but contains 15% by weight IGCC slag. The amount of IGCC slag added coincides with the amount of slag typically used as a degreaser in the ceramic industry. Specimens are fired at 950 °C, 1000 °C, 1050 °C, 1100 °C and 1150 °C. The mineralogical composition and the IGCC slag grain shape within the ceramic matrix are determined by X-ray diffraction, polarized light microscopy and scanning electron microscopy. The results reveal that the surface of the slag grains is welded to the ceramic matrix while the quartz grains are separated, which causes increased water absorption and reduces the mechanical strength. IGCC slag, however, reduces water absorption. This behaviour is due to the softening temperature of the slag. This property is quite important from an industrial viewpoint because IGCC slag can serve as an alternative to traditional degreasing agents in the ceramic building industry. Additionally, using IGCC slag allows for the transformation of waste into a secondary raw material, thereby avoiding disposal at landfills; moreover, these industrial wastes are made inert and improve the properties of ceramics. Copyright © 2013 Elsevier Ltd. All rights reserved.

Effect of silica coating on fracture strength of glass-infiltrated alumina ceramic cemented to dentin.

PubMed

Xie, Haifeng; Zhu, Ye; Chen, Chen; Gu, Ning; Zhang, Feimin

2011-10-01

To examine the availability of sol-gel processed silica coating for alumina-based ceramic bonding, and determine which silica sol concentration was appropriate for silica coating. Sixty disks of In-Ceram alumina ceramic were fabricated and randomly divided into 5 main groups. The disks received 5 different surface conditioning treatments: Group Al, sandblasted; Group AlC, sandblasted + silane coupling agent applied; Groups Al20C, Al30C, and Al40C, sandblasted, silica coating via sol-gel process prepared using 20 wt%, 30 wt%, and 40 wt% silica sols, and then silane coupling agent applied. Before bonding, one-step adhesives were applied on pre-prepared ceramic surfaces of all groups. Then, 60 dentin specimens were prepared and conditioned with phosphoric acid and one-step adhesive. Ceramic disks of all groups were cemented to dentin specimens with dual-curing resin cements. Fracture strength was determined at 24 h and after 20 days of storage in water. Groups Al20C, Al30C, and Al40C revealed significantly higher fracture strength than groups Al and AlC. No statistically significant difference in fracture strength was found between groups Al and AlC, or among groups Al20C, Al30C, and Al40C. Fracture strength values of all the groups did not change after 20 days of water storage. Sol-gel processed silica coating can enhance fracture strength of In-Ceram alumina ceramic after bonding to dentin, and different silica sol concentrations produced the same effects. Twenty days of water storage did not decrease the fracture strength.

Influence of curing protocol and ceramic composition on the degree of conversion of resin cement

PubMed Central

Lanza, Marcos Daniel Septimio; Andreeta, Marcello Rubens Barsi; Pegoraro, Thiago Amadei; Pegoraro, Luiz Fernando; Carvalho, Ricardo Marins De

2017-01-01

Abstract Due to increasing of aesthetic demand, ceramic crowns are widely used in different situations. However, to obtain long-term prognosis of restorations, a good conversion of resin cement is necessary. Objective: To evaluate the degree of conversion (DC) of one light-cure and two dual-cure resin cements under a simulated clinical cementation of ceramic crowns. Material and Methods: Prepared teeth were randomly split according to the ceramic's material, resin cement and curing protocol. The crowns were cemented as per manufacturer's directions and photoactivated either from occlusal suface only for 60 s; or from the buccal, occlusal and lingual surfaces, with an exposure time of 20 s on each aspect. After cementation, the specimens were stored in deionized water at 37°C for 7 days. Specimens were transversally sectioned from occlusal to cervical surfaces and the DC was determined along the cement line with three measurements taken and averaged from the buccal, lingual and approximal aspects using micro-Raman spectroscopy (Alpha 300R/WITec®). Data were analyzed by 3-way ANOVA and Tukey test at =5%. Results: Statistical analysis showed significant differences among cements, curing protocols and ceramic type (p<0.001). The curing protocol 3x20 resulted in higher DC for all tested conditions; lower DC was observed for Zr ceramic crowns; Duolink resin cement culminated in higher DC regardless ceramic composition and curing protocol. Conclusion: The DC of resin cement layers was dependent on the curing protocol and type of ceramic. PMID:29211292

Effect of in vitro aging on the flexural strength and probability to fracture of Y-TZP zirconia ceramics for all-ceramic restorations.

PubMed

Siarampi, Eleni; Kontonasaki, Eleana; Andrikopoulos, Konstantinos S; Kantiranis, Nikolaos; Voyiatzis, George A; Zorba, Triantafillia; Paraskevopoulos, Konstantinos M; Koidis, Petros

2014-12-01

Dental zirconia restorations should present long-term clinical survival and be in service within the oral environment for many years. However, low temperature degradation could affect their mechanical properties and survival. The aim of this study was to investigate the effect of in vitro aging on the flexural strength of yttrium-stabilized (Y-TZP) zirconia ceramics for ceramic restorations. One hundred twenty bar-shaped specimens were prepared from two ceramics (ZENO Zr (WI) and IPS e.max(®) ZirCAD (IV)), and loaded until fracture according to ISO 6872. The specimens from each ceramic (nx=60) were divided in three groups (control, aged for 5h, aged for 10h). One-way ANOVA was used to assess statistically significant differences among flexural strength values (P<0.05). The variability of the flexural strength values was analyzed using the two-parameter Weibull distribution function, which was applied for the estimation of Weibull modulus (m) and characteristic strength (σ0). The crystalline phase polymorphs of the materials (tetragonal, t, and monoclinic, m, zirconia) were investigated by X-ray diffraction (XRD) analysis, Raman spectroscopy and Fourier transform infrared (FTIR) spectroscopy. A slight increase of the flexural strength after 5h, and a decrease after 10h of aging, was recorded for both ceramics, however statistically significant was for the WI group (P<0.05). Both ceramics presented a t→m phase transformation, with the m-phase increasing from 4 to 5% at 5h to around 15% after 10h. The significant reduction of the flexural strength after 10h of in vitro aging, suggests high fracture probability for one of the zirconia ceramics tested. Copyright © 2014 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

CORRELATION BETWEEN METAL-CERAMIC BOND STRENGTH AND COEFFICIENT OF LINEAR THERMAL EXPANSION DIFFERENCE

PubMed Central

Lopes, Stella Crosara; Pagnano, Valéria Oliveira; Rollo, João Manuel Domingos de Almeida; Leal, Mônica Barbosa; Bezzon, Osvaldo Luiz

2009-01-01

The purpose of this study was to evaluate the metal-ceramic bond strength (MCBS) of 6 metal-ceramic pairs (2 Ni-Cr alloys and 1 Pd-Ag alloy with 2 dental ceramics) and correlate the MCBS values with the differences between the coefficients of linear thermal expansion (CTEs) of the metals and ceramics. Verabond (VB) Ni-Cr-Be alloy, Verabond II (VB2), Ni-Cr alloy, Pors-on 4 (P), Pd-Ag alloy, and IPS (I) and Duceram (D) ceramics were used for the MCBS test and dilatometric test. Forty-eight ceramic rings were built around metallic rods (3.0 mm in diameter and 70.0 mm in length) made from the evaluated alloys. The rods were subsequently embedded in gypsum cast in order to perform a tensile load test, which enabled calculating the CMBS. Five specimens (2.0 mm in diameter and 12.0 mm in length) of each material were made for the dilatometric test. The chromel-alumel thermocouple required for the test was welded into the metal test specimens and inserted into the ceramics. ANOVA and Tukey's test revealed significant differences (p=0.01) for the MCBS test results (MPa), with PI showing higher MCBS (67.72) than the other pairs, which did not present any significant differences. The CTE (10-6 °C-1) differences were: VBI (0.54), VBD (1.33), VB2I (-0.14), VB2D (0.63), PI (1.84) and PD (2.62). Pearson's correlation test (r=0.17) was performed to evaluate of correlation between MCBS and CTE differences. Within the limitations of this study and based on the obtained results, there was no correlation between MCBS and CTE differences for the evaluated metal-ceramic pairs. PMID:19274398

Evaluation of surface roughness and polishing techniques for new ceramic materials.

PubMed

Campbell, S D

1989-05-01

The surface roughness of crown and bridge materials should be minimized to obtain optimal biocompatability. This study used scanning electron microscopy to evaluate the effect of polishing procedures on two all-ceramic crown materials (Dicor and Cerestore). The "as formed," unpolished specimens of both Dicor and Cerestore materials presented a rough surface. It was found that any attempt to polish the Cerestore coping material resulted in an extremely rough surface. Finishing of the Dicor ceramic resulted in a smoother but pitted surface. Polishing of both ceramic materials resulted in a surface that was rougher than the glazed metal ceramic controls. The smoothest finish was obtained when the glazed veneer (Cerestore) and shading porcelain (Dicor) were applied to the all-ceramic materials.

Effect of different dental ceramic systems on the wear of human enamel: An in vitro study.

PubMed

Zandparsa, Roya; El Huni, Rabie M; Hirayama, Hiroshi; Johnson, Marc I

2016-02-01

The wear of tooth structure opposing different advanced dental ceramic systems requires investigation. The purpose of this in vitro study was to compare the wear of advanced ceramic systems against human enamel antagonists. Four ceramic systems (IPS e.max Press, IPS e.max CAD, Noritake Super Porcelain EX-3, and LAVA Plus Zirconia) and 1 control group containing human enamel specimens were used in this study (n = 12). All specimens were fabricated as disks 11 mm in diameter and 3 mm thick. The mesiopalatal cusps of the maxillary third molars were prepared to serve as the enamel styluses. All specimens were embedded individually in 25 mm(3) autopolymerizing acrylic resin blocks. Wear was measured with a cyclic loading machine and a newly designed wear simulator. All enamel styluses (cusps) were scanned using the Activity 880 digital scanner (SmartOptics). Data from the base line and follow-up scans were collected and compared with Qualify 2012 3-dimensional (3D) and 2D digital inspection software (Geomagic), which aligned the models and detected the geometric changes and the wear caused by the antagonist specimen. One-way ANOVA was used to analyze the collected data. After 125,000 bidirectional loading cycles, the mean loss of opposing enamel volume for the enamel disks in the control group was 37.08 μm(3), the lowest mean value for IPS e.max Press system was 39.75 μm(3); 40.58 μm(3) for IPS e.max CAD; 45.08 μm(3) for Noritake Super Porcelain EX-3 system; and 48.66 μm(3) for the Lava Plus Zirconia system. No statically significant differences were found among the groups in opposing enamel volume loss (P=.225) or opposing enamel height loss (P=.149). In terms of opposing enamel height loss, Lava Plus Zirconia system showed the lowest mean value of 27.5 μm. The mean value for the IPS e.max CAD system was 27.91 μm; 29.08 μm for the control enamel; 33.25 μm for the IPS e.max Press system; and 34.75 μm for the Noritake Super Porcelain EX-3 system. Within the limitations of this in vitro study, no differences were found in the linear and volumetric reduction of enamel cusps abraded against enamel disks and all other ceramic specimens. All ceramic systems exhibited high durability and were wear-friendly to opposing enamel. Copyright © 2016 Editorial Council for the Journal of Prosthetic Dentistry. Published by Elsevier Inc. All rights reserved.

Effect of metal chloride solutions on coloration and biaxial flexural strength of yttria-stabilized zirconia

NASA Astrophysics Data System (ADS)

Oh, Gye-Jeong; Lee, Kwangmin; Lee, Doh-Jae; Lim, Hyun-Pil; Yun, Kwi-Dug; Ban, Jae-Sam; Lee, Kyung-Ku; Fisher, John G.; Park, Sang-Won

2012-10-01

The effect of three kinds of transition metal dopants on the color and biaxial flexural strength of zirconia ceramics for dental applications was evaluated. Presintered zirconia discs were colored through immersion in aqueous chromium, molybdenum and vanadium chloride solutions and then sintered at 1450 °C. The color of the doped specimens was measured using a digital spectrophotometer. For biaxial flexural strength measurements, specimens infiltrated with 0.3 wt% of each aqueous chloride solution were used. Uncolored discs were used as a control. Zirconia specimens infiltrated with chromium, molybdenum and vanadium chloride solutions were dark brown, light yellow and dark yellow, respectively. CIE L*, a*, and b* values of all the chromium-doped specimens and the specimens infiltrated with 0.1 wt% molybdenum chloride solution were in the range of values for natural teeth. The biaxial flexural strengths of the three kinds of metal chloride groups were similar to the uncolored group. These results suggest that chromium and molybdenum dopants can be used as colorants to fabricate tooth colored zirconia ceramic restorations.

Processing, Microstructure, and Properties of Engineered Diboride Structures

NASA Astrophysics Data System (ADS)

Wittmaier, Connor Charles

The mechanical properties and processing parameters of boride ceramics in foam and laminate architectures were evaluated. The ceramic reticulated foam was produced through a polymer substrate replication technique and the hardness and compressive strength were tested. The laminate structure was tested to evaluate the flexure strength and work of fracture as a function of temperature. The foam architecture was produced using a TiB2 slurry coating on a polyurethane reticulated foam preform. Foams sintered to 2150°C displayed an average grain size of 8.9 +/- 7.3 microm, and a hardness of 17.3 +/- 2.4 GPa. Crush testing foams were sintered at 1975°C, and displayed a specific strength of 208 +/- 63 kPa with an overall porosity of 97%. For these specimens, it is likely that microcracking lowered the hardness, but the overall strength was controlled by the bulk density. The laminate structures were fabricated using alternating layers of ZrB 2 and C-10 vol% ZrB2. The structures were fabricated through the shaping of ceramic loaded thermoplastic polymers that underwent burnout and hot pressing cycles. These specimens had strong phase ZrB2 layers that were about 150 mum thick alternating with weak phase layers that were about 20 mum thick. Specimens exhibited a maximum flexure strength of 311 +/- 10 MPa at 1600°C, and an increased work of fracture compared to conventional ZrB2 ceramics. The maximum fraction of inelastic work of fracture occurred at room temperature, and decreased as temperature increased. This was reflected in the length of the crack path through the specimen. Deflected cracks travelled through the center of the C-ZrB2 layers in the material in Mode II fracture.

Wear characteristics of current aesthetic dental restorative CAD/CAM materials: two-body wear, gloss retention, roughness and Martens hardness.

PubMed

Mörmann, Werner H; Stawarczyk, Bogna; Ender, Andreas; Sener, Beatrice; Attin, Thomas; Mehl, Albert

2013-04-01

This study determined the two-body wear and toothbrushing wear parameters, including gloss and roughness measurements and additionally Martens hardness, of nine aesthetic CAD/CAM materials, one direct resin-based nanocomposite plus that of human enamel as a control group. Two-body wear was investigated in a computer-controlled chewing simulator (1.2 million loadings, 49N at 1.7Hz; 3000 thermocycles 5/50°C). Each of the 11 groups consisted of 12 specimens and 12 enamel antagonists. Quantitative analysis of wear was carried out with a 3D-surface analyser. Gloss and roughness measurements were evaluated using a glossmeter and an inductive surface profilometer before and after abrasive toothbrushing of machine-polished specimens. Additionally Martens hardness was measured. Statistically significant differences were calculated with one-way ANOVA (analysis of variance). Statistically significant differences were found for two-body wear, gloss, surface roughness and hardness. Zirconium dioxide ceramics showed no material wear and low wear of the enamel antagonist. Two-body wear of CAD/CAM-silicate and -lithium disilicate ceramics, -hybrid ceramics and -nanocomposite as well as direct nanocomposite did not differ significantly from that of human enamel. Temporary polymers showed significantly higher material wear than permanent materials. Abrasive toothbrushing significantly reduced gloss and increased roughness of all materials except zirconium dioxide ceramics. Gloss retention was highest with zirconium dioxide ceramics, silicate ceramics, hybrid ceramics and nanocomposites. Temporary polymers showed least gloss retention. Martens hardness differed significantly among ceramics, between ceramics and composites, and between resin composites and acrylic block materials as well. All permanent aesthetic CAD/CAM block materials tested behave similarly or better with respect to two-body wear and toothbrushing wear than human enamel, which is not true for temporary polymer CAD/CAM block materials. Ceramics show the best gloss retention compared to hybrid ceramics, composites and acrylic polymers. Copyright © 2013 Elsevier Ltd. All rights reserved.

Reliability and mode of failure of bonded monolithic and multilayer ceramics.

PubMed

Alessandretti, Rodrigo; Borba, Marcia; Benetti, Paula; Corazza, Pedro Henrique; Ribeiro, Raissa; Della Bona, Alvaro

2017-02-01

To evaluate the reliability of monolithic and multilayer ceramic structures used in the CAD-on technique (Ivoclar), and the mode of failure produced in ceramic structures bonded to a dentin analog material (NEMA-G10). Ceramic specimens were fabricated as follows (n=30): CAD-on- trilayer structure (IPS e.max ZirCAD/IPS e.max Crystall./Connect/IPS e.max CAD); YLD- bilayer structure (IPS e.max ZirCAD/IPS e.max Ceram); LDC- monolithic structure (IPS e.max CAD); and YZW- monolithic structure (Zenostar Zr Translucent). All ceramic specimens were bonded to G10 and subjected to compressive load in 37°C distilled water until the sound of the first crack, monitored acoustically. Failure load (L f ) values were recorded (N) and statistically analyzed using Weibull distribution, Kruskal-Wallis test, and Student-Newman-Keuls test (α=0.05). L f values of CAD-on and YZW structures were statistically similar (p=0.917), but higher than YLD and LDC (p<0.01). Weibull modulus (m) values were statistically similar for all experimental groups. Monolithic structures (LDC and YZW) failed from radial cracks. Failures in the CAD-on and YLD groups showed, predominantly, both radial and cone cracks. Monolithic zirconia (YZW) and CAD-on structures showed similar failure resistance and reliability, but a different fracture behavior. Copyright © 2016 The Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Effect of high-power-laser with and without graphite coating on bonding of resin cement to lithium disilicate ceramic.

PubMed

Feitosa, Fernanda A; de Araújo, Rodrigo M; Tay, Franklin R; Niu, Lina; Pucci, César R

2017-12-12

The present study evaluated the effect of different high-power-laser surface treatments on the bond strength between resin cement and disilicate ceramic. Lithium disilicate ceramic specimens with truncated cones shape were prepared and divided into 5 groups: HF (hydrofluoric acid-etching), Er:YAG laser + HF, Graphite + Er:YAG laser + HF, Nd:YAG laser + HF, and Graphite + Nd:YAG laser + HF. The treated ceramic surfaces were characterized with scanning electron microscopy and surface roughness measurement. Hourglasses-shaped ceramic- resin bond specimens were prepared, thermomechanically cycled and stressed to failure under tension. The results showed that for both the factors "laser" and "graphite", statistically significant differences were observed (p < 0.05). Multiple-comparison tests performed on the "laser" factor were in the order: Er:YAG > Nd:YAG (p < 0.05), and on the "graphite" factor were in the order: graphite coating < without coating (p < 0.05). The Dunnett test showed that Er:YAG + HF had significantly higher tensile strength (p = 0.00). Higher surface roughness was achieved after Er:YAG laser treatment. Thus Er:YAG laser treatment produces higher bond strength to resin cement than other surface treatment protocols. Surface-coating with graphite does not improve bonding of the laser-treated lithium disilicate ceramic to resin cement.

Simple technique for observing subsurface damage in machining of ceramics

DOE Office of Scientific and Technical Information (OSTI.GOV)

Xu, H.H.K.; Jahanmir, S.

1994-05-01

A simple technique is proposed for directly observing subsurface damage in the machining of ceramics. The technique requires two polished specimens and an optical microscope with Nomarski illumination for examination. The subsurface damage created by the grinding of an alumina ceramic is investigated using this technique. The mode of damage is identified as intragrain twinning/slip, and intergranular and transgranular cracking. Chipping along the twinned planes and along the transgranular crack planes, and dislodgement of the intergranularly debonded grains are suggested to be the mechanisms of material removal in the machining of this alumina ceramic.

Processing, structure, and characterizaton of nickel-alumina composites obtained by the partial reduction of zirconia-doped nickel-aluminum oxide and application to the tempering of ceramics

NASA Astrophysics Data System (ADS)

Barbieri, Thomas John

1999-11-01

Partial reduction of the spinel compound NiAl2O4 results in a two phase composite mixture of Ni + Al2O3. The reduction reaction has a volume decrease associated with it, which theoretically could generate large residual stresses, which have the potential to "temper" a ceramic, i.e. to place the surface of a ceramic component into a state of residual compression. As the first step towards tempering a ceramic, it is necessary to demonstrate that appreciable stresses can be generated by this volume change, since they may be relieved by either cracking or diffusional relaxation processes at the high temperature of the reduction reaction. It was necessary to determine the best processing methods to use for producing the tempered specimens. Results are presented from a systematic study on the effect of the variation of processing parameters on the reduction behavior of NiAl2O4 doped with ZrO2. Specimen characteristics of interest were time required for reduction, microstructural development, volume contraction achieved and porosity generated during reduction, and the ability to survive the reduction process without fracturing. These results were applied to the tempering process. A simple specimen geometry was used for tempering which involved an Al 2O3 cylinder bonded to an outer NiAl2O4 ring. Finite element calculations were performed to predict the residual stresses generated by the volume contraction of the ring and the coefficient of thermal expansion, (CTE) mismatch between the Al2O3 core and the reduced composite ring. Stress measurements performed on the Al2 O3 core of each specimen using the "d vs. Sin 2Psi" method of X-ray diffraction indicate that only the CTE-induced stresses remain in the specimens after completion of the tempering process. Microstructural analysis of the tempered specimens was performed to determine if residual stresses were developed during reduction, and what processes occurred to relieve these stresses. The results indicate that stresses are generated during the reduction process, but they are dissipated through catastrophic fracture, cation rearrangement in the lattice, and creep. Further evidence of the presence of residual stresses during reduction was found in a decrease in coarsening rate in tempered specimens.

Results of Mechanical Testing for Pyroceram(tm) Glass-Ceramic

NASA Technical Reports Server (NTRS)

Choi, Sung R.; Gyekenyesi, John P.

2003-01-01

Mechanical testing for Pyroceram (trademark) 9606 glass-ceramic fabricated by Corning was conducted to determine mechanical properties of the material including slow crack growth.Valid testing was not achieved in tension, compression, and shear testing due to inappropriate test specimen configurations provided and primarily due to the existence of fortified layer( in tension).

Influence of core thickness and artificial aging on the biaxial flexural strength of different all-ceramic materials: An in-vitro study.

PubMed

Dikicier, Sibel; Ayyildiz, Simel; Ozen, Julide; Sipahi, Cumhur

2017-05-31

The purpose of this study was to investigate the flexural strength of all-ceramics with varying core thicknesses submitted to aging. In-Ceram Alumina (IC), IPS e.max Press (EM) and Katana (K) (n=40), were selected. Each group contained two core groups based on the core thickness as follows: IC/0.5, IC/0.8, EM/0.5, EM/0.8, K/0.5 and K/0.8 mm in thickness (n=20 each). Ten specimens from each group were subjected to aging and all specimens were tested for strength in a testing machine either with or without being subjected aging. The mean strength of the K were higher (873.05 MPa) than that of the IC (548.28 MPa) and EM (374.32 MPa) regardless of core thickness. Strength values increased with increasing core thickness for all IC, EM and K regardless of aging. Results of this study concluded that strength was not significantly affected by aging. Different core thicknesses affected strength of the all-ceramic materials tested (p<0.05).

Early Pottery Making in Northern Coastal Peru. Part II: Field Firing Experiments

NASA Astrophysics Data System (ADS)

Shimada, I.; Goldstein, D.; Sosa, J.; Wagner, U.

2003-09-01

We present data from three seasons of experimental field work designed to recreate ancient Andean coastal ceramic firing techniques. Based on the recent discovery of two different archaeological ceramic production sites in the La Leche river valley of northern coastal Peru, the opportunity arose to apply Mössbauer spectroscopy and other analytical methods to reconstruct ancient firing procedures. Two sets of firings took place in 1993 and 1997 in Batán Grande using a partially restored Formative kiln from about 800 BC, local hardwood and cow dung as fuel. A third experiment followed in 2000 after the discovery of a Middle Sicán ceramics workshop in use between ca. AD 950 and 1050 at Huaca Sialupe, where an exact replica of an ancient kiln was built from local clay, and fired with local wood and cow dung. Additionally, inverted urns found at Huaca Sialupe were tested for their potential use as furnaces for metal working. Mössbauer spectroscopy was used to compare the physical and chemical state of specimens produced in the field experiments with ancient ceramics and with specimens produced in controlled laboratory experiments.

Foreign Object Damage in a Gas-Turbine Grade Silicon Nitride by Spherical Projectiles of Various Materials

NASA Technical Reports Server (NTRS)

Choi, Sung R.; Racz, Zsolt; Bhatt, Ramakrishna T.; Brewer, David N.

2006-01-01

Assessments of foreign object damage (FOD) of a commercial, gas-turbine grade, in situ toughened silicon nitride ceramic (AS800, Honeywell Ceramics Components) were made using four different projectile materials at ambient temperature. AS800 flexure target specimens rigidly supported were impacted at their centers in a velocity range from 50 to 450 m/s by spherical projectiles with a diameter of 1.59 mm. Four different projectile materials were used including hardened steel, annealed steel, silicon nitride ceramic, and brass. Post-impact strength of each target specimen impacted was determined as a function of impact velocity to appraise the severity of local impact damage. For a given impact velocity, the degree of strength degradation was greatest for ceramic balls, least for brass balls, and intermediate for annealed and hardened steel balls. For steel balls, hardened projectiles yielded more significant impact damage than annealed counterparts. The most important material parameter affecting FOD was identified as hardness of projectiles. Impact load as a function of impact velocity was quasi-statically estimated based on both impact and static indentation associated data.

Marginal Vertical Discrepancies of Monolithic and Veneered Zirconia and Metal-Ceramic Three-Unit Posterior Fixed Dental Prostheses.

PubMed

Lopez-Suarez, Carlos; Gonzalo, Esther; Pelaez, Jesus; Serrano, Benjamin; Suarez, Maria J

2016-01-01

The aim of this study was to investigate and compare the marginal fit of posterior fixed dental prostheses (FDPs) made of monolithic and veneered computer-aided design/computer-assisted manufacture (CAD/CAM) zirconia ceramic with metal-ceramic posterior FDPs. Thirty standardized steel dies were prepared to receive posterior three-unit FDPs. Specimens were randomly divided into three groups (n = 10): (1) metal-ceramic (control group), (2) veneered zirconia, and (3) monolithic zirconia. All FDPs were cemented using a glass-ionomer cement. The specimens were subjected to thermal cycling (5°C to 55°C). A scanning electron microscope (SEM) with a magnification of ×500 was used for measurements. The data were statistically analyzed using one-way analysis of variance and paired t test. Both zirconia groups showed similar vertical marginal discrepancies, and no significant differences (P = .661) in marginal adaptation were observed among the groups. No differences were observed in either group in marginal discrepancies between surfaces or abutments. Monolithic zirconia posterior FDPs exhibit similar vertical marginal discrepancies to veneered zirconia posterior FDPs. No influence of localization measurements was observed.

[Effects of magnetron sputtered ZrN on the bonding strength of titanium porcelain].

PubMed

Zhou, Shu; Zhang, Wen-yan; Guang, Han-bing; Xia, Yang; Zhang, Fei-min

2009-04-01

To investigate the effect of magnetron sputtered ZrN on the bonding strength between a low-fusing porcelain (Ti/Vita titankeramik system) and commercially pure cast titanium. Sixteen specimens were randomly assigned to test group and control group (n=8). The control group received no surface treated. Magnetron sputtered ZrN film was deposited on the surface of specimens in the test group. Then the sixteen titanium-porcelain specimens were prepared in a rectangular shape and went through three-point bending test on a universal test machine. The bond strength of Ti/porcelain was recorded. The phase composition of the specimens was analyzed using X-ray diffraction (XRD). The interface at titanium and porcelain and the titanium surface after debonding were observed with a scanning electron microscopy (SEM) and analyzed using energy depressive spectrum (EDS). New phase of ZrN was found with XRD in the test group. Statistical analysis showed higher bond strength following ZrN surface treatment in the test group [(45.991+/-0.648) MPa] than that in the control group [(29.483+/-1.007) MPa] (P=0.000). Bonded ceramic could be observed in test group, the amount of bonded ceramic was more than that in the control group. No obvious bonded ceramic in control group was found. Magnetron sputtered ZrN can improve bond strength of Ti/Vita titankeramik system significantly.

Wear Characteristics and Volume Loss of CAD/CAM Ceramic Materials.

PubMed

Zurek, Alec D; Alfaro, Maria F; Wee, Alvin G; Yuan, Judy Chia-Chun; Barao, Valentim A; Mathew, Mathew T; Sukotjo, Cortino

2018-03-06

In the field of prosthodontics, patients often require complex and extensive restorative care. This can involve the use of dental restorations to restore teeth on both the maxillary and mandibular arch. Current literature has evaluated the wear properties of different dental ceramics against enamel, but studies regarding dental ceramics opposing one another are limited. The purpose of this study was to assess the wear potential and wear behavior of CAD/CAM zirconia (ZR) and lithium disilicate (LD) materials against a similar ceramic material, and how the surface finish of these dental ceramics might affect patterns of wear. Using a sphere-on-plate tribometer system, different surface finishes (glazed-G and glazed then polished-GP) of ZR and LD were evaluated following wear simulation. Artificial saliva of physiologic pH was used as a lubricant during wear simulation at 37°C. The coefficient of friction (COF) was calculated during the wear simulation. After wear simulation was complete, volume loss, surface roughness, and surface characterization of the specimens were analyzed using white-light interferometry and scanning electron microscopy (SEM). Statistical significance between materials and surface finish was established with two-way ANOVA and Bonferroni post hoc test (α = 0.05). Based on the 2-way ANOVA, material (p = 0.002) significantly affected the COF. LD showed a higher COF (p = 0.002) than ZR. Material (p < 0.001) and surface finish (p = 0.004) significantly affected the surface roughness inside the scar. ZR had significantly lower surface roughness compared to LD (p < 0.001). For outside scar, surface finish (p < 0.001) significantly affected the surface roughness. Polished specimens showed significantly higher roughness compared to glazed specimens for both inside (p = 0.004) and outside scar (p < 0.001). For volume loss, material (p < 0.001) and the interaction between material and surface finish (p < 0.001) were statistically significant. LD had higher volume loss than ZR (p < 0.001). For both glazed and polished finished, LD-G and LD-GP had significantly higher volume loss than ZR-G (p = 0.028), and ZR-GP (p < 0.001), respectively. SEM analysis indicated particle build-up and a grooving mechanism of wear for the LD-GP specimens. This suggested a three-body wear phenomenon occurring for LD-GP specimens, which was not visible in SEM imaging for other specimen types. This study demonstrated the resistance to wear and low abrasiveness of ZR when compared to LD in a simulated masticatory environment. This can be best explained by the increased strength of ZR, and the introduction of three-body wear to LD specimens from the accumulation of embedded wear debris onto its surface. Wear data and comparison of SEM images following wear simulation confirmed this interpretation. © 2018 by the American College of Prosthodontists.

Durability evaluation of ceramic components using CARES/LIFE

NASA Technical Reports Server (NTRS)

Nemeth, Noel N.; Powers, Lynn M.; Janosik, Lesley A.; Gyekenyesi, John P.

1994-01-01

The computer program CARES/LIFE calculates the time-dependent reliability of monolithic ceramic components subjected to thermomechanical and/or proof test loading. This program is an extension of the CARES (Ceramics Analysis and Reliability Evaluation of Structures) computer program. CARES/LIFE accounts for the phenomenon of subcritical crack growth (SCG) by utilizing the power law, Paris law, or Walker equation. The two-parameter Weibull cumulative distribution function is used to characterize the variation in component strength. The effects of multiaxial stresses are modeled using either the principle of independent action (PIA), the Weibull normal stress averaging method (NSA), or the Batdorf theory. Inert strength and fatigue parameters are estimated from rupture strength data of naturally flawed specimens loaded in static, dynamic, or cyclic fatigue. Application of this design methodology is demonstrated using experimental data from alumina bar and disk flexure specimens which exhibit SCG when exposed to water.

Durability evaluation of ceramic components using CARES/LIFE

DOE Office of Scientific and Technical Information (OSTI.GOV)

Nemeth, N.N.; Janosik, L.A.; Gyekenyesi, J.P.

1996-01-01

The computer program CARES/LIFE calculates the time-dependent reliability of monolithic ceramic components subjected to thermomechanical and/or proof test loading. This program is an extension of the CARES (Ceramics Analysis and Reliability Evaluation of Structures) computer program. CARES/LIFE accounts for the phenomenon of subcritical crack growth (SCG) by utilizing the power law, Paris law, or Walker equation. The two-parameter Weibull cumulative distribution function is used to characterize the variation in component strength. The effects of multiaxial stresses are modeled using either the principle of independent action (PIA), the Weibull normal stress averaging method (NSA), or the Batdorf theory. Inert strength andmore » fatigue parameters are estimated from rupture strength data of naturally flawed specimens loaded in static, dynamic, or cyclic fatigue. Application of this design methodology is demonstrated using experimental data from alumina bar and disk flexure specimens, which exhibit SCG when exposed to water.« less

Reliability of void detection in structural ceramics using scanning laser acoustic microscopy

NASA Technical Reports Server (NTRS)

Roth, D. J.; Klima, S. J.; Kiser, J. D.; Baaklini, G. Y.

1985-01-01

The reliability of scanning laser acoustic microscopy (SLAM) for detecting surface voids in structural ceramic test specimens was statistically evaluated. Specimens of sintered silicon nitride and sintered silicon carbide, seeded with surface voids, were examined by SLAM at an ultrasonic frequency of 100 MHz in the as fired condition and after surface polishing. It was observed that polishing substantially increased void detectability. Voids as small as 100 micrometers in diameter were detected in polished specimens with 0.90 probability at a 0.95 confidence level. In addition, inspection times were reduced up to a factor of 10 after polishing. The applicability of the SLAM technique for detection of naturally occurring flaws of similar dimensions to the seeded voids is discussed. A FORTRAN program listing is given for calculating and plotting flaw detection statistics.

Bonding measurement -Strength and fracture mechanics approaches.

PubMed

Anunmana, Chuchai; Wansom, Wiroj

2017-07-26

This study investigated the effect of cross-sectional areas on interfacial fracture toughness and bond strength of bilayered dental ceramics. Zirconia core ceramics were veneered and cut to produce specimens with three different cross-sectional areas. Additionally, monolithic specimens of glass veneer were also prepared. The specimens were tested in tension until fracture at the interface and reported as bond strength. Fracture surfaces were observed, and the apparent interfacial toughness was determined from critical crack size and failure stress. The results showed that cross-sectional area had no effect on the interfacial toughness whereas such factor had a significant effect on interfacial bond strength. The study revealed that cross-sectional area had no effect on the interfacial toughness, but had a significant effect on interfacial bond strength. The interfacial toughness may be a more reliable indicator for interfacial bond quality than interfacial bond strength.

Back-Face Strain for Monitoring Stable Crack Extension in Precracked Flexure Specimens

NASA Technical Reports Server (NTRS)

Salem, Jonathan A.; Ghosn, Louis J.

2010-01-01

Calibrations relating back-face strain to crack length in precracked flexure specimens were developed for different strain gage sizes. The functions were verified via experimental compliance measurements of notched and precracked ceramic beams. Good agreement between the functions and experiments occurred, and fracture toughness was calculated via several operational methods: maximum test load and optically measured precrack length; load at 2 percent crack extension and optical precrack length; maximum load and back-face strain crack length. All the methods gave vary comparable results. The initiation toughness, K(sub Ii) , was also estimated from the initial compliance and load.The results demonstrate that stability of precracked ceramics specimens tested in four-point flexure is a common occurrence, and that methods such as remotely-monitored load-point displacement are only adequate for detecting stable extension of relatively deep cracks.

Report on the Installation and Preparedness of a Protochips Fusion in-situ Heating Holder for TEM

DOE Office of Scientific and Technical Information (OSTI.GOV)

Edmondson, Philip D.

2017-03-01

This brief report documents the procurement and installation of a Protochips Fusion (formerly Aduro) high-temperature, high stability transmission electron microscopy (TEM) specimen holder that allows for the high spatial resolution characterization of material specimens at high temperature in situ of an electron microscope. This specimen holder was specifically procured for use with The FEI Talos F200X Scanning/Transmission Electron Microscope (STEM) in Oak Ridge National Laboratory’s (ORNL’s) Low Activation Materials Development and Analysis (LAMDA) Laboratory. The Protochips Fusion holder will enable high-resolution structural and chemical analysis of irradiated materials at high temperature, becoming a unique capability worldwide, and would encourage high-qualitymore » in situ experiments to be conducted on irradiated materials.« less

Self-aligning hydraulic piston assembly for tensile testing of ceramic

DOEpatents

Liu, Kenneth C.

1987-01-01

The present invention is directed to a self-aligning grip housing assembly that can transmit an uniaxial load to a tensil specimen without introducing bending stresses into the specimen. Disposed inside said grip housing assembly are a multiplicity of supporting pistons connected to a common source of pressurized oil that carry equal shares of the load applied to the specimen irregardless whether there is initial misalignment between the specimen load column assembly and housing axis.

Self-aligning hydraulic piston assembly for tensile testing of ceramic

DOEpatents

Liu, K.C.

1987-08-18

The present invention is directed to a self-aligning grip housing assembly that can transmit an uniaxial load to a tensile specimen without introducing bending stresses into the specimen. Disposed inside said grip housing assembly are a multiplicity of supporting pistons connected to a common source of pressurized oil that carry equal shares of the load applied to the specimen regardless whether there is initial misalignment between the specimen load column assembly and housing axis. 4 figs.

Wetting characteristic of ceramic to water and adhesive resin.

PubMed

Oh, Won-Suck; Shen, Chiayi; Alegre, Brandon; Anusavice, Kenneth J

2002-12-01

Maximum wetting of ceramic by adhesive resin is required to achieve optimal adhesion of the resin to ceramic. It is unknown whether the adhesion of the resin to the ceramic is affected by the surface topography and wetting by water or the adhesive resin. This study was designed to characterize the effect of surface topography on the wetting of ceramics by water and adhesive resin. Three materials, a veneering ceramic, Eris (ERV), and 2 core ceramics, Empress 1 core ceramic (E1C) and an experimental core ceramic (EXC), were used. Four surface-roughening procedures were used. They included polishing through 1200-grit SiC paper (P), air abrasion with 50 microm Al(2)O(3) (A), etching with 5% hydrofluoric acid gel (E), and a combination of airborne particle abrasion and etching (A/E). Forty bar specimens (15 x 10 x 1.5 mm) were prepared from each material (N=120). Twelve groups of 10 specimens each were prepared for the 4 surface-roughening procedures. Advancing (theta(A)) and receding (theta(R)) contact angles were measured with a CAHN Dynamic Contact Analyzer, on the basis of the Wilhelmy plate technique, with water and adhesive resin. The work of adhesion (W(A)) by the probing media was calculated by use of advancing contact angle data. The data were analyzed by t testing, analysis of variance, and Duncan's tests (alpha=0.05) to determine the statistical significance of differences in the contact angles between ceramic and water or resin as a function of surface roughening. In general, the mean theta(A) values were higher than the mean theta(R) values except for groups of E or A/E specimens with water used as a probing medium. E and A/E treatments yielded the lowest contact angle values, followed by A and P treatments (P<.001). The E1C exhibited the highest mean contact angles, whereas EXC exhibited the lowest mean contact angle except for the theta(R) with resin. The corresponding values for ERV were between those of E1C and EXC except for theta(R) values with resin. The resin medium yielded higher mean contact angles than the water medium for the same surfaces. W(A) ranged from 62.9 to 145.2 mJ/m(2). Within the limitations of this study, etching or a combination of air abrasion and etching were comparably effective in increasing the surface area for bonding. The most wettable surface as measured by the resin medium was EXC, followed by ERV and E1C.

Marginal discrepancy of noble metal-ceramic fixed dental prosthesis frameworks fabricated by conventional and digital technologies.

PubMed

Afify, Ahmed; Haney, Stephan; Verrett, Ronald; Mansueto, Michael; Cray, James; Johnson, Russell

2018-02-01

Studies evaluating the marginal adaptation of available computer-aided design and computer-aided manufacturing (CAD-CAM) noble alloys for metal-ceramic prostheses are lacking. The purpose of this in vitro study was to evaluate the vertical marginal adaptation of cast, milled, and direct metal laser sintered (DMLS) noble metal-ceramic 3-unit fixed partial denture (FDP) frameworks before and after fit adjustments. Two typodont teeth were prepared for metal-ceramic FDP abutments. An acrylic resin pattern of the prepared teeth was fabricated and cast in nickel-chromium (Ni-Cr) alloy. Each specimen group (cast, milled, DMLS) was composed of 12 casts made from 12 impressions (n=12). A single design for the FDP substructure was created on a laboratory scanner and used for designing the specimens in the 3 groups. Each specimen was fitted to its corresponding cast by using up to 5 adjustment cycles, and marginal discrepancies were measured on the master Ni-Cr model before and after laboratory fit adjustments. The milled and DMLS groups had smaller marginal discrepancy measurements than those of the cast group (P<.001). Significant differences were found in the number of adjustments among the groups, with the milled group requiring the minimum number of adjustments, followed by the DMLS and cast groups (F=30.643, P<.001). Metal-ceramic noble alloy frameworks fabricated by using a CAD-CAM workflow had significantly smaller marginal discrepancies compared with those with a traditional cast workflow, with the milled group demonstrating the best marginal fit among the 3 test groups. Manual refining significantly enhanced the marginal fit of all groups. All 3 groups demonstrated marginal discrepancies within the range of clinical acceptability. Copyright © 2017 Editorial Council for the Journal of Prosthetic Dentistry. Published by Elsevier Inc. All rights reserved.

Effect of ceramic infrastructure on the failure behavior and stress distribution of fixed partial dentures.

PubMed

Borba, Márcia; Duan, Yuanyuan; Griggs, Jason A; Cesar, Paulo F; Della Bona, Álvaro

2015-04-01

The effect of the ceramic infrastructure (IS) on the failure behavior and stress distribution of fixed partial dentures (FPDs) was evaluated. Twenty FPDs with a connector cross-section of 16 mm(2) were produced for each IS and veneered with porcelain: (YZ) Vita In-Ceram YZ/Vita VM9 porcelain; (IZ) Vita In-Ceram Zirconia/Vita VM7 porcelain; (AL) Vita In-Ceram AL/Vita VM7 porcelain. Two experimental conditions were evaluated (n = 10). For control specimens, load was applied in the center of the pontic at 0.5 mm/min until failure, using a universal testing machine, in 37°C deionized water. For mechanical cycling (MC) specimens, FPDs were subjected to MC (2 Hz, 140 N, 10(6) cycles) and subsequently tested as described for the control group. For YZ, an extra group of 10 FPDs were built with a connector cross-section of 9 mm(2) and tested until failure. Fractography and FEA were performed. Data were analyzed by ANOVA and Tukey's test (α = 0.05). YZ16 showed the greatest fracture load mean value, followed by YZ16-MC. Specimens from groups YZ9, IZ16, IZ16-MC, AL16 and AL16-MC showed no significant difference for the fracture load. The failure behavior and stress distribution of FPDs was influenced by the type of IS. AL and IZ FPDs showed similar fracture load values but different failure modes and stress distribution. YZ showed the best mechanical behavior and may be considered the material of choice to produce posterior FPDs as it was possible to obtain a good mechanical performance even with a smaller connector dimension (9 mm(2)). Copyright © 2015 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Physical and adhesive properties of dental enamel after radiotherapy and bonding of metal and ceramic brackets.

PubMed

Santin, Gabriela Cristina; Palma-Dibb, Regina Guenka; Romano, Fábio Lourenço; de Oliveira, Harley Francisco; Nelson Filho, Paulo; de Queiroz, Alexandra Mussolino

2015-08-01

The increasing success rates for cancer patients treated with radiotherapy and the frequent occurrence of tooth loss during treatment have led to an increased demand for orthodontic treatment after radiotherapy. The aim of this study was to evaluate tooth enamel of irradiated teeth after the bonding and debonding of metal and ceramic brackets. Ten permanent molars were cut into enamel fragments measuring 1 mm(2) and divided into an irradiated group (total dose of 60 Gy) and a nonirradiated group. The fragments were subjected to microshear testing to evaluate whether radiotherapy altered the strength of the enamel. Furthermore, 90 prepared premolars were divided into 6 groups and subgroups (n = 15): group 1, nonirradiated and nonaged; group 2, nonirradiated and aged (thermal cycled); group 3, irradiated and aged; each group was divided into 2 subgroups: metallic and ceramic brackets. After thermal cycling and radiotherapy, the brackets were bonded onto the specimens with Transbond XT (3M Unitek, Monrovia, Calif). After 24 hours, the specimens were subjected to the shear tests. Images of the enamel surfaces were classified using the adhesive remnant index. The composite resin-enamel interface was also evaluated. Enamel fragments subjected to radiation had lower strength than did the nonirradiated samples (P <0.05). The groups and subgroups submitted to radiation and bonded ceramic brackets had the lowest strength values. Groups 1 and 2 with metallic brackets had less adhesive on the surface, whereas groups 1 and 2 with ceramic brackets and group 3 with both metallic and ceramic brackets had more adhesive on the surfaces. On the images of the composite resin-enamel interface, resin tags were more extensive on irradiated tooth enamel. Radiation decreased tooth enamel strength, and the specimens treated with radiotherapy had higher frequencies of adhesive failure between the bracket and the composite resin as well as more extensive tags. Copyright © 2015 American Association of Orthodontists. Published by Elsevier Inc. All rights reserved.

Wear of enamel and veneering ceramics after laboratory and chairside finishing procedures.

PubMed

Magne, P; Oh, W S; Pintado, M R; DeLong, R

1999-12-01

This in vitro study compared the wear of enamel against 3 types of ceramics with high esthetic potential (designed for layering techniques): feldspathic porcelain (Creation), aluminous porcelain (Vitadur alpha), and low-fusing glass (Duceram-LFC). Laboratory finishing (glazing/polishing) and chairside polishing with a Dialite kit were simulated to compare their respective effects on wear. Tooth-material specimen pairs were placed in an artificial mouth using closed-loop servohydraulics. Constant masticatory parameters (13.5 N occlusal force, 0.62 mm lateral excursion; 0.23 second cuspal contact time) were maintained for 300, 000 cycles at a rate of 4 Hz. The occlusal surface of each pair was mapped and digitally recorded before and after each masticatory test. Quantitative changes were measured in terms of depth and volume of wear. Quantitative wear characteristics were assessed by SEM. Significant differences were observed (2-factor ANOVA, P <.05). Duceram-LFC generated increased volume loss of enamel (0.197 mm(3)) compared with Creation (0.135 mm(3)) and Vitadur alpha (0.153 mm(3)). Creation exhibited the lowest ceramic wear and lowest combined volume loss (0.260 mm(3); the sum of the data for enamel and the opposing material) compared with Duceram-LFC (0.363 mm(3)) and Vitadur alpha (0.333 mm(3)). The most significant differences among materials were observed in volume loss, not in depth of wear. For all 3 ceramic systems, qualitative SEM evaluation revealed an abrasive type of wear. Wear characteristics of chairside polished specimens were similar to those of laboratory finished specimens (glazed and polished). Duceram-LFC was the most abrasive ceramic for the antagonistic tooth. Creation ceramic was the least abrasive material and most resistant to wear. Defects, brittleness, and the possibly insufficient toughness of LFC may explain its increased abrasiveness. Laboratory and chairside finishing procedures generated similar results.

Transmission electron microscopy observations on phase transformations during aluminium/mullite composites formation by gas pressure infiltration

DOE Office of Scientific and Technical Information (OSTI.GOV)

Pawlyta, M., E-mail: miroslawa.pawlyta@polsl.pl; Tomiczek, B.; Dobrzański, L.A.

The porous ceramic preforms were manufactured using the powder metallurgy technique. First, the start-up material (halloysite with the addition of carbon fibres as the pore-forming agent) was slowly heated to 800 °C and then sintered at 1300 °C. Degradation of the carbon fibres enabled the open canals to form. At the end of the sintering process, the porous ceramic material consisting mainly of two phases (mullite and cristobalite) was formed, without any residual carbon content. During infiltration, the liquid metal filled the empty spaces (pores) effectively and formed the three-dimensional network of metal in the ceramic. The cristobalite was almostmore » entirely decomposed. In the areas of its previous occurrence, there are new pores, only in the ceramic grains. The mullite, which was formed from halloysite during annealing, crystallized in the Pbam orthorhombic space group, with the (3Al{sub 2}O{sub 3}·2SiO{sub 2}) stoichiometric composition. The mullite structure does not change during the infiltration. The composite components are tightly connected. A transition zone between the ceramics and the metal, having the thickness of about 200 nm, was formed. The nanocrystalline zone, identified as γ-Al{sub 2}O{sub 3}, was formed by diffusing the product of the cristobalite decomposition into the aluminium alloy matrix. There is an additional, new phase, identified as (Mg,Si)Al{sub 2}O{sub 4} in the outer parts of the transition zone. - Highlights: • Phase changes after the infiltration of aluminium into porous mullite preforms were observed by TEM. • TEM observations confirm that during infiltration cristobalite was decomposed and the structure of mullite did not change. • Between the ceramic and the metal, a transition zone comprising a layer of γ-Al{sub 2}O{sub 3} and (Mg,Si)Al{sub 2}O{sub 4} was formed.« less

Characterization of fatigue behavior of 2-D woven fabric reinforced ceramic matrix composite at elevated temperature. Final report

DOE Office of Scientific and Technical Information (OSTI.GOV)

Groner, D.J.

This study investigated the fatigue behavior and associated damage mechanisms in notched and unnotched enhanced SiC/SiC ceramic matrix composite specimens at 1100 deg C. Stiffness degradation, strain variation, and hysteresis were evaluated to characterize material behavior. Microscopic examination was performed to characterize damage mechanisms. During high cycle/low stress fatigue tests, far less fiber/matrix interface debond was evident than in low cycle/high stress fatigue tests. Notched specimens exhibited minimal stress concentration during monotonic tensile testing and minimal notch sensitivity during fatigue testing. Damage mechanisms were also similar to unnotched.

Effects of Different Surface Treatment Methods and MDP Monomer on Resin Cementation of Zirconia Ceramics an In Vitro Study

PubMed Central

Tanış, Merve Çakırbay; Akçaboy, Cihan

2015-01-01

Introduction: Resin cements are generally preferred for cementation of zirconia ceramics. Resin bonding of zirconia ceramics cannot be done with the same methods of traditional ceramics because zirconia is a silica-free material. In recent years, many methods have been reported in the literature to provide the resin bonding of zirconia ceramics. The purpose of this in vitro study is to evaluate effects of different surface treatments and 10-metacryloxydecyl dihydrogen phosphate (MDP) monomer on shear bond strength between zirconia and resin cement. Methods: 120 zirconia specimens were treated as follows: Group I: sandblasting, group II: sandblasting + tribochemical silica coating + silane, group III: sandblasting + Nd:YAG (neodymium: yttrium-aluminum-garnet) laser. One specimen from each group was evaluated under scanning electron microscope (SEM). Specimens in each group were bonded either with conventional resin cement Variolink II or with a MDP containing resin cement Panavia F2.0. Subgroups of bonded specimens were stored in distilled water (37°C) for 24 hours or 14 days. Following water storage shear bond strength test was performed at a crosshead speed of 1 mm/min in a universal test machine. Then statistical analyses were performed. Results: Highest shear bond strength values were observed in group II. No significant difference between group I and III was found when Panavia F2.0 resin cement was used. When Variolink II resin cement was used group III showed significantly higher bond strength than group I. In group I, Panavia F2.0 resin cement showed statistically higher shear bond strength than Variolink II resin cement. In group II no significant difference was found between resin cements. No significant difference was found between specimens stored in 37°C distilled water for 24 hours and 14 days. In group I surface irregularities with sharp edges and grooves were observed. In group II less roughened surface was observed with silica particles. In group III surface microcracks connecting each other were observed. Conclusion: Tribochemical silica coating is an effective method for achieving an acceptable bond between zirconia and resin cement. Use of a MDP monomer containing resin cement increases the bond strength of sandblasted zirconia. PMID:26705464

Surface deterioration of dental materials after simulated toothbrushing in relation to brushing time and load.

PubMed

Heintze, S D; Forjanic, M; Ohmiti, K; Rousson, V

2010-04-01

(1) To evaluate the changes in surface roughness and gloss after simulated toothbrushing of 9 composite materials and 2 ceramic materials in relation to brushing time and load in vitro; (2) to assess the relationship between surface gloss and surface roughness. Eight flat specimens of composite materials (microfilled: Adoro, Filtek Supreme, Heliomolar; microhybrid: Four Seasons, Tetric EvoCeram; hybrid: Compoglass F, Targis, Tetric Ceram; macrohybrid: Grandio), two ceramic materials (IPS d.SIGN and IPS Empress polished) were fabricated according to the manufacturer's instructions and optimally polished with up to 4000 grit SiC. The specimens were subjected to a toothbrushing (TB) simulation device (Willytec) with rotating movements, toothpaste slurry and at three different loads (100g/250g/350g). At hourly intervals from 1h to 10h TB, mean surface roughness Ra was measured with an optical sensor and the surface gloss (Gl) with a glossmeter. Statistical analysis was performed for log-transformed Ra data applying two-way ANOVA to evaluate the interaction between load and material and load and brushing time. There was a significant interaction between material and load as well as between load and brushing time (p<0.0001). The microhybrid and hybrid materials demonstrated more surface deterioration with higher loads, whereas with the microfilled resins Heliomolar and Adoro it was vice versa. For ceramic materials, no or little deterioration was observed over time and independent of the load. The ceramic materials and 3 of the composite materials (roughness) showed no further deterioration after 5h of toothbrushing. Mean surface gloss was the parameter which discriminated best between the materials, followed by mean surface roughness Ra. There was a strong correlation between surface gloss and surface roughness for all the materials except the ceramics. The evaluation of the deterioration curves of individual specimens revealed a more or less synchronous course suspecting hinting specific external conditions and not showing the true variability in relation to the tested material. The surface roughness and gloss of dental materials changes with brushing time and load and thus results in different material rankings. Apart from Grandio, the hybrid composite resins were more prone to surface changes than microfilled composites. The deterioration potential of a composite material can be quickly assessed by measuring surface gloss. For this purpose, a brushing time of 10h (=72,000 strokes) is needed. In further comparative studies, specimens of different materials should be tested in one series to estimate the true variability. Copyright (c) 2009 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Measuring Poisson Ratios at Low Temperatures

NASA Technical Reports Server (NTRS)

Boozon, R. S.; Shepic, J. A.

1987-01-01

Simple extensometer ring measures bulges of specimens in compression. New method of measuring Poisson's ratio used on brittle ceramic materials at cryogenic temperatures. Extensometer ring encircles cylindrical specimen. Four strain gauges connected in fully active Wheatstone bridge self-temperature-compensating. Used at temperatures as low as liquid helium.

[Effect of vacuum deposition technology on the metal-porcelain bond strength of a new type of CO-CR ceramic and framework dental alloy].

PubMed

Wu, Jun-ling; Chao, Yong-lie; Ji, Ping; Gao, Xu

2007-10-01

To investigate the effect of a new engineering technique of vacuum deposition-plasma magnetron reactive sputter deposition technique on the metal-porcelain bond strength of a new type of Co-Cr ceramic and framework dental alloy. Before porcelain painted on the specimens, the standardized metal strips made from DA9-4 dental alloy were coated with a thin Al2O3 ceramic film by plasma magnetron reactive sputter deposition technique. The conformation, structure and thickness of the ceramic film were analyzed. The specimens for three-point bending test made from DA9-4 alloy and VMK95 porcelain were used for metal-porcelain bond strength measurement, in the same time the interface of metal-porcelain and element distribution were also observed. The flexural bonding strength of metal-porcelain of sputtering group and control group were (180.55+/-16.45) MPa and (143.80+/-24.49) MPa. The flexural bonding strength of metal-porcelain of sputtering group was higher than control group significantly through statistical analysis (P<0.01). The plasma magnetron reactive sputter deposition technique has a positive effect in improving the bonding strength of DA9-4 dental alloy and ceramic.

Surface preparation for high purity alumina ceramics enabling direct brazing in hydrogen atmospheres

DOEpatents

Cadden, Charles H.; Yang, Nancy Yuan Chi; Hosking, Floyd M.

2001-01-01

The present invention relates to a method for preparing the surface of a high purity alumina ceramic or sapphire specimen that enables direct brazing in a hydrogen atmosphere using an active braze alloy. The present invention also relates to a method for directly brazing a high purity alumina ceramic or sapphire specimen to a ceramic or metal member using this method of surface preparation, and to articles produced by this brazing method. The presence of silicon, in the form of a SiO.sub.2 -containing surface layer, can more than double the tensile bond strength in alumina ceramic joints brazed in a hydrogen atmosphere using an active Au-16Ni-0.75 Mo-1.75V filler metal. A thin silicon coating applied by PVD processing can, after air firing, produce a semi-continuous coverage of the alumina surface with a SiO.sub.2 film. Room temperature tensile strength was found to be proportional to the fraction of air fired surface covered by silicon-containing films. Similarly, the ratio of substrate fracture versus interface separation was also related to the amount of surface silicon present prior to brazing. This process can replace the need to perform a "moly-manganese" metallization step.

Tests of NASA ceramic thermal barrier coating for gas-turbine engines

NASA Technical Reports Server (NTRS)

Liebert, C. H.

1979-01-01

A two-layer thermal barrier coating system with a bond coating of nickel-chromium-aluminum-yttrium and a ceramic coating of yttria-stabilized zirconia was tested for corrosion protection, thermal protection and durability. Full-scale gas-turbine engine tests demonstrated that this coating eliminated burning, melting, and warping of uncoated parts. During cyclic corrosion resistance tests made in marine diesel fuel products of combustion in a burner rig, the ceramic cracked on some specimens. Metallographic examination showed no base metal deterioration.

Low temperature sintering of fluorapatite glass-ceramics.

PubMed

Denry, Isabelle; Holloway, Julie A

2014-02-01

Fluorapatite glass-ceramics have been shown to be excellent candidates as scaffold materials for bone grafts, however, scaffold production by sintering is hindered by concurrent crystallization of the glass. Objective, our goal was to investigate the effect of Ca/Al ratio on the sintering behavior of Nb-doped fluorapatite-based glasses in the SiO2-Al2O3-P2O5-MgO-Na2O-K2O-CaO-CaF2 system. Methods, glass compositions with Ca/Al ratio of 1 (A), 2 (B), 4 (C) and 19 (D) were prepared by twice melting at 1525°C for 3h. Glasses were either cast as cylindrical ingots or ground into powders. Disk-shaped specimens were prepared by either sectioning from the ingots or powder-compacting in a mold, followed by heat treatment at temperatures ranging between 700 and 1050°C for 1h. The density was measured on both sintered specimens and heat treated discs as controls. The degree of sintering was determined from these measurements. Results and Significance XRD showed that fluorapatite crystallized in all glass-ceramics. A high degree of sintering was achieved at 775°C for glass-ceramic D (98.99±0.04%), and 900°C for glass-ceramic C (91.31±0.10). Glass-ceramics A or B were only partially sintered at 1000°C (63.6±0.8% and 74.1±1.5%, respectively). SEM revealed a unique microstructure of micron-sized spherulitic fluorapatite crystals in glass-ceramics C and D. Increasing the Ca/Al ratio promoted low temperature sintering of fluorapatite glass-ceramics, which are traditionally difficult to sinter. Copyright © 2013 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Low temperature sintering of fluorapatite glass-ceramics

PubMed Central

Denry, Isabelle; Holloway, Julie A.

2014-01-01

Fluorapatite glass-ceramics have been shown to be excellent candidates as scaffold materials for bone grafts, however, scaffold production by sintering is hindered by concurrent crystallization of the glass. Our goal was to investigate the effect of Ca/Al ratio on the sintering behavior of Nb-doped fluorapatite-based glasses in the SiO2-Al2O3-P2O5-MgO-Na2O-K2O-CaO-CaF2 system. Glass compositions with Ca/Al ratio of 1 (A), 2 (B), 4 (C) and 19 (D) were prepared by twice melting at 1525°C for 3h. Glasses were either cast as cylindrical ingots or ground into powders. Disc-shaped specimens were prepared by either sectioning from the ingots or powder-compacting in a mold, followed by heat treatment at temperatures ranging between 700 and 1050°C for 1h. The density was measured on both sintered specimens and heat treated discs as controls. The degree of sintering was determined from these measurements. XRD showed that fluorapatite crystallized in all glass-ceramics. A high degree of sintering was achieved at 775°C for glass-ceramic D (98.99±0.04%), and 900°C for glass-ceramic C (91.31±0.10). Glass-ceramics A or B were only partially sintered at 1000°C (63.6±0.8% and 74.1±1.5%, respectively). SEM revealed a unique microstructure of micron-sized spherulitic fluorapatite crystals in glass-ceramics C and D. Increasing the Ca/Al ratio promoted low temperature sintering of fluorapatite glass-ceramics, which are traditionally difficult to sinter. PMID:24252652

Effect of Nd: YAG laser irradiation on surface properties and bond strength of zirconia ceramics.

PubMed

Liu, Li; Liu, Suogang; Song, Xiaomeng; Zhu, Qingping; Zhang, Wei

2015-02-01

This study investigated the effect of neodymium-doped yttrium aluminum garnet (Nd: YAG) laser irradiation on surface properties and bond strength of zirconia ceramics. Specimens of zirconia ceramic pieces were divided into 11 groups according to surface treatments as follows: one control group (no treatment), one air abrasion group, and nine laser groups (Nd: YAG irradiation). The laser groups were divided by applying with different output power (1, 2, or 3 W) and irradiation time (30, 60, or 90 s). Following surface treatments, the morphological characteristics of ceramic pieces was observed, and the surface roughness was measured. All specimens were bonded to resin cement. After, stored in water for 24 h and additionally aged by thermocycling, the shear bond strength was measured. Dunnett's t test and one-way ANOVA were performed as the statistical analyses for the surface roughness and the shear bond strength, respectively, with α = .05. Rougher surface of the ceramics could be obtained by laser irradiation with higher output power (2 and 3 W). However, cracks and defects were also found on material surface. The shear bond strength of laser groups was not obviously increased, and it was significantly lower than that of air abrasion group. No significant differences of the shear bond strength were found among laser groups treated with different output power or irradiation time. Nd: YAG laser irradiation cannot improve the surface properties of zirconia ceramics and cannot increase the bond strength of the ceramics. Enhancing irradiation power and extending irradiation time cannot induce higher bond strength of the ceramics and may cause material defect.

Fatigue resistance and microleakage of CAD/CAM ceramic and composite molar crowns.

PubMed

Kassem, Amr S; Atta, Osama; El-Mowafy, Omar

2012-01-01

The aim of this study was to determine effect of compressive cyclic loading on fatigue resistance and microleakage of monolithic CAD/CAM molar ceramic and composite crowns. Thirty-two extracted molars were prepared to receive CEREC crowns according to manufacturer's guidelines using a special paralleling device (Parallel-A-Prep). Sixteen feldspathic ceramic crowns (VITABLOCS Mark II) (VMII) and 16 resin-composite crowns (Paradigm-MZ100 blocks) (PMZ) were milled using a CEREC-3D machine. Eight crowns of each group were cemented to their respective teeth using self-etching resin cement (Panavia-F-2.0) (PAN), and eight were cemented using self-adhesive resin cement (RelyX-Unicem-Clicker) (RXU). Following storage for 1 week in water, specimens were subjected to uniaxial compressive cyclic loading in an Instron testing machine at 12 Hz for 1,000,000 cycles. Load was applied at the central fossa, and the cycle range was 60-600 N. Specimens were then subjected to microleakage testing. Data were statistically analyzed using factorial ANOVA and Post Hoc (Tukey HSD) tests. All composite crowns survived compressive cyclic loading without fracture, while three ceramic crowns from the subgroup cemented with RXU developed surface cracks at the center of occlusal surfaces, extending laterally. Microleakage scores of ceramic crowns cemented with PAN were significantly lower than those of the other three subgroups (p < 0.05). After 1,000,000 cycles of compressive cyclic loading, PMZ composite molar crowns were more fatigue-resistant than VMII ceramic crowns. Cement type had a significant effect on fatigue resistance of the ceramic crowns but not the composite ones. Microleakage scores of ceramic crowns cemented with PAN were significantly lower than those of the other subgroups (p < 0.05). © 2011 by The American College of Prosthodontists.

Effect of surface treatments and coffee thermocycling on the color and translucency of CAD-CAM monolithic glass-ceramic.

PubMed

Alp, Gulce; Subasi, Meryem Gulce; Johnston, William M; Yilmaz, Burak

2018-03-15

The effects of surface treatments and coffee thermocycling on the color and relative translucency of a recently introduced computer-aided design and computer-aided manufacturing (CAD-CAM) monolithic glass-ceramic are unknown. The purpose of this in vitro study was to evaluate the effect of coffee thermocycling on the color and relative translucency parameter (RTP) of CAD-CAM monolithic glass-ceramics after different surface treatments. Specimens (1.5-mm-thick) were sectioned from zirconia-reinforced lithium silicate glass-ceramic (ZLS) (n=18) and lithium disilicate glass-ceramic (LDS) blocks (n=18). Two different types of surface treatments (glazing or polishing) were applied to the specimens. The specimens were subjected to 5000 thermocycles in a coffee solution. The color coordinates of specimens were measured before and after coffee thermocycling by using a spectroradiometer, and color differences and relative translucency values were calculated by using CIEDE2000 color difference and RTP formulas. ANOVA was used to analyze the color difference and relative translucency values by using maximum likelihood estimation and the Satterthwaite degrees of freedom methods. Any significant interaction between surface subgroups was further analyzed by using the Tukey-Kramer adjustment (α=.05). Material type had a significant effect on color difference (P=.018). All color difference values of all materials were smaller than the clinical acceptability threshold (<1.8 units). For relative translucency, material (P<.001) and coffee thermocycling had a significant effect (P=.014), and an interaction was found between the surface treatments and materials (P<.001). The Tukey-Kramer test revealed significant differences between glazed and polished subgroups of LDS material, except for ZLS-glazed and ZLS-polished subgroups. Different surface treatments of CAD-CAM monolithic zirconia-reinforced lithium silicate and lithium disilicate glass-ceramics resulted in clinically acceptable color changes after coffee thermocycling. The color changes in all groups, except for LDS-polished, were not perceivable. Lithium disilicate was more translucent than zirconia-reinforced lithium silicate before and after coffee thermocycling. Coffee thermocycling decreased the translucency of both of the materials. Different surface treatments affected the translucency of only lithium disilicate for tested thickness. Copyright © 2017 Editorial Council for the Journal of Prosthetic Dentistry. Published by Elsevier Inc. All rights reserved.

Shear Bond Strength of Repair Systems to New CAD/CAM Restorative Materials.

PubMed

Üstün, Özlem; Büyükhatipoğlu, Işıl Keçik; Seçilmiş, Aslı

2016-11-23

To evaluate the bond strength of repair systems (Ceramic Repair, Clearfil Repair) to computer-aided design/computer-assisted machining (CAD/CAM) restorative materials (IPS e.max CAD, Vita Suprinity, Vita Enamic, Lava Ultimate). Thermally aged CAD/CAM restorative material specimens (5000 cycles between 5°C and 55°C) were randomly divided into two groups according to the repair system: Ceramic Repair (37% phosphoric acid + Monobond-S + Heliobond + Tetric N Ceram) or Clearfil Repair (40% phosphoric acid + mixture of Clearfil Porcelain Bond Activator and Clearfil SE Bond Primer + Clearfil SE Bond + Filtek Z250). The resin composite was light-cured on conditioned specimens. All specimens were stored in distilled water at 37°C for 24 hours and then additionally aged for 5000 thermal cycles. The shear bond strength test was performed using a universal testing machine (0.5 mm/min). Two-way ANOVA was used to detect significance differences according to the CAD/CAM material and composite repair system factors. Subgroup analyses were conducted using the least significant difference post-hoc test. The results of two-way ANOVA indicated that bond strength values varied according to the restorative materials (p < 0.05). No significant differences were observed between the CAD/CAM restorative materials (p > 0.05), except in the Vita Suprinity group (p < 0.05). Moreover, no differences were observed between the repair systems. Both the Clearfil and Ceramic repair systems used in the study allow for successful repairs. © 2016 by the American College of Prosthodontists.

Transmission Kikuchi diffraction and transmission electron forescatter imaging of electropolished and FIB manufactured TEM specimens

DOE Office of Scientific and Technical Information (OSTI.GOV)

Zieliński, W., E-mail: wiziel@inmat.pw.edu.pl; Płociński, T.; Kurzydłowski, K.J.

2015-06-15

We present a study of the efficiency of the utility of scanning electron microscope (SEM)-based transmission methods for characterizing grain structure in thinned bulk metals. Foils of type 316 stainless steel were prepared by two methods commonly used for transmission electron microscopy — double-jet electropolishing and focused ion beam milling. A customized holder allowed positioning of the foils in a configuration appropriate for both transmission electron forward scatter diffraction, and for transmission imaging by the use of a forescatter detector with two diodes. We found that both crystallographic orientation maps and dark-field transmitted images could be obtained for specimens preparedmore » by either method. However, for both methods, preparation-induced artifacts may affect the quality or accuracy of transmission SEM data, especially those acquired by the use of transmission Kikuchi diffraction. Generally, the quality of orientation data was better for specimens prepared by electropolishing, due to the absence of ion-induced damage. - Highlights: • The transmission imaging and diffraction techniques are emerging in scanning electron microscopy (SEM) as promising new field of materials characterization. • The manuscript titled: “Transmission Kikuchi Diffraction and Transmission Electron Forescatter Imaging of Electropolished and FIB Manufactured TEM Specimens” documents how different specimen thinning procedures can effect efficiency of transmission Kikuchi diffraction and transmission electron forescatter imaging. • The abilities to make precision crystallographic orientation maps and dark-field images in transmission was studied on electropolished versus focus ion beam manufactured TEM specimens. • Depending on the need, electropolished and focused ion beam technique may produce suitable specimens for transmission imaging and diffraction in SEM.« less

The effect of storage conditions, contamination modes and cleaning procedures on the resin bond strength to lithium disilicate ceramic.

PubMed

Klosa, Karsten; Wolfart, Stefan; Lehmann, Frank; Wenz, Hans-Jürgen; Kern, Matthias

2009-04-01

The purpose of this in-vitro study was to evaluate the resin bond strength to pre-etched lithium disilicate ceramic using different cleaning methods after two contamination modes (saliva or saliva and silicone). Plexiglas tubes filled with composite resin (MultiCore Flow) were bonded to etched and silanized ceramic disks made of lithium disilicate ceramic (IPS e.max Press) using a luting resin (Multilink Automix). Either etched or unetched ceramic surfaces were contaminated with saliva or with saliva followed by a disclosing silicone. Groups of 16 specimens each were bonded after pretreatment using 4 surface cleaning agents (37% phosphoric acid, 5% hydrofluoric acid, 96% isopropanol, air polishing device with sodium bicarbonate) in different combinations. Before measuring tensile bond strength, specimens were stored for 3 or 150 days with thermocycling. After 150 days of storage, etching of saliva-contaminated surfaces with 5% hydrofluoric acid and/or 37% phosphoric acid provided statistically significantly higher bond strengths (37.9 to 49.5 MPa) than the other cleaning methods (1.7 to 15.5 MPa). After saliva and silicone contamination, etching with 5% hydrofluoric acid provided statistically significantly higher bond strengths (44.5 to 50.3 MPa) than all other cleaning methods (0.3 to 13.5 MPa). Ceramic cleaning methods after try-in procedures have a significant influence on the resin bond strength and are dependent on the type of contamination. Re-etching lithium disilicate ceramic with 5% hydrofluoric acid is most effective in removing contamination with saliva and/or a silicone disclosing medium.

Effect of processing induced particle alignment on the fracture toughness and fracture behavior of multiphase dental ceramics.

PubMed

Gonzaga, Carla C; Okada, Cristina Yuri; Cesar, Paulo F; Miranda, Walter G; Yoshimura, Humberto N

2009-11-01

To investigate the processing induced particle alignment on fracture behavior of four multiphase dental ceramics (one porcelain, two glass-ceramics and a glass-infiltrated-alumina composite). Disks (Ø12 mm x 1.1mm-thick) and bars (3 mm x 4 mm x 20 mm) of each material were processed according to manufacturer instructions, machined and polished. Fracture toughness (K(Ic)) was determined by the indentation strength method using 3-point bending and biaxial flexure fixtures for the fracture of bars and disks, respectively. Microstructural and fractographic analyses were performed with scanning electron microscopy, energy dispersive spectroscopy and X-ray diffraction. The isotropic microstructure of the porcelain and the leucite-based glass-ceramic resulted in similar fracture toughness values regardless of the specimen geometry. On the other hand, materials containing second-phase particles with high aspect ratio (lithium disilicate glass-ceramic and glass-infiltrated-alumina composite) showed lower fracture toughness for disk specimens compared to bars. For the lithium disilicate glass-ceramic disks, it was demonstrated that the occurrence of particle alignment during the heat-pressing procedure resulted in an unfavorable pattern that created weak microstructural paths during the biaxial test. For the glass-infiltrated-alumina composite, the microstructural analysis showed that the large alumina platelets tended to align their large surfaces perpendicularly to the direction of particle deposition during slip casting of green preforms. The fracture toughness of dental ceramics with anisotropic microstructure should be determined by means of biaxial testing, since it results in lower values.

Fluoride release, recharge and mechanical property stability of various fluoride-containing resin composites.

PubMed

Naoum, S; Ellakwa, A; Martin, F; Swain, M

2011-01-01

To determine the fluoride release and recharge of three fluoride-containing resin composites when aged in deionized water (pH 6.5) and lactic acid (pH 4.0) and to assess mechanical properties of these composites following aging. Three fluoride-containing resin composites were analyzed in this study; a new giomer material named Beautifil II, Gradia Direct X, and Tetric EvoCeram. A glass ionomer cement, Fuji IX Extra, was also analyzed for comparison. Specimens were fabricated for two test groups: group 1 included 10 disc specimens initially aged 43 days in deionized water (five specimens) and lactic acid (five specimens). The fluoride release from these specimens was measured using a fluoride-specific electrode on nine specific test days during the aging period. Following 49 days of aging, each specimen was recharged in 5000 ppm neutral sodium fluoride solution for 5 minutes. Specimen recharge was then repeated on a weekly basis for 3 weeks. The subsequent fluoride rerelease was measured at 1, 3, and 7 days after each recharge episode. Group 2 included six disc specimens aged for 3 months in deionized water (three specimens) and lactic acid (three specimens). The hardness and elastic modulus of each specimen was measured using nano-indentation at intervals of 24 hours, 1 month, and 3 months after fabrication. Two-way factorial analysis of variance (ANOVA) and post-hoc (Tukey) testing was used to assess the influence of storage media (two levels) and composite type (three levels) on the fluoride release, fluoride rerelease, hardness, and elastic modulus of the assessed materials. The level of significance was set at p=0.05. All three composites demonstrated fluoride release and recharge when aged in both deionized water and lactic acid. The cumulative fluoride released from Beautifil II into both media was substantially greater than the fluoride released from Gradia Direct X and Tetric EvoCeram after 43 days aging and was significantly (p<0.05, ANOVA, Tukey test) greater during several analysis periods. Beautifil II demonstrated the greatest recharge ability of the three composites over the 3-week recharge period in both media. Fuji IX Extra demonstrated a significantly (p<0.05) greater fluoride release and recharge compared with the three resin composites. The elastic modulus and hardness of the three composites did not decrease significantly (p<0.05) with fluoride release or fluid uptake over the 3-month aging period, in either media. The three composites in the present study demonstrated fluoride release (Beautiful II > Gradia Direct X > Tetric EvoCeram) and fluoride recharge (Beautiful II > Gradia Direct X > Tetric EvoCeram). This capability raises the possibility of fluoride-containing composites exhibiting a lower incidence of recurrent caries than non fluoride–containing composites. The mechanical properties of each composite did not diminish with aging and fluoride release over the testing period.

Strength evaluation test of pressureless-sintered silicon nitride at room temperature

NASA Technical Reports Server (NTRS)

Matsusue, K.; Takahara, K.; Hashimoto, R.

1984-01-01

In order to study strength characteristics at room temperature and the strength evaluating method of ceramic materials, the following tests were conducted on pressureless sintered silicon nitride specimens: bending tests, the three tensile tests of rectangular plates, holed plates, and notched plates, and spin tests of centrally holed disks. The relationship between the mean strength of specimens and the effective volume of specimens are examined using Weibull's theory. The effect of surface grinding on the strength of specimens is discussed.

Analysis of Adhesively Bonded Ceramics Using an Asymmetric Wedge Test

DTIC Science & Technology

2008-12-01

4 Figure 2. Average crack ...flexure specimen. The flaw, indicated by the white arrow, is a subsurface semi-elliptical crack induced by surface machining damage...strength-limiting orthogonal surface machining crack in an alumina flexure specimen coated with a single layer of film adhesive. The white arrow

Motorized manipulator for positioning a TEM specimen

DOEpatents

Schmid, Andreas Karl; Andresen, Nord

2010-12-14

The invention relates to a motorized manipulator for positioning a TEM specimen holder with sub-micron resolution parallel to a y-z plane and rotating the specimen holder in the y-z plane, the manipulator comprising a base (2), and attachment means (30) for attaching the specimen holder to the manipulator, characterized in that the manipulator further comprises at least three nano-actuators (3.sup.a, 3.sup.b, 3.sup.c) mounted on the base, each nano-actuator showing a tip (4.sup.a, 4.sup.b, 4.sup.c), the at least three tips defining the y-z plane, each tip capable of moving with respect to the base in the y-z plane; a platform (5) in contact with the tips of the nano-actuators; and clamping means (6) for pressing the platform against the tips of the nano-actuators; as a result of which the nano-actuators can rotate the platform with respect to the base in the y-z plane and translate the platform parallel to the y-z plane.

Processing and characterization of phase boundaries in ceramic and metallic materials

NASA Astrophysics Data System (ADS)

Zeng, Liang

The goal of this dissertation work was to explore and describe advanced characterization of novel materials processing. These characterizations were carried out using scanning and transmission electron microscopy (SEM and TEM), and X-ray diffraction techniques. The materials studied included ceramics and metallic materials. The first part of this dissertation focuses on the processing, and the resulting interfacial microstructure of ceramics joined using spin-on interlayers. SEM, TEM, and indentation tests were used to investigate the interfacial microstructural and mechanical property evolution of polycrystalline zirconia bonded to glass ceramic MaCor(TM), and polycrystalline alumina to single crystal alumina. Interlayer assisted specimens were joined using a thin amorphous silica interlayer. This interlayer was produced by spin coating an organic based silica bond material precursor and curing at 200°C, followed by joining in a microwave cavity or conventional electric furnace. Experimental results indicate that in the joining of the zirconia and MaCor(TM) no significant interfacial microstructural and mechanical property differences developed between materials joined either with or without interlayers, due to the glassy nature of MaCor(TM). The bond interface was non-planar, as a result of the strong wetting of MaCor(TM) and silica and dissolution of the zirconia. However, without the aid of a silica interlayer, sapphire and 98% polycrystalline alumina failed to join under the experimental conditions under this study. A variety of interfacial morphologies have been observed, including amorphous regions, fine crystalline alumina, and intimate contact between the sapphire and polycrystalline alumina. In addition, the evolution of the joining process from the initial sputter-cure to the final joining state and joining mechanisms were characterized. The second part of this dissertation focused on the effects of working and heat treatment on microstructure, texture, phase boundary movement, and mechanical property evolution in Ti-6Al-4V wire. The as-received wire consisted of equilibrium a and metastable beta phases and had a moderately strong fiber texture with prism plane normals aligned with the wire axis. The wire was worked by extrusion, solution heat-treatment and water quenching, and aging. The extrusion process strengthened the as-received texture. After solutionization and quenching, microstrucual observations showed the presence of many needlelike martensitic platelets in the prior beta phase regions. Texture analysis revealed that a secondary fiber with basal plane normals aligned with the wire axis emerged at the expense of the initial texture, indicating that highly preferred phase boundary motion (variant selection) occurred during the beta → alpha transformation. The strength of the variant selection consistently increased with solutionization temperature and time. In addition, the effects of dislocation type and density on variant selections were further investigated. This implies that strategic prior deformation and heat treatment can be exploited to design the resulting texture and microstructure and consequently optimize the properties of titanium products.

Effects of aeroconvective environments on 2D reinforced ceramic matrix composites

NASA Technical Reports Server (NTRS)

Riccitiello, Salvatore R.; Love, Wendell L.; Balter-Peterson, Aliza; Hood, Thomas; Chang, William

1991-01-01

The effect of aeroconvective heating environment similar to that observed a spacecraft ascent or reentry from orbit, on the performance of a commercial carbon-reinforced ceramic matrix material specimens of two configurations (orthotropic and quasi-isotropic), fabricated by the Societe Europenne Propulsion (SEP) process was investigated using the NASA Ames Research Center 20 Megawatt Panel Test facility. The performance of the commercial material was compared with the SEP prepared materials. It was found that, whereas the quasi-isotropic SEP specimens exhibited a much higher mass loss rate and a significant dimensional change upon exposure to the thermal environment than did the orthotropic ones, the commercial SEP-like materials did not exhibit these characteristics. There was no greater mass loss rate for the quasi-isotropic specimens, and no dimension changes were observed. The Nicalon reinforced materials in both configurations, as fabricated by SEP or by the commercial source, showed no mass changes and no dimensional changes.

Tensile Bond Strength of So-called Universal Primers and Universal Multimode Adhesives to Zirconia and Lithium Disilicate Ceramics.

PubMed

Elsayed, Adham; Younes, Feras; Lehmann, Frank; Kern, Matthias

2017-01-01

To test the bond strength and durability after artificial aging of so-called universal primers and universal multimode adhesives to lithium disilicate or zirconia ceramics. A total of 240 ceramic plates, divided into two groups, were produced and conditioned: 120 acid-etched lithium disilicate plates (IPS e.max CAD) and 120 air-abraded zirconia plates (Zenostar T). Each group was divided into five subgroups (n = 24), and a universal restorative primer or multimode universal adhesive was used for each subgroup to bond plexiglas tubes filled with a composite resin to the ceramic plate. The specimens were stored in water at 37°C for 3 days without thermal cycling, or for 30 or 150 days with 7500 or 37,500 thermal cycles between 5°C and 55°C, respectively. All specimens then underwent tensile bond strength testing. Initially, all bonding systems exhibited high TBS, but some showed a significant reduction after 30 and 150 days of storage. After 3, 30, and 150 days, Monobond Plus, which contains silane and phosphate monomer, showed significantly higher bond strengths than the other universal primer and adhesive systems. The bond strength to lithium disilicate and zirconia ceramic is significantly affected by the bonding system used. Using a separate primer containg silane and phosphate monomer provides more durable bonding than do silanes incorporated in universal multimode adhesives. Only one of five so-called universal primers and adhesives provided durable bonding to lithium disilicate and zirconia ceramic.

Influence of the supporting die structures on the fracture strength of all-ceramic materials.

PubMed

Yucel, Munir Tolga; Yondem, Isa; Aykent, Filiz; Eraslan, Oğuz

2012-08-01

This study investigated the influence of the elastic modulus of supporting dies on the fracture strengths of all-ceramic materials used in dental crowns. Four different types of supporting die materials (dentin, epoxy resin, brass, and stainless steel) (24 per group) were prepared using a milling machine to simulate a mandibular molar all-ceramic core preparation. A total number of 96 zirconia cores were fabricated using a CAD/CAM system. The specimens were divided into two groups. In the first group, cores were cemented to substructures using a dual-cure resin cement. In the second group, cores were not cemented to the supporting dies. The specimens were loaded using a universal testing machine at a crosshead speed of 0.5 mm/min until fracture occurred. Data were statistically analyzed using two-way analysis of variance and Tukey HSD tests (α = 0.05). The geometric models of cores and supporting die materials were developed using finite element method to obtain the stress distribution of the forces. Cemented groups showed statistically higher fracture strength values than non-cemented groups. While ceramic cores on stainless steel dies showed the highest fracture strength values, ceramic cores on dentin dies showed the lowest fracture strength values among the groups. The elastic modulus of the supporting die structure is a significant factor in determining the fracture resistance of all-ceramic crowns. Using supporting die structures that have a low elastic modulus may be suitable for fracture strength tests, in order to accurately reflect clinical conditions.

Microstructural characterization of Ti-6Al-4V metal chips by focused ion beam (FIB) and transmission electron microscopy (TEM)

DOE Office of Scientific and Technical Information (OSTI.GOV)

Schneider, Judy; Dong, Lei; Howe, Jane Y

2011-01-01

The microstructure of the secondary deformation zone (SDZ) near the cutting surface in metal chips of Ti-6Al-4V formed during machining was investigated using focused ion beam (FIB) specimen preparation and transmission electron microscopy (TEM) imaging. Use of the FIB allowed precise extraction of the specimen across this region to reveal its inhomogeneous microstructure resulting from the non-uniform distribution of strain, strain rate, and temperature generated during the cutting process. Initial imaging from conventional TEM foil preparation revealed microstructures ranging from heavily textured to regions of fine grains. Using FIB preparation, the transverse microstructure could be interpreted as fine grains nearmore » the cutting surface which transitioned to coarse grains toward the free surface. At the cutting surface a 10 nm thick recrystallized layer was observed capping a 20 nm thick amorphous layer.« less

Chapter 14: Electron Microscopy on Thin Films for Solar Cells

DOE Office of Scientific and Technical Information (OSTI.GOV)

Romero, Manuel; Abou-Ras, Daniel; Nichterwitz, Melanie

2016-07-22

This chapter overviews the various techniques applied in scanning electron microscopy (SEM) and transmission electron microscopy (TEM), and highlights their possibilities and also limitations. It gives the various imaging and analysis techniques applied on a scanning electron microscope. The chapter shows that imaging is divided into that making use of secondary electrons (SEs) and of backscattered electrons (BSEs), resulting in different contrasts in the images and thus providing information on compositions, microstructures, and surface potentials. Whenever aiming for imaging and analyses at scales of down to the angstroms range, TEM and its related techniques are appropriate tools. In many cases,more » also SEM techniques provide the access to various material properties of the individual layers, not requiring specimen preparation as time consuming as TEM techniques. Finally, the chapter dedicates to cross-sectional specimen preparation for electron microscopy. The preparation decides indeed on the quality of imaging and analyses.« less

Nd:YAG Laser-aided ceramic brackets debonding: Effects on shear bond strength and enamel surface

NASA Astrophysics Data System (ADS)

Han, Xianglong; Liu, Xiaolin; Bai, Ding; Meng, Yao; Huang, Lan

2008-11-01

In order to evaluate the efficiency of Nd:YAG laser-aided ceramic brackets debonding technique, both ceramic brackets and metallic brackets were bonded with orthodontic adhesive to 30 freshly extracted premolars. The specimens were divided into three groups, 10 in each, according to the brackets employed and the debonding techniques used: (1) metallic brackets with shear debonding force, (2) ceramic brackets with shear debonding force, and (3) ceramic brackets with Nd:YAG laser irradiation. The result showed that laser irradiation could diminish shear bond strength (SBS) significantly and produce the most desired ARI scores. Moreover, scanning electron microscopy investigation displayed that laser-aided technique induced little enamel scratch or loss. It was concluded that Nd:YAG laser could facilitate the debonding of ceramic brackets and diminish the amount of remnant adhesive without damaging enamel structure.

Diffraction contrast as a sensitive indicator of femtosecond sub-nanoscale motion in ultrafast transmission electron microscopy

NASA Astrophysics Data System (ADS)

Cremons, Daniel R.; Schliep, Karl B.; Flannigan, David J.

2013-09-01

With ultrafast transmission electron microscopy (UTEM), access can be gained to the spatiotemporal scales required to directly visualize rapid, non-equilibrium structural dynamics of materials. This is achieved by operating a transmission electron microscope (TEM) in a stroboscopic pump-probe fashion by photoelectrically generating coherent, well-timed electron packets in the gun region of the TEM. These probe photoelectrons are accelerated down the TEM column where they travel through the specimen before reaching a standard, commercially-available CCD detector. A second laser pulse is used to excite (pump) the specimen in situ. Structural changes are visualized by varying the arrival time of the pump laser pulse relative to the probe electron packet at the specimen. Here, we discuss how ultrafast nanoscale motions of crystalline materials can be visualized and precisely quantified using diffraction contrast in UTEM. Because diffraction contrast sensitively depends upon both crystal lattice orientation as well as incoming electron wavevector, minor spatial/directional variations in either will produce dynamic and often complex patterns in real-space images. This is because sections of the crystalline material that satisfy the Laue conditions may be heterogeneously distributed such that electron scattering vectors vary over nanoscale regions. Thus, minor changes in either crystal grain orientation, as occurs during specimen tilting, warping, or anisotropic expansion, or in the electron wavevector result in dramatic changes in the observed diffraction contrast. In this way, dynamic contrast patterns observed in UTEM images can be used as sensitive indicators of ultrafast specimen motion. Further, these motions can be spatiotemporally mapped such that direction and amplitude can be determined.

Preparation of viral samples within biocontainment for ultrastructural analysis: Utilization of an innovative processing capsule for negative staining.

PubMed

Monninger, Mitchell K; Nguessan, Chrystal A; Blancett, Candace D; Kuehl, Kathleen A; Rossi, Cynthia A; Olschner, Scott P; Williams, Priscilla L; Goodman, Steven L; Sun, Mei G

2016-12-01

Transmission electron microscopy can be used to observe the ultrastructure of viruses and other microbial pathogens with nanometer resolution. In a transmission electron microscope (TEM), the image is created by passing an electron beam through a specimen with contrast generated by electron scattering from dense elements in the specimen. Viruses do not normally contain dense elements, so a negative stain that places dense heavy metal salts around the sample is added to create a dark border. To prepare a virus sample for a negative stain transmission electron microscopy, a virus suspension is applied to a TEM grid specimen support, which is a 3mm diameter fragile specimen screen coated with a few nanometers of plastic film. Then, deionized (dI) water rinses and a negative stain solution are applied to the grid. All infectious viruses must be handled in a biosafety cabinet (BSC) and many require a biocontainment laboratory environment. Staining viruses in biosafety levels (BSL) 3 and 4 is especially challenging because the support grids are small, fragile, and easily moved by air currents. In this study we evaluated a new device for negative staining viruses called mPrep/g capsule. It is a capsule that holds up to two TEM grids during all processing steps and for storage after staining is complete. This study reports that the mPrep/g capsule method is valid and effective to negative stain virus specimens, especially in high containment laboratory environments. Copyright © 2016 The Authors. Published by Elsevier B.V. All rights reserved.

Influence of the antagonist material on the wear of different composites using two different wear simulation methods.

PubMed

Heintze, S D; Zellweger, G; Cavalleri, A; Ferracane, J

2006-02-01

The aim of the study was to evaluate two ceramic materials as possible substitutes for enamel using two wear simulation methods, and to compare both methods with regard to the wear results for different materials. Flat specimens (OHSU n=6, Ivoclar n=8) of one compomer and three composite materials (Dyract AP, Tetric Ceram, Z250, experimental composite) were fabricated and subjected to wear using two different wear testing methods and two pressable ceramic materials as stylus (Empress, experimental ceramic). For the OHSU method, enamel styli of the same dimensions as the ceramic stylus were fabricated additionally. Both wear testing methods differ with regard to loading force, lateral movement of stylus, stylus dimension, number of cycles, thermocycling and abrasive medium. In the OHSU method, the wear facets (mean vertical loss) were measured using a contact profilometer, while in the Ivoclar method (maximal vertical loss) a laser scanner was used for this purpose. Additionally, the vertical loss of the ceramic stylus was quantified for the Ivoclar method. The results obtained from each method were compared by ANOVA and Tukey's test (p<0.05). To compare both wear methods, the log-transformed data were used to establish relative ranks between material/stylus combinations and assessed by applying the Pearson correlation coefficient. The experimental ceramic material generated significantly less wear in Tetric Ceram and Z250 specimens compared to the Empress stylus in the Ivoclar method, whereas with the OHSU method, no difference between the two ceramic antagonists was found with regard to abrasion or attrition. The wear generated by the enamel stylus was not statistically different from that generated by the other two ceramic materials in the OHSU method. With the Ivoclar method, wear of the ceramic stylus was only statistically different when in contact with Tetric Ceram. There was a close correlation between the attrition wear of the OHSU and the wear of the Ivoclar method (Pearson coefficient 0.83, p=0.01). Pressable ceramic materials can be used as a substitute for enamel in wear testing machines. However, material ranking may be affected by the type of ceramic material chosen. The attrition wear of the OHSU method was comparable with the wear generated with the Ivoclar method.

Comparison of structure, morphology, and leach characteristics of multi-phase ceramics produced via melt processing and hot isostatic pressing

NASA Astrophysics Data System (ADS)

Dandeneau, Christopher S.; Hong, Tao; Brinkman, Kyle S.; Vance, Eric R.; Amoroso, Jake W.

2018-04-01

Melt processing of multi-phase ceramic waste forms offers potential advantages over traditional solid-state synthesis methods given both the prevalence of melters currently in use and the ability to reduce the possibility of airborne radionuclide contamination. In this work, multi-phase ceramics with a targeted hollandite composition of Ba1.0Cs0.3Cr1.0Al0.3Fe1.0Ti5.7O16 were fabricated by melt processing at 1675 °C and hot isostatic pressing (HIP) at 1250 and 1300 °C. X-ray diffraction analysis (XRD) confirmed hollandite as the major phase in all specimens. Zirconolite/pyrochlore peaks and weaker perovskite reflections were observed after melt processing, while HIP samples displayed prominent perovskite peaks and low-intensity zirconolite reflections. Melt processing produced specimens with large (>50 μm) well-defined hollandite grains, while HIP yielded samples with a more fine-grained morphology. Elemental analysis showed "islands" rich in Cs and Ti across the surface of the 1300 °C HIP sample, suggesting partial melting and partitioning of Cs into multiple phases. Photoemission data revealed multiple Cs 3d spin-orbit pairs for the HIP samples, with the lower binding energy doublets likely corresponding to Cs located in more leachable phases. Among all specimens examined, the melt-processed sample exhibited the lowest fractional release rates for Rb and Cs. However, the retention of Sr and Mo was greater in the HIP specimens.

Attritional wear and abrasive surface alterations of composite resin materials in vitro.

PubMed

Göhring, T N; Besek, M J; Schmidlin, P R

2002-01-01

A laboratory study was performed with 232 specimens and 72 human enamel, 24 gold, 24 ceramic and 12 composite antagonists in 22 groups to test attritional and abrasive wear behavior of composite materials compared to wear behavior of human enamel. Belleglass HP, Concept Inlay/Onlay, Targis and Targis Upgrade 99 composite resin for lab-made restorations was tested as well as Tetric Ceram and FHC Merz light as resins for direct restorations. Natural human enamel specimens served as control. All specimens were subjected to long-term thermo-mechanical loading in a computer-controlled masticator, chemical degradation and toothbrush/toothpaste abrasion. Wear of specimen in occlusal contact area (OCA), contact-free occlusal area and wear of natural enamel cusps as well as antagonists made of gold, ceramic and composite in identical form was measured after 120,000, 240,000, 640,000 and 1200,000 load cycles. A qualitative SEM analysis was performed to support quantitative data. Belleglass HP and Targis Upgrade 99 restorative materials showed wear resistance comparable to human enamel when loaded with enamel cusps. Wear of Targis versus composite and gold antagonists was significantly higher (p<0.0001). Analysis of surface alterations showed hygroscopic expansion in all composite resins during the test. As a consequence of this study, necessity to further improve physical properties of composites for long lasting restorations was obvious. Beside of attritional wear in OCA, attention must be given to stable filler-matrix interfaces and prevention of water sorption.

Structural characterizaiton and gas reactions of small metal particles by high-resolution, in-situ TEM and TED

NASA Technical Reports Server (NTRS)

1984-01-01

The existing in-situ transmission electron microscopy (TEM) facility was improved by adding a separately pumped mini-specimen chamber. The chamber contains wire-evaporation sources for three metals and a specimen heater for moderate substrate temperatures. A sample introduction device was constructed, installed, and tested, facilitating rapid introduction of a specimen into the mini-chamber while maintaining the background pressure in that chamber in the 10(-9) millibar range. Small particles and clusters of Pd, grown by deposition from the vapor phase in an in-situ TEM facility on amorphous and crystalline support films of alumina and on ultra-thin carbon films, were analyzed by conventional high-resolution TEM and image analysis in terms of detectability, number density, and size distribution. The smallest particles that could be detected and counted contained no more than 6 atoms; size determinations could be made for particles 1 nm in diameter. The influence of various oxygen plasma treatments, annealing treatments, and of increasing the substrate temperature during deposition was investigated. The TEM technique was employed to demonstrate that under otherwise identica l conditions the lattice parameter of Pd particles in the 1 to 2 nm size range and supported in random orientation on ex-situ prepared mica films is expanded by some 3% when compared to 5 nm size particles. It is believed that this expansion is neither a small-particle diffraction effect nor due to pseudomorphism, but that it is due to a annealing-induced transformation of the small as-deposited particles with predominantly composite crystal structures into larger particles with true f.c.c. structure and thus inherently smaller lattice parameter.

In vitro evaluation of microleakage of various types of dental cements.

PubMed

Medić, Vesna; Obradović-Djuricić, Kosovka; Dodić, Slobodan; Petrović, Renata

2010-01-01

Microleakage is defined as the clinically undetectable seepage of oral fluids containing bacteria and debris between cement layer and tooth restoration. This in vitro study investigated the effect of different dental cements (zinc-phosphate, polycarboxylate, glass-ionomer and resin cement) on microleakage in different ceramic crown systems (metal ceramic crown, metal ceramic crown with a porcelain margin, Empress 2 and in Ceram all-ceramic crowns) fixed on extracted human teeth. One hundred and sixty intact human premolars were randomized to four groups of forty teeth each, according to the different ceramic crown systems. They were prepared in a standardized manner for metal-ceramic and all-ceramic crowns. Crowns were made following a standard laboratory technique, and each group of crowns were divided into four groups according to the different cement agents and cemented on their respective abutments. The specimens were subjected to thermocycling, placed in methylene blue solutions, embedded in resin blocks and vertically cut in the bucco-oral and meso-distal direction. The microleakage in the area of tooth-cement interface was defined as linear penetration of methylene blue and was determined with a microscope to assign microleakage scores using a five-point scale. A significant association was found between a cement type and degree of microleakage (p = 0.001). No statistically significant differences were found among the different ceramic crown systems luted with the same dental cement. The smallest degree of microleakage was observed in specimens luted with resin cement (X = 1.73), followed by glass-ionomer cement (X=2.45) and polycarboxylate cement (X = 3.20). The greatest degree of microleakage was detected in the crowns fixed with zincphosphate cement (X = 3.33). The investigated dental cements revealed different sealing abilities. The use of resin cement resulted in the percentage of 0 microleakage scores. Due to this feature, the resin cement is to be recommended in everyday clinical practice.

Influence of various bonding techniques on the fracture strength of thin CAD/CAM-fabricated occlusal glass-ceramic veneers.

PubMed

Yazigi, Christine; Kern, Matthias; Chaar, Mohamed Sad

2017-11-01

To evaluate the efficiency of immediate dentin sealing and the effects of different bonding protocols on the fracture strength of CAD/CAM occlusal veneers bonded to exposed dentin. Ninety-six extracted maxillary premolars were initially divided into three main groups with 32 specimens each: without immediate dentin sealing, immediate dentin sealing/total etching and immediate dentin sealing/selective etching. Teeth were identically prepared in the dentin to receive occlusal veneers of 0.8mm thickness, milled from lithium disilicate ceramic blocks (IPS e.max CAD). Each main group was later subdivided, according to the pre-cementation surface etching protocol (total/selective), into two subgroups with 16 specimens each. All restorations were adhesively bonded using a resin cement (Variolink Esthetic). Half of the specimens of each subgroup were subjected to thermo-dynamic loading in a chewing simulator with 1,200,000 cycles at 10kg load. The other half and the surviving specimens were subjected to quasi-static loading until failure. Statistical analysis was performed using three-way ANOVA and Tukey's post-hoc tests. All specimens except one survived the artificial aging. A significantly higher fracture strength of restorations (p ≤ 0.001) was obtained when immediate dentin sealing was followed regardless of the etching method with values ranging from a minimum of 1122 ± 336N to a maximum of 1853 ± 333N. Neither the pre-cementation treatment nor the artificial aging had a statistical significant effect on the fracture strength. Immediate dentin sealing protocol is recommended whenever dentin is exposed during the preparation for thin glass-ceramic occlusal veneers. Copyright © 2017 Elsevier Ltd. All rights reserved.

Shear bond strength of a denture base acrylic resin and gingiva-colored indirect composite material to zirconia ceramics.

PubMed

Kubochi, Kei; Komine, Futoshi; Fushiki, Ryosuke; Yagawa, Shogo; Mori, Serina; Matsumura, Hideo

2017-04-01

To evaluate the shear bond strengths of two gingiva-colored materials (an indirect composite material and a denture base acrylic resin) to zirconia ceramics and determine the effects of surface treatment with various priming agents. A gingiva-colored indirect composite material (CER) or denture base acrylic resin (PAL) was bonded to zirconia disks with unpriming (UP) or one of seven priming agents (n=11 each), namely, Alloy Primer (ALP), Clearfil Photo Bond (CPB), Clearfil Photo Bond with Clearfil Porcelain Bond Activator (CPB+Act), Metal Link (MEL), Meta Fast Bonding Liner (MFB), MR. bond (MRB), and V-Primer (VPR). Shear bond strength was determined before and after 5000 thermocycles. The data were analyzed with the Kruskal-Wallis test and Steel-Dwass test. The mean pre-/post-thermalcycling bond strengths were 1.0-14.1MPa/0.1-12.1MPa for the CER specimen and 0.9-30.2MPa/0.1-11.1MPa for the PAL specimen. For the CER specimen, the ALP, CPB, and CPB+Act groups had significantly higher bond strengths among the eight groups, at both 0 and 5000 thermocycles. For the PAL specimen, shear bond strength was significantly lower after thermalcycling in all groups tested. After 5000 thermocycles, bond strengths were significantly higher in the CPB and CPB+Act groups than in the other groups. For the PAL specimens, bond strengths were significantly lower after thermalcycling in all groups tested. The MDP functional monomer improved bonding of a gingiva-colored indirect composite material and denture base acrylic resin to zirconia ceramics. Copyright © 2016 Japan Prosthodontic Society. Published by Elsevier Ltd. All rights reserved.

To Evaluate Effect of Airborne Particle Abrasion using Different Abrasives Particles and Compare Two Commercial Available Zirconia on Flexural Strength on Heat Treatment.

PubMed

Prasad, Hari A; Pasha, Naveed; Hilal, Mohammed; Amarnath, G S; Kundapur, Vinaya; Anand, M; Singh, Sumeet

2017-06-01

The popularity of ceramic restorations can be attributed to its life-like appearance, durability and biocompatibility and therefore ceramic restorations have been widely used for anterior and posterior teeth. Ceramic restorations have esthetic and biocompatible advantages but low fracture resistance. Since it has high flexural strength and fracture resistance, yttria-stabilized tetragonal zirconia polycrystal (Y-TZP) is the dental material most commonly used for the core of ceramic crowns and fixed dental prosthesis. In spite of improved mechanical properties, acceptable marginal adaptation and biocompatibility the whitish opacity of zirconia is an obvious esthetic disadvantage. The zirconia framework is often veneered with conventional feldspathic porcelain to achieve a natural appearance. However it is difficult to achieve sufficient bond strength between zirconia and the veneering material. Achieving sufficient bond strength between the veneering ceramic and the zirconia core is a major challenge in the long term clinical success of veneered zirconia restorations. The main objective of this study is to evaluate the effect of different surface treatments on the fracture strength of the two commercially available Zirconia namely Ceramill and ZR-White (AMANNGIRRBACH and UPCERA) respectively. Two commercially available pre-sinteredyttrium stabilized Zirconia blanks (ZR-White and Ceramill) from AMANNGIRRBACH and UPCERA respectively are used to produce the disc shaped specimens of size (15.2 ± 0.03 mm in diameter and 1.2 ± 0.03 mm thick) from each Zirconia blank. All disc shaped specimens are heated at 1200°C in a furnace for 2 hours to form homogenous tetragonal ZrO 2 . The dimensions of the specimens are measured with a digital caliper (aerospace). The thickness and diameter of each specimen are calculated as the means of 3 measurements made at random sites. 80 discs from each Zirconia blank are divided into ten groups of 8 specimens each. Heat treatment after airborne-particle abrasion using 50 µm Al 2 O 3 particles and 50 µm silica coated Al 2 O 3 are applied to the upper and lower surfaces of the specimens. Each specimen is held under a pressure of 30 psi for 15 seconds at a direction perpendicular to the surface and at a distance of 30mm with an airborne particle abrasion device for the specimens in the airborne particle abraded groups. Heat treatments were performed at a starting temperature of 500°C, heating rate of 100°c/ min, ending at a temperature of 1000°C and 15 minutes holding time without vacuum for the specimens in the group 4, 5, 9 and 10. Airborne-particle abrasion mimicking the preparation for cementation was applied to the lower surfaces with 50 µm alumina and silica coated alumina particles for the specimens in the groups 6, 7, 8, 9 and 10. The specimens were cleaned for 15 minutes in an ultrasonic bath containing distilled water. To determine the fracture strength, a disc of 10 mm diameter was used to place 3 hardened steel balls of 3 mm diameter separated each other by 120 degrees (described in the ISO standard 6872 for dental ceramics). Each specimen was centrally placed on this disc. The lower surface mimicking the internal surface of zirconia was the tension side, facing the supporting device testing, while the upper surface mimicking the external surface of the zirconia core was loaded with a flat punch (1 mm in diameter). A universal testing machine was used to perform the test at a cross head speed of 1mm/min. The failure stress was calculated with the equation listed in ISO 6872. The results were then statistically analyzed. A post hoc test was used for pair wise comparisons. The mean fracture strength of commercially available Zirconia Ceramill (AMANNGIRBACH) showed a significant higher value compared to the ZR-White (UPCERA) Zirconia ( P <0.001), Airborne abrasion treatment to the specimens showed a significant difference between the abraded groups and the control group ( P <0.001); further AMANNGIRRBACH specimens gave a higher value compare to the UPCERA specimens. The study also revealed that the heat treatment of the specimens gave significant value ( P <0.001) compared to the control group, but heat treatment following the air abrasion reduces the fracture strength of the sample than the air abraded group. Within the limitation of this study, it is concluded that, the in vitro fracture strength of Zirconia specimens treated with an airborne abrasion both on the veneering surface (50 µm silica coated Al2O3) and the cementing surface (50 µm Al 2 O 3 ) was significantly higher than the heat treated and the control group. Airborne particle abrasion followed by the heat treatment reduces the fracture strength of the specimen than that ofthe group treated only by the air abrasives. The fracture strength of a commercially available Ceramill (AMANNGIRRBACH) is greater than that of a Zirconia from ZR-White (UPCERA) variety.

To Evaluate Effect of Airborne Particle Abrasion using Different Abrasives Particles and Compare Two Commercial Available Zirconia on Flexural Strength on Heat Treatment

PubMed Central

Prasad, Hari A.; Pasha, Naveed; Hilal, Mohammed; Amarnath, G. S.; Kundapur, Vinaya; Anand, M; Singh, Sumeet

2017-01-01

Background and objective: The popularity of ceramic restorations can be attributed to its life-like appearance, durability and biocompatibility and therefore ceramic restorations have been widely used for anterior and posterior teeth. Ceramic restorations have esthetic and biocompatible advantages but low fracture resistance. Since it has high flexural strength and fracture resistance, yttria-stabilized tetragonal zirconia polycrystal (Y-TZP) is the dental material most commonly used for the core of ceramic crowns and fixed dental prosthesis. In spite of improved mechanical properties, acceptable marginal adaptation and biocompatibility the whitish opacity of zirconia is an obvious esthetic disadvantage. The zirconia framework is often veneered with conventional feldspathic porcelain to achieve a natural appearance. However it is difficult to achieve sufficient bond strength between zirconia and the veneering material. Achieving sufficient bond strength between the veneering ceramic and the zirconia core is a major challenge in the long term clinical success of veneered zirconia restorations. The main objective of this study is to evaluate the effect of different surface treatments on the fracture strength of the two commercially available Zirconia namely Ceramill and ZR-White (AMANNGIRRBACH and UPCERA) respectively. Method: Two commercially available pre-sinteredyttrium stabilized Zirconia blanks (ZR-White and Ceramill) from AMANNGIRRBACH and UPCERA respectively are used to produce the disc shaped specimens of size (15.2 ± 0.03 mm in diameter and 1.2 ± 0.03 mm thick) from each Zirconia blank. All disc shaped specimens are heated at 1200°C in a furnace for 2 hours to form homogenous tetragonal ZrO2. The dimensions of the specimens are measured with a digital caliper (aerospace). The thickness and diameter of each specimen are calculated as the means of 3 measurements made at random sites. 80 discs from each Zirconia blank are divided into ten groups of 8 specimens each. Heat treatment after airborne-particle abrasion using 50 µm Al2O3 particles and 50 µm silica coated Al2O3 are applied to the upper and lower surfaces of the specimens. Each specimen is held under a pressure of 30 psi for 15 seconds at a direction perpendicular to the surface and at a distance of 30mm with an airborne particle abrasion device for the specimens in the airborne particle abraded groups. Heat treatments were performed at a starting temperature of 500°C, heating rate of 100°c/ min, ending at a temperature of 1000°C and 15 minutes holding time without vacuum for the specimens in the group 4, 5, 9 and 10. Airborne-particle abrasion mimicking the preparation for cementation was applied to the lower surfaces with 50 µm alumina and silica coated alumina particles for the specimens in the groups 6, 7, 8, 9 and 10. The specimens were cleaned for 15 minutes in an ultrasonic bath containing distilled water. To determine the fracture strength, a disc of 10 mm diameter was used to place 3 hardened steel balls of 3 mm diameter separated each other by 120 degrees (described in the ISO standard 6872 for dental ceramics). Each specimen was centrally placed on this disc. The lower surface mimicking the internal surface of zirconia was the tension side, facing the supporting device testing, while the upper surface mimicking the external surface of the zirconia core was loaded with a flat punch (1 mm in diameter). A universal testing machine was used to perform the test at a cross head speed of 1mm/min. The failure stress was calculated with the equation listed in ISO 6872. The results were then statistically analyzed. A post hoc test was used for pair wise comparisons. Result: The mean fracture strength of commercially available Zirconia Ceramill (AMANNGIRBACH) showed a significant higher value compared to the ZR-White (UPCERA) Zirconia (P<0.001), Airborne abrasion treatment to the specimens showed a significant difference between the abraded groups and the control group (P<0.001); further AMANNGIRRBACH specimens gave a higher value compare to the UPCERA specimens. The study also revealed that the heat treatment of the specimens gave significant value (P<0.001) compared to the control group, but heat treatment following the air abrasion reduces the fracture strength of the sample than the air abraded group. Conclusion: Within the limitation of this study, it is concluded that, the in vitro fracture strength of Zirconia specimens treated with an airborne abrasion both on the veneering surface (50 µm silica coated Al2O3) and the cementing surface (50 µm Al2O3) was significantly higher than the heat treated and the control group. Airborne particle abrasion followed by the heat treatment reduces the fracture strength of the specimen than that ofthe group treated only by the air abrasives. The fracture strength of a commercially available Ceramill (AMANNGIRRBACH) is greater than that of a Zirconia from ZR-White (UPCERA) variety. PMID:28824346

Microstructure and properties of aluminium-aluminium oxide graded composite materials

NASA Astrophysics Data System (ADS)

Kamaruzaman, F. F.; Nuruzzaman, D. M.; Ismail, N. M.; Hamedon, Z.; Iqbal, A. K. M. A.; Azhari, A.

2018-03-01

In this research works, four-layered aluminium-aluminium oxide (Al-Al2O3) graded composite materials were fabricated using powder metallurgy (PM) method. In processing, metal-ceramic graded composite materials of 0%, 10%, 20% and 30% weight percentage of ceramic concentration were prepared under 30 ton compaction load using a cylindrical die-punch set made of steel. After that, two-step pressureless sintering was carried out at sintering temperature and time 600°C and 3 hours respectively. It was observed that the sintered cylindrical specimens of 30 mm diameter were prepared successfully. The graded composite specimens were analysed and the properties such as density, microstructure and hardness were measured. It was found that after sintering process, the diameter of the graded cylindrical structure was decreased. Using both Archimedes method and rule of mixture (ROM), he density of structure was measured. The obtained results revealed that the microvickers hardness was increased as the ceramic component increases in the graded layer. Moreover, it was observed that the interface of the graded structure is clearly distinguished within the multilayer stack and the ceramic particles are almost uniformly distributed in the Al matrix.

Characterization of some biological specimens using TEM and SEM

NASA Astrophysics Data System (ADS)

Ghosh, Nabarun; Smith, Don W.

2009-05-01

The advent of novel techniques using the Transmission and Scanning Electron Microscopes improved observation on various biological specimens to characterize them. We studied some biological specimens using Transmission and Scanning Electron Microscopes. We followed negative staining technique with Phosphotungstic acid using bacterial culture of Bacillus subtilis. Negative staining is very convenient technique to view the structural morphology of different samples including bacteria, phage viruses and filaments in a cell. We could observe the bacterial cell wall and flagellum very well when trapped the negative stained biofilm from bacterial culture on a TEM grid. We cut ultra thin sections from the fixed root tips of Pisum sativum (Garden pea). Root tips were pre fixed with osmium tetroxide and post fixed with uranium acetate and placed in the BEEM capsule for block making. The ultrathin sections on the grid under TEM showed the granular chromatin in the nucleus. The protein bodies and large vacuoles with the storage materials were conspicuous. We followed fixation, critical point drying and sputter coating with gold to view the tissues with SEM after placing on stubs. SEM view of the leaf surface of a dangerous weed Tragia hispida showed the surface trichomes. These trichomes when break on touching releases poisonous content causing skin irritation. The cultured tissue from in vitro culture of Albizia lebbeck, a tree revealed the regenerative structures including leaf buds and stomata on the tissue surface. SEM and TEM allow investigating the minute details characteristic morphological features that can be used for classroom teaching.

Low blow Charpy impact of silicon carbides

NASA Technical Reports Server (NTRS)

Abe, H.; Chandan, H. C.; Bradt, R. C.

1978-01-01

The room-temperature impact resistance of several commercial silicon carbides was examined using an instrumented pendulum-type machine and Charpy-type specimens. Energy balance compliance methods and fracture toughness approaches, both applicable to other ceramics, were used for analysis. The results illustrate the importance of separating the machine and the specimen energy contributions and confirm the equivalence of KIc and KId. The material's impact energy was simply the specimen's stored elastic strain energy at fracture.

The effect of various primers on shear bond strength of zirconia ceramic and resin composite.

PubMed

Sanohkan, Sasiwimol; Kukiattrakoon, Boonlert; Larpboonphol, Narongrit; Sae-Yib, Taewalit; Jampa, Thibet; Manoppan, Satawat

2013-11-01

To determine the in vitro shear bond strengths (SBS) of zirconia ceramic to resin composite after various primer treatments. Forty zirconia ceramic (Zeno, Wieland Dental) specimens (10 mm in diameter and 2 mm thick) were prepared, sandblasted with 50 μm alumina, and divided into four groups (n = 10). Three experimental groups were surface treated with three primers; CP (RelyX Ceramic Primer, 3M ESPE), AP (Alloy Primer, Kuraray Medical), and MP (Monobond Plus, Ivoclar Vivadent AG). One group was not treated and served as the control. All specimens were bonded to a resin composite (Filtek Supreme XT, 3M ESPE) cylinder with an adhesive system (Adper Scotchbond Multi-Purpose Plus Adhesive, 3M ESPE) and then stored in 100% humidity at 37°C for 24 h before SBS testing in a universal testing machine. Mean SBS (MPa) were analyzed with one-way analysis of variance (ANOVA) and the Tukey's Honestly Significant Difference (HSD) test (α = 0.05). Group AP yielded the highest mean and standard deviation (SD) value of SBS (16.8 ± 2.5 MPa) and Group C presented the lowest mean and SD value (15.4 ± 1.6 MPa). The SBS did not differ significantly among the groups (P = 0.079). Within the limitations of this study, the SBS values between zirconia ceramic to resin composite using various primers and untreated surface were not significantly different.

Effect of oxidation heat treatment on the bond strength between a ceramic and cast and milled cobalt-chromium alloys.

PubMed

Li, Jieyin; Ye, Xiuhua; Li, Bohua; Liao, Juankun; Zhuang, Peilin; Ye, Jiantao

2015-08-01

There is a dearth of dental scientific literature on the effect of different oxidation heat treatments (OHTs) (as surface pretreatments) on the bonding performance of cast and milled cobalt-chromium (CoCr) alloys. The objective of this study was to evaluate the effect of different OHTs on the bond strength between a ceramic and cast and milled CoCr alloys. Cobalt-chromium metallic specimens were prepared using either a cast or a milled method. Specimens were subjected to four different OHT methods: without OHT; OHT under normal atmospheric pressure; OHT under vacuum; and OHT under vacuum followed by sandblasting. The metal-ceramic bond strength was evaluated using a three-point bending test according to ISO9693. Scanning electron microscopy and energy-dispersive spectroscopy were used to study the specimens' microstructure and elemental composition. The bond strength was not affected by the CoCr manufacturing method. Oxidation heat treatment performed under normal atmospheric pressure resulted in the highest bond strength. The concentration of oxygen on the alloy surfaces varied with the different pretreatment methods in the following order: OHT under normal atmospheric pressure > OHT under vacuum > without OHT ≈ OHT under vacuum followed by sandblasting. © 2015 Eur J Oral Sci.

[Study on friction and wear properties of dental zirconia ceramics processed by microwave and conventional sintering methods].

PubMed

Guoxin, Hu; Ying, Yang; Yuemei, Jiang; Wenjing, Xia

2017-04-01

This study evaluated the wear of an antagonist and friction and wear properties of dental zirconia ceramic that was subjected to microwave and conventional sintering methods. Ten specimens were fabricated from Lava brand zirconia and randomly assigned to microwave and conventional sintering groups. A profile tester for surface roughness was used to measure roughness of the specimens. Wear test was performed, and steatite ceramic was used as antagonist. Friction coefficient curves were recorded, and wear volume were calculated. Finally, optical microscope was used to observe the surface morphology of zirconia and steatite ceramics. Field emission scanning electron microscopy was used to observe the microstructure of zirconia. Wear volumes of microwave and conventionally sintered zirconia were (6.940±1.382)×10⁻², (7.952±1.815) ×10⁻² mm³, respectively. Moreover, wear volumes of antagonist after sintering by the considered methods were (14.189±4.745)×10⁻², (15.813±3.481)×10⁻² mm³, correspondingly. Statistically significant difference was not observed in the wear resistance of zirconia and wear volume of steatite ceramic upon exposure to two kinds of sintering methods. Optical microscopy showed that ploughed surfaces were apparent in zirconia. The wear surface of steatite ceramic against had craze, accompanied by plough. Scanning electron microscopy showed that zirconia was sintered compactly when subjected to both conventional sintering and microwave methods, whereas grains of zirconia sintered by microwave alone were smaller and more uniform. Two kinds of sintering methods are successfully used to produce dental zirconia ceramics with similar friction and wear properties.
.

Adhesion mechanisms at the interface between Y-TZP and veneering ceramic with and without modifier.

PubMed

Monaco, Carlo; Tucci, Antonella; Esposito, Leonardo; Scotti, Roberto

2014-11-01

This study investigated the mechanism of action at the interface between a commercially available Y-TZP and its veneering ceramic after final firing. Particular attention was paid, from a microstructural point of view, to evaluating the effects of different surface treatments carried out on the zirconia. In total, 32 specimens of presintered zirconia Y-TZP (LavaFrame, 3M ESPE, Germany) were cut with a low-speed diamond blade. The specimens were divided in two major groups, for testing after fracture or after mirror finishing, and were sintered following the manufacturer's instructions. Each major group was then randomly divided into four subgroups, according to using or not using the dedicated framework modifier, with or without a preliminary silica coating (CoJet, 3M ESPE). A suitable veneering ceramic was used for each group (Lava Ceram Overlay Porcelain, 3M ESPE). A detailed microstructural study of the interfaces of the zirconia-veneering ceramic was performed using a scanning electron microscope equipped with an energy-dispersive X-ray spectrometer to evaluate chemical variation at the interfaces. When the framework modifier was not applied on the Y-TZP surface, microdetachments, porosities, and openings in the ceramic layer were observed at the interlayers. A degree of diffusion of different elements through the interfaces from both the zirconia and veneering layers was detected. Application of the framework modifier can increase the wettability of the zirconia surfaces, allowing a continuous contact with the veneering layer. The micro-analysis performed showed the presence of a reaction area at the interface between the different materials. the increase of the wettability of the zirconia surface could improve the adhesion at interface with the veneering ceramic and reduce the clinical failure as chipping or delamination. Copyright © 2014 Elsevier Ltd. All rights reserved.

Effect of tooth brush abrasion and thermo-mechanical loading on direct and indirect veneer restorations.

PubMed

Rosentritt, Martin; Sawaljanow, Alexander; Behr, Michael; Kolbeck, Carola; Preis, Verena

2015-01-01

This study investigated toothbrush abrasion and in vitro aging on ceramic (indirect technique) and composite veneers (direct technique). Identical composite and individual human incisors were restored with industrially preformed composite veneers, indirectly produced ceramic veneers, and direct composite restorations. Surface roughness was determined before and after tooth brushing. A 5-year period of oral service was simulated by thermal cycling and mechanical loading (TCML). After TCML, all specimens were examined with microscopy and scanning electron microscopy. Specimens without failures during TCML were loaded until failure. analysis of variance; Bonferroni's post hoc analysis, Kaplan-Meier-Log Rank test (α = 0.05). Tooth brushing yielded a non-significant increase (p = 0.560) in roughness in all materials (industrial veneer, 0.12+/-0.07 μm, direct restoration, 0.18+/-0.14 μm, ceramic, 0.35+/-0.16 μm). No significant differences in roughness could be determined between the materials, neither before nor after testing (p < 0.001). After TCML of artificial teeth, direct and preformed composite veneers on composite teeth showed no failures or damages. Two ceramic veneers showed cracking in the labial area. After TCML of human teeth, transmission microscopy indicated a facial crack in a ceramic veneer and chipping in the cervical area of a preformed veneer. Two direct composite veneers lost retention. No significantly different survival rates were found between the three veneer groups. Fracture force on human teeth varied between 527.8+/-132.4 N (ceramic), 478.3+/-165.4 N (preformed composite), and 605.0+/-263.5 N (direct composite). All materials revealed comparable wear resistance. Indirect ceramic, direct restorative composite, and preformed composite veneers showed comparable failure rates and satisfying longevity. The results indicate similar longevity of the chosen materials for veneer restorations.

Color stability of nanocomposites polished with one-step systems.

PubMed

Ergücü, Zeynep; Türkün, L Sebnem; Aladag, Akin

2008-01-01

This study compared the color changes of five novel resin composites polished with two one-step polishing systems when exposed to coffee solution. The resin composites tested were Filtek Supreme XT, Grandio, CeramX, Premise and Tetric EvoCeram. A total of 150 discs (30/resin composites, 10 x 2 mm) were fabricated. Ten specimens/resin composites cured under Mylar strips served as the control. The other samples were polished with PoGo and OptraPol discs for 30 seconds using a slow speed handpiece and immersed in coffee (Nescafé) for seven days. Color measurements were made with Vita Easyshade at baseline and after one and seven days. Repeated Measures ANOVA and Bonferroni tests were used for statistical analyses (p< or =0.05). The differences between the mean DeltaE* values for the resin composites polished with two different one-step systems were statistically significant (p<0.05). After one week, all materials exhibited significant color changes compared to baseline. All Mylar finished specimens showed the most intense staining (p<0.05). There were no significant differences between the OptraPol and PoGo polished groups. Mylar-finished specimens of CeramX, Tetric EvoCeram, Premise and Filtek Supreme XT presented the greatest staining (p<0.05). For Grandio, there were no significant differences between the Mylar and PoGo groups, while the most stain resistant surfaces were attained with OptraPol. Removing the outermost resin layer by polishing procedures is essential to achieving a stain resistant, more esthetically stable surface. One-step polishing systems can be used successfully for polishing nanocomposites.

[Evaluation of alumina effects on the mechanical property and translucency of nano-zirconia all-ceramics].

PubMed

Jiang, Li; Zhao, Yong-qi; Zhang, Jing-chao; Liao, Yun-mao; Li, Wei

2010-06-01

To study the effects of alumina content on sintered density, mechanical property and translucency of zirconia nanocomposite all-ceramics. Specimens of zirconia nanocomposite all-ceramics were divided into five groups based on their alumina content which are 0% (control group), 2.5%, 5.0%, 7.5% and 10.0% respectively. The sintered densities were measured using Archimedes' method. Specimens' bending strengths were measured with three-point bending test (ISO 6872). The visible light transmittances were measured with spectrophotometric arrangements and the fractured surfaces were observed using scanning electron microscope (SEM). The control group of pure zirconia could be sintered to the theoretical density under pressure-less sintering condition. The bending strength was (1100.27 ± 54.82) MPa, the fracture toughness was (4.96 ± 0.35) MPa×m(1/2) and the transmittance could reach 17.03%. The sintered density and transmittance decreased as alumina content increased from 2.5% to 10%. However, the fracture toughness only increased slightly. In all four alumina groups, the additions of alumina had no significant effect on samples' bending strengths (P > 0.05). When the content of alumina was 10%, fracture toughness of specimens reached (6.13 ± 0.44) MPa×m(1/2) while samples' transmittance declined to 6.21%. SEM results showed that alumina particles had no significant effect on the grain size and distribution of tetragonal zirconia polycrystals. Additions of alumina to yttria-tetragonal zirconia polycrystals could influence its mechanical property and translucency. Additions of the other phase to zirconia ceramics should meet the clinical demands of strength and esthetics.

The effect of enamel bleaching on the shear bond strengths of metal and ceramic brackets.

PubMed

Oztaş, E; Bağdelen, G; Kiliçoğlu, H; Ulukapi, H; Aydin, I

2012-04-01

The aim of this study was to evaluate the effects of bleaching and delayed bonding on the shear bond strengths of metal and ceramic brackets bonded with light and chemically cure composite resin to human enamel. One hundred and twenty extracted human premolar teeth were randomly divided into three groups of 40 each. The first two groups were bleached with 20 per cent carbamide peroxide (CP) at-home bleaching agent. No bleaching procedures were applied to the third group and served as control. The first two and control groups were divided into equal subgroups according to different adhesive-bracket combinations. Specimens in group 1 (n = 40) were bonded 24 hours after bleaching process was completed while the specimens in group 2 (n = 40) were bonded 14 days after. The specimens in all groups were debonded with a Universal testing machine while the modified adhesive remnant index was used to evaluate fracture properties. No statistically significant differences were found between the shear bond strengths of metal and ceramic brackets bonded to bleached enamel after 24 hours, 14 days, and unbleached enamel with light or chemical cure adhesives (P > 0.05). The mode of failure was mostly at the bracket/adhesive interface and cohesive failures within the resin were also observed. Our findings indicated that at-home bleaching agents that contain 20 per cent CP did not significantly affect the shear bond strength of metal and ceramic orthodontic brackets to enamel when bonding is performed 24 hours or 14 days after bleaching.

Influence of surface treatment and cyclic loading on the durability of repaired all-ceramic crowns

PubMed Central

ATTIA, Ahmed

2010-01-01

Objective This study investigated the durability of repaired all-ceramic crowns after cyclic loading. Material and methods Eighty In-ceram zirconia crowns were fabricated to restore prepared maxillary premolars. Resin cement was used for cementation of crowns. Palatal cusps were removed to simulate fracture of veneering porcelain and divided into 4 groups (n = 20). Fracture site was treated before repair as follows: roughening with diamond bur, (DB); air abrasion using 50 µm Al2O3, (AA) and silica coating using Cojet system followed by silane application, (SC). Control group (CG) 20 specimens were left without fracture. Palatal cusps were repaired using composite resin. Specimens were stored in water bath at 37°C for one week. Ten specimens of each group were subjected to cyclic loading. Fracture load (N) was recorded for each specimen using a universal testing machine. Two-way analysis of variance (ANOVA) and Tukey honestly significant difference (HSD) test (α=.05) were used for statistical analysis. Results There was statistically significant difference between control and tested groups, (p<0.001). Post Hoc analysis with the Tukey HSD test showed that cyclic loading fatigue significantly decreased means fracture load of control and test groups as follows (CG, 950.4±62.6 / 872.3±87.4, P = 0.0004), (DB, 624.2 ±38 / 425.5± 31.7, P <.001), (AA, 711.5 ±15.5 / 490 ± 25.2, p <0.001) and (SC, 788.7 ± 18.1 / 610.2 ± 25.2, P <.001), while silica coating and silane application significantly increased fracture load of repaired crowns (p<0.05). Conclusion Repair of fractured Inceram zirconia crowns after chairside treatment of the fracture site by silica coating and silane application could improve longevity of repaired In-ceram zirconia crowns. PMID:20485932

Evaluation of ceramics for stator application: Gas turbine engine report

NASA Technical Reports Server (NTRS)

Trela, W.; Havstad, P. H.

1978-01-01

Current ceramic materials, component fabrication processes, and reliability prediction capability for ceramic stators in an automotive gas turbine engine environment are assessed. Simulated engine duty cycle testing of stators conducted at temperatures up to 1093 C is discussed. Materials evaluated are SiC and Si3N4 fabricated from two near-net-shape processes: slip casting and injection molding. Stators for durability cycle evaluation and test specimens for material property characterization, and reliability prediction model prepared to predict stator performance in the simulated engine environment are considered. The status and description of the work performed for the reliability prediction modeling, stator fabrication, material property characterization, and ceramic stator evaluation efforts are reported.

Benefits from bremsstrahlung distribution evaluation to get unknown information from specimen in SEM and TEM

NASA Astrophysics Data System (ADS)

Eggert, F.; Camus, P. P.; Schleifer, M.; Reinauer, F.

2018-01-01

The energy-dispersive X-ray spectrometer (EDS or EDX) is a commonly used device to characterise the composition of investigated material in scanning and transmission electron microscopes (SEM and TEM). One major benefit compared to wavelength-dispersive X-ray spectrometers (WDS) is that EDS systems collect the entire spectrum simultaneously. Therefore, not only are all emitted characteristic X-ray lines in the spectrum, but also the complete bremsstrahlung distribution is included. It is possible to get information about the specimen even from this radiation, which is usually perceived more as a disturbing background. This is possible by using theoretical model knowledge about bremsstrahlung excitation and absorption in the specimen in comparison to the actual measured spectrum. The core aim of this investigation is to present a method for better bremsstrahlung fitting in unknown geometry cases by variation of the geometry parameters and to utilise this knowledge also for characteristic radiation evaluation. A method is described, which allows the parameterisation of the true X-ray absorption conditions during spectrum acquisition. An ‘effective tilt’ angle parameter is determined by evaluation of the bremsstrahlung shape of the measured SEM spectra. It is useful for bremsstrahlung background approximation, with exact calculations of the absorption edges below the characteristic peaks, required for P/B-ZAF model based quantification methods. It can even be used for ZAF based quantification models as a variable input parameter. The analytical results are then much more reliable for the different absorption effects from irregular specimen surfaces because the unknown absorption dependency is considered. Finally, the method is also applied for evaluation of TEM spectra. In this case, the real physical parameter optimisation is with sample thickness (mass thickness), which is influencing the emitted and measured spectrum due to different absorption with TEM measurements. The effects are in the very low energy part of the spectrum, and are much more visible with most recent windowless TEM detectors. The thickness of the sample can be determined in this way from the measured bremsstrahlung spectrum shape.

An improved FIB sample preparation technique for site-specific plan-view specimens: A new cutting geometry.

PubMed

Li, Chen; Habler, Gerlinde; Baldwin, Lisa C; Abart, Rainer

2018-01-01

Focused ion beam (FIB) sample preparation technique in plan-view geometry allows direct correlations of the atomic structure study via transmission electron microscopy with micrometer-scale property measurements. However, one main technical difficulty is that a large amount of material must be removed underneath the specimen. Furthermore, directly monitoring the milling process is difficult unless very large material volumes surrounding the TEM specimen site are removed. In this paper, a new cutting geometry is introduced for FIB lift-out sample preparation with plan-view geometry. Firstly, an "isolated" cuboid shaped specimen is cut out, leaving a "bridge" connecting it with the bulk material. Subsequently the two long sides of the "isolated" cuboid are wedged, forming a triangular prism shape. A micromanipulator needle is used for in-situ transfer of the specimen to a FIB TEM grid, which has been mounted parallel with the specimen surface using a simple custom-made sample slit. Finally, the grid is transferred to the standard FIB grid holder for final thinning with standard procedures. This new cutting geometry provides clear viewing angles for monitoring the milling process, which solves the difficulty of judging whether the specimen has been entirely detached from the bulk material, with the least possible damage to the surrounding materials. With an improved success rate and efficiency, this plan-view FIB lift-out specimen preparation technique should have a wide application for material science. Copyright © 2017 The Authors. Published by Elsevier B.V. All rights reserved.

Effects of silica coating and silane surface conditioning on the bond strength of rebonded metal and ceramic brackets.

PubMed

Atsü, Saadet; Çatalbaş, Bülent; Gelgör, İbrahim Erhan

2011-01-01

The aim of this study was to evaluate the effects of tribochemical silica coating and silane surface conditioning on the bond strength of rebonded metal and ceramic brackets. Twenty debonded metal and 20 debonded ceramic brackets were randomly assigned to receive one of the following surface treatments (n=10 for each group): (1) sandblasting (control); (2) tribochemical silica coating combined with silane. Brackets were rebonded to the enamel surface on the labial and lingual sides of premolars with a light-polymerized resin composite. All specimens were stored in distilled water for 1 week and then thermocycled (5,000 cycles) between 5-55ºC. Shear bond strength values were measured using a universal testing machine. Student's t-test was used to compare the data (α=0.05). Failure mode was assessed using a stereomicroscope, and the treated and non-treated bracket surfaces were observed by scanning electron microscopy. Rebonded ceramic brackets treated with silica coating followed by silanization had significantly greater bond strength values (17.7±4.4 MPa) than the sandblasting group (2.4±0.8 MPa, P<0.001). No significant difference was observed between the rebonded metal brackets treated with silica coating with silanization (15±3.9 MPa) and the sandblasted brackets (13.6±3.9 MPa). Treated rebonded ceramic specimens primarily exhibited cohesive failure in resin and adhesive failure at the enamel-adhesive interface. In comparison to sandblasting, silica coating with aluminum trioxide particles followed by silanization resulted in higher bond strengths of rebonded ceramic brackets.

Assessment of a prototype computer colour matching system to reproduce natural tooth colour on ceramic restorations.

PubMed

Kristiansen, Joshua; Sakai, Maiko; Da Silva, John D; Gil, Mindy; Ishikawa-Nagai, Shigemi

2011-12-01

The aim of this study was to assess the accuracy of a prototype computer colour matching (CCM) system for dental ceramics targeting the colour of natural maxillary central incisors employing a dental spectrophotometer and the Kubelka-Munk theory. Seventeen human volunteers with natural intact maxillary central incisors were selected to participate in this study. One central incisor from each subject was measured in the body region by a spectrophotometer and the reflectance values were used by the CCM system in order to generate a prescription for a ceramic mixture to reproduce the target tooth's colour. Ceramic discs were fabricated based on these prescriptions and layered on a zirconia ceramic core material of a specified colour. The colour match of each two-layered specimen to the target natural tooth was assessed by CIELAB colour coordinates (ΔE(*), ΔL(*), Δa(*) and Δb(*)). The average colour difference ΔE(*) value was 2.58±84 for the ceramic specimen-natural tooth (CS-NT) pairs. ΔL(*) values ranged from 0.17 to 2.71, Δa(*) values ranged from -1.70 to 0.61, and Δb(*) values ranged from -1.48 to 3.81. There was a moderate inverse correlation (R=-0.44, p-value=0.0721) between L(*) values for natural target teeth and ΔE(*) values; no such correlation was found for a(*) and b(*) values. The newly developed prototype CCM system has the potential to be used as an efficient tool in the reproduction of natural tooth colour. Copyright © 2011. Published by Elsevier Ltd.

Evaluation of metal-ceramic bond characteristics of three dental Co-Cr alloys prepared with different fabrication techniques.

PubMed

Wang, Hongmei; Feng, Qing; Li, Ning; Xu, Sheng

2016-12-01

Limited information is available regarding the metal-ceramic bond strength of dental Co-Cr alloys fabricated by casting (CAST), computer numerical control (CNC) milling, and selective laser melting (SLM). The purpose of this in vitro study was to evaluate the metal-ceramic bond characteristics of 3 dental Co-Cr alloys fabricated by casting, computer numerical control milling, and selective laser melting techniques using the 3-point bend test (International Organization for Standardization [ISO] standard 9693). Forty-five specimens (25×3×0.5 mm) made of dental Co-Cr alloys were prepared by CAST, CNC milling, and SLM techniques. The morphology of the oxidation surface of metal specimens was evaluated by scanning electron microscopy (SEM). After porcelain application, the interfacial characterization was evaluated by SEM equipped with energy-dispersive spectrometry (EDS) analysis, and the metal-ceramic bond strength was assessed with the 3-point bend test. Failure type and elemental composition on the debonding interface were assessed by SEM/EDS. The bond strength was statistically analyzed by 1-way ANOVA and Tukey honest significant difference test (α=.05). The oxidation surfaces of the CAST, CNC, and SLM groups were different. They were porous in the CAST group but compact and irregular in the CNC and SLM groups. The metal-ceramic interfaces of the SLM and CNC groups showed excellent combination compared with those of the CAST group. The bond strength was 37.7 ±6.5 MPa for CAST, 43.3 ±9.2 MPa for CNC, and 46.8 ±5.1 MPa for the SLM group. Statistically significant differences were found among the 3 groups tested (P=.028). The debonding surfaces of all specimens exhibited cohesive failure mode. The oxidation surface morphologies and thicknesses of dental Co-Cr alloys are dependent on the different fabrication techniques used. The bond strength of all 3 groups exceed the minimum acceptable value of 25 MPa recommended by ISO 9693; hence, dental Co-Cr alloy fabricated with the SLM techniques could be a promising alternative for metal ceramic restorations. Copyright © 2016 Editorial Council for the Journal of Prosthetic Dentistry. Published by Elsevier Inc. All rights reserved.

Room temperature deformation mechanisms of alumina particles observed from in situ micro-compression and atomistic simulations.

DOE PAGES

Sarobol, Pylin; Chandross, Michael E.; Carroll, Jay D.; ...

2015-09-22

Aerosol deposition (AD) is a solid-state deposition technology that has been developed to fabricate ceramic coatings nominally at room temperature. Sub-micron ceramic particles accelerated by pressurized gas impact, deform, and consolidate on substrates under vacuum. Ceramic particle consolidation in AD coatings is highly dependent on particle deformation and bonding; these behaviors are not well understood. In this work, atomistic simulations and in situ micro-compressions in the scanning electron microscope, and the transmission electron microscope (TEM) were utilized to investigate fundamental mechanisms responsible for plastic deformation/fracture of particles under applied compression. Results showed that highly defective micron-sized alumina particles, initially containingmore » numerous dislocations or a grain boundary, exhibited no observable shape change before fracture/fragmentation. Simulations and experimental results indicated that particles containing a grain boundary only accommodate low strain energy per unit volume before crack nucleation and propagation. In contrast, nearly defect-free, sub-micron, single crystal alumina particles exhibited plastic deformation and fracture without fragmentation. Dislocation nucleation/motion, significant plastic deformation, and shape change were observed. Simulation and TEM in situ micro-compression results indicated that nearly defect-free particles accommodate high strain energy per unit volume associated with dislocation plasticity before fracture. As a result, the identified deformation mechanisms provide insight into feedstock design for AD.« less

Effects of Laser Treatment on the Bond Strength of Differently Sintered Zirconia Ceramics.

PubMed

Dede, Doğu Ömür; Yenisey, Murat; Rona, Nergiz; Öngöz Dede, Figen

2016-07-01

The purpose of this study was to investigate the effects of carbon dioxide (CO2) and Erbium-doped yttrium aluminum garnet (Er:YAG) laser irradiations on the shear bond strength (SBS) of differently sintered zirconia ceramics to resin cement. Eighty zirconia specimens were prepared, sintered in two different periods (short = Ss, long = Ls), and divided into four treatment groups (n = 10 each). These groups were (a) untreated (control), (b) Er:YAG laser irradiated with 6 W power for 5 sec, (c) CO2 laser with 2 W power for 10 sec, (d) CO2 laser with 4 W power for 10 sec. Scanning electron microscope (SEM) images were recorded for each of the eight groups. Eighty composite resin discs (3 × 3 mm) were fabricated and cemented with an adhesive resin cement to ceramic specimens. The SBS test was performed after specimens were stored in water for 24 h by an universal testing machine at a crosshead speed of 1 mm/min. Data were statistically analyzed with two way analysis of variance (ANOVA) and Tukey honest significant difference (HSD) test (α = 0.05). According to the ANOVA, the sintering time, surface treatments and their interaction were statistically significant (p < 0.05). Although each of the laser-irradiated groups were significantly higher than the control groups, there was no statistically significant difference among them (p > 0.05). Variation in sintering time from 2.5 to 5.0 h may have influenced the SBS of Yttrium-stabilized tetragonal zirconia polycrystalline (Y-TZP) ceramics. Although CO2 and Er:YAG laser irradiation techniques may increase the SBS values of both tested zirconia ceramics, they are recommended for clinicians as an alternative pretreatment method.

Qualitative Assessment of Wear Resistance and Surface Hardness of Different Commercially Available Dental Porcelain: An in vitro Study.

PubMed

Singh, Abhishek; Nagpal, Abhishek; Pawah, Salil; Pathak, Chetan; Issar, Gaurav; Sharma, Pankaj

2016-09-01

In an attempt to minimize wear damage to the enamel of antagonist teeth, new low and medium fusing ceramic materials have been developed. Manufacturers usually claim that these ceramics are wear-friendly because of their lower hardness, lower concentrations of crystal phase, and smaller crystal sizes. This study aimed to quantitatively analyze the wear strength of various commercially available dental porcelain with tooth enamel as well as the surface hardness of these dental porcelain. The basic model was designed as a pin on plate arrangement. The tooth specimens were mounted on the stylus which was centered on the ceramic specimen in a wear testing machine. The dental ceramic specimen was centered in the metal die. A load of 40 N was applied at a rate of 80 cycles/minute for 15 minutes. In the current study, mean wear depth (Ra) value, volumetric loss, and surface hardness were obtained by standard quantification method and were statistically evaluated. Ceramco-3 was reported to be most abrasive for enamel; however, Duceram love significantly more abraded itself than the other two, Ceramco-3 and Vita Alpha, and generated the lowest loss of enamel. Also, same abrasive type of wear was revealed for all three variants of tested ceramics. Ceramco-3 was the most abrasive for enamel, while surface roughness (mean wear depth) of Duceram love was maximum and for Ceramco-3 it was minimum. The value of surface roughness for Vita Alpha was in between Duceram love and Ceramco-3. Nonetheless, the mean surface hardness of Duceram love was found to be least and maximum for Vita Alpha. In situations of dental wear and wasting tooth disease (Attrition/Abrasion), Duceram can be applied in lieu of Ceramco-3 so as to prevent worsening of existing dentition. However, in younger patients Vita Alpha would offer maximum durability due to its greater surface hardness.

NDE of structural ceramics

NASA Technical Reports Server (NTRS)

Klima, S. J.; Vary, A.

1986-01-01

Radiographic, ultrasonic, scanning laser acoustic microscopy (SLAM), and thermo-acoustic microscopy techniques were used to characterize silicon nitride and silicon carbide modulus-of-rupture test specimens in various stages of fabrication. Conventional and microfocus X-ray techniques were found capable of detecting minute high density inclusions in as-received powders, green compacts, and fully densified specimens. Significant density gradients in sintered bars were observed by radiography, ultrasonic velocity, and SLAM. Ultrasonic attenuation was found sensitive to microstructural variations due to grain and void morphology and distribution. SLAM was also capable of detecting voids, inclusions and cracks in finished test bars. Consideration is given to the potential for applying thermo-acoustic microscopy techniques to green and densified ceramics. The detection probability statistics and some limitations of radiography and SLAM also are discussed.

Evaluation of Surface Roughness of Ceramic and Resin Composite Material Used for Conservative Indirect Restorations, after Repolishing by Intraoral Means.

PubMed

Vrochari, Areti D; Petropoulou, Aikaterini; Chronopoulos, Vasilios; Polydorou, Olga; Massey, Ward; Hellwig, Elmar

2017-06-01

To evaluate and compare the mean surface roughness (Ra) of one ceramic and one resin composite material used for indirect restorations, after grinding and repolishing by intraoral means. The materials used were the lithium disilicate glass ceramic IPS e.max Press (EMP) and the indirect resin composite restoration system Gradia (GR). Twelve specimen disks were prepared from each material according to the manufacturer of each material. Five initial measurements of the Ra (Ra 1 ) were made on each specimen as a referral basis, and the specimens were ground with a fine (red) diamond bur. The specimens were repolished using (a) Komet Dialite Polishing Kit for EMP and (b) Enhance Finishing and Polishing System and Prisma Gloss Polishing Paste for GR. Five final Ra (Ra 2 ) measurements were performed on each specimen. All measurements were made using a laser profilometer. Scanning electron microscopy (SEM) was also used to visualize the initial surface morphology and the morphological changes on the specimens' surface after repolishing. A highly significant difference was found between Ra 1EMP and Ra 2EMP (p < 0.001), between Ra 1GR and Ra 2GR (p < 0.001), as well as between Ra 2EMP and Ra 2GR (p < 0.001), when compared in pairs. A highly significant difference (p < 0.001) was also found between ΔRa EMP and ΔRa GR , with ΔRa GR being higher than ΔRa EMP . The Ra GR values were higher than the Ra EMP values at all times. SEM revealed that both EMP and GR repolished surfaces presented with irregularities; however, in GR specimens major voids and craters were present. EMP was found to perform better when polished by intraoral means compared with GR. Both materials exhibited Ra 2 above the critical threshold for increased plaque accumulation and periodontal inflammation. If enamel-to-enamel roughness found in occlusal contact areas is considered as baseline, both materials were clinically acceptable after repolishing. © 2015 by the American College of Prosthodontists.

Comparison of structure, morphology, and leach characteristics of multi-phase ceramics produced via melt processing and hot isostatic pressing

DOE Office of Scientific and Technical Information (OSTI.GOV)

Dandeneau, Christopher S.; Hong, Tao; Brinkman, Kyle S.

Melt processing of multi-phase ceramic waste forms offers potential advantages over traditional solid-state synthesis methods given both the prevalence of melters currently in use and the ability to reduce the possibility of airborne radionuclide contamination. In this work, multi-phase ceramics with a targeted hollandite composition of Ba 1.0Cs 0.3Cr 1.0Al 0.3Fe 1.0Ti 5.7O 16 were fabricated by melt processing at 1675 °C and hot isostatic pressing (HIP) at 1250 and 1300 °C. X-ray diffraction analysis (XRD) confirmed hollandite as the major phase in all specimens. Zirconolite/pyrochlore peaks and weaker perovskite reflections were observed after melt processing, while HIP samples displayedmore » prominent perovskite peaks and low-intensity zirconolite reflections. Melt processing produced specimens with large (>50 μm) well-defined hollandite grains, while HIP yielded samples with a more fine-grained morphology. Elemental analysis showed “islands” rich in Cs and Ti across the surface of the 1300 °C HIP sample, suggesting partial melting and partitioning of Cs into multiple phases. Photoemission data revealed multiple Cs 3d spin-orbit pairs for the HIP samples, with the lower binding energy doublets likely corresponding to Cs located in more leachable phases. Among all specimens examined, the melt-processed sample exhibited the lowest fractional release rates for Rb and Cs. However, the retention of Sr and Mo was greater in the HIP specimens.« less

CARES/Life Ceramics Durability Evaluation Software Enhanced for Cyclic Fatigue

NASA Technical Reports Server (NTRS)

Nemeth, Noel N.; Powers, Lynn M.; Janosik, Lesley A.

1999-01-01

The CARES/Life computer program predicts the probability of a monolithic ceramic component's failure as a function of time in service. The program has many features and options for materials evaluation and component design. It couples commercial finite element programs--which resolve a component's temperature and stress distribution--to reliability evaluation and fracture mechanics routines for modeling strength-limiting defects. The capability, flexibility, and uniqueness of CARES/Life have attracted many users representing a broad range of interests and has resulted in numerous awards for technological achievements and technology transfer. Recent work with CARES/Life was directed at enhancing the program s capabilities with regards to cyclic fatigue. Only in the last few years have ceramics been recognized to be susceptible to enhanced degradation from cyclic loading. To account for cyclic loads, researchers at the NASA Lewis Research Center developed a crack growth model that combines the Power Law (time-dependent) and the Walker Law (cycle-dependent) crack growth models. This combined model has the characteristics of Power Law behavior (decreased damage) at high R ratios (minimum load/maximum load) and of Walker law behavior (increased damage) at low R ratios. In addition, a parameter estimation methodology for constant-amplitude, steady-state cyclic fatigue experiments was developed using nonlinear least squares and a modified Levenberg-Marquardt algorithm. This methodology is used to give best estimates of parameter values from cyclic fatigue specimen rupture data (usually tensile or flexure bar specimens) for a relatively small number of specimens. Methodology to account for runout data (unfailed specimens over the duration of the experiment) was also included.

Comparison of structure, morphology, and leach characteristics of multi-phase ceramics produced via melt processing and hot isostatic pressing

DOE PAGES

Dandeneau, Christopher S.; Hong, Tao; Brinkman, Kyle S.; ...

2018-02-08

Melt processing of multi-phase ceramic waste forms offers potential advantages over traditional solid-state synthesis methods given both the prevalence of melters currently in use and the ability to reduce the possibility of airborne radionuclide contamination. In this work, multi-phase ceramics with a targeted hollandite composition of Ba 1.0Cs 0.3Cr 1.0Al 0.3Fe 1.0Ti 5.7O 16 were fabricated by melt processing at 1675 °C and hot isostatic pressing (HIP) at 1250 and 1300 °C. X-ray diffraction analysis (XRD) confirmed hollandite as the major phase in all specimens. Zirconolite/pyrochlore peaks and weaker perovskite reflections were observed after melt processing, while HIP samples displayedmore » prominent perovskite peaks and low-intensity zirconolite reflections. Melt processing produced specimens with large (>50 μm) well-defined hollandite grains, while HIP yielded samples with a more fine-grained morphology. Elemental analysis showed “islands” rich in Cs and Ti across the surface of the 1300 °C HIP sample, suggesting partial melting and partitioning of Cs into multiple phases. Photoemission data revealed multiple Cs 3d spin-orbit pairs for the HIP samples, with the lower binding energy doublets likely corresponding to Cs located in more leachable phases. Among all specimens examined, the melt-processed sample exhibited the lowest fractional release rates for Rb and Cs. However, the retention of Sr and Mo was greater in the HIP specimens.« less

Design of a 300-kV gas environmental transmission electron microscope equipped with a cold field emission gun.

PubMed

Isakozawa, Shigeto; Nagaoki, Isao; Watabe, Akira; Nagakubo, Yasuhira; Saito, Nobuhiro; Matsumoto, Hiroaki; Zhang, Xiao Feng; Taniguchi, Yoshifumi; Baba, Norio

2016-08-01

A new in situ environmental transmission electron microscope (ETEM) was developed based on a 300 kV TEM with a cold field emission gun (CFEG). Particular caution was taken in the ETEM design to assure uncompromised imaging and analytical performance of the TEM. Because of the improved pumping system between the gun and column, the vacuum of CFEG was largely improved and the probe current was sufficiently stabilized to operate without tip flashing for 2-3 h or longer. A high brightness of 2.5 × 10(9) A/cm(2) sr was measured at 300 kV, verifying the high quality of the CFEG electron beam. A specially designed gas injection-heating holder was used in the in situ TEM study at elevated temperatures with or without gas around the TEM specimen. Using this holder in a 10 Pa gas atmosphere and specimen temperatures up to 1000°C, high-resolution ETEM performance and analysis were achieved. © The Author 2016. Published by Oxford University Press on behalf of The Japanese Society of Microscopy. All rights reserved. For permissions, please e-mail: journals.permissions@oup.com.

In Situ TEM Study of Interaction between Dislocations and a Single Nanotwin under Nanoindentation.

PubMed

Wang, Bo; Zhang, Zhenyu; Cui, Junfeng; Jiang, Nan; Lyu, Jilei; Chen, Guoxin; Wang, Jia; Liu, Zhiduo; Yu, Jinhong; Lin, Chengte; Ye, Fei; Guo, Dongming

2017-09-06

Nanotwinned (nt) materials exhibit excellent mechanical properties, and have been attracting much more attention of late. Nevertheless, the fundamental mechanism of interaction between dislocations and a single nanotwin is not understood. In this study, in situ transmission electron microscopy (TEM) nanoindentation is performed, on a specimen of a nickel (Ni) alloy containing a single nanotwin of 89 nm in thickness. The specimen is prepared using focused ion beam (FIB) technique from an nt surface, which is formed by a novel approach under indentation using a developed diamond panel with tips array. The stiffness of the specimen is ten times that of the pristine counterparts during loading. The ultrahigh stiffness is attributed to the generation of nanotwins and the impediment of the single twin to the dislocations. Two peak loads are induced by the activation of a new slip system and the penetration of dislocations over the single nanotwin, respectively. One slip band is parallel to the single nanotwin, indicating the slip of dislocations along the nanotwin. In situ TEM observation of nanoindentation reveals a new insight for the interaction between dislocations and a single nanotwin. This paves the way for design and preparation of high-performance nt surfaces of Ni alloys used for aircraft engines, gas turbines, turbocharger components, ducts, and absorbers.

Improvement of the stability of hydroxyapatite through glass ceramic reinforcement.

PubMed

Ha, Na Ra; Yang, Zheng Xun; Hwang, Kyu Hong; Kim, Tae Suk; Lee, Jong Kook

2010-05-01

Hydroxyapatite has achieved significant application in orthopedic and dental implants due to its excellent biocompatibility. Sintered hydroxyapatites showed significant dissolution, however, after their immersion in water or simulated body fluid (SBF). This grain boundary dissolution, even in pure hydroxyapatites, resulted in grain separation at the surfaces, and finally, in fracture. In this study, hydroxyapatite ceramics containing apatite-wollastonite (AW) or calcium silicate (SG) glass ceramics as additives were prepared to prevent the dissolution. AW and SG glass ceramics were added at 0-7 wt% and powder-compacted uniaxially followed by firing at moisture conditions. The glass phase was incorporated into the hydroxyapatite to act as a sintering aid, followed by crystallization, to improve the mechanical properties without reducing the biocompatibility. As seen in the results of the dissolution test, a significant amount of damage was reduced even after more than 14 days. TEM and SEM showed no decomposition of HA to the secondary phase, and the fracture toughness increased, becoming even higher than that of the commercial hydroxyapatite.

Mechanism of slip and twinning

NASA Technical Reports Server (NTRS)

Rastani, Mansur

1992-01-01

The objectives are to: (1) demonstrate the mechanisms of deformation in body centered cubic (BCC), face centered cubic (FCC), and hexagonal close-packed (HCP)-structure metals and alloys and in some ceramics as well; (2) examine the deformed microstructures (slip lines and twin boundaries) in different grains of metallic and ceramic specimens; and (3) study visually the deformed macrostructure (slip and twin bands) of metals and alloys. Some of the topics covered include: deformation behavior of materials, mechanisms of plastic deformation, slip bands, twin bands, ductile failure, intergranular fracture, shear failure, slip planes, crystal deformation, and dislocations in ceramics.

Fracture resistance of a selection of full-contour all-ceramic crowns: an in vitro study.

PubMed

Zesewitz, Tim F; Knauber, Andreas W; Nothdurft, Frank P

2014-01-01

This study aimed to evaluate the fracture resistance of monolithic single crowns made from zirconia (ZI), lithium disilicate (LS2), or feldspar ceramic (FC). Five groups of crowns representing a maxillary first molar were made with the appropriate dimensions according to the manufacturer's instructions. The ZI and LS2 crowns were luted adhesively or cemented conventionally on a metal abutment tooth analog. The feldspar ceramic crowns were luted adhesively. All specimens underwent axial loading until fracture. The crowns in the ZI groups possessed the highest fracture resistance independent of the mode of fixation.

A simple approach to characterizing block copolymer assemblies: graphene oxide supports for high contrast multi-technique imaging†

PubMed Central

Patterson, Joseph P.; Sanchez, Ana M.; Petzetakis, Nikos; Smart, Thomas P.; Epps, Thomas H.; Portman, Ian

2013-01-01

Block copolymers are well-known to self-assemble into a range of 3-dimensional morphologies. However, due to their nanoscale dimensions, resolving their exact structure can be a challenge. Transmission electron microscopy (TEM) is a powerful technique for achieving this, but for polymeric assemblies chemical fixing/staining techniques are usually required to increase image contrast and protect specimens from electron beam damage. Graphene oxide (GO) is a robust, water-dispersable, and nearly electron transparent membrane: an ideal support for TEM. We show that when using GO supports no stains are required to acquire high contrast TEM images and that the specimens remain stable under the electron beam for long periods, allowing sample analysis by a range of electron microscopy techniques. GO supports are also used for further characterization of assemblies by atomic force microscopy. The simplicity of sample preparation and analysis, as well as the potential for significantly increased contrast background, make GO supports an attractive alternative for the analysis of block copolymer assemblies. PMID:24049544

Effect of the application of surface treatments before and after sintering on the flexural strength, phase transformation and surface topography of zirconia.

PubMed

Kurtulmus-Yilmaz, Sevcan; Aktore, Huseyin

2018-05-01

To evaluate the effects of airborne-particle abrasion (APA) and Er,Cr:YSGG laser irradiation on 4-point-flexural strength, phase transformation and morphologic changes of zirconia ceramics treated at pre-sintered or post-sintered stage. Three hundred and forty-two bar shaped zirconia specimens were milled with different sizes according to the flexural strength test (n = 10), X-ray diffraction (XRD) (n = 4) and field emission scanning electron microscope (FE-SEM) (n = 4) analyses. For each test protocol, specimens were divided into 4 main groups whether the surface treatments applied before or after sintering and whether the specimens received heat treatment or not as pre-sintered, post-sintered no-heat and post-sintered heat-treated groups, and a group was served as control. Main groups were further divided into 6 equal subgroups according to surface treatment method applied (2 W-, 3 W-, 4 W-, 5 W-, 6 W-laser irradiations and APA). Surface treatments were applied to pre-sintered groups before sintering and to post-sintered groups after sintering. Post-sintered heat-treated groups were subjected to veneer ceramic firing simulation after surface treatments. Flexural strength and flexural modulus values were statistically analysed and monoclinic phase content was calculated. Weibull analysis was used to evaluate strength reliability and fractographic analysis was conducted. Highest flexural strength values were detected at post-sintered no-heat APA and 4W-laser groups (P < 0.05). Pre-sintered groups showed statistically lower flexural strength values. Heat treatment decreased the strength of the specimens. Monoclinic phase content was only detected at post-sintered no-heat groups and the highest amount was detected at APA group. Rougher surfaces and deeper irregularities were detected at FE-SEM images pre-sintered groups. Application of surface treatments at pre-sintered stage may be detrimental for zirconia ceramics in terms of flexural strength. Treating the surface of zirconia ceramic before sintering process is not recommended due to significant decrease in flexural strength values. 2 W-4 W Er,Cr:YSGG laser irradiations can be regarded as alternative surface treatment methods when zirconia restoration would be subjected to veneer ceramic firing procedures. Copyright © 2018 Elsevier Ltd. All rights reserved.

"One-sample concept" micro-combinatory for high throughput TEM of binary films.

PubMed

Sáfrán, György

2018-04-01

Phases of thin films may remarkably differ from that of bulk. Unlike to the comprehensive data files of Binary Phase Diagrams [1] available for bulk, complete phase maps for thin binary layers do not exist. This is due to both the diverse metastable, non-equilibrium or instable phases feasible in thin films and the required volume of characterization work with analytical techniques like TEM, SAED and EDS. The aim of the present work was to develop a method that remarkably facilitates the TEM study of the diverse binary phases of thin films, or the creation of phase maps. A micro-combinatorial method was worked out that enables both preparation and study of a gradient two-component film within a single TEM specimen. For a demonstration of the technique thin Mn x Al 1- x binary samples with evolving concentration from x = 0 to x = 1 have been prepared so that the transition from pure Mn to pure Al covers a 1.5 mm long track within the 3 mm diameter TEM grid. The proposed method enables the preparation and study of thin combinatorial samples including all feasible phases as a function of composition or other deposition parameters. Contrary to known "combinatorial chemistry", in which a series of different samples are deposited in one run, and investigated, one at a time, the present micro-combinatorial method produces a single specimen condensing a complete library of a binary system that can be studied, efficiently, within a single TEM session. That provides extremely high throughput for TEM characterization of composition-dependent phases, exploration of new materials, or the construction of phase diagrams of binary films. Copyright © 2018 Elsevier B.V. All rights reserved.

Lisicon Glass-Ceramics Mediated Catalysis of Oxygen Reduction

DTIC Science & Technology

2011-06-01

submitted January 19, 2011; revised manuscript received February 23, 2011. Published March 25, 2011. The Lisicon (lithium super ionic conductor) glass...ceramics is a polycrystalline analogue of Nasicon (sodium super ionic conductor) structure. The general class of Nasicon structures consists of two...with a heating rate of 5C=min. In the BET technique a dry specimen was evacuated of all gases and cooled down to 77 K, liquid nitrogen temperature

Characterization of mechanical damage mechanisms in ceramic composite materials. Technical report, 23 May 1987-24 May 1988

DOE Office of Scientific and Technical Information (OSTI.GOV)

Lankford, J.

High-strain-rate compressive failure mechanisms in fiber-reinforced ceramic-matrix composite materials were characterized. These are contrasted with composite damage development at low-strain rates, and with the dynamic failure of monolithic ceramics. It is shown that it is possible to derive major strain-rate strengthening benefits if a major fraction of the fiber reinforcement is aligned with the load axis. This effect considerably exceeds the inertial microfracture strengthening observed in monolithic ceramics, and non-aligned composites. Its basis is shown to be the trans-specimen propagation time period for heterogeneously-nucleated, high-strain kink bands. A brief study on zirconia focused on the remarkable inverse strength-strain rate resultmore » previously observed for both fully and partially-stabilized zirconia single crystals, whereby the strength decreased with increasing strain rate. Based on the hypothesis that the suppression of microplastic flow, hence, local stress relaxation, might be responsible for this behavior, fully stabilized (i.e., non-transformable) specimens were strain-gaged and subjected to compressive microstrain. The rather stunning observation was that the crystals are highly microplastic, exhibiting plastic yield on loading and anelasticity and reverse plasticity upon unloading. These results clearly support the hypothesis that with increasing strain rate, microcracking is favored at the expense of microplasticity.« less

Least Squares Best Fit Method for the Three Parameter Weibull Distribution: Analysis of Tensile and Bend Specimens with Volume or Surface Flaw Failure

NASA Technical Reports Server (NTRS)

Gross, Bernard

1996-01-01

Material characterization parameters obtained from naturally flawed specimens are necessary for reliability evaluation of non-deterministic advanced ceramic structural components. The least squares best fit method is applied to the three parameter uniaxial Weibull model to obtain the material parameters from experimental tests on volume or surface flawed specimens subjected to pure tension, pure bending, four point or three point loading. Several illustrative example problems are provided.

Using Ultrasonic Lamb Waves To Measure Moduli Of Composites

NASA Technical Reports Server (NTRS)

Kautz, Harold E.

1995-01-01

Measurements of broad-band ultrasonic Lamb waves in plate specimens of ceramic-matrix/fiber and metal-matrix/fiber composite materials used to determine moduli of elasticity of materials. In one class of potential applications of concept, Lamb-wave responses of specimens measured and analyzed at various stages of thermal and/or mechanical processing to determine effects of processing, without having to dissect specimens. In another class, structural components having shapes supporting propagation of Lamb waves monitored ultrasonically to identify signs of deterioration and impending failure.

Dynamic Failure Processes Under Confining Stress in AlON, a Transparent Polycrystalline Ceramic

DTIC Science & Technology

2009-09-01

in a prismatic specimen along one of the three specimen axes, the dynamic loading is imposed (using MKB) along the second specimen axis and the third ...AlON are generally comparable to those of α-Al2O3. Owing to its optically isotropic cubic crystal structure, fully dense, polycrystalline bodies can...illustrated in indentation experiments on Al2O3 [46]) or under tribological loading conditions. During indentation, the region beneath the indenter is

Closed form expressions for crack mouth displacements and stress intensity factors for chevron notched short bar and short rod specimens based on experimental compliance measurements

NASA Technical Reports Server (NTRS)

Bubsey, R. T.; Orange, T. W.; Pierce, W. S.; Shannon, J. L., Jr.

1992-01-01

A set of equations are presented describing certain fracture mechanics parameters for chevron notch bar and rod specimens. They are developed by fitting compliance calibration data reported earlier. The equations present the various parameters in their most useful forms. The data encompass the entire range of the specimen geometries most commonly used. Their use will facilitate the testing and analysis of brittle metals, ceramics, and glasses.

Mechanical behavior of a ceramic matrix composite material. M.S. Thesis Final Report

NASA Technical Reports Server (NTRS)

Grosskopf, Paul P.; Duke, John C., Jr.

1991-01-01

Monolithic ceramic materials have been used in industry for hundreds of years. These materials have proven their usefulness in many applications, yet, their potential for critical structural applications is limited. The existence of an imperfection in a monolithic ceramic on the order of several microns in size may be critical, resulting in catastrophic failure. To overcome this extreme sensitivity to small material imperfections, reinforced ceramic materials were developed. A ceramic matrix which has been reinforced with continuous fibers is not only less sensitive to microscopic flaws, but is also able to sustain significant damage without suffering catastrophic failure. A borosilicate glass reinforced with several layers of plain weave silicon carbide cloth (Nicalon) was studied. The mechanical testing which was performed included both flexural and tensile loading configurations. This testing was done not only to determine the material properties, but also to initiate a controlled amount of damage within each specimen. Several nondestructive testing techniques, including acousto-ultrasonics (AU), were performed on the specimens periodically during testing. The AU signals were monitored through the use of an IBM compatible personal computer with a high speed data acquisition board. Software was written which manipulates the AU signals in both the time and frequency domains, resulting in quantitative measures of the mechanical response of the material. The measured AU parameters are compared to both the mechanical test results and data from other nondestructive methods including ultrasonic C-scans and penetrant enhanced x ray radiography.

Micromorphological characterization of adhesive interface of sound dentin and total-etch and self-etch adhesives.

PubMed

Drobac, Milan; Stojanac, Igor; Ramić, Bojana; Premović, Milica; Petrović, Ljubomir

2015-01-01

The ultimate goal in restorative dentistry has always been to achieve strong and permanent bond between the dental tissues and filling materials. It is not easy to achieve this task because the bonding process is different for enamel and dentin-dentin is more humid and more organic than enamel. It is moisture and organic nature of dentin that make this hard tissue very complex to achieve adhesive bond. One of the first and most widely used tools for examining the adhesive bond between hard dental tissues and composite restorative materials is scanning electron microscopy. The aim of this study was scanning electron microscopy analyzes the interfacial micro morphology of total-etch and self-etch adhesives. Micro morphological characteristics of interface between total-etch adhesive (Prime & Bond NT) in combination with the corresponding composite (Ceram X Mono) were compared with those of self-etching adhesive (AdheSE One) in, combination with the corresponding composite (Tetric EvoCeram). The specimens were observed under 1000 x magnification of scanning electron microscopy (JEOL, JSM-6460 Low Vacuum). Measurement of the thickness of the hybrid layer of the examined com posite systems was performed with the software of the device used (NIH Image Analyser). Micromorphological analysis of interface showed that the hybrid layer in sound dentin was well formed, its average thickness being 2.68 microm, with a large number of resin tags and a large amount of lateral branches for specimens with a composite system Prime & Bond NT-Ceram X Mono. However, the specimens' with composite systems Adhese One-Tetric EvoCeram did not show the presence of hybrid layer and the resin tags were poorly represented. The results of this study suggest that total-etch adhesives bond better with sound dentin than self-etch adhesive.

The color masking ability of a zirconia ceramic on the substrates with different values.

PubMed

Tabatabaian, Farhad; Javadi Sharif, Mahdiye; Massoumi, Farhood; Namdari, Mahshid

2017-01-01

Background. The color masking ability of a restoration plays a significant role in coveringa discolored substructure; however, this optical property of zirconia ceramics has not been clearly determined yet. The aim of this in vitro study was to evaluate the color masking ability of a zirconia ceramic on substrates with different values. Methods. Ten zirconia disk specimens,0.5 mm in thickness and 10 mm in diameter, were fabricated by a CAD/CAM system. Four substrates with different values were prepared, including: white (control), light grey, dark grey, and black. The disk specimens were placed over the substratesfor spectrophotometric measurements. A spectrophotometer measured the L * , a * , and b * color attributes of the specimens. Additionally, ΔE values were calculated to determine the color differences between each group and the control,and were then compared with the perceptional threshold of ΔE=2.6. Repeated-measures ANOVA, Bonferroni, and one-sample t-test were used to analyze data. All the tests were carried out at 0.05 level of significance. Results. The means and standard deviations of ΔE values for the three groups of light grey, dark grey and black were 9.94±2.11, 10.40±2.09, and 13.34±1.77 units, respectively.Significant differences were detected between the groups in the ΔE values (P<0.0001).The ΔE values in all the groups were more than the predetermined perceptional threshold(ΔE>2.6) (P<0.0001). Conclusion. Within the limitations of this study, it was concluded that the tested zirconia ceramic did not exhibit sufficient color masking ability to hide the grey and black substrates.

Fracture resistance measurement of advanced ceramics at elevated-temperatures using Chevron-notched specimens and other novel techniques

DOE Office of Scientific and Technical Information (OSTI.GOV)

Jenkins, M.G.

1995-12-31

The quasi-static fracture behavior of advanced ceramics was assessed in the temperature range of 20{degrees} to 1400{degrees}C. Chevron-notched, three-point flexure specimens and a laser-based CMOD measurement systems were used in testing. Types of materials characterized included monolithic ceramics (SiC, Si{sub 3}N{sub 4}, MgAl{sub 2}O{sub 4}), self-reinforced monoliths (acicular-grained Si{sub 3}N{sub 4}, acicular grained mullite), and ceramic matrix composites (SiC whisker/Al{sub 2}O{sub 3} matrix, TiB{sub 2} particulate/SiC matrix, SiC fibre/CVI SiC matrix, Al{sub 2}O{sub 3} fibre/CVI SiC matrix). Fracture resistance behaviour of the materials was quantified as three distinct regimes of the fracture histories. At crack initiation, the apparent fracture toughnessmore » was evaluated as the critical stress intensity factor, K{sub IC}. During stable crack propagation, the crack growth resistance was characterized by the instantaneous strain energy release rate, G{sub R} using a compliance method assuming linear-elastic unloading to calculate the effective crack lengths. At final fracture, the complete fracture process was quantified using the work-of-fracture, WOF, which can be equated to the fracture surface energy for linearelastic materials. Results indicate that the chevron-notched, three-point flexure specimen facilitates the study of fracture behavior in a wide range of brittle and quasi-brittle materials at elevated temperatures. The unique features of the chevron geometry, which are automatic, in-situ crack initiation and inherent stable crack growth, are crucial to the successful evaluation of the fracture tests.« less

Fracture Resistance of Lithium Disilicate Ceramics Bonded to Enamel or Dentin Using Different Resin Cement Types and Film Thicknesses.

PubMed

Rojpaibool, Thitithorn; Leevailoj, Chalermpol

2017-02-01

To investigate the influence of cement film thickness, cement type, and substrate (enamel or dentin) on ceramic fracture resistance. One hundred extracted human third molars were polished to obtain 50 enamel and 50 dentin specimens. The specimens were cemented to 1-mm-thick lithium disilicate ceramic plates with different cement film thicknesses (100 and 300 μm) using metal strips as spacers. The cements used were etch-and-rinse (RelyX Ultimate) and self-adhesive (RelyX U200) resin cements. Compressive load was applied on the ceramic plates using a universal testing machine, and fracture loads were recorded in Newtons (N). Statistical analysis was performed by multiple regression (p < 0.05). Representative specimens were evaluated by scanning electron microscopy to control the cement film thickness. The RelyX Ultimate group with a cement thickness of 100 μm cemented to enamel showed the highest mean fracture load (MFL; 1591 ± 172.59 N). The RelyX Ultimate groups MFLs were significantly higher than the corresponding RelyX U200 groups (p < 0.05), and thinner film cement demonstrated a higher MFL than thicker films (p < 0.05). Bonding to dentin resulted in lower MFL than with enamel (p < 0.001). Higher fracture loads were related to thinner cement film thickness and RelyX Ultimate resin cement. Bonding to dentin resulted in lower fracture loads than bonding to enamel. Reduced resin film thickness could reduce lithium disilicate restoration fracture. Etch-and-rinse resin cements are recommended for cementing on either enamel or dentin, compared with self-adhesive resin cement, for improved fracture resistance. © 2015 by the American College of Prosthodontists.

Sandblasting and silica coating of a glass-infiltrated alumina ceramic: volume loss, morphology, and changes in the surface composition.

PubMed

Kern, M; Thompson, V P

1994-05-01

Silica coating can improve bonding of resin to glass-infiltrated aluminum oxide ceramic (In-Ceram), and sandblasting is a pretreatment to thermal silica coating (Silicoater MD system) or a tribochemical coating process (Rocatec system). This study evaluated the effects of sandblasting and coating techniques on volume loss, surface morphology, and surface composition of In-Ceram ceramic. Volume loss through sandblasting was 36 times less for In-Ceram ceramic compared with a feldspathic glass ceramic (IPS-Empress), and sandblasting of In-Ceram ceramic did not change its surface composition. After tribochemical coating with the Rocatec system, a layer of small silica particles remained that elevated the silica content to 19.7 weight percentage (energy-dispersive spectroscopy). Ultrasonic cleaning removed loose silica particles from the surface and decreased the silica content to 15.8 weight percentage, which suggested firm attachment of most of the silica layer to the surface. After treatment with the Silicoater MD system, the silica content increased only slightly from that of the sandblasted specimen. The silica layer created by these systems differs greatly in both morphology and thickness, which could result in different bond strengths. Sandblasting of all ceramic clinical restorations with feldspathic glass materials should be avoided, but for In-Ceram ceramic the volume loss was within an acceptable range and similar to that of noble metals.

In vitro study of the effect of three hydrogen peroxide concentrations on the corrosion behavior and surface topography of alumina-reinforced dental ceramic.

PubMed

Abu-Eittah, Manal R; Mandour, Mona H

2011-10-01

This in vitro investigation studied the effect of three hydrogen peroxide (HP) concentrations (30%, 35%, 38% v/v) at two time intervals (1 and 2 hours) on the corrosion behavior and surface topography of a dental ceramic. A total of 62 Vitadur Alpha discs were constructed following manufacturer instructions. Specimens were divided into four main groups (n = 8). Group 1 (control): specimens were immersed in 4% acetic acid for 18 hours at 80°C. Groups 2, 3, and 4: specimens were immersed in 30%, 35%, and 38% HP concentrations, respectively. Each of the three groups was divided into two subgroups (a and b) according to the immersion time (1 and 2 hours, respectively). Specimens of subgroup a were further immersed in 4% acetic acid for 18 hours at 80°C and were designated as subgroup c. The corrosion behavior of the ceramic specimens were tested by solution analysis using the atomic absorption method, weight loss percent, and corrosion rate. Surface topography was investigated by surface roughness (Ra) measurements and scanning electron microscopy (SEM). Results were statistically analyzed. There was a significant increase for ions leached with the increase in time of immersion for all ions at 35% and 38% HP, while at 30% HP, ions of K(+) , Al(3+) , and Si(4+) did not increase significantly with time. The results also showed that at a fixed time of immersion, all ions released were dependent on the increase of HP concentration except for Al(3+) ions (p < 0.05). The combined treatment of specimens with HP followed by acetic acid had a significant effect on the increase of ions leached (p < 0.05). The surface roughness values for all specimens increased significantly with time of immersion as well as with the increase in concentration of HP (p < 0.05). These results were confirmed with SEM. The amount of released ions is directly proportional to HP concentration and time of immersion. Specimens exposed to both HP and acetic acid showed increased weight loss and a higher corrosion rate than those exposed to acetic acid only. Surface roughness values were time and HP concentration dependent. © 2011 by The American College of Prosthodontists.

Contact fatigue mechanisms as a function of crystal aspect ratio in baria-silicate glass ceramics

NASA Astrophysics Data System (ADS)

Suputtamongkol, Kallaya

2003-10-01

Ceramic materials are potentially useful for dental applications because of their esthetic potential and biocompatibility. However, the existence of fatigue damage in ceramics raises considerable concern regarding its effect on the life prediction of dental prostheses. During normal mastication, dental restorations are subjected to repeated loading more than a thousand times per day and relatively high clinical failure rates for ceramic prostheses have been reported. To simulate the intraoral loads, Hertzian indentation loading was used in this study to characterize the fatigue failure mechanisms of ceramic materials using clinically relevant parameters. The baria-silicate system was chosen because of the nearly identical composition between the crystal and the glass matrix. Little or no residual stress is expected from the elastic modulus and thermal expansion mismatches between the two phases. Crystallites with different aspect ratios can also be produced by controlled heat treatment schedules. The objective of this study was to characterize the effect of crystal morphology on the fatigue mechanisms of bariasilicate glass-ceramics under clinically relevant conditions. The results show that the failure of materials with a low toughness such as baria-silicate glass (0.7 MPa•m1/2) and glass-ceramic with an aspect ratio of 3/1 (1.3 MPa•m1/2) initiated from a cone crack developed during cyclic loading for 103 to 105 cycles. The mean strength values of baria-silicate glass and glass-ceramic with an aspect ratio of 3/1 decreased significantly as a result of the presence of a cone crack. Failure of baria-silicate glass-ceramics with an aspect ratio of 8/1 (Kc = 2.1 MPa•m1/2) was initiated from surface flaws caused by either polishing or cyclic loading. The gradual decrease of fracture stress was observed in specimens with an aspect ratio of 8/1 after loading in air for 103 to 10 5 cycles. A reduction of approximately 50% in fracture stress levels was found for specimens with an aspect ratio of 8/1 after loading for 10 5 cycles in deionized water. The mechanisms for cyclic fatigue crack propagation in baria-silicate glass-ceramics are similar to those observed under quasi-static loading conditions. An intergranular fracture path was observed in glass-ceramics with an aspect ratio of 3/1. For an aspect ratio of 8/1, a transgranular fracture mode was dominant.

Influence of different crosshead speeds on diametral tensile strength of a methacrylate based resin composite: An in-vitro study

PubMed Central

Sood, Anubhav; Ramarao, Sathyanarayanan; Carounanidy, Usha

2015-01-01

Aim: The aim was to evaluate the influence of different crosshead speeds on diametral tensile strength (DTS) of a resin composite material (Tetric N-Ceram). Materials and Methods: The DTS of Tetric N-Ceram was evaluated using four different crosshead speeds 0.5 mm/min (DTS 1), 1 mm/min (DTS 2), 5 mm/min (DTS 3), 10 mm/min (DTS 4). A total of 48 specimens were prepared and divided into four subgroups with 12 specimens in each group. Specimens were made using stainless steel split custom molds of dimensions 6 mm diameter and 3 mm height. The specimens were stored in distilled water at room temperature for 24 h. Universal testing machine was used and DTS values were calculated in MPa. Results: Analysis of variance was used to compare the four groups. Higher mean DTS value was recorded in DTS 2 followed by DTS 4, DTS 1, and DTS 3, respectively. However, the difference in mean tensile strength between the groups was not statistically significant (P > 0.05). Conclusion: The crosshead speed variation between 0.5 and 10 mm/min does not seem to influence the DTS of a resin composite. PMID:26069407

Influence of different crosshead speeds on diametral tensile strength of a methacrylate based resin composite: An in-vitro study.

PubMed

Sood, Anubhav; Ramarao, Sathyanarayanan; Carounanidy, Usha

2015-01-01

The aim was to evaluate the influence of different crosshead speeds on diametral tensile strength (DTS) of a resin composite material (Tetric N-Ceram). The DTS of Tetric N-Ceram was evaluated using four different crosshead speeds 0.5 mm/min (DTS 1), 1 mm/min (DTS 2), 5 mm/min (DTS 3), 10 mm/min (DTS 4). A total of 48 specimens were prepared and divided into four subgroups with 12 specimens in each group. Specimens were made using stainless steel split custom molds of dimensions 6 mm diameter and 3 mm height. The specimens were stored in distilled water at room temperature for 24 h. Universal testing machine was used and DTS values were calculated in MPa. Analysis of variance was used to compare the four groups. Higher mean DTS value was recorded in DTS 2 followed by DTS 4, DTS 1, and DTS 3, respectively. However, the difference in mean tensile strength between the groups was not statistically significant (P > 0.05). The crosshead speed variation between 0.5 and 10 mm/min does not seem to influence the DTS of a resin composite.

Thermal Conductivity of Ceramic Thermal Barrier and Environmental Barrier Coating Materials

NASA Technical Reports Server (NTRS)

Zhu, Dong-Ming; Bansal, Narottam P.; Lee, Kang N.; Miller, Robert A.

2001-01-01

Thermal barrier and environmental barrier coatings (TBC's and EBC's) have been developed to protect metallic and Si-based ceramic components in gas turbine engines from high temperature attack. Zirconia-yttria based oxides and (Ba,Sr)Al2Si2O8(BSAS)/mullite based silicates have been used as the coating materials. In this study, thermal conductivity values of zirconia-yttria- and BSAS/mullite-based coating materials were determined at high temperatures using a steady-state laser heat flux technique. During the laser conductivity test, the specimen surface was heated by delivering uniformly distributed heat flux from a high power laser. One-dimensional steady-state heating was achieved by using thin disk specimen configuration (25.4 mm diam and 2 to 4 mm thickness) and the appropriate backside air-cooling. The temperature gradient across the specimen thickness was carefully measured by two surface and backside pyrometers. The thermal conductivity values were thus determined as a function of temperature based on the 1-D heat transfer equation. The radiation heat loss and laser absorption corrections of the materials were considered in the conductivity measurements. The effects of specimen porosity and sintering on measured conductivity values were also evaluated.

Freckle Defect Formation near the Casting Interfaces of Directionally Solidified Superalloys

PubMed Central

Hong, Jianping; Ma, Dexin; Wang, Jun; Wang, Fu; Sun, Baode; Dong, Anping; Li, Fei; Bührig-Polaczek, Andreas

2016-01-01

Freckle defects usually appear on the surface of castings and industrial ingots during the directional solidification process and most of them are located near the interface between the shell mold and superalloys. Ceramic cores create more interfaces in the directionally solidified (DS) and single crystal (SX) hollow turbine blades. In order to investigate the location of freckle occurrence in superalloys, superalloy CM247 LC was directionally solidified in an industrial-sized Bridgman furnace. Instead of ceramic cores, Alumina tubes were used inside of the casting specimens. It was found that freckles occur not only on the casting external surfaces, but also appear near the internal interfaces between the ceramic core and superalloys. Meanwhile, the size, initial position, and area of freckle were investigated in various diameters of the specimens. The initial position of the freckle chain reduces when the diameter of the rods increase. Freckle area follows a linear relationship in various diameters and the average freckle fraction is 1.1% of cross sectional area of casting specimens. The flow of liquid metal near the interfaces was stronger than that in the interdendritic region in the mushy zone, and explained why freckle tends to occur on the outer or inner surfaces of castings. This new phenomenon suggests that freckles are more likely to occur on the outer or inner surfaces of the hollow turbine blades. PMID:28774050

Freckle Defect Formation near the Casting Interfaces of Directionally Solidified Superalloys.

PubMed

Hong, Jianping; Ma, Dexin; Wang, Jun; Wang, Fu; Sun, Baode; Dong, Anping; Li, Fei; Bührig-Polaczek, Andreas

2016-11-16

Freckle defects usually appear on the surface of castings and industrial ingots during the directional solidification process and most of them are located near the interface between the shell mold and superalloys. Ceramic cores create more interfaces in the directionally solidified (DS) and single crystal (SX) hollow turbine blades. In order to investigate the location of freckle occurrence in superalloys, superalloy CM247 LC was directionally solidified in an industrial-sized Bridgman furnace. Instead of ceramic cores, Alumina tubes were used inside of the casting specimens. It was found that freckles occur not only on the casting external surfaces, but also appear near the internal interfaces between the ceramic core and superalloys. Meanwhile, the size, initial position, and area of freckle were investigated in various diameters of the specimens. The initial position of the freckle chain reduces when the diameter of the rods increase. Freckle area follows a linear relationship in various diameters and the average freckle fraction is 1.1% of cross sectional area of casting specimens. The flow of liquid metal near the interfaces was stronger than that in the interdendritic region in the mushy zone, and explained why freckle tends to occur on the outer or inner surfaces of castings. This new phenomenon suggests that freckles are more likely to occur on the outer or inner surfaces of the hollow turbine blades.

Determination of elastic modulus of ceramics using ultrasonic testing

NASA Astrophysics Data System (ADS)

Sasmita, Firmansyah; Wibisono, Gatot; Judawisastra, Hermawan; Priambodo, Toni Agung

2018-04-01

Elastic modulus is important material property on structural ceramics application. However, bending test as a common method for determining this property require particular specimen preparation. Furthermore, elastic modulus of ceramics could vary because it depends on porosity content. For structural ceramics industry, such as ceramic tiles, this property is very important. This drives the development of new method to improve effectivity or verification method as well. In this research, ultrasonic testing was conducted to determine elastic modulus of soda lime glass and ceramic tiles. The experiment parameter was frequency of probe (1, 2, 4 MHz). Characterization of density and porosity were also done for analysis. Results from ultrasonic testing were compared with elastic modulus resulted from bending test. Elastic modulus of soda-lime glass based on ultrasonic testing showed excellent result with error 2.69% for 2 MHz probe relative to bending test result. Testing on red and white ceramic tiles were still contained error up to 41% and 158%, respectively. The results for red ceramic tile showed trend that 1 MHz probe gave better accuracy in determining elastic modulus. However, testing on white ceramic tile showed different trend. It was due to the presence of porosity and near field effect.

Degree of conversion and bond strength of resin-cements to feldspathic ceramic using different curing modes.

PubMed

Novais, Veridiana Resende; Raposo, Luís Henrique Araújo; Miranda, Rafael Resende de; Lopes, Camila de Carvalho Almança; Simamoto, Paulo Cézar; Soares, Carlos José

2017-01-01

The aim of this study was to assess the performance of resin cements when different curing modes are used, by evaluating the degree of conversion and bond strength to a ceramic substrate. Three resin cements were evaluated, two dual-cured (Variolink II and RelyX ARC) and one light-cured (Variolink Veneer). The dual-cured resin cements were tested by using the dual activation mode (base and catalyst) and light-activation mode (base paste only). For degree of conversion (DC) (n=5), a 1.0 mm thick feldspathic ceramic disc was placed over the resin cement specimens and the set was light activated with a QTH unit. After 24 h storage, the DC was measured with Fourier transform infrared spectroscopy (FTIR). For microshear bond strength testing, five feldspathic ceramic discs were submitted to surface treatment, and three cylindrical resin cement specimens were bonded to each ceramic surface according to the experimental groups. After 24 h, microshear bond testing was performed at 0.5 mm/min crosshead speed until the failure. Data were submitted to one-way ANOVA followed by Tukey test (p<0.05). Scanning electron microscopy (SEM) was used for classifying the failure modes. Higher DC and bond strength values were shown by the resin cements cured by using the dual activation mode. The Variolink II group presented higher DC and bond strength values when using light-activation only when compared with the Variolink Veneer group. The base paste of dual-cured resin cements in light-activation mode can be used for bonding translucent ceramic restorations of up to or less than 1.0 mm thick.

Effect of laser welding on the titanium ceramic tensile bond strength.

PubMed

Galo, Rodrigo; Ribeiro, Ricardo Faria; Rodrigues, Renata Cristina Silveira; Pagnano, Valéria de Oliveira; Mattos, Maria da Glória Chiarello de

2011-08-01

Titanium reacts strongly with elements, mainly oxygen at high temperature. The high temperature of titanium laser welding modifies the surface, and may interfere on the metal-ceramic tensile bond strength. The influence of laser welding on the titanium-ceramic bonding has not yet been established. The purpose of this in vitro study was to analyze the influence of laser welding applied to commercially pure titanium (CpTi) substructure on the bond strength of commercial ceramic. The influence of airborne particle abrasion (Al2O3) conditions was also studied. Forty CpTi cylindrical rods (3 mm x 60 mm) were cast and divided into 2 groups: with laser welding (L) and without laser welding (WL). Each group was divided in 4 subgroups, according to the size of the particles used in airborne particle abrasion: A - Al2O3 (250 µm); B - Al2O3 (180 µm); C - Al2O3 (110 µm); D - Al2O3 (50 µm). Ceramic rings were fused around the CpTi rods. Specimens were invested and their tensile strength was measured at fracture with a universal testing machine at a crosshead speed of 2.0 mm/min and 200 kgf load cell. Statistical analysis was carried out with analysis of variance and compared using the independent t test (p<0.05). Significant differences were found among all subgroups (p<0.05). The highest and the lowest bond strength means were recorded in subgroups WLC (52.62 MPa) and LD (24.02 MPa), respectively. Airborne particle abrasion yielded significantly lower bond strength as the Al2O3 particle size decreased. Mechanical retention decreased in the laser-welded specimens, i.e. the metal-ceramic tensile bond strength was lower.

Does 8-methacryloxyoctyl trimethoxy silane (8-MOTS) improve initial bond strength on lithium disilicate glass ceramic?

PubMed

Maruo, Yukinori; Nishigawa, Goro; Yoshihara, Kumiko; Minagi, Shogo; Matsumoto, Takuya; Irie, Masao

2017-03-01

Dental ceramic surfaces are modified with silane coupling agents, such as γ-methacryloxypropyl trimethoxy silane (γ-MPTS), to improve bond strength. For bonding between lithium disilicate glass ceramic and resin cement, the objective was to investigate if 8-methacryloxyoctyl trimethoxy silane (8-MOTS) could yield a similar performance as the widely used γ-MPTS. One hundred and ten lithium disilicate glass ceramic specimens were randomly divided into 11 groups (n=10) according to pretreatment regime. All specimens were pretreated with a different solution composed of one or a combination of these agents: 10 or 20wt% silane coupling agent of γ-MPTS or 8-MOTS, followed by a hydrolysis solution of acetic acid or 10-methacryloyloxydecyl dihydrogen phosphate (10-MDP). Each pretreated surface was luted to a stainless steel rod of 3.6mm diameter and 2.0mm height with resin cement. Shear bond strength between ceramic and cement was measured after 24-h storage in 37°C distilled water. 8-MOTS produced the same bonding performance as γ-MPTS. Both silane coupling agents significantly increased the bond strength of resin cement, depending on their concentration. When activated by 10-MDP hydrolysis solution, 20wt% concentration produced the highest values (γ-MPTS: 24.9±5.1MPa; 8-MOTS: 24.6±7.4MPa). Hydrolysis with acetic acid produced lower bond strengths than with 10-MDP. Silane coupling pretreatment with 8-MOTS increased the initial bond strength between lithium disilicate glass ceramic and resin cement, rendering the same bonding effect as the conventional γ-MPTS. Copyright © 2016 The Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Wear Potential of Dental Ceramics and its Relationship with Microhardness and Coefficient of Friction.

PubMed

Freddo, Rafael Augusto; Kapczinski, Myriam Pereira; Kinast, Eder Julio; de Souza Junior, Oswaldo Baptista; Rivaldo, Elken Gomes; da Fontoura Frasca, Luis Carlos

2016-10-01

To evaluate, by means of pin-on-disk testing, the wear potential of different dental ceramic systems as it relates to friction parameters, surface finish, and microhardness. Three groups of different ceramic systems (Noritake EX3, Eris, Empress II) with 20 disks each (10 glazed, 10 polished) were used. Vickers microhardness (Hv) was determined with a 200-g load for 30 seconds. Friction coefficients (μ) were determined by pin-on-disk testing (5 N load, 600 seconds, and 120 rpm). Wear patterns were assessed by scanning electron microscopy (SEM). The results were analyzed using one-way ANOVA and Tukey's test, with the significance level set at α = 0.05. The coefficients of friction were as follows: Noritake EX3 0.28 ± 0.12 (polished), 0.33 ± 0.08 (glazed); Empress II 0.38 ± 0.08 (polished), 0.45 ± 0.05 (glazed); Eris 0.49 ± 0.05 (polished), 0.49 ± 0.06 (glazed). Microhardness measurements were as follows: Noritake EX3 530.7 ± 8.7 (polished), 525.9 ± 6.2 (glazed); Empress II 534.1 ± 8 (polished), 534.7 ± 4.5 (glazed); Eris, 511.7 ± 6.5 (polished), 519.5 ± 4.1 (glazed). The polished and glazed Noritake EX3 and polished and glazed Eris specimens showed statistically different friction coefficients. SEM image analysis revealed more surface changes, such as small cracks and grains peeling off, in glazed ceramics. Wear potential may be related to the coefficient of friction in Noritake ceramics, which had a lower coefficient than Eris ceramics. Within-group analysis showed no differences in polished or glazed specimens. The differences observed were not associated with microhardness. © 2015 by the American College of Prosthodontists.

Effect of Hydrofluoric Acid Concentration on Resin Adhesion to a Feldspathic Ceramic.

PubMed

Venturini, Andressa Borin; Prochnow, Catina; Rambo, Dagma; Gundel, Andre; Valandro, Luiz Felipe

2015-08-01

To evaluate the effect of different concentrations of hydrofluoric acid (HF) on the contact angle and the resin bond strength durability to feldspathic ceramic. To evaluate the contact angles of distilled water on etched feldspathic ceramic, 25 specimens (12×10×2.4 mm) of VitaBlocks Mark II were used, divided into 5 groups (n=5): one unconditioned control (UC) group with no ceramic surface treatment, and 4 other groups that were etched for 60 s with different concentrations of HF: 1% (HF1), 3% (HF3), 5% (HF5) and 10% (HF10). The bond testing utilized 40 ceramic blocks (12×10×4 mm) that were fabricated and subjected to the same surface treatments as previously mentioned (excluding the control). The etched surfaces were silanized and resin cement was applied. After 24 h, the blocks were sectioned to produce bar specimens that were divided into two groups, non-aged (immediate testing) and aged (storage for 230 days+12,000 thermocycles at 5°C and 55°C), and subjected to microtensile testing (μTBS). Micromorphogical analysis of the treated surfaces was also performed (atomic force and scanning electron microscopy). One-way ANOVA and Tukey's tests were applied for data analysis. UC had the highest contact angle (61.4°), whereas HF10 showed the lowest contact angle (17.5°). In non-aged conditions, different acids promoted statistically similar bond strengths (14.2 to 15.7 MPa) (p>0.05); in terms of bond durability, only the bond strength of the HF1 group presented a statistically significant decrease comparing before and after aging (14.5 to 10.2 MPa). When etched with 3%, 5%, or 10% hydrofluoric acid, the ceramic tested showed stable resin adhesion after long-term aging.

Effect of the microstructure on the lifetime of dental ceramics.

PubMed

Borba, Márcia; de Araújo, Maico D; Fukushima, Karen A; Yoshimura, Humberto N; Cesar, Paulo F; Griggs, Jason A; Della Bona, Alvaro

2011-07-01

To evaluate the effect of the microstructure on the Weibull and slow crack growth (SCG) parameters and on the lifetime of three ceramics used as framework materials for fixed partial dentures (FPDs) (YZ - Vita In-Ceram YZ; IZ - Vita In-Ceram Zirconia; AL - Vita In-Ceram AL) and of two veneering porcelains (VM7 and VM9). Bar-shaped specimens were fabricated according to the manufacturer's instructions. Specimens were tested in three-point flexure in 37°C artificial saliva. Weibull analysis (n=30) and a constant stress-rate test (n=10) were used to determine the Weibull modulus (m) and SCG coefficient (n), respectively. Microstructural and fractographic analyzes were performed using SEM. ANOVA and Tukey's test (α=0.05) were used to statistically analyze data obtained with both microstructural and fractographic analyzes. YZ and AL presented high crystalline content and low porosity (0.1-0.2%). YZ had the highest characteristic strength (σ(0)) value (911MPa) followed by AL (488MPa) and IZ (423MPa). Lower σ(0) values were observed for the porcelains (68-75MPa). Except for IZ and VM7, m values were similar among the ceramic materials. Higher n values were found for YZ (76) and AL (72), followed by IZ (54) and the veneering materials (36-44). Lifetime predictions showed that YZ was the material with the best mechanical performance. The size of the critical flaw was similar among the framework materials (34-48μm) and among the porcelains (75-86μm). The microstructure influenced the mechanical and SCG behavior of the studied materials and, consequently, the lifetime predictions. Copyright © 2011 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

The influence of structure depth on image blurring of micrometres-thick specimens in MeV transmission electron imaging.

PubMed

Wang, Fang; Sun, Ying; Cao, Meng; Nishi, Ryuji

2016-04-01

This study investigates the influence of structure depth on image blurring of micrometres-thick films by experiment and simulation with a conventional transmission electron microscope (TEM). First, ultra-high-voltage electron microscope (ultra-HVEM) images of nanometer gold particles embedded in thick epoxy-resin films were acquired in the experiment and compared with simulated images. Then, variations of image blurring of gold particles at different depths were evaluated by calculating the particle diameter. The results showed that with a decrease in depth, image blurring increased. This depth-related property was more apparent for thicker specimens. Fortunately, larger particle depth involves less image blurring, even for a 10-μm-thick epoxy-resin film. The quality dependence on depth of a 3D reconstruction of particle structures in thick specimens was revealed by electron tomography. The evolution of image blurring with structure depth is determined mainly by multiple elastic scattering effects. Thick specimens of heavier materials produced more blurring due to a larger lateral spread of electrons after scattering from the structure. Nevertheless, increasing electron energy to 2MeV can reduce blurring and produce an acceptable image quality for thick specimens in the TEM. Copyright © 2016 Elsevier Ltd. All rights reserved.

Electrical properties of palladium-doped CaCu3Ti4O12 ceramics

NASA Astrophysics Data System (ADS)

Singh, Arashdeep; Md Mursalin, Sk.; Rana, P.; Sen, Shrabanee

2015-09-01

The effect of doping palladium (Pd) at the Cu site of CaCu3Ti4O12 powders (CCPTO) synthesized by sol-gel technique on electrical properties was studied. XRD analysis revealed the formation of CCTO and CCPTO ceramics with some minor quantities of impurities. SEM micrographs revealed that the grain size decreased with Pd doping. TEM micrographs of CCPTO powder showed the formation of irregular-shaped particles of ~40 nm. The dielectric constant and dielectric loss showed a significant enhancement with Pd doping. A significant decrease in grain-boundary resistance with Pd doping was ascertained by impedance spectroscopy study.

Study of fracture toughness of ZrO2 ceramics

NASA Astrophysics Data System (ADS)

Deryugin, Yevgeny; Narkevich, Natalya; Vlasov, Ilya; Panin, Victor; Danilenko, Igor; Schmauder, Siegfried

2017-12-01

The fracture toughness characteristics of ZrO2ceramics were determined experimentally using an original technique of wedging small-sized chevron notch specimens developed at the Institute of Strength Physics and Materials Science SB RAS (Russia) in the laboratory of physical mesomechanics of materials and non-destructive testing. Measurements have shown that inelastic displacements can be more than 22% of the total displacement of the consoles by the time of the specimen failure. The effect of the Y2O3 stabilizer on the critical stress intensity factor KIc was verified. It was shown that an increase in the Y2O3 stabilizer content from 3 to 8% significantly decreases the fracture toughness. The stress intensity factor KIc falls within the range from 5.7 to 2.35 MPa m1/2.

Fracture Behavior of Ceramics Under Displacement Controlled Loading

NASA Technical Reports Server (NTRS)

Calomino, Anthony; Brewer, David; Ghosn, Louis

1994-01-01

A Mode I fracture specimen and loading method has been developed which permits the observation of stable crack extension in monolithic and in situ toughened ceramics. The developed technique was used to conduct room temperature tests on commercial grade alumina (Coors' AD-995) and silicon nitride (Norton NC-132). The results of these tests are reported. Crack growth for the alumina remained subcritical throughout testing revealing possible effects of environmental stress corrosion. The crack growth resistance curve for the alumina is presented. The silicon nitride tests displayed a series of stable (slow) crack growth segments interrupted by dynamic (rapid) crack extension. Crack initiation and arrest stress intensity factors, K(sub Ic) and K(sub Ia), for silicon nitride are reported. The evolution of the specimen design through testing is briefly discussed.

Fracture toughness of fiber-reinforced glass ceramic and ceramic matrix composites

NASA Technical Reports Server (NTRS)

Stull, Kevin R.; Parvizi-Majidi, A.

1991-01-01

A fracture mechanics investigation of 2D woven Nicalon SiC/SiC and Nicalon SiC/LAS has been undertaken. An energy approach has been adopted to characterize and quantify the fracture properties of these materials. Chevron-notched bend specimens were tested in an edgewise configuration in which the crack propagated perpendicular to the ply direction. R-curves were obtained from repeated loading and unloading of specimens using several methods of data reduction. Values correconding to the plateau regions of the R-curves were taken as steady-state crack-growth resistance. These ranged from 37 to 63 kJ/sq m for 2D-SiC/LAS and 2.6 to 2.8 kJ/sq m for 2D-SiC/SiC composites.

A steady-state high-temperature apparatus for measuring thermal conductivity of ceramics

NASA Astrophysics Data System (ADS)

Filla, B. James

1997-07-01

A one-sided very-high-temperature guarded hot plate has been built to measure thermal conductivity of monolithic ceramics, ceramic composites, thermal barrier coatings, functional graded materials, and high-temperature metal alloys. It is an absolute, steady-state measurement device with an operational temperature range of 400-1400 K. Measurements are made in an atmosphere of low-pressure helium. Specimens examined in this apparatus are 70 mm in diameter, with thicknesses ranging between 1 and 8 mm. Optimal specimen thermal conductivities fall in the range of 0.5-30 W/(mK). Internal heated components are composed entirely of high-purity aluminum oxide, boron nitride, beryllium oxide, and fibrous alumina insulation board. Pure nickel and thermocouple-grade platinum-based alloys are the only metals used in the system. Apparatus design, modeling, and operation are described, along with the methods of data analysis that are unique to this system. An analysis of measurement uncertainty yields a combined measurement uncertainty of ±5%. Experimental measurements on several materials are presented to illustrate the precision and bias of the apparatus.

Ceramic susceptor for induction bonding of metals, ceramics, and plastics

NASA Technical Reports Server (NTRS)

Fox, Robert L.; Buckley, John D.

1991-01-01

A thin (.005) flexible ceramic susceptor (carbon) was discovered. It was developed to join ceramics, plastics, metals, and combinations of these materials using a unique induction heating process. Bonding times for laboratory specimens comparing state of the art technology to induction bonding were cut by a factor of 10 to 100 times. This novel type of carbon susceptor allows for applying heat directly and only to the bondline without heating the entire structure, supports, and fixtures of a bonding assembly. The ceramic (carbon film) susceptor produces molten adhesive or matrix material at the bond interface. This molten material flows through the perforated susceptor producing a fusion between the two parts to be joined, which in many instances has proven to be stronger than the parent material. Bonding can be accomplished in 2 minutes on areas submitted to the inductive heating. Because a carbon susceptor is used in bonding carbon fiber reinforced plastics and ceramics, there is no radar signature or return making it an ideal process for joining advanced aerospace composite structures.

Effect of engraving speeds of CO₂ laser irradiation on In-Ceram Alumina roughness: a pilot study.

PubMed

Ersu, Bahadır; Ersoy, Orkun; Yuzugullu, Bulem; Canay, Senay

2015-05-01

The aim of the study was to determine the effect of CO₂ laser on surface roughness of In-Ceram-Alumina-ceramic. Four aluminum-oxide ceramic disc specimens were prepared of In-Ceram Alumina. Discs received CO₂ laser irradiation with different engraving speeds (100, 400, 600 and 800 mm/min) as a surface treatment. The roughness of the surfaces was measured on digital elevation models reconstructed from stereoscopic images acquired by scanning-electron-microscope. Surface roughness data were analyzed with One-Way-Analysis-of-Variance at a significance level of p<0.05. There was no significant difference between the roughness values (p=0.82). Due to higher laser durations, partial melting signs were observed on the surfaces. Tearing, smearing and swelling occurred on melted surfaces. Swelling accompanying melting increased the surface roughness, while laser power was fixed and different laser engraving speeds were applied. Although different laser irradiation speeds did not affect the roughness of ceramic surfaces, swelling was observed which led to changes on surfaces.

Sintering and microstructure of silicon carbide ceramic with Y3Al5O12 added by sol-gel method*

PubMed Central

Guo, Xing-zhong; Yang, Hui

2005-01-01

Silicon carbide (SiC) ceramic with YAG (Y3Al5O12) additive added by sol-gel method was liquid-phase sintered at different sintering temperatures, and the sintering mechanism and microstructural characteristics of resulting silicon carbide ceramics were analyzed by X-ray diffraction (XRD), scanning electron microscopy (SEM) and elemental distribution of surface (EDS). YAG (yttrium aluminum garnet) phase formed before the sintering and its uniform distribution in the SiC/YAG composite powder decreased the sintering temperature and improved the densification of SiC ceramic. The suitable sintering temperature was 1860 °C with the specimen sintered at this temperature having superior sintering and mechanical properties, smaller crystal size and fewer microstructure defects. Three characteristics of improved toughness of SiC ceramic with YAG added by sol-gel method were microstructural densification, main-crack deflection and crystal ‘bridging’. PMID:15682507

[Cyclic fatigue of Vita mark II machinable ceramics under Hertzian's contact].

PubMed

Liu, Wei-Cai; Zhang, Zhi-Shen; Huang, Cheng-Min; Chao, Yong-Lie; Wan, Qian-Bing

2006-08-01

To investigate the cyclic fatigue modes of Vita mark II machinable ceramics under Hertzian's contact. Hertzian's contact technique (WC spheres r = 3.18 mm) was used to investigate the cyclic fatigue of Vita mark II machinable ceramic. All specimens were fatigued by cyclic loading in moist environment, furthermore, surviving strength was examined by three point test and morphology damage observation. In homogeneous Vita mark II machinable ceramics, two fatigue damage modes existed after cyclic loading with spheres under moist environment, including conventional tensile-driven cone cracking (brittle mode) and shear-driven microdamage accumulation (quasi-plastic mode). The latter generated radial cracks and deeply penetrating secondary cone crack. Initial strength degradation were caused by the cone cracks, subsequent and much more deleterious loss was caused by radial cracks. Cyclic fatigue modes of Vita mark II machinable ceramics includes brittle and quasi-plastic mode.

The Effects of Environment on the Interlaminar Shear Performance of an Oxide/Oxide Ceramic Matrix Composite at Elevated Temperature

DTIC Science & Technology

2007-06-01

of the N720/A specimen tested in creep at –4.0 MPa at 1200 °C in steam for 100 h. This specimen was unloaded, but remained at 1200°C for the...the N720/A specimen tested in creep at –4.0 MPa at 1200 °C in steam for 100 h. This specimen was unloaded, but remained at 1200°C for the duration...tested in creep at –4.0 MPa at 1200 °C in steam for 100 h. This specimen was unloaded, but remained at 1200°C for the duration of the test

The effect of air-abrasion and heat treatment on the fracture behavior of Y-TZP.

PubMed

Passos, Sheila P; Linke, Bernie; Major, Paul W; Nychka, John A

2015-09-01

This study evaluated how the flexural strength and fracture behavior of a zirconia-based ceramic (Y-TZP) were affected by pre- and post-sintering mechanical and thermal treatments. Treatments included sandblasting with different particle size and type (30μm SiO2; 50 and 110μm Al2O3) and thermal conditioning. Two hundred bar-shaped specimens of pre-sintered Y-TZP ceramic (Lava Frame, 3M) were prepared (specimen dimensions: 25mm length×4mm width×0.7mm thickness) and divided into three groups (before sintering, after sintering and after sintering with heating treatment). The before sintering group specimens were airborne-particle abraded prior to dense sintering. Specimens from the after sintering group were airborne-particle abraded after sintering. The after sintering with heating treatment group specimens were submitted to a heating procedure after airborne-particle abrasion. The controls were the specimens that were sintered and not treated with any conditioning procedures. The specimens from all experimental conditions were analyzed by SEM, CLSM and XRD. All specimens were tested in four-point bending. Data were statistically analyzed using one-way ANOVA and Post Hoc tests (α=0.05). A Weibull analysis was used to analyze the strength reliability. Sandblasting pre-sintered zirconia before sintering significantly decreased the flexural strength, except when the smallest blasting particles were used (30μm SiO2). Phase transformation (t-m) was observed after sandblasting and reverse transformation (m-t) was observed after heating. Sandblasting with 30μm SiO2 and 50μm Al2O3 allowed lower phase transformation. However, 30mm SiO2 presented better reliability. Copyright © 2015 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Post-thermocycling shear bond strength of a gingiva-colored indirect composite layering material to three implant framework materials.

PubMed

Komine, Futoshi; Koizuka, Mai; Fushiki, Ryosuke; Taguchi, Kohei; Kamio, Shingo; Matsumura, Hideo

2013-09-01

To evaluate shear bond strength of a gingiva-colored indirect composite to three implant framework materials, before and after thermocycling, and verify the effect of surface pre-treatment for each framework. Commercially pure titanium (CP-Ti), American Dental Association (ADA) type 4 casting gold alloy (Type IV) and zirconia ceramics (Zirconia) were assessed. For each substrate, 96 disks were divided into six groups and primed with one of the following primers: Alloy Primer (ALP), Clearfil Photo Bond (CPB), Clearfil Photo Bond with Clearfil Porcelain Bond Activator (CPB+Activator), Estenia Opaque Primer (EOP), Metal Link (MLP) and V-Primer (VPR). The specimens were then bonded to a gingiva-colored indirect composite (Ceramage Concentrate GUM-D). Shear bond strengths were measured at 0 and 20 000 thermocycles and data were analyzed with the Steel-Dwass test and Mann-Whitney U-test. Shear bond strengths were significantly lower after thermocycling, with the exception of Type IV specimens primed with CPB (p = 0.092) or MLP (p = 0.112). For CP-Ti and Zirconia specimens, priming with CPB or CPB+Activator produced significantly higher bond strengths at 0 and 20 000 thermocycles, as compared with the other groups. For Type IV specimens, priming with ALP or MLP produced higher bond strengths at 0 and 20 000 thermocycles. Shear bond strength of a gingiva-colored indirect composite to CP-Ti, gold alloy and zirconia ceramics was generally lower after thermocycling. Application of a hydrophobic phosphate monomer and polymerization initiator was effective in maintaining bond strength of CP-Ti and zirconia ceramics. Combined use of a thione monomer and phosphoric monomer enhanced the durable bond strength of gold alloy.

The effect of home bleaching agents on the surface roughness of five different composite resins: A SEM evaluation.

PubMed

Cengiz, Esra; Kurtulmus-Yilmaz, Sevcan; Ulusoy, Nuran; Deniz, Sule Tugba; Yuksel-Devrim, Ece

2016-05-01

The aim of this study was to investigate the effect of hydrogen peroxide (HP) and carbamide peroxide (CP) on the surface roughness of five different composite resins using profilometer and scanning electron microscope (SEM). Thirty-six specimens (1 mm thick, 10 mm in diameter) of five composite resins were fabricated. Each composite group was equally divided into three subgroups as control, CP and HP. In control group, specimens were stored in daily refreshed distilled water during the 14-day testing period. In other groups, 10% HP (Opalescence Treswhite) and 10% CP (Opalescence PF) were applied and surface roughness values (Ra) of each specimen were measured with a profilometer at the end of 14 days. Additionally, SEM analysis was performed to evaluate the surface deformations of composite resins. Data were analyzed with Kruskal-Wallis and Mann-Whitney U tests. Ra values of composite groups exposed to bleaching agents were statistically higher than control group (p < 0.05). There was no significant difference between Ra values after HP and CP application within each composite group while SEM micrographs showed higher surface alterations at HP group compared to CP. Among the composite resins tested, Ceram-X Mono revealed the lowest Ra values after CP and HP applications as seen at SEM images. Home bleaching agents increased the surface roughness of all composites. Except CP applied Ceram-X mono specimens, Ra values of all composite resins evaluated in this study exceeded the critical limit of 0.2 μm. Ceram-X mono was the least affected composite material after bleaching application. SCANNING 38:277-283, 2016. © 2016 Wiley Periodicals, Inc. © Wiley Periodicals, Inc.

Efficacy of ceramic repair material on the bond strength of composite resin to zirconia ceramic.

PubMed

Kirmali, Omer; Kapdan, Alper; Harorli, Osman Tolga; Barutcugil, Cagatay; Ozarslan, Mehmet Mustafa

2015-01-01

The aim of this study was to evaluate the shear bond strength of composite resin in five different repair systems. Sixty specimens (7 mm in diameter and 3 mm in height) of zirconia ceramic were fabricated. All specimen surfaces were prepared with a 30 µm fine diamond rotary cutting instrument with water irrigation for 10 s and dried with oil-free air. Specimens were then randomly divided into six groups for the following different intra-oral repair systems (n = 10): Group 1, control group; Group 2, Cojet system (3M ESPE, Seefeld, Germany); Group 3, Cimara® System (Voco, Cuxhaven, Germany); Group 4, Z-Prime Plus System (Bisco Inc., Schaumburg, IL); Group 5, Clearfil™ System (Kuraray, Osaka, Japan); and Group 6, Z-Bond System (Danville, CA). After surface conditioning, a composite resin Grandio (Voco, Cuxhaven, Germany) was applied to the zirconia surface using a cylindrical mold (5 mm in diameter and 3 mm in length) and incrementally filled up, according to the manufacturer's instructions of each intra-oral system. Each specimen was subjected to a shear load at a crosshead speed of 1 mm/min until fracture. One-way analysis of variance (ANOVA) and Tukey post-hoc tests were used to analyze the bond strength values. There were significant differences between Groups 2-6 and Group 1. The highest bond strength values were obtained with Group 2 (17.26 ± 3.22) and Group 3 (17.31 ± 3.62), while the lowest values were observed with Group 1 (8.96 ± 1.62) and Group 6 (12.85 ± 3.95). All repair systems tested increased the bond strength values between zirconia and composite resin that used surface grinding with a diamond bur.

Synthesis of SiCN@TiO2 core-shell ceramic microspheres via PDCs method

NASA Astrophysics Data System (ADS)

Liu, Hongli; Wei, Ning; Li, Jing; Zhang, Haiyuan; Chu, Peng

2018-02-01

A facile and effective polymer-derived ceramics (PDCs) emulsification-crosslinking-pyrolysis method was developed to fabricate SiCN@TiO2 core-shell ceramic microspheres with polyvinylsilazane (PVSZ) and tetrabutyl titanate (TBT) as precursors. The TBT: PVSZ mass ratios, emulsifier concentrations and the pyrolysis temperature were examined as control parameters to tune the size and morphology of microspheres. Scanning electron microscopy (SEM) and transmission electron microscopy (TEM) confirmed the synthesized SiCN@TiO2 microspheres to be comprised of SiCN core coated with TiO2 crystals, with an average size of 0.88 μm when pyrolyzed at 1400 °C. The analysis of Fourier transform infrared spectroscopy (FT-IR), energy dispersive spectroscopy (EDS) and X-ray diffraction (XRD) ensured that SiCN@TiO2 core-shell ceramic microspheres composed of rutile TiO2, β-SiC and Si3N4 crystalline phases, The thermal properties were characterized by thermogravimetric analysis (TGA). The obtained SiCN@TiO2 core-shell ceramic microspheres were the promising candidate of the infrared opacifier in silica aerogels and this technique can be extended to other preceramic polymers.

Color stainability of CAD/CAM and nanocomposite resin materials.

PubMed

Acar, Ozlem; Yilmaz, Burak; Altintas, Subutay Han; Chandrasekaran, Indumathi; Johnston, William M

2016-01-01

The color stainability of recently introduced computer-assisted design/computer-assisted manufacturing (CAD/CAM) hybrid ceramic and resin nanoceramic is unknown. The purpose of this in vitro study was to compare the effect of coffee staining on the color of 3 different CAD/CAM restorative materials and a nanocomposite resin. Specimens from a hybrid dental ceramic (VITA Enamic), a resin nanoceramic (Lava Ultimate), a lithium disilicate glass ceramic (IPS e.max CAD), and a nanocomposite resin (Filtek Supreme Ultra Universal) were evaluated for color change due to thermocycling in coffee (n=5). Specimens 0.5 to 0.7 mm and 1 to 1.2 mm in thickness were thermocycled for 5000 cycles. CIEDE2000 color differences (ΔE00) due to thermocycling in coffee were calculated using the color coordinates obtained from a spectroradiometer. ANCOVA was used to analyze the color differences among the materials with thickness as the covariate. Significant differences at average thickness were analyzed with the Tukey-Kramer test. For color difference due to staining, thickness was a significant covariate (P<.001). Regarding the analysis of color differences, every pair of the tested materials was significantly different (P<.001). Least squares means of color differences (ΔE00) at mean thickness were 4.34 for the nanohybrid composite resin, 3.66 for the resin nanoceramic, 1.35 for the hybrid ceramic, and 0.43 for the lithium disilicate ceramic. When exposed to hot and cold coffee, the color change was beyond clinical acceptability for the tested resin nanoceramic and nanocomposite resin materials. The average color change of the hybrid ceramic was clinically perceivable over the tested thickness values. The color change of lithium disilicate ceramic was not clinically perceivable at any tested thickness. Copyright © 2016 Editorial Council for the Journal of Prosthetic Dentistry. Published by Elsevier Inc. All rights reserved.

Microstructure characterization and SCG of newly engineered dental ceramics.

PubMed

Ramos, Nathália de Carvalho; Campos, Tiago Moreira Bastos; Paz, Igor Siqueira de La; Machado, João Paulo Barros; Bottino, Marco Antonio; Cesar, Paulo Francisco; Melo, Renata Marques de

2016-07-01

The aim of this study was to characterize the microstructure of four dental CAD-CAM ceramics and evaluate their susceptibility to stress corrosion. SEM and EDS were performed for microstructural characterization. For evaluation of the pattern of crystallization of the ceramics and the molecular composition, XRD and FTIR, respectively, were used. Elastic modulus, Poisson's ratio, density and fracture toughness were also measured. The specimens were subjected to biaxial flexure under five stress rates (0.006, 0.06, 0.6, 6 and 60MPa/s) to determine the subcritical crack growth parameters (n and D). Twenty-five specimens were further tested in mineral oil for determination of Weibull parameters. Two hundred forty ceramic discs (12mm diameter and 1.2mm thick) were made from four ceramics: feldspathic ceramic - FEL (Vita Mark II, Vita Zahnfabrik), ceramic-infiltrated polymer - PIC (Vita Enamic, Vita Zahnfabrik), lithium disilicate - LD (IPS e.max CAD, Ivoclar Vivadent) and zirconia-reinforced lithium silicate - LS (Vita Suprinity, Vita Zahnfabrik). PIC discs presented organic and inorganic phases (n=29.1±7.7) and Weibull modulus (m) of 8.96. The FEL discs showed n=36.6±6.8 and m=8.02. The LD discs showed a structure with needle-like disilicate grains in a glassy matrix and had the lowest value of n (8.4±0.8) and m=6.19. The ZLS discs showed similar rod-like grains, n=11.2±1.4 and m=9.98. The FEL and PIC discs showed the lowest susceptibility to slow crack growth (SCG), whereas the LD and ZLS discs presented the highest. PIC presented the lowest elastic modulus and no crystals in its composition, while ZLS presented tetragonal zirconia. The overall strength and SCG of the new materials did not benefit from the additional phase or microconstituents present in them. Copyright © 2016 The Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Contributions of intrinsic and extrinsic polarization species to energy storage properties of Ba0.95Ca0.05Zr0.2Ti0.8O3 ceramics

NASA Astrophysics Data System (ADS)

Zhan, Di; Xu, Qing; Huang, Duan-Ping; Liu, Han-Xing; Chen, Wen; Zhang, Feng

2018-03-01

Ba0.95Ca0.05Zr0.2Ti0.8O3 ceramics were prepared at different sintering temperatures by citrate precursor and solid-state reaction methods, respectively. The crystal structure and microstructure of the specimens were characterized. In view of energy storage capacitor utilizations, the dielectric properties of the specimens were investigated at room temperature as a function of frequency and applied electric field. Moreover, the nature of mobile charge carriers in the specimens was diagnosed by complex impedance spectroscopy at elevated temperatures. While the dielectric constants of the specimens prepared by different methods are quite different (4.4 × 103-2.2 × 104 at 10 kHz) at zero electric field, the energy storage densities at an identical strong electric field are similar (e.g. 0.32-0.41 J/cm3 at 120 kV/cm). The dielectric constants under bias electric field were fitted to a multipolarization mechanism model to resolve the contributions of intrinsic and extrinsic polarization mechanisms. It turned out that the extrinsic contributions fade out within low electric field range (<20 kV/cm) and thereby the intrinsic lattice polarization governs the overall dielectric responses at higher fields. Based on the fitting result, the energy storage properties of the specimens were interpreted.

Engineering of III-Nitride Semiconductors on Low Temperature Co-fired Ceramics.

PubMed

Mánuel, J M; Jiménez, J J; Morales, F M; Lacroix, B; Santos, A J; García, R; Blanco, E; Domínguez, M; Ramírez, M; Beltrán, A M; Alexandrov, D; Tot, J; Dubreuil, R; Videkov, V; Andreev, S; Tzaneva, B; Bartsch, H; Breiling, J; Pezoldt, J; Fischer, M; Müller, J

2018-05-02

This work presents results in the field of advanced substrate solutions in order to achieve high crystalline quality group-III nitrides based heterostructures for high frequency and power devices or for sensor applications. With that objective, Low Temperature Co-fired Ceramics has been used, as a non-crystalline substrate. Structures like these have never been developed before, and for economic reasons will represent a groundbreaking material in these fields of Electronic. In this sense, the report presents the characterization through various techniques of three series of specimens where GaN was deposited on this ceramic composite, using different buffer layers, and a singular metal-organic chemical vapor deposition related technique for low temperature deposition. Other single crystalline ceramic-based templates were also utilized as substrate materials, for comparison purposes.

Fractographic Investigation of Micromechanisms of Fracture in Alumina Ceramics

DTIC Science & Technology

1981-11-30

mechanisms flaw linking work of fracture electron channeling crack branching environmental effects 20. A07 ACT (Continue an reverse side Of necessary and...CLASSIFICATION OF THIS PAGE(I hm Date "ftn.,a environments using multiple techniques such as SEM, TEM, selected area electron channeling , and...94 Selected area electron channeling (SAEC) .. .... ........ 99 V. CONCLUSIONS. .. ............................ 100 VI. REFERENCES

Survival of resin infiltrated ceramics under influence of fatigue.

PubMed

Aboushelib, Moustafa N; Elsafi, Mohamed H

2016-04-01

to evaluate influence of cyclic fatigue on two resin infiltrated ceramics and three all-ceramic crowns manufactured using CAD/CAM technology. CAD/CAM anatomically shaped crowns were manufactured using two resin infiltrated ceramics (Lava Ultimate and Vita Enamic), two reinforced glass ceramic milling blocks ((IPS)Empress CAD and (IPS)e.max CAD) and a veneered zirconia core ((IPS)Zir CAD). (IPS)e.max CAD and (IPS)Zir CAD were milled into 0.5mm thick anatomically shaped core structure which received standardized press-on veneer ceramic. The manufactured crowns were cemented on standardized resin dies using a resin adhesive (Panavia F2.0). Initial fracture strength of half of the specimens was calculated using one cycle load to failure in a universal testing machine. The remaining crowns were subjected to 3.7 million chewing cycles (load range 50-200N at 3s interval) in a custom made pneumatic fatigue tester. Survival statistics were calculated and Weibull modulus was measured from fitted load-cycle-failure diagrams. Scanning electron microscopy was performed to fractographically analyze fractured surfaces. Data were analyzed using two way analysis of variance and Bonferroni post hoc tests (α=0.05). Dynamic fatigue resulted in significant reduction (F=7.54, P<0.005) of the initial fracture strength of the tested specimens. Zirconia showed the highest deterioration percent (34% reduction in strength) followed by (IPS)Empress (32.2%), (IPS)e.max (27.1%) while Lava Ultimate and Vita Enamic showed the lowest percent of reduction in strength. The two types of resin infiltrated ceramics and (IPS)Empress demonstrated the highest percent of fracture incidences under the influence of fatigue (35-45% splitting). None of the tested veneered zirconia restorations were fractured during testing, however, chipping of the veneer ceramics was observed in 6 crowns. The lowest percent of failure was observed for (IPS)e.max crowns manifested as 3 cases of minor chipping in addition to two complete fracture incidences. SEM images demonstrated the internal structure of the tested materials and detected location and size of the critical crack. The internal structure of the tested materials significantly influenced their fatigue behavior. Resin infiltrated ceramics were least influenced by fatigue while the characteristic strength of zirconia prevented core fracture but failure still occurred from the weaker veneer ceramic. Copyright © 2015 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Effects of Universal and Conventional MDP Primers on the Shear Bond Strength of Zirconia Ceramic and Nanofilled Composite Resin

PubMed Central

Sharafeddin, Farahnaz; Shoale, Soodabe

2018-01-01

Statement of the Problem: The clinical success of ceramic depends on the quality of the bond between the zirconia and resin cement. Purpose: In the present study, the effects of universal and conventional MDP-containing primers were evaluated on the shear bond strength of zirconia ceramic and nanofilled composite resin. Materials and Method: Thirty blocks of zirconia ceramic (6mm×2mm) were prepared. Then the inner surfaces were air-abraded and divided into three groups (n= 10) as follows: untreated with primer (control group, I); All- Bond Universal (group II) and Z-Prime Plus (group III). The specimens in each group were bonded with Variolink N cement to cylinders of composite resin Z350XT. After 24 hour water storage, the shear bond strength test was performed with a universal testing machine at a crosshead speed of 1mm/ min and bond strength values (MPa) were calculated and analyzed with one-way ANOVA and post hoc Tukey tests (p< 0.05). The failure mode of each specimen was evaluated under a stereomicroscope and representative specimens were analyzed by scanning electron microscopy (SEM). Results: The mean shear bond strength values (MPa) were 7.58±1.62, 17.51±1.34 and 22.45±3.60 in groups I, II and III, respectively. These results indicated that the shear bond strength were significantly higher in groups II and III compared to the control group (p< 0.001). Chemical pre-treatment of zirconia with Z- Prime Plus revealed significantly higher bond strength than the All-Bond Universal adhesive (p< 0.002). All the failure modes were adhesive in the control group (I) and when using primer treatment, mixed failures occurred in 40% and 50% of specimens in groups II and III, respectively. Conclusion: Treatment with both primers resulted in higher bond strength values compared to the control group. The use of Z-Prime Plus treatment in combination with air-abrasion procedure resulted in the highest bond strength. PMID:29492416

Phase transition behavior of (K,Na)NbO3-based high-performance lead-free piezoelectric ceramic composite with different phase compositions depending on Na fraction

NASA Astrophysics Data System (ADS)

Yamada, Hideto; Matsuoka, Takayuki; Yamazaki, Masato; Ohbayashi, Kazushige; Ida, Takashi

2018-01-01

The structures of the main (K1- x Na x )NbO3 perovskite in a high-performance lead-free piezoelectric ceramic composite (K1- x Na x )0.86Ca0.04Li0.02Nb0.85O3-δ-K0.85Ti0.85Nb1.15O5-BaZrO3-MgO-Fe2O3 (x = 0.52 and 0.70) with trace amounts of LiMgFeTiO4 inverse spinel and (Li,K)2(Mg,Fe,Ti,Nb)6O13 layered structure have been investigated by transmission electron microscopy (TEM) and synchrotron powder X-ray diffractometry (XRD) with varying temperatures. The bright-field TEM images have shown tetragonal 90°-domain contrasts at 80 and 40 °C, and the XRD profile has been simulated by adding an average structure of two differently oriented tetragonal structures bound by a 90°-domain wall for the x = 0.52 sample. Aggregates of tilted NbO6 nanodomains have been observed in a high-resolution TEM image, and the crossover of P4mm-Amm2 features from 60 to 20 °C and diffuse 2 × 2 × 2 superlattice reflections of the tilted NbO6 Imm2 structure have been observed in XRD data for the x = 0.70 sample.

Influence of ceramic thickness and ceramic materials on fracture resistance of posterior partial coverage restorations.

PubMed

Bakeman, E M; Rego, N; Chaiyabutr, Y; Kois, J C

2015-01-01

This study evaluated the influence of ceramic thickness and ceramic materials on fracture resistance of posterior partial coverage ceramic restorations. Forty extracted molars were allocated into four groups (n=10) to test for two variables: 1) the thickness of ceramic (1 mm or 2 mm) and 2) the ceramic materials (a lithium disilicate glass-ceramic [IPS e.max] or leucite-reinforced glass ceramic [IPS Empress]). All ceramic restorations were luted with resin cement (Variolink II) on the prepared teeth. These luted specimens were loaded to failure in a universal testing machine, in the compression mode, with a crosshead speed of 1.0 mm/min. The data were analyzed using two-way analysis of variance and the Tukey Honestly Significantly Different multiple comparison test (α =0.05). The fracture resistance revealed a significant effect for materials (p<0.001); however, the thickness of ceramic was not significant (p=0.074), and the interaction between the thickness of ceramic and the materials was not significant (p=0.406). Mean (standard deviation) fracture resistance values were as follows: a 2-mm thickness of a lithium disilicate bonded to tooth structure (2505 [401] N) revealed a significantly higher fracture resistance than did a 1-mm thickness of leucite-reinforced (1569 [452] N) and a 2-mm thickness of leucite-reinforced ceramic bonded to tooth structure (1716 [436] N) (p<0.05). There was no significant difference in fracture resistance values between a lithium disilicate ceramic at 1-mm thickness (2105 [567] N) and at 2-mm thickness. Using a lithium disilicate glass ceramic for partial coverage restoration significantly improved fracture resistance compared to using a leucite-reinforced glass ceramic. The thickness of ceramic had no significant effect on fracture resistance when the ceramics were bonded to the underlying tooth structure.

In vivo biofilm formation on different dental ceramics.

PubMed

Bremer, Felicia; Grade, Sebastian; Kohorst, Philipp; Stiesch, Meike

2011-01-01

To investigate the formation of oral biofilm on various dental ceramics in vivo. Five different ceramic materials were included: a veneering glass- ceramic, a lithium disilicate glass-ceramic, a yttrium-stabilized zirconia (Y-TZP), a hot isostatically pressed (HIP) Y-TZP ceramic, and an HIP Y-TZP ceramic with 25% alumina. Test specimens were attached to individually designed acrylic appliances; five volunteers wore these appliances for 24 hours in the maxillary arch. After intraoral exposure, the samples were removed from the appliances and the adhering biofilms vitally stained. Then, the two-dimensional surface coating and thickness of the adhering biofilm were determined by confocal laser scanning microscopy. Statistical analysis was performed using one-way ANOVA with the level of significance set at .05. Significant differences (P < .001) in the bacterial surface coating and in the thickness of the biofilm were found between the various ceramic materials. The lowest surface coating (19.0%) and biofilm thickness (1.9 Μm) were determined on the HIP Y-TZP ceramic; the highest mean values were identified with the lithium disilicate glass-ceramic (46.8%, 12.6 Μm). Biofilm formation on various types of dental ceramics differed significantly; in particular, zirconia exhibited low plaque accumulation. In addition to its high strength, low plaque accumulation makes zirconia a promising material for various indications (including implant abutments and telescopic crowns) that previously were met only with metal-based materials.

Synthesis and microstructural TEM investigation of CaCu 3Ru 4O 12 ceramic and thin film

NASA Astrophysics Data System (ADS)

Brizé, Virginie; Autret-Lambert, Cécile; Wolfman, Jérôme; Gervais, Monique; Gervais, François

2011-10-01

CaCu 3Ru 4O 12 (CCRO) is a conductive oxide having the same structure as CaCu 3Ti 4O 12 (CCTO) and close lattice parameters. The later compound is strongly considered for high density parallel plates capacitors application due to its so-called colossal dielectric constant. The need for an electrode inducing CCTO epitaxial growth with a clean and sharp interface is therefore necessary, and CCRO is a good potential candidate. In this paper, the synthesis of monophasic CCRO ceramic is reported, as well as pulsed laser deposition of CCRO thin film onto (001) NdCaAlO 4 substrate. Structural and physical properties of bulk CCRO were studied by transmission electron microscopy and electron spin resonance. CCRO films and ceramic exhibited a metallic behavior down to low temperature. CCRO films were (001) oriented and promoted a CCTO film growth with the same orientation.

Enhanced NIR downconversion luminescence by precipitating nano Ca5(PO4)3F crystals in Eu2+-Yb3+ co-doped glass

NASA Astrophysics Data System (ADS)

Li, Chen; Song, Zhiguo; Li, Yongjin; Lou, Kai; Qiu, Jianbei; Yang, Zhengwen; Yin, Zhaoyi; Wang, Xue; Wang, Qi; Wan, Ronghua

2013-10-01

Eu2+-Yb3+ co-doped transparent glass-ceramic containing nano-Ca5(PO4)3F (FAP) was prepared in reducing atmosphere. XRD and TEM analysis indicated that nano-FAP about 40 nm precipitated homogeneously in glass matrix after heat treatment. Confirmed by spectroscopy measurements, the crystal-like absorption and emission of Eu2+ indicated the partition of Eu2+ into FAP nanocrystals in glass ceramic. NIR emission due to the transition 2F→2F of Yb3+ ions (about 980-1100 nm) was observed from glasses under ultraviolet excitation, ascribed to downconversion from Eu2+ to Yb3+, which can be enhanced by precipitating nano-FAP crystals. The results indicated that Eu2+-Yb3+ co-doped glass-ceramic embedding with nano-FAP is a promising candidate as downconversion materials for enhancing conversion efficiency of solar cells.

Life prediction and mechanical reliability of NT551 silicon nitride

NASA Astrophysics Data System (ADS)

Andrews, Mark Jay

The inert strength and fatigue performance of a diesel engine exhaust valve made from silicon nitride (Si3N4) ceramic were assessed. The Si3N4 characterized in this study was manufactured by Saint Gobain/Norton Industrial Ceramics and was designated as NT551. The evaluation was made utilizing a probabilistic life prediction algorithm that combined censored test specimen strength data with a Weibull distribution function and the stress field of the ceramic valve obtained from finite element analysis. The major assumptions of the life prediction algorithm are that the bulk ceramic material is isotropic and homogeneous and that the strength-limiting flaws are uniformly distributed. The results from mechanical testing indicated that NT551 was not a homogeneous ceramic and that its strength were functions of temperature, loading rate, and machining orientation. Fractographic analysis identified four different failure modes; 2 were identified as inhomogeneities that were located throughout the bulk of NT551 and were due to processing operations. The fractographic analysis concluded that the strength degradation of NT551 observed from the temperature and loading rate test parameters was due to a change of state that occurred in its secondary phase. Pristine and engine-tested valves made from NT551 were loaded to failure and the inert strengths were obtained. Fractographic analysis of the valves identified the same four failure mechanisms as found with the test specimens. The fatigue performance and the inert strength of the Si3N 4 valves were assessed from censored and uncensored test specimen strength data, respectively. The inert strength failure probability predictions were compared to the inert strength of the Si3N4 valves. The inert strength failure probability predictions were more conservative than the strength of the valves. The lack of correlation between predicted and actual valve strength was due to the nonuniform distribution of inhomogeneities present in NT551. For the same reasons, the predicted and actual fatigue performance did not correlate well. The results of this study should not be considered a limitation of the life prediction algorithm but emphasize the requirement that ceramics be homogeneous and strength-limiting flaws uniformly distributed as a perquisite for accurate life prediction and reliability analyses.

Is laser conditioning a valid alternative to conventional etching for aesthetic brackets?

PubMed

Sfondrini, M F; Calderoni, G; Vitale, M C; Gandini, P; Scribante, A

2018-03-01

ER:Yag lasers have been described as a more conservative alternative to conventional acid-etching enamel conditioning technique, when bonding conventional metallic orthodontic brackets. Since the use of aesthetic orthodontic brackets is constantly increasing, the purpose of the present report has been to test laser conditioning with different aesthetic brackets. Study Design: Five different aesthetic brackets (microfilled copolymer, glass fiber, sapphire, polyoxymethylene and sintered ceramic) were tested for shear bond strength and Adhesive Remnant Index scores using two different enamel conditioning techniques (acid etching and ER:Yag laser application). Two hundred bovine incisors were extracted, cleaned and embedded in resin. Specimens were then divided into 10 groups with random tables. Half of the specimens were conditioned with conventional orthophosphoric acid gel, the other half with ER:Yag laser. Different aesthetic brackets (microfilled copolymer, glass fiber, sapphire, polyoxymethylene and sintered ceramic) were then bonded to the teeth. Subsequently all groups were tested in shear mode with a Universal Testing Machine. Shear bond strength values and adhesive remnant index scores were recorded. Statistical analysis was performed. When considering conventional acid etching technique, sapphire, polyoxymethylene and sintered ceramic brackets exhibited the highest SBS values. Lowest values were reported for microfilled copolymer and glass fiber appliances. A significant decrease in SBS values after laser conditioning was reported for sapphire, polyoxymethylene and sintered ceramic brackets, whereas no significant difference was reported for microfilled copolymer and glass fiber brackets. Significant differences in ARI scores were also reported. Laser etching can significantly reduce bonding efficacy of sapphire, polyoxymethylene and sintered ceramic brackets.

A comparative study on the bond strength of porcelain to the millingable Pd-Ag alloy

PubMed Central

Hong, Jun-Tae

2014-01-01

PURPOSE The porcelain fused to gold has been widely used as a restoration both with the natural esthetics of the porcelain and durability and marginal fit of metal casting. However, recently, due to the continuous rise in the price of gold, an interest towards materials to replace gold alloy is getting higher. This study compared the bond strength of porcelain to millingable palladium-silver (Pd-Ag) alloy, with that of 3 conventionally used metal-ceramic alloys. MATERIALS AND METHODS Four types of metal-ceramic alloys, castable nonprecious nickel-chrome alloy, castable precious metal alloys containing 83% and 32% of gold, and millingable Pd-Ag alloy were used to make metal specimens (n=40). And porcelain was applied on the center area of metal specimen. Three-point bending test was performed with universal testing machine. The bond strength data were analyzed with a one-way ANOVA and post hoc Scheffe's tests (α=.05). RESULTS The 3-point bending test showed the strongest (40.42 ± 5.72 MPa) metal-ceramic bond in the nonprecious Ni-Cr alloy, followed by millingable Pd-Ag alloy (37.71 ± 2.46 MPa), precious metal alloy containing 83% of gold (35.89 ± 1.93 MPa), and precious metal alloy containing 32% of gold (34.59 ± 2.63 MPa). Nonprecious Ni-Cr alloy and precious metal alloy containing 32% of gold showed significant difference (P<.05). CONCLUSION The type of metal-ceramic alloys affects the bond strength of porcelain. Every metal-ceramic alloy used in this study showed clinically applicable bond strength with porcelain (25 MPa). PMID:25352959

Effect of different surface treatments on shear bond strength of zirconia to three resin cements

NASA Astrophysics Data System (ADS)

Dadjoo, Nisa

Statement of problem: There are no standard guidelines for material selection to obtain acceptable bonding to high-strength zirconium oxide ceramic. Studies suggest resin cements in combination with MDP-containing primer is a reasonable choice, however, the other cements cannot be rejected and need further investigation. Objective: The purpose of this in vitro study was the evaluation of the shear bond strength of three composite resin cements to zirconia ceramic after using different surface conditioning methods. Materials and methods: One hundred and twenty sintered Y-TZP ceramic (IPS e.max ZirCAD) squares (8 x 8 x 4 mm) were embedded in acrylic molds, then divided into three groups (n=40) based on the type of cement used. Within each group, the specimens were divided into four subgroups (n=10) and treated as follows: (1) Air abrasion with 50microm aluminum oxide (Al2O 3) particles (ALO); (2) Air abrasion + Scotchbond Universal adhesive (SBU); (3) Air abrasion + Monobond Plus (MBP); (4) Air abrasion + Z-Prime Plus (ZPP). Composite cylinders were used as carriers to bond to conditioned ceramic using (1) RelyX Ultimate adhesive resin cement (RX); (2) Panavia SA self-adhesive resin cement (PSA); (3) Calibra esthetic cement (CAL). The bonded specimens were submerged in distilled water and subjected to 24-hour incubation period at 37°C. All specimens were stressed in shear at a constant crosshead speed of 0.5 mm/min until failure. Statistical analysis was performed by ANOVA. The bond strength values (MPa), means and standard deviations were calculated and data were analyzed using analysis of variance with Fisher's PLSD multiple comparison test at the 0.05 level of significance. The nature of failure was recorded. Results: The two-way ANOVA showed Panavia SA to have the highest strength at 44.3 +/- 16.9 MPa (p<0.05). The combination of Scotchbond Universal surface treatment with Panavia SA cement showed statistically higher bond strength (p=0.0054). The highest bond strengths for all three cements were observed with Scotchbond Universal surface treatment (p=0.0041). Calibra in combination with aluminum oxide air abrasion resulted in statistically lowest bond strength at 12.0 +/- 3.9 MPa. The predominant mode of failure was cohesive with cement remaining principally on the zirconium oxide samples in 57.5% of the specimens, followed by cement found on both the zirconium oxide samples and composite rods (mixed) in 32.5% of the samples. Only 10% of the specimens were found with cement on the composite rods (adhesive failure). Conclusions: Within the limitations of this in vitro study, the MDP-containing resin cement, Panavia SA, yielded the strongest bond to Y-TZP ceramic when compared to adhesive (RelyX Ultimate) or esthetic (Calibra) resin cements. Air abrasion particle + Scotchbond Universal surface treatment demonstrated the highest bond strength regardless of the cement. Significance: The variation of surface conditioning methods yielded different results in accordance with the cement types. Overall, Scotchbond Universal adhesive + air abrasion yielded the highest bond strengths among all three surface treatments. The phosphate monomer-containing luting system, Panavia SA, is acceptable for bonding to zirconia ceramics.

Quantifying the Effects of the Influence of a Tungsten Long-rod Projectile into Confined Ceramics at High-velocity Impact

DTIC Science & Technology

2008-01-29

be conducted to demonstrate how the confined, brittle samples behave. The study shows that silicon carbide and boron carbide are the optimal...Exposition on Advanced Ceramics and Composites - 27 JAN to 1 FEB 2008, Daytona Beach, FL, The original document contains color images. 14. ABSTRACT 15...specimens investigated were aluminum nitride, boron carbide, 9606 pyroceram, and silicon carbide. The confining sleeve was modeled with RHA and had a

Effect of a novel bioactive glass-ceramic on dentinal tubule occlusion: an in vitro study.

PubMed

Zhong, Y; Liu, J; Li, X; Yin, W; He, T; Hu, D; Liao, Y; Yao, X; Wang, Y

2015-03-01

This in vitro study aimed to assess the ability and efficacy of HX-BGC, a novel bioactive glass-ceramic (SiO2-P2 O5-CaO-Na2 O-SrO), to reduce dentine tubule permeability. Dentine discs from human third molars were etched and randomly allocated into five groups: Group 1--distilled water; Group 2--Sensodyne Repair toothpaste (containing NovaMin®); Group 3--HX-BGC toothpaste (containing 7.5% HX-BGC); Group 4--control toothpaste (without HX-BGC); and Group 5--HX-BGC powder. Specimens were treated daily by brushing with an electric toothbrush for 20 seconds. Between daily treatments (7 days total), specimens were immersed in artificial saliva for 24 hours. Dentine permeability was measured at baseline, after the first treatment, after the first 24-hour immersion in artificial saliva and at the end of day 7. Dentine morphology and surface deposits were observed by scanning electron microscopy after one day and 7 days of treatment, respectively. Sensodyne Repair and bioactive glass-ceramic toothpaste significantly and immediately lowered dentine permeability. The HX-BGC powder group showed the highest reduction in dentine permeability after 7 days of treatment. The novel bioactive glass-ceramic material HX-BGC is effective in reducing dentine permeability by occluding open dentine tubules, indicating that HX-BGC may be a potential treatment for dentine hypersensitivity. © 2015 Australian Dental Association.

Bonding of TRIP-Steel/Al2O3-(3Y)-TZP Composites and (3Y)-TZP Ceramic by a Spark Plasma Sintering (SPS) Apparatus

PubMed Central

Miriyev, Aslan; Grützner, Steffen; Krüger, Lutz; Kalabukhov, Sergey; Frage, Nachum

2016-01-01

A combination of the high damage tolerance of TRIP-steel and the extremely low thermal conductivity of partially stabilized zirconia (PSZ) can provide controlled thermal-mechanical properties to sandwich-shaped composite specimens comprising these materials. Sintering the (TRIP-steel-PSZ)/PSZ sandwich in a single step is very difficult due to differences in the sintering temperature and densification kinetics of the composite and the ceramic powders. In the present study, we successfully applied a two-step approach involving separate SPS consolidation of pure (3Y)-TZP and composites containing 20 vol % TRIP-steel, 40 vol % Al2O3 and 40 vol % (3Y)-TZP ceramic phase, and subsequent diffusion joining of both sintered components in an SPS apparatus. The microstructure and properties of the sintered and bonded specimens were characterized. No defects at the interface between the TZP and the composite after joining in the 1050–1150 °C temperature range were observed. Only limited grain growth occurred during joining, while crystallite size, hardness, shear strength and the fraction of the monoclinic phase in the TZP ceramic virtually did not change. The slight increase of the TZP layer’s fracture toughness with the joining temperature was attributed to the effect of grain size on transformation toughening. PMID:28773680

Bond and fracture strength of metal-ceramic restorations formed by selective laser sintering

PubMed Central

Bae, Eun-Jeong; Kim, Woong-Chul; Kim, Hae-Young

2014-01-01

PURPOSE The purpose of this study was to compare the fracture strength of the metal and the bond strength in metal-ceramic restorations produced by selective laser sintering (SLS) and by conventional casting (CAST). MATERIALS AND METHODS Non-precious alloy (StarLoy C, DeguDent, Hanau, Germany) was used in CAST group and metal powder (SP2, EOS GmbH, Munich, Germany) in SLS group. Metal specimens in the form of sheets (25.0 × 3.0 × 0.5 mm) were produced in accordance with ISO 9693:1999 standards (n=30). To measure the bond strength, ceramic was fired on a metal specimen and then three-point bending test was performed. In addition, the metal fracture strength was measured by continuing the application of the load. The values were statistically analyzed by performing independent t-tests (α=.05). RESULTS The mean bond strength of the SLS group (50.60 MPa) was higher than that of the CAST group (46.29 MPa), but there was no statistically significant difference. The metal fracture strength of the SLS group (1087.2 MPa) was lower than that of the CAST group (2399.1 MPa), and this difference was statistically significant. CONCLUSION In conclusion the balling phenomenon and the gap formation of the SLS process may increase the metal-ceramic bond strength. PMID:25177469

The Effect of Prophylactic Polishing Pastes on Surface Roughness of Indirect Restorative Materials

PubMed Central

Can Say, Esra; Yurdagüven, Haktan; Malkondu, Özlem; Ünlü, Nimet; Soyman, Mübin; Kazazoğlu, Ender

2014-01-01

The purpose of this study was to evaluate the influence of prophylactic polishing pastes (PPP; Detartrine (DT), Topex (TP)) on surface roughness (R a) of indirect composites (IRC; Tescera (TES), Gradia (GRD), and Estenia C&B (EST)), a glass ceramic (Empress 2 layering (E2)), and a leucite reinforced glass ceramic (Empress Esthetic (EE)) with two different (glazed (G); polished (P)) surface preparations. A total of 90 IRC and 120 ceramic discs, 8 mm in diameter and 2 mm thick, were prepared. E2 and EE specimens were randomly divided into two groups (n = 30). One group was glazed (GE2; GEE), while the other group was polished (PE2; PEE) the same as the IRCs. The specimens in each group were subsequently divided into three subgroups: control (C), DT, and TP. R a (μm) was evaluated with a profilometer. Data were analyzed by Kruskal Wallis, followed by the Dunn's multiple comparison tests (P < 0.05). DT and TP resulted in significant surface roughening for TES, GRD, and EST, while no significant differences were detected between DT and TP (P > 0.05). PE2 and PEE were not affected by DT or TP (P > 0.05), while GE2 and GEE exhibited significant roughening after TP (P < 0.05). Surface roughness of IRCs and glazed ceramics can be affected by PPP applications. PMID:24729757

Elevated Temperature Fatigue Endurance of Three Ceramic Matrix Composites

NASA Technical Reports Server (NTRS)

Kalluri, Sreeramesh; Verrilli, Michael J.

2007-01-01

High-cycle fatigue endurance of three candidate materials for the acoustic liners of the Enabling Propulsion Materials Nozzle Program was investigated. The ceramic matrix composite materials investigated were N720/AS (Nextel 720, 3M Corporation), Sylramic S200 (Dow Corning), and UT 22. High-cycle fatigue tests were conducted in air at 910 C on as-machined specimens and on specimens subjected to tensile cyclic load excursions every 160 hr followed by thermal exposure at 910 C in a furnace up to total exposure times of 2066 and 4000 hr. All the fatigue tests were conducted in air at 100 Hz with a servohydraulic test machine. In the as-machined condition, among the three materials investigated only the Sylramic S200 exhibited a deterministic type of high-cycle fatigue behavior. Both the N720/AS and UT-22 exhibited significant scatter in the experimentally observed high-cycle fatigue lives. Among the thermally exposed specimens, N720/AS and Sylramic S200 materials exhibited a reduction in the high-cycle fatigue lives, particularly at the exposure time of 4000 hr.

Detecting Damage in Ceramic Matrix Composites Using Electrical Resistance

NASA Technical Reports Server (NTRS)

Smith, Craig E.; Gyekenyesi, Andrew

2011-01-01

The majority of damage in SiC/SiC ceramic matrix composites subjected to monotonic tensile loads is in the form of distributed matrix cracks. These cracks initiate near stress concentrations, such as 90 deg fiber tows or large matrix pores and continue to accumulate with additional stress until matrix crack saturation is achieved. Such damage is difficult to detect with conventional nondestructive evaluation techniques (immersion ultrasonics, x-ray, etc.). Monitoring a specimen.s electrical resistance change provides an indirect approach for monitoring matrix crack density. Sylramic-iBN fiber- reinforced SiC composites with a melt infiltrated (MI) matrix were tensile tested at room temperature. Results showed an increase in resistance of more than 500% prior to fracture, which can be detected either in situ or post-damage. A relationship between resistance change and matrix crack density was also determined.

Detecting Cracks in Ceramic Matrix Composites by Electrical Resistance

NASA Technical Reports Server (NTRS)

Smith, Craig; Gyekenyesi, Andrew

2011-01-01

The majority of damage in SiC/SiC ceramic matrix composites subjected to monotonic tensile loads is in the form of distributed matrix cracks. These cracks initiate near stress concentrations, such as 90o fiber tows or large matrix pores and continue to accumulate with additional stress until matrix crack saturation is achieved. Such damage is difficult to detect with conventional nondestructive evaluation techniques (immersion ultrasonics, x-ray, etc.). Monitoring a specimen.s electrical resistance change provides an indirect approach for monitoring matrix crack density. Sylramic-iBN fiber- reinforced SiC composites with a melt infiltrated (MI) matrix were tensile tested at room temperature. Results showed an increase in resistance of more than 500% prior to fracture, which can be detected either in situ or post-damage. A relationship between resistance change and matrix crack density was also determined.

A test for interfacial effects and stress transfer in ceramic matrix composites

NASA Technical Reports Server (NTRS)

1988-01-01

A test specimen was devised for measuring stress transfer between a high modulus fiber and a ceramic matrix. Single filaments of SiC were embedded in chemically vapor deposited SiC on a thin plate of molybdenum. The CVD overcoating which encapsulated the fiber was continuous with a coating of SiC on the molybdenum. When placed in a microtensile test device and loaded in the fiber direction, the fiber fracture characteristics provide information on the fiber/matrix adhesion and stress transfer. Problems were encountered due to the formation of a weak boundary between the SiC and the molybdenum which obviated any meaningful tensile tests. Also, the high CVD temperature used in fabricating these specimens restrict the fiber, matrix (and substrate) to materials having similar thermal coefficients of expansion in order to minimize thermal stresses.

Program For Evaluation Of Reliability Of Ceramic Parts

NASA Technical Reports Server (NTRS)

Nemeth, N.; Janosik, L. A.; Gyekenyesi, J. P.; Powers, Lynn M.

1996-01-01

CARES/LIFE predicts probability of failure of monolithic ceramic component as function of service time. Assesses risk that component fractures prematurely as result of subcritical crack growth (SCG). Effect of proof testing of components prior to service also considered. Coupled to such commercially available finite-element programs as ANSYS, ABAQUS, MARC, MSC/NASTRAN, and COSMOS/M. Also retains all capabilities of previous CARES code, which includes estimation of fast-fracture component reliability and Weibull parameters from inert strength (without SCG contributing to failure) specimen data. Estimates parameters that characterize SCG from specimen data as well. Written in ANSI FORTRAN 77 to be machine-independent. Program runs on any computer in which sufficient addressable memory (at least 8MB) and FORTRAN 77 compiler available. For IBM-compatible personal computer with minimum 640K memory, limited program available (CARES/PC, COSMIC number LEW-15248).

Silicone Disclosing Material used after Ceramic Surface Treatment Reduces Bond Strength.

PubMed

Fraga, Sara; Oliveira, Sara Cioccari; Pereira, Gabriel Kalil Rocha; Beekman, Pieter; Rippe, Marília Pivetta; Kleverlaan, Cornelis J

To evaluate the effect of a silicone disclosing procedure performed at different timepoints on the shear bond strength (SBS) of cements (self-adhesive composite cement, self-etch composite cement, resin-reinforced glass-ionomer cement) to different substrates (zirconia, lithium disilicate, bovine dentin). The substrate/cement combinations were assigned to two groups (n = 15) according to the timepoint, at which the vinyl polyether silicone disclosing agent was applied: after (experimental groups, EXP) or before (control groups, CTRL) specific micromechanical treatments of the substrate surface. To increase standardization, the cements were applied into rubber rings (2.2 mm diameter x 1.0 mm thickness) positioned on the substrate surface. After luting procedures, all specimens were stored in 37°C distilled water for 24 h, then subjected to SBS testing using a wire loop of 0.2 mm diameter at a crosshead speed of 1 mm/min until failure. Failure analysis was performed for all tested specimens. SBS data were submitted to Weibull analysis. The silicone disclosing procedure performed after micromechanical surface treatment reduced the characteristic shear bond strength to zirconia and lithium disilicate when compared to CTRL. However, for dentin specimens, there was no significant difference between CTRL and EXP for any of the cements investigated. Failure analysis showed a predominance of interfacial failures. The silicone disclosing procedure performed after the micromechanical treatment of ceramic surfaces negatively affected the cement bond strength. Therefore, after using it to check the fit of a prosthesis, clinicians should carefully clean the ceramic surface.

A Nonlinear Viscoelastic Model for Ceramics at High Temperatures

NASA Technical Reports Server (NTRS)

Powers, Lynn M.; Panoskaltsis, Vassilis P.; Gasparini, Dario A.; Choi, Sung R.

2002-01-01

High-temperature creep behavior of ceramics is characterized by nonlinear time-dependent responses, asymmetric behavior in tension and compression, and nucleation and coalescence of voids leading to creep rupture. Moreover, creep rupture experiments show considerable scatter or randomness in fatigue lives of nominally equal specimens. To capture the nonlinear, asymmetric time-dependent behavior, the standard linear viscoelastic solid model is modified. Nonlinearity and asymmetry are introduced in the volumetric components by using a nonlinear function similar to a hyperbolic sine function but modified to model asymmetry. The nonlinear viscoelastic model is implemented in an ABAQUS user material subroutine. To model the random formation and coalescence of voids, each element is assigned a failure strain sampled from a lognormal distribution. An element is deleted when its volumetric strain exceeds its failure strain. Element deletion has been implemented within ABAQUS. Temporal increases in strains produce a sequential loss of elements (a model for void nucleation and growth), which in turn leads to failure. Nonlinear viscoelastic model parameters are determined from uniaxial tensile and compressive creep experiments on silicon nitride. The model is then used to predict the deformation of four-point bending and ball-on-ring specimens. Simulation is used to predict statistical moments of creep rupture lives. Numerical simulation results compare well with results of experiments of four-point bending specimens. The analytical model is intended to be used to predict the creep rupture lives of ceramic parts in arbitrary stress conditions.

Long-term Bond Strength between Layering Indirect Composite Material and Zirconia Coated with Silicabased Ceramics.

PubMed

Fushiki, Ryosuke; Komine, Futoshi; Honda, Junichi; Kamio, Shingo; Blatz, Markus B; Matsumura, Hideo

2015-06-01

This study evaluated the long-term shear bond strength between an indirect composite material and a zirconia framework coated with silica-based ceramics, taking the effect of different primers into account. A total of 165 airborne-particle abraded zirconia disks were subjected to one of three pretreatments: no pretreatment (ZR-AB), airborne-particle abrasion of zirconia coated with feldspathic porcelain (ZR-PO-AB), and 9.5% hydrofluoric acid etching of zirconia coated with feldspathic porcelain (ZR-PO-HF). An indirect composite material (Estenia C&B) was then bonded to the zirconia disks after they were treated with one of the following primers: Clearfil Photo Bond (CPB), Clearfil Photo Bond with Clearfil Porcelain Bond Activator (CPB + Activator), Estenia Opaque Primer (EOP), Porcelain Liner M Liquid B (PLB), or no priming (CON, control group). Shear bond strength was tested after 100,000 thermocycles, and the data were analyzed using the Steel-Dwass U-test (α = 0.05). For ZR-PO-AB and ZR-PO-HF specimens, bond strength was highest in the CPB+Activator group (25.8 MPa and 22.4 MPa, respectively). Bond strengths were significantly lower for ZR-AB specimens in the CON and PLB groups and for ZR-PO-AB specimens in the CON, CPB, and EOP groups. Combined application of a hydrophobic phosphate monomer (MDP) and silane coupling agent enhanced the long-term bond strength of indirect composite material to a zirconia coated with silica-based ceramics.

Passivation Behavior of Ultrafine-Grained Pure Copper Fabricated by Accumulative Roll Bonding (ARB) Process

NASA Astrophysics Data System (ADS)

Fattah-alhosseini, Arash; Imantalab, Omid

2016-01-01

In this study, passivation behavior of ultrafine-grained (UFG) pure copper fabricated by ARB process in 0.01 M borax solution has been investigated. Before any electrochemical measurements, evaluation of microstructure was obtained by transmission electron microscopy (TEM). TEM observations revealed that with increasing the number of ARB passes, the grain size of specimens decrease. Also, TEM images showed that UFGs with average size of below 100 nm appeared after 7 passes of ARB. To investigate the passivation behavior of the specimens, electrochemical impedance spectroscopy (EIS) and Mott-Schottky analysis was carried out. For this purpose, three potentials within the passive region were chosen for potentiostatic passive film growth. EIS results showed that both passive film and charge-transfer resistance increases with increasing the number of ARB passes. Moreover, Mott-Schottky analysis revealed that with increasing the number of ARB passes, the acceptor density of the passive films decreased. In conclusion, increasing the number of ARB passes offers better conditions for forming the passive films with higher protection behavior, due to the growth of a much thicker and less defective films.

Radiation effects in cubic zirconia: A model system for ceramic oxides

NASA Astrophysics Data System (ADS)

Thomé, L.; Moll, S.; Sattonnay, G.; Vincent, L.; Garrido, F.; Jagielski, J.

2009-06-01

Ceramics are key engineering materials for electronic, space and nuclear industry. Some of them are promising matrices for the immobilization and/or transmutation of radioactive waste. Cubic zirconia is a model system for the study of radiation effects in ceramic oxides. Ion beams are very efficient tools for the simulation of the radiations produced in nuclear reactors or in storage form. In this article, we summarize the work made by combining advanced techniques (RBS/C, XRD, TEM, AFM) to study the structural modifications produced in ion-irradiated cubic zirconia single crystals. Ions with energies in the MeV-GeV range allow exploring the nuclear collision and electronic excitation regimes. At low energy, where ballistic effects dominate, the damage exhibits a peak around the ion projected range; it accumulates with a double-step process by the formation of a dislocation network. At high energy, where electronic excitations are favored, the damage profiles are rather flat up to several micrometers; the damage accumulation is monotonous (one step) and occurs through the creation and overlap of ion tracks. These results may be generalized to many nuclear ceramics.

A Study on the Rheological and Mechanical Properties of Photo-Curable Ceramic/Polymer Composites with Different Silane Coupling Agents for SLA 3D Printing Technology.

PubMed

Song, Se Yeon; Park, Min Soo; Lee, Jung Woo; Yun, Ji Sun

2018-02-07

Silane coupling agents (SCAs) with different organofunctional groups were coated on the surfaces of Al₂O₃ ceramic particles through hydrolysis and condensation reactions, and the SCA-coated Al₂O₃ ceramic particles were dispersed in a commercial photopolymer based on interpenetrating networks (IPNs). The organofunctional groups that have high radical reactivity and are more effective in UV curing systems are usually functional groups based on acryl, such as acryloxy groups, methacrloxy groups, and acrylamide groups, and these silane coupling agents seem to improve interfacial adhesion and dispersion stability. The coating morphology and the coating thickness distribution of SCA-coated Al₂O₃ ceramic particles according to the different organofunctional groups were observed by FE-TEM. The initial dispersibility and dispersion stability of the SCA-coated Al₂O₃/High-temp composite solutions were investigated by relaxation NMR and Turbiscan. The rheological properties of the composite solutions were investigated by viscoelastic analysis and the mechanical properties of 3D-printed objects were observed with a nanoindenter.

Spectroscopic properties of Nd3+ doped transparent oxyfluoride glass ceramics.

PubMed

Yu, Yunlong; Chen, Daqin; Ma, En; Wang, Yuansheng; Hu, Zhongjian

2007-07-01

In this paper, the spectroscopic properties of Nd(3+) doped transparent oxyfluoride glass ceramics containing LaF(3) nano-crystals were systematically studied. The formation and distribution of LaF(3) nano-crystals in the glass matrix were investigated by X-ray diffraction (XRD) and transmission electron microscopy (TEM). Based on Judd-Ofelt theory, the intensity parameters Omega(t) (t=2, 4, 6), spontaneous emission probability, radiative lifetime, radiative quantum efficiency, width of the emission line and stimulated emission cross-section of Nd(3+) were evaluated. Particularly, the effect of Nd(3+) doping level on them was discussed. With the increase of Nd(3+) concentration in the glass ceramic, the experimental luminescence lifetime, radiative quantum efficiency and stimulated emission cross-section vary from 353.4 micros, 78.3% and 1.86 x 10(-20)cm(2) to 214.7 micros, 39.9% and 1.52 x 10(-20)cm(2), respectively. The comparative study of Nd(3+) spectroscopic parameters in different hosts suggests that the investigated glass ceramic system is potentially applicable as laser materials for 1.06 microm emission.

A Study on the Rheological and Mechanical Properties of Photo-Curable Ceramic/Polymer Composites with Different Silane Coupling Agents for SLA 3D Printing Technology

PubMed Central

Song, Se Yeon; Park, Min Soo; Lee, Jung Woo; Yun, Ji Sun

2018-01-01

Silane coupling agents (SCAs) with different organofunctional groups were coated on the surfaces of Al2O3 ceramic particles through hydrolysis and condensation reactions, and the SCA-coated Al2O3 ceramic particles were dispersed in a commercial photopolymer based on interpenetrating networks (IPNs). The organofunctional groups that have high radical reactivity and are more effective in UV curing systems are usually functional groups based on acryl, such as acryloxy groups, methacrloxy groups, and acrylamide groups, and these silane coupling agents seem to improve interfacial adhesion and dispersion stability. The coating morphology and the coating thickness distribution of SCA-coated Al2O3 ceramic particles according to the different organofunctional groups were observed by FE-TEM. The initial dispersibility and dispersion stability of the SCA-coated Al2O3/High-temp composite solutions were investigated by relaxation NMR and Turbiscan. The rheological properties of the composite solutions were investigated by viscoelastic analysis and the mechanical properties of 3D-printed objects were observed with a nanoindenter. PMID:29414912

Interfacial characterization of ceramic core materials with veneering porcelain for all-ceramic bi-layered restorative systems.

PubMed

Tagmatarchis, Alexander; Tripodakis, Aris-Petros; Filippatos, Gerasimos; Zinelis, Spiros; Eliades, George

2014-01-01

The aim of the study was to characterize the elemental distribution at the interface between all-ceramic core and veneering porcelain materials. Three groups of all-ceramic cores were selected: A) Glass-ceramics (Cergo, IPS Empress, IPS Empress 2, e-max Press, Finesse); B) Glass-infiltrated ceramics (Celay Alumina, Celay Zirconia) and C) Densely sintered ceramics (Cercon, Procera Alumina, ZirCAD, Noritake Zirconia). The cores were combined with compatible veneering porcelains and three flat square test specimens were produced for each system. The core-veneer interfaces were examined by scanning electron microscopy and energy dispersive x-ray microanalysis. The glass-ceramic systems showed interfacial zones reach in Si and O, with the presence of K, Ca, Al in core and Ca, Ce, Na, Mg or Al in veneer material, depending on the system tested. IPS Empress and IPS Empress 2 demonstrated distinct transitional phases at the core-veneer interface. In the glassinfiltrated systems, intermixing of core (Ce, La) with veneer (Na, Si) elements occurred, whereas an abrupt drop of the core-veneer elemental concentration was documented at the interfaces of all densely sintered ceramics. The results of the study provided no evidence of elemental interdiffusion at the core-veneer interfaces in densely sintered ceramics, which implies lack of primary chemical bonding. For the glass-containing systems (glassceramics and glass-infiltrated ceramics) interdiffusion of the glass-phase seems to play a critical role in establishing a primary bonding condition between ceramic core and veneering porcelain.

The Genomic Evolution of Prostate Cancer

DTIC Science & Technology

2017-06-01

This study is supported by the AACI Fellowship for Trans- lational Cancer Research and DOD Prostate Cancer Research Program PRTA (DVW) and the...degraded during post -mor- tem time before fixation, which is supported by the low quality of RNA from matched frozen tissue. A limitation of this study ...is that a portion of the study used autopsy specimens, which have already undergone some degree of post -mor- tem degradation prior to PAXgene and

Bond strength of selected composite resin-cements to zirconium-oxide ceramic

PubMed Central

Fons-Font, Antonio; Amigó-Borrás, Vicente; Granell-Ruiz, María; Busquets-Mataix, David; Panadero, Rubén A.; Solá-Ruiz, Maria F.

2013-01-01

Objectives: The aim of this study was to evaluate bond strengths of zirconium-oxide (zirconia) ceramic and a selection of different composite resin cements. Study Design: 130 Lava TM cylinders were fabricated. The cylinders were sandblasted with 80 µm aluminium oxide or silica coated with CoJet Sand. Silane, and bonding agent and/or Clearfil Ceramic Primer were applied. One hundred thirty composite cement cylinders, comprising two dual-polymerizing (Variolink II and Panavia F) and two autopolymerizing (Rely X and Multilink) resins were bonded to the ceramic samples. A shear test was conducted, followed by an optical microscopy study to identify the location and type of failure, an electron microscopy study (SEM and TEM) and statistical analysis using the Kruskal-Wallis test for more than two independent samples and Mann-Whitney for two independent samples. Given the large number of combinations, Bonferroni correction was applied (α=0.001). Results: Dual-polymerizing cements provided better adhesion values (11.7 MPa) than the autopolymerizing (7.47 MPa) (p-value M-W<0.001). The worst techniques were Lava TM + sandblasting + Silane + Rely X; Lava TM + sandblasting + Silane + Multilink and Lava TM + CoJet + silane + Multilink. Adhesive failure (separation of cement and ceramic) was produced at a lesser force than cohesive failure (fracture of cement) (p-value M-W<0.001). Electron microscopy confirmed that the surface treatments modified the zirconium-oxide ceramic, creating a more rough and retentive surface, thus providing an improved micromechanical interlocking between the cement and the ceramic. Key words:Shear bond strength, silica coating, surface treatment, zirconia ceramics, phosphate monomer. PMID:22926485

Luminescence of Er/Yb and Tm/Yb doped FAp nanoparticles and ceramics

NASA Astrophysics Data System (ADS)

Grigorjeva, L.; Smits, K.; Millers, D.; Jankoviča, Dz

2015-03-01

The nanoparticles of hydroxiapatite and fluorapatite doped with Er/Yb and Tm/Yb were synthesized and characterized by FTIR, XRD, SEM and TEM methods. The results of up-conversion luminescence studies were presented for the samples as prepared, annealed at 500°C and at 900-1000 °C. At annealing above 800°C the ceramic state was formed. It is shown that fluorapatite host is more appropriate than hydroxiapatite host for rare ions luminescence and up-conversion processes. The post preparing annealing of nanarticles significantly enhanced the luminescence intensity. The Tm/Yb doped fluorapatite shows intense up-conversion luminescence in 790-800 nm spectral region and is potentially useful for biomedical applications.

Effect of hydrogen peroxide on the three-dimensional polymer network in composites.

PubMed

Durner, Jürgen; Stojanovic, Marija; Urcan, Ebru; Spahl, Werner; Haertel, Ursula; Hickel, Reinhard; Reichl, Franx-Xaver

2011-06-01

Less data are available about the effects of hydrogen peroxide on the three-dimensional polymer network of polymerized composites. Therefore the study was performed to test the effects of hydrogen peroxide on the three-dimensional polymer network in composites. Polymerized specimens from Tetric Flow®, Tetric Ceram® and Filtek™ Supreme XT were bleached with Opalescence® PF 15% for 5h or PF 35% for 0.5h, respectively, and then stored in methanol for 1d and 7d. Controls were unbleached specimens. The eluates were analyzed by gas chromatography/mass spectrometry. More methacrylic acid (MAA), bisphenol-A (BPA), ethoxylated bisphenol-A-dimethacrylate (BisEMA), hydroquinone monomethyl ether (HQME), 1,10-decanediol dimethacrylate (DDDMA) and/or triethylene glycol dimethacrylate (TEGDMA) were eluted from bleached specimens compared with non bleached controls (1d). The highest DDDMA amount of 419.8 μmol/l was found in the eluates after 7d in Tetric Flow® specimens treated with PF 15. The highest HQME amount of 159.6 μmol/l was found in eluates from Tetric Ceram® specimens treated with PF after 7d. The highest TEGDMA amount of 178.7 μmol/l was found in eluates from Filtek™ Supreme XT specimens treated with PF 35 after 7d. Bleaching with hydrogen peroxide has an effect on the three-dimensional polymer network in polymerized composites leading to an increase in the release of unpolymerized monomers, additives and unspecific oxidative products. Copyright © 2011 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Behavior of ceramics at 1200 C in a simulated gas turbine environment

NASA Technical Reports Server (NTRS)

Sanders, W. A.; Probst, H. B.

1974-01-01

This report summarizes programs at the NASA Lewis Research Center evaluating several classes of commercial ceramics, in a high gas velocity burner rig simulating a gas turbine engine environment. Testing of 23 ceramics in rod geometry identified SiC and Si3N4 as outstanding in resistance to oxidation and thermal stress and identified the failure modes of other ceramics. Further testing of a group of 15 types of SiC and Si3N4 in simulated vane shape geometry has identified a hot pressed SiC, a reaction sintered SiC, and hot pressed Si3N4 as the best of that group. SiC and Si3N4 test specimens were compared on the basis of weight change, dimensional reductions, metallography, fluorescent penetrant inspection, X-ray diffraction analyses, and failure mode.

Stress Distribution and Damage Mode of Ceramic-Dentin Bilayer Systems

NASA Astrophysics Data System (ADS)

Kurtoglu, Cem; Demiroz, S. Suna; Mehmetov, Emirullah; Uysal, Hakan

The aim of this study was to evaluate the damage modes of ceramic systems bonded to dentin under Hertzian indentation. Single-cycle Hertzian contact test over 150-850 N load range was applied randomly to 210 ceramic-dentin bilayer disc specimens of zirconia or IPS Empress II -1 mm, -1.5 mm and of feldspathic porcelain -1 mm, -1.5 mm, -2 mm. Optical microscopy was employed for the identification of quasiplastic mode and radial cracks. Finite element analysis was used to analyze the stress distribution. Our results showed that the degree of damage in both modes evolved progressively and the origin changed with contact load. Stress location and value were consistent with the mechanical test results. It was concluded that microstructure and thickness of the material have a significant effect on the damage modes of ceramic layer systems.

Assessments of Fracture Toughness of Monolithic Ceramics-SEPB Versus SEVNB Methods

NASA Technical Reports Server (NTRS)

Choi, Sung R.; Gyekenyesi, John P.

2006-01-01

Fracture toughness of a total of 13 advanced monolithic ceramics including silicon nitrides, silicon carbide, aluminas, and glass ceramic was determined at ambient temperature by using both single edge precracked beam (SEPB) and single edge v-notched beam (SEVNB) methods. Relatively good agreement in fracture toughness between the two methods was observed for advanced ceramics with flat R-curves; whereas, poor agreement in fracture toughness was seen for materials with rising R-curves. The discrepancy in fracture toughness between the two methods was due to stable crack growth with crack closure forces acting in the wake region of cracks even in SEVNB test specimens. The effect of discrepancy in fracture toughness was analyzed in terms of microstructural feature (grain size and shape), toughening exponent in R-curve, and stable crack growth determined using back-face strain gaging.

Strength and Microstructure of Ceramics

DTIC Science & Technology

1989-11-01

processing defects (pores or inclusions), etc. Theoretically, flaws have been represented as scaled-down versions of large cracks, so that the...no spurious reflections. confirming that the defects were not microtwins, From the TEM evidence. alhing with corresponding observations of fault...Lawn Vol. 71. No. I Interfaces. can be viewred as high-energy planar defects . AS Such. V. Conclusions they represent favored sites for microcrack

Ceramic membrane by tape casting and sol-gel coating for microfiltration and ultrafiltration application

NASA Astrophysics Data System (ADS)

Das, Nandini; Maiti, H. S.

2009-11-01

Alumina membrane filters in the form of thin (0.3-0.8 mm) discs of 25-30 mm diameter suitable for microfiltration application have been fabricated by tape-casting technique. Further using this microfiltration membrane as substrate, boehmite sol coating was applied on it and ultrafiltration membrane with very small thickness was formed. The pore size of the microfiltration membrane could be varied in the range of 0.1-0.7 μm through optimisation of experimental parameter. In addition, each membrane shows a very narrow pore size distribution. The most important factor, which determines the pore size of the membrane, is the initial particle size and its distribution of the ceramic powder. The top thin ultrafiltration, boehmite layer was prepared by sol-gel method, with a thickness of 0.5 μm. Particle size of the sol was approximately 30-40 nm. The structure and formation of the layer was analysed through TEM. At 550 °C formation of the top layer was completed. The pore size of the ultrafiltration membrane measured from TEM micrograph was almost 10 nm. Results of microbial (Escherichia coli—smallest-sized water-borne bacteria) test confirm the possibility of separation through this membrane

Sealing glass-ceramics with near linear thermal strain, Part II: Sequence of crystallization and phase stability

DOE PAGES

Dai, Steve Xunhu; Rodriguez, Mark A.; Griego, James M.

2016-06-01

Here, the sequence of crystallization in a re-crystallizable lithium silicate sealing glass-ceramic Li 2O-SiO 2-Al 2O 3-K 2O-B 2O 3-P 2O 5-ZnO was analyzed by in situ high temperature X-ray diffraction (HTXRD). Glass-ceramic specimens have been subjected to a 2-stage heat treatment schedule, including rapid cooling from sealing temperature to a 1st hold temperature 650 °C, following by heating to a 2nd hold temperature of 810 °C. Notable growth and saturation of Quartz was observed at 650 °C (1st hold).

Two-layer thermal barrier coating. I - Effects of composition and temperature on oxidation behavior and failure

NASA Technical Reports Server (NTRS)

Stecura, Stephan

1989-01-01

The effects of 21 bond and 2 ceramic coating compositions on the specific mass gain, internal crack location at failure, and life of a two-layer thermal barrier coating (TBC) were studied by cyclic testing in a furnace. MAR-M 200 + Hf alloy specimens were completely coated with bond and thermal barrier (ceramic) coatings. Both coatings were applied by air plasma spray deposition. Cyclic test data were obtained at 1110, 1160, and 1220 deg C. The data show that the specific mass gain and the TBC life are significantly affected by the composition of the bond coating and the temperature and only slightly affected by the composition of the ceramic coating.

Durability Testing of Commercial Ceramic Materials

NASA Technical Reports Server (NTRS)

Schienle, J. L.

1996-01-01

Technical efforts by AlliedSignal Engines in DOE/NASA-funded project from February, 1978 through December, 1995 are reported in the fields ceramic materials for gas turbine engines and cyclic thermal durability testing. A total of 29 materials were evaluated in 40 cyclic oxidation exposure durability tests. Ceramic test bars were cyclically thermally exposed to a hot combustion environment at temperatures up to 1371 C (2500 F) for periods of up to 3500 hours, simulating conditions typically encountered by hot flowpath components in an automotive gas turbine engine. Before and after exposure, quarter-point flexure strength tests were performed on the specimens, and fractography examinations including scanning electron microscopy (SEM) were performed to determine failure origins.

Development of Ceramic Systems for High temperature Coatings

NASA Technical Reports Server (NTRS)

Eslamloo-Grami, Maryame

2003-01-01

Professor Eslamloo-Grami will synthesize ceramic powders of various compositions based on pyrochlore, perovskite, and magnetoplumbite structures by doping with various oxides. Sol-gel and combustion synthesis routes will be used for powder syntheses. The powders will be characterized for particle size, surface area, microstructure, sintering etc. Thermal conductivity of the hot pressed specimens will also be measured at various temperatures. At the end, a project report will be prepared describing in details the experimental methods, results, discussion, and future research.

Radiation-Thermal Sintering of Zirconia Powder Compacts Under Conditions of Bilateral Heating Using Beams of Low-Energy Electrons

NASA Astrophysics Data System (ADS)

Ghyngazov, S. A.; Frangulyan, T. S.; Chernyavskii, A. V.; Goreev, A. K.; Naiden, E. P.

2015-06-01

Comparative experiments on sintering zirconia ceramics are performed using colliding beams of low-energy electrons and under conditions of thermal heating. The density and microhardness of ceramic materials manufactured via different processes are determined. The use of a regime of bilateral heating by high-intensity,low-energy electron beams is shown to intensify the sintering process and yield material specimens with improved characteristics compared to those formed by thermal sintering.

Quantitative nondestructive evaluation of ceramic matrix composite by the resonance method

DOE Office of Scientific and Technical Information (OSTI.GOV)

Watanabe, T.; Aizawa, T.; Kihara, J.

The resonance method was developed to make quantitative nondestructive evaluation on the mechanical properties without any troublesome procedure. Since the present method is indifferent to the geometry of specimen, both monolithic and ceramic matrix composite materials in process can be evaluated in the nondestructive manner. Al{sub 2}O{sub 3}, Si{sub 3}N{sub 4}, SiC/Si{sub 3}N{sub 4}, and various C/C composite materials are employed to demonstrate the validity and effectiveness of the present method.

Intrinsic microstructure of Si/GaAs heterointerfaces fabricated by surface-activated bonding at room temperature

NASA Astrophysics Data System (ADS)

Ohno, Yutaka; Yoshida, Hideto; Takeda, Seiji; Liang, Jianbo; Shigekawa, Naoteru

2018-02-01

The intrinsic microstructure of Si/GaAs heterointerfaces fabricated by surface-activated bonding at room temperature is examined by plane-view transmission electron microscopy (TEM) and cross-sectional scanning TEM using damage-free TEM specimens prepared only by mechanochemical etching. The bonded heterointerfaces include an As-deficient crystalline GaAs layer with a thickness of less than 1 nm and an amorphous Si layer with a thickness of approximately 3 nm, introduced by the irradiation of an Ar atom beam for surface activation before bonding. It is speculated that the interface resistance mainly originates from the As-deficient defects in the former layer.

[Compatibility between high-strength dental ceramic (type A) and vintage AL veneering porcelain].

PubMed

Cui, Jun; Chao, Yong-lie; Meng, Yu-kun

2006-05-01

To investigate the interface bond strength and compatibility between High-Strength Dental Ceramic (type A) and Vintage AL veneering porcelain. Twenty bar-shape specimens (ten Vintage AL and ten Vitadur alpha) were fabricated, and shear test was conducted to determine the bond strength. A bilayered composite (1 mm core ceramic and 0.8 mm Vintage AL) was prepared and then fractured for scanning electron microscopy (SEM) and energy dispersive spectroscopy (EDS) analysis. Ten all-ceramic anterior crowns were fabricated and the temperatures of thermal shock resistance were tested. The mean values of the bond strength measured were (55.52 +/- 14.64) MPa and (59.37 +/- 13.93) MPa for Vintage AL and Vitadur alpha respectively (P>0.05). SEM showed tight connection between the High-Strength Dental Ceramic (type A) and the veneering porcelain. Element diffusion was also confirmed by energy dispersive spectroscopy (EDS) analysis. The temperature of thermal shock resistance of this system was (179 +/- 15) degrees C. Vintage AL veneering porcelain has good thermal and chemical compatibility with High-Strength Dental Ceramic (type A).

Aluminum alloy/alumina-based ceramic interactions

DOE Office of Scientific and Technical Information (OSTI.GOV)

Lebeau, T.; Strom-Olsen, J.O.; Gruzleski, J.E.

1995-07-01

Wetting experiments were performed on eutectic ZrO{sub 2}/Al{sub 2}O{sub 3} (ZA), ZrO{sub 2}/Al{sub 2}O{sub 3}/TiO{sub 2} (ZAT), and ZrO{sub 2}/Al{sub 2}O{sub 3}/SiO{sub 2} (ZAS) ceramic substrates with different Al alloys. Four major variables were tested to study the wetting behavior of the different ceramic-metal systems. Variable include holding time, melt temperature, ally, and ceramic compositions. An experimental setup was designed to measure in situ contact angles using the sessile drop method. For any ceramic substrate, a temperature over 950 C was necessary to observe an equilibrium wetting angle of less than 90{degree} with pure Al; by alloying the aluminum, wettingmore » could be observed at lower temperatures ({theta} = 76--86{degree} at 900 C for Al-10 wt. % Si, {theta} {approximately}72{degree} at 850 C for Al-2.4 wt. % Mg) forming clean interfaces. Finally, ZAS specimens reacted with molten Al alloys over 900 C to produce Zr-Al based intermetallics at the metal-ceramic interface.« less

Detection of radiation-induced changes in electrochemical properties of austenitic stainless steels using miniaturized specimens and the single-loop electrochemical potentiokinetic reactivation method

DOE Office of Scientific and Technical Information (OSTI.GOV)

Inazumi, T.; Bell, G.E.C.; Kenik, E.A.

1993-01-01

Single-loop electrochemical potentiokinetic reactivation testing of miniaturized (TEM) specimens can provide reliable data comparable to data obtained with larger specimens. Significant changes in electrochemical properties (increased reactivation current and Flade potential) were detected for PCA and type 316 stainless steels irradiated at 200--420[degrees]C up to 7--9 dpa. Irradiations in the FFTF Materials Open Test Assembly and in the Oak Ridge Research Reactor are reported on. 45 figs., 5 tabs., 52 refs.

Detection of radiation-induced changes in electrochemical properties of austenitic stainless steels using miniaturized specimens and the single-loop electrochemical potentiokinetic reactivation method

DOE Office of Scientific and Technical Information (OSTI.GOV)

Inazumi, T.; Bell, G.E.C.; Kenik, E.A.

1993-01-01

Single-loop electrochemical potentiokinetic reactivation testing of miniaturized (TEM) specimens can provide reliable data comparable to data obtained with larger specimens. Significant changes in electrochemical properties (increased reactivation current and Flade potential) were detected for PCA and type 316 stainless steels irradiated at 200--420{degrees}C up to 7--9 dpa. Irradiations in the FFTF Materials Open Test Assembly and in the Oak Ridge Research Reactor are reported on. 45 figs., 5 tabs., 52 refs.

Development of a ceramic surface replacement for the hip. An experimental Sialon model.

PubMed

Clarke, I C; Phillips, W; McKellop, H; Coster, I R; Hedley, A; Amstutz, H C

1979-01-01

The objective of this study was to investigate the design and fixation advantages of Sialon ceramic surface replacements implanted without acrylic bone cement. The biocompatibility and friction and wear properties of Sialon ceramic were compared with more conventional prosthetic materials such as stainless steel and alumina. A functional load-bearing canine hip surface replacement model was established to test Sialon femoral cups designed for fixation by bone ingrowth. The results of the polyethylene wear tests on highly polished ceramic and stainless steel counterfaces were essentially similar. These laboratory data indicated that the in-vivo polyethylene wear performance on metal or ceramic prosthetic surfaces could be expected to be indistinguishable, i.e. the ceramic/polyethylene combination would not offer any improved wear resistance in-vivo. It was found possible to get bone ingrowth into the macrokeying areas of the ceramic femoral cups but not into the microporous surfaces due to the presence of a fibrous membrane lining their internal surfaces. The biocompatability specimens also appeared to be invested with a fibrous membrane. Further studies are under way to determine the relationship between reaming procedures, micro motion at the interfaces and Sialon biocompatibility.

Correlative Magnetic Imaging of Heat-Assisted Magnetic Recording Media in Cross Section Using Lorentz TEM and MFM

DOE PAGES

Kim, Taeho Roy; Phatak, Charudatta; Petford-Long, Amanda K.; ...

2017-10-23

In order to increase the storage density of hard disk drives, a detailed understanding of the magnetic structure of the granular magnetic layer is essential. Here, we demonstrate an experimental procedure of imaging recorded bits on heat-assisted magnetic recording (HAMR) media in cross section using Lorentz transmission electron microscopy (TEM). With magnetic force microscopy and focused ion beam (FIB), we successfully targeted a single track to prepare cross-sectional TEM specimens. Then, we characterized the magnetic structure of bits with their precise location and orientation using Fresnel mode of Lorentz TEM. Here, this method can promote understanding of the correlation betweenmore » bits and their material structure in HAMR media to design better the magnetic layer.« less

Correlative Magnetic Imaging of Heat-Assisted Magnetic Recording Media in Cross Section Using Lorentz TEM and MFM

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kim, Taeho Roy; Phatak, Charudatta; Petford-Long, Amanda K.

In order to increase the storage density of hard disk drives, a detailed understanding of the magnetic structure of the granular magnetic layer is essential. Here, we demonstrate an experimental procedure of imaging recorded bits on heat-assisted magnetic recording (HAMR) media in cross section using Lorentz transmission electron microscopy (TEM). With magnetic force microscopy and focused ion beam (FIB), we successfully targeted a single track to prepare cross-sectional TEM specimens. Then, we characterized the magnetic structure of bits with their precise location and orientation using Fresnel mode of Lorentz TEM. Here, this method can promote understanding of the correlation betweenmore » bits and their material structure in HAMR media to design better the magnetic layer.« less

Ferroelectric and Piezoelectric Properties of KNbO3 Ceramics Containing Small Amounts of LaFeO3

NASA Astrophysics Data System (ADS)

Kakimoto, Ken-ichi; Masuda, Izumi; Ohsato, Hitoshi

2003-09-01

Dense KNbO3 ceramics have been successfully synthesized by pressure-less sintering under optimized heat-treatment conditions using a small amount of La2O3 and Fe2O3 additives. KNbO3 forms (K1-xLax)(Nb1-xFex)O3 solid solutions and changes in the crystal system, depending on the additive content, from orthorhombic to tetragonal at x of 0.020, and from tetragonal to cubic at x of 0.200 or higher. When only 0.002 mol of La2O3 and Fe2O3 (x=0.002) was added into KNbO3, the highest value (98.8%) of the theoretical density was obtained. This specimen showed orthorhombic symmetry with a high Curie temperature of 420°C, and demonstrated a well-saturated ferroelectric hysteresis loop with large remanent polarization (Pr) of 18 μC/cm2, which is comparable to the value reported for pure KNbO3 ceramics fabricated by hot pressing. Furthermore, the x=0.002 specimen showed a planar electromechanical coupling ratio (kp) of 0.17 and piezoelectric d33 constant of 98 pC/N, regardless of the unsaturated poling state.

Electric properties of a textured BiNaKTiO3 ceramic for energy harvesting system

NASA Astrophysics Data System (ADS)

Lim, D. H.; Song, T. K.; Lee, D. S.; Jeong, S. J.; Kim, Min-Soo; Song, Jae-Sung

2012-01-01

Piezoelectric ceramics with microstructural texturing were fabricated and evaluated to investigate their possibility for use in piezoelectric energy harvest devices in response to external mechanical impact. The microstructural evolution and properties of a Bi0.5(Na0.425K0.075) TiO3 (BNKT) ceramic material with platelike Bi4Ti3O12 (BiT) were investigated. The platelike Bi4Ti3O12 (BiT) was used as a template to induce grain growth under a proper heat treatment. The textured BNKTs were fabricated and heated at 1150 °C for 10 h. They exhibited <001>-oriented large grains and improved of ferroelectric properties. The textured microstructure was due to the occurrence of grain growth around the templates. When subjected to a low stress of 0.8 MPa, the textured BNKT had a slightly larger voltage and power than the randomly-oriented BNKT. Meanwhile, when high stresses over 2 MPa were applied, the voltage and the power of the textured specimen were larger than those of the randomly-oriented specimen. The microstructure textured along the <100> direction may contribute to the improved power generation.

Plasma etching a ceramic composite. [evaluating microstructure

NASA Technical Reports Server (NTRS)

Hull, David R.; Leonhardt, Todd A.; Sanders, William A.

1992-01-01

Plasma etching is found to be a superior metallographic technique for evaluating the microstructure of a ceramic matrix composite. The ceramic composite studied is composed of silicon carbide whiskers (SiC(sub W)) in a matrix of silicon nitride (Si3N4), glass, and pores. All four constituents are important in evaluating the microstructure of the composite. Conventionally prepared samples, both as-polished or polished and etched with molten salt, do not allow all four constituents to be observed in one specimen. As-polished specimens allow examination of the glass phase and porosity, while molten salt etching reveals the Si3N4 grain size by removing the glass phase. However, the latter obscures the porosity. Neither technique allows the SiC(sub W) to be distinguished from the Si3N4. Plasma etching with CF4 + 4 percent O2 selectively attacks the Si3N4 grains, leaving SiC(sub W) and glass in relief, while not disturbing the pores. An artifact of the plasma etching reaction is the deposition of a thin layer of carbon on Si3N4, allowing Si3N4 grains to be distinguished from SiC(sub W) by back scattered electron imaging.

[Effect of silicon coating on bonding strength of ceramics and titanium].

PubMed

Zhou, Shu; Wang, Yu; Zhang, Fei-Min; Guang, Han-Bing

2009-06-01

This study investigated the effect of silicon coating (SiO2) by solution-gelatin (Sol-Gel) technology on bonding strength of titanium and ceramics. Sixteen pure titanium specimens with the size of 25 mm x 3 mm x 0.5 mm were divided into two groups (n=8), test group was silicon coated by Sol-Gel technology, the other one was control group. The middle area of the samples were veneered with Vita Titankeramik system, the phase composition of two specimens were characterized by X-ray diffraction (XRD). The bonding strength of titanium/porcelain was evaluated using three-point bending test. The interface of titanium and porcelain and fractured titanium surface were investigated by scanning electron microscope (SEM) with energy depressive spectrum (EDS). Contents of surface silicon increased after modification with silicon coated by Sol-Gel technology. The mean bonding strength of test group and control group were (37.768 +/- 0.777) MPa and (29.483 +/- 1.007) MPa. There was a statistically significant difference (P=0.000) between them. The bonded ceramic boundary of test group was wider than control group. Silicon coating by Sol-Gel technology was significant in improving bonding strength of titanium/Vita Titankeramik system.

Marginal and Internal Discrepancies of Posterior Zirconia-Based Crowns Fabricated with Three Different CAD/CAM Systems Versus Metal-Ceramic.

PubMed

Ortega, Rocio; Gonzalo, Esther; Gomez-Polo, Miguel; Suárez, María J

2015-01-01

The aim of this study was to analyze the marginal and internal fit of metalceramic and zirconia-based crowns. Forty standardized steel specimens were prepared to receive posterior crowns and randomly divided into four groups (n = 10): (1) metal-ceramic, (2) NobelProcera Zirconia, (3) Lava Zirconia, and (4) VITA In-Ceram YZ. All crowns were cemented with glass-ionomer agent and sectioned buccolingually. A scanning electron microscope was used for measurements. Kruskal-Wallis and Wilcoxon signed rank test (α = .05) statistical analyses were conducted. Significant differences (P < .0001) in marginal discrepancies were observed between metal-ceramic and zirconia groups. No differences were found for the axial wall fit (P = .057). Significant differences were shown among the groups in discrepancies at the occlusal cusp (P = .0012) and at the fossa (P = .0062). No differences were observed between surfaces. All zirconia groups showed better values of marginal discrepancies than the metal-ceramic group. Procera Zirconia showed the lowest gaps.

Dependence of microwave dielectric properties on crystallization behaviour of CaMgSi{sub 2}O{sub 6} glass-ceramics

DOE Office of Scientific and Technical Information (OSTI.GOV)

Choi, Bo Kyeong; Jang, Sung Wook; Kim, Eung Soo, E-mail: eskim@kyonggi.ac.kr

2015-07-15

The effects of the crystallization behaviour of CaMgSi{sub 2}O{sub 6} (diopside) glass-ceramics on their microwave dielectric properties were investigated as functions of the Cr{sub 2}O{sub 3} content and heat-treatment method used (one or two steps). The crystallization behaviours of the specimens were affected by the Cr{sub 2}O{sub 3} content as well as by the heat-treatment method employed, and were evaluated using X-ray diffraction and the combined Rietveld and reference intensity ratio (RIR) method. The dielectric constants (K) of the specimens did not change significantly with an increase in the Cr{sub 2}O{sub 3} content. The quality factor (Qf) of the specimensmore » increased for Cr{sub 2}O{sub 3} contents of up to 0.5 wt% Cr{sub 2}O{sub 3}, but then decreased for higher contents. These results could be attributed to the degree of crystallization. For the same Cr{sub 2}O{sub 3} content, the specimens that underwent a two-step heat treatment showed lower K values and higher Qf values than those heat-treated in one-step. These results could be attributed to the smaller crystallite size and higher degree of crystallization in the specimens obtained from the two-step heat treatment compared with those of the specimens heat-treated in one-step method.« less

Titanium Nitride: An Oxidizable Coating for the High-Temperature Protection of Graphite

NASA Technical Reports Server (NTRS)

Wakelyn, N. T.

1961-01-01

A titanium nitride coating for graphite, prepared by deposition process, protected test specimens for 60 seconds the vapors in a supersonic ceramic-heated air jet with a stagnation temperature of approximately 2,250 K. For the same test conditions, coated specimens showed no damage to the graphite body for the 60-second test, whereas uncoated specimens were very severely damaged after 20 seconds and were destroyed toward the end of the test. A discussion of the coating of these graphite specimens and of some of the conditions necessary for the utilization of oxidizable substances as oxidation-protective coatings for bodies facing high convective heat transfer in the atmosphere is presented.

Reduction-oxidation Enabled Glass-ceramics to Stainless Steel Bonding Part I: screening of doping oxidants

DOE Office of Scientific and Technical Information (OSTI.GOV)

Dai, Steve Xunhu

Lithium silicate-based glass-ceramics with high coefficients of thermal expansion, designed to form matched hermetic seals in 304L stainless steel housing, show little evidence of interfacial chemical bonding, despite extensive inter-diffusion at the glass-ceramic-stainless steel (GC-SS) interface. A series of glass-ceramic compositions modified with a variety of oxidants, AgO, FeO, NiO, PbO, SnO, CuO, CoO, MoO 3 and WO 3, are examined for the feasibility of forming bonding oxides through reduction-oxidation (redox) at the GC-SS interface. The oxidants were selected according to their Gibbs free energy to allow for oxidation of Cr/Mn/Si from stainless steel, and yet to prevent a reductionmore » of P2O5 in the glass-ceramic where the P 2O 5 is to form Li 3PO 4 nuclei for growth of high expansion crystalline SiO 2 phases. Other than the CuO and CoO modified glass-ceramics, bonding from interfacial redox reactions were not achieved in the modified glass-ceramics, either because of poor wetting on the stainless steel or a reduction of the oxidants at the surface of glass-ceramic specimens rather than the GC-SS interface.« less

[Effect of the thickness of reinforced glass ceramics on the degree of conversion of dual-cure resin cements].

PubMed

Zhu, Lin-Lin; Qiu, Li-Hong; Liu, Li-Yang; Li, Xiao-Lin

2017-10-01

To determine the effect of the thickness of reinforced glass ceramics on the degree of conversion (DC) of three dual-cure resin cements (Multilink N, RelyX Ultimate and NX3-Nexus). Upcera reinforced glass ceramics and IPS e.max CAD test specimen were processed, with different thickness, transmittance was tested by ultraviolet and visible spectrometer. The DC was evaluated using Fourier transform infrared (FT-IR) spectrometer, then the degree of conversion of polymerization before and after curing was calculated. SPSS 21.0 software package was used for data analysis. Transmittance decreased along with the thickness of reinforced glass ceramics increased. At 2 mm -thickness transmittance of upcera lithium disilicate glass ceramics was superior to IPS e.max CAD. The DC of dual-cured resin cement was decreased with the increase of thickness. At the same 2 mm group, the DC of Multilink N and RelyX Ultimate under upcera lithium disilicate glass ceramics were superior to that under IPS e.max CAD groups. At 2 mm-thickness transmittance of upcera lithium disilicate glass ceramics was superior to IPS e.max CAD. At the same 2 mm group, the DC of Multilink N and RelyX Ultimate under upcera lithium disilicate glass ceramics were superior to that under IPS e.max CAD groups.

Intensity of the Earth's magnetic field in Greece during the last five millennia: New data from Greek pottery

NASA Astrophysics Data System (ADS)

Tema, Evdokia; Gómez-Paccard, Miriam; Kondopoulou, Despina; Almar, Ylenia

2012-08-01

New archaeointensity results have been obtained from the study of four ceramic collections coming from four different archaeological sites in Greece. The ages of the ceramic fragments, based on archaeological constrains and radiocarbon analysis, range from 2200 BC to 565 AD. Low-field magnetic susceptibility versus temperature reveals a good thermal stability for most of the samples. However, for some samples the thermomagnetic curves are not reversible indicating mineralogical changes during heating. Isothermal remanent magnetisation (IRM) acquisition curves and thermal demagnetisation of three orthogonal IRM components have also been performed. The rock magnetic results identify magnetite and/ or Ti-magnetite as the main magnetic carriers in the studied samples. Classical Thellier experiments with regular partial thermoremanent magnetisation (pTRM) checks have been conducted on 125 specimens belonging to 34 independent ceramic fragments. Only 61 archaeointensity determinations (at specimen level) that correspond to linear NRM-TRM plots were used for the calculation of the site mean archaeointensities. The effect of the anisotropy of the thermoremanent magnetisation (TRM) and cooling rate upon TRM intensity acquisition have been investigated in all specimens. The maximum difference between the TRM anisotropy corrected and uncorrected intensities is around 30% at specimen level confirming that the TRM effect can be very important in ceramic samples. Cooling rate correction factors determined per specimen are up to 10% with only one exception that reaches 35%. Despite the moderate success rate of archaeointensity determination (around 50%) reliable mean site intensities have been obtained, with in situ intensities ranging from 53.6 ± 4.1 to 69.3 ± 3.9 μT, corresponding to virtual axial dipole moments from 9.2 ± 0.7 to 11.9 ± 0.7 × 1022 Am2. The new data are reasonably consistent with other available data for the studied region as well as with the SV reference curves for Greece and the South Balkan Peninsula, and the regional and global geomagnetic field models. Combined with previously published data from the area, they confirm that important changes of the Earth's magnetic field intensity occurred in Greece during the last five millennia. For some periods, the available archaeointensity data for the Balkan area show a large dispersion, even for data corresponding to high quality intensity standards, whereas for other periods their limited number prevents an accurate description of geomagnetic field intensity changes. This evidences the need of new reliable and well dated archaeointensity data in order to obtain a robust description of geomagnetic field intensity changes during the last five millennia in this area.

High temperature tensile testing of ceramic composites

NASA Technical Reports Server (NTRS)

Gyekenyesi, John Z.; Hemann, John H.

1988-01-01

The various components of a high temperature tensile testing system are evaluated. The objective is the high temperature tensile testing of SiC fiber reinforced reaction bonded Si3N4 specimens at test temperatures up to 1650 C (3000 F). Testing is to be conducted in inert gases and air. Gripping fixtures, specimen configurations, furnaces, optical strain measuring systems, and temperature measurement techniques are reviewed. Advantages and disadvantages of the various techniques are also noted.

Effect of hydrofluoric acid surface treatments on micro-shear bond strength of CAD/CAM ceramics

PubMed Central

Mokhtarpour, Faraneh; Alaghehmand, Homayoon; Khafri, Soraya

2017-01-01

Introduction Dental ceramics are appreciated as highly esthetic restorative materials that can simulate the appearance of natural dentition better than other materials. The aim of this study was to evaluate the effect of hydrofluoric acid concentration and etching time on micro-shear bond strength (μSBS) to IPS e.max CAD and Vita Mark II of a dual cured resin cement (Panavia F2.0). Methods This study was an experimental in vitro study, performed in the dental material research center of Babol University of Medical Sciences in 2016. Two hydrofluoric acid concentrations (5% and 10%) and three different etching times (20, 60 and 120 seconds) were used to etch the specimens respectively. A silane coupling agent (Clearfil porcelain activator) and priming and bonding agent (Clearfil SE bond) were used on the etched surfaces in accordance to the manufacturer’s instructions of use. Then resin cement was applied on the prepared ceramic surfaces and light cured. μSBS between resin cement and the porcelains were measured with a universal testing machine. Mode of failure was observed with 40× magnification by means of a Stereo microscope. Data were analyzed with ANOVA and independent-samples t-test and Chi-square tests. Results In both e.max and Vita Mark II groups, μSBS were not significantly different when different etching times (one-way ANOVA) and HF acid concentrations (Independent-samples t-test) were used (p>0.05), but the highest μSBS was shown in e.max specimens etched 60 s with 5% HF and Vita Mark II specimens etched 20 s with 10% HF. μSBS of e.max was significantly higher than Vita Mark II (p=0.00). Conclusion Best surface treatment for e.max and Vita Mark II ceramics is 20 s etch using 5 % hydrofluoric acid. PMID:29238488

Characterization of 3D interconnected microstructural network in mixed ionic and electronic conducting ceramic composites

NASA Astrophysics Data System (ADS)

Harris, William M.; Brinkman, Kyle S.; Lin, Ye; Su, Dong; Cocco, Alex P.; Nakajo, Arata; Degostin, Matthew B.; Chen-Wiegart, Yu-Chen Karen; Wang, Jun; Chen, Fanglin; Chu, Yong S.; Chiu, Wilson K. S.

2014-04-01

The microstructure and connectivity of the ionic and electronic conductive phases in composite ceramic membranes are directly related to device performance. Transmission electron microscopy (TEM) including chemical mapping combined with X-ray nanotomography (XNT) have been used to characterize the composition and 3-D microstructure of a MIEC composite model system consisting of a Ce0.8Gd0.2O2 (GDC) oxygen ion conductive phase and a CoFe2O4 (CFO) electronic conductive phase. The microstructural data is discussed, including the composition and distribution of an emergent phase which takes the form of isolated and distinct regions. Performance implications are considered with regards to the design of new material systems which evolve under non-equilibrium operating conditions.The microstructure and connectivity of the ionic and electronic conductive phases in composite ceramic membranes are directly related to device performance. Transmission electron microscopy (TEM) including chemical mapping combined with X-ray nanotomography (XNT) have been used to characterize the composition and 3-D microstructure of a MIEC composite model system consisting of a Ce0.8Gd0.2O2 (GDC) oxygen ion conductive phase and a CoFe2O4 (CFO) electronic conductive phase. The microstructural data is discussed, including the composition and distribution of an emergent phase which takes the form of isolated and distinct regions. Performance implications are considered with regards to the design of new material systems which evolve under non-equilibrium operating conditions. Electronic supplementary information (ESI) available. See DOI: 10.1039/c3nr06684c

Swelling induced by alpha decay in monazite and zirconolite ceramics: A XRD and TEM comparative study

NASA Astrophysics Data System (ADS)

Deschanels, X.; Seydoux-Guillaume, A. M.; Magnin, V.; Mesbah, A.; Tribet, M.; Moloney, M. P.; Serruys, Y.; Peuget, S.

2014-05-01

Zirconolite and monazite matrices are potential ceramics for the containment of actinides (Np, Cm, Am, Pu) which are produced over the reprocessing of spent nuclear fuel. Actinides decay mainly through the emission of alpha particles, which in turn causes most ceramics to undergo structural and textural changes (amorphization and/or swelling). In order to study the effects of alpha decays on the above mentioned ceramics two parallel approaches were set up. The first involved the use of an external irradiation source, Au, which allowed the deposited recoil energy to be simulated. The second was based on short-lived actinide doping with 238Pu, (i.e. an internal source), via the incorporation of plutonium oxide into both the monazite and zirconolite structures during synthesis. In both types of irradiation experiments, the zirconolite samples became amorphous at room temperature with damage close to 0.3 dpa; corresponding to a critical dose of 4 × 1018 α g-1 (i.e. ∼1.3 × 1021 keV cm-3). Both zirconolite samples also showed the same degree of macroscopic swelling at saturation (∼6%), with ballistic processes being the predominant damaging effect. In the case of the monazite however, the macroscopic swelling and amorphization were dependent on the nature of the irradiation. Externally, (Au), irradiated samples became amorphous while also demonstrating a saturation swelling of up to 8%. In contrast to this, the swelling of the 238Pu doped samples was much smaller at ∼1%. Also, unlike the externally (Au) irradiated monazite these 238Pu doped samples remained crystalline up to 7.5 × 1018 α g-1 (0.8 dpa). XRD, TEM and swelling measurements were used to fully characterize and interpret this behavior. The low swelling and the conservation of the crystalline state of 238Pu doped monazite samples indicates that alpha annealing took place within this material.

Effect of Er:YAG Laser and Sandblasting in Recycling of Ceramic Brackets.

PubMed

Yassaei, Soghra; Aghili, Hossein; Hosseinzadeh Firouzabadi, Azadeh; Meshkani, Hamidreza

2017-01-01

Introduction: This study was performed to determine the shear bond strength of rebonded mechanically retentive ceramic brackets after recycling with Erbium-Doped Yttrium Aluminum Garnet (Er:YAG) laser or sandblasting. Methods: Twenty-eight debonded ceramic brackets plus 14 intact new ceramic brackets were used in this study. Debonded brackets were randomly divided into 2 groups of 14. One group was treated by Er:YAG laser and the other with sandblasting. All the specimens were randomly bonded to 42 intact human upper premolars. The shear bond strength of all specimens was determined with a universal testing machine at a crosshead speed of 0.5 mm/min until bond failure occurred. The recycled bracket base surfaces were observed under a scanning electron microscope (SEM). Analysis of variance (ANOVA) and Tukey tests were used to compare the shear bond strength of the 3 groups. Fisher exact test was used to evaluate the differences in adhesive remnant index (ARI) scores. Results: The highest bond strength belonged to brackets recycled by Sandblasting (16.83 MPa). There was no significant difference between the shear bond strength of laser and control groups. SEM photographs showed differences in 2 recycling methods. The laser recycled bracket appeared to have as well-cleaned base as the new bracket. Although the sandblasted bracket photographs showed no remnant adhesives, remarkable micro-roughening of the base of the bracket was apparent. Conclusion: According to the results of this study, both Er:YAG laser and sandblasting were efficient to mechanically recondition retentive ceramic brackets. Also, Er:YAG laser did not change the design of bracket base while removing the remnant adhesives which might encourage its application in clinical practice.

Effect of Er:YAG Laser and Sandblasting in Recycling of Ceramic Brackets

PubMed Central

Yassaei, Soghra; Aghili, Hossein; Hosseinzadeh Firouzabadi, Azadeh; Meshkani, Hamidreza

2017-01-01

Introduction: This study was performed to determine the shear bond strength of rebonded mechanically retentive ceramic brackets after recycling with Erbium-Doped Yttrium Aluminum Garnet (Er:YAG) laser or sandblasting. Methods: Twenty-eight debonded ceramic brackets plus 14 intact new ceramic brackets were used in this study. Debonded brackets were randomly divided into 2 groups of 14. One group was treated by Er:YAG laser and the other with sandblasting. All the specimens were randomly bonded to 42 intact human upper premolars. The shear bond strength of all specimens was determined with a universal testing machine at a crosshead speed of 0.5 mm/min until bond failure occurred. The recycled bracket base surfaces were observed under a scanning electron microscope (SEM). Analysis of variance (ANOVA) and Tukey tests were used to compare the shear bond strength of the 3 groups. Fisher exact test was used to evaluate the differences in adhesive remnant index (ARI) scores. Results: The highest bond strength belonged to brackets recycled by Sandblasting (16.83 MPa). There was no significant difference between the shear bond strength of laser and control groups. SEM photographs showed differences in 2 recycling methods. The laser recycled bracket appeared to have as well-cleaned base as the new bracket. Although the sandblasted bracket photographs showed no remnant adhesives, remarkable micro-roughening of the base of the bracket was apparent. Conclusion: According to the results of this study, both Er:YAG laser and sandblasting were efficient to mechanically recondition retentive ceramic brackets. Also, Er:YAG laser did not change the design of bracket base while removing the remnant adhesives which might encourage its application in clinical practice. PMID:28912939

Film Cooled Recession of SiC/SiC Ceramic Matrix Composites: Test Development, CFD Modeling and Experimental Observations

NASA Technical Reports Server (NTRS)

Zhu, Dongming; Sakowski, Barbara A.; Fisher, Caleb

2014-01-01

SiCSiC ceramic matrix composites (CMCs) systems will play a crucial role in next generation turbine engines for hot-section component applications because of their ability to significantly increase engine operating temperatures, reduce engine weight and cooling requirements. However, the environmental stability of Si-based ceramics in high pressure, high velocity turbine engine combustion environment is of major concern. The water vapor containing combustion gas leads to accelerated oxidation and corrosion of the SiC based ceramics due to the water vapor reactions with silica (SiO2) scales forming non-protective volatile hydroxide species, resulting in recession of the ceramic components. Although environmental barrier coatings are being developed to help protect the CMC components, there is a need to better understand the fundamental recession behavior of in more realistic cooled engine component environments.In this paper, we describe a comprehensive film cooled high pressure burner rig based testing approach, by using standardized film cooled SiCSiC disc test specimen configurations. The SiCSiC specimens were designed for implementing the burner rig testing in turbine engine relevant combustion environments, obtaining generic film cooled recession rate data under the combustion water vapor conditions, and helping developing the Computational Fluid Dynamics (CFD) film cooled models and performing model validation. Factors affecting the film cooled recession such as temperature, water vapor concentration, combustion gas velocity, and pressure are particularly investigated and modeled, and compared with impingement cooling only recession data in similar combustion flow environments. The experimental and modeling work will help predict the SiCSiC CMC recession behavior, and developing durable CMC systems in complex turbine engine operating conditions.

Extrusion shear strength between an alumina-based ceramic and three different cements.

PubMed

Borges, Gilberto Antonio; de Goes, Mario Fernando; Platt, Jeffrey A; Moore, Keith; de Menezes, Fernando Hueb; Vedovato, Euripedes

2007-09-01

Surface treatment is an essential step in bonding a ceramic to resin. Alumina ceramics are particularly difficult to prepare for adequate bonding to composite resin cements. The purpose of this study was to evaluate the bond strength between a densely sintered alumina ceramic and bovine dentin with 2 adhesive resin cements and a resin-modified glass ionomer cement using an extrusion shear strength test. Alumina cones (n=30), 4 mm in height, 3 mm in diameter at the small end, and with an 8-degree taper, were fabricated. Without any treatment, the cones were cemented in a standardized cavity in 2.5-mm-thick bovine dentin discs using 1 of 3 cement systems: Panavia F, RelyX ARC, or RelyX Luting. The cements were manipulated following the manufacturers' instructions. After 24 hours of storage at 37 degrees C, an extrusion shear test was performed in a universal testing machine at 0.5 mm/min until bonding failure. The data were analyzed using 1-way ANOVA and Tukey HSD test (alpha=.05). All fractured specimens were examined at x25 magnification and classified by fracture mode. Representative specimens were selected for SEM observation. The highest strength values were obtained with Panavia F, and they were significantly higher (P<.05) than each of the other 2 cements, which were not significantly different from each other. Panavia F resulted in predominantly mixed failure and RelyX ARC and RelyX Vitremer showed primarily adhesive failure. An MDP-containing adhesive system (Panavia F) provides better extrusion bond strength to a high-density alumina ceramic than a Bis-GMA resin luting agent system (RelyX ARC) or a resin-modified glass ionomer cement system (RelyX Luting).

Ceramic (Feldspathic & IPS Empress II) vs. laboratory composite (Gradia) veneers; a comparison between their shear bond strength to enamel; an in vitro study.

PubMed

Nikzad, S; Azari, Abbas; Dehgan, S

2010-07-01

Patient demand for aesthetic dentistry is steadily growing. Laminates and free metal restorations have evolved in an attempt to overcome the invasiveness nature of full veneer restorations. Although many different materials have been used for making these restorations, there is no single material that fits best for all purposes. Two groups of ceramic material (Feldspathic and IPS Empress II) and one group of laboratory composite (Gradia) discs (10 discs in each group; 4 mm in diameter and 2 mm in thickness) were prepared according to the manufacturer's instruction. The surface of ceramic discs were etched and silanized. In Gradia group, liquid primer was applied on composite surfaces. Thirty freshly extracted sound human molars and premolars were randomly divided into three groups. The enamel surface of each tooth was slightly flattened (0.3 mm) on the buccal or lingual side and then primed and cemented to the prepared discs with the aid of a dental surveyor. The finishing specimens were thermocycled between 5 degrees C and 55 degrees C for 2500 cycles and then prepared for shear bond strength testing. The resulting data were analyzed by one-way anova and Tukey HSD test. The fractured surfaces of each specimen were inspected by means of stereomicroscope and SEM. There is significant difference between the bond strength of materials tested. The mean bond strengths obtained with Feldspathic ceramic, IPS Empress II and Gradia were 33.10 +/- 4.31 MPa, 26.04 +/- 7.61 MPa and 14.42 +/- 5.82 MPa, respectively. The fracture pattern was mainly mixed for ceramic groups. More scientific evidence needed for standardization of bonding protocols.

Effect of the shades of background substructures on the overall color of zirconia-based all-ceramic crowns

PubMed Central

Tulapornchai, Chantana; Mamani, Jatuphol; Kamchatphai, Wannaporn; Thongpun, Noparat

2013-01-01

PURPOSE The objective of this study was to determine the effect of the color of a background substructure on the overall color of a zirconia-based all-ceramic crown. MATERIALS AND METHODS Twenty one posterior zirconia crowns were made for twenty subjects. Seven premolar crowns and six molar crowns were cemented onto abutments with metal post and core in the first and second group. In the third group, eight molar crowns were cemented onto abutments with a prefabricated post and composite core build-up. The color measurements of all-ceramic crowns were made before try-in, before and after cementation. A repeated measure ANOVA was used for a statistical analysis of a color change of all-ceramic crowns at α=.05. Twenty four zirconia specimens, with different core thicknesses (0.4-1 mm) were also prepared to obtain the contrast ratio of zirconia materials after veneering. RESULTS L*, a*, and b* values of all-ceramic crowns cemented either on a metal cast post and core or on a prefabricated post did not show significant changes (P>.05). However, the slight color changes of zirconia crowns were detected and represented by ΔE*ab values, ranging from 1.2 to 3.1. The contrast ratios of zirconia specimens were 0.92-0.95 after veneering. CONCLUSION No significant differences were observed between the L*, a*, and b* values of zirconia crowns cemented either on a metal cast post and core or a prefabricated post and composite core. However, the color of a background substructure could affect the overall color of posterior zirconia restorations with clinically recommended core thickness according to ΔE*ab values. PMID:24049574

Effect of surface treatments on the bond strength between resin cement and differently sintered zirconium-oxide ceramics.

PubMed

Yenisey, Murat; Dede, Doğu Ömür; Rona, Nergiz

2016-01-01

This study investigated the effects of surface treatments on bond strength between resin cement and differently sintered zirconium-oxide ceramics. 220 zirconium-oxide ceramic (Ceramill ZI) specimens were prepared, sintered in two different period (Short=Ss, Long=Ls) and divided into ten treatment groups as: GC, no treatment; GSil, silanized (ESPE-Sil); GSilPen, silane flame treatment (Silano-Pen); GSb, sandblasted; GSbSil, sandblasted+silanized; GSbCoSil, sandblasted+silica coated (CoJet)+silanized; GSbRoSil, sandblasted+silica coated (Rocatech-Plus)+silanized; GSbDSil, sandblasted+diamond particle abraded (Micron MDA)+silanized; GSbSilPen, sandblasted+silane flame treatment+silanized; GSbLSil, sandblasted+Er:Yag (Asclepion-MCL30) laser treated+silanized. The composite resin (Filtek Z-250) cylinders were cemented to the treated ceramic surfaces with a resin cement (Panavia F2.0). Shear bond strength test was performed after specimens were stored in water for 24h and thermo-cycled for 6000 cycles (5-55 °C). Data were statistically analyzed with two-way analysis of variance (ANOVA) and Tamhane's multiple comparison test (α=0.05). According to the ANOVA, sintering time, surface treatments and their interaction were statistically significant (p<0.05). The highest bond strengths were obtained in GSbCoSil (Ss=13.36/Ls=11.19MPa) and lowest values were obtained in GC (Ss=4.70/Ls=4.62 MPa) for both sinter groups. Sintering time may be effective on the bond strength and 30 μm silica coating (Cojet) with silane coupling application technique increased the bond strength between resin cement and differently sintered zirconium-oxide ceramics. Copyright © 2015 Japan Prosthodontic Society. Published by Elsevier Ltd. All rights reserved.

On the interfacial fracture resistance of resin-bonded zirconia and glass-infiltrated graded zirconia

PubMed Central

Chai, Herzl; Kaizer, Marina; Chughtai, Asima; Tong, Hui; Tanaka, Carina; Zhang, Yu

2015-01-01

Objective A major limiting factor for the widespread use of zirconia in prosthetic dentistry is its poor resin-cement bonding capabilities. We show that this deficiency can be overcome by infiltrating the zirconia cementation surface with glass. Current methods for assessing the fracture resistance of resin-ceramic bonds are marred by uneven stress distribution at the interface, which may result in erroneous interfacial fracture resistance values. We have applied a wedge-loaded double-cantilever-beam testing approach to accurately measure the interfacial fracture resistance of adhesively bonded zirconia-based restorative materials. Methods The interfacial fracture energy GC was determined for adhesively bonded zirconia, graded zirconia and feldspathic ceramic bars. The bonding surfaces were subjected to sandblasting or acid etching treatments. Baseline GC was measured for bonded specimens subjected to 7 days hydration at 37 °C. Long-term GC was determined for specimens exposed to 20,000 thermal cycles between 5 and 55 °C followed by 2-month aging at 37 °C in water. The test data were interpreted with the aid of a 2D finite element fracture analysis. Results The baseline and long-term GC for graded zirconia was 2–3 and 8 times that for zirconia, respectively. More significantly, both the baseline and long-term GC of graded zirconia were similar to those for feldspathic ceramic. Significance The interfacial fracture energy of feldspathic ceramic and graded zirconia was controlled by the fracture energy of the resin cement while that of zirconia by the interface. GC for the graded zirconia was as large as for feldspathic ceramic, making it an attractive material for use in dentistry. PMID:26365987

A Shear Strain Route Dependency of Martensite Formation in 316L Stainless Steel.

PubMed

Kang, Suk Hoon; Kim, Tae Kyu; Jang, Jinsung; Oh, Kyu Hwan

2015-06-01

In this study, the effect of simple shearing on microstructure evolution and mechanical properties of 316L austenitic stainless steel were investigated. Two different shear strain routes were obtained by twisting cylindrical specimens in the forward and backward directions. The strain-induced martensite phase was effectively obtained by alteration of the routes. Formation of the martensite phase clearly resulted in significant hardening of the steel. Grain-size reduction and strain-induced martensitic transformation within the deformed structures of the strained specimens were characterized by scanning electron microscopy - electron back-scattered diffraction, X-ray diffraction, and the TEM-ASTAR (transmission electron microscopy - analytical scanning transmission atomic resolution, automatic crystal orientation/phase mapping for TEM) system. Significant numbers of twin networks were formed by alteration of the shear strain routes, and the martensite phases were nucleated at the twin interfaces.

Grape seed proanthocyanidins increase collagen biodegradation resistance in the dentin/adhesive interface when included in an adhesive.

PubMed

Green, Bradley; Yao, Xiaomei; Ganguly, Arindam; Xu, Changqi; Dusevich, Vladimir; Walker, Mary P; Wang, Yong

2010-11-01

Contemporary methods of dentin bonding could create hybrid layers (HLs) containing voids and exposed, demineralised collagen fibres. Proanthocyanidins (PA) have been shown to cross-link and strengthen demineralised dentin collagen, but their effects on collagen degradation within the HL have not been widely studied. The purpose of this study was to compare the morphological differences of HLs created by BisGMA/HEMA model adhesives with and without the addition of grape seed extract PA under conditions of enzymatic collagen degradation. Model adhesives formulated with and without 5% PA were bonded to the acid etched dentin. 5-μm-thick sections cut from the bonded specimens were stained with Goldner's trichrome. The specimens were then exposed to 0.1% collagenase solution for 0, 1, or 6 days. Following collagenase treatment, the specimens were analysed with SEM/TEM. Staining did not reveal a difference in the HLs created with the two adhesives. SEM showed the presence of intact collagen fibrils in all collagenase treatment conditions for specimens bonded with adhesive containing PA. These integral collagen fibrils were not observed in the specimens bonded with adhesive without PA after the same collagenase treatment. TEM confirmed that the specimens containing PA still showed normal collagen fibril organisation and dimensions after treatment with collagenase solution. In contrast, disorganised collagen fibrils in the interfacial zone lacked the typical cross-banding of normal collagen after collagenase treatment for specimens without PA. The presence of grape seed extract PA in dental adhesives may inhibit the biodegradation of unprotected collagen fibrils within the HL. Copyright © 2010 Elsevier Ltd. All rights reserved.

Influence of surface treatments on bond strength of metal and ceramic brackets to a novel CAD/CAM hybrid ceramic material.

PubMed

Elsaka, Shaymaa E

2016-01-01

This study evaluated the effect of four different surface treatments methods on the shear bond strength (SBS) of ceramic and metal brackets to Vita Enamic (VE) CAD/CAM hybrid ceramic. A total of 240 plates (10 mm × 10 mm × 3 mm) were cut from VE ceramic blocks and divided into two groups. In each group, four subgroups were prepared by hydrofluoric acid (HF); phosphoric acid (H3PO4); diamond ceramic grinding bur; and silica coating using CoJet system (CJ). Maxillary central incisor metal (Victory Series) and ceramic (Clarity) brackets were bonded with light-cure composite and then stored in artificial saliva for 1 week and thermocycled. The SBS test was performed, and the failure types were classified with adhesive remnant index scores. Surface morphology of the ceramic was characterized after treatment using a scanning electron microscope. Data were analyzed using two-way ANOVA, Tukey HSD test, and Weibull analysis. SBS was significantly affected by the type of bracket and by type of treatment (P < 0.001). Specimens treated with CJ presented with significantly higher SBS compared to other groups (P < 0.05). Improvements in SBS values (MPa) were found in the following order: CJ > HF > Bur > H3PO4. Ceramic bracket showed higher SBS compared to metal bracket. Adhesive failures between the ceramic and composite resin were the predominant mode of failure in all groups. Surface treatment of VE CAD/CAM hybrid ceramic with silica coating enhanced the adhesion with ceramic and metal brackets.

A rolling-gliding wear simulator for the investigation of tribological material pairings for application in total knee arthroplasty.

PubMed

Richter, Berna I; Ostermeier, Sven; Turger, Anke; Denkena, Berend; Hurschler, Christof

2010-06-15

Material wear testing is an important technique in the development and evaluation of materials for use in implant for total knee arthroplasty. Since a knee joint induces a complex rolling-gliding movement, standardised material wear testing devices such as Pin-on-Disc or Ring-on-Disc testers are suitable to only a limited extent because they generate pure gliding motion only. A rolling-gliding wear simulator was thus designed, constructed and implemented, which simulates and reproduces the rolling-gliding movement and loading of the knee joint on specimens of simplified geometry. The technical concept was to run a base-plate, representing the tibia plateau, against a pivoted cylindrical counter-body, representing one femur condyle under an axial load. A rolling movement occurs as a result of the friction and pure gliding is induced by limiting the rotation of the cylindrical counter-body. The set up also enables simplified specimens handling and removal for gravimetrical wear measurements. Long-term wear tests and gravimetrical wear measurements were carried out on the well known material pairings: cobalt chrome-polyethylene, ceramic-polyethylene and ceramic-ceramic, over three million motion cycles to allow material comparisons to be made. The observed differences in wear rates between cobalt-chrome on polyethylene and ceramic on polyethylene pairings were similar to the differences of published data for existing material-pairings. Test results on ceramic-ceramic pairings of different frontal-plane geometry and surface roughness displayed low wear rates and no fracture failures. The presented set up is able to simulate the rolling-gliding movement of the knee joint, is easy to use, and requires a minimum of user intervention or monitoring. It is suitable for long-term testing, and therefore a useful tool for the investigation of new and promising materials which are of interest for application in knee joint replacement implants.

A rolling-gliding wear simulator for the investigation of tribological material pairings for application in total knee arthroplasty

PubMed Central

2010-01-01

Background Material wear testing is an important technique in the development and evaluation of materials for use in implant for total knee arthroplasty. Since a knee joint induces a complex rolling-gliding movement, standardised material wear testing devices such as Pin-on-Disc or Ring-on-Disc testers are suitable to only a limited extent because they generate pure gliding motion only. Methods A rolling-gliding wear simulator was thus designed, constructed and implemented, which simulates and reproduces the rolling-gliding movement and loading of the knee joint on specimens of simplified geometry. The technical concept was to run a base-plate, representing the tibia plateau, against a pivoted cylindrical counter-body, representing one femur condyle under an axial load. A rolling movement occurs as a result of the friction and pure gliding is induced by limiting the rotation of the cylindrical counter-body. The set up also enables simplified specimens handling and removal for gravimetrical wear measurements. Long-term wear tests and gravimetrical wear measurements were carried out on the well known material pairings: cobalt chrome-polyethylene, ceramic-polyethylene and ceramic-ceramic, over three million motion cycles to allow material comparisons to be made. Results The observed differences in wear rates between cobalt-chrome on polyethylene and ceramic on polyethylene pairings were similar to the differences of published data for existing material-pairings. Test results on ceramic-ceramic pairings of different frontal-plane geometry and surface roughness displayed low wear rates and no fracture failures. Conclusions The presented set up is able to simulate the rolling-gliding movement of the knee joint, is easy to use, and requires a minimum of user intervention or monitoring. It is suitable for long-term testing, and therefore a useful tool for the investigation of new and promising materials which are of interest for application in knee joint replacement implants. PMID:20550669

Impact of machining on the flexural fatigue strength of glass and polycrystalline CAD/CAM ceramics.

PubMed

Fraga, Sara; Amaral, Marina; Bottino, Marco Antônio; Valandro, Luiz Felipe; Kleverlaan, Cornelis Johannes; May, Liliana Gressler

2017-11-01

To assess the effect of machining on the flexural fatigue strength and on the surface roughness of different computer-aided design, computer-aided manufacturing (CAD/CAM) ceramics by comparing machined and polished after machining specimens. Disc-shaped specimens of yttria-stabilized polycrystalline tetragonal zirconia (Y-TZP), leucite-, and lithium disilicate-based glass ceramics were prepared by CAD/CAM machining, and divided into two groups: machining (M) and machining followed by polishing (MP). The surface roughness was measured and the flexural fatigue strength was evaluated by the step-test method (n=20). The initial load and the load increment for each ceramic material were based on a monotonic test (n=5). A maximum of 10,000 cycles was applied in each load step, at 1.4Hz. Weibull probability statistics was used for the analysis of the flexural fatigue strength, and Mann-Whitney test (α=5%) to compare roughness between the M and MP conditions. Machining resulted in lower values of characteristic flexural fatigue strength than machining followed by polishing. The greatest reduction in flexural fatigue strength from MP to M was observed for Y-TZP (40%; M=536.48MPa; MP=894.50MPa), followed by lithium disilicate (33%; M=187.71MPa; MP=278.93MPa) and leucite (29%; M=72.61MPa; MP=102.55MPa). Significantly higher values of roughness (Ra) were observed for M compared to MP (leucite: M=1.59μm and MP=0.08μm; lithium disilicate: M=1.84μm and MP=0.13μm; Y-TZP: M=1.79μm and MP=0.18μm). Machining negatively affected the flexural fatigue strength of CAD/CAM ceramics, indicating that machining of partially or fully sintered ceramics is deleterious to fatigue strength. Copyright © 2017 The Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

CARES/PC - CERAMICS ANALYSIS AND RELIABILITY EVALUATION OF STRUCTURES

NASA Technical Reports Server (NTRS)

Szatmary, S. A.

1994-01-01

The beneficial properties of structural ceramics include their high-temperature strength, light weight, hardness, and corrosion and oxidation resistance. For advanced heat engines, ceramics have demonstrated functional abilities at temperatures well beyond the operational limits of metals. This is offset by the fact that ceramic materials tend to be brittle. When a load is applied, their lack of significant plastic deformation causes the material to crack at microscopic flaws, destroying the component. CARES/PC performs statistical analysis of data obtained from the fracture of simple, uniaxial tensile or flexural specimens and estimates the Weibull and Batdorf material parameters from this data. CARES/PC is a subset of the program CARES (COSMIC program number LEW-15168) which calculates the fast-fracture reliability or failure probability of ceramic components utilizing the Batdorf and Weibull models to describe the effects of multi-axial stress states on material strength. CARES additionally requires that the ceramic structure be modeled by a finite element program such as MSC/NASTRAN or ANSYS. The more limited CARES/PC does not perform fast-fracture reliability estimation of components. CARES/PC estimates ceramic material properties from uniaxial tensile or from three- and four-point bend bar data. In general, the parameters are obtained from the fracture stresses of many specimens (30 or more are recommended) whose geometry and loading configurations are held constant. Parameter estimation can be performed for single or multiple failure modes by using the least-squares analysis or the maximum likelihood method. Kolmogorov-Smirnov and Anderson-Darling goodness-of-fit tests measure the accuracy of the hypothesis that the fracture data comes from a population with a distribution specified by the estimated Weibull parameters. Ninety-percent confidence intervals on the Weibull parameters and the unbiased value of the shape parameter for complete samples are provided when the maximum likelihood technique is used. CARES/PC is written and compiled with the Microsoft FORTRAN v5.0 compiler using the VAX FORTRAN extensions and dynamic array allocation supported by this compiler for the IBM/MS-DOS or OS/2 operating systems. The dynamic array allocation routines allow the user to match the number of fracture sets and test specimens to the memory available. Machine requirements include IBM PC compatibles with optional math coprocessor. Program output is designed to fit 80-column format printers. Executables for both DOS and OS/2 are provided. CARES/PC is distributed on one 5.25 inch 360K MS-DOS format diskette in compressed format. The expansion tool PKUNZIP.EXE is supplied on the diskette. CARES/PC was developed in 1990. IBM PC and OS/2 are trademarks of International Business Machines. MS-DOS and MS OS/2 are trademarks of Microsoft Corporation. VAX is a trademark of Digital Equipment Corporation.

Real time acousto-ultrasonic NDE technique for monitoring damage in ceramic composites under dynamic loads

NASA Technical Reports Server (NTRS)

Tiwari, Anil

1995-01-01

Research effort was directed towards developing a near real-time, acousto-ultrasonic (AU), nondestructive evaluation (NDE) tool to study the failure mechanisms of ceramic composites. Progression of damage is monitored in real-time by observing the changes in the received AU signal during the actual test. During the real-time AU test, the AU signals are generated and received by the AU transducers attached to the specimen while it is being subjected to increasing quasi-static loads or cyclic loads (10 Hz, R = 1.0). The received AU signals for 64 successive pulses were gated in the time domain (T = 40.96 micro sec) and then averaged every second over ten load cycles and stored in a computer file during fatigue tests. These averaged gated signals are representative of the damage state of the specimen at that point of its fatigue life. This is also the first major attempt in the development and application of real-time AU for continuously monitoring damage accumulation during fatigue without interrupting the test. The present work has verified the capability of the AU technique to assess the damage state in silicon carbide/calcium aluminosilicate (SiC/CAS) and silicon carbide/ magnesium aluminosilicate (SiC/MAS) ceramic composites. Continuous monitoring of damage initiation and progression under quasi-static ramp loading in tension to failure of unidirectional and cross-ply SiC/CAS and quasi-isotropic SiC/MAS ceramic composite specimens at room temperature was accomplished using near real-time AU parameters. The AU technique was shown to be able to detect the stress levels for the onset and saturation of matrix cracks, respectively. The critical cracking stress level is used as a design stress for brittle matrix composites operating at elevated temperatures. The AU technique has found that the critical cracking stress level is 10-15% below the level presently obtained for design purposes from analytical models. An acousto-ultrasonic stress-strain response (AUSSR) model for unidirectional and cross-ply ceramic composites was formulated. The AUSSR model predicts the strain response to increasing stress levels using real-time AU data and classical laminated plate theory. The Weibull parameters of the AUSSR model are used to calculate the design stress for thermo-structural applications. Real-time AU together with the AUSSR model was used to study the failure mechanisms of SiC/CAS ceramic composites under static and fatigue loading. An S-N curve was generated for a cross-ply SiC/CAS ceramic composite material. The AU results are corroborated and complemented by other NDE techniques, namely, in-situ optical microscope video recordings and edge replication.

Effect of different surface treatments on roughness of IPS Empress 2 ceramic.

PubMed

Kara, Haluk Baris; Dilber, Erhan; Koc, Ozlem; Ozturk, A Nilgun; Bulbul, Mehmet

2012-03-01

The aim of this study was to evaluate the influence of different surface treatments (air abrasion, acid etching, laser irradiation) on the surface roughness of a lithium-disilicate-based core ceramic. A total of 40 discs of lithium disilicate-based core ceramic (IPS Empress 2; Ivoclar Vivadent, Schaan, Liechtenstein) were prepared (10 mm in diameter and 1 mm in thickness) according to the manufacturer's instructions. Specimens were divided into four groups (n = 10), and the following treatments were applied: air abrasion with alumina particles (50 μm), acid etching with 5% hydrofluoric acid, Nd:YAG laser irradiation (1 mm distance, 100 mJ, 20 Hz, 2 W) and Er:YAG laser irradiation (1 mm distance, 500 mJ, 20 Hz, 10 W). Following determination of surface roughness (R(a)) by profilometry, specimens were examined with atomic force microscopy. The data were analysed by one-way analysis of variance (ANOVA) and Tukey HSD test (α = 0.05). One-way ANOVA indicated that surface roughness following air abrasion was significantly different from the surface roughness following laser irradiation and acid etching (P < 0.001). The Tukey HSD test indicated that the air abrasion group had a significantly higher mean value of roughness (P < 0.05) than the other groups. No significant difference was found between the acid etching and laser irradiation (both Er:YAG and Nd:YAG) groups (P > 0.05). Air abrasion increased surface roughness of lithium disilicate-based core ceramic surfaces more effectively than acid-etching and laser irradiation.

Irradiation behavior of LiAlO 2 and Li 2ZrO 3 ceramics in the ALICE 3 experiment

NASA Astrophysics Data System (ADS)

Rasneur, B.; Thevenot, G.; Bouilloux, Y.

1992-09-01

Within the framework of the investigation of ceramic breeders for the DEMO relevant solid blankets developed in Europe, the ALICE 3 experiment was foreseen to study the irradiation behavior of the ceramics. The irradiation was performed in the core of the OSIRIS reactor for 46 FPD (full power days) at 400°C and 600°C. The three ceramics in the configuration contemplated in the BIT and BOT concepts were tested, i.e. LiAlO 2 and Li 2ZrO 3 pellets, Li 4SiO 4 and Li 2ZrO 3 pebbles, respectively. In this paper are reported the results of the post-irradiation examination carried out at CEA on CEA Li 2ZrO 3 and LiAlO 2 specimens: dimensions, X-ray diffraction, ultimate bending strength, diametral compressive strength and residual tritium.

Highly Refractory Porous Ceramics,

DTIC Science & Technology

1979-03-14

some cases is not desirable. A uniform distribution of tem- peratures in the melting ch the use of thermally insulating materials, i. e. stability of...materials with micropores that a are inaccessible to penetration by sl s and other melts , which appears, how- ever, to be a very difficult problem...requirements for refractoriness, chemical stability, etc. In accordance with GOST 5040-68, maximum temperatures were established for the melting chamber

Determination of the Influence of Electric Fields upon the Densification of Ionic Ceramics

DTIC Science & Technology

2017-07-21

and assisting the development of new techniques to expose nanoparticles to non -contacting electrostatic fields at temperatures as high as 900...through TEM imaging, and assisting the development of new techniques to expose nanoparticles to non -contacting electrostatic fields at temperatures as...during flash sintering lead to non -homogeneous microstructures. We expect that therefore physical properties may be inhomogeneous depending local

Effect of etching time and resin bond on the flexural strength of IPS e.max Press glass ceramic.

PubMed

Xiaoping, Luo; Dongfeng, Ren; Silikas, Nick

2014-12-01

To evaluate the effect of hydrofluoric acid (HFA) etching time and resin cement bond on the flexural strength of IPS e.max(®) Press glass ceramic. Two hundred and ten bars, 25mm×3mm×2mm, were made from IPS e.max(®) Press ingots through lost-wax, hot-pressed ceramic fabrication technology and randomly divided into five groups with forty-two per group after polishing. The ceramic surfaces of different groups were etched by 9.5% hydrofluoric acid gel for 0, 20, 40, 60 and 120s respectively. Two specimens of each group were selected randomly to examine the surface roughness and 3-dimensional topography with atomic force microscope (AFM), and microstructure was analyzed by the field emission scanning electron microscope (FE-SEM). Then each group were subdivided into two subgroups (n=20). One subgroup of this material was selected to receive a thin (approximately 0.1mm) layer of resin luting agent (Variolink N) whereas the other subgroup remained unaltered. Half of subgroup's specimens were thermocycled 10,000 times before a 3-point bending test in order to determine the flexural strength. Interface between resin cement and ceramic was examined with field emission scanning electronic microscope. Roughness values increased with increasing etching time. The mean flexural strength values of group 0s, 20s, 40s, 60s and 120s were 384±33, 347±43, 330±53, 327±67 and 317±41MPa respectively. Increasing HF etching times reduced the mean flexural strength (p<0.05). However, the mean flexural strength of each group, except group 0s, increased significantly to 420±31, 435±50, 400±39 and 412±58MPa after the application of dual-curing resin cement. In the present investigation, no significant differences after thermocycling on the flexural strengths were evident. Overtime HF etching could have a wakening effect on IPS e.max(®) Press glass ceramic, but resin cement bonding to appropriately etched surface would strengthen the dental ceramic. Copyright © 2014 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Metal-ceramic bond strength between a feldspathic porcelain and a Co-Cr alloy fabricated with Direct Metal Laser Sintering technique.

PubMed

Dimitriadis, Konstantinos; Spyropoulos, Konstantinos; Papadopoulos, Triantafillos

2018-02-01

The aim of the present study was to record the metal-ceramic bond strength of a feldspathic dental porcelain and a Co-Cr alloy, using the Direct Metal Laser Sintering technique (DMLS) for the fabrication of metal substrates. Ten metal substrates were fabricated with powder of a dental Co-Cr alloy using DMLS technique (test group) in dimensions according to ISO 9693. Another ten substrates were fabricated with a casing dental Co-Cr alloy using classic casting technique (control group) for comparison. Another three substrates were fabricated using each technique to record the Modulus of Elasticity ( E ) of the used alloys. All substrates were examined to record external and internal porosity. Feldspathic porcelain was applied on the substrates. Specimens were tested using the three-point bending test. The failure mode was determined using optical and scanning electron microscopy. The statistical analysis was performed using t-test. Substrates prepared using DMLS technique did not show internal porosity as compared to those produced using the casting technique. The E of control and test group was 222 ± 5.13 GPa and 227 ± 3 GPa, respectively. The bond strength was 51.87 ± 7.50 MPa for test group and 54.60 ± 6.20 MPa for control group. No statistically significant differences between the two groups were recorded. The mode of failure was mainly cohesive for all specimens. Specimens produced by the DMLS technique cover the lowest acceptable metal-ceramic bond strength of 25 MPa specified in ISO 9693 and present satisfactory bond strength for clinical use.

Advanced Material-Ordered Nanotubular Ceramic Membranes Covalently Capped with Single-Wall Carbon Nanotubes.

PubMed

Al-Gharabli, Samer; Hamad, Eyad; Saket, Munib; Abu El-Rub, Ziad; Arafat, Hassan; Kujawski, Wojciech; Kujawa, Joanna

2018-05-07

Advanced ceramic materials with a well-defined nano-architecture of their surfaces were formed by applying a two-step procedure. Firstly, a primary amine was docked on the ordered nanotubular ceramic surface via a silanization process. Subsequently, single-wall carbon nanotubes (SWCNTs) were covalently grafted onto the surface via an amide building block. Physicochemical (e.g., hydrophobicity, and surface free energy (SFE)), mechanical, and tribological properties of the developed membranes were improved significantly. The design, preparation, and extended characterization of the developed membranes are presented. Tools such as high-resolution transmission electron microscopy (HR-TEM), single-area electron diffraction (SAED) analysis, microscopy, tribology, nano-indentation, and Raman spectroscopy, among other techniques, were utilized in the characterization of the developed membranes. As an effect of hydrophobization, the contact angles (CAs) changed from 38° to 110° and from 51° to 95° for the silanization of ceramic membranes 20 (CM20) and CM100, respectively. SWCNT functionalization reduced the CAs to 72° and 66° for ceramic membranes carbon nanotubes 20 (CM-CNT-20) and CM-CNT-100, respectively. The mechanical properties of the developed membranes improved significantly. From the nanotribological study, Young’s modulus increased from 3 to 39 GPa for CM-CNT-20 and from 43 to 48 GPa for pristine CM-CNT-100. Furthermore, the nanohardness increased by about 80% after the attachment of CNTs for both types of ceramics. The proposed protocol within this work for the development of functionalized ceramic membranes is both simple and efficient.

Structural and electrical properties of 1 − x(Na{sub 0.5}K{sub 0.5})NbO{sub 3}–x(Sr{sub 0.5}Ca{sub 0.5})TiO{sub 3} ceramics

DOE Office of Scientific and Technical Information (OSTI.GOV)

Lee, Tae-Ho; Lee, Sung-Gap, E-mail: lsgap@gnu.ac.kr; Yeo, Jin-Ho

2014-10-15

Highlights: • We fabricated lead-free (Na{sub 0.5}K{sub 0.5})NbO{sub 3} ceramics. • We studied the structural and electrical properties of 1 − x(Na{sub 0.5}K{sub 0.5})NbO{sub 3}–x(Sr{sub 0.5}Ca{sub 0.5})TiO{sub 3} ceramics. • The structural and electrical properties improved with increasing amount of (Sr{sub 0.5}Ca{sub 0.5})TiO{sub 3}. - Abstract: In this study, 1 − x(Na{sub 0.5}K{sub 0.5})NbO{sub 3}–x(Sr{sub 0.5}Ca{sub 0.5})TiO{sub 3} ceramics were fabricated using the conventional mixed oxide method. The effects of the addition of (Sr{sub 0.5}Ca{sub 0.5})TiO{sub 3} on the structural and electrical properties of the specimens were investigated for their application in piezoelectric devices. As the results of X-ray diffractionmore » analysis show, all specimens display the typical polycrystalline perovskite structure without the presence of the second phase. Sintered densities increased with an increase in the amount of (Sr{sub 0.5}Ca{sub 0.5})TiO{sub 3} added and the specimen with 0.08 mol% of (Sr{sub 0.5}Ca{sub 0.5})TiO{sub 3} added showed the maximum value of 4.54 g/cm{sup 3}. Both average grain size and densification increased with an increase in the amount of (Sr{sub 0.5}Ca{sub 0.5})TiO{sub 3}. The electromechanical coupling factor, dielectric constant ϵ{sub r}, dielectric loss tan δ, d{sub 33} and Curie temperature of the 0.92(Na{sub 0.5}K{sub 0.5})NbO{sub 3}–0.08(Sr{sub 0.5}Ca{sub 0.5})TiO{sub 3} specimens doped with 0.08 mol% of (Sr{sub 0.5}Ca{sub 0.5})TiO{sub 3} were 0.31, 1338, 0.021, 138 and 445 °C, respectively.« less

Uniaxial Tensile Test for Soil.

DTIC Science & Technology

1987-04-01

2.0 by 5.0 cm. This test was also performed on a horizontal specimen; however loading was applied through small metal plates that were embedded in the 6...i. enlarged ends. The specimen was supported by a bed of mercury and had two small ceramic markers mounted in the gage length that were monitored...with a cathetometer to determine displacements. It was found that most tests failed near the location of the embedded metal loading plates making their

Machinability of CAD-CAM materials.

PubMed

Chavali, Ramakiran; Nejat, Amir H; Lawson, Nathaniel C

2017-08-01

Although new materials are available for computer-aided design and computer-aided manufacturing (CAD-CAM) fabrication, limited information is available regarding their machinability. The depth of penetration of a milling tool into a material during a timed milling cycle may indicate its machinability. The purpose of this in vitro study was to compare the tool penetration rate for 2 polymer-containing CAD-CAM materials (Lava Ultimate and Enamic) and 2 ceramic-based CAD-CAM materials (e.max CAD and Celtra Duo). The materials were sectioned into 4-mm-thick specimens (n=5/material) and polished with 320-grit SiC paper. Each specimen was loaded into a custom milling apparatus. The apparatus pushed the specimens against a milling tool (E4D Tapered 2016000) rotating at 40 000 RPM with a constant force of 0.98 N. After a 6-minute timed milling cycle, the length of each milling cut was measured with image analysis software under a digital light microscope. Representative specimens and milling tools were examined with scanning electron microscopy (SEM) and energy dispersive x-ray spectroscopy. The penetration rate of Lava Ultimate (3.21 ±0.46 mm/min) and Enamic (2.53 ±0.57 mm/min) was significantly greater than that of e.max CAD (1.12 ±0.32 mm/min) or Celtra Duo (0.80 ±0.21 mm/min) materials. SEM observations showed little tool damage, regardless of material type. Residual material was found on the tools used with polymer-containing materials, and wear of the embedding medium was seen on the tools used with the ceramic-based materials. Edge chipping was noted on cuts made in the ceramic-based materials. Lava Ultimate and Enamic have greater machinability and less edge chipping than e.max CAD and Celtra Duo. Copyright © 2016 Editorial Council for the Journal of Prosthetic Dentistry. Published by Elsevier Inc. All rights reserved.

Hygroscopic expansion of self-adhesive resin cements and the integrity of all-ceramic crowns.

PubMed

Kirsten, Magdalena; Matta, Ragai Edward; Belli, Renan; Lohbauer, Ulrich; Wichmann, Manfred; Petschelt, Anselm; Zorzin, José

2018-04-27

Low pH neutralization and subsequent remnant hydrophilicity can lead to hygroscopic expansion of self-adhesive resin cements (SARCs) after water storage. The aim of this in vitro study was to investigate the effects of hygroscopic expansion of SARCs, used as luting and partial core build-up material, on integrity and cement gap thickness increase of all-ceramic CAD/CAM crowns. Human third molars (n=48) were prepared and anatomical all-ceramic CAD/CAM crowns were manufactured (VITABLOCS Mark II, VITA Zahnfabrik). Crowns internal surfaces were HF etched and silanized. The prepared teeth with their respective crowns were divided into 6 groups (n=8). In groups 1, 3 and 5 the coronal dentin was removed to simulate a partial core build-up. Groups 1 and 2 were luted with iCEM (Heraeus Kulzer), 3 and 4 with RelyX Unicem 2 Automix (3M), 5 and 6 with Variolink Esthetic DC (Ivoclar Vivadent). All specimens were dual cured and stored in distilled water at 37°C. Crown integrity was controlled at baseline and in regular intervals until 180 days. Cement gap thickness was measured using an optical 3D scanner (ATOS Triple scan, GOM) at baseline and after 180 days. Crown integrity was statistically analysed using Kaplan-Meier survival analysis and cement gap thickness increase using two-way ANOVA (α=0.05). After 180 days storage, crack formation was observed in all specimens of group 1 (mean survival time of 85.5 days), in one specimen of group 2 and in two specimens of group 4. Two-way ANOVA analysis revealed a statistically significant interaction between material type and build-up on cement gap size increase for iCEM. Within the limits of this study, the application of SARCs with low pH neutralization as partial build-up material under CAD/CAM crowns is not recommended for clinical use. Copyright © 2018 The Academy of Dental Materials. Published by Elsevier Inc. All rights reserved.