Electrical conduction and thermoelectric properties of perovskite-type BaBi1-xSbxO3

NASA Astrophysics Data System (ADS)

Yasukawa, Masahiro; Shiga, Yuta; Kono, Toshio

2012-06-01

To elucidate the thermoelectric properties at high temperatures, the electrical conductivity and Seebeck coefficient were measured at temperatures between 423 K and 973 K for perovskite-type ceramics of BaBi1-xSbxO3 solid solutions with x=0.0-0.5. All the ceramics exhibit p-type semiconducting behaviors and electrical conduction is attributed to hopping of small polaronic holes localized on the pentavalent cations. Substitution of Bi with Sb causes the electrical conductivity σ and cell volume to decrease, but the Seebeck coefficient S to increase, suggesting that the Sb atoms are doped as Sb5+ and replace Bi5+, reducing 6s holes conduction from Bi5+(6s0) to Bi3+ (6s2). The thermoelectric power factor S2σ has values of 6×10-8-3×10-5 W m-1 K-2 in the measured temperature range, and is maximized for an Sb-undoped BaBiO3-δ, but decreases upon Sb doping due to the decreased σ values.

A review of anisotropic conductivity models of brain white matter based on diffusion tensor imaging.

PubMed

Wu, Zhanxiong; Liu, Yang; Hong, Ming; Yu, Xiaohui

2018-06-01

The conductivity of brain tissues is not only essential for electromagnetic source estimation (ESI), but also a key reflector of the brain functional changes. Different from the other brain tissues, the conductivity of whiter matter (WM) is highly anisotropic and a tensor is needed to describe it. The traditional electrical property imaging methods, such as electrical impedance tomography (EIT) and magnetic resonance electrical impedance tomography (MREIT), usually fail to image the anisotropic conductivity tensor of WM with high spatial resolution. The diffusion tensor imaging (DTI) is a newly developed technique that can fulfill this purpose. This paper reviews the existing anisotropic conductivity models of WM based on the DTI and discusses their advantages and disadvantages, as well as identifies opportunities for future research on this subject. It is crucial to obtain the linear conversion coefficient between the eigenvalues of anisotropic conductivity tensor and diffusion tensor, since they share the same eigenvectors. We conclude that the electrochemical model is suitable for ESI analysis because the conversion coefficient can be directly obtained from the concentration of ions in extracellular liquid and that the volume fraction model is appropriate to study the influence of WM structural changes on electrical conductivity. Graphical abstract ᅟ.

Electrical and thermal transport through low densified copper doped PbSe for thermoelectric application

DOE Office of Scientific and Technical Information (OSTI.GOV)

Gayner, Chhatrasal; Malik, Iram; Das, Malay K.

2016-05-06

In this paper, Cu doped PbSe is successfully synthesized by solid state reaction. Theinfluence of porosity on thermal and electrical transport in Cu doped PbSe is investigated in this study. Low densified material significantly scatters the electrons as well as phonons through the high number of scattering sites (like pores, cracks, disorder, etc). As a result, the drastic reduction in thermal conductivity and electrical conductivity isnoticed. Additionally, Seebeck coefficient enhances in a low densified materials. Furthermore, Pb{sub 1-x}Cu{sub x}Se (x ∼ 0 to 0.06) has high Seebeck coefficient due to the energy filtering effect and lower charge carrier concentration.

Silicide/Silicon Hetero-Junction Structure for Thermoelectric Applications.

PubMed

Jun, Dongsuk; Kim, Soojung; Choi, Wonchul; Kim, Junsoo; Zyung, Taehyoung; Jang, Moongyu

2015-10-01

We fabricated silicide/silicon hetero-junction structured thermoelectric device by CMOS process for the reduction of thermal conductivity with the scatterings of phonons at silicide/silicon interfaces. Electrical conductivities, Seebeck coefficients, power factors, and temperature differences are evaluated using the steady state analysis method. Platinum silicide/silicon multilayered structure showed an enhanced Seebeck coefficient and power factor characteristics, which was considered for p-leg element. Also, erbium silicide/silicon structure showed an enhanced Seebeck coefficient, which was considered for an n-leg element. Silicide/silicon multilayered structure is promising for thermoelectric applications by reducing thermal conductivity with an enhanced Seebeck coefficient. However, because of the high thermal conductivity of the silicon packing during thermal gradient is not a problem any temperature difference. Therefore, requires more testing and analysis in order to overcome this problem. Thermoelectric generators are devices that based on the Seebeck effect, convert temperature differences into electrical energy. Although thermoelectric phenomena have been used for heating and cooling applications quite extensively, it is only in recent years that interest has increased in energy generation.

Scattering of electromagnetic plane wave from a perfect electric conducting strip placed at interface of topological insulator-chiral medium

NASA Astrophysics Data System (ADS)

Shoukat, Sobia; Naqvi, Qaisar A.

2016-12-01

In this manuscript, scattering from a perfect electric conducting strip located at planar interface of topological insulator (TI)-chiral medium is investigated using the Kobayashi Potential method. Longitudinal components of electric and magnetic vector potential in terms of unknown weighting function are considered. Use of related set of boundary conditions yields two algebraic equations and four dual integral equations (DIEs). Integrand of two DIEs are expanded in terms of the characteristic functions with expansion coefficients which must satisfy, simultaneously, the discontinuous property of the Weber-Schafheitlin integrals, required edge and boundary conditions. The resulting expressions are then combined with algebraic equations to express the weighting function in terms of expansion coefficients, these expansion coefficients are then substituted in remaining DIEs. The projection is applied using the Jacobi polynomials. This treatment yields matrix equation for expansion coefficients which is solved numerically. These unknown expansion coefficients are used to find the scattered field. The far zone scattering width is investigated with respect to different parameters of the geometry, i.e, chirality of chiral medium, angle of incidence, size of the strip. Significant effects of different parameters including TI parameter on the scattering width are noted.

Versatile apparatus for thermoelectric characterization of oxides at high temperatures

NASA Astrophysics Data System (ADS)

Schrade, Matthias; Fjeld, Harald; Norby, Truls; Finstad, Terje G.

2014-10-01

An apparatus for measuring the Seebeck coefficient and electrical conductivity is presented and characterized. The device can be used in a wide temperature range from room temperature to 1050 °C and in all common atmospheres, including oxidizing, reducing, humid, and inert. The apparatus is suitable for samples with different geometries (disk-, bar-shaped), allowing a complete thermoelectric characterization (including thermal conductivity) on a single sample. The Seebeck coefficient α can be measured in both sample directions (in-plane and cross-plane) simultaneously. Electrical conductivity is measured via the van der Pauw method. Perovskite-type CaMnO3 and the misfit cobalt oxide (Ca2CoO3)q(CoO2) are studied to demonstrate the temperature range and to investigate the variation of the electrical properties as a function of the measurement atmosphere.

Versatile apparatus for thermoelectric characterization of oxides at high temperatures.

PubMed

Schrade, Matthias; Fjeld, Harald; Norby, Truls; Finstad, Terje G

2014-10-01

An apparatus for measuring the Seebeck coefficient and electrical conductivity is presented and characterized. The device can be used in a wide temperature range from room temperature to 1050 °C and in all common atmospheres, including oxidizing, reducing, humid, and inert. The apparatus is suitable for samples with different geometries (disk-, bar-shaped), allowing a complete thermoelectric characterization (including thermal conductivity) on a single sample. The Seebeck coefficient α can be measured in both sample directions (in-plane and cross-plane) simultaneously. Electrical conductivity is measured via the van der Pauw method. Perovskite-type CaMnO3 and the misfit cobalt oxide (Ca2CoO3)q(CoO2) are studied to demonstrate the temperature range and to investigate the variation of the electrical properties as a function of the measurement atmosphere.

Temperature correction in conductivity measurements

USGS Publications Warehouse

Smith, Stanford H.

1962-01-01

Electrical conductivity has been widely used in freshwater research but usual methods employed by limnologists for converting measurements to conductance at a given temperature have not given uniformly accurate results. The temperature coefficient used to adjust conductivity of natural waters to a given temperature varies depending on the kinds and concentrations of electrolytes, the temperature at the time of measurement, and the temperature to which measurements are being adjusted. The temperature coefficient was found to differ for various lake and stream waters, and showed seasonal changes. High precision can be obtained only by determining temperature coefficients for each water studied. Mean temperature coefficients are given for various temperature ranges that may be used where less precision is required.

Electrical conductivity of rocks at high pressures and temperatures

NASA Technical Reports Server (NTRS)

Parkhomenko, E. I.; Bondarenko, A. T.

1986-01-01

The results of studies of the electrical conductivity in the most widely distributed types of igneous rocks, at temperatures of up to 1200 C, at atmospheric pressure, and also at temperatures of up to 700 C and at pressures of up to 20,000 kg/sq cm are described. The figures of electrical conductivity, of activaation energy and of the preexponential coefficient are presented and the dependence of these parameters on the petrochemical parameters of the rocks are reviewed. The possible electrical conductivities for the depository, granite and basalt layers of the Earth's crust and of the upper mantle are presented, as well as the electrical conductivity distribution to the depth of 200 to 240 km for different geological structures.

Tuning of the Seebeck Coefficient and the Electrical and Thermal Conductivity of Hybrid Materials Based on Polypyrrole and Bismuth Nanowires.

PubMed

Hnida, Katarzyna E; Pilarczyk, Kacper; Knutelski, Marcin; Marzec, Mateusz; Gajewska, Marta; Kosonowski, Artur; Chlebda, Damian; Lis, Bartłomiej; Przybylski, Marek

2018-04-06

The growing demand for clean energy catalyzes the development of new devices capable of generating electricity from renewable energy resources. One of the possible approaches focuses on the use of thermoelectric materials (TE), which may utilize waste heat, water, and solar thermal energy to generate electrical power. An improvement of the performance of such devices may be achieved through the development of composites made of an organic matrix filled with nanostructured thermoelectric materials working in a synergetic way. The first step towards such designs requires a better understanding of the fundamental interactions between available materials. In this paper, this matter is investigated and the questions regarding the change of electrical and thermal properties of nanocomposites based on low-conductive polypyrrole enriched with bismuth nanowires of well-defined geometry and morphology is answered. It is clearly demonstrated that the electrical conductivity and the Seebeck coefficient may be tuned either simultaneously or separately within particular Bi NWs content ranges, and that both parameters may be increased at the same time. © 2018 Wiley-VCH Verlag GmbH & Co. KGaA, Weinheim.

Variations of thermoelectric performance by electric fields in bilayer MX2 (M = W, Mo; X = S, Se).

PubMed

Wang, Rui-Ning; Dong, Guo-Yi; Wang, Shu-Fang; Fu, Guang-Sheng; Wang, Jiang-Long

2017-02-22

A gate electrode is usually used to controllably tune the carrier concentrations, further modulating the electrical conductivity and the Seebeck coefficient to obtain the optimum thermoelectric figure of merit (ZT) in two-dimensional materials. On the other hand, it is necessary to investigate how an electric field induced by a gate voltage affects the electronic structures, further determining the thermoelectric properties. Therefore, by using density functional calculations in combination with Boltzmann theory, the thermoelectric properties of bilayer MX 2 (M = W, Mo; X = S, Se) with or without a 1 V nm -1 perpendicular electric field are comparatively investigated. First of all, the variations of the electrical conductivity (σ), electron thermal conductivity and Seebeck coefficient (S) with the carrier concentration are studied. Due to the trade-off relationship between S and σ, there is an optimum concentration to obtain the maximum ZT, which increases with the temperature due to the enhancement of the Seebeck coefficient. Moreover, N-type bilayers have larger optimum ZTs than P-type bilayers. In addition, the electric field results in the increase of the Seebeck coefficient in low hole-doped MS 2 bilayers and high hole-doped MSe 2 bilayers, thus leading to similar variations in ZT. The optimum ZTs are reduced from 2.11 × 10 -2 , 3.19 × 10 -2 , 2.47 × 10 -2 , and 2.58 × 10 -2 to 1.57 × 10 -2 , 1.51 × 10 -2 , 2.08 × 10 -2 , and 1.43 × 10 -2 for the hole-doped MoS 2 , MoSe 2 , and WSe 2 bilayers, respectively. For N-type bilayers, the electric field shows a destructive effect, resulting in the obvious reduction of the Seebeck coefficient in the MSe 2 layers and the low electron-doped MS 2 bilayers. In electron-doped bilayers, the optimum ZTs will decrease from 3.03 × 10 -2 , 6.64 × 10 -2 , and 6.69 × 10 -2 to 2.81 × 10 -2 , 3.59 × 10 -2 , and 4.39 × 10 -2 for the MoS 2 , MoSe 2 , and WSe 2 bilayers, respectively.

High-pressure Seebeck coefficients and thermoelectric behaviors of Bi and PbTe measured using a Paris-Edinburgh cell

DOE Office of Scientific and Technical Information (OSTI.GOV)

Baker, Jason; Kumar, Ravhi S.; Park, Changyong

2016-01-01

A new sample cell assembly design for the Paris-Edinburgh type large-volume press for simultaneous measurements of X-ray diffraction, electrical resistance, Seebeck coefficient and relative changes in the thermal conductance at high pressures has been developed. The feasibility of performing in situ measurements of the Seebeck coefficient and thermal measurements is demonstrated by observing well known solid–solid phase transitions of bismuth (Bi) up to 3 GPa and 450 K. A reversible polarity flip has been observed in the Seebeck coefficient across the Bi-I to Bi-II phase boundary. Also, successful Seebeck coefficient measurements have been performed for the classical high-temperature thermoelectric materialmore » PbTe under high pressure and temperature conditions. In addition, the relative change in the thermal conductivity was measured and a relative change in ZT, the dimensionless figure of merit, is described. Furthermore, this new capability enables pressure-induced structural changes to be directly correlated to electrical and thermal properties.« less

High-pressure Seebeck coefficients and thermoelectric behaviors of Bi and PbTe measured using a Paris-Edinburgh cell.

PubMed

Baker, Jason; Kumar, Ravhi; Park, Changyong; Kenney-Benson, Curtis; Cornelius, Andrew; Velisavljevic, Nenad

2016-11-01

A new sample cell assembly design for the Paris-Edinburgh type large-volume press for simultaneous measurements of X-ray diffraction, electrical resistance, Seebeck coefficient and relative changes in the thermal conductance at high pressures has been developed. The feasibility of performing in situ measurements of the Seebeck coefficient and thermal measurements is demonstrated by observing well known solid-solid phase transitions of bismuth (Bi) up to 3 GPa and 450 K. A reversible polarity flip has been observed in the Seebeck coefficient across the Bi-I to Bi-II phase boundary. Also, successful Seebeck coefficient measurements have been performed for the classical high-temperature thermoelectric material PbTe under high pressure and temperature conditions. In addition, the relative change in the thermal conductivity was measured and a relative change in ZT, the dimensionless figure of merit, is described. This new capability enables pressure-induced structural changes to be directly correlated to electrical and thermal properties.

Synthesis and evaluation of lead telluride/bismuth antimony telluride nanocomposites for thermoelectric applications

NASA Astrophysics Data System (ADS)

Ganguly, Shreyashi; Zhou, Chen; Morelli, Donald; Sakamoto, Jeffrey; Uher, Ctirad; Brock, Stephanie L.

2011-12-01

Heterogeneous nanocomposites of p-type bismuth antimony telluride (Bi 2- xSb xTe 3) with lead telluride (PbTe) nanoinclusions have been prepared by an incipient wetness impregnation approach. The Seebeck coefficient, electrical resistivity, thermal conductivity and Hall coefficient were measured from 80 to 380 K in order to investigate the influence of PbTe nanoparticles on the thermoelectric performance of nanocomposites. The Seebeck coefficients and electrical resistivities of nanocomposites decrease with increasing PbTe nanoparticle concentration due to an increased hole concentration. The lattice thermal conductivity decreases with the addition of PbTe nanoparticles but the total thermal conductivity increases due to the increased electronic thermal conductivity. We conclude that the presence of nanosized PbTe in the bulk Bi 2- xSb xTe 3 matrix results in a collateral doping effect, which dominates transport properties. This study underscores the need for immiscible systems to achieve the decreased thermal transport properties possible from nanostructuring without compromising the electronic properties.

Epitaxial Growth, Surface, and Electronic Properties of Unconventional Semiconductors: RE-V/III-V Nanocomposites and Semiconducting Half Heusler Alloys

DTIC Science & Technology

2014-09-01

with approximately 5 × 1018 Si atoms/cm3 to yield a conductive buffer for STM and photoemsission spectroscopy measurements. On some samples a 3 nm ErAs...where S is the Seebeck coefficient, σ is the electrical conductivity , and κ is the thermal conductivity . Here the electronic information is contained... conductivities (κ = κe + κlat). While the electronic component of thermal conductivity κe is inherently tied to electrical conductivity σ via Wiedemann

Thermoelectric properties of p-type perovskite compounds LaCoO3 systems containing the A-site vacancy

NASA Astrophysics Data System (ADS)

Anzai, Mayuka; Kawakami, Hiroshi; Saito, Miwa; Yamamura, Hiroshi

2011-05-01

Thermoelectric properties of Sr-doped LaCoO3 system which includes both La1-xSrxCoO3 and La0.95-xSrxsquare0.05CoO3 containing the A-site vacancy were prepared by solid state reaction. The crystal phases of the samples were investigated by X-ray diffraction method. The electrical conductivity, Seebeck coefficient, and thermal conductivity were investigated, focusing the effect of A-site vacancy. Doping of Sr to LaCoO3 improved the electrical conductivity but decreased the seebeck coefficient and increased the thermal conductivity. A-site vacancy of La0.95-xSrxsquare0.05CoO3 system, in comparison with La1-xSrxCoO3 system, increased electrical conductivity, and decreased lattice thermal conductivity. As a result, it was found that the thermoelectric properties of La0.95-xSrxsquare0.05CoO3 containing the A-site vacancy showed the higher values than those of La1-xSrxCoO3. The introduction of A-site vacancy was effective on the improvement of thermoelectric property.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Takaki, Hirokazu; Kobayashi, Kazuaki; Shimono, Masato

We present the thermoelectric properties of TiN/MgO superlattices employing first-principles calculation techniques. The Seebeck coefficients, the electrical conductances, the thermal conductances, and the figure of merit are investigated employing electrical and thermal transport calculations based on density functional theory combined with the nonequilibrium Green's function and nonequilibrium molecular dynamics simulation methods. The TiN/MgO superlattices with a small lattice mismatch at the interfaces are ideal systems to study the way for an enhancement of thermoelectric properties in artificial nanostructures. We find that the interfacial scattering between the two materials in the metal/insulator superlattices causes the electrical conductance to change rapidly, whichmore » enhances the Seebeck coefficient significantly. We show that the figure of merit for the artificial superlattice nanostructures has a much larger value compared with that of the bulk material and changes drastically with the superlattice configurations at the atomistic level.« less

Ambient temperature thermoelectric performance of thermally evaporated p-type Bi-Sb-Te thin films

NASA Astrophysics Data System (ADS)

Singh, Sukhdeep; Singh, Janpreet; Tripathi, S. K.

2018-04-01

Bismuth antimony telluride (BST) compounds have shown a promising performance in low to medium temperature thermoelectric (TE) conversion. One such composition, Bi1.2Sb0.8Te3, was synthesized by melting elemental entities and thin films of the as-synthesized material were deposited by thermal evaporation. X-Ray Diffraction analysis was conducted to study the crystallographic phases and other structural properties. Electrical conductivity and Seebeck coefficient measurements of as-prepared thin films were conducted in the temperature range from 303-363 K with a view to study ambient temperature application of the synthesized material for power generation in which an increasing trend was observed in the Seebeck coefficient. Electrical conductivity displayed a maximum value of 0.22 × 104 Sm-1 that was comparable to other Bi-Sb-Te compositions whereas power factor had its peak at 323 K. These trends observed in electrical properties indicate that synthesized material can be used for room temperature TE module fabrication.

Hybrid local piezoelectric and conductive functions for high performance airborne sound absorption

NASA Astrophysics Data System (ADS)

Rahimabady, Mojtaba; Statharas, Eleftherios Christos; Yao, Kui; Sharifzadeh Mirshekarloo, Meysam; Chen, Shuting; Tay, Francis Eng Hock

2017-12-01

A concept of hybrid local piezoelectric and electrical conductive functions for improving airborne sound absorption is proposed and demonstrated in composite foam made of porous polar polyvinylidene fluoride (PVDF) mixed with conductive single-walled carbon nanotube (SWCNT). According to our hybrid material function design, the local piezoelectric effect in the PVDF matrix with the polar structure and the electrical resistive loss of SWCNT enhanced sound energy conversion to electrical energy and subsequently to thermal energy, respectively, in addition to the other known sound absorption mechanisms in a porous material. It is found that the overall energy conversion and hence the sound absorption performance are maximized when the concentration of the SWCNT is around the conductivity percolation threshold. For the optimal composition of PVDF/5 wt. % SWCNT, a sound reduction coefficient of larger than 0.58 has been obtained, with a high sound absorption coefficient higher than 50% at 600 Hz, showing their great values for passive noise mitigation even at a low frequency.

Effect of silicide/silicon hetero-junction structure on thermal conductivity and Seebeck coefficient.

PubMed

Choi, Wonchul; Park, Young-Sam; Hyun, Younghoon; Zyung, Taehyoung; Kim, Jaehyeon; Kim, Soojung; Jeon, Hyojin; Shin, Mincheol; Jang, Moongyu

2013-12-01

We fabricated a thermoelectric device with a silicide/silicon laminated hetero-structure by using RF sputtering and rapid thermal annealing. The device was observed to have Ohmic characteristics by I-V measurement. The temperature differences and Seebeck coefficients of the proposed silicide/silicon laminated and bulk structure were measured. The laminated thermoelectric device shows suppression of heat flow from the hot to cold side. This is supported by the theory that the atomic mass difference between silicide and silicon creates a scattering center for phonons. The major impact of our work is that phonon transmission is suppressed at the interface between silicide and silicon without degrading electrical conductivity. The estimated thermal conductivity of the 3-layer laminated device is 126.2 +/- 3.7 W/m. K. Thus, by using the 3-layer laminated structure, thermal conductivity is reduced by around 16% compared to bulk silicon. However, the Seebeck coefficient of the thermoelectric device is degraded compared to that of bulk silicon. It is understood that electrical conductivity is improved by using silicide as a scattering center.

Contactless measurement of electrical conductivity of semiconductor wafers using the reflection of millimeter waves

NASA Astrophysics Data System (ADS)

Ju, Yang; Inoue, Kojiro; Saka, Masumi; Abe, Hiroyuki

2002-11-01

We present a method for quantitative measurement of electrical conductivity of semiconductor wafers in a contactless fashion by using millimeter waves. A focusing sensor was developed to focus a 110 GHz millimeter wave beam on the surface of a silicon wafer. The amplitude and the phase of the reflection coefficient of the millimeter wave signal were measured by which electrical conductivity of the wafer was determined quantitatively, independent of the permittivity and thickness of the wafers. The conductivity obtained by this method agrees well with that measured by the conventional four-point-probe method.

Characterisation of electrical resistance for CMC Materials up to 1200 °C

NASA Astrophysics Data System (ADS)

Stäbler, T.; Böhrk, H.; Voggenreiter, H.

2017-12-01

Damage to thermal protection systems (TPS) during atmospheric re-entry is a severe safety issue, especially when considering re-usability of space transportation systems. There is a need for structural health monitoring systems and non-destructive inspection methods. However, damages are hard to detect. When ceramic matrix composites, in this case carbon fibre reinforced silicon carbide (C/C-SiC), are used as a TPS, the electrical properties of the present semiconductor material can be used for health monitoring, since the resistivity changes with damage, strain and temperature. In this work the electrical resistivity as a function of the material temperature is analysed eliminating effects of thermal electricity and the thermal coefficient of electrical resistance is determined. A sensor network is applied for locally and time resolved monitoring of the 300 mm x 120 mm x 3 mm panel shaped samples. Since the material is used for atmospheric re-entry it needs to be characterised for a wide range of temperatures, in this case as high as 1200 °C. Therefore, experiments in an inductively heated test bench were conducted. Firstly, a reference sample was used with thermocouples for characterising the temperature distribution across the sample surface. Secondly, electrical resistance under heat load was measured, time and spatially resolved. Results will be shown and discussed in terms of resistance dependence on temperature, thermal coefficient of electrical resistance, thermal electricity and electrical path orientation including an analysis on effective conducting cross section. Conversely, the thermal coefficient can also be used to determine the material temperature as a function of electrical resistance.

Nonequilibrium free diffusion in seed leachate

NASA Astrophysics Data System (ADS)

Ortiz G., Luis; Riquelme P., Pablo; Guzmán, R.

2013-11-01

In this work, we use a Schlieren-like Near Field Scattering (SNFS) setup to study nonequilibrium free diffusion behavior of a colloidal solution obtained from seeds leachate. The main objective is to compare the temporal behavior of the diffusion coefficient of seed leachate with an electric conductivity based vigor test. SNFS sizing measurements, based on Mie theory, were carried out to ensure its reliability and sensitivity. Then, we performed a typical nonequilibrium free diffusion experiment of a glycerol-water mixture. In this way, we confirmed that SNFS setup is sensitive to giant concentration fluctuations of nanocolloidal solutions. The results obtained in this stage reproduce properly the data reported elsewhere in literature. Moreover, seed leachate diffuse, in water, in a similar way that glycerol does. In both cases we used the same method (dynamic structure factor) to determine thermo-physical properties. We show that time evolution of diffusion coefficient of Lupinus Albus leachate exhibits three defined regimes as electric conductivity measurements. The results also exhibit a correspondence between the behavior of the diffusion coefficient and electric conductivity values of the two regions in the temporal range studied. Finally, we discuss biological processes involved in germination that could modulate this dependence, and the role played by the electrolytic nature of solutes.

Thermoelectric Figures of Merit of Zn4Sb3 and Zrnisn-based Half-heusler Compounds Influenced by Mev Ion-beam Bombardments

NASA Astrophysics Data System (ADS)

Budak, S.; Guner, S.; Muntele, C. I.; Ila, D.

Semiconducting β-Zn4Sb3 and ZrNiSn-based half-Heusler compound thin films with applications as thermoelectric (TE) materials were prepared using ion beam assisted deposition (IBAD). High-purity solid zinc (Zn) and antimony (Sb) were evaporated by electron beam to grow the β-Zn4Sb3 thin film while high-purity zirconium (Zr) powder and nickel (Ni) tin (Sn) powders were evaporated by electron beam to grow the ZrNiSn-based half-Heusler compound thin film. Rutherford backscattering spectrometry (RBS) was used to analyze the composition of the thin films. The grown thin films were subjected to 5 MeV Si ions bombardment for generation of nanostructures in the films. We measured the thermal conductivity, Seebeck coefficient, and electrical conductivity of these two systems before and after 5 MeV Si ions beam bombardment. The two material systems have been identified as promising TE materials for the application of thermal-to-electrical energy conversion, but the efficiency still limits their applications. The electronic energy deposited due to ionization in the track of MeV ion beam couldcause localized crystallization. The nanostructures produced by MeV ion beam can cause significant change in both the electrical and the thermal conductivity of thin films, thereby improving the efficiency. We used the 3ω-method (3rd harmonic) measurement system to measure the cross-plane thermal conductivity, the van der Pauw measurement system to measure the electrical conductivity, and the Seebeck-coefficient measurement system to measure the cross-plane Seebeck coefficient. The thermoelectric figures of merit of the two material systems were then derived by calculations using the measurement results. The MeV ion-beam bombardment was found to decrease the thermal conductivity of thin films and increase the efficiency of thermal-to-electrical energy conversion.

Thermoelectric Properties of Highly Conductive Poly(3,4-ethylenedioxythiophene) Polystyrene Sulfonate Printed Thin Films.

PubMed

Beretta, Davide; Barker, Alex J; Maqueira-Albo, Isis; Calloni, Alberto; Bussetti, Gianlorenzo; Dell'Erba, Giorgio; Luzio, Alessandro; Duò, Lamberto; Petrozza, Annamaria; Lanzani, Guglielmo; Caironi, Mario

2017-05-31

Organic conductors are being evaluated for potential use in waste heat recovery through lightweight and flexible thermoelectric generators manufactured using cost-effective printing processes. Assessment of the potentiality of organic materials in real devices still requires a deeper understanding of the physics behind their thermoelectric properties, which can pave the way toward further development of the field. This article reports a detailed thermoelectric study of a set of highly conducting inkjet-printed films of commercially available poly(3,4-ethylenedioxythiophene) polystyrene sulfonate formulations characterized by in-plane electrical conductivity, spanning the interval 10-500 S/cm. The power factor is maximized for the formulation showing an intermediate electrical conductivity. The Seebeck coefficient is studied in the framework of Mott's relation, assuming a (semi-)classical definition of the transport function. Ultraviolet photoelectron spectroscopy at the Fermi level clearly indicates that the shape of the density of states alone is not sufficient to explain the observed Seebeck coefficient, suggesting that carrier mobility is important in determining both the electrical conductivity and thermopower. Finally, the cross-plane thermal conductivity is reliably extracted thanks to a scaling approach that can be easily performed using typical pump-probe spectroscopy.

Rigorous theory of graded thermoelectric converters including finite heat transfer coefficients

NASA Astrophysics Data System (ADS)

Gerstenmaier, York Christian; Wachutka, Gerhard

2017-11-01

Maximization of thermoelectric (TE) converter performance with an inhomogeneous material and electric current distribution has been investigated in previous literature neglecting thermal contact resistances to the heat reservoirs. The heat transfer coefficients (HTCs), defined as inverse thermal contact resistances per unit area, are thus infinite, whereas in reality, always parasitic thermal resistances, i.e., finite HTCs, are present. Maximization of the generated electric power and of cooling power in the refrigerator mode with respect to Seebeck coefficients and heat conductivity for a given profile of the material's TE figure of merit Z are mathematically ill-posed problems in the presence of infinite HTCs. As will be shown in this work, a fully self consistent solution is possible for finite HTCs, and in many respects, the results are fundamentally different. A previous theory for 3D devices will be extended to include finite HTCs and is applied to 1D devices. For the heat conductivity profile, an infinite number of solutions exist leading to the same device performance. Cooling power maximization for finite HTCs in 1D will lead to a strongly enhanced corresponding efficiency (coefficient of performance), whereas results with infinite HTCs lead to a non-monotonous temperature profile and coefficient of performance tending to zero for the prescribed heat conductivities. For maximized generated electric power, the corresponding generator efficiency is nearly a constant independent from the finite HTC values. The maximized efficiencies in the generator and cooling mode are equal to the efficiencies for the infinite HTC, provided that the corresponding powers approach zero. These and more findings are condensed in 4 theorems in the conclusions.

Improving the Thermoelectric Properties of Polyaniline by Introducing Poly(3,4-ethylenedioxythiophene)

NASA Astrophysics Data System (ADS)

Wang, Xiao Yang; Liu, Cheng Yan; Miao, Lei; Gao, Jie; Chen, Yu

2016-03-01

By using the parent monomers, 3,4-ethylenedioxythiophene and aniline, a series of nanocomposites consisting of different mass ratios of polyaniline (PANI) to poly(3,4-ethylenedioxythiophene) (PEDOT) have been successfully prepared in hydrochloric acid solution through oxidative polymerization, then redoped with p-toluenesulfonic acid ( p-TSA). Firstly, PEDOT nanoparticles were fabricated via chemical oxidation polymerization in reverse (water-in-oil) microemulsions. Then, PANI-doped PEDOT nanoparticles were formed by oxidative polymerization of aniline to form PANI/PEDOT nanofibers. The resulting nanostructured components were characterized by scanning electron microscopy (SEM) and a series of spectroscopic methods. The presence of PEDOT increased the room-temperature electrical conductivity of the PANI/PEDOT nanocomposites by more than two orders of magnitude in comparison with the parent PANI. Moreover, the PANI/PEDOT nanocomposites showed better thermoelectric properties than PANI. Different concentrations of p-TSA also affected the electrical conductivity and Seebeck coefficient of the nanocomposites. With increasing temperature, both the electrical conductivity and Seebeck coefficient increased.

Study of physical and sound absorbing property of epoxy blended coir dust biocomposite

NASA Astrophysics Data System (ADS)

Nath, G.; Mishra, S. P.

2016-09-01

Reinforcement biocomposite has gained more attention recently due to its low cost, abundantly availability, low density, specific properties, easy method of separation, enhanced energy recovery, CO2 neutrality, biodegradability and recyclable in nature. As a waste product of coconut fruit, the coconut coir dust (CCD) obtained from the coconut husk. The biocomposite material prepared from the CCD modified with the proper blended solution with the help of ultrasonic technique. The study of adiabatic compressibility of acetone / water (70/30) worth its blending property for bleaching of CCD. The biocomposite material of CCD was prepared with epoxy resin. The different physical properties such as sound absorption coefficient, thermal conductivity and electrical conductivity were measured. The morphological study of biocomposite and measurement of sound absorption coefficient shows good evidence of sound absorbing characteristics of biocomposite of CCD. The sound absorption property of composite material shows a significant result where as the thermal conductivity and electrical conductivity executes a weak result. Thus biocomposite of CCD can acts as a good sound absorber and band conductor of heat and electric current.

Electrokinetic coupling in unsaturated porous media.

PubMed

Revil, A; Linde, N; Cerepi, A; Jougnot, D; Matthäi, S; Finsterle, S

2007-09-01

We consider a charged porous material that is saturated by two fluid phases that are immiscible and continuous on the scale of a representative elementary volume. The wetting phase for the grains is water and the nonwetting phase is assumed to be an electrically insulating viscous fluid. We use a volume-averaging approach to derive the linear constitutive equations for the electrical current density as well as the seepage velocities of the wetting and nonwetting phases on the scale of a representative elementary volume. These macroscopic constitutive equations are obtained by volume-averaging Ampère's law together with the Nernst-Planck equation and the Stokes equations. The material properties entering the macroscopic constitutive equations are explicitly described as functions of the saturation of the water phase, the electrical formation factor, and parameters that describe the capillary pressure function, the relative permeability functions, and the variation of electrical conductivity with saturation. New equations are derived for the streaming potential and electro-osmosis coupling coefficients. A primary drainage and imbibition experiment is simulated numerically to demonstrate that the relative streaming potential coupling coefficient depends not only on the water saturation, but also on the material properties of the sample, as well as the saturation history. We also compare the predicted streaming potential coupling coefficients with experimental data from four dolomite core samples. Measurements on these samples include electrical conductivity, capillary pressure, the streaming potential coupling coefficient at various levels of saturation, and the permeability at saturation of the rock samples. We found very good agreement between these experimental data and the model predictions.

Thermoelectric properties of conducting polyaniline/BaTiO3 nanoparticle composite films

NASA Astrophysics Data System (ADS)

Anno, H.; Yamaguchi, K.; Nakabayashi, T.; Kurokawa, H.; Akagi, F.; Hojo, M.; Toshima, N.

2011-05-01

Conducting polyaniline (PANI)/BaTiO3 nanoparticle composite films with different molar ratio values R=1, 5, 10, and 100 have been prepared on a quartz substrate by casting the m-cresol solution of PANI, (±)-10-camphorsulfonic acid (CSA) and BaTiO3 nanoparticle with an average diameter of about 20 nm. The CSA-doped PANI/BaTiO3 composite films were characterized by x-ray diffraction, Fourier transform infrared spectroscopy, and UV-Vis transmission spectroscopy. The Seebeck coefficient and the electrical conductivity of the films with different R values, together with CSA-doped PANI films, were measured in the temperature range from room temperature to ~400 K. The relation between the Seebeck coefficient and the electrical conductivity in the composite films are discussed from a comparison of them with those of CSA-doped PANI films and other PANI composite films.

Electrical Transport Properties of Single-Crystalline β-Zn4Sb3 Prepared Through the Zn-Sn Mixed-Flux Method

NASA Astrophysics Data System (ADS)

Liu, Hongxia; Deng, Shuping; Shen, Lanxian; Wang, Jinsong; Feng, Cheng; Deng, Shukang

2017-03-01

β-Zn4Sb3 is a promising p-type thermoelectric material for utilization in moderate temperatures. This study prepares a group of single-crystalline β-Zn4Sb3 samples using the Zn-Sn mixed-flux method based on the stoichiometric ratios of Zn4+ x Sb3Sn y . The effect of Zn-to-Sn proportion in the flux on the structure and electrical transport properties is investigated. All samples are strip-shaped single crystals of different sizes. The actual Zn content of the present samples is improved (>3.9) compared with that of the samples prepared through the Sn flux method. Larger lattice parameters are also obtained. The carrier concentration of all the samples is in the order of over 1019 cm-3. With increasing Sn rate in the flux, this carrier concentration decreases, whereas mobility is significantly enhanced. The electrical conductivity and Seebeck coefficients of all the samples exhibit a behavior that of a degenerate semiconductor transport. Electrical conductivity initially increases and then decreases as the Sn ratio in the flux increases. The electrical conductivity of the x: y = 5:1 sample reaches 6.45 × 104 S m-1 at 300 K. Benefitting from the electrical conductivity and Seebeck coefficient, the flux proportion of the x: y = 7:1 sample finally achieves the highest power factor value of 1.4 × 10-3 W m-1 K-2 at 598 K.

Tuning Thermoelectric Properties of Type I Clathrate K 8–x Ba x Al 8+x Si 38–x through Barium Substitution

DOE Office of Scientific and Technical Information (OSTI.GOV)

Sui, Fan; Kauzlarich, Susan M.

2016-05-10

The thermal stability and thermoelectric properties of type I clathrate K8Al8Si38 up to 873 K are reported. K8Al8Si38 possesses a high absolute Seebeck coefficient value and high electrical resistivity in the temperature range of 323 to 873 K, which is consistent with previously reported low temperature thermoelectric properties. Samples with Ba partial substitution at the K guest atom sites were synthesized from metal hydride precursors. The samples with the nominal chemical formula of K8–xBaxAl8+xSi38–x (x = 1, 1.5, 2) possess type I clathrate structure (cubic, Pm3n), confirmed by X-ray diffraction. The guest atom site occupancies and thermal motions were investigatedmore » with Rietveld refinement of synchrotron powder X-ray diffraction. Transport properties of Ba-containing samples were characterized from 2 to 300 K. The K–Ba alloy phases showed low thermal conductivity and improved electrical conductivity compared to K8Al8Si38. Electrical resistivity and Seebeck coefficients were measured over the temperature range of 323 to 873 K. Thermal conductivity from 323 to 873 K was estimated from the Wiedemann–Franz relation and lattice thermal conductivity extrapolation from 300 to 873 K. K8–xBaxAl8+xSi38–x (x = 1, 1.5) synthesized with Al deficiency showed enhanced electrical conductivity, and the absolute Seebeck coefficients decrease with the increased carrier concentration. When x = 2, the Al content increases toward the electron balanced composition, and the electrical resistivity increases with the decreasing charge carrier concentration. Overall, K6.5Ba1.5Al9Si37 achieves an enhanced zT of 0.4 at 873 K.« less

Dependence of electrical transport properties of CaO(CaMnO3)m (m = 1, 2, 3, ∞) thermoelectric oxides on lattice periodicity

NASA Astrophysics Data System (ADS)

Baranovskiy, Andrei; Amouyal, Yaron

2017-02-01

The electrical transport properties of CaO(CaMnO3)m (m = 1, 2, 3, ∞) compounds are studied applying the density functional theory (DFT) in terms of band structure at the vicinity of the Fermi level (EF). It is shown that the total density of states (DOS) values at EF increase with increase in the m-values, which implies an increase in the electrical conductivity, σ, with increasing m-values, in full accordance with experimental results. Additionally, the calculated values of the relative slopes of the DOS at EF correlate with the experimentally measured Seebeck coefficients. The electrical conductivity and Seebeck coefficients were calculated in the framework of the Boltzmann transport theory applying the constant relaxation time approximation. By the analysis of experimental and calculated σ(Τ) dependences, the electronic relaxation time and mean free path values were estimated. It is shown that the electrical transport is dominated by electron scattering on the boundaries between perovskite (CaMnO3) and Ca oxide (CaO) layers inside the crystal lattice.

Electrical conductivity of solutions of copper(II) nitrate crystalohydrate in dimethyl sulfoxide

NASA Astrophysics Data System (ADS)

Mamyrbekova, Aigul K.; Mamitova, A. D.; Mamyrbekova, Aizhan K.

2016-06-01

Conductometry is used to investigate the electric conductivity of Cu(NO3)2 ṡ 3H2O solutions in dimethyl sulfoxide in the 0.01-2.82 M range of concentrations and at temperatures of 288-318 K. The limiting molar conductivity of the electrolyte and the mobility of Cu2+ and NO 3 - ions, the effective coefficients of diffusion of copper(II) ions and nitrate ions, and the degree and constant of electrolytic dissociation are calculated for different temperatures from the experimental results. It is established that solutions containing 0.1-0.6 M copper nitrate trihydrate in DMSO having low viscosity and high electrical conductivity can be used in electrochemical deposition.

Heat-transfer tests of aqueous ethylene glycol solutions in an electrically heated tube

NASA Technical Reports Server (NTRS)

Bernardo, Everett; Eian, Carroll S

1945-01-01

As part of an investigation of the cooling characteristics of liquid-cooled engines, tests were conducted with an electrically heated single-tube heat exchanger to determine the heat-transfer characteristics of an-e-2 ethylene glycol and other ethylene glycol-water mixtures. Similar tests were conducted with water and commercial butanol (n-butyl alcohol) for check purposes. The results of tests conducted at an approximately constant liquid-flow rate of 0.67 pound per second (Reynolds number, 14,500 to 112,500) indicate that at an average liquid temperature 200 degrees f, the heat-transfer coefficients obtained using water, nominal (by volume) 30 percent-70 percent and 70 percent-30 percent glycol-water mixtures are approximately 3.8, 2.8, and 1.4 times higher, respectively, than the heat-transfer coefficients obtained using an-e-2 ethylene glycol.

Ba6-3 x Nd8+2 x Ti18O54 Tungsten Bronze: A New High-Temperature n-Type Oxide Thermoelectric

NASA Astrophysics Data System (ADS)

Azough, Feridoon; Freer, Robert; Yeandel, Stephen R.; Baran, Jakub D.; Molinari, Marco; Parker, Stephen C.; Guilmeau, Emmanuel; Kepaptsoglou, Demie; Ramasse, Quentin; Knox, Andy; Gregory, Duncan; Paul, Douglas; Paul, Manosh; Montecucco, Andrea; Siviter, Jonathan; Mullen, Paul; Li, Wenguan; Han, Guang; Man, Elena A.; Baig, Hasan; Mallick, Tapas; Sellami, Nazmi; Min, Gao; Sweet, Tracy

2016-03-01

Semiconducting Ba6-3 x Nd8+2 x Ti18O54 ceramics (with x = 0.00 to 0.85) were synthesized by the mixed oxide route followed by annealing in a reducing atmosphere; their high-temperature thermoelectric properties have been investigated. In conjunction with the experimental observations, atomistic simulations have been performed to investigate the anisotropic behavior of the lattice thermal conductivity. The ceramics show promising n-type thermoelectric properties with relatively high Seebeck coefficient, moderate electrical conductivity, and temperature-stable, low thermal conductivity; For example, the composition with x = 0.27 (i.e., Ba5.19Nd8.54Ti18O54) exhibited a Seebeck coefficient of S 1000K = 210 µV/K, electrical conductivity of σ 1000K = 60 S/cm, and thermal conductivity of k 1000K = 1.45 W/(m K), leading to a ZT value of 0.16 at 1000 K.

Electrical Conductivity of HgTe at High Temperatures

NASA Technical Reports Server (NTRS)

Li, C.; Lehoczky, S. L.; Su, C.-H.; Scripa, R. N.

2004-01-01

The electrical conductivity of HgTe was measured using a rotating magnetic field method from 300 K to the melting point (943 K). A microscopic theory for electrical conduction was used to calculate the expected temperature dependence of the HgTe conductivity. A comparison between the measured and calculated conductivities was used to obtain the estimates of the temperature dependence of Gamma(sub 6)-Gamma(sub 8) energy gap from 300 K to 943 K. The estimated temperature coefficient for the energy gap was comparable to the previous results at lower temperatures (less than or equal to 300 K). A rapid increase in the conductivity just above 300 K and a subsequent decrease at 500 K is attributed to band crossover effects. This paper describes the experimental approach and some of the theoretical calculation details.

Transfer coefficients in ultracold strongly coupled plasma

NASA Astrophysics Data System (ADS)

Bobrov, A. A.; Vorob'ev, V. S.; Zelener, B. V.

2018-03-01

We use both analytical and molecular dynamic methods for electron transfer coefficients in an ultracold plasma when its temperature is small and the coupling parameter characterizing the interaction of electrons and ions exceeds unity. For these conditions, we use the approach of nearest neighbor to determine the average electron (ion) diffusion coefficient and to calculate other electron transfer coefficients (viscosity and electrical and thermal conductivities). Molecular dynamics simulations produce electronic and ionic diffusion coefficients, confirming the reliability of these results. The results compare favorably with experimental and numerical data from earlier studies.

Fiber laser welding of austenitic steel and commercially pure copper butt joint

NASA Astrophysics Data System (ADS)

Kuryntsev, S. V.; Morushkin, A. E.; Gilmutdinov, A. Kh.

2017-03-01

The fiber laser welding of austenitic stainless steel and commercially pure copper in butt joint configuration without filler or intermediate material is presented. In order to melt stainless steel directly and melt copper via heat conduction a defocused laser beam was used with an offset to stainless steel. During mechanical tests the weld seam was more durable than heat affected zone of copper so samples without defects could be obtained. Three process variants of offset of the laser beam were applied. The following tests were conducted: tensile test of weldment, intermediate layer microhardness, optical metallography, study of the chemical composition of the intermediate layer, fractography. Measurements of electrical resistivity coefficients of stainless steel, copper and copper-stainless steel weldment were made, which can be interpreted or recalculated as the thermal conductivity coefficient. It shows that electrical resistivity coefficient of cooper-stainless steel weldment higher than that of stainless steel. The width of intermediate layer between stainless steel and commercially pure copper was 41-53 μm, microhardness was 128-170 HV0.01.

Friction Coefficient Determination by Electrical Resistance Measurements

ERIC Educational Resources Information Center

Tunyagi, A.; Kandrai, K.; Fülöp, Z.; Kapusi, Z.; Simon, A.

2018-01-01

A simple and low-cost, DIY-type, Arduino-driven experiment is presented for the study of friction and measurement of the friction coefficient, using a conductive rubber cord as a force sensor. It is proposed for high-school or college/university-level students. We strongly believe that it is worthwhile planning, designing and performing Arduino…

Measurement of the thermal coefficient of electrical resistivity of a nonmagnetic metal

NASA Astrophysics Data System (ADS)

Lacsný, Boris; Králiková, Petra; Dudáková, Simona; Škorecová, Ivana; Teleki, Aba

2017-05-01

The experiment of a magnet falling through a conductive tube is well-known, and teachers often use it in their classrooms, not only in high schools, but also in undergraduate courses of physics. This article describes the measurement of the thermal coefficient of electrical resistivity of a nonmagnetic metal using this experiment. At room temperature, the experiments designed by the authors are suitable for high schools. For undergraduate courses, we present a set-up with liquid nitrogen to realize the measurement over a wider range of temperatures.

Multiferroic properties of Indian natural ilmenite

NASA Astrophysics Data System (ADS)

Acharya, Truptimayee; Choudhary, R. N. P.

2017-03-01

In this communication, the main results and analysis of extensive studies of electric and magnetic characteristics (relative dielectric constant, tangent loss, electric polarization, electric transport, impedance, magnetic polarization and magneto-electric coupling coefficient) of Indian natural ilmenite (NI) have been presented. Preliminary structural analysis was studied by Rietveld refinement of room temperature XRD data, which suggests the rhombohedral crystal system of NI. Maxwell-Wagner mechanism was used to explain the nature of the frequency dependence of the relative dielectric constant. The impedance analysis reveals that below 270 °C, only the bulk contributes, whereas at higher temperature, both grain boundary and the bulk contribute to the resistive characteristics of the material. The magnitude of the depression angles of the semicircles in the Nyquist plot has been estimated. The correlated barrier hopping model has been used to explain the frequency dependence of ac conductivity of the material. The activation energy of the compound has been estimated using the temperature dependence of dc conductivity plot. The obtained polarization hysteresis loops manifest improper ferroelectric behavior of NI. The existence M-H hysteresis loop supports anti-ferromagnetism in the studied material. The magneto-electric voltage coupling coefficient is found to be 0.7 mV/cm Oe. Hence, other than dielectric constant, electric polarization, magnetization and magneto-electric studies support the existence of multiferroic properties in NI.

Thermoelectric transport properties of BaBiTe{sub 3}-based materials

DOE Office of Scientific and Technical Information (OSTI.GOV)

Zhou, Yiming; Zhao, Li-Dong, E-mail: zhaolidong@buaa.edu.cn

BaBiTe{sub 3}, a material with low thermal conductivity, is an inferior thermoelectric material due to the poor electrical properties originated from its narrow band gap. We choose two types of dopants, K and La, trying to optimize its electrical transport properties. The minority carriers, which harm the Seebeck coefficient in this system, are suppressed by La doping. With the increase of both electrical conductivity and Seebeck coefficient, the power factor of 3% La doped BaBiTe{sub 3} reaches 3.7 μW cm{sup −1} K{sup −2} which increased by 40% from undoped BaBiTe{sub 3}. Besides high power factor, the thermal conductivity is alsomore » reduced in it. Eventually, a high ZT value, 0.25 at 473 K, for n-type BaBiTe{sub 3} is achieved in 3% La doped BaBiTe{sub 3}. - Graphical abstract: BaBiTe{sub 3} possesses a low thermal conductivity. However, it is an inferior thermoelectric material due to the poor electrical properties originated from its narrow band gap. A high ZT value of 0.25 at 473 K for n-type BaBiTe{sub 3} can be achieved through optimizing electrical transport properties via La doping. - Highlights: • BaBiTe{sub 3} is an analogue of these promising thermoelectric materials: such as CsBi{sub 4}Te{sub 6} and K{sub 2}Bi{sub 8}Se{sub 13}, etc. • BaBiTe{sub 3} possesses a low thermal conductivity. • La is an effective dopant to enhance electrical transport properties. • A high ZT value of 0.25 at 473 K can be achieved in n-type La-doped BaBiTe{sub 3}.« less

Electromagnetic interference shielding effectiveness of polypropylene/conducting fiber composites

NASA Astrophysics Data System (ADS)

Lee, Pyoung-Chan; Kim, Bo-Ram; Jeoung, Sun Kyoung; Kim, Yeung Keun

2016-03-01

Electromagnetic released from the automotive electronic parts is harmful to human body. Electromagnetic interference (EMT) shielding refers to the reflection and/or adsorption of electromagnetic radiation by a material, which thereby acts as a shield against the penetration of the radiation through the shield. Polypropylene (PP)/conductive micro fiber composites containing various fiber contents and fiber length were injection-molded. The effect of fiber content and length on electrical properties of the composites was studied by electrical resistivity and EMT shielding measurements. The through-plane electrical conductivity and dielectric permittivity were obtained by measuring dielectric properties. The EMT shielding effectiveness (SE) was investigated by using S-parameter in the range of 100 ~ 1500 MHz. Reflection, absorption and multiple-reflection are the EMT attenuation mechanisms. From the measurement of S-Parameters, the absorption coefficient, reflection coefficient, and the shielding efficiency of the materials were calculated. The EMT SE of PP/conducing fiber composites is 40 dB over a wide frequency range up to 1.5 GHz, which is higher than that of PP/talc composite used automotive parts, viz. 0 dB.

Correlation between electrical conductivity and apparent diffusion coefficient in breast cancer: effect of necrosis on magnetic resonance imaging.

PubMed

Kim, Soo-Yeon; Shin, Jaewook; Kim, Dong-Hyun; Kim, Eun-Kyung; Moon, Hee Jung; Yoon, Jung Hyun; You, Jai Kyung; Kim, Min Jung

2018-03-06

To investigate the correlation between conductivity and ADC in invasive ductal carcinoma according to the presence of necrosis on MRI. Eighty-one women with invasive ductal carcinoma ≥1 cm on T2-weighted fast spin echo sequence of preoperative MRI were included. Phase-based MR electric properties tomography was used to reconstruct conductivity. Mean ADC was measured. Necrosis was defined as an area with very high T2 signal intensity. The relationship between conductivity and ADC was examined using Spearman's correlation coefficient (r). Multiple linear regression analysis was performed to identify factors associated with conductivity or ADC. In the total group, conductivity showed negative correlation with ADC (r = -0.357, p = 0.001). This correlation was maintained in the subgroup without necrosis (n = 53, r = -0.455, p = 0.001), but not in the subgroup with necrosis (n = 28, r = -0.080, p = 0.687). The correlation between the two parameters was different according to necrosis (r = -0.455 vs -0.080, p = 0.047). HER2 enriched subtype was independently associated with conductivity (p = 0.029). Necrosis on MRI was independently associated with ADC (p = 0.027). Conductivity shows negative correlation with ADC that is abolished by the presence of necrosis on MRI. • Electric conductivity showed negative correlation with ADC • However, the correlation was abolished by the presence of necrosis on MRI • HER2-enriched subtype was independently associated with conductivity • Necrosis on MRI was independently associated with ADC.

Determination of consolidation properties using electrical resistivity

NASA Astrophysics Data System (ADS)

Kibria, Golam; Hossain, Sahadat; Khan, Mohammad Sadik

2018-05-01

Electrical conductivity is an indirect method used to evaluate pore-structures and their influence on macro and microscale behavior of soils. Although this method can provide useful information about the consolidation properties of soil samples, insufficient studies have been conducted to identify correlations between electrical and consolidation properties. The current study presents electrical resistivity responses of clayey samples at different consolidation stages. The consolidation properties of four soil specimens were measured in conjunction with electrical conductivity. Scanning electron microscope (SEM) analyses were performed on soil samples before and after consolidation to identify the changes in fabric morphology due to the application of loads. It was observed that the electrical conductivity of samples decreased with the increase of pressure, and the trends of variations were similar to e vs. logP curves. Although a linear correlation exists between electrical conductivity and void ratio, the relationship depends on the structural changes in clay particles. Therefore, changes in fabric structures were analyzed using SEM images, and results showed that the aspect ratio of the particles increased as much as 18.3% after consolidation. Based on the investigation, the coefficient of consolidations and one-dimensional strain were determined using electrical resistivity measurements.

The synthesis of CaZn2Sb2 and its thermoelectric properties

NASA Technical Reports Server (NTRS)

Snyder, J.; Starkll, D.

2002-01-01

CaZn2Sb2 was prepared and examined for use as a hightemperature thermoelectric material. It has a high Seebeck coefficient and high electrical conductivity-comparable to B-Zn4Sb3. These two properties are vital in determining the ability of the compound to change heat into electricity isentropically.

Temperature dependence of electron impact ionization coefficient in bulk silicon

NASA Astrophysics Data System (ADS)

Ahmed, Mowfaq Jalil

2017-09-01

This work exhibits a modified procedure to compute the electron impact ionization coefficient of silicon for temperatures between 77 and 800K and electric fields ranging from 70 to 400 kV/cm. The ionization coefficients are computed from the electron momentum distribution function through solving the Boltzmann transport equation (BTE). The arrangement is acquired by joining Legendre polynomial extension with BTE. The resulting BTE is solved by differences-differential method using MATLAB®. Six (X) equivalent ellipsoidal and non-parabolic valleys of the conduction band of silicon are taken into account. Concerning the scattering mechanisms, the interval acoustic scattering, non-polar optical scattering and II scattering are taken into consideration. This investigation showed that the ionization coefficients decrease with increasing temperature. The overall results are in good agreement with previous experimental and theoretical reported data predominantly at high electric fields.

Lifshitz black branes and DC transport coefficients in massive Einstein-Maxwell-dilaton gravity

NASA Astrophysics Data System (ADS)

Kuang, Xiao-Mei; Papantonopoulos, Eleftherios; Wu, Jian-Pin; Zhou, Zhenhua

2018-03-01

We construct analytical Lifshitz massive black brane solutions in massive Einstein-Maxwell-dilaton gravity theory. We also study the thermodynamics of these black brane solutions and obtain the thermodynamical stability conditions. On the dual nonrelativistic boundary field theory with Lifshitz symmetry, we analytically compute the DC transport coefficients, including the electric conductivity, thermoelectric conductivity, and thermal conductivity. The novel property of our model is that the massive term supports the Lifshitz black brane solutions with z ≠1 in such a way that the DC transport coefficients in the dual field theory are finite. We also find that the Wiedemann-Franz law in this dual boundary field theory is violated, which indicates that it may involve strong interactions.

Enhancing thermoelectric properties of organic composites through hierarchical nanostructures

PubMed Central

Zhang, Kun; Zhang, Yue; Wang, Shiren

2013-01-01

Organic thermoelectric (TE) materials are very attractive due to easy processing, material abundance, and environmentally-benign characteristics, but their potential is significantly restricted by the inferior thermoelectric properties. In this work, noncovalently functionalized graphene with fullerene by π-π stacking in a liquid-liquid interface was integrated into poly(3,4-ethylenedioxythiophene) poly(styrenesulfonate). Graphene helps to improve electrical conductivity while fullerene enhances the Seebeck coefficient and hinders thermal conductivity, resulting in the synergistic effect on enhancing thermoelectric properties. With the integration of nanohybrids, the electrical conductivity increased from ~10000 to ~70000 S/m, the thermal conductivity changed from 0.2 to 2 W·K−1m−1 while the Seebeck coefficient was enhanced by around 4-fold. As a result, nanohybrids-based polymer composites demonstrated the figure of merit (ZT) as high as 6.7 × 10−2, indicating an enhancement of more than one order of magnitude in comparison to single-phase filler-based polymer composites with ZT at the level of 10−3. PMID:24336319

Thermoelectric and phonon transport properties of two-dimensional IV-VI compounds.

PubMed

Shafique, Aamir; Shin, Young-Han

2017-03-30

We explore the thermoelectric and phonon transport properties of two-dimensional monochalcogenides (SnSe, SnS, GeSe, and GeS) using density functional theory combined with Boltzmann transport theory. We studied the electronic structures, Seebeck coefficients, electrical conductivities, lattice thermal conductivities, and figures of merit of these two-dimensional materials, which showed that the thermoelectric performance of monolayer of these compounds is improved in comparison compared to their bulk phases. High figures of merit (ZT) are predicted for SnSe (ZT = 2.63, 2.46), SnS (ZT = 1.75, 1.88), GeSe (ZT = 1.99, 1.73), and GeS (ZT = 1.85, 1.29) at 700 K along armchair and zigzag directions, respectively. Phonon dispersion calculations confirm the dynamical stability of these compounds. The calculated lattice thermal conductivities are low while the electrical conductivities and Seebeck coefficients are high. Thus, the properties of the monolayers show high potential toward thermoelectric applications.

Temperature Coefficients of Electrical Conductivity and Conduction Mechanisms in Butyl Rubber-Carbon Black Composites

NASA Astrophysics Data System (ADS)

Alzamil, M. A.; Alfaramawi, K.; Abboudy, S.; Abulnasr, L.

2018-02-01

Electrical properties of butyl rubber filled with General Purpose Furnace (GPF) carbon black were studied. The carbon black concentration ( X) in the compound was X = 40, 60, 70, 80, and 100 parts by weight per hundred parts by weight of rubber (phr). The corresponding volume fractions of GPF carbon black were 0.447 ± 0.022, 0.548 ± 0.027, 0.586 ± 0.029, 0.618 ± 0.031 and 0.669 ± 0.034, respectively. The concentration dependence of conductivity ( σ ) at constant temperature showed that σ follows a percolation theory; σ ∝ ( {X - Xo } )^{γ } , where X o is the concentration at percolation threshold. The exponent γ was found as 6.6 (at room temperature 30°C). This value agrees with other experimental values obtained by many authors for different rubber-carbon black systems. Electron tunneling between the aggregates, which are dispersed in the insulator rubber, was mainly the conduction process proposed at constant temperature in the butyl-GPF carbon black composites. Temperature dependence of conductivity was investigated in the temperature range from 30°C up to 120°C. All samples exhibit negative temperature coefficients of conductivity (NTCC). The values obtained are - 0.130°C-1, - 0.019°C-1, - 0.0082°C-1, - 0.0094°C-1, and - 0.072°C-1 for carbon black concentrations of 40 phr, 60 phr, 70 phr, 80 phr, and 100 phr, respectively. The samples of concentrations 40 phr and 60 phr have also positive temperature coefficients of conductivity (PTCC) of values + 0.031 and + 0.013, respectively. Electrical conduction at different temperatures showed various mechanisms depending on the carbon black concentration and/or the interval of temperature. The hopping conduction mechanism was noticed at the lower temperature region while carrier thermal activation mechanisms were recorded at the higher temperature range.

Zero temperature coefficient of resistance of the electrical-breakdown path in ultrathin hafnia

NASA Astrophysics Data System (ADS)

Zhang, H. Z.; Ang, D. S.

2017-09-01

The recent widespread attention on the use of the non-volatile resistance switching property of a microscopic oxide region after electrical breakdown for memory applications has prompted basic interest in the conduction properties of the breakdown region. Here, we report an interesting crossover from a negative to a positive temperature dependence of the resistance of a breakdown region in ultrathin hafnia as the applied voltage is increased. As a consequence, a near-zero temperature coefficient of resistance is obtained at the crossover voltage. The behavior may be modeled by (1) a tunneling-limited transport involving two farthest-spaced defects along the conduction path at low voltage and (2) a subsequent transition to a scattering-limited transport after the barrier is overcome by a larger applied voltage.

Thermoelectric Properties of Bi2Te3: CuI and the Effect of Its Doping with Pb Atoms

PubMed Central

Han, Mi-Kyung; Lee, Da-Hee; Kim, Sung-Jin

2017-01-01

In order to understand the effect of Pb-CuI co-doping on the thermoelectric performance of Bi2Te3, n-type Bi2Te3 co-doped with x at % CuI and 1/2x at % Pb (x = 0, 0.01, 0.03, 0.05, 0.07, and 0.10) were prepared via high temperature solid state reaction and consolidated using spark plasma sintering. Electron and thermal transport properties, i.e., electrical conductivity, carrier concentration, Hall mobility, Seebeck coefficient, and thermal conductivity, of CuI-Pb co-doped Bi2Te3 were measured in the temperature range from 300 K to 523 K, and compared to corresponding x% of CuI-doped Bi2Te3 and undoped Bi2Te3. The addition of a small amount of Pb significantly decreased the carrier concentration, which could be attributed to the holes from Pb atoms, thus the CuI-Pb co-doped samples show a lower electrical conductivity and a higher Seebeck coefficient when compared to CuI-doped samples with similar x values. The incorporation of Pb into CuI-doped Bi2Te3 rarely changed the power factor because of the trade-off relationship between the electrical conductivity and the Seebeck coefficient. The total thermal conductivity(κtot) of co-doped samples (κtot ~ 1.4 W/m∙K at 300 K) is slightly lower than that of 1% CuI-doped Bi2Te3 (κtot ~ 1.5 W/m∙K at 300 K) and undoped Bi2Te3 (κtot ~ 1.6 W/m∙K at 300 K) due to the alloy scattering. The 1% CuI-Pb co-doped Bi2Te3 sample shows the highest ZT value of 0.96 at 370 K. All data on electrical and thermal transport properties suggest that the thermoelectric properties of Bi2Te3 and its operating temperature can be controlled by co-doping. PMID:29072613

Thermoelectric Properties of Bi₂Te₃: CuI and the Effect of Its Doping with Pb Atoms.

PubMed

Han, Mi-Kyung; Jin, Yingshi; Lee, Da-Hee; Kim, Sung-Jin

2017-10-26

In order to understand the effect of Pb-CuI co-doping on the thermoelectric performance of Bi₂Te₃, n -type Bi₂Te₃ co-doped with x at % CuI and 1/2 x at % Pb ( x = 0, 0.01, 0.03, 0.05, 0.07, and 0.10) were prepared via high temperature solid state reaction and consolidated using spark plasma sintering. Electron and thermal transport properties, i.e., electrical conductivity, carrier concentration, Hall mobility, Seebeck coefficient, and thermal conductivity, of CuI-Pb co-doped Bi₂Te₃ were measured in the temperature range from 300 K to 523 K, and compared to corresponding x % of CuI-doped Bi₂Te₃ and undoped Bi₂Te₃. The addition of a small amount of Pb significantly decreased the carrier concentration, which could be attributed to the holes from Pb atoms, thus the CuI-Pb co-doped samples show a lower electrical conductivity and a higher Seebeck coefficient when compared to CuI-doped samples with similar x values. The incorporation of Pb into CuI-doped Bi₂Te₃ rarely changed the power factor because of the trade-off relationship between the electrical conductivity and the Seebeck coefficient. The total thermal conductivity(κ tot ) of co-doped samples (κ tot ~ 1.4 W/m∙K at 300 K) is slightly lower than that of 1% CuI-doped Bi₂Te₃ (κ tot ~ 1.5 W/m∙K at 300 K) and undoped Bi₂Te₃ (κ tot ~ 1.6 W/m∙K at 300 K) due to the alloy scattering. The 1% CuI-Pb co-doped Bi₂Te 3 sample shows the highest ZT value of 0.96 at 370 K. All data on electrical and thermal transport properties suggest that the thermoelectric properties of Bi₂Te 3 and its operating temperature can be controlled by co-doping.

Electric currents in E-like planetary ionospheres

NASA Technical Reports Server (NTRS)

Cole, K. D.

1990-01-01

In this paper an MHD approach is used to consider the conduction of electric current in a lightly ionized gas, taking into account the gradients of pressure in the ion and electron gases, in addition to the electric field. The coefficients of electrical conductivity are found for each driver of current. New expressions for the components of heat dissipation associated with each driver of current are developed, which are fully consistent with kinetic theory. The relationship of the results to those obtained by kinetic theory is discussed. New components of currents associated with planetary equatorial electrojets are found. A new diffusion equation for magnetic induction is found, applicable in E-like regions of planetary ionospheres, and stellar photospheres.

Chiral electric separation effect in the quark-gluon plasma

DOE PAGES

Jiang, Yin; Liao, Jinfeng; Huang, Xu-Guang

2015-02-02

In this paper we introduce and compute a new transport coefficient for the quark-gluon plasma (QGP) at very high temperature. This new coefficient σ χe, the CESE (Chiral Electric Separation Effect) conductivity, quantifies the amount of axial current J A that is generated in response to an externally applied electric field eE: J A=σ χe(eE). Starting with a rather general argument in the kinetic theory framework, we show how a characteristic structure σ χe∝μμ5 emerges, which also indicates the CESE as an anomalous transport effect occurring only in a parity-odd environment with nonzero axial charge density μ5 ≠ 0. Usingmore » the Hard-Thermal-Loop framework, the CESE conductivity for the QGP is found to be σ χe = (#)TT rfQ eQ A/g⁴ln(1/g) μμ5/T² to the leading-log accuracy with the numerical constant (#) depending on favor content, e.g., (#)=14.5163 for u, d light flavors.« less

Properties of air-aluminum thermal plasmas

NASA Astrophysics Data System (ADS)

Cressault, Y.; Gleizes, A.; Riquel, G.

2012-07-01

We present the calculation and the main results of the properties of air-aluminum thermal plasmas, useful for complete modelling of arc systems involving aluminum contacts. The properties are calculated assuming thermal equilibrium and correspond to the equilibrium composition, thermodynamic functions, transport coefficients including diffusion coefficients and net emission coefficient representing the divergence of the radiative flux in the hottest plasma regions. The calculation is developed in the temperature range between 2000 and 30 000 K, for a pressure range from 0.1 to 1 bar and for several metal mass proportions. As in the case of other metals, the presence of aluminum vapours has a strong influence on three properties at intermediate temperatures: the electron number density, the electrical conductivity and the net emission coefficient. Some comparisons with other metal vapour (Cu, Fe and Ag) properties are made and show the original behaviour for Al-containing mixtures: mass density at high temperatures is low due to the low Al atomic mass; high electrical conductivity at T < 10 000 K due to low ionization potential (around 2 V less for Al than for the other metals); very strong self-absorption of ionized aluminum lines, leading to a net emission coefficient lower than that of pure air when T > 10 000 K, in contrast to copper or iron radiation.

Thermoelectric Properties of High-Doped Silicon from Room Temperature to 900 K

NASA Astrophysics Data System (ADS)

Stranz, A.; Kähler, J.; Waag, A.; Peiner, E.

2013-07-01

Silicon is investigated as a low-cost, Earth-abundant thermoelectric material for high-temperature applications up to 900 K. For the calculation of module design the Seebeck coefficient and the electrical as well as thermal properties of silicon in the high-temperature range are of great importance. In this study, we evaluate the thermoelectric properties of low-, medium-, and high-doped silicon from room temperature to 900 K. In so doing, the Seebeck coefficient, the electrical and thermal conductivities, as well as the resulting figure of merit ZT of silicon are determined.

Electronic and thermal transport study of sinusoidally corrugated nanowires aiming to improve thermoelectric efficiency.

PubMed

Park, K H; Martin, P N; Ravaioli, U

2016-01-22

Improvement of thermoelectric efficiency has been very challenging in the solid-state industry due to the interplay among transport coefficients which measure the efficiency. In this work, we modulate the geometry of nanowires to interrupt thermal transport with causing only a minimal impact on electronic transport properties, thereby maximizing the thermoelectric power generation. As it is essential to scrutinize comprehensively both electronic and thermal transport behaviors for nano-scale thermoelectric devices, we investigate the Seebeck coefficient, the electrical conductance, and the thermal conductivity of sinusoidally corrugated silicon nanowires and eventually look into an enhancement of the thermoelectric figure-of-merit [Formula: see text] from the modulated nanowires over typical straight nanowires. A loss in the electronic transport coefficient is calculated with the recursive Green function along with the Landauer formalism, and the thermal transport is simulated with the molecular dynamics. In contrast to a small influence on the thermopower and the electrical conductance of the geometry-modulated nanowires, a large reduction of the thermal conductivity yields an enhancement of the efficiency by 10% to 35% from the typical nanowires. We find that this approach can be easily extended to various structures and materials as we consider the geometrical modulation as a sole source of perturbation to the system.

Electrical properties of aluminum-doped zinc oxide (AZO) nanoparticles synthesized by chemical vapor synthesis.

PubMed

Hartner, Sonja; Ali, Moazzam; Schulz, Christof; Winterer, Markus; Wiggers, Hartmut

2009-11-04

Aluminum-doped zinc oxide nanoparticles have been prepared by chemical vapor synthesis, which facilitates the incorporation of a higher percentage of dopant atoms, far above the thermodynamic solubility limit of aluminum. The electrical properties of aluminum-doped and undoped zinc oxide nanoparticles were investigated by impedance spectroscopy. The impedance is measured under hydrogen and synthetic air between 323 and 673 K. The measurements under hydrogen as well as under synthetic air show transport properties depending on temperature and doping level. Under hydrogen atmosphere, a decreasing conductivity with increasing dopant content is observed, which can be explained by enhanced scattering processes due to an increasing disorder in the nanocrystalline material. The temperature coefficient for the doped samples switches from positive temperature coefficient behavior to negative temperature coefficient behavior with increasing dopant concentration. In the presence of synthetic air, the conductivity firstly increases with increasing dopant content by six orders of magnitude. The origin of the increasing conductivity is the generation of free charge carriers upon dopant incorporation. It reaches its maximum at a concentration of 7.7% of aluminum, and drops for higher doping levels. In all cases, the conductivity under hydrogen is higher than under synthetic air and can be changed reversibly by changing the atmosphere.

Thermoelectric Properties in the TiO2/SnO2 System

NASA Technical Reports Server (NTRS)

Dynys, F.; Sayir, A.; Sehirlioglu, A.; Berger, M.

2009-01-01

Nanotechnology has provided a new interest in thermoelectric technology. A thermodynamically driven process is one approach in achieving nanostructures in bulk materials. TiO2/SnO2 system exhibits a large spinodal region with exceptional stable phase separated microstructures up to 1400 C. Fabricated TiO2/SnO2 nanocomposites exhibit n-type behavior with Seebeck coefficients greater than -300 .V/K. Composites exhibit good thermal conductance in the range of 7 to 1 W/mK. Dopant additions have not achieved high electrical conductivity (<1000 S/m). Formation of oxygen deficient composites, TixSn1-xO2-y, can change the electrical conductivity by four orders of magnitude. Achieving higher thermoelectric ZT by oxygen deficiency is being explored. Seebeck coeffcient, thermal conductivity, electrical conductance and microstructure will be discussed in relation to composition and doping.

Electrical and thermal transport properties of layered Bi{sub 2}YO{sub 4}Cu{sub 2}Se{sub 2}

DOE Office of Scientific and Technical Information (OSTI.GOV)

Xiao, Yu; Pei, Yanling; Chang, Cheng

Bi{sub 2}YO{sub 4}Cu{sub 2}Se{sub 2} possesses a low thermal conductivity and high electrical conductivity at room temperature, which was considered as a potential thermoelectric material. In this work, we have investigated the electrical and thermal transport properties of Bi{sub 2}YO{sub 4}Cu{sub 2}Se{sub 2} system in the temperature range from 300 K to 873 K. We found that the total thermal conductivity decreases from ~1.8 W m{sup −1} K{sup −1} to ~0.9 W m{sup −1} K{sup −1}, and the electrical conductivity decreases from ~850 S/cm to ~163 S/cm in the measured temperature range. To investigate how potential of Bi{sub 2}YO{sub 4}Cu{submore » 2}Se{sub 2} system, we prepared the heavily Iodine doped samples to counter-dope intrinsically high carrier concentration and improve the electrical transport properties. Interestingly, the Seebeck coefficient could be enhanced to ~+80 μV/K at 873 K, meanwhile, we found that a low thermal conductivity of ~0.7 W m{sup −1} K{sup −1} could be achieved. The intrinsically low thermal conductivity in this system is related to the low elastic properties, such as Young's modulus of 70–72 GPa, and Grüneisen parameters of 1.55–1.71. The low thermal conductivity makes Bi{sub 2}YO{sub 4}Cu{sub 2}Se{sub 2} system to be a potential thermoelectric material, the ZT value ~0.06 at 873 K was obtained, a higher performance is expected by optimizing electrical transport properties through selecting suitable dopants, modifying band structures or by further reducing thermal conductivity through nanostructuring etc. - Highlights: • The total thermal conductivity decreases from 1.8 to 0.9 Wm{sup –1}K{sup –1} at 300–873K. • The electrical conductivity decreased from 850 to 163 S/cm at 300–873K. • The Seebeck coefficients were enhanced through heavily Iodine doping. • The ZT ~0.06 at 873K suggests that Bi{sub 2}YO{sub 4}Cu{sub 2}Se{sub 2} systems are potential thermoelectrical materials.« less

Thermoelectric Properties of Cu-doped Bi0.4Sb1.6Te3 Prepared by Hot Extrusion

NASA Astrophysics Data System (ADS)

Jung, Woo-Jin; Kim, Il-Ho

2018-06-01

Cu0.003Bi0.4Sb1.6Te3 alloys were prepared by using encapsulated melting and hot extrusion (HE). The hot-extruded specimens had the relative average density of 98%. The ( 00l) planes were preferentially oriented parallel to the extrusion direction, but the specimens showed low crystallographic anisotropy with low orientation factors. The specimens were hot-extruded at 698 K, and they showed excellent mechanical properties with a Vickers hardness of 76 Hv and a bending strength of 59 MPa. However, as the HE temperature increased, the mechanical properties degraded due to grain growth. The hot-extruded specimens showed positive Seebeck coefficients, indicating that the specimens have p-type conduction. These specimens exhibited negative temperature dependences of electrical conductivity, and thus behaved as degenerate semiconductors. The Seebeck coefficient reached the maximum value at 373 K and then decreased with increasing temperature due to intrinsic conduction. Cu-doped specimens exhibited high power factors due to relatively higher electrical conductivities and Seebeck coefficients than those of undoped specimens. A thermal conductivity of 1.00 Wm-1 K-1 was obtained at 373 K for Cu0.003Bi0.4Sb1.6Te3 hot-extruded at 723 K. A maximum dimensionless figure of merit, ZT max = 1.05, and an average dimensionless figure of merit, ZT ave = 0.98, were achieved at 373 K.

Assessment of critical path analyses of the relationship between permeability and electrical conductivity of pore networks

USDA-ARS?s Scientific Manuscript database

Critical path analysis (CPA) is a method for estimating macroscopic transport coefficients of heterogeneous materials that are highly disordered at the micro-scale. Developed originally to model conduction in semiconductors, numerous researchers have noted that CPA might also have relevance to flow ...

Assessing the temporal stability of spatial patterns of soil apparent electrical conductivity using geophysical methods

NASA Astrophysics Data System (ADS)

De Caires, Sunshine A.; Wuddivira, Mark N.; Bekele, Isaac

2014-10-01

Cocoa remains in the same field for decades, resulting in plantations dominated with aging trees growing on variable and depleted soils. We determined the spatio-temporal variability of key soil properties in a (5.81 ha) field from the International Cocoa Genebank, Trinidad using geophysical methods. Multi-year (2008-2009) measurements of apparent electrical conductivity at 0-0.75 m (shallow) and 0.75-1.5 m (deep) were conducted. Apparent electrical conductivity at deep and shallow gave the strongest linear correlation with clay-silt content (R = 0.67 and R = 0.78, respectively) and soil solution electrical conductivity (R = 0.76 and R = 0.60, respectively). Spearman rank correlation coefficients ranged between 0.89-0.97 and 0.81- 0.95 for apparent electrical conductivity at deep and shallow, respectively, signifying a strong linear dependence between measurement days. Thus, in the humid tropics, cocoa fields with thick organic litter layer and relatively dense understory cover, experience minimal fluctuations in transient properties of soil water and temperature at the topsoil resulting in similarly stable apparent electrical conductivity at shallow and deep. Therefore, apparent electrical conductivity at shallow, which covers the depth where cocoa feeder roots concentrate, can be used as a fertility indicator and to develop soil zones for efficient application of inputs and management of cocoa fields.

Optimizing Thermoelectric Properties of In Situ Plasma-Spray-Synthesized Sub-stoichiometric TiO2-x Deposits

NASA Astrophysics Data System (ADS)

Lee, Hwasoo; Seshadri, Ramachandran Chidambaram; Pala, Zdenek; Sampath, Sanjay

2018-06-01

In this article, an attempt has been made to relate the thermoelectric properties of thermal spray deposits of sub-stoichiometric titania to process-induced phase and microstructural variances. The TiO2-x deposits were formed through the in situ reaction of the TiO1.9 or TiO1.7 feedstock within the high-temperature plasma flame and manipulated via varying the amounts of hydrogen fed into in the thermal plasma. Changes in the flow rates of H2 in the plasma plume greatly affected the in-flight particle behavior and composition of the deposits. For reference, a high-velocity oxy-fuel spray torch was also used to deposit the two varieties of feedstocks. Refinements to the representation of the in-flight particle characteristics derived via single particle and ensemble diagnostic methods are proposed using the group parameters (melting index and kinetic energy). The results show that depending on the value of the melting index, there is an inverse proportional relationship between electrical conductivity and Seebeck coefficient, whereas thermal conductivity has a directly proportional relationship with the electrical conductivity. Retention of the original phase and reduced decomposition is beneficial to retain the high Seebeck coefficient or the high electrical conductivity in the TiO2 system.

Electric Motor Thermal Management R&D. Annual Report

DOE Office of Scientific and Technical Information (OSTI.GOV)

Bennion, Kevin

With the push to reduce component volumes, lower costs, and reduce weight without sacrificing performance or reliability, the challenges associated with thermal management increase for power electronics and electric motors. Thermal management for electric motors will become more important as the automotive industry continues the transition to more electrically dominant vehicle propulsion systems. The transition to more electrically dominant propulsion systems leads to higher-power duty cycles for electric drive systems. Thermal constraints place significant limitations on how electric motors ultimately perform, and as thermal management improves, there will be a direct trade-off between motor performance, efficiency, cost, and the sizingmore » of electric motors to operate within the thermal constraints. The goal of this research project is to support broad industry demand for data, analysis methods, and experimental techniques to improve and better understand motor thermal management. Work in FY15 focused on two areas related to motor thermal management: passive thermal performance and active convective cooling. Passive thermal performance emphasized the thermal impact of materials and thermal interfaces among materials within an assembled motor. The research tasks supported the publication of test methods and data for thermal contact resistances and direction-dependent thermal conductivity within an electric motor. Active convective cooling focused on measuring convective heat-transfer coefficients using automatic transmission fluid (ATF). Data for average convective heat transfer coefficients for direct impingement of ATF jets was published. Also, experimental hardware for mapping local-scale and stator-scale convective heat transfer coefficients for ATF jet impingement were developed.« less

Thermoelectric Properties of Bi Doped Tetrahedrite

NASA Astrophysics Data System (ADS)

Prem Kumar, D. S.; Chetty, R.; Femi, O. E.; Chattopadhyay, K.; Malar, P.; Mallik, R. C.

2017-05-01

Bi doped tetrahedrites with nominal compositions of Cu12Sb4- x Bi x S13 ( x = 0, 0.2, 0.4, 0.6, 0.8) were synthesized by the solid state reaction method. Powder x-ray diffraction patterns confirmed that Cu12Sb4S13 (tetrahedrite structure) was the main phase, along with Cu3SbS4 and Cu3SbS3 as the secondary phases. Electron probe microanalysis provided the elemental composition of all the samples. It was confirmed that the main phase is the tetrahedrite phase with slight deviations in the stoichiometry. All the transport properties were measured between 423 K and 673 K. The electrical resistivity increased with an increase in Bi content for all the samples, possibly induced by the variation in the carrier concentration, which may be due to the influence of impurity phases. The increase in electrical resistivity with an increase in temperature indicates the degenerate semiconducting nature of the samples. The absolute Seebeck coefficient is positive throughout the temperature range indicating the p-type nature of the samples. The Seebeck coefficient for all the samples increased with an increase in Bi content as electrical resistivity. The variation of electrical resistivity and the Seebeck coefficient with doping can be attributed to the changes in the carrier concentration of the samples. The total thermal conductivity increases with an increase in temperature and decreases with an increase in the Bi content that could be due to the reduction in carrier thermal conductivity. The highest thermoelectric figure of merit ( zT) 0.84 at 673 K was obtained for the sample with x = 0.2 due to lower thermal conductivity (1.17 W/m K).

Electromagnetic interference shielding effectiveness of polypropylene/conducting fiber composites

DOE Office of Scientific and Technical Information (OSTI.GOV)

Lee, Pyoung-Chan, E-mail: pclee@katech.re.kr; Kim, Bo-Ram; Jeoung, Sun Kyoung

Electromagnetic released from the automotive electronic parts is harmful to human body. Electromagnetic interference (EMT) shielding refers to the reflection and/or adsorption of electromagnetic radiation by a material, which thereby acts as a shield against the penetration of the radiation through the shield. Polypropylene (PP)/conductive micro fiber composites containing various fiber contents and fiber length were injection-molded. The effect of fiber content and length on electrical properties of the composites was studied by electrical resistivity and EMT shielding measurements. The through-plane electrical conductivity and dielectric permittivity were obtained by measuring dielectric properties. The EMT shielding effectiveness (SE) was investigated bymore » using S-parameter in the range of 100 ~ 1500 MHz. Reflection, absorption and multiple-reflection are the EMT attenuation mechanisms. From the measurement of S-Parameters, the absorption coefficient, reflection coefficient, and the shielding efficiency of the materials were calculated. The EMT SE of PP/conducing fiber composites is 40 dB over a wide frequency range up to 1.5 GHz, which is higher than that of PP/talc composite used automotive parts, viz. 0 dB.« less

Ceramics

NASA Astrophysics Data System (ADS)

Zhang, Bo; Chang, Aimin; Zhao, Qing; Ye, Haitao; Wu, Yiquan

2014-11-01

The microstructure and thermoelectric properties of Yb-doped Ca0.9- x Yb x La0.1 MnO3 (0 ≤ x ≤ 0.05) ceramics prepared by using the Pechini method derived powders have been investigated. X-ray diffraction analysis has shown that all samples exhibit single phase with orthorhombic perovskite structure. All ceramic samples possess high relative densities, ranging from 97.04% to 98.65%. The Seebeck coefficient is negative, indicating n-type conduction in all samples. The substitution of Yb for Ca leads to a marked decrease in the electrical resistivity, along with a moderate decrease in the absolute value of the Seebeck coefficient. The highest power factor is obtained for the sample with x = 0.05. The electrical conduction in these compounds is due to electrons hopping between Mn3+ and Mn4+, which is enhanced by increasing Yb content.

Electronic transport coefficients from ab initio simulations and application to dense liquid hydrogen

DOE Office of Scientific and Technical Information (OSTI.GOV)

Holst, Bastian; French, Martin; Redmer, Ronald

2011-06-15

Using Kubo's linear response theory, we derive expressions for the frequency-dependent electrical conductivity (Kubo-Greenwood formula), thermopower, and thermal conductivity in a strongly correlated electron system. These are evaluated within ab initio molecular dynamics simulations in order to study the thermoelectric transport coefficients in dense liquid hydrogen, especially near the nonmetal-to-metal transition region. We also observe significant deviations from the widely used Wiedemann-Franz law, which is strictly valid only for degenerate systems, and give an estimate for its valid scope of application toward lower densities.

System to Measure Thermal Conductivity and Seebeck Coefficient for Thermoelectrics

NASA Technical Reports Server (NTRS)

Kim, Hyun-Jung; Skuza, Jonathan R.; Park, Yeonjoon; King, Glen C.; Choi, Sang H.; Nagavalli, Anita

2012-01-01

The Seebeck coefficient, when combined with thermal and electrical conductivity, is an essential property measurement for evaluating the potential performance of novel thermoelectric materials. However, there is some question as to which measurement technique(s) provides the most accurate determination of the Seebeck coefficient at elevated temperatures. This has led to the implementation of nonstandardized practices that have further complicated the confirmation of reported high ZT materials. The major objective of the procedure described is for the simultaneous measurement of the Seebeck coefficient and thermal diffusivity within a given temperature range. These thermoelectric measurements must be precise, accurate, and reproducible to ensure meaningful interlaboratory comparison of data. The custom-built thermal characterization system described in this NASA-TM is specifically designed to measure the inplane thermal diffusivity, and the Seebeck coefficient for materials in the ranging from 73 K through 373 K.

Electrical properties of Pb{sub 1-x}Mn{sub x}Te single crystals with an excess of tellurium

DOE Office of Scientific and Technical Information (OSTI.GOV)

Bagieva, G. Z., E-mail: bagieva-gjulandam@rambler.ru; Abdinova, G. D.; Mustafayev, N. B.

2013-03-15

The effect of excess Te atoms (as high as 0.5 at %) and thermal treatment at 473 K for 120 h on the electrical conductivity {sigma}, the thermopower coefficient {alpha}, and the Hall coefficient R of Pb{sub 0.96}Mn{sub 0.04}Te single crystals in the temperature range {approx}77-300 K is investigated. It is shown that excess atoms of tellurium predominantly act as acceptor impurity centers at low concentrations in unannealed samples and form antisite defects at relatively high concentrations (0.05 at % or higher) being located mainly in vacancies of the lead sublattice, and decrease the hole concentration. As a result ofmore » annealing, certain lattice defects (for example, deformational) are healed, and the accommodation process for Te atoms at lead-sublattice vacancies is intensified. These processes substantially affect the values of the electrical parameters, their temperature dependences, as well as the sign of the thermopower and Hall coefficients of the samples.« less

Exploring Charge Transport in Guest Molecule Infiltrated Cu 3(BTC) 2 Metal Organic Framework

DOE Office of Scientific and Technical Information (OSTI.GOV)

Leonard, Francois Leonard; Stavila, Vitalie; Allendorf, Mark D.

2014-09-01

The goal of this Exploratory Express project was to expand the understanding of the physical properties of our recently discovered class of materials consisting of metal-organic frameworks with electroactive ‘guest’ molecules that together form an electrically conducting charge-transfer complex (molecule@MOF). Thin films of Cu 3(BTC) 2 were grown on fused silica using solution step-by-step growth and were infiltrated with the molecule tetracyanoquinodimethane (TCNQ). The infiltrated MOF films were extensively characterized using optical microscopy, scanning electron microscopy, Raman spectroscopy, electrical conductivity, and thermoelectric properties. Thermopower measurements on TCNQ@Cu 3(BTC) 2 revealed a positive Seebeck coefficient of ~400 μV/k, indicating that holesmore » are the primary carriers in this material. The high value of the Seebeck coefficient and the expected low thermal conductivity suggest that molecule@MOF materials may be attractive for thermoelectric power conversion applications requiring low cost, solution-processable, and non-toxic active materials.« less

Electronic structure and thermoelectric transport properties of the golden Th{sub 2}S{sub 3}-type Ti{sub 2}O{sub 3} under pressure

DOE Office of Scientific and Technical Information (OSTI.GOV)

Xu, Bin, E-mail: hnsqxubin@163.com; Gao, Changzheng; Zhang, Jing

2016-05-15

A lot of physical properties of Th{sub 2}S{sub 3}-type Ti{sub 2}O{sub 3} have investigated experimentally, hence, we calculated electronic structure and thermoelectric transport properties by the first-principles calculation under pressure. The increase of the band gaps is very fast from 30 GPa to 35 GPa, which is mainly because of the rapid change of the lattice constants. The total density of states becomes smaller with increasing pressure, which shows that Seebeck coefficient gradually decreases. Two main peaks of Seebeck coefficients always decrease and shift to the high doping area with increasing temperature under pressure. The electrical conductivities always decrease withmore » increasing temperature under pressure. The electrical conductivity can be improved by increasing pressure. Electronic thermal conductivity increases with increasing pressure. It is noted that the thermoelectric properties is reduced with increasing temperature.« less

Synthetic thermoelectric materials comprising phononic crystals

DOEpatents

El-Kady, Ihab F; Olsson, Roy H; Hopkins, Patrick; Reinke, Charles; Kim, Bongsang

2013-08-13

Synthetic thermoelectric materials comprising phononic crystals can simultaneously have a large Seebeck coefficient, high electrical conductivity, and low thermal conductivity. Such synthetic thermoelectric materials can enable improved thermoelectric devices, such as thermoelectric generators and coolers, with improved performance. Such synthetic thermoelectric materials and devices can be fabricated using techniques that are compatible with standard microelectronics.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Heimann, Stefan; Schulz, Stephan; Schaumann, Julian

We report on the synthesis of Sb 2Te 3 nanoparticles with record-high figure of merit values of up to 1.5. The central thermoelectric parameters, electrical conductivity, thermal conductivity and Seebeck coefficient, were independently optimized. Critical influence of porosity for the fabrication of highly efficient thermoelectric materials is firstly demonstrated, giving a strong guidance for the optimization of other thermoelectric materials.

Thermoelectric properties of fully hydrogenated graphene: Semi-classical Boltzmann theory

DOE Office of Scientific and Technical Information (OSTI.GOV)

Reshak, A. H., E-mail: maalidph@yahoo.co.uk; Center of Excellence Geopolymer and Green Technology, School of Material Engineering, University Malaysia Perlis, 01007 Kangar, Perlis

2015-06-14

Based on the calculated band structure, the electronic transport coefficients of chair-/boat-like graphane were evaluated by using the semi-classical Boltzmann theory and rigid band model. The maximum value of electrical conductivity for chair (boat)-like graphane of about 1.4 (0.6) × 10{sup 19} (Ωms){sup −1} is achieved at 600 K. The charge carrier concentration and the electrical conductivity linearly increase with increasing the temperature in agreement with the experimental work for graphene. The investigated materials exhibit the highest value of Seebeck coefficient at 300 K. We should emphasize that in the chemical potential between ∓0.125 μ(eV) the investigated materials exhibit minimum value of electronic thermalmore » conductivity, therefore, maximum efficiency. As the temperature increases, the electronic thermal conductivity increases exponentially, in agreement with the experimental data of graphene. We also calculated the power factor of chair-/boat-like graphane at 300 and 600 K as a function of chemical potential between ∓0.25 μ(eV)« less

Thermodynamic properties and transport coefficients of air thermal plasmas mixed with ablated vapors of Cu and polytetrafluoroethylene

DOE Office of Scientific and Technical Information (OSTI.GOV)

Zhang, JunMin, E-mail: jmzhang@buaa.edu.cn, E-mail: guanyg@tsinghua.edu.cn; Lu, ChunRong; Guan, YongGang, E-mail: jmzhang@buaa.edu.cn, E-mail: guanyg@tsinghua.edu.cn

2015-10-15

Because the fault arc in aircraft electrical system often causes a fire, it is particularly important to analyze its energy and transfer for aircraft safety. The calculation of arc energy requires the basic parameters of the arc. This paper is mainly devoted to the calculations of equilibrium composition, thermodynamic properties (density, molar weight, enthalpy, and specific heat at constant pressure) and transport coefficients (thermal conductivity, electrical conductivity, and viscosity) of plasmas produced by a mixture of air, Cu, and polytetrafluoroethylene under the condition of local thermodynamic equilibrium. The equilibrium composition is determined by solving a system of equations around themore » number densities of each species. The thermodynamic properties are obtained according to the standard thermodynamic relationships. The transport coefficients are calculated using the Chapman-Enskog approximations. Results are presented in the temperature range from 3000 to 30 000 K for pressures of 0.08 and 0.1 MPa, respectively. The results are more accurate and are reliable reference data for theoretical analysis and computational simulation of the behavior of fault arc.« less

A novel coefficient for detecting and quantifying asymmetry of California electricity market based on asymmetric detrended cross-correlation analysis.

PubMed

Wang, Fang

2016-06-01

In order to detect and quantify asymmetry of two time series, a novel cross-correlation coefficient is proposed based on recent asymmetric detrended cross-correlation analysis (A-DXA), which we called A-DXA coefficient. The A-DXA coefficient, as an important extension of DXA coefficient ρDXA, contains two directional asymmetric cross-correlated indexes, describing upwards and downwards asymmetric cross-correlations, respectively. By using the information of directional covariance function of two time series and directional variance function of each series itself instead of power-law between the covariance function and time scale, the proposed A-DXA coefficient can well detect asymmetry between the two series no matter whether the cross-correlation is significant or not. By means of the proposed A-DXA coefficient conducted over the asymmetry for California electricity market, we found that the asymmetry between the prices and loads is not significant for daily average data in 1999 yr market (before electricity crisis) but extremely significant for those in 2000 yr market (during the crisis). To further uncover the difference of asymmetry between the years 1999 and 2000, a modified H statistic (MH) and ΔMH statistic are proposed. One of the present contributions is that the high MH values calculated for hourly data exist in majority months in 2000 market. Another important conclusion is that the cross-correlation with downwards dominates over the whole 1999 yr in contrast to the cross-correlation with upwards dominates over the 2000 yr.

Frequency dependence of electrical properties of polyvinylidene fluoride/graphite electrode waste/natural carbon black composite

NASA Astrophysics Data System (ADS)

Insiyanda, D. R.; Indayaningsih, N.; Prihandoko, B.; Subhan, A.; Khaerudini, D. S.; Widodo, H.; Destyorini, F.; Chaer, A.

2018-03-01

Polyvinylidene fluoride (PVdF) is a semi-crystalline thermoplastic material with remarkably high piezoelectric coefficient and an attractive polymer matrix for micro-composite with superior mechanical and electrical properties. The conductive filler is obtained from Graphite Electrode Waste (GEW) and Natural Carbon Black (NCB). The variation of composite content (%) of PVdF/NCB/GEW were 100/0/0, 95/5/0, 95/0/5, 95/2.5/2.5. This experiment employed dry dispersion method for material mixing. The materials were then moulded using hot press machine with compression parameters of P = 5.5 MPa, T = 150 °C, t = 60 minutes, A = 5×5×(0.2 - 0.4) cm3. The electrical conductivity properties of pure PVdF, as well as PVdF/GEW, PVdF/NCB, and PVdF/NCB/GEW composites were investigated in a frequency range of 100 to 100000 Hz. The PVdF/GEW sample obtained the highest electrical conductivity. It is concluded that GEW and NCB can be incorporated into PVdF as a conductive filler to increase the conductivity of conductive material composite without solvent.

Role of grain and grain boundary on the electrical and thermal conductivity of Bi0.9Y0.1Fe0.9Mn0.1O3 ceramics

NASA Astrophysics Data System (ADS)

Pandey, Rabichandra; Panda, Chandrakanta; Kumar, Pawan; Pradhan, Lagen Kumar; Kar, Manoranjan

2017-05-01

Role of grain and grain boundary on electrical and thermal conductivity of Bi0.9Y0.1Fe0.9Mn0.1O3 ceramic was investigated systematically. Tartaric acid modified sol gel method was used to synthesize the compound. X-ray diffraction technique was used to confirm the formation of single phase orthorhombic (Pbnm) structure. Electrical properties of the sample were measured with a wide frequency range from 100Hz to 10MHz at different temperature from 40°C to 250°C. AC impedance studies indicate the presence of grain and grain boundary effect. The negative temperature coefficient of resistance (NTCR) behaviour of the compound has been confirmed by the cole-cole plot. DC electrical and thermal conductivities of the compound were explained on the basis of grain and grain boundaries.

Assessment of critical path analyses of the relationship between permeability and electrical conductivity of pore networks

NASA Astrophysics Data System (ADS)

Skaggs, Todd H.

2011-10-01

Critical path analysis (CPA) is a method for estimating macroscopic transport coefficients of heterogeneous materials that are highly disordered at the micro-scale. Developed originally to model conduction in semiconductors, numerous researchers have noted that CPA might also have relevance to flow and transport processes in porous media. However, the results of several numerical investigations of critical path analysis on pore network models raise questions about the applicability of CPA to porous media. Among other things, these studies found that (i) in well-connected 3D networks, CPA predictions were inaccurate and became worse when heterogeneity was increased; and (ii) CPA could not fully explain the transport properties of 2D networks. To better understand the applicability of CPA to porous media, we made numerical computations of permeability and electrical conductivity on 2D and 3D networks with differing pore-size distributions and geometries. A new CPA model for the relationship between the permeability and electrical conductivity was found to be in good agreement with numerical data, and to be a significant improvement over a classical CPA model. In sufficiently disordered 3D networks, the new CPA prediction was within ±20% of the true value, and was nearly optimal in terms of minimizing the squared prediction errors across differing network configurations. The agreement of CPA predictions with 2D network computations was similarly good, although 2D networks are in general not well-suited for evaluating CPA. Numerical transport coefficients derived for regular 3D networks of slit-shaped pores were found to be in better agreement with experimental data from rock samples than were coefficients derived for networks of cylindrical pores.

Ambipolar thermoelectric power of chemically-exfoliated RuO2 nanosheets

NASA Astrophysics Data System (ADS)

Kim, Jeongmin; Yoo, Somi; Moon, Hongjae; Kim, Se Yun; Ko, Dong-Su; Roh, Jong Wook; Lee, Wooyoung

2018-01-01

The electrical conductivity and Seebeck coefficient of RuO2 nanosheets are enhanced by metal nanoparticle doping using Ag-acetate solutions. In this study, RuO2 monolayer and bilayer nanosheets exfoliated from layered alkali metal ruthenates are transferred to Si substrates for device fabrication, and the temperature dependence of their conductivity and Seebeck coefficients is investigated. For pristine RuO2 nanosheets, the sign of the Seebeck coefficient changes with temperature from 350-450 K. This indicates that the dominant type of charge carrier is dependent on the temperature, and the RuO2 nanosheets show ambipolar carrier transport behavior. By contrast, the sign of the Seebeck coefficient for Ag nanoparticle-doped RuO2 nanosheets does not change with temperature, indicating that the extra charge carriers from metal nanoparticles promote n-type semiconductor behavior.

Enhancement of Seebeck coefficient in graphene superlattices by electron filtering technique

NASA Astrophysics Data System (ADS)

Mishra, Shakti Kumar; Kumar, Amar; Kaushik, Chetan Prakash; Dikshit, Biswaranjan

2018-01-01

We show theoretically that the Seebeck coefficient and the thermoelectric figure of merit can be increased by using electron filtering technique in graphene superlattice based thermoelectric devices. The average Seebeck coefficient for graphene-based thermoelectric devices is proportional to the integral of the distribution of Seebeck coefficient versus energy of electrons. The low energy electrons in the distribution curve are found to reduce the average Seebeck coefficient as their contribution is negative. We show that, with electron energy filtering technique using multiple graphene superlattice heterostructures, the low energy electrons can be filtered out and the Seebeck coefficient can be increased. The multiple graphene superlattice heterostructures can be formed by graphene superlattices with different periodic electric potentials applied above the superlattice. The overall electronic band gap of the multiple heterostructures is dependent upon the individual band gap of the graphene superlattices and can be tuned by varying the periodic electric potentials. The overall electronic band gap of the multiple heterostructures has to be properly chosen such that, the low energy electrons which cause negative Seebeck distribution in single graphene superlattice thermoelectric devices fall within the overall band gap formed by the multiple heterostructures. Although the electrical conductance is decreased in this technique reducing the thermoelectric figure of merit, the overall figure of merit is increased due to huge increase in Seebeck coefficient and its square dependency upon the Seebeck coefficient. This is an easy technique to make graphene superlattice based thermoelectric devices more efficient and has the potential to significantly improve the technology of energy harvesting and sensors.

Evaluation of Temperature-Dependent Effective Material Properties and Performance of a Thermoelectric Module

NASA Astrophysics Data System (ADS)

Chien, Heng-Chieh; Chu, En-Ting; Hsieh, Huey-Lin; Huang, Jing-Yi; Wu, Sheng-Tsai; Dai, Ming-Ji; Liu, Chun-Kai; Yao, Da-Jeng

2013-07-01

We devised a novel method to evaluate the temperature-dependent effective properties of a thermoelectric module (TEM): Seebeck coefficient ( S m), internal electrical resistance ( R m), and thermal conductance ( K m). After calculation, the effective properties of the module are converted to the average material properties of a p- n thermoelectric pillar pair inside the module: Seebeck coefficient ( S TE), electrical resistivity ( ρ TE), and thermal conductivity ( k TE). For a commercial thermoelectric module (Altec 1091) chosen to verify the novel method, the measured S TE has a maximum value at bath temperature of 110°C; ρ TE shows a positive linear trend dependent on the bath temperature, and k TE increases slightly with increasing bath temperature. The results show the method to have satisfactory measurement performance in terms of practicability and reliability; the data for tests near 23°C agree with published values.

Many-body design of highly strained GaInNAs electroabsorption modulators on GaInAs ternary substrates

NASA Astrophysics Data System (ADS)

Fujisawa, Takeshi; Arai, Masakazu; Kano, Fumiyoshi

2010-05-01

Electroabsorption in highly strained GaInAs and GaInNAs quantum wells (QWs) grown on GaInAs or quasi-GaInAs substrates is investigated by using microscopic many-body theory. The effects of various parameters, such as strain, barrier height, substrate composition, and temperature are thoroughly examined. It is shown that the value of the absorption coefficient strongly depends on the depth of the QWs under large bias electric field due to the small overlap integral of wave functions between the conduction and valence bands. The use of GaInNAs QWs makes the strain in the well layer very small. Further, the effective quantum-well depth is increased in GaInNAs QWs due to the anticrossing interaction between the conduction and N-resonant bands, making it possible to obtain larger absorption coefficient under large bias electric fields without using wide-band gap materials for barriers.

Structure Evolution and Thermoelectric Properties of Carbonized Polydopamine Thin Films.

PubMed

Li, Haoqi; Aulin, Yaroslav V; Frazer, Laszlo; Borguet, Eric; Kakodkar, Rohit; Feser, Joseph; Chen, Yan; An, Ke; Dikin, Dmitriy A; Ren, Fei

2017-03-01

Carbonization of nature-inspired polydopamine can yield thin films with high electrical conductivity. Understanding of the structure of carbonized PDA (cPDA) is therefore highly desired. In this study, neutron diffraction, Raman spectroscopy, and other techniques indicate that cPDA samples are mainly amorphous with some short-range ordering and graphite-like structure that emerges with increasing heat treatment temperature. The electrical conductivity and the Seebeck coefficient show different trends with heat treatment temperature, while the thermal conductivity remains insensitive. The largest room-temperature ZT of 2 × 10 -4 was obtained on samples heat-treated at 800 °C, which is higher than that of reduced graphene oxide.

Exact Thermal Transport Properties of Gray-Arsenic using Electon-Phonon Coupling

NASA Astrophysics Data System (ADS)

Kang, Seoung-Hun; Kwon, Young-Kyun

Using various theoretical methods, we investigate the thermoelectric property of gray arsenic. Thermoelectric devices that utilize the Seebeck effect convert heat flow into electrical energy. The conversion efficiency of such a device is determined by its figure of merit or ZT value, which is related to various transport coefficients, such as Seebeck coefficient and the ratio of its electrical conductivity to its thermal counterpart for given temperature. To calculate various transport coefficients and thus the ZT values of gray arsenic, we apply the Boltzmann transport theory to its electronic and phononic structures obtained by density functional theory and density functional perturbation theory together with maximally locallized Wannier functions. During this procedure, we evaluate its relaxation time accurately by explicitly considering electron-phonon coupling. Our result reveals that gray arsenic may be used for a good p-type thermoelectric devices.

Thermoelectric transport in two-dimensional giant Rashba systems

NASA Astrophysics Data System (ADS)

Xiao, Cong; Li, Dingping; Ma, Zhongshui; Niu, Qian

Thermoelectric transport in strongly spin-orbit coupled two-dimensional Rashba systems is studied using the analytical solution of the linearized Boltzmann equation. To highlight the effects of inter-band scattering, we assume point-like potential impurities, and obtain the band-and energy-dependent transport relaxation times. Unconventional transport behaviors arise when the Fermi level lies near or below the band crossing point (BCP), such as the non-Drude electrical conducivity below the BCP, the failure of the standard Mott relation linking the Peltier coefficient to the electrical conductivity near the BCP, the enhancement of diffusion thermopower and figure of merit below the BCP, the zero-field Hall coefficient which is not inversely proportional to and not a monotonic function of the carrier density, the enhanced Nernst coefficient below the BCP, and the enhanced current-induced spin-polarization efficiency.

High temperature electrical resistivity and Seebeck coefficient of Ge2Sb2Te5 thin films

NASA Astrophysics Data System (ADS)

Adnane, L.; Dirisaglik, F.; Cywar, A.; Cil, K.; Zhu, Y.; Lam, C.; Anwar, A. F. M.; Gokirmak, A.; Silva, H.

2017-09-01

High-temperature characterization of the thermoelectric properties of chalcogenide Ge2Sb2Te5 (GST) is critical for phase change memory devices, which utilize self-heating to quickly switch between amorphous and crystalline states and experience significant thermoelectric effects. In this work, the electrical resistivity and Seebeck coefficient are measured simultaneously as a function of temperature, from room temperature to 600 °C, on 50 nm and 200 nm GST thin films deposited on silicon dioxide. Multiple heating and cooling cycles with increasingly maximum temperature allow temperature-dependent characterization of the material at each crystalline state; this is in contrast to continuous measurements which return the combined effects of the temperature dependence and changes in the material. The results show p-type conduction (S > 0), linear S(T), and a positive Thomson coefficient (dS/dT) up to melting temperature. The results also reveal an interesting linearity between dS/dT and the conduction activation energy for mixed amorphous-fcc GST, which can be used to estimate one parameter from the other. A percolation model, together with effective medium theory, is adopted to correlate the conductivity of the material with average grain sizes obtained from XRD measurements. XRD diffraction measurements show plane-dependent thermal expansion for the cubic and hexagonal phases.

Effect of surface deposits on electromagnetic waves propagating in uniform ducts

NASA Technical Reports Server (NTRS)

Baumeister, Kenneth J.

1990-01-01

A finite-element Galerkin formulation was used to study the effect of material surface deposits on the reflective characteristics of straight uniform ducts with PEC (perfectly electric conducting) walls. Over a wide frequency range, the effect of both single and multiple surface deposits on the duct reflection coefficient were examined. The power reflection coefficient was found to be significantly increased by the addition of deposits on the wall.

Diffusion and Electric Mobility of KCI within Isolated Cuticles of Citrus aurantium 1

PubMed Central

Tyree, Melvin T.; Wescott, Charles R.; Tabor, Christopher A.; Morse, Anne D.

1992-01-01

Fick's second law has been used to predict the time course of electrical conductance change in isolated cuticles following the rapid change in bathing solution (KCI) from concentration C to 0.1 C. The theoretical time course is dependent on the coefficient of diffusion of KCI in the cuticle and the cuticle thickness. Experimental results, obtained from cuticles isolated from sour orange (Citrus aurantium), fit with a diffusion model of an isolated cuticle in which about 90% of the conductance change following a solution change is due to salts diffusing from polar pores in the wax, and 10% of the change is due to salt diffusion from the wax. Short and long time constants for the washout of KCI were found to be 0.11 and 3.8 hours, respectively. These time constants correspond to KCI diffusion coefficients of 1 × 10−15 and 3 × 10−17 square meters per second, respectively. The larger coefficient is close to the diffusion coefficient for water in polar pores of Citrus reported elsewhere (M Becker, G Kerstiens, J Schönherr [1986] Trees 1: 54-60). This supports our interpretation of the washout kinetics of KCI following a change in concentration of bathing solution. PMID:16668971

Macroscopic Modeling of In Vivo Drug Transport in Electroporated Tissue.

PubMed

Boyd, Bradley; Becker, Sid

2016-03-01

This study develops a macroscopic model of mass transport in electroporated biological tissue in order to predict the cellular drug uptake. The change in the macroscopic mass transport coefficient is related to the increase in electrical conductivity resulting from the applied electric field. Additionally, the model considers the influences of both irreversible electroporation (IRE) and the transient resealing of the cell membrane associated with reversible electroporation. Two case studies are conducted to illustrate the applicability of this model by comparing transport associated with two electrode arrangements: side-by-side arrangement and the clamp arrangement. The results show increased drug transmission to viable cells is possible using the clamp arrangement due to the more uniform electric field.

The effects of the electric and intense laser field on the binding energies of donor impurity states (1s and 2p±) and optical absorption between the related states in an asymmetric parabolic quantum well

NASA Astrophysics Data System (ADS)

Kasapoglu, E.; Sakiroglu, S.; Sökmen, I.; Restrepo, R. L.; Mora-Ramos, M. E.; Duque, C. A.

2016-10-01

We have calculated the effects of electric and intense laser fields on the binding energies of the ground and some excited states of conduction electrons coupled to shallow donor impurities as well as the total optical absorption coefficient for transitions between 1s and 2p± electron-impurity states in a asymmetric parabolic GaAs/Ga1-x AlxAs quantum well. The binding energies were obtained using the effective-mass approximation within a variational scheme. Total absorption coefficient (linear and nonlinear absorption coefficient) for the transitions between any two impurity states were calculated from first- and third-order dielectric susceptibilities derived within a perturbation expansion for the density matrix formalism. Our results show that the effects of the electric field, intense laser field, and the impurity location on the binding energy of 1s-impurity state are more pronounced compared with other impurity states. If the well center is changed to be Lc<0 (Lc>0), the effective well width decreases (increases), and thus we can obtain the red or blue shift in the resonant peak position of the absorption coefficient by changing the intensities of the electric and non-resonant intense laser field as well as dimensions of the well and impurity positions.

Investigation of thermoelectricity in KScSn half-Heusler compound

NASA Astrophysics Data System (ADS)

Shrivastava, Deepika; Acharya, Nikita; Sanyal, Sankar P.

2018-05-01

The electronic and transport properties of KScSn half-Heusler (HH) compound have been investigated using first-principles density functional theory and semi classical Boltzmann transport theory. The electronic band structure and density of states (total and partial) show semiconducting nature of KScSn with band gap 0.48 eV which agree well with previously reported results. The transport coefficient such as electrical conductivity, Seebeck coefficient, electronic thermal conductivity and power factor as a function of chemical potential are evaluated. KScSn has high power factor for p-type doping and is a potential candidate for thermoelectric applications.

Thickness dependence of optical properties of amorphous indium oxide thin films deposited by reactive evaporation

NASA Astrophysics Data System (ADS)

Uluta, K.; Deer, D.; Skarlatos, Y.

2006-08-01

The electrical conductivity and absorption coefficient of amorphous indium oxide thin films, thermally evaporated on glass substrates at room temperature, were evaluated. For direct transitions the variation of the optical band gap with thickness was determined and this variation was supposed to appear due to the variation of localized gap states, whereas the variation of conductivity with thickness was supposed to be due to the variation of carrier concentration. We attribute the variation of absorption coefficient with thickness to the variation of optical band gap energy rather than optical interference.

Tuning conductivity in boron nanowire by edge geometry

NASA Astrophysics Data System (ADS)

Bhuyan, Prabal Dev; Gupta, Sanjeev K.; Sonvane, Yogesh; Gajjar, P. N.

2018-04-01

In present study, we have investigated electronic and temperature dependent transport properties of carbyne like linear chain and ribbon like zigzag structures of Boron (B) nanowire. The linear chain structure showed higher electric and thermal conductivity, as it is sp-hybridized, than its counterpart ribbon (R) structure. However the conductivity of ribbon structure increases with increases in width due to edge geometry effect. The ribbon (3R) structure showed high electric and thermal conductivity of 8.0×1019 1/Ω m s and 0.59×1015 W/ m K respectively. Interestingly we have observed that B linear chain showed higher thermal conductivity of 0.23×1015 W/ m K than its ribbon R and 2R structure above 600K. Because of high Seebeck co-efficient of boron chain and ribbon (R) structures at low temperature, they could find applications in thermoelectric sensors. Our results show that tuning conductivity property of boron nanowire could be of great interest in research for future electric connector in nanodevices.

The Role of Additional Pulses in Electropermeabilization Protocols

PubMed Central

Suárez, Cecilia; Soba, Alejandro; Maglietti, Felipe; Olaiz, Nahuel; Marshall, Guillermo

2014-01-01

Electropermeabilization (EP) based protocols such as those applied in medicine, food processing or environmental management, are well established and widely used. The applied voltage, as well as tissue electric conductivity, are of utmost importance for assessing final electropermeabilized area and thus EP effectiveness. Experimental results from literature report that, under certain EP protocols, consecutive pulses increase tissue electric conductivity and even the permeabilization amount. Here we introduce a theoretical model that takes into account this effect in the application of an EP-based protocol, and its validation with experimental measurements. The theoretical model describes the electric field distribution by a nonlinear Laplace equation with a variable conductivity coefficient depending on the electric field, the temperature and the quantity of pulses, and the Penne's Bioheat equation for temperature variations. In the experiments, a vegetable tissue model (potato slice) is used for measuring electric currents and tissue electropermeabilized area in different EP protocols. Experimental measurements show that, during sequential pulses and keeping constant the applied voltage, the electric current density and the blackened (electropermeabilized) area increase. This behavior can only be attributed to a rise in the electric conductivity due to a higher number of pulses. Accordingly, we present a theoretical modeling of an EP protocol that predicts correctly the increment in the electric current density observed experimentally during the addition of pulses. The model also demonstrates that the electric current increase is due to a rise in the electric conductivity, in turn induced by temperature and pulse number, with no significant changes in the electric field distribution. The EP model introduced, based on a novel formulation of the electric conductivity, leads to a more realistic description of the EP phenomenon, hopefully providing more accurate predictions of treatment outcomes. PMID:25437512

Mode-coupling theoretical analysis of transport and relaxation properties of liquid dimethylimidazolium chloride

NASA Astrophysics Data System (ADS)

Yamaguchi, T.; Koda, S.

2010-03-01

The mode-coupling theory for molecular liquids based on the interaction-site model is applied to a representative molecular ionic liquid, dimethylimidazolium chloride, and dynamic properties such as shear viscosity, self-diffusion coefficients, reorientational relaxation time, electric conductivity, and dielectric relaxation spectrum are analyzed. Molecular dynamics (MD) simulation is also performed on the same system for comparison. The theory captures the characteristics of the dynamics of the ionic liquid qualitatively, although theoretical relaxation times are several times larger than those from the MD simulation. Large relaxations are found in the 100 MHz region in the dispersion of the shear viscosity and the dielectric relaxation, in harmony with various experiments. The relaxations of the self-diffusion coefficients are also found in the same frequency region. The dielectric relaxation spectrum is divided into the contributions of the translational and reorientational modes, and it is demonstrated that the relaxation in the 100 MHz region mainly stems from the translational modes. The zero-frequency electric conductivity is close to the value predicted by the Nernst-Einstein equation in both MD simulation and theoretical calculation. However, the frequency dependence of the electric conductivity is different from those of self-diffusion coefficients in that the former is smaller than the latter in the gigahertz-terahertz region, which is compensated by the smaller dispersion of the former in the 100 MHz region. The analysis of the theoretical calculation shows that the difference in their frequency dependence is due to the different contribution of the short- and long-range liquid structures.

Aerodynamic resistance reduction of electric and hybrid vehicles

NASA Technical Reports Server (NTRS)

1979-01-01

The generation of an EHV aerodynamic data base was initiated by conducting full-scale wind tunnel tests on 16 vehicles. Zero-yaw drag coefficients ranged from a high of 0.58 for a boxey delivery van and an open roadster to a low of about 0.34 for a current 4-passenger prototype automobile which was designed with aerodynamics as an integrated parameter. Characteristic effects of aspect ratio or fineness ratio which might appear if electric vehicle shape proportions were to vary significantly from current automobiles were identified. Some preliminary results indicate a 5 to 10% variation in drag over the range of interest. Effective drag coefficient wind-weighting factors over J227a driving cycles in the presence of annual mean wind fields were identified. Such coefficients, when properly weighted, were found to be from 5 to 65% greater than the zero-yaw drag coefficient in the cases presented. A vehicle aerodynamics bibliography of over 160 entries, in six general categories is included.

Unavoidable electric current caused by inhomogeneities and its influence on measured material parameters of thermoelectric materials

NASA Astrophysics Data System (ADS)

Song, K.; Song, H. P.; Gao, C. F.

2018-03-01

It is well known that the key factor determining the performance of thermoelectric materials is the figure of merit, which depends on the thermal conductivity (TC), electrical conductivity, and Seebeck coefficient (SC). The electric current must be zero when measuring the TC and SC to avoid the occurrence of measurement errors. In this study, the complex-variable method is used to analyze the thermoelectric field near an elliptic inhomogeneity in an open circuit, and the field distributions are obtained in closed form. Our analysis shows that an electric current inevitably exists in both the matrix and the inhomogeneity even though the circuit is open. This unexpected electric current seriously affects the accuracy with which the TC and SC are measured. These measurement errors, both overall and local, are analyzed in detail. In addition, an error correction method is proposed based on the analytical results.

A novel coefficient for detecting and quantifying asymmetry of California electricity market based on asymmetric detrended cross-correlation analysis

NASA Astrophysics Data System (ADS)

Wang, Fang

2016-06-01

In order to detect and quantify asymmetry of two time series, a novel cross-correlation coefficient is proposed based on recent asymmetric detrended cross-correlation analysis (A-DXA), which we called A-DXA coefficient. The A-DXA coefficient, as an important extension of DXA coefficient ρ D X A , contains two directional asymmetric cross-correlated indexes, describing upwards and downwards asymmetric cross-correlations, respectively. By using the information of directional covariance function of two time series and directional variance function of each series itself instead of power-law between the covariance function and time scale, the proposed A-DXA coefficient can well detect asymmetry between the two series no matter whether the cross-correlation is significant or not. By means of the proposed A-DXA coefficient conducted over the asymmetry for California electricity market, we found that the asymmetry between the prices and loads is not significant for daily average data in 1999 yr market (before electricity crisis) but extremely significant for those in 2000 yr market (during the crisis). To further uncover the difference of asymmetry between the years 1999 and 2000, a modified H statistic (MH) and ΔMH statistic are proposed. One of the present contributions is that the high MH values calculated for hourly data exist in majority months in 2000 market. Another important conclusion is that the cross-correlation with downwards dominates over the whole 1999 yr in contrast to the cross-correlation with upwards dominates over the 2000 yr.

On the transport coefficients of hydrogen in the inertial confinement fusion regime

DOE Office of Scientific and Technical Information (OSTI.GOV)

Lambert, Flavien; Recoules, Vanina; Decoster, Alain

2011-05-15

Ab initio molecular dynamics is used to compute the thermal and electrical conductivities of hydrogen from 10 to 160 g cm{sup -3} and temperatures up to 800 eV, i.e., thermodynamical conditions relevant to inertial confinement fusion (ICF). The ionic structure is obtained using molecular dynamics simulations based on an orbital-free treatment for the electrons. The transport properties were computed using ab initio simulations in the DFT/LDA approximation. The thermal and electrical conductivities are evaluated using Kubo-Greenwood formulation. Particular attention is paid to the convergence of electronic transport properties with respect to the number of bands and atoms. These calculations aremore » then used to check various analytical models (Hubbard's, Lee-More's and Ichimaru's) widely used in hydrodynamics simulations of ICF capsule implosions. The Lorenz number, which is the ratio between thermal and electrical conductivities, is also computed and compared to the well-known Wiedemann-Franz law in different regimes ranging from the highly degenerate to the kinetic one. This allows us to deduce electrical conductivity from thermal conductivity for analytical model. We find that the coupling of Hubbard and Spitzer models gives a correct description of the behavior of electrical and thermal conductivities in the whole thermodynamic regime.« less

Effect of surface deposits on electromagnetic propagation in uniform ducts

NASA Technical Reports Server (NTRS)

Baumeister, Kenneth J.

1991-01-01

A finite-element Galerkin formulation has been used to study the effect of material surface deposits on the reflective characteristics of straight uniform ducts with PEC (perfectly electric conducting) walls. Over a wide frequency range, the effect of both single and multiple dielectric surface deposits on the duct reflection coefficient were examined. The power reflection coefficient was found to be significantly increased by the addition of deposits on the wall.

Thermoelectric properties of pressure-sintered Si(0.8)Ge(0.2) thermoelectric alloys

NASA Technical Reports Server (NTRS)

Vining, Cronin B.; Laskow, William; Hanson, Jack O.; Van Der Beck, Roland R.; Gorsuch, Paul D.

1991-01-01

The thermoelectric properties of 28 sintered Si(0.8)Ge(0.2) alloys, heavily doped with either B or P and prepared from powders with median particle sizes ranging from about 1 to over 100 microns, have been determined from 300 to 1300 K. The thermal conductivity decreases with decreasing particle size; however, the figure of merit is not significantly increased due to a compensating reduction in the electrical conductivity. The thermoelectric figure of merit is in good agreement with results of Dismukes et al. (1964) on similarly doped alloys prepared by zone-leveling techniques. The electrical and thermal conductivity are found to be sensitive to preparation procedure while the Seebeck coefficient and figure of merit are much less sensitive. The high-temperature electrical properties are consistent with charge carrier scattering by acoustic or optical phonons.

Modeling thermoelectric transport in organic materials.

PubMed

Wang, Dong; Shi, Wen; Chen, Jianming; Xi, Jinyang; Shuai, Zhigang

2012-12-28

Thermoelectric energy converters can directly convert heat to electricity using semiconducting materials via the Seebeck effect and electricity to heat via the Peltier effect. Their efficiency depends on the dimensionless thermoelectric figure of merit of the material, which is defined as zT = S(2)σT/κ with S, σ, κ, and T being the Seebeck coefficient, electrical conductivity, thermal conductivity, and absolute temperature respectively. Organic materials for thermoelectric applications have attracted great attention. In this review, we present our recent progress made in developing theories and computational schemes to predict the thermoelectric figure of merit at the first-principles level. The methods have been applied to model thermoelectric transport in closely-packed molecular crystals and one-dimensional conducting polymer chains. The physical insight gained in these studies will help in the design of efficient organic thermoelectric materials.

Upper mantle electrical conductivity for seven subcontinental regions of the Earth

USGS Publications Warehouse

Campbell, W.H.; Schiffmacher, E.R.

1988-01-01

Spherical harmonic analysis coefficients of the external and internal parts of the quiet-day geomagnetic field variations (Sq) separated for the 7 continental regions of the observatories have been used to determine conductivity profiles to depths of about 600 km by the Schmucker equivalent substitute conductor method. The profiles give evidence of increases in conductivity between about 150 and 350 km depth, then a general increase in conductivity thereafter. For South America we found a high conductivity at shallow depths. The European profile showed a highly conducting layer near 125 km. At the greater depths, Europe, Australia and South America had the lowest values of conductivity. North America and east Asia had intermediate values whereas the African and central Asian profiles both showed the conductivities rising rapidly beyond 450 km depth. The regional differences indicate that there may be considerable lateral heterogeneity of electrical conductivity in the Earth's upper mantle. -Authors

Improving our understanding of hydraulic-electrical relations: A case study of the surficial aquifer in Emirate Abu Dhabi

USGS Publications Warehouse

Ikard, Scott; Kress, Wade

2016-01-01

Transmissivity is a bulk hydraulic property that can be correlated with bulk electrical properties of an aquifer. In aquifers that are electrically-resistive relative to adjacent layers in a horizontally stratified sequence, transmissivity has been shown to correlate with bulk transverse resistance. Conversely, in aquifers that are electrically-conductive relative to adjacent layers, transmissivity has been shown to correlate with bulk longitudinal conductance. In both cases, previous investigations have relied on small datasets (on average less than eight observations) that have yielded coefficients of determination (R2) that are typically in the range of 0.6 to 0.7 to substantiate these relations. Compared to previous investigations, this paper explores hydraulic-electrical relations using a much larger dataset. Geophysical data collected from 26 boreholes in Emirate Abu Dhabi, United Arab Emirates, are used to correlate transmissivity modeled from neutron porosity logs to the bulk electrical properties of the surficial aquifer that are computed from deep-induction logs. Transmissivity is found to be highly correlated with longitudinal conductance. An R2 value of 0.853 is obtained when electrical effects caused by variations in pore-fluid salinity are taken into consideration.

Structure evolution and thermoelectric properties of carbonized polydopamine thin films

DOE PAGES

Li, Haoqi; Aulin, Yaroslav V.; Frazer, Laszlo; ...

2017-02-13

Carbonization of nature-inspired polydopamine can yield thin films with high electrical conductivity. Understanding of the structure of carbonized PDA (cPDA) is therefore highly desired. In this study, neutron diffraction, Raman spectroscopy, and other techniques indicate that cPDA samples are mainly amorphous with some short-range ordering and graphite-like structure that emerges with increasing heat treatment temperature. The electrical conductivity and the Seebeck coefficient show different trends with heat treatment temperature, while the thermal conductivity remains insensitive. Finally, the largest room-temperature ZT of 2 × 10 –4 was obtained on samples heat-treated at 800 °C, which is higher than that of reducedmore » graphene oxide.« less

Application of Multivariable Analysis and FTIR-ATR Spectroscopy to the Prediction of Properties in Campeche Honey

PubMed Central

Pat, Lucio; Ali, Bassam; Guerrero, Armando; Córdova, Atl V.; Garduza, José P.

2016-01-01

Attenuated total reflectance-Fourier transform infrared spectrometry and chemometrics model was used for determination of physicochemical properties (pH, redox potential, free acidity, electrical conductivity, moisture, total soluble solids (TSS), ash, and HMF) in honey samples. The reference values of 189 honey samples of different botanical origin were determined using Association Official Analytical Chemists, (AOAC), 1990; Codex Alimentarius, 2001, International Honey Commission, 2002, methods. Multivariate calibration models were built using partial least squares (PLS) for the measurands studied. The developed models were validated using cross-validation and external validation; several statistical parameters were obtained to determine the robustness of the calibration models: (PCs) optimum number of components principal, (SECV) standard error of cross-validation, (R 2 cal) coefficient of determination of cross-validation, (SEP) standard error of validation, and (R 2 val) coefficient of determination for external validation and coefficient of variation (CV). The prediction accuracy for pH, redox potential, electrical conductivity, moisture, TSS, and ash was good, while for free acidity and HMF it was poor. The results demonstrate that attenuated total reflectance-Fourier transform infrared spectrometry is a valuable, rapid, and nondestructive tool for the quantification of physicochemical properties of honey. PMID:28070445

Thermoelectric properties of V2O5 thin films deposited by thermal evaporation

NASA Astrophysics Data System (ADS)

Santos, R.; Loureiro, J.; Nogueira, A.; Elangovan, E.; Pinto, J. V.; Veiga, J. P.; Busani, T.; Fortunato, E.; Martins, R.; Ferreira, I.

2013-10-01

This work reports the structural, optical, electrical and thermoelectric properties of vanadium pentoxide (V2O5) thin films deposited at room temperature by thermal evaporation on Corning glass substrates. A post-deposition thermal treatment up to 973 K under atmospheric conditions induces the crystallization of the as-deposited amorphous films with an orthorhombic V2O5 phase with grain sizes around 26 nm. As the annealing temperature rises up to 773 K the electrical conductivity increases. The films exhibit thermoelectric properties with a maximum Seebeck coefficient of -218 μV/K and electrical conductivity of 5.5 (Ω m)-1. All the films show NIR-Vis optical transmittance above 60% and optical band gap of 2.8 eV.

Flexible Dielectric Nanocomposites with Ultrawide Zero-Temperature Coefficient Windows for Electrical Energy Storage and Conversion under Extreme Conditions.

PubMed

Shehzad, Khurram; Xu, Yang; Gao, Chao; Li, Hanying; Dang, Zhi-Min; Hasan, Tawfique; Luo, Jack; Duan, Xiangfeng

2017-03-01

Polymer dielectrics offer key advantages over their ceramic counterparts such as flexibility, scalability, low cost, and high breakdown voltages. However, a major drawback that limits more widespread application of polymer dielectrics is their temperature-dependent dielectric properties. Achieving dielectric constants with low/zero-temperature coefficient (L/0TC) over a broad temperature range is essential for applications in diverse technologies. Here, we report a hybrid filler strategy to produce polymer composites with an ultrawide L/0TC window of dielectric constant, as well as a significantly enhanced dielectric value, maximum energy storage density, thermal conductivity, and stability. By creating a series of percolative polymer composites, we demonstrated hybrid carbon filler based composites can exhibit a zero-temperature coefficient window of 200 °C (from -50 to 150 °C), the widest 0TC window for all polymer composite dielectrics reported to date. We further show the electric and dielectric temperature coefficient of the composites is highly stable against stretching and bending, even under AC electric field with frequency up to 1 MHz. We envision that our method will push the functional limits of polymer dielectrics for flexible electronics in extreme conditions such as in hybrid vehicles, aerospace, power electronics, and oil/gas exploration.

Bandgap tuning and enhancement of seebeck coefficient in one dimensional GeSe

NASA Astrophysics Data System (ADS)

Kagdada, Hardik L.; Dabhi, Shweta D.; Jha, Prafulla K.

2018-04-01

The first principles based density functional theory is used for tuning the electronic bandgap and thermoelectric properties of bulk, two dimensional (2D) and one dimensional (1D) GeSe. There is an increase in the bandgap going from bulk to 1D with indirect to direct bandgap transition. There is a dramatic change in Seebeck coefficient (S) for GeSe going from bulk to 1D at 300 K. The electrical conductivity and electronic thermal conductivity are lower for 1D GeSe compared to the bulk GeSe due to larger bandgap in the case of 1D GeSe.

Friction coefficient determination by electrical resistance measurements

NASA Astrophysics Data System (ADS)

Tunyagi, A.; Kandrai, K.; Fülöp, Z.; Kapusi, Z.; Simon, A.

2018-05-01

A simple and low-cost, DIY-type, Arduino-driven experiment is presented for the study of friction and measurement of the friction coefficient, using a conductive rubber cord as a force sensor. It is proposed for high-school or college/university-level students. We strongly believe that it is worthwhile planning, designing and performing Arduino and compatible sensor-based experiments in physics class in order to ensure a better understanding of phenomena, develop theoretical knowledge and multiple experimental skills.

A strategy to optimize the thermoelectric performance in a spark plasma sintering process

PubMed Central

Chiu, Wan-Ting; Chen, Cheng-Lung; Chen, Yang-Yuan

2016-01-01

Spark plasma sintering (SPS) is currently widely applied to existing alloys as a means of further enhancing the alloys’ figure of merit. However, the determination of the optimal sintering condition is challenging in the SPS process. This report demonstrates a systematic way to independently optimize the Seebeck coefficient S and the ratio of electrical to thermal conductivity (σ/κ) and thus achieve the maximum figure of merit zT = S2(σ/κ)T. Sb2−xInxTe3 (x = 0–0.2) were chosen as examples to validate the method. Although high sintering temperature and pressure are helpful in enhancing the compactness and electrical conductivity of pressed samples, the resultant deteriorated Seebeck coefficient and increasing thermal conductivity eventually offset the benefit. We found that the optimal sintering temperature coincides with temperatures at which the maximum Seebeck coefficient begins to degrade, whereas the optimal sintering pressure coincided with the pressure at which the σ/κ ratio reaches a maximum. Based on this principle, the optimized sintering conditions were determined, and the zT of Sb1.9In0.1Te3 is raised to 0.92 at 600 K, showing an approximately 84% enhancement. This work develops a facile strategy for selecting the optimal SPS sintering condition to further enhance the zT of bulk specimens. PMID:26975209

Determination of water saturation using gas phase partitioning tracers and time-lapse electrical conductivity measurements

DOE Office of Scientific and Technical Information (OSTI.GOV)

Johnson, Timothy C.; Oostrom, Martinus; Truex, Michael J.

2013-05-21

Water saturation is an important indicator of contaminant distribution and plays a governing role in contaminant transport within the vadose zone. Understanding the water saturation distribution is critical for both remediation and contaminant flux monitoring in unsaturated environments. In this work we propose and demonstrate a method of remotely determining water saturation levels using gas phase partitioning tracers and time-lapse bulk electrical conductivity measurements. The theoretical development includes the partitioning chemistry for the tracers we demonstrate (ammonia and carbon dioxide), as well as a review of the petrophysical relationship governing how these tracers influence bulk conductivity. We also investigate methodsmore » of utilizing secondary information provided by electrical conductivity breakthrough magnitudes induced by the tracers. We test the method on clean, well characterized, intermediate-scale sand columns under controlled conditions. Results demonstrate the capability to predict partitioning coefficients and accurately monitor gas breakthrough curves along the length of the column according to the corresponding electrical conductivity response, leading to accurate water saturation estimates. This work is motivated by the need to develop effective characterization and monitoring techniques for contaminated deep vadose zone environments, and provides a proof-of-concept toward uniquely characterizing and monitoring water saturation levels at the field scale and in three-dimensions using electrical resistivity tomography.« less

Electric currents in F-like planetary ionospheres

NASA Technical Reports Server (NTRS)

Cole, K. D.

1990-01-01

In this paper, electrical transport coefficients are found for charged particles in such lightly ionized gases as exist in planetary and stellar atmospheres, like the F-region of the earth's ionosphere. Electric fields and gradients of pressure in the ions and the electrons are taken as the drivers of electric current. Collisions of electrons with ions, and of ions and electrons with neutral particles, are taken into account, and new expressions are generated for electrical conductivity, heating rates, and diffusion of magnetic field. The paper extends and complements the results of an earlier paper by Cole (1990) which dealt with 'E-like' ionospheric regions. A comparison of the results with those of kinetic theory is made.

Thermoelectric Properties of Poly(selenophene- co-3, 4-ethylenedioxythiophene) via Electropolymerization

NASA Astrophysics Data System (ADS)

Gu, Hua; Ming, Shouli; Lin, Kaiwen; Liu, Hongtao; Chen, Shuai; Lu, Baoyang; Xu, Jingkun

2017-05-01

Conducting polymers as thermoelectric (TE) materials have drawn extensive attention most recently because they are intrinsically light weight, flexible, highly processable, abundant in nature, and have especially low thermal conductivity. Relative studies have been focused on several typical structures such as polyacetylene, polyaniline, polythiophenes. However, TE performance of polyselenophenes have drawn very little attention because of its unstability and difficulty in synthesis. Previously, our group demonstrated that polyselenophene revealed high Seebeck coefficient (>180 μV K-1), but their electrical conductivity was very low (typically 10-5-10-2 S cm-1). For the sake of improving the thermoelectric performance of polyselenophene, the simplest and most effective method is to copolymerize with other high-performance thermoelectric materials. Herein, 3,4-ethylenedioxythiophene (EDOT), the monomer precursor of poly(3,4-ethylenedioxythiophene) (probably the best organic thermoelectric materials so far) was chosen to copolymerize with selenophene (SE) under different feeding ratios via electropolymerization to improve the thermoelectric performance. It is found that the electrical conductivity of all the copolymer films was obviously enhanced with the highest value of 0.91 S cm-1 by inserting EDOT in the conjugated block, whereas their Seebeck coefficient was brought down to 12 μV K-1. In this work, We obtained four different feeding ratios copolymers of SE and EDOT, 2:1 (PA), 1:1 (PB), 1:2 (PC), and 1:5 (PD). The copolymers had improved electrical conductivity and environmental stability compared with polyselenophene. Furthermore, with increasing the feeding ratio of EDOT, the TE performance of the copolymers was significantly improved.

Structural, electrical, optical and magneto-electric characteristics of chemically synthesized CaCu3Ti4O12 dielectric ceramics

NASA Astrophysics Data System (ADS)

Parida, Kalpana; Choudhary, R. N. P.

2017-07-01

CaCu3Ti4O12 (CCTO) was prepared by a chemical reaction method. The pellets prepared from the calcined powder of the material were sintered at 1100 °C. Analysis of x-ray diffraction pattern, recorded on CCTO powder, confirms the phase formation of CCTO. Studies of dielectric (ɛ r, tanδ) and impedance parameters using dielectric and impedance spectroscopy of the compound have provided information about the electrical properties and the dielectric relaxation mechanism of the material. Detailed studies on the variation of electrical conductivity (dc) with temperature show semi-conducting nature of the material. Study of frequency (of applied electric field) dependence of ac conductivity at different temperatures suggests that the compound follows the Jonscher’s power law. Complex impedance spectroscopic analysis suggests that the semicircles formed in the Nyquist plot are connected to the grains, grain boundary and interface effects. An optical energy band gap of ~1.9 eV is obtained from the UV-visible absorbance spectrum. The magnetic data related to magneto-electric (ME) coefficient, measured by varying dc bias magnetic field, have been obtained at room temperature.

Electrical and thermal transport properties of layered Bi2YO4Cu2Se2

NASA Astrophysics Data System (ADS)

Xiao, Yu; Pei, Yanling; Chang, Cheng; Zhang, Xiao; Tan, Xing; Ye, Xinxin; Gong, Shengkai; Lin, Yuanhua; He, Jiaqing; Zhao, Li-Dong

2016-07-01

Bi2YO4Cu2Se2 possesses a low thermal conductivity and high electrical conductivity at room temperature, which was considered as a potential thermoelectric material. In this work, we have investigated the electrical and thermal transport properties of Bi2YO4Cu2Se2 system in the temperature range from 300 K to 873 K. We found that the total thermal conductivity decreases from 1.8 W m-1 K-1 to 0.9 W m-1 K-1, and the electrical conductivity decreases from 850 S/cm to 163 S/cm in the measured temperature range. To investigate how potential of Bi2YO4Cu2Se2 system, we prepared the heavily Iodine doped samples to counter-dope intrinsically high carrier concentration and improve the electrical transport properties. Interestingly, the Seebeck coefficient could be enhanced to +80 μV/K at 873 K, meanwhile, we found that a low thermal conductivity of 0.7 W m-1 K-1 could be achieved. The intrinsically low thermal conductivity in this system is related to the low elastic properties, such as Young's modulus of 70-72 GPa, and Grüneisen parameters of 1.55-1.71. The low thermal conductivity makes Bi2YO4Cu2Se2 system to be a potential thermoelectric material, the ZT value 0.06 at 873 K was obtained, a higher performance is expected by optimizing electrical transport properties through selecting suitable dopants, modifying band structures or by further reducing thermal conductivity through nanostructuring etc.

Electronic transport properties of intermediately coupled superconductors: PdTe2 and Cu0.04PdTe2

NASA Astrophysics Data System (ADS)

Hooda, M. K.; Yadav, C. S.

2018-01-01

We have investigated the electrical resistivity (1.8-480 K), Seebeck coefficient (2.5-300 K) and thermal conductivity (2.5-300 K) of PdTe2 and 4% Cu intercalated PdTe2 compounds. The electrical resistivity for the compounds shows a Bloch-Gruneisen-type linear temperature (T) dependence for 100 \\text{K}, and Fermi liquid behavior (ρ (T) \\propto T2) for T<50 \\text{K} . Seebeck coefficient data exhibit a strong competition between Normal (N) and Umklapp (U) scattering processes at low T. The low-T, thermal conductivity (κ) of the compounds is strongly dominated by the electronic contribution, and exhibits a rare linear T-dependence below 10 K. However, high-T, κ (T) shows the usual 1/T -dependence, dominated by the U-scattering process. The electron-phonon coupling parameters, estimated from the low-T, specific-heat data and first-principle electronic structure calculations suggest that PdTe2 and Cu0.04PdTe2 are intermediately coupled superconductors.

Effects of copper vapour on thermophysical properties of CO2-N2 plasma

NASA Astrophysics Data System (ADS)

Zhong, Linlin; Wang, Xiaohua; Rong, Mingzhe; Cressault, Yann

2016-10-01

CO2-N2 mixtures are often used as arc quenching medium (to replace SF6) in circuit breakers and shielding gas in arc welding. In such applications, copper vapour resulting from electrode surfaces can modify characteristics of plasmas. This paper therefore presents an investigation of the effects of copper on thermophysical properties of CO2-N2 plasma. The equilibrium compositions, thermodynamic properties (including mass density, specific enthalpy, and specific heat), transport coefficients (including electrical conductivity, viscosity, and thermal conductivity), and four kinds of combined diffusion coefficients due to composition gradients, applied electric fields, temperature gradients, and pressure gradients respectively, were calculated and discussed for CO2-N2 (mixing ratio 7:3) plasma contaminated by different proportions of copper vapour. The significant influences of copper were observed on all the properties of CO2-N2-Cu mixtures. The better ionization ability and larger molar mass of copper and larger collision integrals related to copper, should be responsible for such influences.

Enhanced thermoelectric transport in modulation-doped GaN/AlGaN core/shell nanowires.

PubMed

Song, Erdong; Li, Qiming; Swartzentruber, Brian; Pan, Wei; Wang, George T; Martinez, Julio A

2016-01-08

The thermoelectric properties of unintentionally n-doped core GaN/AlGaN core/shell N-face nanowires are reported. We found that the temperature dependence of the electrical conductivity is consistent with thermally activated carriers with two distinctive donor energies. The Seebeck coefficient of GaN/AlGaN nanowires is more than twice as large as that for the GaN nanowires alone. However, an outer layer of GaN deposited onto the GaN/AlGaN core/shell nanowires decreases the Seebeck coefficient at room temperature, while the temperature dependence of the electrical conductivity remains the same. We attribute these observations to the formation of an electron gas channel within the heavily-doped GaN core of the GaN/AlGaN nanowires. The room-temperature thermoelectric power factor for the GaN/AlGaN nanowires can be four times higher than the GaN nanowires. Selective doping in bandgap engineered core/shell nanowires is proposed for enhancing the thermoelectric power.

Large thermoelectric power factor from crystal symmetry-protected non-bonding orbital in half-Heuslers.

PubMed

Zhou, Jiawei; Zhu, Hangtian; Liu, Te-Huan; Song, Qichen; He, Ran; Mao, Jun; Liu, Zihang; Ren, Wuyang; Liao, Bolin; Singh, David J; Ren, Zhifeng; Chen, Gang

2018-04-30

Modern society relies on high charge mobility for efficient energy production and fast information technologies. The power factor of a material-the combination of electrical conductivity and Seebeck coefficient-measures its ability to extract electrical power from temperature differences. Recent advancements in thermoelectric materials have achieved enhanced Seebeck coefficient by manipulating the electronic band structure. However, this approach generally applies at relatively low conductivities, preventing the realization of exceptionally high-power factors. In contrast, half-Heusler semiconductors have been shown to break through that barrier in a way that could not be explained. Here, we show that symmetry-protected orbital interactions can steer electron-acoustic phonon interactions towards high mobility. This high-mobility regime enables large power factors in half-Heuslers, well above the maximum measured values. We anticipate that our understanding will spark new routes to search for better thermoelectric materials, and to discover high electron mobility semiconductors for electronic and photonic applications.

Thermoelectric properties of nanostructured porous silicon

NASA Astrophysics Data System (ADS)

Martín-Palma, R. J.; Cabrera, H.; Martín-Adrados, B.; Korte, D.; Pérez-Cappe, E.; Mosqueda, Y.; Frutis, M. A.; Danguillecourt, E.

2018-01-01

In this work we report on the thermoelectric properties of nanostructured porous silicon (nanoPS) layers grown onto silicon substrates. More specifically, nanoPS layers of different porosity, nanocrystal size, and thickness were fabricated and their electrical conductivities, Seebeck coefficients, and thermal conductivities were subsequently measured. It was found that these parameters show a strong dependence on the characteristics of the nanoPS layers and thus can be controlled.

Computational modeling and analysis of thermoelectric properties of nanoporous silicon

DOE Office of Scientific and Technical Information (OSTI.GOV)

Li, H.; Yu, Y.; Li, G., E-mail: gli@clemson.edu

2014-03-28

In this paper, thermoelectric properties of nanoporous silicon are modeled and studied by using a computational approach. The computational approach combines a quantum non-equilibrium Green's function (NEGF) coupled with the Poisson equation for electrical transport analysis, a phonon Boltzmann transport equation (BTE) for phonon thermal transport analysis and the Wiedemann-Franz law for calculating the electronic thermal conductivity. By solving the NEGF/Poisson equations self-consistently using a finite difference method, the electrical conductivity σ and Seebeck coefficient S of the material are numerically computed. The BTE is solved by using a finite volume method to obtain the phonon thermal conductivity k{sub p}more » and the Wiedemann-Franz law is used to obtain the electronic thermal conductivity k{sub e}. The figure of merit of nanoporous silicon is calculated by ZT=S{sup 2}σT/(k{sub p}+k{sub e}). The effects of doping density, porosity, temperature, and nanopore size on thermoelectric properties of nanoporous silicon are investigated. It is confirmed that nanoporous silicon has significantly higher thermoelectric energy conversion efficiency than its nonporous counterpart. Specifically, this study shows that, with a n-type doping density of 10{sup 20} cm{sup –3}, a porosity of 36% and nanopore size of 3 nm × 3 nm, the figure of merit ZT can reach 0.32 at 600 K. The results also show that the degradation of electrical conductivity of nanoporous Si due to the inclusion of nanopores is compensated by the large reduction in the phonon thermal conductivity and increase of absolute value of the Seebeck coefficient, resulting in a significantly improved ZT.« less

Study on the Lattice Dynamics of the Argyrodite Ag8GeTe6

NASA Astrophysics Data System (ADS)

Hitchcock, Dale; Thompson, Emily; He, Jian; Bredesen, Isaac; Keppends, Veelre; Mandrus, David

2014-03-01

Ag8GeTe6 was initially studied as a super ionic-electronic mixed conductor in the 1970s, and more recently has attracted new interest for its thermoelectric performance. A key to the desirable thermoelectric performance of Ag8GeTe6 is its exceptionally low lattice thermal conductivity (~ 0.25W/m*K at 300K), which is intimately related to its structure, consecutive structural instabilities, and unusual lattice dynamics (e.g., anharmonicity). In this work, we have studied Ag8GeTe6 by means of thermal conductivity, electrical conductivity, Seebeck coefficient, Hall coefficient, magnetic susceptibility, resonant ultrasound spectroscopy (RUS), photoacoustic spectroscopy, and synchrotron x-ray diffraction at low temperatures in order to further understand the coexistence of mixed conduction and high thermoelectric performance at elevated temperatures. This work is supported by NSF DMR 1307740.

Damping-tunable energy-harvesting vehicle damper with multiple controlled generators: Design, modeling and experiments

NASA Astrophysics Data System (ADS)

Xie, Longhan; Li, Jiehong; Li, Xiaodong; Huang, Ledeng; Cai, Siqi

2018-01-01

Hydraulic dampers are used to decrease the vibration of a vehicle, where vibration energy is dissipated as heat. In addition to resulting in energy waste, the damping coefficient in hydraulic dampers cannot be changed during operation. In this paper, an energy-harvesting vehicle damper was proposed to replace traditional hydraulic dampers. The goal is not only to recover kinetic energy from suspension vibration but also to change the damping coefficient during operation according to road conditions. The energy-harvesting damper consists of multiple generators that are independently controlled by switches. One of these generators connects to a tunable resistor for fine tuning the damping coefficient, while the other generators are connected to a control and rectifying circuit, each of which both regenerates electricity and provides a constant damping coefficient. A mathematical model was built to investigate the performance of the energy-harvesting damper. By controlling the number of switched-on generators and adjusting the value of the external tunable resistor, the damping can be fine tuned according to the requirement. In addition to the capability of damping tuning, the multiple controlled generators can output a significant amount of electricity. A prototype was built to test the energy-harvesting damper design. Experiments on an MTS testing system were conducted, with results that validated the theoretical analysis. Experiments show that changing the number of switched-on generators can obviously tune the damping coefficient of the damper and simultaneously produce considerable electricity.

The enhanced thermoelectric properties of BiMnO3 ceramics by Sr-doped

NASA Astrophysics Data System (ADS)

Yu, X. Y.; Wang, Y.; Peng, J. J.; Wang, B. L.; Wei, K. L.; Liu, J. M.; He, Q. Y.

2018-04-01

A series of Bi1‑xSrxMnO3 (x = 0.40, 0.45, 0.50, 0.55) samples labeled as BSMO040, BSMO045, BSMO050, and BSMO055, respectively, have been fabricated by the modified solid-state reaction method. The crystal structural, microstructures, and chemical states of the elements and the thermoelectric properties were investigated with respect to the partial substitution of Sr2+ for Bi3+. The samples were characterized by x-ray diffraction (XRD) at 723 K, scanning electron microscopy (SEM), and x-ray photoelectron spectroscopy (XPS). Moreover, their electrical conductivities (σ), Seebeck coefficients (S), and thermal conductivities (κ) were determined. All the samples exhibited orthorhombic structure. The partial substitution of Sr2+ for Bi3+ caused valence shift of some Mn ions from +3 to +4 to maintain electric charge balance. The change in electric charge led to an increase in electron concentration, and thus, the electrical conductivity as well as the absolute value of Seebeck coefficient increased. Consequently, the power factor also increased. The highest power factor (0.3 × 10‑4 Wm‑1 K‑1) was obtained for BSMO055 at 1023 K. Moreover, the highest dimensionless figure-of-merit (ZT) obtained in this study was 0.015 for BSMO055 at 1073 K. It can be concluded that the partial substitution of Sr2+ for Bi3+ in the Bi1‑xSrxMnO3 samples (x = 0.40, 0.45, 0.50, and 0.55) improved the thermoelectric properties effectively.

Electric and magnetic field modulated energy dispersion, conductivity and optical response in double quantum wire with spin-orbit interactions

NASA Astrophysics Data System (ADS)

Karaaslan, Y.; Gisi, B.; Sakiroglu, S.; Kasapoglu, E.; Sari, H.; Sokmen, I.

2018-02-01

We study the influence of electric field on the electronic energy band structure, zero-temperature ballistic conductivity and optical properties of double quantum wire. System described by double-well anharmonic confinement potential is exposed to a perpendicular magnetic field and Rashba and Dresselhaus spin-orbit interactions. Numerical results show up that the combined effects of internal and external agents cause the formation of crossing, anticrossing, camel-back/anomaly structures and the lateral, downward/upward shifts in the energy dispersion. The anomalies in the energy subbands give rise to the oscillation patterns in the ballistic conductance, and the energy shifts bring about the shift in the peak positions of optical absorption coefficients and refractive index changes.

Metal-like electrical conductivity in LaxSr2-xTiMoO6 oxides for high temperature thermoelectric power generation.

PubMed

Saxena, Mandvi; Maiti, Tanmoy

2017-05-09

Increasing electrical conductivity in oxides, which are inherently insulators, can be a potential route in developing oxide-based thermoelectric power generators with higher energy conversion efficiency. In the present work, environmentally friendly non-toxic double perovskite La x Sr 2-x TiMoO 6 (LSTM) ceramics were synthesized using a solid-state reaction route by optimizing the sintering temperature and atmosphere for high temperature thermoelectric applications. Rietveld refinement of XRD data confirmed a single-phase solid solution with a cubic structure in these double perovskites with the space-group Pm3[combining macron]m. SEM studies showed a highly dense microstructure in these ceramics. High electrical conductivity on the order of 10 5 S m -1 and large carrier concentration (∼10 22 cm -3 ) were obtained in these materials. The temperature-dependent electrical conductivity measurement showed that the LSTM ceramics exhibit a semiconductor to metal transition. Thermopower (S) measurements demonstrated the conductivity switching from a p-type to n-type behavior at higher temperature. A temperature dependent Seebeck coefficient was further explained using a model for coexistence of both types of charge carriers in these oxides. A conductivity mechanism of these double perovskites was found to be governed by a small polaron hopping model.

Some notes on hydrogen-related point defects and their role in the isotope exchange and electrical conductivity in olivine

NASA Astrophysics Data System (ADS)

Karato, Shun-ichiro

2015-11-01

Nominally anhydrous minerals such as olivine dissolve hydrogen in a variety of forms including free (or interstitial) proton (Hrad) and two protons trapped at the M-site ((2 H)M×). The strength of chemical bonding between protons and the surrounding atoms are different among different species, and consequently protons belonging to different species likely have different mobility (diffusion coefficients). I discuss the role of diffusion of protons in different species in the isotope exchange and hydrogen-assisted electrical conductivity adding a few notes to the previous work by Karato (2013) including a new way to test the model. I conclude that in the case of isotope exchange, the interaction among these species is strong because diffusion is heterogeneous, whereas there is no strong interaction among different species in electrical conduction where diffusion is homogeneous (in an infinite crystal). Consequently, the slowest diffusing species controls the rate of isotope exchange, whereas the fastest diffusing species controls electrical conductivity leading to a different temperature dependence of activation energy and anisotropy. This model explains the differences in the activation energy and anisotropy between isotope diffusion and electrical conductivity, and predicts that the mechanism of electrical conductivity changes with temperature providing an explanation for most of the discrepancies among different experimental observations at different temperatures except for those by Poe et al. (2010) who reported anomalously high water content dependence and highly anisotropic activation energy. When the results obtained at high temperatures are used, most of the geophysically observed high and highly anisotropic electrical conductivity in the asthenosphere can be explained without invoking partial melting.

Power electronics cooling apparatus

DOEpatents

Sanger, Philip Albert; Lindberg, Frank A.; Garcen, Walter

2000-01-01

A semiconductor cooling arrangement wherein a semiconductor is affixed to a thermally and electrically conducting carrier such as by brazing. The coefficient of thermal expansion of the semiconductor and carrier are closely matched to one another so that during operation they will not be overstressed mechanically due to thermal cycling. Electrical connection is made to the semiconductor and carrier, and a porous metal heat exchanger is thermally connected to the carrier. The heat exchanger is positioned within an electrically insulating cooling assembly having cooling oil flowing therethrough. The arrangement is particularly well adapted for the cooling of high power switching elements in a power bridge.

Electrical equivalent circuit for microstrip micro-plasma: control of EM propagation and numerical simulations.

PubMed

Mohamad, Almustafa; Tân-Hoa, Vuong; Jacques, David

2012-01-01

An approach to determine an equivalent electrical circuit of a micro planar discharge on a microstrip printed circuit is reported. The micro discharge is used to realize a dynamic microwave switching circuit. This approach is based on the measurement of the discharge current and the transmission coefficient for a given frequency 2.45 GHz. Numerical methods like FEM can be used to study the effect of plasma parameters on the propagation of electromagnetic waves through a microstrip printed circuit. Plasma behaves as flexible elements that can change its electrical proprieties such as conductivity.

Tunable terahertz optical properties of graphene in dc electric fields

NASA Astrophysics Data System (ADS)

Dong, H. M.; Huang, F.; Xu, W.

2018-03-01

We develop a simple theoretical approach to investigate terahertz (THz) optical properties of monolayer graphene in the presence of an external dc electric field. The analytical results for optical coefficients such as the absorptance and reflectivity are obtained self-consistently on the basis of a diagrammatic self-consistent field theory and a Boltzmann equilibrium equation. It is found that the optical refractive index, reflectivity and conductivity can be effectively tuned by not only a gate voltage but also a driving dc electric field. This study is relevant to the applications of graphene as advanced THz optoelectronic devices.

Fluid transport in partially filled porous sol-gel silica glass

NASA Astrophysics Data System (ADS)

D'orazio, Franco; Bhattacharja, Sankar; Halperin, William P.; Gerhardt, Rosario

1990-10-01

Measurements of low-frequency ac electrical conductivity of a porous glass filled with different amounts of a saline solution are compared with the self-diffusion coefficient of water measured in the same sample, reported previously [F. D'Orazio et al., Phys. Rev. Lett. 63, 43 (1989)]. The two transport parameters are consistently related through the Einstein relation under saturation conditions. A more complex picture is revealed for the unsaturated sample, since the presence of a vapor phase enhances the self-diffusion coefficient. Conductivity experiments allow an independent assessment of the contribution to self-diffusion from the liquid phase. However, a comparison between the two experiments indicates that the role of the vapor phase is not well understood.

The calculation of thermophysical properties of nickel plasma

DOE Office of Scientific and Technical Information (OSTI.GOV)

Apfelbaum, E. M.

2015-09-15

The thermophysical properties of Nickel plasma have been calculated for the temperatures 10–60 kK and densities less than 1 g/cm{sup 3}. These properties are the pressure, internal energy, heat capacity, and the electronic transport coefficients (electrical conductivity, thermal conductivity, and thermal power). The thermodynamic values have been calculated by means of the chemical model, which also allows one to obtain the ionic composition of considered plasma. The composition has been used to calculate the electronic transport coefficients within the relaxation time approximation. The results of the present investigation have been compared with the calculations of other researchers and available data ofmore » measurements.« less

The Synthesis and Thermoelectric Properties of p-Type Li1- x NbO2-Based Compounds

NASA Astrophysics Data System (ADS)

Rahman, Jamil Ur; Meang, Eun-Ji; Van Nguyen, Du; Seo, Won-Seon; Hussain, Ali; Kim, Myong Ho; Lee, Soonil

2017-03-01

We investigated the thermoelectric (TE) properties of a p-type oxide material (Li1- x NbO2, with x = 0-0.6). The composition was synthesized via a solid-state reaction method under a reducing atmosphere. The charge transport properties were determined through the electrical conductivity and Seebeck coefficient measurements. The electrical conductivity was non-monotonically varied with x value and showed metallic behavior with increased temperature and above 650 K temperature independent behavior dominated by extrinsic conduction. On the other hand, the Seebeck coefficient was increased with an increase in the temperature, and decreased gradually with an increase in the Li vacancy concentration by both synthesis and gradual phase transition to a Li-rich Li3NbO4 phase with temperature and appeared as an n-type TE at x = 0.6 under high temperatures, which was attributed to an Nb substitution into the Li site. The thermal conductivity was monotonically reduced with the increase in temperature due to the cation disorder defects and second phases. The Li vacancy induced Li1- x NbO2-based compounds under low oxygen partial pressure show promise as a candidate p-type material for thermoelectric applications, particularly for co-processing with n-type oxide thermoelectric materials fabricated under conditions of low oxygen partial pressure.

Band-like temperature dependence of mobility in a solution-processed organic semiconductor

NASA Astrophysics Data System (ADS)

Sakanoue, Tomo; Sirringhaus, Henning

2010-09-01

The mobility μ of solution-processed organic semiconductorshas improved markedly to room-temperature values of 1-5cm2V-1s-1. In spite of their growing technological importance, the fundamental open question remains whether charges are localized onto individual molecules or exhibit extended-state band conduction like those in inorganic semiconductors. The high bulk mobility of 100cm2V-1s-1 at 10K of some molecular single crystals provides clear evidence that extended-state conduction is possible in van-der-Waals-bonded solids at low temperatures. However, the nature of conduction at room temperature with mobilities close to the Ioffe-Regel limit remains controversial. Here we investigate the origin of an apparent `band-like', negative temperature coefficient of the mobility (dμ/dT<0) in spin-coated films of 6,13-bis(triisopropylsilylethynyl)-pentacene. We use optical spectroscopy of gate-induced charge carriers to show that, at low temperature and small lateral electric field, charges become localized onto individual molecules in shallow trap states, but that a moderate lateral electric field is able to detrap them resulting in highly nonlinear, low-temperature transport. The negative temperature coefficient of the mobility at high fields is not due to extended-state conduction but to localized transport limited by thermal lattice fluctuations.

Band-like temperature dependence of mobility in a solution-processed organic semiconductor.

PubMed

Sakanoue, Tomo; Sirringhaus, Henning

2010-09-01

The mobility mu of solution-processed organic semiconductors has improved markedly to room-temperature values of 1-5 cm(2) V(-1) s(-1). In spite of their growing technological importance, the fundamental open question remains whether charges are localized onto individual molecules or exhibit extended-state band conduction like those in inorganic semiconductors. The high bulk mobility of 100 cm(2) V(-1) s(-1) at 10 K of some molecular single crystals provides clear evidence that extended-state conduction is possible in van-der-Waals-bonded solids at low temperatures. However, the nature of conduction at room temperature with mobilities close to the Ioffe-Regel limit remains controversial. Here we investigate the origin of an apparent 'band-like', negative temperature coefficient of the mobility (dmu/dT<0) in spin-coated films of 6,13-bis(triisopropylsilylethynyl)-pentacene. We use optical spectroscopy of gate-induced charge carriers to show that, at low temperature and small lateral electric field, charges become localized onto individual molecules in shallow trap states, but that a moderate lateral electric field is able to detrap them resulting in highly nonlinear, low-temperature transport. The negative temperature coefficient of the mobility at high fields is not due to extended-state conduction but to localized transport limited by thermal lattice fluctuations.

Enhanced Thermoelectric Performance of n-type Bi2O2Se Ceramics Induced by Ge Doping

NASA Astrophysics Data System (ADS)

Ruleova, P.; Plechacek, T.; Kasparova, J.; Vlcek, M.; Benes, L.; Lostak, P.; Drasar, C.

2018-02-01

Ceramic samples with the composition Bi2- x Ge x O2Se1.01 ( x = 0, 0.05, 0.075, and 0.1) were synthesized by solid-state reaction and compacted using a hot-pressing technique. The prepared materials were characterized by x-ray diffraction analysis, electron microscopy, and measurements of electrical conductivity σ, Seebeck coefficient S, and thermal conductivity in the temperature range 300-780 K. Ge in the Bi2O2Se host structure led to an increase of the free electron concentration compared to pristine Bi2O2Se1.01. The donor effect is attributed to point substitutional defects in the Bi sublattice— {Ge}_{{Bi}}^{ + }, and oxygen vacancies {V}_{{O}}^{ + 2} producing free electrons. As a result, we observe an increase in the electrical conductivity and decrease in Seebeck coefficient while thermal conductivity κ changes slightly. The highest value of the dimensionless figure of merit ZT = σS 2 T/ κ reaches 0.25 for the composition Bi1.95Ge0.05O2Se1.01 at T = 723 K, which is, to date, the highest ZT value reported for Bi2O2Se ceramics. Our results suggest that Bi2O2Se is still worth exploring.

Electrical transport and optical band gap of NiFe2Ox thin films

NASA Astrophysics Data System (ADS)

Bougiatioti, Panagiota; Manos, Orestis; Klewe, Christoph; Meier, Daniel; Teichert, Niclas; Schmalhorst, Jan-Michael; Kuschel, Timo; Reiss, Günter

2017-12-01

We fabricated NiFe2Ox thin films on MgAl2O4(001) by reactive dc magnetron co-sputtering varying the oxygen partial pressure. The fabrication of a material with a variable oxygen deficiency leads to controllable electrical and optical properties which are beneficial for the investigations of the transport phenomena and could, therefore, promote the use of such materials in spintronic and spin caloritronic applications. We used several characterization techniques to investigate the film properties, focusing on their structural, magnetic, electrical, and optical properties. From the electrical resistivity, we obtained the conduction mechanisms that govern the systems in the high and low temperature regimes. We further extracted low thermal activation energies which unveil extrinsic transport mechanisms. The thermal activation energy decreases in the less oxidized samples revealing the pronounced contribution of a large amount of electronic states localized in the band gap to the electrical conductivity. The Hall coefficient is negative and decreases with increasing conductivity as expected for n-type conduction, while the Hall- and the drift mobilities show a large difference. The optical band gaps were determined via ultraviolet-visible spectroscopy. They follow a similar trend as the thermal activation energies, with lower band gap values in the less oxidized samples.

Investigation of Transport Properties of a New Biomaterials - GUM Mangosteen

NASA Astrophysics Data System (ADS)

Pradhan, Sourav S.; Sarkar, A.

2006-06-01

Biomaterial has occupied leading position in material science for various scientific and technological applications. This present work is carried out over a natural gum extracted from raw fruit of Mangosteen, an east Indian tree (Gercinia Mangostana) following extraction and purification process. Solid specimen of the said gum is developed following sol-gel like process. AC and DC electrical analysis on the dried solid specimen of the gum were carried out and showed high electrical conduction with σ ~ 1 E-03 S/cm, of which ionic and electronic contributions are 70% and 30% respectively. Analysis shows that origin of high electrical conductivity is due to presence of substantial amount of organic acid unit in its polysaccharide background. In fact the observed σ is about 1000 times of that observed in gum Arabica. Optical absorption of this new bio- materials are also studied using UV-VIS analysis. The results show its high absorption co-efficient in UV and blue part of analysed range. A complete electrical characterization of the material have been made. It has also been observed that the electronic conduction can be enhanced to 70% of the total electrical conductivity by forming complex with Iodine and organic (Citric) acid from Lemon fruit. This high potential material is being studied for development of electronic device application.

Theoretical examination of effective oxygen diffusion coefficient and electrical conductivity of polymer electrolyte fuel cell porous components

NASA Astrophysics Data System (ADS)

Inoue, Gen; Yokoyama, Kouji; Ooyama, Junpei; Terao, Takeshi; Tokunaga, Tomomi; Kubo, Norio; Kawase, Motoaki

2016-09-01

The reduction of oxygen transfer resistance through porous components consisting of a gas diffusion layer (GDL), microporous layer (MPL), and catalyst layer (CL) is very important to reduce the cost and improve the performance of a PEFC system. This study involves a systematic examination of the relationship between the oxygen transfer resistance of the actual porous components and their three-dimensional structure by direct measurement with FIB-SEM and X-ray CT. Numerical simulations were carried out to model the properties of oxygen transport. Moreover, based on the model structure and theoretical equations, an approach to the design of new structures is proposed. In the case of the GDL, the binder was found to obstruct gas diffusion with a negative effect on performance. The relative diffusion coefficient of the MPL is almost equal to that of the model structure of particle packing. However, that of CL is an order of magnitude less than those of the other two components. Furthermore, an equation expressing the relative diffusion coefficient of each component can be obtained with the function of porosity. The electrical conductivity of MPL, which is lower than that of the carbon black packing, is considered to depend on the contact resistance.

High precision optical measurement of displacement and simultaneous determinations of piezoelectric coefficients

NASA Astrophysics Data System (ADS)

Gamboa, Bryan M.; Malladi, Madhuri; Vadlamani, Ramya; Guo, Ruyan; Bhalla, Amar

2016-09-01

PZT are also well known for their applications in Micro Electrical Mechanical Systems (MEMS). It is necessary to study the piezoelectric coefficients of the materials accurately in order to design a sensor as an example, which defines their strain dependent applications. Systematic study of the electro mechanic displacement measurement was conducted and compared using a white light fiber optic sensor, a heterodyne laser Doppler vibrometer, and a homodyne laser interferometry setup. Frequency dependent measurement is conducted to evaluate displacement values well below and near the piezoelectric resonances. UHF-120 ultra-high frequency Vibrometer is used to measure the longitudinal piezoelectric displacement or x33 and the MTI 2000 FotonicTM Sensor is used to measure the transverse piezoelectric displacement or x11 over 100Hz to 2MHz. A Multiphysics Finite Element Analysis method, COMSOL, is also adopted in the study to generate a three dimensional electromechanical coupled model based on experimentally determined strains x33 and x11 as a function of frequency of the electric field applied. The full family of piezoelectric coefficients of the poled electronic ceramic PZT, d33, d31, and d15, can be then derived, upon satisfactory simulation of the COMSOL. This is achieved without the usual need of preparation of piezoelectric resonators of fundamental longitudinal, transversal, and shear modes respectively.

Molecular dynamics simulation of diffusion and electrical conductivity in montmorillonite interlayers

DOE PAGES

Greathouse, Jeffery A.; Cygan, Randall T.; Fredrich, Joanne T.; ...

2016-01-20

In this study, the diffusion of water and ions in the interlayer region of smectite clay minerals represents a direct probe of the type and strength of clay–fluid interactions. Interlayer diffusion also represents an important link between molecular simulation and macroscopic experiments. Here we use molecular dynamics simulation to investigate trends in cation and water diffusion in montmorillonite interlayers, looking specifically at the effects of layer charge, interlayer cation and cation charge (sodium or calcium), water content, and temperature. For Na-montmorillonite, the largest increase in ion and water diffusion coefficients occurs between the one-layer and two-layer hydrates, corresponding to themore » transition from inner-sphere to outer-sphere surface complexes. Calculated activation energies for ion and water diffusion in Na-montmorillonite are similar to each other and to the water hydrogen bond energy, suggesting the breaking of water–water and water–clay hydrogen bonds as a likely mechanism for interlayer diffusion. A comparison of interlayer diffusion with that of bulk electrolyte solutions reveals a clear trend of decreasing diffusion coefficient with increasing electrolyte concentration, and in most cases the interlayer diffusion results are nearly coincident with the corresponding bulk solutions. Trends in electrical conductivities computed from the ion diffusion coefficients are also compared.« less

Quantitative assessment of passive electrical properties of the cardiac T-tubular system by FRAP microscopy

PubMed Central

Scardigli, M.; Ferrantini, C.; Gabbrielli, T.; Silvestri, L.; Coppini, R.; Tesi, C.; Rog-Zielinska, E. A.; Kohl, P.; Cerbai, E.; Poggesi, C.; Pavone, F. S.; Sacconi, L.

2017-01-01

Well-coordinated activation of all cardiomyocytes must occur on every heartbeat. At the cell level, a complex network of sarcolemmal invaginations, called the transverse-axial tubular system (TATS), propagates membrane potential changes to the cell core, ensuring synchronous and uniform excitation–contraction coupling. Although myocardial conduction of excitation has been widely described, the electrical properties of the TATS remain mostly unknown. Here, we exploit the formal analogy between diffusion and electrical conductivity to link the latter with the diffusional properties of TATS. Fluorescence recovery after photobleaching (FRAP) microscopy is used to probe the diffusion properties of TATS in isolated rat cardiomyocytes: A fluorescent dextran inside TATS lumen is photobleached, and signal recovery by diffusion of unbleached dextran from the extracellular space is monitored. We designed a mathematical model to correlate the time constant of fluorescence recovery with the apparent diffusion coefficient of the fluorescent molecules. Then, apparent diffusion is linked to electrical conductivity and used to evaluate the efficiency of the passive spread of membrane depolarization along TATS. The method is first validated in cells where most TATS elements are acutely detached by osmotic shock and then applied to probe TATS electrical conductivity in failing heart cells. We find that acute and pathological tubular remodeling significantly affect TATS electrical conductivity. This may explain the occurrence of defects in action potential propagation at the level of single T-tubules, recently observed in diseased cardiomyocytes. PMID:28507142

Transport and NMR characteristics of the skutterudite-related compound Ca3Rh4Sn13

NASA Astrophysics Data System (ADS)

Tseng, C. W.; Kuo, C. N.; Li, B. S.; Wang, L. M.; Gippius, A. A.; Kuo, Y. K.; Lue, C. S.

2018-02-01

We report the electronic properties of the Yb3Rh4Sn13-type single crystalline Ca3Rh4Sn13 by means of the electrical resistivity, Hall coefficient, Seebeck coefficient, thermal conductivity, as well as 119Sn nuclear magnetic resonance (NMR) measurements. The negative sign of the Hall coefficient and Seebeck coefficient at low temperatures suggests that the n-type carriers dominate the electrical transport in Ca3Rh4Sn13, in contrast to the observations in Sr3Rh4Sn13 which has a p-type conduction. Such a finding indicates a significant difference in the electronic features between these two stannides. Furthermore, we analyzed the temperature-dependent 119Sn NMR spin-lattice relaxation rate for Ca3Rh4Sn13, (Sr0.7Ca0.3)3Rh4Sn13, and Sr3Rh4Sn13 to examine the change of the electronic Fermi-level density of states (DOS) in (Sr1-xCax)3Rh4Sn13. It indicates that the Sn 5s partial Fermi-level DOS enhances with increasing the Ca content, being consistent with the trend of the superconducting temperature. Since the total Fermi-level DOS usually obeys the same trend of the partial Fermi-level DOS, the NMR analysis provides microscopic evidence for the correlation between the electronic DOS and superconductivity of the (Sr1-xCax)3Rh4Sn13 system.

Apparent isotropic electrical property for electrical brain stimulation (EBS) using magnetic resonance diffusion weighted imaging (MR-DWI)

NASA Astrophysics Data System (ADS)

Lee, Mun Bae; Kwon, Oh-In

2018-04-01

Electrical brain stimulation (EBS) is an invasive electrotherapy and technique used in brain neurological disorders through direct or indirect stimulation using a small electric current. EBS has relied on computational modeling to achieve optimal stimulation effects and investigate the internal activations. Magnetic resonance diffusion weighted imaging (DWI) is commonly useful for diagnosis and investigation of tissue functions in various organs. The apparent diffusion coefficient (ADC) measures the intensity of water diffusion within biological tissues using DWI. By measuring trace ADC and magnetic flux density induced by the EBS, we propose a method to extract electrical properties including the effective extracellular ion-concentration (EEIC) and the apparent isotropic conductivity without any auxiliary additional current injection. First, the internal current density due to EBS is recovered using the measured one component of magnetic flux density. We update the EEIC by introducing a repetitive scheme called the diffusion weighting J-substitution algorithm using the recovered current density and the trace ADC. To verify the proposed method, we study an anesthetized canine brain to visualize electrical properties including electrical current density, effective extracellular ion-concentration, and effective isotropic conductivity by applying electrical stimulation of the brain.

Potentialities of silicon nanowire forests for thermoelectric generation

NASA Astrophysics Data System (ADS)

Dimaggio, Elisabetta; Pennelli, Giovanni

2018-04-01

Silicon is a material with very good thermoelectric properties, with regard to Seebeck coefficient and electrical conductivity. Low thermal conductivities, and hence high thermal to electrical conversion efficiencies, can be achieved in nanostructures, which are smaller than the phonon mean free path but large enough to preserve the electrical conductivity. We demonstrate that it is possible to fabricate a leg of a thermoelectric generator based on large collections of long nanowires, placed perpendicularly to the two faces of a silicon wafer. The process exploits the metal assisted etching technique which is simple, low cost, and can be easily applied to large surfaces. Copper can be deposited by electrodeposition on both faces, so that contacts can be provided, on top of the nanowires. Thermal conductivity of silicon nanowire forests with more than 107 nanowires mm-2 have been measured; the result is comparable with that achieved by several groups on devices based on few nanowires. On the basis of the measured parameters, numerical calculations of the efficiency of silicon-based thermoelectric generators are reported, and the potentialities of these devices for thermal to electrical energy conversion are shown. Criteria to improve the conversion efficiency are suggested and described.

Highly Flexible and Conductive Glycerol-Doped PEDOT:PSS Films Prepared Under an Electric Field

NASA Astrophysics Data System (ADS)

Yamaguchi, Hiroyuki; Aizawa, Kengo; Chonan, Yasunori; Komiyama, Takao; Aoyama, Takashi; Sakai, Eiichi; Qiu, Jianhui; Sato, Naoki

2018-06-01

Poly(3,4-ethylenedioxythiophene):poly(4-styrenesulfonate) (PEDOT:PSS) films doped with several sugar alcohols, viz. xylitol (XL), glycerol (GL), and polyglycerol (PG), at various levels have been synthesized and their thermoelectric properties studied. Among these specimens, 2.5 vol.% GL-doped films showed the best performance with electrical conductivity σ, Seebeck coefficient S, and power factor S 2 σ at room temperature reaching 1040 S/cm, 19 μV/K, and 37 μW/m-K2, respectively. Next, we synthesized films under an electric field E pr for the purpose of crystal growth. GL-doped films showed σ enhancement with increase of E pr. The highest σ value of 1300 S/cm was attained at E pr = 4 kV/cm. S and thermal conductivity κ values were almost independent of E pr. The ZT value was calculated to be between 0.017 and 0.101 at room temperature. We also examined film flexibility. High flexibility was achieved on GL doping, and it was not deteriorated when synthesized under an electric field.

Highly Flexible and Conductive Glycerol-Doped PEDOT:PSS Films Prepared Under an Electric Field

NASA Astrophysics Data System (ADS)

Yamaguchi, Hiroyuki; Aizawa, Kengo; Chonan, Yasunori; Komiyama, Takao; Aoyama, Takashi; Sakai, Eiichi; Qiu, Jianhui; Sato, Naoki

2018-04-01

Poly(3,4-ethylenedioxythiophene):poly(4-styrenesulfonate) (PEDOT:PSS) films doped with several sugar alcohols, viz. xylitol (XL), glycerol (GL), and polyglycerol (PG), at various levels have been synthesized and their thermoelectric properties studied. Among these specimens, 2.5 vol.% GL-doped films showed the best performance with electrical conductivity σ, Seebeck coefficient S, and power factor S 2 σ at room temperature reaching 1040 S/cm, 19 μV/K, and 37 μW/m-K2, respectively. Next, we synthesized films under an electric field E pr for the purpose of crystal growth. GL-doped films showed σ enhancement with increase of E pr. The highest σ value of 1300 S/cm was attained at E pr = 4 kV/cm. S and thermal conductivity κ values were almost independent of E pr. The ZT value was calculated to be between 0.017 and 0.101 at room temperature. We also examined film flexibility. High flexibility was achieved on GL doping, and it was not deteriorated when synthesized under an electric field.

In situ estimation of the effective chemical diffusion coefficient of a rock matrix in a fractured aquifer

USGS Publications Warehouse

Gebrekristos, R.A.; Shapiro, A.M.; Usher, B.H.

2008-01-01

An in situ method of estimating the effective diffusion coefficient for a chemical constituent that diffuses into the primary porosity of a rock is developed by abruptly changing the concentration of the dissolved constituent in a borehole in contact with the rock matrix and monitoring the time-varying concentration. The experiment was conducted in a borehole completed in mudstone on the campus of the University of the Free State in Bloemfontein, South Africa. Numerous tracer tests were conducted at this site, which left a residual concentration of sodium chloride in boreholes that diffused into the rock matrix over a period of years. Fresh water was introduced into a borehole in contact with the mudstone, and the time-varying increase of chloride was observed by monitoring the electrical conductivity (EC) at various depths in the borehole. Estimates of the effective diffusion coefficient were obtained by interpreting measurements of EC over 34 d. The effective diffusion coefficient at a depth of 36 m was approximately 7.8??10-6 m2/d, but was sensitive to the assumed matrix porosity. The formation factor and mass flux for the mudstone were also estimated from the experiment. ?? Springer-Verlag 2007.

Magnetosphere-Ionosphere Coupling and Associated Ring Current Energization Processes

NASA Technical Reports Server (NTRS)

Liemohn, M. W.; Khazanov, G. V.

2004-01-01

Adiabatic processes in the ring current are examined. In particular, an analysis of the factors that parameterize the net adiabatic energy gain in the inner magnetosphere during magnetic storms is presented. A single storm was considered, that of April 17, 2002. Three simulations were conducted with similar boundary conditions but with different electric field descriptions. It is concluded that the best parameter for quantifying the net adiabatic energy gain in the inner magnetosphere during storms is the instantaneous value of the product of the maximum westward electric field at the outer simulation boundary with the nightside plasma sheet density. However, all of the instantaneous magnetospheric quantities considered in this study produced large correlation coefficients. Therefore, they all could be considered useful predictors of the net adiabatic energy gain of the ring current. Long integration times over the parameters lessen the significance of the correlation. Finally, some significant differences exist in the correlation coefficients depending on the electric field description.

Role of temperature and oxygen content on structural and electrical properties of LaBaCo2O5+δ thin films

NASA Astrophysics Data System (ADS)

Mace, Brennan; Harrell, Zach; Chen, Chonglin; Enriquez, Erik; Chen, Aiping; Jia, Quanxi

2018-02-01

The role of temperature and the oxygen content in the structural transformation and electrical conductivity of epitaxial double perovskite LaBaCo2O5+δ (0≤ δ ≤ 1) thin films was systematically investigated. Reciprocal space mapping and ω-2θ x-ray diffraction performed at different temperatures in vacuum indicate that oxygen vacancies in the films become ordered at high temperature in a reducing environment. The changes of the oxygen content and the degree of oxygen vacancy ordering in the films result in a strong in-plane anisotropic lattice deformation and a large thermal expansion coefficient along the c-axis direction. The electrical conductivity measurements reveal that these behaviors are related to the degree of oxygen vacancy formation and lattice deformation in the films.

Role of temperature and oxygen content on structural and electrical properties of LaBaCo2O5+δ thin films.

PubMed

Mace, Brennan; Harrell, Zach; Chen, Chonglin; Enriquez, Erik; Chen, Aiping; Jia, Quanxi

2018-02-12

The role of temperature and the oxygen content in the structural transformation and electrical conductivity of epitaxial double perovskite LaBaCo 2 O 5+δ (0≤ δ ≤ 1) thin films was systematically investigated. Reciprocal space mapping and ω-2θ x-ray diffraction performed at different temperatures in vacuum indicate that oxygen vacancies in the films become ordered at high temperature in a reducing environment. The changes of the oxygen content and the degree of oxygen vacancy ordering in the films result in a strong in-plane anisotropic lattice deformation and a large thermal expansion coefficient along the c-axis direction. The electrical conductivity measurements reveal that these behaviors are related to the degree of oxygen vacancy formation and lattice deformation in the films.

Theory of interparticle correlations in dense, high-temperature plasmas. V - Electric and thermal conductivities

NASA Technical Reports Server (NTRS)

Ichimaru, S.; Tanaka, S.

1985-01-01

Ichimaru et al. (1985) have developed a general theory in which the interparticle correlations in dense, high-temperature multicomponent plasmas were formulated systematically over a wide range of plasma parameters. The present paper is concerned with an extension of this theory, taking into account the problems of the electronic transport in such high-density plasmas. It is shown that the resulting theory is capable of describing the transport coefficients accurately over a wide range of the density and temperature parameters. Attention is given to electric and thermal conductivities, generalized Coulomb logarithms, a comparison of the considered theory with other theories, and a comparison of the theory with experimental results.

Thermoelectric Properties of Hot-Pressed and PECS-Sintered Magnesium-Doped Copper Aluminum Oxide

NASA Astrophysics Data System (ADS)

Liu, Chang; Morelli, Donald T.

2011-05-01

Copper aluminum oxide (CuAlO2) is considered as a potential candidate for thermoelectric applications. Partially magnesium-doped CuAlO2 bulk pellets were fabricated using solid-state reactions, hot-pressing, and pulsed electric current sintering (PECS) techniques. X-ray diffraction and scanning electron microscopy were adopted for structural analysis. High-temperature transport property measurements were performed on hot-pressed samples. Electrical conductivity increased with Mg doping before secondary phases became significant, while the Seebeck coefficient displayed the opposite trend. Thermal conductivity was consistently reduced as the Mg concentration increased. Effects of Mg doping, preparation conditions, and future modification on this material's properties are discussed.

Thermal Conductivity of Diamond Composites

PubMed Central

Kidalov, Sergey V.; Shakhov, Fedor M.

2009-01-01

A major problem challenging specialists in present-day materials sciences is the development of compact, cheap to fabricate heat sinks for electronic devices, primarily for computer processors, semiconductor lasers, high-power microchips, and electronics components. The materials currently used for heat sinks of such devices are aluminum and copper, with thermal conductivities of about 250 W/(m·K) and 400 W/(m·K), respectively. Significantly, the thermal expansion coefficient of metals differs markedly from those of the materials employed in semiconductor electronics (mostly silicon); one should add here the low electrical resistivity metals possess. By contrast, natural single-crystal diamond is known to feature the highest thermal conductivity of all the bulk materials studied thus far, as high as 2,200 W/(m·K). Needless to say, it cannot be applied in heat removal technology because of high cost. Recently, SiC- and AlN-based ceramics have started enjoying wide use as heat sink materials; the thermal conductivity of such composites, however, is inferior to that of metals by nearly a factor two. This prompts a challenging scientific problem to develop diamond-based composites with thermal characteristics superior to those of aluminum and copper, adjustable thermal expansion coefficient, low electrical conductivity and a moderate cost, below that of the natural single-crystal diamond. The present review addresses this problem and appraises the results reached by now in studying the possibility of developing composites in diamond-containing systems with a view of obtaining materials with a high thermal conductivity.

Nanoscale Thermoelectrics: A Study of the Absolute Seebeck Coefficient of Thin Films

NASA Astrophysics Data System (ADS)

Mason, Sarah J.

The worlds demand for energy is ever increasing. Likewise, the environmental impact of climate change due generating that energy through combustion of fossil fuels is increasingly alarming. Due to these factors new sources of renewable energies are constantly being sought out. Thermoelectric devices have the ability to generate clean, renewable, energy out of waste heat. However promising that is, their inefficiency severely inhibits applicability and practical use. The usefulness of a thermoelectric material increases with the dimensionless quantity, ZT, which depends on the Seebeck coefficient and electrical and thermal conductivity. These characteristic material parameters have interdependent energy transport contributions that classically prohibit the optimization of one with out the detriment of another. Encouraging advancements of ZT have occurred in the past ten years due to the decoupling of the thermal and electrical conductivity. Further advancements are necessary in order to produce applicable devices. One auspicious way of decoupling or tuning energy transport properties, is through size reduction to the nanoscale. However, with reduced dimensions come complications in measuring material properties. Measurements of properties such as the Seebeck coefficient, S, are primarily contingent upon the measurement apparatus. The Seebeck coefficient is defined as the amount of voltage generated by a thermal gradient. Measuring a thermally generated voltage by traditional methods gives, the voltage measured as a linear function of the Seebeck coefficient of the leads and of the material being tested divided by the applied thermal gradient. If accurate values of the Seebeck coefficients of the leads are available, simple subtraction provides the answer. This is rarely the case in nanoscale measurement devices with leads exclusively made from thin film materials that do not have well known bulk-like thermopower values. We have developed a technique to directly measure, S, as a function of temperature using a micro-machined thermal isolation platform consisting of a suspended, patterned SiN membrane. By measuring a series of thicknesses of metallic films up to the infinitely thin film limit, in which the electrical resistivity is no longer decreasing with increasing film thickness, but still not at bulk values, along with the effective electron mean free path, we are able to show the contribution of the leads needed to measure this property. Having a comprehensive understanding of the background contribution we are able to determine the absolute Seebeck coefficient of a wide variety of thin films. The nature of the design of the SiN membrane also allows the ability to accurately and directly measure thermal and electrical transport of the thin films yielding a comprehensive measurement of the three quantities that characterize a material's efficiency. This can serve to further the development of thermoelectric materials through precise measurements of the material properties that dictate efficiency.

Extraordinary Off-Stoichiometric Bismuth Telluride for Enhanced n-Type Thermoelectric Power Factor.

PubMed

Park, Kunsu; Ahn, Kyunghan; Cha, Joonil; Lee, Sanghwa; Chae, Sue In; Cho, Sung-Pyo; Ryee, Siheon; Im, Jino; Lee, Jaeki; Park, Su-Dong; Han, Myung Joon; Chung, In; Hyeon, Taeghwan

2016-11-02

Thermoelectrics directly converts waste heat into electricity and is considered a promising means of sustainable energy generation. While most of the recent advances in the enhancement of the thermoelectric figure of merit (ZT) resulted from a decrease in lattice thermal conductivity by nanostructuring, there have been very few attempts to enhance electrical transport properties, i.e., the power factor. Here we use nanochemistry to stabilize bulk bismuth telluride (Bi 2 Te 3 ) that violates phase equilibrium, namely, phase-pure n-type K 0.06 Bi 2 Te 3.18 . Incorporated potassium and tellurium in Bi 2 Te 3 far exceed their solubility limit, inducing simultaneous increase in the electrical conductivity and the Seebeck coefficient along with decrease in the thermal conductivity. Consequently, a high power factor of ∼43 μW cm -1 K -2 and a high ZT > 1.1 at 323 K are achieved. Our current synthetic method can be used to produce a new family of materials with novel physical and chemical characteristics for various applications.

Thermomagnetic phenomena in the mixed state of high temperature superconductors

NASA Technical Reports Server (NTRS)

Meilikhov, E. Z.

1995-01-01

Galvano- and thermomagnetic-phenomena in high temperature superconductors, based on kinetic coefficients, are discussed, along with a connection between the electric field and the heat flow in superconductor mixed state. The relationship that determines the transport coefficients of high temperature superconductors in the mixed state based on Seebeck and Nernst effects is developed. It is shown that this relationship is true for a whole transition region of the resistive mixed state of a superconductor. Peltier, Ettingshausen and Righi-Leduc effects associated with heat conductivity as related to high temperature superconductors are also addressed.

Electronic and Thermoelectric Properties of Ternary Chalcohalide Semiconductors: First Principles Study

NASA Astrophysics Data System (ADS)

Khan, Wilayat; Hussain, Sajjad; Minar, Jan; Azam, Sikander

2018-02-01

Ternary chalcohalides have been widely utilized for different device applications. The thermoelectric properties of SbSI, SbSeI and SbSBr have been investigated by theoretical simulations, and the findings have been performed using BoltzTraP code, based on semi-classical Boltzmann transport theory. In this study, we simulated the electronic structures using the Englo-Vosko generalized gradient approximation employed in the WIEN2k program. From the electronic band structures, we found a combination of light and heavy bands around the Fermi level in the valence band, which strongly affect the effective masses of the carriers. The entire thermoelectric parameters, like the electrical, the electronic part of the thermal conductivities, the Seebeck coefficient and the power factor have been analysed as functions of temperature and chemical potential. The correlation between the effective masses and the thermoelectric properties is also included in the discussion because the effective mass reveals the mobility of the carriers which in turn affect the thermoelectric properties. The substitution of sulfur reveals high electrical conductivity and a smaller Seebeck coefficient based on effective mass leads to the increase in the power factor.

Enhanced thermoelectric transport in modulation-doped GaN/AlGaN core/shell nanowires

DOE Office of Scientific and Technical Information (OSTI.GOV)

Song, Erdong; Li, Qiming; Swartzentruber, Brian

2015-11-25

The thermoelectric properties of unintentionally n-doped core GaN/AlGaN core/shell N-face nanowires are reported. We found that the temperature dependence of the electrical conductivity is consistent with thermally activated carriers with two distinctive donor energies. The Seebeck coefficient of GaN/AlGaN nanowires is more than twice as large as that for the GaN nanowires alone. However, an outer layer of GaN deposited onto the GaN/AlGaN core/shell nanowires decreases the Seebeck coefficient at room temperature, while the temperature dependence of the electrical conductivity remains the same. We attribute these observations to the formation of an electron gas channel within the heavily-doped GaN coremore » of the GaN/AlGaN nanowires. The room-temperature thermoelectric power factor for the GaN/AlGaN nanowires can be four times higher than the GaN nanowires. As a result, selective doping in bandgap engineered core/shell nanowires is proposed for enhancing the thermoelectric power.« less

Characterization of grain boundary conductivity of spin-sprayed ferrites using scanning microwave microscope

DOE Office of Scientific and Technical Information (OSTI.GOV)

Myers, J.; Nicodemus, T.; Zhuang, Y., E-mail: yan.zhuang@wright.edu

2014-05-07

Grain boundary electrical conductivity of ferrite materials has been characterized using scanning microwave microscope. Structural, electrical, and magnetic properties of Fe{sub 3}O{sub 4} spin-sprayed thin films onto glass substrates for different length of growth times were investigated using a scanning microwave microscope, an atomic force microscope, a four-point probe measurement, and a made in house transmission line based magnetic permeameter. The real part of the magnetic permeability shows almost constant between 10 and 300 MHz. As the Fe{sub 3}O{sub 4} film thickness increases, the grain size becomes larger, leading to a higher DC conductivity. However, the loss in the Fe{sub 3}O{submore » 4} films at high frequency does not increase correspondingly. By measuring the reflection coefficient s{sub 11} from the scanning microwave microscope, it turns out that the grain boundaries of the Fe{sub 3}O{sub 4} films exhibit higher electric conductivity than the grains, which contributes loss at radio frequencies. This result will provide guidance for further improvement of low loss ferrite materials for high frequency applications.« less

The stress system generated by an electromagnetic field in a suspension of drops

NASA Technical Reports Server (NTRS)

Erdogan, M. E.

1982-01-01

The stress generated in a suspension of drops in the presence of a uniform electric field and a pure straining motion, taking into account that the magnetohydrodynamic effects are dominant was calculated. It was found that the stress generated in the suspension depended on the direction of the applied electric field, the dielectric constants, the vicosity coefficients, the conductivities, and the permeabilities of fluids inside and outside the drops. The expression of the particle stress shows that for fluids which are good conductors and poor dielectrics, especially for larger drops, magnetohydrodynamic effects end to reduce the dependence on the direction of the applied electric field.

Field-effect modulation of the thermoelectric characteristics of silicon nanowires on plastic substrates.

PubMed

Choi, Jinyong; Jeon, Youngin; Cho, Kyoungah; Kim, Sangsig

2016-12-02

In this study, we demonstrate the substantial enhancement of the thermoelectric power factors of silicon nanowires (SiNWs) on plastic substrates achievable by field-effect modulation. The Seebeck coefficient and electrical conductivity are adjusted by varying the charge carrier concentration via electrical modulation with a gate voltage in the 0 to ±5 range, thus enhancing the power factors from 2.08 to 935 μW K -2 m -1 ) for n-type SiNWs, and from 453 to 944 μW K -2 m -1 ) for p-type SiNWs. The electrically modulated thermoelectric characteristics of SiNWs are analyzed and discussed.

Facile Preparation of Highly Conductive Metal Oxides by Self-Combustion for Solution-Processed Thermoelectric Generators.

PubMed

Kang, Young Hun; Jang, Kwang-Suk; Lee, Changjin; Cho, Song Yun

2016-03-02

Highly conductive indium zinc oxide (IZO) thin films were successfully fabricated via a self-combustion reaction for application in solution-processed thermoelectric devices. Self-combustion efficiently facilitates the conversion of soluble precursors into metal oxides by lowering the required annealing temperature of oxide films, which leads to considerable enhancement of the electrical conductivity of IZO thin films. Such enhanced electrical conductivity induced by exothermic heat from a combustion reaction consequently yields high performance IZO thermoelectric films. In addition, the effect of the composition ratio of In to Zn precursors on the electrical and thermoelectric properties of the IZO thin films was investigated. IZO thin films with a composition ratio of In:Zn = 6:2 at the low annealing temperature of 350 °C showed an enhanced electrical conductivity, Seebeck coefficient, and power factor of 327 S cm(-1), 50.6 μV K(-1), and 83.8 μW m(-1) K(-2), respectively. Moreover, the IZO thin film prepared at an even lower temperature of 300 °C retained a large power factor of 78.7 μW m(-1) K(-2) with an electrical conductivity of 168 S cm(-1). Using the combustive IZO precursor, a thermoelectric generator consisting of 15 legs was fabricated by a printing process. The thermoelectric array generated a thermoelectric voltage of 4.95 mV at a low temperature difference (5 °C). We suggest that the highly conductive IZO thin films by self-combustion may be utilized for fabricating n-type flexible printed thermoelectric devices.

A novel method for effective diffusion coefficient measurement in gas diffusion media of polymer electrolyte fuel cells

NASA Astrophysics Data System (ADS)

Yang, Linlin; Sun, Hai; Fu, Xudong; Wang, Suli; Jiang, Luhua; Sun, Gongquan

2014-07-01

A novel method for measuring effective diffusion coefficient of porous materials is developed. The oxygen concentration gradient is established by an air-breathing proton exchange membrane fuel cell (PEMFC). The porous sample is set in a sample holder located in the cathode plate of the PEMFC. At a given oxygen flux, the effective diffusion coefficients are related to the difference of oxygen concentration across the samples, which can be correlated with the differences of the output voltage of the PEMFC with and without inserting the sample in the cathode plate. Compared to the conventional electrical conductivity method, this method is more reliable for measuring non-wetting samples.

Magnetism, optical, and thermoelectric response of CdFe2O4 by using DFT scheme

NASA Astrophysics Data System (ADS)

Mahmood, Q.; Yaseen, M.; Bhamu, K. C.; Mahmood, Asif; Javed, Y.; Ramay, Shahid M.

2018-03-01

Comparative analysis of electronic, magnetic, optical, and thermoelectric properties of CdFe2O4, calculated by employing PBEsol + mBJ has been done. The PBEsol reveals metallic nature, while TB-mBJ illustrates ferromagnetic semiconducting behavior. The reasons behind the origin of ferromagnetism are explored by observing the exchange, crystal field, and John–Teller energies. The optical nature is investigated by analyzing dielectric constants, refraction, absorption coefficient, reflectivity, and optical conductivity. Finally, thermoelectric properties are elaborated by describing the electrical and thermal conductivities, Seebeck coefficient, and power factor. The strong absorption for the visible energy and high power factor suggest CdFe2O4 as the potential candidate for renewable energy applications.

Effect of 50MeV Li{sup 3+} ion irradiation on structural, optical and electrical properties of amorphous Se{sub 95}Zn{sub 5} thin films

DOE Office of Scientific and Technical Information (OSTI.GOV)

Ahmad, Shabir, E-mail: shaphyjmi@gmail.com; Sethi, Riti; Nasir, Mohd

2015-08-28

Present work focuses on the effect of swift heavy ion (SHI) irradiation of 50MeV Li{sup 3+} ions by varying the fluencies in the range of 1×10{sup 12} to 5×10{sup 13} ions/cm{sup 2} on the morphological, structural, optical and electrical properties of amorphous Se{sub 95}Zn{sub 5} thin films. Thin films of ~250nm thickness were deposited on cleaned glass substrates by thermal evaporation technique. X-ray diffraction (XRD) analysis shows the pristine thin film of Se{sub 95}Zn{sub 5} growsin hexagonal phase structure. Also it was found that the small peak observed in XRD spectra vanishes after SHI irradiation indicates the defects of themore » material increases. The optical parameters: absorption coefficient (α), extinction coefficient (K), refractive index (n) optical band gap (E{sub g}) and Urbach’s energy (E{sub U}) are determined from optical absorption spectra data measured from spectrophotometry in the wavelength range 200-1000nm. It was found that the values of absorption coefficient, refractive index and extinction coefficient increases while the value optical band gap decreases with the increase of ion fluence. This post irradiation change in the optical parameters was interpreted in terms of bond distribution model. Electrical properties such as dc conductivity and temperature dependent photoconductivity of investigated thin films were carried out in the temperature range 309-370 K. Analysis of data shows activation energy of dark current is greater as compared to activation energy photocurrent. The value of activation energy decreases with the increase of ion fluence indicates that the defect density of states increases.Also it was found that the value of dc conductivity and photoconductivity increases with the increase of ion fluence.« less

Variable range hopping electric and thermoelectric transport in anisotropic black phosphorus

DOE PAGES

Liu, Huili; Sung Choe, Hwan; Chen, Yabin; ...

2017-09-05

Black phosphorus (BP) is a layered semiconductor with a high mobility of up to ~1000 cm 2 V -1 s -1 and a narrow bandgap of ~0.3 eV, and shows potential applications in thermoelectrics. In stark contrast to most other layered materials, electrical and thermoelectric properties in the basal plane of BP are highly anisotropic. In order to elucidate the mechanism for such anisotropy, we fabricated BP nanoribbons (~100 nm thick) along the armchair and zigzag directions, and measured the transport properties. It is found that both the electrical conductivity and Seebeck co efficient increase with temperature, a behavior contradictorymore » to that of traditional semiconductors. The three-dimensional variable range hopping model is adopted to analyze this abnormal temperature dependency of electrical conductivity and Seebeck coefficient. Furthermore, the hopping transport of the BP nanoribbons, attributed to high density of trap states in the samples, provides a fundamental understanding of the anisotropic BP for potential thermoelectric applications.« less

Variable range hopping electric and thermoelectric transport in anisotropic black phosphorus

DOE Office of Scientific and Technical Information (OSTI.GOV)

Liu, Huili; Sung Choe, Hwan; Chen, Yabin

Black phosphorus (BP) is a layered semiconductor with a high mobility of up to ~1000 cm 2 V -1 s -1 and a narrow bandgap of ~0.3 eV, and shows potential applications in thermoelectrics. In stark contrast to most other layered materials, electrical and thermoelectric properties in the basal plane of BP are highly anisotropic. In order to elucidate the mechanism for such anisotropy, we fabricated BP nanoribbons (~100 nm thick) along the armchair and zigzag directions, and measured the transport properties. It is found that both the electrical conductivity and Seebeck co efficient increase with temperature, a behavior contradictorymore » to that of traditional semiconductors. The three-dimensional variable range hopping model is adopted to analyze this abnormal temperature dependency of electrical conductivity and Seebeck coefficient. Furthermore, the hopping transport of the BP nanoribbons, attributed to high density of trap states in the samples, provides a fundamental understanding of the anisotropic BP for potential thermoelectric applications.« less

Thermoelectric properties of FeAs based superconductors, with thick perovskite- and Sm-O fluorite-type blocking layers

NASA Astrophysics Data System (ADS)

Singh, S. J.; Shimoyama, J.; Ogino, H.; Kishio, K.

2015-11-01

The transport properties (electrical resistivity, Hall and Seebeck coefficient, and thermal conductivity) of iron based superconductors with thick perovskite-type oxide blocking layers and fluorine-doped SmFeAsO were studied to explore their possible potential for thermoelectric applications. The thermal conductivity of former compounds depicts the dominated role of phonon and its value decreases rapidly below the Tc, suggesting the addition of scattering of phonons. Both the Seebeck coefficient (S) and Hall coefficient (RH) of all samples were negative in the whole temperature region below 300 K, indicating that the major contribution to the normal state conductivity is by electrons. In addition, the profile of S(T) and RH(T) of all samples have similar behaviours as would be expected for a multi-band superconductors. Although the estimated thermoelectric figure of merit (ZT) of these compounds was much lower than that of practically applicable thermoelectric materials, however its improvement can be expected by optimizing microstructure of the polycrystalline materials, such as densification and grain orientation.

Thermophysical properties and rheological behavior of electro-rheological fluids at different temperatures

NASA Astrophysics Data System (ADS)

Korobko, Evguenia V.; Korobko, Yulia O.

2000-04-01

Fluid disperse systems, sensitive to the external electric field-electrorheological fluids, are finding increasing use in various areas of industry and technology. Their physicomechanical, electrophysical characteristics determine the valuable specific properties of the materials with assigned structure, obtainable with everwide use of electric fields, which makes it possible to substantially enhance efficiency and productiveness of technological processes and to improve the control of operational regimes of the equipment which employ fluid disperse media. The present investigations has been undertaken with the aim of studying thermophysical properties and rheophysical behavior of low-concentration ER- fluid (diatomite in transformer oil) at different temperatures. It was shown that the electric field, which changes considerably the structure of electrorheological fluid, influences effective thermal conductivity and diffusivity coefficients. Their increase with electric field intensity and the increase of the effective viscosity with temperature are connected with the increase of the conductive component of the overall heat transfer through the contact spots between the solid particles, and with intensification of electric convection in the spaces between the dispersed particles.

Record figure of merit values of highly stoichiometric Sb 2Te 3 porous bulk synthesized from tailor-made molecular precursors in ionic liquids

DOE PAGES

Heimann, Stefan; Schulz, Stephan; Schaumann, Julian; ...

2015-08-06

We report on the synthesis of Sb 2Te 3 nanoparticles with record-high figure of merit values of up to 1.5. The central thermoelectric parameters, electrical conductivity, thermal conductivity and Seebeck coefficient, were independently optimized. Critical influence of porosity for the fabrication of highly efficient thermoelectric materials is firstly demonstrated, giving a strong guidance for the optimization of other thermoelectric materials.

Significant Enhancement in the Thermoelectric Properties of PEDOT:PSS Films through a Treatment with Organic Solutions of Inorganic Salts.

PubMed

Fan, Zeng; Du, Donghe; Yu, Zhimeng; Li, Pengcheng; Xia, Yijie; Ouyang, Jianyong

2016-09-07

Conducting polymers have promising thermoelectric application because they have many advantages including abundant elements, mechanical flexibility, and nontoxicity. The thermoelectric properties of conducting polymers strongly depend on their chemical structure and microstructure. Here, we report a novel and facile method to significantly enhance the thermoelectric properties of poly(3,4-ethylenedioxythiophene):poly(styrenesulfonate) ( PSS) films through a treatment with organic solutions of inorganic salts. N,N-Dimethylformamide (DMF) and a common inorganic salt like zinc chloride (ZnCl2) are used as the solvent and solute of the solutions, respectively. The treatments can significantly increase both the Seebeck coefficient and electrical conductivity of the PSS films. The thermoelectric properties of the PSS films are sensitive to the experimental conditions, such as the salt concentration, treatment temperature, and the cation of the salts. After treatment at the optimal experimental conditions, the PSS films can exhibit a Seebeck coefficient of 26.1 μV/K and an electrical conductivity of over 1400 S/cm at room temperature. The corresponding power factor is 98.2 μW/(m·K(2)). The mechanism for the enhancement in the thermoelectric properties is attributed to the segregation of some PSSH chains from PSS and the conformation change of PEDOT chains as a result of the synergetic effects of inorganic salts and DMF.

Sol-gel preparation of Ag-silica nanocomposite with high electrical conductivity

NASA Astrophysics Data System (ADS)

Ma, Zhijun; Jiang, Yuwei; Xiao, Huisi; Jiang, Bofan; Zhang, Hao; Peng, Mingying; Dong, Guoping; Yu, Xiang; Yang, Jian

2018-04-01

Sol-gel derived noble-metal-silica nanocomposites are very useful in many applications. Due to relatively low price, higher conductivity, and higher chemical stability of silver (Ag) compared with copper (Cu), Ag-silica has gained much more research interest. However, it remains a significant challenge to realize high loading of Ag content in sol-gel Ag-silica composite with high structural controllability and nanoparticles' dispersity. Different from previous works by using multifunctional silicon alkoxide to anchor metal ions, here we report the synthesis of Ag-silica nanocomposite with high loading of Ag nanoparticles by employing acetonitrile bi-functionally as solvent and metal ions stabilizer. The electrical conductivity of the Ag-silica nanocomposite reached higher than 6800 S/cm. In addition, the Ag-silica nanocomposite could simultaneously possess high electrical conductivity and positive conductivity-temperature coefficient by properly controlling the loading content of Ag. Such behavior is potentially advantageous for high-temperature devices (like phosphoric acid fuel cells) and inhibiting the thermal-induced increase of devices' internal resistance. The strategy proposed here is also compatible with block-copolymer directed self-assembly of mesoporous material, spin-coating of film and electrospinning of nanofiber, making it more charming in various practical applications.

Free-standing nanocomposites with high conductivity and extensibility.

PubMed

Chun, Kyoung-Yong; Kim, Shi Hyeong; Shin, Min Kyoon; Kim, Youn Tae; Spinks, Geoffrey M; Aliev, Ali E; Baughman, Ray H; Kim, Seon Jeong

2013-04-26

The prospect of electronic circuits that are stretchable and bendable promises tantalizing applications such as skin-like electronics, roll-up displays, conformable sensors and actuators, and lightweight solar cells. The preparation of highly conductive and highly extensible materials remains a challenge for mass production applications, such as free-standing films or printable composite inks. Here we present a nanocomposite material consisting of carbon nanotubes, ionic liquid, silver nanoparticles, and polystyrene-polyisoprene-polystyrene having a high electrical conductivity of 3700 S cm(-1) that can be stretched to 288% without permanent damage. The material is prepared as a concentrated dispersion suitable for simple processing into free-standing films. For the unstrained state, the measured thermal conductivity for the electronically conducting elastomeric nanoparticle film is relatively high and shows a non-metallic temperature dependence consistent with phonon transport, while the temperature dependence of electrical resistivity is metallic. We connect an electric fan to a DC power supply using the films to demonstrate their utility as an elastomeric electronic interconnect. The huge strain sensitivity and the very low temperature coefficient of resistivity suggest their applicability as strain sensors, including those that operate directly to control motors and other devices.

Optimizing the thermoelectric performance of graphene nano-ribbons without degrading the electronic properties.

PubMed

Tran, Van-Truong; Saint-Martin, Jérôme; Dollfus, Philippe; Volz, Sebastian

2017-05-24

The enhancement of thermoelectric figure of merit ZT requires to either increase the power factor or reduce the phonon conductance, or even both. In graphene, the high phonon thermal conductivity is the main factor limiting the thermoelectric conversion. The common strategy to enhance ZT is therefore to introduce phonon scatterers to suppress the phonon conductance while retaining high electrical conductance and Seebeck coefficient. Although thermoelectric performance is eventually enhanced, all studies based on this strategy show a significant reduction of the electrical conductance. In this study we demonstrate that appropriate sources of disorder, including isotopes and vacancies at lowest electron density positions, can be used as phonon scatterers to reduce the phonon conductance in graphene ribbons without degrading the electrical conductance, particularly in the low-energy region which is the most important range for device operation. By means of atomistic calculations we show that the natural electronic properties of graphene ribbons can be fully preserved while their thermoelectric efficiency is strongly enhanced. For ribbons of width M = 5 dimer lines, room-temperature ZT is enhanced from less than 0.26 to more than 2.5. This study is likely to set the milestones of a new generation of nano-devices with dual electronic/thermoelectric functionalities.

Structural, Transport and Electrochemical Properties of LiFePO4 Substituted in Lithium and Iron Sublattices (Al, Zr, W, Mn, Co and Ni)

PubMed Central

Molenda, Janina; Kulka, Andrzej; Milewska, Anna; Zając, Wojciech; Świerczek, Konrad

2013-01-01

LiFePO4 is considered to be one of the most promising cathode materials for lithium ion batteries for electric vehicle (EV) application. However, there are still a number of unsolved issues regarding the influence of Li and Fe-site substitution on the physicochemical properties of LiFePO4. This is a review-type article, presenting results of our group, related to the possibility of the chemical modification of phosphoolivine by introduction of cation dopants in Li and Fe sublattices. Along with a synthetic review of previous papers, a large number of new results are included. The possibility of substitution of Li+ by Al3+, Zr4+, W6+ and its influence on the physicochemical properties of LiFePO4 was investigated by means of XRD, SEM/EDS, electrical conductivity and Seebeck coefficient measurements. The range of solid solution formation in Li1−3xAlxFePO4, Li1−4xZrxFePO4 and Li1−6xWxFePO4 materials was found to be very narrow. Transport properties of the synthesized materials were found to be rather weakly dependent on the chemical composition. The battery performance of selected olivines was tested by cyclic voltammetry (CV). In the case of LiFe1−yMyPO4 (M = Mn, Co and Ni), solid solution formation was observed over a large range of y (0 < y ≤ 1). An increase of electrical conductivity for the substitution level y = 0.25 was observed. Electrons of 3d metals other than iron do not contribute to the electrical properties of LiFe1−yMyPO4, and substitution level y > 0.25 leads to considerably lower values of σ. The activated character of electrical conductivity with a rather weak temperature dependence of the Seebeck coefficient suggests a small polaron-type conduction mechanism. The electrochemical properties of LiFe1−yMyPO4 strongly depend on the Fe substitution level. PMID:28809235

Present state of boron-carbon thermoelectric materials

NASA Technical Reports Server (NTRS)

Elsner, N. B.; Reynolds, G. H.

1983-01-01

Boron-carbon p-type thermoelectric materials show promise for use in advanced thermal-to-electric space power conversion systems. Here, recent data on the thermoelectric properties of boron-carbon materials, such as B9C, B13C2, B15C2, and B4C, are reviewed. In particular, attention is given to the effect of the compositional homogeneity and residual impurity content on the Seeback coefficient, electrical resistivity, and thermal conductivity of these materials. The effect of carbon content for a given level of impurity and degree of homogeneity is also discussed.

Composite films of highly ordered Si nanowires embedded in SiGe0.3 for thermoelectric applications

NASA Astrophysics Data System (ADS)

Kikuchi, Akiou; Yao, Akifumi; Mori, Isamu; Ono, Takahito; Samukawa, Seiji

2017-10-01

We fabricated a high-density array of silicon nanowires (SiNWs) with a diameter of 10 nm embedded in silicon germanium (SiGe0.3) to give a composite thin film for thermoelectric device applications. The SiNW array was first fabricated by bio-template mask and neutral beam etching techniques. The SiNW array was then embedded in SiGe0.3 by thermal chemical vapor deposition. The cross-plane thermal conductivity of the SiNW-SiGe0.3 composite film with a thickness of 100 nm was 3.5 ± 0.3 W/mK in the temperature range of 300-350 K. Moreover, the temperature dependences of the in-plane electrical conductivity and in-plane Seebeck coefficient of the SiNW-SiGe0.3 composite were evaluated. The fabricated SiNW-SiGe0.3 composite film displayed a maximum power factor of 1 × 103 W/m K2 (a Seebeck coefficient of 4.8 × 103 μV/K and an electrical conductivity of 4.4 × 103 S/m) at 873 K. The present high-density SiNW array structure represents a new route to realize practical thermoelectric devices using mature Si processes without any rare metals.

Enhancement of thermoelectric performance in strontium titanate by praseodymium substitution

NASA Astrophysics Data System (ADS)

Kovalevsky, A. V.; Yaremchenko, A. A.; Populoh, S.; Weidenkaff, A.; Frade, J. R.

2013-02-01

In order to identify the effects of Pr additions on thermoelectric properties of strontium titanate, crystal structure, electrical and thermal conductivity, and Seebeck coefficient of Sr1-xPrxTiO3 (x = 0.02-0.30) materials were studied at 400 < T < 1180 K under highly reducing atmosphere. The mechanism of electronic transport was found to be similar up to 10% of praseodymium content, where generation of the charge carriers upon substitution resulted in significant increase of the electrical conductivity, moderate decrease in Seebeck coefficient, and general improvement of the power factor. Formation of point defects in the course of substitution led to suppression of the lattice thermal conductivity, whilst the contribution from electronic component was increasing with carrier concentration. Possible formation of layered structures and growing distortion of the perovskite lattice resulted in relatively low thermoelectric performance for Sr0.80Pr0.20TiO3 and Sr0.70Pr0.30TiO3. The maximum dimensionless figure of merit was observed for Sr0.90Pr0.10TiO3 and amounted to ˜0.23 at 670 K and ˜0.34 at 1170 K, close to the values, obtained in similar conditions for the best bulk thermoelectrics, based on rare-earth substituted SrTiO3.

Combination of Carrier Concentration Regulation and High Band Degeneracy for Enhanced Thermoelectric Performance of Cu3SbSe4.

PubMed

Zhang, Dan; Yang, Junyou; Jiang, Qinghui; Zhou, Zhiwei; Li, Xin; Xin, Jiwu; Basit, Abdul; Ren, Yangyang; He, Xu; Chu, Weijing; Hou, Jingdi

2017-08-30

The effect of Al-, Ga-, and In-doping on the thermoelectric (TE) properties of Cu 3 SbSe 4 has been comparatively studied on the basis of theoretical prediction and experimental validation. It is found that tiny Al/Ga/In substitution leads to a great enhancement of electrical conductivity with high carrier concentration and also large Seebeck coefficient due to the preserved high band degeneracy and thereby a remarkably high power factor. Ultimately, coupled with the depressed lattice thermal conductivity, all three elements (Al/Ga/In) substituted samples have obtained a highly improved thermoelectric performance with respect to undoped Cu 3 SbSe 4 . Compared to the samples at the same Al/In doping level, the slightly Ga-doped sample presents better TE performance over the wide temperature range, and the Cu 3 Sb 0.995 Ga 0.005 Se 4 sample presents a record high ZT value of 0.9 among single-doped Cu 3 SbSe 4 at 623 K, which is about 80% higher than that of pristine Cu 3 SbSe 4 . This work offers an alternative approach to boost the TE properties of Cu 3 SbSe 4 by selecting efficient dopant to weaken the coupling between electrical conductivity and Seebeck coefficient.

Inversion of multi-frequency electromagnetic induction data for 3D characterization of hydraulic conductivity

USGS Publications Warehouse

Brosten, Troy R.; Day-Lewis, Frederick D.; Schultz, Gregory M.; Curtis, Gary P.; Lane, John W.

2011-01-01

Electromagnetic induction (EMI) instruments provide rapid, noninvasive, and spatially dense data for characterization of soil and groundwater properties. Data from multi-frequency EMI tools can be inverted to provide quantitative electrical conductivity estimates as a function of depth. In this study, multi-frequency EMI data collected across an abandoned uranium mill site near Naturita, Colorado, USA, are inverted to produce vertical distribution of electrical conductivity (EC) across the site. The relation between measured apparent electrical conductivity (ECa) and hydraulic conductivity (K) is weak (correlation coefficient of 0.20), whereas the correlation between the depth dependent EC obtained from the inversions, and K is sufficiently strong to be used for hydrologic estimation (correlation coefficient of − 0.62). Depth-specific EC values were correlated with co-located K measurements to develop a site-specific ln(EC)–ln(K) relation. This petrophysical relation was applied to produce a spatially detailed map of K across the study area. A synthetic example based on ECa values at the site was used to assess model resolution and correlation loss given variations in depth and/or measurement error. Results from synthetic modeling indicate that optimum correlation with K occurs at ~ 0.5 m followed by a gradual correlation loss of 90% at 2.3 m. These results are consistent with an analysis of depth of investigation (DOI) given the range of frequencies, transmitter–receiver separation, and measurement errors for the field data. DOIs were estimated at 2.0 ± 0.5 m depending on the soil conductivities. A 4-layer model, with varying thicknesses, was used to invert the ECa to maximize available information within the aquifer region for improved correlations with K. Results show improved correlation between K and the corresponding inverted EC at similar depths, underscoring the importance of inversion in using multi-frequency EMI data for hydrologic estimation.

Inversion of multi-frequency electromagnetic induction data for 3D characterization of hydraulic conductivity

USGS Publications Warehouse

Brosten, T.R.; Day-Lewis, F. D.; Schultz, G.M.; Curtis, G.P.; Lane, J.W.

2011-01-01

Electromagnetic induction (EMI) instruments provide rapid, noninvasive, and spatially dense data for characterization of soil and groundwater properties. Data from multi-frequency EMI tools can be inverted to provide quantitative electrical conductivity estimates as a function of depth. In this study, multi-frequency EMI data collected across an abandoned uranium mill site near Naturita, Colorado, USA, are inverted to produce vertical distribution of electrical conductivity (EC) across the site. The relation between measured apparent electrical conductivity (ECa) and hydraulic conductivity (K) is weak (correlation coefficient of 0.20), whereas the correlation between the depth dependent EC obtained from the inversions, and K is sufficiently strong to be used for hydrologic estimation (correlation coefficient of -0.62). Depth-specific EC values were correlated with co-located K measurements to develop a site-specific ln(EC)-ln(K) relation. This petrophysical relation was applied to produce a spatially detailed map of K across the study area. A synthetic example based on ECa values at the site was used to assess model resolution and correlation loss given variations in depth and/or measurement error. Results from synthetic modeling indicate that optimum correlation with K occurs at ~0.5m followed by a gradual correlation loss of 90% at 2.3m. These results are consistent with an analysis of depth of investigation (DOI) given the range of frequencies, transmitter-receiver separation, and measurement errors for the field data. DOIs were estimated at 2.0??0.5m depending on the soil conductivities. A 4-layer model, with varying thicknesses, was used to invert the ECa to maximize available information within the aquifer region for improved correlations with K. Results show improved correlation between K and the corresponding inverted EC at similar depths, underscoring the importance of inversion in using multi-frequency EMI data for hydrologic estimation. ?? 2011.

Rheological and electrical properties used to investigate the coagulation process during sludge treatment.

PubMed

Mortadi, A; El Melouky, A; Chahid, E; Nasrellah, H; Bakasse, M; Zradba, A; Cherkaoui, O; El Moznine, R

2018-01-01

Analyses of rheological properties and electrical conductivity (σ dc ) at direct current have been employed in order to investigate the effects of calcium oxide on the coagulation process during sludge treatment in the textile industry. In this context, rheological and electrical measurements were performed on five samples - one that contained raw sludge and the other four that were prepared from the raw sludge and different amounts of calcium oxide: 2, 3, 4, 5% (w/w). Rheological behavior of these samples was analyzed using the Herschel-Bulkley modified model. The influence of calcium oxide content on the rheological parameters such as infinite viscosity, the yield stress, the consistency coefficient, and the consistency index, are presented and discussed. The impact of the calcium oxide content on pH and conductivity were also examined. Similar behaviors have been seen in the evolution of conductivity and infinite viscosity as a function of the calcium oxide content. These latter characteristics were modeled by an equation using two power laws. This equation was able to fit very well the evolution of electrical conductivity and also the viscosity versus the percentage of calcium oxide to predict the optimal amount of calcium oxide (3%) to achieve the coagulation step during sludge treatment.

Soil salinisation and irrigation management of date palms in a Saharan environment.

PubMed

Haj-Amor, Zied; Ibrahimi, Mohamed-Khaled; Feki, Nissma; Lhomme, Jean-Paul; Bouri, Salem

2016-08-01

The continuance of agricultural production in regions of the world with chronic water shortages depends upon understanding how soil salinity is impacted by irrigation practises such as water salinity, irrigation frequency and amount of irrigation. A two-year field study was conducted in a Saharan oasis of Tunisia (Lazala Oasis) to determine how the soil electrical conductivity was affected by irrigation of date palms with high saline water. The study area lacked a saline shallow water table. Field results indicate that, under current irrigation practises, soil electrical conductivity can build up to levels which exceed the salt tolerance of date palm trees. The effects of irrigation practises on the soil electrical conductivity were also evaluated using model simulations (HYDRUS-1D) of various irrigation regimes with different frequencies, different amounts of added water and different water salinities. The comparison between the simulated and observed results demonstrated that the model gave an acceptable estimation of water and salt dynamics in the soil profile, as indicated by the small values of root mean square error (RMSE) and the high values of the Nash-Sutcliffe model efficiency coefficient (NSE). The simulations demonstrated that, under field conditions without saline shallow groundwater, saline irrigation water can be used to maintain soil electrical conductivity and soil water content at safe levels (soil electrical conductivity <4 dS m(-1) and soil water content >0.04 cm(3) cm(-3)) if frequent irrigations with small amounts of water (90 % of the evapotranspiration requirements) were applied throughout the year.

High-performance thermoelectricity in edge-over-edge zinc-porphyrin molecular wires.

PubMed

Noori, Mohammed; Sadeghi, Hatef; Lambert, Colin J

2017-04-20

If high efficiency organic thermoelectric materials could be identified, then these would open the way to a range of energy harvesting technologies and Peltier coolers using flexible and transparent thin-film materials. We have compared the thermoelectric properties of three zinc porphyrin (ZnP) dimers and a ZnP monomer and found that the "edge-over-edge" dimer formed from stacked ZnP rings possesses a high electrical conductance, negligible phonon thermal conductance and a high Seebeck coefficient of the order of 300 μV K -1 . These combine to yield a predicted room-temperature figure of merit of ZT ≈ 4, which is the highest room-temperature ZT ever reported for a single organic molecule. This high value of ZT is a consequence of the low phonon thermal conductance arising from the stacked nature of the porphyrin rings, which hinders phonon transport through the edge-over-edge molecule and enhances the Seebeck coefficient.

Variational bounds on the temperature distribution

NASA Astrophysics Data System (ADS)

Kalikstein, Kalman; Spruch, Larry; Baider, Alberto

1984-02-01

Upper and lower stationary or variational bounds are obtained for functions which satisfy parabolic linear differential equations. (The error in the bound, that is, the difference between the bound on the function and the function itself, is of second order in the error in the input function, and the error is of known sign.) The method is applicable to a range of functions associated with equalization processes, including heat conduction, mass diffusion, electric conduction, fluid friction, the slowing down of neutrons, and certain limiting forms of the random walk problem, under conditions which are not unduly restrictive: in heat conduction, for example, we do not allow the thermal coefficients or the boundary conditions to depend upon the temperature, but the thermal coefficients can be functions of space and time and the geometry is unrestricted. The variational bounds follow from a maximum principle obeyed by the solutions of these equations.

The electric and thermoelectric properties of Cu(II)-Schiff base nano-complexes

NASA Astrophysics Data System (ADS)

Ibrahim, E. M. M.; Abdel-Rahman, Laila H.; Abu-Dief, Ahmed M.; Elshafaie, A.; Hamdan, Samar Kamel; Ahmed, A. M.

2018-05-01

The physical properties, such as electric and optical properties, of metal-Schiff base complexes have been widely investigated. However, their thermoelectric (TE) properties remain unreported. This work presents Cu(II)-Schiff base complexes as promising materials for TE power generation. Therefore, three Cu(II)-Schiff base complexes (namely, [Cu(C32H22N4O2)].3/2H2O, [Cu(C23H17N4O7Br)], and [Cu(C27H22N4O8)].H2O) have been synthesized in nanosized scale. The electric and TE properties have been studied and comprehensive discussions have been presented to promote the nano-complexes (NCs) practical applications in the field of TE power generation. The electrical measurements confirm that the NCs are semiconductors and the electrical conduction process is governed by intermolecular and intramolecular transfer of the charge carriers. The TE measurements reveal that the Cu(II)-Schiff base NCs are nondegenerate P-type semiconductors. The measured Seebeck coefficient values were higher compared to the values reported in previous works for other organic materials indicating that the complexes under study are promising candidates for theremoelectric applications if the electrical conductivity could be enhanced.

Electronic transport coefficients in plasmas using an effective energy-dependent electron-ion collision-frequency

NASA Astrophysics Data System (ADS)

Faussurier, G.; Blancard, C.; Combis, P.; Decoster, A.; Videau, L.

2017-10-01

We present a model to calculate the electrical and thermal electronic conductivities in plasmas using the Chester-Thellung-Kubo-Greenwood approach coupled with the Kramers approximation. The divergence in photon energy at low values is eliminated using a regularization scheme with an effective energy-dependent electron-ion collision-frequency. Doing so, we interpolate smoothly between the Drude-like and the Spitzer-like regularizations. The model still satisfies the well-known sum rule over the electrical conductivity. Such kind of approximation is also naturally extended to the average-atom model. A particular attention is paid to the Lorenz number. Its nondegenerate and degenerate limits are given and the transition towards the Drude-like limit is proved in the Kramers approximation.

Effects of Mn Substitution on the Thermoelectric Properties and Thermal Excitations of the Electron-doped Perovskite Sr1-xLaxTiO3

NASA Astrophysics Data System (ADS)

Okuda, Tetsuji; Hata, Hiroto; Eto, Takahiro; Sobaru, Shogo; Oda, Ryosuke; Kaji, Hiroki; Nishina, Kousuke; Kuwahara, Hideki; Nakamura, Mitsutaka; Kajimoto, Ryoichi

2016-09-01

We studied how Mn substitution affects the thermoelectric properties and thermal excitations of the electron-doped perovskite Sr1-xLaxTiO3 by measuring its electrical and thermal transport properties, magnetization, specific heat, and inelastic neutron scattering. Slight Mn substitution with the lattice defects enhanced the Seebeck coefficient, perhaps because of coupling between itinerant electrons and localized spins or between itinerant electrons and local lattice distortion around Mn3+ ions, while it enhanced anharmonic lattice vibrations, which effectively suppressed thermal conductivity in a state of high electrical conductivity. Consequently, slight Mn substitution increased the dimensionless thermoelectric figure of merit for Sr1-xLaxTiO3 near room temperature.

Electrical resistivity characterization of anisotropy in the Biscayne Aquifer.

PubMed

Yeboah-Forson, Albert; Whitman, Dean

2014-01-01

Electrical anisotropy occurs when electric current flow varies with azimuth. In porous media, this may correspond to anisotropy in the hydraulic conductivity resulting from sedimentary fabric, fractures, or dissolution. In this study, a 28-electrode resistivity imaging system was used to investigate electrical anisotropy at 13 sites in the Biscayne Aquifer of SE Florida using the rotated square array method. The measured coefficient of electrical anisotropy generally ranged from 1.01 to 1.12 with values as high as 1.36 found at one site. The observed electrical anisotropy was used to estimate hydraulic anisotropy (ratio of maximum to minimum hydraulic conductivity) which ranged from 1.18 to 2.83. The largest values generally were located on the Atlantic Coastal Ridge while the lowest values were in low elevation areas on the margin of the Everglades to the west. The higher values of anisotropy found on the ridge may be due to increased dissolution rates of the oolitic facies of the Miami formation limestone compared with the bryozoan facies to the west. The predominate trend of minimum resistivity and maximum hydraulic conductivity was E-W/SE-NW beneath the ridge and E-W/SW-NE farther west. The anisotropy directions are similar to the predevelopment groundwater flow direction as indicated in published studies. This suggests that the observed anisotropy is related to the paleo-groundwater flow in the Biscayne Aquifer. © 2013, National Ground Water Association.

Application of electrical and electromagnetic depth sounding in highly conductive sediments: The concept of vertical electrical anisotropy

NASA Astrophysics Data System (ADS)

Köhler, A.; Bahr, K.

2010-12-01

“Nördlinger Ries” is a meteorite crater in the Bavarian ‘Alb’ of Germany that was formed 15 million years ago, and subsequently filled with salty water. Evaporation resulted in an approximately 300 meter thick layer of young, highly conductive sediments. Audio-frequency Magnetotelluric (AMT) and geoelectric depth sounding (VES) techniques were used to analyze the electrical properties of these sediments. The apparent resistivities measured by the two methods are different, which can be explained by vertical electrical anisotropy (horizontal layering). Applying a joint forward modelling technique with resistivity variations found by a Monte Carlo method results in a best fit model containing a large number of layers, while separate inversions of the two data sets yield 3-layer models. Comparisons of the coefficient of anisotropy with drilling core samples demonstrate the reliability of the results. One difficulty of the AMT method is the low signal-to-noise ratio, because of the source’s deadband. Some suggestions for an “intelligent” processing are presented. Kerch (this session) is employing the result of the integrated conductivity as an input for 3D modelling of collected MT data.

Electrical conductivity and dielectric behavior in sodium zinc divanadates

NASA Astrophysics Data System (ADS)

Sallemi, F.; Louati, B.; Guidara, K.

2014-11-01

The Na2ZnV2O7 compound was obtained by the conventional solid-state reaction. The sample was characterized by X-ray powder diffraction, Raman and impedance spectroscopy. The ac electrical conductivity and dielectric properties have been investigated in the frequency and temperature range of 200 Hz-1 MHz and 513 K-729 K, respectively. The direct current conductivity process is thermally activated. The frequency dependence of the conductivity is interpreted using the power law. The close values of activation energies obtained from the analysis of hopping frequency and dc conductivity implies that the transport is due to Na+ cation displacement parallel to (0 0 1) plane located between ZnO4 and VO4 tetrahedra. The evolution of the complex permittivity as a function of angular frequency was investigated. Several important parameters such as charge carrier concentration, ionic mobility and diffusion coefficient were determined. Thermodynamic parameters such as the free energy of activation ∆F, the enthalpy ∆H, and the change in entropy ∆S have been calculated.

Flexible and reversibly deformable radio-frequency antenna based on stretchable SWCNTs/PANI/Lycra conductive fabric

NASA Astrophysics Data System (ADS)

Guo, Xiaohui; Huang, Ying; Wu, Can; Mao, Leidong; Wang, Yue; Xie, Zhicheng; Liu, Caixia; Zhang, Yugang

2017-10-01

We demonstrated a flexible and reversibly deformable radio-frequency antenna based on SWCNTs/PANI/Lycra conductive fabric and semipermeable film for wireless wearable communications applications. The conductive fabric fabricated by using the ‘dip and dry’ process exhibits good flexibility, electrical stability, stretchability and mechanical properties, and a high electrical conductivity (with low sheet resistance of ˜35 Ω/sq) was obtained based on the SWCNTs/PANI synergistic conductive network. The morphology of the semipermeable film was investigated to further illustrate the waterproof breathable features. Meanwhile, the modeling, fabrication procedure and radiating properties of the radio-frequency textile antenna worked at 2.45 GHz were systematically illustrated. The measured reflection coefficient, VSWR and the -10 dB bandwidth is ˜-18.6 dB, 1.58 and ˜270 MHz respectively, which agreed well with the simulation results. Furthermore, the results indicate that the design methodology for the radio-frequency textile antenna could have promising applications in flexible and reversibly deformable antennas for wearable wireless communications systems.

Enhanced Thermoelectric Properties of Polycrystalline SnSe via LaCl₃ Doping.

PubMed

Li, Fu; Wang, Wenting; Ge, Zhen-Hua; Zheng, Zhuanghao; Luo, Jingting; Fan, Ping; Li, Bo

2018-01-28

LaCl₃ doped polycrystalline SnSe was synthesized by combining mechanical alloying (MA) process with spark plasma sintering (SPS). It is found that the electrical conductivity is enhanced after doping due to the increased carrier concentration and carrier mobility, resulting in optimization of the power factor at 750 K combing with a large Seebeck coefficient over 300 Μvk -1 . Meanwhile, all the samples exhibit lower thermal conductivity below 1.0 W/mK in the whole measured temperature. The lattice thermal conductivity for the doped samples was reduced, which effectively suppressed the increscent of the total thermal conductivity because of the improved electrical conductivity. As a result, a ZT value of 0.55 has been achieved for the composition of SnSe-1.0 wt % LaCl₃ at 750 K, which is nearly four times higher than the undoped one and reveals that rare earth element is an effective dopant for optimization of the thermoelectric properties of SnSe.

Determination of equilibrium electron temperature and times using an electron swarm model with BOLSIG+ calculated collision frequencies and rate coefficients

DOE PAGES

Pusateri, Elise N.; Morris, Heidi E.; Nelson, Eric M.; ...

2015-08-04

Electromagnetic pulse (EMP) events produce low-energy conduction electrons from Compton electron or photoelectron ionizations with air. It is important to understand how conduction electrons interact with air in order to accurately predict EMP evolution and propagation. An electron swarm model can be used to monitor the time evolution of conduction electrons in an environment characterized by electric field and pressure. Here a swarm model is developed that is based on the coupled ordinary differential equations (ODEs) described by Higgins et al. (1973), hereinafter HLO. The ODEs characterize the swarm electric field, electron temperature, electron number density, and drift velocity. Importantmore » swarm parameters, the momentum transfer collision frequency, energy transfer collision frequency, and ionization rate, are calculated and compared to the previously reported fitted functions given in HLO. These swarm parameters are found using BOLSIG+, a two term Boltzmann solver developed by Hagelaar and Pitchford (2005), which utilizes updated cross sections from the LXcat website created by Pancheshnyi et al. (2012). We validate the swarm model by comparing to experimental effective ionization coefficient data in Dutton (1975) and drift velocity data in Ruiz-Vargas et al. (2010). In addition, we report on electron equilibrium temperatures and times for a uniform electric field of 1 StatV/cm for atmospheric heights from 0 to 40 km. We show that the equilibrium temperature and time are sensitive to the modifications in the collision frequencies and ionization rate based on the updated electron interaction cross sections.« less

Ion beam irradiation effect on thermoelectric properties of Bi2Te3 and Sb2Te3 thin films

NASA Astrophysics Data System (ADS)

Fu, Gaosheng; Zuo, Lei; Lian, Jie; Wang, Yongqiang; Chen, Jie; Longtin, Jon; Xiao, Zhigang

2015-09-01

Thermoelectric energy harvesting is a very promising application in nuclear power plants for self-maintained wireless sensors. However, the effects of intensive radiation on the performance of thermoelectric materials under relevant reactor environments such as energetic neutrons are not fully understood. In this work, radiation effects of bismuth telluride (Bi2Te3) and antimony telluride (Sb2Te3) thermoelectric thin film samples prepared by E-beam evaporation are investigated using Ne2+ ion irradiations at different fluences of 5 × 1014, 1015, 5 × 1015 and 1016 ions/cm2 with the focus on the transport and structural properties. Electrical conductivities, Seebeck coefficients and power factors are characterized as ion fluence changes. X-ray diffraction (XRD) and transmission electron microscopy (TEM) of the samples are obtained to assess how phase and microstructure influence the transport properties. Carrier concentration and Hall mobility are obtained from Hall effect measurements, which provide further insight into the electrical conductivity and Seebeck coefficient mechanisms. Positive effects of ion irradiations from Ne2+ on thermoelectric material property are observed to increase the power factor to 208% for Bi2Te3 and 337% for Sb2Te3 materials between fluence of 1 and 5 × 1015 cm2, due to the increasing of the electrical conductivity as a result of ionization radiation-enhanced crystallinity. However, under a higher fluence, 5 × 1015 cm2 in this case, the power factor starts to decrease accordingly, limiting the enhancements of thermoelectric materials properties under intensive radiation environment.

CaMn(1-x)Nb(x)O3 (x < or = 0.08) perovskite-type phases as promising new high-temperature n-type thermoelectric materials.

PubMed

Bocher, L; Aguirre, M H; Logvinovich, D; Shkabko, A; Robert, R; Trottmann, M; Weidenkaff, A

2008-09-15

Perovskite-type CaMn(1-x)Nb(x)O(3+/-delta) (x = 0.02, 0.05, and 0.08) compounds were synthesized by applying both a "chimie douce" (SC) synthesis and a classical solid state reaction (SSR) method. The crystallographic parameters of the resulting phases were determined from X-ray, electron, and neutron diffraction data. The manganese oxidations states (Mn(4+)/Mn(3+)) were investigated by X-ray photoemission spectroscopy. The orthorhombic CaMn(1-x)Nb(x)O(3+/-delta) (x = 0.02, 0.05, and 0.08) phases were studied in terms of their high-temperature thermoelectric properties (Seebeck coefficient, electrical resistivity, and thermal conductivity). Differences in electrical transport and thermal properties can be correlated with different microstructures obtained by the two synthesis methods. In the high-temperature range, the electron-doped manganate phases exhibit large absolute Seebeck coefficient and low electrical resistivity values, resulting in a high power factor, PF (e.g., for x = 0.05, S(1000K) = -180 microV K(-1), rho(1000K) = 16.8 mohms cm, and PF > 1.90 x 10(-4) W m(-1) K(-2) for 450 K < T < 1070 K). Furthermore, lower thermal conductivity values are achieved for the SC-derived phases (kappa < 1 W m(-1) K(-1)) compared to the SSR compounds. High power factors combined with low thermal conductivity (leading to ZT values > 0.3) make these phases the best perovskitic candidates as n-type polycrystalline thermoelectric materials operating in air at high temperatures.

Measurements of wave velocity and electrical conductivity of an amphibolite from southwestern margin of the Tarim Basin at pressures to 1.0 GPa and temperatures to 700 °C: comparison with field observations

NASA Astrophysics Data System (ADS)

Zhou, Wenge; Fan, Dawei; Liu, Yonggang; Xie, Hongsen

2011-12-01

In situ measurements of elastic wave velocities and electrical conductivities in the three structural directions (normal to foliation Z, perpendicular to lineation in foliation Y and parallel to lineation X) for an amphibolite collected from southwestern margin of the Tarim Basin, northwest China, were carried out in the laboratory. The elastic wave velocity was measured with the combined transmission-reflection method at pressures up to 1.0 GPa (at room temperature) and temperatures up to 700 °C (at 1.0 GPa) and the electrical conductivity was measured with the impedance spectroscopy from 250 to 700 °C at 1.0 GPa. The experimentally determined data included compressional (Vp) and shear wave velocities (Vs), velocity anisotropy (Av), intrinsic pressure and temperature derivatives of Vp and Vs, electrical conductivity (σ), electrical conductivity anisotropy (Aσ) and the parameters of the Arrhenius relationship. Elastic wave velocities increase in the structural directions Z, Y, X, with Vp of 6.63, 6.78 and 6.95 km s-1 and Vs of 3.75, 3.82 and 3.96 km s-1 for Z, Y and X, respectively, at pressure of 1.0 GPa. Elastic wave velocities increase linearly with pressure at room temperature and pressures between 0.25 and 1.0 GPa and decrease linearly with increasing temperature at 1.0 GPa. The pressure coefficients of the sample are in the range of 0.1883-0.2308 km s-1 GPa-1 for Vp and 0.1149-0.1678 km s-1 GPa-1 for Vs. The temperature coefficients are in the range of 2.09-2.35 × 10-4 km s-1 GPa-1 for Vp and 1.28-1.68 × 10-4 km s-1 GPa-1 for Vs. The electrical conductivity increases with increasing temperature, consistent with the Arrhenius relationship. Activation energies for the three structural directions of the amphibolite are in the range of 0.71-0.75 eV. The amphibolite shows velocity anisotropy (4.15-4.86 per cent for Vp and 5.29-5.84 per cent for Vs at 0.25-1.0 GPa) and electrical conductivity anisotropy (11.1-25.2 per cent). Based on the regional crust model and geothermal gradient, velocity and electrical conductivity-depth profiles were calculated for the sample. These profiles were then compared with those derived from seismic reflection/refraction data and from electromagnetic data. Our results showed that the amphibolite sample has Vp and Vs in agreement with those of the middle and lower crust obtained from seismic reflection/refraction data, and σ in accord with that of the lower crust deduced from electromagnetic data. The lower crust of the electromagnetic crust model is roughly equivalent to the middle and lower crust layers of the seismic crust model. Therefore, it is suggest that the amphibolite may be one of the constituents of the present middle and lower crust in the Tarim Basin.

Synthesis and Characterization of Rare-Earth Tellurides and Their Composites For High-Temperature Thermoelectric Applications

NASA Astrophysics Data System (ADS)

Cheikh, Dean

Radioisotope thermoelectric generators (RTGs) are solid-state energy conversion devices and have been a vital power generation technology for deep space missions conducted by the National Aeronautics and Space Administration (NASA). At the heart of these generators are thermoelectric materials that convert heat given off by a radioisotope decay into electricity through the Seebeck effect. While these systems have demonstrated long-term reliability, the current state-of-practice materials have thermoelectric figures of merit, ZT, near 1, leading to low system level efficiencies of 6.5%. The figure of merit is defined as ZT = sigmaS 2/kappa T where sigma, S, kappa, and T are electrical conductivity, Seebeck coefficient, thermal conductivity, and temperature, respectively. Development of higher ZT materials would enable future NASA missions to perform a greater number of scientific experiments and extend mission lifetimes. Lanthanum telluride (La3-xTe4) is a state-of-the-art n-type high-temperature thermoelectric material, with a ZT of 1.1 at 1275 K. It has been demonstrated that the electrical resistivity and Seebeck coefficient of this material can be decoupled when nickel inclusions are added to form a composite. This new phenomenon, known as composite assisted funneling of electrons (CAFE), allows for the resistivity of the composite to decrease while leaving the Seebeck coefficient unaffected when 12-15 vol% nickel was incorporated. The initial work presented in this dissertation focused on microstructural modifications to La3-xTe4-Ni composites to attain a better understanding of the CAFE mechanism. This investigation was conducted by varying the size of the nickel particles compared to what were used in the previous composite study. A 60% increase in ZT to a value of 1.9 at 1200 K for the composites with the smallest Ni particle size was obtained due to an increased Seebeck coefficient and decreased thermal conductivity. The next study focused on the extension of the CAFE effect in La 3-xTe4 to use inclusions other than nickel. Cobalt of a similar size to the nickel in the initial La3-xTe4-Ni composite work was used. A series of La3-xTe4-Co composites were synthesized and their thermoelectric properties characterized. A gradual decrease in resistivity was observed above 8 vol% cobalt, suggesting the CAFE mechanism was occurring. An 18% increase to the Seebeck coefficient was observed between 5-8 vol% cobalt, likely due to contamination on the cobalt powder, altering the carrier concentration of the matrix. The increase to the Seebeck coefficient allowed for a ZT of 1.5 at 1225 K to be achieved at 5 vol% cobalt. The final investigation in this dissertation focused on the synthesis and thermoelectric characterization of praseodymium telluride (Pr3-x Te4). Density functional theory (DFT) calculations predicted a large peak in the density of states (DOS) of Pr3-xTe4 at its Fermi level compared to La3-xTe4, due to the 4ƒ electrons of praseodymium. This change in the band structure was predicted to increase the Seebeck coefficient of Pr3-xTe4 over La3-xTe4. A series of Pr3-xTe4 with varying vacancy concentrations were mechanochemically synthesized and characterized. A 25% improvement in the Seebeck coefficient and 25% decrease in the thermal conductivity compared to La3-xTe4 was observed. The thermoelectric properties were found to optimize at a composition of Pr2.74Te4, reaching a ZT of 1.7 at 1200 K.

Separation of Electric Fields Into Potential and Inductive Parts, and Implications for Radial Diffusion

NASA Astrophysics Data System (ADS)

Chan, A. A.; Ilie, R.; Elkington, S. R.; Albert, J.; Huie, W.

2017-12-01

It has been traditional to separate radiation belt radial-diffusion coefficients into two contributions: an "electrostatic" diffusion coefficient, which is assumed to be due to a potential (non-inductive) electric field, and an "electromagnetic" diffusion coefficient , which is assumed to be due to the combined effect of an inductive electric field and the corresponding time-dependent magnetic field. One difficulty in implementing this separation when using magnetospheric fields obtained from measurements, or from MHD simulations, is that only the total electric field is given; the separation of the electric field into potential and inductive parts is not readily available. In this work we separate the electric field using a numerical method based on the Helmholtz decomposition of the total motional electric field calculated by the BATS-R-US MHD code. The inner boundary for the electric potential is based on the Ridley Ionospheric Model solution and we assume floating boundary conditions in the solar wind. Using different idealized solar wind drivers, including a solar wind density that is oscillating at a single frequency or with a broad spectrum of frequencies, we calculate potential and inductive electric fields, electric and magnetic power spectral densities, and corresponding radial diffusion coefficients. Simulations driven by idealized solar wind conditions show a clear separation of the potential and inductive contributions to the power spectral densities and diffusion coefficients. Simulations with more realistic solar wind drivers are underway to better assess the use of electrostatic and electromagnetic diffusion coefficients in understanding ULF wave-particle interactions in Earth's radiation belts.

Synthesis, thermal expansion and high-temperature electrical conductivity of Co-doped (Y,Ca)FeO{sub 3−δ} with orthorhombic perovskite structure

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kalyuzhnaya, A.S.; Drozhzhin, O.A.; Istomin, S.Ya., E-mail: istomin@icr.chem.msu.ru

Highlights: • (Y,Ca)(Fe,Co)O{sub 3−δ} was prepared via citrate-based route with annealing at 1150–1200 °C. • Y{sub 0.9}Ca{sub 0.1}Fe{sub 0.8}Co{sub 0.2}O{sub 3−δ} demonstrates low thermal expansion coefficient of 11.9 ppm K{sup −1}. • Oxides do not react with YSZ and GDC up to 1000 °C and 1100 °C, respectively. • Compounds demonstrate higher electrical conductivity in comparison with Y{sub 0.9}Ca{sub 0.1}FeO{sub 3}. • Pr-doped (Y,Ca)(Fe,Co)O{sub 3−δ} demonstrate both higher electrical conductivity and TEC. - Abstract: Orthorhombic perovskites Y{sub 1−x}Ca{sub x}Fe{sub 1−y}Co{sub y}O{sub 3−δ} (0.1 ≤ x ≤ 0.2, 0.1 ≤ y ≤ 0.2 and x = 0.1, y = 0.3) weremore » synthesized in air by the citrate route at 1150–1300 °C. High-temperature X-ray powder diffraction (HT XRPD) data for Y{sub 0.9}Ca{sub 0.1}Fe{sub 0.8}Co{sub 0.2}O{sub 3−δ} at 25–800 °C showed no phase transition with calculated thermal expansion coefficient (TEC) of 11.9 ppm K{sup −1}. High-temperature electrical conductivity measurements revealed almost composition independent conductivity values of 22–27 S/cm at 900 °C. No chemical interaction of Y{sub 0.8}Ca{sub 0.2}Fe{sub 0.9}Co{sub 0.1}O{sub 3−δ} with (Zr,Y)O{sub 2−x} (YSZ) or (Ce,Gd)O{sub 2−x} (GDC) was observed up to 1000 °C and 1100 °C, respectively. Partial replacement of Y by Pr according to formula Y{sub 0.8−z}Pr{sub z}Ca{sub 0.2}Fe{sub 0.7}Co{sub 0.3}O{sub 3−δ}, 0.1 ≤ z ≤ 0.35, leads to an increase of both electrical conductivity up to 50 S/cm (z = 0.3) at 900 °C and dilatometry measured TEC up to 15.1 ppm K{sup −1}. Moderate values of electrical conductivity in combination with low TEC and stability towards chemical interaction with typical SOFC electrolytes make Co-doped Y{sub 1−x}Ca{sub x}FeO{sub 3−δ} promissing cathode materials for intermediate temperature solid oxide fuel cells (IT-SOFC)« less

Thermoelectric properties of non-stoichiometric lanthanum sulfides

NASA Technical Reports Server (NTRS)

Shapiro, E.; Danielson, L. R.

1983-01-01

The lanthanum sulfides are promising candidate materials for high-efficiency thermoelectric applications at temperatures up to 1300 C. The non-stoichiometric lanthanum sulfides (LaS(x), where x is in the range 1.33-1.50) appear to possess the most favorable thermoelectric properties. The Seebeck coefficient and resistivity vary significantly with composition, so that an optimum value of alpha sq/rho (where alpha is the Seebeck coefficient and rho is the resistivity) can be chosen. The thermal conductivity remains approximately constant with stoichiometry, so a material with an optimum value of alpha sq/rho should possess the optimum figure-of-merit. Data for the Seebeck coefficient and electrical resistivity of non-stoichiometric lanthanum sulfides will be pressed, together with structural properties of these materials.

Thermoelectric Behavior of PbSe Single Crystals

DOE PAGES

Kogo, Gilbert; Pradhan, Aswini K.; Roy, Utpal N.

2016-12-05

The electrical conductivity and Seebeck coefficient of PbSe single crystals grown by the Bridgman technique display metallic behavior. The Seebeck coefficient increases linearly with increasing temperature and showed positive Seebeck values, typically valid for a p-type PbSe crystal. The electronic thermal conductivity decreases with increase in temperature. The power factor increases gradually with temperature until the maximum value of 6.51 × 10 -3 W/mK2 at 260 K, other values are 5.95 × 10 -3 W/mK 2 at 300 K, and 5.40 × 10 -3 W/mK 2 at 320 K. Our results demonstrate that as-grown PbSe crystal is generically p-type duemore » to excess in Pb and can be a potential candidate for thermoelectric power generation.« less

Thermoelectric Properties of Dy-Doped SrTiO3 Ceramics

NASA Astrophysics Data System (ADS)

Liu, J.; Wang, C. L.; Peng, H.; Su, W. B.; Wang, H. C.; Li, J. C.; Zhang, J. L.; Mei, L. M.

2012-11-01

Sr1- x Dy x TiO3 ( x = 0.02, 0.05, 0.10) ceramics were prepared by the reduced solid-state reaction method, and their thermoelectric properties were investigated from room temperature to 973 K. The resistivity increases with temperature, showing metallic behavior. The Seebeck coefficients tend to saturate at high temperatures, presenting narrow-band behavior, as proved by ab initio calculations of the electronic structure. The magnitudes of the Seebeck coefficient and the electrical resistivity decrease with increasing Dy content. At the same time, the thermal conductivity decreases because the lattice thermal conductivity is reduced by Dy substitution. The maximum value of the figure of merit reaches 0.25 at 973 K for the Sr0.9Dy0.1TiO3 sample.

Evolution of Edge Pedestal Profiles Over the L-H Transition

NASA Astrophysics Data System (ADS)

Sayer, M. S.; Stacey, W. M.; Floyd, J. P.; Groebner, R. J.

2012-10-01

The detailed time evolution of thermal diffusivities, electromagnetic forces, pressure gradients, particle pinch and momentum transport frequencies (which determine the diffusion coefficient) have been analyzed during the L-H transition in a DIII-D discharge. Density, temperature, rotation velocity and electric field profiles at times just before and after the L-H transition are analyzed in terms of these quantities. The analysis is based on the fluid particle balance, energy balance, force balance and heat conduction equations, as in Ref. [1], but with much greater time resolution and with account for thermal ion orbit loss. The variation of diffusive and non-diffusive transport over the L-H transition is determined from the variation in the radial force balance (radial electric field, VxB force, and pressure gradient) and the variation in the interpreted diffusive transport coefficients. 6pt [1] W.M. Stacey and R.J. Groebner, Phys. Plasmas 17, 112512 (2010).

Influence of anisotropy on the electrical conductivity and diffusion coefficient of dry K-feldspar: Implications of the mechanism of conduction

NASA Astrophysics Data System (ADS)

Dai, Li-Dong; Hu, Hai-Ying; Li, He-Ping; Sun, Wen-Qing; Jiang, Jian-Jun

2018-02-01

Not Available Project supported by the Strategic Priority Research Program (B) of the Chinese Academy of Sciences (CAS) (Grant No. XDB 18010401), the Key Research Program of Frontier Sciences of CAS (Grant No. QYZDB-SSW-DQC009), the “135” Program of the Institute of Geochemistry of CAS, the Hundred-Talent Program of CAS, and the National Natural Science Foundation of China (Grant Nos. 41474078, 41774099, and 41772042).

Thermoelectric materials with filled skutterudite structure for thermoelectric devices

NASA Technical Reports Server (NTRS)

Fleurial, Jean-Pierre (Inventor); Borshchevsky, Alex (Inventor); Caillat, Thierry (Inventor); Morelli, Donald T. (Inventor); Meisner, Gregory P. (Inventor)

2002-01-01

A class of thermoelectric compounds based on the skutterudite structure with heavy filling atoms in the empty octants and substituting transition metals and main-group atoms. High Seebeck coefficients and low thermal conductivities are achieved in combination with large electrical conductivities in these filled skutterudites for large ZT values. Substituting and filling methods are disclosed to synthesize skutterudite compositions with desired thermoelectric properties. A melting and/or sintering process in combination with powder metallurgy techniques is used to fabricate these new materials.

Thermoelectric devices based on materials with filled skutterudite structures

NASA Technical Reports Server (NTRS)

Fleurial, Jean-Pierre (Inventor); Borshchevsky, Alex (Inventor); Caillat, Thierry (Inventor); Morelli, Donald T. (Inventor); Meisner, Gregory P. (Inventor)

2003-01-01

A class of thermoelectric compounds based on the skutterudite structure with heavy filling atoms in the empty octants and substituting transition metals and main-group atoms. High Seebeck coefficients and low thermal conductivities are achieved in combination with large electrical conductivities in these filled skutterudites for large ZT values. Substituting and filling methods are disclosed to synthesize skutterudite compositions with desired thermoelectric properties. A melting and/or sintering process in combination with powder metallurgy techniques is used to fabricate these new materials.

Thermophysical and radiation properties of high-temperature C4F8-CO2 mixtures to replace SF6 in high-voltage circuit breakers

NASA Astrophysics Data System (ADS)

Zhong, Linlin; Cressault, Yann; Teulet, Philippe

2018-03-01

C4F8-CO2 mixtures are one of the potential substitutes to SF6 in high-voltage circuit breakers. However, the arc quenching ability of C4F8-CO2 mixtures is still unknown. In order to provide the necessary basic data for the further investigation of arc quenching performance, the compositions, thermodynamic properties, transport coefficients, and net emission coefficients (NEC) of various C4F8-CO2 mixtures are calculated at temperatures of 300-30 000 K in this work. The thermodynamic properties are presented as the product of mass density and specific heat, i.e., ρCp. The transport coefficients include electrical conductivity, viscosity, and thermal conductivity. The atomic and molecular radiation are both taken into account in the calculation of NEC. The comparison of the properties between SF6 and C4F8-CO2 mixtures is also discussed to find their differences. The results of compositions show that C4F8-CO2 mixtures have a distinctive advantage over other alternative gases e.g., CF3I and C3F8, because the dissociative product (i.e., C4F6) of C4F8 at low temperatures has a very high dielectric strength. This is good for an arc quenching medium to endure the arc recovery phase. Compared with SF6, C4F8-CO2 mixtures present lower ρCp at temperatures below 2800 K and larger thermal conductivity above 2800 K. Based on the position of peaks in thermal conductivity, we predict that the cooling of C4F8-CO2 arc will be slowed down at higher temperatures than that of SF6 arc. It is also found that the mixing of CO2 shows slight effects on the electrical conductivity and NEC of C4F8-CO2 mixtures.

Physical properties of Ce-TZP at cryogenic temperature

NASA Astrophysics Data System (ADS)

Han, Y. M.; Chen, Z.; Zhou, M.; Huang, R. J.; Huang, C. J.; Li, L. F.

2014-01-01

Electrical insulators, which are used to insulate cryogenic supply lines and conductor windings, are critical units in superconducting TOKAMAK magnets. Electrical insulators used in superconducting magnets fall into axial and radial insulators. These insulators can be made from glass ribbon epoxy densification and have been used in the Experiment Advanced Superconducting Tokamak (EAST). The properties of Ce-TZP can satisfy the requirement of electrical insulators. In this paper, thermal conductivity, mechanical properties and coefficient of thermal expansion of Ce-TZP have been investigated at cryogenic temperatures. Results indicate that the Ce-TZP shows better properties than epoxy and it demonstrates that the Ce-TZP can be used as insulation material in superconducting magnets.

Modeling the transport properties of epitaxially grown thermoelectric oxide thin films using spectroscopic ellipsometry

NASA Astrophysics Data System (ADS)

Sarath Kumar, S. R.; Abutaha, Anas I.; Hedhili, M. N.; Alshareef, H. N.

2012-01-01

The influence of oxygen vacancies on the transport properties of epitaxial thermoelectric (Sr,La)TiO3 thin films is determined using electrical and spectroscopic ellipsometry (SE) measurements. Oxygen vacancy concentration was varied by ex-situ annealing in Ar and Ar/H2. All films exhibited degenerate semiconducting behavior, and electrical conductivity decreased (258-133 S cm-1) with increasing oxygen content. Similar decrease in the Seebeck coefficient is observed and attributed to a decrease in effective mass (7.8-3.2 me), as determined by SE. Excellent agreement between transport properties deduced from SE and direct electrical measurements suggests that SE is an effective tool for studying oxide thin film thermoelectrics.

Apparatus and method for measuring the Seebeck coefficient and resistivity of materials

NASA Technical Reports Server (NTRS)

Hadek, V. (Inventor)

1973-01-01

An apparatus for measuring the thermoelectric properties of materials under high pressure is described that includes a pair of force transmitting assemblies constructed of thermally and electrically conductive material positioned between the ram and anvil of a press. Each force transmitting assembly has a small diameter pressing portion for contacting a face of the sample so that the sample can be squeezed between them. Each assembly also includes a heat exchanger to maintain the sample face at a controlled temperature, and an electrical conductor to carry current generated by the sample. A sleeve of thermally and electrically insulative material closely surrounds the pressing portions of the two assemblies.

Electrokinetic and hydrodynamic properties of charged-particles systems. From small electrolyte ions to large colloids

NASA Astrophysics Data System (ADS)

Nägele, G.; Heinen, M.; Banchio, A. J.; Contreras-Aburto, C.

2013-11-01

Dynamic processes in dispersions of charged spherical particles are of importance both in fundamental science, and in technical and bio-medical applications. There exists a large variety of charged-particles systems, ranging from nanometer-sized electrolyte ions to micron-sized charge-stabilized colloids. We review recent advances in theoretical methods for the calculation of linear transport coefficients in concentrated particulate systems, with the focus on hydrodynamic interactions and electrokinetic effects. Considered transport properties are the dispersion viscosity, self- and collective diffusion coefficients, sedimentation coefficients, and electrophoretic mobilities and conductivities of ionic particle species in an external electric field. Advances by our group are also discussed, including a novel mode-coupling-theory method for conduction-diffusion and viscoelastic properties of strong electrolyte solutions. Furthermore, results are presented for dispersions of solvent-permeable particles, and particles with non-zero hydrodynamic surface slip. The concentration-dependent swelling of ionic microgels is discussed, as well as a far-reaching dynamic scaling behavior relating colloidal long- to short-time dynamics.

Multi-band analysis of temperature-dependent transport coefficients (conductivity, Hall, Seebeck, and Nernst) of Ni-doped CoSb3

NASA Astrophysics Data System (ADS)

Kajikawa, Y.

2016-02-01

The experimental data on the temperature dependence of the four transport coefficients, i.e., the electrical conductivity (σ), Hall coefficient (RH), Seebeck coefficient (S), and Nernst coefficient (Q), of n-type Co0.999Ni0.001Sb3 reported by Sun et al. [Nat. Commun. 6, 7475 (2015)] have been analyzed in a multi-band model, especially focusing on the low temperature data. The multi-band model includes not only the lowest valley of the conduction band at the Γ point but also satellite valleys at the second minima together with an impurity band. The lowest valley at the Γ point is assumed to split into the c1 band and the spin-orbit split-off (so) band. For the analysis, the general expression of the Nernst coefficient in the multi-band model is derived. At such low temperatures that the other bands than the c1 and the impurity band can be neglected, this expression is shown to be approximated as the sum of three terms: the intrinsic terms due to the Nernst coefficients in the two bands themselves and a cross term proportional to the difference of Seebeck coefficients between the two bands. As a result of the analysis, it is proved that the anomalous positive peak of S(T) observed around T = 20 K as well as the sharp rise of the Hall mobility observed from 15 K to 40 K are due to the transition from hopping conduction in the impurity band to conduction in the c1 band. On the other hand, the pronounced peak of Q(T) observed slightly below 40 K is proved to be due to the cross term between the impurity band and the c1 band. In addition, a shoulder of Q(T) appeared around T = 80 K lends clear evidence of the existence of the so band, while the increase in both of σ(T) and | S ( T ) | above 150 K suggests the existence of the satellite valleys.

About the feasibilities of controlling the properties of thermoelectric energy converters using optical radiation

NASA Astrophysics Data System (ADS)

Kshevetsky, Oleg S.

2018-01-01

We represent evaluating analysis of the feasibilities for controlling the properties of thermoelectric energy converters using EM radiation in the regimes of cooling, heating, electromotive force generation, or electric current generation. Thus we investigate the influence of optical radiation both on electric conductivity and thermo-electromotive force coefficient of thermoelectric materials. We also discuss promising applications for controlling the properties of thermoelectric energy converters using EM radiation. We represent the results of experimental study of positionsensitive energy converters in the regimes of electromotive force generation and the electric current generation (in part, photo-thermoelectric position-sensitive temperature detectors), position-sensitive photo-thermoelectric energy converters in the regimes of cooling, heating, parallel photoelectric and thermoelectric conversion of sun-light optical radiation into electric power.

Optimal Electricity Charge Strategy Based on Price Elasticity of Demand for Users

NASA Astrophysics Data System (ADS)

Li, Xin; Xu, Daidai; Zang, Chuanzhi

The price elasticity is very important for the prediction of electricity demand. This paper mainly establishes the price elasticity coefficient for electricity in single period and inter-temporal. Then, a charging strategy is established based on these coefficients. To evaluate the strategy proposed, simulations of the two elastic coefficients are carried out based on the history data of a certain region.

Electrostatic coupling between DNA and its counterions modulates the observed translational diffusion coefficients.

PubMed

Stellwagen, Earle; Stellwagen, Nancy C

2015-09-01

Free solution capillary electrophoresis (CE) is a useful technique for measuring the translational diffusion coefficients of charged analytes. The measurements are relatively fast if the polarity of the electric field is reversed to drive the analyte back and forth past the detection window during each run. We have tested the validity of the resulting diffusion coefficients using double-stranded DNA molecules ranging in size from 20 to 960 base pairs as the model system. The diffusion coefficients of small DNAs are equal to values in the literature measured by other techniques. However, the diffusion coefficients of DNA molecules larger than ∼30 base pairs are anomalously high and deviate increasingly from the literature values with increasing DNA molar mass. The anomalously high diffusion coefficients are due to electrostatic coupling between the DNA and its counterions. As a result, the measured diffusion coefficients vary with the diffusion coefficient of the counterion, as well as with cation concentration and electric field strength. These effects can be reduced or eliminated by measuring apparent diffusion coefficients of the DNA at several different electric field strengths and extrapolating the results to zero electric field.

Electric field control in DC cable test termination by nano silicone rubber composite

NASA Astrophysics Data System (ADS)

Song, Shu-Wei; Li, Zhongyuan; Zhao, Hong; Zhang, Peihong; Han, Baozhong; Fu, Mingli; Hou, Shuai

2017-07-01

The electric field distributions in high voltage direct current cable termination are investigated with silicone rubber nanocomposite being the electric stress control insulator. The nanocomposite is composed of silicone rubber, nanoscale carbon black and graphitic carbon. The experimental results show that the physical parameters of the nanocomposite, such as thermal activation energy and nonlinearity-relevant coefficient, can be manipulated by varying the proportion of the nanoscale fillers. The numerical simulation shows that safe electric field distribution calls for certain parametric region of the thermal activation energy and nonlinearity-relevant coefficient. Outside the safe parametric region, local maximum of electric field strength around the stress cone appears in the termination insulator, enhancing the breakdown of the cable termination. In the presence of the temperature gradient, thermal activation energy and nonlinearity-relevant coefficient work as complementary factors to produce a reasonable electric field distribution. The field maximum in the termination insulator show complicate variation in the transient processes. The stationary field distribution favors the increase of the nonlinearity-relevant coefficient; for the transient field distribution in the process of negative lighting impulse, however, an optimized value of the nonlinearity-relevant coefficient is necessary to equalize the electric field in the termination.

The time and temperature dependence of the thermoelectric properties of silicon-germanium alloy

NASA Technical Reports Server (NTRS)

Raag, V.

1975-01-01

Experimental data on the electrical resistivity and Seebeck coefficient of n-type and p-type silicon-germanium alloys are analyzed in terms of a solid-state dopant precipitation model proposed by Lifshitz and Slyozov (1961). Experimental findings on the time and temperature dependence of the thermal conductivity of these two types of alloy indicate that the thermal conductivity of silicon-germanium alloys changes with time, contrary to previous hypothesis. A preliminary model is presented which stipulates that the observed thermal conductivity decrease in silicon-germanium alloys is due partly to dopant precipitation underlying the electrical property changes and partly to enhanced alloying of the material. It is significant that all three properties asymptotically approach equilibrium values with time. Total characterization of these properties will enable the time change to be fully compensated in the design of a thermoelectric device employing silicon-germanium alloys.

Interface interactions in benzophenone doped by multiwalled carbon nanotubes

NASA Astrophysics Data System (ADS)

Lebovka, N. I.; Goncharuk, A.; Melnyk, V. I.; Puchkovska, G. A.

2009-08-01

The interface interactions were studied by methods of conductometry, low-temperature phosphorescence and differential scanning calorimetry (DSC) in multiwalled carbon nanotubes (MWCNT) and benzophenone (BP) composite. The concentration of MWCNTs was varied within 0-1 wt%. A percolative threshold was found at MWCNT concentrations exceeding 0.1 wt%. The integration of MWCNTs caused melting temperature increase (≈3 K for 1 wt% of MWCNTs). The effect of positive thermal resistively coefficient, as well as substantial hysteretic behaviour of electrical conductivity σ in a heating-cooling cycle, was observed near the melting point of BP ( T m=321.5 K). The activation-type temperature behaviour of electrical conductivity was observed in the temperature range of supercooled BP. The activation energy was decreasing with increase of MWCNT concentration. The observed nonlinear dependencies of electrical conductivity σ vs. applied voltage U reflect the transport mechanism of the charge carriers through amorphous interface films formed near the surface of the MWCNTs. The thermal shifts of phosphorescence spectra measured within the temperature range 5-200 K evidence existence of such interface films of amorphous BP with width of the order of 0.1 μm.

Thermoelectric properties of the ceramic oxide Sr1- x La x TiO3

NASA Astrophysics Data System (ADS)

Mahmud, Iqbal; Yoon, Man-Soon; Kim, Il-Ho; Choi, Moon-Kwan; Ur, Soon-Chul

2016-01-01

The effect of lanthanum on the electric and the thermoelectric properties of the ceramic oxide Sr1- x La x TiO3 (where x = 0.0, 0.04, 0.06, 0.08 and 0.12 mole) have been studied. La-doped SrTiO3 was prepared by using the conventional mixed-oxide reaction method. XRD patterns indicated that almost all the La atoms incorporated into the SrTiO3 crystal provided charge carriers. The lattice parameter increases with increasing La doping content. The relative densities of all the samples varied from 89.6% to 94.8%. The electrical conductivity increased with La doping up to 0.08 moles and then decreased as the content of La was increased above 0.08 moles. The thermal conductivity decreased with increasing La content. The largest absolute value of the Seebeck coefficient, 394 μVK-1 at 973 K, was observed at x = 0.04. The Sr0.92La0.08TiO3 sample showed its maximum electrical conductivity at 773 K and its largest ZT value of 0.20 at 973 K.

Annealing of Heavily Boron-Doped Silicon: Effect on Electrical and Thermoelectric Properties.

PubMed

Zulian, Laura; Segrado, Francesco; Narducci, Dario

2017-03-01

In previous studies it was shown that heavily boron-doped nanocrystalline silicon submitted to thermal treatments at temperatures ≥800 °C is characterized by an anomalously high thermoelectric power factor. Its enhanced performances were ascribed to the formation of SiBx precipitates at grain boundary, leading to the formation of potential barriers that filter out low-energy carriers, then causing a simultaneous enhancement of the Seebeck coefficient and of the electrical conductivity. To further investigate the effect of thermal treatment on boron-doped nanocrystalline silicon, samples were submitted to a host of annealing processes or of sequences of them at temperatures between 900 and 1000 °C and for various amounts of time. Electrical conductivity and Hall effect measurements were carried out after each thermal treatment over the temperature range 20–300 K. They provided evidence of the formation of an impurity band, and of hopping conduction at very low temperatures. Hall resistivity data versus temperature provided therefore important insights in the electronic structure of the system, which will enable a more complete understanding of the factors ruling energy filtering in this class of materials.

Development of advanced thermoelectric materials, phase A

NASA Technical Reports Server (NTRS)

1980-01-01

Work performed on the chemical system characterized by chrome sulfide, chrome selenide, lanthanum selenide, and lanthanum sulfide is described. Most materials within the chemical systems possess the requisites for attractive thermoelectric materials. The preparation of the alloys is discussed. Graphs show the Seebeck coefficient, electrical resistivity, and thermal conductivity of various materials within the chemical systems. The results of selected doping are included.

Enhanced thermoelectric performance of Pb doped Cu2SnSe3 synthesized employing spark plasma sintering

NASA Astrophysics Data System (ADS)

Shyam Prasad, K.; Rao, Ashok; Tyagi, Kriti; Singh Chauhan, Nagendra; Gahtori, Bhasker; Bathula, Sivaiah; Dhar, Ajay

2017-05-01

We report an enhancement in the thermoelectric performance of Cu2SnSe3 alloy on Pb doping, owing to a sharp increase in its power factor. The powder XRD pattern of all samples of Cu2Sn1-xPbxSe3 (0≤x≤0.03), prepared using solid state reaction, exhibited a cubic structure with a space group of F 4 ̅ 3 m . The results show that temperature dependent electrical resistivity, ρ(T) increases with increasing temperature thereby demonstrating that the samples display heavily doped semiconducting nature, which could be satisfactorily described by small polaron hopping model in the whole temperature range of measurement for all the samples. Both the resistivity and the Seebeck coefficient are reduced with 2 vol% Pb doping. The thermal conductivity of all the samples reduces with increasing temperature. Despite a decrease in Seebeck coefficient the power factor shows an increase on Pb doping, owing to a sharp surge in the electrical conductivity which results in an enhanced ZTmax 0.64 at 700 K for an optimized composition of Cu2Sn0.98Pb0.02Se3, which is nearly twice the value of the corresponding undoped counterpart.

Thermoelectric properties of Ca0.8Dy0.2MnO3 synthesized by solution combustion process

NASA Astrophysics Data System (ADS)

Park, Kyeongsoon; Lee, Ga Won

2011-10-01

High-quality Ca0.8Dy0.2MnO3 nano-powders were synthesized by the solution combustion process. The size of the synthesized Ca0.8Dy0.2MnO3 powders was approximately 23 nm. The green pellets were sintered at 1150-1300°C at a step size of 50°C. Sintered Ca0.8Dy0.2MnO3 bodies crystallized in the perovskite structure with an orthorhombic symmetry. The sintering temperature did not affect the Seebeck coefficient, but significantly affected the electrical conductivity. The electrical conductivity of Ca0.8Dy0.2MnO3 increased with increasing temperature, indicating a semiconducting behavior. The absolute value of the Seebeck coefficient gradually increased with an increase in temperature. The highest power factor (3.7 × 10-5 Wm-1 K-2 at 800°C) was obtained for Ca0.8Dy0.2MnO3 sintered at 1,250°C. In this study, we investigated the microstructure and thermoelectric properties of Ca0.8Dy0.2MnO3, depending on sintering temperature.

Thermoelectric properties of Ca0.8Dy0.2MnO3 synthesized by solution combustion process

PubMed Central

2011-01-01

High-quality Ca0.8Dy0.2MnO3 nano-powders were synthesized by the solution combustion process. The size of the synthesized Ca0.8Dy0.2MnO3 powders was approximately 23 nm. The green pellets were sintered at 1150-1300°C at a step size of 50°C. Sintered Ca0.8Dy0.2MnO3 bodies crystallized in the perovskite structure with an orthorhombic symmetry. The sintering temperature did not affect the Seebeck coefficient, but significantly affected the electrical conductivity. The electrical conductivity of Ca0.8Dy0.2MnO3 increased with increasing temperature, indicating a semiconducting behavior. The absolute value of the Seebeck coefficient gradually increased with an increase in temperature. The highest power factor (3.7 × 10-5 Wm-1 K-2 at 800°C) was obtained for Ca0.8Dy0.2MnO3 sintered at 1,250°C. In this study, we investigated the microstructure and thermoelectric properties of Ca0.8Dy0.2MnO3, depending on sintering temperature. PMID:21974984

Thermoelectric properties of Ca0.8Dy0.2MnO3 synthesized by solution combustion process.

PubMed

Park, Kyeongsoon; Lee, Ga Won

2011-10-05

High-quality Ca0.8Dy0.2MnO3 nano-powders were synthesized by the solution combustion process. The size of the synthesized Ca0.8Dy0.2MnO3 powders was approximately 23 nm. The green pellets were sintered at 1150-1300°C at a step size of 50°C. Sintered Ca0.8Dy0.2MnO3 bodies crystallized in the perovskite structure with an orthorhombic symmetry. The sintering temperature did not affect the Seebeck coefficient, but significantly affected the electrical conductivity. The electrical conductivity of Ca0.8Dy0.2MnO3 increased with increasing temperature, indicating a semiconducting behavior. The absolute value of the Seebeck coefficient gradually increased with an increase in temperature. The highest power factor (3.7 × 10-5 Wm-1 K-2 at 800°C) was obtained for Ca0.8Dy0.2MnO3 sintered at 1,250°C. In this study, we investigated the microstructure and thermoelectric properties of Ca0.8Dy0.2MnO3, depending on sintering temperature.

Thermoelectric Properties of Cu-doped Bi2-xSbxTe3 Prepared by Encapsulated Melting and Hot Pressing

NASA Astrophysics Data System (ADS)

Jung, Woo-Jin; Kim, Il-Ho

2018-03-01

P-type Bi2-xSbxTe3:Cum (x = 1.5-1.7 and m = 0.002-0.003) solid solutions were synthesized using encapsulated melting and were consolidated using hot pressing. The effects of Sb substitution and Cu doping on the charge transport and thermoelectric properties were examined. The lattice constants decreased with increasing Sb and Cu contents. As the amount of Sb substitution and Cu doping was increased, the electrical conductivity increased, and the Seebeck coefficient decreased owing to the increase in the carrier concentration. All specimens exhibited degenerate semiconductor characteristics and positive Hall and Seebeck coefficients, indicating p-type conduction. The increased Sb substitution caused a shift in the onset temperature of the intrinsic transition and bipolar conduction to higher temperatures. The electronic thermal conductivity increased with increasing Sb and Cu contents owing to the increase in the carrier concentration, while the lattice thermal conductivity slightly decreased due to alloy scattering. A maximum figure of merit, ZTmax = 1.25, was achieved at 373 K for Bi0.4Sb1.6Te3:Cu0.003.

High-Temperature Thermoelectric Properties of Perovskite-Type Pr0.9Sr0.1Mn1- x Fe x O3 (0 ≤ x ≤ 1)

NASA Astrophysics Data System (ADS)

Nakatsugawa, H.; Saito, M.; Okamoto, Y.

2017-05-01

Polycrystalline samples of Pr0.9Sr0.1Mn1- x Fe x O3 (0 ≤ x ≤ 1) have been synthesized using a conventional solid-state reaction method, and the crystal structure studied at room temperature. The magnetic susceptibility was measured from 5 K to 350 K. The electrical resistivity, Seebeck coefficient, and thermal conductivity were investigated as functions of temperature below 850 K. For all samples, the perovskite structure at room temperature exhibited orthorhombic Pbnm phase. While the Pr0.9Sr0.1MnO3 ( x = 0) sample exhibited ferromagnetic-like ground state below T C = 145 K (Curie temperature), the ferromagnetic transition temperature T C decreased with increasing x. The Seebeck coefficient of the samples with 0 ≤ x ≤ 0.8 decreased with increasing temperature because of double-exchange interaction of Mn ions. In fact, the carrier type for x = 0 changed from hole-like to electron-like behavior above 800 K. On the other hand, the samples with x ≥ 0.9 showed large positive Seebeck coefficient over the entire temperature range, indicating that the low-spin state of Fe ions dominated the electronic structure for this x range. In particular, the sample with x = 1 exhibited p-type thermoelectric properties with relatively high Seebeck coefficient, moderate electrical resistivity, and low thermal conductivity. Thus, the sample with x = 1 showed power factor of 20 μW m-1 K-2 at 850 K leading to ZT of 0.024 at this temperature, indicating that hole-doped perovskite-type iron oxide is a good candidate high-temperature thermoelectric p-type oxide.

The Shubnikov-de Haas effect and thermoelectric properties of Tl-doped Sb{sub 2}Te{sub 3} and Bi{sub 2}Se{sub 3}

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kulbachinskii, V. A., E-mail: kulb@mig.phys.msu.ru; Kudryashov, A. A.; Kytin, V. G.

2015-06-15

The influence of doping with Tl on the Shubnikov-de Haas effect at T = 4.2 K in magnetic fields up to 38 T in p-Sb{sub 2−x}Tl{sub x}Te{sub 3} (x = 0, 0.005, 0.015, and 0.05) and n-Bi{sub 2−x}Tl{sub x}Se{sub 3} (x = 0, 0.01, 0.02, 0.04, and 0.06) single crystals is investigated. Extreme cross-sections of the Fermi surface in both materials decrease upon doping with Tl: the hole concentration decreases in Sb{sub 2−x}Tl{sub x}Te{sub 3} due to the donor effect of Tl and the electron concentration in n-Bi{sub 2−x}Tl{sub x}Se{sub 3} decreases due to the acceptor effect of Tl. Themore » temperature dependences of the Seebeck coefficient, electrical conductivity, thermal conductivity, and dimensionless thermoelectric figure of merit in a temperature range of 77–300 K are measured. The thermal conductivity and electrical conductivity decrease upon doping with Tl both in p-Sb{sub 2−x}Tl{sub x}Te{sub 3} and in n-Bi{sub 2−x}Tl{sub x}Se{sub 3}. The Seebeck coefficient increases in all compositions upon an increase in doping over the entire measured temperature range. The thermoelectric figure of merit increases upon doping with Tl.« less

Thermoelectric Properties of Epitaxial β-FeSi2 Thin Films on Si(111) and Approach for Their Enhancement

NASA Astrophysics Data System (ADS)

Taniguchi, Tatsuhiko; Sakane, Shunya; Aoki, Shunsuke; Okuhata, Ryo; Ishibe, Takafumi; Watanabe, Kentaro; Suzuki, Takeyuki; Fujita, Takeshi; Sawano, Kentarou; Nakamura, Yoshiaki

2017-05-01

We have investigated the intrinsic thermoelectric properties of epitaxial β-FeSi2 thin films and the impact of phosphorus (P) doping. Epitaxial β-FeSi2 thin films with single phase were grown on Si(111) substrates by two different techniques in an ultrahigh-vacuum molecular beam epitaxy (MBE) system: solid-phase epitaxy (SPE), where iron silicide films formed by codeposition of Fe and Si at room temperature were recrystallized by annealing at 530°C to form epitaxial β-FeSi2 thin films on Si(111) substrates, and MBE of β-FeSi2 thin films on epitaxial β-FeSi2 templates formed on Si(111) by reactive deposition epitaxy (RDE) at 530°C (RDE + MBE). Epitaxial SPE thin films based on codeposition had a flatter surface and more abrupt β-FeSi2/Si(111) interface than epitaxial RDE + MBE thin films. We investigated the intrinsic thermoelectric properties of the epitaxial β-FeSi2 thin films on Si(111), revealing lower thermal conductivity and higher electrical conductivity compared with bulk β-FeSi2. We also investigated the impact of doping on the Seebeck coefficient of bulk and thin-film β-FeSi2. A route to enhance the thermoelectric performance of β-FeSi2 is proposed, based on (1) fabrication of thin-film structures for high electrical conductivity and low thermal conductivity, and (2) proper choice of doping for high Seebeck coefficient.

K1.33Mn8O16 as an electrocatalyst and a cathode

NASA Astrophysics Data System (ADS)

Jalili, Seifollah; Moharramzadeh Goliaei, Elham; Schofield, Jeremy

2017-02-01

Density functional theory (DFT) calculations are carried out to investigate the electronic, magnetic and thermoelectric properties of bulk and nanosheet K1.33Mn8O16 materials. The catalytic activity and cathodic performance of bulk and nanosheet structures are examined using the Tran-Blaha modified Becke-Johnson (TB-mBJ) exchange potential. Electronic structure calculations reveal an anti-ferromagnetic ground state, with a TB-mMBJ band gap in bulk K1.33Mn8O16 that is in agreement with experimental results. Density of state plots indicate a partial reduction of Mn4+ ions to Mn3+, without any obvious sign of Jahn-Teller distortion. Moreover, use of the O p-band center as a descriptor of catalytic activity suggests that the nanosheet has enhanced catalytic activity compared to the bulk structure. Thermoelectric parameters such as the Seebeck coefficient, electrical conductivity, and thermal conductivity are also calculated, and it is found that the Seebeck coefficients decrease with increasing temperature. High Seebeck coefficients for both spin-up and spin-down states are found in the nanosheet relative to their value in the bulk K1.33Mn8O16 structure, whereas the electrical and thermal conductivity are reduced relative to the bulk. In addition, figures of merit values are calculated as a function of the chemical potential and it is found that the nanosheet has a figure of merit of 1 at room temperature, compared to 0.5 for the bulk material. All results suggest that K1.33Mn8O16 nanosheets can be used both as a material in waste heat recovery and as an electrocatalyst in fuel cells and batteries.

Impact of the electric compressor for automotive air conditioning system on fuel consumption and performance analysis

NASA Astrophysics Data System (ADS)

Zulkifli, A. A.; Dahlan, A. A.; Zulkifli, A. H.; Nasution, H.; Aziz, A. A.; Perang, M. R. M.; Jamil, H. M.; Misseri, M. N.

2015-12-01

Air conditioning system is the biggest auxiliary load in a vehicle where the compressor consumed the largest. Problem with conventional compressor is the cooling capacity cannot be control directly to fulfill the demand of thermal load inside vehicle cabin. This study is conducted experimentally to analyze the difference of fuel usage and air conditioning performance between conventional compressor and electric compressor of the air conditioning system in automobile. The electric compressor is powered by the car battery in non-electric vehicle which the alternator will recharge the battery. The car is setup on a roller dynamometer and the vehicle speed is varied at 0, 30, 60, 90 and 110 km/h at cabin temperature of 25°C and internal heat load of 100 and 400 Watt. The results shows electric compressor has better fuel consumption and coefficient of performance compared to the conventional compressor.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Dupertuis, M.A.; Proctor, M.; Acklin, B.

Energy balance and reciprocity relations are studied for harmonic inhomogeneous plane waves that are incident upon a stack of continuous absorbing dielectric media that are macroscopically characterized by their electric and magnetic permittivities and their conductivities. New cross terms between parallel electric and parallel magnetic modes are identified in the fully generalized Poynting vector. The symmetry and the relations between the general Fresnel coefficients are investigated in the context of energy balance at the interface. The contributions of the so-called mixed Poynting vector are discussed in detail. In particular a new transfer matrix is introduced for energy fluxes in thin-filmmore » optics based on the Poynting and mixed Poynting vectors. Finally, the study of reciprocity relations leads to a generalization of a theorem of reversibility for conducting and dielectric media. 16 refs.« less

Contactless Mobility, Carrier Density, and Sheet Resistance Measurements on Si, GaN, and AlGaN/GaN High Electron Mobility Transistor (HEMT) Wafers

DTIC Science & Technology

2015-02-01

to the electrical characterization of semiconductor materials. The Hall effect occurs when an electrical conductor is placed in a magnetic field...system. The TE11 mode is caused by the Hall effect when under an applied magnetic field. This effect rotates the TE10 mode 90° where the forward...conductivity tensors σxx and σxy, where σxx and σxy are functions of the magnetic field (H). The Hall coefficient (RH) for a given H is then

Shockwave Consolidation of Nanostructured Thermoelectric Materials

NASA Technical Reports Server (NTRS)

Prasad, Narasimha S.; Taylor, Patrick; Nemir, David

2014-01-01

Nanotechnology based thermoelectric materials are considered attractive for developing highly efficient thermoelectric devices. Nano-structured thermoelectric materials are predicted to offer higher ZT over bulk materials by reducing thermal conductivity and increasing electrical conductivity. Consolidation of nano-structured powders into dense materials without losing nanostructure is essential towards practical device development. Using the gas atomization process, amorphous nano-structured powders were produced. Shockwave consolidation is accomplished by surrounding the nanopowder-containing tube with explosives and then detonating. The resulting shock wave causes rapid fusing of the powders without the melt and subsequent grain growth. We have been successful in generating consolidated nano-structured bismuth telluride alloy powders by using the shockwave technique. Using these consolidated materials, several types of thermoelectric power generating devices have been developed. Shockwave consolidation is anticipated to generate large quantities of nanostructred materials expeditiously and cost effectively. In this paper, the technique of shockwave consolidation will be presented followed by Seebeck Coefficient and thermal conductivity measurements of consolidated materials. Preliminary results indicate a substantial increase in electrical conductivity due to shockwave consolidation technique.

Synthesis and thermoelectric properties of tantalum-doped ZrNiSn half-Heusler alloys

NASA Astrophysics Data System (ADS)

Zhao, Degang; Zuo, Min; Wang, Zhenqing; Teng, Xinying; Geng, Haoran

2014-04-01

The Ta-doped ZrNiSn half-Heusler alloys, Zr1-xTaxNiSn, were synthesized by arc melting and hot-press sintering. Microstructure of Zr1-xTaxNiSn compounds were analyzed and the thermoelectric (TE) properties of Zr1-xTaxNiSn compounds were measured from room temperature to 823 K. The electrical conductivity increased with increasing Ta content. The Seebeck coefficient of Zr1-xTaxNiSn compounds was sharply decreased with increasing Ta content. The Hall mobility was proportional to T-1.5 above 673 K, indicating that the acoustic phonon scattering was predominant in the temperature range. The thermal conductivity was effectively depressed by introducing Ta substitution. The figure of merit of ZrNiSn compounds was improved due to the decreased thermal conductivity and increased electrical conductivity. The maximum ZT value of 0.60 was achieved for Zr0.97Ta0.03NiSn sample at 823 K.

Thermoelectric Properties of Complex Zintl Phases

NASA Astrophysics Data System (ADS)

Snyder, G. Jeffrey

2008-03-01

Complex Zintl phases make ideal thermoelectric materials because they can exhibit the necessary ``electron-crystal, phonon-glass'' properties required for high thermoelectric efficiency. Complex crystal structures can lead to high thermoelectric figure of merit (zT) by having extraordinarily low lattice thermal conductivity. A recent example is the discovery that Yb14MnSb11, a complex Zintl compound, has twice the zT as the SiGe based material currently in use at NASA. The high temperature (300K - 1300K) electronic properties of Yb14MnSb11 can be understood using models for heavily doped semiconductors. The free hole concentration, confirmed by Hall effect measurements, is set by the electron counting rules of Zintl and the valence of the transition metal (Mn^+2). Substitution of nonmagnetic Zn^+2 for the magnetic Mn^+2 reduces the spin-disorder scattering and leads to increased zT (10%). The reduction of spin-disorder scattering is consistent with the picture of Yb14MnSb11 as an underscreened Kondo lattice as derived from low temperature measurements. The hole concentration can be reduced by the substitution of Al^+3 for Mn^+2, which leads to an increase in the Seebeck coefficient and electrical resistivity consistent with models for degenerate semiconductors. This leads to further improvements (about 25%) in zT and a reduction in the temperature where the zT peaks. The peak in zT is due to the onset of minority carrier conduction and can be correlated with reduction in Seebeck coefficient, increase in electrical conductivity and increase in thermal conductivity due to bipolar thermal conduction.

Thermal and Electrical Transport in Oxide Heterostructures

NASA Astrophysics Data System (ADS)

Ravichandran, Jayakanth

This dissertation presents a study of thermal and electrical transport phenomena in heterostructures of transition metal oxides, with specific interest in understanding and tailoring thermoelectricity in these systems. Thermoelectric energy conversion is a promising method for waste heat recovery and the efficiency of such an engine is directly related to a material dependent figure of merit, Z, given as S2sigma/kappa, where S is thermopower and sigma and kappa are electrical and thermal conductivity respectively. Achieving large figure of merit has been hampered by the coupling between these three thermoelectric coefficients, and the primary aim of this study is to understand the nature of thermoelectricity in complex oxides and identify mechanisms which can allow tuning of one or more thermoelectric coefficients in a favorable manner. Unlike the heavily studied conventional thermoelectric semiconductors, transition metals based complex oxides show conduction band characteristics dominated by d-bands, with much larger effective masses and varying degrees of electron correlations. These systems provide for exotic thermoelectric effects which are typically not explained by conventional theories and hence provide an ideal platform for exploring the limits of thermoelectricity. Meanwhile, oxides are composed of earth abundant elements and have excellent high temperature stability, thus providing compelling technological possibilities for thermoelectrics based power generation. In this dissertation, we address specific aspects of thermoelectricity in model complex oxide systems such as perovskite titanates and layered cobaltates to understand thermal and thermoelectric behavior and explore the tunability of thermoelectricity in these systems. The demonstration of band engineering as a viable method to tune physical properties of materials is explored. The model system used for this case is strontium titanate, where two dopants such as La on the Sr-site and oxygen vacancies are employed to achieve band engineering. This method was used to obtain tunable transparent conducting properties and thermoelectric properties for heavily doped strontium titanate. The second aspect investigated is the use of strongly correlated materials for thermoelectricity. The cobaltates, specifically layered cobaltates, show large thermopower even at very large carrier densities. The coupling of thermopower and electrical conductivity is shown to be weaker for a strongly correlated material such as cobaltate, which opens up possibilities of complete decoupling of all three thermoelectric coefficients. Finally, the thermal properties of complex oxides, specifically in perovskite titanates, is addressed in detail. Thermal conductivity is demonstrated to be a sensitive probe for defects in a system, where processing conditions play a significant role in modulating the crystallinity of the material. The perovskite titanate superlattice system of strontium titanate and calcium titanate is used beat alloy limit. It also shows interesting period thickness dependent thermal properties. The possible origin of this effect is briefly discussed and future directions for this research is also elaborated in detail.

Heterovalent Substitution to Enrich Electrical Conductivity in Cu2CdSn1-xGaxSe4 Series for High Thermoelectric Performances

PubMed Central

Wang, Bo; Li, Yu; Zheng, Jiaxin; Xu, Ming; Liu, Fusheng; Ao, Weiqing; Li, Junqing; Pan, Feng

2015-01-01

Serials of Ga doping on Sn sites as heterovalent substitution in Cu2CdSnSe4 are prepared by the melting method and the spark plasma sintering (SPS) technique to form Cu2CdSn1-xGaxSe4 (x = 0, 0.025, 0.05, 0.075, 0.01, and 0.125). Massive atomic vacancies are found at x = 0.10 by the heterovalent substitution, which contributes significantly to the increase of electrical conductivity and the decrease of lattice thermal conductivity. The electrical conductivity is increased by about ten times at 300 K after Ga doping. Moreover, the seebeck coefficient only decreases slightly from 310 to 226 μV/K at 723 K, and a significant increase of the power factor is obtained. As a result, a maxium value of 0.27 for the figure of merit (ZT) is obtained at x = 0.10 and at 723 K. Through an ab initio study of the Ga doping effect, we find that the Fermi level of Cu2CdSnSe4 is shifted downward to the valence band, thus improving the hole concentration and enhancing the electrical conductivity at low doping levels. Our experimental and theoretical studies show that a moderate Ga doping on Sn sites is an effective method to improve the thermoelectric performance of Cu2CdSnSe4. PMID:25791823

Synthesis and Thermoelectric Properties of Partially Double-Filled (Ce1- z Pr z ) y Fe4- x Co x Sb12 Skutterudites

NASA Astrophysics Data System (ADS)

Cha, Ye-Eun; Shin, Dong-Kil; Kim, Il-Ho

2018-06-01

Partially double-filled p-type (Ce1- z Pr z ) y Fe4- x Co x Sb12 ( z = 0.25, 0.75; y = 0.8; x = 0, 0.5, 1.0) skutterudites were synthesized by encapsulated melting and consolidated by hot pressing. The microstructure, phase, charge transport characteristics, and thermoelectric properties of the hot-pressed specimens were analyzed. Detailed measurements indicated that the skutterudite phase was successfully synthesized, but a small amount of a secondary phase (FeSb2) was also identified. However, the amount of the FeSb2 phase decreased with an increase in the Co substitution. Unlike for the filled Ce1- z Pr z Fe4- x Co x Sb12 skutterudites with y = 1, the (Ce,Pr)Sb2 phases were not formed by partial filling with Ce/Pr. The electrical conductivity decreased with increasing temperature, similar to the behavior shown by degenerate semiconductors. The Hall coefficient and the Seebeck coefficients were positive, indicating that all specimens exhibited p-type characteristics. The electrical conductivity and the electronic thermal conductivity decreased with increasing Pr filling and Co substitution because of the decreased carrier concentration caused by charge compensation. A maximum dimensionless figure of merit, ZTmax = 0.84, was obtained at 623 K for (Ce0.75Pr0.25)0.8Fe3CoSb12.

Syntheses, structures, and physical properties of CsRE(2)Ag(3)Te(5) (RE = Pr, Nd, Sm, Gd-Er) and RbR(2)Ag(3)Te(5) (RE = Sm, Gd-Dy).

PubMed

Meng, Chang-Yu; Chen, Hong; Wang, Peng

2014-07-07

A new series of quaternary CsRE2Ag3Te5 (RE = Pr, Nd, Sm, Gd-Er) and RbRE2Ag3Te5 (RE = Sm, Gd-Dy), which have been synthesized from the elemental mixtures in ACl flux (A = Rb, Cs) and crystallized in the orthorhombic space group Cmcm, with a = 4.620(2)-4.504(2) Å, b = 16.232(8)-16.027(8) Å, c = 18.84(1)-18.32(2) and Z = 4, are isostructural to RbSm2Ag3Se5. These isostructural ARE2Ag3Te5 feature a three-dimensional tunnel framework constructed by ionically bound RETe6 octahedron and covalently bound AgTe4 tetrahedron in which tunnels are filled by A. Typical semiconducting behavior is revealed by the electrical conductivity, Seebeck coefficient, optical band gap measurement, and the theoretical calculations. The undoped sintered polycrystalline pellets of CsRE2Ag3Te5 (containing 1.1-1.7% CsCl impurity) show very low electrical conductivity (σr.t. = 0.5-2.4 S/cm), very low thermal conductivity (kr,t = 0.66-0.53 W/(m·K)), and moderate Seebeck coefficient (160-200 μV/K at 700 K).

Nano- and Microstructure Engineering: An Effective Method for Creating High Efficiency Magnesium Silicide Based Thermoelectrics.

PubMed

Farahi, Nader; Prabhudev, Sagar; Botton, Gianluigi A; Salvador, James R; Kleinke, Holger

2016-12-21

Considering the effect of CO 2 emission together with the depletion of fossil fuel resources on future generations, industries in particular the transportation sector are in deep need of a viable solution to follow the environmental regulation to limit the CO 2 emission. Thermoelectrics may be a practical choice for recovering the waste heat, provided their conversion energy can be improved. Here, the high temperature thermoelectric properties of high purity Bi doped Mg 2 (Si,Sn) are presented. The samples Mg 2 Si 1-x-y Sn x Bi y with x(Sn) ≥ 0.6 and y(Bi) ≥ 0.03 exhibited electrical conductivities and Seebeck coefficients of approximately 1000 Ω -1 cm -1 and -200 μV K -1 at 773 K, respectively, attributable to a combination of band convergence and microstructure engineering through ball mill processing. In addition to the high electrical conductivity and Seebeck coefficient, the thermal conductivity of the solid solutions reached values below 2.5 W m -1 K -1 due to highly efficient phonon scattering from mass fluctuation and grain boundary effects. These properties combined for zT values of 1.4 at 773 K with an average zT of 0.9 between 400 and 773 K. The transport properties were both highly reproducible across several measurement systems and were stable with thermal cycling.

Transport properties of CO2-bearing MgSiO3 melt at mantle conditions

NASA Astrophysics Data System (ADS)

Ghosh, D. B.; Karki, B. B.

2017-12-01

Carbon dioxide, generally considered as the second most abundant volatile component in silicate magmas, is expected to significantly influence various melt properties. In particular, our knowledge about its dynamical effects is lacking over most of the Earth's mantle pressure regime. Here we report the first-principles molecular dynamics results on the transport properties of carbonated MgSiO3 liquid under the conditions of mantle relevance. They show that dissolved CO2 systematically enhances the diffusion rates of all elements and the associated electrical conductivity and lowers the melt viscosity on average by factors of 1.5 to 3 over the pressure range considered. They also predict anomalous dynamical behavior - increasing diffusivity and conductivity, and decreasing viscosity with compression in the low pressure regime. We attempt to link the predicted transport coefficients to the microsocopic structural changes that occur in response to pressure and temperature. This anomaly and the concomitant increase of pressure and temperature with depth together make these transport coefficients vary modestly over extended portions of the mantle regime. It is possible that the melt electrical conductivity at conditions corresponding to the 410 and 660 km seismic discontinuities is at a detectable level by electromagnetic sounding observation. Also, the low melt viscosity values 0.2-0.5 Pa s at these depths and near the core-mantle boundary may imply high mobility of possible melts in these regions.

On chemical reaction and porous medium effect in the MHD flow due to a rotating disk with variable thickness

NASA Astrophysics Data System (ADS)

Hayat, Tasawar; Nazar, Hira; Imtiaz, Maria; Alsaedi, Ahmed

2017-06-01

The present analysis describes the magnetohydrodynamic (MHD) axisymmetric flow of a viscous fluid due to a rotating disk with variable thickness. An electrically conducting fluid fills the porous space. The first-order chemical reaction is considered. The equations of the present problem representing the flow of a fluid are reduced into nonlinear ordinary differential equations. Convergent series solutions are obtained. The impacts of the various involved dimensionless parameters on fluid flow, temperature, concentration, skin frction coefficient and Nusselt number are examined. The radial, tangential and axial components of velocity are affected in a similar manner on changing the thickness coefficient of the disk. Similar effects of the disk thickness coefficient are observed for both the temperature and concentration profile.

The theoretical ultimate magnetoelectric coefficients of magnetoelectric composites by optimization design

NASA Astrophysics Data System (ADS)

Wang, H.-L.; Liu, B.

2014-03-01

This paper investigates what is the largest magnetoelectric (ME) coefficient of ME composites, and how to realize it. From the standpoint of energy conservation, a theoretical analysis is carried out on an imaginary lever structure consisting of a magnetostrictive phase, a piezoelectric phase, and a rigid lever. This structure is a generalization of various composite layouts for optimization on ME effect. The predicted theoretical ultimate ME coefficient plays a similar role as the efficiency of ideal heat engine in thermodynamics, and is used to evaluate the existing typical ME layouts, such as the parallel sandwiched layout and the serial layout. These two typical layouts exhibit ME coefficient much lower than the theoretical largest values, because in the general analysis the stress amplification ratio and the volume ratio can be optimized independently and freely, but in typical layouts they are dependent or fixed. To overcome this shortcoming and achieve the theoretical largest ME coefficient, a new design is presented. In addition, it is found that the most commonly used electric field ME coefficient can be designed to be infinitely large. We doubt the validity of this coefficient as a reasonable ME effect index and consider three more ME coefficients, namely the electric charge ME coefficient, the voltage ME coefficient, and the static electric energy ME coefficient. We note that the theoretical ultimate value of the static electric energy ME coefficient is finite and might be a more proper measure of ME effect.

The theoretical ultimate magnetoelectric coefficients of magnetoelectric composites by optimization design

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wang, H.-L.; Liu, B., E-mail: liubin@tsinghua.edu.cn

2014-03-21

This paper investigates what is the largest magnetoelectric (ME) coefficient of ME composites, and how to realize it. From the standpoint of energy conservation, a theoretical analysis is carried out on an imaginary lever structure consisting of a magnetostrictive phase, a piezoelectric phase, and a rigid lever. This structure is a generalization of various composite layouts for optimization on ME effect. The predicted theoretical ultimate ME coefficient plays a similar role as the efficiency of ideal heat engine in thermodynamics, and is used to evaluate the existing typical ME layouts, such as the parallel sandwiched layout and the serial layout.more » These two typical layouts exhibit ME coefficient much lower than the theoretical largest values, because in the general analysis the stress amplification ratio and the volume ratio can be optimized independently and freely, but in typical layouts they are dependent or fixed. To overcome this shortcoming and achieve the theoretical largest ME coefficient, a new design is presented. In addition, it is found that the most commonly used electric field ME coefficient can be designed to be infinitely large. We doubt the validity of this coefficient as a reasonable ME effect index and consider three more ME coefficients, namely the electric charge ME coefficient, the voltage ME coefficient, and the static electric energy ME coefficient. We note that the theoretical ultimate value of the static electric energy ME coefficient is finite and might be a more proper measure of ME effect.« less

A lightweight scalable agarose-gel-synthesized thermoelectric composite

NASA Astrophysics Data System (ADS)

Kim, Jin Ho; Fernandes, Gustavo E.; Lee, Do-Joong; Hirst, Elizabeth S.; Osgood, Richard M., III; Xu, Jimmy

2018-03-01

Electronic devices are now advancing beyond classical, rigid systems and moving into lighweight flexible regimes, enabling new applications such as body-wearables and ‘e-textiles’. To support this new electronic platform, composite materials that are highly conductive yet scalable, flexible, and wearable are needed. Materials with high electrical conductivity often have poor thermoelectric properties because their thermal transport is made greater by the same factors as their electronic conductivity. We demonstrate, in proof-of-principle experiments, that a novel binary composite can disrupt thermal (phononic) transport, while maintaining high electrical conductivity, thus yielding promising thermoelectric properties. Highly conductive Multi-Wall Carbon Nanotube (MWCNT) composites are combined with a low-band gap semiconductor, PbS. The work functions of the two materials are closely matched, minimizing the electrical contact resistance within the composite. Disparities in the speed of sound in MWCNTs and PbS help to inhibit phonon propagation, and boundary layer scattering at interfaces between these two materials lead to large Seebeck coefficient (> 150 μV/K) (Mott N F and Davis E A 1971 Electronic Processes in Non-crystalline Materials (Oxford: Clarendon), p 47) and a power factor as high as 10 μW/(K2 m). The overall fabrication process is not only scalable but also conformal and compatible with large-area flexible hosts including metal sheets, films, coatings, possibly arrays of fibers, textiles and fabrics. We explain the behavior of this novel thermoelectric material platform in terms of differing length scales for electrical conductivity and phononic heat transfer, and explore new material configurations for potentially lightweight and flexible thermoelectric devices that could be networked in a textile.

Thermoelectric Properties of Lanthanum Sulfide

NASA Technical Reports Server (NTRS)

Wood, C.; Lockwood, R.; Parker, J. B.; Zoltan, A.; Zoltan, L. D.; Danielson, L.; Raag, V.

1987-01-01

Report describes measurement of Seebeck coefficient, electrical resistivity, thermal conductivity, and Hall effect in gamma-phase lanthanum sulfide with composition of La3-x S4. Results of study, part of search for high-temperature thermoelectric energy-conversion materials, indicate this sulfide behaves like extrinsic semiconductor over temperature range of 300 to 1,400 K, with degenerate carrier concentration controlled by stoichiometric ratio of La to S.

Electronic, thermoelectric and transport properties of cesium cadmium trifluoride: A DFT study

NASA Astrophysics Data System (ADS)

Abraham, Jisha Annie; Pagare, G.; Sanyal, Sankar P.

2018-04-01

The full potential linearized augmented plane wave method based on density functional theory is employed to investigate the electronic structure of CsCdF3. The electronic properties of this compound have been studied from the band structure plot and density of states. The presence of indirect energy gap reveals its insulating nature. Using constant relaxation time, the electrical conductivity, electronic thermal conductivity, Seebeck coefficient and figure of merit are calculated by using Boltzmann transport theory. We have also studied the temperature dependence of thermoelectric properties of this compound.

T700 power turbine rotor multiplane/multispeed balancing demonstration

NASA Technical Reports Server (NTRS)

Burgess, G.; Rio, R.

1979-01-01

Research was conducted to demonstrate the ability of influence coefficient based multispeed balancing to control rotor vibration through bending criticals. Rotor dynamic analyses were conducted of the General Electric T700 power turbine rotor. The information was used to generate expected rotor behavior for optimal considerations in designing a balance rig and a balance technique. The rotor was successfully balanced 9500 rpm. Uncontrollable coupling behavior prevented observations through the 16,000 rpm service speed. The balance technique is practical and with additional refinement it can meet production standards.

Electrical conductivity and thermopower of (1 - x) BiFeO(3) - xBi(0.5)K(0.5)TiO3 (x = 0.1, 0.2) ceramics near the ferroelectric to paraelectric phase transition.

PubMed

Wefring, E T; Einarsrud, M-A; Grande, T

2015-04-14

Ferroelectric BiFeO3 has attractive properties such as high strain and polarization, but a wide range of applications of bulk BiFeO3 are hindered due to high leakage currents and a high coercive electric field. Here, we report on the thermal behaviour of the electrical conductivity and thermopower of BiFeO3 substituted with 10 and 20 mol% Bi0.5K0.5TiO3. A change from p-type to n-type conductivity in these semi-conducting materials was demonstrated by the change in the sign of the Seebeck coefficient and the change in the slope of the isothermal conductivity versus partial pressure of O. A minimum in the isothermal conductivity was observed at ∼10(-2) bar O2 partial pressure for both solid solutions. The strong dependence of the conductivity on the partial pressure of O2 was rationalized by a point defect model describing qualitatively the conductivity involving oxidation/reduction of Fe(3+), the dominating oxidation state of Fe in stoichiometric BiFeO3. The ferroelectric to paraelectric phase transition of 80 and 90 mol% BiFeO3 was observed at 648 ± 15 and 723 ± 15 °C respectively by differential thermal analysis and confirmed by dielectric spectroscopy and high temperature powder X-ray diffraction.

Thermal and electrical transport in metals and superconductors across antiferromagnetic and topological quantum transitions

NASA Astrophysics Data System (ADS)

Chatterjee, Shubhayu; Sachdev, Subir; Eberlein, Andreas

2017-08-01

We study thermal and electrical transport in metals and superconductors near a quantum phase transition where antiferromagnetic order disappears. The same theory can also be applied to quantum phase transitions involving the loss of certain classes of intrinsic topological order. For a clean superconductor, we recover and extend well-known universal results. The heat conductivity for commensurate and incommensurate antiferromagnetism coexisting with superconductivity shows a markedly different doping dependence near the quantum critical point, thus allowing us to distinguish between these states. In the dirty limit, the results for the conductivities are qualitatively similar for the metal and the superconductor. In this regime, the geometric properties of the Fermi surface allow for a very good phenomenological understanding of the numerical results on the conductivities. In the simplest model, we find that the conductivities do not track the doping evolution of the Hall coefficient, in contrast to recent experimental findings. We propose a doping dependent scattering rate, possibly due to quenched short-range charge fluctuations below optimal doping, to consistently describe both the Hall data and the longitudinal conductivities.

Top electrode size effects in the piezoresponse force microscopy of piezoelectric thin films attached to a rigid substrate

NASA Astrophysics Data System (ADS)

Wang, J. H.

2017-10-01

In order to avoid the highly concentrated electric field induced beneath the sharp tip, the technique using a top coating electrode in the piezoresponse force microscopy (PFM) has been developed to detect the piezoelectric coefficients. Reliable theory should be erected to explain the broadly reported top electrode size effects and relate the responses with material constants. In this paper, the surface displacement, electric potential inside the film, electric charge and effective piezoelectric coefficient are expressed as a set of integral equations. Analytical solutions are obtained for two limiting cases, i.e., half space (HS) and infinitely thin film (IT). The effective piezoelectric coefficient of the HS case is proved to be the same as that from the PFM of a piezoelectric half plane without a top coating. For the IT case, it is identical to the well-known piezoelectric coefficient result of piezoelectric thin film clamped between flat rigid electrodes subject to homogeneous external electric field. For PZT4 thin layer, numerical results reveal that the surface displacement obviously decreases and the electric potential distributions inside the film become more and more homogeneous as the electrode radius to film thickness ratio (a/t) enlarges. The electric charge dramatically increases while the effective piezoelectric coefficient evidently decreases and they both transfer from the HS solutions to the IT results when a/t varies from 0.001 to 20. The transition occurs at about a/t = 1 in agreement with the experimental observations. A critical top electrode size, i.e., a/t > 10, is obtained and applicable to other piezoelectric materials. Under such circumstances, one can readily gain the piezoelectric coefficients e 33, d 33 and the dielectric coefficient {\\in }33 if other mechanical coefficients and one piezoelectric constant are known a prior.

Apparatus for measuring Seebeck coefficient and electrical resistivity of small dimension samples using infrared microscope as temperature sensor.

PubMed

Jaafar, W M N Wan; Snyder, J E; Min, Gao

2013-05-01

An apparatus for measuring the Seebeck coefficient (α) and electrical resistivity (ρ) was designed to operate under an infrared microscope. A unique feature of this apparatus is its capability of measuring α and ρ of small-dimension (sub-millimeter) samples without the need for microfabrication. An essential part of this apparatus is a four-probe assembly that has one heated probe, which combines the hot probe technique with the Van der Pauw method for "simultaneous" measurements of the Seebeck coefficient and electrical resistivity. The repeatability of the apparatus was investigated over a temperature range of 40 °C-100 °C using a nickel plate as a standard reference. The results show that the apparatus has an uncertainty of ±4.9% for Seebeck coefficient and ±5.0% for electrical resistivity. The standard deviation of the apparatus against a nickel reference sample is -2.43 μVK(-1) (-12.5%) for the Seebeck coefficient and -0.4 μΩ cm (-4.6%) for the electrical resistivity, respectively.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Nieroda, Pawel; Zybala, Rafal; Wojciechowski, Krzysztof T.

The aim of the study was to develop a fast and simple method for preparation of polycrystalline Mg{sub 2}Si. For this purpose a Spark Plasma Sintering (SPS) method was used and synthesis conditions were adjusted in such a manner that no excess Mg was required. Materials were synthesized by the direct reaction of Mg and Si raw powders. To determine the phase and chemical composition, the fabricated samples were studied by X-ray diffraction and SEM microscopy coupled with EDX chemical analysis. Thermoelectric properties of samples (thermal conductivity, electrical conductivity and Seebeck coefficient) were measured all over temperature range of 300-650more » K. The analysis by the scanning thermoelectric microprobe (STM) shows that samples have uniform distribution of Seebeck coefficient with mean value of about -405 {mu}VK{sup -1} and standard deviation of 94 {mu}VK{sup -1}. Prepared materials have intrinsic band gap of 0.45 eV and thermal conductivity {lambda}= 7.5 Wm{sup -1}K{sup -1} at room temperature.« less

Systematic study of the elastic, optoelectronic, and thermoelectric behavior of MRh2O4 (M = Zn, Cd) based on first principles calculations

NASA Astrophysics Data System (ADS)

Abbas, Syed Adeel; Rashid, Muhammad; Faridi, Muhammad Ayub; Saddique, Muhammad Bilal; Mahmood, Asif; Ramay, Shahid Muhammad

2018-02-01

In the present study, we performed first principles total energy calculations to explore the electronic, elastic, optical, and thermoelectric behavior of MRh2O4(M = Zn, Cd) spinel oxides. We employed Perdew-Burke-Ernzerhof-sol as well as the modified Becke and Johnson potential to compute the elastic, optoelectronic, and thermoelectric behavior of MRh2O4(M = Zn, Cd). The optical behavior was investigated by calculating the complex dielectric constant, refractive index, optical reflectivity, absorption coefficient, and optical conductivity. All of the optical parameters indicated a shift to lower energies as the atomic size increased from Zn to Cd, thereby suggesting potential applications of the spinel oxides in optoelectronic device. Moreover, the thermoelectric properties of MRh2O4(M = Zn, Cd) spinel oxides were computed in terms of the electrical conductivity (σ), Seebeck coefficient (S), thermal conductivity (k), and power factor (σS2) using the BoltzTraP code.

Electrical resistivity of CuAlMo thin films grown at room temperature by dc magnetron sputtering

NASA Astrophysics Data System (ADS)

Birkett, Martin; Penlington, Roger

2016-07-01

We report on the thickness dependence of electrical resistivity of CuAlMo films grown by dc magnetron sputtering on glass substrates at room temperature. The electrical resistance of the films was monitored in situ during their growth in the thickness range 10-1000 nm. By theoretically modelling the evolution of resistivity during growth we were able to gain an insight into the dominant electrical conduction mechanisms with increasing film thickness. For thicknesses in the range 10-25 nm the electrical resistivity is found to be a function of the film surface roughness and is well described by Namba’s model. For thicknesses of 25-40 nm the experimental data was most accurately fitted using the Mayadas and Shatkes model which accounts for grain boundary scattering of the conduction electrons. Beyond 40 nm, the thickness of the film was found to be the controlling factor and the Fuchs-Sonheimer (FS) model was used to fit the experimental data, with diffuse scattering of the conduction electrons at the two film surfaces. By combining the Fuchs and Namba (FN) models a suitable correlation between theoretical and experimental resistivity can be achieved across the full CuAlMo film thickness range of 10-1000 nm. The irreversibility of resistance for films of thickness >200 nm, which demonstrated bulk conductivity, was measured to be less than 0.03% following subjection to temperature cycles of -55 and +125 °C and the temperature co-efficient of resistance was less than ±15 ppm °C-1.

18O-tracer diffusion along nanoscaled Sc2O3/yttria stabilized zirconia (YSZ) multilayers: on the influence of strain.

PubMed

Aydin, Halit; Korte, Carsten; Janek, Jürgen

2013-06-01

The oxygen tracer diffusion coefficient describing transport along nano-/microscaled YSZ/Sc 2 O 3 multilayers as a function of the thick-ness of the ion-conducting YSZ layers has been measured by isotope exchange depth profiling (IEDP), using secondary ion mass spec-trometry (SIMS). The multilayer samples were prepared by pulsed laser deposition (PLD) on (0001) Al 2 O 3 single crystalline substrates. The values for the oxygen tracer diffusion coefficient were analyzed as a combination of contributions from bulk and interface contributions and compared with results from YSZ/Y 2 O 3 -multilayers with similar microstructure. Using the Nernst-Einstein equation as the relation between diffusivity and electrical conductivity we find very good agreement between conductivity and diffusion data, and we exclude substantial electronic conductivity in the multilayers. The effect of hetero-interface transport can be well explained by a simple interface strain model. As the multilayer samples consist of columnar film crystallites with a defined inter-face structure and texture, we also discuss the influence of this particular microstructure on the interfacial strain.

Effects of Pd substitution on the thermoelectric and electronic properties of delafossite Cu{sub 1−x}Pd{sub x}FeO{sub 2} (x=0.01, 0.03 and 0.05)

DOE Office of Scientific and Technical Information (OSTI.GOV)

Ruttanapun, Chesta, E-mail: chesta.ruttanapun@gmail.com

Cu{sub (1−x)}Pd{sub (x)}FeO{sub 2} (x=0.01, 0.03 and 005) delafossite was prepared by solid state reactions and was calcined/sintered at 1050 °C. The effect of Pd{sup 2+} substitution for the Cu{sup 1+} sites on the thermoelectric and electronic properties of Cu{sub (1−x)}Pd{sub (x)}FeO{sub 2} were investigated. The crystal structure, oxygen decomposition, thermoelectric and electronic properties were characterized by X-ray diffraction, thermogravimetric analysis, X-ray photoelectron spectroscopy (XPS), Seebeck coefficient, electrical conductivity and thermal conductivity measurements. The characterization showed that Cu{sub (1−x)}Pd{sub (x)}FeO{sub 2} formed a hexagonal delafossite structure with R3−m symmetry. The existence of Pd{sup 2+}, Cu{sup 1+}, Cu{sup 2+}, Fe{sup 3+},more » Fe{sup 4+} and O was revealed from the XPS results. Confirmation of Pd{sup 2+} substitution for the Cu{sup 1+} sites occurred by increasing the c-axis in the lattice parameter with a Pd content. The O content intercalated at the center of the triangular Cu acted as a support to produce Cu{sup 2+} ions and was reduced with an increasing Pd content. The mixed valencies of Cu{sup 1+}/Cu{sup 2+} and Cu{sup 1+}/Pd{sup 2+} in the Cu layer changed the electrical conductivity and the Fe{sup 3+}/Fe{sup 4+} mixed valencies in the FeO{sub 6} layer caused the Seebeck coefficient to increase. Both the electrical conductivity and Seebeck coefficient for Pd contents of x=0.01 and 0.03 were higher than that of non-doped CuFeO{sub 2}. The low thermal conductivity of Cu{sub (1−x)}Pd{sub (x)}FeO{sub 2} resulted from the substitution of Pd, which has a large atomic mass, into structure. The Jonker plot indicated that the electronic properties displayed a degenerate density of states and that Cu{sub (1−x)}Pd{sub (x)}FeO{sub 2} was a semiconductor. A high ZT value of 0.055 was obtained for a Pd content of 0.03 at 950 K. The Pd{sup 2+} substitution for the Cu{sup 1+} sites influenced the thermoelectric and electronic properties of the delafossite Cu{sub (1−x)}Pd{sub (x)}FeO{sub 2} samples. - Graphical abstract: Cu{sub (1−x)}Pd{sub (x)}FeO{sub 2} (x=0.01, 0.03 and 005) delafossite was prepared by solid state reactions. The characterization showed that Cu{sub (1−x)}Pd{sub (x)}FeO{sub 2} formed a hexagonal delafossite structure with R3−m symmetry. The existence of Pd{sup 2+}, Cu{sup 1+}, Cu{sup 2+}, Fe{sup 3+}, Fe{sup 4+} and O was revealed from the XPS results. The O content intercalated at the center of the triangular Cu acted as a support to produce Cu{sup 2+} ions and was reduced with an increasing Pd content. The mixed valencies of Cu{sup 1+}/Cu{sup 2+} and Cu{sup 1+}/Pd{sup 2+} in the Cu layer changed the electrical conductivity and the Fe{sup 3+}/Fe{sup 4+} mixed valencies in the FeO{sub 6} layer caused the Seebeck coefficient to increase. Both the electrical conductivity and Seebeck coefficient for Pd contents of x=0.01 and 0.03 were higher than that of non-doped CuFeO{sub 2}. The low thermal conductivity of Cu{sub (1−x)}Pd{sub (x)}FeO{sub 2} resulted from the substitution of Pd, which has a large atomic mass, into structure. A high ZT value of 0.055 was obtained for a Pd content of 0.03 at 950 K. The Pd{sup 2+} substitution for the Cu{sup 1+} sites influenced the thermoelectric and electronic properties of the delafossite Cu{sub (1−x)}Pd{sub (x)}FeO{sub 2} samples. - Highlights: • New compound of Cu{sub 1−x}Pd{sub x}FeO{sub 2} (x=0.01, 0.03 and 0.05) forms phase of delafossite. • The compound displays p-type thermoelectric materials. • The Pd-substituted for Cu{sup 1+} sites forms Pd{sup 2+}. • Mixed valencies of Cu{sup +}/Cu{sup 2+}, Cu{sup +}/Pd{sup 2+} and Fe{sup 3+}/Fe{sup 4+} appear in the compound. • Large atomic mass of Pd-substituted causes low thermal conductivity.« less

Electronic Structure, Optical and Transport Properties of Double Perovskite La2NbMnO6: A Theoretical Understanding from DFT Calculations

NASA Astrophysics Data System (ADS)

Parrey, Khursheed Ahmad; Khandy, Shakeel Ahmad; Islam, Ishtihadah; Laref, Amel; Gupta, Dinesh C.; Niazi, Asad; Aziz, Anver; Ansari, S. G.; Khenata, R.; Rubab, Seemin

2018-03-01

Double perovskite La2NbMnO6 was systematically studied using the first-principles calculations. The structural, electronic, optical and transport properties of this compound were calculated. Spin resolved band structure predicted this material as a half-metal with an energy gap of 3.75 eV in spin down state. The optical coefficients including optical conductivity, reflectivity and electron energy loss are calculated for photon energy up to 30.00 eV to understand the optical response of this perovskite. The strong absorption of all the ultraviolet and infrared frequencies of the spectrum by this material may suggest the potential application of this material for the optoelectronic devices in ultraviolet and infra-red region. Also, the thermoelectric properties with a speculation from the half-metallic electronic structure are reported. Subsequently, the Seebeck coefficient, electrical and thermal conductivity coefficients are calculated to predict the thermoelectric figure of merit (zT), the maximum of which is found out to be 0.14 at 800 K.

Thermoelectric Properties in Fermi Level Tuned Topological Materials (Bi1-xSnx)2Te3

NASA Astrophysics Data System (ADS)

Lin, Chan-Chieh; Shon, Won Hyuk; Rathnam, Lydia; Rhyee, Jong-Soo

2018-03-01

We investigated the thermoelectric properties of Sn-doped (Bi1-xSnx)2Te3 (x = 0, 0.1, 0.3, 0.5, and 0.7%) compounds, which is known as topological insulators. Fermi level tuning by Sn-doping can be justified by the n- to p-type transition with increasing Sn-doping concentration, as confirmed by Seebeck coefficient and Hall coefficient. Near x = 0.3 and 0.5%, the Fermi level resides inside the bulk band gap, resulting in a low Seebeck coefficient and increase of electrical resistivity. The magnetoconductivity with applying magnetic field showed weak antilocalization (WAL) effect for pristine Bi2Te3 while Sn-doped compounds do not follow the WAL behavior of magneto-conductivity, implying that the topological surface Dirac band contribution in magneto-conductivity is suppressed with decreasing the Fermi level by Sn-doping. This research can be applied to the topological composite of p-type/n-type topological materials by Fermi level tuning via Sn-doping in Bi2Te3 compounds.

U(1) current from the AdS/CFT: diffusion, conductivity and causality

NASA Astrophysics Data System (ADS)

Bu, Yanyan; Lublinsky, Michael; Sharon, Amir

2016-04-01

For a holographically defined finite temperature theory, we derive an off-shell constitutive relation for a global U(1) current driven by a weak external non-dynamical electromagnetic field. The constitutive relation involves an all order gradient expansion resummed into three momenta-dependent transport coefficient functions: diffusion, electric conductivity, and "magnetic" conductivity. These transport functions are first computed analytically in the hydrodynamic limit, up to third order in the derivative expansion, and then numerically for generic values of momenta. We also compute a diffusion memory function, which, as a result of all order gradient resummation, is found to be causal.

Thermoelectric Properties of the Ca1- x R x MnO3 Perovskite System (R: Pr, Nd, Sm) for High-Temperature Applications

NASA Astrophysics Data System (ADS)

Choi, Soon-Mok; Lim, Chang-Hyun; Seo, Won-Seon

2011-05-01

Perovskite oxides have attracted considerable attention in the area of thermoelectrics owing to the advantages of their isotropic crystal structure and straightforward control of their electrical properties. Among the many perovskites, different types of polycrystalline Ca1- x R x MnO3 (R: Pr, Nd, Sm) were prepared by solid-state reaction in this study. Three different rare-earth dopants were substituted at the Ca-ion site at various amounts. Considering phase stability, rare-earth ions with nearly the same ionic radius as Ca2+ were selected. To assess thermoelectric performance, the electrical conductivity, Seebeck coefficient, and power factor were measured, and phase analysis was conducted. The effects of ionic radius variation on single phase formation and the effect of doping amount on carrier concentration are discussed.

Simulation Study to Improve Focalization of a Figure Eight Coil by Using a Conductive Shield Plate and a Ferromagnetic Block.

PubMed

Zhao, Chen; Zhang, Shunqi; Liu, Zhipeng; Yin, Tao

2015-07-01

A new method to improve the focalization and efficiency of the Figure of Eight (FOE) coil in rTMS is discussed in this paper. In order to decrease the half width of the distribution curve (HWDC), as well to increase the ratio of positive peak value to negative peak value (RPN) of the induced electric field, a shield plate with a window and a ferromagnetic block are assumed to enhance the positive peak value of the induced electrical field. The shield is made of highly conductive copper, and the block is made of highly permeable soft magnetic ferrite. A computer simulation is conducted on ANSYS® software to conduct the finite element analysis (FEA). Two comparing coefficients were set up to optimize the sizes of the shield window and the block. Simulation results show that a shield with a 60 mm × 30 mm sized window, together with a block 40 mm thick, can decrease the focal area of a FOE coil by 46.7%, while increasing the RPN by 135.9%. The block enhances the peak value of the electrical field induced by a shield-FOE by 8.4%. A real human head model was occupied in this paper to further verify our method.

Preparation and Dielectric Properties of SiC/LSR Nanocomposites for Insulation of High Voltage Direct Current Cable Accessories

PubMed Central

Shang, Nanqiang; Chen, Qingguo; Wei, Xinzhe

2018-01-01

The conductivity mismatch in the composite insulation of high voltage direct current (HVDC) cable accessories causes electric field distribution distortion and even insulation breakdown. Therefore, a liquid silicone rubber (LSR) filled with SiC nanoparticles is prepared for the insulation of cable accessories. The micro-morphology of the SiC/LSR nanocomposites is observed by scanning electron microscopy, and their trap parameters are characterized using thermal stimulated current (TSC) tests. Moreover, the dielectric properties of SiC/LSR nanocomposites with different SiC concentrations are tested. The results show that the 3 wt % SiC/LSR sample has the best nonlinear conductivity, more than one order of magnitude higher than that of pure LSR with improved temperature and nonlinear conductivity coefficients. The relative permittivity increased 0.2 and dielectric loss factor increased 0.003, while its breakdown strength decreased 5 kV/mm compared to those of pure LSR. Moreover, the TSC results indicate the introduction of SiC nanoparticles reduced the trap level and trap density. Furthermore, the SiC nanoparticles filling significantly increased the sensitivity of LSR to electric field stress and temperature changes, enhancing the conductivity and electric field distribution within the HVDC cable accessories, thus improving the reliability of the HVDC cable accessories. PMID:29518054

Preparation and Dielectric Properties of SiC/LSR Nanocomposites for Insulation of High Voltage Direct Current Cable Accessories.

PubMed

Shang, Nanqiang; Chen, Qingguo; Wei, Xinzhe

2018-03-08

The conductivity mismatch in the composite insulation of high voltage direct current (HVDC) cable accessories causes electric field distribution distortion and even insulation breakdown. Therefore, a liquid silicone rubber (LSR) filled with SiC nanoparticles is prepared for the insulation of cable accessories. The micro-morphology of the SiC/LSR nanocomposites is observed by scanning electron microscopy, and their trap parameters are characterized using thermal stimulated current (TSC) tests. Moreover, the dielectric properties of SiC/LSR nanocomposites with different SiC concentrations are tested. The results show that the 3 wt % SiC/LSR sample has the best nonlinear conductivity, more than one order of magnitude higher than that of pure LSR with improved temperature and nonlinear conductivity coefficients. The relative permittivity increased 0.2 and dielectric loss factor increased 0.003, while its breakdown strength decreased 5 kV/mm compared to those of pure LSR. Moreover, the TSC results indicate the introduction of SiC nanoparticles reduced the trap level and trap density. Furthermore, the SiC nanoparticles filling significantly increased the sensitivity of LSR to electric field stress and temperature changes, enhancing the conductivity and electric field distribution within the HVDC cable accessories, thus improving the reliability of the HVDC cable accessories.

Transport Properties of the Nuclear Pasta Phase with Quantum Molecular Dynamics

NASA Astrophysics Data System (ADS)

Nandi, Rana; Schramm, Stefan

2018-01-01

We study the transport properties of nuclear pasta for a wide range of density, temperature, and proton fractions, relevant for different astrophysical scenarios adopting a quantum molecular dynamics model. In particular, we estimate the values of shear viscosity as well as electrical and thermal conductivities by calculating the static structure factor S(q) using simulation data. In the density and temperature range where the pasta phase appears, the static structure factor shows irregular behavior. The presence of a slab phase greatly enhances the peak in S(q). However, the effect of irregularities in S(q) on the transport coefficients is not very dramatic. The values of all three transport coefficients are found to have the same orders of magnitude as found in theoretical calculations for the inner crust matter of neutron stars without the pasta phase; therefore, the values are in contrast to earlier speculations that a pasta layer might be highly resistive, both thermally and electrically.

Analysis of Advanced Thermoelectric Materials and Their Functional Limits

NASA Technical Reports Server (NTRS)

Kim, Hyun Jung

2015-01-01

The world's demand for energy is increasing dramatically, but the best energy conversion systems operate at approximately 30% efficiency. One way to decrease energy loss is in the recovery of waste heat using thermoelectric (TE) generators. A TE generator is device that generates electricity by exploiting heat flow across a thermal gradient. The efficiency of a TE material for power generation and cooling is determined by the dimensionless Figure of Merit (ZT): ZT = S(exp. 2)sigmaT/?: where S is the Seebeck coefficient, sigma is the electrical conductivity, T is the absolute temperature, and ? is the thermal conductivity. The parameters are not physically independent, but intrinsically coupled since they are a function of the transport properties of electrons. Traditional research on TE materials has focused on synthesizing bulk semiconductor-type materials that have low thermal conductivity and high electrical conductivity affording ZT values of 1. The optimization of the s/? ratio is difficult to achieve using current material formats, as these material constants are complementary. Recent areas of research are focusing on using nanostructural artifacts that introduce specific dislocations and boundary conditions that scatter the phonons. This disrupts the physical link between thermal (phonon) and electrical (electron) transport. The result is that ? is decreased without decreasing s. These material formats give ZT values of up to 2 which represent approximately 18% energy gain from waste heat recovery. The next challenge in developing the next generation of TE materials with superior performance is to tailor the interconnected thermoelectric physical parameters of the material system. In order to approach this problem, the fundamental physics of each parameter S, sigma, and ? need to be physically understood in their context of electron/phonon interaction for the construction of new high ZT thermoelectric devices. Is it possible to overcome the physical limit imposed by of the effect of phonon lattice oscillation and energetic electrons towards thermal conductivity? Is the Seebeck coefficient, based on the difference in voltage over temperature gradient ( deltaV/deltaT), an intrinsic parameter of each material? All these parameters were manipulated using nano-bridge and twin-lattice structural concepts at the NASA Langley Research Center. This talk will review the current trend of TE research to optimize the ZT and discuss about new approaches on increasing ZT within functional limits of each parameter.

Thermoelectric Properties and Thermal Tolerance of Indium Tin Oxide Nanowires.

PubMed

Hernandez, Jose A; Carpena Nunez, Jennifer; Fonseca, Luis F; Pettes, Michael Thompson; Yacaman, Miguel Jose; Benitez, Alfredo

2018-06-14

Single-crystalline indium tin oxide (ITO) nanowires were grown via a vapor-liquid-solid (VLS) method, with thermal tolerance up to ~1300°C. We report the electric and thermoelectric properties of the ITO nanowires before and after heat treatments and draw conclusions about their applicability as thermoelectric building blocks in nanodevices that can operate in high temperature conditions. The Seebeck coefficient and the thermal and electrical conductivities were measured in each individual nanowire by means of specialized micro-bridge thermometry devices. Measured data was analyzed and explained in terms of changes in charge carrier density, impurities and vacancies due to the thermal treatments. © 2018 IOP Publishing Ltd.

Superionic phase transition in silver chalcogenide nanocrystals realizing optimized thermoelectric performance.

PubMed

Xiao, Chong; Xu, Jie; Li, Kun; Feng, Jun; Yang, Jinlong; Xie, Yi

2012-03-07

Thermoelectric has long been recognized as a potentially transformative energy conversion technology due to its ability to convert heat directly into electricity. However, how to optimize the three interdependent thermoelectric parameters (i.e., electrical conductivity σ, Seebeck coefficient S, and thermal conductivity κ) for improving thermoelectric properties is still challenging. Here, we put forward for the first time the semiconductor-superionic conductor phase transition as a new and effective way to selectively optimize the thermoelectric power factor based on the modulation of the electric transport property across the phase transition. Ultra low value of thermal conductivity was successfully retained over the whole investigated temperature range through the reduction of grain size. As a result, taking monodisperse Ag(2)Se nanocrystals for an example, the maximized ZT value can be achieved around the temperature of phase transition. Furthermore, along with the effective scattering of short-wavelength phonons by atomic defects created by alloying, the alloyed ternary silver chalcogenide compounds, monodisperse Ag(4)SeS nanocrystals, show better ZT value around phase transition temperature, which is cooperatively contributed by superionic phase transition and alloying at nanoscale. © 2012 American Chemical Society

Using Multivariate Geostatistics to Assess Patterns of Spatial Dependence of Apparent Soil Electrical Conductivity and Selected Soil Properties

PubMed Central

Siqueira, Glécio Machado; Dafonte, Jorge Dafonte; Valcárcel Armesto, Montserrat; Silva, Ênio Farias França e

2014-01-01

The apparent soil electrical conductivity (ECa) was continuously recorded in three successive dates using electromagnetic induction in horizontal (ECa-H) and vertical (ECa-V) dipole modes at a 6 ha plot located in Northwestern Spain. One of the ECa data sets was used to devise an optimized sampling scheme consisting of 40 points. Soil was sampled at the 0.0–0.3 m depth, in these 40 points, and analyzed for sand, silt, and clay content; gravimetric water content; and electrical conductivity of saturated soil paste. Coefficients of correlation between ECa and gravimetric soil water content (0.685 for ECa-V and 0.649 for ECa-H) were higher than those between ECa and clay content (ranging from 0.197 to 0.495, when different ECa recording dates were taken into account). Ordinary and universal kriging have been used to assess the patterns of spatial variability of the ECa data sets recorded at successive dates and the analyzed soil properties. Ordinary and universal cokriging methods have improved the estimation of gravimetric soil water content using the data of ECa as secondary variable with respect to the use of ordinary kriging. PMID:25614893

Using multivariate geostatistics to assess patterns of spatial dependence of apparent soil electrical conductivity and selected soil properties.

PubMed

Siqueira, Glécio Machado; Dafonte, Jorge Dafonte; Valcárcel Armesto, Montserrat; França e Silva, Ênio Farias

2014-01-01

The apparent soil electrical conductivity (ECa) was continuously recorded in three successive dates using electromagnetic induction in horizontal (ECa-H) and vertical (ECa-V) dipole modes at a 6 ha plot located in Northwestern Spain. One of the ECa data sets was used to devise an optimized sampling scheme consisting of 40 points. Soil was sampled at the 0.0-0.3 m depth, in these 40 points, and analyzed for sand, silt, and clay content; gravimetric water content; and electrical conductivity of saturated soil paste. Coefficients of correlation between ECa and gravimetric soil water content (0.685 for ECa-V and 0.649 for ECa-H) were higher than those between ECa and clay content (ranging from 0.197 to 0.495, when different ECa recording dates were taken into account). Ordinary and universal kriging have been used to assess the patterns of spatial variability of the ECa data sets recorded at successive dates and the analyzed soil properties. Ordinary and universal cokriging methods have improved the estimation of gravimetric soil water content using the data of ECa as secondary variable with respect to the use of ordinary kriging.

Crystal Structure and Thermoelectric Properties of β-Pyrochlore-Type Alkali Iron Tungsten Oxides with Cage-Like Structure

NASA Astrophysics Data System (ADS)

Mizuta, Kohei; Ohtaki, Michitaka

2016-03-01

We report the electrical and thermal properties of β-pyrochlore (defect pyrochlore) oxides AFe0.33W1.67O6 ( A = K, Rb, Cs) with a crystal structure having a small cation surrounded by oversized cage-like framework. The thermal conductivity, κ, of CsFe0.33W1.67O6 and RbFe0.33W1.67O6 showed extremely low values as oxides (below 1.0 W/mK) similar to those of ATaWO6 ( A = K, Rb, Cs) which we have already reported. These low κ values are ascribed to a "rattling" motion of the A cations, evidenced by their crystal structure refinement and the Raman spectra. Their electrical conductivity, σ, was in the order of 10-3 S/cm, and the Seebeck coefficient, S, was -500 to -600 μV/K. The electrical conductivity of AFe0.33W1.67O6 ( A = Rb, Cs) was much higher than those of ATaWO6 ( A = Rb, Cs), suggesting that an appropriate selection of the framework composition enables us to have better thermoelectric performance.

Electromagnetic reflection from multi-layered snow models

NASA Technical Reports Server (NTRS)

Linlor, W. I.; Jiracek, G. R.

1975-01-01

The remote sensing of snow-pack characteristics with surface installations or an airborne system could have important applications in water-resource management and flood prediction. To derive some insight into such applications, the electromagnetic response of multilayered snow models is analyzed in this paper. Normally incident plane waves at frequencies ranging from 1 MHz to 10 GHz are assumed, and amplitude reflection coefficients are calculated for models having various snow-layer combinations, including ice layers. Layers are defined by thickness, permittivity, and conductivity; the electrical parameters are constant or prescribed functions of frequency. To illustrate the effect of various layering combinations, results are given in the form of curves of amplitude reflection coefficients versus frequency for a variety of models. Under simplifying assumptions, the snow thickness and effective dielectric constant can be estimated from the variations of reflection coefficient as a function of frequency.

Estimation of soil-soil solution distribution coefficient of radiostrontium using soil properties.

PubMed

Ishikawa, Nao K; Uchida, Shigeo; Tagami, Keiko

2009-02-01

We propose a new approach for estimation of soil-soil solution distribution coefficient (K(d)) of radiostrontium using some selected soil properties. We used 142 Japanese agricultural soil samples (35 Andosol, 25 Cambisol, 77 Fluvisol, and 5 others) for which Sr-K(d) values had been determined by a batch sorption test and listed in our database. Spearman's rank correlation test was carried out to investigate correlations between Sr-K(d) values and soil properties. Electrical conductivity and water soluble Ca had good correlations with Sr-K(d) values for all soil groups. Then, we found a high correlation between the ratio of exchangeable Ca to Ca concentration in water soluble fraction and Sr-K(d) values with correlation coefficient R=0.72. This pointed us toward a relatively easy way to estimate Sr-K(d) values.

Ionic and electronic transport properties in dense plasmas by orbital-free density functional theory

DOE PAGES

Sjostrom, Travis; Daligault, Jérôme

2015-12-09

We validate the application of our recent orbital-free density functional theory (DFT) approach, [Phys. Rev. Lett. 113, 155006 (2014)], for the calculation of ionic and electronic transport properties of dense plasmas. To this end, we calculate the self-diffusion coefficient, the viscosity coefficient, the electrical and thermal conductivities, and the reflectivity coefficient of hydrogen and aluminum plasmas. Very good agreement is found with orbital-based Kohn-Sham DFT calculations at lower temperatures. Because the computational costs of the method do not increase with temperature, we can produce results at much higher temperatures than is accessible by the Kohn-Sham method. Our results for warmmore » dense aluminum at solid density are inconsistent with the recent experimental results reported by Sperling et al. [Phys. Rev. Lett. 115, 115001 (2015)].« less

Transport, Structural and Mechanical Properties of Quaternary FeVTiAl Alloy

NASA Astrophysics Data System (ADS)

Bhat, Tahir Mohiuddin; Gupta, Dinesh C.

2016-11-01

The electronic, structural, magnetic and transport properties of FeVTiAl quaternary alloy have been investigated within the framework of density functional theory. The material is a completely spin-polarized half-metallic ferromagnet in its ground state with F-43m structure. The structural stability was further confirmed by elastic constants in the cubic phase with high Young's modulus and brittle nature. The present study predicts an energy band gap of 0.72 eV in a localized minority spin channel at equilibrium lattice parameter of 6.00 Å. The transport properties of the material are discussed based on the Seebeck coefficient, and electrical and thermal conductivity coefficients. The alloy presents large values of Seebeck coefficients, ~39 μV K-1 at room temperature (300 K), and has an excellent thermoelectric performance with ZT = ~0.8.

Stefan-Maxwell Relations and Heat Flux with Anisotropic Transport Coefficients for Ionized Gases in a Magnetic Field with Application to the Problem of Ambipolar Diffusion

NASA Astrophysics Data System (ADS)

Kolesnichenko, A. V.; Marov, M. Ya.

2018-01-01

The defining relations for the thermodynamic diffusion and heat fluxes in a multicomponent, partially ionized gas mixture in an external electromagnetic field have been obtained by the methods of the kinetic theory. Generalized Stefan-Maxwell relations and algebraic equations for anisotropic transport coefficients (the multicomponent diffusion, thermal diffusion, electric and thermoelectric conductivity coefficients as well as the thermal diffusion ratios) associated with diffusion-thermal processes have been derived. The defining second-order equations are derived by the Chapman-Enskog procedure using Sonine polynomial expansions. The modified Stefan-Maxwell relations are used for the description of ambipolar diffusion in the Earth's ionospheric plasma (in the F region) composed of electrons, ions of many species, and neutral particles in a strong electromagnetic field.

Chemical Potential Evaluation of Thermoelectric and Mechanical Properties of Zr2CoZ (Z = Si, Ge) Heusler Alloys

NASA Astrophysics Data System (ADS)

Yousuf, Saleem; Gupta, Dinesh C.

2018-04-01

The electronic, mechanical and thermoelectric properties of Zr2CoZ (Z = Si, Ge) Heusler alloys are investigated by the full-potential linearized augmented plane wave method. Using the Voigt-Reuss approximation, we calculated the various elastic constants, the shear and Young's moduli, and Poisson's ratio which predict the ductile nature of the alloys. Thermoelectric coefficients viz., Seebeck, electrical conductivity and figure of merit show Zr2CoZ alloys as n-type thermoelectric materials showing a linearly increasing Seebeck coefficient with temperature mainly because of the existence of almost flat conduction bands along L to D directions of a high symmetry Brillouin zone. The efficiency of conversion was measured as the figure of merit by taking into effect the lattice thermal part that achieves an upper-limit of 0.14 at 1200 K which may favour their use for waste heat recovery at higher temperatures.

Thermophysical Properties of 60-NITINOL for Mechanical Component Applications

NASA Technical Reports Server (NTRS)

Stanford, Malcolm K.

2012-01-01

The linear thermal expansion coefficient, specific heat capacity, electrical resistivity and thermal conductivity of 60- NITINOL were studied over a range of temperatures representing the operating environment of an oil-lubricated bearing. The behavior of this material appears to follow wellestablished theories applicable to either metal alloys, in general, or to intermetallic compounds, more specifically and the measured data were found to be comparable to those for conventional bearing alloys.

Hydrothermal synthesis of stable metallic 1T phase WS2 nanosheets for thermoelectric application

NASA Astrophysics Data System (ADS)

Piao, Mingxing; Chu, Jin; Wang, Xiao; Chi, Yao; Zhang, Heng; Li, Chaolong; Shi, Haofei; Joo, Min-Kyu

2018-01-01

Two-dimensional materials have gained great attention as a promising thermoelectric (TE) material due to their unique density of state with confined electrons and holes. Here, we synthesized 1T phase tungsten disulfide (WS2) nanosheets with high TE performance via the hydrothermal method. Flexible WS2 nanosheets restacked thin films were fabricated by employing the vacuum filtration technique. The measured electrical conductivity was 45 S cm-1 with a Seebeck coefficient of +30 μV K-1 at room temperature, indicating a p-type characteristic. Furthermore, the TE performance could be further improved by thermal annealing treatment. It was found the electrical conductivity could be enhanced 2.7 times without sacrificing the Seebeck coefficient, resulting in the power factor of 9.40 μW m-1 K-2. Moreover, such 1T phase WS2 nanosheets possess high phase stability since the TE properties maintained constant at least half one year in the air atmosphere. Notably, other kinds of 1T phase transitional metal dichalcogenides (TMDCs) with excellent TE performance also could be imitated by using the procedure in this work. Finally, we believe a variety of materials based on 1T phase TMDCs nanosheets have great potential as candidate for future TE applications.

Calibration of a modified temperature-light intensity logger for quantifying water electrical conductivity

NASA Astrophysics Data System (ADS)

Gillman, M. A.; Lamoureux, S. F.; Lafrenière, M. J.

2017-09-01

The Stream Temperature, Intermittency, and Conductivity (STIC) electrical conductivity (EC) logger as presented by Chapin et al. (2014) serves as an inexpensive (˜50 USD) means to assess relative EC in freshwater environments. This communication demonstrates the calibration of the STIC logger for quantifying EC, and provides examples from a month long field deployment in the High Arctic. Calibration models followed multiple nonlinear regression and produced calibration curves with high coefficient of determination values (R2 = 0.995 - 0.998; n = 5). Percent error of mean predicted specific conductance at 25°C (SpC) to known SpC ranged in magnitude from -0.6% to 13% (mean = -1.4%), and mean absolute percent error (MAPE) ranged from 2.1% to 13% (mean = 5.3%). Across all tested loggers we found good accuracy and precision, with both error metrics increasing with increasing SpC values. During 10, month-long field deployments, there were no logger failures and full data recovery was achieved. Point SpC measurements at the location of STIC loggers recorded via a more expensive commercial electrical conductivity logger followed similar trends to STIC SpC records, with 1:1.05 and 1:1.08 relationships between the STIC and commercial logger SpC values. These results demonstrate that STIC loggers calibrated to quantify EC are an economical means to increase the spatiotemporal resolution of water quality investigations.

Effects of anhydrous AlCl3 dopant on the structural, optical and electrical properties of PVA-PVP polymer composite films

NASA Astrophysics Data System (ADS)

Shanmugam, G.; Krishnakumar, V.

2018-05-01

Polymer composite films based on PVA-PVP with AlCl3 as the dopant at different concentrations were prepared using solution casting technique. XRD patterns reveal the increase in amorphousity of the films with AlCl3 doping. Optical absorption studies exhibit that the values of optical absorption coefficient, direct and indirect optical band gaps are found to decrease with increase in AlCl3 concentration. It confirms the charge transfer in complexes between the polymer and the dopant. The dielectric studies show the increase in dielectric constant at low frequency with increasing AlCl3 concentration and temperature. The ac conductivity and ionic conductivity increase with the AlCl3 content and the maximum value at room temperature is found to be 6.89 × 10-4 and 8.05 × 10-5 S/cm for higher AlCl3 doped PVA-PVP film. The estimated ionic conductivity value is three or four orders of magnitude greater than those obtained in the certain representative polymer-salt complexes as reported earlier. Electrical modulus plots confirm the removal of electrode polarization and the low conductivity relaxation time with Al doping. The activation energy estimated from the temperature dependent dc conductivity plot is agreed well with the migration energy calculated from the temperature dependent electric modulus plot.

Foldable Thermoelectric Materials: Improvement of the Thermoelectric Performance of Directly Spun CNT Webs by Individual Control of Electrical and Thermal Conductivity.

PubMed

An, Cheng Jin; Kang, Young Hun; Lee, A-Young; Jang, Kwang-Suk; Jeong, Youngjin; Cho, Song Yun

2016-08-31

We suggest the fabrication of foldable thermoelectric (TE) materials by embedding conducting polymers into Au-doped CNT webs. The CNT bundles, which are interconnected by a direct spinning method to form 3D networks without interfacial contact resistance, provide both high electrical conductivity and high carrier mobility. The ZT value of the spun CNT web is significantly enhanced through two simple processes. Decorating the porous CNT webs with Au nanoparticles increases the electrical conductivity, resulting in an optimal ZT of 0.163, which represents a more than 2-fold improvement compared to the ZT of pristine CNT webs (0.079). After decoration, polyaniline (PANI) is integrated into the Au-doped CNT webs both to improve the Seebeck coefficient by an energy-filtering effect and to decrease the thermal conductivity by the phonon-scattering effect. This leads to a ZT of 0.203, which is one of the highest ZT values reported for organic TE materials. Moreover, Au-doped CNT/PANI web is ultralightweight, free-standing, thermally stable, and mechanically robust, which makes it a viable candidate for a hybrid TE conversion device for wearable electronics. When a 20 K temperature gradient is applied to the TE module consisting of seven p-n couples, 1.74 μW of power is generated.

Crystal Lattice Controlled SiGe Thermoelectric Materials with High Figure of Merit

NASA Technical Reports Server (NTRS)

Kim, Hyun-Jung; Park, Yeonjoon; King, Glen C.; Lee, Kunik; Choi, Sang H.

2010-01-01

Direct energy conversion between thermal and electrical energy, based on thermoelectric (TE) effect, has the potential to recover waste heat and convert it to provide clean electric power. The energy conversion efficiency is related to the thermoelectric figure of merit ZT expressed as ZT=S(exp 2)(sigma)T/Kappa, T is temperature, S is the Seebeck coefficient, sigma is conductance and Kappa is thermal conductivity. For a lower thermal conductivity Kappa and high power factor (S(exp 2)(sigma)), our current strategy is the development of rhombohedrally strained single crystalline SiGe materials that are highly [111]-oriented twinned. The development of a SiGe "twin lattice structure (TLS)" plays a key role in phonon scattering. The TLS increases the electrical conductivity and decreases thermal conductivity due to phonon scattering at stacking faults generated from the 60 X rotated primary twin structure. To develop high performance materials, the substrate temperature, chamber working pressure, and DC sputtering power are controlled for the aligned growth production of SiGe layer and TLS on a c-plane sapphire. Additionally, a new elevated temperature thermoelectric characterization system, that measures the thermal diffusivity and Seebeck effect nondestructively, was developed. The material properties were characterized at various temperatures and optimized process conditions were experimentally determined. The present paper encompasses the technical discussions toward the development of thermoelectric materials and the measurement techniques.

Modeling and Predicting the Electrical Conductivity of Composite Cathode for Solid Oxide Fuel Cell by Using Support Vector Regression

NASA Astrophysics Data System (ADS)

Tang, J. L.; Cai, C. Z.; Xiao, T. T.; Huang, S. J.

2012-07-01

The electrical conductivity of solid oxide fuel cell (SOFC) cathode is one of the most important indices affecting the efficiency of SOFC. In order to improve the performance of fuel cell system, it is advantageous to have accurate model with which one can predict the electrical conductivity. In this paper, a model utilizing support vector regression (SVR) approach combined with particle swarm optimization (PSO) algorithm for its parameter optimization was established to modeling and predicting the electrical conductivity of Ba0.5Sr0.5Co0.8Fe0.2 O3-δ-xSm0.5Sr0.5CoO3-δ (BSCF-xSSC) composite cathode under two influence factors, including operating temperature (T) and SSC content (x) in BSCF-xSSC composite cathode. The leave-one-out cross validation (LOOCV) test result by SVR strongly supports that the generalization ability of SVR model is high enough. The absolute percentage error (APE) of 27 samples does not exceed 0.05%. The mean absolute percentage error (MAPE) of all 30 samples is only 0.09% and the correlation coefficient (R2) as high as 0.999. This investigation suggests that the hybrid PSO-SVR approach may be not only a promising and practical methodology to simulate the properties of fuel cell system, but also a powerful tool to be used for optimal designing or controlling the operating process of a SOFC system.

Effect of Se addition on optical and electrical properties of chalcogenide CdSSe thin films

NASA Astrophysics Data System (ADS)

Hassanien, A. S.; Akl, Alaa A.

2016-01-01

Compositional dependence of optical and electrical properties of chalcogenide CdSxSe1-x (0.4 ≥ x ≥ 0.0 at. %) thin films was studied. Cadmium sulphoselenide films were deposited by thermal evaporation technique at vacuum (8.2 × 10-4 Pa) onto preheated glass substrates (523 K). The evaporation rate and film thickness were kept constant at 2.50 nm/s and 375 ± 5 nm, respectively. X-ray diffractograms showed that, the deposited films have the low crystalline nature. Energy dispersive analysis by X-ray (EDAX) was used to check the compositional elements of deposited films. The absorption coefficient was determined from transmission and reflection measurements at room temperature in the wavelength range 300-2500 nm. Optical density, skin depth, optical energy gap and Urbach's parameters of CdSSe thin films have also been estimated. The direct optical energy gap decreased from 2.248 eV to 1.749 eV when the ratio of Se-content was increased from 0.60 to 1.00 . Conduction band and valance band positions were evaluated. The temperature dependence of dc-electrical resistivity in the temperature range (293-450 K) has been reported. Three conduction regions due to different conduction mechanisms were detected. Electrical sheet resistance, activation energy and pre-exponential parameters were discussed. The estimated values of optical and electrical parameters were strongly dependent upon the Se-content in CdSSe matrix.

A comparison of upper mantle subcontinental electrical conductivity for North America, Europe, and Asia.

USGS Publications Warehouse

Campbell, W.H.; Schiffmacher, E.R.

1986-01-01

Spherical harmonic analysis coefficients of the external and internal parts of the quiet-day geomagnetic field variations (Sq), separated for the N American, European, Central Asian and E Asian regions, were used to determine conductivity profiles to depths of about 600km by the Schmucker equivalent-substitute conductor method. All 3 regions showed a roughly exponential increase of conductivity with depth. Distinct discontinuities seemed to be evident near 255-300km and near 450-600km. Regional differences in the conductivity profiles were shown by the functional fittings to the data. For depths less than about 275km, the N American conductivities seemed to be significantly higher than the other regions. For depths greater than about 300km, the E Asian conductivities were largest. -Authors

Influence of Sn on the thermoelectric properties of (Bi{sub x}Sb{sub 1-x}){sub 2}Te{sub 3} single crystals

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kulbachinskii, V.A., E-mail: kulb@mig.phys.msu.ru; Kytin, V.G.; Kudryashov, A.A.

2012-09-15

The influence of tin on the thermoelectric properties of p-(Bi{sub x}Sb{sub 1-x}){sub 2}Te{sub 3} single crystals (x=0; 0.25; 0.5) has been investigated. The temperature dependence of the Seebeck coefficient S, the electrical conductivity {sigma}, the heat conductivity k and the thermoelectric figure of merit of p-(Bi{sub x}Sb{sub 1-x}){sub 2}Te{sub 3} single crystals were measured in the temperature range 7-300 K. By an increase the Sn content, the hole concentration increases in p-(Bi{sub x}Sb{sub 1-x}){sub 2-y}Sn{sub y}Te{sub 3}. The heat conductivity k of the p-(Bi{sub x}Sb{sub 1-x}){sub 2-y}Sn{sub y}Te{sub 3} crystals decreases due to the Sn doping, while the electrical conductivitymore » {sigma} increases in the temperature interval about 200« less

Thermoelectric materials by using two-dimensional materials with negative correlation between electrical and thermal conductivity

PubMed Central

Lee, Myoung-Jae; Ahn, Ji-Hoon; Sung, Ji Ho; Heo, Hoseok; Jeon, Seong Gi; Lee, Woo; Song, Jae Yong; Hong, Ki-Ha; Choi, Byeongdae; Lee, Sung-Hoon; Jo, Moon-Ho

2016-01-01

In general, in thermoelectric materials the electrical conductivity σ and thermal conductivity κ are related and thus cannot be controlled independently. Previously, to maximize the thermoelectric figure of merit in state-of-the-art materials, differences in relative scaling between σ and κ as dimensions are reduced to approach the nanoscale were utilized. Here we present an approach to thermoelectric materials using tin disulfide, SnS2, nanosheets that demonstrated a negative correlation between σ and κ. In other words, as the thickness of SnS2 decreased, σ increased whereas κ decreased. This approach leads to a thermoelectric figure of merit increase to 0.13 at 300 K, a factor ∼1,000 times greater than previously reported bulk single-crystal SnS2. The Seebeck coefficient obtained for our two-dimensional SnS2 nanosheets was 34.7 mV K−1 for 16-nm-thick samples at 300 K. PMID:27323662

Quadratic Electro-optic Effect in a Novel Nonconjugated Conductive Polymer, iodine-doped Polynorbornene

NASA Astrophysics Data System (ADS)

Narayanan, Ananthakrishnan; Thakur, Mrinal

2009-03-01

Quadratic electro-optic effect in a novel nonconjugated conductive polymer, iodine-doped polynorbornene has been measured using field-induced birefringence at 633 nm. The electrical conductivity^1 of polynorbornene increases by twelve orders of magnitude to about 0.01 S/cm upon doping with iodine. The electro-optic measurement has been made in a film doped at the medium doping-level. The electro-optic modulation signal was recorded using a lock-in amplifier for various applied ac voltages (4 kHz) and the quadratic dependence of the modulation on the applied voltage was observed. A modulation of about 0.01% was observed for an applied electric field of 3 V/micron for a 100 nm thick film The Kerr coefficient as determined is about 1.77x10-11m/V^2. This exceptionally large quadratic electro-optic effect has been attributed to the confinement of this charge-transfer system within a sub-nanometer dimension. 1. A. Narayanan, A. Palthi and M. Thakur, J. Macromol. Sci. -- PAC, accepted.

Transparent conducting ZnO-CdO thin films deposited by e-beam evaporation technique

NASA Astrophysics Data System (ADS)

Mohamed, H. A.; Ali, H. M.; Mohamed, S. H.; Abd El-Raheem, M. M.

2006-04-01

Thin films of Zn{1-x} Cd{x}O with x = 0, 0.1, 0.2, 0.3, 0.4 and 0.5 at.% were deposited by electron-beam evaporation technique. It has been found that, for as-deposited films, both the transmittance and electrical resistivity decreased with increasing the Cd content. To improve the optical and electrical properties of these films, the effect of annealing temperature and time were taken into consideration for Zn{1-x} Cd{x}O film with x = 0.2. It was found that, the optical transmittance and the electrical conductivity were improved significantly with increasing the time of annealing. At fixed temperature of 300 °C, the transmittance increased with increasing the time of annealing and reached its maximum values of 81% in the visible region and 94% in the NIR region at annealing time of 120 min. The low electrical resistivity of 3.6 × 10-3 Ω cm was achieved at the same conditions. Other parameters named free carrier concentrations, refractive index, extinction coefficient, plasma frequency, and relaxation time were studied as a function of annealing temperature and time for 20% Cd content.

Controlled Transdermal Iontophoresis by Polypyrrole/Poly(Acrylic Acid) Hydrogel

NASA Astrophysics Data System (ADS)

Chansai, Phithupha; Sirivat, Anuvat

2008-03-01

Transdermal drug delivery system delivers a drug into a body at desired site and rate. The conductive polymer-hydrogel blend between polypyrrole (PPy) doped with anionic drug and poly(acrylic acid) (PAA) were developed as a matrix/carrier of drug for the transdermal drug delivery in which the characteristic releases depend on the electrical field applied. The PAA films and their blend films were prepared by solution casting using ethylene glycol dimethacrylate (EGDMA) as a crosslinking agent. A mechanical blending of PPy particles and PAA matrix was then carried out. Drug diffusions in the blended PPy/PAA hydrogel and the non-blended one were investigated and determined by using a modified Franz-diffusion cell with an acetate buffer, pH 5.5, at 37 0C, for a period of 48 hours to determine the effects of crosslinking ratio and electric field strength. Amounts of the released drug were measured by UV-Visible spectrophotometry. The diffusion coefficient of drug was determined through the Higuchi equation via different conditions, with and without an electric field. Moreover, thermal properties and electrical conductivity of the polypyrrole and drug-loaded polypyrrole were investigated by means of the thermogravimetric analysis and by using a two-point probe meter, respectively.

Surface-properties relationship in sputtered Ag thin films: Influence of the thickness and the annealing temperature in nitrogen

NASA Astrophysics Data System (ADS)

Guillén, C.; Herrero, J.

2015-01-01

Metal layers with high roughness and electrical conductivity are required as back-reflector electrodes in several optoelectronic devices. The metal layer thickness and the process temperature should be adjusted to reduce the material and energetic costs for the electrode preparation. Here, Ag thin films with thickness ranging from 30 to 200 nm have been deposited by sputtering at room temperature on glass substrates. The structure, morphology, optical and electrical properties of the films have been analyzed in the as-grown conditions and after thermal treatment in flowing nitrogen at various temperatures in the 150-550 °C range. The surface texture has been characterized by the root-mean-square roughness and the correlation length coefficients, which are directly related to the electrical resistivity and the light-scattering parameter (reflectance haze) for the various samples. The increment in the reflectance haze has been used to detect surface agglomeration processes that are found dependent on both the film thickness and the annealing temperature. A good compromise between light-scattering and electrical conductivity has been achieved with 70 nm-thick Ag films after 350 °C heating.

Thermoelectric transport coefficients in mono-layer MoS{sub 2} and WSe{sub 2}: Role of substrate, interface phonons, plasmon, and dynamic screening

DOE Office of Scientific and Technical Information (OSTI.GOV)

Ghosh, Krishnendu, E-mail: kghosh3@buffalo.edu; Singisetti, Uttam, E-mail: uttamsin@buffalo.edu

2015-10-07

The thermoelectric transport coefficients of electrons in two recently emerged transition metal di-chalcogenides (TMD), MoS{sub 2} and WSe{sub 2}, are calculated by solving Boltzmann transport equation using Rode's iterative technique in the diffusive transport regime and the coupled current (electrical and heat) equations. Scattering from remote phonons along with the hybridization of TMD plasmon with remote phonon modes and dynamic screening under linear polarization response are investigated in TMDs sitting on a dielectric environment. The transport coefficients are obtained for a varying range of temperature and doping density for three different types of substrates—SiO{sub 2}, Al{sub 2}O{sub 3}, and HfO{submore » 2}. The Seebeck co-efficient for MoS{sub 2} and WSe{sub 2} is found to be higher than 3D semiconductors even with diffusive transport. The electronic thermal conductivity is found to be low, however, the thermoelectric figure of merit is limited by the high phonon thermal conductivity. It is found that judicious selection of a dielectric environment based on temperature of operation and carrier density is crucial to optimize the thermoelectric performance of TMD materials.« less

Influence of Oxygen Partial Pressure during Processing on the Thermoelectric Properties of Aerosol-Deposited CuFeO₂.

PubMed

Stöcker, Thomas; Exner, Jörg; Schubert, Michael; Streibl, Maximilian; Moos, Ralf

2016-03-24

In the field of thermoelectric energy conversion, oxide materials show promising potential due to their good stability in oxidizing environments. Hence, the influence of oxygen partial pressure during synthesis on the thermoelectric properties of Cu-Delafossites at high temperatures was investigated in this study. For these purposes, CuFeO₂ powders were synthetized using a conventional mixed-oxide technique. X-ray diffraction (XRD) studies were conducted to determine the crystal structures of the delafossites associated with the oxygen content during the synthesis. Out of these powders, films with a thickness of about 25 µm were prepared by the relatively new aerosol-deposition (AD) coating technique. It is based on a room temperature impact consolidation process (RTIC) to deposit dense solid films of ceramic materials on various substrates without using a high-temperature step during the coating process. On these dense CuFeO₂ films deposited on alumina substrates with electrode structures, the Seebeck coefficient and the electrical conductivity were measured as a function of temperature and oxygen partial pressure. We compared the thermoelectric properties of both standard processed and aerosol deposited CuFeO₂ up to 900 °C and investigated the influence of oxygen partial pressure on the electrical conductivity, on the Seebeck coefficient and on the high temperature stability of CuFeO₂. These studies may not only help to improve the thermoelectric material in the high-temperature case, but may also serve as an initial basis to establish a defect chemical model.

Investigation of transport properties of FeTe compound

NASA Astrophysics Data System (ADS)

Lodhi, Pavitra Devi; Solanki, Neha; Choudhary, K. K.; Kaurav, Netram

2018-05-01

Transport properties of FeTe parent compound has been investigated by measurements of electrical resistivity, magnetic susceptibility and Seebeck coefficient. The sample was synthesized through a standard solid state reaction route via vacuum encapsulation and characterized by x-ray diffraction, which indicated a tetragonal phase with space group P4/nmm. The parent FeTe compound does not exhibit superconductivity but shows an anomaly in the resistivity measurement at around 67 K, which corresponds to a structural phase transition along with in the vicinity of a magnetic phase transition. In the low temperature regime, Seebeck coefficient, S(T), exhibited an anomalous dip feature and negative throughout the temperature range, indicating electron-like charge carrier conduction mechanism.

Photo-Seebeck effect in tetragonal PbO single crystals

DOE Office of Scientific and Technical Information (OSTI.GOV)

Mondal, P. S.; Okazaki, R.; Taniguchi, H.

2013-11-07

We report the observation of photo-Seebeck effect in tetragonal PbO crystals. The photo-induced carriers contribute to the transport phenomena, and consequently the electrical conductivity increases and the Seebeck coefficient decreases with increasing photon flux density. A parallel-circuit model is used to evaluate the actual contributions of photo-excited carriers from the measured transport data. The photo-induced carrier concentration estimated from the Seebeck coefficient increases almost linearly with increasing photon flux density, indicating a successful photo-doping effect on the thermoelectric property. The mobility decreases by illumination but the reduction rate strongly depends on the illuminated photon energy. Possible mechanisms of such photon-energy-dependentmore » mobility are discussed.« less

On physical optics for calculating scattering from coated bodies

NASA Technical Reports Server (NTRS)

Baldauf, J.; Lee, S. W.; Ling, H.; Chou, R.

1989-01-01

The familiar physical optics (PO) approximation is no longer valid when the perfectly conducting scatterer is coated with dielectric material. This paper reviews several possible PO formulations. By comparing the PO formulation with the moment method solution based on the impedance boundary condition for the case of the coated cone-sphere, a PO formulation using both electric and magnetic currents consistently gives the best numerical results. Comparisons of the exact moment method with the PO formulations using the impedance boundary condition and the PO formulation using the Fresnel reflection coefficient for the case of scattering from the cone-ellipsoid demonstrate that the Fresnel reflection coefficient gives the best numerical results in general.

Electrical properties of epitaxial yttrium iron garnet ultrathin films at high temperatures

NASA Astrophysics Data System (ADS)

Thiery, N.; Naletov, V. V.; Vila, L.; Marty, A.; Brenac, A.; Jacquot, J.-F.; de Loubens, G.; Viret, M.; Anane, A.; Cros, V.; Ben Youssef, J.; Beaulieu, N.; Demidov, V. E.; Divinskiy, B.; Demokritov, S. O.; Klein, O.

2018-02-01

We report a study on the electrical properties of 19-nm-thick yttrium iron garnet (YIG) films grown by liquid phase epitaxy on gadolinium gallium garnet single crystal. The electrical conductivity and Hall coefficient are measured in the high-temperature range [300,400] K using a Van der Pauw four-point probe technique. We find that the electrical resistivity decreases exponentially with increasing temperature following an activated behavior corresponding to a band gap of Eg≈2 eV. It drops to values about 5 ×103Ω cm at T =400 K, thus indicating that epitaxial YIG ultrathin films behave as large gap semiconductors. We also infer the Hall mobility, which is found to be positive (p type) at 5 cm2V-1sec-1 and almost independent of temperature. We discuss the consequence for nonlocal spin transport experiments performed on YIG at room temperature and demonstrate the existence of electrical offset voltages to be disentangled from pure spin effects.

Estimating thermal conductivity and thermoelectricity in PbTiO3 from first principles

NASA Astrophysics Data System (ADS)

Roy, Anindya

A combination of density functional theory and Boltzmann transport equation is used in this study to calculate the lattice thermal conductivity (κL) of PbTiO3 (PTO). We cannot apply this procedure to determine κL in presence of imaginary phonon modes (''soft modes''). Hence the tetragonal structure of PTO is used in these calculations, and the predicted κL is extrapolated to higher temperature using insights from experiments. The computed κL of PTO is low, possibly due to the anharmonicity associated with the ferroelectric/paraelectric transition. Electronic transport parameters such as the Seebeck coefficient and the electrical conductivity are also determined (under constant scattering time approximation in semiclassical Boltzmann theory) for PTO. The low κL and the electronic transport parameters together indicate excellent thermoelectric properties of PTO (zT > 1.5 at 1000 K). As a technologically important ferroelectric/piezoelectric material, PTO is used in alloys and in layered structures. These morphologies could bring down the κL further, improving its thermoelectric performance. Synthesis of electrically conducting samples of PTO would allows us to verify the above predictions.

Field-effect-dependent thermoelectric power in highly resistive Sb2Se3 single nanowire

NASA Astrophysics Data System (ADS)

Sun, Kien Wen; Ko, Ting-Yu; Shellaiah, Muthaiah

2018-04-01

In this paper, we report the results of our experiments on and measurements of electrical resistivity and thermoelectric power (Seebeck coefficient) from single-crystalline antimony triselenide (Sb2Se3) single nanowires (NWs) with high resistivity ( σ 4.37 × 10-4 S/m). A positive Seebeck coefficient of approximately 661 µV/K at room temperature was obtained using a custom-made thermoelectric power probe with an alternating current lock-in method (the 2ω technique), which indicates that the thermal transport is dominated by holes. The measured Seebeck coefficient of the NWs is a factor of 2-3 lower than their bulk counterparts and is comparable to that of a highly conductive Sb2Se3 single NWs (approximately - 750 µV/K). We observed an increase in the Seebeck coefficients with increased bias voltages by field-effect gating, which cannot be explained by the modulation of the Fermi level in the NWs.

Dual Vacancies: An Effective Strategy Realizing Synergistic Optimization of Thermoelectric Property in BiCuSeO.

PubMed

Li, Zhou; Xiao, Chong; Fan, Shaojuan; Deng, Yu; Zhang, Wenshuai; Ye, Bangjiao; Xie, Yi

2015-05-27

Vacancy is a very important class of phonon scattering center to reduce thermal conductivity for the development of high efficient thermoelectric materials. However, conventional monovacancy may also act as an electron or hole acceptor, thereby modifying the electrical transport properties and even worsening the thermoelectric performance. This issue urges us to create new types of vacancies that scatter phonons effectively while not deteriorating the electrical transport. Herein, taking BiCuSeO as an example, we first reported the successful synergistic optimization of electrical and thermal parameters through Bi/Cu dual vacancies. As expected, as compared to its pristine and monovacancy samples, these dual vacancies further increase the phonon scattering, which results in an ultra low thermal conductivity of 0.37 W m(-1) K(-1) at 750 K. Most importantly, the clear-cut evidence in positron annihilation unambiguously confirms the interlayer charge transfer between these Bi/Cu dual vacancies, which results in the significant increase of electrical conductivity with relatively high Seebeck coefficient. As a result, BiCuSeO with Bi/Cu dual vacancies shows a high ZT value of 0.84 at 750 K, which is superior to that of its native sample and monovacancies-dominant counterparts. These findings undoubtedly elucidate a new strategy and direction for rational design of high performance thermoelectric materials.

Anisotropic electrical and lattice transport properties of ordered quaternary phases Cr2TiAlC2 and Mo2TiAlC2: A first principles study

NASA Astrophysics Data System (ADS)

Li, Y. F.; Ding, Y. C.; Xiao, B.; Cheng, Y. H.

2016-11-01

Electrical conductivities of Cr2TiAlC2 and Mo2TiAlC2 in a and c directions are calculated from semi-classic Boltzmann transport theory. The values are found to be σa = 5.68 ×105 S /m (6.56 ×105 S /m) and σc = 2.15 ×105 S /m (2.69 ×105 S /m) for Cr2TiAlC2 (Mo2TiAlC2) at 300 K. Using the phonon-mode Debye temperature and Slack-model, the lattice thermal conductivities in the two directions are also evaluated, and the values are κa = 18.71 W /m K (16.11 W/m K) and κc = 0.48 W /m K (0.25 W /m K) for Cr2TiAlC2 (Mo2TiAlC2) at room temperature. The anisotropy in lattice thermal conductivity is found to be stronger than that of electrical conductivity. The predicted Seebeck coefficients and thermoelectric figure of merit (ZT) indicate that they are poor thermoelectric materials. Due to the relatively high conductivities, they might be used to fabricate high temperature conductive components in aerospace industry. In addition, our results in a direction have the direct implications for the relevant properties of MXenes (Cr2TiC2 and Mo2TiC2), produced from their bulk phases.

Optical reading of field-effect transistors by phase-space absorption quenching in a single InGaAs quantum well conducting channel

NASA Astrophysics Data System (ADS)

Chemla, D. S.; Bar-Joseph, I.; Klingshirn, C.; Miller, D. A. B.; Kuo, J. M.

1987-03-01

Absorption switching in a semiconductor quantum well by electrically varying the charge density in the quantum well conducting channel of a selectively doped heterostructure transistor is reported for the first time. The phase-space absorption quenching (PAQ) is observed at room temperature in an InGaAs/InAlAs grown on InP FET, and it shows large absorption coefficient changes with relatively broad spectral bandwidth. This PAQ is large enough to be used for direct optical determination of the logic state of the FET.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Pereyra, Pedro, E-mail: pereyrapedro@gmail.com; Mendoza-Figueroa, M. G.

Transport properties of electrons through biased double barrier semiconductor structures with finite transverse width w{sub y}, in the presence of a channel-mixing transverse electric field E{sub T} (along the y-axis), were studied. We solve the multichannel Schrödinger equation using the transfer matrix method and transport properties, like the conductance G and the transmission coefficients T{sub ij} have been evaluated as functions of the electrons' energy E and the transverse and longitudinal (bias) electric forces, f{sub T} and f{sub b}. We show that peak-suppression effects appear, due to the applied bias. Similarly, coherent interference of wave-guide states induced by the transversemore » field is obtained. We show also that the coherent interference of resonant wave-guide states gives rise to resonant conductance, which can be tuned to produce broad resonant peaks, implying operation frequencies of the order of 10 THz or larger.« less

Certain physical properties of cobalt and nickel borides

NASA Technical Reports Server (NTRS)

Kostetskiy, I. I.; Lvov, S. N.

1981-01-01

The temperature dependence of the electrical resistivity, the thermal conductivity, and the thermal emf of cobalt and nickel borides were studied. In the case of the nickel borides the magnetic susceptibility and the Hall coefficient were determined at room temperature. The results are discussed with allowance for the current carrier concentration, the effect of various mechanisms of current-carrier scattering and the location of the Fermi level in relation to the 3d band.

High-fidelity plasma codes for burn physics

DOE Office of Scientific and Technical Information (OSTI.GOV)

Cooley, James; Graziani, Frank; Marinak, Marty

Accurate predictions of equation of state (EOS), ionic and electronic transport properties are of critical importance for high-energy-density plasma science. Transport coefficients inform radiation-hydrodynamic codes and impact diagnostic interpretation, which in turn impacts our understanding of the development of instabilities, the overall energy balance of burning plasmas, and the efficacy of self-heating from charged-particle stopping. Important processes include thermal and electrical conduction, electron-ion coupling, inter-diffusion, ion viscosity, and charged particle stopping. However, uncertainties in these coefficients are not well established. Fundamental plasma science codes, also called high-fidelity plasma codes, are a relatively recent computational tool that augments both experimental datamore » and theoretical foundations of transport coefficients. This paper addresses the current status of HFPC codes and their future development, and the potential impact they play in improving the predictive capability of the multi-physics hydrodynamic codes used in HED design.« less

Multilayered models for electromagnetic reflection amplitudes

NASA Technical Reports Server (NTRS)

Linlor, W. I.

1976-01-01

The remote sensing of snowpack characteristics with surface installations or with an airborne system could have important applications in water resource management and flood prediction. To derive some insight into such applications, the electromagnetic response of multilayer snow models is analyzed. Normally incident plane waves are assumed at frequencies ranging from 10 to the 6th power to 10 to the 10th power Hz, and amplitude reflection coefficients are calculated for models having various snow-layer combinations, including ice sheets. Layers are defined by a thickness, permittivity, and conductivity; the electrical parameters are constant or prescribed functions of frequency. To illustrate the effect of various layering combinations, results are given in the form of curves of amplitude reflection coefficients, versus frequency for a variety of models. Under simplifying assumptions, the snow thickness and effective dielectric constant can be estimated from the reflection coefficient variations as a function of frequency.

Properties of C4F7N–CO2 thermal plasmas: thermodynamic properties, transport coefficients and emission coefficients

NASA Astrophysics Data System (ADS)

Wu, Yi; Wang, Chunlin; Sun, Hao; Murphy, Anthony B.; Rong, Mingzhe; Yang, Fei; Chen, Zhexin; Niu, Chunpin; Wang, Xiaohua

2018-04-01

The thermophysical properties, including composition, thermodynamic properties, transport coefficients and net emission coefficients, of thermal plasmas formed from pure iso-C4 perfluoronitrile C4F7N and C4F7N–CO2 mixtures are calculated for temperatures from 300 to 30 000 K and pressures from 0.1 to 20 atm. These gases have received much attention as alternatives to SF6 for use in circuit breakers, due to the low global warming potential and good dielectric properties of C4F7N. Since the parameters of the large molecules formed in the dissociation of C4F7N are unavailable, the partition function and enthalpy of formation were calculated using computational chemistry methods. From the equilibrium composition calculations, it was found that when C4F7N is mixed with CO2, CO2 can capture C atoms from C4F7N, producing CO, since the system consisting of small molecules such as CF4 and CO has lower energy at room temperature. This is in agreement with previous experimental results, which show that CO dominates the decomposition products of C4F7N–CO2 mixtures; it could limit the repeated breaking performance of C4F7N. From the point of view of chemical stability, the mixing ratio of CO2 should therefore be chosen carefully. Through comparison with common arc quenching gases (including SF6, CF3I and C5F10O), it is found that for the temperature range for which electrical conductivity remains low, pure C4F7N has similar ρC p (product of mass density and specific heat) properties to SF6, and higher radiative emission coefficient, properties that are correlated with good arc extinguishing capability. For C4F7N–CO2 mixtures, the electrical conductivity is very close to that of SF6 while the ρC p peak at 7000 K caused by decomposition of CO implies inferior interruption capability to that of SF6. The calculated properties will be useful in arc simulations.

The influence of an interface electric field on the distribution coefficient of chromium in LiNbO 3

NASA Astrophysics Data System (ADS)

Uda, Satoshi; Tiller, William A.

1992-06-01

The effective solute partitioning of chromium was investigated on single crystals of LiNbO 3 grown by the laser-heated pedestal growth (LHPG) technique. Electric field effects at the interface influence this solute partitioning, leading to an electric field-dependent effective solute distribution coefficient, kE. The LHPG technique made it possible to explore these field effects by controllably changing the growth velocity ( V) and the temperature gradient ( GS, GL) near the interface over a wide range. The electric field generated via the temperature gradient is associated with the thermoelectric power while an additional electric field is growth rate associated via a charge separation effect. By applying the Burton-Prim-Slichter (BPS) theory to our experimental data, we found the phase diagram solute partition coefficient to be k0 ≈ 3.65, while the field-influenced solute partition coefficient ( V = 0) was k' EO ≈ 8.17 at GL ≈ 11500°C/cm. It is theoretically shown that the same considerations can be applied to all ionic partitioning at a solid-liquid interface.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Bouziane, M.; Taibi, M., E-mail: taibiens@yahoo.fr; Boukhari, A.

Electrical properties of Pb{sub 2}Na{sub 0.8}Eu{sub 0.2}Nb{sub 4.8}Fe{sub 0.2}O{sub 15} tungsten bronze compound were investigated. Ferroelectric phase transition of diffuse type is observed at 395 °C. Conductivity study as a function of temperature (RT-600 °C) and at three different frequencies (10, 100 and 1000 kHz) suggests the existence of dominant ionic conduction. The rise of ac conductivity on increasing temperature supports the NTCR (negative temperature coefficient of resistance) behaviour of the material. The activation energies have been evaluated from ac conductivity using Arrhenius equation and discussed. Different conduction mechanisms were identified. For comparison, the conducting properties of Pb{sub 2}Na{sub 0.8}R{submore » 0.2}Nb{sub 4.8}Fe{sub 0.2}O{sub 15} (R=Dy, Nd, La) were also investigated. - Graphical abstract: Thermal evolution of lnσ{sub ac} of Pb{sub 2}Na{sub 0.8}Eu{sub 0.2}Nb{sub 4.8}Fe{sub 0.2}O{sub 15} at selected frequencies. Display Omitted - Highlights: • We found that TB compounds exhibit a diffuse type of first- order transition. • A negative temperature coefficient of resistance (NTCR) behaviour is observed. • Three conduction mechanisms were identified: n-and/or p-type at low temperatures. • The conduction mechanism in the studied compounds is very complex.« less

Electrolyte transport in neutral polymer gels embedded with charged inclusions

NASA Astrophysics Data System (ADS)

Hill, Reghan

2005-11-01

Ion permeable membranes are the basis of a variety of molecular separation technologies, including ion exchange, gel electrophoresis and dialysis. This work presents a theoretical model of electrolyte transport in membranes comprised of a continuous polymer gel embedded with charged spherical inclusions, e.g., biological cells and synthetic colloids. The microstructure mimics immobilized cell cultures, where electric fields have been used to promote nutrient transport. Because several important characteristics can, in principle, be carefully controlled, the theory provides a quantitative framework to help tailor the bulk properties for enhanced molecular transport, microfluidic pumping, and physicochemical sensing applications. This talk focuses on the electroosmotic flow driven by weak electric fields and electrolyte concentration gradients. Also of importance is the influence of charge on the effective ion diffusion coefficients, bulk electrical conductivity, and membrane diffusion potential.

Optical and electrical properties of bismuth-sulfide (Bi2S3) thin films prepared by thermal evaporation.

NASA Astrophysics Data System (ADS)

Mahmoud, Siham; Sharaf, Fouad

Thin films of Bi2S3, of thickness in the range 300 to 500 nm, were produced by thermal evaporation technique. The reaction consisted in depositing the two elements (bismuth and sulfur) from a boat source and allowing their atoms to interdiffuse to form the compound during the deposition on quartz substrates. The material has been characterized by X-ray studies, optical and electrical measurements. When these films were annealed at 353 K, 393 K and 453 K for 5 hours, a nearly amorphous to polycrystalline transition was observed. The absorption coefficient revealed the existence of an allowed direct transition with Eg = 1.56 eV. The activation energies for electrical conduction in low and high temperature regions are 0.28 eV and 0.73 eV, respectively.

Molding of Plasmonic Resonances in Metallic Nanostructures: Dependence of the Non-Linear Electric Permittivity on System Size and Temperature

PubMed Central

Alabastri, Alessandro; Tuccio, Salvatore; Giugni, Andrea; Toma, Andrea; Liberale, Carlo; Das, Gobind; De Angelis, Francesco; Di Fabrizio, Enzo; Zaccaria, Remo Proietti

2013-01-01

In this paper, we review the principal theoretical models through which the dielectric function of metals can be described. Starting from the Drude assumptions for intraband transitions, we show how this model can be improved by including interband absorption and temperature effect in the damping coefficients. Electronic scattering processes are described and included in the dielectric function, showing their role in determining plasmon lifetime at resonance. Relationships among permittivity, electric conductivity and refractive index are examined. Finally, a temperature dependent permittivity model is presented and is employed to predict temperature and non-linear field intensity dependence on commonly used plasmonic geometries, such as nanospheres. PMID:28788366

Electrical properties of Ba(Dy{sub 1/2}Nb{sub 1/2})O{sub 3} ceramic

DOE Office of Scientific and Technical Information (OSTI.GOV)

Nath, K. Amar, E-mail: karn190@gmail.com; Chandra, K. P., E-mail: kpchandra23@gmail.com; Dubey, K., E-mail: kirandubey45@yahoo.com

2016-05-06

Polycrystalline Ba(Dy{sub 1/2}Nb{sub 1/2})O{sub 3} was prepared using a high-temperature solid-state reaction method. X-ray diffraction analysis indicated the formation of a single-phase cubic structure having space group Pm3m. AC impedance plots as a function of frequency at different temperatures were used to analyse the electrical behaviour of the sample, which indicated the negative temperature coefficient of resistance character. Complex impedance analysis targeted non-Debye type dielectric relaxation. Frequency dependent ac conductivity data obeyed Jonscher’s power law. The apparent activation energy was estimated to be 0.97 eV at 1 kHz.

Influence of sputtering power on the optical properties of ITO thin films

NASA Astrophysics Data System (ADS)

K, Aijo John; Kumar, Vineetha V.; M, Deepak; T, Manju

2014-10-01

Tin doped indium oxide films are widely used in transparent conducting coatings such as flat panel displays, crystal displays and in optical devices such as solar cells and organic light emitting diodes due to the high electrical resistivity and optical transparency in the visible region of solar spectrum. The deposition parameters have a commendable influence on the optical and electrical properties of the thin films. In this study, ITO thin films were prepared by RF magnetron sputtering. The properties of the films prepared under varying sputtering power were compared using UV- visible spectrophotometry. Effect of sputtering power on the energy band gap, absorption coefficient and refractive index are investigated.

Impedance spectroscopy study of 2, 2, 7, 7' -tetra kis-(N,N-di-4-methoxy phenyl amino)-9,9'-spirobifluorene thin films

NASA Astrophysics Data System (ADS)

Rana, Omwati; Agrawal, Kalpana; Rajput, S. S.; Zulfequar, M.; Husain, M.; Kamalasanan, M. N.; Srivastava, Ritu

2016-05-01

The electrical properties of thermally evaporated film of 2,2,7,7'-tetrakis-(N,N-di-4-methoxyphenylamino)-9,9'-spirobifluorene (Spiro MeO TAD) have been investigated for hole only devices as a function of temperatures at frequency range from 1Hz to 1 MHz using Impedance spectroscopy. Cole-Cole plots, at each temperature, show semicircles that can be modeled with a contact resistance and parallel resistance -capacitor(R-C) circuits. Bulk resistance decreases and electrical conductivity increases with increasing temperature which indicate negative temperature coefficient of resistance nature and short range translational type hopping mechanism in Spiro MeO TAD thin films.

18O-tracer diffusion along nanoscaled Sc2O3/yttria stabilized zirconia (YSZ) multilayers: on the influence of strain

PubMed Central

Aydin, Halit; Korte, Carsten; Janek, Jürgen

2013-01-01

The oxygen tracer diffusion coefficient describing transport along nano-/microscaled YSZ/Sc2O3 multilayers as a function of the thick­ness of the ion-conducting YSZ layers has been measured by isotope exchange depth profiling (IEDP), using secondary ion mass spec­trometry (SIMS). The multilayer samples were prepared by pulsed laser deposition (PLD) on (0001) Al2O3 single crystalline substrates. The values for the oxygen tracer diffusion coefficient were analyzed as a combination of contributions from bulk and interface contributions and compared with results from YSZ/Y2O3-multilayers with similar microstructure. Using the Nernst–Einstein equation as the relation between diffusivity and electrical conductivity we find very good agreement between conductivity and diffusion data, and we exclude substantial electronic conductivity in the multilayers. The effect of hetero-interface transport can be well explained by a simple interface strain model. As the multilayer samples consist of columnar film crystallites with a defined inter­face structure and texture, we also discuss the influence of this particular microstructure on the interfacial strain. PMID:27877580

MeV Si ion modifications on the thermoelectric generators from Si/Si + Ge superlattice nano-layered films

NASA Astrophysics Data System (ADS)

Budak, S.; Heidary, K.; Johnson, R. B.; Colon, T.; Muntele, C.; Ila, D.

2014-08-01

The performance of thermoelectric materials and devices is characterized by a dimensionless figure of merit, ZT = S2σT/K, where, S and σ denote, respectively, the Seebeck coefficient and electrical conductivity, T is the absolute temperature in Kelvin and K represents the thermal conductivity. The figure of merit may be improved by means of raising either S or σ or by lowering K. In our laboratory, we have fabricated and characterized the performance of a large variety of thermoelectric generators (TEG). Two TEG groups comprised of 50 and 100 alternating layers of Si/Si + Ge multi-nanolayered superlattice films have been fabricated and thoroughly characterized. Ion beam assisted deposition (IBAD) was utilized to assemble the alternating sandwiched layers, resulting in total thickness of 300 nm and 317 nm for 50 and 100 layer devices, respectively. Rutherford Backscattering Spectroscopy (RBS) was employed in order to monitor the precise quantity of Si and Ge utilized in the construction of specific multilayer thin films. The material layers were subsequently impregnated with quantum dots and/or quantum clusters, in order to concurrently reduce the cross plane thermal conductivity, increase the cross plane Seebeck coefficient and raise the cross plane electrical conductivity. The quantum dots/clusters were implanted via the 5 MeV Si ion bombardment which was performed using a Pelletron high energy ion beam accelerator. We have achieved remarkable results for the thermoelectric and optical properties of the Si/Si + Ge multilayer thin film TEG systems. We have demonstrated that with optimal setting of the 5 MeV Si ion beam bombardment fluences, one can fabricate TEG systems with figures of merits substantially higher than the values previously reported.

Cross-plane electrical and thermal transport in oxide metal/semiconductor superlattices

NASA Astrophysics Data System (ADS)

Jha, Pankaj

Perovskite oxides display a rich variety of electronic properties as metals, ferroelectrics, ferromagnetics, multiferroics, and thermoelectrics. Cross-plane electron filtering transport in metal/semiconductor superlattices provides a potential approach to increase the thermoelectric figure of merit (ZT). La0.67Sr0.33MnO3 (LSMO) and LaMnO3 (LMO) thin-film depositions were optimized using pulsed laser deposition (PLD) to achieve low resistivity constituent materials for LSMO/LMO superlattice heterostructures on (100)-strontium titanate (STO) substrates. X-ray diffraction and high-resolution reciprocal space mapping (RSM) indicate that the superlattices are epitaxial and pseudomorphic. Cross-plane devices were fabricated by etching cylindrical pillar structures in superlattices using inductively-coupled-plasma reactive-ion etching. The cross-plane electrical conductivity data for LSMO/LMO superlattices reveal an effective barrier height of 220 meV. The cross-plane LSMO/LMO superlattices showed a giant Seebeck coefficient of 2560 microV/K at 300K that increases to 16640 microV/K at 360K. The large Seebeck coefficient may arise due to hot electron and spin filtering as LSMO/LMO superlattice constituent materials exhibit spintronic properties where charges and spin current are intertwined and can generate a spin-Seebeck effect. The room temperature thermal conductivity achieved in low resistivity superlattices was 0.92 W/mK, which indicates that cross-plane phonon scattering at interfaces reduces the lattice contribution to the thermal conductivity. The giant contribution of spin-Seebeck, the large temperature dependence of the cross-plane power factor, and the low thermal conductivity in low resistance LSMO/LMO superlattices may offer opportunities to realize spin-magnetic thermoelectric devices, and suggests a direction for further investigations of the potential of LSMO/LMO oxide superlattices for thermoelectric devices.

Globally Convergent Numerical Methods for Coefficient Inverse Problems

DTIC Science & Technology

2008-09-23

backgrounds. Probing radiations are usually thought as electric and acoustic waves for the first two applications and light originated by lasers in...fundamental laws of physics. Electric , acoustic or light scattering properties of both unknown targets and the backgrounds are described by coefficients of...with the back-reflected data here, Army applications are quite feasible. The 2-D inverse problem of the determination of the unknown electric

Optoelectronic properties and Seebeck coefficient in SnSe thin films

NASA Astrophysics Data System (ADS)

Urmila, K. S.; Namitha, T. A.; Rajani, J.; Philip, R. R.; Pradeep, B.

2016-09-01

SnSe thin films of thickness 180 nm have been deposited on glass substrates by reactive evaporation at an optimized substrate temperature of 523 ± 5 K and pressure of 10-5 mbar. The as-prepared SnSe thin films are characterized for their structural, optical and electrical properties by various experimental techniques. The p-type conductivity, near-optimum direct band gap, high absorption coefficient and good photosensitivity of the SnSe thin film indicate its suitability for photovoltaic applications. The optical constants, loss factor, quality factor and optical conductivity of the films are evaluated. The results of Hall and thermoelectric power measurements are correlated to determine the density of states, Fermi energy and effective mass of carriers and are obtained as 2.8 × 1017 cm-3, 0.03 eV and 0.05m 0 respectively. The high Seebeck coefficient ≈ 7863 μV/K, reasonably good power factor ≈ 7.2 × 10-4 W/(m·K2) and thermoelectric figure of merit ≈ 1.2 observed at 42 K suggests that, on further work, the prepared SnSe thin films can also be considered as a possible candidate for cryogenic thermoelectric applications.

Performance evaluation of Mn and Fe doped SrCo0.9Nb0.1O3-δ cathode for IT-SOFC application

NASA Astrophysics Data System (ADS)

Bele, Lokesh; Lenka, R. K.; Patro, P. K.; Muhmood, L.; Mahata, T.; Sinha, P. K.

2018-02-01

Cathode materials of Mn and Fe doped SrCo0.9Nb0.1O3-δ, are synthesized by solid state route for intermediate temperature fuel cell applications. Phase pure material is obtained after calcining the precursors at 1100 °C. Phase compatibility is observed between this novel cathode material with gadolinia doped ceria (GDC) electrolyte material as reflected in the diffraction pattern. The state of art YSZ electrolyte is not compatible with this cathode material. Average thermal expansion coefficient of the material varies between 17 to 22 X 10-6 K-1 on doping, from room temperature to 800 °C. Increase in thermal expansion coefficient is observed with Mn and Fe doping associated with the loss of oxygen from the crystal. The electrical conductivity of the cathode material decreases with Fe and Mn doping. Mn doped samples show lowest conductivity. From the symmetric cell measurement lower area specific resistance (0.16 Ω-cm2) is obtained for un-doped samples, at 850 °C. From the initial results it can be inferred that Mn/Fe doping improves neither the thermal expansion co-efficient nor the electrochemical activity.

Insight into mechanical properties and thermoelectric efficiency of Zr2CoZ (Z  =  Si, Ge) Heusler alloys

NASA Astrophysics Data System (ADS)

Yousuf, Saleem; Gupta, Dinesh C.

2017-11-01

We investigated the electronic, mechanical and thermoelectric properties of Zr2CoZ (Z  =  Si, Ge) Heusler alloys using the first-principles calculation. From the analysis of various elastic constants, the shear and Young’s moduli, Poisson’s ratio, the ductile nature of the alloys is predicted. Thermoelectric coefficients viz., Seebeck, electrical conductivity and figure of merit show Zr2CoZ alloys as n-type thermoelectric materials showing linearly increasing Seebeck coefficient with temperature. The value of total absolute Seebeck coefficients at 1200 K of Zr2CoSi and Zr2CoGe are 60 µV K-1 and 40 µV K-1 respectively mainly because of the existence of almost flat conduction bands along L to Г directions of high symmetry Brillouin zone. Further, the chemical potential variation of power factor confirms the n-type doping fruitful to increase their TE performance. The figure of merit achieves an upper-limit of 0.95 at 850 K and can favour their use for waste heat recovery at higher temperatures and thermoelectric spin generators.

Geometry effect on electrokinetic flow and ionic conductance in pH-regulated nanochannels

NASA Astrophysics Data System (ADS)

Sadeghi, Morteza; Saidi, Mohammad Hassan; Moosavi, Ali; Sadeghi, Arman

2017-12-01

Semi-analytical solutions are obtained for the electrical potential, electroosmotic velocity, ionic conductance, and surface physicochemical properties associated with long pH-regulated nanochannels of arbitrary but constant cross-sectional area. The effects of electric double layer overlap, multiple ionic species, and surface association/dissociation reactions are all taken into account, assuming low surface potentials. The method of analysis includes series solutions which the pertinent coefficients are obtained by applying the wall boundary conditions using either of the least-squares or point matching techniques. Although the procedure is general enough to be applied to almost any arbitrary cross section, nine nanogeometries including polygonal, trapezoidal, double-trapezoidal, rectangular, elliptical, semi-elliptical, isosceles triangular, rhombic, and isotropically etched profiles are selected for presentation. For the special case of an elliptic cross section, full analytical solutions are also obtained utilizing the Mathieu functions. We show that the geometrical configuration plays a key role in determination of the ionic conductance, surface charge density, electrical potential and velocity fields, and proton enhancement. In this respect, the net electric charge and convective ionic conductance are higher for channels of larger perimeter to area ratio, whereas the opposite is true for the average surface charge density and mean velocity; the geometry impact on the two latest ones, however, vanishes if the background salt concentration is high enough. Moreover, we demonstrate that considering a constant surface potential equal to the average charge-regulated potential provides sufficiently accurate results for smooth geometries such as an ellipse at medium-high aspect ratios but leads to significant errors for geometries having narrow corners such as a triangle.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Tietz, F., E-mail: f.tietz@fz-juelich.de; Arul Raj, I.; Ma, Q.

An overview is presented on the variation of electrical conductivity, oxygen permeation, and thermal expansion coefficient as a function of the composition of perovskites in the quasi-ternary system LaFeO{sub 3}–LaCoO{sub 3}–LaNiO{sub 3}. Powders of thirteen nominal perovskite compositions were synthesized under identical conditions by the Pechini method. The powder X-ray diffraction data of two series, namely La(Ni{sub 0.5}Fe{sub 0.5}){sub 1−x}Co{sub x}O{sub 3} and LaNi{sub 0.5-x}Fe{sub x}Co{sub 0.5}O{sub 3}, are presented after the powders had been sintered at 1100 °C for 6 h in air. The measurements revealed a rhombohedral structure for all compositions except LaNi{sub 0.5}Fe{sub 0.5}O{sub 3} for whichmore » 60% rhombohedral and 40% orthorhombic phase was found. The maximum DC electrical conductivity value of the perovskites at 800 °C was 1229 S cm{sup −1} for the composition LaCoO{sub 3} and the minimum was 91 S cm{sup −1} for the composition LaCo{sub 0.5}Fe{sub 0.5}O{sub 3}. The oxygen permeation of samples with promising conductivities at 800 °C was one order of magnitude lower than that of La{sub 0.6}Sr{sub 0.4}Co{sub 0.8}Fe{sub 0.2}O{sub 3} (LSCF). The highest value of 0.017 ml cm{sup −2} min{sup −1} at 950 °C was obtained with LaNi{sub 0.5}Co{sub 0.5}O{sub 3}. The coefficients of thermal expansion varied in the range of 13.2×10{sup −6} K{sup −1} and 21.9×10{sup −6} K{sup −1} for LaNi{sub 0.5}Fe{sub 0.5}O{sub 3} and LaCoO{sub 3}, respectively. {sup 57}Fe Mössbauer spectroscopy was used as probe for the oxidation states, local environment and magnetic properties of iron ions as a function of chemical composition. The substitution had a great influence on the chemical properties of the materials. - Graphical abstract: Compositional dependence of isothermal electrical conductivity at 800 °C and thermal expansion coefficient in the series La(Fe{sub 0.5}Ni{sub 0.5}){sub (1−x)}Co{sub x}O{sub 3} and LaNi{sub 0.5−x}Fe{sub x}Co{sub 0.5}O{sub 3}.« less

THERMAL AND ELECTRICAL PROPERTIES OF Ba0.5Sr0.5CoxFe1-x-yNiyO3-δ (x = 0.4, 0 ≤ y ≤ 0.25) AS CATHODE MATERIAL FOR IT-SOFCs

NASA Astrophysics Data System (ADS)

Burnwal, Suman Kumar; Kistaiah, P.

2015-03-01

Ba0.5Sr0.5CoxFe1-x-yNiyO3-δ (BSCFNi; x = 0.4, 0 ≤ y ≤ 0.25) were studied in relation to their potential use as intermediate temperature solid oxide fuel cell (IT-SOFC) cathode. An emphasis is made on the effect of Ni-doping on crystal structure, thermal expansion coefficient (TEC) and dc electrical conductivity. A cubic perovskite structure was observed in the X-ray diffraction (XRD) measurement. The TEC of BSCFNi obtained for 0 ≤ y ≤ 0.25, varies in the range of (12.38-18.81) × 10-6 K-1, measured in the temperature range of 30°C to 800°C. The electrical conductivity which is a major defect of Ba0.5Sr0.5CoxFe1-xO3-δ (BSCF) was improved by Ni-doping. The compound with y = 0.20 and 0.25 demonstrated a conductivity of σ = 62.59 S-cm-1 and 72.64 S-cm-1 at 400°C and 77.01 S-cm-1 and 89.68 S-cm-1 at 500°C.

FT-MIR supported Electrical Impedance Spectroscopy based study of sugar adulterated honeys from different floral origin.

PubMed

Das, Chirantan; Chakraborty, Subhadip; Acharya, Krishnendu; Bera, Nirmal Kumar; Chattopadhyay, Dipankar; Karmakar, Anupam; Chattopadhyay, Sanatan

2017-08-15

This study sought to detect the presence of sucrose as an adulterant in selected honey varieties from different floral origins by employing Electrical Impedance Spectroscopy (EIS) technique which has been simultaneously supported by Fourier Transform-Mid Infrared Spectroscopy (FT-MIR) measurements to provide a rapid, robust yet simple platform for honey quality evaluation. Variation of electrical parameters such as impedance, capacitance and conductance for 10%, 20%, 30%, 40%, 50%, 60% and 70% (w/w) sucrose syrup (SS) adulterated honey samples are analyzed and their respective current-voltage (I-V) characteristics are studied. Capacitance, conductance and net current flowing through the system are observed to decrease linearly whereas system impedance has been found to increase similarly with the increase in adulterant content. Also, FT-MIR measurements in the spectral region between 1800cm -1 and 650cm -1 reveal the increment of absorbance values due to the addition of SS. Full-Width-at-Half-Maximum (FWHM) is estimated from the spectral peak 1056cm -1 for all pure and adulterated honey samples and is observed to be linearly increasing with increase in adulterant content. Finally, the coefficient of sensitivity has been extracted for all varieties of honey considered in terms of the measured conductance values. Copyright © 2017 Elsevier B.V. All rights reserved.

Ab Initio Calculations of Transport Properties of Vanadium Oxides

NASA Astrophysics Data System (ADS)

Lamsal, Chiranjivi; Ravindra, N. M.

2018-04-01

The temperature-dependent transport properties of vanadium oxides have been studied near the Fermi energy using the Kohn-Sham band structure approach combined with Boltzmann transport equations. V2O5 exhibits significant thermoelectric properties, which can be attributed to its layered structure and stability. Highly anisotropic electrical conduction in V2O5 is clearly manifested in the calculations. Due to specific details of the band structure and anisotropic electron-phonon interactions, maxima and crossovers are also seen in the temperature-dependent Seebeck coefficient of V2O5. During the phase transition of VO2, the Seebeck coefficient changes by 18.9 µV/K, which is close to (within 10% of) the observed discontinuity of 17.3 µV/K.

Giant Pressure-Induced Enhancement of Seebeck Coefficient and Thermoelectric Efficiency in SnTe

DOE Office of Scientific and Technical Information (OSTI.GOV)

Baker, Jason; Kumar, Ravhi; Park, Changyong

The thermoelectric properties of polycrystalline SnTe have been measured up to 4.5 GPa at 330 K. SnTe shows an enormous enhancement in Seebeck coefficient, greater than 200 % after 3 GPa, which correlates to a known pressure-induced structural phase transition that is observed through simultaneous in situ X-ray diffraction measurement. We also measured electrical resistance and relative changes to the thermal conductivity, enabling the determination of relative changes in the dimensionless figure of merit (ZT), which increases dramatically after 3 GPa, reaching 350 % of the lowest pressure ZT value. Our results demonstrate a fundamental relationship between structure and thermoelectricmore » behaviours and suggest that pressure is an effective tool to control them.« less

Giant Pressure-Induced Enhancement of Seebeck Coefficient and Thermoelectric Efficiency in SnTe

DOE Office of Scientific and Technical Information (OSTI.GOV)

Baker, Jason; Kumar, Ravhi; Park, Changyong

The thermoelectric properties of polycrystalline SnTe have been measured up to 4.5 GPa at 330 K. SnTe shows an enormous enhancement in Seebeck coefficient, greater than 200 % after 3 GPa, which correlates to a known pressure-induced structural phase transition that is observed through simultaneous in situ X-ray diffraction measurement. Electrical resistance and relative changes to the thermal conductivity were also measured, enabling the determination of relative changes in the dimensionless figure of merit (ZT), which increases dramatically after 3 GPa, reaching 350 % of the lowest pressure ZT value. The results demonstrate a fundamental relationship between structure and thermoelectricmore » behaviours and suggest that pressure is an effective tool to control them.« less

Saturation and negative temperature coefficient of electrical resistivity in liquid iron-sulfur alloys at high densities from first-principles calculations

NASA Astrophysics Data System (ADS)

Wagle, Fabian; Steinle-Neumann, Gerd; de Koker, Nico

2018-03-01

We report results on electronic transport properties of liquid Fe-S alloys at conditions of planetary cores, computed using first-principle techniques in the Kubo-Greenwood formalism. We describe a combined effect of resistivity saturation due to temperature, compression, and chemistry by comparing the electron mean free path from the Drude response of optical conductivity to the mean interatomic distance. At high compression and high sulfur concentration the Ioffe-Regel condition is satisfied, and the temperature coefficient of resistivity changes sign from positive to negative. We show that this happens due to a decrease in the d density of states at the Fermi level in response to thermal broadening.

Giant Pressure-Induced Enhancement of Seebeck Coefficient and Thermoelectric Efficiency in SnTe

DOE PAGES

Baker, Jason; Kumar, Ravhi; Park, Changyong; ...

2017-10-30

The thermoelectric properties of polycrystalline SnTe have been measured up to 4.5 GPa at 330 K. SnTe shows an enormous enhancement in Seebeck coefficient, greater than 200 % after 3 GPa, which correlates to a known pressure-induced structural phase transition that is observed through simultaneous in situ X-ray diffraction measurement. We also measured electrical resistance and relative changes to the thermal conductivity, enabling the determination of relative changes in the dimensionless figure of merit (ZT), which increases dramatically after 3 GPa, reaching 350 % of the lowest pressure ZT value. Our results demonstrate a fundamental relationship between structure and thermoelectricmore » behaviours and suggest that pressure is an effective tool to control them.« less

Electrochemical Behavior of Sulfur in Aqueous Alkaline Solutions

NASA Astrophysics Data System (ADS)

Mamyrbekova, Aigul; Mamitova, A. D.; Mamyrbekova, Aizhan

2018-03-01

The kinetics and mechanism of the electrode oxidation-reduction of sulfur on an electrically conductive sulfur-graphite electrode in an alkaline solution was studied by the potentiodynamic method. To examine the mechanism of electrode processes occurring during AC polarization on a sulfur-graphite electrode, the cyclic polarization in both directions and anodic polarization curves were recorded. The kinetic parameters: charge transfer coefficients (α), diffusion coefficients ( D), heterogeneous rate constants of electrode process ( k s), and effective activation energies of the process ( E a) were calculated from the results of polarization measurements. An analysis of the results and calculated kinetic parameters of electrode processes showed that discharge ionization of sulfur in alkaline solutions occurs as a sequence of two stages and is a quasireversible process.

Improving high-altitude emp modeling capabilities by using a non-equilibrium electron swarm model to monitor conduction electron evolution

NASA Astrophysics Data System (ADS)

Pusateri, Elise Noel

An Electromagnetic Pulse (EMP) can severely disrupt the use of electronic devices in its path causing a significant amount of infrastructural damage. EMP can also cause breakdown of the surrounding atmosphere during lightning discharges. This makes modeling EMP phenomenon an important research effort in many military and atmospheric physics applications. EMP events include high-energy Compton electrons or photoelectrons that ionize air and produce low energy conduction electrons. A sufficient number of conduction electrons will damp or alter the EMP through conduction current. Therefore, it is important to understand how conduction electrons interact with air in order to accurately predict the EMP evolution and propagation in the air. It is common for EMP simulation codes to use an equilibrium ohmic model for computing the conduction current. Equilibrium ohmic models assume the conduction electrons are always in equilibrium with the local instantaneous electric field, i.e. for a specific EMP electric field, the conduction electrons instantaneously reach steady state without a transient process. An equilibrium model will work well if the electrons have time to reach their equilibrium distribution with respect to the rise time or duration of the EMP. If the time to reach equilibrium is comparable or longer than the rise time or duration of the EMP then the equilibrium model would not accurately predict the conduction current necessary for the EMP simulation. This is because transport coefficients used in the conduction current calculation will be found based on equilibrium reactions rates which may differ significantly from their non-equilibrium values. We see this deficiency in Los Alamos National Laboratory's EMP code, CHAP-LA (Compton High Altitude Pulse-Los Alamos), when modeling certain EMP scenarios at high altitudes, such as upward EMP, where the ionization rate by secondary electrons is over predicted by the equilibrium model, causing the EMP to short abruptly. The objective of the PhD research is to mitigate this effect by integrating a conduction electron model into CHAP-LA which can calculate the conduction current based on a non-equilibrium electron distribution. We propose to use an electron swarm model to monitor the time evolution of conduction electrons in the EMP environment which is characterized by electric field and pressure. Swarm theory uses various collision frequencies and reaction rates to study how the electron distribution and the resultant transport coefficients change with time, ultimately reaching an equilibrium distribution. Validation of the swarm model we develop is a necessary step for completion of the thesis work. After validation, the swarm model is integrated in the air chemistry model CHAP-LA employs for conduction electron simulations. We test high altitude EMP simulations with the swarm model option in the air chemistry model to show improvements in the computational capability of CHAP-LA. A swarm model has been developed that is based on a previous swarm model developed by Higgins, Longmire and O'Dell 1973, hereinafter HLO. The code used for the swarm model calculation solves a system of coupled differential equations for electric field, electron temperature, electron number density, and drift velocity. Important swarm parameters, including the momentum transfer collision frequency, energy transfer collision frequency, and ionization rate, are recalculated and compared to the previously reported empirical results given by HLO. These swarm parameters are found using BOLSIG+, a two term Boltzmann solver developed by Hagelaar and Pitchford 2005. BOLSIG+ utilizes updated electron scattering cross sections that are defined over an expanded energy range found in the atomic and molecular cross section database published by Phelps in the Phelps Database 2014 on the LXcat website created by Pancheshnyi et al. 2012. The swarm model is also updated from the original HLO model by including additional physical parameters such as the O2 electron attachment rate, recombination rate, and mutual neutralization rate. This necessitates tracking the positive and negative ion densities in the swarm model. Adding these parameters, especially electron attachment, is important at lower EMP altitudes where atmospheric density is high. We compare swarm model equilibrium temperatures and times using the HLO and BOLSIG+ coefficients for a uniform electric field of 1 StatV/cm for a range of atmospheric heights. This is done in order to test sensitivity to the swarm parameters used in the swarm model. It is shown that the equilibrium temperature and time are sensitive to the modifications in the collision frequency and ionization rate based on the updated electron interaction cross sections. We validate the swarm model by comparing ionization coefficients and equilibrium drift velocities to experimental results over a wide range of reduced electric field values. The final part of the PhD thesis work includes integrating the swarm model into CHAP-LA. We discuss the physics included in the CHAP-LA EMP model and demonstrate EMP damping behavior caused by the ohmic model at high altitudes. We report on numerical techniques for incorporation of the swarm model into CHAP-LA's Maxwell solver. This includes a discussion of integration techniques for Maxwell's equations in CHAP-LA using the swarm model calculated conduction current. We show improvements on EMP parameter calculations when modeling a high altitude, upward EMP scenario. This provides a novel computational capability that will have an important impact on the atmospheric and EMP research community.

Electrostatic Charging of Spacecraft in Geosynchronous Orbit

DTIC Science & Technology

1992-12-17

degrees above and below the equatorial plane. All mirrors are fabricated from " Zerodur * which has a very low coefficient of expansion, and are coated with a...conducting black paint, and the mirror itself is constructed of Zerodur and silvered on the front surface. The mirror is electrically isolated from the...TM Sp 389 provides East-West scanning, and the radiometer mirror is used to scan in the North-South direction; the mirror is moved by two pixels pcr

European Conference on Thermophysical Properties (11th) Held on 13-16 June 1988, University of Umea, Sweden. Abstracts

DTIC Science & Technology

1988-06-16

University of Urnea 901 87 UMEA SWEDEN E Karawacki Dept of Physics 48 Chalmers Tekniska Hogskola 412 96 GOTEBORG SWEDEN S Klarsfeld Glass Properties...Saunders, Electrical Conductivity and Dielectric Constant of Samarium Phosphate Glasses © 0 Andersson, P Andersson, R G Ross & G Backstrcm. Thermophysical...delivers extinction coefficients of about 50 m-/kg for pure (conventional) glass fiber insulations. We have thoroughly studied the potentials for a

Composition- and crystallinity-dependent thermoelectric properties of ternary BixSb2-xTey films

NASA Astrophysics Data System (ADS)

Kim, Jiwon; Lim, Jae-Hong; Myung, Nosang V.

2018-01-01

BixSb2-xTey films with controlled compositions were synthesized by a simple and cost-effective electrodeposition technique followed by post-annealing, for thermoelectric applications. Tailoring the chemical composition of ternary BixSb2-xTey materials is critical to adjust the carrier concentration and carrier type, which are crucial to determine their thermoelectric performance. Herein, the composition of electrodeposited BixSb2-xTey film was simply tailored by controlling the [Sb]/[Bi] ratio in the electrolytes while maintaining their dense and uniform morphology. Crystallographic properties of the BixSb2-xTey films, such as crystallinity and grain size changes, were confirmed by X-ray diffraction. Room-temperature measurements of electrical conductivity, Hall mobility, and carrier concentration revealed that the substitution of Bi with Sb decreased the carrier concentration, and increased the mobility. The Seebeck coefficient of the ternary BixSb2-xTey films transitioned between p- and n-type characteristics with an increase in the Bi content. Moreover, the mobility-dependent electrical conductivity of the Bi10Sb30Te60 film resulted in a high Seebeck coefficient owing to decreased carrier concentration of the film, leading to a power factor (PF) of ∼490 μW/m K2. This is more than 10 times higher than the PF values of binary nanocrystalline Sb2Te3 films.

Using Ge Secondary Phases to Enhance the Power Factor and Figure of Merit of Ge17Sb2Te20

NASA Astrophysics Data System (ADS)

Williams, Jared B.; Morelli, Donald T.

2017-05-01

Thermoelectric materials are the leading candidate today for applications in solid-state waste-heat recovery/cooling applications. Research and engineering has pushed the ZT, and overall conversion efficiency, of these materials to values which can be deemed practical for commercialization. However, many of the state-of-the-art thermoelectric materials of today utilize elements which are toxic, such as Ag, Pb, Tl, and Cd. Alloys of GeTe and Sb2Te3 were first explored for their applications in phase-change memory, because of their ability to rapidly alternate between crystalline and amorphous phases. Recently, these materials have been identified as materials with ZT ( S 2 T/ ρκ, where S is the Seebeck coefficient, ρ is the electrical resistivity, T is the operating temperature, and κ is the thermal conductivity) much greater than unity. In this work, the influence of elemental Ge as a secondary phase on transport in Ge17Sb2Te20 was explored. It was found that Ge introduces an additional scattering mechanism, which leads to increased electrical resistivity, Seebeck coefficient, and power factor values as high as 36 μW cm-1 K-2. The thermal conductivity was slightly reduced and the ZT was enhanced across the entire temperature range of measurement, with peak values greater than 2.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Rasit Koc; Geoffrey Swift; Hua Xie

Solid oxide fuel cell interconnect materials must meet stringent requirements. Such interconnects must operate at temperatures approaching 800 C while resisting oxidation and reduction, which can occur from the anode and cathode materials and the operating environment. They also must retain their electrical conductivity under these conditions and possess compatible coefficients of thermal expansion as the anode and cathode. Results are presented in this report for fuel cell interconnect candidate materials currently under investigation based upon nano-size titanium carbide (TiC) powders. The TiC is liquid phase sintered with either nickel (Ni) or nickel-aluminide (Ni{sub 3}Al) in varying concentrations. The oxidationmore » resistance of the submicron grain TiC-metal materials is presented as a function weight change versus time at 700 C and 800 C for varying content of metal/intermetallic in the system. Electrical conductivity at 800 C as a function of time is also presented for TiC-Ni to demonstrate the vitality of these materials for interconnect applications. TGA studies showed that the weight gain was 0.8 mg/cm{sup 2} for TiC(30)-Ni(30wt.%) after 100 hours in wet air at 800 C and the weight gain was calculated to be 0.5205 mg/cm{sup 2} for TiC(30)- Ni(10 wt.%) after 100 hours at 700 C and 100 hours at 800 C. At room temperature the electrical conductivity was measured to be 2444 1/[ohm.cm] for TiC-Ni compositions. The electrical conductivities at 800 C in air was recorded to be 19 1/[ohm.cm] after 125 hours. Two identical samples were supplied to PNNL (Dr. Jeff Stevenson) for ASR testing during the pre-decision period and currently they are being tested there. Fabrication, oxidation resistance and electrical conductivity studies indicate that TiC-Ni-Ni{sub 3}Al ternary appears to be a very important system for the development of interconnect composition for solid oxide fuel cells.« less

Atomic-layer-deposited Al2O3-HfO2-Al2O3 dielectrics for metal-insulator-metal capacitor applications

NASA Astrophysics Data System (ADS)

Ding, Shi-Jin; Zhu, Chunxiang; Li, Ming-Fu; Zhang, David Wei

2005-08-01

Atomic-layer-deposited Al2O3-HfO2-Al2O3 dielectrics have been investigated to replace conventional silicon oxide and nitride for radio frequency and analog metal-insulator-metal capacitors applications. In the case of 1-nm-Al2O3, sufficiently good electrical performances are achieved, including a high dielectric constant of ˜17, a small dissipation factor of 0.018 at 100kHz, an extremely low leakage current of 7.8×10-9A/cm2 at 1MV/cm and 125°C, perfect voltage coefficients of capacitance (74ppm/V2 and 10ppm/V). The quadratic voltage coefficient of capacitance decreases with the applied frequency due to the change of relaxation time with different carrier mobility in insulator, and correlates with the dielectric composition and thickness, which is of intrinsic property owing to electric field polarization. Furthermore, the conduction mechanism of the AHA dielectrics is also discussed, indicating the Schottky emission dominated at room temperature.

Novel Proton Conducting Solid Bio-polymer Electrolytes Based on Carboxymethyl Cellulose Doped with Oleic Acid and Plasticized with Glycerol

NASA Astrophysics Data System (ADS)

Chai, M. N.; Isa, M. I. N.

2016-06-01

The plasticized solid bio-polymer electrolytes (SBEs) system has been formed by introducing glycerol (Gly) as the plasticizer into the carboxymethyl cellulose (CMC) doped with oleic acid (OA) via solution casting techniques. The ionic conductivity of the plasticized SBEs has been studied using Electrical Impedance Spectroscopy. The highest conductivity achieved is 1.64 × 10-4 S cm-1 for system containing 40 wt. % of glycerol. FTIR deconvolution technique had shown that the conductivity of CMC-OA-Gly SBEs is primarily influenced by the number density of mobile ions. Transference number measurement has shown that the cation diffusion coefficient and ionic mobility is higher than anion which proved the plasticized polymer system is a proton conductor.

Influence of Oxygen Partial Pressure during Processing on the Thermoelectric Properties of Aerosol-Deposited CuFeO2

PubMed Central

Stöcker, Thomas; Exner, Jörg; Schubert, Michael; Streibl, Maximilian; Moos, Ralf

2016-01-01

In the field of thermoelectric energy conversion, oxide materials show promising potential due to their good stability in oxidizing environments. Hence, the influence of oxygen partial pressure during synthesis on the thermoelectric properties of Cu-Delafossites at high temperatures was investigated in this study. For these purposes, CuFeO2 powders were synthetized using a conventional mixed-oxide technique. X-ray diffraction (XRD) studies were conducted to determine the crystal structures of the delafossites associated with the oxygen content during the synthesis. Out of these powders, films with a thickness of about 25 µm were prepared by the relatively new aerosol-deposition (AD) coating technique. It is based on a room temperature impact consolidation process (RTIC) to deposit dense solid films of ceramic materials on various substrates without using a high-temperature step during the coating process. On these dense CuFeO2 films deposited on alumina substrates with electrode structures, the Seebeck coefficient and the electrical conductivity were measured as a function of temperature and oxygen partial pressure. We compared the thermoelectric properties of both standard processed and aerosol deposited CuFeO2 up to 900 °C and investigated the influence of oxygen partial pressure on the electrical conductivity, on the Seebeck coefficient and on the high temperature stability of CuFeO2. These studies may not only help to improve the thermoelectric material in the high-temperature case, but may also serve as an initial basis to establish a defect chemical model. PMID:28773351

Fractional calculus applied to the analysis of spectral electrical conductivity of clay-water system.

PubMed

Korosak, Dean; Cvikl, Bruno; Kramer, Janja; Jecl, Renata; Prapotnik, Anita

2007-06-16

The analysis of the low-frequency conductivity spectra of the clay-water mixtures is presented. The frequency dependence of the conductivity is shown to follow the power-law with the exponent n=0.67 before reaching the frequency-independent part. When scaled with the value of the frequency-independent part of the spectrum the conductivity spectra for samples at different water content values are shown to fit to a single master curve. It is argued that the observed conductivity dispersion is a consequence of the anomalously diffusing ions in the clay-water system. The fractional Langevin equation is then used to describe the stochastic dynamics of the single ion. The results indicate that the experimentally observed dielectric properties originate in anomalous ion transport in clay-water system characterized with time-dependent diffusion coefficient.

Drying temperature effects on electrical and optical properties of poly[2-methoxy-5-(2'-ethyl-hexyloxy)-1,4-phenylene vinylene] (MEH-PPV) thin film

NASA Astrophysics Data System (ADS)

Azhar, N. E. A.; Affendi, I. H. H.; Shafura, A. K.; Shariffudin, S. S.; Alrokayan, Salman A. H.; Khan, Haseeb A.; Rusop, M.

2016-07-01

Temperature effects on electrical and optical properties of a representative semiconducting polymer, poly[2-methoxy-5-(2'-ethyl-hexyloxy)-1,4-phenylene vinylene] (MEH-PPV), has recently attracted much attention. The MEH-PPV thin films were deposited at different drying temperature (anneal temperature) using spin-coating technique. The spin coating technique was used to produce uniform film onto large area. The MEH-PPV was dissolved in toluene solution to exhibits different optical and electrical properties. The absorption coefficient and bandgap was measured using UV-Visible-NIR (UV-VIS-NIR). The bandgap of MEH-PPV was effect by the thickness of thin films. For electrical properties, two-point probe was used to characterize the current-voltage measurement. The current-voltage measurement shows that the MEH-PPV thin films become more conductive at high temperature. This study will provide better performance and suitable for optoelectronic device especially OLEDs applications.

Drying temperature effects on electrical and optical properties of poly[2-methoxy-5-(2’-ethyl-hexyloxy)-1,4-phenylene vinylene] (MEH-PPV) thin film

DOE Office of Scientific and Technical Information (OSTI.GOV)

Azhar, N. E. A., E-mail: najwaezira@yahoo.com; Affendi, I. H. H., E-mail: irmahidayanti.halim@gmail.com; Shafura, A. K., E-mail: shafura@ymail.com

Temperature effects on electrical and optical properties of a representative semiconducting polymer, poly[2-methoxy-5-(2’-ethyl-hexyloxy)-1,4-phenylene vinylene] (MEH-PPV), has recently attracted much attention. The MEH-PPV thin films were deposited at different drying temperature (anneal temperature) using spin-coating technique. The spin coating technique was used to produce uniform film onto large area. The MEH-PPV was dissolved in toluene solution to exhibits different optical and electrical properties. The absorption coefficient and bandgap was measured using UV-Visible-NIR (UV-VIS-NIR). The bandgap of MEH-PPV was effect by the thickness of thin films. For electrical properties, two-point probe was used to characterize the current-voltage measurement. The current-voltage measurement showsmore » that the MEH-PPV thin films become more conductive at high temperature. This study will provide better performance and suitable for optoelectronic device especially OLEDs applications.« less

Sweeping as a multistep enrichment process in micellar electrokinetic chromatography: the retention factor gradient effect.

PubMed

El-Awady, Mohamed; Pyell, Ute

2013-07-05

The application of a new method developed for the assessment of sweeping efficiency in MEKC under homogeneous and inhomogeneous electric field conditions is extended to the general case, in which the distribution coefficient and the electric conductivity of the analyte in the sample zone and in the separation compartment are varied. As test analytes p-hydroxybenzoates (parabens), benzamide and some aromatic amines are studied under MEKC conditions with SDS as anionic surfactant. We show that in the general case - in contrast to the classical description - the obtainable enrichment factor is not only dependent on the retention factor of the analyte in the sample zone but also dependent on the retention factor in the background electrolyte (BGE). It is shown that in the general case sweeping is inherently a multistep focusing process. We describe an additional focusing/defocusing step (the retention factor gradient effect, RFGE) quantitatively by extending the classical equation employed for the description of the sweeping process with an additional focusing/defocusing factor. The validity of this equation is demonstrated experimentally (and theoretically) under variation of the organic solvent content (in the sample and/or the BGE), the type of organic solvent (in the sample and/or the BGE), the electric conductivity (in the sample), the pH (in the sample), and the concentration of surfactant (in the BGE). It is shown that very high enrichment factors can be obtained, if the pH in the sample zone makes possible to convert the analyte into a charged species that has a high distribution coefficient with respect to an oppositely charged micellar phase, while the pH in the BGE enables separation of the neutral species under moderate retention factor conditions. Copyright © 2013 Elsevier B.V. All rights reserved.

Anisotropic Effects on the Thermoelectric Properties of Highly Oriented Electrodeposited Bi2Te3 Films

PubMed Central

Manzano, Cristina V.; Abad, Begoña; Muñoz Rojo, Miguel; Koh, Yee Rui; Hodson, Stephen L.; Lopez Martinez, Antonio M.; Xu, Xianfan; Shakouri, Ali; Sands, Timothy D.; Borca-Tasciuc, Theodorian; Martin-Gonzalez, Marisol

2016-01-01

Highly oriented [1 1 0] Bi2Te3 films were obtained by pulsed electrodeposition. The structure, composition, and morphology of these films were characterized. The thermoelectric figure of merit (zT), both parallel and perpendicular to the substrate surface, were determined by measuring the Seebeck coefficient, electrical conductivity, and thermal conductivity in each direction. At 300 K, the in-plane and out-of-plane figure of merits of these Bi2Te3 films were (5.6 ± 1.2)·10−2 and (10.4 ± 2.6)·10−2, respectively. PMID:26776726

A potential half-Heusler thermoelectric material ScAuSn: A first principle study

NASA Astrophysics Data System (ADS)

Joshi, H.; Rai, D. P.; Thapa, R. K.

2018-04-01

Density Functional Theory along with semi classical Boltzmann transport theory have been applied to study the electronic and thermoelectric property of the Heusler alloy ScAuSn. It has been found that ScAuSn is an indirect band gap semiconductor with a gap of 0.344 eV. The thermoelectric properties such as electrical conductivity (σ), Seebeck coefficient (S), electronic thermal conductivity (κ) etc. are reported as a function of chemical potential in the region ± 2.0 eV, with respect to constant temperature. The calculated ZT value is almost equal to 1, thus making ScAuSn a potential thermoelectric candidate.

In vivo electrical conductivity of hepatic tumours.

PubMed

Haemmerich, Dieter; Staelin, S T; Tsai, J Z; Tungjitkusolmun, S; Mahvi, D M; Webster, J G

2003-05-01

Knowledge of electrical tissue conductivity is necessary to determine deposition of electromagnetic energy and can further be used to diagnostically differentiate between normal and neoplastic tissue. We measured 17 rats with a total of 24 tumours of the K12/TRb rat colon cancer cell line. In each animal we measured in vivo hepatic tumour and normal tissue conductivity at seven frequencies from 10 Hz to 1 MHz, at different tumour stages between 6 and 12 weeks after induction. Conductivity of normal liver tissue was 1.26 +/- 0.15 mS cm(-1) at 10 Hz, and 4.61 +/- 0.42 mS cm(-1) at 1 MHz. Conductivity of tumour was 2.69 +/- 0.91 mS cm(-1) at 10 Hz, and 5.23 +/- 0.82 mS cm(-1) at 1 MHz. Conductivity was significantly different between normal and tumour tissue (p < 0.05). We determined the percentage of necrosis and fibrosis at the measurement site. We fitted the conductivity data to the Cole-Cole model. For the tumour data we determined Spearman's correlation coefficients between the Cole-Cole parameters and age, necrosis, fibrosis and tumour volume and found significant correlation between necrosis and the Cole-Cole parameters (p < 0.05). We conclude that necrosis within the tumour and the associated membrane breakdown is likely responsible for the observed change in conductivity.

Side-Chain Effects on the Thermoelectric Properties of Fluorene-Based Copolymers.

PubMed

Liang, Ansheng; Zhou, Xiaoyan; Zhou, Wenqiao; Wan, Tao; Wang, Luhai; Pan, Chengjun; Wang, Lei

2017-09-01

Three conjugated polymers with alkyl chains of different lengths are designed and synthesized, and their structure-property relationship as organic thermoelectric materials is systematically elucidated. All three polymers show similar photophysical properties, thermal properties, and mechanical properties; however, their thermoelectric performance is influenced by the length of their side chains. The length of the alkyl chain significantly influences the electrical conductivity of the conjugated polymers, and polymers with a short alkyl chain exhibit better conductivity than those with a long alkyl chain. The length of the alkyl chain has little effect on the Seebeck coefficient. Only a slight increase in the Seebeck coefficient is observed with the increasing length of the alkyl chain. The purpose of this study is to provide comprehensive insight into fine-tuning the thermoelectric properties of conjugated polymers as a function of side-chain engineering, thereby providing a novel perspective into the design of high-performance thermoelectric conjugated polymers. © 2017 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Thermoelectric properties of doped BaHfO{sub 3}

DOE Office of Scientific and Technical Information (OSTI.GOV)

Dixit, Chandra Kr., E-mail: ckparadise@gmail.com, E-mail: sharmarameshfgiet@gmail.com; Bhamu, K. C.; Sharma, Ramesh, E-mail: ckparadise@gmail.com, E-mail: sharmarameshfgiet@gmail.com

2016-05-06

We have studied the structural stability, electronic structure, optical properties and thermoelectric properties of doped BaHfO{sub 3} by full potential linearized augmented plane wave (FP-LAPW) method. The electronic structure of BaHfO{sub 3} doped with Sr shows enhances the indirect band gaps of 3.53 eV, 3.58 eV. The charge density plots show strong ionic bonding in Ba-Hf, and ionic and covalent bonding between Hf and O. Calculations of the optical spectra, viz., the dielectric function, refractive index and extinction coefficient are performed for the energy range are calculated and analyzed. Thermoelectric properties of semi conducting are also reported first time. Themore » doped BaHfO{sub 3} is approximately wide band gap semiconductor with the large p-type Seebeck coefficient. The power factor of BaHfO{sub 3} is increased with Sr doping, decreases because of low electrical resistivity and thermal conductivity.« less

Numerical study of MHD nanofluid flow and heat transfer past a bidirectional exponentially stretching sheet

NASA Astrophysics Data System (ADS)

Ahmad, Rida; Mustafa, M.; Hayat, T.; Alsaedi, A.

2016-06-01

Recent advancements in nanotechnology have led to the discovery of new generation coolants known as nanofluids. Nanofluids possess novel and unique characteristics which are fruitful in numerous cooling applications. Current work is undertaken to address the heat transfer in MHD three-dimensional flow of magnetic nanofluid (ferrofluid) over a bidirectional exponentially stretching sheet. The base fluid is considered as water which consists of magnetite-Fe3O4 nanoparticles. Exponentially varying surface temperature distribution is accounted. Problem formulation is presented through the Maxwell models for effective electrical conductivity and effective thermal conductivity of nanofluid. Similarity transformations give rise to a coupled non-linear differential system which is solved numerically. Appreciable growth in the convective heat transfer coefficient is observed when nanoparticle volume fraction is augmented. Temperature exponent parameter serves to enhance the heat transfer from the surface. Moreover the skin friction coefficient is directly proportional to both magnetic field strength and nanoparticle volume fraction.

Thermoelectric properties of AgSbTe₂ from first-principles calculations

DOE Office of Scientific and Technical Information (OSTI.GOV)

Rezaei, Nafiseh; Akbarzadeh, Hadi; Hashemifar, S. Javad, E-mail: hashemifar@cc.iut.ac.ir

2014-09-14

The structural, electronic, and transport properties of AgSbTe₂ are studied by using full-relativistic first-principles electronic structure calculation and semiclassical description of transport parameters. The results indicate that, within various exchange-correlation functionals, the cubic Fd3⁻m and trigonal R3⁻m structures of AgSbTe₂ are more stable than two other considered structures. The computed Seebeck coefficients at different values of the band gap and carrier concentration are accurately compared with the available experimental data to speculate a band gap of about 0.1–0.35 eV for AgSbTe₂ compound, in agreement with our calculated electronic structure within the hybrid HSE (Heyd-Scuseria-Ernzerhof) functional. By calculating the semiclassical Seebeckmore » coefficient, electrical conductivity, and electronic part of thermal conductivity, we present the theoretical upper limit of the thermoelectric figure of merit of AgSbTe₂ as a function of temperature and carrier concentration.« less

High Performance Graphene Nano-ribbon Thermoelectric Devices by Incorporation and Dimensional Tuning of Nanopores

PubMed Central

Sharafat Hossain, Md; Al-Dirini, Feras; Hossain, Faruque M.; Skafidas, Efstratios

2015-01-01

Thermoelectric properties of Graphene nano-ribbons (GNRs) with nanopores (NPs) are explored for a range of pore dimensions in order to achieve a high performance two-dimensional nano-scale thermoelectric device. We reduce thermal conductivity of GNRs by introducing pores in them in order to enhance their thermoelectric performance. The electrical properties (Seebeck coefficient and conductivity) of the device usually degrade with pore inclusion; however, we tune the pore to its optimal dimension in order to minimize this degradation, enhancing the overall thermoelectric performance (high ZT value) of our device. We observe that the side channel width plays an important role to achieve optimal performance while the effect of pore length is less pronounced. This result is consistent with the fact that electronic conduction in GNRs is dominated along its edges. Ballistic transport regime is assumed and a semi-empirical method using Huckel basis set is used to obtain the electrical properties, while the phononic system is characterized by Tersoff empirical potential model. The proposed device structure has potential applications as a nanoscale local cooler and as a thermoelectric power generator. PMID:26083450

DOE Office of Scientific and Technical Information (OSTI.GOV)

Hu, Dehua; Liu, Qing; Tisdale, Jeremy

This paper reports Seebeck effects driven by both surface polarization difference and entropy difference by using intramolecular charge-transfer states in n-type and p-type conjugated polymers, namely IIDT and IIDDT, based on vertical conductor/polymer/conductor thin-film devices. Large Seebeck coefficients of -898 V/K and 1300 V/K from are observed from n-type IIDT p-type IIDDT, respectively, when the charge-transfer states are generated by a white light illumination of 100 mW/cm2. Simultaneously, electrical conductivities are increased from almost insulating states in dark condition to conducting states under photoexcitation in both n-type IIDT and p-type IIDDT devices. We find that the intramolecular charge-transfer states canmore » largely enhance Seebeck effects in the n-type IIDT and p-type IIDDT devices driven by both surface polarization difference and entropy difference. Furthermore, the Seebeck effects can be shifted between polarization and entropy regimes when electrical conductivities are changed. This reveals a new concept to develop Seebeck effects by controlling polarization and entropy regimes based on charge-transfer states in vertical conductor/polymer/conductor thin-film devices.« less

Geophysical and Geotechnical Characterization of Beta-1,3/1,6-glucan Biopolymer treated Soil

NASA Astrophysics Data System (ADS)

Chang, I.; Cho, G.

2012-12-01

Bacteria or microbes in soil excrete hydrocarbon (e.g. polysaccharide) by-products which are called biopolymers. These biopolymers (or sometime biofilms) recently begun to make a mark on soil erosion control, aggregate stabilization, and drilling enhancement. However, the biological effect on soil behavior (e.g. bio-clogging or bio-cementation) has been poorly understood. In this study, the bio-cementation and bio-clogging effect induced by the existence of β-1,3/1,6-glucan biopolymers in soil were evaluated through a series of geophysical and geotechnical characterization tests in laboratory. According to the experimental test results, as the β-1,3/1,6-glucan content in soil increases, the compressive strength and shear wave velocity increase (i.e., bio-cementation) while the hydraulic conductivity decreases (i.e., bio-clogging) but the electrical conductivity increases due to the high electrical conductivity characteristic of β-1,3/1,6-glucan fibers. Coefficient of consolidation variation with the increases of β-1,3/1,6-glucan content in soil. SEM image of β-1,3/1,6-glucan treated soil. Fibers are form matices with soil particles.

Electrical and thermoelectric transport properties of two-dimensional fermionic systems with k-cubic spin-orbit coupling.

PubMed

Mawrie, Alestin; Verma, Sonu; Ghosh, Tarun Kanti

2017-10-25

We investigate the effect of k-cubic spin-orbit interaction on the electrical and thermoelectric transport properties of two-dimensional fermionic systems. We obtain exact analytical expressions of the inverse relaxation time (IRT) and the Drude conductivity for long-range Coulomb and short-range delta scattering potentials. The IRT reveals that the scattering is completely suppressed along the three directions [Formula: see text] with [Formula: see text]. We also obtain analytical results of the thermopower and thermal conductivity at low temperature. The thermoelectric transport coefficients obey the Wiedemann-Franz law, even in the presence of k-cubic Rashba spin-orbit interaction (RSOI) at low temperature. In the presence of a quantizing magnetic field, the signature of the RSOI is revealed through the appearance of the beating pattern in the Shubnikov-de Haas (SdH) oscillations of thermopower and thermal conductivity in the low magnetic field regime. The empirical formulae for the SdH oscillation frequencies accurately describe the locations of the beating nodes. The beating pattern in magnetothermoelectric measurement can be used to extract the spin-orbit coupling constant.

High Performance Graphene Nano-ribbon Thermoelectric Devices by Incorporation and Dimensional Tuning of Nanopores.

PubMed

Hossain, Md Sharafat; Al-Dirini, Feras; Hossain, Faruque M; Skafidas, Efstratios

2015-06-17

Thermoelectric properties of Graphene nano-ribbons (GNRs) with nanopores (NPs) are explored for a range of pore dimensions in order to achieve a high performance two-dimensional nano-scale thermoelectric device. We reduce thermal conductivity of GNRs by introducing pores in them in order to enhance their thermoelectric performance. The electrical properties (Seebeck coefficient and conductivity) of the device usually degrade with pore inclusion; however, we tune the pore to its optimal dimension in order to minimize this degradation, enhancing the overall thermoelectric performance (high ZT value) of our device. We observe that the side channel width plays an important role to achieve optimal performance while the effect of pore length is less pronounced. This result is consistent with the fact that electronic conduction in GNRs is dominated along its edges. Ballistic transport regime is assumed and a semi-empirical method using Huckel basis set is used to obtain the electrical properties, while the phononic system is characterized by Tersoff empirical potential model. The proposed device structure has potential applications as a nanoscale local cooler and as a thermoelectric power generator.

Optical and electrical properties of CuMO2 transparent p-type conductors

NASA Astrophysics Data System (ADS)

Draeseke, A. D.; Jayaraj, M. K.; Ulbrich, T.; Kroupp, M.; Tate, J.; Nagarajan, R.; Oblezov, A.; Sleight, A. W.

2001-03-01

Wide band gap oxides of the type CuMO2 with the delafossite structure are p-type conductors and many of them are transparent. Films of these p-type oxides have been grown by sputtering and thermal evaporation, and characterized electrically and optically. We present transport and optical transmission measurements for CuY_1-xCa_xO_2, CuScO_2+x and other similar materials. Conductivities are in the range 1 200 S/cm and depend on details of film preparation. The carriers are p-type as determined by thermopower measurements, and typical Seebeck coefficients are several hundred µV/K. Optical transparency varies considerably, but is about 40% at 550 nm for the highest conductivity films. Excellent transparency can be achieved at the expense of conductivity, and optimization is being studied. Band gaps derived from optical transmission are larger than 3.1 eV. Prototype all-oxide pn diodes have been fabricated. This work was partially supported by the NSF under DMR-0071727 and by the Research Corporation under RA0291.

Effect of Printing Parameters on Tensile, Dynamic Mechanical, and Thermoelectric Properties of FDM 3D Printed CABS/ZnO Composites.

PubMed

Aw, Yah Yun; Yeoh, Cheow Keat; Idris, Muhammad Asri; Teh, Pei Leng; Hamzah, Khairul Amali; Sazali, Shulizawati Aqzna

2018-03-22

Fused deposition modelling (FDM) has been widely used in medical appliances, automobile, aircraft and aerospace, household appliances, toys, and many other fields. The ease of processing, low cost and high flexibility of FDM technique are strong advantages compared to other techniques for thermoelectric polymer composite fabrication. This research work focuses on the effect of two crucial printing parameters (infill density and printing pattern) on the tensile, dynamic mechanical, and thermoelectric properties of conductive acrylonitrile butadiene styrene/zinc oxide (CABS/ZnO composites fabricated by FDM technique. Results revealed significant improvement in tensile strength and Young's modulus, with a decrease in elongation at break with infill density. Improvement in dynamic storage modulus was observed when infill density changed from 50% to 100%. However, the loss modulus and damping factor reduced gradually. The increase of thermal conductivity was relatively smaller compared to the improvement of electrical conductivity and Seebeck coefficient, therefore, the calculated figure of merit (ZT) value increased with infill density. Line pattern performed better than rectilinear, especially in tensile properties and electrical conductivity. From the results obtained, FDM-fabricated CABS/ZnO showed much potential as a promising candidate for thermoelectric application .

PEDOT:PSS/graphene quantum dots films with enhanced thermoelectric properties via strong interfacial interaction and phase separation.

PubMed

Du, Fei-Peng; Cao, Nan-Nan; Zhang, Yun-Fei; Fu, Ping; Wu, Yan-Guang; Lin, Zhi-Dong; Shi, Run; Amini, Abbas; Cheng, Chun

2018-04-24

The typical conductive polymer of PEDOT:PSS has recently attracted intensive attention in thermoelectric conversion because of its low cost and low thermal conductivity as well as high electrical conductivity. However, compared to inorganic counterparts, the relatively poor thermoelectric performance of PEDOT:PSS has greatly limited its development and high-tech applications. Here, we report a dramatic enhancement in the thermoelectric performance of PEDOT:PSS by constructing unique composite films with graphene quantum dots (GQDs). At room temperature, the electrical conductivity and Seebeck coefficient of PEDOT:PSS/GQDs reached to 7172 S/m and 14.6 μV/K, respectively, which are 30.99% and 113.2% higher than those of pristine PEDOT:PSS. As a result, the power factor of the optimized PEDOT:PSS/GQDs composite is 550% higher than that of pristine PEDOT:PSS. These significant improvements are attributed to the ordered alignment of PEDOT chains on the surface of GQDs, originated from the strong interfacial interaction between PEDOT:PSS and GQDs and the separation of PEDOT and PSS phases. This study evidently provides a promising route for PEDOT:PSS applied in high-efficiency thermoelectric conversion.

Electrical properties of dislocations in III-Nitrides

NASA Astrophysics Data System (ADS)

Cavalcoli, D.; Minj, A.; Pandey, S.; Cavallini, A.

2014-02-01

Research on GaN, AlN, InN (III-N) and their alloys is achieving new heights due their high potential applications in photonics and electronics. III-N semiconductors are mostly grown epitaxially on sapphire, and due to the large lattice mismatch and the differences in the thermal expansion coefficients, the structures usually contain many threading dislocations (TDs). While their structural properties have been widely investigated, their electrical characteristics and their role in the transport properties of the devices are still debated. In the present contribution we will show conductive AFM studies of TDs in GaN and Al/In GaN ternary alloys to evidence the role of strain, different surface polarity and composition on their electrical properties. Local I-V curves measured at TDs allowed us to clarify their role in the macroscopic electrical properties (leakage current, mobilities) of III-N based devices. Samples obtained by different growers (AIXTRON, III-V Lab) were studied. The comparison between the results obtained in the different alloys allowed us to understand the role of In and Al on the TDs electrical properties.

Ionic molal conductivities, activity coefficients, and dissociation constants of HAsO42− and H2AsO4− from 5 to 90°C and ionic strengths from 0.001 up to 3 mol kg−1 and applications in natural systems

USGS Publications Warehouse

Zhu, Xiangyu; Nordstrom, D. Kirk; McCleskey, R. Blaine; Wang, Rucheng

2016-01-01

Arsenic is known to be one of the most toxic inorganic elements, causing worldwide environmental contamination. However, many fundamental properties related to aqueous arsenic species are not well known which will inhibit our ability to understand the geochemical behavior of arsenic (e.g. speciation, transport, and solubility). Here, the electrical conductivity of Na2HAsO4 solutions has been measured over the concentration range of 0.001–1 mol kg−1 and the temperature range of 5–90°C. Ionic strength and temperature-dependent equations were derived for the molal conductivity of HAsO42−and H2AsO4− aqueous ions. Combined with speciation calculations and the approach used by McCleskey et al. (2012b), these equations can be used to calculate the electrical conductivities of arsenic-rich waters having a large range of effective ionic strengths (0.001–3 mol kg−1) and temperatures (5–90°C). Individual ion activity coefficients for HAsO42− and H2AsO4− in the form of the Hückel equation were also derived using the mean salt method and the mean activity coefficients of K2HAsO4 (0.001–1 mol kg−1) and KH2AsO4 (0.001–1.3 mol kg−1). A check on these activity coefficients was made by calculating mean activity coefficients for Na2HAsO4 and NaH2AsO4 solutions and comparing them to measured values. At the same time Na-arsenate complexes were evaluated. The NaH2AsO40 ion pair is negligible in NaH2AsO4 solutions up to 1.3 mol kg−1. The NaHAsO4− ion pair is important in NaHAsO4 solutions >0.1 mol kg−1 and the formation constant of 100.69 was confirmed. The enthalpy, entropy, free energy and heat capacity for the second and third arsenic acid dissociation reactions were calculated from pH measurements. These properties have been incorporated into a widely used geochemical calculation code WATEQ4F and applied to natural arsenic waters. For arsenic spiked water samples from Yellowstone National Park, the mean difference between the calculated and measured conductivities have been improved from −18% to −1.0% with a standard deviation of 2.4% and the mean charge balances have been improved from 28% to 0.6% with a standard deviation of 1.5%.

Plasma Polypyrrole Coated Hybrid Composites with Improved Mechanical and Electrical Properties for Aerospace Applications

NASA Astrophysics Data System (ADS)

Yavuz, Hande; Bai, Jinbo

2018-06-01

This paper deals with the dielectric barrier discharge assisted continuous plasma polypyrrole deposition on CNT-grafted carbon fibers for conductive composite applications. The simultaneous effects of three controllable factors have been studied on the electrical resistivity (ER) of these two material systems based on multivariate experimental design methodology. A posterior probability referring to Benjamini-Hochberg (BH) false discovery rate was explored as multiple testing corrections of the t-test p values. BH significance threshold of 0.05 was produced truly statistically significant coefficients to describe ER of two material systems. A group of plasma modified samples was chosen to be used for composite manufacturing to drive an assessment of interlaminar shear properties under static loading. Transversal and longitudinal electrical resistivity (DC, ω =0) of composite samples were studied to compare both the effects of CNT grafting and plasma modification on ER of resultant composites.

Plasma Polypyrrole Coated Hybrid Composites with Improved Mechanical and Electrical Properties for Aerospace Applications

NASA Astrophysics Data System (ADS)

Yavuz, Hande; Bai, Jinbo

2017-09-01

This paper deals with the dielectric barrier discharge assisted continuous plasma polypyrrole deposition on CNT-grafted carbon fibers for conductive composite applications. The simultaneous effects of three controllable factors have been studied on the electrical resistivity (ER) of these two material systems based on multivariate experimental design methodology. A posterior probability referring to Benjamini-Hochberg (BH) false discovery rate was explored as multiple testing corrections of the t-test p values. BH significance threshold of 0.05 was produced truly statistically significant coefficients to describe ER of two material systems. A group of plasma modified samples was chosen to be used for composite manufacturing to drive an assessment of interlaminar shear properties under static loading. Transversal and longitudinal electrical resistivity (DC, ω =0) of composite samples were studied to compare both the effects of CNT grafting and plasma modification on ER of resultant composites.

Electric heater for nuclear fuel rod simulators

DOEpatents

McCulloch, Reginald W.; Morgan, Jr., Chester S.; Dial, Ralph E.

1982-01-01

The present invention is directed to an electric cartridge-type heater for use as a simulator for a nuclear fuel pin in reactor studies. The heater comprises an elongated cylindrical housing containing a longitudinally extending helically wound heating element with the heating element radially inwardly separated from the housing. Crushed cold-pressed preforms of boron nitride electrically insulate the heating element from the housing while providing good thermal conductivity. Crushed cold-pressed preforms of magnesia or a magnesia-15 percent boron nitride mixture are disposed in the cavity of the helical heating element. The coefficient of thermal expansion of the magnesia or the magnesia-boron nitride mixture is higher than that of the boron nitride disposed about the heating element for urging the boron nitride radially outwardly against the housing during elevated temperatures to assure adequate thermal contact between the housing and the boron nitride.

Magnetic field tunable ac electrical transport of LaFeO3-wax nanocomposites

NASA Astrophysics Data System (ADS)

Roy, Supratim; Mandal, S. K.; Debnath, Rajesh; Nath, Debajyoti; Dey, P.

2018-04-01

Single phase perovskite LaFeO3 nanoparticles have been prepared through chemical pyrophoric reaction process. It is further grinded with paraffin wax of quantity 0.5 wt% of total composition to obtain an organic composite 99.5%LaFeO3-0.5%Wax. Studies of ac electrical properties viz. complex impedance, dielectric response, loss coefficient have been done in presence of external dc magnetic field, which reveals a good magnetoimpedance (˜221%) and a negative magnetodielectric (˜ 64%). The value of impedance, its real and imaginary part is observed to increase with dc field. The composite exhibits high dielectric constant (˜4760). The ac conductivity is found to decrease with applied field and increase with ac frequency.

Electrical properties of surface and interface layers of the N- and In-polar undoped and Mg-doped InN layers grown by PA MBE

NASA Astrophysics Data System (ADS)

Komissarova, T. A.; Kampert, E.; Law, J.; Jmerik, V. N.; Paturi, P.; Wang, X.; Yoshikawa, A.; Ivanov, S. V.

2018-01-01

Electrical properties of N-polar undoped and Mg-doped InN layers and In-polar undoped InN layers grown by plasma-assisted molecular beam epitaxy (PA MBE) were studied. Transport parameters of the surface and interface layers were determined from the measurements of the Hall coefficient and resistivity as well as the Shubnikov-de Haas oscillations at magnetic fields up to 60 T. Contributions of the 2D surface, 3D near-interface, and 2D interface layers to the total conductivity of the InN films were defined and discussed to be dependent on InN surface polarity, Mg doping, and PA MBE growth conditions.

Nonreciprocity of electrically excited thermal spin signals in CoFeAl-Cu-Py lateral spin valves

NASA Astrophysics Data System (ADS)

Hu, Shaojie; Cui, Xiaomin; Nomura, Tatsuya; Min, Tai; Kimura, Takashi

2017-03-01

Electrical and thermal spin currents excited by an electric current have been systematically investigated in lateral spin valves consisting of CoFeAl and Ni80Fe20 (Py) wires bridged by a Cu strip. In the electrical spin signal, the reciprocity between the current and voltage probes was clearly confirmed. However, a significant nonreciprocity was observed in the thermal spin signal. This provides clear evidence that a large spin-dependent Seebeck coefficient is more important than the spin polarization for efficient thermal spin injection and detection. We demonstrate that the spin-dependent Seebeck coefficient can be simply evaluated from the thermal spin signals for two configurations. Our experimental description paves a way for evaluating a small spin-dependent Seebeck coefficient for conventional ferromagnets without using complicated parameters.

Potential reduction of energy consumption in public university library

NASA Astrophysics Data System (ADS)

Noranai, Z.; Azman, ADF

2017-09-01

Efficient electrical energy usage has been recognized as one of the important factor to reduce cost of electrical energy consumption. Various parties have been emphasized about the importance of using electrical energy efficiently. Inefficient usage of electrical energy usage lead to biggest factor increasing of administration cost in Universiti Tun Hussein Onn Malaysia. With this in view, a project the investigate potential reduction electrical energy consumption in Universiti Tun Hussein Onn Malaysia was carried out. In this project, a case study involving electrical energy consumption of Perpustakaan Tunku Tun Aminah was conducted. The scopes of this project are to identify energy consumption in selected building and to find the factors that contributing to wastage of electrical energy. The MS1525:2001, Malaysian Standard - Code of practice on energy efficiency and use of renewable energy for non-residential buildings was used as reference. From the result, 4 saving measure had been proposed which is change type of the lamp, install sensor, decrease the number of lamp and improve shading coefficient on glass. This saving measure is suggested to improve the efficiency of electrical energy consumption. Improve of human behaviour toward saving energy measure can reduce 10% from the total of saving cost while on building technical measure can reduce 90% from total saving cost.

Importance of Schottky barriers for wide-bandgap thermoelectric devices

NASA Astrophysics Data System (ADS)

Wais, M.; Held, K.; Battiato, M.

2018-04-01

The development of thermoelectric devices faces not only the challenge of optimizing the Seebeck coefficient, the electrical and thermal conductivity of the active material, but also further bottlenecks when going from the thermoelectric material to an actual device, e.g., the dopant diffusion at the hot contact. We show that for large bandgap thermoelectrics another aspect can dramatically reduce the efficiency of the device: the formation of Schottky barriers. Understanding the effect, it can then be fixed rather cheaply by a two-metal contact solution.

Electromagnetic Fields of a Uniform Sphere in a Uniform Conducting Medium with Application to Dipole Sources

DTIC Science & Technology

1991-09-01

12b. DISTRIBUTION CODE Approved for public release; distribution is unlimited. 13. ABSTRACT (Maximum 200 words) Vector spherical harmonic expansions are...electric and magnetic field vectors from E rand B - r alone. Genural expressions are given relating the scattered field expansion coefficients to the source...Prescnbed by ANSI Std. Z39-18 29W-102 NCSC TR 426-90 CONTENTS Pag o INTRODUCTION 1 BACKGROUND 1 ANGULAR MOMENTUM OPERATOR AND VECTOR SPHERICAL

Decouple electronic and phononic transport in nanotwinned structures: a new strategy for enhancing the figure-of-merit of thermoelectrics.

PubMed

Zhou, Yanguang; Gong, Xiaojing; Xu, Ben; Hu, Ming

2017-07-20

Thermoelectric (TE) materials manifest themselves to enable direct conversion of temperature differences to electric power and vice versa. Though remarkable advances have been achieved in the past decades for various TE systems, the energy conversion efficiency of TE devices, which is characterized by a dimensionless figure-of-merit (ZT = S 2 σT/(κ el + κ ph )), generally remains a poor factor that severely limits TE devices' competitiveness and range of employment. The bottleneck for substantially boosting the ZT coefficient lies in the strong interdependence of the physical parameters involved in electronic (S and σ, and κ el ) and phononic (κ ph ) transport. Herein, we propose a new strategy of incorporating nanotwinned structures to decouple electronic and phononic transport. Combining the new concept of nanotwinned structures with the previously widely used nanocrystalline approach, the power factor of the nanotwin-nanocrystalline Si heterostructures is enhanced by 120% compared to that of bulk crystalline Si, while the lattice thermal conductivity is reduced to a level well below the amorphous limit, yielding a theoretical limit of 0.52 and 0.9 for ZT coefficient at room temperature and 1100 K, respectively. This value is almost two orders of magnitude larger than that for bulk Si and twice that for polycrystalline Si. Even for the experimentally obtained nanotwin-nanocrystalline heterostructures (e.g. grain size of 5 nm), the ZT coefficient can be as high as 0.26 at room temperature and 0.7 at 1100 K, which is the highest ZT value among all Si-based bulk nanostructures found thus far. Such substantial improvement stems from two aspects: (1) the improvement in the power factor is caused due to an increase in the Seebeck coefficient (degeneracy of the band valley) and the enhancement of electrical conductivity (the reduction of the effective band mass) and (2) the significant reduction of the lattice thermal conductivity is mainly caused due to the extremely strong phonon-grain boundary and phonon-twin boundary scattering. Our results suggest that nanotwinned structures are excellent building blocks for enhancing TE performance in diamond-like semiconductors, and our study provides a new strategy for the innovative development of other TE materials.

Supercritical fluid in the mantle transition zone deduced from H-D interdiffusion of wadsleyite

NASA Astrophysics Data System (ADS)

Sun, Wei; Yoshino, Takashi; Sakamoto, Naoya; Yurimoto, Hisayoshi

2018-02-01

Knowledge of the distribution of water in the Earth's mantle is key to understanding the mantle convection and geochemical evolution of the Earth. As wadsleyite and ringwoodite can incorporate large amounts of water in their crystal structures, proton conduction has been invoked to account for the widespread conductive anomalies observed in the mantle wedge, where descending slab stagnates at the transition zone. However, there is a lot of controversy on whether proton conduction by itself is able to explain such anomalies, because of large discrepancy in the extent of the water effect deduced from previous electrical conductivity measurements on hydrous polycrystalline wadsleyite and ringwoodite. Here we report the hydrogen self-diffusion coefficient obtained from H-D interdiffusion experiments in wadsleyite single-crystal couples. Our results demonstrate that the effect of water on the electrical conductivity of wadsleyite is limited and hydrous wadsleyite by itself is unable to explain conductive anomalies in the transition zone. In contrast, the expected hydrogen effective diffusion does not allow the wide propagation of water between the stagnant slab and surrounding mantle, probably leading to persistence of local water saturation and continuous release of supercritical fluids at the stagnant slab roof on geological time scales. This phenomenon provides an alternative explanation for both the high-conductivity and seismic-velocity anomalies observed in the mantle wedge at the transition-zone depth.

Thermoelectric properties of Sn doped BiCuSeO

NASA Astrophysics Data System (ADS)

Das, Sayan; Chetty, Raju; Wojciechowski, Krzysztof; Suwas, Satyam; Mallik, Ramesh Chandra

2017-10-01

BiCuSeO and Bi1-xSnxCuSeO (x = 0.02, 0.04, 0.06, 0.08) were prepared by a two-step solid state synthesis. The phase purity and the crystal structure were investigated by the X-Ray Diffraction (XRD) and confirmed by Energy Dispersive Spectroscopy (EDS). The volatilization of Bi and Bi2O3 lead to off-stoichiometry of the main phase and the formation of CuSe2 secondary phase in the undoped sample. SnO2 secondary phases were found in the doped samples. Both the Seebeck coefficient and the electrical resistivity, measured from the room temperature to 773 K linearly increases with the temperature, which indicates that the sample have metallic like behavior. The origin of such a behavior is due to high hole concentration originating from the Bi and the O vacancies. The Sn +4 valence state was confirmed from the X-Ray Photoelectron Spectroscopy (XPS) and from the reduction of lattice parameter 'a' with doping. The substitution of Sn+4 in the place of Bi+3 leads to the higher Seebeck coefficient and electrical resistivity in the doped samples. Highest power-factor (∼1 mW/m-K2 at 773 K), was obtained for the undoped sample and the 4% Sn doped sample (Bi0.96Sn0.04CuSeO). The lowest thermal conductivity was obtained for the undoped sample, from the room temperature to 773 K. The presence of thermally-conducting SnO2 secondary phases in the doped samples increases the thermal conductivity in comparison with the undoped sample. The zTs of the doped samples were lower compared to the undoped sample, owing to their higher thermal conductivity. The oxygen vacancies as well as the all-length scale phonon scattering, lowers the thermal conductivity of the undoped sample and, as a result, a maximum zT of 1.09 was achieved at 773 K.

Simulations of Cyclic Voltammetry for Electric Double Layers in Asymmetric Electrolytes: A Generalized Modified Poisson-Nernst-Planck Model

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wang, Hainan; Thiele, Alexander; Pilon, Laurent

2013-11-15

This paper presents a generalized modified Poisson–Nernst–Planck (MPNP) model derived from first principles based on excess chemical potential and Langmuir activity coefficient to simulate electric double-layer dynamics in asymmetric electrolytes. The model accounts simultaneously for (1) asymmetric electrolytes with (2) multiple ion species, (3) finite ion sizes, and (4) Stern and diffuse layers along with Ohmic potential drop in the electrode. It was used to simulate cyclic voltammetry (CV) measurements for binary asymmetric electrolytes. The results demonstrated that the current density increased significantly with decreasing ion diameter and/or increasing valency |z i| of either ion species. By contrast, the ionmore » diffusion coefficients affected the CV curves and capacitance only at large scan rates. Dimensional analysis was also performed, and 11 dimensionless numbers were identified to govern the CV measurements of the electric double layer in binary asymmetric electrolytes between two identical planar electrodes of finite thickness. A self-similar behavior was identified for the electric double-layer integral capacitance estimated from CV measurement simulations. Two regimes were identified by comparing the half cycle period τ CV and the “RC time scale” τ RC corresponding to the characteristic time of ions’ electrodiffusion. For τ RC ← τ CV, quasi-equilibrium conditions prevailed and the capacitance was diffusion-independent while for τ RC → τ CV, the capacitance was diffusion-limited. The effect of the electrode was captured by the dimensionless electrode electrical conductivity representing the ratio of characteristic times associated with charge transport in the electrolyte and that in the electrode. The model developed here will be useful for simulating and designing various practical electrochemical, colloidal, and biological systems for a wide range of applications.« less

A systematic study on the effect of electron beam irradiation on structural, electrical, thermo-electric power and magnetic property of LaCoO3

NASA Astrophysics Data System (ADS)

Benedict, Christopher J.; Rao, Ashok; Sanjeev, Ganesh; Okram, G. S.; Babu, P. D.

2016-01-01

In this communication, the effect of electron beam irradiation on the structural, electrical, thermo-electric power and magnetic properties of LaCoO3 cobaltites have been investigated. Rietveld refinement of XRD data reveals that all samples are single phased with rhombohedral structure. Increase in electrical resistivity data is observed with increase in dosage of electron beam irradiation. Analysis of the measured electrical resistivity data indicates that the small polaron hopping model is operative in the high temperature regime for all samples. The Seebeck coefficient (S) of the pristine and the irradiated samples exhibits a crossover from positive to negative values, and a colossal value of Seebeck coefficient (32.65 mV/K) is obtained for pristine sample, however, the value of S decreases with increase in dosage of irradiation. The analysis of Seebeck coefficient data confirms that the small polaron hopping model is operative in the high temperature region. The magnetization results give clear evidence of increase in effective magnetic moment due to increase in dosage of electron beam irradiation.

Convective Heat Transfer Coefficients of Automatic Transmission Fluid Jets with Implications for Electric Machine Thermal Management: Preprint

DOE Office of Scientific and Technical Information (OSTI.GOV)

Bennion, Kevin; Moreno, Gilberto

2015-09-29

Thermal management for electric machines (motors/ generators) is important as the automotive industry continues to transition to more electrically dominant vehicle propulsion systems. Cooling of the electric machine(s) in some electric vehicle traction drive applications is accomplished by impinging automatic transmission fluid (ATF) jets onto the machine's copper windings. In this study, we provide the results of experiments characterizing the thermal performance of ATF jets on surfaces representative of windings, using Ford's Mercon LV ATF. Experiments were carried out at various ATF temperatures and jet velocities to quantify the influence of these parameters on heat transfer coefficients. Fluid temperatures weremore » varied from 50 degrees C to 90 degrees C to encompass potential operating temperatures within an automotive transaxle environment. The jet nozzle velocities were varied from 0.5 to 10 m/s. The experimental ATF heat transfer coefficient results provided in this report are a useful resource for understanding factors that influence the performance of ATF-based cooling systems for electric machines.« less

Electrically Driven Liquid Film Boiling Experiment

NASA Technical Reports Server (NTRS)

Didion, Jeffrey R.

2016-01-01

This presentation presents the science background and ground based results that form the basis of the Electrically Driven Liquid Film Boiling Experiment. This is an ISS experiment that is manifested for 2021. Objective: Characterize the effects of gravity on the interaction of electric and flow fields in the presence of phase change specifically pertaining to: a) The effects of microgravity on the electrically generated two-phase flow. b) The effects of microgravity on electrically driven liquid film boiling (includes extreme heat fluxes). Electro-wetting of the boiling section will repel the bubbles away from the heated surface in microgravity environment. Relevance/Impact: Provides phenomenological foundation for the development of electric field based two-phase thermal management systems leveraging EHD, permitting optimization of heat transfer surface area to volume ratios as well as achievement of high heat transfer coefficients thus resulting in system mass and volume savings. EHD replaces buoyancy or flow driven bubble removal from heated surface. Development Approach: Conduct preliminary experiments in low gravity and ground-based facilities to refine technique and obtain preliminary data for model development. ISS environment required to characterize electro-wetting effect on nucleate boiling and CHF in the absence of gravity. Will operate in the FIR - designed for autonomous operation.

Low-temperature thermoelectric properties of Pb doped Cu2SnSe3

NASA Astrophysics Data System (ADS)

Prasad K, Shyam; Rao, Ashok; Gahtori, Bhasker; Bathula, Sivaiah; Dhar, Ajay; Chang, Chia-Chi; Kuo, Yung-Kang

2017-09-01

A series of Cu2Sn1-xPbxSe3 (0 ≤ x ≤ 0.04) compounds was prepared by solid state synthesis technique. The electrical resistivity (ρ) decreased with increase in Pb content up to x = 0.01, thereafter it increased with further increase in x (till x = 0.03). However, the lowest value of electrical resistivity is observed for Cu2Sn0.96Pb0.04Se3. Analysis of electrical resistivity of all the samples suggests that small poloron hoping model is operative in the high temperature regime while variable range hopping is effective in the low temperature regime. The positive Seebeck coefficient (S) for pristine and doped samples in the entire temperature range indicates that the majority charge carriers are holes. The electronic thermal conductivity (κe) of the Cu2Sn1-xPbxSe3 compounds was estimated by the Wiedemann-Franz law and found that the contribution from κe is less than 1% of the total thermal conductivity (κ). The highest ZT 0.013 was achieved at 400 K for the sample Cu2Sn0.98Pb0.02Se3, about 30% enhancement as compared to the pristine sample.

Influence of electrically induced refraction and absorption on the measurement of spin current by pockels effect in GaAs

DOE Office of Scientific and Technical Information (OSTI.GOV)

Liu, Houquan; She, Weilong, E-mail: shewl@mail.sysu.edu.cn

2015-03-14

The pockels effect could be utilized to measure spin current in semiconductors for linear electro-optic coefficient can be induced by spin current. When dc electric field is applied, the carriers will shift in k space, which could lead to the change of refraction and absorption coefficients. In this paper, we investigate the influence of the induced change of the refraction and absorption coefficients on the measurement of spin current by pockels effect in GaAs.

Use of LANDSAT 8 images for depth and water quality assessment of El Guájaro reservoir, Colombia

NASA Astrophysics Data System (ADS)

González-Márquez, Luis Carlos; Torres-Bejarano, Franklin M.; Torregroza-Espinosa, Ana Carolina; Hansen-Rodríguez, Ivette Renée; Rodríguez-Gallegos, Hugo B.

2018-03-01

The aim of this study was to evaluate the viability of using Landsat 8 spectral images to estimate water quality parameters and depth in El Guájaro Reservoir. On February and March 2015, two samplings were carried out in the reservoir, coinciding with the Landsat 8 images. Turbidity, dissolved oxygen, electrical conductivity, pH and depth were evaluated. Through multiple regression analysis between measured water quality parameters and the reflectance of the pixels corresponding to the sampling stations, statistical models with determination coefficients between 0.6249 and 0.9300 were generated. Results indicate that from a small number of measured parameters we can generate reliable models to estimate the spatial variation of turbidity, dissolved oxygen, pH and depth, as well the temporal variation of electrical conductivity, so models generated from Landsat 8 can be used as a tool to facilitate the environmental, economic and social management of the reservoir.

THz conductivities of indium-tin-oxide nanowhiskers as a graded-refractive-index structure.

PubMed

Yang, Chan-Shan; Chang, Chia-Hua; Lin, Mao-Hsiang; Yu, Peichen; Wada, Osamu; Pan, Ci-Ling

2012-07-02

Indium-tin-oxide (ITO) nanowhiskers with attractive electrical and anti-reflection properties were prepared by the glancing-angle electron-beam evaporation technique. Structural and crystalline properties of such nanostructures were examined by scanning transmission electron microscopy and X-ray diffraction. Their frequency-dependent complex conductivities, refractive indices and absorption coefficients have been characterized with terahertz time-domain spectroscopy (THz-TDS), in which the nanowhiskers were considered as a graded-refractive-index (GRIN) structure instead of the usual thin film model. The electrical properties of ITO GRIN structures are analyzed and fitted well with Drude-Smith model in the 0.2~2.0 THz band. Our results indicate that the ITO nanowhiskers and its bottom layer atop the substrate exhibit longer carrier scattering times than ITO thin films. This signifies that ITO nanowhiskers have an excellent crystallinity with large grain size, consistent with X-ray data. Besides, we show a strong backscattering effect and fully carrier localization in the ITO nanowhiskers.

Recent progress in oxide thermoelectric materials: p-type Ca3Co4O9 and n-type SrTiO3(-).

PubMed

Ohta, Hiromichi; Sugiura, Kenji; Koumoto, Kunihito

2008-10-06

Thermoelectric energy conversion technology to convert waste heat into electricity has received much attention. In addition, metal oxides have recently been considered as thermoelectric power generation materials that can operate at high temperatures on the basis of their potential advantages over heavy metallic alloys in chemical and thermal robustness. We have fabricated high-quality epitaxial films composed of oxide thermoelectric materials that are suitable for clarifying the intrinsic "real" properties. This review focuses on the thermoelectric properties of two representative oxide epitaxial films, p-type Ca 3Co 4O 9 and n-type SrTiO 3, which exhibit the best thermoelectric figures of merit, ZT (= S (2)sigma Tkappa (-1), S = Seebeck coefficient, sigma = electrical conductivity, kappa = thermal conductivity, and T = absolute temperature) among oxide thermoelectric materials reported to date. In addition, we introduce the recently discovered giant S of two-dimensional electrons confined within a unit cell layer thickness ( approximately 0.4 nm) of SrTiO 3.

Thickness dependent structural, optical and electrical properties of Se85In12Bi3 nanochalcogenide thin films

NASA Astrophysics Data System (ADS)

Tripathi, Ravi P.; Zulfequar, M.; Khan, Shamshad A.

2018-04-01

Our aim is to study the thickness dependent effects on structure, electrical and optical properties of Se85In12Bi3 nanochalcogenide thin films. Bulk alloy of Se85In12Bi3 was synthesized by melt-quenching technique. The amorphous as well as glassy nature of Se85In12Bi3 chalcogenide was confirmed by non-isothermal Differential Scanning Calorimetry (DSC) measurements. The nanochalcogenide thin films of thickness 30, 60 and 90 nm were prepared on glass/Si wafer substrate using Physical Vapour Condensation Technique (PVCT). From XRD studies it was found that thin films have amorphous texture. The surface morphology and particle size of films were studied by Field Emission Scanning Electron Microscope (FESEM). From optical studies, different optical parameters were estimated for Se85In12Bi3 thin films at different thickness. It was found that the absorption coefficient (α) and extinction coefficient (k) increases with photon energy and decreases with film thickness. The optical absorption process followed the rule of indirect transitions and optical band gap were found to be increase with film thickness. The value of Urbach energy (Et) and steepness parameter (σ) were also calculated for different film thickness. For electrical studies, dc-conductivity measurement was done at different temperature and activation energy (ΔEc) were determined and found to be increase with film thickness.

In-situ analysis of microwave conductivity and impedance spectroscopy for evaluation of charge carrier dynamics at interfaces

NASA Astrophysics Data System (ADS)

Choi, Wookjin; Inoue, Junichi; Tsutsui, Yusuke; Sakurai, Tsuneaki; Seki, Shu

2017-11-01

A unique concerted analysis comprising non-contact microwave conductivity measurements and impedance spectroscopy was developed to simultaneously assess the charge carrier mobility and injection barriers. The frequency dependence of the microwave conductivity as well as the electrical current was analyzed by applying sinusoidal voltage to determine the equivalent circuit parameters. Based on the temperature dependence of the circuit parameters, the energy of the injection barrier was estimated to be 0.4 eV with the Richardson-Schottky model, and the band-like transport was confirmed with the negative temperature coefficient with the β value of 1.4 in the intra-layer conduction of C8-BTBT. In contrast, the increase in the resistance of the C8-BTBT layer with decreasing temperature implied the occurrence of hopping-like transport in the inter-layer conduction of C8-BTBT.

Electronic and thermoelectric analysis of phases in the In 2O 3(ZnO) k system

DOE PAGES

Hopper, E. Mitchell; Zhu, Qimin; Song, Jung-Hwan; ...

2011-01-01

The high-temperature electrical conductivity and thermopower of several compounds in the In 2O 3(ZnO) k system (k = 3, 5, 7, and 9) were measured, and the band structures of the k = 1, 2, and 3 structures were predicted based on first-principles calculations. These phases exhibit highly dispersed conduction bands consistent with transparent conducting oxide behavior. Jonker plots (Seebeck coefficient vs. natural logarithm of conductivity) were used to obtain the product of the density of states and mobility for these phases, which were related to the maximum achievable power factor (thermopower squared times conductivity) for each phase by Ioffemore » analysis (maximum power factor vs. Jonker plot intercept). With the exception of the k = 9 phase, all other phases were found to have maximum predicted power factors comparable to other thermoelectric oxides if suitably doped.« less

ThE SYnthesis of R z Fe4- x Co x Sb12 (R: Yb, La, Ce) skutterudites and their thermoelectric properties

NASA Astrophysics Data System (ADS)

Park, Kwan-Ho; Lee, Soonil; Seo, Won-Seon; Shin, Dong-Kil; Kim, Il-Ho

2014-03-01

Rare-earth-filled skutterudites R z Fe4- x Co x Sb12 (R: Yb, La, Ce) were prepared, and their transport and thermoelectric properties were examined. All specimens showed p-type conduction and exhibited a degenerate semiconductor behavior. R0.9Fe3CoSb12 had lower electrical conductivities and higher Seebeck coefficients than RFe4Sb12, which meant that Co led to charge compensation through electron donations. All specimens had positive Hall coefficients, and their carrier concentrations were decreased by charge compensation with increasing Co substitution. The thermal conductivities of R0.9Fe3CoSb12 were lower than those of RFe4Sb12 due to the decreased carrier concentration, as well as the lattice scattering induced by the substitution of Co for Fe. Yb-filled and La-filled skutterudites showed enhanced thermoelectric figures of merit through charge compensation with Co, but Ce-filled skutterudites did not. Yb2˜3+ and La3+ ions required charge compensation to stabilize their skutterudite phases, but Ce3˜4+ ions did not.

Effects of Mev Si Ions and Thermal Annealing on Thermoelectric and Optical Properties of SiO2/SiO2+Ge Multi-nanolayer thin Films

NASA Astrophysics Data System (ADS)

Budak, S.; Alim, M. A.; Bhattacharjee, S.; Muntele, C.

Thermoelectric generator devices have been prepared from 200 alternating layers of SiO2/SiO2+Ge superlattice films using DC/RF magnetron sputtering. The 5 MeV Si ionsbombardmenthasbeen performed using the AAMU Pelletron ion beam accelerator to formquantum dots and / or quantum clusters in the multi-layer superlattice thin films to decrease the cross-plane thermal conductivity, increase the cross-plane Seebeck coefficient and increase the cross-plane electrical conductivity to increase the figure of merit, ZT. The fabricated devices have been annealed at the different temperatures to tailor the thermoelectric and optical properties of the superlattice thin film systems. While the temperature increased, the Seebeck coefficient continued to increase and reached the maximum value of -25 μV/K at the fluenceof 5x1013 ions/cm2. The decrease in resistivity has been seen between the fluence of 1x1013 ions/cm2 and 5x1013 ions/cm2. Transport properties like Hall coefficient, density and mobility did not change at all fluences. Impedance spectroscopy has been used to characterize the multi-junction thermoelectric devices. The loci obtained in the C*-plane for these data indicate non-Debye type relaxation displaying the presence of the depression parameter.

Structurally-driven Enhancement of Thermoelectric Properties within Poly(3,4-ethylenedioxythiophene) thin Films

PubMed Central

Petsagkourakis, Ioannis; Pavlopoulou, Eleni; Portale, Giuseppe; Kuropatwa, Bryan A.; Dilhaire, Stefan; Fleury, Guillaume; Hadziioannou, Georges

2016-01-01

Due to the rising need for clean energy, thermoelectricity has raised as a potential alternative to reduce dependence on fossil fuels. Specifically, thermoelectric devices based on polymers could offer an efficient path for near-room temperature energy harvesters. Thus, control over thermoelectric properties of conducting polymers is crucial and, herein, the structural, electrical and thermoelectric properties of poly(3,4-ethylenedioxythiophene) (PEDOT) thin films doped with p-toluenesulfonate (Tos) molecules were investigated with regards to thin film processing. PEDOT:Tos thin films were prepared by in-situ polymerization of (3,4-ethylenedioxythiophene) monomers in presence of iron(III) p-toluenesulfonate with different co-solvents in order to tune the film structure. While the Seebeck coefficient remained constant, a large improvement in the electrical conductivity was observed for thin films processed with high boiling point additives. The increase of electrical conductivity was found to be solely in-plane mobility-driven. Probing the thin film structure by Grazing Incidence Wide Angle X-ray Scattering has shown that this behavior is dictated by the structural properties of the PEDOT:Tos films; specifically by the thin film crystallinity combined to the preferential edge-on orientation of the PEDOT crystallites. Consequentially enhancement of the power factor from 25 to 78.5 μW/mK2 has been readily obtained for PEDOT:Tos thin films following this methodology. PMID:27470637

Structurally-driven Enhancement of Thermoelectric Properties within Poly(3,4-ethylenedioxythiophene) thin Films.

PubMed

Petsagkourakis, Ioannis; Pavlopoulou, Eleni; Portale, Giuseppe; Kuropatwa, Bryan A; Dilhaire, Stefan; Fleury, Guillaume; Hadziioannou, Georges

2016-07-29

Due to the rising need for clean energy, thermoelectricity has raised as a potential alternative to reduce dependence on fossil fuels. Specifically, thermoelectric devices based on polymers could offer an efficient path for near-room temperature energy harvesters. Thus, control over thermoelectric properties of conducting polymers is crucial and, herein, the structural, electrical and thermoelectric properties of poly(3,4-ethylenedioxythiophene) (PEDOT) thin films doped with p-toluenesulfonate (Tos) molecules were investigated with regards to thin film processing. Tos thin films were prepared by in-situ polymerization of (3,4-ethylenedioxythiophene) monomers in presence of iron(III) p-toluenesulfonate with different co-solvents in order to tune the film structure. While the Seebeck coefficient remained constant, a large improvement in the electrical conductivity was observed for thin films processed with high boiling point additives. The increase of electrical conductivity was found to be solely in-plane mobility-driven. Probing the thin film structure by Grazing Incidence Wide Angle X-ray Scattering has shown that this behavior is dictated by the structural properties of the Tos films; specifically by the thin film crystallinity combined to the preferential edge-on orientation of the PEDOT crystallites. Consequentially enhancement of the power factor from 25 to 78.5 μW/mK(2) has been readily obtained for Tos thin films following this methodology.

Electron transport in electrically biased inverse parabolic double-barrier structure

NASA Astrophysics Data System (ADS)

M, Bati; S, Sakiroglu; I, Sokmen

2016-05-01

A theoretical study of resonant tunneling is carried out for an inverse parabolic double-barrier structure subjected to an external electric field. Tunneling transmission coefficient and density of states are analyzed by using the non-equilibrium Green’s function approach based on the finite difference method. It is found that the resonant peak of the transmission coefficient, being unity for a symmetrical case, reduces under the applied electric field and depends strongly on the variation of the structure parameters.

High Thermoelectric Performance of In4Se3-Based Materials and the Influencing Factors.

PubMed

Yin, Xin; Liu, Jing-Yuan; Chen, Ling; Wu, Li-Ming

2018-02-20

Materials that can directly convert electricity into heat, i.e., thermoelectric materials, have attracted renewed attention globally for sustainable energy applications. As one of the state-of-the-art thermoelectric materials, In 4 Se 3 features an interesting crystal structure of quasi-two-dimensional sheets comprising In/Se chains that provide a platform to achieve a Peierls distortion and support a charge density wave instability. Single-crystal In 4 Se 3-δ (δ = 0.65) shows strong anisotropy in its thermoelectric properties with a very high ZT of 1.48 at 705 K in the b-c plane (one of the highest values for an n-type thermoelectric material to date) but a much lower ZT of approximately 0.5 in the a-b plane. Because of the random dispersion of grains and the grain boundary effect, the electrical transport properties of polycrystalline In 4 Se 3 are poor, which is the main impediment to improve their performance. The In4-site in the In 4 Se 3 unit cell is substitutional for dopants such as Pb, which increases the carrier concentration by 2 orders of magnitude and the electrical conductivity to 143 S/cm. Furthermore, the electrical conductivity markedly increases to approximately 160 S/cm when Cu is doped into the interstitial site but remains as low as 30 S/cm with In1/In2/In3-site dopants, e.g., Ni, Zn, Ga, and Sn. In particular, the In4-site dopant ytterbium introduces a pinning level that highly localizes the charge carriers; thus, the electrical conductivity is maintained within an order of magnitude of 30 S/cm. Meanwhile, ytterbium also creates resonance states around the Fermi level that increase the Seebeck coefficient to -350 μV/K, the highest value at the ZT peak. However, the maximum solubility of the dopant may be limited by the Se-vacancy concentration. In addition, a Se vacancy also destroys the regular lattice vibrations and weakens phonon transport. Finally, nanoinclusions can effectively scatter the middle wavelength phonons, resulting in a decrease in the lattice thermal conductivity. Because of the multiple-dopant strategy, polycrystalline materials are competitive with single crystals regarding ZT values; for instance, Pb/Sn-co-doped In 4 Pb 0.01 Sn 0.04 Se 3 has ZT = 1.4 at 733 K, whereas In 4 Se 2.95 (CuI) 0.01 has ZT = 1.34 at 723 K. These properties illustrate the promise of polycrystalline In 4 Se 3 -based materials for various applications. Finally, the ZT values of all single crystalline and polycrystalline In 4 Se 3 materials have been summarized as a function of the doping strategy applied at the different lattice sites. Additionally, the correlations between the electrical conductivity and the Seebeck coefficient of all the polycrystalline materials are presented. These insights may provide new ideas in the search for and selection of new thermoelectric compounds in the In/Se and related In/Te, Sn/Se, and Sn/Te systems.

Study of light-absorbing crystal birefringence and electrical modulation mechanisms for coupled thermal-optical effects.

PubMed

Zhou, Ji; He, Zhihong; Ma, Yu; Dong, Shikui

2014-09-20

This paper discusses Gaussian laser transmission in double-refraction crystal whose incident light wavelength is within its absorption wave band. Two scenarios for coupled radiation and heat conduction are considered: one is provided with an applied external electric field, the other is not. A circular heat source with a Gaussian energy distribution is introduced to present the crystal's light-absorption process. The electromagnetic field frequency domain analysis equation and energy equation are solved to simulate the phenomenon by using the finite element method. It focuses on the influence of different values such as wavelength, incident light intensity, heat transfer coefficient, ambient temperature, crystal thickness, and applied electric field strength. The results show that the refraction index of polarized light increases with the increase of crystal temperature. It decreases as the strength of the applied electric field increases if it is positive. The mechanism of electrical modulation for the thermo-optical effect is used to keep the polarized light's index of refraction constant in our simulation. The quantitative relation between thermal boundary condition and strength of applied electric field during electrical modulation is determined. Numerical results indicate a possible approach to removing adverse thermal effects such as depolarization and wavefront distortion, which are caused by thermal deposition during linear laser absorption.

Thermoelectric Properties of Highly-Crystallized Ge-Te-Se Glasses Doped with Cu/Bi.

PubMed

Srinivasan, Bhuvanesh; Boussard-Pledel, Catherine; Dorcet, Vincent; Samanta, Manisha; Biswas, Kanishka; Lefèvre, Robin; Gascoin, Franck; Cheviré, François; Tricot, Sylvain; Reece, Michael; Bureau, Bruno

2017-03-23

Chalcogenide semiconducting systems are of growing interest for mid-temperature range (~500 K) thermoelectric applications. In this work, Ge 20 Te 77 Se₃ glasses were intentionally crystallized by doping with Cu and Bi. These effectively-crystallized materials of composition (Ge 20 Te 77 Se₃) 100- x M x (M = Cu or Bi; x = 5, 10, 15), obtained by vacuum-melting and quenching techniques, were found to have multiple crystalline phases and exhibit increased electrical conductivity due to excess hole concentration. These materials also have ultra-low thermal conductivity, especially the heavily-doped (Ge 20 Te 77 Se₃) 100- x Bi x ( x = 10, 15) samples, which possess lattice thermal conductivity of ~0.7 Wm -1 K -1 at 525 K due to the assumable formation of nano-precipitates rich in Bi, which are effective phonon scatterers. Owing to their high metallic behavior, Cu-doped samples did not manifest as low thermal conductivity as Bi-doped samples. The exceptionally low thermal conductivity of the Bi-doped materials did not, alone, significantly enhance the thermoelectric figure of merit, zT. The attempt to improve the thermoelectric properties by crystallizing the chalcogenide glass compositions by excess doping did not yield power factors comparable with the state of the art thermoelectric materials, as these highly electrically conductive crystallized materials could not retain the characteristic high Seebeck coefficient values of semiconducting telluride glasses.

Thermoelectric Properties of Highly-Crystallized Ge-Te-Se Glasses Doped with Cu/Bi

PubMed Central

Srinivasan, Bhuvanesh; Boussard-Pledel, Catherine; Dorcet, Vincent; Samanta, Manisha; Biswas, Kanishka; Lefèvre, Robin; Gascoin, Franck; Cheviré, François; Tricot, Sylvain; Reece, Michael; Bureau, Bruno

2017-01-01

Chalcogenide semiconducting systems are of growing interest for mid-temperature range (~500 K) thermoelectric applications. In this work, Ge20Te77Se3 glasses were intentionally crystallized by doping with Cu and Bi. These effectively-crystallized materials of composition (Ge20Te77Se3)100−xMx (M = Cu or Bi; x = 5, 10, 15), obtained by vacuum-melting and quenching techniques, were found to have multiple crystalline phases and exhibit increased electrical conductivity due to excess hole concentration. These materials also have ultra-low thermal conductivity, especially the heavily-doped (Ge20Te77Se3)100−xBix (x = 10, 15) samples, which possess lattice thermal conductivity of ~0.7 Wm−1 K−1 at 525 K due to the assumable formation of nano-precipitates rich in Bi, which are effective phonon scatterers. Owing to their high metallic behavior, Cu-doped samples did not manifest as low thermal conductivity as Bi-doped samples. The exceptionally low thermal conductivity of the Bi-doped materials did not, alone, significantly enhance the thermoelectric figure of merit, zT. The attempt to improve the thermoelectric properties by crystallizing the chalcogenide glass compositions by excess doping did not yield power factors comparable with the state of the art thermoelectric materials, as these highly electrically conductive crystallized materials could not retain the characteristic high Seebeck coefficient values of semiconducting telluride glasses. PMID:28772687

Estimates of genetics and phenotypics parameters for the yield and quality of soybean seeds.

PubMed

Zambiazzi, E V; Bruzi, A T; Guilherme, S R; Pereira, D R; Lima, J G; Zuffo, A M; Ribeiro, F O; Mendes, A E S; Godinho, S H M; Carvalho, M L M

2017-09-27

Estimating genotype x environment (GxE) parameters for quality and yield in soybean seed grown in different environments in Minas Gerais State was the goal of this study, as well as to evaluate interaction effects of GxE for soybean seeds yield and quality. Seeds were produced in three locations in Minas Gerais State (Lavras, Inconfidentes, and Patos de Minas) in 2013/14 and 2014/15 seasons. Field experiments were conducted in randomized blocks in a factorial 17 x 6 (GxE), and three replications. Seed yield and quality were evaluated for germination in substrates paper and sand, seedling emergence, speed emergency index, mechanical damage by sodium hypochlorite, electrical conductivity, speed aging, vigor and viability of seeds by tetrazolium test in laboratory using completely randomized design. Quadratic component genotypic, GXE variance component, genotype determination coefficient, genetic variation coefficient and environmental variation coefficient were estimated using the Genes software. Percentage analysis of genotypes contribution, environments and genotype x environment interaction were conducted by sites combination two by two and three sites combination, using the R software. Considering genotypes selection of broad adaptation, TMG 1179 RR, CD 2737 RR, and CD 237 RR associated better yield performance at high physical and physiological potential of seed. Environmental effect was more expressive for most of the characters related to soybean seed quality. GxE interaction effects were expressive though genotypes did not present coincidental behavior in different environments.

Effects of interdot hopping and Coulomb blockade on the thermoelectric properties of serially coupled quantum dots

PubMed Central

2012-01-01

We have theoretically studied the thermoelectric properties of serially coupled quantum dots (SCQDs) embedded in an insulator connected to metallic electrodes. In the framework of Keldysh Green’s function technique, the Landauer formula of transmission factor is obtained using the equation of motion method. Based on such analytical expressions of charge and heat currents, we calculate the electrical conductance, Seebeck coefficient, electron thermal conductance, and figure of merit (ZT) of SCQDs in the linear response regime. The effects of interdot hopping and electron Coulomb interactions on ZT are analyzed. We demonstrate that ZT is not a monotonic increasing function of interdot electron hopping strength (tc). We also show that in the absence of phonon thermal conductance, SCQD can reach the Carnot efficiency as tcapproaches zero. PMID:22591807

Temperature dependent thermoelectric property of reduced graphene oxide-polyaniline composite

DOE Office of Scientific and Technical Information (OSTI.GOV)

Mitra, Mousumi, E-mail: mousumimitrabesu@gmail.com; Banerjee, Dipali, E-mail: dipalibanerjeebesu@gmail.com; Kargupta, Kajari, E-mail: karguptakajari2010@gmail.com

2016-05-06

A composite material of reduced graphene oxide (rG) nanosheets with polyaniline (PANI) protonated by 5-sulfosalicylic acid has been synthesized via in situ oxidative polymerization method. The morphological and spectral characterizations have been done using FESEM and XRD measurements. The thermoelectric (TE) properties of the reduced graphene oxide-polyaniline composite (rG-P) has been studied in the temperature range from 300-400 K. The electrical conductivity and the Seebeck coefficient of rG-P is higher than the of pure PANI, while the thermal conductivity of the composite still keeps much low value ensuing an increase in the dimensionless figure of merit (ZT) in the wholemore » temperature range.« less

Thermoelectric properties of p-type sb-doped Cu2SnSe3 near room and mid temperature applications

NASA Astrophysics Data System (ADS)

Prasad, K. Shyam; Rao, Ashok; Chauhan, Nagendra S.; Bhardwaj, Ruchi; Vishwakarma, Avinash; Tyagi, Kriti

2018-02-01

In this study, we report low and mid temperature range thermoelectric properties of Sb-substituted Cu2SnSe3 compounds. The Cu2Sn1- x Sb x Se3 (0 ≤ x ≤ 0.04) alloys were prepared using conventional solid-state reaction followed by spark plasma sintering. The crystal structure was characterized using XRD and it reveals that all the samples exhibit cubic structure with space group -4/3m. The electrical transport characteristics indicate degenerate semiconducting behavior. Electrical resistivity was found to follow small polaron hopping (SPH) model in the entire temperature range of investigation. The Seebeck coefficient data reveals that the majority of charge carriers are holes and the analysis of Seebeck coefficient data gives negative values of Fermi energy indicating that the Fermi energy is below the edge of valence band. The electronic contribution ( κ e) for total thermal conductivity is found to be less than 1%. The maximum ZT value of 0.64 is observed for the sample with x = 0.03 (at 700 K) which is approximately 2.3 times that of the pristine sample.

Influence of substrate temperature on structural, morphological, optical and electrical properties of Bi-doped MnInS4 thin films prepared by nebuliser spray pyrolysis technique

NASA Astrophysics Data System (ADS)

Kennedy, A.; Senthil Kumar, V.; Pradeev Raj, K.

2017-11-01

Bismuth (Bi)-doped manganese indium sulphide (MnInS4) thin films were deposited on heated glass substrates using an aqueous solution of MnCl2, InCl3, (NH2)2CS and BiCl3 by the common nebuliser spray pyrolysis technique. The thin films were grown at various substrate temperatures ranging from 250 to 400 °C with a constant spray time (5 min). The present work aims to study the effect of substrate temperature on the structural, optical, photoluminescence and electrical properties of the grown thin films using various techniques like X-ray diffraction (XRD), field emission scanning electron microscopy (FE-SEM), energy dispersive spectrum (EDS), UV-Vis absorption spectroscopy, photoluminescence spectra (PL) and four probe methods. The XRD pattern reveals that the Bi-doped MnInS4 thin films were polycrystalline in nature with a cubic spinel structure whose particle size varies between 8.2 and 23.5 nm. From the FE-SEM micrographs, due to the change in the substrate temperature, shapes such as spherical, needle-shaped and T-shaped grains were observed throughout the surface of the films. The energy dispersive analysis spectrum (EDS) shows the presence of Mn, In, S and Bi in the film grown at 250 °C. It is interesting to note that the structural homogeneity and crystallinity of the film is improved due to the decrease in the absorption coefficient (α) and extinction coefficient (K) with an increase in substrate temperature. Also, with an increase in the substrate temperature, the calculated band gap energy was found to decrease from 1.87 to 1.59 eV. From the PL spectra, several intense peaks corresponding to blue, green, yellow, orange and red band emissions were observed in the wavelength region of 350-650 nm. Moreover as the intensity of the peak increases with increase in the substrate temperature, the crystallinity of the material of the film greatly improves concomitant with minimum strain and defect states. From the electrical studies, the electrical conductivity increases with increase in substrate temperature and a maximum electrical conductivity of 3.73 × 10-3 Ω-1m-1 were obtained for the film prepared at 400 °C. The thickness of the films was also measured and the values ranged between 743 nm (250 °C) to 629 nm (400 °C). The high absorption coefficient (1.85 × 104 cm-1) and high transmittance of the films make them an efficient window layer for solar cell applications. Incorporation of Bismuth (Bi) into MnInS4 matrix leads to improve the optical transmittance (85%) and electrical conductivity (3.11 × 10-3 Ω-1 m-1) of the film grown at 400 °C. Other important parameters like dislocation density (δ), strain (ε), the number of crystallites per unit area (N) and lattice distortion (LD), which are commonly used to describe the structural analysis were also presented. Bi-doped MnInS4 thin films were grown by a variety of deposition methods. Among them, spray pyrolysis is an eco-friendly method because of its low cost, mass production capacity, large area coatings and minimum wastage of the source materials.

A setup for measuring the Seebeck coefficient and the electrical resistivity of bulk thermoelectric materials

NASA Astrophysics Data System (ADS)

Fu, Qiang; Xiong, Yucheng; Zhang, Wenhua; Xu, Dongyan

2017-09-01

This paper presents a setup for measuring the Seebeck coefficient and the electrical resistivity of bulk thermoelectric materials. The sample holder was designed to have a compact structure and can be directly mounted in a standard cryostat system for temperature-dependent measurements. For the Seebeck coefficient measurement, a thin bar-shaped sample is mounted bridging two copper bases; and two ceramic heaters are used to generate a temperature gradient along the sample. Two type T thermocouples are used to determine both temperature and voltage differences between two widely separated points on the sample. The thermocouple junction is flattened into a disk and pressed onto the sample surface by using a spring load. The flexible fixation method we adopted not only simplifies the sample mounting process but also prevents thermal contact deterioration due to the mismatch of thermal expansion coefficients between the sample and other parts. With certain modifications, the sample holder can also be used for four-probe electrical resistivity measurements. High temperature measurements are essential for thermoelectric power generation. The experimental system we developed is capable of measuring the Seebeck coefficient and the electrical resistivity of bulk thermoelectric materials in a wide temperature range from 80 to 500 K, which can be further extended to even higher temperatures. Measurements on two standard materials, constantan and nickel, confirmed the accuracy and the reliability of the system.

The calibration of a model for simulating the thermal and electrical performance of a 2.8 kW AC solid-oxide fuel cell micro-cogeneration device

NASA Astrophysics Data System (ADS)

Beausoleil-Morrison, Ian; Lombardi, Kathleen

The concurrent production of heat and electricity within residential buildings using solid-oxide fuel cell (SOFC) micro-cogeneration devices has the potential to reduce primary energy consumption, greenhouse gas emissions, and air pollutants. A realistic assessment of this emerging technology requires the accurate simulation of the thermal and electrical production of SOFC micro-cogeneration devices concurrent with the simulation of the building, its occupants, and coupled plant components. The calibration of such a model using empirical data gathered from experiments conducted with a 2.8 kW AC SOFC micro-cogeneration device is demonstrated. The experimental configuration, types of instrumentation employed, and the operating scenarios examined are treated. The propagation of measurement uncertainty into the derived quantities that are necessary for model calibration are demonstrated by focusing upon the SOFC micro-cogeneration system's gas-to-water heat exchanger. The calibration coefficients necessary to accurately simulate the thermal and electrical performance of this prototype device are presented and the types of analyses enabled to study the potential of the technology are demonstrated.

Silicon nanowire arrays as thermoelectric material for a power microgenerator

NASA Astrophysics Data System (ADS)

Dávila, D.; Tarancón, A.; Fernández-Regúlez, M.; Calaza, C.; Salleras, M.; San Paulo, A.; Fonseca, L.

2011-10-01

A novel design of a silicon-based thermoelectric power microgenerator is presented in this work. Arrays of silicon nanowires, working as thermoelectric material, have been integrated in planar uni-leg thermocouple microstructures to convert waste heat into electrical energy. Homogeneous, uniformly dense, well-oriented and size-controlled arrays of silicon nanowires have been grown by chemical vapor deposition using the vapor-liquid-solid mechanism. Compatibility issues between the nanowire growth method and microfabrication techniques, such as electrical contact patterning, are discussed. Electrical measurements of the nanowire array electrical conductivity and the Seebeck voltage induced by a controlled thermal gradient or under harvesting operation mode have been carried out to demonstrate the feasibility of the microdevice. A resistance of 240 Ω at room temperature was measured for an array of silicon nanowires 10 µm -long, generating a Seebeck voltage of 80 mV under an imposed thermal gradient of 450 °C, whereas only 4.5 mV were generated under a harvesting operation mode. From the results presented, a Seebeck coefficient of about 150-190 µV K-1 was estimated, which corresponds to typical values for bulk silicon.

Analytic expressions for ULF wave radiation belt radial diffusion coefficients

PubMed Central

Ozeke, Louis G; Mann, Ian R; Murphy, Kyle R; Jonathan Rae, I; Milling, David K

2014-01-01

We present analytic expressions for ULF wave-derived radiation belt radial diffusion coefficients, as a function of L and Kp, which can easily be incorporated into global radiation belt transport models. The diffusion coefficients are derived from statistical representations of ULF wave power, electric field power mapped from ground magnetometer data, and compressional magnetic field power from in situ measurements. We show that the overall electric and magnetic diffusion coefficients are to a good approximation both independent of energy. We present example 1-D radial diffusion results from simulations driven by CRRES-observed time-dependent energy spectra at the outer boundary, under the action of radial diffusion driven by the new ULF wave radial diffusion coefficients and with empirical chorus wave loss terms (as a function of energy, Kp and L). There is excellent agreement between the differential flux produced by the 1-D, Kp-driven, radial diffusion model and CRRES observations of differential electron flux at 0.976 MeV—even though the model does not include the effects of local internal acceleration sources. Our results highlight not only the importance of correct specification of radial diffusion coefficients for developing accurate models but also show significant promise for belt specification based on relatively simple models driven by solar wind parameters such as solar wind speed or geomagnetic indices such as Kp. Key Points Analytic expressions for the radial diffusion coefficients are presented The coefficients do not dependent on energy or wave m value The electric field diffusion coefficient dominates over the magnetic PMID:26167440

Diameter-Controlled and Surface-Modified Sb2Se3 Nanowires and Their Photodetector Performance

NASA Astrophysics Data System (ADS)

Choi, Donghyeuk; Jang, Yamujin; Lee, Jeehee; Jeong, Gyoung Hwa; Whang, Dongmok; Hwang, Sung Woo; Cho, Kyung-Sang; Kim, Sang-Wook

2014-10-01

Due to its direct and narrow band gap, high chemical stability, and high Seebeck coefficient (1800 μVK-1), antimony selenide (Sb2Se3) has many potential applications, such as in photovoltaic devices, thermoelectric devices, and solar cells. However, research on the Sb2Se3 materials has been limited by its low electrical conductivity in bulk state. To overcome this challenge, we suggest two kinds of nano-structured materials, namely, the diameter-controlled Sb2Se3 nanowires and Ag2Se-decorated Sb2Se3 nanowires. The photocurrent response of diameter-controlled Sb2Se3, which depends on electrical conductivity of the material, increases non-linearly with the diameter of the nanowire. The photosensitivity factor (K = Ilight/Idark) of the intrinsic Sb2Se3 nanowire with diameter of 80-100 nm is highly improved (K = 75). Additionally, the measurement was conducted using a single nanowire under low source-drain voltage. The dark- and photocurrent of the Ag2Se-decorated Sb2Se3 nanowire further increased, as compared to that of the intrinsic Sb2Se3 nanowire, to approximately 50 and 7 times, respectively.

Dramatic Changes in Thermoelectric Power of Germanium under Pressure: Printing n–p Junctions by Applied Stress

PubMed Central

Korobeinikov, Igor V.; Morozova, Natalia V.; Shchennikov, Vladimir V.; Ovsyannikov, Sergey V.

2017-01-01

Controlled tuning the electrical, optical, magnetic, mechanical and other characteristics of the leading semiconducting materials is one of the primary technological challenges. Here, we demonstrate that the electronic transport properties of conventional single-crystalline wafers of germanium may be dramatically tuned by application of moderate pressures. We investigated the thermoelectric power (Seebeck coefficient) of p– and n–type germanium under high pressure to 20 GPa. We established that an applied pressure of several GPa drastically shifts the electrical conduction to p–type. The p–type conduction is conserved across the semiconductor-metal phase transition at near 10 GPa. Upon pressure releasing, germanium transformed to a metastable st12 phase (Ge-III) with n–type semiconducting conductivity. We proposed that the unusual electronic properties of germanium in the original cubic-diamond-structured phase could result from a splitting of the “heavy” and “light” holes bands, and a related charge transfer between them. We suggested new innovative applications of germanium, e.g., in technologies of printing of n–p and n–p–n junctions by applied stress. Thus, our work has uncovered a new face of germanium as a ‘smart’ material. PMID:28290495

Diameter-controlled and surface-modified Sb₂Se₃ nanowires and their photodetector performance.

PubMed

Choi, Donghyeuk; Jang, Yamujin; Lee, JeeHee; Jeong, Gyoung Hwa; Whang, Dongmok; Hwang, Sung Woo; Cho, Kyung-Sang; Kim, Sang-Wook

2014-10-22

Due to its direct and narrow band gap, high chemical stability, and high Seebeck coefficient (1800 μVK(-1)), antimony selenide (Sb2Se3) has many potential applications, such as in photovoltaic devices, thermoelectric devices, and solar cells. However, research on the Sb2Se3 materials has been limited by its low electrical conductivity in bulk state. To overcome this challenge, we suggest two kinds of nano-structured materials, namely, the diameter-controlled Sb2Se3 nanowires and Ag2Se-decorated Sb2Se3 nanowires. The photocurrent response of diameter-controlled Sb2Se3, which depends on electrical conductivity of the material, increases non-linearly with the diameter of the nanowire. The photosensitivity factor (K = I(light)/I(dark)) of the intrinsic Sb2Se3 nanowire with diameter of 80-100 nm is highly improved (K = 75). Additionally, the measurement was conducted using a single nanowire under low source-drain voltage. The dark- and photocurrent of the Ag2Se-decorated Sb2Se3 nanowire further increased, as compared to that of the intrinsic Sb2Se3 nanowire, to approximately 50 and 7 times, respectively.

Seebeck Effects in N-Type and P-Type Polymers Driven Simultaneously by Surface Polarization and Entropy Differences Based on Conductor/Polymer/Conductor Thin-Film Devices

DOE PAGES

Hu, Dehua; Liu, Qing; Tisdale, Jeremy; ...

2015-04-15

This paper reports Seebeck effects driven by both surface polarization difference and entropy difference by using intramolecular charge-transfer states in n-type and p-type conjugated polymers, namely IIDT and IIDDT, based on vertical conductor/polymer/conductor thin-film devices. Large Seebeck coefficients of -898 V/K and 1300 V/K from are observed from n-type IIDT p-type IIDDT, respectively, when the charge-transfer states are generated by a white light illumination of 100 mW/cm2. Simultaneously, electrical conductivities are increased from almost insulating states in dark condition to conducting states under photoexcitation in both n-type IIDT and p-type IIDDT devices. We find that the intramolecular charge-transfer states canmore » largely enhance Seebeck effects in the n-type IIDT and p-type IIDDT devices driven by both surface polarization difference and entropy difference. Furthermore, the Seebeck effects can be shifted between polarization and entropy regimes when electrical conductivities are changed. This reveals a new concept to develop Seebeck effects by controlling polarization and entropy regimes based on charge-transfer states in vertical conductor/polymer/conductor thin-film devices.« less

Enhancement of Thermoelectric Properties of PEDOT:PSS and Tellurium-PEDOT:PSS Hybrid Composites by Simple Chemical Treatment.

PubMed

Bae, Eun Jin; Kang, Young Hun; Jang, Kwang-Suk; Cho, Song Yun

2016-01-05

The thermoelectric properties of poly(3,4-ethylenedioxythiophene):poly(styrenesulfonate) ( PSS) and tellurium- PSS (Te- PSS) hybrid composites were enhanced via simple chemical treatment. The performance of thermoelectric materials is determined by their electrical conductivity, thermal conductivity, and Seebeck coefficient. Significant enhancement of the electrical conductivity of PSS and Te- PSS hybrid composites from 787.99 and 11.01 to 4839.92 and 334.68 S cm(-1), respectively was achieved by simple chemical treatment with H2SO4. The power factor of the developed materials could be effectively tuned over a very wide range depending on the concentration of the H2SO4 solution used in the chemical treatment. The power factors of the developed thermoelectric materials were optimized to 51.85 and 284 μW m(-1) K(-2), respectively, which represent an increase of four orders of magnitude relative to the corresponding parameters of the untreated thermoelectric materials. Using the Te- PSS hybrid composites, a flexible thermoelectric generator that could be embedded in textiles was fabricated by a printing process. This thermoelectric array generates a thermoelectric voltage of 2 mV using human body heat.

Electrical and thermoelectric transport properties of two-dimensional fermionic systems with k-cubic spin-orbit coupling.

PubMed

Mawrie, Alestin; Verma, Sonu; Ghosh, Tarun Kanti

2017-09-01

We investigate effect of <i>k</i>-cubic spin-orbit interaction on electrical and thermoelectric transport properties of two-dimensional fermionic systems. We obtain exact analytical expressions of the inverse relaxation time (IRT) and the Drude conductivity for long-range Coulomb and short-range delta scattering potentials. The IRT reveals that the scattering is completely suppressed along the three directions θ = (2n+1)π/3 with n=1,2,3. We also obtain analytical results of the thermopower and thermal conductivity at low temperature. The thermoelectric transport coefficients obey the Wiedemann-Franz law, even in the presence of <i>k</i>-cubic Rashba spin-orbit interaction (RSOI) at low temperature. In the presence of quantizing magnetic field, the signature of the RSOI is revealed through the appearance of the beating pattern in the Shubnikov-de Haas (SdH) oscillations of thermopower and thermal conductivity in low magnetic field regime. The empirical formulae for the SdH oscillation frequencies accurately describe the locations of the beating nodes. The beating pattern in magnetothermoelectric measurement can be used to extract the spin-orbit coupling constant. © 2017 IOP Publishing Ltd.

Electrical and thermoelectric transport properties of two-dimensional fermionic systems with k-cubic spin-orbit coupling

NASA Astrophysics Data System (ADS)

Mawrie, Alestin; Verma, Sonu; Kanti Ghosh, Tarun

2017-11-01

We investigate the effect of k-cubic spin-orbit interaction on the electrical and thermoelectric transport properties of two-dimensional fermionic systems. We obtain exact analytical expressions of the inverse relaxation time (IRT) and the Drude conductivity for long-range Coulomb and short-range delta scattering potentials. The IRT reveals that the scattering is completely suppressed along the three directions θ^\\prime = (2n+1)π/3 with n=1, 2, 3 . We also obtain analytical results of the thermopower and thermal conductivity at low temperature. The thermoelectric transport coefficients obey the Wiedemann-Franz law, even in the presence of k-cubic Rashba spin-orbit interaction (RSOI) at low temperature. In the presence of a quantizing magnetic field, the signature of the RSOI is revealed through the appearance of the beating pattern in the Shubnikov-de Haas (SdH) oscillations of thermopower and thermal conductivity in the low magnetic field regime. The empirical formulae for the SdH oscillation frequencies accurately describe the locations of the beating nodes. The beating pattern in magnetothermoelectric measurement can be used to extract the spin-orbit coupling constant.

Electrical properties and transport mechanisms of p-znte/n-si heterojunctions

NASA Astrophysics Data System (ADS)

Seyam, M. A. M.; El-Shair, H. T.; Salem, G. F.

2008-03-01

Zinc telluride thin films have been deposited on glass and silicon wafers substrates at room temperature by thermal evaporation technique in a vacuum of 10-5 Torr. The thickness dependence of both the dc electrical resistivity and thermoelectric power of ZnTe were carried out at room temperature and after being annealed over a thickness range from 22 nm to 170 nm. The type of conduction, the carriers concentration and the conduction mechanisms were revealed. The average thermal activation energy Δ E equals to 0.324 eV for the as deposited films and 0.306 eV for annealed films, it is found to correspond with the ionization energy reported for intrinsic defect levels in ZnTe. Seebeck coefficient measurements showed that ZnTe thin films behave as p-type semiconductor and the average value of the free charge carrier concentration is found to be 1.6×1019 cm-3. The built-in voltage, the width of the depletion region, the diode quality factor and the operating conduction mechanisms have been determined from dark current-voltage (I-V) and capacitance-voltage (C-V) characteristics of p-ZnTe/ n-Si heterojunctions.

Low Thermal Conductivity of RE-Doped SrO(SrTiO3)1 Ruddlesden Popper Phase Bulk Materials Prepared by Molten Salt Method

NASA Astrophysics Data System (ADS)

Putri, Yulia Eka; Said, Suhana Mohd; Refinel, Refinel; Ohtaki, Michitaka; Syukri, Syukri

2018-04-01

The SrO(SrTiO3)1 (Sr2TiO4) Ruddlesden Popper (RP) phase is a natural superlattice comprising of alternately stacking perovskite-type SrTiO3 layers and rock salt SrO layers along the crystallographic c direction. This paper discusses the properties of the Sr2TiO4 and (La, Sm)-doped Sr2TiO4 RP phase synthesized via molten salt method, within the context of thermoelectric applications. A good thermoelectric material requires high electrical conductivity, high Seebeck coefficient and low thermal conductivity. All three conditions have the potential to be fulfilled by the Sr2TiO4 RP phase, in particular, the superlattice structure allows a higher degree of phonon scattering hence resulting in lowered thermal conductivity. In this work, the Sr2TiO4 RP phase is doped with Sm and La respectively, which allows injection of charge carriers, modification of its electronic structure for improvement of the Seebeck coefficient, and most significantly, reduction of thermal conductivity. The particles with submicron size allows excessive phonon scattering along the boundaries, thus reduces the thermal conductivity by fourfold. In particular, the Sm-doped sample exhibited even lower lattice thermal conductivity, which is believed to be due to the mismatch in the ionic radius of Sr and Sm. This finding is useful as a strategy to reduce thermal conductivity of Sr2TiO4 RP phase materials as thermoelectric candidates, by employing dopants of differing ionic radius.

Theoretical Study of Electronic Structure and Thermoelectric Properties of Doped CuAlO2

NASA Astrophysics Data System (ADS)

Poopanya, P.; Yangthaisong, A.; Rattanapun, C.; Wichainchai, A.

2011-05-01

The doping level dependence of thermoelectric properties of delafossite CuAlO2 has been investigated in the constant scattering time ( τ) approximation, starting from the first principles of electronic structure. In particular, the lattice parameters and the energy band structure were calculated using the total energy plane-wave pseudopotential method. It was found that the lattice parameters of CuAlO2 are a = 2.802 Å and c = 16.704 Å, and the internal parameter is u = 0.1097. CuAlO2 has an indirect band gap of 2.17 eV and a direct gap of 3.31 eV. The calculated energy band structures were then used to calculate the electrical transport coefficients of CuAlO2. By considering the effects of doping level and temperature, it was found that the Seebeck coefficient S( T) increases with increasing acceptor doping ( A d) level. The values of S( T) in our experiments correspond to an A d level at 0.262 eV, which is identified as the Fermi level of CuAlO2. Based on our experimental Seebeck coefficient and the electrical conductivity, the constant relaxation time is estimated to be 1 × 10-16 s. The power factor is large for a low A d level and increases with temperature. It is suggested that delafossite CuAlO2 can be considered as a promising thermoelectric oxide material at high doping and high temperature.

High-throughput screening for combinatorial thin-film library of thermoelectric materials.

PubMed

Watanabe, Masaki; Kita, Takuji; Fukumura, Tomoteru; Ohtomo, Akira; Ueno, Kazunori; Kawasaki, Masashi

2008-01-01

A high-throughput method has been developed to evaluate the Seebeck coefficient and electrical resistivity of combinatorial thin-film libraries of thermoelectric materials from room temperature to 673 K. Thin-film samples several millimeters in size were deposited on an integrated Al2O3 substrate with embedded lead wires and local heaters for measurement of the thermopower under a controlled temperature gradient. An infrared camera was used for real-time observation of the temperature difference Delta T between two electrical contacts on the sample to obtain the Seebeck coefficient. The Seebeck coefficient and electrical resistivity of constantan thin films were shown to be almost identical to standard data for bulk constantan. High-throughput screening was demonstrated for a thermoelectric Mg-Si-Ge combinatorial library.

Thermoelectric transport properties in graphene connected molecular junctions

NASA Astrophysics Data System (ADS)

Rodriguez, S. T.; Grosu, I.; Crisan, M.; Ţifrea, I.

2018-02-01

We study the electronic contribution to the main thermoelectric properties of a molecular junction consisting of a single quantum dot coupled to graphene external leads. The system electrical conductivity (G), Seebeck coefficient (S), and the thermal conductivity (κ), are numerically calculated based on a Green's function formalism that includes contributions up to the Hartree-Fock level. We consider the system leads to be made either of pure or gapped-graphene. To describe the free electrons in the gapped-graphene electrodes we used two possible scenarios, the massive gap scenario, and the massless gap scenario, respectively. In all cases, the Fano effect is responsible for a strong violation of the Wiedemann-Franz law and we found a substantial increase of the system figure of merit ZT due to a drastic reduction of the system thermal coefficient. In the case of gapped-graphene electrodes, the system figure of merit presents a maximum at an optimal value of the energy gap of the order of Δ / D ∼ 0.002 (massive gap scenario) and Δ / D ∼ 0.0026 (massless gap scenario). Additionally, for all cases, the system figure of merit is temperature dependent.

The Effects of Excess Co on the Phase Composition and Thermoelectric Properties of Half-Heusler NbCoSb.

PubMed

Huang, Lihong; Wang, Junchen; Chen, Xi; He, Ran; Shuai, Jing; Zhang, Jianjun; Zhang, Qinyong; Ren, Zhifeng

2018-05-11

NbCoSb with nominal 19 valence electrons, and is supposed to be metallic, has recently been reported to also exhibit the thermoelectric properties of a heavily doped n-type semiconductor. In this study, we prepared Co-rich NbCo 1+ x Sb samples ( x = 0, 0.2, 0.3, 0.4, 0.5), and their phase compositions, microstructures and thermoelectric properties were investigated. The Seebeck coefficient increased a great deal with increasing x , due to decreasing carrier concentration, and the total thermal conductivity reduced mainly because of declining κ e . Finally, a peak thermoelectric figure of merit, ZT , was about 0.46 for NbCo 1.3 Sb at 973 K. This enhancement was mainly attributed to the reduction of electric thermal conductivity and the increase of Seebeck coefficient. The excess Co had effects on the carrier concentration, deformation potential E def and DOS effective mass m * . Adding an excessive amount of Co leads to a very high E def , which was detrimental for transport characteristics.

Relaxation processes and conduction mechanism in bismuth ferrite lead titanate composites

NASA Astrophysics Data System (ADS)

Sahu, Truptimayee; Behera, Banarji

2018-02-01

In this study, samarium (Sm)-doped multiferroic composites of 0.8BiSmxFe1-xO3-0.2PbTiO3 where x = 0.05, 0.10, 0.15, and 0.20 were prepared via the conventional solid state reaction route. The electrical properties of these composites were analyzed using an impedance analyzer over a wide range of temperatures and frequencies (102-106 Hz). The impedance and modulus analyses confirmed the presence of both bulk and grain boundary effects in the materials. The temperature dependence of impedance and modulus spectrum indicated the negative temperature coefficient of resistance behavior. The dielectric relaxation exhibited non-Debye type behavior and it was temperature dependent. The relaxation time (τ) and DC conductivity followed an Arrhenius type behavior. The frequency-dependent AC conductivity obeyed Jonscher's power law. The correlated barrier hopping model was appropriate to understand the conduction mechanism in the composites considered.

Small Fermi surfaces and strong correlation effects in Dirac materials with holography

NASA Astrophysics Data System (ADS)

Seo, Yunseok; Song, Geunho; Park, Chanyong; Sin, Sang-Jin

2017-10-01

Recent discovery of transport anomaly in graphene demonstrated that a system known to be weakly interacting may become strongly correlated if system parameter (s) can be tuned such that fermi surface is sufficiently small. We study the strong correlation effects in the transport coefficients of Dirac materials doped with magnetic impurity under the magnetic field using holographic method. The experimental data of magneto-conductivity are well fit by our theory, however, not much data are available for other transports of Dirac material in such regime. Therefore, our results on heat transport, thermo-electric power and Nernst coefficients are left as predictions of holographic theory for generic Dirac materials in the vicinity of charge neutral point with possible surface gap. We give detailed look over each magneto-transport observable and 3Dplots to guide future experiments.

Thermoelectric properties of n-type polycrystalline BixSb2-xTe3 alloys

NASA Technical Reports Server (NTRS)

Snyder, J.; Gerovac, N.; Caillat, T.

2002-01-01

(BixSbl-x)2Te3(.5 = x = .7) polycrystalline samples were synthesized using a combination of melting and powder metallurgy techniques. The samples were hot pressed in graphite dies and cut perpendicular and parallel to the pressing direction. Samples were examined by microprobe analysis to determine their atomic composition. The thermoelectric properties were measured at room temperature in both directions. These properties include Seebeck coefficient, thermal conductivity, electrical resistivity, and Hall effect. The thermoelectric figure-of-merit, ZT, was calculated fiom these properties.

Thermoelectric properties of cerium monopnictides

NASA Technical Reports Server (NTRS)

Danielson, L. R.; Alexander, M. N.; Wood, C.; Lockwood, R. A.; Vandersande, J. W.

1987-01-01

Several cerium pnictides have been synthesized from the pure elements and hot pressed into test samples. Measurements of Seebeck coefficients and electrical resistivities were performed on these samples from room temperature to 1000 C. Cerium arsenide and cerium antimonide are n-type; cerium nitride changes from p-type to n-type conduction at 800 C. The materials are semimetals with resistivities below 1 mohm/cm. Cerium arsenide is the most favorable of the pnictides studied for high-temperature thermoelectric energy conversion, with an average power factor of 15 microW/cm K sq from 500 to 1000 C.

Molecular dynamics simulations of dense plasmas

DOE Office of Scientific and Technical Information (OSTI.GOV)

Collins, L.A.; Kress, J.D.; Kwon, I.

1993-12-31

We have performed quantum molecular dynamics simulations of hot, dense plasmas of hydrogen over a range of temperatures(0.1-5eV) and densities(0.0625-5g/cc). We determine the forces quantum mechanically from density functional, extended Huckel, and tight binding techniques and move the nuclei according to the classical equations of motion. We determine pair-correlation functions, diffusion coefficients, and electrical conductivities. We find that many-body effects predominate in this regime. We begin to obtain agreement with the OCP and Thomas-Fermi models only at the higher temperatures and densities.

DC conductivity and magnetic properties of piezoelectric-piezomagnetic composite system

NASA Astrophysics Data System (ADS)

Hemeda, O. M.; Tawfik, A.; A-Al-Sharif; Amer, M. A.; Kamal, B. M.; El Refaay, D. E.; Bououdina, M.

2012-11-01

A series of composites (1-x) (Ni0.8Zn0.2Fe2O4)+x (BaTiO3), where x=0%, 20%, 40%, 60%, 80% and 100% BT content, have been prepared by the standard ceramic technique, then sintered at 1200 °C for 8 h. X-ray diffraction analysis shows that the prepared composites consist of two phases, ferrimagnetic and ferroelectric. DC electrical resistivity, thermoelectric power, charge carriers concentration and charge carrier mobility have been studied at different temperatures. It was found that the DC electrical conductivity increases with increasing BT content. The values of the thermoelectric power were positive and negative for the composites indicating that there are two conduction mechanisms, hopping and band conduction, respectively. Using the values of DC electrical conductivity and thermoelectric power, the values of charge carrier mobility and the charge carrier concentration were calculated. Magnetic measurements (hysteresis loop and magnetic permeability) show that the magnetization decreases by increasing BT content. M-H loop of pure Ni0.6 Zn0.4 Fe2O4 composite indicates that it is paramagnetic at room temperature and that the magnetization is diluted by increasing the BT content in the composite system. The value of magnetoelectric coefficient for the composites decreases by increasing BT content for all the compositions except for 40% BT content, which may be due to the low resistivity of magnetic phase compared with the BT phase that causes a leakage of induced charges on the piezoelectric phase. Since both ferroelectric and magnetic phases preserve their basic properties in the bulk composite, the present BT-NZF composite are potential candidates for applications as pollution sensors and electromagnetic waves.

Electrical and Nonlinear Optical Studies of Specific Organic Molecular and Nonconjugated Conductive Polymeric Systems

NASA Astrophysics Data System (ADS)

Narayanan, Ananthakrishnan

In this research, structural, electrical and nonlinear optical characteristics of: (a) single crystal films involving a noncentrosymmetric molecule DAST and a laser dye IR125 and (b) specific nonconjugated conducting polymers including poly(beta-pinene) and polynorbornene have been studied. 4'-dimethylamino-N-methyl-4-stilbazolium tosylate (DAST) is a well known second order nonlinear optical material. This material has exceptionally high electro-optic coefficients, high thermal stability and ultrafast response time. In this work single crystal films involving a combination of DAST and IR125 have been prepared using modified shear method and the films have been characterized using polarized optical microscopy, X-ray diffraction, polarization dependent optical absorption and photoluminescence spectroscopy. The electro-optic coefficient of these films measured at 633nm was found to be 300pm/V. Since IR-125 has a strong absorption band from 500nm to 800nm, these films are promising for various applications in nonlinear optics at longer wavelength and for light emission. Nonconjugated conducting polymers are a class of polymers that have at least one double bond in their repeat units. 1,4-cis polyisoprene, polyalloocimene, styrene butadiene rubber, poly(ethylenepyrrolediyl) derivatives, and poly(beta-pinene) are some of the well known examples of nonconjugated conducting polymers. In this work, polynorborne, a new addition to the class of nonconjugated conducting polymers is discussed. Like other polymers in this class, polynorbornene exhibits increase in electrical conductivity by many orders of magnitude upon doping with iodine. The maximum electrical conductivity of this material is 0.01 S/cm. As shown by using FTIR microscopy, the C=C bonds are transformed into cation radicals when polynorborne is doped. This is due to the charge-transfer from the double bond to the dopant (iodine). These materials like other nonconjugated conducting polymers have significant applications in electro-optics and photonics. Electron paramagnetic resonance measurements on poly(beta-pinene) before and after doping with iodine are reported in this work. The EPR signal of this polymer increases proportionally with the iodine concentration due to the formation of cation radicals upon doping and charge-transfer. The results agree well with the doping mechanism of nonconjugated conducting polymers discussed earlier in literature. Hyperfine splitting in heavily doped polymers is observed due to the reduced distance between the cation radical and the iodine anion. Off-resonant electro-optic measurements in doped poly(beta-pinene) at 790nm, 800nm, 810nm and 1.55microm using field-induced birefringence technique have been studied. The results show that this material exhibits the highest cubic nonlinearities of all known materials. The Kerr coefficient measured at 1.55microm is 1.6x10-10 m/V2 which is about 30 times higher than that of conjugated polymers. Results of two photon measurements in this doped polymer using pump-probe technique with a pulsed, mode-locked (150 fs pulses) beam from a Ti-Sapphire laser are reported. The measured value of alpha2 at 790 nm and 795 nm were found to be 2.28+/-0.1 cm/MW and 2.5+/-0.1 cm/MW respectively. The data confirms that the nonlinearity in this material is ultrafast and electronic in nature. Such large nonlinearities in these materials are attributed the charge confinement in these materials in a sub-nanometer domain (upon doping) resulting in a metal-like quantum dot structure. Photovoltaic measurements in a composite involving poly(beta-pinene) and C60 are discussed. This is the first time a nonconjugated conducting polymer based photovoltaic cell has been fabricated. A composite involving 4% C60 by weight produced a photovoltage of 280mV for an incident light intensity of 6mW/sq.cm. These low cost devices have applications in solar cells, photodetectors etc. A nonlinear optical waveguide was prepared by casting a thin film of poly(beta-pinene) on bare multi-mode optical fiber and doping it with iodine. The doped fibers were of excellent optical quality. Two-photon absorption experiments were conducted using these waveguides and large changes in transmission upto 28% was observed in 15cm long fiber. More work needs to be done to confirm this result. This is a significant step in the direction of making these materials a viable choice for ultrafast (femtosecond time-scale) optical devices. To summarize, these works included detailed investigations of structural, electrical and nonlinear optical characteristics of specific molecular crystal films and nonconjugated conducting polymers.

Nanostructured silicon for thermoelectric

NASA Astrophysics Data System (ADS)

Stranz, A.; Kähler, J.; Waag, A.; Peiner, E.

2011-06-01

Thermoelectric modules convert thermal energy into electrical energy and vice versa. At present bismuth telluride is the most widely commercial used material for thermoelectric energy conversion. There are many applications where bismuth telluride modules are installed, mainly for refrigeration. However, bismuth telluride as material for energy generation in large scale has some disadvantages. Its availability is limited, it is hot stable at higher temperatures (>250°C) and manufacturing cost is relatively high. An alternative material for energy conversion in the future could be silicon. The technological processing of silicon is well advanced due to the rapid development of microelectronics in recent years. Silicon is largely available and environmentally friendly. The operating temperature of silicon thermoelectric generators can be much higher than of bismuth telluride. Today silicon is rarely used as a thermoelectric material because of its high thermal conductivity. In order to use silicon as an efficient thermoelectric material, it is necessary to reduce its thermal conductivity, while maintaining high electrical conductivity and high Seebeck coefficient. This can be done by nanostructuring into arrays of pillars. Fabrication of silicon pillars using ICP-cryogenic dry etching (Inductive Coupled Plasma) will be described. Their uniform height of the pillars allows simultaneous connecting of all pillars of an array. The pillars have diameters down to 180 nm and their height was selected between 1 micron and 10 microns. Measurement of electrical resistance of single silicon pillars will be presented which is done in a scanning electron microscope (SEM) equipped with nanomanipulators. Furthermore, measurement of thermal conductivity of single pillars with different diameters using the 3ω method will be shown.

In-situ Observation of Size and Irradiation Effects on Thermoelectric Properties of Bi-Sb-Te Nanowire in FIB Trimming

PubMed Central

Chien, Chia-Hua; Lee, Ping-Chung; Tsai, Wei-Han; Lin, Chien-Hung; Lee, Chih-Hao; Chen, Yang-Yuan

2016-01-01

In this report, the thermoelectric properties of a Bi0.8Sb1.2Te2.9 nanowire (NW) were in-situ studied as it was trimmed from 750 down to 490 and 285 nm in diameter by a focused ion beam. While electrical and thermal conductivities both indubitably decrease with the diameter reduction, the two physical properties clearly exhibit different diameter dependent behaviors. For 750 and 490 nm NWs, much lower thermal conductivities (0.72 and 0.69 W/m-K respectively) were observed as compared with the theoretical prediction of Callaway model. The consequence indicates that in addition to the size effect, extra phonon scattering of defects created by Ga ion irradiation was attributed to the reduction of thermal conductivities. As the NW was further trimmed down to 285 nm, both the electrical and thermal conductivities exhibited a dramatic reduction which was ascribed to the formation of amorphous structure due to Ga ion irradiation. The size dependence of Seebeck coefficient and figure of merit (ZT) show the maximum at 750 nm, then decrease linearly with size decrease. The study not only provides the thoroughly understanding of the size and defect effects on the thermoelectric properties but also proposes a possible method to manipulate the thermal conductivity of NWs via ion irradiation. PMID:27030206

Use of 3-D magnetic resonance electrical impedance tomography in detecting human cerebral stroke: a simulation study*

PubMed Central

Gao, Nuo; Zhu, Shan-an; He, Bin

2005-01-01

We have developed a new three dimensional (3-D) conductivity imaging approach and have used it to detect human brain conductivity changes corresponding to acute cerebral stroke. The proposed Magnetic Resonance Electrical Impedance Tomography (MREIT) approach is based on the J-Substitution algorithm and is expanded to imaging 3-D subject conductivity distribution changes. Computer simulation studies have been conducted to evaluate the present MREIT imaging approach. Simulations of both types of cerebral stroke, hemorrhagic stroke and ischemic stroke, were performed on a four-sphere head model. Simulation results showed that the correlation coefficient (CC) and relative error (RE) between target and estimated conductivity distributions were 0.9245±0.0068 and 8.9997%±0.0084%, for hemorrhagic stroke, and 0.6748±0.0197 and 8.8986%±0.0089%, for ischemic stroke, when the SNR (signal-to-noise radio) of added GWN (Gaussian White Noise) was 40. The convergence characteristic was also evaluated according to the changes of CC and RE with different iteration numbers. The CC increases and RE decreases monotonously with the increasing number of iterations. The present simulation results show the feasibility of the proposed 3-D MREIT approach in hemorrhagic and ischemic stroke detection and suggest that the method may become a useful alternative in clinical diagnosis of acute cerebral stroke in humans. PMID:15822161

Influence and Correction from the Human Body on the Measurement of a Power-Frequency Electric Field Sensor

PubMed Central

Xiao, Dongping; Liu, Huaitong; Zhou, Qiang; Xie, Yutong; Ma, Qichao

2016-01-01

According to the operating specifications of existing electric field measuring instruments, measuring technicians must be located far from the instruments to eliminate the influence of the human body occupancy on a spatial electric field. Nevertheless, in order to develop a portable safety protection instrument with an effective electric field warning function for working staff in a high-voltage environment, it is necessary to study the influence of an approaching human body on the measurement of an electric field and to correct the measurement results. A single-shaft electric field measuring instrument called the Type LP-2000, which was developed by our research team, is used as the research object in this study. First, we explain the principle of electric field measurement and describe the capacitance effect produced by the human body. Through a theoretical analysis, we show that the measured electric field value decreases as a human body approaches. Their relationship is linearly proportional. Then, the ratio is identified as a correction coefficient to correct for the influence of human body proximity. The conclusion drawn from the theoretical analysis is proved via simulation. The correction coefficient kb = 1.8010 is obtained on the basis of the linear fitting of simulated data. Finally, a physical experiment is performed. When no human is present, we compare the results from the Type LP-2000 measured with Narda EFA-300 and the simulated value to verify the accuracy of the Type LP-2000. For the case of an approaching human body, the correction coefficient kb* = 1.9094 is obtained by comparing the data measured with the Type LP-2000 to the simulated value. The correction coefficient obtained from the experiment (i.e., kb*) is highly consistent with that obtained from the simulation (i.e., kb). Two experimental programs are set; under these programs, the excitation voltages and distance measuring points are regulated to produce different electric field intensities. Using kb = 1.9094, the corrected measurement of electric field intensity can accurately reflect the original environmental electric field intensity, and the maximal error is less than 6% in all the data comparisons. These results verify the effectiveness of our proposed method. PMID:27294936

Influence and Correction from the Human Body on the Measurement of a Power-Frequency Electric Field Sensor.

PubMed

Xiao, Dongping; Liu, Huaitong; Zhou, Qiang; Xie, Yutong; Ma, Qichao

2016-06-10

According to the operating specifications of existing electric field measuring instruments, measuring technicians must be located far from the instruments to eliminate the influence of the human body occupancy on a spatial electric field. Nevertheless, in order to develop a portable safety protection instrument with an effective electric field warning function for working staff in a high-voltage environment, it is necessary to study the influence of an approaching human body on the measurement of an electric field and to correct the measurement results. A single-shaft electric field measuring instrument called the Type LP-2000, which was developed by our research team, is used as the research object in this study. First, we explain the principle of electric field measurement and describe the capacitance effect produced by the human body. Through a theoretical analysis, we show that the measured electric field value decreases as a human body approaches. Their relationship is linearly proportional. Then, the ratio is identified as a correction coefficient to correct for the influence of human body proximity. The conclusion drawn from the theoretical analysis is proved via simulation. The correction coefficient kb = 1.8010 is obtained on the basis of the linear fitting of simulated data. Finally, a physical experiment is performed. When no human is present, we compare the results from the Type LP-2000 measured with Narda EFA-300 and the simulated value to verify the accuracy of the Type LP-2000. For the case of an approaching human body, the correction coefficient kb* = 1.9094 is obtained by comparing the data measured with the Type LP-2000 to the simulated value. The correction coefficient obtained from the experiment (i.e., kb*) is highly consistent with that obtained from the simulation (i.e., kb). Two experimental programs are set; under these programs, the excitation voltages and distance measuring points are regulated to produce different electric field intensities. Using kb = 1.9094, the corrected measurement of electric field intensity can accurately reflect the original environmental electric field intensity, and the maximal error is less than 6% in all the data comparisons. These results verify the effectiveness of our proposed method.

Effective ionization coefficients, limiting electric fields, and electron energy distributions in CF{sub 3}I + CF{sub 4} + Ar ternary gas mixtures

DOE Office of Scientific and Technical Information (OSTI.GOV)

Tezcan, S. S.; Dincer, M. S.; Bektas, S.

2016-07-15

This paper reports on the effective ionization coefficients, limiting electric fields, electron energy distribution functions, and mean energies in ternary mixtures of (Trifluoroiodomethane) CF{sub 3}I + CF{sub 4} + Ar in the E/N range of 100–700 Td employing a two-term solution of the Boltzmann equation. In the ternary mixture, CF{sub 3}I component is increased while the CF{sub 4} component is reduced accordingly and the 40% Ar component is kept constant. It is seen that the electronegativity of the mixture increases with increased CF{sub 3}I content and effective ionization coefficients decrease while the limiting electric field values increase. Synergism in themore » mixture is also evaluated in percentage using the limiting electric field values obtained. Furthermore, it is possible to control the mean electron energy in the ternary mixture by changing the content of CF{sub 3}I component.« less

Room temperature magnetoelectric coupling and electrical properties of Ni doped Co - ferrite - PZT nanocomposites

NASA Astrophysics Data System (ADS)

Chakraborty, Sarit; Mandal, S. K.; Dey, P.; Saha, B.

2018-04-01

Multiferroic magnetoelectric materials are very interesting for the researcher for the potential application in device preparation. We have prepared 0.3Ni0.5Co0.5Fe2O4 - 0.7PbZr0.58Ti0.42O3 magnetoelectric nanocomposites through chemical pyrophoric reaction process followed by solid state reaction and represented magnetoelectric coupling coefficient, thermally and magnetically tunable AC electrical properties. For the structural characterization XRD pattern and SEM micrograph have been analyzed. AC electrical properties reveal that the grain boundaries resistances are played dominating role in the conduction process in the system. Dielectric studies are represents that the dielectric polarization is decreased with frequency as well as magnetic field where it increases with increasing temperature. The dielectric profiles also represents the electromechanical resonance at a frequency of ˜183 kHz. High dielectric constant and low dielectric loss at room temperature makes the material very promising for the application of magnetic field sensor devices.

Effect of oxygen vacancy distribution on the thermoelectric properties of La-doped SrTiO3 epitaxial thin films

NASA Astrophysics Data System (ADS)

Sarath Kumar, S. R.; Abutaha, A. I.; Hedhili, M. N.; Alshareef, H. N.

2012-12-01

A detailed study of the role of oxygen vacancies in determining the effective mass and high temperature (300-1000 K) thermoelectric properties of La-doped epitaxial SrTiO3 thin films is presented. It is observed that at intermediate temperatures, a transition from degenerate to non-degenerate behavior is observed in the Seebeck coefficient, but not electrical conductivity, which is attributed to heterogeneous oxygen non-stoichiometry. Heikes formula is found to be invalid for the films with oxygen vacancies. By fitting the spectroscopic ellipsometry (SE) data, obtained in the range 300-2100 nm, using a Drude-Lorentz dispersion relation with two Lorentz oscillators, the electrical and optical properties of the films are extracted. Using the excellent agreement between the transport properties extracted from SE modeling and direct electrical measurements, we demonstrate that an increase in concentration of oxygen vacancies results in a simultaneous increase of both carrier concentration and electron effective mass, resulting in a higher power factor.

Thermoelectric properties of bismuth telluride nanoplate thin films determined using combined infrared spectroscopy and first-principles calculation

NASA Astrophysics Data System (ADS)

Wada, Kodai; Tomita, Koji; Takashiri, Masayuki

2018-06-01

The thermoelectric properties of bismuth telluride (Bi2Te3) nanoplate thin films were estimated using combined infrared spectroscopy and first-principles calculation, followed by comparing the estimated properties with those obtained using the standard electrical probing method. Hexagonal single-crystalline Bi2Te3 nanoplates were first prepared using solvothermal synthesis, followed by preparing Bi2Te3 nanoplate thin films using the drop-casting technique. The nanoplates were joined by thermally annealing them at 250 °C in Ar (95%)–H2 (5%) gas (atmospheric pressure). The electronic transport properties were estimated by infrared spectroscopy using the Drude model, with the effective mass being determined from the band structure using first-principles calculations based on the density functional theory. The electrical conductivity and Seebeck coefficient obtained using the combined analysis were higher than those obtained using the standard electrical probing method, probably because the contact resistance between the nanoplates was excluded from the estimation procedure of the combined analysis method.

4D ERT-based calibration and prediction of biostimulant induced changes in fluid conductivity

NASA Astrophysics Data System (ADS)

Johnson, T. C.; Versteeg, R. J.; Day-Lewis, F. D.; Major, W. R.; Wright, K. E.

2008-12-01

In-situ bioremediation is an emerging and cost-effective method of removing organic contaminants from groundwater. The performance of bioremedial systems depends on the adequate delivery and distribution of biostimulants to contaminated zones. Monitoring the distribution of biostimulants using monitoring wells is expensive, time consuming, and provides inadequate information between sampling wells. We discuss a Hydrogeophysical Performance Monitoring System (HPMS) deployed to monitor bioremediation efforts at a TCE-contaminated Superfund site in Brandywine MD. The HPMS enables autonomous electrical geophysical data acquisition, processing, quality-assurance/quality-control, and inversion. Our objective is to demonstrate the feasibility and cost effectiveness of the HPMS to provide near real-time information on the spatiotemporal behavior of injected biostimulants. As a first step, we use time-lapse electrical resistivity tomography (ERT) to estimate changes in bulk conductivity caused by the injectate. We demonstrate how ERT-based bulk conductivity estimates can be calibrated with a small number of fluid conductivity measurements to produce ERT-based estimates of fluid conductivity. The calibration procedure addresses the spatially variable resolution of the ERT tomograms. To test the validity of these estimates, we used the ERT results to predict the fluid conductivity at tens of points prior to field sampling of fluid conductivity at the same points. The comparison of ERT-predicted vs. observed fluid conductivity displays a high degree of correlation (correlation coefficient over 0.8), and demonstrates the ability of the HPMS to estimate the four-dimensional (4D) distribution of fluid conductivity caused by the biostimulant injection.

Review on measurement techniques of transport properties of nanowires Additions and Corrections. See DOI:10.1039/C3NR03242F Click here for additional data file.

PubMed Central

Rojo, Miguel Muñoz; Calero, Olga Caballero; Lopeandia, A. F.; Rodriguez-Viejo, J.

2013-01-01

Physical properties at the nanoscale are novel and different from those in bulk materials. Over the last few decades, there has been an ever growing interest in the fabrication of nanowire structures for a wide variety of applications including energy generation purposes. Nevertheless, the study of their transport properties, such as thermal conductivity, electrical conductivity or Seebeck coefficient, remains an experimental challenge. For instance, in the particular case of nanostructured thermoelectrics, theoretical calculations have shown that nanowires offer a promising way of enhancing the hitherto low efficiency of these materials in the conversion of temperature differences into electricity. Therefore, within the thermoelectrical community there has been a great experimental effort in the measurement of these quantities in actual nanowires. The measurements of these properties at the nanoscale are also of interest in fields other than energy, such as electrical components for microchips, field effect transistors, sensors, and other low scale devices. For all these applications, knowing the transport properties is mandatory. This review deals with the latest techniques developed to perform the measurement of these transport properties in nanowires. A thorough overview of the most important and modern techniques used for the characterization of different kinds of nanowires will be shown. PMID:24113712

Development of Ni-Ferrite-Based PVDF Nanomultiferroics

NASA Astrophysics Data System (ADS)

Behera, C.; Choudhary, R. N. P.; Das, Piyush R.

2017-10-01

Thin-film polyvinylidene fluoride (PVDF)-spinel ferrite nanocomposites with 0-3 connectivity and varying composition, i.e., (1 - x)PVDF- xNiFe2O4 ( x = 0.05, 0.1, 0.15), have been fabricated by a solution-casting route. The basic crystal data and microstructure of the composite samples were obtained by x-ray powder diffraction analysis and scanning electron microscopy, respectively. Preliminary structural analysis showed the presence of polymeric electroactive β-phase of PVDF (matrix) and spinel ferrite (filler) phase in the composites. The composites were found to be flexible with high relative dielectric constant ( ɛ r) and low loss tangent (tan δ). Detailed studies of their electrical characteristics using complex impedance spectroscopy showed the contributions of bulk (grains) and grain boundaries in the resistive and capacitive properties of the composites. Study of the frequency-dependent electrical conductivity at different temperatures showed that Jonscher's power law could be used to interpret the transport properties of the composites. Important experimental data and results obtained from magnetic as well ferroelectric hysteresis loops and the first-order magnetoelectric coefficient suggest the suitability of some of these composites for fabrication of multifunctional devices. The low electrical conductivity, high dielectric constant, and low loss tangent suggest that such composites could be used in capacitor devices.

Industrial Applications of Graphite Fluoride Fibers

NASA Technical Reports Server (NTRS)

Hung, Ching-Cheh; Kucera, Donald

1991-01-01

Based on fluorination technology developed during 1934 to 1959, and the fiber technology developed during the 1970s, a new process was developed to produce graphite fluoride fibers. In the process, pitch based graphitized carbon fibers are at first intercalated and deintercalated several times by bromine and iodine, followed by several cycles of nitrogen heating and fluorination at 350 to 370 C. Electrical, mechanical, and thermal properties of this fiber depend on the fluorination process and the fluorine content of the graphite fluoride product. However, these properties are between those of graphite and those of PTFE (Teflon). Therefore, it is considered to be a semiplastic. The physical properties suggest that this new material may have many new and unexplored applications. For example, it can be a thermally conductive electrical insulator. Its coefficient of thermal expansion (CTE) can be adjusted to match that of silicon, and therefore, it can be a heat sinking printed circuit board which is CTE compatible with silicon. Using these fibers in printed circuit boards may provide improved electrical performance and reliability of the electronics on the board over existing designs. Also, since it releases fluorine at 300 C or higher, it can be used as a material to store fluorine and to conduct fluorination. This application may simplify the fluorination process and reduce the risk of handling fluorine.

Thickness dependent optical and electrical properties of CdSe thin films

DOE Office of Scientific and Technical Information (OSTI.GOV)

Purohit, A., E-mail: anuradha.purohit34@gmail.com; Chander, S.; Nehra, S. P.

2016-05-06

The effect of thickness on the optical and electrical properties of CdSe thin films is investigated in this paper. The films of thickness 445 nm, 631 nm and 810 nm were deposited on glass and ITO coated glass substrates using thermal evaporation technique. The deposited thin films were thermally annealed in air atmosphere at temperature 100°C and were subjected to UV-Vis spectrophotometer and source meter for optical and electrical analysis respectively. The absorption coefficient is observed to increase with photon energy and found maximum in higher photon energy region. The extinction coefficient and refractive index are also calculated. The electrical analysis shows thatmore » the electrical resistivity is observed to be decreased with thickness.« less

Imaging Electric Properties of Biological Tissues by RF Field Mapping in MRI

PubMed Central

Zhang, Xiaotong; Zhu, Shanan; He, Bin

2010-01-01

The electric properties (EPs) of biological tissue, i.e., the electric conductivity and permittivity, can provide important information in the diagnosis of various diseases. The EPs also play an important role in specific absorption rate (SAR) calculation, a major concern in high-field Magnetic Resonance Imaging (MRI), as well as in non-medical areas such as wireless-telecommunications. The high-field MRI system is accompanied by significant wave propagation effects, and the radio frequency (RF) radiation is dependent on the EPs of biological tissue. Based on the measurement of the active transverse magnetic component of the applied RF field (known as B1-mapping technique), we propose a dual-excitation algorithm, which uses two sets of measured B1 data to noninvasively reconstruct the electric properties of biological tissues. The Finite Element Method (FEM) was utilized in three-dimensional (3D) modeling and B1 field calculation. A series of computer simulations were conducted to evaluate the feasibility and performance of the proposed method on a 3D head model within a transverse electromagnetic (TEM) coil and a birdcage (BC) coil. Using a TEM coil, when noise free, the reconstructed EP distribution of tissues in the brain has relative errors of 12% ∼ 28% and correlated coefficients of greater than 0.91. Compared with other B1-mapping based reconstruction algorithms, our approach provides superior performance without the need for iterative computations. The present simulation results suggest that good reconstruction of electric properties from B1 mapping can be achieved. PMID:20129847

DOE Office of Scientific and Technical Information (OSTI.GOV)

Hossain, M. Anwar; Center for Crystal Science and Technology, University of Yamanashi, Miyamae 7-32, Kofu, Yamanashi 400-8511; Tanaka, Isao

We studied thermoelectric properties of YB{sub 41}Si{sub 1.3} single crystals grown by the floating zone method. The composition of the grown crystal was confirmed by electron probe micro-analysis. We have determined the growth direction for the first time for these borosilicides, and discovered relatively large anisotropy in electrical properties. We measured the electrical resistivity and Seebeck coefficient along [510] (the growth direction) and [052] directions and we found that this crystal exhibits strong electrical anisotropy with a maximum of more than 8 times. An interesting layered structural feature is revealed along [510] with dense boron cluster layers and yttrium layers,more » with conductivity enhanced along this direction. We obtained 3.6 times higher power factor along [510] compared to that along [052]. Although the ZT of the present system is low, anisotropy in the thermoelectric properties of a boride was reported for the first time, and can be a clue in developing other boride systems also. - Graphical abstract: The growth direction ([510]) was determined for the first time in YB{sub 41}Si{sub 1.3} single crystals and revealed an interesting layered feature of boron clusters and metal atoms, along which the electrical conductivity and thermoelectric power factor was strongly enhanced. - Highlights: • We have grown YB{sub 41}Si{sub 1.3} single crystals by the floating zone method. • Growth direction of [510] determined for first time in REB{sub 41}Si{sub 1.2}. • Electrical resistivity was strongly anisotropic with possible enhancement along metal layers. • The obtained power factor along [510] is 3.6 times higher than that along [052].« less

Thermoelectric properties of Te doped bulk Bi2Se3 system

NASA Astrophysics Data System (ADS)

Adam, A. M.; Elshafaie, A.; Mohamed, Abd El-Moez A.; Petkov, P.; Ibrahim, E. M. M.

2018-03-01

Polycrystalline bulk samples of Bi2(Se1‑xTex)3 system with x = 0.0–0.9 were prepared by the conventional melting method. Successfully and cheaply, Se atoms were replaced by Te atoms to get Bi2Se3-Bi2Te3 or even Bi2Te3 alone. Difference of mass and size between Te and Se atoms is expected to result in interesting properties in the Bi2(Se1‑xTex)3 system. All compounds showed a metal-semiconductor conductivity transition. The electrical conduction in the pristine Bi2Se3 compound increases with the low Te doping ratio (x = 0.3) then decreases monotonically for further amounts of Te. The Seebeck coefficient of Bi2Se3 compound is positive showing up a p-type conduction. However, introducing Te content increases the n-type conduction with a decrease in the Seebeck coefficient absolute value. In addition, Bi2Se3 compound is found to exhibit relatively high room temperature power factor and figure of merit values of 2.13 μW/m.k2. In an attempt to determine the figure of merit ZT, Bi2Se3 seems to be the best for room temperature, whereas, Te addition at high values makes the system just suitable for high temperature application.

Endocannabinoid Release Modulates Electrical Coupling between CCK Cells Connected via Chemical and Electrical Synapses in CA1

PubMed Central

Iball, Jonathan; Ali, Afia B.

2011-01-01

Electrical coupling between some subclasses of interneurons is thought to promote coordinated firing that generates rhythmic synchronous activity in cortical regions. Synaptic activity of cholecystokinin (CCK) interneurons which co-express cannabinoid type-1 (CB1) receptors are powerful modulators of network activity via the actions of endocannabinoids. We investigated the modulatory actions of endocannabinoids between chemically and electrically connected synapses of CCK cells using paired whole-cell recordings combined with biocytin and double immunofluorescence labeling in acute slices of rat hippocampus at P18–20 days. CA1 stratum radiatum CCK Schaffer collateral-associated cells were coupled electrically with each other as well as CCK basket cells and CCK cells with axonal projections expanding to dentate gyrus. Approximately 50% of electrically coupled cells received facilitating, asynchronously released inhibitory postsynaptic potential (IPSPs) that curtailed the steady-state coupling coefficient by 57%. Tonic CB1 receptor activity which reduces inhibition enhanced electrical coupling between cells that were connected via chemical and electrical synapses. Blocking CB1 receptors with antagonist, AM-251 (5 μM) resulted in the synchronized release of larger IPSPs and this enhanced inhibition further reduced the steady-state coupling coefficient by 85%. Depolarization induced suppression of inhibition (DSI), maintained the asynchronicity of IPSP latency, but reduced IPSP amplitudes by 95% and enhanced the steady-state coupling coefficient by 104% and IPSP duration by 200%. However, DSI did not did not enhance electrical coupling at purely electrical synapses. These data suggest that different morphological subclasses of CCK interneurons are interconnected via gap junctions. The synergy between the chemical and electrical coupling between CCK cells probably plays a role in activity-dependent endocannabinoid modulation of rhythmic synchronization. PMID:22125513

Low temperature hall effect investigation of conducting polymer-carbon nanotubes composite network.

PubMed

Bahrami, Afarin; Talib, Zainal Abidin; Yunus, Wan Mahmood Mat; Behzad, Kasra; M Abdi, Mahnaz; Din, Fasih Ud

2012-11-14

Polypyrrole (PPy) and polypyrrole-carboxylic functionalized multi wall carbon nanotube composites (PPy/f-MWCNT) were synthesized by in situ chemical oxidative polymerization of pyrrole on the carbon nanotubes (CNTs). The structure of the resulting complex nanotubes was characterized by transmission electron microscopy (TEM) and X-ray diffraction (XRD). The effects of f-MWCNT concentration on the electrical properties of the resulting composites were studied at temperatures between 100 K and 300 K. The Hall mobility and Hall coefficient of PPy and PPy/f-MWCNT composite samples with different concentrations of f-MWCNT were measured using the van der Pauw technique. The mobility decreased slightly with increasing temperature, while the conductivity was dominated by the gradually increasing carrier density.

Facile synthesis of PbTe nanoparticles and thin films in alkaline aqueous solution at room temperature

NASA Astrophysics Data System (ADS)

Wang, Y. Y.; Cai, K. F.; Yao, X.

2009-12-01

A novel, simple, and cost-effective route to PbTe nanoparticles and films is reported in this paper. The PbTe nanoparticles and films are fabricated by a chemical bath method, at room temperature and ambient pressure, using conventional chemicals as starting materials. The average grain size of the nanoparticles collected at the bottom of the bath is ˜25 nm. The film deposited on glass substrate is dense, smooth, and uniform with silver gray metallic luster. The film exhibits p-type conduction and has a moderate Seebeck coefficient value (˜147 μV K -1) and low electrical conductivity (˜0.017 S cm -1). The formation mechanism of the PbTe nanoparticles and films is proposed.

Intrinsic high electrical conductivity of stoichiometric SrNb O3 epitaxial thin films

NASA Astrophysics Data System (ADS)

Oka, Daichi; Hirose, Yasushi; Nakao, Shoichiro; Fukumura, Tomoteru; Hasegawa, Tetsuya

2015-11-01

SrV O3 and SrNb O3 are perovskite-type transition-metal oxides with the same d1 electronic configuration. Although SrNb O3 (4 d1 ) has a larger d orbital than SrV O3 (3 d1 ), the reported electrical resistivity of SrNb O3 is much higher than that of SrV O3 , probably owing to nonstoichiometry. In this paper, we grew epitaxial, high-conductivity stoichiometric SrNb O3 using pulsed laser deposition. The growth temperature strongly affected the Sr/Nb ratio and the oxygen content of the films, and we obtained stoichiometric SrNb O3 at a very narrow temperature window around 630 °C. The stoichiometric SrNb O3 epitaxial thin films grew coherently on KTa O3 (001) substrates with high crystallinity. The room-temperature resistivity of the stoichiometric film was 2.82 ×10-5Ω cm , one order of magnitude lower than the lowest reported value of SrNb O3 and comparable with that of SrV O3 . We observed a T -square dependence of resistivity below T*=180 K and non-Drude behavior in near-infrared absorption spectroscopy, attributable to the Fermi-liquid nature caused by electron correlation. Analysis of the T -square coefficient A of resistivity experimentally revealed that the 4 d orbital of Nb that is larger than the 3 d ones certainly contributes to the high electrical conduction of SrNb O3 .

Hydrogen self-diffusion in single crystal olivine and electrical conductivity of the Earth’s mantle

DOE Office of Scientific and Technical Information (OSTI.GOV)

Novella, Davide; Jacobsen, Benjamin; Weber, Peter K.

Nominally anhydrous minerals formed deep in the mantle and transported to the Earth’s surface contain tens to hundreds of ppm wt H 2O, providing evidence for the presence of dissolved water in the Earth’s interior. Even at these low concentrations, H 2O greatly affects the physico-chemical properties of mantle materials, governing planetary dynamics and evolution. The diffusion of hydrogen (H) controls the transport of H 2O in the Earth’s upper mantle, but is not fully understood for olivine ((Mg, Fe) 2SiO 4) the most abundant mineral in this region. Here we present new hydrogen self-diffusion coefficients in natural olivine singlemore » crystals that were determined at upper mantle conditions (2 GPa and 750–900 °C). Hydrogen self-diffusion is highly anisotropic, with values at 900 °C of 10 -10.9, 10 -12.8 and 10 -11.9 m 2/s along [100], [010] and [001] directions, respectively. Combined with the Nernst-Einstein relation, these diffusion results constrain the contribution of H to the electrical conductivity of olivine to be σH = 10 2.12S/m·C H2O·exp -187kJ/mol/(RT). Comparisons between the model presented in this study and magnetotelluric measurements suggest that plausible H 2O concentrations in the upper mantle (≤250 ppm wt) can account for high electrical conductivity values (10 -2–10 -1 S/m) observed in the asthenosphere.« less

Hydrogen self-diffusion in single crystal olivine and electrical conductivity of the Earth’s mantle

DOE PAGES

Novella, Davide; Jacobsen, Benjamin; Weber, Peter K.; ...

2017-07-13

Nominally anhydrous minerals formed deep in the mantle and transported to the Earth’s surface contain tens to hundreds of ppm wt H 2O, providing evidence for the presence of dissolved water in the Earth’s interior. Even at these low concentrations, H 2O greatly affects the physico-chemical properties of mantle materials, governing planetary dynamics and evolution. The diffusion of hydrogen (H) controls the transport of H 2O in the Earth’s upper mantle, but is not fully understood for olivine ((Mg, Fe) 2SiO 4) the most abundant mineral in this region. Here we present new hydrogen self-diffusion coefficients in natural olivine singlemore » crystals that were determined at upper mantle conditions (2 GPa and 750–900 °C). Hydrogen self-diffusion is highly anisotropic, with values at 900 °C of 10 -10.9, 10 -12.8 and 10 -11.9 m 2/s along [100], [010] and [001] directions, respectively. Combined with the Nernst-Einstein relation, these diffusion results constrain the contribution of H to the electrical conductivity of olivine to be σH = 10 2.12S/m·C H2O·exp -187kJ/mol/(RT). Comparisons between the model presented in this study and magnetotelluric measurements suggest that plausible H 2O concentrations in the upper mantle (≤250 ppm wt) can account for high electrical conductivity values (10 -2–10 -1 S/m) observed in the asthenosphere.« less

Hydrogen self-diffusion in single crystal olivine and electrical conductivity of the Earth's mantle.

PubMed

Novella, Davide; Jacobsen, Benjamin; Weber, Peter K; Tyburczy, James A; Ryerson, Frederick J; Du Frane, Wyatt L

2017-07-13

Nominally anhydrous minerals formed deep in the mantle and transported to the Earth's surface contain tens to hundreds of ppm wt H 2 O, providing evidence for the presence of dissolved water in the Earth's interior. Even at these low concentrations, H 2 O greatly affects the physico-chemical properties of mantle materials, governing planetary dynamics and evolution. The diffusion of hydrogen (H) controls the transport of H 2 O in the Earth's upper mantle, but is not fully understood for olivine ((Mg, Fe) 2 SiO 4 ) the most abundant mineral in this region. Here we present new hydrogen self-diffusion coefficients in natural olivine single crystals that were determined at upper mantle conditions (2 GPa and 750-900 °C). Hydrogen self-diffusion is highly anisotropic, with values at 900 °C of 10 -10.9 , 10 -12.8 and 10 -11.9 m 2 /s along [100], [010] and [001] directions, respectively. Combined with the Nernst-Einstein relation, these diffusion results constrain the contribution of H to the electrical conductivity of olivine to be σ H  = 10 2.12 S/m·C H2O ·exp -187kJ/mol/(RT) . Comparisons between the model presented in this study and magnetotelluric measurements suggest that plausible H 2 O concentrations in the upper mantle (≤250 ppm wt) can account for high electrical conductivity values (10 -2 -10 -1  S/m) observed in the asthenosphere.

Interpretation of the human skin biotribological behaviour after tape stripping

PubMed Central

Pailler-Mattei, C.; Guerret-Piécourt, C.; Zahouani, H.; Nicoli, S.

2011-01-01

The present study deals with the modification of the human skin biotribological behaviour after tape stripping. The tape-stripping procedure consists in the sequential application and removal of adhesive tapes on the skin surface in order to remove stratum corneum (SC) layers, which electrically charges the skin surface. The skin electric charges generated by tape stripping highly change the skin friction behaviour by increasing the adhesion component of the skin friction coefficient. It has been proposed to rewrite the friction adhesion component as the sum of two terms: the first classical adhesion term depending on the intrinsic shear strength, τ0, and the second term depending on the electric shear strength, τelec. The experimental results allowed to estimate a numerical value of the electric shear strength τelec. Moreover, a plan capacitor model with a dielectric material inside was used to modelize the experimental system. This physical model permitted to evaluate the friction electric force and the electric shear strength values to calculate the skin friction coefficient after the tape stripping. The comparison between the experimental and the theoretical value of the skin friction coefficient after the tape stripping has shown the importance of the electric charges on skin biotribological behaviour. The static electric charges produced by tape stripping on the skin surface are probably able to highly modify the interaction of formulations with the skin surface and their spreading properties. This phenomenon, generally overlooked, should be taken into consideration as it could be involved in alteration of drug absorption. PMID:21227961

Interpretation of the human skin biotribological behaviour after tape stripping.

PubMed

Pailler-Mattei, C; Guerret-Piécourt, C; Zahouani, H; Nicoli, S

2011-07-06

The present study deals with the modification of the human skin biotribological behaviour after tape stripping. The tape-stripping procedure consists in the sequential application and removal of adhesive tapes on the skin surface in order to remove stratum corneum (SC) layers, which electrically charges the skin surface. The skin electric charges generated by tape stripping highly change the skin friction behaviour by increasing the adhesion component of the skin friction coefficient. It has been proposed to rewrite the friction adhesion component as the sum of two terms: the first classical adhesion term depending on the intrinsic shear strength, τ(0), and the second term depending on the electric shear strength, τ(elec). The experimental results allowed to estimate a numerical value of the electric shear strength τ(elec). Moreover, a plan capacitor model with a dielectric material inside was used to modelize the experimental system. This physical model permitted to evaluate the friction electric force and the electric shear strength values to calculate the skin friction coefficient after the tape stripping. The comparison between the experimental and the theoretical value of the skin friction coefficient after the tape stripping has shown the importance of the electric charges on skin biotribological behaviour. The static electric charges produced by tape stripping on the skin surface are probably able to highly modify the interaction of formulations with the skin surface and their spreading properties. This phenomenon, generally overlooked, should be taken into consideration as it could be involved in alteration of drug absorption.

Measurement of CO 2, CO, SO 2, and NO emissions from coal-based thermal power plants in India

NASA Astrophysics Data System (ADS)

Chakraborty, N.; Mukherjee, I.; Santra, A. K.; Chowdhury, S.; Chakraborty, S.; Bhattacharya, S.; Mitra, A. P.; Sharma, C.

Measurements of CO 2 (direct GHG) and CO, SO 2, NO (indirect GHGs) were conducted on-line at some of the coal-based thermal power plants in India. The objective of the study was three-fold: to quantify the measured emissions in terms of emission coefficient per kg of coal and per kWh of electricity, to calculate the total possible emission from Indian thermal power plants, and subsequently to compare them with some previous studies. Instrument IMR 2800P Flue Gas Analyzer was used on-line to measure the emission rates of CO 2, CO, SO 2, and NO at 11 numbers of generating units of different ratings. Certain quality assurance (QA) and quality control (QC) techniques were also adopted to gather the data so as to avoid any ambiguity in subsequent data interpretation. For the betterment of data interpretation, the requisite statistical parameters (standard deviation and arithmetic mean) for the measured emissions have been also calculated. The emission coefficients determined for CO 2, CO, SO 2, and NO have been compared with their corresponding values as obtained in the studies conducted by other groups. The total emissions of CO 2, CO, SO 2, and NO calculated on the basis of the emission coefficients for the year 2003-2004 have been found to be 465.667, 1.583, 4.058, and 1.129 Tg, respectively.

Characterization and optimization of polycrystalline Si70%Ge30% for surface micromachined thermopiles in human body applications

NASA Astrophysics Data System (ADS)

Wang, Ziyang; Fiorini, Paolo; Leonov, Vladimir; Van Hoof, Chris

2009-09-01

This paper presents the material characterization methods, characterization results and the optimization scheme for polycrystalline Si70%Ge30% (poly-SiGe) from the perspective of its application in a surface micromachined thermopile. Due to its comparative advantages, such as lower thermal conductivity and ease of processing, over other materials, poly-SiGe is chosen to fabricate a surface micromachined thermopile and eventually a wearable thermoelectric generator (TEG) to be used on a human body. To enable optimal design of advanced thermocouple microstructures, poly-SiGe sample materials prepared by two different techniques, namely low-pressure chemical vapor deposition (LPCVD) with in situ doping and rapid thermal chemical vapor deposition (RTCVD) with ion implantation, have been characterized. Relevant material properties, including electrical resistivity, Seebeck coefficient, thermal conductivity and specific contact resistance, have been reported. For the determination of thermal conductivity, a novel surface-micromachined test structure based on the Seebeck effect is designed, fabricated and measured. Compared to the traditional test structures, it is more advantageous for sample materials with a relatively large Seebeck coefficient, such as poly-SiGe. Based on the characterization results, a further optimization scheme is suggested to allow independent respective optimization of the figure of merit and the specific contact resistance.

Study of the thermoelectric properties of lead selenide doped with boron, gallium, indium, or thallium.

PubMed

Zhang, Qian; Cao, Feng; Lukas, Kevin; Liu, Weishu; Esfarjani, Keivan; Opeil, Cyril; Broido, David; Parker, David; Singh, David J; Chen, Gang; Ren, Zhifeng

2012-10-24

Group IIIA elements (B, Ga, In, and Tl) have been doped into PbSe for enhancement of thermoelectric properties. The electrical conductivity, Seebeck coefficient, and thermal conductivity were systematically studied. Room-temperature Hall measurements showed an effective increase in the electron concentration upon both Ga and In doping and the hole concentration upon Tl doping to ~7 × 10(19) cm(-3). No resonant doping phenomenon was observed when PbSe was doped with B, Ga, or In. The highest room-temperature power factor ~2.5 × 10(-3) W m(-1) K(-2) was obtained for PbSe doped with 2 atom % B. However, the power factor in B-doped samples decreased with increasing temperature, opposite to the trend for the other dopants. A figure of merit (ZT) of ~1.2 at ~873 K was achieved in PbSe doped with 0.5 atom % Ga or In. With Tl doping, modification of the band structure around the Fermi level helped to increase the Seebeck coefficient, and the lattice thermal conductivity decreased, probably as a result of effective phonon scattering by both the heavy Tl(3+) ions and the increased grain boundary density after ball milling. The highest p-type ZT value was ~1.0 at ~723 K.

Preparation and Thermoelectric Properties of the Skutterudite-Related Phase Ru(0.5)Pd(0.5)Sb3

NASA Technical Reports Server (NTRS)

Caillat, T.; Kulleck, J.; Borshchevsky, A.; Fleurial, J.-P.

1996-01-01

A new skutterudite phase Ru(0.5)Pd(0.5)Sb3 was prepared. This new phase adds to a large number of already known materials with the skutterudite structure which have shown good potential for thermoelectric applications. Single phase, polycrystalline samples were prepared and characterized by x-ray analysis, electron probe microanalysis, density, sound velocity, thermal-expansion coefficient, and differential thermal analysis measurements. Ru(0.5)Pd(0.5)Sb3 has a cubic lattice, space group Im3 (T(sup 5, sub h)), with a = 9.298 A and decomposes at about 920 K. The Seebeck coefficient, the electrical resistivity, the Hall effect, and the thermal conductivity were measured on hot-pressed samples over a wide range of temperatures. Preliminary results show that Ru(0.5)Pd(0.5)Sb3 behaves as a heavily doped semiconductor with an estimated band gap of about 0.6 eV. The lattice thermal conductivity of Ru(0.5)Pd(0.5)Sb3 is substantially lower than that of the binary isostructural compounds CoSb3 and IrSb3. The unusually low thermal conductivity might be explained by additional hole and charge transfer phonon scattering in this material. The potential of this material for thermoelectric applications is discussed.

Structural, electronic, mechanical, and thermoelectric properties of a novel half Heusler compound HfPtPb

NASA Astrophysics Data System (ADS)

Kaur, Kulwinder; Rai, D. P.; Thapa, R. K.; Srivastava, Sunita

2017-07-01

We explore the structural, electronic, mechanical, and thermoelectric properties of a new half Heusler compound HfPtPb, an all metallic heavy element, recently proposed to be stable [Gautier et al., Nat. Chem. 7, 308 (2015)]. In this work, we employ density functional theory and semi-classical Boltzmann transport equations with constant relaxation time approximation. The mechanical properties, such as shear modulus, Young's modulus, elastic constants, Poisson's ratio, and shear anisotropy factor, have been investigated. The elastic and phonon properties reveal that this compound is mechanically and dynamically stable. Pugh's ratio and Frantsevich's ratio demonstrate its ductile behavior, and the shear anisotropic factor reveals the anisotropic nature of HfPtPb. The band structure predicts this compound to be a semiconductor with a band gap of 0.86 eV. The thermoelectric transport parameters, such as Seebeck coefficient, electrical conductivity, electronic thermal conductivity, and lattice thermal conductivity, have been calculated as a function of temperature. The highest value of Seebeck coefficient is obtained for n-type doping at an optimal carrier concentration of 1.0 × 1020 e/cm3. We predict the maximum value of figure of merit (0.25) at 1000 K. Our investigation suggests that this material is an n-type semiconductor.

Calculation of the octanol-water partition coefficient of armchair polyhex BN nanotubes

NASA Astrophysics Data System (ADS)

Mohammadinasab, E.; Pérez-Sánchez, H.; Goodarzi, M.

2017-12-01

A predictive model for determination partition coefficient (log P) of armchair polyhex BN nanotubes by using simple descriptors was built. The relationship between the octanol-water log P and quantum chemical descriptors, electric moments, and topological indices of some armchair polyhex BN nanotubes with various lengths and fixed circumference are represented. Based on density functional theory electric moments and physico-chemical properties of those nanotubes are calculated.

Electrical transport properties in Co nanocluster-assembled granular film

NASA Astrophysics Data System (ADS)

Zhang, Qin-Fu; Wang, Lai-Sen; Wang, Xiong-Zhi; Zheng, Hong-Fei; Liu, Xiang; Xie, Jia; Qiu, Yu-Long; Chen, Yuanzhi; Peng, Dong-Liang

2017-03-01

A Co nanocluster-assembled granular film with three-dimensional cross-connection paralleled conductive paths was fabricated by using the plasma-gas-condensation method in a vacuum environment. The temperature-dependent longitudinal resistivity and anomalous Hall effect of this new type granular film were systematically studied. The longitudinal resistivity of the Co nanocluster-assembled granular film first decreased and then increased with increasing measuring temperature, revealing a minimum value at certain temperature, T min . In a low temperature region ( T < T min ), the barrier between adjacent nanoclusters governed the electrical transport process, and the temperature coefficient of resistance (TCR) showed an insulator-type behavior. The thermal fluctuation-induced tunneling conduction progressively increased with increasing temperature, which led to a decrease in the longitudinal resistivity. In a high temperature region, the TCR showed a metallic-type behavior, which was primarily attributed to the temperature-dependent scattering. Different from the longitudinal resistivity behavior, the saturated anomalous Hall resistivity increased monotonically with increasing measuring temperature. The value of the anomalous Hall coefficient ( R S ) reached 2.3 × 10-9 (Ω cm)/G at 300 K, which was about three orders of magnitude larger than previously reported in blocky single-crystal Co [E. N. Kondorskii, Sov. Phys. JETP 38, 977 (1974)]. Interestingly, the scaling relation ( ρx y A ∝ ρx x γ ) between saturated anomalous Hall resistivity ( ρx y A ) and longitudinal resistivity ( ρ x x ) was divided into two regions by T min . However, after excluding the contribution of tunneling, the scaling relation followed the same rule. The corresponding physical mechanism was also proposed to explain these phenomena.

Thermomagnetic coolers based on Bi and Bi-Sb nanocomposites

NASA Astrophysics Data System (ADS)

Huber, Tito E.; Constant, Pierre

2001-02-01

Bulk Bi, a semimetal, and Bi-Sb, have the highest thermoelectric figure of merit Z at 100 K. The thermoelectric properties of these materials are strongly anisotropic. The best thermoelectric performance is observed when the electrical current flows along the trigonal axis. However, Bi single crystals are easily cleaved along the trigonal planes. This lack of strength has largely prevented the use of these materials in practical thermoelectric coolers. Composite technology offers the opportunity to increase the toughness of Bi and Bi-Sb. Also, microengineering Bi into composites may lead to a significant improvement in their thermoelectric performance, because of the reduction of phonon conductivity from phonon scattering at the grain boundaries and interfaces. It has been shown theoretically that quantum-wire structures have the potential to significantly improve Z over the bulk value. We have synthesized microwire composites and present measurements of its electrical conductivity and Seebeck coefficient that are very encouraging. The role that a tough thermoelectric cooler could have in extending the lifetime of a space system such as Space InfraRed Telescope Facility (SIRTF) is briefly discussed. .

Anomalous electrical conductivity of a gold thin film percolation system

NASA Astrophysics Data System (ADS)

Tao, Xiang-Ming; Ye, Gao-Xiang; Ye, Quan-Lin; Jin, Jin-Sheng; Lao, Yan-Feng; Jiao, Zheng-Kuan

2002-09-01

A gold thin film percolation system, deposited on a glass surface by the vapor deposition method, has been fabricated. By using the expansive and mobile properties of the silicone oil drop, a characteristic wedge-shaped film system with a slope of ~10-5 naturally forms during deposition. The electrical conductivity of the bandlike film, i.e., the uniform part of the wedge-shaped film with a fixed thickness, is measured with the four-probe method. It is found that the hopping and tunneling effects of the films are stronger than those of the other films. The dependence between the dc sheet resistance R0 and temperature T shows that the samples exhibit a negative coefficient dR0/dT below the temperature T*. According to our experiment, it is suggested that all the anomalous behaviors of the system should be related to the characteristic microstructure of the samples, which results from the immediate quench processes by the oil drop during deposition. The experiment indicates that the relaxation period of the microstructure of the samples may be longer than 30 min.

Thermoelectric generator based on composites obtained by sintering of detonation nanodiamonds

NASA Astrophysics Data System (ADS)

Eidelman, E. D.; Meilakhs, A. P.; Semak, B. V.; Shakhov, F. M.

2017-11-01

A model of a thermoelectric generator is proposed, in which composite materials obtained by sintering diamond nanoparticles are used as the main component. To increase the useful conversion of heat into electric current, it is proposed to use the effect of electron drag by ballistic phonons. To reduce the ineffective heat spread, it is proposed to use the effect of thermal resistance of the boundaries between the graphite-like and diamond-like phases of the composite. An experimental confirmation of the existence of an optimal volume ratio between graphite-like and diamond-like phases of the composite is predicted and obtained. The highest achieved value of thermoelectric coefficient in the actual structure is 80 µV K-1 (which means 20 times increase compared to that of composites not of the optimal structure), with a thermal conductivity of 50 W m-1 K-1. These results were obtained with constant electrical conductivity. The combined influence of these two effects in case of the ideal composite structure should result in an increase of the thermoelectric efficiency parameter by three orders of magnitude.

A facile fabrication of chemically converted graphene oxide thin films and their uses as absorber materials for solar cells

NASA Astrophysics Data System (ADS)

Adelifard, Mehdi; Darudi, Hosein

2016-07-01

There is a great interest in the use of graphene sheets in thin film solar cells with low-cost and good-optoelectronic properties. Here, the production of absorbent conductive reduced graphene oxide (RGO) thin films was investigated. RGO thin films were prepared from spray-coated graphene oxide (GO) layers at various substrate temperature followed by a simple hydrazine-reducing method. The structural, morphological, optical, and electrical characterizations of graphene oxide (GO) and RGO thin films were investigated. X-ray diffraction analysis showed a phase shift from GO to RGO due to hydrazine treatment, in agreement with the FTIR spectra of the layers. FESEM images clearly exhibited continuous films resulting from the overlap of graphene nanosheets. The produced low-cost thin films had high absorption coefficient up to 1.0 × 105 cm-1, electrical resistance as low as 0.9 kΩ/sq, and effective optical band gap of about 1.50 eV, close to the optimum value for solar conversion. The conductive absorbent properties of the reduced graphene oxide thin films would be useful to develop photovoltaic cells.

Atomically thick bismuth selenide freestanding single layers achieving enhanced thermoelectric energy harvesting.

PubMed

Sun, Yongfu; Cheng, Hao; Gao, Shan; Liu, Qinghua; Sun, Zhihu; Xiao, Chong; Wu, Changzheng; Wei, Shiqiang; Xie, Yi

2012-12-19

Thermoelectric materials can realize significant energy savings by generating electricity from untapped waste heat. However, the coupling of the thermoelectric parameters unfortunately limits their efficiency and practical applications. Here, a single-layer-based (SLB) composite fabricated from atomically thick single layers was proposed to optimize the thermoelectric parameters fully. Freestanding five-atom-thick Bi(2)Se(3) single layers were first synthesized via a scalable interaction/exfoliation strategy. As revealed by X-ray absorption fine structure spectroscopy and first-principles calculations, surface distortion gives them excellent structural stability and a much increased density of states, resulting in a 2-fold higher electrical conductivity relative to the bulk material. Also, the surface disorder and numerous interfaces in the Bi(2)Se(3) SLB composite allow for effective phonon scattering and decreased thermal conductivity, while the 2D electron gas and energy filtering effect increase the Seebeck coefficient, resulting in an 8-fold higher figure of merit (ZT) relative to the bulk material. This work develops a facile strategy for synthesizing atomically thick single layers and demonstrates their superior ability to optimize the thermoelectric energy harvesting.

Prediction on the charging demand for electric vehicles in Chengdu

NASA Astrophysics Data System (ADS)

yun, Cai; wanquan, Zhang; wei, You; pan, Mao

2018-03-01

The development of the electric vehicle charging station facilities speed directly affect the development of electric vehicle speed. And the charging demand of electric vehicles is one of the main factors influencing the electric vehicle charging facilities. The paper collected and collated car ownership in recent years, the use of elastic coefficient to predict Chengdu electric vehicle ownership, further modeling to give electric vehicle charging demand.

Skylight energy performance and design optimization

DOE Office of Scientific and Technical Information (OSTI.GOV)

Arasteh, D.; Johnson, R.; Selkowitz, S.

1984-02-01

Proper skylight utilization can significantly lower energy requirements and peak electrical loads for space conditioning and lighting in commercial buildings. In this study we systematically explore the energy effects of skylight systems in a prototypical office building and examine the savings from daylighting. The DOE-2.1B energy analysis computer program with its newly incorporated daylighting algorithms was used to generate more than 2000 parametric simulations for seven US climates. The parameters varied include skylight-to-roof ratio, shading coefficient, visible transmittance, skylight well light loss, electric lighting power density, roof heat transfer coefficient, and type of electric lighting control. For specific climates wemore » identify roof/skylight characteristics that minimize total energy or peak electrical load requirements.« less

Design and development of high efficiency 140W space TWT with graphite collector

NASA Astrophysics Data System (ADS)

Srivastava, V.; Purohit, G.; Sharma, R. K.; Sharma, S. M.; Bera, A.; Bhaskar, P. V.; Singh, R. R.; Prasad, K.; Kiran, V.

2008-05-01

4-stage graphite collector assembly has been designed and developed for a 140W Ku-band space TWT to achieve the collector efficiency more than 80%. The UHV compatible, high density, copper impregnated POCO graphite (DFP-1C) was used to fabricate the four collector electrodes of the 4-stage depressed collector. Copper impregnated graphite material is used for the collector electrodes because of its low secondary electron emission coefficient, high thermal and electrical conductivities, easy machining and brazing, low thermal expansion coefficient and low weight. The graphite material was characterized for the UHV compatibility. The collector electrodes were precisely fabricated by careful machining, and technology was developed for brazing of graphite electrodes with high voltage alumina insulators. Complete TWT with four-stage graphite collector was developed and 140W output power at gain more than 55 dB was achieved. The TWT was pumped from both the gun and the collector ends.

Stabilization of glucose-oxidase in the graphene paste for screen-printed glucose biosensor

NASA Astrophysics Data System (ADS)

Pepłowski, Andrzej; Janczak, Daniel; Jakubowska, Małgorzata

2015-09-01

Various methods and materials for enzyme stabilization within screen-printed graphene sensor were analyzed. Main goal was to develop technology allowing immediate printing of the biosensors in single printing process. Factors being considered were: toxicity of the materials used, ability of the material to be screen-printed (squeezed through the printing mesh) and temperatures required in the fabrication process. Performance of the examined sensors was measured using chemical amperometry method, then appropriate analysis of the measurements was conducted. The analysis results were then compared with the medical requirements. Parameters calculated were: correlation coefficient between concentration of the analyte and the measured electrical current (0.986) and variation coefficient for the particular concentrations of the analyte used as the calibration points. Variation of the measured values was significant only in ranges close to 0, decreasing for the concentrations of clinical importance. These outcomes justify further development of the graphene-based biosensors fabricated through printing techniques.

ProbeZT: Simulation of transport coefficients of molecular electronic junctions under environmental effects using Büttiker's probes

NASA Astrophysics Data System (ADS)

Korol, Roman; Kilgour, Michael; Segal, Dvira

2018-03-01

We present our in-house quantum transport package, ProbeZT. This program provides linear response coefficients: electrical and electronic thermal conductances, as well as the thermopower of molecular junctions in which electrons interact with the surrounding thermal environment. Calculations are performed based on the Büttiker probe method, which introduces decoherence, energy exchange and dissipation effects phenomenologically using virtual electrode terminals called probes. The program can realize different types of probes, each introducing various environmental effects, including elastic and inelastic scattering of electrons. The molecular system is described by an arbitrary tight-binding Hamiltonian, allowing the study of different geometries beyond simple one-dimensional wires. Applications of the program to study the thermoelectric performance of molecular junctions are illustrated. The program also has a built-in functionality to simulate electron transport in double-stranded DNA molecules based on a tight-binding (ladder) description of the junction.

Effect of on-site Coulomb interaction on electronic and transport properties of 100% spin polarized CoMnVAs

NASA Astrophysics Data System (ADS)

Bhat, Tahir Mohiuddin; Gupta, Dinesh C.

2017-08-01

The structural, electronic, magnetic and transport properties of a new quaternary Heusler alloy CoMnVAs have been investigated by employing generalized gradient approximation (GGA), modified Becke-Johnson (mBJ) and GGA with Hubbard U correction (GGA + U). The alloy is energetically more stable in ferromagnetic Y1 type structure. Elastic parameters reveal high anisotropy and ductile nature of the material. CoMnVAs shows half-metallic ferromagnet character with 100% spin polarization at Fermi level with band gap of 0.55 eV in the minority spin state. The alloy also possesses high electrical conductivity and Seebeck coefficients with 15 μVK-1 at room temperature, achieving a figure of merit of 0.65 at high temperatures. The high degree of ductility, 100% spin polarization and large Seebeck coefficient, makes it an attractive candidate to be used in spin voltage generators and thermoelectric materials.

Relationship between electrical properties and crystallization of indium oxide thin films using ex-situ grazing-incidence wide-angle x-ray scattering

DOE Office of Scientific and Technical Information (OSTI.GOV)

González, G. B.; Okasinski, J. S.; Buchholz, D. B.

Grazing-incidence, wide-angle x-ray scattering measurements were conducted on indium oxide thin films grown on silica substrates via pulsed laser deposition. Growth temperatures (T G) in this study ranged from -50 °C to 600 °C, in order to investigate the thermal effects on the film structure and its spatial homogeneity, as well as their relationship to electrical properties. Films grown below room temperature were amorphous, while films prepared at T G = 25 °C and above crystallized in the cubic bixbyite structure, and their crystalline fraction increased with deposition temperature. The electrical conductivity (σ) and electrical mobility (μ) were strongly enhancedmore » at low deposition temperatures. For T G = 25 °C and 50 °C, a strong < 100 > preferred orientation (texture) occurred, but it decreased as the deposition temperature, and consequential crystallinity, increased. Higher variations in texture coefficients and in lattice parameters were measured at the film surface compared to the interior of the film, indicating strong microstructural gradients. At low crystallinity, the in-plane lattice spacing expanded, while the out-of-plane spacing contracted, and those values merged at T G = 400 °C, where high μ was measured. This directional difference in lattice spacing, or deviatoric strain, was linear as a function of both deposition temperature and the degree of crystallinity. The crystalline sample with T G = 100 °C had the lowest mobility, as well as film diffraction peaks which split into doublets. The deviatoric strains from these doublet peaks differ by a factor of four, supporting the presence of both a microstructure and strain gradient in this film. More isotropic films exhibit larger l values, indicating that the microstructure directly correlates with electrical properties. Lastly, these results provide valuable insights that can help to improve the desirable properties of indium oxide, as well as other transparent conducting oxides.« less