Corrosion Properties of SAC305 Solder in Different Solution of HCl and NaCl

NASA Astrophysics Data System (ADS)

Nurwahida, M. Z.; Mukridz, M. M.; Ahmad, A. M.; Muhammad, F. M. N.

2018-03-01

Potentiodynamic polarization was used to studied the corrosion properties of SAC305 solder in different solution of 1.0 M HCl and 3.5 wt.% NaCl using the same scanning rate of 1.0 mV/s. The polarization curves indicated that corrosion in NaCl was less severe than in HCl solution based on corrosion current and passivation behavior obtained. Morphology and phases obtained after corrosion using SEM and XRD were analyzed. Microstructure analysis shows the present of compact corrosion product with presence of larger flake for polarization in NaCl compared to HCl. Phases present in XRD analysis confirmed the present of SnO and SnO2 corrosion product for sample from both solutions.

Corrosion of Tungsten Microelectrodes used in Neural Recording Applications

PubMed Central

Patrick, Erin; Orazem, Mark E.; Sanchez, Justin C.; Nishida, Toshikazu

2011-01-01

In neuroprosthetic applications, long-term electrode viability is necessary for robust recording of the activity of neural populations used for generating communication and control signals. The corrosion of tungsten microwire electrodes used for intracortical recording applications was analyzed in a controlled bench-top study and compared to the corrosion of tungsten microwires used in an in vivo study. Two electrolytes were investigated for the benchtop electrochemical analysis: 0.9% phosphate buffered saline (PBS) and 0.9% PBS containing 30 mM of hydrogen peroxide. The oxidation and reduction reactions responsible for corrosion were found by measurement of the open circuit potential and analysis of Pourbaix diagrams. Dissolution of tungsten to form the tungstic ion was found to be the corrosion mechanism. The corrosion rate was estimated from the polarization resistance, which was extrapolated from the electrochemical impedance spectroscopy data. The results show that tungsten microwires in an electrolyte of PBS have a corrosion rate of 300–700 µm/yr. The corrosion rate for tungsten microwires in an electrolyte containing PBS and 30 mM H2O2 is accelerated to 10,000–20,000 µm/yr. The corrosion rate was found to be controlled by the concentration of the reacting species in the cathodic reaction (e.g. O2 and H2O2). The in vivo corrosion rate, averaged over the duration of implantation, was estimated to be 100 µm/yr. The reduced in vivo corrosion rate as compared to the benchtop rate is attributed to decreased rate of oxygen diffusion caused by the presence of a biological film and a reduced concentration of available oxygen in the brain. PMID:21470563

Corrosion of tungsten microelectrodes used in neural recording applications.

PubMed

Patrick, Erin; Orazem, Mark E; Sanchez, Justin C; Nishida, Toshikazu

2011-06-15

In neuroprosthetic applications, long-term electrode viability is necessary for robust recording of the activity of neural populations used for generating communication and control signals. The corrosion of tungsten microwire electrodes used for intracortical recording applications was analyzed in a controlled bench-top study and compared to the corrosion of tungsten microwires used in an in vivo study. Two electrolytes were investigated for the bench-top electrochemical analysis: 0.9% phosphate buffered saline (PBS) and 0.9% PBS containing 30 mM of hydrogen peroxide. The oxidation and reduction reactions responsible for corrosion were found by measurement of the open circuit potential and analysis of Pourbaix diagrams. Dissolution of tungsten to form the tungstic ion was found to be the corrosion mechanism. The corrosion rate was estimated from the polarization resistance, which was extrapolated from the electrochemical impedance spectroscopy data. The results show that tungsten microwires in an electrolyte of PBS have a corrosion rate of 300-700 μm/yr. The corrosion rate for tungsten microwires in an electrolyte containing PBS and 30 mM H₂O₂ is accelerated to 10,000-20,000 μm/yr. The corrosion rate was found to be controlled by the concentration of the reacting species in the cathodic reaction (e.g. O₂ and H₂O₂). The in vivo corrosion rate, averaged over the duration of implantation, was estimated to be 100 μm/yr. The reduced in vivo corrosion rate as compared to the bench-top rate is attributed to decreased rate of oxygen diffusion caused by the presence of a biological film and a reduced concentration of available oxygen in the brain. Copyright © 2011 Elsevier B.V. All rights reserved.

Experimental investigation of microbiologically influenced corrosion of selected steels in sugarcane juice environment.

PubMed

Wesley, Sunil Bala; Maurya, Devendra Prasad; Goyal, Hari Sharan; Negi, Sangeeta

2013-12-01

In the current study, ferritic stainless grades AISI 439 and AISI 444 were investigated as possible construction materials for machinery and equipment in the cane-sugar industry. Their performance in corrosive cane-sugar juice environment was compared with the presently used low carbon steel AISI 1010 and austenitic stainless steel AISI 304. The Tafel plot electrochemical technique was used to evaluate general corrosion performance. Microbiologically influenced corrosion (MIC) behaviour in sugarcane juice environment was studied. Four microbial colonies were isolated from the biofilms on the metal coupon surfaces on the basis of their different morphology. These were characterized as Brevibacillus parabrevis, Bacillus azotoformans, Paenibacillus lautus and Micrococcus sp. The results of SEM micrographs showed that AISI 439 and AISI 304 grades had suffered maximum localized corrosion. MIC investigations revealed that AISI 444 steel had the best corrosion resistance among the tested materials. However from the Tafel plots it was evident that AISI 1010 had the least corrosion resistance and AISI 439 the best corrosion resistance.

Corrosion-Resistant Ti- xNb- xZr Alloys for Nitric Acid Applications in Spent Nuclear Fuel Reprocessing Plants

NASA Astrophysics Data System (ADS)

Manivasagam, Geetha; Anbarasan, V.; Kamachi Mudali, U.; Raj, Baldev

2011-09-01

This article reports the development, microstructure, and corrosion behavior of two new alloys such as Ti-4Nb-4Zr and Ti-2Nb-2Zr in boiling nitric acid environment. The corrosion test was carried out in the liquid, vapor, and condensate phases of 11.5 M nitric acid, and the potentiodynamic anodic polarization studies were performed at room temperature for both alloys. The samples subjected to three-phase corrosion testing were characterized using scanning electron microscopy (SEM) and energy-dispersive X-ray microanalysis (EDAX). As Ti-2Nb-2Zr alloy exhibited inferior corrosion behavior in comparison to Ti-4Nb-4Zr in all three phases, weldability and heat treatment studies were carried out only on Ti-4Nb-4Zr alloy. The weldability of the new alloy was evaluated using tungsten inert gas (TIG) welding processes, and the welded specimen was thereafter tested for its corrosion behavior in all three phases. The results of the present investigation revealed that the newly developed near alpha Ti-4Nb-4Zr alloy possessed superior corrosion resistance in all three phases and excellent weldability compared to conventional alloys used for nitric acid application in spent nuclear reprocessing plants. Further, the corrosion resistance of the beta heat-treated Ti-4Nb-4Zr alloy was superior when compared to the sample heat treated in the alpha + beta phase.

Studies on microstructure, mechanical and pitting corrosion behaviour of similar and dissimilar stainless steel gas tungsten arc welds

NASA Astrophysics Data System (ADS)

Mohammed, Raffi; Dilkush; Srinivasa Rao, K.; Madhusudhan Reddy, G.

2018-03-01

In the present study, an attempt has been made to weld dissimilar alloys of 5mm thick plates i.e., austenitic stainless steel (316L) and duplex stainless steel (2205) and compared with that of similar welds. Welds are made with conventional gas tungsten arc welding (GTAW) process with two different filler wires namely i.e., 309L and 2209. Welds were characterized using optical microscopy to observe the microstructural changes and correlate with mechanical properties using hardness, tensile and impact testing. Potentio-dynamic polarization studies were carried out to observe the pitting corrosion behaviour in different regions of the welds. Results of the present study established that change in filler wire composition resulted in microstructural variation in all the welds with different morphology of ferrite and austenite. Welds made with 2209 filler showed plate like widmanstatten austenite (WA) nucleated at grain boundaries. Compared to similar stainless steel welds inferior mechanical properties was observed in dissimilar stainless steel welds. Pitting corrosion resistance is observed to be low for dissimilar stainless steel welds when compared to similar stainless steel welds. Overall study showed that similar duplex stainless steel welds having favorable microstructure and resulted in better mechanical properties and corrosion resistance. Relatively dissimilar stainless steel welds made with 309L filler obtained optimum combination of mechanical properties and pitting corrosion resistance when compared to 2209 filler and is recommended for industrial practice.

The corrosion protection of several aluminum alloys by chromic acid and sulfuric acid anodizing

NASA Technical Reports Server (NTRS)

Danford, M. D.

1994-01-01

The corrosion protection afforded 7075-T6, 7075-T3, 6061-T6, and 2024-T3 aluminum alloys by chromic acid and sulfuric acid anodizing was examined using electrochemical techniques. From these studies, it is concluded that sulfuric acid anodizing provides superior corrosion protection compared to chromic acid anodizing.

Pitting corrosion inhibition of aluminum 2024 by Bacillus biofilms secreting polyaspartate or gamma-polyglutamate.

PubMed

Ornek, D; Jayaraman, A; Syrett, B C; Hsu, C-H; Mansfeld, F B; Wood, T K

2002-04-01

Pitting corrosion of aluminum 2024 in Luria Bertani medium was reduced by the secretion of anionic peptides by engineered and natural Bacillus biofilms and was studied in continuous reactors using electrochemical impedance spectroscopy. Compared to sterile controls, pitting was reduced dramatically by the presence of the biofilms. The secretion of a 20 amino acid polyaspartate peptide by an engineered Bacillus subtilis WB600/pBE92-Asp biofilm slightly reduced the corrosion rate of the passive aluminum alloy at pH 6.5; however, the secretion of gamma-polyglutamate by a Bacillus licheniformis biofilm reduced the corrosion rate by 90% (compared to the B. subtilis WB600/pBE92 biofilm which did not secrete polyaspartate or gamma-polyglutamate). The corrosion potential ( E(corr)) of aluminum 2024 was increased by about 0.15-0.44 V due to the formation of B. subtilis and B. licheniformis biofilms as compared to sterile controls. The increase of E(corr) and the observed prevention of pitting indicate that the pitting potential ( E(pit)) had increased. This result and the further decrease of corrosion rates for the passive aluminum alloy suggest that the rate of the anodic metal dissolution reaction was reduced by an inhibitor produced by the biofilms. Purified gamma-polyglutamate also decreased the corrosion rates of aluminum 2024.

The corrosion protection of 6061-T6 aluminum by a polyurethane-sealed anodized coat

NASA Technical Reports Server (NTRS)

Danford, M. D.

1990-01-01

The corrosion protection of 6061-T6 anodized aluminum afforded by a newly patented polyurethane seal was studied using the ac impedance technique. Values of the average corrosion rates over a 27-day exposure period in 3.5 percent NaCl solutions at pH 5.2 and pH 9.5 compared very favorably for Lockheed-prepared polyurethane-sealed and dichromate-sealed coats of the same thickness. Average corrosion rates for both specimens over the first 7 days of exposure compared well with those for a hard anodized, dichromate-sealed coat, but rose well above those for the hard anodized coat over the entire 27-day period. This is attributed both to the greater thickness of the hard anodized coat, and possibly to its inherently better corrosion protective capability.

Characterization of Encapsulated Corrosion Inhibitors Containing Microparticles for Environmentally Friendly Smart Coatings

NASA Technical Reports Server (NTRS)

Pearman, Benjamin Pieter; Calle, Luz M.

2015-01-01

This poster presents the results obtained from experiments designed to evaluate the release properties, as well as the corrosion inhibition effectiveness, of several encapsulated corrosion inhibitors. Microencapsulation has been used in the development of environmentally friendly multifunctional smart coatings. This technique enables the incorporation of autonomous corrosion detection, inhibition and self-healing functionalities into many commercially available coating systems. Select environmentally friendly corrosion inhibitors were encapsulated in organic and inorganic pH-sensitive microparticles and their release in basic solutions was studied. The release rate results showed that the encapsulation can be tailored from fast, for immediate corrosion protection, to slow, which will provide continued long-term corrosion protection. The incorporation of several corrosion inhibitor release profiles into a coating provides effective corrosion protection properties. To investigate the corrosion inhibition efficiency of the encapsulated inhibitors, electrochemical techniques were used to obtain corrosion potential, polarization curve and polarization resistance data. These measurements were performed using the free as well as the encapsulated inhibitors singly or in combinations. Results from these electrochemical tests will be compared to those obtained from weight loss and other accelerated corrosion experiments.

Study on electrochemical corrosion mechanism of steel foot of insulators for HVDC lines

NASA Astrophysics Data System (ADS)

Zheng, Weihua; Sun, Xiaoyu; Fan, Youping

2017-09-01

The main content of this paper is the mechanism of electrochemical corrosion of insulator steel foot in HVDC transmission line, and summarizes five commonly used artificial electrochemical corrosion accelerated test methods in the world. Various methods are analyzed and compared, and the simulation test of electrochemical corrosion of insulator steel feet is carried out by water jet method. The experimental results show that the experimental environment simulated by water jet method is close to the real environment. And the three suspension modes of insulators in the actual operation, the most serious corrosion of the V type suspension hardware, followed by the tension string suspension, and the linear string corrosion rate is the slowest.

Corrosion Behavior of Zirconium Treated Mild Steel with and Without Organic Coating: a Comparative Study

NASA Astrophysics Data System (ADS)

Ghanbari, Alireza; Attar, Mohammadreza Mohammadzade

2014-10-01

In this study, the anti-corrosion performance of phosphated and zirconium treated mild steel (ZTMS) with and without organic coating was evaluated using AC and DC electrochemical techniques. The topography and morphology of the zirconium treated samples were studied using atomic force microscopy (AFM) and field emission scanning electron microscope (FE-SEM) respectively. The results revealed that the anti-corrosion performance of the phosphate layer was superior to the zirconium conversion layer without an organic coating due to very low thickness and porous nature of the ZTMS. Additionally, the corrosion behavior of the organic coated substrates was substantially different. It was found that the corrosion protection performance of the phosphate steel and ZTMS with an organic coating is in the same order.

Ni-P/Zn-Ni compositionally modulated multilayer coatings - Part 2: Corrosion and protection mechanisms

NASA Astrophysics Data System (ADS)

Bahadormanesh, Behrouz; Ghorbani, Mohammad

2018-06-01

The Ni-P/Zn-Ni compositionally modulated multilayer coatings CMMCs were electrodeposited from a single bath by switching the deposition current density. The corrosion resistance of the deposits was studied and compared with that of monolayers of Ni-P and Zn-Ni alloys via Tafel polarization, EIS and salt spray tests. Characterization of corrosion products by means of EDS and XRD revealed more details from the corrosion mechanism of the monolayers and multilayers. The corrosion current density of Ni-P/Zn-Ni CMMCs were around one tenth of Zn-Ni monolayer. The CMMC with incomplete layers performed lower polarization resistance and higher corrosion current density compared to the CMMC with complete layers. The electrical circuit that was proposed for modeling the corrosion process based on the EIS spectrum, proved that layering reduces the porosity and consequently improves the barrier properties. Although, layering of Zn-Ni layers with Ni-P deposits increased the time to red rust in salt spray test, the time for white rust formation decreased. The corrosion mechanism of both Zn-Ni and Ni-P (containing small amount of Zn) was preferential dissolution of Zn and the corrosion products were comprised of mainly Zn hydroxychloride and Zn hydroxycarbonate. Also, Ni and P did not take part in the corrosion products. Based on the electrochemical character of the layers and the morphology of the corroded surface, the corrosion mechanism of multilayers was discussed.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Berke, N.S.; Dallaire, M.P.; Hicks, M.C.

Corrosion of steel in concrete is studied typically in uncracked concrete. In the field, however, concrete often has cracks that extend to the reinforcing steel. Electrochemical corrosion testing was performed in cracked concrete of two qualities. Results were compared to physical examination of the embedded reinforcement. Corrosion resistance improved significantly as the concrete properties and reinforcement cover approached that recommended in American Concrete Institute 318. Calcium nitrite additions to the concrete reduced corrosion significantly. Results indicated testing in cracked concrete should be performed in concrete representative of that specified in ACl 318.

Comparative Studies on microstructure, mechanical and corrosion behaviour of DMR 249A Steel and its welds

NASA Astrophysics Data System (ADS)

Mohammed, Raffi; Dilkush; Madhusudhan Reddy, G.; Srinivasa Rao, K.

2018-03-01

DMR249A Medium strength (low carbon) Low-alloy steels are used as structural components in naval applications due to its low cost and high availability. An attempt has been made to weld the DMR 249A steel plates of 8mm thickness using shielded metal arc welding (SMAW) and gas tungsten arc welding (GTAW). Welds were characterized for metallography to carry out the microstructural changes, mechanical properties were evaluated using vickers hardness tester and universal testing machine. Potentio-dynamic polarization tests were carried out to determine the pitting corrosion behaviour. Constant load type Stress corrosion cracking (SCC) testing was done to observe the cracking tendency of the joints in a 3.5%NaCl solution. Results of the present study established that SMA welds resulted in formation of relatively higher amount of martensite in ferrite matrix when compared to gas tungsten arc welding (GTAW). It is attributed to faster cooling rates achieved due to high thermal efficiency. Improved mechanical properties were observed for the SMA welds and are due to higher amount of martensite. Pitting corrosion and stress corrosion cracking resistance of SMA welds were poor when compared to GTA welds.

Comparative study on corrosion behaviour of Nitinol and stainless steel orthodontic wires in simulated saliva solution in presence of fluoride ions.

PubMed

Mirjalili, M; Momeni, M; Ebrahimi, N; Moayed, M H

2013-05-01

Localized corrosion and effects of pre-passivation treatment of Nitinol and SS304 orthodontic wires in simulated saliva solution in the presence and absence of fluoride ions were investigated by means of potentiodynamic and potentiostatic polarisations. Results revealed that Nitinol does not show pitting corrosion in saliva solution however, SS304 shows pitting corrosion. Meanwhile fluoride ion has deteriorative effect on pitting corrosion of Nitinol, while its effect on SS304 was marginally constructive. Additionally, the presence of artificial crevice has no effect on corrosion behaviour in the presence of fluoride. Pre-passivation treatment has positive influence on pitting corrosion of both alloys in the presence of F(-) ions. Copyright © 2012 Elsevier B.V. All rights reserved.

Comparative study of the corrosion behavior of peripheral stents in an accelerated corrosion model: experimental in vitro study of 28 metallic vascular endoprostheses

PubMed Central

Paprottka, Karolin J.; Paprottka, Philipp M.; Reiser, Maximilian F.; Waggershauser, Tobias

2015-01-01

PURPOSE Clinical cases of stent-fractures show that corrosion behavior might play a role in these fractures. Implanted in vivo, especially in combination with other implanted foreign materials, these metallic products are exposed to special conditions, which can cause a process of corrosion. Here, we aimed to test the corrosion potential of stents made of different materials in an in vitro setting. METHODS A total of 28 peripheral stents of different materials (nitinol, cobalt-chromium-nickel, tantalum, V4A) and surface treatments (electropolish, mechanical polish, no polish) were tested in vitro. Corrosion was accelerated by applying a constant voltage of 3.5 V and amperage of 1.16 mA in 0.9% NaCl. RESULTS Nitinol stents showed the lowest susceptibility to corrosion and the longest period without damage. The Memotherm II® (BARD Angiomed®) was the only stent that showed neither macroscopic nor microscopic damages. The worst performing material was cobalt-chromium-nickel, which showed corrosion damages about ten times earlier compared to nitinol. Considering the reasons for termination of the test, nitinol stents primarily showed length deficits, while V4A and tantalum stents showed fractures. Cobalt-chromium-nickel stents had multiple fractures or a complete lysis in equal proportions. When placed in direct contact, nitinol stents showed best corrosion resistance, regardless of what material they were combined with. In terms of polishing treatments, electropolished stents performed the best, mechanical-polished stents and those without polishing treatment followed. CONCLUSION The analysis of corrosion behavior may be useful to select the right stent fulfilling the individual needs of the patient within a large number of different stents. PMID:26268301

Natural analogues of nuclear waste glass corrosion.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Abrajano, T.A. Jr.; Ebert, W.L.; Luo, J.S.

1999-01-06

This report reviews and summarizes studies performed to characterize the products and processes involved in the corrosion of natural glasses. Studies are also reviewed and evaluated on how well the corrosion of natural glasses in natural environments serves as an analogue for the corrosion of high-level radioactive waste glasses in an engineered geologic disposal system. A wide range of natural and experimental corrosion studies has been performed on three major groups of natural glasses: tektite, obsidian, and basalt. Studies of the corrosion of natural glass attempt to characterize both the nature of alteration products and the reaction kinetics. Information availablemore » on natural glass was then compared to corresponding information on the corrosion of nuclear waste glasses, specifically to resolve two key questions: (1) whether one or more natural glasses behave similarly to nuclear waste glasses in laboratory tests, and (2) how these similarities can be used to support projections of the long-term corrosion of nuclear waste glasses. The corrosion behavior of basaltic glasses was most similar to that of nuclear waste glasses, but the corrosion of tektite and obsidian glasses involves certain processes that also occur during the corrosion of nuclear waste glasses. The reactions and processes that control basalt glass dissolution are similar to those that are important in nuclear waste glass dissolution. The key reaction of the overall corrosion mechanism is network hydrolysis, which eventually breaks down the glass network structure that remains after the initial ion-exchange and diffusion processes. This review also highlights some unresolved issues related to the application of an analogue approach to predicting long-term behavior of nuclear waste glass corrosion, such as discrepancies between experimental and field-based estimates of kinetic parameters for basaltic glasses.« less

Effect of free Cr content on corrosion behavior of 3Cr steels in a CO2 environment

NASA Astrophysics Data System (ADS)

Li, Wei; Xu, Lining; Qiao, Lijie; Li, Jinxu

2017-12-01

The corrosion behavior of 3Cr steels with three microstructures (martensite, bainite, combined ferrite and pearlite) in simulated oil field formation water with a CO2 partial pressure of 0.8 MPa was investigated. The relationships between Cr concentrations in corrosion scales and corrosion rates were studied. The precipitated phases that contained Cr were observed in steels of different microstructures, and free Cr content levels were compared. The results showed that steel with the martensite microstructure had the highest free Cr content, and thus had the highest corrosion resistance. The free Cr content of bainite steel was lower than that of martensite steel, and the corrosion rate of bainite steel was higher than that of martensite steel. Because large masses of Cr were combined in ferrite and pearlite steel, the corrosion rates of ferrite and pearlite steel were the highest. Free Cr content in steel affects its corrosion behavior greatly.

Corrosion Performance of Inconel 625 in High Sulphate Content

NASA Astrophysics Data System (ADS)

Ismail, Azzura

2016-05-01

Inconel 625 (UNS N06625) is a type of nickel-chromium-molybdenum alloy with excellent corrosion resistance in a wide range of corrosive media, being especially resistant to pitting and crevice corrosion. However, in aggressive environment, Inconel 625 will suffer corrosion attack like other metals. This research compared the corrosion performance of Inconel 625 when exposed to higher sulphate content compared to real seawater. The results reveal that Inconel 625 is excellent in resist the corrosion attack in seawater. However, at increasing temperature, the corrosion resistance of this metal decrease. The performance is same in seawater with high sulphate content at increasing temperature. It can be concluded that sulphate promote perforation on Inconel 625 and become aggressive agents that accelerate the corrosion attack.

Part I. Corrosion studies of continuous alumina fiber reinforced aluminum-matrix composites. Part II. Galvanic corrosion between continuous alumina fiber reinforced aluminum-matrix composites and 4340 steel

NASA Astrophysics Data System (ADS)

Zhu, Jun

Part I. The corrosion performance of continuous alumina fiber reinforced aluminum-matrix composites (CF-AMCs) was investigated in both the laboratory and field environments by comparing them with their respective monolithic matrix alloys, i.e., pure Al, A1-2wt%Cu T6, and Al 6061 T6. The corrosion initiation sites were identified by monitoring the changes in the surface morphology. Corrosion current densities and pH profiles at localized corrosion sites were measured using the scanning-vibrating electrode technique and the scanning ion-selective electrode technique, respectively. The corrosion damage of the materials immersed in various electrolytes, as well as those exposed in a humidity chamber and outdoor environments, was evaluated. Potentiodynamic polarization behavior was also studied. The corrosion initiation for the composites in 3.15 wt% NaCl occurred primarily around the Fe-rich intermetallic particles, which preferentially existed around the fiber/matrix interface on the composites. The corrosion initiation sites were also caused by physical damage (e.g., localized deformation) to the composite surface. At localized corrosion sites, the buildup of acidity was enhanced by the formation of micro-crevices resulting from fibers left in relief as the matrix corroded. The composites that were tested in exposure experiments exhibited higher corrosion rates than their monolithic alloys. The composites and their monolithic alloys were subjected to pitting corrosion when anodically polarized in the 3.15 wt% NaCl, while they passivated when anodically polarized in 0.5 M Na2SO4. The experimental results indicated that the composites exhibited inferior corrosion resistance compared to their monolithic matrix alloys. Part II. Galvanic corrosion studies were conducted on CF-AMCs coupled to 4340 steel since CF-AMCs have low density and excellent mechanical properties and are being considered as potential jacketing materials for reinforcing steel gun barrels. Coupled and uncoupled coupons were immersed in various electrolytes, exposed to a humidity chamber, and exposed at outdoor test sites. Results showed that the corrosion rates of the CF-AMCs increased, while those of the 4340 steel decreased after being coupled together, in most cases. Crevice corrosion was also observed in these exposure experiments. Zero resistance ammeter (ZRA) experiments were conducted to record the galvanic-corrosion rates and potentials of the couples. The CF-AMCs were found to serve as anodes, while the steel was cathodic, in most test conditions. Galvanic performance predicted by polarization experiments was in close agreement with the ZRA results. Key words. Aluminum, metal-matrix composites, alumina fiber, pitting corrosion, galvanic corrosion.

Effect of temperature on crack growth rates of stress corrosion cracks in metal alloys exposed to water

DOE Office of Scientific and Technical Information (OSTI.GOV)

Vogt, H.; Speidel, M.O.

1996-12-01

The effect of temperature on stress corrosion crack growth rates was studied using four commercial alloys: an Al-Mg-Zn alloy (7000-Series), an Al-Cu alloy (2000-Series), a Mg-rare earth alloy and a Zr 2.5% Nb alloy. Stress Corrosion crack growth rate data were obtained using fracture mechanic specimens which were tested in high purity water in the temperature range of {minus}10 C to 320 C, depending on the alloy. Attention was directed towards region 2 behavior, where the crack propagation rate is independent of stress intensity but sensitive to test temperature. The experimental activation energies of the different alloys were compared withmore » literature on rate-controlling steps in order to identify the possible stress corrosion cracking mechanisms. The results were also compared with the activation energies obtained from general corrosion and hydrogen diffusion experiments.« less

Metal roof corrosion related to volcanic ash deposition

NASA Astrophysics Data System (ADS)

Oze, C.; Cole, J. W.; Scott, A.; Wilson, T.; Wilson, G.; Gaw, S.; Hampton, S.; Doyle, C.; Li, Z.

2013-12-01

Volcanoes produce a wide range of hazards capable of leading to increased rates of corrosion to the built environment. Specifically, widely distributed volcanic ash derived from explosive volcanic eruptions creates both short- and long-term hazards to infrastructure including increased corrosion to exposed building materials such as metal roofing. Corrosion has been attributed to volcanic ash in several studies, but these studies are observational and are beset by limitations such as not accounting for pre-existing corrosion damage and/or other factors that may have also directly contributed to corrosion. Here, we evaluate the corrosive effects of volcanic ash, specifically focusing on the role of ash leachates, on a variety of metal roofing materials via weathering chamber experiments. Weathering chamber tests were carried out for up to 30 days using a synthetic ash dosed with an acidic solution to produce a leachate comparable to a real volcanic ash. Visual, chemical and surface analyses did not definitively identify significant corrosion in any of the test roofing metal samples. These experiments attempted to provide quantitative information with regards to the rates of corrosion of different types of metal roof materials. However, they demonstrate that no significant corrosion was macroscopically or microscopically present on any of the roofing surfaces despite the presence of corrosive salts after a duration of thirty days. These results suggest ash leachate-related corrosion is not a major or immediate concern in the short-term (< 1 month).

Comparative microstructural and corrosion development of VCrNiCoFeCu equiatomic multicomponent alloy produced by induction melting and spark plasma sintering

NASA Astrophysics Data System (ADS)

Fazakas, É.; Heczel, A.; Molnár, D.; Varga, B.; Zadorozhnyy, V.; Vida, Á.

2018-03-01

The present study focuses on the corrosion behavior of a single-phase FCC high entropy alloy (VCrNiCoFeCu) casted by two different methods: induction melting and spark plasma sintering. The corrosion resistance has been evaluated using immersion tests in 3.5% NaCl solution, the potentiodynamic polarization measurements and the results are compared how is dependent the corrosion rate as a function of the production methods. Our results show that induction melted sample is stable in salty environment. On the other hand, based on the changes of polarization curves, there must be an evolution of oxide films on the SPSed sample until reaching the stable oxide layer.

Microbial fouling and corrosion of carbon steel in deep anoxic alkaline groundwater.

PubMed

Rajala, Pauliina; Bomberg, Malin; Vepsäläinen, Mikko; Carpén, Leena

2017-02-01

Understanding the corrosion of carbon steel materials of low and intermediate level radioactive waste under repository conditions is crucial to ensure the safe storage of radioactive contaminated materials. The waste will be in contact with the concrete of repository silos and storage containers, and eventually with groundwater. In this study, the corrosion of carbon steel under repository conditions as well as the microbial community forming biofilm on the carbon steel samples, consisting of bacteria, archaea, and fungi, was studied over a period of three years in a groundwater environment with and without inserted concrete. The number of biofilm forming bacteria and archaea was 1,000-fold lower, with corrosion rates 620-times lower in the presence of concrete compared to the natural groundwater environment. However, localized corrosion was detected in the concrete-groundwater environment indicating the presence of local microenvironments where the conditions for pitting corrosion were favorable.

An innovative spraying setup to obtain uniform salt(s) mixture deposition to investigate hot corrosion

NASA Astrophysics Data System (ADS)

Mannava, Venkateswararao; Swaminathan, A. Vignesh; Kamaraj, M.; Kottada, Ravi Sankar

2016-02-01

A hot corrosion study via molten salt deposition and its interaction with creep/fatigue play a critical role in predicting the life of gas turbine engine components. To do systematic hot corrosion studies, deposition of molten salts on specimens should be uniform with good adherence. Thus, the present study describes an in-house developed spraying setup that produces uniform and reliable molten salt deposition in a repeatable fashion. The efficacy of the present method was illustrated by depositing 90 wt. % Na2SO4 + 5 wt. % NaCl + 5 wt. % NaV O3 salt mixture on hot corrosion coupons and on creep specimens, and also by comparing with other deposition methods.

Impact of Soil Composition and Electrochemistry on Corrosion of Rock-cut Slope Nets along Railway Lines in China.

PubMed

Chen, Jiao; Chen, Zhaoqiong; Ai, Yingwei; Xiao, Jingyao; Pan, Dandan; Li, Wei; Huang, Zhiyu; Wang, Yumei

2015-10-09

Taking the slope of Suiyu Railway to study, the research separately studied soil resistivity, soil electrochemistry (corrosion potential, oxidization reduction potential, electric potential gradient and pH), soil anions (total soluble salt, Cl(-), SO4(2-) and ), and soil nutrition (moisture content, organic matter, total nitrogen, alkali-hydrolysable nitrogen, available phosphorus, and available potassium) at different slope levels, and conducted corrosion grade evaluation on artificial soil according to its single index and comprehensive indexes. Compared with other factors, water has the biggest impact on the corrosion of slope protection net, followed by anion content. Total soluble salt has the moderate impact on the corrosion of slope protection net, and stray current has the moderate impact on the corrosion of mid-slope protection net. Comprehensive evaluation on the corrosive degree of soil samples indicates that the corrosion of upper slope is moderate, and the corrosion of mid-slope and lower slope is strong. Organic matter in soil is remarkably relevant to electric potential gradient. Available nitrogen, available potassium and available phosphorus are remarkably relevant to anions. The distribution of soil nutrient is indirectly relevant to slope type.

Impact of Soil Composition and Electrochemistry on Corrosion of Rock-cut Slope Nets along Railway Lines in China

PubMed Central

Chen, Jiao; Chen, Zhaoqiong; Ai, Yingwei; Xiao, Jingyao; Pan, Dandan; Li, Wei; Huang, Zhiyu; Wang, Yumei

2015-01-01

Taking the slope of Suiyu Railway to study, the research separately studied soil resistivity, soil electrochemistry (corrosion potential, oxidization reduction potential, electric potential gradient and pH), soil anions (total soluble salt, Cl−, SO42− and ), and soil nutrition (moisture content, organic matter, total nitrogen, alkali-hydrolysable nitrogen, available phosphorus, and available potassium) at different slope levels, and conducted corrosion grade evaluation on artificial soil according to its single index and comprehensive indexes. Compared with other factors, water has the biggest impact on the corrosion of slope protection net, followed by anion content. Total soluble salt has the moderate impact on the corrosion of slope protection net, and stray current has the moderate impact on the corrosion of mid-slope protection net. Comprehensive evaluation on the corrosive degree of soil samples indicates that the corrosion of upper slope is moderate, and the corrosion of mid-slope and lower slope is strong. Organic matter in soil is remarkably relevant to electric potential gradient. Available nitrogen, available potassium and available phosphorus are remarkably relevant to anions. The distribution of soil nutrient is indirectly relevant to slope type. PMID:26450811

A novel high-strength and highly corrosive biodegradable Fe-Pd alloy: Structural, mechanical and in vitro corrosion and cytotoxicity study.

PubMed

Čapek, Jaroslav; Msallamová, Šárka; Jablonská, Eva; Lipov, Jan; Vojtěch, Dalibor

2017-10-01

Recently, iron-based materials have been considered as candidates for the fabrication of biodegradable load-bearing implants. Alloying with palladium has been found to be a suitable approach to enhance the insufficient corrosion rate of iron-based alloys. In this work, we have extensively compared the microstructure, the mechanical and corrosion properties, and the cytotoxicity of an FePd2 (wt%) alloy prepared by three different routes - casting, mechanical alloying and spark plasma sintering (SPS), and mechanical alloying and the space holder technique (SHT). The properties of the FePd2 (wt%) were compared with pure Fe prepared in the same processes. The preparation route significantly influenced the material properties. Materials prepared by SPS possessed the highest values of mechanical properties (CYS~750-850MPa) and higher corrosion rates than the casted materials. Materials prepared by SHT contained approximately 60% porosity; therefore, their mechanical properties reached the lowest values, and they had the highest corrosion rates, approximately 0.7-1.2mm/a. Highly porous FePd2 was tested in vitro according to the ISO 10993-5 standard using L929 cells, and two-fold diluted extracts showed acceptable cytocompatibility. In general, alloying with Pd enhanced both mechanical properties and corrosion rates and did not decrease the cytocompatibility of the studied materials. Copyright © 2017 Elsevier B.V. All rights reserved.

Sulphonamides as corrosion inhibitor: Experimental and DFT studies

NASA Astrophysics Data System (ADS)

Obayes, Hasan R.; Al-Amiery, Ahmed A.; Alwan, Ghadah H.; Abdullah, Thamer Adnan; Kadhum, Abdul Amir H.; Mohamad, Abu Bakar

2017-06-01

Inhibitors are synthetic and natural molecules have various functional groups like double or triple bonds and heteroatoms; N, O or S, which permit adsorption onto the MS (metal surface). These inhibitors have the ability to adsorb onto the MS and block the active site that was reducing the corrosion rate. Inhibition efficiencies of the investigated compounds: Sulfacetamide (SAM), Sulfamerazine (SMR), Sulfapyridine (SPY) and Sulfathiazole (STI), as inhibitors in corrosive solution were evaluated based on weight loss technique. Nitro and Amino groups were chosen for the study of the substituted reaction of four corrosion inhibitor compounds: SAM, SMR, SPY and STI, theoretically utilizing the thickness capacities hypothesis DFT (density functions theory) method with the level [rB3LYP/6-311G(d,p)]. Our research demonstrated that the nitration of studied molecules lead to a diminishing in inhibition efficiencies, group lead to an increase in inhibition efficiency. Compared with corrosion inhibitor molecules these results gave a significant improvement in inhibition efficiency for corrosion inhibitor molecules.

Welding Thermal Simulation and Corrosion Study of X-70 Deep Sea Pipeline Steel

NASA Astrophysics Data System (ADS)

Zhang, Weipeng; Li, Zhuoran; Gao, Jixiang; Peng, Zhengwu

2017-12-01

Gleeble thermomechanical processing machine was used to simulate coarse grain heat affected zone (CGHAZ) of API X-70 thick wall pipeline steel used in deep sea. Microstructures and corresponding corrosion behavior of the simulated CGHAZs using different cooling rate were investigated and compared to the as-received material by scanning electron microscope and electrochemical experiments carried out in 3.5 wt. % NaCl solution. Results of this study show that the as-received samples exhibited a little bit higher corrosion resistance than the simulated CGHAZs. Among 3 sets of simulation experiments, the maximum corrosion tendency was exhibited at the t8/5 = 20 s with the most martensite-austensite (M-A) microstructure and highest corrosion potential was shown at the t8/5 = 60 s.

A Comparative Study of the Corrosion Behavior of Three Stainless Steels in an Eutectic (Li,Na,K)2CO3 Melt with and without (Na,K)Cl Additives at 973K in Air

NASA Astrophysics Data System (ADS)

Zeng, C. L.; Liu, Y.

2011-04-01

The ternary carbonate eutectic mixture of Li2CO3, K2CO3 and Na2CO3 as a heat transfer and storage medium has excellent thermophysical properties, but with high viscidity as compared with some other inorganic salts such as chlorides and nitrates. The addition of chlorides or fluorides to molten carbonates may improve their fluidity, but possibly making the melt become more corrosive. In this study, the corrosion behavior of type 304, 310 and 316 stainless steels in an eutectic (Li,Na,K)2CO3 melt with and without an eutectic mixture of NaCl and KCl at 973K in air have been examined. The experimental results indicated that 310 steel shows a much better corrosion resistance in molten carbonates than both 304 and 316 steels, due to the formation of a continuous LiCrO2 scale. The addition of chlorides to carbonates melt accelerated the corrosion of the steels, especially 310 steel, producing scales with more porosity.

Corrosion control when using secondary treated municipal wastewater as alternative makeup water for cooling tower systems.

PubMed

Hsieh, Ming-Kai; Li, Heng; Chien, Shih-Hsiang; Monnell, Jason D; Chowdhury, Indranil; Dzombak, David A; Vidic, Radisav D

2010-12-01

Secondary treated municipal wastewater is a promising alternative to fresh water as power plant cooling water system makeup water, especially in arid regions. Laboratory and field testing was conducted in this study to evaluate the corrosiveness of secondary treated municipal wastewater for various metals and metal alloys in cooling systems. Different corrosion control strategies were evaluated based on varied chemical treatment. Orthophosphate, which is abundant in secondary treated municipal wastewater, contributed to more than 80% precipitative removal of phosphorous-based corrosion inhibitors. Tolyltriazole worked effectively to reduce corrosion of copper (greater than 95% inhibition effectiveness). The corrosion rate of mild steel in the presence of free chlorine 1 mg/L (as Cl2) was approximately 50% higher than in the presence of monochloramine 1 mg/L (as Cl2), indicating that monochloramine is a less corrosive biocide than free chlorine. The scaling layers observed on the metal alloys contributed to corrosion inhibition, which could be seen by comparing the mild steel 21-day average corrosion rate with the last 5-day average corrosion rate, the latter being approximately 50% lower than the former.

Assessing corrosion of MSE wall reinforcement.

DOT National Transportation Integrated Search

2010-09-01

The primary objective of this study was to extract reinforcement coupons from select MSE walls and document the extent of corrosion. In doing this, a baseline has been established against which coupons extracted in the future can be compared. A secon...

Evaluation of several corrosion protective coating systems on aluminum

NASA Technical Reports Server (NTRS)

Higgins, R. H.

1981-01-01

A study of several protective coating systems for use on aluminum in seawater/seacoast environments was conducted to review the developments made on protective coatings since early in the Space Shuttle program and to perform comparative studies on these coatings to determine their effectiveness for providing corrosion protection during exposure to seawater/seacoast environments. Panels of 2219-T87 aluminum were coated with 21 different systems and exposed to a 5 percent salt spray for 4000 hr. Application properties, adhesion measurements, heat resistance and corrosion protection were evaluated. For comparative studies, the presently specified Bostik epoxy system used on the SRB structures was included. Results of these tests indicate four systems with outstanding performance and four additional systems with protection almost as good. These systems are based on a chromated pretreatment, a chromate epoxy primer, and a polyurethane topcoat. Consideration for one of these systems should be included for those applications where superior corrosion protection for aluminum surfaces is required.

A Comparative Study on Ni-Based Coatings Prepared by HVAF, HVOF, and APS Methods for Corrosion Protection Applications

NASA Astrophysics Data System (ADS)

Sadeghimeresht, E.; Markocsan, N.; Nylén, P.

2016-12-01

Selection of the thermal spray process is the most important step toward a proper coating solution for a given application as important coating characteristics such as adhesion and microstructure are highly dependent on it. In the present work, a process-microstructure-properties-performance correlation study was performed in order to figure out the main characteristics and corrosion performance of the coatings produced by different thermal spray techniques such as high-velocity air fuel (HVAF), high-velocity oxy fuel (HVOF), and atmospheric plasma spraying (APS). Previously optimized HVOF and APS process parameters were used to deposit Ni, NiCr, and NiAl coatings and compare with HVAF-sprayed coatings with randomly selected process parameters. As the HVAF process presented the best coating characteristics and corrosion behavior, few process parameters such as feed rate and standoff distance (SoD) were investigated to systematically optimize the HVAF coatings in terms of low porosity and high corrosion resistance. The Ni and NiAl coatings with lower porosity and better corrosion behavior were obtained at an average SoD of 300 mm and feed rate of 150 g/min. The NiCr coating sprayed at a SoD of 250 mm and feed rate of 75 g/min showed the highest corrosion resistance among all investigated samples.

A Comparative Study of Cyclic Oxidation and Sulfates-Induced Hot Corrosion Behavior of Arc-Sprayed Ni-Cr-Ti Coatings at Moderate Temperatures

NASA Astrophysics Data System (ADS)

Guo, Wenmin; Wu, Yuping; Zhang, Jianfeng; Hong, Sheng; Chen, Liyan; Qin, Yujiao

2015-06-01

The cyclic oxidation and sulfates-induced hot corrosion behaviors of a Ni-43Cr-0.3Ti arc-sprayed coating at 550-750 °C were characterized and compared in this study. In general, all the oxidation and hot corrosion kinetic curves of the coating followed a parabolic law, i.e., the weight of the specimens showed a rapid growth initially and then reached the gradual state. However, the initial stage of the hot corrosion process was approximately two times longer than that of the oxidation process, indicating a longer preparation time required for the formation of a protective scale in the former process. At 650 °C, the parabolic rate constant for the hot corrosion was 7.2 × 10-12 g2/(cm4·s), approximately 1.7 times higher than that for the oxidation at the same temperature. The lower parabolic rate constant for the oxidation was mainly attributed to the formation of a protective oxide scale on the surface of corroded specimens, which was composed of a mixture of NiO, Cr2O3, and NiCr2O4. However, as the liquid molten salts emerged during the hot corrosion, these protective oxides would be dissolved and the coating was corrupted acceleratedly.

Ultimate strength performance of tankers associated with industry corrosion addition practices

NASA Astrophysics Data System (ADS)

Kim, Do Kyun; Kim, Han Byul; Zhang, Xiaoming; Li, Chen Guang; Paik, Jeom Kee

2014-09-01

In the ship and offshore structure design, age-related problems such as corrosion damage, local denting, and fatigue damage are important factors to be considered in building a reliable structure as they have a significant influence on the residual structural capacity. In shipping, corrosion addition methods are widely adopted in structural design to prevent structural capacity degradation. The present study focuses on the historical trend of corrosion addition rules for ship structural design and investigates their effects on the ultimate strength performance such as hull girder and stiffened panel of double hull oil tankers. Three types of rules based on corrosion addition models, namely historic corrosion rules (pre-CSR), Common Structural Rules (CSR), and harmonised Common Structural Rules (CSRH) are considered and compared with two other corrosion models namely UGS model, suggested by the Union of Greek Shipowners (UGS), and Time-Dependent Corrosion Wastage Model (TDCWM). To identify the general trend in the effects of corrosion damage on the ultimate longitudinal strength performance, the corrosion addition rules are applied to four representative sizes of double hull oil tankers namely Panamax, Aframax, Suezmax, and VLCC. The results are helpful in understanding the trend of corrosion additions for tanker structures

Research on A3 steel corrosion behavior of basic magnesium sulfate cement

NASA Astrophysics Data System (ADS)

Xing, Sainan; Wu, Chengyou; Yu, Hongfa; Jiang, Ningshan; Zhang, Wuyu

2017-11-01

In this paper, Tafel polarization technique is used to study the corrosion behavior of A3 steel basic magnesium sulfate, and then analyzing the ratio of raw materials cement, nitrites rust inhibitor and wet-dry cycle of basic magnesium sulfate corrosion of reinforced influence, and the steel corrosion behavior of basic magnesium sulfate compared with magnesium oxychloride cement and Portland cement. The results show that: the higher MgO/MgSO4 mole ratio will reduce the corrosion rate of steel; Too high and too low H2O/MgSO4 mole ratio may speed up the reinforcement corrosion effect; Adding a small amount of nitrite rust and corrosion inhibitor, not only can obviously reduce the alkali type magnesium sulfate in the early hydration of cement steel bar corrosion rate, but also can significantly reduce dry-wet circulation under the action of alkali type magnesium sulfate cement corrosion of reinforcement effect. Basic magnesium sulfate cement has excellent ability to protect reinforced, its long-term corrosion of reinforcement effect and was equal to that of Portland cement. Basic magnesium sulfate corrosion of reinforced is far below the level in the MOC in the case.

Comparative Studies on Microstructure, Mechanical and Pitting Corrosion of Post Weld Heat Treated IN718 Superalloy GTA and EB Welds

NASA Astrophysics Data System (ADS)

Dilkush; Mohammed, Raffi; Madhusudhan Reddy, G.; Srinivasa Rao, K.

2018-03-01

In the present study, an attempt has been made to weld Inconel 718 nickel-base superalloy (IN718 alloy) using gas tungsten arc welding (GTAW) and electron beam welding (EBW) processes. Both the weldments were subjected to post-weld heat treatment condition as follows -980°C / 20 min followed by direct aging condition (DA) as 720°C/8 h/FC followed by 620°C/8 h/AC. The GTA and EB welds of IN718 alloy were compared in two conditions as-received and 980STA conditions. Welds were characterized to observe mechanical properties, pitting corrosion resistance by correlating with observed microstructures. The rate of higher cooling ranges, the fusion zone of EBW exhibited discrete and relative finer lave phases whereas the higher niobium existed laves with coarser structure were observed in GTAW. The significant dissolution of laves were observed at 980STA of EBW. Due to these effects, the EBW of IN718 alloy showed the higher mechanical properties than GTAW. The electrochemical potentiostatic etch test was carried out in 3.5wt% sodium chloride (NaCl) solution to study the pitting corrosion behaviour of the welds. Results of the present investigation established that mechanical properties and pitting corrosion behaviour are significantly better in post weld heat treated condition. The comparative studies showed that the better combination of mechanical properties and pitting corrosion resistance were obtained in 980STA condition of EBW than GTAW.

Influence of silica nanospheres on corrosion behavior of magnesium matrix syntactic foam

NASA Astrophysics Data System (ADS)

Qureshi, W.; Kannan, S.; Vincent, S.; Eddine, N. N.; Muhammed, A.; Gupta, M.; Karthikeyan, R.; Badari, V.

2018-04-01

Over the years, the development of Magnesium alloys as biodegradable implants has seen significant advancements. Magnesium based materials tend to provide numerous advantages in the field of biomedical implants over existing materials such as titanium or stainless steel. The present research focuses on corrosive behavior of Magnesium reinforced with different volume percentages of Hollow Silica Nano Spheres (HSNS). These behaviors were tested in two different simulated body fluids (SBF) namely, Hank’s Buffered Saline Solution (HBSS) and Phosphate Buffered Solution (PBS). This corrosion study was done using the method of electrochemical polarization with a three-electrode configuration. Comparative studies were established by testing pure Mg which provided critical information on the effects of the reinforcing material. The HSNS reinforced Mg displayed desirable characteristics after corrosion experiments; increased corrosion resistance was witnessed with higher volume percentage of HSNS.

Mechanical Behavior of Stainless Steel Fiber-Reinforced Composites Exposed to Accelerated Corrosion

PubMed Central

O’Brien, Caitlin; McBride, Amanda; E. Zaghi, Arash; Burke, Kelly A.; Hill, Alex

2017-01-01

Recent advancements in metal fibers have introduced a promising new type of stainless steel fiber with high stiffness, high failure strain, and a thickness < 100 μm (<0.00394 in.) that can be utilized in a steel fiber-reinforced polymer. However, stainless steel is known to be susceptible to pitting corrosion. The main goal of this study is to compare the impact of corrosion on the mechanical properties of steel fiber-reinforced composites with those of conventional types of stainless steel. By providing experimental evidences, this study may promote the application of steel fiber-reinforced composite as a viable alternative to conventional metals. Samples of steel fiber-reinforced polymer and four different types of stainless steel were subjected to 144 and 288 h of corrosion in ferric chloride solution to simulate accelerated corrosion conditions. The weight losses due to corrosion were recorded. The corroded and control samples were tested under monotonic tensile loading to measure the ultimate stresses and strains. The effect of corrosion on the mechanical properties of the different materials was evaluated. The digital image correlation (DIC) technique was used to investigate the failure mechanism of the corrosion-damaged specimens. Overall, steel fiber-reinforced composites had the greatest corrosion resistance. PMID:28773132

Review and study of physics driven pitting corrosion modeling in 2024-T3 aluminum alloys

NASA Astrophysics Data System (ADS)

Yu, Lingyu; Jata, Kumar V.

2015-04-01

Material degradation due to corrosion and corrosion fatigue has been recognized to significantly affect the airworthiness of civilian and military aircraft, especially for the current fleet of airplanes that have served beyond their initial design life. The ability to predict the corrosion damage development in aircraft components and structures, therefore, is of great importance in managing timely maintenance for the aging aircraft vehicles and in assisting the design of new ones. The assessment of aircraft corrosion and its influence on fatigue life relies on appropriate quantitative models that can evaluate the initiation of the corrosion as well as the accumulation during the period of operation. Beyond the aircraft regime, corrosion has also affected the maintenance, safety and reliability of other systems such as nuclear power systems, steam and gas turbines, marine structures and so on. In the work presented in this paper, we reviewed and studied several physics based pitting corrosion models that have been reported in the literature. The classic work of particle induced pitting corrosion by Wei and Harlow is reviewed in detail. Two types of modeling, a power law based simplified model and a microstructure based model, are compared for 2024-T3 alloy. Data from literatures are used as model inputs. The paper ends with conclusions and recommendations for future work.

Wear and corrosion behaviour of tungsten carbide based coatings with different metallic binder

NASA Astrophysics Data System (ADS)

Kamdi, Z.; Apandi, M. N. M.; Ibrahim, M. D.

2017-12-01

Tungsten carbide based coating has been well known as wear and corrosion resistance materials. However, less study is done on comparing the coating with different binder. Thus, in this work the wear and corrosion behaviour of high velocity oxy-fuel (HVOF) coatings, namely (i) tungsten carbide cobalt and (ii) tungsten carbide nickel will be evaluated. Both coatings were characterised using X-ray Diffractometer (XRD) and Scanning Electron Microscope (SEM). The wear behaviour has been examined using the modified grinder machine by weight loss measurement. Two types of abrasive have been used that include 3 g by weight alumina and silica. While for the corrosion behaviour, it is monitored by three electrodes of electrochemical test and immersion test for 30 days in an acidic environment. The electrolyte used was 0.5 M sulphuric acids (H2SO4). It was found that the cobalt binder shows higher wear resistance compares to the nickel binder for both slurry types. The harder alumina compared to silica results in higher wear rate with removal of carbide and binder is about the same rate. For silica abrasive, due to slightly lower hardness compared to the carbide, the wear is dominated by binder removal followed by carbide detachment. For corrosion, the nickel binder shows four times higher wear resistance compared to the cobalt binder as expected due to its natural behaviour. These finding demonstrate that the selection of coating to be used in different application in this case, wear and corrosion shall be chosen carefully to maximize the usage of the coating.

Comparative Study on Corrosion Protection of Reinforcing Steel by Using Amino Alcohol and Lithium Nitrite Inhibitors

PubMed Central

Lee, Han-Seung; Ryu, Hwa-Sung; Park, Won-Jun; Ismail, Mohamed A.

2015-01-01

In this study, the ability of lithium nitrite and amino alcohol inhibitors to provide corrosion protection to reinforcing steel was investigated. Two types of specimens—reinforcing steel and a reinforced concrete prism that were exposed to chloride ion levels resembling the chloride attack environment—were prepared. An autoclave accelerated corrosion test was then conducted. The variables tested included the chloride-ion concentration and molar ratios of anti-corrosion ingredients in a CaOH2-saturated aqueous solution that simulated a cement-pore solution. A concentration of 25% was used for the lithium nitrite inhibitor LiNO2, and an 80% solution of dimethyl ethanolamine ((CH3)2NCH2CH2OH, hereinafter DMEA) was used for the amino alcohol inhibitor. The test results indicated that the lithium nitrite inhibitor displayed anti-corrosion properties at a molar ratio of inhibitor of ≥0.6; the amino alcohol inhibitor also displayed anti-corrosion properties at molar ratios of inhibitor greater than approximately 0.3. PMID:28787936

Isolation of a sulfide-producing bacterial consortium from cooling-tower water: Evaluation of corrosive effects on galvanized steel.

PubMed

Ilhan-Sungur, Esra; Ozuolmez, Derya; Çotuk, Ayşın; Cansever, Nurhan; Muyzer, Gerard

2017-02-01

Sulfidogenic Clostridia and sulfate reducing bacteria (SRB) often cohabit in nature. The presence of these microorganisms can cause microbially influenced corrosion (MIC) of materials in different ways. To investigate this aspect, bacteria were isolated from cooling tower water and used in corrosion tests of galvanized steel. The identity of the isolates was determined by comparative sequence analysis of PCR-amplified 16S rDNA gene fragments, separated by denaturing gradient gel electrophoresis (DGGE). This analysis showed that, in spite of the isolation process, colonies were not pure and consisted of a mixture of bacteria affiliated with Desulfosporosinus meridiei and Clostridium sp. To evaluate the corrosive effect, galvanized steel coupons were incubated with a mixed culture for 4, 8, 24, 72, 96, 168, 360 and 744 h, along with a control set in sterile culture medium only. The corrosion rate was determined by weight loss, and biofilm formation and corroded surfaces were observed by scanning electron microscopy (SEM). Although the sulfide-producing bacterial consortium led to a slight increase in the corrosion of galvanized steel coupons, when compared to the previous studies it can be said that Clostridium sp. can reduce the corrosive effect of the Desulfosporosinus sp. strain. Copyright © 2016 Elsevier Ltd. All rights reserved.

Cr-Free Metallic-Ceramic Coatings

DTIC Science & Technology

2014-11-01

Comparable to Aluminum-Chromate/ Phosphate Humidity Resistance Galvanic Corrosion Resistance Nov. 2014 ASETSDefense 2014, Fort Myer, VA...Aluminum-Silicate Comparable to Aluminum-Chromate/ Phosphate  Humidity, Galvanic Corrosion , Heat/Salt Resistance  Adhesion & Compatibility...WP-TR-2007-4069, Sept. 2006 Sealed Aluminum-Silicate Not Comparable to Sealed Aluminum-Chromate/ Phosphate in PEWG Evaluation  Corrosion

Lamb-Wave-Based Tomographic Imaging Techniques for Hole-Edge Corrosion Monitoring in Plate Structures

PubMed Central

Wang, Dengjiang; Zhang, Weifang; Wang, Xiangyu; Sun, Bo

2016-01-01

This study presents a novel monitoring method for hole-edge corrosion damage in plate structures based on Lamb wave tomographic imaging techniques. An experimental procedure with a cross-hole layout using 16 piezoelectric transducers (PZTs) was designed. The A0 mode of the Lamb wave was selected, which is sensitive to thickness-loss damage. The iterative algebraic reconstruction technique (ART) method was used to locate and quantify the corrosion damage at the edge of the hole. Hydrofluoric acid with a concentration of 20% was used to corrode the specimen artificially. To estimate the effectiveness of the proposed method, the real corrosion damage was compared with the predicted corrosion damage based on the tomographic method. The results show that the Lamb-wave-based tomographic method can be used to monitor the hole-edge corrosion damage accurately. PMID:28774041

Effect of thermal oxidation on corrosion and corrosion-wear behaviour of a Ti-6Al-4V alloy.

PubMed

Güleryüz, Hasan; Cimenoğlu, Hüseyin

2004-07-01

In this study, comparative investigation of thermal oxidation treatment for Ti-6Al-4V was carried out to determine the optimum oxidation conditions for further evaluation of corrosion-wear performance. Characterization of modified surface layers was made by means of microscopic examinations, hardness measurements and X-ray diffraction analysis. Optimum oxidation condition was determined according to the results of accelerated corrosion tests made in 5m HCl solution The examined Ti-6Al-4V alloy exhibited excellent resistance to corrosion after oxidation at 600 degrees C for 60 h. This oxidation condition achieved 25 times higher wear resistance than the untreated alloy during reciprocating wear test conducted in a 0.9% NaCl solution.

Comparative study on the corrosion behavior of the cold rolled and hot rolled low-alloy steels containing copper and antimony in flue gas desulfurization environment

NASA Astrophysics Data System (ADS)

Park, S. A.; Kim, J. G.; He, Y. S.; Shin, K. S.; Yoon, J. B.

2014-12-01

The correlation between the corrosion and microstructual characteristics of cold rolled and hot rolled low-alloy steels containing copper and antimony was established. The corrosion behavior of the specimens used in flue gas desulfurization systems was examined by electrochemical and weight loss measurements in an aggressive solution of 16.9 vol % H2SO4 + 0.35 vol % HCl at 60°C, pH 0.3. It has been shown that the corrosion rate of hot rolled steel is lower than that of cold rolled steel. The corrosion rate of cold rolled steel was increased by grain refinement, inclusion formation, and preferred grain orientation.

Corrosion Behaviour of Sn-based Lead-Free Solders in Acidic Solution

NASA Astrophysics Data System (ADS)

Nordarina, J.; Mohd, H. Z.; Ahmad, A. M.; Muhammad, F. M. N.

2018-03-01

The corrosion properties of Sn-9(5Al-Zn), Sn-Cu and SAC305 were studied via potentiodynamic polarization method in an acidic solution of 1 M hydrochloric acid (HCl). Sn-9(5Al-Zn) produced different polarization profile compared with Sn-Cu and SAC305. The morphological analysis showed that small, deep grooves shaped of corrosion product formed on top of Sn-9(5Al-Zn) solder while two distinctive structures of closely packed and loosely packed corrosion product formed on top of Sn-Cu and SAC305 solder alloys. Phase analysis revealed the formations of various corrosion products such as SnO and SnO2 mainly dominant on surface of solder alloys after potentiodynamic polarization in 1 M hydrochloric acid (HCl).

Investigating inhibition of microbes inducing microbiologically-influenced-corrosion by Tectona grandis based Fe-nanoparticle material

NASA Astrophysics Data System (ADS)

Okeniyi, Joshua Olusegun; Omotosho, Olugbenga Adeshola; Inyang, Michael Anietie; Okeniyi, Elizabeth Toyin; Nwaokorie, Ikechi Thaddeus; Adidi, Emmanuel Amanogho; Owoeye, Taiwo Felicia; Nwakudu, Kelechukwu Chinedu; Akinlabu, Deborah Kehinde; Gabriel, Olanrewaju Oyewale; Taiwo, Olugbenga Samson; Awotoye, Olufisayo Adebola

2017-02-01

In this paper, inhibition of microbes inducing microbiologically-influenced-corrosion (MIC) of metals by Tectona grandis based Fe (iron) Nanoparticle material was investigated. For this, extract was obtained from the leaf of Tectona grandis and this was employed as precursor for synthesizing the Fe-nanoparticle material. From this, the synthesized plant extract based nanoparticle material was characterized using scanning electron microscopy and energy dispersive spectroscopy (SEM+EDS) instrument. The developed Fe bio-nanoparticle material was then employed for sensitivity and/or resistance study application against different strains of microbes that are known to induce microbiologically-influenced-corrosion, in metallic materials, and for this, microbial growth inhibition effect was compared with that from a commercial antibiotic employed as control. Results showed that the Tectona grandis based Fe-nanoparticle exhibited good inhibition effects on the growth of many of the MIC inducing microbes investigated. Sensitivity measures of zone of inhibition against the growth of MIC inducing microbial strains either outperformed or compares well with that obtained from the commercial antibiotic control, in the study. These results indicate positive prospect on the suitability of Fe bio-nanoparticle for corrosion inhibition applications for the protection of metals against microbiological corrosion influencing environment.

Effect of CeO2 on Cyclic Hot-Corrosion Behavior of Detonation-Gun Sprayed Cr3C2-NiCr Coatings on Ni-Based Superalloy

NASA Astrophysics Data System (ADS)

Saladi, Sekar; Menghani, Jyoti; Prakash, Satya

2015-03-01

The hot-corrosion behavior of detonation-gun sprayed Cr3C2-NiCr coatings with and without 0.4 wt.% CeO2 additive on Ni-based superalloy inconel-718 is comparatively discussed in the present study. Hot-corrosion studies were carried out at 900 °C for 100 cycles in Na2SO4-60%V2O5 molten salt environment under cyclic heating and cooling conditions on bare and coated superalloys. The thermo-gravimetric technique was used to establish kinetics of hot-corrosion. XRD, FESEM/EDAX, and EDX mapping techniques were used to analyze the corrosion products of bare and coated samples. The results indicate that Cr3C2-NiCr-CeO2-coated superalloy showed better hot-corrosion resistance as compared to bare and Cr3C2-NiCr-coated superalloys. The addition of CeO2 has improved micro-hardness, porosity, and surface roughness values of Cr3C2-NiCr-CeO2 coating. The overall weight gain and parabolic rate constant of Cr3C2-NiCr-CeO2-coated superalloy were found to be lowest in the present study signifying that the addition of CeO2 in Cr3C2-NiCr powder has contributed to the development of adherent and dense oxide scale on the coating at elevated temperature.

Microstructure and Corrosion Characterization of Squeeze Cast AM50 Magnesium Alloys

NASA Astrophysics Data System (ADS)

Sachdeva, Deepika; Tiwari, Shashank; Sundarraj, Suresh; Luo, Alan A.

2010-12-01

Squeeze casting of magnesium alloys potentially can be used in lightweight chassis components such as control arms and knuckles. This study documents the microstructural analysis and corrosion behavior of AM50 alloys squeeze cast at different pressures between 40 and 120 MPa and compares them with high-pressure die cast (HPDC) AM50 alloy castings and an AM50 squeeze cast prototype control arm. Although the corrosion rates of the squeeze cast samples are slightly higher than those observed for the HPDC AM50 alloy, the former does produce virtually porosity-free castings that are required for structural applications like control arms and wheels. This outcome is extremely encouraging as it provides an opportunity for additional alloy and process development by squeeze casting that has remained relatively unexplored for magnesium alloys compared with aluminum. Among the microstructural parameters analyzed, it seems that the β-phase interfacial area, indicating a greater degree of β network, leads to a lower corrosion rate. Weight loss was the better method for determining corrosion behavior in these alloys that contain a large fraction of second phase, which can cause perturbations to an overall uniform surface corrosion behavior.

Synthesis and corrosion inhibition application of NATN on mild steel surface in acidic media complemented with DFT studies

NASA Astrophysics Data System (ADS)

Al-Baghdadi, Shaimaa B.; Hashim, Fanar G.; Salam, Ahmed Q.; Abed, Talib K.; Gaaz, Tayser Sumer; Al-Amiery, Ahmed A.; Kadhum, Abdul Amir H.; Reda, Khalid S.; Ahmed, Wahab K.

2018-03-01

The corrosion inhibition effectiveness of thiosemicarbazide compound, namely 3-nitro-5-(2-amino-1,3,4-thiadiazolyl)nitrobenzene (NATN), on mild steel in 1 M hydrochloric acid media has been investigated by weight loss technique. The results exhibit that the corrosion ratio of mild steel was reduced regarding to adding NATN. The corrosion inhibition rate for the NATN was 92.3% at the highest investigated NATN concentration. From the weight loss results it could be concluded that NATN with sulfur, nitrogen and oxygen atoms has clarified best corrosion inhibition achievement comparing to 3,5-dinitrobenzoic acid. Regarding to theoretical studies, DFT was employee to figured geometrical structure and electronic characteristics on NATN. The investigation have been extensive to the HOMO and LUMO analysis to evaluate the energy gap, Ionization potential, Electron Affinity, Global Hardness, Chemical Potential, Electrophilicity, Electronegativity and Polarizability.

Effect of load deflection on corrosion behavior of NiTi wire.

PubMed

Liu, I H; Lee, T M; Chang, C Y; Liu, C K

2007-06-01

For dental orthodontic applications, NiTi wires are used under bending conditions in the oral environment for a long period. The purpose of this study was to investigate the effect of bending stress on the corrosion of NiTi wires using potentiodynamic and potentiostatic tests in artificial saliva. The results indicated that bending stress induces a higher corrosion rate of NiTi wires in passive regions. It is suggested that the passive oxide film of specimens would be damaged under bending conditions. Auger electron spectroscopic analysis showed a lower thickness of passive films on stressed NiTi wires compared with unstressed specimens in the passive region. By scanning electron microscopy, localized corrosion was observed on stressed Sentalloy specimens after a potentiodynamic test at pH 2. In conclusion, this study indicated that bending stress changed the corrosion properties and surface characteristics of NiTi wires in a simulated intra-oral environment.

Is rigid endoscopy necessary with childhood corrosive ingestion? a retrospective comparative analysis of 458 cases.

PubMed

Bosnali, O; Moralioglu, S; Celayir, A; Pektas, O Z

2017-02-01

The aim of this study was to determine the necessity of endoscopy in cases in which a corrosive substance was ingested and to find a practical way to avoid unnecessary endoscopies for similar cases in the future. The clinical records of 458 hospitalized cases with clinical histories of corrosive substance ingestion between January 2007 and December 2013 were retrospectively reviewed. The demographics of the cases, the ingested substances, and the rigid endoscopy findings were evaluated. The three most commonly ingested corrosive agents were household bleach (22.9%), household degreaser (15.9%), and drain cleaner (13.1%). Rigid esophagoscopy was performed in 367 of the 458 cases. Corrosive agents were grouped according to their purpose of household use; eight groups were created. The degree of corrosive injury observed in the different groups was compared with the degree of injury caused by household bleach. Among the corrosive agent groups, dishwashing machine products (Gr.1), laundry products (Gr.2), liquid cleaners (Gr.3), and household bleach (Gr.4) did not cause high-grade injuries. The resulting injuries and esophagoscopy results among the above groups, whether symptomatic or not, did not differ from one another. Corrosive agents such as drain cleaner (Gr.6), household degreaser (Gr.7), and several other acidic products (Gr.8) caused high-grade injuries in the esophagus; however, lime remover/HCl (Gr.5) did not. Thus, hospitalization and rigid endoscopy seem unnecessary to assess esophageal injury in most cases, if the ingested corrosive agent fits into group 1, 2, 3, or 4 and if the patient can be easily fed. Esophagoscopy is useful to shorten the hospitalization times in cases where strong corrosive agents were ingested, such as those in groups 5, 6, 7, and 8. © 2016 International Society for Diseases of the Esophagus.

Super-Hydrophobic Green Corrosion Inhibitor On Carbon Steel

NASA Astrophysics Data System (ADS)

Hassan, H.; Ismail, A.; Ahmad, S.; Soon, C. F.

2017-06-01

There are many examples of organic coatings used for corrosion protection. In particular, hydrophobic and super-hydrophobic coatings are shown to give good protection because of their enhanced ability to slow down transport of water and ions through the coating. The purpose of this research is to develop water repellent coating to avoid direct contact between metal and environment corrosive and mitigate corrosion attack at pipeline system. This water repellent characteristic on super-hydrophobic coating was coated by electrodeposition method. Wettability of carbon steel with super-hydrophobic coating (cerium chloride and myristic acid) and oxidized surface was investigated through contact angle and inhibitor performance test. The inhibitor performance was studied in 25% tannin acid corrosion test at 30°C and 3.5% sodium chloride (NaCl). The water contact angle test was determined by placing a 4-μL water droplet of distilled water. It shows that the wettability of contact angle super-hydrophobic with an angle of 151.60° at zero minute can be classified as super-hydrophobic characteristic. By added tannin acid as inhibitor the corrosion protection on carbon steel becomes more consistent. This reveals that the ability of the coating to withstand with the corrosion attack in the seawater at different period of immersions. The results elucidate that the weight loss increased as the time of exposure increased. However, the corrosion rates for uncoated carbon steel is high compared to coated carbon steel. As a conclusion, from both samples it can be seen that the coated carbon steel has less corrosion rated compared to uncoated carbon steel and addition of inhibitor to the seawater provides more protection to resist corrosion attack on carbon steel.

Passive Films, Surface Structure and Stress Corrosion and Crevice Corrosion Susceptibility.

DTIC Science & Technology

1980-08-01

with pure titanium ( 4 ], it is of interest to pursue the effects on titanium -palladium alloys, to evaluate their susceptibility to stress corrosion...cracking due to hydrogen embrittlement with the field ion microscope, and to compare the results with those previously obtained with pure titanium [ 4 ...characterized as 99.99+ percent pure, and was used in the previous field ion microscopy study of titanium [ 4 ], where it was found that strain annealing titanium

Dependence of Crystallographic Orientation on Pitting Corrosion Behavior of Ni-Fe-Cr Alloy 028

NASA Astrophysics Data System (ADS)

Zhang, LiNa; Szpunar, Jerzy A.; Dong, JianXin; Ojo, Olanrewaju A.; Wang, Xu

2018-06-01

The influence of crystallographic orientation on the pitting corrosion behavior of Ni-Fe-Cr alloy 028 was studied using a combination of X-ray diffraction (XRD), electron backscatter diffraction (EBSD), potentiodynamic polarization technique, and atomic force microscopy (AFM). The results show that there is anisotropy of pitting corrosion that strongly depends on crystallographic orientation of the surface plane. The distribution of pit density in a standard stereographic triangle indicates that the crystallographic planes close to {100} are more prone to pitting corrosion compared to planes {110} and {111}. The surface energy calculation of (001) and (111) shows that the plane with a high atomic packing density has a low surface energy with concomitant strong resistance to pitting corrosion. A correlation function between crystallographic orientation and pitting corrosion susceptibility suggests a method that not only predicts the pitting resistance of known textured materials, but also could help to improve corrosion resistance by controlling material texture.

Understanding effect of 3.5 wt.% NaCl on the corrosion of Al0.1CoCrFeNi high-entropy alloy

NASA Astrophysics Data System (ADS)

Kumar, N.; Fusco, M.; Komarasamy, M.; Mishra, R. S.; Bourham, M.; Murty, K. L.

2017-11-01

High entropy alloys are a new class of metallic materials with potential for use in a wide variety of applications including their use in corrosive environment. The present study focused on the corrosion behavior of a single-phase, face-centered cubic high entropy alloy (HEA) Al0.1CoCrFeNi in as-cast condition, and the results are compared with the corrosion behavior of the SS304. The microstructural characterization of the alloys in as-received condition was carried out using optical microscopy, electron backscattered diffraction, energy dispersive spectroscopy, and X-ray diffraction. Corrosion behavior was studied using potentiodynamic polarization test in a 3.5 wt% NaCl solution and electrochemical impedance spectroscopy at room temperature. It was observed that the general corrosion resistance of the HEA was better than that of SS304. Pitting potential of the HEA was found to be superior to that of the SS304. Corrosion pits size was slightly smaller in SS304 than that in the HEA. 3D imaging determined that the pit depths were of the same order in both cases. Overall, the HEA Al0.1CoCrFeNi demonstrated a better resistance to general and pitting corrosion.

The corrosion behavior of CVI SiC matrix in SiCf/SiC composites under molten fluoride salt environment

NASA Astrophysics Data System (ADS)

Wang, Hongda; Feng, Qian; Wang, Zhen; Zhou, Haijun; Kan, Yanmei; Hu, Jianbao; Dong, Shaoming

2017-04-01

High temperature corrosion behavior and microstructural evolution of designed chemical-vapor-infiltrated SiC matrix in SiC fiber reinforced SiC ceramic matrix composites in 46.5LiF-11.5NaF-42.0KF (mol. %) eutectic salt at 800 °C for various corrosion time was studied. Worse damage was observed as extending the exposure time, with the mass loss ratio increasing from 0.716 wt. % for 50 h to 5.914 wt. % for 500 h. The mass loss rate showed a trend of first decrease and then increase with the extended corrosion exposure. Compared with the near-stoichiometric SiC matrix layers, the O-contained boundaries between deposited matrix layers and the designed Si-rich SiC matrix layers were much less corrosion resistant and preferentially corroded. Liner relationship between the mass loss ratio and the corrosion time obtained from 50 h to 300 h indicated that the corrosion action was reaction-control process. Further corrosion would lead to matrix layer exfoliation and higher mass loss ratio.

Effect of high repetition laser shock peening on biocompatibility and corrosion resistance of magnesium

NASA Astrophysics Data System (ADS)

Caralapatti, Vinodh Krishna; Narayanswamy, Sivakumar

2017-02-01

Magnesium, as a biomaterial has the potential to replace conventional implant materials owing to its numerous advantages. However, high corrosion rate is a major obstacle that has to be addressed for its implementation as implants. This study aims to evaluate the feasibility and effects of High Repetition Laser Shock Peening (HRLSP) on biocompatibility and corrosion resistance of Mg samples and as well as to analyze the effect of operational parameters such as peening with overlap on corrosion rate. From the results obtained using hydrogen evolution and mass loss methods, it was found that corrosion rates of both 0% overlap and 66% overlap peened samples reduced by more than 50% compared to that of unpeened sample and sample peened with 66% overlap exhibited least corrosion. The biocompatibility of peened Mg samples was also enhanced as there was neither rapid pH variation nor large hydrogen bubble formation around samples.

Electrochemical Corrosion Properties of Commercial Ultra-Thin Copper Foils

NASA Astrophysics Data System (ADS)

Yen, Ming-Hsuan; Liu, Jen-Hsiang; Song, Jenn-Ming; Lin, Shih-Ching

2017-08-01

Ultra-thin electrodeposited Cu foils have been developed for substrate thinning for mobile devices. Considering the corrosion by residual etchants from the lithography process for high-density circuit wiring, this study investigates the microstructural features of ultra-thin electrodeposited Cu foils with a thickness of 3 μm and their electrochemical corrosion performance in CuCl2-based etching solution. X-ray diffraction and electron backscatter diffraction analyses verify that ultra-thin Cu foils exhibit a random texture and equi-axed grains. Polarization curves show that ultra-thin foils exhibit a higher corrosion potential and a lower corrosion current density compared with conventional (220)-oriented foils with fan-like distributed fine-elongated columnar grains. Chronoamperometric results also suggest that ultra-thin foils possess superior corrosion resistance. The passive layer, mainly composed of CuCl and Cu2O, forms and dissolves in sequence during polarization.

Effect of Zr Inhibitor on Corrosion of Haynes 230 and NS-163 Alloys in Flinak

NASA Astrophysics Data System (ADS)

Peng, Yuxiang; Reddy, Ramana G.

The intrinsic corrosion behavior of Haynes 230 and NS-163 alloys after adding corrosion inhibitor Zr to LiF-NaF-KF (FLiNaK) salts was evaluated. Thermodynamic modeling studies were performed to investigate the compatibility of Haynes alloys for solar thermal energy storage applications in the molten salts. Equilibrium conditions were considered for predicting the corrosion products and weight loss of salts at higher temperatures (700 - 1000°C). Weight loss of FLiNaK salt after corrosion with or without inhibitor is less than 5%, indicating no significant change in compositions of FLiNaK even with Zr inhibitor. Furthermore, to compare with experimental data, modeling calculation with known amount of trace impurities (Ni2+, Fe3+ and so on) added to the molten salts, shows similar trend and corrosion product with and without Zr inhibitor.

Effects of Stress on Corrosion in a Molten Salt Environment

NASA Astrophysics Data System (ADS)

Girdzis, Samuel; Manos, Dennis; Cooke, William

Molten salt is often used as a heat transfer and energy storage fluid in concentrating solar power plants. Despite its suitable thermal properties, molten salt can present challenges in terms of corrosion. Previous studies have focused extensively on mass loss due to molten salt-induced corrosion. In contrast, we have investigated how corrosion begins and how it changes the surface of stainless steel. Samples of alloys including 304 and 316 stainless steel were exposed to the industry-standard NaNO3-KNO3 (60%-40% by weight) mixture at temperatures over 500°C and then analyzed using Hirox, SEM, and TOF-SIMS. We compare the corrosion at grain boundaries to that within single grain surfaces, showing the effect of the increased internal stresses and the weakened passivation layer. Also, we have examined the enhanced corrosion of samples under mechanical stress, simulating the effects of thermal stresses in a power plant.

Axenic aerobic biofilms inhibit corrosion of copper and aluminum.

PubMed

Jayaraman, A; Ornek, D; Duarte, D A; Lee, C C; Mansfeld, F B; Wood, T K

1999-11-01

The corrosion behavior of unalloyed copper and aluminum alloy 2024 in modified Baar's medium has been studied with continuous reactors using electrochemical impedance spectroscopy. An axenic aerobic biofilm of either Pseudomonas fragi K or Bacillus brevis 18 was able to lessen corrosion as evidenced by a consistent 20-fold increase in the low-frequency impedance value of copper as well as by a consistent four- to seven-fold increase in the polarization resistance of aluminum 2024 after six days exposure compared to sterile controls. This is the first report of axenic aerobic biofilms inhibiting generalized corrosion of copper and aluminum. Addition of the representative sulfate-reducing bacterium (SRB) Desulfovibrio vulgaris (to simulate consortia corrosion behavior) to either the P. fragi K or B. brevis 18 protective biofilm on copper increased the corrosion to that of the sterile control unless antibiotic (ampicillin) was added to inhibit the growth of SRB in the biofilm.

Comparative Behaviour of Nitrite and Nitrate for the Protection of Rebar Corrosion

NASA Astrophysics Data System (ADS)

Ahmad, Altaf; Kumar, Anil

2017-10-01

Corrosion of rebar steel due to environmental causes has been studied through various approaches, and among the protection techniques use of inhibitors has gained encouragement. Nitrites and nitrates of sodium have gained sufficient scientific coverage. Recently, nitrites and nitrates of calcium have been verified in some studies, which, however, needs further experimentation through different angles. Simple polarization technique has been utilized in the present study to compare inhibitive efficiency of these salts of sodium and calcium, which indicate that calcium salts are more efficient.

The Growth of Small Corrosion Fatigue Cracks in Alloy 7075

NASA Technical Reports Server (NTRS)

Piascik, Robert S.

2015-01-01

The corrosion fatigue crack growth characteristics of small (greater than 35 micrometers) surface and corner cracks in aluminum alloy 7075 is established. The early stage of crack growth is studied by performing in situ long focal length microscope (500×) crack length measurements in laboratory air and 1% sodium chloride (NaCl) environments. To quantify the "small crack effect" in the corrosive environment, the corrosion fatigue crack propagation behavior of small cracks is compared to long through-the-thickness cracks grown under identical experimental conditions. In salt water, long crack constant K(sub max) growth rates are similar to small crack da/dN.

The Growth of Small Corrosion Fatigue Cracks in Alloy 7075

NASA Technical Reports Server (NTRS)

Piascik, R. S.

2001-01-01

The corrosion fatigue crack growth characteristics of small (less than 35 microns) surface and corner cracks in aluminum alloy 7075 is established. The early stage of crack growth is studied by performing in situ long focal length microscope (500X) crack length measurements in laboratory air and 1% NaCl environments. To quantify the "small crack effect" in the corrosive environment, the corrosion fatigue crack propagation behavior of small cracks is compared to long through-the-thickness cracks grown under identical experimental conditions. In salt water, long crack constant K(sub max) growth rates are similar to small crack da/dN.

In vitro evaluation of the electrochemical behaviour of stainless steel and Ni-Ti orthodontic archwires at different temperatures.

PubMed

Pakshir, M; Bagheri, T; Kazemi, M R

2013-08-01

The aim of this study was to compare the electrochemical corrosion behaviour of stainless steel (SS) and nickel-titanium (Ni-Ti) orthodontic archwires in Ringer's solution at temperatures ranging from 15 to 55°C by using linear sweep voltametry and electrochemical impedance spectroscopy. Polarization curves show that the corrosion current density of SS is greater than that of Ni-Ti alloy. Since the corrosion current density is directly proportional to the corrosion rate, a great corrosion current density shows a lower resistance against corrosion. Therefore, in comparison with SS, Ni-Ti alloys have a lower corrosion rate. Results show that the temperature of the solution affects the corrosion rates of the alloys. As the temperature increases, the corrosion resistance of both of the alloys decreases, although these variations were not so large. Impedance measurements show that the electrochemical behaviour of Ni-Ti exhibits higher polarization resistance and lower capacitance, which means that passive film formed on this alloy is more homogeneous and thicker in comparison with SS. Results also show that polarization resistance of both alloys decreases slowly with increases in the temperature of the solution.

PAINT ADHESION AND CORROSION PERFORMANCE OF CHROMIUM-FREE PRETREATMENTS OF 55% AL-ZN-COATED STEEL

EPA Science Inventory

The adhesion and corrosion performances for several pretreatments of 55% Al-Zn-coated steels which were coil-coated with polyester paint systems were determined. The objective of this study was to evaluate new, silane-based metal pretreatments and to compare their performance wit...

Kinetics of Corrosion Inhibition of Aluminum in Acidic Media by Water-Soluble Natural Polymeric Pectates as Anionic Polyelectrolyte Inhibitors.

PubMed

Hassan, Refat M; Zaafarany, Ishaq A

2013-06-17

Corrosion inhibition of aluminum (Al) in hydrochloric acid by anionic polyeletrolyte pectates (PEC) as a water-soluble natural polymer polysaccharide has been studied using both gasometric and weight loss techniques. The results drawn from these two techniques are comparable and exhibit negligible differences. The inhibition efficiency was found to increase with increasing inhibitor concentration and decrease with increasing temperature. The inhibition action of PEC on Al metal surface was found to obey the Freundlich isotherm. Factors such as the concentration and geometrical structure of the inhibitor, concentration of the corrosive medium, and temperature affecting the corrosion rates were examined. The kinetic parameters were evaluated and a suitable corrosion mechanism consistent with the kinetic results is discussed in the paper.

Kinetics of Corrosion Inhibition of Aluminum in Acidic Media by Water-Soluble Natural Polymeric Pectates as Anionic Polyelectrolyte Inhibitors

PubMed Central

Hassan, Refat M.; Zaafarany, Ishaq A.

2013-01-01

Corrosion inhibition of aluminum (Al) in hydrochloric acid by anionic polyeletrolyte pectates (PEC) as a water-soluble natural polymer polysaccharide has been studied using both gasometric and weight loss techniques. The results drawn from these two techniques are comparable and exhibit negligible differences. The inhibition efficiency was found to increase with increasing inhibitor concentration and decrease with increasing temperature. The inhibition action of PEC on Al metal surface was found to obey the Freundlich isotherm. Factors such as the concentration and geometrical structure of the inhibitor, concentration of the corrosive medium, and temperature affecting the corrosion rates were examined. The kinetic parameters were evaluated and a suitable corrosion mechanism consistent with the kinetic results is discussed in the paper. PMID:28809282

Corrosion Behavior of an Abradable Seal Coating System

NASA Astrophysics Data System (ADS)

Zhang, Feng; Xu, Cunguan; Lan, Hao; Huang, Chuanbing; Zhou, Yang; Du, Lingzhong; Zhang, Weigang

2014-08-01

A novel NiTi/BN composite abradable coating and two traditional Ni/C and Ni/BN coatings were manufactured with NiAl as the bond layer using thermal spray technology and their corrosion behaviors were investigated. In salt spray corrosion testing of the Ni/BN coating, defective sites of the metal matrix were corroded preferentially. Simulated occlusion experiments and electrochemical tests indicated that migration of ions resulted in pH decrease and Cl- enrichment in defects, and a more aggressive electrolyte led to a decrease of the corrosion potential of the metal inside defects but an increase of the corrosion current density, representing an autocatalytic corrosion process. Moreover, galvanic corrosion between the top and bond coatings of the abradable system was studied via the electrochemical technique. The results showed that, for the NiTi/BN, Ni/BN, and Ni/graphite coatings with a NiAl bond coating, current flow was generated between the anode and cathode. The NiTi/BN coating acted as the cathode due to its passivation, while the Ni/BN and Ni/graphite coatings acted as the anode because of their lower corrosion potential compared with the NiAl coating. The anode suffered serious corrosion damage due to galvanic corrosion, while the cathode corroded only slightly.

Effect of Molybdenum on the Corrosion Behavior of High-Entropy Alloys CoCrFeNi 2 and CoCrFeNi 2 Mo 0.25 under Sodium Chloride Aqueous Conditions

DOE PAGES

Rodriguez, Alvaro A.; Tylczak, Joseph H.; Gao, Michael C.; ...

2018-01-01

The corrosion behavior of high-entropy alloys (HEAs) CoCrFeNi 2 and CoCrFeNi 2 Mo 0.25 was investigated in 3.5 wt. percent sodium chloride (NaCl) at 25°C by electrochemical methods. Their corrosion parameters were compared to those of HASTELLOY® C-276 (UNS N10276) and stainless steel 316L (UNS 31600) to assess the suitability of HEAs for potential industrial applications in NaCl simulating seawater type environments. The corrosion rates were calculated using corrosion current determined from electrochemical experiments for each of the alloys. In addition, potentiodynamic polarization measurements can indicate active, passive, and transpassive behavior of the metal as well as potential susceptibility to pittingmore » corrosion. Cyclic voltammetry (CV) can confirm the alloy susceptibility to pitting corrosion. Electrochemical impedance spectroscopy (EIS) elucidates the corrosion mechanism under studied conditions. The results of the electrochemical experiments and scanning electron microscopy (SEM) analyses of the corroded surfaces revealed general corrosion on alloy CoCrFeNi 2 Mo 0.25 and HASTELLOY C-276 and pitting corrosion on alloy CoCrFeNi 2 and stainless steel 316L.« less

Effect of Molybdenum on the Corrosion Behavior of High-Entropy Alloys CoCrFeNi 2 and CoCrFeNi 2 Mo 0.25 under Sodium Chloride Aqueous Conditions

DOE Office of Scientific and Technical Information (OSTI.GOV)

Rodriguez, Alvaro A.; Tylczak, Joseph H.; Gao, Michael C.

The corrosion behavior of high-entropy alloys (HEAs) CoCrFeNi 2 and CoCrFeNi 2 Mo 0.25 was investigated in 3.5 wt. percent sodium chloride (NaCl) at 25°C by electrochemical methods. Their corrosion parameters were compared to those of HASTELLOY® C-276 (UNS N10276) and stainless steel 316L (UNS 31600) to assess the suitability of HEAs for potential industrial applications in NaCl simulating seawater type environments. The corrosion rates were calculated using corrosion current determined from electrochemical experiments for each of the alloys. In addition, potentiodynamic polarization measurements can indicate active, passive, and transpassive behavior of the metal as well as potential susceptibility to pittingmore » corrosion. Cyclic voltammetry (CV) can confirm the alloy susceptibility to pitting corrosion. Electrochemical impedance spectroscopy (EIS) elucidates the corrosion mechanism under studied conditions. The results of the electrochemical experiments and scanning electron microscopy (SEM) analyses of the corroded surfaces revealed general corrosion on alloy CoCrFeNi 2 Mo 0.25 and HASTELLOY C-276 and pitting corrosion on alloy CoCrFeNi 2 and stainless steel 316L.« less

Influence of Hydrostatic Pressure on the Corrosion Behavior of Superhydrophobic Surfaces on Bare and Oxidized Aluminum Substrates.

PubMed

Ou, J F; Fang, X Z; Zhao, W J; Lei, S; Xue, M S; Wang, F J; Li, C Q; Lu, Y L; Li, W

2018-05-22

It is generally recognized that superhydrophobic surfaces in water may be used for corrosion resistance due to the entrapped air in the solid/liquid interface and could find potential applications in the protection of ship hull. For a superhydrophobic surface, as its immersion depth into water increases, the resultant hydrostatic pressure is also increased, and the entrapped air can be squeezed out much more easily. It is therefore predicted that high hydrostatic pressure would cause an unexpected decrease in corrosion resistance for the vessels in deep water (e.g., submarines) because of the unstable entrapped air. In this work, in order to clarify the role of hydrostatic pressure in the corrosion behavior of superhydrophobic surfaces, two typical superhydrophobic surfaces (SHSs) were prepared on bare and oxidized aluminum substrates, respectively, and then were immersed into the NaCl aqueous solutions with different depths of ∼0 cm (hydrostatic pressure ∼0 kPa), 10 cm (1 kPa), and 150 cm (15 kPa). It was found out for the SHSs on the oxidized Al, as the hydrostatic pressure increased, the corrosion behavior became severe. However, for the SHSs on the bare Al, their corrosion behavior was complex due to hydrostatic pressure. It was found that the corrosion resistance under 1 kPa was the highest. Further mechanism analysis revealed that this alleviated corrosion behavior under 1 kPa resulted from suppressing the oxygen diffusion through the liquid and reducing the subsequent corrosion rate as compared with 0 kPa, whereas the relatively low hydrostatic pressure (HP) could stabilize the entrapped air and hence enhance the corrosion resistance, compared with 15 kPa. The present study therefore provided a fundamental understanding for the applications of SHSs to prevent the corrosion, especially for various vessels in deep water.

In vitro corrosion resistance of porous NiTi intervertebral fusion devices

NASA Astrophysics Data System (ADS)

Schrooten, Jan; Assad, Michel; Van Humbeeck, Jan; Leroux, Michel A.

2007-02-01

Porous titanium-nickel (PTN) intervertebral fusion devices, produced by self-propagating high-temperature synthesis, represent an alternative to traditional long-term implants in the orthopaedic field. PTN promotes tissue ingrowth and has succeeded short-term and long-term biocompatibility in vivo testing. In this in vitro study, the PTN morphology was characterized using microfocus computer tomography (μCT) in order to calculate the active PTN surface. Potentiodynamic polarization testing was then performed to evaluate the in vitro corrosion resistance of PTN devices in Hanks' based salt solution. Direct coupling experiments of PTN with Ti6Al4V were also performed in order to establish the galvanic corrosion resistance of PTN intervertebral implants in the presence of potential Ti6Al4V supplemental fixation devices. Compared to the behaviour of other orthopaedic biomaterials and solid NiTi devices, PTN devices showed a level of corrosion resistance that is comparable to other NiTi devices and acceptable for the intended orthopaedic application. Further improvement of the corrosion resistance is still possible by specific electrochemical surface treatments.

Determination of the Corrosive Conditions Present within Aircraft Lap-Splice Joints

NASA Technical Reports Server (NTRS)

Lewis, Karen S.; Kelly, Robert G.; Piascik, Robert S.

1999-01-01

The complexity of airframe structure lends itself to damage resulting from crevice corrosion. Fuselage lap-splice joints are a particularly important structural detail in this regard because of the difficulty associated with detection and measurement of corrosion in these occluded regions. The objective of this work is to develop a laboratory corrosion test protocol to identify the chemistry to which lap joints are exposed and to develop a model of the corrosion within the joints. A protocol for collecting and identifying the chemistry of airframe crevice corrosion has been developed. Capillary electrophoresis (CE) is used to identify the ionic species contained in corrosion product samples removed from fuselage lap splice joints. CE analysis has been performed on over sixty corrosion product samples removed from both civilian and military aircraft. Over twenty different ions have been detected. Measurements of pH of wetted corroded surfaces indicated an alkaline occluded solution. After determining the species present and their relative concentrations, the resultant solution was reproduced in bulk and electrochemical tests were performed to determine the corrosion rate. Electrochemical analyses of the behavior of AA2024-T3 in these solutions gave corrosion rates of up to 250 microns per year (10 mpy). Additional tests have determined the relative importance of each of the detected ions in model solutions used for future predictive tests. The statistically significant ions have been used to create a second generation solution. Laboratory studies have also included exposure tests involving artificial lap joints exposed to various simulated bulk and crevice environments. The extent and morphology of the attack in artificial lap joints has been compared to studies of corroded samples from actual aircraft. Other effects, such as temperature and potential, as well as the impact of the environment on fatigue crack growth have also been studied.

A Micro-Electrochemical Study of Friction Stir Welded Aluminum 6061-T6

NASA Technical Reports Server (NTRS)

Hintze, Paul E.; Calle, Luz M.

2005-01-01

The corrosion behavior of friction stir welded Aluminum alloy 606 1-T6 was studied using a micro-electrochemical cell. The micro-electrochemical cell has a measurement area of about 0.25 square mm which allows for measurement of corrosion properties at a very small scale. The corrosion and breakdown potentials were measured at many points inside and outside the weld along lines perpendicular to the weld. The breakdown potential is approximately equal inside and outside the weld; however, it is lower in the narrow border between the weld and base material. The results of electrochemical measurements were correlated to micro-structural analysis. The corrosion behavior of the friction stir welded samples was compared to tungsten inert gas (TIG) welded samples of the same material.

A systematic study of mechanical properties, corrosion behavior and biocompatibility of AZ31B Mg alloy after ultrasonic nanocrystal surface modification.

PubMed

Hou, Xiaoning; Qin, Haifeng; Gao, Hongyu; Mankoci, Steven; Zhang, Ruixia; Zhou, Xianfeng; Ren, Zhencheng; Doll, Gary L; Martini, Ashlie; Sahai, Nita; Dong, Yalin; Ye, Chang

2017-09-01

Magnesium alloys have tremendous potential for biomedical applications due to their good biocompatibility, osteoconductivity, and degradability, but can be limited by their poor mechanical properties and fast corrosion in the physiological environment. In this study, ultrasonic nanocrystal surface modification (UNSM), a recently developed surface processing technique that utilizes ultrasonic impacts to induce plastic strain on metal surfaces, was applied to an AZ31B magnesium (Mg) alloy. The mechanical properties, corrosion resistance, and biocompatibility of the alloy after UNSM treatment were studied systematically. Significant improvement in hardness, yield stress and wear resistance was achieved after the UNSM treatment. In addition, the corrosion behavior of UNSM-treated AZ31B was not compromised compared with the untreated samples, as demonstrated by the weight loss and released element concentrations of Mg and Al after immersion in alpha-minimum essential medium (α-MEM) for 24h. The in vitro biocompatibility of the AZ31B Mg alloys toward adipose-derived stem cells (ADSCs) before and after UNSM processing was also evaluated using a cell culture study. Comparable cell attachments were achieved between the two groups. These studies showed that UNSM could significantly improve the mechanical properties of Mg alloys without compromising their corrosion rate and biocompatibility in vitro. These findings suggest that UNSM is a promising method to treat biodegradable Mg alloys for orthopaedic applications. Copyright © 2017 Elsevier B.V. All rights reserved.

Hot corrosion behavior of platinum-modified nickel- and cobalt-based alloys and coatings

NASA Astrophysics Data System (ADS)

Deodeshmukh, Vinay Prakash

High temperature degradation by hot corrosion (650-1000°C) and/or oxidation (>1000°C) can severely reduce the longevity of advanced gas turbine engine components. The protection of high-temperature components against hot corrosion or oxidation is typically conferred by the application of either a diffusion or overlay metallic coating that is able to form a continuous, adherent, and slow-growing oxide scale. There are currently no coatings that provide adequate protection to both hot corrosion and oxidation. Indeed, there is a particular need for such protective coatings because many advanced aero, marine, and industrial gas-turbines operate in both hot corrosion and oxidation regimes in their duty cycle. Recent work at Iowa State University (ISU) has showed that a wide range Pt+Hf-modified gamma'-Ni3Al + gamma-Ni alloy compositions form a very adherent and slow-growing Al 2O3 scale. In fact, the results reported suggest that Pt+Hf-modified gamma' + gamma coatings offer a viable superior alternative to beta-NiAl(Pt)-based coatings. The main thrust of this study was to assess and establish optimum target gamma' + gamma coating compositions for extending the service life of high-temperature gas turbine components exposed to hot corrosion and oxidation conditions. Both high temperature hot-corrosion (HTHC-900°C) and low temperature hot-corrosion (LTHC-705°C) behaviors of the Pt+Hf-modified gamma' + gamma alloys were assessed. The salt used to bring about hot corrosion was Na 2SO4. Quite interestingly, it was found that the HTHC resistance of gamma' + gamma alloys improved with up to about 10 at.% Pt addition, but then decreased significantly with increasing Pt content up to 30 at.% (the maximum level studied); however, under LTHC conditions the resistance of gamma' + gamma alloys improved with increasing Pt content up to 30 at.%. To further improve hot corrosion resistance of Pt+Hf-modified gamma' + gamma alloys, the effects of systematic additions of Cr, Si, and Cr+Si were assessed. The effects pre-oxidation treatments were also studied to further improve the hot corrosion resistance. In addition, high-temperature oxidation behavior of various modified of gamma' + gamma alloys was studied in air at 1150°C under both isothermal and cyclic oxidation conditions. Certain modified versions of gamma' + gamma coating composition(s) exhibited excellent resistance to both hot corrosion and oxidation. Finally, the HTHC and LTHC resistance of novel Pt+Hf-modified gamma' + gamma-based diffusion coatings using a pack cementation process developed at ISU were studied and compared with state-of-the-art commercial coatings. It was found that the Pt+Hf-modified gamma' + gamma coating exhibited superior resistance to both types of hot corrosion with the preoxidation treatment; while, only Pt-modified beta exhibited excellent LTHC resistance with no pre-oxidation treatment. This study also involved evaluating the hot corrosion resistance of various commercially available Pt-modified beta-NiAl diffusion aluminides and CoCrAlY-based overlay coatings for marine gas turbine engine components under both HTHC and LTHC conditions. The Al-Pt-rich beta aluminide exhibited improved resistance to both types of hot corrosion compared to the various Ni-rich beta aluminide and CoCrAlY coatings.

Atmospheric corrosion of metals in industrial city environment.

PubMed

Kusmierek, Elzbieta; Chrzescijanska, Ewa

2015-06-01

Atmospheric corrosion is a significant problem given destruction of various materials, especially metals. The corrosion investigation in the industrial city environment was carried out during one year exposure. Corrosion potential was determined using the potentiometric method. The highest effect of corrosion processes was observed during the winter season due to increased air pollution. Corrosion of samples pre-treated in tannic acid before the exposure was more difficult compared with the samples without pretreatment. The corrosion products determined with the SEM/EDS method prove that the most corrosive pollutants present in the industrial city air are SO2, CO2, chlorides and dust.

Pitting and Stress Corrosion Cracking Susceptibility of Nanostructured Al-Mg Alloys in Natural and Artificial Environments

NASA Astrophysics Data System (ADS)

Sharma, Mala M.; Ziemian, Constance W.

2008-12-01

The stress corrosion cracking (SCC) behavior of two developmental nanocrystalline 5083 alloys with varied composition and processing conditions was studied. The results were compared to a commercial aluminum AA 5083 (H111) alloy. The pitting densities, size and depths, and residual tensile strengths were measured after alternate immersion in artificial seawater and atmospheric exposure under different loading conditions. Optical and scanning electron microscopy (SEM) with EDX was used to analyze the fracture surfaces of failed specimen after removal at selected intervals and tensile testing. One of the nanostructured Al-Mg alloys exhibited significantly superior pitting resistance when compared to conventional microstructured AA 5083. Under conditions where pitting corrosion showed up as local tunnels toward phase inclusions, transgranular cracking was observed, whereas under conditions when pitting corrosion evolved along grain boundaries, intergranular cracking inside the pit was observed. Pit initiation resistance of the nano alloys appears to be better than that of the conventional alloys. However, long-term pit propagation is a concern and warrants further study. The objective of this investigation was to obtain information regarding the role that ultra-fine microstructures play in their degradation in marine environments and to provide insight into the corrosion mechanisms and damage processes of these alloys.

Corrosion fatigue behaviors of two biomedical Mg alloys - AZ91D and WE43 - In simulated body fluid.

PubMed

Gu, X N; Zhou, W R; Zheng, Y F; Cheng, Y; Wei, S C; Zhong, S P; Xi, T F; Chen, L J

2010-12-01

Magnesium alloys have been recently developed as biodegradable implant materials, yet there has been no study concerning their corrosion fatigue properties under cyclic loading. In this study the die-cast AZ91D (A for aluminum 9%, Z for zinc 1% and D for a fourth phase) and extruded WE43 (W for yttrium 4%, E for rare earth mischmetal 3%) alloys were chosen to evaluate their fatigue and corrosion fatigue behaviors in simulated body fluid (SBF). The die-cast AZ91D alloy indicated a fatigue limit of 50MPa at 10⁷ cycles in air compared to 20MPa at 10⁶ cycles tested in SBF at 37°C. A fatigue limit of 110MPa at 10⁷ cycles in air was observed for extruded WE43 alloy compared to 40MPa at 10⁷ cycles tested in SBF at 37°C. The fatigue cracks initiated from the micropores when tested in air and from corrosion pits when tested in SBF, respectively. The overload zone of the extruded WE43 alloy exhibited a ductile fracture mode with deep dimples, in comparison to a brittle fracture mode for the die-cast AZ91D. The corrosion rate of the two experimental alloys increased under cyclic loading compared to that in the static immersion test. Copyright © 2010 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

Surface modification techniques for increased corrosion tolerance of zirconium fuel cladding

NASA Astrophysics Data System (ADS)

Carr, James Patrick, IV

Corrosion is a major issue in applications involving materials in normal and severe environments, especially when it involves corrosive fluids, high temperatures, and radiation. Left unaddressed, corrosion can lead to catastrophic failures, resulting in economic and environmental liabilities. In nuclear applications, where metals and alloys, such as steel and zirconium, are extensively employed inside and outside of the nuclear reactor, corrosion accelerated by high temperatures, neutron radiation, and corrosive atmospheres, corrosion becomes even more concerning. The objectives of this research are to study and develop surface modification techniques to protect zirconium cladding by the incorporation of a specific barrier coating, and to understand the issues related to the compatibility of the coatings examined in this work. The final goal of this study is to recommend a coating and process that can be scaled-up for the consideration of manufacturing and economic limits. This dissertation study builds on previous accident tolerant fuel cladding research, but is unique in that advanced corrosion methods are tested and considerations for implementation by industry are practiced and discussed. This work will introduce unique studies involving the materials and methods for accident tolerant fuel cladding research by developing, demonstrating, and considering materials and processes for modifying the surface of zircaloy fuel cladding. This innovative research suggests that improvements in the technique to modify the surface of zirconium fuel cladding are likely. Three elements selected for the investigation of their compatibility on zircaloy fuel cladding are aluminum, silicon, and chromium. These materials are also currently being investigated at other labs as alternate alloys and coatings for accident tolerant fuel cladding. This dissertation also investigates the compatibility of these three elements as surface modifiers, by comparing their microstructural and mechanical properties. To test their application for use in corrosive atmospheres, the corrosion behaviors are also compared in steam, water, and boric-acid environments. Various methods of surface modification were attempted in this investigation, including dip coating, diffusion bonding, casting, sputtering, and evaporation. The benefits and drawbacks of each method are discussed with respect to manufacturing and economic limits. Characterization techniques utilized in this work include optical microscopy, scanning electron microscopy, energy-dispersive spectroscopy, X-ray diffraction, nanoindentation, adhesion testing, and atomic force microscopy. The composition, microstructure, hardness, modulus, and coating adhesion were studied to provide encompassing properties to determine suitable comparisons and to choose an ideal method to scale to industrial applications. The experiments, results, and detailed discussions are presented in the following chapters of this dissertation research.

System for corrosion monitoring in pipeline applying fuzzy logic mathematics

NASA Astrophysics Data System (ADS)

Kuzyakov, O. N.; Kolosova, A. L.; Andreeva, M. A.

2018-05-01

A list of factors influencing corrosion rate on the external side of underground pipeline is determined. Principles of constructing a corrosion monitoring system are described; the system performance algorithm and program are elaborated. A comparative analysis of methods for calculating corrosion rate is undertaken. Fuzzy logic mathematics is applied to reduce calculations while considering a wider range of corrosion factors.

Corrosion rates of fasteners in treated wood exposed to 100% relative humidity

Treesearch

Samuel L. Zelinka; Douglas R. Rammer

2009-01-01

In the past, gravimetric corrosion data for fasteners exposed to treated wood has been reported as a percent weight loss. Although percent weight loss is a valid measure of corrosion for comparing identical fasteners, it can distort the corrosion performance of fasteners with different geometries and densities. This report reevaluates a key report on the corrosiveness...

Stress Corrosion Cracking of Pipeline Steels in Fuel Grade Ethanol and Blends - Study to Evaluate Alternate Standard Tests and Phenomenological Understanding of SCC

DOT National Transportation Integrated Search

2011-10-30

Main aim of this project was to evaluate alternate standard test methods for stress corrosion cracking (SCC) and compare them with the results from slow strain rate test (SSRT) results under equivalent environmental conditions. Other important aim of...

Corrosion properties of powder bed fusion additively manufactured 17-4 PH stainless steel

DOE PAGES

Schaller, Rebecca; Taylor, Jason; Rodelas, Jeffrey; ...

2017-02-20

The corrosion susceptibility of a laser powder bed fusion (LPBF) additively manufactured alloy, UNS S17400 (17-4 PH), was explored compared to conventional wrought material. Microstructural characteristics were characterized and related to corrosion behavior in quiescent, aqueous 0.6 M NaCl solutions. Electrochemical measurements demonstrated that the LPBF 17-4 PH alloy exhibited a reduced passivity range and active corrosion compared to its conventional wrought counterpart. Lastly, a micro-electrochemical cell was employed to further understand the effects of the local scale and attributed the reduced corrosion resistance of the LPBF material to pores with diameters ≥ 50 µm.

Corrosion properties of powder bed fusion additively manufactured 17-4 PH stainless steel

DOE Office of Scientific and Technical Information (OSTI.GOV)

Schaller, Rebecca; Taylor, Jason; Rodelas, Jeffrey

The corrosion susceptibility of a laser powder bed fusion (LPBF) additively manufactured alloy, UNS S17400 (17-4 PH), was explored compared to conventional wrought material. Microstructural characteristics were characterized and related to corrosion behavior in quiescent, aqueous 0.6 M NaCl solutions. Electrochemical measurements demonstrated that the LPBF 17-4 PH alloy exhibited a reduced passivity range and active corrosion compared to its conventional wrought counterpart. Lastly, a micro-electrochemical cell was employed to further understand the effects of the local scale and attributed the reduced corrosion resistance of the LPBF material to pores with diameters ≥ 50 µm.

The effect of zeolite and diatomite on the corrosion of reinforcement steel in 1 M HCl solution

NASA Astrophysics Data System (ADS)

Gerengi, Husnu; Kurtay, Mine; Durgun, Hatice

The greatest disadvantage of reinforced concrete structures is the corrosion occurring in the reinforcement which, over time, causes a reduction in the reinforcement-concrete adherence and eventual sectional loss. The purpose of this study was to reveal the corrosion mechanism of ribbed reinforcement inside additive-free (reference), 20% zeolite-doped and 20% diatomite-doped concrete samples after exposure to 1 M HCl over 240 days. Electrochemical impedance spectroscopy (EIS) measurements were made every 10 days. Consequently, it was determined that the 20% zeolite-doped concrete samples had higher concrete and reinforcement resistance compared to the 20% diatomite-doped and the reference concrete, i.e. they exhibited less corrosion.

Kinetics of corrosion inhibition of aluminum in acidic media by water-soluble natural polymeric chondroitin-4-sulfate as anionic polyelectrolyte inhibitor.

PubMed

Hassan, Refat M; Ibrahim, Samia M; Takagi, Hideo D; Sayed, Suzan A

2018-07-15

Corrosion inhibition of aluminum (Al) in hydrochloric acid by anionic polyelectrolyte chondroitin-4-sulfate (CS) polysaccharide has been studied using both gasometrical and weight-loss techniques. The results drawn from these two techniques are comparable and exhibit negligible differences. The inhibition efficiency was found to increase with increasing the inhibitor concentration and decreased with increasing temperature. The inhibition action of CS on Al metal surface was found to obey both of Langmuir and Freundlich isotherms. The factors affecting the corrosion rates such as the concentration and geometrical structure of the inhibitor, concentration of the corrosive medium, and the temperature were examined. The kinetic parameters were evaluated and a suitable corrosion mechanism consistent with the results obtained is discussed. Copyright © 2018. Published by Elsevier Ltd.

SEM and EDX Study of Stainless Steels, Suggested as Human Body Implants

NASA Astrophysics Data System (ADS)

Simitchiiska, R. N.; Ivanova, D.; Fachikov, L.

2018-06-01

The most important requirement for any material used as an implant is to be biocompatible and not to cause undesirable effects in the human body. Corrosion of implants is included in the topic of biocompatibility because it is a determining factor in their sustainability and seamless fulfillment of their functional purpose. The work presents the results obtained in the comparative study of two austenitic stainless steels (Cr18Ni9 and Cr18Mn12N) in two models of artificial saliva, accepted as environments for testing the corrosion behavior of materials for these aims. The nature of the corrosion attack, the composition of the corrosion products at 37°C and the pH 5.5 and pH 6.75 of the model media were determined using physical methods such as SEM and EDX of investigation and analysis. It was found that Cr18Mn12N steel (0.61 % N), exhibits higher corrosion resistance.

Biocorrosion of mild steel and copper used in cooling tower water and its control.

PubMed

Li, Xiao Lei; Narenkumar, Jayaraman; Rajasekar, Aruliah; Ting, Yen-Peng

2018-03-01

The present study describes the biocorrosion of mild steel (MS1010) and pure copper (Cu) in cooling water environments (both field and lab study). Electrochemical and surface analyses of both metals were carried out to confirm the corrosion susceptibility in the presence of bacteria and inhibitor. Surface analysis of the MS and Cu coupons revealed that biofilm was developed with increasing exposure time in the field study. In the lab study, accumulation of extracellular polymeric substance over the metal surface was noticed and led to the severe pitting type of corrosion on both metal surfaces. Besides, the anti-corrosive study was carried out using the combinations of commercial corrosion inhibitor (S7653-10 ppm) with biocide (F5100-5 ppm), and the results reveal that the corrosion rate of MS and Cu was highly reduced to 0.0281 and 0.0021 mm/year (inhibitor system) than 0.1589 and 0.0177 mm/year (control system). Inhibition efficiency for both metals in the presence of inhibitor with biocide was found as 82 and 88% for MS and Cu, respectively. The present study concluded that MS was very susceptible to biocorrosion, compared to copper metal in cooling water environment. Further, the combination of the both inhibitor and biocide was effectively inhibiting the biocorrosion which was due to its antibacterial and anti-corrosive properties.

Marine corrosion of mild steel at Lumut, Perak

NASA Astrophysics Data System (ADS)

Ting, Ong Shiou; Potty, Narayanan Sambu; Liew, Mohd. Shahir

2012-09-01

The corrosion rate of structural steels in the adverse marine and offshore environments affects the economic interest of offshore structures since the loss of steel may have significant impact on structural safety and performance. With more emphasis to maintain existing structures in service for longer time and hence to defer replacement costs, there is increasing interest in predicting corrosion rate at a given location for a given period of exposure once the protection coating or cathodic protection is lost. The immersion depth, salinity, steel composition and water pollution will be taken into account. Various corrosion allowances are prescribed for structural members by different standards. There are no studies to determine the appropriate corrosion allowance for steel structures in marine environment in Malaysia. The objectives of the research are to determine the nature and rate of corrosion in mm/year for steel structures in marine environment. It also tries to identify whether the corrosion rate is affected by differences in the chemical composition of the steels, and microalgae. Two sets of corrosion coupons of Type 3 Steel consisting of mild steel were fabricated and immersed in seawater using steel frames. The corrosion rate of the coupon in mm/ per year is estimated based on the material weight loss with time in service. The results are compared with recommendations of the code.

In vitro corrosion resistance of Lotus-type porous Ni-free stainless steels.

PubMed

Alvarez, Kelly; Hyun, Soong-Keun; Fujimoto, Shinji; Nakajima, Hideo

2008-11-01

The corrosion behavior of three kinds of austenitic high nitrogen Lotus-type porous Ni-free stainless steels was examined in acellular simulated body fluid solutions and compared with type AISI 316L stainless steel. The corrosion resistance was evaluated by electrochemical techniques, the analysis of released metal ions was performed by inductively coupled plasma mass spectrometry (ICP-MS) and the cytotoxicity was investigated in a culture of murine osteoblasts cells. Total immunity to localized corrosion in simulated body fluid (SBF) solutions was exhibited by Lotus-type porous Ni-free stainless steels, while Lotus-type porous AISI 316L showed very low pitting corrosion resistance evidenced by pitting corrosion at a very low breakdown potential. Additionally, Lotus-type porous Ni-free stainless steels showed a quite low metal ion release in SBF solutions. Furthermore, cell culture studies showed that the fabricated materials were non-cytotoxic to mouse osteoblasts cell line. On the basis of these results, it can be concluded that the investigated alloys are biocompatible and corrosion resistant and a promising material for biomedical applications.

Assessment of tap water quality and corrosion scales from the selected distribution systems in northern Pakistan.

PubMed

Baig, Shams Ali; Lou, Zimo; Baig, Muzaffar Ali; Qasim, Muhammad; Shams, Dilawar Farhan; Mahmood, Qaisar; Xu, Xinhua

2017-04-01

Corrosion deposits formed within drinking water distribution systems deteriorate drinking water quality and resultantly cause public health consequences. In the present study, an attempt was made to investigate the concurrent conditions of corrosion scales and the drinking water quality in selected water supply schemes (WSS) in districts Chitral, Peshawar, and Abbottabad, northern Pakistan. Characterization analyses of the corrosion by-products revealed the presence of α-FeOOH, γ-FeOOH, Fe 3 O 4 , and SiO 2 as major constituents with different proportions. The constituents of all the representative XRD peaks of Peshawar WSS were found insignificant as compared to other WSS, and the reason could be the variation of source water quality. Well-crystallized particles in SEM images indicated the formation of dense oxide layer on corrosion by-products. A wider asymmetric vibration peak of SiO 2 appeared only in Chitral and Abbottabad WSS, which demonstrated higher siltation in the water source. One-way ANOVA analysis showed significant variations in pH, turbidity, TDS, K, Mg, PO 4 , Cl, and SO 4 values, which revealed that these parameters differently contributed to the source water quality. Findings from this study suggested the implementation of proper corrosion prevention measures and the establishment of international collaboration for best corrosion practices, expertise, and developing standards.

Study of mechanical joint strength of aluminum alloy 7075-T6 and dual phase steel 980 welded by friction bit joining and weld-bonding under corrosion medium

DOE PAGES

Lim, Yong Chae; Squires, Lile; Pan, Tsung-Yu; ...

2014-12-30

We have employed a unique solid-sate joining process, called friction bit joining (FBJ), to spot weld aluminum alloy (AA) 7075-T6 and dual phase (DP) 980 steel. Static joint strength was studied in the lap shear tension configuration. In addition, weld-bonding (adhesive + FBJ) joints were studied in order to evaluate the ability of adhesive to mitigate the impact of corrosion on joint properties. Accelerated laboratory cyclic corrosion tests were carried out for both FBJ only and weld-bonding joints. Furthermore, the FBJ only joints that emerged from corrosion testing had lap shear failure loads that were significantly lower than freshly preparedmore » joints. However, weld-bonding specimens retained more than 80% of the lap shear failure load of the freshly prepared weld-bonding specimens. Moreover, examination of joint cross sections confirmed that the presence of adhesive in the weld-bonding joints mitigated the effect of the corrosion environment, compared to FBJ only joints.« less

Corrosion and mechanical performance of AZ91 exposed to simulated inflammatory conditions.

PubMed

Brooks, Emily K; Der, Stephanie; Ehrensberger, Mark T

2016-03-01

Magnesium (Mg) and its alloys, including Mg-9%Al-1%Zn (AZ91), are biodegradable metals with potential use as temporary orthopedic implants. Invasive orthopedic procedures can provoke an inflammatory response that produces hydrogen peroxide (H2O2) and an acidic environment near the implant. This study assessed the influence of inflammation on both the corrosion and mechanical properties of AZ91. The AZ91 samples in the inflammatory protocol were immersed for three days in a complex biologically relevant electrolyte (AMEM culture media) that contained serum proteins (FBS), 150 mM of H2O2, and was titrated to a pH of 5. The control protocol immersed AZ91 samples in the same biologically relevant electrolyte (AMEM & FBS) but without H2O2 and the acid titration. After 3 days all samples were switched into fresh AMEM & FBS for an additional 3-day immersion. During the initial immersion, inflammatory protocol samples showed increased corrosion rate determined by mass loss testing, increased Mg and Al ion released to solution, and a completely corroded surface morphology as compared to the control protocol. Although corrosion in both protocols slowed once the test electrolyte solution was replaced at 3 days, the samples originally exposed to the simulated inflammatory conditions continued to display enhanced corrosion rates as compared to the control protocol. These lingering effects may indicate the initial inflammatory corrosion processes modified components of the surface oxide and corrosion film or initiated aggressive localized processes that subsequently left the interface more vulnerable to continued enhanced corrosion. The electrochemical properties of the interfaces were also evaluated by EIS, which found that the corrosion characteristics of the AZ91 samples were potentially influenced by the role of intermediate adsorption layer processes. The increased corrosion observed for the inflammatory protocol did not affect the flexural mechanical properties of the AZ91 at any time point assessed. Copyright © 2015 Elsevier B.V. All rights reserved.

Atmospheric corrosion of metals in industrial city environment

PubMed Central

Kusmierek, Elzbieta; Chrzescijanska, Ewa

2015-01-01

Atmospheric corrosion is a significant problem given destruction of various materials, especially metals. The corrosion investigation in the industrial city environment was carried out during one year exposure. Corrosion potential was determined using the potentiometric method. The highest effect of corrosion processes was observed during the winter season due to increased air pollution. Corrosion of samples pre-treated in tannic acid before the exposure was more difficult compared with the samples without pretreatment. The corrosion products determined with the SEM/EDS method prove that the most corrosive pollutants present in the industrial city air are SO2, CO2, chlorides and dust. PMID:26217736

Effect of Different Cooling Rates on the Corrosion Behavior of High-Carbon Pearlitic Steel

NASA Astrophysics Data System (ADS)

Katiyar, Prvan Kumar; Misra, Sudhir; Mondal, K.

2018-03-01

The present work discusses the effect of pearlitic morphology on the corrosion behavior of high-carbon fully pearlitic steel in 3.5% NaCl solution. Four different types of pearlitic steels (furnace-cooled, as-received, air-cooled and forced-air-cooled) consisting of coarse, medium, fine and very fine microstructures, respectively, were tested. Electrochemical behavior of these steels was studied with the help of dynamic and linear polarization and AC impedance spectroscopic tests. The corrosion resistance improved with fineness of the microstructure in general. However, with further reduction in interlamellar spacing beyond a limit, the corrosion resistance reduced slightly. Formation of homogeneous distribution of microgalvanic cells between cementite and ferrite lamellae of fine pearlitic steel improved the corrosion resistance. However, entanglement of the lamellae of pearlite in very fine pearlitic structure as well as breaking of cementite lamellae due to finer pearlitic colonies was attributed to the higher corrosion of the forced-air-cooled steel as compared to the air-cooled steel.

Corrosion behaviour of friction-bit-joined and weld-bonded AA7075-T6/galvannealed DP980

DOE PAGES

Lim, Yong Chae; Squires, Lile; Pan, Tsung-Yu; ...

2016-12-22

Joining of aluminium alloys 7075-T6 and galvannealed dual phase 980 steel was achieved by friction bit joining (FBJ) and weld-bonding (FBJ + adhesive) processes. Accelerated laboratory-scale corrosion tests were performed on both FBJ only and weld-bonded specimens to study joint strength under a corrosive environment. Static lap shear tests showed that both FBJ only and weld-bonded cases generally retained more than 80% of the joint strength of non-corroded specimens at the end of corrosion testing. The presence of Zn/Fe coating on the steel substrate resulted in improved corrosion resistance for FBJ specimens, compared to joints produced with bare steel. Finally,more » an optical microscopy was used for cross-sectional analysis of corroded specimens. Some corrosion on the joining bit was observed near the bit head. However, the joining bit was still intact on the steel substrate, indicating that the primary bond was sound.« less

Corrosion behaviour of friction-bit-joined and weld-bonded AA7075-T6/galvannealed DP980

DOE Office of Scientific and Technical Information (OSTI.GOV)

Lim, Yong Chae; Squires, Lile; Pan, Tsung-Yu

Joining of aluminium alloys 7075-T6 and galvannealed dual phase 980 steel was achieved by friction bit joining (FBJ) and weld-bonding (FBJ + adhesive) processes. Accelerated laboratory-scale corrosion tests were performed on both FBJ only and weld-bonded specimens to study joint strength under a corrosive environment. Static lap shear tests showed that both FBJ only and weld-bonded cases generally retained more than 80% of the joint strength of non-corroded specimens at the end of corrosion testing. The presence of Zn/Fe coating on the steel substrate resulted in improved corrosion resistance for FBJ specimens, compared to joints produced with bare steel. Finally,more » an optical microscopy was used for cross-sectional analysis of corroded specimens. Some corrosion on the joining bit was observed near the bit head. However, the joining bit was still intact on the steel substrate, indicating that the primary bond was sound.« less

Interrelationship of mechanical and corrosion-mechanical characteristics of type 12KhN4MF steel

DOE Office of Scientific and Technical Information (OSTI.GOV)

Voronin, V.P.; Goncharov, A.F.; Maslov, V.A.

1985-11-01

Investigations presented include a comparative evaluation of the corrosionmechanical characteristics of specimens of high-strength chrome-nickelmolybdenum steel taking into consideration the different methods of melting of the original metal. A comparison of the corrosion-mechanical test results obtained with the results of acceptance tests are presented. A study of the fracture surfaces and the specimen material with the use of fractographic, macroscopic, and microscopic analyses is given. The systematization of the corrosion-mechanical test results with the use of methods of mathematical statistics are presented.

[Study of a new medical stainless steel].

PubMed

Ren, Yibin; Yang, Ke; Zhang, Bingchun; Yang, Huibin

2006-10-01

Medical implantable stainless steels are widely used in medical field due to their excellent properties, besides its allergic response to human body, the nickel ion released from the steels due to corrosion has the harm of malformation and carcingenesis. The mechanical property, corrosion resistance and blood compatibility of a new nickel-free stainless steel (BIOSSN4) is researched in this paper. Compared with the traditional 316L medical stainless steel, BIOSSN4 shows wide future applications because of its better combination of strength and toughness, good corrosion resistance and biocompatibility.

Efficacy of keratinocyte growth factor (palifermin) for the treatment of caustic esophageal burns

PubMed Central

NUMANOĞLU, KEMAL VARIM; TATLI, DUYGU; BEKTAŞ, SIBEL; ER, EBUBEKIR

2014-01-01

Current treatment strategies against the development of corrosive esophageal strictures remain unsatisfactory. Thus, the aim of the present study was to investigate the efficacy of keratinocyte growth factor, in the form of palifermin, for the prevention of stricture development following esophageal caustic injuries in a rat model. A total of 32 female Wistar albino rats were divided into four groups, which included the control (C), burn (B), steroid (S) and steroid plus palifermin (S/P) groups. An experimental corrosive esophageal burn model was established in the B, S and S/P groups. Weight gain was recorded and histopathological evaluation was performed for each group. Weight gain in the S and B groups was compared with the control group and statistically significant differences were observed. In addition, statistically significant differences in weight gain were observed between the S/P group and the B group. Histopathologically, statistically significant differences were identified with regard to submucosal collagen deposition, muscularis mucosa and tunica muscularis damage when comparing the B group with the C group. In addition, statistically significant differences were observed when comparing the S and S/P groups with the B group. Furthermore, significant submucosal collagen deposition and tunica muscularis damage were observed in the S group when compared with the S/P group. The stenosis indexes in the C and S groups were significantly lower compared with the B group. In addition, the stenosis index in the S/P group was significantly lower compared with the S group. To the best of our knowledge, the present study is the first to investigate the effect of palifermin on corrosive esophageal burns. The addition of palifermin to the corrosive esophageal burn standard treatment regimen was found to reduce the degree of fibrosis and ameliorate histopathological damage in an experimental model of corrosive esophagitis in rats. PMID:25187801

Carbon Corrosion in PEM Fuel Cells and the Development of Accelerated Stress Tests

DOE PAGES

Macauley, Natalia; Papadias, Dennis D.; Fairweather, Joseph; ...

2018-03-15

Here, carbon corrosion is an important degradation mechanism that can impair PEMFC performance through the destruction of catalyst connectivity, collapse of the electrode pore structure, loss of hydrophobic character, and an increase of the catalyst particle size. In this study, carbon corrosion was quantified in situ by measurement of carbon dioxide in the fuel cell exhaust gases through non-dispersive infrared spectroscopy during simulated drive cycle operations consisting of potential cycling with varying upper and lower potential limits. These studies were conducted for three different types of carbon supports. A reduction in the catalyst layer thickness was observed during a simulatedmore » drive cycle operation with a concomitant decrease in catalyst layer porosity, which led to performance losses due to increased mass transport limitations. The observed thickness reduction was primarily due to compaction of the catalyst layer, with the actual mass of carbon oxidation (loss) contributing only a small fraction (< 20%). The dynamics of carbon corrosion are presented along with a model that simulates the transient and dynamic corrosion rates observed in our experiments. Accelerated carbon corrosion stress tests are presented and their effects are compared to those observed for the drive cycle test.« less

Carbon Corrosion in PEM Fuel Cells and the Development of Accelerated Stress Tests

DOE Office of Scientific and Technical Information (OSTI.GOV)

Macauley, Natalia; Papadias, Dennis D.; Fairweather, Joseph

Here, carbon corrosion is an important degradation mechanism that can impair PEMFC performance through the destruction of catalyst connectivity, collapse of the electrode pore structure, loss of hydrophobic character, and an increase of the catalyst particle size. In this study, carbon corrosion was quantified in situ by measurement of carbon dioxide in the fuel cell exhaust gases through non-dispersive infrared spectroscopy during simulated drive cycle operations consisting of potential cycling with varying upper and lower potential limits. These studies were conducted for three different types of carbon supports. A reduction in the catalyst layer thickness was observed during a simulatedmore » drive cycle operation with a concomitant decrease in catalyst layer porosity, which led to performance losses due to increased mass transport limitations. The observed thickness reduction was primarily due to compaction of the catalyst layer, with the actual mass of carbon oxidation (loss) contributing only a small fraction (< 20%). The dynamics of carbon corrosion are presented along with a model that simulates the transient and dynamic corrosion rates observed in our experiments. Accelerated carbon corrosion stress tests are presented and their effects are compared to those observed for the drive cycle test.« less

Effect of titanium nitride/titanium coatings on the stress corrosion of nickel-titanium orthodontic archwires in artificial saliva

NASA Astrophysics Data System (ADS)

Liu, Jia-Kuang; Liu, I.-Hua; Liu, Cheng; Chang, Chen-Jung; Kung, Kuan-Chen; Liu, Yen-Ting; Lee, Tzer-Min; Jou, Jin-Long

2014-10-01

The purpose of this investigation was to develop titanium nitride (TiN)/titanium (Ti) coating on orthodontic nickel-titanium (NiTi) wires and to study the stress corrosion of specimens in vitro, simulating the intra-oral environment in as realistic a manner as possible. TiN/Ti coatings were formed on orthodontic NiTi wires by physical vapor deposition (PVD). The characteristics of untreated and TiN/Ti-coated NiTi wires were evaluated by measurement of corrosion potential (Ecorr), corrosion current densities (Icorr), breakdown potential (Eb), and surface morphology in artificial saliva with different pH and three-point bending conditions. From the potentiodynamic polarization and SEM results, the untreated NiTi wires showed localized corrosion compared with the uniform corrosion observed in the TiN/Ti-coated specimen under both unstressed and stressed conditions. The bending stress influenced the corrosion current density and breakdown potential of untreated specimens at both pH 2 and pH 5.3. Although the bending stress influenced the corrosion current of the TiN/Ti-coated specimens, stable and passive corrosion behavior of the stressed specimen was observed even at 2.0 V (Ag/AgCl). It should be noted that the surface properties of the NiTi alloy could determine clinical performance. For orthodontic application, the mechanical damage destroys the protective oxide film of NiTi; however, the self-repairing capacity of the passive film of NiTi alloys is inferior to Ti in chloride-containing solutions. In this study, the TiN coating was found able to provide protection against mechanical damage, while the Ti interlayer improved the corrosion properties in an aggressive environment.

Potentiodynamic polarization study of the in vitro corrosion behavior of 3 high-palladium alloys and a gold-palladium alloy in 5 media.

PubMed

Sun, Desheng; Monaghan, Peter; Brantley, William A; Johnston, William M

2002-01-01

Corrosion of cast alloy restorations may lead to their failure or adversely affect their biocompatibility. Although some documentation of the corrosion behavior of the high-palladium dental alloys exists, questions remain about their corrosion resistance and mechanisms. This study compared the in vitro corrosion characteristics of 3 high-palladium alloys and 1 gold-palladium alloy in simulated body fluid and oral environments. Two Pd-Cu-Ga alloys and 1 Pd-Ga alloy were selected; an Au-Pd alloy served as the control. The corrosion behavior for the as-cast and simulated porcelain-firing (heat-treated) conditions of each alloy (N = 5) was evaluated in 0.9% NaCl, 0.09% NaCl, and Fusayama solutions. Heat-treated specimens of each alloy (N = 5) were also tested in N(2)-deaerated 0.09% NaCl and Fusayama solutions (pH 4). After immersion in the electrolyte for 24 hours, the open-circuit potential (OCP) was measured, and linear polarization was performed from -20 mV to +20 mV (vs. OCP) at a scanning rate of 0.125 mV/s. Cyclic polarization was performed from -300 mV to +1000 mV and back to -300 mV (vs. OCP) at a scanning rate of 1 mV/s. Data were evaluated with analysis of variance and the Ryan-Einot-Gabriel-Welsch multiple-range test (alpha=.05). The OCP of each alloy varied with the condition (as-cast or heat-treated) and electrolyte used. Corrosion resistance was similar for the 4 alloys tested. For cyclic polarization, all alloys showed active-passive or spontaneous passive behavior in nearly all electrolytes. During some reverse scans, the 3 high-palladium alloys displayed 3 or 5 anodic peaks. No positive hysteresis was observed for any of the alloy/electrolyte combinations evaluated. The corrosion resistances of the 3 high-palladium alloys in simulated body fluid and oral environments were comparable to that of the gold-palladium alloy. The similar corrosion resistance for the 3 high-palladium alloys was attributed to their high noble metal content and theorized stable structure at the submicron level. Selective corrosion of different phases and elements, surface enrichment of palladium, and adsorption of species are possible corrosion mechanisms. The cyclic polarization results suggest that none of the 4 alloys would be prone to pitting or crevice corrosion under in vivo conditions, but crevice conditions should nonetheless be avoided for these alloys in the oral environment.

Sub-categorisation of skin corrosive chemicals by the EpiSkin™ reconstructed human epidermis skin corrosion test method according to UN GHS: revision of OECD Test Guideline 431.

PubMed

Alépée, N; Grandidier, M H; Cotovio, J

2014-03-01

The EpiSkin™ skin corrosion test method was formally validated and adopted within the context of OECD TG 431 for identifying corrosive and non-corrosive chemicals. The EU Classification, Labelling and Packaging Regulation (EU CLP) system requires the sub-categorisation of corrosive chemicals into the three UN GHS optional subcategories 1A, 1B and 1C. The present study was undertaken to investigate the usefulness of the validated EpiSkin™ test method to identify skin corrosive UN GHS Categories 1A, 1B and 1C using the original and validated prediction model and adapted controls for direct MTT reduction. In total, 85 chemicals selected by the OECD expert group on skin corrosion were tested in three independent runs. The results obtained were highly reproducible both within (>80%) and between (>78%) laboratories when compared with historical data. Moreover the results obtained showed that the EpiSkin™ test method is highly sensitive (99%) and specific (80%) in discriminating corrosive from non-corrosive chemicals and allows reliable and relevant identification of the different skin corrosive UN GHS subcategories, with high accuracies being obtained for both UN GHS Categories 1A (83%) and 1B/1C (76%) chemicals. The overall accuracy of the test method to subcategorise corrosive chemicals into three or two UN GHS subcategories ranged from 75% to 79%. Considering those results, the revised OECD Test Guideline 431 permit the use of EpiSkin™ for subcategorising corrosive chemicals into at least two classes (Category 1A and Category 1B/1C). Copyright © 2013. Published by Elsevier Ltd.

A new, bright and hard aluminum surface produced by anodization

NASA Astrophysics Data System (ADS)

Hou, Fengyan; Hu, Bo; Tay, See Leng; Wang, Yuxin; Xiong, Chao; Gao, Wei

2017-07-01

Anodized aluminum (Al) and Al alloys have a wide range of applications. However, certain anodized finishings have relatively low hardness, dull appearance and/or poor corrosion resistance, which limited their applications. In this research, Al was first electropolished in a phosphoric acid-based solution, then anodized in a sulfuric acid-based solution under controlled processing parameters. The anodized specimen was then sealed by two-step sealing method. A systematic study including microstructure, surface morphology, hardness and corrosion resistance of these anodized films has been conducted. Results show that the hardness of this new anodized film was increased by a factor of 10 compared with the pure Al metal. Salt spray corrosion testing also demonstrated the greatly improved corrosion resistance. Unlike the traditional hard anodized Al which presents a dull-colored surface, this newly developed anodized Al alloy possesses a very bright and shiny surface with good hardness and corrosion resistance.

The corrosion protection of aluminum by various anodizing treatments

NASA Technical Reports Server (NTRS)

Danford, Merlin D.

1989-01-01

Corrosion protection to 6061-T6 aluminum, afforded by both teflon-impregnated anodized coats (Polylube and Tufram) and hard-anodized coats (water sealed and dichromate sealed), was studied at both pH 5.5 and pH 9.5, with an exposure period of 28 days in 3.5 percent NaCl solution (25 C) for each specimen. In general, corrosion protection for all specimens was better at pH 9.5 than at pH 5.5. Protection by a Tufram coat proved superior to that afforded by Polylube at each pH, with corrosion protection by the hard-anodized, water-sealed coat at pH 9.5 providing the best protection. Electrochemical work in each case was corroborated by microscopic examination of the coats after exposure. Corrosion protection by Tufram at pH 9.5 was most comparable to that of the hard-anodized samples, although pitting and some cracking of the coat did occur.

Review of SiCf/SiCm corrosion, erosion and erosion-corrosion in high temperature helium relevant to GFR conditions

NASA Astrophysics Data System (ADS)

Fitzgerald, Kerr; Shepherd, Daniel

2018-01-01

The good thermal, mechanical and nuclear properties of silicon carbide composites (SiCf/SiCm) has led to their proposal as a gas-cooled fast reactor (GFR) fuel cladding material. Accordingly, previous studies on the corrosion, erosion and erosion-corrosion of SiCf/SiCm have been reviewed. A significant amount of corrosion data was compared for various SiCf/SiCm types tested under different conditions, which suggested that it may be suitable for use in a GFR. However some issues remain, specifically the potential for removal by oxidation of the pyrolytic carbon (PyC) interphase below 900 °C and highly damaging active oxidation at temperatures above 1200 °C. Few relevant papers were found on the erosion and erosion-corrosion behaviour of SiCf/SiCm, though those that were did indicate improved erosion resistance compared to metals. However, most data concerned particulate rather than gas erosion, and at relatively low temperatures. Exacerbation of erosion by corrosion (and vice versa) is hypothesised due to both phenomena potentially causing and being worsened by increased composite porosity. The possibility for this to be further exacerbated mechanically was also identified e.g. by surface damage or by crack formation and growth. The potential impact of irradiation in fast reactor conditions also needs to be better understood. Overall, limited data was found that is representative of anticipated GFR conditions and only in the form of separate effect corrosion tests, thus highlighting the need for erosion and combined effect experiments to progress SiCf/SiCm towards qualification as GFR fuel cladding. Finally, some potential means for improving performance have been identified including environmental adjustment and/or alternative composite design.

Effects of cement alkalinity, exposure conditions and steel-concrete interface on the time-to-corrosion and chloride threshold for reinforcing steel in concrete

NASA Astrophysics Data System (ADS)

Nam, Jingak

Effects of (1) cement alkalinity (low, normal and high), (2) exposure conditions (RH and temperature), (3) rebar surface condition (as-received versus cleaned) and (4) density and distribution of air voids at the steel-concrete interface on the chloride threshold and time-to-corrosion for reinforcing steel in concrete have been studied. Also, experiments were performed to evaluate effects of RH and temperature on the diffusion of chloride in concrete and develop a method for ex-situ pH measurement of concrete pore water. Once specimens were fabricated and exposed to a corrosive chloride solution, various experimental techniques were employed to determine time-to-corrosion, chloride threshold, diffusion coefficient and void density along the rebar trace as well as pore water pH. Based upon the resultant data, several findings related to the above parameters have been obtained as summarized below. First, time for the corrosion initiation was longest for G109 concrete specimens with high alkalinity cement (HA). Also, chloride threshold increased with increasing time-to-corrosion and cement alkalinity. Consequently, the HA specimens exhibited the highest chloride threshold compared to low and normal alkalinity ones. Second, high temperature and temperature variations reduced time-to-corrosion of reinforcing steel in concrete since chloride diffusion was accelerated at higher temperature and possibly by temperature variations. The lowest chloride threshold values were found for outdoor exposed specimens suggesting that variation of RH or temperature (or both) facilitated rapid chloride diffusion. Third, an elevated time-to-corrosion and chloride threshold values were found for the wire brushed steel specimens compared to as-received ones. The higher ratio of [OH-]/[Fe n+] on the wire brushed steel surface compared to that of as-received case can be the possible cause because the higher ratio of this parameter enables the formation of a more protective passive film on the rebar. Fourth, voids at the steel-concrete interface facilitated passive film breakdown and onset of localized corrosion. This tendency for corrosion initiation increased in proportion to void size irrespective of specimen type. Also, [Cl -]th decreased with increasing void diameter. In addition, new ex-situ leaching method for determining concrete pore water alkalinity was developed.

Oleic acid-grafted chitosan/graphene oxide composite coating for corrosion protection of carbon steel.

PubMed

Fayyad, Eman M; Sadasivuni, Kishor Kumar; Ponnamma, Deepalekshmi; Al-Maadeed, Mariam Al Ali

2016-10-20

An anticorrosion coating film based on the formation of nanocomposite coating is reported in this study. The composite consisted of chitosan (green matrix), oleic acid, and graphene oxide (nano filler). The nanocomposite coating was arranged on the surface of carbon steel, and the corrosion resistance was monitored using electrochemical impedance spectroscopy (EIS) and potentiodynamic polarization (PP). Compared to the pure chitosan (CS) coating, the corrosion resistance of oleic acid-modified chitosan/graphene oxide film (CS/GO-OA) is increased by 100 folds. Since the well-dispersed smart grafted nanolayers delayed the penetration rate of corrosive species and thus maintained long term anticorrosive stability which is correlated with hydrophobicity and permeability. Copyright © 2016 Elsevier Ltd. All rights reserved.

Corrosion behavior of stainless steel weldments in physiological solutions

NASA Astrophysics Data System (ADS)

Farooq, A.; Azam, M.; Deen, K. M.

2018-01-01

In this study corrosion behavior of TIG welded 316L stainless steel plates in simulated biological solutions is investigated. The mechanical testing results showed slight decrease in ductility after welding and the fracture surface represented mixed cleavage and inclusions containing dimple structure. The heat affected and weld zone (WZ) demonstrated higher corrosion potential and relatively large pitting tendency than base metal (BM) in both Hank’s and Ringer’s solution. The formation of delta (δ) ferrite in the heat affected and WZ decreased the corrosion resistance as confirmed from potentiodynamic Tafel scans. The decrease in pitting resistance and lower protection tendency of the WZ compared to BM and heat affected zone was also quantified from the cyclic polarization trends.

Comparative study on lithium borates as corrosion inhibitors of aluminum current collector in lithium bis(fluorosulfonyl)imide electrolytes

NASA Astrophysics Data System (ADS)

Park, Kisung; Yu, Sunghun; Lee, Chulhaeng; Lee, Hochun

2015-11-01

Lithium bis(fluorosulfonyl)imide (LiFSI) is a promising salt that can possibly overcome the limitations of lithium hexafluorophosphate (LiPF6) in current Li-ion batteries (LIBs). Aluminum (Al) corrosion issue, however, is a major bottleneck for the wide use of LiFSI. This study investigates lithium borate salts as Al corrosion inhibitors in LiFSI electrolytes. Through a systematic comparison among lithium tetrafluoroborate (LiBF4), lithium bis(oxalato)borate (LiBOB), and lithium difluoro(oxalato)borate (LiDFOB), and LiPF6, the inhibition ability of the additives is revealed to be in the following order: LiDFOB > LiBF4 ≈ LiPF6 > LiBOB. In particular, the inhibition effect of LiDFOB is outstanding; the anodic behavior of Al in 0.8 M LiFSI + 0.2 M LiDFOB ethylene carbonate (EC)-based electrolyte is comparable to that of corrosion-free 1 M LiPF6 solution. The superior inhibition ability of LiDFOB is attributed to the formation of a passive layer composed of Al-F, Al2O3, and B-O species, as evidenced by X-ray photoelectron spectroscopy (XPS) measurements. A LiCoO2/graphite cell with 0.8 M LiFSI + 0.2 M LiDFOB electrolyte exhibits a rate capability comparable to a cell with 1 M LiPF6 solution, whereas a cell with 0.8 M LiFSI solution without LiDFOB suffers from poor power performance resulting from severe Al corrosion.

A comparative study of the in vitro corrosion behavior and cytotoxicity of a superferritic stainless steel, a Ti-13Nb-13Zr alloy, and an austenitic stainless steel in Hank's solution.

PubMed

Assis, S L; Rogero, S O; Antunes, R A; Padilha, A F; Costa, I

2005-04-01

In this study, the in vitro corrosion resistance of a superferritic stainless steel in naturally aerated Hank's solution at 37 degrees C has been determined to evaluate the steel for use as a biomaterial. The potentiodynamic polarization method and electrochemical impedance spectroscopy (EIS) were used to determine the corrosion resistance. The polarization results showed very low current densities at the corrosion potential and electrochemical behavior typical of passive metals. At potentials above 0.75 V (SCE), and up to that of the oxygen evolution reaction, the superferritic steel exhibited transpassive behavior followed by secondary passivation. The superferritic stainless steel exhibited high pitting resistance in Hank's solution. This steel did not reveal pits even after polarization to 3000 mV (SCE). The EIS results indicated high impedance values at low frequencies, supporting the results obtained from the polarization measurements. The results obtained for the superferritic steel have been compared with those of the Ti-13Nb-13Zr alloy and an austenitic stainless steel, as Ti alloys are well known for their high corrosion resistance and biocompatibility, and the austenitic stainless steel is widely used as an implant material. The cytotoxicity tests indicated that the superferritic steel, the austenitic steel, and the Ti-13Nb-13Zr alloy were not toxic. Based on corrosion resistance and cytotoxicity results, the superferritic stainless steel can be considered as a potential biomaterial. (c) 2005 Wiley Periodicals, Inc.

Characterization and corrosion property of nano-rod-like HA on fluoride coating supported on Mg-Zn-Ca alloy.

PubMed

Feng, Yashan; Zhu, Shijie; Wang, Liguo; Chang, Lei; Yan, Bingbing; Song, Xiaozhe; Guan, Shaokang

2017-06-01

The poor corrosion resistance of biodegradable magnesium alloys is the dominant factor that limits their clinical application. In this study, to deal with this challenge, fluoride coating was prepared on Mg-Zn-Ca alloy as the inner coating and then hydroxyapatite (HA) coating as the outer coating was deposited on fluoride coating by pulse reverse current electrodeposition (PRC-HA/MgF 2 ). As a comparative study, the microstructure and corrosion properties of the composite coating with the outer coating fabricated by traditional constant current electrodeposition (TED-HA/MgF 2 ) were also investigated. Scanning electron microscopy (SEM) images of the coatings show that the morphology of PRC-HA/MgF 2 coating is dense and uniform, and presents nano-rod-like structure. Compared with that of TED-HA/MgF 2 , the corrosion current density of Mg alloy coated with PRC-HA/MgF 2 coatings decreases from 5.72 × 10 -5 A/cm 2 to 4.32 × 10 -7 A/cm 2 , and the corrosion resistance increases by almost two orders of magnitude. In immersion tests, samples coated with PRC-HA/MgF 2 coating always show the lowest hydrogen evolution amount, and could induce deposition of the hexagonal structure-apatite on the surface rapidly. The results show that the corrosion resistance and the bioactivity of the coatings have been improved by adopting double-pulse current mode in the process of preparing HA on fluoride coating, and the PRC-HA/MgF 2 coating is worth of further investigation.

Assessment of nickel titanium and beta titanium corrosion resistance behavior in fluoride and chloride environments.

PubMed

Kassab, Elisa J; Gomes, José Ponciano

2013-09-01

To assess the influence of fluoride concentration on the corrosion behavior of nickel titanium (NiTi) superelastic wire and to compare the corrosion resistance of NiTi with that of beta titanium alloy in physiological solution with and without addition of fluoride. NiTi corrosion resistance was investigated through electrochemical impedance spectroscopy and anodic polarization in sodium chloride (NaCl 0.15 M) with and without addition of 0.02 M sodium fluoride (NaF), and the results were compared with those associated with beta titanium. The influence of fluoride concentration on NiTi corrosion behavior was assessed in NaCl (0.15 M) with and without 0.02, 0.04, 0.05, 0.07, and 0.12 M NaF solution. Galvanic corrosion between NiTi and beta titanium were investigated. All samples were characterized by scanning electron microscopy. Polarization resistance decreased when NaF concentration was increased, and, depending on NaF concentration, NiTi can suffer localized or generalized corrosion. In NaCl solution with 0.02 M NaF, NiTi suffer localized corrosion, while beta titanium alloys remained passive. Current values near zero were observed by galvanic coupling of NiTi and beta titanium. There is a decrease in NiTi corrosion resistance in the presence of fluoride. The corrosion behavior of NiTi alloy depends on fluoride concentration. When 0.02 and 0.04 M of NaF were added to the NaCl solution, NiTi presented localized corrosion. When NaF concentration increased to 0.05, 0.07, and 0.12 M, the alloy presented general corrosion. NiTi corrosion resistance behavior is lower than that of beta titanium. Galvanic coupling of these alloys does not increase corrosion rates.

Skin corrosion test: a comparison between reconstructed human epidermis and full thickness skin models.

PubMed

Catarino, Carolina Motter; do Nascimento Pedrosa, Tatiana; Pennacchi, Paula Comune; de Assis, Silvia Romano; Gimenes, Fabrícia; Consolaro, Márcia Edilaine Lopes; de Moraes Barros, Silvia Berlanga; Maria-Engler, Silvya Stuchi

2018-04-01

Currently, there is a strong global trend towards the development of in vitro models to replace the use of animals in safety evaluation tests. Reconstructed Human Epidermis (RHE) models have been employed as an alternative method to animal testing of skin corrosion and irritation potential of chemical compounds. However, the consequences of an absence of the dermal compartment in these models should be considered since the cross-talk between fibroblasts and keratinocytes is fundamental for promoting proper epidermal stratification, homeostasis, inflammatory response and wound healing. In this study, we compare in-house developed models of Reconstructed Human Epidermis (i.e. USP-RHE) and full thickness skin (i.e. USP-FTS) regarding their response when submitted to skin corrosion assays, based on Guideline 431 (OECD). The results show that both models correctly classified the four substances tested (2-phenylethyl bromide, benzylacetone, lactic acid, octanoic acid) as corrosive or non-corrosive. Furthermore, we have demonstrated higher cell viability of the USP-FTS model compared to the USP-RHE model, a sign of its improved barrier function, following the exposure to the substances test on the corrosion assay. This emphasizes the importance of employing in vitro models that are more physiologically relevant and that better mimic the in vivo situation for the toxicological screening of substances. Copyright © 2018 Elsevier B.V. All rights reserved.

Effects of nitrogen in shielding gas on microstructure evolution and localized corrosion behavior of duplex stainless steel welding joint

NASA Astrophysics Data System (ADS)

Zhang, Zhiqiang; Jing, Hongyang; Xu, Lianyong; Han, Yongdian; Zhao, Lei; Zhou, Chao

2017-05-01

The effects of nitrogen addition in shielding gas on microstructure evolution and localized corrosion behavior of duplex stainless steel (DSS) welds were studied. N2-supplemented shielding gas facilitated the primary austenite formation, suppressed the Cr2N precipitation in weld root, and increased the microhardnesses of weld metal. Furthermore, N2-supplemented shielding gas increased pitting resistance equivalent number (PREN) of austenite, but which decreased slightly PREN of ferrite. The modified double loop electrochemical potentiokinetic reactivation in 2 M H2SO4 + 1 M HCl was an effective method to study the localized corrosion of the different zones in the DSS welds. The adding 2% N2 to pure Ar shielding gas improved the localized corrosion resistance in the DSS welds, which was due to compensation for nitrogen loss and promoting nitrogen further solution in the austenite phases, suppression of the Cr2N precipitation in the weld root, and increase of primary austenite content with higher PREN than the ferrite and secondary austenite. Secondary austenite are prone to selective corrosion because of lower PREN compared with ferrite and primary austenite. Cr2N precipitation in the pure Ar shielding weld root and heat affected zone caused the pitting corrosion within the ferrite and the intergranular corrosion at the ferrite boundary. In addition, sigma and M23C6 precipitation resulted in the intergranular corrosion at the ferrite boundary.

Corrosion resistance of monolayer hexagonal boron nitride on copper

PubMed Central

Mahvash, F.; Eissa, S.; Bordjiba, T.; Tavares, A. C.; Szkopek, T.; Siaj, M.

2017-01-01

Hexagonal boron nitride (hBN) is a layered material with high thermal and chemical stability ideal for ultrathin corrosion resistant coatings. Here, we report the corrosion resistance of Cu with hBN grown by chemical vapor deposition (CVD). Cyclic voltammetry measurements reveal that hBN layers inhibit Cu corrosion and oxygen reduction. We find that CVD grown hBN reduces the Cu corrosion rate by one order of magnitude compared to bare Cu, suggesting that this ultrathin layer can be employed as an atomically thin corrosion-inhibition coating. PMID:28191822

The Role of Deformation and Microchemistry in the Corrosion Processes of Type 304 Stainless Steel in Simulated Pressurized Water Reactor Environments

NASA Astrophysics Data System (ADS)

Fisher, Kevin B.

Degradation of structural components in nuclear environments is a limiting factor in the lifetime of nuclear power plants. Despite decades of research on the topic, there are still aspects of the degradation phenomena that are not well understood, leading to premature failure of components that can be both expensive to repair and potentially dangerous. The current work addresses the role of material deformation on the corrosion phenomena of 304 SS in a simulated nuclear reactor environment by studying the relationship of the material microstructure and microchemistry with the resulting corrosion products using a multiscale analysis approach. The general corrosion phenomenon was studied in relation to the surface deformation of the material, and it was determined that surface deformation not only increases the rate of oxidation, but also has a pronounced impact on the microchemical structure of the oxide film when compared to undeformed material. These findings were applied to understanding the role of deformation in the more complex corrosion phenomena of stress corrosion cracking (SCC) and corrosion fatigue cracking (CFC). In SCC experiments, material deformation in the form of cold work played a synergistic role with unique microchemical features of the materials studied to promote the cracking process under certain environmental and material heat treatment conditions. Despite the fact that the materials studied were low carbon heats of 304L SS thought to be immune to the sensitization and therefore resistant to SCC, elevated boron and delta ferrites in the material were implicated in the SCC susceptibility after heat treatment. On the other hand, low levels of residual deformation played only a minor role in the corrosion processes occurring during CFC experiments over a wide range of rise times. Instead, deformation was suspected to play a larger role in the mechanical cracking response of the material. By studying multiple corrosion processes of 304 SS a greater understanding of the role of deformation and microchemical factors in the related corrosion phenomena has been achieved, and provides evidence that material and component fabrication, in terms of surface and bulk deformation, material microchemistry, and heat treatment must be considered to avoid degradation issues.

An investigation into the effects of polishing on surface hardness and corrosion of orthodontic archwires.

PubMed

Hunt, N P; Cunningham, S J; Golden, C G; Sheriff, M

1999-10-01

The purpose of this study was to investigate the effect of surface roughness on the relative corrosion rates of wires of four alloys-stainless steel, nickel titanium, cobalt chromium, and beta titanium. Batches of wire were divided into two groups. Wires in one group were industrially polished to provide a uniform surface finish; wires in the other group were left for comparison "as received." Wire diameter, hardness, and relative corrosion rates were compared within groups before and after polishing. Comparisons were also made across the four groups of alloys. The samples of as-received wires showed variations in surface finish, with beta titanium having the roughest appearance and cobalt chromium the smoothest. Nickel titanium and stainless steel surfaces were similar. Polishing provided a more uniform finish, but significantly reduced the diameter of the wires. Microhardness testing of wire surfaces of each alloy indicated that no significant work-hardening occurred as a result of polishing. The relative corrosion rates (expressed in terms of corrosion current density) in a 0.9% sodium chloride solution were estimated using the electrochemical technique of polarization resistance. Nickel titanium wires exhibited the greatest corrosion current density in the as-received state. Polishing significantly reduced the corrosion rate of nickel titanium, such that comparison between the four alloys in the polished state revealed no significant difference in their relative corrosion rate/corrosion current density.

Mitigation of corrosion attack on carbon steel coated cermet alloy in different anion contents

NASA Astrophysics Data System (ADS)

Khalid, Muhamad Azrin Mohd; Ismail, Azzura

2017-12-01

This research study evaluated the corrosion mechanism attack on carbon steel coated with cermet alloys (WC-9% Ni) in seawater at different sulphate-to-chloride ratios. The four different sulphate-to-chloride ratios were synthesised with the same seawater salinity of 3.5 % and same pH of real seawater. The corrosion tests involved immersion and electrochemical tests. The immersion test is used to determine the cermet coating ability to withstand the corrosion attack based on different ratios of anions present in the seawater at different periods of immersion. The corrosion attack was characterized by optical and Scanning Electron Microscopy (SEM). The aggressive anions present in the seawater influenced the corrosion attack on the cermet coating. For immersion test, results revealed that increasing sulphate more than chloride, increased the weight loss of cermets. The electrochemistry analysis showed that the passive layer forms on cermet coating prevented the material from further corrosion attack. However, due to its porosity, the passive layer collapsed and exposed the material for other corrosion reaction. For electrochemical test, the result shows that the solution with sulphate-to-chloride ratio of 0.14 (real seawater) has the highest corrosion current and Open Circuit Potential (OCP) compared to other solutions (different sulphate-to-chloride ratio). In conclusion, sulfate and chloride show their competition to attack the cermet coating on carbon steel and the higher the amount of chloride present in seawater, the higher the corrosion rate and pits formed on the cermet coating.

An electrochemical investigation of TMJ implant metal alloys in an artificial joint fluid environment: the influence of pH variation.

PubMed

Royhman, Dmitry; Radhakrishnan, Rashmi; Yuan, Judy Chia-Chun; Mathew, Mathew T; Mercuri, Louis G; Sukotjo, Cortino

2014-10-01

To investigate the corrosion behaviour of commonly used TMJ implants alloys (CoCrMo and Ti6Al4V) under simulated physiological conditions. Corrosion behaviour was evaluated using standard electrochemical corrosion techniques and galvanic corrosion techniques as per ASTM standards. Standard electrochemical tests (E(corr), I(corr), R(p) and C(f)) were conducted in bovine calf serum (BCS), as a function of alloys type and different pHs. Galvanic corrosion tests were conducted in BCS at a pH of 7.6. Alloy surfaces were characterized using white-light interferometry (WLI) and scanning electron microscopy (SEM). The potentiodynamic test results exhibited the enhanced passive layer growth and a better corrosion resistance of Ti6Al4V compared to CoCrMo. Electrochemical impedance spectroscopy measurements demonstrated the influence of protein as a function of pH on corrosion mechanisms/kinetics. Galvanic coupling was not a major contributor to corrosion. SEM and WLI images demonstrated a significantly higher in surface roughness in CoCrMo after corrosion. The results of this study suggest that Ti6Al4V shows superior corrosion behaviour to CoCrMo due to its strong passive layer, simulated joint fluid components can affect the electrochemical nature of the metal/electrolyte interface as a function of pH, and the galvanic effect of coupling CoCrMo and Ti6Al4V in a single joint is weak. Published by Elsevier Ltd.

In vitro and in vivo corrosion evaluation of nickel-chromium- and copper-aluminum-based alloys.

PubMed

Benatti, O F; Miranda, W G; Muench, A

2000-09-01

The low resistance to corrosion is the major problem related to the use of copper-aluminum alloys. This in vitro and in vivo study evaluated the corrosion of 2 copper-aluminum alloys (Cu-Al and Cu-Al-Zn) compared with a nickel-chromium alloy. For the in vitro test, specimens were immersed in the following 3 corrosion solutions: artificial saliva, 0.9% sodium chloride, and 1.0% sodium sulfide. For the in vivo test, specimens were embedded in complete dentures, so that one surface was left exposed. The 3 testing sites were (1) close to the oral mucosa (partial self-cleaning site), (2) surface exposed to the oral cavity (self-cleaning site), and (3) specimen bottom surface exposed to the saliva by means of a tunnel-shaped perforation (non-self-cleaning site). Almost no corrosion occurred with the nickel-chromium alloy, for either the in vitro or in vivo test. On the other hand, the 2 copper-aluminum-based alloys exhibited high corrosion in the sulfide solution. These same alloys also underwent high corrosion in non-self-cleaning sites for the in vivo test, although minimal attack was observed in self-cleaning sites. The nickel-chromium alloy presented high resistance to corrosion. Both copper-aluminum alloys showed considerable corrosion in the sulfide solution and clinically in the non-self-cleaning site. However, in self-cleaning sites these 2 alloys did not show substantial corrosion.

Corrosion behavior of 2205 duplex stainless steel.

PubMed

Platt, J A; Guzman, A; Zuccari, A; Thornburg, D W; Rhodes, B F; Oshida, Y; Moore, B K

1997-07-01

The corrosion of 2205 duplex stainless steel was compared with that of AISI type 316L stainless steel. The 2205 stainless steel is a potential orthodontic bracket material with low nickel content (4 to 6 wt%), whereas the 316L stainless steel (nickel content: 10 to 14 wt%) is a currently used bracket material. Both stainless steels were subjected to electrochemical and immersion (crevice) corrosion tests in 37 degrees C, 0.9 wt% sodium chloride solution. Electrochemical testing indicates that 2205 has a longer passivation range than 316L. The corrosion rate of 2205 was 0.416 MPY (milli-inch per year), whereas 316L exhibited 0.647 MPY. When 2205 was coupled to 316L with equal surface area ratio, the corrosion rate of 2205 reduced to 0.260 MPY, indicating that 316L stainless steel behaved like a sacrificial anode. When 316L is coupled with NiTi, TMA, or stainless steel arch wire and was subjected to the immersion corrosion test, it was found that 316L suffered from crevice corrosion. On the other hand, 2205 stainless steel did not show any localized crevice corrosion, although the surface of 2205 was covered with corrosion products, formed when coupled to NiTi and stainless steel wires. This study indicates that considering corrosion resistance, 2205 duplex stainless steel is an improved alternative to 316L for orthodontic bracket fabrication when used in conjunction with titanium, its alloys, or stainless steel arch wires.

Copper-nickel superalloys as inert alloy anodes for aluminum electrolysis

NASA Astrophysics Data System (ADS)

Shi, Zhongning; Xu, Junli; Qiu, Zhuxian; Wang, Zhaowen; Gao, Bingliang

2003-11-01

The superalloys Cu-Ni-Al, Cu-Ni-Fe, and Cu-Ni-Cr were studied as anodes for aluminum electrolysis. The alloys were tested for corrosion in acidic electrolyte molten salt and for oxidation in both air and oxygen. The results showed that the Cu-Ni-Al anodes possess excellent resistance to oxidation and corrosion, and the oxidation rates of Cu-Ni-Fe and Cu-Ni-Al anodes were slower than those of pure copper or nickel. During electrolysis, the cell voltage of the Cu-Ni-Al anode was affected most by the concentration of alumina in cryolite molten salt. The Cu-Ni-Fe anode exhibited corrosion resistance in electrolyte molten salt. Comparatively, the Cu-Ni-Cr anode showed poor resistance to oxidation and corrosion. The testing found that further study is warranted on the use of Cu-Ni-Al and Cu-Ni-Fe as inert alloy anodes.

Corrosion Behavior of Aluminum Alloys in Acidic Media

NASA Astrophysics Data System (ADS)

Ramli, Rosliza; Seoh, S. Y.; Nik, W. B. Wan; Senin, H. B.

2007-05-01

The corrosion inhibition of Al and its alloys are the subject of tremendous technological importance due to the increased industrial applications of these materials. This study will report the results of weight loss, polarization and electrochemical impedance spectroscopic (EIS) measurements on the corrosion inhibition of AA6061 and AA6063 aluminum alloys in acidic media using sodium benzoate as an inhibitor. The results showed that addition of sodium benzoate retards the rate of dissolution and hence inhibits the corrosion of the aluminum alloy in acidic media. The inhibition efficiency increases with the increase of immersion time in acetic acid however it displays a different behavior in sulfuric acid. Langmuir adsorption isotherm fits well with the experimental data. EIS studies showed that there was a significant increase in overall resistance after addition of sodium benzoate, when compared to the case without inhibitor. Langmuir adsorption isotherm fits well with the experimental data.

Effects of Variations in Salt-Spray Conditions on the Corrosion Mechanisms of an AE44 Magnesium Alloy

DOE PAGES

Martin, Holly J.; Horstemeyer, M. F.; Wang, Paul T.

2010-01-01

The understanding of how corrosion affects magnesium alloys is of utmost importance as the automotive and aerospace industries have become interested in the use of these lightweight alloys. However, the standardized salt-spray test does not produce adequate corrosion results when compared with field data, due to the lack of multiple exposure environments. This research explored four test combinations through three sets of cycles to determine how the corrosion mechanisms of pitting, intergranular corrosion, and general corrosion were affected by the environment. Of the four test combinations, Humidity-Drying was the least corrosive, while the most corrosive test condition was Salt Spray-Humidity-Drying.more » The differences in corrosivity of the test conditions are due to the various reactions needed to cause corrosion, including the presence of chloride ions to cause pit nucleation, the presence of humidity to cause galvanic corrosion, and the drying phase which trapped chloride ions beneath the corrosion by-products.« less

Effects of gaseous nitriding AISI4140 alloy steel on corrosion and hardness properties

NASA Astrophysics Data System (ADS)

Tamil Moli, L.; Wahab, N.; Gopinathan, M.; Karmegam, K.; Maniyarasi, M.

2016-10-01

Corrosion is one of the major problems in the industry especially on machinery since it weakens the structure of the machinery part and causes the mechanical failure. This will stop the production and increase the maintenance cost. In this study, the corrosion behaviour of gas nitriding on a screw press machine shaft made from AISI 4140 steel was investigated. Pitting corrosion was identified as a major cause of the shaft failure and this study was conducted to improve the corrosion resistance on the AISI 4140 alloy steel shaft by gas nitriding as a surface hardening treatment. Gas nitriding was performed with composition of 15% ammonia and 85% nitrogen at temperatures of 525 °C, 550 °C and 575 °C and with the soaking time of 30, 45 and 60 minutes, respectively. The samples were prepared as rectangular sized of 30mm x 12mm x 3mm for immersion testing. The results showed that corrosion rate of untreated samples was 77% higher compared to the nitrided samples. It was also found that hardness of the nitrided samples was higher than untreated sample. All in all, it can be concluded that gaseous nitriding can significantly improve the surface hardness and the corrosion resistance of the shaft made of AISI 4140 alloy steel, hence reduces the pitting that is the root cause of failure.

Corrosion of Continuous Fiber Reinforced Aluminum Metal Matrix Composites (CF-AMCs)

NASA Astrophysics Data System (ADS)

Tiwari, Shruti

The first objective of this research is to study the atmospheric corrosion behavior of continuous reinforced aluminum matrix composites (CF-AMCs). The materials used for this research were alumina (Al2O3) and nickel (Ni) coated carbon (C) fibers reinforced AMCs. The major focus is to identify the correlation between atmospheric parameters and the corrosion rates of CF-AMCs in the multitude of microclimates and environments in Hawai'i. The micro-structures of CF-AMCs were obtained to correlate the microstructures with their corrosion performances. Also electrochemical polarization experiments were conducted in the laboratory to explain the corrosion mechanism of CF-AMCs. In addition, CF-AMCs were exposed to seven different test sites for three exposure periods. The various climatic conditions like temperature (T), relative humidity (RH), rainfall (RF), time of wetness (TOW), chloride (Cl- ) and sulfate (SO42-) deposition rate, and pH were monitored for three exposure period. Likewise, mass losses of CF-AMCs at each test site for three exposure periods were determined. The microstructure of the CF-AMCS showed that Al/C/50f MMCs contained a Ni-rich phase in the matrix, indicating that the Ni coating on the C fiber dissolved in the matrix. The intermetallic phases obtained in Al-2wt% Cu/Al 2O3/50f-T6 MMC and Al-2wt%-T6 monolith were rich in Cu and Fe. The intermetallic phases obtained in Al 7075/Al2O3/50f-T6 MMC and Al 7075-T6 monolith also contained traces of Mg, Zn, Ni, and Si. Electrochemical polarization experiment indicated that the Al/Al 2O3/50f Al-2wt% Cu/Al2O3/50f-T6 and Al 7075/Al2O3/50f-T6 MMC showed similar corrosion trends as their respective monoliths pure Al, Al-2wt%-T6 and Al 7075-T6 in both aerated and deaerated condition. Al2O3 fiber, being an insulator, did not have a great effect on the polarization behavior of the composites. Al/C/50f MMCs corroded at a much faster rate as compared to pure Al monolith due to the galvanic effect between C and Al. According to the mass loss data of Al/C/50f MMCs, corrosion rate was high at marine environments (high Cl-) when compared to a tropical rainforest microclimate and low in a test site with a high SO2 and acid rain. Due to presence of conductive C fiber, the galvanic corrosion was a dominating corrosion mechanism. Due to high volume fraction of C, the corrosion phenomenon was cathodically controlled. The galvanic corrosion between C fiber and Al matrix showed a strong positive correlation with Cl - deposition rate. Lower corrosion rate at volcanic test site was attributed to dissolution of Ni rich phase, a potential cathodic site that promotes corrosion of Al/C/50f MMCs. Based on the mass loss data of Al2O3 based CF-AMCs and the monoliths showed maximum corrosion at volcanic test site when compared to any other test site. Due to the small volume fraction of intermetallic phases, the corrosion was anodically controlled. And hence the maximum anodic dissolution was found at volcanic test site (high SO2 and acid rain). The second objective of this thesis is to study the effect localized deformation on the corrosion of CF-AMCs. Corrosion initiation on Al (2 wt% Cu)/Al2O3/60f (60% fiber), Al 6061/Al2O 3/60f, and Al/Al2O3/60f CF-AMCs was studied in an aqueous environment The CF-AMCs and their monolithic alloys were deformed locally using a 1/16" diameter silicon nitride ball and 15-60 Kg load in a Rockwell hardness testing machine. Corrosion initiated at the deformed sites, and after longer exposures, spread over the entire region. Localized mechanical deformation resulted in micro-crevice formations at the fiber matrix interface. When deformed material is exposed to a corrosive solution, the crevices at the fiber matrix interface likely increased the hydrogen ion concentration lowering the pH at those regions, a process that leads to premature corrosion. The copper (Cu) rich CF-AMCs in aqueous solution resulted in dissolution of Cu rich phase and their subsequent deposition and redistribution as Cu over the deformed CF-AMCs surface. The corrosion rates of deformed CF-AMCs were higher than the non-deformed CF-AMCs.

Effects of porosity on corrosion resistance of Mg alloy foam produced by powder metallurgy technology

DOE Office of Scientific and Technical Information (OSTI.GOV)

Aghion, E., E-mail: egyon@bgu.ac.il; Perez, Y.

2014-10-15

Magnesium alloy foams have the potential to serve as structural material for regular light-weight applications as well as for biodegradable scaffold implants. However, their main disadvantage relates to the high reactivity of magnesium and consequently their natural tendency to corrode in regular service conditions and in physiological environments. The present study aims at evaluating the effect of porosity on the corrosion resistance of MRI 201S magnesium alloy foams in 0.9% NaCl solution and in phosphate buffer saline solution as a simulated physiological electrolyte. The magnesium foams were produced by powder metallurgy technology using space-holding particles to control the porosity content.more » Machined chips were used as raw material for the production of Mg alloy powder by milling process. The microstructure of the foams was examined using optical and scanning electron microscopy, X-ray diffraction, and X-ray photoelectron spectroscopy analysis. The corrosion behavior was evaluated by immersion test and potentiodynamic polarization analysis. The results obtained clearly demonstrate that the porosity has a significant effect on the corrosion resistance of the tested foams. Foams with 14–19% porosity have a corrosion rate of 4–10 mcd and 7–15 mcd in NaCl and phosphate buffer saline solution, respectively, compared to only 0.10 mcd for the same alloy in as cast conditions. This increased corrosion degradation of the Mg foams by more than one order of magnitude compared to the cast alloy may limit their potential application in regular and physiological environments. - Highlights: • Porosity has a detrimental effect on corrosion resistance of MRI 201S Mg foams. • 14–19% porosity increases the corrosion rate by more than one order of magnitude. • Accelerated corrosion limits the use of foams in regular/physiological environments.« less

Lubrication studies of some type III deep eutectic solvents (DESs)

NASA Astrophysics Data System (ADS)

Ahmed, Essa. I.; Abbott, Andrew. P.; Ryder, Karl S.

2017-09-01

It has previously been shown that eutectic mixtures of quaternary ammonium salts and hydrogen bond donors form liquids with properties similar to ionic liquids [1; 2]. These so-called deep eutectic solvents (DESs) have been shown to have physical properties which would make them useful as base lubricants. The base lubricant needs to show specific properties, including high viscosity index (VI), low friction coefficient (μ), low pour point and corrosivity. To determine the applicability of DESs as base lubricants, physical properties, corrosion and lubrication properties for four type III DESs have been studied and the results have been compared with mineral base oil. The data show that the lubrication properties of DESs are superior to mineral base oil for short distances. All DESs assessed here have higher VI (191, 147, 121 for Ethaline, Glyceline and Reline respectively compared with 100 for mineral base oil), lower pour points than mineral base oil and most of the liquids studied have shown very low corrosion rates (< 3 µm year-1 for mild steel).

Corrosion of Nickel-Titanium Orthodontic Archwires in Saliva and Oral Probiotic Supplements

PubMed Central

Turco, Gianluca; Contardo, Luca; Serdarević, Nikolina Leona; Otmačić, Helena; Ćurković; Špalj, Stjepan

2017-01-01

Objectives The aim of the study was to examine how probiotic supplements affect the corrosion stability of orthodontic archwires made of nickel-titanium alloy (NiTi). Materials and Methods NiTi archwires (0.508x0.508 and having the length of 2.5 cm) were tested. The archwires (composition Ni=50.4%, Ti=49.6%) were uncoated, nitrified and rhodium coated. Surface microgeometry was observed by using scanning electron microscope and surface roughness was measured by profilometer through these variables: roughness average, maximum height and maximum roughness depth. Corrosion was examined by electrochemical method of cyclic polarisation. Results Rhodium coated alloy in saliva has significantly higher general corrosion in saliva than nitrified alloy and uncoated alloy, with large effect size (p=0.027; η2=0.700). In the presence of probiotics, the result was even more pronounced (p<0.001; η2=0.936). Probiotic supplement increases general and localised corrosion of rhodium coated archwire and slightly decreases general corrosion and increases localised corrosion in uncoated archwire, while in the case of nitrified archwire the probability of corrosion is very low. The differences in surface roughness between NiTi wires before corrosion are not significant. Exposure to saliva decreases roughness average in rhodium coated wire (p=0.015; η2=0.501). Media do not significantly influence surface microgeometry in nitrified and uncoated wires. Conclusion Probiotic supplement affects corrosion depending on the type of coating of the NiTi archwire. It increases general corrosion of rhodium coated wire and causes localised corrosion of uncoated and rhodium coated archwire. Probiotic supplement does not have greater influence on surface roughness compared to that of saliva. PMID:29872237

Corrosion Characterization in Nickel Plated 110 ksi Low Alloy Steel and Incoloy 925: An Experimental Case Study

NASA Astrophysics Data System (ADS)

Thomas, Kiran; Vincent, S.; Barbadikar, Dipika; Kumar, Shresh; Anwar, Rebin; Fernandes, Nevil

2018-04-01

Incoloy 925 is an age hardenable Nickel-Iron-Chromium alloy with the addition of Molybdenum, Copper, Titanium and Aluminium used in many applications in oil and gas industry. Nickel alloys are preferred mostly in corrosive environments where there is high concentration of H2S, CO2, chlorides and free Sulphur as sufficient nickel content provides protection against chloride-ion stress-corrosion cracking. But unfortunately, Nickel alloys are very expensive. Plating an alloy steel part with nickel would cost much lesser than a part make of nickel alloy for large quantities. A brief study will be carried out to compare the performance of nickel plated alloy steel with that of an Incoloy 925 part by conducting corrosion tests. Tests will be carried out using different coating thicknesses of Nickel on low alloy steel in 0.1 M NaCl solution and results will be verified. From the test results we can confirm that Nickel plated low alloy steel is found to exhibit fairly good corrosion in comparison with Incoloy 925 and thus can be an excellent candidate to replace Incoloy materials.

Corrosion performance tests for reinforcing steel in concrete : test procedures.

DOT National Transportation Integrated Search

2009-09-01

The existing test method to assess the corrosion performance of reinforcing steel embedded in concrete, mainly : ASTM G109, is labor intensive, time consuming, slow to provide comparative results, and often expensive. : However, corrosion of reinforc...

Corrosion performance tests for reinforcing steel in concrete : technical report.

DOT National Transportation Integrated Search

2009-10-01

The existing test method used to assess the corrosion performance of reinforcing steel embedded in : concrete, mainly ASTM G 109, is labor intensive, time consuming, slow to provide comparative results, : and can be expensive. However, with corrosion...

Corrosion studies using potentiodynamic and EIS electrochemical techniques of welded lean duplex stainless steel UNS S82441

NASA Astrophysics Data System (ADS)

Brytan, Z.; Niagaj, J.; Reiman, Ł.

2016-12-01

The corrosion characterisation of lean duplex stainless steel (1.4662) UNS S82441 welded joints using the potentiodynamic test and electrochemical impedance spectroscopy in 1 M NaCl solution are discussed. The influence of autogenous TIG welding parameters (amount of heat input and composition of shielding gases like Ar and Ar-N2 and an Ar-He mixture), as well as A-TIG welding was studied. The influence of welding parameters on phase balance, microstructural changes and the protective properties of passive oxide films formed at the open circuit potential or during the anodic polarisation were studied. From the results of the potentiodynamic test and electrochemical impedance spectroscopy of TIG and A-TiG, welded joints show a lower corrosion resistance compared to non-welded parent metal, but introducing heat input properly during welding and applying shielding gases rich in nitrogen or helium can increase austenitic phase content, which is beneficial for corrosion resistance, and improves surface oxide layer resistance in 1 M NaCl solution.

Enhancement of anticorrosion property of 304 stainless steel using silane coatings

NASA Astrophysics Data System (ADS)

Akhtar, Sultan; Matin, Asif; Madhan Kumar, A.; Ibrahim, Ahmed; Laoui, Tahar

2018-05-01

In the present work, silane coatings based on glycidoxypropyltrimethoxysilane/methyltrimethoxysilane (GPTMS/MTMS) and silica nanoparticles were prepared by a sol-gel method. A simple dip-coating method was applied for film deposition and the effect of immersion time and number of immersion cycles on corrosion behavior of 304 stainless steel (SS) was investigated. Scanning electron microscopy with energy dispersive X-ray spectroscopy (SEM/EDS) was used to study the surface morphology and elemental composition of the modified surfaces. The corrosion behavior of the coated and uncoated SS substrates was studied by potentiodynamic polarization and electrochemical impedance spectroscopy in 0.6 M sodium chloride solution. Our results showed that the presence of coatings improved the anti-corrosion property of SS substrates. The coating with a dipping time of 10 min and 3 dipping cycles exhibited the best protection efficiency compared to other coatings and the uncoated substrate. SEM/EDS findings and contact angle measurements supported the conclusions drawn from the corrosion study.

Effect of zinc phosphate chemical conversion coating on corrosion behaviour of mild steel in alkaline medium: protection of rebars in reinforced concrete.

PubMed

Simescu, Florica; Idrissi, Hassane

2008-12-01

We outline the ability of zinc phosphate coatings, obtained by chemical conversion, to protect mild steel rebars against localized corrosion, generated by chloride ions in alkaline media. The corrosion resistance of coated steel, in comparison with uncoated rebars and coated and uncoated steel rebars embedded in mortar, were evaluated by open-circuit potential, potentiodynamic polarization, cronoamperometry and electrochemical impedance spectroscopy. The coated surfaces were characterized by x-ray diffraction and scanning electron microscopy. First, coated mild steel rebars were studied in an alkaline solution with and without chloride simulating a concrete pore solution. The results showed that the slow dissolution of the coating generates hydroxyapatite Ca 10 (PO 4 ) 6 (OH) 2 . After a long immersion, the coating became dense and provided an effective corrosion resistance compared with the mild steel rebar. Secondly, the coated and uncoated steel rebars embedded in mortar and immersed in chloride solution showed no corrosion or deterioration of the coated steel. Corrosion rate is considerably lowered by this phosphate coating.

Effect of zinc phosphate chemical conversion coating on corrosion behaviour of mild steel in alkaline medium: protection of rebars in reinforced concrete

NASA Astrophysics Data System (ADS)

Simescu, Florica; Idrissi, Hassane

2008-12-01

We outline the ability of zinc phosphate coatings, obtained by chemical conversion, to protect mild steel rebars against localized corrosion, generated by chloride ions in alkaline media. The corrosion resistance of coated steel, in comparison with uncoated rebars and coated and uncoated steel rebars embedded in mortar, were evaluated by open-circuit potential, potentiodynamic polarization, cronoamperometry and electrochemical impedance spectroscopy. The coated surfaces were characterized by x-ray diffraction and scanning electron microscopy. First, coated mild steel rebars were studied in an alkaline solution with and without chloride simulating a concrete pore solution. The results showed that the slow dissolution of the coating generates hydroxyapatite Ca10(PO4)6(OH)2. After a long immersion, the coating became dense and provided an effective corrosion resistance compared with the mild steel rebar. Secondly, the coated and uncoated steel rebars embedded in mortar and immersed in chloride solution showed no corrosion or deterioration of the coated steel. Corrosion rate is considerably lowered by this phosphate coating.

Graphene: corrosion-inhibiting coating.

PubMed

Prasai, Dhiraj; Tuberquia, Juan Carlos; Harl, Robert R; Jennings, G Kane; Rogers, Bridget R; Bolotin, Kirill I

2012-02-28

We report the use of atomically thin layers of graphene as a protective coating that inhibits corrosion of underlying metals. Here, we employ electrochemical methods to study the corrosion inhibition of copper and nickel by either growing graphene on these metals, or by mechanically transferring multilayer graphene onto them. Cyclic voltammetry measurements reveal that the graphene coating effectively suppresses metal oxidation and oxygen reduction. Electrochemical impedance spectroscopy measurements suggest that while graphene itself is not damaged, the metal under it is corroded at cracks in the graphene film. Finally, we use Tafel analysis to quantify the corrosion rates of samples with and without graphene coatings. These results indicate that copper films coated with graphene grown via chemical vapor deposition are corroded 7 times slower in an aerated Na(2)SO(4) solution as compared to the corrosion rate of bare copper. Tafel analysis reveals that nickel with a multilayer graphene film grown on it corrodes 20 times slower while nickel surfaces coated with four layers of mechanically transferred graphene corrode 4 times slower than bare nickel. These findings establish graphene as the thinnest known corrosion-protecting coating.

Effect of zinc phosphate chemical conversion coating on corrosion behaviour of mild steel in alkaline medium: protection of rebars in reinforced concrete

PubMed Central

Simescu, Florica; Idrissi, Hassane

2008-01-01

We outline the ability of zinc phosphate coatings, obtained by chemical conversion, to protect mild steel rebars against localized corrosion, generated by chloride ions in alkaline media. The corrosion resistance of coated steel, in comparison with uncoated rebars and coated and uncoated steel rebars embedded in mortar, were evaluated by open-circuit potential, potentiodynamic polarization, cronoamperometry and electrochemical impedance spectroscopy. The coated surfaces were characterized by x-ray diffraction and scanning electron microscopy. First, coated mild steel rebars were studied in an alkaline solution with and without chloride simulating a concrete pore solution. The results showed that the slow dissolution of the coating generates hydroxyapatite Ca10(PO4)6(OH)2. After a long immersion, the coating became dense and provided an effective corrosion resistance compared with the mild steel rebar. Secondly, the coated and uncoated steel rebars embedded in mortar and immersed in chloride solution showed no corrosion or deterioration of the coated steel. Corrosion rate is considerably lowered by this phosphate coating. PMID:27878037

Corrosion on the acetabular liner taper from retrieved modular metal-on-metal total hip replacements.

PubMed

Gascoyne, Trevor C; Dyrkacz, Richard M; Turgeon, Thomas R; Burnell, Colin D; Wyss, Urs P; Brandt, Jan-M

2014-10-01

Eight retrieved metal-on-metal total hip replacements displayed corrosion damage along the cobalt-chromium alloy liner taper junction with the Ti alloy acetabular shell. Scanning electron microscopy indicated the primary mechanism of corrosion to be grain boundary and associated crevice corrosion, which was likely accelerated through mechanical micromotion and galvanic corrosion resulting from dissimilar alloys. Coordinate measurements revealed up to 4.3mm(3) of the cobalt-chromium alloy taper surface was removed due to corrosion, which is comparable to previous reports of corrosion damage on head-neck tapers. The acetabular liner-shell taper appears to be an additional source of metal corrosion products in modular total hip replacements. Patients with these prostheses should be closely monitored for signs of adverse reaction towards corrosion by-products. Copyright © 2014 Elsevier Inc. All rights reserved.

A comparative study of atmospheric corrosion in the Caribbean area

DOE Office of Scientific and Technical Information (OSTI.GOV)

Maldonado, L.; Castro, P.; Echeverria, M.

1995-10-01

Atmospheric corrosion is a phenomenon of such a magnitude that has been cause of study in several countries for decades. Nevertheless, in Mexico, it became of recent interest due to new economic factors that have involved the Peninsula of Yucatan too. The Yucatan Peninsula is limited to the North and West by the Gulf of Mexico and to the East by the Caribbean Sea. This is a non industrialized region so that in the past very little importance was given to the atmospheric corrosion damage or to the quantification of the high corrosion rates, empirically observed. However, in recent timesmore » increased tourism, industrial growth and petroleum extraction have exhibited the need for a better understanding of the atmospheric corrosion processes, as well as a realistic correlation to parameters such as time-of-wetness, levels of pollution by airborne salinity, atmospheric S0{sub 2} and corrosivity categories for the metals. To evaluate these parameters, five tests sites were selected following ISO recommendations. Three sites are marines atmospheres, one urban and one rural. Corrosion rates for commercial laminated Cu and carbon steel, as well as deposition rates of pollutants, were determined after one year exposure in the test sites. Applying the standard practice ISO 9223 a categorization of the corrosivity and of the level of pollutants was carried out. The marine environments were classified as of atmospheric corrosivity C{sub 5}, while the urban and the rural could be classified as C{sub 3}, respectively. The pollution values showed that the exposure sites were essentially contaminated with chloride with classification S{sub 1} for the rural site and S{sub 3} for the marine atmosphere.« less

Corrosion of pure aluminium and aluminium alloy: a comparative study using a slow positron beam

NASA Astrophysics Data System (ADS)

Wu, Y. C.; Li, P. H.; Xue, X. D.; Wang, S. J.; Kallis, A.; Coleman, P. G.; Zhai, T.

2011-01-01

Corrosion-related defects in pure Al and AA 2037 Al alloy have been investigated by positron beam-based Doppler broadening energy spectroscopy. Defect profiles have been analyzed by measuring the S parameter as a function of incident positron energy up to 30 keV. When pure Al samples are immersed in 1M NaOH for various times, a significant increase in the S parameter near the surface is observed. This implies that the corrosion process involves the creation of defects and nanometer voids. In contrast, a significant decrease in the S parameter is observed after the corrosion of water-quenched Al alloy by the same method, which is interpreted as being a result of Cu enrichment near the metal-oxide interface layer.

Pitting corrosion resistance of a novel duplex alloy steel in alkali-activated slag extract in the presence of chloride ions

NASA Astrophysics Data System (ADS)

Shi, Jin-jie; Ming, Jing; Liu, Xin

2017-10-01

In this study, two types of reinforcing steels (conventional low-carbon steel and a novel duplex alloy steel with Cr and Mo) were exposed to chloride-contaminated extract solutions (ordinary Portland cement (OPC) extract and alkali-activated slag (AAS) extract) to investigate their pitting corrosion resistance. The results confirm that the pitting corrosion resistance of the alloy steel is much higher than that of the low-carbon steel in both extract solutions with various NaCl concentrations. Moreover, for each type of steel, the AAS extract contributes to a higher pitting corrosion resistance compared with the OPC extract in the presence of chloride ions, likely because of the formation of flocculent precipitates on the steel surface.

Corrosion behaviour of Al-Fe-Ti-V medium entropy alloy

NASA Astrophysics Data System (ADS)

Bodunrin, M. O.; Obadele, B. A.; Chown, L. H.; Olubambi, P. A.

2017-12-01

Alloys containing up to four multi-principal elements in equiatomic ratios are referred to as medium entropy alloys (MEA). These alloys have attracted the interest of many researchers due to the superior mechanical properties it offers over the traditional alloys. The design approach of MEA often results to simple solid solution with either body centered cubic; face centered cubic structures or both. As the consideration for introducing the alloys into several engineering application increases, there have been efforts to study the corrosion behaviour of these alloys. Previous reports have shown that some of these alloys are more susceptible to corrosion when compared with traditional alloys due to lack of protective passive film. In this research, we have developed AlFeTiV medium entropy alloys containing two elements (Ti and Al) that readily passivate when exposed to corrosive solutions. The alloys were produced in vacuum arc furnace purged with high purity argon. Open circuit potential and potentiodynamic polarisation tests were used to evaluate the corrosion behaviour of the as-cast AlFeTiV alloy in 3.5 wt% NaCl and 1 M H2SO4. The corrosion performance of the alloy was compared with Ti-6Al-4V alloy tested under similar conditions. The results show that unlike in Ti-6Al-4V alloy, the open circuit potential of the AlFeTiV alloy move towards the negative values in both 3.5 wt% NaCl and 1 M H2SO4 solutions indicating that self-activation occurred rapidly on immersion. Anodic polarisation of the alloys showed that AlFeTiV alloy exhibited a narrow range of passivity in both solutions. In addition, the alloys exhibited lower Ecorr and higher Icorr when compared with traditional Ti-6Al-4V alloy. The traditional Ti-6Al-4V alloy showed superior corrosion resistant to the AlFeTiV alloy in both 3.5 wt.% NaCl and 1 M H2SO4 solutions.

Electrochemical Corrosion and In Vitro Bioactivity of SiO2:ZrO2-Coated 316L Stainless Steel in Simulated Body Fluid

NASA Astrophysics Data System (ADS)

Srinivasan, A.; Rajendran, N.

2015-08-01

The effect of Si:Zr ratio on the in vitro bioactivity and electrochemical corrosion behavior of SiO2:ZrO2-mixed oxide-coated 316L stainless steel (SS) was evaluated in simulated body fluid (SBF) solution for 72, 120, and 168 h. Growth of Hydroxyapatite (HAp) was accelerated when Si content in the coating was increased. The Zr content in the coating improved the corrosion resistance of 316L SS rather than accelerating the HAp growth. When the Si:Zr ratio was 50:50, the coating exhibited significant improvement in corrosion resistance as well as HAp growth. The mechanism of HAp growth was proposed based on the change in surface zeta potential values of the coatings. Potentiodynamic polarization studies revealed about 10 and 5 times reduction in corrosion current density ( i corr) values for SiO2:ZrO2 (50:50)-coated 316L SS after 168 h of immersion compared to SiO2, ZrO2, and Si:Zr (70:30) coatings in SBF solutions thus confirming the superior corrosion resistance. The equivalent circuit parameters derived from electrochemical impedance spectroscopy studies further confirmed significant improvement in charge transfer resistance value even after 168 h of exposure.

Comparative Corrosion Behavior of Two Palladium Containing Titanium Alloys

DOE Office of Scientific and Technical Information (OSTI.GOV)

Lian, T; Yashiki, T; Nakayama, T

2006-02-05

The ASTM standard B 265 provides the requirements for the chemical composition of titanium (Ti) alloys. It is planned to use corrosion resistant and high strength titanium alloys to fabricate the drip shield at the proposed Yucca Mountain Repository. Titanium grade (Gr) 7 (R52400) and other Ti alloys are currently being characterized for this application. Ti Gr 7 contains 0.15% Palladium (Pd) to increase its corrosion performance. In this article we report results on the comparative short term corrosion behavior of Ti Gr 7 and a Ruthenium (Ru) containing alloy (Ti Gr 33). Ti Gr 33 also contains a smallmore » amount of Pd. Limited electrochemical testing such as polarization resistance and cyclic potentiodynamic curves showed that both alloys have a similar corrosion behavior in the tested environments.« less

COMPARATIVE CORROSION BEHAVIOR OF TWO PALLADIUM CONTAINING TITANIUM ALLOYS

DOE Office of Scientific and Technical Information (OSTI.GOV)

T. Lian, T. Yashiki, T. Nakayama, T. Nakanishi, R. B. Rebak

2006-07-23

The ASTM standard B 265 provides the requirements for the chemical composition of titanium (Ti) alloys. It is planned to use corrosion resistant and high strength titanium alloys to fabricate the drip shield at the proposed Yucca Mountain Repository. Titanium grade (Gr) 7 (R52400) and other Ti alloys are currently being characterized for this application. Ti Gr 7 contains 0.15% Palladium (Pd) to increase its corrosion performance. In this article we report results on the comparative short term corrosion behavior of Ti Gr 7 and a Ruthenium (Ru) containing alloy (Ti Gr 33). Ti Gr 33 also contains a smallmore » amount of Pd. Limited electrochemical testing such as polarization resistance and cyclic potentiodynamic curves showed that both alloys have a similar corrosion behavior in the tested environments.« less

Stainless and Galvanized Steel, Hydrophobic Admixture and Flexible Polymer-Cement Coating Compared in Increasing Durability of Reinforced Concrete Structures

NASA Astrophysics Data System (ADS)

Tittarelli, Francesca; Giosuè, Chiara; Mobili, Alessandra

2017-08-01

The use of stainless or galvanized steel reinforcements, a hydrophobic admixture or a flexible polymer-cement coating were compared as methods to improve the corrosion resistance of sound or cracked reinforced concrete specimens exposed to chloride rich solutions. The results show that in full immersion condition, negligible corrosion rates were detected in all cracked specimens, except those treated with the flexible polymer-cement mortar as preventive method against corrosion and the hydrophobic concrete specimens. High corrosion rates were measured in all cracked specimens exposed to wet-dry cycles, except for those reinforced with stainless steel, those treated with the flexible polymer-cement coating as restorative method against reinforcement corrosion and for hydrophobic concrete specimens reinforced with galvanized steel reinforcements.

Corrosion Behavior of Plasma-Passivated Cu

DOE Office of Scientific and Technical Information (OSTI.GOV)

Barbour, J.C.; Braithwaite, J.W.; Son, K.A.

1999-07-09

A new approach is being pursued to study corrosion in Cu alloy systems by using combinatorial analysis combined with microscopic experimentation (the Combinatorial Microlab) to determine mechanisms for copper corrosion in air. Corrosion studies are inherently difficult because of complex interactions between materials and environment, forming a multidimensional phase space of corrosion variables. The Combinatorial Microlab was specifically developed to address the mechanism of Cu sulfidation, which is an important reliability issue for electronic components. This approach differs from convention by focusing on microscopic length scales, the relevant scale for corrosion. During accelerated aging, copper is exposed to a varietymore » of corrosive environments containing sulfidizing species that cause corrosion. A matrix experiment was done to determine independent and synergistic effects of initial Cu oxide thickness and point defect density. The CuO{sub x} was controlled by oxidizing Cu in an electron cyclotron resonance (ECR) O{sub 2} plasma, and the point defect density was modified by Cu ion irradiation. The matrix was exposed to 600 ppb H{sub 2}S in 65% relative humidity air atmosphere. This combination revealed the importance of oxide quality in passivating Cu and prevention of the sulfidizing reaction. A native oxide and a defect-laden ECR oxide both react at 20 C to form a thick Cu{sub 2}S layer after exposure to H{sub 2}S, while different thicknesses of as-grown ECR oxide stop the formation of Cu{sub 2}S. The species present in the ECR oxide will be compared to that of an air oxide, and the sulfide layer growth rate will be presented.« less

Fretting crevice corrosion of stainless steel stem-CoCr femoral head connections: comparisons of materials, initial moisture, and offset length.

PubMed

Gilbert, Jeremy L; Mehta, Manav; Pinder, Bryan

2009-01-01

Modular tapers continue to be used in a wide variety of orthopedic implants. In this study, stainless steel (ASTM F-1568) femoral hip stems combined with Co-Cr-Mo alloy heads (SS/CoCr) were tested in an in vitro fretting corrosion test set-up to assess the propensity for mechanically assisted corrosion. Three different aspects of the modular design were evaluated in this study: (1) material combination compared to CoCr/CoCr, (2) wet versus dry assembly for SS/CoCr couples, and (3) 0- and 6-mm head offset for SS/CoCr couples. Fretting corrosion tests over a range of cyclic loads up to 3300 N were performed, and continuous cyclic loading at 3300 N for 1 M cycles were performed on each group (n = 5). Fretting micromotion was measured as a function of cyclic load on select couples to detect the nature and extent of motion present. The results showed that SS/CoCr couples were more susceptible to fretting corrosion than CoCr/CoCr couples, that dry assembly does not prevent fretting corrosion from taking place but raises the onset load, and that 6-mm offset heads had higher visual evidence of fretting damage but showed mixed statistical results in terms of onset loads and OCP shifts and currents compared to the 0-mm offset samples. Current and voltage excursions over 1 million cycles tended to diminish towards their unloaded control levels but did not fully recover until cyclic loading ceased. Micromotion measurements indicated fretting motions in the range of 10-25 microm where 0-mm heads tended to piston on the trunion, while 6 mm heads tended to rock. (c) 2008 Wiley Periodicals, Inc.

Effect of coating mild steel with CNTs on its mechanical properties and corrosion behaviour in acidic medium

NASA Astrophysics Data System (ADS)

Abdulmalik Abdulrahaman, Mahmud; Kamaldeeen Abubakre, Oladiran; Ambali Abdulkareem, Saka; Oladejo Tijani, Jimoh; Aliyu, Ahmed; Afolabi, Ayo Samuel

2017-03-01

The study investigated the mechanical properties and corrosion behaviour of mild steel coated with carbon nanotubes at different coating conditions. Multi-walled carbon nanotubes (MWCNTs) were synthesized via the conventional chemical vapour deposition reaction using bimetallic Fe-Ni catalyst supported on kaolin, with acetylene gas as a carbon source. The HRSEM/HRTEM analysis of the purified carbon materials revealed significant reduction in the diameters of the purified MWCNT bundles from 50 nm to 2 nm and was attributed to the ultrasonication assisted dispersion with surfactant (gum arabic) employed in purification process. The network of the dispersed MWCNTs was coated onto the surfaces of mild steel samples, and as the coating temperature and holding time increased, the coating thickness reduced. The mechanical properties (tensile strength, yield strength, hardness value) of the coated steel samples increased with increase in coating temperature and holding time. Comparing the different coating conditions, coated mild steels at the temperature of 950 °C for 90 min holding time exhibited high hardness, yield strength and tensile strength values compared to others. The corrosion current and corrosion rate of the coated mild steel samples decreased with increase in holding time and coating temperature. The lowest corrosion rate was observed on sample coated at 950 °C for 90 min.

Synthesizing the Nanocrytalline Cobalt-Iron Coating Through The Electrodeposition Process With Different Time Deposition

NASA Astrophysics Data System (ADS)

Rozlin Nik Masdek, Nik; Sorfian Hafiz Mansor, Mohd; Salleh, Zuraidah; Hyie, Koay Mei

2018-03-01

In the engineering world, electrodeposition or electroplating has become the most popular method of surface coating in improving corrosion behavior and mechanical properties of material. Therefore in this study, CoFe nanoparticle protective coating has been synthesized on the mild steel washer using electrodeposition method. The electrodeposition was conducted in the acidic environment with the pH value range from 1 to 2 with the controlled temperature of 50°C. The influence of deposition time (30, 60, 90 minutes) towards characteristic and properties such as particle size, surface morphology, corrosion behavior, and microhardness were studied in this investigation. Several results can be obtained by doing this experiment and testing. First, the surface morphology of Cobalt Iron (CoFe) on the electrodeposited mild steel washer are obtained. In addition, the microhardness of the mild steel washer due to the different deposition time are determined. Next, the observation on the difference in the grain size of CoFe that has been electrodeposited on the mild steel plate is made. Last but not least, the corrosion behavior was investigated. CoFe nanoparticles deposited for 30 minutes produced the smallest particle size and the highest microhardness of 86.17 and 236.84 HV respectively. The CoFe nanoparticles also exhibit the slowest corrosion rate at 30 minutes as compared to others. The crystalline size also increases when the time deposition is increased. The sample with 30 minute depositon time indicate the smallest crystalline size which is 15nm. The decrement of deposition time plays an important role in synthesizing CoFe nanoparticles with good corrosion resistance and microhardness. CoFe nanoparticles obtained at 30 minutes shows high corrosion resistance compared to others. In a nutshell, it was observed that the decrement of deposition time improved mechanical and corrosion properties of CoFe nanoparticles.

Fatigue 󈨛. Volume 3,

DTIC Science & Technology

1987-06-01

Corrosion and Cathodic Protection 1169 on Crack Growth in Offshore Platform Steels in Sea Water - EINAR BARDAL The Influence of Crack Conditions on...PROTECTION ON CRACK GROWTH IN OFFSHORE PLATFORM STEELS IN SEA WATER: EINAR BARDAL* Corrosion fatigue of steel for offshore platforms has been studied at...surfaces (6). When results from experiments with natural sea water are compared with corresponding results obtained in synthetic sea water, no significant

Morphometric Analysis of Aqueous Humor Outflow Structures with Spectral-Domain Optical Coherence Tomography

PubMed Central

Francis, Andrew W.; Kagemann, Larry; Wollstein, Gadi; Ishikawa, Hiroshi; Folz, Steven; Overby, Darryl R.; Sigal, Ian A.; Wang, Bo; Schuman, Joel S.

2012-01-01

Purpose. To describe morphometric details of the human aqueous humor (AH) outflow microvasculature visualized with 360-degree virtual castings during active AH outflow in cadaver eyes and to compare these structures with corrosion casting studies. Methods. The conventional AH outflow pathways of donor eyes (n = 7) and eyes in vivo (n = 3) were imaged with spectral-domain optical coherence tomography (SD-OCT) and wide-bandwidth superluminescent diode array during active AH outflow. Digital image contrast was adjusted to isolate AH microvasculature, and images were viewed in a 3D viewer. Additional eyes (n = 3) were perfused with mock AH containing fluorescent tracer microspheres to compare microvasculature patterns. Results. Observations revealed components of the conventional outflow pathway from Schlemm's canal (SC) to the superficial intrascleral venous plexus (ISVP). The superficial ISVP in both our study and corrosion casts were composed of interconnected venules (10–50 μm) forming a hexagonal meshwork. Larger radial arcades (50–100 μm) drained the region nearest SC and converged with larger tortuous vessels (>100 μm). A 360-degree virtual casting closely approximated corrosion casting studies. Tracer studies corroborated our findings. Tracer decorated several larger vessels (50–100 μm) extending posteriorly from the limbus in both raw and contrast-enhanced fluorescence images. Smaller tracer-labeled vessels (30–40 μm) were seen branching between larger vessels and exhibited a similar hexagonal network pattern. Conclusions. SD-OCT is capable of detailed morphometric analysis of the conventional outflow pathway in vivo or ex vivo with details comparable to corrosion casting techniques. PMID:22499987

Modeling corrosion inhibition efficacy of small organic molecules as non-toxic chromate alternatives using comparative molecular surface analysis (CoMSA).

PubMed

Fernandez, Michael; Breedon, Michael; Cole, Ivan S; Barnard, Amanda S

2016-10-01

Traditionally many structural alloys are protected by primer coatings loaded with corrosion inhibiting additives. Strontium Chromate (or other chromates) have been shown to be extremely effectively inhibitors, and find extensive use in protective primer formulations. Unfortunately, hexavalent chromium which imbues these coatings with their corrosion inhibiting properties is also highly toxic, and their use is being increasingly restricted by legislation. In this work we explore a novel tridimensional Quantitative-Structure Property Relationship (3D-QSPR) approach, comparative molecular surface analysis (CoMSA), which was developed to recognize "high-performing" corrosion inhibitor candidates from the distributions of electronegativity, polarizability and van der Waals volume on the molecular surfaces of 28 small organic molecules. Multivariate statistical analysis identified five prototypes molecules, which are capable of explaining 71% of the variance within the inhibitor data set; whilst a further five molecules were also identified as archetypes, describing 75% of data variance. All active corrosion inhibitors, at a 80% threshold, were successfully recognized by the CoMSA model with adequate specificity and precision higher than 70% and 60%, respectively. The model was also capable of identifying structural patterns, that revealed reasonable starting points for where structural changes may augment corrosion inhibition efficacy. The presented methodology can be applied to other functional molecules and extended to cover structure-activity studies in a diverse range of areas such as drug design and novel material discovery. Copyright © 2016 Elsevier Ltd. All rights reserved.

Experimental Study On Flexural Behaviour Of Beams Reinforced With GFRP Rebars

NASA Astrophysics Data System (ADS)

Naveen Kumar, G.; Sundaravadivelu, Karthik

2017-07-01

In saline, moisture and cold conditions corrosion of steel is inevitable and the lot of economy is used for rehabilitation works. Corrosion of steel is nothing but oxidation of iron in moisture conditions and this corrosion leads to the spalling of concrete which intern reduces the strength of the structure. To reduce this corrosion effects, new materials with resistance against corrosion have to be introduced. Many experiments are going on using Glass Fiber Reinforced Polymer (GFRP) as alternate material for steel due to its non-corrosive nature, weight of GFRP is nearly one third of steel and ultimate tensile strength is higher than steel. In this paper, six beams are casted in which three beams are casted with steel as main and shear reinforcement and another three beams are casted with GFRP as main reinforcement with steel as shear reinforcing material. All beams casted are of same dimensions with variation in reinforcement percentage. The size of the beams casted is of length 1200 mm, breadth 100 mm and depth 200 mm. The clear cover of 25 mm is provided on top and bottom of the beam. Beams are tested under two-point loading with constant aspect ratio (a/d) and comparing the flexural strength, load deflection curves and types of failures of beams reinforced with GFRP as main reinforcement and beams reinforced with conventional steel. The final experimental results are compared with numerical results. M30 grade concrete with Conplast as a superplasticizer is used for casting beams.

Corrosion resistance of new beta type titanium alloy, Ti-29Nb-13Ta-4.6Zr in artificial saliva solution

NASA Astrophysics Data System (ADS)

Gunawarman; Giatmana, D. D.; Ilhamdi; Affi, J.; Fonna, S.; Niinomi, M.; Nakai, M.

2018-05-01

The corrosion resistance of Ti-29Nb-13Ta-4.6Zr (TNTZ) and Ti-6Al-4V alloys in oral cavity environment were studied by investigating its corrosion rate in artificial saliva solution. Corrosion measurement was conducted in 600 ml solution of Fusayama-Meyer artificial saliva containing 0.4g NaCl, 0.4g KCl, 0.795g CaCl2.2H2O, 0.69g NaH2PO4, and 1 g urea using a potentiostat controlled by a personal computer. The solution was maintained at pH 5.2 and controlled the temperature of 37°C to imitate oral cavity condition. After corrosion test, specimen surfaces were examined by SEM and EDX. The results show that the average corrosion rate of TNTZ and Ti-6Al-4V is 4,5×10-9 mmy-1 and 6,4×10-8 mmy-1, respectively, indicating that the corrosion resistance of TNTZ is slightly better than Ti-6Al-4V. This is suggested mainly due to the formation of multiple layers of Ti, Nb and Zr oxides in the surface of TNTZ. However, the formation of micro-pitting corrosion is more severe in TNTZ as compared to that of Ti-6Al-4V. The intense pitting corrosion in TNTZ is found strongly corresponded to its high impurities content and wide elemental segregation. It is recommended, therefore, a longer homogenizing process is required in TNTZ for reducing pitting corrosion attack. However, the details of corrosion mechanism are needed to be explored further.

Comparison of the corrosion of fasteners embedded in wood measured in outdoor exposure with the predictions from a combined hygrothermal-corrosion model

Treesearch

Samuel L. Zelinka; Samuel V. Glass; Charles R. Boardman; Dominique Derome

2016-01-01

This paper examines the accuracy of a recently developed hygrothermal-corrosion model which predictsthe corrosion of fasteners embedded in wood by comparing the results of the model to a one year fieldtest. Steel and galvanized steel fasteners were embedded into untreated and preservative treated woodand exposed outdoors while weather data were collected. Qualitatively...

Environmental and alloying effects on corrosion of metals and alloys

NASA Astrophysics Data System (ADS)

Liang, Dong

2009-12-01

In the first part of this project, corrosion studies were carried out on 304L stainless steel samples welded with Cr-free consumables, which were developed to minimize the concentration of chromate species in the weld fume. The corrosion properties of Ni-Cu and Ni-Cu-Pd Gas Tungsten Arc (GTA) welds and Shielded Metal Arc (SMA) welds are comparable to those of welds fabricated with SS308L consumable, which is the standard consumable for welding 304L. Although the breakdown potentials of the new welds from both welding processes are lower than that of the SS308L weld, the repassivation potential of these new welds is much higher. Generally, the repassivation potential is a more conservative measure of susceptibility to localized corrosion. Our studies showed that the Ni-Cu and Ni-Cu-Pd welds are more resistant to crevice corrosion than SS308L welds, which is related to the high repassivation potential. Also, addition of Pd improved the corrosion resistance of the new welds, which is consistent with previous studies from button samples and bead-on-plate samples. Other corrosion studies such as creviced and uncreviced long time immersion, atmospheric exposure, and slow strain rate testing suggest that Ni-Cu-Pd welds can be a qualified substitute for SS308 weld. In the second part of this project, efforts are put on the connection between lab and field exposure tests because sometimes the correspondence between lab atmospheric corrosion tests (ASTM B117) and field exposures is poor as a result of differences in the critical conditions controlling chemical and electrochemical reactions on surfaces. Recent studies in atmospheric chemistry revealed the formation of extremely reactive species from interactions between UV light, chloride aerosols above oceans and oxidizing agents such as ozone or peroxide. Atmospheric corrosion of metals can be affected by these species which might be transported long distances in the atmosphere to locations far from oceans. However, these species could be missed in standard laboratory exposures such as ASTM B117. Initial efforts focused on the effects UV radiation, O3, relative humidity on the atmospheric corrosion of bare silver. Later work addressed the corrosion of silver samples deposited with NaCl particles. An exposure chamber that can simulate various environmental effects was built. The effects of UV radiation, O3, and relative humidity were varied separately while keeping the other factors the same level. The corrosion products were analyzed by the galvanostatic reduction method and characterization techniques such as SEM and EDS. It was found that both UV and O3 are necessary for fast corrosion on bare silver and this fast corrosion reaction results from atomic oxygen generated photodegradation of O3. In the presence of UV and O3, relative humidity has little effect on the atmospheric corrosion of bare silver in contrast to conventional atmospheric corrosion. The degree of corrosion is found to increase with O3 concentration. Moreover, a kinetic study of atmospheric corrosion of bare silver found that an incubation time for the atmospheric corrosion attack is needed. This incubation time is related to the chemisorption process of atomic oxygen. Though UV radiation can form reactive atomic oxygen which is more reactive than O3 alone as shown in the last chapter, the enhancement of corrosion by UV is limited for Ag with NaCl particles at low ozone concentration and high RH. The corrosion rate of silver with NaCl particles is found to increase with relative humidity, which is different than the case of bare silver. This indicates that different mechanisms control the atmospheric corrosion of silver. The incubation time for corrosion of silver with NaCl particles is shorter than for bare silver. This result from chemisorption of Cl 2 is favored over that of atomic oxygen. Interestingly, the total corrosion product of silver with NaCl particles is less than that of bare silver. This could be due to limited amount of NaCl and also higher oxidizing power of atomic oxygen. Finally, bare silver samples were exposed in salt spray chamber according to ASTM B117 up to 4 months. Very little corrosion products were detected after exposure, which is attributed to the lack of reactive species such as O and O3 in the environment. (Abstract shortened by UMI.)

Reciprocal interaction between dental alloy biocorrosion and Streptococcus mutans virulent gene expression.

PubMed

Zhang, Songmei; Qiu, Jing; Ren, Yanfang; Yu, Weiqiang; Zhang, Fuqiang; Liu, Xiuxin

2016-04-01

Corrosion of dental alloys is a major concern in dental restorations. Streptococcus mutans reduces the pH in oral cavity and induces demineralization of the enamel as well as corrosion of restorative dental materials. The rough surfaces of dental alloys induced by corrosion enhance the subsequent accumulation of plaque. In this study, the corrosion process of nickel-chromium (Ni-Cr) and cobalt-chromium (Co-Cr) alloys in a nutrient-rich medium containing S. mutans was studied using inductively coupled plasma atomic emission spectrometry (ICP-AES), X-ray photoelectron spectroscopy (XPS) and electrochemical corrosion test. Our results showed that the release of Ni and Co ions increased, particularly after incubation for 3 days. The electrochemical corrosion results showed a significant decrease in the corrosion resistance (Rp) value after the alloys were immersed in the media containing S. mutans for 3 days. Correspondingly, XPS revealed a reduction in the relative dominance of Ni, Co, and Cr in the surface oxides after the alloys were immersed in the S. mutans culture. After removal of the biofilm, the pre-corroded alloys were re-incubated in S. mutans medium, and the expressions of genes associated with the adhesion and acidogenesis of S. mutans, including gtfBCD, gbpB, fif and ldh, were evaluated by detecting the mRNA levels using real-time reverse transcription polymerase chain reaction (RT-PCR). We found that the gtfBCD, gbpB, ftf and Idh expression of S. mutans were noticeably increased after incubation with pre-corroded alloys for 24 h. This study demonstrated that S. mutans enhanced the corrosion behavior of the dental alloys, on the other hand, the presence of corroded alloy surfaces up-regulated the virulent gene expression in S. mutans. Compared with smooth surfaces, the rough corroded surfaces of dental alloys accelerated the bacteria-adhesion and corrosion process by changing the virulence gene expression of S. mutans.

Electrochemical noise measurements of sustained microbially influenced pitting corrosion in a laboratory flow loop system

DOE Office of Scientific and Technical Information (OSTI.GOV)

Lin, Y.; Frank, J.R.; St. Martin, E.J.

Because of the chaotic nature of the corrosion process and the complexity of the electrochemical noise signals that are generated, there is no generally accepted method of measuring and interpreting these signals that allows the consistent detection and identification of sustained localized pitting (SLP) as compared to general corrosion. The authors have reexamined electrochemical noise analysis (ENA) of localized corrosion using different hardware, signal collection, and signal processing designs than those used in conventional ENA techniques. The new data acquisition system was designed to identify and monitor the progress of SLP by analyzing the power spectral density (PSD) of themore » trend of the corrosion current noise level (CNL) and potential noise level (PNL). Each CNL and PNL data point was calculated from the root-mean-square value of the ac components of current and potential fluctuation signals, which were measured simultaneously during a short time period. The PSD analysis results consistently demonstrated that the trends of PNL and CNL contain information that can be used to differentiate between SLP and general corrosion mechanisms. The degree of linear slope in the low-frequency portion of the PSD analysis was correlated with the SLP process. Laboratory metal coupons as well as commercial corrosion probes were tested to ensure the reproducibility and consistency of the results. The on-line monitoring capability of this new ENA method was evaluated in a bench-scale flow-loop system, which simulated microbially influenced corrosion (MIC) activity. The conditions in the test flow-loop system were controlled by the addition of microbes and different substrates to favor accelerated corrosion. The ENA results demonstrated that this in-situ corrosion monitoring system could effectively identify SLP corrosion associated with MIC, compared to a more uniform general corrosion mechanism. A reduction in SLP activity could be clearly detected by the ENA monitoring system when a corrosion inhibitor was added into one of the test loops during the corrosion testing.« less

Electrochemical noise measurements of sustained microbially influenced pitting corrosion in a laboratory flow loop system.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Lin, Y. J.

Because of the chaotic nature of the corrosion process and the complexity of the electrochemical noise signals that are generated, there is no generally accepted method of measuring and interpreting these signals that allows the consistent detection and identification of sustained localized pitting (SLP) as compared to general corrosion. We have reexamined electrochemical noise analysis (ENA) of localized corrosion using different hardware, signal collection, and signal processing designs than those used in conventional ENA techniques. The new data acquisition system was designed to identify and monitor the progress of SLP by analyzing the power spectral density (PSD) of the trendmore » of the corrosion current noise level (CNL) and potential noise level (PNL). Each CNL and PNL data point was calculated from the root-mean- square value of the ac components of current and potential fluctuation signals, which were measured simultaneously during a short time period. The PSD analysis results consistently demonstrated that the trends of PNL and CNL contain information that can be used to differentiate between SLP and general corrosion mechanisms. The degree of linear slope in the low-frequency portion of the PSD analysis was correlated with the SLP process. Laboratory metal coupons as well as commercial corrosion probes were tested to ensure the reproducibility and consistency of the results. The on-line monitoring capability of this new ENA method was evaluated in a bench-scale flow-loop system, which simulated microbially influenced corrosion (MIC) activity. The conditions in the test flow-loop system were controlled by the addition of microbes and different substrates to favor accelerated corrosion. The ENA results demonstrated that this in-situ corrosion monitoring system could effectively identify SLP corrosion associated with MIC, compared to a more uniform general corrosion mechanism. A reduction in SLP activity could be clearly detected by the ENA monitoring system when a corrosion inhibitor was added into one of the test loops during the corrosion testing.« less

Ultrafast lasers for precise and corrosion free marking on chirurgical steels

NASA Astrophysics Data System (ADS)

Neugebauer, Christoph; Aalderink, Dennis; Maurer, Erich; Faisst, Birgit; Budnicki, Aleksander

2017-02-01

The unique properties of ultrashort laser pulses and the decrease of invest pave the way to numerous novel applications. Even in the very price sensitive field of laser marking, ultrashort laser can compete due to a new cost structure and remarkable properties of the marking results. In this study we concentrated on industrial marking of medical equipment by using IR ultrashort lasers and compared the results with common marking laser systems. We demonstrate the benefits of ultrashort lasers marking on chirurgical devices, observing the influence of pulse energy, pulse duration, scanning velocity in respect to the visibility, corrosion resistance and long term durability under clinical conditions. Nowadays many parts and products are marked for the purpose of identification and traceability. One kind of laser marking is the well known annealing of stainless steel by nanosecond marking lasers. When annealing occurs a colored oxide layer grows due to the local heating of the material surface. Compared to the raw material, the annealed marking shows increased corrosion sensitivity. Regarding the traceability, the poor durability of the ns marking resulting in contrast reduction and the corrosion susceptibility are a huge problem. Therefore three different laser sources with ns-psfs pulse duration were observed. The focus rests on the realization of parameter studies (various lasers) and their effect on the corrosion and passivation behavior. Furthermore analysis of the oxide layers by use of EDX and XRD were performed to obtain further information on the composition and structure of the markings.

Rebar corrosion monitoring in concrete structure under salt water enviroment using fiber Bragg grating

NASA Astrophysics Data System (ADS)

Pan, Yuheng; Liu, Tiegen; Jiang, Junfeng; Liu, Kun; Wang, Shuang; He, Pan; Yan, Jinlin

2015-08-01

Monitoring corrosion of steel reinforcing bars is critical for the durability and safety of reinforced concrete structures. Corrosion sensors based on fiber optic have proved to exhibit meaningful benefits compared with the conventional electric ones. In recent years, Fiber Bragg Grating (FBG) has been used as a new kind of sensing element in an attempt to directly monitor the corrosion in concrete structure due to its remarkable advantages. In this paper, we present a novel kind of FBG based rebar corrosion monitoring sensor. The rebar corrosion is detected by volume expansion of the corroded rebar by transferring it to the axial strain of FBG when concrete structure is soaked in salt water. An accelerated salt water corrosion test was performed. The experiment results showed the corrosion can be monitored effectively and the corrosion rate is obtained by volume loss rate of rebar.

Pitting Corrosion Behaviour of New Corrosion-Resistant Reinforcement Bars in Chloride-Containing Concrete Pore Solution

PubMed Central

Liu, Yao; Chu, Hong-yan; Wang, Danqian; Ma, Han; Sun, Wei

2017-01-01

In this study, the pitting behaviour of a new corrosion-resistant alloy steel (CR) is compared to that of low-carbon steel (LC) in a simulated concrete pore solution with a chloride concentration of 5 mol/L. The electrochemical behaviour of the bars was characterised using linear polarisation resistance (LPR) and electrochemical impedance spectroscopy (EIS). The pitting profiles were detected by reflective digital holographic microscopy (DHM), scanning electron microscopy (SEM), and the chemical components produced in the pitting process were analysed by X-ray energy dispersive spectroscopy (EDS). The results show that the CR bars have a higher resistance to pitting corrosion than the LC bars. This is primarily because of the periodic occurrence of metastable pitting during pitting development. Compared to the pitting process in the LC bars, the pitting depth grows slowly in the CR bars, which greatly reduces the risk of pitting. The possible reason for this result is that the capability of the CR bars to heal the passivation film helps to restore the metastable pits to the passivation state. PMID:28777327

Bio-corrosion and cytotoxicity studies on novel Zr 55Co 30Ti 15 and Cu 60Zr 20Ti 20 metallic glasses

DOE PAGES

Vincent, S.; Daiwile, A.; Devi, S. S.; ...

2014-09-26

Metallic glasses are a potential and compatible implant candidate for biomedical applications. In the present investigation, a comparative study between novel Zr 55Co 30Ti 15 and Cu 60Zr 20Ti 20 metallic glasses is carried out to evaluate in vitro biocompatibility using simulated body fluids. The bio-corrosion behavior of Zr- and Cu-based metallic glasses in different types of artificial body fluids such as artificial saliva solution, phosphate-buffered saline solution, artificial blood plasma solution, and Hank’s balanced saline solution is evaluated using potentiodynamic polarization studies at a constant body temperature of 310.15 K (37 °C). Surface morphology of samples after bio-corrosion experimentsmore » was observed by scanning electron microscopy. In vitro cytotoxicity test on glassy alloys were performed using human osteosarcoma cell line as per 10993-5 guidelines from International Organization for Standardization. As a result, the comparative study between Zr- and Cu-based glassy alloys provides vital information about the effect of elemental composition on biocompatibility of metallic glasses.« less

The corrosion mechanism of the sintered (Ce, Nd)-Fe-B magnets prepared by double main phase and single main phase approaches

NASA Astrophysics Data System (ADS)

Shi, Xiaoning; Zhu, Minggang; Zhou, Dong; Song, Liwei; Guo, Zhaohui; Li, Jia; Li, Wei

2018-05-01

The sintered (Ce, Nd)-Fe-B magnets were produced widely by Double Main Phase (DMP) method in China as the magnetic properties of the DMP magnets are superior to those of single main phase (SMP) magnets with the same nominal composition. In this work, the microstructure and corrosion mechanism of the sintered (Ce0.2Nd0.8)30FebalB (wt.%) magnets prepared by DMP and SMP method were studied in detail. Compared to SMP magnets, the DMP magnets have more positive corrosion potential, lower corrosion current density, larger electron transfer resistance, and lower mass loss of the free corrosion experiment in 0.5mol/l Na2SO4 aqueous solution. All of the results show that the DMP magnets have better corrosion resistance than SMP magnets. The back scattered electron images show that the crystalline grains of the DMP magnets are sphericity with a smooth surface while the SMP ones have plenty of edges and corners. Besides, the distribution of Ce/Nd is much more uneven in both magnetic phase and rare earth (Re)-rich phase of the DMP magnets than those of SMP magnets. After corrosion, DMP magnets show eroded magnetic phase and intact Re-rich phase, which indicate that galvanic corrosion of the Re-rich phase acting as the cathode appears.

Effects of silicon and titanium on the corrosion of low-alloy steels in a simulated coal gasification environment at 600 C

DOE Office of Scientific and Technical Information (OSTI.GOV)

Soler, J.L.J.; Baxter, D.J.; Norton, J.F.

1999-12-01

Results of corrosion tests carried out on a series of Fe-12% Cr alloys in coal gasification environments t 600 C were studied. Effects of Si and Ti on corrosion resistance were assessed using data obtained from a commercial 12% Cr alloy, type 410 (UNS S41000), three specially cast model 12% Cr alloys containing 2.7% Si with Ti levels of 0%, 0.4% and 0.7%, respectively, and a higher alloy (type 28 [UNS N08028]) heat exchanger steel. Corrosion tests were carried out using simulated dry-feed entrained slagging gasifier gas The gas (64% carbon monoxide [CO], 3.8% carbon dioxide [CO{sub 2}], 0.8% hydrogenmore » sulfide [H{sub 2}S], and balance H{sub 2} [in vol%]) was premixed and passed over the test pieces at a rate high enough to prevent thermodynamic equilibrium achievement. Results showed that Si had a strongly beneficial influence on corrosion resistance. Ti, depending upon the amount added, exerted a positive or negative influence on corrosion resistance and reduced problems associated with workability. The kinetics of corrosion were presented in terms of weight-change and metal-loss measurements, the synergistic influences of Si and Ti were discussed, and corrosion resistance was compared with that exhibited by a commercial 12% Cr steel and type 28, the higher alloy material.« less

Corrosion in drinking water pipes: the importance of green rusts.

PubMed

Swietlik, Joanna; Raczyk-Stanisławiak, Urszula; Piszora, Paweł; Nawrocki, Jacek

2012-01-01

Complex crystallographic composition of the corrosion products is studied by diffraction methods and results obtained after different pre-treatment of samples are compared. The green rusts are found to be much more abundant in corrosion scales than it has been assumed so far. The characteristic and crystallographic composition of corrosion scales and deposits suspended in steady waters were analyzed by X-ray diffraction (XRD). The necessity of the examination of corrosion products in the wet conditions is indicated. The drying of the samples before analysis is shown to substantially change the crystallographic phases originally present in corrosion products. On sample drying the unstable green rusts is converted into more stable phases such as goethite and lepidocrocite, while the content of magnetite and siderite decreases. Three types of green rusts in wet materials sampled from tubercles are identified. Unexpectedly, in almost all corrosion scale samples significant amounts of the least stable green rust in chloride form was detected. Analysis of corrosion products suspended in steady water, which remained between tubercles and possibly in their interiors, revealed complex crystallographic composition of the sampled material. Goethite, lepidocrocite and magnetite as well as low amounts of siderite and quartz were present in all samples. Six different forms of green rusts were identified in the deposits separated from steady waters and the most abundant was carbonate green rust GR(CO(3)(2-))(I). Copyright © 2011 Elsevier Ltd. All rights reserved.

Corrosion barriers processed by Al electroplating and their resistance against flowing Pb-15.7Li

NASA Astrophysics Data System (ADS)

Krauss, Wolfgang; Konys, Jürgen; Wulf, Sven-Erik

2014-12-01

In the HCLL blanket design, ferritic-martensitic steels are in direct contact with the flowing liquid breeder Pb-15.7Li and have to withstand severe corrosion attack. Beyond corrosion, T-permeation from the breeder into the RAFM-steels is also an important issue and has to be reduced significantly. Earlier work showed that Al-based coatings can act as barriers for both, however, applied processes e.g. HDA or VPS exhibited strong drawbacks in the past. Meanwhile new industrial relevant coating processes, using electroplating technology are under development and called ECA (electrochemical aluminization) and ECX (electrochemical deposition from ionic liquids) process. In this study electrochemically Al-coated and heat-treated Eurofer samples were tested in PICOLO loop for exposure times up to 12,000 h (ECA) and 2000 h (first results ECX) respectively to determine corrosion properties in flowing Pb-15.7Li (550 °C, 0.1 m/s). Cross section analysis afterward corrosion testing proved the ability of thin Al-based barriers made by electrochemical techniques to protect the bare Eurofer from corrosion attack even at exposure times of 12,000 h. Determined radial corrosion rates lay between 10 and 20 μm/a. First results for ECX coated samples (2000 h) revealed more homogeneous corrosion behavior of the barrier layer itself compared to ECA.

The influence of external factors on the corrosion resistance of high temperature superconductor thin films against moisture

NASA Astrophysics Data System (ADS)

Murugesan, M.; Obara, H.; Yamasaki, H.; Kosaka, S.

2006-12-01

High temperature superconductor (HTS) thin films have been systematically investigated for their corrosion resistance against moisture by studying the role of external factors such as temperature (T), relative humidity (RH), and the type of substrates in the corrosion. In general, (i) the corrosion is progressed monotonously with increasing T as well as RH, (ii) a threshold level of water vapor is needed to cause degradation, and (iii) between T and RH, the influence of T is more dominant. HTS films on SrTiO3 and CeO2 buffered sapphire (cbs) substrates showed better corrosion stability and a low rate of degradation in the critical current density as compared to that of the film grown on MgO substrate. Between DyBa2Cu3Oz (DBCO) and YBa2Cu3Oz, the former is reproducibly found to have many fold higher corrosion resistance against moisture. This observed enhancement in the corrosion resistance in DBCO could be explained by the improved microstructure in the films and the better lattice matching with the substrate. Thus, the dual advantage of DBCO/cbs films, i.e., the enhanced corrosion stability of DBCO and the appropriate dielectric properties of sapphire, can be readily exploited for the use of DBCO/cbs films in the microwave and power devices.

Stress-corrosion behavior of aluminum-lithium alloys in aqueous salt environments

NASA Technical Reports Server (NTRS)

Pizzo, P. P.; Galvin, R. P.; Nelson, H. G.

1984-01-01

The stress corrosion susceptibility of two powder metallurgy (P/M) alloys, Al-Li-Cu and Al-Li-Cu-Mg; two mechanically attrited (M/A) alloys, Al-Li-Cu and Al-Li-Mg; and two wrought, ingot alloys, X-2020 and AA7475, are compared. Time-dependent fracture in an aqueous sodium chloride environment under alternate immersion condition was found to vary significantly between alloys. The stress corrosion behavior of the two powder metallurgy processed alloys was studied in detail under conditions of crack initiation, static crack growth, and fatigue crack growth. A variety of stress corrosion tests were performed including smooth surface, time-to-failure tests; potentiostatic tests on smooth surfaces exposed to constant applied strain rates; and fracture mechanics-type tests under static and cyclic loads. Both alloys show surface pitting and subsequent intergranular corrosion. Pitting is more severe in the magnesium-bearing alloy and is associated with stringer particles strung along the extrusion direction as a result of P/M processing.

Stress-corrosion behavior of aluminum-lithium alloys in aqueous environments

NASA Technical Reports Server (NTRS)

Pizzo, P. P.; Galvin, R. P.; Nelson, H. G.

1983-01-01

The stress corrosion susceptibility of two powder metallurgy (P/M) alloys, Al-Li-Cu and Al-Li-Cu-Mg two mechanically attrited (M/A) alloys, Al-Li-Cu and Al-Li-Mg; and two wrought, ingot alloys, X-2020 and AA7475, are compared. Time-dependent fracture in an aqueous sodium chloride environment under alternate immersion condition was found to vary significantly between alloys. The stress corrosion behavior of the two powder metallurgy processed alloys was studied in detail under conditions of crack initiation, static crack growth, and fatigue crack growth. A variety of stress corrosion tests were performed including smooth surface, time-to-failure tests; potentiostatic tests on smooth surfaces exposed to constant applied strain rates; and fracture mechanics-type tests under static and cyclic loads. Both alloys show surface pitting and subsequent intergranular corrosion. Pitting is more severe in the magnesium-bearing alloy and is associated with stringer particles strung along the extrusion direction as a result of P/M processing.

Comparison of some dietary habits on corrosion behavior of stainless steel brackets: an in vitro study.

PubMed

Shahabi, M; Jahanbin, A; Esmaily, H; Sharifi, H; Salari, S

2011-01-01

Resistance to corrosion is an advantageous property of orthodontic brackets; however, due to low levels of pH found in the mouth of a patient, localized corrosion may occur This can affect tooth movement by increasing friction between the arch wire and bracket slot and initiate enamel discoloration. Additionally, corrosion causes the release of elements that may lead to cytotoxic and biological side effects. The aim of this study was to compare the amount of corrosion caused by lemon juice, vinegar and Coca-Cola on orthodontic brackets in vitro and then to recommend the most suitable diet during orthodontic treatment. Sixty orthodontic brackets in three groups of twenty were immersed in a test solution (Fusamaya-Meyer artificial saliva plus lemon juice, vinegar or Coca-Cola) at a temperature of 37 degrees C +/- 1. Moreover, a negative control consisting of twenty brackets were put in pure artificial saliva. After 6 weeks the amount of corrosion was determined by measuring delta W of mean weights of brackets and the results were analyzed by general linear models (repeated measurement). Significant differences were seen during different weeks of the study (P < 0.001) and different solutions (P < 0.001). This study showed the amount of corrosion in orthodontic brackets was the most for cola followed by vinegar and then lemon juice. In addition, mean differences for cola versus lemon juice was -0.010 (sig. <0.001), vinegar versus lemon juice was -0.006 (sig. = 0.001) and cola versus vinegar was -0.004 (sig. = 0.013). Acidic effervescent soft drinks such as cola have to be eliminated or minimized in the nutritional diet of orthodontic patients because of their harmful effects on their brackets.

The Use of AC-DC-AC Methods in Assessing Corrosion Resistance Performance of Coating Systems for Magnesium Alloys

NASA Astrophysics Data System (ADS)

McCune, Robert C.; Upadhyay, Vinod; Wang, Yar-Ming; Battocchi, Dante

The potential utility of AC-DC-AC electrochemical methods in comparative measures of corrosion-resisting coating system performance for magnesium alloys under consideration for the USAMP "Magnesium Front End Research and Development" project was previously shown in this forum [1]. Additional studies of this approach using statistically-designed experiments have been conducted with focus on alloy types, pretreatment, topcoat material and topcoat thickness as the variables. Additionally, sample coupons made for these designed experiments were also subjected to a typical automotive cyclic corrosion test cycle (SAE J2334) as well as ASTM B117 for comparison of relative performance. Results of these studies are presented along with advantages and limitations of the proposed methodology.

Mechanical and corrosion properties of newly developed biodegradable Zn-based alloys for bone fixation.

PubMed

Vojtěch, D; Kubásek, J; Serák, J; Novák, P

2011-09-01

In the present work Zn-Mg alloys containing up to 3wt.% Mg were studied as potential biodegradable materials for medical use. The structure, mechanical properties and corrosion behavior of these alloys were investigated and compared with those of pure Mg, AZ91HP and casting Zn-Al-Cu alloys. The structures were examined by light and scanning electron microscopy (SEM), and tensile and hardness testing were used to characterize the mechanical properties of the alloys. The corrosion behavior of the materials in simulated body fluid with pH values of 5, 7 and 10 was determined by immersion tests, potentiodynamic measurements and by monitoring the pH value evolution during corrosion. The surfaces of the corroded alloys were investigated by SEM, energy-dispersive spectrometry and X-ray photoelectron spectroscopy. It was found that a maximum strength and elongation of 150MPa and 2%, respectively, were achieved at Mg contents of approximately 1wt.%. These mechanical properties are discussed in relation to the structural features of the alloys. The corrosion rates of the Zn-Mg alloys were determined to be significantly lower than those of Mg and AZ91HP alloys. The former alloys corroded at rates of the order of tens of microns per year, whereas the corrosion rates of the latter were of the order of hundreds of microns per year. Possible zinc doses and toxicity were estimated from the corrosion behavior of the zinc alloys. It was found that these doses are negligible compared with the tolerable biological daily limit of zinc. Copyright © 2011 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

Corrosion protection service life of epoxy-coated reinforcing steel in Virginia bridge decks.

DOT National Transportation Integrated Search

2003-01-01

The corrosion protection service life extension provided by epoxy-coated reinforcement (ECR) was determined by comparing ECR and bare steel bars from 10 Virginia bridge decks built between 1981 and 1995. The objective was to determine the corrosion p...

Studies on microstructure, mechanical and corrosion properties of high nitrogen stainless steel shielded metal arc welds

NASA Astrophysics Data System (ADS)

Mohammed, Raffi; Madhusudhan Reddy, G.; Srinivasa Rao, K.

2018-03-01

The present work is aimed at studying the microstructure, mechanical and corrosion properties of high nitrogen stainless steel shielded metal arc (SMA) welds made with Cromang-N electrode. Basis for selecting this electrode is to increase the solubility of nitrogen in weld metal due to high chromium and manganese content. Microstructures of the welds were characterized using optical microscopy (OM), field emission scanning electron microscopy (FESEM) and electron back scattered diffraction (EBSD) mainly to determine the morphology, phase analysis, grain size and orientation image mapping. Hardness, tensile and ductility bend tests were carried out to determine mechanical properties. Potentio-dynamic polarization testing was carried out to study the pitting corrosion resistance using a GillAC basic electrochemical system. Constant load type testing was carried out to study stress corrosion cracking (SCC) behaviour of welds. The investigation results shown that the selected Cr–Mn–N type electrode resulted in favourable microstructure and completely solidified as single phase coarse austenite. Mechanical properties of SMA welds are found to be inferior when compared to that of base metal and is due to coarse and dendritic structure.

Corrosion Performance of New Generation Aluminum-Lithium Alloys for Aerospace Applications

NASA Astrophysics Data System (ADS)

Moran, James P.; Bovard, Francine S.; Chrzan, James D.; Vandenburgh, Peter

Over the past several years, a new generation of aluminum-lithium alloys has been developed. These alloys are characterized by excellent strength, low density, and high modulus of elasticity and are therefore of interest for lightweight structural materials applications particularly for construction of current and future aircraft. These new alloys have also demonstrated significant improvements in corrosion resistance when compared with the legacy and incumbent alloys. This paper documents the superior corrosion resistance of the current commercial tempers of these materials and also discusses the corrosion performance as a function of the degree of artificial aging. Results from laboratory corrosion tests are compared with results from exposures in a seacoast atmosphere to assess the predictive capability of the laboratory tests. The correlations that have been developed between the laboratory tests and the seacoast exposures provide confidence that a set of available methods can provide an accurate assessment of the corrosion performance of this new generation of alloys.

Effect of Precipitate State on Mechanical Properties, Corrosion Behavior, and Microstructures of Al-Zn-Mg-Cu Alloy

NASA Astrophysics Data System (ADS)

Peng, Xiaoyan; Li, Yao; Xu, Guofu; Huang, Jiwu; Yin, Zhimin

2018-03-01

The mechanical properties, corrosion behavior and microstructures of the Al-Zn-Mg-Cu alloy under various ageing treatments were investigated comparatively. The results show that the tensile strength and corrosion resistance are strongly affected by the precipitate state. Massive fine intragranular precipitates contribute to high strength. Discontinuous coarse grain boundary precipitates containing high Cu content, as well as the narrow precipitate free zone, result in low corrosion susceptibility. After the non-isothermal ageing (NIA) treatment, the tensile strength of 577 MPa is equivalent to that of 579 MPa for the T6 temper. Meanwhile, the stress corrosion susceptibility r tf and the maximum corrosion depth are 97.8% and 23.5 μm, which are comparable to those of 92.8% and 26.7 μm for the T73 temper. Moreover, the total ageing time of the NIA treatment is only 7.25 h, which is much less than that of 48.67 h for the retrogression and re-ageing condition.

Corrosion behavior of alloy 800H (Fe-21Cr-32Ni) in supercritical water

DOE Office of Scientific and Technical Information (OSTI.GOV)

Tan, Lizhen; Allen, Todd R.; Yang, Ying

2011-01-01

The effect of testing conditions (temperature, time, and oxygen content) and material's microstructure (the as-received and the grain boundary engineered conditions) on the corrosion behavior of alloy 800H in high-temperature pressurized water was studied using a variety of characterization techniques. Oxidation was observed as the primary corrosion behavior on the samples. Oxide exfoliation was significantly mitigated on the grain boundary engineered samples compared to the as-received ones. The oxide formation, including some 'mushroom-shaped oxidation', is predicted via a combination of thermodynamics and kinetics influenced by the preferential diffusion of specific species using short-cut diffusion paths.

Corrosion of carbon steels, stainless steels, and titanium in aqueous lithium bromide solution

DOE Office of Scientific and Technical Information (OSTI.GOV)

Guinon, J.L.; Garcia-Anton, J.; Perez-Herranz, V.

1994-03-01

Effects of lithium bromide (LiBr) concentration, pH, temperature, exposure time, and the action of some inhibitors on corrosion of several carbon (C) steels, stainless steels (SS), and a titanium (Ti) alloy were studied. Corrosion rates were determined by the polarization resistance method and compared to rates determined by weight-loss measurements. Pitting potentials (E[sub p]) were evaluated in neutral LiBr solution and with different inhibitors. Pit density and average pit depth depended on the metal tested, with lowest values for Ti, the next lowest values for type 316 SS (UNS S31600), and the highest values for UNS G41350 tempered steel.

A Comparative Study on the Effect of MWCNT as Reinforcement on the Corrosion Parameters of Different Ni-W/MWCNTs Nanocomposite Coatings in Various Corrosive Media

NASA Astrophysics Data System (ADS)

Mohammadpour, Zahra; Zare, Hamid R.

2018-07-01

Nickel-tungsten multi-walled carbon nanotubes (Ni-W/MWCNTs) nanocomposite coatings were co-electrodeposited in the ammonium-free bath by means of constant direct current coulometry. The results indicate that the amount of MWCNTs incorporated into the nanocomposite coatings has a key role in the improvement of their microhardness and corrosion resistance. The corrosion behavior of the coatings was evaluated using potentiodynamic polarization and electrochemical impedance spectroscopy methods in three corrosive media of 3.5 wt% NaCl, 1.0 M NaOH, and 0.5 M H2SO4. The experimental data of the corrosion current density (jcorr), corrosion rate (CR), the polarization resistance (Rp), and microhardness indicate that the presence of MWCNTs in coatings improves the quality of those coatings. The surface morphology of the coatings and the elemental analysis data were obtained by scanning electron microscopy and energy dispersive X-ray microanalysis respectively. As the results showed, the coatings were uniform and crack-free in the presence of 5.3 wt% carbon. Also, a microhardness test revealed that the nanocomposite coating containing 5.3 wt% carbon obtained in an ammonium-free bath which provided the higher content of tungsten had the highest hardness value among others.

A Comparative Study on the Effect of MWCNT as Reinforcement on the Corrosion Parameters of Different Ni-W/MWCNTs Nanocomposite Coatings in Various Corrosive Media

NASA Astrophysics Data System (ADS)

Mohammadpour, Zahra; Zare, Hamid R.

2018-03-01

Nickel-tungsten multi-walled carbon nanotubes (Ni-W/MWCNTs) nanocomposite coatings were co-electrodeposited in the ammonium-free bath by means of constant direct current coulometry. The results indicate that the amount of MWCNTs incorporated into the nanocomposite coatings has a key role in the improvement of their microhardness and corrosion resistance. The corrosion behavior of the coatings was evaluated using potentiodynamic polarization and electrochemical impedance spectroscopy methods in three corrosive media of 3.5 wt% NaCl, 1.0 M NaOH, and 0.5 M H2SO4. The experimental data of the corrosion current density (jcorr), corrosion rate (CR), the polarization resistance (Rp), and microhardness indicate that the presence of MWCNTs in coatings improves the quality of those coatings. The surface morphology of the coatings and the elemental analysis data were obtained by scanning electron microscopy and energy dispersive X-ray microanalysis respectively. As the results showed, the coatings were uniform and crack-free in the presence of 5.3 wt% carbon. Also, a microhardness test revealed that the nanocomposite coating containing 5.3 wt% carbon obtained in an ammonium-free bath which provided the higher content of tungsten had the highest hardness value among others.

Wear and Corrosion Properties of 316L-SiC Composite Coating Deposited by Cold Spray on Magnesium Alloy

NASA Astrophysics Data System (ADS)

Chen, Jie; Ma, Bing; Liu, Guang; Song, Hui; Wu, Jinming; Cui, Lang; Zheng, Ziyun

2017-08-01

In order to improve the wear and corrosion resistance of commonly used magnesium alloys, 316L stainless steel coating and 316L-SiC composite coating have been deposited directly on commercial AZ80 magnesium alloy using cold spraying technology (CS). The microstructure, hardness and bonding strength of as-sprayed coatings were studied. Their tribological properties sliding against Si3N4 and GCr15 steel under unlubricated conditions were evaluated by a ball-on-disk tribometer. Corrosion behaviors of coated samples were also evaluated and compared to that of uncoated magnesium alloy substrate in 3.5 wt.% NaCl solution by electrochemical measurements. Scanning electron microscopy was used to characterize the corresponding wear tracks and corroded surfaces to determine wear and corrosion mechanisms. The results showed that the as-sprayed coatings possessed higher microhardness and more excellent wear resistance than magnesium alloy substrate. Meanwhile, 316L and 316L-SiC coating also reduced the corrosion current density of magnesium alloy and the galvanic corrosion of the substrates was not observed after 200-h neutral salt spray exposure, which demonstrated that corrosion resistance of a magnesium alloy substrate could be greatly improved by cold-sprayed stainless steel-based coatings.

Corrosion and tribological properties of basalt fiber reinforced composite materials

NASA Astrophysics Data System (ADS)

Ha, Jin Cheol; Kim, Yun-Hae; Lee, Myeong-Hoon; Moon, Kyung-Man; Park, Se-Ho

2015-03-01

This experiment has examined the corrosion and tribological properties of basalt fiber reinforced composite materials. There were slight changes of weight after the occurring of corrosion based on time and H2SO4 concentration, but in general, the weight increased. It is assumed that this happens due to the basalt fiber precipitate. Prior to the corrosion, friction-wear behavior showed irregular patterns compared to metallic materials, and when it was compared with the behavior after the corrosion, the coefficient of friction was 2 to 3 times greater. The coefficient of friction of all test specimen ranged from 0.1 to 0.2. Such a result has proven that the basalt fiber, similar to the resin rubber, shows regular patterns regardless of time and H2SO4 concentration because of the space made between resins and reinforced materials.

Corrosion Effects on the Fatigue Crack Propagation of Giga-Grade Steel and its Heat Affected Zone in pH Buffer Solutions for Automotive Application

NASA Astrophysics Data System (ADS)

Lee, H. S.

2018-03-01

Corrosion fatigue crack propagation test was conducted of giga-grade steel and its heat affected zone in pH buffer solutions, and the results were compared with model predictions. Pure corrosion effect on fatigue crack propagation, particularly, in corrosive environment was evaluated by means of the modified Forman equation. As shown in results, the average corrosion rate determined from the ratio of pure corrosion induced crack length to entire crack length under a cycle load were 0.11 and 0.37 for base metal and heat affected zone, respectively, with load ratio of 0.5, frequency of 0.5 and pH 10.0 environment. These results demonstrate new interpretation methodology for corrosion fatigue crack propagation enabling the pure corrosion effects on the behavior to be determined.

Biodegradability engineering of biodegradable Mg alloys: Tailoring the electrochemical properties and microstructure of constituent phases

PubMed Central

Cha, Pil-Ryung; Han, Hyung-Seop; Yang, Gui-Fu; Kim, Yu-Chan; Hong, Ki-Ha; Lee, Seung-Cheol; Jung, Jae-Young; Ahn, Jae-Pyeong; Kim, Young-Yul; Cho, Sung-Youn; Byun, Ji Young; Lee, Kang-Sik; Yang, Seok-Jo; Seok, Hyun-Kwang

2013-01-01

Crystalline Mg-based alloys with a distinct reduction in hydrogen evolution were prepared through both electrochemical and microstructural engineering of the constituent phases. The addition of Zn to Mg-Ca alloy modified the corrosion potentials of two constituent phases (Mg + Mg2Ca), which prevented the formation of a galvanic circuit and achieved a comparable corrosion rate to high purity Mg. Furthermore, effective grain refinement induced by the extrusion allowed the achievement of much lower corrosion rate than high purity Mg. Animal studies confirmed the large reduction in hydrogen evolution and revealed good tissue compatibility with increased bone deposition around the newly developed Mg alloy implants. Thus, high strength Mg-Ca-Zn alloys with medically acceptable corrosion rate were developed and showed great potential for use in a new generation of biodegradable implants. PMID:23917705

The Use of Neutron Analysis Techniques for Detecting The Concentration And Distribution of Chloride Ions in Archaeological Iron

PubMed Central

Watkinson, D; Rimmer, M; Kasztovszky, Z; Kis, Z; Maróti, B; Szentmiklósi, L

2014-01-01

Chloride (Cl) ions diffuse into iron objects during burial and drive corrosion after excavation. Located under corrosion layers, Cl is inaccessible to many analytical techniques. Neutron analysis offers non-destructive avenues for determining Cl content and distribution in objects. A pilot study used prompt gamma activation analysis (PGAA) and prompt gamma activation imaging (PGAI) to analyse the bulk concentration and longitudinal distribution of Cl in archaeological iron objects. This correlated with the object corrosion rate measured by oxygen consumption, and compared well with Cl measurement using a specific ion meter. High-Cl areas were linked with visible damage to the corrosion layers and attack of the iron core. Neutron techniques have significant advantages in the analysis of archaeological metals, including penetration depth and low detection limits. PMID:26028670

Mössbauer study of oxide films of Fe-, Sn-, Cr- doped zirconium alloys during corrosion in autoclave

NASA Astrophysics Data System (ADS)

Filippov, V. P.; Bateev, A. B.; Lauer, Yu. A.

2016-12-01

Mössbauer investigations were used to compare iron atom states in oxide films of binary Zr-Fe, ternary Zr-Fe-Cu and quaternary Zr-Fe-Cr-Sn alloys. Oxide films are received in an autoclave at a temperature of 350-360 °C and at pressure of 16.8 MPa. The corrosion process decomposes the intermetallic precipitates in alloys and forms metallic iron with inclusions of chromium atoms α-Fe(Cr), α-Fe(Cu), α-Fe 2O3 and Fe 3O4 compounds. Some iron ions are formed in divalent and in trivalent paramagnetic states. The additional doping influences on corrosion kinetics and concentration of iron compounds and phases formed in oxide films. It was shown the correlation between concentration of iron in different chemical states and corrosion resistance of alloys.

Corrosion resistance and in-vitro bioactivity of BaO containing Na2O-CaO-P2O5 phosphate glass-ceramic coating prepared on 316 L, duplex stainless steel 2205 and Ti6Al4V

NASA Astrophysics Data System (ADS)

Edathazhe, Akhila B.; Shashikala, H. D.

2018-03-01

The phosphate glass with composition 11Na2O-15BaO-29CaO-45P2O5 was coated on biomedical implant materials such as stainless steel 316 L, duplex stainless steel (DSS) 2205 and Ti6Al4V alloy by thermal enamelling method. The structural properties and composition of glass coated substrates were studied by x-ray diffraction (XRD), Scanning electron microscopy (SEM) and Energy dispersive x-ray spectroscopy (EDS) analysis. The coatings were partially crystalline in nature with porous structure and pore size varied from micro to nanometer range. The polarization curve was obtained for uncoated and coated substrates from electrochemical corrosion test which was conducted at 37 °C in Hank’s balanced salt solution (HBSS). The corrosion resistance of 316 L substrate increased after coating, whereas it decreased in case of DSS 2205 and Ti6Al4V. The XRD and SEM/EDS studies indicated the bioactive hydroxyapatite (HAp) layer formation on all the coated surfaces after electrochemical corrosion test, which improved the corrosion resistance. The observed electrochemical corrosion behavior can be explained based on protective HAp layer formation, composition and diffusion of ions on glass coated surfaces. The in-vitro bioactivity test was carried out at 37 °C in HBS solution for 14 days under static conditions for uncoated and coated substrates. pH and ion release rate measurements from the coated samples were conducted to substantiate the electrochemical corrosion test. The lower ion release rates of Na+ and Ca2+ from coated 316 L supported its higher electrochemical corrosion resistance among coated samples. Among the uncoated substrates, DSS showed higher electrochemical corrosion resistance. Amorphous calcium-phosphate (ACP) layer formation on all the coated substrates after in-vitro bioactivity test was confirmed by XRD, SEM/EDS and ion release measurements. The present work is a comparative study of corrosion resistance and bioactivity of glass coated and uncoated biomedical implants such as 316 L, DSS and Ti6Al4V.

In-situ monitoring of undercoating corrosion damage by Direct Optical Interrogation (DOI)

NASA Astrophysics Data System (ADS)

Lopez-Garrity, Meng

An approach referred to as "Direct Optical Interrogation" (DOI) has been developed as an extension of the thin film pitting approach developed and used by Frankel and others. Samples were prepared by depositing Al and Al-Cu alloy metallizations about 800 nm thick on glass substrates. These metallizations were then coated with various coatings and coating systems. Samples were introduced to aggressive environments and the progression of corrosion of the metallization under the coating was monitored in situ using low power videography. Because metallizations were thin, corrosion quickly penetrated through the metal layer to the glass substrate and then spread laterally. Measurement of the lateral spread of corrosion enabled non-electrochemical assessment of the corrosion kinetics. In Al-Cu thin films, both aged and as-deposited, corrosion sites are irregularly shaped because there is not enough cathodic current to propagate the entire corrosion site margin at equal rates. In a number of cases, corrosion propagates with a filamentary morphology resembling filiform corrosion. Cu played a strong role in determining under coating corrosion morphology and growth kinetics in experiments with Al-Cu thin films substrates. As-deposited Al-Cu metallizations were more corrosion resistant than aged metallization and both were more corrosion resistant than pure Al. Cu-rich dendrites were formed on the corrosion front. Corrosion rate (current density) was calculated using Faraday's law by collecting corrosion site perimeter and bottom area. Systematic exploration of the effects of a chromate and chromate-free conversion coatings, chromate and chromate-free primer coatings and the presence or absence of a polyurethane topcoat confirmed the extraordinary corrosion protection by chromates. A commercial praseodymium-pigmented primer coating was not particularly effective in retarding undercoating corrosion site growth unless paired with a chromate conversion coating. The presence of a topcoat dramatically reduces undercoating corrosion and masks many deficiencies of a conversion coating or primer. DOI was used to compare undercoating corrosion that developed due to exposure in ASTM B117, ASTM G85-A5 and outdoor environments. Similar corrosion morphologies developed in ASTM B117 and static immersion exposures. A single and stable corrosions site nucleated and propagated with a filamentary morphology. In general, salt spray exposure was more aggressive than static immersion. ASTM G85-A5 exposure produced different corrosion morphologies. Corrosion sites were round rather than filamentary. Massive nucleation of small corrosion sites across the whole surface also occurred. ASTM G85 environment was mild compared with the ASTM B117 and static immersion exposures. In outdoor exposure testing carried out for 5 months, no signs of corrosion was observed. To assess the extent to which oxygen reduction occurring on the coated surface supported corrosion site growth, a universal pH indicator was added to agar gels or PVB coatings applied on top of metallizations. Color changes indicating pH changes associated with local alkalization or acidification due to local cell action were assessed visually. Overall, the evidence is consistent with the idea that both hydrogen reduction and oxygen reduction support local corrosion site growth. In practical embodiments of corrosion protection, every effort should be made to restrict oxygen reduction to slow corrosion growth rates.

Comparative Stress Corrosion Cracking and General Corrosion Resistance of Annealed and Hardened 440 C Stainless Steel - New Techniques in Stress Corrosion Testing

NASA Technical Reports Server (NTRS)

Mendreck, M. J.; Hurless, B. E.; Torres, P. D.; Danford, M. D.

1998-01-01

The corrosion and stress corrosion cracking (SCC) characteristics of annealed and hardened 440C stainless steel were evaluated in high humidity and 3.5-percent NaCl solution. Corrosion testing consisted of an evaluation of flat plates, with and without grease, in high humidity, as well as electrochemical testing in 3.5-percent NaCl. Stress corrosion testing consisted of conventional, constant strain, smooth bar testing in high humidity in addition to two relatively new techniques under evaluation at MSFC. These techniques involve either incremental or constant rate increases in the load applied to a precracked SE(B) specimen, monitoring the crack-opening-displacement response for indications of crack growth. The electrochemical corrosion testing demonstrated an order of magnitude greater general corrosion rate in the annealed 440C. All techniques for stress corrosion testing showed substantially better SCC resistance in the annealed material. The efficacy of the new techniques for stress corrosion testing was demonstrated both by the savings in time and the ability to better quantify SCC data.

Biofilms affecting progression of mild steel corrosion by Gram positive Bacillus sp.

PubMed

Lin, Johnson; Madida, Bafana B

2015-10-01

The biodeterioration of metals have detrimental effects on the environment with economic implications. The deterioration of metals is of great concern to industry. In this study, mild steel coupons which were immersed in a medium containing Gram-positive Bacillus spp. and different nutrient sources were compared with the control in sterile deionized water. The weight loss of the coupons in the presence of Bacillus spp. alone was lower than the control and was further reduced when additional carbon sources, especially fructose, were added. The level of metal corrosion was significantly increased in the presence of nitrate with or without bacteria. There was a significant strong correlation between the weight loss and biofilm level (r =  0.64; p < 0.05). The addition of nitrate and Bacillus spp. produced more biofilms on the coupons and resulted in greater weight loss compared to that with Bacillus spp. only under the same conditions. However, Bacillus spp. enriched with carbon sources formed less biofilms and results in lower weight loss compared to that with Bacillus spp. only. The production of biofilm by Bacillus spp. influences the level of metal corrosion under different environmental conditions, thereby, supporting the development of a preventive strategy against corrosion. © 2015 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Studies on corrosion resistance and bio-activity of plasma spray deposited hydroxylapatite (HA) based TiO2 and ZrO2 dispersed composite coatings on titanium alloy (Ti-6Al-4V) and the same after post spray heat treatment

NASA Astrophysics Data System (ADS)

Kumari, Renu; Majumdar, Jyotsna Dutta

2017-10-01

In the present study, the effect of plasma spray deposited hydroxylapatite (HA) based TiO2 dispersed (HA + 50 wt.% TiO2), coating and post spray heat treatment to be referred as HA-TiO2 (heat treated at 650 °C for 2 h) and ZrO2 dispersed (HA + 10 wt.% ZrO2), to be referred as HA-ZrO2 coating (heat treated at 750 °C for 2 h) on corrosion resistance and bioactivity of Ti-6Al-4V substrate has been undertaken. There is partial decomposition of HA to tri-calcium-phosphate (Ca3(PO4)2) and formation of CaTiO3 phase in HA-TiO2 coating and CaZrO3 phase in the HA-ZrO2 coating. Corrosion study in Hank's solution shows that there is shifting of corrosion potential (Ecorr) towards active potential (-1.1 V(SCE) for as-sprayed and post spray heat treated HA-TiO2 coating, -1.1 V(SCE) for as-sprayed HA-ZrO2 coating and -1 V(SCE) for HA-ZO2 coating after post spray heat treatment), and deterioration in pitting corrosion (Epit) resistance in as-sprayed coatings and the same after heat treatment (-0.7 V(SCE) for both HA-TiO2 and HA-ZrO2 coating as compared to as received substrate (-0.3 V(SCE)). The corrosion rate was increased for both the coatings with a maximum increase in HA-ZrO2 coating. Bioactivity test shows a higher degree of apatite deposition in as-sprayed coating and the same after heat treatment as compared to as received Ti-6Al-4V though the as-sprayed one showed a superior behavior.

Preparation and corrosion resistance of electroless Ni-P/SiC functionally gradient coatings on AZ91D magnesium alloy

NASA Astrophysics Data System (ADS)

Wang, Hui-Long; Liu, Ling-Yun; Dou, Yong; Zhang, Wen-Zhu; Jiang, Wen-Feng

2013-12-01

In this paper, the protective electroless Ni-P/SiC gradient coatings on AZ91D magnesium alloy substrate were successfully prepared. The prepared Ni-P/SiC gradient coatings were characterized for its microstructure, morphology, microhardness and adhesion to the substrate. The deposition reaction kinetics was investigated and an empirical rate equation for electroless Ni-P/SiC plating on AZ91D magnesium alloy was developed. The anticorrosion properties of the Ni-P/SiC gradient coatings in 3.5 wt.% NaCl solution were evaluated by potentiodynamic polarization and electrochemical impedance spectroscopy (EIS) studies. The potentiodynamic polarization measurements revealed that the SiC concentration in the bath and heat treatment can influence the corrosion protection performance of electroless deposited Ni-P/SiC gradient coatings. EIS studies indicated that higher charge transfer resistance and slightly lower capacitance values were obtained for Ni-P/SiC gradient coatings compared to Ni-P coatings. The corrosion resistance of the Ni-P/SiC gradient coatings increases initially and decreases afterwards with the sustained increasing of immersion time in the aggressive medium. The electroless Ni-P/SiC gradient coatings can afford better corrosion protection for magnesium alloy substrate compared with Ni-P coatings.

Study on Microstructure and Electrochemical Corrosion Behavior of PEO Coatings Formed on Aluminum Alloy

NASA Astrophysics Data System (ADS)

Xiang, N.; Song, R. G.; Li, H.; Wang, C.; Mao, Q. Z.; Xiong, Y.

2015-12-01

Plasma electrolytic oxidation (PEO) treated 6063 aluminum alloy was applied in a silicate- and borate-based alkaline solution. The microstructure and electrochemical corrosion behavior were studied by scanning electron microscopy, electrochemical impedance spectroscopy (EIS), and potentiodynamic polarization techniques. The results showed that the silicate-based PEO coating was of a denser structure compared with that of borate-based PEO coating. In addition, the silicate-based PEO coating was composed of more phased (Al9Si) than borate-based PEO coating. The results of corrosion test indicated that the silicate-based PEO coating provided a superior protection to 6063 aluminum alloy substrate, while borate-based PEO coating with a porous structure showed an inferior conservancy against corrosive electrolyte. Furthermore, the EIS tests proved that both coatings were capable to resist the aggressive erosion in 0.5 M NaCl solution after 72 h of immersion. However, the borate-based PEO coating could not provide sufficient protection to the substrate after 72-h immersion in 1 M NaCl solution.

Solid lipid nanoparticles suspension versus commercial solutions for dermal delivery of minoxidil.

PubMed

Padois, Karine; Cantiéni, Céline; Bertholle, Valérie; Bardel, Claire; Pirot, Fabrice; Falson, Françoise

2011-09-15

Solid lipid nanoparticles have been reported as possible carrier for skin drug delivery. Solid lipid nanoparticles are produced from biocompatible and biodegradable lipids. Solid lipid nanoparticles made of semi-synthetic triglycerides stabilized with a mixture of polysorbate and sorbitan oleate were loaded with 5% of minoxidil. The prepared systems were characterized for particle size, pH and drug content. Ex vivo skin penetration studies were performed using Franz-type glass diffusion cells and pig ear skin. Ex vivo skin corrosion studies were realized with a method derived from the Corrositex(®) test. Solid lipid nanoparticles suspensions were compared to commercial solutions in terms of skin penetration and skin corrosion. Solid lipid nanoparticles suspensions have been shown as efficient as commercial solutions for skin penetration; and were non-corrosive while commercial solutions presented a corrosive potential. Solid lipid nanoparticles suspensions would constitute a promising formulation for hair loss treatment. Copyright © 2011 Elsevier B.V. All rights reserved.

Corrosion studies of DC reactive magnetron sputtered alumina coating on 304 SS

NASA Astrophysics Data System (ADS)

Thangaraj, Baskar; Mahadevan, Krishnan

2017-12-01

Aluminum oxide films on SS 304 deposited by DC reactive magnetron sputtering technique were studied with respect to the composition of the sputter gas (Ar:O2), gas pressure, substrate temperature, current etc. to achieve good insulating films with high corrosion resistance. The films were characterized by XRD and SEM techniques. Potentiodynamic polarization and electrochemical impedance spectroscopy measurements were made under static conditions in order to evaluate the corrosion performance of the alumina-coated SS 304 for various immersion durations in 0.5 M and 1 M NaCl solution. Alumina-coated SS 304 has low corrosion value of 0.4550 and 1.1090MPY for 24 h immersion time in both solutions. The impedance plots for the alumina coated SS 304 in 1 M NaCl solution at different durations are slightly different to when compared to its immersion in 0.5 M NaCl solutions and are composed of two depressed semi circles. For the alumina coated film, the impedance spectrum decreased, when immersion time increased.

Corrosion resistant metallic glasses for biosensing applications

NASA Astrophysics Data System (ADS)

Sagasti, Ariane; Lopes, Ana Catarina; Lasheras, Andoni; Palomares, Verónica; Carrizo, Javier; Gutierrez, Jon; Barandiaran, J. Manuel

2018-04-01

We report the fabrication by melt spinning, the magnetic and magnetoelastic characterization and corrosion behaviour study (by potentiodynamic methods) of an Fe-based, Fe-Ni-Cr-Si-B metallic glass to be used as resonant platform for biological and chemical detection purposes. The same study has been performed in Fe-Co-Si-B (with excellent magnetoelastic properties) and Fe-Ni-B (with good corrosion properties due to the substitution of Co by Ni) composition amorphous alloys. The well-known, commercial metallic glass with high corrosion resistance Metglas 2826MB®(Fe40Ni38Mo4B18), widely used for such biological and chemical detection purposes, has been also fully characterized and used as reference. For our Fe-Ni-Cr-Si-B alloy, we have measured values of magnetization (1.22 T), magnetostriction (11.5 ppm) and ΔE effect (6.8 %) values, as well as corrosion potential (-0.25 V), current density (2.54 A/m2), and polarization resistance (56.22 Ω.cm2) that make this composition very promising for the desired biosensing applications. The obtained parameters from our exhaustive characterization are compared with the values obtained for the other different composition metallic glasses and discussed in terms of Ni and Cr content.

Corrosion and Microstructure Correlation in Molten LiCl-KCl Medium

NASA Astrophysics Data System (ADS)

Ravi Shankar, A.; Mathiya, S.; Thyagarajan, K.; Kamachi Mudali, U.

2010-07-01

Pyrochemical reprocessing in molten chloride salt medium has been considered as one of the best options for the reprocessing of spent metallic fuels of future fast breeder reactors. The unit operations such as salt preparation, electrorefining, and cathode processing involve the presence of molten LiCl-KCl eutectic salt from 673 to 1373 K (400 to 1100 °C). The present work discusses the corrosion behavior of electroformed nickel (EF Ni) without and with nickel-tungsten (Ni-W) coating, 316L SS, and INCONEL 625 alloy in molten LiCl-KCl eutectic salt at 673 K, 773 K, and 873 K (400 °C, 500 °C, and 600 °C) in the presence of air. The weight percent loss of the exposed samples was determined by the weight loss method and surface morphology of the salt exposed, and product layers were examined by scanning electron microscopy (SEM). X-ray diffraction (XRD) and energy-dispersive X-ray (EDX) analysis were also carried out on the exposed and corrosion product layers to understand the phases present and the corrosion mechanism involved. The results of the present study indicated that INCONEL 625 alloy showed superior corrosion resistance compared to electroformed nickel (EF Ni), EF Ni with nickel-tungsten (Ni-W) coating (EF Ni-W), and 316L SS. The EF Ni with Ni-W coating exhibits better corrosion resistance than EF Ni without tungsten coating. Based on the surface morphology, XRD, and EDX analysis of corrosion product layers, the mechanism of corrosion of INCONEL 625 and 316L involves formation of chromium-rich compound at the surface and subsequent spallation. For the EF Ni, the porous thick NiO corrosion product allows the penetration of salt, thus accelerating the corrosion. Improved corrosion resistance of EF Ni-W was attributed to the W-rich NiO layer, while for INCONEL 625, the adherent and protective NiO layer improved the corrosion resistance. The article highlights the results of the present investigation.

Influence of laser surface treated on the characterization and corrosion behavior of Al-Fe aerospace alloys

NASA Astrophysics Data System (ADS)

Pariona, Moisés Meza; Teleginski, Viviane; dos Santos, Kelly; de Lima, Angela A. O. C.; Zara, Alfredo J.; Micene, Katieli Tives; Riva, Rudimar

2013-07-01

In this research laser surface remelting without protective coating with a 2 kW Yb-fiber laser (IPG YLR-2000S) was applied in the Al-1.5 wt.%Fe alloy in order to investigate the layer treated with different techniques of superficial characterization, thereby, the technique of optical microscopy, atomic force microscopy and low-angle X-ray diffraction were used. The present work mainly focuses on the corrosion study by diverse techniques in aggressive environment of the laser-treated area and the substrate material was carried out, thereby, at open circuit potential testing, the results have shown a displacement to more anodic values in the corrosion potential for the laser-treated specimen when compared to the untreated specimen; in potentiodynamic polarization tests have shown that as a result of the laser treatment, the corrosion current can be reduced by as much as ten times, and a passive region was obtained, which served as an effective barrier for reducing anodic dissolution and finally, the result in cyclic polarization curves of the untreated sample there was a greater area of the hysteresis loop, implying that it is more susceptible to corrosion. This study was complemented by other techniques mentioned above in order to elucidate this study. Laser surface remelting process has definitely modified the surface film, which results in higher corrosion resistance, a large range of passivation and a lower area of the hysteresis loop.

Effects of annealing heat treatment on the corrosion resistance of Zn/Mg/Zn multilayer coatings

NASA Astrophysics Data System (ADS)

Bae, KiTae; La, JoungHyun; Lee, InGyu; Lee, SangYul; Nam, KyungHoon

2017-05-01

Zn coatings alloyed with magnesium offer superior corrosion resistance compared to pure Zn or other Zn-based alloy coatings. In this study, Zn/Mg/Zn multilayer coatings with various Mg layer thicknesses were synthesized using an unbalanced magnetron sputtering process and were annealed to form Zn-Mg intermetallic phases. The effects of the annealing heat treatment on the corrosion resistance of the Zn/Mg/Zn multilayer coatings were evaluated using electrochemical measurements. The extensive diffusion of magnesium species into the upper and lower zinc layer from the magnesium layer in the middle of the coating was observed after the heat treatment. This phenomenon caused (a) the porous microstructure to transition into a dense structure and (b) the formation of a MgZn2 intermetallic phase. The results of the electrochemical measurements demonstrated that the heat treated Zn/Mg/Zn multilayer coatings possessed higher levels of corrosion resistance than the non-heat treated coatings. A Zn/Mg/Zn multilayer coating with MgZn2 and (Zn) phases showed the best corrosion resistance among the heat treated coatings, which could be attributed to the reduced galvanic corrosion effects due to a small potential gradient between the MgZn2 and zinc.

Effect of Glucose Concentration on Electrochemical Corrosion Behavior of Pure Titanium TA2 in Hanks’ Simulated Body Fluid

PubMed Central

Liu, Shuyue; Wang, Bing; Zhang, Peirong

2016-01-01

Titanium and its alloys have been widely used as implant materials due to their excellent mechanical property and biocompatibility. In the present study, the effect of glucose concentration on corrosion behavior of pure titanium TA2 in Hanks’ simulated body fluid is investigated by the electrochemical impedance spectrum (EIS) and potentiodynamic polarization methods. The range of glucose concentrations investigated in this research includes 5 mmol/L (limosis for healthy people), 7 mmol/L (after diet for healthy people), 10 mmol/L (limosis for hyperglycemia patient), and 12 mmol/L (after diet for hyperglycemia patient), as well as, 15 mmol/L and 20 mmol/L, which represent different body fluid environments. The results indicate that the pure titanium TA2 demonstrates the best corrosion resistance when the glucose concentration is less than 10 mmol/L, which shows that the pure titanium TA2 as implant material can play an effective role in the body fluids with normal and slight high glucose concentrations. Comparatively, the corrosion for the pure titanium implant is more probable when the glucose concentration is over 10 mmol/L due to the premature penetration through passive film on the material surface. Corrosion defects of pitting and crevice exist on the corroded surface, and the depth of corrosion is limited to three microns with a low corrosion rate. The oxidation film on the surface of pure titanium TA2 has a protective effect on the corrosion behavior of the implant inner material. The corrosion behavior of pure titanium TA2 will happen easily once the passive film has been penetrated through. The corrosion rate for TA2 implant will accelerate quickly and a pure titanium implant cannot be used. PMID:28773993

Corrosion Behaviour in Human Stimulation Media of a High Entropy Titan-Based Alloy

NASA Astrophysics Data System (ADS)

Ghiban, B.; Popescu, G.; Lazar, C.; Rosu, L.; Constantin, I.; Olaru, M.; Carlan, B.

2018-06-01

The paper presents results on the corrosion behavior of high entropy alloys, commonly called BIOHEA in human physiological simulating media, respectively in the NaCl infusion solution and Ringer’s lactate infusion solution. Corrosion tests were performed by potendiodinamic test using AUTOLAB type potentiostat equipped with specialized corrosion software including the PGSTAT302N, BA and SCAN250 modules. Three entropy alloy systems were investigated: FeTa0.5Nb0.5Ti1.5Zr0.5 (BIOHEA 1), FeMnNb0.5TiZr0.5 (BIOHEA 3), FeTa0.5Nb0.5TiZr0.5 (BIOHEA 4), and BIOHEA alloy 2 was obtained by remelting BIOHEA 1. A comparison of the results obtained in the present tests and the data from the literature shows, on the one hand, that the global results can be compared with the different results from the literature, and, on the other hand, the results are new, in the sense that in any work there are no combinations of alloys studied here or human simulating medians used for testing. The conclusion of the experimental investigations in the present paper is the fact that regardless of the simulation test environment, all the alloys experimental alloys have similar behaviors, there is a difference between the chemical composition of the experimental alloy and the displacement of the corrosion potential values at electropositive values, decreasing of corrosion current, and corrosion rates. The experimental results allow the corrosion resistance of the investigated alloys, alloy BIOHEA 2 having the best corrosion behavior in both test media, with very low corrosion rates (respectivelly 0.067 μm/year in NaCl infusion solution, and 0.021 μm / year in Ringer’s lactate infusion solution).

Titanium Ions Release from an Innovative Titanium-Magnesium Composite: an in Vitro Study.

PubMed

Stanec, Zlatko; Halambek, Jasna; Maldini, Krešimir; Balog, Martin; Križik, Peter; Schauperl, Zdravko; Ćatić, Amir

2016-03-01

The innovative titanium-magnesium composite (Ti-Mg) was produced by powder metallurgy (P/M) method and is characterized in terms of corrosion behavior. Two groups of experimental material, 1 mass% (Ti-1Mg) and 2 mass% (Ti-2Mg) of magnesium in titanium matrix, were tested and compared to commercially pure titanium (CP Ti). Immersion test and chemical analysis of four solutions: artificial saliva; artificial saliva pH 4; artificial saliva with fluoride and Hank balanced salt solution were performed after 42 days of immersion, using inductively coupled plasma mass spectrometry (ICP-MS) to detect the amount of released titanium ions (Ti). SEM and EDS analysis were used for surface characterization. The difference between the results from different test solutions was assessed by ANOVA and Newman-Keuls test at p<0.05. The influence of predictor variables was found by multiple regression analysis. The results of the present study revealed a low corrosion rate of titanium from the experimental Ti-Mg group. Up to 46 and 23 times lower dissolution of Ti from Ti-1Mg and Ti-2Mg, respectively was observed compared to the control group. Among the tested solutions, artificial saliva with fluorides exhibited the highest corrosion effect on all specimens tested. SEM micrographs showed preserved dual phase surface structure and EDS analysis suggested a favorable surface bioactivity. In conclusion, Ti-Mg produced by P/M as a material with better corrosion properties when compared to CP Ti is suggested.

Corrosion of Cu-xZn alloys in slightly alkaline chloride solutions studied by stripping voltammetry and microanalysis.

PubMed

Milosev, I; Minović, A

2001-01-01

The mechanism of corrosion of Cu-xZn alloys (x = 10-40 wt %) in slightly alkaline chloride solutions was investigated by analysing solid reaction products by energy dispersive X-ray analysis (EDS) and dissolved reaction products by differential anodic pulse stripping (DAPS) voltammetry. The corrosion process was studied under open circuit and under potentiostatic conditions at selected potentials. Pure metals were studied comparatively so that an interacting effect of particular metal components in the alloy could be determined. All four Cu-xZn alloys show an improved behaviour compared to pure metals. Under open-circuit condition both components dissolve simultaneously in the solution. With increasing immersion time the preferential, dissolution of zinc in the solution becomes pronounced. It is the highest for Cu-10Zn and the lowest for Cu-30Zn alloy. Under potentiostatic control the dissolution mechanism depends on the electrode potential and changes from exclusive dissolution of zinc to simultaneous dissolution of both components with preferential dissolution of zinc. The latter decreases, as the electrode potential becomes more positive.

Chromium-free conversion coatings based on inorganic salts (Zr/Ti/Mn/Mo) for aluminum alloys used in aircraft applications

NASA Astrophysics Data System (ADS)

Santa Coloma, P.; Izagirre, U.; Belaustegi, Y.; Jorcin, J. B.; Cano, F. J.; Lapeña, N.

2015-08-01

Novel chromium-free conversion coatings based on Zr/Ti/Mn/Mo compounds were developed at a pilot scale to improve the corrosion resistance of the AA2024-T3 and AA7075-T6 aluminum alloys for aircraft applications. The influence of the presence of Zr and Ti in the Zr/Ti/Mn/Mo conversion bath's formulation on the corrosion resistance of the coated alloys was investigated. The corrosion resistance provided by the conversion coatings was evaluated by salt spray exposure and potentiodynamic sweeps. Optical and scanning electron microscopy coupled with energy dispersive spectroscopy (SEM/EDS) and atomic force microscopy (AFM) operating in the Kelvin Probe mode (SKPFM) were used to provide microstructural information of the coated samples that achieved the best results in the corrosion tests. The salt spray test evidenced the higher corrosion resistance of the coated samples compared to the bare surfaces for both alloys. The potentiodynamic tests showed that the corrosion current density decreased for coated AA7075-T6 and AA2024-T3 alloys, which indicated an obvious improvement of the corrosion resistance with all the processes for both alloys. Although the corrosion resistance of the coated samples appeared to be higher for the alloy AA7075-T6 than for the alloy AA2024-T3, both alloys achieved the best corrosion protection with the coatings deposited from conversion bath formulations containing no titanium salts. The microscopy analysis on the coated AA7075-T6 samples revealed that a local deposition of Zr compounds and, possibly, an oxidation process occurred in the vicinity of the alloy's intermetallic particles. The amount of the Zr deposits at these locations increased with coating's formulations without Ti, which provided the best corrosion resistance. The Cr-free conversion coatings developed in this study for the AA7075-T6 and AA2024-T3 alloys do not meet yet the strict requirements of the aircraft industry. However, they significantly improved the corrosion performance with respect to the bare alloys and could be a good starting point for further studies and optimization.

The combined effects of prior-corrosion and aggressive chemical environments on fatigue crack growth behavior in aluminum alloy 7075-T651

NASA Astrophysics Data System (ADS)

Mills, Thomas Brian

1997-11-01

Exfoliation corrosion is a potentially severe form of corrosion that frequently affects high-strength aluminum, particularly 2xxx- and 7xxx-series alloys. Exfoliation degrades components such as sheets, plates, and extrusions that have highly elongated grain structures. Few attempts have been made to investigate the effects of this form of corrosion on the fatigue performance of these materials, so a preliminary study was conducted to determine the effects of exfoliation corrosion on the fatigue response of quarter-inch 7075-T651 aluminum alloy plate. This was accomplished by subjecting aluminum panels to an ASTM standard corrosive solution known as EXCO then fatiguing the panels in corrosion fatigue environments of dry air, humid air, and artificial acid rain. Statistical analyses of the fatigue crack growth data suggest that prior-corrosion and corrosion fatigue are competing mechanisms that both have the potential of accelerating crack growth rates. In the dry air cases, exfoliation accelerated crack growth rates a maximum of 4.75 times over the uncorroded material at lower stress intensities such as 5 ksi surdinch. This accelerated behavior dropped off rapidly, however, and was nonexistent at higher stress intensities. Humid air increased crack velocities considerably as compared to the dry air uncorroded case, but the addition of exfoliation corrosion to the humid cases did not have a significant effect on crack growth behavior. On the other hand, specimens containing exfoliation corrosion and then exposed to artificial acid rain had significantly higher crack growth rates than their uncorroded counterparts. Finally, fractographic examinations of the specimens revealed evidence of lower energy, quasi-cleavage fracture persisting near to the exfoliated edge of specimens tested in the dry air, humid air, and artificial acid rain environments. The implications of this research are that prior-corrosion damage has the ability to significantly increase crack growth rates in this material, and this could render unconservative the inspection intervals determined by damage tolerant analyses based on pristine, uncorroded structure in aircraft where this alloy and damage mechanism are present. The problem is further compounded in the event that prior-corrosion damage and corrosion fatigue act synergisticaliy to increase cracking rates.

Corrosion sealing of amalgam restorations in vitro.

PubMed

Mahler, David B; Pham, Bao V; Adey, Jerry D

2009-01-01

Amalgam restorations, when first placed, have been shown to exhibit a gap at the amalgam/tooth interface. With time in service, this gap fills with corrosion products that have the potential to "seal" the restoration. With the advent of high-copper, more corrosion-resistant amalgams, there has been concern that the time required to create this seal would be increased significantly when compared with low-copper traditional amalgams. The current study was designed to address this concern. Amalgam was condensed into a MACOR mold, simulating a Class I cavity form and then immersed into a 1.0% NaCl solution to simulate oral conditions. Using an air pressure test, the sealing was monitored over time. The results showed that the sealing was influenced by the size of the initial gap prior to immersion as well as corrosion resistance of the amalgam and that a corrosion-resistant amalgam with a small initial gap size can seal as quickly as a corrosion-prone amalgam. Therefore, it is not possible to predict sealing behavior based on corrosion resistance, alone. Furthermore, the presence of zinc in the amalgam alloy has been shown to result in the formation of zinc corrosion products in the amalgam/mold margin, which contributes to more rapid sealing. Analysis of a tooth extracted after 16 years of clinical service that had been restored with an amalgam-containing zinc was also shown to contain zinc corrosion products in the occlusal marginal area. This could explain the reported reduction in marginal fracture of clinically placed amalgam restorations made from zinc-containing alloys.

Nuclear waste viewed in a new light; a synchrotron study of uranium encapsulated in grout.

PubMed

Stitt, C A; Hart, M; Harker, N J; Hallam, K R; MacFarlane, J; Banos, A; Paraskevoulakos, C; Butcher, E; Padovani, C; Scott, T B

2015-03-21

How do you characterise the contents of a sealed nuclear waste package without breaking it open? This question is important when the contained corrosion products are potentially reactive with air and radioactive. Synchrotron X-rays have been used to perform micro-scale in-situ observation and characterisation of uranium encapsulated in grout; a simulation for a typical intermediate level waste storage packet. X-ray tomography and X-ray powder diffraction generated both qualitative and quantitative data from a grout-encapsulated uranium sample before, and after, deliberately constrained H2 corrosion. Tomographic reconstructions provided a means of assessing the extent, rates and character of the corrosion reactions by comparing the relative densities between the materials and the volume of reaction products. The oxidation of uranium in grout was found to follow the anoxic U+H2O oxidation regime, and the pore network within the grout was observed to influence the growth of uranium hydride sites across the metal surface. Powder diffraction analysis identified the corrosion products as UO2 and UH3, and permitted measurement of corrosion-induced strain. Together, X-ray tomography and diffraction provide means of accurately determining the types and extent of uranium corrosion occurring, thereby offering a future tool for isolating and studying the reactions occurring in real full-scale waste package systems. Copyright © 2014 Elsevier B.V. All rights reserved.

Corrosion of high-level radioactive waste iron-canisters in contact with bentonite.

PubMed

Kaufhold, Stephan; Hassel, Achim Walter; Sanders, Daniel; Dohrmann, Reiner

2015-03-21

Several countries favor the encapsulation of high-level radioactive waste (HLRW) in iron or steel canisters surrounded by highly compacted bentonite. In the present study the corrosion of iron in contact with different bentonites was investigated. The corrosion product was a 1:1 Fe layer silicate already described in literature (sometimes referred to as berthierine). Seven exposition test series (60 °C, 5 months) showed slightly less corrosion for the Na-bentonites compared to the Ca-bentonites. Two independent exposition tests with iron pellets and 38 different bentonites clearly proved the role of the layer charge density of the swelling clay minerals (smectites). Bentonites with high charged smectites are less corrosive than bentonites dominated by low charged ones. The type of counterion is additionally important because it determines the density of the gel and hence the solid/liquid ratio at the contact to the canister. The present study proves that the integrity of the multibarrier-system is seriously affected by the choice of the bentonite buffer encasing the metal canisters in most of the concepts. In some tests the formation of a patina was observed consisting of Fe-silicate. Up to now it is not clear why and how the patina formed. It, however, may be relevant as a corrosion inhibitor. Copyright © 2014 Elsevier B.V. All rights reserved.

Effect of repeated sterilization cycles on the physical properties of scaling instruments: a scanning electron microscopy study.

PubMed

Porto, Alessandra Nogueira; Borges, Álvaro Henrique; Semenoff-Segundo, Alex; Raslan, Suzane A; Pedro, Fábio Luis Miranda; Jorge, Antônio Olavo Cardoso; Bandeca, Matheus Coelho

2015-05-01

Repeated sterilizations cycles cause undesirable alterations in the material properties of the instruments, such as corrosion, alterations in the hardness of the metal and the loss of the cutting sharpness of the instrument. This research examined the effect of repeated dry heat sterilization and autoclaves cycles on carbon steel (CS) and stainless steel (SS) curettes during the scaling and root planning. A total of 77 Gracey curettes were used in this study. Of these, 35 were SS and 42 were CS curettes submitted in different process: Dry heat, autoclave, inhibition of corrosion and autoclave, scaling, root planning and dry heat, scaling, root planning, inhibition of corrosion and autoclave. The inhibition of corrosion used on the carbon curettes (prior to sterilization in the autoclave) was sodium nitrite at 2%. The curettes received 10 consecutive cycles of sterilization and after that the cutting edges were examined in the electronic microscope, at 60 and 100 magnification times. The images were evaluated by three independent examiners, who compared the photographs of each group with the control group. The surface corrosion products and a deterioration of the edges were observed and the results showed that the SS curettes suffered little alteration with sterilization, scaling, root planning whereas the CS curettes were visibly affected by sterilization in the autoclave, but when the inhibition of corrosion was used prior to the sterilization, the oxidation was considerably reduced.

An evaluation of carbon steel corrosion under stagnant seawater conditions.

PubMed

Lee, Jason S; Ray, Richard I; Lemieux, Edward J; Falster, Alexander U; Little, Brenda J

2004-01-01

Corrosion of 1020 carbon steel coupons in natural seawater over a 1-year period was more aggressive under strictly anaerobic stagnant conditions than under aerobic stagnant conditions as measured by weight loss and instantaneous corrosion rate (polarization resistance). Under oxygenated conditions, a two-tiered oxide layer of lepidocrocite/goethite formed. The inner layer was extremely tenacious and resistant to acid cleaning. Under anaerobic conditions, the corrosion product was initially a non-tenacious sulphur-rich corrosion product, mackinawite, with enmeshed bacteria. As more sulphide was produced the mackinawite was transformed to pyrrhotite. In both aerobic and anaerobic exposures, corrosion was more aggressive on horizontally oriented coupons compared to vertically oriented samples.

Preparing and Study the effects of Composite Coatings in Protection of Oil Pipes from the Risk of Corrosion that resulting from Associated water with Petroleum Products

NASA Astrophysics Data System (ADS)

– Sarraf, A. R. Al; Yaseen, M. A.

2018-05-01

In order to inhibit the metallic corrosion in the oil pipelines,the protection method with composite coating of unsaturated polyester and reinforced by Caolin at weight percentage (20%) was studied. Where, the work samples were classified into two groups according to internal composite coatings layers for all groups of these samples. The first group is nitrocellulose coating reinforced by nano and micro powder of Mgo, the second group is sodium silicate coating reinforced by nano powder of Mgo. The following weight percentages (0%, 1%, 3% and 5%) were adopted as reinforcement ratios for nano powders, as well as the weight percentages (0%, 3%, 5% and 7%) as reinforcement ratios for micro powders Tribology properties and Electrochemical Corrosion Resistance by Polarization method (Tafel) and Adhesion Strength were studied. The results showed an improvement in the corrosion resistance of protected steel by coatings compare with uncoated steel, as well as improvement in mechanical properties and adhesion strength of composite coatings.

Stress corrosion study of PH13-8Mo stainless steel using the Slow Strain Rate Technique

NASA Technical Reports Server (NTRS)

Torres, Pablo D.

1989-01-01

The need for a fast and reliable method to study stress corrosion in metals has caused increased interest in the Slow Strain Rate Technique (SSRT) during the last few decades. PH13-8MoH950 and H1000 round tensile specimens were studied by this method. Percent reduction-in-area, time-to-failure, elongation at fracture, and fracture energy were used to express the loss in ductility, which has been used to indicate susceptibility to stress corrosion cracking (SCC). Results from a 3.5 percent salt solution (corrosive medium) were compared to those in air (inert medium). A tendency to early failure was found when testing in the vicinity of 1.0 x 10(-6) mm/mm/sec in the 3.5 percent salt solution. PH13-8Mo H1000 was found to be less likely to suffer SCC than PH13-8Mo H950. This program showed that the SSRT is promising for the SCC characterization of metals and results can be obtained in much shorter times (18 hr for PH steels) than those required using conventional techniques.

A study of early corrosion behaviors of FeCrAl alloys in liquid lead-bismuth eutectic environments

NASA Astrophysics Data System (ADS)

Lim, Jun; Nam, Hyo On; Hwang, Il Soon; Kim, Ji Hyun

2010-12-01

Lead and lead-bismuth eutectic (LBE) alloy have been increasingly receiving attention as heavy liquid metal coolants (HLMC) for future nuclear energy systems. The compatibility of structural materials and components with lead-bismuth eutectic liquid at high temperature is one of key issues for the commercialization of lead fast reactors. In the present study, the corrosion behaviors of iron-based alumina-forming alloys (Kanthal-AF®, PM2000, MA956) were investigated by exposing to stagnant LBE environments at 500 °C and 550 °C for up to 500 h. After exposures, the thickness and chemistry of the oxide layer on the specimens were analyzed by scanning electron microscopy, scanning transmission electron microscopy and energy dispersive X-ray spectroscopy. As a result, the oxide characteristics and the corrosion resistance were compared. In this study, it was shown that the corrosion resistance of FeCrAl ODS steels (PM2000, MA956) are superior to that of FeCrAl ferritic steel (Kanthal-AF®) in higher temperature LBE.

2D Heterostructure coatings of hBN-MoS2 layers for corrosion resistance

NASA Astrophysics Data System (ADS)

Vandana, Sajith; Kochat, Vidya; Lee, Jonghoon; Varshney, Vikas; Yazdi, Sadegh; Shen, Jianfeng; Kosolwattana, Suppanat; Vinod, Soumya; Vajtai, Robert; Roy, Ajit K.; Sekhar Tiwary, Chandra; Ajayan, P. M.

2017-02-01

Heterostructures of atomically thin 2D materials could have improved physical, mechanical and chemical properties as compared to its individual components. Here we report, the effect of heterostructure coatings of hBN and MoS2 on the corrosion behavior as compared to coatings employing the individual 2D layer compositions. The poor corrosion resistance of MoS2 (widely used as wear resistant coating) can be improved by incorporating hBN sheets. Depending on the atomic stacking of the 2D sheets, we can further engineer the corrosion resistance properties of these coatings. A detailed spectroscopy and microscopy analysis has been used to characterize the different combinations of layered coatings. Detailed DFT based calculation reveals that the effect on the electrical properties due to atomic stacking is one of the major reasons for the improvement seen in corrosion resistance.

Deposition of nanostructured fluorine-doped hydroxyapatite-polycaprolactone duplex coating to enhance the mechanical properties and corrosion resistance of Mg alloy for biomedical applications.

PubMed

Bakhsheshi-Rad, H R; Hamzah, E; Kasiri-Asgarani, M; Jabbarzare, S; Iqbal, N; Abdul Kadir, M R

2016-03-01

The present study addressed the synthesis of a bi-layered nanostructured fluorine-doped hydroxyapatite (nFHA)/polycaprolactone (PCL) coating on Mg-2Zn-3Ce alloy via a combination of electrodeposition (ED) and dip-coating methods. The nFHA/PCL composite coating is composed of a thick (70-80 μm) and porous layer of PCL that uniformly covered the thin nFHA film (8-10 μm) with nanoneedle-like microstructure and crystallite size of around 70-90 nm. Electrochemical measurements showed that the nFHA/PCL composite coating presented a high corrosion resistance (R(p)=2.9×10(3) kΩ cm(2)) and provided sufficient protection for a Mg substrate against galvanic corrosion. The mechanical integrity of the nFHA/PCL composite coatings immersed in SBF for 10 days showed higher compressive strength (34% higher) compared with the uncoated samples, indicating that composite coatings can delay the loss of compressive strength of the Mg alloy. The nFHA/PCL coating indicted better bonding strength (6.9 MPa) compared to PCL coating (2.2 MPa). Immersion tests showed that nFHA/PCL composite-coated alloy experienced much milder corrosion attack and more nucleation sites for apatite compared with the PCL coated and uncoated samples. The bi-layered nFHA/PCL coating can be a good alternative method for the control of corrosion degradation of biodegradable Mg alloy for implant applications. Copyright © 2015 Elsevier B.V. All rights reserved.

Role of calcium-depositing bacteria Agrobacterium tumefaciens and its influence on corrosion of different engineering metals used in cooling water system.

PubMed

Narenkumar, Jayaraman; Sathishkumar, Kuppusamy; Selvi, Adikesavan; Gobinath, Rajagopalan; Murugan, Kadarkarai; Rajasekar, Aruliah

2017-12-01

The present investigation deals with the role of calcium-depositing bacterial community on corrosion of various engineering metals, namely, brass alloy (BS), copper (Cu), stainless steel (SS) and mild steel (MS). Based on the corrosion behavior, Agrobacterium tumefaciens EN13, an aerobic bacterium is identified as calcium-depositing bacteria on engineering metals. The results of the study are supported with biochemical characterization, 16S rRNA gene sequencing, calcium quantification, weight loss, electrochemical (impedance and polarization) and surface analysis (XRD and FTIR) studies. The calcium quantification study showed carbonate precipitation in abiotic system/biotic system as 50 and 700 ppm, respectively. FTIR results too confirmed the accumulation of calcium deposits from the environment on the metal surface by EN13. Electrochemical studies too supported the corrosion mechanism by showing a significant increase in the charge transfer resistance ( R ct ) of abiotic system (44, 33.6, 45, 29.6 Ω cm 2 ) than compared to biotic system (41, 10.1 29 and 25 Ω cm 2 ). Hence, the outcome of the present study confirmed the enhanced bioaccumulation behavior of calcium by the strain, EN13.

Corrosion of rock anchors in US coal mines

NASA Astrophysics Data System (ADS)

Bylapudi, Gopi

The mining industry is a major consumer of rock bolts in the United States. Due to the high humidity in the underground mining environment, the rock bolts corrode and loose their load bearing capacity which in turn reduces the life expectancy of the ground support and, thus, creates operational difficulties and number of safety concerns[1]. Research on rock anchor corrosion has not been adequately extensive in the past and the effects of several factors in the mine atmosphere and waters are not clearly understood. One of the probable reasons for this lack of research may be attributed to the time required for gathering meaningful data that makes the study of corrosion quite challenging. In this particular work underground water samples from different mines in the Illinois coal basin were collected and the major chemical content was analyzed and used for the laboratory testing. The corrosion performance of the different commercial rock anchors was investigated by techniques such as laboratory immersion tests in five different corrosion chambers, and potentiodynamic polarization tests in simulated ground waters based on the Illinois coal basin. The experiments were conducted with simulate underground mining conditions (corrosive). The tensile strengths were measured for the selected rock anchors taken every 3 months from the salt spray corrosion chambers maintained at different pH values and temperatures. The corrosion potential (Ecorr ), corrosion current (Icorr) and the corresponding corrosion rates (CR) of the selected commercial rock bolts: #5, #6, #6 epoxy coated and #7 forged head rebar steels, #6 and #7 threaded head rebar steels were measured at the solution pH values of 5 and 8 at room temperature. The open circuit potential (OCP) values of the different rock anchors were recorded in 3 selected underground coal mines (A, B & C) in the Illinois coal basin and the data compared with the laboratory electrochemical tests for analyzing the life of the rock anchors installed in the mines with respect to corrosion potential and corrosion current measured. The results of this research were statistically validated. This research will have direct consequence to the rock related safety. The results of this research indicate that certain corrosive conditions are commonly found in mines but uniform corrosion (around 0.01-0.03mm loss per year across the diameter) is generally not considered a serious issue. From this study, longer term research for longterm excavation support is recommended that could quantify the problem depending on the rock anchor used and specific strata conditions.

Improvement of corrosion resistance and antibacterial effect of NiTi orthopedic materials by chitosan and gold nanoparticles

NASA Astrophysics Data System (ADS)

Ahmed, Rasha A.; Fadl-allah, Sahar A.; El-Bagoury, Nader; El-Rab, Sanaa M. F. Gad

2014-02-01

Biocomposite consists of gold nanoparticles (AuNPs) and a natural polymer as Chitosan (CS) was electrodeposited over NiTi alloy to improve biocompatibility, biostability, surface corrosion resistance and antibacterial effect for orthopedic implantation. The forming process and surface morphology of this biocomposite coats over NiTi alloy were studied. The results showed that the nm-scale gold particles were embedded in the composite forming compact, thick and smooth coat. Elemental analysis revealed significant less Ni ion release from the coated NiTi alloy compared with the uncoated one by 20 fold. Furthermore, the electrochemical corrosion measurements indicated that AuNPs/CS composite coat was effective for improving corrosion resistance in different immersion times and at all pH values, which suggests that the coated NiTi alloys have potential for orthopedic applications. Additionally, the efficiencies of the biocomposite coats for inhibiting bacterial growth indicate high antibacterial effect.

Corrosion of 85-5-5-5 bronze in natural and synthetic acid rain

NASA Astrophysics Data System (ADS)

Morselli, L.; Bernardi, E.; Chiavari, C.; Brunoro, G.

In order to investigate the decay of bronzes exposed to acid wet depositions, a comparative study has been performed by following the corrosion behaviour of different sets of bronze specimens exposed either to natural rain or to a similar solution, without organic compounds, artificially reproduced in laboratory. The as cast G85 bronze specimens were exposed to aggressive solutions for different periods through a wet-dry technique. The pH trend of the solutions and the amount of metals transferred into the solutions were periodically monitored. OM, SEM, XRD, RAMAN analyses and ac electrochemical measurements were performed on the artificially weathered specimens. Preliminary results, showing the difference between the ageing in natural and synthetic rain, suggest the influence of the organic components on the corrosion process. In particular, the growth of a more uniform protective layer of corrosion products on the metal surface exposed to the natural rain could be attributed to these components.

Avoidance of stress corrosion susceptibility in high strength aluminum alloys by control of grain boundary and matrix microstructure

NASA Technical Reports Server (NTRS)

Adler, P.; Deiasi, R.

1974-01-01

The relation of microstructure to the mechanical strength and stress corrosion resistance of highest strength and overaged tempers of BAR and 7050 aluminum alloys was investigated. Comparison is made with previously studied 7075 aluminum alloy. Optical microscopy, transmission electron microscopy, and differential scanning calorimetry were used to characterize the grain morphology, matrix microstructure, and grain boundary microstructure of these tempers. Grain boundary interparticle spacing was significant to stress corrosion crack propagation for all three alloys; increasing interparticle spacing led to increased resistance to crack propagation. In addition, the fire grain size in Bar and 7050 appears to enhance crack propagation. The highest strength temper of 7050 has a comparatively high resistance to crack initiation. Overall stress corrosion behavior is dependent on environment pH, and evaluation over a range of pH is recommended.

Innovative Formulation Combining Al, Zr and Si Precursors to Obtain Anticorrosion Hybrid Sol-Gel Coating.

PubMed

Genet, Clément; Menu, Marie-Joëlle; Gavard, Olivier; Ansart, Florence; Gressier, Marie; Montpellaz, Robin

2018-05-10

The aim of our study is to improve the aluminium alloy corrosion resistance with Organic-Inorganic Hybrid (OIH) sol-gel coating. Coatings are obtained from unusual formulation with precursors mixing: glycidoxypropyltrimethoxysilane (GPTMS), zirconium (IV) propoxide (TPOZ) and aluminium tri-sec-butoxide (ASB). This formulation was characterized and compared with sol formulations GPTMS/TPOZ and GPTMS/ASB. In each formulation, a corrosion inhibitor, cerium (III) nitrate hexahydrate, is employed to improve the corrosion performance. Coatings obtained from sol based on GPTMS/TPOZ/ASB have good anti-corrosion performances with Natural Salt Spray (NSS) resistance of 500 h for a thickness lower than 4 µm. Contact angle measurement showed a coating hydrophobic behaviour. To understand these performances, nuclear magnetic resonance (NMR) analyses were performed, results make sol-gel coating condensation evident and are in very good agreement with previous results.

Microstructure, Mechanical Properties, and Corrosion Resistance of Thermomechanically Processed AlZn6Mg0.8Zr Alloy

PubMed Central

Kowalski, Aleksander; Ozgowicz, Wojciech; Jurczak, Wojciech; Grajcar, Adam; Boczkal, Sonia; Żelechowski, Janusz

2018-01-01

The paper presents results of the investigations on the effect of low-temperature thermomechanical treatment (LTTT) on the microstructure of AlZn6Mg0.8Zr alloy (7000 series) and its mechanical properties as well as electrochemical and stress corrosion resistance. For comparison of the LTTT effect, the alloy was subjected to conventional precipitation hardening. Comparative studies were conducted in the fields of metallographic examinations and static tensile tests. It was found that mechanical properties after the LTTT were better in comparison to after conventional heat treatment (CHT). The tested alloy after low-temperature thermomechanical treatment with increasing plastic deformation shows decreased electrochemical corrosion resistance during potentiodynamic tests. The alloy after low-temperature thermomechanical treatment with deformation degree in the range of 10 to 30% is characterized by a high resistance to stress corrosion specified by the level of PSCC indices. PMID:29642448

Microstructure Characterization and Corrosion Resistance Behavior of New Cobalt-Free Maraging Steel Produced Through ESR Techniques

NASA Astrophysics Data System (ADS)

Seikh, Asiful H.; Halfa, Hossam; Baig, Muneer; Khan, Sohail M. A.

2017-04-01

In this study, two different grades (M23 and M29) of cobalt-free low nickel maraging steel have been produced through electroslag remelting (ESR) process. The corrosion resistance of these ESR steels was investigated in 1 M H2SO4 solution using linear potentiodynamic polarization (LPP) and electrochemical impedance spectroscopy (EIS) techniques. The experiments were performed for different immersion time and solution temperature. To evaluate the corrosion resistance of the ESR steels, some significant characterization parameters from LPP and EIS curves were analyzed and compared with that of conventional C250 maraging steel. Irrespective of measurement techniques used, the results show that the corrosion resistance of the ESR steels was higher than the C250 steel. The microstructure of ESR steels was composed of uniform and well-distributed martensite accompanied with little amount of retained austenite in comparison with C250 steel.

Preliminary Investigation of the Corrosion Behavior of Proprietary Micro-alloyed Steels in Aerated and Deaerated Brine Solutions

NASA Astrophysics Data System (ADS)

Onyeji, Lawrence; Kale, Girish

2017-12-01

The corrosion performance of fairly new generation of micro-alloyed steels was compared in different concentrations of aerated and deaerated brines. Electrochemical polarization, weight loss and surface analyses techniques were employed. The results showed a threshold of corrosion rate at 3.5 wt.% NaCl in both aerated and deaerated solutions. The average corrosion current density for steel B, for example, increased from 1.3 µA cm-2 in 1 wt.% NaCl to 1.5 µA cm-2 in 3.5 wt.% NaCl, but decreased to 1.4 µA cm-2 in 10 wt.% deaerated NaCl solutions. The aerated solutions exhibited an average of over 80% increase in corrosion current density in the respective concentrations when compared with the deaerated solution. These results can be attributed to the effects of dissolved oxygen (DO) which has a maximum solubility in 3.5 wt.% NaCl. DO as a depolarizer and electron acceptor in cathodic reactions accelerates anodic metal dissolution. The difference in carbon content and microstructures occasioned by thermo-mechanical treatment contributed to the witnessed variation in corrosion performance of the steels. Specifically, the results of the various corrosion techniques corroborated each other and showed that the corrosion rate of the micro-alloyed steels can be ranked as CRSteel A < CRX65 < CRSteel B < CRSteel C.

Galvanic Corrosion of and Ion Release from Various Orthodontic Brackets and Wires in a Fluoride-containing Mouthwash.

PubMed

Tahmasbi, Soodeh; Ghorbani, Mohammad; Masudrad, Mahdis

2015-01-01

Background and aims. This study compared the galvanic corrosion of orthodontic wires and brackets from various manufacturers following exposure to a fluoride mouthwash. Materials and methods. This study was conducted on 24 lower central incisor 0.022" Roth brackets of four different commercially available brands (Dentaurum, American Orthodontics, ORJ, Shinye). These brackets along with stainless steel (SS) or nickel-titanium (NiTi) orthodontic wires (0.016", round) were immersed in Oral-B mouthwash containing 0.05% sodium fluoride for 28 days. The electric potential (EP) difference of each bracket-wire couple was measured with a Saturated Calomel Reference Electrode (Ag/AgCl saturated with KCl) via a voltmeter. The ions released in the electrolyte weremeasured with an atomic absorption spectrometer. All the specimens were assessed under a stereomicroscope and specimens with corrosion were analyzed with scanning electron microscopy (SEM). Data were analyzed using ANOVA. Results. The copper ions released from specimens with NiTi wire were greater than those of samples containing SS wire. ORJ brackets released more Cu ions than other samples. The Ni ions released from Shinye brackets were significantly more than those of other specimens (P < 0.05). Corrosion rate of brackets coupled with NiTi wires was higher than that of brackets coupled with SS wires. Light and electron microscopic observations showed greater corrosion of ORJ brackets. Conclusion. In fluoride mouthwash, Shinye and ORJ brackets exhibited greater corrosion than Dentaurum and American Orthodontics brackets. Stainless steel brackets used with NiTi wires showed greater corrosion and thus caution is recommended when using them.

Corrosion Behavior of Bi2Te3-Based Thermoelectric Materials Fabricated by Melting Method

NASA Astrophysics Data System (ADS)

Kohri, Hitoshi; Yagasaki, Takayoshi

2017-05-01

Bi2Te3-based compounds are used practically as thermoelectric cooling materials. Bi2Te3-Sb2Te3 or Bi2Te3-Bi2Se3 pseudobinary system compounds are usually applied as p- or n-type material, respectively. Atmospheric water may condense on the surface of thermoelectric materials constituting Peltier modules, depending on their operating environment. Very few studies on the corrosion resistance of Bi2Te3-based compounds have been reported in literature. Moreover, the detailed corrosion behavior of Bi2Te3-based compounds remains unclear. In this study, the corrosion behavior of cleavage planes of Bi2Te3-based compounds fabricated by a melting method has been investigated. Bi2Te3, Sb2Te3, and Bi2Se3 were prepared by the vertical Bridgman method, respectively. Their electrochemical properties evaluated at room temperature by cyclic voltammetry in a standard three-electrode cell with naturally aerated 0.6 mass% or 3.0 mass% NaCl solution as working electrolyte. The c-planes of Bi2Te3 and Sb2Te3 exhibited similar corrosion potential. The corrosion potential of c-plane of Bi2Se3 was more cathodic compared with that of the telluride. The passive current density of the Bi2Te3-based compounds was single or double digit lower than that of stainless steel. X-ray photoelectron spectroscopy results for the electrolyte after testing indicated the possibility that a corrosion product diffuses to the environment including NaCl for Sb2Te3 and Bi2Se3.

Galvanic Corrosion of and Ion Release from Various Orthodontic Brackets and Wires in a Fluoride-containing Mouthwash

PubMed Central

Tahmasbi, Soodeh; Ghorbani, Mohammad; Masudrad, Mahdis

2015-01-01

Background and aims. This study compared the galvanic corrosion of orthodontic wires and brackets from various manufacturers following exposure to a fluoride mouthwash. Materials and methods. This study was conducted on 24 lower central incisor 0.022" Roth brackets of four different commercially available brands (Dentaurum, American Orthodontics, ORJ, Shinye). These brackets along with stainless steel (SS) or nickel-titanium (NiTi) orthodontic wires (0.016", round) were immersed in Oral-B mouthwash containing 0.05% sodium fluoride for 28 days. The electric potential (EP) difference of each bracket-wire couple was measured with a Saturated Calomel Reference Electrode (Ag/AgCl saturated with KCl) via a voltmeter. The ions released in the electrolyte weremeasured with an atomic absorption spectrometer. All the specimens were assessed under a stereomicroscope and specimens with corrosion were analyzed with scanning electron microscopy (SEM). Data were analyzed using ANOVA. Results. The copper ions released from specimens with NiTi wire were greater than those of samples containing SS wire. ORJ brackets released more Cu ions than other samples. The Ni ions released from Shinye brackets were significantly more than those of other specimens (P < 0.05). Corrosion rate of brackets coupled with NiTi wires was higher than that of brackets coupled with SS wires. Light and electron microscopic observations showed greater corrosion of ORJ brackets. Conclusion. In fluoride mouthwash, Shinye and ORJ brackets exhibited greater corrosion than Dentaurum and American Orthodontics brackets. Stainless steel brackets used with NiTi wires showed greater corrosion and thus caution is recommended when using them. PMID:26697148

Corrosion behaviours of the dental magnetic keeper complexes made by different alloys and methods.

PubMed

Wu, Min-Ke; Song, Ning; Liu, Fei; Kou, Liang; Lu, Xiao-Wen; Wang, Min; Wang, Hang; Shen, Jie-Fei

2016-09-29

The keeper and cast dowel-coping, as a primary component for a magnetic attachment, is easily subjected to corrosion in a wet environment, such as the oral cavity, which contains electrolyte-rich saliva, complex microflora and chewing behaviour and so on. The objective of this in vitro study was to examine the corrosion resistance of a dowel and coping-keeper complex fabricated by finish keeper and three alloys (cobalt-chromium, CoCr; silver-palladium-gold, PdAu; gold-platinum, AuPt) using a laser-welding process and a casting technique. The surface morphology characteristics and microstructures of the samples were examined by means of metallographic microscope and scanning electron microscope (SEM). Energy-dispersive spectroscopy (EDS) with SEM provided elements analysis information for the test samples after 10% oxalic acid solution etching test. Tafel polarization curve recordings demonstrated parameter values indicating corrosion of the samples when subjected to electrochemical testing. This study has suggested that massive oxides are attached to the surface of the CoCr-keeper complex but not to the AuPt-keeper complex. Only the keeper area of cast CoCr-keeper complex displayed obvious intergranular corrosion and changes in the Fe and Co elements. Both cast and laser-welded AuPt-keeper complexes had the highest free corrosion potential, followed by the PdAu-keeper complex. We concluded that although the corrosion resistance of the CoCr-keeper complex was worst, the keeper surface passive film was actually preserved to its maximum extent. The laser-welded CoCr- and PdAu-keeper complexes possessed superior corrosion resistance as compared with their cast specimens, but no significant difference was found between the cast and laser-welded AuPt-keeper complexes. The Fe-poor and Cr-rich band, appearing on the edge of the keeper when casting, has been proven to be a corrosion-prone area.

Corrosion behaviours of the dental magnetic keeper complexes made by different alloys and methods

PubMed Central

Wu, Min-Ke; Song, Ning; Liu, Fei; Kou, Liang; Lu, Xiao-Wen; Wang, Min; Wang, Hang; Shen, Jie-Fei

2016-01-01

The keeper and cast dowel–coping, as a primary component for a magnetic attachment, is easily subjected to corrosion in a wet environment, such as the oral cavity, which contains electrolyte-rich saliva, complex microflora and chewing behaviour and so on. The objective of this in vitro study was to examine the corrosion resistance of a dowel and coping-keeper complex fabricated by finish keeper and three alloys (cobalt–chromium, CoCr; silver–palladium–gold, PdAu; gold–platinum, AuPt) using a laser-welding process and a casting technique. The surface morphology characteristics and microstructures of the samples were examined by means of metallographic microscope and scanning electron microscope (SEM). Energy-dispersive spectroscopy (EDS) with SEM provided elements analysis information for the test samples after 10% oxalic acid solution etching test. Tafel polarization curve recordings demonstrated parameter values indicating corrosion of the samples when subjected to electrochemical testing. This study has suggested that massive oxides are attached to the surface of the CoCr–keeper complex but not to the AuPt–keeper complex. Only the keeper area of cast CoCr–keeper complex displayed obvious intergranular corrosion and changes in the Fe and Co elements. Both cast and laser-welded AuPt–keeper complexes had the highest free corrosion potential, followed by the PdAu–keeper complex. We concluded that although the corrosion resistance of the CoCr–keeper complex was worst, the keeper surface passive film was actually preserved to its maximum extent. The laser-welded CoCr– and PdAu–keeper complexes possessed superior corrosion resistance as compared with their cast specimens, but no significant difference was found between the cast and laser-welded AuPt–keeper complexes. The Fe-poor and Cr-rich band, appearing on the edge of the keeper when casting, has been proven to be a corrosion-prone area. PMID:27388806

Low toxic corrosion inhibitors for aluminum in fresh water

NASA Technical Reports Server (NTRS)

Humphries, T. S.

1978-01-01

Combinations of chemical compounds that reportedly reduce the corrosion of aluminum in fresh water were evaluated. These included combinations of borates, nitrates, nitrites, phosphates, silicates, and mercaptobenzothiazole. Eight of fifty inhibitor combinations evaluated gave excellent corrosion protection and compared favorably with sodium chromate, which has generally been considered standard for many years.

Effect of Phosphate-Buffered Solution Corrosion on the Ratcheting Fatigue Behavior of a Duplex Mg-Li-Al Alloy

NASA Astrophysics Data System (ADS)

Yuan, Xin; Yu, Dunji; Gao, Li-Lan; Gao, Hong

2016-05-01

This work reports the uniaxial ratcheting and fatigue behavior of a duplex Mg-Li-Al alloy under the influence of phosphate-buffered solution corrosion. Microstructural observations reveal pitting and filament corrosion defects, which impair the load-bearing capacity of the alloy and cause stress concentration, thus leading to an accelerated accumulation of ratcheting strain and shortened fatigue life under the same nominal loading conditions. Comparing Smith model, Smith-Watson-Topper model, and Paul-Sivaprasad-Dhar model, a ratcheting fatigue life prediction model based on the Broberg damage rule and the Paul-Sivaprasad-Dhar model was proposed, and the model yielded a superior prediction for the studied magnesium alloy.

Characterization of Encapsulated Corrosion Inhibitors for Environmentally Friendly Smart Coatings

NASA Technical Reports Server (NTRS)

Pearman, Benjamin Pieter; Li, Wenyan; Buhrow, Jerry; Zhang, Xuejun; Surma, Jan; Fitzpatrick, Lilly; Montgomery, Eliza; Calle, Luz Marina

2014-01-01

Research efforts are under way to replace current corrosion inhibitors with more environmentally friendly alternatives. However, problems with corrosion inhibition efficiency, coating compatibility and solubility have hindered the use of many of these materials as simple pigment additives.This paper will present technical details on how the Corrosion Technology Lab at NASAs Kennedy Space Center (KSC) has addressed these issues by encapsulating environmentally friendly inhibitors into organic and inorganic microparticles and microcapsules. The synthetic process for polymer particles was characterized and post-synthesis analysis was performed to determine the interactions between the inhibitors and the encapsulation material. The pH-controlled release of inhibitors from various particle formulations in aqueous base was monitored and compared to both electrochemical and salt immersion accelerated corrosion experiment. Furthermore, synergistic corrosion inhibition effects observed during the corrosion testing of several inhibitor combinations will be presented.

Improving the corrosion properties of magnesium AZ31 alloy GTA weld metal using microarc oxidation process

NASA Astrophysics Data System (ADS)

Siva Prasad, M.; Ashfaq, M.; Kishore Babu, N.; Sreekanth, A.; Sivaprasad, K.; Muthupandi, V.

2017-05-01

In this work, the morphology, phase composition, and corrosion properties of microarc oxidized (MAO) gas tungsten arc (GTA) weldments of AZ31 alloy were investigated. Autogenous gas tungsten arc welds were made as full penetration bead-on-plate welding under the alternating-current mode. A uniform oxide layer was developed on the surface of the specimens with MAO treatment in silicate-based alkaline electrolytes for different oxidation times. The corrosion behavior of the samples was evaluated by potentiodynamic polarization and electrochemical impedance spectroscopy. The oxide film improved the corrosion resistance substantially compared to the uncoated specimens. The sample coated for 10 min exhibited better corrosion properties. The corrosion resistance of the coatings was concluded to strongly depend on the morphology, whereas the phase composition and thickness were concluded to only slightly affect the corrosion resistance.

Distributed fiber optic strain sensing to detect artificial pitting corrosion in stirrups

NASA Astrophysics Data System (ADS)

Zhang, Jiachen; Kancharla, Vinutha; Hoult, Neil A.

2017-04-01

Pitting corrosion is difficult to identify through visual inspection and can lead to sudden structural failures. As such, an experimental study was undertaken to investigate whether distributed fiber optic strain sensors are capable of detecting the locations and strain changes associated with stirrup corrosion in reinforced concrete beams. In comparison to conventional strain gauges, this type of sensor can measure the strain response along the entire length of the fiber optic cable. Two specimens were tested: a control and a deteriorated beam. The deteriorated beam was artificially corroded by reducing the cross sectional area of the closed stirrups by 50% on both sides of the stirrup at the mid-height. This level of area reduction represents severe pitting corrosion. The beams were instrumented with nylon coated fiber optic sensors to measure the distributed strains, and then tested to failure under three point bending. The load deflection behavior of the two specimens was compared to assess the impact of the artificial pitting corrosion on the capacity. Digital Image Correlation was used to locate the extent and trajectory of the crack paths. It was found that the pitting corrosion had no impact on capacity or stiffness. Also, in this investigation the fiber optic sensing system failed to detect the location and strain changes due to pitting corrosion since the shear cracks did not intersect with the pitting location.

Galvanic Corrosion of Lead by Iron (Oxyhydr)Oxides: Potential Impacts on Drinking Water Quality.

PubMed

Trueman, Benjamin F; Sweet, Gregory A; Harding, Matthew D; Estabrook, Hayden; Bishop, D Paul; Gagnon, Graham A

2017-06-20

Lead exposure via drinking water remains a significant public health risk; this study explored the potential effects of upstream iron corrosion on lead mobility in water distribution systems. Specifically, galvanic corrosion of lead by iron (oxyhydr)oxides was investigated. Coupling an iron mineral cathode with metallic lead in a galvanic cell increased lead release by 531 μg L -1 on average-a 9-fold increase over uniform corrosion in the absence of iron. Cathodes were composed of spark plasma sintered Fe 3 O 4 or α-Fe 2 O 3 or field-extracted Fe 3 O 4 and α-FeOOH. Orthophosphate immobilized oxidized lead as insoluble hydroxypyromorphite, while humic acid enhanced lead mobility. Addition of a humic isolate increased lead release due to uniform corrosion by 81 μg L -1 and-upon coupling lead to a mineral cathode-release due to galvanic corrosion by 990 μg L -1 . Elevated lead in the presence of humic acid appeared to be driven by complexation, with 208 Pb and UV 254 size-exclusion chromatograms exhibiting strong correlation under these conditions (R 2 average = 0.87). A significant iron corrosion effect was consistent with field data: lead levels after lead service line replacement were greater by factors of 2.3-4.7 at sites supplied by unlined cast iron distribution mains compared with the alternative, lined ductile iron.

Detection of active corrosion in reinforced and prestressed concrete: overview of NIST TIP project

NASA Astrophysics Data System (ADS)

Gonzalez-Nunez, M. A.; Nanni, A.; Matta, F.; Ziehl, P.

2011-04-01

The US transportation infrastructure has been receiving intensive public and private attention in recent years. The Federal Highway Administration estimates that 42 percent of the nearly 600,000 bridges in the Unites States are in need of structural or functional rehabilitation1. Corrosion of reinforcement steel is the main durability issue for reinforced and prestressed concrete structures, especially in coastal areas and in regions where de-icing salts are regularly used. Acoustic Emission (AE) has proved to be a promising method for detecting corrosion in steel reinforced and prestressed concrete members. This type of non-destructive test method primarily measures the magnitude of energy released within a material when physically strained. The expansive ferrous byproducts resulting from corrosion induce pressure at the steel-concrete interface, producing longitudinal and radial microcracks that can be detected by AE sensors. In the experimental study presented herein, concrete block specimens with embedded steel reinforcing bars and strands were tested under accelerated corrosion to relate the AE activity with the onset and propagation stages of corrosion. AE data along with half cell potential measurements and galvanic current were recorded to examine the deterioration process. Finally, the steel strands and bars were removed from the specimens, cleaned and weighed. The results were compared vis-à-vis Faraday's law to correlate AE measurements with degree of corrosion in each block.

Effect of the Type of Surface Treatment and Cement on the Chloride Induced Corrosion of Galvanized Reinforcements

NASA Astrophysics Data System (ADS)

Tittarelli, Francesca; Mobili, Alessandra; Vicerè, Anna Maria; Roventi, Gabriella; Bellezze, Tiziano

2017-10-01

The effect of a new passivation treatment, obtained by immersion of the galvanized reinforcements in a trivalent chromium salts based solution, on the chlorides induced corrosion has been investigated. To investigate also the effect of cement alkalinity on corrosion behaviour of reinforcements, concretes manufactured with three different European cements were compared. The obtained results show that the alternative treatment based on hexavalent chromium-free baths forms effective protection layers on the galvanized rebar surfaces. The higher corrosion rates of zinc coating in concrete manufactured with Portland cement compared to those recorded for bars in concrete manufactured with pozzolanic cement depends strongly on the higher chloride content at the steel concrete interface.

Thermal spray coating for corrosion under insulation (CUI) prevention

NASA Astrophysics Data System (ADS)

Fuad, Mohd Fazril Irfan Ahmad; Razak, Khalil Abdul; Alias, Nur Hashimah; Othman, Nur Hidayati; Lah, Nik Khairul Irfan Nik Ab

2017-12-01

Corrosion under insulation (CUI) is one of the predominant issues affecting process of Oil and Gas and Petrochemical industries. CUI refers to external corrosion, but it is difficult to be detected as the insulation cover masks the corrosion problem. One of the options to prevent CUI is by utilizing the protective coating systems. Thermal spray coating (TSC) is an advanced coating system and it shows promising performance in harsh environment, which could be used to prevent CUI. However, the application of TSC is not attractive due to the high initial cost. This work evaluates the potential of TSC based on corrosion performance using linear polarization resistance (LPR) method and salt spray test (SST). Prior to the evaluation, the mechanical performance of TSC was first investigated using adhesion test and bend test. Microstructure characterization of the coating was investigated using Scanning Electron Microscope (SEM). The LPR test results showed that low corrosion rate of 0.05 mm/years was obtained for TSC in compared to the bare steel especially at high temperature of 80 °C, where usually normal coating would fail. For the salt spray test, there was no sign of corrosion products especially at the center (fully coated region) was observed. From SEM images, no corrosion defects were observed after 336 hours of continuous exposure to salt fog test. This indicates that TSC protected the steel satisfactorily by acting as a barrier from a corrosive environment. In conclusion, TSC can be a possible solution to minimize the CUI in a long term. Further research should be done on corrosion performance and life cycle cost by comparing TSC with other conventional coating technology.

Structural modifications and corrosion behavior of martensitic stainless steel nitrided by plasma immersion ion implantation

NASA Astrophysics Data System (ADS)

Figueroa, C. A.; Alvarez, F.; Zhang, Z.; Collins, G. A.; Short, K. T.

2005-07-01

In this work we report a study of the structural modifications and corrosion behavior of martensitic stainless steels (MSS) nitrided by plasma immersion ion implantation (PI3). The samples were characterized by x-ray diffraction, scanning electron microscopy, energy dispersive x-ray spectroscopy, photoemission electron spectroscopy, and potentiodynamic electrochemical measurements. Depending on the PI3 treatment temperature, three different material property trends are observed. At lower implantation temperatures (e.g., 360 °C), the material corrosion resistance is improved and a compact phase of ɛ-(Fe,Cr)3N, without changes in the crystal morphology, is obtained. At intermediate temperatures (e.g., 430 °C), CrN precipitates form principally at grain boundaries, leading to a degradation in the corrosion resistance compared to the original MSS material. At higher temperatures (e.g., 500 °C), the relatively great mobility of the nitrogen and chromium in the matrix induced random precipitates of CrN, transforming the original martensitic phase into α-Fe (ferrite), and causing a further degradation in the corrosion resistance.

Durability of recycled aggregate concrete using pozzolanic materials.

PubMed

Ann, K Y; Moon, H Y; Kim, Y B; Ryou, J

2008-01-01

In this study, pulverized fuel ash (PFA) and ground granulated blast furnace slag (GGBS) were used to compensate for the loss of strength and durability of concrete containing recycled aggregate. As a result, 30% PFA and 65% GGBS concretes increased the compressive strength to the level of control specimens cast with natural granite gravel, but the tensile strength was still lowered at 28 days. Replacement with PFA and GGBS was effective in raising the resistance to chloride ion penetrability into the concrete body, measured by a rapid chloride ion penetration test based on ASTM C 1202-91. It was found that the corrosion rate of 30% PFA and 65% GGBS concretes was kept at a lower level after corrosion initiation, compared to the control specimens, presumably due to the restriction of oxygen and water access. However, it was less effective in increasing the chloride threshold level for steel corrosion. Hence, it is expected that the corrosion time for 30% PFA and 65% GGBS concrete containing recycled aggregate mostly equates to the corrosion-free life of control specimens.

Improving the Corrosion Resistance of Biodegradable Magnesium Alloys by Diffusion Coating Process

NASA Astrophysics Data System (ADS)

Levy, Galit Katarivas; Aghion, Eli

Magnesium alloys suffer from accelerated corrosion in physiological environment and hence their use as a structural material for biodegradable implants is limited. The present study focuses on a diffusion coating treatment that amplifies the beneficial effect of Neodymium on the corrosion resistance of magnesium alloys. The diffusion coating layer was obtained by applying 1 µm Nd coating on EW10X04 magnesium alloy using Electron-gun evaporator and PVD process. The coated alloy was heat treated at 350°C for 3 hours in a protective atmosphere of N2+0.2%SF6. The micro structure characteristics were evaluated by SEM, XRD, and XPS; the corrosion resistance was examined by potentiodynamic polarization and EIS analysis. The corrosion resistance of the diffusion coated alloy was significantly improved compared to the uncoated material. This was related to: (i) formation of Nd2O3 in the outer scale, (ii) integration of Nd in the MgO oxide layer, and (iii) formation of secondary phase Mg41Nd5 along the grain boundaries of α-Mg.

Investigation on the influence of nitrogen in process atmospheres on the corrosion behavior of brazed stainless steel joints

NASA Astrophysics Data System (ADS)

Fedorov, V.; Uhlig, T.; Wagner, G.; Langohr, A.; Holländer, U.

2018-06-01

Brazing of stainless steels is commonly carried out using nickel-based brazing fillers, which provide a high corrosion and oxidation resistance of the resulting joints. These brazed stainless steel joints are mostly used for manufacturing of heat exchangers for energy and air conditioning technologies. The joints of the study were produced at temperatures of 1000 °C, 1125 °C and 1150 °C in vacuum furnaces or continuous furnaces. In both cases, the parts interact with process gases like nitrogen within the brazing process, especially during cooling. The amount of nitrogen in the braze metal as well as in the base material was determined by the carrier gas hot extraction technique. The occurring diffusion of nitrogen into the braze metal and the base material causes a shift in the corrosion potentials. In this work, the influence of the nitrogen enrichment on the corrosion behavior was investigated using a capillary microcell. The corrosion measurements were carried out on the braze metal and the base material. The results of samples, brazed with and without the influence of nitrogen, were compared.

Corrosion resistance of a new AL 6013-20 SiC(P) in salt spray chamber

NASA Astrophysics Data System (ADS)

Ahmad, Zaki; Aleem, B. J. Abdul

2000-06-01

Aluminum 6013 alloy (0.82Si, 0.95Mg, and 0.35Mn) is finding increasing usage in new aircraft designs, automotives, and structural applications due to its good stretch forming character in T4 temper (solution heat treated and naturally aged to a substantially stable conditions) compared to alloy 2024 (4.4Cu, 0.6Mn, 1.5Mg, and balance Al) and Al6061 (Si0.51 to 0.71, Fe0.35, Cu0.15, Mn0.85, Mg0.15, 0.25Cr, 0.15Zn, and balanced Al). The newly developed A1 6013 reinforced with 20 vol.% SiC(P) has a higher strength than its unreinforced counterpart. Whereas the corrosion behavior of A1 6013 has been reported in literature, there is no previous data on A1 6013 reinforced with SiC(P). A knowledge of the corrosion behavior of this alloy is crucial to its applications in aerospace, structural, and automotive industry. The first results of corrosion study of this alloy in 3.5 wt.% Na Cl in a salt spray chamber are presented. Three tempers F (as fabricated), O (annealed), and T4 (age hardened and stabilized at room temperature) of the alloy A1 6013-30 SiC(P) were exposed to environmental chamber in accordance with ASTM recommended practice. The corrosion rate of the alloy showed a decrease with increased exposure period and after 800 h of exposure no appreciable change in the rate of corrosion was observed. The lowest rate of corrosion (4.83 mdd) was shown by temper T4 followed by tempers F and O after 1200 h of exposure in the increasing order of corrosion rate. Fluctuations in the corrosion rate with time are related to the kinetics of growth and dissolution of Al(OH)3 film, which was detected by fourier transformation infrared (FTIR) spectroscopy (FTIS). The film was composed of an inner compact layer and outer bulk layer dependent on the refreshment rate from the bulk solution. Micrograph examination by scanning electron microscopy (SEM) showed the presence of pits covered by aluminum hydroxide gel, which isolates the pit from the bulk solution. The acidic conditions of pits also cause intergranular attack. Pitting was observed to be less pronounced in temper T4 compared to F and O tempers, the former also showing the highest resistance to corrosion. The data generated predict promising application potential of this alloy in environment where resistance to corrosion is also a major consideration.

Research on a new type of fiber Bragg grating based corrosion sensor

NASA Astrophysics Data System (ADS)

Li, Peng; Song, Shide; Wang, Xiaona; Zhou, Weijie; Zhang, Zuocai

2015-08-01

Investigations of the corrosion of rebars in concrete structures are widely studied because of the serious damage to concrete caused by rebar corrosion. The rebar corrosion products in reinforced concrete take up 2~6 times the volume of the rebar. Based on this principle, a new type of fiber Bragg grating (FBG) corrosion sensor is proposed in this paper, which consists of two sensors, an FBG corrosion measurement sensor to measure the expansion strain caused by rebar corrosion, and a temperature compensation sensor to eliminate the cross-sensitivity of FBG corrosion sensor. The corrosion rate is derived by the wavelength shift of FBG corrosion sensor, so rebar corrosion can be monitored and assessed by the FBG wavelength shift. A customized rebar with epoxy fixing groove is designed to install a corrosion sensor on its surface and an embedded temperature compensation sensor. The corrosion sensor is embedded in cement mortar and subsequently casted in concrete. The performance of the corrosion sensor is studied in an accelerated electrochemical corrosion test. Experimental results show that the new type of corrosion sensor has advantage of relatively large measurement range of corrosion rate. The corrosion sensor is suitable to monitor slightly and moderately corroded rebars.

Two new supramolecular metal diphosphonates: Synthesis, characterization, crystal structure and inhibiting effects on metallic corrosion

DOE Office of Scientific and Technical Information (OSTI.GOV)

Gholivand, Khodayar, E-mail: gholi_kh@modares.ac.ir; Yaghoubi, Rouhollah; Farrokhi, Alireza

Two new divalent metal(II) aminodiphosphonates with layered structure, namely, Cu(H{sub 3}L{sup 1}){sub 2}·2H{sub 2}O (1), [H4L{sup 1}=methyl-N(CH{sub 2}PO{sub 3}H{sub 2}){sub 2}] and Cd{sub 2}(H{sub 2}L{sup 2}){sub 4}(2), [H{sub 4}L{sup 2}=n-propyl-N(CH{sub 2}PO{sub 3}H{sub 2}){sub 2}] were synthesized and characterized. The Cu(II) ions in complex 1 are octahedrally coordinated by four oxygen atoms from two chelating ligands and two phosphonate oxygen atoms from two neighboring Cu(H{sub 3}L{sup 1}){sub 2} units. The Cu(H{sub 3}L{sup 1}){sub 2} units are interconnected by bridging phosphonate groups, forming a 2-D metal phosphonate layer. The structure of complex 2 contains two unique Cd(II) ions octahedrally-coordinated by six phosphonatemore » oxygen atoms from four H{sub 2}L{sup 2} diphosphonate anions. Corrosion inhibition performances of 1 and 2 were also compared with each other in order to study the effect of combinations of externally added Cd/H{sub 4}L{sup 2} and Cu/H{sub 4}L{sup 1} (1:1 ratio) on corrosion rates of carbon steel. It was found that at pH 3.0, Cd/H{sub 4}L{sup 2} or Cu/H{sub 4}L{sup 1} combinations do not have noticeable corrosion inhibition efficiency for carbon steel. In contrast, at pH 7.0, higher corrosion inhibition efficiency was achieved for Cd/H{sub 4}L{sup 2}. Physical characterizations such as scanning electron microscopy (SEM), Energy-dispersive X-ray spectroscopy (EDS) and Fourier transform infrared spectroscopy (FTIR) were applied to study the corrosion specimens and film material. - Graphical abstract: Two new metal phosphonates have been synthesized and characterized by single-crystal X-ray diffraction and thermogravimetric analysis. corrosion inhibition performances 1 and 2 are also compared.« less

Precipitation Phenomena: Deformation and Aging. Proceedings of an International Conference Held in Conjunction with the 1988 World Materials Congress, Chicago, Illinois, USA, 24-30 September 1988

DTIC Science & Technology

1988-01-01

corrosion and stress analytical methods. corrosion cracking (SCC) in certain aqueous 3 EXPERIMENTAL PROCEDURE treatments were performed using variable time...properly oriented with the applied uniaxial approach a comparable EPR-DOS in the control stress are influenced. Deformation may specimens. EPR-DOS values...corrosion and stress corrosion. Atteridge, Sensitization Development Deformation above 20% prior strain, however, in Austenitic Stainless Steel: II. induces

Carbon corrosion in PEM fuel cells during drive cycle operation

DOE PAGES

Borup, Rodney L.; Papadias, D. D.; Mukundan, Rangachary; ...

2015-09-14

One of the major contributors to degradation involves the electrocatalyst, including the corrosion of the carbons used as catalyst supports, which leads to changes in the catalyst layer structure. We have measured and quantified carbon corrosion during drive cycle operation and as a variation of the upper and lower potential limits used during drive cycle operation. The amount of carbon corrosion is exacerbated by the voltage cycling inherent in the drive cycle compared with constant potential operation. The potential gap between upper and lower potentials appears to be more important than the absolute operating potentials in the normal operating potentialmore » regime (0.40V to 0.95V) as changes in the measured carbon corrosion are similar when the upper potential was lower compared to raising the lower potential. Catalyst layer thinning was observed during the simulated drive cycle operation which had an associated decrease in catalyst layer porosity. This catalyst layer thinning is not due solely to carbon corrosion, although carbon corrosion likely plays a role; much of this thinning must be from compaction of the material in the catalyst layer. As a result, the decrease in catalyst layer porosity leads to additional performance losses due to mass transport losses.« less

'Long-Cell Action' Corrosion: A Basic Mechanism Hidden Behind Components Degradation Issues in Nuclear Power Plants

DOE Office of Scientific and Technical Information (OSTI.GOV)

Genn Saji

2006-07-01

In spite of industries' effort over the last 40 years, corrosion-related issues continue to be one of the largest unresolved problems for nuclear power plants worldwide. There are several types of strange corrosion phenomena from the point of view of our current understanding of corrosion science established in other fields. Some of these are IGSCC, PWSCC, AOA, and FAC (Erosion-Corrosion). Through studying and coping with diverse corrosion phenomena, the author believes that they share a common basis with respect to the assumed corrosion mechanism (e.g., 'local cell action' hypothesis). In general, local cell action is rarely severe since it producesmore » a fairly uniform corrosion. The 'long cell action' that transports electrons through structures far beyond the region of local cell corrosion activities has been identified as a basic mechanism in soil corrosion. If this mechanism is assumed in nuclear power plants, the structure becomes anodic in the area where the potential is less positive and cathodic where this potential is more positive. Metallic ions generated at anodic corrosion sites are transported to remote cathodic sites through the circulation of water and deposits as corrosion products. The SCC, FAC (E-C) and PWSCC occur in the anodic sites as the structure itself acts as a short-circuiting conductor between the two sites, the action is similar to a galvanic cell but in a very large scale. This situation is the same as a battery that has been short-circuited at the terminals. No apparent external potential difference exists between the two electrodes, but an electrochemical reaction is still taking place inside the battery cell with a large internal short current. In this example what is important is the potential difference between the local coolant and the surface of the structural material. Long cell action corrosion is likely enhancing the local cell action's anodic corrosion activities, such as SCC, FAC/E-C, and PWSCC. It tends to be more hazardous because of its localized nature compared with the local cell action corrosion. There exist various mechanisms (electrochemical cell configurations) that induce such potential differences, including: ionic concentration, aeration, temperature, flow velocity, radiation and corrosion potentials. In this paper, the author will discuss these potential differences and their relevance to the un-resolved corrosion issues in nuclear power plants. Due to the importance of this potential mechanism the author is calling for further verification experiments as a joint international project. (author)« less

Corrosion of 316 stainless steel in high temperature molten Li2BeF4 (FLiBe) salt

NASA Astrophysics Data System (ADS)

Zheng, Guiqiu; Kelleher, Brian; Cao, Guoping; Anderson, Mark; Allen, Todd; Sridharan, Kumar

2015-06-01

In support of structural material development for the fluoride-salt-cooled high-temperature reactor (FHR), corrosion tests of 316 stainless steel were performed in the potential primary coolant, molten Li2BeF4 (FLiBe) at 700 °C for an exposure duration up to 3000 h. Tests were performed in both 316 stainless steel and graphite capsules. Corrosion in both capsule materials occurred by the dissolution of chromium from the stainless steel into the salt which led to the depletion of chromium predominantly along the grain boundaries of the test samples. The samples tested in graphite capsules showed a factor of two greater depth of corrosion attack as measured in terms of chromium depletion, compared to those tested in 316 stainless steel capsules. The samples tested in graphite capsules showed the formation of Cr7C3 particulate phases throughout the depth of the corrosion layer. Samples tested in both types of capsule materials showed the formation of MoSi2 phase due to increased activity of Mo and Si as a result of Cr depletion, and furthermore corrosion promoted the formation of a α-ferrite phase in the near-surface regions of the 316 stainless steel. Based on the corrosion tests, the corrosion attack depth in FLiBe salt was predicted as 17.1 μm/year and 31.2 μm/year for 316 stainless steel tested in 316 stainless steel and in graphite capsules respectively. It is in an acceptable range compared to the Hastelloy-N corrosion in the Molten Salt Reactor Experiment (MSRE) fuel salt.

Progress in the understanding of the long-term corrosion behaviour of copper canisters

NASA Astrophysics Data System (ADS)

King, Fraser; Lilja, Christina; Vähänen, Marjut

2013-07-01

Copper has been proposed as a canister material for the disposal of spent nuclear fuel in a deep geologic repository in a number of countries worldwide. Since it was first proposed for this purpose in 1978, a significant number of studies have been performed to assess the corrosion performance of copper under repository conditions. These studies are critically reviewed and the suitability of copper as a canister material for nuclear waste is re-assessed. Over the past 30-35 years there has been considerable progress in our understanding of the expected corrosion behaviour of copper canisters. Crucial to this progress has been the improvement in the understanding of the nature of the repository environment and how it will evolve over time. With this improved understanding, it has been possible to predict the evolution of the corrosion behaviour from the initial period of warm, aerobic conditions in the repository to the long-term phase of cool, anoxic conditions dominated by the presence of sulphide. An historical review of the treatment of the corrosion behaviour of copper canisters is presented, from the initial corrosion assessment in 1978, through a major review of the corrosion behaviour in 2001, through to the current level of understanding based on the results of on-going studies. Compared with the initial corrosion assessment, there has been considerable progress in the treatment of localised corrosion, stress corrosion cracking, and microbiologically influenced corrosion of the canisters. Progress in the mechanistic modelling of the evolution of the corrosion behaviour of the canister is also reviewed, as is the continuing debate about the thermodynamic stability of copper in pure water. The overall conclusion of this critical review is that copper is a suitable material for the disposal of spent nuclear fuel and offers the prospect of containment of the waste for an extended period of time. The corrosion behaviour is influenced by the presence of the highly compacted bentonite buffer which (i) inhibits the transport of reactants to, and of corrosion products away from, the canister surface, (ii) limits the amount of atmospheric O2 initially trapped in the repository, and (iii) suppresses microbial activity close to the canister surface [5,6,9]. The environment will evolve with time as the initially trapped atmospheric O2 is consumed and as the canister cools. This evolution can be described as a transition from an early period of warm, oxidising conditions to an indefinite period of cool, anoxic conditions. In turn, this environmental evolution will impact the corrosion behaviour of the canister. Localised corrosion and stress corrosion cracking (SCC) will only be possible for a limited period of time initially when there is sufficient oxidant available to support these forms of corrosion. This aerobic phase is only expected to last a few tens or hundreds of years [10,11]. For the vast majority of the service life of the canister, the redox conditions will be determined by the absence of O2 and the presence of sulphide. Although obvious, it is important to remember that the corrosion behaviour is determined by the environmental conditions at the canister surface. Because of the presence of the compacted bentonite, the environment at the canister surface will be quite different from that in the ground water in the rock. In particular, the interfacial concentration of HS- will be small as the rate of corrosion in the presence of sulphide is transport limited [1,2,12]. The low interfacial [HS-] has important implications for various sulphur-related corrosion mechanisms. The relatively high salinity of the ground water (and, hence, of the bentonite pore water) promotes the general dissolution of copper and inhibits localised corrosion and SCC [5,6].

Imparting passivity to vapor deposited magnesium alloys

NASA Astrophysics Data System (ADS)

Wolfe, Ryan C.

Magnesium has the lowest density of all structural metals. Utilization of low density materials is advantageous from a design standpoint, because lower weight translates into improved performance of engineered products (i.e., notebook computers are more portable, vehicles achieve better gas mileage, and aircraft can carry more payload). Despite their low density and high strength to weight ratio, however, the widespread implementation of magnesium alloys is currently hindered by their relatively poor corrosion resistance. The objective of this research dissertation is to develop a scientific basis for the creation of a corrosion resistant magnesium alloy. The corrosion resistance of magnesium alloys is affected by several interrelated factors. Among these are alloying, microstructure, impurities, galvanic corrosion effects, and service conditions, among others. Alloying and modification of the microstructure are primary approaches to controlling corrosion. Furthermore, nonequilibrium alloying of magnesium via physical vapor deposition allows for the formation of single-phase magnesium alloys with supersaturated concentrations of passivity-enhancing elements. The microstructure and surface morphology is also modifiable during physical vapor deposition through the variation of evaporation power, pressure, temperature, ion bombardment, and the source-to-substrate distance. Aluminum, titanium, yttrium, and zirconium were initially chosen as candidates likely to impart passivity on vapor deposited magnesium alloys. Prior to this research, alloys of this type have never before been produced, much less studied. All of these metals were observed to afford some degree of corrosion resistance to magnesium. Due to the especially promising results from nonequilibrium alloying of magnesium with yttrium and titanium, the ternary magnesium-yttrium-titanium system was investigated in depth. While all of the alloys are lustrous, surface morphology is observed under the scanning electron microscope. The corrosion rate of the nonequilibrium sputtered alloys, as determined by polarization resistance, is significantly reduced compared to the most corrosion resistant commercial magnesium alloys. The open circuit potentials of the sputter deposited alloys are significantly more noble compared to commercial, equilibrium phase magnesium alloys. Galvanic corrosion susceptibility has also been considerably reduced. Nonequilibrium magnesium-yttrium-titanium alloys have been shown to achieve passivity autonomously by alteration of the composition chemistry of the surface oxide/hydroxide layer. Self-healing properties are also evident, as corrosion propagation can be arrested after initial pitting of the material. A clear relationship exists between the corrosion resistance of sputter vapor deposited magnesium alloys and the amount of ion bombardment incurred by the alloy during deposition. Argon pressure, the distance between the source and the substrate, and alloy morphology play important roles in determining the ability of the alloy to develop a passive film. Thermal effects, both during and after alloy deposition, alter the stress state of the alloys, precipitation of second phases, and the mechanical stability of the passive film. An optimal thermal treatment has been developed in order to maximize the corrosion resistance of the magnesium-yttrium-titanium alloys. The significance of the results includes the acquisition of electrochemical data for these novel materials, as well as expanding the utilization of magnesium alloys by the improvement in their corrosion resistance. The magnesium alloys developed in this work are more corrosion resistant than any commercial magnesium alloy. Structural components comprised of these alloys would therefore exhibit unprecedented corrosion performance. Coatings of these alloys on magnesium components would provide a corrosion resistant yet galvanically-compatible coating. The broad impact of these contributions is that these new low-density, corrosion resistant magnesium alloys can be used to produce engineering components for vehicles that have greater acceleration, longer range, heavier payloads, lower life cycle costs, and longer inspection intervals.

Effect of eliminating the residual fluoride gel on titanium bracket corrosion.

PubMed

Khoury, Elie S; Abboud, Maher; Bassil-Nassif, Nayla; Bouserhal, Joseph

2011-09-01

Fluoride ions, in long-term applications on titanium brackets, cause their corrosion. Fluoride gel used for caries prevention during orthodontic treatment has a very high concentration in fluoride ions, and therefore has the potential for causing bracket corrosion. The main aim of this study was to determine the effect of eliminating the residual fluoride gel, by rinsing it, on the corrosion of titanium brackets. The secondary aim was to evaluate the corrosion of titanium brackets in the presence of fluoride gel. One hundred titanium brackets were divided into five groups of 20 brackets each. Group 1 being the control group, the rest of the groups were immersed in fluoride gel: Group 2 for 4 minutes and kept for 30 minutes with the residual fluoride gel on; Group 3 for 4 minutes followed by immediate water rinsing; Group 4 for 12 minutes and kept for 90 minutes with the residual fluoride gel on and Group 5 for 12 minutes followed by immediate water rinsing. All groups were rinsed then dried, for 20 hours, using Silica gel in a desiccator maintained at 37°C before testing. Gravimetrical results and SEM analysis showed no significant difference between Groups 2, 3 and 5 compared to each other and to the control group. Only Group 4 showed significant weight loss and pitting corrosion in four of the 20 brackets. In sliding resistance, no significant difference was detected between any of the groups. Short time applications of fluoride gel do not affect sliding resistance of titanium brackets. No titanium corrosion was detected for one application of concentrated fluoride gel and some brackets showed pitting corrosion for three applications. The rinsing of residual fluoride gel eliminates completely the risk of bracket corrosion. Copyright © 2011 CEO. Published by Elsevier Masson SAS. All rights reserved.

Influence of gas-powder laser cladding’s technological parameters on structural characteristics of corrosion-resistant steels’ restored surface layer

NASA Astrophysics Data System (ADS)

Krylova, S. E.; Oplesnin, S. P.; Goltyapin, M. I.

2018-03-01

The results of the developed industrial technology for surface restoration of corrosion-resistant steels by laser surfacing are presented in the article. A comparative analysis of the microstructure of the welded wear-resistant layer, the fusion zone with the base material and the diffusion zone for different technological surfacing regimes are given. Dyrometric studies and nondestructive testing of the deposited layer for defects were performed

Effect of ECAP processing on corrosion resistance of AE21 and AE42 magnesium alloys

NASA Astrophysics Data System (ADS)

Minárik, P.; Král, R.; Janeček, M.

2013-09-01

Corrosion properties of AE21 and AE42 magnesium alloys were investigated in the extruded state and after subsequent 8 passes of Equal Channel Angular Pressing (ECAP) via route Bc, by Electrochemical Impedance Spectroscopy (EIS) in 0.1 M NaCl solution. The resulting microstructure was observed by the Transmission Electron Microscope (TEM) and the Scanning Electron Microscope (SEM). Corrosion layer created after 7 days of immersion was observed by (SEM) in order to explain different evolution of the corrosion resistance after ECAP processing in both alloys. It was found that Al-rich Al11RE3 dispersed particles (present in both alloys) strongly influence the corrosion process and enhance the corrosion resistance. Ultra-fine grained structure was found to reduce the corrosion resistance in AE21. On the other hand, the microstructure of AE42 after ECAP and particularly the better distribution of the alloying elements in the matrix enhance the corrosion resistance when compared to the extruded material.

Localized CO2 corrosion of carbon steel with different microstructures in brine solutions with an imidazoline-based inhibitor

NASA Astrophysics Data System (ADS)

Zhang, Huan-huan; Pang, Xiaolu; Gao, Kewei

2018-06-01

CO2 corrosion behavior of carbon steel with different microstructures (H steel: coarse laminar pearlite; T steel: globular and shot rod shaped pearlite) was analyzed in 3 wt.% NaCl solution at 60 °C with imidazoline-based inhibitor by electrochemical and weight loss methods. Electrochemical measurements showed that, compared to H steel, the inhibitor film adsorbed on T steel had a higher pitting corrosion resistance and the inhibition efficiency for T steel was larger at each concentration of inhibitor. Weight loss results exhibited that both steels suffered general corrosion in absence of inhibitor; however, localized corrosion was observed on the samples with insufficient concentration of inhibitor. H steel suffered more severe localized corrosion than T steel, it was related to that H steel had a higher density of dislocations in the pearlite area and the larger driving force for galvanic corrosion. The localized corrosion on H steel mainly distributed on the laminar pearlite area.

Effect of Microstructure on Stress Corrosion Cracking Behaviour of High Nitrogen Stainless Steel Gas Tungsten Arc Welds

NASA Astrophysics Data System (ADS)

Mohammed, Raffi; Srinivasa Rao, K.; Madhusudhan Reddy, G.

2018-03-01

Present work is aimed to improve stress corrosion cracking resistance of high nitrogen steel and its welds. An attempt to weld high nitrogen steel of 5 mm thick plate using gas tungsten arc welding (GTAW) with three high strength age hardenable fillers i.e., 11-10 PH filler, PH 13- 8Mo and maraging grade of MDN 250 filler is made. Welds were characterized by optical microscopy and scanning electron microscopy. Vickers hardness testing of the welds was carried out to study the mechanical behaviour of welds. Potentio-dynamic polarization studies were done to determine pitting corrosion resistance in aerated 3.5% NaCl solution. Stress corrosion cracking (SCC) testing was carried out using constant load type machine with applied stress of 50% yield strength and in 45% MgCl2 solution boiling at 155°C. The results of the present investigation established that improvement in resistance to stress corrosion cracking was observed for PH 13- 8Mo GTA welds when compared to 11-10 PH and MDN 250 GTA welds. However, All GTA welds failed in the weld interface region. This may be attributed to relatively lower pitting potential in weld interface which acts as active site and the initiation source of pitting.

Effect of Fluoride on Nickel-Titanium and Stainless Steel Orthodontic Archwires: An In-Vitro Study

PubMed Central

Heravi, Farzin; Moayed, Mohamad Hadi; Mokhber, Nima

2015-01-01

Objectives: The commonly used Nickel-Titanium (NiTi) archwires in orthodontic treatment are often exposed to fluoride-containing mouthwashes. The aim of this in-vitro study was to evaluate and compare the corrosion resistance of three commercially available NiTi archwires exposed to 0.05 wt% and 0.2 wt% fluoride mouthwashes. Materials and Methods: Three different types of NiTi archwires, 0.016″ in diameter, from Dentaurum, Global, and GAC, and a stainless steel archwire from Dentaurum were examined to assess their corrosion resistance in Fusayama-Meyer artificial saliva and in two other artificial saliva containing 0.05 wt% and 0.2 wt% sodium fluoride (NaF). After the primary setup of wires, they were tested by potentiodynamic and potentiostatic polarization and corrosion potential/time analyses. Their surfaces were evaluated using a scanning electronic microscope (SEM). Results: The results showed that all the wires were passive in artificial saliva. In contrast, by adding fluoride ions to the solution, the decrease in the archwires’ corrosion resistance was in direct proportion to the increase in fluoride concentration. Conclusion: The NiTi wires experienced deterioration of their corrosion properties under the effect of fluoride but not as much as the stainless steel archwires. PMID:26005454

Deterministic analysis of processes at corroding metal surfaces and the study of electrochemical noise in these systems

DOE Office of Scientific and Technical Information (OSTI.GOV)

Latanision, R.M.

1990-12-01

Electrochemical corrosion is pervasive in virtually all engineering systems and in virtually all industrial circumstances. Although engineers now understand how to design systems to minimize corrosion in many instances, many fundamental questions remain poorly understood and, therefore, the development of corrosion control strategies is based more on empiricism than on a deep understanding of the processes by which metals corrode in electrolytes. Fluctuations in potential, or current, in electrochemical systems have been observed for many years. To date, all investigations of this phenomenon have utilized non-deterministic analyses. In this work it is proposed to study electrochemical noise from a deterministicmore » viewpoint by comparison of experimental parameters, such as first and second order moments (non-deterministic), with computer simulation of corrosion at metal surfaces. In this way it is proposed to analyze the origins of these fluctuations and to elucidate the relationship between these fluctuations and kinetic parameters associated with metal dissolution and cathodic reduction reactions. This research program addresses in essence two areas of interest: (a) computer modeling of corrosion processes in order to study the electrochemical processes on an atomistic scale, and (b) experimental investigations of fluctuations in electrochemical systems and correlation of experimental results with computer modeling. In effect, the noise generated by mathematical modeling will be analyzed and compared to experimental noise in electrochemical systems. 1 fig.« less

Pitting corrosion as a mixed system: coupled deterministic-probabilistic simulation of pit growth

NASA Astrophysics Data System (ADS)

Ibrahim, Israr B. M.; Fonna, S.; Pidaparti, R.

2018-05-01

Stochastic behavior of pitting corrosion poses a unique challenge in its computational analysis. However, it also stems from electrochemical activity causing general corrosion. In this paper, a framework for corrosion pit growth simulation based on the coupling of the Cellular Automaton (CA) and Boundary Element Methods (BEM) is presented. The framework assumes that pitting corrosion is controlled by electrochemical activity inside the pit cavity. The BEM provides the prediction of electrochemical activity given the geometrical data and polarization curves, while the CA is used to simulate the evolution of pit shapes based on electrochemical activity provided by BEM. To demonstrate the methodology, a sample case of local corrosion cells formed in pitting corrosion with varied dimensions and polarization functions is considered. Results show certain shapes tend to grow in certain types of environments. Some pit shapes appear to pose a higher risk by being potentially significant stress raisers or potentially increasing the rate of corrosion under the surface. Furthermore, these pits are comparable to commonly observed pit shapes in general corrosion environments.

Information Theory Filters for Wavelet Packet Coefficient Selection with Application to Corrosion Type Identification from Acoustic Emission Signals

PubMed Central

Van Dijck, Gert; Van Hulle, Marc M.

2011-01-01

The damage caused by corrosion in chemical process installations can lead to unexpected plant shutdowns and the leakage of potentially toxic chemicals into the environment. When subjected to corrosion, structural changes in the material occur, leading to energy releases as acoustic waves. This acoustic activity can in turn be used for corrosion monitoring, and even for predicting the type of corrosion. Here we apply wavelet packet decomposition to extract features from acoustic emission signals. We then use the extracted wavelet packet coefficients for distinguishing between the most important types of corrosion processes in the chemical process industry: uniform corrosion, pitting and stress corrosion cracking. The local discriminant basis selection algorithm can be considered as a standard for the selection of the most discriminative wavelet coefficients. However, it does not take the statistical dependencies between wavelet coefficients into account. We show that, when these dependencies are ignored, a lower accuracy is obtained in predicting the corrosion type. We compare several mutual information filters to take these dependencies into account in order to arrive at a more accurate prediction. PMID:22163921

In vitro electrochemical corrosion and cell viability studies on nickel-free stainless steel orthopedic implants.

PubMed

Salahinejad, Erfan; Hadianfard, Mohammad Jafar; Macdonald, Digby Donald; Sharifi-Asl, Samin; Mozafari, Masoud; Walker, Kenneth J; Rad, Armin Tahmasbi; Madihally, Sundararajan V; Tayebi, Lobat

2013-01-01

The corrosion and cell viability behaviors of nanostructured, nickel-free stainless steel implants were studied and compared with AISI 316L. The electrochemical studies were conducted by potentiodynamic polarization and electrochemical impedance spectroscopic measurements in a simulated body fluid. Cytocompatibility was also evaluated by the adhesion behavior of adult human stem cells on the surface of the samples. According to the results, the electrochemical behavior is affected by a compromise among the specimen's structural characteristics, comprising composition, density, and grain size. The cell viability is interpreted by considering the results of the electrochemical impedance spectroscopic experiments.

A quantitative study on magnesium alloy stent biodegradation.

PubMed

Gao, Yuanming; Wang, Lizhen; Gu, Xuenan; Chu, Zhaowei; Guo, Meng; Fan, Yubo

2018-06-06

Insufficient scaffolding time in the process of rapid corrosion is the main problem of magnesium alloy stent (MAS). Finite element method had been used to investigate corrosion of MAS. However, related researches mostly described all elements suffered corrosion in view of one-dimensional corrosion. Multi-dimensional corrosions significantly influence mechanical integrity of MAS structures such as edges and corners. In this study, the effects of multi-dimensional corrosion were studied using experiment quantitatively, then a phenomenological corrosion model was developed to consider these effects. We implemented immersion test with magnesium alloy (AZ31B) cubes, which had different numbers of exposed surfaces to analyze differences of dimension. It was indicated that corrosion rates of cubes are almost proportional to their exposed-surface numbers, especially when pitting corrosions are not marked. The cubes also represented the hexahedron elements in simulation. In conclusion, corrosion rate of every element accelerates by increasing corrosion-surface numbers in multi-dimensional corrosion. The damage ratios among elements with the same size are proportional to the ratios of corrosion-surface numbers under uniform corrosion. The finite element simulation using proposed model provided more details of changes of morphology and mechanics in scaffolding time by removing 25.7% of elements of MAS. The proposed corrosion model reflected the effects of multi-dimension on corrosions. It would be used to predict degradation process of MAS quantitatively. Copyright © 2018 Elsevier Ltd. All rights reserved.

Prediction of corrosion rates of water distribution pipelines according to aggressive corrosive water in Korea.

PubMed

Chung, W S; Yu, M J; Lee, H D

2004-01-01

The drinking water network serving Korea has been used for almost 100 years. Therefore, pipelines have suffered various degrees of deterioration due to aggressive environments. The pipe breaks were caused by in-external corrosion, water hammer, surface loading, etc. In this paper, we focused on describing corrosion status in water distribution pipes in Korea and reviewing some methods to predict corrosion rates. Results indicate that corrosive water of lakes was more aggressive than river water and the winter was more aggressive compared to other seasons. The roughness growth rates of Dongbok lake showed 0.23 mm/year. The high variation of corrosion rates is controlled by the aging pipes and smaller diameter. Also the phenolphthalein test on a cementitious core of cement mortar lined ductile cast iron pipe indicated the pipes over 15 years old had lost 50-100% of their lime active cross sectional area.

Corrosion Behavior of Steels in Supercritical CO 2 for Power Cycle Applications

DOE Office of Scientific and Technical Information (OSTI.GOV)

Repukaiti, Richard; Teeter, Lucas; Ziomek-Moroz, Margaret

In order to understand issues with corrosion of heat exchanger materials in direct supercritical carbon dioxide (sCO 2) power cycles, a series of autoclave exposure experiments and electrochemical experiments have been conducted. Corrosion behaviors of 347H stainless steel and P91 martensitic-ferrtic steel in sCO 2 environment have been compared. In autoclave exposure tests performed at 50°C- 245°C and 80 bar. Mass change measurements, surface characterization, and corrosion product analysis have been conducted to understand the corrosion behavior of steels in sCO 2 containing H 2O and O 2. Electrochemical tests performed at room temperature and 50°C, a simulation environment ofmore » water condensation phase with dissolved CO 2 was prepared to evaluate the corrosion resistance of materials. From both types of experiments, generally 347H showed higher corrosion resistance than P91.« less

Titanium Ions Release from an Innovative Titanium-Magnesium Composite: an in Vitro Study

PubMed Central

Halambek, Jasna; Maldini, Krešimir; Balog, Martin; Križik, Peter; Schauperl, Zdravko; Ćatić, Amir

2016-01-01

Background The innovative titanium-magnesium composite (Ti-Mg) was produced by powder metallurgy (P/M) method and is characterized in terms of corrosion behavior. Material and methods Two groups of experimental material, 1 mass% (Ti-1Mg) and 2 mass% (Ti-2Mg) of magnesium in titanium matrix, were tested and compared to commercially pure titanium (CP Ti). Immersion test and chemical analysis of four solutions: artificial saliva; artificial saliva pH 4; artificial saliva with fluoride and Hank balanced salt solution were performed after 42 days of immersion, using inductively coupled plasma mass spectrometry (ICP-MS) to detect the amount of released titanium ions (Ti). SEM and EDS analysis were used for surface characterization. Results The difference between the results from different test solutions was assessed by ANOVA and Newman-Keuls test at p<0.05. The influence of predictor variables was found by multiple regression analysis. The results of the present study revealed a low corrosion rate of titanium from the experimental Ti-Mg group. Up to 46 and 23 times lower dissolution of Ti from Ti-1Mg and Ti-2Mg, respectively was observed compared to the control group. Among the tested solutions, artificial saliva with fluorides exhibited the highest corrosion effect on all specimens tested. SEM micrographs showed preserved dual phase surface structure and EDS analysis suggested a favorable surface bioactivity. Conclusion In conclusion, Ti-Mg produced by P/M as a material with better corrosion properties when compared to CP Ti is suggested. PMID:27688425

Effect of cloric acid concentration on corrosion behavior of Ni/Cr coated on carbon steel

NASA Astrophysics Data System (ADS)

Desiati, Resetiana Dwi; Sugiarti, Eni; Thosin, K. A. Zaini

2018-05-01

Corrosion is one of the causes of metal degradation. Carbon steel (Fe) is easy to corrode in the extreme environment. Coating on carbon steel is required to improve corrosion resistance owing to protection or hindrance to extreme environmental conditions. In this present work, carbon steel was coated by electroplating techniques for nickel and pack cementation for chrome. The corrosion rate test was performed by Weight Loss method on FeNiCr, FeNi, FeCr and uncoated Fe as comparator which was dyed in 37% HCl and 25% HCl which had previously been measured dimension and mass. The immersion test result of FeNiCr and FeNi specimen were better than FeCr and uncoated Fe in terms of increasing corrosion resistance. The corrosion rate for 56 hours in 37% HCl for FeNiCr was 1.592 mm/y and FeNi was 3.208 mm/y, FeCr only lasted within 32 hours with corrosion rate was 6.494 mm/y. Surface of the sample after the corrosion test there was pitting, crevice corrosion and alloy cracking caused by chloride. The higher the concentration of HCl the faster the corrosion rate.

Microstructure and Corrosion Behavior of Laser Melted 304L SS Weldment in Nitric Acid Medium

NASA Astrophysics Data System (ADS)

Suresh, Girija; Kishor, P. S. V. R. A.; Dasgupta, Arup; Upadhyay, B. N.; Mallika, C.; Kamachi Mudali, U.

2017-02-01

The manuscript presents the effect of laser surface melting on the corrosion property of 304L SS weldment in nitric acid medium. 304L SS weldment was prepared by gas tungsten arc welding process and subsequently laser surface melted using Nd:YAG laser. The microstructure and corrosion resistance of laser surface melted 304L SS weldment was evaluated and compared with that of 304L SS as-weldment and 304L SS base. Microstructural evaluation was carried out using optical and scanning electron microscopes attached with energy-dispersive x-ray spectroscopy. Corrosion investigations were carried out in 4 and 8 M nitric acid by potentiodynamic polarization technique. From the results, it was found that laser surface melting of the weldment led to chemical and microstructural homogeneities, accompanied by a substantial decrease in delta ferrite content, that enhanced the corrosion resistance of the weldment in 4 and 8 M nitric acid. However, the enhancement in the corrosion resistance was not substantial. The presence of small amount of delta ferrite (2-4 wt.%) in the laser surface melted specimens was found to be detrimental in nitric acid. X-ray photoelectron spectroscopy studies were carried out to investigate the composition of the passive film.

Electrochemical Study of Polymer and Ceramic-Based Nanocomposite Coatings for Corrosion Protection of Cast Iron Pipeline

PubMed Central

Ammar, Ameen Uddin; Shahid, Muhammad; Ahmed, Muhammad Khitab; Khan, Munawar; Khalid, Amir

2018-01-01

Coating is one of the most effective measures to protect metallic materials from corrosion. Various types of coatings such as metallic, ceramic and polymer coatings have been investigated in a quest to find durable coatings to resist electrochemical decay of metals in industrial applications. Many polymeric composite coatings have proved to be resistant against aggressive environments. Two major applications of ferrous materials are in marine environments and in the oil and gas industry. Knowing the corroding behavior of ferrous-based materials during exposure to these aggressive applications, an effort has been made to protect the material by using polymeric and ceramic-based coatings reinforced with nano materials. Uncoated and coated cast iron pipeline material was investigated during corrosion resistance by employing EIS (electrochemical impedance spectroscopy) and electrochemical DC corrosion testing using the “three electrode system”. Cast iron pipeline samples were coated with Polyvinyl Alcohol/Polyaniline/FLG (Few Layers Graphene) and TiO2/GO (graphene oxide) nanocomposite by dip-coating. The EIS data indicated better capacitance and higher impedance values for coated samples compared with the bare metal, depicting enhanced corrosion resistance against seawater and “produce water” of a crude oil sample from a local oil rig; Tafel scans confirmed a significant decrease in corrosion rate of coated samples. PMID:29495339

Electrochemical Study of Polymer and Ceramic-Based Nanocomposite Coatings for Corrosion Protection of Cast Iron Pipeline.

PubMed

Ammar, Ameen Uddin; Shahid, Muhammad; Ahmed, Muhammad Khitab; Khan, Munawar; Khalid, Amir; Khan, Zulfiqar Ahmad

2018-02-25

Coating is one of the most effective measures to protect metallic materials from corrosion. Various types of coatings such as metallic, ceramic and polymer coatings have been investigated in a quest to find durable coatings to resist electrochemical decay of metals in industrial applications. Many polymeric composite coatings have proved to be resistant against aggressive environments. Two major applications of ferrous materials are in marine environments and in the oil and gas industry. Knowing the corroding behavior of ferrous-based materials during exposure to these aggressive applications, an effort has been made to protect the material by using polymeric and ceramic-based coatings reinforced with nano materials. Uncoated and coated cast iron pipeline material was investigated during corrosion resistance by employing EIS (electrochemical impedance spectroscopy) and electrochemical DC corrosion testing using the "three electrode system". Cast iron pipeline samples were coated with Polyvinyl Alcohol/Polyaniline/FLG (Few Layers Graphene) and TiO₂/GO (graphene oxide) nanocomposite by dip-coating. The EIS data indicated better capacitance and higher impedance values for coated samples compared with the bare metal, depicting enhanced corrosion resistance against seawater and "produce water" of a crude oil sample from a local oil rig; Tafel scans confirmed a significant decrease in corrosion rate of coated samples.

Effect of Repeated Sterilization Cycles on the Physical Properties of Scaling Instruments: A Scanning Electron Microscopy Study

PubMed Central

Porto, Alessandra Nogueira; Borges, Álvaro Henrique; Semenoff-Segundo, Alex; Raslan, Suzane A; Pedro, Fábio Luis Miranda; Jorge, Antônio Olavo Cardoso; Bandeca, Matheus Coelho

2015-01-01

Background: Repeated sterilizations cycles cause undesirable alterations in the material properties of the instruments, such as corrosion, alterations in the hardness of the metal and the loss of the cutting sharpness of the instrument. This research examined the effect of repeated dry heat sterilization and autoclaves cycles on carbon steel (CS) and stainless steel (SS) curettes during the scaling and root planning. Materials and Methods: A total of 77 Gracey curettes were used in this study. Of these, 35 were SS and 42 were CS curettes submitted in different process: Dry heat, autoclave, inhibition of corrosion and autoclave, scaling, root planning and dry heat, scaling, root planning, inhibition of corrosion and autoclave. The inhibition of corrosion used on the carbon curettes (prior to sterilization in the autoclave) was sodium nitrite at 2%. The curettes received 10 consecutive cycles of sterilization and after that the cutting edges were examined in the electronic microscope, at 60 and 100 magnification times. Results: The images were evaluated by three independent examiners, who compared the photographs of each group with the control group. Conclusion: The surface corrosion products and a deterioration of the edges were observed and the results showed that the SS curettes suffered little alteration with sterilization, scaling, root planning whereas the CS curettes were visibly affected by sterilization in the autoclave, but when the inhibition of corrosion was used prior to the sterilization, the oxidation was considerably reduced. PMID:26028893

Studies on Fusion Welding of High Nitrogen Stainless Steel: Microstructure, Mechanical and corrosion Behaviour

NASA Astrophysics Data System (ADS)

Mohammed, Raffi; Srinivasa Rao, K.; Madhusudhan Reddy, G.

2018-03-01

An attempt has been made in the present investigation to weld high nitrogen steel of 5mm thick plates using various process i.e., shielded metal arc welding (SMAW), gas tungsten arc welding (GTAW) and autogenous electron beam welding (EBW) process. Present work is aimed at studying the microstructural changes and its effects on mechanical properties and corrosion resistance. Microstructure is characterized by optical, scanning electron microscopy and electron back scattered diffraction technique. Vickers hardness, tensile properties, impact toughness and face bend ductility testing of the welds was carried out. Pitting corrosion resistance of welds was determined using potentio-dynamic polarization testing in 3.5%NaCl solution. Results of the present investigation established that SMA welds made using Cr-Mn-N electrode were observed to have a austenite dendritic grain structure in the weld metal and is having poor mechanical properties but good corrosion resistance. GTA welds made using 18Ni (MDN 250) filler wire were observed to have a reverted austenite in martensite matrix of the weld metal and formation of unmixed zone at the fusion boundary which resulted in better mechanical properties and poor corrosion resistance. Fine grains and uniform distribution of delta ferrite in the austenite matrix and narrow width of weld zone are observed in autogeneous electron beam welds. A good combination of mechanical properties and corrosion resistance was achieved for electron beam welds of high nitrogen steel when compared to SMA and GTA welds.

Corrosive Metabolic Activity of Desulfovibrio sp. on 316L Stainless Steel

NASA Astrophysics Data System (ADS)

Arkan, Simge; Ilhan-Sungur, Esra; Cansever, Nurhan

2016-12-01

The present study investigated the effects of chemical parameters (SO4 2-, PO4 3-, Cl-, pH) and the contents of extracellular polymeric substances (EPS) regarding the growth of Desulfovibrio sp. on the microbiologically induced corrosion of 316L stainless steel (SS). The experiments were carried out in laboratory-scaled test and control systems. 316L SS coupons were exposed to Desulfovibrio sp. culture over 720 h. The test coupons were removed at specific sampling times for enumeration of Desulfovibrio sp., determination of the corrosion rate by the weight loss measurement method and also for analysis of carbohydrate and protein in the EPS. The chemical parameters of the culture were also established. Biofilm/film formation and corrosion products on the 316L SS surfaces were investigated by scanning electron microscopy and energy-dispersive x-ray spectrometry analyses in the laboratory-scaled systems. It was found that Desulfovibrio sp. led to the corrosion of 316L SS. Both the amount of extracellular protein and chemical parameters (SO4 2- and PO4 3-) of the culture caused an increase in the corrosion of metal. There was a significantly positive relationship between the sessile and planktonic Desulfovibrio sp. counts ( p < 0.01). It was detected that the growth phases of the sessile and planktonic Desulfovibrio sp. were different from each other and the growth phases of the sessile Desulfovibrio sp. vary depending on the subspecies of Desulfovibrio sp. and the type of metal when compared with the other published studies.

Differential magnesium implant corrosion coat formation and contribution to bone bonding.

PubMed

Rahim, Muhammad Imran; Weizbauer, Andreas; Evertz, Florian; Hoffmann, Andrea; Rohde, Manfred; Glasmacher, Birgit; Windhagen, Henning; Gross, Gerhard; Seitz, Jan-Marten; Mueller, Peter P

2017-03-01

Magnesium alloys are presently under investigation as promising biodegradable implant materials with osteoconductive properties. To study the molecular mechanisms involved, the potential contribution of soluble magnesium corrosion products to the stimulation of osteoblastic cell differentiation was examined. However, no evidence for the stimulation of osteoblast differentiation could be obtained when cultured mesenchymal precursor cells were differentiated in the presence of metallic magnesium or in cell culture medium containing elevated magnesium ion levels. Similarly, in soft tissue no bone induction by metallic magnesium or by the corrosion product magnesium hydroxide could be observed in a mouse model. Motivated by the comparatively rapid accumulation solid corrosion products physicochemical processes were examined as an alternative mechanism to explain the stimulation of bone growth by magnesium-based implants. During exposure to physiological solutions a structured corrosion coat formed on magnesium whereby the elements calcium and phosphate were enriched in the outermost layer which could play a role in the established biocompatible behavior of magnesium implants. When magnesium pins were inserted into avital bones, corrosion lead to increases in the pull out force, suggesting that the expanding corrosion layer was interlocking with the surrounding bone. Since mechanical stress is a well-established inducer of bone growth, volume increases caused by the rapid accumulation of corrosion products and the resulting force development could be a key mechanism and provide an explanation for the observed stimulatory effects of magnesium-based implants in hard tissue. © 2016 Wiley Periodicals, Inc. J Biomed Mater Res Part A: 105A: 697-709, 2017. © 2016 Wiley Periodicals, Inc.

The influence of buffer system and biological fluids on the degradation of magnesium.

PubMed

Törne, Karin; Örnberg, Andreas; Weissenrieder, Jonas

2017-08-01

The influence of frequently used buffer system 4-(2-hydroxyethyl)-1-piperazineethanesulfonic acid (HEPES) compared to CO 2 /HCO3- on the corrosion of magnesium is investigated. Samples were immersed in simulated body fluid (m-SBF) while monitored by electrochemical impedance spectroscopy (EIS) for up to 30 days. In CO 2 /HCO3- the initial corrosion rate was 0.11 mm yr -1 . An inner protective layer of magnesium oxide was formed within the first 30 min exposure and subsequently covered by an outer layer of apatite within 24 h . The corrosion mechanism thereafter is best described as passive pitting with a porosity of ∼10%. Using HEPES as buffer agent increased the corrosion rate to 3.37 mm yr -1 . Cross sectional microscopy show a porous outer corrosion layer allowing rapid diffusion of aggressive ions through the film. Here the EIS results are best described by an active pitting model with an inner layer 5 to 10 times less protective compared to the inner layer formed without HEPES. Further the suitability of human whole blood and plasma as in vitro models for Mg degradation was evaluated. Mg corrosion caused coagulation after 24 h in both biological fluids. The corrosion during the first 24 h is similar to the corrosion in m-SBF with HEPES. © 2016 Wiley Periodicals, Inc. J Biomed Mater Res Part B: Appl Biomater, 105B: 1490-1502, 2017. © 2016 Wiley Periodicals, Inc.

Corrosion protection of copper by polypyrrole film studied by electrochemical impedance spectroscopy and the electrochemical quartz microbalance

NASA Astrophysics Data System (ADS)

Lei, Yanhua; Ohtsuka, Toshiaki; Sheng, Nan

2015-12-01

Polypyrrole (PPy) films were synthesized on copper in solution of sodium di-hydrogen phosphate and phytate for corrosion protection. The protection properties of PPy films were comparatively investigated in NaCl solution. During two months immersion, the PPy film doped with phytate anions, working as a cationic perm-selective membrane, inhibited the dissolution of copper to 1% of bare copper. Differently, the PPy film doped with di-hydrogen phosphate anions, possessing anionic perm-selectivity, was gradually reduced, and inhibited the dissolution to 7.8% of bare copper. Degradation of the PPy films was studied by comparing the electrochemical impedance spectroscopy change at different immersion time and Raman spectra change after immersion.

Simulation of Fatigue Crack Initiation at Corrosion Pits With EDM Notches

NASA Technical Reports Server (NTRS)

Smith, Stephen W.; Newman, John A.; Piascik, Robert S.

2003-01-01

Uniaxial fatigue tests were conducted to compare the fatigue life of laboratory produced corrosion pits, similar to those observed in the shuttle main landing gear wheel bolt-hole, and an electro-discharged-machined (EDM) flaw. EDM Jaws are used to simulate corrosion pits during shuttle wheel (dynamometer) testing. The aluminum alloy, (AA 7050) laboratory fatigue tests were conducted to simulate the local stress level contained in the wheel bolt-hole. Under this high local stress condition, the EDM notch produced a fatigue life similar to test specimens containing corrosion pits of similar size. Based on the laboratory fatigue test results, the EDM Jaw (semi-circular disc shaped) produces a local stress state similar to corrosion pits and can be used to simulate a corrosion pit during the shuttle wheel dynamometer tests.

Erosion-corrosion and cavitation-erosion measurements on copper alloys utilizing thin layer activation technique

DOE Office of Scientific and Technical Information (OSTI.GOV)

Tsai, C.H.; Hsu, K.Y.; Kai, J.J.

1992-12-31

The surface layers of copper alloy specimens were made radioactive by bombarding with 5 MeV protons from a van de Graaff accelerator which converted Cu-65 into Zn-65 through (p,n) reaction. The amount of surface material loss could then be monitored by measuring the total remaining {gamma}-ray activity generated from Zn-65 decay. This technique, termed thin layer activation (TLA), has the advantage of in situ monitoring the rate of surface removal due to corrosion, erosion-corrosion, wearing, etc. In this work, the erosion-corrosion tests on aluminum brass and 90Cu-10Ni were conducted in circulating sea water and the erosion-corrosion rates measured using TLAmore » and conventional methods such as linear polarization resistance (LPR) method and weight loss coupons were compared. A vibrational cavitation-erosion test was also performed on aluminum bronze, in which the measurements by TLA were compared with those of weight loss measurements.« less

In vitro corrosion behaviour of Ti-Nb-Sn shape memory alloys in Ringer's physiological solution.

PubMed

Rosalbino, F; Macciò, D; Scavino, G; Saccone, A

2012-04-01

The nearly equiatomic Ni-Ti alloy (Nitinol) has been widely employed in the medical and dental fields owing to its shape memory or superelastic properties. The main concern about the use of this alloy derives form the fact that it contains a large amount of nickel (55% by mass), which is suspected responsible for allergic, toxic and carcinogenic reactions. In this work, the in vitro corrosion behavior of two Ti-Nb-Sn shape memory alloys, Ti-16Nb-5Sn and Ti-18Nb-4Sn (mass%) has been investigated and compared with that of Nitinol. The in vitro corrosion resistance was assessed in naturally aerated Ringer's physiological solution at 37°C by corrosion potential and electrochemical impedance spectroscopy (EIS) measurements as a function of exposure time, and potentiodynamic polarization curves. Corrosion potential values indicated that both Ni-Ti and Ti-Nb-Sn alloys undergo spontaneous passivation due to spontaneously formed oxide film passivating the metallic surface, in the aggressive environment. It also indicated that the tendency for the formation of a spontaneous oxide is greater for the Ti-18Nb-5Sn alloy. Significantly low anodic current density values were obtained from the polarization curves, indicating a typical passive behaviour for all investigated alloys, but Nitinol exhibited breakdown of passivity at potentials above approximately 450 mV(SCE), suggesting lower corrosion protection characteristics of its oxide film compared to the Ti-Nb-Sn alloys. EIS studies showed high impedance values for all samples, increasing with exposure time, indicating an improvement in corrosion resistance of the spontaneous oxide film. The obtained EIS spectra were analyzed using an equivalent electrical circuit representing a duplex structure oxide film, composed by an outer and porous layer (low resistance), and an inner barrier layer (high resistance) mainly responsible for the alloys corrosion resistance. The resistance of passive film present on the metals' surface increases with exposure time displaying the highest values to Ti-18Nb-4Sn alloy. All these electrochemical results suggest that Ti-Nb-Sn alloys are promising materials for biomedical applications.

Bioengineered silver nanoparticles as potent anti-corrosive inhibitor for mild steel in cooling towers.

PubMed

Narenkumar, Jayaraman; Parthipan, Punniyakotti; Madhavan, Jagannathan; Murugan, Kadarkarai; Marpu, Sreekar Babu; Suresh, Anil Kumar; Rajasekar, Aruliah

2018-02-01

Silver nanoparticle-aided enhancement in the anti-corrosion potential and stability of plant extract as ecologically benign alternative for microbially induced corrosion treatment is demonstrated. Bioengineered silver nanoparticles (AgNPs) surface functionalized with plant extract material (proteinacious) was generated in vitro in a test tube by treating ionic AgNO 3 with the leaf extract of Azadirachta indica that acted as dual reducing as well as stabilizing agent. Purity and crystallinity of the AgNPs, along with physical and surface characterizations, were evaluated by performing transmission electron microscopy, Fourier transform infrared spectroscopy, energy dispersive x-ray spectra, single-area electron diffractions, zeta potential, and dynamic light scattering measurements. Anti-corrosion studies against mild steel (MS1010) by corrosion-inducive bacterium, Bacillus thuringiensis EN2 isolated from cooling towers, were evaluated by performing electrochemical impedance spectroscopy (EIS), weight loss analysis, and surface analysis by infrared spectroscopy. Our studies revealed that AgNPs profoundly inhibited the biofilm on MS1010 surface and reduced the corrosion rates with the CR of 0.5 mm/y and an inhibition efficiency of 77% when compared to plant extract alone with a CR of 2.2 mm/y and an inhibition efficiency of 52%. Further surface analysis by infrared spectra revealed that AgNPs formed a protective layer of self-assembled film on the surface of MS1010. Additionally, EIS and surface analysis revealed that the AgNPs have inhibited the bacterial biofilm and reduced the pit on MS1010. This is the first report disclosing the application of bioengineered AgNP formulations as potent anti-corrosive inhibitor upon forming a protective layer over mild steel in cooling water towers. Graphical Abstract ᅟ.

Development in corrosion resistance by microstructural refinement in Zr-16 SS 304 alloy using suction casting technique

DOE Office of Scientific and Technical Information (OSTI.GOV)

Das, N., E-mail: nirupamd@barc.gov.in; Sengupta, P.; Abraham, G.

Highlights: • Grain refinement was made in Zr–16 wt.% SS alloy while prepared by suction casting process. • Distribution of Laves phase, e.g., Zr{sub 2}(Fe, Cr) was raised in suction cast (SC) Zr–16 wt.% SS. • Corrosion resistance was improved in SC alloy compared to that of arc-melt-cast alloy. • Grain refinement in SC alloy assisted for an increase in its corrosion resistance. - Abstract: Zirconium (Zr)-stainless steel (SS) hybrid alloys are being considered as baseline alloys for developing metallic-waste-form (MWF) with the motivation of disposing of Zr and SS base nuclear metallic wastes. Zr–16 wt.% SS, a MWF alloymore » optimized from previous studies, exhibit significant grain refinement and changes in phase assemblages (soft phase: Zr{sub 2}(Fe, Cr)/α-Zr vs. hard phase: Zr{sub 3}(Fe, Ni)) when prepared by suction casting (SC) technique in comparison to arc-cast-melt (AMC) route. Variation in Cr-distribution among different phases are found to be low in suction cast alloy, which along with grain refinement restricted Cr-depletion at the Zr{sub 2}(Fe, Cr)/Zr interfaces, prone to localized attack. Hence, SC alloy, compared to AMC alloy, showed lower current density, higher potential at the breakdown of passivity and higher corrosion potential during polarization experiments (carried out under possible geological repository environments, viz., pH 8, 5 and 1) indicating its superior corrosion resistance.« less

Effect of Organic Oxygen Scavenger on Performance of Pyrrole as Corrosion Inhibitor

NASA Astrophysics Data System (ADS)

Kassim, E. S. Mohd; Ibrahim, I. M.; Jai, J.; So’aib, M. S.; Zamanhuri, N. Ahmad; Husin, H.; Hashim, M. A.

2018-05-01

Abstract.The inhibitory effect of pyrrole in the presence of methyl ethyl ketoxime (MEKO) and erythorbic acid (EA) on the corrosion of carbon steel in static of condition 3.5 wt% NaCl solution were studied using Linear Polarization Resistance (LPR) method. Experimental results found that the inhibition effect of pyrrole increased with the increase of oxygen scavenger concentration.The inhibition efficiency was observed to be about 67% after addition of erythorbic acid (EA) into saline solution containing 100 ppm of pyrrole compared by adding MEKO which recorded about 59%. The addition of oxygen scavenger could reducing the corrosion rate of carbon steel by reacting with dissolved oxygen in the solution and thus further to protect metal surface.

Microstructure, Properties and Weldability of Duplex Stainless Steel 2101

NASA Astrophysics Data System (ADS)

Ma, Li; Hu, Shengsun; Shen, Junqi

2017-01-01

The continuous development of duplex stainless steels (DSSs) is due to their excellent corrosion resistance in aggressive environments and their mechanical strength, which is usually twice of conventional austenitic stainless steels (ASSs). In this paper, a designed lean duplex stainless steel 2101, with the alloy design of reduced nickel content and increased additions of manganese and nitrogen, is studied by being partly compared with typical ASS 304L steels. The microstructure, mechanical properties, impact toughness, corrosion resistance and weldability of the designed DSS 2101 were conducted. The results demonstrated that both 2101 steel and its weldment show excellent mechanical properties, impact toughness and corrosion resistance, so DSS 2101 exhibits good comprehensive properties and can be used to replace 304L in numerous applications.

Properties and Corrosion Performance of Self-reinforced Composite PEEK for Proposed Use as a Modular Taper Gasket.

PubMed

Ouellette, Eric S; Gilbert, Jeremy L

2016-11-01

Fretting corrosion in medical alloys is a persistent problem, and the need for biomaterials that can effectively suppress mechanically assisted crevice corrosion in modular taper junctions or otherwise insulate metal-on-metal interfaces in mechanically demanding environments is as yet unmet. The purpose of this study is to characterize a novel material, self-reinforced composite polyetheretherketone (SRC-PEEK) and to evaluate its ability to inhibit fretting corrosion in a pin-on-disk metal-on-metal interface test. SRC-PEEK was fabricated by hot compaction of in-house-made PEEK fibers by compacting uniaxial layups at 344°C under a load of 18,000 N for 10 minutes. SRC-PEEK, bulk isotropic PEEK, and the in-house-made PEEK fibers were analyzed for thermal transitions (T g , T m ) through differential scanning calorimetry, crystallinity, crystal size, crystalline orientation (Hermanns orientation parameter) through wide-angle x-ray scattering, and modulus, tensile strength, yield stress, and strain to failure through monotonic tensile testing. SRC-insulated pin-on-disk samples were compared with metal-on-metal control samples in pin-on-disk fretting corrosion experiments using fretting current and fretting mechanics measurements. Fifty-micron cyclic motion at 2.5 Hz was applied to the interface, first over a range of loads (0.5-35 N) while held at -0.05 V versus Ag/AgCl and then over a range of voltages (-0.5 to 0.5 V) at a constant contact stress of 73 ± 19 MPa for SRC-PEEK and 209 ± 41 MPa for metal-on-metal, which were different for each group as a result of changes in true contact area due to variations in modulus between sample groups. Pins, disks, and SRC samples were imaged for damage (on alloy and SRC surfaces) and evidence of corrosion (on alloy pin and disk surfaces). SRC specimens were analyzed for traces of alloy transferred to the surface using energy dispersive spectroscopy after pin-on-disk testing. SRC-PEEK showed improved mechanical properties to bulk PEEK (modulus = 5.0 ± 0.3 GPa, 2.8 ± 0.1 GPa, respectively, p < 0.001) and higher crystallinity to bulk PEEK (44.2% ± 3%, 39.5% ± 0.5%, respectively, p = 0.039), but had comparable crystalline orientation as compared with the initial PEEK fibers. SRC-PEEK reduced fretting currents compared with metal-on-metal controls by two to three orders of magnitude in both variable load (4.0E-5 ± 3.8E-5 μA versus 2.9E-3 ± 7.1E-4 μA, respectively, p = 0.018) and variable potential (7.5E-6 ± 4.7E-6 μA versus 5.3E-3 ± 1.4E-3 μA, respectively, p = 0.022) fretting corrosion testing. Minimal damage was observed on surfaces insulated with SRC-PEEK, whereas control surfaces showed considerable fretting corrosion damage and metal transfer. The SRC-PEEK gaskets in this study demonstrated higher crystallinity and crystalline orientation and improved monotonic tensile properties compared with bulk PEEK with the ability to effectively insulate Ti6Al4V and CoCrMo alloy surfaces and prevent the initiation of fretting corrosion under high contact-stress conditions. This novel SRC-PEEK material may offer potential as a thin film gasket material for modular tapers. Pending further in vitro and in vivo analyses, this approach may be able to preserve the advantages of modular junctions for surgeons while potentially limiting the downside risks associated with mechanically assisted crevice corrosion.

High Velocity Oxidation and Hot Corrosion Resistance of Some ODS Alloys

NASA Technical Reports Server (NTRS)

Lowell, C. E.; Deadmore, D. L.

1977-01-01

Several oxide dispersion strengthened (ODS) alloys were tested for cyclic, high velocity, oxidation, and hot corrosion resistance. These results were compared to the resistance of an advanced, NiCrAl coated superalloy. An ODS FeCrAl were identified as having sufficient oxidation and hot corrosion resistance to allow potential use in an aircraft gas turbine without coating.

End-of-life management of corrosive drywall.

PubMed

Kim, Hwidong; Krause, Max J; Townsend, Timothy

2016-11-01

Recently, gypsum drywall products imported to the United States (US) were found to cause metal corrosion and tarnishing in some homes, often necessitating that this drywall be discarded. Research assessed the potential implications of recycling and landfilling corrosive/imported drywall. Samples of corrosive drywall were collected from homes in Florida, US and these characteristics were assessed relative to domestically-produced drywall purchased from retail outlets. The total and synthetic precipitation leaching procedure (SPLP) leachable heavy metal concentrations were measured and compared to risk-based regulatory thresholds to assess the possible land application risk. In a majority of samples, concentrations were below levels of regulatory concern. The mean concentration of several elements exceeded the thresholds in a few samples for the direct exposure assessment (As) and the groundwater leaching assessment (Al, B, Hg, Mn, Sr and V); but the results did not suggest that corrosive drywall would present a greater risk than domestic drywall. To assess landfilling concerns, the potential for sulfur gases emissions upon disposal was evaluated. Experiments indicated that corrosive drywall would not pose a greater risk of long-term H2S emissions compared to domestic drywall. Copyright © 2016 Elsevier Ltd. All rights reserved.

Study on Corrosion-induced Crack Initiation and Propagation of Sustaining Loaded RCbeams

NASA Astrophysics Data System (ADS)

Zhong, X. P.; Li, Y.; Yuan, C. B.; Yang, Z.; Chen, Y.

2018-05-01

For 13 pieces of reinforced concrete beams with HRB500 steel bars under long-term sustained loads, at time of corrosion-induced initial crack of concrete, and corrosion-induced crack widths of 0.3mm and 1mm, corrosion of steel bars and time-varying behavior of corrosion-induced crack width were studied by the ECWD (Electro-osmosis - constant Current – Wet and Dry cycles) accelerated corrosion method. The results show that when cover thickness was between 30 and 50mm,corrosion rates of steel bars were between 0.8% and 1.7% at time of corrosion-induced crack, and decreased with increasing concrete cover thickness; when corrosion-induced crack width was 0.3mm, the corrosion rate decreased with increasing steel bar diameter, and increased with increasing cover thickness; its corrosion rate varied between 0.98% and 4.54%; when corrosion-induced crack width reached 1mm, corrosion rate of steel bars was between 4% and 4.5%; when corrosion rate of steel bars was within 5%, the maximum and average corrosion-induced crack and corrosion rate of steel bars had a good linear relationship. The calculation model predicting the maximum and average width of corrosion-induced crack is given in this paper.

Electrophoretic deposition of colloidal particles on Mg with cytocompatibility, antibacterial performance, and corrosion resistance.

PubMed

Sun, Jiadi; Zhu, Ye; Meng, Long; Chen, Peng; Shi, Tiantian; Liu, Xiaoya; Zheng, Yufeng

2016-11-01

Magnesium (Mg) has recently received increasing attention due to its unique biological performance, including cytocompatibility, antibacterial and biodegradable properties. However, rapid corrosion in physiological environment and potential toxicity limits its clinical applications. To improve the corrosion resistance meanwhile not compromise other excellent performance, self-assembled colloidal particles were deposited onto magnesium surfaces in ethanol by a simple and effective electrophoretic deposition (EPD) method. The fabricated functional nanostructured coatings were investigated using Fourier transform infrared spectroscopy (FTIR), X-ray diffraction (XRD) analyses, and scanning electron microscopy (SEM). The electrochemical test, pH value, and Mg ion concentration data show that the corrosion resistance of Mg samples is enhanced appreciably after surface treatment. In vitro cellular response and antibacterial capability of the modified Mg substrates are performed. Significantly increased cell adhesion and viability are observed from the coated Mg samples, and the amounts of adherent bacteria on the treated Mg surfaces diminish remarkably compared to the bare Mg. Furthermore, the bare and coated Mg samples were implanted in New Zealand white rabbits for 12 weeks to examine the in vivo long-term corrosion performance and in situ inflammation behavior. The experiment results confirmed that compared with bare Mg substrate the corrosion and foreign-body reactions of the coated Mg samples were suppressed. The above results suggested that our coatings, which effectively enhance the biocompatibility, antimicrobial properties, and corrosion resistance of Mg substrate, provide a simple and practical strategy to expedite clinical acceptance of biodegradableMg and its alloys. Biomedical Mg metals have been considered as promising biodegradable implants because of their intended functions, such as cytocompatibility, antibacterial, and biodegradable properties. However, rapid corrosion in physiological environment limits their clinical applications. Alloying and surface coatings have been used to reduce the degradation rate. But this would compromise other excellent performance of Mg samples, including antibacterial and anti-inflammatory activity. Thus, while the rapid degradation of Mg samples must be solved, good antibacterial property and acceptable cytocompatibility are also necessary. In this study, polymer-based coatings were fabricated on Mg surfaces by electrophoretic deposition of poly(isobornyl acrylate-co-dimethylaminoethyl methacrylate)/tannic acid (P(ISA-co-DMA)/TA) colloidal particles. It suggested that the coating materials effectively improved the biocompatibility, antimicrobial behavior, and corrosion resistance of biomedical Mg. Copyright © 2016 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

High-temperature fireside corrosion monitoring in the superheater section of a pulverized-coal-fired boiler. Final report

DOE Office of Scientific and Technical Information (OSTI.GOV)

Mok, W.Y.; Cox, W.M.

1992-12-01

The work described in this report was the first British in-plant application of continuous online electrochemical corrosion monitoring technology in pulverized coal-fired superheater environments. The work was conducted at Drax Power Station, National Power plc, UK. The investigation was to evaluate the relative corrosion performance of stainless steel Alloys 316 and 310. Two electrochemical sensor assemblies fabricated from the test alloys were attached to the end of a coupon exposure probe which was inserted into the superheater section of a 660MW boiler. The probe assemblies were exposed at a nominal temperature of 665{degrees}C (1229{degrees}F) during the trial. two series ofmore » short term temperature scanning tests were carried out. Alloy 310 performed comparatively better than Alloy 316. Minimal corrosion loss was sustained by Alloy 310 whilst a characteristic wastage flat was observed on Alloy 316. It was shown that variations in boiler operation could affect the minute-to-minute corrosion behavior of the test materials. The results of the brief temperature scan program indicated a trend of increasing corrosion with exposure temperature. No evidence was observed of the ``bell-shaped`` curve behavior reported in laboratory studies of molten salt corrosion. Metallographic examination of the sensors indicated that only small and discrete areas of internal sulfur enrichment beneath the surface scale. This is untypical of the morphology of sulfur enriched scale found in molten salt corrosion systems. The corrosion processes were predominately in the form of oxidation/sulfidation. The formation of a wastage flat was postulated to have been caused by an electrochemical mechanism similar to that of flow assisted corrosion in aqueous electrolytes. These results confirmed that continuous on-line electrochemical instrumentation could be used to investigate, monitor and characterize high temperature oxidation in power generation boiler superheaters.« less

High-temperature fireside corrosion monitoring in the superheater section of a pulverized-coal-fired boiler

DOE Office of Scientific and Technical Information (OSTI.GOV)

Mok, W.Y.; Cox, W.M.

1992-12-01

The work described in this report was the first British in-plant application of continuous online electrochemical corrosion monitoring technology in pulverized coal-fired superheater environments. The work was conducted at Drax Power Station, National Power plc, UK. The investigation was to evaluate the relative corrosion performance of stainless steel Alloys 316 and 310. Two electrochemical sensor assemblies fabricated from the test alloys were attached to the end of a coupon exposure probe which was inserted into the superheater section of a 660MW boiler. The probe assemblies were exposed at a nominal temperature of 665[degrees]C (1229[degrees]F) during the trial. two series ofmore » short term temperature scanning tests were carried out. Alloy 310 performed comparatively better than Alloy 316. Minimal corrosion loss was sustained by Alloy 310 whilst a characteristic wastage flat was observed on Alloy 316. It was shown that variations in boiler operation could affect the minute-to-minute corrosion behavior of the test materials. The results of the brief temperature scan program indicated a trend of increasing corrosion with exposure temperature. No evidence was observed of the bell-shaped'' curve behavior reported in laboratory studies of molten salt corrosion. Metallographic examination of the sensors indicated that only small and discrete areas of internal sulfur enrichment beneath the surface scale. This is untypical of the morphology of sulfur enriched scale found in molten salt corrosion systems. The corrosion processes were predominately in the form of oxidation/sulfidation. The formation of a wastage flat was postulated to have been caused by an electrochemical mechanism similar to that of flow assisted corrosion in aqueous electrolytes. These results confirmed that continuous on-line electrochemical instrumentation could be used to investigate, monitor and characterize high temperature oxidation in power generation boiler superheaters.« less

In Vivo and In Vitro Nitinol Corrosion Properties

NASA Astrophysics Data System (ADS)

Lonn, Melissa K.; Metcalf, Justin M.; Choules, Brian D.

2015-09-01

Regulatory authorities often require in vitro testing on medical devices prior to approval. Current standardized corrosion testing methods (ASTM F2129) require testing in a non-physiologic, de-oxygenated solution for a pre-exposure time of ≤1 h; however, no correlations between the prescribed simulated environment and whole blood conditions have been elucidated. This study compared open circuit potential (OCP), breakdown potentials (Eb), Eb - OCP, and cyclic polarization curves tested in vivo (OCP only) and in vitro in whole blood to those tested in phosphate-buffered saline (PBS). Two oxide thicknesses of Nitinol, two solution oxygen contents (deaerated and aerated solutions), and two pre-exposure durations (acute and chronic) were investigated. The in vitro OCP in whole blood was not significantly different than the in vivo OCP, suggesting that whole blood in vitro can be used to determine baseline corrosion behavior of medical implants. Eb - OCP tested per ASTM F2129 was comparable to acute whole blood and was conservative compared to chronic whole blood for both oxide thicknesses. However, OCP, Eb, and cyclic polarization curves were not always comparable to whole blood. Testing in aerated PBS achieved Eb, Eb - OCP, and cyclic polarization curves that were comparable to or more conservative than whole blood testing, regardless of pre-exposure duration and oxide thickness.

Evaluating Rebar Corrosion Using Nonlinear Ultrasound

NASA Astrophysics Data System (ADS)

Woodward, Clinton; Amin, Md. Nurul

2008-02-01

The early detection of rebar corrosion in reinforced concrete is difficult using current methods. This pilot study investigated the viability of using nonlinear ultrasound to detect the effects of rebar corrosion in its early stages. The study utilized three accelerated corrosion specimens and one control specimen. Results showed that when corrosion developed in the area isonified by a Rayleigh wave, nonlinear parameters increased. As corrosion progressed, these nonlinear parameters also increased.

Influence of MC3T3-E1 preosteoblast culture on the corrosion of a T6-treated AZ91 alloy

PubMed Central

Brooks, Emily K.; Tobias, Menachem E.; Yang, Shuying; Bone, Lawrence B.; Ehrensberger, Mark T.

2015-01-01

This study investigated the corrosion of artificially aged T6 heat-treated Mg-9%Al-1%Zn (AZ91) for biomedical applications. Corrosion tests and surface analysis were completed both with and without a monolayer of mouse preosteoblast MC3T3-E1 cells cultured on the sample. Electrochemical impedance spectroscopy (EIS) and inductively coupled plasma mass spectroscopy (ICPMS) were used to explore the corrosion processes after either 3 or 21 days of AZ91 incubation in cell culture medium (CCM). The EIS showed both the inner layer resistance (Rin) and outer layer resistance (Rout) were lower for samples without cells cultured on the surface at 3 days (Rin = 2.64 e4 Ω/cm2, Rout = 140 Ω/cm2) compared to 21 days (Rin = 3.60 e4 Ω/cm2, Rout = 287 Ω/cm2) due to precipitation of magnesium and calcium phosphates over time. Samples with preosteoblasts cultured on the surface had a slower initial corrosion (3 day, Rin = 1.88 e5 Ω/cm2, Rout = 1060 Ω/cm2) which was observed to increase over time (21 day, Rin = 2.99 e4 Ω/cm2, Rout = 287 Ω/cm2). Changes in the corrosion processes were thought to be related to changes in the coverage provided by the cell layer. Our results reveal that the presence of cells and biological processes are able to significantly influence the corrosion rate of AZ91. PMID:25715925

The influence of loading on the corrosion of steel in cracked ordinary Portland cement and high performance concretes

NASA Astrophysics Data System (ADS)

Jaffer, Shahzma Jafferali

Most studies that have examined chloride-induced corrosion of steel in concrete have focused on sound concrete. However, reinforced concrete is seldom uncracked and very few studies have investigated the influence of cracked concrete on rebar corrosion. Furthermore, the studies that have examined the relationship between cracks and corrosion have focused on unloaded or statically loaded cracks. However, in practice, reinforced concrete structures (e.g. bridges) are often dynamically loaded. Hence, the cracks in such structures open and close which could influence the corrosion of the reinforcing steel. Consequently, the objectives of this project were (i) to examine the effect of different types of loading on the corrosion of reinforcing steel, (ii) the influence of concrete mixture design on the corrosion behaviour and (iii) to provide data that can be used in service-life modelling of cracked reinforced concretes. In this project, cracked reinforced concrete beams made with ordinary Portland cement concrete (OPCC) and high performance concrete (HPC) were subjected to no load, static loading and dynamic loading. They were immersed in salt solution to just above the crack level at their mid-point for two weeks out of every four (wet cycle) and, for the remaining two weeks, were left in ambient laboratory conditions to dry (dry cycle). The wet cycle led to three conditions of exposure for each beam: (i) the non-submerged region, (ii) the sound, submerged region and (iii) the cracked mid-section, which was also immersed in the solution. Linear polarization resistance and galvanostatic pulse techniques were used to monitor the corrosion in the three regions. Potentiodynamic polarization, electrochemical current noise and concrete electrical resistance measurements were also performed. These measurements illustrated that (i) rebar corroded faster at cracks than in sound concrete, (ii) HPC was more protective towards the rebar than OPCC even at cracks and (iii) there was a minor effect of the type of loading on rebar corrosion within the period of the project. These measurements also highlighted the problems associated with corrosion measurements, for example, identifying the actual corroding area and the influence of the length of rebar. The numbers of cracks and crack-widths in each beam were measured after the beam's initial exposure to salt solution and, again, after the final corrosion measurements. HPC beams had more cracks than the OPCC. Also, final measurements illustrated increased crack-widths in dynamically loaded beams, regardless of the concrete type. The cracks in both statically and dynamically loaded OPCC and HPC beams bifurcated at the rebar level and propagated parallel to the rebar. This project also examined the extent of corrosion on the rebars and the distribution of corrosion products in the concrete and on the concrete walls of the cracks. Corrosion occurred only at cracks in the concrete and was spread over a larger area on the rebars in HPC than those in OPCC. The damage due to corrosion was superficial in HPC and crater-like in OPCC. Regardless of the concrete type, there was a larger distribution of corrosion products on the crack walls of the dynamically loaded beams. Corrosion products diffused into the cement paste and the paste-aggregate interface in OPCC but remained in the crack in HPC. The most voluminous corrosion product identified was ferric hydroxide. Elemental analysis of mill-scale on rebar which was not embedded in concrete or exposed to chlorides was compared to that of the bars that had been embedded in uncontaminated concrete and in cracked concrete exposed to chlorides. In uncontaminated concrete, mill-scale absorbed calcium and silicon. At a crack, a layer, composed of a mixture of cement paste and corrosion products, developed between the mill-scale and the substrate steel. Based on the results, it was concluded that (i) corrosion occurred on the rebar only at cracks in the concrete, (ii) corrosion was initiated at the cracks immediately upon exposure to salt solution, (ii) the type of loading had a minor influence on the corrosion rates of reinforcing steel and (iv) the use of polarized area led to a significant underestimation of the current density at the crack. It is recommended that the effect of cover-depth on (i) the time to initiation of corrosion and (ii) the corrosion current density in cracked concrete be investigated.

Corrosion resistance of high-Cr oxide dispersion strengthened ferritic steels in super-critical pressurized water

NASA Astrophysics Data System (ADS)

Cho, H. S.; Kimura, A.

2007-08-01

The effects of alloying elements, such as Cr and Al, on corrosion resistance in super critical pressurized water (SCPW) have been investigated to develop corrosion resistant oxide-dispersion-strengthened (ODS) steels. Corrosion tests were performed in a SCPW (783 K, 25 MPa) environment. Weight gain was measured after exposure to the SCPW, and then oxide layers were analyzed by low angle X-ray diffraction and SEM microscopy. The weight gains of all high-Cr ODS steels are smaller than an austenitic stainless steel (SUS316L). More uniform and thinner oxidation layers were observed on the ODS steels after corrosion compared to those on 9Cr martensitic steel and SUS316L.

Improvement of diamond-like carbon electrochemical corrosion resistance by addition of nanocrystalline diamond.

PubMed

Marciano, F R; Almeida, E C; Bonetti, L F; Corat, E J; Trava-Airoldi, V J

2010-02-15

Nanocrystalline diamond (NCD) particles were incorporated into diamond-like carbon (DLC) films in order to investigate NCD-DLC electrochemical corrosion resistance. The films were grown over 304 stainless steel using plasma-enhanced chemical vapor deposition. NCD particles were incorporated into DLC during the deposition process. The investigation of NCD-DLC electrochemical corrosion behavior was performed using potentiodynamic polarization against NaCl. NCD-DLC films presented more negative corrosion potential and lower anodic and cathodic current densities. The electrochemical analysis indicated that NCD-DLC films present superior impedance and polarization resistance compared to the pure DLC, which indicate that they are promising corrosion protective coatings in aggressive solutions. Copyright 2009 Elsevier Inc. All rights reserved.

Effect of polishing process on corrosion behavior of 308L stainless steel in high temperature water

NASA Astrophysics Data System (ADS)

Ma, Cheng; Han, En-Hou; Peng, Qunjia; Ke, Wei

2018-06-01

Effect of change in surface composition and roughness by different polishing processes on corrosion of 308L stainless steel in high temperature water was investigated. The investigation was conducted by comparing the corrosion behavior of electropolished specimens with that of the 40 nm-colloidal silica slurry polished specimens. The result revealed that the electropolished specimens had a higher corrosion rate than the colloidal silica slurry polished specimens, which was attributed to formation of an amount of chromium hydroxide and higher roughness of the electropolished surface. Moreover, the ferrite in 308L stainless steel was found to have a higher resistance to corrosion than the austenite matrix.

Polarized Neutron Reflectometry of Nickel Corrosion Inhibitors.

PubMed

Wood, Mary H; Welbourn, Rebecca J L; Zarbakhsh, Ali; Gutfreund, Philipp; Clarke, Stuart M

2015-06-30

Polarized neutron reflectometry has been used to investigate the detailed adsorption behavior and corrosion inhibition mechanism of two surfactants on a nickel surface under acidic conditions. Both the corrosion of the nickel surface and the structure of the adsorbed surfactant layer could be monitored in situ by the use of different solvent contrasts. Layer thicknesses and roughnesses were evaluated over a range of pH values, showing distinctly the superior corrosion inhibition of one negatively charged surfactant (sodium dodecyl sulfate) compared to a positively charged example (dodecyl trimethylammonium bromide) due to its stronger binding interaction with the surface. It was found that adequate corrosion inhibition occurs at significantly less than full surface coverage.

A Comparative Biocompatibility Analysis of Ternary Nitinol Alloys

PubMed Central

Haider, Waseem; Munroe, Norman; Pulletikurthi, Chandan; Singh Gill, Puneet K.; Amruthaluri, Sushma

2009-01-01

Nitinol alloys are rapidly being utilized as the material of choice in a variety of applications in the medical industry. It has been used for self-expanding stents, graft support systems, and various other devices for minimally invasive interventional and endoscopic procedures. However, the biocompatibility of this alloy remains a concern to many practitioners in the industry due to nickel sensitivity experienced by many patients. In recent times, several new Nitinol alloys have been introduced with the addition of a ternary element. Nevertheless, there is still a dearth of information concerning the biocompatibility and corrosion resistance of these alloys. This study compared the biocompatibility of two ternary Nitinol alloys prepared by powder metallurgy (PM) and arc melting (AM) and critically assessed the influence of the ternary element. ASTM F 2129-08 cyclic polarization in vitro corrosion tests were conducted to evaluate the corrosion resistance in phosphate buffered saline (PBS). The growth of endothelial cells on NiTi was examined using optical microscopy. PMID:19956791

A Comparative Biocompatibility Analysis of Ternary Nitinol Alloys

NASA Astrophysics Data System (ADS)

Haider, Waseem; Munroe, Norman; Pulletikurthi, Chandan; Gill, Puneet K. Singh; Amruthaluri, Sushma

2009-08-01

Nitinol alloys are rapidly being utilized as the material of choice in a variety of applications in the medical industry. It has been used for self-expanding stents, graft support systems, and various other devices for minimally invasive interventional and endoscopic procedures. However, the biocompatibility of this alloy remains a concern to many practitioners in the industry due to nickel sensitivity experienced by many patients. In recent times, several new Nitinol alloys have been introduced with the addition of a ternary element. Nevertheless, there is still a dearth of information concerning the biocompatibility and corrosion resistance of these alloys. This study compared the biocompatibility of two ternary Nitinol alloys prepared by powder metallurgy (PM) and arc melting (AM) and critically assessed the influence of the ternary element. ASTM F 2129-08 cyclic polarization in vitro corrosion tests were conducted to evaluate the corrosion resistance in phosphate buffered saline (PBS). The growth of endothelial cells on NiTi was examined using optical microscopy.

A Comparative Biocompatibility Analysis of Ternary Nitinol Alloys.

PubMed

Haider, Waseem; Munroe, Norman; Pulletikurthi, Chandan; Singh Gill, Puneet K; Amruthaluri, Sushma

2009-08-01

Nitinol alloys are rapidly being utilized as the material of choice in a variety of applications in the medical industry. It has been used for self-expanding stents, graft support systems, and various other devices for minimally invasive interventional and endoscopic procedures. However, the biocompatibility of this alloy remains a concern to many practitioners in the industry due to nickel sensitivity experienced by many patients. In recent times, several new Nitinol alloys have been introduced with the addition of a ternary element. Nevertheless, there is still a dearth of information concerning the biocompatibility and corrosion resistance of these alloys. This study compared the biocompatibility of two ternary Nitinol alloys prepared by powder metallurgy (PM) and arc melting (AM) and critically assessed the influence of the ternary element. ASTM F 2129-08 cyclic polarization in vitro corrosion tests were conducted to evaluate the corrosion resistance in phosphate buffered saline (PBS). The growth of endothelial cells on NiTi was examined using optical microscopy.

Corrosion Studies of 2195 Al-Li Alloy and 2219 Al Alloy with Differing Surface Treatments

NASA Technical Reports Server (NTRS)

Danford, M. D.; Mendrek, M. J.

1998-01-01

Corrosion studies of 2195 Al-Li and 2219 Al alloys have been conducted using the scanning reference electrode technique (SRET) and the polarization resistance (PR) technique. The SRET was used to study corrosion mechanisms, while corrosion rate measurements were studied with the PR technique. Plates of Al203 blasted, soda blasted and conversion coated 2219 Al were coated with Deft primer and the corrosion rates studied with the EIS technique. Results from all of these studies are presented.

Experimental Study on Rebar Corrosion Using the Galvanic Sensor Combined with the Electronic Resistance Technique

PubMed Central

Xu, Yunze; Li, Kaiqiang; Liu, Liang; Yang, Lujia; Wang, Xiaona; Huang, Yi

2016-01-01

In this paper, a new kind of carbon steel (CS) and stainless steel (SS) galvanic sensor system was developed for the study of rebar corrosion in different pore solution conditions. Through the special design of the CS and SS electronic coupons, the electronic resistance (ER) method and zero resistance ammeter (ZRA) technique were used simultaneously for the measurement of both the galvanic current and the corrosion depth. The corrosion processes in different solution conditions were also studied by linear polarization resistance (LPR) and the measurements of polarization curves. The test result shows that the galvanic current noise can provide detailed information of the corrosion processes. When localized corrosion occurs, the corrosion rate measured by the ER method is lower than the real corrosion rate. However, the value measured by the LPR method is higher than the real corrosion rate. The galvanic current and the corrosion current measured by the LPR method shows linear correlation in chloride-containing saturated Ca(OH)2 solution. The relationship between the corrosion current differences measured by the CS electronic coupons and the galvanic current between the CS and SS electronic coupons can also be used to evaluate the localized corrosion in reinforced concrete. PMID:27618054

Experimental Study on Rebar Corrosion Using the Galvanic Sensor Combined with the Electronic Resistance Technique.

PubMed

Xu, Yunze; Li, Kaiqiang; Liu, Liang; Yang, Lujia; Wang, Xiaona; Huang, Yi

2016-09-08

In this paper, a new kind of carbon steel (CS) and stainless steel (SS) galvanic sensor system was developed for the study of rebar corrosion in different pore solution conditions. Through the special design of the CS and SS electronic coupons, the electronic resistance (ER) method and zero resistance ammeter (ZRA) technique were used simultaneously for the measurement of both the galvanic current and the corrosion depth. The corrosion processes in different solution conditions were also studied by linear polarization resistance (LPR) and the measurements of polarization curves. The test result shows that the galvanic current noise can provide detailed information of the corrosion processes. When localized corrosion occurs, the corrosion rate measured by the ER method is lower than the real corrosion rate. However, the value measured by the LPR method is higher than the real corrosion rate. The galvanic current and the corrosion current measured by the LPR method shows linear correlation in chloride-containing saturated Ca(OH)₂ solution. The relationship between the corrosion current differences measured by the CS electronic coupons and the galvanic current between the CS and SS electronic coupons can also be used to evaluate the localized corrosion in reinforced concrete.

Study of development and utilization of a multipurpose atmospheric corrosion sensor

NASA Technical Reports Server (NTRS)

Diwan, Ravinder M.; Raman, A.; Bhattacharya, P. K.

1994-01-01

There has been a critical need for analyzing various aspects of atmospheric corrosion and for the development of atmospheric corrosion microsensors. The project work has involved the following activities: (1) making of multielectrode corrosion monitors on dielectric substrates; (2) testing them in the laboratory for functional characteristics; (3) preparing a report on the state of the art of atmospheric corrosion sensor development around the world; and (4) corrosion testing of electrochemical changes of sensor specimens and related fog testing. The study included work on the subject of development and utilization of a multipurpose atmospheric corrosion sensor and this report is the annual report on work carried out on this research project. This has included studies on the development of sensors of two designs, stage 1 and stage 2, and with glass and alumina substrate, experimentation and development and characterization of the coating uniformity, aspects of corrosion monitoring, literature search on the corrosion sensors and their development. A state of the art report on atmospheric corrosion sensor development was prepared and submitted.

On the properties of two binary NiTi shape memory alloys. Effects of surface finish on the corrosion behaviour and in vitro biocompatibility.

PubMed

Es-Souni, Mohammed; Es-Souni, Martha; Fischer-Brandies, Helge

2002-07-01

The present paper compares the transformation behaviour and mechanical properties of two orthodontic wires of close chemical compositions. The effects of surface topography and surface finish residues on the potentiodynamic corrosion behaviour and biocompatibility are also reported. The cytotoxicity tests were performed on both alloys in fibroblast cell cultures from human gingiva using the MTT test. It is shown that the surface finish and the amounts of surface finish residues affect dramatically the corrosion resistance. Bad surface finish results in lower corrosion resistance. The in vitro biocompatibility, though not affected to the extent of corrosion resistance, is also reduced as the surface roughness and the amounts of residues increase. This is thought to be due to surface effects on corrosion and metallic ions release.

Temperature factors effect on occurrence of stress corrosion cracking of main gas pipeline

NASA Astrophysics Data System (ADS)

Nazarova, M. N.; Akhmetov, R. R.; Krainov, S. A.

2017-10-01

The purpose of the article is to analyze and compare the data in order to contribute to the formation of an objective opinion on the issue of the growth of stress corrosion defects of the main gas pipeline. According to available data, a histogram of the dependence of defects due to stress corrosion on the distance from the compressor station was constructed, and graphs of the dependence of the accident density due to stress corrosion in the winter and summer were also plotted. Data on activation energy were collected and analyzed in which occurrence of stress corrosion is most likely constructed, a plot of activation energy versus temperature is plotted, and the process of occurrence of stress corrosion by the example of two different grades of steels under the action of different temperatures was analyzed.

Management and control of microbiologically influenced corrosion (MIC) in the oil and gas industry-Overview and a North Sea case study.

PubMed

Skovhus, Torben Lund; Eckert, Richard B; Rodrigues, Edgar

2017-08-20

Microbiologically influenced corrosion (MIC) is the terminology applied where the actions of microorganisms influence the corrosion process. In literature, terms such as microbial corrosion, biocorrosion, microbially influenced/induced corrosion, and biodegradation are often applied. MIC research in the oil and gas industry has seen a revolution over the past decade, with the introduction of molecular microbiological methods: (MMM) as well as new industry standards and procedures of sampling biofilm and corrosion products from the process system. This review aims to capture the most important trends the oil and gas industry has seen regarding MIC research over the past decade. The paper starts out with an overview of where in the process stream MIC occurs - from the oil reservoir to the consumer. Both biotic and abiotic corrosion mechanisms are explained in the context of managing MIC using a structured corrosion management (CM) approach. The corrosion management approach employs the elements of a management system to ensure that essential corrosion control activities are carried out in an effective, sustainable, well-planned and properly executed manner. The 3-phase corrosion management approach covering of both biotic and abiotic internal corrosion mechanisms consists of 1) corrosion assessment, 2) corrosion mitigation and 3) corrosion monitoring. Each of the three phases are described in detail with links to recent field cases, methods, industry standards and sampling protocols. In order to manage the corrosion threat, operators commonly use models to support decision making. The models use qualitative, semi-quantitative or quantitative measures to help assess the rate of degradation caused by MIC. The paper reviews four existing models for MIC Threat Assessment and describe a new model that links the threat of MIC in the oil processing system located on an offshore platform with a Risk Based Inspection (RBI) approach. A recent field case highlights and explains the conflicting historic results obtained through serial dilution of culture media using the most probable number (MPN) method as compared to data obtained from corrosion monitoring and the quantitative polymerase chain reaction (qPCR) method. Results from qPCR application in the field case have changed the way MIC is monitored on the oil production facility in the North Sea. A number of high quality resources have been published as technical conference papers, books, educational videos and peer-reviewed scientific papers, and thus we end the review with an updated list of state-of-the-art resources for anyone desiring to become more familiar with the topic of MIC in the upstream oil and gas sector. Copyright © 2017 Elsevier B.V. All rights reserved.

The importance of extracellular speciation and corrosion of copper nanoparticles on lung cell membrane integrity.

PubMed

Hedberg, Jonas; Karlsson, Hanna L; Hedberg, Yolanda; Blomberg, Eva; Odnevall Wallinder, Inger

2016-05-01

Copper nanoparticles (Cu NPs) are increasingly used in various biologically relevant applications and products, e.g., due to their antimicrobial and catalytic properties. This inevitably demands for an improved understanding on their interactions and potential toxic effects on humans. The aim of this study was to investigate the corrosion of copper nanoparticles in various biological media and to elucidate the speciation of released copper in solution. Furthermore, reactive oxygen species (ROS) generation and lung cell (A549 type II) membrane damage induced by Cu NPs in the various media were studied. The used biological media of different complexity are of relevance for nanotoxicological studies: Dulbecco's modified eagle medium (DMEM), DMEM(+) (includes fetal bovine serum), phosphate buffered saline (PBS), and PBS+histidine. The results show that both copper release and corrosion are enhanced in DMEM(+), DMEM, and PBS+histidine compared with PBS alone. Speciation results show that essentially no free copper ions are present in the released fraction of Cu NPs in neither DMEM(+), DMEM nor histidine, while labile Cu complexes form in PBS. The Cu NPs were substantially more membrane reactive in PBS compared to the other media and the NPs caused larger effects compared to the same mass of Cu ions. Similarly, the Cu NPs caused much more ROS generation compared to the released fraction only. Taken together, the results suggest that membrane damage and ROS formation are stronger induced by Cu NPs and by free or labile Cu ions/complexes compared with Cu bound to biomolecules. Copyright © 2016 The Authors. Published by Elsevier B.V. All rights reserved.

Erosion-corrosion resistance properties of 316L austenitic stainless steels after low-temperature liquid nitriding

NASA Astrophysics Data System (ADS)

Zhang, Xiangfeng; Wang, Jun; Fan, Hongyuan; Pan, Dong

2018-05-01

The low-temperature liquid nitriding of stainless steels can result in the formation of a surface zone of so-called expanded austenite (S-phase) by the dissolution of large amounts of nitrogen in the solid solution and formation of a precipitate-free layer supersaturated with high hardness. Erosion-corrosion measurements were performed on low-temperature nitrided and non-nitrided 316L stainless steels. The total erosion-corrosion, erosion-only, and corrosion-only wastages were measured directly. As expected, it was shown that low-temperature nitriding dramatically reduces the degree of erosion-corrosion in stainless steels, caused by the impingement of particles in a corrosive medium. The nitrided 316L stainless steels exhibited an improvement of almost 84% in the erosion-corrosion resistance compared to their non-nitrided counterparts. The erosion-only rates and synergistic levels showed a general decline after low-temperature nitriding. Low-temperature liquid nitriding can not only reduce the weight loss due to erosion but also significantly reduce the weight loss rate of interactions, so that the total loss of material decreased evidently. Therefore, 316L stainless steels displayed excellent erosion-corrosion behaviors as a consequence of their highly favorable corrosion resistances and superior wear properties.

Influence of reactive fillers on concrete corrosion resistance

NASA Astrophysics Data System (ADS)

Rakhimbayev, Sh M.; Tolypina, N. M.; Khakhaleva, E. N.

2018-03-01

Contact surfaces represent the weakest link in a conglomerate structure of materials. They ensure the diffusion of aggressive agents inside the material. To reduce the conductivity of contact surfaces it is advisable to use reactive fillers, which interact with cement matrix via certain mechanisms, which in turn, reduces the permeability of the contact layer and fosters durability of products. The interaction of reactive fillers with calcium hydroxide of a concrete liquid phase in a contact area leads to the formation of hydrated calcium silicates of a tobermorite group. Such compounds, being settled in pores and capillaries of a product, colmatage and clog them to some extent thus leading to diffusion delay (inhibition) with regard to aggressive components of external media inside porous material, which in turn inhibits the corrosion rate. The authors studied and compared the corrosion of cement concrete with a standard filler (quartz sand) and a reactive filler (perlite and urtit). The experiments confirmed the positive influence of active fillers on concrete corrosion resistance.

RGDC Peptide-Induced Biomimetic Calcium Phosphate Coating Formed on AZ31 Magnesium Alloy

PubMed Central

Cao, Lin; Wang, Lina; Fan, Lingying; Xiao, Wenjun; Lin, Bingpeng; Xu, Yimeng; Liang, Jun; Cao, Baocheng

2017-01-01

Magnesium alloys as biodegradable metal implants have received a lot of interest in biomedical applications. However, magnesium alloys have extremely high corrosion rates a in physiological environment, which have limited their application in the orthopedic field. In this study, calcium phosphate compounds (Ca–P) coating was prepared by arginine–glycine–aspartic acid–cysteine (RGDC) peptide-induced mineralization in 1.5 simulated body fluid (SBF) to improve the corrosion resistance and biocompatibility of the AZ31 magnesium alloys. The adhesion of Ca–P coating to the AZ31 substrates was evaluated by a scratch test. Corrosion resistance and cytocompatibility of the Ca–P coating were investigated. The results showed that the RGDC could effectively promote the nucleation and crystallization of the Ca–P coating and the Ca–P coating had poor adhesion to the AZ31 substrates. The corrosion resistance and biocompatibility of the biomimetic Ca–P coating Mg alloys were greatly improved compared with that of the uncoated sample. PMID:28772717

The Effect of Corrosion on the Seismic Behavior of Buried Pipelines and a Remedy for Their Seismic Retrofit

NASA Astrophysics Data System (ADS)

Hosseini, Mahmood; Salek, Shamila; Moradi, Masoud

2008-07-01

The effect of corrosion phenomenon has been investigated by performing some sets of 3-Dimensional Nonlinear Time History Analysis (3-D NLTHA) in which soil structure interaction as well as wave propagation effects have been taken into consideration. The 3-D NLTHA has been performed by using a finite element computer program, and both states of overall and local corrosions have been considered for the study. The corrosion has been modeled in the computer program by introducing decreased values of either pipe wall thickness or modulus of elasticity and Poisson ratio. Three sets of 3-component accelerograms have been used in analyses, and some appropriate numbers of zeros have been added at the beginning of records to take into account the wave propagation in soil and its multi-support excitation effect. The soil has been modeled by nonlinear springs in longitudinal, lateral, and vertical directions. A relatively long segment of the pipeline has been considered for the study and the effect of end conditions has been investigated by assuming different kinds end supports for the segment. After studying the corroded pipeline, a remedy has been considered for the seismic retrofit of corroded pipe by using a kind of Fiber Reinforced Polymers (FRP) cover. The analyses have been repeated for the retrofitted pipeline to realize the adequacy of FRP cover. Numerical results show that if the length of the pipeline segment is large enough, comparing to the wave length of shear wave in the soil, the end conditions do not have any major effect on the maximum stress and strain values in the pipe. Results also show that corrosion can lead to the increase in plastic strain values in the pipe up to 4 times in the case of overall corrosion and up to 20 times in the case of local corrosion. The satisfactory effect of using FRP cover is also shown by the analyses results, which confirm the decrease of strain values to 1/3.

Comparing the Methodologies in ASTM G198 Using Combined Hygrothermal-Corrosion Modeling

Treesearch

Samuel L. Zelinka

2013-01-01

ASTM G198, “Standard test method for determining the relative corrosion performance of driven fasteners in contact with treated wood,” was accepted by consensus and published in 2011. The method has two different exposure conditions for determining fastener corrosion performance in treated wood. The first method places the wood and embedded fasteners in a...

Development of Novel Fe-Based Coating Systems for Internal Combustion Engines

NASA Astrophysics Data System (ADS)

Bobzin, K.; Öte, M.; Königstein, T.; Dröder, K.; Hoffmeister, H.-W.; Mahlfeld, G.; Schläfer, T.

2018-04-01

Nowadays, combustion engines are the most common way to power vehicles. Thereby, losses occur due to cooling, exhaust gas and friction. With regard to frictional losses, highest potentials for optimization can be found in the tribological system of the inner surface of combustion chamber and piston ring. Besides friction, corrosive stress increases, e.g., due to utilization of exhaust gas recovery. In order to save energy, reduce emissions and enhance the life span of combustion engines, the demand for innovative coating material systems, especially for the inner surface of combustion chamber, increases. This study focuses on the development of innovative iron-based coating materials for the combustion chamber. As a first step, the plasma transferred wire arc and rotating single wire arc (RSW) technologies were compared using 0.8% C-steel as a reference. Subsequently, RSW was used for coating deposition using an innovative iron-based feedstock material. In order to improve wear and corrosion resistance, boron and chromium were added to the feedstock material. After deposition, different honing topographies were manufactured and compared under tribological load. Furthermore, electrochemical corrosion tests were conducted using an electrolyte simulating the exhaust gas concentrate. Especially with regard to corrosion, the novel coating system FeCrBMn showed promising results.

Exceptionally high cavitation erosion and corrosion resistance of a high entropy alloy.

PubMed

Nair, R B; Arora, H S; Mukherjee, Sundeep; Singh, S; Singh, H; Grewal, H S

2018-03-01

Cavitation erosion and corrosion of structural materials are serious concerns for marine and offshore industries. Durability and performance of marine components are severely impaired due to degradation from erosion and corrosion. Utilization of advanced structural materials can play a vital role in limiting such degradation. High entropy alloys (HEAs) are a relatively new class of advanced structural materials with exceptional properties. In the present work, we report on the cavitation erosion behavior of Al 0.1 CoCrFeNi HEA in two different media: distilled water with and without 3.5wt% NaCl. For comparison, conventionally used stainless steel SS316L was also evaluated in identical test conditions. Despite lower hardness and yield strength, the HEA showed significantly longer incubation period and lower erosion-corrosion rate (nearly 1/4th) compared to SS316L steel. Enhanced erosion resistance of HEA was attributed to its high work-hardening behavior and stable passivation film on the surface. The Al 0.1 CoCrFeNi HEA showed lower corrosion current density, high pitting resistance and protection potential compared to SS316L steel. Further, HEA showed no evidence of intergranular corrosion likely due to the absence of secondary precipitates. Although, the degradation mechanisms (formation of pits and fatigue cracks) were similar for both the materials, the damage severity was found to be much higher for SS316L steel compared to HEA. Copyright © 2017 Elsevier B.V. All rights reserved.

Comparing Monofractal and Multifractal Analysis of Corrosion Damage Evolution in Reinforcing Bars

PubMed Central

Xu, Yidong; Qian, Chunxiang; Pan, Lei; Wang, Bingbing; Lou, Chi

2012-01-01

Based on fractal theory and damage mechanics, the aim of this paper is to describe the monofractal and multifractal characteristics of corrosion morphology and develop a new approach to characterize the nonuniform corrosion degree of reinforcing bars. The relationship between fractal parameters and tensile strength of reinforcing bars are discussed. The results showed that corrosion mass loss ratio of a bar cannot accurately reflect the damage degree of the bar. The corrosion morphology of reinforcing bars exhibits both monofractal and multifractal features. The fractal dimension and the tensile strength of corroded steel bars exhibit a power function relationship, while the width of multifractal spectrum and tensile strength of corroded steel bars exhibit a linear relationship. By comparison, using width of multifractal spectrum as multifractal damage variable not only reflects the distribution of corrosion damage in reinforcing bars, but also reveals the influence of nonuniform corrosion on the mechanical properties of reinforcing bars. The present research provides a new approach for the establishment of corrosion damage constitutive models of reinforcing bars. PMID:22238682

Chloride-induced corrosion mechanism and rate of enamel- and epoxy-coated deformed steel bars embedded in mortar

DOE Office of Scientific and Technical Information (OSTI.GOV)

Tang, Fujian; Chen, Genda; Brow, Richard K.

The chloride-induced corrosion mechanisms of uncoated, pure enamel (PE)-coated, mixed enamel (ME)-coated, double enamel (DE)-coated, and fusion bonded epoxy (FBE)-coated deformed steel bars embedded in mortar cylinders are investigated in 3.5 wt.% NaCl solution and compared through electrochemical tests and visual inspection. Corrosion initiated after 29 or 61 days of tests in all uncoated and enamel-coated steel bars, and after 244 days of tests in some FBE-coated steel bars. In active stage, DE- and FBE-coated steel bars are subjected to the highest and lowest corrosion rates, respectively. The uncoated and ME-coated steel bars revealed relatively uniform corrosion while the PE-,more » DE-, and FBE-coated steel bars experienced pitting corrosion around damaged coating areas. Due to the combined effect of ion diffusion and capillary suction, wet–dry cyclic immersion caused more severe corrosion than continuous immersion. Both exposure conditions affected the corrosion rate more significantly than the water–cement ratio in mortar design.« less

Evaluation of Microstructure, Mechanical Properties and Corrosion Resistance of Friction Stir-Welded Aluminum and Magnesium Dissimilar Alloys

NASA Astrophysics Data System (ADS)

Verma, Jagesvar; Taiwade, Ravindra V.; Sapate, Sanjay G.; Patil, Awanikumar P.; Dhoble, Ashwinkumar S.

2017-10-01

Microstructure, mechanical properties and corrosion resistance of dissimilar friction stir-welded aluminum and magnesium alloys were investigated by applying three different rotational speeds at two different travel speeds. Sound joints were obtained in all the conditions. The microstructure was examined by an optical and scanning electron microscope, whereas localized chemical information was studied by energy-dispersive spectroscopy. Stir zone microstructure showed mixed bands of Al and Mg with coarse and fine equiaxed grains. Grain size of stir zone reduced compared to base metals, indicated by dynamic recrystallization. More Al patches were observed in the stir zone as rotational speed increased. X-ray diffraction showed the presence of intermetallics in the stir zone. Higher tensile strength and hardness were obtained at a high rotational speed corresponding to low travel speed. Tensile fractured surface indicated brittle nature of joints. Dissimilar friction stir weld joints showed different behaviors in different corrosive environments, and better corrosion resistance was observed at a high rotational speed corresponding to low travel speed (FW3) in a sulfuric and chloride environments. Increasing travel speed did not significantly affect on microstructure, mechanical properties and corrosion resistance as much as the rotational speed.

Measurement and simulation of millimeter wave scattering cross-sections from steel-reinforced concrete

NASA Astrophysics Data System (ADS)

Hassan, A. M.; Martys, N. S.; Garboczi, E. J.; McMichael, R. D.; Stiles, M. D.; Plusquellic, D. F.; Stutzman, P. E.; Wang, S.; Provenzano, V.; Surek, J. T.; Novotny, D. R.; Coder, J. B.; Janezic, M. D.; Kim, S.

2014-02-01

Some iron oxide corrosion products exhibit antiferromagnetic magnetic resonances (AFMR) at frequencies on the order of 100 GHz at ambient temperatures. AFMR can be detected in laboratory conditions, which serves as the basis for a new non-destructive spectroscopic method for detecting early corrosion. When attempting to measure the steel corrosion in reinforced concrete in the field, rebar geometry must be taken into account. Experiments and numerical simulations have been developed at frequencies near 100 GHz to sort out these effects. The experimental setup involves a vector network analyzer with converter heads to up-convert the output frequency, which is then connected to a horn antenna followed by a 7.5 cm diameter polymer lens to focus the waves on the sample. Two sets of samples were studied: uniform cylindrical rods and rebar corrosion samples broken out of concrete with different kinds of coatings. Electromagnetic scattering from uniform rods were calculated numerically using classical modal expansion. A finite-element electromagnetic solver was used to model more complex rebar geometry and non-uniform corrosion layers. Experimental and numerical data were compared to help quantify and understand the anticipated effect of local geometrical features on AFMR measurements.

Improving the tribological and corrosive properties of MoS2-based coatings by dual-doping and multilayer construction

NASA Astrophysics Data System (ADS)

Shang, Kedong; Zheng, Shaoxian; Ren, Siming; Pu, Jibin; He, Dongqing; Liu, Shuan

2018-04-01

The pure MoS2 coating always performs high friction coefficient and short service life when used in high humidity or after long-time storage in humid atmospheric environment. In this study, the MoS2/Pb-Ti composite and MoS2/Pb-Ti multilayer coatings are deposited to improve the corrosion resistance in 3.5 wt% NaCl solution and tribological performance in high humidity condition. The electrochemical impedance spectra and salt spray test shown that the MoS2/Pb-Ti composite and multilayer coatings can inhibit the permeation of oxygen and other corrosive elements, thus resulting a high corrosion resistance. Furthermore, compared with pure MoS2 coating, the tribological performance of the MoS2/Pb-Ti composite and multilayer coatings is also improved significantly owing to the high mechanical properties and compact structure. Moreover, the heterogenous interfaces in MoS2/Pb-Ti multilayer coating play an important role to improve the corrosion resistance and tribological performance of coatings. Overall, the dual-doping and multilayer construction are promising approaches to design the MoS2 coatings as the environmentally adaptive lubricants.

Inhibiting mild steel corrosion from sulfate-reducing bacteria using antimicrobial-producing biofilms in Three-Mile-Island process water.

PubMed

Zuo, R; Ornek, D; Syrett, B C; Green, R M; Hsu, C-H; Mansfeld, F B; Wood, T K

2004-04-01

Biofilms were used to produce gramicidin S (a cyclic decapeptide) to inhibit corrosion-causing, sulfate-reducing bacteria (SRB). In laboratory studies these biofilms protected mild steel 1010 continuously from corrosion in the aggressive, cooling service water of the AmerGen Three-Mile-Island (TMI) nuclear plant, which was augmented with reference SRB. The growth of both reference SRB (Gram-positive Desulfosporosinus orientis and Gram-negative Desulfovibrio vulgaris) was shown to be inhibited by supernatants of the gramicidin-S-producing bacteria as well as by purified gramicidin S. Electrochemical impedance spectroscopy and mass loss measurements showed that the protective biofilms decreased the corrosion rate of mild steel by 2- to 10-fold when challenged with the natural SRB of the TMI process water supplemented with D. orientis or D. vulgaris. The relative corrosion inhibition efficiency was 50-90% in continuous reactors, compared to a biofilm control which did not produce the antimicrobial gramicidin S. Scanning electron microscope and reactor images also revealed that SRB attack was thwarted by protective biofilms that secrete gramicidin S. A consortium of beneficial bacteria (GGPST consortium, producing gramicidin S and other antimicrobials) also protected the mild steel.

Survey of degradation modes of candidate materials for high-level radioactive-waste disposal containers

DOE Office of Scientific and Technical Information (OSTI.GOV)

Farmer, J.C.; Van Konynenburg, R.A.; McCright, R.D.

1988-04-01

Three iron- to nickel-based austenitic alloys (Types 304L and 316L stainless steels and Alloy 825) are being considered as candidate materials for the fabrication of high-level radioactive-waste containers. Waste will include fuel assemblies from reactors as well as high-level waste in borosilicate glass forms, and will be sent to the prospective repository at Yucca Mountain, Nevada. The decay of radionuclides in the repository will result in the generation of substantial heat and in fluences of gamma radiation. Container materials may undergo any of several modes of degradation in this environment, including atmospheric oxidation; uniform aqueous phase corrosion; pitting; crevice corrosion;more » sensitization and intergranular stress corrosion cracking (IGSCC); and transgranular stress corrosion cracking (TGSCC). This report is an analysis of data relevant to the pitting, crevice corrosion, and stress corrosion cracking (SCC) of the three austenitic candidate alloys. The candidates are compared in terms of their susceptibilities to these forms of corrosion. Although all three candidates have demonstrated pitting and crevice corrosion in chloride-containing environments, Alloy 825 has the greatest resistance to these types of localized corrosion (LC); such resistance is important because pits can penetrate the metal and serve as crack initiation sites. Both Types 304L and 316L stainless steels are susceptible to SCC in acidic chloride media. In contrast, SCC has not been documented in Alloy 825 under comparable conditions. Gamma radiation has been found to enhance SCC in Types 304 and 304L stainless steels, but it has no detectable effect on the resistance of Alloy 825 to SCC. Furthermore, while the effects of microbiologically induced corrosion have been observed for 300-series stainless steels, nickel-based alloys such as Alloy 825 seem to be immune to such problems. 211 refs., 49 figs., 10 tabs.« less

Studies of surface modified NiTi alloy

NASA Astrophysics Data System (ADS)

Shevchenko, N.; Pham, M.-T.; Maitz, M. F.

2004-07-01

A corrosion resistant and nickel free surface on NiTi (nitinol) for biomedical applications should be produced by ion implantation. Ar + and/or N + implantation in NiTi alloy was performed at energies of 20-40 keV and fluences of (3-5) × 10 17 cm -2 by means of plasma immersion ion implantation. The modification of the NiTi alloy and its biocompatibility properties were studied. The near surface layers were analysed by Auger electron spectroscopy (AES), grazing incidence X-ray diffraction (GIXRD) and cell culture tests, and electrochemical corrosion analysis of these layers was performed. A nickel depleted surface layer is produced by the implantation, which was sealed by the formation of TiN or Ti oxide layers at the different implantation regimes, respectively. No differences in biocompatibility were seen on the modified compared with the initial surfaces. The corrosion stability increased by this treatment.

A comparative study on the electrochemical corrosion behavior of iron and X-65 steel in 4.0 wt % sodium chloride solution after different exposure intervals.

PubMed

Sherif, El-Sayed M

2014-07-09

In this work, the results obtained from studying the anodic dissolution of pure iron and API X-65 5L pipeline steel after 40 min and 12 h exposure period in 4.0 wt % NaCl solutions at room temperature were reported. Potential-time, electrochemical impedance spectroscopy, potentiodynamic polarization, and chronoamperometric current-time at constant potential techniques were employed. It has been found that the iron electrode corrodes in the chloride test solutions faster than the API X-65 5L steel does under the same conditions. Increasing the exposure period for the electrodes from 40 min to 12 h showed a significant reduction in the corrosion parameters for both iron and steel in the 4.0 wt % NaCl solution. Results together confirmed clearly that the X-65 steel is superior to iron against corrosion in sodium chloride solutions.

Timescale Correlation between Marine Atmospheric Exposure and Accelerated Corrosion Testing - Part 2

NASA Technical Reports Server (NTRS)

Montgomery, Eliza L.; Calle, Luz Marina; Curran, Jerome C.; Kolody, Mark R.

2012-01-01

Evaluation of metals to predict service life of metal-based structures in corrosive environments has long relied on atmospheric exposure test sites. Traditional accelerated corrosion testing relies on mimicking the exposure conditions, often incorporating salt spray and ultraviolet (UV) radiation, and exposing the metal to continuous or cyclic conditions similar to those of the corrosive environment. Their reliability to correlate to atmospheric exposure test results is often a concern when determining the timescale to which the accelerated tests can be related. Accelerated corrosion testing has yet to be universally accepted as a useful tool in predicting the long-term service life of a metal, despite its ability to rapidly induce corrosion. Although visual and mass loss methods of evaluating corrosion are the standard, and their use is crucial, a method that correlates timescales from accelerated testing to atmospheric exposure would be very valuable. This paper presents work that began with the characterization of the atmospheric environment at the Kennedy Space Center (KSC) Beachside Corrosion Test Site. The chemical changes that occur on low carbon steel, during atmospheric and accelerated corrosion conditions, were investigated using surface chemistry analytical methods. The corrosion rates and behaviors of panels subjected to long-term and accelerated corrosion conditions, involving neutral salt fog and alternating seawater spray, were compared to identify possible timescale correlations between accelerated and long-term corrosion performance. The results, as well as preliminary findings on the correlation investigation, are presented.

Properties and durability of the passive films on a nickel-chromium-molybdenum alloy and an iron-based bulk metallic glass

NASA Astrophysics Data System (ADS)

Pharkya, Pallavi

Alloy 22, a Ni-Cr-Mo-W alloy, and SAM1651, an Fe-Cr-Mo-B-Y-C bulk metallic glass are highly corrosion-resistant alloys. The high corrosion resistance of these alloys is due to the formation of tenacious oxide films on their surfaces. This study examines the reformation behavior of the passive films as a function of the corrosion resistance of the alloys and the corrosivity of the environment. The main tasks of this study were (i) to determine the chemical durability of passive films on these highly corrosion-resistant alloys in aggressive environments, (ii) to investigate the durability after mechanically damaging the passive films either locally or over the entire surface area and to study the reformation kinetics, (iii) to compare the durability of the passive films of the aforementioned highly corrosion resistant alloys with an alloy of intermediate corrosion resistance, AL6XN, and an alloy of less corrosion resistance, 316L SS, (iv) to examine the evolution of the electronic properties of the passive films on alloy 22 and SAM1651 under different environmental conditions such as concentrated chloride solution, acidic solution, temperature, potential and oxyanions, and (v) to develop an understanding of the relationship between the passive films' composition, electronic and electrochemical properties and the performance. A combination of techniques was utilized to meet the above mentioned objectives. Cyclic potentiodynamic polarization (CPP) was used to determine the electrochemical parameters such as freely corroding, breakdown and repassivation potentials. Electrochemical impedance spectroscopy (EIS) was used to determine the electronic properties such as impedance, thickness and capacitance of the passive films. Mott-Schottky (M-S) analysis was used to determine the type and the density of the defects in the passive films. The mechanical durability and reformation kinetics of the passive films was investigated using a scratch-repassivation method. The quality and the protectiveness of the reformed passive films after scribing were examined using EIS, M-S analysis, and AES. The results show that the passive films on alloy 22 and SAM1651 possess high chemical and mechanical durability. The reformed passive films acquired the same electronic and elemental properties as the passive films which were undamaged. The passive films on SAM1651 and alloy 22 showed better corrosion resistance and durability than did the passive films on AL6XN and 316L SS. The results also showed that the passive film behavior depends on the inherent corrosion resistance of an alloy and the corrosivity of the environment. The inherent corrosion resistance depends on the concentration of the passivity-providing elements such as Cr and Mo in the bulk composition of the alloy (and passive film), and the corrosivity of the environment which is influenced by chloride concentration, oxyanions, temperature, pH, and oxidizing potential.

Corrosion of Iron by Sulfate-Reducing Bacteria: New Views of an Old Problem

PubMed Central

Garrelfs, Julia

2014-01-01

About a century ago, researchers first recognized a connection between the activity of environmental microorganisms and cases of anaerobic iron corrosion. Since then, such microbially influenced corrosion (MIC) has gained prominence and its technical and economic implications are now widely recognized. Under anoxic conditions (e.g., in oil and gas pipelines), sulfate-reducing bacteria (SRB) are commonly considered the main culprits of MIC. This perception largely stems from three recurrent observations. First, anoxic sulfate-rich environments (e.g., anoxic seawater) are particularly corrosive. Second, SRB and their characteristic corrosion product iron sulfide are ubiquitously associated with anaerobic corrosion damage, and third, no other physiological group produces comparably severe corrosion damage in laboratory-grown pure cultures. However, there remain many open questions as to the underlying mechanisms and their relative contributions to corrosion. On the one hand, SRB damage iron constructions indirectly through a corrosive chemical agent, hydrogen sulfide, formed by the organisms as a dissimilatory product from sulfate reduction with organic compounds or hydrogen (“chemical microbially influenced corrosion”; CMIC). On the other hand, certain SRB can also attack iron via withdrawal of electrons (“electrical microbially influenced corrosion”; EMIC), viz., directly by metabolic coupling. Corrosion of iron by SRB is typically associated with the formation of iron sulfides (FeS) which, paradoxically, may reduce corrosion in some cases while they increase it in others. This brief review traces the historical twists in the perception of SRB-induced corrosion, considering the presently most plausible explanations as well as possible early misconceptions in the understanding of severe corrosion in anoxic, sulfate-rich environments. PMID:24317078

Development of new corrosion inhibitor tested on mild steel supported by electrochemical study

NASA Astrophysics Data System (ADS)

Habeeb, Hussein Jwad; Luaibi, Hasan Mohammed; Dakhil, Rifaat Mohammed; Kadhum, Abdul Amir H.; Al-Amiery, Ahmed A.; Gaaz, Tayser Sumer

2018-03-01

Mild steel is a metal which is commonly used in industrials and manufacturing of equipment for most industries round the world. It is cheaper cost compared with the other metals and its durable, hard and easy-to-wear physical properties make it a major choice in the manufacture of equipment parts. The main problem through the uses of mild steel in industry is its resistance against corrosion, especially in acidic solutions. This case led to raise the cost of maintenance of equipment that used mild steel and as a result increased costs for the company. Organic corrosive inhibitors that also act as green chemicals, 4-hydroxybenzylideneaminomethyl-5-ethyl-1,3,4-thiadiazol have been synthesized. This inhibitor is tested as corrosion inhibitor on a mild steel sample MS in 1 M hydrochloric acid solution (HCl) using electrochemical measurements test includes PD (Potentiodynamic), EIS (Electrochemical impedance spectroscopy), OCP (Open circuit potential) and EFM (electrochemical frequency modulation). The obtained results indicate that 4-hydroxybenzylideneaminomethyl-5-ethyl-1,3,4-thiadiazol acts as a good corrosion inhibitor for mild steel sample in HCl solution with efficiency above 90%. Changes in the impedance parameters postulated adsorption on the mild steel specimens' surfaces of, which it going to the formation of protective coating layer. It also shows that 4-hydroxybenzylideneaminomethyl-5-ethyl-1,3,4-thiadiazol corrosion inhibitors are effective in helping to reduce and slow down the corrosion process that occurs on mild steel surface in hydrochloric acid solution. Increase of corrosion inhibitor concentration provides a protective layer of mild steel. However, this protective layer becomes weak when the temperature of the solution increases.

Image analysis of corrosion pit initiation on ASTM type A240 stainless steel and ASTM type A 1008 carbon steel

NASA Astrophysics Data System (ADS)

Nine, H. M. Zulker

The adversity of metallic corrosion is of growing concern to industrial engineers and scientists. Corrosion attacks metal surface and causes structural as well as direct and indirect economic losses. Multiple corrosion monitoring tools are available although those are time-consuming and costly. Due to the availability of image capturing devices in today's world, image based corrosion control technique is a unique innovation. By setting up stainless steel SS 304 and low carbon steel QD 1008 panels in distilled water, half-saturated sodium chloride and saturated sodium chloride solutions and subsequent RGB image analysis in Matlab, in this research, a simple and cost-effective corrosion measurement tool has identified and investigated. Additionally, the open circuit potential and electrochemical impedance spectroscopy results have been compared with RGB analysis to gratify the corrosion. Additionally, to understand the importance of ambiguity in crisis communication, the communication process between Union Carbide and Indian Government regarding the Bhopal incident in 1984 was analyzed.

Mechanical and Microstructural Characterization of a New Corrosion Resistant Stainless Steel

NASA Astrophysics Data System (ADS)

Voiculescu, I.; Geantă, V.; Stefănoiu, R.; Cotruţ, C.; Ciocoiu, R.; Ionescu, M.

2018-06-01

The paper investigates the manner in which the chemical composition and delivery status of a new type of stainless steel, highly alloyed with Ni and Cr, affect mechanical properties, microstructure and corrosion resistance. The results obtained during the mechanical test (tensile, compression, Charpy test and micro-hardness) have revealed promising values. During the corrosion test, the preferential attack of the reagent (Aqua regia) located on the grain boundaries, inclusions or polyhedral precipitates have been observed. On the corroded surfaces, some localized pitting effects on grain boundaries have been revealed. The analyses of the parameter values recorded during the corrosion test revealed that the corrosion current density had a low value, comparable to that of other specific types of stainless steels. The actual Icorr (1.089 µA/cm2) value measured for the experimental alloy proves good resistance to corrosion in 3% NaCl saline solution. The estimated rate of corrosion presented acceptable values (0.011 mm/year).

Corrosion anisotropy of titanium deformed by the hydrostatic extrusion

NASA Astrophysics Data System (ADS)

Chojnacka, A.; Kawalko, J.; Koscielny, H.; Guspiel, J.; Drewienkiewicz, A.; Bieda, M.; Pachla, W.; Kulczyk, M.; Sztwiertnia, K.; Beltowska-Lehman, E.

2017-12-01

The corrosion behaviour of titanium rods deformed by hydrostatic extrusion (HE) in artificial saliva (Carter-Brugirard's solution of pH 7.6) was investigated using open-circuit potentials (OCPs), (DC) potentiodynamic polarisation curves and (AC) electrochemical impedance spectroscopy (EIS) techniques. Various electrochemical parameters (corrosion potential Ecorr, corrosion current (icorr), polarisation resistance Rp, charge transfer resistance Rct and oxide film resistance Rf) were analysed. Significant coherence was observed between results achieved from these procedures, i.e., all applied techniques showed the same trend for corrosion resistance. The obtained electrochemical data were then related to the microstructure parameters (crystallographic texture, grain size, grain boundary distribution and density) determined using the EBSD/SEM technique. It was found that the corrosion behaviour of titanium processed by the HE method was superior compared to the unprocessed Ti, and this was clearly dependent on the extrusion direction. The highest corrosion resistance was revealed for the HE-deformed Ti rod of the surface oriented longitudinal (parallel) to the extrusion direction.

In Vitro Electrochemical Corrosion and Cell Viability Studies on Nickel-Free Stainless Steel Orthopedic Implants

PubMed Central

Salahinejad, Erfan; Hadianfard, Mohammad Jafar; Macdonald, Digby Donald; Sharifi-Asl, Samin; Mozafari, Masoud; Walker, Kenneth J.; Rad, Armin Tahmasbi; Madihally, Sundararajan V.; Tayebi, Lobat

2013-01-01

The corrosion and cell viability behaviors of nanostructured, nickel-free stainless steel implants were studied and compared with AISI 316L. The electrochemical studies were conducted by potentiodynamic polarization and electrochemical impedance spectroscopic measurements in a simulated body fluid. Cytocompatibility was also evaluated by the adhesion behavior of adult human stem cells on the surface of the samples. According to the results, the electrochemical behavior is affected by a compromise among the specimen's structural characteristics, comprising composition, density, and grain size. The cell viability is interpreted by considering the results of the electrochemical impedance spectroscopic experiments. PMID:23630603

Corrosion Studies of Wrought and Cast NASA-23 Alloy

NASA Technical Reports Server (NTRS)

Danford, M. D.

1997-01-01

Corrosion studies were carried out for wrought and cast NASA-23 alloy using electrochemical methods. The scanning reference electrode technique (SRET), the polarization resistance technique (PR), and the electrochemical impedance spectroscopy (EIS) were employed. These studies corroborate the findings of stress corrosion studies performed earlier, in that the material is highly resistant to corrosion.

Catalysis of copper corrosion products on chlorine decay and HAA formation in simulated distribution systems.

PubMed

Zhang, Hong; Andrews, Susan A

2012-05-15

This study investigated the effect of copper corrosion products, including Cu(II), Cu(2)O, CuO and Cu(2)(OH)(2)CO(3), on chlorine degradation, HAA formation, and HAA speciation under controlled experimental conditions. Chlorine decay and HAA formation were significantly enhanced in the presence of copper with the extent of copper catalysis being affected by the solution pH and the concentration of copper corrosion products. Accelerated chlorine decay and increased HAA formation were observed at pH 8.6 in the presence of 1.0 mg/L Cu(II) compared with that observed at pH 6.6 and pH 7.6. Further investigation of chlorine decay in the presence of both Suwannee River NOM and Cu(II) indicated that an increased reactivity of NOM with dissolved and/or solid surface-associated Cu(II), rather than chlorine auto-decomposition, was a primary reason for the observed rapid chlorine decay. Copper corrosion solids [Cu(2)O, CuO, Cu(2)(OH)(2)CO(3)] exhibited catalytic effects on both chlorine decay and HAA formation. Contrary to the results observed when in the absence of copper corrosion products, DCAA formation was consistently predominant over other HAA species in the presence of copper corrosion products, especially at neutral and high pH. This study improves the understanding for water utilities and households regarding chlorine residuals and HAA concentrations in distribution systems, in particular once the water reaches domestic plumbing where copper is widely used. Copyright © 2012 Elsevier Ltd. All rights reserved.

Effect of PWHT on Microstructure, Mechanical and Corrosion Behaviour of Gas Tungsten Arc Welds of IN718 Superalloys

NASA Astrophysics Data System (ADS)

Dilkush; Mohammed, Raffi; Madhusudhan Reddy, G.; Srinivasa Rao, K.

2018-03-01

The present work aims to improve corrosion resistance and mechanical behavior of the welds with suitable post weld heat treatment i.e. direct aging and solutionizing treatments (980STA, 1080STA). Gas tungsten arc welding (GTAW) has been performed on Inconel 718 (IN718) nickel based super alloy plates with 3mm thickness. The structural –property relationship of the post weld heat treated samples is judged by correlating the microstructural changes with observed mechanical behavior and pitting corrosion resistance of the welds As-recevied, direct aging (DA), 980STA,1080STA were studied. Welds were characterized for microstructure changes with scanning electron microscopy (SEM) and optical microscopy (OM).Vickers micro- hardness tester was used to measure the hardness of the weldments. Potential-dynamic polarization testing was carried out to study the pitting corrosion resistance in 3.5%NaCl (Sodium chloride) solution at 30°C.Results of the present study established that post weld heat treatments resulted in promoting the element segregation diffusion and resolve them from brittle laves particles in the matrix. Increased precipitation of strengthening phases lead to a significant increase in fusion zone hardness of 1080STA post weld heat treated condition compared to as welded, direct aged, 980STA conditions. Due to significant changes in the microstructural behavior of 1080STA condition resulted in superior pitting corrosion resistance than 980STA, direct aged and as- recevied conditions of IN718 GTA welds

Flow-induced corrosion of absorbable magnesium alloy: In-situ and real-time electrochemical study

PubMed Central

Wang, Juan; Jang, Yongseok; Wan, Guojiang; Giridharan, Venkataraman; Song, Guang-Ling; Xu, Zhigang; Koo, Youngmi; Qi, Pengkai; Sankar, Jagannathan; Huang, Nan; Yun, Yeoheung

2016-01-01

An in-situ and real-time electrochemical study in a vascular bioreactor was designed to analyze corrosion mechanism of magnesium alloy (MgZnCa) under mimetic hydrodynamic conditions. Effect of hydrodynamics on corrosion kinetics, types, rates and products was analyzed. Flow-induced shear stress (FISS) accelerated mass and electron transfer, leading to an increase in uniform and localized corrosions. FISS increased the thickness of uniform corrosion layer, but filiform corrosion decreased this layer resistance at high FISS conditions. FISS also increased the removal rate of localized corrosion products. Impedance-estimated and linear polarization-measured polarization resistances provided a consistent correlation to corrosion rate calculated by computed tomography. PMID:28626241

Flow-induced corrosion of absorbable magnesium alloy: In-situ and real-time electrochemical study.

PubMed

Wang, Juan; Jang, Yongseok; Wan, Guojiang; Giridharan, Venkataraman; Song, Guang-Ling; Xu, Zhigang; Koo, Youngmi; Qi, Pengkai; Sankar, Jagannathan; Huang, Nan; Yun, Yeoheung

2016-03-01

An in-situ and real-time electrochemical study in a vascular bioreactor was designed to analyze corrosion mechanism of magnesium alloy (MgZnCa) under mimetic hydrodynamic conditions. Effect of hydrodynamics on corrosion kinetics, types, rates and products was analyzed. Flow-induced shear stress (FISS) accelerated mass and electron transfer, leading to an increase in uniform and localized corrosions. FISS increased the thickness of uniform corrosion layer, but filiform corrosion decreased this layer resistance at high FISS conditions. FISS also increased the removal rate of localized corrosion products. Impedance-estimated and linear polarization-measured polarization resistances provided a consistent correlation to corrosion rate calculated by computed tomography.

Corrosion of dental alloys in artificial saliva with Streptococcus mutans.

PubMed

Lu, Chunhui; Zheng, Yuanli; Zhong, Qun

2017-01-01

A comparative study of the corrosion resistance of CoCr and NiCr alloys in artificial saliva (AS) containing tryptic soy broth (Solution 1) and Streptococcus mutans (S. mutans) species (Solution 2) was performed by electrochemical methods, including open circuit potential measurements, impedance spectroscopy, and potentiodynamic polarization. The adherence of S. mutans to the NiCr and CoCr alloy surfaces immersed in Solution 2 for 24 h was verified by scanning electron microscopy, while the results of electrochemical impedance spectroscopy confirmed the importance of biofilm formation for the corrosion process. The R(QR) equivalent circuit was successfully used to fit the data obtained for the AS mixture without S. mutans, while the R(Q(R(QR))) circuit was found to be more suitable for describing the biofilm properties after treatment with the AS containing S. mutans species. In addition, a negative shift of the open circuit potential with immersion time was observed for all samples regardless of the solution type. Both alloys exhibited higher charge transfer resistance after treatment with Solution 2, and lower corrosion current densities were detected for all samples in the presence of S. mutans. The obtained results suggest that the biofilm formation observed after 24 h of exposure to S. mutans bacteria might enhance the corrosion resistance of the studied samples by creating physical barriers that prevented oxygen interactions with the metal surfaces.

Comparison of organic peracids in wastewater treatment: Disinfection, oxidation and corrosion.

PubMed

Luukkonen, Tero; Heyninck, Tom; Rämö, Jaakko; Lassi, Ulla

2015-11-15

The use of organic peracids in wastewater treatment is attracting increasing interest. The common beneficial features of peracids are effective anti-microbial properties, lack of harmful disinfection by-products and high oxidation power. In this study performic (PFA), peracetic (PAA) and perpropionic acids (PPA) were synthesized and compared in laboratory batch experiments for the inactivation of Escherichia coli and enterococci in tertiary wastewater, oxidation of bisphenol-A and for corrosive properties. Disinfection tests revealed PFA to be a more potent disinfectant than PAA or PPA. 1.5 mg L(-1) dose and 2 min of contact time already resulted in 3.0 log E. coli and 1.2 log enterococci reduction. Operational costs of disinfection were estimated to be 0.0114, 0.0261 and 0.0207 €/m(3) for PFA, PAA and PPA, respectively. Disinfection followed the first order kinetics (Hom model or S-model) with all studied peracids. However, in the bisphenol-A oxidation experiments involving Fenton-like conditions (pH = 3.5, Fe(2+) or Cu(2+) = 0.4 mM) peracids brought no additional improvement to traditionally used and lower cost hydrogen peroxide. Corrosion measurements showed peracids to cause only a negligible corrosion rate (<6 μm year(-1)) on stainless steel 316L while corrosion rates on the carbon steel sample were significantly higher (<500 μm year(-1)). Copyright © 2015 Elsevier Ltd. All rights reserved.

Electrochemical Behavior of Biomedical Titanium Alloys Coated with Diamond Carbon in Hanks' Solution

NASA Astrophysics Data System (ADS)

Gnanavel, S.; Ponnusamy, S.; Mohan, L.; Radhika, R.; Muthamizhchelvan, C.; Ramasubramanian, K.

2018-03-01

Biomedical implants in the knee and hip are frequent failures because of corrosion and stress on the joints. To solve this important problem, metal implants can be coated with diamond carbon, and this coating plays a critical role in providing an increased resistance to implants toward corrosion. In this study, we have employed diamond carbon coating over Ti-6Al-4V and Ti-13Nb-13Zr alloys using hot filament chemical vapor deposition method which is well-established coating process that significantly improves the resistance toward corrosion, wears and hardness. The diamond carbon-coated Ti-13Nb-13Zr alloy showed an increased microhardness in the range of 850 HV. Electrochemical impedance spectroscopy and polarization studies in SBF solution (simulated body fluid solution) were carried out to understand the in vitro behavior of uncoated as well as coated titanium alloys. The experimental results showed that the corrosion resistance of Ti-13Nb-13Zr alloy is relatively higher when compared with diamond carbon-coated Ti-6Al-4V alloys due to the presence of β phase in the Ti-13Nb-13Zr alloy. Electrochemical impedance results showed that the diamond carbon-coated alloys behave as an ideal capacitor in the body fluid solution. Moreover, the stability in mechanical properties during the corrosion process was maintained for diamond carbon-coated titanium alloys.

Corrosion of dental alloys in artificial saliva with Streptococcus mutans

PubMed Central

Lu, Chunhui; Zheng, Yuanli; Zhong, Qun

2017-01-01

A comparative study of the corrosion resistance of CoCr and NiCr alloys in artificial saliva (AS) containing tryptic soy broth (Solution 1) and Streptococcus mutans (S. mutans) species (Solution 2) was performed by electrochemical methods, including open circuit potential measurements, impedance spectroscopy, and potentiodynamic polarization. The adherence of S. mutans to the NiCr and CoCr alloy surfaces immersed in Solution 2 for 24 h was verified by scanning electron microscopy, while the results of electrochemical impedance spectroscopy confirmed the importance of biofilm formation for the corrosion process. The R(QR) equivalent circuit was successfully used to fit the data obtained for the AS mixture without S. mutans, while the R(Q(R(QR))) circuit was found to be more suitable for describing the biofilm properties after treatment with the AS containing S. mutans species. In addition, a negative shift of the open circuit potential with immersion time was observed for all samples regardless of the solution type. Both alloys exhibited higher charge transfer resistance after treatment with Solution 2, and lower corrosion current densities were detected for all samples in the presence of S. mutans. The obtained results suggest that the biofilm formation observed after 24 h of exposure to S. mutans bacteria might enhance the corrosion resistance of the studied samples by creating physical barriers that prevented oxygen interactions with the metal surfaces. PMID:28350880

Comparative study on Ti/Zr/V and chromate conversion treated aluminum alloys: Anti-corrosion performance and epoxy coating adhesion properties

NASA Astrophysics Data System (ADS)

Zhu, Wen; Li, Wenfang; Mu, Songlin; Fu, Nianqing; Liao, Zhongmiao

2017-05-01

In this study, a Ti/Zr/V conversion coating (TZVCC) was deposited on the surface of aluminum alloy 6063 (AA6063) as an alternative of the chromate conversion coating (CCC). Both the TZVCC treated AA6063 (TZVCC/AA6063) and CCC treated AA6063 (CCC/AA6063) were characterized by scanning electron microscopy (SEM), X-ray photoelectron spectroscopy (XPS), atomic force microscope (AFM) and contact angle measuring device. The anti-corrosion performance of the TZVCC/AA6063 and CCC/AA6063 was evaluated by electrochemical measurements and neutral salt spray tests. It showed that both the surface roughness and surface free energy of the AA6063 were significantly increased after TZVCC treatment. The anti-corrosion performance of TZVCC/AA6063 was superior to that of CCC/AA6063. In addition, the effects of the TZVCC and CCC on the adhesion properties and anti-corrosion performance of epoxy coating applied on samples were examined by pull-off tests and electrochemical impedance spectroscopy (EIS). The dry, wet and recovery adhesive strengths of the epoxy coating on TZVCC treated samples (epoxy coated TZVCC/AA6063) were very close to those of epoxy coating on CCC treated ones (epoxy coated CCC/AA6063). The epoxy coated TZVCC/AA6063 showed better corrosion resistance than the epoxy coated CCC/AA6063 and epoxy coated AA6063.

An electrochemical study of the corrosion behavior of primer coated 2219-T87 aluminum

NASA Technical Reports Server (NTRS)

Danford, M. D.; Higgins, R. H.

1985-01-01

The corrosion behavior for 2219-T87 aluminum coated with various primers, including those used for the external tank and solid rocket boosters of the Space Shuttle Transportation System, were investigated using electrochemical techniques. Corrosion potential time, polarization resistance time, electrical resistance time, and corrosion rate time measurements were all investigated. It was found that electrical resistance time and corrosion rate time measurement were most useful for studying the corrosion behavior of painted aluminum. Electrical resistance time determination give useful information concerning the porosity of paint films, while corrosion rate time curves give important information concerning overall corrosion rates and corrosion mechanisms. In general, the corrosion rate time curves all exhibited at least one peak during the 30 day test period, which was attributed, according to the proposed mechanisms, to the onset of the hydrogen evolution reaction and the beginning of destruction of the protective properties of the paint film.

Corrosive sliding wear behavior of laser clad Mo 2Ni 3Si/NiSi intermetallic coating

NASA Astrophysics Data System (ADS)

Lu, X. D.; Wang, H. M.

2005-05-01

Many ternary metal silicides such as W 2Ni 3Si, Ti 2Ni 3Si and Mo 2Ni 3Si with the topologically closed-packed (TCP) hP12 MgZn 2 type Laves phase crystal structure are expected to have outstanding wear and corrosion resistance due to their inherent high hardness and sluggish temperature dependence and strong atomic bonds. In this paper, Mo 2Ni 3Si/NiSi intermetallic coating was fabricated on substrate of an austenitic stainless steel AISI321 by laser cladding using Ni-Mo-Si elemental alloy powders. Microstructure of the coating was characterized by optical microscopy (OM), scanning electron microscopy (SEM), X-ray diffraction (XRD) and energy dispersive X-ray analysis (EDS). Wear resistance of the coating is evaluated under corrosive sliding wear test condition. Influence of corrosion solutions on the wear resistance of the coating was studied and the wear mechanism was discussed based on observations of worn surface morphology. Results showed that the laser clad Mo 2Ni 3Si/NiSi composite coating have a fine microstructure of Mo 2Ni 3Si primary dendrites and the interdendritic Mo 2Ni 3Si/NiSi eutectics. The coating has excellent corrosive wear resistance compared with austenitic stainless steel AISI321 under acid, alkaline and saline corrosive environments.

Enhancement of corrosion resistance of polypyrrole using metal oxide nanoparticles: Potentiodynamic and electrochemical impedance spectroscopy study.

PubMed

Hosseini, Marzieh; Fotouhi, Lida; Ehsani, Ali; Naseri, Maryam

2017-11-01

We introduce a simple and facile strategy for dispersing of nanoparticles within a p-type conducting polymer matrix by in situ electropolymerization using oxalic acid as the supporting electrolyte. Coatings prepared from polypyrrole-nano-metal oxide particles synthesized by in situ polymerization were found to exhibit excellent corrosion resistance much superior to polypyrrole (Ppy) in aggressive environments. The anti-corrosion behavior of polypyrrole films in different states and the presence of TiO 2 , Mn 2 O 3 and ZnO nanoparticles synthesized by electropolymerization on Al electrodes have been investigated in corrosive solutions using potentiodynamic polarization and electrochemical impedance spectroscopy. The electrochemical response of the coated electrodes in polymer and nanocomposite state was compared with bare electrodes. The use of TiO 2 nanoparticles has proved to be a great improvement in the performances of polypyrrole films for corrosion protection of Al samples. The polypyrrole synthesized in the presence of TiO 2 nanoparticles coated electrodes offered a noticeable enhancement of protection against corrosion processes. The exceptional improvement of performance of these coatings has been associated with the increase in barrier to diffusion, prevention of charge transport by the nanosize TiO 2 , redox properties of polypyrrole as well as very large surface area available for the liberation of dopant due to nano-size additive. Copyright © 2017 Elsevier Inc. All rights reserved.

Alkali activated slag mortars provide high resistance to chloride-induced corrosion of steel

NASA Astrophysics Data System (ADS)

Criado, Maria; Provis, John L.

2018-06-01

The pore solutions of alkali-activated slag cements and Portland-based cements are very different in terms of their chemical and redox characteristics, particularly due to the high alkalinity and high sulfide content of alkali-activated slag cement. Therefore, differences in corrosion mechanisms of steel elements embedded in these cements could be expected, with important implications for the durability of reinforced concrete elements. This study assesses the corrosion behaviour of steel embedded in alkali-activated blast furnace slag (BFS) mortars exposed to alkaline solution, alkaline chloride-rich solution, water, and standard laboratory conditions, using electrochemical techniques. White Portland cement (WPC) mortars and blended cement mortars (white Portland cement and blast furnace slag) were also tested for comparative purposes. The steel elements embedded in immersed alkali-activated slag mortars presented very negative redox potentials and high apparent corrosion current values; the presence of sulfide reduced the redox potential, and the oxidation of the reduced sulfur-containing species within the cement itself gave an electrochemical signal that classical electrochemical tests for reinforced concrete durability would interpret as being due to steel corrosion processes. However, the actual observed resistance to chloride-induced corrosion was very high, as measured by extraction and characterisation of the steel at the end of a 9-month exposure period, whereas the steel embedded in white Portland cement mortars was significantly damaged under the same conditions.

Effect of concentration of hyaluronic acid and NaCl on corrosion behavior of 316L austenitic stainless steel

NASA Astrophysics Data System (ADS)

Bansod, Ankur V.; Khobragade, Nilay N.; Giradkar, Karansagar V.; Patil, Awanikumar P.

2017-11-01

Due to low cost and easily available material, 316L stainless steel (SS) is used for biomedical implants. The electrochemical corrosion behavior of 316L (SS) was studied as a function of the concentration of simulated biological fluid (hyaluronic acid), the influence of Cl- and the combined effect of NaCl and hyaluronic acid (HA). For the electrochemical tests, potentiodynamic polarization test and electrochemical impedance spectroscopy (EIS) were undertaken. With the increase in HA concentration, corrosion rate increases. Whereas, with the addition of NaCl to HA the solution, the corrosion resistance of the sample was enhanced. Also, in pure NaCl solution, the corrosion current density (i corr) increased as compared to bare HA and HA  +  NaCl. This is due to the adhesion property of the HA on the sample surface. EIS result agrees with the findings of potentiodynamic polarization tests. X-ray photoelectron spectroscopy (XPS) was executed to analyze the passive film formed in the solution of HA and NaCl on 316L SS. XPS spectra confirms the formation of the passive film containing chromium oxide and hydroxides. Also, the formation of MoO2 helps in improving better corrosion resistance. The peak of nitrogen was observed in the sample immersed in HA solution. Scanning electron microscope (SEM) was carried out to analyze the surface morphology.

Ultrasonic cavitation erosion-corrosion behavior of friction stir processed stainless steel.

PubMed

Selvam, Karthikeyan; Mandal, Priya; Grewal, Harpreet Singh; Arora, Harpreet Singh

2018-06-01

Cavitation erosion remains the primary cause of material degradation in fluid machinery components operating at high speed. Micro-jets/shock waves caused by implosion of bubbles on material surface results in significant material loss and premature failure of the components. The presence of corrosive medium further exuberates this effect, causing rapid degradation. Here, we demonstrate a novel pathway to control cavitation erosion-corrosion by tailoring the surface properties using submerged friction stir processing (FSP), a severe plastic deformation process. FSP parameters were varied over wide range of strain-rates to generate tailored microstructures. High strain-rate processing resulted in nearly single phase fine grained structure while low strain-rate processing resulted in phase transformation in addition to grain refinement. As-received and processed samples were subjected to ultrasonic cavitation in distilled water as well as in corrosive environment of 3.5% NaCl solution. Individual roles of cavitation erosion, corrosion and their synergistic effects were analyzed. Depending on the microstructure, processed samples showed nearly 4-6 times higher cavitation erosion resistance compared to as-received alloy. Superior cavitation erosion-corrosion resistance of processed samples was attributed to surface strengthening, higher strain-hardening ability and quick passivation kinetics. The results of current study could be potentially transformative in designing robust materials for hydro-dynamic applications. Copyright © 2018 Elsevier B.V. All rights reserved.

Preparation and corrosion resistance of magnesium phytic acid/hydroxyapatite composite coatings on biodegradable AZ31 magnesium alloy.

PubMed

Zhang, Min; Cai, Shu; Zhang, Feiyang; Xu, Guohua; Wang, Fengwu; Yu, Nian; Wu, Xiaodong

2017-06-01

In this work, a magnesium phytic acid/hydroxyapatite composite coating was successfully prepared on AZ31 magnesium alloy substrate by chemical conversion deposition technology with the aim of improving its corrosion resistance and bioactivity. The influence of hydroxyapatite (HA) content on the microstructure and corrosion resistance of the coatings was investigated. The results showed that with the increase of HA content in phytic acid solution, the cracks on the surface of the coatings gradually reduced, which subsequently improved the corrosion resistance of these coated magnesium alloy. Electrochemical measurements in simulated body fluid (SBF) revealed that the composite coating with 45 wt.% HA addition exhibited superior surface integrity and significantly improved corrosion resistance compared with the single phytic acid conversion coating. The results of the immersion test in SBF showed that the composite coating could provide more effective protection for magnesium alloy substrate than that of the single phytic acid coating and showed good bioactivity. Magnesium phytic acid/hydroxyapatite composite, with the desired bioactivity, can be synthesized through chemical conversion deposition technology as protective coatings for surface modification of the biodegradable magnesium alloy implants. The design idea of the new type of biomaterial is belong to the concept of "third generation biomaterial". Corrosion behavior and bioactivity of coated magnesium alloy are the key issues during implantation. In this study, preparation and corrosion behavior of magnesium phytic acid/hydroxyapatite composite coatings on magnesium alloy were studied. The basic findings and significance of this paper are as follows: 1. A novel environmentally friendly, homogenous and crack-free magnesium phytic acid/hydroxyapatite composite coating was fabricated on AZ31 magnesium alloy via chemical conversion deposition technology with the aim of enhancing its corrosion resistance and bioactivity. The chemical conversion coatings, which are formed through the reaction between the substrate and the environment, have attracted increasing attention owing to the relative low treatment temperature, favorable bonding to substrate and simple implementation process. 2. With the increasing of hydroxyapatite (HA) content, the crack width in the composite coatings and the thickness of the coatings exhibit obviously decreased. The reason is probably that when adding HA into the phytic acid solution, the amount of active hydroxyl groups in the phytic acid are reduced via forming the coordination bond between P-OH groups from phytic acid and P-OH groups from the surface of HA, thus decreasing the coating thickness and hydrogen formation, as well as avoiding coating cracking. 3. By adjusting the HA content to 45 wt.%, a dense and relatively smooth composite coating with ~1.4 μm thickness is obtained on magnesium alloy, and exhibits high corrosion resistance and good bioactivity when compared with the single phytic acid conversion coating.

Electrochemical corrosion and surface analyses of a ni-cr alloy in bleaching agents.

PubMed

Tamam, Evşen; Aydın, A Kevser; Bilgiç, Semra

2014-10-01

The aim of this study was to evaluate the corrosion behavior of a Ni-Cr dental casting alloy subjected to 10% hydrogen peroxide (HP) and 10% carbamide peroxide (CP) bleaching solutions and to determine the composition of the surface oxide layer formed on the alloy specimens. Ten cylindrical specimens (4 mm in diameter × 25 mm in height) were cast from a Ni-Cr alloy (Wiron 99) and divided into two groups (n = 5). A potentiodynamic polarization test was used to compare the corrosion rates of specimens in HP and CP (pH = 6.5). Before cyclic polarization tests, all alloy specimens were allowed to reach a steady open circuit potential (Ecorr ) for a period of 1 hour. Then tests were initiated at 100 mV versus standard calomel electrode (SCE) below Ecorr and scanned at a rate of 1 mV/s in the anodic direction until reaching 1000 mV over the Ecorr value. The scan then was reversed back to the Ecorr of the specimens. The open circuit potentials (Ecorr ) and the current densities (Icorr ) were determined using the anodic Tafel regions extrapolating from the curves. Differences in Ecorr and Icorr were determined using one-way ANOVA (α = 0.05). In addition, corrosion rates were calculated from these curves. Before and after polarization tests, a scanning electron microscope (SEM) examination accompanied by energy dispersive X-ray spectroscopy (EDS) was used to analyze the surface morphology. The surface characterization of the passive film formed on alloy specimens was also performed by using X-ray photoelectron spectroscopy (XPS). In this study, bleaching agents had an effect on the anodic process for two groups. Although no statistical difference was identified between the groups for both corrosion parameters, results indicated that the effect of CP on the corrosion behavior was less than that of HP. These results agreed with the SEM observations. XPS data showed that oxide layers formed on all groups contained mainly Cr2 O3 , NiO, and MoO3 , and the amounts of oxides formed on CP-treated specimens were higher than HP treated ones. Also, molybdenum rates were increased with CP application compared to HP. The comparison of the effects of the two bleaching agents at 10% showed that the alloy suffered less corrosion with CP than HP. This result was also confirmed by the SEM and XPS data. The presence of Mo on the oxide layer affected the oxide layer, leading to lower corrosion rates. © 2014 by the American College of Prosthodontists.

Corrosion behavior of sensitized duplex stainless steel.

PubMed

Torres, F J; Panyayong, W; Rogers, W; Velasquez-Plata, D; Oshida, Y; Moore, B K

1998-01-01

The present work investigates the corrosion behavior of 2205 duplex stainless steel in 0.9% NaCl solution after various heat-treatments, and compares it to that of 316L austenitic stainless steel. Both stainless steels were heat-treated at 500, 650, and 800 degrees C in air for 1 h, followed by furnace cooling. Each heat-treated sample was examined for their microstructures and Vickers micro-hardness, and subjected to the X-ray diffraction for the phase identification. Using potentiostatic polarization method, each heat-treated sample was corrosion-tested in 37 degrees C 0.9% NaCl solution to estimate its corrosion rate. It was found that simulated sensitization showed an adverse influence on both steels, indicating that corrosion rates increased by increasing the sensitization temperatures.

Status of the DOE/NASA critical gas turbine research and technology project

NASA Technical Reports Server (NTRS)

Clark, J. S.

1980-01-01

Activities performed in order to provide an R&T data base for utility gas turbine systems burning coal-derived fuels are described. Experiments were run to determine the corrosivity effects of trace metal contaminants (and potential fuel additives) on gas turbine materials and these results were correlated in a corrosion-life prediction model. Actual fuels were burned in a burner rig hot corrosion test to verify the model. A deposition prediction model was assembled and compared with results of actual coal-derived fuel deposition tests. Thermal barrier coatings were tested to determine their potential for protecting gas turbine hardware from the corrosive contaminants. Several coatings were identified with significantly improved spallation-resistance (and, hence, corrosion resistance).

Retardation of surface corrosion of biodegradable magnesium-based materials by aluminum ion implantation

NASA Astrophysics Data System (ADS)

Wu, Guosong; Xu, Ruizhen; Feng, Kai; Wu, Shuilin; Wu, Zhengwei; Sun, Guangyong; Zheng, Gang; Li, Guangyao; Chu, Paul K.

2012-07-01

Aluminum ion implantation is employed to modify pure Mg as well as AZ31 and AZ91 magnesium alloys and their surface degradation behavior in simulated body fluids is studied. Polarization tests performed in conjunction with scanning electron microscopy (SEM) reveal that the surface corrosion resistance after Al ion implantation is improved appreciably. This enhancement can be attributed to the formation of a gradient surface structure with a gradual transition from an Al-rich oxide layer to Al-rich metal layer. Compared to the high Al-content magnesium alloy (AZ91), a larger reduction in the degradation rate is achieved from pure magnesium and AZ31. Our results reveal that the surface corrosion resistance of Mg alloys with no or low Al content can be improved by Al ion implantation.

Effect of Native Oxide Film on Commercial Magnesium Alloys Substrates and Carbonate Conversion Coating Growth and Corrosion Resistance

PubMed Central

Feliu, Sebastián; Samaniego, Alejandro; Bermudez, Elkin Alejandro; El-Hadad, Amir Abdelsami; Llorente, Irene; Galván, Juan Carlos

2014-01-01

Possible relations between the native oxide film formed spontaneously on the AZ31 and AZ61 magnesium alloy substrates with different surface finish, the chemistry of the outer surface of the conversion coatings that grows after their subsequent immersion on saturated aqueous NaHCO3 solution treatment and the enhancement of corrosion resistance have been studied. The significant increase in the amount of aluminum and carbonate compounds on the surface of the conversion coating formed on the AZ61 substrate in polished condition seems to improve the corrosion resistance in low chloride ion concentration solutions. In contrast, the conversion coatings formed on the AZ31 substrates in polished condition has little effect on their protective properties compared to the respective as-received surface. PMID:28788582

Effect of Native Oxide Film on Commercial Magnesium Alloys Substrates and Carbonate Conversion Coating Growth and Corrosion Resistance.

PubMed

Feliu, Sebastián; Samaniego, Alejandro; Bermudez, Elkin Alejandro; El-Hadad, Amir Abdelsami; Llorente, Irene; Galván, Juan Carlos

2014-03-28

Possible relations between the native oxide film formed spontaneously on the AZ31 and AZ61 magnesium alloy substrates with different surface finish, the chemistry of the outer surface of the conversion coatings that grows after their subsequent immersion on saturated aqueous NaHCO₃ solution treatment and the enhancement of corrosion resistance have been studied. The significant increase in the amount of aluminum and carbonate compounds on the surface of the conversion coating formed on the AZ61 substrate in polished condition seems to improve the corrosion resistance in low chloride ion concentration solutions. In contrast, the conversion coatings formed on the AZ31 substrates in polished condition has little effect on their protective properties compared to the respective as-received surface.

Aqueous chloride stress corrosion cracking of titanium - A comparison with environmental hydrogen embrittlement

NASA Technical Reports Server (NTRS)

Nelson, H. G.

1974-01-01

The physical characteristics of stress corrosion cracking of titanium in an aqueous chloride environment are compared with those of embrittlement of titanium by a gaseous hydrogen environment in an effort to help contribute to the understanding of the possible role of hydrogen in the complex stress corrosion cracking process. Based on previous studies, the two forms of embrittlement are shown to be similar at low hydrogen pressures (100 N/sq m) but dissimilar at higher hydrogen pressures. In an effort to quantify this comparison, tests were conducted in an aqueous chloride solution using the same material and test techniques as had previously been employed in a gaseous hydrogen environment. The results of these tests strongly support models based on hydrogen as the embrittling species in an aqueous chloride environment.

Corrosion Behavior of Nuclear Waste Storage Canister Materials

NASA Astrophysics Data System (ADS)

Grant, John

The nature of interaction of mild steel nuclear waste storage containers with technetium ions is not fully known. Technetium is formed during nuclear processing and some of this technetium has leaked at the Hanford nuclear waste storage site in Washington State. It is often found as highly oxidized pertechnetate (TeO4-) anions at these storage sites which also happen to be highly alkaline and contain a significant amount of nitrate. Theoretically, pertechnetate anions can act as electron acceptors and interact with the mild steel containers and accelerate the oxidation (corrosion) of steel. It is of interest to identify if pertechnetate anions pose a corrosion hazard to the mild steel nuclear waste storage tanks, under the conditions of the storage sites, as that can accelerate the degradation of the tanks and lead to further contamination. In this thesis, the interaction of two relevant container materials, namely, steel alloys A285 and A537 with a technetium surrogate, rhenium was studied. Perrhenate was used as an analog for pertechnetate. As all isotopes of technetium are radioactive, rhenium was chosen as the experimental surrogate due to its chemical similarity to technetium. Electrochemical behavior was evaluated using potentiodynamic polarization tests, and the surface morphology was studied using optical microscopy and scanning electron microscopy. Potentiodynamic polarization tests were conducted in 1.0M NaNO3 + 0.1M NaOH and 1.0M NaNO3 + 0.1M NaOH + 0.02M NaReO4. Tests were performed at three different temperatures, namely, (i) room temperature, (ii) 50°C and (iii) 80°C to study the effect of higher temperatures found in the storage sites. Corrosion current, corrosion potential, anodic and cathodic Tafel slopes, polarization resistance and corrosion rates were obtained from electrochemical testing and evaluated. Increasing temperatures was found to lead to increasing corrosion rates for all samples. The data also revealed increased corrosion from sodium perrhenate on the mild steel A285 samples. The perrhenate anion (ReO4-) formed a redox couple with iron in the mild steel and accelerated metal dissolution that increased with temperature. Pitting and uniform corrosion was observed in the A285 and A537 mild steel samples. The A537 mild steel, however, displayed lower corrosion rates in the presence of perrhenate compared in the absence of perrhenate. A hypothesis has been proposed to explain the differences between the two alloys.

Comparison of corrosion performance and mechanisms of Al-Cu alloys with and without Li addition

NASA Astrophysics Data System (ADS)

Henon, Christine; Rouault, Sacha

The corrosion behaviour (intergranular corrosion, exfoliation and SCC) of alloy 2050 (AlCuLi) has been evaluated as a function of tempering and compared with some 2xxx Li free alloys. They show a similar qualitative behaviour: sensitivity to corrosion in underaged conditions, desensitization near peak age and re-sensitization in overaged conditions. The desentization can be rationalized on the basis of microstructural investigations and electrochemical measurements: preferential dissolution in underaged conditions is attributed to a Cu depleted zone near grain boundary. The re-sensitization in an overaged temper needs further investigations.

Effect of Annealing Treatments on the Microstructure, Mechanical Properties and Corrosion Behavior of Direct Metal Laser Sintered Ti-6Al-4V

NASA Astrophysics Data System (ADS)

Xu, Yangzi; Lu, Yuan; Sundberg, Kristin L.; Liang, Jianyu; Sisson, Richard D.

2017-05-01

An experimental investigation on the effects of post-annealing treatments on the microstructure, mechanical properties and corrosion behavior of direct metal laser sintered Ti-6Al-4V alloys has been conducted. The microstructure and phase evolution as affected by annealing treatment temperature were examined through scanning electron microscopy and x-ray diffraction. The tensile properties and Vickers hardness were measured and compared to the commercial Grade 5 Ti-6Al-4V alloy. Corrosion behavior of the parts was analyzed electrochemically in simulated body fluid at 37 °C. It was found out that the as-printed parts mainly composed of non-equilibrium α' phase. Annealing treatment allowed the transformation from α' to α phase and the development of β phase. The tensile test results indicated that post-annealing treatment could improve the ductility and decrease the strength. The as-printed Ti-6Al-4V part exhibits inferior corrosion resistance compared to the commercial alloy, and post-annealing treatment can reduce its susceptibility to corrosion by reducing the two-phase interface area.

Evaluation of Non-Chromate Passivations on Electroplated gamma-Phase Zinc Nickel

NASA Astrophysics Data System (ADS)

Volz, Steven Michael

This research focused on the corrosion response and electrochemical behavior of electroplated low hydrogen embrittlement alkaline gamma-phase zinc nickel with passivation layers. The motivation was the need to replace hexavalent chromium conversion coatings in military grade electrical systems with a more environment friendly alternative. The passivation layers were employed for the purpose of mitigating corrosion attack while maintaining low contact resistance. Trivalent chromium-based passivations and cerium-based passivations were compared against the currently used hexavalent chromium conversion coating. The coating systems were compared using electrochemical impedance spectroscopy, cyclic potentiodymanic scans, salt spray exposure testing, electrical resistance measurements, microstructure analysis, and compositional analysis. Coating systems with lower open circuit had a lower corrosion current and performed better during salt spray testing. All of the systems evaluated had corrosion products consistent with oxidized zinc compounds but the morphology of the passivation was dependent on the passivation. The electrical contact resistance ranged from 1 to 108 mO/cm 2, after salt spray testing. Two versions of Trivalent chromium-based passivations, were able to meet military performance specifications after corrosion testing.

NASA's Beachside Corrosion Test Site and Current Environmentally Friendly Corrosion Control Initiatives

NASA Technical Reports Server (NTRS)

Russell, Richard W.; Calle, Luz Marina; Johnston, Frederick; Montgomery, Eliza L.; Curran, Jerome P.; Kolody, Mark R.

2013-01-01

NASA began corrosion studies at the Kennedy Space Center (KSC) in 1966 during the Gemini/Apollo Programs with the evaluation of long-term corrosion protective coatings for carbon steel. KSC's Beachside Corrosion Test Site (BCTS), which has been documented by the American Society of Materials (ASM) as one of the most corrosive, naturally occurring, environments in the world, was established at that time. With the introduction of the Space Shuttle in 1981, the already highly corrosive conditions at the launch pad were rendered even more severe by the acid ic exhaust from the solid rocket boosters. In the years that followed, numerous studies have identified materials, coatings, and maintenance procedures for launch hardware and equipment exposed to the highly corrosive environment at the launch pad. This paper presents a historical overview of over 45 years of corrosion and coating evaluation studies and a description of the BCTS's current capabilities. Additionally, current research and testing programs involving chromium free coatings, environmentally friendly corrosion preventative compounds, and alternates to nitric acid passivation will be discussed.

Thermal Spray Coatings for High-Temperature Corrosion Protection in Biomass Co-Fired Boilers

NASA Astrophysics Data System (ADS)

Oksa, M.; Metsäjoki, J.; Kärki, J.

2015-01-01

There are over 1000 biomass boilers and about 500 plants using waste as fuel in Europe, and the numbers are increasing. Many of them encounter serious problems with high-temperature corrosion due to detrimental elements such as chlorides, alkali metals, and heavy metals. By HVOF spraying, it is possible to produce very dense and well-adhered coatings, which can be applied for corrosion protection of heat exchanger surfaces in biomass and waste-to-energy power plant boilers. Four HVOF coatings and one arc sprayed coating were exposed to actual biomass co-fired boiler conditions in superheater area with a probe measurement installation for 5900 h at 550 and 750 °C. The coating materials were Ni-Cr, IN625, Fe-Cr-W-Nb-Mo, and Ni-Cr-Ti. CJS and DJ Hybrid spray guns were used for HVOF spraying to compare the corrosion resistance of Ni-Cr coating structures. Reference materials were ferritic steel T92 and nickel super alloy A263. The circulating fluidized bed boiler burnt a mixture of wood, peat and coal. The coatings showed excellent corrosion resistance at 550 °C compared to the ferritic steel. At higher temperature, NiCr sprayed with CJS had the best corrosion resistance. IN625 was consumed almost completely during the exposure at 750 °C.

KCl-Induced High-Temperature Corrosion Behavior of HVAF-Sprayed Ni-Based Coatings in Ambient Air

NASA Astrophysics Data System (ADS)

Jafari, Reza; Sadeghimeresht, Esmaeil; Farahani, Taghi Shahrabi; Huhtakangas, Matti; Markocsan, Nicolaie; Joshi, Shrikant

2018-02-01

KCl-induced high-temperature corrosion behavior of four HVAF-sprayed Ni-based coatings (Ni21Cr, Ni5Al, Ni21Cr7Al1Y and Ni21Cr9Mo) under KCl deposit has been investigated in ambient air at 600 °C up to 168 h. The coatings were deposited onto 16Mo3 steel—a widely used boiler tube material. Uncoated substrate, 304L and Sanicro 25 were used as reference materials in the test environment. SEM/EDS and XRD techniques were utilized to characterize the as-sprayed and exposed samples. The results showed that the small addition of KCl significantly accelerated degradation to the coatings. All coatings provided better corrosion resistance compared to the reference materials. The alumina-forming Ni5Al coating under KCl deposit was capable of forming a more protective oxide scale compared to the chromia-forming coatings as penetration of Cl through diffusion paths was hindered. Both active corrosion and chromate formation mechanisms were found to be responsible for the corrosion damages. The corrosion resistance of the coatings based on the microstructure analysis and kinetics had the following ranking (from the best to worst): Ni5Al > Ni21Cr > Ni21Cr7Al1Y > Ni21Cr9Mo.

Corrosion behavior and microstructures of experimental Ti-Au alloys.

PubMed

Takahashi, Masatoshi; Kikuchi, Masafumi; Takada, Yukyo; Okuno, Osamu; Okabe, Toru

2004-06-01

Anodic polarization was performed in 0.9% NaCl and 1% lactic acid solutions to characterize the relationship between the corrosion behavior and microstructures of cast Ti-Au (5-40%) alloys. An abrupt increase in the current density occurred at approximately 0.6 V vs. SCE for the 30% and 40% Au alloys in the 0.9% NaCl solution. The microstructures after corrosion testing indicated that this breakdown may have been caused by the preferential dissolution of the Ti3Au. However, the potential for preferential dissolution was higher than the breakdown potential of stainless steel or Co-Cr alloy, which meant that the corrosion resistance of the Ti-Au alloys was superior. In 1% lactic acid solution, the corrosion resistance of the Ti-Au alloys was excellent, with no breakdown at any composition. In the present test solutions, the Ti-Au alloys up to 20% Au had good corrosion resistance comparable to that for pure titanium.

Corrosion Behavior of Aqua-Blasted and Laser-Engraved Type 316L Stainless Steel

NASA Astrophysics Data System (ADS)

Krawczyk, B.; Cook, P.; Hobbs, J.; Engelberg, D. L.

2017-12-01

The effect of aqua blasting and laser engraving on surface microstructure development, residual stress and corrosion resistance of type 316L stainless steel has been investigated. Aqua blasting resulted in a deformed near-surface microstructure containing compressive residual stresses. Subsequent laser engraving produced a surface layer with tensile residual stresses reaching to a depth of 200 microns. Changes of surface roughness topography were accompanied by the development of a thick oxide/hydroxide film after laser engraving. The atmospheric corrosion behavior of all surfaces with MgCl2-laden droplets was compared to their electrochemical response in 1M NaCl and 0.7 M HCl aqueous solutions. The measured total volume loss after atmospheric corrosion testing was similar for all investigated surface conditions. Laser-engraved surface exhibited the smallest number of corrosion sites, but the largest mean corrosion depth.

Reliability-based management of buried pipelines considering external corrosion defects

NASA Astrophysics Data System (ADS)

Miran, Seyedeh Azadeh

Corrosion is one of the main deteriorating mechanisms that degrade the energy pipeline integrity, due to transferring corrosive fluid or gas and interacting with corrosive environment. Corrosion defects are usually detected by periodical inspections using in-line inspection (ILI) methods. In order to ensure pipeline safety, this study develops a cost-effective maintenance strategy that consists of three aspects: corrosion growth model development using ILI data, time-dependent performance evaluation, and optimal inspection interval determination. In particular, the proposed study is applied to a cathodic protected buried steel pipeline located in Mexico. First, time-dependent power-law formulation is adopted to probabilistically characterize growth of the maximum depth and length of the external corrosion defects. Dependency between defect depth and length are considered in the model development and generation of the corrosion defects over time is characterized by the homogenous Poisson process. The growth models unknown parameters are evaluated based on the ILI data through the Bayesian updating method with Markov Chain Monte Carlo (MCMC) simulation technique. The proposed corrosion growth models can be used when either matched or non-matched defects are available, and have ability to consider newly generated defects since last inspection. Results of this part of study show that both depth and length growth models can predict damage quantities reasonably well and a strong correlation between defect depth and length is found. Next, time-dependent system failure probabilities are evaluated using developed corrosion growth models considering prevailing uncertainties where three failure modes, namely small leak, large leak and rupture are considered. Performance of the pipeline is evaluated through failure probability per km (or called a sub-system) where each subsystem is considered as a series system of detected and newly generated defects within that sub-system. Sensitivity analysis is also performed to determine to which incorporated parameter(s) in the growth models reliability of the studied pipeline is most sensitive. The reliability analysis results suggest that newly generated defects should be considered in calculating failure probability, especially for prediction of long-term performance of the pipeline and also, impact of the statistical uncertainty in the model parameters is significant that should be considered in the reliability analysis. Finally, with the evaluated time-dependent failure probabilities, a life cycle-cost analysis is conducted to determine optimal inspection interval of studied pipeline. The expected total life-cycle costs consists construction cost and expected costs of inspections, repair, and failure. The repair is conducted when failure probability from any described failure mode exceeds pre-defined probability threshold after each inspection. Moreover, this study also investigates impact of repair threshold values and unit costs of inspection and failure on the expected total life-cycle cost and optimal inspection interval through a parametric study. The analysis suggests that a smaller inspection interval leads to higher inspection costs, but can lower failure cost and also repair cost is less significant compared to inspection and failure costs.

Vibrational Spectroscopy in Studies of Atmospheric Corrosion

PubMed Central

Hosseinpour, Saman; Johnson, Magnus

2017-01-01

Vibrational spectroscopy has been successfully used for decades in studies of the atmospheric corrosion processes, mainly to identify the nature of corrosion products but also to quantify their amounts. In this review article, a summary of the main achievements is presented with focus on how the techniques infrared spectroscopy, Raman spectroscopy, and vibrational sum frequency spectroscopy can be used in the field. Several different studies have been discussed where these instruments have been used to assess both the nature of corrosion products as well as the properties of corrosion inhibitors. Some of these techniques offer the valuable possibility to perform in-situ measurements in real time on ongoing corrosion processes, which allows the kinetics of formation of corrosion products to be studied, and also minimizes the risk of changing the surface properties which may occur during ex-situ experiments. Since corrosion processes often occur heterogeneously over a surface, it is of great importance to obtain a deeper knowledge about atmospheric corrosion phenomena on the nano scale, and this review also discusses novel vibrational microscopy techniques allowing spectra to be acquired with a spatial resolution of 20 nm. PMID:28772781

Relationship between H2 sorption properties and aqueous corrosion mechanisms in A2Ni7 hydride forming alloys (A = Y, Gd or Sm)

NASA Astrophysics Data System (ADS)

Charbonnier, Véronique; Monnier, Judith; Zhang, Junxian; Paul-Boncour, Valérie; Joiret, Suzanne; Puga, Beatriz; Goubault, Lionel; Bernard, Patrick; Latroche, Michel

2016-09-01

Intermetallic compounds A2B7 (A = rare earth, B = transition metal) are of interest for Ni-MH batteries. Indeed they are able to absorb hydrogen reversibly and exhibit good specific capacity in electrochemical route. To understand the effect of rare earth on properties of interest such as thermodynamic, cycling stability and corrosion, we synthesized and studied three compounds: Y2Ni7, Gd2Ni7 and Sm2Ni7. Using Sieverts' method, we plot P-c-isotherms up to 10 MPa and study hydride stability upon solid-gas cycling. Electrochemical cycling was also performed, as well as calendar and cycling corrosion study. Corrosion products were characterized by means of X-ray diffraction, electron diffraction, Raman micro-spectroscopy and scanning and transmission electron microscopies. Magnetic measurements were also performed to calculate corrosion rates. A corrosion mechanism, based on the nature of corrosion products, is proposed. By combining results from solid-gas cycling, electrochemical cycling and corrosion study, we attribute the loss in capacity either to corrosion or loss of crystallinity.

Simulation on the steel galvanic corrosion and acoustic emission

NASA Astrophysics Data System (ADS)

Yu, Yang; Shi, Xin; Yang, Ping

2015-12-01

Galvanic corrosion is a very destructive localized corrosion. The research on galvanic corrosion could determine equipment corrosion and prevent the accidents occurrence. Steel corrosion had been studied by COMSOL software with mathematical modeling. The galvanic corrosion of steel-aluminum submerged into 10% sodium chloride solution had been on-line detected by PIC-2 acoustic emission system. The results show that the acoustic emission event counts detected within unit time can qualitative judge galvanic corrosion rate and further erosion trend can be judged by the value changes.

Corrosion Performance of Fe-Based Alloys in Simulated Oxy-Fuel Environment

DOE Office of Scientific and Technical Information (OSTI.GOV)

Zeng, Zuotao; Natesan, Ken; Cai, Zhonghou

The long-term corrosion of Fe-based alloys in simulated oxy-fuel environment at 1023 K (750 A degrees C) was studied. Detailed results are presented on weight change, scale thickness, internal penetration, microstructural characteristics of the corrosion products, and the cracking of scales for the alloys after exposure at 1023 K (750 A degrees C) for up to 3600 hours. An incubation period during which the corrosion rate was low was observed for the alloys. After the incubation period, the corrosion accelerated, and the corrosion process followed linear kinetics. Effects of alloy, CaO-containing ash, and gas composition on the corrosion rate weremore » also studied. In addition, synchrotron nanobeam X-ray analysis was employed to determine the phase and chemical composition of the oxide layers on the alloy surface. Results from these studies are being used to address the long-term corrosion performance of Fe-based alloys in various coal-ash combustion environments and to develop methods to mitigate high-temperature ash corrosion.« less

Cyclic Oxidation and Hot Corrosion Behavior of Nickel-Iron-Based Superalloy

NASA Astrophysics Data System (ADS)

Chellaganesh, D.; Adam Khan, M.; Winowlin Jappes, J. T.; Sathiyanarayanan, S.

2018-01-01

The high temperature oxidation and hot corrosion behavior of nickel-iron-based superalloy are studied at 900 ° and 1000 °C. The significant role of alloying elements with respect to the exposed medium is studied in detail. The mass change per unit area was catastrophic for the samples exposed at 1000 °C and gradual increase in mass change was observed at 900 °C for both the environments. The exposed samples were further investigated with SEM, EDS and XRD analysis to study the metallurgical characteristics. The surface morphology has expressed the in situ nature of the alloy and its affinity toward the environment. The EDS and XRD analysis has evidently proved the presence of protective oxides formation on prolonged exposure at elevated temperature. The predominant oxide formed during the exposure at high temperature has a major contribution toward the protection of the samples. The nickel-iron-based superalloy is less prone to oxidation and hot corrosion when compared to the existing alloy in gas turbine engine simulating marine environment.

An alternate to chromate conversion coatings for the corrosion protection of aluminum 2024-T3

NASA Astrophysics Data System (ADS)

Guo, Ruiguang

Corrosion of high-strength aluminum alloys used for airspace application is an expensive and serious problem. The most significant environmental factor contributing to the corrosion of these alloys is water condensed from humid air and contaminated with soluble chloride salts. The Al 2024 series used for aircraft are particularly susceptible to corrosion in aqueous chloride solutions due to alloying constituents such as copper and other impurities. Chromates are efficient inhibitors of corrosion of aluminum in near neutral aqueous environments containing aggressive anions such as chlorides. Usually, aluminum alloys are initially protected by chromate conversion coatings. Additional polymer coatings are sometimes added during exposure to corrosive atmospheres such as marine environments. Although chromate coatings are widely used, they require the use of noxious solutions, so they have always presented effluent disposal problems. There are health and safety concerns over the use of chromates due to their toxicity and carcinogenic nature and, as a consequence, the environmental and health risks associated with the use of such coatings will be restricted in the future. It was these health and safety concerns that led to the development of alternative non-toxic coating processes with comparable adhesion properties and corrosion protection. A variety of process technologies are under development and are vying for acceptance in industrial markets. As an alternate conversion coating, a new titanate conversion coating was systematically researched and developed. Research concentrated on producing passive surfaces from a simple titanate solution using an immersion process. The corrosion resistance of the treated surface has been evaluated using simple, rapid electrochemical techniques as well as a more long-term salt spray test. Passivation by titanate conversion treatment exhibits many similarities to chromate conversion treatment. Based on this study of corrosion protection of the titanate coating formed at different conditions, a possible formation mechanism of a titanate coating is proposed. A conclusion may be drawn that titanate coating seems to be a viable alternative to chromate coatings.

Morphological and physicochemical characteristics of iron corrosion scales formed under different water source histories in a drinking water distribution system.

PubMed

Yang, Fan; Shi, Baoyou; Gu, Junnong; Wang, Dongsheng; Yang, Min

2012-10-15

The corrosion scales on iron pipes could have great impact on the water quality in drinking water distribution systems (DWDS). Unstable and less protective corrosion scale is one of the main factors causing "discolored water" issues when quality of water entering into distribution system changed significantly. The morphological and physicochemical characteristics of corrosion scales formed under different source water histories in duration of about two decades were systematically investigated in this work. Thick corrosion scales or densely distributed corrosion tubercles were mostly found in pipes transporting surface water, but thin corrosion scales and hollow tubercles were mostly discovered in pipes transporting groundwater. Magnetite and goethite were main constituents of iron corrosion products, but the mass ratio of magnetite/goethite (M/G) was significantly different depending on the corrosion scale structure and water source conditions. Thick corrosion scales and hard shell of tubercles had much higher M/G ratio (>1.0), while the thin corrosion scales had no magnetite detected or with much lower M/G ratio. The M/G ratio could be used to identify the characteristics and evaluate the performances of corrosion scales formed under different water conditions. Compared with the pipes transporting ground water, the pipes transporting surface water were more seriously corroded and could be in a relatively more active corrosion status all the time, which was implicated by relatively higher siderite, green rust and total iron contents in their corrosion scales. Higher content of unstable ferric components such as γ-FeOOH, β-FeOOH and amorphous iron oxide existed in corrosion scales of pipes receiving groundwater which was less corroded. Corrosion scales on groundwater pipes with low magnetite content had higher surface area and thus possibly higher sorption capacity. The primary trace inorganic elements in corrosion products were Br and heavy metals. Corrosion products obtained from pipes transporting groundwater had higher levels of Br, Ti, Ba, Cu, Sr, V, Cr, La, Pb and As. Copyright © 2012 Elsevier Ltd. All rights reserved.

49 CFR 195.573 - What must I do to monitor external corrosion control?

Code of Federal Regulations, 2010 CFR

2010-10-01

... circumstances in which a close-interval survey or comparable technology is practicable and necessary to... corrosion by electrical survey, or where an electrical survey is impractical, by other means that include...

49 CFR 195.573 - What must I do to monitor external corrosion control?

Code of Federal Regulations, 2012 CFR

2012-10-01

... circumstances in which a close-interval survey or comparable technology is practicable and necessary to... corrosion by electrical survey, or where an electrical survey is impractical, by other means that include...

49 CFR 195.573 - What must I do to monitor external corrosion control?

Code of Federal Regulations, 2011 CFR

2011-10-01

... circumstances in which a close-interval survey or comparable technology is practicable and necessary to... corrosion by electrical survey, or where an electrical survey is impractical, by other means that include...

Structural Characteristics and In Vitro Biodegradation of a Novel Zn-Li Alloy Prepared by Induction Melting and Hot Rolling

NASA Astrophysics Data System (ADS)

Zhao, Shan; McNamara, Cameron T.; Bowen, Patrick K.; Verhun, Nicholas; Braykovich, Jacob P.; Goldman, Jeremy; Drelich, Jaroslaw W.

2017-03-01

Zinc shows great promise as a bioabsorbable metal; however, the low tensile strength of pure zinc limits its application for endovascular stent purposes. In this study, a new Zn- xLi alloy (with x = 2, 4, 6 at. pct) was prepared by induction melting in an argon atmosphere and processed through hot rolling. Structures of the formulated binary alloys were characterized by X-ray diffraction and optical microscopy. Mechanical testing showed that the incorporation of Li into Zn increased ultimate tensile strength from <120 MPa (pure Zn) to >560 MPa ( x = 6 at. pct). In vitro corrosion behavior was evaluated by immersion tests in simulated body fluid. The Zn-2Li and Zn-4Li corrosion study demonstrated that corrosion rates and products resemble those observed for pure Zn in vivo, and in addition, the Zn-4Li alloy exhibits higher resistance to corrosion as compared to Zn-2Li. The findings herein encourage further exploration of Zn-Li systems for structural use in biomedical vascular support applications with the ultimate goal of simplifying stent procedures, thereby reducing stent-related complications.

Corrosion behavior of plasma-sprayed Al 2O 3-Cr 2O 3 coatings in hot lithium molten salt

NASA Astrophysics Data System (ADS)

Cho, Soo Haeng; Park, Sung Bin; Kang, Dae Seong; Jeong, Myeong Soo; Park, Heong; Hur, Jin Mok; Lee, Han Soo

2010-04-01

In this study, hot corrosion studies were performed on bare as well as coated superalloy specimens after exposure to molten lithium chloride environment at 675 °C for 216 h under an oxidizing atmosphere. The substrates of the IN713LC superalloy specimens were sprayed with an aluminized NiCrAlY bond coat and then with an Al 2O 3-Cr 2O 3 top coat. The as-coated and tested specimens were examined by optical microscopy (OM), scanning electron microscopy (SEM)/X-ray energy dispersive spectrometry (EDS) and X-ray diffraction (XRD), respectively. The bare superalloy reveals an obvious weight loss, and the scale formed on the surface of the bare superalloy was spalled due to the rapid scale growth and thermal stress. The top coatings showed a much better hot corrosion resistance in the presence of LiCl-3 wt.% Li 2O molten salt when compared with those of the uncoated superalloy and the aluminized bond coatings. These coatings have been found to be beneficial for increasing to the hot corrosion resistance of the structural materials for handling high temperature lithium molten salts.

Events as power source: wireless sustainable corrosion monitoring.

PubMed

Sun, Guodong; Qiao, Guofu; Zhao, Lin; Chen, Zhibo

2013-12-17

This study presents and implements a corrosion-monitoring wireless sensor platform, EPS (Events as Power Source), which monitors the corrosion events in reinforced concrete (RC) structures, while being powered by the micro-energy released from the corrosion process. In EPS, the proposed corrosion-sensing device serves both as the signal source for identifying corrosion and as the power source for driving the sensor mote, because the corrosion process (event) releases electric energy; this is a novel idea proposed by this study. For accumulating the micro-corrosion energy, we integrate EPS with a COTS (Commercial Off-The-Shelf) energy-harvesting chip that recharges a supercapacitor. In particular, this study designs automatic energy management and adaptive transmitted power control polices to efficiently use the constrained accumulated energy. Finally, a set of preliminary experiments based on concrete pore solution are conducted to evaluate the feasibility and the efficacy of EPS.

In vitro biocorrosion of Co-Cr-Mo implant alloy by macrophage cells.

PubMed

Lin, Hsin-Yi; Bumgardner, Joel D

2004-11-01

We hypothesized that macrophage cells and their released reactive chemical species (RCS) affect Co-Cr-Mo alloy's corrosion properties and that alloy corrosion products change macrophage cell behavior. A custom cell culture corrosion cell was used to evaluate how culture medium, cells, and RCS altered alloy corrosion in 3-day tests. Corrosion was evaluated by measuring total charge transfer at a constant potential using a potentiostat and metal ion release by atomic emission spectroscopy. Viability, proliferation, and NO (nitric oxide) and IL-1beta (interlukin-1beta) release were used to assess cellular response to alloy corrosion products. In the presence of activated cells, total charge transfers and Co ion release were the lowest (p < 0.05). This was attributed to an enhancement of the surface oxide by RCS. Cr and Mo release were not different between cells and activated cells. Low levels of metal ions did not affect cell viability, proliferation, or NO release, though IL-1beta released from the activated cells was higher on the alloy compared to the controls. These data support the hypothesis that macrophage cells and their RCS affect alloy corrosion. Changes in alloy corrosion by cells may be important to the development of host responses to the alloy and its corrosion products.

The effects of argon ion bombardment on the corrosion resistance of tantalum

NASA Astrophysics Data System (ADS)

Ramezani, A. H.; Sari, A. H.; Shokouhy, A.

2017-02-01

Application of ion beam has been widely used as a surface modification method to improve surface properties. This paper investigates the effect of argon ion implantation on surface structure as well as resistance against tantalum corrosion. In this experiment, argon ions with energy of 30 keV and in doses of 1 × 1017-10 × 1017 ions/cm2 were used. The surface bombardment with inert gases mainly produces modified topography and morphology of the surface. Atomic Force Microscopy was also used to patterned the roughness variations prior to and after the implantation phase. Additionally, the corrosion investigation apparatus wear was applied to compare resistance against tantalum corrosion both before and after ion implantation. The results show that argon ion implantation has a substantial impact on increasing resistance against tantalum corrosion. After the corrosion test, scanning electron microscopy (SEM) analyzed the samples' surface morphologies. In addition, the elemental composition is characterized by energy-dispersive X-ray (EDX) analysis. The purpose of this paper was to obtain the perfect condition for the formation of tantalum corrosion resistance. In order to evaluate the effect of the ion implantation on the corrosion behavior, potentiodynamic tests were performed. The results show that the corrosion resistance of the samples strongly depends on the implantation doses.

Uniform Corrosion and General Dissolution of Aluminum Alloys 2024-T3, 6061-T6, and 7075-T6

NASA Astrophysics Data System (ADS)

Huang, I.-Wen

Uniform corrosion and general dissolution of aluminum alloys was not as well-studied in the past, although it was known for causing significant amount of weight loss. This work comprises four chapters to understand uniform corrosion of aluminum alloys 2024-T3, 6061-T6, and 7075-T6. A preliminary weight loss experiment was performed for distinguishing corrosion induced weight loss attributed to uniform corrosion and pitting corrosion. The result suggested that uniform corrosion generated a greater mass loss than pitting corrosion. First, to understand uniform corrosion mechanism and kinetics in different environments, a series of static immersion tests in NaCl solutions were performed to provide quantitative measurement of uniform corrosion. Thereafter, uniform corrosion development as a function of temperature, pH, Cl-, and time was investigated to understand the influence of environmental factors. Faster uniform corrosion rate has been found at lower temperature (20 and 40°C) than at higher temperature (60 and 80°C) due to accelerated corrosion product formation at high temperatures inhibiting corrosion reactions. Electrochemical tests including along with scanning electron microscopy (SEM) were utilized to study the temperature effect. Second, in order to further understand the uniform corrosion influence on pit growth kinetics, a long term exposures for 180 days in both immersion and ASTM-B117 test were performed. Uniform corrosion induced surface recession was found to have limited impact on pit geometry regardless of exposure methods. It was also found that the competition for limited cathodic current from uniform corrosion the primary rate limiting factor for pit growth. Very large pits were found after uniform corrosion growth reached a plateau due to corrosion product coverage. Also, optical microscopy and focused ion beam (FIB) imaging has provided more insights of distinctive pitting geometry and subsurface damages found from immersion samples and B117 samples. Although uniform corrosion was studied in various electrolytes, the pH impact was still difficult to discern due to ongoing cathodic reactions that changed electrolyte pH with time. Therefore, buffered pH electrolytes with pH values of 3, 5, 8, and 10 were prepared static immersion tests. Electrochemical experiments were performed in each buffered pH conditions for understanding corrosion mechanisms. Uniform corrosion was found exhibiting higher corrosion rate in buffered acidic and alkaline electrolytes due to pH- and temperature-dependent corrosion product precipitation. Observations were supported by electrochemical, SEM, and EDS observations. Due to the complexity of corrosion data, a reliable corrosion prediction based on empirical observations could be challenging. Artificial neural network (ANN) modeling was used for corrosion data pattern recognition by mimicking human neural network systems. Predictive models were developed based on corrosion data acquired in this study. The model was adaptable through iteratively update its prediction by error minimization during the training phase. Trained ANN model can predict uniform corrosion successfully. In addition to ANN, fuzzy curve analysis was utilized to rank the influence of each input (temperature, pH, Cl-, and time). For example, temperature and pH were found to be the most influential parameters to uniform corrosion. This information can provide feedback for ANN improvement, also known as "data pruning".

Anaerobic hydrocarbon and fatty acid metabolism by syntrophic bacteria and their impact on carbon steel corrosion.

PubMed

Lyles, Christopher N; Le, Huynh M; Beasley, William Howard; McInerney, Michael J; Suflita, Joseph M

2014-01-01

The microbial metabolism of hydrocarbons is increasingly associated with the corrosion of carbon steel in sulfate-rich marine waters. However, how such transformations influence metal biocorrosion in the absence of an electron acceptor is not fully recognized. We grew a marine alkane-utilizing, sulfate-reducing bacterium, Desulfoglaeba alkanexedens, with either sulfate or Methanospirillum hungatei as electron acceptors, and tested the ability of the cultures to catalyze metal corrosion. Axenically, D. alkanexedens had a higher instantaneous corrosion rate and produced more pits in carbon steel coupons than when the same organism was grown in syntrophic co-culture with the methanogen. Since anaerobic hydrocarbon biodegradation pathways converge on fatty acid intermediates, the corrosive ability of a known fatty acid-oxidizing syntrophic bacterium, Syntrophus aciditrophicus was compared when grown in pure culture or in co-culture with a H2-utilizing sulfate-reducing bacterium (Desulfovibrio sp., strain G11) or a methanogen (M. hungatei). The instantaneous corrosion rates in the cultures were not substantially different, but the syntrophic, sulfate-reducing co-culture produced more pits in coupons than other combinations of microorganisms. Lactate-grown cultures of strain G11 had higher instantaneous corrosion rates and coupon pitting compared to the same organism cultured with hydrogen as an electron donor. Thus, if sulfate is available as an electron acceptor, the same microbial assemblages produce sulfide and low molecular weight organic acids that exacerbated biocorrosion. Despite these trends, a surprisingly high degree of variation was encountered with the corrosion assessments. Differences in biomass, initial substrate concentration, rates of microbial activity or the degree of end product formation did not account for the variations. We are forced to ascribe such differences to the metallurgical properties of the coupons.

Sulfur recirculation for increased electricity production in Waste-to-Energy plants.

PubMed

Andersson, Sven; Blomqvist, Evalena W; Bäfver, Linda; Jones, Frida; Davidsson, Kent; Froitzheim, Jan; Karlsson, Martin; Larsson, Erik; Liske, Jesper

2014-01-01

Sulfur recirculation is a new technology for reducing boiler corrosion and dioxin formation. It was demonstrated in full-scale tests at a Waste to Energy plant in Göteborg (Sweden) during nearly two months of operation. Sulfur was recirculated as sulfuric acid from the flue gas cleaning back to the boiler, thus creating a sulfur loop. The new technology was evaluated by extensive measurement campaigns during operation under normal conditions (reference case) and operation with sulfur recirculation. The chlorine content of both fly ash and boiler ash decreased and the sulfur content increased during the sulfur recirculation tests. The deposit growth and the particle concentration decreased with sulfur recirculation and the dioxin concentration (I-TEQ) of the flue gas was reduced by approximately 25%. Sulfuric acid dew point measurements showed that the sulfuric acid dosage did not lead to elevated SO3 concentrations, which may otherwise induce low temperature corrosion. In the sulfur recirculation corrosion probe exposures, the corrosion rate decreased for all tested materials (16Mo3, Sanicro 28 and Inconel 625) and material temperatures (450 °C and 525 °C) compared to the reference exposure. The corrosion rates were reduced by 60-90%. Sulfur recirculation prevented the formation of transition metal chlorides at the metal/oxide interface, formation of chromate and reduced the presence of zinc in the corrosion products. Furthermore, measured corrosion rates at 525 °C with sulfur recirculation in operation were similar or lower compared to those measured at 450 °C material temperature in reference conditions, which corresponds to normal operation at normal steam temperatures. This implies that sulfur recirculation allows for higher steam data and electricity production without increasing corrosion. Copyright © 2013 The Authors. Published by Elsevier Ltd.. All rights reserved.

Anaerobic hydrocarbon and fatty acid metabolism by syntrophic bacteria and their impact on carbon steel corrosion

PubMed Central

Lyles, Christopher N.; Le, Huynh M.; Beasley, William Howard; McInerney, Michael J.; Suflita, Joseph M.

2014-01-01

The microbial metabolism of hydrocarbons is increasingly associated with the corrosion of carbon steel in sulfate-rich marine waters. However, how such transformations influence metal biocorrosion in the absence of an electron acceptor is not fully recognized. We grew a marine alkane-utilizing, sulfate-reducing bacterium, Desulfoglaeba alkanexedens, with either sulfate or Methanospirillum hungatei as electron acceptors, and tested the ability of the cultures to catalyze metal corrosion. Axenically, D. alkanexedens had a higher instantaneous corrosion rate and produced more pits in carbon steel coupons than when the same organism was grown in syntrophic co-culture with the methanogen. Since anaerobic hydrocarbon biodegradation pathways converge on fatty acid intermediates, the corrosive ability of a known fatty acid-oxidizing syntrophic bacterium, Syntrophus aciditrophicus was compared when grown in pure culture or in co-culture with a H2-utilizing sulfate-reducing bacterium (Desulfovibrio sp., strain G11) or a methanogen (M. hungatei). The instantaneous corrosion rates in the cultures were not substantially different, but the syntrophic, sulfate-reducing co-culture produced more pits in coupons than other combinations of microorganisms. Lactate-grown cultures of strain G11 had higher instantaneous corrosion rates and coupon pitting compared to the same organism cultured with hydrogen as an electron donor. Thus, if sulfate is available as an electron acceptor, the same microbial assemblages produce sulfide and low molecular weight organic acids that exacerbated biocorrosion. Despite these trends, a surprisingly high degree of variation was encountered with the corrosion assessments. Differences in biomass, initial substrate concentration, rates of microbial activity or the degree of end product formation did not account for the variations. We are forced to ascribe such differences to the metallurgical properties of the coupons. PMID:24744752

Chemical passivation as a method of improving the electrochemical corrosion resistance of Co-Cr-based dental alloy.

PubMed

Rylska, Dorota; Sokołowski, Grzegorz; Sokołowski, Jerzy; Łukomska-Szymańska, Monika

2017-01-01

The purpose of the study was to evaluate corrosion resistance of Wirobond C® alloy after chemical passivation treatment. The alloy surface undergone chemical passivation treatment in four different media. Corrosion studies were carried out by means of electrochemical methods in saline solution. Corrosion effects were determined using SEM. The greatest increase in the alloy polarization resistance was observed for passive layer produced in Na2SO4 solution with graphite. The same layer caused the highest increase in corrosion current. Generally speaking, the alloy passivation in Na2SO4 solution with graphite caused a substantial improvement of the corrosion resistance. The sample after passivation in Na2SO4 solution without graphite, contrary to others, lost its protective properties along with successive anodic polarization cycles. The alloy passivation in Na3PO4 solution with graphite was the only one that caused a decrease in the alloy corrosion properties. The SEM studies of all samples after chemical passivation revealed no pit corrosion - in contrast to the sample without any modification. Every successive polarization cycle in anodic direction of pure Wirobond C® alloy enhances corrosion resistance shifting corrosion potential in the positive direction and decreasing corrosion current value. The chemical passivation in solutions with low pH values decreases susceptibility to electrochemical corrosion of Co-Cr dental alloy. The best protection against corrosion was obtained after chemical passivation of Wirobond C® in Na2SO4 solution with graphite. Passivation with Na2SO4 in solution of high pH does not cause an increase in corrosion resistance of WIROBOND C. Passivation process increases alloy resistance to pit corrosion.

Caprylate Salts Based on Amines as Volatile Corrosion Inhibitors for Metallic Zinc: Theoretical and Experimental Studies.

PubMed

Valente, Marco A G; Teixeira, Deiver A; Azevedo, David L; Feliciano, Gustavo T; Benedetti, Assis V; Fugivara, Cecílio S

2017-01-01

The interaction of volatile corrosion inhibitors (VCI), caprylate salt derivatives from amines, with zinc metallic surfaces is assessed by density functional theory (DFT) computer simulations, electrochemical impedance (EIS) measurements and humid chamber tests. The results obtained by the different methods were compared, and linear correlations were obtained between theoretical and experimental data. The correlations between experimental and theoretical results showed that the molecular size is the determining factor in the inhibition efficiency. The models used and experimental results indicated that dicyclohexylamine caprylate is the most efficient inhibitor.

Biodegradable magnesium alloys for orthopaedic applications: A review on corrosion, biocompatibility and surface modifications.

PubMed

Agarwal, Sankalp; Curtin, James; Duffy, Brendan; Jaiswal, Swarna

2016-11-01

Magnesium (Mg) and its alloys have been extensively explored as potential biodegradable implant materials for orthopaedic applications (e.g. Fracture fixation). However, the rapid corrosion of Mg based alloys in physiological conditions has delayed their introduction for therapeutic applications to date. The present review focuses on corrosion, biocompatibility and surface modifications of biodegradable Mg alloys for orthopaedic applications. Initially, the corrosion behaviour of Mg alloys and the effect of alloying elements on corrosion and biocompatibility is discussed. Furthermore, the influence of polymeric deposit coatings, namely sol-gel, synthetic aliphatic polyesters and natural polymers on corrosion and biological performance of Mg and its alloy for orthopaedic applications are presented. It was found that inclusion of alloying elements such as Al, Mn, Ca, Zn and rare earth elements provides improved corrosion resistance to Mg alloys. It has been also observed that sol-gel and synthetic aliphatic polyesters based coatings exhibit improved corrosion resistance as compared to natural polymers, which has higher biocompatibility due to their biomimetic nature. It is concluded that, surface modification is a promising approach to improve the performance of Mg-based biomaterials for orthopaedic applications. Copyright © 2016 Elsevier B.V. All rights reserved.

On the in vitro biocompatibility of Elgiloy, a co-based alloy, compared to two titanium alloys.

PubMed

Es-Souni, Martha; Fischer-Brandies, Helge; Es-Souni, Mohammed

2003-01-01

The aim of the present investigation was to contribute to an understanding of the effects of surface topography and chemical composition on the corrosion behavior and thus the biocompatibility of Elgiloy (RMO, Denver, CO, USA), a common Co-based alloy. The results are compared with those obtained for a binary NiTi alloy, Neo Sentalloy (GAC, Central Islip, NY, USA) and a beta-III-Ti alloy, TMA (Ormco, Glendora, CA, USA). In the present study, the surface topography and the chemical composition of two different grades of Elgiloy, Blue Elgiloy (soft) and Yellow Elgiloy (ductile), were examined by means of scanning electron microscopy (SEM) and energy-dispersive spectroscopy analysis (EDS). Their corrosion behavior in half-strength Ringer solution and in an artificial saliva solution according to Barrett [1] was investigated using potentiodynamic corrosion testing (PDC). The photometry-based PAN method was used to quantify the released Ni and Co ions. The in vitro biocompatibility of the two grades of Elgiloy was tested in three different cell cultures: in L929, a commercially available mouse fibroblast cell line, and in primary human epithelial cells and fibroblasts. The results of the corrosion testing showed satisfactorily high pitting corrosion potentials but lower repassivation potentials and a strong increase in current density once pitting had occurred. The photometric results revealed the release of Ni and Co ions in both tested electrolytes. The tested native surfaces exhibited numerous grinding and polishing grooves, inclusions and inhomogeneities of the microstructure. After corrosion testing the same surfaces displayed numerous signs of corrosion, especially in areas with microstructural inhomogeneities. In vitro biocompatibility testing showed a substantially reduced dehydrogenase activity in the presence of Elgiloy. The reduced quality of surface finish resulting from the manufacturing process led in the case of the tested Elgiloy types to decreased corrosion resistance with consequently reduced in vitro biocompatibility. In this context it is also conceivable that patients with a proven allergy to nickel, cobalt or chromium may react sensitively to the deployment of this alloy, at least in the surface quality tested by us. From this aspect, the introduction of a binding standard for the surface quality of materials used in orthodontic appliances is urgently recommended.

Stress corrosion cracking of an aluminum alloy used in external fixation devices.

PubMed

Cartner, Jacob L; Haggard, Warren O; Ong, Joo L; Bumgardner, Joel D

2008-08-01

Treatment for compound and/or comminuted fractures is frequently accomplished via external fixation. To achieve stability, the compositions of external fixators generally include aluminum alloy components due to their high strength-to-weight ratios. These alloys are particularly susceptible to corrosion in chloride environments. There have been several clinical cases of fixator failure in which corrosion was cited as a potential mechanism. The aim of this study was to evaluate the effects of physiological environments on the corrosion susceptibility of aluminum 7075-T6, since it is used in orthopedic external fixation devices. Electrochemical corrosion curves and alternate immersion stress corrosion cracking tests indicated aluminum 7075-T6 is susceptible to corrosive attack when placed in physiological environments. Pit initiated stress corrosion cracking was the primary form of alloy corrosion, and subsequent fracture, in this study. Anodization of the alloy provided a protective layer, but also caused a decrease in passivity ranges. These data suggest that once the anodization layer is disrupted, accelerated corrosion processes occur. (c) 2007 Wiley Periodicals, Inc.

Biofilm-Growing Bacteria Involved in the Corrosion of Concrete Wastewater Pipes: Protocols for Comparative Metagenomic Analyses

EPA Science Inventory

Advances in high-throughput next-generation sequencing (NGS) technology for direct sequencing of environmental DNA (i.e. shotgun metagenomics) is transforming the field of microbiology. NGS technologies are now regularly being applied in comparative metagenomic studies, which pr...

Synergy effect of naphthenic acid corrosion and sulfur corrosion in crude oil distillation unit

NASA Astrophysics Data System (ADS)

Huang, B. S.; Yin, W. F.; Sang, D. H.; Jiang, Z. Y.

2012-10-01

The synergy effect of naphthenic acid corrosion and sulfur corrosion at high temperature in crude oil distillation unit was studied using Q235 carbon-manganese steel and 316 stainless steel. The corrosion of Q235 and 316 in corrosion media containing sulfur and/or naphthenic acid at 280 °C was investigated by weight loss, scanning electron microscope (SEM), EDS and X-ray diffractometer (XRD) analysis. The results showed that in corrosion media containing only sulfur, the corrosion rate of Q235 and 316 first increased and then decreased with the increase of sulfur content. In corrosion media containing naphthenic acid and sulfur, with the variations of acid value or sulfur content, the synergy effect of naphthenic acid corrosion and sulfur corrosion has a great influence on the corrosion rate of Q235 and 316. It was indicated that the sulfur accelerated naphthenic acid corrosion below a certain sulfur content but prevented naphthenic acid corrosion above that. The corrosion products on two steels after exposure to corrosion media were investigated. The stable Cr5S8 phases detected in the corrosion products film of 316 were considered as the reason why 316 has greater corrosion resistance to that of Q235.

Corrosion of orthodontic brackets in different spices: in vitro study.

PubMed

Chaturvedi, T P

2014-01-01

Moist environment in the mouth varies and causes variable amounts of corrosion of dental materials. This is of concern particularly when metallic implants, metallic fillings, orthodontic appliances are placed in the hostile electrolytic environment in the human mouth. Components of diet rich in salt and spices are important factors influencing the corrosion of metallic appliances placed in the oral cavity. To study in vitro corrosion of orthodontic metallic brackets immersed in solutions of salt and spices in artificial saliva. Orthodontic brackets were used for corrosion studies in artificial saliva, salt, and spices using electrochemical technique and surface analysis. Electrochemical studies using different parameters were done in solutions of artificial saliva containing salt and spices. Photomicrographs from the optical microscope were also obtained. RESULTS of corrosion studies have clearly demonstrated that certain spices such as turmeric and coriander are effective in reducing corrosion, whereas salt and red chili have been found to enhance it. Surface analysis of small pits present on the surface of the as-received bracket will initiate corrosion which leads to more pitting.

The Effects of Hot Corrosion Pits on the Fatigue Resistance of a Disk Superalloy

NASA Technical Reports Server (NTRS)

Gabb, Timothy P.; Telesman, Jack; Hazel, Brian; Mourer, David P.

2009-01-01

The effects of hot corrosion pits on low cycle fatigue life and failure modes of the disk superalloy ME3 were investigated. Low cycle fatigue specimens were subjected to hot corrosion exposures producing pits, then tested at low and high temperatures. Fatigue lives and failure initiation points were compared to those of specimens without corrosion pits. Several tests were interrupted to estimate the fraction of fatigue life that fatigue cracks initiated at pits. Corrosion pits significantly reduced fatigue life by 60 to 98 percent. Fatigue cracks initiated at a very small fraction of life for high temperature tests, but initiated at higher fractions in tests at low temperature. Critical pit sizes required to promote fatigue cracking were estimated, based on measurements of pits initiating cracks on fracture surfaces.

Controlled Release from Core-Shell Nanoporous Silica Particles for Corrosion Inhibition of Aluminum Alloys

DOE PAGES

Jiang, Xingmao; Jiang, Ying-Bing; Liu, Nanguo; ...

2011-01-01

Ceriumore » m (Ce) corrosion inhibitors were encapsulated into hexagonally ordered nanoporous silica particles via single-step aerosol-assisted self-assembly. The core/shell structured particles are effective for corrosion inhibition of aluminum alloy AA2024-T3. Numerical simulation proved that the core-shell nanostructure delays the release process. The effective diffusion coefficient elucidated from release data for monodisperse particles in water was 1.0 × 10 − 14  m 2 s for Ce 3+ compared to 2.5 × 10 − 13  m 2 s for NaCl. The pore size, pore surface chemistry, and the inhibitor solubility are crucial factors for the application. Microporous hydrophobic particles encapsulating a less soluble corrosion inhibitor are desirable for long-term corrosion inhibition.« less

The Effect of Fly Ash on the Corrosion Behaviour of Galvanised Steel Rebarsin Concrete

NASA Astrophysics Data System (ADS)

Tittarelli, Francesca; Mobili, Alessandra; Bellezze, Tiziano

2017-08-01

The effect of fly ash on the corrosion behaviour of galvanised steel rebars in cracked concrete specimens exposed to wet-dry cycles in a chloride solution has been investigated. The obtained results show that the use of fly ash, replacing either cement or aggregate, always improves the corrosion behaviour of galvanised steel reinforcements. In particular, the addition of fly ash, even in the presence of concrete cracks, decreases the corrosion rate monitored in very porous concretes, as those with w/c = 0.80, to values comparable with those obtained in good quality concretes, as those with w/c = 0.45. Therefore, fly ash cancels the negative effect, at least from the corrosion point of view, of a great porosity of the cement matrix.

Flow-induced corrosion behavior of absorbable magnesium-based stents.

PubMed

Wang, Juan; Giridharan, Venkataraman; Shanov, Vesselin; Xu, Zhigang; Collins, Boyce; White, Leon; Jang, Yongseok; Sankar, Jagannathan; Huang, Nan; Yun, Yeoheung

2014-12-01

The aim of this work was to study corrosion behavior of magnesium (Mg) alloys (MgZnCa plates and AZ31 stents) under varied fluid flow conditions representative of the vascular environment. Experiments revealed that fluid hydrodynamics, fluid flow velocity and shear stress play essential roles in the corrosion behavior of absorbable magnesium-based stent devices. Flow-induced shear stress (FISS) accelerates the overall corrosion (including localized, uniform, pitting and erosion corrosions) due to the increased mass transfer and mechanical force. FISS increased the average uniform corrosion rate, the localized corrosion coverage ratios and depths and the removal rate of corrosion products inside the corrosion pits. For MgZnCa plates, an increase of FISS results in an increased pitting factor but saturates at an FISS of ∼0.15Pa. For AZ31 stents, the volume loss ratio (31%) at 0.056Pa was nearly twice that (17%) at 0Pa before and after corrosion. Flow direction has a significant impact on corrosion behavior as more severe pitting and erosion corrosion was observed on the back ends of the MgZnCa plates, and the corrosion product layer facing the flow direction peeled off from the AZ31 stent struts. This study demonstrates that flow-induced corrosion needs be understood so that Mg-based stents in vascular environments can be effectively designed. Copyright © 2014 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

Field Testing of High Current Electrokinetic Nanoparticle Treatment for Corrosion Mitigation in Reinforced Concrete

NASA Technical Reports Server (NTRS)

Cardenas, Henry; Alexander, Joshua; Kupwade-Patil, Kunal; Calle, Luz marina

2010-01-01

Electrokinetic Nanoparticle (EN) treatment was used as a rapid repair measure to mitigate chloride induced corrosion of reinforced concrete in the field. EN treatment uses an electric field to transport positively charged nanoparticles to the reinforcement through the concrete capillary pores. Cylindrical reinforced concrete specimens were batched with 4.5 wt % salt content (based on cement mass). Three distinct electrokinetic treatments were conducted using high current density (up to 5 A/m2) to form a chloride penetration barrier that was established in 5 days, as opposed to the traditional 6-8 weeks, generally required for electrochemical chloride extraction (ECE). These treatments included basic EN treatment, EN with additional calcium treatment, and basic ECE treatment. Field exposures were conducted at the NASA Beachside Corrosion Test Site, Kennedy Space Center, Florida, USA. The specimens were subjected to sea water immersion at the test site as a posttreatment exposure. Following a 30-day post-treatment exposure period, the specimens were subjected to indirect tensile testing to evaluate treatment impact. The EN treated specimens exhibited 60% and 30% increases in tensile strength as compared to the untreated controls and ECE treated specimens respectively. The surfaces of the reinforcement bars of the control specimens were 67% covered by corrosion products. In contrast, the EN treated specimens exhibited corrosion coverage of only 4%. Scanning electron microscopy (SEM) revealed a dense concrete microstructure adjacent to the bars of the treated specimens as compared to the control and ECE specimens. Energy dispersive spectroscopic (EDS) analysis of the polished EN treated specimens showed a reduction in chloride content by a factor of 20 adjacent to the bars. This study demonstrated that EN treatment was successful in forming a chloride penetration barrier rapidly. This work also showed that the chloride barrier was effective when samples were exposed to field conditions at one of the most severely corrosive environments in North America.

Effects of Sn and Sb on the corrosion resistance of AH 32 steel in a cargo oil tank environment

NASA Astrophysics Data System (ADS)

Ahn, SooHoon; Park, Kyung Jin; Oh, KkochNim; Hwang, SungDoo; Park, ByungJoon; Kwon, HyukSang; Shon, MinYoung

2015-09-01

Effects of the alloying elements, Sn and Sb, on the corrosion resistance of modified AH 32 steel for the cargo oil tanks (COT) were examined using an electrochemical test and weight loss measurement. All experiments were carried out in acidic chloride solution (0.14 M HCl and 10 wt% NaCl, pH 0.85) at 30 °C, simulating the inner bottom plate of COT. It was clearly found that the small amount addition of Sn and Sb improved the corrosion resistance of modified AH 32 steel, which is confirmed by the higher polarization resistance of AH 32 steel modified with Sn and Sb addition compared with that of the base steel. X-ray photoelectron spectroscopy analysis of the corroded surface after immersion of 72 h presented that the AH 32 steel modified with Sn and Sb addition created the protective corrosion products including SnO2 and Sb2O5. These oxides act as high corrosion inhibitor to anodic corrosion reaction, and hence leading to the improvement in the corrosion resistance of the modified AH 32 steels.

Analysis of Acoustic Emission Parameters from Corrosion of AST Bottom Plate in Field Testing

NASA Astrophysics Data System (ADS)

Jomdecha, C.; Jirarungsatian, C.; Suwansin, W.

Field testing of aboveground storage tank (AST) to monitor corrosion of the bottom plate is presented in this chapter. AE testing data of the ten AST with different sizes, materials, and products were employed to monitor the bottom plate condition. AE sensors of 30 and 150 kHz were used to monitor the corrosion activity of up to 24 channels including guard sensors. Acoustic emission (AE) parameters were analyzed to explore the AE parameter patterns of occurring corrosion compared to the laboratory results. Amplitude, count, duration, and energy were main parameters of analysis. Pattern recognition technique with statistical was implemented to eliminate the electrical and environmental noises. The results showed the specific AE patterns of corrosion activities related to the empirical results. In addition, plane algorithm was utilized to locate the significant AE events from corrosion. Both results of parameter patterns and AE event locations can be used to interpret and locate the corrosion activities. Finally, basic statistical grading technique was used to evaluate the bottom plate condition of the AST.

Intelligent Evaluation Method of Tank Bottom Corrosion Status Based on Improved BP Artificial Neural Network

NASA Astrophysics Data System (ADS)

Qiu, Feng; Dai, Guang; Zhang, Ying

According to the acoustic emission information and the appearance inspection information of tank bottom online testing, the external factors associated with tank bottom corrosion status are confirmed. Applying artificial neural network intelligent evaluation method, three tank bottom corrosion status evaluation models based on appearance inspection information, acoustic emission information, and online testing information are established. Comparing with the result of acoustic emission online testing through the evaluation of test sample, the accuracy of the evaluation model based on online testing information is 94 %. The evaluation model can evaluate tank bottom corrosion accurately and realize acoustic emission online testing intelligent evaluation of tank bottom.

Hydrogen assisted cracking and CO2 corrosion behaviors of low-alloy steel with high strength used for armor layer of flexible pipe

NASA Astrophysics Data System (ADS)

Liu, Zhenguang; Gao, Xiuhua; Du, Linxiu; Li, Jianping; Zhou, Xiaowei; Wang, Xiaonan; Wang, Yuxin; Liu, Chuan; Xu, Guoxiang; Misra, R. D. K.

2018-05-01

In this study, hydrogen induced cracking (HIC), sulfide stress corrosion cracking (SSCC) and hydrogen embrittlement (HE) were carried out to study hydrogen assisted cracking behavior (HIC, SSCC and HE) of high strength pipeline steel used for armor layer of flexible pipe in ocean. The CO2 corrosion behavior of designed steel with high strength was studied by using immersion experiment. The experimental results demonstrate that the corrosion resistance of designed steel with tempered martensite to HIC, SSCC and HE is excellent according to specific standards, which contributes to the low concentration of dislocation and vacancies previously formed in cold rolling process. The corrosion mechanism of hydrogen induced cracking of designed steel, which involves in producing process, microstructure and cracking behavior, is proposed. The designed steel with tempered martensite shows excellent corrosion resistance to CO2 corrosion. Cr-rich compound was first formed on the coupon surface exposed to CO2-saturated brine condition and chlorine, one of the corrosion ions in solution, was rich in the inner layer of corrosion products.

The chloride induced localised corrosion of aluminium and beryllium: A study by electron and X-ray spectroscopies

NASA Astrophysics Data System (ADS)

Mallinson, Christopher F.

Beryllium is an important metal in the nuclear industry for which there are no suitable replacements. It undergoes localised corrosion at the site of heterogeneities in the metal surface. Corrosion pits are associated with a range of second phase particles. To investigate the role of these particles in corrosion, a safe experimental protocol was established using an aluminium alloy as a corrosion material analogue. The 7075-T6 alloy had not previously been investigated using the experimental methodology used in this thesis. This work led to the development of the experimental methodology and safe working practices for handling beryllium. The range and composition of the second phase particles present in S-65 beryllium billet were identified using a combination of SEM, AES, EDX and WDX. Following the identification of a range of particles with various compositions, including the AlFeBe4 precipitate which has been previously associated with corrosion, the location of the particles were marked to enable their repeated study. Attention was focused on the microchemistry in the vicinity of second phase particles, as a function of immersion time in pH 7, 0.1 M NaCl solution. The corrosion process associated with different particles was followed by repeatedly relocating the particles to perform analysis by means of SEM, AES and EDX. The use of traditional chlorinated vapour degreasing solvents on beryllium was investigated and compared to two modern commercially available cleaning solutions designed as drop-in replacements. This work expanded the range of solvents suitable for cleaning beryllium and validated the conclusions from previous thermodynamic modelling. Additionally, a new experimental methodology has been developed which enables the acquisition of chemical state information from the surface of micron scale features. This was applied to sub-micron copper and iron particles, as well as a copper intermetallic.

Corrosion Characteristics of Ni-Based Hardfacing Alloy Deposited on Stainless Steel Substrate by Laser Cladding

NASA Astrophysics Data System (ADS)

Awasthi, Reena; Abraham, Geogy; Kumar, Santosh; Bhattacharyya, Kaustava; Keskar, Nachiket; Kushwaha, R. P.; Rao, Ramana; Tewari, R.; Srivastava, D.; Dey, G. K.

2017-06-01

In this study, corrosion characteristics of a nickel-based Ni-Mo-Cr-Si hardfacing alloy having 32Mo, 15Cr, and 3Si (wt pct) as alloying elements, deposited on stainless steel SS316L substrate by laser cladding, have been presented. Corrosion behavior of the laser clad layer was evaluated in reducing (0.1 M HCl) and oxidizing (0.5 M HNO3) environments, in comparison with the reference substrate SS316L, using electrochemical potentiodynamic technique at room temperature. The corrosion mechanisms have been evaluated on the basis of microstructural and microchemical analysis using scanning electron microscopy attached with energy-dispersive spectrometry. Passivity behavior of the laser clad layer was studied in 0.5 M H2SO4, using the potentiostatic technique and analyzing the passive layer by X-ray photoelectron spectroscopy. Laser clad layer of Ni-Mo-Cr-Si exhibited higher pitting corrosion resistance in chloride (reducing) environment, indicated by much higher breakdown potential ( 0.8 VSCE) and the absence of pitting as compared to substrate SS316L ( 0.3 VSCE). However, in oxidizing (0.5 M HNO3) environment, both the laser clad layer and substrate SS316L showed excellent and similar corrosion resistance exhibiting high breakdown potential ( 0.85 VSCE) and wide passivation range ( 0.8 VSCE) with low passive current density ( 4 to 7 × 10-6 A/cm2). The stable passive layer formed on laser clad layer of Ni-Mo-Cr-Si after exposure in 0.5 M H2SO4 solution at constant potential 0.6 VSCE (within the passive range), consisted oxides of Mo as Mo+4 (MoO2) and Mo+6 (MoO4)-2, Cr as Cr3+ (mixture of both Cr2O3 and Cr (OH)3), and Si as Si4+(SiO2), which have contributed to passivation and repassivation and therefore excellent corrosion behavior.

Effect of alloying elements Al and Ca on corrosion resistance of plasma anodized Mg alloys

NASA Astrophysics Data System (ADS)

Anawati, Asoh, Hidetaka; Ono, Sachiko

2016-04-01

Plasma anodizing is a surface treatment used to form a ceramic-type oxide film on Mg alloys by the application of a high anodic voltage to create intense plasma near the metal surface. With proper selection of the process parameters, the technique can produce high quality oxide with superior adhesion, corrosion resistance, micro-hardness, wear resistance and strength. The effect of alloying element Al on plasma anodizing process of Mg alloys was studied by comparing the anodizing curves of pure Mg, AZ31, and AZ61 alloys while the effect of Ca were studied on AZ61 alloys containing 0, 1, and 2 wt% Ca. Anodizing was performed in 0.5 M Na3PO4 solution at a constant current density of 200 Am-2 at 25°C. Anodic oxide films with lava-like structure having mix composition of amorphous and crystal were formed on all of the alloys. The main crystal form of the oxide was Mg3(PO4)2 as analyzed by XRD. Alloying elements Al and Ca played role in modifying the plasma lifetime during anodization. Al tended to extend the strong plasma lifetime and therefore accelerated the film thickening. The effect of Ca on anodizing process was still unclear. The anodic film thickness and chemical composition were altered by the presence of Ca in the alloys. Electrochemical corrosion test in 0.9% NaCl solution showed that the corrosion behavior of the anodized specimens depend on the behavior of the substrate. Increasing Al and Ca content in the alloys tended to increase the corrosion resistance of the specimens. The corrosion resistance of the anodized specimens improved significantly about two orders of magnitude relative to the bare substrate.

Tribocorrosion: Ceramic and Oxidized Zirconium vs Cobalt-Chromium Heads in Total Hip Arthroplasty.

PubMed

Tan, Sok Chuen; Lau, Adrian C K; Del Balso, Christopher; Howard, James L; Lanting, Brent A; Teeter, Matthew G

2016-09-01

This matched-cohort study aims to compare tribocorrosion between matched ceramic and cobalt-chromium femoral head trunnions and between matched Oxinium and cobalt-chromium femoral head trunnions. Secondary objectives were to investigate whether taper design, depth of trunnion, implantation time, age, body mass index, and gender have an effect on fretting and corrosion. All hip prostheses retrieved between 1999 and 2015 at one center were reviewed, giving a total of 52 ceramic heads. These were matched to a cobalt-chromium cohort according to taper design, head size, neck length, and implantation time. The trunnions were examined by 2 observers using a 4-point scoring technique and scored in 3 zones: apex, middle, and base. The observers were blinded to clinical and manufacturing data where possible. A separate matched-cohort analysis was performed between 8 Oxinium heads and 8 cobalt-chromium heads, which were similarly scored. Ceramic head trunnions demonstrated a lower median fretting and corrosion score at the base zone (P < .001), middle zone (P < .001), and in the combined score (P < .001). Taper design had a significant effect on fretting and corrosion in the apex zone (P = .04) of the ceramic group, as well as the cobalt-chromium group (P = .03). Between Oxinium heads and cobalt-chromium heads, there was no significant difference in the fretting and corrosion score across all 3 zones (base: P = .22; middle: P = .92; and apex: P = .71) and for the combined score (P = .67). This study shows that ceramic head confers an advantage in trunnion fretting and corrosion. Taper design and implantation time were also significant factors for fretting and corrosion. Copyright © 2016 Elsevier Inc. All rights reserved.

Evaluation of corrosion resistance and surface characteristics of orthodontic wires immersed in different mouthwashes.

PubMed

Nalbantgil, Didem; Ulkur, Feyza; Kardas, Gulfeza; Culha, Mustafa

2016-11-25

Patients use mouthwashes in addition to mechanical cleaning during orthodontic treatment. The effects of mouthwashes on the archwires have not been examined yet. To compare the corrosion resistance of four different arch wires and corrosion effects of different mouthwashes to formulate a biocompatible and mechanically useful arch wire and mouthwash combination. Each group comprised of 4 wire samples of 2 cm 0.016 × 0.022 inch. 1st group: ion implanted nickel titanium (INT), 2nd group: nickel titanium, without ion implantation (NT), 3rd group: micro layered esthetic nickel titanium (ENT), 4th group: stainless steel (SS) wires. They were immersed inside 2 ml of artificial saliva solutions (AS) for the control, or AS (9%) combined with 1 of the 3 mouthwashes (91%) for study groups, for 24 hours. These mouthwashes were essential oil (EO), chlorhexidine (CHX), sodium-fluoride (NaF). An electrochemical analyzer was used for electrochemical impedance spectroscopy measurements. High corrosion resistance was obtained for ENT than the other wires. The corrosion potentials are 0.007, -0.042, 0.074 and -0.015 V (Ag/AgCl) for ENT, INT, SS and NT in the artificial salivary, respectively. In NaF containing mouthwash Rp value of ENT is significantly high in comparison to others. The impedance responses of all materials increased significantly in the presence of NaF mouthwash as well as in the CHX mouthwash. Low frequencies are seen at all materials in EO mouthwash. Diameters of loops are 22, 5.9, 5.9 and 3.7 MΩ at ENT, INT, SS and NT. In this study, micro layered esthetic nickel titanium wires are found biocompatible among other wires and NaF and CHX mouthwashes can be recommend for their good corrosion resistance during fixed orthodontic therapy.

Investigation of anti-corrosive properties of poly(aniline-co-2-pyridylamine-co-2,3-xylidine) and its nanocomposite poly(aniline-co-2-pyridylamine-co-2,3-xylidine)/ZnO on mild steel in 0.1 M HCl

NASA Astrophysics Data System (ADS)

Alam, Ruman; Mobin, Mohammad; Aslam, Jeenat

2016-04-01

A soluble terpolymer of aniline (AN), 2-pyridylamine (PA) and 2,3-xylidine (XY), poly(AN-co-PA-co-XY) and its nanocomposite with ZnO nanoparticles namely, poly(AN-co-PA-co-XY)/ZnO were synthesized by chemical oxidative polymerization employing ammonium persulfate as an oxidant. Nanocomposites of homopolymers, polyaniline/ZnO, poly(XY)/ZnO and poly(PA)/ZnO were also synthesized by following similar synthesis route. FTIR, XRD and SEM techniques were used to characterize the synthesized compounds. The synthesized compounds were chemically deposited on mild steel specimens by solvent evaporation method using N-methyl-2-pyrrolidone (NMP) as solvent and 10% epoxy resin (by weight) as binder. Anticorrosive properties of homopolymer nanocomposites, terpolymer and its nanocomposite coatings were studied in 0.1 M HCl by subjecting them to various corrosion tests which includes: free corrosion potential measurement (OCP), weight loss measurements, potentiodynamic polarization, and AC impedance technique. The surface morphology of the corroded and uncorroded coated steel specimens was evaluated using SEM. The corrosion protection performance of terpolymer nanocomposite coating was compared to the terpolymer and individual homopolymers nanocomposites coatings after 30 days immersion in corrosive medium.

Comprehensive Isotopic and Elemental Analysis of a Multi-Oxide Glass By Multicollector ICP-MS in Isotope Substitution Studies

DOE Office of Scientific and Technical Information (OSTI.GOV)

v, Mitroshkov; JV, Ryan

2016-04-07

Multicollector ICP-MS was used to comprehensively analyze different types of isotopically-modified glass created in order to investigate the processes of glass corrosion in the water. The analytical methods were developed for the analyses of synthesized, isotopically-modified solid glass and the release of glass constituents upon contact with deionized water. To validate the methods, results from an acid digestion sample of the Analytical Reference Glass (ARG) showed good agreement when compared to data from multiple prior analyses on the same glass [Smith-1]. In this paper, we present the results of this comprehensive analysis from the acid digestion of six types ofmore » isotopically-modified glass and the release of glass constituents into water corrosion after one year of aqueous corrosion.« less

Evaluation of mechanical and corrosion properties of MMFX reinforcing steel for concrete

DOT National Transportation Integrated Search

2004-01-01

The corrosion performance of MMFX and conventional reinforcing steels is compared based on macrocell and bench-scale tests. The conventional steel includes epoxy-coated and uncoated bars. Macrocell tests are conducted on bare bars and bars symmetrica...

Stress Corrosion Cracking of Certain Aluminum Alloys

NASA Technical Reports Server (NTRS)

Hasse, K. R.; Dorward, R. C.

1983-01-01

SC resistance of new high-strength alloys tested. Research report describes progress in continuing investigation of stress corrosion (SC) cracking of some aluminum alloys. Objective of program is comparing SC behavior of newer high-strength alloys with established SC-resistant alloy.

A study of the effects of phosphates on copper corrosion in drinking water: Copper release, electrochemical, and surface analysis approach

NASA Astrophysics Data System (ADS)

Kang, Young C.

The following work is the study to evaluate the impact of corrosion inhibitors on the copper metal in drinking water and to investigate the corrosion mechanism in the presence and absence of inhibitors. Electrochemical experiments were conducted to understand the effect of specific corrosion inhibitors in synthetic drinking water which was prepared with controlled specific water quality parameters. Water chemistry was studied by Inductively Coupled Plasma--Atomic Emission Spectroscopy (ICP--AES) to investigate the copper leaching rate with time. Surface morphology, crystallinity of corrosion products, copper oxidation status, and surface composition were characterized by various solid surface analysis methods, such as Scanning Electron Microscopy/Energy--Dispersive Spectrometry (SEM/EDS), Grazing-Incidence-angle X-ray Diffraction (GIXRD), X-ray Photoelectron Spectroscopy (XPS), and Time-of-Flight Secondary Ions Mass Spectrometry (ToF-SIMS). The purpose of the first set of experiments was to test various electrochemical techniques for copper corrosion for short term before studying a long term loop system. Surface analysis techniques were carried out to identify and study the corrosion products that form on the fresh copper metal surface when copper coupons were exposed to test solutions for 2 days of experiments time. The second phase of experiments was conducted with a copper pipe loop system in a synthetic tap water over an extended period of time, i.e., 4 months. Copper release and electrochemically measured corrosion activity profiles were monitored carefully with and without corrosion inhibitor, polyphosphate. A correlation between the copper released into the solution and the electrochemically measured corrosion activities was also attempted. To investigate corrosion products on the copper pipe samples, various surface analysis techniques were applied in this study. Especially, static mass spectra acquisition and element distribution mapping were carried out by ToF-SIMS. Dynamic SIMS provided shallow depth profile of corroded copper sample. The third set of the experiments was related to electrochemical noise (EN) measurement through copper coupons to pipes. Calculating corrosion rate of a metal and predicting exactly how long it lasts are problematic since the metal corrosion may be caused by combined corrosion types. Many other metals undergo not only uniform corrosion, but localized corrosion. Uniform corrosion may be conducive for copper pipe to prevent it from further severe corrosion and form passivated film, but localized corrosion causes pinhole leaks and limits the copper pipe applications. The objective of this set of experiment is to discuss the application of electrochemical noise approaches to drinking water copper corrosion problems. Specially, a fundamental description of EN is presented including a discussion of how to interpret the results and technique limitations. Although it was indicated with electrochemical analysis that the corrosion activity was affected by orthophosphate addition in the short-term test, no copper-phosphate complex or compound was found by copper surface characterization. Apparently, orthophosphate can inhibit corrosion by adsorption on the copper surface, but cannot form solid complexes with copper in such a short time, 2 days. When polyphosphate was added into recirculating copper pipe system, copper level increased and polarization resistance decreased. Greenish blue residue on the copper pipe was suspected as copper phosphate complex and corrosion inhibition mechanism was proposed.

Experimental investigation on cleaning of corroded ancient coins using a Nd:YAG laser

NASA Astrophysics Data System (ADS)

Zhu, Huazhong; Lu, Jian; Ni, Xiaowu; Shen, Zhonghua

2017-05-01

The objective of the work reported is to study experimentally on the removal of corrosion layer from the ancient coins using laser beam as the conservation tool. With the use of Q-switched Nd:YAG laser radiation at 1064 nm, dry laser cleaning, steam laser cleaning and chemical-assisted laser cleaning were used to find out a more suitable and efficient laser treatment for corrosion removal. Cleaning tests were performed on ancient Chinese coins. Experimental results shows that the dry laser cleaning was not successful at removing all types of corrosion crust. It was possible to remove the outer thicker layer of the corrosion products (typically known as patina), but failed on the thinner layer of cuprite. The steam laser cleaning could decrease the initial removal threshold and improve the removal efficiency especially for the oxidation with powdery structure. As for chemical-assisted laser treatment, the cleaning results demonstrate that the combination of laser and chemical reagent could provide a considerable improvement in corrosion removal compared with the conventional laser treatments. Most of the corrosion contaminant was stripped, even the cuprite layer. Moreover, no secondary pollution was formed on the cleaned surface. X-ray fluorescence was applied to determine the variation of composition of surface layer and bulk metal before and after the coins cleaned. It shows that all of the three laser treatments were efficient to reduce the chlorine concentration on the surface of the coins more than 75%.

ENVIRONMENTAL BENIGN MITIGATION OF MICROBIOLOGICALLY INFLUENCED CORROSION (MIC)

DOE Office of Scientific and Technical Information (OSTI.GOV)

J.R. Paterek; G. Husmillo; V. Trbovic

The overall program objective is to develop and evaluate environmental benign agents or products that are effective in the prevention, inhibition, and mitigation of microbially influenced corrosion (MIC) in the internal surfaces of metallic natural gas pipelines. The goal is one or more environmental benign, a.k.a. ''green'' products that can be applied to maintain the structure and dependability of the natural gas infrastructure. The technical approach for this quarter were isolation and cultivation of MIC-causing microorganisms from corroded pipeline samples, optimizing parameters in the laboratory-scale corrosion test loop system and testing the effective concentrations of Capsicum sp. extracts to verifymore » the extent of corrosion on metal coupons by batch culture method. A total of 22 strains from the group of heterotrophic, acid producing, denitrifying and sulfate reducing bacteria were isolated from the gas pipeline samples obtained from Northern Indiana Public Service Company in Trenton, Indiana. They were purified and will be sent out for identification. Bacterial strains of interest were used in antimicrobial screenings and test loop experiments. Parameters for the laboratory-scale test loop system such as gas and culture medium flow rate; temperature; inoculation period; and length of incubation were established. Batch culture corrosion study against Desulfovibrio vulgaris showed that one (S{sub 1}M) out of the four Capsicum sp. extracts tested was effective in controlling the corrosion rate in metal coupons by 33.33% when compared to the untreated group.« less

Microstructural, phase evolution and corrosion properties of silicon carbide reinforced pulse electrodeposited nickel-tungsten composite coatings

NASA Astrophysics Data System (ADS)

Singh, Swarnima; Sribalaji, M.; Wasekar, Nitin P.; Joshi, Srikant; Sundararajan, G.; Singh, Raghuvir; Keshri, Anup Kumar

2016-02-01

Silicon carbide (SiC) reinforced nickel-tungsten (Ni-W) coatings were successfully fabricated on steel substrate by pulse electrodeposition method (PED) and the amount of SiC was varied as 0 g/l, 2 g/l, and 5 g/l in Ni-W coating. Effect of subsequent addition of SiC on microstructures, phases and on corrosion property of the coating was investigated. Field emission scanning electron microscopy (FE-SEM) image of the surface morphology of the coating showed the transformation from the dome like structure to turtle shell like structure. X-ray diffraction (XRD) of Ni-W-5 g/l SiC showed the disappearance of (220) plane of Ni(W), peak splitting in major peak of Ni(W) and formation of distinct peak of W(Ni) solid solution. Absence of (220) plane, peak splitting and presence of W(Ni) solid solution was explained by the high resolution transmission electron microscopy (HR-TEM) images. Tafel polarization plot was used to study the corrosion property of the coatings in 0.5 M NaCl solution. Ni-W-5 g/l SiC coating was showed higher corrosion resistance (i.e. ∼21% increase in corrosion potential, Ecorr) compared to Ni-W coating. Two simultaneous phenomena have been identified for the enhanced corrosion resistance of Ni-W-5 g/l SiC coating. (a) Presence of crystallographic texture (b) formation of continuous double barrier layer of NiWO4 and SiO2.

Online monitoring of corrosion behavior in molten metal using laser-induced breakdown spectroscopy

NASA Astrophysics Data System (ADS)

Zeng, Qiang; Pan, Congyuan; Li, Chaoyang; Fei, Teng; Ding, Xiaokang; Du, Xuewei; Wang, Qiuping

2018-04-01

The corrosion behavior of structure materials in direct contact with molten metals is widespread in metallurgical industry. The corrosion of casting equipment by molten metals is detrimental to the production process, and the corroded materials can also contaminate the metals being produced. Conventional methods for studying the corrosion behavior by molten metal are offline. This work explored the application of laser-induced breakdown spectroscopy (LIBS) for online monitoring of the corrosion behavior of molten metal. The compositional changes of molten aluminum in crucibles made of 304 stainless steel were obtained online at 1000 °C. Several offline techniques were combined to determine the corrosion mechanism, which was highly consistent with previous studies. Results proved that LIBS was an efficient method to study the corrosion mechanism of solid materials in molten metal.

Comments on Cadmium Alternatives and Testing - IHE vs. EHE (Briefing Charts)

DTIC Science & Technology

2011-11-17

Boeing. All rights reserved. 6 • Provides Corrosion Protection to Steel - No red rust – Corrosion Resistant Coating in Salt Water (Compared to Zinc ...Cd corrosion rate in salt water is lower than zinc • Sacrificially Protects Steel – If Cd coating is scratched Cd coating will corrode first and...prevent steel from corroding • Soft and Ductile – Does Not Reduce the Fatigue Life of High Strength Steel (HSS) – Provides lubricous coating to

Influence of the post-weld surface treatment on the corrosion resistance of the duplex stainless steel 1.4062

NASA Astrophysics Data System (ADS)

Rosemann, P.; Müller, C.; Baumann, O.; Modersohn, W.; Halle, T.

2017-03-01

The duplex stainless steel 1.4062 (X2CrNiN22-2) is used as alternative material to austenitic stainless steels in the construction industry. The corrosion resistance of welded seams is influenced by the base material, the weld filler material, the welding process and also by the final surface treatment. The scale layer next to the weld seam can be removed by grinding, pickling, electro-polished or blasting depending on the application and the requested corrosion resistance. Blasted surfaces are often used in industrial practice due to the easier and cheaper manufacturing process compared to pickled or electro-polished surfaces. Furthermore blasting with corundum-grain is more effective than blasting with glass-beads which also lower the process costs. In recent years, stainless steel surfaces showed an unusually high susceptibility to pitting corrosion after grinding with corundum. For this reason, it is now also questioned critically whether the corrosion resistance is influenced by the applied blasting agent. This question was specifically investigated by comparing grinded, pickled, corundum-grain- and glass-bead-blasted welding seams. Results of the SEM analyses of the blasting agents and the blasted surfaces will be presented and correlated with the different performed corrosion tests (potential measurement, KorroPad-test and pitting potential) on welding seams with different surface treatments.

Enhanced Imaging of Corrosion in Aircraft Structures with Reverse Geometry X-ray(registered tm)

NASA Technical Reports Server (NTRS)

Winfree, William P.; Cmar-Mascis, Noreen A.; Parker, F. Raymond

2000-01-01

The application of Reverse Geometry X-ray to the detection and characterization of corrosion in aircraft structures is presented. Reverse Geometry X-ray is a unique system that utilizes an electronically scanned x-ray source and a discrete detector for real time radiographic imaging of a structure. The scanned source system has several advantages when compared to conventional radiography. First, the discrete x-ray detector can be miniaturized and easily positioned inside a complex structure (such as an aircraft wing) enabling images of each surface of the structure to be obtained separately. Second, using a measurement configuration with multiple detectors enables the simultaneous acquisition of data from several different perspectives without moving the structure or the measurement system. This provides a means for locating the position of flaws and enhances separation of features at the surface from features inside the structure. Data is presented on aircraft specimens with corrosion in the lap joint. Advanced laminographic imaging techniques utilizing data from multiple detectors are demonstrated to be capable of separating surface features from corrosion in the lap joint and locating the corrosion in multilayer structures. Results of this technique are compared to computed tomography cross sections obtained from a microfocus x-ray tomography system. A method is presented for calibration of the detectors of the Reverse Geometry X-ray system to enable quantification of the corrosion to within 2%.

Microhardness and In Vitro Corrosion of Heat-Treated Mg–Y–Ag Biodegradable Alloy

PubMed Central

Vlček, Marián; Lukáč, František; Kudrnová, Hana; Smola, Bohumil; Stulíková, Ivana; Luczak, Monika; Szakács, Gábor; Hort, Norbert; Willumeit-Römer, Regine

2017-01-01

Magnesium alloys are promising candidates for biodegradable medical implants which reduce the necessity of second surgery to remove the implants. Yttrium in solid solution is an attractive alloying element because it improves mechanical properties and exhibits suitable corrosion properties. Silver was shown to have an antibacterial effect and can also enhance the mechanical properties of magnesium alloys. Measurements of microhardness and electrical resistivity were used to study the response of Mg–4Y and Mg–4Y–1Ag alloys to isochronal or isothermal heat treatments. Hardening response and electrical resistivity annealing curves in these alloys were compared in order to investigate the effect of silver addition. Procedures for solid solution annealing and artificial aging of the Mg–4Y–1Ag alloy were developed. The corrosion rate of the as-cast and heat-treated Mg–4Y–1Ag alloy was measured by the mass loss method. It was found out that solid solution heat treatment, as well artificial aging to peak hardness, lead to substantial improvement in the corrosion properties of the Mg–4Y–1Ag alloy. PMID:28772414

Effect of povidone-iodine addition on the corrosion behavior of cp-Ti in normal saline.

PubMed

Bhola, Rahul; Bhola, Shaily M; Mishra, Brajendra; Olson, David L

2010-05-01

The effect of various concentrations of povidone-iodine (PI) on the corrosion behavior of a commercially pure titanium alloy (Ti-1) has been investigated in normal saline solution to simulate the povidone-iodine addition in an oral environment. The open circuit potential, electrochemical impedance spectroscopy and potentiodynamic polarization measurements have been used to characterize the electrochemical phenomena occurring on the alloy surface. The open circuit potential values for Ti-1 in various concentrations of PI shift considerably towards noble direction as compared to pure normal saline. In the potentiodynamic polarization curve for Ti-1 in various solutions, the cathodic current density has increased for all concentrations of PI and the anodic current density has decreased. Only the 0.1% PI concentration is able to inhibit corrosion of Ti-1 in normal saline and the other higher concentrations studied, accelerate corrosion. The EIS data for Ti-1 in normal saline and in various concentrations of PI follows a one time constant circuit, suggesting the formation of a single passive film on Ti-1 which is not altered by the addition of PI to normal saline.

Surface properties of AZ91 magnesium alloy after PEO treatment using molybdate salts and low current densities

NASA Astrophysics Data System (ADS)

Pezzato, Luca; Brunelli, Katya; Napolitani, Enrico; Magrini, Maurizio; Dabalà, Manuele

2015-12-01

Plasma electrolytic oxidation (PEO) process is a recently developed electrochemical method used to produce on the surface of various metals oxide ceramic coatings that improve corrosion and wear properties of the substrate. In this work, PEO process was applied on AZ91 magnesium alloy using low current densities (0.05 A/cm2) and an alkaline solution of silicates with different concentrations of sodium molybdate (0.3-3 g/l). The effect of the low current densities of process and of molybdate salts on the corrosion resistance of the coatings was studied with potentiodynamic polarization tests and electrochemical impedance spectroscopy (EIS) in chloride and sulfate environment. The morphology, the phases and the chemical composition of the coatings were examined using a scanning electron microscope equipped with EDS, X-ray diffraction, secondary ion mass spectrometry and X-ray photoelectron spectroscopy. The corrosion properties of the PEO coated samples were remarkably improved if compared with the uncoated samples. The addition of sodium molybdate, in determinate conditions, had a positive effect on the characteristics of the coatings in terms of corrosion resistance.

Corrosion and stress corrosion cracking in supercritical water

NASA Astrophysics Data System (ADS)

Was, G. S.; Ampornrat, P.; Gupta, G.; Teysseyre, S.; West, E. A.; Allen, T. R.; Sridharan, K.; Tan, L.; Chen, Y.; Ren, X.; Pister, C.

2007-09-01

Supercritical water (SCW) has attracted increasing attention since SCW boiler power plants were implemented to increase the efficiency of fossil-based power plants. The SCW reactor (SCWR) design has been selected as one of the Generation IV reactor concepts because of its higher thermal efficiency and plant simplification as compared to current light water reactors (LWRs). Reactor operating conditions call for a core coolant temperature between 280 °C and 620 °C at a pressure of 25 MPa and maximum expected neutron damage levels to any replaceable or permanent core component of 15 dpa (thermal reactor design) and 100 dpa (fast reactor design). Irradiation-induced changes in microstructure (swelling, radiation-induced segregation (RIS), hardening, phase stability) and mechanical properties (strength, thermal and irradiation-induced creep, fatigue) are also major concerns. Throughout the core, corrosion, stress corrosion cracking, and the effect of irradiation on these degradation modes are critical issues. This paper reviews the current understanding of the response of candidate materials for SCWR systems, focusing on the corrosion and stress corrosion cracking response, and highlights the design trade-offs associated with certain alloy systems. Ferritic-martensitic steels generally have the best resistance to stress corrosion cracking, but suffer from the worst oxidation. Austenitic stainless steels and Ni-base alloys have better oxidation resistance but are more susceptible to stress corrosion cracking. The promise of grain boundary engineering and surface modification in addressing corrosion and stress corrosion cracking performance is discussed.

Accelerated Degradation Test and Predictive Failure Analysis of B10 Copper-Nickel Alloy under Marine Environmental Conditions

PubMed Central

Sun, Bo; Ye, Tianyuan; Feng, Qiang; Yao, Jinghua; Wei, Mumeng

2015-01-01

This paper studies the corrosion behavior of B10 copper-nickel alloy in marine environment. Accelerated degradation test under marine environmental conditions was designed and performed based on the accelerated testing principle and the corrosion degradation mechanism. With the prolongation of marine corrosion time, the thickness of Cu2O film increased gradually. Its corrosion product was Cu2(OH)3Cl, which increased in quantity over time. Cl− was the major factor responsible for the marine corrosion of copper and copper alloy. Through the nonlinear fitting of corrosion rate and corrosion quantity (corrosion weight loss), degradation data of different corrosion cycles, the quantitative effects of two major factors, i.e., dissolved oxygen (DO) and corrosion medium temperature, on corrosion behavior of copper alloy were analyzed. The corrosion failure prediction models under different ambient conditions were built. One-day corrosion weight loss under oxygenated stirring conditions was equivalent to 1.31-day weight loss under stationary conditions, and the corrosion rate under oxygenated conditions was 1.31 times higher than that under stationary conditions. In addition, corrosion medium temperature had a significant effect on the corrosion of B10 copper sheet. PMID:28793549

Accelerated Degradation Test and Predictive Failure Analysis of B10 Copper-Nickel Alloy under Marine Environmental Conditions.

PubMed

Sun, Bo; Ye, Tianyuan; Feng, Qiang; Yao, Jinghua; Wei, Mumeng

2015-09-10

This paper studies the corrosion behavior of B10 copper-nickel alloy in marine environment. Accelerated degradation test under marine environmental conditions was designed and performed based on the accelerated testing principle and the corrosion degradation mechanism. With the prolongation of marine corrosion time, the thickness of Cu₂O film increased gradually. Its corrosion product was Cu₂(OH)₃Cl, which increased in quantity over time. Cl - was the major factor responsible for the marine corrosion of copper and copper alloy. Through the nonlinear fitting of corrosion rate and corrosion quantity (corrosion weight loss), degradation data of different corrosion cycles, the quantitative effects of two major factors, i.e. , dissolved oxygen (DO) and corrosion medium temperature, on corrosion behavior of copper alloy were analyzed. The corrosion failure prediction models under different ambient conditions were built. One-day corrosion weight loss under oxygenated stirring conditions was equivalent to 1.31-day weight loss under stationary conditions, and the corrosion rate under oxygenated conditions was 1.31 times higher than that under stationary conditions. In addition, corrosion medium temperature had a significant effect on the corrosion of B10 copper sheet.

Ceramic Heads Decrease Metal Release Caused by Head-taper Fretting and Corrosion.

PubMed

Kocagoz, Sevi B; Underwood, Richard J; MacDonald, Daniel W; Gilbert, Jeremy L; Kurtz, Steven M

2016-04-01

Metal release resulting from taper fretting and corrosion is a clinical concern, because wear and corrosion products may stimulate adverse local tissue reactions. Unimodular hip arthroplasties have a conical taper between the femoral head (head bore taper) and the femoral stem (stem cone taper). The use of ceramic heads has been suggested as a way of reducing the generation of wear and corrosion products from the head bore/stem cone taper junction. A previous semiquantitative study found that ceramic heads had less visual evidence of fretting-corrosion damage compared with CoCr heads; but, to our knowledge, no studies have quantified the volumetric material loss from the head bore and stem cone tapers of a matched cohort of ceramic and metal heads. We asked: (1) Do ceramic heads result in less volume of material loss at the head-stem junction compared with CoCr heads; (2) do stem cone tapers have less volumetric material loss compared with CoCr head bore tapers; (3) do visual fretting-corrosion scores correlate with volumetric material loss; and (4) are device, patient, or intraoperative factors associated with volumetric material loss? A quantitative method was developed to estimate volumetric material loss from the head and stem taper in previously matched cohorts of 50 ceramic and 50 CoCr head-stem pairs retrieved during revision surgery for causes not related to adverse reactions to metal particles. The cohorts were matched according to (1) implantation time, (2) stem flexural rigidity, and (3) lateral offset. Fretting corrosion was assessed visually using a previously published four-point, semiquantitative scoring system. The volumetric loss was measured using a precision roundness machine. Using 24 equally spaced axial traces, the volumetric loss was estimated using a linear least squares fit to interpolate the as-manufactured surfaces. The results of this analysis were considered in the context of device (taper angle clearance, head size, head offset, lateral offset, stem material, and stem surface finish) and patient factors that were obtained from the patients' operative records (implantation time, age at insertion, activity level, and BMI). The cumulative volumetric material losses estimated for the ceramic cohort had a median of 0.0 mm(3) per year (range, 0.0-0.4 mm(3)). The cumulative volumetric material losses estimated for the CoCr cohort had a median of 0.1 mm(3) per year (range, 0.0-8.8 mm(3)). An order of magnitude reduction in volumetric material loss was found when a ceramic head was used instead of a CoCr head (p < 0.0001). In the CoCr cohort, the femoral head bore tapers had a median material loss of 0.02 mm(3) (range, 0.0-8.7 mm(3)) and the stem cone tapers had a median material loss of 0.0 mm(3) (range, 0.0-0.32 mm(3)/year). There was greater material loss from femoral head bore tapers compared with stem cone tapers in the CoCr cohort (p < 0.001). There was a positive correlation between visual scoring and volumetric material loss (Spearman's ρ = 0.67, p < 0.01). Although visual scoring was effective for preliminary screening to separate tapers with no or mild damage from tapers with moderate to severe damage, it was not capable of discriminating in the large range of material loss observed at the taper surfaces with moderate to severe fretting-corrosion damage, indicated with a score of 3 or 4. We observed no correlations between volumetric material loss and device and patient factors. The majority of estimated material loss from the head bore-stem cone junctions resulting from taper fretting and corrosion was from the CoCr head bore tapers as opposed to the stem cone tapers. Additionally, the total material loss from the ceramic cohort showed a reduction in the amount of metal released by an order of magnitude compared with the CoCr cohort. We found that ceramic femoral heads may be an effective means by which to reduce metal release caused by taper fretting and corrosion at the head bore-stem cone modular interface in THAs.

In vitro corrosion behavior of cast iron-platinum magnetic alloys.

PubMed

Watanabe, I; Hai, K; Tanaka, Y; Hisatsune, K; Atsuta, M

2001-05-01

The objective of this study was to investigate the corrosion resistance of cast Fe-Pt alloys of varying compositions for use as attachment keepers and to make a comparison with the corrosion resistance of magnetic stainless steel. The corrosion behavior of cast Fe-Pt alloy keepers (Fe-40 at%Pt, Fe-38 at%Pt, Fe-37 at%Pt and Fe-36 at%Pt) was evaluated by means of an immersion test and an anodic polarization test. The solutions used were a 1.0% lactic acid aqueous solution (pH=2.3) (10 ml) and 0.9% NaCl solution (pH=7.3) (10 ml). As a control, the corrosion resistance of a magnetic stainless steel keeper (SUS 447J1: HICOREX) was also measured. Chromium and platinum ions were not detected in either the 1.0% lactic acid or 0.9% NaCl solutions. The only released ions detected were the Fe ions in the 1.0% lactic acid solution. The amounts of Fe ions released from the Fe-40 at%Pt and Fe-38 at%Pt alloys were significantly (p<0.05) lower than from the Fe-37at%Pt, Fe-36 at%Pt and SUS 447J1 alloys. In the anodic polarization test, the potentials at the beginning of passivation for the four Fe-Pt alloys were higher than for the SUS 447J1 alloy in both solutions. The Fe-Pt alloys, especially the alloys with higher Pt percentages (Fe-40 and 38 at%Pt), indicated a high corrosion resistance compared to the magnetic stainless steel keeper. A reduction in the Pt percentage may decrease the corrosion resistance in the oral environment.

Effects of chemical composition on the corrosion of dental alloys.

PubMed

Galo, Rodrigo; Ribeiro, Ricardo Faria; Rodrigues, Renata Cristina Silveira; Rocha, Luís Augusto; de Mattos, Maria da Glória Chiarello

2012-01-01

The aim of this study was to determine the effect of the oral environment on the corrosion of dental alloys with different compositions, using electrochemical methods. The corrosion rates were obtained from the current-potential curves and electrochemical impedance spectroscopy (EIS). The effect of artificial saliva on the corrosion of dental alloys was dependent on alloy composition. Dissolution of the ions occurred in all tested dental alloys and the results were strongly dependent on the general alloy composition. Regarding the alloys containing nickel, the Ni-Cr and Ni-Cr-Ti alloys released 0.62 mg/L of Ni on average, while the Co-Cr dental alloy released ions between 0.01 and 0.03 mg/L of Co and Cr, respectively.The open-circuit potential stabilized at a higher level with lower deviation (standard deviation: Ni-Cr-6Ti = 32 mV/SCE and Co-Cr = 54 mV/SCE). The potenciodynamic curves of the dental alloys showed that the Ni-based dental alloy with >70 wt% of Ni had a similar curve and the Co-Cr dental alloy showed a low current density and hence a high resistance to corrosion compared with the Ni-based dental alloys. Some changes in microstructure were observed and this fact influenced the corrosion behavior for the alloys. The lower corrosion resistance also led to greater release of nickel ions to the medium. The quantity of Co ions released from the Co-Cr-Mo alloy was relatively small in the solutions. In addition, the quantity of Cr ions released into the artificial saliva from the Co-Cr alloy was lower than Cr release from the Ni-based dental alloys.

Influence of MC3T3-E1 preosteoblast culture on the corrosion of a T6-treated AZ91 alloy.

PubMed

Brooks, Emily K; Tobias, Menachem E; Yang, Shuying; Bone, Lawrence B; Ehrensberger, Mark T

2016-02-01

This study investigated the corrosion of artificially aged T6 heat-treated Mg-9%Al-1%Zn (AZ91) for biomedical applications. Corrosion tests and surface analysis were completed both with and without a monolayer of mouse preosteoblast MC3T3-E1 cells cultured on the sample. Electrochemical impedance spectroscopy (EIS) and inductively coupled plasma mass spectroscopy (ICPMS) were used to explore the corrosion processes after either 3 or 21 days of AZ91 incubation in cell culture medium (CCM). The EIS showed both the inner layer resistance (Rin ) and outer layer resistance (Rout ) were lower for samples without cells cultured on the surface at 3 days (Rin  = 2.64 e4 Ω/cm(2) , Rout  = 140 Ω/cm(2) ) compared to 21 days (Rin  = 3.60 e4 Ω/cm(2) , Rout  = 287 Ω/cm(2) ) due to precipitation of magnesium and calcium phosphates over time. Samples with preosteoblasts cultured on the surface had a slower initial corrosion (3 day, Rin  = 1.88 e5 Ω/cm(2) , Rout  = 1060 Ω/cm(2) ) which was observed to increase over time (21 day, Rin  = 2.99 e4 Ω/cm(2) , Rout  = 287 Ω/cm(2) ). Changes in the corrosion processes were thought to be related to changes in the coverage provided by the cell layer. Our results reveal that the presence of cells and biological processes are able to significantly influence the corrosion rate of AZ91. © 2015 Wiley Periodicals, Inc.

Effect of applied bias voltage on corrosion-resistance for TiC 1- xN x and Ti 1- xNb xC 1- yN y coatings

NASA Astrophysics Data System (ADS)

Caicedo, J. C.; Amaya, C.; Yate, L.; Aperador, W.; Zambrano, G.; Gómez, M. E.; Alvarado-Rivera, J.; Muñoz-Saldaña, J.; Prieto, P.

2010-02-01

Corrosion-resistance behavior of titanium carbon nitride (Ti-C-N) and titanium niobium carbon nitride (Ti-Nb-C-N) coatings deposited onto Si(1 0 0) and AISI 4140 steel substrates via r.f. magnetron sputtering process was analyzed. The coatings in contact with a solution of sodium chloride at 3.5% were studied by Tafel polarization curves and impedance spectroscopy methods (EIS). Variations of the bias voltage were carried out for each series of deposition to observe the influence of this parameter upon the electrochemical properties of the coatings. The introduction of Nb in the ternary Ti-C-N film was evaluated via X-ray diffraction (XRD) analysis. The structure was characterized by using Raman spectroscopy to identify ternary and quaternary compounds. Surface corrosion processes were characterized using optical microscopy and scanning electron microscopy (SEM). XRD results show conformation of the quaternary phase, change in the strain of the film, and lattice parameter as the effect of the Nb inclusion. The main Raman bands were assigned to interstitial phases and "impurities" of the coatings. Changes in Raman intensities were attributed to the incorporation of niobium in the Ti-C-N structure and possibly to resonance enhancement. Finally, the corrosion data obtained for Ti-C-N were compared with the results of corrosion tests of Ti-Nb-C-N coating. The results obtained showed that the incorporation of niobium to Ti-C-N coatings led to an increase in the corrosion-resistance. On another hand, an increase in the bias voltage led to a decrease in the corrosion-resistance for both Ti-C-N and Ti-Nb-C-N coatings.

Aqueous corrosion and corrosion-sensitive embrittlement of Fe{sub 3}Al-based and lean-aluminum iron aluminides

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kim, J.G.; Buchanan, R.A.

Aqueous corrosion and corrosion-sensitive embrittlement of iron aluminides were characterized as functions of environment, alloying content, notch sensitivity, and strain rate. Polarization resistance and cyclic anodic polarization evaluations were performed in 3.5 wt % NaCl, 200 ppM Cl{sup {minus}} (pH = 4), and 1 N NaOH solutions. In the mild acid-chloride solution [200 ppM Cl{sup {minus}} (pH = 4)], the pitting-corrosion resistance of the new lean-aluminum iron aluminides (FAP-Y and CM-Mo) was comparable to that of the Fe{sub 3}Al-based FAL-Mo. In the higher-chloride 3.5 wt % NaCl, the resistance of CM-Mo was slightly less but FAP-Y showed quite similar behaviormore » to FAL-Mo. In 1 N NaOH solution, all materials exhibited ideal passive behavior. Under slow-strain-rate test conditions in the mild acid-chloride electrolyte, prior work had shown the ductilities (% elongations) of Fe{sub 3}Al-based materials to be {approximately}7% and {approximately}1% at the freely-corroding and hydrogen-charging potentials, respectively. Present studied on the lean-aluminum materials have shown the ductilities to be {approximately}17% and {approximately}5%, respectively. Thus, the present results indicate that these new materials have reasonably-good aqueous-corrosion properties in chloride environments and significantly-enhanced ductilities under aqueous corrosion conditions. The strain rate and notch sensitivities of high-aluminum iron aluminide (FA-129) were investigated by performing slow-strain-rate tests. The notch sensitivity was independent of strain rate and the notch sensitivity in the aqueous environment was similar to that in air.« less

The Application of Electrochemical and Surface Analysis Approaches to Studying Copper Corrosion in Water: Fundamentals, Limitations, and Examples

EPA Science Inventory

Corrosion control is a concern for many drinking water utilities. The Lead and Copper Rule established a regulatory need to maintain a corrosion control program. Other corrosion-related issues such as “red” water resulting from excessive iron corrosion and copper pinhole leaks ...

NDI method to locate intergranular corrosion around fastener holes in aluminum wing skins

NASA Astrophysics Data System (ADS)

Rutherford, Paul S.

1998-03-01

Contact between galvanically dissimilar metals, such as cadmium plated steel fasteners and aluminum wing skins are known to be a source of corrosion. There is a design requirement to fill the void between the contacting surfaces of steel fasteners with a wet sealant. However, if the contacting surface is damaged or a void exists between the fastener head and the aluminum skin, moisture can collect and intergranular corrosion may occur along aluminum grain boundaries, which run parallel to the surface of the wing skin. If intergranular corrosion is allowed to propagate, delamination of the thin layers of aluminum, known as exfoliation corrosion will occur. When this intergranular corrosion reaches an exfoliated state, extensive rework is involved in removing the corrosion. This paper discusses the results of a USAF E-3A Engineering Service Task 89-E3B3-16 to develop a nondestructive inspection procedure to detect intergranular corrosion in an incipient state before it reaches exfoliation. Eddy current and ultrasonic inspection techniques were evaluated. A novel ultrasonic pulse echo technique was developed which utilizes a focus transducer with a hand held fixture. Inspections were performed on test parts which were removed from the upper wing skin of a retired 707 which had varying degrees of intergranular and exfoliation corrosion. Inspection results are compared to the results from the mechanical rework of the wing skin and dissection of a wing skin fastener hole.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Demchenko, V.S.; Filipov, V.I.; Semenyuk, V.I.

This article shows how the protective properties of preservative greases and oils can be determined by using an index which characterizes the kinetics of the corrosion processes on the metal surface under the layer of the lubricant. The index takes into account the actual time of existence of the corrosion products (from the moment of their appearance to the end of the test) and the actual area of the metal test specimens occupied by these products. In order to compare the proposed index to the indexes being used, the protective properties of aviation oil MS-20s, industrial oils I-12A and I-50A,more » and spindle oil AU, to which oil-soluble corrosion inhibitors were added, are examined. The mean rate of spreading of initial corrosion (referred to the total test time of 60 days) and the mean rate of corrosion (the total metal weight loss divided by the total surface area of the metal panel and the total test time) are calculated. It is concluded that in order to improve the reliability of protection ratings of preservative oils and greases, it is preferable to determine the rate of spreading of corrosion damage, the metal panel weight loss, and the increase in depth of the corrosion with allowance for the actual time of existence of corrosion (from the moment of appearance to the end of the test) and the actual area covered by the corrosion products. Includes a table.« less

ZM-21 magnesium alloy corrosion properties and cryogenic to elevated temperature mechanical properties

NASA Technical Reports Server (NTRS)

Montana, J. W.; Nelson, E. E.

1972-01-01

The mechanical properties of bare ZM-21 magnesium alloy flat tensile specimens were determined for test temperatures of +400 F, +300 F, +200 F, +80 F, 0 F, -100 F, -200 F, and -320 F. The ultimate tensile and yield strengths of the material increased with decreasing temperature with a corresponding reduction in elongation values. Stress corrosion tests performed under: (1) MSFC atmospheric conditions; (2) 95% relative humidity; and (3) submerged in 100 ppm chloride solution for 8 weeks indicated that the alloy is not susceptible to stress corrosion. The corrosion tests indicated that the material is susceptible to attack by crevice corrosion in high humidity and chemical type attack by chloride solution. Atmospheric conditions at MSFC did not produce any adverse effects on the material, probably due to the rapid formation of a protective oxide coating. In both the mechanical properties and the stress corrosion evaluations the test specimens which were cut transverse to the rolling direction had superior properties when compared to the longitudinal properties.

Corrosion behavior of low alloy steels in a wet-dry acid humid environment

NASA Astrophysics Data System (ADS)

Zhao, Qing-he; Liu, Wei; Yang, Jian-wei; Zhu, Yi-chun; Zhang, Bin-li; Lu, Min-xu

2016-09-01

The corrosion behavior of corrosion resistant steel (CRS) in a simulated wet-dry acid humid environment was investigated and compared with carbon steel (CS) using corrosion loss, polarization curves, X-ray diffraction (XRD), scanning electron microscopy (SEM), electron probe micro-analysis (EPMA), N2 adsorption, and X-ray photoelectron spectroscopy (XPS). The results show that the corrosion kinetics of both steels were closely related to the composition and compactness of the rust, and the electrochemical properties of rusted steel. Small amounts of Cu, Cr, and Ni in CRS increased the amount of amorphous phases and decreased the content of γ-FeOOH in the rust, resulting in higher compactness and electrochemical stability of the CRS rust. The elements Cu, Cr, and Ni were uniformly distributed in the CRS rust and formed CuFeO2, Cu2O, CrOOH, NiFe2O4, and Ni2O3, which enhanced the corrosion resistance of CRS in the wet-dry acid humid environment.

Magnesium based degradable biomaterials: A review

NASA Astrophysics Data System (ADS)

Gu, Xue-Nan; Li, Shuang-Shuang; Li, Xiao-Ming; Fan, Yu-Bo

2014-09-01

Magnesium has been suggested as a revolutionary biodegradable metal for biomedical applications. The corrosion of magnesium, however, is too rapid to match the rates of tissue healing and, additionally, exhibits the localized corrosion mechanism. Thus it is necessary to control the corrosion behaviors of magnesium for their practical use. This paper comprehensively reviews the research progress on the development of representative magnesium based alloys, including Mg-Ca, Mg-Sr, Mg-Zn and Mg-REE alloy systems as well as the bulk metallic glass. The influence of alloying element on their microstructures, mechanical properties and corrosion behaviors is summarized. The mechanical and corrosion properties of wrought magnesium alloys are also discussed in comparison with those of cast alloys. Furthermore, this review also covers research carried out in the field of the degradable coatings on magnesium alloys for biomedical applications. Calcium phosphate and biodegradable polymer coatings are discussed based on different preparation techniques used. We also compare the effect of different coatings on the corrosion behaviors of magnesium alloys substrate.

Effect of Aging Temperature on Corrosion Behavior of Sintered 17-4 PH Stainless Steel in Dilute Sulfuric Acid Solution

NASA Astrophysics Data System (ADS)

Szewczyk-Nykiel, Aneta; Kazior, Jan

2017-07-01

The general corrosion behavior of sintered 17-4 PH stainless steel processed under different processing conditions in dilute sulfuric acid solution at 25 °C was studied by open-circuit potential measurement and potentiodynamic polarization technique. The corrosion resistance was evaluated based on electrochemical parameters, such as polarization resistance, corrosion potential, corrosion current density as well as corrosion rate. The results showed that the precipitation-hardening treatment could significantly improve the corrosion resistance of the sintered 17-4 PH stainless steel in studied environment. As far as the influence of aging temperature on corrosion behavior of the sintered 17-4 PH stainless steel is concerned, polarization resistance and corrosion rate are reduced with increasing aging temperature from 480 up to 500 °C regardless of the temperature of solution treatment. It can be concluded that the highest corrosion resistance in 0.5 M H2SO4 solution exhibits 17-4 PH after solution treatment at 1040 °C followed by aging at 480 °C.

The effect of platform switching on the levels of metal ion release from different implant–abutment couples

PubMed Central

Alrabeah, Ghada O; Knowles, Jonathan C; Petridis, Haralampos

2016-01-01

The improved peri-implant bone response demonstrated by platform switching may be the result of reduced amounts of metal ions released to the surrounding tissues. The aim of this study was to compare the levels of metal ions released from platform-matched and platform-switched implant–abutment couples as a result of accelerated corrosion. Thirty-six titanium alloy (Ti-6Al-4V) and cobalt–chrome alloy abutments were coupled with titanium cylinders forming either platform-switched or platform-matched groups (n=6). In addition, 18 unconnected samples served as controls. The specimens were subjected to accelerated corrosion by static immersion in 1% lactic acid for 1 week. The amount of metal ions ion of each test tube was measured using inductively coupled plasma mass spectrometry. Scanning electron microscope (SEM) images and energy dispersive spectroscopy X-ray analyses were performed pre- and post-immersion to assess corrosion at the interface. The platform-matched groups demonstrated higher ion release for vanadium, aluminium, cobalt, chrome, and molybdenum compared with the platform-switched groups (P<0.05). Titanium was the highest element to be released regardless of abutment size or connection (P<0.05). SEM images showed pitting corrosion prominent on the outer borders of the implant and abutment platform surfaces. In conclusion, implant–abutment couples underwent an active corrosion process resulting in metal ions release into the surrounding environment. The highest amount of metal ions released was recorded for the platform-matched groups, suggesting that platform-switching concept has a positive effect in reducing the levels of metal ion release from the implant–abutment couples. PMID:27357323

The effect of pH on the corrosion behavior of intermetallic compounds Ni{sub 3}(Si,Ti) and Ni{sub 3}(Si,Ti) + 2Mo in sodium chloride solutions

DOE Office of Scientific and Technical Information (OSTI.GOV)

Priyotomo, Gadang, E-mail: gada001@lipi.go.id; Nuraini, Lutviasari, E-mail: Lutviasari@gmail.com; Kaneno, Yasuyuki, E-mail: kaneno@mtr.osakafu-u.ac.id

The corrosion behavior of the intermetallic compounds, Ni{sub 3}(Si,Ti) (L1{sub 2}: single phase) and Ni{sub 3}(Si,Ti) + 2Mo (L1{sub 2} and (L12 + Ni{sub ss}) mixture region), has been investigated using an immersion test, electrochemical method and surface analytical method (SEM; scanning electron microscope and EDAX: Energy Dispersive X-ray) in 0.5 kmol/m{sup 3} NaCl solutions at various pH. The corrosion behavior of nickel alloy C-276 was studied under the same experimental conditions as a reference. It was found that the uniform attack was observed on Ni{sub 3}(Si,Ti) for the immersion test at lower pH, while the pitting attack was observedmore » on this compound for this test at neutral solution. Furthermore, Ni{sub 3}(Si,Ti)+2Mo had the preferential dissolution of L1{sub 2} compared to (L1{sub 2} + Ni{sub ss}) mixture region at lower pH, while pitting attack occurred in (L1{sub 2} + Ni{sub ss}) mixture region at neutral solution. For both intermetallic compounds, the magnitude of pitting and uniform attack decrease with increasing pH of solutions. From the immersion test and polarization curves, the corrosion resistance of Ni{sub 3}(Si,Ti)+2Mo is lower than that of Ni{sub 3}(Si,Ti), while the nickel alloy C-276 is the highest one at various pH of solutions. On the other hand, in the lower pH of solutions, the corrosion resistance of tested materials decreased significantly compared to those in neutral and higher pH of solutions.« less

Effect of an Mg-rich matrix on the corrosion behavior of As-cast magnesium-aluminum alloys

NASA Astrophysics Data System (ADS)

Lee, Choong Do; Kang, Choon Sik; Shin, Kwang Seon

2000-10-01

In the present study, the corrosion behavior of as-cast Mg-Al and Mg-Al-Zn alloys was studied as a function of the Al content in the matrix. Corrosion properties such as the corrosion rate, corrosion potential, and repassivation tendency were estimated through immersion and electrochemical tests. The corrosion potential and corrosion rate of a solutionized alloy depend mainly on the Al content of the as-cast alloy. The variation of Al content in the Mg-rich matrix influences the stability of the passive film and the repassivation tendency, i.e., as the Al content of the matrix increases, the repassivation tendency of the surface protective film after its breakage deteriorates. Also, it was proven that the enhancement of corrosion resistance by heat treatment, as in T6, is due to the decrease of solute concentration in the matrix, in addition to the effect of the precipitate, which plays the role of a barrier against corrosion.

Effect of Waterproofing Admixtures on the Flexural Strength and Corrosion Resistance of Concrete

NASA Astrophysics Data System (ADS)

Geetha, A.; Perumal, P.

2012-02-01

This paper deals about the flexural strength and corrosion behaviour of concrete using waterproofing admixtures. The effect of waterproofing admixtures on the corrosion behaviour of RCC specimen has been studied by conducting accelerated corrosion test. To identify the effect of corrosion in pull out strength, corrosion process was induced by means of accelerated corrosion procedure. To accelerate the reinforcement corrosion, direct electric current was impressed on the rebar embedded in the specimen using a DC power supply system that has a facility to adjust voltage. The addition of waterproofing admixtures also shows the improvement in the flexural strength of concrete has been studied by conducting flexural strength tests on the concrete prism specimen of size 100 × 100 × 500 mm with and without admixtures for various dosages and various curing periods of 7 and 28 days. The results showed that the presence of waterproofing admixtures always improves the corrosion resistance and thus increases the strength of concrete due to the hydrophobic action of waterproofing admixtures.

High temperature gradient cobalt based clad developed using microwave hybrid heating

NASA Astrophysics Data System (ADS)

Prasad, C. Durga; Joladarashi, Sharnappa; Ramesh, M. R.; Sarkar, Anunoy

2018-04-01

The development of cobalt based cladding on a titanium substrate using microwave cladding technique is benchmark in coating area. The developed cladding would serve the function of a corrosion resistant coating under high temperatures. Clads of thickness 500 µm have been developed by microwave hybrid heating. A microwave furnace of 2.45GHz frequency was used at a 900W power level for processing. Impact of processing time on melting and adhesion of clad has been discussed. The study also extended to static thermal analysis of simple parts with cladding using commercial Finite Element analysis (FEA) software. A comparative study is explored between four variants of the clad being developed. The analysis has been conducted using a square sample. Similar temperature gradient is also shown for a proposed multi-layer coating, which includes a thermal barrier coating yttria stabilized zirconia (YSZ) on top of the corrosion resistant clad. The YSZ coating would protect the corrosion resistant cladding and substrate from high temperatures.

Quantitative sensing of corroded steel rebar embedded in cement mortar specimens using ultrasonic testing

NASA Astrophysics Data System (ADS)

Owusu Twumasi, Jones; Le, Viet; Tang, Qixiang; Yu, Tzuyang

2016-04-01

Corrosion of steel reinforcing bars (rebars) is the primary cause for the deterioration of reinforced concrete structures. Traditional corrosion monitoring methods such as half-cell potential and linear polarization resistance can only detect the presence of corrosion but cannot quantify it. This study presents an experimental investigation of quantifying degree of corrosion of steel rebar inside cement mortar specimens using ultrasonic testing (UT). A UT device with two 54 kHz transducers was used to measure ultrasonic pulse velocity (UPV) of cement mortar, uncorroded and corroded reinforced cement mortar specimens, utilizing the direct transmission method. The results obtained from the study show that UPV decreases linearly with increase in degree of corrosion and corrosion-induced cracks (surface cracks). With respect to quantifying the degree of corrosion, a model was developed by simultaneously fitting UPV and surface crack width measurements to a two-parameter linear model. The proposed model can be used for predicting the degree of corrosion of steel rebar embedded in cement mortar under similar conditions used in this study up to 3.03%. Furthermore, the modeling approach can be applied to corroded reinforced concrete specimens with additional modification. The findings from this study show that UT has the potential of quantifying the degree of corrosion inside reinforced cement mortar specimens.

Laser diagnostics for NTP fuel corrosion studies

NASA Technical Reports Server (NTRS)

Wantuck, Paul J.; Butt, D. P.; Sappey, A. D.

1993-01-01

Viewgraphs and explanations on laser diagnostics for nuclear thermal propulsion (NTP) fuel corrosion studies are presented. Topics covered include: NTP fuels; U-Zr-C system corrosion products; planar laser-induced fluorescence (PLIF); utilization of PLIF for corrosion product characterization of nuclear thermal rocket fuel elements under test; ZrC emission spectrum; and PLIF imaging of ZrC plume.

High-temperature corrosion of metals in the salt and metallic melts containing rare earths

NASA Astrophysics Data System (ADS)

Karpov, V. V.; Abramov, A. V.; Zhilyakov, A. Yu.; Belikov, S. V.; Volkovich, V. A.; Polovov, I. B.; Rebrin, O. I.

2016-09-01

A complex of independent methods was employed to study the corrosion resistance of molybdenum, zirconium, tantalum and tungsten in chloride, chloride-fluoride and fluoride-oxide melts based on LiCl, CaCl2, NaCl- KCl, LiF, and containing rare earths. Tests were conducted for 30 h at 750-1050 °C. The metals showed excellent corrosion resistance in fused chlorides (the corrosion rates were below 0.0005 g/(m2 h). Despite the presence of chemically active fluoride ions in the chloride-fluoride melts, the metals studied also showed very low corrosion rates, except molybdenum, for which the rate of corrosion was 0,8 g/(m2 h). The corrosion resistance of tantalum was considerably reduced in the fluoride-oxide melts; the corrosion rate was over 1 g/(m2 h) corresponding to the 8-th grade of stability and placing tantalum to the group of "low stability" materials.

Stress Corrosion Cracking Study of Aluminum Alloys Using Electrochemical Noise Analysis

NASA Astrophysics Data System (ADS)

Rathod, R. C.; Sapate, S. G.; Raman, R.; Rathod, W. S.

2013-12-01

Stress corrosion cracking studies of aluminum alloys AA2219, AA8090, and AA5456 in heat-treated and non heat-treated condition were carried out using electrochemical noise technique with various applied stresses. Electrochemical noise time series data (corrosion potential vs. time) was obtained for the stressed tensile specimens in 3.5% NaCl aqueous solution at room temperature (27 °C). The values of drop in corrosion potential, total corrosion potential, mean corrosion potential, and hydrogen overpotential were evaluated from corrosion potential versus time series data. The electrochemical noise time series data was further analyzed with rescaled range ( R/ S) analysis proposed by Hurst to obtain the Hurst exponent. According to the results, higher values of the Hurst exponents with increased applied stresses showed more susceptibility to stress corrosion cracking as confirmed in case of alloy AA 2219 and AA8090.

Research on Performance and Microstructure of Sewage Pipe Mortar Strengthened with Different Anti-Corrosion Technologies

NASA Astrophysics Data System (ADS)

Mu, Song; Zhou, Huaxin; Shi, Liang; Liu, Jianzhong; Cai, Jingshun; Wang, Feng

2017-10-01

Mostly urban underground sewage is the acidic corrosion environment with a high concentration of aggressive ions and microbe, which resulted in performance deterioration and service-life decrease of sewage concrete pipe. In order to effectively protect durability of the concrete pipe, the present paper briefly analysed the main degradation mechanism of concrete pipe attacked by urban underground sewage, and proposed that using penetrating and strengthening surface sealer based on inorganic chemistry. In addition, using index of compressive strength, weight loss and appearance level to investigate the influence of the sealer on corrosion resistance of mortar samples after different dry-wet cycles. Besides, comparative research on effect of the sealer, aluminate cement and admixture of corrosion resistance was also addressed. At last, the SEM technology was used to reveal the improvement mechanism of different technologies of corrosion resistance. The results indicated that the sealer and aluminate cement can significantly improve corrosion resistance of mortar. Besides, the improvement effect can be described as the descending order: the penetrating and strengthening surface sealer > aluminate cement > admixture of corrosion resistance. The mortar sample treated with the sealer displayed the condensed and sound microstructure which proved that the sealer can improve the corrosion resistance to urban underground sewage.

Analysis of in vivo corrosion of 316L stainless steel posterior thoracolumbar plate systems: a retrieval study.

PubMed

Majid, Kamran; Crowder, Terence; Baker, Erin; Baker, Kevin; Koueiter, Denise; Shields, Edward; Herkowitz, Harry N

2011-12-01

One hundred eighteen patients retrieved 316L stainless steel thoracolumbar plates, of 3 different designs, used for fusion in 60 patients were examined for evidence of corrosion. A medical record review and statistical analysis were also carried out. This study aims to identify types of corrosion and examine preferential metal ion release and the possibility of statistical correlation to clinical effects. Earlier studies have found that stainless steel spine devices showed evidence of mild-to-severe corrosion; fretting and crevice corrosion were the most commonly reported types. Studies have also shown the toxicity of metal ions released from stainless steel corrosion and how the ions may adversely affect bone formation and/or induce granulomatous foreign body responses. The retrieved plates were visually inspected and graded based on the degree of corrosion. The plates were then analyzed with optical microscopy, scanning electron microscopy, and energy dispersive x-ray spectroscopy. A retrospective medical record review was performed and statistical analysis was carried out to determine any correlations between experimental findings and patient data. More than 70% of the plates exhibited some degree of corrosion. Both fretting and crevice corrosion mechanisms were observed, primarily at the screw plate interface. Energy dispersive x-ray spectroscopy analysis indicated reductions in nickel content in corroded areas, suggestive of nickel ion release to the surrounding biological environment. The incidence and severity of corrosion was significantly correlated with the design of the implant. Stainless steel thoracolumbar plates show a high incidence of corrosion, with statistical dependence on device design.

Corrosion of metals in wood : comparing the results of a rapid test method with long-term exposure tests across six wood treatments

Treesearch

Samuel L. Zelinka; Donald S. Stone

2011-01-01

This paper compares two methods of measuring the corrosion of steel and galvanized steel in wood: a long-term exposure test in solid wood and a rapid test method where fasteners are electrochemically polarized in extracts of wood treated with six different treatments. For traditional wood preservatives, the electrochemical extract method correlates with solid wood...

Corrosion fatigue studies on a bulk glassy Zr-based alloy under three-point bending

NASA Astrophysics Data System (ADS)

Grell, Daniel; Wilkin, Yannic; Gostin, Petre F.; Gebert, Annett; Kerscher, Eberhard

2016-12-01

Corrosion fatigue (CF) tests were carried out on bulk glassy Zr52.5Cu17.9Al10Ni14.6Ti5 (Vitreloy 105) samples under load-controlled three-point bending conditions with a load ratio of R = 0.1 in 0.01 M Na2SO4 + 0.01 M NaCl electrolyte. During cyclic testing, the bar-shaped specimens were polarized in situ at constant potentials and the current was monitored. Three different anodic potentials within the interval between the pitting potential EP and the repassivation potential ER, and three different load amplitudes were applied. In some cases, in situ microscopic observations revealed the formation of black corrosion products in the vicinity of the crack tip during anodic polarization. Fractographic analysis revealed a clear distinction between two modes of crack growth characterized by smooth dissolution induced regions on the one hand and slim fast fracture areas on the other hand. Both alternating features contributed to a broad striated corrosion fatigue fracture surface. Moreover, further fatigue tests were carried out under free corrosion conditions yielding additional information on crack initiation and crack propagation period by means of the open circuit potential (OCP) changes. Thereby, a slight increase in OCP was detected after rupture of the passive layer due to bare metal exposed to the electrolyte. The electrochemical response increased continuously according to stable crack propagation until fracture occurred. Finally, the fracture surfaces of the corrosion fatigue samples were investigated by energy dispersive X-ray with the objective of analyzing the elemental distribution after anodic dissolution. Interestingly, anodic polarization at a near repassivation potential of -50 mV vs. SCE (Saturated Calomel Electrode, E = 0.241 V vs. SHE, Standard Hydrogen Electrode) led to favorable effects on the fatigue lifetime. In conclusion, all results are conflated to a corrosion fatigue model for bulk glassy Vitreloy 105 under anodic polarization in chloride-containing electrolyte and compared to the previously proposed stress corrosion mechanisms under similar conditions.

The corrosion effect of ozonated seawater solution on titanium in polymer generated crevice environments

DOE Office of Scientific and Technical Information (OSTI.GOV)

Leveillee, S.Y.

1998-01-01

Two different tests were designed to evaluate the reaction of various polymers and grade-2 titanium in ozonated seawater in conjunction with a comparative analysis in an aerated seawater solution. The first was a weight loss test measuring the weight change of Polyvinyl chloride (PVC), Polyethylene and Teflon{trademark} in both ozonated and aerated artificial seawater baths. The second test was designed to induce crevice corrosion on the titanium test samples using various crevice generating materials in both ozonated and aerated solutions. The materials used to create the crevices were grade-2 titanium washers, PVC, Polyethylene, Saran and Teflon{trademark}. The weight loss testmore » showed that all three polymers lost weight in the ozonated bath. The results of the titanium washer crevice test provided no indication of corrosion or surface discoloration in either the ozonated or aerated solutions. Energy dispersive spectrometry (EDS) analysis found no fluorine, chlorine or other corrosion product. The PVC samples in the aerated bath also showed no signs of corrosion, but the PVC samples in the ozonated tank had light brown rings of surface discoloration. One of the ozonated PVC samples did show evidence of chlorine in the corrosion product. The outer circumference of the ozonated PVC washers exhibited the same type bleaching effect as in the weight loss samples, but the whitening of these samples were more pronounced. The polyethylene samples under aeration showed no discoloration or presence of fluorine or chlorine. The polyethylene crevice samples in the ozonated solution all exhibited the distinct brilliant blue color of titanium oxide. Fluorine was found in the corrosion product on only one of the samples. Chlorine was found on the surface of one of the other corrosion coupons. The results of the Teflon{trademark} crevice samples substantiated the previous Rensselaer study.« less

Identification of corrosion product on medium carbon steel under the exposure of Banda Aceh’s atmosphere

NASA Astrophysics Data System (ADS)

Thalib, Sulaiman; Ikhsan, Muharil; Fonna, Syarizal; Huzni, Syifaul; Ridha, Syahrir

2018-05-01

This research was conducted to study the form of corrosion products of medium carbon steel under the exposure of Banda Aceh’s atmosphere. The medium carbon steel samples which the size based on ASTM G 50 were exposed in open areas around the Engineering Faculty, Syiah Kuala University, Darussalam - Banda Aceh, Aceh province, Indonesia. The study was carried out from January through December 2016. The corrosion product formed on the surface of the samples was studied using X-ray Diffraction (XRD) and Scanning Electron Microscope (SEM) method. Measurements of weight loss due to atmospheric corrosion as a basis for calculating corrosion rates was referring to ASTM G1. Corrosion product found based on XRD analysis was lepidocrocite (FeO2, γ-FeOOH) and goethite (FeO2, α-FeOOH). The results agreed with SEM analysis that also indicates to lepidocrocite and goethite. The corrosion rate for twelve months showed that the highest rate occurs in the period of March-April that was 0.024 mpy. During twelve months exposure, the corrosion products consist of lepidocrocite and goethite. Significant changes began to occur in the eighth month, where the product of corrosion was almost entirely goethite.

Application of thin layer activation technique for monitoring corrosion of carbon steel in hydrocarbon processing environment.

PubMed

Saxena, R C; Biswal, Jayashree; Pant, H J; Samantray, J S; Sharma, S C; Gupta, A K; Ray, S S

2018-05-01

Acidic crude oil transportation and processing in petroleum refining and petrochemical operations cause corrosion in the pipelines and associated components. Corrosion monitoring is invariably required to test and prove operational reliability. Thin Layer Activation (TLA) technique is a nuclear technique used for measurement of corrosion and erosion of materials. The technique involves irradiation of material with high energy ion beam from an accelerator and measurement of loss of radioactivity after the material is subjected to corrosive environment. In the present study, TLA technique has been used to monitor corrosion of carbon steel (CS) in crude oil environment at high temperature. Different CS coupons were irradiated with a 13 MeV proton beam to produce Cobalt-56 radioisotope on the surface of the coupons. The corrosion studies were carried out by subjecting the irradiated coupons to a corrosive environment, i.e, uninhibited straight run gas oil (SRGO) containing known amount of naphthenic acid (NA) at high temperature. The effects of different parameters, such as, concentration of NA, temperature and fluid velocity (rpm) on corrosion behaviour of CS were studied. Copyright © 2018 Elsevier Ltd. All rights reserved.

Corrosion resistance of sodium sulfate coated cobalt-chromium-aluminum alloys at 900 C, 1000 C, and 1100 C

NASA Technical Reports Server (NTRS)

Santoro, G. J.

1979-01-01

The corrosion of sodium sulfate coated cobalt alloys was measured and the results compared to the cyclic oxidation of alloys with the same composition, and to the hot corrosion of compositionally equivalent nickel-base alloys. Cobalt alloys with sufficient aluminum content to form aluminum containing scales corrode less than their nickel-base counterparts. The cobalt alloys with lower aluminum levels form CoO scales and corrode more than their nickel-base counterparts which form NiO scales.

Structural Effects of Reinforced Concrete Beam Due to Corrosion

NASA Astrophysics Data System (ADS)

Noh, Hamidun Mohd; Idris, Nur'ain; Noor, Nurazuwa Md; Sarpin, Norliana; Zainal, Rozlin; Kasim, Narimah

2018-03-01

Corrosion of steel in reinforced concrete is one of the main issues among construction stakeholders. The main consequences of steel corrosion include loss of cross section of steel area, generation of expansive pressure which caused cracking of concrete, spalling and delaminating of the concrete cover. Thus, it reduces the bond strength between the steel reinforcing bar and concrete, and deteriorating the strength of the structure. The objective of this study is to investigate the structural effects of corrosion damage on the performance of reinforced concrete beam. A series of corroded reinforced concrete beam with a corrosion rate of 0%, 20% and 40% of rebar corrosion is used in parametric study to assess the influence of different level of corrosion rate to the structural performance. As a result, the used of interface element in the finite element modelling predicted the worst case of corrosion analysis since cracks is induced and generate at this surface. On the other hand, a positive linear relationship was sketched between the increase of expansive pressure and the corrosion rate. Meanwhile, the gradient of the graph is decreased with the increase of steel bar diameter. Furthermore, the analysis shows that there is a significant effect on the load bearing capacity of the structure where the higher corrosion rate generates a higher stress concentration at the mid span of the beam. This study could predict the residual strength of reinforced concrete beam under the corrosion using the finite element analysis. The experimental validation is needed on the next stage to investigate the quantitative relation between the corrosion rate and its influence on the mechanical properties.

Effect of environmental factor and microstructure on morphology of corrosion products in CO{sub 2} environments

DOE Office of Scientific and Technical Information (OSTI.GOV)

Ueda, Masakatsu; Takabe, Hideki

The effect of environmental factors such as HCO{sup 3+} ion, CH{sub 3}COO{minus} ion, and Ca{sup 2+} ion, and microstructure on morphology of corrosion products was investigated in CO{sub 2} environments with 0.3MPa CO{sub 2} at 80 C. Steel J55 with ferritic-pearlitic microstructure and Steel N80 with martensitic microstructure were used as testing materials. Steel J55 showed good localized-corrosion resistance compared with Steel N80. A linear relationship between pH and corrosion rate was obtained in Steel J55 with homogeneous corrosion, but the relationship was not so good in Steel N80 with heterogeneous corrosion. The good localized-corrosion of Steel J55 can bemore » explained from the morphology of corrosion products. Namely, as Steel J55 corrodes away, there is lamellar cementite left behind. An increase in the local concentration of Fe{sup 2+} ions arises in the cavities between lamellar cementites and leads to FeCO{sub 3} formation between those. Then, the lamellar cementite helps to anchor the corrosion product. In Steel N80 with the homogeneous dispersed-cementite to act as cathodic site, the corrosion product peels off partially because not having the anchor effect in Steel J55. Therefore, Steel N80 suffered from severe corrosion on locations without the corrosion product. In CaCl{sub 2} solution, FeCO{sub 3} and CaCO{sub 3} were identified as corrosion product of Steel J55 by X-ray analysis. In this case, FeCO{sub 3} forms in the cavities between lamellar cementites due to a local flow stagnation and higher local Fe{sup 2+} ion concentration, but in former ferrite phase, the higher local Fe{sup 2+} concentration does not arise and CaCO{sub 3} crystallizes.« less

Corrosion fatigue of Inconel 718 and Incoloy 903

NASA Technical Reports Server (NTRS)

Franklin, D. B.; Nelson, E. E.

1981-01-01

Corrosion fatigue tests were conducted on Inconel 718 and Incoloy 903 in distilled water, 500 ppm NaCl, and 3.5% NaCl. Results were compared to the endurance limit in air. For Inconel 718, the corrosion fatigue strength (CFS) IN 3.5% NaCl WAS 328 MPa or 75 percent of the endurance limit. For Incoloy 903, the CFS ranged from 234 MPa in distilled water (68 percent of the endurance limit) to 103 MPa in 3.5% NaCl (30 percent of the endurance limit). Results indicate that, for components which have limited fatigue life, an evaluation of the combined effects of fatigue and the corrosive atmosphere must be considered in projecting useful lifetimes.

Electrochemical monitoring of high-temperature molten-salt corrosion

DOE Office of Scientific and Technical Information (OSTI.GOV)

Gao, G.; Stott, F.H.; Dawson, J.L.

1990-02-01

Hot molten-salt corrosion can cause serious metal degradation in boiler plant, incinerators, and furnaces. In this research, electrochemical-impedance and electrochemical-noise techniques have been evaluated for the monitoring of hot-corrosion processes in such plants. Tests have been carried out on Ni-1% Co and Alloy 800, a commercial material of interest to operators of industrial plants. Electrochemical-impedance and electrochemical-noise data were compared with the results of metallographic examination of the test alloys and showed reasonable correlation between the electrochemical data and the actual degradation processes. This preliminary work indicated that the electrochemical techniques show considerable promise as instruments for the monitoring ofmore » high-temperature corrosion processes.« less

Corrosion Behavior of Low-C Medium-Mn Steel in Simulated Marine Immersion and Splash Zone Environment

NASA Astrophysics Data System (ADS)

Zhang, Dazheng; Gao, Xiuhua; Su, Guanqiao; Du, Linxiu; Liu, Zhenguang; Hu, Jun

2017-05-01

The corrosion behavior of low-C medium-Mn steel in simulated marine immersion and splash zone environment was studied by static immersion corrosion experiment and wet-dry cyclic corrosion experiment, respectively. Corrosion rate, corrosion products, surface morphology, cross-sectional morphology, elemental distribution, potentiodynamic polarization curves and electrochemical impedance spectra were used to elucidate the corrosion behavior of low-C medium-Mn steel. The results show that corrosion rate in immersion zone is much less than that in splash zone owing to its relatively mild environment. Manganese compounds are detected in the corrosion products and only appeared in splash zone environment, which can deteriorate the protective effect of rust layer. With the extension of exposure time, corrosion products are gradually transformed into dense and thick corrosion rust from the loose and porous one in these two environments. But in splash zone environment, alloying elements of Mn appear significant enrichment in the rust layer, which decrease the corrosion resistance of the steel.

In-situ electrochemical study of interaction of tribology and corrosion in artificial hip prosthesis simulators.

PubMed

Yan, Yu; Dowson, Duncan; Neville, Anne

2013-02-01

The second generation Metal-on-Metal (MoM) hip replacements have been considered as an alternative to commonly used Polyethylene-on-Metal (PoM) joint prostheses due to polyethylene wear debris induced osteolysis. However, the role of corrosion and the biofilm formed under tribological contact are still not fully understood. Enhanced metal ion concentrations have been reported widely from hair, blood and urine samples of patients who received metal hip replacements and in isolated cases when abnormally high levels have caused adverse local tissue reactions. An understanding of the origin of metal ions is really important in order to design alloys for reduced ion release. Reciprocating pin-on-plate wear tester is a standard instrument to assess the interaction of corrosion and wear. However, more realistic hip simulator can provide a better understanding of tribocorrosion process for hip implants. It is very important to instrument the conventional hip simulator to enable electrochemical measurements. In this study, simple reciprocating pin-on-plate wear tests and hip simulator tests were compared. It was found that metal ions originated from two sources: (a) a depassivation of the contacting surfaces due to tribology (rubbing) and (b) corrosion of nano-sized wear particles generated from the contacting surfaces. Copyright © 2012 Elsevier Ltd. All rights reserved.

Resistance of Nanostructured Environmental Barrier Coatings to the Movement of Molten Salts

NASA Astrophysics Data System (ADS)

Rao, S.; Frederick, L.; McDonald, A.

2012-09-01

Corrosion of components in a recovery boiler is a major problem faced by the pulp and paper industry. The superheater tubes become severely corroded due to the presence of sulfidic gases in the boiler and molten salts which are deposited on the surface of the tubes. As a result, the boiler must be decommissioned for expensive maintenance and repairs. Yttria-stabilized zirconia (YSZ) coatings have been shown to provide corrosion resistance when applied on gas turbines operating at high temperatures. Air plasma-sprayed YSZ environmental barrier coatings on Type 309 stainless steel were exposed to three different corrosive environments: Test A—600 °C, salt vapors, flue gases, 168 h; Test B—600 °C, molten salt, air, 168 h; and Test C—600 °C, molten salt, flue gases, 168 h. Two different types of YSZ coatings—conventional YSZ and nanostructured YSZ—were tested to study their resistance to corrosion and molten salt penetration. The performances of both types of coatings were evaluated, and a comparative study was conducted. It was found that the nanostructured YSZ samples protected the stainless steel substrate better than their conventional counterparts. This superior performance was attributed to the presence of semi-molten nano-agglomerates present in the coating microstructure, which acted as collection points for the penetrating molten salts.

The Evaluation of Hydroxyapatite (HA) Coated and Uncoated Porous Tantalum for Biomedical Material Applications

NASA Astrophysics Data System (ADS)

Safuan, Nadia; Sukmana, Irza; Kadir, Mohammed Rafiq Abdul; Noviana, Deni

2014-04-01

Porous tantalum has been used as an orthopedic implant for bone defects as it has a good corrosion resistance and fatigue behaviour properties. However, there are some reports on the rejection of porous Ta after the implantation. Those clinical cases refer to the less bioactivity of metallic-based materials. This study aims to evaluate hydroxyapatite coated and uncoated porous Tantalum in order to improve the biocompatibility of porous tantalum implant and osseointegration. Porous tantalum was used as metallic-base substrate and hydroxyapatite coating has been done using plasma-spraying technique. Scanning Electron Microscopy (SEM) and Field Emission Scanning Electron Microscopy (FESEM) techniques were utilizes to investigate the coating characteristics while Confocal Raman Microscopy to investigate the interface and image. The effect of coating to the corrosion behaviour was assessed by employing potentiodynamic polarization tests in simulated body fluid at 37±1 °C. Based on SEM and FESEM results, the morphologies as well the weight element consists in the uncoated and hydroxyapatite coated porous tantalum were revealed. The results indicated that the decrease in corrosion current density for HA coated porous Ta compared to the uncoated porous Ta. This study concluded that by coating porous tantalum with HA supports to decrease the corrosion rate of pure porous.

Surface chemistry of bulk nanocrystalline pure iron and electrochemistry study in gas-flow physiological saline.

PubMed

Nie, F L; Zheng, Y F

2012-07-01

Conventional microcrystalline pure iron (MC-Fe) becomes a new candidate as biodegradable metals, which has the insufficient physical feature and inferior biodegradation behavior. Novel bulk nanocrystalline pure iron (NC-Fe) was fabricated via equal channel angular pressing technique in the present work to overcome these problems. The contact angle test with water and glycerol droplets shows a smaller angle (though >90°) of NC-Fe than that of MC-Fe, which implies a lower surface energy of NC-Fe. The surface roughness of NC-Fe increased greatly than that of MC-Fe. A further comparative study of corrosion and electrochemistry performance between NC-Fe and its original MC-Fe was investigated in physiological saline with different dissolved oxygen concentration, aiming to in vitro simulate the corrosion process of coronary stent occurred in physiological environment. The electrochemical impedance spectra analysis and anodic polarization measurements indicated that the NC-Fe exhibited higher corrosion resistance than that of the MC-Fe; meanwhile obvious enhanced corrosion resistance with the decrement of dissolved oxygen concentration was observed. Related equivalent circuit model and surface reconstruction process were further discussed, and the degradation mechanism of the MC-Fe and NC-Fe were finally established. Copyright © 2012 Wiley Periodicals, Inc.

Controlling Surface Chemistry to Deconvolute Corrosion Benefits Derived from SMAT Processing

NASA Astrophysics Data System (ADS)

Murdoch, Heather A.; Labukas, Joseph P.; Roberts, Anthony J.; Darling, Kristopher A.

2017-07-01

Grain refinement through surface plastic deformation processes such as surface mechanical attrition treatment has shown measureable benefits for mechanical properties, but the impact on corrosion behavior has been inconsistent. Many factors obfuscate the particular corrosion mechanisms at work, including grain size, but also texture, processing contamination, and surface roughness. Many studies attempting to link corrosion and grain size have not been able to decouple these effects. Here we introduce a preprocessing step to mitigate the surface contamination effects that have been a concern in previous corrosion studies on plastically deformed surfaces; this allows comparison of corrosion behavior across grain sizes while controlling for texture and surface roughness. Potentiodynamic polarization in aqueous NaCl solution suggests that different corrosion mechanisms are responsible for samples prepared with the preprocessing step.

How Dangerous Can Localized Corrosion Be? An Experiment that Studies Its Effects.

ERIC Educational Resources Information Center

Celdran, R.; Gonzalo, P.

1988-01-01

Considers three common cases of localized corrosion of metals: pitting, crevice, and stress corrosion. Provides experimental methods for studying all three methods. Includes a discussion of expected results. (ML)