Sample records for chromizing
-
NASA Astrophysics Data System (ADS)
Meng, T. X.; Guo, Q.; Xi, W.; Ding, W. Q.; Liu, X. Z.; Lin, N. M.; Yu, S. W.; Liu, X. P.
2018-03-01
Double glow plasma surface alloying was applied to prepare chromizing layer in the surface of AISI440B stainless steel. Prior to chromizing, the stainless steel was etched by microwave plasma chemical vapor deposition to change the surface morphology and composition, and then heated for chromizing at 950 °C for 3 h. The cyclical oxidation of steel after chromizing was carried out at 900 °C for 100 h. Scanning electron microscopy, glow discharge optical emission spectrometer and X-ray diffractometer were used to characterize microstructure, composition and phase structure of alloyed and oxidized samples. The results show that the surface was composed of the Cr-rich top layer and Cr23C6, Cr7C3 and {Cr,Fe}7C3 below layer after chromizing. The bonding between the chromizing layer and the substrate after etching treatment was obviously strengthened. AISI440B steel shows a poor oxidation resistance and the weight gain oxidized for 100 h was up to 31.1 mg/cm2. Weight gains for chromizing and etching + chromizing treated samples were 0.67 mg/cm2 and 8 mg/cm2, respectively. Both oxidized surfaces of chromizing and etching + chromizing were composed of Cr2O3, but the oxide scale of etching + chromizing treated samples was more compact than that of samples without etching.
-
NASA Astrophysics Data System (ADS)
Bai, Ching-Yuan; Wen, Tse-Min; Hou, Kung-Hsu; Ger, Ming-Der
The low-temperature pack chromization, a reforming pack cementation process, is employed to modify AISI 1045 steel for the application of bipolar plates in PEMFC. The process is conducted to yield a coating, containing major Cr-carbides and minor Cr-nitrides, on the substrate in view of enhancing the steel's corrosion resistance and lowering interfacial contact resistance between the bipolar plate and gas diffusion layer. Electrical discharge machining and rolling approach are used as the pretreatment to produce an activated surface on the steel before pack chromization process to reduce operating temperatures and increase deposition rates. The rolled-chromized steel shows the lowest corrosion current density, 3 × 10 -8 A cm -2, and the smallest interfacial contact resistance, 5.9 mΩ cm 2, at 140 N cm -2 among all tested steels. This study clearly states the performance of 1045 carbon steel modified by activated and low-temperature pack chromization processes, which possess the potential to be bipolar plates in the application of PEMFC.
-
NASA Astrophysics Data System (ADS)
Hu, Jianjun; Ma, Chaoping; Yang, Xian; Xu, Hongbin; Guo, Ning; Yu, Hongbing
2017-11-01
In this study, induction heating chromizing (IHC) and box-type furnace heating chromizing (BFHC) were conducted on commercial AISI 5140 steels, respectively. Microstructure, microhardness and wear resistance of the chromized samples were characterized. The results show that the IHC samples have thicker Cr coating layer and stronger interface bond due to pre-compressive stress among the packed powders. Three kinds of microstructures including alloyed cementite (AC-layer), fine pearlite zone (FP-zone) and carbon-poor zone (CP-zone) are formed near the interface in the IHC samples. The main reason given for this is that different contents of Cr and C have different effects on pearlite phase and morphology. The IHC sample shows better wear properties due to its stronger interface bonding strength than that of the BFHC sample. The formation mechanism of CP-zone and its influences on microhardness and wear resistance are also discussed.
-
Effects of combined plasma chromizing and shot peening on the fatigue properties of a Ti6Al4V alloy
NASA Astrophysics Data System (ADS)
Yu, Shouming; Liu, Daoxin; Zhang, Xiaohua; Du, Dongxing
2015-10-01
A plasma chromizing treatment was conducted on Ti6Al4V samples by employing the recently developed double glow plasma surface alloying technology. The Cr-alloyed layer consisted of four sub-layers, namely the Cr deposition, Cr2Ti, CrTi4, and Cr-Ti solid-solution layers. The local hardness and moduli were determined via nanoindentation. In addition, the fatigue properties of the samples were evaluated by using a rotating-bending fatigue machine under a given load. The results showed that the hardness or elastic moduli of the adjacent sub-layers differed significantly and the fatigue properties of the Ti6Al4V alloy deteriorated with the plasma chromizing treatment. This deterioration stemmed mainly from cracks initiated at the interfaces between the sub-layers and the microstructural changes of the substrate; these changes were induced by the high temperature used in the plasma chromizing process. However, the fatigue life of the plasma-chromized samples was increased by a shot peening post-treatment. The fatigue life of the samples resulting from this combination of treatments was slightly higher than that of the single-shot-peened Ti6Al4V substrate. In fact, the sample retaining only the Cr-Ti solid-solution layer (that is, the first three sub-layers were removed), when shot-peened, exhibited the highest fatigue life among all the tested samples; this was attributed to that sample having the highest residual compressive stress, the significant work hardening, and the good hardness to toughness balance.
-
High temperature oxidation in boiler environment of chromized steel
NASA Astrophysics Data System (ADS)
Alia, F. F.; Kurniawan, T.; Asmara, Y. P.; Ani, M. H. B.; Nandiyanto, A. B. D.
2017-10-01
The demand for increasing efficiency has led to the development and construction of higher operating temperature power plant. This condition may lead to more severe thickness losses in boiler tubes due to excessive corrosion process. Hence, the research to improve the corrosion resistance of the current operated material is needed so that it can be applied for higher temperature application. In this research, the effect of chromizing process on the oxidation behaviour of T91 steel was investigated under steam condition. In order to deposit chromium, mixture of chromium (Cr) powder as master alloy, halide salt (NH4Cl) powder as activator and alumina (Al2O3) powder as inert filler were inserted into alumina retort together with the steel sample and heated inside furnace at 1050°C for ten hours under argon gas environment. Furthermore, for the oxidation process, steels were exposed at 700°C at different oxidation time (6h-24h) under steam condition. From FESEM/EDX analysis, it was found that oxidation rate of pack cemented steel was lower than the un-packed steel. These results show that Cr from chromizing process was able to become reservoir for the formation of Cr2O3 in high temperature steam oxidation, and its existence can be used for a longer oxidation time.
-
NASA Astrophysics Data System (ADS)
Wang, Qin-Ying; Behnamian, Yashar; Luo, Hong; Wang, Xian-Zong; Leitch, Michael; Zeng, Hongbo; Luo, Jing-Li
2017-10-01
A hash service environment containing H2S and CO2 in oil industry usually causes corrosion of carbon steel. In this study, the chromized coatings with different deposited time were prepared on the surface of carbon steel by the method of pack cementation to enhance its corrosion resistance. Then the microstructure, hardness, corrosion resistance as well as the semiconductor behavior of coatings in the simulated solution with saturated H2S and CO2 were investigated. The results show that the content of Cr in coating was increased by prolonging deposited time, and both chromium carbides and chromium nitrides were formed. Furthermore, coatings display higher polarization resistance, Rp, than that of the substrate, indicating a higher resistance to charge transfer on coating surface. The corrosion rates of coatings with different deposited time were significantly lower than that of substrate. Chemical analysis showed the formation of heavy sulfides on the surface of substrates after corrosion, while the least corrosion products were detected on the surface of coating with deposited time of 12 h. Mott-Schottky results indicated that coating of 12 h displayed less defects than the other two coatings with deposited time of 4 h and 8 h, which will be beneficial to improve corrosion resistance. The investigation showed that chromized coatings exhibited high corrosion resistance and owned a potential application in oil industry for corrosion prevention.
-
NASA Astrophysics Data System (ADS)
Domec, Brennan S.
In today's industry, engineering materials are continuously pushed to the limits. Often, the application only demands high-specification properties in a narrowly-defined region of the material, such as the outermost surface. This, in combination with the economic benefits, makes case hardening an attractive solution to meet industry demands. While case hardening has been in use for decades, applications demanding high hardness, deep case depth, and high corrosion resistance are often under-served by this process. Instead, new solutions are required. The goal of this study is to develop and characterize a new borochromizing process applied to a pre-carburized AISI 8620 alloy steel. The process was successfully developed using a combination of computational simulations, calculations, and experimental testing. Process kinetics were studied by fitting case depth measurement data to Fick's Second Law of Diffusion and an Arrhenius equation. Results indicate that the kinetics of the co-diffusion method are unaffected by the addition of chromium to the powder pack. The results also show that significant structural degradation of the case occurs when chromizing is applied sequentially to an existing boronized case. The amount of degradation is proportional to the chromizing parameters. Microstructural evolution was studied using metallographic methods, simulation and computational calculations, and analytical techniques. While the co-diffusion process failed to enrich the substrate with chromium, significant enrichment is obtained with the sequential diffusion process. The amount of enrichment is directly proportional to the chromizing parameters with higher parameters resulting in more enrichment. The case consists of M7C3 and M23C6 carbides nearest the surface, minor amounts of CrB, and a balance of M2B. Corrosion resistance was measured with salt spray and electrochemical methods. These methods confirm the benefit of surface enrichment by chromium in the sequential diffusion method with corrosion resistance increasing directly with chromium concentration. The results also confirm the deleterious effect of surface-breaking case defects and the need to reduce or eliminate them. The best combination of microstructural integrity, mean surface hardness, effective case depth, and corrosion resistance is obtained in samples sequentially boronized and chromized at 870°C for 6hrs. Additional work is required to further optimize process parameters and case properties.
-
The influence of Cr and Al pack cementation on low carbon steel to improve oxidation resistance
NASA Astrophysics Data System (ADS)
Prasetya, Didik; Sugiarti, Eni; Destyorini, Fredina; Thosin, Kemas Ahmad Zaini
2012-06-01
Pack chromizing and aluminizing has been widely used for many years to improve hot temperature oxidation and corrosion resistance of metals. The coating process involves packing the steel in a powder mixture which contain aluminum and chromium source, and inert filler (usually alumina), and halide activator NH4Cl. Al and Cr were deposited onto carbon steel by pack cementation process using elemental Al and Cr powder as Al and Cr source, whereas NiCo alloys codeposited by electrodeposition. The position of Al and Cr could be under or over Ni-Co alloys deposited. Pack cementation was heated on dry inert gas at temperature 800 °C about 5 hours and 20 minute for Cr and Al respectively. Al and Cr was successfully deposited. Laying down effect of Al and Cr onto carbon steel whether up and down toward NiCo alloys coating have affected to oxidation resistance. The pack aluminizing as top layer given best resitance to restrain excessive oxide scale, in contrast pack chromizing reveal bad oxidation resistance, moreover occured spallation on layer.
-
PLURAL METALLIC COATINGS ON URANIUM AND METHOD OF APPLYING SAME
Gray, A.G.
1958-09-16
A method is described of applying protective coatings to uranlum articles. It consists in applying chromium plating to such uranium articles by electrolysis in a chromic acid bath and subsequently applying, to this minum containing alloy. This aluminum contalning alloy (for example one of aluminum and silicon) may then be used as a bonding alloy between the chromized surface and an aluminum can.
-
Tribological properties of CrN coatings deposited by nitro-chromizing treatment on AISI D2 steel
NASA Astrophysics Data System (ADS)
Durmaz, M.; Kilinc, B.; Abakay, E.; Sen, U.; Sen, S.
2015-03-01
In this work, the wear test of uncoated and chromium nitride coated AISI D2 cold work tool steel against alumina ball realized at 0.1 m/s sliding speeds and under the loads of 2.5N, 5N and 10N. Steel samples were nitrided at 575°C for 8 h in the first step of the coating process, and then chromium nitride coating was performed thermo-reactive deposition technique (TRD) in a powder mixture consisting of ferro-chromium, ammonium chloride and alumina at 1000°C for 2 h. Nitro-chromized samples were characterized by X-Ray diffraction analysis (XRD), scanning electron microscopy (SEM), micro-hardness and ball on disk wear tests. The coating layer formed on the AISI D2 steel was compact and homogeneous. X-ray studies showed that the phase formed in the coated layer is Cr2N. The depth of the layer was 8.15 µm. The average hardness of the layer was 2160±15 HV0.025. For uncoated and chromium nitride materials, wear rate increased with increasing load. The results of friction coefficient and wear rate of the tested materials showed that the CrN coating presents the lowest results.
-
Tribological properties of CrN coatings deposited by nitro-chromizing treatment on AISI D2 steel
DOE Office of Scientific and Technical Information (OSTI.GOV)
Durmaz, M., E-mail: mdurmaz@sakarya.edu.tr; Abakay, E.; Sen, U.
2015-03-30
In this work, the wear test of uncoated and chromium nitride coated AISI D2 cold work tool steel against alumina ball realized at 0.1 m/s sliding speeds and under the loads of 2.5N, 5N and 10N. Steel samples were nitrided at 575°C for 8 h in the first step of the coating process, and then chromium nitride coating was performed thermo-reactive deposition technique (TRD) in a powder mixture consisting of ferro-chromium, ammonium chloride and alumina at 1000°C for 2 h. Nitro-chromized samples were characterized by X-Ray diffraction analysis (XRD), scanning electron microscopy (SEM), micro-hardness and ball on disk wear tests. The coating layermore » formed on the AISI D2 steel was compact and homogeneous. X-ray studies showed that the phase formed in the coated layer is Cr{sub 2}N. The depth of the layer was 8.15 µm. The average hardness of the layer was 2160±15 HV{sub 0.025}. For uncoated and chromium nitride materials, wear rate increased with increasing load. The results of friction coefficient and wear rate of the tested materials showed that the CrN coating presents the lowest results.« less
-
NASA Technical Reports Server (NTRS)
Johnson, J. R.; Young, S. G.
1972-01-01
A cast nickel-base superalloy, NX-188, coated and uncoated, was tested in a high-velocity gas stream for resistance to oxidation and thermal fatigue by cycling between room temperature and 980, 1040, and 1090 C. Contrary to the behavior of more conventional nickel-base alloys, uncoated NX-188 exhibited the greatest weight loss at the lowest test temperature. In general, on the basis of weight change and metallographic observations a coating consisting of vapor-deposited Fe-Cr-Al-Y over a chromized substrate exhibited the best overall performance in resistance to oxidation and thermal fatigue.
-
Diffusion and surface alloying of gradient nanostructured metals
Lu, Ke
2017-01-01
Gradient nanostructures (GNSs) have been optimized in recent years for desired performance. The diffusion behavior in GNS metals is crucial for understanding the diffusion mechanism and relative characteristics of different interfaces that provide fundamental understanding for advancing the traditional surface alloying processes. In this paper, atomic diffusion, reactive diffusion, and surface alloying processes are reviewed for various metals with a preformed GNS surface layer. We emphasize the promoted atomic diffusion and reactive diffusion in the GNS surface layer that are related to a higher interfacial energy state with respect to those in relaxed coarse-grained samples. Accordingly, different surface alloying processes, such as nitriding and chromizing, have been modified significantly, and some diffusion-related properties have been enhanced. Finally, the perspectives on current research in this field are discussed. PMID:28382244
-
Synthesis, Microstructure and Properties of Nickel Aluminide Foams
NASA Technical Reports Server (NTRS)
Dunand, David C.
2003-01-01
Two Ph.D. students were involved in the project: Mr. Christopher Schuh (part-time, graduated in Spring 2001) and Ms. Andrea Hodge (full-time, graduated Summer 2002). One post-doctoral fellow, Dr. Heeman Choe, worked full-time on the project from July to December 2002. A new process to aluminize and chromize nickel foams was created. A kinetic aluminization model was developed. Creep testing was conducted on the foams. A finite-element model and a simplified analytical model for foam creep were produced. Four articles were written: one is published, two are accepted for publication, and one is in preparation. Ms. Hodge spent four months at NASA Glenn Research Center (9-12/2001 and 2-3/2002) under the supervision of Dr. Nathal. She conducted research on NiAl foam fabrication, mechanical testing and numerical modeling. She gave a talk at the ASM annual conference in November 2001 and presented her results at NASA in December 2001.
-
NASA Technical Reports Server (NTRS)
Blankenship, C. P.; Saunders, N. T.
1972-01-01
Manufacturing processes were developed for TD-NiCr providing small sheet (45 x 90 cm), and larger sheet (60 x 150 cm) and foil. The alternate alloy, DS-NiCr, was produced by pack-chromizing Ni-ThO2 sheet. Formability criteria are being established for basic sheet forming processes, which are brake forming, corrugation forming, joggling, dimpling, and beading. Resistance spot welding (fusion and solid state), resistance seam welding, solid state diffusion welding, and brazing are included in the joining programs. Major emphasis is centered on an Al-modified Ni-Cr-ThO2 alloy development. These alloys, containing 3 to 5% Al, form the protective Al2O3 scale. This enhances oxidation resistance under reentry conditions. Both TD-NiCrAl and DS-NiCrAl alloys are included. A tentative composition of Ni-16Cr-3.5Al-2ThO2 was selected based on oxidation resistance and fabricability.
-
Development of fracture mechanics data for two hydrazine APU turbine wheel materials
NASA Technical Reports Server (NTRS)
Curbishley, G.
1975-01-01
The effects of high temperature, high pressure ammonia were measured on the fracture mechanics and fatigue properties of Astroloy and Rene' 41 turbine wheel materials. Also, the influence of protective coatings on these properties was investigated. Specimens of forged bar stock were subjected to LCF and HCF tests at 950 K (1250 F) and 3.4 MN/sq m (500 psig) pressure, in ammonia containing about 1.5 percent H2O. Aluminized samples (Chromizing Company's Al-870) and gold plated test bars were compared with uncoated specimens. Comparison tests were also run in air at 950 K (1250 F), but at ambient pressures. K sub IE and K sub TH were determined on surface flawed specimens in both the air and ammonia in both uncoated and gold plated conditions. Gold plated specimens exhibited better properties than uncoated samples, and aluminized test bars generally had lower properties. The fatigue properties of specimens tested in ammonia were higher than those tested in air, yet the K sub TH values of ammonia tested samples were lower than those tested in air. However, insufficient specimens were tested to develop significant design data.