Comparative study on the role of gelatin, chitosan and their combination as tissue engineered scaffolds on healing and regeneration of critical sized bone defects: an in vivo study.

PubMed

Oryan, Ahmad; Alidadi, Soodeh; Bigham-Sadegh, Amin; Moshiri, Ali

2016-10-01

Gelatin and chitosan are natural polymers that have extensively been used in tissue engineering applications. The present study aimed to evaluate the effectiveness of chitosan and gelatin or combination of the two biopolymers (chitosan-gelatin) as bone scaffold on bone regeneration process in an experimentally induced critical sized radial bone defect model in rats. Fifty radial bone defects were bilaterally created in 25 Wistar rats. The defects were randomly filled with chitosan, gelatin and chitosan-gelatin and autograft or left empty without any treatment (n = 10 in each group). The animals were examined by radiology and clinical evaluation before euthanasia. After 8 weeks, the rats were euthanized and their harvested healing bone samples were evaluated by radiology, CT-scan, biomechanical testing, gross pathology, histopathology, histomorphometry and scanning electron microscopy. Gelatin was biocompatible and biodegradable in vivo and showed superior biodegradation and biocompatibility when compared with chitosan and chitosan-gelatin scaffolds. Implantation of both the gelatin and chitosan-gelatin scaffolds in bone defects significantly increased new bone formation and mechanical properties compared with the untreated defects (P < 0.05). Combination of the gelatin and chitosan considerably increased structural and functional properties of the healing bones when compared to chitosan scaffold (P < 0.05). However, no significant differences were observed between the gelatin and gelatin-chitosan groups in these regards (P > 0.05). In conclusion, application of the gelatin alone or its combination with chitosan had beneficial effects on bone regeneration and could be considered as good options for bone tissue engineering strategies. However, chitosan alone was not able to promote considerable new bone formation in the experimentally induced critical-size radial bone defects.

Poly(ɛ-caprolactone)/gelatin composite electrospun scaffolds with porous crater-like structures for tissue engineering.

PubMed

Hwang, Patrick T J; Murdock, Kyle; Alexander, Grant C; Salaam, Amanee D; Ng, Joshua I; Lim, Dong-Jin; Dean, Derrick; Jun, Ho-Wook

2016-04-01

Electrospinning has been widely used to fabricate scaffolds imitating the structure of natural extracellular matrix (ECM). However, conventional electrospinning produces tightly compacted nanofiber layers with only small superficial pores and a lack of bioactivity, which limit the usefulness of electrospinning in biomedical applications. Thus, a porous poly(ε-caprolactone) (PCL)/gelatin composite electrospun scaffold with crater-like structures was developed. Porous crater-like structures were created on the scaffold by a gas foaming/salt leaching process; this unique fiber structure had more large pore areas and higher porosity than the conventional electrospun fiber network. Various ratios of PCL/gelatin (concentration ratios: 100/0, 75/25, and 50/50) composite electrospun scaffolds with and without crater-like structures were characterized by their microstructures, surface chemistry, degradation, mechanical properties, and ability to facilitate cell growth and infiltration. The combination of PCL and gelatin endowed the scaffold with both structural stability of PCL and bioactivity of gelatin. All ratios of scaffolds with crater-like structures showed fairly similar surface chemistry, degradation rates, and mechanical properties to equivalent scaffolds without crater-like structures; however, craterized scaffolds displayed higher human mesenchymal stem cell (hMSC) proliferation and infiltration throughout the scaffolds after 7-day culture. Therefore, these results demonstrated that PCL/gelatin composite electrospun scaffolds with crater-like structures can provide a structurally and biochemically improved three-dimensional ECM-mimicking microenvironment. © 2016 Wiley Periodicals, Inc.

Poly(ε-caprolactone)/gelatin composite electrospun scaffolds with porous crater-like structures for tissue engineering

PubMed Central

Hwang, Patrick T.J.; Murdock, Kyle; Alexander, Grant C.; Salaam, Amanee D.; Ng, Joshua I.; Lim, Dong-Jin; Dean, Derrick; Jun, Ho-Wook

2016-01-01

Electrospinning has been widely used to fabricate scaffolds imitating the structure of natural extracellular matrix (ECM). However, conventional electrospinning produces tightly compacted nanofiber layers with only small superficial pores and a lack of bioactivity, which limit the usefulness of electrospinning in biomedical applications. Thus, a porous poly(ε-caprolactone) (PCL)/gelatin composite electrospun scaffold with crater-like structures was developed. Porous crater-like structures were created on the scaffold by a gas foaming/salt leaching process; this unique fiber structure had more large pore areas and higher porosity than the conventional electrospun fiber network. Various ratios of PCL/gelatin (concentration ratios: 100/0, 75/25, and 50/50) composite electrospun scaffolds with and without crater-like structures were characterized by their microstructures, surface chemistry, degradation, mechanical properties, and ability to facilitate cell growth and infiltration. The combination of PCL and gelatin endowed the scaffold with both structural stability of PCL and bioactivity of gelatin. All ratios of scaffolds with crater-like structures showed fairly similar surface chemistry, degradation rates, and mechanical properties to equivalent scaffolds without crater-like structures; however, craterized scaffolds displayed higher human mesenchymal stem cell (hMSC) proliferation and infiltration throughout the scaffolds after 7-day culture. Therefore, these results demonstrated that PCL/gelatin composite electrospun scaffolds with crater-like structures can provide a structurally and biochemically improved three-dimensional ECM-mimicking microenvironment. PMID:26567028

Control of cell proliferation by a porous chitosan scaffold with multiple releasing capabilities

NASA Astrophysics Data System (ADS)

Cai, Shu-Jyun; Li, Ching-Wen; Weihs, Daphne; Wang, Gou-Jen

2017-12-01

The aim of this study was to develop a porous chitosan scaffold with long-acting drug release as an artificial dressing to promote skin wound healing. The dressing was fabricated by pre-freezing at different temperatures (-20 and -80 °C) for different periods of time, followed by freeze-drying to form porous chitosan scaffolds with different pore sizes. The chitosan scaffolds were then used to investigate the effect of the controlled release of fibroblast growth factor-basic (bFGF) and transforming growth factor-β1 (TGFβ1) on mouse fibroblast cells (L929) and bovine carotid endothelial cells (BEC). The biocompatibility of the prepared chitosan scaffold was confirmed with WST-1 proliferation and viability assay, which demonstrated that the material is suitable for cell growth. The results of this study show that the pore sizes of the porous scaffolds prepared by freeze-drying can change depending on the pre-freezing temperature and time via the formation of ice crystals. In this study, the scaffolds with the largest pore size were found to be 153 ± 32 μm and scaffolds with the smallest pores to be 34 ± 9 μm. Through cell culture analysis, it was found that the concentration that increased proliferation of L929 cells for bFGF was 0.005 to 0.1 ng/mL, and the concentration for TGFβ1 was 0.005 to 1 ng/mL. The cell culture of the chitosan scaffold and growth factors shows that 3.75 ng of bFGF in scaffolds with pore sizes of 153 ± 32 μm can promote L929 cell proliferation, while 400 pg of TGFβ1 in scaffolds with pore size of 34 ± 9 μm can enhance the proliferation of L929 cells, but also inhibit BEC proliferation. It is proposed that the prepared chitosan scaffolds can form a multi-drug (bFGF and TGFβ1) release dressing that has the ability to control wound healing via regulating the proliferation of different cell types.

Oxygen Plasma Treatment on 3D-Printed Chitosan/Gelatin/Hydroxyapatite Scaffolds for Bone Tissue Engineering.

PubMed

Lee, Chang-Min; Yang, Seong-Won; Jung, Sang-Chul; Kim, Byung-Hoon

2017-04-01

The 3D hydroxyapatite/gelatin/chitosan composite scaffolds were fabricated by 3D printing technique. The scaffolds were treated by oxygen plasma to improve the bioactivity and its surface characterization and in vitro cell culture were investigated. The scaffolds exhibited the good porosity and interconnectivity of pores. After oxygen plasma etching, roughness and wettability on the scaffolds surface are increased. Plasma treated scaffolds showed higher proliferation than that of untreated scaffolds. Oxygen plasma treatment could be used as potential tool to enhance the biocompatibility on the 3D composite scaffolds.

[EXPERIMENTAL STUDY ON CHITOSAN/ALLOGENEIC BONE POWDER COMPOSITE POROUS SCAFFOLD TO REPAIR BONE DEFECTS IN RATS].

PubMed

Kang, Xiangang; Zhao, Zhiyuan; Wu, Xuzhi; Shen, Qingxin; Wang, Zhiqiang; Kang, Yue; Xing, Zhenguang; Zhang, Tao

2016-03-01

To explore the feasibility of chitosan/allogeneic bone powder composite porous scaffold as scaffold material of bone tissue engineering in repairing bone defect. The composite porous scaffolds were prepared with chitosan and decalcified allogeneic bone powder at a ratio of 1 : 5 by vacuum freeze-drying technique. Chitosan scaffold served as control. Ethanol alternative method was used to measure its porosity, and scanning electron microscopy (SEM) to measure pore size. The hole of 3.5 mm in diameter was made on the bilateral femoral condyles of 40 adult Sprague Dawley rats. The composite porous scaffolds and chitosan scaffolds were implanted into the hole of the left femoral condyle (experimental group) and the hole of the right femoral condyle (control group), respectively. At 2, 4, 8, and 12 weeks after implantation, the tissues were harvested for gross observation, histological observation, and immunohistochemical staining. The composite porous scaffold prepared by vacuum freeze-drying technique had yellowish color, and brittle and easily broken texture; pore size was mostly 200-300 μm; and the porosity was 76.8% ± 1.1%, showing no significant difference when compared with the porosity of pure chitosan scaffold (78.4% ± 1.4%) (t = -2.10, P = 0.09). The gross observation and histological observation showed that the defect area was filled with new bone with time, and new bone of the experimental group was significantly more than that of the control group. At 4, 8, and 12 weeks after implantation, the bone forming area of the experimental group was significantly larger than that of the control group (P < 0.05). The immunohistochemical staining results showed that osteoprotegerin (OPG) positive expression was found in the experimental group at different time points, and the positive expression level was significantly higher than that in the control group (P < 0.05). Chitosan/allogeneic bone powder composite porous scaffold has suitable porosity and good

Control of cell proliferation by a porous chitosan scaffold with multiple releasing capabilities

PubMed Central

Cai, Shu-Jyun; Li, Ching-Wen; Weihs, Daphne; Wang, Gou-Jen

2017-01-01

Abstract The aim of this study was to develop a porous chitosan scaffold with long-acting drug release as an artificial dressing to promote skin wound healing. The dressing was fabricated by pre-freezing at different temperatures (−20 and −80 °C) for different periods of time, followed by freeze-drying to form porous chitosan scaffolds with different pore sizes. The chitosan scaffolds were then used to investigate the effect of the controlled release of fibroblast growth factor-basic (bFGF) and transforming growth factor-β1 (TGFβ1) on mouse fibroblast cells (L929) and bovine carotid endothelial cells (BEC). The biocompatibility of the prepared chitosan scaffold was confirmed with WST-1 proliferation and viability assay, which demonstrated that the material is suitable for cell growth. The results of this study show that the pore sizes of the porous scaffolds prepared by freeze-drying can change depending on the pre-freezing temperature and time via the formation of ice crystals. In this study, the scaffolds with the largest pore size were found to be 153 ± 32 μm and scaffolds with the smallest pores to be 34 ± 9 μm. Through cell culture analysis, it was found that the concentration that increased proliferation of L929 cells for bFGF was 0.005 to 0.1 ng/mL, and the concentration for TGFβ1 was 0.005 to 1 ng/mL. The cell culture of the chitosan scaffold and growth factors shows that 3.75 ng of bFGF in scaffolds with pore sizes of 153 ± 32 μm can promote L929 cell proliferation, while 400 pg of TGFβ1 in scaffolds with pore size of 34 ± 9 μm can enhance the proliferation of L929 cells, but also inhibit BEC proliferation. It is proposed that the prepared chitosan scaffolds can form a multi-drug (bFGF and TGFβ1) release dressing that has the ability to control wound healing via regulating the proliferation of different cell types. PMID:29230255

A healing method of tympanic membrane perforations using three-dimensional porous chitosan scaffolds.

PubMed

Kim, Jangho; Kim, Seung Won; Choi, Seong Jun; Lim, Ki Taek; Lee, Jong Bin; Seonwoo, Hoon; Choung, Pill-Hoon; Park, Keehyun; Cho, Chong-Su; Choung, Yun-Hoon; Chung, Jong Hoon

2011-11-01

Both surgical tympanoplasty and paper patch grafts are frequently procedured to heal tympanic membrane (TM) perforation or chronic otitis media, despite their many disadvantages. In this study, we report a new healing method of TM perforation by using three-dimensional (3D) porous chitosan scaffolds (3D chitosan scaffolds) as an alternative method to surgical treatment or paper patch graft. Various 3D chitosan scaffolds were prepared; and the structural characteristics, mechanical property, in vitro biocompatibility, and healing effects of the 3D chitosan scaffolds as an artificial TM in in vivo animal studies were investigated. A 3D chitosan scaffold of 5 wt.% chitosan concentration showed good proliferation of TM cells in an in vitro study, as well as suitable structural characteristics and mechanical property, as compared with either 1% or 3% chitosan. In in vivo animal studies, 3D chitosan scaffold were able to migrate through the pores and surfaces of TM cells, thus leading to more effective TM regeneration than paper patch technique. Histological observations demonstrated that the regenerated TM with the 3D chitosan scaffold consisted of three (epidermal, connective tissue, and mucosal) layers and were thicker than normal TMs. The 3D chitosan scaffold technique may be an optimal healing method used in lieu of surgical tympanoplasty in certain cases to heal perforated TMs.

Preparation and Characterization of a Chitosan/Gelatin/Extracellular Matrix Scaffold and Its Application in Tissue Engineering.

PubMed

Wang, Xiaoyan; Yu, Tailong; Chen, Guanghua; Zou, Jilong; Li, Jianzhong; Yan, Jinglong

2017-03-01

Previous studies have demonstrated that extracellular matrix (ECM) can be used in tissue engineering due to its bioactivity. However, adipose-derived ECM (A-dECM) has never been applied in bone tissue engineering, and it is unknown whether it would be beneficial to the growth of bone marrow mesenchymal stem cells (BMSCs). In this study, we produced chitosan/gelatin/A-dECM (C/G/A-dECM) scaffolds via lyophilization and crosslinking; chitosan/gelatin (C/G) scaffolds were used as controls. For the C/G/A-dECM scaffolds, the average pore size was 285.93 ± 85.39 μm; the average porosity was 90.62 ± 3.65%; the average compressive modulus was 0.87 ± 0.05 kPa; and the average water uptake ratio was 13.73 ± 1.16. In vitro, A-dECM scaffolds could promote the attachment and proliferation of BMSCs. In the same osteogenic-inducing reagent, better osteogenic differentiation could be observed for the C/G/A-dECM scaffolds than for the C/G scaffolds. Thus, we conclude that A-dECM is a promising material and that C/G/A-dECM scaffolds are a candidate for bone tissue engineering.

Highly aligned porous Ti scaffold coated with bone morphogenetic protein-loaded silica/chitosan hybrid for enhanced bone regeneration.

PubMed

Jung, Hyun-Do; Yook, Se-Won; Han, Cheol-Min; Jang, Tae-Sik; Kim, Hyoun-Ee; Koh, Young-Hag; Estrin, Yuri

2014-07-01

Porous Ti has been widely investigated for orthopedic and dental applications on account of their ability to promote implant fixation via bone ingrowth into pores. In this study, highly aligned porous Ti scaffolds coated with a bone morphogenetic protein (BMP)-loaded silica/chitosan hybrid were produced, and their bone regeneration ability was evaluated by in vivo animal experiments. Reverse freeze casting allowed for the creation of highly aligned pores, resulting in a high compressive strength of 254 ± 21 MPa of the scaffolds at a porosity level of ∼51 vol %. In addition, a BMP-loaded silica/chitosan hybrid coating layer with a thickness of ∼1 μm was uniformly deposited on the porous Ti scaffold, which enabled the sustained release of the BMP over a prolonged period of time up to 26 days. The cumulative amount of the BMP released was ∼4 μg, which was much higher than that released from the specimen without a hybrid coating layer. In addition, the bone regeneration ability of the porous Ti scaffold with a BMP-loaded silica/chitosan coating layer was examined by in vivo animal testing using a rabbit calvarial defect model and compared with those of the as-produced porous Ti scaffold and porous Ti scaffold with a silica/chitosan coating layer. After 4 weeks of healing, the specimen coated with a BMP-loaded silica/chitosan hybrid showed a much higher bone regeneration volume (∼36%) than the as-produced specimen (∼15%) (p < 0.005) and even the specimen coated with a silica/chitosan hybrid (∼25%) (p < 0.05). © 2013 Wiley Periodicals, Inc.

Preparation and characterization of gelatin-chitosan-nanoβ-TCP based scaffold for orthopaedic application.

PubMed

Maji, Kanchan; Dasgupta, Sudip; Pramanik, Krishna; Bissoyi, Akalabya

2018-05-01

The primary aim of this study was to fabricate gelatin/chitosan/β-TCP (GCT) composite scaffold to improve its compressive mechanical behaviour and in-vivo biocompatibility with predictable degradation rate. Beta tricalcium phosphate (β-TCP) powder was synthesized in size range between 70-100 nm using aqueous precipitation route at a fixed Ca/P molar ratio of 1.5:1 at pH 10 and after subsequent heat treatment of as precipitated powder at 800 °C for 4 hours. The composite scaffolds were fabricated using solid-liquid phase separation of the slurry containing gelatin, chitosan, β-tricalcium phosphate in varying proportion and subsequent lyophilisation of the phase separated mixture. The prepared scaffolds exhibited high porosity (>80%) with pore sizes ranging between 78-382 μm as determined using Hg-porosimetry. SEM result revealed that incorporation of β-TCP to the extent of 30 wt% resulted in well-shaped and uniformly distributed interconnected pores of average pore size of 120 ± 18.6 μm in it. Compressive strength of the scaffolds was increased from 0.8 MPa to 2.45 MPa on increase in β-TCP content from 10 wt%-30 wt% in the prepared scaffold. Human Umbilical Cord derived mesenchymal stem cells (MSCs) exhibited higher degree of lamellopodia and fillopodia extensions and better spreading behaviour onto GCT30 scaffold. MTT assay and immunocytochemistry studies with cultured MSCs revealed that GCT30 scaffolds were more conducive to MSC's proliferation and differentiation into osteoblast lineage. In vivo implantation of GCT30 scaffold subcutaneously into mice did not indicate any significant inflammatory reaction, but ongoing vascularization. Copyright © 2018. Published by Elsevier B.V.

Fabrication and characterization of novel nano-biocomposite scaffold of chitosan-gelatin-alginate-hydroxyapatite for bone tissue engineering.

PubMed

Sharma, Chhavi; Dinda, Amit Kumar; Potdar, Pravin D; Chou, Chia-Fu; Mishra, Narayan Chandra

2016-07-01

A novel nano-biocomposite scaffold was fabricated in bead form by applying simple foaming method, using a combination of natural polymers-chitosan, gelatin, alginate and a bioceramic-nano-hydroxyapatite (nHAp). This approach of combining nHAp with natural polymers to fabricate the composite scaffold, can provide good mechanical strength and biological property mimicking natural bone. Environmental scanning electron microscopy (ESEM) images of the nano-biocomposite scaffold revealed the presence of interconnected pores, mostly spread over the whole surface of the scaffold. The nHAp particulates have covered the surface of the composite matrix and made the surface of the scaffold rougher. The scaffold has a porosity of 82% with a mean pore size of 112±19.0μm. Swelling and degradation studies of the scaffold showed that the scaffold possesses excellent properties of hydrophilicity and biodegradability. Short term mechanical testing of the scaffold does not reveal any rupturing after agitation under physiological conditions, which is an indicative of good mechanical stability of the scaffold. In vitro cell culture studies by seeding osteoblast cells over the composite scaffold showed good cell viability, proliferation rate, adhesion and maintenance of osteoblastic phenotype as indicated by MTT assay, ESEM of cell-scaffold construct, histological staining and gene expression studies, respectively. Thus, it could be stated that the nano-biocomposite scaffold of chitosan-gelatin-alginate-nHAp has the paramount importance for applications in bone tissue-engineering in future regenerative therapies. Copyright © 2016 Elsevier B.V. All rights reserved.

Influence of processing parameters on pore structure of 3D porous chitosan-alginate polyelectrolyte complex scaffolds.

PubMed

Florczyk, Stephen J; Kim, Dae-Joon; Wood, David L; Zhang, Miqin

2011-09-15

Fabrication of porous polymeric scaffolds with controlled structure can be challenging. In this study, we investigated the influence of key experimental parameters on the structures and mechanical properties of resultant porous chitosan-alginate (CA) polyelectrolyte complex (PEC) scaffolds, and on proliferation of MG-63 osteoblast-like cells, targeted at bone tissue engineering. We demonstrated that the porous structure is largely affected by the solution viscosity, which can be regulated by the acetic acid and alginate concentrations. We found that the CA PEC solutions with viscosity below 300 Pa.s yielded scaffolds of uniform pore structure and that more neutral pH promoted more complete complexation of chitosan and alginate, yielding stiffer scaffolds. CA PEC scaffolds produced from solutions with viscosities below 300 Pa.s also showed enhanced cell proliferation compared with other samples. By controlling the key experimental parameters identified in this study, CA PEC scaffolds of different structures can be made to suit various tissue engineering applications. Copyright © 2011 Wiley Periodicals, Inc.

Preparation of three-dimensional macroporous chitosan-gelatin B microspheres and HepG2-cell culture.

PubMed

Huang, Fang; Cui, Long; Peng, Cheng-Hong; Wu, Xu-Bo; Han, Bao-San; Dong, Ya-Dong

2016-12-01

Chitosan-gelatin B microspheres with an open, interconnected, highly macroporous (100-200 µm) structure were prepared via a three-step protocol combining freeze-drying with an electrostatic and ionic cross-linking method. Saturated tripolyphosphate ethanol solution (85% ethanol) was chosen as the crosslinking agent to prevent destruction of the porous structure and to improve the biostability of the chitosan-gelatin B microspheres, with N-(3-dimethylaminopropyl)-N'-ethyl-carbodiimide/N-hydroxysuccinimide as a second crosslinking agent to react with gelatin A and fixed chitosan-gelatin B microspheres to attain improved biocompatibility. Water absorption of the three-dimensional macroporous chitosan-gelatin B microspheres (3D-P-CGMs) was 12.84, with a porosity of 85.45%. In vitro lysozyme degradation after 1, 3, 5, 7, 10, 14, and 21 days showed improved biodegradation in the 3D-P-CGMs. The morphology of human hepatoma cell lines (HepG2 cells) cultured on the 3D-P-CGMs was spherical, unlike that of cells cultured under traditional two-dimensional conditions. Scanning electron microscopy and paraffin sections were used to confirm the porous structure of the 3D-P-CGMs. HepG2 cells were able to migrate inside through the pore. Cell proliferation and levels of albumin and lactate dehydrogenase suggested that the 3D-P-CGMs could provide a larger specific surface area and an appropriate microenvironment for cell growth and survival. Hence, the 3D-P-CGMs are eminently suitable as macroporous scaffolds for cell cultures in tissue engineering and cell carrier studies. Copyright © 2014 John Wiley & Sons, Ltd. Copyright © 2014 John Wiley & Sons, Ltd.

A gelatin composite scaffold strengthened by drug-loaded halloysite nanotubes.

PubMed

Ji, Lijun; Qiao, Wei; Zhang, Yuheng; Wu, Huayu; Miao, Shiyong; Cheng, Zhilin; Gong, Qianming; Liang, Ji; Zhu, Aiping

2017-09-01

Mechanical properties and anti-infection are two of the most concerned issues for artificial bone grafting materials. Bone regeneration porous scaffolds with sustained drug release were developed by freeze-drying the mixture of nanosized drug-loaded halloysite nanotubes (HNTs) and gelatin. The scaffolds showed porous structure and excellent biocompatibility. The mechanical properties of the obtained composite scaffolds were enhanced significantly by HNTs to >300%, comparing to those of gelatin scaffold, and match to those of natural cancellous bones. The ibuprofen-loaded HNTs incorporated in the scaffolds allowed extended drug release over 100h, comparing to 8h when directly mixed the drug into the gelatin scaffold. The biological properties of the composite scaffolds were investigated by culturing MG63 cells on them. The HNTs/gelatin scaffolds with excellent mechanical properties and sustained drug release could be a promising artificial bone grating material. Copyright © 2017 Elsevier B.V. All rights reserved.

Electrically Conductive Chitosan/Carbon Scaffolds for Cardiac Tissue Engineering

PubMed Central

2015-01-01

In this work, carbon nanofibers were used as doping material to develop a highly conductive chitosan-based composite. Scaffolds based on chitosan only and chitosan/carbon composites were prepared by precipitation. Carbon nanofibers were homogeneously dispersed throughout the chitosan matrix, and the composite scaffold was highly porous with fully interconnected pores. Chitosan/carbon scaffolds had an elastic modulus of 28.1 ± 3.3 KPa, similar to that measured for rat myocardium, and excellent electrical properties, with a conductivity of 0.25 ± 0.09 S/m. The scaffolds were seeded with neonatal rat heart cells and cultured for up to 14 days, without electrical stimulation. After 14 days of culture, the scaffold pores throughout the construct volume were filled with cells. The metabolic activity of cells in chitosan/carbon constructs was significantly higher as compared to cells in chitosan scaffolds. The incorporation of carbon nanofibers also led to increased expression of cardiac-specific genes involved in muscle contraction and electrical coupling. This study demonstrates that the incorporation of carbon nanofibers into porous chitosan scaffolds improved the properties of cardiac tissue constructs, presumably through enhanced transmission of electrical signals between the cells. PMID:24417502

Gelatin Scaffolds with Controlled Pore Structure and Mechanical Property for Cartilage Tissue Engineering.

PubMed

Chen, Shangwu; Zhang, Qin; Nakamoto, Tomoko; Kawazoe, Naoki; Chen, Guoping

2016-03-01

Engineering of cartilage tissue in vitro using porous scaffolds and chondrocytes provides a promising approach for cartilage repair. However, nonuniform cell distribution and heterogeneous tissue formation together with weak mechanical property of in vitro engineered cartilage limit their clinical application. In this study, gelatin porous scaffolds with homogeneous and open pores were prepared using ice particulates and freeze-drying. The scaffolds were used to culture bovine articular chondrocytes to engineer cartilage tissue in vitro. The pore structure and mechanical property of gelatin scaffolds could be well controlled by using different ratios of ice particulates to gelatin solution and different concentrations of gelatin. Gelatin scaffolds prepared from ≥70% ice particulates enabled homogeneous seeding of bovine articular chondrocytes throughout the scaffolds and formation of homogeneous cartilage extracellular matrix. While soft scaffolds underwent cellular contraction, stiff scaffolds resisted cellular contraction and had significantly higher cell proliferation and synthesis of sulfated glycosaminoglycan. Compared with the gelatin scaffolds prepared without ice particulates, the gelatin scaffolds prepared with ice particulates facilitated formation of homogeneous cartilage tissue with significantly higher compressive modulus. The gelatin scaffolds with highly open pore structure and good mechanical property can be used to improve in vitro tissue-engineered cartilage.

Performance of PRP Associated with Porous Chitosan as a Composite Scaffold for Regenerative Medicine

PubMed Central

Shimojo, Andréa Arruda Martins; Perez, Amanda Gomes Marcelino; Galdames, Sofia Elisa Moraga; Brissac, Isabela Cambraia de Souza; Santana, Maria Helena Andrade

2015-01-01

This study aimed to evaluate the in vitro performance of activated platelet-rich plasma associated with porous sponges of chitosan as a composite scaffold for proliferation and osteogenic differentiation of human adipose tissue-derived mesenchymal stem cells. The sponges were prepared by controlled freezing (−20, −80, or −196°C) and lyophilization of chitosan solutions (1, 2, or 3% w/v). The platelet-rich plasma was obtained from controlled centrifugation of whole blood and activated with calcium and autologous serum. The composite scaffolds were prepared by embedding the sponges with the activated platelet-rich plasma. The results showed the performance of the scaffolds was superior to that of activated platelet-rich plasma alone, in terms of delaying the release of growth factors and increased proliferation of the stem cells. The best preparation conditions of chitosan composite scaffolds that coordinated the physicochemical and mechanical properties and cell proliferation were 3% (w/v) chitosan and a −20°C freezing temperature, while −196°C favored osteogenic differentiation. Although the composite scaffolds are promising for regenerative medicine, the structures require stabilization to prevent the collapse observed after five days. PMID:25821851

Three-dimensional dynamic fabrication of engineered cartilage based on chitosan/gelatin hybrid hydrogel scaffold in a spinner flask with a special designed steel frame.

PubMed

Song, Kedong; Li, Liying; Li, Wenfang; Zhu, Yanxia; Jiao, Zeren; Lim, Mayasari; Fang, Meiyun; Shi, Fangxin; Wang, Ling; Liu, Tianqing

2015-10-01

Cartilage transplantation using in vitro tissue engineered cartilage is considered a promising treatment for articular cartilage defects. In this study, we assessed the advantages of adipose derived stem cells (ADSCs) combined with chitosan/gelatin hybrid hydrogel scaffolds, which acted as a cartilage biomimetic scaffold, to fabricate a tissue engineered cartilage dynamically in vitro and compared this with traditional static culture. Physical properties of the hydrogel scaffolds were evaluated and ADSCs were inoculated into the hydrogel at a density of 1×10(7) cells/mL and cultured in a spinner flask with a special designed steel framework and feed with chondrogenic inductive media for two weeks. The results showed that the average pore size, porosity, swelling rate and elasticity modulus of hybrid scaffolds with good biocompatibility were 118.25±19.51 μm, 82.60±2.34%, 361.28±0.47% and 61.2±0.16 kPa, respectively. ADSCs grew well in chitosan/gelatin hybrid scaffold and successfully differentiated into chondrocytes, showing that the scaffolds were suitable for tissue engineering applications in cartilage regeneration. Induced cells cultivated in a dynamic spinner flask with a special designed steel frame expressed more proteoglycans and the cell distribution was much more uniform with the scaffold being filled mostly with extracellular matrix produced by cells. A spinner flask with framework promoted proliferation and chondrogenic differentiation of ADSCs within chitosan/gelatin hybrid scaffolds and accelerated dynamic fabrication of cell-hydrogel constructs, which could be a selective and good method to construct tissue engineered cartilage in vitro. Copyright © 2015 Elsevier B.V. All rights reserved.

Alginate/Gelatin scaffolds incorporated with Silibinin-loaded Chitosan nanoparticles for bone formation in vitro.

PubMed

Leena, R S; Vairamani, M; Selvamurugan, N

2017-10-01

Silibinin is a plant derived flavonolignan known for its multiple biological properties, but its role in the promotion of bone formation has not yet been well studied. Moreover, the delivery of Silibinin is hindered by its complex hydrophobic nature, which limits its bioavailability. Hence, in this study, we fabricated a drug delivery system using chitosan nanoparticles loaded with Silibinin at different concentrations (20μM, 50μM, and 100μM). They were then incorporated into scaffolds containing Alginate and Gelatin (Alg/Gel) for the sustained and prolonged release of Silibinin. The Silibinin-loaded chitosan nanoparticles (SCN) were prepared using the ionic gelation technique, and the scaffolds (Alg/Gel-SCN) were synthesized by the conventional method of freeze drying. The scaffolds were subjected to physicochemical and material characterization studies. The addition of SCN did not affect the porosity of the scaffolds, yet increased the protein adsorption, degradation rates, and bio-mineralization. These scaffolds were biocompatible with mouse mesenchymal stem cells. The scaffolds loaded with 50μM Silibinin promoted osteoblast differentiation, which was determined at cellular and molecular levels. Recent studies indicated the role of microRNAs (miRNAs) in osteogenesis and we found that the Silibinin released from scaffolds regulated miRNAs that control the bone morphogenetic protein pathway. Hence, our results suggest the potential for sustained and prolonged release of Silibinin to promote bone formation and, thus, these Alg/Gel-SCN scaffolds may be candidates for bone tissue engineering applications. Copyright © 2017 Elsevier B.V. All rights reserved.

Development of Novel Biocomposite Scaffold of Chitosan-Gelatin/Nanohydroxyapatite for Potential Bone Tissue Engineering Applications

NASA Astrophysics Data System (ADS)

Dan, Yang; Liu, Ouyang; Liu, Yong; Zhang, Yuan-Yuan; Li, Shuai; Feng, Xiao-bo; Shao, Zeng-wu; Yang, Cao; Yang, Shu-Hua; Hong, Ji-bo

2016-11-01

In this study, a three-dimensional chitosan-gelatin/nanohydroxyapatite (ChG/nHaP) scaffold was successfully fabricated and characterized in terms of swelling, degradation, cell proliferation, cell attachment, and mineralization characterizations. The ChG/nHaP scaffold was fabricated with a mean pore size of 100-180 μm. Our results showed that the physicochemical and biological properties of the scaffolds were affected by the presence of HaP. The swelling and degradation characteristics of the ChG scaffold were remarkably decreased by the addition of HaP. On the other hand, the presence of HaP remarkably improved the MC3T3-E1 cell attachment and cell growth in the scaffold membrane. The biocompatible nature of the ChG/nHaP scaffold leads to the development of finely scaled mineral deposits on the scaffold membrane. Thus, HaP played an important role in improving the biological performance of the scaffold. Therefore, the ChG/nHaP scaffold could be applied as a suitable material for bone tissue engineering applications.

Preparation and characterization of collagen/PLA, chitosan/PLA, and collagen/chitosan/PLA hybrid scaffolds for cartilage tissue engineering.

PubMed

Haaparanta, Anne-Marie; Järvinen, Elina; Cengiz, Ibrahim Fatih; Ellä, Ville; Kokkonen, Harri T; Kiviranta, Ilkka; Kellomäki, Minna

2014-04-01

In this study, three-dimensional (3D) porous scaffolds were developed for the repair of articular cartilage defects. Novel collagen/polylactide (PLA), chitosan/PLA, and collagen/chitosan/PLA hybrid scaffolds were fabricated by combining freeze-dried natural components and synthetic PLA mesh, where the 3D PLA mesh gives mechanical strength, and the natural polymers, collagen and/or chitosan, mimic the natural cartilage tissue environment of chondrocytes. In total, eight scaffold types were studied: four hybrid structures containing collagen and/or chitosan with PLA, and four parallel plain scaffolds with only collagen and/or chitosan. The potential of these types of scaffolds for cartilage tissue engineering applications were determined by the analysis of the microstructure, water uptake, mechanical strength, and the viability and attachment of adult bovine chondrocytes to the scaffolds. The manufacturing method used was found to be applicable for the manufacturing of hybrid scaffolds with highly porous 3D structures. All the hybrid scaffolds showed a highly porous structure with open pores throughout the scaffold. Collagen was found to bind water inside the structure in all collagen-containing scaffolds better than the chitosan-containing scaffolds, and the plain collagen scaffolds had the highest water absorption. The stiffness of the scaffold was improved by the hybrid structure compared to plain scaffolds. The cell viability and attachment was good in all scaffolds, however, the collagen hybrid scaffolds showed the best penetration of cells into the scaffold. Our results show that from the studied scaffolds the collagen/PLA hybrids are the most promising scaffolds from this group for cartilage tissue engineering.

Chitosan-silica hybrid porous membranes.

PubMed

Pandis, Christos; Madeira, Sara; Matos, Joana; Kyritsis, Apostolos; Mano, João F; Ribelles, José Luis Gómez

2014-09-01

Chitosan-silica porous hybrids were prepared by a novel strategy in order to improve the mechanical properties of chitosan (CHT) in the hydrogel state. The inorganic silica phase was introduced by sol-gel reactions in acidic medium inside the pores of already prepared porous scaffolds. In order to make the scaffolds insoluble in acidic media chitosan was cross-linked by genipin (GEN) with an optimum GEN concentration of 3.2 wt.%. Sol-gel reactions took place with Tetraethylorthosilicate (TEOS) and 3-glycidoxypropyltrimethoxysilane (GPTMS) acting as silica precursors. GPTMS served also as a coupling agent between the free amino groups of chitosan and the silica network. The morphology study of the composite revealed that the silica phase appears as a layer covering the chitosan membrane pore walls. The mechanical properties of the hybrids were characterized by means of compressive stress-strain measurements. By immersion in water the hybrids exhibit an increase in elastic modulus up to two orders of magnitude. Copyright © 2014 Elsevier B.V. All rights reserved.

Patient-Derived Human Induced Pluripotent Stem Cells From Gingival Fibroblasts Composited With Defined Nanohydroxyapatite/Chitosan/Gelatin Porous Scaffolds as Potential Bone Graft Substitutes.

PubMed

Ji, Jun; Tong, Xin; Huang, Xiaofeng; Zhang, Junfeng; Qin, Haiyan; Hu, Qingang

2016-01-01

Human embryonic stem cells and adult stem cells have always been the cell source for bone tissue engineering. However, their limitations are obvious, including ethical concerns and/or a short lifespan. The use of human induced pluripotent stem cells (hiPSCs) could avoid these problems. Nanohydroxyapatite (nHA) is an important component of natural bone and bone tissue engineering scaffolds. However, its regulation on osteogenic differentiation with hiPSCs from human gingival fibroblasts (hGFs) is unknown. The purpose of the present study was to investigate the osteogenic differentiation of hiPSCs from patient-derived hGFs regulated by nHA/chitosan/gelatin (HCG) scaffolds with different nHA ratios, such as HCG-111 (1 wt/vol% nHA) and HCG-311 (3 wt/vol% nHA). First, hGFs were reprogrammed into hiPSCs, which have enhanced osteogenic differentiation capability. Second, HCG-111 and HCG-311 scaffolds were successfully synthesized. Finally, hiPSC/HCG complexes were cultured in vitro or subcutaneously transplanted into immunocompromised mice in vivo. The osteogenic differentiation effects of two types of HCG scaffolds on hiPSCs were assessed for up to 12 weeks. The results showed that HCG-311 increased osteogenic-related gene expression of hiPSCs in vitro proved by quantitative real-time polymerase chain reaction, and hiPSC/HCG-311 complexes formed much bone-like tissue in vivo, indicated by cone-beam computed tomography imaging, H&E staining, Masson staining, and RUNX-2, OCN immunohistochemistry staining. In conclusion, our study has shown that osteogenic differentiation of hiPSCs from hGFs was improved by HCG-311. The mechanism might be that the nHA addition stimulates osteogenic marker expression of hiPSCs from hGFs. Our work has provided an innovative autologous cell-based bone tissue engineering approach with soft tissues such as clinically abundant gingiva. The present study focused on patient-personalized bone tissue engineering. Human induced pluripotent stem cells

Patient-Derived Human Induced Pluripotent Stem Cells From Gingival Fibroblasts Composited With Defined Nanohydroxyapatite/Chitosan/Gelatin Porous Scaffolds as Potential Bone Graft Substitutes

PubMed Central

Ji, Jun; Tong, Xin; Huang, Xiaofeng; Zhang, Junfeng

2016-01-01

Human embryonic stem cells and adult stem cells have always been the cell source for bone tissue engineering. However, their limitations are obvious, including ethical concerns and/or a short lifespan. The use of human induced pluripotent stem cells (hiPSCs) could avoid these problems. Nanohydroxyapatite (nHA) is an important component of natural bone and bone tissue engineering scaffolds. However, its regulation on osteogenic differentiation with hiPSCs from human gingival fibroblasts (hGFs) is unknown. The purpose of the present study was to investigate the osteogenic differentiation of hiPSCs from patient-derived hGFs regulated by nHA/chitosan/gelatin (HCG) scaffolds with different nHA ratios, such as HCG-111 (1 wt/vol% nHA) and HCG-311 (3 wt/vol% nHA). First, hGFs were reprogrammed into hiPSCs, which have enhanced osteogenic differentiation capability. Second, HCG-111 and HCG-311 scaffolds were successfully synthesized. Finally, hiPSC/HCG complexes were cultured in vitro or subcutaneously transplanted into immunocompromised mice in vivo. The osteogenic differentiation effects of two types of HCG scaffolds on hiPSCs were assessed for up to 12 weeks. The results showed that HCG-311 increased osteogenic-related gene expression of hiPSCs in vitro proved by quantitative real-time polymerase chain reaction, and hiPSC/HCG-311 complexes formed much bone-like tissue in vivo, indicated by cone-beam computed tomography imaging, H&E staining, Masson staining, and RUNX-2, OCN immunohistochemistry staining. In conclusion, our study has shown that osteogenic differentiation of hiPSCs from hGFs was improved by HCG-311. The mechanism might be that the nHA addition stimulates osteogenic marker expression of hiPSCs from hGFs. Our work has provided an innovative autologous cell-based bone tissue engineering approach with soft tissues such as clinically abundant gingiva. Significance The present study focused on patient-personalized bone tissue engineering. Human induced

Hierarchically porous structure, mechanical strength and cell biological behaviors of calcium phosphate composite scaffolds prepared by combination of extrusion and porogen burnout technique and enhanced by gelatin.

PubMed

Feng, Shenglei; He, Fupo; Ye, Jiandong

2018-01-01

In this study, hierarchically porous calcium phosphate scaffolds (HTCP) with unidirectional pores, transversely interconnected pores, and micropores were fabricated by the combination of extrusion and porogen burnout technique. Gelatin was incorporated into the HTCP scaffolds by vacuum-impregnation of gelatin solution and subsequent freeze-drying. The phase composition, microstructure, physical and cytobiological properties were analyzed. The results showed that the HTCP scaffolds were composed of β-tricalcium phosphate with minor hydroxyapatite. The HTCP scaffolds had unidirectional pores (~400μm), transversely interconnected pores (~130μm) and micropores (~1μm). The incorporation of gelatin significantly increased the compressive strength, toughness, and cell seeding of the HTCP scaffolds. The composite scaffolds showed excellent cytocompatibility. The hierarchically porous calcium phosphate composite scaffolds may have potential application prospects in bone tissue engineering. Copyright © 2017 Elsevier B.V. All rights reserved.

Anti-biofouling 3D porous systems: the blend effect of oxazoline-based oligomers on chitosan scaffolds.

PubMed

Correia, Vanessa G; Coelho, Margarida; Barroso, Telma; Raje, Vivek P; Bonifácio, Vasco D B; Casimiro, Teresa; Pinho, Mariana G; Aguiar-Ricardo, Ana

2013-01-01

The production, characterization and anti-biofouling activity of 3D porous scaffolds combining different blends of chitosan and oxazoline-based antimicrobial oligomers is reported. The incorporation of ammonium quaternized oligo(2-oxazoline)s into the composition of the scaffold enhances the stability of the chitosan scaffold under physiological conditions as well as its ability to repel protein adsorption. The blended scaffolds showed mean pore sizes in the range of 18-32 μm, a good pore interconnectivity and high porosity, as well as a large surface area, ultimate key features for anti-biofouling applications. Bovine serum albumin (BSA) adhesion profiles showed that the composition of the scaffolds plays a critical role in the chitosan-oligooxazoline system. Oligobisoxazoline-enriched scaffolds (20% w/w, CB8020) decreased protein adsorption (BSA) by up to 70%. Moreover, 1 mg of CB8020 was able to kill 99.9% of Escherichia coli cells upon contact, demonstrating its potential as promising material for production of tailored non-fouling 3D structures to be used in the construction of novel devices with applications in the biomedical field and water treatment processes.

3D porous chitosan scaffolds suit survival and neural differentiation of dental pulp stem cells.

PubMed

Feng, Xingmei; Lu, Xiaohui; Huang, Dan; Xing, Jing; Feng, Guijuan; Jin, Guohua; Yi, Xin; Li, Liren; Lu, Yuanzhou; Nie, Dekang; Chen, Xiang; Zhang, Lei; Gu, Zhifeng; Zhang, Xinhua

2014-08-01

A key aspect of cell replacement therapy in brain injury treatment is construction of a suitable biomaterial scaffold that can effectively carry and transport the therapeutic cells to the target area. In the present study, we created small 3D porous chitosan scaffolds through freeze-drying, and showed that these can support and enhance the differentiation of dental pulp stem cells (DPSCs) to nerve cells in vitro. The DPSCs were collected from the dental pulp of adult human third molars. At a swelling rate of ~84.33 ± 10.92 %, the scaffold displayed high porosity and interconnectivity of pores, as revealed by SEM. Cell counting kit-8 assay established the biocompatibility of the chitosan scaffold, supporting the growth and survival of DPSCs. The successful neural differentiation of DPSCs was assayed by RT-PCR, western blotting, and immunofluorescence. We found that the scaffold-attached DPSCs showed high expression of Nestin that decreased sharply following induction of differentiation. Exposure to the differentiation media also increased the expression of neural molecular markers Microtubule-associated protein 2, glial fibrillary acidic protein, and 2',3'-cyclic nucleotide phosphodiesterase. This study demonstrates that the granular 3D chitosan scaffolds are non-cytotoxic, biocompatible, and provide a conducive and favorable micro-environment for attachment, survival, and neural differentiation of DPSCs. These scaffolds have enormous potential to facilitate future advances in treatment of brain injury.

Electrostatic flocking of chitosan fibres leads to highly porous, elastic and fully biodegradable anisotropic scaffolds.

PubMed

Gossla, Elke; Tonndorf, Robert; Bernhardt, Anne; Kirsten, Martin; Hund, Rolf-Dieter; Aibibu, Dilibar; Cherif, Chokri; Gelinsky, Michael

2016-10-15

Electrostatic flocking - a common textile technology which has been applied in industry for decades - is based on the deposition of short polymer fibres in a parallel aligned fashion on flat or curved substrates, covered with a layer of a suitable adhesive. Due to their highly anisotropic properties the resulting velvet-like structures can be utilised as scaffolds for tissue engineering applications in which the space between the fibres can be defined as pores. In the present study we have developed a fully resorbable compression elastic flock scaffold from a single material system based on chitosan. The fibres and the resulting scaffolds were analysed concerning their structural and mechanical properties and the biocompatibility was tested in vitro. The tensile strength and Young's modulus of the chitosan fibres were analysed as a function of the applied sterilisation technique (ethanol, supercritical carbon dioxide, γ-irradiation and autoclaving). All sterilisation methods decreased the Young's modulus (from 14GPa to 6-12GPa). The tensile strength was decreased after all treatments - except after the autoclaving of chitosan fibres submerged in water. Compressive strength of the highly porous flock scaffolds was 18±6kPa with a elastic modulus in the range of 50-100kPa. The flocked scaffolds did not show any cytotoxic effect during indirect or direct culture of human mesenchymal stem cells or the sarcoma osteogenic cell line Saos-2. Furthermore cell adhesion and proliferation of both cell types could be observed. This is the first demonstration of a fully biodegradable scaffold manufactured by electrostatic flocking. Most tissues possess anisotropic fibrous structures. In contrast, most of the commonly used scaffolds have an isotropic morphology. By utilising the textile technology of electrostatic flocking, highly porous and clearly anisotropic scaffolds can be manufactured. Flocking leads to parallel aligned short fibres, glued on the surface of a substrate

Anti-inflammatory effects of sodium alginate/gelatine porous scaffolds merged with fucoidan in murine microglial BV2 cells.

PubMed

Nguyen, Van-Tinh; Ko, Seok-Chun; Oh, Gun-Woo; Heo, Seong-Yeong; Jeon, You-Jin; Park, Won Sun; Choi, Il-Whan; Choi, Sung-Wook; Jung, Won-Kyo

2016-12-01

Microglia are the immune cells of the central nervous system (CNS). Overexpression of inflammatory mediators by microglia can induce several neurological diseases. Thus, the underlying basic requirement for neural tissue engineering is to develop materials that exhibit little or no neuro-inflammatory effects. In this study, we have developed a method to create porous scaffolds by adding fucoidan (Fu) into porous sodium alginate (Sa)/gelatine (G) (SaGFu). For mechanical characterization, in vitro degradation, stress/strain, swelling, and pore size were measured. Furthermore, the biocompatibility was evaluated by assessing the adhesion and proliferation of BV2 microglial cells on the SaGFu porous scaffolds using scanning electron microscopy (SEM) and lactate dehydrogenase (LDH) assay, respectively. Moreover, we studied the neuro-inflammatory effects of SaGFu on BV2 microglial cells. The effect of gelatine and fucoidan content on the various properties of the scaffold was investigated and the results showed that mechanical properties increased porosity and swelling ratio with an increase in the gelatine and fucoidan, while the in vitro biodegradability decreased. The average SaGFu diameter attained by fabrication of SaGFu ranged from 60 to 120μm with high porosity (74.44%-88.30%). Cell culture using gelatine 2.0% (SaG2Fu) and 4.0% (SaG4Fu), showed good cell proliferation; more than 60-80% that with Sa alone. Following stimulation with 0.5μg/mL LPS, microglia cultured in porous SaGFu decreased their expression of nitric oxide (NO), prostaglandin E2 (PGE2), and reactive oxygen species (ROS). SaG2Fu and SaG4Fu also inhibited the activation and translocation of p65 NF-κB protein levels, resulting in reduction of NO, ROS, and PGE2 production. These results provide insights into the diverse biological effects and opens new avenues for the applications of SaGFu in neuroscience. Copyright © 2016 Elsevier B.V. All rights reserved.

Preparation of 3D fibroin/chitosan blend porous scaffold for tissue engineering via a simplified method.

PubMed

Ruan, Yuhui; Lin, Hong; Yao, Jinrong; Chen, Zhengrong; Shao, Zhengzhong

2011-03-10

In this work, we developed a simple and flexible method to manufacture a 3D porous scaffold based on the blend of regenerated silk fibroin (RSF) and chitosan (CS). No crosslinker or other toxic reagents were used in this method. The pores of resulted 3D scaffolds were connected with each other, and their sizes could be easily controlled by the concentration of the mixed solution. Compared with pure RSF scaffolds, the water absorptivities of these RSF/CS blend scaffolds with significantly enhanced mechanical properties were greatly increased. The results of MTT and RT-PCR tests indicated that the chondrocytes grew very well in these blend RSF/CS porous scaffolds. This suggested that the RSF/CS blend scaffold prepared by this new method could be a promising candidate for applications in tissue engineering. Copyright © 2011 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Molecular interactions in gelatin/chitosan composite films.

PubMed

Qiao, Congde; Ma, Xianguang; Zhang, Jianlong; Yao, Jinshui

2017-11-15

Gelatin and chitosan were mixed at different mass ratios in solution forms, and the rheological properties of these film-forming solutions, upon cooling, were studied. The results indicate that the significant interactions between gelatin and chitosan promote the formation of multiple complexes, reflected by an increase in the storage modulus of gelatin solution. Furthermore, these molecular interactions hinder the formation of gelatin networks, consequently decreasing the storage modulus of polymer gels. Both hydrogen bonds and electrostatic interactions are formed between gelatin and chitosan, as evidenced by the shift of the amide-II bands of polymers. X-ray patterns of composite films indicate that the contents of triple helices decrease with increasing chitosan content. Only one glass transition temperature (T g ) was observed in composite films with different composition ratios, and it decreases gradually with an increase in chitosan proportion, indicating that gelatin and chitosan have good miscibility and form a wide range of blends. Copyright © 2017 Elsevier Ltd. All rights reserved.

Comparison of the properties of collagen-chitosan scaffolds after γ-ray irradiation and carbodiimide cross-linking.

PubMed

Chen, Zihao; Du, Tianming; Tang, Xiangyu; Liu, Changjun; Li, Ruixin; Xu, Cheng; Tian, Feng; Du, Zhenjie; Wu, Jimin

2016-07-01

The property of collagen-chitosan porous scaffold varies according to cross-linking density and scaffold composition. This study was designed to compare the properties of collagen-chitosan porous scaffolds cross-linked with γ-irradiation and carbodiimide (CAR) for the first time. Eleven sets of collagen-chitosan scaffolds containing different concentrations of chitosan at a 5% increasing gradient were fabricated. Fourier transform infrared spectroscopy was performed to confirm the success of cross-linking in the scaffolds. The scaffold morphology was evaluated under scanning electron microscope (SEM). SEM revealed that chitosan was an indispensable material for the fabrication of γ-ray irradiation scaffold. The microstructure of γ-ray irradiation scaffold was less stable than those of alternative scaffolds. Based upon swelling ratio, porosity factor, and collagenase degradation, γ-ray irradiation scaffold was less stable than CAR and 25% proportion of chitosan scaffolds. Mechanical property determines the orientation in γ-irradiation and CAR scaffold. In vitro degradation test indicated that γ-irradiation and CAR cross-linking can elevate the scaffold biocompatibility. Compared with γ-ray irradiation, CAR cross-linked scaffold containing 25% chitosan can more significantly enhance the bio-stability and biocompatibility of collagen-chitosan scaffolds. CAR cross-linked scaffold may be the best choice for future tissue engineering.

Characterization of gelatin/chitosan scaffold blended with aloe vera and snail mucus for biomedical purpose.

PubMed

López Angulo, Daniel Enrique; do Amaral Sobral, Paulo José

2016-11-01

Biologically active scaffolds used in tissue engineering and regenerative medicine have been generating promising results in skin replacement. The present study aims to test the hypothesis that the incorporation of Aloe vera and snail mucus into scaffolds based on gelatin and chitosan could improve their structure, composition and biodegradability, with a potential effect on bioactivity. Homogeneous pore diameter as well as pore walls in the composite scaffold could be seen in the SEM image. The pores in the scaffolds were interconnected and their sizes ranged from 93 to 296μm. The addition of Aloe vera and snail mucus enlarged the mean pore size with increased porosity and caused changes in the pore architecture. The FTIR analysis has shown good affinity and interaction between the matrix and the Aloe, which may decrease water-binding sites, so this fact hindered the water absorption capacity of the material. The mechanical properties could explain the highest swelling capacity of the snail scaffold, because the high percentage of elongation could facilitate the entry of liquid in it, generating a matrix with plenty of fluid retention. The real innovation in the present work could be the use of these substances (Aloe and snail mucus) for tissue engineering. Copyright © 2016 Elsevier B.V. All rights reserved.

Functionalization of chitosan/poly(lactic acid-glycolic acid) sintered microsphere scaffolds via surface heparinization for bone tissue engineering.

PubMed

Jiang, Tao; Khan, Yusuf; Nair, Lakshmi S; Abdel-Fattah, Wafa I; Laurencin, Cato T

2010-06-01

Scaffolds exhibiting biological recognition and specificity play an important role in tissue engineering and regenerative medicine. The bioactivity of scaffolds in turn influences, directs, or manipulates cellular responses. In this study, chitosan/poly(lactic acid-co-glycolic acid) (chitosan/PLAGA) sintered microsphere scaffolds were functionalized via heparin immobilization. Heparin was successfully immobilized on chitosan/PLAGA scaffolds with controllable loading efficiency. Mechanical testing showed that heparinization of chitosan/PLAGA scaffolds did not significantly alter the mechanical properties and porous structures. In addition, the heparinized chitosan/PLAGA scaffolds possessed a compressive modulus of 403.98 +/- 19.53 MPa and a compressive strength of 9.83 +/- 0.94 MPa, which are in the range of human trabecular bone. Furthermore, the heparinized chitosan/PLAGA scaffolds had an interconnected porous structure with a total pore volume of 30.93 +/- 0.90% and a median pore size of 172.33 +/- 5.89 mum. The effect of immobilized heparin on osteoblast-like MC3T3-E1 cell growth was investigated. MC3T3-E1 cells proliferated three dimensionally throughout the porous structure of the scaffolds. Heparinized chitosan/PLAGA scaffolds with low heparin loading (1.7 microg/scaffold) were shown to be capable of stimulating MC3T3-E1 cell proliferation by MTS assay and cell differentiation as evidenced by elevated osteocalcin expression when compared with nonheparinized chitosan/PLAGA scaffold and chitosan/PLAGA scaffold with high heparin loading (14.1 microg/scaffold). This study demonstrated the potential of functionalizing chitosan/PLAGA scaffolds via heparinization with improved cell functions for bone tissue engineering applications.

Evaluation of the effect of the degree of acetylation on the inflammatory response to 3D porous chitosan scaffolds.

PubMed

Barbosa, Judite N; Amaral, Isabel F; Aguas, Artur P; Barbosa, Mário A

2010-04-01

The effect of the degree of acetylation (DA) of 3D chitosan (Ch) scaffolds on the inflammatory reaction was investigated. Chitosan porous scaffolds with DAs of 4 and 15% were implanted using a subcutaneous air-pouch model of inflammation. The initial acute inflammatory response was evaluated 24 and 48 h after implantation. To characterize the initial response, the recruitment and adhesion of inflammatory cells to the implant site was studied. The fibrous capsule formation and the infiltration of inflammatory cells within the scaffolds were evaluated for longer implantation times (2 and 4 weeks). Chitosan with DA 15% attracted the highest number of leukocytes to the implant site. High numbers of adherent inflammatory cells were also observed in this material. For longer implantation periods Ch scaffolds with a DA of 15% induced the formation of a thick fibrous capsule and a high infiltration of inflammatory cells within the scaffold. Our results indicate that the biological response to implanted Ch scaffolds was influenced by the DA. Chitosan with a DA of 15% induce a more intense inflammatory response when compared with DA 4% Ch. Because inflammation and healing are interrelated, this result may provide clues for the relative importance of acetyl and amine functional groups in tissue repair and regeneration.

Engineered 3D-scaffolds of photocrosslinked chitosan-gelatin hydrogel hybrids for chronic wound dressings and regeneration.

PubMed

Carvalho, Isadora C; Mansur, Herman S

2017-09-01

Wound repair is one of the most complex biological processes in human life. To date, no ideal biomaterial solution has been identified, which that encompasses all functions and properties of real skin tissue. Thus, this study focused on the synthesis of new biocompatible hybrid hydrogel scaffolds based on methacrylate-functionalized high molecular mass chitosan with gelatin-A photocrosslinked with UV radiation to tailor matrix network properties. These hybrid hydrogels were produced via freeze-drying and were extensively characterized by swelling and degradation measurements, Fourier transform infrared spectroscopy (FTIR), UV-visible spectroscopy (UV-Vis), scanning electron microscopy (SEM-EDS), and micro-computed tomography (micro-CT). The results demonstrated that hydrogels were produced with broadly designed swelling degrees typically ranging from 500% to 2000%, which were significantly dependent on the relative concentration of polymers and irradiation time for crosslinking. Analogously, degradation was reduced with increased photocrosslinking of the network. Moreover, insights into the mechanism of photochemical crosslinking were suggested based on FTIR and UV-Vis analyses of the characteristic functional groups involved in the reactions. SEM analysis associated with micro-CT imaging of the hybrid scaffolds showed uniformly interconnected 3D porous structures, with architectural features affected by the crosslinking of the network. These hydrogels were biocompatible, with live cell viability responses of human embryonic kidney (HEK293T) cells being above 95%. Hence, novel hybrid hydrogels were designed and produced with tunable properties through photocrosslinking and with a biocompatible response suitable for use in wound dressing and skin tissue repair applications. Copyright © 2017 Elsevier B.V. All rights reserved.

Antibacterial chitosan coating on nano-hydroxyapatite/polyamide66 porous bone scaffold for drug delivery.

PubMed

Huang, Di; Zuo, Yi; Zou, Qin; Zhang, Li; Li, Jidong; Cheng, Lin; Shen, Juan; Li, Yubao

2011-01-01

This study describes a new drug-loaded coating scaffold applied in infection therapy during bone regeneration. Chitosan (CS) containing antibacterial berberine was coated on a nano-hydroxyapatite/polyamide66 (n-HA/PA66) scaffold to realize bone regeneration together with antimicrobial properties. The porous scaffold was fabricated using the phase-inversion method with a porosity of about 84% and macropore size of 400-600 μm. The morphology, mechanical properties and drug-release behavior were investigated at different ratios of chitosan to berberine. The results show that the elastic modulus and compressive strength of the coated scaffolds were improved to 35.4 MPa and 1.7 MPa, respectively, about 7 times and 3 times higher than the uncoated scaffolds. After a burst release of berberine within the first 3 h in PBS solution, a continuous berberine release can last 150 h, which is highly dependent on the coating concentration and suitable for antibacterial requirement of orthopaedic surgery. The bactericidal test confirms a strong antibiotic effect of the delivery system and the minimum inhibitory concentration of the drug is 0.02 mg/ml. Moreover, in vitro biological evaluation demonstrates that the coating scaffolds act as a good matrix for MG63 adhesion, crawl, growth and proliferation, suggesting that the antibacterial delivery system has no cytotoxicity. We expect the drug-delivery system to have a potential application in bone regeneration or defect repair.

Fabrication, characterization and cell cultures on a novel composite chitosan-nano-hydroxyapatite scaffold.

PubMed

Palazzo, B; Gallo, A; Casillo, A; Nitti, P; Ambrosio, L; Piconi, C

2011-01-01

This paper deals with the characterizations made during the development of a nano-HAp loaded chitosan scaffold, obtained by the freeze-drying technique combined with a novel in situ crystal growth method. The nano-composites were characterized by a highly porous and interconnected structure. The XRD patterns and calculated domain sizes of the HAp nano-crystals nucleated on the chitosan scaffolds are very similar to the ones recorded for deproteinated bone apatite. Both osteoblasts (MG63) and mesenchimal cells (hMSC) were showing good proliferation and adhesion onto the scaffolds. The presence of extensive filopodia and excellent spreading in and around the interconnected porous structure, indicated a strong cellular adhesion and growth. Moreover a good hMSC osteogenic differentiation has been verified. The observations related to well-developed structure morphology, physicochemical properties and high cytocompatibility suggest that the obtained chitosan-nHA porous scaffolds are potential candidate materials for bone regeneration.

Sustained release of adipose-derived stem cells by thermosensitive chitosan/gelatin hydrogel for therapeutic angiogenesis.

PubMed

Cheng, Nai-Chen; Lin, Wei-Jhih; Ling, Thai-Yen; Young, Tai-Horng

2017-03-15

developed a thermosensitive chitosan/gelatin hydrogel that not only enhances the viability of the encapsulated ASCs, the gradual degradation of gelatin also result in a more porous architecture, leading to sustained release of ASCs from the hydrogel. ASC-encapsulated hydrogel enhanced in vitro wound healing of fibroblasts and tube formation of endothelial cells. It also promoted in vivo angiogenesis in a chick embryo chorioallantoic membrane assay and a mice wound model. Therefore, chitosan/gelatin hydrogel represents an effective delivery system that allows for controlled release of viable ASCs for therapeutic angiogenesis. Copyright © 2017 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

Development of Biomimetic Hybrid Porous Scaffold of Chitosan/Polyvinyl Alcohol/Carboxymethyl Cellulose by Freeze-Dried and Salt Leached Technique.

PubMed

Kanimozhi, K; Basha, S Khaleel; Kumari, V Sugantha; Kaviyarasu, K

2018-07-01

Freeze drying and salt leaching methods were applied to fabricate Chitosan/Poly(vinyl alcohol)/Carboxymethyl cellulose (CPCMC) biomimetic porous scaffolds for soft tissue engineering. The properties of these scaffolds were investigated and compared to those by freeze drying and salt leaching methods respectively. The salt-leached CS/PVA/CMC scaffolds were easily formed into desired shapes with a uniformly distributed and interconnected pore structure with an average pore size. The mechanical strength of the scaffolds increased with the porosity, and were easily modulated by the addition of carboxymethyl cellulose. The morphology of the porous scaffolds observed using a SEM exhibited good porosity and interconnectivity of pores. MTT assay using L929 fibroblast cells demonstrated that the cell viability of the porous scaffold was good. Scaffolds prepared by salt leached method show larger swelling capacity, and mechanical strength, potent antibacterial activity and more cell viability than freeze dried method. It is found that salt leaching method has distinguished characteristics of simple, efficient, feasible and less economic than freeze dried scaffolds.

3D printing process of oxidized nanocellulose and gelatin scaffold.

PubMed

Xu, Xiaodong; Zhou, Jiping; Jiang, Yani; Zhang, Qi; Shi, Hongcan; Liu, Dongfang

2018-08-01

For tissue engineering applications tissue scaffolds need to have a porous structure to meet the needs of cell proliferation/differentiation, vascularisation and sufficient mechanical strength for the specific tissue. Here we report the results of a study of the 3D printing process for composite materials based on oxidized nanocellulose and gelatin, that was optimised through measuring rheological properties of different batches of materials after different crosslinking times, simulation of the pneumatic extrusion process and 3D scaffolds fabrication with Solidworks Flow Simulation, observation of its porous structure by SEM, measurement of pressure-pull performance, and experiments aimed at finding out the vitro cytotoxicity and cell morphology. The materials printed are highly porous scaffolds with good mechanical properties.

Development of gelatin/carboxymethyl chitosan/nano-hydroxyapatite composite 3D macroporous scaffold for bone tissue engineering applications.

PubMed

Maji, Somnath; Agarwal, Tarun; Das, Joyjyoti; Maiti, Tapas Kumar

2018-06-01

The present study delineates a relatively simpler approach for fabrication of a macroporous three-dimensional scaffold for bone tissue engineering. The novelty of the work is to obtain a scaffold with macroporosity (interconnected networks) through a combined approach of high stirring induced foaming of the gelatin/carboxymethyl chitosan (CMC)/nano-hydroxyapatite (nHAp) matrix followed by freeze drying. The fabricated macroporous (SGC) scaffold had a greater pore size, higher porosity, higher water retention capacity, slow and sustained enzymatic degradation rate along with higher compressive strength compared to that of non-macroporous (NGC, prepared by conventional freeze drying methodology) scaffold. The biological studies revealed the increased percentage of viability, proliferation, and differentiation as well as higher mineralization of differentiated human Wharton's jelly MSC microtissue (wjhMSC-MT) on SGC as compared to NGC scaffold. RT-PCR also showed enhanced expression level of collagen type I, osteocalcin and Runx2 when seeded on SGC. μCT and histological analysis further revealed a penetration of cellular spheroid to a greater depth in SGC scaffold than NGC scaffold. Furthermore, the effect of cryopreservation on microtissue survival on the three-dimensional construct revealed significant higher viability upon revival in macroporous SGC scaffolds. These results together suggest that high stirring based macroporous scaffolds could have a potential application in bone tissue engineering. Copyright © 2018 Elsevier Ltd. All rights reserved.

Challenges for Nerve Repair Using Chitosan-Siloxane Hybrid Porous Scaffolds

PubMed Central

Shirosaki, Yuki; Hayakawa, Satoshi; Osaka, Akiyoshi; Lopes, Maria A.; Santos, José D.; Geuna, Stefano; Mauricio, Ana C.

2014-01-01

The treatment of peripheral nerve injuries remains one of the greatest challenges of neurosurgery, as functional recover is rarely satisfactory in these patients. Recently, biodegradable nerve guides have shown great potential for enhancing nerve regeneration. A major advantage of these nerve guides is that no foreign material remains after the device has fulfilled its task, which spares a second surgical intervention. Recently, we studied peripheral nerve regeneration using chitosan-γ-glycidoxypropyltrimethoxysilane (chitosan-GPTMS) porous hybrid membranes. In our studies, these porous membranes significantly improved nerve fiber regeneration and functional recovery in rat models of axonotmetic and neurotmetic sciatic nerve injuries. In particular, the number of regenerated myelinated nerve fibers and myelin thickness were significantly higher in rat treated with chitosan porous hybrid membranes, whether or not they were used in combination with mesenchymal stem cells isolated from the Wharton's jelly of the umbilical cord. In this review, we describe our findings on the use of chitosan-GPTMS hybrids for nerve regeneration. PMID:25054129

Porous hydroxyapatite/gelatine scaffolds with ice-designed channel-like porosity for biomedical applications.

PubMed

Landi, Elena; Valentini, Federica; Tampieri, Anna

2008-11-01

A cryogenic process, including freeze-casting and drying has been performed to obtain hydroxyapatite (HA) scaffolds (approx. diameter 10 mm, height 20 mm) with completely lamellar morphology due to preferentially aligned channel-like pores. Changing the process parameters that influence the cold transmission efficiency from the bottom to the top of the poured HA slurry, lamellar ice crystals with different thickness grew throughout the samples. After sintering, scaffolds with porosity features nearly resembling the ice ones were obtained. The interconnection of pores and the ability of the scaffolds to be rapidly penetrated by synthetic body fluid has been proven. Biohybrid HA/gel composites were prepared, infiltrating HA lamellar scaffolds (45-55 vol.% of porosity) with a 10wt.% solution of gelatine. Colouring genipine was used to cross-link gelatine and clearly show the distribution of the protein in the composite. The compressive mechanical properties of lamellar scaffolds improved with the addition of gelatine: the strength increased up to 5-6 times, while the elastic modulus and strain approximately doubled. The effectiveness of the cross-linkage has been preliminarily verified following scaffold degradation in synthetic body fluid.

Biomimetic formation of apatite on the surface of porous gelatin/bioactive glass nanocomposite scaffolds

NASA Astrophysics Data System (ADS)

Mozafari, Masoud; Rabiee, Mohammad; Azami, Mahmoud; Maleknia, Saied

2010-12-01

There have been several attempts to combine bioactive glasses (BaGs) with biodegradable polymers to create a scaffold material with excellent biocompatibility, bioactivity, biodegradability and toughness. In the present study, the nanocomposite scaffolds with compositions based on gelatin (Gel) and BaG nanoparticles in the ternary SiO 2-CaO-P 2O 5 system were prepared. In vitro evaluations of the nanocomposite scaffolds were performed, and for investigating their bioactive capacity these scaffolds were soaked in a simulated body fluid (SBF) at different time intervals. The scaffolds showed significant enhancement in bioactivity within few days of immersion in SBF solution. The apatite formation at the surface of the nanocomposite samples confirmed by Fourier transform infrared spectroscopy (FTIR), scanning electron microscopy (SEM), energy dispersive X-ray spectroscopy (EDX) and X-ray powder diffraction (XRD) analyses. In vitro experiments with osteoblast cells indicated an appropriate penetration of the cells into the scaffold's pores, and also the continuous increase in cell aggregation on the bioactive scaffolds with increase in the incubation time demonstrated the ability of the scaffolds to support cell growth. The SEM observations revealed that the prepared scaffolds were porous with three dimensional (3D) and interconnected microstructure, pore size was 200-500 μm and the porosity was 72-86%. The nanocomposite scaffold made from Gel and BaG nanoparticles could be considered as a highly bioactive and potential bone tissue engineering implant.

Sphere-shaped nano-hydroxyapatite/chitosan/gelatin 3D porous scaffolds increase proliferation and osteogenic differentiation of human induced pluripotent stem cells from gingival fibroblasts.

PubMed

Ji, Jun; Tong, Xin; Huang, Xiaofeng; Wang, Tiancong; Lin, Zitong; Cao, Yazhou; Zhang, Junfeng; Dong, Lei; Qin, Haiyan; Hu, Qingang

2015-07-08

Hydroxyapatite (HA) is an important component of human bone and bone tissue engineering scaffolds. A plethora of bone tissue engineering scaffolds have been synthesized so far, including nano-HA/chitosan/gelatin (nHA/CG) scaffolds; and for seeding cells, stem cells, especially induced pluripotent stem cells (iPSCs), have been a promising cell source for bone tissue engineering recently. However, the influence of different HA nano-particle morphologies on the osteogenic differentiation of human iPSCs (hiPSCs) from human gingival fibroblasts (hGFs) is unknown. The purpose of this study was to investigate the osteogenic differentiation of hiPSCs from hGFs seeded on nHA/CG scaffolds with 2 shapes (rod and sphere) of nHA particles. Firstly, hGFs isolated from discarded normal gingival tissues were reprogrammed into hiPSCs. Secondly, hiPSCs were seeded on rod-like nHA/CG (rod-nHA/CG) and sphere-shaped nHA/CG (sphere-nHA/CG) scaffolds respectively and then cell/scaffold complexes were cultured in vitro. Scanning electron microscope, hematoxyline and eosin (HE) staining, Masson's staining, and quantitative real-time polymerase chain reaction techniques were used to examine hiPSC morphology, proliferation, and differentiation on rod-nHA/CG and sphere-nHA/CG scaffolds. Finally, hiPSCs composited with 2 kinds of nHA/CG were transplanted in vivo in a subcutaneous implantation model for 12 weeks; pure scaffolds were also transplanted as a blank control. HE, Masson's, and immunohistochemistry staining were applied to detect new bone regeneration ability. The results showed that sphere-nHA/CG significantly increased hiPSCs from hGF proliferation and osteogenic differentiation in vitro. hiPSCs and sphere-nHA/CG composities generated large bone, whereas hiPSCs and rod-nHA/CG composities produced tiny bone in vivo. Moreover, pure scaffolds without cells almost produced no bone. In conclusion, our work provided a potential innovative bone tissue engineering approach using

Antibacterial and wound healing analysis of gelatin/zeolite scaffolds.

PubMed

Ninan, Neethu; Muthiah, Muthunarayanan; Bt Yahaya, Nur Aliza; Park, In-Kyu; Elain, Anne; Wong, Tin Wui; Thomas, Sabu; Grohens, Yves

2014-03-01

In this article, gelatin/copper activated faujasites (CAF) composite scaffolds were fabricated by lyophilisation technique for promoting partial thickness wound healing. The optimised scaffold with 0.5% (w/w) of CAF, G (0.5%), demonstrated pore size in the range of 10-350 μm. Agar disc diffusion tests verified the antibacterial role of G (0.5%) and further supported that bacterial lysis was due to copper released from the core of CAF embedded in the gelatin matrix. The change in morphology of bacteria as a function of CAF content in gelatin scaffold was studied using SEM analysis. The confocal images revealed the increase in mortality rate of bacteria with increase in concentration of incorporated CAF in gelatin matrix. Proficient oxygen supply to needy cells is a continuing hurdle faced by tissue engineering scaffolds. The dissolved oxygen measurements revealed that CAF embedded in the scaffold were capable of increasing oxygen supply and thereby promote cell proliferation. Also, G (0.5%) exhibited highest cell viability on NIH 3T3 fibroblast cells which was mainly attributed to the highly porous architecture and its ability to enhance oxygen supply to cells. In vivo studies conducted on Sprague Dawley rats revealed the ability of G (0.5%) to promote skin regeneration in 20 days. Thus, the obtained data suggest that G (0.5%) is an ideal candidate for wound healing applications. Crown Copyright © 2013. Published by Elsevier B.V. All rights reserved.

Relevance of fiber integrated gelatin-nanohydroxyapatite composite scaffold for bone tissue regeneration

NASA Astrophysics Data System (ADS)

Halima Shamaz, Bibi; Anitha, A.; Vijayamohan, Manju; Kuttappan, Shruthy; Nair, Shantikumar; Nair, Manitha B.

2015-10-01

Porous nanohydroxyapatite (nanoHA) is a promising bone substitute, but it is brittle, which limits its utility for load bearing applications. To address this issue, herein, biodegradable electrospun microfibrous sheets of poly(L-lactic acid)-(PLLA)-polyvinyl alcohol (PVA) were incorporated into a gelatin-nanoHA matrix which was investigated for its mechanical properties, the physical integration of the fibers with the matrix, cell infiltration, osteogenic differentiation and bone regeneration. The inclusion of sacrificial fibers like PVA along with PLLA and leaching resulted in improved cellular infiltration towards the center of the scaffold. Furthermore, the treatment of PLLA fibers with 1-ethyl-3-(3-dimethylaminopropyl) carbodiimide enhanced their hydrophilicity, ensuring firm anchorage between the fibers and the gelatin-HA matrix. The incorporation of PLLA microfibers within the gelatin-nanoHA matrix reduced the brittleness of the scaffolds, the effect being proportional to the number of layers of fibrous sheets in the matrix. The proliferation and osteogenic differentiation of human adipose-derived mesenchymal stem cells was augmented on the fibrous scaffolds in comparison to those scaffolds devoid of fibers. Finally, the scaffold could promote cell infiltration, together with bone regeneration, upon implantation in a rabbit femoral cortical defect within 4 weeks. The bone regeneration potential was significantly higher when compared to commercially available HA (Surgiwear™). Thus, this biomimetic, porous, 3D composite scaffold could be offered as a promising candidate for bone regeneration in orthopedics.

Biomimetic mineralized hierarchical hybrid scaffolds based on in situ synthesis of nano-hydroxyapatite/chitosan/chondroitin sulfate/hyaluronic acid for bone tissue engineering.

PubMed

Hu, Yimin; Chen, Jingdi; Fan, Tiantang; Zhang, Yujue; Zhao, Yao; Shi, Xuetao; Zhang, Qiqing

2017-09-01

Biomimetic mineralized hybrid scaffolds are widely used as natural bone substitute materials in tissue engineering by mimicking vital characters of extracellular matrix (ECM). However, the fabrication of hybrid scaffolds with suitable mechanical properties and good biocompatibility remains a challenge. To solve the problems mentioned above, biomimetic calcium phosphate mineralized organic-inorganic hybrid scaffold composed of nano hydroxyapatite (nHAP), Chitosan (CS), Chondroitin sulfate (CSA) and hyaluronic acid (HA) with hierarchical micro/nano structures was successfully developed. In this process, an efficient and easy-to-accomplish method combining in situ biomimetic synthesis with freeze-drying technology was applied. The chemical structure of the scaffolds was confirmed by Fourier transform infrared spectroscopy (FTIR) and X-ray diffraction (XRD). Surface morphology of scaffolds was characterized by Scanning electron microscopy (SEM). The nHAP/CS/CSA/HA hybrid scaffolds with a well-distributed pore size showed suitable mechanical strength which is not only due to the addition of the nHAP but also the interaction between the positively charged CS and the negatively charged CSA and HA. Simultaneously, the biocompatibility was evaluated by the MTT cytotoxicity assay, alkaline phosphatase (ALP) activity, Hoechst 33258 fluorescence staining. All those results proved that the scaffolds possess good biocompatibility and the components added have enhanced the proliferation and differentiation of osteoblast. Thus, it can be anticipated that the in situ biomimetic mineralized nHAP/CS/CAS/HA hybrid scaffolds will be promising candidates for bone tissue engineering. Copyright © 2017 Elsevier B.V. All rights reserved.

Production of Composite Scaffold Containing Silk Fibroin, Chitosan, and Gelatin for 3D Cell Culture and Bone Tissue Regeneration.

PubMed

Li, Jianqing; Wang, Qiuke; Gu, Yebo; Zhu, Yu; Chen, Liang; Chen, Yunfeng

2017-11-08

BACKGROUND Bone tissue engineering, a powerful tool to treat bone defects, is highly dependent on use of scaffolds. Both silk fibroin (SF) and chitosan (Cs) are biocompatible and actively studied for reconstruction of tissue engineering. Gelatin (Gel) is also widely applied in the biomedical field due to its low antigenicity and physicochemical stability. MATERIAL AND METHODS In this study, 4 different types of scaffolds were constructed - SF, SF/Cs, SF/Gel, and SF/Cs/Gel - and we compared their physical and chemical properties as well as biological characterization of these scaffolds to determine the most suitable scaffold for use in bone regeneration. First, these scaffolds were produced via chemical cross-linking method and freeze-drying technique. Next, the characterization of internal structure was studied using scanning electron microscopy and the porosity was evaluated by liquid displacement method. Then, we compared physicochemical properties such as water absorption rate and degradation property. Finally, MC3T3-E1 cells were inoculated on the scaffolds to study the biocompatibility and osteogenesis of the three-dimensional (3D) scaffolds in vitro. RESULTS The composite scaffold formed by all 3 components was the best for use in bone regeneration. CONCLUSIONS We conclude that the best scaffold among the 4 studied for MC3T3-E1 cells is our SF/Cs/Gel scaffold, suggesting a new choice for bone regeneration that can be used to treat bone defects or fractures in clinical practice.

A Porous Hydroxyapatite/Gelatin Nanocomposite Scaffold for Bone Tissue Repair: In Vitro and In Vivo Evaluation.

PubMed

Azami, Mahmoud; Tavakol, Shima; Samadikuchaksaraei, Ali; Hashjin, Mehran Solati; Baheiraei, Nafiseh; Kamali, Mehdi; Nourani, Mohammad Reza

2012-01-01

In this study, a nano-structured scaffold was designed for bone repair using hydroxapatite and gelatin as its main components. The scaffold was prepared via layer solvent casting combined with freeze-drying and lamination techniques and characterized by the commonly used bulk techniques. The biocompatibility and osteoconductivity of this scaffold and its capacity to promote bone healing were also evaluated. Osteoblast-like cells were seeded on these scaffolds and their proliferation rate, intracellular alkaline phosphatase (ALP) activity and ability to form mineralized bone nodules were compared with those osteoblasts grown on cell culture plastic surfaces. Also, the scaffolds were implanted in a critical bone defect created on rat calvarium. Engineering analyses show that the scaffold posses a three dimensional interconnected homogenous porous structure with a porosity of about 82% and pore sizes ranging from 300 to 500 μm. Mechanical indices are in the range of spongy bones. The results obtained from biological assessment show that this scaffold does not negatively affect osteoblasts proliferation rate and improves osteoblasts function as shown by increasing the ALP activity and calcium deposition and formation of mineralized bone nodules. In addition, the scaffold promoted healing of critical size calvarial bone defect in rats. It could be concluded that this scaffold fulfills all the main requirements to be considered as a bone substitute.

Treatment of osteomyelitis defects by a vancomycin-loaded gelatin/β-tricalcium phosphate composite scaffold

PubMed Central

Zhou, J.; Zhou, X. G.; Wang, J. W.; Zhou, H.; Dong, J.

2018-01-01

Objective In the present study, we aimed to assess whether gelatin/β-tricalcium phosphate (β-TCP) composite porous scaffolds could be used as a local controlled release system for vancomycin. We also investigated the efficiency of the scaffolds in eliminating infections and repairing osteomyelitis defects in rabbits. Methods The gelatin scaffolds containing differing amounts of of β-TCP (0%, 10%, 30% and 50%) were prepared for controlled release of vancomycin and were labelled G-TCP0, G-TCP1, G-TCP3 and G-TCP5, respectively. The Kirby-Bauer method was used to examine the release profile. Chronic osteomyelitis models of rabbits were established. After thorough debridement, the osteomyelitis defects were implanted with the scaffolds. Radiographs and histological examinations were carried out to investigate the efficiency of eliminating infections and repairing bone defects. Results The prepared gelatin/β-TCP scaffolds exhibited a homogeneously interconnected 3D porous structure. The G-TCP0 scaffold exhibited the longest duration of vancomycin release with a release duration of eight weeks. With the increase of β-TCP contents, the release duration of the β-TCP-containing composite scaffolds was decreased. The complete release of vancomycin from the G-TCP5 scaffold was achieved within three weeks. In the treatment of osteomyelitis defects in rabbits, the G-TCP3 scaffold showed the most efficacious performance in eliminating infections and repairing bone defects. Conclusions The composite scaffolds could achieve local therapeutic drug levels over an extended duration. The G-TCP3 scaffold possessed the optimal porosity, interconnection and controlled release performance. Therefore, this scaffold could potentially be used in the treatment of chronic osteomyelitis defects. Cite this article: J. Zhou, X. G. Zhou, J. W. Wang, H. Zhou, J. Dong. Treatment of osteomyelitis defects by a vancomycin-loaded gelatin/β-tricalcium phosphate composite scaffold. Bone Joint Res

Preparation and characterization of poly (hydroxy butyrate)/chitosan blend scaffolds for tissue engineering applications

PubMed Central

Karbasi, Saeed; Khorasani, Saied Nouri; Ebrahimi, Somayeh; Khalili, Shahla; Fekrat, Farnoosh; Sadeghi, Davoud

2016-01-01

Background: Poly (hydroxy butyrate) (PHB) is a biodegradable and biocompatible polymer with good mechanical properties. This polymer could be a promising material for scaffolds if some features improve. Materials and Methods: In the present work, new PHB/chitosan blend scaffolds were prepared as a three-dimensional substrate in cartilage tissue engineering. Chitosan in different weight percent was added to PHB and solved in trifluoroacetic acid. Statistical Taguchi method was employed in the design of experiments. Results: The Fourier-transform infrared spectroscopy test revealed that the crystallization of PHB in these blends is suppressed with increasing the amount of chitosan. Scanning electron microscopy images showed a thin and rough top layer with a nodular structure, supported with a porous sub-layer in the surface of the scaffolds. In vitro degradation rate of the scaffolds was higher than pure PHB scaffolds. Maximum degradation rate has been seen for the scaffold with 90% wt. NaCl and 40% wt. chitosan. Conclusions: The obtained results suggest that these newly developed PHB/chitosan blend scaffolds may serve as a three-dimensional substrate in cartilage tissue engineering. PMID:28028517

Preparation and characterization of poly (hydroxy butyrate)/chitosan blend scaffolds for tissue engineering applications.

PubMed

Karbasi, Saeed; Khorasani, Saied Nouri; Ebrahimi, Somayeh; Khalili, Shahla; Fekrat, Farnoosh; Sadeghi, Davoud

2016-01-01

Poly (hydroxy butyrate) (PHB) is a biodegradable and biocompatible polymer with good mechanical properties. This polymer could be a promising material for scaffolds if some features improve. In the present work, new PHB/chitosan blend scaffolds were prepared as a three-dimensional substrate in cartilage tissue engineering. Chitosan in different weight percent was added to PHB and solved in trifluoroacetic acid. Statistical Taguchi method was employed in the design of experiments. The Fourier-transform infrared spectroscopy test revealed that the crystallization of PHB in these blends is suppressed with increasing the amount of chitosan. Scanning electron microscopy images showed a thin and rough top layer with a nodular structure, supported with a porous sub-layer in the surface of the scaffolds. In vitro degradation rate of the scaffolds was higher than pure PHB scaffolds. Maximum degradation rate has been seen for the scaffold with 90% wt. NaCl and 40% wt. chitosan. The obtained results suggest that these newly developed PHB/chitosan blend scaffolds may serve as a three-dimensional substrate in cartilage tissue engineering.

Dynamic compression of rabbit adipose-derived stem cells transfected with insulin-like growth factor 1 in chitosan/gelatin scaffolds induces chondrogenesis and matrix biosynthesis.

PubMed

Li, Jianjun; Zhao, Qun; Wang, Enbo; Zhang, Chuanhui; Wang, Guangbin; Yuan, Quan

2012-05-01

Articular cartilage is routinely subjected to mechanical forces and growth factors. Adipose-derived stem cells (ASCs) are multi-potent adult stem cells and capable of chondrogenesis. In the present study, we investigated the comparative and interactive effects of dynamic compression and insulin-like growth factor-I (IGF-I) on the chondrogenesis of rabbit ASCs in chitosan/gelatin scaffolds. Rabbit ASCs with or without a plasmid overexpressing of human IGF-1 were cultured in chitosan/gelatin scaffolds for 2 days, then subjected to cyclic compression with 5% strain and 1 Hz for 4 h per day for seven consecutive days. Dynamic compression induced chondrogenesis of rabbit ASCs by activating calcium signaling pathways and up-regulating the expression of Sox-9. Dynamic compression plus IGF-1 overexpression up-regulated expression of chondrocyte-specific extracellular matrix genes including type II collagen, Sox-9, and aggrecan with no effect on type X collagen expression. Furthermore, dynamic compression and IGF-1 expression promoted cellular proliferation and the deposition of proteoglycan and collagen. Intracellular calcium ion concentration and peak currents of Ca(2+) ion channels were consistent with chondrocytes. The tissue-engineered cartilage from this process had excellent mechanical properties. When applied together, the effects achieved by the two stimuli (dynamic compression and IGF-1) were greater than those achieved by either stimulus alone. Our results suggest that dynamic compression combined with IGF-1 overexpression might benefit articular cartilage tissue engineering in cartilage regeneration. Copyright © 2011 Wiley Periodicals, Inc.

Fabrication of chemically cross-linked porous gelatin matrices.

PubMed

Bozzini, Sabrina; Petrini, Paola; Altomare, Lina; Tanzi, Maria Cristina

2009-01-01

The aim of this study was to chemically cross-link gelatin, by reacting its free amino groups with an aliphatic diisocyanate. To produce hydrogels with controllable properties, the number of reacting amino groups was carefully determined. Porosity was introduced into the gelatin-based hydrogels through the lyophilization process. Porous and non-porous matrices were characterized with respect to their chemical structure, morphology, water uptake and mechanical properties. The physical, chemical and mechanical properties of the porous matrices are related to the extent of their cross-linking, showing that they can be controlled by varying the reaction parameters. Water uptake values (24 hours) vary between 160% and 200% as the degree of cross-linking increases. The flexibility of the samples also decreases by changing the extent of cross-linking. Young's modulus shows values between 0.188 KPa, for the highest degree, and 0.142 KPa for the lowest degree. The matrices are potential candidates for use as tissue-engineering scaffolds by modulating their physical chemical properties according to the specific application.

Surface biofunctionalization of three-dimensional porous poly(lactic acid) scaffold using chitosan/OGP coating for bone tissue engineering.

PubMed

Zeng, Sen; Ye, Jianhua; Cui, Zhixiang; Si, Junhui; Wang, Qianting; Wang, Xiaofeng; Peng, Kaiping; Chen, Wenzhe

2017-08-01

As one of the stimulators on bone formation, osteogenic growth peptide (OGP) improves both proliferation and differentiation of the bone cells in vitro and in vivo. The aim of this work was the preparation of three dimensional porous poly(lactic acid) (PLA) scaffold with high porosity from PLA-dioxane-water ternary system with the use of vacuum-assisted solvent casting, phase separation, solvent extraction and particle leaching methods. Then, by surface coating of PLA scaffold with chitosan (CS)/OGP solution, biofunctionalization of PLA scaffold had been completed for application in bone regeneration. The effects of frozen temperature (-20, -50, -80°C) and PLA solution concentration (10, 12, 14wt%) on the microstructure, water absorption, porosity, hydrophilicity, mechanical properties, and biocompatibility of PLA and CS/OGP/PLA scaffold were investigated. Results showed that both PLA and CS/OGP/PLA scaffolds have an interconnected network structure and a porosity of up to 96.1% and 91.5%, respectively. The CS/OGP/PLA scaffold exhibited better hydrophilicity and mechanical properties than that of uncoated PLA scaffold. Moreover, the results of cell culture test showed that CS/OGP coating could stimulate the proliferation and growth of osteoblast cells on CS/OGP/PLA scaffold. These finding suggested that the surface biofunctionalization by CS/OGP coating layer could be an effective method on enhancing cell adhesion to synthetic polymer-based scaffolds in tissue engineering application and the developed porous CS/OGP/PLA scaffold should be considered as alternative biomaterials for bone regeneration. Copyright © 2017 Elsevier B.V. All rights reserved.

Development of various composition multicomponent chitosan/fish collagen/glycerin 3D porous scaffolds: Effect on morphology, mechanical strength, biostability and cytocompatibility.

PubMed

Ullah, Saleem; Zainol, Ismail; Chowdhury, Shiplu Roy; Fauzi, M B

2018-05-01

The various composition multicomponent chitosan/fish collagen/glycerin 3D porous scaffolds were developed and investigated the effect of various composition chitosan/fish collagen/glycerin on scaffolds morphology, mechanical strength, biostability and cytocompatibility. The scaffolds were fabricated via freeze-drying technique. The effects of various compositions consisting in 3D scaffolds were investigated via FT-IR analysis, porosity, swelling and mechanical tests, and effect on the morphology of scaffolds investigated microscopically. The biostability and cytocompatibility tests were used to explore the ability of scaffolds to use for tissue engineering application. The average pore sizes of scaffolds were in range of 100.73±27.62-116.01±52.06, porosity 71.72±3.46-91.17±2.42%, tensile modulus in dry environment 1.47±0.08-0.17±0.03MPa, tensile modulus in wet environment 0.32±0.03-0.14±0.04MPa and biodegradation rate (at day 30) 60.38±0.70-83.48±0.28%. In vitro culture of human fibroblasts and keratinocytes showed that the various composition multicomponent 3D scaffolds were good cytocompatibility however, the scaffolds contained high amount of fish collagen excellently facilitated cell proliferation and adhesion. It was found that the high amount fish collagen and glycerin scaffolds have high porosity, enough mechanical strength and biostability, and excellent cytocompatibility. Copyright © 2018 Elsevier B.V. All rights reserved.

Fabrication of a three-dimensional β-tricalcium-phosphate/gelatin containing chitosan-based nanoparticles for sustained release of bone morphogenetic protein-2: Implication for bone tissue engineering.

PubMed

Bastami, Farshid; Paknejad, Zahrasadat; Jafari, Maissa; Salehi, Majid; Rezai Rad, Maryam; Khojasteh, Arash

2017-03-01

Fabrication of an ideal scaffold having proper composition, physical structure and able to have sustained release of growth factors still is challenging for bone tissue engineering. Current study aimed to design an appropriate three-dimensional (3-D) scaffold with suitable physical characteristics, including proper compressive strength, degradation rate, porosity, and able to sustained release of bone morphogenetic protein-2 (BMP2), for bone tissue engineering. A highly porous 3-D β-tricalcium phosphate (β-TCP) scaffolds, inside of which two perpendicular canals were created, was fabricated using foam-casting technique. Then, scaffolds were coated with gelatin layer. Next, BMP2-loaded chitosan (CS) nanoparticles were dispersed into collagen hydrogel and filled into the scaffold canals. Physical characteristics of fabricated constructs were evaluated. Moreover, the capability of given construct for bone regeneration has been evaluated in vitro in interaction with human buccal fat pad-derived stem cells (hBFPSCs). The results showed that gelatin-coated TCP scaffold with rhBMP2 delivery system not only could act as a mechanically and biologically compatible framework, but also act as an osteoinductive graft by sustained delivering of rhBMP2 in a therapeutic window for differentiation of hBFPSCs towards the osteoblast lineage. The proposed scaffold model can be suggested for delivering of cells and other growth factors such as vascular endothelial growth factor (VEGF), alone or in combination, for future investigations. Copyright © 2016 Elsevier B.V. All rights reserved.

Novel Biodegradable Porous Scaffold Applied to Skin Regeneration

PubMed Central

Wang, Hui-Min; Chou, Yi-Ting; Wen, Zhi-Hong; Wang, Zhao-Ren; Chen, Chun-Hong; Ho, Mei-Ling

2013-01-01

Skin wound healing is an important lifesaving issue for massive lesions. A novel porous scaffold with collagen, hyaluronic acid and gelatin was developed for skin wound repair. The swelling ratio of this developed scaffold was assayed by water absorption capacity and showed a value of over 20 g water/g dried scaffold. The scaffold was then degraded in time- and dose-dependent manners by three enzymes: lysozyme, hyaluronidase and collagenase I. The average pore diameter of the scaffold was 132.5±8.4 µm measured from SEM images. With human skin cells growing for 7 days, the SEM images showed surface fractures on the scaffold due to enzymatic digestion, indicating the biodegradable properties of this scaffold. To simulate skin distribution, the human epidermal keratinocytes, melanocytes and dermal fibroblasts were seeded on the porous scaffold and the cross-section immunofluorescent staining demonstrated normal human skin layer distributions. The collagen amount was also quantified after skin cells seeding and presented an amount 50% higher than those seeded on culture wells. The in vivo histological results showed that the scaffold ameliorated wound healing, including decreasing neutrophil infiltrates and thickening newly generated skin compared to the group without treatments. PMID:23762223

Investigation of different cross-linking approaches on 3D gelatin scaffolds for tissue engineering application: A comparative analysis.

PubMed

Shankar, K Gopal; Gostynska, Natalia; Montesi, Monica; Panseri, Silvia; Sprio, Simone; Kon, Elizaveta; Marcacci, Maurilio; Tampieri, Anna; Sandri, Monica

2017-02-01

The present study aims to investigate the physical-chemical and biological features exhibited by porous scaffolds for regeneration of cartilaginous tissues obtained through stabilization of 3D gelatin hydrogels by physical (DHT), chemical (BDDGE) and natural (Genipin) cross-linking approaches. The study aimed at comparatively assessing the porous microstructure and the long-term resistance of the scaffolds upon degradation in wet physiological conditions (37°C, pH=7.4). The degree of cross-linking increases as function of incorporation of cross-linkers which was maximum up to 73% for BDDGE. The infrared spectroscopy and thermal analysis confirmed the gelatin structure was preserved during the cross-linking treatments. Mechanical properties of the scaffolds were analysed by static and dynamic compression test, which showed different viscoelastic behaviour upon various cross-linking strategies. The biological performance of the scaffolds investigated using human chondrocytes showed good cell adhesion, viability and proliferation, as well as extensive 3D scaffold colonization. Besides, the analysis of gene expression related to the formation of new chondral tissue reported increasing ability with time in the formation of new extra-cellular matrix. In conclusion, out of three different cross-linking methods, the gelatin scaffolds subjected to dehydrothermal treatment (DHT) represented to be the most favourable 3D scaffold for cartilage regeneration. Copyright © 2016 Elsevier B.V. All rights reserved.

The enhancement of differentiating adipose derived mesenchymal stem cells toward hepatocyte like cells using gelatin cryogel scaffold.

PubMed

Ghaderi Gandomani, Maryam; Sahebghadam Lotfi, Abbas; Kordi Tamandani, Dormohammad; Arjmand, Sareh; Alizadeh, Shaban

2017-09-30

Liver tissue engineering creates a promising methodology for developing functional tissue to restore or improve the function of lost or damaged liver by using appropriate cells and biologically compatible scaffolds. The present paper aims to study the hepatogenic potential of human adipose derived mesenchymal stem cells (hADSCs) on a 3D gelatin scaffold in vitro. For this purpose, mesenchymal stem cells were isolated from human adipose tissue and characterized by flowcytometry analysis and mesodermal lineage differentiation capacity. Then, porous cryogel scaffolds were fabricated by cryogelating the gelatin using glutaraldehyde as the crosslinking agent. The structure of the scaffolds as well as the adhesion and proliferation of the cells were then determined by Scanning Electron Microscopy (SEM) analysis and MTT assay, respectively. The efficiency of hepatic differentiation of hADSCs on 2D and 3D culture systems has been assessed by means of morphological, cytological, molecular and biochemical approaches. Based on the results of flowcytometry, the isolated cells were positive for hMSC specific markers and negative for hematopoietic markers. Further, the multipotency of these cells was confirmed by adipogenic and osteogenic differentiation and the highly porous structure of scaffolds was characterized by SEM images. Biocompatibility was observed in the fabricated gelatin scaffolds and the adhesion and proliferation of hADSCs were promoted without any cytotoxicity effects. In addition, compared to 2D TCPS, the fabricated scaffolds provided more appropriate microenvironment resulting in promoting the differentiation of hADSCs toward hepatocyte-like cells with higher expression of hepatocyte-specific markers and appropriate functional characteristics such as increased levels of urea biosynthesis and glycogen storage. Finally, the created 3D gelatin scaffold could provide an appropriate matrix for hepatogenic differentiation of hADSCs, which could be considered for

Characterization of Silk Fibroin/Chitosan 3D Porous Scaffold and In Vitro Cytology.

PubMed

Zeng, Shuguang; Liu, Lei; Shi, Yong; Qiu, Junqi; Fang, Wei; Rong, Mingdeng; Guo, Zehong; Gao, Wenfeng

2015-01-01

Bone tissue engineering is a powerful tool to treat bone defects caused by trauma, infection, tumors and other factors. Both silk fibroin (SF) and chitosan (CS) are non-toxic and have good biocompatibility, but are poor biological scaffolds when used alone. In this study, the microscopic structure and related properties of SF/CS composite scaffolds with different component ratios were examined. The scaffold material most suitable for osteoblast growth was determined, and these results offer an experimental basis for the future reconstruction of bone defects. First, via freeze-drying and chemical crosslinking methods, SF/CS composites with different component ratios were prepared and their structure was characterized. Changes in the internal structure of the SF and CS mixture were observed, confirming that the mutual modification between the two components was complete and stable. The internal structure of the composite material was porous and three-dimensional with a porosity above 90%. We next studied the pore size, swelling ratio, water absorption ratio, degradation and in vitro cell proliferation. For the 40% SF-60% CS group, the pore size of the scaffold was suitable for the growth of osteoblasts, and the rate of degradation was steady. This favors the early adhesion, growth and proliferation of MG-63 cells. In addition to good biocompatibility and satisfactory cell affinity, this material promotes the secretion of extracellular matrix materials by osteoblasts. Thus, 40% SF-60% CS is a good material for bone tissue engineering.

Reinforced chitosan-based heart valve scaffold and utility of bone marrow-derived mesenchymal stem cells for cardiovascular tissue engineering

NASA Astrophysics Data System (ADS)

Albanna, Mohammad Zaki

Recent research has demonstrated a strong correlation between the differentiation profile of mesenchymal stem cells (MSCs) and scaffold stiffness. Chitosan is being widely studied for tissue engineering applications due to its biocompatibility and biodegradability. However, its use in load-bearing applications is limited due to moderate to low mechanical properties. In this study, we investigated the effectiveness of a fiber reinforcement method for enhancing the mechanical properties of chitosan scaffolds. Chitosan fibers were fabricated using a solution extrusion and neutralization method and incorporated into porous chitosan scaffolds. The effects of different fiber/scaffold mass ratios, fiber mechanical properties and fiber lengths on scaffold mechanical properties were studied. The results showed that incorporating fibers improved scaffold strength and stiffness in proportion to the fiber/scaffold mass ratio. A fiber-reinforced heart valve leaflet scaffold achieved strength values comparable to the radial values of human pulmonary and aortic valves. Additionally, the effects of shorter fibers (2 mm) were found to be up to 3-fold greater than longer fibers (10 mm). Despite this reduction in fiber mechanical properties caused by heparin crosslinking, the heparin-modified fibers still improved the mechanical properties of the reinforced scaffolds, but to a lesser extent than the unmodified fibers. The results demonstrate that chitosan fiber-reinforcement can be used to generate tissue-matching mechanical properties in porous chitosan scaffolds and that fiber length and mechanical properties are important parameters in defining the degree of mechanical improvement. We further studied various chemical and physical treatments to improve the mechanical properties of chitosan fibers. With combination of chemical and physical treatments, fiber stiffness improved 40fold compared to unmodified fibers. We also isolated ovine bone marrow-derived MSCs and evaluated their

Gelatine/PLLA sponge-like scaffolds: morphological and biological characterization.

PubMed

Lazzeri, Luigi; Cascone, Maria Grazia; Danti, Serena; Serino, Lorenzo Pio; Moscato, Stefania; Bernardini, Nunzia

2006-12-01

Biodegradable synthetic polymers such as poly(lactic acid) are widely used to prepare scaffolds for cell transplantation and tissue growth, using different techniques set up for the purpose. However the poor hydrophilicity of these polymers represents the main limitation to their use as scaffolds because it causes a low affinity for the cells. An effective way to solve this problem could be represented by the addition of biopolymers that are in general highly hydrophilic. The present work concerns porous biodegradable sponge-like systems based on poly(L-lactic acid) and gelatine. Morphology and porosity characteristics of the sponges were studied by scanning electron microscopy and mercury intrusion porosimetry respectively. Blood compatibility was investigated by bovine plasma fibrinogen adsorption test and platelet adhesion test. The cell culture method was used in order to evaluate the ability of the matrices to work as scaffolds for tissue regeneration. The obtained results indicate that the sponges have interesting porous characteristics, good blood compatibility and above all good ability to support cell adhesion and growth. In fact viable and metabolically active animal cells were found inside the sponges after 8 weeks in culture. On this basis the systems produced seem to be good candidates as scaffolds for tissue regeneration.

Gelatine/PLLA sponge-like scaffolds: morphological and biological characterization.

PubMed

Lazzeri, Luigi; Cascone, Maria Grazia; Danti, Serena; Serino, Lorenzo Pio; Moscato, Stefania; Bernardini, Nunzia

2007-07-01

Biodegradable synthetic polymers such as poly(lactic acid) (PLA) are widely used to prepare scaffolds for cell transplantation and tissue growth, using different techniques set up for the purpose. However the poor hydrophilicity of these polymers represents the main limitation to their use as scaffolds because it causes a low affinity for the cells. An effective way to solve this problem could be represented by the addition of biopolymers that are in general highly hydrophilic. The present work concerns porous biodegradable sponge-like systems based on poly(L-lactic acid) (PLLA) and gelatine. Morphology and porosity characteristics of the sponges were studied by scanning electron microscopy and mercury intrusion porosimetry respectively. Blood compatibility was investigated by bovine plasma fibrinogen (BPF) adsorption test and platelet adhesion test (PAT). The cell culture method was used in order to evaluate the ability of the matrices to work as scaffolds for tissue regeneration. The obtained results indicate that the sponges have interesting porous characteristics, good blood compatibility and above all good ability to support cell adhesion and growth. In fact viable and metabolically active animal cells were found inside the sponges after 8 weeks in culture. On this basis the systems produced seem to be good candidates as scaffolds for tissue regeneration.

Silk scaffolds connected with different naturally occurring biomaterials for prostate cancer cell cultivation in 3D.

PubMed

Bäcker, Anne; Erhardt, Olga; Wietbrock, Lukas; Schel, Natalia; Göppert, Bettina; Dirschka, Marian; Abaffy, Paul; Sollich, Thomas; Cecilia, Angelica; Gruhl, Friederike J

2017-02-01

In the present work, different biopolymer blend scaffolds based on the silk protein fibroin from Bombyx mori (BM) were prepared via freeze-drying method. The chemical, structural, and mechanical properties of the three dimensional (3D) porous silk fibroin (SF) composite scaffolds of gelatin, collagen, and chitosan as well as SF from Antheraea pernyi (AP) and the recombinant spider silk protein spidroin (SSP1) have been systematically investigated, followed by cell culture experiments with epithelial prostate cancer cells (LNCaP) up to 14 days. Compared to the pure SF scaffold of BM, the blend scaffolds differ in porous morphology, elasticity, swelling behavior, and biochemical composition. The new composite scaffold with SSP1 showed an increased swelling degree and soft tissue like elastic properties. Whereas, in vitro cultivation of LNCaP cells demonstrated an increased growth behavior and spheroid formation within chitosan blended scaffolds based on its remarkable porosity, which supports nutrient supply matrix. Results of this study suggest that silk fibroin matrices are sufficient and certain SF composite scaffolds even improve 3D cell cultivation for prostate cancer research compared to matrices based on pure biomaterials or synthetic polymers. © 2016 Wiley Periodicals, Inc.

Multilayered Magnetic Gelatin Membrane Scaffolds

PubMed Central

Samal, Sangram K.; Goranov, Vitaly; Dash, Mamoni; Russo, Alessandro; Shelyakova, Tatiana; Graziosi, Patrizio; Lungaro, Lisa; Riminucci, Alberto; Uhlarz, Marc; Bañobre-López, Manuel; Rivas, Jose; Herrmannsdörfer, Thomas; Rajadas, Jayakumar; De Smedt, Stefaan; Braeckmans, Kevin; Kaplan, David L.; Dediu, V. Alek

2016-01-01

A versatile approach for the design and fabrication of multilayer magnetic scaffolds with tunable magnetic gradients is described. Multilayer magnetic gelatin membrane scaffolds with intrinsic magnetic gradients were designed to encapsulate magnetized bioagents under an externally applied magnetic field for use in magnetic-field-assisted tissue engineering. The temperature of the individual membranes increased up to 43.7 °C under an applied oscillating magnetic field for 70 s by magnetic hyperthermia, enabling the possibility of inducing a thermal gradient inside the final 3D multilayer magnetic scaffolds. On the basis of finite element method simulations, magnetic gelatin membranes with different concentrations of magnetic nanoparticles were assembled into 3D multilayered scaffolds. A magnetic-gradient-controlled distribution of magnetically labeled stem cells was demonstrated in vitro. This magnetic biomaterial–magnetic cell strategy can be expanded to a number of different magnetic biomaterials for various tissue engineering applications. PMID:26451743

Multilayered Magnetic Gelatin Membrane Scaffolds.

PubMed

Samal, Sangram K; Goranov, Vitaly; Dash, Mamoni; Russo, Alessandro; Shelyakova, Tatiana; Graziosi, Patrizio; Lungaro, Lisa; Riminucci, Alberto; Uhlarz, Marc; Bañobre-López, Manuel; Rivas, Jose; Herrmannsdörfer, Thomas; Rajadas, Jayakumar; De Smedt, Stefaan; Braeckmans, Kevin; Kaplan, David L; Dediu, V Alek

2015-10-21

A versatile approach for the design and fabrication of multilayer magnetic scaffolds with tunable magnetic gradients is described. Multilayer magnetic gelatin membrane scaffolds with intrinsic magnetic gradients were designed to encapsulate magnetized bioagents under an externally applied magnetic field for use in magnetic-field-assisted tissue engineering. The temperature of the individual membranes increased up to 43.7 °C under an applied oscillating magnetic field for 70 s by magnetic hyperthermia, enabling the possibility of inducing a thermal gradient inside the final 3D multilayer magnetic scaffolds. On the basis of finite element method simulations, magnetic gelatin membranes with different concentrations of magnetic nanoparticles were assembled into 3D multilayered scaffolds. A magnetic-gradient-controlled distribution of magnetically labeled stem cells was demonstrated in vitro. This magnetic biomaterial-magnetic cell strategy can be expanded to a number of different magnetic biomaterials for various tissue engineering applications.

Porous Nanocomposite Comprising Ultralong Hydroxyapatite Nanowires Decorated with Zinc-Containing Nanoparticles and Chitosan: Synthesis and Application in Bone Defect Repair.

PubMed

Sun, Tuan-Wei; Yu, Wei-Lin; Zhu, Ying-Jie; Chen, Feng; Zhang, Yong-Gang; Jiang, Ying-Ying; He, Yao-Hua

2018-06-21

Hydroxyapatite nanowires exhibit a great potential in biomedical applications owing to their high specific surface area, high flexibility, excellent mechanical properties, and similarity to mineralized collagen fibrils of natural bone. In this work, zinc-containing nanoparticle-decorated ultralong hydroxyapatite nanowires (Zn-UHANWs) with a hierarchical nanostructure have been synthesized by a one-step solvothermal method. The highly flexible Zn-UHANWs exhibit a hierarchical rough surface and enhanced specific surface area as compared with ultralong hydroxyapatite nanowires (UHANWs). To evaluate the potential application of Zn-UHANWs in bone regeneration, the biomimetic Zn-UHANWs/chitosan (CS) (Zn-UHANWs/CS) composite porous scaffold with 80 wt % Zn-UHANWs was prepared by incorporating Zn-UHANWs into the chitosan matrix by the freeze-drying process. The as-prepared Zn-UHANWs/CS composite porous scaffold exhibits enhanced mechanical properties, highly porous structure, and excellent water retention capacity. In addition, the Zn-UHANWs/CS porous scaffold has a good biodegradability with the sustainable release of Zn, Ca, and P elements in aqueous solution. More importantly, the Zn-UHANWs/CS porous scaffold can promote the osteogenic differentiation of rat bone marrow derived mesenchymal stem cells and facilitate in vivo bone regeneration as compared with the pure CS porous scaffold or UHANWs/CS porous scaffold. Thus, both the Zn-UHANWs and Zn-UHANWs/CS porous scaffold developed in this work are promising for application in bone defect repair. © 2018 Wiley-VCH Verlag GmbH & Co. KGaA, Weinheim.

Chitosan-chitin nanocrystal composite scaffolds for tissue engineering.

PubMed

Liu, Mingxian; Zheng, Huanjun; Chen, Juan; Li, Shuangli; Huang, Jianfang; Zhou, Changren

2016-11-05

Chitin nanocrystals (CNCs) with length and width of 300 and 20nm were uniformly dispersed in chitosan (CS) solution. The CS/CNCs composite scaffolds prepared utilizing a dispersion-based freeze dry approach exhibit significant enhancement in compressive strength and modulus compared with pure CS scaffold both in dry and wet state. A well-interconnected porous structure with size in the range of 100-200μm and over 80% porosity are found in the composite scaffolds. The crystal structure of CNCs is retained in the composite scaffolds. The incorporation of CNCs leads to increase in the scaffold density and decrease in the water swelling ratio. Moreover, the composite scaffolds are successfully applied as scaffolds for MC3T3-E1 osteoblast cells, showing their excellent biocompatibility and low cytotoxicity. The results of fluorescent micrographs images reveal that CNCs can markedly promote the cell adhesion and proliferation of the osteoblast on CS. The biocompatible composite scaffolds with enhanced mechanical properties have potential application in bone tissue engineering. Copyright © 2016 Elsevier Ltd. All rights reserved.

Synthesis and characterization of chitosan-alginate scaffolds for seeding human umbilical cord derived mesenchymal stem cells.

PubMed

Kumbhar, Sneha G; Pawar, S H

2016-01-01

Chitosan and alginate are two natural and accessible polymers that are known to be biocompatible, biodegradable and possesses good antimicrobial activity. When combined, they exhibit desirable characteristics and can be created into a scaffold for cell culture. In this study interaction of chitosan-alginate scaffolds with mesenchymal stem cells are studied. Mesenchymal stem cells were derived from human umbilical cord tissues, characterized by flow cytometry and other growth parameters studied as well. Proliferation and viability of cultured cells were studied by MTT Assay and Trypan Blue dye exclusion assay. Besides chitosan-alginate scaffold was prepared by freeze-drying method and characterized by FTIR, SEM and Rheological properties. The obtained 3D porous structure allowed very efficient seeding of hUMSCs that are able to inhabit the whole volume of the scaffold, showing good adhesion and proliferation. These materials showed desirable rheological properties for facile injection as tissue scaffolds. The results of this study demonstrated that chitosan-alginate scaffold may be promising biomaterial in the field of tissue engineering, which is currently under a great deal of examination for the development and/or restoration of tissue and organs. It combines the stem cell therapy and biomaterials.

Chitosan porous 3D scaffolds embedded with resolvin D1 to improve in vivo bone healing.

PubMed

Vasconcelos, Daniela P; Costa, Madalena; Neves, Nuno; Teixeira, José H; Vasconcelos, Daniel M; Santos, Susana G; Águas, Artur P; Barbosa, Mário A; Barbosa, Judite N

2018-06-01

The aim of this study was to investigate the effect chitosan (Ch) porous 3D scaffolds embedded with resolvin D1 (RvD1), an endogenous pro-resolving lipid mediator, on bone tissue healing. These scaffolds previous developed by us have demonstrated to have immunomodulatory properties namely in the modulation of the macrophage inflammatory phenotypic profile in an in vivo model of inflammation. Herein, results obtained in an in vivo rat femoral defect model demonstrated that two months after Ch + RvD1 scaffolds implantation, an increase in new bone formation, in bone trabecular thickness, and in collagen type I and Coll I/Coll III ratio were observed. These results suggest that Ch scaffolds embedded with RvD1 were able to lead to the formation of new bone with improvement of trabecular thickness. This study shows that the presence of RvD1 in the acute phase of the inflammatory response to the implanted biomaterial had a positive role in the subsequent bone tissue repair, thus demonstrating the importance of innovative approaches for the control of immune responses to biomedical implants in the design of advanced strategies for regenerative medicine. © 2018 Wiley Periodicals, Inc. J Biomed Mater Res Part A: 106A: 1626-1633, 2018. © 2018 Wiley Periodicals, Inc.

In vitro evaluation of chitosan/poly(lactic acid-glycolic acid) sintered microsphere scaffolds for bone tissue engineering.

PubMed

Jiang, Tao; Abdel-Fattah, Wafa I; Laurencin, Cato T

2006-10-01

A three-dimensional (3-D) scaffold is one of the major components in many tissue engineering approaches. We developed novel 3-D chitosan/poly(lactic acid-glycolic acid) (PLAGA) composite porous scaffolds by sintering together composite chitosan/PLAGA microspheres for bone tissue engineering applications. Pore sizes, pore volume, and mechanical properties of the scaffolds can be manipulated by controlling fabrication parameters, including sintering temperature and sintering time. The sintered microsphere scaffolds had a total pore volume between 28% and 37% with median pore size in the range 170-200microm. The compressive modulus and compressive strength of the scaffolds are in the range of trabecular bone making them suitable as scaffolds for load-bearing bone tissue engineering. In addition, MC3T3-E1 osteoblast-like cells proliferated well on the composite scaffolds as compared to PLAGA scaffolds. It was also shown that the presence of chitosan on microsphere surfaces increased the alkaline phosphatase activity of the cells cultured on the composite scaffolds and up-regulated gene expression of alkaline phosphatase, osteopontin, and bone sialoprotein.

Optimization and characterization of gelatin and chitosan extracted from fish and shrimp waste

NASA Astrophysics Data System (ADS)

Ait Boulahsen, M.; Chairi, H.; Laglaoui, A.; Arakrak, A.; Zantar, S.; Bakkali, M.; Hassani, M.

2018-05-01

Fish and seafood processing industries generate large quantities of waste which are at the origin of several environmental, economic and social problems. However fish waste could contain high value-added substances such as biopolymers. This work focuses on optimizing the gelatin and chitosan extraction from tilapia fish skins and shrimp shells respectively. The gelatin extraction process was optimized using alkali acid treatment prior to thermal hydrolysis. Three different acids were tested at different concentrations. Chitosan was obtained after acid demineralization followed by simultaneous hydrothermal deproteinization and deacetylation by an alkali treatment with different concentrations of HCl and NaOH. The extracted gelatin and chitosan with the highest yield were characterized by determining their main physicochemical properties (Degree of deacetylation, viscosity, pH, moisture and ash content). Results show a significant influence of the acid type and concentration on the extraction yield of gelatin and chitosan, with an average yield of 12.24% and 3.85% respectively. Furthermore, the obtained physicochemical properties of both extracted gelatin and chitosan were within the recommended standard values of the commercial ones used in the industry.

Effects of flow configuration on bone tissue engineering using human mesenchymal stem cells in 3D chitosan composite scaffolds.

PubMed

Sellgren, Katelyn L; Ma, Teng

2015-08-01

Perfusion bioreactor plays important role in supporting 3D bone construct development. Scaffolds of chitosan composites have been studied to support bone tissue regeneration from osteogenic progenitor cells including human mesenchymal stem cells (hMSC). In this study, porous scaffolds of hydroxyapatite (H), chitosan (C), and gelatin (G) were fabricated by phase-separation and press-fitted in the perfusion bioreactor system where media flow is configured either parallel or transverse with respect to the scaffolds to investigate the impact of flow configuration on hMSC proliferation and osteogenic differentiation. The in vitro results showed that the interstitial flow in the transverse flow (TF) constructs reduced cell growth during the first week of culture but improved spatial cell distribution and early onset of osteogenic differentiation measured by alkaline phosphatase and expression of osteogenic genes. After 14 days of bioreactor culture, the TF constructs have comparable cell number but higher expression of bone markers genes and proteins compared to the parallel flow constructs. To evaluate ectopic bone formation, the HCG constructs seeded with hMSCs pre-cultured under two flow configurations for 7 days were implanted in CD-1 nude mice. While Masson's Trichrom staining revealed bone formation in both constructs, the TF constructs have improved spatial cell and osteoid distribution throughout the 2.0 mm constructs. The results highlight the divergent effects of media flow over the course of construct development and suggest that the flow configuration is an important parameter regulating the cellular events leading to bone construct formation in the HCG scaffolds. © 2014 Wiley Periodicals, Inc.

Preparation and characterization of gelatin/chitosan/carbodiimide films

USDA-ARS?s Scientific Manuscript database

In prior studies, we examined the effects of 1-ethyl-3-(3-dimethylaminopropyl) carbodiimide (EDC) and water-dispersible polycarbodiimides (pCDIs) on the properties of gels produced from gelatin and a gelatin/chitosan blend that may be suitable for a role in leather processing. Those studies showed m...

Fabrication and characterization of hydrothermal cross-linked chitosan porous scaffolds for cartilage tissue engineering applications.

PubMed

Shamekhi, Mohammad Amin; Rabiee, Ahmad; Mirzadeh, Hamid; Mahdavi, Hamid; Mohebbi-Kalhori, Davod; Baghaban Eslaminejad, Mohamadreza

2017-11-01

The use of various chemical cross-linking agents for the improvement of scaffolds physical and mechanical properties is a common practical method, which is limited by cytotoxicity effects. Due to exerting contract type forces, chondrocytes are known to implement shrinkage on the tissue engineered constructs, which can be avoided by the scaffold cross-linking. In the this research, chitosan scaffolds are cross-linked with hydrothermal treatment with autoclave sterilization time of 0, 10, 20 and 30min, to avoid the application of the traditional chemical toxic materials. The optimization studies with gel content and crosslink density measurements indicate that for 20min sterilization time, the gel content approaches to ~80%. The scaffolds are fully characterized by the conventional techniques such as SEM, porosity and permeability, XRD, compression, thermal analysis and dynamic mechanical thermal analysis (DMTA). FT-IR studies shows that autoclave inter-chain cross-linking reduces the amine group absorption at 1560cm -1 and increase the absorption of N-acetylated groups at 1629cm -1 . It is anticipated, that this observation evidenced by chitosan scaffold browning upon autoclave cross-linking is an indication of the familiar maillard reaction between amine moieties and carbonyl groups. The biodegradation rate analysis shows that chitosan scaffolds with lower concentrations, possess suitable degradation rate for cartilage tissue engineering applications. In addition, cytotoxicity analysis shows that fabricated scaffolds are biocompatible. The human articular chondrocytes seeding into 3D cross-linked scaffolds shows a higher viability and proliferation in comparison with the uncross-linked samples and 2D controls. Investigation of cell morphology on the scaffolds by SEM, shows a more spherical morphology of chondrocytes on the cross-linked scaffolds for 21days of in vitro culture. Copyright © 2017. Published by Elsevier B.V.

Pectin-chitosan-PVA nanofibrous scaffold made by electrospinning and its potential use as a skin tissue scaffold.

PubMed

Lin, Hsin-Yi; Chen, Hsin-Hung; Chang, Shih-Hsin; Ni, Tsung-Sheng

2013-01-01

Scaffolds made of chitosan nanofibers are often too mechanically weak for their application and often their manufacturing processes involve the use of harmful and flammable organic solvents. In the attempt to improve the mechanical properties of nanofibrous scaffolds made of chitosan without the use of harmful chemicals, pectin, an anionic polymer was blended with chitosan, a cationic polymer, to form a polyelectrolyte complex and electrospun into nanofibers for the first time. The electrospun chitosan-pectin scaffolds, when compared to electrospun chitosan scaffolds, had a 58% larger diameter, a 21% higher Young's modulus, a 162% larger strain at break, and a 104% higher ultimate tensile strength. Compared to the chitosan scaffolds, the chitosan-pectin scaffolds' swelling ratios decreased by 55% after 60 min in a saline solution and more quickly released the preloaded tetracycline HCl. The L929 fibroblast cells proliferated slightly slower on the chitosan-pectin scaffolds than on the chitosan scaffolds. Nonetheless, cells on both materials deposited similar levels of extracellular type I collagen on a per DNA basis. In conclusion, a novel chitosan-pectin nanofibrous scaffold with superior mechanical properties than a chitosan nanofibrous scaffold was successfully made without the use of harmful solvents.

Graphene oxide nanoflakes incorporated gelatin-hydroxyapatite scaffolds enhance osteogenic differentiation of human mesenchymal stem cells

NASA Astrophysics Data System (ADS)

Nair, Manitha; Nancy, D.; Krishnan, Amit G.; Anjusree, G. S.; Vadukumpully, Sajini; Nair, Shantikumar V.

2015-04-01

In this study, graphene oxide (GO) nanoflakes (0.5 and 1 wt%) were incorporated into a gelatin-hydroxyapatite (GHA) matrix through a freeze drying technique and its effect to enhance mechanical strength and osteogenic differentiation was studied. The GHA matrix with GO demonstrated less brittleness in comparison to GHA scaffolds. There was no significant difference in mechanical strength between GOGHA0.5 and GOGHA1.0 scaffolds. When the scaffolds were immersed in phosphate buffered saline (to mimic physiologic condition) for 60 days, around 50-60% of GO was released in sustained and linear manner and the concentration was within the toxicity limit as reported earlier. Further, GOGHA0.5 scaffolds were continued for cell culture experiments, wherein the scaffold induced osteogenic differentiation of human adipose derived mesenchymal stem cells without providing supplements like dexamethasone, L-ascorbic acid and β glycerophosphate in the medium. The level of osteogenic differentiation of stem cells was comparable to those cultured on GHA scaffolds with osteogenic supplements. Thus biocompatible, biodegradable and porous GO reinforced gelatin-HA 3D scaffolds may serve as a suitable candidate in promoting bone regeneration in orthopaedics.

Bioinspired double polysaccharides-based nanohybrid scaffold for bone tissue engineering.

PubMed

Fan, Tiantang; Chen, Jingdi; Pan, Panpan; Zhang, Yujue; Hu, Yimin; Liu, Xiaocui; Shi, Xuetao; Zhang, Qiqing

2016-11-01

The fabrication of bone scaffolds with interconnected porous structure, adequate mechanical properties and excellent biocompatibility presents a great challenge. Herein, a hybrid nanostructured chitosan/chondroitin sulfate/hydroxyapatite (ChS/CSA/HAP) in situ composite scaffold was prepared by in situ fabrication and freeze-drying technique. The composition and morphology of scaffold were characterized by Fourier transform infrared (FT-IR) spectroscopy, X-ray diffraction (XRD) and scanning electron microscopy (SEM). It proved that the low crystallinity of HAP crystals were uniformly distributed in ChS/CSA organic matrix and the nanostructured hybrid scaffold exhibited good mechanical property. The biocompatibility and in vitro bioactivity were detected by MTT-assay, maturation (alkaline phosphatase (ALP) activity), Hoechst 33258 and PI fluorescence staining. In vitro tests indicated that the hybrid scaffold not only promoted the adhesion and proliferation of osteoblasts, but also improved the growth of the osteoblasts. Therefore, it is promising for bone repair application in bone tissue engineering. Copyright © 2016 Elsevier B.V. All rights reserved.

Modeling and optimization of gelatin-chitosan micro-carriers preparation for soft tissue engineering: Using Response Surface Methodology.

PubMed

Radaei, Payam; Mashayekhan, Shohreh; Vakilian, Saeid

2017-06-01

Electrospray ionization is a wide spread technique for producing polymeric microcarriers (MCs) by applying electrostatic force and ionic cross-linker, simultaneously. In this study, fabrication process of gelatin-chitosan MCs and its optimization using the Response Surface Methodology (RSM) is reported. Gelatin/chitosan (G/C) blend ratio, applied voltage and feeding flow rate, their individual and interaction effects on the diameter and mechanical strength of the MCs were investigated. The obtained models for diameter and mechanical strength of MCs have a quadratic relationship with G/C blend ratio, applied voltage and feeding flow rate. Using the desirability curve, optimized G/C blend ratios that are introduced, include the desirable quantities for MCs diameter and mechanical strength. MCs of the same desirable diameter (350μm) and different G/C blend ratio (1, 2, and 3) were fabricated and their elasticity was investigated via Atomic Force Microscopy (AFM). The biocompatibility of the MCs was evaluated using MTT assay. The results showed that human Umbilical Cord Mesenchymal Stem Cells (hUCMSCs) could attach and proliferate on fabricated MCs during 7days of culturing especially on those prepared with G/C blend ratios of 1 and 2. Such gelatin-chitosan MCs may be considered as a promising candidate for injectable tissue engineering scaffolds, supporting attachment and proliferation of hUCMSCs. Copyright © 2017 Elsevier B.V. All rights reserved.

Reinforced nanohydroxyapatite/polyamide66 scaffolds by chitosan coating for bone tissue engineering.

PubMed

Huang, Di; Zuo, Yi; Zou, Qin; Wang, Yanying; Gao, Shibo; Wang, Xiaoyan; Liu, Haohuai; Li, Yubao

2012-01-01

High porosity of scaffold is always accompanied by poor mechanical property; the aim of this study was to enhance the strength and modulus of the highly porous scaffold of nanohydroxyapatite/polyamide66 (n-HA/PA66) by coating chitosan (CS) and to investigate the effect of CS content on the scaffold physical properties and cytological properties. The results show that CS coating can reinforce the scaffold effectively. The compress modulus and strength of the CS coated n-HA/PA66 scaffolds are improved to 32.71 and 2.38 MPa, respectively, being about six times and five times of those of the uncoated scaffolds. Meanwhile, the scaffolds still exhibit a highly interconnected porous structure and the porosity is approximate about 78%, slightly lower than the value (84%) of uncoated scaffold. The cytological properties of scaffolds were also studied in vitro by cocultured with osteoblast-like MG63 cells. The cytological experiments demonstrate that the reinforced scaffolds display favorable cytocompatibility and have no significant difference with the uncoated n-HA/PA66 scaffolds. The CS reinforced n-HA/PA66 scaffolds can meet the basic mechanical requirement of bone tissue engineering scaffold, presenting a potential for biomedical application in bone reconstruction and repair. Copyright © 2011 Wiley Periodicals, Inc.

Effect of inorganic/organic ratio and chemical coupling on the performance of porous silica/chitosan hybrid scaffolds.

PubMed

Wang, Daming; Liu, Wei; Feng, Qian; Dong, Chaoqun; Liu, Qisong; Duan, Li; Huang, Jianghong; Zhu, Weimin; Li, Zemeng; Xiong, Jianyi; Liang, Yujie; Chen, Jielin; Sun, Rong; Bian, Liming; Wang, Daping

2017-01-01

Inorganic/organic hybrid scaffolds have great potential for tissue engineering applications due to controllable mechanical properties and tailorable biodegradation. Here, silica/chitosan hybrid scaffolds were fabricated through the sol-gel method with a freeze drying process. 3-Glycidoxypropyl trimethoxysilane (GPTMS) and tetraethylorthosilicate (TEOS) were used as the covalent inorganic/organic coupling agent and the separate inorganic source, respectively. Hybrid scaffolds with various inorganic/organic weight ratios (I/Os) and molar ratios of chitosan and GPTMS (GCs) were examined and compared in this study. FTIR showed that higher GPTMS content resulted in the increased covalent cross-linking of the chitosan and the silica network in hybrids. Compression testing indicated that increasing the GPTMS content greatly improved the compressive strength of scaffold. LIVE/DEAD assay showed that enhanced cytocompatibility was obtained as the silica content increased. Therefore, the results confirmed that the two parameters I/O and GC can largely influence the scaffold performance, which can be used to tailor the hybrid properties. Copyright © 2016 Elsevier B.V. All rights reserved.

Pore size and LbL chitosan coating influence mesenchymal stem cell in vitro fibrosis and biomineralization in 3D porous poly(epsilon-caprolactone) scaffolds.

PubMed

Mehr, Nima Ghavidel; Li, Xian; Chen, Gaoping; Favis, Basil D; Hoemann, Caroline D

2015-07-01

Poly(epsilon-caprolactone) (PCL) is a hydrophobic bioplastic under development for bone tissue engineering applications. Limited information is available on the role of internal geometry and cell-surface attachment on osseous integration potential. We tested the hypothesis that human bone marrow mesenchymal stem cells (MSCs) deposit more mineral inside porous 3D PCL scaffolds with fully interconnected 84 or 141 µm pores, when the surfaces are coated with chitosan via Layer-by-Layer (LbL)-deposited polyelectrolytes. Freshly trypsinized MSCs were seeded on PCL 3D cylinders using a novel static cold seeding method in 2% serum to optimally populate all depths of the scaffold discs, followed by 10 days of culture in proliferation medium and 21 additional days in osteogenic medium. MSCs were observed by SEM and histology to spread faster and to proliferate more on chitosan-coated pore surfaces. Most pores, with or without chitosan, became filled by collagen networks sparsely populated with fibroblast-like cells. After 21 days of culture in osteogenic medium, sporadic matrix mineralization was detected histologically and by micro-CT in highly cellular surface layers that enveloped all scaffolds and in cell aggregates in 141 µm pores near the edges. LbL-chitosan promoted punctate mineral deposition on the surfaces of 84 µm pores (p < 0.05 vs. PCL-only) but not the 141 µm pores. This study revealed that LbL-chitosan coatings are sufficient to promote MSC attachment to PCL but only enhance mineral formation in 84 µm pores, suggesting a potential inhibitory role for MSC-derived fibroblasts in osteoblast terminal differentiation. © 2014 Wiley Periodicals, Inc.

Development of Useful Biomaterial for Bone Tissue Engineering by Incorporating Nano-Copper-Zinc Alloy (nCuZn) in Chitosan/Gelatin/Nano-Hydroxyapatite (Ch/G/nHAp) Scaffold.

PubMed

Forero, Juan Carlos; Roa, Eduardo; Reyes, Juan G; Acevedo, Cristian; Osses, Nelson

2017-10-17

Ceramic and metallic nanoparticles can improve the mechanical and biological properties of polymeric scaffolds for bone tissue engineering (BTE). In this work, nanohydroxyapatite (nHAp) and nano-copper-zinc alloy (nCuZn) were added to a chitosan/gelatin (Ch/G) scaffold in order to investigate the effects on morphological, physical, and biocompatibility properties. Scaffolds were fabricated by a freeze-drying technique using different pre-freezing temperatures. Microstructure and morphology were studied by scanning electron microscopy (SEM), glass transition ( T g ) was studied using differential scanning calorimetry (DSC), cell growth was estimated by MTT assay, and biocompatibility was examined in vitro and in vivo by histochemistry analyses. Scaffolds and nanocomposite scaffolds presented interconnected pores, high porosity, and pore size appropriate for BTE. T g of Ch/G scaffolds was diminished by nanoparticle inclusion. Mouse embryonic fibroblasts (MEFs) cells loaded in the Ch/G/nHAp/nCuZn nanocomposite scaffold showed suitable behavior, based on cell adhesion, cell growth, alkaline phosphatase (ALP) activity as a marker of osteogenic differentiation, and histological in vitro cross sections. In vivo subcutaneous implant showed granulation tissue formation and new tissue infiltration into the scaffold. The favorable microstructure, coupled with the ability to integrate nanoparticles into the scaffold by freeze-drying technique and the biocompatibility, indicates the potential of this new material for applications in BTE.

Fish gelatin combined with chitosan coating inhibits myofibril degradation of golden pomfret (Trachinotus blochii) fillet during cold storage.

PubMed

Feng, Xiao; Bansal, Nidhi; Yang, Hongshun

2016-06-01

Coating of gelatin and chitosan can improve fish fillet's quality, but the mechanism is not clear. Chitosan/gelatin coatings significantly prevented deterioration of golden pomfret fillet at 4 °C. Chitosan with 7.2% gelatin group showed the best effect on preserving the length of myofibril, which remained greater than 15 μm at day 17 of storage, while for control, chitosan and chitosan combined with 3.6% gelatin group, it was 5.03, 10.04 and 9.02 μm, respectively. The MALDI-TOF MS result revealed that the coatings slowed down the protein deterioration of fillet. On days 13 and 17, the myosin light chain and myoglobin in control group degraded, while the two proteins still existed in chitosan/gelatin coated groups. Overall, the chitosan with 7.2% gelatin coating had the best effect on preserving fillet's quality during storage. The coating may exert its protective effect via inhibiting myofibril degradation within fillet. Copyright © 2016 Elsevier Ltd. All rights reserved.

Fabrication and evaluation of a sustained-release chitosan-based scaffold embedded with PLGA microspheres.

PubMed

Song, Kedong; Liu, Yingchao; Macedo, Hugo M; Jiang, Lili; Li, Chao; Mei, Guanyu; Liu, Tianqing

2013-04-01

Nutrient depletion within three-dimensional (3D) scaffolds is one of the major hurdles in the use of this technology to grow cells for applications in tissue engineering. In order to help in addressing it, we herein propose to use the controlled release of encapsulated nutrients within polymer microspheres into chitosan-based 3D scaffolds, wherein the microspheres are embedded. This method has allowed maintaining a stable concentration of nutrients within the scaffolds over the long term. The polymer microspheres were prepared using multiple emulsions (w/o/w), in which bovine serum albumin (BSA) and poly (lactic-co-glycolic) acid (PLGA) were regarded as the protein pattern and the exoperidium material, respectively. These were then mixed with a chitosan solution in order to form the scaffolds by cryo-desiccation. The release of BSA, entrapped within the embedded microspheres, was monitored with time using a BCA kit. The morphology and structure of the PLGA microspheres containing BSA before and after embedding within the scaffold were observed under a scanning electron microscope (SEM). These had a round shape with diameters in the range of 27-55 μm, whereas the chitosan-based scaffolds had a uniform porous structure with the microspheres uniformly dispersed within their 3D structure and without any morphological change. In addition, the porosity, water absorption and degradation rate at 37 °C in an aqueous environment of 1% chitosan-based scaffolds were (92.99±2.51) %, (89.66±0.66) % and (73.77±3.21) %, respectively. The studies of BSA release from the embedded microspheres have shown a sustained and cumulative tendency with little initial burst, with (20.24±0.83) % of the initial amount released after 168 h (an average rate of 0.12%/h). The protein concentration within the chitosan-based scaffolds after 168 h was found to be (11.44±1.81)×10(-2) mg/mL. This novel chitosan-based scaffold embedded with PLGA microspheres has proven to be a promising technique

Construction of a fluorescent nanostructured chitosan-hydroxyapatite scaffold by nanocrystallon induced biomimetic mineralization and its cell biocompatibility.

PubMed

Wang, Guancong; Zheng, Lin; Zhao, Hongshi; Miao, Junying; Sun, Chunhui; Liu, Hong; Huang, Zhen; Yu, Xiaoqiang; Wang, Jiyang; Tao, Xutang

2011-05-01

Biomaterial surfaces and their nanostructures can significantly influence cell growth and viability. Thus, manipulating surface characteristics of scaffolds can be a potential strategy to control cell functions for stem cell tissue engineering. In this study, in order to construct a hydroxyapatite (HAp) coated genipin-chitosan conjugation scaffold (HGCCS) with a well-defined HAp nanostructured surface, we have developed a simple and controllable approach that allows construction of a two-level, three-dimensional (3D) networked structure to provide sufficient calcium source and achieve desired mechanical function and mass transport (permeability and diffusion) properties. Using a nontoxic cross-linker (genipin) and a nanocrystallon induced biomimetic mineralization method, we first assembled a layer of HAp network-like nanostructure on a 3D porous chitosan-based framework. X-ray diffraction (XRD) and high resolution transmission electron microscopy (HRTEM) analysis confirm that the continuous network-like nanostructure on the channel surface of the HGCCS is composed of crystalline HAp. Compressive testing demonstrated that the strength of the HGCCS is apparently enhanced because of the strong cross-linking of genipin and the resulting reinforcement of the HAp nanonetwork. The fluorescence properties of genipin-chitosan conjugation for convenient monitoring of the 3D porous scaffold biodegradability and cell localization in the scaffold was specifically explored using confocal laser scanning microscopy (CLSM). Furthermore, through scanning electron microscope (SEM) observation and immunofluorescence measurements of F-actin, we found that the HAp network-like nanostructure on the surface of the HGCCS can influence the morphology and integrin-mediated cytoskeleton organization of rat bone marrow-derived mesenchymal stem cells (BMSCs). Based on cell proliferation assays, rat BMSCs tend to have higher viability on HGCCS in vitro. The results of this study suggest that

Boron nitride nanotubes enhance properties of chitosan-based scaffolds.

PubMed

Emanet, Melis; Kazanç, Emine; Çobandede, Zehra; Çulha, Mustafa

2016-10-20

With their low toxicity, high mechanical strength and chemical stability, boron nitride nanotubes (BNNTs) are good candidates to enhance the properties of polymers, composites and scaffolds. Chitosan-based scaffolds are exhaustively investigated in tissue engineering because of their biocompatibility and antimicrobial activity. However, their spontaneous degradation prevents their use in a range of tissue engineering applications. In this study, hydroxylated BNNTs (BNNT-OH) were included into a chitosan scaffold and tested for their mechanical strength, swelling behavior and biodegradability. The results show that inclusion of BNNTs-OH into the chitosan scaffold increases the mechanical strength and pore size at values optimal for high cellular proliferation and adhesion. The chitosan/BNNT-OH scaffold was also found to be non-toxic to Human Dermal Fibroblast (HDF) cells due to its slow degradation rate. HDF cell proliferation and adhesion were increased as compared to the chitosan-only scaffold as observed by scanning electron microscopy (SEM) and fluorescent microscopy images. Copyright © 2016 Elsevier Ltd. All rights reserved.

Modified gum arabic cross-linked gelatin scaffold for biomedical applications.

PubMed

Sarika, P R; Cinthya, Kuriakose; Jayakrishnan, A; Anilkumar, P R; James, Nirmala Rachel

2014-10-01

The present work deals with development of modified gum arabic cross-linked gelatin scaffold for cell culture. A new biocompatible scaffold was developed by cross-linking gelatin (Gel) with gum arabic, a polysaccharide. Gum arabic was subjected to periodate oxidation to obtain gum arabic aldehyde (GAA). GAA was reacted with gelatin under appropriate pH to prepare the cross-linked hydrogel. Cross-linking occurred due to Schiff's base reaction between aldehyde groups of oxidized gum arabic and amino groups of gelatin. The scaffold prepared from the hydrogel was characterized by swelling properties, degree of cross-linking, in vitro degradation and scanning electron microscopy (SEM). Cytocompatibility evaluation using L-929 and HepG2 cells confirmed non-cytotoxic and non-adherent nature of the scaffold. These properties are essential for generating multicellular spheroids and hence the scaffold is proposed to be a suitable candidate for spheroid cell culture. Copyright © 2014 Elsevier B.V. All rights reserved.

Preparation and characterization of three-dimensional scaffolds based on hydroxypropyl chitosan-graft-graphene oxide.

PubMed

Sivashankari, P R; Moorthi, A; Abudhahir, K Mohamed; Prabaharan, M

2018-04-15

Hydroxypropyl chitosan (HPCH), a water soluble derivative of chitosan, is widely considered for tissue engineering and wound healing applications due to its biocompatibility and biodegradability. Graphene oxide (GO) is a carbon-based nanomaterial which is capable of imparting desired properties to the scaffolds. Hence, the integration of GO into HPCH could allow for the production of HPCH-based scaffolds with improved swelling character, mechanical strength, and stability aimed at being used in tissue engineering. In this study, hydroxypropyl chitosan-graft-graphene oxide (HPCH-g-GO) with varying GO content (0.5, 1, 3 and 4wt.%) was prepared using HPCH and GO as a tissue engineering scaffold material. The formation of HPCH-g-GO was confirmed by FTIR and XRD analysis. Using the HPCH-g-GO as a matrix material and glutaraldehyde as a crosslinking agent, the three dimensional (3D) porous scaffolds were fabricated by the freeze-drying method. The HPCH-g-GO scaffolds exhibited uniform porosity as observed in SEM analysis. The pore size and porosity reduced as the content of GO was increased. These scaffolds presented good swelling capacity, water retention ability, mechanical strength and in vitro degradation properties. The HPCH-g-GO scaffolds irrespective of their GO content demonstrated good cell viability when compared to control. Altogether, these results suggest that HPCH-g-GO scaffolds can be used as potential tissue engineering material. Copyright © 2017 Elsevier B.V. All rights reserved.

Poly(N-isopropylacrylamide) hydrogel/chitosan scaffold hybrid for three-dimensional stem cell culture and cartilage tissue engineering.

PubMed

Mellati, Amir; Kiamahalleh, Meisam Valizadeh; Madani, S Hadi; Dai, Sheng; Bi, Jingxiu; Jin, Bo; Zhang, Hu

2016-11-01

Providing a controllable and definable three-dimensional (3D) microenvironment for chondrogenic differentiation of mesenchymal stem cells (MSCs) remains a great challenge for cartilage tissue engineering. In this work, poly(N-isopropylacrylamide) (PNIPAAm) polymers with the degrees of polymerization of 100 and 400 (NI100 and NI400) were prepared and the polymer solutions were introduced into the preprepared chitosan porous scaffolds (CS) to form hybrids (CSNI100 and CSNI400, respectively). SEM images indicated that the PNIPAAm gel partially occupied chitosan pores while the interconnected porous structure of chitosan was preserved. MSCs were incorporated within the hybrid and cell proliferation and chondrogenic differentiation were monitored. After 7-day incubation of the cell-laden constructs in a growth medium, the cell viability in CSNI100 and CSNI400 were 54 and 108% higher than that in CS alone, respectively. Glycosaminoglycan and total collagen contents increased 2.6- and 2.5-fold after 28-day culture of cell-laden CSNI400 in the chondrogenic medium. These results suggest that the hybrid structure composed of the chitosan porous scaffold and the well-defined PNIPAAm hydrogel, in particular CSNI400, is suitable for 3D stem cell culture and cartilage tissue engineering. © 2016 Wiley Periodicals, Inc. J Biomed Mater Res Part A: 104A: 2764-2774, 2016. © 2016 Wiley Periodicals, Inc.

A dual-application poly (dl-lactic-co-glycolic) acid (PLGA)-chitosan composite scaffold for potential use in bone tissue engineering.

PubMed

Boukari, Yamina; Qutachi, Omar; Scurr, David J; Morris, Andrew P; Doughty, Stephen W; Billa, Nashiru

2017-11-01

The development of patient-friendly alternatives to bone-graft procedures is the driving force for new frontiers in bone tissue engineering. Poly (dl-lactic-co-glycolic acid) (PLGA) and chitosan are well-studied and easy-to-process polymers from which scaffolds can be fabricated. In this study, a novel dual-application scaffold system was formulated from porous PLGA and protein-loaded PLGA/chitosan microspheres. Physicochemical and in vitro protein release attributes were established. The therapeutic relevance, cytocompatibility with primary human mesenchymal stem cells (hMSCs) and osteogenic properties were tested. There was a significant reduction in burst release from the composite PLGA/chitosan microspheres compared with PLGA alone. Scaffolds sintered from porous microspheres at 37 °C were significantly stronger than the PLGA control, with compressive strengths of 0.846 ± 0.272 MPa and 0.406 ± 0.265 MPa, respectively (p < 0.05). The formulation also sintered at 37 °C following injection through a needle, demonstrating its injectable potential. The scaffolds demonstrated cytocompatibility, with increased cell numbers observed over an 8-day study period. Von Kossa and immunostaining of the hMSC-scaffolds confirmed their osteogenic potential with the ability to sinter at 37 °C in situ.

Nanostructured 3D constructs based on chitosan and chondroitin sulphate multilayers for cartilage tissue engineering.

PubMed

Silva, Joana M; Georgi, Nicole; Costa, Rui; Sher, Praveen; Reis, Rui L; Van Blitterswijk, Clemens A; Karperien, Marcel; Mano, João F

2013-01-01

Nanostructured three-dimensional constructs combining layer-by-layer technology (LbL) and template leaching were processed and evaluated as possible support structures for cartilage tissue engineering. Multilayered constructs were formed by depositing the polyelectrolytes chitosan (CHT) and chondroitin sulphate (CS) on either bidimensional glass surfaces or 3D packet of paraffin spheres. 2D CHT/CS multi-layered constructs proved to support the attachment and proliferation of bovine chondrocytes (BCH). The technology was transposed to 3D level and CHT/CS multi-layered hierarchical scaffolds were retrieved after paraffin leaching. The obtained nanostructured 3D constructs had a high porosity and water uptake capacity of about 300%. Dynamical mechanical analysis (DMA) showed the viscoelastic nature of the scaffolds. Cellular tests were performed with the culture of BCH and multipotent bone marrow derived stromal cells (hMSCs) up to 21 days in chondrogenic differentiation media. Together with scanning electronic microscopy analysis, viability tests and DNA quantification, our results clearly showed that cells attached, proliferated and were metabolically active over the entire scaffold. Cartilaginous extracellular matrix (ECM) formation was further assessed and results showed that GAG secretion occurred indicating the maintenance of the chondrogenic phenotype and the chondrogenic differentiation of hMSCs.

Improved Mesenchymal Stem Cells Attachment and In Vitro Cartilage Tissue Formation on Chitosan-Modified Poly(l-Lactide-co-Epsilon-Caprolactone) Scaffold

PubMed Central

Wu, Yingnan; Li, Chao; Zhang, Tianting; Zou, Yu; Hui, James H.P.; Lee, Eng Hin

2012-01-01

Considering the load-bearing physiological requirement of articular cartilage, scaffold for cartilage tissue engineering should exhibit appropriate mechanical responses as natural cartilage undergoing temporary deformation on loading with little structural collapse, and recovering to the original geometry on unloading. A porous elastomeric poly l-lactide-co-ɛ-caprolactone (PLCL) was generated and crosslinked at the surface to chitosan to improve its wettability. Human bone marrow derived mesenchymal stem cells (MSC) attachment, morphological change, proliferation and in vitro cartilage tissue formation on the chitosan-modified PLCL scaffold were compared with the unmodified PLCL scaffold. Chitosan surface promoted more consistent and even distribution of the seeded MSC within the scaffold. MSC rapidly adopted a distinct spread-up morphology on attachment on the chitosan-modified PLCL scaffold with the formation of F-actin stress fiber which proceeded to cell aggregation; an event much delayed in the unmodified PLCL. Enhanced cartilage formation on the chitosan-modified PLCL was shown by real-time PCR analysis, histological and immunochemistry staining and biochemical assays of the cartilage extracellular matrix components. The Young's modulus of the derived cartilage tissues on the chitosan-modified PLCL scaffold was significantly increased and doubled that of the unmodified PLCL. Our results show that chitosan modification of the PLCL scaffold improved the cell compatibility of the PLCL scaffold without significant alteration of the physical elastomeric properties of PLCL and resulted in the formation of cartilage tissue of better quality. PMID:21902611

Characterization of konjac glucomannan-gelatin IPN physical hydrogel scaffold

NASA Astrophysics Data System (ADS)

Chen, Xiliang; Chen, Qinghua; Yan, Tingting; Liu, Jinkun

2017-06-01

A novel IPN hydrogel scaffold is prepared by freeze-drying method, in which konjac galactomannan (KGM) and gelatin are physically crosslinked respectively. This scaffold is thermostable, and the structure of this scaffold is analysed by scanning electron microscope, Fourier transform infrared spectrum, and X-ray diffraction method. The FT-IR results show that hydrogen bonds are formed between KGM and gelatin molecules, which hinder the formation of their respective crosslinking. This is consistent with the XRD results that the crystallinity gets lower in the IPN gels compared with pure gelatin and KGM gels. The morphologies of freeze-dried hydrogels are observed by SEM and the mechanical properties of the scaffolds are tested to analyse the relationship between the structures and properties. Although this novel IPN hydrogel is physical gel, it shows rubber-like performance as chemical gels. And it is nontoxic, so it can be used as the scaffold for cartilage tissue engineering that embedded in human bodies.

Properties of gelatin-based films incorporated with chitosan-coated microparticles charged with rutin.

PubMed

Dammak, Ilyes; Bittante, Ana Mônica Quinta Barbosa; Lourenço, Rodrigo Vinicius; do Amaral Sobral, Paulo José

2017-08-01

The aim of this study was development an active film based on gelatin incorporated with antioxidant, rutin carried into microparticles. The complexation between oppositely charged lecithin and chitosan was applied to prepare the chitosan-coated microparticles. The generated microparticles had an average size of 520±4nm and a span of 0.3 were formulated by a rotor-stator homogenize at the homogenization speed 10,000rpm. Composite films were prepared by incorporating chitosan-coated microparticles, at various concentrations (0.05, 0.1, 0.5, or 1% (based on the weight of the gelatin powder)) in the gelatin-based films. For the prepared films, the results showed that obtained physicochemical, water vapor barrier, and mechanical were compared with native gelatin film with a slight decrease for chitosan concentration higher than 0.5%. The microstructure studies done by scanning electron microscopes, revealed different micropores embedded with oil resulting from the incorporation of the microparticles into the gelatin matrix. Moreover, the calorimetric results were comparable to those of gelatin control film with T g value 45°C and increased crystallinity percentage with increasing incorporation of microparticles. This original concept of composite biodegradable films may thus be a good alternative to incorporate liposoluble active compounds to design an active packaging with good properties. Copyright © 2017 Elsevier B.V. All rights reserved.

Ultrafast Spreading Effect Induced Rapid Cell Trapping into Porous Scaffold with Superhydrophilic Surface.

PubMed

Wang, Chenmiao; Qiao, Chunyan; Song, Wenlong; Sun, Hongchen

2015-08-19

In this contribution, superhydrophilic chitosan-based scaffolds with ultrafast spreading property were fabricated and used to improve the trapped efficiency of cells. The ultrafast spreading property allowed cells to be trapped into the internal 3D porous structures of the prepared scaffolds more quickly and effectively. Cell adhesion, growth, and proliferation were also improved, which could be attributed to the combination of UV irradiation and ultrafast spreading property. The construction of ultrafast spreading property on the scaffold surface will offer a novel way to design more effective scaffold in tissue engineering that could largely shorten the therapeutic time for patients.

Development of core-shell coaxially electrospun composite PCL/chitosan scaffolds.

PubMed

Surucu, Seda; Turkoglu Sasmazel, Hilal

2016-11-01

This study was related to combining of synthetic Poly (ε-caprolactone) (PCL) and natural chitosan polymers to develop three dimensional (3D) PCL/chitosan core-shell scaffolds for tissue engineering applications. The scaffolds were fabricated with coaxial electrospinning technique and the characterizations of the samples were done by thickness and contact angle (CA) measurements, scanning electron microscopy (SEM), transmission electron microscopy (TEM), X-Ray Photoelectron Spectroscopy (XPS) analyses, mechanical and PBS absorption and shrinkage tests. The average inter-fiber diameter values were calculated for PCL (0.717±0.001μm), chitosan (0.660±0.007μm) and PCL/chitosan core-shell scaffolds (0.412±0.003μm), also the average inter-fiber pore size values exhibited decreases of 66.91% and 61.90% for the PCL and chitosan scaffolds respectively, compared to PCL/chitosan core-shell ones. XPS analysis of the PCL/chitosan core-shell structures exhibited the characteristic peaks of PCL and chitosan polymers. The cell culture studies (MTT assay, Confocal Laser Scanning Microscope (CLSM) and SEM analyses) carried out with L929 ATCC CCL-1 mouse fibroblast cell line proved that the biocompatibility performance of the scaffolds. The obtained results showed that the created micro/nano fibrous structure of the PCL/chitosan core-shell scaffolds in this study increased the cell viability and proliferation on/within scaffolds. Copyright © 2016 Elsevier B.V. All rights reserved.

Phosphatidylcholine nanovesicles coated with chitosan or chondroitin sulfate as novel devices for bacteriocin delivery

NASA Astrophysics Data System (ADS)

da Silva, Indjara Mallmann; Boelter, Juliana Ferreira; da Silveira, Nádya Pesce; Brandelli, Adriano

2014-07-01

There is increased interest on the use of natural antimicrobial peptides in biomedicine and food preservation technologies. In this study, the antimicrobial activity of nisin encapsulated into nanovesicles containing polyanionic polysaccharides was investigated. Nisin was encapsulated in phosphatidylcholine (PC) liposomes containing chitosan or chondroitin sulfate by the thin-film hydration method and tested for antimicrobial activity against Listeria spp. The mean particle size of PC liposomes was 145 nm and varied to 210 and 134 nm with the incorporation of chitosan and chondroitin sulfate, respectively. Nisin-containing nanovesicles with and without incorporation of polysaccharides had a zeta potential values around -20 mV, showing mostly spherical structures when observed by transmission electron microscopy. Encapsulated nisin had similar efficiency as free nisin in inhibiting Listeria spp. isolated from bovine carcass, and greater efficiency in inhibiting Listeria monocytogenes. The formulation containing chitosan was more stable and more efficient in inhibiting L. monocytogenes when compared to the other nanovesicles tested. After 24 h, the viable cell counts were 2 log lower as compared with the other treatments and 7 log comparing to controls.

Selection of a chitosan gelatin-based edible coating for color preservation of beef in retail display.

PubMed

Cardoso, Giselle Pereira; Dutra, Monalisa Pereira; Fontes, Paulo Rogério; Ramos, Alcinéia de Lemos Souza; Gomide, Lúcio Alberto de Miranda; Ramos, Eduardo Mendes

2016-04-01

Chitosan gelatin-based coating films were applied to beef steaks, and their effects on color preservation and lipid oxidation during retail display were evaluated. Response surface methodology was used to model and describe the effects of different biopolymer concentrations (0 to 6% gelatin; 0.5 to 1.5% chitosan; and 0 to 12% glycerol based on dry gelatin+chitosan weight) in the coating film for optimizing the best combination for meat application. Film application reduced weight loss and lipid oxidation of the steaks after 5 days of storage, and films with higher gelatin concentrations were more effective. The percentage levels of different myoglobin-redox forms were not affected by coating, but myoglobin oxidation during retail display was reduced and the percentage of deoxymyoglobin increased with the gelatin content of the film. Steak color stability during retail display was promoted by film application; the steaks exhibited a darker, more intensely red color when coated in blends with higher gelatin and chitosan contents. Blends containing between 3% and 6% gelatin, between 0.5% and 1.0% chitosan and 6% glycerol exhibited the best results and provide a promising alternative to the preservation of beef in retail display. Copyright © 2015 Elsevier Ltd. All rights reserved.

Long-term liver-specific functions of hepatocytes in electrospun chitosan nanofiber scaffolds coated with fibronectin.

PubMed

Rajendran, Divya; Hussain, Ali; Yip, Derek; Parekh, Amit; Shrirao, Anil; Cho, Cheul H

2017-08-01

In this study, a new 3D liver model was developed using biomimetic nanofiber scaffolds and co-culture system consisting of hepatocytes and fibroblasts for the maintenance of long-term liver functions. The chitosan nanofiber scaffolds were fabricated by the electrospinning technique. To enhance cellular adhesion and spreading, the surfaces of the chitosan scaffolds were coated with fibronectin (FN) by adsorption and evaluated for various cell types. Cellular phenotype, protein expression, and liver-specific functions were extensively characterized by immunofluorescent and histochemical stainings, albumin enzyme-linked immunosorbent assay and Cytochrome p450 detoxification assays, and scanning electron microscopy. The electrospun chitosan scaffolds exhibited a highly porous and randomly oriented nanofibrous structure. The FN coating on the surface of the chitosan nanofibers significantly enhanced cell attachment and spreading, as expected, as surface modification with this cell adhesion molecule on the chitosan surface is important for focal adhesion formation and integrin binding. Comparison of hepatocyte mono-cultures and co-cultures in 3D culture systems indicated that the hepatocytes in co-cultures formed colonies and maintained their morphologies and functions for prolonged periods of time. The 3D liver tissue model developed in this study will provide useful tools toward the development of engineered liver tissues for drug screening and tissue engineering applications. © 2017 Wiley Periodicals, Inc. J Biomed Mater Res Part A: 105A: 2119-2128, 2017. © 2017 Wiley Periodicals, Inc.

Biochemical properties of Hemigraphis alternata incorporated chitosan hydrogel scaffold.

PubMed

Annapoorna, M; Sudheesh Kumar, P T; Lakshman, Lakshmi R; Lakshmanan, Vinoth-Kumar; Nair, Shantikumar V; Jayakumar, R

2013-02-15

In this work, Hemigraphis alternata extract incorporated chitosan scaffold was synthesized and characterized for wound healing. The antibacterial activity of Hemigraphis incorporated chitosan scaffold (HIC) against Escherichia coli and Staphylococcus aureus was evaluated which showed a reduction in total colony forming units by 45-folds toward E. coli and 25-fold against S. aureus respectively. Cell viability studies using Human Dermal Fibroblast cells (HDF) showed 90% viability even at 48 h when compared to the chitosan control. The herbal scaffold made from chitosan was highly haemostatic and antibacterial. The obtained results were in support that the herbal scaffold can be effectively applied for infectious wounds. Copyright © 2012 Elsevier Ltd. All rights reserved.

Effect of Plasticizers on Physicochemical and Mechanical Properties of Chitosan-Gelatin Films

NASA Astrophysics Data System (ADS)

Manshor, N. Mohammed; Rezali, M. I.; Jai, J.; Yahya, A.

2018-05-01

Composite chitosan-gelatin films were produced to investigate the effect of plasticizer and composition of chitosan and gelatin on physicochemical and mechanical properties of the films. The films were prepared according to ratio of chitosan: gelatin of 1:1, 1:2 and 2:1. For each film, glycerol, sorbitol and sucrose were added as plasticizer. The film forming solution was poured on a glass plate and dried for 12 hours in an oven at 60°C. The highest tensile strength was 4.04 MPa for films of ratio 2:1 plasticized with glycerol compared to sorbitol and sucrose which were 3.94 MPa and 3.84 MPa, respectively. However, films plasticized with sorbitol at ratio of 1:2 had the highest percent elongation which was 68.20%, followed by glycerol and sucrose which were 26.51% and 24.08%, respectively.

Improving effects of chitosan nanofiber scaffolds on osteoblast proliferation and maturation

PubMed Central

Ho, Ming-Hua; Liao, Mei-Hsiu; Lin, Yi-Ling; Lai, Chien-Hao; Lin, Pei-I; Chen, Ruei-Ming

2014-01-01

Osteoblast maturation plays a key role in regulating osteogenesis. Electrospun nanofibrous products were reported to possess a high surface area and porosity. In this study, we developed chitosan nanofibers and examined the effects of nanofibrous scaffolds on osteoblast maturation and the possible mechanisms. Macro- and micro observations of the chitosan nanofibers revealed that these nanoproducts had a flat surface and well-distributed fibers with nanoscale diameters. Mouse osteoblasts were able to attach onto the chitosan nanofiber scaffolds, and the scaffolds degraded in a time-dependent manner. Analysis by scanning electron microscopy further showed mouse osteoblasts adhered onto the scaffolds along the nanofibers, and cell–cell communication was also detected. Mouse osteoblasts grew much better on chitosan nanofiber scaffolds than on chitosan films. In addition, human osteoblasts were able to adhere and grow on the chitosan nanofiber scaffolds. Interestingly, culturing human osteoblasts on chitosan nanofiber scaffolds time-dependently increased DNA replication and cell proliferation. In parallel, administration of human osteoblasts onto chitosan nanofibers significantly induced osteopontin, osteocalcin, and alkaline phosphatase (ALP) messenger (m)RNA expression. As to the mechanism, chitosan nanofibers triggered runt-related transcription factor 2 mRNA and protein syntheses. Consequently, results of ALP-, alizarin red-, and von Kossa-staining analyses showed that chitosan nanofibers improved osteoblast mineralization. Taken together, results of this study demonstrate that chitosan nanofibers can stimulate osteoblast proliferation and maturation via runt-related transcription factor 2-mediated regulation of osteoblast-associated osteopontin, osteocalcin, and ALP gene expression. PMID:25246786

Coating electrospun poly(epsilon-caprolactone) fibers with gelatin and calcium phosphate and their use as biomimetic scaffolds for bone tissue engineering.

PubMed

Li, Xiaoran; Xie, Jingwei; Yuan, Xiaoyan; Xia, Younan

2008-12-16

Electrospinning was employed to fabricate fibrous scaffolds of poly(epsilon-caprolactone) in the form of nonwoven mats. The surfaces of the fibers were then coated with gelatin through layer-by-layer self-assembly, followed by functionalization with a uniform coating of bonelike calcium phosphate by mineralization in the 10 times concentrated simulated body fluid for 2 h. Transmission electron microscopy, water contact angle, and scanning electron microscopy measurements confirmed the presence of gelatin and calcium phosphate coating layers, and X-ray diffraction results suggested that the deposited mineral phase was a mixture of dicalcium phosphate dehydrate (a precursor to apatite) and apatite. It was also demonstrated that the incorporation of gelatin promoted nucleation and growth of calcium phosphate. The porous scaffolds could mimic the structure, composition, and biological function of bone extracellular matrix. It was found that the preosteoblastic MC3T3-E1 cells attached, spread, and proliferated well with a flat morphology on the mineralized scaffolds. The proliferation rate of the cells on the mineralized scaffolds was significantly higher (by 1.9-fold) than that on the pristine fibrous scaffolds after culture for 7 days. These results indicated that the hybrid system containing poly(epsilon-caprolactone), gelatin, and calcium phosphate could serve as a new class of biomimetic scaffolds for bone tissue engineering.

Preparation, characterization and biological test of 3D-scaffolds based on chitosan, fibroin and hydroxyapatite for bone tissue engineering.

PubMed

Lima, Paulo Autran Leite; Resende, Cristiane Xavier; Soares, Glória Dulce de Almeida; Anselme, Karine; Almeida, Luís Eduardo

2013-08-01

This work describes the preparation and characterization of porous 3D-scaffolds based on chitosan (CHI), chitosan/silk fibroin (CHI/SF) and chitosan/silk fibroin/hydroxyapatite (CHI/SF/HA) by freeze drying. The biomaterials were characterized by X-ray diffraction, attenuated total reflection Fourier transform infrared spectroscopy, thermogravimetric analysis, differential scanning calorimetry, scanning electron microscopy and energy dispersive spectroscopy. In addition, studies of porosity, pore size, contact angle and biological response of SaOs-2osteoblastic cells were performed. The CHI scaffolds have a porosity of 94.2±0.9%, which is statistically higher than the one presented by CHI/SF/HA scaffolds, 89.7±2.6%. Although all scaffolds were able to promote adhesion, growth and maintenance of osteogenic differentiation of SaOs-2 cells, the new 3D-scaffold based on CHI/SF/HA showed a significantly higher cell growth at 7 days and 21 days and the level of alkaline phosphatase at 14 and 21 days was statistically superior compared to other tested materials. Copyright © 2013 Elsevier B.V. All rights reserved.

Release behavior and signaling effect of vitamin D3 in layered double hydroxides-hydroxyapatite/gelatin bone tissue engineering scaffold: An in vitro evaluation.

PubMed

Fayyazbakhsh, Fateme; Solati-Hashjin, Mehran; Keshtkar, Abbas; Shokrgozar, Mohammad Ali; Dehghan, Mohammad Mehdi; Larijani, Bagher

2017-10-01

Incorporating the controlled release of vitamin D3 (VD3) into biodegradable porous scaffolds is a new approach to equipping multifunctional therapeutics for osteoporosis. The current investigation involves the encapsulation of VD3 into gelatin through the one-step desolvation method. The layered double hydroxides-hydroxyapatite nanocomposite (LDH-HAp) and pure LDH were combined with the gelatin-VD3 complex to reinforce the porous biodegradable structure and enhance the biological response. Afterwards, glutaraldehyde was used to form crosslinks within the gelatin chains. The encapsulation efficiency and loading capacity showed approximately 40% and 50% reduction after crosslinking, respectively. The particle size, zeta potential, contact angle, Young's modulus and porosity were measured to find the effect of VD3 on the scaffolds' physiochemical properties. To explore the bioactivity and degradation behavior, the scaffolds were immersed in simulated body fluid. The VD3 release kinetics followed the Korsmeyer-Peppas model and non-Fickian release pattern. The greater osteblastic expression was observed in VD3-containing scaffolds due to the higher alkaline phosphatase activity which was excited more by HAp (P<0.05). Alizarin red staining illustrated that VD3 induced more calcium deposition, which indicates the signaling role of VD3 on osteoconductivity and biomineralization. The findings provide new insights on the VD3 encapsulation within hydrophilic matrices to protect VD3 and enable the signaling ability for bone tissue engineering scaffolds, which could improve the bone healing efficiency. Copyright © 2017 Elsevier B.V. All rights reserved.

Effect of enzymatic degradation of chitosan in polyhydroxybutyrate/chitosan/calcium phosphate composites on in vitro osteoblast response.

PubMed

Giretova, Maria; Medvecky, Lubomir; Stulajterova, Radoslava; Sopcak, Tibor; Briancin, Jaroslav; Tatarkova, Monika

2016-12-01

Polyhydroxybutyrate/chitosan/calcium phosphate composites are interesting biomaterials for utilization in regenerative medicine and they may by applied in reconstruction of deeper subchondral defects. Insufficient informations were found in recent papers about the influence of lysozyme degradation of chitosan in calcium phosphate/chitosan based composites on in vitro cytotoxicity and proliferation activity of osteoblasts. The effect of enzymatic chitosan degradation on osteoblasts proliferation was studied on composite films in which the porosity of origin 3D scaffolds was eliminated and the surface texture was modified. The significantly enhanced proliferation activity with faster population growth of osteoblasts were found on enzymatically degraded biopolymer composite films with α-tricalcium phosphate and nanohydroxyapatite. No cytotoxicity of composite films prepared from lysozyme degraded scaffolds containing a large fraction of low molecular weight chitosans (LMWC), was revealed after 10 days of cultivation. Contrary to above in the higher cytotoxicity origin untreated nanohydroxyapatite films and porous composite scaffolds. The results showed that the synergistic effect of surface distribution, morphology of nanohydroxyapatite particles, microtopography and the presence of LMWC due to chitosan degradation in composite films were responsible for compensation of the cytotoxicity of nanohydroxyapatite composite films or porous composite scaffolds.

Fabrication of Chitosan Silk-based Tracheal Scaffold Using Freeze-Casting Method

PubMed Central

Nematollahi, Zeinab; Tafazzoli-Shadpour, Mohammad; Zamanian, Ali; Seyedsalehi, Amir; Mohammad-Behgam, Shadmehr; Ghorbani, Fariba; Mirahmadi, Fereshte

2017-01-01

Background: Since the treatments of long tracheal lesions are associated with some limitations, tissue engineered trachea is considered as an alternative option. This study aimed at preparing a composite scaffold, based on natural and synthetic materials for tracheal tissue engineering. Methods: Nine chitosan silk-based scaffolds were fabricated using three freezing rates (0.5, 1, and 2°C/min) and glutaraldehyde (GA) concentrations (0, 0.4, and 0.8 wt%). Samples were characterized, and scaffolds having mechanical properties compatible with those of human trachea and proper biodegradability were selected for chondrocyte cell seeding and subsequent biological assessments. Results: The pore sizes were highly influenced by the freezing rate and varied from 135.3×372.1 to 37.8×83.4 µm. Swelling and biodegradability behaviors were more affected by GA rather than freezing rate. Tensile strength raised from 120 kPa to 350 kPa by an increment of freezing rate and GA concentration. In addition, marked stiffening was demonstrated by increasing elastic modulus from 1.5 MPa to 12.2 MPa. Samples having 1 and 2°C/min of freezing rate and 0.8 wt% GA concentration made a non-toxic, porous structure with tensile strength and elastic modulus in the range of human trachea, facilitating the chondrocyte proliferation. The results of 21-day cell culture indicated that glycosaminoglycans content was significantly higher for the rate of 2°C/min (12.04 µg/min) rather than the other (9.6 µg/min). Conclusion: A homogenous porous structure was created by freeze drying. This allows the fabrication of a chitosan silk scaffold cross-linked by GA for cartilage tissue regeneration with application in tracheal regeneration. PMID:28131109

Silk fibroin-chondroitin sulfate scaffold with immuno-inhibition property for articular cartilage repair.

PubMed

Zhou, Feifei; Zhang, Xianzhu; Cai, Dandan; Li, Jun; Mu, Qin; Zhang, Wei; Zhu, Shouan; Jiang, Yangzi; Shen, Weiliang; Zhang, Shufang; Ouyang, Hong Wei

2017-11-01

The demand of favorable scaffolds has increased for the emerging cartilage tissue engineering. Chondroitin sulfate (CS) and silk fibroin have been investigated and reported with safety and excellent biocompatibility as tissue engineering scaffolds. However, the rapid degradation rate of pure CS scaffolds presents a challenge to effectively recreate neo-tissue similar to natural articular cartilage. Meanwhile the silk fibroin is well used as a structural constituent material because its remarkable mechanical properties, long-lasting in vivo stability and hypoimmunity. The application of composite silk fibroin and CS scaffolds for joint cartilage repair has not been well studied. Here we report that the combination of silk fibroin and CS could synergistically promote articular cartilage defect repair. The silk fibroin (silk) and silk fibroin/CS (silk-CS) scaffolds were fabricated with salt-leaching, freeze-drying and crosslinking methodologies. The biocompatibility of the scaffolds was investigated in vitro by cell adhesion, proliferation and migration with human articular chondrocytes. We found that silk-CS scaffold maintained better chondrocyte phenotype than silk scaffold; moreover, the silk-CS scaffolds reduced chondrocyte inflammatory response that was induced by interleukin (IL)-1β, which is in consistent with the well-documented anti-inflammatory activities of CS. The in vivo cartilage repair was evaluated with a rabbit osteochondral defect model. Silk-CS scaffold induced more neo-tissue formation and better structural restoration than silk scaffold after 6 and 12weeks of implantation in ICRS histological evaluations. In conclusion, we have developed a silk fibroin/ chondroitin sulfate scaffold for cartilage tissue engineering that exhibits immuno-inhibition property and can improve the self-repair capacity of cartilage. Severe cartilage defect such as osteoarthritis (OA) is difficult to self-repair because of its avascular, aneural and alymphatic nature

In vitro evaluation of crosslinked electrospun fish gelatin scaffolds.

PubMed

Gomes, S R; Rodrigues, G; Martins, G G; Henriques, C M R; Silva, J C

2013-04-01

Gelatin from cold water fish skin was electrospun, crosslinked and investigated as a substrate for the adhesion and proliferation of cells. Gelatin was first dissolved in either water or concentrated acetic acid and both solutions were successfully electrospun. Cross-linking was achieved via three different routes: glutaraldehyde vapor, genipin and dehydrothermal treatment. Solution's properties (surface tension, electrical conductivity and viscosity) and scaffold's properties (chemical bonds, weight loss and fiber diameters) were measured. Cellular viability was analyzed culturing 3T3 fibroblasts plated on the scaffolds and grown up to 7 days. The cells were fixed and observed with SEM or stained for DNA and F-actin and observed with confocal microscopy. In all scaffolds, the cells attached and spread with varying degrees. The evaluation of cell viability showed proliferation of cells until confluence in scaffolds crosslinked by glutaraldehyde and genipin; however the rate of growth in genipin crosslinked scaffolds was slow, recovering only by day five. The results using the dehydrothermal treatment were the less satisfactory. Our results show that glutaraldehyde treated fish gelatin is the most suitable substrate, of the three studied, for fibroblast adhesion and proliferation. Copyright © 2012 Elsevier B.V. All rights reserved.

Preparation of aminated chitosan/alginate scaffold containing halloysite nanotubes with improved cell attachment.

PubMed

Amir Afshar, Hamideh; Ghaee, Azadeh

2016-10-20

The chemical nature of biomaterials play important role in cell attachment, proliferation and migration in tissue engineering. Chitosan and alginate are biodegradable and biocompatible polymers used as scaffolds for various medical and clinical applications. Amine groups of chitosan scaffolds play an important role in cell attachment and water adsorption but also associate with alginate carboxyl groups via electrostatic interactions and hydrogen bonding, consequently the activity of amine groups in the scaffold decreases. In this study, chitosan/alginate/halloysite nanotube (HNTs) composite scaffolds were prepared using a freeze-drying method. Amine treatment on the scaffold occurred through chemical methods, which in turn caused the hydroxyl groups to be replaced with carboxyl groups in chitosan and alginate, after which a reaction between ethylenediamine, 1-ethyl-3,(3-dimethylaminopropyl) carbodiimide (EDC) and scaffold triggered the amine groups to connect to the carboxyl groups of chitosan and alginate. The chemical structure, morphology and mechanical properties of the composite scaffolds were investigated by FTIR, CHNS, SEM/EDS and compression tests. The electrostatic attraction and hydrogen bonding between chitosan, alginate and halloysite was confirmed by FTIR spectroscopy. Chitosan/alginate/halloysite scaffolds exhibit significant enhancement in compressive strength compared with chitosan/alginate scaffolds. CHNS and EDS perfectly illustrate that amine groups were effectively introduced in the aminated scaffold. The growth and cell attachment of L929 cells as well as the cytotoxicity of the scaffolds were investigated by SEM and Alamar Blue (AB). The results indicated that the aminated chitosan/alginate/halloysite scaffold has better cell growth and cell adherence in comparison to that of chitosan/alginate/halloysite samples. Aminated chitosan/alginate/halloysite composite scaffolds exhibit great potential for applications in tissue engineering, ideally in

Genipin-Crosslinked Chitosan Gels and Scaffolds for Tissue Engineering and Regeneration of Cartilage and Bone

PubMed Central

Muzzarelli, Riccardo A. A.; El Mehtedi, Mohamad; Bottegoni, Carlo; Aquili, Alberto; Gigante, Antonio

2015-01-01

The present review article intends to direct attention to the technological advances made since 2009 in the area of genipin-crosslinked chitosan (GEN-chitosan) hydrogels. After a concise introduction on the well recognized characteristics of medical grade chitosan and food grade genipin, the properties of GEN-chitosan obtained with a safe, spontaneous and irreversible chemical reaction, and the quality assessment of the gels are reviewed. The antibacterial activity of GEN-chitosan has been well assessed in the treatment of gastric infections supported by Helicobacter pylori. Therapies based on chitosan alginate crosslinked with genipin include stem cell transplantation, and development of contraction free biomaterials suitable for cartilage engineering. Collagen, gelatin and other proteins have been associated to said hydrogels in view of the regeneration of the cartilage. Viability and proliferation of fibroblasts were impressively enhanced upon addition of poly-l-lysine. The modulation of the osteocytes has been achieved in various ways by applying advanced technologies such as 3D-plotting and electrospinning of biomimetic scaffolds, with optional addition of nano hydroxyapatite to the formulations. A wealth of biotechnological advances and know-how has permitted reaching outstanding results in crucial areas such as cranio-facial surgery, orthopedics and dentistry. It is mandatory to use scaffolds fully characterized in terms of porosity, pore size, swelling, wettability, compressive strength, and degree of acetylation, if the osteogenic differentiation of human mesenchymal stem cells is sought: in fact, the novel characteristics imparted by GEN-chitosan must be simultaneously of physico-chemical and cytological nature. Owing to their high standard, the scientific publications dated 2010–2015 have met the expectations of an interdisciplinary audience. PMID:26690453

Genipin-Crosslinked Chitosan Gels and Scaffolds for Tissue Engineering and Regeneration of Cartilage and Bone.

PubMed

Muzzarelli, Riccardo A A; El Mehtedi, Mohamad; Bottegoni, Carlo; Aquili, Alberto; Gigante, Antonio

2015-12-11

The present review article intends to direct attention to the technological advances made since 2009 in the area of genipin-crosslinked chitosan (GEN-chitosan) hydrogels. After a concise introduction on the well recognized characteristics of medical grade chitosan and food grade genipin, the properties of GEN-chitosan obtained with a safe, spontaneous and irreversible chemical reaction, and the quality assessment of the gels are reviewed. The antibacterial activity of GEN-chitosan has been well assessed in the treatment of gastric infections supported by Helicobacter pylori. Therapies based on chitosan alginate crosslinked with genipin include stem cell transplantation, and development of contraction free biomaterials suitable for cartilage engineering. Collagen, gelatin and other proteins have been associated to said hydrogels in view of the regeneration of the cartilage. Viability and proliferation of fibroblasts were impressively enhanced upon addition of poly-l-lysine. The modulation of the osteocytes has been achieved in various ways by applying advanced technologies such as 3D-plotting and electrospinning of biomimetic scaffolds, with optional addition of nano hydroxyapatite to the formulations. A wealth of biotechnological advances and know-how has permitted reaching outstanding results in crucial areas such as cranio-facial surgery, orthopedics and dentistry. It is mandatory to use scaffolds fully characterized in terms of porosity, pore size, swelling, wettability, compressive strength, and degree of acetylation, if the osteogenic differentiation of human mesenchymal stem cells is sought: in fact, the novel characteristics imparted by GEN-chitosan must be simultaneously of physico-chemical and cytological nature. Owing to their high standard, the scientific publications dated 2010-2015 have met the expectations of an interdisciplinary audience.

The effects of crosslinkers on physical, mechanical, and cytotoxic properties of gelatin sponge prepared via in-situ gas foaming method as a tissue engineering scaffold.

PubMed

Poursamar, S Ali; Lehner, Alexander N; Azami, Mahmoud; Ebrahimi-Barough, Somayeh; Samadikuchaksaraei, Ali; Antunes, A P M

2016-06-01

In this study porous gelatin scaffolds were prepared using in-situ gas foaming, and four crosslinking agents were used to determine a biocompatible and effective crosslinker that is suitable for such a method. Crosslinkers used in this study included: hexamethylene diisocyanate (HMDI), poly(ethylene glycol) diglycidyl ether (epoxy), glutaraldehyde (GTA), and genipin. The prepared porous structures were analyzed using Fourier Transform Infrared Spectroscopy (FT-IR), thermal and mechanical analysis as well as water absorption analysis. The microstructures of the prepared samples were analyzed using Scanning Electron Microscopy (SEM). The effects of the crosslinking agents were studied on the cytotoxicity of the porous structure indirectly using MTT analysis. The affinity of L929 mouse fibroblast cells for attachment on the scaffold surfaces was investigated by direct cell seeding and DAPI-staining technique. It was shown that while all of the studied crosslinking agents were capable of stabilizing prepared gelatin scaffolds, there are noticeable differences among physical and mechanical properties of samples based on the crosslinker type. Epoxy-crosslinked scaffolds showed a higher capacity for water absorption and more uniform microstructures than the rest of crosslinked samples, whereas genipin and GTA-crosslinked scaffolds demonstrated higher mechanical strength. Cytotoxicity analysis showed the superior biocompatibility of the naturally occurring genipin in comparison with other synthetic crosslinking agents, in particular relative to GTA-crosslinked samples. Copyright © 2016 Elsevier B.V. All rights reserved.

Nerve growth factor loaded heparin/chitosan scaffolds for accelerating peripheral nerve regeneration.

PubMed

Li, Guicai; Xiao, Qinzhi; Zhang, Luzhong; Zhao, Yahong; Yang, Yumin

2017-09-01

Artificial chitosan scaffolds have been widely investigated for peripheral nerve regeneration. However, the effect was not as good as that of autologous grafts and therefore could not meet the clinical requirement. In the present study, the nerve growth factor (NGF) loaded heparin/chitosan scaffolds were fabricated via electrostatic interaction for further improving nerve regeneration. The physicochemical properties including morphology, wettability and composition were measured. The heparin immobilization, NGF loading and release were quantitatively and qualitatively characterized, respectively. The effect of NGF loaded heparin/chitosan scaffolds on nerve regeneration was evaluated by Schwann cells culture for different periods. The results showed that the heparin immobilization and NGF loading did not cause the change of bulk properties of chitosan scaffolds except for morphology and wettability. The pre-immobilization of heparin in chitosan scaffolds could enhance the stability of subsequently loaded NGF. The NGF loaded heparin/chitosan scaffolds could obviously improve the attachment and proliferation of Schwann cells in vitro. More importantly, the NGF loaded heparin/chitosan scaffolds could effectively promote the morphology development of Schwann cells. The study may provide a useful experimental basis to design and develop artificial implants for peripheral nerve regeneration and other tissue regeneration. Copyright © 2017 Elsevier Ltd. All rights reserved.

Microfluidic Fabrication of Cell Adhesive Chitosan Microtubes

PubMed Central

Oh, Jonghyun; Kim, Keekyoung; Won, Sung Wook; Cha, Chaenyung; Gaharwar, Akhilesh; Selimović, Šeila; Bae, Hojae; Lee, Kwang Ho; Lee, Dong Hwan; Lee, Sang-Hoon; Khademhosseini, Ali

2013-01-01

Chitosan has been used as a scaffolding material in tissue engineering due to its mechanical properties and biocompatibility. With increased appreciation of the effect of micro- and nanoscale environments on cellular behavior, there is increased emphasis on generating microfabricated chitosan structures. Here we employed a microfluidic coaxial flow-focusing system to generate cell adhesive chitosan microtubes of controlled sizes by modifying the flow rates of a chitosan pre-polymer solution and phosphate buffered saline (PBS). The microtubes were extruded from a glass capillary with a 300 μm inner diameter. After ionic crosslinking with sodium tripolyphosphate (TPP), fabricated microtubes had inner and outer diameter ranges of 70-150 μm and 120-185 μm. Computational simulation validated the controlled size of microtubes and cell attachment. To enhance cell adhesiveness on the microtubes, we mixed gelatin with the chitosan pre-polymer solution and adjusted the pH values of the chitosan pre-polymer solution with gelatin and TPP. During the fabrication of microtubes, fibroblasts suspended in core PBS flow adhered to the inner surface of chitosan-gelatin microtubes. To achieve physiological pH values, we adjusted pH values of chiotsan pre-polymer solution and TPP. In particular, we were able to improve cell viability to 92% with pH values of 5.8 and 7.4 for chitosan and TPP solution respectively. Cell culturing for three days showed that the addition of the gelatin enhanced cell spreading and proliferation inside the chitosan-gelatin microtubes. The microfluidic fabrication method for ionically crosslinked chitosan microtubes at physiological pH can be compatible with a variety of cells and used as a versatile platform for microengineered tissue engineering. PMID:23355068

Electrospun oriented gelatin-hydroxyapatite fiber scaffolds for bone tissue engineering.

PubMed

Salifu, Ali A; Lekakou, Constantina; Labeed, Fatima H

2017-07-01

Tissue engineering of human fetal osteoblast cells was investigated on gelatin-hydroxyapatite (HA), crosslinked, electrospun oriented fiber scaffolds at the different HA concentrations of 0, 10, 20, and 25 wt % in the dry fibers and different fiber diameter, pore size and porosity of scaffolds. Rheological tests and proton nuclear magnetic resonance spectroscopy were conducted for all solutions used for electrospinning. It was found that 25 wt % HA-gelatin scaffolds electrospun at 20 kV led to the greatest cell attachment, cell proliferation and extracellular matrix (ECM) production while fiber orientation improved the mechanical properties, where crosslinked electrospun 25 wt % HA-gelatin fiber scaffolds yielded a Young's modulus in the range of 0.5-0.9 GPa and a tensile strength in the range of 4-10 MPa in the fiber direction for an applied voltage of 20-30 kV, respectively, in the electrospinning of scaffolds. Biological characterization of cell seeded scaffolds yielded the rate of cell growth and ECM (collagen and calcium) production by the cells as a function of time; it included cell seeding efficiency tests, alamar blue cell proliferation assay, alkaline phosphate (ALP) assay, collagen assay, calcium colorimetric assay, fluorescence microscopy for live and dead cells, and scanning electron microscopy for cell culture from 1 to 18 days. After 18 days, cells seeded and grown on the 25 wt % HA-gelatin scaffold, electrospun at 20 kV, reached production of collagen at 370 μg/L and calcium production at 0.8 mM. © 2016 Wiley Periodicals, Inc. J Biomed Mater Res Part A: 105A: 1911-1926, 2017. © 2017 Wiley Periodicals, Inc.

Investigating the potential of electrospun gelatin and collagen scaffolds for tissue engineering applications

NASA Astrophysics Data System (ADS)

Sisson, Kristin M.

Electrospinning provides an avenue to explore tissue engineering with the ability to produce nano- and micro-sized fibers in a non-woven construct with properties ideal for a tissue engineered scaffold including: small diameter fibers, which create a large surface to volume ratio, and an interconnected porous network that enables cell migration, good mechanical integrity and a three-dimensional structure. A tissue engineered scaffold also must be biocompatible, biodegradable, non-toxic and able to be sterilized. All of these requirements can be satisfied by choosing an appropriate polymer and solvent system for electrospinning. The main objective of this research is to create a non-toxic, flat, bone tissue engineered scaffold to place into a non-immune compromised mouse. The current bone tissue repair and replacement methodologies include using metal and ceramic replacements or autologous and autogenous bone grafts. Each of these has its own set of disadvantages. Autologous grafts are bone harvested in one location in a patient and used in another location. This procedure is expensive, often results in pain and infection at the replacement site, and the actual harvesting procedure can cause problems for the patient. Autogenous grafts are bone harvested in one patient and used in another patient. The shortcomings include low donor availability and the possibility of rejection of the implant. The other options include using metal and ceramics to create replacement bone. However, metals provide good mechanical stability but can fail due to infection and also have poor integration into natural tissue. Ceramics, on the other hand, are brittle and have very low tensile strength. The natural extracellular matrix (ECM) of bone consists mainly of collagen type I. Electrospun fiber diameters closely resemble those of the natural ECM of bone. Thus, electrospinning a natural polymer like collagen type I for bone tissue engineering could make sense. Applications for these

Chitosan/γ-poly(glutamic acid) scaffolds with surface-modified albumin, elastin and poly-l-lysine for cartilage tissue engineering.

PubMed

Kuo, Yung-Chih; Ku, Hao-Fu; Rajesh, Rajendiran

2017-09-01

Cartilage has limited ability to self-repair due to the absence of blood vessels and nerves. The application of biomaterial scaffolds using biomimetic extracellular matrix (ECM)-related polymers has become an effective approach to production of engineered cartilage. Chitosan/γ-poly(glutamic acid) (γ-PGA) scaffolds with different mass ratios were prepared using genipin as a cross-linker and a freeze-drying method, and their surfaces were modified with elastin, human serum albumin (HSA) and poly-l-lysine (PLL). The scaffolds were formed through a complex between NH 3 + of chitosan and COO - of γ-PGA, confirmed by Fourier transform infrared spectroscopy, and exhibited an interconnected porous morphology in field emission scanning electron microscopy analysis. The prepared chitosan/γ-PGA scaffolds, at a 3:1 ratio, obtained the required porosity (90%), pore size (≥100μm), mechanical strength (compressive strength>4MPa, Young's modulus>4MPa) and biodegradation (30-60%) for articular cartilage tissue engineering applications. Surface modification of the scaffolds showed positive indications with improved activity toward cell proliferation (deoxyribonucleic acid), cell adhesion and ECM (glycoaminoglycans and type II collagen) secretion of bovine knee chondrocytes compared with unmodified scaffolds. In caspase-3 detection, elastin had a higher inhibitory effect on chondrocyte apoptosis in vitro, followed by HSA, and then PLL. We concluded that utilizing chitosan/γ-PGA scaffolds with surface active biomolecules, including elastin, HSA and PLL, can effectively promote the growth of chondrocytes, secrete ECM and improve the regenerative ability of cartilaginous tissues. Copyright © 2017 Elsevier B.V. All rights reserved.

Strategies for neurotrophin-3 and chondroitinase ABC release from freeze-cast chitosan-alginate nerve-guidance scaffolds.

PubMed

Francis, Nicola L; Hunger, Philipp M; Donius, Amalie E; Wegst, Ulrike G K; Wheatley, Margaret A

2017-01-01

Freeze casting, or controlled unidirectional solidification, can be used to fabricate chitosan-alginate (C-A) scaffolds with highly aligned porosity that are suitable for use as nerve-guidance channels. To augment the guidance of growth across a spinal cord injury lesion, these scaffolds are now evaluated in vitro to assess their ability to release neurotrophin-3 (NT-3) and chondroitinase ABC (chABC) in a controlled manner. Protein-loaded microcapsules were incorporated into C-A scaffolds prior to freeze casting without affecting the original scaffold architecture. In vitro protein release was not significantly different when comparing protein loaded directly into the scaffolds with release from scaffolds containing incorporated microcapsules. NT-3 was released from the C-A scaffolds for 8 weeks in vitro, while chABC was released for up to 7 weeks. Low total percentages of protein released from the scaffolds over this time period were attributed to limitation of diffusion by the interpenetrating polymer network matrix of the scaffold walls. NT-3 and chABC released from the scaffolds retained bioactivity, as determined by a neurite outgrowth assay, and the promotion of neurite growth across an inhibitory barrier of chondroitin sulphate proteoglycans. This demonstrates the potential of these multifunctional scaffolds for enhancing axonal regeneration through growth-inhibiting glial scars via the sustained release of chABC and NT-3. Copyright © 2014 John Wiley & Sons, Ltd. Copyright © 2014 John Wiley & Sons, Ltd.

Biomimetic Engineering of Nanofibrous Gelatin Scaffolds with Noncollagenous Proteins for Enhanced Bone Regeneration

PubMed Central

Sun, Yao; Jiang, Yong; Liu, Qilin; Gao, Tian; Feng, Jian Q.; Dechow, Paul; D'Souza, Rena N.; Qin, Chunlin

2013-01-01

Biomimetic approaches are widely used in scaffolding designs to enhance tissue regeneration. In this study, we integrated noncollagenous proteins (NCPs) from bone extracellular matrix (ECM) with three-dimensional nanofibrous gelatin (NF-Gelatin) scaffolds to form an artificial matrix (NF-Gelatin-NCPs) mimicking both the nano-structured architecture and chemical composition of natural bone ECM. Through a chemical coupling process, the NCPs were evenly distributed over all the surfaces (inner and outer) of the NF-gelatin-NCPs. The in vitro study showed that the number of osteoblasts (MC3T3-E1) on the NF-Gelatin-NCPs was significantly higher than that on the NF-Gelatin after being cultured for 14 days. Both the alkaline phosphatase (ALP) activity and the expression of osteogenic genes (OPN, BSP, DMP1, CON, and Runx2) were significantly higher in the NF-Gelatin-NCPs than in the NF-Gelatin at 3 weeks. Von Kossa staining, backscattered scanning electron microscopy, and microcomputed tomography all revealed a higher amount of mineral deposition in the NF-Gelatin-NCPs than in the NF-Gelatin after in vitro culturing for 3 weeks. The in vivo calvarial defect study indicated that the NF-Gelatin-NCPs recruited more host cells to the defect and regenerated a higher amount of bone than the controls after implantation for 6 weeks. Immunohistochemical staining also showed high-level mineralization of the bone matrix in the NF-Gelatin-NCPs. Taken together, both the in vitro and in vivo results confirmed that the incorporation of NCPs onto the surfaces of the NF-Gelatin scaffold significantly enhanced osteogenesis and mineralization. Biomimetic engineering of the surfaces of the NF-Gelatin scaffold with NCPs, therefore, is a promising strategy to enhance bone regeneration. PMID:23469769

Characteristic study of chitosan addition in Tilapia (Oreochromis niloticus) bone based gelatin film

NASA Astrophysics Data System (ADS)

Atmaka, W.; Yudhistira, B.; Putro, M. I. S.

2018-03-01

Tilapia (Oreochromis niloticus) is one of popular fish species in Indonesia. The high number in tilapia’s production and export of tilapia resulting in the increase of bone fish waste. an attempt to decrease the amount of the aforementioned waste, the fish bones were turned into gelatine. The gelatine produced from this waste can be put to good use by turning it into edible film due to its high water resistance and low tensile strength value. However, in order to make a proper film, both the water resistance and the tensile strength value needs another appropriate additional biopolymer. In this case, the appropriate biopolymer needed both to form the film and to repair its characteristics is chitosan. The purpose of this research is to find out the effect of the chitosan addition on the tilapia bone based gelatine film. The research used several mixtures of gelatine (G) and chitosan (C) with the following ratio: G100:C0 (GC1), G75:C25 (GC2), G50:C50 (GC3), G25:C75 (GC4), G0:C100 (GC5). ANOVA results (P<0.05) shows that the addition of chitosan on the gelatine film affected its characteristics in thickness, solubility, tensile strength, elongation at break, Fourier Transform Infrared (FTIR), color a, and color b but no significant effects on the vapor permeability and color L. The best result is shown on GC2 with thickness 0.119 mm; solubility 74.95%; tensile strength 2.635 Mpa; elongation at break 68.26%; water vapor permeability 5.897 g/h m2 and FTIR. The parameters in GC2 shows good compatibility between the two biopolymers.

PCL and PCL-gelatin nanofibers as esophageal tissue scaffolds: optimization, characterization and cell-matrix interactions.

PubMed

Kuppan, Purushothaman; Sethuraman, Swaminathan; Krishnan, Uma Maheswari

2013-09-01

Nanofiber based scaffolds offer great promise in regeneration of various tissues including esophagus. Diseases of the esophagus such as malignancy and strictures require surgical intervention to repair the affected region using an appropriate substitute. Long gap esophageal atresia poses a clinical challenge to bridge the gap. In this study, nanofibrous scaffolds made of PCL and PCL-gelatin were fabricated through electrospinning. The average diameter of PCL and PCL-gelatin nanofibers were found to be 324 +/- 50 nm and 242 +/- 30 nm respectively. PCL-gelatin nanofibers was characterized using FTIR, DSC, UTM, Goniometer, suture retention strength and in vitro degradation and the results were compared with the PCL nanofibers. PCL nanofiber characterization results showed that it exhibited higher tensile strength, suture retention strength, contact angle and slower degradation when compared with the PCL-gelatin nanofibers. Further, the interaction of human esophageal epithelial cells with PCL and PCL-gelatin nanofibrous scaffold was determined by cell adhesion, proliferation and gene expression studies. Our results demonstrated that the epithelial cells adhered and proliferated well on both PCL and PCL-gelatin nanofibrous scaffolds and also exhibited the characteristic cobblestone morphology. Cell proliferation on PCL-gelatin nanofibrous scaffold was significantly higher than the PCL nanofibrous scaffold (*p <0.05). Therefore, these scaffolds could be explored as potential candidates for regeneration of functional esophagus.

Fabrication and characterization of DTBP-crosslinked chitosan scaffolds for skin tissue engineering.

PubMed

Adekogbe, Iyabo; Ghanem, Amyl

2005-12-01

Chitosan, the deacetylated derivative of chitin, is a promising scaffold material for skin tissue engineering applications. It is biocompatible and biodegradable, and the degradation products are resorbable. However, the rapid degradation of chitosan and its low mechanical strength are concerns that may limit its use. In this study, chitosan with 80%, 90% and 100% degree of deacetylation (DDA) was crosslinked with dimethyl 3-3, dithio bis' propionimidate (DTBP) and compared to uncrosslinked scaffolds. The scaffolds were characterized with respect to important tissue engineering properties. The tensile strength of scaffolds made from 100% DDA chitosan was significantly higher than for scaffolds made from 80% and 90% DDA chitosan. Crosslinking of scaffolds with DTBP increased the tensile strength. Crosslinking with DTBP had no significant effect on water vapour transmission rate (WVTR) or water absorption but had significant effect on the pore size and porosity of the samples. All samples showed a WVTR and pore size distribution suitable for skin tissue engineering; however, the water absorption and porosity were lower than the optimal values for skin tissue engineering. The biodegradation rate of scaffolds crosslinked with DTBP and glutaraldehyde (GTA) were reduced while no significant effect was observed in biodegradation of the samples made from 100% DDA chitosan whether crosslinked or uncrosslinked after 24 days of degradation.

Efficacy of chitosan and sodium alginate scaffolds for repair of spinal cord injury in rats

PubMed Central

Yao, Zi-ang; Chen, Feng-jia; Cui, Hong-li; Lin, Tong; Guo, Na; Wu, Hai-ge

2018-01-01

Spinal cord injury results in the loss of motor and sensory pathways and spontaneous regeneration of adult mammalian spinal cord neurons is limited. Chitosan and sodium alginate have good biocompatibility, biodegradability, and are suitable to assist the recovery of damaged tissues, such as skin, bone and nerve. Chitosan scaffolds, sodium alginate scaffolds and chitosan-sodium alginate scaffolds were separately transplanted into rats with spinal cord hemisection. Basso-Beattie-Bresnahan locomotor rating scale scores and electrophysiological results showed that chitosan scaffolds promoted recovery of locomotor capacity and nerve transduction of the experimental rats. Sixty days after surgery, chitosan scaffolds retained the original shape of the spinal cord. Compared with sodium alginate scaffolds- and chitosan-sodium alginate scaffolds-transplanted rats, more neurofilament-H-immunoreactive cells (regenerating nerve fibers) and less glial fibrillary acidic protein-immunoreactive cells (astrocytic scar tissue) were observed at the injury site of experimental rats in chitosan scaffold-transplanted rats. Due to the fast degradation rate of sodium alginate, sodium alginate scaffolds and composite material scaffolds did not have a supporting and bridging effect on the damaged tissue. Above all, compared with sodium alginate and composite material scaffolds, chitosan had better biocompatibility, could promote the regeneration of nerve fibers and prevent the formation of scar tissue, and as such, is more suitable to help the repair of spinal cord injury. PMID:29623937

[Biomimetic nanohydroxyapatite/gelatin composite material preparation and in vitro study].

PubMed

Li, Siriguleng; Hu, Xiaowen

2014-09-01

To prepare nHA/gelatin porous scaffold and to evaluate its physical and chemical properties and biocompatibility. We used nano-powders of HA and gelatin to prepare 3D porous composite scaffold by freeze-drying technique, and used scanning electron microscope, fourier transform infrared spectroscopy and universal testing machine to characterize the composite material. Osteoblasts were primarily cultured, and the third-passage osteoblasts were co-cultured with the composite material. The cell adhesion and morphology were examined under scanning electron microscope. The cell viability analysis was performed by MTT assay, and the alkaline phosphatase activity was measured with alkaline phosphatase kit. Scanning electron microscope showed that the scaffold possessed a 3-dimensional interconnected homogenous porous structure with pore sizes ranging from 150 to 400 μm. Fourier transform infrared spectroscopy showed that the composite material had a strong chemical bond between the inorganic phase and organic phase. The scaffold presented the compressive strength of (3.28 ± 0.51) MPa and porosities of (80.6 ± 4.1)%. Composite materials showed features of had good biocompatibility. Mouse osteoblasts were well adhered and spread on the materials. The grade of the cell toxicity ranged from I to II. On the 5th and 7th day the proliferative rate of osteoblasts on scaffolds in the composite materials was significantly higher than that in the control group. The activity of alkaline phosphatase was obviously higher than that in the control group on Day 1 and 3. Nano-hydroxyapatite and gelatin in certain proportions and under certain conditions can be prepared into a composite biomimetic porous scaffolds with high porosity and three-dimensional structure using freeze-drying method. The scaffold shows good biocompatibility with mouse osteoblasts and may be a novel scaffolds for bone tissue engineering.

Effect of strontium addition and chitosan concentration variation on cytotoxicity of chitosan-alginate-carbonate apatite based bone scaffold

NASA Astrophysics Data System (ADS)

Perkasa, Rilis Eka; Umniati, B. Sri; Sunendar, Bambang

2017-09-01

Bone scaffold is one of the most important component in bone tissue engineering. Basically, bone scaffold is a biocompatible structure designed to replace broken bone tissue temporarily. Unlike conventional bone replacements, an advanced bone scaffold should be bioactive (e.g: supporting bone growth) and biodegradable as new bone tissue grow, while retain its mechanical properties similarity with bone. It is also possible to add more bioactive substrates to bone scaffold to further support its performance. One of the substrate is strontium, an element that could improve the ability of the bone to repair itself. However, it must be noted that excessive consumption of strontium could lead to toxicity and diseases, such as osteomalacia and hypocalcemia. This research aimed to investigate the effect of strontium addition to the cytotoxic property of chitosan-alginate-carbonate apatite bone scaffold. The amount of strontium added to the bone scaffold was 5% molar of the carbonate apatite content. As a control, bone scaffold without stronsium (0% molar) were also made. The effect of chitosan concentration variation on the cytotoxicity were also observed, where the concentration varies on 1% and 3% w/v of chitosan solution. The results showed an optimum result on bone scaffold sample with 5% molar of strontium and 3% chitosan, where 87.67% cells in the performed MTS-Assay cytotoxicity testing survived. This showed that the use of up to 5% molar addition of strontium and 3% chitosan could enhance the survivability of the cell.

Development of a Multi-Functional Biopolymer Scaffold for Neural Tissue Engineering

NASA Astrophysics Data System (ADS)

Francis, Nicola Louise

Spinal cord injury (SCI) affects approximately 270,000 people in the U.S., with approximately 12,000 new cases occurring every year. Several strategies have been investigated to enhance axonal regeneration after SCI, however, the resulting growth can be random and disorganized. Bioengineered scaffolds provide a physical substrate for the guidance of regenerating axons towards their targets, and can be produced by freeze casting. This technique involves the controlled directional solidification of an aqueous solution or suspension, resulting in a linearly aligned porous structure caused by ice templating. In this thesis, freeze casting was used to create novel porous chitosan-alginate (C/A) scaffolds with longitudinally aligned channels and a compressive modulus (5.08 ± 0.61 kPa) comparable to that of native spinal cord tissue. These C/A scaffolds supported the viability, attachment, and directionally oriented growth of chick dorsal root ganglia (DRG) neurites in vitro, with surface adsorptions of polycations and laminin promoting significantly longer neurite growth than the uncoated scaffolds (p<0.001). In order to integrate therapeutic biomolecules within the scaffolds for sustained release, alginate and chitosan microcapsules produced by spray drying were used to encapsulate brain-derived neurotrophic factor (BDNF) and neurotrophin-3 (NT-3), and the enzyme chondroitinase ABC (chABC) prior to scaffold incorporation. BDNF and NT-3 were released from the C/A scaffolds in a sustained manner for 8 weeks in vitro, while chABC was released for up to 35 days. However, up to 85% of biomolecules emained entrapped within the scaffold walls, due to limitation of diffusion by the scaffold wall mesh size. Release of bioactive chABC and neurotrophins from the multifunctional scaffolds promoted the growth of DRG neurites through an in vitro barrier of chondroitin sulfate proteoglycans, a main inhibitory component of the growth-inhibiting glial scar in the injured spinal cord

3D Porous Chitosan-Alginate Scaffolds as an In Vitro Model for Evaluating Nanoparticle-Mediated Tumor Targeting and Gene Delivery to Prostate Cancer.

PubMed

Wang, Kui; Kievit, Forrest M; Florczyk, Stephen J; Stephen, Zachary R; Zhang, Miqin

2015-10-12

Cationic nanoparticles (NPs) for targeted gene delivery are conventionally evaluated using 2D in vitro cultures. However, this does not translate well to corresponding in vivo studies because of the marked difference in NP behavior in the presence of the tumor microenvironment. In this study, we investigated whether prostate cancer (PCa) cells cultured in three-dimensional (3D) chitosan-alginate (CA) porous scaffolds could model cationic NP-mediated gene targeted delivery to tumors in vitro. We assessed in vitro tumor cell proliferation, formation of tumor spheroids, and expression of marker genes that promote tumor malignancy in CA scaffolds. The efficacy of NP-targeted gene delivery was evaluated in PCa cells in 2D cultures, PCa tumor spheroids grown in CA scaffolds, and PCa tumors in a mouse TRAMP-C2 flank tumor model. PCa cells cultured in CA scaffolds grew into tumor spheroids and displayed characteristics of higher malignancy as compared to those in 2D cultures. Significantly, targeted gene delivery was only observed in cells cultured in CA scaffolds, whereas cells cultured on 2D plates showed no difference in gene delivery between targeted and nontarget control NPs. In vivo NP evaluation confirmed targeted gene delivery, indicating that only CA scaffolds correctly modeled NP-mediated targeted delivery in vivo. These findings suggest that CA scaffolds serve as a better in vitro platform than 2D cultures for evaluation of NP-mediated targeted gene delivery to PCa.

Chitosan-collagen scaffolds with nano/microfibrous architecture for skin tissue engineering.

PubMed

Sarkar, Soumi Dey; Farrugia, Brooke L; Dargaville, Tim R; Dhara, Santanu

2013-12-01

In this study, a hierarchical nano/microfibrous chitosan/collagen scaffold that approximates structural and functional attributes of native extracellular matrix has been developed for applicability in skin tissue engineering. Scaffolds were produced by electrospinning of chitosan followed by imbibing of collagen solution, freeze-drying, and subsequent cross-linking of two polymers. Scanning electron microscopy showed formation of layered scaffolds with nano/microfibrous architechture. Physicochemical properties of scaffolds including tensile strength, swelling behavior, and biodegradability were found satisfactory for intended application. 3T3 fibroblasts and HaCaT keratinocytes showed good in vitro cellular response on scaffolds thereby indicating the matrices, cytocompatible nature. Scaffolds tested in an ex vivo human skin equivalent wound model, as a preliminary alternative to animal testing, showed keratinocyte migration and wound re-epithelization-a prerequisite for healing and regeneration. Taken together, the herein proposed chitosan/collagen scaffold, shows good potential for skin tissue engineering. Copyright © 2013 Wiley Periodicals, Inc., a Wiley Company.

Anti-infective efficacy, cytocompatibility and biocompatibility of a 3D-printed osteoconductive composite scaffold functionalized with quaternized chitosan.

PubMed

Yang, Ying; Yang, Shengbing; Wang, Yugang; Yu, Zhifeng; Ao, Haiyong; Zhang, Hongbo; Qin, Ling; Guillaume, Olivier; Eglin, David; Richards, R Geoff; Tang, Tingting

2016-12-01

Contaminated or infected bone defects remain serious challenges in clinical trauma and orthopaedics, and a bone substitute with both osteoconductivity and antibacterial properties represents an improvement for treatment strategy. In this study, quaternized chitosan (hydroxypropyltrimethyl ammonium chloride chitosan, HACC) was grafted to 3D-printed scaffolds composed of polylactide-co-glycolide (PLGA) and hydroxyapatite (HA), in order to design bone engineering scaffolds endowed with antibacterial and osteoconductive properties. We found that both the PLGA/HA/HACC and PLGA/HACC composite scaffolds decreased bacterial adhesion and biofilm formation under in vitro and in vivo conditions. Additionally, ATP leakage assay indicated that immobilizing HACC on the scaffolds could effectively disrupt microbial membranes. Using human bone marrow-derived mesenchymal stem cells (hBMSCs), we demonstrated that HA incorporated scaffolds, including PLGA/HA and PLGA/HA/HACC, favoured cell attachment, proliferation, spreading and osteogenic differentiation compared to HA-free PLGA or PLGA/HACC scaffolds. Finally, an in vivo biocompatibility assay conducted on rats, showed that HA incorporated scaffolds (including PLGA/HA and PLGA/HA/HACC scaffolds) exhibited good neovascularization and tissue integration. Taken together, our findings support the approach for developing porous PLGA/HA/HACC composite scaffold with potential clinical application in the treatment of infected bone. Although plenty of conductive scaffold biomaterials have been exploited to improve bone regeneration under infection, potential tissue toxicity under high concentration and antibiotic-resistance are their main deficiencies. This study indicated that HACC-grafted PLGA/HA composite scaffold prepared using an innovative 3D-printing technique and covalent grafting strategy showed significantly enhanced antibacterial activities, especially against the antibiotic-resistant strains, together with good osteogenic

Enhancement of stem cell differentiation to osteogenic lineage on hydroxyapatite-coated hybrid PLGA/gelatin nanofiber scaffolds.

PubMed

Sanaei-Rad, Parisa; Jafarzadeh Kashi, Tahereh-Sadat; Seyedjafari, Ehsan; Soleimani, Masoud

2016-11-01

A combination of polymeric materials and bioceramics has recently received a great deal of attention for bone tissue engineering applications. In the present study, hybrid nanofibrous scaffolds were fabricated from PLGA and gelatin via electrospinning and then were coated with hydroxyapatite (HA). They were then characterized and used in stem cell culture studies for the evaluation of their biological behavior and osteogenic differentiation in vitro. This study showed that all PLGA, hybrid PLGA/gelatin and HA-PLGA/gelatin scaffolds were composed of ultrafine fibers with smooth morphology and interconnected pores. The MTT assay confirmed that the scaffolds can support the attachment and proliferation of stem cells. During osteogenic differentiation, bone-related gene expression, ALP activity and biomineralization on HA-PLGA/gelatin scaffolds were higher than those observed on other scaffolds and TCPS. PLGA/gelatin electrospun scaffolds also showed higher values of these markers than TCPS. Taking together, it was shown that nanofibrous structure enhanced osteogenic differentiation of adipose-tissue derived stem cells. Furthermore, surface-coated HA stimulated the effect of nanofibers on the commitment of stem cells toward osteolineage. In conclusion, HA-PLGA/gelatin electrospun scaffolds were demonstrated to have significant potential for bone tissue engineering applications. Copyright © 2016 International Alliance for Biological Standardization. Published by Elsevier Ltd. All rights reserved.

Chitosan based metallic nanocomposite scaffolds as antimicrobial wound dressings.

PubMed

Mohandas, Annapoorna; Deepthi, S; Biswas, Raja; Jayakumar, R

2018-09-01

Chitosan based nanocomposite scaffolds have attracted wider applications in medicine, in the area of drug delivery, tissue engineering and wound healing. Chitosan matrix incorporated with nanometallic components has immense potential in the area of wound dressings due to its antimicrobial properties. This review focuses on the different combinations of Chitosan metal nanocomposites such as Chitosan/nAg, Chitosan/nAu, Chitosan/nCu, Chitosan/nZnO and Chitosan/nTiO 2 towards enhancement of healing or infection control with special reference to the antimicrobial mechanism of action and toxicity.

Biologically active and biomimetic dual gelatin scaffolds for tissue engineering.

PubMed

Sánchez, P; Pedraz, J L; Orive, G

2017-05-01

We have designed, developed and optimized Genipin cross-linked 3D gelatin scaffolds that were biologically active and biomimetic, show a dual activity both for growth factor and cell delivery. Type B gelatin powder was dissolved in DI water. 100mg of genipin was dissolved in 10ml of DI water. Three genipin concentrations were prepared: 0.1%, 0.2% and 0.3% (w/v). Solutions were mixed at 40°C and under stirring and then left crosslinking for 72h. Scaffolds were obtained by punching 8 mm-cylinders into ethanol 70% solution for 10min and then freeze-drying. Scaffolds were biologically, biomechanically and morphologically evaluated. Cell adhesion and morphology of D1-Mesenchymal stem cells (MSCs) and L-929 fibroblast was studied. Vascular endothelial grwoth factor (VEGF) and Sonic hedgehog (SHH) were used as model proteins. Swelling ratio increased and younǵs module decreased along with the concentration of genipin. All scaffolds were biocompatible according to the toxicity test. MSC and L-929 cell adhesion improved in 0.2% of genipin, obtaining better results with MSCs. VEGF and SHH were released from the gels. This preliminary study suggest that the biologically active and dual gelatin scaffolds may be used for tissue engineering approaches like bone regeneration. Copyright © 2017 Elsevier B.V. All rights reserved.

A review on chitosan centred scaffolds and their applications in tissue engineering.

PubMed

Ahmed, Shakeel; Annu; Sheikh, Javed; Ali, Akbar

2018-05-03

The diversity and availability of biopolymer and increased clinical demand for safe scaffolds lead to an increased interest in fabricating scaffolds in order to achieve fruitful progress in tissue engineering. Due to biocompatibility, biodegradability, inherent antimicrobial character, chitosan has drawn ample consideration in recent years. Chitosan is a biopolymer obtained by de-acetylation of chitin extracted from shells of crustaceans and fungi. Due to the presence of reactive functionality in the molecular chain chitosan can be modified either chemically or physically to fabricate the tailor-made scaffolds having desired properties for tissue engineering centered applications. In this review chitosan, its properties and role either virgin, chemically or physically modified, 2D or 3D scaffolds for tissue engineering application have been highlighted. Copyright © 2017. Published by Elsevier B.V.

Architectural and Mechanical Cues Direct Mesenchymal Stem Cell Interactions with Crosslinked Gelatin Scaffolds

PubMed Central

McAndrews, Kathleen M.; Kim, Min Jeong; Lam, Tuyet Y.; McGrail, Daniel J.

2014-01-01

Naturally derived biomaterials have emerged as modulators of cell function and tissue substitutes. Here, we developed crosslinked glutaraldehyde (GTA) scaffolds for the expansion and differentiation of mesenchymal stem cells (MSCs). The mechanical and architectural properties of the scaffolds were altered by varying the concentration of gelatin and GTA. Higher GTA concentrations were associated with an increase in more confined pores and osteogenic differentiation. In addition, myogenic potential varied with crosslinking degree, although bulk mechanical properties were unaltered. Correlation analysis revealed that ALP activity of differentiated MSCs on higher gelatin concentration scaffolds was dependent on traditional effectors, including environment elasticity and spread area. In contrast, the differentiation capacity of cells cultured on lower gelatin concentration scaffolds did not correlate with these factors, instead it was dependent on the hydrated pore structure. These results suggest that scaffold composition can determine what factors direct differentiation and may have critical implications for biomaterial design. PMID:24873687

Biodegradable and biocompatible high elastic chitosan scaffold is cell-friendly both in vitro and in vivo

PubMed Central

Lin, Xianfeng; Yang, Lin; Wang, Qiang; Wang, Zhengke; Shan, Zhi; Li, Shengyun; Wang, Jiying; Fan, Shunwu; Hu, Qiaoling

2017-01-01

Biodegradable and biocompatible macromolecule chitosan has been favored for a variety of clinical applications. We reported herein the fabrication of a novel chitosan scaffold with high elasticity. This scaffold can be easily compressed and thus enable the insertion of such scaffold into surgical lesions during minimal invasive surgeries. In addition, this novel scaffold can restore its shape when released. We evidenced that this high elastic scaffold has better biocompatibility than traditional chitosan scaffold. Therefore, this new chitosan material might lead to the manufacture of a variety of novel biodegradable biomedical materials and devices. PMID:28103580

Development of nanocomposite scaffolds based on TiO2 doped in grafted chitosan/hydroxyapatite by freeze drying method and evaluation of biocompatibility.

PubMed

Abd-Khorsand, Saber; Saber-Samandari, Samaneh; Saber-Samandari, Saeed

2017-08-01

Porous three-dimensional scaffolds with potential for application as cancellous bone graft substitutes were prepared using the freeze-drying technique. Hydroxyapatite with different weight ratio was embedded in the network of poly(acrylic acid) grafted chitosan accompanied by using TiO 2 as an auxiliary component to fabricate porous nanocomposite bone scaffolds. Fourier transform infrared spectroscopy, scanning electron microscopy, energy-dispersive X-ray spectroscopy, and X-ray diffraction analysis and mechanical tests were carried out to characterize the prepared scaffolds. These scaffolds showed well-controlled and interconnected porous structures. The pore size and porosity of the scaffolds could be effectively modulated by selecting appropriate amounts of hydroxyapatite. The results obtained from mechanical properties measurements indicated that the scaffolds could basically retain their strength in their dry state and have adequate mechanical properties close to those of cancellous bone. The swelling behavior of the scaffolds was also examined in both water and phosphate buffer saline solution. The cytotoxicity of the scaffold was determined by MTT assays on human fibroblast gum (HuGu) cells for 24, 48 and 72h. In conclusion, this investigation demonstrates that the fabricated nanocomposite scaffolds are suitable for bone tissue engineering. Copyright © 2017 Elsevier B.V. All rights reserved.

Controlled release of an extract of Calendula officinalis flowers from a system based on the incorporation of gelatin-collagen microparticles into collagen I scaffolds: design and in vitro performance.

PubMed

Jiménez, Ronald A; Millán, Diana; Suesca, Edward; Sosnik, Alejandro; Fontanilla, Marta R

2015-06-01

Aiming to develop biological skin dresses with improved performance in the treatment of skin wounds, acellular collagen I scaffolds were modified with polymeric microparticles and the subsequent loading of a hydroglycolic extract of Calendula officinalis flowers. Microparticles made of gelatin-collagen were produced by a water-in-oil emulsion/cross-linking method. Thereafter, these microparticles were mixed with collagen suspensions at three increasing concentrations and the resulting mixtures lyophilized to make microparticle-loaded porous collagen scaffolds. Resistance to enzymatic degradation, ability to associate with the C. officinalis extract, and the extract release profile of the three gelatin-collagen microparticle-scaffold prototypes were assessed in vitro and compared to collagen scaffolds without microparticles used as control. Data indicated that the incorporation of gelatin-collagen microparticles increased the resistance of the scaffolds to in vitro enzymatic degradation, as well as their association with the C. officinalis flower extract. In addition, a sharp decrease in cytotoxicity, as well as more prolonged release of the extract, was attained. Overall results support the potential of these systems to develop innovative dermal substitutes with improved features. Furthermore, the gelatin-collagen mixture represents a low-cost and scalable alternative with high clinical transferability, especially appealing in developing countries.

Development of chitosan/gelatin/keratin composite containing hydrocortisone sodium succinate as a buccal mucoadhesive patch to treat desquamative gingivitis.

PubMed

Davoudi, Zahra; Rabiee, Mohammad; Houshmand, Behzad; Eslahi, Niloofar; Khoshroo, Kimia; Rasoulianboroujeni, Morteza; Tahriri, Mohammadreza; Tayebi, Lobat

2018-01-01

The aim of this research was to develop chitosan/gelatin/keratin composite containing hydrocortisone sodium succinate as a buccal mucoadhesive patch to treat desquamative gingivitis, which was fabricated through an environmental friendly process. Mucoadhesive films increase the advantage of higher efficiency and drug localization in the affected region. In this research, mucoadhesive films, for the release of hydrocortisone sodium succinate, were prepared using different ratios of chitosan, gelatin and keratin. In the first step, chitosan and gelatin proportions were optimized after evaluating the mechanical properties, swelling capacity, water uptake, stability, and biodegradation of the films. Then, keratin was added at different percentages to the optimum composite of chitosan and gelatin together with the drug. The results of surface pH showed that none of the samples were harmful to the buccal cavity. FTIR analysis confirmed the influence of keratin on the structure of the composite. The presence of a higher amount of keratin in the composite films resulted in high mechanical, mucoadhesive properties and stability, low water uptake and biodegradation in phosphate buffer saline (pH = 7.4) containing 10 4  U/ml lysozyme. The release profile of the films ascertained that keratin is a rate controller in the release of the hydrocortisone sodium succinate. Finally, chitosan/gelatin/keratin composite containing hydrocortisone sodium succinate can be employed in dental applications.

Fabrication of porous scaffolds with decellularized cartilage matrix for tissue engineering application.

PubMed

Nasiri, Bita; Mashayekhan, Shohreh

2017-07-01

Due to the avascular nature of articular cartilage, damaged tissue has little capacity for spontaneous healing. Three-dimensional scaffolds have potential for use in tissue engineering approach for cartilage repair. In this study, bovine cartilage tissue was decellularized and chemically crosslinked hybrid chitosan/extracellular matrix (ECM) scaffolds were fabricated with different ECM weight ratios by simple freeze drying method. Various properties of chitosan/ECM scaffolds such as microstructure, mechanical strength, swelling ratio, and biodegradability rate were investigated to confirm improved structural and biological characteristics of chitosan scaffolds in the presence of ECM. The results indicated that by introducing ECM to chitosan, pore sizes in scaffolds with 1% and 2% ECM decreased and thus the mechanical properties were improved. The presence of ECM in the same scaffolds also improved the swelling ratio and biodegradation rate in the hybrid scaffolds. MTT cytotoxicity assays performed on chondrocyte cells cultured on chitosan/ECM scaffolds having various amounts of ECM showed that the greatest cell attachment belongs to the sample with intermediate ECM content (2% ECM). Overall, it can be concluded from all obtained results that the prepared scaffold with intermediate concentration of ECM could be a proper candidate for use in cartilage tissue engineering. Copyright © 2017 International Alliance for Biological Standardization. Published by Elsevier Ltd. All rights reserved.

Biocompatibility Assessment of Novel Collagen-Sericin Scaffolds Improved with Hyaluronic Acid and Chondroitin Sulfate for Cartilage Regeneration

PubMed Central

Gălăţeanu, Bianca; Albu, Mădălina

2013-01-01

Cartilage tissue engineering (CTE) applications are focused towards the use of implantable biohybrids consisting of biodegradable scaffolds combined with in vitro cultured cells. Hyaluronic acid (HA) and chondroitin sulfate (CS) were identified as the most potent prochondrogenic factors used to design new biomaterials for CTE, while human adipose-derived stem cells (ASCs) were proved to display high chondrogenic potential. In this context, our aim was not only to build novel 3D porous scaffolds based on natural compounds but also to evaluate their in vitro biological performances. Therefore, for prospective CTE, collagen-sericin (Coll-SS) scaffolds improved with HA (5% or 10%) and CS (5% or 10%) were used as temporary physical supports for ASCs and were analyzed in terms of structural, thermal, morphological, and swelling properties and cytotoxic potential. To complete biocompatibility data, ASCs viability and proliferation potential were also assessed. Our studies revealed that Coll-SS hydrogels improved with 10% HA and 5% CS displayed the best biological performances in terms of cell viability, proliferation, morphology, and distribution. Thus, further work will address a novel 3D system including both HA 10% and CS 5% glycoproteins, which will probably be exposed to prochondrogenic conditions in order to assess its potential use in CTE applications. PMID:24308001

Electrospun polycaprolactone/gelatin composites with enhanced cell-matrix interactions as blood vessel endothelial layer scaffolds.

PubMed

Jiang, Yong-Chao; Jiang, Lin; Huang, An; Wang, Xiao-Feng; Li, Qian; Turng, Lih-Sheng

2017-02-01

During the fabrication of tissue engineering scaffolds and subsequent tissue regeneration, surface bioactivity is vital for cell adhesion, spreading, and proliferation, especially for endothelium dysfunction repair. In this paper, synthetic polymer polycaprolactone (PCL) was blended with natural polymer gelatin at four different weight ratios followed by crosslinking (i.e., 100:0, 70:30, 50:50, 30:70, labeled as PCL-C, P7G3-C, P5G5-C, and P3G7-C) to impart enhanced bioactivity and tunable mechanical properties. The PCL/gelatin blends were first dissolved in 2,2,2-trifluroethanol (TFE) and supplementary acetic acid (1% relative to TFE) solvent, electrospun, and then cross-linked to produce PBS-proof fibrous scaffolds. Scanning electron micrographs (SEM) indicated that fibers of each sample were smooth and homogeneous, with the fiber diameters increasing from 1.01±0.51μm to 1.61±0.46μm as the content of gelatin increased. While thermal resistance and crystallization of the blends were affected by the presence of gelatin, as reflected by differential scanning calorimetry (DSC) results, water contact angle (WCA) tests confirmed that the scaffold surfaces became more hydrophilic. Tensile tests showed that PCL-C and P7G3-C scaffolds had mechanical properties comparable to those of human coronary arteries. As for cytocompatibility, skeleton staining images showed that human mesenchymal stem cells (hMSCs) had more favorable binding sites on PCL/gelatin scaffolds than those on PCL scaffolds. Cell proliferation assays revealed that P7G3-C scaffolds could support the most number of hMSCs. The results of this study demonstrated the enhanced cell-matrix interactions and potential use of electrospun PCL/gelatin scaffolds in the tissue engineering field, especially in wound dressings and endothelium regeneration. Copyright © 2016 Elsevier B.V. All rights reserved.

Injectable and microporous scaffold of densely-packed, growth factor-encapsulating chitosan microgels.

PubMed

Riederer, Michael S; Requist, Brennan D; Payne, Karin A; Way, J Douglas; Krebs, Melissa D

2016-11-05

In this work, an emulsion crosslinking method was developed to produce chitosan-genipin microgels which acted as an injectable and microporous scaffold. Chitosan was characterized with respect to pH by light scattering and aqueous titration. Microgels were characterized with swelling, light scattering, and rheometry of densely-packed microgel solutions. The results suggest that as chitosan becomes increasingly deprotonated above the pKa, repulsive forces diminish and intermolecular attractions cause pH-responsive chain aggregation; leading to microgel-microgel aggregation as well. The microgels with the most chitosan and least cross-linker showed the highest yield stress and a storage modulus of 16kPa when condensed as a microgel paste at pH 7.4. Two oppositely-charged growth factors could be encapsulated into the microgels and endothelial cells were able to proliferate into the 3D microgel scaffold. This work motivates further research on the applications of the chitosan microgel scaffold as an injectable and microporous scaffold in regenerative medicine. Copyright © 2016 Elsevier Ltd. All rights reserved.

Chitosan scaffold as an alternative adsorbent for the removal of hazardous food dyes from aqueous solutions.

PubMed

Esquerdo, V M; Cadaval, T R S; Dotto, G L; Pinto, L A A

2014-06-15

The dye adsorption with chitosan is considered an eco-friendly alternative technology in relation to the existing water treatment technologies. However, the application of chitosan for dyes removal is limited, due to its low surface area and porosity. Then we prepared a chitosan scaffold with a megaporous structure as an alternative adsorbent to remove food dyes from solutions. The chitosan scaffold was characterized by infrared spectroscopy, scanning electron microscopy and structural characteristics. The potential of chitosan scaffold to remove five food dyes from solutions was investigated by equilibrium isotherms and thermodynamic study. The scaffold-dyes interactions were elucidated, and desorption studies were carried out. The chitosan scaffold presented pore sizes from 50 to 200 μm, porosity of 92.2±1.2% and specific surface area of 1135±2 m(2) g(-1). The two-step Langmuir model was suitable to represent the equilibrium data. The adsorption was spontaneous, favorable, exothermic and enthalpy-controlled process. Electrostatic interactions occurred between chitosan scaffold and dyes. Desorption was possible with NaOH solution (0.10 mol L(-1)). The chitosan megaporous scaffold showed good structural characteristics and high adsorption capacities (788-3316 mg g(-1)). Copyright © 2014 Elsevier Inc. All rights reserved.

The Influence of Chitosan Concentration on Synthesis of Hydroxyapatite Scaffold on Crystallinity and Surface Morphology

NASA Astrophysics Data System (ADS)

Yudyanto; Hartatiek; Prasasti, R. W.; Hariyanto, Y. A.; Hidayat, N.

2018-05-01

Hydroxyapatite (HA) is a bioceramic material having a chemical formula (Ca10(PO4)6(OH)2) similar to the chemical structure of bone and hard tissue in humans. Recently, HA-scaffold has been intensively developed by many researchers due to its potential application in dealing with tissue injured. The implantation of HA-scaffold into bone defect aims to help and stimulate the growth of new bone tissue. Crystallinity and microstructure are properties that need to be considered to synthesis HA scaffold. Although, HA is biocompatible and osteoconductive but low biodegradable, to solve these problems added chitosan. Chitosan is a biopolymeric material with specific properties, in terms of biocompatible, non-toxic, osteoconductive, biodegradable, and not carcinogenc. In addition, a natural polymeric chitosan has similarities with the extracellular matrix, in terms of good biological performance and inherent cellular interactions. In this study, HA-scaffold was synthesized using Ca(OH)2 as the raw material of natural calcite mineral, H3PO4, and a solid polyurethane polymer (sponge) as forming of pores by sol-gel method. The addition of chitosan concentration of 0 %, 2 % and 3 % in hydroxyapatite scaffold evaluated its influences on crystallinity and surface morphology. The phase, crystallinity and crystal size are evaluated by XRD. Functional groups in HA scaffold and HA compounds were evaluated with FTIR. The results showed that HA has Ca/P ratio of 1.64. The addition of chitosan concentration caused the decrease of crystallinity and increased the pore size. Meanwhile the crystal sizes were obtained: 49.99 nm (HA), 54.37 nm (HA-scaffold without chitosan), 54.98 nm (HA-scaffold with 2% chitosan), and 40.44 nm (HA-scaffold with 3 % chitosan).

Bone repair by periodontal ligament stem cellseeded nanohydroxyapatite-chitosan scaffold

PubMed Central

Ge, Shaohua; Zhao, Ning; Wang, Lu; Yu, Meijiao; Liu, Hong; Song, Aimei; Huang, Jing; Wang, Guancong; Yang, Pishan

2012-01-01

Background A nanohydroxyapatite-coated chitosan scaffold has been developed in recent years, but the effect of this composite scaffold on the viability and differentiation of periodontal ligament stem cells (PDLSCs) and bone repair is still unknown. This study explored the behavior of PDLSCs on a new nanohydroxyapatite-coated genipin-chitosan conjunction scaffold (HGCCS) in vitro as compared with an uncoated genipin-chitosan framework, and evaluated the effect of PDLSC-seeded HGCCS on bone repair in vivo. Methods Human PDLSCs were cultured and identified, seeded on a HGCCS and on a genipin-chitosan framework, and assessed by scanning electron microscopy, confocal laser scanning microscopy, MTT, alkaline phosphatase activity, and quantitative real-time polymerase chain reaction at different time intervals. Moreover, PDLSC-seeded scaffolds were used in a rat calvarial defect model, and new bone formation was assessed by hematoxylin and eosin staining at 12 weeks postoperatively. Results PDLSCs were clonogenic and positive for STRO-1. They had the capacity to undergo osteogenic and adipogenic differentiation in vitro. When seeded on HGCCS, PDLSCs exhibited significantly greater viability, alkaline phosphatase activity, and upregulated the bone-related markers, bone sialoprotein, osteopontin, and osteocalcin to a greater extent compared with PDLSCs seeded on the genipin-chitosan framework. The use of PDLSC-seeded HGCCS promoted calvarial bone repair. Conclusion This study demonstrates the potential of HGCCS combined with PDLSCs as a promising tool for bone regeneration. PMID:23091383

Hybrid Macro-Porous Titanium Ornamented by Degradable 3D Gel/nHA Micro-Scaffolds for Bone Tissue Regeneration

PubMed Central

Yin, Bo; Ma, Pei; Chen, Jun; Wang, Hai; Wu, Gui; Li, Bo; Li, Qiang; Huang, Zhifeng; Qiu, Guixing; Wu, Zhihong

2016-01-01

Porous titanium is a kind of promising material for bone substitution, while its bio-inert property results in demand of modifications to improve the osteointegration capacity. In this study, gelatin (Gel) and nano-hydroxyapatite (nHA) were used to construct 3D micro-scaffolds in the pores of porous titanium in the ratios of Gel:nHA = 1:0, Gel:nHA = 1:1, and Gel:nHA = 1:3, respectively. Cell attachment and proliferation, and gene and protein expression levels of osteogenic markers were evaluated in MC3T3-E1 cells, followed by bone regeneration assessment in a rabbit radius defect model. All hybrid scaffolds with different composition ratio were found to have significant promotional effects in cell adhesion, proliferation and differentiation, in which the group with Gel:nHA = 1:1 showed the best performance in vitro, as well as the most bone regeneration volume in vivo. This 3D micro-scaffolds modification may be an innovative method for porous titanium ornamentation and shows potential application values in clinic. PMID:27092492

Hybrid Macro-Porous Titanium Ornamented by Degradable 3D Gel/nHA Micro-Scaffolds for Bone Tissue Regeneration.

PubMed

Yin, Bo; Ma, Pei; Chen, Jun; Wang, Hai; Wu, Gui; Li, Bo; Li, Qiang; Huang, Zhifeng; Qiu, Guixing; Wu, Zhihong

2016-04-15

Porous titanium is a kind of promising material for bone substitution, while its bio-inert property results in demand of modifications to improve the osteointegration capacity. In this study, gelatin (Gel) and nano-hydroxyapatite (nHA) were used to construct 3D micro-scaffolds in the pores of porous titanium in the ratios of Gel:nHA = 1:0, Gel:nHA = 1:1, and Gel:nHA = 1:3, respectively. Cell attachment and proliferation, and gene and protein expression levels of osteogenic markers were evaluated in MC3T3-E1 cells, followed by bone regeneration assessment in a rabbit radius defect model. All hybrid scaffolds with different composition ratio were found to have significant promotional effects in cell adhesion, proliferation and differentiation, in which the group with Gel:nHA = 1:1 showed the best performance in vitro, as well as the most bone regeneration volume in vivo. This 3D micro-scaffolds modification may be an innovative method for porous titanium ornamentation and shows potential application values in clinic.

In vivo immuno-reactivity analysis of the porous three-dimensional chitosan/SiO2 and chitosan/SiO2 /hydroxyapatite hybrids.

PubMed

Guo, Mengxia; Dong, Yifan; Xiao, Jiangwei; Gu, Ruicai; Ding, Maochao; Huang, Tao; Li, Junhua; Zhao, Naru; Liao, Hua

2018-05-01

Inorganic/organic hybrid silica-chitosan (CS) scaffolds have promising potential for bone defect repair, due to the controllable mechanical properties, degradation behavior, and scaffold morphology. However, the precise in vivo immuno-reactivity of silica-CS hybrids with various compositions is still poorly defined. In this study, we fabricated the three-dimensional (3D) interconnected porous chitosan-silica (CS/SiO 2 ) and chitosan-silica-hydroxyapatite (CS/SiO 2 /HA) hybrids, through sol-gel process and 3D plotting skill, followed by the naturally or freeze drying separately. Scanning electron microscopy demonstrated the hybrids possessed the uniform geometric structure, while, transmission electron microscopy displayed nanoscale silica, or HA nanoparticles dispersed homogeneously in the CS matrix, or CS/silica hybrids. After intramuscular implantation, CS/SiO 2 and CS/SiO 2 /HA hybrids triggered a local and limited monocyte/macrophage infiltration and myofiber degeneration. Naturally dried CS/SiO 2 hybrid provoked a more severe inflammation than the freeze-dried ones. Dendritic cells were attracted to invade into the implants embedded-muscle, but not be activated to prime the adaptive immunity, because the absence of cytotoxic T cells and B cells in muscle received the implants. Fluorescence-activated cell sorting (FACS) analysis indicated the implanted hybrids were incapable to initiate splenocytes activation. Plasma complement C3 enzyme linked immunosorbent assay (ELISA) assay showed the hybrids induced C3 levels increase in early implanting phase, and the subsequent striking decrease. Thus, the present results suggest that, in vivo, 3D plotted porous CS/SiO 2 and CS/SiO 2 /HA hybrids are relatively biocompatible in vivo, which initiate a localized inflammatory procedure, instead of a systematic immune response. © 2018 Wiley Periodicals, Inc. J Biomed Mater Res Part A: 106A: 1223-1235, 2018. © 2018 Wiley Periodicals, Inc.

Enhancement of VEGF-Mediated Angiogenesis by 2-N,6-O-Sulfated Chitosan-Coated Hierarchical PLGA Scaffolds.

PubMed

Yu, Yuanman; Chen, Jie; Chen, Rui; Cao, Lingyan; Tang, Wei; Lin, Dan; Wang, Jing; Liu, Changsheng

2015-05-13

Rapid and controlled vascularization within scaffolds remains one of the key limitations in tissue engineering applications. This study describes the fabrication and characterization of 2-N,6-O-sulfated chitosan (26SCS)-coated hierarchical scaffold composed of poly(lactic-co-glycolic acid) (PLGA) microspheres, as a desirable vehicle for vascular endothelial growth factor (VEGF) delivery and consequent angiogenic boosting in vitro. Owing to the hierarchical porous structure and high affinity between VEGF and 26SCS, the 26SCS-modified PLGA (S-PLGA) scaffold possesses excellent entrapment and sustained release of VEGF. Using human umbilical vein endothelial cells (HUVECs) as a cell model, the VEGF-loaded S-PLGA scaffold shows desirable cell viability and attachment. The bioactivity of released VEGF is validated by intracellular nitric oxide secretion and capillary tube formation, demonstrating the improved capacity of VEGF-mediated pro-angiogenesis ascribed to 26SCS incorporation. Such a strategy will afford an effective method to prepare a scaffold with promoted angiogenesis.

Bioactive nanoparticle-gelatin composite scaffold with mechanical performance comparable to cancellous bones.

PubMed

Wang, Chen; Shen, Hong; Tian, Ye; Xie, Yue; Li, Ailing; Ji, Lijun; Niu, Zhongwei; Wu, Decheng; Qiu, Dong

2014-08-13

Mechanical properties are among the most concerned issues for artificial bone grafting materials. The scaffolds used for bone grafts are either too brittle (glass) or too weak (polymer), and therefore composite scaffolds are naturally expected as the solution. However, despite the intensive studies on composite bone grafting materials, there still lacks a material that could be matched to the natural cancellous bones. In this study, nanosized bioactive particles (BP) with controllable size and good colloidal stability were used to composite with gelatin, forming macroporous scaffolds. It was found that the mechanical properties of obtained composite scaffolds, in terms of elastic modulus, compressive strength, and strain at failure, could match to that of natural cancellous bones. This is ascribed to the good distribution of particle in matrix and strong interaction between particle and gelatin. Furthermore, the incorporation of BPs endues the composite scaffolds with bioactivity, forming HA upon reacting with simulated body fluid (SBF) within days, thus stimulating preosteoblasts attachment, growth, and proliferation in these scaffolds. Together with their good mechanical properties, these composite scaffolds are promising artificial bone grating materials.

Boron nitride nanotubes included thermally cross-linked gelatin-glucose scaffolds show improved properties.

PubMed

Şen, Özlem; Culha, Mustafa

2016-02-01

Boron nitride nanotubes (BNNTs) are increasingly investigated for their medical and biomedical applications due to their unique properties such as resistance to oxidation, thermal and electrical insulation, and biocompatibility. BNNTs can be used to enhance mechanical strength of biomedical structures such as scaffolds in tissue engineering applications. In this study, we report the use of BNNTs and hydroxylated BNNTs (BNNT-OH) to improve the properties of gelatin-glucose scaffolds prepared with electrospinning technique. Human dermal fibroblast (HDF) cells are used for the toxicity assessment and cell seeding studies. It is found that the addition of BNNTs into the scaffold does not influence cell viability, decreases the scaffold degradation rate, and improves cell attachment and proliferation compared to only-gelatin scaffold. Copyright © 2015 Elsevier B.V. All rights reserved.

Gelatin-Modified Polyurethanes for Soft Tissue Scaffold

PubMed Central

Kucińska-Lipka, Justyna; Janik, Helena

2013-01-01

Recently, in the field of biomaterials for soft tissue scaffolds, the interest of their modification with natural polymersis growing. Synthetic polymers are often tough, and many of them do not possess fine biocompatibility. On the other hand, natural polymers are biocompatible but weak when used alone. The combination of natural and synthetic polymers gives the suitable properties for tissue engineering requirements. In our study, we modified gelatin synthetic polyurethanes prepared from polyester poly(ethylene-butylene adipate) (PEBA), aliphatic 1,6-hexamethylene diisocyanate (HDI), and two different chain extenders 1,4-butanediol (BDO) or 1-ethoxy-2-(2-hydroxyethoxy)ethanol (EHEE). From a chemical point of view, we replaced expensive components for building PU, such as 2,6-diisocyanato methyl caproate (LDI) and 1,4-diisocyanatobutane (BDI), with cost-effective HDI. The gelatin was added in situ (in the first step of synthesis) to polyurethane to increase biocompatibility and biodegradability of the obtained material. It appeared that the obtained gelatin-modified PU foams, in which chain extender was BDO, had enhanced interactions with media and their hydrolytic degradation profile was also improved for tissue engineering application. Furthermore, the gelatin introduction had positive impact on gelatin-modified PU foams by increasing their hemocompatibility. PMID:24363617

Incorporation of mesoporous silica nanoparticles into random electrospun PLGA and PLGA/gelatin nanofibrous scaffolds enhances mechanical and cell proliferation properties.

PubMed

Mehrasa, Mohammad; Asadollahi, Mohammad Ali; Nasri-Nasrabadi, Bijan; Ghaedi, Kamran; Salehi, Hossein; Dolatshahi-Pirouz, Alireza; Arpanaei, Ayyoob

2016-09-01

Poly(lactic-co-glycolic acid) (PLGA) and PLGA/gelatin random nanofibrous scaffolds embedded with different amounts of mesoporous silica nanoparticles (MSNPs) were fabricated using electrospinning method. To evaluate the effects of nanoparticles on the scaffolds, physical, chemical, and mechanical properties as well as in vitro degradation behavior of scaffolds were investigated. The mean diameters of nanofibers were 974±68nm for the pure PLGA scaffolds vs 832±70, 764±80, and 486±64 for the PLGA/gelatin, PLGA/10wt% MSNPs, and the PLGA/gelatin/10wt% MSNPs scaffolds, respectively. The results suggested that the incorporation of gelatin and MSNPs into PLGA-based scaffolds enhances the hydrophilicity of scaffolds due to an increase of hydrophilic functional groups on the surface of nanofibers. With porosity examination, it was concluded that the incorporation of MSNPs and gelatin decrease the porosity of scaffolds. Nanoparticles also improved the tensile mechanical properties of scaffolds. Using in vitro degradation analysis, it was shown that the addition of nanoparticles to the nanofibers matrix increases the weight loss percentage of PLGA-based samples, whereas it decreases the weight loss percentage in the PLGA/gelatin composites. Cultivation of rat pheochromocytoma cell line (PC12), as precursor cells of dopaminergic neural cells, on the scaffolds demonstrated that the introduction of MSNPs into PLGA and PLGA/gelatin matrix leads to improved cell attachment and proliferation and enhances cellular processes. Copyright © 2016 Elsevier B.V. All rights reserved.

Oxygen and nitrogen plasma etching of three-dimensional hydroxyapatite/chitosan scaffolds fabricated by additive manufacturing

NASA Astrophysics Data System (ADS)

Myung, Sung-Woon; Kim, Byung-Hoon

2016-01-01

Three-dimensional (3D) chitosan and hydroxyapatite (HAp)/chitosan (CH) scaffolds were fabricated by additive manufacturing, then their surfaces were etched with oxygen (O2) and nitrogen (N2) plasma. O2 and N2 plasma etching was performed to increase surface properties such as hydrophilicity, roughness, and surface chemistry on the scaffolds. After etching, hydroxyapatite was exposed on the surface of 3D HAp/CH scaffolds. The surface morphology and chemical properties were characterized by contact angle measurement, scanning electron microscopy, X-ray diffraction, and attenuated total reflection Fourier infrared spectroscopy. The cell viability of 3D chitosan scaffolds was examined by 3-(4,5-dimethylthiazol-2-yl)-2,5-diphenyltetrazolium bromide assay. The differentiation of preosteoblast cells was evaluated by alkaline phosphatase assay. The cell viability was improved by O2 and N2 plasma etching of 3D chitosan scaffolds. The present fabrication process for 3D scaffolds might be applied to a potential tool for preparing biocompatible scaffolds.

Chitosan-g-lactide copolymers for fabrication of 3D scaffolds for tissue engineering

NASA Astrophysics Data System (ADS)

Demina, T. S.; Zaytseva-Zotova, D. S.; Timashev, P. S.; Bagratashvili, V. N.; Bardakova, K. N.; Sevrin, Ch; Svidchenko, E. A.; Surin, N. M.; Markvicheva, E. A.; Grandfils, Ch; Akopova, T. A.

2015-07-01

Chitosan-g-oligo (L, D-lactide) copolymers were synthesized and assessed to fabricate a number of 3D scaffolds using a variety of technologies such as oil/water emulsion evaporation technique, freeze-drying and two-photon photopolymerization. Solid-state copolymerization method allowed us to graft up to 160 wt-% of oligolactide onto chitosan backbone via chitosan amino group acetylation with substitution degree reaching up to 0.41. Grafting of hydrophobic oligolactide side chains with polymerization degree up to 10 results in chitosan amphiphilic properties. The synthesized chitosan-g-lactide copolymers were used to design 3D scaffolds for tissue engineering such as spherical microparticles and macroporous hydrogels.

Effect of recombinant galectin-1 on the growth of immortal rat chondrocyte on chitosan-coated PLGA scaffold.

PubMed

Chen, Shiang-Jiuun; Lin, Chien-Chung; Tuan, Wei-Cheh; Tseng, Ching-Shiow; Huang, Rong-Nan

2010-06-15

The effect of galectin-1 (GAL1) on the growth of immortal rat chondrocyte (IRC) on chitosan-modified PLGA scaffold is investigated. The experimental results showed that water absorption ratio of chitosan-modified PLGA scaffold was 70% higher than that of PLGA alone after immersion in ddH(2)O for 2 weeks, indicating that chitosan-modification significantly enhances the hydrophilicity of PLGA. The experimental results also showed that GALl efficiently and spontaneously coats the chitosan-PLGA scaffold surface to promote adhesion and growth of immortal rat chondrocyte (IRC). To investigate the effect of endogenous GAL1, the full-length GAL1 cDNAs were cloned and constructed into pcDNA3.1 vectors to generate a plasmid expressed in IRC (IRC-GAL1). The results showed that IRC-GAL1 growth was significantly higher than that of IRC on chitosan-PLGA scaffold. The GAL1-potentiated IRC growth on chitosan-PLGA scaffold was dose-dependently inhibited by TDG (specific inhibitor of GAL1 binding). These results strongly suggest that GAL1 is critical for enhancing IRC cell adhesion and growth on chitosan-PLGA scaffold. Moreover, GAL1-coating or expression tends to promote IRC cell-cell aggregation on chitosan-PLGA scaffold and significantly enhances IRC migration. These results suggest that GAL1 probably could induce tissue differentiation and facilitates cartilage reconstruction. In conclusion, the experimental results suggest that both GAL1 and chitosan are important for enhancing IRC cell adhesion and growth on PLGA scaffold, and GAL1 is a potential biomaterial for tissue engineering. (c) 2009 Wiley Periodicals, Inc.

Macro- and micro-designed chitosan-alginate scaffold architecture by three-dimensional printing and directional freezing.

PubMed

Reed, Stephanie; Lau, Grace; Delattre, Benjamin; Lopez, David Don; Tomsia, Antoni P; Wu, Benjamin M

2016-01-07

While many tissue-engineered constructs aim to treat cartilage defects, most involve chondrocyte or stem cell seeding on scaffolds. The clinical application of cell-based techniques is limited due to the cost of maintaining cellular constructs on the shelf, potential immune response to allogeneic cell lines, and autologous chondrocyte sources requiring biopsy from already diseased or injured, scarce tissue. An acellular scaffold that can induce endogenous influx and homogeneous distribution of native stem cells from bone marrow holds great promise for cartilage regeneration. This study aims to develop such an acellular scaffold using designed, channeled architecture that simultaneously models the native zones of articular cartilage and subchondral bone. Highly porous, hydrophilic chitosan-alginate (Ch-Al) scaffolds were fabricated in three-dimensionally printed (3DP) molds designed to create millimeter scale macro-channels. Different polymer preform casting techniques were employed to produce scaffolds from both negative and positive 3DP molds. Macro-channeled scaffolds improved cell suspension distribution and uptake overly randomly porous scaffolds, with a wicking volumetric flow rate of 445.6 ± 30.3 mm(3) s(-1) for aqueous solutions and 177 ± 16 mm(3) s(-1) for blood. Additionally, directional freezing was applied to Ch-Al scaffolds, resulting in lamellar pores measuring 300 μm and 50 μm on the long and short axes, thus creating micrometer scale micro-channels. After directionally freezing Ch-Al solution cast in 3DP molds, the combined macro- and micro-channeled scaffold architecture enhanced cell suspension uptake beyond either macro- or micro-channels alone, reaching a volumetric flow rate of 1782.1 ± 48 mm(3) s(-1) for aqueous solutions and 440.9 ± 0.5 mm(3) s(-1) for blood. By combining 3DP and directional freezing, we can control the micro- and macro-architecture of Ch-Al to drastically improve cell influx into and distribution within the scaffold

Antibiotic-Releasing Porous Polymethylmethacrylate/Gelatin/Antibiotic Constructs for Craniofacial Tissue Engineering

PubMed Central

Shi, Meng; Kretlow, James D.; Spicer, Patrick P.; Tabata, Yasuhiko; Demian, Nagi; Wong, Mark E.; Kasper, F. Kurtis; Mikos, Antonios G.

2011-01-01

An antibiotic-releasing porous polymethylmethacrylate (PMMA) construct was developed to maintain the bony space and prime the wound site in the initial step of a two-stage regenerative medicine approach toward reconstructing significant bony or composite craniofacial tissue defects. Porous polymethylmethacrylate (PMMA) constructs incorporating gelatin microparticles (GMPs) were fabricated by the sequential assembly of GMPs, the antibiotic colistin, and a clinically used bone cement formulation of PMMA powder and methylmethacrylate liquid. PMMA/gelatin/antibiotic constructs with varying gelatin incorporation and drug content were investigated to elucidate the relationship between material composition and construct properties (porosity and drug release kinetics). The porosity of PMMA/gelatin/antibiotic constructs ranged between 7.6±1.8–38.4±1.4% depending on the amount of gelatin incorporated and the drug solution added for gelatin swelling. The constructs released colistin over 10 or 14 days with an average release rate per day above 10 µg/ml. The porosity and in vitro colistin release kinetics of PMMA/gelatin/antibiotic constructs were tuned by varying the material composition and fabrication parameters. This study demonstrates the potential of gelatin-incorporating PMMA constructs as a functional space maintainer for both promoting tissue healing/coverage and addressing local infections, enabling better long-term success of the definitive regenerated tissue construct. PMID:21295086

3D-printed porous titanium changed femoral head repair growth patterns: osteogenesis and vascularisation in porous titanium.

PubMed

Zhu, Wei; Zhao, Yan; Ma, Qi; Wang, Yingjie; Wu, Zhihong; Weng, Xisheng

2017-04-01

Osteonecrosis of the femoral head (ONFH) is a major cause of morbidity, and total hip arthroplasty is both traumatic and expensive. Here, we created a gelatine scaffold embedded in uniquely shaped, 3D-printed porous titanium parts, which could attract and promote the proliferation of osteoblasts as well as bone regeneration, as the extracellular matrix (ECM) does in vivo. Interestingly, after hybridisation with platelets, the scaffold exhibited a low yet considerable rate of stable, safe and long-term growth factor release. Additionally, a novel ONFH model was constructed and verified. Scaffolds implanted in this model were found to accelerate bone repair. In conclusion, our scaffold successfully simulates the ECM and considerably accelerates bone regeneration, in which platelets play an indispensable role. We believe that platelets should be emphasised as carriers that may be employed to transport drugs, cytokines and other small molecules to target locations in vivo. In addition, this novel scaffold is a useful material for treating ONFH. An overview of the novel scaffold mimicking the extracellular environment in bone repair. a and b: A gelatine scaffold was cross-linked and freeze-dried within 3D-printed porous titanium. c: Platelets were coated onto the gelatine microscaffold after freeze-drying platelet-rich plasma. d: The microscaffold supported the migration of cells into the titanium pores and their subsequent growth, while the platelets slowly released cell factors, exerting bioactivity.

Collagen-grafted porous HDPE/PEAA scaffolds for bone reconstruction.

PubMed

Kim, Chang-Shik; Jung, Kyung-Hye; Kim, Hun; Kim, Chan-Bong; Kang, Inn-Kyu

2016-01-01

After tumor resection, bone reconstruction such as skull base reconstruction using interconnected porous structure is absolutely necessary. In this study, porous scaffolds for bone reconstruction were prepared using heat-pressing and salt-leaching methods. High-density polyethylene (HDPE) and poly(ethylene-co-acrylic acid) (PEAA) were chosen as the polymer composites for producing a porous scaffold of high mechanical strength and having high reactivity with biomaterials such as collagen, respectively. The porous structure was observed through surface images, and its intrusion volume and porosity were measured. Owing to the carboxylic acids on PEAA, collagen was successfully grafted onto the porous HDPE/PEAA scaffold, which was confirmed by FT-IR spectroscopy and electron spectroscopy for chemical analysis. Osteoblasts were cultured on the collagen-grafted porous scaffold, and their adhesion, proliferation, and differentiation were investigated. The high viability and growth of the osteoblasts suggest that the collagen-grafted porous HDPE/PEAA is a promising scaffold material for bone generation.

Proliferation and enrichment of CD133(+) glioblastoma cancer stem cells on 3D chitosan-alginate scaffolds.

PubMed

Kievit, Forrest M; Florczyk, Stephen J; Leung, Matthew C; Wang, Kui; Wu, Jennifer D; Silber, John R; Ellenbogen, Richard G; Lee, Jerry S H; Zhang, Miqin

2014-11-01

Emerging evidence implicates cancer stem cells (CSCs) as primary determinants of the clinical behavior of human cancers, representing an ideal target for next-generation anti-cancer therapies. However CSCs are difficult to propagate in vitro, severely limiting the study of CSC biology and drug development. Here we report that growing cells from glioblastoma (GBM) cell lines on three dimensional (3D) porous chitosan-alginate (CA) scaffolds dramatically promotes the proliferation and enrichment of cells possessing the hallmarks of CSCs. CA scaffold-grown cells were found more tumorigenic in nude mouse xenografts than cells grown from monolayers. Growing in CA scaffolds rapidly promoted expression of genes involved in the epithelial-to-mesenchymal transition that has been implicated in the genesis of CSCs. Our results indicate that CA scaffolds have utility as a simple and inexpensive means to cultivate CSCs in vitro in support of studies to understand CSC biology and develop more effective anti-cancer therapies. Copyright © 2014 Elsevier Ltd. All rights reserved.

Novel macro-microporous gelatin scaffold fabricated by particulate leaching for soft tissue reconstruction with adipose-derived stem cells.

PubMed

Phull, Manraj K; Eydmann, Trevor; Roxburgh, Judy; Sharpe, Justin R; Lawrence-Watt, Diana J; Phillips, Gary; Martin, Yella

2013-02-01

The restoration of body contours as shaped by adipose tissue remains a clinical challenge specifically in patients who have experienced loss of contour due to trauma, surgical removal of tumours or congenital abnormalities. We have developed a novel macro-microporous biomaterial for use in soft tissue re-bulking and augmentation. Alginate beads provided the pore template for the construct. Incorporation, and subsequent dissolution, of the beads within a 7 % (w/v) gelatin matrix, produced a highly porous scaffold with an average pore size of 2.01 ± 0.08 mm. The ability of this scaffold to support the in vitro growth and differentiation of human adipose-derived stem cells (ADSCs) was then investigated. Histological analysis confirmed that the scaffold itself provided a suitable environment to support the growth of ADSCs on the scaffold walls. When delivered into the macropores in a fibrin hydrogel, ADSCs proliferated and filled the pores. In addition, ADSCs could readily be differentiated along the adipogenic lineage. These results therefore describe a novel scaffold that can support the proliferation and delivery of ADSCs. The scaffold is the first stage in developing a clinical alternative to current treatment methods for soft tissue reconstruction.

Evaluation of egg white ovomucin-based porous scaffold as an implantable biomaterial for tissue engineering.

PubMed

Carpena, Nathaniel T; Abueva, Celine D G; Padalhin, Andrew R; Lee, Byong-Taek

2017-10-01

Studies have shown the technological and functional properties of ovomucin (OVN) in the food-agricultural industry. But research has yet to explore its potential as an implantable biomaterial for tissue engineering and regenerative medicine. In this study we isolated OVN from egg white by isoelectric precipitation and fabricated scaffolds with tunable porosity by utilizing its foaming property. Gelatin a known biocompatible material was introduced to stabilize the foams, wherein different ratios of OVN and gelatin had a significant effect on the degree of porosity, pore size and stability of the formed hydrogels. The porous scaffolds were crosslinked with EDC resulting in stable scaffolds with prolonged degradation. Improved cell proliferation and adhesion of rat bone marrow-derived mesenchymal stem cells were observed for OVN containing scaffolds. Although, scaffolds with 75% OVN showed decrease in cell proliferation for L929 fibroblast type of cells. Further biocompatibility assessment as implant material was determined by subcutaneous implantation in rats of selected scaffold. H&E staining showed reasonable vascularization over time and little evidence of severe fibrosis at the implant site. Persistent polarization of classically activated macrophage was not observed, potentially reducing inflammatory response, and showed increased expression of alternatively activated macrophage cells that is favorable for tissue repair. Analysis of IgE levels in rat serum after implantation indicated minimal and resolvable allergic response to the OVN implants. The results demonstrate OVN as an acceptable implant scaffold that could provide new opportunities as an alternative natural biocompatible and functional biomaterial in various biomedical applications. © 2016 Wiley Periodicals, Inc. J Biomed Mater Res Part B: Appl Biomater, 105B: 2107-2117, 2017. © 2016 Wiley Periodicals, Inc.

Development of affinity-based delivery of NGF from a chondroitin sulfate biomaterial.

PubMed

Butterfield, Karen Chao; Conovaloff, Aaron W; Panitch, Alyssa

2011-01-01

Chondroitin sulfate is a major component of the extracellular matrix in both the central and peripheral nervous systems. Chondroitin sulfate is upregulated at injury, thus methods to promote neurite extension through chondroitin sulfate-rich matrices and synthetic scaffolds are needed. We describe the use of both chondroitin sulfate and a novel chondroitin sulfate-binding peptide to control the release of nerve growth factor. Interestingly, the novel chondroitin sulfate-binding peptide enhances the controlled release properties of the chondroitin sulfate gels. While introduction of chondroitin sulfate into a scaffold inhibits primary cortical outgrowth, the combination of chondroitin sulfate, chondroitin sulfate-binding peptide and nerve growth factor promotes primary cortical neurite outgrowth in chondroitin sulfate gels.

Chitosan-poly(lactide-co-glycolide) microsphere-based scaffolds for bone tissue engineering: in vitro degradation and in vivo bone regeneration studies.

PubMed

Jiang, Tao; Nukavarapu, Syam P; Deng, Meng; Jabbarzadeh, Ehsan; Kofron, Michelle D; Doty, Stephen B; Abdel-Fattah, Wafa I; Laurencin, Cato T

2010-09-01

Natural polymer chitosan and synthetic polymer poly(lactide-co-glycolide) (PLAGA) have been investigated for a variety of tissue engineering applications. We have previously reported the fabrication and in vitro evaluation of a novel chitosan/PLAGA sintered microsphere scaffold for load-bearing bone tissue engineering applications. In this study, the in vitro degradation characteristics of the chitosan/PLAGA scaffold and the in vivo bone formation capacity of the chitosan/PLAGA-based scaffolds in a rabbit ulnar critical-sized-defect model were investigated. The chitosan/PLAGA scaffold showed slower degradation than the PLAGA scaffold in vitro. Although chitosan/PLAGA scaffold showed a gradual decrease in compressive properties during the 12-week degradation period, the compressive strength and compressive modulus remained in the range of human trabecular bone. Chitosan/PLAGA-based scaffolds were able to guide bone formation in a rabbit ulnar critical-sized-defect model. Microcomputed tomography analysis demonstrated that successful bridging of the critical-sized defect on the sides both adjacent to and away from the radius occurred using chitosan/PLAGA-based scaffolds. Immobilization of heparin and recombinant human bone morphogenetic protein-2 on the chitosan/PLAGA scaffold surface promoted early bone formation as evidenced by complete bridging of the defect along the radius and significantly enhanced mechanical properties when compared to the chitosan/PLAGA scaffold. Furthermore, histological analysis suggested that chitosan/PLAGA-based scaffolds supported normal bone formation via intramembranous formation. 2010 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

Fabrication of chitosan/gallic acid 3D microporous scaffold for tissue engineering applications.

PubMed

Thangavel, Ponrasu; Ramachandran, Balaji; Muthuvijayan, Vignesh

2016-05-01

This study explores the potential of gallic acid incorporated chitosan (CS/GA) 3D scaffolds for tissue engineering applications. Scaffolds were prepared by freezing and lyophilization technique and characterized. FTIR spectra confirmed the presence of GA in chitosan (CS) gel. DSC and TGA analysis revealed that the structure of chitosan was not altered due to the incorporation of GA, but thermal stability was significantly increased compared to the CS scaffold. SEM micrographs showed smooth, homogeneous, and microporous architecture of the scaffolds with good interconnectivity. CS/GA scaffolds exhibited approximately 90% porosity on average, increased swelling (600-900%) and controlled biodegradation (15-40%) in PBS (pH 7.4 at 37°C) with 1 mg/mL of lysozyme. CS/GA scaffolds showed 2-4 fold decrease in CFUs (p < 0.05) for both gram positive and gram negative bacteria compared to the CS scaffold. Cytotoxicity of these scaffolds was evaluated using NIH 3T3 L1 fibroblast cells. CS/GA 0.25% scaffold showed similar viability with CS scaffold at 24 and 48 h. CS/GA scaffolds (0.5-1.0%) showed 60-75% viability at 24 h and 90% at 48 h. SEM images showed that an increased cell attachment was observed for CS/GA scaffolds compared to CS scaffolds. These findings authenticate that CS/GA scaffolds were cytocompatible and would be useful for tissue engineering applications. © 2015 Wiley Periodicals, Inc.

Healing of skin wounds with a chitosan-gelatin sponge loaded with tannins and platelet-rich plasma.

PubMed

Lu, Bitao; Wang, Tianyou; Li, Zhiquan; Dai, Fangying; Lv, Lingmei; Tang, Fengling; Yu, Kun; Liu, Jiawei; Lan, Guangqian

2016-01-01

A chitosan-gelatin sponge (CSGT) was prepared using a chitosan/ascorbic acid solution blend containing gelatin, followed by crosslinking with tannin acid and freeze-drying, thereby combining the chitosan sponge and gelatin sponge. The structure of the CSGT was observed by scanning electron microscopy and was shown to have uniform and abundant pores measuring about 145-240μm in size. We also characterized the sponges by infrared spectroscopy, thermogravimetric analysis, mechanical property tests, swelling behavior analysis, water retention capacity tests, antibacterial property analysis, and cytotoxicity tests. Our data showed that the CSGT had good thermostability and mechanical properties as well as efficient water absorption and retention capacities. Moreover, the CSGT could effectively inhibit the growth of Escherichia coli and Staphylococcus aureus with low toxicity. In animal experiments, macroscopic observations and histological examinations showed that the wound covered by the CSGT healed quickly. Additionally, loading of the CSGT with platelet-rich plasma resulted in further acceleration of wound healing. Therefore, the CSGT and the CSGT with platelet-rich plasma were suitable for application as a wound dressing and may have potential for use in various biomedical applications. Copyright © 2015 Elsevier B.V. All rights reserved.

In vitro cartilage construct generation from silk fibroin- chitosan porous scaffold and umbilical cord blood derived human mesenchymal stem cells in dynamic culture condition.

PubMed

Agrawal, Parinita; Pramanik, Krishna; Biswas, Amit; Ku Patra, Ranjan

2018-02-01

Cartilage construct generation includes a scaffold with appropriate composition to mimic matrix of the damaged tissue on which the stem cells grow and differentiate. In this study, umbilical cord blood (UCB) derived human mesenchymal stem cells (hMSCs) were seeded on freeze dried porous silk-fibroin (SF)/chitosan (CS) scaffolds. Influence of static and dynamic (spinner flask bioreactor) culture conditions on the developing cartilage construct were studied by in-vitro characterization for viability, proliferation, distribution, and chondrogenic differentiation of hMSCs over the scaffold. Constructs developed in spinner flask consisted of 62% live cells, and exhibited 543% more cell density at the core than constructs cultured in static system. Quantification of DNA and glycosaminoglycans accumulation after 21 days showed the progression of chondrogenic differentiation of hMSCs was higher in dynamic culture compared to static one. In constructs generated under dynamic condition, histology staining for proteoglycan matrix, and fluorescence staining for collagen-II and aggrecan showed positive correlation between early and late stage chondrogenic markers, which was further confirmed by quantitative PCR analysis, showing low collagen-I expression and highly expressed Sox9, collagen-II and aggrecan. The present study demonstrated that construct generated by combining 3D SF/CS scaffold with UCB-hMSCs under dynamic condition using spinner flask bioreactor can be used for cartilage tissue regeneration for future medical treatments. © 2017 Wiley Periodicals, Inc. J Biomed Mater Res Part A: 106A: 397-407, 2018. © 2017 Wiley Periodicals, Inc.

Electrospun PCL/Gelatin composite fibrous scaffolds: mechanical properties and cellular responses.

PubMed

Yao, Ruijuan; He, Jing; Meng, Guolong; Jiang, Bo; Wu, Fang

2016-06-01

Electrospinning of hybrid polymer has gained widespread interest by taking advantages of the biological property of the natural polymer and the mechanical property of the synthetic polymer. However, the effect of the blend ratio on the above two properties has been less reported despite the importance to balance these two properties in various tissue engineering applications. To this aim, we investigated the electrospun PCL/Gelatin composite fibrous scaffolds with different blend ratios of 4:1, 2:1, 1:1, 1:2, 1:4, respectively. The morphology of the electrospun samples was observed by SEM and the result showed that the fiber diameter distribution became more uniform with the increase of the gelatin content. The mechanical testing results indicated that the 2:1 PCL/Gelatin sample had both the highest tensile strength of 3.7 MPa and the highest elongation rate of about 90%. Surprisingly, the 2:1 PCL/Gelatin sample also showed the best mesenchymal stem cell responses in terms of attachment, spreading, and cytoskeleton organization. Such correlation might be partly due to the fact that the enhanced mechanical property, an integral part of the physical microenvironment, likely played an important role in regulating the cellular functions. Overall, our results indicated that the PCL/Gelatin sample with the blend ratio of 2:1 was a superior candidate for scaffolds for tissue engineering applications.

ALP gene expression in cDNA samples from bone tissue engineering using a HA/TCP/Chitosan scaffold

NASA Astrophysics Data System (ADS)

Stephanie, N.; Katarina, H.; Amir, L. R.; Gunawan, H. A.

2017-08-01

This study examined the potential use of hydroxyapatite (HA)/tricalcium phosphate (TCP)/Chitosan as a bone tissue engineering scaffold. The potential for using HA/TCP/chitosan as a scaffold was analyzed by measuring expression of the ALP osteogenic gene in cDNA from bone biopsies from four Macaque nemestrina. Experimental conditions included control (untreated), treatment with HA/TCP 70:30, HA/TCP 50:50, and HA/TCP/chitosan. cDNA samples were measured quantitively with Real-Time PCR (qPCR) and semi-quantitively by gel electrophoresis. There were no significant differences in ALP gene expression between treatment subjects after two weeks, but the HA/TCP/chitosan treatment gave the highest level of expression after four weeks. The scaffold using the HA/TCP/chitosan combination induced a higher level of expression of the osteogenic gene ALP than did scaffold without chitosan.

A novel, visible light-induced, rapidly cross-linkable gelatin scaffold for osteochondral tissue engineering

PubMed Central

Mazaki, Tetsuro; Shiozaki, Yasuyuki; Yamane, Kentaro; Yoshida, Aki; Nakamura, Mariko; Yoshida, Yasuhiro; Zhou, Di; Kitajima, Takashi; Tanaka, Masato; Ito, Yoshihiro; Ozaki, Toshifumi; Matsukawa, Akihiro

2014-01-01

Osteochondral injuries remain difficult to repair. We developed a novel photo-cross-linkable furfurylamine-conjugated gelatin (gelatin-FA). Gelatin-FA was rapidly cross-linked by visible light with Rose Bengal, a light sensitizer, and was kept gelled for 3 weeks submerged in saline at 37°C. When bone marrow-derived stromal cells (BMSCs) were suspended in gelatin-FA with 0.05% Rose Bengal, approximately 87% of the cells were viable in the hydrogel at 24 h after photo-cross-linking, and the chondrogenic differentiation of BMSCs was maintained for up to 3 weeks. BMP4 fusion protein with a collagen binding domain (CBD) was retained in the hydrogels at higher levels than unmodified BMP4. Gelatin-FA was subsequently employed as a scaffold for BMSCs and CBD-BMP4 in a rabbit osteochondral defect model. In both cases, the defect was repaired with articular cartilage-like tissue and regenerated subchondral bone. This novel, photo-cross-linkable gelatin appears to be a promising scaffold for the treatment of osteochondral injury. PMID:24662725

bFGF-containing electrospun gelatin scaffolds with controlled nano-architectural features for directed angiogenesis

PubMed Central

Montero, Ramon B.; Vial, Ximena; Nguyen, Dat Tat; Farhand, Sepehr; Reardon, Mark; Pham, Si M.; Tsechpenakis, Gavriil; Andreopoulos, Fotios M.

2011-01-01

Current therapeutic angiogenesis strategies are focused on the development of biologically responsive scaffolds that can deliver multiple angiogenic cytokines and/or cells in ischemic regions. Herein, we report on a novel electrospinning approach to fabricate cytokine-containing nanofibrous scaffolds with tunable architecture to promote angiogenesis. Fiber diameter and uniformity were controlled by varying the concentration of the polymeric (i.e. gelatin) solution, the feed rate, needle to collector distance, and electric field potential between the collector plate and injection needle. Scaffold fiber orientation (random vs. aligned) was achieved by alternating the polarity of two parallel electrodes placed on the collector plate thus dictating fiber deposition patterns. Basic fibroblast growth factor (bFGF) was physically immobilized within the gelatin scaffolds at variable concentrations and human umbilical vein endothelial cells (HUVEC) were seeded on the top of the scaffolds. Cell proliferation and migration was assessed as a function of growth factor loading and scaffold architecture. HUVECs successfully adhered onto gelatin B scaffolds and cell proliferation was directly proportional to the loading concentrations of the growth factor (0–100 bFGF ng/mL). Fiber orientation had a pronounced effect on cell morphology and orientation. Cells were spread along the fibers of the electrospun scaffolds with the aligned orientation and developed a spindle-like morphology parallel to the scaffold's fibers. In contrast, cells seeded onto the scaffolds with random fiber orientation, did not demonstrate any directionality and appeared to have a rounder shape. Capillary formation (i.e. sprouts length and number of sprouts per bead), assessed in a 3-D in vitro angiogenesis assay, was a function of bFGF loading concentration (0 ng, 50 ng and 100 ng per scaffold) for both types of electrospun scaffolds (i.e. with aligned or random fiber orientation). PMID:22200610

3D printing biodegradable scaffolds with chitosan materials for tissue engineering

NASA Astrophysics Data System (ADS)

Bardakova, K. N.; Demina, T. S.; Grebenik, E. A.; Minaev, N. V.; Akopova, T. A.; Bagratashvili, V. N.; Timashev, P. S.

2018-04-01

Chitosan-g-oligo (L,L-lactide) copolymer was synthesized through a solvent-free reaction in an extruder. Three-dimensional scaffolds based on photosensitive composition contained the synthetized copolymer were formed by two-photon polymerization. The optimum ratio of components, methods of preparation of photopolymerizable mixtures, parameters of the laser structuring and procedure of washing from unbound crosslinkers have been optimized. Chitosan scaffolds were non-cytotoxic and might therefore be a suitable candidate for treating spinal cord injuries and other neuronal degenerative diseases.

An overview of chitin or chitosan/nano ceramic composite scaffolds for bone tissue engineering.

PubMed

Deepthi, S; Venkatesan, J; Kim, Se-Kwon; Bumgardner, Joel D; Jayakumar, R

2016-12-01

Chitin and chitosan based nanocomposite scaffolds have been widely used for bone tissue engineering. These chitin and chitosan based scaffolds were reinforced with nanocomponents viz Hydroxyapatite (HAp), Bioglass ceramic (BGC), Silicon dioxide (SiO 2 ), Titanium dioxide (TiO 2 ) and Zirconium oxide (ZrO 2 ) to develop nanocomposite scaffolds. Plenty of works have been reported on the applications and characteristics of the nanoceramic composites however, compiling the work done in this field and presenting it in a single article is a thrust area. This review is written with an aim to fill this gap and focus on the preparations and applications of chitin or chitosan/nHAp, chitin or chitosan/nBGC, chitin or chitosan/nSiO 2 , chitin or chitosan/nTiO 2 and chitin or chitosan/nZrO 2 in the field of bone tissue engineering in detail. Many reports so far exemplify the importance of ceramics in bone regeneration. The effect of nanoceramics over native ceramics in developing composites, its role in osteogenesis etc. are the gist of this review. Copyright © 2016 Elsevier B.V. All rights reserved.

Multilayer porous UHMWPE scaffolds for bone defects replacement.

PubMed

Maksimkin, A V; Senatov, F S; Anisimova, N Yu; Kiselevskiy, M V; Zalepugin, D Yu; Chernyshova, I V; Tilkunova, N A; Kaloshkin, S D

2017-04-01

Reconstruction of the structural integrity of the damaged bone tissue is an urgent problem. UHMWPE may be potentially used for the manufacture of porous implants simulating as closely as possible the porous cancellous bone tissue. But the extremely high molecular weight of the polymer does not allow using traditional methods of foaming. Porous and multilayer UHMWPE scaffolds with nonporous bulk layer and porous layer that mimics cancellous bone architecture were obtained by solid-state mixing, thermopressing and washing in subcritical water. Structural and mechanical properties of the samples were studied. Porous UHMWPE samples were also studied in vitro and in vivo. The pores of UHMWPE scaffold are open and interconnected. Volume porosity of the obtained samples was 79±2%; the pore size range was 80-700μm. Strong connection of the two layers in multilayer UHMWPE scaffolds was observed with decreased number of fusion defects. Functionality of implants based on multilayer UHMWPE scaffolds is provided by the fixation of scaffolds in the bone defect through ingrowths of the connective tissue into the pores, which ensures the maintenance of the animals' mobility. Copyright © 2016 Elsevier B.V. All rights reserved.

Development of a reconstructed cornea from collagen-chondroitin sulfate foams and human cell cultures.

PubMed

Vrana, N Engin; Builles, Nicolas; Justin, Virginie; Bednarz, Jurgen; Pellegrini, Graziella; Ferrari, Barbara; Damour, Odile; Hulmes, David J S; Hasirci, Vasif

2008-12-01

To develop an artificial cornea, the ability to coculture the different cell types present in the cornea is essential. Here the goal was to develop a full-thickness artificial cornea using an optimized collagen-chondroitin sulfate foam, with a thickness close to that of human cornea, by coculturing human corneal epithelial and stromal cells and transfected human endothelial cells. Corneal extracellular matrix was simulated by a porous collagen/glycosaminoglycan-based scaffold seeded with stromal keratocytes and then, successively, epithelial and endothelial cells. Scaffolds were characterized for bulk porosity and pore size distribution. The performance of the three-dimensional construct was studied by histology, immunofluorescence, and immunohistochemistry. The scaffold had 85% porosity and an average pore size of 62.1 microm. Keratocytes populated the scaffold and produced a newly synthesized extracellular matrix as characterized by immunohistochemistry. Even though the keratocytes lost their CD34 phenotype marker, the absence of smooth muscle actin fibers showed that these cells had not differentiated into myofibroblasts. The epithelial cells formed a stratified epithelium and began basement membrane deposition. An endothelial cell monolayer beneath the foam was also apparent. These results demonstrate that collagen-chondroitin sulfate scaffolds are good substrates for artificial cornea construction with good resilience, long-term culture capability, and handling properties.

Nano/macro porous bioactive glass scaffold

NASA Astrophysics Data System (ADS)

Wang, Shaojie

Bioactive glass (BG) and ceramics have been widely studied and developed as implants to replace hard tissues of the musculo-skeletal system, such as bones and teeth. Recently, instead of using bulk materials, which usually do not degrade rapidly enough and may remain in the human body for a long time, the idea of bioscaffold for tissue regeneration has generated much interest. An ideal bioscaffold is a porous material that would not only provide a three-dimensional structure for the regeneration of natural tissue, but also degrade gradually and, eventually be replaced by the natural tissue completely. Among various material choices the nano-macro dual porous BG appears as the most promising candidate for bioscaffold applications. Here macropores facilitate tissue growth while nanopores control degradation and enhance cell response. The surface area, which controls the degradation of scaffold can also be tuned by changing the nanopore size. However, fabrication of such 3D structure with desirable nano and macro pores has remained challenging. In this dissertation, sol-gel process combined with spinodal decomposition or polymer sponge replication method has been developed to fabricate the nano-macro porous BG scaffolds. Macropores up to 100microm are created by freezing polymer induced spinodal structure through sol-gel transition, while larger macropores (>200um) of predetermined size are obtained by the polymer sponge replication technique. The size of nanopores, which are inherent to the sol-gel method of glass fabrication, has been tailored using several approaches: Before gel point, small nanopores are generated using acid catalyst that leads to weakly-branched polymer-like network. On the other hand, larger nanopores are created with the base-catalyzed gel with highly-branched cluster-like structure. After the gel point, the nanostructure can be further modified by manipulating the sintering temperature and/or the ammonia concentration used in the solvent

Chitosan composite three dimensional macrospheric scaffolds for bone tissue engineering.

PubMed

Vyas, Veena; Kaur, Tejinder; Thirugnanam, Arunachalam

2017-11-01

The present work deals with the fabrication of chitosan composite scaffolds with controllable and predictable internal architecture for bone tissue engineering. Chitosan (CS) based composites were developed by varying montmorillonite (MMT) and hydroxyapatite (HA) combinations to fabricate macrospheric three dimensional (3D) scaffolds by direct agglomeration of the sintered macrospheres. The fabricated CS, CS/MMT, CS/HA and CS/MMT/HA 3D scaffolds were characterized for their physicochemical, biological and mechanical properties. The XRD and ATR-FTIR studies confirmed the presence of the individual constituents and the molecular interaction between them, respectively. The reinforcement with HA and MMT showed reduced swelling and degradation rate. It was found that in comparison to pure CS, the CS/HA/MMT composites exhibited improved hemocompatibility and protein adsorption. The sintering of the macrospheres controlled the swelling ability of the scaffolds which played an important role in maintaining the mechanical strength of the 3D scaffolds. The CS/HA/MMT composite scaffold showed 14 folds increase in the compressive strength when compared to pure CS scaffolds. The fabricated scaffolds were also found to encourage the MG 63 cell proliferation. Hence, from the above studies it can be concluded that the CS/HA/MMT composite 3D macrospheric scaffolds have wider and more practical application in bone tissue regeneration applications. Copyright © 2017 Elsevier B.V. All rights reserved.

Evaluation of chitosan-hydroxyapatite-collagen composite strength as scaffold material by immersion in simulated body fluid

NASA Astrophysics Data System (ADS)

Sari, N. K.; Indrani, D. J.; Johan, C.; Corputty, J. E. M.

2017-08-01

The reconstruction of bone tissue defects is a major challenge facing oral and maxillofacial surgeons. The essential elements needed for tissue engineering are cells, scaffolds (matrix), and stimulant molecules (growth factors). The mechanical properties of chitosan-hydroxyapatite-collagen scaffolds produced by BATAN, Jakarta, have not yet been studied. This study therefore analyzed the mechanical properties of chitosan-hydroxyapatite-collagen composite scaffolds prepared by BATAN, Jakarta, before and after immersion in simulated body fluid (SBF) for eight days. The compressive and tensile strengths of the chitosan-hydroxyapatite-collagen composite scaffolds were analyzed after immersion in SBF at 37°C for eight days. Each scaffold was removed and dried at room temperature on days 0, 2, 4, 6, and 8. The data obtained were processed and analyzed. Variations in the compressive strength and tensile strength were attributed to several aspects, such the specimen size, which was not uniform, the scaffold composition, scaffold pore size, which was also not uniform, and the degradation of the polymer. The chitosan-hydroxyapatite-collagen composite scaffold does not exhibit differences in the tensile strength and compressive strength before and after immersion in SBF.

Image-based metrology of porous tissue engineering scaffolds

NASA Astrophysics Data System (ADS)

Rajagopalan, Srinivasan; Robb, Richard A.

2006-03-01

Tissue engineering is an interdisciplinary effort aimed at the repair and regeneration of biological tissues through the application and control of cells, porous scaffolds and growth factors. The regeneration of specific tissues guided by tissue analogous substrates is dependent on diverse scaffold architectural indices that can be derived quantitatively from the microCT and microMR images of the scaffolds. However, the randomness of pore-solid distributions in conventional stochastic scaffolds presents unique computational challenges. As a result, image-based characterization of scaffolds has been predominantly qualitative. In this paper, we discuss quantitative image-based techniques that can be used to compute the metrological indices of porous tissue engineering scaffolds. While bulk averaged quantities such as porosity and surface are derived directly from the optimal pore-solid delineations, the spatially distributed geometric indices are derived from the medial axis representations of the pore network. The computational framework proposed (to the best of our knowledge for the first time in tissue engineering) in this paper might have profound implications towards unraveling the symbiotic structure-function relationship of porous tissue engineering scaffolds.

Highly defined 3D printed chitosan scaffolds featuring improved cell growth.

PubMed

Elviri, Lisa; Foresti, Ruben; Bergonzi, Carlo; Zimetti, Francesca; Marchi, Cinzia; Bianchera, Annalisa; Bernini, Franco; Silvestri, Marco; Bettini, Ruggero

2017-07-12

The augmented demand for medical devices devoted to tissue regeneration and possessing a controlled micro-architecture means there is a need for industrial scale-up in the production of hydrogels. A new 3D printing technique was applied to the automation of a freeze-gelation method for the preparation of chitosan scaffolds with controlled porosity. For this aim, a dedicated 3D printer was built in-house: a preliminary effort has been necessary to explore the printing parameter space to optimize the printing results in terms of geometry, tolerances and mechanical properties of the product. Analysed parameters included viscosity of the starting chitosan solution, which was measured with a Brookfield viscometer, and temperature of deposition, which was determined by filming the process with a cryocooled sensor thermal camera. Optimized parameters were applied to the production of scaffolds from solutions of chitosan alone or with the addition of raffinose as a viscosity modifier. Resulting hydrogels were characterized in terms of morphology and porosity. In vitro cell culture studies comparing 3D printed scaffolds with their homologous produced by solution casting evidenced an improvement in biocompatibility deriving from the production technique as well as from the solid state modification of chitosan stemming from the addition of the viscosity modifier.

Novel layered double hydroxides-hydroxyapatite/gelatin bone tissue engineering scaffolds: Fabrication, characterization, and in vivo study.

PubMed

Fayyazbakhsh, Fateme; Solati-Hashjin, Mehran; Keshtkar, Abbas; Shokrgozar, Mohammad Ali; Dehghan, Mohammad Mehdi; Larijani, Bagher

2017-07-01

Developing porous biodegradable scaffolds through simple methods is one of the main approaches of bone tissue engineering (BTE). In this work, a novel BTE composite containing layered double hydroxides (LDH), hydroxyapatite (HA) and gelatin (GEL) was fabricated using co-precipitation and solvent-casting methods. Physiochemical characterizations showed that the chemical composition and microstructure of the scaffolds were similar to the natural spongy bone. Interconnected macropores ranging over 100 to 600μm were observed for both scaffolds while the porosity of 90±0.12% and 92.11±0.15%, as well as, Young's modulus of 19.8±0.41 and 12.5±0.35GPa were reported for LDH/GEL and LDH-HA/GEL scaffolds, respectively. The scaffolds were degraded in deionized water after a month. The SEM images revealed that between two scaffolds, the LDH-HA/GEL with needle-like secondary HA crystals showed better bioactivity. According to the alkaline phosphatase activity and Alizarin red staining results, LDH-HA/GEL scaffolds demonstrated better bone-specific activities comparing to LDH/Gel scaffold as well as control sample (P<0.05). The rabbit adipose stem cells (ASCs) were extracted and cultured, then seeded on the LDH-HA/GEL scaffolds after confluence. Three groups of six adult rabbits were prepared: the scaffold+ASCs group, the empty scaffold group and the control group. The critical defects were made on the left radius and the scaffolds with or without ASCs were implanted there while the control group was left without any treatment. All animals were sacrificed after 12weeks. Histomorphometric results showed that the regeneration of defects was accelerated by scaffold implantation but ASC-seeding significantly improved the quality of new bone formation (P<0.05). The results confirmed the good performance of LDH-HA/GEL scaffold to induce bone regeneration. Copyright © 2017 Elsevier B.V. All rights reserved.

Fabrication and characterization of highly porous barium titanate based scaffold coated by Gel/HA nanocomposite with high piezoelectric coefficient for bone tissue engineering applications.

PubMed

Ehterami, Arian; Kazemi, Mansure; Nazari, Bahareh; Saraeian, Payam; Azami, Mahmoud

2018-03-01

It is well established that the piezoelectric effect plays an important physiological role in bone growth, remodeling and fracture healing. Barium titanate, as a well-known piezoelectric ceramic, is especially an attractive material as a scaffold for bone tissue engineering applications. In this regard, we tried to fabricate a highly porous barium titanate based scaffolds by foam replication method and polarize them by applying an external electric field. In order to enhance the mechanical and biological properties, polarized/non-polarized scaffolds were coated with gelatin and nanostructured HA and characterized for their morphologies, porosities, piezoelectric and mechanical properties. The results showed that the compressive strength and piezoelectric coefficient of porous scaffolds increased with the increase of sintering temperature. After being coated with Gel/HA nanocomposite, the interconnected porous structure and pore size of the scaffolds almost remain unchanged while the Gel/nHA-coated scaffolds exhibited enhanced compressive strength and elastic modulus compared with the uncoated samples. Also, the effect of polarizing and coating of optimal scaffolds on adhesion, viability, and proliferation of the MG63 osteoblast-like cell line was evaluated by scanning electron microscope (SEM) and MTT assay. The cell culture experiments revealed that developed scaffolds had good biocompatibility and cells were able to adhere, proliferate and migrate into pores of the scaffolds. Furthermore, cell density was significantly higher in the coated scaffolds at all tested time-points. These results indicated that highly porous barium titanate scaffolds coated with Gel/HA nanocomposite has great potential in tissue engineering applications for bone tissue repair and regeneration. Copyright © 2018 Elsevier Ltd. All rights reserved.

Chitosan/chondroitin sulfate hydrogels prepared in [Hmim][HSO4] ionic liquid.

PubMed

Nunes, Cátia S; Rufato, Kessily B; Souza, Paulo R; de Almeida, Elizângela A M S; da Silva, Michael J V; Scariot, Débora B; Nakamura, Celso V; Rosa, Fernanda A; Martins, Alessandro F; Muniz, Edvani C

2017-08-15

[Hmim][HSO 4 ] ionic liquid (IL) and bio-renewable sources as chitosan (CHT) and chondroitin sulfate (CS) were used to yield hydrogel-based materials (CHT/CS). The use of IL to solubilize both polysaccharides was considered an innovative way based on "green chemistry" principle, aiming the production of CHT/CS blended systems. CHT/CS hydrogels were carried out in homogeneous medium from short dissolution times. The hydrogels were characterized and achieved with excellent stabilities (in the 1.2-10pH range), larger swelling capacities, as well as devoid of cytotoxicity towards the normal VERO and diseased HT29 cells. The CHT/CS hydrogels carried out in [Hmim][HSO 4 ] could be applied in many technological purposes, like medical, pharmaceutical, and environmental fields. Copyright © 2017 Elsevier Ltd. All rights reserved.

Microsphere-based scaffolds encapsulating chondroitin sulfate or decellularized cartilage

PubMed Central

Gupta, Vineet; Tenny, Kevin M; Barragan, Marilyn; Berkland, Cory J; Detamore, Michael S

2016-01-01

Extracellular matrix materials such as decellularized cartilage (DCC) and chondroitin sulfate (CS) may be attractive chondrogenic materials for cartilage regeneration. The goal of the current study was to investigate the effects of encapsulation of DCC and CS in homogeneous microsphere-based scaffolds, and to test the hypothesis that encapsulation of these extracellular matrix materials would induce chondrogenesis of rat bone marrow stromal cells. Four different types of homogeneous scaffolds were fabricated from microspheres of poly(D,L-lactic-co-glycolic acid): Blank (poly(D,L-lactic-co-glycolic acid) only; negative control), transforming growth factor-β3 encapsulated (positive control), DCC encapsulated, and CS encapsulated. These scaffolds were then seeded with rat bone marrow stromal cells and cultured for 6 weeks. The DCC and CS encapsulation altered the morphological features of the microspheres, resulting in higher porosities in these groups. Moreover, the mechanical properties of the scaffolds were impacted due to differences in the degree of sintering, with the CS group exhibiting the highest compressive modulus. Biochemical evidence suggested a mitogenic effect of DCC and CS encapsulation on rat bone marrow stromal cells with the matrix synthesis boosted primarily by the inherently present extracellular matrix components. An important finding was that the cell seeded CS and DCC groups at week 6 had up to an order of magnitude higher glycosaminoglycan contents than their acellular counterparts. Gene expression results indicated a suppressive effect of DCC and CS encapsulation on rat bone marrow stromal cell chondrogenesis with differences in gene expression patterns existing between the DCC and CS groups. Overall, DCC and CS were easily included in microsphere-based scaffolds; however, there is a requirement to further refine their concentrations to achieve the differentiation profiles we seek in vitro. PMID:27358376

Design of a hybrid biomaterial for tissue engineering: Biopolymer-scaffold integrated with an autologous hydrogel carrying mesenchymal stem-cells.

PubMed

Weinstein-Oppenheimer, Caroline R; Brown, Donald I; Coloma, Rodrigo; Morales, Patricio; Reyna-Jeldes, Mauricio; Díaz, María J; Sánchez, Elizabeth; Acevedo, Cristian A

2017-10-01

Biologically active biomaterials as biopolymers and hydrogels have been used in medical applications providing favorable results in tissue engineering. In this research, a wound dressing device was designed by integration of an autologous clot hydrogel carrying mesenchymal stem-cells onto a biopolymeric scaffold. This hybrid biomaterial was tested in-vitro and in-vivo, and used in a human clinical case. The biopolymeric scaffold was made with gelatin, chitosan and hyaluronic acid, using a freeze-drying method. The scaffold was a porous material which was designed evaluating both physical properties (glass transition, melting temperature and pore size) and biological properties (cell viability and fibronectin expression). Two types of chitosan (120 and 300kDa) were used to manufacture the scaffold, being the high molecular weight the most biologically active and stable after sterilization with gamma irradiation (25kGy). A clot hydrogel was formulated with autologous plasma and calcium chloride, using an approach based on design of experiments. The optimum hydrogel was used to incorporate cells onto the porous scaffold, forming a wound dressing biomaterial. The wound dressing device was firstly tested in-vitro using human cells, and then, its biosecurity was evaluated in-vivo using a rabbit model. The in-vitro results showed high cell viability after one week (99.5%), high mitotic index (19.8%) and high fibronectin expression. The in-vivo application to rabbits showed adequate biodegradability capacity (between 1 and 2weeks), and the histological evaluation confirmed absence of rejection signs and reepithelization on the wound zone. Finally, the wound dressing biomaterial was used in a single human case to implant autologous cells on a skin surgery. The medical examination indicated high biocompatibility, partial biodegradation at one week, early regeneration capacity at 4weeks and absence of rejection signs. Copyright © 2017 Elsevier B.V. All rights reserved.

Chitosan-based scaffolds for the support of smooth muscle constructs in intestinal tissue engineering

PubMed Central

Zakhem, Elie; Raghavan, Shreya; Gilmont, Robert R; Bitar, Khalil N

2012-01-01

Intestinal tissue engineering is an emerging field due to a growing demand for intestinal lengthening and replacement procedures secondary to massive resections of the bowel. Here, we demonstrate the potential use of a chitosan/collagen scaffold as a 3D matrix to support the bioengineered circular muscle constructs maintain their physiological functionality. We investigated the biocompatibility of chitosan by growing rabbit colonic circular smooth muscle cells (RCSMCs) on chitosan-coated plates. The cells maintained their spindle-like morphology and preserved their smooth muscle phenotypic markers. We manufactured tubular scaffolds with central openings composed of chitosan and collagen in a 1:1 ratio. Concentrically-aligned 3D circular muscle constructs were bioengineered using fibrin-based hydrogel seeded with RCSMCs. The constructs were placed around the scaffold for 2 weeks, after which they were taken off and tested for their physiological functionality. The muscle constructs contracted in response to Acetylcholine (Ach) and potassium chloride (KCl) and they relaxed in response to vasoactive intestinal peptide (VIP). These results demonstrate that chitosan is a biomaterial possibly suitable for intestinal tissue engineering applications. PMID:22483012

A Novel Collagen-Gelatin Scaffold for the Treatment of Deep Dermal Wounds-An Evaluation in a Minipig Model.

PubMed

Held, Manuel; Rahmanian-Schwarz, Afshin; Schiefer, Jennifer; Rath, Rebekka; Werner, Jan-Ole; Rahmanian, Shahab; Schaller, Hans-Eberhard; Petersen, Wiebke

2016-06-01

Today, autologous skin transplantation is frequently used for full-thickness skin defects. There is still a high demand for new wound-healing products to replace autologous skin transplantation. In this context, the effect of a new collagen-gelatin scaffold on full-thickness skin defects was evaluated. Four full-thickness skin defects were created surgically on the dorsum of 6 Göttingen minipigs. Three wounds were randomly treated with a novel collagen-gelatin scaffold in different thicknesses, whereas the fourth wound was left untreated and served as a control wound. During the experimental period of 21 days, a close-up photographic documentation was performed. Afterwards, the areas of the initial wounds were excised and examined histologically. The systematic evaluation of 24 wounds showed that treatment with the new collagen-gelatin scaffold led to an accelerated wound repair of 1.1 days. Compared to control wounds, it also demonstrated improved skin quality in regard to epidermal thickness. The new collagen-gelatin scaffold supports and accelerates dermal wound repair compared to untreated control wounds. Nevertheless, wound treatment with the scaffold was only performed on the first day. In further studies, the impact of multiple scaffold applications on full-thickness skin defects should be investigated.

Characterization of a chondroitin sulfate hydrogel for nerve root regeneration

NASA Astrophysics Data System (ADS)

Conovaloff, Aaron; Panitch, Alyssa

2011-10-01

Brachial plexus injury is a serious medical problem that affects many patients annually, with most cases involving damage to the nerve roots. Therefore, a chondroitin sulfate hydrogel was designed to both serve as a scaffold for regenerating root neurons and deliver neurotrophic signals. Capillary electrophoresis showed that chondroitin sulfate has a dissociation constant in the micromolar range with several common neurotrophins, and this was determined to be approximately tenfold stronger than with heparin. It was also revealed that nerve growth factor exhibits a slightly stronger affinity for hyaluronic acid than for chondroitin sulfate. However, E8 chick dorsal root ganglia cultured in the presence of nerve growth factor revealed that ganglia cultured in chondroitin sulfate scaffolds showed more robust growth than those cultured in control gels of hyaluronic acid. It is hypothesized that, despite the stronger affinity of nerve growth factor for hyaluronic acid, chondroitin sulfate serves as a better scaffold for neurite outgrowth, possibly due to inhibition of growth by hyaluronic acid chains.

Enrichment of glioma stem cell-like cells on 3D porous scaffolds composed of different extracellular matrix.

PubMed

Wang, Xuanzhi; Dai, Xingliang; Zhang, Xinzhi; Li, Xinda; Xu, Tao; Lan, Qing

2018-04-15

Cancer stem cells (CSCs), being tumor-initiating with self-renewal capacity and heterogeneity, are most likely the cause of tumor resistance, reoccurrence and metastasis. To further investigate the role of CSCs in tumor biology, there is a need to develop an effective culture system to grow, maintain and enrich CSCs. Three-dimensional (3D) cell culture model has been widely used in tumor research and drug screening. Recently, researchers have begun to utilize 3D models to culture cancer cells for CSCs enrichment. In this study, glioma cell line was cultured with 3D porous chitosan (CS) scaffolds or chitosan-hyaluronic acid (CS-HA) scaffolds to explore the possibility of glioma stem cells (GSCs)-like cells enrichment, to study the morphology, gene expression, and in vivo tumorigenicity of 3D scaffolds cells, and to compare results to 2D controls. Results showed that glioma cells on both CS and CS-HA scaffolds could form tumor cell spheroids and increased the expression of GSCs biomarkers compared to conventional 2D monolayers. Furthermore, cells in CS-HA scaffolds had higher expression levels of epithelial-to-mesenchymal transition (EMT)-related gene. Specifically, the in vivo tumorigenicity capability of CS-HA scaffold cultured cells was greater than 2D cells or CS scaffold cultured cells. It is indicated that the chemical composition of scaffold plays an important role in the enrichment of CSCs. Our results suggest that CS-HA scaffolds have a better capability to enrich GSCs-like cells and can serve as a simple and effective way to cultivate and enrich CSCs in vitro to support the study of CSCs biology and development of novel anti-cancer therapies. Copyright © 2018 Elsevier Inc. All rights reserved.

Composition of chitosan-hydroxyapatite-collagen composite scaffold evaluation after simulated body fluid immersion as reconstruction material

NASA Astrophysics Data System (ADS)

Verisqa, F.; Triaminingsih, S.; Corputty, J. E. M.

2017-08-01

Hydroxyapatite (HA) formation is one of the most important aspects of bone regeneration. Because domestically made chitosan-hydroxyapatite-collagen composite scaffolding from crab shell and bovine bone and tendon has potential as a maxillofacial reconstruction material, the material’s HA-forming ability requires evaluation. The aim of this research is to investigate chitosan-hydroxyapatite-collagen composite scaffold’s potential as a maxillofacial reconstruction material by observing the scaffold’s compositional changes. Scaffold specimens were immersed in 37°C simulated body fluid (SBF) for periods of 2, 4, 6, and 8 days. Scaffold composition was then evaluated by using energy dispersive spectroscopy (EDS). The calcium (Ca) and phosphorus (P) percentages of the scaffold were found to increase following SBF immersion. The high Ca/P ratio (3.82) on the scaffold indicated HA formation. Ion exchange played a significant role in the increased percentages of Ca and P, which led to new HA layer formation. The scaffold’s HA acted as a nucleation site of Ca and P from the SBF, with collagen and chitosan as the scaffold’s matrix. Chitosan-hydroxyapatite-collagen composite scaffold shows potential as a maxillofacial reconstruction material, since its composition favors HA formation.

Mechanical Properties, Cytocompatibility and Manufacturability of Chitosan:PEGDA Hybrid-Gel Scaffolds by Stereolithography.

PubMed

Morris, Viola B; Nimbalkar, Siddharth; Younesi, Mousa; McClellan, Phillip; Akkus, Ozan

2017-01-01

Extracellular matrix mimetic hydrogels which hybridize synthetic and natural polymers offer molecularly-tailored, bioactive properties and tunable mechanical strength. In addition, 3D bioprinting by stereolithography allows fabrication of internal pores and defined macroscopic shapes. In this study, we formulated a hybrid biocompatible resin using natural and synthetic polymers (chitosan and polyethylene glycol diacrylate (PEGDA), respectively) by controlling molecular weight of chitosan, feed-ratios, and photo-initiator concentration. Ear-shaped, hybrid scaffolds were fabricated by a stereolithographic method using a 405 nm laser. Hybrid hydrogel scaffolds of chitosan (50-190 kDa) and PEGDA (575 Da) were mixed at varying feed-ratios. Some of the cationic, amino groups of chitosan were neutralized by dialysis in acidic solution containing chitosan in excess of sodium acetate solution to inhibit quenching of newly formed photoradicals. A feed-ratio of 1:7.5 was found to be the most appropriate of the formulations considered in this study in terms of mechanical properties, cell adhesion, and printability. The biofabricated hybrid scaffold showed interconnected, homogeneous pores with a nominal pore size of 50 µm and an elastic modulus of ~400 kPa. Moreover, long-term cell viability and cell spreading was observed via actin filament staining. Printability of the biocompatible resin was confirmed by printing thresholded MR images of an ear and the feed ratio of 1:7.5 provided the most faithful reproduction of the shape. To the best of our knowledge, this is the first report of stereolithographic printing hybridizing cell-adhesive properties of chitosan with mechanical robustness of PEG in scaffolds suitable for repair of complex tissue geometries, such as those of the human ear.

Antimicrobial and anticancer activities of porous chitosan-alginate biosynthesized silver nanoparticles.

PubMed

Venkatesan, Jayachandran; Lee, Jin-Young; Kang, Dong Seop; Anil, Sukumaran; Kim, Se-Kwon; Shim, Min Suk; Kim, Dong Gyu

2017-05-01

The main aim of this study was to obtain porous antimicrobial composites consisting of chitosan, alginate, and biosynthesized silver nanoparticles (AgNPs). Chitosan and alginate were used owing to their pore-forming capacity, while AgNPs were used for their antimicrobial property. The developed porous composites of chitosan-alginate-AgNPs were characterized using Fourier transform infrared spectroscopy (FT-IR), ultraviolet-visible spectroscopy, X-ray diffraction (XRD) analysis, and scanning electron microscopy (SEM). The FT-IR results revealed the presence of a strong chemical interaction between chitosan and alginate due to polyelectrolyte complex; whereas, the XRD results confirmed the presence of AgNPs in the composites. The dispersion of AgNPs in the porous membrane was uniform with a pore size of 50-500μm. Antimicrobial activity of the composites was checked with Escherichia coli and Staphylococcus aureus. The developed composites resulted in the formation of a zone of inhibition of 11±1mm for the Escherichia coli, and 10±1mm for Staphylococcus aureus. The bacterial filtration efficiency of chitosan-alginate-AgNPs was 1.5-times higher than that of the chitosan-alginate composite. The breast cancer cell line MDA-MB-231 was used to test the anticancer activity of the composites. The IC 50 value of chitosan-alginate-AgNPs on MDA-MB-231 was 4.6mg. The developed chitosan-alginate-AgNPs composite showed a huge potential for its applications in antimicrobial filtration and cancer treatment. Copyright © 2017 Elsevier B.V. All rights reserved.

A tissue engineering approach for prenatal closure of myelomeningocele: comparison of gelatin sponge and microsphere scaffolds and bioactive protein coatings.

PubMed

Watanabe, Miho; Li, Hiaying; Roybal, Jessica; Santore, Matthew; Radu, Antonetta; Jo, Jun-Ichiro; Kaneko, Michio; Tabata, Yasuhiko; Flake, Alan

2011-04-01

Myelomeningocele (MMC) is a common and devastating malformation. As an alternative to fetal surgical repair, tissue engineering has the potential to provide a less invasive approach for tissue coverage applicable at an earlier stage of gestation. We have previously evaluated the use of gelatin hydrogel composites composed of gelatin sponges and sheets as a platform for tissue coverage of the MMC defect in the retinoic acid induced fetal rat model of MMC. In the current study, we compare our previous composite with gelatin microspheres as a scaffold for tissue ingrowth and cellular adhesion within the amniotic fluid environment. We also examine the relative efficacy of various bioactive protein coatings on the adhesion of amniotic fluid cells to the construct within the amniotic cavity. We conclude from this study that gelatin microspheres are as effective as gelatin sponges as a scaffold for cellular ingrowth and amniotic fluid cell adhesion and that collagen type I and fibronectin coatings enhance amniotic fluid cell adhesion to the gelatin-based scaffolds. These findings support the potential for the development of a tissue-engineered injectable scaffold that could be applied by ultrasound-guided injection, much earlier and less invasively than sponge or sheet-based composites.

Mechanical enhancement and in vitro biocompatibility of nanofibrous collagen-chitosan scaffolds for tissue engineering.

PubMed

Zou, Fengjuan; Li, Runrun; Jiang, Jianjun; Mo, Xiumei; Gu, Guofeng; Guo, Zhongwu; Chen, Zonggang

2017-12-01

The collagen-chitosan complex with a three-dimensional nanofiber structure was fabricated to mimic native ECM for tissue repair and biomedical applications. Though the three-dimensional hierarchical fibrous structures of collagen-chitosan composites could provide more adequate stimulus to facilitate cell adhesion, migrate and proliferation, and thus have the potential as tissue engineering scaffolding, there are still limitations in their applications due to the insufficient mechanical properties of natural materials. Because poly (vinyl alcohol) (PVA) and thermoplastic polyurethane (TPU) as biocompatible synthetic polymers can offer excellent mechanical properties, they were introduced into the collagen-chitosan composites to fabricate the mixed collagen/chitosan/PVA fibers and a sandwich structure (collagen/chitosan-TPU-collagen/chitosan) of nanofiber in order to enhance the mechanical properties of the nanofibrous collagen-chitosan scaffold. The results showed that the tensile behavior of materials was enhanced to different degrees with the difference of collagen content in the fibers. Besides the Young's modulus had no obvious changes, both the break strength and the break elongation of materials were heightened after reinforced by PVA. For the collagen-chitosan nanofiber reinforced by TPU, both the break strength and the Young's modulus of materials were heightened in different degrees with the variety of collagen content in the fibers despite the decrease of the break elongation of materials to some extent. In vitro cell test demonstrated that the materials could provide adequate environment for cell adhesion and proliferation. All these indicated that the reinforced collagen-chitosan nanofiber could be as potential scaffold for tissue engineering according to the different mechanical requirements in clinic.

Chitosan-functionalized silk fibroin 3D scaffold for keratocyte culture.

PubMed

Guan, Linan; Tian, Pei; Ge, Hongyan; Tang, Xianling; Zhang, Hong; Du, Lingling; Liu, Ping

2013-10-01

The goal of this study was to evaluate the potential suitability of an artificial membrane composed of silk fibroin (SF) functionalized by different ratios of chitosan (CS) as a substrate for the stroma of the cornea. Keratocytes were cultured on translucent membranes made of SF and CS with different ratios. The biophysical properties of the silk fibroin and chitosan (SF/CS) membrane were examined. The SF/CS showed tensile strengths that increased as the CS concentration increased, but the physical and mechanical properties of chitosan-functionalized silk fibroin scaffolds weakened significantly compared with those of native corneas. The resulting cell scaffolds were evaluated using western blot in addition to light and electron microscopy. The cell attachment and proliferation on the scaffold were similar to those on a plastic plate. Keratocytes cultured in serum on SF/CS exhibited stellate morphology along with a marked increase in the expression of keratocan compared with identical cultures on tissue culture plastics. The biocompatibility was tested by transplanting the acellular membrane into rabbit corneal stromal pockets. There was no inflammatory complication detected at any time point on the macroscopic level. Taken together, these results indicate that SF/CS holds promise as a substrate for corneal reconstruction.

Role of chondroitin sulphate tethered silk scaffold in cartilaginous disc tissue regeneration.

PubMed

Bhattacharjee, Maumita; Chawla, Shikha; Chameettachal, Shibu; Murab, Sumit; Bhavesh, Neel Sarovar; Ghosh, Sourabh

2016-04-12

Strategies for tissue engineering focus on scaffolds with tunable structure and morphology as well as optimum surface chemistry to simulate the anatomy and functionality of the target tissue. Silk fibroin has demonstrated its potential in supporting cartilaginous tissue formation both in vitro and in vivo. In this study, we investigate the role of controlled lamellar organization and chemical composition of biofunctionalized silk scaffolds in replicating the structural properties of the annulus region of an intervertebral disc using articular chondrocytes. Covalent attachment of chondroitin sulfate (CS) to silk is characterized. CS-conjugated silk constructs demonstrate enhanced cellular metabolic activity and chondrogenic redifferentiation potential with significantly improved mechanical properties over silk-only constructs. A matrix-assisted laser desorption ionization-time of flight analysis and protein-protein interaction studies help to generate insights into how CS conjugation can facilitate the production of disc associated matrix proteins, compared to a silk-only based construct. An in-depth understanding of the interplay between such extra cellular matrix associated proteins should help in designing more rational scaffolds for cartilaginous disc regeneration needs.

Microfluidic-based screening of resveratrol and drug-loading PLA/Gelatine nano-scaffold for the repair of cartilage defect.

PubMed

Ming, Li; Zhipeng, Yuan; Fei, Yu; Feng, Rao; Jian, Weng; Baoguo, Jiang; Yongqiang, Wen; Peixun, Zhang

2018-03-26

Cartilage defect is common in clinical but notoriously difficult to treat for low regenerative and migratory capacity of chondrocytes. Biodegradable tissue engineering nano-scaffold with a lot of advantages has been the direction of material to repair cartilage defect in recent years. The objective of our study is to establish a biodegradable drug-loading synthetic polymer (PLA) and biopolymer (Gelatine) composite 3D nano-scaffold to support the treatment of cartilage defect. We designed a microfluidic chip-based drug-screening device to select the optimum concentration of resveratrol, which has strong protective capability for chondrocyte. Then biodegradable resveratrol-loading PLA/Gelatine 3D nano-scaffolds were fabricated and used to repair the cartilage defects. As a result, we successfully cultured primary chondrocytes and screened the appropriate concentrations of resveratrol by the microfluidic device. We also smoothly obtained superior biodegradable resveratrol-loading PLA/Gelatine 3D nano-scaffolds and compared the properties and therapeutic effects of cartilage defect in rats. In summary, our microfluidic device is a simple but efficient platform for drug screening and resveratrol-loading PLA/Gelatine 3D nano-scaffolds could greatly promote the cartilage formation. It would be possible for materials and medical researchers to explore individualized pharmacotherapy and drug-loading synthetic polymer and biopolymer composite tissue engineering scaffolds for the repair of cartilage defect in future.

Functional 3-D cardiac co-culture model using bioactive chitosan nanofiber scaffolds.

PubMed

Hussain, Ali; Collins, George; Yip, Derek; Cho, Cheul H

2013-02-01

The in vitro generation of a three-dimensional (3-D) myocardial tissue-like construct employing cells, biomaterials, and biomolecules is a promising strategy in cardiac tissue regeneration, drug testing, and tissue engineering applications. Despite significant progress in this field, current cardiac tissue models are not yet able to stably maintain functional characteristics of cardiomyocytes for long-term culture and therapeutic purposes. The objective of this study was to fabricate bioactive 3-D chitosan nanofiber scaffolds using an electrospinning technique and exploring its potential for long-term cardiac function in the 3-D co-culture model. Chitosan is a natural polysaccharide biomaterial that is biocompatible, biodegradable, non-toxic, and cost effective. Electrospun chitosan was utilized to provide structural scaffolding characterized by scale and architectural resemblance to the extracellular matrix (ECM) in vivo. The chitosan fibers were coated with fibronectin via adsorption in order to enhance cellular adhesion to the fibers and migration into the interfibrous milieu. Ventricular cardiomyocytes were harvested from neonatal rats and studied in various culture conditions (i.e., mono- and co-cultures) for their viability and function. Cellular morphology and functionality were examined using immunofluorescent staining for alpha-sarcomeric actin (SM-actin) and gap junction protein, Connexin-43 (Cx43). Scanning electron microscopy (SEM) and light microscopy were used to investigate cellular morphology, spatial organization, and contractions. Calcium indicator was used to monitor calcium ion flux of beating cardiomyocytes. The results demonstrate that the chitosan nanofibers retained their cylindrical morphology in long-term cell cultures and exhibited good cellular attachment and spreading in the presence of adhesion molecule, fibronectin. Cardiomyocyte mono-cultures resulted in loss of cardiomyocyte polarity and islands of non-coherent contractions. However

Graphene Oxide-A Tool for the Preparation of Chemically Crosslinking Free Alginate-Chitosan-Collagen Scaffolds for Bone Tissue Engineering.

PubMed

Kolanthai, Elayaraja; Sindu, Pugazhendhi Abinaya; Khajuria, Deepak Kumar; Veerla, Sarath Chandra; Kuppuswamy, Dhandapani; Catalani, Luiz Henrique; Mahapatra, D Roy

2018-04-18

Developing a biodegradable scaffold remains a major challenge in bone tissue engineering. This study was aimed at developing novel alginate-chitosan-collagen (SA-CS-Col)-based composite scaffolds consisting of graphene oxide (GO) to enrich porous structures, elicited by the freeze-drying technique. To characterize porosity, water absorption, and compressive modulus, GO scaffolds (SA-CS-Col-GO) were prepared with and without Ca 2+ -mediated crosslinking (chemical crosslinking) and analyzed using Raman, Fourier transform infrared (FTIR), X-ray diffraction (XRD), and scanning electron microscopy techniques. The incorporation of GO into the SA-CS-Col matrix increased both crosslinking density as indicated by the reduction of crystalline peaks in the XRD patterns and polyelectrolyte ion complex as confirmed by FTIR. GO scaffolds showed increased mechanical properties which were further increased for chemically crosslinked scaffolds. All scaffolds exhibited interconnected pores of 10-250 μm range. By increasing the crosslinking density with Ca 2+ , a decrease in the porosity/swelling ratio was observed. Moreover, the SA-CS-Col-GO scaffold with or without chemical crosslinking was more stable as compared to SA-CS or SA-CS-Col scaffolds when placed in aqueous solution. To perform in vitro biochemical studies, mouse osteoblast cells were grown on various scaffolds and evaluated for cell proliferation by using MTT assay and mineralization and differentiation by alizarin red S staining. These measurements showed a significant increase for cells attached to the SA-CS-Col-GO scaffold compared to SA-CS or SA-CS-Col composites. However, chemical crosslinking of SA-CS-Col-GO showed no effect on the osteogenic ability of osteoblasts. These studies indicate the potential use of GO to prepare free SA-CS-Col scaffolds with preserved porous structure with elongated Col fibrils and that these composites, which are biocompatible and stable in a biological medium, could be used for

Antibacterial chitosan/silk sericin 3D porous scaffolds as a wound dressing material.

PubMed

Karahaliloglu, Zeynep; Kilicay, Ebru; Denkbas, Emir Baki

2017-09-01

Antimicrobial mixed dressings have traditionally been used to minimize bacterial infection of burns and other wounds. This study presents the advancement of biocompatible chitosan/silk sericin (CHT/SS) scaffolds combined with lauric acid (LA) and zinc oxide nanoparticles (nZnO) for the successful wound dressing applications. Antibacterial assay results showed that the diameters of the inhibition zone increased from 2 ± 0.4 to 7 ± 0.1 mm for Escherichia coli, as well as from 2.5 ± 0.2 to 6 ± 0.4 mm for Staphylococcus aureus while CHTS/SS/100nZnO compared to CHT/SS/0.01LA. The results not only showed excellent inhibition against Gram-positive and Gram-negative bacterial growth but also revealed improved proliferation and extended viability for HaCaT cells.

Chitosan-based hydrogel tissue scaffolds made by 3D plotting promotes osteoblast proliferation and mineralization.

PubMed

Liu, I-Hsin; Chang, Shih-Hsin; Lin, Hsin-Yi

2015-05-13

A 3D plotting system was used to make chitosan-based tissue scaffolds with interconnected pores using pure chitosan (C) and chitosan cross-linked with pectin (CP) and genipin (CG). A freeze-dried chitosan scaffold (CF/D) was made to compare with C, to observe the effects of structural differences. The fiber size, pore size, porosity, compression strength, swelling ratio, drug release efficacy, and cumulative weight loss of the scaffolds were measured. Osteoblasts were cultured on the scaffolds and their proliferation, type I collagen production, alkaline phosphatase activity, calcium deposition, and morphology were observed. C had a lower swelling ratio, degradation, porosity and drug release efficacy and a higher compressional stiffness and cell proliferation compared to CF/D (p < 0.05). Of the 3D-plotted samples, cells on CP exhibited the highest degree of mineralization after 21 d (p < 0.05). CP also had the highest swelling ratio and fastest drug release, followed by C and CG (p < 0.05). Both CP and CG were stiffer and degraded more slowly in saline solution than C (p < 0.05). In summary, 3D-plotted scaffolds were stronger, less likely to degrade and better promoted osteoblast cell proliferation in vitro compared to the freeze-dried scaffolds. C, CP and CG were structurally similar, and the different crosslinking caused significant changes in their physical and biological performances.

2-hydroxyethyl metahcrylate/gelatin based superporous hydrogels for tissue regeneration

NASA Astrophysics Data System (ADS)

Tomić, Simonida Lj.; Babić, Marija M.; Vuković, Jovana S.; Perišić, Marija D.; Filipović, Vuk V.; Davidović, Sladjana Z.; Filipović, Jovanka M.

2016-05-01

In this study, superporous hydrogels were synthesized by free radical polymerization of 2-hydroxyethyl methacrylate without and in the presence of gelatin. Highly porous hydrogel structures were obtained by two different techniques: using a gas blowing agent, sodium bicarbonate, and a cryogenic treatment followed by freeze-drying. After the gel synthesis, gelatin molecules were covalently immobilised onto PHEMA via glytaraldehyde activation. All samples were characterized for morphological, mechanical, swelling and antibacterial properties. The results obtained show that samples with gelatin show better properties in comparison with PHEMA samples, which make these materials highly attractive for developing hydrogel scaffolds for tissue regeneration.

Modified n-HA/PA66 scaffolds with chitosan coating for bone tissue engineering: cell stimulation and drug release.

PubMed

Zou, Qin; Li, Junfeng; Niu, Lulu; Zuo, Yi; Li, Jidong; Li, Yubao

2017-09-01

The dipping-drying procedure and cross-linking method were used to make drug-loaded chitosan (CS) coating on nano-hydroxyapatite/polyamide66 (nHA/PA66) composite porous scaffold, endowing the scaffold controlled drug release functionality. The prefabricated scaffold was immersed into an aqueous drug/CS solution in a vacuum condition and then crosslinked by vanillin. The structure, porosity, composition, compressive strength, swelling ratio, drug release and cytocompatibility of the pristine and coating scaffolds were investigated. After coating, the scaffold porosity and pore interconnection were slightly decreased. Cytocompatibility performance was observed through an in vitro experiment based on cell attachment and the MTT assay by MG63 cells which revealed positive cell viability and increasing proliferation over the 11-day period in vitro. The drug could effectively release from the coated scaffold in a controlled fashion and the release rate was sustained for a long period and highly dependent on coating swelling, suggesting the possibility of a controlled drug release. Our results demonstrate that the scaffold with drug-loaded crosslinked CS coating can be used as a simple technique to render the surfaces of synthetic scaffolds active, thus enabling them to be a promising high performance biomaterial in bone tissue engineering.

Direct Scaffolding of Biomimetic Hydroxyapatite-gelatin Nanocomposites using Aminosilane Cross-linker for Bone Regeneration

PubMed Central

Chiu, Chi-Kai; Ferreira, Joao; Luo, Tzy-Jiun M.; Geng, Haixia; Lin, Feng-Chang; Ko, Ching-Chang

2012-01-01

Hydroxyapatite-gelatin modified siloxane (GEMOSIL) nanocomposite was developed by coating, kneading and hardening processes to provide formable scaffolding for alloplastic graft applications. The present study aims to characterize scaffolding formability and mechanical properties of GEMOSIL, and to test the in vitro and in vivo biocompatibility of GEMOSIL. Buffer Solution initiated formable paste followed by the sol-gel reaction led to a final hardened composite. Results showed the adequate coating of aminosilane, 11–19 wt%, affected the cohesiveness of the powders and the final compressive strength (69 MPa) of the composite. TGA and TEM results showed the effective aminosilane coating that preserves hydroxyapatite-gelatin nanocrystals from damage. Both GEMOSIL with and without titania increased the mineralization of preosteoblasts in vitro. Only did titania additives revealed good in vivo bone formation in rat calvarium defects. The scaffolding formability, due to cohesive bonding among GEMOSIL particles, could be further refined to fulfill the complicated scaffold processes. PMID:22669282

Cartilaginous extracellular matrix-modified chitosan hydrogels for cartilage tissue engineering.

PubMed

Choi, Bogyu; Kim, Soyon; Lin, Brian; Wu, Benjamin M; Lee, Min

2014-11-26

Cartilaginous extracellular matrix (ECM) components such as type-II collagen (Col II) and chondroitin sulfate (CS) play a crucial role in chondrogenesis. However, direct clinical use of natural Col II or CS as scaffolds for cartilage tissue engineering is limited by their instability and rapid enzymatic degradation. Here, we investigate the incorporation of Col II and CS into injectable chitosan hydrogels designed to gel upon initiation by exposure to visible blue light (VBL) in the presence of riboflavin. Unmodified chitosan hydrogel supported proliferation and deposition of cartilaginous ECM by encapsulated chondrocytes and mesenchymal stem cells. The incorporation of native Col II or CS into chitosan hydrogels further increased chondrogenesis. The incorporation of Col II, in particular, was found to be responsible for the enhanced cellular condensation and chondrogenesis observed in modified hydrogels. This was mediated by integrin α10 binding to Col II, increasing cell-matrix adhesion. These findings demonstrate the potential of cartilage ECM-modified chitosan hydrogels as biomaterials to promote cartilage regeneration.

Robotic deposition and in vitro characterization of 3D gelatin-bioactive glass hybrid scaffolds for biomedical applications.

PubMed

Gao, Chunxia; Rahaman, Mohamed N; Gao, Qiang; Teramoto, Akira; Abe, Koji

2013-07-01

The development of inorganic-organic hybrid scaffolds with controllable degradation and bioactive properties is receiving considerable interest for bone and tissue regeneration. The objective of this study was to create hybrid scaffolds of gelatin and bioactive glass (BG) with a controlled, three-dimensional (3D) architecture by a combined sol-gel and robotic deposition (robocasting) method and evaluate their mechanical response, bioactivity, and response to cells in vitro. Inks for robotic deposition of the scaffolds were prepared by dissolving gelatin in a sol-gel precursor solution of the bioactive glass (70SiO2 -25CaO-5P2 O5 ; mol%) and aging the solution to form a gel with the requisite viscosity. After drying and crosslinking, the gelatin-BG scaffolds, with a grid-like architecture (filament diameter ∼350 µm; pore width ∼550 µm), showed an elasto-plastic response, with a compressive strength of 5.1 ± 0.6 MPa, in the range of values for human trabecular bone (2-12 MPa). When immersed in phosphate-buffered saline, the crosslinked scaffolds rapidly absorbed water (∼440% of its dry weight after 2 h) and showed an elastic response at deformations up to ∼60%. Immersion of the scaffolds in a simulated body fluid resulted in the formation of a hydroxyapatite-like surface layer within 5 days, indicating their bioactivity in vitro. The scaffolds supported the proliferation, alkaline phosphatase activity, and mineralization of osteogenic MC3T3-E1 cells in vitro, showing their biocompatibility. Altogether, the results indicate that these gelatin-BG hybrid scaffolds with a controlled, 3D architecture of inter-connected pores have potential for use as implants for bone regeneration. Copyright © 2012 Wiley Periodicals, Inc.

The Production of Porous Hydroxyapatite Scaffolds with Graded Porosity by Sequential Freeze-Casting.

PubMed

Lee, Hyun; Jang, Tae-Sik; Song, Juha; Kim, Hyoun-Ee; Jung, Hyun-Do

2017-03-31

Porous hydroxyapatite (HA) scaffolds with porosity-graded structures were fabricated by sequential freeze-casting. The pore structures, compressive strengths, and biocompatibilities of the fabricated porous HA scaffolds were evaluated. The porosities of the inner and outer layers of the graded HA scaffolds were controlled by adjusting the initial HA contents of the casting slurries. The interface between the dense and porous parts was compact and tightly adherent. The porosity and compressive strengths of the scaffold were controlled by the relative thicknesses of the dense/porous parts. In addition, the porous HA scaffolds showed good biocompatibility in terms of preosteoblast cell attachment and proliferation. The results suggest that porous HA scaffolds with load-bearing parts have potential as bone grafts in hard-tissue engineering.

The Production of Porous Hydroxyapatite Scaffolds with Graded Porosity by Sequential Freeze-Casting

PubMed Central

Lee, Hyun; Jang, Tae-Sik; Song, Juha; Kim, Hyoun-Ee; Jung, Hyun-Do

2017-01-01

Porous hydroxyapatite (HA) scaffolds with porosity-graded structures were fabricated by sequential freeze-casting. The pore structures, compressive strengths, and biocompatibilities of the fabricated porous HA scaffolds were evaluated. The porosities of the inner and outer layers of the graded HA scaffolds were controlled by adjusting the initial HA contents of the casting slurries. The interface between the dense and porous parts was compact and tightly adherent. The porosity and compressive strengths of the scaffold were controlled by the relative thicknesses of the dense/porous parts. In addition, the porous HA scaffolds showed good biocompatibility in terms of preosteoblast cell attachment and proliferation. The results suggest that porous HA scaffolds with load-bearing parts have potential as bone grafts in hard-tissue engineering. PMID:28772735

Chondroitin Sulfate, Hyaluronic Acid and Chitin/Chitosan Production Using Marine Waste Sources: Characteristics, Applications and Eco-Friendly Processes: A Review

PubMed Central

Vázquez, José Antonio; Rodríguez-Amado, Isabel; Montemayor, María Ignacia; Fraguas, Javier; del Pilar González, María; Murado, Miguel Anxo

2013-01-01

In the last decade, an increasing number of glycosaminoglycans (GAGs), chitin and chitosan applications have been reported. Their commercial demands have been extended to different markets, such as cosmetics, medicine, biotechnology, food and textiles. Marine wastes from fisheries and aquaculture are susceptible sources for polymers but optimized processes for their recovery and production must be developed to satisfy such necessities. In the present work, we have reviewed different alternatives reported in the literature to produce and purify chondroitin sulfate (CS), hyaluronic acid (HA) and chitin/chitosan (CH/CHs) with the aim of proposing environmentally friendly processes by combination of various microbial, chemical, enzymatic and membranes strategies and technologies. PMID:23478485

Tissue response and biodegradation of composite scaffolds prepared from Thai silk fibroin, gelatin and hydroxyapatite.

PubMed

Tungtasana, Hathairat; Shuangshoti, Somruetai; Shuangshoti, Shanop; Kanokpanont, Sorada; Kaplan, David L; Bunaprasert, Tanom; Damrongsakkul, Siriporn

2010-12-01

This work aimed to investigate tissue responses and biodegradation, both in vitro and in vivo, of four types of Bombyx mori Thai silk fibroin based-scaffolds. Thai silk fibroin (SF), conjugated gelatin/Thai silk fibroin (CGSF), hydroxyapatite/Thai silk fibroin (SF4), and hydroxyapatite/conjugated gelatin/Thai silk fibroin (CGSF4) scaffolds were fabricated using salt-porogen leaching, dehydrothermal/chemical crosslinking and an alternate soaking technique for mineralization. In vitro biodegradation in collagenase showed that CGSF scaffolds had the slowest biodegradability, due to the double crosslinking by dehydrothermal and chemical treatments. The hydroxyapatite deposited from alternate soaking separated from the surface of the protein scaffolds when immersed in collagenase. From in vivo biodegradation studies, all scaffolds could still be observed after 12 weeks of implantation in subcutaneous tissue of Wistar rats and also following ISO10993-6: Biological evaluation of medical devices. At 2 and 4 weeks of implantation the four types of Thai silk fibroin based-scaffolds were classified as "non-irritant" to "slight-irritant", compared to Gelfoam(®) (control samples). These natural Thai silk fibroin-based scaffolds may provide suitable biomaterials for clinical applications.

3D- Printed Poly(ε-caprolactone) Scaffold Integrated with Cell-laden Chitosan Hydrogels for Bone Tissue Engineering.

PubMed

Dong, Liang; Wang, Shao-Jie; Zhao, Xin-Rong; Zhu, Yu-Fang; Yu, Jia-Kuo

2017-10-17

Synthetic polymeric scaffolds are commonly used in bone tissue engineering (BTE) due to their biocompatibility and adequate mechanical properties. However, their hydrophobicity and the lack of specific cell recognition sites confined their practical application. In this study, to improve the cell seeding efficiency and osteoinductivity, an injectable thermo-sensitive chitosan hydrogel (CSG) was incorporated into a 3D-printed poly(ε-caprolactone) (PCL) scaffold to form a hybrid scaffold. To demonstrate the feasibility of this hybrid system for BTE application, rabbit bone marrow mesenchymal stem cells (BMMSCs) and bone morphogenetic protein-2 (BMP-2) were encapsulated in CSG. Pure PCL scaffolds were used as controls. Cell proliferation and viability were investigated. Osteogenic gene expressions of BMMSCs in various scaffolds were determined with reverse transcription polymerase chain reaction (RT-PCR). Growth factor releasing profile and mechanical tests were performed. CCK-8 assay confirmed greater cell retention and proliferation in chitosan and hybrid groups. Confocal microscopy showed even distribution of cells in the hybrid system. After 2-week osteogenic culture in vitro, BMMSCs in hybrid and chitosan scaffolds showed stronger osteogenesis and bone-matrix formation. To conclude, chitosan/PCL hybrid scaffolds are a favorable platform for BTE due to its capacity to carry cells and drugs, and excellent mechanical strength.

Chitosan nanofiber scaffold improves bone healing via stimulating trabecular bone production due to upregulation of the Runx2/osteocalcin/alkaline phosphatase signaling pathway

PubMed Central

Ho, Ming-Hua; Yao, Chih-Jung; Liao, Mei-Hsiu; Lin, Pei-I; Liu, Shing-Hwa; Chen, Ruei-Ming

2015-01-01

Osteoblasts play critical roles in bone formation. Our previous study showed that chitosan nanofibers can stimulate osteoblast proliferation and maturation. This translational study used an animal model of bone defects to evaluate the effects of chitosan nanofiber scaffolds on bone healing and the possible mechanisms. In this study, we produced uniform chitosan nanofibers with fiber diameters of approximately 200 nm. A bone defect was surgically created in the proximal femurs of male C57LB/6 mice, and then the left femur was implanted with chitosan nanofiber scaffolds for 21 days and compared with the right femur, which served as a control. Histological analyses revealed that implantation of chitosan nanofiber scaffolds did not lead to hepatotoxicity or nephrotoxicity. Instead, imaging analyses by X-ray transmission and microcomputed tomography showed that implantation of chitosan nanofiber scaffolds improved bone healing compared with the control group. In parallel, microcomputed tomography and bone histomorphometric assays further demonstrated augmentation of the production of new trabecular bone in the chitosan nanofiber-treated group. Furthermore, implantation of chitosan nanofiber scaffolds led to a significant increase in the trabecular bone thickness but a reduction in the trabecular parameter factor. As to the mechanisms, analysis by confocal microscopy showed that implantation of chitosan nanofiber scaffolds increased levels of Runt-related transcription factor 2 (Runx2), a key transcription factor that regulates osteogenesis, in the bone defect sites. Successively, amounts of alkaline phosphatase and osteocalcin, two typical biomarkers that can simulate bone maturation, were augmented following implantation of chitosan nanofiber scaffolds. Taken together, this translational study showed a beneficial effect of chitosan nanofiber scaffolds on bone healing through stimulating trabecular bone production due to upregulation of Runx2-mediated alkaline

Collagen-chitosan scaffold - Lauric acid plasticizer for skin tissue engineering on burn cases

NASA Astrophysics Data System (ADS)

Widiyanti, Prihartini; Setyadi, Ewing Dian; Rudyardjo, Djony Izak

2017-02-01

The prevalence of burns in the world is more than 800 cases per one million people each year and this is the second highest cause of death due to trauma after traffic accident. Many studies are turning to skin substitute methods of tissue engineering. The purpose of this study is to determine the composition of the collagen, chitosan, and lauric acid scaffold, as well as knowing the results of the characterization of the scaffold. The synthesis of chitosan collagen lauric acid scaffold as a skin tissue was engineered using freeze dried method. Results from making of collagen chitosan lauric acid scaffold was characterized physically, biologically and mechanically by SEM, cytotoxicity, biodegradation, and tensile strength. From the morphology test, the result obtained is that pore diameter size ranges from 94.11 to 140.1 µm for samples A,B,C,D, which are in the range of normal pore size 63-150 µm, while sample E has value below the standard which is about 37.87 to 47.36 µm. From cytotoxicity assay, the result obtained is the percentage value of living cells between 20.11 to 21.51%. This value is below 50% the standard value of living cells. Incompatibility is made possible because of human error mainly the replication of washing process over the standard. Degradation testing obtained values of 19.44% - 40% by weight which are degraded during the 7 days of observation. Tensile test results obtained a range of values of 0.192 - 3.53 MPa. Only sample A (3.53 MPa) and B (1.935 MPa) meet the standard values of skin tissue scaffold that is 1-24 MPa. Based on the results of the characteristics of this study, composite chitosan collagen scaffold with lauric acid plasticizer has a potential candidate for skin tissue engineering for skin burns cases.

Microstructure and in vitro cellular response to novel soy protein-based porous structures for tissue regeneration applications.

PubMed

Olami, Hilla; Zilberman, Meital

2016-02-01

Interest in the development of new bioresorbable structures for various tissue engineering applications is on the rise. In the current study, we developed and studied novel soy protein-based porous blends as potential new scaffolds for such applications. Soy protein has several advantages over the various types of natural proteins employed for biomedical applications due to its low price, non-animal origin and relatively long storage time and stability. In the present study, blends of soy protein with other polymers (gelatin, pectin and alginate) were added and chemically cross-linked using the cross-linking agents carbodiimide or glyoxal, and the porous structure was obtained through lyophilization. The resulting blend porous structures were characterized using environmental scanning microscopy, and the cytotoxicity of these scaffolds was examined in vitro. The biocompatibility of the scaffolds was also evaluated in vitro by seeding and culturing human fibroblasts on these scaffolds. Cell growth morphology and adhesion were examined histologically. The results show that these blends can be assembled into porous three-dimensional structures by combining chemical cross-linking with freeze-drying. The achieved blend structures combine suitable porosity with a large pore size (100-300 µm). The pore structure in the soy-alginate scaffolds possesses adequate interconnectivity compared to that of the soy-gelatin scaffolds. However, porous structure was not observed for the soy-pectin blend, which presented a different structure with significantly lower porosities than all other groups. The in vitro evaluation of these porous soy blends demonstrated that soy-alginate blends are advantageous over soy-gelatin blends and exhibited adequate cytocompatibility along with better cell infiltration and stability. These soy protein scaffolds may be potentially useful as a cellular/acellular platform for skin regeneration applications. © The Author(s) 2015.

Supermacroprous chitosan–agarose–gelatin cryogels: in vitro characterization and in vivo assessment for cartilage tissue engineering

PubMed Central

Bhat, Sumrita; Tripathi, Anuj; Kumar, Ashok

2011-01-01

The study focuses on the synthesis of a novel polymeric scaffold having good porosity and mechanical characteristics synthesized by using natural polymers and their optimization for application in cartilage tissue engineering. The scaffolds were synthesized via cryogelation technology using an optimized ratio of the polymer solutions (chitosan, agarose and gelatin) and cross-linker followed by the incubation at sub-zero temperature (−12°C). Microstructure examination of the chitosan–agarose–gelatine (CAG) cryogels was done using scanning electron microscopy (SEM) and fluorescent microscopy. Mechanical analysis, such as the unconfined compression test, demonstrated that cryogels with varying chitosan concentrations, i.e. 0.5–1% have a high compression modulus. In addition, fatigue tests revealed that scaffolds are suitable for bioreactor studies where gels are subjected to continuous cyclic strain. In order to confirm the stability, cryogels were subjected to high frequency (5 Hz) with 30 per cent compression of their original length up to 1 × 105 cycles, gels did not show any significant changes in their mass and dimensions during the experiment. These cryogels have exhibited degradation capacity under aseptic conditions. CAG cryogels showed good cell adhesion of primary goat chondrocytes examined by SEM. Cytotoxicity of the material was checked by MTT assay and results confirmed the biocompatibility of the material. In vivo biocompatibility of the scaffolds was checked by the implantation of the scaffolds in laboratory animals. These results suggest the potential of CAG cryogels as a good three-dimensional scaffold for cartilage tissue engineering. PMID:20943683

In situ mineralization of hydroxyapatite on electrospun chitosan-based nanofibrous scaffolds.

PubMed

Yang, Dongzhi; Jin, Yu; Zhou, Yingshan; Ma, Guiping; Chen, Xiangmei; Lu, Fengmin; Nie, Jun

2008-03-10

A biocomposite of hydroxyapatite (HAp) with electrospun nanofibrous scaffolds was prepared by using chitosan/polyvinyl alcohol (CS/PVA) and N-carboxyethyl chitosan/PVA (CECS/PVA) electrospun membranes as organic matrix, and HAp was formed in supersaturated CaCl2 and KH2PO4 solution. The influences of carboxylic acid groups in CECS/PVA fibrous scaffold and polyanionic additive poly(acrylic acid) (PAA) in the incubation solution on the crystal distribution of the HAp were investigated. Field-emission scanning electron microscopy (FE-SEM), energy-dispersive spectroscopy (EDS), wide-angle X-ray diffraction (WAXD), and Fourier transform infrared (FTIR) were used to characterize the morphology and structure of the deposited mineral phase on the scaffolds. It was found that addition of PAA to the mineral solution and use of matrix with carboxylic acid groups promoted mineral growth and distribution of HAp. MTT testing and SEM imaging from mouse fibroblast (L929) cell culture revealed the attachment and growth of mouse fibroblast on the surface of biocomposite scaffold, and that the cell morphology and viability were satisfactory for the composite to be used in bioapplications.

Immunological compatibility status of placenta-derived stem cells is mediated by scaffold 3D structure.

PubMed

Azizian, Sara; Khatami, Fatemeh; Modaresifar, Khashayar; Mosaffa, Nariman; Peirovi, Habibollah; Tayebi, Lobat; Bahrami, Soheyl; Redl, Heinz; Niknejad, Hassan

2018-02-23

Placenta-derived amniotic epithelial cells (AECs), a great cell source for tissue engineering and stem cell therapy, are immunologically inert in their native state; however, immunological changes in these cells after culture and differentiation have challenged their applications. The aim of this study was to investigate the effect of 2D and 3D scaffolds on human lymphocyte antigens (HLA) expression by AECs. The effect of different preparation parameters including pre-freezing time and temperature was evaluated on 3D chitosan-gelatine scaffolds properties. Evaluation of MHC class I, HLA-DR and HLA-G expression in AECs after 7 d culture on 2D bed and 3D scaffold of chitosan-gelatine showed that culture of AECs on the 2D substrate up-regulated MHC class I and HLA-DR protein markers on AECs surface and down-regulated HLA-G protein. In contrast, 3D scaffold did not increase protein expression of MHC class I and HLA-DR. Moreover, HLA-G protein expression remained unchanged in 3D culture. These results confirm that 3D scaffold can remain AECs in their native immunological state and modification of physical properties of the scaffold is a key regulator of immunological markers at the gene and protein expression levels; a strategy which circumvents rejection challenge of amniotic stem cells to be translated into the clinic.

Effect of doping in carbon nanotubes on the viability of biomimetic chitosan-carbon nanotubes-hydroxyapatite scaffolds.

PubMed

Fonseca-García, Abril; Mota-Morales, Josué D; Quintero-Ortega, Iraís A; García-Carvajal, Zaira Y; Martínez-López, V; Ruvalcaba, Erika; Landa-Solís, Carlos; Solis, Lilia; Ibarra, Clemente; Gutiérrez, María C; Terrones, Mauricio; Sanchez, Isaac C; del Monte, Francisco; Velasquillo, María C; Luna-Bárcenas, G

2014-10-01

This work describes the preparation and characterization of biomimetic chitosan/multiwall carbon nanotubes/nano-hydroxyapatite (CTS/MWCNT/nHAp) scaffolds and their viability for bone tissue engineering applications. The cryogenic process ice segregation-induced self-assembly (ISISA) was used to fabricate 3D biomimetic CTS scaffolds. Proper combination of cryogenics, freeze-drying, nature and molecular ratio of solutes give rise to 3D porous interconnected scaffolds with clusters of nHAp distributed along the scaffold surface. The effect of doping in CNT (e.g. with oxygen and nitrogen atoms) on cell viability was tested. Under the same processing conditions, pore size was in the range of 20-150 μm and irrespective on the type of CNT. Studies on cell viability with scaffolds were carried out using human cells from periosteum biopsy. Prior to cell seeding, the immunophenotype of mesenchymal periosteum or periosteum-derived stem cells (MSCs-PCs) was characterized by flow cytometric analysis using fluorescence-activated and characteristic cell surface markers for MSCs-PCs. The characterized MSCs-PCs maintained their periosteal potential in cell cultures until the 2nd passage from primary cell culture. Thus, the biomimetic CTS/MWCNT/nHAp scaffolds demonstrated good biocompatibility and cell viability in all cases such that it can be considered as promising biomaterials for bone tissue engineering. © 2013 Wiley Periodicals, Inc.

Injectable and porous PLGA microspheres that form highly porous scaffolds at body temperature.

PubMed

Qutachi, Omar; Vetsch, Jolanda R; Gill, Daniel; Cox, Helen; Scurr, David J; Hofmann, Sandra; Müller, Ralph; Quirk, Robin A; Shakesheff, Kevin M; Rahman, Cheryl V

2014-12-01

Injectable scaffolds are of interest in the field of regenerative medicine because of their minimally invasive mode of delivery. For tissue repair applications, it is essential that such scaffolds have the mechanical properties, porosity and pore diameter to support the formation of new tissue. In the current study, porous poly(dl-lactic acid-co-glycolic acid) (PLGA) microspheres were fabricated with an average size of 84±24μm for use as injectable cell carriers. Treatment with ethanolic sodium hydroxide for 2min was observed to increase surface porosity without causing the microsphere structure to disintegrate. This surface treatment also enabled the microspheres to fuse together at 37°C to form scaffold structures. The average compressive strength of the scaffolds after 24h at 37°C was 0.9±0.1MPa, and the average Young's modulus was 9.4±1.2MPa. Scaffold porosity levels were 81.6% on average, with a mean pore diameter of 54±38μm. This study demonstrates a method for fabricating porous PLGA microspheres that form solid porous scaffolds at body temperature, creating an injectable system capable of supporting NIH-3T3 cell attachment and proliferation in vitro. Copyright © 2014 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

Electrospinning of gelatin and SMPU with carbon nanotubes for tissue engineering scaffolds.

PubMed

Mejia, Monica A; Hoyos, Lina M; Zapata, Jenniffer; Restrepo, Luz M; Moneada, Maria E

2016-08-01

The nanofibres created by electrospinning technique are currently used for a variety of applications in tissue engineering; and Gelatin and Polyurethane Shape-Memory (SMPU) have important results in biomedicine. Similarly, carbon nanotubes combined with other biomaterials change important properties, opening new opportunities for biomedical applications. In this work, we constructed scaffold using electrospinning technique based in bovine-hide gelatin, SMPU and both materials hybrid with carbon nanotube. Morphology and cytotoxicity were evaluated and mechanical properties for two materials were obtained in scaffold building. Morphological, mechanical and citotoxic properties of the electrospun fibers were found to be dependent of alteration in materials concentration, electrospinning conditions and MWCNT concentration. According to morphological, cytotoxic and mechanical analysis, SMPU more MWCNT were the best material, with nanofibers of 451 nm, tensile strength of 1.912 MPa, and a high ratio surface volume.

Composite Scaffolds Containing Silk Fibroin, Gelatin, and Hydroxyapatite for Bone Tissue Regeneration and 3D Cell Culturing

PubMed Central

Moisenovich, M. M.; Arkhipova, A. Yu.; Orlova, A. A.; Drutskaya, M. S; Volkova, S. V.; Zacharov, S. E.; Agapov, I. I.; Kirpichnikov, M. P.

2014-01-01

Three-dimensional (3D) silk fibroin scaffolds were modified with one of the major bone tissue derivatives (nano-hydroxyapatite) and/or a collagen derivative (gelatin). Adhesion and proliferation of mouse embryonic fibroblasts (MEF) within the scaffold were increased after modification with either nano-hydroxyapatite or gelatin. However, a significant increase in MEF adhesion and proliferation was observed when both additives were introduced into the scaffold. Such modified composite scaffolds provide a new and better platform to study wound healing, bone and other tissue regeneration, as well as artificial organ bioengineering. This system can further be applied to establish experimental models to study cell-substrate interactions, cell migration and other complex processes, which may be difficult to address using the conventional two-dimensional culture systems. PMID:24772332

Characterization of Electrospun Nanofibrous Scaffolds for Nanobiomedical Applications

NASA Astrophysics Data System (ADS)

Emul, E.; Saglam, S.; Ates, H.; Korkusuz, F.; Saglam, N.

2016-08-01

The electrospinning method is employed in the production of porous fiber scaffolds, and the usage of electrospun scaffolds especially as drug carrier and bone reconstructive material such as implants is promising for future applications in tissue engineering. The number of publications has grown very rapidly in this field through the fabrication of complex scaffolds, novel approaches in nanotechnology, and improvements of imaging methods. Hence, characterization of these materials has also grown significantly important for getting satisfied and accurate results. This advantageous and versatile method is ideal for mimicking bone extracellular matrix, and many biodegradable and biocompatible polymers are preferred in the field of bone reconstruction. In this study, gelatin, gelatin/nanohydroxyapatite (nHAp) and gelatin/PLLA/nHAp scaffolds were fabricated by the electrospinning process. These composite fibers showed clear and continuous morphology according to observation through a scanning electron microscope and their component analyses were also determined by Fourier transform infrared spectrometer analyses. These characterization experiments revealed the great effects of the electrospinning method for biomedical applications and have an especially important role in bone reconstruction and production of implant coating material.

Adipose-derived stem cells and BMP-2 delivery in chitosan-based 3D constructs to enhance bone regeneration in a rat mandibular defect model.

PubMed

Fan, Jiabing; Park, Hyejin; Lee, Matthew K; Bezouglaia, Olga; Fartash, Armita; Kim, Jinku; Aghaloo, Tara; Lee, Min

2014-08-01

Reconstructing segmental mandiblular defects remains a challenge in the clinic. Tissue engineering strategies provide an alternative option to resolve this problem. The objective of the present study was to determine the effects of adipose-derived stem cells (ASCs) and bone morphogenetic proteins-2 (BMP-2) in three-dimensional (3D) scaffolds on mandibular repair in a small animal model. Noggin expression levels in ASCs were downregulated by a lentiviral short hairpin RNA strategy to enhance ASC osteogenesis (ASCs(Nog-)). Chitosan (CH) and chondroitin sulfate (CS), natural polysaccharides, were fabricated into 3D porous scaffolds, which were further modified with apatite coatings for enhanced cellular responses and efficient delivery of BMP-2. The efficacy of 3D apatite-coated CH/CS scaffolds supplemented with ASCs(Nog-) and BMP-2 were evaluated in a rat critical-sized mandibular defect model. After 8 weeks postimplantation, the scaffolds treated with ASCs(Nog-) and BMP-2 significantly promoted rat mandibular regeneration as demonstrated by micro-computerized tomography, histology, and immunohistochemistry, compared with the groups treated with ASCs(Nog-) or BMP-2 alone. These results suggest that our combinatorial strategy of ASCs(Nog-)+BMP-2 in 3D apatite microenvironments can significantly promote mandibular regeneration, and these may provide a potential tissue engineering approach to repair large bony defects.

Effects of chitosan-coated fibers as a scaffold for three-dimensional cultures of rabbit fibroblasts for ligament tissue engineering.

PubMed

Sarukawa, Junichiro; Takahashi, Masaaki; Abe, Masashi; Suzuki, Daisuke; Tokura, Seiichi; Furuike, Tetsuya; Tamura, Hiroshi

2011-01-01

Material selection in tissue-engineering scaffolds is one of the primary factors defining cellular response and matrix formation. In this study, we fabricated chitosan-coated poly(lactic acid) (PLA) fiber scaffolds to test our hypothesis that PLA fibers coated with chitosan highly promoted cell supporting properties compared to those without chitosan. Both PLA fibers (PLA group) and chitosan-coated PLA fibers (PLA-chitosan group) were fabricated for this study. Anterior cruciate ligament (ACL) fibroblasts were isolated from Japanese white rabbits and cultured on scaffolds consisting of each type of fiber. The effects of cell adhesivity, proliferation, and synthesis of the extracellular matrix (ECM) for each fiber were analyzed by cell counting, hydroxyproline assay, scanning electron microscopy and quantitative RT-PCR. Cell adhesivity, proliferation, hydroxyproline content and the expression of type-I collagen mRNA were significantly higher in the PLA-chitosan group than in the PLA group. Scanning electron microscopic observation showed that fibroblasts proliferated with a high level of ECM synthesis around the cells. Chitosan coating improved ACL fibroblast adhesion and proliferation, and had a positive effect on matrix production. Thus, the advantages of chitosan-coated PLA fibers show them to be a suitable biomaterial for ACL tissue-engineering scaffolds.

Differentiation of bone marrow stromal cells in poly(lactide-co-glycolide)/chitosan scaffolds.

PubMed

Kuo, Yung-Chih; Yeh, Chun-Fu; Yang, Jen-Tsung

2009-12-01

This study investigates the physicochemical properties of poly(lactide-co-glycolide) (PLGA)/chitosan scaffolds and the neuron growth factor (NGF)-guided differentiation of bone marrow stromal cells (BMSCs) in the scaffolds. The scaffolds were prepared by the crosslinking of 1-(3-dimethylaminopropyl)-3-ethylcarbodiimide hydrochloride, N-hydroxysuccinimide and genipin, and the differentiating BMSCs were characterized against CD44, CD90 and NeuN. The scaffold with 20% PLGA yielded 95% porosity, Young's modulus of 13MPa, 70% adhesion of BMSCs and 1.6-fold increase in the cell viability over 7-day cultivation. BMSCs without guidance in the PLGA/chitosan scaffolds were prone to differentiate toward osteoblasts with apparent deposition of calcium. When NGF was introduced, an increased weight percentage of PLGA yielded more identified neurons. In addition, mature neurons emerged from the PLGA-rich biomaterials after induction with NGF over 2 days. A proper control over the physical and biomedical property of the scaffolds and the NGF-guided differentiation of BMSCs can be promising for nerve regeneration.

Evaluation of the kinetic and relaxation time of gentamicin sulfate released from hybrid biomaterial Bioglass-chitosan scaffolds

NASA Astrophysics Data System (ADS)

Wers, E.; Oudadesse, H.; Lefeuvre, B.; Merdrignac-Conanec, O.; Barroug, A.

2015-10-01

Chitosan scaffolds, combined with bioactive glass 46S6, were prepared to serve as gentamicin sulfate delivery in situ systems for bone biomaterials. This work presents a study about the effect of the ratio chitosan/bioactive glass (CH/BG) on the release of gentamicin sulfate and on the bioactivity during in vitro experiments. SEM observations allowed understanding the bond between the glass grains and the chitosan matrix. In vitro results showed that scaffolds form a hydroxyapatite (HA) Ca10(PO4)6(OH)2 after 15 days of immersion in a simulated body fluid (SBF).The interest of this study is to see that the increase of the content of bioactive glass in the chitosan matrix slows the release of gentamicin sulfate in the liquid medium. Starting concentration of gentamicin sulfate has an influence on the relaxation time of the scaffolds. Indeed, an increasing concentration delays the return to a new equilibrium. Contents of chitosan and bioactive glass do not affect the relaxation time. Synthesized scaffolds could be adapted to a clinical situation: severity and type of infection, weight and age of the patient.

Effect of laminated hydroxyapatite/gelatin nanocomposite scaffold structure on osteogenesis using unrestricted somatic stem cells in rat.

PubMed

Tavakol, Shima; Azami, Mahmoud; Khoshzaban, Ahad; Ragerdi Kashani, Iraj; Tavakol, Behnaz; Hoveizi, Elham; Rezayat Sorkhabadi, Seyed Mahdi

2013-11-01

Bone matrix consists of two major phases at the nanoscale: organic and hydroxyapatite. Nanotechnology as a diverse and interdisciplinary area of research has the capacity to revolutionise many areas of applications such as bone tissue engineering. Nanohydroxyapatite/gelatin composite has higher osteoblast attachment and proliferation than micro-sized ones, and shorter culturing period and lower cell seeding density compared to pure gelatin. A nanostructured scaffold was fabricated by three methods for bone repair using nanohydroxyapatite and gelatin as the main components. Its biocompatibility, alizarin red test on the 14th and 21st days, gene expression on the 21st day in in vitro using and histomorphometry after 4 and 8 weeks post-implantation in the rat were investigated. Cultured unrestricted somatic stem cells used for in vitro study showed an excellent level of cell attachment to the scaffold. Cells induced more osteoblast differentiation on the scaffold than in 2D cell culture. Osteoblast differentiation and bone regeneration results of in vitro and in vivo investigation on scaffold were extremely significant, better than control and treatment groups. These effects could be attributed to the shape and size of nanoHA particles and good architecture of the scaffold. The results confirm the feasibility of bone regeneration using synthesised scaffold as a temporary bone substitute. © 2013 International Federation for Cell Biology.

Optimization, characterization, and efficacy evaluation of 2% chitosan scaffold for tissue engineering and wound healing

PubMed Central

Chhabra, Priyanka; Tyagi, Priyanka; Bhatnagar, Aseem; Mittal, Gaurav; Kumar, Amit

2016-01-01

Objective: To develop a chitosan-based scaffold and carry out a complete comprehensive study encompassing optimization of exact chitosan strength, product characterization, toxicity evaluation, in vitro validation in cell culture experiments, and finally in vivo efficacy in animal excision wound model. Materials and Methods: Developed chitosan scaffolds (CSs) were optimized for tissue engineering and wound healing efficacy by means of microstructure, toxicity, and biocompatibility evaluation. Results: Scanning electron microscope (SEM) studies revealed that porosity of CS decreased with increase in chitosan concentration. Chemical stability and integrity of scaffolds were confirmed by Fourier transform infrared studies. Highest swelling percentage (SP) of 500% was observed in 2%, while lowest (200%) was observed in 1% CS. Reabsorption and noncytotoxic property of optimized scaffold were established by enzymatic degradation and MTT assay. Enzymatic degradation suggested 20–45% of weight loss (WL) within 14 days of incubation. Cytotoxicity analysis showed that scaffolds were noncytotoxic against normal human dermal fibroblast human dermal fibroblast cell lines. Significant cellular adherence over the scaffold surface with normal cellular morphology was confirmed using SEM analysis. In vivo efficacy evaluation was carried out by means of reduction in wound size on Sprague-Dawley rats. Sprague-Dawley rats treated with optimized scaffold showed ~ 100% wound healing in comparison to ~80% healing in betadine-treated animals within 14 days. Histological examination depicted advance re-epithelization with better organization of collagen bundle in wound area treated with 2% CS in comparison to conventional treatment or no treatment. Conclusion: This study, thus, reveals that 2% CSs were found to have a great potential in wound healing. PMID:28216954

A review: fabrication of porous polyurethane scaffolds.

PubMed

Janik, H; Marzec, M

2015-03-01

The aim of tissue engineering is the fabrication of three-dimensional scaffolds that can be used for the reconstruction and regeneration of damaged or deformed tissues and organs. A wide variety of techniques have been developed to create either fibrous or porous scaffolds from polymers, metals, composite materials and ceramics. However, the most promising materials are biodegradable polymers due to their comprehensive mechanical properties, ability to control the rate of degradation and similarities to natural tissue structures. Polyurethanes (PUs) are attractive candidates for scaffold fabrication, since they are biocompatible, and have excellent mechanical properties and mechanical flexibility. PU can be applied to various methods of porous scaffold fabrication, among which are solvent casting/particulate leaching, thermally induced phase separation, gas foaming, emulsion freeze-drying and melt moulding. Scaffold properties obtained by these techniques, including pore size, interconnectivity and total porosity, all depend on the thermal processing parameters, and the porogen agent and solvents used. In this review, various polyurethane systems for scaffolds are discussed, as well as methods of fabrication, including the latest developments, and their advantages and disadvantages. Copyright © 2014. Published by Elsevier B.V.

Natural stimulus responsive scaffolds/cells for bone tissue engineering: influence of lysozyme upon scaffold degradation and osteogenic differentiation of cultured marrow stromal cells induced by CaP coatings.

PubMed

Martins, Ana M; Pham, Quynh P; Malafaya, Patrícia B; Raphael, Robert M; Kasper, F Kurtis; Reis, Rui L; Mikos, Antonios G

2009-08-01

This work proposes the use of nonporous, smart, and stimulus responsive chitosan-based scaffolds for bone tissue engineering applications. The overall vision is to use biodegradable scaffolds based on chitosan and starch that present properties that will be regulated by bone regeneration, with the capability of gradual in situ pore formation. Biomimetic calcium phosphate (CaP) coatings were used as a strategy to incorporate lysozyme at the surface of chitosan-based materials with the main objective of controlling and tailoring their degradation profile as a function of immersion time. To confirm the concept, degradation tests with a lysozyme concentration similar to that incorporated into CaP chitosan-based scaffolds were used to study the degradation of the scaffolds and the formation of pores as a function of immersion time. Degradation studies with lysozyme (1.5 g/L) showed the formation of pores, indicating an increase of porosity ( approximately 5-55% up to 21 days) resulting in porous three-dimensional structures with interconnected pores. Additional studies investigated the influence of a CaP biomimetic coating on osteogenic differentiation of rat marrow stromal cells (MSCs) and showed enhanced differentiation of rat MSCs seeded on the CaP-coated chitosan-based scaffolds with lysozyme incorporated. At all culture times, CaP-coated chitosan-based scaffolds with incorporated lysozyme demonstrated greater osteogenic differentiation of MSCs, bone matrix production, and mineralization as demonstrated by calcium deposition measurements, compared with controls (uncoated scaffolds). The ability of these CaP-coated chitosan-based scaffolds with incorporated lysozyme to create an interconnected pore network in situ coupled with the demonstrated positive effect of these scaffolds upon osteogenic differentiation of MSCs and mineralized matrix production illustrates the strong potential of these scaffolds for application in bone tissue engineering strategies.

A compound scaffold with uniform longitudinally oriented guidance cues and a porous sheath promotes peripheral nerve regeneration in vivo.

PubMed

Huang, Liangliang; Zhu, Lei; Shi, Xiaowei; Xia, Bing; Liu, Zhongyang; Zhu, Shu; Yang, Yafeng; Ma, Teng; Cheng, Pengzhen; Luo, Kai; Huang, Jinghui; Luo, Zhuojing

2018-03-01

Scaffolds with inner fillers that convey directional guidance cues represent promising candidates for nerve repair. However, incorrect positioning or non-uniform distribution of intraluminal fillers might result in regeneration failure. In addition, proper porosity (to enhance nutrient and oxygen exchange but prevent fibroblast infiltration) and mechanical properties (to ensure fixation and to protect regenerating axons from compression) of the outer sheath are also highly important for constructing advanced nerve scaffolds. In this study, we constructed a compound scaffold using a stage-wise strategy, including directionally freezing orientated collagen-chitosan (O-CCH) filler, electrospinning poly(ε-caprolactone) (PCL) sheaths and assembling O-CCH/PCL scaffolds. Based on scanning electron microscopy (SEM) and mechanical tests, a blend of collagen/chitosan (1:1) was selected for filler fabrication, and a wall thickness of 400 μm was selected for PCL sheath production. SEM and three-dimensional (3D) reconstruction further revealed that the O-CCH filler exhibited a uniform, longitudinally oriented microstructure (over 85% of pores were 20-50 μm in diameter). The electrospun PCL porous sheath with pore sizes of 6.5 ± 3.3 μm prevented fibroblast invasion. The PCL sheath exhibited comparable mechanical properties to commercially available nerve conduits, and the O-CCH filler showed a physiologically relevant substrate stiffness of 2.0 ± 0.4 kPa. The differential degradation time of the filler and sheath allows the O-CCH/PCL scaffold to protect regenerating axons from compression stress while providing enough space for regenerating nerves. In vitro and in vivo studies indicated that the O-CCH/PCL scaffolds could promote axonal regeneration and Schwann cell migration. More importantly, functional results indicated that the CCH/PCL compound scaffold induced comparable functional recovery to that of the autograft group at the end of the study. Our

Chitosan-hyaluronan/nano chondroitin sulfate ternary composite sponges for medical use.

PubMed

Anisha, B S; Sankar, Deepthi; Mohandas, Annapoorna; Chennazhi, K P; Nair, Shantikumar V; Jayakumar, R

2013-02-15

In this work chitosan-hyaluronan composite sponge incorporated with chondroitin sulfate nanoparticle (nCS) was developed. The fabrication of hydrogel was based on simple ionic cross-linking using EDC, followed by lyophilization to obtain the composite sponge. nCS suspension was characterized using DLS and SEM and showed a size range of 100-150 nm. The composite sponges were characterized using SEM, FT-IR and TG-DTA. Porosity, swelling, biodegradation, blood clotting and platelet activation of the prepared sponges were also evaluated. Nanocomposites showed a porosity of 67% and showed enhanced swelling and blood clotting ability. Cytocompatibility and cell adhesion studies of the sponges were done using human dermal fibroblast (HDF) cells and the nanocomposite sponges showed more than 90% viability. Nanocomposite sponges also showed enhanced proliferation of HDF cells within two days of study. These results indicated that this nanocomposite sponges would be a potential candidate for wound dressing. Copyright © 2012 Elsevier Ltd. All rights reserved.

Injectable and porous PLGA microspheres that form highly porous scaffolds at body temperature

PubMed Central

Qutachi, Omar; Vetsch, Jolanda R.; Gill, Daniel; Cox, Helen; Scurr, David J.; Hofmann, Sandra; Müller, Ralph; Quirk, Robin A.; Shakesheff, Kevin M.; Rahman, Cheryl V.

2014-01-01

Injectable scaffolds are of interest in the field of regenerative medicine because of their minimally invasive mode of delivery. For tissue repair applications, it is essential that such scaffolds have the mechanical properties, porosity and pore diameter to support the formation of new tissue. In the current study, porous poly(dl-lactic acid-co-glycolic acid) (PLGA) microspheres were fabricated with an average size of 84 ± 24 μm for use as injectable cell carriers. Treatment with ethanolic sodium hydroxide for 2 min was observed to increase surface porosity without causing the microsphere structure to disintegrate. This surface treatment also enabled the microspheres to fuse together at 37 °C to form scaffold structures. The average compressive strength of the scaffolds after 24 h at 37 °C was 0.9 ± 0.1 MPa, and the average Young’s modulus was 9.4 ± 1.2 MPa. Scaffold porosity levels were 81.6% on average, with a mean pore diameter of 54 ± 38 μm. This study demonstrates a method for fabricating porous PLGA microspheres that form solid porous scaffolds at body temperature, creating an injectable system capable of supporting NIH-3T3 cell attachment and proliferation in vitro. PMID:25152354

Chitosan functionalized poly-ε-caprolactone electrospun fibers and 3D printed scaffolds as antibacterial materials for tissue engineering applications.

PubMed

Tardajos, Myriam G; Cama, Giuseppe; Dash, Mamoni; Misseeuw, Lara; Gheysens, Tom; Gorzelanny, Christian; Coenye, Tom; Dubruel, Peter

2018-07-01

Tissue engineering (TE) approaches often employ polymer-based scaffolds to provide support with a view to the improved regeneration of damaged tissues. The aim of this research was to develop a surface modification method for introducing chitosan as an antibacterial agent in both electrospun membranes and 3D printed poly-ε-caprolactone (PCL) scaffolds. The scaffolds were functionalized by grafting methacrylic acid N-hydroxysuccinimide ester (NHSMA) onto the surface after Ar-plasma/air activation. Subsequently, the newly-introduced NHS groups were used to couple with chitosan of various molecular weights (Mw). High Mw chitosan exhibited a better coverage of the surface as indicated by the higher N% detected by X-ray photoelectron spectroscopy (XPS) and the observations with either scanning electron microscopy (SEM)(for fibers) or Coomassie blue staining (for 3D-printed scaffolds). A lactate dehydrogenase assay (LDH) using L929 fibroblasts demonstrated the cell-adhesion and cell-viability capacity of the modified samples. The antibacterial properties against S. aureus ATCC 6538 and S. epidermidis ET13 revealed a slower bacterial growth rate on the surface of the chitosan modified scaffolds, regardless the chitosan Mw. Copyright © 2018 Elsevier Ltd. All rights reserved.

Electrospun Gelatin/β-TCP Composite Nanofibers Enhance Osteogenic Differentiation of BMSCs and In Vivo Bone Formation by Activating Ca (2+) -Sensing Receptor Signaling.

PubMed

Zhang, Xuehui; Meng, Song; Huang, Ying; Xu, Mingming; He, Ying; Lin, Hong; Han, Jianmin; Chai, Yuan; Wei, Yan; Deng, Xuliang

2015-01-01

Calcium phosphate- (CaP-) based composite scaffolds have been used extensively for the bone regeneration in bone tissue engineering. Previously, we developed a biomimetic composite nanofibrous membrane of gelatin/β-tricalcium phosphate (TCP) and confirmed their biological activity in vitro and bone regeneration in vivo. However, how these composite nanofibers promote the osteogenic differentiation of bone marrow mesenchymal stem cells (BMSCs) is unknown. Here, gelatin/β-TCP composite nanofibers were fabricated by incorporating 20 wt% β-TCP nanoparticles into electrospun gelatin nanofibers. Electron microscopy showed that the composite β-TCP nanofibers had a nonwoven structure with a porous network and a rough surface. Spectral analyses confirmed the presence and chemical stability of the β-TCP and gelatin components. Compared with pure gelatin nanofibers, gelatin/β-TCP composite nanofibers caused increased cell attachment, proliferation, alkaline phosphatase activity, and osteogenic gene expression in rat BMSCs. Interestingly, the expression level of the calcium-sensing receptor (CaSR) was significantly higher on the composite nanofibrous scaffolds than on pure gelatin. For rat calvarial critical sized defects, more extensive osteogenesis and neovascularization occurred in the composite scaffolds group compared with the gelatin group. Thus, gelatin/β-TCP composite scaffolds promote osteogenic differentiation of BMSCs in vitro and bone regeneration in vivo by activating Ca(2+)-sensing receptor signaling.

An improved polymeric sponge replication method for biomedical porous titanium scaffolds.

PubMed

Wang, Chunli; Chen, Hongjie; Zhu, Xiangdong; Xiao, Zhanwen; Zhang, Kai; Zhang, Xingdong

2017-01-01

Biomedical porous titanium (Ti) scaffolds were fabricated by an improved polymeric sponge replication method. The unique formulations and distinct processing techniques, i.e. a mixture of water and ethanol as solvent, multiple coatings with different viscosities of the Ti slurries and centrifugation for removing the extra slurries were used in the present study. The optimized porous Ti scaffolds had uniform porous structure and completely interconnected macropores (~365.1μm). In addition, two different sizes of micropores (~45.4 and ~6.2μm) were also formed in the skeleton of the scaffold. The addition of ethanol to the Ti slurry increased the compressive strength of the scaffold by improving the compactness of the skeleton. A compressive strength of 83.6±4.0MPa was achieved for a porous Ti scaffold with a porosity of 66.4±1.8%. Our cellular study also revealed that the scaffolds could support the growth and proliferation of mesenchymal stem cells (MSCs). Copyright © 2016 Elsevier B.V. All rights reserved.

Balancing mechanical strength with bioactivity in chitosan-calcium phosphate 3D microsphere scaffolds for bone tissue engineering: air- vs. freeze-drying processes.

PubMed

Nguyen, D T; McCanless, J D; Mecwan, M M; Noblett, A P; Haggard, W O; Smith, R A; Bumgardner, J D

2013-01-01

The objective of this study was to evaluate the potential benefit of 3D composite scaffolds composed of chitosan and calcium phosphate for bone tissue engineering. Additionally, incorporation of mechanically weak lyophilized microspheres within those air-dried (AD) was considered for enhanced bioactivity. AD microsphere, alone, and air- and freeze-dried microsphere (FDAD) 3D scaffolds were evaluated in vitro using a 28-day osteogenic culture model with the Saos-2 cell line. Mechanical testing, quantitative microscopy, and lysozyme-driven enzymatic degradation of the scaffolds were also studied. FDAD scaffold showed a higher concentration (p < 0.01) in cells per scaffold mass vs. AD constructs. Collagen was ∼31% greater (p < 0.01) on FDAD compared to AD scaffolds not evident in microscopy of microsphere surfaces. Alternatively, AD scaffolds demonstrated a superior threefold increase in compressive strength over FDAD (12 vs. 4 MPa) with minimal degradation. Inclusion of FD spheres within the FDAD scaffolds allowed increased cellular activity through improved seeding, proliferation, and extracellular matrix production (as collagen), although mechanical strength was sacrificed through introduction of the less stiff, porous FD spheres.

Realization and testing of multi-material 3D printer for bone scaffold fabrication

NASA Astrophysics Data System (ADS)

Whulanza, Yudan; Hidayaturrahmi, Pretty; Kurniawati, Tri; AJ, Rahyussalim

2017-02-01

This research realized 3D constructs by integrating more than one material with multi fabrication system within a single session. A commercial rapid prototyping system, RepRap MendelTM, is modified so that it enables us to realize microenvironment composed of multi materials namely gelatin hydrogel and polylactic acid. Firstly, the session is preceded by realization of 3D scaffold using polylactic acid (PLA) with porosity and modulus elasticity as characterized. Later, the gelatin extrusion took place to seed the cellular in determined spatial arrangement. The results show that our apparatus able to realized scaffold that using PLA as matrix filled with gelatin that act as cell carrier in future application. The scaffolds have porous around 0.25 mm2 porosity with a modulus of elasticity around 160 MPa.

A hybrid composite system of biphasic calcium phosphate granules loaded with hyaluronic acid-gelatin hydrogel for bone regeneration.

PubMed

Faruq, Omar; Kim, Boram; Padalhin, Andrew R; Lee, Gun Hee; Lee, Byong-Taek

2017-10-01

An ideal bone substitute should be made of biocompatible materials that mimic the structure, characteristics, and functions of natural bone. Many researchers have worked on the fabrication of different bone scaffold systems including ceramic-polymer hybrid system. In the present study, we incorporated hyaluronic acid-gelatin hydrogel to micro-channeled biphasic calcium phosphate granules as a carrier to improve cell attachment and proliferation through highly interconnected porous structure. This hybrid system is composed of ceramic biphasic calcium phosphate granules measuring 1 mm in diameter with seven holes and hyaluronic acid-gelatin hydrogel. This combination of biphasic calcium phosphate and hyaluronic acid-gelatin retained suitable characteristics for bone regeneration. The resulting scaffold had a porosity of 56% with a suitable pore sizes. The mechanical strength of biphasic calcium phosphate granule increased after loading hyaluronic acid-gelatin from 4.26 ± 0.43 to 6.57 ± 0.25 MPa, which is highly recommended for cancellous bone substitution. Swelling and degradation rates decreased in the hybrid scaffold compared to hydrogel due to the presence of granules in hybrid scaffold. In vitro cytocompatibility studies were observed by preosteoblasts (MC3T3-E1) cell line and the result revealed that biphasic calcium phosphate/hyaluronic acid-gelatin significantly increased cell growth and proliferation compared to biphasic calcium phosphate granules. Analysis of micro-computed tomography data and stained tissue sections from the implanted samples showed that the hybrid scaffold had good osseointegration and better bone formation in the scaffold one and two months postimplantation. Histological section confirmed the formation of dense collagenous tissue and new bone in biphasic calcium phosphate/hyaluronic acid-gelatin scaffolds at two months. Our study demonstrated that such hybrid biphasic calcium phosphate/hyaluronic acid-gelatin scaffold is a

Collagen and collagen-chondroitin sulfate scaffolds with uniaxially aligned pores for the biomimetic, three dimensional culture of trabecular meshwork cells.

PubMed

Osmond, Matthew; Bernier, Sarah M; Pantcheva, Mina B; Krebs, Melissa D

2017-04-01

Glaucoma is a disease in which damage to the optic nerve leads to progressive, irreversible vision loss. The intraocular pressure (IOP) is the only modifiable risk factor for glaucoma and its lowering is considered a useful strategy for preventing or slowing down the progression of glaucomatous neuropathy. Elevated intraocular pressure associated with glaucoma is due to increased aqueous humor outflow resistance, primarily through the trabecular meshwork (TM) of the eye. Current in vitro models of the trabecular meshwork are oversimplified and do not capture the organized and complex three-dimensional nature of this tissue that consists primarily of collagen and glycoasaminoglycans. In this work, collagen and collagen-chondroitin sulfate (CS) scaffolds were fabricated via unidirectional freezing and lyophilization to induce the formation of aligned pores. Scaffolds were characterized by scanning electron microscopy, dynamic mechanical analysis, and a chondroitin sulfate quantification assay. Scaffold characterization confirmed the formation of aligned pores, and also that the CS was leaching out of the scaffolds over time. Primary porcine trabecular meshwork (TM) cells were seeded onto the surface of scaffolds and their gene expression, proliferation, viability, migration into the scaffolds, and morphology were examined. The TM cells were viable and proliferated 2 weeks after seeding. The cells migrated down into the internal scaffold structure and their morphology reflected the topography and alignment of the scaffold structure. This work is a promising step toward the development of a three dimensional in vitro model of the TM that can be used for testing of glaucoma pharmacological agents in future experimentation and to better our understanding of the trabecular meshwork and its complex physiology. Biotechnol. Bioeng. 2017;114: 915-923. © 2016 Wiley Periodicals, Inc. © 2016 Wiley Periodicals, Inc.

Novel fiber-based pure chitosan scaffold for tendon augmentation: biomechanical and cell biological evaluation.

PubMed

Nowotny, J; Aibibu, D; Farack, J; Nimtschke, U; Hild, M; Gelinsky, M; Kasten, P; Cherif, Ch

2016-07-01

One possibility to improve the mechanical properties after tendon ruptures is augmentation with a scaffold. Based on wet spinning technology, chitosan fibres were processed to a novel pure high-grade multifilament yarn with reproducible quality. The fibres were braided to obtain a 3D tendon scaffold. The CS fibres and scaffolds were evaluated biomechanically and compared to human supraspinatus (SSP) tendons. For the cytobiological characterization, in vitro cell culture experiments with human mesenchymal stem cells (hMSC) were performed. Three types of 3D circular braided scaffolds were fabricated. Significantly, higher ultimate stress values were measured for scaffold with larger filament yarn, compared to scaffold with smaller filament yarn. During cultivation over 28 days, the cells showed in dependence of isolation method and/or donor a doubling or tripling of the cell number or even a six-fold increase on the CS scaffold, which was comparable to the control (polystyrene) or in the case of cells obtained from human biceps tendon even higher proliferation rates. After 14 days, the scaffold surface was covered homogeneously with a cell layer. In summary, the present work demonstrates that braided chitosan scaffolds constitute a straightforward approach for designing tendon analogues, maintaining important flexibility in scaffold design and providing favourable mechanical properties of the resulting construct.

Tubular scaffolds of gelatin and poly(ε-caprolactone)-block-poly(γ-glutamic acid) blending hydrogel for the proliferation of the primary intestinal smooth muscle cells of rats.

PubMed

Jwo, Shyh-Chuan; Chiu, Chu-Hua; Tang, Shye-Jye; Hsieh, Ming-Fa

2013-12-01

The proper regeneration of intestinal muscle for functional peristalsis is the most challenging aspect of current small intestine tissue engineering. This study aimed to fabricate a hydrogel scaffold for the proliferation of intestinal smooth muscle cells (ISMCs). Tubular porous scaffolds of 10-20 wt% gelatin and 0.05-0.1 wt% poly(ε-caprolactone)-block-poly(γ-glutamic acid) blending hydrogel were cross-linked by carbodiimide and succinimide in an annular space of a glass mold. The scaffolds with higher gelatin contents degraded slower in the phosphate buffer solution. In rheological measurements, the hydrated scaffolds were elastic (all tangent delta <0.45); they responded differentially to frequency, indicating a complete viscoelastic property that is beneficial for soft tissue regeneration. Isolated rat ISMCs, with the characteristic biomarkers α-SMA, calponin and myh11, were loaded into the scaffolds by using either static or centrifugal methods. The average cell density inside the scaffolds increased in a time-dependent manner in most scaffolds of both seeding groups, although at early time points (seven days) the centrifugal seeding method trapped cells more efficiently and yielded a higher cell density than the static seeding method. The static seeding method increased the cell density from 7.5-fold to 16.3-fold after 28 days, whereas the centrifugal procedure produced a maximum increase of only 2.4-fold in the same period. In vitro degradation data showed that 50-80% of the scaffold was degraded by the 14th day. However, the self-secreted extracellular matrix maintained the integrity of the scaffolds for cell proliferation and spreading for up to 28 days. Confocal microscopic images revealed cell-cell contacts with the formation of a 3D network, demonstrating that the fabricated scaffolds were highly biocompatible. Therefore, these polymeric biomaterials hold great promise for in vivo applications of intestinal tissue engineering.

Aerogels made of chitosan and chondroitin sulfate at high degree of neutralization: Biological properties toward wound healing.

PubMed

Concha, Miguel; Vidal, Alejandra; Giacaman, Annesi; Ojeda, Javier; Pavicic, Francisca; Oyarzun-Ampuero, Felipe A; Torres, César; Cabrera, Marcela; Moreno-Villoslada, Ignacio; Orellana, Sandra L

2018-02-09

In this study, highly neutralized, highly porous, and ultralight polymeric aerogels prepared from aqueous colloidal suspensions of chitosan (CS) and chondroitin sulfate (ChS) nanocomplexes, formulated as quasi-equimolar amounts of both, are described. These aerogels were designed as healing agents under the inspiration of minimizing the amount of matter applied to wounds, reducing the electrostatic potential of the material and avoiding covalent cross-linkers in order to decrease metabolic stress over wounds. Aerogels synthesized under these criteria are biocompatible and provide specific properties for the induction of wound healing. They do not affect neither the metabolic activity of cultured 3T3 fibroblasts nor the biochemical parameters of experimental animals, open wounds close significantly faster and, unlike control wounds, complete reepithelialization and scarring can be attained 14 days after surgery. Because of its hydration abilities, rapid adaptation to the wound bed and the early accelerator effect of wound closure, the CS/ChS aerogels appear to be functional inducers of the healing. Previous information show that CS/ChS aerogels improve wound bed quality, increase granulation tissue and have pain suppressive effect. CS/ChS aerogels are useful as safe, inexpensive and easy to handle materials for topical applications, such as skin chronic wounds. © 2018 Wiley Periodicals, Inc. J Biomed Mater Res Part B: Appl Biomater, 2018. © 2018 Wiley Periodicals, Inc.

Dramatic Improvement of the Mechanical Strength of Silane-Modified Hydroxyapatite–Gelatin Composites via Processing with Cosolvent

PubMed Central

2018-01-01

Bone tissue engineering (BTE) requires a sturdy biomaterial for scaffolds for restoration of large bone defects. Ideally, the scaffold should have a mechanical strength comparable to the natural bone in the implanted site. We show that adding cosolvent during the processing of our previously developed composite of hydroxyapatite–gelatin with a silane cross-linker can significantly affect its mechanical strength. When processed with tetrahydrofuran (THF) as the cosolvent, the new hydroxyapatite–gelatin composite can demonstrate almost twice the compressive strength (97 vs 195 MPa) and biaxial flexural strength (222 vs 431 MPa) of the previously developed hydroxyapatite–gelatin composite (i.e., processed without THF), respectively. We further confirm that this mechanical strength improvement is due to the improved morphology of both the enTMOS network and the composite. Furthermore, the addition of cosolvents does not appear to negatively impact the cell viability. Finally, the porous scaffold can be easily fabricated, and its compressive strength is around 11 MPa under dry conditions. All these results indicate that this new hydroxyapatite–gelatin composite is a promising material for BTE application. PMID:29623305

Porous magnesium-based scaffolds for tissue engineering.

PubMed

Yazdimamaghani, Mostafa; Razavi, Mehdi; Vashaee, Daryoosh; Moharamzadeh, Keyvan; Boccaccini, Aldo R; Tayebi, Lobat

2017-02-01

Significant amount of research efforts have been dedicated to the development of scaffolds for tissue engineering. Although at present most of the studies are focused on non-load bearing scaffolds, many scaffolds have also been investigated for hard tissue repair. In particular, metallic scaffolds are being studied for hard tissue engineering due to their suitable mechanical properties. Several biocompatible metallic materials such as stainless steels, cobalt alloys, titanium alloys, tantalum, nitinol and magnesium alloys have been commonly employed as implants in orthopedic and dental treatments. They are often used to replace and regenerate the damaged bones or to provide structural support for healing bone defects. Among the common metallic biomaterials, magnesium (Mg) and a number of its alloys are effective because of their mechanical properties close to those of human bone, their natural ionic content that may have important functional roles in physiological systems, and their in vivo biodegradation characteristics in body fluids. Due to such collective properties, Mg based alloys can be employed as biocompatible, bioactive, and biodegradable scaffolds for load-bearing applications. Recently, porous Mg and Mg alloys have been specially suggested as metallic scaffolds for bone tissue engineering. With further optimization of the fabrication techniques, porous Mg is expected to make a promising hard substitute scaffold. The present review covers research conducted on the fabrication techniques, surface modifications, properties and biological characteristics of Mg alloys based scaffolds. Furthermore, the potential applications, challenges and future trends of such degradable metallic scaffolds are discussed in detail. Copyright © 2016 Elsevier B.V. All rights reserved.

Local delivery of HMGB1 in gelatin sponge scaffolds combined with mesenchymal stem cell sheets to accelerate fracture healing.

PubMed

Xue, Deting; Zhang, Wei; Chen, Erman; Gao, Xiang; Liu, Ling; Ye, Chenyi; Tan, Yanbin; Pan, Zhijun; Li, Hang

2017-06-27

Fracture nonunion and delayed union continue to pose challenges for orthopedic surgeons. In the present study, we combined HMGB1 gelatin sponges with MSC sheets to promote bone healing after surgical treatment of rat tibial fractures. The HMGB1 gelatin sponge scaffolds supported the expansion of mesenchymal stem cells (MSCs) and promoted the osteogenic differentiation of MSCs and MSC sheets. Lentiviral vectors were then used to overexpress HMGB1 in MSCs. The results indicated that HMGB1 promotes the osteogenic differentiation of MSCs through the STAT3 pathway. Both siRNA and a STAT3 inhibitor downregulated STAT3, further confirming that HMGB1 induces the osteogenic differentiation of MSCs partly via the STAT3 signal pathway. In a rat tibial osteotomy model, we demonstrated the ability of HMGB1 gelatin sponge scaffolds to increase bone formation. The addition of MSC sheets further enhanced fracture healing. These findings support the use of HMGB1-loaded gelatin sponge scaffolds combined with MSC sheets to enhance fracture healing after surgical intervention.

Local delivery of HMGB1 in gelatin sponge scaffolds combined with mesenchymal stem cell sheets to accelerate fracture healing

PubMed Central

Xue, Deting; Zhang, Wei; Chen, Erman; Gao, Xiang; Liu, Ling; Ye, Chenyi; Tan, Yanbin; Pan, Zhijun; Li, Hang

2017-01-01

Fracture nonunion and delayed union continue to pose challenges for orthopedic surgeons. In the present study, we combined HMGB1 gelatin sponges with MSC sheets to promote bone healing after surgical treatment of rat tibial fractures. The HMGB1 gelatin sponge scaffolds supported the expansion of mesenchymal stem cells (MSCs) and promoted the osteogenic differentiation of MSCs and MSC sheets. Lentiviral vectors were then used to overexpress HMGB1 in MSCs. The results indicated that HMGB1 promotes the osteogenic differentiation of MSCs through the STAT3 pathway. Both siRNA and a STAT3 inhibitor downregulated STAT3, further confirming that HMGB1 induces the osteogenic differentiation of MSCs partly via the STAT3 signal pathway. In a rat tibial osteotomy model, we demonstrated the ability of HMGB1 gelatin sponge scaffolds to increase bone formation. The addition of MSC sheets further enhanced fracture healing. These findings support the use of HMGB1-loaded gelatin sponge scaffolds combined with MSC sheets to enhance fracture healing after surgical intervention. PMID:28431400

Preparation and characterization of malonic acid cross-linked chitosan and collagen 3D scaffolds: an approach on non-covalent interactions.

PubMed

Mitra, Tapas; Sailakshmi, G; Gnanamani, A; Mandal, A B

2012-05-01

The present study emphasizes the influence of non-covalent interactions on the mechanical and thermal properties of the scaffolds of chitosan/collagen origin. Malonic acid (MA), a bifuncitonal diacid was chosen to offer non-covalent cross-linking. Three dimensional scaffolds was prepared using chitosan at 1.0% (w/v) and MA at 0.2% (w/v), similarly collagen 0.5% (w/v) and MA 0.2% (w/v) and characterized. Results on FT-IR, TGA, DSC, SEM and mechanical properties (tensile strength, stiffness, Young's modulus, etc.) assessment demonstrated the existence of non-covalent interaction between MA and chitosan/collagen, which offered flexibility and high strength to the scaffolds suitable for tissue engineering research. Studies using NIH 3T3 fibroblast cells suggested biocompatibility nature of the scaffolds. Docking simulation study further supports the intermolecular hydrogen bonding interactions between MA and chitosan/collagen.

A novel chondroitin sulfate hydrogel for nerve repair

NASA Astrophysics Data System (ADS)

Conovaloff, Aaron William

Brachial plexus injuries affect numerous patients every year, with very debilitating results. The majority of these cases are very severe, and involve damage to the nerve roots. To date, repair strategies for these injuries address only gross tissue damage, but do not supply cells with adequate regeneration signals. As a result, functional recovery is often severely lacking. Therefore, a chondroitin sulfate hydrogel that delivers neurotrophic signals to damaged neurons is proposed as a scaffold to support nerve root regeneration. Capillary electrophoresis studies revealed that chondroitin sulfate can physically bind with a variety of neurotrophic factors, and cultures of chick dorsal root ganglia demonstrated robust neurite outgrowth in chondroitin sulfate hydrogels. Outgrowth in chondroitin sulfate gels was greater than that observed in control gels of hyaluronic acid. Furthermore, the chondroitin sulfate hydrogel's binding activity with nerve growth factor could be enhanced by incorporation of a synthetic bioactive peptide, as revealed by fluorescence recovery after photobleaching. This enhanced binding was observed only in chondroitin sulfate gels, and not in hyaluronic acid control gels. This enhanced binding activity resulted in enhanced dorsal root ganglion neurite outgrowth in chondroitin sulfate gels. Finally, the growth of regenerating dorsal root ganglia in these gels was imaged using label-free coherent anti-Stokes scattering microscopy. This technique generated detailed, high-quality images of live dorsal root ganglion neurites, which were comparable to fixed, F-actin-stained samples. Taken together, these results demonstrate the viability of this chondroitin sulfate hydrogel to serve as an effective implantable scaffold to aid in nerve root regeneration.

Architecture engineering of hierarchically porous chitosan/vacuum-stripped graphene scaffold as bioanode for high performance microbial fuel cell.

PubMed

He, Ziming; Liu, Jing; Qiao, Yan; Li, Chang Ming; Tan, Timothy Thatt Yang

2012-09-12

The bioanode is the defining feature of microbial fuel cell (MFC) technology and often limits its performance. In the current work, we report the engineering of a novel hierarchically porous architecture as an efficient bioanode, consisting of biocompatible chitosan and vacuum-stripped graphene (CHI/VSG). With the hierarchical pores and unique VSG, an optimized bioanode delivered a remarkable maximum power density of 1530 mW m(-2) in a mediator-less MFC, 78 times higher than a carbon cloth anode.

Porous alumina scaffold produced by sol-gel combined polymeric sponge method

NASA Astrophysics Data System (ADS)

Hasmaliza, M.; Fazliah, M. N.; Shafinaz, R. J.

2012-09-01

Sol gel is a novel method used to produce high purity alumina with nanometric scale. In this study, three-dimensional porous alumina scaffold was produced using sol-gel polymeric sponge method. Briefly, sol gel alumina was prepared by evaporation and polymeric sponge cut to designated sizes were immersed in the sol gel followed by sintering at 1250 and 1550°C. In order to study the cell interaction, the porous alumina scaffold was sterilized using autoclave prior to Human Mesenchymal Stem Cells (HMSCs) seeding on the scaffold and the cell proliferation was assessed by alamarBlue® assay. SEM results showed that during the 21 day period, HMSCs were able to attach on the scaffold surface and the interconnecting pores while maintaining its proliferation. These findings suggested the potential use of the porous alumina produced as a scaffold for implantation procedure.

Porous Biodegradable Metals for Hard Tissue Scaffolds: A Review

PubMed Central

Yusop, A. H.; Bakir, A. A.; Shaharom, N. A.; Abdul Kadir, M. R.; Hermawan, H.

2012-01-01

Scaffolds have been utilized in tissue regeneration to facilitate the formation and maturation of new tissues or organs where a balance between temporary mechanical support and mass transport (degradation and cell growth) is ideally achieved. Polymers have been widely chosen as tissue scaffolding material having a good combination of biodegradability, biocompatibility, and porous structure. Metals that can degrade in physiological environment, namely, biodegradable metals, are proposed as potential materials for hard tissue scaffolding where biodegradable polymers are often considered as having poor mechanical properties. Biodegradable metal scaffolds have showed interesting mechanical property that was close to that of human bone with tailored degradation behaviour. The current promising fabrication technique for making scaffolds, such as computation-aided solid free-form method, can be easily applied to metals. With further optimization in topologically ordered porosity design exploiting material property and fabrication technique, porous biodegradable metals could be the potential materials for making hard tissue scaffolds. PMID:22919393

Chitosan/silk fibroin-based, Schwann cell-derived extracellular matrix-modified scaffolds for bridging rat sciatic nerve gaps.

PubMed

Gu, Yun; Zhu, Jianbin; Xue, Chengbin; Li, Zhenmeiyu; Ding, Fei; Yang, Yumin; Gu, Xiaosong

2014-02-01

Extracellular matrix (ECM) plays a prominent role in establishing and maintaining an ideal microenvironment for tissue regeneration, and ECM scaffolds are used as a feasible alternative to cellular and molecular therapy in the fields of tissue engineering. Because of their advantages over tissue-derived ECM scaffolds, cultured cell-derived ECM scaffolds are beginning to attract attention, but they have been scarcely studied for peripheral nerve repair. Here we aimed to develop a tissue engineered nerve scaffold by reconstituting nerve cell-derived ECM with natural biomaterials. A protocol was adopted to prepare and characterize the cultured Schwann cell (SC)-derived ECM. A chitosan conduit and silk fibroin (SF) fibers were prepared, cultured with SCs for ECM deposition, and subjected to decellularization, followed by assembly into a chitosan/SF-based, SC-derived ECM-modified scaffold, which was used to bridge a 10 mm rat sciatic nerve gap. The results from morphological analysis as well as electrophysiological examination indicated that regenerative outcomes achieved by our developed scaffold were similar to those by an acellular nerve graft (namely a nerve tissue-derived ECM scaffold), but superior to those by a plain chitosan/SF scaffold. Moreover, blood and histopathological parameters confirmed the safety of scaffold modification by SC-derived ECM. Therefore, a hybrid scaffold based on joint use of acellular and classical biomaterials represents a promising approach to nerve tissue engineering. Copyright © 2013 Elsevier Ltd. All rights reserved.

Chondrogenesis of infrapatellar fat pad derived adipose stem cells in 3D printed chitosan scaffold.

PubMed

Ye, Ken; Felimban, Raed; Traianedes, Kathy; Moulton, Simon E; Wallace, Gordon G; Chung, Johnson; Quigley, Anita; Choong, Peter F M; Myers, Damian E

2014-01-01

Infrapatellar fat pad adipose stem cells (IPFP-ASCs) have been shown to harbor chondrogenic potential. When combined with 3D polymeric structures, the stem cells provide a source of stem cells to engineer 3D tissues for cartilage repair. In this study, we have shown human IPFP-ASCs seeded onto 3D printed chitosan scaffolds can undergo chondrogenesis using TGFβ3 and BMP6. By week 4, a pearlescent, cartilage-like matrix had formed that penetrated the top layers of the chitosan scaffold forming a 'cap' on the scaffold. Chondrocytic morphology showed typical cells encased in extracellular matrix which stained positively with toluidine blue. Immunohistochemistry demonstrated positive staining for collagen type II and cartilage proteoglycans, as well as collagen type I. Real time PCR analysis showed up-regulation of collagen type II, aggrecan and SOX9 genes when IPFP-ASCs were stimulated by TGFβ3 and BMP6. Thus, IPFP-ASCs can successfully undergo chondrogenesis using TGFβ3 and BMP6 and the cartilage-like tissue that forms on the surface of 3D-printed chitosan scaffold may prove useful as an osteochondral graft.

Perlecan and vascular endothelial growth factor-encoding DNA-loaded chitosan scaffolds promote angiogenesis and wound healing.

PubMed

Lord, Megan S; Ellis, April L; Farrugia, Brooke L; Whitelock, John M; Grenett, Hernan; Li, Chuanyu; O'Grady, Robert L; DeCarlo, Arthur A

2017-03-28

The repair of dermal wounds, particularly in the diabetic population, poses a significant healthcare burden. The impaired wound healing of diabetic wounds is attributed to low levels of endogenous growth factors, including vascular endothelial growth factor (VEGF), that normally stimulate multiple phases of wound healing. In this study, chitosan scaffolds were prepared via freeze drying and loaded with plasmid DNA encoding perlecan domain I and VEGF189 and analyzed in vivo for their ability to promote dermal wound healing. The plasmid DNA encoding perlecan domain I and VEGF189 loaded scaffolds promoted dermal wound healing in normal and diabetic rats. This treatment resulted in an increase in the number of blood vessels and sub-epithelial connective tissue matrix components within the wound beds compared to wounds treated with chitosan scaffolds containing control DNA or wounded controls. These results suggest that chitosan scaffolds containing plasmid DNA encoding VEGF189 and perlecan domain I have the potential to induce angiogenesis and wound healing. Copyright © 2017 Elsevier B.V. All rights reserved.

Physicochemical properties and bioactivity of freeze-cast chitosan nanocomposite scaffolds reinforced with bioactive glass.

PubMed

Pourhaghgouy, Masoud; Zamanian, Ali; Shahrezaee, Mostafa; Masouleh, Milad Pourbaghi

2016-01-01

Chitosan based nanocomposite scaffolds were prepared by freeze casting method through blending constant chitosan concentration with different portions of synthesized bioactive glass nanoparticles (BGNPs). Transmission Electron Microscopy (TEM) image showed that the particles size of bioactive glass (64SiO2.28CaO.8P2O5) prepared by sol-gel method was approximately less than 20 nm. Fourier Transform Infrared Spectroscopy (FT-IR) and X-ray Diffraction (XRD) analysis showed proper interfacial bonding between BGNPs and chitosan polymers. Scanning Electron Microscopy (SEM) images depicted a unidirectional structure with homogenous distribution of BGNPs among chitosan matrix associated with the absence of pure chitosan scaffold's wall pores after addition of only 10 wt.% BGNPs. As the BGNP content increased from 0 to 50 wt.%, the compressive strength and compressive module values increased from 0.034 to 0.419 MPa and 0.41 to 10.77 MPa, respectively. Biodegradation study showed that increase in BGNP content leads to growth of weight loss amount. The in vitro biomineralization studies confirmed the bioactive nature of all nanocomposites. Amount of 30 wt.% BGNPs represented the best concentration for absorption capacity and bioactivity behaviors. Copyright © 2015. Published by Elsevier B.V.

Electrospun biomimetic scaffold of hydroxyapatite/chitosan supports enhanced osteogenic differentiation of mMSCs

NASA Astrophysics Data System (ADS)

Peng, Hongju; Yin, Zi; Liu, Huanhuan; Chen, Xiao; Feng, Bei; Yuan, Huihua; Su, Bo; Ouyang, Hongwei; Zhang, Yanzhong

2012-12-01

Engaging functional biomaterial scaffolds to regulate stem cell differentiation has drawn a great deal of attention in the tissue engineering and regenerative medicine community. In this study, biomimetic composite nanofibrous scaffolds of hydroxyapatite/chitosan (HAp/CTS) were prepared to investigate their capacity for inducing murine mesenchymal stem cells (mMSCs) to differentiate into the osteogenic lineage, in the absence and presence of an osteogenic supplementation (i.e., ascorbic acid, β-glycerol phosphate, and dexamethasone), respectively. Using electrospun chitosan (CTS) nanofibrous scaffolds as the control, cell morphology, growth, specific osteogenic genes expression, and quantified proteins secretion on the HAp/CTS scaffolds were sequentially examined and assessed. It appeared that the HAp/CTS scaffolds supported better attachment and proliferation of the mMSCs. Most noteworthy was that in the absence of the osteogenic supplementation, expression of osteogenic genes including collagen I (Col I), runt-related transcription factor 2 (Runx2), alkaline phosphatase (ALP), and osteocalcin (OCN) were significantly upregulated in mMSCs cultured on the HAp/CTS nanofibrous scaffolds. Also increased secretion of the osteogenesis protein markers of alkaline phosphatase and collagen confirmed that the HAp/CTS nanofibrous scaffold markedly promoted the osteogenic commitment in the mMSCs. Moreover, the presence of osteogenic supplementation proved an enhanced efficacy of mMSC osteogenesis on the HAp/CTS nanofibrous scaffolds. Collectively, this study demonstrated that the biomimetic nanofibrous HAp/CTS scaffolds could support and enhance the adhesion, proliferation, and particularly osteogenic differentiation of the mMSCs. It also substantiated the potential of using biomimetic nanofibrous scaffolds of HAp/CTS for functional bone repair and regeneration applications.

3D printed porous ceramic scaffolds for bone tissue engineering: a review.

PubMed

Wen, Yu; Xun, Sun; Haoye, Meng; Baichuan, Sun; Peng, Chen; Xuejian, Liu; Kaihong, Zhang; Xuan, Yang; Jiang, Peng; Shibi, Lu

2017-08-22

This study summarizes the recent research status and development of three-dimensional (3D)-printed porous ceramic scaffolds in bone tissue engineering. Recent literature on 3D-printed porous ceramic scaffolds was reviewed. Compared with traditional processing and manufacturing technologies, 3D-printed porous ceramic scaffolds have obvious advantages, such as enhancement of the controllability of the structure or improvement of the production efficiency. More sophisticated scaffolds were fabricated by 3D printing technology. 3D printed bioceramics have broad application prospects in bone tissue engineering. Through understanding the advantages and limitations of different 3D-printing approaches, new classes of bone graft substitutes can be developed.

The effect of hydroxyapatite addition on the mechanical properties of polyvinyl alcohol/chitosan biomaterials for bone scaffolds application

NASA Astrophysics Data System (ADS)

Ramahdita, Ghiska; Puspita, Debie Maya; Albab, Muh Fadhil; Alfata, Rowi; Sofyan, Nofrijon; Yuwono, Akhmad Herman

2018-02-01

The increasing number of bone fracture incident in Indonesia from year to year needs an urgent problem solving of the limited bone substitute which can meet the necessary criteria for that purpose. Motivated by this, therefore, the current study is focusing on the optimization of material properties used as bone scaffold. A biomaterial of polyvinyl alcohol (PVA)/chitosan-hydroxyapatite (HA) composite was successfully made by wet chemistry method, followed by freeze thawing and freeze drying. For comparison purposes, the percentage of HA has been varied from 0, 25 and 40 % (wt/v). The resulting composites were characterized by Fourier transform infrared (FTIR) spectroscopy, scanning electron microscope (SEM), compressive test, and swelling behavior. The results showed that the addition of HA up to 40% (wt/v) has yielded a porous structure with an average pore size of 42.39 µm. In addition, the compressive modulus was enhanced from 14 MPa for 0% HA to 143, and 191 MPa for composites with the addition of HA from 25 to 40% (wt/v). The addition of HA has also reduced the swelling ratio from 296% for the sample without HA to 85 and 78 % for sample with addition of HA from 25 to 40 (wt/v), respectively. The obtained results show that PVA/chitosan-HA in this study is potential to be used as scaffold in bone tissue engineering.

Collagen scaffolds derived from a marine source and their biocompatibility.

PubMed

Song, Eun; Yeon Kim, So; Chun, Taehoon; Byun, Hyun-Jung; Lee, Young Moo

2006-05-01

The primary sources of industrial collagens are calf skin and bone. However, these carry a high risk of bovine spongiform encephalopathy or transmissible spongiform encephalopathy. In this study, a novel form of acid-soluble collagen was extracted from jellyfish in an effort to obtain an alternative and safer collagen. Porous scaffolds composed of jellyfish collagen were prepared by freeze-drying and cross-linking with 1-ethyl-(3-3-dimethylaminopropyl) carbodiimide hydrochloride/N-hydroxysuccinimide to be used in tissue engineering applications. Enzymatic degradation kinetics of jellyfish collagen scaffolds were controlled by EDC/NHS-cross-linking density. Results from an MTT assay indicated that jellyfish collagen exhibited higher cell viability than other naturally derived biomaterials, including bovine collagen, gelatin, hyaluronic acid, and glucan. Jellyfish collagen scaffolds also had a highly porous and interconnected pore structure, which is useful for an high-density cell seeding, an efficient nutrient and an oxygen supply to the cells cultured in the three-dimensional matrices. To determine whether jellyfish collagen evokes any specific inflammatory response compared to that induced by bovine collagen or gelatin, we measured the levels of pro-inflammatory cytokines and antibody secretions and monitored the population changes of immune cells after in vivo implantation. Jellyfish collagen was found to induce an immune response at least comparable to those caused by bovine collagen and gelatin.

Preparation and biological properties of a novel composite scaffold of nano-hydroxyapatite/chitosan/carboxymethyl cellulose for bone tissue engineering

PubMed Central

Liuyun, Jiang; Yubao, Li; Chengdong, Xiong

2009-01-01

In this study, we report the physico-chemical and biological properties of a novel biodegradable composite scaffold made of nano-hydroxyapatite and natural derived polymers of chitosan and carboxymethyl cellulose, namely, n-HA/CS/CMC, which was prepared by freeze-drying method. The physico-chemical properties of n-HA/CS/CMC scaffold were tested by infrared absorption spectra (IR), transmission electron microscope(TEM), scanning electron microscope(SEM), universal material testing machine and phosphate buffer solution (PBS) soaking experiment. Besides, the biological properties were evaluated by MG63 cells and Mesenchymal stem cells (MSCs) culture experiment in vitro and a short period implantation study in vivo. The results show that the composite scaffold is mainly formed through the ionic crossing-linking of the two polyions between CS and CMC, and n-HA is incorporated into the polyelectrolyte matrix of CS-CMC without agglomeration, which endows the scaffold with good physico-chemical properties such as highly interconnected porous structure, high compressive strength and good structural stability and degradation. More important, the results of cells attached, proliferated on the scaffold indicate that the scaffold is non-toxic and has good cell biocompatibility, and the results of implantation experiment in vivo further confirm that the scaffold has good tissue biocompatibility. All the above results suggest that the novel degradable n-HA/CS/CMC composite scaffold has a great potential to be used as bone tissue engineering material. PMID:19594953

Gelatin and galactomannan-based scaffolds: Characterization and potential for tissue engineering applications.

PubMed

Siqueira, Nataly M; Paiva, Bruno; Camassola, Melissa; Rosenthal-Kim, Emily Q; Garcia, Ketlin C; dos Santos, Francisco P; Soares, Rosane M D

2015-11-20

In this work, we produced gelatin films containing different concentrations of galactomannan by casting solutions. The films were crosslinked by immersion in 30mM solution of 1-(3-dimethylaminopropyl)-3-ethylcarbodiimide hydrochloride (EDC). The crosslinking of gelatin-containing films was confirmed by the reduction of free amine band intensity (3400-3200cm(-1)) in the GEL IR, as well as by the evaluation of its behavior when immersed in phosphate-buffer solution. The crosslinking of galactomannan film was confirmed by the formation of new ether bonds, as observed by increasing intensity of the band at 1148cm(-1), and the reduction of OH band intensity (3600-3200cm(-1)). The presence of galactomannan and the crosslinking mediated by EDC were responsible to improve elasticity in the gelatin-based films. The samples did not show cytotoxicity during 24h or 48h. In addition, rat mesenchymal stem cells adhered to the films regardless of galactomannan concentration. The results indicated that the gelatin/galactomannan films are potential biomaterials for use as scaffolds for tissue engineering. Copyright © 2015 Elsevier Ltd. All rights reserved.

Aspergillus niger PA2 Tyrosinase Covalently Immobilized on a Novel Eco-Friendly Bio-Composite of Chitosan-Gelatin and Its Evaluation for L-DOPA Production

PubMed Central

Agarwal, Pragati; Dubey, Swati; Singh, Mukta; Singh, Rajesh P.

2016-01-01

Tyrosinase (EC 1.14.18.1) a copper-containing monooxygenase, isolated from a fungal isolate Aspergillus niger PA2 was subjected for immobilization onto a composite consisting of chitosan and gelatin biopolymers. The homogeneity of the chitosan-gelatin biocomposite film was characterized by X-ray diffraction analyses. To evaluate immobilization efficiency, chitosan-gelatin-Tyr bio-composite films were analyzed by field emission scanning electron microscopy, atomic force microscopy and UV-spectroscopy. The rough morphology of the film led to a high loading of enzyme and it could retain its bioactivity for a longer period. The enzyme adsorbed onto the film exhibited 72% of its activity after 10 days and exhibited good repeatability for up to nine times, after intermittent storage. Moreover, the immobilized enzyme exhibited broader pH and temperature profile as compared to free counterpart. Immobilized enzyme was further evaluated for the synthesis of L-DOPA (2,4-dihydroxy phenylalanine) which is a precursor of dopamine and a potent drug for the treatment of Parkinson's disease and for myocardium neurogenic injury. PMID:28066399

Pore architecture and cell viability on freeze dried 3D recombinant human collagen-peptide (RHC)-chitosan scaffolds.

PubMed

Zhang, Jing; Zhou, Aimei; Deng, Aipeng; Yang, Yang; Gao, Lihu; Zhong, Zhaocai; Yang, Shulin

2015-04-01

Pore architecture of 3D scaffolds used in tissue engineering plays a critical role in the maintenance of cell survival, proliferation and further promotion of tissue regeneration. We investigated the pore size and structure, porosity, swelling as well as cell viability of a series of recombinant human collagen-peptide-chitosan (RHCC) scaffolds fabricated by lyophilization. In this paper, freezing regime containing a final temperature of freezing (Tf) and cooling rates was applied to obtain scaffolds with pore size ranging from 100μm to 120μm. Other protocols of RHC/chitosan suspension concentration and ratio modification were studied to produce more homogenous and appropriate structural scaffolds. The mean pore size decreased along with the decline of Tf at a slow cooling rate of 0.7°C/min; a more rapid cooling rate under 5°C/min resulted to a smaller pore size and more homogenous microstructure. High concentration could reduce pore size and lead to thick well of scaffold, while improved the ratio of RHC, lamellar and fiber structure coexisted with cellular pores. Human umbilical vein endothelial cells (HUVECs) were seeded on these manufactured scaffolds, the cell viability represented a negative correlation to the pore size. This study provides an alternative method to fabricate 3D RHC-chitosan scaffolds with appropriate pores for potential tissue engineering. Copyright © 2014 Elsevier B.V. All rights reserved.

Gelatin/nano-hydroxyapatite hydrogel scaffold prepared by sol-gel technology as filler to repair bone defects.

PubMed

Raucci, Maria Grazia; Demitri, Christian; Soriente, Alessandra; Fasolino, Ines; Sannino, Alessandro; Ambrosio, Luigi

2018-03-25

This study reports on the development of a scaffold with a gradient of bioactive solid signal embedded in the biodegradable polymer matrix by combining a sol-gel approach and freeze-drying technology. The chemical approach based on the sol-gel transition of calcium phosphates ensures the particles dispersion into the gelatin matrix and a direct control of interaction among COOH gelatin /Ca 2+ ions. Morphological analysis demonstrated that on the basis of the amount of inorganic component and by using specific process conditions, it is possible to control the spatial distribution of nanoparticles around the gelatin helix. In fact, methodology and formulations were able to discriminate between the different hydroxyapatite concentrations and their respective morphology. The good biological response represented by good cell attachment, proliferation and increased levels of alkaline phosphatase as an indicator of osteoblastic differentiation of human mesenchymal stem cells toward the osteogenic lineage, demonstrating the effect of bioactive solid signals on cellular behavior. Furthermore, the inhibition of reactive oxygen species production by composite materials predicted potential anti-inflammatory properties of scaffolds thus confirming their biocompatibility. Indeed, these interesting biological results suggest good potential application of this scaffold as filler to repair bone defects. © 2018 Wiley Periodicals, Inc. J Biomed Mater Res Part A, 2018. © 2018 Wiley Periodicals, Inc.

Construction of biocompatible porous tissue scaffold from the decellularized umbilical artery.

PubMed

Xin, Yi; Wu, Guanghui; Wu, Man; Zhang, Xiaoxia; Velot, Emilie; Decot, Véronique; Cui, Wei; Huang, Yimin; Stoltz, Jean-Francois; Du, Jie; Li, Na

2015-01-01

The scaffolds prepared from the tissue decellularization conserve the porous 3-D structure and provide an optimal matrix for the tissue regeneration. Since decade, the enzymatic digestion, chemical reagent treatment and mechanical actions such as eversion and abrasion have been used to remove the cells from the intact matrix. In this study, we optimized an enzymatic method to decellularize the umbilical artery to construct a 3-D porous scaffold which is suitable for the culture of mesenchymal stem cells (MSCs). The scaffold maintained the interconnected porous structure. It remained the similar high water content 95.3 ± 1% compared to 94.9 ± 0.6% in the intact umbilical artery (p>0.05). The decellularization process decreased the stress from 0.24 ± 0.05 mPa to 0.15 ± 0.06 mPa (p<0.05). However the decellularization did not change the strain of the artery (45 ± 15% vs. 53 ± 10%, p>0.05). When the scaffold was transplanted to the subcutaneous tissue in the wild type mice, there were less T cells appeared in the surrounding tissue which meant the decreased the immunogenicity by decellularization. This scaffold also supported the adhesion and proliferation of the MSCs. In this study, we constructed a biological compatible porous scaffold from the decellularized umbilical artery which may provide a suitable scaffold for cell-matrix interaction studies and for tissue engineering.

Silver Nanoparticles Synthesized Using Mint Extract and their Application in Chitosan/Gelatin Composite Packaging Film

NASA Astrophysics Data System (ADS)

Bhoir, Shraddha A.; Chawla, S. P.

The present study reports synthesis of silver nanoparticles (AgNPs) using mint extract (ME) in the presence of polyvinyl alcohol (PVA) as capping material. PVA, ME and silver nitrate at concentration of 1%, 0.01% and 0.02%, respectively were found to be optimum for the synthesis of nanoparticles. The formation of AgNPs was confirmed by measuring surface plasmon resonance (SPR) peak. The intensity of SPR peak remained unaltered thus suggesting stability of colloid without aggregation during storage. The nanoparticles inhibited the growth of food borne bacteria namely Escherichia coli, Pseudomonas aeruginosa and Bacillus cereus. The incorporation of these nanoparticles in chitosan and gelatin blend resulted in homogenous films. Mechanical properties and water vapor transmission rate of chitosan-gelatin films improved due to addition of AgNPs, whereas optical (opacity and UV light transmittance) and oxygen permeability properties remained unchanged. These films had the ability to inhibit growth of 5 log CFU of the above test organisms. These findings suggest that the AgNPs obtained by reduction of silver by ME can be effectively utilized to prepare antibacterial eco-friendly food packaging material.

Tricalcium phosphate and glutaraldehyde crosslinked gelatin incorporating bone morphogenetic protein--a viable scaffold for bone tissue engineering.

PubMed

Yang, Shu-Hua; Hsu, Chung-King; Wang, Kuo-Cheng; Hou, Sheng-Mou; Lin, Feng-Huei

2005-07-01

Bone defects caused by various etiologies must be filled with suitable substances to promote bone repair. Autogenous iliac crest graft is most frequently used, but is often associated with morbidities. Several bone graft substitutes have been developed to provide osteoconductive matrices as well as to enhance osteoinductivity. A tricalcium phosphate and glutaraldehyde crosslinked gelatin (GTG) scaffold, incorporated with bone morphogenetic proteins (BMPs), was developed to provide an alternative mean of bone tissue engineering. This study investigated differences between GTG and BMP-4 immobilized GTG (GTG-BMP) scaffolds on neonatal rat calvaria osteoblast activities. The GTG scaffold possessed an average pore size of 200 microm and a porosity of 75%. HE staining revealed uniform cell distribution throughout the scaffold 24 h post cell seeding. Alkaline phosphatase (ALP) activity of the GTG samples increased initially and then stabilized at 3 weeks postseeding. ALP activity of the GTG-BMP samples was similar to that of the GTG samples in the second and third weeks, but it continued increasing and became significantly greater than that of the GTG samples by the fourth week. Gla-type osteocalcin (Gla-OC) activity of the GTG-BMP samples was initially lower, but also became significantly greater than that of the GTG samples by the fourth week. An HE stain revealed greater numbers of attached cells and a richer matrix deposits in the GTG-BMP samples. A von Kossa stain showed larger mineralizing nodules, in greater numbers, after 4 weeks of in vitro cultivation. These findings suggest that the GTG scaffold provides an excellent porous structure, conductive to greater cell attachment and osteoblast differentiation, and that utility can be significantly enhanced by the inclusion of BMPs. A GTG-BMP scaffold holds promise as a superior bioactive material for bone tissue engineering. Copyright 2005 Wiley Periodicals, Inc.

3D-printed gelatin scaffolds of differing pore geometry modulate hepatocyte function and gene expression.

PubMed

Lewis, Phillip L; Green, Richard M; Shah, Ramille N

2018-03-15

Three dimensional (3D) printing is highly amenable to the fabrication of tissue-engineered organs of a repetitive microstructure such as the liver. The creation of uniform and geometrically repetitive tissue scaffolds can also allow for the control over cellular aggregation and nutrient diffusion. However, the effect of differing geometries, while controlling for pore size, has yet to be investigated in the context of hepatocyte function. In this study, we show the ability to precisely control pore geometry of 3D-printed gelatin scaffolds. An undifferentiated hepatocyte cell line (HUH7) demonstrated high viability and proliferation when seeded on 3D-printed scaffolds of two different geometries. However, hepatocyte specific functions (albumin secretion, CYP activity, and bile transport) increases in more interconnected 3D-printed gelatin cultures compared to a less interconnected geometry and to 2D controls. Additionally, we also illustrate the disparity between gene expression and protein function in simple 2D culture modes, and that recreation of a physiologically mimetic 3D environment is necessary to induce both expression and function of cultured hepatocytes. Three dimensional (3D) printing provides tissue engineers the ability spatially pattern cells and materials in precise geometries, however the biological effects of scaffold geometry on soft tissues such as the liver have not been rigorously investigated. In this manuscript, we describe a method to 3D print gelatin into well-defined repetitive geometries that show clear differences in biological effects on seeded hepatocytes. We show that a relatively simple and widely used biomaterial, such as gelatin, can significantly modulate biological processes when fabricated into specific 3D geometries. Furthermore, this study expands upon past research into hepatocyte aggregation by demonstrating how it can be manipulated to enhance protein function, and how function and expression may not precisely correlate in

Microwave-induced biomimetic approach for hydroxyapatite coatings of chitosan scaffolds.

PubMed

Kaynak Bayrak, Gökçe; Demirtaş, T Tolga; Gümüşderelioğlu, Menemşe

2017-02-10

Simulated body fluid (SBF) can form calcium phosphates on osteoinductive materials, so it is widely used for coating of bone scaffolds to mimic natural extracellular matrix (ECM). However, difficulties of bulk coating in 3D scaffolds and the necessity of long process times are the common problems for coating with SBF. In the present study, a microwave-assisted process was developed for rapid and internal coating of chitosan scaffolds. The scaffolds were fabricated as superporous hydrogel (SPH) by combining microwave irradiation and gas foaming methods. Then, they were immersed into 10x  SBF-like solution and homogenous bone-like hydroxyapatite (HA) coating was achieved by microwave treatment at 600W without the need of any nucleating agent. Cell culture studies with MC3T3-E1 preosteoblasts showed that microwave-assisted biomimetic HA coating process could be evaluated as an efficient and rapid method to obtain composite scaffolds for bone tissue engineering. Copyright © 2016 Elsevier Ltd. All rights reserved.

Chitosan-co-Hyaluronic acid porous cryogels and their application in tissue engineering.

PubMed

Kutlusoy, Tuğçe; Oktay, Burcu; Apohan, Nilhan Kayaman; Süleymanoğlu, Mediha; Kuruca, Serap Erdem

2017-10-01

In this work, the usability of chitosan-co-hyaluronic acid cryogels as a tissue-engineering scaffold was investigated. Chitosan-co-hyaluronic acid cryogels were synthesized at subzero temperature. Cryogels which were composed of various compositions of chitosan and hyaluronic acid (0, 10, 20, 30 and 50wt% hyaluronic acid) was prepared. Morphological studies showed that the macroporous cryogels have been developed with 90-95% porosity. Particularly, the mechanical and biomaterial property of pure chitosan was improved by making copolymer with hyaluronic acid in different concentration. The MTT cell viability results demonstrated that the cryogels have no significant cytotoxicity effect on 3T3 fibroblast and SAOS-2 cells. Copyright © 2017 Elsevier B.V. All rights reserved.

Composite porous scaffold of PEG/PLA support improved bone matrix deposition in vitro compared to PLA-only scaffolds.

PubMed

Bhaskar, Birru; Owen, Robert; Bahmaee, Hossein; Wally, Zena; Sreenivasa Rao, Parcha; Reilly, Gwendolen C

2018-05-01

Controllable pore size and architecture are essential properties for tissue-engineering scaffolds to support cell ingrowth colonization. To investigate the effect of polyethylene glycol (PEG) addition on porosity and bone-cell behavior, porous polylactic acid (PLA)-PEG scaffolds were developed with varied weight ratios of PLA-PEG (100/0, 90/10, 75/25) using solvent casting and porogen leaching. Sugar 200-300 µm in size was used as a porogen. To assess scaffold suitability for bone tissue engineering, MLO-A5 murine osteoblast cells were cultured and cell metabolic activity, alkaline phosphatase (ALP) activity and bone-matrix production determined using (alizarin red S staining for calcium and direct red 80 staining for collagen). It was found that metabolic activity was significantly higher over time on scaffolds containing PEG, ALP activity and mineralized matrix production were also significantly higher on scaffolds containing 25% PEG. Porous architecture and cell distribution and penetration into the scaffold were analyzed using SEM and confocal microscopy, revealing that inclusion of PEG increased pore interconnectivity and therefore cell ingrowth in comparison to pure PLA scaffolds. The results of this study confirmed that PLA-PEG porous scaffolds support mineralizing osteoblasts better than pure PLA scaffolds, indicating they have a high potential for use in bone tissue engineering applications. © 2018 Wiley Periodicals, Inc. J Biomed Mater Res Part A: 106A: 1334-1340, 2018. © 2018 Wiley Periodicals, Inc.

Development of highly porous scaffolds based on bioactive silicates for dental tissue engineering

DOE Office of Scientific and Technical Information (OSTI.GOV)

Goudouri, O.M., E-mail: menti.goudouri@ww.uni-erlangen.de; Department of Physics, Aristotle University of Thessaloniki, 54124 Thessaloniki; Theodosoglou, E.

Graphical abstract: - Highlights: • Synthesis of an Mg-based glass-ceramic via the sol–gel technique. • The heat treatment of the glass-ceramic promoted the crystallization of akermanite. • Akermanite scaffolds coated with gelatin were successfully fabricated. • An HCAp layer was developed on the surface of all scaffolds after 9 days in SBF. - Abstract: Various scaffolding materials, ceramics and especially Mg-based ceramic materials, including akermanite (Ca{sub 2}MgSi{sub 2}O{sub 7}) and diopside (CaMgSi{sub 2}O{sub 6}), have attracted interest for dental tissue regeneration because of their improved mechanical properties and controllable biodegradation. The aim of the present work was the synthesis ofmore » an Mg-based glass-ceramic, which would be used for the construction of workable akermanite scaffolds. The characterization of the synthesized material was performed by Fourier Transform Infrared Spectroscopy (FTIR) X-Ray Diffractometry (XRD) and Scanning Electron Microscopy (SEM). Finally, the apatite forming ability of the scaffolds was assessed by immersion in simulated body fluid. The scaffolds were fabricated by the foam replica technique and were subsequently coated with gelatin to provide a functional surface for increased cell attachment. Finally, SEM microphotographs and FTIR spectra of the scaffolds after immersion in SBF solution indicated the inorganic bioactive character of the scaffolds suitable for the intended applications in dental tissue engineering.« less

Collagen-gelatin-genipin-hydroxyapatite composite scaffolds colonized by human primary osteoblasts are suitable for bone tissue engineering applications: in vitro evidences.

PubMed

Vozzi, G; Corallo, C; Carta, S; Fortina, M; Gattazzo, F; Galletti, M; Giordano, N

2014-05-01

The application of porous hydroxyapatite (HAp)-collagen as a bone tissue engineering scaffold represents a new trend of mimicking the specific bone extracellular matrix (ECM). The use of HAp in reconstructive surgery has shown that it is slowly invaded by host tissue. Therefore, implant compatibility may be augmented by seeding cells before implantation. Human primary osteoblasts were seeded onto innovative collagen-gelatin-genipin (GP)-HAp scaffolds containing respectively 10%, 20%, and 30% HAp. Cellular adhesion, proliferation, alkaline phosphatase (ALP) activity, osteopontin (OPN), and osteocalcin (OC) expressions were evaluated after 3, 7, 15, and 21 days. The three types of scaffolds showed increased cellular proliferation over time in culture (maximum at 21 days) but the highest was recorded in 10% HAp scaffolds. ALP activity was the highest in 10% HAp scaffolds in all the times of evaluation. OC and OPN resulted in higher concentration in 10% HAp scaffolds compared to 20% and 30% HAp (maximum at 21 days). Finally, scanning electron microscopy analysis showed progressive scaffolds adhesion and colonization from the surface to the inside from day 3 to day 21. In vitro attachment, proliferation, and colonization of human primary osteoblasts on collagen-GP-HAp scaffolds with different percentages of HAp (10%, 20%, and 30%) all increased over time in culture, but comparing different percentages of HAp, they seem to increase with decreasing of HAp component. Therefore, the mechanical properties (such as the stiffness due to the HAp%) coupled with a good biomimetic component (collagen) are the parameters to set up in composite scaffolds design for bone tissue engineering. Copyright © 2013 Wiley Periodicals, Inc.

Biomedical potential of chitosan/HA and chitosan/β-1,3-glucan/HA biomaterials as scaffolds for bone regeneration--A comparative study.

PubMed

Przekora, Agata; Palka, Krzysztof; Ginalska, Grazyna

2016-01-01

The aim of this work was to compare biomedical potential of chitosan/hydroxyapatite (chit/HA) and novel chitosan/β-1,3-glucan/hydroxyapatite (chit/glu/HA) materials as scaffolds for bone regeneration via characterization of their biocompatibility, porosity, mechanical properties, and water uptake behaviour. Biocompatibility of the scaffolds was assessed in direct-contact with the materials using normal human foetal osteoblast cell line. Cytotoxicity and osteoblast proliferation rate were evaluated. Porosity was assessed using computed microtomography analysis and mechanical properties were determined by compression testing. Obtained results demonstrated that chit/HA scaffold possessed significantly better mechanical properties (compressive strength: 1.23 MPa, Young's modulus: 0.46 MPa) than chit/glu/HA material (compressive strength: 0.26 MPa, Young's modulus: 0.25 MPa). However, addition of bacterial β-1,3-glucan to the chit/HA scaffold improved its flexibility and porosity. Moreover, chit/glu/HA scaffold revealed significantly higher water uptake capability (52.6% after 24h of soaking) compared to the chit/HA (30.7%) and thus can serve as a very good drug delivery carrier. Chit/glu/HA scaffold was also more favourable to osteoblast survival (near 100% viability after 24-h culture), proliferation, and spreading compared to the chit/HA (63% viability). The chit/glu/HA possesses better biomedical potential than chit/HA scaffold. Nevertheless, poor mechanical properties of the chit/glu/HA limit its application to non-load bearing implantation area. Copyright © 2015 Elsevier B.V. All rights reserved.

Chitosan-Based Bilayer Hydroxyapatite Nanorod Composite Scaffolds for Osteochondral Regeneration

NASA Astrophysics Data System (ADS)

Swanson, Shawn

Osteochondral defects involve injury to bone and cartilage. As articular cartilage is worn down, bone in the joint begins to rub together, causing bone spurs. This is known as osteoarthritis, and is a common issue among the aging population. This problem presents an interesting opportunity for tissue engineering. Tissue engineering is an approach to treatment of tissue defects where synthetic, three dimensional (3-D) scaffolds are implanted in a defect to facilitate healing. The osteochondral scaffold consists of two regions in the form of a bilayer scaffold- one to mimic bone with osteoconductive properties, and one to mimic cartilage with biomimetic properties. One approach to improving the osteoconductivity of tissue engineering scaffolds is the addition of hydroxyapatite (HAp), the main mineral phase in bone. HAp with nanorod morphology is desirable because it is biomimetic for the calcium phosphate found in bone. Incorporating HAp nanorods in bone tissue engineering scaffolds to form a composite material may increase scaffold osteoconductivity. The cartilage scaffold is fabricated from chitosan and hyaluronic acid (HA). HA is a known component of cartilage and thus is biomimetic. The bilayer scaffolds were seeded with osteoblast-like MG-63 cells to investigate cell migration and were evaluated with Alamar Blue proliferation assay. The cells successfully migrated to the bone region of the scaffold, indicating that the bilayer scaffold provides a promising osteochondral scaffold.

Exploring the kinetics of gelation and final architecture of enzymatically cross-linked chitosan/gelatin gels.

PubMed

da Silva, Marcelo A; Bode, Franziska; Grillo, Isabelle; Dreiss, Cécile A

2015-04-13

Small-angle neutron scattering (SANS) was used to characterize the nanoscale structure of enzymatically cross-linked chitosan/gelatin hydrogels obtained from two protocols: a pure chemical cross-linking process (C), which uses the natural enzyme microbial transglutaminase, and a physical-co-chemical (PC) hybrid process, where covalent cross-linking is combined with the temperature-triggered gelation of gelatin, occurring through the formation of triple-helices. SANS measurements on the final and evolving networks provide a correlation length (ξ), which reflects the average size of expanding clusters. Their growth in PC gels is restricted by the triple-helices (ξ ∼ 10s of Å), while ξ in pure chemical gels increases with cross-linker concentration (∼100s of Å). In addition, the shear elastic modulus in PC gels is higher than in pure C gels. Our results thus demonstrate that gelatin triple helices provide a template to guide the cross-linking process; overall, this work provides important structural insight to improve the design of biopolymer-based gels.

A novel porous scaffold fabrication technique for epithelial and endothelial tissue engineering.

PubMed

McHugh, Kevin J; Tao, Sarah L; Saint-Geniez, Magali

2013-07-01

Porous scaffolds have the ability to minimize transport barriers for both two- (2D) and three-dimensional tissue engineering. However, current porous scaffolds may be non-ideal for 2D tissues such as epithelium due to inherent fabrication-based characteristics. While 2D tissues require porosity to support molecular transport, pores must be small enough to prevent cell migration into the scaffold in order to avoid non-epithelial tissue architecture and compromised function. Though electrospun meshes are the most popular porous scaffolds used today, their heterogeneous pore size and intense topography may be poorly-suited for epithelium. Porous scaffolds produced using other methods have similar unavoidable limitations, frequently involving insufficient pore resolution and control, which make them incompatible with 2D tissues. In addition, many of these techniques require an entirely new round of process development in order to change material or pore size. Herein we describe "pore casting," a fabrication method that produces flat scaffolds with deterministic pore shape, size, and location that can be easily altered to accommodate new materials or pore dimensions. As proof-of-concept, pore-cast poly(ε-caprolactone) (PCL) scaffolds were fabricated and compared to electrospun PCL in vitro using canine kidney epithelium, human colon epithelium, and human umbilical vein endothelium. All cell types demonstrated improved morphology and function on pore-cast scaffolds, likely due to reduced topography and universally small pore size. These results suggest that pore casting is an attractive option for creating 2D tissue engineering scaffolds, especially when the application may benefit from well-controlled pore size or architecture.

Chitosan and Its Potential Use as a Scaffold for Tissue Engineering in Regenerative Medicine

PubMed Central

Rodríguez-Vázquez, Martin; Vega-Ruiz, Brenda; Ramos-Zúñiga, Rodrigo; Saldaña-Koppel, Daniel Alexander; Quiñones-Olvera, Luis Fernando

2015-01-01

Tissue engineering is an important therapeutic strategy to be used in regenerative medicine in the present and in the future. Functional biomaterials research is focused on the development and improvement of scaffolding, which can be used to repair or regenerate an organ or tissue. Scaffolds are one of the crucial factors for tissue engineering. Scaffolds consisting of natural polymers have recently been developed more quickly and have gained more popularity. These include chitosan, a copolymer derived from the alkaline deacetylation of chitin. Expectations for use of these scaffolds are increasing as the knowledge regarding their chemical and biological properties expands, and new biomedical applications are investigated. Due to their different biological properties such as being biocompatible, biodegradable, and bioactive, they have given the pattern for use in tissue engineering for repair and/or regeneration of different tissues including skin, bone, cartilage, nerves, liver, and muscle. In this review, we focus on the intrinsic properties offered by chitosan and its use in tissue engineering, considering it as a promising alternative for regenerative medicine as a bioactive polymer. PMID:26504833

Cytotoxicity assessment of polyhydroxybutyrate/chitosan/nano- bioglass nanofiber scaffolds by stem cells from human exfoliated deciduous teeth stem cells from dental pulp of exfoliated deciduous tooth.

PubMed

Hashemi-Beni, Batool; Khoroushi, Maryam; Foroughi, Mohammad Reza; Karbasi, Saeed; Khademi, Abbas Ali

2018-01-01

The aim of this study was to compare the cytotoxicity and the biocompatibility of three different nanofibers scaffolds after seeding of stem cells harvested from human deciduous dental pulp. Given the importance of scaffold and its features in tissue engineering, this study demonstrated the construction of polyhydroxybutyrate (PHB)/chitosan/nano-bioglass (nBG) nanocomposite scaffold using electrospinning method. This experimental study was conducted on normal exfoliated deciduous incisors obtained from 6-year-old to 11-year-old healthy children. The dental pulp was extracted from primary incisor teeth which are falling aseptically. After digesting the tissue with 4 mg/ml of type I collagenase, the cells were cultured in medium solution. Identification of stem cells from human exfoliated deciduous teeth was performed by flowcytometry using CD19, CD14, CD146, and CD90 markers. Then, 1 × 10 4 stem cells were seeded on the scaffold with a diameter of 10 mm × 0.3 mm. Cell viability was evaluated on days 3, 5, and 7 through methyl thiazol tetrazolium techniques ( P < 0.05) on different groups that they are groups included (1) PHB scaffold (G1), (2) PHB/chitosan scaffold (G2), (3) the optimal PHB/chitosan/nBG scaffold (G3), (4) mineral trioxide aggregate (MTA), and (5) the G3 + MTA scaffold (G3 + MTA). Data were analyzed with two-way ANOVA at significance level of P < 0.05. The results indicated that the PHB/chitosan/nBG scaffold and PHB/chitosan/nBG scaffold + MTA groups showed significant difference compared with the PHB/chitosan scaffold and PHB scaffold groups on the 7 th day ( P < 0.05). Thus, it can be concluded that the scaffold with nBG nanoparticles is more biocompatible than the other scaffolds and can be considered as a suitable scaffold for growth and proliferation of stem cells.

Strategies on process engineering of chondrocyte culture for cartilage tissue regeneration.

PubMed

Mallick, Sarada Prasanna; Rastogi, Amit; Tripathi, Satyavrat; Srivastava, Pradeep

2017-04-01

The current work is an attempt to study the strategies for cartilage tissue regeneration using porous scaffold in wavy walled airlift bioreactor (ALBR). Novel chitosan, poly (L-lactide) and hyaluronic acid based composite scaffold were prepared. The scaffolds were cross-linked with 1-ethyl-3-(3-dimethylaminopropyl) carbodiimide, N-hydroxysuccinimide and chondroitin sulfate to obtain interconnected 3D microstructure showing excellent biocompatibility, higher cellular differentiation and increased stability. The surface morphology and porosity of the scaffolds were analyzed using scanning electron microscopy (SEM) and mercury intrusion porosimeter and optimized for chondrocyte regeneration. The study shows that the scaffolds were highly porous with pore size ranging from 48 to 180 µm and the porosities in the range 80-92%. Swelling and in vitro degradation studies were performed for the composite scaffolds; by increasing the chitosan: HA ratio in the composite scaffolds, the swelling property increases and stabilizes after 24 h. There was controlled degradation of composite scaffolds for 4 weeks. The uniform chondrocyte distribution in the scaffold using various growth modes in the shake flask and ALBR was studied by glycosaminoglycans (GAG) quantification, MTT assay and mixing time evaluation. The cell culture studies demonstrated that efficient designing of ALBR increases the cartilage regeneration as compared to using a shake flask. The free chondrocyte microscopy and cell attachment were performed by inverted microscope and SEM, and from the study it was confirmed that the cells uniformly attached to the scaffold. This study focuses on optimizing strategies for the culture of chondrocyte using suitable scaffold for improved cartilage tissue regeneration.

The effect of hydroxyapatite in biopolymer-based scaffolds on release of naproxen sodium.

PubMed

Asadian-Ardakani, Vahid; Saber-Samandari, Samaneh; Saber-Samandari, Saeed

2016-12-01

A scaffold capable of controlling drug release is highly desirable for bone tissue engineering. The objective of this study was to develop and characterize a highly porous biodegradable scaffold and evaluate the kinetic release behavior for the application of anti-inflammatory drug delivery. Porous scaffolds consisting of chitosan, poly(acrylic acid), and nano-hydroxyapatite were prepared using the freeze-drying method. The nanocomposite scaffolds were characterized for structure, pore size, porosity, and mechanical properties. The nanocomposite scaffolds were tested and characterized using Fourier transform infrared (FTIR) spectroscopy, scanning electron microscopy (SEM), energy-dispersive analysis of X-ray (EDS), X-ray diffraction (XRD) analysis, and tensile test instrument. The results showed that the pores of the scaffolds were interconnected, and their sizes ranged from 145 µm to 213 μm. The mechanical properties were found close to those of trabecular bone of the same density. The ability of the scaffolds to deliver naproxen sodium as a model drug in vitro was investigated. The release profile of naproxen sodium was measured in a phosphate-buffered saline solution by a ultra-violet spectrophotometer that was controlled by the Fickian diffusion mechanism. These results indicated that the chitosan-graft-poly(acrylic acid)/nano-hydroxyapatite scaffold may be a promising biomedical scaffold for clinical use in bone tissue engineering with a potential for drug delivery. © 2016 Wiley Periodicals, Inc. J Biomed Mater Res Part A: 104A: 2992-3003, 2016. © 2016 Wiley Periodicals, Inc.

Immobilized Lentivirus Vector on Chondroitin Sulfate-Hyaluronate Acid-Silk Fibroin Hybrid Scaffold for Tissue-Engineered Ligament-Bone Junction

PubMed Central

Sun, Liguo; Li, Hongguo; Qu, Ling; Zhu, Rui; Fan, Xiangli; Xue, Yingsen; Xie, Zhenghong; Fan, Hongbin

2014-01-01

The lack of a fibrocartilage layer between graft and bone remains the leading cause of graft failure after anterior cruciate ligament (ACL) reconstruction. The objective of this study was to develop a gene-modified silk cable-reinforced chondroitin sulfate-hyaluronate acid-silk fibroin (CHS) hybrid scaffold for reconstructing the fibrocartilage layer. The scaffold was fabricated by lyophilizing the CHS mixture with braided silk cables. The scanning electronic microscopy (SEM) showed that microporous CHS sponges were formed around silk cables. Each end of scaffold was modified with lentiviral-mediated transforming growth factor-β3 (TGF-β3) gene. The cells on scaffold were transfected by bonded lentivirus. In vitro culture demonstrated that mesenchymal stem cells (MSCs) on scaffolds proliferated vigorously and produced abundant collagen. The transcription levels of cartilage-specific genes also increased with culture time. After 2 weeks, the MSCs were distributed uniformly throughout scaffold. Deposited collagen was also found to increase. The chondral differentiation of MSCs was verified by expressions of collagen II and TGF-β3 genes in mRNA and protein level. Histology also confirmed the production of cartilage extracellular matrix (ECM) components. The results demonstrated that gene-modified silk cable-reinforced CHS scaffold was capable of supporting cell proliferation and differentiation to reconstruct the cartilage layer of interface. PMID:25019087

Effect of freezing temperature in thermally induced phase separation method in hydroxyapatite/chitosan-based bone scaffold biomaterial

NASA Astrophysics Data System (ADS)

Albab, Muh Fadhil; Yuwono, Akhmad Herman; Sofyan, Nofrijon; Ramahdita, Ghiska

2017-02-01

In the current study, hydroxyapatite (HA)/chitosan-based bone scaffold has been fabricated using Thermally Induced Phase Separation (TIPS) method under freezing temperature variation of -20, -30, -40 and -80 °C. The samples with weight percent ratio of 70% HA and 30% chitosan were homogeneously mixed and subsequently dissolved in 2% acetic acid. The synthesized samples were further characterized using Fourier transform infrared (FTIR), compressive test and scanning electron microscope (SEM). The investigation results showed that low freezing temperature reduced the pore size and increased the compressive strength of the scaffold. In the freezing temperature of -20 °C, the pore size was 133.93 µm with the compressive strength of 5.9 KPa, while for -80 °C, the pore size declined to 60.55 µm with the compressive strength 29.8 KPa. Considering the obtained characteristics, HA/chitosan obtained in this work has potential to be applied as a bone scaffold.

Fabrication of chitosan-silver nanoparticle hybrid 3D porous structure as a SERS substrate for biomedical applications

NASA Astrophysics Data System (ADS)

Jung, Gyeong-Bok; Kim, Ji-Hye; Burm, Jin Sik; Park, Hun-Kuk

2013-05-01

We propose a simple, low-cost, large-area, and functional surface enhanced Raman scattering (SERS) substrate for biomedical applications. The SERS substrate with chitosan-silver nanoparticles (chitosan-Ag NPs) hybrid 3D porous structure was fabricated simply by a one-step method. The chitosan was used as a template for the Ag NPs deposition. SERS enhancement by the chitosan-Ag NPs substrate was experimentally verified using rhodamine B as an analyte. Thiolated single stranded DNA was also measured for atopic dermatitis genetic markers (chemokines CCL17) at a low concentration of 5 pM. We successfully designed a novel SERS substrate with silver nanoparticle hybridized 3D porous chitosan that has the potential to become a highly sensitive and selective tool for biomedical applications.

Scaffolds containing chitosan/carboxymethyl cellulose/mesoporous wollastonite for bone tissue engineering.

PubMed

Sainitya, R; Sriram, M; Kalyanaraman, V; Dhivya, S; Saravanan, S; Vairamani, M; Sastry, T P; Selvamurugan, N

2015-09-01

Scaffold based bone tissue engineering utilizes a variety of biopolymers in different combinations aiming to deliver optimal properties required for bone regeneration. In the current study, we fabricated bio-composite scaffolds containing chitosan (CS), carboxymethylcellulose (CMC) with varied concentrations of mesoporous wollastonite (m-WS) particles by the freeze drying method. The CS/CMC/m-WS scaffolds were characterized by the SEM, EDS and FT-IR studies. Addition of m-WS particles had no effect on altering the porosity of the scaffolds. m-WS particles at 0.5% concentration in the CS/CMC scaffolds showed significant improvement in the bio-mineralization and protein adsorption properties. Addition of m-WS particles in the CS/CMC scaffolds significantly reduced their swelling and degradation properties. The CS/CMC/m-WS scaffolds also showed cyto-friendly nature to human osteoblastic cells. The osteogenic potential of CS/CMC/m-WS scaffolds was confirmed by calcium deposition and expression of an osteoblast specific microRNA, pre-mir-15b. Thus, the current investigations support the use of CS/CMC/m-WS scaffolds for bone tissue engineering applications. Copyright © 2015 Elsevier B.V. All rights reserved.

Enhancing the mechanical and in vitro performance of robocast bioglass scaffolds by polymeric coatings: Effect of polymer composition.

PubMed

Motealleh, Azadeh; Eqtesadi, Siamak; Pajares, Antonia; Miranda, Pedro

2018-08-01

The effect of different polymeric coatings, including natural and synthetic compositions, on the mechanical performance of 45S5 bioglass robocast scaffolds is systematically analyzed in this work. Fully amorphous 45S5 bioglass robocast scaffolds sintered at 550 °C were impregnated with natural (gelatin, alginate, and chitosan) and synthetic (polycaprolactone, PCL and poly-lactic acid, PLA) polymers through a dip-coating process. Mechanical enhancement provided by these coatings in terms of both compressive strength and strain energy density was evaluated. Natural polymers, in general, and chitosan, in particular, were found to produce the greater reinforcement. The effect of these coatings on the in vitro bioactivity and degradation behavior of 45S5 bioglass robocast scaffolds was also investigated through immersion tests in simulated body fluid (SBF). Coatings from natural polymers, especially chitosan, are shown to have a positive effect on the bioactivity of 45S5 bioglass, accelerating the formation of an apatite-like layer. Besides, most coating compositions reduced the degradation (weight loss) rate of the scaffold, which has a positive impact on the evolution of their mechanical properties. Copyright © 2018 Elsevier Ltd. All rights reserved.

Porous ceramic scaffolds with complex architectures

NASA Astrophysics Data System (ADS)

Munch, E.; Franco, J.; Deville, S.; Hunger, P.; Saiz, E.; Tomsia, A. P.

2008-06-01

This work compares two novel techniques for the fabrication of ceramic scaffolds for bone tissue engineering with complex porosity: robocasting and freeze casting. Both techniques are based on the preparation of concentrated ceramic suspensions with suitable properties for the process. In robocasting, the computer-guided deposition of the suspensions is used to build porous materials with designed three dimensional geometries and microstructures. Freeze casting uses ice crystals as a template to form porous lamellar ceramic materials. Preliminary results on the compressive strengths of the materials are also reported.

Supercritical CO2 assisted process for the production of high-purity and sterile nano-hydroxyapatite/chitosan hybrid scaffolds.

PubMed

Ruphuy, G; Souto-Lopes, M; Paiva, D; Costa, P; Rodrigues, A E; Monteiro, F J; Salgado, C L; Fernandes, M H; Lopes, J C; Dias, M M; Barreiro, M F

2018-04-01

Hybrid scaffolds composed of hydroxyapatite (HAp), in particular in its nanometric form (n-HAp), and chitosan (CS) are promising materials for non-load-bearing bone graft applications. The main constraints of their production concern the successful implementation of the final purification/neutralization and sterilization steps. Often, the used purification strategies can compromise scaffold structural features, and conventional sterilization techniques can result in material's thermal degradation and/or contamination with toxic residues. In this context, this work presents a process to produce n-HAp/CS scaffolds mimicking bone composition and structure, where an innovative single step based on supercritical CO 2 extraction was used for both purification and sterilization. A removal of 80% of the residual acetic acid was obtained (T = 75°C, p = 8.0 MPa, 2 extraction cycles of 2 h) giving rise to scaffolds exhibiting adequate interconnected porous structure, fast swelling and storage modulus compatible with non-load-bearing applications. Moreover, the obtained scaffolds showed cytocompatibility and osteoconductivity without further need of disinfection/sterilization procedures. Among the main advantages, the proposed process comprises only three steps (n-HAp/CS dispersion preparation; freeze-drying; and supercritical CO 2 extraction), and the supercritical CO 2 extraction show clear advantages over currently used procedures based on neutralization steps. © 2017 Wiley Periodicals, Inc. J Biomed Mater Res Part B: Appl Biomater, 106B: 965-975, 2018. © 2017 Wiley Periodicals, Inc.

Interaction of chitin/chitosan with salivary and other epithelial cells-An overview.

PubMed

Patil, Sharvari Vijaykumar; Nanduri, Lalitha S Y

2017-11-01

Chitin and its deacetylated form, chitosan, have been widely used for tissue engineering of both epithelial and mesenchymal tissues. Epithelial cells characterised by their sheet-like tight cellular arrangement and polarised nature, constitute a major component in various organs and play a variety of roles including protection, secretion and maintenance of tissue homeostasis. Regeneration of damaged epithelial tissues has been studied using biomaterials such as chitin, chitosan, hyaluronan, gelatin and alginate. Chitin and chitosan are known to promote proliferation of various embryonic and adult epithelial cells. However it is not clearly understood how this activity is achieved or what are the mechanisms involved in the chitin/chitosan driven proliferation of epithelial cells. Mechanistic understanding of influence of chitin/chitosan on epithelial cells will guide us to develop more targeted regenerative scaffold/hydrogel systems. Therefore, current review attempts to elicit a mechanistic insight into how chitin and chitosan interact with salivary, mammary, skin, nasal, lung, intestinal and bladder epithelial cells. Copyright © 2017 Elsevier B.V. All rights reserved.

Culture on 3D Chitosan-Hyaluronic Acid Scaffolds Enhances Stem Cell Marker Expression and Drug Resistance in Human Glioblastoma Cancer Stem Cells.

PubMed

Wang, Kui; Kievit, Forrest M; Erickson, Ariane E; Silber, John R; Ellenbogen, Richard G; Zhang, Miqin

2016-12-01

The lack of in vitro models that support the growth of glioblastoma (GBM) stem cells (GSCs) that underlie clinical aggressiveness hinders developing new, effective therapies for GBM. While orthotopic patient-derived xenograft models of GBM best reflect in vivo tumor behavior, establishing xenografts is a time consuming, costly, and frequently unsuccessful endeavor. To address these limitations, a 3D porous scaffold composed of chitosan and hyaluronic acid (CHA) is synthesized. Growth and expression of the cancer stem cell (CSC) phenotype of the GSC GBM6 taken directly from fresh xenogratfs grown on scaffolds or as adherent monolayers is compared. While 2D adherent cultures grow as monolayers of flat epitheliod cells, GBM6 cells proliferate within pores of CHA scaffolds as clusters of self-adherent ovoid cells. Growth on scaffolds is accompanied by greater expression of genes that mediate epithelial-mesenchymal transition and maintain a primitive, undifferentiated phenotype, hallmarks of CSCs. Scaffold-grown cells also display higher expression of genes that promote resistance to hypoxia-induced oxidative stress. In accord, scaffold-grown cells show markedly greater resistance to clinically utilized alkylating agents compared to adherent cells. These findings suggest that our CHA scaffolds better mimic in vivo biological and clinical behavior and provide insights for developing novel individualized treatments. © 2016 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

The effect of controlled release of PDGF-BB from heparin-conjugated electrospun PCL/gelatin scaffolds on cellular bioactivity and infiltration

PubMed Central

Lee, Jongman; Yoo, James J.; Atala, Anthony; Lee, Sang Jin

2013-01-01

Heparin-conjugated electrospun poly(ε-caprolactone) (PCL)/gelatin scaffolds were developed to provide controlled release of platelet-derived growth factor-BB (PDGF-BB) and allow prolonged bioactivity of this molecule. A mixture of PCL and gelatin was electrospun into three different morphologies. Next, heparin molecules were conjugated to the reactive surface of the scaffolds. This heparin-conjugated scaffold allowed the immobilization of PDGF-BB via electrostatic interaction. In vitro PDGF-BB release profiles indicated that passive physical adsorption of PDGF-BB to non-heparinized scaffolds resulted in an initial burst release of PDGF-BB within 5 days, which then leveled off. However, electrostatic interaction between PDGF-BB and the heparin-conjugated scaffolds gave rise to a sustained release of PDGF-BB over the course of 20 days without an initial burst. Moreover, PDGF-BB that was strongly bound to the heparin-conjugated scaffolds enhanced smooth muscle cell (SMC) proliferation. In addition, scaffolds composed of 3.0 µm diameter fibers that were immobilized with PDGF-BB accelerated SMC infiltration into the scaffold when compared to scaffolds composed of smaller diameter fibers or scaffolds that did not release PDGF-BB. We concluded that the combination of the large pore structure in the scaffolds and the heparin-mediated delivery of PDGF-BB provided the most effective cellular interactions through synergistic physical and chemical cues. PMID:22770570

Cytotoxicity assessment of polyhydroxybutyrate/chitosan/nano- bioglass nanofiber scaffolds by stem cells from human exfoliated deciduous teeth stem cells from dental pulp of exfoliated deciduous tooth

PubMed Central

Hashemi-Beni, Batool; Khoroushi, Maryam; Foroughi, Mohammad Reza; Karbasi, Saeed; Khademi, Abbas Ali

2018-01-01

Background: The aim of this study was to compare the cytotoxicity and the biocompatibility of three different nanofibers scaffolds after seeding of stem cells harvested from human deciduous dental pulp. Given the importance of scaffold and its features in tissue engineering, this study demonstrated the construction of polyhydroxybutyrate (PHB)/chitosan/nano-bioglass (nBG) nanocomposite scaffold using electrospinning method. Materials and Methods: This experimental study was conducted on normal exfoliated deciduous incisors obtained from 6-year-old to 11-year-old healthy children. The dental pulp was extracted from primary incisor teeth which are falling aseptically. After digesting the tissue with 4 mg/ml of type I collagenase, the cells were cultured in medium solution. Identification of stem cells from human exfoliated deciduous teeth was performed by flowcytometry using CD19, CD14, CD146, and CD90 markers. Then, 1 × 104 stem cells were seeded on the scaffold with a diameter of 10 mm × 0.3 mm. Cell viability was evaluated on days 3, 5, and 7 through methyl thiazol tetrazolium techniques (P < 0.05) on different groups that they are groups included (1) PHB scaffold (G1), (2) PHB/chitosan scaffold (G2), (3) the optimal PHB/chitosan/nBG scaffold (G3), (4) mineral trioxide aggregate (MTA), and (5) the G3 + MTA scaffold (G3 + MTA). Data were analyzed with two-way ANOVA at significance level of P < 0.05. Results: The results indicated that the PHB/chitosan/nBG scaffold and PHB/chitosan/nBG scaffold + MTA groups showed significant difference compared with the PHB/chitosan scaffold and PHB scaffold groups on the 7th day (P < 0.05). Conclusion: Thus, it can be concluded that the scaffold with nBG nanoparticles is more biocompatible than the other scaffolds and can be considered as a suitable scaffold for growth and proliferation of stem cells. PMID:29576778

Tumor cell culture on collagen-chitosan scaffolds as three-dimensional tumor model: A suitable model for tumor studies.

PubMed

Mahmoudzadeh, Aziz; Mohammadpour, Hemn

2016-07-01

Tumor cells naturally live in three-dimensional (3D) microenvironments, while common laboratory tests and evaluations are done in two-dimensional (2D) plates. This study examined the impact of cultured 4T1 cancer cells in a 3D collagen-chitosan scaffold compared with 2D plate cultures. Collagen-chitosan scaffolds were provided and passed confirmatory tests. 4T1 tumor cells were cultured on scaffolds and then tumor cells growth rate, resistance to X-ray radiation, and cyclophosphamide as a chemotherapy drug were analyzed. Furthermore, 4T1 cells were extracted from the scaffold model and were injected into the mice. Tumor growth rate, survival rate, and systemic immune responses were evaluated. Our results showed that 4T1 cells infiltrated the scaffolds pores and constructed a 3D microenvironment. Furthermore, 3D cultured tumor cells showed a slower proliferation rate, increased levels of survival to the X-ray irradiation, and enhanced resistance to chemotherapy drugs in comparison with 2D plate cultures. Transfer of extracted cells to the mice caused enhanced tumor volume and decreased life span. This study indicated that collagen-chitosan nanoscaffolds provide a suitable model of tumor that would be appropriate for tumor studies. Copyright © 2016. Published by Elsevier B.V.

Fabrication of chitin-chitosan/nano TiO2-composite scaffolds for tissue engineering applications.

PubMed

Jayakumar, R; Ramachandran, Roshni; Divyarani, V V; Chennazhi, K P; Tamura, H; Nair, S V

2011-03-01

In this study, we prepared chitin-chitosan/nano TiO(2) composite scaffolds using lyophilization technique for bone tissue engineering. The prepared composite scaffold was characterized using SEM, XRD, FTIR and TGA. In addition, swelling, degradation and biomineralization capability of the composite scaffolds were evaluated. The developed composite scaffold showed controlled swelling and degradation when compared to the control scaffold. Cytocompatibility of the scaffold was assessed by MTT assay and cell attachment studies using osteoblast-like cells (MG-63), fibroblast cells (L929) and human mesenchymal stem cells (hMSCs). Results indicated no sign of toxicity and cells were found attached to the pore walls within the scaffolds. These results suggested that the developed composite scaffold possess the prerequisites for tissue engineering scaffolds and it can be used for tissue engineering applications. Copyright © 2010 Elsevier B.V. All rights reserved.

Preparation and characterization of shape memory polymer scaffolds via solvent casting/particulate leaching.

PubMed

De Nardo, Luigi; Bertoldi, Serena; Cigada, Alberto; Tanzi, Maria Cristina; Haugen, Håvard Jostein; Farè, Silvia

2012-09-27

Porous Shape Memory Polymers (SMPs) are ideal candidates for the fabrication of defect fillers, able to support tissue regeneration via minimally invasive approaches. In this regard, control of pore size, shape and interconnection is required to achieve adequate nutrient transport and cell ingrowth. Here, we assessed the feasibility of the preparation of SMP porous structures and characterized their chemico-physical properties and in vitro cell response. SMP scaffolds were obtained via solvent casting/particulate leaching of gelatin microspheres, prepared via oil/water emulsion. A solution of commercial polyether-urethane (MM-4520, Mitsubishi Heavy Industries) was cast on compacted microspheres and leached-off after polymer solvent evaporation. The obtained structures were characterized in terms of morphology (SEM and micro-CT), thermo-mechanical properties (DMTA), shape recovery behavior in compression mode, and in vitro cytocompatibility (MG63 Osteoblast-like cell line). The fabrication process enabled easy control of scaffold morphology, pore size, and pore shape by varying the gelatin microsphere morphology. Homogeneous spherical and interconnected pores have been achieved together with the preservation of shape memory ability, with recovery rate up to 90%. Regardless of pore dimensions, MG63 cells were observed adhering and spreading onto the inner surface of the scaffolds obtained for up to seven days of static in vitro tests. A new class of SMP porous structures has been obtained and tested in vitro: according to these preliminary results reported, SMP scaffolds can be further exploited in the design of a new class of implantable devices.

A TPMS-based method for modeling porous scaffolds for bionic bone tissue engineering.

PubMed

Shi, Jianping; Zhu, Liya; Li, Lan; Li, Zongan; Yang, Jiquan; Wang, Xingsong

2018-05-09

In the field of bone defect repair, gradient porous scaffolds have received increased attention because they provide a better environment for promoting tissue regeneration. In this study, we propose an effective method to generate bionic porous scaffolds based on the TPMS (triply periodic minimal surface) and SF (sigmoid function) methods. First, cortical bone morphological features (e.g., pore size and distribution) were determined for several regions of a rabbit femoral bone by analyzing CT-scans. A finite element method was used to evaluate the mechanical properties of the bone at these respective areas. These results were used to place different TPMS substructures into one scaffold domain with smooth transitions. The geometrical parameters of the scaffolds were optimized to match the elastic properties of a human bone. With this proposed method, a functional gradient porous scaffold could be designed and produced by an additive manufacturing method.

Chitosan Composites for Bone Tissue Engineering—An Overview

PubMed Central

Venkatesan, Jayachandran; Kim, Se-Kwon

2010-01-01

Bone contains considerable amounts of minerals and proteins. Hydroxyapatite [Ca10(PO4)6(OH)2] is one of the most stable forms of calcium phosphate and it occurs in bones as major component (60 to 65%), along with other materials including collagen, chondroitin sulfate, keratin sulfate and lipids. In recent years, significant progress has been made in organ transplantation, surgical reconstruction and the use of artificial protheses to treat the loss or failure of an organ or bone tissue. Chitosan has played a major role in bone tissue engineering over the last two decades, being a natural polymer obtained from chitin, which forms a major component of crustacean exoskeleton. In recent years, considerable attention has been given to chitosan composite materials and their applications in the field of bone tissue engineering due to its minimal foreign body reactions, an intrinsic antibacterial nature, biocompatibility, biodegradability, and the ability to be molded into various geometries and forms such as porous structures, suitable for cell ingrowth and osteoconduction. The composite of chitosan including hydroxyapatite is very popular because of the biodegradability and biocompatibility in nature. Recently, grafted chitosan natural polymer with carbon nanotubes has been incorporated to increase the mechanical strength of these composites. Chitosan composites are thus emerging as potential materials for artificial bone and bone regeneration in tissue engineering. Herein, the preparation, mechanical properties, chemical interactions and in vitro activity of chitosan composites for bone tissue engineering will be discussed. PMID:20948907

Evaluation of structural and mechanical properties of electrospun nano-micro hybrid of poly hydroxybutyrate-chitosan/silk scaffold for cartilage tissue engineering.

PubMed

Karbasi, Saeed; Fekrat, Farnoosh; Semnani, Daryoush; Razavi, Shahnaz; Zargar, Elham Naghash

2016-01-01

One of the new methods of scaffold fabrication is a nano-micro hybrid structure in which the properties of the scaffold are improved by introducing nanometer and micrometer structures. This method could be suitable for scaffold designing if some features improve. In this study, electrospun nanofibers of 9% weight solution of poly (3-hydroxybutyrate) (P3HB) and a 15% weight of chitosan by trifluoroacetic acid were coated on both the surface of a silk knitted substrate in the optimum condition to improve the mechanical properties of scaffolds for cartilage tissue engineering application. These hybrid nano-micro fibrous scaffolds were characterized by structural and mechanical evaluation methods. Scanning electron microscopy values and porosity analysis showed that average diameter of nanofibers was 584.94 nm in electrospinning part and general porosity was more than 80%. Fourier transform infrared spectroscopy results indicated the presence of all elements without pollution. The tensile test also stated that by electrospinning, as well as adding chitosan, both maximum strength and maximum elongation increased to 187 N and 10 mm. It means that the microfibrous part of scaffold could affect mechanical properties of nano part of the hybrid scaffold, significantly. It could be concluded that P3HB-chitosan/silk hybrid scaffolds can be a good candidate for cartilage tissue engineering.

Effects of chitosan and bioactive glass modifications of knitted and rolled polylactide-based 96/4 L/D scaffolds on chondrogenic differentiation of adipose stem cells.

PubMed

Ahtiainen, Katja; Sippola, Laura; Nurminen, Manu; Mannerström, Bettina; Haimi, Suvi; Suuronen, Riitta; Hyttinen, Jari; Ylikomi, Timo; Kellomäki, Minna; Miettinen, Susanna

2015-01-01

The performance of biodegradable knitted and rolled 3-dimensional (3D) polylactide-based 96/4 scaffolds modified with bioactive glass (BaG) 13-93, chitosan and both was compared with regard to the viability, proliferation and chondrogenic differentiation of rabbit adipose stem cells (ASCs). Scaffold porosities were determined by micro-computed tomography (μCT). Water absorption and degradation of scaffolds were studied during 28-day hydrolysis in Tris-buffer. Viability, number and differentiation of ASCs in PLA96/4 scaffolds were examined in vitro. The dimensions of the scaffolds were maintained during hydrolysis and mass loss was detected only in the BaG13-93 containing scaffolds. ASCs adhered and proliferated on each scaffold type. Cell aggregation and expression of chondral matrix components improved in all scaffold types in chondrogenic medium. Signs of hypertrophy were detected in the modified scaffolds but not in the plain PLA96/4 scaffold. Chondrogenic differentiation was most enhanced in the presence of chitosan. These findings indicate that the plain P scaffold provided a good 3D-matrix for ASC proliferation whereas the addition of chitosan to the PLA96/4 scaffold induced chondrogenic differentiation independent of the medium. Accordingly, a PLA96/4 scaffold modified by chitosan could provide a functional and bioactive basis for tissue-engineered chondral implants. Copyright © 2012 John Wiley & Sons, Ltd.

Porous titanium scaffolds fabricated using a rapid prototyping and powder metallurgy technique.

PubMed

Ryan, Garrett E; Pandit, Abhay S; Apatsidis, Dimitrios P

2008-09-01

One of the main issues in orthopaedic implant design is the fabrication of scaffolds that closely mimic the biomechanical properties of the surrounding bone. This research reports on a multi-stage rapid prototyping technique that was successfully developed to produce porous titanium scaffolds with fully interconnected pore networks and reproducible porosity and pore size. The scaffolds' porous characteristics were governed by a sacrificial wax template, fabricated using a commercial 3D-printer. Powder metallurgy processes were employed to generate the titanium scaffolds by filling around the wax template with titanium slurry. In the attempt to optimise the powder metallurgy technique, variations in slurry concentration, compaction pressure and sintering temperature were investigated. By altering the wax design template, pore sizes ranging from 200 to 400 microm were achieved. Scaffolds with porosities of 66.8 +/- 3.6% revealed compression strengths of 104.4+/-22.5 MPa in the axial direction and 23.5 +/- 9.6 MPa in the transverse direction demonstrating their anisotropic nature. Scaffold topography was characterised using scanning electron microscopy and microcomputed tomography. Three-dimensional reconstruction enabled the main architectural parameters such as pore size, interconnecting porosity, level of anisotropy and level of structural disorder to be determined. The titanium scaffolds were compared to their intended designs, as governed by their sacrificial wax templates. Although discrepancies in architectural parameters existed between the intended and the actual scaffolds, overall the results indicate that the porous titanium scaffolds have the properties to be potentially employed in orthopaedic applications.

Preparation of porous collagen/hyaluronic acid hybrid scaffolds for biomimetic functionalization through biochemical binding affinity.

PubMed

Lee, Su Jin; Kim, So Yeon; Lee, Young Moo

2007-08-01

This study demonstrated the feasibility of introducing an avidin-biotin system to three-dimensional and highly porous scaffolds for the purpose of designing scaffolds that have binding affinity with bioactive molecules for various biomimetic modifications. Porous hybrid scaffolds composed of collagen and hyaluronic acid (HA) were prepared by a novel overrun process. The overrun-processed scaffolds showed a uniform dual-pore structure because of the injection of gas bubbles and ice recrystallization during the fabrication process and had a higher porosity than scaffolds prepared by a conventional freeze-drying method. The mechanical strength and biodegradation kinetics were controlled by the method of preparation and the composition of collagen/HA. Collagen/HA scaffolds did not show any significant adverse effects on cell viability even after 10 days of incubation. The fibroblasts cultured in the overrun-processed scaffolds were widely distributed and had proliferated on the surfaces of the macropores in the scaffolds, whereas the cells that were seeded in the freeze-dried scaffolds had attached mainly on the dense surface of the scaffolds. As the collagen content in the scaffolds increased, the cellular ingrowth into the inner pores of the scaffolds decreased because of the high affinity between the collagen and the cells. Measurements obtained via confocal microscopy revealed that the porous collagen/HA scaffolds could be functionalized with the biotin by incorporating avidin. Therefore, the present biotinylation approach may allow the incorporation of various bioactive molecules (DNA, growth factors, drug, peptide, etc) into the three-dimensional porous scaffolds.

Multiphoton imaging of myogenic differentiation in gelatin-based hydrogels as tissue engineering scaffolds.

PubMed

Kim, Min Jeong; Shin, Yong Cheol; Lee, Jong Ho; Jun, Seung Won; Kim, Chang-Seok; Lee, Yunki; Park, Jong-Chul; Lee, Soo-Hong; Park, Ki Dong; Han, Dong-Wook

2016-01-01

Hydrogels can serve as three-dimensional (3D) scaffolds for cell culture and be readily injected into the body. Recent advances in the image technology for 3D scaffolds like hydrogels have attracted considerable attention to overcome the drawbacks of ordinary imaging technologies such as optical and fluorescence microscopy. Multiphoton microscopy (MPM) is an effective method based on the excitation of two-photons. In the present study, C2C12 myoblasts differentiated in 3D gelatin hydroxyphenylpropionic acid (GHPA) hydrogels were imaged by using a custom-built multiphoton excitation fluorescence microscopy to compare the difference in the imaging capacity between conventional microscopy and MPM. The physicochemical properties of GHPA hydrogels were characterized by using scanning electron microscopy and Fourier-transform infrared spectroscopy. In addition, the cell viability and proliferation of C2C12 myoblasts cultured in the GHPA hydrogels were analyzed by using Live/Dead Cell and CCK-8 assays, respectively. It was found that C2C12 cells were well grown and normally proliferated in the hydrogels. Furthermore, the hydrogels were shown to be suitable to facilitate the myogenic differentiation of C2C12 cells incubated in differentiation media, which had been corroborated by MPM. It was very hard to get clear images from a fluorescence microscope. Our findings suggest that the gelatin-based hydrogels can be beneficially utilized as 3D scaffolds for skeletal muscle engineering and that MPM can be effectively applied to imaging technology for tissue regeneration.

Biodegradable gelatin-chitosan films incorporated with essential oils as antimicrobial agents for fish preservation.

PubMed

Gómez-Estaca, J; López de Lacey, A; López-Caballero, M E; Gómez-Guillén, M C; Montero, P

2010-10-01

Essential oils of clove (Syzygium aromaticum L.), fennel (Foeniculum vulgare Miller), cypress (Cupressus sempervirens L.), lavender (Lavandula angustifolia), thyme (Thymus vulgaris L.), herb-of-the-cross (Verbena officinalis L.), pine (Pinus sylvestris) and rosemary (Rosmarinus officinalis) were tested for their antimicrobial activity on 18 genera of bacteria, which included some important food pathogen and spoilage bacteria. Clove essential oil showed the highest inhibitory effect, followed by rosemary and lavender. In an attempt to evaluate the usefulness of these essential oils as food preservatives, they were also tested on an extract made of fish, where clove and thyme essential oils were the most effective. Then, gelatin-chitosan-based edible films incorporated with clove essential oil were elaborated and their antimicrobial activity tested against six selected microorganisms: Pseudomonas fluorescens, Shewanella putrefaciens, Photobacterium phosphoreum, Listeria innocua, Escherichia coli and Lactobacillus acidophilus. The clove-containing films inhibited all these microorganisms irrespectively of the film matrix or type of microorganism. In a further experiment, when the complex gelatin-chitosan film incorporating clove essential oil was applied to fish during chilled storage, the growth of microorganisms was drastically reduced in gram-negative bacteria, especially enterobacteria, while lactic acid bacteria remained practically constant for much of the storage period. The effect on the microorganisms during this period was in accordance with biochemical indexes of quality, indicating the viability of these films for fish preservation. 2010 Elsevier Ltd. All rights reserved.

Skin derived precursor Schwann cell-generated acellular matrix modified chitosan/silk scaffolds for bridging rat sciatic nerve gap.

PubMed

Zhu, Changlai; Huang, Jing; Xue, Chengbin; Wang, Yaxian; Wang, Shengran; Bao, Shuangxi; Chen, Ruyue; Li, Yuan; Gu, Yun

2017-12-27

Extracellular/acellular matrix has been attracted much research interests for its unique biological characteristics, and ACM modified neural scaffolds shows the remarkable role of promoting peripheral nerve regeneration. In this study, skin-derived precursors pre-differentiated into Schwann cells (SKP-SCs) were used as parent cells to generate acellular(ACM) for constructing a ACM-modified neural scaffold. SKP-SCs were co-cultured with chitosan nerve guidance conduits (NGC) and silk fibroin filamentous fillers, followed by decellularization to stimulate ACM deposition. This NGC-based, SKP-SC-derived ACM-modified neural scaffold was used for bridging a 10 mm long rat sciatic nerve gap. Histological and functional evaluation after grafting demonstrated that regenerative outcomes achieved by this engineered neural scaffold were better than those achieved by a plain chitosan-silk fibroin scaffold, and suggested the benefits of SKP-SC-derived ACM for peripheral nerve repair. Copyright © 2017 Elsevier Ireland Ltd and Japan Neuroscience Society. All rights reserved.

Fabrication of Porous α-TCP/Gellan Gum Scaffold for Bone Tissue Engineering.

PubMed

Wen, Jian; Kim, Ill Yong; Kikuta, Koichi; Ohtsuki, Chikara

2016-03-01

α-tricalcium phosphate (α-TCP, α-Ca3(PO4)2) receives great attention for bone repairing due to its biodegradability and capability of transformation to human bone's main inorganic components, hydroxyapatite (HAp). α-TCP porous scaffold is easily procurable by sintering of the low-temperature polymorph of TCP, β-TCR Still, porous body of α-TCP is too brittle to being handled and shaped, limiting its clinical application as implant materials. To improve mechanical properties of α-TCP porous scaffold, the present study focused on coating of a type of polysaccharides on α-TCP scaffolds. Gellan gum was chosen as the polysaccharide for coating because of its biodegradability as well as the potential acting as substrate for HAp deposition during hydration of α-TCP after exposure to body fluid. After coating of gellan gum on α-TCP scaffolds with porosity of 75 vol%, the compressive strength increased from 0.45 MPa to around 2.00 MPa. Among the coated scaffold, the maximum compressive strength, 3.97 MPa, was obtained on the scaffold with porosity of 63 vol%. Improvement of mechanical properties of α-TCP/gellan gum composites was achieved to show easy handling performance for a bone substitute for tissue repairing. The dissolving rate of the coated scaffolds was also controlled by adjusting the concentration of GG solutions.

Soft chitosan microbeads scaffold for 3D functional neuronal networks.

PubMed

Tedesco, Maria Teresa; Di Lisa, Donatella; Massobrio, Paolo; Colistra, Nicolò; Pesce, Mattia; Catelani, Tiziano; Dellacasa, Elena; Raiteri, Roberto; Martinoia, Sergio; Pastorino, Laura

2018-02-01

The availability of 3D biomimetic in vitro neuronal networks of mammalian neurons represents a pivotal step for the development of brain-on-a-chip experimental models to study neuronal (dys)functions and particularly neuronal connectivity. The use of hydrogel-based scaffolds for 3D cell cultures has been extensively studied in the last years. However, limited work on biomimetic 3D neuronal cultures has been carried out to date. In this respect, here we investigated the use of a widely popular polysaccharide, chitosan (CHI), for the fabrication of a microbead based 3D scaffold to be coupled to primary neuronal cells. CHI microbeads were characterized by optical and atomic force microscopies. The cell/scaffold interaction was deeply characterized by transmission electron microscopy and by immunocytochemistry using confocal microscopy. Finally, a preliminary electrophysiological characterization by micro-electrode arrays was carried out. Copyright © 2017 Elsevier Ltd. All rights reserved.

The role of three-dimensional pure bovine gelatin scaffolds in tendon healing, modeling, and remodeling: an in vivo investigation with potential clinical value.

PubMed

Oryan, Ahmad; Sharifi, Pardis; Moshiri, Ali; Silver, Ian A

2017-09-01

Large tendon defects involving extensive tissue loss present complex clinical problems. Surgical reconstruction of such injuries is normally performed by transplanting autogenous and allogenous soft tissues that are expected to remodel to mimic a normal tendon. However, the use of grafts has always been associated with significant limitations. Tissue engineering employing artificial scaffolds may provide acceptable alternatives. Gelatin is a hydrolyzed form of collagen that is bioactive, biodegradable, and biocompatible. The present study has investigated the suitability of gelatin scaffold for promoting healing of a large tendon-defect model in rabbits. An experimental model of a large tendon defect was produced by partial excision of the Achilles tendon of the left hind leg in adult rabbits. To standardize and stabilize the length of the tendon defect a modified Kessler core suture was anchored in the sectioned tendon ends. The defects were either left untreated or filled with three-dimensional gelatin scaffold. Before euthanasia 60 days after injury, the progress of healing was evaluated clinically. Samples of healing tendon were harvested at autopsy and evaluated by gross, histopathologic, scanning, and transmission electron microscopy, and by biomechanical testing. The treated animals showed superior weight-bearing and physical activity compared with those untreated, while frequency of peritendinous adhesions around the healing site was reduced. The gelatin scaffold itself was totally degraded and replaced by neo-tendon that morphologically had significantly greater numbers, diameters, density, and maturation of collagen fibrils, fibers, and fiber bundles than untreated tendon scar tissue. It also had mechanically higher ultimate load, yield load, stiffness, maximum stress and elastic modulus, when compared to the untreated tendons. Gelatin scaffold may be a valuable option in surgical reconstruction of large tendon defects.

Doppler optical coherence tomography imaging of local fluid flow and shear stress within microporous scaffolds

NASA Astrophysics Data System (ADS)

Jia, Yali; Bagnaninchi, Pierre O.; Yang, Ying; Haj, Alicia El; Hinds, Monica T.; Kirkpatrick, Sean J.; Wang, Ruikang K.

2009-05-01

Establishing a relationship between perfusion rate and fluid shear stress in a 3D cell culture environment is an ongoing and challenging task faced by tissue engineers. We explore Doppler optical coherence tomography (DOCT) as a potential imaging tool for in situ monitoring of local fluid flow profiles inside porous chitosan scaffolds. From the measured fluid flow profiles, the fluid shear stresses are evaluated. We examine the localized fluid flow and shear stress within low- and high-porosity chitosan scaffolds, which are subjected to a constant input flow rate of 0.5 ml.min-1. The DOCT results show that the behavior of the fluid flow and shear stress in micropores is strongly dependent on the micropore interconnectivity, porosity, and size of pores within the scaffold. For low-porosity and high-porosity chitosan scaffolds examined, the measured local fluid flow and shear stress varied from micropore to micropore, with a mean shear stress of 0.49+/-0.3 dyn.cm-2 and 0.38+/-0.2 dyn.cm-2, respectively. In addition, we show that the scaffold's porosity and interconnectivity can be quantified by combining analyses of the 3D structural and flow images obtained from DOCT.

Evaluation of structural and mechanical properties of electrospun nano-micro hybrid of poly hydroxybutyrate-chitosan/silk scaffold for cartilage tissue engineering

PubMed Central

Karbasi, Saeed; Fekrat, Farnoosh; Semnani, Daryoush; Razavi, Shahnaz; Zargar, Elham Naghash

2016-01-01

Background: One of the new methods of scaffold fabrication is a nano-micro hybrid structure in which the properties of the scaffold are improved by introducing nanometer and micrometer structures. This method could be suitable for scaffold designing if some features improve. Materials and Methods: In this study, electrospun nanofibers of 9% weight solution of poly (3-hydroxybutyrate) (P3HB) and a 15% weight of chitosan by trifluoroacetic acid were coated on both the surface of a silk knitted substrate in the optimum condition to improve the mechanical properties of scaffolds for cartilage tissue engineering application. These hybrid nano-micro fibrous scaffolds were characterized by structural and mechanical evaluation methods. Results: Scanning electron microscopy values and porosity analysis showed that average diameter of nanofibers was 584.94 nm in electrospinning part and general porosity was more than 80%. Fourier transform infrared spectroscopy results indicated the presence of all elements without pollution. The tensile test also stated that by electrospinning, as well as adding chitosan, both maximum strength and maximum elongation increased to 187 N and 10 mm. It means that the microfibrous part of scaffold could affect mechanical properties of nano part of the hybrid scaffold, significantly. Conclusions: It could be concluded that P3HB-chitosan/silk hybrid scaffolds can be a good candidate for cartilage tissue engineering. PMID:28028520

Fabrication of three-dimensional collagen scaffold using an inverse mould-leaching process.

PubMed

Ahn, SeungHyun; Lee, SuYeon; Cho, Youngseok; Chun, Wook; Kim, GeunHyung

2011-09-01

Natural biopolymers, such as collagen or chitosan, are considered ideal for biomedical scaffolds. However, low processability of the materials has hindered the fabrication of designed pore structures controlled by various solid freeform-fabrication methods. A new technique to fabricate a biomedical three-dimensional collagen scaffold, supplemented with a sacrificial poly(ethylene oxide) mould is proposed. The fabricated collagen scaffold shows a highly porous surface and a three-dimensional structure with high porosity as well as mechanically stable structure. To show its feasibility for biomedical applications, fibroblasts/keratinocytes were co-cultured on the scaffold, and the cell proliferation and cell migration of the scaffold was more favorable than that obtained with a spongy-type collagen scaffold.

Physical characterization and modeling of chitosan/peg blends for injectable scaffolds.

PubMed

Lima, Daniel B; Almeida, Renata D; Pasquali, Matheus; Borges, Sílvia P; Fook, Marcus L; Lisboa, Hugo M

2018-06-01

Injectable scaffolds find many applications on the biomedical field due to several advantages on preformed scaffolds such as being able to fill any defect can be used in minimal invasion surgeries and are ready to use products. The most critical parameter for an injectable scaffold usage is its injectability, which can be related with rheological properties. Therefore, the objective of the present work was to increase knowledge about the critical parameters influencing injectability of biopolymers used for injectable scaffolds. Rheological and mechanical properties of a biopolymer blend in combination with injectability tests for a given design space controlled by the concentrations of both polymers and temperatures was made. Then those results were modeled to better understand the impact of parameters on injectability. The biopolymer blend chosen was Chitosan physically blended with Poly(ethylene glycol) where variations of both polymer concentrations and molecular weights were tested. Rheological and mechanical properties of all samples were determined, together with the injection force using a compression test at different injection conditions. All solutions were clear and transparent suggesting perfect miscibility. Rheological results were modeled using Ostwald-Waelle law and revealed a shear thinning pseudo-plastic solution at any composition and temperature, being chitosan concentration the most influencing variable. Compression tests results revealed mean injection forces ranging from 9.9 ± 0.06N to 29.9 ± 0.65N and it was possible to accurately estimate those results. Simulations revealed draw speed as the most influencing parameter. Cell viability tests revealed a non-cytotoxic biopolymer blend. Copyright © 2018 Elsevier Ltd. All rights reserved.

Vancomycin incorporated chitosan/gelatin coatings coupled with TiO2-SrHAP surface modified cp-titanium for osteomyelitis treatment.

PubMed

D, Nancy; N, Rajendran

2018-04-15

Commercially pure Titanium (Cp-Ti) was electrophoretically modified using double layer coatings consisting of TiO 2 -SrHAP as the first layer (TH) followed by vancomycin incorporated Chitosan/Gelatin as the second layer (THV). The nano crystalline phase of coated Strontium incorporated hydroxyapatite (Sr-HAP) confirmed through X-ray diffraction studies (XRD). The polyelectrolyte complex formation between chitosan and gelatin, the stability of the drug, the bonding between chitosan and Sr-HAP were confirmed through infra-red spectroscopic studies (IR). The average roughness (R a ) value calculated from atomic force microscopy (AFM) corroborates with the water contact angle data, which clearly confirms the tuning property of the surface in relation to the surface energy and roughness of the coated samples. The total amount of vancomycin encapsulated was calculated to be 11.5 μg. Antibacterial activity was found against both Staphylococcus aureus strains methicillin resistant Staphylococcus aureus (MRSA) and methicillin sensitive Staphylococcus aureus (MRSA) for a drug concentration of 2.74 μg released after 12 h of immersion. The in-vitro cell culture studies showed enhanced cellular activity for THV samples. Thus, THV samples have a dual action at the surface, by resisting the bacterial adhesion and enhancing cellular interaction at the bio-interface, making it a promising candidate to treat osteomyelitis infection. Copyright © 2018. Published by Elsevier B.V.