Environmentally Friendly Bio-Based Vinyl Ester Resins for Military Composite Structures

DTIC Science & Technology

2008-12-01

composites, fatty acid , vinyl ester 9. Distribution $tatement (requr’iedl lsmanuscript subjectto export control? E ruo I yes Circfe appropriate l tter and...resins is to replace some or all of the styrene with fatty acid -based monomers. These fatty acid vinyl ester resins allow for the formulation of high...validation studies have been performed, showing that the fatty acid -based resins have sufficient, modulus, strength, glass transition temperature, and

High performance mixed bisimide resins and composites based thereon

NASA Technical Reports Server (NTRS)

Parker, J. A.; ations.

1986-01-01

Mixtures of bismaleimide/biscitraconirnide resins produces materials which have better handling, processing or mechanical and thermal properties, particularly in graphite composites, than materials made with the individual resins. The mechanical strength of cured graphite composites prepared from a 1:1 copolymer of such bisimide resins is excellent at both ambient and elevated temperatures. The copolymer mixture provides improved composites which are lighter than metals and replace metals in many aerospace applications.

Difference in the color stability of direct and indirect resin composites

PubMed Central

LEE, Yong-Keun; YU, Bin; LIM, Ho-Nam; LIM, Jin Ik

2011-01-01

Indirect resin composites are generally regarded to have better color stability than direct resin composites since they possess higher conversion degree Objective The present study aimed at comparing the changes in color (∆E) and color coordinates (∆L, ∆a and ∆b) of one direct (Estelite Sigma: 16 shades) and 2 indirect resin composites (BelleGlass NG: 16 shades; Sinfony: 26 shades) after thermocycling. Material and Methods Resins were packed into a mold and light cured; post-curing was performed on indirect resins. Changes in color and color coordinates of 1-mm-thick specimens were determined after 5,000 cycles of thermocycling on a spectrophotometer. Results ∆E values were in the range of 0.3 to 1.2 units for direct resins, and 0.3 to 1.5 units for indirect resins, which were clinically acceptable (∆E<3.3). Based on t-test, ∆E values were not significantly different by the type of resins (p>0.05), while ∆L, ∆a and ∆b values were significantly different by the type of resins (p<0.05). For indirect resins, ∆E values were influenced by the brand, shade group and shade designation based on three-way ANOVA (p<0.05). Conclusion Direct and indirect resin composites showed similar color stability after 5,000 cycles of thermocycling; however, their changes in the color coordinates were different. PMID:21552717

Metal-composite adhesion based on diazonium chemistry.

PubMed

Oweis, Yara; Alageel, Omar; Kozak, Paige; Abdallah, Mohamed-Nur; Retrouvey, Jean-Marc; Cerruti, Marta; Tamimi, Faleh

2017-11-01

Composite resins do not adhere well to dental alloys. This weak bond can result in failure at the composite-metal interface in fixed dental prostheses and orthodontic brackets. The aim of this study was to develop a new adhesive, based on diazonium chemistry, to facilitate chemical bonding between dental alloys and composite resin. Samples of two types of dental alloys, stainless steel and cobalt chromium were primed with a diazonium layer in order to create a surface coating favorable for composite adhesion. Untreated metal samples served as controls. The surface chemical composition of the treated and untreated samples was analyzed by X-ray photoelectron spectroscopy (XPS) and the tensile strength of the bond with composite resin was measured. The diazonium adhesive was also tested for shear bond strength between stainless steel orthodontic brackets and teeth. XPS confirmed the presence of a diazonium coating on the treated metals. The coating significantly increased the tensile and shear bond strengths by three and four folds respectively between the treated alloys and composite resin. diazonium chemistry can be used to develop composite adhesives for dental alloys. Diazonium adhesion can effectively achieve a strong chemical bond between dental alloys and composite resin. This technology can be used for composite repair of fractured crowns, for crown cementation with resin based cements, and for bracket bonding. Copyright © 2017 The Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Development of Refined Natural Resin based Cashew Nut Shell Oil Liquid (CNSL) for Brake Pads Composite

NASA Astrophysics Data System (ADS)

Wahyuningsih, S.; Ramelan, A. H.; Rahmawati, P.; Tamtama, B. P. N.; Sari, P. P.; Sari, P. L.; Ichsan, S.; Kristiawan, Y. R.; Aini, F. N.

2017-02-01

Brake is one of the most important components in the vehicle. One type of brake that widely used is brake-based composites. One of the manufacture of composite material is resin. Cashew Nut Shell Liquid (CNSL) is a natural material which has chemical structure similar to synthetic phenol so it can be an alternative as a resin. Brake pads manufacture using CNSL as resin composites made to obtain the brake which is strong, wear-resistant, and environmentally friendly. The composite made using powder metallurgy techniques by mixing ingredients such as rubber, fibre glass, carbon, mineral sands and phenolic resin. Two formulas were composed by varying the resin and iron mineral sands in 5 grams. Composites were tested using Universal Testing Machine (UTM). The tensile strength result of those formulas are 600 N and 900 N and the elongations are 1.98 mm and 2.59 mm respectively. Formula 2 has a better tensile strength due to the addition of more resin is 15%. Since the better properties, formula 2 was derivated to 4 extended formulas and showed excellent pressure strength reached 20.000 N. It indicates that the addition of the resin can improve the mechanical properties of a composite.

Magnetocaloric effect and corrosion resistance of La(Fe, Si)13 composite plates bonded by different fraction of phenolic resin

NASA Astrophysics Data System (ADS)

Zhang, K. S.; Xue, J. N.; Wang, Y. X.; Sun, H.; Long, Y.

2018-04-01

La(Fe, Si)13-based composite plates were successfully fabricated using different amount of phenolic resin. The introduction of phenolic resin as binder increased the corrosion resistance and maintained giant magnetocaloric effect for La(Fe, Si)13-based composite plates. It was found that corroded spots were firstly observed on the boundaries between resin and La(Fe, Si)13 particles, rather than in La(Fe, Si)13-based particles, after being immersed in static distilled water. The corrosion rate decreased significantly with the increase of resin content. And the increase of the content of phenolic resin leads to the reduction of corrosion current density. Meanwhile, the volumetric magnetic entropy change ΔSM decreases slightly as the content of phenolic resin increases. The ΔSM of the plates with 3 wt.%, 5 wt.% and 8 wt.% resin are 63.1, 61.2 and 59.8 mJ/cm3 K under a low magnetic field change of 1 T, respectively.

Characterization of PMR polyimide resin and prepreg

NASA Technical Reports Server (NTRS)

Lindenmeyer, P. H.; Sheppard, C. H.

1984-01-01

Procedures for the chemical characterization of PMR-15 resin solutions and graphite-reinforced prepregs were developed, and a chemical data base was established. In addition, a basic understanding of PMR-15 resin chemistry was gained; this was translated into effective processing procedures for the production of high quality graphite composites. During the program the PMR monomers and selected model compounds representative of postulated PMR-15 solution chemistry were acquired and characterized. Based on these data, a baseline PMR-15 resin was formulated and evaluated for processing characteristics and composite properties. Commercially available PMR-15 resins were then obtained and chemically characterized. Composite panels were fabricated and evaluated.

Performance Properties of Graphite Reinforced Composites with Advanced Resin Matrices

NASA Technical Reports Server (NTRS)

Kourtides, Demetrius A.

1980-01-01

This article looks at the effect of different resin matrices on thermal and mechanical properties of graphite composites, and relates the thermal and flammability properties to the anaerobic char yield of the resins. The processing parameters of graphite composites utilizing graphite fabric and epoxy or other advanced resins as matrices are presented. Thermoset resin matrices studied were: aminecured polyfunctional glycidyl aminetype epoxy (baseline), phenolicnovolac resin based on condensation of dihydroxymethyl-xylene and phenol cured with hexamine, two types of polydismaleimide resins, phenolic resin, and benzyl resin. The thermoplastic matrices studied were polyethersulfone and polyphenylenesulfone. Properties evaluated in the study included anaerobic char yield, limiting oxygen index, smoke evolution, moisture absorption, and mechanical properties at elevated temperatures including tensile, compressive, and short-beam shear strengths. Generally, it was determined that graphite composites with the highest char yield exhibited optimum fire-resistant properties.

A comparative evaluation of the staining capacity of microhybrid and nanohybrid resin-based composite to indian spices and food colorants: An In vitro study.

PubMed

Usha, Carounanidy; Rao, Sathyanarayanan Rama; George, Geena Mary

2018-01-01

Resin composite restorative materials can mimic the natural color and shade of the tooth. However, exogenous colorants from food and drinks can stain them due to adsorption. The influence of Indian food colorants and spices on resin composite restorations has not been evaluated extensively. This study aims to evaluate the staining capacity of microhybrid and nanohybrid resin-based composites, to saffron extract, tandoori powder, and turmeric powder. Forty samples of microhybrid (Kulzer Charisma) and nanohybrid (3M Filtek Z350) resin composites were prepared using an acrylic template of dimension 5 mm × 3 mm. They were randomly divided into four groups and immersed into solutions of saffron extract, tandoori powder, and turmeric powder. Distilled water was used as the control group. Color values (LFNx01, aFNx01, bFNx01) were measured by colorimeter using the CIE LFNx01aFNx01bFNx01 system before and after 72 h of immersion. Color differences ΔEFNx01ab were statistically analyzed. Two-way ANOVA and post-hoc Tukey (honest significant difference) test were done using IBM SPSS Statistics for Windows, Version 19.0. Armonk, NY: IBM Corp. : All the immersion media changed the color of the resin composites to varying degrees. However, turmeric solution showed the maximum mean color variation ΔEFNx01ab of 14.8 ± 2.57 in microhybrid resin composites and 16.8 ± 3.50 in nanohybrid resin composites. Microhybrid and nanohybrid resin composites tend to stain to Indian food colorants, especially to turmeric powder.

Characterization of water sorption, solubility, and roughness of silorane- and methacrylate-based composite resins.

PubMed

Giannini, M; Di Francescantonio, M; Pacheco, R R; Cidreira Boaro, L C; Braga, R R

2014-01-01

The objective of this study was to evaluate the surface roughness (SR), water sorption (WS), and solubility (SO) of four composite resins after finishing/polishing and after one year of water storage. Two low-shrinkage composites (Filtek Silorane [3M ESPE] and Aelite LS [Bisco Inc]) and two composites of conventional formulations (Heliomolar and Tetric N-Ceram [Ivoclar Vivadent]) were tested. Their respective finishing and polishing systems (Sof-Lex Discs, 3M ESPE; Finishing Discs Kit, Bisco Inc; and Astropol F, P, HP, Ivoclar Vivadent) were used according to the manufacturers' instructions. Ten disc-shaped specimens of each composite resin were made for each evaluation. Polished surfaces were analyzed using a profilometer after 24 hours and one year. For the WS and SO, the discs were stored in desiccators until constant mass was achieved. Specimens were then stored in water for seven days or one year, at which time the mass of each specimen was measured. The specimens were dried again and dried specimen mass determined. The WS and SO were calculated from these measurements. Data were analyzed by two-way analysis of variance and Tukey post hoc test (α=0.05). Filtek Silorane showed the lowest SR, WS, and SO means. Water storage for one year increased the WS means for all composite resins tested. The silorane-based composite resin results were better than those obtained for methacrylate-based resins. One-year water storage did not change the SR and SO properties in any of the composite resins.

Composites

NASA Astrophysics Data System (ADS)

Taylor, John G.

The Composites market is arguably the most challenging and profitable market for phenolic resins aside from electronics. The variety of products and processes encountered creates the challenges, and the demand for high performance in critical operations brings value. Phenolic composite materials are rendered into a wide range of components to supply a diverse and fragmented commercial base that includes customers in aerospace (Space Shuttle), aircraft (interiors and brakes), mass transit (interiors), defense (blast protection), marine, mine ducting, off-shore (ducts and grating) and infrastructure (architectural) to name a few. For example, phenolic resin is a critical adhesive in the manufacture of honeycomb sandwich panels. Various solvent and water based resins are described along with resin characteristics and the role of metal ions for enhanced thermal stability of the resin used to coat the honeycomb. Featured new developments include pultrusion of phenolic grating, success in RTM/VARTM fabricated parts, new ballistic developments for military vehicles and high char yield carbon-carbon composites along with many others. Additionally, global regional market resin volumes and sales are presented and compared with other thermosetting resin systems.

Aqueous vinylidene fluoride polymer coating composition

NASA Technical Reports Server (NTRS)

Bartoszek, Edward J. (Inventor); Christofas, Alkis (Inventor)

1978-01-01

A water-based coating composition which may be air dried to form durable, fire resistant coatings includes dispersed vinylidene fluoride polymer particles, emulsified liquid epoxy resin and a dissolved emulsifying agent for said epoxy resin which agent is also capable of rapidly curing the epoxy resin upon removal of the water from the composition.

Effect of in-office bleaching agents on physical properties of dental composite resins.

PubMed

Mourouzis, Petros; Koulaouzidou, Elisabeth A; Helvatjoglu-Antoniades, Maria

2013-04-01

The physical properties of dental restorative materials have a crucial effect on the longevity of restorations and moreover on the esthetic demands of patients, but they may be compromised by bleaching treatments. The purpose of this study was to evaluate the effects of in-office bleaching agents on the physical properties of three composite resin restorative materials. The bleaching agents used were hydrogen peroxide and carbamide peroxide at high concentrations. Specimens of each material were prepared, cured, and polished. Measurements of color difference, microhardness, and surface roughness were recorded before and after bleaching and data were examined statistically by analysis of variance (ANOVA) and Tukey HSD post-hoc test at P < .05. The measurements showed that hue and chroma of silorane-based composite resin altered after the bleaching procedure (P < .05). No statistically significant differences were found when testing the microhardness and surface roughness of composite resins tested (P > .05). The silorane-based composite resin tested showed some color alteration after bleaching procedures. The bleaching procedure did not alter the microhardness and the surface roughness of all composite resins tested.

Correlations of norbornenyl crosslinked polyimide resin structures with resin thermo-oxidative stability, resin glass transition temperature and composite initial mechanical properties

NASA Technical Reports Server (NTRS)

Alston, William B.

1988-01-01

PMR (polymerization of monomeric reactants) methodology was used to prepare 70 different polyimide oligomeric resins and 30 different unidirectional graphite fiber/polyimide composites. Monomeric composition as well as chain length between sites of crosslinks were varied to examine their effects on resin thermo-oxidative stability and glass transition temperature (Tg) of the cured/postcured resins. A linear correlation of decreasing 316 C resin weight loss/surface area versus (1) decreasing aliphatic content, or (2) increasing benzylic/aliphatic content stoichiometry ratio over a wide range of resin compositions was observed. An almost linear correlation of Tg versus molecular distance between the crosslinks was also observed. An attempt was made to correlate Tg with initial composite mechanical properties (flexural strength and interlaminar shear strength). However, the scatter in mechanical strength data prevented obtaining a clear correlation. Instead, only a range of composite mechanical properties was obtained at 25, 288, and 316 C. Perhaps more importantly, what did become apparent during the correlation study was (1) the PMR methodology could be used to prepare composites from resins containing a wide variety of monomer modifications, (2) that these composites almost invariably provided satisfactory initial mechanical properties as long as the resins formulated exhibited satisfactory processing flow, and (3) that PMR resins exhibited predictable rates of 316 C weight loss/surface area based on their benzylic/aliphatic stoichiometery ratio.

"Greener" hybrid adhesives composed of urea formaldehyde resin and cottonseed meal for wood based composites

USDA-ARS?s Scientific Manuscript database

Urea formaldehyde (UF) resins are one of the most widely used adhesives in wood based composites. The major concerns of the resin utilization are free formaldehyde release and poor water resistance. As a renewable raw materials, water washed conttonseed meal can be used in wood bonding. To produce “...

Hybridized polymer matrix composite

NASA Technical Reports Server (NTRS)

Stern, B. A.; Visser, T.

1981-01-01

Under certain conditions of combined fire and impact, graphite fibers are released to the atmosphere by graphite fiber composites. The retention of graphite fibers in these situations is investigated. Hybrid combinations of graphite tape and cloth, glass cloth, and resin additives are studied with resin systems. Polyimide resins form the most resistant composites and resins based on simple novolac epoxies the least resistant of those tested. Great improvement in the containment of the fibers is obtained in using graphite/glass hybrids, and nearly complete prevention of individual fiber release is made possible by the use of resin additives.

Analytical methods for the measurement of polymerization kinetics and stresses of dental resin-based composites: A review

PubMed Central

Ghavami-Lahiji, Mehrsima; Hooshmand, Tabassom

2017-01-01

Resin-based composites are commonly used restorative materials in dentistry. Such tooth-colored restorations can adhere to the dental tissues. One drawback is that the polymerization shrinkage and induced stresses during the curing procedure is an inherent property of resin composite materials that might impair their performance. This review focuses on the significant developments of laboratory tools in the measurement of polymerization shrinkage and stresses of dental resin-based materials during polymerization. An electronic search of publications from January 1977 to July 2016 was made using ScienceDirect, PubMed, Medline, and Google Scholar databases. The search included only English-language articles. Only studies that performed laboratory methods to evaluate the amount of the polymerization shrinkage and/or stresses of dental resin-based materials during polymerization were selected. The results indicated that various techniques have been introduced with different mechanical/physical bases. Besides, there are factors that may contribute the differences between the various methods in measuring the amount of shrinkages and stresses of resin composites. The search for an ideal and standard apparatus for measuring shrinkage stress and volumetric polymerization shrinkage of resin-based materials in dentistry is still required. Researchers and clinicians must be aware of differences between analytical methods to make proper interpretation and indications of each technique relevant to a clinical situation. PMID:28928776

Composite resins in the 21st century.

PubMed

Willems, G; Lambrechts, P; Braem, M; Vanherle, G

1993-09-01

Human enamel and dentin should be used as the physiologic standards with which to compare composite resins, especially in the posterior region. The intrinsic surface roughness of composite resins must be equal to or lower than the surface roughness of human enamel on enamel-to-enamel occlusal contact areas (Ra = 0.64 microns). Roughness determines the biologic strength of composite resins. The nanoindentation hardness value of the filler particles (2.91 to 8.84 GPa) must not be higher than that of the hydroxyapatite crystals of human enamel (3.39 GPa). Composite resins intended for posterior use should have a Young's modulus at least equal to, and preferably higher than, that of dentin (18.500 MPa). The compressive strength of enamel (384 MPa) and dentin (297 MPa) and the fracture strength of a natural tooth (molar = 305 MPa; premolar = 248 MPa) offer excellent mechanical standards to select the optimal strength for posterior composite resins. The in vivo occlusal contact area wear rate of composite resins must be comparable to the attritional enamel wear rate (about 39 microns/y) in molars. Differential wear between enamel and composite resin on the same tooth is a new criterion for visualizing and quantifying the wear resistance of composite resins in a biologic way. Posterior resins must have a radiographic opacity that is slightly in excess of that of human enamel (198% Al). Based on these standard criteria, it can be concluded that in the 21st century the ultrafine compact-filled composite resins may be the materials of choice for restoring posterior cavities.

Reducing composite restoration polymerization shrinkage stress through resin modified glass-ionomer based adhesives.

PubMed

Naoum, S J; Mutzelburg, P R; Shumack, T G; Thode, Djg; Martin, F E; Ellakwa, A E

2015-12-01

The aim of this study was to determine whether employing resin modified glass-ionomer based adhesives can reduce polymerization contraction stress generated at the interface of restorative composite adhesive systems. Five resin based adhesives (G Bond, Optibond-All-in-One, Optibond-Solo, Optibond-XTR and Scotchbond-Universal) and two resin modified glass-ionomer based adhesives (Riva Bond-LC, Fuji Bond-LC) were analysed. Each adhesive was applied to bond restorative composite Filtek-Z250 to opposing acrylic rods secured within a universal testing machine. Stress developed at the interface of each adhesive-restorative composite system (n = 5) was calculated at 5-minute intervals over 6 hours. The resin based adhesive-restorative composite systems (RBA-RCS) demonstrated similar interface stress profiles over 6 hours; initial rapid contraction stress development (0-300 seconds) followed by continued contraction stress development ≤0.02MPa/s (300 seconds - 6 hours). The interface stress profile of the resin modified glass-ionomer based adhesive-restorative composite systems (RMGIBA-RCS) differed substantially to the RBA-RCS in several ways. Firstly, during 0-300 seconds the rate of contraction stress development at the interface of the RMGIBA-RCS was significantly (p < 0.05) lower than at the interface of the RBA-RCS. Secondly, at 300 seconds and 6 hours the interface contraction stress magnitude of the RMGIBA-RCS was significantly (p < 0.05) lower than the stress of all assessed RBA-RCS. Thirdly, from 300 seconds to 6 hours both the magnitude and rate of interface stress of the RMGIBA-RCS continued to decline over the 6 hours from the 300 seconds peak. The use of resin modified glass-ionomer based adhesives can significantly reduce the magnitude and rate of polymerization contraction stress developed at the interface of adhesive-restorative composite systems. © 2015 Australian Dental Association.

Prosthetic limb sockets from plant-based composite materials.

PubMed

Campbell, Andrew I; Sexton, Sandra; Schaschke, Carl J; Kinsman, Harry; McLaughlin, Brian; Boyle, Martin

2012-06-01

There is a considerable demand for lower limb prostheses globally due to vascular disease, war, conflict, land mines and natural disasters. Conventional composite materials used for prosthetic limb sockets include acrylic resins, glass and carbon fibres, which produce harmful gasses and dust in their manufacture. To investigate the feasibility of using a renewable plant oil-based polycarbonate-polyurethane copolymer resin and plant fibre composite, instead of conventional materials, to improve safety and accessibility of prosthetic limb manufacture. Experimental, bench research. Test pieces of the resin with a range of plant fibres (10.0% by volume) were prepared and tensile strengths were tested. Test sockets of both conventional composite materials and plant resin with plant fibres were constructed and tested to destruction. Combinations of plant resin and either banana or ramie fibres gave high tensile strengths. The conventional composite material socket and plant resin with ramie composite socket failed at a similar loading, exceeding the ISO 10328 standard. Both wall thickness and fibre-matrix adhesion played a significant role in socket strength. From this limited study we conclude that the plant resin and ramie fibre composite socket has the potential to replace the standard layup. Further mechanical and biocompatibility testing as well as a full economic analysis is required. Using readily sourced and renewable natural fibres and a low-volatile bio-resin has potential to reduce harm to those involved in the manufacture of artificial limb sockets, without compromising socket strength and benefitting clinicians working in poorer countries where safety equipment is scarce. Such composite materials will reduce environmental impact.

Polyimides Based on Asymmetric Dianhydrides (II) (a-BPDA vs a-BTDA) for Resin Transfer Molding (RTM)

NASA Technical Reports Server (NTRS)

Chuang, Kathy C.; Criss, Jim M.; Mintz, Eric A.

2010-01-01

A new series of low-melt viscosity imide resins (10-20 poise at 280 C) were formulated from asymmetric 2,3,3',4' -benzophenone dianhydride (a-BTDA) and 4-phenylethynylphthalic endcaps, along with 3,4' -oxydianiline, 3,3' -methylenedianiline and 3,3'- diaminobenzophenone, using a solvent-free melt process. a-BTDA RTM resins exhibited higher glass transition temperatures (Tg's = 330-400 C) compared to those prepared by asymmetric 2,3,3',4' -biphenyl dianhydride, (a-BPDA, Tg's = 320-370 C). These low-melt viscosity imide resins were fabricated into polyimide/T650-35 carbon fiber composites by a RTM process. Composites properties of a-BTDA resins, such as open-hole compression and short-beam shear strength, are compared to those of composites made from a-BPDA based resin at room temperature, 288 C and 315 C. These novel, high temperature RTM imide resins exhibit outstanding properties beyond the performance of conventional RTM resins, such as epoxy and BMI resins which have use-temperatures around 177 C and 232 C for aerospace applications.

Bisphenol A Release: Survey of the Composition of Dental Composite Resins

PubMed Central

Dursun, Elisabeth; Fron-Chabouis, Hélène; Attal, Jean-Pierre; Raskin, Anne

2016-01-01

Background: Bisphenol A (BPA) is an endocrine disruptor with potential toxicity. Composite resins may not contain pure BPA, but its derivatives are widely used. Several studies found doses of BPA or its derivatives in saliva or urine of patients after composite resin placement. Objective: The aims of this study were to establish an exhaustive list of composite resins marketed in Europe and their composition, and to assess the extent of BPA derivatives used. Methods: A research on manufacturers' websites was performed to reference all composite resins marketed in Europe, then their composition was determined from both material safety data sheets and a standardized questionnaire sent to manufacturers. Manufacturers had to indicate whether their product contained the monomers listed, add other monomers if necessary, or indicate “not disclosed”. Results: 160 composite resins were identified from 31 manufacturers and 23 manufacturers (74.2%) responded to the survey. From the survey and websites, the composition of 130 composite resins (81.2%) was: 112 (86.2%) based on BPA derivatives, 97 (74.7%) on bis-GMA, 17 (13.1%) without monomer derived from BPA (UDMA, sometimes with TEGDMA) and 6 (4.6%) with UDMA (only); 1 (0.8%) did not contain a BPA derivative or UDMA or TEGDMA. Pure BPA was never reported. Conclusion: This work has established a list of 18 composite resins that contain no BPA derivative. Manufacturers should be required to report the exact composition of their products as it often remains unclear or incomplete. PMID:27708726

Bisphenol A Release: Survey of the Composition of Dental Composite Resins.

PubMed

Dursun, Elisabeth; Fron-Chabouis, Hélène; Attal, Jean-Pierre; Raskin, Anne

2016-01-01

Bisphenol A (BPA) is an endocrine disruptor with potential toxicity. Composite resins may not contain pure BPA, but its derivatives are widely used. Several studies found doses of BPA or its derivatives in saliva or urine of patients after composite resin placement. The aims of this study were to establish an exhaustive list of composite resins marketed in Europe and their composition, and to assess the extent of BPA derivatives used. A research on manufacturers' websites was performed to reference all composite resins marketed in Europe, then their composition was determined from both material safety data sheets and a standardized questionnaire sent to manufacturers. Manufacturers had to indicate whether their product contained the monomers listed, add other monomers if necessary, or indicate "not disclosed". 160 composite resins were identified from 31 manufacturers and 23 manufacturers (74.2%) responded to the survey. From the survey and websites, the composition of 130 composite resins (81.2%) was: 112 (86.2%) based on BPA derivatives, 97 (74.7%) on bis-GMA, 17 (13.1%) without monomer derived from BPA (UDMA, sometimes with TEGDMA) and 6 (4.6%) with UDMA (only); 1 (0.8%) did not contain a BPA derivative or UDMA or TEGDMA. Pure BPA was never reported. This work has established a list of 18 composite resins that contain no BPA derivative. Manufacturers should be required to report the exact composition of their products as it often remains unclear or incomplete.

Effect of ceramic thickness and composite bases on stress distribution of inlays--a finite element analysis.

PubMed

Durand, Letícia Brandão; Guimarães, Jackeline Coutinho; Monteiro Junior, Sylvio; Baratieri, Luiz Narciso

2015-01-01

The purpose of this study was to determine the effect of cavity depth, ceramic thickness, and resin bases with different elastic modulus on von Mises stress patterns of ceramic inlays. Tridimensional geometric models were developed with SolidWorks image software. The differences between the models were: depth of pulpal wall, ceramic thickness, and presence of composite bases with different thickness and elastic modulus. The geometric models were constrained at the proximal surfaces and base of maxillary bone. A load of 100 N was applied. The stress distribution pattern was analyzed with von Mises stress diagrams. The maximum von Mises stress values ranged from 176 MPa to 263 MPa and varied among the 3D-models. The highest von Mises stress value was found on models with 1-mm-thick composite resin base and 1-mm-thick ceramic inlay. Intermediate values (249-250 MPa) occurred on models with 2-mm-thick composite resin base and 1-mm-thick ceramic inlay and 1-mm-thick composite resin base and 2-mm-thick ceramic inlay. The lowest values were observed on models restored exclusively with ceramic inlay (176 MPa to 182 MPa). It was found that thicker inlays distribute stress more favorably and bases with low elastic modulus increase stress concentrations on the internal surface of the ceramic inlay. The increase of ceramic thickness tends to present more favorable stress distribution, especially when bonded directly onto the cavity without the use of supporting materials. When the use of a composite base is required, composite resin with high elastic modulus and reduced thickness should be preferred.

Resin infusion of layered metal/composite hybrid and resulting metal/composite hybrid laminate

NASA Technical Reports Server (NTRS)

Cano, Roberto J. (Inventor); Grimsley, Brian W. (Inventor); Weiser, Erik S. (Inventor); Jensen, Brian J. (Inventor)

2009-01-01

A method of fabricating a metal/composite hybrid laminate is provided. One or more layered arrangements are stacked on a solid base to form a layered structure. Each layered arrangement is defined by a fibrous material and a perforated metal sheet. A resin in its liquid state is introduced along a portion of the layered structure while a differential pressure is applied across the laminate structure until the resin permeates the fibrous material of each layered arrangement and fills perforations in each perforated metal sheet. The resin is cured thereby yielding a metal/composite hybrid laminate.

Microshear bond strength of preheated silorane- and methacrylate-based composite resins to dentin.

PubMed

Demirbuga, Sezer; Ucar, Faruk Izzet; Cayabatmaz, Muhammed; Zorba, Yahya Orcun; Cantekin, Kenan; Topçuoğlu, Hüseyin Sinan; Kilinc, Halil Ibrahim

2016-01-01

The aim of this study was to investigate the effect of preheating on microshear bond strength (MSBS) of silorane and methacrylate-based composite resins to human dentin. The teeth were randomly divided into three main groups: (1) composite resins were heated upto 68 °C; (2) cooled to 4 °C; and (3) control [room temperature (RT)]. Each group was then randomly subdivided into four subgroups according to adhesive system used [Solobond M (Voco), All Bond SE (Bisco), Clearfil SE Bond (CSE) (Kuraray), Silorane adhesive system (SAS) (3M ESPE)]. Resin composite cylinders were formed (0.9 mm diameter × 0.7 mm length) and MSBS of each specimen was tested. The preheated groups exhibited the highest MSBS (p < 0.001) and the groups cooled to 4 °C exhibited the lowest MSBS (p < 0.001). The CSE showed higher MSBS than the other adhesives (p < 0.001). This study concludes that preheating of composite resins may be an alternative way to increase the MSBS of composites on dentin. © Wiley Periodicals, Inc.

Future perspectives of resin-based dental materials.

PubMed

Jandt, Klaus D; Sigusch, Bernd W

2009-08-01

This concise review and outlook paper gives a view of selected potential future developments in the area of resin-based biomaterials with an emphasis on dental composites. A selection of key publications (1 book, 35 scientific original publications and 1 website source) covering the areas nanotechnology, antimicrobial materials, stimuli responsive materials, self-repairing materials and materials for tissue engineering with direct or indirect relations and/or implications to resin-based dental materials is critically reviewed and discussed. Connections between these fields and their potential for resin-based dental materials are highlighted and put in perspective. The need to improve shrinkage properties and wear resistance is obvious for dental composites, and a vast number of attempts have been made to accomplish these aims. Future resin-based materials may be further improved in this respect if, for example nanotechnology is applied. Dental composites may, however, reach a completely new quality by utilizing new trends from materials science, such as introducing nanostructures, antimicrobial properties, stimuli responsive capabilities, the ability to promote tissue regeneration or repair of dental tissues if the composites were able to repair themselves. This paper shows selected potential future developments in the area of resin-based dental materials, gives basic and industrial researchers in dental materials science, and dental practitioners a glance into the potential future of these materials, and should stimulate discussion about needs and future developments in the area.

Influence of a peracetic acid-based immersion on indirect composite resin.

PubMed

Samuel, Susana Maria Werner; Fracaro, Gisele Baggio; Collares, Fabrício Mezzomo; Leitune, Vicente Castelo Branco; Campregher, Ulisses Bastos

2011-06-01

The aim of this study was to evaluate the influence of immersion in a 0.2% peracetic acid-based disinfectant on the three-point flexural strength, water sorption and water solubility of an indirect composite resin. Specimens were produced according to ISO 4049:2000 specifications and were divided in two groups: Control group, with no disinfection and Disinfected group, with three 10 min immersions in the peracetic acid intercalated with 10 min immersions in sterile distilled water. All evaluations were conducted in compliance with ISO specifications. Three-point flexural strength, water sorption and solubility of indirect composite resin before and after immersion showed no statistical significant differences (p > 0.05) and met ISO standard requirements. Immersion in peracetic acid solution showed no influence in indirect composite resin tested properties.

Maleimido substituted cyclotriphosphazene resins for fire and heat resistant composites

NASA Technical Reports Server (NTRS)

Kumar, D.; Fohlen, G. M.; Parker, J. A.

1983-01-01

A new class of fire- and heat-resistant matrix resins have been synthesized by the thermal polymerization of maleimido substituted phenoxycyclotriphosphazenes. The resins have exhibited a char yield of 82 percent at 800 C in nitrogen and 81 percent at 700 C in air. Graphite-fabric laminates based on a resin of this class have shown a limiting oxygen index of 100 percent even at 300 C. Details of the fabrication of the resins and the composites and testing procedures are discussed.

Mesoporous silica fillers and resin composition effect on dental composites cytocompatibility.

PubMed

Attik, Nina; Hallay, Franck; Bois, Laurence; Brioude, Arnaud; Grosgogeat, Brigitte; Colon, Pierre

2017-02-01

Many new dental composites containing mesoporous silica fillers have been developed to improve rheological properties and enhance the resin-filler interface. To investigate the correlation between the cytocompatibility of several dental composites and their composition; two aspects have been considered: presence of bisphenol A (BPA)-glycidyl methacrylate (Bis-GMA) or triethyleneglycol-dimethacrylate (TEGDMA) among the resin monomers and presence of porous particles among the filler blends. Five commercial composites with different resin matrices and mineral fillers were compared to four experimental composites designed without any BPA-based monomers or TEGDMA. Porous fillers, with or without silanation, were added in some of the experimental composites. Two reference resin matrices were also selected. Cytocompatibility with cultured primary human gingival fibroblasts was assessed by confocal laser scanning microscopy with time-lapse imaging. Fourier transform infrared spectroscopy was used to control monomer conversion rate. Conversion rates of the experimental composites ranged from 57% to 71%, a comparable ratio for dental composites. Experimental samples were better tolerated than tested commercial samples not containing TEGDMA and significantly better than those containing TEGDMA. Experimental composites with porous fillers exhibited good cytocompatibility, especially when surfaces were silanated. Cytotoxicity was associated with resin amount and especially resin nature. Composites containing porous fillers might behave as if the resin trapped into pores has no effect on toxicity. The cytotoxicity of composites with and without BPA derivatives was mainly attributed to the release of residual TEGDMA rather than the BPA derivatives. Copyright © 2016 The Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Influence of Sea Water Aging on the Mechanical Behaviour of Acrylic Matrix Composites

NASA Astrophysics Data System (ADS)

Davies, P.; Le Gac, P.-Y.; Le Gall, M.

2017-02-01

A new matrix resin was recently introduced for composite materials, based on acrylic resin chemistry allowing standard room temperature infusion techniques to be used to produce recyclable thermoplastic composites. This is a significant advance, particularly for more environmentally-friendly production of large marine structures such as boats. However, for such applications it is essential to demonstrate that composites produced with these resins resist sea water exposure in service. This paper presents results from a wet aging study of unreinforced acrylic and glass and carbon fibre reinforced acrylic composites. It is shown that the acrylic matrix resin is very stable in seawater, showing lower property losses after seawater aging than those of a commonly-used epoxy matrix resin. Carbon fibre reinforced acrylic also shows good property retention after aging, while reductions in glass fibre reinforced composite strengths suggest that specific glass fibre sizing may be required for optimum durability.

Fiber Reinforced Polyester Resins Polymerized by Microwave Source

NASA Astrophysics Data System (ADS)

Visco, A. M.; Calabrese, L.; Cianciafara, P.; Bonaccorsi, L.; Proverbio, E.

2007-12-01

Polyester resin based composite materials are widely used in the manufacture of fiberglass boats. Production time of fiberglass laminate components could be strongly reduced by using an intense energy source as well as microwaves. In this work a polyester resin was used with 2% by weight of catalyst and reinforced with chopped or woven glass fabric. Pure resin and composite samples were cured by microwaves exposition for different radiation times. A three point bending test was performed on all the cured samples by using an universal testing machine and the resulting fracture surfaces were observed by means of scanning electron microscopy (SEM). The results of mechanical and microscopy analyses evidenced that microwave activation lowers curing time of the composite while good mechanical properties were retained. Microwaves exposition time is crucial for mechanical performance of the composite. It was evidenced that short exposition times suffice for resin activation while long exposure times cause fast cross linking and premature matrix fracture. Furthermore high-radiation times induce bubbles growth or defects nucleation within the sample, decreasing composite performance. On the basis of such results microwave curing activation of polyester resin based composites could be proposed as a valid alternative method for faster processing of laminated materials employed for large-scale applications.

Comparison of time-dependent changes in the surface hardness of different composite resins

PubMed Central

Ozcan, Suat; Yikilgan, Ihsan; Uctasli, Mine Betul; Bala, Oya; Kurklu, Zeliha Gonca Bek

2013-01-01

Objective: The aim of this study was to evaluate the change in surface hardness of silorane-based composite resin (Filtek Silorane) in time and compare the results with the surface hardness of two methacrylate-based resins (Filtek Supreme and Majesty Posterior). Materials and Methods: From each composite material, 18 wheel-shaped samples (5-mm diameter and 2-mm depth) were prepared. Top and bottom surface hardness of these samples was measured using a Vicker's hardness tester. The samples were then stored at 37°C and 100% humidity. After 24 h and 7, 30 and 90 days, the top and bottom surface hardness of the samples was measured. In each measurement, the rate between the hardness of the top and bottom surfaces were recorded as the hardness rate. Statistical analysis was performed by one-way analysis of variance, multiple comparisons by Tukey's test and binary comparisons by t-test with a significance level of P = 0.05. Results: The highest hardness values were obtained from each two surfaces of Majesty Posterior and the lowest from Filtek Silorane. Both the top and bottom surface hardness of the methacrylate based composite resins was high and there was a statistically significant difference between the top and bottom hardness values of only the silorane-based composite, Filtek Silorane (P < 0.05). The lowest was obtained with Filtek Silorane. The hardness values of all test groups increased after 24 h (P < 0.05). Conclusion: Although silorane-based composite resin Filtek Silorane showed adequate hardness ratio, the use of incremental technic during application is more important than methacrylate based composites. PMID:24966724

Nontoxic Resins Advance Aerospace Manufacturing

NASA Technical Reports Server (NTRS)

2009-01-01

The 2008 NASA Commercial Invention of the Year, PETI-330, is a polyimide matrix resin that performs well at high temperatures and is easily processed into composites in a simple, short curing cycle. Invented by scientists at Langley Research Center, PETI-330 is now licensed to Ube Industries, based in Japan with its American headquarters in New York. In addition to being durable and lightweight, the resin is also nontoxic, which makes it safe for workers to handle. PETI-330 was created specifically for heat-resistant composites formed with resin transfer molding and resin infusion, which formerly could only be used with low temperature resin systems.

Cytotoxic evaluation of hydroxyapatite-filled and silica/hydroxyapatite-filled acrylate-based restorative composite resins: An in vitro study.

PubMed

Chadda, Harshita; Naveen, Sangeetha Vasudevaraj; Mohan, Saktiswaren; Satapathy, Bhabani K; Ray, Alok R; Kamarul, Tunku

2016-07-01

Although the physical and mechanical properties of hydroxyapatite-filled dental restorative composite resins have been examined, the biocompatibility of these materials has not been studied in detail. The purpose of this in vitro study was to analyze the toxicity of acrylate-based restorative composite resins filled with hydroxyapatite and a silica/hydroxyapatite combination. Five different restorative materials based on bisphenol A-glycidyl methacrylate (bis-GMA) and tri-ethylene glycol dimethacrylate (TEGDMA) were developed: unfilled (H0), hydroxyapatite-filled (H30, H50), and silica/hydroxyapatite-filled (SH30, SH50) composite resins. These were tested for in vitro cytotoxicity by using human bone marrow mesenchymal stromal cells. Surface morphology, elemental composition, and functional groups were determined by scanning electron microscopy (SEM), energy-dispersive x-ray spectroscopy (EDX), and Fourier-transformed infrared spectroscopy (FTIR). The spectra normalization, baseline corrections, and peak integration were carried out by OPUS v4.0 software. Both in vitro cytotoxicity results and SEM analysis indicated that the composite resins developed were nontoxic and supported cell adherence. Elemental analysis with EDX revealed the presence of carbon, oxygen, calcium, silicon, and gold, while the presence of methacrylate, hydroxyl, and methylene functional groups was confirmed through FTIR analysis. The characterization and compatibility studies showed that these hydroxyapatite-filled and silica/hydroxyapatite-filled bis-GMA/TEGDMA-based restorative composite resins are nontoxic to human bone marrow mesenchymal stromal cells and show a favorable biologic response, making them potential biomaterials. Copyright © 2016 Editorial Council for the Journal of Prosthetic Dentistry. Published by Elsevier Inc. All rights reserved.

Polymerization shrinkage of different types of composite resins and microleakage with and without liner in class II cavities.

PubMed

Karaman, E; Ozgunaltay, G

2014-01-01

To determine the volumetric polymerization shrinkage of four different types of composite resin and to evaluate microleakage of these materials in class II (MOD) cavities with and without a resin-modified glass ionomer cement (RMGIC) liner, in vitro. One hundred twenty-eight extracted human upper premolar teeth were used. After the teeth were divided into eight groups (n=16), standardized MOD cavities were prepared. Then the teeth were restored with different resin composites (Filtek Supreme XT, Filtek P 60, Filtek Silorane, Filtek Z 250) with and without a RMGIC liner (Vitrebond). The restorations were finished and polished after 24 hours. Following thermocycling, the teeth were immersed in 0.5% basic fuchsin for 24 hours, then midsagitally sectioned in a mesiodistal plane and examined for microleakage using a stereomicroscope. The volumetric polymerization shrinkage of materials was measured using a video imaging device (Acuvol, Bisco, Inc). Data were statistically analyzed with Kruskal-Wallis and Mann-Whitney U-tests. All teeth showed microleakage, but placement of RMGIC liner reduced microleakage. No statistically significant differences were found in microleakage between the teeth restored without RMGIC liner (p>0.05). Filtek Silorane showed significantly less volumetric polymerization shrinkage than the methacrylate-based composite resins (p<0.05). The use of RMGIC liner with both silorane- and methacrylate-based composite resin restorations resulted in reduced microleakage. The volumetric polymerization shrinkage was least with the silorane-based composite.

Diametral and compressive strength of dental core materials.

PubMed

Cho, G C; Kaneko, L M; Donovan, T E; White, S N

1999-09-01

Strength greatly influences the selection of core materials. Many disparate material types are now recommended for use as cores. Cores must withstand forces due to mastication and parafunction for many years. This study compared the compressive and diametral tensile strengths of 8 core materials of various material classes and formulations (light-cured hybrid composite, autocured titanium containing composite, amalgam, glass ionomer, glass ionomer cermet, resin-modified glass ionomer, and polyurethane). Materials were manipulated according to manufacturers' instructions for use as cores. Mean compressive and diametral strengths with associated standard errors were calculated for each material (n = 10). Analyses of variance were computed (P <.0001) and multiple comparisons tests discerned many differences among materials. Compressive strengths varied widely from 61.1 MPa for a polyurethane to 250 MPa for a resin composite. Diametral tensile strengths ranged widely from 18.3 MPa for a glass ionomer cermet to 55.1 MPa for a resin composite. Some resin composites had compressive and tensile strengths equal to those of amalgam. Light-cured hybrid resin composites were stronger than autocured titanium containing composites. The strengths of glass ionomer-based materials and of a polyurethane material were considerably lower than for resin composites or amalgam.

Molecular composition and paleobotanical origin of Eocene resin from northeast India

NASA Astrophysics Data System (ADS)

Rudra, Arka; Dutta, Suryendu; Raju, Srinivasan V.

2014-06-01

The molecular composition of fossil resins from early to middle Eocene coal from northeast India, has been analyzed for the first time to infer their paleobotanical source. The soluble component of fossil resin was analyzed using gas chromatography-mass spectrometry (GC-MS). The resin extracts are composed of cadalene-based C15 sesquiterpenoids and diagenetically altered triterpenoids. The macromolecular composition was investigated using pyrolysis gas chromatography-mass spectrometry (Py-GC-MS) and Fourier transform infrared (FTIR) spectroscopy. The major pyrolysis products are C15 bicyclic sesquiterpenoids, alkylated naphthalenes, benzenes and a series of C17-C34 n-alkene- n-alkane pairs. Spectroscopic analysis revealed the dominance of aliphatic components. The presence of cadalene-based sequiterpenoids confirms the resin to be Class II or dammar resin, derived from angiosperms of Dipterocarpaceae family. These sesquiterpenoids are often detected in many SE Asian fluvio-deltaic oils. Dipterocarpaceae are characteristic of warm tropical climate suggesting the prevalence of such climate during early Eocene in northeast India.

Polyimide Composites Properties of RTM370 Fabricated by Vacuum Assisted Resins Transfer Molding (VARTM)

NASA Technical Reports Server (NTRS)

Chuang, Kathy C.; Criss, Jim M.; Mintz, Eric A.

2011-01-01

RTM370 imide resin based on 2,3,3 ,4 -biphenyl dianhydride ( a-BPDA), 3,4 -oxydianinline (3,4 -ODA) with 4-phenylethynylphthalic (PEPA) endcap has shown to exhibit high Tg (370 C) and low melt viscosity (10-30 poise) at 280 C with a pot-life of 1-2 h. Previously, RTM370 resin has been fabricated into composites with T650-35 carbon fabrics by resin transfer molding (RTM) successfully. RTM370 composites exhibit excellent mechanical properties up to 327 C (620 F), and outstanding property retention after aging at 288 C (550 F) for 1000 hrs. In this presentation, RTM 370 composites will be fabricated by vacuum assisted resins transfer molding (VARTM), using vacuum bags without mold. The mechanical properties of RTM370 composites fabricated by VARTM will be compared to those of RTM370 made by RTM.

Composite Properties of RTM370 Polyimide Fabricated by Vacuum Assisted Resin Transfer Molding (VARTM)

NASA Technical Reports Server (NTRS)

Chuang, Kathy C.; Criss, James M.; Mintz, Eric A.; Shonkwiler, Brian; McCorkle, Linda S.

2011-01-01

RTM370 imide resin based on 2,3,3?,4?-biphenyl dianhydride (a-BPDA), 3,4'-oxydianinline (3,4'-ODA) with the 4-phenylethynylphthalic (PEPA) endcap has been shown to exhibit a high cured T(sub g) (370 C) and low melt viscosity (10-30 poise) at 280 C with a pot-life of 1-2 h. Previously, RTM370 resin has been successfully fabricated into composites reinforced with T650-35 carbon fabrics by resin transfer molding (RTM). RTM370 composites exhibit excellent mechanical properties up to 327?C (620?F), and outstanding property retention after aging at 288?C (550?F) for 1000 h. In this work, RTM370 composites were fabricated by vacuum assisted resin transfer molding (VARTM), using vacuum bags on a steel plate. The mechanical properties of RTM370 composites fabricated by VARTM are compared to those prepared by RTM.

Thermosetting epoxy resin/thermoplastic system with combined shape memory and self-healing properties

NASA Astrophysics Data System (ADS)

Yao, Yongtao; Wang, Jingjie; Lu, Haibao; Xu, Ben; Fu, Yongqing; Liu, Yanju; Leng, Jinsong

2016-01-01

A novel and facile strategy was proposed to construct a thermosetting/thermoplastic system with both shape memory and self-healing properties based on commercial epoxy resin and poly(ɛ-caprolactone)-PCL. Thermoplastic material is capable of re-structuring and changing the stiffness/modulus when the temperature is above melting temperature. PCL microfiber was used as a plasticizer in epoxy resin-based blends, and served as a ‘hard segment’ to fix a temporary shape of the composites during shape memory cycles. In this study, the electrospun PCL membrane with a porous network structure enabled a homogenous PCL fibrous distribution and optimized interaction between fiber and epoxy resin. The self-healing capability is achieved by phase transition during curing of the composites. The mechanism of the shape memory effect of the thermosetting (rubber)/thermoplastic composite is attributed to the structural design of the thermoplastic network inside the thermosetting resin/rubber matrix.

Towards reinforcement solutions for urban fibre/fabric waste using bio-based biodegradable resins.

NASA Astrophysics Data System (ADS)

Agrawal, Pramod; Hermes, Alina; Bapeer, Solaf; Luiken, Anton; Bouwhuis, Gerrit; Brinks, Ger

2017-10-01

The main research question is how to systematically define and characterize urban textile waste and how to effectively utilise it to produce reinforcement(s) with selected bio-based biodegradable resin(s). Several composite samples have been produced utilising predominantly natural and predominantly synthetic fibres by combining loose fibres with PLA, nonwoven fabric with PLA, woven fabric with PLA, two-layer composite & four-layer composite samples. Physio-chemical characterisations according to the established standards have been conducted. The present work is a step toward the circular economy and closing the loop in textile value chain.

Clinical assessment of class II resin-based composites versus preformed metal crowns performed on primary molars in patients at high risk of caries.

PubMed

Alyahya, A; Khanum, A; Qudeimat, M

2018-02-01

To compare class II resin composite with preformed metal crowns (PMC) in the treatment of proximal dentinal caries in high caries-risk patients. The charts (270) of paediatric patients with proximal caries of their primary molars were reviewed. Success or failure of a procedure was assessed using the dental notes. Survival analysis was used to calculate the mean survival time (MST) for both procedures. The influence of variables on the mean survival time was investigated. A total of 593 class II resin composites and 243 PMCs were placed in patients ranging between 4-13 years of age. The failure percentage of class II resin composites was 22.6% with the majority having been due to recurrent caries, while the failure percentage of PMCs was 15.2% with the majority due to loss of the crown. There was no significant difference between the MST of class II resin composites and PMCs, 41.3 and 45.6 months respectively (p value = 0.06). In class II resin composites, mesial restorations were associated with lower MST compared to distal restorations (p-value < 0.001). The MST of resin composites and PMCs were comparable when performed on high caries-risk patients.

The Effect of Titanium Tetrafluoride and Sodium Hypochlorite on the Shear Bond Strength of Methacrylate and Silorane Based Composite Resins: an In-Vitro Study.

PubMed

Sharafeddin, Farahnaz; Koohpeima, Fatemeh; Razazan, Nader

2017-06-01

The bond strength of composites with different adhesive systems with dentin is an important factor in long term durability of composite restorations. The effect of titanium tetrafluoride (TiF 4 ) as anti caries agent and sodium hypochlorite (NaOCl) as disinfectant on the shear bond of nanofilled and silorane based composite resins have not been investigated in previous studies. This study was conducted to determine bond strength between dentin and two composite systems, by means of shear bond test using TiF 4 and NaOCl. Middle dentin of 60 intact extracted maxillary premolar teeth were exposed by sectioning the crowns at a depth of 2mm from central groove and parallel to the occlusal surface. Standardized smear layer was created using a 600-grit silicon carbide paper and then samples were embedded in acrylic resin blocks. Then the samples were randomly divided into 6 \\groups summarized as Group I: Z350, Group II: Z350+ NaOCl, Group III: Z350+ TiF 4 , Group IV: P90, Group V: P90+ NaOCl, Group VI: P90+ TiF 4 according to manufacturer's instruction. Then samples were subjected to shear bond strength (SBS) test using universal testing machine and data were analyzed using ANOVA and Tukey tests ( p < 0.05). Application of 5% NaOCl caused a significant decrease in SBS of nanofilled composite resin ( p = 0.004), and also silorane based composite resin ( p = 0.006). Application of 4% TiF 4 caused a significant increase in SBS of silorane based composite resin ( p = 0.001). The effect of TiF 4 on nanofilled composite was not statistically significant. Using TiF 4 has a positive effect on increasing the shear bond while NaOCl has negative effect on bond strength.

Polyimide Composites Based on Asymmetric Dianhydrides (a-ODPA vs a-BPDA)

NASA Technical Reports Server (NTRS)

Chuang, Kathy C.; Criss, James M.; Mintz, Eric A.

2009-01-01

RTM Resins based on a-ODPA and a-BPDA with kinked diamines exhibit low-melt viscosity (approximately 10 poise). Composites made from a-ODPA resins (T(sub g) = 265-330 C) by RTM display good mechanical properties at 288 C (550 F), but soften at 315 C (600 F). Composites of RTM370 based on a-BPDA retain excellent mechanical properties at 315 C, exceeding BMI-5270-1 capability.

Development of dental restorative materials based on visible light-cured multi-methacrylates

NASA Astrophysics Data System (ADS)

Tiba, Amer

The studies described in this dissertation focus on new visible light-curing (VLC) oligomers exhibiting low shrinkage, low water sorption, and improved mechanical properties. A family of multi-methacrylates, based on poly(isopropylidenediphenol) resin (BPA), was synthesized, characterized, and evaluated. The commercial BPA resin is prepared from enzymatic polymerization (oligomerization) of bisphenol A. The BPA resin, having an average of eight phenolic hydroxyl groups per molecule, was treated with propylene carbonate, and the resultant product, i.e., propoxylated BPA (PEBPA) oligomer, was confirmed by Fourier transform infrared spectroscopy (FT-IR) and sp{13}C nuclear magnetic resonance (NMR). The propoxylated BPA was subsequently treated with methacryloyl chloride to produce the multi-methacrylates, identified by FT-IR and NMR. The PEBPA oligomer multimethacrylate: triethylene glycol dimethacrylate (TEGDMA) (50:50/wt:wt) blends were combined with 0.5 wt. % camphoroquinone (CQ) and 1.0 wt. % N,N-dimethylaminoethyl methacrylate (DMAEMA). The control polymers were 2,2-bis(4-(2-hydroxy-3-methacryloyloxypropoxy)phenyl) propane (BisGMA): TEGDMA(50:50/wt:wt) blends having the same levels of CQ/DMAEMA. Differential photocalorimetry (DPC) and differential scanning calorimetry (DSC) showed these multimethacrylate/TEGDMA (neat resin) blends have polymerization characteristics comparable to the BisGMA/TEGDMA controls. These new multifunctional oligomers have lower polymerization shrinkage and lower uptake of water and other liquids, compared to BisGMA based materials. In addition, two experimental oligomers, PEBPA #2 and #3, have higher compressive strength than the BisGMA control. A biocompatibility test of the polymerized multi-methacrylate resins was performed and compared with the conventional BisGMA/TEGDMA resin and blank controls, using cell culture techniques. Human gingival fibroblasts were used for biocompatibility evaluation of these resins. The results revealed that the BPA oligomer (multi-methacrylate) based resin significantly favored the cell growth of the human gingival fibroblasts, compared to the control. An experimental composite was made from EPBPA oligomers (multi-methacrylates). The compressive strength of the experimental EPBPA containing composite was not significantly different than the commercial composite Herculite HXR. SEM photomicrographs revealed more voids in the experimental composites than the commercial composite on both the external surfaces of the prepared specimens and the subsequent fractured surfaces. This is due to the molding technique for specimen preparation and lack of good mechanical mixing for filler incorporation prior to placement of the resin in the mold for subsequent photopolymerization. However, the water sorption for the experimental EPBPA-based composite was significantly lower than the commercial Herculite (HXR) composite. This is most likely related to the hydrophobic nature of the experimental resin. These results suggest that the new type of polyfunctional methacrylate oligomers (PEBPA) have potential application in formulating dental composites as direct esthetic restorative materials with improved properties.

Antibacterial effect of composite resins containing quaternary ammonium polyethyleneimine nanoparticles

NASA Astrophysics Data System (ADS)

Yudovin-Farber, Ira; Beyth, Nurit; Weiss, Ervin I.; Domb, Abraham J.

2010-02-01

Quaternary ammonium polyethyleneimine (QA-PEI)-based nanoparticles were synthesized by crosslinking with dibromopentane followed by N-alkylation with various alkyl halides and further N-methylation with methyl iodide. Insoluble pyridinium-type particles were prepared by suspension polymerization of 4-vinyl pyridine followed by N-alkylation with alkyl halides. Polyamine-based nanoparticles embedded in restorative composite resin at 1% w/w were tested for antibacterial activity against Streptococcus mutans using direct contact test. Activity analysis revealed that the alkyl chain length of the QA-PEI nanoparticles plays a significant role in antibacterial activity of the reagent. The most potent compound was octyl-alkylated QA-PEI embedded in restorative composite resin at 1% w/w that totally inhibited S. mutans growth in 3-month-aged samples. This data indicates that restorative composite resin with antibacterial properties can be produced by the incorporation of QA-PEI nanoparticles.

Filler particle size and composite resin classification systems.

PubMed

Lang, B R; Jaarda, M; Wang, R F

1992-11-01

The currently used composite resin classification systems need review if they are to continue to serve as descriptives and quantitative parameters denoting the filler particle content of these materials. Examination of the particles in 12 composite resins using a technique of washing the filler particles from the matrix of the composite resin was presented as yet another method of grouping composites according to filler particle content. Light microscopic examination of the filler particles that remained provided a separation of the 12 materials into four easily distinguished groups based on filler particle sizes. The wear of the 12 composite resins determined in a previous study was examined in relation to the classification of the materials by the currently available systems. The wear values were also examined using the groupings of the materials according to their filler particle sizes as determined by separating the particles from the matrix by the washing technique. Grouping composites on the basis of the filler particle sizes found after washing was easily correlated with wear and supported the suggestion that composites with smaller filler particles wear less.

Quantitative analysis of enamel on debonded orthodontic brackets.

PubMed

Cochrane, Nathan J; Lo, Thomas W G; Adams, Geoffrey G; Schneider, Paul M

2017-09-01

Iatrogenic damage to the tooth surface in the form of enamel tearouts can occur during removal of fixed orthodontic appliances. The aim of this study was to assess debonded metal and ceramic brackets attached with a variety of bonding materials to determine how frequently this type of damage occurs. Eighty-one patients close to finishing fixed orthodontic treatment were recruited. They had metal brackets bonded with composite resin and a 2-step etch-and-bond technique or ceramic brackets bonded with composite resin and a 2-step etch-and- bond technique, and composite resin with a self-etching primer or resin-modified glass ionomer cement. Debonded brackets were examined by backscattered scanning electron microscopy with energy dispersive x-ray spectroscopy to determine the presence and area of enamel on the base pad. Of the 486 brackets collected, 26.1% exhibited enamel on the bonding material on the bracket base pad. The incidences of enamel tearouts for each group were metal brackets, 13.3%; ceramic brackets, 30.2%; composite resin with self-etching primer, 38.2%; and resin-modified glass ionomer cement, 21.2%. The percentage of the bracket base pad covered in enamel was highly variable, ranging from 0% to 46.1%. Enamel damage regularly occurred during the debonding process with the degree of damage being highly variable. Damage occurred more frequently when ceramic brackets were used (31.9%) compared with metal brackets (13.3%). Removal of ceramic brackets bonded with resin-modified glass ionomer cement resulted in less damage compared with the resin bonding systems. Copyright © 2017 American Association of Orthodontists. Published by Elsevier Inc. All rights reserved.

Processing and Characterization of Peti Composites Fabricated by High Temperature Vartm (Section)

NASA Technical Reports Server (NTRS)

Ghose, Sayata; Cano, Roberto J.; Watson, Kent A.; Britton, Sean M.; Jensen, Brian J.; Connell, John W.; Smith, Joseph G., Jr.; Loos, Alfred C.; Heider, Dirk

2011-01-01

The use of composites as primary structures on aerospace vehicles has increased dramatically over the past decade, but so have the production costs associated with their fabrication. For certain composites, high temperature vacuum assisted resin transfer molding (HT-VARTM) can offer reduced fabrication costs compared to conventional autoclave techniques. The process has been successfully used with phenylethynyl terminated imide (PETI) resins developed by NASA Langley Research Center (LaRC). In the current study, three PETI resins have been used to make test specimens using HT-VARTM. Based on previous work at NASA LaRC, larger panels with a quasi-isotropic lay-up were fabricated. The resultant composite specimens exhibited void contents of 3% by volume depending on the type of carbon fabric preform used. Mechanical properties of the panels were determined at both room and elevated temperatures. Fabric permeability characterizations and limited process modeling efforts were carried out to determine infusion times and composite panel size limitations. In addition, new PETI based resins were synthesized specifically for HT-VARTM.

Non-destructive evaluation of teeth restored with different composite resins using synchrotron based micro-imaging.

PubMed

Fatima, A; Kulkarni, V K; Banda, N R; Agrawal, A K; Singh, B; Sarkar, P S; Tripathi, S; Shripathi, T; Kashyap, Y; Sinha, A

2016-01-01

Application of high resolution synchrotron micro-imaging in microdefects studies of restored dental samples. The purpose of this study was to identify and compare the defects in restorations done by two different resin systems on teeth samples using synchrotron based micro-imaging techniques namely Phase Contrast Imaging (PCI) and micro-computed tomography (MCT). With this aim acquired image quality was also compared with routinely used RVG (Radiovisiograph). Crowns of human teeth samples were fractured mechanically involving only enamel and dentin, without exposure of pulp chamber and were divided into two groups depending on the restorative composite materials used. Group A samples were restored using a submicron Hybrid composite material and Group B samples were restored using a Nano-Hybrid restorative composite material. Synchrotron based PCI and MCT was performed with the aim of visualization of tooth structure, composite resin and their interface. The quantitative and qualitative comparison of phase contrast and absorption contrast images along with MCT on the restored teeth samples shows comparatively large number of voids in Group A samples. Quality assessment of dental restorations using synchrotron based micro-imaging suggests Nano-Hybrid resin restorations (Group B) are better than Group A.

Biocompatibility of composite resins

PubMed Central

Mousavinasab, Sayed Mostafa

2011-01-01

Dental materials that are used in dentistry should be harmless to oral tissues, so they should not contain any leachable toxic and diffusible substances that can cause some side effects. Reports about probable biologic hazards, in relation to dental resins, have increased interest to this topic in dentists. The present paper reviews the articles published about biocompatibility of resin-restorative materials specially resin composites and monomers which are mainly based on Bis-GMA and concerns about their degradation and substances which may be segregated into oral cavity. PMID:23372592

Progress in dimethacrylate-based dental composite technology and curing efficiency.

PubMed

Leprince, Julian G; Palin, William M; Hadis, Mohammed A; Devaux, Jacques; Leloup, Gaetane

2013-02-01

This work aims to review the key factors affecting the polymerization efficiency of light-activated resin-based composites. The different properties and methods used to evaluate polymerization efficiency will also be critically appraised with focus on the developments in dental photopolymer technology and how recent advances have attempted to improve the shortcomings of contemporary resin composites. Apart from the classical literature on the subject, the review focused in particular on papers published since 2009. The literature research was performed in Scopus with the terms "dental resin OR dimethacrylate". The list was screened and all papers relevant to the objectives of this work were included. Though new monomer technologies have been developed and some of them already introduced to the dental market, dimethacrylate-based composites still currently represent the vast majority of commercially available materials for direct restoration. The photopolymerization of resin-based composites has been the subject of numerous publications, which have highlighted the major impact of the setting process on material properties and quality of the final restoration. Many factors affect the polymerization efficiency, be they intrinsic; photoinitiator type and concentration, viscosity (co-monomer composition and ratio, filler content) and optical properties, or extrinsic; light type and spectrum, irradiation parameters (radiant energy, time and irradiance), curing modes, temperature and light guide tip positioning. : This review further highlights the apparent need for a more informative approach by manufacturers to relay appropriate information in order for dentists to optimize material properties of resin composites used in daily practice. Copyright © 2012 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Evaluation of Polymerization Efficacy in Composite Resins via FT-IR Spectroscopy and Vickers Microhardness Test.

PubMed

Jafarzadeh, Tahereh-Sadat; Erfan, Mohammad; Behroozibakhsh, Marjan; Fatemi, Mostafa; Masaeli, Reza; Rezaei, Yashar; Bagheri, Hossein; Erfan, Yasaman

2015-01-01

Background and aims. Polymerization efficacy affects the properties and performance of composite resin restorations.The purpose of this study was to evaluate the effectiveness of polymerization of two micro-hybrid, two nano-hybrid and one nano-filled ormocer-based composite resins, cured by two different light-curing systems, using Fourier transformation infrared (FT-IR) spectroscopy and Vickers microhardness testing at two different depths (top surface, 2 mm). Materials and methods. For FT-IR spectrometry, five cylindrical specimens (5mm in diameter × 2 mm in length) were prepared from each composite resin using Teflon molds and polymerized for 20 seconds. Then, 70-μm wafers were sectioned at the top surface and at2mm from the top surface. The degree of conversion for each sample was calculated using FT-IR spectroscopy. For Vickers micro-hardness testing, three cylindrical specimens were prepared from each composite resin and polymerized for 20 seconds. The Vickers microhardness test (Shimadzu, Type M, Japan) was performed at the top and bottom (depth=2 mm) surfaces of each specimen. Three-way ANOVA with independent variables and Tukey tests were performed at 95% significance level. Results. No significant differences were detected in degree of conversion and microhardness between LED and QTH light-curing units except for the ormocer-based specimen, CeramX, which exhibited significantly higher DC by LED. All the composite resins showed a significantly higher degree of conversion at the surface. Microhardness was not significantly affected by depth, except for Herculite XRV Ultra and CeramX, which showed higher values at the surface. Conclusion. Composite resins containing nano-particles generally exhibited more variations in degree of conversion and microhardness.

Evaluation of Polymerization Efficacy in Composite Resins via FT-IR Spectroscopy and Vickers Microhardness Test

PubMed Central

Jafarzadeh, Tahereh-Sadat; Erfan, Mohammad; Behroozibakhsh, Marjan; Fatemi, Mostafa; Masaeli, Reza; Rezaei, Yashar; Bagheri, Hossein; Erfan, Yasaman

2015-01-01

Background and aims. Polymerization efficacy affects the properties and performance of composite resin restorations.The purpose of this study was to evaluate the effectiveness of polymerization of two micro-hybrid, two nano-hybrid and one nano-filled ormocer-based composite resins, cured by two different light-curing systems, using Fourier transformation infrared (FT-IR) spectroscopy and Vickers microhardness testing at two different depths (top surface, 2 mm). Materials and methods. For FT-IR spectrometry, five cylindrical specimens (5mm in diameter × 2 mm in length) were prepared from each composite resin using Teflon molds and polymerized for 20 seconds. Then, 70-μm wafers were sectioned at the top surface and at2mm from the top surface. The degree of conversion for each sample was calculated using FT-IR spectroscopy. For Vickers micro-hardness testing, three cylindrical specimens were prepared from each composite resin and polymerized for 20 seconds. The Vickers microhardness test (Shimadzu, Type M, Japan) was performed at the top and bottom (depth=2 mm) surfaces of each specimen. Three-way ANOVA with independent variables and Tukey tests were performed at 95% significance level. Results. No significant differences were detected in degree of conversion and microhardness between LED and QTH light-curing units except for the ormocer-based specimen, CeramX, which exhibited significantly higher DC by LED. All the composite resins showed a significantly higher degree of conversion at the surface. Microhardness was not significantly affected by depth, except for Herculite XRV Ultra and CeramX, which showed higher values at the surface. Conclusion. Composite resins containing nano-particles generally exhibited more variations in degree of conversion and microhardness. PMID:26889359

Color stability and flexural strength of poly (methyl methacrylate) and bis-acrylic composite based provisional crown and bridge auto-polymerizing resins exposed to beverages and food dye: an in vitro study.

PubMed

Gujjari, Anil K; Bhatnagar, Vishrut M; Basavaraju, Ravi M

2013-01-01

To evaluate the color stability and flexural strength of poly (methyl methacrylate) (PMMA) and bis-acrylic composite based provisional crown and bridge auto-polymerizing resins exposed to tea, coffee, cola, and food dye. Two provisional crown and bridge resins, one DPI self-cure tooth molding powder (PMMA) (Group A), and one Protemp 4 Temporization Material (bis-acrylic composite) (Group B) were used. Disk-shaped specimens for color stability testing (n = 30 for each material) and bar-shaped specimens for flexural strength testing (n = 30 for each material) were fabricated using a metal mold. The specimens were immersed in artificial saliva, artificial saliva + tea, artificial saliva + coffee, artificial saliva + cola, and artificial saliva + food dye solutions and stored in an incubator at 37°C. Color measurements were taken before immersion, and then after 3 and 7 days of immersion. Flexural strength was evaluated after 7 days of immersion. Group A showed significantly higher color stability as compared to Group B, and artificial saliva + coffee solution had the most staining capacity for the resins. Test solutions had no effect on the flexural strength of Group A, but Group B specimens immersed in artificial saliva + cola showed significantly lower flexural strength values as compared to the control group. The findings of the study showed that for materials used in the study, PMMA was more color stable than bis-acrylic composite based resin. Also, material based on PMMA was more resistant to damage from dietary beverages as compared to bis-acrylic composite based provisional crown and bridge resin.

Shrinkage Stresses Generated during Resin-Composite Applications: A Review

PubMed Central

Schneider, Luis Felipe J.; Cavalcante, Larissa Maria; Silikas, Nick

2010-01-01

Many developments have been made in the field of resin composites for dental applications. However, the manifestation of shrinkage due to the polymerization process continues to be a major problem. The material's shrinkage, associated with dynamic development of elastic modulus, creates stresses within the material and its interface with the tooth structure. As a consequence, marginal failure and subsequent secondary caries, marginal staining, restoration displacement, tooth fracture, and/or post-operative sensitivity are clinical drawbacks of resin-composite applications. The aim of the current paper is to present an overview about the shrinkage stresses created during resin-composite applications, consequences, and advances. The paper is based on results of many researches that are available in the literature. PMID:20948573

Factors affecting marginal integrity of class II bulk-fill composite resin restorations

PubMed Central

Savadi Oskoee, Siavash; Bahari, Mahmoud; Jafari Navimipour, Elmira; Ajami, Amir Ahmad; Ghiasvand, Negar; Savadi Oskoee, Ayda

2017-01-01

Background. Bulk-fill composite resins are a new type of resin-based composite resins, claimed to have the capacity to be placed in thick layers, up to 4 mm. This study was carried out to evaluate factors affecting gap formation in Cl II cavities restored using the bulk-fill technique. Methods. A total of 60 third molars were used in this study. Two Cl II cavities were prepared in each tooth, one on the mesial aspect 1 mm coronal to the CEJ and one on the distal aspect 1 mm apical to the CEJ. The teeth were divided into 4 groups: A: The cavities were restored using the bulk-fill technique with Filtek P90 composite resin and its adhesive system and light-cured with quartz tungsten halogen (QTH) light-curing unit. B: The cavities were restored similar to that in group A but light-cured with an LED light-curing unit. C: The cavities were restored using the bulk-fill technique with X-tra Fil composite resin and Clearfil SE Bond adhesive system and light-cured with a QTH curing unit. D: The cavities were restored similar to that in group C but light-cured with an LED light-curing unit. The gaps were examined under a stereomicroscope at ×60. Data were analyzed with General Linear Model test. In cases of statistical significance (P<0.05), post hoc Bonferroni test was used for further analyses. Results. The light-curing unit type had no effect on gap formation. However, the results were significant in relation to the composite resin type and margin location (P<0.001). The cumulative effects of light-curing unit*gingival margin and light-curing unit*composite resin type were not significant; however, the cumulative effect of composite rein type*gingival margin was significant (P=0.04) Conclusion. X-tra Fil composite exhibited smaller gaps compared with Filtek P90 composite with both light-curing units. Both composite resins exhibited smaller gaps at enamel margins. PMID:28748051

The in vivo wear resistance of 12 composite resins.

PubMed

Lang, B R; Bloem, T J; Powers, J M; Wang, R F

1992-09-01

The in vivo wear resistance of 12 composite resins were compared with an amalgam control using the Latin Square experimental design. Sixteen edentulous patients wearing specially designed complete dentures formed the experimental population. The Michigan Computer Graphics Measurement System was used to digitize the surface of the control and composite resin samples before and after 3-month test periods to obtain wear data. The 12 composite resins selected for this investigation based on their published composite classification types were seven fine particle composites, three blends, and two microfilled composite resins. The Latin Square experimental design was found to be valid with the factor of material being statistically different at the 5% level of significance. Wear was computed as volume loss (mm3/mm2), and all of the composites studied had more wear than the amalgam control (P = .001). After 3 months, the mean (error) of wear of the amalgam was 0.028 (0.006). Means (error) of wear for the 12 composites were ranked from most to least wear by mean wear volume loss. The absence of any relationship between mean wear volume loss and the volume percentage filler was confirmed by the correlation coefficient r = -0.158.

Change in surface roughness of esthetic restorative materials after exposure to different immersion regimes in a cola drink.

PubMed

Bajwa, Navroop Kaur; Pathak, Anuradha

2014-01-01

Context. An in vitro study carried out to evaluate and compare the effect of Cola drink on surface roughness of esthetic restorative materials. Purpose. To compare the effect of different immersion regimes in a Cola drink on surface roughness of esthetic restorative materials. Method. Two hundred samples were grouped into 4 equal groups of 50 samples each: Group I: conventional glass ionomer, Group II: resin modified glass ionomer, Group III: polyacid-modified resin composite, Group IV: Composite resin. Each group was further subdivided into 5 subgroups of 10 samples each. Subgroup A (Control Subgroup). Samples were kept immersed in artificial saliva. Subgroup B. Samples were immersed in Cola drink once a day. Subgroup C. Samples were immersed in Cola drink, 3 times a day. Subgroup D. Samples were immersed in Cola drink 5 times a day. Subgroup E. Samples were immersed in Cola drink 10 times a day. Each immersion lasted 5 minutes. The immersion protocol was repeated for 7 days. Results. Maximum surface roughness was seen in Group I conventional glass ionomer cement, followed by Group II resin modified glass ionomer, Group III polyacid modified resin composite, and Group IV composite resin samples. Conclusion. Resistance to change in surface roughness is more in resin based restorative materials as compared to glass ionomer based materials.

Change in Surface Roughness of Esthetic Restorative Materials after Exposure to Different Immersion Regimes in a Cola Drink

PubMed Central

Bajwa, Navroop Kaur; Pathak, Anuradha

2014-01-01

Context. An in vitro study carried out to evaluate and compare the effect of Cola drink on surface roughness of esthetic restorative materials. Purpose. To compare the effect of different immersion regimes in a Cola drink on surface roughness of esthetic restorative materials. Method. Two hundred samples were grouped into 4 equal groups of 50 samples each: Group I: conventional glass ionomer, Group II: resin modified glass ionomer, Group III: polyacid-modified resin composite, Group IV: Composite resin. Each group was further subdivided into 5 subgroups of 10 samples each. Subgroup A (Control Subgroup). Samples were kept immersed in artificial saliva. Subgroup B. Samples were immersed in Cola drink once a day. Subgroup C. Samples were immersed in Cola drink, 3 times a day. Subgroup D. Samples were immersed in Cola drink 5 times a day. Subgroup E. Samples were immersed in Cola drink 10 times a day. Each immersion lasted 5 minutes. The immersion protocol was repeated for 7 days. Results. Maximum surface roughness was seen in Group I conventional glass ionomer cement, followed by Group II resin modified glass ionomer, Group III polyacid modified resin composite, and Group IV composite resin samples. Conclusion. Resistance to change in surface roughness is more in resin based restorative materials as compared to glass ionomer based materials. PMID:25006464

A review of devices used for photocuring resin-based composites.

PubMed

Small, B W

2001-01-01

Composite resin shrinks up to 5% by volume upon curing. This shrinkage and the associated contraction stress remain the two most significant clinical problems with curing resin composite restorations. Many patients continue to experience sensitivity following placement of direct composites and seating of indirect restorations utilizing resin cements. Unfortunately, some claims made by manufacturers or certain clinicians that promise to alleviate these problems are made from a marketing standpoint, with no refereed literature to support those claims. Even within the literature, contradictory results have been reported, perpetuating the confusion. It is of utmost importance that all practicing dentists be aware of the various types of curing systems available and the advantages and disadvantages of each system. It is the opinion of the author that no existing system will alleviate every problem. Until new composite systems are perfected, such as the cyclopolymerizable resins and expanding polymers, we will continue to have shrinkage and stress. Be aware of false claims, read and interpret the literature, and, most importantly, do what is best for your patients.

High elastic modulus nanopowder reinforced resin composites for dental applications

NASA Astrophysics Data System (ADS)

Wang, Yijun

2007-12-01

Dental restorations account for more than $3 billion dollars a year on the market. Among them, all-ceramic dental crowns draw more and more attention and their popularity has risen because of their superior aesthetics and biocompatibility. However, their relatively high failure rate and labor-intensive fabrication procedure still limit their application. In this thesis, a new family of high elastic modulus nanopowder reinforced resin composites and their mechanical properties are studied. Materials with higher elastic modulus, such as alumina and diamond, are used to replace the routine filler material, silica, in dental resin composites to achieve the desired properties. This class of composites is developed to serve (1) as a high stiffness support to all-ceramic crowns and (2) as a means of joining independently fabricated crown core and veneer layers. Most of the work focuses on nano-sized Al2O3 (average particle size 47 nm) reinforcement in a polymeric matrix with 50:50 Bisphenol A glycidyl methacrylate (Bis-GMA): triethylene glycol dimethacrylate (TEGDMA) monomers. Surfactants, silanizing agents and primers are examined to obtain higher filler levels and enhance the bonding between filler and matrix. Silane agents work best. The elastic modulus of a 57.5 vol% alumina/resin composite is 31.5 GPa compared to current commercial resin composites with elastic modulus <15 GPa. Chemical additives can also effectively raise the hardness to as much as 1.34 GPa. Besides>alumina, diamond/resin composites are studied. An elastic modulus of about 45 GPa is obtained for a 57 vol% diamond/resin composite. Our results indicate that with a generally monodispersed nano-sized high modulus filler, relatively high elastic modulus resin-based composite cements are possible. Time-dependent behavior of our resin composites is also investigated. This is valuable for understanding the behavior of our material and possible fatigue testing in the future. Our results indicate that with effective coupling agents and higher filler loading, viscous flow can be greatly decreased due to the attenuation of mobility of polymer chains. Complementary studies indicate that our resin composites are promising for the proposed applications as a stiff support to all-ceramic crowns.

Foam, Foam-resin composite and method of making a foam-resin composite

NASA Technical Reports Server (NTRS)

MacArthur, Doug E. (Inventor); Cranston, John A. (Inventor)

1995-01-01

This invention relates to a foam, a foam-resin composite and a method of making foam-resin composites. The foam set forth in this invention comprises a urethane modified polyisocyanurate derived from an aromatic amino polyol and a polyether polyol. In addition to the polyisocyanurate foam, the composite of this invention further contains a resin layer, wherein the resin may be epoxy, bismaleimide, or phenolic resin. Such resins generally require cure or post-cure temperatures of at least 350.degree. F.

Synthesis of improved phenolic resins

NASA Technical Reports Server (NTRS)

Delano, C. B.; Mcleod, A. H.

1979-01-01

Twenty seven addition cured phenolic resin compositions were prepared and tested for their ability to give char residues comparable to state-of-the-art phenolic resins. Cyanate, epoxy, allyl, acrylate, methacrylate and ethynyl derivatized phenolic oligomers were investigated. The novolac-cyanate and propargyl-novolac resins provided anaerobic char yields at 800 C of 58 percent. A 59 percent char yield was obtained from modified epoxy novolacs. A phosphonitrilic derivative was found to be effective as an additive for increasing char yields. The novolac-cyanate, epoxy-novolac and methacrylate-epoxy-novolac systems were investigated as composite matrices with Thornel 300 graphite fiber. All three resins showed good potential as composite matrices. The free radical cured methacrylate-epoxy-novolac graphite composite provided short beam shear strengths at room temperature of 93.3 MPa (13.5 ksi). The novolac-cyanate graphite composite produced a short beam shear strength of 74 MPa (10.7 ksi) and flexural strength of 1302 MPa (189 ksi) at 177 C. Air heat aging of the novolac-cyanate and epoxy novolac based composites for 12 weeks at 204 C showed good property retention.

Effect of natural fibers and bio-resins on mechanical properties in hybrid and non-hybrid composites

NASA Astrophysics Data System (ADS)

Fragassa, Cristiano

2016-05-01

The aim of the present experimental investigation was to perform a comparative analysis concerning the influence on mechanical properties of natural fibers and/or bio-resins in reinforced thermoset composites. Flax and basalt fibers were selected as natural reinforcements, as single constituents or in hybrid combination. Glass synthetic fibers were used for comparison. Eco-friendly matrixes, both epoxy or vinylester, were considered and compared with composites based on traditional resins. Samples were fabricated by hand lay-up and resin infusion techniques. Cures were accelerated and controlled by applying heat and pressure in autoclave. Tensile, flexural and impact tests were carried out according to ASTM standards.

Advances in the history of composite resins.

PubMed

Minguez, Nieves; Ellacuria, Joseba; Soler, José Ignacio; Triana, Rodrigo; Ibaseta, Guillermo

2003-11-01

The use of composite resins as direct restoration material in posterior teeth has demonstrated a great increase, due to esthetic requirements and the controversy regarding the mercury content in silver amalgams. In this article, we have reviewed the composition modifications which have occurred in materials based on resins since their introduction over a half a century ago which have enabled great improvements in their physical and mechanical properties. Likewise, we have highlighted current lines of research, centered on finding the ideal material for replacing silver amalgam as a direct filling material.

In-office bleaching efficacy on stain removal from CAD/CAM and direct resin composite materials.

PubMed

Alharbi, Amal; Ardu, Stefano; Bortolotto, Tissiana; Krejci, Ivo

2018-01-01

To evaluate the efficacy of in-office bleaching on stain removal from stained resin composite and ceramic computer-assisted design/computer-assisted manufacturing (CAD/CAM) blocks and direct resin composites. Forty disk-shaped samples were fabricated from each of nine materials: six CAD/CAM (VITABLOCS Mark II, Paradigm MZ100, Exp Vita Hybrid Ceramic, VITA ENAMIC, Exp Kerr, and LAVA Ultimate) and three direct resin composites (Filtek Supreme, Venus Diamond, and Filtek Silorane). Samples were randomly divided into five groups (n = 8), each stained with a particular staining solution. Using a calibrated spectrophotometer and a black background, L*a*b* values were assessed before and after 120 days of staining. Samples were subjected to in-office bleaching using 40% hydrogen peroxide gel for one hour. At subsequent assessment, color change (ΔE) was calculated as the difference between L*a*b* values. Both ANOVA and the Duncan test were used to identify differences between groups (α = 0.05). Bleaching resulted in significant differences in ΔE values for all materials (P < .001). Bleaching efficacy was highly influenced by material composition and staining solution. Residual color values after bleaching for ceramic and hybrid ceramics ranged from -0.49 to 2.35, within the clinically acceptable maximum of 3.3. Values after bleaching for resin-based CAD/CAM ranged from -0.7 to 7.08 while direct resin composites values ranged from -1.47 to 25.13. Coffee left the greatest residual color on all materials. Based on material nature, 40% hydrogen peroxide bleaching can remove staining. The new resin-based CAD/CAM blocks showed promising results in terms of color stability. Bleaching using 40% hydrogen peroxide can be an effective method to remove stains from dental restorations. In this way, restoration replacement as a result of discoloration may no longer be necessary. © 2017 Wiley Periodicals, Inc.

High performance dental resin composites with hydrolytically stable monomers.

PubMed

Wang, Xiaohong; Huyang, George; Palagummi, Sri Vikram; Liu, Xiaohui; Skrtic, Drago; Beauchamp, Carlos; Bowen, Rafael; Sun, Jirun

2018-02-01

The objectives of this project were to: 1) develop strong and durable dental resin composites by employing new monomers that are hydrolytically stable, and 2) demonstrate that resin composites based on these monomers perform superiorly to the traditional bisphenol A glycidyl dimethacrylate/triethylene glycol dimethacrylate (Bis-GMA/TEGDMA) composites under testing conditions relevant to clinical applications. New resins comprising hydrolytically stable, ether-based monomer, i.e., triethylene glycol divinylbenzyl ether (TEG-DVBE), and urethane dimethacrylate (UDMA) were produced via composition-controlled photo-polymerization. Their composites contained 67.5wt% of micro and 7.5wt% of nano-sized filler. The performances of both copolymers and composites were evaluated by a battery of clinically-relevant assessments: degree of vinyl conversion (DC: FTIR and NIR spectroscopy); refractive index (n: optical microscopy); elastic modulus (E), flexural strength (F) and fracture toughness (K IC ) (universal mechanical testing); Knoop hardness (HK; indentation); water sorption (W sp ) and solubility (W su ) (gravimetry); polymerization shrinkage (S v ; mercury dilatometry) and polymerization stress (tensometer). The experimental UDMA/TEG-DVBE composites were compared with the Bis-GMA/TEGDMA composites containing the identical filler contents, and with the commercial micro hybrid flowable composite. UDMA/TEG-DBVE composites exhibited n, E, W sp , W su and S v equivalent to the controls. They outperformed the controls with respect to F (up to 26.8% increase), K IC (up to 27.7% increase), modulus recovery upon water sorption (full recovery vs. 91.9% recovery), and stress formation (up to 52.7% reduction). In addition, new composites showed up to 27.7% increase in attainable DC compared to the traditional composites. Bis-GMA/TEGDMA controls exceeded the experimental composites with respect to only one property, the composite hardness. Significantly, up to 18.1% lower HK values in the experimental series (0.458GPa) were still above the clinically required threshold of approx. 0.4GPa. Hydrolytic stability, composition-controlled polymerization and the overall enhancement in clinically-relevant properties of the new resin composites make them viable candidates to replace traditional resin composites as a new generation of strong and durable dental restoratives. Copyright © 2017 The Academy of Dental Materials. All rights reserved.

Effect of Different Surface Treatments on Repair Micro-shear Bond Strength of Silica- and Zirconia-filled Composite Resins

PubMed Central

Joulaei, Mohammad; Bahari, Mahmoud; Ahmadi, Anahid; Savadi Oskoee, Siavash

2012-01-01

Background and aims Effect of surface treatments on repair bond strength of aged composite resins might be different due to their dissimilar fillers. The aim was to evaluate the effect of different surface treatments on repair micro-shear bond strength (µSBS) of silica- (Spectrum TPH) and zirconia-filled (Filtek Z250) composite resins. Materials and methods Twenty-seven composite resin blocks were made from each type of composite resin: Z250 and Spectrum TPH. After aging, blocks of each type were randomly divided into three groups according to surface treatments: alloy primer, silane, and only surface roughening. Subsequently, each group was further subdivided into 3 subgroups based on the adhesive system used: Single Bond, Clearfil SE Bond, and Margin Bond. Four composite resin columns were added on each block. After thermocycling, µSBStest were done at cross head speed of 0.5 mm/min. Data was analysed using multifactor ANOVA, one-way ANOVA and a post-hoc Bonferroni tests (α = 0.05). Results Analysis of data showed that the effect of composite resin type was not significant (p > 0.05), but the effects of the type of surface treatment (p = 0.01) and the type of adhesive system (p = 0.01) were significant on repair µSBS. In addition, the cumulative effect of the composite type-surface treatment and the composite type with the type of adhesive system were not statistically significant (p > 0.05). However, the cumulative effects of the adhesive system-surface treatment (p = 0.03) and the composite type-the adhesive system-surface treatments (p = 0.002) were significant. Conclusion Although repair µSBS values of both silica- and zirconia-filled composite resins were similar, use of different combinations of surface treatments and adhesive systems affected their repair µSBS differently. PMID:23277859

Embedding piezoresistive pressure sensors to obtain online pressure profiles inside fiber composite laminates.

PubMed

Moghaddam, Maryam Kahali; Breede, Arne; Brauner, Christian; Lang, Walter

2015-03-27

The production of large and complex parts using fiber composite materials is costly due to the frequent formation of voids, porosity and waste products. By embedding different types of sensors and monitoring the process in real time, the amount of wastage can be significantly reduced. This work focuses on developing a knowledge-based method to improve and ensure complete impregnation of the fibers before initiation of the resin cure. Piezoresistive and capacitive pressure sensors were embedded in fiber composite laminates to measure the real-time the pressure values inside the laminate. A change of pressure indicates resin infusion. The sensors were placed in the laminate and the resin was infused by vacuum. The embedded piezoresistive pressure sensors were able to track the vacuum pressure in the fiber composite laminate setup, as well as the arrival of the resin at the sensor. The pressure increase due to closing the resin inlet was also measured. In contrast, the capacitive type of sensor was found to be inappropriate for measuring these quantities. The following study demonstrates real-time monitoring of pressure changes inside the fiber composite laminate, which validate the use of Darcy's law in porous media to control the resin flow during infusion.

Effect of Polymer Form and its Consolidation on Mechanical Properties and Quality of Glass/PBT Composites

NASA Astrophysics Data System (ADS)

Durai Prabhakaran, R. T.; Pillai, Saju; Charca, Samuel; Oshkovr, Simin Ataollahi; Knudsen, Hans; Andersen, Tom Løgstrup; Bech, Jakob Ilsted; Thomsen, Ole Thybo; Lilholt, Hans

2014-04-01

The aim of this study was to understand the role of the processing in determining the mechanical properties of glass fibre reinforced polybutylene terephthalate composites (Glass/PBT). Unidirectional (UD) composite laminates were manufactured by the vacuum consolidation technique using three different material systems included in this study; Glass/CBT (CBT160 powder based resin), Glass/PBT (prepreg tapes), and Glass/PBT (commingled yarns). The different types of thermoplastic polymer resin systems used for the manufacturing of the composite UD laminate dictate the differences in final mechanical properties which were evaluated by through compression, flexural and short beam transverse bending tests. Microscopy was used to evaluate the quality of the processed laminates, and fractography was used to characterize the observed failure modes. The study provides an improved understanding of the relationships between processing methods, resin characteristics, and mechanical performance of thermoplastic resin composite materials.

Depth of Cure of New Flowable Composite Resins

DTIC Science & Technology

2012-03-30

Flowable composites were introduced to the dental community in the late 1990’s (Ikeda, 2009; Bayne, 1998). The advantage of flowable composite-based...Depth of Cure of New Flowable Composite Resins A THESIS Presented to the Faculty of The Air Force Postgraduate Dental School...SCIENCE In Oral Biology By Inaam A. Pedalino, BS, DDS Dunn Dental Clinic Lackland AFB, TX 30 March 2012 Depth of Cure of New

ALL NATURAL COMPOSITE SANDWICH BEAMS FOR STRUCTURAL APPLICATIONS. (R829576)

EPA Science Inventory

As part of developing an all natural composite roof for housing application,
structural panels and unit beams were manufactured out of soybean oil based resin
and natural fibers (flax, cellulose, pulp, recycled paper, chicken feathers)
using vacuum assisted resin tran...

PERFORMANCE ENHANCEMENT OF COMPRESSION MOLDED KENAF FIBER REINFORCED VINYL ESTER COMPOSITES THROUGH RESIN ADDITIVE

DOE Office of Scientific and Technical Information (OSTI.GOV)

Fifield, Leonard S.; Simmons, Kevin L.; Laddha, Sachin

2010-05-17

Plant-based bio-fiber has the potential to achieve weight and cost savings over glass fiber in automotive polymer composites if moisture stability and fiber-resin compatibility issues can be solved. This paper describes the compression molding of 50vol% 2 inch random nonwoven mat kenaf fiber vinyl ester composites with and without chemical resin additives intended to improve moisture stability and resin compatibility. The 2wt% addition of n-undecanoyl chloride or 10-undecenoyl chloride to the styrene-based resin prior to molding of the kenaf composites was observed to decrease the 24hr, 25oC moisture uptake of the molded panels by more than 50%. The tensile stiffnessmore » and flexural stiffness of the soaked panels containing these additives were seen to increase by more than 30% and 70%, respectively, relative to panels made with no additives. While ‘dry’ panel (50% relative humidity at 25oC) strengths did not significantly change in the presence of the additives, tensile strength was observed to increase by more than 40% and flexural strength more than doubled for the soaked panels.« less

Polymerization shrinkage stress of composite resins and resin cements - What do we need to know?

PubMed

Soares, Carlos José; Faria-E-Silva, André Luis; Rodrigues, Monise de Paula; Vilela, Andomar Bruno Fernandes; Pfeifer, Carmem Silvia; Tantbirojn, Daranee; Versluis, Antheunis

2017-08-28

Polymerization shrinkage stress of resin-based materials have been related to several unwanted clinical consequences, such as enamel crack propagation, cusp deflection, marginal and internal gaps, and decreased bond strength. Despite the absence of strong evidence relating polymerization shrinkage to secondary caries or fracture of posterior teeth, shrinkage stress has been associated with post-operative sensitivity and marginal stain. The latter is often erroneously used as a criterion for replacement of composite restorations. Therefore, an indirect correlation can emerge between shrinkage stress and the longevity of composite restorations or resin-bonded ceramic restorations. The relationship between shrinkage and stress can be best studied in laboratory experiments and a combination of various methodologies. The objective of this review article is to discuss the concept and consequences of polymerization shrinkage and shrinkage stress of composite resins and resin cements. Literature relating to polymerization shrinkage and shrinkage stress generation, research methodologies, and contributing factors are selected and reviewed. Clinical techniques that could reduce shrinkage stress and new developments on low-shrink dental materials are also discussed.

Tailoring surface properties of ArF resists thin films with functionally graded materials (FGM)

NASA Astrophysics Data System (ADS)

Takemoto, Ichiki; Ando, Nobuo; Edamatsu, Kunishige; Fuji, Yusuke; Kuwana, Koji; Hashimoto, Kazuhiko; Funase, Junji; Yokoyama, Hiroyuki

2007-03-01

Our recent research effort has been focused on new top coating-free 193nm immersion resists with regard to leaching of the resist components and lithographic performance. We have examined methacrylate-based resins that control the surface properties of ArF resists thin films by surface segregation behavior. For a better understanding of the surface properties of thin films, we prepared the six resins (Resin 1-6) that have three types fluorine containing monomers, a new monomer (Monomer A), Monomer B and Monomer C, respectively. We blended the base polymer (Resin 0) with Resin (1-6), respectively. We evaluated contact angles, surface properties and lithographic performances of the polymer blend resists. The static and receding contact angles of the resist that contains Resin (1-6) are greater than that of the base polymer (Resin 0) resist. The chemical composition of the surface of blend polymers was investigated with X-ray photoelectron spectroscopy (XPS). It was shown that there was significant segregation of the fluorine containing resins to the surface of the blend films. We analyzed Quantitative Structure-Property Relationships (QSPR) between the surface properties and the chemical composition of the surface of polymer blend resists. The addition of 10 wt% of the polymer (Resin 1-6) to the base polymer (Resin 0) did not influence the lithographic performance. Consequently, the surface properties of resist thin films can be tailored by the appropriate choice of fluorine containing polymer blends.

Radiopacity of Methacrylate and Silorane Composite Resins Using a Digital Radiographic System.

PubMed

Firoozmand, Leily Macedo; Cordeiro, Mariana Gonçalves; Da Silva, Marcos André Dos Santos; De Jesus Tavarez, Rudys Rodolfo; Matos Maia Filho, Etevaldo

The aim of this study was to evaluate the radiopacity of silorane and methacrylate resin composites, comparing them to the enamel, dentin, and aluminum penetrometer using a digital image. From six resin composites (Filtek ™ P90, Filtek Z350, Filtek Z350 XT flow, Tetric Ceram, TPH Spectrum, and SureFil SDR flow) cylindrical disks (5 × 1 mm) were made and radiographed by a digital method, together with a 15-step aluminum step-wedge and a 1 mm slice of human tooth. The degree of radiopacity of each image was quantified using digital image processing. The mean values of the shades of gray of the tested materials were measured and the equivalent width of aluminum was calculated for each resin. The results of our work yielded the following radiopacity values, given here in descending order: Tetric Ceram > TPH > SDR > Z350 > Z350 flow > P90 > enamel > dentin. The radiopacity of the materials was different both for the enamel and for the dentin, except for resin P90, which was no different than enamel. In conclusion, silorane-based resin exhibited a radiopacity higher than dentin and closest to the enamel; a large portion of the methacrylate-based flow and conventional resins demonstrated greater radiopacity in comparison to dentin and enamel.

Degradation of strength properties of epoxy resin filled with natural-based particles

NASA Astrophysics Data System (ADS)

Valášek, Petr; Habrová, Karolína; Müller, Miroslav

2018-05-01

Degradation of polymeric materials can be considered as a limiting factor for their use. Mechanical characteristics of epoxy resins are reduced, for example, by the action and changes of temperature or humidity. Degradation also occurs in composite systems where the epoxy resins function as matrices, i.e. in polymer composite materials. If a natural filler is used together with the epoxy resin, we refer to these materials as biocomposites, where also the natural character of the filler material greatly affects the degradation process. The paper focuses on the description of the shear strength of the resin filled with particles prepared from the seeds of dates of Phoenix Dactylifera plant. The degradation was evaluated experimentally in laboratory conditions via the climatic chamber. The experiment describes composites with a particle size of filler 100-200 μm with a concentration of 5 - 10 wt%. As the number of degradation cycles increased, the tensile strength of both the unfilled and the filled epoxy resin decreased. After 5 weeks, the drop was up to 50%. The presence of the particles did not significantly affect the shear strength compared to the non-filled resin. The described way of utilization of the natural-based particles is the possibility of material utilization of secondary natural materials.

Does the light source affect the repairability of composite resins?

PubMed

Karaman, Emel; Gönülol, Nihan

2014-01-01

The aim of this study was to examine the effect of the light source on the microshear bond strength of different composite resins repaired with the same substrate. Thirty cylindrical specimens of each composite resin--Filtek Silorane, Filtek Z550 (3M ESPE), Gradia Direct Anterior (GC), and Aelite Posterior (BISCO)--were prepared and light-cured with a QTH light curing unit (LCU). The specimens were aged by thermal cycling and divided into three subgroups according to the light source used--QTH, LED, or PAC (n = 10). They were repaired with the same substrate and a Clearfil Repair Kit (Kuraray). The specimens were light-cured and aged for 1 week in distilled water at 37 °C. The microshear bond strength and failure modes were assessed. There was no significant difference in the microshear bond strength values among the composite resins, except for the Filtek Silorane group that showed significantly lower bond strength values when polymerized with the PAC unit compared to the QTH or LED unit. In conclusion, previously placed dimethacrylate-based composites can be repaired with different light sources; however, if the composite to be repaired is silorane-based, then using a QTH or LED device may be the best option.

Effect of low-shrinkage monomers on the physicochemical properties of experimental composite resin

PubMed Central

He, Jingwei; Garoushi, Sufyan; Vallittu, Pekka K.; Lassila, Lippo

2018-01-01

Abstract This study was conducted to determine whether novel experimental low-shrinkage dimethacrylate co-monomers could provide low polymerization shrinkage composites without sacrifice to degree of conversion, and mechanical properties of the composites. Experimental composites were prepared by mixing 28.6 wt% of bisphenol-A-glycidyl dimethacrylate based resin matrix (bis-GMA) with various weight-fractions of co-monomers; tricyclo decanedimethanol dacrylate (SR833s) and isobornyl acrylate (IBOA) to 71.4 wt% of particulate-fillers. A composite based on bis-GMA/TEGDMA (triethylene glycol dimethacrylate) was used as a control. Fracture toughness and flexural strength were determined for each experimental material following international standards. Degree of monomer-conversion (DC%) was determined by FTIR spectrometry. The volumetric shrinkage in percent was calculated as a buoyancy change in distilled water by means of the Archimedes’ principle. Polymerization shrinkage-strain and -stress of the specimens were measured using the strain-gage technique and tensilometer, respectively with respect to time. Statistical analysis revealed that control group had the highest double-bond conversion (p < .05) among the experimental resins tested. All of the experimental composite resins had comparable flexural strength, modulus, and fracture toughness (p > .05). Volumetric shrinkage and shrinkage stress decreased with increasing IBOA concentration. Replacing TEGDMA with SR833s and IBOA can decrease the volumetric shrinkage, shrinkage strain, and shrinkage stress of composite resins without affecting the mechanical properties. However, the degree of conversion was also decreased. PMID:29536025

Effect of low-shrinkage monomers on the physicochemical properties of experimental composite resin.

PubMed

He, Jingwei; Garoushi, Sufyan; Vallittu, Pekka K; Lassila, Lippo

2018-01-01

This study was conducted to determine whether novel experimental low-shrinkage dimethacrylate co-monomers could provide low polymerization shrinkage composites without sacrifice to degree of conversion, and mechanical properties of the composites. Experimental composites were prepared by mixing 28.6 wt% of bisphenol-A-glycidyl dimethacrylate based resin matrix ( bis -GMA) with various weight-fractions of co-monomers; tricyclo decanedimethanol dacrylate (SR833s) and isobornyl acrylate (IBOA) to 71.4 wt% of particulate-fillers. A composite based on bis -GMA/TEGDMA (triethylene glycol dimethacrylate) was used as a control. Fracture toughness and flexural strength were determined for each experimental material following international standards. Degree of monomer-conversion (DC%) was determined by FTIR spectrometry. The volumetric shrinkage in percent was calculated as a buoyancy change in distilled water by means of the Archimedes' principle. Polymerization shrinkage-strain and -stress of the specimens were measured using the strain-gage technique and tensilometer, respectively with respect to time. Statistical analysis revealed that control group had the highest double-bond conversion ( p  < .05) among the experimental resins tested. All of the experimental composite resins had comparable flexural strength, modulus, and fracture toughness ( p  > .05). Volumetric shrinkage and shrinkage stress decreased with increasing IBOA concentration. Replacing TEGDMA with SR833s and IBOA can decrease the volumetric shrinkage, shrinkage strain, and shrinkage stress of composite resins without affecting the mechanical properties. However, the degree of conversion was also decreased.

Microleakage and shear punch bond strength in class II primary molars cavities restored with low shrink silorane based versus methacrylate based composite using three different techniques.

PubMed

Fahmy, Amal Ezzeldin; Farrag, Nadia Moustafa

2010-01-01

This in vitro study aimed to evaluate the gingival microleakage in class II cavities in primary molars restored with a low shrink silorane resin composite (Filtek P90) or a nanohybride composite resin (Filtek supreme XT) using three different techniques, (total bonding, closed or open sandwich techniques) lined by nano-filled resin modified glass ionomer cement RMGIC (Ketac N100). Additionally, the shear punch bond strength between the two types of composite and KNIO0 was also examined. For microleakage test, two standardized class II slot cavities were prepared in proximal surfaces of 60 sound extracted primary molars which were divided into 2 groups of 30 each according to the type of composite. Each group was subdivided into 3 groups (n = 10) according to the restorative technique used. The restored teeth were examined for microleakage after immersion in 2% methylene blue dye using stereomicroscope at 20 X. Microleakage scores among the groups were compared using Kruskal Wallis test followed by pair wise Mann Whitney U test at P < or = 0.05. Thirty disc specimens were prepared for determining the shear punch bond strength between the two composite materials and the KN100. Specimens were divided into 5 groups (n = 6) according to the adhesive protocol. The differences in mean bond strength values in MPa between groups were statistically analyzed using ANOVA followed by pair wise Tukey Post hoc test at P < or = 0. 05. Mode of failure was also evaluated for all groups. Both the silorane resin and nano-composite resin showed superior marginal seal with the total bonding technique compared to closed and open sandwich techniques. The recorded mean shear punch bond strength values showed no statistical significant difference between the two resin composites without or with their adhesive bonding systems when bonded to the nano-ionomer. All specimens showed cohesive mode of failures except for silorane resin with Adper Easy Bond Self Etch Adhesive (AEBSEA) which showed adhesive mode of failure. The best marginal seal was obtained with the total bonding technique using both resin composites. The shear punch bond strength between KN100 and the two composite materials was not affected by either of the used adhesive bonding agent.

Insufficient cure under the condition of high irradiance and short irradiation time.

PubMed

Feng, Li; Carvalho, Ricardo; Suh, Byoung I

2009-03-01

To investigate if and why a plasma arc curing (PAC) light tends to undercure methacrylate-based resins or resin composites. Model dimethacrylate resins, commercial dental adhesives, and commercial resin composites were cured using a PAC light and a halogen light with the similar radiant exposures but different combinations of irradiance and irradiation time. The degree of double bond conversion (DC) was measured with FTIR spectroscopy and analyzed as a function of radiant exposure. The PAC light produced a lower DC than the halogen light for the model resin with the lowest viscosity and for three of the four adhesives. With a high irradiance, the PAC light could cure three of the four composites as thoroughly as its halogen counterpart. When the irradiance was reduced, however, three composites yielded a lower DC. Insufficient cure by PAC lights or any curing lights with very high irradiance is likely to happen when too short an irradiation time is used. It is because under higher irradiance, the lifetime of free radicals is shorter.

Cure Cycle Design Methodology for Fabricating Reactive Resin Matrix Fiber Reinforced Composites: A Protocol for Producing Void-free Quality Laminates

NASA Technical Reports Server (NTRS)

Hou, Tan-Hung

2014-01-01

For the fabrication of resin matrix fiber reinforced composite laminates, a workable cure cycle (i.e., temperature and pressure profiles as a function of processing time) is needed and is critical for achieving void-free laminate consolidation. Design of such a cure cycle is not trivial, especially when dealing with reactive matrix resins. An empirical "trial and error" approach has been used as common practice in the composite industry. Such an approach is not only costly, but also ineffective at establishing the optimal processing conditions for a specific resin/fiber composite system. In this report, a rational "processing science" based approach is established, and a universal cure cycle design protocol is proposed. Following this protocol, a workable and optimal cure cycle can be readily and rationally designed for most reactive resin systems in a cost effective way. This design protocol has been validated through experimental studies of several reactive polyimide composites for a wide spectrum of usage that has been documented in the previous publications.

Characterization of porous glass fiber-reinforced composite (FRC) implant structures: porosity and mechanical properties.

PubMed

Ylä-Soininmäki, Anne; Moritz, Niko; Lassila, Lippo V J; Peltola, Matti; Aro, Hannu T; Vallittu, Pekka K

2013-12-01

The aim of this study was to characterize the microstructure and mechanical properties of porous fiber-reinforced composites (FRC). Implants made of the FRC structures are intended for cranial applications. The FRC specimens were prepared by impregnating E-glass fiber sheet with non-resorbable bifunctional bis-phenyl glycidyl dimethacrylate and triethylene glycol dimethacrylate resin matrix. Four groups of porous FRC specimens were prepared with a different amount of resin matrix. Control group contained specimens of fibers, which were bound together with sizing only. Microstructure of the specimens was analyzed using a micro computed tomography (micro-CT) based method. Mechanical properties of the specimens were measured with a tensile test. The amount of resin matrix in the specimens had an effect on the microstructure. Total porosity was 59.5 % (median) in the group with the lowest resin content and 11.2 % (median) in the group with the highest resin content. In control group, total porosity was 94.2 % (median). Correlations with resin content were obtained for all micro-CT based parameters except TbPf. The tensile strength of the composites was 21.3 MPa (median) in the group with the highest resin content and 43.4 MPa (median) in the group with the highest resin content. The tensile strength in control group was 18.9 MPa (median). There were strong correlations between the tensile strength of the specimens and most of the micro-CT based parameters. This experiment suggests that porous FRC structures may have the potential for use in implants for cranial bone reconstructions, provided further relevant in vitro and in vivo tests are performed.

Radiopacity of conventional, resin-modified glass ionomer, and resin-based luting materials.

PubMed

Tsuge, Takuma

2009-06-01

The purpose of the present study was to evaluate the radiopacity of currently available dental luting materials. Five conventional cements, six resin-modified glass ionomers (RMGIs), two methyl methacrylate (MMA)-based acrylic resins (eight shades), and nine composite luting materials were evaluated. Radiographs of the specimens were taken together with tooth slices and aluminum step wedges. The density of the specimens was determined with a densitometer and was expressed in terms of the equivalent thickness of aluminum per 2.0-mm unit thickness of specimen. The radiopacity values for human enamel and dentin were 4.3 and 2.3 mm Al/2.0 mm specimen, respectively. The values for materials ranged from 5.1 to 12.9 for conventional luting materials, from 3.4 to 6.3 for RMGIs, from less than 0.5 to 7.3 for MMA resins, and from 2.3 to 9.9 for the composite luting materials. A zinc phosphate cement showed the highest value (12.9), whereas five shades of MMA resin resulted in the lowest value (less than 0.5). Two RMGIs and three composite luting materials exhibited radiopacity values between those of enamel (4.3) and dentin (2.3). It can be concluded that the radiopacity value of luting materials varies considerably, and that care must be taken when selecting luting materials, considering the material composition of restorations.

Update on dental nanocomposites.

PubMed

Chen, M-H

2010-06-01

Dental resin-composites are comprised of a photo-polymerizable organic resin matrix and mixed with silane-treated reinforcing inorganic fillers. In the development of the composites, the three main components can be modified: the inorganic fillers, the organic resin matrix, and the silane coupling agents. The aim of this article is to review recent studies of the development of dental nanocomposites and their clinical applications. In nanocomposites, nanofillers are added and distributed in a dispersed form or as clusters. For increasing the mineral content of the tooth, calcium and phosphate ion-releasing composites and fluoride-releasing nanocomposites were developed by the addition of DCPA-whiskers or TTCP-whiskers or by the use of calcium fluoride or kaolinite. For enhancing mechanical properties, nanocomposites reinforced with nanofibers or nanoparticles were investigated. For reducing polymerization shrinkage, investigators modified the resin matrix by using methacrylate and epoxy functionalized nanocomposites based on silsesquioxane cores or epoxy-resin-based nanocomposites. The effects of silanization were also studied. Clinical consideration of light-curing modes and mechanical properties of nanocomposites, especially strength durability after immersion, was also addressed.

Effect of bulk-fill base material on fracture strength of root-filled teeth restored with laminate resin composite restorations.

PubMed

Taha, N A; Maghaireh, G A; Ghannam, A S; Palamara, J E

2017-08-01

To evaluate the effect of using a bulk-fill flowable base material on fracture strength and fracture patterns of root-filled maxillary premolars with MOD preparations restored with laminate restorations. Fifty extracted maxillary premolars were selected for the study. Standardized MOD cavities with endodontic treatment were prepared for all teeth, except for intact control. The teeth were divided randomly into five groups (n=10); (Group 1) sound teeth, (Group 2) unrestored teeth; (Group 3) MOD cavities with Vitrebond base and resin-based composite (Ceram. X One Universal); (Group 4) MOD cavities with 2mm GIC base (Fuji IX GP) and resin-based composite (Ceram. X One Universal) open laminate, (Group 5) MOD cavities were restored with 4mm of bulk-fill flowable base material (SDR) and resin-based composite (Ceram. X One Universal). All teeth were thermocycled and subjected to a 45° ramped oblique load in a universal testing machine. Fracture load and fracture patterns were recorded. Data were analyzed using one-way ANOVA and Dunnett's T3 test. Restoration in general increased the fracture strength compared to unrestored teeth. The fracture strength of group 5 (bulk-fill) was significantly higher than the fracture strength of the GIC laminate groups and not significantly different from the intact teeth (355±112N, P=0.118). The type of failure was unfavorable for most of the groups, with the majority being mixed failures. The use of a bulk-fill flowable base material significantly increased the fracture strength of extracted root-filled teeth with MOD cavities; however it did not improve fracture patterns to more favorable ones. Investigating restorative techniques that may improve the longevity of root-filled premolar teeth restored with direct resin restorations. Copyright © 2017 Elsevier Ltd. All rights reserved.

Aspects of the Fracture Toughness of Carbon Nanotube Modified Epoxy Polymer Composites

NASA Astrophysics Data System (ADS)

Mirjalili, Vahid

Epoxy resins used in fibre reinforced composites exhibit a brittle fracture behaviour, because they show no sign of damage prior to a catastrophic failure. Rubbery materials and micro-particles have been added to epoxy resins to improve their fracture toughness, which reduces strength and elastic properties. In this research, carbon nanotubes (CNTs) are investigated as a potential toughening agent for epoxy resins and carbon fibre reinforced composites, which can also enhance strength and elastic properties. More specifically, the toughening mechanisms of CNTs are investigated theoretically and experimentally. The effect of aligned and randomly oriented carbon nanotubes (CNTs) on the fracture toughness of polymers was modelled using Elastic Plastic Fracture Mechanics. Toughening from CNT pull-out and rupture were considered, depending on the CNTs critical length. The model was used to identify the effect of CNTs geometrical and mechanical properties on the fracture toughness of CNT-modified epoxies. The modelling results showed that a uniform dispersion and alignment of a high volume fraction of CNTs normal to the crack growth plane would lead to the maximum fracture toughness enhancement. To achieve a uniform dispersion, the effect of processing on the dispersion of single walled and multi walled CNTs in epoxy resins was investigated. An instrumented optical microscope with a hot stage was used to quantify the evolution of the CNT dispersion during cure. The results showed that the reduction of the resin viscosity at temperatures greater than 100 °C caused an irreversible re-agglomeration of the CNTs in the matrix. The dispersion quality was then directly correlated to the fracture toughness of the modified resin. It was shown that the fine tuning of the ratio of epoxy resin, curing agent and CNT content was paramount to the improvement of the base resin fracture toughness. For the epoxy resin (MY0510 from Hexcel), an improvement of 38% was achieved with 0.3 wt.% of Single Walled CNT (SWNT). Finally, the CNT-modified epoxy resin was used to manufacture carbon fibre laminates by resin film infusion and prepreg technologies. The Mode I and Mode II delamination properties of the CNT-modified composite increased by 140% and 127%, respectively. In contrast, this improvement was not observed for the base CNT-modified polymers, used to manufacture the composite laminates. A qualitative analysis of the fractured surface using a Scanning Electron Microscope revealed a good dispersion in the composites samples, confirming the importance of processing to harness the full potential of carbon nanotubes for toughening polymer composites.

Polymeric composites on the basis of Martian ground for building future mars stations

NASA Astrophysics Data System (ADS)

Mukbaniani, O. V.; Aneli, J. N.; Markarashvili, E. G.; Tarasashvili, M. V.; Aleksidze, N. D.

2016-04-01

The colonization of Mars will require obtaining building materials which can be put in place and processed into buildings via various constructive technologies. We tried to use artificial Martian ground - AMG (GEO PAT 11-234 (2015)) and special resins for the preparation of building block prototypes. The composite material has been obtained based on the AMG as filler, epoxy resin (type ED-20) and tetraethoxysilane - TEOS. We have studied strengthening - softening temperatures and water absorption of the AMG polymer composites that are determined by epoxy resin and TEOS modification. Comparison of the experimental results shows that composites containing modified filler have higher values of the maximum ultimate strength, resistance and flexibility parameters than unmodified composites with definite loading. Modified composites also have a higher softening temperature and lower water absorption.

Monitoring in situ in real time of resin infusion for thermoset composite structures

NASA Astrophysics Data System (ADS)

Faci, A.; Wang, P.; Cochrane, C.; Koncar, V.

2017-10-01

The presented work investigates changes in electrical resistance of embedded sensory yarns as a method to monitor the resin flow front position and curing degree of resin during manufacturing of composite structures by vacuum infusion technology. The sensor concept is based on Piezo-resistive sensors integrated to the flax fabric, having almost identical propriety and dimensions as the flax threads used for the production of reinforcements. In the first time sensors have been characterized and first measures of the resin infusion have been realized in order to demonstrate the feasibility of the proposed approach. Then, the measures in real time were realized with fibrous sensors added to the flax fabric (green composites) to monitor the flow front of resin. A large amount of data recorded, filtered, examined, analysed and processed in order to understand and to optimize the infusion and polymerization process.

Bacterial adhesion on direct and indirect dental restorative composite resins: An in vitro study on a natural biofilm.

PubMed

Derchi, Giacomo; Vano, Michele; Barone, Antonio; Covani, Ugo; Diaspro, Alberto; Salerno, Marco

2017-05-01

Both direct and indirect techniques are used for dental restorations. Which technique should be preferred or whether they are equivalent with respect to bacterial adhesion is unclear. The purpose of this in vitro study was to determine the affinity of bacterial biofilm to dental restorative composite resins placed directly and indirectly. Five direct composite resins for restorations (Venus Diamond, Adonis, Optifil, Enamel Plus HRi, Clearfil Majesty Esthetic) and 3 indirect composite resins (Gradia, Estenia, Signum) were selected. The materials were incubated in unstimulated whole saliva for 1 day. The biofilms grown were collected and their bacterial cells counted. In parallel, the composite resin surface morphology was analyzed with atomic force microscopy. Both bacterial cell count and surface topography parameters were subjected to statistical analysis (α=.05). Indirect composite resins showed significantly lower levels than direct composite resins for bacterial cell adhesion, (P<.001). No significant differences were observed within the direct composite resins (P>.05). However, within the indirect composite resins a significantly lower level was found for Gradia than Estenia or Signum (P<.01). A partial correlation was observed between composite resin roughness and bacterial adhesion when the second and particularly the third-order statistical moments of the composite resin height distributions were considered. Indirect dental restorative composite resins were found to be less prone to biofilm adhesion than direct composite resins. A correlation of bacterial adhesion to surface morphology exists that is described by kurtosis; thus, advanced data analysis is required to discover possible insights into the biologic effects of morphology. Copyright © 2016 Editorial Council for the Journal of Prosthetic Dentistry. Published by Elsevier Inc. All rights reserved.

[Disintegration of visible light-cured composite resins caused by long-term water immersion].

PubMed

Hino, T; Arai, K

1989-05-01

The purpose of this study is to clarify a cause of disintegration of composite resins by long-term immersion in distilled water. Three kinds of visible light-cured composite resins (Heliosit, Plurafil Super and Visio Dispers) and one conventional composite resin (Clearfil F II) were prepared as the specimens with a 20 mm diameter and 1 mm thickness. These specimens were immersed in distilled water at 37 +/- 1 degree C for 3 years. These specimens were analysed and observed by a comprehensive multi analyzer and scanning electron microscope. The other hand residues in distilled water were analysed by infrared (IR) and nuclear magnetic resonance (NMR) spectrometers. The surface layer of all four composite resins showed signs of disintegration. The composite resins with abundant dissolved substances had disintegrated markedly, and such disintegration occurred deep inside the specimens. In IR and 1H-NMR spectra of dissolved substances, two visible light-cured composite resins (Heliosit and Plurafil Super) could be detected unreacted monomers, but one visible light-cured composite resin (Visio Dispers) and one conventional composite resin (Clearfil F II) could not be detected them. In 1H-NMR spectra of dissolved substances of all four composite resins, new signals not composed originally were observed. The progress of disintegration were demonstrated clearly. The dissolved substances were shown as the disintegrated substance between resin matrixs and silane coupling agents. It is suggested that the disintegration of composite resins by long-term water immersion is derived from hydrolysis.

Mechanical fatigue degradation of ceramics versus resin composites for dental restorations.

PubMed

Belli, Renan; Geinzer, Eva; Muschweck, Anna; Petschelt, Anselm; Lohbauer, Ulrich

2014-04-01

For posterior partial restorations an overlap of indication exists where either ceramic or resin-based composite materials can be successfully applied. The aim of this study was to compare the fatigue resistance of modern dental ceramic materials versus dental resin composites in order to address such conflicts. Bar specimens of five ceramic materials and resin composites were produced according to ISO 4049 and stored for 14 days in distilled water at 37°C. The following ceramic materials were selected for testing: a high-strength zirconium dioxide (e.max ZirCAD, Ivoclar), a machinable lithium disilicate (e.max CAD, Ivoclar), a pressable lithium disilicate ceramic (e-max Press, Ivoclar), a fluorapatite-based glass-ceramic (e.max Ceram, Ivoclar), and a machinable color-graded feldspathic porcelain (Trilux Forte, Vita). The composite materials selected were: an indirect machinable composite (Lava Ultimate, 3M ESPE) and four direct composites with varying filler nature (Clearfil Majesty Posterior, Kuraray; GrandioSO, Voco; Tetric EvoCeram, Ivoclar-Vivadent; and CeramX Duo, Dentsply). Fifteen specimens were tested in water for initial strength (σin) in 4-point bending. Using the same test set-up, the residual flexural fatigue strength (σff) was determined using the staircase approach after 10(4) cycles at 0.5 Hz (n=25). Weibull parameters σ0 and m were calculated for the σin specimens, whereas the σff and strength loss in percentage were obtained from the fatigue experiment. The zirconium oxide ceramic showed the highest σin and σff (768 and 440 MPa, respectively). Although both lithium disilicate ceramics were similar in the static test, the pressable version showed a significantly higher fatigue resistance after cyclic loading. Both the fluorapatite-based and the feldspathic porcelain showed equivalent initial and cyclic fatigue properties. From the composites, the highest filled direct material Clearfil Majesty Posterior showed superior fatigue performance. From all materials, e.max Press and Clearfil Majesty Posterior showed the lowest strength loss (29.6% and 32%, respectively), whereas the other materials lost between 41% and 62% of their flexural strength after cyclic loading. Dental ceramics and resin composite materials show equivalent fatigue strength degradation at loads around 0.5σin values. Apart from the zirconium oxide and the lithium disilicate ceramics, resin composites generally showed better σff after 10,000 cycles than the fluorapatite glass-ceramic and the feldspathic porcelain. Resin composite restorations may be used as an equivalent alternative to glass-rich-ceramic inlays regarding mechanical performance. Copyright © 2014 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Embedding Piezoresistive Pressure Sensors to Obtain Online Pressure Profiles Inside Fiber Composite Laminates

PubMed Central

Kahali Moghaddam, Maryam; Breede, Arne; Brauner, Christian; Lang, Walter

2015-01-01

The production of large and complex parts using fiber composite materials is costly due to the frequent formation of voids, porosity and waste products. By embedding different types of sensors and monitoring the process in real time, the amount of wastage can be significantly reduced. This work focuses on developing a knowledge-based method to improve and ensure complete impregnation of the fibers before initiation of the resin cure. Piezoresistive and capacitive pressure sensors were embedded in fiber composite laminates to measure the real-time the pressure values inside the laminate. A change of pressure indicates resin infusion. The sensors were placed in the laminate and the resin was infused by vacuum. The embedded piezoresistive pressure sensors were able to track the vacuum pressure in the fiber composite laminate setup, as well as the arrival of the resin at the sensor. The pressure increase due to closing the resin inlet was also measured. In contrast, the capacitive type of sensor was found to be inappropriate for measuring these quantities. The following study demonstrates real-time monitoring of pressure changes inside the fiber composite laminate, which validate the use of Darcy’s law in porous media to control the resin flow during infusion. PMID:25825973

Conservative Approach for the Esthetic Management of Multiple Interdental Spaces: A Systematic Approach.

PubMed

Báez Rosales, Abelardo; De Nordenflycht Carvacho, Diego; Schlieper Cacciutolo, Ramón; Gajardo Guineo, Manuel; Gandarillas Fuentes, Claudio

2015-01-01

To describe a conservative approach using resin-based composites following a buccolingual layering technique with a customized silicon index for the management of multiple diastemas. This clinical article describes the case of a patient with their anterior teeth esthetically compromised by multiple diastemas, incisal wear, and dull/low-value cervical composite resin restorations that were managed with nanofilled composite resin using the "buccolingual technique" with a customized silicon index made from a wax-up to build up the restorations. The first layer of composite placed lingually that represents the enamel replacement was placed directly on the silicon index so that it provides in one single step the lingual profile and the position of the incisal edge of the restoration. Then, dentine and effect composite resin can be applied in a precise three-dimensional configuration. To solve esthetic dental problems, as anterior diastemas, in a very conservative and even reversible way, the use of direct resin composites for layering is an excellent choice, but should be performed based on simple and reproducible techniques, as the buccolingual technique. The clinical technique described in this paper shows the advantages of a conservative approach to correct diastemas on maxillary anterior teeth. The application of these techniques can not only help achieve optimal esthetics, but also avoid the removal of extensive dental hard tissue and achieve a predictable final result, especially in esthetically demanding cases. © 2015 Wiley Periodicals, Inc.

Fracture resistance of endodontically treated teeth restored with a bulkfill flowable material and a resin composite

PubMed Central

Isufi, Almira; Plotino, Gianluca; Grande, Nicola Maria; Ioppolo, Pietro; Testarelli, Luca; Bedini, Rossella; Al-Sudani, Dina; Gambarini, Gianluca

2016-01-01

Summary Aim To determine and compare the fracture resistance of endodontically treated teeth restored with a bulk fill flowable material (SDR) and a traditional resin composite. Methods Thirty maxillary and 30 mandibular first molars were selected based on similar dimensions. After cleaning, shaping and filling of the root canals and adhesive procedures, specimens were assigned to 3 subgroups for each tooth type (n=10): Group A: control group, including intact teeth; Group B: access cavities were restored with a traditional resin composite (EsthetX; Dentsply-Italy, Rome, Italy); Group C: access cavities were restored with a bulk fill flowable composite (SDR; Dentsply-Italy), except 1.5 mm layer of the occlusal surface that was restored with the same resin composite as Group B. The specimens were subjected to compressive force in a material static-testing machine until fracture occurred, the maximum fracture load of the specimens was measured (N) and the type of fracture was recorded as favorable or unfavorable. Data were statistically analyzed with one-way analysis of variance (ANOVA) and Bonferroni tests (P<0.05). Results No statistically significant differences were found among groups (P<0.05). Fracture resistance of endodontically treated teeth restored with a traditional resin composite and with a bulk fill flowable composite (SDR) was similar in both maxillary and mandibular molars and showed no significant decrease in fracture resistance compared to intact specimens. Conclusions No significant difference was observed in the mechanical fracture resistance of endodontically treated molars restored with traditional resin composite restorations compared to bulk fill flowable composite restorations. PMID:27486505

Fracture resistance of endodontically treated teeth restored with a bulkfill flowable material and a resin composite.

PubMed

Isufi, Almira; Plotino, Gianluca; Grande, Nicola Maria; Ioppolo, Pietro; Testarelli, Luca; Bedini, Rossella; Al-Sudani, Dina; Gambarini, Gianluca

2016-01-01

To determine and compare the fracture resistance of endodontically treated teeth restored with a bulk fill flowable material (SDR) and a traditional resin composite. Thirty maxillary and 30 mandibular first molars were selected based on similar dimensions. After cleaning, shaping and filling of the root canals and adhesive procedures, specimens were assigned to 3 subgroups for each tooth type (n=10): Group A: control group, including intact teeth; Group B: access cavities were restored with a traditional resin composite (EsthetX; Dentsply-Italy, Rome, Italy); Group C: access cavities were restored with a bulk fill flowable composite (SDR; Dentsply-Italy), except 1.5 mm layer of the occlusal surface that was restored with the same resin composite as Group B. The specimens were subjected to compressive force in a material static-testing machine until fracture occurred, the maximum fracture load of the specimens was measured (N) and the type of fracture was recorded as favorable or unfavorable. Data were statistically analyzed with one-way analysis of variance (ANOVA) and Bonferroni tests (P<0.05). No statistically significant differences were found among groups (P<0.05). Fracture resistance of endodontically treated teeth restored with a traditional resin composite and with a bulk fill flowable composite (SDR) was similar in both maxillary and mandibular molars and showed no significant decrease in fracture resistance compared to intact specimens. No significant difference was observed in the mechanical fracture resistance of endodontically treated molars restored with traditional resin composite restorations compared to bulk fill flowable composite restorations.

Near-Infrared Spectroscopic Method for Monitoring Water Content in Epoxy Resins and Fiber-Reinforced Composites

PubMed Central

Gagani, Abedin I.; Echtermeyer, Andreas T.

2018-01-01

Monitoring water content and predicting the water-induced drop in strength of fiber-reinforced composites are of great importance for the oil and gas and marine industries. Fourier transform infrared (FTIR) spectroscopic methods are broadly available and often used for process and quality control in industrial applications. A benefit of using such spectroscopic methods over the conventional gravimetric analysis is the possibility to deduce the mass of an absolutely dry material and subsequently the true water content, which is an important indicator of water content-dependent properties. The objective of this study is to develop an efficient and detailed method for estimating the water content in epoxy resins and fiber-reinforced composites. In this study, Fourier transform near-infrared (FT-NIR) spectroscopy was applied to measure the water content of amine-epoxy neat resin. The method was developed and successfully extended to glass fiber-reinforced composite materials. Based on extensive measurements of neat resin and composite samples of varying water content and thickness, regression was performed, and the quantitative absorbance dependence on water content in the material was established. The mass of an absolutely dry resin was identified, and the true water content was obtained. The method was related to the Beer–Lambert law and explained in such terms. A detailed spectroscopic method for measuring water content in resins and fiber-reinforced composites was developed and described. PMID:29641451

Near-Infrared Spectroscopic Method for Monitoring Water Content in Epoxy Resins and Fiber-Reinforced Composites.

PubMed

Krauklis, Andrey E; Gagani, Abedin I; Echtermeyer, Andreas T

2018-04-11

Monitoring water content and predicting the water-induced drop in strength of fiber-reinforced composites are of great importance for the oil and gas and marine industries. Fourier transform infrared (FTIR) spectroscopic methods are broadly available and often used for process and quality control in industrial applications. A benefit of using such spectroscopic methods over the conventional gravimetric analysis is the possibility to deduce the mass of an absolutely dry material and subsequently the true water content, which is an important indicator of water content-dependent properties. The objective of this study is to develop an efficient and detailed method for estimating the water content in epoxy resins and fiber-reinforced composites. In this study, Fourier transform near-infrared (FT-NIR) spectroscopy was applied to measure the water content of amine-epoxy neat resin. The method was developed and successfully extended to glass fiber-reinforced composite materials. Based on extensive measurements of neat resin and composite samples of varying water content and thickness, regression was performed, and the quantitative absorbance dependence on water content in the material was established. The mass of an absolutely dry resin was identified, and the true water content was obtained. The method was related to the Beer-Lambert law and explained in such terms. A detailed spectroscopic method for measuring water content in resins and fiber-reinforced composites was developed and described.

Longevity of direct and indirect resin composite restorations in permanent posterior teeth: A systematic review and meta-analysis.

PubMed

da Veiga, Ana Maria Antonelli; Cunha, Amanda Carneiro; Ferreira, Daniele Masterson Tavares Pereira; da Silva Fidalgo, Tatiana Kelly; Chianca, Thomaz Kauark; Reis, Kátia Rodrigues; Maia, Lucianne Cople

2016-11-01

The aim of this systematic review and meta-analysis was to assess the differences in clinical performance in direct and indirect resin composite restorations in permanent posterior teeth. PubMed, the Cochrane Library, Web of Science, Scopus, LILACS, BBO, ClinicalTrials.gov and SiGLE were searched without restrictions. We included randomized clinical trials (RCTs) that compared the clinical performance of direct and indirect resin composite restorations in Class I and Class II cavities in permanent teeth, with at least two years of follow-up. The risk of bias tool suggested by Cochrane Collaboration was used for quality assessment. After duplicate removal, 912 studies were identified. Twenty fulfilled the inclusion criteria after the abstract screening. Two articles were added after a hand search of the reference list of included studies. After examination, nine RCTs were included in the qualitative analysis and five were considered to have a 'low' risk of bias. The overall risk difference in longevity between direct and indirect resin composite restorations in permanent posterior teeth (p>0.05) at five-year follow-up was 1.494 [0.893-2.500], and regardless of the type of tooth restored, that of molar and premolars was 0.716 [0.177-2.888] at three-year follow-up. Based on the findings, there was no difference in longevity of direct and indirect resin composite restorations regardless of the type of material and the restored tooth. Contemporary dentistry is based on minimally invasive restorations. Any indication of a less conservative technique must have unquestionable advantages. In vitro and in vivo studies reveal contradictory evidence of the clinical performance of direct and indirect resin composite restorations in posterior teeth. Thus this study clarified this doubt. Copyright © 2016 Elsevier Ltd. All rights reserved.

High Temperature Transfer Molding Resins Based on 2,3,3',4'-Biphenyltetracarboxylic Dianhydride

NASA Technical Reports Server (NTRS)

Smith, J. G., Jr.; Connell, J. W.; Hergenrother, P. M.; Yokota, R.; Criss, J. M.

2002-01-01

As part of an ongoing effort to develop materials for resin transfer molding (RTM) processes to fabricate high performance/high temperature composite structures, phenylethynyl containing imides have been under investigation. New phenylethynyl containing imide compositions were prepared using 2,3,3',4'-biphenyltetracarboxylic dianhydride (a-BPDA) and evaluated for cured glass transition temperature (Tg), melt flow behavior, and for processability into flat composite panels via RTM. The a-BPDA imparts a unique combination of properties that are desirable for high temperature transfer molding resins. In comparison to its symmetrical counterpart (i.e. 3,3',4,4'-biphenyltetracarboxylic dianhydride), a-BPDA affords oligomers with lower melt viscosities and when cured, higher Tgs. Several candidates exhibited the appropriate combination of properties such as a low and stable melt viscosity required for RTM processes, high cured Tg, and moderate toughness. The chemistry, physical, and composite properties of select resins will be discussed.

Correlation of shear and dielectric ion viscosity of dental resins - Influence of composition, temperature and filler content.

PubMed

Steinhaus, Johannes; Hausnerova, Berenika; Haenel, Thomas; Selig, Daniela; Duvenbeck, Fabian; Moeginger, Bernhard

2016-07-01

Shear viscosity and ion viscosity of uncured visible light-curing (VLC) resins and resin based composites (RBC) are correlated with respect to the resin composition, temperature and filler content to check where Dielectric Analysis (DEA) investigations of VLC RBC generate similar results as viscosity measurements. Mixtures of bisphenol A glycidyl methacrylate (Bis-GMA) and triethylene glycol dimethacrylate (TEGDMA) as well as the pure resins were investigated and compared with two commercial VLC dental resins and RBCs (VOCO, Arabesk Top and Grandio). Shear viscosity data was obtained using a Haake Mars III, Thermo Scientific. Ion viscosity measurements performed by a dielectric cure analyzer (DEA 231/1 Epsilon with Mini IDEX-Sensor, Netzsch-Gerätebau). Shear viscosity depends reciprocally on the mobility of molecules, whereas the ion viscosity also depends on the ion concentration as it is affected by both ion concentration and mixture viscosity. Except of pure TEGDMA, shear and ion viscosities depend on the resin composition qualitatively in a similar manner. Furthermore, shear and ion viscosities of the commercial VLC dental resins and composites exhibited the same temperature dependency regardless of filler content. Application of typical rheological models (Kitano and Quemada) revealed that ion viscosity measurements can be described with respect to filler contents of up to 30vol.%. Rheological behavior of a VLC RBC can be characterized by DEA under the condition that the ion concentration is kept constant. Both methods address the same physical phenomenon - motion of molecules. The proposed relations allows for calculating the viscosity of any Bis-GMA-TEGDMA mixture on the base of the viscosities of the pure components. This study demonstrated the applicability of DEA investigations of VLC RBCs with respect to quality assurance purposes. Copyright © 2016 The Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Two-year interfacial bond durability and nanoleakage of repaired silorane-based resin composite.

PubMed

Mobarak, E; El-Deeb, H

2013-01-01

To investigate the effect of silane primer application, intermediate adhesive agent/repair composite, and storage period on the interfacial microtensile bond strength (μTBS) of repaired silorane-based resin composite compared with unrepaired composites and on the nanoleakage. Forty-eight 1-month-old substrate specimens from Filtek P90 were roughened, etched, and distributed over two groups (n=24) based on receiving silane (Clearfil Ceramic Primer) or not. Then, half of the specimens (n=12) were repaired with P90 System Adhesive/Filtek P90 and the other half with Adper Scotchbond Multipurpose adhesive/Filtek Z250 resin composite. Within each repair category, repaired specimens were stored in artificial saliva at 37°C for either 24 hours (n=6) or two years before being serially sectioned into sticks (0.6 ± 0.01 mm(2)). From each specimen, two sticks were prepared for nanoleakage determination and four sticks were used for μTBS testing. Additional unrepaired specimens from each composite (n=12) were made to determine the cohesive strength at 24 hours and two years. Mean μTBS were calculated and statistically analyzed. Modes of failure were also determined. General linear model analysis revealed no significant effect for the silane priming, intermediate adhesive agent/repair composite, and storage period or for their interactions on the μTBS values of the repaired specimens. There was no significant difference between the cohesive strength of Filtek P90 and Filtek Z250; both were significantly higher than all repaired categories. At 24 hours, nanoleakage was not detected when silorane-based composite was repaired with the same material. However, after two years, all repair categories showed nanoleakage. Silane application has no effect on μTBS and nanoleakage. Durability of the interfacial bond of repaired silorane-based resin composite appeared successful regardless of the chemistry of the intermediate adhesive agent/composite used for repair. However, nanoleakage was detected early when a different repair intermediate adhesive agent/composite was used.

Self-healing of damage in fibre-reinforced polymer-matrix composites.

PubMed

Hayes, S A; Zhang, W; Branthwaite, M; Jones, F R

2007-04-22

Self-healing resin systems have been discussed for over a decade and four different technologies had been proposed. However, little work on their application as composite matrices has been published although this was one of the stated aims of the earliest work in the field. This paper reports on the optimization of a solid-state self-healing resin system and its subsequent use as a matrix for high volume fraction glass fibre-reinforced composites. The resin system was optimized using Charpy impact testing and repeated healing, while the efficiency of healing in composites was determined by analysing the growth of delaminations following repeated impacts with or without a healing cycle. To act as a reference, a non-healing resin system was subjected to the same treatments and the results are compared with the healable system. The optimized resin system displays a healing efficiency of 65% after the first healing cycle, dropping to 35 and 30% after the second and third healing cycles, respectively. Correction for any healability due to further curing showed that approximately 50% healing efficiency could be achieved with the bisphenol A-based epoxy resin containing 7.5% of polybisphenol-A-co-epichlorohydrin. The composite, on the other hand, displays a healing efficiency of approximately 30%. It is therefore clear that the solid-state self-healing system is capable of healing transverse cracks and delaminations in a composite, but that more work is needed to optimize matrix healing within a composite and to develop a methodology for assessing recovery in performance.

Effect of mechanical properties of fillers on the grindability of composite resin adhesives.

PubMed

Iijima, Masahiro; Muguruma, Takeshi; Brantley, William A; Yuasa, Toshihiro; Uechi, Jun; Mizoguchi, Itaru

2010-10-01

The purpose of this study was to investigate the effect of filler properties on the grindability of composite resin adhesives. Six composite resin products were selected: Transbond XT (3M Unitek, Monrovia, Calif), Transbond Plus (3M Unitek), Enlight (Ormco, Glendora, Calif), Kurasper F (Kuraray Medical, Tokyo, Japan), Beauty Ortho Bond (Shofu, Kyoto, Japan), and Beauty Ortho Bond Salivatect (Shofu). Compositions and weight fractions of fillers were determined by x-ray fluorescence analysis and ash test, respectively. The polished surface of each resin specimen was examined with a scanning electron microscope. Vickers hardness of plate specimens (15 × 10 × 3 mm) was measured, and nano-indentation was performed on large filler particles (>10 μm). Grindability for a low-speed tungsten-carbide bur was estimated. Data were compared with anlaysis of variance (ANOVA) and the Tukey multiple range test. Relationships among grindability, filler content, filler nano-indentation hardness (nano-hardness), filler elastic modulus, and Vickers hardness of the composite resins were investigated with the Pearson correlation coefficient test. Morphology and filler size of these adhesives showed great variations. The products could be divided into 2 groups, based on composition, which affected grindability. Vickers hardness of the adhesives did not correlate (r = 0.140) with filler nano-hardness, which showed a significant negative correlation (r = -0.664) with grindability. Filler nano-hardness greatly influences the grindability of composite resin adhesives. Copyright © 2010 American Association of Orthodontists. Published by Mosby, Inc. All rights reserved.

Influence of different staining beverages on color stability, surface roughness and microhardness of silorane and methacrylate-based composite resins.

PubMed

Karaman, Emel; Tuncer, Duygu; Firat, Esra; Ozdemir, Oguz Suleyman; Karahan, Sevilay

2014-05-01

To investigate the influence of different staining beverages on color stability, surface roughness and microhardness of silorane and methacrylate-based composite resins. Three different composite resins (Filtek Silorane, Filtek P60, Filtek Supreme XT) were tested. Thirty cylindrical specimens (10 × 2 mm) per material were prepared and polished with a series of aluminum-oxide polishing disks. Each group was then randomly subdivided into three groups according to the test beverages: distilled water (control), cola and coffee. The samples were immersed into different beverages for 15 days. Color, surface roughness and microhardness values were measured by a spectrophotometer, prophylometer and Vickers hardness device respectively, at baseline and after 15 days. The data were subjected to statistical analysis. Immersion in coffee resulted in a significant discoloration for all the composites tested, although the color change was lower in Filtek Silorane than that of MBCs (p < 0.05). All the composites tested showed similar surface roughness changes after immersion in different beverages (p > 0.05). Besides coffee caused more roughness change than others. Immersion in coffee caused highest microhardness change in Filtek Supreme XT (p < 0.05). Cola and coffee altered, to some degree, the color, surface roughness and/or microhardness of the tested resin composites, depending on the characteristics of the materials.

Nonequilibrium material effects on the behavior of polymeric composite matrices and their related composites

NASA Technical Reports Server (NTRS)

Wilkes, G. L.

1982-01-01

The effects of physical aging on the material properties of some linear and network macromolecular glasses are discussed. The free volume concept is used to describe this behavior. The effect of physical aging on properties of some uniaxial graphite/fiber epoxy resin composites is investigated using stress relaxation in both tensile and flexural modes. The matrix polymers used were resins both of which are based on a 4,4-methylenedianiline derivative of epichlorohydrin with diamino diphenyl sulfone (DDS) as the curing agent. The matrix resin, as used in the practical application in composites, not fully cured and the glass transition of the network was dependent on the curing schedule. The physical aging of the bulk crosslinked epoxy was found to depend on the annealing temperature, and the T sub g of the resin. The physical aging of the composite, monitored by the stress relaxation method, was found to be dependent on the testing direction.

Do Red-cockaded Woodpeckers Select Cavity Trees Based on Chemical Composition of Pine Resin?

Treesearch

Richard N. Conner; Robert H. Johnson; D. Craig Rudolph; Daniel Saenz

2003-01-01

We examined resin chemistry of loblolly (Pinus taeda) and shortleaf (P. echinata) pines selected as cavity trees by Red-cockaded Woodpeckers (Picoides borealis) in eastern Texas. We sampled resin from (1) pines selected by Red-cockaded Woodpeckers that contained naturally excavated active cavities, (2) pines...

DGEBF epoxy blends for use in the resin impregnation of extremely large composite parts

DOE PAGES

Madhukar, M. S.; Martovetsky, N. N.

2015-01-16

Large superconducting electromagnets used in fusion reactors utilize a large amount of glass/epoxy composite for electrical insulation and mechanical and thermal strengths. Moreover, the manufacture of these magnets involves wrapping each superconducting cable bundle with dry glass cloth followed by the vacuum-assisted resin transfer molding of the entire magnet. Due to their enormous size (more than 100 tons), it requires more than 40 h for resin impregnation and the subsequent pressure cycles to ensure complete impregnation and removal of any trapped air pockets. Diglycidyl ether of bisphenol F epoxy resin cross-linked with methyltetrahydrophthalic anhydride with an accelerator has been shownmore » to be a good candidate for use in composite parts requiring long impregnation cycles. Viscosity, gel time, and glass transition temperature of four resin-blends of diglycidyl ether of bisphenol F resin system were monitored as a function of time and temperature with an objective to find the blend that provides a working window longer than 40h at low viscosity without lowering its glass transition temperature. A resin-blend in the weight ratios of resin:hardener:accelerator=100:82:0.125 is shown to provide more than 60h at low resin viscosity while maintaining the same glass transition temperature as obtained with previously used resin-blends, based on the results.« less

Effect of surface treatments on the bond strengths of facing composite resins to zirconia copings.

PubMed

Tsumita, M; Kokubo, Y; Kano, T

2012-09-01

The present study evaluated and compared the bond strength between zirconia and facing composite resin using different surface conditioning methods before and after thermocycling. Four primers, three opaque resins, and two facing composite resins were used, and 10 surface treatment procedures were conducted. The bond strength was measured before and after 4,000 cycles of thermocycling. The mean values of each group were statistically analyzed using one-way analysis of variance (ANOVA). The bond strengths of facing composite resins to zirconia after various treatments varied depending on the primers, opaque resins, body resins, and thermocycling. The application of primers and opaque resins to the zirconia surface after sandblasting is expected to yield strong bond strength of the facing composite resin (Estenia CG&B) even after thermocycling.

Effect of Different Liners on Fracture Resistance of Premolars Restored with Conventional and Short Fiber-Reinforced Composite Resins.

PubMed

Shafiei, Fereshteh; Doozandeh, Maryam; Ghaffaripour, Dordaneh

2018-01-11

To see whether applying four different liners under short fiber-reinforced composite (SFRC), everX Posterior, compared to conventional composite resin, Z250, affected their strengthening property in premolar MOD cavities. Mesio-occluso-distal (MOD) cavities were prepared in 120 sound maxillary premolars divided into 10 groups (n = 12) in terms of two composite resin types and 4 liners or no liner. For each composite resin, in 5 groups no liner, resin-modified glass ionomer (RMGI), conventional flowable composite (COFL), self-adhesive flowable composite resin (SAFL), and self-adhesive resin cement (SARC) were applied prior to restoring incrementally. After water storage and thermocycling, static fracture resistance was tested. Data (in Newtons) were analyzed using two-way ANOVA (α = 0.05). Fracture resistance was significantly affected by composite resin type (p = 0.02), but not by the liner (p > 0.05). The interaction of the two factors was not statistically significant (p > 0.05). SFRC exhibited higher fracture strength (1470 ± 200 N) compared to conventional composite resin (1350 ± 290), irrespective of the application of liners. Application of SARC and SAFL liners led to a higher number of restorable fractures for both composite resins. The four liners can be used without interfering with the higher efficacy of SFRC, compared to conventional composite resins, to improve the fracture strength of premolar MOD cavities. © 2018 by the American College of Prosthodontists.

Dynamic measurement of local displacements within curing resin-based dental composite using optical coherence elastography

NASA Astrophysics Data System (ADS)

Tomlins, Peter H.; Rahman, Mohammed Wahidur; Donnan, Robert S.

2016-04-01

This study aimed to determine the feasibility of using optical coherence elastography to measure internal displacements during the curing phase of a light-activated, resin-based composite material. Displacement vectors were spatially mapped over time within a commercial dental composite. Measurements revealed that the orientation of cure-induced displacement vectors varied spatially in a complex manner; however, each vector showed a systematic evolution with time. Precision of individual displacements was estimated to be ˜1 to 2 μm, enabling submicrometer time-varying displacements to be detected.

[Studies on the dynamic durability of dental restorative materials. Part 4. Materials evaluation of initial and fatigue specimen for composite resins by acoustic emission method].

PubMed

Kondo, S; Okawa, S; Hanawa, T; Sugawara, T; Ota, M

1981-10-01

Present study is directed towards development for a method of materials evaluation of the static and dynamic properties for dental restorative materials and nondestructive inspection of the dental restorations in oral cavity by acoustic emission (AE) method. AE characteristics and deformation-fracture behavior of hour commercial composite resins under three points bending test are examined in order to evaluate initial and fatigue specimen for conventional and microfilled composite resins. Experimental results obtained are as follows: (1) Deformation-fracture behavior of conventional and microfilled composite resins exhibits different mode, corresponding to relatively brittle and ductile fracture behavior, respectively. Therefore, the primary sources of AE for conventional and microfilled composite resins under bending test are related mainly to the nucleation and propagation of cracks and plastic deformation, respectively. (2) In conventional composite resins under bending test, the burst type AE signal of higher amplitude and shorter decay time and more many AE total counts tend to be observed. In microfilled composite resins under bending test, the burst type AE signal of lower amplitude and longer decay time and more a few total counts tend to be observed. (3) Composite resins, particularly conventional composite resins under unload and repeated bending load are indicative of different AE characteristics. Accordingly, application of AE method for composite resins offers a method to evaluate the static and dynamic strength of composite resins. (4) In conventional composite resins under bending test, as characteristic AE are observed in a few stress regions before fracture, it may be possible to monitor nondestructively the restorations in oral cavity by using AE method.

Resin composite repair: Quantitative microleakage evaluation of resin-resin and resin-tooth interfaces with different surface treatments

PubMed Central

Celik, Cigdem; Cehreli, Sevi Burcak; Arhun, Neslihan

2015-01-01

Objective: The aim was to evaluate the effect of different adhesive systems and surface treatments on the integrity of resin-resin and resin-tooth interfaces after partial removal of preexisting resin composites using quantitative image analysis for microleakage testing protocol. Materials and Methods: A total of 80 human molar teeth were restored with either of the resin composites (Filtek Z250/GrandioSO) occlusally. The teeth were thermocycled (1000×). Mesial and distal 1/3 parts of the restorations were removed out leaving only middle part. One side of the cavity was finished with course diamond bur and the other was air-abraded with 50 μm Al2O3. They were randomly divided into four groups (n = 10) to receive: Group 1: Adper Single Bond 2; Group 2: All Bond 3; Group 3: ClearfilSE; Group 4: BeautiBond, before being repaired with the same resin composite (Filtek Z250). The specimens were re-thermocycled (1000×), sealed with nail varnish, stained with 0.5% basic fuchsin, sectioned mesiodistally and photographed digitally. The extent of dye penetration was measured by image analysis software (ImageJ) for both bur-finished and air-abraded surfaces at resin-tooth and resin-resin interfaces. The data were analyzed statistically. Results: BeautiBond exhibited the most microleakage at every site. Irrespective of adhesive and initial composite type, air-abrasion showed less microleakage except for BeautiBond. The type of initial repaired restorative material did not affect the microleakage. BeautiBond adhesive may not be preferred in resin composite repair in terms of microleakage prevention. Conclusions: Surface treatment with air-abrasion produced the lowest microleakage scores, independent of the adhesive systems and the pre-existing resin composite type. Pre-existing composite type does not affect the microleakage issue. All-in-one adhesive resin (BeautiBond) may not be preferred in resin composite repair in terms of microleakage prevention. PMID:25713491

Color change of composite resins subjected to accelerated artificial aging.

PubMed

Tornavoi, Denise Cremonezzi; Agnelli, José Augusto Marcondes; Panzeri, Heitor; Dos Reis, Andréa Cândido

2013-01-01

The aim of this study was to evaluate the influence of accelerated artificial aging (AAA) on the color change of composite resins used in dentistry. Three composite resins were evaluated: Two microhybrids and one hybrid of higher viscosity, with different amounts and sizes of filler particles, shades C2 and B2. A total of 54 specimens were obtained (18 for each composite resin), made of a Teflon matrix (15 mm in diameter and 2 mm in height). The color measurements were obtained with a Spectrophotometer, (PCB 6807 BYK Gardner) before and after AAA. Data were submitted to the Kolmogorov-Smirnov test (α >0.05), ANOVA and Tukey test (α <0.05). After statistical analysis, the color difference among composite resins with the same shades was analyzed. All composite resins showed unacceptable color changes after AAA (ΔE > 3). Considering the variable ∆E, it was observed that the color tone C2 was already statistically different for the microhybrid composite resin prior to AAA (P < 0.05) and in shade B2 for hybrid of higher viscosity and microhybrid with barium glass fluoride aluminum and silica dioxide (P < 0.01). After this process, a statistically significant difference was observed only for shade B2 between microhybrid composite resins (P < 0.01) and for hybrid of higher viscosity and microhybrid with barium glass fluoride aluminum and silica dioxide (P < 0.05). Regarding the color difference within a same composite resin group, before aging the composite resin hybrid of higher viscosity B2 showed the highest color variation rate and microhybrid with zirconium/silica C2 showed the lowest. All composite resins presented unacceptable color changes after 382 h of aging and different composite resins with same hue, presented different colors before being subjected to the aging process (B2 and C2) and after (B2). It was also observed color difference within a group of the same composite resin and same hue.

Polymerization Behavior and Mechanical Properties of High-Viscosity Bulk Fill and Low Shrinkage Resin Composites.

PubMed

Shibasaki, S; Takamizawa, T; Nojiri, K; Imai, A; Tsujimoto, A; Endo, H; Suzuki, S; Suda, S; Barkmeier, W W; Latta, M A; Miyazaki, M

The present study determined the mechanical properties and volumetric polymerization shrinkage of different categories of resin composite. Three high viscosity bulk fill resin composites were tested: Tetric EvoCeram Bulk Fill (TB, Ivoclar Vivadent), Filtek Bulk Fill posterior restorative (FB, 3M ESPE), and Sonic Fill (SF, Kerr Corp). Two low-shrinkage resin composites, Kalore (KL, GC Corp) and Filtek LS Posterior (LS, 3M ESPE), were used. Three conventional resin composites, Herculite Ultra (HU, Kerr Corp), Estelite ∑ Quick (EQ, Tokuyama Dental), and Filtek Supreme Ultra (SU, 3M ESPE), were used as comparison materials. Following ISO Specification 4049, six specimens for each resin composite were used to determine flexural strength, elastic modulus, and resilience. Volumetric polymerization shrinkage was determined using a water-filled dilatometer. Data were evaluated using analysis of variance followed by Tukey's honestly significant difference test (α=0.05). The flexural strength of the resin composites ranged from 115.4 to 148.1 MPa, the elastic modulus ranged from 5.6 to 13.4 GPa, and the resilience ranged from 0.70 to 1.0 MJ/m 3 . There were significant differences in flexural properties between the materials but no clear outliers. Volumetric changes as a function of time over a duration of 180 seconds depended on the type of resin composite. However, for all the resin composites, apart from LS, volumetric shrinkage began soon after the start of light irradiation, and a rapid decrease in volume during light irradiation followed by a slower decrease was observed. The low shrinkage resin composites KL and LS showed significantly lower volumetric shrinkage than the other tested materials at the measuring point of 180 seconds. In contrast, the three bulk fill resin composites showed higher volumetric change than the other resin composites. The findings from this study provide clinicians with valuable information regarding the mechanical properties and polymerization kinetics of these categories of current resin composite.

Bioinspired Catecholic Primers for Rigid and Ductile Dental Resin Composites.

PubMed

Shin, Eeseul; Ju, Sung Won; An, Larry; Ahn, Eungjin; Ahn, Jin-Soo; Kim, Byeong-Su; Ahn, B Kollbe

2018-01-17

In the construction of dental restorative polymer composite materials, surface priming on mineral fillers is essential to improve the mechanical performance of the composites. Here we present bioinspired catechol-functionalized primers for a tougher dental resin composite containing glass fillers. The catecholic primers with different polymerizable end groups were designed and then coated on glass surfaces using a simple drop-casting or dip-coating process. The surface binding ability and possible cross-linking (coupling or chemical bridging between the glass substrate and the dental resin) of the catecholic bifunctional primers were evaluated using atomic force microscopy, contact angle measurements, and the knife shear bonding test and compared to a state-of-the-art silane-based coupling agent. Various mechanical tests including shrinkage and compression tests of the dental resin composites were also conducted. Compression tests of the composites containing the catecholic primed fillers exhibited enhanced mechanical properties, owing to the bidentate hydrogen bonding of catechol moieties to the oxide mineral surface. Furthermore, the superior biocompatibility of the primed surface was confirmed via cell attachment assay, thus providing applicability of catecholic primers for practical dental and biomedical applications.

Mechanical characterization of composite repairs for fiberglass wind turbine blades

NASA Astrophysics Data System (ADS)

Chawla, Tanveer Singh

While in service, wind turbine blades experience various modes of loading. An example is impact loading in the form of hail or bird strikes, which might lead to localized damage or formation of cracks a few plies deep on the blade surface. One of the methods to conduct repairs on wind turbine blades that are damaged while in service is hand lay-up of the repair part after grinding out the damaged portion and some of its surrounding area. The resin used for such repairs usually differs from the parent plate resin in composition and properties such as gel time, viscosity, etc. As a result the properties of the repaired parts are not the same as that of the undamaged blades. Subsequent repetitive loading can be detrimental to weak repairs to such an extent so as to cause delamination at the parent-repair bondline causing the repairs to eventually fall off the blade. Thus the strength and toughness of the repair are of critical importance. Initial part of this work consists of an effort to increase repair strength by identifying an optimum hand layup repair resin for fiberglass wind turbine blades currently being manufactured by a global company. As delamination of the repair from the parent blade is a major concern and unidirectional glass fibers along with a polymer resin are used to manufacture blades under consideration, testing method detailed in ASTM D 5528 (Test Method for Mode I Interlaminar Fracture Toughness of Unidirectional Fiber-Reinforced Polymer Matrix Composites) was followed to determine propagation fracture toughness values of the prospective vinyl ester repair resin candidates. These values were compared to those for a base polyester repair resin used by the company. Experimental procedure and results obtained from the above mentioned testing using double cantilever beam (DCB) specimens are detailed. Three new repair resins were shortlisted through mode I testing. It was also found that variation in the depth of the ground top ply of the parent part affects the propagation fracture toughness values of the repair. Repairs conducted on surfaces with partially ground top plies possess higher fracture toughness values than those conducted on surfaces with complete top plies ground off. The three top repair resin candidates were then evaluated against the base repair resin under fatigue loading. The specimen configuration and testing method were chosen so as to be able to test hand layup repairs under tension -- tension cyclic loading. It was observed that all three new repair resins perform better than the base repair resin. The selection of the optimum repair resin was based on results from mode I and fatigue testing. Global manufacturing regulations and standards were also of prime concern. The final new repair resin is being used by the company in all of its plants over the globe. The balance of this work involves study of the effect of mixed mode I -- mode II loading on the strength of repairs conducted on fiber reinforced composite parts using hand lay-up technique. The specimens for this part were similar to those manufactured for mode I testing but with different dimensions and layup. They were made and tested in accordance with ASTM D 6671 (Standard Test Method for Mixed Mode I -- Mode II Interlaminar Fracture Toughness of Unidirectional Fiber Reinforced Polymer Matrix Composites). Comparison was made between the fracture toughness of the above chosen optimum repair resin and the base repair resin. At least two levels of mode mixture GII/G (Mode II fracture toughness / Mode I and II fracture toughness) were examined. Also, two levels of grinding were considered (complete ply vs. partial ply ground off) in order to establish the influence of varying top-ply grinding depths on the strength of hand layup repairs conducted on fiberglass composite structures. The results of this work have the potential to improve the repair process for current fiberglass wind turbine blades.

In-situ measurement of thermoset resin degree of cure using embedded fiber optic

NASA Astrophysics Data System (ADS)

Breglio, Giovanni; Cusano, Andrea; Cutolo, Antonello; Calabro, Antonio M.; Cantoni, Stefania; Di Vita, Gandolfo; Buonocore, Vincenzo; Giordano, Michele; Nicolais, Luigi, II

1999-12-01

In this work, a fiber optic sensor based on Fresnel principle is presented. It is used to monitor the variations of the refractive index due to the cure process of an epoxy based resin. These materials are widely used in polymer- matrix composites. The process of thermoset matrix based composite involves mass and heat transfer coupled with irreversible chemical reactions inducing physical changes: the transformation of a fluid resin into a rubber and then into a solid glass. To improve the quality and the reliability of these materials key points are the cure monitoring and the optimization of the manufacturing process. To this aim, the fiber optic embedded sensor has been designed, developed and tested. Preliminary results on sensor capability to monitor the cure kinetics are shown. Correlation between the sensor output and conversion advancement has been proposed following the Lorentz-Lorenz law. Isothermal data form the sensor have been compared with calorimetric analysis of an epoxy based resin.

[Dental plaque microcosm biofilm behavior on a resin composite incorporated with nano-antibacterial inorganic filler containing long-chain alkyl quaternary ammonium salt].

PubMed

Junling, Wu; Qiang, Zhang; Ruinan, Sun; Ting, Zhu; Jianhua, Ge; Chuanjian, Zhou

2015-12-01

To develop a resin composite incorporated with nano-antibacterial inorganic filler containing long-chain alkyl quaternary ammonium salt, and to measure its effect on human dental plaque microcosm biofilm. A novel nano-antibacterial inorganic filler containing long-chain alkyl quaternary ammonium salt was synthesized according to methods introduced in previous research. Samples of the novel nano-antibacterial inorganic fillers were modified by a coupling agent and then added into resin composite at 0%, 5%, 10%, 15% or 20% mass fractions; 0% composite was used as control. A flexural test was used to measure resin composite mechanical properties. Results showed that a dental plaque microcosm biofilm model with human saliva as inoculum was formed. Colony-forming unit (CFU) counts, lactic acid production, and live/dead assay of biofilm on the resin composite were calculated to test the effect of the resin composite on human dental plaque microcosm biofilm. The incorporation of nano-antibacterial inorganic fillers with as much as 15% concentration into the resin composite showed no adverse effect on the mechanical properties of the resin composite (P > 0.05). Resin composite containing 5% or more nano-antibacterial inorganic fillers significantly inhibited the metabolic activity of dental plaque microcosm biofilm, suggesting its strong antibacterial potency (P < 0.05). This novel resin composite exhibited a strong antibacterial property upon the addition of up to 5% nano-antibacterial inorganic fillers, thereby leading to effective caries inhibition in dental application.

Minimally Invasive Dentistry: A Conservative Approach to Smile Makeover.

PubMed

Rosenberg, Jeffrey M

2017-01-01

The concept of minimally invasive dentistry is based on preserving tooth structure, especially enamel. A conservative method to treat discolored teeth that have diastemas is a freehand additive technique using composite resin. While selecting the correct shade of resin can be challenging, newer composite resin formulations are being developed with optical properties that enable the material to more effectively blend into the dentition. This case report describes the use of conservative approaches and materials to treat discolored, unevenly spaced teeth and restore harmony and balance to a patient's smile.

Biphenyl liquid crystalline epoxy resin as a low-shrinkage resin-based dental restorative nanocomposite.

PubMed

Hsu, Sheng-Hao; Chen, Rung-Shu; Chang, Yuan-Ling; Chen, Min-Huey; Cheng, Kuo-Chung; Su, Wei-Fang

2012-11-01

Low-shrinkage resin-based photocurable liquid crystalline epoxy nanocomposite has been investigated with regard to its application as a dental restoration material. The nanocomposite consists of an organic matrix and an inorganic reinforcing filler. The organic matrix is made of liquid crystalline biphenyl epoxy resin (BP), an epoxy resin consisting of cyclohexylmethyl-3,4-epoxycyclohexanecarboxylate (ECH), the photoinitiator 4-octylphenyl phenyliodonium hexafluoroantimonate and the photosensitizer champhorquinone. The inorganic filler is silica nanoparticles (∼70-100 nm). The nanoparticles were modified by an epoxy silane of γ-glycidoxypropyltrimethoxysilane to be compatible with the organic matrix and to chemically bond with the organic matrix after photo curing. By incorporating the BP liquid crystalline (LC) epoxy resin into conventional ECH epoxy resin, the nanocomposite has improved hardness, flexural modulus, water absorption and coefficient of thermal expansion. Although the incorporation of silica filler may dilute the reinforcing effect of crystalline BP, a high silica filler content (∼42 vol.%) was found to increase the physical and chemical properties of the nanocomposite due to the formation of unique microstructures. The microstructure of nanoparticle embedded layers was observed in the nanocomposite using scanning and transmission electron microscopy. This unique microstructure indicates that the crystalline BP and nanoparticles support each other and result in outstanding mechanical properties. The crystalline BP in the LC epoxy resin-based nanocomposite was partially melted during exothermic photopolymerization, and the resin expanded via an order-to-disorder transition. Thus, the post-gelation shrinkage of the LC epoxy resin-based nanocomposite is greatly reduced, ∼50.6% less than in commercialized methacrylate resin-based composites. This LC epoxy nanocomposite demonstrates good physical and chemical properties and good biocompatibility, comparable to commercialized composites. The results indicate that this novel LC nanocomposite is worthy of development and has potential for further applications in clinical dentistry. Copyright © 2012 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

Shear Bond Strength between Fiber-Reinforced Composite and Veneering Resin Composites with Various Adhesive Resin Systems.

PubMed

AlJehani, Yousef A; Baskaradoss, Jagan K; Geevarghese, Amrita; AlShehry, Marey A; Vallittu, Pekka K

2016-07-01

The aim of this research was to evaluate the shear bond strength of different laboratory resin composites bonded to a fiber-reinforced composite substrate with some intermediate adhesive resins. Mounted test specimens of a bidirectional continuous fiber-reinforced substrate (StickNet) were randomly assigned to three equal groups. Three types of commercially available veneering resin composites - BelleGlass®, Sinfony®, and GC Gradia® were bonded to these specimens using four different adhesive resins. Half the specimens per group were stored for 24 hours; the remaining were stored for 30 days. There were 10 specimens in the test group (n). The shear bond strengths were calculated and expressed in MPa. Data were analyzed statistically, and variations in bond strength within each group were additionally evaluated by calculating the Weibull modulus. Shear bond values of those composites are influenced by the different bonding resins and different indirect composites. There was a significant difference in the shear bond strengths using different types of adhesive resins (p = 0.02) and using different veneering composites (p < 0.01). Belle-Glass® had the highest mean shear bond strength when bonded to StickNet substrate using both Prime & Bond NT and OptiBond Solo Plus. Sinfony® composite resin exhibited the lowest shear bond strength values when used with the same adhesive resins. The adhesive mode of failure was higher than cohesive with all laboratory composite resins bonded to the StickNet substructure at both storage times. Water storage had a tendency to lower the bond strengths of all laboratory composites, although the statistical differences were not significant. Within the limitations of this study, it was found that bonding of the veneering composite to bidirectional continuous fiber-reinforced substrate is influenced by the brand of the adhesive resin and veneering composite. © 2015 by the American College of Prosthodontists.

Characterization of PMR-15 polyimide composition in thermo-oxidatively exposed graphite fiber composites

NASA Technical Reports Server (NTRS)

Alston, W. B.

1980-01-01

The contributions of individual resin components to total resin weight loss in 600 F air aged Celion 6000/PMR-15 polyimide composites were determined from the overall resin weight loss in the composite by chemically separating the PMR-15 matrix resin into its monomeric components. The individual resin components were also analyzed by spectroscopic techniques in order to elucidate curing and degradation mechanisms of the PMR-15 matrix resin. The isothermal weight loss of the individual resin components during prolonged 600 F thermo-oxidative aging of the composite was correlated to the changes observed in the Fourier Transform infrared spectra and Fourier Transform nuclear magnetic resonance spectra of the individual resin components. The correlation was used to identify the molecular site of the thermo-oxidative changes in PMR-15 polyimide matrix resin during 600 F curing the prolonged 600 F thermo-oxidative aging.

Comparison of microleakage of three acid-base luting cements versus one resin-bonded cement for Class V direct composite inlays.

PubMed

Piemjai, Morakot; Miyasaka, Kumiko; Iwasaki, Yasuhiko; Nakabayashi, Nobuo

2002-12-01

Demineralized dentin beneath set cement may adversely affect microleakage under fixed restorations. Microleakage of direct composite inlays cemented with acid-base cements and a methyl methacrylate resin cement were evaluated to determine their effect on the integrity of the underlying hybridized dentin. Sixty Class V box preparations (3 mm x 3 mm x 1.5 mm) were precisely prepared in previously frozen bovine teeth with one margin in enamel and another margin in dentin. Direct composite inlays (EPIC-TMPT) for each preparation were divided into 4 groups of 15 specimens each and cemented with 3 acid-base cements (control group): Elite, Ketac-Cem, Hy-Bond Carbo-Cem, and 1 adhesive resin cement: C&B Metabond. All specimens were stored in distilled water for 24 hours at 37 degrees C before immersion in 0.5% basic fuchsin for 24 hours. The dye penetration was measured on the sectioned specimens at the tooth-cement interface of enamel and cementum margins and recorded with graded criteria under light microscopy (Olympus Vanox-T) at original magnification x 50, 100, and 200. A Kruskal-Wallis and the Mann-Whitney test at P<.05 were used to analyze leakage score. All cementum margins of the 3 acid-base cements tested demonstrated significantly higher leakage scores than cementum margins for inlays cemented with the resin cement tested(P<.01). No leakage along the tooth-cement interface was found for inlays retained with the adhesive resin cement. Within the limitations of this study, the 3 acid-base cements tested exhibited greater microleakage at the cementum margins than did the adhesive resin cement that was tested.

PETI-298 Prepared by Microwave Synthesis: Neat Resin and Composite Properties

NASA Technical Reports Server (NTRS)

Smith, Joseph G.; Connell, John W.; Li, Chao-Jun; Wu, Wei; Criss, Jim M., Jr.

2004-01-01

PETI-298 is a high temperature/high performance matrix resin that is processable into composites by resin transfer molding (RTM), resin infusion and vacuum assisted RTM techniques. It is typically synthesized in a polar aprotic solvent from the reaction of an aromatic anhydride and a combination of diamines and endcapped with phenylethynylphthalic anhydride. Microwave synthesis of PETI-298 was investigated as a means to eliminate solvent and decrease reaction time. The monomers were manually mixed and placed in a microwave oven for various times to determine optimum reaction conditions. The synthetic process was subsequently scaled-up to 330g. Three batches were synthesized and combined to give 1 kg of material that was characterized for thermal and rheological properties and compared to PETI-298 prepared by the classic solution based synthetic method. The microwave synthesized PETI-298 was subsequently used to fabricate flat laminates on T650 carbon fabric by RTM. The composite panels were analyzed and mechanical properties determined and compared with those fabricated from PETI-298 prepared by the classic solution method. The microwave synthesis process and characterization of neat resin and carbon fiber reinforced composites fabricated by RTM will be presented. KEY WORDS: Resin Transfer Molding, High Temperature Polymers, Phenylethynyl Terminated Imides, Microwave Synthesis

The effects of different opacifiers on the translucency of experimental dental composite resins.

PubMed

Haas, Karine; Azhar, Gulelala; Wood, Duncan J; Moharamzadeh, Keyvan; van Noort, Richard

2017-08-01

The aim of this study was to evaluate the effects of different opacifiers on the translucency of experimental dental composite-resins. Three metal oxides that are used as opacifiers were tested in this study: titanium oxide (TiO 2 ), aluminium oxide (Al 2 O 3 ) and zirconium oxide (ZrO 2 ). Experimental composite-resins were fabricated containing 25wt.% urethane dimethacrylate (UDMA)-based resin matrix and 75% total filler including different concentrations of metal oxides (0, 0.25, 0.5, 0.75 and 1wt.%) blended into silane treated barium-silicate filler. The specimens (15.5mm diameter and 1mm thickness) were light-cured and tested in the transmittance mode using a UV/VIS spectrophotometer at wavelengths from 380 to 700nm under a standard illuminant D65. The color differences (ΔE* ab) between different concentrations of opacifiers were also measured in transmittance mode based on their Lab values. Statistical analysis by ANOVA and Tukey's test showed a significant decrease (p<0.05) in light transmittance with the addition of opacifiers to the experimental composite-resins. There was a linear correlation between different concentrations of TiO 2 and Al 2 O 3 and total transmittance. Total transmittance was also found to be wavelength dependent. The color differences for the concentrations of 0-1wt.% of the opacifiers were above 1 ΔE* unit, with Al 2 O 3 showing the smallest color shift. The type and the amount of the opacifiers used in this study had a significant effect on the translucency of the experimental UDMA-based dental composite resins. The most effective opacifier was TiO 2 , followed by ZrO 2 and Al 2 O 3 in decreasing order, respectively. Copyright © 2017 The Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Grinding efficiency of abutment tooth with both dentin and core composite resin on axial plane.

PubMed

Miho, Otoaki; Sato, Toru; Matsukubo, Takashi

2015-01-01

The purpose of this study was to evaluate grinding efficiency in abutment teeth comprising both dentin and core composite resin in the axial plane. Grinding was performed over 5 runs at two loads (0.5 or 0.25 N) and two feed rates (1 or 2 mm/sec). The grinding surface was observed with a 3-D laser microscope. Tomographic images of the grinding surfaces captured perpendicular to the feed direction were also analyzed. Using a non-ground surface as a reference, areas comprising only dentin, both dentin and core composite resin, or only core composite resin were analyzed to determine the angle of the grinding surface. Composite resins were subjected to the Vickers hardness test and scanning electron microscopy. Data were statistically analyzed using a one-way analysis of variance and multiple comparison tests. Multiple regression analysis was performed for load, feed rate, and Vickers hardness of the build-up material depending on number of runs. When grinding was performed at a constant load and feed rate, a greater grinding angle was observed in areas comprising both dentin and composite resin or only composite resin than in areas consisting of dentin alone. A correlation was found between machinability and load or feed rate in areas comprising both dentin and composite resin or composite resin alone, with a particularly high correlation being observed between machinability and load. These results suggest that great caution should be exercised in a clinical setting when the boundary between the dentin and composite resin is to be ground, as the angle of the grinding surface changes when the rotating diamond point begins grinding the composite resin.

Processing and Characterization of PETI Composites Fabricated by High Temperature VARTM

NASA Technical Reports Server (NTRS)

Ghose, Sayata; Cano, Roberto J.; Watson, Kent A.; Britton, Sean M.; Jensen, Brian J.; Connell, John W.; Smith, Joseph G.; Loos, Alfred C.; Heider, Dirk

2011-01-01

The use of composites as primary structures on aerospace vehicles has increased dramatically over the past decade. As these advanced structures increase in size and complexity, their production costs have grown significantly. A major contributor to these manufacturing costs is the requirement of elevated processing pressures, during the thermal cure, to create fully consolidated composites. For certain composite parts, high temperature vacuum assisted resin transfer molding (HT-VARTM) can offer reduced fabrication costs compared to conventional autoclave techniques. The process has been successfully used with phenylethynyl terminated imide (PETI) resins developed by NASA LaRC. In the current study, two PETI resins, LARC(TradeMark) PETI-330 and LARC(TradeMark) PETI-8 have been used to make test specimens using HT-VARTM. Based on previous work at NASA LaRC, larger panels with a quasi-isotropic lay-up were fabricated. The resultant composite specimens exhibited void contents <3% by volume depending on the type of carbon fabric preform used. Mechanical properties of the panels were determined at both room and elevated temperatures. These included open-hole compressive (OHC) and short beam shear (SBS) properties. Limited process modeling efforts were carried out including infusion times, composite panel size limitations and fabric permeability characterization. Work has also been carried out to develop new PETI based resins specifically geared towards HT-VARTM. The results of this work are presented herein.

Properties of radiation stable, low viscosity impregnating resin for cryogenic insulation system

NASA Astrophysics Data System (ADS)

Wu, Zhixiong; Zhang, Hao; Yang, Huihui; Chu, Xinxin; Song, Yuntao; Wu, Weiyue; Liu, Huajun; Li, Laifeng

2011-06-01

Impregnating resins in fusion magnet technology are required to be radiation stable, low viscosity, long usable life and high toughness. To meet these objectives, we developed a new epoxy based composite which consists of triglycidyl-p-aminophenol (TGPAP) epoxy resin and isopropylidenebisphenol bis[(2-glycidyloxy-3-n-butoxy)-1-propylether] (IPBE). The ratio of TGPAP to IPBE can be varied to achieve desired viscosity and working time. The boron-free glass fiber reinforced composites were prepared by vacuum pressure impregnation. The radiation resistance was evaluated by 60Co γ-ray irradiation of 1 MGy at ambient temperature. The mechanical properties of the composites have been measured at room temperature and at 77 K.

Clinical Evaluation of Indirect Particle-Filled Composite Resin CAD/CAM Partial Crowns after 24 Months.

PubMed

Zimmermann, Moritz; Koller, Christina; Reymus, Marcel; Mehl, Albert; Hickel, Reinhard

2017-04-19

Resin-based CAD/CAM compound materials might be promising for single-tooth restorations. Insufficient clinical data are available for this new material class. The purpose of this study was to describe initial clinical in vivo results for indirect particle-filled composite resin CAD/CAM restorations after 24 months. Indirect particle-filled composite resin restorations were fabricated with a CAD/CAM method (CEREC Bluecam intraoral scanner, CEREC MCXL milling unit) by calibrated dental students. Forty-two partial crown restorations were seated adhesively in 30 patients with caries lesions or insufficient restorations (baseline). Strict inclusion criteria were defined for the patient collective. Follow-up evaluation comprised 40 restorations after 12 months and 33 restorations after 24 months. Evaluation criteria were modified FDI criteria with grades (1) to (5). Rating with FDI criteria (5) was defined as clinical failure. Statistical analysis was performed with Wilcoxon-Test (p < 0.05). The success rate of indirect particle-filled composite resin CAD/CAM restorations after 12 months was 95.0% with two debondings observed. The cumulative success rate for indirect particle-filled composite resin CAD/CAM restorations after 24 months was 85.7% with two tooth fractures and one debonding. Statistically significant differences were found for baseline and 24-month follow-up evaluation for anatomic form and marginal adaptation criterion examined in respect to FDI criteria guidelines (Wilcoxon-Test, p < 0.05). This study demonstrates particle-filled composite resin CAD/CAM restorations having a clinical success rate of 85.7% after 24 months. Adhesive bonding procedures need to be ensured carefully. A longer clinical evaluation period is necessary to draw further conclusions. © 2017 by the American College of Prosthodontists.

Fatigue Resistance of CAD/CAM Resin Composite Molar Crowns

PubMed Central

Shembish, Fatma A.; Tong, Hui; Kaizer, Marina; Janal, Malvin N.; Thompson, Van P.; Opdam, Niek J.; Zhang, Yu

2016-01-01

Objective To demonstrate the fatigue behavior of CAD/CAM resin composite molar crowns using a mouth-motion step-stress fatigue test. Monolithic leucite-reinforced glass-ceramic crowns were used as a reference. Methods Fully anatomically shaped monolithic resin composite molar crowns (Lava Ultimate, n = 24) and leucite reinforced glass-ceramic crowns (IPS Empress CAD, n = 24) were fabricated using CAD/CAM systems. Crowns were cemented on aged dentin-like resin composite tooth replicas (Filtek Z100) with resin-based cements (RelyX Ultimate for Lava Ultimate or Multilink Automix for IPS Empress). Three step-stress profiles (aggressive, moderate and mild) were employed for the accelerated sliding-contact mouth-motion fatigue test. Twenty one crowns from each group were randomly distributed among these three profiles (1:2:4). Failure was designated as chip-off or bulk fracture. Optical and electronic microscopes were used to examine the occlusal surface and subsurface damages, as well as the material microstructures. Results The resin composite crowns showed only minor occlusal damage during mouth-motion step-stress fatigue loading up to 1700 N. Cross-sectional views revealed contact-induced cone cracks in all specimens, and flexural radial cracks in 2 crowns. Both cone and radial cracks were relatively small compared to the crown thickness. Extending these cracks to the threshold for catastrophic failure would require much higher indentation loads or more loading cycles. In contrast, all of the glass-ceramic crowns fractured, starting at loads of approximately 450 N. Significance Monolithic CAD/CAM resin composite crowns endure, with only superficial damage, fatigue loads 3 – 4 times higher than those causing catastrophic failure in glass-ceramic CAD crowns. PMID:26777092

Effect of sealant agents on the color stability and surface roughness of nanohybrid composite resins.

PubMed

Dede, Doğu Ömür; Şahin, Onur; Koroglu, Aysegül; Yilmaz, Burak

2016-07-01

The effect of sealant agents on the surface roughness and color stability of nanohybrid composite resins is unknown. The purpose of this in vitro study was to evaluate the effect of sealant agents on the surface roughness and color stability of 4 nanohybrid composite resin materials. Forty disks (10×2 mm) were fabricated for each nanohybrid composite resin material (Z-550, Tetric EvoCeram, Clearfill Majesty, Ice) (N=160) and divided into 4 surface treatment groups: 1 conventional polishing (control) and 3 different sealant agent (Palaseal, Optiglaze, BisCover) coupling groups (n=10). The specimens were thermocycled, and surface roughness (Ra) values were obtained with a profilometer. Scanning electron microscope images were also recorded. CIELab color parameters of each specimen were measured with a spectrophotometer before and after 7 days of storage in a coffee solution. Color differences were calculated by the CIEDE 2000 (ΔE00) formula. The data were statistically analyzed by 2-way ANOVA and by the Tukey HSD test (α=.05). The surface treatment technique significantly affected the Ra values of the composite resins tested (P<.001). The interaction between the surface treatment technique and composite resin material was also significant for ΔE00 values (P<.05). Within the composite resin groups, significant decreases in Ra were observed only for the Palaseal agent coupled composite resin groups (except Ice) compared with the control groups (P<.05). Scanning electron microscope images revealed rougher surfaces with conventionally polished groups compared with test groups. Conventionally polished groups had the highest ΔE00 (3.09 to 3.49) values for each composite resin group, except for BisCover applied Clearfill Majesty (P<.05). Within the composite resin groups, significant differences were observed between the color change seen with BisCover and other sealants for Clearfill Majesty composite resin (P<.05). Using Palaseal agent on all tested composite resins except for Ice produced smoother surfaces. All surface sealant agents provided less discoloration of nanohybrid composite resins after coffee staining compared with conventional polishing except for BisCover applied Clearfill Majesty composite resin. Copyright © 2016 Editorial Council for the Journal of Prosthetic Dentistry. Published by Elsevier Inc. All rights reserved.

Fluorinated Alkyl Ether Epoxy Resin Compositions and Applications Thereof

NASA Technical Reports Server (NTRS)

Connell, John W. (Inventor); Wohl, Christopher J. (Inventor); Siochi, Emilie J. (Inventor); Gardner, John M. (Inventor); Smith, Joseph G. (Inventor); Palmieri, Frank M. (Inventor)

2017-01-01

Epoxy resin compositions prepared using amino terminated fluoro alkyl ethers. The epoxy resin compositions exhibit low surface adhesion properties making them useful as coatings, paints, moldings, adhesives, and fiber reinforced composites.

Bond Strength of Silorane- and Methacrylate-Based Composites to Resin-Modified Glass Ionomers

DTIC Science & Technology

2012-01-13

genre was given the name of resin-modified glass ionomers (RMGI) (Antonucci et al., 1988). The addition of resin improved many of the drawbacks of...entire surface for 15 seconds then gentle air was used to create an even film over the sample. This layer was cured for 10 seconds using the Bluephase

Incorporation of antimicrobial macromolecules in acrylic denture base resins: a research composition and update.

PubMed

Sivakumar, Indumathi; Arunachalam, Kuthalingam Subbiah; Sajjan, Suresh; Ramaraju, Alluri Venkata; Rao, Bheemalingeshwara; Kamaraj, Bindu

2014-06-01

Contemporary research in acrylic denture base materials focuses on the development of a novel poly(methyl methacrylate) (PMMA) resin with antimicrobial properties. Although PMMA resin has fulfilled all the requirements of an ideal denture base material, its susceptibility to microbial colonization in the oral environment is a formidable concern to clinicians. Many mechanisms including the absence of ionic charge in the methyl methacrylate resins, hydrophobic interactions, electrostatic interactions, and mechanical attachment have been found to contribute to the formation of biofilm. The present article outlines the basic categories of potential antimicrobial polymer (polymeric biocides) formulations (modified PMMA resins) and considers their applicability, biological status, and usage potential over the coming years. © 2013 by the American College of Prosthodontists.

Design Guide: Designing and Building High Voltage Power Supplies. Volume 2

DTIC Science & Technology

1988-08-01

and edges. * Isolation system: * One layer ol’ Tedlar: or type 120 glass fabric with a compatible resin : or finish. 199 5.4.2 Composite Joints...plastics Cellulose esters Asphalt Cork Chloride flux Epoxy resins Copper (bare) Masonite Fiber board Melamine resins Greases Nylon Polyvinyl chloride resins ...cycloaliphatic epoxy to a level inferior to the porcelain. In one application having a glass -cloth epoxy- based laminate coated with cycloaliphatic epoxy the

Boswellia gum resin/chitosan polymer composites: Controlled delivery vehicles for aceclofenac.

PubMed

Jana, Sougata; Laha, Bibek; Maiti, Sabyasachi

2015-01-01

This study was undertaken to evaluate the effect of Boswellia gum resin on the properties of glutaraldehyde (GA) crosslinked chitosan polymer composites and their potential as oral delivery vehicles for a non-steroidal anti-inflammatory drug, aceclofenac. The incorporation of resinous material caused a significant improvement in drug entrapment efficiency (∼40%) of the polymer composites. Fourier transform infrared (FTIR) spectroscopic analysis confirmed the formation of chitosan-gum resin composites and did not show any evidence of drug-polymer chemical interaction. Field emission scanning electron microscopy (FE-SEM) suggested the formation of particulate polymer composites up to chitosan:gum resin mass ratio of 1:3. Only 8-17% drug was released into HCl solution (pH 1.2) in 2h. The drug release rate of polymer composites was faster in phosphate buffer solution (pH 6.8). The composites released ∼60-68% drug load in 7h. In same duration, the drug release rate suddenly boosted up to 92% as the concentration of gum resin in the composites was raised to 80%. The drug release mechanism deviated from non-Fickian to case-II type with increasing resin concentration in the composites. Hence, GA-treated Boswellia resin-chitosan composites could be considered as alternative vehicles for oral delivery of aceclofenac. Copyright © 2015 Elsevier B.V. All rights reserved.

Marginal integrity of low-shrinkage and methacrylate-based composite resins: Effect of three different hemostatic agents

PubMed Central

Khoroushi, Maryam; Sahraneshin-Samani, Mahsa

2016-01-01

Background Moisture control is very important in restorative procedures in dentistry. Use of hemostatic agents helps control moisture; however, they might result in changes on enamel and dentin surfaces, affecting composite resin bond quality. The aim of this in vitro study was to evaluate the marginal microleakage of two different composite resins with the use of three different hemostatic agents. Material and Methods Standardized Class V cavities were prepared on the buccal and lingual surfaces of 48 premolars with cervical margins 1 mm apical to the cementoenamel junction (CEJ). The samples were randomly divided into 8 groups. In groups 1 to 4, an etch-and-rinse adhesive (Adper Single Bond) was applied as the bonding system, followed by exposure to different hemostatic agent: group 1: no hemostatic agent (control); group 2: ViscoStat; group 3: ViscoStat Clear; and group 4: trichloracetic acid, as hemostatic agents. The cavities were restored with Z-250 composite resin. In group 5 to 8 Silorane System Adhesive (Filtek P90 Adhesive) was applied as a bonding agent, followed by exposure to different hemostatic agents in a manner similar to that in groups 1to 4. The cavities were restored with Filtek P90, a low-shrinkage composite resin. The samples in each group were evaluated for dye penetration under a stereomicroscope at ×36 after 24 hours and a 500-round thermocycling procedure at enamel and dentin margins. Statistical analysis was carried out using Kruskal-Wallis and Mann-Whitney tests (α=0.05). Results Z-250 composite resin exhibited significantly higher dentin microleakage scores compared to Filtek P90 (P = 0.004). Trichloracetic acid increased dentin microleakage with Filtek P90 (P=0.033). Conclusions Under the limitations of this in vitro study, application of hemostatic agents did not affect microleakage of the two tested composite resins except for trichloracetic acid that increased marginal microleakage when used with Filtek P90. Key words:Composite resin, dental leakage, hemostatics, silorane system adhesive. PMID:27034759

A study on the compatibility between one-bottle dentin adhesives and composite resins using micro-shear bond strength.

PubMed

Song, Minju; Shin, Yooseok; Park, Jeong-Won; Roh, Byoung-Duck

2015-02-01

This study was performed to determine whether the combined use of one-bottle self-etch adhesives and composite resins from same manufacturers have better bond strengths than combinations of adhesive and resins from different manufacturers. 25 experimental micro-shear bond test groups were made from combinations of five dentin adhesives and five composite resins with extracted human molars stored in saline for 24 hr. Testing was performed using the wire-loop method and a universal testing machine. Bond strength data was statistically analyzed using two way analysis of variance (ANOVA) and Tukey's post hoc test. Two way ANOVA revealed significant differences for the factors of dentin adhesives and composite resins, and significant interaction effect (p < 0.001). All combinations with Xeno V (Dentsply De Trey) and Clearfil S(3) Bond (Kuraray Dental) adhesives showed no significant differences in micro-shear bond strength, but other adhesives showed significant differences depending on the composite resin (p < 0.05). Contrary to the other adhesives, Xeno V and BondForce (Tokuyama Dental) had higher bond strengths with the same manufacturer's composite resin than other manufacturer's composite resin. Not all combinations of adhesive and composite resin by same manufacturers failed to show significantly higher bond strengths than mixed manufacturer combinations.

Development of new and improved polymer matrix resin systems, phase 1

NASA Technical Reports Server (NTRS)

Hsu, M. S.

1983-01-01

Vinystilbazole (vinylstryrylpyridine) and vinylpolystyrulpyridine were prepared for the purpose of modifying bismaleimide composite resins. Cure studies of resins systems were investigated by differential scanning calorimetry. The vinylstyrylpyridine-modified bismaleimide composite resins were found to have lower cure and gel temperatures, and shorter cure times than the corresponding unmodified composite resins. The resin systems were reinforced with commercially avialable satin-weave carbon cloth. Prepregs were fabricated by solvent or hot melt techniques. Thermal stability, flammability, moisture absorption, and mechanical properties of the composites (such as flexural strength, modulus, tensile and short beam shear strength) were determined. Composite laminates showed substantial improvements in both processability and mechanical properties compared to he bismaleimide control systems. The vinylstyrylpyridine modified bismaleimide resins can be used as advanced matrix resins for graphite secondary structures where ease of processing, fireworthiness, and high temperature stability are required for aerospace applications.

Cuspal Deflection of Premolars Restored with Bulk-Fill Composite Resins.

PubMed

Behery, Haytham; El-Mowafy, Omar; El-Badrawy, Wafa; Saleh, Belal; Nabih, Sameh

2016-01-01

This in vitro study compared cuspal deflection of premolars restored with three bulk-fill composite resins to that of incrementally-restored ones with a low-shrinkage silorane-based restorative material. Forty freshly-extracted intact human upper premolars were used. Reference points at buccal and palatal cusp tips were acid-etched and composite rods were horizontally bonded to them (TPH-Spectra-HV, Dentsply). Two acrylic resin guiding paths were made for each premolar to guide beaks of a digital micrometer used for cuspal deflection measurements. Standardized MOD cavities, 3 mm wide bucco-lingually and 3.5 mm deep, were prepared on each premolar. Prepared teeth were then equally divided into four groups (n = 10) and each group was assigned to one of four composite resin (QuiXX, Dentsply; X-tra fil, Voco; Tetric EvoCeram Bulk Fill, Ivoclar Vivadent; low-shrinkage Filtek LS, 3M/ESPE). Adper Single Bond-Plus, 3M/ESPE was used with all bulk-fill restoratives. LS-System Adhesive, 3M/ESPE was used with Filtek LS. For each prepared premolar, cuspal deflection was measured in microns as the difference between two readings between reference points before and after restoration completion. Means and SDs were calculated and data statistically-analyzed using One-way ANOVA and Tukey's test. Filtek LS showed the lowest mean cuspal deflection value 6.4(0.84)μm followed by Tetric EvoCeram Bulk Fill 10.1(1.2) μm and X-tra fil 12.4(1.35)μm, while QuiXX showed the highest mean 13(1.05)μm. ANOVA indicated significant difference among mean values of groups (p < 0.001). Tukey's test indicated no significant difference in mean values between QuiXX and X-tra fil (p = 0.637). Tetric EvoCeram Bulk Fill had significantly lower mean cuspal deflection compared with the two other bulk-fill composite resins tested. Filtek LS had the lowest significant mean cuspal deflection in comparison to all tested bulk-fill restoratives. The use of Tetric EvoCeram Bulk fill composite resin restorative for class II MOD cavities resulted in reduced cuspal deflection in comparison to the two other bulk-fill composite resins tested. The silorane-based Filtek LS restorative resulted in the least cuspal deflection in comparison to all tested bulk-fill composite restoratives. © 2016 Wiley Periodicals, Inc.

Effect of the Purple Corn Beverage "Chicha Morada" in Composite Resin during Dental Bleaching.

PubMed

Acuña, Eric Dario; Delgado-Cotrina, Leyla; Rumiche, Francisco Aurelio; Tay, Lidia Yileng

2016-01-01

During dental bleaching the staining potential of the surface would increase. This study aims to evaluate the staining susceptibility of one bleached composite resin after the exposure to three different beverages: Peruvian purple corn based beverage (chicha morada), green tea, and distilled water. Thirty disk-shaped specimens of one nanofill composite resin were prepared. The specimens were then divided into six groups (n = 5): purple corn (P), purple corn + bleaching (PB), green tea (T), green tea + bleaching (TB), distilled water (W), and distilled water + bleaching (WB). In groups that received bleaching, two sessions of bleaching with 35% hydrogen peroxide were done. Following bleaching, specimens were exposed to each liquid thirty minutes daily. Color was measured with a digital spectrophotometer. For statistical analysis, color measurement differences between the obtained results were used: during bleaching, after bleaching, and during + after bleaching. Two-way ANOVA was used to compare the color changes in the resins of all groups (p < 0.05). We conclude that all the evaluated beverages produced changes of color in the composite resin regardless of the bleaching procedure. However, purple corn was the only beverage that caused a perceptible color change (ΔE > 3.3).

Effect of the Purple Corn Beverage “Chicha Morada” in Composite Resin during Dental Bleaching

PubMed Central

Acuña, Eric Dario; Delgado-Cotrina, Leyla; Rumiche, Francisco Aurelio

2016-01-01

During dental bleaching the staining potential of the surface would increase. This study aims to evaluate the staining susceptibility of one bleached composite resin after the exposure to three different beverages: Peruvian purple corn based beverage (chicha morada), green tea, and distilled water. Thirty disk-shaped specimens of one nanofill composite resin were prepared. The specimens were then divided into six groups (n = 5): purple corn (P), purple corn + bleaching (PB), green tea (T), green tea + bleaching (TB), distilled water (W), and distilled water + bleaching (WB). In groups that received bleaching, two sessions of bleaching with 35% hydrogen peroxide were done. Following bleaching, specimens were exposed to each liquid thirty minutes daily. Color was measured with a digital spectrophotometer. For statistical analysis, color measurement differences between the obtained results were used: during bleaching, after bleaching, and during + after bleaching. Two-way ANOVA was used to compare the color changes in the resins of all groups (p < 0.05). We conclude that all the evaluated beverages produced changes of color in the composite resin regardless of the bleaching procedure. However, purple corn was the only beverage that caused a perceptible color change (ΔE > 3.3). PMID:27034897

Post-irradiation hardness development, chemical softening, and thermal stability of bulk-fill and conventional resin-composites.

PubMed

Alshali, Ruwaida Z; Salim, Nesreen A; Satterthwaite, Julian D; Silikas, Nick

2015-02-01

To measure bottom/top hardness ratio of bulk-fill and conventional resin-composite materials, and to assess hardness changes after dry and ethanol storage. Filler content and kinetics of thermal decomposition were also tested using thermogravimetric analysis (TGA). Six bulk-fill (SureFil SDR, Venus bulk fill, X-tra base, Filtek bulk fill flowable, Sonic fill, and Tetric EvoCeram bulk-fill) and eight conventional resin-composite materials (Grandioso flow, Venus Diamond flow, X-flow, Filtek Supreme Ultra Flowable, Grandioso, Venus Diamond, TPH Spectrum, and Filtek Z250) were tested (n=5). Initial and 24h (post-cure dry storage) top and bottom microhardness values were measured. Microhardness was re-measured after the samples were stored in 75% ethanol/water solution. Thermal decomposition and filler content were assessed by TGA. Results were analysed using one-way ANOVA and paired sample t-test (α=0.05). All materials showed significant increase of microhardness after 24h of dry storage which ranged from 100.1% to 9.1%. Bottom/top microhardness ratio >0.9 was exhibited by all materials. All materials showed significant decrease of microhardness after 24h of storage in 75% ethanol/water which ranged from 14.5% to 74.2%. The extent of post-irradiation hardness development was positively correlated to the extent of ethanol softening (R(2)=0.89, p<0.001). Initial thermal decomposition temperature assessed by TGA was variable and was correlated to ethanol softening. Bulk-fill resin-composites exhibit comparable bottom/top hardness ratio to conventional materials at recommended manufacturer thickness. Hardness was affected to a variable extent by storage with variable inorganic filler content and initial thermal decomposition shown by TGA. The manufacturer recommended depth of cure of bulk-fill resin-composites can be reached based on the microhardness method. Characterization of the primary polymer network of a resin-composite material should be considered when evaluating its stability in the aqueous oral environment. Copyright © 2014 Elsevier Ltd. All rights reserved.

Assessing the irradiance delivered from light-curing units in private dental offices in Jordan.

PubMed

Maghaireh, Ghada A; Alzraikat, Hanan; Taha, Nessrin A

2013-08-01

The authors conducted a study to examine the irradiance from light-curing units (LCUs) used in dental offices in Jordan. Two of the authors visited 295 private dental offices (15 percent) in Jordan and collected the following information about the LCUs: age, type (quartz-tungsten-halogen or light-emitting diode), date of last maintenance, type of maintenance, last date of use, number of times used during the day, availability of a radiometer, exposure time for each resin-based composite increment, size of light-curing tips and presence of resin-based composite on the tips. The authors used a radiometer to measure the irradiance from the LCUs. They used linear regression with stepwise correlation for the statistical analysis. The authors set the minimum acceptable irradiance at 300 milliwatts/square centimeter. The mean irradiance of the 295 LCUs examined was 361 mW/cm(2), and 136 LCUs (46.1 percent) delivered an irradiance of less than 300 mW/cm(2). The unit's age, type and presence of resin-based composite on the light-curing tips had a significant effect on the irradiance (P ≤ .001). Only 37 of the 141 quartz-tungsten-halogen units (26.2 percent) and 122 of the 154 light-emitting diode units (79.2 percent) delivered at least 300 mW/cm(2). Resin contamination on the light-curing tips had a significant effect on the irradiance delivered. The irradiance from the LCUs decreased with use. Practical Implications. The irradiance from many of the units in this study was less than 300 mW/cm(2), which may affect the quality of resin-based composite restorations. Dentists should monitor the performance of the LCUs in their offices weekly.

Fast Curing of Composite Wood Products

DOE Office of Scientific and Technical Information (OSTI.GOV)

Dr. Arthur J. Ragauskas

2006-04-26

The overall objective of this program is to develop low temperature curing technologies for UF and PF resins. This will be accomplished by: • Identifying the rate limiting UF and PF curing reactions for current market resins; • Developing new catalysts to accelerate curing reactions at reduced press temperatures and times. In summary, these new curing technologies will improve the strength properties of the composite wood products and minimize the detrimental effects of wood extractives on the final product while significantly reducing energy costs for wood composites. This study is related to the accelerated curing of resins for wood compositesmore » such as medium density fiberboard (MDF), particle board (PB) and oriented strandboard (OSB). The latter is frequently manufactured with a phenol-formaldehyde resin whereas ureaformaldehyde (UF) resins are usually used in for the former two grades of composite wood products. One of the reasons that hinder wider use of these resins in the manufacturing of wood composites is the slow curing speed as well as inferior bondability of UF resin. The fast curing of UP and PF resins has been identified as an attractive process development that would allow wood to be bonded at higher moisture contents and at lower press temperatures that currently employed. Several differing additives have been developed to enhance cure rates of PF resins including the use of organic esters, lactones and organic carbonates. A model compound study by Conner, Lorenz and Hirth (2002) employed 2- and 4-hydroxymethylphenol with organic esters to examine the chemical basis for the reported enhanced reactivity. Their studies suggested that the enhance curing in the presence of esters could be due to enhanced quinone methide formation or enhanced intermolecular SN2 reactions. In either case the esters do not function as true catalysts as they are consumed in the reaction and were not found to be incorporated in the polymerized resin product. An alternative approach to accelerated PF curing can be accomplished with the addition amines or amides. The later functionality undergoes base catalyzed hydrolysis yielding the corresponding carboxyl ate and free amine which rapidly reacts with the phenolic methylol groups facilitating polymerization and curing of the PF resin (Pizzi, 1997).« less

[Effect of Radii barrier sleeves on cure depth of composite resin].

PubMed

Wang, Binping; DU, Yongxiu

2009-01-01

To explore the effect of Radii barrier sleeves on the cure depth of composite resin. Cylinder mold was prepared, and the resin was filled strictly into the mold. The surface was flattened and then cured with plastic engraver's knife.The depth of composite resin which was cured by QHL75TM with or without Radii barrier sleeves was compared. The cure depth of composite resin which were cured by QHL75TM with or without Radii barrier sleeves of photo-curing machine was 4.38 mm and 4.27 mm respectively,with no statistical difference. The cure depth of composite resin is not influenced by Radii barrier sleeves under the same light condition.

Physical and mechanical properties of bio-composites from wood particles and liquefied wood resin

Treesearch

Hui Pan; Todd F. Shupe; Chung-Yun Hse

2009-01-01

Compression molded composites were made from wood particles and a liquefied wood/phenol/formaldehyde co-condensed resin. Based on our previous research, a phenol to wood (P/W) ratio of 2/1 was chosen for this study. The two experimental variables selected were: 1) liquefaction temperature (150o and 180oC) and 2) cooking method (atmospheric and sealed). Panels were...

Effect of LED and Argon Laser on Degree of Conversion and Temperature Rise of Hybrid and Low Shrinkage Composite Resins

PubMed Central

Pahlevan, Ayob; Tabatabaei, Masumeh Hasani; Arami, Sakineh; Valizadeh, Sara

2016-01-01

Objectives: Different light curing units are used for polymerization of composite resins. The aim of this study was to evaluate the degree of conversion (DC) and temperature rise in hybrid and low shrinkage composite resins cured by LED and Argon Laser curing lights. Materials and Methods: DC was measured using FTIR spectroscopy. For measuring temperature rise, composite resin samples were placed in Teflon molds and cured from the top. The thermocouple under samples recorded the temperature rise. After initial radiation and specimens reaching the ambient temperature, reirradiation was done and temperature was recorded again. Both temperature rise and DC data submitted to one-way ANOVA and Tukey-HSD tests (5% significance). Results: The obtained results revealed that DC was not significantly different between the understudy composite resins or curing units. Low shrinkage composite resin showed a significantly higher temperature rise than hybrid composite resin. Argon laser caused the lowest temperature rise among the curing units. Conclusion: Energy density of light curing units was correlated with the DC. Type of composite resin and light curing unit had a significant effect on temperature rise due to polymerization and curing unit, respectively. PMID:27843507

Effect of LED and Argon Laser on Degree of Conversion and Temperature Rise of Hybrid and Low Shrinkage Composite Resins.

PubMed

Pahlevan, Ayob; Tabatabaei, Masumeh Hasani; Arami, Sakineh; Valizadeh, Sara

2016-01-01

Different light curing units are used for polymerization of composite resins. The aim of this study was to evaluate the degree of conversion (DC) and temperature rise in hybrid and low shrinkage composite resins cured by LED and Argon Laser curing lights. DC was measured using FTIR spectroscopy. For measuring temperature rise, composite resin samples were placed in Teflon molds and cured from the top. The thermocouple under samples recorded the temperature rise. After initial radiation and specimens reaching the ambient temperature, reirradiation was done and temperature was recorded again. Both temperature rise and DC data submitted to one-way ANOVA and Tukey-HSD tests (5% significance). The obtained results revealed that DC was not significantly different between the understudy composite resins or curing units. Low shrinkage composite resin showed a significantly higher temperature rise than hybrid composite resin. Argon laser caused the lowest temperature rise among the curing units. Energy density of light curing units was correlated with the DC. Type of composite resin and light curing unit had a significant effect on temperature rise due to polymerization and curing unit, respectively.

Fracture Resistance of Endodontically Treated Teeth Restored with Biodentine, Resin Modified GIC and Hybrid Composite Resin as a Core Material.

PubMed

Subash, Dayalan; Shoba, Krishnamma; Aman, Shibu; Bharkavi, Srinivasan Kumar Indu; Nimmi, Vijayan; Abhilash, Radhakrishnan

2017-09-01

The restoration of a severely damaged tooth usually needs a post and core as a part of treatment procedure to provide a corono - radicular stabilization. Biodentine is a class of dental material which possess high mechanical properties with excellent biocompatibility and bioactive behaviour. The sealing ability coupled with optimum physical properties could make Biodentine an excellent option as a core material. The aim of the study was to determine the fracture resistance of Biodentine as a core material in comparison with resin modified glass ionomer and composite resin. Freshly extracted 30 human permanent maxillary central incisors were selected. After endodontic treatment followed by post space preparation and luting of Glass fibre post (Reforpost, Angelus), the samples were divided in to three groups based on the type of core material. The core build-up used in Group I was Biodentine (Septodont, France), Group II was Resin-Modified Glass Ionomer Cement (GC, Japan) and Group III was Hybrid Composite Resin (TeEconom plus, Ivoclar vivadent). The specimens were subjected to fracture toughness using Universal testing machine (1474, Zwick/Roell, Germany) and results were compared using One-way analysis of variance with Tukey's Post hoc test. The results showed that there was significant difference between groups in terms of fracture load. Also, composite resin exhibited highest mean fracture load (1039.9 N), whereas teeth restored with Biodentine demonstrated the lowest mean fracture load (176.66 N). Resin modified glass ionomer exhibited intermediate fracture load (612.07 N). The primary mode of failure in Group I and Group II was favourable (100%) while unfavourable fracture was seen in Group III (30%). Biodentine, does not satisfy the requirements to be used as an ideal core material. The uses of RMGIC's as a core build-up material should be limited to non-stress bearing areas. Composite resin is still the best core build-up material owing to its high fracture resistance and bonding to tooth.

Alternative methods for determining shrinkage in restorative resin composites.

PubMed

de Melo Monteiro, Gabriela Queiroz; Montes, Marcos Antonio Japiassú Resende; Rolim, Tiago Vieira; de Oliveira Mota, Cláudia Cristina Brainer; de Barros Correia Kyotoku, Bernardo; Gomes, Anderson Stevens Leônidas; de Freitas, Anderson Zanardi

2011-08-01

The purpose of this study was to evaluate polymerization shrinkage of resin composites using a coordinate measuring machine, optical coherence tomography and a more widely known method, such as Archimedes Principle. Two null hypothesis were tested: (1) there are no differences between the materials tested; (2) there are no differences between the methods used for polymerization shrinkage measurements. Polymerization shrinkage of seven resin-based dental composites (Filtek Z250™, Filtek Z350™, Filtek P90™/3M ESPE, Esthet-X™, TPH Spectrum™/Dentsply 4 Seasons™, Tetric Ceram™/Ivoclar-Vivadent) was measured. For coordinate measuring machine measurements, composites were applied to a cylindrical Teflon mold (7 mm × 2 mm), polymerized and removed from the mold. The difference between the volume of the mold and the volume of the specimen was calculated as a percentage. Optical coherence tomography was also used for linear shrinkage evaluations. The thickness of the specimens was measured before and after photoactivation. Polymerization shrinkage was also measured using Archimedes Principle of buoyancy (n=5). Statistical analysis of the data was performed with ANOVA and the Games-Howell test. The results show that polymerization shrinkage values vary with the method used. Despite numerical differences the ranking of the resins was very similar with Filtek P90 presenting the lowest shrinkage values. Because of the variations in the results, reported values could only be used to compare materials within the same method. However, it is possible rank composites for polymerization shrinkage and to relate these data from different test methods. Independently of the method used, reduced polymerization shrinkage was found for silorane resin-based composite. Copyright © 2011 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Polishing and toothbrushing alters the surface roughness and gloss of composite resins.

PubMed

Kamonkhantikul, Krid; Arksornnukit, Mansuang; Takahashi, Hidekazu; Kanehira, Masafumi; Finger, Werner J

2014-01-01

This study aimed to investigate the surface roughness and gloss of composite resins after using two polishing systems and toothbrushing. Six composite resins (Durafill VS, Filtek Z250, Filtek Z350 XT, Kalore, Venus Diamond, and Venus Pearl) were evaluated after polishing with two polishing systems (Sof-Lex, Venus Supra) and after toothbrushing up to 40,000 cycles. Surface roughness (Ra) and gloss were determined for each composite resin group (n=6) after silicon carbide paper grinding, polishing, and toothbrushing. Two-way ANOVA indicated significant differences in both Ra and gloss between measuring stages for the composite resins tested, except Venus Pearl, which showed significant differences only in gloss. After polishing, the Filtek Z350 XT, Kalore, and Venus Diamond showed significant increases in Ra, while all composite resin groups except the Filtek Z350 XT and Durafill VS with Sof-Lex showed increases in gloss. After toothbrushing, all composite resin demonstrated increases in Ra and decreases in gloss.

Comparative physico-mechanical characterization of new hybrid restorative materials with conventional glass-ionomer and resin composite restorative materials.

PubMed

Gladys, S; Van Meerbeek, B; Braem, M; Lambrechts, P; Vanherle, G

1997-04-01

The recently developed hybrid restorative materials contain the essential components of conventional glass ionomers and light-cured resins. The objective of this study was to determine several physical and mechanical properties of eight such materials in comparison with two conventional glass ionomers, one micro-filled, and one ultrafine compact-filled resin composite. The two resin composites and two of the three polyacid-modified resin composites could be polished to a higher gloss than the conventional as well as the resin-modified glass ionomers. After abrasion, surface roughness increased for all materials, but not at the same extent, being the least for the conventional resin composites and one polyacid-modified resin composite, Dyract. In contrast to the later resin composites, of which the surface roughness is principally determined by the presence of protruding filler particles above the resin matrix, roughness of conventional and resin-modified glass ionomers results from both protruding filler particles and intruding porosities. The mean particle size of the hybrid restorative materials fell between the smaller mean particle size of the resin composites and the larger one of the conventional glass ionomers. The micro-hardness and Young's modulus values varied substantially among all eight hybrid restorative materials. For all the resin-modified glass-ionomer restorative materials, the Young's modulus reached a maximum value one month after mixing and remained relatively stable thereafter. The Young's modulus of the conventional and the polyacid-modified resin composites decreased slightly after one month. The conventional glass-ionomer materials undoubtedly set the slowest, since their Young's modulus took six months to reach its maximum. The flexural fatigue limit of the hybrid restorative materials is comparable with that of the micro-filled composite. From this investigation, it can be concluded that the physico-mechanical properties vary widely among the eight hybrid restorative materials, indicating that these materials probably have yet to achieve their optimum properties. Their mechanical strength is inadequate for use in stress-bearing areas, and their appearance keeps them from use where esthetics is a primary concern.

Annealing effects on magnetic properties of silicone-coated iron-based soft magnetic composites

NASA Astrophysics Data System (ADS)

Wu, Shen; Sun, Aizhi; Zhai, Fuqiang; Wang, Jin; Zhang, Qian; Xu, Wenhuan; Logan, Philip; Volinsky, Alex A.

2012-03-01

This paper focuses on novel iron-based soft magnetic composites synthesis utilizing high thermal stability silicone resin to coat iron powder. The effect of an annealing treatment on the magnetic properties of synthesized magnets was investigated. The coated silicone insulating layer was characterized by scanning electron microscopy and energy dispersive X-ray spectroscopy. Silicone uniformly coated the powder surface, resulting in a reduction of the imaginary part of the permeability, thereby increasing the electrical resistivity and the operating frequency of the synthesized magnets. The annealing treatment increased the initial permeability, the maximum permeability, and the magnetic induction, and decreased the coercivity. Annealing at 580 °C increased the maximum permeability by 72.5%. The result of annealing at 580 °C shows that the ferromagnetic resonance frequency increased from 2 kHz for conventional epoxy resin coated samples to 80 kHz for the silicone resin insulated composites.

Curing Effects on Interfacial Adhesion between Recycled Carbon Fiber and Epoxy Resin Heated by Microwave Irradiation

PubMed Central

Shimamoto, Daisuke; Hotta, Yuji

2018-01-01

The interfacial adhesion of recycled carbon fiber (CF) reinforced epoxy composite heated by microwave (MW) irradiation were investigated by changing the curing state of the epoxy resin. The recycled CF was recovered from the composite, which was prepared by vacuum-assisted resin transfer molding, by thermal degradation at 500 or 600 °C. Thermogravimetric analysis showed that the heating at 600 °C caused rough damage to the CF surface, whereas recycled CF recovered at 500 °C have few defects. The interfacial shear strength (IFSS) between recycled CF and epoxy resin was measured by a single-fiber fragmentation test. The test specimen was heated by MW after mixing the epoxy resin with a curing agent or pre-curing, in order to investigate the curing effects on the matrix resin. The IFSSs of the MW-irradiated samples were significantly varied by the curing state of the epoxy resin and the surface condition of recycled CF, resulting that they were 99.5 to 131.7% of oven heated samples Furthermore, rheological measurements showed that the viscosity and shrinking behaviors of epoxy resin were affected based on the curing state of epoxy resin before MW irradiation. PMID:29587422

Curing Effects on Interfacial Adhesion between Recycled Carbon Fiber and Epoxy Resin Heated by Microwave Irradiation.

PubMed

Tominaga, Yuichi; Shimamoto, Daisuke; Hotta, Yuji

2018-03-26

The interfacial adhesion of recycled carbon fiber (CF) reinforced epoxy composite heated by microwave (MW) irradiation were investigated by changing the curing state of the epoxy resin. The recycled CF was recovered from the composite, which was prepared by vacuum-assisted resin transfer molding, by thermal degradation at 500 or 600 °C. Thermogravimetric analysis showed that the heating at 600 °C caused rough damage to the CF surface, whereas recycled CF recovered at 500 °C have few defects. The interfacial shear strength (IFSS) between recycled CF and epoxy resin was measured by a single-fiber fragmentation test. The test specimen was heated by MW after mixing the epoxy resin with a curing agent or pre-curing, in order to investigate the curing effects on the matrix resin. The IFSSs of the MW-irradiated samples were significantly varied by the curing state of the epoxy resin and the surface condition of recycled CF, resulting that they were 99.5 to 131.7% of oven heated samples Furthermore, rheological measurements showed that the viscosity and shrinking behaviors of epoxy resin were affected based on the curing state of epoxy resin before MW irradiation.

On-demand tuned hazard free elastomeric composites: A green approach.

PubMed

Manoharan, Partheban; Chandra Das, Narayan; Naskar, Kinsuk

2017-07-01

Rising ecological concerns and depletion of the potentially harmful environmental impacts caused by rubber products, are of prime importance in the industry. Therefore, implementation of sustainable greener materials is required to minimize the detrimental influences. In this research, we investigated the beneficial influence of naturally derived bio-resin toward the effects of association with Zinc Oxide Nanoparticles in highly dispersible silica (HDS) reinforced Natural rubber (NR)/Epoxidized Natural Rubber (ENR)-based composites. This novel green composite offers impressive properties which were analyzed based on bound rubber content, transmission electron microscopy, physico-mechanical, dynamic mechanical, and cure characteristics. Nanoindentation studies demonstrated the enhanced hysteresis phenomenon of the green composites. The small angle X-ray scattering (SAXS) characterization has been studied by using a Beaucage model and results corroborates that the insertion of bio-resin exhibits ameliorated state of silica dispersion in the green composites. Overall, the study with the bio-resin has provided the impetus in employing it as an alternative to the expensive synthetic route of silane coupling agent and toxic process oil. © 2017 Wiley Periodicals, Inc.

Flight-service program for advanced composite rudders on transport aircraft

NASA Technical Reports Server (NTRS)

1979-01-01

Flight service experience and in-service inspection results are reported for DC-10 graphite composite rudders during the third year of airline service. Test results and status are also reported for ground-based and airborne graphite-epoxy specimens with three different epoxy resin systems to obtain moisture absorption data. Twenty graphite composite rudders were produced, nine of which were installed on commercial aircraft during the past three years. The rudders collectively accumulated 75,863 flight hours. The high time rudder accumulated 12,740 flight hours in slightly over 36 months. The graphite composite rudders were inspected visually at approximately 1000 flight hour intervals and ultrasonically at approximately 3000 flight hour intervals in accordance with in-service inspection plans. All rudders were judged acceptable for continued service as a result of these inspections. Composite moisture absorption data on small specimens, both ground-based and carried aboard three flight-service aircraft, are given. The specimens include Thornel 300 fibers in Narmco 5208 and 5209 resin systems, and Type AS fibers in the Hercules 3501-6 resin system.

Thermal and Mechanical Characteristics of Polymer Composites Based on Epoxy Resin, Aluminium Nanopowders and Boric Acid

NASA Astrophysics Data System (ADS)

Nazarenko, O. B.; Melnikova, T. V.; Visakh, P. M.

2016-01-01

The epoxy polymers are characterized by low thermal stability and high flammability. Nanoparticles are considered to be effective fillers of polymer composites for improving their thermal and functional properties. In this work, the epoxy composites were prepared using epoxy resin ED-20, polyethylene polyamine as a hardener, aluminum nanopowder and boric acid fine powder as flame-retardant filler. The thermal characteristics of the obtained samples were studied using thermogravimetric analysis and differential scanning calorimetry. The mechanical characteristics of epoxy composites were also studied. It was found that an addition of all fillers enhances the thermal stability and mechanical characteristics of the epoxy composites. The best thermal stability showed the epoxy composite filled with boric acid. The highest flexural properties showed the epoxy composite based on the combination of boric acid and aluminum nanopowder.

Assessment of resin-dentin interfacial morphology of two ethanol-based universal adhesives: A scanning electron microscopy study

PubMed Central

Awad, Mohamed Moustafa

2017-01-01

Objective: The objective of this study was to assess the resin-dentin interfacial morphology created by two universal adhesives using scanning electron microscopy (SEM). Materials and Methods: The occlusal surfaces of ten (n = 5) molars were reduced to expose a flat surface of dentin. Two universal adhesives, Scotchbond Universal Adhesive and Tetric N-Bond Universal, were independently applied to air-dried dentin. Light-cured resin-based composite restorative materials were used to incrementally build a composite “buildup.” The specimen was sectioned mesiodistally to expose the resin-dentin interface. The inner surfaces of the specimens were polished. Samples were immersed in hydrochloric acid and then rinsed using distilled water. This was followed by immersion of the samples in 1% sodium hypochlorite solution. Then, samples were thoroughly rinsing with distilled water. Dehydration of samples was performed using ascending concentration of ethyl alcohol. Prepared samples were observed SEM at magnifications ×1500 and x4000. Results: Both universal adhesives could penetrate dentin-forming well-defined resin tags, lateral branches as well as a uniform hybrid layer. Conclusions: Two tested universal adhesives applied in self-etch mode can infiltrate into dentin-producing high-quality interfacial morphology. Similar interfacial morphology may be due to the similarity in composition and application mode. PMID:28729794

HPLC for quality control of polyimides

NASA Technical Reports Server (NTRS)

Young, P. R.; Sykes, G. F.

1979-01-01

High Pressure Liquid Chromatography (HPLC) as a quality control tool for polyimide resins and prepregs are presented. A data base to help establish accept/reject criteria for these materials was developed. This work is intended to supplement, not replace, standard quality control tests normally conducted on incoming resins and prepregs. To help achieve these objectives, the HPLC separation of LARC-160 polyimide precursor resin was characterized. Room temperature resin aging effects were studied. Graphite reinforced composites made from fresh and aged resin were fabricated and tested to determine if changes observed by HPLC were significant.

Glass Reinforcement of Various Epoxy Resins-Polyurea Systems

NASA Astrophysics Data System (ADS)

Joshi, Medha; Jauhari, Smita

2012-07-01

Polyureas (PUs) were prepared by the polycondensation reaction of disperse dyes containing -NH2 group and toluene 2, 4-diisocyanate. The disperse dyes have been prepared by coupling of various 2-diazobenzothiazoles with 1,3-benzenediamine. All the PUs were characterized by elemental analysis, spectral studies, number average molecular weight ( {overline{{Mn}} } ), and thermogravimetry. Further reaction of PUs was carried out with an epoxy resin (i.e., DGEBA). The curing study of prepared resins was monitored by differential scanning calorimeter (DSC). Based on DSC, thermograms glass fiber-reinforced composites have been laminated and characterized by chemical, mechanical, and electrical properties. The unreinforced cured resins were subjected to thermogravimetric analysis (TGA). The laminated composites showed excellent resistance properties against chemicals and good mechanical and electrical properties.

Measurement of composite resin filler particles by using scanning electron microscopy and digital imaging.

PubMed

Jaarda, M J; Lang, B R; Wang, R F; Edwards, C A

1993-04-01

Composite resins are routinely classified on the basis of filler particle size for purposes of research, clinical applications, and communications. The size and characterizations of filler particles have also been considered a significant factor in the rate of wear of composites. Making valid correlations between the filler particles within a composite and wear requires accuracy of filler particle size and characterization. This study was initiated to examine two methods that would (1) qualify the filler particle content of a composite resin and (2) quantify the number, size, and the area occupied by the filler particles in composite resins. Three composite resins, BIS-FIL I, Visio-Fil, and Ful-Fil, were selected as the materials to be examined, on the basis of their published composite classification type as fine particle. The findings demonstrated that scientific methods are available to examine qualitatively and measure quantitatively the composite resin filler particles in terms of their numbers, sizes, and area occupied by use of a scanning electron microscope and digital imaging. Significant differences in the filler particle numbers, sizes, and the area occupied were found for the three composite resins in this study that were classified as fine particle.

Characteristics of low polymerization shrinkage flowable resin composites in newly-developed cavity base materials for bulk filling technique.

PubMed

Nitta, Keiko; Nomoto, Rie; Tsubota, Yuji; Tsuchikawa, Masuji; Hayakawa, Tohru

2017-11-29

The purpose of this study was to evaluate polymerization shrinkage and other physical properties of newly-developed cavity base materials for bulk filling technique, with the brand name BULK BASE (BBS). Polymerization shrinkage was measured according to ISO/FDIS 17304. BBS showed the significantly lowest polymerization shrinkage and significantly higher depth of cure than conventional flowable resin composites (p<0.05). The Knoop hardness, flexural strength and elastic modulus of that were significantly lower than conventional flowable resin composites (p<0.05). BBS had the significantly greatest filler content (p<0.05). SEM images of the surface showed failure of fillers. The lowest polymerization shrinkage was due to the incorporation of a new type of low shrinkage monomer, which has urethane moieties. There were no clear correlations between inorganic filler contents and polymerization shrinkage, flexural strength and elastic modulus. In conclusion, the low polymerization shrinkage of BBS will be useful for cavity treatment in dental clinics.

Synthesis and characterizations of melamine-based epoxy resins.

PubMed

Ricciotti, Laura; Roviello, Giuseppina; Tarallo, Oreste; Borbone, Fabio; Ferone, Claudio; Colangelo, Francesco; Catauro, Michelina; Cioffi, Raffaele

2013-09-05

A new, easy and cost-effective synthetic procedure for the preparation of thermosetting melamine-based epoxy resins is reported. By this innovative synthetic method, different kinds of resins can be obtained just by mixing the reagents in the presence of a catalyst without solvent and with mild curing conditions. Two types of resins were synthesized using melamine and a glycidyl derivative (resins I) or by adding a silane derivative (resin II). The resins were characterized by means of chemical-physical and thermal techniques. Experimental results show that all the prepared resins have a good thermal stability, but differ for their mechanical properties: resin I exhibits remarkable stiffness with a storage modulus value up to 830 MPa at room temperature, while lower storage moduli were found for resin II, indicating that the presence of silane groups could enhance the flexibility of these materials. The resins show a pot life higher than 30 min, which makes these resins good candidates for practical applications. The functionalization with silane terminations can be exploited in the formulation of hybrid organic-inorganic composite materials.

Synthesis and Characterizations of Melamine-Based Epoxy Resins

PubMed Central

Ricciotti, Laura; Roviello, Giuseppina; Tarallo, Oreste; Borbone, Fabio; Ferone, Claudio; Colangelo, Francesco; Catauro, Michelina; Cioffi, Raffaele

2013-01-01

A new, easy and cost-effective synthetic procedure for the preparation of thermosetting melamine-based epoxy resins is reported. By this innovative synthetic method, different kinds of resins can be obtained just by mixing the reagents in the presence of a catalyst without solvent and with mild curing conditions. Two types of resins were synthesized using melamine and a glycidyl derivative (resins I) or by adding a silane derivative (resin II). The resins were characterized by means of chemical-physical and thermal techniques. Experimental results show that all the prepared resins have a good thermal stability, but differ for their mechanical properties: resin I exhibits remarkable stiffness with a storage modulus value up to 830 MPa at room temperature, while lower storage moduli were found for resin II, indicating that the presence of silane groups could enhance the flexibility of these materials. The resins show a pot life higher than 30 min, which makes these resins good candidates for practical applications. The functionalization with silane terminations can be exploited in the formulation of hybrid organic-inorganic composite materials. PMID:24013372

Influence of matrix and filler fraction on biofilm formation on the surface of experimental resin-based composites.

PubMed

Ionescu, Andrei; Brambilla, Eugenio; Wastl, Daniel S; Giessibl, Franz J; Cazzaniga, Gloria; Schneider-Feyrer, Sibylle; Hahnel, Sebastian

2015-01-01

The aim of this study was to investigate the impact of resin matrix chemistry and filler fraction on biofilm formation on the surface of experimental resin-based composites (RBCs). Specimens were prepared from eight experimental RBC formulations differing in resin matrix blend (BisGMA/TEGDMA in a 7:3 wt% ratio or UDMA/aliphatic dimethacrylate in a 1:1 wt% ratio) and filler fraction (no fillers; 65 wt% dental glass with an average diameter of 7 or 0.7 µm or 65 wt% SiO2 with an average diameter of 20 nm). Surface roughness, surface free energy, and chemical surface composition were determined; surface topography was visualized using atomic force microscopy. Biofilm formation was simulated under continuous flow conditions for a 48 h period using a monospecies Streptococcus mutans and a multispecies biofilm model. In the monospecies biofilm model, the impact of the filler fraction overruled the influence of the resin matrix, indicating lowest biofilm formation on RBCs with nano-scaled filler particles and those manufactured from the neat resin blends. The multispecies model suggested a more pronounced effect of the resin matrix blend, as significantly higher biofilm formation was identified on RBCs with a UDMA/dimethacrylate matrix blend than on those including a BisGMA/TEGDMA matrix blend but analogous filler fractions. Although significant differences in surface properties between the various materials were identified, correlations between the surface properties and biofilm formation were poor, which highlights the relevance of surface topography and chemistry. These results may help to tailor novel RBC formulations which feature reduced biofilm formation on their surface.

Evaluation of the Shear Bond Strength of Composite Resin to Wet and Dry Enamel Using Dentin Bonding Agents Containing Various Solvents.

PubMed

Usha, Carounanidy; Ramarao, Sathyanarayanan; John, Bindu Meera; Rajesh, Praveen; Swatha, S

2017-01-01

Bonding of composite resin to dentin mandates a wet substrate whereas, enamel should be dry. This may not be easily achievable in intracoronal preparations where enamel and dentin are closely placed to each other. Therefore, Dentin Bonding Agents (DBA) are recommended for enamel and dentinal bonding, where enamel is also left moist. A research question was raised if the "enamel-only" preparations will also benefit from wet enamel bonding and contemporary DBA. The aim of this study was to compare the shear bond strengths of composite resin, bonded to dry and wet enamel using fifth generation DBA (etch and rinse system) containing various solvents such as ethanol/water, acetone and ethanol. The crowns of 120 maxillary premolars were split into buccal and lingual halves. They were randomly allocated into four groups of DBA: Group 1-water/ethanol based, Group 2-acetone based, Group 3-ethanol based, Group 4-universal bonding agent (control group). The buccal halves and lingual halves were bonded using the wet bonding and dry bonding technique respectively. After application of the DBAs and composite resin build up, shear bond strength testing was done. Group 1 (ethanol/water based ESPE 3M, Adper Single Bond) showed highest bond strength of (23.15 MPa) in dry enamel. Group 2 (acetone based Denstply, Prime and Bond NT, showed equal bond strength in wet and dry enamel condition (18.87 MPa and 18.02 MPa respectively). Dry enamel bonding and ethanol/water based etch and rinse DBA can be recommended for "enamel-only" tooth preparations.

Thermally stable laminating resins

NASA Technical Reports Server (NTRS)

Jones, R. J.; Vaughan, R. W.; Burns, E. A.

1972-01-01

Improved thermally stable laminating resins were developed based on the addition-type pyrolytic polymerization. Detailed monomer and polymer synthesis and characterization studies identified formulations which facilitate press molding processing and autoclave fabrication of glass and graphite fiber reinforced composites. A specific resin formulation, termed P10P was utilized to prepare a Courtaulds HMS reinforced simulated airfoil demonstration part by an autoclave molding process.

Thermal cycling effects on adhesion of resin-bovine enamel junction among different composite resins.

PubMed

Chen, Wen-Cheng; Ko, Chia-Ling; Wu, Hui-Yu; Lai, Pei-Ling; Shih, Chi-Jen

2014-10-01

Thermal cycling is used to mimic the changes in oral cavity temperature experienced by composite resins when used clinically. The purpose of this study is to assess the thermal cycling effects of in-house produced composite resin on bonding strength. The dicalcium phosphate anhydrous filler surfaces are modified using nanocrystals and silanization (w/NP/Si). The resin is compared with commercially available composite resins Filtek Z250, Z350, and glass ionomer restorative material GIC Fuji-II LC (control). Different composite resins were filled into the dental enamel of bovine teeth. The bond force and resin-enamel junction graphical structures of the samples were determined after thermal cycling between 5 and 55°C in deionized water for 600 cycles. After thermal cycling, the w/NP/Si 30wt%, 50wt% and Filtek Z250, Z350 groups showed higher shear forces than glass ionomer GIC, and w/NP/Si 50wt% had the highest shear force. Through SEM observations, more of the fillings with w/NP/Si 30wt% and w/NP/Si 50wt% groups flowed into the enamel tubule, forming closed tubules with the composite resins. The push-out force is proportional to the resin flow depth and uniformity. The push-out tubule pore and resin shear pattern is the most uniform and consistent in the w/NP/Si 50wt% group. Accordingly, this developed composite resin maintains great mechanical properties after thermal cycling. Thus, it has the potential to be used in a clinical setting when restoring non-carious cervical lesions. Copyright © 2014 Elsevier Ltd. All rights reserved.

Bond strength of self-adhesive resin cements to composite submitted to different surface pretreatments.

PubMed

Dos Santos, Victor Hugo; Griza, Sandro; de Moraes, Rafael Ratto; Faria-E-Silva, André Luis

2014-02-01

Extensively destroyed teeth are commonly restored with composite resin before cavity preparation for indirect restorations. The longevity of the restoration can be related to the proper bonding of the resin cement to the composite. This study aimed to evaluate the microshear bond strength of two self-adhesive resin cements to composite resin. COMPOSITE DISCS WERE SUBJECT TO ONE OF SIX DIFFERENT SURFACE PRETREATMENTS: none (control), 35% phosphoric acid etching for 30 seconds (PA), application of silane (silane), PA + silane, PA + adhesive, or PA + silane + adhesive (n = 6). A silicone mold containing a cylindrical orifice (1 mm(2) diameter) was placed over the composite resin. RelyX Unicem (3M ESPE) or BisCem (Bisco Inc.) self-adhesive resin cement was inserted into the orifices and light-cured. Self-adhesive cement cylinders were submitted to shear loading. Data were analyzed by two-way ANOVA and Tukey's test (p < 0.05). Independent of the cement used, the PA + Silane + Adhesive group showed higher microshear bond strength than those of the PA and PA + Silane groups. There was no difference among the other treatments. Unicem presented higher bond strength than BisCem for all experimental conditions. Pretreatments of the composite resin surface might have an effect on the bond strength of self-adhesive resin cements to this substrate.

Differences in the intensity of light-induced fluorescence emitted by resin composites.

PubMed

Kim, Bo-Ra; Kang, Si-Mook; Kim, Gyung-Min; Kim, Baek-Il

2016-03-01

The aims of this study were to compare the intensities of fluorescence emitted by different resin composites as detected using quantitative light-induced fluorescence (QLF) technology, and to compare the fluorescence intensity contrast with the color contrast between a restored composite and the adjacent region of the tooth. Six brands of light-cured resin composites (shade A2) were investigated. The composites were used to prepare composite discs, and fill holes that had been prepared in extracted human teeth. White-light and fluorescence images of all specimens were obtained using a fluorescence camera based on QLF technology (QLF-D) and converted into 8-bit grayscale images. The fluorescence intensity of the discs as well as the fluorescence intensity contrast and the color contrast between the composite restoration and adjacent tooth region were calculated as grayscale levels. The grayscale levels for the composite discs differed significantly with the brand (p<0.001): DenFil (10.84±0.35, mean±SD), Filtek Z350 (58.28±1.37), Premisa (156.94±1.58), Grandio (177.20±0.81), Charisma (207.05±0.77), and Gradia direct posterior (211.52±1.66). The difference in grayscale levels between a resin restoration and the adjacent tooth was significantly greater in fluorescence images for each brand than in white-light images, except for the Filtek Z350 (p<0.05). However, the Filtek Z350 restoration was distinguishable from the adjacent tooth in a fluorescence image. The intensities of fluorescence detected from the resin composites varied. The differences between the composite and adjacent tooth were greater for the fluorescence intensity contrast than for the colors observed in the white-light images. Copyright © 2016 Elsevier B.V. All rights reserved.

Isosorbide as the structural component of bio-based unsaturated polyesters for use as thermosetting resins.

PubMed

Sadler, Joshua M; Toulan, Faye R; Nguyen, Anh-Phuong T; Kayea, Ronald V; Ziaee, Saeed; Palmese, Giuseppe R; La Scala, John J

2014-01-16

In recent years, the development of renewable bio-based resins has gained interest as potential replacements for petroleum based resins. Modified carbohydrate-based derivatives have favorable structural features such as fused bicyclic rings that offer promising candidates for the development of novel renewable polymers with improved thermomechanical properties when compared to early bio-based resins. Isosorbide is one such compound and has been utilized as the stiffness component for the synthesis of novel unsaturated polyesters (UPE) resins. Resin blends of BioUPE systems with styrene were shown to possess viscosities (120-2200 cP) amenable to a variety of liquid molding techniques, and after cure had Tgs (53-107 °C) and storage moduli (430-1650 MPa) that are in the desired range for composite materials. These investigations show that BioUPEs containing isosorbide can be tailored during synthesis of the prepolymer to meet the needs of different property profiles. Copyright © 2013 Elsevier Ltd. All rights reserved.

Salivary bisphenol A levels and their association with composite resin restoration.

PubMed

Lee, Jung-Ha; Yi, Seung-Kyoo; Kim, Se-Yeon; Kim, Ji-Soo; Son, Sung-Ae; Jeong, Seung-Hwa; Kim, Jin-Bom

2017-04-01

Composite resin has been increasingly used in an effort to remove minimal amount of tooth structure and are used for restoring not just carious cavities but also cervical abrasion. To synthesize composite resin, bisphenol A (BPA) is used. The aim of the study was to measure the changes in salivary BPA level related with composite resin restoration. ELISA was used to examine the BPA levels in the saliva collected from 30 volunteers whose teeth were filled with composite resin. Salivary samples were collected immediately before filling and 5 min and 7 d after filling. Wilcoxon signed-ranks test and linear regression were performed to test the significant differences of the changes in BPA levels in saliva. Before a new composite resin filling, there was no significant difference between with and without existing filling of composite resin and BPA level in the saliva was not correlated to the number of filled surfaces with composite resin. However, BPA level in the saliva increased to average 3.64 μg/L from average 0.15 μg/L after filling 5 min. BPA level increased in proportion with the number of filled surfaces. BPA level decreased to average 0.59 after filling 7 d. However it was higher than the BPA level before a new composite resin filling. Considering 50 μg/kg/day as the Tolerable Daily Intake of BPA suggested by European Food Safety Authority, the amount of BPA eluted in saliva after the composite resin filling is considered a safe level that is not a hazard to health at all. Copyright © 2016 Elsevier Ltd. All rights reserved.

Effect of organic solvents compared to sandblasting on the repair bond strength of nanohybrid and nanofilled composite resins.

PubMed

Brum, Rafael Torres; Vieira, Sergio; Freire, Andrea; Mazur, Rui Fernando; De Souza, Evelise Machado; Rached, Rodrigo Nunes

2017-01-01

This study evaluated the effect of different surface treatments on the repair bond strength of nanohybrid (Empress Direct) and nanofilled (Filtek Z350 XT) composite resins. A total of 120 specimens of each material (7.5 x 4.5 x 3 mm) were prepared and polished with SiC paper. Half of the specimens were kept in water for seven days and the other half for six months; they were then divided into six groups according to the type of surface treatment: negative control (no treatment), Al2O3sandblasted, liquid acetone, acetone gel, liquid alcohol and alcohol gel. Following application of the silane coupling agent and the adhesive system, composite resin cylinders were fabricated on the specimens and light cured (20 seconds). The same composite resins were used for the repair. Additionally, ten intact specimens of each composite resin (without repair) were prepared (positive control). The specimens were then loaded to failure in the microshear mode. Three additional specimens were fabricated in each group, and the surface treatments were analyzed by atomic force microscopy, energy-dispersive X-ray spectroscopy (EDS) and scanning electron microscopy (SEM). The nanofilled composite resin showed higher cohesive strength and repair bond strength than the nanohybrid composite resin. The aging process affected the repair bond strength of the nanofilled composite resin. Al2O3sandblasting was more efficient for the nanofilled composite resin and promoted greater surface roughness in both materials. The solvents demonstrated higher efficacy for the nanohybrid composite resin. The strengths resulting from the solvents were material dependent, and Al2O3sandblasting resulted in superior repair bond strength in both materials.

Synthesis of improved phenolic and polyester resins

NASA Technical Reports Server (NTRS)

Delano, C. B.

1980-01-01

Thirty-seven cured phenolic resin compositions were prepared and tested for their ability to provide improved char residues and moisture resistance over state of the art epoxy resin composite matrices. Cyanate, epoxy novolac and vinyl ester resins were investigated. Char promoter additives were found to increase the anaerobic char yield at 800 C of epoxy novolacs and vinyl esters. Moisture resistant cyanate and vinyl ester compositions were investigated as composite matrices with Thornel 300 graphite fiber. A cyanate composite matrix provided state of the art composite mechanical properties before and after humidity exposure and an anaerobic char yield of 46 percent at 800 C. The outstanding moisture resistance of the matrix was not completely realized in the composite. Vinyl ester resins showed promise as candidates for improved composite matrix systems.

Optical approach in characterizing dental biomaterials

NASA Astrophysics Data System (ADS)

Demoli, Nazif; Vučić, Zlatko; Milat, Ognjen; Gladić, Jadranko; Lovrić, Davorin; Pandurić, Vlatko; Marović, Danijela; Moguš-Milanković, Andrea; Ristić, Mira; Čalogović, Marina; Tarle, Zrinka

2013-04-01

The purpose of this paper is to present the current activities of a research collaborative program between three institutions from Zagreb (School of Dental Medicine, Institute of Physics, and Institute Ruđer Bo\\vsković). Within the scope of this program, it is planned to investigate and find guidelines for the refinement of the properties of dental biomaterials (DBs) and of procedures in restorative dental medicine. It is also planned to identify and model the dominant mechanisms which control polymerization of DBs. The materials to be investigated include methacrylate based composite resins, new composite materials with amorphous calcium phosphate, silorane based composite resins, glass-ionomer cements, and giomer.

Qualitative Beam Profiling of Light Curing Units for Resin Based Composites.

PubMed

Haenel, Thomas; Hausnerová, Berenika; Steinhaus, Johannes; Moeginger, Ing Bernhard

2016-12-01

This study investigates two technically simple methods to determine the irradiance distribution of light curing units that governs the performance of a visible-light curing resin-based composites. Insufficient light irradiation leads to under-cured composites with poor mechanical properties and elution of residual monomers. The unknown irradiance distribution and its effect on the final restoration are the main critical issues requiring highly sophisticated experimental equipment. The study shows that irradiance distributions of LCUs can easily be determined qualitatively with generally available equipment. This significantly helps dentists in practices to be informed about the homogeneity of the curing lights. Copyright© 2016 Dennis Barber Ltd.

Structure-to-property relationships in addition cured polymers. 4: Correlations between thermo-oxidative weight losses of norbornenyl cured polyimide resins and their composites

NASA Technical Reports Server (NTRS)

Alston, William B.

1992-01-01

Relationships are identified between the thermo-oxidative stability (TOS) at 316 C of a wide variety of PMR (polymerization of monomeric reactants) addition cured polyimide resins and their corresponding graphite fiber composites. Weight loss results at 316 C confirmed the expected relationship of increasing aliphatic endcap content with decreasing TOS. Moreover, the resin TOS study also showed an unexpected linear correlation of decreasing weight loss to increasing ratio of benzylic diamine to aliphatic endcap in the range of the stoichiometries studied. Only after long term 316 C aging does the dianhydride used with the benzylic diamines become an additional factor in influencing the amount of PMR resin and composite weight losses. Also, the benzylic systems consistently showed much lower resin and composite weight losses at 316 C than the corresponding nonbenzylic norbornenyl resins and composites, except when the nonbenzylic diamine monomer does not contain a connecting group. Instead, this diamine resulted in a 316 C resin and composite weight loss that was only competitive with benzylic type diamines. Results show excellent correlation between TOS of all graphite fiber PMR composites and resins.

[Effect of bleaching agents on the color of indirect and direct composite resins].

PubMed

Xing, Wenzhong; Jiang, Tao; Chen, Xiaodong; Wang, Yining

2014-09-01

To evaluate the effect of bleaching agents on the color of indirect and direct composite resins. Five resin composite materials were tested in this in vitro study. The five composites were as follow: two indirect composite resins (Adoro SR, Ceramage) and three direct composite resins (Filtek Z350, Clearfil Majesty Esthetic, and Gradia Direct Anterior). For each material, twenty disk-shaped specimens were prepared and randomly divided into five groups according to the color parameters of specimens before bleaching treatment. The composite resin specimens were treated by one of five sample solutions which were at-home bleaching agents (10% and 15% carbarmide peroxide), in- office bleaching agents (38% H(2)O(2) and 35%H(2)O(2)) and deionized water (control group). The color parameters of specimens were measured by spectrophotometer at baseline and after bleaching treatments. The color differences (ΔE values) between baseline and post-treatments were calculated. The data of color differences were evaluated statistically using two-way analysis with a significance level of 0.05. The color changes of the resin composites were less than 2.0 after bleaching agent treatment, therefore were not perceptible. Slight increase of L(*) values and decrease of C(*)ab values in color parameters of specimens were observed. There were statistically significant differences in ΔE values for different bleaching treatments and resin materials (P = 0.001). The bleaching agents did not affect the color of indirect and direct composite resins tested.

Resin impregnation process for producing a resin-fiber composite

NASA Technical Reports Server (NTRS)

Palmer, Raymond J. (Inventor); Moore, William E. (Inventor)

1994-01-01

Process for vacuum impregnation of a dry fiber reinforcement with a curable resin to produce a resin-fiber composite, by drawing a vacuum to permit flow of curable liquid resin into and through a fiber reinforcement to impregnate same and curing the resin-impregnated fiber reinforcement at a sufficient temperature and pressure to effect final curing. Both vacuum and positive pressure, e.g. autoclave pressure, are applied to the dry fiber reinforcement prior to application of heat and prior to any resin flow to compact the dry fiber reinforcement, and produce a resin-fiber composite of reduced weight, thickness and resin content, and improved mechanical properties. Preferably both a vacuum and positive pressure, e.g. autoclave pressure, are also applied during final curing.

Comparative study between the radiopacity levels of high viscosity and of flowable composite resins, using digital imaging.

PubMed

Arita, Emiko S; Silveira, Gilson P; Cortes, Arthur R; Brucoli, Henrique C

2012-01-01

The development of countless types and trends of high viscosite and flowable composite resins, with different physical and chemical properties applicable to their broad use in dental clinics calls for further studies regarding their radiopacity level. The aim of this study was to evaluate the radiopacity levels of high viscosity and the flowable composite resins, using digital imaging. 96 composite resin discs 5 mm in diameter and 3 mm thick were radiographed and analyzed. The image acquisition system used was the Digora® Phosphor Storage System and the images were analyzed with the Digora software for Windows. The exposure conditions were: 70 kVp, 8 mA, and 0.2 s. The focal distance was 40 cm. The image densities were obtained with the pixel values of the materials in the digital image. Most of the high viscosity composite resins presented higher radiopacity levels than the flowable composite resins, with statistically significant differences between the trends and groups analyzed (P < 0.05). Among the high viscosity composite resins, Tetric®Ceram presented the highest radiopacity levels and Glacier® presented the lowest. Among the flowable composite resins, Tetric®Flow presented the highest radiopacity levels and Wave® presented the lowest.

Stain susceptibility of composite and ceramic CAD/CAM blocks versus direct resin composites with different resinous matrices.

PubMed

Alharbi, Amal; Ardu, Stefano; Bortolotto, Tissiana; Krejci, Ivo

2017-04-01

To evaluate the stain susceptibility of CAD/CAM blocks and direct composite after long term exposure to various staining agents. 40 disk-shaped samples were fabricated from each of nine materials; six CAD/CAM (Vitablocs Mark II, Paradigm MZ100, Experimental Vita Hybrid Ceramic, Vita Enamic, Experimental Kerr and Lava Ultimate) and three direct composites (Filtek Supreme, Venus Diamond and Filtek Silorane). Samples were randomly divided into five groups (n = 8) according to different staining solutions (distilled water, tea, red wine, coffee and artificial saliva). Initial L*a*b* values were assessed using a calibrated digital spectrophotometer. Specimens were immersed in staining solutions and stored in an incubator at 37 °C for 120 days. L*a*b* values were assessed again and color change (∆E) was calculated as difference between recorded L*a*b* values. ANOVA, and Duncan test were used to identify differences between groups (α = 0.05). Significant differences in ∆E values were detected between materials (p = 0.000). Among all staining solutions, the highest ∆E value was observed with red wine. The new CAD/CAM blocks (Vita Enamic, Vita Hybrid Ceramic and Lava Ultimate) showed the highest resistance to staining compared to the MZ100 composite resin blocks. Filtek Silorane, a direct composite, showed high stain resistance values compared to CAD/CAM materials and other direct composites. Ceramic and composite CAD/CAM blocks had lower staining susceptibility than methacrylate based direct composite. Staining susceptibility of the new resin based CAD/CAM materials Vita Enamic and Lava Ultimate was comparable to feldspathic ceramic blocks (Vitablocs Mark II). Filtek Silorane showed promising results that were comparable to some CAD/CAM blocks.

Evaluating the shear bond strength of enamel and dentin with or without etching: A comparative study between dimethacrylate-based and silorane-based adhesives

PubMed Central

Hajizadeh, Hila; Nasseh, Atefeh; Rahmanpour, Naim

2015-01-01

Background Silorane-based composites and their specific self-etch adhesive were introduced to conquest the polymerization shrinkage of methacrylate-based composites. It has been shown that additional etching of enamel and dentin can improve the bond strength of self-etch methacrylate-based adhesives but this claim is not apparent about silorane-based adhesives. Our objective was to compare the shear bond strength (SBS) of enamel and dentin between silorane-based adhesive resin and a methacrylate-based resin with or without additional etching. Material and Methods 40 sound human premolars were prepared and divided into two groups: 1- Filtek P60 composite and Clearfil SE Bond adhesive; 2- Filtek P90 composite and Silorane adhesive. Each group divided into two subgroups: with or without additional etching. For additional etching, 37% acid phosphoric was applied before bonding procedure. A cylinder of the composite was bonded to the surface. After 24 hours storage and 500 thermo cycling between 5-55°C, shear bond strength was assessed with the cross head speed of 0.5 mm/min. Then, bonded surfaces were observed under stereomicroscope to determine the failure mode. Data were analyzed with two-way ANOVA and Fischer exact test. Results Shear bond strength of Filtek P60 composite was significantly higher than Filtek P90 composite both in enamel and dentin surfaces (P<0.05). However, additional etching had no significant effect on shear bond strength in enamel or dentin for each of the composites (P>0.05). There was no interaction between composite type and additional etching (P>0.05). Failure pattern was mainly adhesive and no significant correlation was found between failure and composite type or additional etching (P>0.05). Conclusions Shear bond strength of methacrylate-based composite was significantly higher than silorane-based composite both in enamel and dentin surfaces and additional etching had no significant effect on shear bond strength in enamel or dentin for each of the composites. The mode of failure had no meaningful relation to the type of composite and etching factor. Key words:Shear bond strength, adhesive, composite resin, silorane, methacrylate. PMID:26644830

Mechanical and anticorrosive properties of graphene/epoxy resin composites coating prepared by in-situ method.

PubMed

Zhang, Zhiyi; Zhang, Wenhui; Li, Diansen; Sun, Youyi; Wang, Zhuo; Hou, Chunling; Chen, Lu; Cao, Yang; Liu, Yaqing

2015-01-20

The graphene nanosheets-based epoxy resin coating (0, 0.1, 0.4 and 0.7 wt %) was prepared by a situ-synthesis method. The effect of polyvinylpyrrolidone/reduced graphene oxide (PVP-rGO) on mechanical and thermal properties of epoxy resin coating was investigated using nanoindentation technique and thermogravimetric analysis, respectively. A significant enhancement (ca. 213% and 73 °C) in the Young modulus and thermal stability of epoxy resin coating was obtained at a loading of 0.7 wt %, respectively. Furthermore, the erosion resistance of graphene nanosheets-based epoxy resin coating was investigated by electrochemical measurement. The results showed also that the Rrcco (ca. 0.3 mm/year) of graphene nanosheets-based epoxy resin coating was far lower than neat epoxy resin (1.3 mm/year). Thus, this approach provides a novel route for improving erosion resistance and mechanical-thermal stability of polymers coating, which is expected to be used in mechanical-thermal-corrosion coupling environments.

Mechanical and Anticorrosive Properties of Graphene/Epoxy Resin Composites Coating Prepared by in-Situ Method

PubMed Central

Zhang, Zhiyi; Zhang, Wenhui; Li, Diansen; Sun, Youyi; Wang, Zhuo; Hou, Chunling; Chen, Lu; Cao, Yang; Liu, Yaqing

2015-01-01

The graphene nanosheets-based epoxy resin coating (0, 0.1, 0.4 and 0.7 wt %) was prepared by a situ-synthesis method. The effect of polyvinylpyrrolidone/reduced graphene oxide (PVP-rGO) on mechanical and thermal properties of epoxy resin coating was investigated using nanoindentation technique and thermogravimetric analysis, respectively. A significant enhancement (ca. 213% and 73 °C) in the Young modulus and thermal stability of epoxy resin coating was obtained at a loading of 0.7 wt %, respectively. Furthermore, the erosion resistance of graphene nanosheets-based epoxy resin coating was investigated by electrochemical measurement. The results showed also that the Rrcco (ca. 0.3 mm/year) of graphene nanosheets-based epoxy resin coating was far lower than neat epoxy resin (1.3 mm/year). Thus, this approach provides a novel route for improving erosion resistance and mechanical-thermal stability of polymers coating, which is expected to be used in mechanical-thermal-corrosion coupling environments. PMID:25608656

Infiltration/cure modeling of resin transfer molded composite materials using advanced fiber architectures

NASA Technical Reports Server (NTRS)

Loos, Alfred C.; Weideman, Mark H.; Long, Edward R., Jr.; Kranbuehl, David E.; Kinsley, Philip J.; Hart, Sean M.

1991-01-01

A model was developed which can be used to simulate infiltration and cure of textile composites by resin transfer molding. Fabric preforms were resin infiltrated and cured using model generated optimized one-step infiltration/cure protocols. Frequency dependent electromagnetic sensing (FDEMS) was used to monitor in situ resin infiltration and cure during processing. FDEMS measurements of infiltration time, resin viscosity, and resin degree of cure agreed well with values predicted by the simulation model. Textile composites fabricated using a one-step infiltration/cure procedure were uniformly resin impregnated and void free. Fiber volume fraction measurements by the resin digestion method compared well with values predicted using the model.

Compatibility between dental adhesive systems and dual-polymerizing composite resins.

PubMed

Michaud, Pierre-Luc; MacKenzie, Alexandra

2016-10-01

Information is lacking about incompatibilities between certain types of adhesive systems and dual-polymerizing composite resins, and universal adhesives have yet to be tested with these resins. The purpose of this in vitro study was to investigate the bonding outcome of dual-polymerizing foundation composite resins by using different categories of adhesive solutions and to determine whether incompatibilities were present. One hundred and eighty caries-free, extracted third molar teeth were allocated to 9 groups (n=20), in which 3 different bonding agents (Single Bond Plus [SB]), Scotchbond Multi-purpose [MP], and Scotchbond Universal [SU]) were used to bond 3 different composite resins (CompCore AF [CC], Core Paste XP [CP], and Filtek Supreme Ultra [FS]). After restorations had been fabricated using an Ultradent device, the specimens were stored in water at 37°C for 24 hours. The specimens were tested under shear force at a rate of 0.5 mm/min. The data were analyzed with Kruskal-Wallis tests and post hoc pairwise comparisons (α=.05). All 3 composite resins produced comparable shear bond strengths when used with MP (P=.076). However, when either SB or SU was used, the light-polymerized composite resin (FS) and 1 dual-polymerized foundation composite resin (CC) bonded significantly better than the other dual-polymerized foundation composite resin (CP) (P<.005). Both FS and CC performed best with SU but had acceptable results with all of the bonding agents. CP only performed acceptably with MP (P=.023) and had poor results with both other agents. Dual-polymerizing composite resins can obtain equally good bond strengths as light-polymerizing alternatives. However, not all dual-polymerizing composite resins perform well with all bonding systems; some incompatibilities exist between different products. Copyright © 2016 Editorial Council for the Journal of Prosthetic Dentistry. Published by Elsevier Inc. All rights reserved.

Effect of indirect composite treatment microtensile bond strength of self-adhesive resin cements

PubMed Central

Escribano, Nuria; Baracco, Bruno; Romero, Martin; Ceballos, Laura

2016-01-01

Background No specific indications about the pre-treatment of indirect composite restorations is provided by the manufacturers of most self-adhesive resin cements. The potential effect of silane treatment to the bond strength of the complete tooth/indirect restoration complex is not available.The aim of this study was to determine the contribution of different surface treatments on microtensile bond strength of composite overlays to dentin using several self-adhesive resin cements and a total-etch one. Material and Methods Composite overlays were fabricated and bonding surfaces were airborne-particle abraded and randomly assigned to two different surface treatments: no treatment or silane application (RelyX Ceramic Primer) followed by an adhesive (Adper Scotchbond 1 XT). Composite overlays were luted to flat dentin surfaces using the following self-adhesive resin cements: RelyX Unicem, G-Cem, Speedcem, Maxcem Elite or Smartcem2, and the total-etch resin cement RelyX ARC. After 24 h, bonded specimens were cut into sticks 1 mm thick and stressed in tension until failure. Two-way ANOVA and SNK tests were applied at α=0.05. Results Bond strength values were significantly influenced by the resin cement used (p<0.001). However, composite surface treatment and the interaction between the resin cement applied and surface treatment did not significantly affect dentin bond strength (p>0.05). All self-adhesive resin cements showed lower bond strength values than the total-etch RelyX ARC. Among self-adhesive resin cements, RelyX Unicem and G-Cem attained statistically higher bond strength values. Smartcem2 and Maxcem Elite exhibited 80-90% of pre-test failures. Conclusions The silane and adhesive application after indirect resin composite sandblasting did not improve the bond strength of dentin-composite overlay complex. Selection of the resin cement seems to be a more relevant factor when bonding indirect composites to dentin than its surface treatment. Key words:Bond strength, self-adhesive cement, silane, dentin, indirect composite. PMID:26855700

Fiber reinforced thermoplastic resin matrix composites

NASA Technical Reports Server (NTRS)

Jones, Robert J. (Inventor); Chang, Glenn E. C. (Inventor)

1989-01-01

Polyimide polymer composites having a combination of enhanced thermal and mechanical properties even when subjected to service temperatures as high as 700.degree. F. are described. They comprise (a) from 10 to 50 parts by weight of a thermoplastic polyimide resin prepared from 2,2-bis[4-(4-aminophenoxy)phenyl]hexafluoropropane and (b) from 90 to 50 parts by weight of continuous reinforcing fibers, the total of (a) and (b) being 100 parts by weight. Composites based on polyimide resin formed from 2,2-bis[4-(4-aminophenoxy)phenyl]hexafluoropropane and pyromellitic dianhydride and continuous carbon fibers retained at least about 50% of their room temperature shear strength after exposure to 700.degree. F. for a period of 16 hours in flowing air. Preferably, the thermoplastic polyimide resin is formed in situ in the composite material by thermal imidization of a corresponding amide-acid polymer prepared from 2,2-bis[4-(4-aminophenoxy)phenyl]hexafluoropropane. It is also preferred to initially size the continuous reinforcing fibers with up to about one percent by weight of an amide-acid polymer prepared from 2,2-bis[4-(4-aminophenoxy)phenyl]hexafluoropropane. In this way imidization at a suitable elevated temperature results in the in-situ formation of a substantially homogeneous thermoplastic matrix of the polyimide resin tightly and intimately bonded to the continuous fibers. The resultant composites tend to have optimum thermo-mechanical properties.

Fabrication and Evaluation of Bis-GMA/TEGDMA Dental Resins/Composites Containing Nano Fibrillar Silicate

PubMed Central

Tian, Ming; Gao, Yi; Liu, Yi; Liao, Yiliang; Hedin, Nyle E.; Fong, Hao

2008-01-01

Objective To investigate the reinforcement of Bis-GMA/TEGDMA dental resins (without conventional glass filler) and composites (with conventional glass filler) with various mass fractions of nano fibrillar silicate (FS). Methods Three dispersion methods were studied to separate the silanized FS as nano-scaled single crystals and uniformly distribute them into dental matrices. The photo-curing behaviors of the Bis-GMA/TEGDMA/FS resins were monitored in situ by RT-NIR to study the photopolymerization rate and the vinyl double bond conversion. Mechanical properties (flexural strength, elastic modulus and work of fracture) of the nano FS reinforced resins/composites were tested, and Analysis of Variance (ANOVA) was used for the statistical analysis of the acquired data. The morphology of nano FS and the representative fracture surfaces of its reinforced resins/composites were examined by SEM/TEM. Results Impregnation of small mass fractions (1 % and 2.5 %) of nano FS into Bis-GMA/TEGDMA (50/50 mass ratio) dental resins/composites improved the mechanical properties substantially. Larger mass fraction of impregnation (7.5 %), however, did not further improve the mechanical properties (one way ANOVA, P > 0.05) and may even reduce the mechanical properties. The high degree of separation and uniform distribution of nano FS into dental resins/composites was a challenge. Impregnation of nano FS into dental resins/composites could result in two opposite effects: a reinforcing effect due to the highly separated and uniformly distributed nano FS single crystals, or a weakening effect due to the formation of FS agglomerates/particles. Significance Uniform distribution of highly separated nano FS single crystals into dental resins/composites could significantly improve the mechanical properties of the resins/composites. PMID:17572485

Fabrication and evaluation of Bis-GMA/TEGDMA dental resins/composites containing nano fibrillar silicate.

PubMed

Tian, Ming; Gao, Yi; Liu, Yi; Liao, Yiliang; Hedin, Nyle E; Fong, Hao

2008-02-01

To investigate the reinforcement of Bis-GMA/TEGDMA dental resins (without conventional glass filler) and composites (with conventional glass filler) with various mass fractions of nano fibrillar silicate (FS). Three dispersion methods were studied to separate the silanized FS as nano-scaled single crystals and uniformly distribute them into dental matrices. The photo-curing behaviors of the Bis-GMA/TEGDMA/FS resins were monitored in situ by RT-NIR to study the photopolymerization rate and the vinyl double bond conversion. Mechanical properties (flexural strength, elastic modulus and work-of-fracture) of the nano FS reinforced resins/composites were tested, and analysis of variance (ANOVA) was used for the statistical analysis of the acquired data. The morphology of nano FS and the representative fracture surfaces of its reinforced resins/composites were examined by SEM/TEM. Impregnation of small mass fractions (1% and 2.5%) of nano FS into Bis-GMA/TEGDMA (50/50 mass ratio) dental resins/composites improved the mechanical properties substantially. Larger mass fraction of impregnation (7.5%), however, did not further improve the mechanical properties (one way ANOVA, P>0.05) and may even reduce the mechanical properties. The high degree of separation and uniform distribution of nano FS into dental resins/composites was a challenge. Impregnation of nano FS into dental resins/composites could result in two opposite effects: a reinforcing effect due to the highly separated and uniformly distributed nano FS single crystals, or a weakening effect due to the formation of FS agglomerates/particles. Uniform distribution of highly separated nano FS single crystals into dental resins/composites could significantly improve the mechanical properties of the resins/composites.

Evaluation of Microleakage and Marginal Ridge Fracture Resistance of Primary Molars Restored with Three Restorative Materials: A Comparative in vitro Study

PubMed Central

Yeolekar, Tapan Satish; Mukunda, KS; Kiran, NK

2015-01-01

ABSTRACT Composite restorations are popular because of their superior esthetics and acceptable clinical performance. But shrinkage is still a drawback. Polymerization shrinkage results in volumetric contraction, leading to deformation of the cusps, microleakage, decrease of marginal adaptation, enamel micro-cracks and postoperative sensitivity. A new class of ring opening resin composite based on silorane chemistry has been introduced with claims of less than 1% shrinkage during polymerization. The present study was conducted to evaluate and compare the ability of low shrink silorane based material, a packable composite and a compomer to resist microleakage in class II restorations on primary molars and evaluate marginal ridge fracture resistance of these materials. Sixty human primary molars were selected. Class II cavities were prepared and the teeth were divided into three groups of twenty each. Groups were as follows group I: low shrink composite resin (Filtek P90). Group II: packable composite (Filtek P60) and Group III: compomer (Compoglass F). Half of the teeth were used for microleakage and the rest for marginal ridge fracture resistance. For microleakage testing, dye penetration method was used with 1% methylene blue dye. Followed by evaluation and grading under stereomicroscope at 10* magnification. Fracture resistance was tested with universal testing machine. It was concluded that low shrink silorane based composite resin showed the least amount of microleakage, whereas compomer showed the highest microleakage. Packable composite resisted fracture of marginal ridge better than other composite resins. Marginal ridge fracture resistance of packable composite was comparable to the intact side. How to cite this article: Yeolekar TS, Chowdhary NR, Mukunda KS, Kiran NK. Evaluation of Microleakage and Marginal Ridge Fracture Resistance of Primary Molars Restored with Three Restorative Materials: A Comparative in vitro Study. Int J Clin Pediatr Dent 2015;8(2):108-113. PMID:26379377

Direct Midline Diastema Closure with Composite Layering Technique: A One-Year Follow-Up.

PubMed

Korkut, Bora; Yanikoglu, Funda; Tagtekin, Dilek

2016-01-01

Objective. Maxillary anterior spacing is a common aesthetic complaint of patients. Midline diastema has a multifactorial etiology such as labial frenulum, microdontia, mesiodens, peg-shaped lateral incisors, agenesis, cysts, habits such as finger sucking, tongue thrusting, or lip sucking, dental malformations, genetics, proclinations, dental-skeletal discrepancies, and imperfect coalescence of interdental septum. Appropriate technique and material for effective treatment are based on time, physical, psychological, and economical limitations. Direct composite resins in diastema cases allow dentist and patient complete control of these limitations and formation of natural smile. Clinical Considerations. In this case report a maxillary midline diastema was closed with direct composite resin restorations in one appointment without any preparation. One bottle total etch adhesive was used and translucent/opaque composite resin shades were layered on mesial surfaces of the teeth that were isolated with rubber dam and Teflon bands. Finishing and polishing procedures were achieved by using polishing discs. Patient was informed for recalls for every 6 months. Conclusions. At one-year recall no sensitivities, discolorations, or fractures were detected on teeth and restorations. Direct composite resins seemed to be highly aesthetic and durable restorations that can satisfy patients as under the conditions of case presented.

High renewable content sandwich structures based on flax-basalt hybrids and biobased epoxy polymers

NASA Astrophysics Data System (ADS)

Colomina, S.; Boronat, T.; Fenollar, O.; Sánchez-Nacher, L.; Balart, R.

2014-05-01

In the last years, a growing interest in the development of high environmental efficiency materials has been detected and this situation is more accentuated in the field of polymers and polymer composites. In this work, green composite sandwich structures with high renewable content have been developed with core cork materials. The base resin for composites was a biobased epoxy resin derived from epoxidized vegetable oils. Hybrid basalt-flax fabrics have been used as reinforcements for composites and the influence of the stacking sequence has been evaluated in order to optimize the appropriate laminate structure for the sandwich bases. Core cork materials with different thickness have been used to evaluate performance of sandwich structures thus leading to high renewable content composite sandwich structures. Results show that position of basalt fabrics plays a key role in flexural fracture of sandwich structures due to differences in stiffness between flax and basalt fibers.

Modeling the Residual Stresses in Reactive Resins-Based Materials: a Case Study of Photo-Sensitive Composites for Dental Applications

DOE Office of Scientific and Technical Information (OSTI.GOV)

Grassia, Luigi; D'Amore, Alberto

Residual stresses in reactive resins-based composites are associated to the net volumetric contraction (shrinkage) arising during the cross-linking reactions. Depending on the restoration geometry (the ratio of the free surface area to the volume of the cavity) the frozen-in stresses can be as high as the strength of the dental composites. This is the main reason why the effectiveness and then the durability of restorations with composites remains quite lower than those realized with metal alloys based materials. In this paper we first explore the possibility to circumvent the mathematical complexity arising from the determination of residual stresses in reactivemore » systems three-dimensionally constrained. Then, the results of our modeling approach are applied to a series of commercially available composites showing that almost all samples develop residual stresses such that the restoration undergoes failure as soon as it is realized.« less

Repair bond strength in aged methacrylate- and silorane-based composites.

PubMed

Bacchi, Atais; Consani, Rafael Leonardo; Sinhoreti, Mario Alexandre; Feitosa, Victor Pinheiro; Cavalcante, Larissa Maria; Pfeifer, Carmem Silva; Schneider, Luis Felipe

2013-10-01

To evaluate the tensile bond strength at repaired interfaces of aged dental composites, either dimethacrylate- or silorane-based, when subjected to different surface treatments. The composites used were Filtek P60 (methacrylate-based, 3M ESPE) and Filtek P90 (silorane-based, 3M ESPE), of which 50 slabs were stored for 6 months at 37°C. The surface of adhesion was abraded with a 600-grit silicone paper and the slabs repaired with the respective composite, according to the following surface treatment protocols: G1: no treatment; G2: adhesive application; G3: silane + adhesive; G4: sandblasting (Al2O3) + adhesive; G5: sandblasting (Al2O3) + silane + adhesive. After 24-h storage in distilled water at 37°C, tensile bond strength (TBS) was determined in a universal testing machine (Instron 4411) at a crosshead speed of 0.5 mm/min. The original data were submitted to two-way ANOVA and Tukey's test (α = 5%). The methacrylate-based composite presented a statistically significantly higher repair potential than did the silorane-based resin (p = 0.0002). Of the surface treatments for the silorane-based composite, aluminum-oxide air abrasion and adhesive (18.5 ± 3.3MPa) provided higher bond strength than only adhesive application or the control group without surface treatment. For Filtek P60, the control without treatment presented lower repair strength than all other groups with surface treatments, which were statistically similar to each other. The interaction between the factors resin composite and surface treatment was significant (p = 0.002). For aged silorane-based materials, repairs were considered successful after sandblasting (Al2O3) and adhesive application. For methacrylate resin, repair was successful with all surface treatments tested.

Evaluation of the flexural strength and microhardness of provisional crown and bridge materials fabricated by different methods

PubMed Central

Digholkar, Shruti; Madhav, V. N. V.; Palaskar, Jayant

2016-01-01

Purpose: The purpose of this study was to evaluate and compare the flexural strength and microhardness of provisional restorative materials fabricated utilizing rapid prototyping (RP), Computer Assisted Designing and Computer Assisted Milling (CAD-CAM) and conventional method. Materials and Methods: Twenty specimens of dimensions 25 mm × 2 mm × 2 mm (ADA-ANSI specification #27) were fabricated each using: (1) Three dimensional (3D) printed light-cured micro-hybrid filled composite by RP resin group, (2) a milled polymethyl methacrylate (CH) using CAD-CAM (CC resin group), and (3) a conventionally fabricated heat activated polymerized CH resin group. Flexural strength and microhardness were measured and values obtained were evaluated. Results: The measured mean flexural strength values (MegaPascals) were 79.54 (RP resin group), 104.20 (CC resin group), and 95.58 (CH resin group). The measured mean microhardness values (Knoop hardness number) were 32.77 (RP resin group), 25.33 (CC resin group), and 27.36 (CH resin group). The analysis of variance (ANOVA) test shows that there is statistically significant difference in the flexural strength values of the three groups (P < 0.05). According to the pairwise comparison of Tukey's honest significant difference (HSD) test, flexural strength values of CC resin group and CH resin group were higher and statistically significant than those of the RP resin group (P < 0.05). However, there was no significant difference between flexural strength values of CC resin and CH resin group (P = 0.64). The difference in microhardness values of the three groups was statistically significant according to ANOVA as well as the intergroup comparison done using the Tukey's HSD (post hoc) test (P < 0.05). Conclusions: CC-based CH had the highest flexural strength whereas RP-based 3D printed and light cured micro-hybrid filled composite had the highest microhardness. PMID:27746595

ATR technique, an appropriate method for determining the degree of conversion in dental giomers

NASA Astrophysics Data System (ADS)

Prejmerean, Cristina; Prodan, Doina; Vlassa, Mihaela; Streza, Mihaela; Buruiana, Tinca; Colceriu, Loredana; Prejmerean, Vasile; Cuc, Stanca; Moldovan, Marioara

2016-12-01

Dental light-curing giomers were developed to combine the favourable properties of diacrylic resin composites (DRCs) and glass-ionomer cements (GICs) in a single material and to eliminate their inherent drawbacks. Giomers are characterized by their aesthetic appearance, high mechanical properties, adhesion to dental tissues as well as fluoride release and recharge abilities. The qualities of the giomers are greatly influenced by the level of conversion of the component resins. Infrared spectroscopy is one of the most largely used techniques for the determination of the degree of conversion in resin-based dental materials. However different results were obtained due to the performances of the used methods. The present work presents the determination of conversion degree in a series of dental copolymers and their corresponding giomers using transmission Fourier transform infrared spectroscopy (FTIR) and an attenuated total reflection technique (ATR) technique, respectively, the main aim being the study of the influence of the materials composition and of the light curing modes upon the achieved conversion in the cured giomers. Beautifil II commercial giomer was used as a control. A halogen lamp and a diode-blue LED lamp were used for the curing of the materials. The results showed that the composition of the resins greatly influenced the conversion. The highest conversions (up to 79%) were obtained in the case of the experimental giomers which contained the experimental Bis-GMA urethane analogue, followed by the Beautifil II giomer (61%) and experimental giomers based on commercial Bis-GMA (up to 50%), respectively. The resins light-cured by using the diode-blue LED lamp presented slightly higher conversions than the resins cured by halogen lamp. The study demonstrates the possibility to evaluate easily and reproducibly the conversion in light-curing composite materials with complex chemical composition and structure, particularly in the case of giomers by using the ATR technique.

Comparison of the Effects of Two Different Drinks on Microhardness of a Silorane-based Composite Resin.

PubMed

Sadat HashemiKamangar, Sedighe; Ghavam, Maryam; Mirkhezri, Zhina; Karazifard, Mohammad Javad

2015-09-01

Acidic foods and drinks can erode composite resins. Silorane-based composite is a new low shrinkage composite with higher hydrophobicity which might resist the erosive effect of beverages. The aim of this study was to determine the effects of 100% orange juice and non-alcoholic carbonated beer on microhardness of a silorane-based composite in comparison with two methacrylate-based composite resins. Ninety disc-shaped composite specimens were fabricated of Filtek P90, Filtek Z350 XT Enamel and Filtek Z250 (3M-ESPE) (n=30) and randomly divided into 3 subgroups of 10.Group 1 was immersed in distilled water, group 2 in 100% orange juice, and group 3 in non-alcoholic beer for 3 h/day. Primary, secondary and final Vickers microhardness tests were performed at the beginning of the study and 7 and 28 days later. Surface of 2 specimens in each group was evaluated under scanning electron microscope on day 28. Data were analyzed using repeated measures of ANOVA model (α=0.05). The primary and secondary microhardness of P90 was significantly lower than that of Z350, and Z250 (p< 0.001). Microhardness of Z350 was also lower than that of Z250 (p= 0.002). On day 28, microhardness of P90 was lower than Z250 and Z350 (p< 0.001); however, microhardness values of Z250 and Z350 were not significantly different (p= 0.054). Microhardness of specimens subjected to non-alcoholic beer was significantly lower than that of controls (p= 0.003). Meanwhile, the microhardness value of resins in orange juice was somewhere between the two mentioned values with no significant difference with any of them (p> 0.05). Although 28 days of immersion in 100% orange juice and non-alcoholic beer decreased the microhardness of all specimens, P90 experienced the greatest reduction of microhardness and non-alcoholic beer had the highest effect on reducing microhardness.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Gantayat, S., E-mail: subhra-gantayat@rediffmail.com; Rout, D.; Swain, S. K.

The effect of the functionalization of multiwalled carbon nanotube on the structure and electrical properties of composites was investigated. Samples based on epoxy resin with different weight percentage of MWCNTs were prepared and characterized. The interaction between MWCNT & epoxy resin was noticed by Fourier transform infrared spectroscopy (FTIR). The structure of functionalized multiwalled carbon nanotube (f-MWCNT) reinforced epoxy composite was studied by field emission scanning electron microscope (FESEM). The dispersion of f-MWCNT in epoxy resin was evidenced by high resolution transmission electron microscope (HRTEM). Electrical properties of epoxy/f-MWCNT nanocomposites were measured & the result indicated that the conductivity increasedmore » with increasing concentration of f-MWCNTs.« less

Influence of Bleaching Agents on Color and Translucency of Aged Resin Composites.

PubMed

Lago, Maristela; Mozzaquatro, Lisandra R; Rodrigues, Camila; Kaizer, Marina R; Mallmann, André; Jacques, Letícia B

2017-09-01

Evaluate the influence of two bleaching agents (16% carbamide peroxide-CP and 35% hydrogen peroxide-HP) on color and translucency of one resin composite (Filtek Z350 XT) in two opacities (enamel and dentin) previously aged in deionized water or red wine. Sixty specimens of each material were divided in two groups (n = 30): aged in water or red wine for 14 days. Then the specimens were divided in three subgroups (n = 10): control/no treatment, treated with 16% carbamide peroxide (Mix Night), treated with 35% hydrogen peroxide (Mix One). Color readings were performed 24 hours after polishing (baseline); after the 14 days of aging; and after bleaching treatment. Color coordinates CIE L*a*b* were measured using a spectrophotometer (SP60 X-Rite). Color change (CIEDE2000) and translucency parameter were calculated. Data were analyzed with repeated measures two-way ANOVA, and Student-Newman-Keuls tests (5%). Bleaching decreased color change in stained resin composites (aged in red wine), whereas increased it in non-stained enamel resin composites (aged in water). CP had better bleaching results with stained resin composites than HP. Translucency of non-stained dentin resin composite decreased with aging, but did not change with bleaching. For stained resin composites, aging caused reduced translucency, whereas bleaching increased it. Effective bleaching of discolored resin composites aged in an acidic and alcoholic media rich in staining agents was achieved, improving color and translucency. Carbamide peroxide showed better performance than hydrogen peroxide for the bleaching of stained resin composites. (J Esthet Restor Dent 29:368-377, 2017). © 2016 Wiley Periodicals, Inc.

Tensile bond strength of indirect composites luted with three new self-adhesive resin cements to dentin.

PubMed

Türkmen, Cafer; Durkan, Meral; Cimilli, Hale; Öksüz, Mustafa

2011-08-01

The aims of this study were to evaluate the tensile bond strengths between indirect composites and dentin of 3 recently developed self-adhesive resin cements and to determine mode of failure by SEM. Exposed dentin surfaces of 70 mandibular third molars were used. Teeth were randomly divided into 7 groups: Group 1 (control group): direct composite resin restoration (Alert) with etch-and-rinse adhesive system (Bond 1 primer/adhesive), Group 2: indirect composite restoration (Estenia) luted with a resin cement (Cement-It) combined with the same etch-and-rinse adhesive, Group 3: direct composite resin restoration with self-etch adhesive system (Nano-Bond), Group 4: indirect composite restoration luted with the resin cement combined with the same self-etch adhesive, Groups 5-7: indirect composite restoration luted with self-adhesive resin cements (RelyX Unicem, Maxcem, and Embrace WetBond, respectively) onto the non-pretreated dentin surfaces. Tensile bond strengths of groups were tested with a universal testing machine at a constant speed of 1 mm/min using a 50 kgf load cell. Results were statistically analyzed by the Student's t-test. The failure modes of all groups were also evaluated. The indirect composite restorations luted with the self-adhesive resin cements (groups 5-7) showed better results compared to the other groups (p<0.05). Group 4 showed the weakest bond strength (p>0.05). The surfaces of all debonded specimens showed evidence of both adhesive and cohesive failure. The new universal self-adhesive resins may be considered an alternative for luting indirect composite restorations onto non-pretreated dentin surfaces.

Surface discoloration of composite resins: Effects of staining and bleaching.

PubMed

Poggio, Claudio; Beltrami, Riccardo; Scribante, Andrea; Colombo, Marco; Chiesa, Marco

2012-09-01

The purpose of this in vitro study was to evaluate surface discoloration of three microhybrid composite resins (Esthet•X HD, Clearfil AP-X, Gradia Direct) and five nanohybrid composite resins (Ceram•X, GC Kalore, G-aenial, Grandio, GrandioSO), after staining and bleaching procedures. The composite resins were polymerized with a curing light (Celalux II, Voco, Cuxhaven, Germany) into 160 silicon molds (6,4 mm in diameter and 2 mm in thickness) to obtain identical specimens. Twenty samples for each composite resin were prepared. The specimens were polished using an automated polishing machine with the sequence of 600-, 800-, 1000-grit abrasive paper under water irrigation. The specimens were immersed in tea and distilled water: the specimens were dipped for 20 min, once a day (every 24 h), for 14 days into the drinks. The specimens were then bleached with carbamide peroxide at 17% (Perfect Bleach-Voco). The color of specimens was measured with a spectrophotometer according to the CIE L(*)a(*)b(*) system after light-polymerization of composite resin specimens, after 7 days, after 14 days, and after bleaching. The color difference h index (DEab(*)) between each measurement was calculated. Statistical analysis was made using analysis of variance (ANOVA). All specimens showed a significant increase in staining with a similar trend and no significant differences between microhybrid and nanohybrid composite resins. After whitening procedures, materials tested showed both significant and unsignificant differences of the h index. Microhybrid and nanohybrid composite resins had similar in vitro surface discoloration in tea. After bleaching, discoloration was removed from some composite resins tested.

Surface discoloration of composite resins: Effects of staining and bleaching

PubMed Central

Poggio, Claudio; Beltrami, Riccardo; Scribante, Andrea; Colombo, Marco; Chiesa, Marco

2012-01-01

Background: The purpose of this in vitro study was to evaluate surface discoloration of three microhybrid composite resins (Esthet•X HD, Clearfil AP-X, Gradia Direct) and five nanohybrid composite resins (Ceram•X, GC Kalore, G-aenial, Grandio, GrandioSO), after staining and bleaching procedures. Materials and Methods: The composite resins were polymerized with a curing light (Celalux II, Voco, Cuxhaven, Germany) into 160 silicon molds (6,4 mm in diameter and 2 mm in thickness) to obtain identical specimens. Twenty samples for each composite resin were prepared. The specimens were polished using an automated polishing machine with the sequence of 600-, 800-, 1000-grit abrasive paper under water irrigation. The specimens were immersed in tea and distilled water: the specimens were dipped for 20 min, once a day (every 24 h), for 14 days into the drinks. The specimens were then bleached with carbamide peroxide at 17% (Perfect Bleach-Voco). The color of specimens was measured with a spectrophotometer according to the CIE L*a*b* system after light-polymerization of composite resin specimens, after 7 days, after 14 days, and after bleaching. The color difference h index (DEab*) between each measurement was calculated. Statistical analysis was made using analysis of variance (ANOVA). Results: All specimens showed a significant increase in staining with a similar trend and no significant differences between microhybrid and nanohybrid composite resins. After whitening procedures, materials tested showed both significant and unsignificant differences of the h index. Conclusions: Microhybrid and nanohybrid composite resins had similar in vitro surface discoloration in tea. After bleaching, discoloration was removed from some composite resins tested. PMID:23559921

DOE Office of Scientific and Technical Information (OSTI.GOV)

Madhukar, M. S.; Martovetsky, N. N.

Large superconducting electromagnets used in fusion reactors utilize a large amount of glass/epoxy composite for electrical insulation and mechanical and thermal strengths. Moreover, the manufacture of these magnets involves wrapping each superconducting cable bundle with dry glass cloth followed by the vacuum-assisted resin transfer molding of the entire magnet. Due to their enormous size (more than 100 tons), it requires more than 40 h for resin impregnation and the subsequent pressure cycles to ensure complete impregnation and removal of any trapped air pockets. Diglycidyl ether of bisphenol F epoxy resin cross-linked with methyltetrahydrophthalic anhydride with an accelerator has been shownmore » to be a good candidate for use in composite parts requiring long impregnation cycles. Viscosity, gel time, and glass transition temperature of four resin-blends of diglycidyl ether of bisphenol F resin system were monitored as a function of time and temperature with an objective to find the blend that provides a working window longer than 40h at low viscosity without lowering its glass transition temperature. A resin-blend in the weight ratios of resin:hardener:accelerator=100:82:0.125 is shown to provide more than 60h at low resin viscosity while maintaining the same glass transition temperature as obtained with previously used resin-blends, based on the results.« less

Differences in interfacial bond strengths of graphite fiber-epoxy resin composites

NASA Technical Reports Server (NTRS)

Needles, H. L.

1985-01-01

The effect of epoxy-size and degree of cure on the interfacial bonding of an epoxy-amine-graphite fiber composite system is examined. The role of the fiber-resin interface in determining the overall mechanical properties of composites is poorly understood. A good interfacial adhesive bond is required to achieve maximum stress transfer to the fibers in composites, but at the same time some form of energy absorbing interfacial interaction is needed to achieve high fracture toughening. The incompatibility of these two processes makes it important to understand the nature and basic factors involved at the fiber-resin interface as stress is applied. The mechanical properties including interlaminar shear values for graphite fiber-resin composites are low compared to glass and boron-resin composites. These differences have been attributed to poor fiber-matrix adhesion. Graphite fibers are commonly subjected to post-treatments including application of organic sizing in order to improve their compatibility with the resin matrix and to protect the fiber tow from damage during processing and lay-up. In such processes, sized graphite fiber tow is impregnated with epoxy resin and then layed-up i nto the appropriate configuration. Following an extended ambient temperature cure, the graphite-resin composite structure is cured at elevated temperature using a programmed temperature sequence to cure and then cool the product.

Fluorine analysis of human dentin surrounding resin composite after fluoride application by μ-PIGE/PIXE analysis

NASA Astrophysics Data System (ADS)

Okuyama, Katsushi; Komatsu, Hisanori; Yamamoto, Hiroko; Pereira, Patricia N. R.; Bedran-Russo, Ana K.; Nomachi, Masaharu; Sato, Takahiro; Sano, Hidehiko

2011-10-01

The use of fluoride for the prevention of caries is based on the transformation of hydroxylapatite to fluoroapatite in the presence of fluoride ions, thereby strengthening tooth structure. Adhesion of dentin and resin composite (tooth-colored restoration material) requires a dentin bonding system, since resin composite is not able to adhere to dentin directly. Demineralization of dentin by acid etching is an important step in the dentin bonding system, however, demineralization also introduces weaknesses in tooth structure. If the demineralized dentin could be strengthened by the application of fluoride, then the dentin-resin composite bond strength might also improve. To test this hypothesis, the present study evaluated the influence of fluoride applications on the strength of the dentin-resin composite bond by (1) tensile strength testing analyses, (2) SEM analyses of tooth structure, and (3) detection of calcium (Ca) and fluorine (F) distribution patterns by micro proton-induced X-ray emission (μ-PIXE) and micro proton-induced gamma-ray emission (μ-PIGE) analyses conducted at the Takasaki Ion Accelerators for Advanced Radiation Application (TIARA) at the Takasaki Advanced Radiation Research Institute (TARRI). In this study, the dentin in extracted human molars was exposed by grinding and the dentin was etched with 35% phosphoric acid. Fluoride was applied at two concentrations, 0.022% (100 ppm F) and 2.21% (10,000 ppm F) NaF solution, for two time periods, 30 and 60 s, prior to bonding the resin composite with the treated dentin. Controls were prepared in the same manner, but without the fluoride application. Bond strength was measured with a micro-tensile testing unit, and the fluorine and calcium distributions at the interface between dentin and resin composite were detected by μ-PIGE and μ-PIXE analysis, respectively. Results indicate that the 10,000 ppm F applications resulted in higher bond strengths than observed in either the 100 ppm F applications or the control group. In addition, PIGE analyses showed high concentrations of fluorine in the hybrid bonding layer of the 10,000 ppm F samples, suggesting that the fluorine contributes to the strength of the dentin-resin composite bond. Detection of fluoroapatite within the hybrid bonding layer suggests that bond strength involves remineralization processes.

Nano-Particle Enhanced Polymer Materials for Space Flight Applications

NASA Technical Reports Server (NTRS)

Criss, Jim M., Jr.; Powell, William D.; Connell, John W.; Stallworth-Bordain, Yemaya; Brown, Tracy R.; Mintz, Eric A.; Schlea, Michelle R.; Shofne, Meisha L.

2009-01-01

Recent advances in materials technology both in polymer chemistry and nano-materials warrant development of enhanced structures for space flight applications. This work aims to develop spacecraft structures based on polymer matrix composites (PMCs) that utilize these advancements.. Multi-wall carbon nano-tubes (MWCNTs) are expected ·to increase mechanical performance, lower coefficient of thermal expansion (CTE), increase electrical conductivity (mitigate electrostatic charge), increase thermal conductivity, and reduce moisture absorption of the resultant space structures. In this work, blends of MWCNTs with PETI-330 were prepared and characterized. The nano-reinforced resins were then resin transfer molded (RTM) into composite panels using M55J carbon fabric and compared to baseline panels fabricated from a cyanate ester (RS-3) or a polyimide (PETI-330) resin containing no MWCNTs. In addition, methods of pre-loading the fabric with the MWCNTs were also investigated. The effects of the MWCNTs on the resin processing properties and on the composite end-use properties were also determined.

An in vitro study of anticariogenic compounds incorporated into Bis-GMA/TEGDMA copolymer

NASA Astrophysics Data System (ADS)

Pilly Yadaiah, Vinay Kumar

Composite resins continue to evolve and are increasingly favoured by the people. However, drawbacks such as decreased longevity, secondary caries and costs make choosing composites a dilemma. This study evaluated drug release, inhibitory growth against Streptococcus mutans and drug stability of epigallocatechin-gallate (EGCg) incorporated into dental copolymer compared to resins containing chlorhexidine (CHX). Resin discs (5mm x 3mm) were prepared from 70 mol% Bis-GMA and 30 mol% TEGDMA comonomers containing: placebo, CHX and EGCg. Two corresponding concentrations in weight% of each drug for 0.5 and 1.0 x MIC were incorporated into paste resins and tested at time points: 24 hours, 7 days, 30 days, 60 days and 90 days. There is a significant difference in the 90 days drug delivery and bacterial inhibition among different drugs and drug ratios, which showed stability after 90 days. The results indicate that drug-based composites may reduce bacterial growth, which may improve its longevity.

Evaluation of the Shear Bond Strength of Composite Resin to Wet and Dry Enamel Using Dentin Bonding Agents Containing Various Solvents

PubMed Central

Ramarao, Sathyanarayanan; John, Bindu Meera; Rajesh, Praveen; Swatha, S

2017-01-01

Introduction Bonding of composite resin to dentin mandates a wet substrate whereas, enamel should be dry. This may not be easily achievable in intracoronal preparations where enamel and dentin are closely placed to each other. Therefore, Dentin Bonding Agents (DBA) are recommended for enamel and dentinal bonding, where enamel is also left moist. A research question was raised if the “enamel-only” preparations will also benefit from wet enamel bonding and contemporary DBA. Aim The aim of this study was to compare the shear bond strengths of composite resin, bonded to dry and wet enamel using fifth generation DBA (etch and rinse system) containing various solvents such as ethanol/water, acetone and ethanol. Materials and Methods The crowns of 120 maxillary premolars were split into buccal and lingual halves. They were randomly allocated into four groups of DBA: Group 1-water/ethanol based, Group 2-acetone based, Group 3-ethanol based, Group 4-universal bonding agent (control group). The buccal halves and lingual halves were bonded using the wet bonding and dry bonding technique respectively. After application of the DBAs and composite resin build up, shear bond strength testing was done. Results Group 1 (ethanol/water based ESPE 3M, Adper Single Bond) showed highest bond strength of (23.15 MPa) in dry enamel. Group 2 (acetone based Denstply, Prime and Bond NT, showed equal bond strength in wet and dry enamel condition (18.87 MPa and 18.02 MPa respectively). Conclusion Dry enamel bonding and ethanol/water based etch and rinse DBA can be recommended for “enamel-only” tooth preparations. PMID:28274042

Versatile composite resins simplifying the practice of restorative dentistry.

PubMed

Margeas, Robert

2014-01-01

After decades of technical development and refinement, composite resins continue to simplify the practice of restorative dentistry, offering clinicians versatility, predictability, and enhanced physical properties. With a wide range of products available today, composite resins are a reliable, conservative, multi-functional restorative material option. As manufacturers strive to improve such properties as compression strength, flexural strength, elastic modulus, coefficient of thermal expansion, water sorption, and wear resistance, several classification systems of composite resins have been developed.

The management of defective resin composite restorations: current trends in dental school teaching in Japan.

PubMed

Lynch, C D; Hayashi, M; Seow, L L; Blum, I R; Wilson, N H F

2013-01-01

The aim of this article is to investigate the contemporary teaching of the management of defective direct resin composite restorations in dental schools in Japan. A questionnaire relating to the teaching of the management of defective resin composite restorations was developed and e-mailed to 29 dental schools in Japan in 2010. Completed responses were received from 19 of the 29 invited schools (response rate = 66%). Eighteen schools (95%) report that they included the teaching of repair of direct defective resin composite restorations in their dental school programs. Thirteen schools reported that they included both clinical and didactic instruction on the repair of direct resin composite restorations. Fourteen schools did not teach any mechanical roughening of the exposed resin composite restoration surface before undertaking a repair. The most commonly reported treatment was acid etching with phosphoric acid (12 schools). The most commonly taught material for completing repairs was a flowable resin composite (16 schools). The teaching of repair of defective resin composite restorations is well established within many Japanese dental schools, to a greater extent than in some other regions of the world. The impact of this teaching on subsequent clinical practices in Japan should be investigated. Furthermore, it is concluded that there is a need for much stronger leadership in operative and conservative dentistry, ideally at the global level, to resolve differences in key aspects of operative procedures such as repairs.

Effects of the peracetic acid and sodium hypochlorite on the colour stability and surface roughness of the denture base acrylic resins polymerised by microwave and water bath methods.

PubMed

Fernandes, Flavio H C N; Orsi, Iara A; Villabona, Camilo A

2013-03-01

This study evaluated the surface roughness (Ra) and color stability of acrylic resin colors (Lucitone 550, QC-20 and Vipi-Wave) used for fabricating bases for complete, removable dentures, overdentures and prosthetic protocol after immersion in chemical disinfectants (1% sodium hypochlorite and 2% peracetic acid) for 30 and 60 minutes. Sixty specimens were made of each commercial brand of resin composite, and divided into 2 groups according to the chemical disinfectants. Specimens had undergone the finishing and polishing procedures, the initial color and roughness measurements were taken (t=0), and after this, ten test specimens of each commercial brand of resin composite were immersed in sodium hypochlorite and ten in peracetic acid, for 30 and 60 minutes, with measurements being taken after each immersion period. These data were submitted to statistical analysis. There was evidence of an increase in Ra after 30 minutes immersion in the disinfectants in all the resins, with QC-20 presenting the highest Ra values, and Vipi-Wave the lowest. After 60 minutes immersion in the disinfectants all the resins presented statistically significant color alteration. Disinfection with 1% sodium hypochlorite and peracetic acid altered the properties of roughness and color of the resins. © 2012 The Gerodontology Society and John Wiley & Sons A/S.

Composite resins in 2013: an update on their progress.

PubMed

Radz, Gary M

2013-01-01

Having steadily evolved and improved over the past several decades, composite resins are providing clinicians with an increased array of options for successfully restoring teeth in a minimally invasive manner. Numerous advances compared to early composite resin systems, such as increased shade availability, reduced polymerization shrinkage, and the development of nanoparticles, have enabled composite resins to offer long-term esthetic solutions for patients. This article summarizes the changes that have occurred, discusses popular applications for the use of composite materials, and presents brief case studies demonstrating their capabilities.

Silane surface modification effects on the electromagnetic properties of phosphatized iron-based SMCs

NASA Astrophysics Data System (ADS)

Fan, Liang-Fang; Hsiang, Hsing-I.; Hung, Jia-Jing

2018-03-01

It is difficult to achieve homogeneous phosphatized iron powder dispersion in organic resins during the preparation of soft magnetic composites (SMCs). Inhomogeneous iron powder mixing in organic resins generally leads to the formation of micro-structural defects in SMCs and hence causes the magnetic properties to become worse. Phosphatized iron powder dispersion in organic resins can be improved by coating the phosphatized iron powder surfaces with a coupling agent. This study investigated the (3-aminopropyl) triethoxysilane (APTES) surface modification effects on the electromagnetic properties of phosphatized iron-based soft magnetic composites (SMCs). The results showed that the phosphatized iron powder surface can be modified using APTES to improve the phosphatized iron powder and epoxy resin compatibility and hence enhance phosphate iron powder epoxy mixing. The tensile strength, initial permeability, rated current under DC-bias superposition and magnetic loss in SMCs prepared using phosphatized iron powders can be effectively improved using APTES surface modification, which provides a promising candidate for power chip inductor applications.

Research on Recycling Mixed Wastes Based on Fiberglass and Organic Resins

NASA Astrophysics Data System (ADS)

Platon, M. A.; Ştef, M.; Popa, C.; Tiuc, A. E.; Nemeş, O.

2018-06-01

In recycling, according to principles of Directive 2008/98/EC of the European Parliament and of the Council on waste, research is upheld for achieving innovative technologies for reuse and keep as long it is possible, in economic chain, a waste. The aim of this research is to study and test a new composite material based on fiberglass waste mixed with organic resins with large application in the industry but not limited to this. Fiberglass is a material widely used for reinforcement of composite materials. As waste, fiberglass was less studied for ways to be reused. Filling fiberglass mixed with organic resins as PMMA and epoxy resins possess proper physical features for thermoforming. Three mixes are studied: fiberglass with PMMA, fiberglass with PMMA and rubber granules or sawdust. Samples will be tested for to define the mechanical and chemical behavior to have a complete description of the material. Analyzing the results can be concluded that mixes are suitable for board production, with improved features, compared with equivalent products on the market.

Metabolomics Reveals the Origins of Antimicrobial Plant Resins Collected by Honey Bees

PubMed Central

Wilson, Michael B.; Spivak, Marla; Hegeman, Adrian D.; Rendahl, Aaron; Cohen, Jerry D.

2013-01-01

The deposition of antimicrobial plant resins in honey bee, Apis mellifera, nests has important physiological benefits. Resin foraging is difficult to approach experimentally because resin composition is highly variable among and between plant families, the environmental and plant-genotypic effects on resins are unknown, and resin foragers are relatively rare and often forage in unobservable tree canopies. Subsequently, little is known about the botanical origins of resins in many regions or the benefits of specific resins to bees. We used metabolomic methods as a type of environmental forensics to track individual resin forager behavior through comparisons of global resin metabolite patterns. The resin from the corbiculae of a single bee was sufficient to identify that resin's botanical source without prior knowledge of resin composition. Bees from our apiary discriminately foraged for resin from eastern cottonwood (Populus deltoides), and balsam poplar (P. balsamifera) among many available, even closely related, resinous plants. Cottonwood and balsam poplar resin composition did not show significant seasonal or regional changes in composition. Metabolomic analysis of resin from 6 North American Populus spp. and 5 hybrids revealed peaks characteristic to taxonomic nodes within Populus, while antimicrobial analysis revealed that resin from different species varied in inhibition of the bee bacterial pathogen, Paenibacillus larvae. We conclude that honey bees make discrete choices among many resinous plant species, even among closely related species. Bees also maintained fidelity to a single source during a foraging trip. Furthermore, the differential inhibition of P. larvae by Populus spp., thought to be preferential for resin collection in temperate regions, suggests that resins from closely related plant species many have different benefits to bees. PMID:24204850

Room Temperature Curing Resin Systems for Graphite/Epoxy Composite Repair.

DTIC Science & Technology

1979-12-01

ROOM TEMPERATURE CURING RESIN SYSTEMS FOR GRAPHITE/EPOXY COMPOS--ETC(UI DEC 79 0 J CRABTREE N62269-79-C-G224 UNCLASSIFIE O80-46 NADC -781 1-6 NL END...Room Temperature Curing Resin Sys-U3 linal for Graphite/Epoxy Composite Repair •.Dec *79 NOR- -46h: V111IT NUM8ER(s) 4362269-79- ,722 S. PERFORMING...repair, composite repair room temperature cure resin , moderate temperature cure resins , epoxies, adhesives, vinyl eater polymers, anaerobic curing polymers

Mechanical behavior of bioactive composite cements consisting of resin and glass-ceramic powder in a simulated body fluid: effect of silane coupling agent.

PubMed

Miyata, N; Matsuura, W; Kokubo, T; Nakamura, T

2004-09-01

Time-dependent strength behavior was investigated for bisphenol-a-glycidyl methacrylate/triethylene glycol dimethacrylate (Bis-GMA/TEGDMA) resin cements combined with glass-ceramic A-W filler treated with various kinds of silane coupling agents. The fracture strength of the composite resin cements was measured by three-point bending as a function of stressing rate in a simulated body fluid (SBF), and thereby the stress-corrosion susceptibility constant was evaluated. The fracture strength was found to depend on the kind of coupling agent used. For the present Bis-GMA/TEGDMA resin, the silane coupling agents without hydrophilic amine groups can be used to obtain good adhesion between resin and A-W filler owing to their nature of co-polymerizing with the resin. On the other hand, all the composite resin cements showed nearly the same degree of stress-corrosion susceptibility whether the A-W fillers were treated or untreated with silane coupling agents. This means that the stress-corrosion susceptibility of the present composite cements is predominantly affected by that of the matrix resin. Thus, the microcrack formation and growth at the resin matrix near particle - resin interface were thought to determine overall time-dependent strength behavior of the composite cements.

An investigation of sustainable and recyclable composites for structural applications

NASA Astrophysics Data System (ADS)

Moller, Johannes Paul

Motivated by the need for more sustainable materials in general and the issues concerning the life cycle of wind turbine blades in particular, the focus of this research work is to better understand what is needed to create high-performance bio-epoxy composites, and to explore their repair and recycling. To further these ends, glass fiber reinforced composites were manufactured using an epoxidized linseed oil (ELO) based matrix cured with various anhydride curatives and catalysts. Based on mechanical properties measurements of these materials, ELO cured with methyltetrahydrophthalic anhydride (MTHPA) and catalyzed with 2-ethyl-4-methylimidazole (2E4MI) yielded the best performance among all fou iulations tested, and avoided the void foiniation issues associated with the use of 1,8-diazabicyclo[5.4.0]undec-7-ene (DBU) as a catalyst. In addition to the mechanical characterization of the composite, the applicability and processability of a range of bio-epoxy formulations was evaluated in the context of for vacuum-assisted resin transfer molding (VARTM). In particular, a new methodology for assessing the infusability of a resin was developed and the bioepoxy formulations were demonstrated to be more amenable to resin infusion than a conventional control. Having demonstrated the potential for bio-based resins to produce more sustainable high-performance composites, further studies were carried out to address end-of-life issues. Here different approaches for healing and recycling of epoxy vitrimers (epoxies rendered reworkable by the inclusion of a transesterification catalyst) and their composites were introduced and proof-of-concept experiments were performed. By exposing a fractured glass fiber epoxy vitrimer composite to elevated temperatures and pressure for times on the order often minutes, a healing efficiency of 55% was achieved. Additionally, two different recycling approaches were explored. First, mechnical recycling (grinding followed by reconsolidation via compression molding) was successfully demonstrated for epoxy vitrimers and epoxy vitrimer composites. Dynamic thermomechanical and quasi-static tensile data vs. particle size indicate that the finest powder yielded the best results. In addition to mechanical recycling, a new approach to chemical recycling via fiber reclamation was introduced. Here, removal of the matrix was achieved via high temperature transesterification of the resin in a large excess of an alcohol solvent, and new continuously reinforced composites were succesfully prepared from the reclaimed fibers.

Argon Ion Laser Polymerized Acrylic Resin: A Comparative Analysis of Mechanical Properties of Laser Cured, Light Cured and Heat Cured Denture Base Resins

PubMed Central

Murthy, S Srinivasa; Murthy, Gargi S

2015-01-01

Background: Dentistry in general and prosthodontics in particular is evolving at greater pace, but the denture base resins poly methyl methacrylate. There has been vast development in modifying chemically and the polymerization techniques for better manipulation and enhancement of mechanical properties. One such invention was introduction of visible light cure (VLC) denture base resin. Argon ion lasers have been used extensively in dentistry, studies has shown that it can polymerize restorative composite resins. Since composite resin and VLC resin share the same photo initiator, Argon laser is tested as activator for polymerizing VLC resin. In the Phase 1 study, the VLC resin was evaluated for exposure time for optimum polymerization using argon ion laser and in Phase 2; flexural strength, impact strength, surface hardness and surface characteristics of laser cured resin was compared with light cure and conventional heat cure resin. Materials and Methods: Phase 1; In compliance with American Dental Association (ADA) specification no. 12, 80 samples were prepared with 10 each for different curing time using argon laser and evaluated for flexural strength on three point bend test. Results were compared to established performance requirement specified. Phase 2, 10 specimen for each of the mechanical properties (30 specimen) were polymerized using laser, visible light and heat and compared. Surface and fractured surface of laser, light and heat cured resins were examined under scanning electron microscope (SEM). Results: In Phase 1, the specimen cured for 7, 8, 9 and 10 min fulfilled ADA requirement. 8 min was taken as suitable curing time for laser curing. Phase 2 the values of mechanical properties were computed and subjected to statistical analysis using one-way ANOVA and Tukey post-hoc test. The means of three independent groups showed significant differences between any two groups (P < 0.001). Conclusion: Triad VLC resin can be polymerized by argon ion laser with 1 W/mm2 power and exposure time of 8 min to satisfy ADA specification. Impact strength, surface hardness of laser cure was better than light cure and heat cure resin. Flexural strength of light cure was better than laser cure and heat cure resin. The SEM study showed similar density on surface, the fractured surface of heat cure resin was dense and compact. PMID:26124596

Effect of different bleaching strategies on microhardness of a silorane-based composite resin.

PubMed

Bahari, Mahmoud; Savadi Oskoee, Siavash; Mohammadi, Narmin; Ebrahimi Chaharom, Mohammad Esmaeel; Godrati, Mostafa; Savadi Oskoee, Ayda

2016-01-01

Background. Dentists' awareness of the effects of bleaching agents on the surface and mechanical properties of restorative materials is of utmost importance. Therefore, this in vitro study was undertaken to investigate the effects of different bleaching strategies on the microhardness of a silorane-based composite resin. Methods. Eighty samples of a silorane-based composite resin (measuring 4 mm in diameter and 2 mm in thickness) were prepared within acrylic molds. The samples were polished and randomly assigned to 4 groups (n=20). Group 1 (controls) were stored in distilled water for 2 weeks. The samples in group 2 underwent a bleaching procedure with 15% carbamide peroxide for two weeks two hours daily. The samples in group 3 were bleached with 35% hydrogen peroxide twice 5 days apart for 30 minutes each time. The samples in group 4 underwent a bleaching procedure with light-activated 35% hydrogen peroxide under LED light once for 40 minutes. Then the microhardness of the samples was determined using Vickers method. Data were analyzed with one-way ANOVA and post hoc Tukey tests (P < 0.05). Results. All the bleaching agents significantly decreased microhardness compared to the control group (P < 0.05). In addition, there were significant differences in microhardness between groups 2 and 4 (P = 0.001) and between groups 3 and 4 (P<0.001). However, no significant differences were detected in microhardness between groups 2 and 3 (P > 0.05). Conclusion. Bleaching agents decreased microhardness of silorane-based composite resin restorations, the magnitude of which depending on the bleaching strategy used.

Effect of surface preparation with Nd:YAG and Er,Cr:YSGG lasers on the repair bond strength of lithium disilicate glass ceramic to a silorane-based composite resin.

PubMed

Ebrahimi Chaharom, Mohammad Esmaeel; Pournaghi Azar, Fatemeh; Mohammadi, Narmin; Nasiri, Rezvan

2018-01-01

Background. This study was undertaken to evaluate the repair bond strength of lithium disilicate glass ceramic to a silorane-based composite resin after surface preparation with Nd:YAG and Er,Cr:YSGG lasers. Methods. A total of 102 lithium disilicate glass ceramic samples (IPS e.max Press), measuring 5 mm in diameter and 4 mm in thickness, were randomly assigned to 6 groups (n=17): group 1, no surface preparation (control); group 2, acid etching with 9.5% hydrofluoric acid (HF); group 3, surface preparation with 4.5-W Nd:YAG laser; group 4, surface preparation with 6-W Nd:YAG laser; group 5, surface preparation with 1.5-W Er,Cr:YSGG laser; and group 6, surface preparation with 6-W Er,Cr:YSGG laser. After preparation of surfaces and application of silane, all the samples were repaired with the use of a silorane-based composite resin, followed by storage in distilled water at a temperature of 37°C for 24 hours and thermocycling. Finally, the samples were subjected to a shearing bond strength test; the fracture modes were determined under a stereomi-croscope. Results. There were significant differences between the HF group and the other groups (P=0.000). Two-by-two comparisons of the other groups revealed no significant differences (P>0.05). Conclusion. Use of HF proved the most effective surface preparation technique to increase the repair bond strength between lithium disilicate glass ceramic and silorane-based composite resin; compared to the control group.

Liquid monobenzoxazine based resin system

DOEpatents

Tietze, Roger; Nguyen, Yen-Loan; Bryant, Mark

2014-10-07

The present invention provides a liquid resin system including a liquid monobenzoxazine monomer and a non-glycidyl epoxy compound, wherein the weight ratio of the monobenzoxazine monomer to the non-glycidyl epoxy compound is in a range of about 25:75 to about 60:40. The liquid resin system exhibits a low viscosity and exceptional stability over an extended period of time making its use in a variety of composite manufacturing methods highly advantageous.

Preparation and characterization of silane-modified SiO2 particles reinforced resin composites with fluorinated acrylate polymer.

PubMed

Liu, Xue; Wang, Zengyao; Zhao, Chengji; Bu, Wenhuan; Na, Hui

2018-04-01

A series of fluorinated dental resin composites were prepared with two kinds of SiO 2 particles. Bis-GMA (bisphenol A-glycerolate dimethacrylate)/4-TF-PQEA (fluorinated acrylate monomer)/TEGDMA (triethylene glycol dimethacrylate) (40/30/30, wt/wt/wt) was introduced as resin matrix. SiO 2 nanopartices (30nm) and SiO 2 microparticles (0.3µm) were silanized with 3-methacryloxypropyl trimethoxysilane (γ-MPS) and used as fillers. After mixing the resin matrix with 0%, 10%, 20%, 30% SiO 2 nanopartices and 0%, 10%, 20%, 30%, 40%, 50% SiO 2 microparticles, respectively, the fluorinated resin composites were obtained. Properties including double bond conversion (DC), polymerization shrinkage (PS), water sorption (W p ), water solubility (W y ), mechanical properties and cytotoxicity were investigated in comparison with those of neat resin system. The results showed that, filler particles could improve the overall performance of resin composites, particularly in improving mechanical properties and reducing PS of composites along with the addition of filler loading. Compared to resin composites containing SiO 2 microparticles, SiO 2 nanoparticles resin composites had higher DC, higher mechanical properties, lower PS and lower W p under the same filler content. Especially, 50% SiO 2 microparticles reinforced resins exhibited the best flexural strength (104.04 ± 7.40MPa), flexural modulus (5.62 ± 0.16GPa), vickers microhardness (37.34 ± 1.13 HV), compressive strength (301.54 ± 5.66MPa) and the lowest polymerization (3.42 ± 0.22%). Copyright © 2018 Elsevier Ltd. All rights reserved.

Biofilm inhibition by an experimental dental resin composite containing octenidine dihydrochloride.

PubMed

Rupf, Stefan; Balkenhol, Markus; Sahrhage, Tim O; Baum, Alexandra; Chromik, Julia N; Ruppert, Klaus; Wissenbach, Dirk K; Maurer, Hans H; Hannig, Matthias

2012-09-01

The aim of the present study was to investigate an antimicrobial additive containing experimental resin composite with regards to its impact on biofilm formation under oral conditions. Biofilms were established in situ on composite specimens (n=192) which contained octenidine dihydrochloride (ODH, 3 wt.% or 6 wt.%). Samples without antimicrobial additive served as control (n=96). Composite specimens were fixed on custom made splints and exposed to the oral cavity of six healthy volunteers for three or seven days. Biofilm formation was assessed by scanning electron microscopy (SEM) and fluorescence microscopy (FM). The biofilm formation was significantly reduced on ODH containing samples compared to controls after three as well as after seven days in situ. FM evaluation additionally showed a lower viability of the reduced biofilms for both ODH concentrations. During this short term investigation, incorporation of ODH into resin based composite materials caused biofilm inhibiting effects in situ. Copyright © 2012 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Cytotoxicity and cytokine expression induced by silorane and methacrylate-based composite resins

PubMed Central

LONGO, Daniele Lucca; PAULA-SILVA, Francisco Wanderley Garcia; FACCIOLI, Lucia Helena; GATÓN-HERNÁNDEZ, Patrícia Maria; de QUEIROZ, Alexandra Mussolino; da SILVA, Léa Assed Bezerra

2016-01-01

ABSTRACT The successful use of composite resins in Dentistry depends on physicochemical properties, but also on the biological compatibility of resins, because of the close association between pulp and dentin. Objective The aim of this study was to evaluate cytotoxicity and cytokine production induced by light-cured or non-light-cured methacrylate-based and silorane composite resins in RAW 264.7 macrophages. Material and Methods Cells were stimulated with the extracts from light-cured or non-light-cured composite resins. After incubation for 24 h, cytotoxicity was assessed with the lactate dehydrogenase (LDH) and methyl thiazolyl tetrazolium (MTT) assays, and total protein was quantified using the Lowry method. TNF-α detection was examined with an enzyme-linked immunosorbent assay (ELISA) conducted with cell supernatants after cell stimulation for 6, 12, and 24 h. Data were analyzed using one-way analysis of variance (ANOVA) and Tukey’s post hoc test (α=0.05). Results KaloreTM and FiltekTM Silorane were cytotoxic with or without light curing (p<0.05) after 24 h of incubation. KaloreTM stimulated the early production of TNF-α in comparison with control (p<0.05), whereas FiltekTM Silorane did not affect TNF-α levels after 6 and 12 h (p>0.05). However, after 24 h FiltekTM Silorane inhibited the production of TNF-α (p<0.05). Conclusions KaloreTM and FiltekTM Silorane were cytotoxic regardless of light curing. The extract obtained from KaloreTM after 15 days of incubation stimulated the production of TNF-α, unlike that obtained from FiltekTM Silorane. PMID:27556204

An in vitro study of the effect of different restorative materials on the reliability of a veneering porcelain.

PubMed

Anderson, Matthew R; Chung, Kwok-Hung; Flinn, Brian D; Raigrodski, Ariel J

2013-12-01

Implant-supported, porcelain veneered restorations experience a greater rate of porcelain fracture than tooth-supported restorations. For completely edentulous patients, one approach to minimizing porcelain fracture is to use acrylic resin in the mandible, although its efficacy is unknown. The purpose of this study was to evaluate the reliability of a veneering porcelain fatigued with different restorative materials in vitro. Fifty-nine veneering porcelain disk specimens were fabricated by layering veneering porcelain on nickel-chromium base metal alloy disks. Four groups of different indenter materials fatigued the porcelain specimens: group WC, tungsten carbide served as a control; group FC, pressed leucite glass ceramic; group NHC, nanohybrid composite resin denture tooth; and group AR, unfilled acrylic resin denture tooth. Porcelain specimens were randomly divided into 4 groups (n=14). A step-stress accelerated life-testing model was used. Use-level probability Weibull plots were generated, and the reliability of each group was estimated for a theoretical completion of 50 000 cycles at 150 N. Nanohybrid composite resin and unfilled acrylic resin denture tooth groups had higher reliability than tungsten carbide and leucite glass ceramic groups. No significant differences existed between the reliability of the tungsten carbide and leucite glass ceramic groups and the nanohybrid composite resin and acrylic resin denture tooth groups. Veneering porcelain disk specimens fatigued with the unfilled acrylic resin and nanohybrid composite resin denture tooth indenters exhibited higher reliability than the specimens fatigued with either the tungsten carbide or leucite glass ceramic indenters. All of the veneering porcelain disk specimens failed with the same mode of fracture, although the surface posttest exhibited different fracture characteristics among specimens fatigued with the 4 different materials. Copyright © 2013 Editorial Council for the Journal of Prosthetic Dentistry. Published by Mosby, Inc. All rights reserved.

Effect of electron beam irradiation on thermal and mechanical properties of aluminum based epoxy composites

NASA Astrophysics Data System (ADS)

Visakh, P. M.; Nazarenko, O. B.; Sarath Chandran, C.; Melnikova, T. V.; Nazarenko, S. Yu.; Kim, J.-C.

2017-07-01

The epoxy resins are widely used in nuclear and aerospace industries. The certain properties of epoxy resins as well as the resistance to radiation can be improved by the incorporation of different fillers. This study examines the effect of electron beam irradiation on the thermal and mechanical properties of the epoxy composites filled with aluminum nanoparticles at percentage of 0.35 wt%. The epoxy composites were exposed to the irradiation doses of 30, 100 and 300 kGy using electron beam generated by the linear electron accelerator ELU-4. The effects of the doses on thermal and mechanical properties of the aluminum based epoxy composites were investigated by the methods of thermal gravimetric analysis, tensile test, and dynamic mechanical analysis. The results revealed that the studied epoxy composites showed good radiation resistance. The thermal and mechanical properties of the aluminum based epoxy composites increased with increasing the irradiation dose up to 100 kGy and decreased with further increasing the dose.

Comparison of Flexural Strength of Different CAD/CAM PMMA-Based Polymers.

PubMed

Alp, Gülce; Murat, Sema; Yilmaz, Burak

2018-01-28

To compare the flexural strength of different computer-aided design/computer-aided manufacturing (CAD/CAM) poly(methyl methacrylate)-based (PMMA) polymers and conventional interim resin materials after thermocycling. Rectangular-shaped specimens (n = 15, for each material) (25 × 2 × 2 mm 3 ) were fabricated from 3 CAD/CAM PMMA-based polymers (Telio CAD [T]; M-PM-Disc [M]; Polident-PMMA [P]), 1 bis-acrylate composite resin (Protemp 4 [PT]), and 1 conventional PMMA (ArtConcept Artegral Dentine [C]) according to ISO 10477:2004 Standards (Dentistry-Polymer-Based Crown and Bridge Materials). The specimens were subjected to 10,000 thermocycles (5 to 55°C). Three-point flexural strength of the specimens was tested in a universal testing machine at a 1.0 mm/min crosshead speed, and the flexural strength data (σ) were calculated (MPa). The flexural strength values were statistically analyzed using 1-way ANOVA, and Tukey HSD post-hoc test for multiple comparisons (α = 0.05). Flexural strength values ranged between 66.1 ± 13.1 and 131.9 ± 19.8 MPa. There were significant differences among the flexural strengths of tested materials, except for between T and P CAD/CAM PMMA-based polymers (p > 0.05). CAD/CAM PMMA-based polymer M had the highest flexural strength and conventional PMMA had the lowest (p < 0.05). CAD/CAM PMMA-based T and P polymers had significantly higher flexural strength than the bis-acrylate composite resin (p < 0.05), and conventional PMMA (p < 0.0001), and significantly lower flexural strength compared to CAD/CAM PMMA-based M (p < 0.05). The flexural strength of CAD/CAM PMMA-based polymers was greater than the flexural strength of bis-acrylate composite resin, which had a greater flexural strength compared to conventional PMMA resin. © 2018 by the American College of Prosthodontists.

Effect of in-office bleaching agents on the color changes of stained ceromers and direct composite resins.

PubMed

Xing, Wenzhong; Jiang, Tao; Liang, Shanshan; Sa, Yue; Wang, Zhejun; Chen, Xiaodong; Wang, Yining

2014-11-01

To evaluate the effect of two in-office bleaching agents on the color changes of two ceromers (Ceramage and Adoro SR) and one direct composite resin (Gradia Direct Anterior) after staining by tea and coffee. Twenty-four disk-shaped specimens were fabricated for each resin material and randomly divided into three groups (n = 8). The specimens were immersed in tea, coffee or deionized water, respectively, for 7 days. Each group was then equally divided into two sub-groups (n = 4), which were subjected to two in-office bleaching agents (BEYOND and Opalescence Boost), respectively. The color of the specimens was measured by a spectrophotometer at baseline, after staining and after bleaching. The color differences (ΔE values) between baseline and after treatments were calculated. Statistical analysis indicated that the staining solution had significant influence on the color change of resin composites tested (p < 0.001). The discolorations of resin composites were perceptible after immersing in tea or coffee solutions (ΔE>2.0). There was no statistically significant difference between BEYOND and Opalescence Boost in stains removal from discolored resins (p = 0.550). The color changes in ΔE value between baseline and after bleaching were less than 2.0 for all resin composite groups. Tea solution produces severe discoloration of three resin composites tested. The two in-office bleaching agents can effectively remove the stains from two ceromers and one direct composite resin tested in this study.

Vegetable Fibers for Composite Materials In Constructive Sector

NASA Astrophysics Data System (ADS)

Giglio, Francesca; Savoja, Giulia

2017-08-01

The aim of the research is to study and to test bio-mixture for laminas to use in construction field components. Composite materials are becoming more common in different sectors, but their embodied energy is an environmental problem. For this, in recent years, the researchers investigate new mixtures for composites, in particular with vegetable fibers and bio-based epoxy resin. The research carried out different laboratory tests for material and mechanical characterization, starting from the analysis of vegetable fibers, and arriving to test different kind of laminas with sundry fabrics and bio-based epoxy resin. In the most general organization of the theme, the research has the overall objective to contribute to reduce composites environmental impacts, with the promotion of local production chains about innovative materials from renewable and sustainable sources.

Composite resin reinforcement of flared canals using light-transmitting plastic posts.

PubMed

Lui, J L

1994-05-01

Composite resins have been advocated as a reinforcing build-up material for badly damaged endodontically treated teeth with flared canals. However, the control of an autocuring composite resin is difficult because it polymerizes rapidly within the root canal. While the light-curing composite resins are more user friendly, their polymerization can be a problem deep in the root canal. Light-transmitting plastic posts allow the transmission of light into the root canal and enable intraradicular composite resin reconstitution and reinforcement of weakened roots. At the same time, the light-transmitting plastic post forms an optimal post canal in the rehabilitated root and can accurately fit a matching retentive final post. These light-transmitting posts are a useful addition to the dental armamentarium.

Effect of incremental filling technique on adhesion of light-cured resin composite to cavity floor.

PubMed

Chikawa, Hirokazu; Inai, Norimichi; Cho, Eitetsu; Kishikawa, Ryuzo; Otsuki, Masayuki; Foxton, Richard M; Tagami, Junji

2006-09-01

The purpose of this study was to evaluate the effect of various incremental filling techniques on adhesion between composite and cavity floor using light-cured resin composite. Black ABS resin and hybrid resin composite were used as mold materials--instead of dentin--for the preparation of cavities, and standardized to 5x5x5 mm. Each cavity was then treated with a bonding system (Clearfil SE bond). Resin composite (Clearfil Photo Core) was placed on the bonding resin using different incremental filling techniques or in bulk and irradiated for a total of 80 seconds using a halogen light unit. Specimens were subjected to the micro-tensile bond test at a crosshead speed of 1 mm/min. Data were analyzed by two-way ANOVA. The results indicated that an incremental filling technique was more effective in improving adhesion to the cavity floor than a bulk filling technique.

Resin adhesion strengths to zirconia ceramics after primer treatment with silane coupling monomer or oligomer.

PubMed

Okada, Masahiro; Inoue, Kazusa; Irie, Masao; Taketa, Hiroaki; Torii, Yasuhiro; Matsumoto, Takuya

2017-09-26

Resin bonding to zirconia ceramics is difficult to achieve using the standard methods for conventional silica-based dental ceramics, which employ silane coupling monomers as primers. The hypothesis in this study was that a silane coupling oligomer -a condensed product of silane coupling monomers- would be a more suitable primer for zirconia. To prove this hypothesis, the shear bond strengths between a composite resin and zirconia were compared after applying either a silane coupling monomer or oligomer. The shear bond strength increased after applying a non-activated ethanol solution of the silane coupling oligomer compared with that achieved when applying the monomer. Thermal treatment of the zirconia at 110°C after application of the silane coupling agents was essential to improve the shear bond strength between the composite resin cement and zirconia.

Selective Clay Placement within a Silicate Clay-Epoxy Blend Nanocomposite and the Effect on Physical Properties

NASA Technical Reports Server (NTRS)

Miller, Sandi G.; Scheiman, Daniel A; Kohlmman, Lee W.

2009-01-01

Many epoxy systems under consideration for composite pressure vessels are composed of toughened epoxy resins. In this work, epoxy blends containing both rigid aromatic and flexible aliphatic components were prepared, to model toughened systems, and determine the optimum route of silicate addition. Compositions were chosen such that both glassy and rubbery resins were obtained at room temperature. The physical properties of the nanocomposites varied with T(g) and silicate placement, however, nanocomposite T(g)s were observed which exceeded that of the base resin by greater than 10 C. The tensile strength of the glassy resin remained constant or decreased on the dispersion of clay while that of the rubbery material doubled. Selectively placing the clay in the aliphatic component of the rubbery blend resulted in a greater than 100% increase in material toughness.

Injection repair of carbon fiber/bismaleimide composite panels with bisphenol E cyanate ester resin

DOE Office of Scientific and Technical Information (OSTI.GOV)

Thunga, Mahendra; Bauer, Amy; Obusek, Kristine

2014-08-01

Resin injection of bisphenol E cyanate ester, a low viscosity resin that cures into a high temperature thermoset polymer, is investigated as a reliable repair method to restore strength and stiffness in delaminated carbon fiber/bismaleimide composites used in aircraft panels. The influence of temperature on the viscosity of the uncured resin was measured to optimize the injection conditions for high resin infiltration into the delaminations. The repair efficiency of the resin was evaluated by varying the panel thickness and the method by which the delamination damage was created in the composite specimens. Ultrasonic scanning (C-scan), flash thermography images, and cross-sectionmore » analysis of repaired panels revealed excellent resin infiltration into the damaged region. Evaluation of mechanical repair efficiency using both bending stiffness and in-plain compressive strength of the composite panels as the repair metrics showed values exceeding 100%.« less

Tough composite materials: Recent developments

NASA Technical Reports Server (NTRS)

Vosteen, L. F. (Editor); Johnston, N. J. (Editor); Teichman, L. A. (Editor); Blankenship, C. P. (Editor)

1985-01-01

The present volume broadly considers topics in composite fracture toughness and impact behavior characterization, composite system constituent properties and their interrelationships, and matrix systems' synthesis and characterization. Attention is given to the characterization of interlaminar crack growth in composites by means of the double cantilever beam specimen, the characterization of delamination resistance in toughened resin composites, the effect of impact damage and open holes on the compressive strength of tough resin/high strain fiber laminates, the effect of matrix and fiber properties on compression failure mechanisms and impact resistance, the relation of toughened neat resin properties to advanced composite mechanical properties, and constituent and composite properties' relationships in thermosetting matrices. Also treated are the effect of cross-link density on the toughening mechanism of elastomer-modified epoxies, the chemistry of fiber/resin interfaces, novel carbon fibers and their properties, the development of a heterogeneous laminating resin, solvent-resistant thermoplastics, NASA Lewis research in advanced composites, and opportunities for the application of composites in commercial aircraft transport structures.

Second generation PMR polyimide/fiber composites

NASA Technical Reports Server (NTRS)

Cavano, P. J.

1979-01-01

A second generation polymerization monomeric reactants (PMR) polyimdes matrix system (PMR 2) was characterized in both neat resin and composite form with two different graphite fiber reinforcements. Three different formulated molecular weight levels of laboratory prepared PMR 2 were examined, in addition to a purchased experimental fully formulated PMR 2 precurser solution. Isothermal aging of graphite fibers, neat resin samples and composite specimens in air at 316 C were investigated. Humidity exposures at 65 C and 97 percent relative humidity were conducted for both neat resin and composites for eight day periods. Anaerobic char of neat resin and fire testing of composites were conducted with PMR 15, PMR 2, and an epoxy system. Composites were fire tested on a burner rig developed for this program. Results indicate that neat PMR 2 resins exhibit excellent isothermal resistance and that PMR 2 composite properties appear to be influenced by the thermo-oxidative stability of the reinforcing fiber.

Dynamic response of phenolic resin and its carbon-nanotube composites to shock wave loading

DOE PAGES

Arman, B.; An, Q.; Luo, S. N.; ...

2011-01-04

We investigate with nonreactive molecular dynamics simulations the dynamic response of phenolic resin and its carbon-nanotube (CNT) composites to shock wave compression. For phenolic resin, our simulations yield shock states in agreement with experiments on similar polymers except the “phase change” observed in experiments, indicating that such phase change is chemical in nature. The elastic–plastic transition is characterized by shear stress relaxation and atomic-level slip, and phenolic resin shows strong strain hardening. Shock loading of the CNT-resin composites is applied parallel or perpendicular to the CNT axis, and the composites demonstrate anisotropy in wave propagation, yield and CNT deformation. Themore » CNTs induce stress concentrations in the composites and may increase the yield strength. Our simulations indicate that the bulk shock response of the composites depends on the volume fraction, length ratio, impact cross-section, and geometry of the CNT components; the short CNTs in current simulations have insignificant effect on the bulk response of resin polymer.« less

Depth of cure, flexural properties and volumetric shrinkage of low and high viscosity bulk-fill giomers and resin composites.

PubMed

Tsujimoto, Akimasa; Barkmeier, Wayne W; Takamizawa, Toshiki; Latta, Mark A; Miyazaki, Masashi

2017-03-31

The purpose of this study was to investigate the depth of cure, flexural properties and volumetric shrinkage of low and high viscosity bulk-fill giomers and resin composites. Depth of cure and flexural properties were determined according to ISO 4049, and volumetric shrinkage was measured using a dilatometer. The depths of cure of giomers were significantly lower than those of resin composites, regardless of photo polymerization times. No difference in flexural strength and modulus was found among either high or low viscosity bulk fill materials. Volumetric shrinkage of low and high viscosity bulk-fill resin composites was significantly less than low and high viscosity giomers. Depth of cure of both low and high viscosity bulk-fill materials is time dependent. Flexural strength and modulus of high viscosity or low viscosity bulk-fill giomer or resin composite materials are not different for their respective category. Resin composites exhibited less polymerization shrinkage than giomers.

Reduced toxicity polyester resins and microvascular pre-preg tapes for advanced composites manufacturing

NASA Astrophysics Data System (ADS)

Poillucci, Richard

Advanced composites manufacturing broadly encapsulates topics ranging from matrix chemistries to automated machines that lay-up fiber-reinforced materials. Environmental regulations are stimulating research to reduce matrix resin formulation toxicity. At present, composites fabricated with polyester resins expose workers to the risk of contact with and inhalation of styrene monomer, which is a potential carcinogen, neurotoxin, and respiratory irritant. The first primary goal of this thesis is to reduce the toxicity associated with polyester resins by: (1) identification of potential monomers to replace styrene, (2) determination of monomer solubility within the polyester, and (3) investigation of approaches to rapidly screen a large resin composition parameter space. Monomers are identified based on their ability to react with polyester and their toxicity as determined by the Globally Harmonized System (GHS) and a green screen method. Solubilities were determined by the Hoftyzer -- Van Krevelen method, Hansen solubility parameter database, and experimental mixing of monomers. A combinatorial microfluidic mixing device is designed and tested to obtain distinct resin compositions from two input chemistries. The push for safer materials is complemented by a thrust for multifunctional composites. The second primary goal of this thesis is to design and implement the manufacture of sacrificial fiber materials suitable for use in automated fiber placement of microvascaular multifunctional composites. Two key advancements are required to achieve this goal: (1) development of a roll-to-roll method to place sacrificial fibers onto carbon fiber pre-preg tape; and (2) demonstration of feasible manufacture of microvascular carbon fiber plates with automated fiber placement. An automated method for placing sacrificial fibers onto carbon fiber tapes is designed and a prototype implemented. Carbon fiber tows with manual placement of sacrificial fibers is implemented within an automated fiber placement machine and the successful fabrication of a carbon fiber plate with an integrated microvascular channel is demonstrated.

Fatigue of the Resin-Enamel Bonded Interface and the Mechanisms of Failure

PubMed Central

Yahyazadehfar, Mobin; Mutluay, Mustafa Murat; Majd, Hessam; Ryou, Heonjune; Arola, Dwayne

2013-01-01

The durability of adhesive bonds to enamel and dentin and the mechanisms of degradation caused by cyclic loading are important to the survival of composite restorations. In this study a novel method of evaluation was used to determine the strength of resin-enamel bonded interfaces under both static and cyclic loading, and to identify the mechanisms of failure. Specimens with twin interfaces of enamel bonded to commercial resin composite were loaded in monotonic and cyclic 4-point flexure to failure within a hydrated environment. Results for the resin-enamel interface were compared with those for the resin composite (control) and values reported for resin-dentin adhesive bonds. Under both modes of loading the strength of the resin-enamel interface was significantly (p≤0.0001) lower than that of the resin composite and the resin-dentin bonded interface. Fatigue failure of the interface occurred predominately by fracture of enamel, adjacent to the interface, and not due to adhesive failures. In the absence of water aging or acid production of biofilms, the durability of adhesive bonds to enamel is lower than that achieved in dentin bonding. PMID:23571321

Microtensile bond strength of indirect resin composite to resin-coated dentin: interaction between diamond bur roughness and coating material.

PubMed

Kameyama, Atsushi; Oishi, Takumi; Sugawara, Toyotarou; Hirai, Yoshito

2009-02-01

This aim of this study was to determine the effect of type of bur and resin-coating material on microtensile bond strength (microTBS) of indirect composite to dentin. Dentin surfaces were first ground with two types of diamond bur and resin-coated using UniFil Bond (UB) or Adper Single Bond (SB), and then bonded to a resin composite disc for indirect restoration with adhesive resin cement. After storage for 24 hr in distilled water at 37 degrees C, microTBS was measured (crosshead speed 1 mm/min). When UB was applied to dentin prepared using the regular-grit diamond bur, microTBS was significantly lower than that in dentin prepared using the superfine-grit bur. In contrast, no significant difference was found between regular-grit and superfine-grit bur with SB. However, more than half of the superfine-grit specimens failed before microTBS testing. These results indicate that selection of bur type is important in improving the bond strength of adhesive resin cement between indirect resin composite and resin-coated dentin.

Effects of air-polishing powders on color stability of composite resins.

PubMed

Güler, Ahmet Umut; Duran, Ibrahim; Yücel, Ali Çağin; Ozkan, Pelin

2011-10-01

The purpose of this study was to investigate the effect of different air-polishing powders on the color stability of different types of composite resin restorative materials. Thirty cylindrical specimens (15×2 mm) were prepared for each of 7 composite resin restorative materials. All specimens were polished with a series of aluminum oxide polishing discs (Sof-Lex). The prepared specimens of each composite resin were randomly divided into 3 groups of 10 specimens each, for control (Group-C) and two air-powder applications (Group-CP: Cavitron Prophy-Jet; Group-PS: Sirona ProSmile prophylaxis powder). A standard air-polishing unit (ProSmile Handly) was used. All specimens were air-powdered for 10 s at 4-bar pressure. The distance of the spray nosel from the specimens was approximately 10 mm and angulation of the nosel was 90°. Specimens were stored in 100 mL of coffee (Nescafe Classic) for 24 h at 37°C. Color measurement of all specimens was recorded before and after exposure to staining agent with a colorimeter (Minolta CR-300). Color differences (∆E*) between the 2 color measurements (baseline and after 24 h storage) were calculated. The data were analyzed with a 2-way ANOVA test, and mean values were compared by the Tukey HSD test (p<0.05). According to the 2-way ANOVA results, composite resin restorative materials, air-polishing powders, and their interaction were statistically significant (p<0.05) For Aelite Aesthetic Enemal, Filtek Z250, Grandio, CeramX Mono, and Quixfil composite resin restorative materials, no significant difference was observed between Group-PS and Group-CP (p>.05) and these groups demonstrated the highest ∆E* values. For Filtek Silorane and IntenS, the highest ∆E* values were observed in Group-PS. The lowest ∆E* values for all composite resin groups were observed in Group-C. When comparing the 7 composite resin restorative materials, Aelite Aesthetic Enemal demonstrated significantly less ∆E* values than the other composite resins tested. The highest ∆E* values were observed in Quixfil. Except for Quixfil, all control groups of composite resins that were polished Sof-Lex exhibited clinically acceptable ∆E values (<3.7). Air-polishing applications increased the color change for all composite resin restorative materials tested. Composite restorations may require re-polishing after air-polishing.

Effects of air-polishing powders on color stability of composite resins

PubMed Central

GÜLER, Ahmet Umut; DURAN, Ibrahim; YÜCEL, Ali Çagin; ÖZKAN, Pelin

2011-01-01

Objectives The purpose of this study was to investigate the effect of different air-polishing powders on the color stability of different types of composite resin restorative materials. Material and methods Thirty cylindrical specimens (15×2 mm) were prepared for each of 7 composite resin restorative materials. All specimens were polished with a series of aluminum oxide polishing discs (Sof-Lex). The prepared specimens of each composite resin were randomly divided into 3 groups of 10 specimens each, for control (Group-C) and two air-powder applications (Group-CP: Cavitron Prophy-Jet; Group-PS: Sirona ProSmile prophylaxis powder). A standard air-polishing unit (ProSmile Handly) was used. All specimens were air-powdered for 10 s at 4-bar pressure. The distance of the spray nosel from the specimens was approximately 10 mm and angulation of the nosel was 90º. Specimens were stored in 100 mL of coffee (Nescafe Classic) for 24 h at 37ºC. Color measurement of all specimens was recorded before and after exposure to staining agent with a colorimeter (Minolta CR-300). Color differences (∆E*) between the 2 color measurements (baseline and after 24 h storage) were calculated. The data were analyzed with a 2-way ANOVA test, and mean values were compared by the Tukey HSD test (p≤0.05). Results According to the 2-way ANOVA results, composite resin restorative materials, air-polishing powders, and their interaction were statistically significant (p<0.05) For Aelite Aesthetic Enemal, Filtek Z250, Grandio, CeramX Mono, and Quixfil composite resin restorative materials, no significant difference was observed between Group-PS and Group-CP (p>.05) and these groups demonstrated the highest ∆E* values. For Filtek Silorane and IntenS, the highest ∆E* values were observed in Group-PS. The lowest ∆E* values for all composite resin groups were observed in Group-C. When comparing the 7 composite resin restorative materials, Aelite Aesthetic Enemal demonstrated significantly less ∆E* values than the other composite resins tested. The highest ∆E* values were observed in Quixfil. Conclusion Except for Quixfil, all control groups of composite resins that were polished Sof-Lex exhibited clinically acceptable ∆E values (<3.7). Air-polishing applications increased the color change for all composite resin restorative materials tested. Composite restorations may require re-polishing after air-polishing. PMID:21922122

The correlation of low-velocity impact resistance of graphite-fiber-reinforced composites with matrix properties

NASA Technical Reports Server (NTRS)

Bowles, K. J.

1986-01-01

Summarized are basic studies that were conducted to correlate the impact resistance of graphite-fiber-reinforced composites with polymer matrix properties. Three crosslinked epoxy resins and a linear polysulfone were selected as composite matrices. As a group, these resins possess a significantly large range of mechanical properties. The mechanical properties of the resins and their respective composites were measured. Neat resin specimens and unidirectional and crossply composite specimens were impact tested with an instrumented dropweight tester. Impact resistances of the specimens were assessed on the basis of loading capability, energy absorption, and extent of damage.

Changes in properties of polyacid-modified composite resins (compomers) following storage in acidic solutions.

PubMed

Nicholson, J W; Gjorgievska, E; Bajraktarova, B; McKenzie, M A

2003-06-01

The interaction of three polyacid-modified composite resins (compomers) with various acidic storage solutions, and also water, over periods of time up to 6 months has been studied and compared with those of a glass-ionomer and a composite resin. This interaction has been shown to vary in a complex way with length of storage and nature of the acid, and citric acid was found to be the most aggressive storage medium for glass-ionomer cement, and also for the compomers. The pure composite resin, by contrast, was relatively unaffected by all of the acid solutions examined. In all acids, the compomers showed a distinct buffering effect, i.e. they increased the pH towards neutral, as did the glass-ionomer. The extent of this also varied with duration of storage and nature of the acid. The biaxial flexure strength was determined and found to be essentially unaffected by the complex chemical interactions with acidic storage solutions. Values obtained for the compomers were lower than those of the composite resin, but above those of the glass-ionomer. Fourier-transform infrared (FT-IR) spectroscopy was employed to study the changes in the compomers following storage in the aqueous media, but bands were broad and no detailed assignments could be made. There were changes in the region of the spectra associated with metal carboxylates however, and this indicates that the secondary acid-base reaction had occurred following water uptake.

Curing kinetics and thermomechanical properties of latent epoxy/carbon fiber composites

NASA Astrophysics Data System (ADS)

Dalle Vacche, S.; Michaud, V.; Demierre, M.; Bourban, P.-E.; Månson, J.-A. E.

2016-07-01

In this work, resins based on diglycidyl ether of bisphenol A (DGEBA) epoxy and a latent hardener, dicyandiamide (DICY), as well as carbon fiber (CF) composites based on them, were prepared with three commercial accelerators: a methylene bis (phenyl dimethyl urea), a cycloaliphatic substituted urea, and a modified polyamine. The curing kinetics of the three DGEBA/DICY/accelerator systems were investigated by chemorheology and differential scanning calorimetry (DSC), in isothermal and over temperature change conditions. Differences in the reaction onset temperature, and in the glass transition temperature (Tg) were highlighted. For curing of thick resin samples, a slow curing cycle at the lowest possible temperature was used, followed by high temperature (160 - 180 °C) post-curing. Indeed, fast curing at higher temperatures caused the formation of hot spots and led to local burning of the samples. The obtained thermomechanical properties, assessed by ultimate tensile testing and dynamic mechanical analysis (DMA) in single cantilever configuration, were all in the expected range for epoxy resins, with tensile moduli close to 3 GPa and Tg > 140 °C. The longterm stability of these resins at room temperature was verified by DSC. Composite samples were prepared by hand lay-up by manually impregnating four layers of 5-harness satin CF textile, and curing in vacuum bag. Impregnation quality and void content were assessed by optical microscopy. The flexural properties of the post-cured composites were assessed by three-point bending test at room temperature and showed no relevant differences, all composites having bending moduli of 45 - 50 GPa. Finally, composites cured with a faster high temperature curing cycle (20 min at 140 °C) were prepared with the DGEBA/DICY/ methylene bis (phenyl dimethyl urea) system, obtaining similar properties as with the slower curing cycle, showing that the prepreg system allowed more flexibility in terms of curing cycle than the bulk resin samples.

Comparison of the wear and flexural characteristics of flowable resin composites for posterior lesions.

PubMed

Sumino, Natsu; Tsubota, Keishi; Takamizawa, Toshiki; Shiratsuchi, Koji; Miyazaki, Masashi; Latta, Mark A

2013-01-01

To determine the localized wear and flexural properties of flowable resin composites for posterior lesions compared with universal resin composites produced by the same manufacturers. Ten specimens of each of three flowable resins, G-ænial Universal Flo, G-ænial Flo and Clearfil Majesty Flow, and the corresponding resin composite materials, Kalore and Clearfil Majesty Esthetics, were prepared in custom fixtures and subjected to 400,000 wear machine cycles to simulate localized wear. The total maximum depth and volume loss of the wear facets was calculated for each specimen using a profilometer. A three-point bending test was performed to determine the flexural strength, modulus of elasticity and resilience. Values were statistically compared using one-way analysis of variance (ANOVA) followed by Tukey's Honestly Significant Difference (HSD) test. The wear depth ranged from 58.3-126.9 m and the volumetric loss ranged from 0.019-0.049 mm(3), with significant differences observed between restorative materials. The wear depth of G-ænial Universal Flo was significantly smaller than those of the other resin composites tested. The flexural strengths and elastic modulus ranged from 90.5-135.1 MPa and from 4.7-7.6 GPa, respectively. A significantly greater flexural strength and higher elastic modulus was found for G-ænial Universal Flo than the other composites. The wear and mechanical properties of the flowable resin composites tested suggested improved performance compared with universal resin composites.

Effect of resin on impact damage tolerance of graphite/epoxy laminates

NASA Technical Reports Server (NTRS)

Williams, J. G.; Rhodes, M. D.

1982-01-01

Twenty-four different epoxy resin systems were evaluated by a variety of test techniques to identify materials that exhibited improved impact damage tolerance in graphite/epoxy composite laminates. Forty-eight-ply composite panels of five of the material systems were able to sustain 100 m/s impact by a 1.27-cm-diameter aluminum projectile while statically loaded to strains of 0.005. Of the five materials with the highest tolerance to impact, two had elastomeric additives, two had thermoplastic additives, and one had a vinyl modifier; all the five systems used bisphenol A as the base resin. An evaluation of test results shows that the laminate damage tolerance is largely determined by the resin tensile properties, and that improvements in laminate damage tolerance are not necessarily made at the expense of room-temperature mechanical properties. The results also suggest that a resin volume fraction of 40 percent or greater may be required to permit the plastic flow between fibers necessary for improved damage tolerance.

Synthesis and Characterization of Novel Epoxy Geopolymer Hybrid Composites

PubMed Central

Roviello, Giuseppina; Ricciotti, Laura; Ferone, Claudio; Colangelo, Francesco; Cioffi, Raffaele; Tarallo, Oreste

2013-01-01

The preparation and the characterization of novel geopolymer-based hybrid composites are reported. These materials have been prepared through an innovative synthetic approach, based on a co-reticulation in mild conditions of commercial epoxy based organic resins and a metakaolin-based geopolymer inorganic matrix. This synthetic strategy allows the obtainment of a homogeneous dispersion of the organic particles in the inorganic matrix, up to 25% in weight of the resin. The materials obtained present significantly enhanced compressive strengths and toughness with respect to the neat geopolymer, suggesting their wide utilization for structural applications. A preliminary characterization of the porous materials obtained by removing the organic phase from the hybrid composites by means of heat treatments is also reported. Possible applications of these materials in the field of water purification, filtration, or as lightweight insulating materials are envisaged. PMID:28788310

Curing potential of experimental resin composites with systematically varying amount of bioactive glass: Degree of conversion, light transmittance and depth of cure.

PubMed

Par, Matej; Spanovic, Nika; Bjelovucic, Ruza; Skenderovic, Hrvoje; Gamulin, Ozren; Tarle, Zrinka

2018-06-17

The aim of this work was to investigate the curing potential of an experimental resin composite series with the systematically varying amount of bioactive glass 45S5 by evaluating the degree of conversion, light transmittance and depth of cure. Resin composites based on a Bis-GMA/TEGDMA resin with a total filler load of 70 wt% and a variable amount of bioactive glass (0-40 wt%) were prepared. The photoinitiator system was camphorquinone and ethyl-4-(dimethylamino) benzoate. The degree of conversion and light transmittance were measured by Raman spectroscopy and UV-vis spectroscopy, respectively. The depth of cure was evaluated according to the classical ISO 4049 test. The initial introduction of bioactive glass into the experimental series diminished the light transmittance while the further increase in the bioactive glass amount up to 40 wt% caused minor variations with no clear trend. The curing potential of the experimental composites was similar to or better than that of commercial resin composites. However, unsilanized bioactive glass fillers demonstrated the tendency to diminish both the maximum attainable conversion and the curing efficiency at depth. Experimental composite materials containing bioactive glass showed a clinically acceptable degree of conversion and depth of cure. The degree of conversion and depth of cure were diminished by bioactive glass fillers in a dose-dependent manner, although light transmittance was similar among all of the experimental composites containing 5-40 wt% of bioactive glass. Reduced curing potential caused by the bioactive glass has possible consequences on mechanical properties and biocompatibility. Copyright © 2018 Elsevier Ltd. All rights reserved.

Tough poly(arylene ether) thermoplastics as modifiers for bismaleimides

NASA Technical Reports Server (NTRS)

Stenzenberger, H. D.; Roemer, W.; Hergenrother, P. M.; Jensen, B. J.

1989-01-01

Several aspects of research on thermoplastics as toughness modifiers are discussed, including the contribution of the backbone chemistry and the concentration of the poly(arylene ether) thermoplastic to fracture toughness, influence of the molecular weight of the poly(arylene ether) thermoplastic on neat resin fracture toughness, and the morphology of the thermoplastic modified networks. The results show that fracture toughness of brittle bismaleimide resins can be improved significantly with poly(arylene ether) thermoplastic levels of 20 percent by weight, and that high molecular weight poly(arylene ether) based on bisphenol A provides the highest degree of toughening. Preliminary composite evaluation shows that improvements in neat resin toughness translate into carbon fabric composite.

Effect of preheating of low shrinking resin composite on intrapulpal temperature and microtensile bond strength to dentin

PubMed Central

El-Deeb, Heba A.; Abd El-Aziz, Sara; Mobarak, Enas H.

2014-01-01

The effect of preheating of the silorane-based resin composite on intrapulpal temperature (IPT) and dentin microtensile bond strength (μTBS) was evaluated. For the IPT, teeth (n = 15) were sectioned to obtain discs of 0.5 mm thickness (2 discs/tooth). The discs were divided into three groups (n = 10/group) according to the temperature of the Filtek LS™ silorane-based resin composite during its placement, either at room temperature (23 ± 1 °C) or preheated to 54 °C or 68 °C using a commercial Calset™ device. Discs were subjected to a simulated intrapulpal pressure (IPP) and placed inside a specially constructed incubator adjusted at 37 °C. IPT was measured before, during and after placement and curing of the resin composite using K-type thermocouple. For μTBS testing, flat occlusal middentin surfaces (n = 24) were obtained. P90 System Adhesive was applied according to manufacturer’s instructions then Filtek LS was placed at the tested temperatures (n = 6). Restorative procedures were done while the specimens were connected to IPP simulation. IPP was maintained and the specimens were immersed in artificial saliva at 37 °C for 24 h before testing. Each specimen was sectioned into sticks (0.9 ± 0.01 mm2). The sticks (24/group) were subjected to μTBS test and their modes of failure were determined using scanning electron microscope (SEM). For both preheated groups, IPT increased equally by 1.5–2 °C upon application of the composite. After light curing, IPT increased by 4–5 °C in all tested groups. Nevertheless, the IPT of the preheated groups required a longer time to return to the baseline temperature. One-way ANOVA revealed no significant difference between the μTBS values of all groups. SEM revealed predominately mixed mode of failure. Preheating of silorane-based resin composite increased the IPT but not to the critical level and had no effect on dentin μTBS. PMID:26257945

Resin transfer molding of textile preforms for aircraft structural applications

NASA Technical Reports Server (NTRS)

Hasko, Gregory H.; Dexter, H. Benson; Weideman, Mark H.

1992-01-01

The NASA LaRC is conducting and supporting research to develop cost-effective fabrication methods that are applicable to primary composite aircraft structures. One of the most promising fabrication methods that has evolved is resin transfer molding (RTM) of dry textile material forms. RTM has been used for many years for secondary structures, but has received increased emphasis because it is an excellent method for applying resin to damage-tolerant textile preforms at low cost. Textile preforms based on processes such as weaving, braiding, knitting, stitching, and combinations of these have been shown to offer significant improvements in damage tolerance compared to laminated tape composites. The use of low-cost resins combined with textile preforms could provide a major breakthrough in achieving cost-effective composite aircraft structures. RTM uses resin in its lowest cost form, and storage and spoilage costs are minimal. Near net shape textile preforms are expected to be cost-effective because automated machines can be used to produce the preforms, post-cure operations such as machining and fastening are minimized, and material scrap rate may be reduced in comparison with traditional prepreg molding. The purpose of this paper is to discuss experimental and analytical techniques that are under development at NASA Langley to aid the engineer in developing RTM processes for airframe structural elements. Included are experimental techniques to characterize preform and resin behavior and analytical methods that were developed to predict resin flow and cure kinetics.

Liquid-Crystal Thermosets, a New Generation of High-Performance Liquid-Crystal Polymers

NASA Technical Reports Server (NTRS)

Dingemans, Theo; Weiser, Erik; Hou, Tan; Jensen, Brian; St. Clair, Terry

2004-01-01

One of the major challenges for NASA's next-generation reusable-launch-vehicle (RLV) program is the design of a cryogenic lightweight composite fuel tank. Potential matrix resin systems need to exhibit a low coefficient of thermal expansion (CTE), good mechanical strength, and excellent barrier properties at cryogenic temperatures under load. In addition, the resin system needs to be processable by a variety of non-autoclavable techniques, such as vacuum-bag curing, resin-transfer molding (RTM), vacuum-assisted resin-transfer molding (VaRTM), resin-film infusion (RFI), pultrusion, and advanced tow placement (ATP). To meet these requirements, the Advanced Materials and Processing Branch (AMPB) at NASA Langley Research Center developed a new family of wholly aromatic liquid-crystal oligomers that can be processed and thermally cross-linked while maintaining their liquid-crystal order. All the monomers were polymerized in the presence of a cross-linkable unit by use of an environmentally benign melt-condensation technique. This method does not require hazardous solvents, and the only side product is acetic acid. The final product can be obtained as a powder or granulate and has an infinite shelf life. The obtained oligomers melt into a nematic phase and do not exhibit isotropization temperatures greater than the temperatures of decomposition (Ti > T(sub dec)). Three aromatic formulations were designed and tested and included esters, ester-amides, and ester-imides. One of the major advantages of this invention, named LaRC-LCR or Langley Research Center-Liquid Crystal Resin, is the ability to control a variety of resin characteristics, such as melting temperature, viscosity, and the cross-link density of the final part. Depending on the formulation, oligomers can be prepared with melt viscosities in the range of 10-10,000 poise (100 rad/s), which can easily be melt-processed using a variety of composite-processing techniques. This capability provides NASA with custom-made matrix resins that meet the required processing conditions for the fabrication of textile composites. Once the resin is in place, the temperature is raised to 375 C and the oligomers are cross-linked into a high-glass-transition-temperature (Tg) nematic network without releasing volatiles. The mechanical properties of the fully crosslinked, composite articles are comparable to typical composites based on commercially available epoxy resins.

Three-Dimensional High Fidelity Progressive Failure Damage Modeling of NCF Composites

NASA Technical Reports Server (NTRS)

Aitharaju, Venkat; Aashat, Satvir; Kia, Hamid G.; Satyanarayana, Arunkumar; Bogert, Philip B.

2017-01-01

Performance prediction of off-axis laminates is of significant interest in designing composite structures for energy absorption. Phenomenological models available in most of the commercial programs, where the fiber and resin properties are smeared, are very efficient for large scale structural analysis, but lack the ability to model the complex nonlinear behavior of the resin and fail to capture the complex load transfer mechanisms between the fiber and the resin matrix. On the other hand, high fidelity mesoscale models, where the fiber tows and matrix regions are explicitly modeled, have the ability to account for the complex behavior in each of the constituents of the composite. However, creating a finite element model of a larger scale composite component could be very time consuming and computationally very expensive. In the present study, a three-dimensional mesoscale model of non-crimp composite laminates was developed for various laminate schemes. The resin material was modeled as an elastic-plastic material with nonlinear hardening. The fiber tows were modeled with an orthotropic material model with brittle failure. In parallel, new stress based failure criteria combined with several damage evolution laws for matrix stresses were proposed for a phenomenological model. The results from both the mesoscale and phenomenological models were compared with the experiments for a variety of off-axis laminates.

Fabrication and testing of SMA composite beam with shape control

NASA Astrophysics Data System (ADS)

Noolvi, Basavaraj; S, Raja; Nagaraj, Shanmukha; Mudradi, Varada Raj

2017-07-01

Smart materials are the advanced materials that have characteristics of sensing and actuation in response to the external stimuli like pressure, heat or electric charge etc. These materials can be integrated in to any structure to make it smart. From the different types of smart materials available, Shape Memory Alloy (SMA) is found to be more useful in designing new applications, which can offer more actuating speed, reduce the overall weight of the structure. The unique property of SMA is the ability to remember and recover from large strains of upto 8% without permanent deformation. Embedding the SMA wire/sheet in fiber-epoxy/flexible resin systems has many potential applications in Aerospace, Automobile, Medical, Robotics and various other fields. In this work the design, fabrication, and testing of smart SMA composite beam has been carried out. Two types of epoxy based resin systems namely LY 5210 resin system and EPOLAM 2063 resin system are used in fabricating the SMA composite specimens. An appropriate mould is designed and fabricated to retain the pre-strain of SMA wire during high temperature post curing of composite specimens. The specimens are fabricated using vacuum bag technique.

Relative biocompatibility of micro-hybrid and nano-hybrid light-activated composite resins.

PubMed

Olabisi Arigbede, Abiodun; Folasade Adeyemi, Bukola; Femi-Akinlosotu, Omowumi

2017-01-01

Background. In vitro studies have revealed a direct association between resin content and cytotoxicity of composite resins; however, implantation studies in this regard are sparse. This study investigates the relationship between filler content of composite resins and biocompatibility. Methods. This research employed twelve 180‒200-gr male Wistar rats, 1 nano-hybrid (Prime-Dent Inc.) and 1 micro-hybrid (Medental Inc.) composite resins containing 74% and 80‒90% filler content, respectively. The samples were assessed on the 2nd, 14th and 90th day of implantation. Four rats were allocated to each day in this experimental study. A section of 1.5mm long cured nano-hybrid and micro-hybrid materials were implanted into the right and left upper and lower limbs of the rats, respectively. Eight samples were generated on each day of observation. Inflammation was graded according to the criteria suggested by Orstavik and Major. Pearson's chi-squared test was employed to determine the relationship between the tissue responses of the two materials. Statistical significance was set at P < 0.05. Results . The average grade of inflammation for the nano-hybrid on the 2nd day of implantation was 3.3. The micro-hybrid resin had a score of 3.0 for cellular inflammation. On the 14th day, the micro-hybrid resin also exhibited a lower average grade for cellular inflammation. On the 90th day, the micro-hybrid resin had a higher grade of inflammation (0.9) compared to 0.3 recorded for nano-hybrid. The composite resins with higher filler content elicited a significantly lower grade of inflammation irrespective of the duration (χ=20.000, df=8, P=0.010) while the composite resins with lower filler content elicited a significantly lower inflammatory response on the 90th day (χ=4.000, df=1, P=0.046). Conclusion. The composite resins with higher filler content generally elicited significantly lower grades of inflammation, and the composite resins with lower filler content exhibited significantly lower inflammatory response on the 90th day of implantation.

Relative biocompatibility of micro-hybrid and nano-hybrid light-activated composite resins

PubMed Central

Olabisi Arigbede, Abiodun; Folasade Adeyemi, Bukola; Femi-Akinlosotu, Omowumi

2017-01-01

Background. In vitro studies have revealed a direct association between resin content and cytotoxicity of composite resins; however, implantation studies in this regard are sparse. This study investigates the relationship between filler content of composite resins and biocompatibility. Methods. This research employed twelve 180‒200-gr male Wistar rats, 1 nano-hybrid (Prime-Dent Inc.) and 1 micro-hybrid (Medental Inc.) composite resins containing 74% and 80‒90% filler content, respectively. The samples were assessed on the 2nd, 14th and 90th day of implantation. Four rats were allocated to each day in this experimental study. A section of 1.5mm long cured nano-hybrid and micro-hybrid materials were implanted into the right and left upper and lower limbs of the rats, respectively. Eight samples were generated on each day of observation. Inflammation was graded according to the criteria suggested by Orstavik and Major. Pearson’s chi-squared test was employed to determine the relationship between the tissue responses of the two materials. Statistical significance was set at P < 0.05. Results. The average grade of inflammation for the nano-hybrid on the 2nd day of implantation was 3.3. The micro-hybrid resin had a score of 3.0 for cellular inflammation. On the 14th day, the micro-hybrid resin also exhibited a lower average grade for cellular inflammation. On the 90th day, the micro-hybrid resin had a higher grade of inflammation (0.9) compared to 0.3 recorded for nano-hybrid. The composite resins with higher filler content elicited a significantly lower grade of inflammation irrespective of the duration (χ=20.000, df=8, P=0.010) while the composite resins with lower filler content elicited a significantly lower inflammatory response on the 90th day (χ=4.000, df=1, P=0.046). Conclusion. The composite resins with higher filler content generally elicited significantly lower grades of inflammation, and the composite resins with lower filler content exhibited significantly lower inflammatory response on the 90th day of implantation. PMID:28413588

Microhardness of light- and dual-polymerizable luting resins polymerized through 7.5-mm-thick endocrowns.

PubMed

Gregor, Ladislav; Bouillaguet, Serge; Onisor, Ioana; Ardu, Stefano; Krejci, Ivo; Rocca, Giovanni Tommaso

2014-10-01

The complete polymerization of luting resins through thick indirect restorations is still questioned. The purpose of this study was to evaluate the degree of polymerization of light- and dual-polymerizable luting resins under thick indirect composite resin and ceramic endocrowns by means of Vickers microhardness measurements. The Vickers microhardness measurements of a light-polymerizable microhybrid composite resin and a dual-polymerizable luting cement directly polymerized in a natural tooth mold for 40 seconds with a high-power light-emitting diode lamp (control) were compared with measurements after indirect irradiation through 7.5-mm-thick composite resin and ceramic endocrowns for 3 × 90 seconds. A test-to-control microhardness values ratio of 0.80 at a depth of 0.5 mm below the surface was assumed as the criterion for adequate conversion. For the Vickers microhardness measurements of a dual-polymerizable luting cement, no differences (P>.05) were found between Vickers microhardness control values and values reported after polymerization through composite resin and ceramic endocrowns. For The Vickers microhardness measurements (±SD) of a light-polymerizable microhybrid composite resin, control values were significantly (P<.05) higher (111 ±3.3) than those reported after polymerization through composite resin (100.5 ±3.8) and ceramic (99.7 ±2.3) endocrowns. However, the hardness values of The Vickers microhardness measurements of a light-polymerizable microhybrid composite resin polymerized through the endocrowns were approximately 10% to 12% lower than those of the control values. Two-way ANOVA showed the influence of the luting material on the Vickers microhardness values (P<.05). The effect of endocrown material was not significant (P>.05). Under the conditions of this in vitro study, Vickers microhardness values of the dual-polymerizable resin cement and the light-polymerizable restorative composite resin irradiated for 3 × 90 seconds with a high irradiance light-emitting diode lamp through 7.5-mm-thick endocrowns reached at least 80% of the control Vickers microhardness values, which means that both materials can be adequately polymerized when they are used for luting thick indirect restorations. Copyright © 2014 Editorial Council for the Journal of Prosthetic Dentistry. Published by Elsevier Inc. All rights reserved.

Advanced resin systems and 3D textile preforms for low cost composite structures

NASA Technical Reports Server (NTRS)

Shukla, J. G.; Bayha, T. D.

1993-01-01

Advanced resin systems and 3D textile preforms are being evaluated at Lockheed Aeronautical Systems Company (LASC) under NASA's Advanced Composites Technology (ACT) Program. This work is aimed towards the development of low-cost, damage-tolerant composite fuselage structures. Resin systems for resin transfer molding and powder epoxy towpreg materials are being evaluated for processability, performance and cost. Three developmental epoxy resin systems for resin transfer molding (RTM) and three resin systems for powder towpregging are being investigated. Various 3D textile preform architectures using advanced weaving and braiding processes are also being evaluated. Trials are being conducted with powdered towpreg, in 2D weaving and 3D braiding processes for their textile processability and their potential for fabrication in 'net shape' fuselage structures. The progress in advanced resin screening and textile preform development is reviewed here.

Reinforcing effects of different fibers on denture base resin based on the fiber type, concentration, and combination.

PubMed

Yu, Sang-Hui; Lee, Yoon; Oh, Seunghan; Cho, Hye-Won; Oda, Yutaka; Bae, Ji-Myung

2012-01-01

The aim of this study was to evaluate the reinforcing effects of three types of fibers at various concentrations and in different combinations on flexural properties of denture base resin. Glass (GL), polyaromatic polyamide (PA) and ultra-high molecular weight polyethylene (PE) fibers were added to heat-polymerized denture base resin with volume concentrations of 2.6%, 5.3%, and 7.9%, respectively. In addition, hybrid fiber-reinforced composite (FRC) combined with either two or three types of fibers were fabricated. The flexural strength, modulus and toughness of each group were measured with a universal testing machine at a crosshead speed of 5 mm/min. In the single fiber-reinforced composite groups, the 5.3% GL and 7.9% GL had the highest flexural strength and modulus; 5.3% PE was had the highest toughness. Hybrid FRC such as GL/PE, which showed the highest toughness and the flexural strength, was considered to be useful in preventing denture fractures clinically.

Carbon fiber content measurement in composite

NASA Astrophysics Data System (ADS)

Wang, Qiushi

Carbon fiber reinforced polymers (CFRPs) have been widely used in various structural applications in industries such as aerospace and automotive because of their high specific stiffness and specific strength. Their mechanical properties are strongly influenced by the carbon fiber content in the composites. Measurement of the carbon fiber content in CFRPs is essential for product quality control and process optimization. In this work, a novel carbonization-in-nitrogen method (CIN) is developed to characterize the fiber content in carbon fiber reinforced thermoset and thermoplastic composites. In this method, a carbon fiber composite sample is carbonized in a nitrogen environment at elevated temperatures, alongside a neat resin sample. The carbon fibers are protected from oxidization while the resin (the neat resin and the resin matrix in the composite sample) is carbonized under the nitrogen environment. The residue of the carbonized neat resin sample is used to calibrate the resin carbonization rate and calculate the amount of the resin matrix in the composite sample. The new method has been validated on several thermoset and thermoplastic resin systems and found to yield an accurate measurement of fiber content in carbon fiber polymer composites. In order to further understand the thermal degradation behavior of the high temperature thermoplastic polymer during the carbonization process, the mechanism and the kinetic model of thermal degradation behavior of carbon fiber reinforced poly (phenylene sulfide) (CPPS) are studied using thermogravimetry analysis (TGA). The CPPS is subjected to TGA in an air and nitrogen atmosphere at heating rates from 5 to 40°C min--1. The TGA curves obtained in air are different from those in nitrogen. This demonstrates that weight loss occurs in a single stage in nitrogen but in two stages in air. To elucidate this difference, thermal decomposition kinetics is analyzed by applying the Kissinger, Flynn-Wall-Ozawa, Coat-Redfern and Malek methods. The activation energy (Ea) of the solid-state process is determined to be 202 kJ mol--1 in an oxidative atmosphere using Kissinger's method, which is 10-15 kJ mol--1 more than the results calculated in a nitrogen atmosphere. The value of the activation energy obtained using Ozawa-Flynn methods is in agreement with that using the Kissinger method. Different degradation mechanisms are used to compare with this value. Based on the analytical result, the actual thermal degradation mechanism of the CPPS is a Dn deceleration type. The carbonization temperature range of the CPPS is the same as pure PPS resin.

Structure-to-property relationships in addition cured polymers. II - Resin Tg and composite initial mechanical properties of norbornenyl cured polyimide resins

NASA Technical Reports Server (NTRS)

Alston, William B.

1986-01-01

PRM (polymerization of monomeric reactants) methodology was used to prepare thirty different polyimide oligomeric resins. Monomeric composition as well as chain length between sites of crosslinks were varied to examine their effects on glass transition temperature (Tg) of the cured/postcured resins. An almost linear correlation of Tg versus molecular distance between the crosslinks was observed. An attempt was made to correlate Tg with initial mechanical properties (flexural strength and interlaminar shear strength) of unidirectional graphite fiber composites prepared with these resins. However, the scatter in mechanical strength data prevented obtaining as clear a correlation as was observed for the structural modification/crosslink distance versus Tg. Instead, only a range of composite mechanical properties was obtained at the test temperatures studied (room temperature, 288 and 316 C). Perhaps more importantly, what did become apparent during the attempted correlation study was: (1) that PMR methodology could be used to prepare composites from resins that contain a wide variety of monomer modifications, and (2) that these composites almost invariably provided satisfactory initial mechanical properties as long as the resins selected were melt processable.

Structure-to-property Relationships in Addition Cured Polymers 2: Resin Tg Composite Initial Mechanical Properties of Norbornenyl Cured Polyimide Resins

NASA Technical Reports Server (NTRS)

Alston, W. B.

1986-01-01

PRM (polymerization of monomeric reactants) methodology was used to prepare thirty different polyimide oligomeric resins. Monomeric composition as well as chain length between sites of crosslinks were varied to examine their effects on glass transition temperature (Tg) of the cured/postcured resins. An almost linear correlation of Tg versus molecular distance between the crosslinks was observed. An attempt was made to correlate Tg with initial mechanical properties (flexural strength and interlaminar shear strength) of unidirectional graphite fiber composites prepared with these resins. However, the scatter in mechanical strength data prevented obtaining as clear a correlation as was observed for the structural modification/crosslink distance versus Tg. Instead, only a range of composite mechanical properties was obtained at the test temperatures studied (room temperature, 288 and 316 C). Perhaps more importantly, what did become apparent during the attempted correlation study was: (1) that PMR methodology could be used to prepare composites from resins that contain a wide variety of monomer modifications, and (2) that these composites almost invariably provided satisfactory initial mechanical properties as long as the resins selected were melt processable.

Modeling of process-induced residual stresses and resin flow behavior in resin transfer molded composites with woven fiber mats

NASA Astrophysics Data System (ADS)

Golestanian, Hossein

This research focuses on modeling Resin Transfer Molding process for manufacture of composite parts with woven fiber mats. Models are developed to determine cure dependent stiffness matrices for composites manufactured with two types of woven fiber mats. Five-harness carbon and eight-harness fiberglass mats with EPON 826 resin composites are considered. The models presented here take into account important material/process parameters with emphasis on; (1) The effects of cure-dependent resin mechanical properties, (2) Fiber undulation due to the weave of the fiber fill and warp bundles, and (3) Resin interaction with the fiber bundles at a microscopic scale. Cure-dependent mechanical properties were then used in numerical models to determine residual stresses and deformation in the composite parts. The complete cure cycle was modeled in these analyses. Also the cool down stage after the composite cure was analyzed. The effect of 5% resin shrinkage on residual stresses and deformations was also investigated. In the second part of the study, Finite Element models were developed to simulate mold filling in RTM processes. Resin flow in the fiber mats was modeled as flow through porous media. Physical models were also developed to investigate resin flow behavior into molds of rectangular and irregular shapes. Silicone fluids of 50 and 100 centistoke viscosities as well as EPON 826 epoxy resin were used in the mold filling experiments. The reinforcements consisted of several layers of woven fiberglass and carbon fiber mats. The effects of injection pressure, fluid viscosity, type of reinforcement, and mold geometry on mold filling times were investigated. Fiber mat permeabilities were determined experimentally for both types of reinforcements. Comparison of experimental and numerical resin front positions indicated the importance of edge effects in resin flow behavior in small cavities. The resin front positions agreed well for the rectangular mold geometry.

A novel method based on selective laser sintering for preparing high-performance carbon fibres/polyamide12/epoxy ternary composites

NASA Astrophysics Data System (ADS)

Zhu, Wei; Yan, Chunze; Shi, Yunsong; Wen, Shifeng; Liu, Jie; Wei, Qingsong; Shi, Yusheng

2016-09-01

A novel method based on selective laser sintering (SLS) process is proposed for the first time to prepare complex and high-performance carbon fibres/polyamide12/epoxy (CF/PA12/EP) ternary composites. The procedures are briefly described as follows: prepare polyamide12 (PA12) coated carbon fibre (CF) composite powder; build porous green parts by SLS; infiltrate the green parts with high-performance thermosetting epoxy (EP) resin; and finally cure the resin at high temperature. The obtained composites are a ternary composite system consisting of the matrix of novolac EP resin, the reinforcement of CFs and the transition thin layer of PA12 with a thickness of 595 nm. The SEM images and micro-CT analysis prove that the ternary system is a three-dimensional co-continuous structure and the reinforcement of CFs are well dispersed in the matrix of EP with the volume fraction of 31%. Mechanical tests show that the composites fabricated by this method yield an ultimate tensile strength of 101.03 MPa and a flexural strength of 153.43 MPa, which are higher than those of most of the previously reported SLS materials. Therefore, the process proposed in this paper shows great potential for manufacturing complex, lightweight and high-performance CF reinforced composite components in aerospace, automotive industries and other areas.

A novel method based on selective laser sintering for preparing high-performance carbon fibres/polyamide12/epoxy ternary composites

PubMed Central

Zhu, Wei; Yan, Chunze; Shi, Yunsong; Wen, Shifeng; Liu, Jie; Wei, Qingsong; Shi, Yusheng

2016-01-01

A novel method based on selective laser sintering (SLS) process is proposed for the first time to prepare complex and high-performance carbon fibres/polyamide12/epoxy (CF/PA12/EP) ternary composites. The procedures are briefly described as follows: prepare polyamide12 (PA12) coated carbon fibre (CF) composite powder; build porous green parts by SLS; infiltrate the green parts with high-performance thermosetting epoxy (EP) resin; and finally cure the resin at high temperature. The obtained composites are a ternary composite system consisting of the matrix of novolac EP resin, the reinforcement of CFs and the transition thin layer of PA12 with a thickness of 595 nm. The SEM images and micro-CT analysis prove that the ternary system is a three-dimensional co-continuous structure and the reinforcement of CFs are well dispersed in the matrix of EP with the volume fraction of 31%. Mechanical tests show that the composites fabricated by this method yield an ultimate tensile strength of 101.03 MPa and a flexural strength of 153.43 MPa, which are higher than those of most of the previously reported SLS materials. Therefore, the process proposed in this paper shows great potential for manufacturing complex, lightweight and high-performance CF reinforced composite components in aerospace, automotive industries and other areas. PMID:27650254

Resin/graphite fiber composites

NASA Technical Reports Server (NTRS)

Cavano, P. J.; Jones, R. J.; Vaughan, R. W.

1972-01-01

High temperature resin matrices suitable for use in advanced graphite fiber composites for jet engine applications were evaluated. A series of planned, sequential screening experiments with resin systems in composite form were performed to reduce the number of candidates to a single A-type polyimide resin that repetitively produced void-free, high strength and modulus composites acceptable for use in the 550 F range for 1000 hours. An optimized processing procedure was established for this system. Extensive mechanical property studies characterized this single system, at room temperature, 500 F, 550 F and 600 F, for various exposure times.

Matrix resin effects in composite delamination - Mode I fracture aspects

NASA Technical Reports Server (NTRS)

Hunston, Donald L.; Moulton, Richard J.; Johnston, Norman J.; Bascom, Willard D.

1987-01-01

A number of thermoset, toughened thermoset, and thermoplastic resin matrix systems were characterized for Mode I critical strain energy release rates, and their composites were tested for interlaminar critical strain energy release rates using the double cantilever beam method. A clear correlation is found between the two sets of data. With brittle resins, the interlaminar critical strain energy release rates are somewhat larger than the neat resin values due to a full transfer of the neat resin toughness to the composite and toughening mechanisms associated with crack growth. With tougher matrices, the higher critical strain energy release rates are only partially transferred to the composites, presumably because the fibers restrict the crack-tip deformation zones.

Equivalent Young's modulus of composite resin for simulation of stress during dental restoration.

PubMed

Park, Jung-Hoon; Choi, Nak-Sam

2017-02-01

For shrinkage stress simulation in dental restoration, the elastic properties of composite resins should be acquired beforehand. This study proposes a formula to measure the equivalent Young's modulus of a composite resin through a calculation scheme of the shrinkage stress in dental restoration. Two types of composite resins remarkably different in the polymerization shrinkage strain were used for experimental verification: the methacrylate-type (Clearfil AP-X) and the silorane-type (Filtek P90). The linear shrinkage strains of the composite resins were gained through the bonded disk method. A formula to calculate the equivalent Young's moduli of composite resin was derived on the basis of the restored ring substrate. Equivalent Young's moduli were measured for the two types of composite resins through the formula. Those values were applied as input to a finite element analysis (FEA) for validation of the calculated shrinkage stress. Both of the measured moduli through the formula were appropriate for stress simulation of dental restoration in that the shrinkage stresses calculated by the FEA were in good agreement within 3.5% with the experimental values. The concept of equivalent Young's modulus so measured could be applied for stress simulation of 2D and 3D dental restoration. Copyright © 2016 The Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Bio-active glass air-abrasion has the potential to remove resin composite restorative material selectively

NASA Astrophysics Data System (ADS)

Milly, Hussam; Andiappan, Manoharan; Thompson, Ian; Banerjee, Avijit

2014-06-01

The aims of this study were to assess: (a) the chemistry, morphology and bioactivity of bio-active glass (BAG) air-abrasive powder, (b) the effect of three air-abrasion operating parameters: air pressure, powder flow rate (PFR) and the abrasive powder itself, on the selective removal of resin composite and (c) the required "time taken". BAG abrasive particles were characterised using scanning electron microscopy-energy dispersive X-ray spectrometry (SEM-EDX) and Fourier-transform infrared spectroscopy (FTIR). Standardised resin composite restorations created within an enamel analogue block (Macor™) in vitro, were removed using air-abrasion undersimulated clinical conditions. 90 standardised cavities were scanned before and after resin composite removal using laser profilometry and the volume of the resulting 3D images calculated. Multilevel linear model was used to identify the significant factors affecting Macor™ removal. BAG powder removed resin composite more selectively than conventional air-abrasion alumina powder using the same operating parameters (p < 0.001) and the effect of altering the unit's operating parameters was significant (p < 0.001). In conclusion, BAG powder is more efficient than alumina in the selective removal of resin composite particularly under specific operating parameters, and therefore may be recommended clinically as a method of preserving sound enamel structure when repairing and removing defective resin composite restorations.

Bonding to new CAD/CAM resin composites: influence of air abrasion and conditioning agents as pretreatment strategy.

PubMed

Reymus, Marcel; Roos, Malgorzata; Eichberger, Marlis; Edelhoff, Daniel; Hickel, Reinhard; Stawarczyk, Bogna

2018-04-27

Because of their industrially standardized process of manufacturing, CAD/CAM resin composites show a high degree of conversion, making a reliable bond difficult to achieve. The purpose of this experiment was to investigate the tensile bond strength (TBS) of luting composite to CAD/CAM resin composite materials as influenced by air abrasion and pretreatment strategies. The treatment factors of the present study were (1) brand of the CAD/CAM resin composite (Brilliant Crios [Coltene/Whaledent], Cerasmart [GC Europe], Shofu Block HC [Shofu], and Lava Ultimate [3M]); (2) air abrasion vs. no air abrasion; and (3) pretreatment using a silane primer (Clearfil Ceramic Primer, Kuraray) vs. a resin primer (One Coat 7 Universal, Coltene/Whaledent). Subsequently, luting composite (DuoCem, Coltene/Whaledent) was polymerized onto the substrate surface using a mold. For each combination of the levels of the three treatment factors (4 (materials) × 2 (air abrasion vs. no air abrasion; resin) × 2 (primer vs. silane primer)), n = 15, specimens were prepared. After 24 h of water storage at 37 °C and 5000 thermo-cycles (5/55 °C), TBS was measured and failure types were examined. The resulting data was analyzed using Kaplan-Meier estimates of the cumulative failure distribution function with Breslow-Gehan tests and non-parametric ANOVA (Kruskal-Wallis test) followed by the multiple pairwise Mann-Whitney U test with α-error adjustment using the Benjamini-Hochberg procedure and chi-square test (p < 0.05). The additional air abrasion step increased TBS values and lowered failure rates. Specimens pretreated using a resin primer showed significantly higher TBS and lower failure rates than those pretreated using a silane primer. The highest failure rates were observed for groups pretreated with a silane primer. Within the Shofu Block HC group, all specimens without air abrasion and pretreatment with a silane primer debonded during the aging procedure. Before fixation of CAD/CAM resin composites, the restorations should be air abraded and pretreated using a resin primer containing methyl-methacrylate to successfully bond to the luting composite. The pretreatment of the CAD/CAM resin composite using merely a silane primer results in deficient adhesion. For a reliable bond of CAD/CAM resin composites to the luting composite, air abrasion and a special pretreatment strategy are necessary in order to achieve promising long-term results.

Effect of Energy Drinks on Discoloration of Silorane and Dimethacrylate-Based Composite Resins.

PubMed

Ahmadizenouz, Ghazaleh; Esmaeili, Behnaz; Ahangari, Zohreh; Khafri, Soraya; Rahmani, Aghil

2016-08-01

This study aimed to assess the effects of two energy drinks on color change (ΔE) of two methacrylate-based and a silorane-based composite resin after one week and one month. Thirty cubic samples were fabricated from Filtek P90, Filtek Z250 and Filtek Z350XT composite resins. All the specimens were stored in distilled water at 37°C for 24 hours. Baseline color values (L*a*b*) of each specimen were measured using a spectrophotometer according to the CIEL*a*b* color system. Ten randomly selected specimens from each composite were then immersed in the two energy drinks (Hype, Red Bull) and artificial saliva (control) for one week and one month. Color was re-assessed after each storage period and ΔE values were calculated. The data were analyzed using the Kruskal Wallis and Mann-Whitney U tests. Filtek Z250 composite showed the highest ΔE irrespective of the solutions at both time points. After seven days and one month, the lowest ΔE values were observed in Filtek Z350XT and Filtek P90 composites immersed in artificial saliva, respectively. The ΔE values of Filtek Z250 and Z350XT composites induced by Red Bull and Hype energy drinks were not significantly different. Discoloration of Filtek P90 was higher in Red Bull energy drink at both time points. Prolonged immersion time in all three solutions increased ΔE values of all composites. However, the ΔE values were within the clinically acceptable range (<3.3) at both time points.

SEM/XPS analysis of fractured adhesively bonded graphite fibre surface resin-rich/graphite fibre composites

NASA Technical Reports Server (NTRS)

Devilbiss, T. A.; Wightman, J. P.; Progar, D. J.

1988-01-01

Samples of graphite fiber-reinforced polyimide were fabricated allowing the resin to accumulate at the composite surface. These surface resin-rich composites were then bonded together and tested for lap shear strength both before and after thermal aging. Lap shear strength did not appear to show a significant improvement over that previously recorded for resin-poor samples and was shown to decrease with increasing aging time and temperature.

Standard tests for toughened resin composites, revised edition

NASA Technical Reports Server (NTRS)

1983-01-01

Several toughened resin systems are evaluated to achieve commonality for certain kinds of tests used to characterize toughened resin composites. Specifications for five tests were standardized; these test standards are described.

Color stability of microfilled, microhybrid and nanocomposite resins--an in vitro study.

PubMed

Nasim, Iffat; Neelakantan, Prasanna; Sujeer, R; Subbarao, C V

2010-01-01

The aim of this study was to evaluate the effect of two beverages-Tea and Pepsi on the color stability of three different composite resins after a period of 7 and 30 days. Color stability of a microfilled, microhybrid and nanocomposite was evaluated after storage in Tea, a carbonated drink or Distilled Water for 7 and 30 days. Color measurement was done using reflectance spectrophotometer based on the CIE L*a*b* color scale. Mean values of the different groups were compared using three-way analysis of variance and multiple comparisons of the mean values were done using Tukey-Kramer test with 0.05 as significance level. All tested resin composites showed color change after a period of 7 and 30 days. The color change exhibited by all three groups was significantly different for all three beverages studied, at both time periods (p<0.05). Amongst the resin composites studied microhybrid composite was found to be more color stable. The microfilled composite discolored most in Distilled Water and Pepsi at the 7th and 30th day. The nanocomposite discolored most in Tea at 7th and 30th day. All efforts should be made to minimize discoloration of composite restorations by adopting excellent polishing techniques. Patients should also be educated on the possibility of the restoration to undergo staining under the influence of beverages. Copyright © 2010 Elsevier Ltd. All rights reserved.

Evaluation of Double-Vacuum-Bag Process For Composite Fabrication

NASA Technical Reports Server (NTRS)

Hou, T. H.; Jensen, B. J.

2004-01-01

A non-autoclave vacuum bag process using atmospheric pressure alone that eliminates the need for external pressure normally supplied by an autoclave or a press is an attractive method for composite fabrication. This type of process does not require large capital expenditures for tooling and processing equipment. In the molding cycle (temperature/pressure profile) for a given composite system, the vacuum application point has to be carefully selected to achieve the final consolidated laminate net shape and resin content without excessive resin squeeze-out. The traditional single-vacuum- bag (SVB) process is best suited for molding epoxy matrix based composites because of their superior flow and the absence of reaction by-products or other volatiles. Other classes of materials, such as polyimides and phenolics, generate water during cure. In addition, these materials are commonly synthesized as oligomers using solvents to facilitate processability. Volatiles (solvents and reaction byproducts) management therefore becomes a critical issue. SVB molding, without additional pressure, normally fails to yield void-free quality composites for these classes of resin systems. A double-vacuum- bag (DVB) process for volatile management was envisioned, designed and built at the NASA Langley Research Center. This experimental DVB process affords superior volatiles management compared to the traditional SVB process. Void-free composites are consistently fabricated as measured by C-scan and optical photomicroscopy for high performance polyimide and phenolic resins.

Studies on the application of temperature-responsive ion exchange polymers with whey proteins.

PubMed

Maharjan, Pankaj; Campi, Eva M; De Silva, Kirthi; Woonton, Brad W; Jackson, W Roy; Hearn, Milton T W

2016-03-18

Several new types of temperature-responsive ion exchange resins of different polymer composition have been prepared by grafting the products from the co-polymerisation of N-phenylacrylamide, N-iso-propylacrylamide and acrylic acid derivatives onto cross-linked agarose. Analysis of the binding isotherms for these different resins obtained under batch adsorption conditions indicated that the resin based on N-iso-propylacrylamide containing 5% (w/w) N-phenylacrylamide and 5% (w/w) acrylic acid resulted in the highest adsorption capacity, Bmax, for the whey protein, bovine lactoferrin, e.g. 14 mg bovine lactoferrin/mL resin at 4 °C and 62 mg bovine lactoferrin/mL resin at 40 °C, respectively. Under dynamic loading conditions at 40 °C, 94% of the loaded bovine lactoferrin on a normalised mg protein per mL resin basis was adsorbed by this new temperature-responsive ion-exchanger, and 76% was eluted by a single cycle temperature shift to 4 °C without varying the composition of the 10mM sodium dihydrogen phosphate buffer, pH 6.5, or the flow rate. The binding characteristics of these different ion exchange resins with bovine lactoferrin were also compared to results obtained using other resins based on N-isopropylacrylamide but contained N-tert-butylacrylamide rather than N-phenylacrylamide, where the corresponding dynamic capture and release properties for bovine lactoferrin required different temperature conditions of 20 °C and 50 °C, respectively for optimal desorption/adsorption. The cationic protein, bovine lactoperoxidase, was also adsorbed and desorbed with these temperature-responsive resins under similar conditions of changing temperature, whereas the anionic protein, bovine β-lactoglobulin, was not adsorbed under this regime of temperature conditions but instead eluted in the flow-through. Copyright © 2016 Elsevier B.V. All rights reserved.

Immediate versus one-month wet storage fatigue of restorative materials.

PubMed

Gladys, S; Braem, M; Van Meerbeek, B; Lambrechts, P; Vanherle, G

1998-03-01

Immediate finishing is a highly desirable property of restorative materials. In general, the resin composites, the polyacid-modified resin composites and resin-modified glass-ionomers are finished immediately after light-curing. For the conventional glass-ionomers a waiting period of 24 h is recommended. Therefore, the objective of this study was to investigate whether immediate finishing and application of cyclic loading under water spray on resin-modified glass-ionomers, a conventional glass-ionomer, a polyacid-modified resin composite and a resin composite are reflected in their Young's modulus and fatigue resistance after 1-month wet storage compared with a control group that could mature untroubled for 1 month. From this study, it could be concluded that there is a material-dependent response on immediate finishing. For the conventional glass-ionomer, the waiting period of 24 h is highly advisable. The resin composite suffered more than the other test materials. A second statement is that one must be cautious by the extrapolation of findings obtained on quasi static tests (Young's modulus) towards dynamic properties (flexural fatigue limit).

Ballistic Performance of Alimina/S-2 Glass-Reinforced Polymer-Matrix Composite Hybrid Lightweight Armor Against Armor Piercing (AP) and Non-AP Projectiles

DTIC Science & Technology

2007-01-01

and a phenolic -resin based polymeric matrix. Such armor panels offer superior protection against fragmented ballistic threats when compared to...database does not contain a material model for the HJ1 composite but provides a model for a Kevlar Fiber Reinforced Polymer (KFRP) containing 53 vol... phenolic resin and epoxy yield stresses and then with a ratio of the S-2 glass and aramid fibers volume fractions. To test the validity of the

Kinetics and mechanics of photo-polymerized triazole-containing thermosetting composites via the copper(I)-catalyzed azide-alkyne cycloaddition

PubMed Central

Song, Han Byul; Wang, Xiance; Patton, James R.; Stansbury, Jeffrey W.; Bowman, Christopher N.

2017-01-01

Objectives Several features necessary for polymer composite materials in practical applications such as dental restorative materials were investigated in photo-curable CuAAC (copper(I)-catalyzed azide-alkyne cycloaddition) thermosetting resin-based composites with varying filler loadings and compared to a conventional BisGMA/TEGDMA based composite. Methods Tri-functional alkyne and di-functional azide monomers were synthesized for CuAAC resins and incorporated with alkyne-functionalized silica microfillers for CuAAC composites. Polymerization kinetics, in situ temperature change, and shrinkage stress were monitored simultaneously with a tensometer coupled with FTIR spectroscopy and a data-logging thermocouple. The glass transition temperature was analyzed by dynamic mechanical analysis. Flexural modulus/strength and flexural toughness were characterized in three-point bending on a universal testing machine. Results The photo-CuAAC polymerization of composites containing between 0 and 60 wt% microfiller achieved ~99% conversion with a dramatic reduction in the maximum heat of reaction (~20 °C decrease) for the 60 wt% filled CuAAC composites as compared with the unfilled CuAAC resin. CuAAC composites with 60 wt% microfiller generated more than twice lower shrinkage stress of 0.43±0.01 MPa, equivalent flexural modulus of 6.1±0.7 GPa, equivalent flexural strength of 107±9 MPa, and more than 10 times higher energy absorption of 10±1 MJ m−3 when strained to 11% relative to BisGMA-based composites at equivalent filler loadings. Significance Mechanically robust and highly tough, photo-polymerized CuAAC composites with reduced shrinkage stress and a modest reaction exotherm were generated and resulted in essentially complete conversion. PMID:28363645

Kinetics and mechanics of photo-polymerized triazole-containing thermosetting composites via the copper(I)-catalyzed azide-alkyne cycloaddition.

PubMed

Song, Han Byul; Wang, Xiance; Patton, James R; Stansbury, Jeffrey W; Bowman, Christopher N

2017-06-01

Several features necessary for polymer composite materials in practical applications such as dental restorative materials were investigated in photo-curable CuAAC (copper(I)-catalyzed azide-alkyne cycloaddition) thermosetting resin-based composites with varying filler loadings and compared to a conventional BisGMA/TEGDMA based composite. Tri-functional alkyne and di-functional azide monomers were synthesized for CuAAC resins and incorporated with alkyne-functionalized glass microfillers for CuAAC composites. Polymerization kinetics, in situ temperature change, and shrinkage stress were monitored simultaneously with a tensometer coupled with FTIR spectroscopy and a data-logging thermocouple. The glass transition temperature was analyzed by dynamic mechanical analysis. Flexural modulus/strength and flexural toughness were characterized in three-point bending on a universal testing machine. The photo-CuAAC polymerization of composites containing between 0 and 60wt% microfiller achieved ∼99% conversion with a dramatic reduction in the maximum heat of reaction (∼20°C decrease) for the 60wt% filled CuAAC composites as compared with the unfilled CuAAC resin. CuAAC composites with 60wt% microfiller generated more than twice lower shrinkage stress of 0.43±0.01MPa, equivalent flexural modulus of 6.1±0.7GPa, equivalent flexural strength of 107±9MPa, and more than 10 times higher energy absorption of 10±1MJm -3 when strained to 11% relative to BisGMA-based composites at equivalent filler loadings. Mechanically robust and highly tough, photo-polymerized CuAAC composites with reduced shrinkage stress and a modest reaction exotherm were generated and resulted in essentially complete conversion. Copyright © 2017 The Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Kenaf-glass fiber reinforced unsaturated polyester hybrid composites: Tensile properties

NASA Astrophysics Data System (ADS)

Zhafer, S. F.; Rozyanty, A. R.; Shahnaz, S. B. S.; Musa, L.; Zuliahani, A.

2016-07-01

The use of natural fibers in composite is rising in recent years due their lightweight, non-abrasive, combustible, non-toxic, low cost and biodegradable properties. However, in comparison with synthetic fibers, the mechanical properties of natural fibers are lower. Therefore, the inclusion of synthetic fibers could improve the mechanical performance of natural fiber based composites. In this study, kenaf bast fiber and glass fiber at different weight percentage loading were used as reinforcement to produce hybrid composites. Unsaturated polyester (UP) resin was used as matrix and hand lay-up process was performed to apply the UP resin on the hybrid kenaf bast/glass fiber composite. Effect of different fiber loading on tensile strength, tensile modulus and elongation at break of the hybrid composite was studied. It has been found that the highest value of tensile strength and modulus was achieved at 10 wt.% kenaf/10 wt.% glass fiber loading. It was concluded that addition of glass fiber has improved the tensile properties of kenaf bast fiber based UP composites.

Masking of Enamel Fluorosis Discolorations and Tooth Misalignment With a Combination of At-Home Whitening, Resin Infiltration, and Direct Composite Restorations.

PubMed

Perdigão, J; Lam, V Q; Burseth, B G; Real, C

This clinical report illustrates a conservative technique to mask enamel discolorations in maxillary anterior teeth caused by hypomineralization associated with enamel fluorosis and subsequent direct resin composite to improve the anterior esthetics. The treatment consisted of at-home whitening with 10% carbamide peroxide gel with potassium nitrate and sodium fluoride in a custom-fitted tray to mask the brown-stained areas, followed by resin infiltration to mask the white spot areas. An existing resin composite restoration in the maxillary right central incisor was subsequently replaced after completion of the whitening and resin infiltration procedures, whereas the two misaligned and rotated maxillary lateral incisors were built up with direct resin composite restorations to provide the illusion of adequate arch alignment, as the patient was unable to use orthodontic therapy.

Interlaminar shear properties of graphite fiber, high-performance resin composites

NASA Technical Reports Server (NTRS)

Needles, H. L.; Kourtides, D. A.; Fish, R. H.; Varma, D. S.

1983-01-01

Short beam testing was used to determine the shear properties of laminates consisting of T-300 and Celion 3000 and 6000 graphite fibers, in epoxy, hot melt and solvent bismaleimide, polyimide and polystyrylpyridine (PSP). Epoxy, composites showed the highest interlaminar shear strength, with values for all other resins being substantially lower. The dependence of interlaminar shear properties on the fiber-resin interfacial bond and on resin wetting characteristics and mechanical properties is investigated, and it is determined that the lower shear strength of the tested composites, by comparison with epoxy resin matrix composites, is due to their correspondingly lower interfacial bond strengths. An investigation of the effect of the wettability of carbon fiber tow on shear strength shows wetting variations among resins that are too small to account for the large shear strength property differences observed.

Theoretical modeling and experimental study of dielectric loss of the multi-push-pull mode magnetoelectric laminate composites

NASA Astrophysics Data System (ADS)

Xu, Bingbing; Ma, Jiashuai; Fang, Cong; Yao, Meng; Di, Wenning; Li, Xiaobing; Luo, Haosu

2018-02-01

In this work, we establish a dielectric loss model for multi-push-pull mode ME laminate composites. It deduces that the total dielectric loss of the ME composites equals the linear average of the dielectric loss of piezoelectric plate and epoxy resin. But further analysis of this model has indicated that we can ignore the dielectric loss of epoxy resin. To verify this model, we use three kinds of epoxy resin with different dielectric loss to fabricate multi-push-pull mode PMNT/Metglas ME laminate composites respectively. It turns out that the different kinds of epoxy resin have little influence on the total dielectric loss, capacitance and piezoelectricity of the composites, which demonstrates that our model conforms to the practical case. Therefore, we can pay more attention to the mechanical properties of epoxy resin rather than its dielectric loss on fabricating the ME laminate composites.

Dimensional stability of pineapple leaf fibre reinforced phenolic composites

NASA Astrophysics Data System (ADS)

Asim, M.; Jawaid, M.; Abdan, K.; Ishak, M. R.

2017-12-01

In this research, pineapple leaves fibre (PALF)/phenolic resin (PF) composites were fabricated by hand lay-up method. The aim of this work is to investigate the physical properties (water absorption and thickness swelling) of PALF reinforced phenolic resin composites. Long-term water absorption (WA) and thickness swelling (TS) behaviours of the PALF/PF composites were investigated at several water immersion times. The effects of different fibre loading on WA and TS of PALF/PF composites were also analyzed. Obtained results indicated that the WA and TS of PALF/PF composites vary with fibres content and water immersion time before reaching to equilibrium. WA and TS of PALF/PF composites were increased by increasing fibre loading. Results obtained in this study will be used for further study on hybridization of PALF and Kenaf fibre based phenolic composites.

Shear bond strength of a denture base acrylic resin and gingiva-colored indirect composite material to zirconia ceramics.

PubMed

Kubochi, Kei; Komine, Futoshi; Fushiki, Ryosuke; Yagawa, Shogo; Mori, Serina; Matsumura, Hideo

2017-04-01

To evaluate the shear bond strengths of two gingiva-colored materials (an indirect composite material and a denture base acrylic resin) to zirconia ceramics and determine the effects of surface treatment with various priming agents. A gingiva-colored indirect composite material (CER) or denture base acrylic resin (PAL) was bonded to zirconia disks with unpriming (UP) or one of seven priming agents (n=11 each), namely, Alloy Primer (ALP), Clearfil Photo Bond (CPB), Clearfil Photo Bond with Clearfil Porcelain Bond Activator (CPB+Act), Metal Link (MEL), Meta Fast Bonding Liner (MFB), MR. bond (MRB), and V-Primer (VPR). Shear bond strength was determined before and after 5000 thermocycles. The data were analyzed with the Kruskal-Wallis test and Steel-Dwass test. The mean pre-/post-thermalcycling bond strengths were 1.0-14.1MPa/0.1-12.1MPa for the CER specimen and 0.9-30.2MPa/0.1-11.1MPa for the PAL specimen. For the CER specimen, the ALP, CPB, and CPB+Act groups had significantly higher bond strengths among the eight groups, at both 0 and 5000 thermocycles. For the PAL specimen, shear bond strength was significantly lower after thermalcycling in all groups tested. After 5000 thermocycles, bond strengths were significantly higher in the CPB and CPB+Act groups than in the other groups. For the PAL specimens, bond strengths were significantly lower after thermalcycling in all groups tested. The MDP functional monomer improved bonding of a gingiva-colored indirect composite material and denture base acrylic resin to zirconia ceramics. Copyright © 2016 Japan Prosthodontic Society. Published by Elsevier Ltd. All rights reserved.

Comparison of Shear Bond Strength of RMGI and Composite Resin for Orthodontic Bracket Bonding

PubMed Central

Yassaei, Soghra; Davari, Abdolrahim; Goldani Moghadam, Mahjobeh; Kamaei, Ahmad

2014-01-01

Objective: The aim of this study was to compare the shear bond strength (SBS) of resin modified glass ionomer (RMGI) and composite resin for bonding metal and ceramic brackets. Materials and Methods: Eighty-eight human premolars extracted for orthodontic purposes were divided into 4 groups (n=22). In groups 1 and 2, 22 metal and ceramic brackets were bonded using composite resin (Transbond XT), respectively. Twenty-two metal and ceramic brackets in groups 3 and 4, respectively were bonded using RMGI (Fuji Ortho LC, Japan). After photo polymerization, the teeth were stored in water and thermocycled (500 cycles between 5° and 55°). The SBS value of each sample was determined using a Universal Testing Machine. The amount of residual adhesive remaining on each tooth was evaluated under a stereomicroscope. Statistical analyses were done using two-way ANOVA. Results: RMGI bonded brackets had significantly lower SBS value compared to composite resin bonded groups. No statistically significant difference was observed between metal and ceramic brackets bonded with either the RMGI or composite resin. The comparison of the adhesive remnant index (ARI) scores between the groups indicated that the bracket failure mode was significantly different among groups (P<0.001) with more adhesive remaining on the teeth bonded with composite resin. Conclusion: RMGIs have significantly lower SBS compared to composite resin for orthodontic bonding purposes; however the provided SBS is still within the clinically acceptable range. PMID:25628663

Color stability of sealed composite resin restorative materials after ultraviolet artificial aging and immersion in staining solutions.

PubMed

Catelan, Anderson; Briso, André Luiz Fraga; Sundfeld, Renato Hermann; Goiato, Marcelo Coelho; dos Santos, Paulo Henrique

2011-04-01

The color alteration of resin-based materials is one of the most common reasons to replace esthetic dental restorations. This study assessed the influence of surface sealant (Biscover) on the color stability of nanofilled (Supreme XT) and microhybrid (Vit-l-escence and Opallis) composite resins after artificial aging. One hundred disc-shaped (6 × 1.5 mm) specimens were made for each composite resin. After 24 hours, all specimens were polished and sealant was applied to 50 specimens of each material. Baseline color was measured according to the CIE L*a*b* system using a reflection spectrophotometer. Ten specimens of each group were aged for 252 h in an ultraviolet (UV)-accelerated aging chamber or immersed for 4 weeks in cola soft drink, orange juice, red wine staining solutions or distilled water as control. Color difference (ΔE) after aging was calculated based on the color coordinates before (baseline) and after aging/staining treatment. Data were analyzed with 2-way ANOVA and Fisher's test (α=.05). The results showed significant changes in color after artificial aging in all the groups (P<.05). Independent of the material studied, red wine resulted in the highest level of discoloration. Intermediate values were found for orange juice, UV accelerated aging, and the cola soft drink. The lowest values of ΔE were found for specimens stored in distilled water. All composite resins showed some color alteration after the aging methods. The surface sealant did not alter the color stability of the tested materials. Copyright © 2011 The Editorial Council of the Journal of Prosthetic Dentistry. Published by Mosby, Inc. All rights reserved.

In vitro enamel remineralization capacity of composite resins containing sodium trimetaphosphate and fluoride.

PubMed

Tiveron, Adelisa Rodolfo Ferreira; Delbem, Alberto Carlos Botazzo; Gaban, Gabriel; Sassaki, Kikue Takebayashi; Pedrini, Denise

2015-11-01

This study evaluated the in vitro enamel remineralization capacity of experimental composite resins containing sodium trimetaphosphate (TMP) combined or not with fluoride (F). Bovine enamel slabs were selected upon analysis of initial surface hardness (SH1) and after induction of artificial carious lesions (SH2). Experimental resins were as follows: resin C (control—no sodium fluoride (NaF) or TMP), resin F (with 1.6% NaF), resin TMP (with 14.1% TMP), and resin TMP/F (with NaF and TMP). Resin samples were made and attached to enamel slabs (n = 12 slabs per material). Those specimens (resin/enamel slab) were subjected to pH cycling to promote remineralization, and then final surface hardness (SH3) was measured to calculate the percentage of surface hardness recovery (%SH). The integrated recovery of subsurface hardness (ΔKHN) and F concentration in enamel were also determined. Data was analyzed by ANOVA and Student-Newman-Keuls test (p < 0.05). Resins F and TMP/F showed similar SH3 values (p = 0.478) and %SH (p = 0.336) and differed significantly from the other resins (p < 0.001). Considering ΔKHN values, resin TMP/F presented the lowest area of lesion (p < 0.001). The presence of F on enamel was different among the fluoridated resins (p = 0.042), but higher than in the other resins (p < 0.001). The addition of TMP to a fluoridated composite resin enhanced its capacity for remineralization of enamel in vitro. The combination of two agents with action on enamel favored remineralization, suggesting that composite resins containing sodium trimetaphosphate and fluoride could be indicated for clinical procedures in situations with higher cariogenic challenges.

Pultruded composites using soy-based polyurethane resin.

DOT National Transportation Integrated Search

2008-07-01

Fiber Reinforced Polymer (FRP) composites offer inherent advantages over traditional materials with regard to high strength-to-weight ratio, design flexibility, corrosion resistance, low maintenance, and extended service life. FRP materials can be us...

Repair of dimethacrylate-based composite restorations by a silorane-based composite: a one-year randomized clinical trial.

PubMed

Popoff, D A V; Santa Rosa, T T A; Ferreira, R C; Magalhães, C S; Moreira, A N; Mjör, I A

2012-01-01

To investigate clinical performance of a low-shrinkage silorane-based composite resin when used for repairing conventional dimethacrylate-based composite restorations. Despite the continued development of resin-based materials, polymerization shrinkage and shrinkage stress still require improvement. A silorane-based monomer system was recently made available for dental restorations. This report refers to the use of this material for making repairs and evaluates the clinical performance of this alternative treatment. One operator repaired the defective dimethacrylate-based composite resin restorations that were randomly assigned to one of two treatment groups: control (n=50) repair with Adper SE Plus (3M/ESPE) and Filtek P60 Posterior Restorative (3M/ESPE), and test (n=50) repair with P90 System Adhesive Self-Etch Primer and Bond (3M/ESPE) and Filtek P90 Low Shrink Posterior Restorative (3M/ESPE). After one week, restorations were finished and polished. Two calibrated examiners (Kw≥0.78) evaluated all repaired restorations, blindly and independently, at baseline and one year. The parameters examined were marginal adaptation, anatomic form, surface roughness, marginal discoloration, postoperative sensitivity, and secondary caries. The restorations were classified as Alpha, Bravo, or Charlie, according to modified US Public Health Service criteria. Mann-Whitney and Wilcoxon tests were used to compare the groups. Of the 100 restorations repaired in this study, 93 were reexamined at baseline. Dropout from baseline to one-year recall was 11%. No statistically significant differences were found between the materials for all clinical criteria, at baseline or at one-year recall (p>0.05). No statistically significant differences were registered (p>0.05) for each material when compared for all clinical criteria at baseline and at one-year recall. The hypothesis tested in this randomized controlled clinical trial was accepted. After the one-year evaluations, the silorane-based composite exhibited a similar performance compared with dimethacrylate-based composite when used to make repairs.

Comparison of Microleakage of Composite Resin Veneering Systems at the Alloy Interface

DTIC Science & Technology

1988-09-01

of oral fluids at the metal- resin interface and breakdown of the acrylic resin were factors that have limited the acceptance and widespread use of...percolation of oral fluids at the resin -metal interface, and low resistance to toothbrush abrasion. If chemical means could be used to achieve resin -metal...bonding, 1) esthetics could be improved because of a more uniform layer of the opaque and composite resin , and 2) percolation of fluids at the metal

Estrogenicity of resin-based composites and sealants used in dentistry.

PubMed Central

Olea, N; Pulgar, R; Pérez, P; Olea-Serrano, F; Rivas, A; Novillo-Fertrell, A; Pedraza, V; Soto, A M; Sonnenschein, C

1996-01-01

We tested some resin-based composites used in dentistry for their estrogenic activity. A sealant based on bisphenol-A diglycidylether methacrylate (bis-GMA) increased cell yields, progesterone receptor expression, and pS2 secretion in human estrogen-target, serum-sensitive MCF7 breast cancer cells. Estrogenicity was due to bisphenol-A and bisphenol-A dimethacrylate, monomers found in the base paste of the dental sealant and identified by mass spectrometry. Samples of saliva from 18 subjects treated with 50 mg of a bis-GMA-based sealant applied on their molars were collected 1 hr before and after treatment. Bisphenol-A (range 90-931 micrograms) was identified only in saliva collected during a 1-hr period after treatment. The use of bis-GMA-based resins in dentistry, and particularly the use of sealants in children, appears to contribute to human exposure to xenoestrogens. Images Figure 1. A Figure 1. B Figure 2. Figure 3. A Figure 3. B Figure 4. A Figure 4. B Figure 5. A Figure 5. B Figure 6. A Figure 6. B Figure 7. A Figure 7. B Figure 8. Figure 9. Figure 10. PMID:8919768

Modified Epoxy Composites

NASA Technical Reports Server (NTRS)

Gilwee, W. J.

1984-01-01

The properties of a rubber-modified experimental epoxy resin and a standard epoxy as composite matrices were studied. In addition, a brominated epoxy resin was used in varying quantities to improve the fire resistance of the composite. The experimental resin was tris-(hydroxyphenyl)methane triglycidyl ether, known as tris epoxy novolac (TEN). The standard epoxy resin used was tetraglycidyl 4,4'-diaminodiphenyl methane (TGDDM). The above resins were modified with carboxyl-terminated butadiene acrylonitrile (CTBN) rubber. It is concluded that: (1) modification of TEN resin with bromine gives better impact resistance than rubber modification alone; (2) 25% rubber addition is necessary to obtain significant improvement in impact resistance; (3) impact resistance increases with bromine content; (4) impact velocity does not significantly affect the energy absorbed by the test sample; (5) Tg did not decline with rubber modification; and (6) TEN resin had better hot/wet properties than TGDDM resin.

Three-body-wear resistance of the experimental composites containing filler treated with hydrophobic silane coupling agents.

PubMed

Nihei, Tomotaro; Dabanoglu, Alp; Teranaka, Toshio; Kurata, Shigeaki; Ohashi, Katsura; Kondo, Yukishige; Yoshino, Norio; Hickel, Reinhard; Kunzelmann, Karl-Heinz

2008-06-01

This paper evaluated the wear resistance of resin composite materials with fillers which were modified with a novel hydrophobic silane coupling agent. The novel silane coupling agent containing hydrophobic phenyl group 3-(3-methoxy-4-methacryloyloxyphenyl)propyltrimethoxysilane (p-MBS) was synthesized. The experimental light-cure hybrid composites containing 85wt% of filler modified with this silane were formulated. Twelve specimens were prepared for the three-body-wear test with the ACTA machine and the collected data were analyzed statistically using a one-way ANOVA and Tukey's multiple comparison test as the post hoc test. The wear of the composites containing fillers treated with p-MBS was significantly lower compared with the composite materials containing fillers pretreated with 3-methacryloyloxypropyltrimethoxysilane or the commercially composites (AP-X and ELS extra low shrinkage) after a wear test for 200,000 cycles (p<0.05). It is suggested that the resin composites containing fillers modified with the novel hydrophobic silane has high wear resistant, because of the coupling layers treated with this silane had an excellent affinity with the base resin and formed a highly hydrophobic layer on the filler surface.

Screening programme to select a resin for Gravity Probe-B composites

NASA Technical Reports Server (NTRS)

Will, E. T.

1992-01-01

The Gravity Probe-B (GP-B) program undertook a screening program to select a possible replacement resin for the E-787 resin currently used in composite neck tubes and support struts. The goal was to find a resin with good cryogenic and structural properties, low-helium permeation and an easily repeatable fabrication process. Cycom 92, SCI REZ 081 and RS-3 were selected for comparison with E-787. Identical composite tubes made from each resin and gamma-alumina fiber (85 percent Al2O3, 15 percent SiO2) were evaluated for cryogenic and structural performance and for processability. Cryogenic performance was evaluated by measuring low-temperature permeation and leaks to determine cryogenic strain behavior. Structural performance was evaluated by comparing the resin-dominated shear strength of the composites. Processability was evaluated from fabrication comments and GP-B's own experience. SCI REZ 081 was selected as the best overall resin with superior strength and cryogenic performance and consistent processability.

Effect of components and surface treatments of fiber-reinforced composite posts on bond strength to composite resin.

PubMed

Asakawa, Yuya; Takahashi, Hidekazu; Kobayashi, Masahiro; Iwasaki, Naohiko

2013-10-01

The aim of this study was to clarify the effect of the components and surface treatments of fiber-reinforced composite (FRC) posts on the durable bonding to core build-up resin evaluated using the pull-out and microtensile tests. Four types of experimental FRC posts, combinations of two types of matrix resins (polymethyl methacrylate and urethane dimethacrylate) and two types of fiberglass (E-glass and zirconia-containing glass) were examined. The FRC posts were subjected to one of three surface treatments (cleaned with ethanol, dichloromethane, or sandblasting). The bond strength between the FRC posts and core build-up resin were measured using the pull-out and microtensile tests before and after thermal cycling. The bond strengths obtained by each test before and after thermal cycling were statistically analyzed by three-way ANOVA and Tukey's multiple comparisons test (p<0.05). The bond strengths except for UDMA by the pull-out test decreased after thermal cycling. Regardless the test method and thermal cycling, matrix resins, the surface treatment and their interaction were statistically significant, but fiberglass did not. Dichloromethane treatment was effective for the PMMA-based FRC posts by the pull-out test, but not by the microtensile test. Sandblasting was effective for both PMMA- and UDMA-based FRC posts, regardless of the test method. The bond strengths were influenced by the matrix resin of the FRC post and the surface treatment. The bond strengths of the pull-out test showed a similar tendency of those of the microtensile test, but the value obtained by these test were different. Copyright © 2013 Elsevier Ltd. All rights reserved.

Color-Matching and Blending-Effect of Universal Shade Bulk-Fill-Resin-Composite in Resin-Composite-Models and Natural Teeth.

PubMed

Abdelraouf, Rasha M; Habib, Nour A

2016-01-01

Objectives . To assess visually color-matching and blending-effect (BE) of a universal shade bulk-fill-resin-composite placed in resin-composite-models with different shades and cavity sizes and in natural teeth (extracted and patients' teeth). Materials and Methods . Resin-composite-discs (10 mm × 1 mm) were prepared of universal shade composite and resin-composite of shades: A1, A2, A3, A3.5, and A4. Spectrophotometric-color-measurement was performed to calculate color-difference (Δ E ) between the universal shade and shaded-resin-composites discs and determine their translucency-parameter (TP). Visual assessment was performed by seven normal-color-vision-observers to determine the color-matching between the universal shade and each shade, under Illuminant D65. Color-matching visual scoring (VS) values were expressed numerically (1-5): 1: mismatch/totally unacceptable, 2: Poor-Match/hardly acceptable, 3: Good-Match/acceptable, 4: Close-Match/small-difference, and 5: Exact-Match/no-color-difference. Occlusal cavities of different sizes were prepared in teeth-like resin-composite-models with shades A1, A2, A3, A3.5, and A4. The cavities were filled by the universal shade composite. The same scale was used to score color-matching between the fillings and composite-models. BE was calculated as difference in mean-visual-scores in models and that of discs. Extracted teeth with two different class I-cavity sizes as well as ten patients' lower posterior molars with occlusal caries were prepared, filled by universal shade composite, and assessed similarly. Results . In models, the universal shade composite showed close matching in the different cavity sizes and surrounding shades (4 ≤ VS < 5) (BE = 0.6-2.9 in small cavities and 0.5-2.8 in large cavities). In extracted teeth, there was good-to-close color-matching (VS = 3.7-4.4 in small cavities, BE = 2.5-3.2) (VS = 3-3.5, BE = 1.8-2.3 in large cavities). In patients' molars, the universal shade composite showed good-matching (VS = 3-3.3, BE = -0.9-2.1). Conclusions . Color-matching of universal shade resin-composite was satisfactory rather than perfect in patients' teeth.

Surface roughness of composite resin veneer after application of herbal and non-herbal toothpaste

NASA Astrophysics Data System (ADS)

Nuraini, S.; Herda, E.; Irawan, B.

2017-08-01

The aim of this study was to find out the surface roughness of composite resin veneer after brushing. In this study, 24 specimens of composite resin veneer are divided into three subgroups: brushed without toothpaste, brushed with non-herbal toothpaste, and brushed with herbal toothpaste. Brushing was performed for one set of 5,000 strokes and continued for a second set of 5,000 strokes. Roughness of composite resin veneer was determined using a Surface Roughness Tester. The results were statistically analyzed using Kruskal-Wallis nonparametric test and Post Hoc Mann-Whitney. The results indicate that the highest difference among the Ra values occurred within the subgroup that was brushed with the herbal toothpaste. In conclusion, the herbal toothpaste produced a rougher surface on composite resin veneer compared to non-herbal toothpaste.

Effect of saliva and blood contamination after etching upon the shear bond strength between composite resin and enamel

NASA Astrophysics Data System (ADS)

Armadi, A. S.; Usman, M.; Suprastiwi, E.

2017-08-01

The aim of this study was to find out the surface roughness of composite resin veneer after brushing. In this study, 24 specimens of composite resin veneer are divided into three subgroups: brushed without toothpaste, brushed with non-herbal toothpaste, and brushed with herbal toothpaste. Brushing was performed for one set of 5,000 strokes and continued for a second set of 5,000 strokes. Roughness of composite resin veneer was determined using a Surface Roughness Tester. The results were statistically analyzed using Kruskal-Wallis nonparametric test and Post Hoc Mann-Whitney. The results indicate that the highest difference among the Ra values occurred within the subgroup that was brushed with the herbal toothpaste. In conclusion, the herbal toothpaste produced a rougher surface on composite resin veneer compared to non-herbal toothpaste.

[Bonding of visible light cured composite resins to glass ionomer and Cermet cements].

PubMed

Kakaboura, A; Vougiouklakis, G

1990-04-01

The "sandwich" technique involves combination of composite resins to etched glassionomer cements, is used today in restorative dentistry. The purpose of this study is to evaluate the bond strength between several composite resins and glass ionomer or cerment cements. Cylindrical specimens of the cements Ketac-Silver, Ionobond and GC-Lining Ce-ment were inserted in a mold and their flat free surfaces were etched for 30". Cylindrical plastic tubes were set upon each one of these surfaces and filled with the Composite resins Durafill, Brilliant Lux, Estilux posterior, Estilux posterior CVS and Herculite XR. Half of the specimens transferred in tap water for 24 hours and the others after thermocycling in the first month, kept for 4 months. Shear bond strengths were determined in Monsanto Testing Machine and some fractured surfaces were examined under SEM. The results of this investigation indicate that this technique produces bond strengths between composite resins and glassioners and the combination type of resin and type of cement, affects the values of the strength. Glass cermeet--small particle resin provides the most effective strength and glass ionomer--microfill resins the least. Storage time and thermocycling don't significantly effect the bond strength. SEM examination showed that all fracture failures were obtained in the cement while the opposite resin surfaces were covered with particles of the cements.

[Comparison of surface roughness of nanofilled and microhybrid composite resins after curing and polishing].

PubMed

Jiang, Hong; Lv, Da; Liu, Kailei; Zhang, Weisheng; Yao, Yao; Liao, Chuhong

2014-05-01

To compare the surface roughness of nanofilled dental composite resin and microhybrid composite resins after curing and polishing. A nanofilled composite (Z350) and 4 microhybrid composites (P60, Z250, Spectrum, and AP-X) were fabricated from the lateral to the medial layers to prepare 8 mm×8 mm×5 mm cubical specimens. The 4 lateral surfaces of each specimens were polished with abrasive disks (Super-Snap). Profilometer was used to test the mean surface roughness (Ra) after polishing. P60 had the lowest Ra (0.125∓0.030 µm) followed by Z250 and Spectrum. The Ra of Z350 (0.205∓0.052 µm) was greater than that of the other 3 resins, and AP-X had the roughest surfaces. Under scanning electron microscope, the polished faces of P60 resin were characterized by minor, evenly distributed particles with fewer scratches; the polished faces of Z350 presented with scratches where defects of the filling material could be seen. The nanofilled composite Z350 has smooth surface after polishing by abrasive disks, but its smoothness remains inferior to that of other micro-hybrid composite resins.

The application of epoxy resin coating in grounding grid

NASA Astrophysics Data System (ADS)

Hu, Q.; Chen, Z. R.; Xi, L. J.; Wang, X. Y.; Wang, H. F.

2018-01-01

Epoxy resin anticorrosion coating is widely used in grounding grid corrosion protection because of its wide range of materials, good antiseptic effect and convenient processing. Based on the latest research progress, four kinds of epoxy anticorrosive coatings are introduced, which are structural modified epoxy coating, inorganic modified epoxy coating, organic modified epoxy coating and polyaniline / epoxy resin composite coating. In this paper, the current research progress of epoxy base coating is analyzed, and prospected the possible development direction of the anti-corrosion coating in the grounding grid, which provides a reference for coating corrosion prevention of grounding materials.

Composites with improved fiber-resin interfacial adhesion

NASA Technical Reports Server (NTRS)

Cizmecioglu, Muzaffer (Inventor)

1989-01-01

The adhesion of fiber reinforcement such as high modulus graphite to a matrix resin such as polycarbonate is greatly enhanced by applying a very thin layer, suitably from 50 Angstroms to below 1000 Angstroms, to the surface of the fiber such as by immersing the fiber in a dilute solution of the matrix resin in a volatile solvent followed by draining to remove excess solution and air drying to remove the solvent. The thin layer wets the fiber surface. The very dilute solution of matrix resin is able to impregnate multifilament fibers and the solution evenly flows onto the surface of the fibers. A thin uniform layer is formed on the surface of the fiber after removal of the solvent. The matrix resin coated fiber is completely wetted by the matrix resin during formation of the composite. Increased adhesion of the resin to the fibers is observed at fracture. At least 65 percent of the surface of the graphite fiber is covered with polycarbonate resin at fracture whereas uncoated fibers have very little matrix resin adhering to their surfaces at fracture and epoxy sized graphite fibers exhibit only slightly higher coverage with matrix resin at fracture. Flexural modulus of the composite containing matrix resin coated fibers is increased by 50 percent and flexural strength by 37 percent as compared to composites made with unsized fibers.

Application of the pentaiodide strong base resin disinfectant to the U.S. space program

NASA Technical Reports Server (NTRS)

Marchin, George L.

1990-01-01

A pentaiodide resin is described which has 70 percent of its weight composed of elemental iodine, has a relatively low iodine residual, and may offer superior disinfection capability for applications on long-duration space vehicles. Such a disinfectant is crucial for use on spacecraft for long periods of time where water would be recycled through various systems. The pentaiodide resin is capable of devitalizing 1 x 10 to the 9th bacteria per ml in aqueous suspension within 10 seconds of contact with the resin bed. A number of organisms have already been tested and the resin continues to prove effective. Resin properties and composition are discussed and a detailed account of the first investigation of the pentaiodide resin as a disinfectant against the intestinal parasite Giardia lamblia is provided.

Influence of the vacuum resin process, on the ballistic behaviour of lightweight armouring solutions

NASA Astrophysics Data System (ADS)

Lefebvre, M.; Boussu, F.; Coutellier, D.; Vallee, D.

2012-08-01

The armour of vehicles against conventional threats is mainly composed with steel or aluminium panels. Efficient heavy solutions exist, but the involved industries require new lightweight structures. Moreover, unconventional threats as IEDs (Improvised Explosive Devices) may cause severe damages on these structural and protective panel solutions. Thus, combination of aluminium or steel plates with textile composite structures used as a backing, leads to the mass reduction and better performance under delamination behaviour against these new threats. This paper is a part of a study dealing with the impact behaviour of three warp interlocks weaving structures under Fragment Simulating Projectile (FSP) impact. During this research, several parameters has being studied as the influence of the yarns insertions [1-4], the degradation of the yarns during the weaving process [5-7], and the influence of the resin rate on the ballistic behaviour. The resin rate inside composite materials is dependant on the final application. In ballistic protection, we need to control the resin rate in order to have a deformable structure in order to absorb the maximum of energy. However, with the warp interlocks weaving structure, the yarns insertions induce empty spaces between the yarns where the resin takes place without being evacuated. The resin rate inside the warp interlocks structures is in the most of cases less than 50%, which lead to have brittle and hard material during the impact. Contrary to interlocks structures, the existing protection based on prepreg structure have a high fibres ratio around 88% of weight. That leads to have the best ballistic properties during the impact and good deformability of the structure. The aim of this paper is to evaluate the influence of the resin rate on the ballistic results of the composites materials. For that, we have chosen two kinds of warp interlocks fabrics which were infused with epoxy resin following two processes. The first is a classical vacuum resin infusion; the second used a press in order to reach a resin ratio near to the existing protection. The existing protection is a prepreg structure with a fibre content of 88%. It has been revealed that a resin rate less than 35% inside the warp interlocks composite material leads to have equivalent ballistics performances than existing protection.

Caries Detection around Restorations Using ICDAS and Optical Devices.

PubMed

Diniz, Michele Baffi; Eckert, George Joseph; González-Cabezas, Carlos; Cordeiro, Rita de Cássia Loiola; Ferreira-Zandona, Andrea Gonçalves

2016-01-01

Secondary caries is the major reason for replacement of restorations in operative dentistry. New detection methods and technology have the potential to improve the accuracy for diagnosis of secondary carious lesions. This in vitro study evaluated the performance of the ICDAS (International Caries Detection and Assessment System) visual criteria and optical devices for detecting secondary caries around amalgam and composite resin restorations in permanent teeth. A total of 180 extracted teeth with Class I amalgam (N = 90) and resin composite (N = 90) restorations were selected. Two examiners analyzed the teeth twice using the visual criteria (ICDAS), laser fluorescence (LF), light-emitting diode device (MID), quantitative light-induced fluorescence system (QLF), and a prototype system based on the Fluorescence Enamel Imaging technique (Professional Caries Detection System, PCDS). The gold standard was determined by means of confocal laser scanning microscopy. High-reproducibility values were shown for all methods, except for MID in the amalgam group. For both groups the QLF and PCDS were the most sensitive methods, whereas the other methods presented better specificity (p < 0.05). All methods, except the MID device appeared to be potential methods for detecting secondary caries only around resin composite restorations, whereas around amalgam restorations all methods seemed to be questionable. Using Internal Caries Detection and Assessment System (ICDAS), an LF device, quantitative light-induced fluorescence and a novel method based on Fluorescence Enamel Imaging technique may be effective for evaluating secondary caries around composite resin restorations. © 2016 Wiley Periodicals, Inc.

Clinical and semiquantitative marginal analysis of four tooth-coloured inlay systems at 3 years.

PubMed

Gladys, S; Van Meerbeek, B; Inokoshi, S; Willems, G; Braem, M; Lambrechts, P; Vanherle, G

1995-12-01

The marginal quality of four tooth-coloured inlay systems was clinically investigated and subjected to computer-aided semiquantitative marginal analysis under scanning electron microscopy (SEM) after 3 years of clinical service. Three of the restoration types were made using the Cerec CAD-CAM apparatus: one was milled from preformed glass ceramic blocks, and the two other inlay types were milled from preformed porcelain blocks. The fourth system was based on an experimental indirect resin composite inlay system. Each inlay type was luted with a different luting resin composite. The clinical evaluation was performed with a mirror and explorer by two clinicians separately, and the marginal analysis was conducted microscopically on replicas (SEM x 200). After 3 years in situ, all the restorations were clinically acceptable. No recurrent caries was observed. Marginal analysis under SEM detected a high percentage of submargination for all four systems, which suggests that their respective resin composite luting agents were all subject to wear. The percentage of marginal fractures on the enamel side as well as on the inlay side did not increase dramatically compared to the 6-month results. The first recall after 6 months of clinical service indicated how tooth-coloured inlays behave at their margins. The 3-year results confirmed the early findings, indicating that wear of resin composite lutes is important and present in all systems. The two ceramic materials showed a similar behaviour at the margins. The resin composite inlay performed better at the inlay site than at the enamel site.

Effect of bench time polymerization on depth of cure of dental composite resin

NASA Astrophysics Data System (ADS)

Harahap, K.; Yudhit, A.; Sari, F.

2017-07-01

The aim of this research was to investigate the effect of bench time before light cured polymerization on the depth of cure of dental composite resin. Nanofiller composite resin (Filtek Z350 XT,3M, ESPE,China) was used in this study. Sixty samples of nanofiller composite resin were made and divided into control and test groups with bench time for 0, 15, 30, 45, and 60 min. For the test group, composite resins were stored in refrigerator with 4°C temperatures. Meanwhile, for the control groups, the composite resin was stored at room temperature. The samples were prepared using metal mould with size diameter of 6 mm and 4 mm in thickness. Samples were cured for 20 s by using visible blue light curing unit. Part of samples that unpolymerized were removed by using a plastic spatula. The remaining parts of samples were measured by digital caliper and noted as depth of cure (mm). Data were analyzed to one-way ANOVA and LSD tests (p≤0.05). Results showed there was no significance differences between test groups (p=0.5). A 60 minutes bench time group showed the highest depth of cure value among test group, and it was almost similar with control group value. It can be concluded that longer bench time can increase the depth of cure of composite resin.

The effect of processing on autohesive strength development in thermoplastic resins and composites

NASA Technical Reports Server (NTRS)

Howes, Jeremy C.; Loos, Alfred C.; Hinkley, Jeffrey A.

1989-01-01

In the present investigation of processing effects on the autohesive bond strength of neat polysulfone resin and graphite-reinforced polysulfone-matrix composites measured resin bond strength development in precracked compact tension specimens 'healed' by heating over a contact period at a given temperature. The critical strain energy release rate of refractured composite specimens did not exhibit the strong time or temperature dependence of the neat resin tests; only 80-90 percent of the undamaged fracture energy is recoverable.

Effects of molecular structure of the resins on the volumetric shrinkage and the mechanical strength of dental restorative composites.

PubMed

Kim, L U; Kim, J W; Kim, C K

2006-09-01

To prepare a dental composite that has a low amount of curing shrinkage and excellent mechanical strength, various 2,2-bis[4-(2-hydroxy-3-methacryloyloxy propoxy) phenyl] propane (Bis-GMA) derivatives were synthesized via molecular structure design, and afterward, properties of their mixtures were explored. Bis-GMA derivatives, which were obtained by substituting methyl groups for hydrogen on the phenyl ring in the Bis-GMA, exhibited lower curing shrinkage than Bis-GMA, whereas their viscosities were higher than that of Bis-GMA. Other Bis-GMA derivatives, which contained a glycidyl methacrylate as a molecular end group exhibited reduced curing shrinkage and viscosity. Methoxy substitution for hydroxyl groups on the Bis-GMA derivatives was performed for the further reduction of the viscosity and curing shrinkage. Various resin mixtures, which had the same viscosity as the commercial one, were prepared, and their curing shrinkage was examined. A resin mixture containing 2,2-bis[3,5-dimethyl, 4-(2-methoxy-3-methacryloyloxy propoxy) phenyl] propane] (TMBis-M-GMA) as a base resin and 4-tert-butylphenoxy-2-methyoxypropyl methacrylate (t-BP-M-GMA) as a diluent exhibited the lowest curing shrinkage among them. The composite prepared from this resin mixture also exhibited the lowest curing shrinkage along with enhanced mechanical properties.

Creep and creep-recovery of a thermoplastic resin and composite

NASA Technical Reports Server (NTRS)

Hiel, Clem

1988-01-01

The database on advanced thermoplastic composites, which is currently available to industry, contains little data on the creep and viscoelastic behavior. This behavior is nevertheless considered important, particularly for extended-service reliability in structural applications. The creep deformation of a specific thermoplastic resin and composite is reviewed. The problem to relate the data obtained on the resin to the data obtained on the composite is discussed.

Synthesis of wrinkled mesoporous silica and its reinforcing effect for dental resin composites.

PubMed

Wang, Ruili; Habib, Eric; Zhu, X X

2017-10-01

The aim of this work is to explore the reinforcing effect of wrinkled mesoporous silica (WMS), which should allow micromechanical resin matrix/filler interlocking in dental resin composites, and to investigate the effect of silica morphology, loading, and compositions on their mechanical properties. WMS (average diameter of 496nm) was prepared through the self-assembly method and characterized by the use of the electron microscopy, dynamic light scattering, and the N 2 adsorption-desorption measurements. The mechanical properties of resin composites containing silanized WMS and nonporous smaller silica were evaluated with a universal mechanical testing machine. Field-emission scanning electron microscopy was used to study the fracture morphology of dental composites. Resin composites including silanized silica particles (average diameter of 507nm) served as the control group. Higher filler loading of silanized WMS substantially improved the mechanical properties of the neat resin matrix, over the composites loaded with regular silanized silica particles similar in size. The impregnation of smaller secondary silica particles with diameters of 90 and 190nm, denoted respectively as Si90 and Si190, increased the filler loading of the bimodal WMS filler (WMS-Si90 or WMS-Si190) to 60wt%, and the corresponding composites exhibited better mechanical properties than the control fillers made with regular silica particles. Among all composites, the optimal WMS-Si190- filled composite (mass ratio WMS:Si190=10:90, total filler loading 60wt%) exhibited the best mechanical performance including flexural strength, flexural modulus, compressive strength and Vickers microhardness. The incorporation of WMS and its mixed bimodal fillers with smaller silica particles led to the design and formulation of dental resin composites with superior mechanical properties. Copyright © 2017 The Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Efficacy of polishing kits on the surface roughness and color stability of different composite resins.

PubMed

Kocaagaoglu, H; Aslan, T; Gürbulak, A; Albayrak, H; Taşdemir, Z; Gumus, H

2017-05-01

Different polishing kits may have different effects on the composite resin surfaces. The aim of this study was to evaluate the surface roughness and color stability of four different composites which was applied different polishing technique. Thirty specimens were made for each composite resin group (nanohybrid, GrandioSo-GS; nanohybrid, Clearfil Majesty Esthetic-CME; hybrid, Valux Plus-VP; micro-hybrid, Ruby Comp-RC; [15 mm in diameter and 2 mm height]), with the different monomer composition and particle size from a total of 120 specimens. Each composite group was divided into three subgroups (n = 10). The first subgroup of the each composite subgroups served as control (C) and had no surface treatment. The second subgroup of the each composite resin groups was polished with finishing discs (Bisco Finishing Discs; Bisco Inc., Schaumburg, IL, USA). The third subgroup of the each composite resin was polished with polishing wheel (Enhance and PoGo, Dentsply, Konstanz, Germany). The surface roughness and the color differences measurement of the specimens were made and recorded. The data were compared using Kruskal-Wallis test, and regression analysis was used in order to examine the correlation between surface roughness and color differences of the specimens (α = 0.05). The Kruskal-Wallis test indicated significant difference among the composite resins in terms of ΔE (P < 0.05), and there was no statistically significant difference among composite resins in terms of surface roughness (P > 0.05). Result of the regression analysis indicated statistically significant correlation between Ra and ΔE values (P < 0.05, r2 = 0.74). The findings of the present study have clinical relevance in the choice of polishing kits used.

The effect of tooth age on colour adjustment potential of resin composite restorations.

PubMed

Tanaka, A; Nakajima, M; Seki, N; Foxton, R M; Tagami, J

2015-02-01

The purpose of this study was to investigate the effect of tooth age on colour adjustment potential of resin composite restorations in human teeth. Twenty extracted human premolars with an A2 shade, extracted for orthodontic reasons from younger patients (20-28yrs) (younger teeth) and periodontal reasons from older patients (45-69yrs) (older teeth), were used in this study. Cylindrical shaped cavities (3.0mm depth; 2.0mm diameter) were prepared in the centre of the crowns on the buccal surface. One of four resin composites of A2 shade (Kalore, KA; Solare, SO; Clearfil Majesty, MJ; Beautifil II, BF) was placed in the cavity, and the colour was measured at four areas (0.4mm×0.4mm) on the restored teeth (area 1; tooth area 1.0mm away from the border of resin composite restoration: area 2; tooth border area 0.3mm away from margin of resin composite restoration: area 3; resin composite border area 0.3mm away from margin of resin composite restoration: area 4; resin composite area at the centre of resin composite restoration) using a spectrophotometer (Crystaleye). The colour of each area was determined according to the CIELAB colour scale. Colour differences (ΔE*) between the areas of 1 and 2, 2 and 3, 3 and 4 and 1 and 4 were calculated, and also the ratio of ΔE*area2-3 to ΔE*area1-4 (ΔE*area2-3/1-4), ΔE*area3-4 to ΔE*area1-4 (ΔE*area3-4/1-4) and ΔE*area1-2 to ΔE*area1-4 (ΔE*area1-2/1-4) as a parameter of the colour shift in resin composite restoration, were determined. Moreover, the light transmission characteristics of the resin materials and dentine discs from the younger and older teeth were measured using a goniophotometer. The data were statistically analyzed using two-way ANOVA, and Dunnett's T3 and t-test for the post hoc test. ΔE*area2-3 (colour difference between resin composite and tooth at the border) and ΔE*area1-4 (colour difference between resin composite and tooth) of the older teeth groups were significantly larger than those of younger teeth groups (p<0.05). The ΔE*area2-3/1-4 (mis-match rate in colour shifting at the border) of the older teeth groups was larger than that of the younger teeth groups (p<0.05). ΔE*area3-4/1-4 (colour shifting rate of resin composite side) was significantly larger in older teeth than younger teeth (p<0.05), while ΔE*area1-2/1-4 (colour shifting rate of tooth side), was significantly smaller in older teeth than younger teeth (p<0.05). In each tooth group, there were no significant differences in ΔE*area2-3, ΔE*area1-4, ΔE*area2-3/1-4, ΔE*area3-4/1-4 and ΔE*area1-2/1-4 between the materials (p>0.05). Analysis of the light transmission properties indicated that older dentine transmitted more light, while younger dentine exhibited greater light diffusion and transmitted less light. The colour shifting effects at the border of the resin composite restorations were influenced by the age of the tooth. This behaviour might be influenced by the light transmission characteristics of dentine in restored teeth. The potential for colour adjustment of resin composite restorations may be less in older teeth than younger teeth. Copyright © 2014 Elsevier Ltd. All rights reserved.

Changes in fats and resins of Pinus radiata associated with heartwood formation

Treesearch

Richard W. Hemingway; W.E. Hillis

1971-01-01

In an analysis of Australian grown P. radiata marked changes were found in the relative proportions and compositions of the resin acids, fatty acids, and fatty acid esters associated with heartwood formation. While the proportion of resin acids increased substantially in the heartwood, there was little change in resin acid composition from outer...

Curing behavior and reaction kinetics of binder resins for 3D-printing investigated by dielectric analysis (DEA)

NASA Astrophysics Data System (ADS)

Möginger, B.; Kehret, L.; Hausnerova, B.; Steinhaus, J.

2016-05-01

3D-Printing is an efficient method in the field of additive manufacturing. In order to optimize the properties of manufactured parts it is essential to adapt the curing behavior of the resin systems with respect to the requirements. Thus, effects of resin composition, e.g. due to different additives such as thickener and curing agents, on the curing behavior have to be known. As the resin transfers from a liquid to a solid glass the time dependent ion viscosity was measured using DEA with flat IDEX sensors. This allows for a sensitive measurement of resin changes as the ion viscosity changes two to four decades. The investigated resin systems are based on the monomers styrene and HEMA. To account for the effects of copolymerization in the calculation of the reaction kinetics it was assumed that the reaction can be considered as a homo-polymerization having a reaction order n≠1. Then the measured ion viscosity curves are fitted with the solution of the reactions kinetics - the time dependent degree of conversion (DC-function) - for times exceeding the initiation phase representing the primary curing. The measured ion viscosity curves can nicely be fitted with the DC-function and the determined fit parameters distinguish distinctly between the investigated resin compositions.

Contact angle and surface free energy of experimental resin-based dental restorative materials after chewing simulation.

PubMed

Rüttermann, Stefan; Beikler, Thomas; Janda, Ralf

2014-06-01

To investigate contact angle and surface free energy of experimental dental resin composites containing novel delivery systems of polymeric hollow beads and low-surface tension agents after chewing simulation test. A delivery system of novel polymeric hollow beads differently loaded with two low-surface tension agents was used in different amounts to modify commonly formulated experimental dental resin composites. The non-modified resin was used as standard. Surface roughness Ra, contact angle Θ, total surface free energy γS, its apolar γS(LW), polar γS(AB), Lewis acid γS(+) and base γS(-) terms were determined and the results prior to and after chewing simulation test were compared. Significance was p<0.05. After chewing simulation Ra increased, Θ decreased, Ra increased for two test materials and γS decreased or remained constant for the standard or the test materials after chewing simulation. Ra of one test material was higher than of the standard, Θ and γS of the test materials remained lower than of the standard and, indicating their highly hydrophobic character (Θ≈60-75°, γS≈30mJm(-2)). γS(LW), and γS(-) of the test materials were lower than of the standard. Some of the test materials had lower γS(AB) and γS(+) than of the standard. Delivery systems based on novel polymeric hollow beads highly loaded with low-surface tension agents were found to significantly increase contact angle and thus to reduce surface free energy of experimental dental resin composites prior to and after chewing simulation test. Copyright © 2014 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Simulation Based Low-Cost Composite Process Development at the US Air Force Research Laboratory

NASA Technical Reports Server (NTRS)

Rice, Brian P.; Lee, C. William; Curliss, David B.

2003-01-01

Low-cost composite research in the US Air Force Research Laboratory, Materials and Manufacturing Directorate, Organic Matrix Composites Branch has focused on the theme of affordable performance. Practically, this means that we use a very broad view when considering the affordability of composites. Factors such as material costs, labor costs, recurring and nonrecurring manufacturing costs are balanced against performance to arrive at the relative affordability vs. performance measure of merit. The research efforts discussed here are two projects focused on affordable processing of composites. The first topic is the use of a neural network scheme to model cure reaction kinetics, then utilize the kinetics coupled with simple heat transport models to predict, in real-time, future exotherms and control them. The neural network scheme is demonstrated to be very robust and a much more efficient method that mechanistic cure modeling approach. This enables very practical low-cost processing of thick composite parts. The second project is liquid composite molding (LCM) process simulation. LCM processing of large 3D integrated composite parts has been demonstrated to be a very cost effective way to produce large integrated aerospace components specific examples of LCM processes are resin transfer molding (RTM), vacuum assisted resin transfer molding (VARTM), and other similar approaches. LCM process simulation is a critical part of developing an LCM process approach. Flow simulation enables the development of the most robust approach to introducing resin into complex preforms. Furthermore, LCM simulation can be used in conjunction with flow front sensors to control the LCM process in real-time to account for preform or resin variability.

Color Stability Assessment of Two Different Composite Resins with Variable Immersion Time Using Various Beverages: An In vitro Study

PubMed Central

Kumar, M. Senthil; Ajay, R.; Miskeen Sahib, S. A.; Chittrarasu, M.; Navarasu, M.; Ragavendran, N.; Burhanuddin Mohammed, Omar Farooq

2017-01-01

Purpose of the Study: The aim of the study was to evaluate the difference in the color of microhybrid (MH) and nanofilled (NF) composite resins after 24 and 48 h in beverages such as red wine (RW), Coca-Cola, and distilled water. The specific objective of this study was to investigate the cumulative effect of the colorant solutions on the dental composites. Materials and Methods: MH and NF composite resins (A2 shade) were used in this current study. Sixty disk-shaped material specimens (10 mm in diameter × 2 mm in thickness) were prepared using a fiber mold (ring), with the desired dimensions. The specimen surfaces were polished using super-snap polishing system. Sixty specimens were divided into two groups of 30 each (Group I: MH resin composite; Group II: NF resin composite). Both the groups divided into six subgroups (Subgroup I: RW for 24 h [RW-24]; Subgroup II: RW for 48 h; Subgroup III: Coca-Cola for 24 h [CC-24]; Subgroup IV: Coca-Cola for 48 h [CC-48]; Subgroup V: Distilled water for 24 h [DW-24]; Subgroup VI: Distilled water for 48 h [DW-48]). All the samples were immersed in respective drinks for a period of 24 h, and color differences were measured using ultraviolet spectrophotometer. Once again, all the samples were immersed for another 24 h in the same drinks. After 48 h, the color change of the samples was measured. Measurements were made according to the CIE L × a × b × color space relative to the CIE standard illuminant D65. The color changes of the specimens were evaluated using the following formula: Statistical analysis was performed. The data were analyzed using the one-way ANOVA and t-test at a significance level of 0.05. Conclusion: Color stability of MH composite resin was found to be inferior than the NF resin composite irrespective of immersion medium and time. In RW, the color change observed was maximum for both composite resins followed by Coca-Cola. Immersing the resin composites in distilled water for 24 and 48 h had negligible color change. A 48-h immersion of both composite resins in all three immersion mediums showed greater color change than 24 h immersion. PMID:29284957

Color Stability Assessment of Two Different Composite Resins with Variable Immersion Time Using Various Beverages: An In vitro Study.

PubMed

Kumar, M Senthil; Ajay, R; Miskeen Sahib, S A; Chittrarasu, M; Navarasu, M; Ragavendran, N; Burhanuddin Mohammed, Omar Farooq

2017-11-01

The aim of the study was to evaluate the difference in the color of microhybrid (MH) and nanofilled (NF) composite resins after 24 and 48 h in beverages such as red wine (RW), Coca-Cola, and distilled water. The specific objective of this study was to investigate the cumulative effect of the colorant solutions on the dental composites. MH and NF composite resins (A2 shade) were used in this current study. Sixty disk-shaped material specimens (10 mm in diameter × 2 mm in thickness) were prepared using a fiber mold (ring), with the desired dimensions. The specimen surfaces were polished using super-snap polishing system. Sixty specimens were divided into two groups of 30 each (Group I: MH resin composite; Group II: NF resin composite). Both the groups divided into six subgroups (Subgroup I: RW for 24 h [RW-24]; Subgroup II: RW for 48 h; Subgroup III: Coca-Cola for 24 h [CC-24]; Subgroup IV: Coca-Cola for 48 h [CC-48]; Subgroup V: Distilled water for 24 h [DW-24]; Subgroup VI: Distilled water for 48 h [DW-48]). All the samples were immersed in respective drinks for a period of 24 h, and color differences were measured using ultraviolet spectrophotometer. Once again, all the samples were immersed for another 24 h in the same drinks. After 48 h, the color change of the samples was measured. Measurements were made according to the CIE L × a × b × color space relative to the CIE standard illuminant D65. The color changes of the specimens were evaluated using the following formula: Statistical analysis was performed. The data were analyzed using the one-way ANOVA and t -test at a significance level of 0.05. Color stability of MH composite resin was found to be inferior than the NF resin composite irrespective of immersion medium and time. In RW, the color change observed was maximum for both composite resins followed by Coca-Cola. Immersing the resin composites in distilled water for 24 and 48 h had negligible color change. A 48-h immersion of both composite resins in all three immersion mediums showed greater color change than 24 h immersion.

Glass Fiber Resin Composites and Components at Arctic Temperatures

DTIC Science & Technology

2015-06-01

NAVAL POSTGRADUATE SCHOOL MONTEREY, CALIFORNIA THESIS Approved for public release; distribution is unlimited GLASS FIBER RESIN...3. REPORT TYPE AND DATES COVERED Master’s Thesis 4. TITLE AND SUBTITLE GLASS FIBER RESIN COMPOSITES AND COMPONENTS AT ARCTIC TEMPERATURES 5...public release; distribution is unlimited 12b. DISTRIBUTION CODE 13. ABSTRACT (maximum 200 words) Glass fiber reinforced composites (GFRC

Mechanically stiff, electrically conductive composites of polymers and carbon nanotubes

DOEpatents

Worsley, Marcus A.; Kucheyev, Sergei O.; Baumann, Theodore F.; Kuntz, Joshua D.; Satcher, Jr., Joe H.; Hamza, Alex V.

2015-07-21

Using SWNT-CA as scaffolds to fabricate stiff, highly conductive polymer (PDMS) composites. The SWNT-CA is immersing in a polymer resin to produce a SWNT-CA infiltrated with a polymer resin. The SWNT-CA infiltrated with a polymer resin is cured to produce the stiff and electrically conductive composite of carbon nanotube aerogel and polymer.

Mechanically stiff, electrically conductive composites of polymers and carbon nanotubes

DOEpatents

Worsley, Marcus A.; Kucheyev, Sergei O.; Baumann, Theodore F.; Kuntz, Joshua D.; Satcher, Jr., Joe H.; Hamza, Alex V.

2017-10-17

Using SWNT-CA as scaffolds to fabricate stiff, highly conductive polymer (PDMS) composites. The SWNT-CA is immersing in a polymer resin to produce a SWNT-CA infiltrated with a polymer resin. The SWNT-CA infiltrated with a polymer resin is cured to produce the stiff and electrically conductive composite of carbon nanotube aerogel and polymer.

Piezoresistivity of Resin-Impregnated Carbon Nanotube Film at High Temperatures.

PubMed

Li, Min; Zuo, Tianyi; Wang, Shaokai; Gu, Yizhuo; Gao, Limin; Li, Yanxia; Zhang, Zuoguang

2018-06-13

This paper presents the development of a continuous carbon nanotube (CNT) composite film sensor with a strain detecting range of 0-2% for structural composites. The strain-dependent resistance responses of continuous CNT film and its resin-impregnated composite films were investigated at temperatures as high as 200 °C. The results manifest that impregnation with resin leads to a much larger gauge factor than pristine film. Both the pristine and composite films show an increase in resistivity with increasing temperature. For different composite films, the ordering of gauge factors is consistent with that of the matrix moduli. This indicates that a resin matrix with higher modulus and strong interactions between CNTs/CNT bundles and the resin matrix are beneficial for enhancing the piezoresistive effect. The CNT/PAA composite film has a gauge factor of 4.3 at 150 °C, an order of magnitude higher than the metal foil sensor. Therefore, the CNT composite films have great potential for simultaneous application for reinforcement and as strain sensor to realise a multifunctional composite. © 2018 IOP Publishing Ltd.

Effect of esthetic core shades on the final color of IPS Empress all-ceramic crowns.

PubMed

Azer, Shereen S; Ayash, Ghada M; Johnston, William M; Khalil, Moustafa F; Rosenstiel, Stephen F

2006-12-01

Clinically relevant assessment of all-ceramic crowns supported by esthetic composite resin foundations has not been evaluated with regard to color reproducibility. This in vitro study quantitatively evaluated the influence of different shades of composite resin foundations and resin cement on the final color of a leucite-reinforced all-ceramic material. A total of 128 disks were fabricated; 64 (20 x 1 mm) were made of all-ceramic material (IPS Empress) and 64 (20 x 4 mm) of 4 different shades composite resin (Tetric Ceram). The ceramic and composite resin disks were luted using 2 shades (A3 and Transparent) of resin cement (Variolink II). Color was measured using a colorimeter configured with a diffuse illumination/0-degree viewing geometry, and Commission Internationale de l'Eclairage (CIE) L( *)a( *)b( *) values were directly calculated. Descriptive statistical analysis was performed, and color differences (DeltaE) for the average L( *), a( *) and b( *) color parameters were calculated. Repeated measures analysis of variance (ANOVA) was used to compare mean values and SDs between the different color combinations (alpha=.05). The CIE L( *)a( *)b( *) color coordinate values showed no significant differences for variation in color parameters due to the effect of the different composite resin shades (P=.24) or cement shades (P=.12). The mean color difference (DeltaE) value between the groups was 0.8. Within the limitations of this study, the use of different shades for composite resin cores and resin cements presented no statistically significant effect on the final color of IPS Empress all-ceramic material.

Selective degradation of organic dyes by a resin modified Fe-based metal-organic framework under visible light irradiation

NASA Astrophysics Data System (ADS)

Araya, Tirusew; Chen, Chun-cheng; Jia, Man-ke; Johnson, David; Li, Ruiping; Huang, Ying-ping

2017-02-01

Metal organic frameworks (MOFs), a new class of porous crystalline materials have attracted attention because of potential applications in environmental remediation. In this work, an Fe-based MOF, FeBTC (BTC = 1,3,5-tricarboxylic acid), was successfully modified with Amberlite IRA-200 resin to yield a novel heterogeneous photocatalyst, A@FeBTC. The modification resulted in higher photocatalytic activity than FeBTC under the same conditions. After 60 min of visible light illumination (λ ≥ 420 nm) 99% of rhodamine B was degraded. The modification lowers the zeta potential, enhancing charge-based selective adsorption and subsequent photocatalytic degradation of cationic dye pollutants. The composite also improved catalyst stability and recyclability by significantly reducing loss of iron leaching. Photoluminescence studies show that introduction of the resin reduces the recombination rate of photogenerated charge carriers thereby improving the photocatalytic activity of the composite. Finally, a plausible photocatalytic reaction mechanism is proposed.

Evaluation of Four Different Restorative Materials for Restoration of the Periodontal Condition of Wedge-Shaped Defect: A Comparative Study.

PubMed

Ruan, Jian-Yong; Gong, Zheng-Lin; Zhang, Rui-Zhi; Zhang, Zhe; Xu, Ran; Li, Da-Xu; Ren, Le; Tao, Hong

2017-09-16

BACKGROUND This study aimed to conduct a clinical evaluation of four restorative materials for restoration of dental wedge-shaped defect (WSD) and their impacts on periodontal tissues. MATERIAL AND METHODS A total of 280 maxillary premolars with dental WSD were selected from 106 patients; the patient cases were divided into eight groups according to different combinations of restorative materials (flowable resin composites, Dyract compomers, glass ionomer cement (GIC), light-curing composite resin), and WSD positions (approaching gingival and subgingival positions). Gingival crevicular fluid (GCF) volume, levels of aspartate aminotransferase (AST), alkaline phosphatase (ALP), and interleukin-1β (IL-1β) in GCF were analyzed, while probing depth (PD), plaque index (PLI), and sulcus bleeding index (SBI) were also measured. The periodontal conditions of all patients were followed prior to restoration, as well as six months and 12 months after restoration. RESULTS After six months of restoration, the overall clinical success rates of flowable resin composites, Dyract compomers, and light-curing composite resin were greater than those of GIC. GCF volume, GCF-AST, IL-1β levels, PD, PLI, and SBI of cases restored by GIC were higher than those restored by the other three materials. After 12 months of restoration, the overall clinical success rates of flowable resin composites and Dyract compomers were greater than those of light-curing composite resin and GIC. GCF volume, GCF-AST, GCF-ALP, IL-1β levels, PD, PLI, and SBI of cases restored by GIC were higher than those restored by the other three materials. CONCLUSIONS Our study provided evidence that the clinical efficacy of flowable resin composites, Dyract compomers, and light-curing composite resin was greater than that of GIC for restoration of dental WSD.

Evaluation of Four Different Restorative Materials for Restoration of the Periodontal Condition of Wedge-Shaped Defect: A Comparative Study

PubMed Central

Ruan, Jian-Yong; Gong, Zheng-Lin; Zhang, Rui-Zhi; Zhang, Zhe; Xu, Ran; Li, Da-Xu; Ren, Le; Tao, Hong

2017-01-01

Background This study aimed to conduct a clinical evaluation of four restorative materials for restoration of dental wedge-shaped defect (WSD) and their impacts on periodontal tissues. Material/Methods A total of 280 maxillary premolars with dental WSD were selected from 106 patients; the patient cases were divided into eight groups according to different combinations of restorative materials (flowable resin composites, Dyract compomers, glass ionomer cement (GIC), light-curing composite resin), and WSD positions (approaching gingival and subgingival positions). Gingival crevicular fluid (GCF) volume, levels of aspartate aminotransferase (AST), alkaline phosphatase (ALP), and interleukin-1β (IL-1β) in GCF were analyzed, while probing depth (PD), plaque index (PLI), and sulcus bleeding index (SBI) were also measured. The periodontal conditions of all patients were followed prior to restoration, as well as six months and 12 months after restoration. Results After six months of restoration, the overall clinical success rates of flowable resin composites, Dyract compomers, and light-curing composite resin were greater than those of GIC. GCF volume, GCF-AST, IL-1β levels, PD, PLI, and SBI of cases restored by GIC were higher than those restored by the other three materials. After 12 months of restoration, the overall clinical success rates of flowable resin composites and Dyract compomers were greater than those of light-curing composite resin and GIC. GCF volume, GCF-AST, GCF-ALP, IL-1β levels, PD, PLI, and SBI of cases restored by GIC were higher than those restored by the other three materials. Conclusions Our study provided evidence that the clinical efficacy of flowable resin composites, Dyract compomers, and light-curing composite resin was greater than that of GIC for restoration of dental WSD. PMID:28917087

Fracture strength testing of crowns made of CAD/CAM composite resins.

PubMed

Okada, Ryota; Asakura, Masaki; Ando, Akihiro; Kumano, Hirokazu; Ban, Seiji; Kawai, Tatsushi; Takebe, Jun

2018-03-28

The purpose of this study was to ascertain whether computer aided design/computer aided manufacturing (CAD/CAM) composite resin crowns have sufficient strength to withstand the bite force of the molar teeth. The null hypothesis was that the fracture strength of CAD/CAM composite resin crowns is lower than the average maximum bite force of the molar tooth. The crowns, which shape is the right maxillary first molar, were fabricated using four CAD/CAM blanks made of composite resins (Block HC: HC, KZR-CAD HR: HR, KZR-CAD HR2: HR2, Avencia Block: AVE) and one CAD/CAM blank made of lithium disilicate glass-ceramic (IPS e.max CAD: IPS), which was used as a control. Fracture strength of fabricated crowns bonded to metal abutment and biaxial flexural strength of the materials were evaluated. The results of fracture strength test and biaxial flexural strength test showed different tendencies. The fracture strength of CAD/CAM composite resin crowns except HC ranged from 3.3kN to 3.9kN, and was similar to that of IPS (3.3kN). In contrast, biaxial flexural strength of CAD/CAM composite resins ranged from 175MPa to 247MPa, and was significantly lower than that of IPS (360MPa). All CAD/CAM composite resin crowns studied presented about 3-4 times higher fracture strength than the average maximum bite force of the molar tooth (700-900N), which result leads to the conclusion that CAD/CAM composite resin crowns would have sufficient strength to withstand the bite force of the molar teeth. Copyright © 2017 Japan Prosthodontic Society. Published by Elsevier Ltd. All rights reserved.

Evaluation of three different decontamination techniques on biofilm formation, and on physical and chemical properties of resin composites.

PubMed

André, Carolina Bosso; Dos Santos, Andressa; Pfeifer, Carmem Silvia; Giannini, Marcelo; Girotto, Emerson Marcelo; Ferracane, Jack Liborio

2018-04-01

This study evaluated three different sterilization/disinfection techniques for resin composites on bacterial growth and surface modification after decontamination. Two resin composites were sterilized/disinfected with three different techniques: UV light, 1% chloramine T, and 70% ethanol. Four different times were used for each technique to determine the shortest time that the solution or UV light was effective. The influence of sterilization/disinfection technique on bacterial growth was evaluated by analyzing the metabolic activity, using the AlamarBlue™ assay, bacterial viability, and SEM images from biofilms of Streptococcus mutans. The surface change, after the process, was analyzed with ATR/FTIR and SEM images. The solutions used for decontamination (1% chloramine-T and 70% ethanol) were analyzed with 1 H-NMR to identify any resin compounds leached during the process. One minute of decontamination was efficient for all three methods tested. Chloramine-T increased the surface porosity on resin composites, no changes were observed for UV light and 70% ethanol, however, 1 H-NMR identified leached monomers only when 70% ethanol was used. No chemical change of the materials was found under ATR/FTIR analyses after the decontamination process. Chloramine-T, with no previous wash, increased the bacterial viability for both resin composites and increased the bacterial metabolism for the resin composite without fluoride. UV light had no interference on the resin composites properties tested using 1 min of exposure compared to the other decontamination methods. © 2017 Wiley Periodicals, Inc. J Biomed Mater Res Part B: Appl Biomater, 106B: 945-953, 2018. © 2017 Wiley Periodicals, Inc.

Composite Cure Process Modeling and Simulations using COMPRO(Registered Trademark) and Validation of Residual Strains using Fiber Optics Sensors

NASA Technical Reports Server (NTRS)

Sreekantamurthy, Thammaiah; Hudson, Tyler B.; Hou, Tan-Hung; Grimsley, Brian W.

2016-01-01

Composite cure process induced residual strains and warping deformations in composite components present significant challenges in the manufacturing of advanced composite structure. As a part of the Manufacturing Process and Simulation initiative of the NASA Advanced Composite Project (ACP), research is being conducted on the composite cure process by developing an understanding of the fundamental mechanisms by which the process induced factors influence the residual responses. In this regard, analytical studies have been conducted on the cure process modeling of composite structural parts with varied physical, thermal, and resin flow process characteristics. The cure process simulation results were analyzed to interpret the cure response predictions based on the underlying physics incorporated into the modeling tool. In the cure-kinetic analysis, the model predictions on the degree of cure, resin viscosity and modulus were interpreted with reference to the temperature distribution in the composite panel part and tool setup during autoclave or hot-press curing cycles. In the fiber-bed compaction simulation, the pore pressure and resin flow velocity in the porous media models, and the compaction strain responses under applied pressure were studied to interpret the fiber volume fraction distribution predictions. In the structural simulation, the effect of temperature on the resin and ply modulus, and thermal coefficient changes during curing on predicted mechanical strains and chemical cure shrinkage strains were studied to understand the residual strains and stress response predictions. In addition to computational analysis, experimental studies were conducted to measure strains during the curing of laminated panels by means of optical fiber Bragg grating sensors (FBGs) embedded in the resin impregnated panels. The residual strain measurements from laboratory tests were then compared with the analytical model predictions. The paper describes the cure process procedures and residual strain predications, and discusses pertinent experimental results from the validation studies.

Studies on mechanical properties of graphene based hybrid composites reinforced with kenaf/glass fiber

NASA Astrophysics Data System (ADS)

Kumar, S. C. Ramesh; Shivanand, H. K.; Vidayasagar, H. N.; Nagabhushan, V.

2018-04-01

The polymer composites are developed with natural fibers and fillers as a alternate material for some of the engineering applications in the field of automobiles and domestic purposes are being investigated. The natural fiber composites such as banana, sisal, jute, coir, kenaf and hemp polymer composites appear more effective due to their lightweight, higher specific strength, biodegradable and cost is low. The main objective is to prepare the Kenaf/Glass fiber hybrid composite filled with graphene as nano filler and to investigate the mechanical properties of hybrid composites. The different types of hybrid composites laminates are fabricated without filler, 0.5, 1 & 1.5Wt % of graphene by using kenaf and glass fiber as reinforcing material with epoxy resin. The specimen were prepared as per the ASTM standards and results shows that the mixing of graphene in epoxy resin improves the mechanical properties of hybrid composites.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Arman, B.; An, Q.; Luo, S. N.

We investigate with nonreactive molecular dynamics simulations the dynamic response of phenolic resin and its carbon-nanotube (CNT) composites to shock wave compression. For phenolic resin, our simulations yield shock states in agreement with experiments on similar polymers except the “phase change” observed in experiments, indicating that such phase change is chemical in nature. The elastic–plastic transition is characterized by shear stress relaxation and atomic-level slip, and phenolic resin shows strong strain hardening. Shock loading of the CNT-resin composites is applied parallel or perpendicular to the CNT axis, and the composites demonstrate anisotropy in wave propagation, yield and CNT deformation. Themore » CNTs induce stress concentrations in the composites and may increase the yield strength. Our simulations indicate that the bulk shock response of the composites depends on the volume fraction, length ratio, impact cross-section, and geometry of the CNT components; the short CNTs in current simulations have insignificant effect on the bulk response of resin polymer.« less

Halogen-free benzoxazine based curable compositions for high TG applications

DOE Office of Scientific and Technical Information (OSTI.GOV)

Tietze, Roger; Nguyen, Yen-Loan

The present invention provides a halogen-free curable composition including a benzoxazine monomer, at least one epoxy resin, a catalyst, a toughening agent and a solvent. The halogen-free curable composition is especially suited for use in automobile and aerospace applications since the composition, upon curing, produces a composite having a high glass transition temperature.

Halogen free benzoxazine based curable compositions for high T.sub.g applications

DOE Office of Scientific and Technical Information (OSTI.GOV)

Tietze, Roger; Nguyen, Yen-Loan

A method for forming a halogen-free curable composition containing a benzoxazine monomer, at least one epoxy resin, a catalyst, a toughening agent and a solvent. The halogen-free curable composition is especially suited for use in automobile and aerospace applications since the composition, upon curing, produces a composite having a high glass transition temperature.

The effect of remin pro and MI paste plus on bleached enamel surface roughness.

PubMed

Ahmad Akhoundi, Mohammad Sadegh; Aghajani, Farzaneh; Chalipa, Javad; Sadrhaghighi, Amir Hooman

2014-03-01

Increased number of adult patients requesting orthodontic treatment result in bonding bracket to ceramic restorations more than before. The aim of this study was to evaluate and compare the shear bond strength of orthodontic brackets bonded to two types of ceramic bases with conventional orthodontic bonding resin and a new nano-filled composite resin. Twenty four feldespathic porcelain and 24 lithium disilicate ceramic disks were fabricated. All of the samples were conditioned by sandblasting, hydrofluoric acid and silane. Maxillary incisor metal brackets were bonded to half of the disks in each group by conventional orthodontic bonding resin and the other half bonded with a nano-filled composite. The samples then were thermocycled for 2000 cycle between 5-55° C. Shear bond strength was measured and the mode of failure was examined. Randomly selected samples were also evaluated by SEM. The lowest bond strength value was found infeldespathic ceramic bonded by nano-filled composite (p<0.05). There was not any statistically significant difference between other groups regarding bond strength. The mode of failure in the all groups except group 1 was cohesive and porcelain damages were detected. Since less damages to feldspathic porcelain was observed when the nano-filled composite was used to bond brackets, the use of nano-filled composite resins can be suggested for bonding brackets to feldspathic porcelain restorations.

The Effect of Remin Pro and MI Paste Plus on Bleached Enamel Surface Roughness

PubMed Central

Ahmad Akhoundi, Mohammad Sadegh; Aghajani, Farzaneh; Chalipa, Javad; Sadrhaghighi, Amir Hooman

2014-01-01

Objective Increased number of adult patients requesting orthodontic treatment result in bonding bracket to ceramic restorations more than before. The aim of this study was to evaluate and compare the shear bond strength of orthodontic brackets bonded to two types of ceramic bases with conventional orthodontic bonding resin and a new nano-filled composite resin. Materials and Methods: Twenty four feldespathic porcelain and 24 lithium disilicate ceramic disks were fabricated. All of the samples were conditioned by sandblasting, hydrofluoric acid and silane. Maxillary incisor metal brackets were bonded to half of the disks in each group by conventional orthodontic bonding resin and the other half bonded with a nano-filled composite. The samples then were thermocycled for 2000 cycle between 5–55° C. Shear bond strength was measured and the mode of failure was examined. Randomly selected samples were also evaluated by SEM. Results: The lowest bond strength value was found infeldespathic ceramic bonded by nano-filled composite (p<0.05). There was not any statistically significant difference between other groups regarding bond strength. The mode of failure in the all groups except group 1 was cohesive and porcelain damages were detected. Conclusion: Since less damages to feldspathic porcelain was observed when the nano-filled composite was used to bond brackets, the use of nano-filled composite resins can be suggested for bonding brackets to feldspathic porcelain restorations. PMID:24910698

Composite impact strength improvement through a fiber/matrix interphase

NASA Technical Reports Server (NTRS)

Cavano, P. J.; Winters, W. E.

1975-01-01

Research was conducted to improve the impact strength and toughness of fiber/resin composites by means of a fiber coating interphase. Graphite fiber/epoxy resin composites were fabricated with four different fiber coating systems introduced in a matrix-fiber interphase. Two graphite fibers, a high strength and a high modulus type, were studied with the following coating systems: chemical vapor deposited boron, electroless nickel, a polyamide-imide resin and a thermoplastic polysulfone resin. Evaluation methods included the following tests: Izod, flexure, shear fracture toughness, longitudinal and transverse tensile, and transverse and longitudinal compression. No desirable changes could be effected with the high strength fiber, but significant improvements in impact performance were observed with the polyamide-imide resin coated high modulus fiber with no loss in composite modulus.

Effect of Energy Drinks on Discoloration of Silorane and Dimethacrylate-Based Composite Resins

PubMed Central

Ahmadizenouz, Ghazaleh; Esmaeili, Behnaz; Ahangari, Zohreh; Khafri, Soraya; Rahmani, Aghil

2016-01-01

Objectives: This study aimed to assess the effects of two energy drinks on color change (ΔE) of two methacrylate-based and a silorane-based composite resin after one week and one month. Materials and Methods: Thirty cubic samples were fabricated from Filtek P90, Filtek Z250 and Filtek Z350XT composite resins. All the specimens were stored in distilled water at 37°C for 24 hours. Baseline color values (L*a*b*) of each specimen were measured using a spectrophotometer according to the CIEL*a*b* color system. Ten randomly selected specimens from each composite were then immersed in the two energy drinks (Hype, Red Bull) and artificial saliva (control) for one week and one month. Color was re-assessed after each storage period and ΔE values were calculated. The data were analyzed using the Kruskal Wallis and Mann–Whitney U tests. Results: Filtek Z250 composite showed the highest ΔE irrespective of the solutions at both time points. After seven days and one month, the lowest ΔE values were observed in Filtek Z350XT and Filtek P90 composites immersed in artificial saliva, respectively. The ΔE values of Filtek Z250 and Z350XT composites induced by Red Bull and Hype energy drinks were not significantly different. Discoloration of Filtek P90 was higher in Red Bull energy drink at both time points. Conclusions: Prolonged immersion time in all three solutions increased ΔE values of all composites. However, the ΔE values were within the clinically acceptable range (<3.3) at both time points. PMID:28127318

Composite anion-exchangers modified with nanoparticles of hydrated oxides of multivalent metals

NASA Astrophysics Data System (ADS)

Maltseva, T. V.; Kolomiets, E. O.; Dzyazko, Yu. S.; Scherbakov, S.

2018-02-01

Organic-inorganic composite ion-exchangers based on anion exchange resins have been obtained. Particles of one-component and two-component modifier were embedded using the approach, which allows us to realize purposeful control of a size of the embedded particles. The approach is based on Ostwald-Freundlich equation, which was adapted to deposition in ion exchange matrix. The equation was obtained experimentally. Hydrated oxides of zirconium and iron were applied to modification, concentration of the reagents were varied. The embedded particles accelerate sorption, the rate of which is fitted by the model equation of chemical reactions of pseudo-second order. When sorption of arsenate ions from very diluted solution (50 µg dm-3) occurs, the composites show higher distribution coefficients comparing with the pristine resin.

Color change of CAD-CAM materials and composite resin cements after thermocycling.

PubMed

Gürdal, Isil; Atay, Ayse; Eichberger, Marlis; Cal, Ebru; Üsümez, Aslihan; Stawarczyk, Bogna

2018-04-24

The color of resin cements and computer-aided-design and computer-aided-manufacturing (CAD-CAM) restorations may change with aging. The purpose of this in vitro study was to analyze the influence of thermocycling on the color of CAD-CAM materials with underlying resin cement. Seven different CAD-CAM materials, composite resins and glass-ceramics were cut into 0.7-mm and 1.2-mm thicknesses (n=10) and cemented with a dual-polymerizing resin cement, a light-polymerizing resin cement, and a preheated composite resin (N=420). Color values were measured by using spectrophotometry. Specimens were subjected to thermocycling (5°C and 55°C; 5000 cycles). The measured color difference (ΔE) data were analyzed by using descriptive statistics. Normality of data distribution was tested by using the Kolmogorov-Smirnov test. Three-way and 1-way ANOVA followed by the Scheffé post-hoc test and unpaired 2-sample Student t test were computed to determine the significant differences among the tested parameters (α=.05). ΔE values were significantly influenced by the CAD-CAM material (η p 2 =0.85, P<.001) and the resin composite cement (η P 2 =0.03, P=.003) but were not influenced by thickness (P=.179). Significant interactions were present among thickness, cement, and CAD-CAM materials (P<.001). Vita Suprinity and GC Cerasmart showed significantly the lowest ΔE values (P<.001). The highest ΔE values were observed for IPS Empress CAD. The dual-polymerizing resin cement showed significantly lower ΔE values than the preheated composite resin (P=.003). Restoration materials and composite resin cement types used for cementation influence the amount of color change due to aging. Copyright © 2018 Editorial Council for the Journal of Prosthetic Dentistry. Published by Elsevier Inc. All rights reserved.

Incombustible resin composition

NASA Technical Reports Server (NTRS)

Akima, T.

1982-01-01

Incombustible resin compositions composed of aromatic compounds were obtained through (1) combustion polymer material and (2) bisphenol A or halogenated bisphenol A and bisphenol A diglycidl ether or halogenated bisphenol A diglycidyl ether. The aromatic compound is an adduct of bifunctional phenols and bifunctional epoxy resins.

Standard test evaluation of graphite fiber/resin matrix composite materials for improved toughness

NASA Technical Reports Server (NTRS)

Chapman, Andrew J.

1984-01-01

Programs sponsored by NASA with the commercial transport manufacturers to develop a technology data base are required to design and build composite wing and fuselage structures. To realize the full potential of composite structures in these strength critical designs, material systems having improved ductility and interlaminar toughness are being sought. To promote systematic evaluation of new materials, NASA and the commercial transport manufacturers have selected and standardized a set of five common tests. These tests evaluate open hole tension and compression performance, compression performance after impact at an energy level of 20 ft-lb, and resistance to delamination. Ten toughened resin matrix/graphite fiber composites were evaluated using this series of tests, and their performance is compared with a widely used composite system.

Effect of hybrid layer on stress distribution in a premolar tooth restored with composite or ceramic inlay: an FEM study.

PubMed

Belli, Sema; Eskitaşcioglu, Gürcan; Eraslan, Oguz; Senawongse, Pisol; Tagami, Junji

2005-08-01

The aim of this finite elemental stress analysis study was to evaluate the effect of hybrid layer on distribution and amount of stress formed under occlusal loading in a premolar tooth restored with composite or ceramic inlay. The mandibular premolar tooth was selected as the model based on the anatomical measurements suggested by Wheeler. The analysis is performed by using a Pentium II IBM compatible computer with the SAP 2000 structural analysis program. Four different mathematical models including the following structures were evaluated: 1) composite inlay, adhesive resin, and tooth structure; 2) composite inlay, adhesive resin, hybrid layer, and tooth structure; 3) ceramic inlay, adhesive resin, and tooth structure; 4) ceramic inlay, adhesive resin, hybrid layer, and tooth structure. Loading was applied from the occlusal surface of the restoration, and shear stresses under loading were evaluated. The findings were drawn by the Saplot program, and the results were analyzed by graphical comparison method. The output indicated that the hybrid layer acts as a stress absorber in models 2 and 4. The hybrid layer has also changed mathematical values of stress on cavity floors in both restoration types. Ceramic inlay collected the stress inside the body of the material, but the composite inlay directly transferred the stress through dental tissues. As a result, it was concluded that the hybrid layer has an effect on stress distribution under loading in a premolar tooth model restored with composite or ceramic inlay. Copyright 2005 Wiley Periodicals, Inc.

Comparison of microleakage in Class II cavities restored with silorane-based and methacrylate-based composite resins using different restorative techniques over time.

PubMed

Khosravi, Kazem; Mousavinasab, Seyed-Mostafa; Samani, Mahsa Sahraneshin

2015-01-01

Despite the growing tendency toward tooth-colored restorations in dentistry, polymerization shrinkage and subsequent marginal microleakage remains a problem. The aim of this in vitro study was to compare microleakage between silorane-based and methacrylate-based composite resins at different time intervals and with different restorative techniques. In this in vitro study, 108 sound extracted human molar teeth were used. Mesial and distal proximal class II boxes with dimensions of 1.5 mm depth and 4 mm width were prepared. The gingival margins of all cavities were 1 mm below the cement enamel junction. The teeth were randomly divided into three groups based on test materials. In the first group, the teeth were restored by a nanocomposite (Filtek Z350XT, 3MESPE) and SE Bond adhesive (Kuraray, Japan), in the second group, the teeth were restored with a silorane-based (Filtek P90, 3MESPE) and Filtek P90 Adhesive (3M ESPE, USA) and in the third group, the teeth were restored with a microhybrid posterior composite resin (Filtek P60, 3MESPE) and SE Bond adhesive (Kuraray, Japan). Half of the proximal cavities in each of these three groups were restored in two horizontal layers and the other half in four horizontal layers. After a period of aging (24-h, 3-month and 6-month) in water and then application of 500 thermal cycles, the teeth were immersed for 24-h in 0.5% fuchsin and evaluated under a stereomicroscope at ×36 magnification to evaluate leakage in gingival margin. Data was statistically analyzed using Kruskal-Wallis and Mann-Whitney U-tests. P ≤ 0.05 was considered as significant. In Z350XT statistically significant differences were observed in microleakage in comparison of 24-h and 6-month intervals (P = 0.01) that was higher in 6-month. Comparison of microleakage in P90 and P60 composite resins was also statistically significant and was less in P90. Microleakage was not significantly different between P90 and Z350XT at 24-h. However, this difference was significant at 3-month and 6-month intervals. Differences in microleakage of P60 and Z-350XT composite resins were not statistically significant in all intervals (P = 0.38). P90 showed the lowest microleakage during storage in water. Z350XT had microleakage similar to P90 within 24-h, but after 6-month of storage in water, it showed the highest microleakage among all the groups. The number of layers (2 layers vs. 4 layers) did not result in any differences in microleakage scores of the composite resins (P = 0.42). Water storage times did not result in any significant effect on microleakage of P90 and P60.

Bisimide amine cured epoxy /IME/ resins and composites. II - Ten-degree off-axis tensile and shear properties of Celion 6000/IME composites

NASA Technical Reports Server (NTRS)

Scola, D. A.

1982-01-01

Bisimide amines (BIAs), which are presently used as curing agents in a state-of-the-art epoxy resin, are oligomeric and polymeric mixtures. A series of composites consisting of the novel BIA-cured epoxy resin reinforced with Celion 6000 graphite fibers were fabricated and evaluated, and the ten-degree, off-axis uniaxial tensile and shear properties of these composites were determined. The use of the intralaminar shear strain-to-failure was used in the calculation of resin shear strain-to-failure. Study results indicate that several of these novel composite systems exhibit shear strain properties that are superior to those of the control composite system of the present experiments, which employed a sulfone curing agent.

Resin selection criteria for tough composite structures

NASA Technical Reports Server (NTRS)

Chamis, C. C.; Smith, G. T.

1983-01-01

Resin selection criteria are derived using a structured methodology consisting of an upward integrated mechanistic theory and its inverse (top-down structured theory). These criteria are expressed in a "criteria selection space" which are used to identify resin bulk properties for improved composite "toughness". The resin selection criteria correlate with a variety of experimental data including laminate strength, elevated temperature effects and impact resistance.

Evaluation of esthetic parameters of resin-modified glass-ionomer materials and a polyacid-modified resin composite in Class V cervical lesions.

PubMed

Gladys, S; Van Meerbeek, B; Lambrechts, P; Vanherle, G

1999-09-01

The purpose of this study was to compare the esthetics of 3 resin-modified glass-ionomer materials and 1 polyacid-modified resin composite to the esthetics of a conventional glass-ionomer control material. One hundred eighty-seven Class V cervical restorations were observed clinically over 18 months. The esthetic index system that was used evaluated color match, translucency or opacity, and surface roughness. The tested materials behaved very dissimilarly and inconsistently. In general, the esthetic results of the resin-modified glass-ionomer materials and the polyacid-modified resin composite were far from optimal. The esthetic appearance of restorations seriously deteriorated during clinical service, mainly because of discoloration of margins, changes in translucency and opacity, and rapidly appearing roughness or dullness on the surface. Both the resin-modified glass-ionomer materials and the polyacid-modified resin composite evaluated in this study performed better esthetically than did the conventional glass-ionomer material. Indications for these combination materials are limited to areas where esthetics is not a primary concern but where their ease of application may guarantee a more durable functional result.

Nanomechanical properties of biochemically modified dentin bonded interfaces

PubMed Central

dos Santos, Paulo H; Karol, Sachin; Bedran-Russo, Ana Karina B

2014-01-01

Summary The effect of biomodification of dentin matrices using collagen cross-linkers, glutaraldehyde (GD) and grape seed extract (GSE), on the reduced modulus of elasticity (Er) and nanohardness (H) of the hybrid layer and underlying dentin was investigated at the dentin-resin bonded interface. The coronal dentin of nine molars were exposed and divided into groups: 5% GD, 6.5% GSE and control. Control samples were etched, bonded with Adper Single Bond Plus and Premise composite. GD and GSE were applied for 1 hour prior to bonding procedures. After 24 hours, samples were sectioned, and resin-dentin beams were either kept in distilled water or exposed to collagenase treatment for 24 hours. Nano-indentations were performed at the hybrid layer and underlying dentin. GD and GSE treatment increased the Er and H of resin-dentin interface structures when compared to the control group (p < 0.05), particularly the hybrid layer, and may be a promising novel approach to strengthen the dentin-resin bonded interface structures when using these adhesive system and resin-based composite. PMID:21058972

Analytical prediction of moisture absorption/desorption in resin matrix composites exposed to aircraft environments

NASA Technical Reports Server (NTRS)

Unnam, J.; Tenney, D. R.

1977-01-01

The moisture absorption/desorption behavior of resin matrix composites was mathematically modeled by classical diffusion theory using an effective diffusion coefficient. Good agreement was found between calculated moisture content and published data for T300/5208 graphite fiber reinforced epoxy matrix composite. Weather Bureau data for Langley Air Force Base and Norfolk, Va., were used to calculate the amount of moisture a T300/5208 composite panel would contain if exposed outdoors. Results obtained by using average monthly weather data for several high aircraft usage locations around the world suggest that, except for desert areas, geographical locations should have only minimal effect on the moisture absorption level reached in composites. Solar radiation data together with cloud and wind information were included in the analysis to estimate an effective temperature of the composite panel during ground exposure.

Composite Materials

NASA Technical Reports Server (NTRS)

1988-01-01

Langley Research Center researchers invented an advanced polymer, a chemical compound formed by uniting many small molecules to create a complex molecule with different chemical properties. The material is a thermoplastic polyimide that resists solvents. Other polymers of this generic type are soluble in solvents, thus cannot be used where solvents are present. High Technology Services (HTS), Inc. licensed technology and is engaged in development and manufacture of high performance plastics, resins and composite materials. Techimer Materials Division is using technology for composite matrix resins that offer heat resistance and protection from radiation, electrical and chemical degradation. Applications of new polymer include molding resins, adhesives and matrix resins for fiber reinforced composites.

Burning characteristics and fiber retention of graphite/resin matrix composites

NASA Technical Reports Server (NTRS)

Bowles, K. J.

1980-01-01

Graphite fiber reinforced resin matrix composites were subjected to controlled burning conditions to determine their burning characteristics and fiber retention properties. Small samples were burned with a natural gas fired torch to study the effects of fiber orientation and structural flaws such as holes and slits that were machined into the laminates. Larger laminate samples were burned in a modified heat release rate calorimeter. Unidirectional epoxy/graphite and polyimide/graphite composites and boron powder filled samples of each of the two composite systems were burn tested. The composites were exposed to a thermal radiation of 5.3 Btu/sq ft-sec in air. Samples of each of the unfilled composite were decomposed anaerobically in the calorimeter. Weight loss data were recorded for burning and decomposition times up to thirty-five minutes. The effects of fiber orientation, flaws, and boron filler additives to the resins were evaluated. A high char forming polyimide resin was no more effective in retaining graphite fibers than a low char forming epoxy resin when burned in air. Boron powder additions to both the polyimide and the epoxy resins stabilized the chars and effectively controlled the fiber release.

Effect of disaccharide, gamma radiation and temperature on the physico-mechanical properties of jute fabrics reinforced unsaturated polyester resin-based composite

NASA Astrophysics Data System (ADS)

Sahadat Hossain, Md.; Chowdhury, A. M. Sarwaruddin; Khan, Ruhul A.

2017-06-01

The jute fabrics reinforced unsaturated polyester resin (jute/UPR)-based composites were prepared successfully by the hand-lay-up technique. The percentage of jute fabrics was kept constant at 40% fiber (by weight). The disaccharide percentage was also kept constant at 2% (by weight), but at this percentage the mechanical properties were lower than the untreated composites. Gamma radiation dose was varied at 0, 2.5, 5 and 7.5 kGy for jute/UPR-based composites. At 5.0 kGy gamma dose highest TS, TM and Eb were obtained. The jute/UPR-based composites were treated under 30°C, 50°C and -18°C for the measurement of mechanical properties. At low temperature (-18°C), the highest mechanical properties were observed. The water uptake properties were measured for disaccharide-treated and disaccharide-untreated composites up to 10 days, but no water was absorbed by the composites. The soil degradation test was carried out under 12 inch soil containing at least 25% water, but no significant decrease was observed for untreated and sucrose-treated composites. For the functional group analysis, FT-IR was carried out. For the fiber matrix adhesion analysis, the scanning electron microscopic image was taken.

Preparation and properties studies of UV-curable silicone modified epoxy resin composite system.

PubMed

Yu, Zhouhui; Cui, Aiyong; Zhao, Peizhong; Wei, Huakai; Hu, Fangyou

2018-01-01

Modified epoxy suitable for ultraviolet (UV) curing is prepared by using organic silicon toughening. The curing kinetics of the composite are studied by dielectric analysis (DEA), and the two-phase compatibility of the composite is studied by scanning electron microscopy (SEM). The tensile properties, heat resistance, and humidity resistance of the cured product are explored by changing the composition ratio of the silicone and the epoxy resin. SEM of silicone/epoxy resin shows that the degree of cross-linking of the composites decreases with an increase of silicone resin content. Differential thermal analysis indicates that the glass transition temperature and the thermal stability of the composites decrease gradually with an increase of silicone resin content. The thermal degradation rate in the high temperature region, however, first decreases and then increases. In general, after adding just 10%-15% of the silicone resin and exposing to light for 15 min, the composite can still achieve a better curing effect. Under such conditions, the heat resistance of the cured product decreases a little. The tensile strength is kept constant so that elongation at breakage is apparently improved. The change rate after immersion in distilled water at 60°C for seven days is small, which shows excellent humidity resistance.

Conjugation of diisocyanate side chains to dimethacrylate reduces polymerization shrinkage and increases the hardness of composite resins.

PubMed

Jan, Yih-Dean; Lee, Bor-Shiunn; Lin, Chun-Pin; Tseng, Wan-Yu

2014-04-01

Polymerization shrinkage is one of the main causes of dental restoration failure. This study tried to conjugate two diisocyanate side chains to dimethacrylate resins in order to reduce polymerization shrinkage and increase the hardness of composite resins. Diisocyanate, 2-hydroxyethyl methacrylate, and bisphenol A dimethacrylate were reacted in different ratios to form urethane-modified new resin matrices, and then mixed with 50 wt.% silica fillers. The viscosities of matrices, polymerization shrinkage, surface hardness, and degrees of conversion of experimental composite resins were then evaluated and compared with a non-modified control group. The viscosities of resin matrices increased with increasing diisocyanate side chain density. Polymerization shrinkage and degree of conversion, however, decreased with increasing diisocyanate side chain density. The surface hardness of all diisocyanate-modified groups was equal to or significantly higher than that of the control group. Conjugation of diisocyanate side chains to dimethacrylate represents an effective means of reducing polymerization shrinkage and increasing the surface hardness of dental composite resins. Copyright © 2012. Published by Elsevier B.V.

Urea-formaldehyde resins: production, application, and testing

NASA Astrophysics Data System (ADS)

Nuryawan, A.; Risnasari, I.; Sucipto, T.; Heri Iswanto, A.; Rosmala Dewi, R.

2017-07-01

Urea-formaldehyde (UF) resin, one of the most important formaldehyde resin adhesives, is a polymeric condensation product of formaldehyde with urea, and being widely used for the manufacture of wood-based composite panels, such as plywood, particleboard, and fiberboard. In spite of its benefits such as fast curing, good performance in the panels (colorless), and lower cost; formaldehyde emission (FE) originated from either UF resin itself or composite products bonded by UF resins is considered a critical drawback as it affects human health particularly in indoor environment. In order to reduce the FE, lowering formaldehyde/urea (F/U) mole ratio in the synthesis of the UF resin was done. In this study, synthesis of UF resins was carried out following the conventional alkaline-acid two-step reaction with a second addition of urea, resulting in F/U mole ratio around 1.0, namely 0.95; 1.05, and 1.15. The UF resins produced were used as binder for particleboard making. The board was manufactured in the laboratory using shaving type particle of Gmelina wood, 8% UF resin based on oven dry particle, and 1% NH4Cl (20%wt) as hardener for the resin. The target of the thickness was 10 mm and the dimension was 25 cm x 25 cm. The resulted particleboard then was evaluated the physical and the mechanical properties by Japanese Industrial Standard (JIS) A 5908 (2003). Further, the resulted particleboard also was used for the mice cage’s wall in order to mimic the real living environment. After four weeks exposure in the cages, the mice then were evaluated their mucous organs as well as their blood. The experiment results were as follows: 1) It was possible to synthesis UF resins with low F/U mole ratio; 2) However, the particleboard bonded UF resins with low F/U mole ratio showed poor properties, particularly on the thickness swelling and modulus of elasticity; 3) There was no significant differences among the mucous organs of the mice after a month exposure FE originated from cages wall using histopathology assessment.

Fingerprint test data report: FM 5064J (Kaiser) lots No. 1 (K) - No. 4 (K). [resin matrix composites

NASA Technical Reports Server (NTRS)

1986-01-01

Quality control tests are presented for resin matrix and carbon-carbon composites. Tests performed are filler test, resin test, prepregs test, and fabric test. The test results are presented in chart form.

Effect of sulfuric acid etching of polyetheretherketone on the shear bond strength to resin cements.

PubMed

Sproesser, Oliver; Schmidlin, Patrick R; Uhrenbacher, Julia; Roos, Malgorzata; Gernet, Wolfgang; Stawarczyk, Bogna

2014-10-01

To examine the influence of etching duration on the bond strength of PEEK substrate in combination with different resin composite cements. In total, 448 PEEK specimens were fabricated, etched with sulfuric acid for 5, 15, 30, 60, 90, 120, and 300 s and then luted with two conventional resin cements (RelyX ARC and Variolink II) and one self-adhesive resin cement (Clearfil SA Cement) (n = 18/subgroup). Non-etched specimens served as the control group. Specimens were stored in distilled water for 28 days at 37°C and shear bond strengths were measured. Data were analyzed nonparametrically using Kruskal-Wallis-H (p < 0.05). Non-etched PEEK demonstrated no bond strength to resin composite cements. The optimal etching duration varied with the type of resin composite: 60 s for RelyX ARC (15.3 ± 7.2 MPa), 90 s for Variolink II (15.2 ± 7.2 MPa), and 120 s for Clearfil SA Cement (6.4 ± 5.9 MPa). Regardless of etching duration, however, the self-etching resin composite cement showed significantly lower shear bond strength values when compared to groups luted with the conventional resin composites. Although sulfuric acid seems to be suitable and effective for PEEK surface pre-treatment, further investigations are required to examine the effect of other adhesive systems and cements.

Rheologic properties of flowable, conventional hybrid, and condensable composite resins.

PubMed

Lee, In-Bog; Son, Ho-Hyun; Um, Chung-Moon

2003-06-01

This research was undertaken to investigate the viscoelastic properties related to handling characteristics of five commercial flowable, two conventional hybrid and two condensable composite resins and to investigate the effect on the viscosity of filler volume fraction of composites. A dynamic oscillatory shear test was used to evaluate the storage shear modulus (G'), loss shear modulus (G"), loss tangent (tan delta) and complex viscosity (eta(*)) of the composite resins as a function of frequency (omega)-dynamic frequency sweep test from 0.01 to 100 rad/s at 25 degrees C-using an Advanced Rheometric Expansion System. To investigate the effect on the viscosity of the composites of the filler volume fraction, the filler weight% and filler volume% were measured by the Archimedes' principle using a pyknometer. The complex viscosity eta(*) of flowable composites was lower than that of the hybrid composites and significant differences were observed between brands. The complex viscosity eta(*) of condensable composites was higher than that of hybrid composites. The order of complex viscosity eta(*) at omega=10 rad/s in order of decreasing viscosity was as follows, Synergy compact, P-60, Z-250, Z-100, Aeliteflo, Tetric flow, Compoglass flow, Flow it and Revolution. The complex viscosity of flowable composites, normalized with respect to Z-100, was 0.04-0.56 but Synergy compact was 2.158 times higher than that of Z-100. The patterns of the change of loss tangent (tan delta) of the composite resins with increasing frequency were significantly different between brands. Phase angles delta ranged from 30.9 to 78.1 degrees at omega=10 rad/s. All composite resins exhibit pseudoplastic behavior with increasing shear rate. The relationships between the complex shear modulus G(*), the phase angle delta, and the shear rate omega were represented by the frequency domain phasor form, G(*)(omega)=G(*)e(i delta)=G(*) 90 degree angle delta. Only a weak relationship was found between filler volume% and the viscosity of the composite resins. This investigation shows that the viscoelasticity of composites in the same class is significantly different between brands. This rheologic property of composite resins influences the handling characteristics of the materials. The locus of frequency domain phasor plots in a complex plane is a valuable method of representing the viscoelastic properties of composite resins.

Repair of bis-acryl provisional restorations using flowable composite resin.

PubMed

Bohnenkamp, David M; Garcia, Lily T

2004-11-01

Provisional restorations provide interim coverage for prepared teeth while fixed definitive restorations are fabricated. Several types of autopolymerizing acrylic resins have been used for many years to fabricate provisional restorations. In recent years, bis-acryl resin composite material has gained popularity among clinicians for the direct fabrication of provisional fixed restorations. Occasionally, deficiencies may occur while fabricating a direct provisional restoration and require chairside repair. This article describes an effective procedure for the use of light-polymerized flowable composite resin for the intraoral repair of bis-acryl provisional restorations.

The effects of aircraft fuel and fluids on the strength properties of Resin Transfer Molded (RTM) composites

NASA Technical Reports Server (NTRS)

Falcone, Anthony; Dow, Marvin B.

1993-01-01

The resin transfer molding (RTM) process offers important advantages for cost-effective composites manufacturing, and consequently has become the subject of intense research and development efforts. Several new matrix resins have been formulated specifically for RTM applications in aircraft and aerospace vehicles. For successful use on aircraft, composite materials must withstand exposure to the fluids in common use. The present study was conducted to obtain comparative screening data on several state-ofthe-art RTM resins after environmental exposures were performed on RTM composite specimens. Four graphite/epoxy composites and one graphite/bismaleimide composite were tested; testing of two additional graphite epoxy composites is in progress. Zero-deg tension tests were conducted on specimens machined from eight-ply (+45-deg, -45-deg) laminates, and interlaminar shear tests were conducted on 32-ply 0-deg laminate specimens. In these tests, the various RTM resins demonstrated widely different strengths, with 3501-6 epoxy being the strongest. As expected, all of the matrix resins suffered severe strength degradation from exposure to methylene chloride (paint stripper). The 3501-6 epoxy composites exhibited about a 30 percent drop in tensile strength in hot, wet tests. The E905-L epoxy exhibited little loss of tensile strength (less than 8 percent) after exposure to water. The CET-2 and 862 epoxies as well as the bismaleimide exhibited reduced strengths at elevated temperature after exposure to oils and fuel. In terms of the percentage strength reductions, all of the RTM matrix resins compared favorably with 3501-6 epoxy.

Improved high-temperature resistant matrix resins

NASA Technical Reports Server (NTRS)

Green, H. E.; Chang, G. E.; Wright, W. F.; Ueda, K.; Orell, M. K.

1989-01-01

A study was performed with the objective of developing matrix resins that exhibit improved thermo-oxidative stability over state-of-the-art high temperature resins for use at temperatures up to 644 K (700 F) and air pressures up to 0.7 MPa (100 psia). The work was based upon a TRW discovered family of polyimides currently licensed to and marketed by Ethyl Corporation as EYMYD(R) resins. The approach investigated to provide improved thermo-oxidative properties was to use halogenated derivatives of the diamine, 2, 2-bis (4-(4-aminophenoxy)phenyl) hexafluoropropane (4-BDAF). Polyimide neat resins and Celion(R) 12,000 composites prepared from fluorine substituted 4-BDAF demonstrated unexpectedly lower glass transition temperatures (Tg) and thermo-oxidative stabilities than the baseline 4-BDAF/PMDA polymer.

Electromagnetic, morphological and structural characterization of microwave absorbers based on POMA/magnetic filament composites

NASA Astrophysics Data System (ADS)

de Souza Pinto, Simone; Machado, João Paulo Barros; Gomes, Newton A. S.; Rezende, Mirabel Cerqueira

2018-03-01

This study aims to combine dielectric and magnetic properties of different materials in an unique composite. For this, poly(o-methoxyaniline), POMA, was chemically synthesized in situ on magnetic metallic filaments (MF). The obtained composite was inserted into an epoxy resin matrix in the proportions of 40, 50 and 70%, in weight (wt%). The samples were characterized by scanning electron microscopy (SEM), X ray diffraction (XRD) and electromagnetic measurements. On the last case, the measurements considered the reflectivity and the complex parameters of electrical permittivity and magnetic permeability in the frequency range of 8.2-12.4 GHz (X-band). Specimens with different thicknesses were evaluated by reflectivity. XRD results show that the filaments are based on Fe-α steel and SEM analyses show the good incorporation of POMA/MF in the epoxy resin composite. The complex parameters show that the real component of permittivity shows the largest variation with the POMA/MF concentration increasing in epoxy resin and the loss tangent indicates that the magnetic losses are preponderant on dielectric ones. The reflectivity measurements show that the 5 mm-specimen with 50 wt% of POMA/MF presents the best result of attenuation (-21.5 dB, i.e. above 99% of attenuation). Already, the sample containing 70 wt% shows the worst performance (up to -9.0 dB). The increase of POMA/MF concentration in epoxy resin confers maximum attenuation values for less thick specimens. The results show that the combination of dielectric and magnetic materials in a composite contributes for the improvement of microwave absorbing performance, and extends the possibilities of RAM processing with different characteristics.

Monitoring cure of composite resins using frequency dependent electromagnetic sensing techniques

NASA Technical Reports Server (NTRS)

Kranbuehl, D. E.; Hoff, M. S.; Loos, A. C.; Freeman, W. T., Jr.; Eichinger, D. A.

1988-01-01

A nondestructive in situ measurement technique has been developed for monitoring and measuring the cure processing properties of composite resins. Frequency dependent electromagnetic sensors (FDEMS) were used to directly measure resin viscosity during cure. The effects of the cure cycle and resin aging on the viscosity during cure were investigated using the sensor. Viscosity measurements obtained using the sensor are compared with the viscosities calculated by the Loos-Springer cure process model. Good overall agreement was obtained except for the aged resin samples.

Interfacial Structure and Properties of Wood/Polypropylene Composites

Treesearch

Timothy G. Rials; Michael P. Wolcott; Suzhow Yin

2000-01-01

Composite wood products have traditionally relied on thermosetting polymers like phenol-formaldehyde and urea-formaldehyde resins as binders. The continuing need to effectively utilize lignocellulosic fiber from low-quality hardwoods and from recycling streams has prompted consideration of new composites based on thermoplastic polymers [1,2]. Much of the development...

Correlation between three-dimentional surface topography and color stability of different nanofilled composites.

PubMed

Öztürk, Elif; Güder, Gizem

2015-01-01

The aim of this study was to evaluate the 3-dimensional (3D) surface topography and color stability of four different resin composites after immersion in different soft-beverages. One hundred sixty disk-shaped specimens (diameter: 10 mm, and thickness: 2 mm) were made from four different resin composites (i.e., Filtek Z550, Tetric N-Ceram, Clearfil Majesty Esthetic, and Cavex Quadrant Universal LC). Each specimen was cured under mylar strips for 20 sec for both top and bottom surfaces. All of the specimens were stored in distilled water for 24 h at 37°C. Surface measurements were carried out using a noncontact 3D-optical-profilometer in terms of surface topography (Ra values). Color measurements of each specimen were performed with Vita Easy Shade system. All the measurements were performed at baseline and after 30 days of immersion in the selected soft-beverages (Redbull, Coca-Cola and Dimes-Lemonade). Control groups were stored in distilled water during the study. Ra values and color changes (ΔE values) of the groups were recorded. The data were statistically analyzed using a one way ANOVA and Tukey's post-hoc tests (SPSS 18.0). The tested soft-beverages in the present study caused color changes at a 30-day evaluation period for the tested resin composites (p < 0.05). However, 3D surface topography of resin composites was not influenced by the tested soft-beverages (p > 0.05). There was no significant interaction between the composite and beverage type on the Ra values of the resin composites (p > 0.05). No correlation was found between color stability and 3D surface topography of the resin composites. Color stability of resin composites may be affected by soft beverages. © Wiley Periodicals, Inc.

Effect of dentin dehydration and composite resin polymerization mode on bond strength of two self-etch adhesives.

PubMed

Samimi, Pooran; Alizadeh, Mehdi; Shirban, Farinaz; Davoodi, Amin; Khoroushi, Maryam

2016-01-01

Dual-cured composite resins are similar to self-cured composite resins in some of their clinical applications due to inadequate irradiation, lack of irradiation, or delayed irradiation. Therefore, incompatibility with self-etch adhesives (SEAs) should be taken into account with their use. On the other, the extent of dentin dehydration has a great role in the quality of adhesion of these resin materials to dentin. The aim of this study was to investigate the effect of dentin dehydration and composite resin polymerization mode on bond strength of two SEAs. A total of 120 dentinal specimens were prepared from extracted intact third molars. Half of the samples were dehydrated in ethanol with increasing concentrations. Then Clearfil SE Bond (CSEB) and Prompt L-Pop (PLP) adhesives were applied in the two groups. Cylindrical composite resin specimens were cured using three polymerization modes: (1) Immediate light-curing, (2) delayed light-curing after 20 min, and (3) self-curing. Bond strength was measured using universal testing machine at a crosshead speed of 1 mm/min. Data were analyzed with two-way ANOVA and Duncan post hoc tests. Statistical significance was defined at P < 0.05. There were no significant differences for CSEB subgroups with hydrated and dehydrated dentin samples between the three different curing modes (P > 0.05). PLP showed significant differences between subgroups with the lowest bond strength in hydrated dentin with delayed light-curing and self-cured mode of polymerization. Within the limitations of this study, a delay in composite resin light-curing or using chemically cured composite resin had a deleterious effect on dentin bond strength of single-step SEAs used in the study.

Effect of dentin dehydration and composite resin polymerization mode on bond strength of two self-etch adhesives

PubMed Central

Samimi, Pooran; Alizadeh, Mehdi; Shirban, Farinaz; Davoodi, Amin; Khoroushi, Maryam

2016-01-01

Background: Dual-cured composite resins are similar to self-cured composite resins in some of their clinical applications due to inadequate irradiation, lack of irradiation, or delayed irradiation. Therefore, incompatibility with self-etch adhesives (SEAs) should be taken into account with their use. On the other, the extent of dentin dehydration has a great role in the quality of adhesion of these resin materials to dentin. The aim of this study was to investigate the effect of dentin dehydration and composite resin polymerization mode on bond strength of two SEAs. Materials and Methods: A total of 120 dentinal specimens were prepared from extracted intact third molars. Half of the samples were dehydrated in ethanol with increasing concentrations. Then Clearfil SE Bond (CSEB) and Prompt L-Pop (PLP) adhesives were applied in the two groups. Cylindrical composite resin specimens were cured using three polymerization modes: (1) Immediate light-curing, (2) delayed light-curing after 20 min, and (3) self-curing. Bond strength was measured using universal testing machine at a crosshead speed of 1 mm/min. Data were analyzed with two-way ANOVA and Duncan post hoc tests. Statistical significance was defined at P < 0.05. Results: There were no significant differences for CSEB subgroups with hydrated and dehydrated dentin samples between the three different curing modes (P > 0.05). PLP showed significant differences between subgroups with the lowest bond strength in hydrated dentin with delayed light-curing and self-cured mode of polymerization. Conclusion: Within the limitations of this study, a delay in composite resin light-curing or using chemically cured composite resin had a deleterious effect on dentin bond strength of single-step SEAs used in the study. PMID:27041894

[Aging of silorane- and methacrylate-based composite resins: effects on color and translucency].

PubMed

Liu, Chang; Pan, Jie; Lin, Hong; Shen, Song

2015-10-01

To evaluate the color stability and translucency of silorane-based low shrinkage composite after in vitro aging procedures of thermal cycling and water storage respectively, and to compare with those of conventional methacrylate-based posterior composite. Three light-cured composite resins, dimethacrylate-based composite A (Filtek™ Z350), B (Filtek™ P60) and silorane-based composite C (Filtek™ P90), were tested in this study. Ten specimens (10 mm in diameter, 1 mm in height) of each composite were prepared. The ten specimens in each group were then divided into two subgroups (n = 5). One subgroup underwent thermal cycling [(5.0 ± 0.5)~(55.0 ± 1.0) °C, 10 000 cycles] and the other was stored in 37 C° distilled water for 180 days. With a spectrophotometer, the CIE L * a * b * parameters of the specimens were tested before and after artificial aging against white, medium grey and black backgrounds, respectively. △E, TP and △TP were calculated and data were analyzed using independent-samples t test and partial analysis (P < 0.05). With regard to color stability, silorane-based composite showed color alteration above the clinically acceptable levels (△E > 3.3), and also showed higher △E with a statistically significant difference in comparison with the other composites (B and C) (P < 0.05) after artificial aging. With regard to translucency, composite C showed more alteration compared with composite B (P < 0.05) after thermal cycling. It may be concluded that the silorane-based composite underwent greater alteration with regard to color stability and translucency.

Rubber dam isolation--key to success in diastema closure technique with direct composite resin.

PubMed

Barros de Campos, Paulo Ricardo; Maia, Rodrigo Rocha; Rodrigues de Menezes, Livia; Barbosa, Isabel Ferreira; Carneiro da Cunha, Amanda; da Silveira Pereira, Gisele Damiana

2015-01-01

The use of direct composite resin for diastema closure has technique advantages, including that the restorative procedure can be carried out in one appointment at a reasonable cost and without the removal of sound tooth structure. The use of a rubber dam for closing diastemas with composite resin is of paramount importance as it prevents moisture contamination and ensures increased gingival retraction compared to other techniques. This provides better access to the cervical area of the tooth, facilitating proper placement of resin to recreate the natural anatomical contours and contact point. Thus, there is a more natural adaptation of the restoration to the gingival tissue, avoiding a space between the papilla and the restored tooth. To illustrate the advantages of this technique, two diastema closure cases are presented using direct composite resin with rubber dam isolation.

Burning characteristics and fiber retention of graphite/resin matrix composites

NASA Technical Reports Server (NTRS)

Bowles, K. J.

1980-01-01

Graphite fiber reinforced resin matrix composites were subjected to controlled burning conditions to determine their burning characteristics and fiber retention properties. Two types of burning equipment were used. Small samples were burned with a natural gas fired torch to study the effects of fiber orientation and structural flaws such as holes and slits that were machined into the laminates. Larger laminate samples were burned in a Heat Release Rate Calorimeter. Unidirectional epoxy/graphite and polyimide/graphite composites and boron powder filled samples of each of the two composite systems were burn tested and exposed to a thermal radiation. The effects of fiber orientation, flaws, and boron filler additives to the resins were evaluated. A high char forming polyimide resin was no more effective in retaining graphite fibers than a low char forming epoxy resin when burning in air.

Method and solvent composition for regenerating an ion exchange resin

DOEpatents

Even, William R.; Irvin, David J.; Irvin, Jennifer A.; Tarver, Edward E.; Brown, Gilbert M.; Wang, James C. F.

2002-01-01

A method and composition for removing perchlorate from a highly selective ion exchange resin is disclosed. The disclosed approach comprises treating the resin in a solution of super critical or liquid carbon dioxide and one or more quaternary ammonium chloride surfactant compounds.

Evaluation of degree of conversion and the effect of thermal aging on the color stability of resin cements and flowable composite.

PubMed

Prieto, Lúcia Trazzi; Pimenta de Araújo, Cíntia Tereza; Araujo Pierote, Josué Junior; Salles de Oliveira, Dayane Carvalho Ramos; Coppini, Erick Kamiya; Sartini Paulillo, Luís Alexandre Maffei

2018-01-01

The aim of this in vitro study was to evaluate the color stability and degree of conversion (DC) of dual-cure and light-cure cements and flowable composites after thermal aging. A total of 50 human incisors were prepared and divided into six groups ( n = 10). Veneers were fabricated using IPS Empress Direct composite resin were bonded with three types of luting agents: Light-cured, conventional dual, and flowable composite according to the manufacturer's instructions. The groups were as follows: Filtek Z350XT Flow/Single Bond 2, RelyX ARC/Single Bond 2, RelyX Veneer/Single Bond 2, Tetric N-Flow/Tetric N-Bond, and Variolink II/Tetric N-Bond. Commission Internationale de l'Éclairage L*, a* and b* color coordinates were measured 24 h after cementation procedure with a color spectrophotometer and reevaluated after 10,000 thermal cycles. To evaluate the DC 50 specimens ( n = 10) of each resin material were obtained and Fourier transform infrared spectroscopy was used to evaluate the absorption spectra. Statistical analysis was performed with one-way ANOVA and Tukey's test (α = 0.05). No statistically significant differences in ΔE* occurred after aging. The greatest change in lightness occurred in the Variolink II resin cement. Changes in red-green hue were very small for the same cement and largest in the Tetric N-Flow flowable resin composite, while the greatest change in blue-yellow hue was a yellowing of the RelyX ARC luting cement. RelyX ARC exhibited the highest DC, and there were no statistically significant differences in DC among the other cements. Resin-based luting agent might affect the final of ceramic veneer restorations. The thermal aging affected the final color of the evaluated materials, and these were regarded as clinically unacceptable (ΔE >3.3).

Effect of filler type and polishing on the discoloration of composite resin artificial teeth.

PubMed

Imamura, Soichiro; Takahashi, Hidekazu; Hayakawa, Iwao; Loyaga-Rendon, Paola G; Minakuchi, Shunsuke

2008-11-01

In this study, the effects of filler type and polishing on the discoloration of composite resin artificial teeth were examined. Four types of experimental resins were prepared: one was a matrix resin, while the others were composite resins containing three different types of fillers (nano-sized silica filler with or without silanization, and prepolymerized filler). Specimens were immersed in distilled water, coffee, red wine, or curry. Color change after immersion was measured using a colorimeter. Color difference values (delta E) and changes in translucency parameter (delta TP) were statistically analyzed using three-way ANOVA and Tukey's comparison. On the influence of the polishing factor, statistically significant differences were neither observed in delta E nor delta TP between polished and non-polished tooth surfaces. On the contrary, the influences of filler type and discoloration medium, and their interaction thereof, were significant. With unsilanized filler, the delta E value of composite resin artificial teeth was significantly increased.

RADIATION SHIELDING COMPOSITION

DOEpatents

Dunegan, H.L.

1963-01-29

A light weight radiation shielding composition is described whose mechanical and radiological properties can be varied within wide limits. The composition of this shielding material consists of four basic ingredients: powder of either Pb or W, a plastic resin, a resin plasticizer, and a polymerization catalyst to promote an interaction of the plasticizer with the plastic resin. Air may be mixed into the above ingredients in order to control the density of the final composition. For equivalent gamma attenuation, the shielding composition weighs one-third to one-half as much as conventional Pb shielding. (AEC)

Composite panels made with biofiber or office wastepaper bonded with thermoplastic and/or thermosetting resin

Treesearch

James H. Muehl; Andrzej M. Krzysik; Poo Chow

2004-01-01

The purpose of this study was to evaluate two groups of composite panels made from two types of underutilized natural fiber sources, kenaf bast fiber and office wastepaper, for their suitability in composite panels. All panels were made with 5% thermosetting phenol-formaldehyde (PF) resin and 1.5% wax. Also, an additional 10% polypropylene (PP) thermoplastic resin was...

Integrating dental anatomy and biomaterials: an innovative use of composite resin.

PubMed

Allen, Kenneth L; McAndrew, Maureen

2004-01-01

As part of the new integrated curriculum at the New York University College of Dentistry, a pilot program uses composite resins to teach dental anatomy. The Department of Biomaterials and Biomimetics, in conjunction with the Department of Cariology and Operative Dentistry, has created a teaching module to replicate the morphology of a central incisor through the manipulation and placement of a composite resin.

Self-Healing Nanofiber-Reinforced Polymer Composites. 1. Tensile Testing and Recovery of Mechanical Properties.

PubMed

Lee, Min Wook; An, Seongpil; Jo, Hong Seok; Yoon, Sam S; Yarin, Alexander L

2015-09-09

The present work aims at development of self-healing materials capable of partially restoring their mechanical properties under the conditions of prolonged periodic loading and unloading, which is characteristic, for example, of aerospace applications. Composite materials used in these and many other applications frequently reveal multiple defects stemming from their original inhomogeneity, which facilitates microcracking and delamination at ply interfaces. Self-healing nanofiber mats may effectively prevent such damage without compromising material integrity. Two types of core-shell nanofibers were simultaneously electrospun onto the same substrate in order to form a mutually entangled mat. The first type of core-shell fibers consisted of resin monomer (dimethylsiloxane) within the core and polyacrylonitrile within the shell. The second type of core-shell nanofibers consisted of cure (dimethyl-methyl hydrogen-siloxane) within the core and polyacrylonitrile within the shell. These mutually entangled nanofiber mats were used for tensile testing, and they were also encased in polydimethylsiloxane to form composites that were also subsequently subjected to tensile testing. During tensile tests, the nanofibers can be damaged in stretching up to the plastic regime of deformation. Then, the resin monomer and cure was released from the cores and the polydimethylsiloxane resin was polymerized, which might be expected to result in the self-healing properties of these materials. To reveal and evaluate the self-healing properties of the polyacrylonitrile-resin-cure nanofiber mats and their composites, the results were compared to the tensile test results of the monolithic polyacrylonitrile nanofiber mats or composites formed by encasing polyacrylonitrile nanofibers in a polydimethylsiloxane matrix. The latter do not possess self-healing properties, and indeed, do not recover their mechanical characteristics, in contrast to the polyacrylonitrile-resin-cure nanofiber mats and the composites reinforced by such mats. This is the first work, to the best of our knowledge, where self-healing nanofibers and composites based on them were developed, tested, and revealed restoration of mechanical properties (stiffness) in a 24 h rest period at room temperature.

Highly conductive, multi-layer composite precursor composition to fuel cell flow field plate or bipolar plate

DOEpatents

Jang, Bor Z [Centerville, OH; Zhamu, Aruna [Centerville, OH; Guo, Jiusheng [Centerville, OH

2011-02-15

This invention provides a moldable, multiple-layer composite composition, which is a precursor to an electrically conductive composite flow field plate or bipolar plate. In one preferred embodiment, the composition comprises a plurality of conductive sheets and a plurality of mixture layers of a curable resin and conductive fillers, wherein (A) each conductive sheet is attached to at least one resin-filler mixture layer; (B) at least one of the conductive sheets comprises flexible graphite; and (C) at least one resin-filler mixture layer comprises a thermosetting resin and conductive fillers with the fillers being present in a sufficient quantity to render the resulting flow field plate or bipolar plate electrically conductive with a conductivity no less than 100 S/cm and thickness-direction areal conductivity no less than 200 S/cm.sup.2.

Effect of a surface sealant on the color stability of composite resins after immersion in staining solution.

PubMed

Pedroso, Lauana Borges; Barreto, Luma Franciélle Cabreira; Miotti, Leonardo Lamberti; Nicoloso, Gabriel Ferreira; Durand, Leticia Brandão

2016-01-01

This study evaluated the influence of surface sealants on the color stability of 2 different composite resins after immersion in coffee. Four groups were created (n = 10): microhybrid composite, microhybrid with surface sealant, nanofilled composite, and nanofilled composite with surface sealant. Half of the specimens of each group were immersed in distilled water and half were immersed in coffee for 48 hours. Color was measured before and after immersion. Groups with surface sealants presented less color variation when compared with the groups without surface sealants. The nanofilled resin specimens presented the greatest color variation within the groups without sealant. The surface sealant positively influenced the color stability of composite resin specimens immersed in coffee. When surface sealant was not applied, the microhybrid specimens had better color stability than the nanofilled.

Mechanical behavior of bulk direct composite versus block composite and lithium disilicate indirect Class II restorations by CAD-FEM modeling.

PubMed

Ausiello, Pietro; Ciaramella, Stefano; Fabianelli, Andrea; Gloria, Antonio; Martorelli, Massimo; Lanzotti, Antonio; Watts, David C

2017-06-01

To study the influence of resin based and lithium disilicate materials on the stress and strain distributions in adhesive class II mesio-occlusal-distal (MOD) restorations using numerical finite element analysis (FEA). To investigate the materials combinations in the restored teeth during mastication and their ability to relieve stresses. One 3D model of a sound lower molar and three 3D class II MOD cavity models with 95° cavity-margin-angle shapes were modelled. Different material combinations were simulated: model A, with a 10μm thick resin bonding layer and a resin composite bulk filling material; model B, with a 70μm resin cement with an indirect CAD-CAM resin composite inlay; model C, with a 70μm thick resin cement with an indirect lithium disilicate machinable inlay. To simulate polymerization shrinkage effects in the adhesive layers and bulk fill composite, the thermal expansion approach was used. Shell elements were employed for representing the adhesive layers. 3D solid CTETRA elements with four grid points were employed for modelling the food bolus and tooth. Slide-type contact elements were used between the tooth surface and food. A vertical occlusal load of 600 N was applied, and nodal displacements on the bottom cutting surfaces were constrained in all directions. All the materials were assumed to be isotropic and elastic and a static linear analysis was performed. Displacements were different in models A, B and C. Polymerization shrinkage hardly affected model A and mastication only partially affected mechanical behavior. Shrinkage stress peaks were mainly located marginally along the enamel-restoration interface at occlusal and mesio-distal sites. However, at the internal dentinal walls, stress distributions were critical with the highest maximum stresses concentrated in the proximal boxes. In models B and C, shrinkage stress was only produced by the 70μm thick resin layer, but the magnitudes depended on the Young's modulus (E) of the inlay materials. Model B mastication behavior (with E=20GPa) was similar to the sound tooth stress relief pattern. Model B internally showed differences from the sound tooth model but reduced maximum stresses than model A and partially than model C. Model C (with E=70GPa) behaved similarly to model B with well redistributed stresses at the occlusal margins and the lateral sides with higher stress concentrations in the proximal boxes. Models B and C showed a more favorable performance than model A with elastic biomechanics similar to the sound tooth model. Bulk filling resin composite with 1% linear polymerization shrinkage negatively affected the mechanical behavior of class II MOD restored teeth. Class II MOD direct resin composite showed greater potential for damage because of higher internal and marginal stress evolution during resin polymerization shrinkage. With a large class II MOD cavity an indirect composite or a lithium disilicate inlay restoration may provide a mechanical response close to that of a sound tooth. Copyright © 2017 The Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Bisphenol A release from an orthodontic resin composite: A GC/MS and LC/MS study.

PubMed

Deviot, Marc; Lachaise, Isabelle; Högg, Christof; Durner, Jürgen; Reichl, Franz-Xaver; Attal, Jean-Pierre; Dursun, Elisabeth

2018-02-01

First, to analyse the in vitro release of BPA and Bis-GMA from an orthodontic resin composite (Transbond XT, 3M Unitek), stored in various conditions, by gas chromatography/mass spectrometry (GC/MS) and liquid chromatography/mass spectrometry (LC/MS); then to extrapolate the data to the clinical situation. Secondly, to explore the thermal stability of Bis-GMA. Cylinders of resin composite were prepared and stored according to 3 different protocols: (1) they were light-cured 20s, then placed in artificial saliva; (2) they were light-cured 2s, then placed in acetonitrile; (3) they were light-cured 2s, then placed in methanol. For each group, BPA and Bis-GMA release were determined with GC/MS and/or LC/MS at least after one week. Besides, 120 brackets (10 of each type) were bonded over metal teeth, then debonded, and the weight and the surface of resin composite residues were measured. BPA and Bis-GMA release of adhesive residues were extrapolated from the data obtained with the cylinders. Besides, BPA release from a heated Bis-GMA solution was measured. With GC/MC, BPA was detected in all samples. With LC/MS, BPA was detected only from samples immersed in MeOH; Bis-GMA was detected, in varying amount according to the extraction media and the light-curing time. BPA was found after heating of the Bis-GMA solution. Contamination risk and the heat applied in GC/MS may overestimate the BPA release from resin composite. Based on the LC/MS results, the risk of BPA release after orthodontic bonding would be more than 42000 times lower than the TDI for a 30-kg child. Copyright © 2017 The Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Determining efficacy of monitoring devices on ceramic bond to resin composite

PubMed Central

Osorio, Estrella; Aguilera, Fátima S.; Osorio, Raquel; García-Godoy, Franklin; Cabrerizo-Vilchez, Miguel A.; Toledano, Manuel

2012-01-01

Objectives: This paper aims to assess the effectiveness of 3D nanoroughness and 2D microroughness evaluations, by their correlation with contact angle measurements and shear bond strength test, in order to evaluate the effect of two different acids conditioning on the bonding efficacy of a leucite-based glass-ceramic to a composite resin. Study Design: Ceramic (IPS Empress) blocks were treated as follows: 1) no treatment, 2) 37% phosphoric acid (H3PO4), 15 s, 3) 9% hydrofluoric acid (HF), 5 min. Micro- and nano-roughness were assessed with a profilometer and by means of an atomic force microscopy (AFM). Water contact angle (CA) measurements were determined to assess wettability of the ceramic surfaces with the asixymetric drop shape analysis contact diameter technique. Shear bond strength (SBS) was tested to a resin composite (Z100) with three different adhesive systems (Scotchbond Multipurpose Plus, Clearfil New Bond, ProBOND). Scanning electron microscopy (SEM) images were performed. Results: Nanoroughness values assessed in 50x50 μm areas were higher for the HF group, these differences were not detected by profilometric analysis. HF treatment created the nano- roughest surfaces and the smallest CA (p<0.05), producing the highest SBS to the composite resin with all tested adhesive systems (p<0.05). No differences existed between the SBS produced by the adhesive systems evaluated with any of the surface treatments tested. Conclusions: Nano-roughness obtained in a 50x50 µm scan size areas was the most reliable data to evaluate the topographical changes produced by the different acid treatments on ceramic surfaces. Key words:Dental ceramic, acid etching, bonding efficacy, resin composite, adhesive systems, contact angle, roughness. PMID:22549693

Adhesive luting of indirect restorations.

PubMed

Krämer, N; Lohbauer, U; Frankenberger, R

2000-11-01

To describe the potential of adhesive luting procedures with respect to (1) material characteristics and classifications, (2) film thickness, (3) overhang control, (4) bonding to different inlay materials, (5) adhesion to tooth substrates and the problem of hypersensitivities, (6) wear of luting composites, and (7) clinical performance. A literature review of relevant studies of various in vitro and in vivo studies enables an overview of possibilities and limitations of adhesively luted indirect restorations. (1) Resin-based composites are the material of choice for adhesive luting. Both material properties and wear behavior of fine particle hybrid-type resin-based composites are superior to other materials. The use of compomers is questionable due to hygroscopic expansion and possible crack formation as proven for IPS Empress caps in vitro and in vivo. (2) Recent luting cements exhibit excellent flow characteristics with mean film thicknesses ranging between 8 microm and 21 microm. The ultrasonic insertion technique is recommended for viscous luting composites or conventional restorative composites utilizing their thixotropic properties. (3) For successful overhang control, good fit of the restoration (during luting) and high radiopacity of the cement (after luting) are indispensable. Overhang control is estimated easier when the ultrasonic insertion technique is applied. (4) The pre-treatments of ceramic inlays using hydrofluoric acid or silica coating result in effective bonding; for pre-treatment of resin-based composite inlays, silica coating is promising as well. (5) Bonding to enamel and dentin is proven clinically acceptable, but it should be performed with multi-step systems providing separate primers and bonding agents producing a perfect internal seal with almost no hypersensitivities. Dual-cured multi-step bonding agents provide the most promising potential. (6) The viscosity and filler content of the resin composite used for luting does not influence the wear characteristics within the marginal luting area in vivo. However, the ultrasonic insertion technique involving high viscosity materials provides enhanced handling characteristics for luting of tooth-colored inlays. (7) Clinical results with tooth-colored inlays and veneers are promising over periods of up to 10 yrs, including use in severely destroyed teeth.

Inhibitory effect of resin composite containing S-PRG filler on Streptococcus mutans glucose metabolism.

PubMed

Kitagawa, Haruaki; Miki-Oka, Saeki; Mayanagi, Gen; Abiko, Yuki; Takahashi, Nobuhiro; Imazato, Satoshi

2018-03-01

Resin composites containing surface pre-reacted glass-ionomer (S-PRG) fillers have been reported to inhibit Streptococcus mutans growth on their surfaces, and their inhibitory effects were attributed to BO 3 3- and F - ions. The aim of this study was to evaluate S. mutans acid production through glucose metabolism on resin composite containing S-PRG fillers and assess inhibitory effects of BO 3 3- and F - on S. mutans metabolic activities. The pH change through S. mutans acid production on experimental resin composite was periodically measured after the addition of glucose. Inhibitory effects of BO 3 3- or F - solutions on S. mutans metabolism were evaluated by XTT assays and measurement of the acid production rate. The pH of experimental resin containing S-PRG fillers was significantly higher than that of control resin containing silica fillers (p < 0.05). OD 450 values by XTT assays and S. mutans acid production rates significantly decreased in the presence of BO 3 3- and F - compared with the absence of these ions (p < 0.05). pH reduction by S. mutans acid production was inhibited on resin composite containing S-PRG fillers. Moreover, S. mutans glucose metabolism and acid production were inhibited in the presence of low concentrations of BO 3 3- or F - . BO 3 3- or F - released from resin composite containing S-PRG fillers exhibits inhibitory effects on S. mutans metabolism at concentrations lower than those which inhibit bacterial growth. Copyright © 2017 Elsevier Ltd. All rights reserved.

Direct spectrometry: a new alternative for measuring the fluorescence of composite resins and dental tissues.

PubMed

da Silva, Tm; de Oliveira, Hpm; Severino, D; Balducci, I; Huhtala, Mfrl; Gonçalves, Sep

2014-01-01

The aim of this study was to evaluate the fluorescence intensity of different composite resins and compare those values with the fluorescence intensity of dental tissues. Different composite resins were used to make 10 discs (2 mm in depth and 4 mm in diameter) of each brand, divided into groups: 1) Z (Filtek Z350, 3M ESPE), 2) ES (Esthet-X, Dentsply), 3) A (Amelogen Plus, Ultradent), 4) DVS (Durafill-VS, Heraeus Kulzer) with 2 mm composite resin for enamel (A2), 5) OES ([Esthet-X] opaque-OA [1 mm] + enamel-A2 [1 mm]); 6) ODVSI ([Charisma-Opal/Durafill-VSI], opaque-OM (1 mm) + translucent [1mm]), and 7) DVSI ([Durafill- VSI] translucent [2 mm]). Dental tissue specimens were obtained from human anterior teeth cut in a mesiodistal direction to obtain enamel, dentin, and enamel/dentin samples (2 mm). The fluorescence intensity of specimens was directly measured using an optic fiber associated with a spectrometer (Ocean Optics USB 4000) and recorded in graphic form (Origin 8.0 program). Data were submitted to statistical analysis using Dunnet, Tukey, and Kruskall-Wallis tests. Light absorption of the composite resins was obtained in a spectral range from 250 to 450 nm, and that of dental tissues was between 250 and 300 nm. All composite resins were excited at 398 nm and exhibited maximum emissions of around 485 nm. Fluorescence intensity values for all of the resins showed statistically significant differences (measured in arbitrary units [AUs]), with the exception of groups Z and DVS. Group DVSI had the highest fluorescence intensity values (13539 AU), followed by ODVS (10440 AU), DVS (10146 AU), ES (3946 AU), OES (3841 AU), A (3540 AU), and Z (1146 AU). The fluorescence intensity values for the composite resins differed statistically from those of dental tissues (E=1380 AU; D=6262 AU; E/D=3251 AU). The opacity interfered with fluorescence intensity, and group Z demonstrated fluorescence intensity values closest to that of tooth enamel. It is concluded that the fluorescence intensity values were significantly different among the composite resins and compared with dental tissues. The direct spectrofluorimetric method represents a tool for evaluating the fluorescence of composite resins.

Polymerization kinetics of experimental bioactive composites containing bioactive glass.

PubMed

Par, Matej; Tarle, Zrinka; Hickel, Reinhard; Ilie, Nicoleta

2018-06-21

To investigate the polymerization kinetics and the degree of conversion (DC) of experimental resin composites with varying amount of bioactive glass 45S5 (BG). Experimental resin composites based on a photo-curable Bis-GMA/TEGDMA resin system were prepared. The composite series contained 0, 5, 10, 20, and 40 wt% of BG and reinforcing fillers up to the total filler amount of 70 wt%. Composite specimens were light cured with 1,219 mW/cm 2 for 20 or 40 s and their DC was monitored during 5 min at the data collection rate of 2 s -1 using attenuated total reflectance Fourier transform infrared spectroscopy (ATR-FTIR). The 5-min DC values for experimental composites were in the range of 42.4-55.9% and 47.3-57.9% for curing times of 20 and 40 s, respectively. The differences in the 5-min DC between curing times of 20 s or 40 s became more pronounced in materials with higher BG amount. Within both curing times, a decreasing trend of the 5-min DC values was observed with the increasing percentage of BG fillers. The maximum polymerization rate also decreased consistently with the increasing BG amount. Unsilanized BG fillers showed a dose-dependent inhibitory effect on polymerization rate and the DC. Extending the curing time from 20 to 40 s showed a limited potential to improve the DC of composites with higher BG amount. The observed inhibitory effect of BG fillers on the polymerization of resin composites may have a negative influence on mechanical properties and biocompatibility. Copyright © 2018. Published by Elsevier Ltd.

Interaction of LED light with coinitiator-containing composite resins: effect of dual peaks.

PubMed

Sim, Jae-Seong; Seol, Hyo-Joung; Park, Jeong-Kil; Garcia-Godoy, Franklin; Kim, Hyung-Il; Kwon, Yong Hoon

2012-10-01

Recently the colour stability of composite resins has been an issue due to the emphasis on the aesthetics of restored teeth. The purpose of the present study was to investigate how dual-peak LED units affect the polymerization of coinitiator-containing composite resins. Five composite resins [coinitiator-containing: Aelite LS Posterior (AL), Tetric EvoCeram (TE), and Vit-l-escence (VI); only CQ-containing: Grandio (GD) and Filtek Z350 (Z3)] were light cured using four different light-curing units (LCUs). Among them, Bluephase G2 (BP) and G-light (GL) were dual-peak LED LCUs. Microhardness, polymerization shrinkage, flexural, and compressive properties were measured. BP and GL had no consistent effect on the microhardness of AL, TE, and VI on the top and bottom surfaces of resin specimens. Among the specimens, AL and VI showed the least (9.86-10.41 μm) and greatest (17.58-19.21 μm) polymerization shrinkage, respectively. However, the effect of BP and GL on the shrinkage of specimens was not consistent. Among the specimens, GD showed the greatest flexural properties [strength (FS) and modulus (FM)] and TE showed the lowest flexural and compressive properties [strength (CS) and modulus (CM)]. In same resin product, maximum FS and CS differences due to the different LCUs were 10.3-21.0% and 3.6-9.2%, respectively. Furthermore, the influences of BP and GL on FS and CS were not consistent. The tested dual-peak LED LCUs had no consistent synergic effect on the polymerization of coinitiator-containing composite resins as compared with QTH and single-peak LED LCUs. The dual-peak LED LCUs achieve a similar degree of polymerization in coinitiator-composite resins as QTH and single-peak LED LCUs did. Choice of LCU does not appear to be a determinant of the light curing of coinitiator-composite resins. Copyright © 2012 Elsevier Ltd. All rights reserved.

Carbon Fiber Composites for Cryogenic Filament-Wound Vessels.

DTIC Science & Technology

in terms of cryogenic strength properties in epoxy composites. Of the resin systems tested in NOL Ring composites, CTBN /ERLB 4617 exhibited the...bidirectional composite bars showed that the Epon 828/Empol 1040 resin was better at all test temperatures, with the CTBN /ERLB 4617 composites giving somewhat

Resin Flow Behavior Simulation of Grooved Foam Sandwich Composites with the Vacuum Assisted Resin Infusion (VARI) Molding Process

PubMed Central

Zhao, Chenhui; Zhang, Guangcheng; Wu, Yibo

2012-01-01

The resin flow behavior in the vacuum assisted resin infusion molding process (VARI) of foam sandwich composites was studied by both visualization flow experiments and computer simulation. Both experimental and simulation results show that: the distribution medium (DM) leads to a shorter molding filling time in grooved foam sandwich composites via the VARI process, and the mold filling time is linearly reduced with the increase of the ratio of DM/Preform. Patterns of the resin sources have a significant influence on the resin filling time. The filling time of center source is shorter than that of edge pattern. Point pattern results in longer filling time than of linear source. Short edge/center patterns need a longer time to fill the mould compared with Long edge/center sources.

The nonlinear viscoelastic response of resin matrix composite laminates

NASA Technical Reports Server (NTRS)

Hiel, C.; Cardon, A. H.; Brinson, H. F.

1984-01-01

Possible treatments of the nonlinear viscoelastic behavior of materials are reviewed. A thermodynamic based approach, developed by Schapery, is discussed and used to interpret the nonlinear viscoelastic response of a graphite epoxy laminate, T300/934. Test data to verify the analysis for Fiberite 934 neat resin as well as transverse and shear properties of the unidirectional T300/934 composited are presented. Long time creep characteristics as a function of stress level and temperature are generated. Favorable comparisons between the traditional, graphical, and the current analytical approaches are shown. A free energy based rupture criterion is proposed as a way to estimate the life that remains in a structure at any time.

Cytotoxicity Evaluation of Two Bis-Acryl Composite Resins Using Human Gingival Fibroblasts.

PubMed

Gonçalves, Fabiano Palmeira; Alves, Gutemberg; Guimarães, Vladi Oliveira; Gallito, Marco Antônio; Oliveira, Felipe; Scelza, Míriam Zaccaro

2016-01-01

Bis-acryl resins are used for temporary dental restorations and have shown advantages over other materials. The aim of this work was to evaluate the in vitro cytotoxicity of two bis-acryl composite resins (Protemp 4 and Luxatemp Star), obtained at 1, 7 and 40 days after mixing the resin components, using a standardized assay employing human primary cells closely related to oral tissues. Human gingival fibroblast cell cultures were exposed for 24 h to either bis-acryl composite resins, polystyrene beads (negative control) and latex (positive control) extracts obtained after incubation by the different periods, at 37 °C under 5% CO2. Cell viability was evaluated using a multiparametric procedure involving sequential assessment (using the same cells) of mitochondrial activity (XTT assay), membrane integrity (neutral red test) and total cell density (crystal violet dye exclusion test). The cells exposed to the resin extracts showed cell viability indexes exceeding 75% after 24 h. Even when cells were exposed to extracts prepared with longer conditioning times, the bis-acryl composite resins showed no significant cytotoxic effects (p>0.05), compared to the control group or in relation to the first 24 h of contact with the products. There were no differences among the results obtained for the bis-acryl composite resins evaluated 24 h, 7 days and 40 days after mixing. It may be concluded that the bis-acryl resins Protemp 4 and Luxatemp Star were cytocompatible with human gingival fibroblasts, suggesting that both materials are suitable for use in contact with human tissues.

Elastic memory composites (EMC) for deployable industrial and commercial applications

NASA Astrophysics Data System (ADS)

Arzberger, Steven C.; Tupper, Michael L.; Lake, Mark S.; Barrett, Rory; Mallick, Kaushik; Hazelton, Craig; Francis, William; Keller, Phillip N.; Campbell, Douglas; Feucht, Sara; Codell, Dana; Wintergerst, Joe; Adams, Larry; Mallioux, Joe; Denis, Rob; White, Karen; Long, Mark; Munshi, Naseem A.; Gall, Ken

2005-05-01

The use of smart materials and multifunctional components has the potential to provide enhanced performance, improved economics, and reduced safety concerns for applications ranging from outer space to subterranean. Elastic Memory Composite (EMC) materials, based on shape memory polymers and used to produce multifunctional components and structures, are being developed and qualified for commercial use as deployable components and structures. EMC materials are similar to traditional fiber-reinforced composites except for the use of a thermoset shape memory resin that enables much higher packaging strains than traditional composites without damage to the fibers or the resin. This unique capability is being exploited in the development of very efficient EMC structural components for deployable spacecraft systems as well as capability enhancing components for use in other industries. The present paper is intended primarily to describe the transition of EMC materials as smart structure technologies into viable industrial and commercial products. Specifically, the paper discusses: 1) TEMBO EMC materials for deployable space/aerospace systems, 2) TEMBO EMC resins for terrestrial applications, 3) future generation EMC materials.

Evaluation of RTM370 Polyimide Composites by Resin Film Infusion (RFI)

NASA Technical Reports Server (NTRS)

Chuang, Kathy C.; Yip, Thomas A.; Kollmansberger, Ronald B.; Tsotsis, Thomas K.

2014-01-01

RTM370 imide oligomer based on 2,3,3',4'-biphenyl dianhydride (a-BPDA), 3,4'-oxydianiline (3,4'-ODA) and terminated with the 4-phenylethynylphthalic (PEPA) endcap has been shown to exhibit a low melt viscosity (10-30 poise) at 280 C with a pot-life of 1-2 h and a high cured glass-transition temperature (Tg) of 370 C. RTM370 resin has been successfully infused into fiberglass-stitched T650-35 carbon-fabric preforms (ranged from 3- to 6-mm thick) by resin film infusion (RFI). The resulting composite panels were inspected by ultrasonic C-scan and by photomicrographs before and after post-curing as a quality control. Mechanical tests such as unnotched compression (UNC), open-hole compression (OHC), and short-beam shear strength (SBS) at ambient and elevated temperatures were performed before and after isothermal aging at 288 C for 1000 h to assess high-temperature performance. Thermal cycling of RTM370 stitched composites was also conducted from -54 C to 288 C for up to 1600 cycles to evaluate the microcrack resistance of RTM370 polyimide composites fabricated by RFI.

700 F properties of autoclave cured PMR-II composites

NASA Technical Reports Server (NTRS)

Cifani, Diane

1988-01-01

Studies were conducted to develop autoclave processing parameters for graphite reinforced PMR-2 resin composite materials intended for use in applications at temperatures up to 371 degrees (700 F). The effect of resin composition on autoclaveability was investigated. The effect of various graphite fibers and resin composition on 343 C (650 F) and 371 C (700 F) thermo-oxidative stability and mechanical properties was also investigated. The results of the processing studies show that PMR-2 resin composites can be easily fabricated under autoclave conditions. Autoclaved laminates exposed to 1 atm of air at 343 C (650 F) and 371 C (700 F) exhibited less than 5 percent weight loss after 750 hr exposure to 650 F air and 8 percent weight loss during exposure to 700 F air for 500 hr. After 500 hr exposure, autoclaved laminates exhibited greater than 90 percent retention of initial 650 and 700 F flexural and interlaminar shear strengths. The effect of resin formulated molecular weight and postcure conditions on laminate glass transition temperature is also discussed.

The 700 F properties of autoclave cured PMR-2 composites

NASA Technical Reports Server (NTRS)

Vannucci, Raymond D.; Cifani, Diane

1988-01-01

Studies were conducted to develop autoclave processing parameters for graphite reinforced PMR-2 resin composite materials intended for use in applications at temperatures up to 371 degrees (700 F). The effect of resin composition on autoclaveability was investigated. The effect of various graphite fibers and resin composition on 343 C (650 F) and 371 C (700 F) thermo-oxidative stability and mechanical properties was also investigated. The results of the processing studies show that PMR-2 resin composites can be easily fabricated under autoclave conditions. Autoclaved laminates exposed to 1 atm of air at 343 C (650 F) and 371 C (700 F) exhibited less than 5 percent weight loss after 750 hr exposure to 650 F air and 8 percent weight loss during exposure to 700 F air for 500 hr. After 500 hr exposure, autoclaved laminates exhibited greater than 90 percent retention of initial 650 and 700 F flexural and interlaminar shear strengths. The effect of resin formulated molecular weight and postcure conditions on laminate glass transition temperature is also discussed.

Effects of protective resin coating on the surface roughness and color stability of resin-based restorative materials.

PubMed

Bagis, Bora; Tüzüner, Tamer; Turgut, Sedanur; Korkmaz, Fatih Mehmet; Baygın, Özgül; Bağış, Yıldırım Hakan

2014-01-01

The aim of this study was to evaluate the effects of nanofilled protective resin coating (RC) on the surface roughness (Ra) and color stability (ΔE) of resin-based restorative materials (RM) (compomer (C), nanofilled composite (NF), and microhybrid composite (MH)) after being submitted to the ultraviolet aging (UV) method. Thirty-six specimens were prepared (n = 6 for each group). The Ra and (ΔE) values and SEM images were obtained before and after UV. Significant interactions were found among the RM-RC-UV procedures for Ra (P < 0.001). After the specimens were submitted to UV, the Ra values were significantly increased, regardless of the RC procedure (with RC; P < 0.01 for all, without RC; C (P < 0.01), NF (P < 0.001), and MH (P < 0.001)) for each RM. Significant interactions were found between the RM-RC (P < 0.001) procedures for the ΔE values. The ΔE values were increased in each group after applying the RC procedures (P < 0.001). Protective RC usage for RM could result in material-related differences in Ra and ΔE as with used UV method.

Effects of Protective Resin Coating on the Surface Roughness and Color Stability of Resin-Based Restorative Materials

PubMed Central

Tüzüner, Tamer; Korkmaz, Fatih Mehmet; Baygın, Özgül; Bağış, Yıldırım Hakan

2014-01-01

The aim of this study was to evaluate the effects of nanofilled protective resin coating (RC) on the surface roughness (Ra) and color stability (ΔE) of resin-based restorative materials (RM) (compomer (C), nanofilled composite (NF), and microhybrid composite (MH)) after being submitted to the ultraviolet aging (UV) method. Thirty-six specimens were prepared (n = 6 for each group). The Ra and (ΔE) values and SEM images were obtained before and after UV. Significant interactions were found among the RM-RC-UV procedures for Ra (P < 0.001). After the specimens were submitted to UV, the Ra values were significantly increased, regardless of the RC procedure (with RC; P < 0.01 for all, without RC; C (P < 0.01), NF (P < 0.001), and MH (P < 0.001)) for each RM. Significant interactions were found between the RM-RC (P < 0.001) procedures for the ΔE values. The ΔE values were increased in each group after applying the RC procedures (P < 0.001). Protective RC usage for RM could result in material-related differences in Ra and ΔE as with used UV method. PMID:25162066

Modeling the VARTM Composite Manufacturing Process

NASA Technical Reports Server (NTRS)

Song, Xiao-Lan; Loos, Alfred C.; Grimsley, Brian W.; Cano, Roberto J.; Hubert, Pascal

2004-01-01

A comprehensive simulation model of the Vacuum Assisted Resin Transfer Modeling (VARTM) composite manufacturing process has been developed. For isothermal resin infiltration, the model incorporates submodels which describe cure of the resin and changes in resin viscosity due to cure, resin flow through the reinforcement preform and distribution medium and compaction of the preform during the infiltration. The accuracy of the model was validated by measuring the flow patterns during resin infiltration of flat preforms. The modeling software was used to evaluate the effects of the distribution medium on resin infiltration of a flat preform. Different distribution medium configurations were examined using the model and the results were compared with data collected during resin infiltration of a carbon fabric preform. The results of the simulations show that the approach used to model the distribution medium can significantly effect the predicted resin infiltration times. Resin infiltration into the preform can be accurately predicted only when the distribution medium is modeled correctly.

The effect of additional enamel etching and a flowable composite to the interfacial integrity of Class II adhesive composite restorations.

PubMed

Belli, S; Inokoshi, S; Ozer, F; Pereira, P N; Ogata, M; Tagami, J

2001-01-01

This in vitro study evaluated the interfacial integrity of Class II resin composite restorations. The influence of a flowable composite and additional enamel etching was also evaluated. Deep, saucer-shaped Class II cavities were prepared in the mesial and distal proximal surfaces of 25 extracted human molars and assigned to five treatment groups. The gingival margins were extended to approximately 1 mm above the CEJ in 40 cavities and below the CEJ in 10 cavities. The prepared cavities were then restored with a self-etching primer system (Clearfil Liner Bond II) and a hybrid resin composite (Clearfil AP-X), with and without a flowable composite (Protect Liner F) and additional enamel etching with 37% phosphoric acid gel (K-etchant). After finishing, polishing and thermocycling (4 and 60 degrees C, x300), the samples were longitudinally sectioned through the restorations and resin-tooth interfaces were observed directly under a laser scanning microscope. Statistical analysis indicated that the use of a flowable composite produced significantly more (p = 0.04) gap-free resin-dentin interfaces than teeth restored without the flowable composite. However, both flowable composite and enamel etching could not prevent gap formation at enamel-resin interfaces and crack formation on enamel walls.

Effect of light dispersion of LED curing lights on resin composite polymerization.

PubMed

Vandewalle, Kraig S; Roberts, Howard W; Andrus, Jeffrey L; Dunn, William J

2005-01-01

This study evaluated the effect of light dispersion of halogen and LED curing lights on resin composite polymerization. One halogen (Optilux 501, SDS/Kerr, Orange, CA, USA) and five light-emitting diode (LED) curing lights (SmartLite iQ, Dentsply Caulk, Milford, DE, USA; LEDemetron 1, SDS/Kerr; FLASHlite 1001, Discus Dental, Culver City, CA, USA; UltraLume LED 5, Ultradent Products, South Jordan, UT, USA; Allegro, Den-Mat, Santa Maria, CA, USA) were used in this study. Specimens (8 mm diameter by 2 mm thick) were made in polytetrafluoroethylene molds using hybrid (Z100, 3M ESPE, St. Paul, MN, USA) and microfill (A110, 3M ESPE) composite resins. The top surface was polymerized for 5 seconds with the curing light guide tip positioned at a distance of 1 and 5 mm. Degree of conversion (DC) of the composite specimens was analyzed on the bottom surface using micro-Fourier Transform Infrared (FTIR) spectroscopy (Perkin-Elmer FTIR Spectrometer, Wellesley, PA, USA) 10 minutes after light activation. DC at the bottom of the 2 mm specimen was expressed as a percentage of the mean maximum DC. Five specimens were created per curing light and composite type (n=5). Percent mean DC ratios and SDs were calculated for each light under each testing condition. Data were analyzed by analysis of variance (ANOVA)/Tukey's test (alpha = .05). A beam analyzer (LBA-700, Spiricon, Logan, UT, USA) was used to record the emitted light from the curing lights at 0 and 5 mm distances (n=5). A Top Hat factor was used to compare the quality of the emitted beam profile (LBA/PC, Spiricon). The divergence angle from vertical was also determined in the x- and y-axes (LBA/PC). Mean values and SDs were calculated for each light under each testing condition (0 and 5 mm, x- and y-axes) and analyzed by a two-way ANOVA/Tukey's test (alpha = .05). For DC ratios, significant differences were found based on curing light and curing distance (p < .05). At 1 mm, Optilux 501 and FLASHlite 1001 produced significantly higher DC ratios with the hybrid resin composite. No differences were found among lights with the microfill at 1 mm. At 5 mm, SmartLite iQ, FLASHlite 1001, LEDemetron 1, and UltraLume LED 5 produced significantly higher DC ratios with the hybrid resin composite, whereas LEDemetron 1 and SmartLite iQ produced significantly higher DC ratios with the microfill resin composite. The UltraLume LED 5, Allegro, and Optilux 501 had significant reductions in mean DC ratios at curing distances of 1 and 5 mm with both resin composite types. For dispersion of light, significant differences were found in Top Hat factor and divergence angle (p < .001). SmartLite iQ had overall the highest Top Hat factor and lowest divergence angle of tested lights. A linear regression analysis relating pooled DC with pooled Top Hat factors and divergence angles found a very good correlation (r2 = .86) between dispersion of light over distance and the ability to polymerize resin composite. The latest generation of LED curing lights provides DC ratios similar to or better than the halogen curing light at a curing distance of 5 mm. Dispersion of light plays a significant role in the DC of resin composite. To maximize curing effectiveness, light guides should be maintained in close proximity to the surface of the light-activated restorative material.

Fracture Resistance of Premolars Restored by Various Types and Placement Techniques of Resin Composites

PubMed Central

Moosavi, Horieh; Zeynali, Mahsa; Pour, Zahra Hosseini

2012-01-01

To verify the fracture resistance of premolars with mesioocclusodistal preparations restored by different resin composites and placement techniques. Sixty premolars were randomly divided into two groups based on type of composite resin: Filtek P60 or Nulite F, and then each group was separated into three subgroups: bulk, centripetal, and fiber insert according to the type of placement method (n = 10). Single-bond adhesive system was used as composite bonding according to the manufacturer's instructions. Specimens were restored in Groups 1, 2, and 3 with Filtek P60 and in Groups 4, 5, and 6 with Nulite F. After being stored 24 hours at 37°C, a 4 mm diameter steel sphere in a universal testing machine was applied on tooth buccal and lingual cusps at a cross-head speed of 5 mm/min until fracture occurred. Groups 3 and 6 showed higher fracture resistance than Groups 1, 2, 4, and 5. Among the placement techniques, the fiber insert method had a significant effect, but the type of composite was ineffective. The insertion technique in contrast to the type of material had a significant influence on the fracture resistance of premolar teeth. PMID:22666255

[Three-dimensional finite element analysis of the upper cervical-defected incisor with labial access or lingual access].

PubMed

Su, Fan; Zhao, Ying; Su, Qin

2013-08-01

To evaluate the stress distribution of the cervical-defected incisor with labial or lingual endodontic access with finite element analysis (FEA), and to explore the advantage of resistance in labial endodontic access. 3-D finite element models of upper cervical-defected incisor were established using cone-beam CT (CBCT), Mimics Catia, and Ansys software. The subjects were categorized according to the two endodontic accesses and three restorative ways, which were composite resin, glass fiber-reinforced composite resin and glass fiber-reinforced post-crown. All the models were loaded.The von Mises stress values and distribution were recorded and analyzed with Ansys 10.0 software. In this study, direct composite resin restoration showed no significant difference between the labial and lingual access. In glass fiber-reinforced composite resin, labial access could transfer the stress concentration area. It could reduce the incidence of fracture of the cervical lesion but increase the incidence of root fracture. Post-crown restoration could obviously reduce the incidence of fracture of the cervical lesion. When the cervical-defected incisor is restored with composite resin, labial and lingual accesses can be considered. Labial access with glass fiber-reinforced composite resin or post-crown restoration is a good choice.

The Effect of Irradiation Distance on Microhardness of Resin Composites Cured with Different Light Curing Units

PubMed Central

Cekic-Nagas, Isil; Egilmez, Ferhan; Ergun, Gulfem

2010-01-01

Objectives: The aim of this study was to compare the microhardness of five different resin composites at different irradiation distances (2 mm and 9 mm) by using three light curing units (quartz tungsten halogen, light emitting diodes and plasma arc). Methods: A total of 210 disc-shaped samples (2 mm height and 6 mm diameter) were prepared from different resin composites (Simile, Aelite Aesthetic Enamel, Clearfil AP-X, Grandio caps and Filtek Z250). Photoactivation was performed by using quartz tungsten halogen, light emitting diode and plasma arc curing units at two irradiation distances (2 mm and 9 mm). Then the samples (n=7/per group) were stored dry in dark at 37°C for 24 h. The Vickers hardness test was performed on the resin composite layer with a microhardness tester (Shimadzu HMV). Data were statistically analyzed using nonparametric Kruskal Wallis and Mann-Whitney U tests. Results: Statistical analysis revealed that the resin composite groups, the type of the light curing units and the irradiation distances have significant effects on the microhardness values (P<.05). Conclusions: Light curing unit and irradiation distance are important factors to be considered for obtaining adequate microhardness of different resin composite groups. PMID:20922164

Fingerprint test data report: FM 5834 test lots No. 1, 3, 4, and 5. [resin matrix composites

NASA Technical Reports Server (NTRS)

1986-01-01

Quality control testing is presented for various lots of resin matrix composites. The tests conducted were filler test, resin test, fabric test, and prepreg test for lots 1, 3, 4, and 5. The results of the tests are presented in chart forms.

Antibacterial activity of resin composites containing surface pre-reacted glass-ionomer (S-PRG) filler.

PubMed

Miki, Saeki; Kitagawa, Haruaki; Kitagawa, Ranna; Kiba, Wakako; Hayashi, Mikako; Imazato, Satoshi

2016-09-01

A surface pre-reacted glass-ionomer (S-PRG) filler is a technology of interest for providing bio-functions to restorative materials. Resin composites containing S-PRG filler have been reported to show less plaque accumulation and reduced bacterial attachment. In this study, experimental resin composites containing S-PRG filler at various concentrations were fabricated, and the inhibitory effects on bacterial growth on their surface and the association of ions released from S-PRG filler with antibacterial activity were evaluated. Five kinds of experimental resin composites containing S-PRG filler at 0, 13.9, 27.3, 41.8, or 55.9 (vol.%) were fabricated. Streptococcus mutans was cultured on the cured discs for 18h to examine the growth of bacteria in contact with the surface of the experimental resins. The concentrations of Al(3+), BO3(3-), F(-), Na(+), SiO3(2-), or Sr(2+) released from each experimental resin into water were measured. The standardized solutions of each ion were prepared at the concentrations determined to be released from the experimental resin, and their inhibitory effects of single ion species on S. mutans growth were evaluated by using each standardized solution. Resin composites containing S-PRG filler at 13.9 (vol.%) or greater inhibited S. mutans growth on their surface. When S. mutans was incubated in the presence of six kinds of ions at the concentrations released from the resin composite containing S-PRG filler at 55.9 (vol.%), a significant reduction in bacterial number was observed for BO3(3-), F(-), Al(3+), and SiO3(2-). Among these four ions, BO3(3-) and F(-) demonstrated the strongest inhibitory effect on S. mutans growth. Our findings suggest that resin composites containing S-PRG filler inhibit the growth of S. mutans on their surface. BO3(3-), F(-), Al(3+) and SiO3(2-) released from S-PRG filler have the ability to inhibit S. mutans growth, and the inhibitory effects are mainly attributed to release of BO3(3-) and F(-). Copyright © 2016 The Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Marginal adaptation of composite resins under two adhesive techniques.

PubMed

Dačić, Stefan; Veselinović, Aleksandar M; Mitić, Aleksandar; Nikolić, Marija; Cenić, Milica; Dačić-Simonović, Dragica

2016-11-01

In the present research, different adhesive techniques were used to set up fillings with composite resins. After the application of etch and rinse or self etch adhesive technique, marginal adaptation of composite fillings was estimated by the length of margins without gaps, and by the microretention of resin in enamel and dentin. The study material consisted of 40 extracted teeth. Twenty Class V cavities were treated with 35% phosphorous acid and restored after rinsing by Adper Single Bond 2 and Filtek Ultimate-ASB/FU 3M ESPE composite system. The remaining 20 cavities were restored by Adper Easy One-AEO/FU 3M ESPE composite system. Marginal adaptation of composite fillings was examined using a scanning electron microscope (SEM). The etch and rinse adhesive technique showed a significantly higher percentage of margin length without gaps (in enamel: 92.5%, in dentin: 57.3%), compared with the self-etch technique with lower percentage of margin length without gaps, in enamel 70.4% (p < .001), and in dentin-22.6% (p < .05). In the first technique, microretention was composed of adhesive and hybrid layers as well as resin tugs in interprismatic spaces of enamel, while the dentin microretention was composed of adhesive and hybrid layers with resin tugs in dentin canals. In the second technique, resin tugs were rarely seen and a microgap was dominant along the border of restoration margins. The SEM analysis showed a better marginal adaptation of composite resin to enamel and dentin with better microretention when the etch and rinse adhesive procedure was applied. © 2016 Wiley Periodicals, Inc.

Effects of tributylborane-activated adhesive and two silane agents on bonding computer-aided design and manufacturing (CAD/CAM) resin composite.

PubMed

Shinohara, Ayano; Taira, Yohsuke; Sawase, Takashi

2017-10-01

The present study was conducted to evaluate the effects of an experimental adhesive agent [methyl methacrylate-tributylborane liquid (MT)] and two adhesive agents containing silane on the bonding between a resin composite block of a computer-aided design and manufacturing (CAD/CAM) system and a light-curing resin composite veneering material. The surfaces of CAD/CAM resin composite specimens were ground with silicon-carbide paper, treated with phosphoric acid, and then primed with either one of the two silane agents [Scotchbond Universal Adhesive (SC) and GC Ceramic Primer II (GC)], no adhesive control (Cont), or one of three combinations (MT/SC, MT/GC, and MT/Cont). A light-curing resin composite was veneered on the primed CAD/CAM resin composite surface. The veneered specimens were subjected to thermocycling between 4 and 60 °C for 10,000 cycles, and the shear bond strengths were determined. All data were analyzed using analysis of variance and a post hoc Tukey-Kramer HSD test (α = 0.05, n = 8). MT/SC (38.7 MPa) exhibited the highest mean bond strengths, followed by MT/GC (30.4 MPa), SC (27.9 MPa), and MT/Cont (25.7 MPa), while Cont (12.9 MPa) and GC (12.3 MPa) resulted in the lowest bond strengths. The use of MT in conjunction with a silane agent significantly improved the bond strength. Surface treatment with appropriate adhesive agents was confirmed as a prerequisite for veneering CAD/CAM resin composite restorations.

Tensile bond strength of an aged resin composite repaired with different protocols.

PubMed

Celik, Esra Uzer; Ergücü, Zeynep; Türkün, L Sebnem; Ercan, Utku Kürșat

2011-08-01

To evaluate the effect of different surface treatments and bonding procedures on the tensile bond strength (TBS) of resin composites repaired 6 months after polymerization. Resin composite sticks were aged in distilled water at 37°C for 6 months. They were divided into 12 groups (n = 10) according to the combination of surface treatment/bonding procedures [none, only bur treatment, XP Bond (XPB/Dentsply/DeTrey) with/without bur, AdheSE (A-SE/Ivoclar/Vivadent) with/without bur, Composite Primer (CP/GC) with/without bur, CP after bur and acid-etching, XPB after acid etching and CP with bur, A-SE after bur and CP]. The ultimate tensile bond strength (UTS) of the resin composites was tested in intact but aged specimens. Tensile bond strengths were tested with a universal testing machine (Shimadzu). Data were analyzed using one-way ANOVA and Duncan Multiple Comparisons tests (p < 0.05). All repaired groups showed significantly higher TBS than the group without any sureface treatment (p < 0.05). Four groups resulted in TBS similar to those of intact resin composite UTS: A-SE, A-SE with bur, A-SE after CP with bur, and XPB after acid etching+CP with bur. Bur treatment, silane primer or etch-and-rinse adhesive application alone were not successful in the repair process of aged resin composite, whereas self-etching adhesive alone showed similar performance to the intact specimens. Combined procedures generally showed better performance: A-SE with bur, A-SE after CP with bur, and XPB after acid etching +CP with bur showed TBS similar to those of the intact specimens. It was concluded that bur roughening of the surfaces and rebonding procedures were essential for repairing aged resin composites.

Laboratory evaluation of the effect of unfilled resin after the use of self-etch and total-etch dentin adhesives on the Shear Bond Strength of composite to dentin.

PubMed

Nasseri, Ehsan Baradaran; Majidinia, Sara; Sharbaf, Davood Aghasizadeh

2017-05-01

Based on the frequent application of composite resins as tooth-colored fillings, this method is considered a viable alternative to dental amalgam. However, this method has the low bond strength of the composite to dentin. To solve this issue, various dental adhesive systems with different characteristics have been developed by dentistry experts. To assess the effect of an additional layer of unfilled resin in self-etch and total-etch dentin adhesives on the shear bond strength (SBS) of composite to dentin. Moreover, we assessed the effects of sample storage in artificial saliva on the SBS of composite to dentin. Methods: This experimental study was conducted on 160 freshly extracted human first or second premolar teeth, which were randomly divided into 16 groups. The teeth were prepared from Mashhad University of Medical Sciences, Mashhad, Iran (2008-2009). Scotchbond Multi-purpose (SBMP), single bond (SB), Clearfil SE Bond, and Clearfil S3 Bond were applied to dentin surface with or without the placement of hydrophobic resin (Margin Bond) in accordance with the instructions of the manufacturers. To expose the coronal dentin, the teeth were abraded with 600 grit SiC paper. Immediately after restoration, half of the samples were tested in terms of SBS, while the other samples were evaluated in terms of SBS after three months of storage in artificial saliva. SBS rates of dental composites evaluated by universal testing machine and samples were studied by optical stereomicroscopy to verify the failure type. Data analysis was performed in SPSS V.16 using Kolmogorov-Smirnov test, independent-samples t-test, ANOVA, and Duncan's logistic regression test. In this study, a significant reduction was observed in the SBS rates of SB and S3 bond adhesive systems after storage with and without hydrophobic resin (p>0.000). Without storage in normal saline, a significant increase was observed in the SBS rate of the SE bond (p=0.013). In addition, SBS rate of SBMP significantly increased after storage with hydrophobic resin (p=0.001). Finally, the highest and lowest rates of SBS were observed in the SE and S3 bonds in all the experimental groups, respectively. The effects of using a hydrophobic resin layer on shear bond strength values seem to be effective. The mild self-etch adhesive exhibited the best resin-dentine bond strength after aging.

Laboratory evaluation of the effect of unfilled resin after the use of self-etch and total-etch dentin adhesives on the Shear Bond Strength of composite to dentin

PubMed Central

Nasseri, Ehsan Baradaran; Majidinia, Sara; Sharbaf, Davood Aghasizadeh

2017-01-01

Background Based on the frequent application of composite resins as tooth-colored fillings, this method is considered a viable alternative to dental amalgam. However, this method has the low bond strength of the composite to dentin. To solve this issue, various dental adhesive systems with different characteristics have been developed by dentistry experts. Aim To assess the effect of an additional layer of unfilled resin in self-etch and total-etch dentin adhesives on the shear bond strength (SBS) of composite to dentin. Moreover, we assessed the effects of sample storage in artificial saliva on the SBS of composite to dentin. Methods Methods: This experimental study was conducted on 160 freshly extracted human first or second premolar teeth, which were randomly divided into 16 groups. The teeth were prepared from Mashhad University of Medical Sciences, Mashhad, Iran (2008–2009). Scotchbond Multi-purpose (SBMP), single bond (SB), Clearfil SE Bond, and Clearfil S3 Bond were applied to dentin surface with or without the placement of hydrophobic resin (Margin Bond) in accordance with the instructions of the manufacturers. To expose the coronal dentin, the teeth were abraded with 600 grit SiC paper. Immediately after restoration, half of the samples were tested in terms of SBS, while the other samples were evaluated in terms of SBS after three months of storage in artificial saliva. SBS rates of dental composites evaluated by universal testing machine and samples were studied by optical stereomicroscopy to verify the failure type. Data analysis was performed in SPSS V.16 using Kolmogorov-Smirnov test, independent-samples t-test, ANOVA, and Duncan’s logistic regression test. Results In this study, a significant reduction was observed in the SBS rates of SB and S3 bond adhesive systems after storage with and without hydrophobic resin (p>0.000). Without storage in normal saline, a significant increase was observed in the SBS rate of the SE bond (p=0.013). In addition, SBS rate of SBMP significantly increased after storage with hydrophobic resin (p=0.001). Finally, the highest and lowest rates of SBS were observed in the SE and S3 bonds in all the experimental groups, respectively. Conclusion The effects of using a hydrophobic resin layer on shear bond strength values seem to be effective. The mild self-etch adhesive exhibited the best resin-dentine bond strength after aging PMID:28713512

Preform Characterization in VARTM Process Model Development

NASA Technical Reports Server (NTRS)

Grimsley, Brian W.; Cano, Roberto J.; Hubert, Pascal; Loos, Alfred C.; Kellen, Charles B.; Jensen, Brian J.

2004-01-01

Vacuum-Assisted Resin Transfer Molding (VARTM) is a Liquid Composite Molding (LCM) process where both resin injection and fiber compaction are achieved under pressures of 101.3 kPa or less. Originally developed over a decade ago for marine composite fabrication, VARTM is now considered a viable process for the fabrication of aerospace composites (1,2). In order to optimize and further improve the process, a finite element analysis (FEA) process model is being developed to include the coupled phenomenon of resin flow, preform compaction and resin cure. The model input parameters are obtained from resin and fiber-preform characterization tests. In this study, the compaction behavior and the Darcy permeability of a commercially available carbon fabric are characterized. The resulting empirical model equations are input to the 3- Dimensional Infiltration, version 5 (3DINFILv.5) process model to simulate infiltration of a composite panel.

Novel matrix resins for composites for aircraft primary structures, phase 1

NASA Technical Reports Server (NTRS)

Woo, Edmund P.; Puckett, P. M.; Maynard, S.; Bishop, M. T.; Bruza, K. J.; Godschalx, J. P.; Mullins, M. J.

1992-01-01

The objective of the contract is the development of matrix resins with improved processability and properties for composites for primarily aircraft structures. To this end, several resins/systems were identified for subsonic and supersonic applications. For subsonic aircraft, a series of epoxy resins suitable for RTM and powder prepreg was shown to give composites with about 40 ksi compressive strength after impact (CAI) and 200 F/wet mechanical performance. For supersonic applications, a thermoplastic toughened cyanate prepreg system has demonstrated excellent resistance to heat aging at 360 F for 4000 hours, 40 ksi CAI and useful mechanical properties at greater than or equal to 310 F. An AB-BCB-maleimide resin was identified as a leading candidate for the HSCT. Composite panels fabricated by RTM show CAI of approximately 50 ksi, 350 F/wet performance and excellent retention of mechanical properties after aging at 400 F for 4000 hours.

Creep of experimental short fiber-reinforced composite resin.

PubMed

Garoushi, Sufyan; Kaleem, Muhammad; Shinya, Akikazu; Vallittu, Pekka K; Satterthwaite, Julian D; Watts, David C; Lassila, Lippo V J

2012-01-01

The purpose of this study was to investigate the reinforcing effect of short E-glass fiber fillers oriented in different directions on composite resin under static and dynamic loading. Experimental short fiber-reinforced composite resin (FC) was prepared by mixing 22.5 wt% of short E-glass fibers, 22.5 wt% of resin, and 55 wt% of silane-treated silica fillers. Three groups of specimens (n=5) were tested: FC with isotropic fiber orientation, FC with anisotropic fiber orientation, and particulate-filled composite resin (PFC) as a control. Time-dependent creep and recovery were recorded. ANOVA revealed that after secondary curing in a vacuum oven and after storage in dry condition for 30 days, FC with isotropic fiber orientation (1.73%) exhibited significantly lower static creep value (p<0.05) than PFC (2.54%). For the different curing methods and storage conditions evaluated in this study, FC achieved acceptable static and dynamic creep values when compared to PFC.

Qualitative and quantitative studies of chemical composition of sandarac resin by GC-MS.

PubMed

Kononenko, I; de Viguerie, L; Rochut, S; Walter, Ph

2017-01-01

The chemical composition of sandarac resin was investigated qualitatively and quantitatively by gas chromatography-mass spectrometry (GC-MS). Six compounds with labdane and pimarane skeletons were identified in the resin. The obtained mass spectra were interpreted and the mass spectrometric behaviour of these diterpenoids under EI conditions was described. Quantitative analysis by the method of internal standard revealed that identified diterpenoids represent only 10-30% of the analysed sample. The sandarac resin from different suppliers was analysed (from Kremer, Okhra, Color Rare, La Marchande de Couleurs, L'Atelier Montessori, Hevea). The analysis of different lumps of resins showed that the chemical composition differs from one lump to another, varying mainly in the relative distributions of the components.

Core-shell quantum dots tailor the fluorescence of dental resin composites.

PubMed

Alves, Leandro P; Pilla, Viviane; Murgo, Dírian O A; Munin, Egberto

2010-02-01

We characterized the optical properties, such as absorbance and fluorescence, of dental resins containing quantum dots (QD). We also determined the doping level needed to obtain a broad and nearly flat emission spectrum that provides the perception of white color. The samples studied were resin composites from Charisma (Heraeus Kulzer) prepared with CdSe/ZnS core-shell QD (0.05-0.77 mass%). The results showed that the fluorescence of dental resin composites can be tailored by using CdSe/ZnS core-shell quantum dots. QD core incorporation into dental resins allows the fabrication of restorative materials with fluorescence properties that closely match those of natural human teeth. Copyright 2009 Elsevier Ltd. All rights reserved.

An infiltration/cure model for manufacture of fabric composites by the resin infusion process

NASA Technical Reports Server (NTRS)

Weideman, Mark H.; Loos, Alfred C.; Dexter, H. Benson; Hasko, Gregory H.

1992-01-01

A 1-D infiltration/cure model was developed to simulate fabrication of advanced textile composites by the resin film infusion process. The simulation model relates the applied temperature and pressure processing cycles, along with the experimentally measured compaction and permeability characteristics of the fabric preforms, to the temperature distribution, the resin degree of cure and viscosity, and the infiltration flow front position as a function of time. The model also predicts the final panel thickness, fiber volume fraction, and resin mass for full saturation as a function of compaction pressure. Composite panels were fabricated using the RTM (Resin Transfer Molding) film infusion technique from knitted, knitted/stitched, and 2-D woven carbon preforms and Hercules 3501-6 resin. Fabric composites were fabricated at different compaction pressures and temperature cycles to determine the effects of the processing on the properties. The composites were C-scanned and micrographed to determine the quality of each panel. Advanced cure cycles, developed from the RTM simulation model, were used to reduce the total cure cycle times by a factor of 3 and the total infiltration times by a factor of 2.

Macro- and microtopographical examination and quantification of CAD-CAM composite resin 2- and 3-body wear.

PubMed

Stöckl, Carolin; Hampe, Rüdiger; Stawarczyk, Bogna; Haerst, Miriam; Roos, Malgorzata

2018-04-05

The selection of an appropriate restorative material based on wear behavior is important for the long-term success of a dental restoration. For computer-aided design and computer-aided manufacturing (CAD-CAM) composite resins, information about their wear resistance and wear mechanism is scarce. The purpose of this in vitro study was to compare the 2- and 3-body wear of CAD-CAM composite resins with that of lithium disilicate ceramic and to develop analysis software. Flat specimens were prepared from the following CAD-CAM composite resins: Cerasmart (CS), SHOFU Block HC (SH), Katana Avencia (KA), Brilliant Crios (BC), an experimental composite resin (EXP), and lithium disilicate ceramic IPS e.max CAD (REF). The specimens underwent 2-body wear (50 N, 5/55°C, 400 000 cycles) opposed by human enamel antagonists. Specimen wheels were prepared with each material on each wheel for 3-body wear with a millet slurry (15 N, 15% slip, 200 000 cycles). All specimens were digitized by using a dedicated laser scanner. Analysis software was developed to calculate macrotopographical examination of volume loss. The microtopography of the surfaces was examined by using scanning electron microscopy. For data analysis, the Kruskal-Wallis test with the Tukey-Kramer post hoc test and the 1-sample Wilcoxon test were used (α=.05). After 2-body wear simulation, SH and KA presented higher volume loss than the other CAD-CAM materials. For 3-body wear, REF had lower volume loss than CS, SH, or BC. In addition, BC led to higher volume loss than EXP. The patterns of 2- and 3-body wear were different. The ceramic showed good global wear resistance. The volume loss of the CAD-CAM composite resins differed and depended on the material. The 2- and 3-body wear test methods tended to differ with regard to volume loss. Examination of the worn surfaces revealed different mechanisms acting in 2- and 3-body wear test. Copyright © 2017 Editorial Council for the Journal of Prosthetic Dentistry. Published by Elsevier Inc. All rights reserved.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Li, Yang; Zhao, Qiangsheng; Mirdamadi, Mansour

Woven fabric carbon fiber/epoxy composites made through compression molding are one of the promising choices of material for the vehicle light-weighting strategy. Previous studies have shown that the processing conditions can have substantial influence on the performance of this type of the material. Therefore the optimization of the compression molding process is of great importance to the manufacturing practice. An efficient way to achieve the optimized design of this process would be through conducting finite element (FE) simulations of compression molding for woven fabric carbon fiber/epoxy composites. However, performing such simulation remains a challenging task for FE as multiple typesmore » of physics are involved during the compression molding process, including the epoxy resin curing and the complex mechanical behavior of woven fabric structure. In the present study, the FE simulation of the compression molding process of resin based woven fabric composites at continuum level is conducted, which is enabled by the implementation of an integrated material modeling methodology in LS-Dyna. Specifically, the chemo-thermo-mechanical problem of compression molding is solved through the coupling of three material models, i.e., one thermal model for temperature history in the resin, one mechanical model to update the curing-dependent properties of the resin and another mechanical model to simulate the behavior of the woven fabric composites. Preliminary simulations of the carbon fiber/epoxy woven fabric composites in LS-Dyna are presented as a demonstration, while validations and models with real part geometry are planned in the future work.« less

[Effect of thermal cycling on surface microstructure of different light-curing composite resins].

PubMed

Lv, Da; Liu, Kai-Lei; Yao, Yao; Zhang, Wei-Sheng; Liao, Chu-Hong; Jiang, Hong

2015-04-01

To evaluate the effect of thermal cycling on surface microstructure of different light-curing composite resins. A nanofilled composite (Z350) and 4 microhybrid composites (P60, Z250, Spectrum, and AP-X) were fabricated from lateral to center to form cubic specimens. The lateral surfaces were abrased and polished before water storage and 40 000 thermal cycles (5/55 degrees celsius;). The mean surface roughness (Ra) were measured and compared before and after thermal cycling, and the changes of microstructure were observed under scanning electron microscope (SEM). Significant decreases of Ra were observed in the composites, especially in Spectrum (from 0.164±0.024 µm to 0.140±0.017 µm, P<0.001) and Z250 (from 0.169±0.035 µm to 0.144±0.033 µm, P<0.001), whose Ra approximated that of P60 (0.121±0.028 µm) with smoothly polished surface. SEM revealed scratches and shallower pits on the surface of all the 5 resins, and fissures occurred on Z350 following the thermal cycling. Water storage and thermal cycling may produce polishing effect on composite resins and cause fissures on nanofilled composite resins.

Influence of irradiance on Knoop hardness, degree of conversion, and polymerization shrinkage of nanofilled and microhybrid composite resins.

PubMed

Fugolin, Ana Paula Piovezan; Correr-Sobrinho, Lourenço; Correr, Américo Bortolazzo; Sinhoreti, Mário Alexandre Coelho; Guiraldo, Ricardo Danil; Consani, Simonides

2016-01-01

The purpose of this study was to investigate the influence of the irradiance emitted by a light-curing unit on microhardness, degree of conversion (DC), and gaps resulting from shrinkage of 2 dental composite resins. Cylinders of nanofilled and microhybrid composites were fabricated and light cured. After 24 hours, the tops and bottoms of the specimens were evaluated via indentation testing and Fourier transform infrared spectroscopy to determine Knoop hardness number (KHN) and DC, respectively. Gap width (representing polymerization shrinkage) was measured under a scanning electron microscope. The nanofilled composite specimens presented significantly greater KHNs than did the microhybrid specimens (P < 0.05). The microhybrid composite resin exhibited significantly greater DC and gap width than the nanofilled material (P < 0.05). Irradiance had a mostly material-dependent influence on the hardness and DC, but not the polymerization shrinkage, of composite resins.

Studies on Hot-Melt Prepregging on PRM-II-50 Polyimide Resin with Graphite Fibers

NASA Technical Reports Server (NTRS)

Shin, E. Eugene; Sutter, James K.; Juhas, John; Veverka, Adrienne; Klans, Ojars; Inghram, Linda; Scheiman, Dan; Papadopoulos, Demetrios; Zoha, John; Bubnick, Jim

2004-01-01

A second generation PMR (in situ Polymerization of Monomer Reactants) polyimide resin PMR-II-50, has been considered for high temperature and high stiffness space propulsion composites applications for its improved high temperature performance. As part of composite processing optimization, two commercial prepregging methods: solution vs. hot-melt processes were investigated with M40J fabrics from Toray. In a previous study a systematic chemical, physical, thermal and mechanical characterization of these composites indicated the poor resin-fiber interfacial wetting, especially for the hot-melt process, resulted in poor composite quality. In order to improve the interfacial wetting, optimization of the resin viscosity and process variables were attempted in a commercial hot-melt prepregging line. In addition to presenting the results from the prepreg quality optimization trials, the combined effects of the prepregging method and two different composite cure methods, i.e. hot press vs. autoclave on composite quality and properties are discussed.

Studies on Hot-Melt Prepregging of PMR-II-50 Polyimide Resin with Graphite Fibers

NASA Technical Reports Server (NTRS)

Shin, E. Eugene; Sutter, James K.; Juhas, John; Veverka, Adrienne; Klans, Ojars; Inghram, Linda; Scheiman, Dan; Papadopoulos, Demetrios; Zoha, John; Bubnick, Jim

2003-01-01

A Second generation PMR (in situ Polymerization of Monomer Reactants) polyimide resin, PMR-II-50, has been considered for high temperature and high stiffness space propulsion composites applications for its improved high temperature performance. As part of composite processing optimization, two commercial prepregging methods: solution vs. hot-melt processes were investigated with M40J fabrics from Toray. In a previous study a systematic chemical, physical, thermal and mechanical characterization of these composites indicated that poor resin-fiber interfacial wetting, especially for the hot-melt process, resulted in poor composite quality. In order to improve the interfacial wetting, optimization of the resin viscosity and process variables were attempted in a commercial hot-melt prepregging line. In addition to presenting the results from the prepreg quality optimization trials, the combined effects of the prepregging method and two different composite cure methods, i.e., hot press vs. autoclave on composite quality and properties are discussed.

Degree of conversion of nanofilled and microhybrid composite resins photo-activated by different generations of LEDs.

PubMed

Ribeiro, Benicia Carolina Iaskieviscz; Boaventura, Juliana Maria Capelozza; Brito-Gonçalves, Joel de; Rastelli, Alessandra Nara de Souza; Bagnato, Vanderlei Salvador; Saad, José Roberto Cury

2012-01-01

This study aimed at evaluating the degree of conversion (DC) of four composite resins, being one nanofilled and 3 microhybrid resins, photo-activated with second- and third-generation light-emitting diodes (LEDs). Filtek™ Z350 nanofilled composite resins and Amelogen® Plus, Vit-l-escence™ and Opallis microhybrid resins were photo-activated with two second-generation LEDs (Radii-cal and Elipar Free Light™ 2) and one third-generation LED (Ultra-Lume LED 5) by continuous light mode, and a quartz halogen-tungsten bulb (QHT, control). After 24 h of storage, the samples were pulverized into fine powder and 5 mg of each material were mixed with 100 mg of potassium bromide (KBr). After homogenization, they were pressed, which resulted in a pellet that was evaluated using an infrared spectromer (Nexus 470, Thermo Nicolet) equipped with TGS detector using diffuse reflectance (32 scans, resolution of 4 cm(-1)) coupled to a computer. The percentage of unreacted carbon-carbon double bonds (% C=C) was determined from the ratio of absorbance intensities of aliphatic C=C (peak at 1637 cm-1) against internal standard before and after curing of the specimen: aromatic C-C (peak at 1610 cm-1). The ANOVA showed a significant effect on the interaction between the light-curing units (LCUs) and the composite resins (p<0.001). The Tukey’s test showed that the nanofilled resin (Filtek™ Z350) and Opallis when photo-activated by the halogen lamp (QTH) had the lowest DC compared with the other microhybrid composite resins. The DC of the nanofilled resin (Filtek™ Z350) was also lower using LEDs. The highest degrees of conversion were obtained using the third-generation LED and one of second-generation LEDs (Elipar Free Light™ 2). The nanofilled resin showed the lowest DC, and the Vit-l-escence™ microhybrid composite resin showed the highest DC. Among the LCUs, it was not possible to establish an order, even though the second-generation LED Radii-cal provided the lowest DC.

Degree of conversion of nanofilled and microhybrid composite resins photo-activated by different generations of LEDs

PubMed Central

RIBEIRO, Benicia Carolina Iaskieviscz; BOAVENTURA, Juliana Maria Capelozza; de BRITO-GONÇALVES, Joel; RASTELLI, Alessandra Nara de Souza; BAGNATO, Vanderlei Salvador; SAAD, José Roberto Cury

2012-01-01

Objective This study aimed at evaluating the degree of conversion (DC) of four composite resins, being one nanofilled and 3 microhybrid resins, photo-activated with second- and third-generation light-emitting diodes (LEDs). Material and methods FiltekTM Z350 nanofilled composite resins and Amelogen® Plus, Vit-l-escenceTM and Opallis microhybrid resins were photo-activated with two second-generation LEDs (Radii-cal and Elipar Free LightTM 2) and one third-generation LED (Ultra-Lume LED 5) by continuous light mode, and a quartz halogen-tungsten bulb (QHT, control). After 24 h of storage, the samples were pulverized into fine powder and 5 mg of each material were mixed with 100 mg of potassium bromide (KBr). After homogenization, they were pressed, which resulted in a pellet that was evaluated using an infrared spectromer (Nexus 470, Thermo Nicolet) equipped with TGS detector using diffuse reflectance (32 scans, resolution of 4 cm-1) coupled to a computer. The percentage of unreacted carbon-carbon double bonds (% C=C) was determined from the ratio of absorbance intensities of aliphatic C=C (peak at 1637 cm-1) against internal standard before and after curing of the specimen: aromatic C-C (peak at 1610 cm-1). Results The ANOVA showed a significant effect on the interaction between the light-curing units (LCUs) and the composite resins (p<0.001). The Tukey's test showed that the nanofilled resin (FiltekTM Z350) and Opallis when photo-activated by the halogen lamp (QTH) had the lowest DC compared with the other microhybrid composite resins. The DC of the nanofilled resin (FiltekTM Z350) was also lower using LEDs. The highest degrees of conversion were obtained using the third-generation LED and one of second-generation LEDs (Elipar Free LightTM 2). Conclusions The nanofilled resin showed the lowest DC, and the Vit-l-escenceTM microhybrid composite resin showed the highest DC. Among the LCUs, it was not possible to establish an order, even though the second-generation LED Radii-cal provided the lowest DC. PMID:22666839

Epoxy Resin Composite Based on Functional Hybrid Fillers

PubMed Central

Oleksy, Mariusz; Szwarc-Rzepka, Karolina; Heneczkowski, Maciej; Oliwa, Rafał; Jesionowski, Teofil

2014-01-01

A study was carried out involving the filling of epoxy resin (EP) with bentonites and silica modified with polyhedral oligomeric silsesquioxane (POSS). The method of homogenization and the type of filler affect the functional and canceling properties of the composites was determined. The filler content ranged from 1.5% to 4.5% by mass. The basic mechanical properties of the hybrid composites were found to improve, and, in particular, there was an increase in tensile strength by 44%, and in Charpy impact strength by 93%. The developed hybrid composites had characteristics typical of polymer nanocomposites modified by clays, with a fine plate morphology of brittle fractures observed by SEM, absence of a plate separation peak in Wide Angles X-ray Scattering (WAXS) curves, and an exfoliated structure observed by TEM. PMID:28788177

Finite Element Simulation of Compression Molding of Woven Fabric Carbon Fiber/Epoxy Composites: Part I Material Model Development

DOE PAGES

Li, Yang; Zhao, Qiangsheng; Mirdamadi, Mansour; ...

2016-01-06

Woven fabric carbon fiber/epoxy composites made through compression molding are one of the promising choices of material for the vehicle light-weighting strategy. Previous studies have shown that the processing conditions can have substantial influence on the performance of this type of the material. Therefore the optimization of the compression molding process is of great importance to the manufacturing practice. An efficient way to achieve the optimized design of this process would be through conducting finite element (FE) simulations of compression molding for woven fabric carbon fiber/epoxy composites. However, performing such simulation remains a challenging task for FE as multiple typesmore » of physics are involved during the compression molding process, including the epoxy resin curing and the complex mechanical behavior of woven fabric structure. In the present study, the FE simulation of the compression molding process of resin based woven fabric composites at continuum level is conducted, which is enabled by the implementation of an integrated material modeling methodology in LS-Dyna. Specifically, the chemo-thermo-mechanical problem of compression molding is solved through the coupling of three material models, i.e., one thermal model for temperature history in the resin, one mechanical model to update the curing-dependent properties of the resin and another mechanical model to simulate the behavior of the woven fabric composites. Preliminary simulations of the carbon fiber/epoxy woven fabric composites in LS-Dyna are presented as a demonstration, while validations and models with real part geometry are planned in the future work.« less

The effect of home bleaching agents on the surface roughness of five different composite resins: A SEM evaluation.

PubMed

Cengiz, Esra; Kurtulmus-Yilmaz, Sevcan; Ulusoy, Nuran; Deniz, Sule Tugba; Yuksel-Devrim, Ece

2016-05-01

The aim of this study was to investigate the effect of hydrogen peroxide (HP) and carbamide peroxide (CP) on the surface roughness of five different composite resins using profilometer and scanning electron microscope (SEM). Thirty-six specimens (1 mm thick, 10 mm in diameter) of five composite resins were fabricated. Each composite group was equally divided into three subgroups as control, CP and HP. In control group, specimens were stored in daily refreshed distilled water during the 14-day testing period. In other groups, 10% HP (Opalescence Treswhite) and 10% CP (Opalescence PF) were applied and surface roughness values (Ra) of each specimen were measured with a profilometer at the end of 14 days. Additionally, SEM analysis was performed to evaluate the surface deformations of composite resins. Data were analyzed with Kruskal-Wallis and Mann-Whitney U tests. Ra values of composite groups exposed to bleaching agents were statistically higher than control group (p < 0.05). There was no significant difference between Ra values after HP and CP application within each composite group while SEM micrographs showed higher surface alterations at HP group compared to CP. Among the composite resins tested, Ceram-X Mono revealed the lowest Ra values after CP and HP applications as seen at SEM images. Home bleaching agents increased the surface roughness of all composites. Except CP applied Ceram-X mono specimens, Ra values of all composite resins evaluated in this study exceeded the critical limit of 0.2 μm. Ceram-X mono was the least affected composite material after bleaching application. SCANNING 38:277-283, 2016. © 2016 Wiley Periodicals, Inc. © Wiley Periodicals, Inc.

Comparison of stabilities in translucency, fluorescence and opalescence of direct and indirect composite resins.

PubMed

Yu, Bin; Lee, Young-Keun

2013-01-01

To evaluate translucency, fluorescence and opalescence stabilities of direct and indirect composite resins after aging. One direct (16 shades) and two indirect composite resins (16 and 26 shades) were investigated. Resins were filled in a mold (1 mm thick) and light cured; post-curings were performed for indirect resins. Color was measured before and after 5,000 cycles of thermocycling on a reflection spectrophotometer in reflectance and transmittance modes to calculate parameters for translucency (TP), fluorescence (FL) and opalescence (OP). Differences in the changes of TP, FL and OP after aging by the type of resin were determined by t test, and those were also determined by one-way ANOVA with the factor of the brand or the shade group (P < 0.05). Changes in TP, FL and OP were -1.2 to 0.7, -0.2 to 0.4 and -0.6 to 1.3, respectively, for direct resins; and were -2.0 to 1.8, -0.9 to 0.4 and -2.9 to 3.7, respectively, for indirect resins. Changes in TP were not significantly different by the type of resin, but those in FL and OP were different (P = 0.05). Changes in optical parameters were influenced by the brand or the shade group of the resins (P < 0.05). Stabilities in optical properties of resins varied depending on type, brand or shade group. Aging significantly affected fluorescence and opalescence, but not translucency, of indirect resins compared to those of direct resins.

Bio-Based Nanocomposites: An Alternative to Traditional Composites

ERIC Educational Resources Information Center

Tate, Jitendra S.; Akinola, Adekunle T.; Kabakov, Dmitri

2009-01-01

Polymer matrix composites (PMC), often referred to as fiber reinforced plastics (FRP), consist of fiber reinforcement (E-glass, S2-glass, aramid, carbon, or natural fibers) and polymer matrix/resin (polyester, vinyl ester, polyurethane, phenolic, and epoxies). Eglass/ polyester and E-glass/vinyl ester composites are extensively used in the marine,…

Lignin-based monomers: Utilization in high-performance polymers and the effects of their structures on polymer properties

NASA Astrophysics Data System (ADS)

Stanzione, Joseph F., III

With the uncertainty of petroleum reserves and future crude oil prices, lignocellulosic biomass is becoming an increasingly valuable resource for the sustainable development of fuels, chemicals, and materials, including vinyl ester resins (VERs). Petroleum-based VERs are used to produce polymer composites for a wide variety of commercial applications. Although possessing relatively high moduli, strengths, and glass transition temperatures, commercial VERs typically contain high concentrations of a reactive diluent, such as styrene. However, these reactive diluents are often considered hazardous air pollutants (HAPs), volatile organic compounds (VOCs), and anticipated carcinogens. Moreover, bisphenol-A, which has gained considerable attention due to potential associated health-related issues, is utilized as a precursor in the synthesis of VERs. A green chemistry and engineering approach in the development of new VERs and renewable reactive diluents that are based on lignin is presented in this dissertation. Lignin, which is currently an abundant, renewable waste product of the paper and pulping industry, is primarily burned as a low value fuel. However, lignin has the potential to be a low cost feedstock in future lignocellulosic biorefineries that could yield highly valuable aromatic chemicals (lignin model compounds, LMCs) when strategically depolymerized. The incorporation of aromaticity in a resin's chemical structure is known to improve overall polymer composite performance and the high aromatic content found in lignin is ideal for novel resin development. Highlighted in this dissertation are three projects: (1) the synthesis and characterization of a lignin-based bio-oil resin/reactive diluent, (2) the use of functionalized LMCs as styrene replacements in VERs, and (3) the synthesis and characterization of a vanillin-based resin. Through the use of traditional and new polymer theory coupled with spectroscopic, thermal, and mechanical techniques, structure-property relationships are identified and related to polymer performance. These findings have important implications for the optimization and design of polymer composites that are based on sustainable resources and processes, are petroleum-independent, and have reduced toxicity with beneficial environmental impacts. In addition, these findings provide the incentive for continued investment in using lignin as a respected materials' feedstock. Lastly, several lignin-related research opportunities of scientific and commercial interest are recommended.

Analytical method for dissolved-organic carbon fractionation

USGS Publications Warehouse

Leenheer, Jerry A.; Huffman, Edward W. D.

1979-01-01

A standard procedure for analytical-scale dissolved organic carbon fractionation is presented, whereby dissolved organic carbon in water is first fractionated by a nonionic macroreticular resin into acid, base, and neutral hydrophobic organic solute fractions, and next fractionated by ion-exchange resins into acid, base, and neutral hydrophilic solute fractions. The hydrophobic solutes are defined as those sorbed on a nonionic, acrylic-ester macroreticular resin and are differentiated into acid, base, and nautral fractions by sorption/desorption controlled by pH adjustment. The hydrophilic bases are next sorbed on strong-acid ion-exchange resin, followed by sorption of hydrophilic acids on a strong-base ion-exchange resin. Hydrophilic neutrals are not sorbed and remain dissolved in the deionized water at the end of the fractionation procedure. The complete fractionation can be performed on a 200-milliliter filtered water sample, whose dissolved organic carbon content is 5-25 mg/L and whose specific conductance is less than 2,000 μmhos/cm at 25°C. The applications of dissolved organic carbon fractionation analysis range from field studies of changes of organic solute composition with synthetic fossil fuel production, to fundamental studies of the nature of sorption processes.

Low-Cost Resin Transfer Molding Process Developed for High-Temperature Polyimide Matrix Composites

NASA Technical Reports Server (NTRS)

1996-01-01

The use of high-temperature polymer matrix composites (PMC's) in aircraft engine applications can significantly reduce engine weight and improve performance and fuel efficiency. High-temperature PMC's, such as those based on the PMR-15 polyimide matrix resin developed by the NASA Lewis Research Center, have been used extensively in military applications where performance improvements have justified their use regardless of the cost involved in producing the component. However, in commercial engines cost is a primary driver, and PMC components must be produced at costs comparable to those of the metal components that they will replace.

Assessment of microleakage of class V restored by resin composite and resin-modified glass ionomer and pit and fissure resin-based sealants following Er:YAG laser conditioning and acid etching: in vitro study

PubMed Central

Luong, Emilie; Shayegan, Amir

2018-01-01

Aim The aim of this study was to make a comparison between microleakage of conventionally restored class V cavities using acid etchant and the ones conditioned by erbium-doped yttrium aluminum garnet (Er:YAG) laser, and also to assess and compare the effectiveness of enamel surface treatments of occlusal pits and fissures by acid etching and conditioned by Er:YAG laser-etch. Materials and methods Seventy-two extracted third molars were used in this study. The samples were divided into two major groups: class V cavities and pit and fissure sealants. Each subgroup was divided into conventional acid etching, Er:YAG laser conditioning and conventional acid etching, and combination with Er:YAG laser conditioning (n=12). The teeth were placed in 2% methylene blue dye solution, were sectioned, and were evaluated according to the dye penetration criteria. Two samples per subgroup were chosen for scanning electron microscopic (SEM) analysis. Results There was a significant difference between occlusal and cervical margin groups. Laser conventional composite cementum group showed more microleakage values compared to other groups. There was no significant difference between occlusal margin groups. However, there was a significant difference between cervical margin groups in terms of microleakage. In sealant groups, there was a significant difference between laser and conventional with/without laser treatment groups in terms of microleakage. Conclusion Based on the results reported in this study, it can be concluded that the application of the Er:YAG laser beneath the resin composite, the resin-modified glass ionomers (GIs), and the fissure sealant placement may be an alternative enamel and dentin etching method to acid etching. PMID:29881311

Shelf Life of PMR Polyimide Monomer Solutions and Prepregs Extended

NASA Technical Reports Server (NTRS)

Alston, William B.; Scheiman, Daniel A.

2000-01-01

PMR (Polymerization of Monomeric Reactants) technology was developed in the mid-1970's at the NASA Glenn Research Center at Lewis Field for fabricating high-temperature stable polyimide composites. This technology allowed a solution of polyimide monomers or prepreg (a fiber, such as glass or graphite, impregnated with PMR polyimide monomers) to be thermally cured without the release of volatiles that cause the formation of voids unlike the non-PMR technology used for polyimide condensation type resins. The initial PMR resin introduced as PMR 15 is still commercially available and is used worldwide by aerospace industries as the state-of-the-art resin for high-temperature polyimide composite applications. PMR 15 offers easy composite processing, excellent composite mechanical property retention, a long lifetime at use temperatures of 500 to 550 F, and relatively low cost. Later, second-generation PMR resin versions, such as PMR II 50 and VCAP 75, offer improvements in the upper-use temperature (to 700 F) and in the useful life at temperature without major compromises in processing and property retention but with significant increases in resin cost. Newer versions of nontoxic (non-methylene dianiline) PMR resins, such as BAX PMR 15, offer similar advantages as originally found for PMR 15 but also with significant increases in resin cost. Thus, the current scope of the entire PMR technology available meets a wide range of aeronautical requirements for polymer composite applications.

Evaluation of tensile retention of Y-TZP crowns cemented on resin composite cores: effect of the cement and Y-TZP surface conditioning.

PubMed

Rippe, M P; Amaral, R; Oliveira, F S; Cesar, P F; Scotti, R; Valandro, L F; Bottino, M A

2015-01-01

This study evaluated the effect of the cement type (adhesive resin, self-adhesive, glass ionomer, and zinc phosphate) on the retention of crowns made of yttria-stabilized polycrystalline tetragonal zirconia (Y-TZP). Therefore, 108 freshly extracted molars were embedded in acrylic resin, perpendicular to their long axis, and prepared for full crowns: the crown preparations were removed and reconstructed using composite resin plus fiber posts with dimensions identical to the prepared dentin. The preparations were impressed using addition silicone, and Y-TZP copings were produced, which presented a special setup for the tensile testing. Cementation was performed with two adhesive resin cements (Multilink Automix, Ivoclar-Vivadent; RelyX ARC, 3M ESPE, St Paul, MN, USA), one self-adhesive resin cement (RelyX U100, 3M ESPE), one glass ionomer based cement (RelyX Luting, 3M ESPE), and one zinc phosphate cement (Cimento de Zinco, SS White, Rio de Janeiro, Brazil). For the resin cement groups, the inner surfaces of the crowns were subjected to three surface treatments: cleaning with isopropyl alcohol, tribochemical silica coating, or application of a thin low-fusing glass porcelain layer plus silanization. After 24 hours, all groups were subjected to thermocycling (6000 cycles) and included in a special device for tensile testing in a universal testing machine to test the retention of the infrastructure. After testing, the failure modes of all samples were analyzed under a stereomicroscope. The Kruskal-Wallis test showed that the surface treatment and cement type (α=0.05) affected the tensile retention results. The Multilink cement presented the highest tensile retention values, but that result was not statistically different from RelyX ARC. The surface treatment was statistically relevant only for the Multilink cement. The cement choice was shown to be more important than the crown surface treatment for cementation of a Y-TZP crown to a composite resin substrate.

Asphaltenes-based polymer nano-composites

DOEpatents

Bowen, III, Daniel E

2013-12-17

Inventive composite materials are provided. The composite is preferably a nano-composite, and comprises an asphaltene, or a mixture of asphaltenes, blended with a polymer. The polymer can be any polymer in need of altered properties, including those selected from the group consisting of epoxies, acrylics, urethanes, silicones, cyanoacrylates, vulcanized rubber, phenol-formaldehyde, melamine-formaldehyde, urea-formaldehyde, imides, esters, cyanate esters, allyl resins.

Adhesive strength of paint-on resins to crown and bridge composites.

PubMed

Kanie, Takahito; Arikawa, Hiroyuki; Fujii, Koichi; Ban, Seiji

2004-12-01

This paper examined the adhesive strength of paint-on resin to crown and bridge composites after soaking in water and thermal-cycling. Three shades of paint-on resin were coated on three kinds of crown and bridge composite under four surface treatment conditions (a combination of sandblaster and pretreatment liquid). These specimens were soaked in water at 37 degrees C for 1 day, 1 month, and 1 year, and at 4 degrees C and 60 degrees C alternatively for 1-minute periods for 10,000 cycles by thermal-cycling machine. The adhesive strengths were obtained by shear test. There were no significant differences among the adhesive strengths of three shades of paint-on resin to three composites after storage (p > 0.05). The adhesive strengths to composites with sandblasting showed higher values than those without it (p < 0.01).

Advanced Thermoplastic Resins for Manufacturing Wind Turbine Blades |

Science.gov Websites

Turbine Blades Advanced Thermoplastic Resins for Manufacturing Wind Turbine Blades At its Composites Arkema's Elium liquid thermoplastic resin. Photo of men working on turbine blades in a dome-shaped building composite structures of wind turbine blades. Capabilities Learn more about NREL's IACMI projects and its

Thermal Expansion and Swelling of Cured Epoxy Resin Used in Graphite/Epoxy Composite

NASA Technical Reports Server (NTRS)

Adamson, M. J.

1979-01-01

The thermal expansion and swelling of resin material as influenced by variations in temperature during moisture absorption is discussed. Comparison measurements using composites constructed of graphite fibers and each of two epoxy resin matrices are included. Polymer theory relative to these findings is discussed and modifications are proposed.

Three-body wear of resin denture teeth with and without nanofillers.

PubMed

Stober, Thomas; Henninger, Moritz; Schmitter, Marc; Pritsch, Maria; Rammelsberg, Peter

2010-02-01

The wear behavior of newly developed denture teeth with nanofillers may be different from teeth with other chemical formulations. The purpose of this study was to examine the 3-body wear resistance of 11 different commercially available resin denture teeth. The materials tested were conventional (SR Orthotyp PE, Orthognath) and cross-linked acrylic resin teeth without inorganic fillers (Premium 8, SR Postaris DCL, Trubyte Portrait, Artiplus), composite resin teeth with inorganic fillers (SR Orthosit PE, Vitapan), and composite resin teeth (experimental materials) with inorganic nanofillers (NC Veracia Posterior, e-Ha, Mondial). Human enamel and a ceramic denture tooth (Lumin Vacuum) were used as reference materials. The 3-body wear test was performed in a wear machine developed by the Academic Center for Dentistry Amsterdam (ACTA), with millet suspension acting as an abrasive medium (n=10, test load: 15 N, slip rate: 20%, number of cycles: 100,000). Wear was determined with the aid of a profilometer. Data were analyzed with the Kruskal-Wallis test and Mann-Whitney U test using the closed testing approach (significance level for familywise error rate, alpha=.05). None of the acrylic and composite resin materials tested in this study demonstrated the 3-body wear resistance of ceramic teeth or human enamel. Teeth with inorganic fillers demonstrated significantly lower wear values than conventional or cross-linked acrylic resin teeth without fillers. Composite resin teeth with traditional fillers showed significantly lower wear than composite resin teeth with nanofillers. Denture teeth with and without inorganic fillers differed significantly with regard to the degree of wear generated in the ACTA wear simulator. The incorporation of nanofillers did not improve the wear resistance compared to teeth with traditional fillers.

Recyclable epoxy resins: An example of green approach for advanced composite applications

NASA Astrophysics Data System (ADS)

Cicala, Gianluca; Rosa, Daniela La; Musarra, Marco; Saccullo, Giuseppe; Banatao, Rey; Pastine, Stefan

2016-05-01

Automotive composite applications are increasingly growing due to demand for lightweight structures to comply to the requirements for fuel reduction. HP-RTM is gaining relevance as one of the preferred production technologies for high volume applications. The BMW i3 life module being a notable example of HP-RTM application. The key aspects of HP-RTM are the short injection times (i.e. less than 1min) and the fast curing of the thermoset resins (i.e. less than 10min). The choice of using thermosets poses relevant issues for their limited recycling options. The standard recycling solution is the incineration but, this solution poses some concerns in terms of global environmental impact. Novel solutions are presented in this work based on the use of recyclable epoxy systems. In our work the results of experimentation carried out by our group with cleavable ammines by Connora Technologies and bioepoxy resins by Entropy Resins will be discussed. The multiple uses of recycled matrices obtained treating the recyclable epoxy resins are discussed in the framework of a "cradle" to "crave" approach. Finally, Life Cycle Assessment (LCA) is used to evaluate the environmental benefits of the proposed approach.

Develop and demonstrate manufacturing processes for fabricating graphite filament reinforced polymide (Gr/PI) composite structural elements

NASA Technical Reports Server (NTRS)

Chase, V. A.; Harrison, E. S.

1985-01-01

A study was conducted to assess the merits of using graphite/polyimide, NR-150B2 resin, for structural applications on advanced space launch vehicles. The program was divided into two phases: (1) Fabrication Process Development; and (2) Demonstration Components. The first phase of the program involved the selection of a graphite fiber, quality assurance of the NR-150B2 polyimide resin, and the quality assurance of the graphite/polyimide prepreg. In the second phase of the program, a limited number of components were fabricated before the NR-150B2 resin system was removed from the market by the supplier, Du Pont. The advancement of the NR-150B2 polyimide resin binder was found to vary significantly based on previous time and temperature history during the prepregging operation. Strength retention at 316C (600F) was found to be 50% that of room temperature strength. However, the composite would retain its initial strength after 200 hours exposure at 316C (600F). Basic chemistry studies are required for determining NR-150B2 resin binder quality assurance parameters. Graphite fibers are available that can withstand high temperature cure and postcure cycles.

Preparation and Electrochemical Properties of Graphene/Epoxy Resin Composite Coating

NASA Astrophysics Data System (ADS)

Liao, Zijun; Zhang, Tianchi; Qiao, Sen; Zhang, Luyihang

2017-11-01

The multilayer graphene powder as filler, epoxy modified silicone resin as film-forming agent, anticorrosion composite coating has been created using sand dispersion method, the electrochemical performance was compared with different content of graphene composite coating and pure epoxy resin coating. The open circuit potential (OCP), potentiodynamic polarization curves (Tafel Plot) and electrochemical impedance spectroscopy (EIS) were tested. The test results showed that the anti-corrosion performance of multilayer graphene added has improved greatly, and the content of the 5% best corrosion performance of graphene composite coating.

Nonlinear DC Conduction Behavior in Graphene Nanoplatelets/Epoxy Resin Composites

NASA Astrophysics Data System (ADS)

Yuan, Yang; Wang, Qingguo; Qu, Zhaoming

2018-01-01

Graphene nanoplatelets (GNPs)/Epoxy resin (ER) with a low percolation threshold were fabricated. Then the nonlinear DC conduction behavior of GNPs/ER composites was investigated, which indicates that dispersion, exfoliation level and conductivity of GNPs in specimens are closely related to the conduction of composites. Moreover, it could be seen that the modified graphene nanoplatelets made in this paper could be successfully used for increasing the electric conductivity of the epoxy resin, and the GNPs/ER composites with nonlinear conduction behavior have a good application prospects in the field of intelligent electromagnetic protection.

Tensile and thickness swelling properties of strands from Southern hardwoods and Southern pine : effect of hot-pressing and resin application

Treesearch

Zhiyong Cai; Qinglin Wu; Guangping Han; Jong N. Lee

2007-01-01

Tensile and the moisture-induced thickness swelling properties of wood strands are among the most fundamental parameters in modeling and predicting engineering constants of strand-based composites such as oriented strandboard (OSB). The effects of hot-pressing and resin-curing on individual strand properties were investigated in this study. Strands from four Louisiana-...

Restorative dentistry for children.

PubMed

Donly, Kevin J

2013-01-01

This article discusses contemporary pediatric restorative dentistry. Indications and contraindications for the choice of different restorative materials in different clinical situations, including the risk assessment of the patient, are presented. The specific use of glass ionomer cement or resin-modified glass ionomer cement, resin-based composite, and stainless steel crowns is discussed so that preparation design and restoration placement is understood. Copyright © 2013 Elsevier Inc. All rights reserved.

Effects of Composites Containing Bioactive Glasses on Demineralized Dentin.

PubMed

Tezvergil-Mutluay, A; Seseogullari-Dirihan, R; Feitosa, V P; Cama, G; Brauer, D S; Sauro, S

2017-08-01

The aim of this study was to evaluate the degradation of completely demineralized dentin specimens in contact with a filler-free or 2 ion-releasing resins containing micrometer-sized particles of Bioglass 45S5 (BAG) or fluoride-containing phosphate-rich bioactive glass (BAG-F). Fourier transform infrared spectroscopy (FTIR) and scanning electron microscopy (SEM) were also used to evaluate the remineralization induced by the experimental ion-releasing resin-based materials. Dentin beams were totally demineralized in H 3 PO 4 (10%) and placed in direct contact with a filler-free (RESIN) or 2 experimental ion-releasing resins (BAG or BAG-F) and immersed in artificial saliva (AS) up to 30 d. Further specimens were also processed and submitted to FTIR and SEM analysis to evaluate the remineralization induced by such ion-releasing resins before and after AS immersion. BAG and BAG-F alkalinized the incubation media. A significant decrease of the dry mass was observed between the specimens of all groups stored for 3 and 30 d in AS. However, the fluoride-containing phosphate-rich bioactive glass incorporated into a resin-based material (BAG-F) showed greater ability in reducing the solubilization of C-terminal cross-linked telopeptide (ICTP) and C-terminal telopeptide (CTX) after prolonged AS storage. Moreover, after 30 d of AS storage, BAG-F showed the greatest remineralizing effect on the stiffness of the completely demineralized dentin matrices. In conclusion, fluoride-containing phosphate-rich bioactive glass incorporated as micrometer-sized filler in dental composites may offer greater beneficial effects than Bioglass 45S5 in reducing the enzyme-mediated degradation and remineralization of demineralized dentin.

Modern high powered led curing lights and their effect on pulp chamber temperature of bulk and incrementally cured composite resin.

PubMed

Oberholzer, T G; Makofane, M E; du Preez, I C; George, R

2012-06-01

Pulpal temperature changes induced by modern high powered light emitting diodes (LEDs) are of concern when used to cure composite resins. This study showed an increase in pulp chamber temperature with an increase in power density for all light cure units (LCU) when used to bulk cure composite resin. Amongst the three LEDs tested, the Elipar Freelight-2 recorded the highest temperature changes. Bulk curing recorded a significantly larger rise in pulp chamber temperature change than incrementally cured resin for all light types except for the Smartligh PS. Both the high powered LED and the conventional curing units can generate heat. Though this temperature rise may not be sufficient to cause irreversible pulpal damage, it would be safer to incrementally cure resins.

A 15-year randomized controlled study of a reduced shrinkage stress resin composite.

PubMed

van Dijken, Jan W V; Lindberg, Anders

2015-09-01

The aim of this randomized controlled study was to evaluate the long term effectiveness of a reduced shrinkage stress resin composite in Class II restorations. The material was compared intra-individually with a microhybrid resin composite. Each of 50 patients with at least one pair of two similar sized Class II cavities participated (22 female, 28 male, mean age 43 years, range 18-64). Each participant received in each pair, in a randomized way, one Class II restoration performed with a reduced shrinkage stress resin composite (InTen-S) and the other restoration with a microhybrid resin composite restoration (Point 4). Both restorations were placed with an etch-and-rinse bonding system and an oblique layering technique. A total of 106 restorations, 33 premolar and 73 molars, were placed. The restorations were evaluated blindly each year using modified USPHS criteria. The overall performance of the experimental restorations was tested after intra-individual comparison using the Friedmańs two-way analysis of variance test. The hypothesis was rejected at the 5% level. At 15 years, 91 restorations were evaluated. The drop out frequency was 15 restorations (5 male, 3 female participants; 2 premolar and 13 molar restorations). Except for 2 participants, who reported slight symptoms during a few weeks after placement, no post-operative sensitivity was observed at the recalls. The overall success rate at 15 years was 77%. Twenty-one non acceptable restorations were observed during the 15 years follow up, 10 InTen-S (21.7%) and 11 Point 4 (24.4%) restorations (p>0.05). Annual failure rates for the resin composites were 1.5% and 1.6%, respectively. The main reasons for failure were secondary caries (8) and resin composite fracture (7). The differences between premolar vs. molar restorations and between restorations in male vs. female participants were not significant. Significant differences were observed between 2-surface vs. 3-surface restorations. During the 15-year follow up, the reduced shrinkage stress resin composite showed a good clinical durability in Class II cavities, but not significantly better than the control microhybrid resin composite. Secondary caries and material fracture were the main reasons of failure. Copyright © 2015 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Interpretation of Mechanical and Thermal Properties of Heavy Duty Epoxy Based Floor Coating Doped by Nanosilica

NASA Astrophysics Data System (ADS)

Nikje, M. M. Alavi; Khanmohammadi, M.; Garmarudi, A. Bagheri

Epoxy-nano silica composites were prepared using Bisphenol-A epoxy resin (Araldite® GY 6010) resin obtained from in situ polymerization or blending method. SiO2 nanoparticles were pretreated by a silan based coupling agent. Surface treated nano silica was dispersed excellently by mechanical and ultrasonic homogenizers. A dramatic increase in the interfacial area between fillers and polymer can significantly improve the properties of the epoxy coating product such as tensile, elongation, abrasion resistance, etc.

Bismaleimides and related maleimido polymers as matrix resins

NASA Technical Reports Server (NTRS)

Parker, J. A.; Kourtides, D. A.; Fohlen, G. M.

1985-01-01

Significant processing and property improvements can be achieved by copolymerization of state-of-the-art bisimides with various vinyl stilbazole derivatives to give both fire resistance and high-temperature properties from hot-melt compositions. Significant improvement in mechanical properties is achieved through these modifications, which may make these new matrix resins ideal candidates for fireworthy secondary graphite composite structures. Phosphorous modifications of maleimido polymers through phosphonate structure and tricyclophosphazene derivatives provide families of new matrix resins for short-time applications in severe thermo-oxidative environments. With further research these may provide matrix resins for long-term thermo-oxidative stability of advanced composites at temperatures up to 400 to 500 C.

Development of a novel resin-based dental material with dual biocidal modes and sustained release of Ag+ ions based on photocurable core-shell AgBr/cationic polymer nanocomposites.

PubMed

Cao, Weiwei; Zhang, Yu; Wang, Xi; Chen, Yinyan; Li, Qiang; Xing, Xiaodong; Xiao, Yuhong; Peng, Xuefeng; Ye, Zhiwen

2017-07-01

Research on the incorporation of cutting-edge nano-antibacterial agent for designing dental materials with potent and long-lasting antibacterial property is demanding and provoking work. In this study, a novel resin-based dental material containing photocurable core-shell AgBr/cationic polymer nanocomposite (AgBr/BHPVP) was designed and developed. The shell of polymerizable cationic polymer not only provided non-releasing antibacterial capability for dental resins, but also had the potential to polymerize with other methacrylate monomers and prevented nanoparticles from aggregating in the resin matrix. As a result, incorporation of AgBr/BHPVP nanocomposites did not adversely affect the flexural strength and modulus but greatly increased the Vicker's hardness of resin disks. By continuing to release Ag + ions without the impact of anaerobic environment, resins containing AgBr/BHPVP nanoparticles are particularly suitable to combat anaerobic cariogenic bacteria. By reason of the combined bactericidal effect of the contact-killing cationic polymers and the releasing-killing Ag + ions, AgBr/BHPVP-containing resin disks had potent bactericidal activity against S. mutans. The long-lasting antibacterial activity was also achieved through the sustained release of Ag + ions due to the core-shell structure of the nanocomposites. The results of macrophage cytotoxicity showed that the cell viability of dental resins loading less than 1.0 wt% AgBr/BHPVP was close to that of neat resins. The AgBr/BHPVP-containing dental resin with dual bactericidal capability and long term antimicrobial effect is a promising material aimed at preventing second caries and prolonging the longevity of resin composite restorations.

Influence of polymerization time and depth of cure of resin composites determined by Vickers hardness.

PubMed

Lombardini, Marco; Chiesa, Marco; Scribante, Andrea; Colombo, Marco; Poggio, Claudio

2012-11-01

Adequate polymerization of resin composites could be considered as a crucial factor in obtaining good clinical performance, particularly in stress-bearing areas. An insufficient curing degree affects the resin composite's chemical properties The current in vitro study evaluated the influence of polymerization time and depth of cure of six commercial resin composites by Vickers microhardness (VK). SIX RESIN COMPOSITES WERE SELECTED: Three microhybrid (Esthet.X HD, Amaris, Filtek Silorane), two nanohybrid (Grandio, Ceram.X mono), and one nanofilled (Filtek Supreme XT). The VK of the surface was determined by a microhardness tester using a Vickers diamond indenter and a 200 g load applied for 15 s. The bottom to top mean VK ratio was calculated using the formula: Hardness ratio = VK of bottom surface/VK of top surface. Vickers hardness values of test materials during exposure time of 20 and 40 s and depths of cure of 2 and 3 mm were determined and compared. Data were analyzed using analysis of variance (ANOVA) test. For all the tested materials and with all the exposure time periods, hardness ratio was higher than the minimum value indicated in literature (0.8). Exposure time and depth of cure did not affect hardness ratio values for Filtek Silorane, Grandio, and Filtek Supreme XT. Among the materials tested, the nanofilled and the nanohybrid resin composites were rather insensible to thickness variations. Miicrohybrid composites, instead, had features different from one another.

Effect of light-curing units on microleakage under dental composite resins

NASA Astrophysics Data System (ADS)

Queiroz, R. S.; Bandéca, M. C.; Calixto, L. R.; Saade, E. G.; Nadalin, M. R.; Andrade, M. F.; Porto-Neto, S. T.

2009-09-01

The aim of this study was to determine the effect of two light-curing units (QTH and LED) on microleakage of Class II composite resin restorations with dentin cavosurface margins. Twenty extracted mandibular first premolars, free of caries and fractures were prepared two vertical “slot” cavities in the occluso-mesial and -destal surfaces (2 mm buccal-lingually, 2 mm proximal-axially and cervical limit in enamel) and divided into 4 equal groups ( n = 8): GI and GII: packable posterior composite light-activated with LED and QTH, respectively; GIII and GIV: micro-hybrid composite resin light-activated with LED and QTH, respectively. The composite resins were applied following the manufacturer’s instructions. After 24 h of water storage specimens were subjected to thermocycling for a total of 500 cycles at 5 and 55°C and the teeth were then sealed with impermeable material. Teeth were immersed in 0.5% Basic fuchsin during 24 h at room temperature, and zero to three levels of penetration score were attributed. The Mann-Whitney and Kruskal-Wallis tests showed significant statistically similar ( P > 0.05) from GI to GII and GIII to GIV, which the GII (2.750) had the highest mean scores and the GIII and GIV (0.875) had lowest mean scores. The use of different light-curing units has no influence on marginal integrity of Class II composite resin restorations and the proprieties of composite resins are important to reduce the microleakage.

Fabrication and evaluation of Bis-GMA/TEGDMA dental resins/composites containing halloysite nanotubes

PubMed Central

Chen, Qi; Zhao, Yong; Wu, Weidong; Xu, Tao; Fong, Hao

2012-01-01

Objective To investigate the reinforcement of Bis-GMA/TEGDMA dental resins (without conventional glass filler) and the corresponding composites (with conventional glass filler)containing vari ed mass fractions of halloysite nanotubes (HNTs). Methods Three dispersion methods were studied to separate the silanized halloysite as individual HNTs and to uniformly distribute them into dental matrices. Photopolymerization induced volumetric shrinkage was measured by using a mercury dilatometer. Real time near infrared spectroscopy was adopted to study the degree of vinyl double bond conversion and the photopolymerization rate. Mechanical properties of the composites were tested by a universal mechanical testing machine. Analysis of Variance (ANOVA) was used for the statistical analysis of the acquired data. Morphologies of halloysite/HNTs and representative fracture surfaces of the reinforced dental resins/composites were examined by SEM and TEM. Results Impregnation of small mass fractions (e.g., 1% and 2.5%) of the silanized HNTs in Bis-GMA/TEGDMA dental resins/composites improved mechanical properties significantly; however; large mass fractions (e.g., 5%) of impregnation did not further improve the mechanical properties. The impregnation of HNTs into dental resins/composites could result in two opposite effects: the reinforcing effect due to the highly separated and uniformly distributed HNTs, and the weakening effect due to the formation of HNT agglomerates/particles. Significance Uniform distribution of a small amount of well-separated silanized HNTs into Bis-GMA/TEGDMA dental resins/composites could result in substantial improvements on mechanical properties. PMID:22796038

Fabrication and evaluation of Bis-GMA/TEGDMA dental resins/composites containing halloysite nanotubes.

PubMed

Chen, Qi; Zhao, Yong; Wu, Weidong; Xu, Tao; Fong, Hao

2012-10-01

To investigate the reinforcement of Bis-GMA/TEGDMA dental resins (without conventional glass filler) and the corresponding composites (with conventional glass filler) containing varied mass fractions of halloysite nanotubes (HNTs). Three dispersion methods were studied to separate the silanized halloysite as individual HNTs and to uniformly distribute them into dental matrices. Photopolymerization induced volumetric shrinkage was measured by using a mercury dilatometer. Real time near infrared spectroscopy was adopted to study the degree of vinyl double bond conversion and the photopolymerization rate. Mechanical properties of the composites were tested by a universal mechanical testing machine. Analysis of variance (ANOVA) was used for the statistical analysis of the acquired data. Morphologies of halloysite/HNTs and representative fracture surfaces of the reinforced dental resins/composites were examined by SEM and TEM. Impregnation of small mass fractions (e.g., 1% and 2.5%) of the silanized HNTs in Bis-GMA/TEGDMA dental resins/composites improved mechanical properties significantly; however; large mass fractions (e.g., 5%) of impregnation did not further improve the mechanical properties. The impregnation of HNTs into dental resins/composites could result in two opposite effects: the reinforcing effect due to the highly separated and uniformly distributed HNTs, and the weakening effect due to the formation of HNT agglomerates/particles. Uniform distribution of a small amount of well-separated silanized HNTs into Bis-GMA/TEGDMA dental resins/composites could result in substantial improvements on mechanical properties. Copyright © 2012 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Effective Mechanical Properties of Fuzzy Fiber Composites

DTIC Science & Technology

2012-03-16

fibers’’. Numerical examples of compositesmade of epoxy resin , carbonfibers and carbon nanotubes are presented and the impact of the carbon nanotubes...allows us to compute effective properties of composites with multiple types of ??fuzzy fibers??. Numerical examples of composites made of epoxy resin ...length (Fig. 1 in [42]). The CNTs have inter- nal radius 0.51 nm and external radius 0.85 nm. The ‘‘fuzzy fibers’’ are embedded in EPIKOTE 862 resin . The

Effects of toothbrush hardness on in vitro wear and roughness of composite resins.

PubMed

Kyoizumi, Hideaki; Yamada, Junji; Suzuki, Toshimitsu; Kanehira, Masafumi; Finger, Werner J; Sasaki, Keiichi

2013-11-01

To investigate and compare the effects of toothbrushes with different hardness on abrasion and surface roughness of composite resins. Toothbrushes (DENT. EX Slimhead II 33, Lion Dental Products Co. Ltd., Tokyo, Japan) marked as soft, medium and hard, were used to brush 10 beam-shaped specimens of each of three composites resins (Venus [VEN], Venus Diamond [VED] and Venus Pearl [VEP]; HeraeusKulzer) with standardized calcium carbonate slurry in a multistation testing machine (2N load, 60 Hz). After each of five cycles with 10k brushing strokes the wear depth and surface roughness of the specimens were determined. After completion of 50k strokes representative samples were inspected by SEM. Data were treated with ANOVA and regression analyses (p < 0.05). Abrasion of the composite resins increased linearly with increasing number of brushing cycles (r² > 0.9). Highest wear was recorded for VEN, lowest for VED. Hard brushes produced significantly higher wear on VEN and VEP, whereas no difference in wear by toothbrush type was detected for VED. Significantly highest surface roughness was found on VED specimens (Ra > 1.5 µm), the lowest one on VEN (Ra < 0.3 µm). VEN specimens showed increased numbers of pinhole defects when brushed with hard toothbrushes, surfaces of VEP were uniformly abraded without level differences between the prepolymerized fillers and the glass filler-loaded matrix, VED showed large glass fillers protruding over the main filler-loaded matrix portion under each condition. Abrasion and surface roughness of composite resins produced by toothbrushing with dentifrice depend mainly on the type of restorative resin. Hardness grades of toothbrushes have minor effects only on abrasion and surface roughness of composite resins. No relationship was found between abrasion and surface roughness. The grade of the toothbrush used has minor effect on wear, texture and roughness of the composite resin.

The influence of ceramic surface treatments on the micro-shear bond strength of composite resin to IPS Empress 2.

PubMed

Panah, Faride Gerami; Rezai, Sosan Mir Mohammad; Ahmadian, Leila

2008-07-01

An increasing demand for esthetic restorations has resulted in the development of new ceramic systems, but fracture of veneering ceramics still remains the primary cause of failure. Porcelain repair frequently involves replacement with composite resin, but the bond strength between composite resin and all-ceramic coping materials has not been studied extensively. The purpose of this study was to evaluate the influence of different ceramic surface treatments on the micro-shear bond strength of composite resin to IPS Empress 2 coping material. Sixteen 7 x 7 x 1 mm(3) lithia disilicate-based core ceramic plates were fabricated using the lost wax technique. The plates were divided into eight groups, and eight different surface treatments were performed: (1) no treatment (NT); (2) airborne-particle abrasion with 50-mum alumina particles (Al); (3) acid etching with 9.6% hydrofluoric acid for 1 min (HF); (4) silane coating (S); (5) AlHF; (6) AlS; (7) HFS; and (8) AlHFS. Then, ten composite resin cylinders (0.8-mm diameter x 0.5-mm height) were light-polymerized onto the ceramic plates in each group. Each specimen was subjected to a shear load at a crosshead speed of 0.5 mm/min until fracture occurred. The fracture sites were examined with scanning electron microscopy (SEM) to determine the location of failure during debonding and to examine the surface treatment effects. One-way analysis of variance (ANOVA) and multiple comparison (Dunnet T3) tests were used for statistical analysis of data. The mean micro-shear bond strength values (SD) in MPa were--NT: 4.10 (3.06), Al: 7.56 (4.11), HF: 14.04 (2.60), S: 14.58 (2.14), AlHF: 15.56 (3.36), AlS: 23.02 (4.17), HFS: 24.7 (4.43), AlHFS: 26.0 (3.71). ANOVA indicated the influence of surface treatment was significant (p < 0.0001). SEM analysis did not reveal entirely cohesive failure in any composite or ceramic. The micro-shear bond strength of a composite resin to IPS Empress 2 was significantly different depending on the surface treatment method. Among the investigated methods, silane coating after airborne-particle abrasion and etching was the most effective surface treatment in terms of bond strength increase.

Can pulpal floor debonding be detected from occlusal surface displacement in composite restorations?

PubMed

Novaes, João Batista; Talma, Elissa; Las Casas, Estevam Barbosa; Aregawi, Wondwosen; Kolstad, Lauren Wickham; Mantell, Sue; Wang, Yan; Fok, Alex

2018-01-01

Polymerization shrinkage of resin composite restorations can cause debonding at the tooth-restoration interface. Theory based on the mechanics of materials predicts that debonding at the pulpal floor would half the shrinkage displacement at the occlusal surface. The aim of this study is to test this theory and to examine the possibility of detecting subsurface resin composite restoration debonding by measuring the superficial shrinkage displacements. A commercial dental resin composite with linear shrinkage strain of 0.8% was used to restore 2 groups of 5 model Class-II cavities (8-mm long, 4-mm wide and 4-mm deep) in aluminum blocks (8-mm thick, 10-mm wide and 14-mm tall). Group I had the restorations bonded to all cavity surfaces, while Group II had the restorations not bonded to the cavity floor to simulate debonding. One of the proximal surfaces of each specimen was sprayed with fine carbon powder to allow surface displacement measurement by Digital Image Correlation. Images of the speckled surface were taken before and after cure for displacement calculation. The experiment was simulated using finite element analysis (FEA) for comparison. Group I showed a maximum occlusal displacement of 34.7±6.7μm and a center of contraction (COC) near the pulpal floor. Group II had a COC coinciding with the geometric center and showed a maximum occlusal displacement of 17.4±3.8μm. The difference between the two groups was statistically significant (p-value=0.0007). Similar results were obtained by FEA. The theoretical shrinkage displacement was 44.6 and 22.3μm for Group I and II, respectively. The lower experimental displacements were probably caused by slumping of the resin composite before cure and deformation of the adhesive layer. The results confirmed that the occlusal shrinkage displacement of a resin composite restoration was reduced significantly by pulpal floor debonding. Recent in vitro studies seem to indicate that this reduction in shrinkage displacement could be detected by using the most accurate intraoral scanners currently available. Thus, subject to clinical validation, the occlusal displacement of a resin composite restoration may be used to assess its interfacial integrity. Copyright © 2017 The Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Electron and proton absorption calculations for a graphite/epoxy composite model. [large space structures

NASA Technical Reports Server (NTRS)

Long, E. R., Jr.

1979-01-01

The Bethe-Bloch stopping power relations for inelastic collisions were used to determine the absorption of electron and proton energy in cured neat epoxy resin and the absorption of electron energy in a graphite/epoxy composite. Absorption of electron energy due to bremsstrahlung was determined. Electron energies from 0.2 to 4.0 MeV and proton energies from 0.3 to 1.75 MeV were used. Monoenergetic electron energy absorption profiles for models of pure graphite, cured neat epoxy resin, and graphite/epoxy composites are reported. A relation is determined for depth of uniform energy absorption in a composite as a function of fiber volume fraction and initial electron energy. Monoenergetic proton energy absorption profiles are reported for the neat resin model. A relation for total proton penetration in the epoxy resin as a function of initial proton energy is determined. Electron energy absorption in the composite due to bremsstrahlung is reported. Electron and proton energy absorption profiles in cured neat epoxy resin are reported for environments approximating geosynchronous earth orbit.

Composite Properties of Polyimide Resins Made From "Salt-Like" Solution Precursors

NASA Technical Reports Server (NTRS)

Cano, Roberto J.; Weiser, Erik S.; SaintClair, Terry L.; Echigo, Yoshiaki; Kaneshiro, Hisayasu

1997-01-01

Recent work in high temperature materials at NASA Langley Research Center (LaRC (trademark)) have led to the development of new polyimide resin systems with very attractive properties. The majority of the work done with these resin systems has concentrated on determining engineering mechanical properties of composites prepared from a poly(amide acid) precursor. Three NASA Langley-developed polyimide matrix resins, LaRC (trademark) -IA, LaRC (trademark) -IAX, and LaRC (trademark) -8515, were produced via a salt-like process developed by Unitika Ltd. The 'salt-like' solutions (sixty-five percent solids in NMP) were prepregged onto Hexcel IM7 carbon fiber using the NASA LaRC Multipurpose Tape Machine. Process parameters were determined and composite panels fabricated. Mechanical properties are presented for these three intermediate modulus carbon fiber/polyimide matrix composites and compared to existing data on the same polyimide resin systems and IM7 carbon fiber manufactured via poly(amide acid) solutions (thirty-five percent solids in NMP). This work studies the effects of varying the synthetic route on the processing and mechanical properties of polyimide composites.

Tooth brush abrasion of paint-on resins for shade modification of crown and bridge resins.

PubMed

Fujii, Koichi; Ban, Seiji; McCabe, John F

2003-09-01

The purpose of this study was to evaluate the surface roughness and resistance to toothbrush abrasion of three experimental paint-on composite resins developed for the shade modification of crown and bridge resins. The paint-on resins had less filler volume fraction than restorative composites or the crown and bridge resins and consequently were of low viscosity. The maximum surface roughness (Rmax) and the maximum depth loss by abrasion for the paint-on resins following 40,000 cycles of brushing ranged from 2.45 to 4.07 microm and 8.63 to 13.67 microm, respectively. Rmax values were 37.7-67.5% lower than that for the crown and bridge resin subjected to the same test. Wear depth was 19.9-49.4% lower than for the crown and bridge resin. These results suggest that the paint-on resins are expected to have adequate resistance to toothbrush abrasion and may therefore be suitable for clinical use.

Development of Textile Reinforced Composites for Aircraft Structures

NASA Technical Reports Server (NTRS)

Dexter, H. Benson

1998-01-01

NASA has been a leader in development of composite materials for aircraft applications during the past 25 years. In the early 1980's NASA and others conducted research to improve damage tolerance of composite structures through the use of toughened resins but these resins were not cost-effective. The aircraft industry wanted affordable, robust structures that could withstand the rigors of flight service with minimal damage. The cost and damage tolerance barriers of conventional laminated composites led NASA to focus on new concepts in composites which would incorporate the automated manufacturing methods of the textiles industry and which would incorporate through-the-thickness reinforcements. The NASA Advanced Composites Technology (ACT) Program provided the resources to extensively investigate the application of textile processes to next generation aircraft wing and fuselage structures. This paper discusses advanced textile material forms that have been developed, innovative machine concepts and key technology advancements required for future application of textile reinforced composites in commercial transport aircraft. Multiaxial warp knitting, triaxial braiding and through-the-thickness stitching are the three textile processes that have surfaced as the most promising for further development. Textile reinforced composite structural elements that have been developed in the NASA ACT Program are discussed. Included are braided fuselage frames and window-belt reinforcements, woven/stitched lower fuselage side panels, stitched multiaxial warp knit wing skins, and braided wing stiffeners. In addition, low-cost processing concepts such as resin transfer molding (RTM), resin film infusion (RFI), and vacuum-assisted resin transfer molding (VARTM) are discussed. Process modeling concepts to predict resin flow and cure in textile preforms are also discussed.

Implications of resin-based composite (RBC) restoration on cuspal deflection and microleakage score in molar teeth: Placement protocol and restorative material.

PubMed

McHugh, Lauren E J; Politi, Ioanna; Al-Fodeh, Rami S; Fleming, Garry J P

2017-09-01

To assess the cuspal deflection of standardised large mesio-occluso-distal (MOD) cavities in third molar teeth restored using conventional resin-based composite (RBC) or their bulk fill restorative counterparts compared with the unbound condition using a twin channel deflection measuring gauge. Following thermocycling, the cervical microleakage of the restored teeth was assessed to determine marginal integrity. Standardised MOD cavities were prepared in forty-eight sound third molar teeth and randomly allocated to six groups. Restorations were placed in conjunction with (and without) a universal bonding system and resin restorative materials were irradiated with a light-emitting-diode light-curing-unit. The dependent variable was the restoration protocol, eight oblique increments for conventional RBCs or two horizontal increments for the bulk fill resin restoratives. The cumulative buccal and palatal cuspal deflections from a twin channel deflection measuring gauge were summed, the restored teeth thermally fatigued, immersed in 0.2% basic fuchsin dye for 24h, sectioned and examined for cervical microleakage score. The one-way analysis of variance (ANOVA) identified third molar teeth restored using conventional RBC materials had significantly higher mean total cuspal deflection values compared with bulk fill resin restorative restoration (all p<0.0001). For the conventional RBCs, Admira Fusion (bonded) third molar teeth had significantly the lowest microleakage scores (all p<0.001) while the Admira Fusion x-tra (bonded) bulk fill resin restored teeth had significantly the lowest microleakage scores compared with Tetric EvoCeram Bulk Fill (bonded and non-bonded) teeth (all p<0.001). Not all conventional RBCs or bulk fill resin restoratives behave in a similar manner when used to restore standardised MOD cavities in third molar teeth. It would appear that light irradiation of individual conventional RBCs or bulk fill resin restoratives may be problematic such that material selection is vital in the absence of clinical data. Copyright © 2017 The Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Effect of abutment shade, ceramic thickness, and coping type on the final shade of zirconia all-ceramic restorations: in vitro study of color masking ability.

PubMed

Oh, Seon-Hee; Kim, Seok-Gyu

2015-10-01

The aim of the study was to evaluate the effect of abutment shade, ceramic thickness, and coping type on the final shade of zirconia all-ceramic restorations. Three different types of disk-shaped zirconia coping specimens (Lava, Cercon, Zirkonzahn: ø10 mm × 0.4 mm) were fabricated and veneered with IPS e.max Press Ceram (shade A2), for total thicknesses of 1 and 1.5 mm. A total of sixty zirconia restoration specimens were divided into six groups based on their coping types and thicknesses. The abutment specimens (ø10 mm × 7 mm) were prepared with gold alloy, base metal (nickel-chromium) alloy, and four different shades (A1, A2, A3, A4) of composite resins. The average L*, a*, b* values of the zirconia specimens on the six abutment specimens were measured with a dental colorimeter, and the statistical significance in the effects of three variables was analyzed by using repeated measures analysis of variance (α=.05).The average shade difference (ΔE) values of the zirconia specimens between the A2 composite resin abutment and other abutments were also evaluated. The effects of zirconia specimen thickness (P<.001), abutment shade (P<.001), and type of zirconia copings (P<.003) on the final shade of the zirconia restorations were significant. The average ΔE value of Lava specimens (1 mm) between the A2 composite resin and gold alloy abutments was higher (close to the acceptability threshold of 5.5 ΔE) than th ose between the A2 composite resin and other abutments. This in-vitro study demonstrated that abutment shade, ceramic thickness, and coping type affected the resulting shade of zirconia restorations.

Composite Design and Engineering

NASA Astrophysics Data System (ADS)

van der Woude, J. H. A.; Lawton, E. L.

Fiberglass is a versatile and cost-effective reinforcement for composites. Many processes, resins, and forms of fiberglass facilitate this versatility. The design, engineering, manufacture, and properties of fiberglass-reinforced composite products from diverse thermoset and thermoplastic resins are described. The attributes of fiberglass-reinforced composites include its mechanical and chemical properties, lightweight, corrosion resistance, longevity, low total system cost, and Class A surface properties. Specific examples illustrate the importance of the form of the fiberglass reinforcement and of the interfacial bond between the glass fibers and the matrix resin in optimizing composite properties. In addition, recent advances are described with regard to the fabrication of fiberglass-reinforced wind turbine blades.

Dielectric properties of CaCu3Ti4O12-silicone resin composites

NASA Astrophysics Data System (ADS)

Babu, Sanjesh; Singh, Kirti; Govindan, Anil

2012-06-01

CaCu3Ti4O12 (CCTO)-silicone resin composites with various CCTO volume fractions were prepared. Relatively high dielectric constant ( ɛ=119) and low loss (tan δ=0.35) of the composites with CCTO volume fraction of 0.9 were observed. Two theoretical models were employed to predict the dielectric constant of these composites; the dielectric constant obtained via the Maxwell-Garnett model was in close agreement with the experimental data. The dielectric constant of CCTO-silicone resin composites showed a weak frequency dependence at the measuring frequency range and the loss tangent apparently decreases with increase in frequency.